  1. Electrospun submicron bioactive glass fibers for bone tissue scaffold.

    Science.gov (United States)

    Lu, H; Zhang, T; Wang, X P; Fang, Q F

    2009-03-01

    Submicron bioactive glass fibers 70S30C (70 mol% SiO(2), 30 mol% CaO) acting as bone tissue scaffolds were fabricated by electrospinning method. The scaffold is a hierarchical pore network that consists of interconnected fibers with macropores and mesopores. The structure, morphological characterization and mechanical properties of the submicron bioactive glass fibers were studied by XRD, EDS, FIIR, SEM, N(2) gas absorption analyses and nanoindentation. The effect of the voltage on the morphology of electrospun bioactive glass fibers was investigated. It was found that decreasing the applied voltage from 19 to 7 kV can facilitate the formation of finer fibers with fewer bead defects. The hardness and Young's modulus of submicron bioactive glass fibers were measured as 0.21 and 5.5 GPa, respectively. Comparing with other bone tissue scaffolds measured by nanoindentation, the elastic modulus of the present scaffold was relatively high and close to the bone.

  2. Submicron bioactive glass tubes for bone tissue engineering.

    Science.gov (United States)

    Xie, Jingwei; Blough, Eric R; Wang, Chi-Hwa

    2012-02-01

    Herein we describe a method to fabricate submicron bioactive glass tubes using sol-gel and coaxial electrospinning techniques for applications in bone tissue engineering. Heavy mineral oil and gel solution were delivered by two independent syringe pumps during the coaxial electrospinning process. Subsequently, submicron bioactive glass tubes were obtained by removal of poly(vinyl pyrrolidone) and heavy mineral oil via calcination at 600 °C for 5 h. Tubular structure was confirmed by scanning electron microscopy and transmission electron microscopy imaging. We examined the bioactivity of submicron bioactive glass tubes and fibers and evaluated their biocompatibility, using electrospun poly(ε-caprolactone) fibers--a bioinactive material--for comparison. The bioactivity of the glass tubes was examined in a simulated body fluid and they demonstrated the formation of hydroxyapatite-like minerals on both the outer and inner surfaces. In contrast, mineralization only occurred on their surface for bioactive glass solid fibers. Energy-dispersive X-ray data suggested that the bioactive glass tubes had a faster induction of mineral formation than the solid fibers. We demonstrate that the proliferation rate of mouse preosteoblastic MC3T3-E1 cells on bioactive glass tubes was comparable to that on solid fibers. We also show that bioactive glass tubes can be loaded with a model protein drug, bovine serum albumin, and that these structures exhibit delayed release properties. The bioactivity of released lysozyme can be as high as 90.9%. Taken together, these data suggest that submicron bioactive glass tubes could hold great potential for use in bone tissue engineering as well as topical drug or gene delivery. Copyright © 2011 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

  3. Facile synthesis and characterization of novel rapid-setting spherical sub-micron bioactive glasses cements and their biocompatibility in vitro.

    Science.gov (United States)

    Li, Yuli; Liang, Qiming; Lin, Cai; Li, Xian; Chen, Xiaofeng; Hu, Qing

    2017-06-01

    Dental pulp vitality is extremely important for the tooth viability, since it provides nutrition and forms the dentin. Bioactive glasses (BGs) may be promising materials for pulp repair due to their excellent abilities of rapidly bonding to bone and stimulating new bone growth. However, the unsatisfied handling property, low plasticity, and poor rapid-setting property of traditional BGs limit its application in vital pulp therapy. Spherical bioactive glasses (SBGs) exhibited higher osteogenesis and odontogenic differentiation than irregular BGs. This study focuses on the application of SBGs with rapid setting property for dental pulp repair. Here, SBGs with various compositions were successfully synthesized by a sol-gel process using dodecylamine (DDA) served as both a catalyst and a template. The maximum content of CaO in SBGs was about 15%. The non-bridge oxygen amounts of the SiO network and the apatite-forming ability increased with the content proportion of CaO and P2O5. Bioactive glass pulp capping materials (BGPCMs) were prepared by mixing the SBGs powders and the phosphate buffer solution (PBS). The K3CaH(PO4)2 and hydroxyapatite (HA) formed between SBGs particles as soon as they were mixed with PBS solution. The compressive strengths of fully set BCPCM-2 molded were measured to be 31.76±1.9577MPa after setting for 24h. The K3CaH(PO4)2 and the low crystallinity HA phases at the initial stage of solidification transformed to crystalline HA for 3days, and the compressive strength was still higher than 10MPa. Additionally, SBG-2 with a designed molar composition of 35% SiO2, 55% CaO and 10% P2O5 more promoted dental pulp cell proliferation, and could be potential pulp capping applications. Copyright © 2017. Published by Elsevier B.V.

  4. Bioactive glass in tissue engineering

    Science.gov (United States)

    Rahaman, Mohamed N.; Day, Delbert E.; Bal, B. Sonny; Fu, Qiang; Jung, Steven B.; Bonewald, Lynda F.; Tomsia, Antoni P.

    2011-01-01

    This review focuses on recent advances in the development and use of bioactive glass for tissue engineering applications. Despite its inherent brittleness, bioactive glass has several appealing characteristics as a scaffold material for bone tissue engineering. New bioactive glasses based on borate and borosilicate compositions have shown the ability to enhance new bone formation when compared to silicate bioactive glass. Borate-based bioactive glasses also have controllable degradation rates, so the degradation of the bioactive glass implant can be more closely matched to the rate of new bone formation. Bioactive glasses can be doped with trace quantities of elements such as Cu, Zn and Sr, which are known to be beneficial for healthy bone growth. In addition to the new bioactive glasses, recent advances in biomaterials processing have resulted in the creation of scaffold architectures with a range of mechanical properties suitable for the substitution of loaded as well as non-loaded bone. While bioactive glass has been extensively investigated for bone repair, there has been relatively little research on the application of bioactive glass to the repair of soft tissues. However, recent work has shown the ability of bioactive glass to promote angiogenesis, which is critical to numerous applications in tissue regeneration, such as neovascularization for bone regeneration and the healing of soft tissue wounds. Bioactive glass has also been shown to enhance neocartilage formation during in vitro culture of chondrocyte-seeded hydrogels, and to serve as a subchondral substrate for tissue-engineered osteochondral constructs. Methods used to manipulate the structure and performance of bioactive glass in these tissue engineering applications are analyzed. PMID:21421084

  5. Bioactive glasses and glass-ceramics.

    Science.gov (United States)

    Rawlings, R D

    1993-01-01

    Bioactive materials are designed to induce a specific biological activity; in most cases the desired biological activity is one that will give strong bonding to bone. A range of materials has been assessed as being capable of bonding to bone, but this paper is solely concerned with bioactive glasses and glass-ceramics. Firstly, the structure and processing of glasses and glass-ceramics are described, as a basic knowledge is essential for the understanding of the development and properties of the bioactive materials. The effect of composition and structure on the bioactivity is then discussed, and it will be shown that bioactivity is associated with the formation of an apatite layer on the surface of the implant. A survey of mechanical performance demonstrates that the structure and mechanical properties of glass-ceramics depend upon whether the processing involves casting or sintering and that the strength and toughness of glass-ceramics are superior to those of glasses. Attempts to further improve the mechanical performance by the use of non-monolithic components, i.e. bioactive coatings on metal substrates and glass and glass-ceramic matrix composites, are also reviewed and are shown to have varying degrees of success. Finally, some miscellaneous applications, namely bioactive bone cements and bone fillers, are briefly covered.

  6. Bioactive glasses: Frontiers and challenges

    Directory of Open Access Journals (Sweden)

    Larry L. Hench

    2015-11-01

    Full Text Available Bioactive glasses were discovered in 1969 and provided for the first time an alternative to nearly inert implant materials. Bioglass formed a rapid, strong and stable bond with host tissues. This article examines the frontiers of research crossed to achieve clinical use of bioactive glasses and glass-ceramics. In the 1980’s it was discovered that bioactive glasses could be used in particulate form to stimulate osteogenesis, which thereby led to the concept of regeneration of tissues. Later, it was discovered that the dissolution ions from the glasses behaved like growth factors, providing signals to the cells. This article summarizes the frontiers of knowledge crossed during four eras of development of bioactive glasses that have led from concept of bioactivity to widespread clinical and commercial use, with emphasis on the first composition, 45S5 Bioglass®. The four eras are: a discovery; b clinical application; c tissue regeneration; and d innovation. Questions still to be answered for the fourth era are included to stimulate innovation in the field and exploration of new frontiers that can be the basis for a general theory of bioactive stimulation of regeneration of tissues and application to numerous clinical needs.

  7. Bioactive glasses and glass-ceramics

    Directory of Open Access Journals (Sweden)

    de Aza, P. N.

    2007-04-01

    Full Text Available Since the late 1960´s, a great interest in the use of bioceramic materials for biomedical applications has been developed. In a previous paper, the authors reviewed crystalline bioceramic materials “sensus stricto”, it is to say, those ceramic materials, constituted for non-metallic inorganic compounds, crystallines and consolidates by thermal treatment of powders at high temperature. In the present review, the authors deal with those called bioactive glasses and glassceramics. Although all of them are also obtained by thermal treatment at high temperature, the first are amorphous and the second are obtained by devitrification of a glass, although the vitreous phase normally prevails on the crystalline phases. After an introduction to the concept of bioactive materials, a short historical review of the bioactive glasses development is made. Its preparation, reactivity in physiological media, mechanism of bonding to living tissues and mechanical strength of the bone-implant interface is also reported. Next, the concept of glass-ceramic and the way of its preparation are exposed. The composition, physicochemical properties and biological behaviour of the principal types of bioactive glasses and glass-ceramic materials: Bioglass®, Ceravital®, Cerabone®, Ilmaplant® and Bioverit® are also reviewed. Finally, a short review on the bioactive-glass coatings and bioactive-composites and most common uses of bioactive-glasses and glass-ceramics are carried out too.

    Desde finales de los años sesenta, se ha despertado un gran interés por el uso de los materiales biocerámicos para aplicaciones biomédicas. En un trabajo previo, los autores hicieron una revisión de los denominados materiales biocerámicos cristalinos en sentido estricto, es decir, de aquellos materiales, constituidos por compuestos inorgánicos no metálicos, cristalinos y consolidados mediante tratamientos térmicos a altas temperaturas. En el presente trabajo, los autores

  8. Bare Bones of Bioactive Glass

    Science.gov (United States)

    2000-01-01

    Paul Ducheyne, a principal investigator in the microgravity materials science program and head of the University of Pernsylvania's Center for Bioactive Materials and Tissue Engineering, is leading the trio as they use simulated microgravity to determine the optimal characteristics of tiny glass particles for growing bone tissue. The result could make possible a much broader range of synthetic bone-grafting applications. Even in normal gravity, bioactive glass particles enhance bone growth in laboratory tests with flat tissue cultures. Ducheyne and his team believe that using the bioactive microcarriers in a rotating bioreactor in microgravity will produce improved, three-dimensional tissue cultures. The work is sponsored by NASA's Office of Biological and Physical Research. The bioreactor is managed by the Biotechnology Cell Science Program at NASA's Johnson Space Center (JSC). NASA-sponsored bioreactor research has been instrumental in helping scientists to better understand normal and cancerous tissue development. In cooperation with the medical community, the bioreactor design is being used to prepare better models of human colon, prostate, breast and ovarian tumors. Cartilage, bone marrow, heart muscle, skeletal muscle, pancreatic islet cells, liver and kidney are just a few of the normal tissues being cultured in rotating bioreactors by investigators. Credit: NASA and University of Pennsylvania Center for Bioactive Materials and Tissue Engineering.

  9. Bioactive Glasses in Dentistry: A Review

    Directory of Open Access Journals (Sweden)

    Abbasi Z

    2015-03-01

    Full Text Available Bioactive glasses are silicate-based and can form a strong chemical bond with the tissues. These biomaterials are highly biocompatible and can form a hydroxyapatite layer when implanted in the body or soaked in the simulated body fluid. Due to several disadvantages, conventional glass processing method including melting of glass components, is replaced by sol-gel method with a large number of benefits such as low processing temperature, higher purity and homogeneity and therefore better control of bioactivity. Bioactive glasses have a wide range of applications, particularly in dentistry. These glasses can be used as particulates or monolithic shapes and porous or dense constructs in different applications such as remineralization or hypersensitivity treatment. Some properties of bioactive glasses such as antibacterial properties can be promoted by adding different elements into the glass. Bioactive glasses can also be used to modify different biocompatible materials that need to be bioactive. This study reviews the significant developments of bioactive glasses in clinical application, especially dentistry. Furthermore, we will discuss the field of bioactive glasses from beginning to the current developments, which includes processing methods, applications, and properties of these glasses.

  10. Bioactive glasses materials, properties and applications

    CERN Document Server

    Ylänen, Heimo

    2011-01-01

    Due to their biocompatibility and bioactivity, bioactive glasses are used as highly effective implant materials throughout the human body to replace or repair damaged tissue. As a result, they have been in continuous use since shortly after their invention in the late 1960s and are the subject of extensive research worldwide.Bioactive glasses provides readers with a detailed review of the current status of this unique material, its properties, technologies and applications. Chapters in part one deal with the materials and mechanical properties of bioactive glass, examining topics such

  11. Bioactive glasses potential biomaterials for future therapy

    CERN Document Server

    Kaur, Gurbinder

    2017-01-01

    This book describes the history, origin and basic characteristics of bioactive materials. It includes a chapter dedicated to hydroxyapatite mineral, its formation and its bioactive properties. The authors address how cytotoxicity is a determining step for bioactivity. Applications of bioactive materials in the contexts of tissue regeneration, bone regeneration and cancer therapy are also covered. Silicate, metallic and mesoporous glasses are described, as well as the challenges and future prospects of research in this field.

  12. Bioactive glass-ceramics coatings on alumina

    Energy Technology Data Exchange (ETDEWEB)

    Vitale Brovarone, C.; Verne, E.; Lupo, F. [Politecnico di Torino (Italy). Materials Science and Chemical Eng. Dept.; Moisescu, C. [Jena Univ. (Germany). Otto-Schott-Inst. fuer Glaschemie; Zanardi, L.; Bosetti, M.; Cannas, M. [Eastern Piemont Univ., Novara (Italy). Medical Science Dept.

    2001-07-01

    In this work, aiming to combine the mechanical performances of alumina with the surface properties of a bioactive material, we coated full density alumina substrates by a bioactive glass-ceramic GC. This latter was specially tailored, in term of costituents and specific quantity to have a thermal expansion coefficient close to that of alumina (8.5-9{sup *}10{sup -6}/ C) which is lower than most of the bioactive glasses and glass-ceramics already in use. In this way, we sought to avoid, as much as possible, the crack formation and propagation due to residual stresses generated by the thermal expansion coefficients mismatch. Furthermore, the high reactivity of alumina toward the glass-ceramic was carefully controlled to avoid deep compositional modification of the GC that will negatively affect its bioactivity. At this purpose, an intermediate layer of an appropriate glass G was coated prior to coat the bioactive glass-ceramic. On the materials obtained, preliminary biological tests have been done to evaluate glass-ceramic biocompatibility respect to alumina. (orig.)

  13. Interaction between bioactive glasses and human dentin.

    Science.gov (United States)

    Efflandt, S E; Magne, P; Douglas, W H; Francis, L F

    2002-06-01

    This study explores the interaction between bioactive glasses and dentin from extracted human teeth in simulated oral conditions. Bioactive glasses in the Na(2)O-CaO-P(2)O(5)-SiO(2) and MgO-CaO-P(2)O(5)-SiO(2) systems were prepared as polished disks. Teeth were prepared by grinding to expose dentin and etching with phosphoric acid. A layer of saliva was placed between the two, and the pair was secured with an elastic band and immersed in saliva at 37 degrees C for 5, 21 or 42 days. The bioactive glasses adhered to dentin, while controls showed no such interaction. A continuous interface between the bioactive glass and dentin was imaged using cryogenic-scanning electron microscopy (SEM). However, after alcohol dehydration and critical point drying, fracture occurred due to stresses from dentin shrinkage. SEM investigations showed a microstructurally different material at the fractured interface. Chemical analyses revealed that ions from the glass penetrated into the dentin and that the surface of the glass in contact with the dentin was modified. Microdiffractometry showed the presence of apatite at the interface. Bonding appears to be due to an affinity of collagen for the glass surface and chemical interaction between the dentin and glass, leading to apatite formation at the interface.

  14. Effect of particle size on the in vitro bioactivity, hydrophilicity and mechanical properties of bioactive glass-reinforced polycaprolactone composites

    Energy Technology Data Exchange (ETDEWEB)

    Tamjid, E. [Institute for Nanoscience and Nanotechnology (INST), Sharif University of Technology, Azadi Ave. P.O. Box: 11365-9466, 14588 Tehran (Iran, Islamic Republic of); Bagheri, R., E-mail: rezabagh@sharif.edu [Department of Materials Science and Engineering, Sharif University of Technology, Azadi Ave. P.O. Box: 11365-9466, 14588 Tehran (Iran, Islamic Republic of); Vossoughi, M. [Institute for Nanoscience and Nanotechnology (INST), Sharif University of Technology, Azadi Ave. P.O. Box: 11365-9466, 14588 Tehran (Iran, Islamic Republic of); Department of Chemical and Petroleum Engineering, Sharif University of Technology, Azadi Ave. P.O. Box: 11365-9466, 14588 Tehran (Iran, Islamic Republic of); Simchi, A., E-mail: simchi@sharif.edu [Institute for Nanoscience and Nanotechnology (INST), Sharif University of Technology, Azadi Ave. P.O. Box: 11365-9466, 14588 Tehran (Iran, Islamic Republic of); Department of Materials Science and Engineering, Sharif University of Technology, Azadi Ave. P.O. Box: 11365-9466, 14588 Tehran (Iran, Islamic Republic of)

    2011-10-10

    Polycaprolactone (PCL) composite films containing 5 wt.% bioactive glass (BG) particles of different sizes (6 {mu}m, 250 nm, < 100 nm) were prepared by solvent casting methods. The ultra-fine BG particles were prepared by high-energy mechanical milling of commercial 45S5 Bioglass (registered) particles. The characteristics of bioactive glass particles were studied by field-emission scanning electron microscopy (FE-SEM), transmission electron microscopy (TEM), dynamic light scattering (DLS), and X-ray diffraction (XRD) methods. In vitro bioactivity of the PCL/BG composite films was evaluated through immersion in the simulated body fluid (SBF). The films were analyzed by FE-SEM, energy dispersive spectrometry (EDS), XRD, and atomic force microscopy (AFM). The mechanical properties of highly-porous PCL/BG composites were examined on cylindrical specimens under quasi-static compression load. It was found that partial crystallization of amorphous BG particles during a prolonged mechanical milling occurred and calcium silicate (CaSiO{sub 3}) and sodium calcium silicate (Na{sub 2}CaSiO{sub 4}) phases were formed. The introduction of submicron BG particles (250 nm) was shown to improve the bioactivity of PCL films. In contrast to BG microparticles, the submicron BG particles were distributed on the film surfaces, providing a high surface exposure to SBF with an improved nanotopography. A notable increase in the stiffness and elastic modulus of the composite was also obtained. As compared to submicron BG particles, lower bioactivity and elastic modulus were acquired for PCL/BG nanoparticles. It was also shown that in spite of high specific surface area of the nanoparticles, partial crystallization during mechanical milling and agglomeration of the nanoparticles during processing decrease the bioactivity, hydrophilicity and mechanical response of the BG-reinforced PCL composites. Highlights: {yields} The effect of Bioglass particle size on the in vitro bioactivity of

  15. Synthesis and in vitro bioactivity of mesoporous bioactive glass scaffolds

    Energy Technology Data Exchange (ETDEWEB)

    Shih, C.J., E-mail: cjshih@kmu.edu.tw [Department of Fragrance and Cosmetic Science, College of Pharmacy, Kaohsiung Medical University, Kaohsiung 807, Taiwan (China); Chen, H.T. [Department of Fragrance and Cosmetic Science, College of Pharmacy, Kaohsiung Medical University, Kaohsiung 807, Taiwan (China); Huang, L.F. [School of Pharmacy, College of Pharmacy, Kaohsiung Medical University, Kaohsiung 807, Taiwan (China); Lu, P.S.; Chang, H.F. [Department of Fragrance and Cosmetic Science, College of Pharmacy, Kaohsiung Medical University, Kaohsiung 807, Taiwan (China); Chang, I.L., E-mail: 84004@cch.org.tw [Department of Orthopaedic Surgery, Chang-Hua Christian Hospital, Changhua 500, Taiwan (China)

    2010-06-15

    The main objective of the present study was to determine the effect of thermal treatment procedures (calcination temperature, heating rate and duration time) on the synthesis of SiO{sub 2}-CaO-P{sub 2}O{sub 5} mesoporous bioactive glass scaffolds. This is accomplished by thermogravimetric analyses, Fourier transform infrared (FTIR) absorption spectra, X-ray diffraction (XRD) and by analysis of nitrogen adsorption/desorption isotherms. In vitro bioactivity can also be assessed by the cytotoxic effect of the glasses on the NIH-3T3 cell line, and by characterization of MC-3T3-E1 cell attachment.

  16. Bioactive glass ceramics: properties and applications.

    Science.gov (United States)

    Kokubo, T

    1991-03-01

    Heat treatment of an MgO-CaO-SiO2-P2O5 glass gave a glass ceramic containing crystalline apatite (Ca10(PO4)6O,F2] and beta-wollastonite (CaO,SiO2) in an MgO-CaO-SiO2 glassy matrix. It showed bioactivity and a fairly high mechanical strength which decreased only slowly, even under load-bearing conditions in the body. It is used clinically as artificial vertebrae, iliac bones, etc. The bioactivity of this glass ceramic was attributed to apatite formation on its surface in the body. Dissolution of calcium and silicate ions from the glass ceramic was considered to play an important role in forming the surface apatite layer. It was shown that some new kinds of bioactive materials can be developed from CaO,SiO2-based glasses. Ceramics, metals and organic polymers coated with bone-like apatite were obtained when such materials were placed in the vicinity of a CaO,SiO2-based glass in a simulated body fluid. A bioactive bone cement which was hardened within 4 min and bonded to living bone, forming an apatite, was obtained by mixing a CaO,SiO2-based glass powder with a neutral ammonium phosphate solution. Its compressive strength reached 80 MPa comparable to that of poly(methyl methacrylate) within 3 d. A bioactive and ferromagnetic glass ceramic containing crystalline magnetite (Fe3O4) in a matrix of CaO,SiO2-based glassy and crystalline phases was obtained by a heat treatment of a Fe2O3-CaO.SiO2-B2O3-P2O5 glass. This glass ceramic was shown to be useful as thermoseeds for hyperthermia treatment of cancer.

  17. Hierarchically Nanoporous Bioactive Glasses for High Efficiency Immobilization of Enzymes

    DEFF Research Database (Denmark)

    He, W.; Min, D.D.; Zhang, X.D.

    2014-01-01

    Bioactive glasses with hierarchical nanoporosity and structures have been heavily involved in immobilization of enzymes. Because of meticulous design and ingenious hierarchical nanostructuration of porosities from yeast cell biotemplates, hierarchically nanostructured porous bioactive glasses can...

  18. Bioactive glass coatings for orthopedic metallic implants

    Energy Technology Data Exchange (ETDEWEB)

    Lopez-Esteban, Sonia; Saiz, Eduardo; Fujino, Sigheru; Oku, Takeo; Suganuma, Katsuaki; Tomsia, Antoni P.

    2003-06-30

    The objective of this work is to develop bioactive glass coatings for metallic orthopedic implants. A new family of glasses in the SiO2-Na2O-K2O-CaO-MgO-P2O5 system has been synthesized and characterized. The glass properties (thermal expansion, softening and transformation temperatures, density and hardness) are in line with the predictions of established empirical models. The optimized firing conditions to fabricate coatings on Ti-based and Co-Cr alloys have been determined and related to the glass properties and the interfacial reactions. Excellent adhesion to alloys has been achieved through the formation of 100-200 nm thick interfacial layers (Ti5Si3 on Ti-based alloys and CrOx on Co-Cr). Finally, glass coatings, approximately 100 mu m thick, have been fabricated onto commercial Ti alloy-based dental implants.

  19. Bioactive and inert dental glass-ceramics.

    Science.gov (United States)

    Montazerian, Maziar; Zanotto, Edgar Dutra

    2017-02-01

    The global market for dental materials is predicted to exceed 10 billion dollars by 2020. The main drivers for this growth are easing the workflow of dentists and increasing the comfort of patients. Therefore, remarkable research projects have been conducted and are currently underway to develop improved or new dental materials with enhanced properties or that can be processed using advanced technologies, such as CAD/CAM or 3D printing. Among these materials, zirconia, glass or polymer-infiltrated ceramics, and glass-ceramics (GCs) are of great importance. Dental glass-ceramics are highly attractive because they are easy to process and have outstanding esthetics, translucency, low thermal conductivity, high strength, chemical durability, biocompatibility, wear resistance, and hardness similar to that of natural teeth, and, in certain cases, these materials are bioactive. In this review article, we divide dental GCs into the following two groups: restorative and bioactive. Most restorative dental glass-ceramics (RDGCs) are inert and biocompatible and are used in the restoration and reconstruction of teeth. Bioactive dental glass-ceramics (BDGCs) display bone-bonding ability and stimulate positive biological reactions at the material/tissue interface. BDGCs are suggested for dentin hypersensitivity treatment, implant coating, bone regeneration and periodontal therapy. Throughout this paper, we elaborate on the history, processing, properties and applications of RDGCs and BDGCs. We also report on selected papers that address promising types of dental glass-ceramics. Finally, we include trends and guidance on relevant open issues and research possibilities. © 2016 Wiley Periodicals, Inc. J Biomed Mater Res Part A: 105A: 619-639, 2017. © 2016 Wiley Periodicals, Inc.

  20. Hierarchical Structures and Shaped Particles of Bioactive Glass and Its In Vitro Bioactivity

    Directory of Open Access Journals (Sweden)

    U. Boonyang

    2013-01-01

    Full Text Available In this study, bioactive glass particles with controllable structure and porosity were prepared using dual-templating methods. Block copolymers used as one template component produced mesopores in the calcined samples. Polymer colloidal crystals as the other template component yielded either three-dimensionally ordered macroporous (3DOM products or shaped bioactive glass nanoparticles. The in vitro bioactivity of these bioactive glasses was studied by soaking the samples in simulated body fluid (SBF at body temperature (37°C for varying lengths of time and monitoring the formation of bone-like apatite on the surface of the bioactive glass. A considerable bioactivity was found that all of bioactive glass samples have the ability to induce the formation of an apatite layer on its surface when in contact with SBF. The development of bone-like apatite is faster for 3DOM bioactive glasses than for nanoparticles.

  1. Fluoride-containing bioactive glasses: Glass design, structure, bioactivity, cellular interactions, and recent developments.

    Science.gov (United States)

    Shah, Furqan A

    2016-01-01

    Bioactive glasses (BGs) are known to bond to both hard and soft tissues. Upon exposure to an aqueous environment, BG undergoes ion exchange, hydrolysis, selective dissolution and precipitation of an apatite layer on their surface, which elicits an interfacial biological response resulting in bioactive fixation, inhibiting further dissolution of the glass, and preventing complete resorption of the material. Fluorine is considered one of the most effective in-vivo bone anabolic factors. In low concentrations, fluoride ions (F(-)) increase bone mass and mineral density, improve the resistance of the apatite structure to acid attack, and have well documented antibacterial properties. F(-) ions may be incorporated into the glass in the form of calcium fluoride (CaF2) either by part-substitution of network modifier oxides, or by maintaining the ratios of the other constituents relatively constant. Fluoride-containing bioactive glasses (FBGs) enhance and control osteoblast proliferation, differentiation and mineralisation. And with their ability to release fluoride locally, FBGs make interesting candidates for various clinical applications, dentinal tubule occlusion in the treatment of dentin hypersensitivity. This paper reviews the chemistry of FBGs and the influence of F(-) incorporation on the thermal properties, bioactivity, and cytotoxicity; and novel glass compositions for improved mechanical properties, processing, and bioactive potential. Copyright © 2015 Elsevier B.V. All rights reserved.

  2. Fluoride-containing bioactive glasses: Glass design, structure, bioactivity, cellular interactions, and recent developments

    Energy Technology Data Exchange (ETDEWEB)

    Shah, Furqan A., E-mail: furqan.ali.shah@biomaterials.gu.se

    2016-01-01

    Bioactive glasses (BGs) are known to bond to both hard and soft tissues. Upon exposure to an aqueous environment, BG undergoes ion exchange, hydrolysis, selective dissolution and precipitation of an apatite layer on their surface, which elicits an interfacial biological response resulting in bioactive fixation, inhibiting further dissolution of the glass, and preventing complete resorption of the material. Fluorine is considered one of the most effective in-vivo bone anabolic factors. In low concentrations, fluoride ions (F{sup −}) increase bone mass and mineral density, improve the resistance of the apatite structure to acid attack, and have well documented antibacterial properties. F{sup −} ions may be incorporated into the glass in the form of calcium fluoride (CaF{sub 2}) either by part-substitution of network modifier oxides, or by maintaining the ratios of the other constituents relatively constant. Fluoride-containing bioactive glasses (FBGs) enhance and control osteoblast proliferation, differentiation and mineralisation. And with their ability to release fluoride locally, FBGs make interesting candidates for various clinical applications, dentinal tubule occlusion in the treatment of dentin hypersensitivity. This paper reviews the chemistry of FBGs and the influence of F{sup −} incorporation on the thermal properties, bioactivity, and cytotoxicity; and novel glass compositions for improved mechanical properties, processing, and bioactive potential. - Highlights: • Fluoride ions form charged CaF{sup +} species rather than Si–F bonds. • Fluoride incorporation lowers glass transition and crystallisation temperatures. • Oxynitride and oxyfluoronitride glasses with superior mechanical properties • Mixed-alkali and alkali-free compositions with better processing characteristics.

  3. Assessment of nickel oxide substituted bioactive glass-ceramic on in vitro bioactivity and mechanical properties

    Energy Technology Data Exchange (ETDEWEB)

    Kumar Vyas, V.; Sampath Kumar, A.; Ali, A.; Prasad, S.; Srivastava, P.; Prasanna Mallick, S.; Ershad, Md.; Prasad Singh, S.; Pyare, R.

    2016-07-01

    Many type of oxide substituted glass-ceramics like strontium, cobalt, barium and titanium have shown bioactivity with improved mechanical properties. The present work reports the in vitro bioactivity and mechanical properties of nickel oxide substituted in bioactive glass-ceramic and results were compared with 45S5 bioactive glass-ceramic. Bioactive glass ceramics were processed through controlled crystallization of their respective bioactive glasses. The formed crystalline phases in bioactive glass-ceramics were identified using X-ray diffraction (XRD) analysis. The formation of HA layer was assessed by immersing them in the simulated body fluid (SBF) for different soaking periods. The formation of hydroxyapatite was confirmed by FTIR spectrometry, SEM and pH measurement. Densities and mechanical properties of the samples were found to increase considerably with an increasing the concentration of nickel oxide. A decrease in glass transition temperature (Tg) with NiO addition showed that the nickel oxide had acted as an intermediate in smaller quantities in the bioactive glass. The cell culture studies demonstrated that the samples containing low concentration of NiO from 0 to 1.65mol% were non-cytotoxic against osteoblast cells. Finally, this investigation clearly concluded that NiO doped bioactive glass would be potential biomaterials for biomedical applications. (Author)

  4. Spherical bioactive glass particles and their interaction with human mesenchymal stem cells in vitro.

    Science.gov (United States)

    Labbaf, Sheyda; Tsigkou, Olga; Müller, Karin H; Stevens, Molly M; Porter, Alexandra E; Jones, Julian R

    2011-02-01

    Sub-micron particles of bioactive glass (SMBGs) with composition 85 mol% SiO(2) and 15 mol% CaO were synthesised and characterised. Bioactivity was demonstrated by the formation of calcium apatite following 5 days immersion in simulated body fluid (SBF). The effect of a 24 h exposure of SMBGs (100 μg/ml, 150 μg/ml, 200 μg/ml) to human mesenchymal stem cells (hMSCs) on cell viability, metabolic activity and proliferation were determined using the LIVE/DEAD, MTT, total DNA and LDH assays after 1, 4 and 7 days of culture. None of the SMBG concentrations caused significant cytotoxicity at 1 and 4 days, but the doses of 150 and 200 μg/ml significantly decreased hMSC metabolic activity after 7 days of culture. Cell proliferation decreased as SMBG concentration increased; however none of the SMBGs tested had a significant effect on DNA quantity compared to the control. Confocal microscopy confirmed cellular uptake and localisation of the SMBGs in the hMSC cytoskeleton. Transmission electron microscopy revealed that the SMBGs localised inside the cell cytoplasm and cell endosomes. These findings are important for assessing the toxicity of sub-micron particles that may either be used as injectables for bone regeneration or generated by wear or degradation of bioactive glass scaffolds. Copyright © 2010 Elsevier Ltd. All rights reserved.

  5. Bioactive glasses: Importance of structure and properties in bone regeneration

    Science.gov (United States)

    Hench, Larry L.; Roki, Niksa; Fenn, Michael B.

    2014-09-01

    This review provides a brief background on the applications, mechanisms and genetics involved with use of bioactive glass to stimulate regeneration of bone. The emphasis is on the role of structural changes of the bioactive glasses, in particular Bioglass, which result in controlled release of osteostimulative ions. The review also summarizes the use of Raman spectroscopy, referred to hereto forward as bio-Raman spectroscopy, to obtain rapid, real time in vitro analysis of human cells in contact with bioactive glasses, and the osteostimulative dissolution ions that lead to osteogenesis. The bio-Raman studies support the results obtained from in vivo studies of bioactive glasses, as well as extensive cell and molecular biology studies, and thus offers an innovative means for rapid screening of new bioactive materials while reducing the need for animal testing.

  6. Bioactive glass 45S5 from diatom biosilica

    Directory of Open Access Journals (Sweden)

    Luqman A. Adams

    2017-12-01

    Full Text Available A major draw-back to large scale production of bioactive glasses is the high cost of the standard silica precursor, usually tetraethyl orthosilicate (TEOS. The current study describes a novel sol–gel preparation of 45S5 bioactive glass using diatom biosilica from cultured cells of the diatom, Aulacoseira granulata as substitute to TEOS. The glass formed was characterized using mechanical tester, scanning electron microscopy (SEM, energy dispersive X-ray analysis (EDX, X-ray diffraction (XRD and Fourier transform infrared (FTIR spectroscopy. Results showed that the glass possessed a compressive strength of 3.75 ± 0.18 and formed carbonated hydroxyapatite (HCA within 7 days in simulated body fluid (SBF, attributable to good surface chemistry. The performance of the glass was compared with that of those formed using TEOS. Diatom biosilica could be a potential economically friendly starting material for large scale fabrication of bioactive glasses.

  7. Abrasive wear behaviour of bio-active glass ceramics containing ...

    Indian Academy of Sciences (India)

    Unknown

    Abstract. In this study, abrasive wear behaviour of bio-active glass ceramic materials produced with two different processes is studied. Hot pressing process and conventional casting and controlled crystallization process were used to produce bio-active ceramics. Fracture toughness of studied material was calculated by.

  8. In vitro bioactivity of polymer matrices reinforced with a bioactive glass phase

    Directory of Open Access Journals (Sweden)

    Oréfice Rodrigo L.

    2000-01-01

    Full Text Available Composites that can mimic the in vitro bioactive behavior of bioactive glasses were designed to fulfill two main features of bioactive glasses that are responsible for their high bond-to-bone rates: (1 capability of providing ions such as calcium and phosphate to the nearby environment and (2 ideal surface structure that allows fast heterogeneous precipitation of hydroxy-carbonate-apatite (HCA. The novel composites were prepared by incorporating bioactive glass particles into polymer matrices. The in vitro bioactivity test was performed by introducing samples into a buffered solution as well as into a simulated body fluid solution. FTIR was used to evaluate the kinetics of HCA (hydroxy-carbonate-apatite precipitation. The results showed that the obtained composites can supply ions, such as silicates and phosphates in rates and concentrations comparable or superior than bulk bioactive glasses. Moreover, the surface chemistry of the composites was altered to mimic the surface of bioactive glasses. It was demonstrated that the in vitro bioactivity of the composites was enhanced by chemically modifying polymer surfaces through the introduction of special alkoxysilane groups.

  9. Influence of barium substitution on bioactivity, thermal and physico-mechanical properties of bioactive glass

    Energy Technology Data Exchange (ETDEWEB)

    Arepalli, Sampath Kumar, E-mail: askumar.rs.cer11@iitbhu.ac.in; Tripathi, Himanshu; Vyas, Vikash Kumar; Jain, Shubham; Suman, Shyam Kumar; Pyare, Ram; Singh, S.P., E-mail: spsinghceram@gmail.com

    2015-04-01

    Barium with low concentration in the glasses acts as a muscle stimulant and is found in human teeth. We have made a primary study by substituting barium in the bioactive glass. The chemical composition containing (46.1 − X) SiO{sub 2−}–24.3 Na{sub 2}O–26.9 CaO–2.6 P{sub 2}O{sub 5}, where X = 0, 0.4, 0.8, 1.2 and 1.6 mol% of BaO was chosen and melted in an electric furnace at 1400 ± 5 °C. The glasses were characterized to determine their use in biomedical applications. The nucleation and crystallization regimes were determined by DTA and the controlled crystallization was carried out by suitable heat treatment. The crystalline phase formed was identified by using XRD technique. Bioactivity of these glasses was assessed by immersion in simulated body fluid (SBF) for various time periods. The formation of hydroxy carbonate apatite (HCA) layer was identified by FTIR spectrometry, scanning electron microscope (SEM) and XRD which showed the presence of HCA as the main phase in all tested bioactive glass samples. Flexural strength and densities of bioactive glasses have been measured and found to increase with increasing the barium content. The human blood compatibility of the samples was evaluated and found to be pertinent. - Highlights: • In vitro bioactivity of soda-lime–baria-phospho-silicate glass was investigated. • HCA formed on surface of glasses was confirmed by XRD, SEM and FTIR spectrometry. • Mechanical properties of glasses were found to increase with barium addition. • Hemolysis showed that 1.2 mol% BaO bioactive glass exhibited better biocompatibility. • Barium substituted bioactive glasses can be used as bone implants.

  10. EFFECTS OF INCORPORATING NATURAL MINERALS ON PRODUCTION AND BIOACTIVITY OF BIOACTIVE GLASS CERAMICS

    Directory of Open Access Journals (Sweden)

    Franco Matias Stabile

    2016-07-01

    Full Text Available Two glass-ceramics composition were produced from natural minerals. Quartzes and feldspars were pre-selected on the basis of their purities studied by X-ray diffraction (XRD and chemical analysis. Prepared compositions of glasses precursors were two different theoretical leucite (KAlSi₂O₆ /Bioglass 45S5 (L/Bg ratios. Transformations of raw materials mixtures and glass precursors were studied by differential thermal analyses. On the basis of thermal analysis results, glass ceramics were produced and characterized by XRD. Glass-ceramics were composed of two major crystalline phases, leucite and sodium calcium silicate. Bioactivity tests were performed submerging the glass-ceramics into simulated body fluid (SBF for different periods (1, 5 and 10 days. Bioactive behavior was monitored by XRD and scanning electron microscopy (SEM. Studied samples were found to be bioactive, in which hydroxyapatite layer was developed within 5 days of contact with SBF.

  11. Modification of resin modified glass ionomer cement by addition of bioactive glass nanoparticles.

    Science.gov (United States)

    Valanezhad, Alireza; Odatsu, Tetsuro; Udoh, Koichi; Shiraishi, Takanobu; Sawase, Takashi; Watanabe, Ikuya

    2016-01-01

    In the present study, sol-gel derived nanoparticle calcium silicate bioactive glass was added to the resin-modified light cure glass-ionomer cement to assess the influence of additional bioactive glass nanoparticles on the mechanical and biological properties of resin-modified glass-ionomer cement. The fabricated bioactive glass nanoparticles added resin-modified glass-ionomer cements (GICs) were immersed in the phosphate buffer solution for 28 days to mimic real condition for the mechanical properties. Resin-modified GICs containing 3, 5 and 10 % bioactive glass nanoparticles improved the flexural strength compared to the resin-modified glass-ionomer cement and the samples containing 15 and 20 % bioactive glass nanoparticles before and after immersing in the phosphate buffer solution. Characterization of the samples successfully expressed the cause of the critical condition for mechanical properties. Cell study clarified that resin-modified glass-ionomer cement with high concentrations of bioactive glass nanoparticles has higher cell viability and better cell morphology compare to control groups. The results for mechanical properties and toxicity approved that the considering in selection of an optimum condition would have been a more satisfying conclusion for this study.

  12. Reaction kinetics of bioactive glass and a resorbable polysaccharide

    Energy Technology Data Exchange (ETDEWEB)

    Thompson, I.; Hench, L.L. [Imperial Coll. of Science, Technology and Medicine, London (United Kingdom). Dept. of Materials

    2001-07-01

    The kinetics of bioactive glass systems has been well documented. The addition of a resorpable polysaccharide, dextran, has improved the handling properties of particulate glass. This paper describes the methodology that has shown the Bioglass {sup trademark} putty system increases the crystallisation of the amorphous calcium hydroxide layer by just 5 hours when compared to Bioglass {sup trademark} particles alone. (orig.)

  13. Investigation of bioactivity and cell effects of nano-porous sol–gel derived bioactive glass film

    Energy Technology Data Exchange (ETDEWEB)

    Ma, Zhijun, E-mail: mokuu@zju.edu.cn [State Key Laboratory of Luminescent Materials and Devices, South China University of Technology, Guangzhou, 510640 (China); Ji, Huijiao [College of Life Science, Zhejiang University, Hangzhou, 310028 (China); Hu, Xiaomeng [School of Materials Science and Engineering, South China University of Technology, Guangzhou, 510640 (China); Teng, Yu [State Key Laboratory of Luminescent Materials and Devices, South China University of Technology, Guangzhou, 510640 (China); Zhao, Guiyun; Mo, Lijuan; Zhao, Xiaoli [College of Life Science, Zhejiang University, Hangzhou, 310028 (China); Chen, Weibo [School of Materials Science and Engineering, South China University of Technology, Guangzhou, 510640 (China); Qiu, Jianrong, E-mail: qjr@scut.edu.cn [State Key Laboratory of Luminescent Materials and Devices, South China University of Technology, Guangzhou, 510640 (China); Zhang, Ming, E-mail: zhangming201201@126.com [College of Life Science, Zhejiang University, Hangzhou, 310028 (China)

    2013-11-01

    In orthopedic surgery, bioactive glass film coating is extensively studied to improve the synthetic performance of orthopedic implants. A lot of investigations have confirmed that nano-porous structure in bioactive glasses can remarkably improve their bioactivity. Nevertheless, researches on preparation of nano-porous bioactive glasses in the form of film coating and their cell response activities are scarce. Herein, we report the preparation of nano-porous bioactive glass film on commercial glass slide based on a sol–gel technique, together with the evaluation of its in vitro bioactivity through immersion in simulated body fluid and monitoring the precipitation of apatite-like layer. Cell responses of the samples, including attachment, proliferation and osteogenic differentiation, were also investigated using BMSCS (bone marrow derived mesenchymal stem cells) as a model. The results presented here provide some basic information on structural influence of bioactive glass film on the improvement of bioactivity and cellular effects.

  14. A study of fracture and inelastic behavior of bioactive glass-ceramics and glasses.

    Science.gov (United States)

    Hirao, K; Benino, Y; Soga, N

    1992-01-01

    The fracture and inelastic behavior of A-W glass-ceramics, phosphate glasses, silicate glasses, and borate glasses were determined in simulated body fluid (SBF), kerosene, and water. By using the stable crack growth technique, an inelastic behavior was observed on the diagram of load versus load-point displacement. From these studies, it was suggested that the inelastic behavior of bioactive glass-ceramics was produced by the plastic deformation of glassy phase on the grain boundary.

  15. Nano/macro porous bioactive glass scaffold

    Science.gov (United States)

    Wang, Shaojie

    Bioactive glass (BG) and ceramics have been widely studied and developed as implants to replace hard tissues of the musculo-skeletal system, such as bones and teeth. Recently, instead of using bulk materials, which usually do not degrade rapidly enough and may remain in the human body for a long time, the idea of bioscaffold for tissue regeneration has generated much interest. An ideal bioscaffold is a porous material that would not only provide a three-dimensional structure for the regeneration of natural tissue, but also degrade gradually and, eventually be replaced by the natural tissue completely. Among various material choices the nano-macro dual porous BG appears as the most promising candidate for bioscaffold applications. Here macropores facilitate tissue growth while nanopores control degradation and enhance cell response. The surface area, which controls the degradation of scaffold can also be tuned by changing the nanopore size. However, fabrication of such 3D structure with desirable nano and macro pores has remained challenging. In this dissertation, sol-gel process combined with spinodal decomposition or polymer sponge replication method has been developed to fabricate the nano-macro porous BG scaffolds. Macropores up to 100microm are created by freezing polymer induced spinodal structure through sol-gel transition, while larger macropores (>200um) of predetermined size are obtained by the polymer sponge replication technique. The size of nanopores, which are inherent to the sol-gel method of glass fabrication, has been tailored using several approaches: Before gel point, small nanopores are generated using acid catalyst that leads to weakly-branched polymer-like network. On the other hand, larger nanopores are created with the base-catalyzed gel with highly-branched cluster-like structure. After the gel point, the nanostructure can be further modified by manipulating the sintering temperature and/or the ammonia concentration used in the solvent

  16. History and trends of bioactive glass-ceramics.

    Science.gov (United States)

    Montazerian, Maziar; Dutra Zanotto, Edgar

    2016-05-01

    The interest around bioactive glass-ceramics (GCs) has grown significantly over the last two decades due to their appropriate biochemical and mechanical properties. The intense research effort in this field has led to some new commercial products for biomedical applications. This review article begins with the basic concepts of GC processing and development via controlled heat treatments of monolithic pieces or sinter-crystallization of powdered glasses. We then go on to describe the processing, properties, and applications of some commercial bioactive GCs and discuss selected valuable reported researches on several promising types of bioactive GCs. The article finishes with a section on open relevant research directions for bioactive GC development. © 2016 Wiley Periodicals, Inc.

  17. Effect of nitrogen and fluorine on mechanical properties and bioactivity in two series of bioactive glasses.

    Science.gov (United States)

    Bachar, Ahmed; Mercier, Cyrille; Tricoteaux, Arnaud; Hampshire, Stuart; Leriche, Anne; Follet, Claudine

    2013-07-01

    Bioactive glasses are able to bond to bone through formation of carbonated hydroxyapatite in body fluids, and fluoride-releasing bioactive glasses are of interest for both orthopaedic and, in particular, dental applications for caries inhibition. However, because of their poor strength their use is restricted to non-load-bearing applications. In order to increase their mechanical properties, doping with nitrogen has been performed on two series of bioactive glasses: series (I) was a "bioglass" composition (without P2O5) within the quaternary system SiO2-Na2O-CaO-Si3N4 and series (II) was a simple substitution of CaF2 for CaO in series (I) glasses keeping the Na:Ca ratio constant. The objective of this work was to evaluate the effect of the variation in nitrogen and fluorine content on the properties of these glasses. The density, glass transition temperature, hardness and elastic modulus all increased linearly with nitrogen content which indicates that the incorporation of nitrogen stiffens the glass network because N is mainly in 3-fold coordination with Si atoms. Fluorine addition significantly decreases the thermal property values but the mechanical properties of these glasses remain unchanged with fluorine. The combination of both nitrogen and fluorine in oxyfluoronitride glasses gives better mechanical properties at much lower melting temperatures since fluorine reduces the melting point, allows higher solubility of nitrogen and does not affect the higher mechanical properties arising from incorporation of nitrogen. The characterization of these N and F substituted bioactive glasses using (29)Si MAS NMR has shown that the increase in rigidity of the glass network can be explained by the formation of SiO3N, SiO2N2 tetrahedra and Q(4) units with extra bridging anions at the expense of Q(3) units. Bioactivity of the glasses was investigated in vitro by examining apatite formation on the surface of glasses treated in acellular simulated body fluid (SBF) with ion

  18. In vitro biocompatibility tests of glass ionomer cements impregnated with collagen or bioactive glass to fibroblasts.

    Science.gov (United States)

    Subbarao, C; Neelakantan, P; Subbarao, C V

    2012-01-01

    To evaluate the biocompatibility of glass ionomer cement (GIC) impregnated with collagen or bioactive glass to BHK-21 fibroblasts in vitro. Mineral Trioxide Aggregate was used as the standard for comparison. Human maxillary central incisors (n = 70) were instrumented with a rotary NiTi system and filled. Following resection of the apical 3mm, root end cavities were prepared and restored with conventional GIC (group 1) or GIC with 0.01%, 0.1% or 1% collagen (groups 2, 3, 4 respectively) or, 10%, 30% or 50% bioactive glass (groups 5, 6, 7 respectively), or Mineral Trioxide Aggregate (group 8). The root slices were incubated in tissue culture plates with BHK-21 fibroblast cell line. Phase contrast and scanning electron microscopes were used to score cell quantity, morphology and cell attachment. The data were statistically analyzed by one way ANOVA with Post Hoc Tukey HSD test (p = 0.05). Group 5 showed the highest scores which was significantly higher than all other groups (p 0.05). Glass ionomer cement with 10% bioactive glass showed better adhesion and spreading of cells than glass ionomer cement with 0.01% collagen. The biocompatibility of collagen and bioactive glass was concentration dependent. The addition of bioactive glass improved the biocompatibility of glass ionomer cement to fibroblasts better than addition of collagen.

  19. A review of glass-ionomers: From conventional glass-ionomer to bioactive glass-ionomer

    Science.gov (United States)

    Khoroushi, Maryam; Keshani, Fateme

    2013-01-01

    Materials used in the body, especially the materials used in various oral cavity regions should be stable and passive without any interactions with the body tissues or fluids. Dental amalgam, composite resins and dental cements are the materials of choice with such properties. The first attempts to produce active materials, which could interact with the human body tissues and fluids were prompted by the concept that fluoride-releasing materials exert useful effects in the body. The concept of using the “smart” materials in dentistry has attracted a lot of attention in recent years. Conventional glass-ionomer (GI) cements have a large number of applications in dentistry. They are biocompatible with the dental pulp to some extent. GI is predominantly used as cements in dentistry; however, they have some disadvantages, the most important of which is lack of adequate strength and toughness. In an attempt to improve the mechanical properties of the conventional GI, resin-modified glass-ionomers have been marketed, with hydrophilic monomers, such as hydroxyethyl methacrylated (HEMA). Some recent studies have evaluated GI with bioactive glass in its structure to validate the claims that such a combination will improve tooth bioactivity, regeneration capacity and restoration. There is ever-increasing interest in the application of bioactive materials in the dental field in an attempt to remineralize affected dentin. The aim of this review article is to evaluate these materials and their characteristics and applications. PMID:24130573

  20. A review of glass-ionomers: From conventional glass-ionomer to bioactive glass-ionomer

    Directory of Open Access Journals (Sweden)

    Maryam Khoroushi

    2013-01-01

    Full Text Available Materials used in the body, especially the materials used in various oral cavity regions should be stable and passive without any interactions with the body tissues or fluids. Dental amalgam, composite resins and dental cements are the materials of choice with such properties. The first attempts to produce active materials, which could interact with the human body tissues and fluids were prompted by the concept that fluoride-releasing materials exert useful effects in the body. The concept of using the "smart" materials in dentistry has attracted a lot of attention in recent years. Conventional glass-ionomer (GI cements have a large number of applications in dentistry. They are biocompatible with the dental pulp to some extent. GI is predominantly used as cements in dentistry; however, they have some disadvantages, the most important of which is lack of adequate strength and toughness. In an attempt to improve the mechanical properties of the conventional GI, resin-modified glass-ionomers have been marketed, with hydrophilic monomers, such as hydroxyethyl methacrylated (HEMA. Some recent studies have evaluated GI with bioactive glass in its structure to validate the claims that such a combination will improve tooth bioactivity, regeneration capacity and restoration. There is ever-increasing interest in the application of bioactive materials in the dental field in an attempt to remineralize affected dentin. The aim of this review article is to evaluate these materials and their characteristics and applications.

  1. Effect of nanoparticulate bioactive glass particles on bioactivity and cytocompatibility of poly(3-hydroxybutyrate) composites.

    Science.gov (United States)

    Misra, Superb K; Ansari, Tahera; Mohn, Dirk; Valappil, Sabeel P; Brunner, Tobias J; Stark, Wendelin J; Roy, Ipsita; Knowles, Jonathan C; Sibbons, Paul D; Jones, Eugenia Valsami; Boccaccini, Aldo R; Salih, Vehid

    2010-03-06

    This work investigated the effect of adding nanoparticulate (29 nm) bioactive glass particles on the bioactivity, degradation and in vitro cytocompatibility of poly(3-hydroxybutyrate) (P(3HB)) composites/nano-sized bioactive glass (n-BG). Two different concentrations (10 and 20 wt %) of nanoscale bioactive glass particles of 45S5 Bioglass composition were used to prepare composite films. Several techniques (Raman spectroscopy, scanning electron microscopy, atomic force microscopy, energy dispersive X-ray) were used to monitor their surface and bioreactivity over a 45-day period of immersion in simulated body fluid (SBF). All results suggested the P(3HB)/n-BG composites to be highly bioactive, confirmed by the formation of hydroxyapatite on material surfaces upon immersion in SBF. The weight loss and water uptake were found to increase on increasing bioactive glass content. Cytocompatibility study (cell proliferation, cell attachment, alkaline phosphatase activity and osteocalcin production) using human MG-63 osteoblast-like cells in osteogenic and non-osteogenic medium showed that the composite substrates are suitable for cell attachment, proliferation and differentiation.

  2. Effect of nanoparticulate bioactive glass particles on bioactivity and cytocompatibility of poly(3-hydroxybutyrate) composites

    Science.gov (United States)

    Misra, Superb K.; Ansari, Tahera; Mohn, Dirk; Valappil, Sabeel P.; Brunner, Tobias J.; Stark, Wendelin J.; Roy, Ipsita; Knowles, Jonathan C.; Sibbons, Paul D.; Jones, Eugenia Valsami; Boccaccini, Aldo R.; Salih, Vehid

    2010-01-01

    This work investigated the effect of adding nanoparticulate (29 nm) bioactive glass particles on the bioactivity, degradation and in vitro cytocompatibility of poly(3-hydroxybutyrate) (P(3HB)) composites/nano-sized bioactive glass (n-BG). Two different concentrations (10 and 20 wt %) of nanoscale bioactive glass particles of 45S5 Bioglass composition were used to prepare composite films. Several techniques (Raman spectroscopy, scanning electron microscopy, atomic force microscopy, energy dispersive X-ray) were used to monitor their surface and bioreactivity over a 45-day period of immersion in simulated body fluid (SBF). All results suggested the P(3HB)/n-BG composites to be highly bioactive, confirmed by the formation of hydroxyapatite on material surfaces upon immersion in SBF. The weight loss and water uptake were found to increase on increasing bioactive glass content. Cytocompatibility study (cell proliferation, cell attachment, alkaline phosphatase activity and osteocalcin production) using human MG-63 osteoblast-like cells in osteogenic and non-osteogenic medium showed that the composite substrates are suitable for cell attachment, proliferation and differentiation. PMID:19640877

  3. [Cytocompatibility of two porous bioactive glass-ceramic in vitro].

    Science.gov (United States)

    Zhang, Yan; Jiang, Xinquan; Zhang, Xiuli; Wang, Deping; Zhen, Lei

    2013-06-01

    To compare the cytocompatibility of two kinds porous bioactive glass-ceramic made by same raw materials. Apatite/wollastonite bioactive glass-ceramic (4006) were prepared by sol-gel method, and bioactive glass (45S5) were prepared by melting method. Bone marrow stromal cells (BMSCs) were cultivated, differentiated and proliferated into osteoblasts, from a rabbit's marrow in the differentiatiofn culture medium with active function. The viability of BMSCs cultivated with extraction of these two kinds of biomaterial, which could represent the cytotoxicity effect of 4006 and 45S5 against BMSCs, was evaluated by the MTp assay. BMSCs were seeded and cocultivated with two kinds of biomaterial scaffolds respectively in vitro. The proliferation and biological properties of cells adhered to scaffolds were observed by inverted phase contrast microscope, scanning electron microscope (SEM), and environmental scanning electron microscope (ESEM), and a suitable cell amount for seeding on the scaffold was searched. There was no difference on the viability of BMSCs only cultured for one day by complete extract of 4006 and culture medium (P>0.05), but there was significant difference between them when the cells had been cultured for 3 days(Pglass-ceramic has good bioactivity and cytocompatibility. Therefore, it may have the potential to be a new cell vehicle for bone tissue engineering. And the suitable seeding cell amount of apatite/wollastonite bioactive glass-ceramic should be 2x10(7) cells.mL-1 or even more than that.

  4. A heat-generating bioactive glass-ceramic for hyperthermia.

    Science.gov (United States)

    Ohura, K; Ikenaga, M; Nakamura, T; Yamamuro, T; Ebisawa, Y; Kokubo, T; Kotoura, Y; Oka, M

    1991-01-01

    Glass plates of the chemical composition: CaO (29.0), SiO 2 (31.0), Fe 2O 3 (40.0), B 2O 3 (3.0), P 2O 5 (3.0) in weight ratio were heated to 1050 degrees C at a rate of 5 degrees C/min and then cooled to laboratory temperature. The resulting glass-ceramic containing magnetite and wollastonite crystals showed high-saturation magnetization. The bonding ability of this new glass-ceramic to bone tissue was evaluated using rabbit tibiae, and compared with glass of the same composition. This glass-ceramic formed a Ca, P-rich layer on its surface and bonded tightly with bone within 8 weeks of implantation. However, the glass did not form this Ca, P-rich layer, nor had it bonded with bone at 25 weeks. The bone-heating ability of this glass-ceramic was investigated by applying a max. 300-Oe, 100-kHz magnetic field. The granules of the glass-ceramic filled in the rabbit tibiae heated the whole surrounding bone to more than 42 degrees C and maintained this temperature for 30 min. Bioactive ceramics reinforce the mechanical strength of bone tissue. Furthermore, this heat-generating bioactive glass-ceramic can be used for hyperthermic treatment of bone tumors.

  5. Bioactive glass for long bone infection: a systematic review.

    Science.gov (United States)

    Aurégan, Jean-Charles; Bégué, Thierry

    2015-12-01

    Long bone infection remains a challenging situation for the orthopaedic surgeon. For most, treatment comprises a thorough debridement of all the infected bone, the filling of the resultant cavity with a bone substitute, and general antibiotics for a certain time. However, the type of bone substitute to insert in the cavity is still debated. In this study, we aimed to systematically review the results of studies using bioactive glass for long bone infection in the clinical setting. We searched systematically Medline via Pubmed for studies published until August 2015 that report the results of bioactive glass for long bone infection in humans. Three studies, including a total of 41 patients, met the inclusion criteria. Mean age was 46.5 (16-84). Twenty-nine were male and twelve were female. Period of inclusion went from 2007 to 2013. All the patients had a clinically and radiologically diagnosed osteomyelitis. They all underwent a state of the art surgical procedure to address osteomyelitis. All the patients were implanted with BAG-S53P4 granules (BonAlive Biomaterials Ltd, Turku, Finland) to fill in the resultant cavity. Mean volume inserted was 16.8 milliliters (2-60). After a mean follow-up of 21 months (10-38), three cases of osteomyelitis recurred. In two cases, a new procedure was performed. No complication directly related to the bioactive glass was reported. Despite a limited use for long bone infection in humans, bioactive glass seems to be an interesting option as bone substitute after thorough bone debridement and skin coverage. It associates antibacterial activities, osteoconductive properties and vascular stimulation. From this review, bioactive glass seems to be a useful bone substitute for long bone infection in humans. Few recurrences occurred after its use. In these cases, the volume of bone glass to insert was frequently underestimated and/or the skin coverage not adequate. Copyright © 2015 Elsevier Ltd. All rights reserved.

  6. Bioactive glass coupling with natural polyphenols: Surface modification, bioactivity and anti-oxidant ability

    Energy Technology Data Exchange (ETDEWEB)

    Cazzola, Martina [Politecnico di Torino, Department of Applied Science and Technology, Institute of Materials Physics and Engineering, C.so Duca degli Abruzzi 24, Torino 10129 (Italy); Corazzari, Ingrid [Università degli Studi di Torino, Department of Chemistry, Via Pietro Giuria 7, Torino 10125 (Italy); Centro Interdipartimentale “G. Scansetti” per lo studio degli amianti e di altri particolati nocivi, Via Pietro Giuria 9, 10125 Torino (Italy); Prenesti, Enrico [Università degli Studi di Torino, Department of Chemistry, Via Pietro Giuria 7, Torino 10125 (Italy); Bertone, Elisa [Politecnico di Torino, Department of Applied Science and Technology, Institute of Materials Physics and Engineering, C.so Duca degli Abruzzi 24, Torino 10129 (Italy); Vernè, Enrica, E-mail: enrica.verne@polito.it [Politecnico di Torino, Department of Applied Science and Technology, Institute of Materials Physics and Engineering, C.so Duca degli Abruzzi 24, Torino 10129 (Italy); Ferraris, Sara [Politecnico di Torino, Department of Applied Science and Technology, Institute of Materials Physics and Engineering, C.so Duca degli Abruzzi 24, Torino 10129 (Italy)

    2016-03-30

    Graphical abstract: - Highlights: • Surface functionalization of bioactive glass with biomolecules has been optimized. • Biomolecules are present and active on the glass surface after functionalization. • Biomolecules affect deposition kinetics and morphology of hydroxyapatite. • Free radical scavenging activity is seen for the first time on bioactive glasses. - Abstract: Polyphenols are actually achieving an increasing interest due to their potential health benefits, such as antioxidant, anticancer, antibacterial and bone stimulation abilities. However their poor bioavailability and stability hamper an effective clinical application as therapeutic principles. The opportunity to couple these biomolecules with synthetic biomaterials, in order to obtain local delivery at the site of interest, improve their bioavailability and stability and combine their properties with the ones of the substrate, is a challenging opportunity for the biomedical research. A silica based bioactive glass, CEL2, has been successfully coupled with gallic acid and natural polyphenols extracted from red grape skins and green tea leaves. The effectiveness of grafting has been verified by means of XPS analyses and the Folin&Ciocalteu tests. In vitro bioactivity has been investigated by soaking in simulated body fluid (SBF). Surface modification after functionalization and early stage reactivity in SBF have been studied by means of zeta potential electrokinetic measurements in KCl and SBF. Finally the antioxidant properties of bare and modified bioactive glasses has been investigated by means of the evaluation of free radical scavenging activity by Electron Paramagnetic Resonance (EPR)/spin trapping technique after UV photolysis of H{sub 2}O{sub 2} highlighting scavenging activity of the bioactive glass.

  7. Chitosan/bioactive glass nanoparticle composite membranes for periodontal regeneration

    NARCIS (Netherlands)

    Mota, J.; Yu, N.; Caridade, S.G.; Luz, G.M.; Gomes, M.E.R.; Reis, R.L.; Jansen, J.A.; Walboomers, X.F.; Mano, J.F.

    2012-01-01

    Barrier membranes are used in periodontal applications with the aim of supporting periodontal regeneration by physically blocking migration of epithelial cells. The present work proposes a combination of chitosan (CHT) with bioactive glass nanoparticles (BG-NPs) in order to produce a novel guided

  8. Treatment of Aneurysmal Bone Cysts with Bioactive Glass in Children.

    Science.gov (United States)

    Syvänen, J; Nietosvaara, Y; Kohonen, I; Koskimies, E; Haara, M; Korhonen, J; Pajulo, O; Helenius, I

    2017-09-01

    Aneurysmal bone cysts represent about 1% of primary bone tumors. The standard treatment is curettage, followed by local adjuvant treatments and bone grafting. The problem is the high recurrence rate. The purpose of this study was to evaluate retrospectively the use of bioactive glass as a filling material in the treatment of aneurysmatic bone cysts in children. A total of 18 consecutive children (mean 11.3 years at surgery; 10 males; 11 lower, 6 upper limb, 1 pelvis; 15 with primary surgery) with histologically proven primary aneurysmal bone cysts operated with curettage and bioactive glass filling between 2008 and 2013 were evaluated after a mean follow-up of 2.0 years (range, 0.7-5.1 years). Two (11%) patients showed evidence of aneurysmal bone cyst recurrence and both have been re-operated for recurrence. Bone remodeling was noted in all patients with remaining growth and no growth plate disturbances were recorded. Two patients needed allogeneic blood transfusion. No intraoperative or postoperative complications were recorded. We conclude that bioactive glass is a suitable filling material for children with primary aneurysmal bone cyst. Bioactive glass did not affect bone growth and no side effects were reported.

  9. Absorbability of bulk sol-gel bioactive glasses

    Energy Technology Data Exchange (ETDEWEB)

    Hamadouche, M.; Meunier, A.; Blanchat, C.; Sedel, L. [Paris-7 Univ. (France). Lab. de Recherches Orthopediques; Greenspan, D.C.; Zhong, J.P.; Torre, G.P. la [US Biomaterials Corp., Alachua, FL (United States)

    2001-07-01

    Melt-derived bioactive glasses have been used with success in various clinical applications for over 10 years. Recently, particles of sol-gel derived bioactive glasses with an initial high specific area have exhibited high osteoconductive properties, but also a significant degradability. In this work, we explored the in-vivo bioactivity and degradability of bulk sol-gel derived glasses. Two sol-gel compositions (58S and 77S Bioglass) were used. Bulk 45S5 were used as a control. Both sol-gel derived demonstrated similar osteoconductive properties to 45S% Bioglass. In addition, absorbability was observed for sol-gel derived glasses after 12 weeks of implantation. Total absorption reached 40% after 52 weeks. No degradation could be measured in the case of 45S5 melt derived Bioglass. The degradation process was highly time dependent as demonstrated by regression analysis. New bone formation was found to fill in areas that had been resorbed similar to bone remodeling. New bone was found to fill in areas that had been absorbed, similar to natural bone remodeling. This absorbability can be assumed to be at least partially related to an osteoclastic resorption, as viable osteoclasts-like cells were found directly in contact with the glass surfaces. (orig.)

  10. Silver-containing mesoporous bioactive glass with improved antibacterial properties.

    Science.gov (United States)

    Gargiulo, Nicola; Cusano, Angela Maria; Causa, Filippo; Caputo, Domenico; Netti, Paolo Antonio

    2013-09-01

    The aim of the present work is the study of the bacteriostatic/bactericidal effect of a silver-containing mesoporous bioactive glass obtained by evaporation-induced self-assembly and successive thermal stabilization. Samples of the manufactured mesophase were characterized by means of transmission electron microscopy and N₂ adsorption/desorption at 77 K, revealing structural and textural properties similar to SBA-15 mesoporous silica. Glass samples used for bioactivity experiments were put in contact with a standardized, commercially available cell culture medium instead of lab-produced simulated body fluid, and were then characterized by means of X-ray diffraction, field emission scanning electron microscopy and Fourier transform infrared spectroscopy. All these analyses confirmed the development of a hydroxyl carbonate apatite layer on glass particles. Moreover, the investigated mesostructure showed a very good antibacterial effect against S. aureus strain, with a strong evidence of bactericidal activity already registered at 0.5 mg/mL of glass concentration. A hypothesis about the mechanism by which Ag affects the bacterial viability, based on the intermediate formation of crystalline AgCl, was also taken into account. With respect to what already reported in the literature, these findings claim a deeper insight into the possible use of silver-containing bioactive glasses as multifunctional ceramic coatings for orthopedic devices.

  11. Fluoride release and bioactivity evaluation of glass ionomer: Forsterite nanocomposite

    Science.gov (United States)

    Sayyedan, Fatemeh Sadat; Fathi, Mohammadhossein; Edris, Hossein; Doostmohammadi, Ali; Mortazavi, Vajihesadat; Shirani, Farzaneh

    2013-01-01

    Background: The most important limitation of glass ionomer cements (GICs) is the weak mechanical properties. Our previous research showed that higher mechanical properties could be achieved by addition of forsterite (Mg2SiO4) nanoparticles to ceramic part of GIC. The objective of the present study was to fabricate a glass ionomer- Mg2SiO4 nanocomposite and to evaluate the effect of addition of Mg2SiO4 nanoparticles on bioactivity and fluoride release behavior of prepared nanocomposite. Materials and Methods: Forsterite nanoparticles were made by sol-gel process. X-ray diffraction (XRD) technique was used in order to phase structure characterization and determination of grain size of Mg2SiO4 nanopowder. Nanocomposite was fabricated via adding 3wt.% of Mg2SiO4 nanoparticles to ceramic part of commercial GIC (Fuji II GC). Fluoride ion release and bioactivity of nanocomposite were measured using the artificial saliva and simulated body fluid (SBF), respectively. Bioactivity of specimens was investigated by Fourier transitioned-infrared spectroscopy (FTIR), scanning electronmicroscopy (SEM), Inductively Coupled Plasma Optical Emission Spectroscopy (ICP-OES) and registration of the changes in pH of soaking solution at the soaking period. Statistical analysis was carried out by one Way analysis of variance and differences were considered significant if P Glass ionomer- Mg2SiO4 nanocomposite could be a good candidate for dentistry and orthopedic applications, through of desirable fluoride ion release and bioactivity. PMID:24130579

  12. Biological Impact of Bioactive Glasses and Their Dissolution Products.

    Science.gov (United States)

    Hoppe, Alexander; Boccaccini, Aldo R

    2015-01-01

    For many years, bioactive glasses (BGs) have been widely considered for bone tissue engineering applications due to their ability to bond to hard as well as soft tissue (a property termed bioactivity) and for their stimulating effects on bone formation. Ionic dissolution products released during the degradation of the BG matrix induce osteogenic gene expression leading to enhanced bone regeneration. Recently, adding bioactive metallic ions (e.g. boron, copper, cobalt, silver, zinc and strontium) to silicate (or phosphate and borate) glasses has emerged as a promising route for developing novel BG formulations with specific therapeutic functionalities, including antibacterial, angiogenic and osteogenic properties. The degradation behaviour of BGs can be tailored by adjusting the glass chemistry making these glass matrices potential carrier systems for controlled therapeutic ion release. This book chapter summarises the fundamental aspects of the effect of ionic dissolution products from BGs on osteogenesis and angiogenesis, whilst discussing novel BG compositions with controlled therapeutic ion release. © 2015 S. Karger AG, Basel.

  13. Fiber glass-bioactive glass composite for bone replacing and bone anchoring implants.

    Science.gov (United States)

    Vallittu, Pekka K; Närhi, Timo O; Hupa, Leena

    2015-04-01

    Although metal implants have successfully been used for decades, devices made out of metals do not meet all clinical requirements, for example, metal objects may interfere with some new medical imaging systems, while their stiffness also differs from natural bone and may cause stress-shielding and over-loading of bone. Peer-review articles and other scientific literature were reviewed for providing up-dated information how fiber-reinforced composites and bioactive glass can be utilized in implantology. There has been a lot of development in the field of composite material research, which has focused to a large extent on biodegradable composites. However, it has become evident that biostable composites may also have several clinical benefits. Fiber reinforced composites containing bioactive glasses are relatively new types of biomaterials in the field of implantology. Biostable glass fibers are responsible for the load-bearing capacity of the implant, while the dissolution of the bioactive glass particles supports bone bonding and provides antimicrobial properties for the implant. These kinds of combination materials have been used clinically in cranioplasty implants and they have been investigated also as oral and orthopedic implants. The present knowledge suggests that by combining glass fiber-reinforced composite with particles of bioactive glass can be used in cranial implants and that the combination of materials may have potential use also as other types of bone replacing and repairing implants. Copyright © 2015 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

  14. Fabrication and characterization of bioactive glass-ceramic using soda-lime-silica waste glass.

    Science.gov (United States)

    Abbasi, Mojtaba; Hashemi, Babak

    2014-04-01

    Soda-lime-silica waste glass was used to synthesize a bioactive glass-ceramic through solid-state reactions. In comparison with the conventional route, that is, the melt-quenching and subsequent heat treatment, the present work is an economical technique. Structural and thermal properties of the samples were examined by X-ray diffraction (XRD) and differential thermal analysis (DTA). The in vitro test was utilized to assess the bioactivity level of the samples by Hanks' solution as simulated body fluid (SBF). Bioactivity assessment by atomic absorption spectroscopy (AAS) and scanning electron microscopy (SEM) was revealed that the samples with smaller amount of crystalline phase had a higher level of bioactivity. Copyright © 2014 Elsevier B.V. All rights reserved.

  15. A bioactive coating with submicron-sized titania crystallites fabricated by induction heating of titanium after tensile deformations.

    Science.gov (United States)

    Li, Ning-Bo; Xu, Wen-Hua; Xiao, Gui-Yong; Zhao, Jun-Han; Lu, Yu-Peng

    2017-11-01

    Thermal oxidation technology was widely investigated as one of effective surface modification method for improving the bioactivity and biocompatibility of titanium and its alloys. In this work, the induction heat oxidization method, a fast, efficient, economical and environmental protective technology, was applied to prepare the submicron-morphological oxide coating with variable rutile TiO2 equiaxed crystallites on the surface of pure Ti substrates after cold-drawing with 10-20% deformations. The results showed the plastic-deformed Ti cylinders recrystallized during induction heating treatment (IHT) for 10-20s which resulted in evolution of microstructures as well as slight improvement of microhardness. The surface characteristics of TiO2 crystallites in oxidation layers were determined by the microstructural evolutions of Ti substrate in terms of the nucleation and growth of TiO2 crystallites. Specially, the oxidized surface with 50-75nm roughness and more uniform and finer equiaxed oxide grains remarkablely improved the apatite deposition after bioactive evaluation in 1.5 × SBF for 7 days. This work provided a potential method to create controlled bioactive oxide coatings with submicro-/nano-scaled TiO2 crystallites on titanium substrate in terms of the role of metallographic microstructure in the formation process of titanium oxides. Copyright © 2017 Elsevier Ltd. All rights reserved.

  16. In Vitro Bioactivity and Antimicrobial Tuning of Bioactive Glass Nanoparticles Added with Neem (Azadirachta indica) Leaf Powder

    Science.gov (United States)

    Prabhu, M.; Ruby Priscilla, S.; Kavitha, K.; Manivasakan, P.; Rajendran, V.; Kulandaivelu, P.

    2014-01-01

    Silica and phosphate based bioactive glass nanoparticles (58SiO2-33CaO-9P2O5) with doping of neem (Azadirachta indica) leaf powder and silver nanoparticles were prepared and characterised. Bioactive glass nanoparticles were produced using sol-gel technique. In vitro bioactivity of the prepared samples was investigated using simulated body fluid. X-ray diffraction (XRD) pattern of prepared glass particles reveals amorphous phase and spherical morphology with a particle size of less than 50 nm. When compared to neem doped glass, better bioactivity was attained in silver doped glass through formation of hydroxyapatite layer on the surface, which was confirmed through XRD, Fourier transform infrared (FTIR), and scanning electron microscopy (SEM) analysis. However, neem leaf powder doped bioactive glass nanoparticles show good antimicrobial activity against Staphylococcus aureus and Escherichia coli and less bioactivity compared with silver doped glass particles. In addition, the biocompatibility of the prepared nanocomposites reveals better results for neem doped and silver doped glasses at lower concentration. Therefore, neem doped bioactive glass may act as a potent antimicrobial agent for preventing microbial infection in tissue engineering applications. PMID:25276834

  17. Physicochemical properties and bioactivity of freeze-cast chitosan nanocomposite scaffolds reinforced with bioactive glass

    Energy Technology Data Exchange (ETDEWEB)

    Pourhaghgouy, Masoud, E-mail: m.pourhaghgouy@merc.ac.ir [Department of Nanotechnology & Advanced Materials, Materials & Energy Research Center, Karaj, P.O. Box: 13145-1659 (Iran, Islamic Republic of); Zamanian, Ali, E-mail: a-zamanian@merc.ac.ir [Department of Nanotechnology & Advanced Materials, Materials & Energy Research Center, Karaj, P.O. Box: 13145-1659 (Iran, Islamic Republic of); Shahrezaee, Mostafa, E-mail: moshahrezaee@yahoo.com [Department of Orthopedic Surgery, AJA University of Medical Sciences, Tehran (Iran, Islamic Republic of); Masouleh, Milad Pourbaghi, E-mail: miladpourbaghi@gmail.com [Department of Nanotechnology & Advanced Materials, Materials & Energy Research Center, Karaj, P.O. Box: 13145-1659 (Iran, Islamic Republic of)

    2016-01-01

    Chitosan based nanocomposite scaffolds were prepared by freeze casting method through blending constant chitosan concentration with different portions of synthesized bioactive glass nanoparticles (BGNPs). Transmission Electron Microscopy (TEM) image showed that the particles size of bioactive glass (64SiO{sub 2}.28CaO.8P{sub 2}O{sub 5}) prepared by sol–gel method was approximately less than 20 nm. Fourier Transform Infrared Spectroscopy (FT-IR) and X-ray Diffraction (XRD) analysis showed proper interfacial bonding between BGNPs and chitosan polymers. Scanning Electron Microscopy (SEM) images depicted a unidirectional structure with homogenous distribution of BGNPs among chitosan matrix associated with the absence of pure chitosan scaffold's wall pores after addition of only 10 wt.% BGNPs. As the BGNP content increased from 0 to 50 wt.%, the compressive strength and compressive module values increased from 0.034 to 0.419 MPa and 0.41 to 10.77 MPa, respectively. Biodegradation study showed that increase in BGNP content leads to growth of weight loss amount. The in vitro biomineralization studies confirmed the bioactive nature of all nanocomposites. Amount of 30 wt.% BGNPs represented the best concentration for absorption capacity and bioactivity behaviors. - Highlights: • Particle size of synthesized bioactive glass was approximately less than 20 nm. • Increase in BGNP content did not change the pore channels size. • Addition of 10 wt.% of BGNP led to absence of the pores located on chitosan walls. • Mechanical properties of chitosan scaffold significantly improved by addition of BGNPs. • Chi-BGNPs30 scaffold indicated acceptable absorption capacity and bioactivity behavior.

  18. Application of I-structure though-glass interconnect filled with submicron gold particles to a hermetic sealing device

    Science.gov (United States)

    Nomura, Kazuya; Okada, Akiko; Shoji, Shuichi; Ogashiwa, Toshinori; Mizuno, Jun

    2016-10-01

    We propose hermetic sealing of a glass-to-glass structure with an I-structure through-glass interconnect via (TGV) filled with submicron Au particles. The top and bottom bumps and the TGV were formed by a simple filling process with a bump-patterned dry film resist. The sealing devices consisting of two glass substrates were bonded via Au interlayers. Vacuum ultraviolet irradiation in the presence of oxygen gas (VUV/O3) pretreatment was used for low-temperature Au-Au bonding at 200 °C. The bonded samples showed He leakage rates of less than 1.3  ×  10-9 Pa m3 s-1. The cross-sectional scanning electron microscope images of the fabricated I-structure TGV showed perfect adhesion between the I-structure TGV and glass substrate. These results indicate that the proposed I-structure TGV is suitable for hermetic sealing devices.

  19. Composite bone cements loaded with a bioactive and ferrimagnetic glass-ceramic: Leaching, bioactivity and cytocompatibility

    Energy Technology Data Exchange (ETDEWEB)

    Verné, Enrica, E-mail: enrica.verne@polito.it [Institute of Materials Physics and Engineering, Applied Science and Technology Department, Politecnico di Torino, C. so Duca degli Abruzzi 24, 10129 Torino (Italy); Bruno, Matteo [Institute of Materials Physics and Engineering, Applied Science and Technology Department, Politecnico di Torino, C. so Duca degli Abruzzi 24, 10129 Torino (Italy); Miola, Marta [Institute of Materials Physics and Engineering, Applied Science and Technology Department, Politecnico di Torino, C. so Duca degli Abruzzi 24, 10129 Torino (Italy); Department of Health Sciences, Università del Piemonte Orientale “Amedeo Avogadro”, Via Solaroli 17, 28100 Novara (Italy); Maina, Giovanni; Bianco, Carlotta [Traumatology Orthopedics and Occupational Medicine Dept., Università di Torino, Via G. Zuretti 29, 10126 Torino (Italy); Cochis, Andrea [Department of Health Sciences, Università del Piemonte Orientale “Amedeo Avogadro”, Via Solaroli 17, 28100 Novara (Italy); Rimondini, Lia [Department of Health Sciences, Università del Piemonte Orientale “Amedeo Avogadro”, Via Solaroli 17, 28100 Novara (Italy); Consorzio Interuniversitario Nazionale per la Scienza e Tecnologia dei Materiali, Via G. Giusti, 9, 50121 Firenze (Italy)

    2015-08-01

    In this work, composite bone cements, based on a commercial polymethylmethacrylate matrix (Palamed®) loaded with ferrimagnetic bioactive glass-ceramic particles (SC45), were produced and characterized in vitro. The ferrimagnetic bioactive glass-ceramic belongs to the system SiO{sub 2}–Na{sub 2}O–CaO–P{sub 2}O{sub 5}–FeO–Fe{sub 2}O{sub 3} and contains magnetite (Fe{sub 3}O{sub 4}) crystals into a residual amorphous bioactive phase. Three different formulations (containing 10, 15 and 20 wt.% of glass-ceramic particles respectively) have been investigated. These materials are intended to be applied as bone fillers for the hyperthermic treatment of bone tumors. The morphological, compositional, calorimetric and mechanical properties of each formulation have been already discussed in a previous paper. The in vitro properties of the composite bone cements described in the present paper are related to iron ion leaching test (by graphite furnace atomic absorption spectrometer), bioactivity (i.e. the ability to stimulate the formation of a hydroxyapatite – HAp – layer on their surface after soaking in simulated body fluid SBF) and cytocompatibility toward human osteosarcoma cells (ATCC CRL-1427, Mg63). Morphological and chemical characterizations by scanning electron microscopy and energy dispersion spectrometry have been performed on the composite samples after each test. The iron release was negligible and all the tested samples showed the growth of HAp on their surface after 28 days of immersion in a simulated body fluid (SBF). Cells showed good viability, morphology, adhesion, density and the ability to develop bridge-like structures on all investigated samples. A synergistic effect between bioactivity and cell mineralization was also evidenced. - Highlights: • An in vitro biological characterization was carried out on ferromagnetic and bioactive composite cements. • No release of iron was revealed in the physiological solution. • Bioactivity tests

  20. Composite bone cements loaded with a bioactive and ferrimagnetic glass-ceramic: Leaching, bioactivity and cytocompatibility.

    Science.gov (United States)

    Verné, Enrica; Bruno, Matteo; Miola, Marta; Maina, Giovanni; Bianco, Carlotta; Cochis, Andrea; Rimondini, Lia

    2015-08-01

    In this work, composite bone cements, based on a commercial polymethylmethacrylate matrix (Palamed®) loaded with ferrimagnetic bioactive glass-ceramic particles (SC45), were produced and characterized in vitro. The ferrimagnetic bioactive glass-ceramic belongs to the system SiO2-Na2O-CaO-P2O5-FeO-Fe2O3 and contains magnetite (Fe3O4) crystals into a residual amorphous bioactive phase. Three different formulations (containing 10, 15 and 20 wt.% of glass-ceramic particles respectively) have been investigated. These materials are intended to be applied as bone fillers for the hyperthermic treatment of bone tumors. The morphological, compositional, calorimetric and mechanical properties of each formulation have been already discussed in a previous paper. The in vitro properties of the composite bone cements described in the present paper are related to iron ion leaching test (by graphite furnace atomic absorption spectrometer), bioactivity (i.e. the ability to stimulate the formation of a hydroxyapatite - HAp - layer on their surface after soaking in simulated body fluid SBF) and cytocompatibility toward human osteosarcoma cells (ATCC CRL-1427, Mg63). Morphological and chemical characterizations by scanning electron microscopy and energy dispersion spectrometry have been performed on the composite samples after each test. The iron release was negligible and all the tested samples showed the growth of HAp on their surface after 28 days of immersion in a simulated body fluid (SBF). Cells showed good viability, morphology, adhesion, density and the ability to develop bridge-like structures on all investigated samples. A synergistic effect between bioactivity and cell mineralization was also evidenced. Copyright © 2015 Elsevier B.V. All rights reserved.

  1. Radio-opaque nanosized bioactive glass for potential root canal application: evaluation of radiopacity, bioactivity and alkaline capacity.

    Science.gov (United States)

    Mohn, D; Zehnder, M; Imfeld, T; Stark, W J

    2010-03-01

    To produce novel nanosized bioactive glass particles with radio-opaque properties and high alkaline capacity and to evaluate their performance as a potential bioactive root canal dressing or filling material. Flame spray-derived bioactive glass particles in the nanometre range were produced including bismuth oxide as a radiopacifier. Calcium hydroxide, barium sulphate and bismuth oxide served as controls. Corresponding materials were compressed to obtain dense specimens with increased alkaline capacity. Radiopacity was evaluated, and in vitro bioactivity was monitored using Raman spectroscopy and scanning electron microscopy. Leaching of bismuth was controlled using atomic absorption spectroscopy. Bioactive glass particles with up to 50 wt% bismuth oxide revealed radiopacity with an equivalent of 4.94-mm aluminium. The introduction of bismuth into the bioactive glass altered the alkaline capacity and the in vitro bioactivity only for high bismuth oxide quantities. Bismuth oxide leaching out of the glass matrix was hardly detectable. Bioactive glass can be modified with bismuth oxide to become radio-opaque.

  2. Characterization,Mechanical, and In Vitro Bioactivity Properties of Hydroxyapatite/Bioactive Glass Composite

    Directory of Open Access Journals (Sweden)

    Israa Kahatan Sabree

    2016-12-01

    Full Text Available Bioactive ceramic materials can help bone reparation and regeneration by offering support to bone growth. Biological hydroxyapatite powder was prepared by burning animal bone followed by studying the mechanical properties of hydroxyapatite (HA/ (20wt.%, and 40wt.% of binary bioactive glass (70% SiO2- 30% CaO in order to evaluate the influence of composition on the compressive strength and hardness. HA-composite material exhibited increasing density, microhardness, and compressive strength with increasing amount of glass addition. X-ray diffraction after sintering at 1200°C showed no alter of HA to secondary phases while the hydroxyapatite/ bioactive glass composites contained a HA phase and different amounts of wollastonite phase, depending on the amount of bioglass added. In vitro tests, the samples were soaked in simulated body fluid (SBF for ten days in order to evaluate the change in compression strength, weight loss, and pH. The HA composite reinforced with 40 wt % bioglass showed highest compression strength, and lowest weight loss

  3. Bioactive glass for dentin remineralization: A systematic review.

    Science.gov (United States)

    Fernando, Delihta; Attik, Nina; Pradelle-Plasse, Nelly; Jackson, Phil; Grosgogeat, Brigitte; Colon, Pierre

    2017-07-01

    Strategies to achieve dentin remineralization is at present an important target of restorative dentistry. Remineralization of dentin by a bioactive material is complete only when the tissue regains its functionality. This is achieved when there is adequate apatite formation which most importantly translates into improved mechanical properties of dentin as a result of intrafibrillar mineralization. Bioactive glass (BAG) is a well-known implant material for bone regeneration and is proven to have excellent ability of apatite formation. Hence, recent studies have proposed BAGs as one of the most desired materials for remineralization of dentin. Therefore the aim of this systematic review was to scope the evidence of bioactive glass to remineralize dentin. The following research question was formulated: "Is there strong evidence for bioactive glass to remineralize dentin?" Three databases (Web of science, PubMed and Science direct) were scanned independently following PRISMA guidelines. Inclusion and exclusion criteria were set to identify relevant articles based on title and abstract screening. Finally, potentially relevant articles were downloaded and the full text was scrutinized to select the articles included in this review. The first phase of search returned 303 articles. A total of 19 papers with full text were scrutinized for inclusion, of which 3 papers were chosen for the final synthesis. All three studies confirm that BAG treatment leads to enhanced apatite formation in dentin. Only 1 of the 3 studies has reported the mechanical properties of dentin after BAG treatment and it revealed that the Young's modulus and flexural bend strength of BAG treated dentin were much lower than natural dentin even though they had similar apatite content. This review highlights the importance of assessing the mechanical properties of dentin alongside to the newly formed apatite content in order to prove BAGs efficiency to remineralize this tissue. Though studies have

  4. The impact of gallium content on degradation, bioactivity, and antibacterial potency of zinc borate bioactive glass.

    Science.gov (United States)

    Rahimnejad Yazdi, Alireza; Torkan, Lawrence; Stone, Wendy; Towler, Mark R

    2017-02-02

    Zinc borate glasses with increasing gallium content (0, 2.5, 5, 10, and 15 Wt % Ga) were synthesized and their degradation, bioactivity in simulated body fluid (SBF), and antibacterial properties were investigated. ICP measurements showed that increased gallium content in the glass resulted in increased gallium ion release and decreased release of other ions. Degradability declined with the addition of gallium, indicating the formation of more symmetric BO3 units with three bridging oxygens and asymmetric BO3 units with two bridging oxygens in the glass network as the gallium content in the series increased. The formation of amorphous CaP on the glass surface after 24 h of incubation in SBF was confirmed by SEM, XRD, and FTIR analyses. Finally, antibacterial evaluation of the glasses using the agar disc-diffusion method demonstrated that the addition of gallium increased the antibacterial potency of the glasses against P. aeruginosa (Gram-negative) while decreasing it against S. epidermidis (Gram-positive); considering the ion release trends, this indicates that the gallium ion is responsible for the glasses' antibacterial behavior against P. aeruginosa while the zinc ion controls the antibacterial activity against S. epidermidis. The statistical significance of the observed trends in the measurements were confirmed by applying the Kruskal-Wallis H Test. © 2017 Wiley Periodicals, Inc. J Biomed Mater Res Part B: Appl Biomater, 2017. © 2017 Wiley Periodicals, Inc.

  5. Enhanced bioactivity of glass ionomer cement by incorporating calcium silicates.

    Science.gov (United States)

    Chen, Song; Cai, Yixiao; Engqvist, Håkan; Xia, Wei

    2016-01-01

    Glass ionomer cements (GIC) are known as a non-bioactive dental cement. During setting the GIC have an acidic pH, driven by the acrylic acid component. It is a challenge to make GIC alkaline without disturbing its mechanical properties. One strategy was to add slowly reacting systems with an alkaline pH. The aim of the present study is to investigate the possibility of forming a bioactive dental material based on the combination of glass ionomer cement and calcium silicates. Two types of GIC were used as control. Wollastonite (CS also denoted β-CaSiO3) or Mineral Trioxide Aggregate (MTA) was incorporated into the 2 types of GIC. The material formulations' setting time, compressive strength, pH and bioactivity were compared between modified GIC and GIC control. Apatite crystals were found on the surfaces of the modified cements but not on the control GIC. The compressive strength of the cement remained with the addition of 20% calcium silicate or 20% MTA after one day immersion. In addition, the compressive strength of GIC modified with 20% MTA had been increased during the 14 d immersion (p < 0 .05).

  6. Enhanced bioactivity of glass ionomer cement by incorporating calcium silicates

    Science.gov (United States)

    Chen, Song; Cai, Yixiao; Engqvist, Håkan; Xia, Wei

    2016-01-01

    Abstract Glass ionomer cements (GIC) are known as a non-bioactive dental cement. During setting the GIC have an acidic pH, driven by the acrylic acid component. It is a challenge to make GIC alkaline without disturbing its mechanical properties. One strategy was to add slowly reacting systems with an alkaline pH. The aim of the present study is to investigate the possibility of forming a bioactive dental material based on the combination of glass ionomer cement and calcium silicates. Two types of GIC were used as control. Wollastonite (CS also denoted β-CaSiO3) or Mineral Trioxide Aggregate (MTA) was incorporated into the 2 types of GIC. The material formulations’ setting time, compressive strength, pH and bioactivity were compared between modified GIC and GIC control. Apatite crystals were found on the surfaces of the modified cements but not on the control GIC. The compressive strength of the cement remained with the addition of 20% calcium silicate or 20% MTA after one day immersion. In addition, the compressive strength of GIC modified with 20% MTA had been increased during the 14 d immersion (p < 0 .05). PMID:26787304

  7. Antibacterial polylactic acid/chitosan nanofibers decorated with bioactive glass

    Energy Technology Data Exchange (ETDEWEB)

    Goh, Yi-fan; Akram, Muhammad; Alshemary, Ammarz [Department of Chemistry, Faculty of Science, Universiti Teknologi Malaysia, 81310 Johor Bahru, Johor (Malaysia); Hussain, Rafaqat, E-mail: rafaqat@comsats.edu.pk [Department of Physics, COMSATS Institute of Information Technology, Islamabad (Pakistan)

    2016-11-30

    Highlights: • PLA/Chitosan nanofibers were coated with functional bioglass. • Polymer/ceramic composite fibers exhibited good in-vitro bioactivity. • Nanofibers coated with Ag doped bioglass exhibited good antibacterial activity. - Abstract: In this study, we have presented the structural and in vitro characterization of electrospun polylactic acid (PLA)/Chitosan nanofibers coated with cerium, copper or silver doped bioactive glasses (CeBG/CuBG/AgBG). Bead-free, smooth surfaced nanofibers were successfully prepared by using electrospinning technique. The nanocomposite fibers were obtained using a facile dip-coating method, their antibacterial activities against E. coliE. coli (ATCC 25922 strains) were measured by the disk diffusion method after 24 h of incubation at 37 °C. CeBG and CuBG decorated PLA/Chitosan nanofibers did not develop an inhibition zone against the bacteria. On the other hand, nanofibers coated with AgBG developed an inhibition zone against the bacteria. The as-prepared nanocomposite fibers were immersed in SBF for 1, 3 and 7 days in Simulated Body Fluid (SBF) for evaluation of in vitro bioactivity. All samples induced the formation of crystallites with roughly ruffled morphology and the pores of fibers were covered with the extensive growth of crystallites. Energy Dispersive X-ray (EDX) composition analysis showed that the crystallites possessed Ca/P ratio close to 1.67, confirming the good in-vitro bioactivity of the fibers.

  8. Bioactive glass thin films synthesized by advanced pulsed laser techniques

    Science.gov (United States)

    Mihailescu, N.; Stan, George E.; Ristoscu, C.; Sopronyi, M.; Mihailescu, Ion N.

    2016-10-01

    Bioactive materials play an increasingly important role in the biomaterials industry, and are extensively used in a range of applications, including biodegradable metallic implants. We report on Bioactive Glasses (BG) films deposition by pulsed laser techniques onto biodegradable substrates. The BG coatings were obtained using a KrF* excimer laser source (λ= 248 nm, τFWHM ≤ 25 ns).Their thickness has been determined by Profilometry measurements, whilst their morphology has been analysed by Scanning Electron Microscopy (SEM). The obtained coatings fairly preserved the targets composition and structure, as revealed by Energy Dispersive X-Ray Spectroscopy, Grazing Incidence X-Ray Diffraction, and Fourier Transform Infra-Red Spectroscopy analyses.

  9. In vitro characterisation of zirconia coated by bioactive glass.

    Science.gov (United States)

    Bosetti, M; Vernè, E; Ferraris, M; Ravaglioli, A; Cannas, M

    2001-05-01

    An in vitro evaluation of a biomedical device, which combines the mechanical properties of zirconia substrates with the bioactivity of two different glass layers (AP40 and RKKP), was performed. In this work, data on different kinds of analysis were reported both on as-sintered zirconia samples and on RKKP- and AP40-coated zirconia substrates. Structure, composition and morphology of the apatite layer growth on the coated samples after 30 days of soaking in an acellular simulated body fluid, serum protein adsorption, fibroblasts and human osteoblast-like cells adhesion, growth, morphology and biochemical aspects were studied. Results of soaking test in SBF, revealed the growth of an apatite layer on the surface of the glass-coated samples. Proteins adsorbed to the materials were analysed by sodium dodecyl sulphate-polyacrylamide gel electrophoresis and results evidenced that the two glass-coated materials bound a higher amount of total protein than did the zirconia substrate. Fibroblasts and osteoblast-like cells cultured on RKKP- and AP40-coated zirconia showed a higher proliferation rate, leading to confluent cultures with higher cell density and a generally better expression of osteoblast alkaline phosphatase activity in comparison with zirconia substrate. In conclusion, our results indicate that the surface chemical characteristics of the two glass coatings AP40 and RKKP, with no great differences between them, substantially enhance zirconia integration with bone cells at least in vitro. This effect may be of significance in the stability of glass-coated zirconia orthopaedic and dental implants.

  10. Fluoride release and bioactivity evaluation of glass ionomer: Forsterite nanocomposite

    Directory of Open Access Journals (Sweden)

    Fatemeh Sadat Sayyedan

    2013-01-01

    Full Text Available Background: The most important limitation of glass ionomer cements (GICs is the weak mechanical properties. Our previous research showed that higher mechanical properties could be achieved by addition of forsterite (Mg 2 SiO 4 nanoparticles to ceramic part of GIC. The objective of the present study was to fabricate a glass ionomer- Mg 2 SiO 4 nanocomposite and to evaluate the effect of addition of Mg 2 SiO 4 nanoparticles on bioactivity and fluoride release behavior of prepared nanocomposite. Materials and Methods: Forsterite nanoparticles were made by sol-gel process. X-ray diffraction (XRD technique was used in order to phase structure characterization and determination of grain size of Mg 2 SiO 4 nanopowder. Nanocomposite was fabricated via adding 3wt.% of Mg 2 SiO 4 nanoparticles to ceramic part of commercial GIC (Fuji II GC. Fluoride ion release and bioactivity of nanocomposite were measured using the artificial saliva and simulated body fluid (SBF, respectively. Bioactivity of specimens was investigated by Fourier transitioned-infrared spectroscopy (FTIR, scanning electronmicroscopy (SEM, Inductively Coupled Plasma Optical Emission Spectroscopy (ICP-OES and registration of the changes in pH of soaking solution at the soaking period. Statistical analysis was carried out by one Way analysis of variance and differences were considered significant if P < 0.05. Results: The results of XRD analysis confirmed that nanocrystalline and pure Mg 2 SiO 4 powder was obtained. Fluoride ion release evaluation showed that the values of released fluoride ions from nanocomposite are somewhat less than Fuji II GC. SEM images, pH changes of the SBF and results of the ICP-OES and FTIR tests confirmed the bioactivity of the nanocomposite. Statistical analysis showed that the differences between the results of all groups were significant (P < 0.05. Conclusion: Glass ionomer- Mg 2 SiO 4 nanocomposite could be a good candidate for dentistry and orthopedic

  11. Electrophoretic deposition of mesoporous bioactive glass on glass-ceramic foam scaffolds for bone tissue engineering.

    Science.gov (United States)

    Fiorilli, Sonia; Baino, Francesco; Cauda, Valentina; Crepaldi, Marco; Vitale-Brovarone, Chiara; Demarchi, Danilo; Onida, Barbara

    2015-01-01

    In this work, the coating of 3-D foam-like glass-ceramic scaffolds with a bioactive mesoporous glass (MBG) was investigated. The starting scaffolds, based on a non-commercial silicate glass, were fabricated by the polymer sponge replica technique followed by sintering; then, electrophoretic deposition (EPD) was applied to deposit a MBG layer on the scaffold struts. EPD was also compared with other techniques (dipping and direct in situ gelation) and it was shown to lead to the most promising results. The scaffold pore structure was maintained after the MBG coating by EPD, as assessed by SEM and micro-CT. In vitro bioactivity of the scaffolds was assessed by immersion in simulated body fluid and subsequent evaluation of hydroxyapatite (HA) formation. The deposition of a MBG coating can be a smart strategy to impart bioactive properties to the scaffold, allowing the formation of nano-structured HA agglomerates within 48 h from immersion, which does not occur on uncoated scaffold surfaces. The mechanical properties of the scaffold do not vary after the EPD (compressive strength ~19 MPa, fracture energy ~1.2 × 10(6) J m(-3)) and suggest the suitability of the prepared highly bioactive constructs as bone tissue engineering implants for load-bearing applications.

  12. Plasma spraying of bioactive glass-ceramics containing bovine bone

    Directory of Open Access Journals (Sweden)

    Annamária Dobrádi

    2017-06-01

    Full Text Available Natural bone derived glass-ceramics are promising biomaterials for implants. However, due to their price and weak mechanical properties they are preferably applied as coatings on load bearing implants. This paper describes result obtained by plasma spraying of bioactive glass-ceramics containing natural bone onto selected implant materials, such as stainless steel, alumina, and titanium alloy. Adhesion of plasma sprayed coating was tested by computed X-ray tomography and SEM of cross sections. The results showed defect free interface between the coating and substrate, without cracks or gaps. Dissolution rate of the coating in simulated body fluid (SBF was readily controlled by the bone additives (phase composition, as well as microstructure. The SBF treatment of the plasma sprayed coating did not influence the boundary between the coating and substrate.

  13. Tailoring properties of porous Poly (vinylidene fluoride) scaffold through nano-sized 58s bioactive glass.

    Science.gov (United States)

    Shuai, Cijun; Huang, Wei; Feng, Pei; Gao, Chengde; Shuai, Xiong; Xiao, Tao; Deng, Youwen; Peng, Shuping; Wu, Ping

    2016-01-01

    The biological properties of porous poly (vinylidene fluoride) (PVDF) scaffolds fabricated by selective laser sintering were tailored through nano-sized 58s bioactive glass. The results showed that 58s bioactive glass distributed evenly in the PVDF matrix. There were some exposed particles on the surface which provided attachment sites for biological response. It was confirmed that the scaffolds had highly bioactivity by the formation of bone-like apatite in simulated body fluid. And the bone-like apatite became dense with the increase in 58s bioactive glass and culture time. Moreover, the scaffolds were suitable for cell adhesion and proliferation compared with the PVDF scaffolds without 58s bioactive glass. The research showed that the PVDF/58s bioactive glass scaffolds had latent application in bone tissue engineering.

  14. LASER-INDUCED BIOACTIVITY IN DENTAL PORCELAIN MODIFIED BY BIOACTIVE GLASS

    Directory of Open Access Journals (Sweden)

    ANASTASIA BEKETOVA

    2012-12-01

    Full Text Available The aim of this study was to investigate the impact of laser-liquid-solid interaction method in the bioactivity of dental porcelain modified by bioactive glass. Forty sol-gel derived specimens were immersed in Dulbecco's Modified Eagle's Medium, 31 and 9 specimens of which were treated with Er:YAG and Nd:YAG laser respectively. Untreated specimens served as controls. Incubation of specimens followed. Bioactivity was evaluated, using Fourier Transform Infrared spectroscopy (FTIR, Scanning Electron Microscopy (SEM/Energy Dispersive Spectroscopy (EDS and Transmission Electron Microscopy (TEM. FTIR detected peaks associated with hydroxyapatite on 1 Nd:YAG- and 4 Er:YAG-treated specimens. SEM analysis revealed that Er:YAG-treated specimens were covered by granular hydroxyapatite layer, while Nd:YAG treated specimen presented growth of flake-like hydroxyapatite. TEM confirmed the results. The untreated controls presented delayed bioactivity. In conclusion, Nd:YAG and Er:YAG laser treatment of the material, under certain fluencies, accelerates hydroxyapatite formation. Nd:YAG laser treatment of specific parameters causes the precipitation of flake-like hydroxyapatite in nano-scale.

  15. Antibacterial and antifungal potential of Ga-bioactive glass and Ga-bioactive glass/polymeric hydrogel composites.

    Science.gov (United States)

    Keenan, T J; Placek, L M; Hall, M M; Wren, A W

    2017-07-01

    A bioactive glass series (0.42SiO2 -0.10Na2 O-0.08CaO-(0.40 - x)ZnO-(x)Ga2 O3 ) was synthesized, and it is efficacy against the Gram (-ve) bacteria Escherichia coli (E. coli), the Gram (+ve) bacteria Staphylococcus aureus (S. aureus), and the fungus Candida albicans (C. albicans), were characterized through liquid broth analysis. The glass series was also seeded in CMC-Dex hydrogels at three different loadings (0.05, 0.10, and 0.25 m(2) ), and the antibacterial and antifungal efficacies of the resulting composites were characterized using both liquid broth and agar diffusion analysis. Liquid broth analysis was conducted using liquid extracts, which for glass samples were obtained after incubation for up to 30 days in both ultrapure water and phosphate buffered saline (PBS), while glass-hydrogel extracts were obtained solely in PBS. Glass extracts (water) decreased C. albicans viability, while those obtained in PBS decreased the viability of both E. coli and C. albicans. Glass-hydrogel extracts exhibited slight inhibition of E. coli and C. albicans. However, none of the liquid extracts decreased S. aureus viability. Glass-hydrogel composites produced inhibition zones in all three microbial cultures, with the greatest efficacy against C. albicans. The results of this study suggest these materials have potential as bone void-filling materials which display antifungal, and possibly, antibacterial properties. © 2016 Wiley Periodicals, Inc. J Biomed Mater Res Part B: Appl Biomater, 105B: 1102-1113, 2017. © 2016 Wiley Periodicals, Inc.

  16. Antibacterial polylactic acid/chitosan nanofibers decorated with bioactive glass

    Science.gov (United States)

    Goh, Yi-fan; Akram, Muhammad; Alshemary, Ammarz; Hussain, Rafaqat

    2016-11-01

    In this study, we have presented the structural and in vitro characterization of electrospun polylactic acid (PLA)/Chitosan nanofibers coated with cerium, copper or silver doped bioactive glasses (CeBG/CuBG/AgBG). Bead-free, smooth surfaced nanofibers were successfully prepared by using electrospinning technique. The nanocomposite fibers were obtained using a facile dip-coating method, their antibacterial activities against E. coliE. coli (ATCC 25922 strains) were measured by the disk diffusion method after 24 h of incubation at 37 °C. CeBG and CuBG decorated PLA/Chitosan nanofibers did not develop an inhibition zone against the bacteria. On the other hand, nanofibers coated with AgBG developed an inhibition zone against the bacteria. The as-prepared nanocomposite fibers were immersed in SBF for 1, 3 and 7 days in Simulated Body Fluid (SBF) for evaluation of in vitro bioactivity. All samples induced the formation of crystallites with roughly ruffled morphology and the pores of fibers were covered with the extensive growth of crystallites. Energy Dispersive X-ray (EDX) composition analysis showed that the crystallites possessed Ca/P ratio close to 1.67, confirming the good in-vitro bioactivity of the fibers.

  17. The osteogenic response of mesenchymal stromal cells to strontium‐substituted bioactive glasses

    Science.gov (United States)

    Santocildes‐Romero, Martin E.; Crawford, Aileen; Goodchild, Rebecca L.; Reaney, Ian M.; Miller, Cheryl A.

    2015-01-01

    Abstract Bioactive glasses are known to stimulate bone healing, and the incorporation of strontium has the potential to increase their potency. In this study, calcium oxide in the 45S5 bioactive glass composition was partially (50%, Sr50) or fully (100%, Sr100) substituted with strontium oxide on a molar basis. The effects of the substitution on bioactive glass properties were studied, including density, solubility, and in vitro cytotoxicity. Stimulation of osteogenic differentiation was investigated using mesenchymal stromal cells obtained from rat bone marrow. Strontium substitution resulted in altered physical properties including increased solubility. Statistically significant reductions in cell viability were observed with the addition of bioactive glass powders to culture medium. Specifically, addition of ≥ 13.3 mg/ml of 45S5 bioactive glass or Sr50, or ≥ 6.7 mg/ml of Sr100, resulted in significant inhibition. Real‐time PCR analyses detected the upregulation of genes associated with osteoblastic differentiation in the presence of all bioactive glass compositions. Some genes, including Alpl and Bglap, were further stimulated in the presence of Sr50 and Sr100. It was concluded that strontium‐substituted bioactive glasses promoted osteogenesis in a differentiating bone cell culture model and, therefore, have considerable potential for use as improved bioactive glasses for bone tissue regeneration. © 2015 The Authors. Journal of Tissue Engineering and Regenerative Medicine Published by John Wiley & Sons Ltd. PMID:25757935

  18. The osteogenic response of mesenchymal stromal cells to strontium-substituted bioactive glasses.

    Science.gov (United States)

    Santocildes-Romero, Martin E; Crawford, Aileen; Hatton, Paul V; Goodchild, Rebecca L; Reaney, Ian M; Miller, Cheryl A

    2015-05-01

    Bioactive glasses are known to stimulate bone healing, and the incorporation of strontium has the potential to increase their potency. In this study, calcium oxide in the 45S5 bioactive glass composition was partially (50%, Sr50) or fully (100%, Sr100) substituted with strontium oxide on a molar basis. The effects of the substitution on bioactive glass properties were studied, including density, solubility, and in vitro cytotoxicity. Stimulation of osteogenic differentiation was investigated using mesenchymal stromal cells obtained from rat bone marrow. Strontium substitution resulted in altered physical properties including increased solubility. Statistically significant reductions in cell viability were observed with the addition of bioactive glass powders to culture medium. Specifically, addition of ≥ 13.3 mg/ml of 45S5 bioactive glass or Sr50, or ≥ 6.7 mg/ml of Sr100, resulted in significant inhibition. Real-time PCR analyses detected the upregulation of genes associated with osteoblastic differentiation in the presence of all bioactive glass compositions. Some genes, including Alpl and Bglap, were further stimulated in the presence of Sr50 and Sr100. It was concluded that strontium-substituted bioactive glasses promoted osteogenesis in a differentiating bone cell culture model and, therefore, have considerable potential for use as improved bioactive glasses for bone tissue regeneration. © 2015 The Authors. Journal of Tissue Engineering and Regenerative Medicine Published by John Wiley & Sons Ltd.

  19. Bioactive Glass Nanoparticles: From Synthesis to Materials Design for Biomedical Applications.

    Science.gov (United States)

    Vichery, Charlotte; Nedelec, Jean-Marie

    2016-04-14

    Thanks to their high biocompatibility and bioactivity, bioactive glasses are very promising materials for soft and hard tissue repair and engineering. Because bioactivity and specific surface area intrinsically linked, the last decade has seen a focus on the development of highly porous and/or nano-sized materials. This review emphasizes the synthesis of bioactive glass nanoparticles and materials design strategies. The first part comprehensively covers mainly soft chemistry processes, which aim to obtain dispersible and monodispersed nanoparticles. The second part discusses the use of bioactive glass nanoparticles for medical applications, highlighting the design of materials. Mesoporous nanoparticles for drug delivery, injectable systems and scaffolds consisting of bioactive glass nanoparticles dispersed in a polymer, implant coatings and particle dispersions will be presented.

  20. Flexural strength and morphological characteristics of resin-modified glass-ionomer containing bioactive glass.

    Science.gov (United States)

    Mousavinasab, Sayed Mostafa; Khoroushi, Maryam; Keshani, Fateme; Hashemi, Shirin

    2011-01-01

    Recent advances in dental materials have led to the production of smart materials. Recently, addition of bioactive materials to glass-ionomer cements has resulted in new capabilities beyond the beneficial effects of fluoride release. This in vitro study compared the flexural strengths (FS) of a resin-modified glass-ionomer containing bioactive glass (RMGIBAG) with that of a commonly used resin-modified glass-ionomer (RMGI). A total of forty RMGI and RMGI-BAG bars (20 × 4 × 4 mm) were prepared in stainless steel molds. Each of the RMGI and RMGI-BAG bars was set for FS test. FS values of the specimens were measured using three-point bending test at a crosshead speed of 0.5 mm/min. The surface changes and the amounts of elements on the materials' surfaces were also evaluated by SEM/EDS analyses. Data were analyzed using SPSS 11.5 and t-test (α = 0.05). The means ± SD in the study groups were 61.46 ± 22.52 and 39.90 ± 9.11 MPa respectively. There were significant differences between FS of the two study groups (p = 0.003). While adding 20 wt% of BAG to the RMGI powder evaluated in this study decreases FS of the material significantly, the mean value of FS is in the acceptable range of the reported FS values for conventional GIs and RMGIs that are commercially available for clinical use. While flexural strength of RMGI decreases subsequent to addition of bioactive glass, it is still clinically acceptable considering the flexural strength values reported for clinically used GIs and RMGIs. Further studies are recommended.

  1. Synchrotron X-ray Absorption and In Vitro Bioactivity of Magnetic Macro/Mesoporous Bioactive Glasses

    Directory of Open Access Journals (Sweden)

    Thanida Charoensuk

    2015-12-01

    Full Text Available Iron oxides in macro/mesoporous bioactive glasses were characterized by synchrotron X-ray absorption near edge structure (XANES spectroscopy. This magnetic phase was introduced by adding Fe(NO33 9H2O during the sol-gel synthesis. The obtained bioactive glass scaffolds exhibited superparamagnetism, in which the magnetization was increased with the increase in the Fe molar ratio from 10 to 20%. The linear combination fits of the XANES spectra indicated that the increase in the Fe molar ratio to 20% enhanced the γ-Fe2O3 formation at the expense of the α- Fe2O3 phase. This variation also promoted the formation of fine-grained bone-like apatites on the surface of the scaffolds in the in vitro test. The apatite growth between three and seven days was confirmed by the changing elemental compositions. However, the highest magnetic proportion led to the distortion of the skeleton walls and the collapse of the porous networks.

  2. Development of nano-macroporous soda-lime phosphofluorosilicate bioactive glass and glass-ceramics.

    Science.gov (United States)

    Moawad, H M M; Jain, H

    2009-07-01

    We have extended the usefulness of bioactive glass-ceramics for the repair and reconstruction of hard tissues by introducing F ions that are known to be beneficial, especially in dentistry. Nano-macro multimodal porosity in soda-lime phosphofluorosilicate bulk samples was introduced by the recently developed melt-quench-heat-etch method. The choice of starting glass composition is based on 48SiO2-2.7P2O5-xCaF2-yCaO-zNa2O where x = 0, 1, 4, 8, 10, 12, and (y + z) = 49.3-x (mol%). The effect of thermal and chemical treatment on the microstructure of samples is characterized by SEM, XRD and EDX. We find the formation of many crystalline phases, but mainly sodium calcium silicate, calcium phosphate, fluorapatite and calcium silicate. The bioactivity of soda-lime phosphofluorosilicate glass-ceramics is assessed by monitoring the formation of hydroxyl apatite (HA) layer: fluorapatite phase accelerates the rate of HA layer formation; the initial composition and multi-modal porosity are other key parameters that impact the formation of HA. The present porous glass-ceramics should be superior candidates for use in dental bone regeneration.

  3. Mesoporous Bioactive Glass Functionalized 3D Ti-6Al-4V Scaffolds with Improved Surface Bioactivity

    Directory of Open Access Journals (Sweden)

    Xiaotong Ye

    2017-10-01

    Full Text Available Porous Ti-6Al-4V scaffolds fabricated by means of selective laser melting (SLM, having controllable geometrical features and preferable mechanical properties, have been developed as a class of biomaterials that hold promising potential for bone repair. However, the inherent bio-inertness of the Ti-6Al-4V alloy as the matrix of the scaffolds results in a lack in the ability to stimulate bone ingrowth and regeneration. The aim of the present study was to develop a bioactive coating on the struts of SLM Ti-6Al-4V scaffolds in order to add the desired surface osteogenesis ability. Mesoporous bioactive glasses (MBGs coating was applied on the strut surfaces of the SLM Ti-6Al-4V scaffolds through spin coating, followed by a heat treatment. It was found that the coating could maintain the characteristic mesoporous structure and chemical composition of MBG, and establish good interfacial adhesion to the Ti-6Al-4V substrate. The compressive strength and pore interconnectivity of the scaffolds were not affected by the coating. Moreover, the results obtained from in vitro cell culture experiments demonstrated that the attachment, proliferation, and differentiation of human bone marrow stromal cells (hBMSCs on the MBG-coated Ti-6Al-4V scaffolds were improved as compared with those on the conventional bioactive glass (BG-coated Ti-6Al-4V scaffolds and bare-metal Ti-6Al-4V scaffolds. Our results demonstrated that the MBG coating by using the spinning coating method could be an effective approach to achieving enhanced surface biofunctionalization for SLM Ti-6Al-4V scaffolds.

  4. Controlling ion release from bioactive glass foam scaffolds with antibacterial properties.

    Science.gov (United States)

    Jones, Julian R; Ehrenfried, Lisa M; Saravanapavan, Priya; Hench, Larry L

    2006-11-01

    Bioactive glass scaffolds have been produced, which meet many of the criteria for an ideal scaffold for bone tissue engineering applications, by foaming sol-gel derived bioactive glasses. The scaffolds have a hierarchical pore structure that is very similar to that of cancellous bone. The degradation products of bioactive glasses have been found to stimulate the genes in osteoblasts. This effect has been found to be dose dependent. The addition of silver ions to bioactive glasses has also been investigated to produce glasses with bactericidal properties. This paper discusses how changes in the hierarchical pore structure affect the dissolution of the glass and therefore its bioactivity and rate of ion delivery and demonstrates that silver containing bioactive glass foam scaffolds can be synthesised. It was found that the rate of release of Si and Ca ions was more rapid for pore structures with a larger modal pore diameter, although the effect of tailoring the textural porosity on the rate of ion release was more pronounced. Bioactive glass scaffolds, containing 2 mol% silver, released silver ions at a rate that was similar to that which has previously been found to be bactericidal but not high enough to be cytotoxic to bone cells.

  5. Characteristics of defect formation in aluminium oxide reinforced bioactive glass

    Energy Technology Data Exchange (ETDEWEB)

    Szarska, S. [Institute of Physics, Wroclaw University of Technology, 50-370 Wroclaw, Wyb.Wyspianskiego 27 (Poland)], E-mail: stanislawa.szarska@pwr.wroc.pl; Jungner, H. [Dating Laboratory, University of Helsinki, P.O. Box 64, FIN-00014 Helsinki (Finland); Staniewicz-Brudnik, B. [Poland Institute of Advanced Manufacturing Technology, Cracow, Wroclawska Street 37a (Poland); Wiatr, M. [Institute of Physics, Wroclaw University of Technology, 50-370 Wroclaw, Wyb.Wyspianskiego 27 (Poland)

    2007-04-15

    Composite materials containing a bioactive phase (sol-gel-derived bioglass) and a mechanical strength phase (bubble alumina or sintered corundum) are promising materials for repair of living tissues. The microstructure of the biocomposite material, its mechanical properties and the processing routes used are all very strongly interrelated. SEM was used to investigate the phenomena occurring at the two phase interfaces. Porosity is one of the most common defects in this composite, which negatively affects strength. The systems were irradiated with beta radiation at different doses. Absorption and luminescence of these biocomposites were studied with the main attention paid to trap centres. The measurement results prove a high sensitivity of our experimental method to the effects of the surface glass modifications.

  6. Bioactive Glass Scaffolds for Dental Pulp and Dentin Tissue Engineering

    Science.gov (United States)

    Shawli, Hassan Talat

    Current and historical endodontic "root canal" treatments employ inert obturating materials inserted into the teeth's pulp chambers and root canals, often saving teeth but without adequate function. Furthermore, the occurrence of pulpal necrosis in the immature permanent tooth is considered to be a challenging situation, clinically, in treatment because the thin and often short roots increase the risk of fracture. The ideal treatment would be to promote continued root development. This work demonstrated that endodontically-shaped and durable scaffolds of slowly resorbable fibrous (HT) glass and faster-resorbing small-particle Bioglass can be sintered at 900 degrees C for such placement, and that cell growth of osteoblasts in these scaffolds shows good early results. Retained bioactivity in the sintered specimen was revealed by Multiple Attenuated Internal Reflection Infrared Spectroscopy.

  7. In vitro bioactivity and cytotoxicity of chemically treated glass fibers

    Directory of Open Access Journals (Sweden)

    Ângela Leão Andrade

    2004-12-01

    Full Text Available Samples of a commercial glass fiber FM® (Fiber Max were used to test the efficacy of a chemical sol-gel surface treatment to enhance their bioactivity. After treatment with tetraethoxysilane (TEOS, individual fiber samples were soaked into a simulated body fluid (SBF solution, from which they were removed at intervals of 5 and 10 days. Micrographs obtained by scanning electron microscopy (SEM analysis of samples chemically treated with TEOS revealed the formation of a hydroxyapatite (HA coating layer after 5 days into SBF solution. Fourier transform infrared spectroscopic (FTIR analyses confirmed that the coating layer has P-O vibration bands characteristic of HA. The in vitro cytotoxicity was evaluated using a direct contact test, minimum essential medium elution test (ISO 10993-5 and MTT assay. Fibers immersed in SBF and their extracts exhibited lower cytotoxicity than the controls not subjected to immersion, suggesting that SBF treatment improves the biocompatibility of the fiber.

  8. Through the looking glass; bioactive glass S53P4 (BonAlive®) in the treatment of chronic osteomyelitis.

    LENUS (Irish Health Repository)

    McAndrew, J

    2013-09-01

    In terms of eradication, osteomyelitis represents one of the most challenging infective conditions in medicine and surgery. In recent years, the use of bioactive glass in conjunction with antimicrobial therapy has emerged as a viable new treatment.

  9. A novel bioactive glass-ceramic for treating dentin hypersensitivity

    Directory of Open Access Journals (Sweden)

    Camila Tirapelli

    2010-12-01

    Full Text Available Dentin hypersensitivity (DH is a painful response to stimulus applied to the open dentinal tubules of a vital tooth. It's a common oral condition, however, without an ideal treatment available yet. This work evaluated in vitro the effect of micron-sized particles from a novel bioactive glass-ceramic (Biosilicate in occluding open dentinal tubules. A dentin disc model was employed to observe comparatively, using scanning electron microscopy (SEM, dentinal tubule occlusion by different products and deposition of hydroxyl carbonate apatite (HCA on dentin surface by Biosilicate, after a single application: G1 - Dentifrice with potassium nitrate and fluoride; G2 - Two-step calcium phosphate precipitation treatment; G3 - Water-free gel containing Biosilicate particles (1%; G4 - Biosilicate particles mixed with distilled water in a 1:10 ratio; all of them after 1, 12 and 24 hours of immersion in artificial saliva. Fourier transform infrared spectroscopy (FTIR was performed to detect HCA formation on dentin discs filled with Biosilicate after 2 minutes, 30 minutes and 12 hours of immersion in artificial saliva. SEM showed a layer of HCA formed on dentin surface after 24 hours by G4. G1, G2 and G3 promoted not total occlusion of open dentinal tubules after 24 hours. FTIR showed HCA precipitation on the dentin surface induced by Biosilicate after 30 minutes. The micron-sized particles from the bioactive glass-ceramic thus were able to induce HCA deposition in open dentinal tubules in vitro. This finding suggests that Biosilicate may provide a new option for treating DH.

  10. Chitosan/bioactive glass nanoparticles scaffolds with shape memory properties.

    Science.gov (United States)

    Correia, Cristina O; Leite, Álvaro J; Mano, João F

    2015-06-05

    We propose a combination of chitosan (CHT) with bioactive glass nanoparticles (BG-NPs) in order to produce CHT/BG-NPs scaffolds that combine the shape memory properties of chitosan and the biomineralization ability of BG-NPs for applications in bone regeneration. The addition of BG-NPs prepared by a sol-gel route to the CHT polymeric matrix improved the bioactivity of the nanocomposite scaffold, as seen by the precipitation of bone-like apatite layer upon immersion in simulated body fluid (SBF). Shape memory tests were carried out while the samples were immersed in varying compositions of water/ethanol mixtures. Dehydration with ethanol enables to fix a temporary shape of a deformed scaffold that recovers the initial geometry upon water uptake. The scaffolds present good shape memory properties characterized by a recovery ratio of 87.5% for CHT and 89.9% for CHT/BG-NPs and a fixity ratio of 97.2% for CHT and 98.2% for CHT/BG-NPs (for 30% compressive deformation). The applicability of such structures was demonstrated by a good geometrical accommodation of a previously compressed scaffold in a bone defect. The results indicate that the developed CHT/BG-NPs nanocomposite scaffolds have potential for being applied in bone tissue engineering. Copyright © 2015 Elsevier Ltd. All rights reserved.

  11. Fluorine environment in bioactive glasses: ab initio molecular dynamics simulations.

    Science.gov (United States)

    Christie, Jamieson K; Pedone, Alfonso; Menziani, Maria Cristina; Tilocca, Antonio

    2011-03-10

    Fluorinated bioactive glasses (FBGs) combine the antibacterial properties of fluorine with the biological activity of phosphosilicate glasses. Because their biomedical application depends on the release of fluorine, the detailed characterization of the fluorine environment in FBGs is the key to understand their properties. Car-Parrinello molecular dynamics (CPMD) simulations have been performed on a 45S5 Bioglass composition in which 10 mol % of the CaO has been replaced with CaF(2), and have allowed us to resolve some longstanding issues about the atomic structure of fluorinated bioglasses, with particular regard to the structural role of fluorine. F is coordinated almost entirely to the modifier ions Na and Ca, with a very small amount of residual Si-F bonds, whose fraction only becomes significant in the melt precursor. High temperature leads to Si-F bonds in both tetra- (SiO(3)F) and, less frequently, penta-coordinated (SiO(4)F and SiO(3)F(2)) complexes, showing that formation of these bonds through the expansion of the SiO(4) coordination shell is generally less favored. There is no evidence for preferential bonding of F to either modifier ion: almost all F atoms are coordinated to both calcium and sodium in a "mixed state", rather than exclusively to either, as had been conjectured. We discuss the consequences of these findings on the properties of fluorine-containing bioglasses. © 2011 American Chemical Society

  12. In-vitro apatite formation capacity of a bioactive glass - containing toothpaste.

    Science.gov (United States)

    Kanwal, Nasima; Brauer, Delia S; Earl, Jonathan; Wilson, Rory M; Karpukhina, Natalia; Hill, Robert G

    2017-10-31

    The in-vitro dissolution of bioactive glass-based toothpastes and their capacity to form apatite-like phases in buffer solutions have been investigated. The commercial toothpaste samples were tested on immersion in artificial saliva, Earle's salt solution and Tris buffer for duration from 10min to four days. The powder samples collected at the end of the immersion were studied using solid-state 31P and 19F nuclear magnetic resonance spectroscopy (NMR), X-ray powder diffraction and Fourier transform infrared (FTIR) spectroscopy. The fluoride concentration in the solution remained after the immersion was measured. In artificial saliva and in presence of sodium monofluorophosphate (MFP), the bioactive glass and bioactive glass-based toothpastes formed fluoridated apatite-like phases in under 10min. A small amount of apatite-like phase was detected by 31P NMR in the toothpaste with MFP but no bioactive glass. The toothpaste with bioactive glass but no fluoride formed an apatite-like phase as rapidly as the paste containing bioactive glass and fluoride. By contrast, apatite-like phase formation was much slower in Earle's salt solution than artificial saliva and slower than Tris buffer. The results of this lab-based study showed that the toothpaste with MFP and bioactive glass formed a fluoridated apatite in artificial saliva and in Tris buffer, as did the mixture of bioactive glass and MFP. The presence of fluoride in bioactive glass-containing toothpastes can potentially lead to the formation of a fluoridated apatite, which may result in improved clinical effectiveness and durability. However, this should be further tested intra-orally. Copyright © 2017 Elsevier Ltd. All rights reserved.

  13. Sol-gel synthesis and in vitro bioactivity of copper and zinc-doped silicate bioactive glasses and glass-ceramics.

    Science.gov (United States)

    Bejarano, Julian; Caviedes, Pablo; Palza, Humberto

    2015-03-11

    Metal doping of bioactive glasses based on ternary 60SiO2-36CaO-4P2O5 (58S) and quaternary 60SiO2-25CaO-11Na2O-4P2O5 (NaBG) mol% compositions synthesized using a sol-gel process was analyzed. In particular, the effect of incorporating 1, 5 and 10 mol% of CuO and ZnO (replacing equivalent quantities of CaO) on the texture, in vitro bioactivity, and cytocompatibility of these materials was evaluated. Our results showed that the addition of metal ions can modulate the textural property of the matrix and its crystal structure. Regarding the bioactivity, after soaking in simulated body fluid (SBF) undoped 58S and NaBG glasses developed an apatite surface layer that was reduced in the doped glasses depending on the type of metal and its concentration with Zn displaying the largest inhibitions. Both the ion release from samples and the ion adsorption from the medium depended on the type of matrix with 58S glasses showing the highest values. Pure NaBG glass was more cytocompatible to osteoblast-like cells (SaOS-2) than pure 58S glass as tested by 3-(4, 5-dimethylthiazol-2-yl)-2, 5-diphenyltetrazolium bromide (MTT) assay. The incorporation of metal ions decreased the cytocompatibility of the glasses depending on their concentration and on the glass matrix doped. Our results show that by changing the glass composition and by adding Cu or Zn, bioactive materials with different textures, bioactivity and cytocompatibility can be synthesized.

  14. Using machine learning for improving knowledge on antibacterial effect of bioactive glass.

    Science.gov (United States)

    Echezarreta-López, M M; Landin, M

    2013-09-10

    The aim of this work was to find relationships between critical bioactive glass characteristics and their antibacterial behaviour using an artificial intelligence tool. A large dataset including ingredients and process variables of the bioactive glasses production, bacterial characteristics and microbiological experimental conditions was generated from literature and analyzed by neurofuzzy logic technology. Our findings allow an explanation on the variability in antibacterial behaviour found by different authors and to obtain general conclusions about critical parameters of bioactive glasses to be considered in order to achieve activity against some of the most common skin and implant surgery pathogens. Copyright © 2013 Elsevier B.V. All rights reserved.

  15. Enhanced bioactive properties of BiodentineTM modified with bioactive glass nanoparticles

    Science.gov (United States)

    CORRAL NUÑEZ, Camila; COVARRUBIAS, Cristian; FERNANDEZ, Eduardo; de OLIVEIRA, Osmir Batista

    2017-01-01

    Abstract Objective To prepare nanocomposite cements based on the incorporation of bioactive glass nanoparticles (nBGs) into BiodentineTM (BD, Septodent, Saint-Maur-des-Fosses Cedex, France) and to assess their bioactive properties. Material and Methods nBGs were synthesised by the sol-gel method. BD nanocomposites (nBG/BD) were prepared with 1 and 2% nBGs by weight; unmodified BD and GC Fuji IX (GIC, GC Corporation, Tokyo, Japan) were used as references. The in vitro ability of the materials to induce apatite formation was assessed in SBF by X-ray diffraction (XRD), attenuated total reflectance with Fourier transform infrared spectroscopy (ATR-FTIR), and scanning electron microscopy (SEM) with energy dispersive X-ray (EDX) analysis. BD and nBG/BD were also applied to dentine discs for seven days; the morphology and elemental composition of the dentine-cement interface were analysed using SEM-EDX. Results One and two percent nBG/BD composites accelerated apatite formation on the disc surface after short-term immersion in SBF. Apatite was detected on the nBG/BD nanocomposites after three days, compared with seven days for unmodified BD. No apatite formation was detected on the GIC surface. nBG/BD formed a wider interfacial area with dentine than BD, showing blockage of dentine tubules and Si incorporation, suggesting intratubular precipitation. Conclusions The incorporation of nBGs into BD improves its in vitro bioactivity, accelerating the formation of a crystalline apatite layer on its surface after immersion in SBF. Compared with unmodified BD, nBG/BD showed a wider interfacial area with greater Si incorporation and intratubular precipitation of deposits when immersed in SBF. PMID:28403358

  16. Enhanced bioactive properties of BiodentineTM modified with bioactive glass nanoparticles

    Directory of Open Access Journals (Sweden)

    Camila CORRAL NUÑEZ

    Full Text Available Abstract Objective To prepare nanocomposite cements based on the incorporation of bioactive glass nanoparticles (nBGs into BiodentineTM (BD, Septodent, Saint-Maur-des-Fosses Cedex, France and to assess their bioactive properties. Material and Methods nBGs were synthesised by the sol-gel method. BD nanocomposites (nBG/BD were prepared with 1 and 2% nBGs by weight; unmodified BD and GC Fuji IX (GIC, GC Corporation, Tokyo, Japan were used as references. The in vitro ability of the materials to induce apatite formation was assessed in SBF by X-ray diffraction (XRD, attenuated total reflectance with Fourier transform infrared spectroscopy (ATR-FTIR, and scanning electron microscopy (SEM with energy dispersive X-ray (EDX analysis. BD and nBG/BD were also applied to dentine discs for seven days; the morphology and elemental composition of the dentine-cement interface were analysed using SEM-EDX. Results One and two percent nBG/BD composites accelerated apatite formation on the disc surface after short-term immersion in SBF. Apatite was detected on the nBG/BD nanocomposites after three days, compared with seven days for unmodified BD. No apatite formation was detected on the GIC surface. nBG/BD formed a wider interfacial area with dentine than BD, showing blockage of dentine tubules and Si incorporation, suggesting intratubular precipitation. Conclusions The incorporation of nBGs into BD improves its in vitro bioactivity, accelerating the formation of a crystalline apatite layer on its surface after immersion in SBF. Compared with unmodified BD, nBG/BD showed a wider interfacial area with greater Si incorporation and intratubular precipitation of deposits when immersed in SBF.

  17. Bioactive Glass Nanopowder for theTreatment of Oral Bone Defects

    Directory of Open Access Journals (Sweden)

    MH. Fathi

    2007-09-01

    Full Text Available Objective: Osseous defects around dental implants are often seen when implants are placed in areas with inadequate alveolar bone, or around failing implants. Bone regenera-tion in these areas using bone grafts or its substitutes may improve dental implants prog-nosis. The aim of this study was to prepare and characterize the bioactive glass nanopow-der and development of its coating for treatment of oral bone defects.Materials and Methods: Bioactive bioglass coating was made on stainless steel plates by sol-gel technique. The powder shape and size was evaluated by transmission electron mi-cropscopy, and thermal properties studied using differential thermal analysis (DTA. Structural characterization techniques (XRD were used to analyze and study the structure and phase present in the prepared bioactive glass nanopowder. This nanopowder was immersed in the simulated body fluid (SBF solution. Fourier transform infrared spec-troscopy (FTIR was utilized to recognize and confirm the formation of apatite layer on prepared bioactive glass nanopowder.Results: The bioglass powder size was less than 100 nanometers which was necessary for better bioactivity, and preparing a homogeneous coating. The formation of apatite layer confirmed the bioactivity of the bioglass nanopowder. Crack-free and homogeneous bioglass coatings were achieved with no observable defects.Conclusion: It was concluded that the prepared bioactive glass nanopowder could be more effective as a bone replacement material than conventional bioactive glass to pro-mote bone formation in osseous defects. The prepared bioactive glass nanopowder could be more useful for treatment of oral bone defects compare to conventional hydroxyapatite or bioactive glass.

  18. Thermoluminescence as a probe in bioactivity studies; the case of 58S sol-gel bioactive glass

    Energy Technology Data Exchange (ETDEWEB)

    Polymeris, George S; Tsirliganis, Nestor C [Archaeometry Laboratory, Cultural and Educational Technology Institute (CETI), RC Athena, Tsimiski 58, 67100-Xanthi (Greece); Goudouri, Ourania Menti; Paraskevopoulos, Konstantinos M [Solid State Section, Department of Physics, Aristotle University of Thessaloniki, 54124 Thessaloniki (Greece); Kontonasaki, Eleana [Department of Fixed Prosthodontics, School of Dentistry, Aristotle University of Thessaloniki, Thessaloniki 54124 (Greece); Kitis, George, E-mail: polymers@auth.gr [Nuclear and Elementary Particle Physics Laboratory, Department of Physics, Aristotle University of Thessaloniki, 54124 Thessaloniki (Greece)

    2011-10-05

    The formation of a carbonated hydroxyapatite (HCAp) layer on the surface of bioactive materials is the main reaction that takes place upon their immersion in physiological fluids. To date, all techniques used for the identification of this HCAp formation are rather time consuming and not well suited to detailed and rapid monitoring of changes in the bioactivity response of the material. The aim of this work is to explore the possibility of using thermoluminescence (TL) for the discrimination between different bioactive responses in the case of the 58S bioactive glass. Results provided strong indications that the 110 deg. C TL peak of quartz can be used effectively in the study of the bioactive behaviour of 58S bioactive glass, since it is unambiguously present in all samples and does not require deconvolution analysis. Furthermore, the intensity of the 110 deg. C TL peak is proven to be very sensitive to the different bioactive responses, identifying the loss of silica which takes place at the first stages of the sequence. The discontinuities of the 110 deg. C TL peak intensity plot versus immersion time at 8 and 1440 min provide experimental indications regarding the timescale for both the beginning of amorphous CaP formation as well as the end of crystalline hydroxyl-apatite formation respectively, while the spike in the sensitization of the 110 deg. C TL peak, which was observed for immersion times ranging between 20 and 40 min, could be an experimental feature indicating the beginning of the crystalline HCAp formation.

  19. Strontium-substituted bioactive glasses in vitro osteogenic and antibacterial effects.

    Science.gov (United States)

    Liu, Jie; Rawlinson, Simon C F; Hill, Robert G; Fortune, Farida

    2016-03-01

    Bioactive glass forms a bone mineral apatite interface and can be engineered to promote optimal bone regeneration. Strontium (Sr(2+)) stimulates osteoblast and inhibits osteoclast activities in vitro, and is used clinically as a treatment for osteoporosis. Dental bone defect repair requires rapid bone formation for early osseointegration but, can be subject to infection. The aim of this study was to investigate the osteogenic and antibacterial effects of strontium-substituted bioactive glasses in vitro. Strontium-substituted bioactive glasses were designed and produced. Then the osteogenic potential and antibacterial effects of bioactive glass particulates were explored. Alkaline phosphatase activity, cell number, Type I collagen and mineral nodule formation of MC3T3-E1 cells were significantly promoted by the 5% strontium-substituted glass (5Sr). Furthermore, after incubation with 0.001g and 0.01g glass particulates, the growth of sub-gingival bacteria, Aggregatibacter actinomycetemcomitans and Porphyromonas gingivalis was significantly inhibited; the antibacterial activity being dependent on the percentage of strontium in the glasses. These results show that strontium-substituted bioactive glasses significantly promote osteogenic responses of MC3T3-E1 osteoblast-like cells and inhibit the growth of A. actinomycetemcomitans and P. gingivalis. Crown Copyright © 2015. Published by Elsevier Ltd. All rights reserved.

  20. Bioactive glass scaffolds for bone tissue engineering: state of the art and future perspectives

    OpenAIRE

    Fu, Qiang; Saiz, Eduardo; Rahaman, Mohamed N.; Tomsia, Antoni P.

    2011-01-01

    The repair and regeneration of large bone defects resulting from disease or trauma remains a significant clinical challenge. Bioactive glass has appealing characteristics as a scaffold material for bone tissue engineering, but the application of glass scaffolds for the repair of load-bearing bone defects is often limited by their low mechanical strength and fracture toughness. This paper provides an overview of recent developments in the fabrication and mechanical properties of bioactive glas...

  1. Sol-gel processing of bioactive glass nanoparticles: A review.

    Science.gov (United States)

    Zheng, Kai; Boccaccini, Aldo R

    2017-03-21

    Silicate-based bioactive glass nanoparticles (BGN) are gaining increasing attention in various biomedical applications due to their unique properties. Controlled synthesis of BGN is critical to their effective use in biomedical applications since BGN characteristics, such as morphology and composition, determining the properties of BGN, are highly related to the synthesis process. In the last decade, numerous investigations focusing on BGN synthesis have been reported. BGN can mainly be produced through the conventional melt-quench approach or by sol-gel methods. The latter approaches are drawing widespread attention, considering the convenience and versatility they offer to tune the properties of BGN. In this paper, we review the strategies of sol-gel processing of BGN, including those adopting different catalysts for initiating the hydrolysis and condensation of silicate precursors as well as those combining sol-gel chemistry with other techniques. The processes and mechanism of different synthesis approaches are introduced and discussed in detail. Considering the importance of the BGN morphology and composition to their biomedical applications, strategies put forward to control the size, shape, pore structure and composition of BGN are discussed. BGN are particularly interesting biomaterials for bone-related applications, however, they also have potential for other biomedical applications, e.g. in soft tissue regeneration/repair. Therefore, in the last part of this review, recently reported applications of BGN in soft tissue repair and wound healing are presented. Copyright © 2017 Elsevier B.V. All rights reserved.

  2. Phosphorus Effects of Mesoporous Bioactive Glass on Occlude Exposed Dentin

    Directory of Open Access Journals (Sweden)

    Wen-Cheng Chen

    2013-11-01

    Full Text Available In recent studies, sealing of exposed dentinal tubules is generally considered as one of the most effective strategies to treat dentin hypersensitivity. Mesoporous bioactive glass (MBG is a potential material for treating dentin hypersensitivity due to its highly specific areas for dissolution and re-precipitated reaction for reduction in dentin permeability. The groups of commercial products of PerioGlas®, synthetic MBG and MBG without phosphorus (MBGNP were compared. The MBG and MBGNP powders were prepared by the sol-gel method and mixed with different calculated ratios of phosphoric acid (PA and then was brushed onto dentin surfaces. We used X-ray diffractometer (XRD, scanning electronic microscope (SEM, and Fourier transform infrared spectroscopy (FTIR to investigate the physiochemistry and the occlusion ability of dentinal tubules. The results showed that MBG paste mixed with PA solution has a better ability for occluding dentinal tubules than MBGNP; it has a short reaction time and good operability. The major crystallite phase of MBG agents was monocalcium phosphate monohydrate [Ca(H2PO42·H2O] in the early stages of the reactions. MBG pastes that were mixed with 30% and 40% PA had the ability to create excellent penetration depth greater than 80 μm. These agents have the potential to treat dentin hypersensitivity.

  3. Nanoengineering of bioactive glasses: hollow and dense nanospheres

    Energy Technology Data Exchange (ETDEWEB)

    Luz, Gisela M., E-mail: gisela.luz@dep.uminho.pt; Mano, Joao F., E-mail: jmano@dep.uminho.pt [University of Minho, Headquarters of the European Institute of Excellence on Tissue Engineering and Regenerative Medicine, 3B' s Research Group, Biomaterials, Biodegradables and Biomimetics (Portugal)

    2013-02-15

    The possibility of engineering bioactive glass (BG) nanoparticles into suitable sizes and shapes represents a significant achievement regarding the development of new osteoconductive biomaterials for therapeutic strategies to replace or regenerate damaged mineralised tissues. Herein we report the structural and chemical evolution of sol-gel derived BG nanoparticles for both the binary (SiO{sub 2}:CaO (mol%) = 70:30) and ternary (SiO{sub 2}:CaO:P{sub 2}O{sub 5} (mol%) = 55:40:5) formulations, in order to understand how the particles formation can be directed. Hollow BG nanospheres were obtained through Ostwald ripening. The presence of a non ionic surfactant, poly(ethylene glycol) (PEG), allowed the formation of dense BG nanospheres with controllable diameters depending on the molecular weight of PEG. A deep insight into the genesis of BG nanoparticles formation is essential to design BG based materials with controlled compositions, morphologies and sizes at the nanoscale, in order to improve their performance in orthopaedic applications including bone tissue engineering.

  4. Nanoparticulate bioactive-glass-reinforced gellan-gum hydrogels for bone-tissue engineering.

    Science.gov (United States)

    Gantar, Ana; da Silva, Lucilia P; Oliveira, Joaquim M; Marques, Alexandra P; Correlo, Vitor M; Novak, Saša; Reis, Rui L

    2014-10-01

    This work presents bioactive-glass-reinforced gellan-gum spongy-like hydrogels (GG-BAG) as novel hydrophilic materials for use as the scaffolding in bone-tissue engineering. The reinforcement with bioactive-glass particles resulted in an improvement to the microstructure and to the mechanical properties of the material. These mechanical properties were found to be dependent on the composition and improved with the amount of bioactive glass; however, values necessary to accommodate biomechanical loading were not achieved in this study. Nevertheless, by incorporating the bioactive-glass particles, the composite material acquired the ability to form an apatite layer when soaked in simulated body fluid. Furthermore, human-adipose-derived stem cells were able to adhere and spread within the gellan-gum, spongy-like hydrogels reinforced with the bioactive glass, and remain viable, which is an important result when considering their use in bone-tissue engineering. Thus, hydrogels based on gellan gum and bioactive glass are promising biomaterials for use either alone or with cells, and with the potential for use in osteogenic differentiation. Copyright © 2014 Elsevier B.V. All rights reserved.

  5. Influence of strontium for calcium substitution in bioactive glasses on degradation, ion release and apatite formation

    Science.gov (United States)

    Fredholm, Yann C.; Karpukhina, Natalia; Brauer, Delia S.; Jones, Julian R.; Law, Robert V.; Hill, Robert G.

    2012-01-01

    Bioactive glasses are able to bond to bone through the formation of hydroxy-carbonate apatite in body fluids while strontium (Sr)-releasing bioactive glasses are of interest for patients suffering from osteoporosis, as Sr was shown to increase bone formation both in vitro and in vivo. A melt-derived glass series (SiO2–P2O5–CaO–Na2O) with 0–100% of calcium (Ca) replaced by Sr on a molar base was prepared. pH change, ion release and apatite formation during immersion of glass powder in simulated body fluid and Tris buffer at 37°C over up to 8 h were investigated and showed that substituting Sr for Ca increased glass dissolution and ion release, an effect owing to an expansion of the glass network caused by the larger ionic radius of Sr ions compared with Ca. Sr release increased linearly with Sr substitution, and apatite formation was enhanced significantly in the fully Sr-substituted glass, which allowed for enhanced osteoblast attachment as well as proliferation and control of osteoblast and osteoclast activity as shown previously. Studying the composition–structure–property relationship in bioactive glasses enables us to successfully design next-generation biomaterials that combine the bone regenerative properties of bioactive glasses with the release of therapeutically active Sr ions. PMID:21993007

  6. The effect of bioactive glass content on synthesis and bioactivity of composite poly (lactic-co-glycolic acid)/bioactive glass substrate for tissue engineering.

    Science.gov (United States)

    Yao, Jun; Radin, Shula; S Leboy, Phoebe; Ducheyne, Paul

    2005-05-01

    Tissue engineering offers a promising new approach to bone tissue grafting. One material that has received attention in this regard is the polymer poly (lactic-co-glycolic acid) (PLGA). It has the advantage of controllable bioresorption and ease of processing. Another material of interest is bioactive glass (BG), which shows the ability to stimulate osteoblastic differentiation of osteoprogenitor cells. In this study, we reported on the optimal synthesis parameters and the kinetics of formation of calcium phosphate (Ca-P) phase at the surface of PLGA/BG composites. The formation of calcium phosphate layer was confirmed using scanning electron microscopy/energy dispersive X-ray analysis (SEM/EDXA). PLGA-30%BG microspheres based porous scaffolds for bone tissue engineering were examined for their ability to promote osteogenesis of marrow stromal cells (MSC). This porous scaffold supported both MSC proliferation and promoted MSC differentiation into cells expressing the osteoblast phenotype. It therefore demonstrates significant potential as a bone replacement material.

  7. COMPARISON OF BIOACTIVITY IN VITRO OF GLASS AND GLASS CERAMIC MATERIALS DURING SOAKING IN SBF AND DMEM MEDIUM

    Directory of Open Access Journals (Sweden)

    GABRIELA LUTIŠANOVÁ

    2011-09-01

    Full Text Available This paper investigated the surface reactivity of two sets of glasses and glass ceramic materials belonging to the Li2O–SiO2–CaO–P2O5–CaF2 system. The in vitro bioactivity of coatings was evaluated using simulated body fluid (SBF and Dulbecco’s Modified Eagle’s Medium (DMEM soaking test in static regime for up to 28 days at 36.5°C in microincubator. The surface structure changes were examined by scanning electron microscopy (SEM and electron probe micro-analyzer (EPMA methods. The functional groups of the silicate and phosphates were identified by infrared spectroscopy (IR. The crystal phases of the glasses and glass ceramics were identified by X-ray diffraction analysis (XRD. The results suggest the bioactivity behavior for all compositions of glasses as well as glass ceramic samples after 28 days in the SBF and DMEM medium. The surface characterization and in vitro tests revealed a few variations in the reactivity of the different glasses and glass ceramic samples in their pristine form. The best results show the samples of glass and glass ceramic samples with higher content of fluorapatite (FA. The use of the acellular culture medium DMEM resulted in a delay at the start of precipitation.

  8. In vitro study of manganese-doped bioactive glasses for bone regeneration

    Energy Technology Data Exchange (ETDEWEB)

    Miola, Marta, E-mail: marta.miola@polito.it [Applied Science and Technology Department, Politecnico di Torino, C.so Duca degli Abruzzi 24, 10129 Turin (Italy); Brovarone, Chiara Vitale [Applied Science and Technology Department, Politecnico di Torino, C.so Duca degli Abruzzi 24, 10129 Turin (Italy); Maina, Giovanni [Department of Clinical and Biological Sciences, University of Turin, Via Zuretti 29, 10126 Turin (Italy); Rossi, Federica [Department of Public Health and Pediatric Sciences, Piazza Polonia, 94, 10126 Torino (Italy); Bergandi, Loredana; Ghigo, Dario [Department of Oncology, University of Turin, Via Santena 5/bis, 10126 Turin (Italy); Saracino, Silvia; Maggiora, Marina; Canuto, Rosa Angela; Muzio, Giuliana [Department of Clinical and Biological Sciences, University of Turin, Corso Raffaello 30, 10125 Turin (Italy); Vernè, Enrica [Applied Science and Technology Department, Politecnico di Torino, C.so Duca degli Abruzzi 24, 10129 Turin (Italy)

    2014-05-01

    A glass belonging to the system SiO{sub 2}–P{sub 2}O{sub 5}–CaO–MgO–Na{sub 2}O–K{sub 2}O was modified by introducing two different amounts of manganese oxide (MnO). Mn-doped glasses were prepared by melt and quenching technique and characterized by means of X-ray diffraction (XRD), scanning electron microscopy (SEM) observation and energy dispersion spectrometry (EDS) analysis. In vitro bioactivity test in simulated body fluid (SBF) showed a slight decrease in the reactivity kinetics of Mn-doped glasses compared to the glass used as control; however the glasses maintained a good degree of bioactivity. Mn-leaching test in SBF and minimum essential medium (MEM) revealed fluctuating trends probably due to a re-precipitation of Mn compounds during the bioactivity process. Cellular tests showed that all the Mn-doped glasses, up to a concentration of 50 μg/cm{sup 2} (μg of glass powders/cm{sup 2} of cell monolayer), did not produce cytotoxic effects on human MG-63 osteoblasts cultured for up to 5 days. Finally, biocompatibility tests demonstrated a good osteoblast proliferation and spreading on Mn-doped glasses and most of all that the Mn-doping can promote the expression of alkaline phosphatase (ALP) and some bone morphogenetic proteins (BMPs). - Highlights: • Novel bioactive glasses doped with manganese were prepared. • Mn-doped bioactive glasses were not cytotoxic towards human MG-63 osteoblasts. • The Mn introduction promotes the expression of ALP and bone morphogenetic proteins. • Mn-doped glass may be a promising material for bone regeneration procedures.

  9. Strontium substituted bioactive glasses for tissue engineered scaffolds: the importance of octacalcium phosphate.

    Science.gov (United States)

    Sriranganathan, Danujan; Kanwal, Nasima; Hing, Karin A; Hill, Robert G

    2016-02-01

    Porous bioactive glasses are attractive for use as bone scaffolds. There is increasing interest in strontium containing bone grafts, since strontium ions are known to up-regulate osteoblasts and down regulate osteoclasts. This paper investigates the influence of partial to full substitution of strontium for calcium on the dissolution and phase formation of a multicomponent high phosphate content bioactive glass. The glasses were synthesised by a high temperature melt quench route and ground to a powder of strontium substituted SP-17Sr-17Ca glass showed no clear evidence of apatite like phase formation in Tris, but evidence of an apatite like phase was observed after 7 days incubation in SBF. The SP-35Sr-0Ca glass formed a new crystalline phase termed "X Phase" in Tris buffer which FTIR indicated was a form of crystalline orthophosphate. The SP-35Sr-0Ca glass appeared to support apatite like phase formation in SBF by 28 days incubation. The results indicate that strontium substitution for calcium in high phosphate content bioactive glasses can retard apatite like phase formation. It is proposed that apatite formation with high phosphate bioactive glasses occurs via an octacalcium phosphate (OCP) precursor phase that subsequently transforms to apatite. The equivalent octa-strontium phosphate does not exist and consequently in the absence of calcium, apatite formation does not occur. The amount of strontium that can be substituted for calcium in OCP probably determines the amount of strontium in the final apatite phase and the speed with which it forms.

  10. Investigating in vitro bioactivity and magnetic properties of the ferrimagnetic bioactive glass-ceramic fabricated using soda-lime-silica waste glass

    Science.gov (United States)

    Abbasi, M.; Hashemi, B.; Shokrollahi, H.

    2014-04-01

    The main purpose of the current research is the production and characterization of a ferrimagnetic bioactive glass-ceramic prepared through the solid-state reaction method using soda-lime-silica waste glass as the main raw material. In comparison with the conventional route, that is, the melt-quenching and subsequent heat treatment, the present work is an economical technique. Structural, thermal and magnetic properties of the samples were examined by X-ray diffraction (XRD), differential thermal analysis (DTA) and vibrating sample magnetometer (VSM). The in vitro test was utilized to assess the bioactivity level of the samples by Hanks' solution as simulated body fluid (SBF). The apatite surface layer formation was examined by the scanning electron microscopy (SEM) equipped with energy dispersive spectroscopy (EDS). The calcium ion concentration in the solutions was measured by atomic absorption spectroscopy (AAS). VSM results revealed that with the addition of 5-20 wt% strontium hexaferrite to bioactive glass-ceramics, the ferrimagnetic bioactive glass-ceramics with hysteresis losses between 7024 and 75,852 erg/g were obtained. The in vitro test showed that the onset formation time of hydroxyapatite layer on the surface of the samples was 14 days and after 30 days, this layer was completed.

  11. Hydroxyapatite and bioactive glass surfaces for fiber reinforced composite implants via surface ablation by Excimer laser.

    Science.gov (United States)

    Kulkova, Julia; Moritz, Niko; Huhtinen, Hannu; Mattila, Riina; Donati, Ivan; Marsich, Eleonora; Paoletti, Sergio; Vallittu, Pekka K

    2017-11-01

    In skeletal reconstructions, composites, such as bisphenol-A-glycidyldimethacrylate resin reinforced with glass fibers, are potentially useful alternatives to metallic implants. Recently, we reported a novel method to prepare bioactive surfaces for these composites. Surface etching by Excimer laser was used to expose bioactive glass granules embedded in the resin. The purpose of this study was to analyze two types of bioactive surfaces created by this technique. The surfaces contained bioactive glass and hydroxyapatite granules. The selected processing parameters were adequate for the creation of the surfaces. However, the use of porous hydroxyapatite prevented the complete exposure the granules. In cell culture, for bioactive glass coatings, the pattern of proliferation of MG63 cells was comparable to that in the positive control group (Ti6Al4V) while inferior cell proliferation was observed on the surfaces containing hydroxyapatite granules. Scanning electron microscopy revealed osteointegration of implants with both types of surfaces. The technique is suitable for the exposure of solid bioactive glass granules. However, the long-term performance of the surfaces needs further assessment. Copyright © 2017 Elsevier Ltd. All rights reserved.

  12. Bioactive glasses with improved processing. Part 1. Thermal properties, ion release and apatite formation.

    Science.gov (United States)

    Groh, Daniel; Döhler, Franziska; Brauer, Delia S

    2014-10-01

    Bioactive glasses, particularly Bioglass® 45S5, have been used to clinically regenerate human bone since the mid-1980s; however, they show a strong tendency to undergo crystallization upon heat treatment, which limits their range of applications. Attempts at improving their processing (by reducing their tendency to crystallize) have included increasing their silica content (and thus their network connectivity), incorporating intermediate oxides or reducing their phosphate content, all of which reduce glass bioactivity. Therefore, bioactive glasses known for their good processing (e.g. 13-93) are considerably less bioactive. Here, we investigated if the processing of 45S5 bioactive glass can be improved while maintaining its network connectivity and phosphate content. The results show that, by increasing the calcium:alkali cation ratio, partially substituting potassium for sodium (thereby making use of the mixed alkali effect) and adding small amounts of fluoride, bioactive glasses can be obtained which have a larger processing window (suggesting that they can be processed more easily, allowing for sintering of scaffolds or drawing into fibres) while degrading readily and forming apatite in aqueous solution within a few hours. Copyright © 2014 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

  13. Bioplotting of a bioactive alginate dialdehyde-gelatin composite hydrogel containing bioactive glass nanoparticles.

    Science.gov (United States)

    Leite, Álvaro J; Sarker, Bapi; Zehnder, Tobias; Silva, Raquel; Mano, João F; Boccaccini, Aldo R

    2016-07-19

    Alginate dialdehyde-gelatin (ADA-GEL) constructs incorporating bioactive glass nanoparticles (BGNPs) were produced by biofabrication to obtain a grid-like highly-hydrated composite. The material could induce the deposition of an apatite layer upon immersion in a biological-like environment to sustain cell attachment and proliferation. Composites were formulated with different concentrations of BGNPs synthetized from a sol-gel route, namely 0.1% and 0.5% (w/v). Strontium doped BGNPs were also used. EDS analysis suggested that the BGNPs loading promoted the growth of bone-like apatite layer on the surface when the constructs were immersed in a simulated body fluid. Moreover, the composite constructs could incorporate with high efficiency ibuprofen as a drug model. Furthermore, the biofabrication process allowed the successful incorporation of MG-63 cells into the composite material. Cells were distributed homogeneously within the hydrogel composite, and no differences were found in cell viability between ADA-GEL and the composite constructs, proving that the addition of BGNPs did not influence cell fate. Overall, the composite material showed potential for future applications in bone tissue engineering.

  14. Capacity of mesoporous bioactive glass nanoparticles to deliver therapeutic molecules

    Science.gov (United States)

    El-Fiqi, Ahmed; Kim, Tae-Hyun; Kim, Meeju; Eltohamy, Mohamed; Won, Jong-Eun; Lee, Eun-Jung; Kim, Hae-Won

    2012-11-01

    Inorganic bioactive nanomaterials are attractive for hard tissue regeneration, including nanocomponents for bone replacement composites and nanovehicles for delivering therapeutics. Bioactive glass nanoparticles (BGn) have recently gained potential usefulness as bone and tooth regeneratives. Here we demonstrate the capacity of the BGn with mesopores to load and deliver therapeutic molecules (drugs and particularly genes). Spherical BGn with sizes of 80-90 nm were produced to obtain 3-5 nm sized mesopores through a sono-reacted sol-gel process. A simulated body fluid test of the mesoporous BGn confirmed their excellent apatite forming ability and the cellular toxicity study demonstrated their good cell viability up to 100 μg ml-1. Small molecules like chemical drug (Na-ampicillin) and gene (small interfering RNA; siRNA) were introduced as model drugs considering the mesopore size of the nanoparticles. Moreover, amine-functionalization allowed switchable surface charge property of the BGn (from -20-30 mV to +20-30 mV). Loading of ampicillin or siRNA saturated within a few hours (~2 h) and reflected the mesopore structure. While the ampicillin released relatively rapidly (~12 h), the siRNA continued to release up to 3 days with almost zero-order kinetics. The siRNA-nanoparticles were easily taken up by the cells, with a transfection efficiency as high as ~80%. The silencing effect of siRNA delivered from the BGn, as examined by using bcl-2 model gene, showed dramatic down-regulation (~15% of control), suggesting the potential use of BGn as a new class of nanovehicles for genes. This, in conjunction with other attractive properties, including size- and mesopore-related high surface area and pore volume, tunable surface chemistry, apatite-forming ability, good cell viability and the possible ion-related stimulatory effects, will potentiate the usefulness of the BGn in hard tissue regeneration.Inorganic bioactive nanomaterials are attractive for hard tissue regeneration

  15. Bioactive glass scaffolds for bone tissue engineering: state of the art and future perspectives.

    Science.gov (United States)

    Fu, Qiang; Saiz, Eduardo; Rahaman, Mohamed N; Tomsia, Antoni P

    2011-10-10

    The repair and regeneration of large bone defects resulting from disease or trauma remains a significant clinical challenge. Bioactive glass has appealing characteristics as a scaffold material for bone tissue engineering, but the application of glass scaffolds for the repair of load-bearing bone defects is often limited by their low mechanical strength and fracture toughness. This paper provides an overview of recent developments in the fabrication and mechanical properties of bioactive glass scaffolds. The review reveals the fact that mechanical strength is not a real limiting factor in the use of bioactive glass scaffolds for bone repair, an observation not often recognized by most researchers and clinicians. Scaffolds with compressive strengths comparable to those of trabecular and cortical bones have been produced by a variety of methods. The current limitations of bioactive glass scaffolds include their low fracture toughness (low resistance to fracture) and limited mechanical reliability, which have so far received little attention. Future research directions should include the development of strong and tough bioactive glass scaffolds, and their evaluation in unloaded and load-bearing bone defects in animal models.

  16. Inhibition of multi-species oral biofilm by bromide doped bioactive glass.

    Science.gov (United States)

    Galarraga-Vinueza, M E; Passoni, B; Benfatti, C A M; Mesquita-Guimarães, J; Henriques, B; Magini, R S; Fredel, M C; Meerbeek, B V; Teughels, W; Souza, J C M

    2017-07-01

    Bioactive glass is an attractive biomaterial that has shown excellent osteogenic and angiogenic effects for oral bone repairing procedures. However, anti-biofilm potential related to such biomaterial has not been completely validated, mainly against multi-species biofilms involved in early tissue infections. The aim of the present study was to evaluate the anti-biofilm effect of 58 S bioactive glass embedding calcium bromide compounds at different concentrations. Bioactive glass free or containing 5, or 10 wt % CaBr 2 was synthesized by alkali sol-gel method and then characterized by physco-chemical analyses and scanning electron microscopy (SEM). Then, samples were tested by microbiological assays using optical density, real time q-PCR, and SEM. Bioactive glass particles showed accurate chemical composition and an angular shape with a bimodal size distribution ranging from 0.6 to 110 µm. The mean particle size was around 29 µm. Anti-biofilm effect was recorded for 5 wt % CaBr 2 -doped bioactive glass against S. mitis, V. parvula, P. gingivais, S. gordoni, A. viscosus, F, nucleatum, P. gingivais. F. nucleatum, and P. gingivalis. Such species are involved in the biofilm structure related to infections on hard and soft tissues in the oral cavity. The incorporation of calcium bromide into bioactive glass can be a strategy to enhance the anti-biofilm potential of bioactive glasses for bone healing and infection treatment. © 2016 Wiley Periodicals, Inc. J Biomed Mater Res Part A: 105A: 1994-2003, 2017. © 2017 Wiley Periodicals, Inc.

  17. STATIC AND DYNAMIC IN VITRO TEST OF BIOACTIVITY OF GLASS CERAMICS

    Directory of Open Access Journals (Sweden)

    JANA KOZÁNKOVÁ

    2011-06-01

    Full Text Available The bioactivity of glass ceramics from Li2O–SiO2–CaO–P2O5–CaF2 system, with different amount of fluorapatite expressed as P2O5 content, has been tested in vitro under static and dynamic regime. The paper reports the results of bioactivity test of glass ceramics in static and dynamic regime. XRD, SEM and EPMA analysis were used to characterise the sample as well as to detect the presence of new phase onto the surface of glass ceramics. The bioactivity, as demonstrated by the formation of new apatite layer, depends on P2O5 content and testing regime. In static regime, one can observe a fine microstructure of hydroxyapatite layer on the surface on glass ceramics samples. In dynamic regime, the formation rate of this layer seems to be retarded in comparison with that of static regime.

  18. An overview of the effects of thermal processing on bioactive glasses

    Directory of Open Access Journals (Sweden)

    Bellucci D.

    2010-01-01

    Full Text Available Bioglass® 45S5 is widely used in biomedical applications due to its ability to bond to bone and even to soft tissues. The sintering ability of Bioglass® powders is a key factor from a technological point of view, since its govern the production of advanced devices, ranging from highly porous scaffolds to functionalized coatings. Unfortunately this particular glass composition is prone to crystallize at the temperature required for sintering and this may impair the bioactivity of the original glass. For these reasons, a prerequisite to tailor the fabrication of Bioglass®-derived implants is to understand the interaction between sintering, crystallization and bioactivity. In this work the structural transformations which occur during the heat treatment of Bioglass® are reviewed and a special attention is paid to the sintering and crystallization processes. Moreover the bioactivity of the final glass-ceramics is discussed and some alternative glass formulations are reported.

  19. Alkali-free bioactive glasses for bone tissue engineering: a preliminary investigation.

    Science.gov (United States)

    Goel, Ashutosh; Kapoor, Saurabh; Rajagopal, Raghu Raman; Pascual, Maria J; Kim, Hae-Won; Ferreira, José M F

    2012-01-01

    An alkali-free series of bioactive glasses has been designed and developed in the glass system CaO-MgO-SiO(2)-P(2)O(5)-CaF(2) along the diopside (CaMgSi(2)O(6))-fluorapatite (Ca(5)(PO(4))(3)F)-tricalcium phosphate (3CaO·P(2)O(5)) join. The silicate network in all the investigated glasses is predominantly coordinated in Q(2) (Si) units, while phosphorus tends to remain in an orthophosphate (Q(0)) environment. The in vitro bioactivity analysis of glasses has been made by immersion of glass powders in simulated body fluid (SBF) while chemical degradation has been studied in Tris-HCl in accordance with ISO-10993-14. Some of the investigated glasses exhibit hydroxyapatite formation on their surface within 1-12 h of their immersion in SBF solution. The sintering and crystallization kinetics of glasses has been investigated by differential thermal analysis and hot-stage microscopy, respectively while the crystalline phase evolution in resultant glass-ceramics has been studied in the temperature range of 800-900°C using powder X-ray diffraction and scanning electron microscopy. The alkaline phosphatase activity and osteogenic differentiation for glasses have been studied in vitro on sintered glass powder compacts using rat bone marrow mesenchymal stem cells. The as-designed glasses are ideal candidates for their potential applications in bone tissue engineering in the form of bioactive glasses as well as glass/glass-ceramic scaffolds. Published by Elsevier Ltd.

  20. Addition of bioactive glass to glass ionomer cements: Effect on the physico-chemical properties and biocompatibility.

    Science.gov (United States)

    De Caluwé, T; Vercruysse, C W J; Ladik, I; Convents, R; Declercq, H; Martens, L C; Verbeeck, R M H

    2017-04-01

    Glass ionomer cements (GICs) are a subject of research because of their inferior mechanical properties, despite their advantages such as fluoride release and direct bonding to bone and teeth. Recent research aims to improve the bioactivity of the GICs and thereby improve mechanical properties on the long term. In this study, two types of bioactive glasses (BAG) (45S5F and CF9) are combined with GICs to evaluate the physico-chemical properties and biocompatibility of the BAG-GIC combinations. The effect of the addition of Al 3+ to the BAG composition and the use of smaller BAG particles on the BAG-GIC properties was also investigated. Conventional aluminosilicate glass (ASG) and (modified) BAG were synthesized by the melt method. BAG-GIC were investigated on setting time, compressive strength and bioactivity. Surface changes were evaluated by Fourier transform infrared (FT-IR), scanning electron microscopy (SEM), EDS and PO 4 3- -and Ca 2+ uptake in SBF. Biocompatibility of selected BAG-GICs was determined by a direct toxicity assay. The addition of BAG improves the bioactivity of the GIC, which can be observed by the formation of an apatite (Ap) layer, especially in CF9-containing GICs. More BAG leads to more bioactivity but decreases strength. The addition of Al 3+ to the BAG composition improves strength, but decreases bioactivity. BAGs with smaller particle sizes have no effect on bioactivity and decrease strength. The formation of an Ap layer seems beneficial to the biocompatibility of the BAG-GICs. Bioactive GICs may have several advantages over conventional GICs, such as remineralization of demineralized tissue, adhesion and proliferation of bone- and dental cells, allowing integration in surrounding tissue. CF9 BAG-GIC combinations containing maximum 10mol% Al 3+ are most promising, when added in ≤20wt% to a GIC. Copyright © 2017 The Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

  1. Nanostructured bioactive glass-ceramic coatings deposited by the liquid precursor plasma spraying process

    Energy Technology Data Exchange (ETDEWEB)

    Xiao Yanfeng; Song Lei; Liu Xiaoguang; Huang Yi; Huang Tao; Wu Yao; Chen Jiyong [National Engineering Research Center for Biomaterials, Sichuan University, 29 Wangjiang Road Chengdu, Sichuan 610064 (China); Wu Fang, E-mail: fwu@scu.edu.cn [National Engineering Research Center for Biomaterials, Sichuan University, 29 Wangjiang Road Chengdu, Sichuan 610064 (China)

    2011-01-01

    Bioactive glass-ceramic coatings have great potential in dental and orthopedic medical implant applications, due to its excellent bioactivity, biocompatibility and osteoinductivity. However, most of the coating preparation techniques either produce only thin thickness coatings or require tedious preparation steps. In this study, a new attempt was made to deposit bioactive glass-ceramic coatings on titanium substrates by the liquid precursor plasma spraying (LPPS) process. Tetraethyl orthosilicate, triethyl phosphate, calcium nitrate and sodium nitrate solutions were mixed together to form a suspension after hydrolysis, and the liquid suspension was used as the feedstock for plasma spraying of P{sub 2}O{sub 5}-Na{sub 2}O-CaO-SiO{sub 2} bioactive glass-ceramic coatings. The in vitro bioactivities of the as-deposited coatings were evaluated by soaking the samples in simulated body fluid (SBF) for 4 h, 1, 2, 4, 7, 14, and 21 days, respectively. The as-deposited coating and its microstructure evolution behavior under SBF soaking were systematically analyzed by scanning electron microscopy (SEM), X-ray diffraction (XRD), inductively coupled plasma (ICP), and Fourier transform infrared (FTIR) spectroscopy. The results showed that P{sub 2}O{sub 5}-Na{sub 2}O-CaO-SiO{sub 2} bioactive glass-ceramic coatings with nanostructure had been successfully synthesized by the LPPS technique and the synthesized coatings showed quick formation of a nanostructured HCA layer after being soaked in SBF. Overall, our results indicate that the LPPS process is an effective and simple method to synthesize nanostructured bioactive glass-ceramic coatings with good in vitro bioactivity.

  2. Electrophoretic deposition of chitosan/45S5 bioactive glass composite coatings doped with Zn and Sr

    Directory of Open Access Journals (Sweden)

    Marta eMiola

    2015-10-01

    Full Text Available In this research work the original 45S5 bioactive glass (BG was modified by introducing zinc and/or strontium oxide (6% mol in place of calcium oxide. Sr was added for its ability to stimulate bone formation, Zn for its role in bone metabolism, antibacterial properties and anti-inflammatory effect. The glasses were produced by means of melting and quenching process. SEM and XRD analyses evidenced that Zr and Sr introduction did not modify the glass structure and morphology, while compositional analysis (EDS demonstrated the effective addition of these elements inside the glass network. Bioactivity test in simulated body fluid (SBF up to one month evidenced a reduced bioactivity kinetics for Zn-doped glasses. Doped glasses were combined with chitosan to produce organic/inorganic composite coatings on stainless steel AISI 316L by electrophoretic deposition (EPD. Two EPD processes were considered for coating development, namely direct current EPD (DC-EPD and alternating current EPD (AC-EPD. The stability of the suspension was analysed and the deposition parameters were optimized. Tape and bending tests demonstrated a good coating-substrate adhesion for coatings containing 45S5-Sr and 45S5-ZnSr glasses, while the adhesion to the substrate decreased by using 45S5-Zn glass. FTIR analyses demonstrated the composite nature of coatings and SEM observations indicated that glass particles were well integrated in the polymeric matrix, the coatings were fairly homogeneous and free of cracks; moreover the AC-EPD technique provided better results than DC-EPD in terms of coating quality. SEM, XRD analyses and Raman spectroscopy, performed after bioactivity test in SBF solution, confirmed the bioactive behaviour of 45S5-Sr containing coating, while coatings containing Zn exhibited no hydroxyapatite formation.

  3. Comparison of Calcium Hydroxide and Bioactive Glass after Direct Pulp Capping in Primary Teeth

    Directory of Open Access Journals (Sweden)

    R. Haghgoo

    2007-12-01

    Full Text Available Objective: Bioactive glass is often used as a filler material for repair of dental bone defects.In different studies osteogenic potential of this material was proved, but its dentinogenesisproperty is in doubt. The purpose of this study was to evaluate the histological pulp responses of Calcium hydroxide and Bioactive glass placed directly on exposed pulp tissues.Materials and Methods: Twenty teeth to be extracted due to orthodontic reasons were selected. These teeth were divided into two groups and treated with direct pulp capping.Calcium hydroxide was used for 10 teeth and Bioactive glass for 10 teeth. After 60 daysthe teeth were extracted and prepared for histological evaluation. Finally the data was analyzed with exact Fisher test.Results: All teeth treated with Calcium hydroxide showed inflammation. Internal resorption was seen in six teeth, abscess in five teeth and dentinal bridge in two teeth. Inflammationwas seen in three Bioactive glass samples and dentinal bridge in seven teeth, but internal resorption and abscess were not seen.Conclusion: Bioactive glass appears to be superior to Calcium hydroxide as a pulp capping agent in primary teeth.

  4. Anti-biofilm properties of bioactive glasses embedding organic active compounds.

    Science.gov (United States)

    Galarraga-Vinueza, M E; Mesquita-Guimarães, J; Magini, R S; Souza, J C M; Fredel, M C; Boccaccini, A R

    2017-02-01

    Bioactive glasses (BGs) are promising materials for bone repair due to their desirable properties such as osteoconductivity, biodegradability, angiogenic potential, and antibacterial activity. Ionic dissolution products from bioactive glasses increase the medium pH inhibiting surrounding bacteria proliferation. The activity of BGs against biofilm formation has been enhanced by incorporating organic antibacterial compounds. The aim of this review was to summarize evidence in literature which assesses the efficacy of antibacterial and anti-biofilm compounds embedded in bioactive glasses to prevent peri-implant infection during bone healing. A PubMed bibliographical research was carried out including articles published in the last 20 years. Most previous studies evaluated antibacterial efficiency in planktonic cultures but did not investigate biofilm inhibition, underestimating biofilm clinical relevance. Multifactorial features such as biocompatibility of embedded compounds, receptor site characteristics, and drug delivery efficiency have been found to influence the bioactive glass capability of acting both as an anti-biofilm agent and as a bone repairing biomaterial. Accordingly, further in vitro and in vivo studies are required to select the most promising anti-biofilm agents which should be incorporated into bioactive glasses to counteract biofilm proliferation, without inducing toxic effects on human cells, and with the added functionality of promoting bone regeneration. © 2016 Wiley Periodicals, Inc. J Biomed Mater Res Part A: 105A: 672-679, 2017. © 2016 Wiley Periodicals, Inc.

  5. Repair of critical size defects using bioactive glass seeded with adipose-derived mesenchymal stem cells.

    Science.gov (United States)

    Saçak, Bülent; Certel, Furkan; Akdeniz, Zeynep D; Karademir, Betül; Ercan, Feriha; Özkan, Naziye; Akpinar, İhsan Nuri; Çelebiler, Özhan

    2017-07-01

    Bioactive glass has been demonstrated as a biocompatible bone substitute. However bone healing process can be prolonged due to late resorption of the material. Adipose derived stem cells (ASC) have osteogenic differentiation potential and hence can be a cell source for bone regeneration. The aim of this study was to test whether combination of bioactive glass with ASCs would enhance bone regeneration. Following creation of critical sized defects on the calvaria of 32 Wistar rats, the animals were randomly divided into four groups: Group C (control): Defects were left untreated; Group G: Defects were covered with autologous bone graft; Group BG: Defects were filled with bioactive glass; Group BG/ASC: Defects were filled with bioactive glass seeded with ASCs. The defect size was significantly greater in Group C compared to all other groups. Bone density was significantly lower in Group C compared to Group G and Group BG/ASC. Bone regeneration score of Group C was significantly lower than other groups. Group BG/ASC demonstrated lamellar bone and havers canal formation. The results of this study demonstrated that bioactive glass implanted with ASC is a biocompatible construct stimulating radiologically and histologically evident bone regeneration similar to autologous bone grafting. © 2016 Wiley Periodicals, Inc. J Biomed Mater Res Part B: Appl Biomater, 105B: 1002-1008, 2017. © 2016 Wiley Periodicals, Inc.

  6. Risedronate adsorption on bioactive glass surface for applications as bone biomaterial

    Energy Technology Data Exchange (ETDEWEB)

    Mosbahi, Siwar [University of Rennes 1, UMR CNRS 6226, Campus de Beaulieu, 35042 Rennes (France); Orthopaedic and Traumatology Laboratory, Sfax Faculty of Medicine, Sfax (Tunisia); Oudadesse, Hassane, E-mail: hassane.oudadesse@univ-rennes1.fr [University of Rennes 1, UMR CNRS 6226, Campus de Beaulieu, 35042 Rennes (France); Lefeuvre, Bertand [University of Rennes 1, UMR CNRS 6226, Campus de Beaulieu, 35042 Rennes (France); Barroug, Allal [University Cadi Ayyad, Faculty of Science Semlalia, Marrakech (Morocco); CNRST, Rabat (Morocco); Elfeki, Hafed [Science Materials and Environement Laboratory, Sfax Faculty of Science, Sfax (Tunisia); Elfeki, Abdelfattah [Animal Ecophysiology Laboratory, Sfax Faculty of Science, Department of Life Sciences, Sfax (Tunisia); Roiland, Claire [University of Rennes 1, UMR CNRS 6226, Campus de Beaulieu, 35042 Rennes (France); Keskes, Hassib [Orthopaedic and Traumatology Laboratory, Sfax Faculty of Medicine, Sfax (Tunisia)

    2016-03-30

    Highlights: • The fixation of risèdronates on the bioactive glass surface has been highlighted. • Scanning electron microscopy shows the new morphology of this composite. • Chemical analyses reveal the stability of adsorption process after 40 min of incubation. - Abstract: The aim of the current work is to study the physicochemical interactions between bisphosphonates molecules, risedronate (RIS) and bioactive glass (46S6) after their association by adsorption phenomenon. To more understand the interaction processes of RIS with the 46S6 surface we have used complementary physicochemical techniques such as infrared (FTIR), Raman and nuclear magnetic resonance (NMR) spectroscopy. The obtained results suggest that risedronate adsorption corresponds to an ion substitution reaction with silicon ions occurring at the bioactive glass surface. Thus, a pure bioactive glass was synthesized and fully characterized comparing the solids after adsorption (46S6-XRIS obtained after the interaction of 46S6 and X% risedronate). Therefore, based on the spectroscopic results FTIR, Raman and MAS-NMR, it can be concluded that strong interactions have been established between RIS ions and 46S6 surface. In fact, FTIR and Raman spectroscopy illustrate the fixation of risedronate on the bioactive glass surface by the appearance of several bands characterizing risedronate. The {sup 31}P MAS-NMR of the composite 46S6-XRIS show the presence of two species at a chemical shift of 15 and 19 ppm demonstrating thus the fixation of the RIS on 46S6 surface.

  7. Hypoxia-mimicking bioactive glass/collagen glycosaminoglycan composite scaffolds to enhance angiogenesis and bone repair.

    Science.gov (United States)

    Quinlan, Elaine; Partap, Sonia; Azevedo, Maria M; Jell, Gavin; Stevens, Molly M; O'Brien, Fergal J

    2015-06-01

    One of the biggest challenges in regenerative medicine is promoting sufficient vascularisation of tissue-engineered constructs. One approach to overcome this challenge is to target the cellular hypoxia inducible factor (HIF-1α) pathway, which responds to low oxygen concentration (hypoxia) and results in the activation of numerous pro-angiogenic genes including vascular endothelial growth factor (VEGF). Cobalt ions are known to mimic hypoxia by artificially stabilising the HIF-1α transcription factor. Here, resorbable bioactive glass particles (38 μm and 100 μm) with cobalt ions incorporated into the glass network were used to create bioactive glass/collagen-glycosaminoglycan scaffolds optimised for bone tissue engineering. Inclusion of the bioactive glass improved the compressive modulus of the resulting composite scaffolds while maintaining high degrees of porosity (>97%). Moreover, in vitro analysis demonstrated that the incorporation of cobalt bioactive glass with a mean particle size of 100 μm significantly enhanced the production and expression of VEGF in endothelial cells, and cobalt bioactive glass/collagen-glycosaminoglycan scaffold conditioned media also promoted enhanced tubule formation. Furthermore, our results prove the ability of these scaffolds to support osteoblast cell proliferation and osteogenesis in all bioactive glass/collagen-glycosaminoglycan scaffolds irrespective of the particle size. In summary, we have developed a hypoxia-mimicking tissue-engineered scaffold with pro-angiogenic and pro-osteogenic capabilities that may encourage bone tissue regeneration and overcome the problem of inadequate vascularisation of grafts commonly seen in the field of tissue engineering. Copyright © 2015 Elsevier Ltd. All rights reserved.

  8. In vitro study of manganese-doped bioactive glasses for bone regeneration.

    Science.gov (United States)

    Miola, Marta; Brovarone, Chiara Vitale; Maina, Giovanni; Rossi, Federica; Bergandi, Loredana; Ghigo, Dario; Saracino, Silvia; Maggiora, Marina; Canuto, Rosa Angela; Muzio, Giuliana; Vernè, Enrica

    2014-05-01

    A glass belonging to the system SiO2-P2O5-CaO-MgO-Na2O-K2O was modified by introducing two different amounts of manganese oxide (MnO). Mn-doped glasses were prepared by melt and quenching technique and characterized by means of X-ray diffraction (XRD), scanning electron microscopy (SEM) observation and energy dispersion spectrometry (EDS) analysis. In vitro bioactivity test in simulated body fluid (SBF) showed a slight decrease in the reactivity kinetics of Mn-doped glasses compared to the glass used as control; however the glasses maintained a good degree of bioactivity. Mn-leaching test in SBF and minimum essential medium (MEM) revealed fluctuating trends probably due to a re-precipitation of Mn compounds during the bioactivity process. Cellular tests showed that all the Mn-doped glasses, up to a concentration of 50 μg/cm(2) (μg of glass powders/cm(2) of cell monolayer), did not produce cytotoxic effects on human MG-63 osteoblasts cultured for up to 5 days. Finally, biocompatibility tests demonstrated a good osteoblast proliferation and spreading on Mn-doped glasses and most of all that the Mn-doping can promote the expression of alkaline phosphatase (ALP) and some bone morphogenetic proteins (BMPs). Copyright © 2014 Elsevier B.V. All rights reserved.

  9. Corrosion mechanism and bioactivity of borate glasses analogue to Hench’s bioglass

    Directory of Open Access Journals (Sweden)

    Mona A. Ouis

    2012-09-01

    Full Text Available Bioactive borate glasses (from the system Na2O-CaO-B2O3-P2O5 and corresponding glass-ceramics as a new class of scaffold material were prepared by full replacement of SiO2 with B2O3 in Hench patented bioactive glass. The prepared samples were investigated by differential thermal analysis (DTA, Fourier transform infrared (FTIR spectroscopy and X-ray diffraction (XRD analysis. The DTA data were used to find out the proper heat treatment temperatures for preparation of the appropriate glass-ceramics with high crystallinity. The prepared crystalline glass-ceramics derivatives were examined by XRD to identify the crystalline phases that were precipitated during controlled thermal treatment. The FTIR spectroscopy was used to justify the formation of hydroxyapatite as an indication of the bioactivity potential or activity of the studied ternary borate glasses or corresponding glass-ceramics after immersion in aqueous phosphate solution. The corrosion results are interpreted on the basis of suggested recent views on the corrosion mechanism of such modified borate glasses in relation to their composition and constitution.

  10. In vitro study of polycaprolactone/bioactive glass composite coatings on corrosion and bioactivity of pure Mg

    Energy Technology Data Exchange (ETDEWEB)

    Yang, Yuyun; Michalczyk, Carolin [Institute of Biomaterials, University of Erlangen-Nuremberg, 91058 Erlangen (Germany); Singer, Ferdinand [Institute of Surface Science and Corrosion, University of Erlangen-Nuremberg, 91058 Erlangen (Germany); Virtanen, Sannakaisa, E-mail: virtanen@ww.uni-erlangen.de [Institute of Surface Science and Corrosion, University of Erlangen-Nuremberg, 91058 Erlangen (Germany); Boccaccini, Aldo R., E-mail: aldo.boccaccini@ww.uni-erlangen.de [Institute of Biomaterials, University of Erlangen-Nuremberg, 91058 Erlangen (Germany)

    2015-11-15

    Highlights: • Bioactive glass nanoparticles (nBG) enhance bioactivity of PCL coatings on Mg. • Barrier properties of PCL can be altered by nBG addition. • Degradation of PCL increased by addition of nBG. - Abstract: The influence of the addition of nano-scaled bioactive glass (nBG) powder into polycaprolactone (PCL) coatings on the biodegradation and bioactivity of pure Mg was investigated in the present work. Scanning electron microscopy (SEM), energy-dispersive X-ray spectrometry (EDS), Fourier transform infrared spectroscopy (FTIR) and electrochemical methods were employed to characterize the morphology, chemical composition and anticorrosion properties of the coatings. The results indicate that nBG addition in PCL increases the degradation of PCL in physiological solution; depending on the amount of nBG in the composite coating, the barrier properties of PCL therefore can be modified. At the same time, the addition of nBG facilitates the formation of hydroxyapatite during 7 days immersion in simulated body fluid (SBF).

  11. Bioactive glass-ionomer cement with potential therapeutic function to dentin capping mineralization.

    Science.gov (United States)

    Xie, Dong; Zhao, Jun; Weng, Yiming; Park, Jong-Gu; Jiang, Hui; Platt, Jeffrey A

    2008-10-01

    We have developed a novel bioactive resin-modified glass-ionomer cement system with therapeutic function to dentin capping mineralization. In the system, the newly synthesized star-shape poly(acrylic acid) was formulated with water, Fuji II LC filler, and bioactive glass S53P4 to form resin-modified glass-ionomer cement. Compressive strength (CS) was used as a screening tool for evaluation. The commercial glass-ionomer cement Fuji II LC was used as a control. All the specimens were conditioned in simulated body fluid (SBF) at 37 degrees C prior to testing. The effect of aging in SBF on CS and microhardness of the cements was investigated. Scanning electron microscopy was used to examine the in vitro dentin surface changes caused by the incorporation of bioactive glass. The results show that the system not only provided strengths comparable to original commercial Fuji II LC cement but also allowed the cement to help mineralize the dentin in the presence of SBF. It appears that this bioactive glass-ionomer cement system has direct therapeutic impact on dental restorations that require root surface fillings.

  12. Mechanochemically synthesized kalsilite based bioactive glass-ceramic composite for dental vaneering

    Science.gov (United States)

    Kumar, Pattem Hemanth; Singh, Vinay Kumar; Kumar, Pradeep

    2017-08-01

    Kalsilite glass-ceramic composites have been prepared by a mechanochemical synthesis process for dental veneering application. The aim of the present study is to prepare bioactive kalsilite composite material for application in tissue attachment and sealing of the marginal gap between fixed prosthesis and tooth. Mechanochemical synthesis is used for the preparation of microfine kalsilite glass-ceramic. Low temperature frit and bioglass have been prepared using the traditional quench method. Thermal, microstructural and bioactive properties of the composite material have been examined. The feasibility of the kalsilite to be coated on the base commercial opaque as well as the bioactive behavior of the coated specimen has been confirmed. This study indicates that the prepared kalsilite-based composites show similar structural, morphological and bioactive behavior to that of commercial VITA VMK95 Dentin 1M2.

  13. A novel approach to re-pegging hydroxyapatite implants using bioactive glass.

    Science.gov (United States)

    Heringer, Dustin M; Ng, John D

    2006-01-01

    To determine if bioactive glass, originally designed for craniomaxillofacial use, can be used effectively for re-pegging of hydroxyapatite orbital implants. Over a 2-year period, 3 patients with pegged hydroxyapatite orbital implants and related complications that did not respond to conservative treatment, underwent removal of the implant pegs and/or sleeves. Peg tracts were subsequently filled with bioactive glass. No complications occurred in any case during 3 years of follow-up. After 2 months, 2 patients underwent successful re-drilling of the peg site and insertion of titanium pegs. Both patients were satisfied with the results. The third patient has deferred re-pegging at this time. Bioactive glass is effective for refilling old peg tracts and allowing timely re-pegging of hydroxyapatite implants.

  14. Drug delivery property, bactericidal property and cytocompatibility of magnetic mesoporous bioactive glass

    Energy Technology Data Exchange (ETDEWEB)

    Liu, Yi-Zhuo [The Education Ministry Key Lab of Resource Chemistry, Shanghai Normal University, Shanghai 200234 (China); Shanghai Key Laboratory of Rare Earth Functional Materials, Shanghai Normal University, Shanghai 200234 (China); Li, Yang [Shanghai Key Laboratory of Orthopedic Implant, Department of Orthopedic Surgery, Shanghai Ninth People' s Hospital, Shanghai Jiao Tong University School of Medicine, Shanghai 200011 (China); Yu, Xi-Bin [The Education Ministry Key Lab of Resource Chemistry, Shanghai Normal University, Shanghai 200234 (China); Shanghai Key Laboratory of Rare Earth Functional Materials, Shanghai Normal University, Shanghai 200234 (China); Liu, Li-Na [Shanghai Key Laboratory of Orthopedic Implant, Department of Orthopedic Surgery, Shanghai Ninth People' s Hospital, Shanghai Jiao Tong University School of Medicine, Shanghai 200011 (China); Zhu, Zhen-An, E-mail: zhuzhenan2006@126.com [Shanghai Key Laboratory of Orthopedic Implant, Department of Orthopedic Surgery, Shanghai Ninth People' s Hospital, Shanghai Jiao Tong University School of Medicine, Shanghai 200011 (China); Guo, Ya-Ping, E-mail: ypguo@shnu.edu.cn [The Education Ministry Key Lab of Resource Chemistry, Shanghai Normal University, Shanghai 200234 (China); Shanghai Key Laboratory of Rare Earth Functional Materials, Shanghai Normal University, Shanghai 200234 (China)

    2014-08-01

    A multifunctional magnetic mesoporous bioactive glass (MMBG) has been widely used for a drug delivery system, but its biological properties have been rarely reported. Herein, the effects of mesopores and Fe{sub 3}O{sub 4} nanoparticles on drug loading–release property, bactericidal property and biocompatibility have been investigated by using mesoporous bioactive glass (MBG) and non-mesoporous bioactive glass (NBG) as control samples. Both MMBG and MBG have better drug loading efficiency than NBG because they possess ordered mesoporous channels, big specific surface areas and high pore volumes. As compared with MBG, the Fe{sub 3}O{sub 4} nanoparticles in MMBG not only provide magnetic property, but also improve sustained drug release property. For gentamicin-loaded MMBG (Gent-MMBG), the sustained release of gentamicin and the Fe{sub 3}O{sub 4} nanoparticles minimize bacterial adhesion significantly and prevent biofilm formation against Staphylococcus aureus (S. aureus) and Staphylococcus epidermidis (S. epidermidis). Moreover, the magnetic Fe{sub 3}O{sub 4} nanoparticles in MMBG can promote crucial cell functions such as cell adhesion, spreading and proliferation. The excellent biocompatibility and drug delivery property of MMBG suggest that Gent-MMBG has great potentials for treatment of implant-associated infections. - Highlights: • Multifunctional magnetic mesoporous bioactive glass is fabricated. • The bioactive glass has great biocompatibility. • The bioactive glass exhibits high drug loading–release properties. • The drug delivery system has bactericidal property. • Magnetic particles improve cell adhesion, spreading and proliferation.

  15. Synthesis and In Vitro Activity Assessment of Novel Silicon Oxycarbide-Based Bioactive Glasses

    Directory of Open Access Journals (Sweden)

    Isabel Gonzalo-Juan

    2016-11-01

    Full Text Available Novel bioactive glasses based on a Ca- and Mg-modified silicon oxycarbide (SiCaMgOC were prepared from a polymeric single-source precursor, and their in vitro activity towards hydroxyapatite mineralization was investigated upon incubating the samples in simulated body fluid (SBF at 37 °C. The as-prepared materials exhibit an outstanding resistance against devitrification processes and maintain their amorphous nature even after exposure to 1300 °C. The X-ray diffraction (XRD analysis of the SiCaMgOC samples after the SBF test showed characteristic reflections of apatite after only three days, indicating a promising bioactivity. The release kinetics of the Ca2+ and Mg2+ and the adsorption of H+ after immersion of SiCaMgOC in simulated body fluid for different soaking times were analyzed via optical emission spectroscopy. The results show that the mechanism of formation of apatite on the surface of the SiCaMgOC powders is similar to that observed for standard (silicate bioactive glasses. A preliminary cytotoxicity investigation of the SiOC-based bioactive glasses was performed in the presence of mouse embryonic fibroblasts (MEF as well as human embryonic kidney cells (HEK-293. Due to their excellent high-temperature crystallization resistance in addition to bioactivity, the Ca- and Mg-modified SiOC glasses presented here might have high potential in applications related to bone repair and regeneration.

  16. Hydrogel/bioactive glass composites for bone regeneration applications: Synthesis and characterisation

    Energy Technology Data Exchange (ETDEWEB)

    Killion, John A., E-mail: jkillion@research.ait.ie [Materials Research Institute, Athlone Institute of Technology, Dublin Rd, Athlone, Co. Westmeath (Ireland); Kehoe, Sharon, E-mail: sh625116@dal.ca [Department of Applied Oral Sciences, Dalhousie University, Halifax, NS B3H 34R2 (Canada); Geever, Luke M., E-mail: lgeever@ait.ie [Materials Research Institute, Athlone Institute of Technology, Dublin Rd, Athlone, Co. Westmeath (Ireland); Devine, Declan M., E-mail: ddevine@ait.ie [Materials Research Institute, Athlone Institute of Technology, Dublin Rd, Athlone, Co. Westmeath (Ireland); Sheehan, Eoin, E-mail: eoinsheehan@aol.com [Department of Trauma and Orthopaedics, MRHT, Tullamore, Co. Offaly (Ireland); Boyd, Daniel, E-mail: d.boyd@dal.ca [Department of Applied Oral Sciences, Dalhousie University, Halifax, NS B3H 34R2 (Canada); Higginbotham, Clement L., E-mail: chigginbotham@ait.ie [Materials Research Institute, Athlone Institute of Technology, Dublin Rd, Athlone, Co. Westmeath (Ireland)

    2013-10-15

    Due to the deficiencies of current commercially available biological bone grafts, alternative bone graft substitutes have come to the forefront of tissue engineering in recent times. The main challenge for scientists in manufacturing bone graft substitutes is to obtain a scaffold that has sufficient mechanical strength and bioactive properties to promote formation of new tissue. The ability to synthesise hydrogel based composite scaffolds using photopolymerisation has been demonstrated in this study. The prepared hydrogel based composites were characterised using techniques including Fourier Transform Infrared Spectroscopy (FTIR), X-ray diffraction (XRD), scanning electron microscopy (SEM), Energy-dispersive X-ray spectrometry (EDX), rheological studies and compression testing. In addition, gel fraction, differential scanning calorimetry (DSC), thermogravimetric analysis (TGA), porosity and swelling studies of the composites were carried out. It was found that these novel hydrogel bioglass composite formulations did not display the inherent brittleness that is typically associated with bioactive glass based bone graft materials and exhibited enhanced biomechanical properties compared to the polyethylene glycol hydrogel scaffolds along. Together, the combination of enhanced mechanical properties and the deposition of apatite on the surface of these hydrogel based composites make them an ideal candidate as bone graft substitutes in cancellous bone defects or low load bearing applications. Highlights: • Young's modulus increases with the addition of bioactive glasses. • Hydrogel based composites formed an apatite layer in simulated body fluid. • Storage modulus increases with addition of bioactive glasses. • Compressive strength is dependent on molecular weight and bioactive glass loading.

  17. Synthesis and In Vitro Activity Assessment of Novel Silicon Oxycarbide-Based Bioactive Glasses.

    Science.gov (United States)

    Gonzalo-Juan, Isabel; Detsch, Rainer; Mathur, Sanjay; Ionescu, Emanuel; Boccaccini, Aldo R; Riedel, Ralf

    2016-11-24

    Novel bioactive glasses based on a Ca- and Mg-modified silicon oxycarbide (SiCaMgOC) were prepared from a polymeric single-source precursor, and their in vitro activity towards hydroxyapatite mineralization was investigated upon incubating the samples in simulated body fluid (SBF) at 37 °C. The as-prepared materials exhibit an outstanding resistance against devitrification processes and maintain their amorphous nature even after exposure to 1300 °C. The X-ray diffraction (XRD) analysis of the SiCaMgOC samples after the SBF test showed characteristic reflections of apatite after only three days, indicating a promising bioactivity. The release kinetics of the Ca2+ and Mg2+ and the adsorption of H⁺ after immersion of SiCaMgOC in simulated body fluid for different soaking times were analyzed via optical emission spectroscopy. The results show that the mechanism of formation of apatite on the surface of the SiCaMgOC powders is similar to that observed for standard (silicate) bioactive glasses. A preliminary cytotoxicity investigation of the SiOC-based bioactive glasses was performed in the presence of mouse embryonic fibroblasts (MEF) as well as human embryonic kidney cells (HEK-293). Due to their excellent high-temperature crystallization resistance in addition to bioactivity, the Ca- and Mg-modified SiOC glasses presented here might have high potential in applications related to bone repair and regeneration.

  18. Early stage reactivity and in vitro behavior of silica-based bioactive glasses and glass-ceramics.

    Science.gov (United States)

    Verné, E; Bretcanu, O; Balagna, C; Bianchi, C L; Cannas, M; Gatti, S; Vitale-Brovarone, C

    2009-01-01

    The surface reactivity of different sets of glasses and glass-ceramics belonging to the SiO(2)-P(2)O(5)-CaO-MgO-K(2)O-Na(2)O system have been investigated. The attention was focused on the role of their composition on the bioactivity kinetics, in terms of pH modifications, silica-gel formation and its evolution toward hydroxycarbonatoapatite, after different times of soaking in simulated body fluid. Glasses and glass ceramics have been characterized by thermal analysis, SEM-EDS observations and phase analysis (XRD). XPS measurements have been carried out on the most representative set of sample in order to evaluate the evolution of the surface species during the growth of silica-gel and hydroxycarbonatoapatite. The response of murine fibroblast 3T3 to the material before and after a conditioning pre-treatment (immersion in SBF) has been investigated on the same set of samples in order to point out the role of the bioactivity mechanism on cell viability. The main differences among the various glasses have been related to the modifier oxides ratio and to the MgO content, which seems to have an influence on the glass stability, both in terms of thermal properties and surface reactivity. The surface characterization and in vitro tests revealed few variations in the reactivity of the different glasses and glass-ceramics in their pristine form. On the contrary, the different surface properties before and after the pre-treatment in SBF seem to play a role on the biocompatibility of both glass and glass-ceramics, due to the different ion release and hydrophilicity of the surfaces, affecting both cell viability and protein adsorption.

  19. In vitro bioactivity of glass-ceramic/fibroin composites

    Directory of Open Access Journals (Sweden)

    Lachezar Radev

    2017-06-01

    Full Text Available Bioactive composite materials were prepared by mixing 20 wt.% of silk fibroin (SF and 80 wt.% of glassceramics from CaO-SiO2-P2O5-MgO system. In vitro bioactivity of the prepared composites was evaluated in 1.5 simulated body fluid (1.5 SBF in static conditions. The obtained samples before and after in vitro tests were characterized by X-ray diffraction (XRD analysis, Fourier transform infrared spectroscopy (FTIR, and X-ray photoelectron spectroscopy (XPS. The changes in 1.5 SBF solutions after soaking the samples were evaluated by inductively coupled plasma atomic emission spectroscopy (ICP-AES. MG63 osteosarcoma cells were used for the biological experiments. The obtained experimental data proved that the synthesized composites exhibit excellent in vitro bioactivity.

  20. Role of SrO on the bioactivity behavior of some ternary borate glasses and their glass ceramic derivatives.

    Science.gov (United States)

    Abdelghany, A M; Ouis, M A; Azooz, M A; ElBatal, H A; El-Bassyouni, G T

    2016-01-05

    Borate glasses containing SrO substituting both CaO and NaO were prepared and characterized for their bioactivity or bone bonding ability. Glass ceramic derivatives were prepared by thermal heat treatment process. FTIR, XRD and SEM measurements for the prepared glass and glass-ceramics before and after immersion in sodium phosphate solution for one and two weeks were carried out. The appearance of two IR peaks within the range 550-680cm(-1) after immersion in phosphate solution indicates the formation of hydroxyapatite or equivalent Sr phosphate layer. X-ray diffraction data agree with the FTIR spectral analysis. The solubility test was carried out for both glasses and glass ceramics derivatives in the same phosphate solution. The introduction of SrO increases the solubility for both glasses and glass ceramics and this is assumed to be due to the formation of Sr phosphate which is more soluble than calcium phosphate (hydroxyapatite). SEM images reveal varying changes in the surfaces of glass ceramics after immersion according to the SrO content. Copyright © 2015 Elsevier B.V. All rights reserved.

  1. In vitro study of nano-sized zinc doped bioactive glass

    Energy Technology Data Exchange (ETDEWEB)

    Goh, Yi-Fan; Alshemary, Ammar Z.; Akram, Muhammad [Department of Chemistry, Faculty of Science, Universiti Teknologi Malaysia, 81310 UTM skudai, Johor Darul Ta' zim (Malaysia); Abdul Kadir, Mohammed Rafiq [Medical Implant Technology Group, Faculty of Biomedical Engineering and Health Science, Universiti Teknologi Malaysia, 81310 UTMJohor Bahru (Malaysia); Hussain, Rafaqat, E-mail: rafaqat@kimia.fs.utm.my [IbnuSina Institute for Fundamental Science Studies, Universiti Teknologi Malaysia, 81310 UTM Johor Bahru, Johor DarulTa' zim (Malaysia)

    2013-01-15

    Surface reactivity in physiological fluid has been linked to bioactivity of a material. Past research has shown that bioactive glass containing zinc has the potential in bone regeneration field due to its enhanced bioactivity. However, results from literature are always contradictory. Therefore, in this study, surface reactivity of bioactive glass containing zinc was evaluated through the study of morphology and composition of apatite layer formed after immersion in simulated body fluid (SBF). Nano-sized bioactive glass with 5 and 10 mol% zinc were synthesized through quick alkali sol-gel method. The synthesized Zn-bioglass was characterized using field emission scanning electron microscope (FESEM), energy dispersive X-ray spectrometer (EDX), X-ray diffractometer (XRD) and Fourier transform infrared spectrometer (FTIR). Samples after SBF immersion were characterized using scanning electron microscope (SEM) and EDX. Morphological study through SEM showed the formation of spherical apatite particles with Ca/P ratio closer to 1.67 on the surface of 5 mol% Zn-bioglass. Whereas, the 10 mol% Zn-bioglass samples induced the formation of flake-like structure of calcite in addition to the spherical apatite particles with much higher Ca/P ratio. Our results suggest that the higher Zn content increases the bioactivity through the formation of bone-bonding calcite as well as the spherical apatite particles. -- Highlights: Black-Right-Pointing-Pointer Nano-sized bioactive glasses were synthesized through quick alkali sol-gel method. Black-Right-Pointing-Pointer 5 and 10 mol% Zn-bioglass induced the formation of spherical particles in SBF test. Black-Right-Pointing-Pointer 10 mol% Zn-bioglass also induced the formation of flake-like structure. Black-Right-Pointing-Pointer The flake-like structure is calcium carbonate; spherical particles are apatite. Black-Right-Pointing-Pointer High Zn contents negatively influence the chemical composition of the apatite layer.

  2. Exploiting Bisphosphonate-Bioactive-Glass Interactions for the Development of Self-Healing and Bioactive Composite Hydrogels.

    Science.gov (United States)

    Diba, Mani; An, Jie; Schmidt, Stephan; Hembury, Mathew; Ossipov, Dmitri; Boccaccini, Aldo R; Leeuwenburgh, Sander C G

    2016-12-01

    Hydrogels are widely recognized as promising candidates for various biomedical applications, such as tissue engineering. Recently, extensive research efforts have been devoted to the improvement of the biological and mechanical performance of hydrogel systems by incorporation of functional groups and/or inorganic particles in their composition. Bisphosphonates are a class of drugs, commonly used for treatment of osteoporosis, which exhibit a strong binding affinity for hydroxyapatite. In this study, the binding affinity of a bisphosphonate-functionalized polymer, hyaluronan, toward a bioactive glass (i.e., 45S5 Bioglass) is evaluated using force-distance measurements with atomic force microscopy. The strong interaction between bisphosphonate and bioactive glass is then exploited to develop organic-inorganic composite hydrogels and the viscoelastic and self-healing ability of these materials are investigated. Finally, the stability and mineralization behavior of these hydrogels are evaluated in simulated body fluid. Following this approach, injectable, bioactive and self-healing organic-inorganic composite hydrogels are produced, which mineralize abundantly and rapidly in simulated body fluid. These properties render these composite gels suitable for applications in bone-tissue engineering. © 2016 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

  3. Laser sintering of nano 13-93 glass scaffolds: Microstructure, mechanical properties and bioactivity

    Directory of Open Access Journals (Sweden)

    Cao Y.

    2015-01-01

    Full Text Available As the only bioactive material that can bond with both hard tissues and soft tissues, bioactive glass has become much important in the field of tissue engineering. 13-93 bioactive glass scaffolds were fabricated via selective laser sintering (SLS. It was focused on the effects of laser sintering on microstructure and mechanical properties of the scaffolds. The experimental results showed that the sintered layer gradually became dense with the laser power increasing and then some defects occurred, such as macroscopic caves. The optimum compressive strength and fracture toughness were 21.43±0.87 MPa and 1.14±0.09 MPa.m1/2, respectively. In vitro bioactivity showed that there was the bone-like apatite layer on the surface of the scaffolds after soaking in simulated body fluid (SBF, which was further evaluated by Fourier transform infrared spectroscopy (FTIR. Moreover, cell culture study showed MG-63 cells adhered and spread well on the scaffolds, and proliferated with increasing time in cell culture. These indicated excellent bioactivity and biocompatibility of nano 13-93 glass scaffolds.

  4. Quenched/unquenched nano bioactive glass-ceramics: Synthesis and in vitro bioactivity evaluation in Ringer’s solution with BSA

    Directory of Open Access Journals (Sweden)

    Nabian Nima

    2013-01-01

    Full Text Available The paper reports the first attempt at changing cooling treatment of synthesizing method in order to investigate its effect on the physical properties of sol-gel derived nano bioactive glass-ceramic in the system 58SiO2-33CaO-9P2O5 (wt.%. We hypothesized that the method of cooling may affect the properties of nano bioactive glass-ceramic. To test this hypothesis, two different method of cooling treatment was applied after calcinations in synthesizing method. Both quenched and unquenched nano bioactive glass-ceramics were soaked in Ringer’s solution with bovine serum albumin (BSA for bioactivity evaluation. The obtained samples were analyzed for their composition, crystalinity and morphology through X-ray powder diffraction (XRD, Fourier transform infrared spectroscopy (FTIR, surface electron microscope (SEM and transmission electron microscope (TEM. The SEM images showed that the morphology of nano bioactive glass-ceramics was completely changed by quenching process. Results of in vitro bioactivity evaluation revealed that the unquenched attains faster apatite formation ability than the quenched sample. Other properties of these two morphologically different nano bioactive glass-ceramics were strongly discussed.

  5. Remineralization efficiency of bioactive glass on artificially induced carious lesion an in-vitro study

    Directory of Open Access Journals (Sweden)

    Sai Sathya Narayana

    2014-01-01

    Full Text Available Objectives: The objective of this study is to investigate the efficacy of bioactive glass containing product on remineralization of artificial induced carious enamel lesion and to compare its efficiency with other remineralization products using an in-vitro pH cycling method. The null hypothesis tested was bioactive glass has no effect on enamel remineralization. Materials and Methods: A total of 20 enamel samples of human molar teeth were subjected to artificial caries lesion formation using pH cycling method and was verified using high resolution scanning electron microscope (HRSEM. Each demineralized sample was then divided into five test groups each containing twenty. Group A - Bioactive glass (SHY-NM, Group B - Fluoride tooth paste (Amflor, Group C - CPP-ACP (Tooth mousse, Group D - CPP-ACPF (Tooth mousse plus, Group E - control. All the test groups were exposed to the pH cycling regime, the remineralizing agents were applied for 10 min except control. After 10 days period, the entire test groups were evaluated with HRSEM and quantitative assessment by energy dispersive X-ray spectroscopy. The obtained data was analyzed statistically using one-way ANOVA, Student′s t-test and Tukey′s multiple comparison tests. P ≤ 0.05 was considered to be significant. Results: Rejection of the null hypothesis and highlights the concept of biomimetic bioactive glass as an effective remineralizing agent. Clinical Relevance: To focus on the importance of minimal invasive treatment on incipient carious lesion by remineralization.

  6. Comparison of three methods in evaluation of bone ingrowth into porous bioactive glass and titanium implants

    Energy Technology Data Exchange (ETDEWEB)

    Ylaenen, H.O.; Ekholm, C.; Karlsson, K.H. [Abo Akademi Univ. (Finland). Process Chemistry Group; Beliaev, N. [Turku Univ. (Finland). Biomaterials Project; Aro, H.T. [Turku Univ. (Finland). Dept. of Surgery

    2001-07-01

    The current study compared two standard methods of color based histomorphometry and image analysis of BEI-SEM to EDXA based mineral analysis combined with microanalysis of X-ray maps of selected elements in measurement of bone ingrowth to porous bioactive glass and titanium implants. The analysis was performed on the implants after 6 and/or 12 weeks in rabbit femur. In titanium implants, EDXA and BEI-SEM gave highly comparable results after the BEI-SEM data was corrected for false pixels at metal-soft tissue interfaces. In bioactive glass implants, uncorrected BEI-SEM showed higher bone values than EDXA at early stages of bioactive glass incorporation, histomorphometry and corrected BEI-SEM showed lower values than the two other methods. Both EDXA and corrected BEI-SEM are suitable for measurement of bone ingrowth in porous titanium implants. EDXA-based mineral analysis seems to be the method of choice in measurement of osteogenesis into porous bioactive glass implants. Histomorphometry remains as the only method or evaluation of fibrous tissue ingrowth. (orig.)

  7. Role of cellulose functionality in bio-inspired synthesis of nano bioactive glass.

    Science.gov (United States)

    Gupta, Nidhi; Santhiya, Deenan

    2017-06-01

    In search of abundant cheaper natural polymer for bio-inspired bioactive glass nanoparticles synthesis, cellulose and its derivatives have been considered as a template. Different templates explored in the present studies are pure cellulose, methyl cellulose and amine grafted cellulose. To the best of our knowledge, for the first time of the considered templates, pure cellulose and amine grafted cellulose results in in situ nano particulate composite formation while interestingly methyl cellulose proves to be an excellent sacrificial template for the synthesis of uniform bioglass nanoparticles of diameter in the range of 55nm. Further, viscoelastic measurements were carried out using dynamic mechanical analyzer. Herein, an attempt has been made to establish structure-mechanical relationship based on the templates. Moreover, in vitro bioactivity is also observed to be affected by the nature of the template molecule used for the synthesis of bioactive glass. Copyright © 2017 Elsevier B.V. All rights reserved.

  8. Bioactive type glass-ceramics within incorporated aluminium; Vitroceramicos del tipo bioactivo con aluminio incorporado

    Energy Technology Data Exchange (ETDEWEB)

    Volzone, C.; Stabile, F.M.; Ortiga, J., E-mail: volzcris@netverk.com.ar [Centro de Tecnologia de Recursos Minerales y Ceramica (CETMIC), Buenos Aires (Argentina)

    2012-07-01

    Bioactive glass-ceramics are used as biomaterials for the reparation of bone tissue. They are prepared, generally, by bioglass of specific composition for each particular use. The aluminium addition in the formulation at very small quantities influences on the structural properties. Two glass-ceramics obtained by P{sub 2}O{sub 5}-Na{sub 2}O-CaO-SiO{sub 2} formulation within aluminium (0.5 % in Al{sub 2}O{sub 3} base) added through a reactive alumina and purified feldspar were analyzed. The results showed structural differences between both glass-ceramics. (author)

  9. Bioactive glass induced in vitro apatite formation on composite GBR membranes.

    Science.gov (United States)

    Tirri, Teemu; Rich, Jaana; Wolke, Joop; Seppälä, Jukka; Yli-Urpo, Antti; Närhi, Timo O

    2008-08-01

    The aim of this study was to investigate in vitro bioactivity of different thermoplastic biodegradable barrier membranes. Three experimental GBR membranes were fabricated using Poly(epsilon-caprolactone-co-D: ,L-lactide) P(CL/DL-LA) and particulate bioactive glass S53P4 (BAG; granule size 90-315 microm): (A) composite membrane with 60-wt.% of BAG, (B) membrane coated with BAG; and (C) copolymer membrane without BAG. Membranes were immersed in simulated body fluid (SBF), and their surfaces were characterized with SEM, XRD and EDS after 6 and 12 h and after 1, 3, 5, 7, and 14 days. Calcium phosphate (Ca-P) surface formation was observed on both composite membranes (A and B) but not on the copolymer membrane without bioactive glass (C). The Ca-P precipitation appeared to be initiated on the bioactive glass followed by growth of the layer along the polymer surface. In 6-12 h ion dissolution of the bioactive glass led to formation of the silica rich layer on the surface of the exposed glass granules on composite membrane B whereas only small amounts of silica was observed on the polymer surface of the composite membrane A. At 24 h nucleation of Ca-P precipitation was observed, and by 3-5 days membrane surface was covered with a uniform Ca-P layer transforming from amorphous to low crystalline structure. At 7 days composition and structure of the apatite surface resembled the apatite in bone. Once nucleated, the surface topography seemed to have significant effect on the growth of the apatite layer.

  10. Cerium, gallium and zinc containing mesoporous bioactive glass coating deposited on titanium alloy

    Energy Technology Data Exchange (ETDEWEB)

    Shruti, S., E-mail: biotech.shruti@gmail.com; Andreatta, F.; Furlani, E.; Marin, E.; Maschio, S.; Fedrizzi, L.

    2016-08-15

    Highlights: • Mesoporous bioactive glass substituted with Ce, Ga or Zn coated on Ti6Al4 V alloy. • Ce, Ga and Zn play vital role in bone metabolism. • Coating was homogenous and crack free retaining the characteristics of glass samples. • Apatite layer formed on unsubstituted, Ce and Ga substituted samples by 15 d. • Zn substituted samples lack apatite layer formation ability. - Abstract: Surface modification is one of the methods for improving the performance of medical implants in biological environment. In this study, cerium, gallium and zinc substituted 80%SiO{sub 2}-15%CaO-5%P{sub 2}O{sub 5} mesoporous bioactive glass (MBG) in combination with polycaprolactone (PCL) were coated over Ti6Al4 V substrates by dip-coating method in order to obtain an inorganic—organic hybrid coating (MBG-PCL). Structural characterization was performed using XRD, nitrogen adsorption, SEM-EDXS, FTIR. The MBG-PCL coating uniformly covered the substrate with the thickness found to be more than 1 μm. Glass and polymer phases were detected in the coating along with the presence of biologically potent elements cerium, gallium and zinc. In addition, in vitro bioactivity was investigated by soaking the coated samples in simulated body fluid (SBF) for up to 30 days at 37 °C. The apatite-like layer was monitored by FTIR, SEM-EDXS and ICP measurements and it formed in all the samples within 15 days except zinc samples. In this way, an attempt was made to develop a new biomaterial with improved in vitro bioactive response due to bioactive glass coating and good mechanical strength of Ti6Al4 V alloy along with inherent biological properties of cerium, gallium and zinc.

  11. Antibacterial effect of bioactive glass nanoparticles prepared via sol gel method

    Directory of Open Access Journals (Sweden)

    Zahra Nazemi

    2014-10-01

    Full Text Available Background: Infection constitutes the most important complication caused by biomaterials. Bioactive glasses have properties such as osteoconductivity and good restorability, some of which have revealed antibacterial effects. Therefore, these biomaterials are appropriate candidates for orthopedic and dental applications. The present study was conducted to analyze the antibacterial effect of bioactive glass nanoparticles. Methods: In this experimental study, 37S and 58S glass compositions were synthesized via sol-gel technique. Characterization techniques such as X-ray diffraction (XRD, scanning electron microscopy (SEM and X-ray fluorescent (XRF were used for the prepared powders. The antibacterial activity of these compounds was studied using Escherichia coli as gram negative and Staphylococcus aureus as gram positive bacteria. The antibacterial effect of samples was evaluated at concentration of 25, 50 and 100 mg/ml. Results: The particle size of the samples was mainly less than 100 nm. The 37S glass showed the highest antibacterial activity and the minimum bactericidal (MBC at 25 mg/ml concentration against both bacteria. At broth concentrations below 100 mg/ml, 58S showed no antibacterial activity; however, it completely eliminated Escherichia bacteria and reduced the growth of Staphylococcus aureus bacteria. Conclusion: These bioactive glass nanopowders can be regarded as good candidates in orthopedic application for the treatment of bone and dental defects but need supplementary and more evaluation considering their antibacterial effect on two important bacteria.

  12. Bioactive and Antibacterial Glass Powders Doped with Copper by Ion-Exchange in Aqueous Solutions

    Directory of Open Access Journals (Sweden)

    Marta Miola

    2016-05-01

    Full Text Available In this work, two bioactive glass powders (SBA2 and SBA3 were doped with Cu by means of the ion-exchange technique in aqueous solution. SBA2 glass was subjected to the ion-exchange process by using different Cu salts (copper(II nitrate, chloride, acetate, and sulphate and concentrations. Structural (X-ray diffraction-XRD, morphological (Scanning Electron Microscopy-SEM, and compositional (Energy Dispersion Spectrometry-EDS analyses evidenced the formation of crystalline phases for glasses ion-exchanged in copper(II nitrate and chloride solutions; while the ion-exchange in copper(II acetate solutions lead to the incorporation of higher Cu amount than the ion-exchange in copper(II sulphate solutions. For this reason, the antibacterial test (inhibition halo towards S. aureus was performed on SBA2 powders ion-exchanged in copper(II acetate solutions and evidenced a limited antibacterial effect. A second glass composition (SBA3 was developed to allow a greater incorporation of Cu in the glass surface; SBA3 powders were ion-exchanged in copper(II acetate solutions (0.01 M and 0.05 M. Cu-doped SBA3 powders showed an amorphous structure; morphological analysis evidenced a rougher surface for Cu-doped powders in comparison to the undoped glass. EDS and X-ray photoelectron spectroscopy (XPS confirmed the Cu introduction as Cu(II ions. Bioactivity test in simulated body fluid (SBF showed that Cu introduction did not alter the bioactive behaviour of the glass. Finally, inhibition halo test towards S. aureus evidenced a good antimicrobial effect for glass powders ion-exchanged in copper(II acetate solutions 0.05 M.

  13. A new sol-gel process for producing Na(2)O-containing bioactive glass ceramics.

    Science.gov (United States)

    Chen, Qi-Zhi; Li, Yuan; Jin, Li-Yu; Quinn, Julian M W; Komesaroff, Paul A

    2010-10-01

    The sol-gel process of producing SiO(2)-CaO bioactive glasses is well established, but problems remain with the poor mechanical properties of the amorphous form and the bioinertness of its crystalline counterpart. These properties may be improved by incorporating Na(2)O into bioactive glasses, which can result in the formation of a hard yet biodegradable crystalline phase from bioactive glasses when sintered. However, production of Na(2)O-containing bioactive glasses by sol-gel methods has proved to be difficult. This work reports a new sol-gel process for the production of Na(2)O-containing bioactive glass ceramics, potentially enabling their use as medical implantation materials. Fine powders of 45S5 (a Na(2)O-containing composition) glass ceramic have for the first time been successfully synthesized using the sol-gel technique in aqueous solution under ambient conditions, with the mean particle size being approximately 5 microm. A comparative study of sol-gel derived S70C30 (a Na(2)O-free composition) and 45S5 glass ceramic materials revealed that the latter possesses a number of features desirable in biomaterials used for bone tissue engineering, including (i) the crystalline phase Na(2)Ca(2)Si(3)O(9) that couples good mechanical strength with satisfactory biodegradability, (ii) formation of hydroxyapatite, which may promote good bone bonding and (iii) cytocompatibility. In contrast, the sol-gel derived S70C30 glass ceramic consisted of a virtually inert crystalline phase CaSiO(3). Moreover, amorphous S70C30 largely transited to CaCO(3) with minor hydroxyapatite when immersed in simulated body fluid under standard tissue culture conditions. In conclusion, sol-gel derived Na(2)O-containing glass ceramics have significant advantages over related Na(2)O-free materials, having a greatly improved combination of mechanical capability and biological absorbability. 2010 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

  14. Designing antimicrobial bioactive glass materials with embedded metal ions synthesized by the sol–gel method

    Energy Technology Data Exchange (ETDEWEB)

    Palza, Humberto, E-mail: hpalza@ing.uchile.cl [Departamento de Ingeniería Química y Biotecnología, Facultad de Ciencias Físicas y Matemáticas, Universidad de Chile, Santiago (Chile); Escobar, Blanca; Bejarano, Julian [Departamento de Ingeniería Química y Biotecnología, Facultad de Ciencias Físicas y Matemáticas, Universidad de Chile, Santiago (Chile); Bravo, Denisse [Departamento de Patología, Facultad de Odontología, Universidad de Chile, Santiago (Chile); Diaz-Dosque, Mario [Departamento de Ciencias Básicas y Comunitarias, Facultad de Odontología, Universidad de Chile, Santiago (Chile); Perez, Javier [Departamento de Ingeniería Química y Biotecnología, Facultad de Ciencias Físicas y Matemáticas, Universidad de Chile, Santiago (Chile)

    2013-10-15

    Bioactive glasses (SiO{sub 2}–P{sub 2}O{sub 5}–CaO) having tailored concentrations of different biocide metal ions (copper or silver) were produced by the sol–gel method. All the particles release phosphorous ions when immersed in water and simulated body fluid (SBF). Moreover, a surface layer of polycrystalline hydroxy-carbonate apatite was formed on the particle surfaces after 10 day immersion in SBF as confirmed by X-ray diffraction and scanning electron microscopy (SEM) showing the bioactive materials. Samples with embedded either copper or silver ions were able to further release the biocide ions with a release rate that depends on the metal embedded and the dissolution medium: water or SBF. This biocide ion release from the samples explains the antimicrobial effect of our active particles against Escherichia coli DH5α ampicillin-resistant (Gram-negative) and Streptococcus mutans (Gram-positive) as determined by the Minimum Bactericidal Concentration (MBC) method. The antimicrobial behavior of the particles depends on the bacteria and the biocide ion used. Noteworthy, although samples with copper are able to release more metal ion than samples with silver, they present higher MBC showing the high effect of silver against these bacteria. - Highlights: • Copper and silver act as antimicrobial additives in bioactive glass materials. • Silver is more toxic than copper ions in these bioactive materials. • Sol–gel method allows the synthesis of antimicrobial bioactive materials.

  15. New bioactive glass-ceramic: synthesis and application in PMMA bone cement composites.

    Science.gov (United States)

    Abd Samad, Hamizah; Jaafar, Mariatti; Othman, Radzali; Kawashita, Masakazu; Abdul Razak, Noor Hayati

    2011-01-01

    In present study, a new composition of glass-ceramic was synthesized based on the Na2O-CaO-SiO2-P2O5 glass system. Heat treatment of glass powder was carried out in 2 stages: 600 °C as the nucleation temperature and different temperature on crystallization at 850, 950 and 1000 °C. The glass-ceramic heat-treated at 950 °C was selected as bioactive filler in commercial PMMA bone cement; (PALACOS® LV) due to its ability to form 2 high crystallization phases in comparison with 850 and 1000 °C. The results of this newly glass-ceramic filled PMMA bone cement at 0-16 wt% of filler loading were compared with those of hydroxyapatite (HA). The effect of different filler loading on the setting properties was evaluated. The peak temperature during the polymerization of bone cement decreased when the liquid to powder (L/P) ratio was reduced. The setting time, however, did not show any trend when filler loading was increased. In contrast, dough time was observed to decrease with increased filler loading. Apatite morphology was observed on the surface of the glass-ceramic and selected cement after bioactivity test.

  16. TRIS buffer in simulated body fluid distorts the assessment of glass-ceramic scaffold bioactivity.

    Science.gov (United States)

    Rohanová, Dana; Boccaccini, Aldo Roberto; Yunos, Darmawati Mohamad; Horkavcová, Diana; Březovská, Iva; Helebrant, Aleš

    2011-06-01

    The paper deals with the characterisation of the bioactive phenomena of glass-ceramic scaffold derived from Bioglass® (containing 77 wt.% of crystalline phases Na(2)O·2CaO·3SiO(2) and CaO·SiO(2) and 23 wt.% of residual glass phase) using simulated body fluid (SBF) buffered with tris-(hydroxymethyl) aminomethane (TRIS). A significant effect of the TRIS buffer on glass-ceramic scaffold dissolution in SBF was detected. To better understand the influence of the buffer, the glass-ceramic scaffold was exposed to a series of in vitro tests using different media as follows: (i) a fresh liquid flow of SBF containing tris (hydroxymethyl) aminomethane; (ii) SBF solution without TRIS buffer; (iii) TRIS buffer alone; and (iv) demineralised water. The in vitro tests were provided under static and dynamic arrangements. SBF buffered with TRIS dissolved both the crystalline and residual glass phases of the scaffold and a crystalline form of hydroxyapatite (HAp) developed on the scaffold surface. In contrast, when TRIS buffer was not present in the solutions only the residual glassy phase dissolved and an amorphous calcium phosphate (Ca-P) phase formed on the scaffold surface. It was confirmed that the TRIS buffer primarily dissolved the crystalline phase of the glass-ceramic, doubled the dissolving rate of the scaffold and moreover supported the formation of crystalline HAp. This significant effect of the buffer TRIS on bioactive glass-ceramic scaffold degradation in SBF has not been demonstrated previously and should be considered when analysing the results of SBF immersion bioactivity tests of such systems. Copyright © 2011 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

  17. Combined PIXE and SEM study of the behaviour of trace elements in gel formed around implant coated with bioactive glass

    Science.gov (United States)

    Oudadesse, H.; Irigaray, J. L.; Barbotteau, Y.; Brun, V.; Moretto, Ph.

    2002-05-01

    Bioactive glasses are used as coating biomaterials to facilitate anchorage of metallic prostheses implanted into the body. The aim of this work is to study the behavior of gel formed in contact with alloys and BVA and BVH bioactive glasses implanted. Cylinders of metallic implants composed by Ti, Al and V, are coated with bioactive glass. Three sheep were implanted for different time length: 3, 6 and 12 months in the femoral epiphysis. Results obtained with particle induced X-ray emission and scanning electron microscopy show that BVA coating induces a better contact between the metallic implant and bone. On the other hand, BVH coating prevents corrosion from the metallic implant.

  18. The Fabrication and Characterization of PCL/Rice Husk Derived Bioactive Glass-Ceramic Composite Scaffolds

    OpenAIRE

    Farnaz Naghizadeh; Naznin Sultana; Mohammed Rafiq Abdul Kadir; Tengku Muzaffar Tengku Md Shihabudin; Rafaqat Hussain; Tunku Kamarul

    2014-01-01

    The present study was conducted to fabricate a 3D scaffold using polycaprolactone (PCL) and silicate based bioactive glass-ceramic (R-SBgC). Different concentrations of R-SBgC prepared from rice husk ash (RHA) were combined with PCL to fabricate a composite scaffold using thermally induced phase separation (TIPS) method. The products were then characterized using SEM and EDX. The results demonstrated that R-SBgC in PCL matrix produced a bioactive material which has highly porous structure wit...

  19. Preparation, in vitro mineralization and osteoblast cell response of electrospun 13-93 bioactive glass nanofibers.

    Science.gov (United States)

    Deliormanlı, Aylin M

    2015-08-01

    In this study, silicate based 13-93 bioactive glass fibers were prepared through sol-gel processing and electrospinning technique. A precursor solution containing poly (vinyl alcohol) and bioactive glass sol was used to produce fibers. The mixture was electrospun at a voltage of 20 kV by maintaining tip to a collector distance of 10 cm. The amorphous glass fibers with an average diameter of 464±95 nm were successfully obtained after calcination at 625 °C. Hydroxyapatite formation on calcined 13-93 fibers was investigated in simulated body fluid (SBF) using two different fiber concentrations (0.5 and 1 mg/ml) at 37 °C. When immersed in SBF, conversion to a calcium phosphate material showed a strong dependence on the fiber concentration. At 1mg/ml, the surface of the fibers converted to the hydroxyapatite-like material in SBF only after 30 days. At lower solid concentrations (0.5 mg/ml), an amorphous calcium phosphate layer formation was observed followed by the conversion to hydroxyapatite phase after 7 days of immersion. The XTT (2,3-Bis-(2-Methoxy-4-Nitro-5-Sulfophenyl)-2H-Tetrazolium-5-Carboxanilide) assay was conducted to evaluate the osteoblast cell response to the bioactive glass fibers. Copyright © 2015 Elsevier B.V. All rights reserved.

  20. ZK30-bioactive glass composites for orthopedic applications: A comparative study on fabrication method and characteristics

    Energy Technology Data Exchange (ETDEWEB)

    Huan, Z.G.; Leeflang, M.A. [Department of Biomechanical Engineering, Delft University of Technology, Mekelweg 2, 2628 CD Delft (Netherlands); Zhou, J., E-mail: j.zhou@tudelft.nl [Department of Biomechanical Engineering, Delft University of Technology, Mekelweg 2, 2628 CD Delft (Netherlands); Duszczyk, J. [Department of Biomechanical Engineering, Delft University of Technology, Mekelweg 2, 2628 CD Delft (Netherlands)

    2011-12-15

    Highlights: Black-Right-Pointing-Pointer Biodegradable Mg-bioglass composites were made using casting; powder metallurgy. Black-Right-Pointing-Pointer Bioglass powder retained its composition and morphology. Black-Right-Pointing-Pointer Accelerated deposition of Ca; P ions on composites occurred due to bioglass. Black-Right-Pointing-Pointer Mg-bioglass composites made from powders had reduced degradation rates. Black-Right-Pointing-Pointer Powder metallurgy appeared to be better for making biodegradable composites. - Abstract: Previous in vivo studies on biodegradable magnesium alloys for orthopedic implant applications showed the need to improve early-stage bioactivity. Introducing bioactive particles into a magnesium alloy to form a metal matrix composite (MMC) represents an effective way to enhance the bioactivity of the alloy. In this study, composites with the ZK30 alloy as the matrix and the 45S5 bioactive glass (BG) as the reinforcement phase were fabricated using a semi-solid casting (SSC) method and a powder metallurgy (P/M) method. The SSC and P/M biocomposites with the same weight percents of bioactive glass particles were compared. Optical microscopy showed homogeneously dispered BG particles in the SSC and P/M composites. SEM and EDX analyses confirmed the retention of the morphological characteristics and composition of BG particles in the composites. However, the SSC composites exhibited micro-porous structures, while the P/M composites had nearly fully densified structures. As compared with the ZK30 matrix, the SSC composites exhibited significantly higher degradation rates, while the P/M composites possessed lower degradation rates. On the surface of all the composites, accelerated deposition of Ca and P ions occurred during immersion in the cell culture medium, indicating an improved surface bioactivity of the composites. The P/M method was found to be advantageous over the SSC method and could yield magnesium-matrix composites with enhanced

  1. A review of the biological response to ionic dissolution products from bioactive glasses and glass-ceramics.

    Science.gov (United States)

    Hoppe, Alexander; Güldal, Nusret S; Boccaccini, Aldo R

    2011-04-01

    Several inorganic materials such as special compositions of silicate glasses, glass-ceramics and calcium phosphates have been shown to be bioactive and resorbable and to exhibit appropriate mechanical properties which make them suitable for bone tissue engineering applications. However, the exact mechanism of interaction between the ionic dissolution products of such inorganic materials and human cells are not fully understood, which has prompted considerable research work in the biomaterials community during the last decade. This review comprehensively covers literature reports which have investigated specifically the effect of dissolution products of silicate bioactive glasses and glass-ceramics in relation to osteogenesis and angiogenesis. Particularly, recent advances made in fabricating dense biomaterials and scaffolds doped with trace elements (e.g. Zn, Sr, Mg, and Cu) and investigations on the effect of these elements on the scaffold biological performance are summarized and discussed in detail. Clearly, the biological response to artificial materials depends on many parameters such as chemical composition, topography, porosity and grain size. This review, however, focuses only on the ion release kinetics of the materials and the specific effect of the released ionic dissolution products on human cell behaviour, providing also a scope for future investigations and identifying specific research needs to advance the field. The biological performance of pure and doped silicate glasses, phosphate based glasses with novel specific compositions as well as several other silicate based compounds are discussed in detail. Cells investigated in the reviewed articles include human osteoblastic and osteoclastic cells as well as endothelial cells and stem cells. Copyright © 2011 Elsevier Ltd. All rights reserved.

  2. [Effects of bioactive glass on reducing the hypersensitivity after full crown preparation].

    Science.gov (United States)

    Li, H; Liu, Y H; Luo, Z Q

    2017-08-18

    To evaluate the efficacy of the 45S5 bioactive glass on the reduction of hypersensitivity of teeth prepared for full coverage crowns. In the study, 31 prepared abutment teeth with vital pulp from 18 patients satisfied the inclusion criteria and exclusion criteria. The patients were informed consent and recruited into the study. This was a before and after self-control, single blind clinical trial. The severity of tooth hypersensitivity at baseline was evaluated, after application of the placebo, which was the powder of zinc oxide, and after application of the 45S5 bioactive glass on the same tooth. Tooth hypersensitivity was evaluated by Yeaple probe and visual analogue scale (VAS) when the tooth was stimulated by a fixed value of mechanical pressure and a blast of cold air respectively. And the dentist gave the subjective score, and the Schiff score at the same time. The three methods of measurement were repeated at baseline, after application of placebo and after application of the powder of 45S5 bioactive glass. Student's t test and nonparametric test were used for statistical analysis. The indexes measured at baseline, after the application of the placebo and after the application of the 45S5 bioactive glass were as follows, respectively: Tactile value (29.03±9.44) g, (29.68±9.48) g and (44.19±11.19) g, VAS value (50.79±22.92) mm, (46.63±22.06) mm and (30.90±20.30) mm, Schiff score 2.13±0.67, 1.97±0.66 and 1.42±0.56. After the application of bioactive glass, the values of Tactile, the VAS, and the Schiff score were statistically different from those at baseline or after application of the placebo (P0.05). Statistical differences between the Schiff scores of the groups were associated with gender, tooth position, primary or secondary tooth preparation. RESULTS of the clinical trial showed that the powders of 45S5 bioactive glass were significantly effective on reducing the hypersensitivity of teeth with vital pulp after the full crown preparation.

  3. Biomimetic formation of apatite on the surface of porous gelatin/bioactive glass nanocomposite scaffolds

    Energy Technology Data Exchange (ETDEWEB)

    Mozafari, Masoud, E-mail: mmozafari@aut.ac.ir [Biomaterials Group, Faculty of Biomedical Engineering (Center of Excellence), Amirkabir University of Technology, PO Box 15875-4413, Tehran (Iran, Islamic Republic of); Rabiee, Mohammad; Azami, Mahmoud; Maleknia, Saied [Biomaterials Group, Faculty of Biomedical Engineering (Center of Excellence), Amirkabir University of Technology, PO Box 15875-4413, Tehran (Iran, Islamic Republic of)

    2010-12-15

    There have been several attempts to combine bioactive glasses (BaGs) with biodegradable polymers to create a scaffold material with excellent biocompatibility, bioactivity, biodegradability and toughness. In the present study, the nanocomposite scaffolds with compositions based on gelatin (Gel) and BaG nanoparticles in the ternary SiO{sub 2}-CaO-P{sub 2}O{sub 5} system were prepared. In vitro evaluations of the nanocomposite scaffolds were performed, and for investigating their bioactive capacity these scaffolds were soaked in a simulated body fluid (SBF) at different time intervals. The scaffolds showed significant enhancement in bioactivity within few days of immersion in SBF solution. The apatite formation at the surface of the nanocomposite samples confirmed by Fourier transform infrared spectroscopy (FTIR), scanning electron microscopy (SEM), energy dispersive X-ray spectroscopy (EDX) and X-ray powder diffraction (XRD) analyses. In vitro experiments with osteoblast cells indicated an appropriate penetration of the cells into the scaffold's pores, and also the continuous increase in cell aggregation on the bioactive scaffolds with increase in the incubation time demonstrated the ability of the scaffolds to support cell growth. The SEM observations revealed that the prepared scaffolds were porous with three dimensional (3D) and interconnected microstructure, pore size was 200-500 {mu}m and the porosity was 72-86%. The nanocomposite scaffold made from Gel and BaG nanoparticles could be considered as a highly bioactive and potential bone tissue engineering implant.

  4. Titanium addition influences antibacterial activity of bioactive glass coatings on metallic implants.

    Science.gov (United States)

    Rodriguez, Omar; Stone, Wendy; Schemitsch, Emil H; Zalzal, Paul; Waldman, Stephen; Papini, Marcello; Towler, Mark R

    2017-10-01

    In an attempt to combat the possibility of bacterial infection and insufficient bone growth around metallic, surgical implants, bioactive glasses may be employed as coatings. In this work, silica-based and borate-based glass series were synthesized for this purpose and subsequently characterized in terms of antibacterial behavior, solubility and cytotoxicity. Borate-based glasses were found to exhibit significantly superior antibacterial properties and increased solubility compared to their silica-based counterparts, with BRT0 and BRT3 (borate-based glasses with 0 and 15 mol% of titanium dioxide incorporated, respectively) outperforming the remainder of the glasses, both borate and silicate based, in these respects. Atomic Absorption Spectroscopy confirmed the release of zinc ions (Zn(2+)), which has been linked to the antibacterial abilities of glasses SRT0, BRT0 and BRT3, with inhibition effectively achieved at concentrations lower than 0.7 ppm. In vitro cytotoxicity studies using MC3T3-E1 osteoblasts confirmed that cell proliferation was affected by all glasses in this study, with decreased proliferation attributed to a faster release of sodium ions over calcium ions in both glass series, factor known to slow cell proliferation in vitro.

  5. Effects of porosity and crystallinity of glass ceramics on the in vivo bioactive response

    Energy Technology Data Exchange (ETDEWEB)

    Xin Renlong [School of Materials Science and Engineering, Chongqing University, Chongqing (China); Zhang Qiyi; Leng Yang [Department of Mechanical Engineering, Hong Kong University of Science and Technology, Hong Kong (China); Chen Jiyong [Engineering Research Center in Biomaterials, Sichuan University, Chengdu (China)], E-mail: rlxin@cqu.edu.cn

    2008-12-15

    Two types of glass ceramics with different porosities and crystallinities were produced by sintering 45S5 Bioglass (registered) particulates. The in vivo bioactive response of the glass ceramics was evaluated by implanting them in rabbit muscle sites. After six weeks implantation, silicon-rich networks were observed on both types of ceramics, but the number of networks was much larger in the poorly crystallized dense ceramics than in the well crystallized porous ones. This indicated that the crystallization of glass ceramics retarded the formation of networks on surfaces. Apatite precipitation was found in pore areas of the porous ceramics, but not on the dense ones, suggesting that porosity was necessary for glass ceramics to induce apatite precipitation in a rabbit model. (communication)

  6. Effect of Ti(+4) on in vitro bioactivity and antibacterial activity of silicate glass-ceramics.

    Science.gov (United States)

    Riaz, Madeeha; Zia, Rehana; Saleemi, Farhat; Hussain, Tousif; Bashir, Farooq; Ikhram, Hafeez

    2016-12-01

    A novel glass-ceramic series in (48-x) SiO2-36 CaO-4 P2O5-12 Na2O-xTiO2 (where x=0, 3.5, 7, 10.5 and 14mol %) system was synthesized by crystallization of glass powders, obtained by melt quenching technique. The differential scanning calorimetric analysis (DSC) was used to study the non-isothermal crystallization kinetics of the as prepared glasses. The crystallization behaviour of glasses was analyzed under non-isothermal conditions, and qualitative phase analysis of glass-ceramics was made by X-ray diffraction. The in vitro bioactivity of synthesized glass-ceramics was studied in stimulated body fluid at 37°C under static condition for 24days. The formation of hydroxyl-carbonated apatite layer; evident of bioactivity of the material, was elucidated by XRD, FTIR, AAS, SEM and EDX analysis. The result showed that partial substitution of TiO2 with SiO2 negatively influenced bioactivity; it decreased with increase in concentration of TiO2. As Ti(+4) having stronger field strength as compared to Si(+4) so its replacement became the cause for reduction in degradation that in turn improved the chemical stability. The compressive strength was also enhanced with progress addition of TiO2 in the system. The antibacterial properties were examined against Staphylococcus Epidermidis. Strong antibacterial efficacy was observed with the addition of TiO2 in the system. Copyright © 2016 Elsevier B.V. All rights reserved.

  7. Bone augmentation with bioactive glass in three cases of dental implant placement.

    Science.gov (United States)

    Gatti, Antonietta M; Simonetti, Leopoldo A; Monari, Emanuela; Guidi, Stefano; Greenspan, David

    2006-04-01

    This study reports the clinical use of a bioactive bone graft material, PerioGlas, in the treatment of dental extraction sites before dental implant placement, to effect bone regeneration and to give early fixation to the implant.PerioGlas, granules, ranging from 90 to 710 mm, are implanted after tooth extraction in three patients; after 6 months bone biopsies were performed in the site of the glass implantation and observed under Electron Scanning Microscopy. All the granules showed a biodegradation involving precipitation of calcium phosphate that worked as a scaffold for osteoblasts colonization. All cases examined showed the bioactivity of PerioGlas granules resulting in new bone formation and biodegradation of the glass. After a two-year clinical follow-up all the implants were successfully loaded and appeared stable.

  8. Gallium-containing phospho-silicate glasses: Synthesis and in vitro bioactivity

    Energy Technology Data Exchange (ETDEWEB)

    Franchini, Mirco; Lusvardi, Gigliola; Malavasi, Gianluca, E-mail: gmalavasi@unimo.it; Menabue, Ledi

    2012-08-01

    A series of Ga-containing phospho-silicate glasses based on Bioglass 45S5, having molar formula 46.2SiO{sub 2}{center_dot}24.3Na{sub 2}O{center_dot}26.9CaO{center_dot}2.6P{sub 2}O{sub 5}{center_dot}xGa{sub 2}O{sub 3} (x = 1.0, 1.6, 3.5), were prepared by fusion method. The reference Bioglass 45S5 without gallium was also prepared. The synthesized glasses were immersed in simulated body fluid (SBF) for 30 days in order to observe ion release and hydroxyapatite (HA) formation. All Ga-containing glasses maintain the ability of HA formation as indicated by main X-ray diffractometric peaks and/or electronic scanning microscopy results. HA layer was formed after 1 day of SBF soaking in 45S5 glass containing up to 1.6% Ga{sub 2}O{sub 3} content. Moreover, gallium released by the glasses was found to be partially precipitated on the glass surface as gallium phosphate. Further increase in gallium content reduced the ion release in SBF. The maximum of Ga{sup 3+} concentration measured in solution is {approx} 6 ppm determined for 3.5% Ga{sub 2}O{sub 3} content. This amount is about half of the toxic level (14 ppm) of gallium and the glasses release gallium till 30 days of immersion in SBF. Considering the above results, the studied materials can be proposed as bioactive glasses with additional antimicrobial effect of gallium having no toxic outcome. - Highlights: Black-Right-Pointing-Pointer A new class of potential bioactive glasses gallium content. Black-Right-Pointing-Pointer Controlled ions release from the glass surface. Black-Right-Pointing-Pointer Effect of Ga{sub 2}O{sub 3} content on bioactivity (hydroxyapatite formation). Black-Right-Pointing-Pointer Formation of calcite when the phosphate concentration is low in SBF.

  9. Prospective cohort comparison of bioactive glass implants and conchal cartilage in reconstruction of the posterior canal wall during tympanomastoidectomy

    NARCIS (Netherlands)

    Abramovich, S.; Hannan, S. A.; Huins, C. T.; Georgalas, C.; McGuinness, J.; Vats, A.; Thompson, I.

    2008-01-01

    OBJECTIVE: To compare the effectiveness of bioactive glass implants and conchal cartilage in reconstructing the posterior canal wall during tympanomastoidectomy. STUDY DESIGN: Prospective cohort clinical study. SETTING: Teaching hospital. PATIENTS: Patients with clinically diagnosed chronic

  10. Correlation between acoustical and structural properties of glasses: Extension of Abd El-Moneim model for bioactive silica based glasses

    Energy Technology Data Exchange (ETDEWEB)

    Abd El-Moneim, Amin, E-mail: aminabdelmoneim@hotmail.com

    2016-04-15

    Correlation between room temperature ultrasonic attenuation coefficient and the most significant structural parameters has been studied in the bioactive silica based glasses, for the first time. The correlation has been carried out in the quaternary SiO{sub 2}–Na{sub 2}O–CaO–P{sub 2}O{sub 5} glass system using the two semi-empirical formulas, which have been presented recently by the author. Changes in the elastic properties, related to the substitution of SiO{sub 2} by alkali Na{sub 2}O and alkaline earth CaO oxides, have also been deduced by evaluating the mean atomic volume, packing density, fractal bond connectivity and density of the analogous crystalline structure. Furthermore, values of the theoretical elastic moduli have been calculated on the basis of Makishima-Mackenzie theory and compared with the corresponding observed values. Results show that the correlation between ultrasonic attenuation coefficient and the oxygen density, average atomic ring size, first-order stretching force constant and experimental bulk modulus was achieved at 5 MHz frequency. Values of the theoretically calculated shear modulus are in excellent correlation (C. R. ≻95%) with the corresponding experimental ones. The divergence between the theoretical and experimental values of bulk modulus has been discussed. - Highlights: • Abd El-Moneim model was extended for bioactive glasses. • Ultrasonic attenuation was correlated with structural parameters. • Correlation was carried out in Si–Na–Ca–P glasses. • The model is valid for all investigated glass samples. • Agreement between theoretical and experimental elastic moduli was studied.

  11. Response of MC3T3-E1cells on microroughen bioactive glass coated zirconia

    Directory of Open Access Journals (Sweden)

    Sapna Laxmi Tuladhar

    2017-10-01

    Full Text Available Background & Objectives:The objective of this study was to determine the cellular response of micro-roughened bioactive glass coated zirconia substrate (ZBR and non roughen bioactive glass coated zirconia substrate (ZB, and compare them with uncoated zirconia substrate (Z.  Materials & Methods:Surface micro-roughening was obtained using an Al2O3 sandblasting method. Abrasive blasting of zirconia coated bioactive glass produced an irregular finish with surface roughness average Ra 0.85 µm as determined by profilometer and scan electron microscope. Surface roughness of the samples in ascending order was ZBR>ZB>Z. Murine derived preosteoblast (MC3T3-E1 cells were seeded on the samples, and the cell morphology, growth, differentiation, were observed. Cell morphology was evaluated by means of scanning electron microscope (SEM, while cell proliferation and differentiation using MTT (3-(4,5-Dimethylthiazol-2-yl-2,5-diphenyltetrazolium bromide test and alkaline phosphates activity respectively. Results:The cell growth on all the samples continual increase with culturing up to 5days, showing good cell viability. However, there was no significant difference (p>0.05 with respect to the Z, ZB, and ZBR at day 5 at MTT assay. In particular, the alkaline phosphatase (ALP activity of the cells was significantly higher on the ZB and ZBR than Z samples at both 7 and 14 days.   Conclusion:Our findings demonstrate that bioactive glass coated surface was found to have better surface conditions to regulate bone cell differentiation 

  12. Fabrication of interpenetrate chitosan: bioactive glass, using dense gas CO2.

    Science.gov (United States)

    Fathi, Ali; Ravarian, Roya; Dehghani, Fariba

    2011-01-01

    Success of bone tissue engineering relies on using bioactive scaffolds with ideal pore morphology which can mimic the properties of the natural extracellular matrix (ECM). The objective of this study was to interpenetrate bioactive glass components throughout the three dimensional (3D) structure of the chitosan scaffold to increase the average pore size of the scaffold and also the osteoconductivity and osteoinductivity of the fabricated scaffold. Scanning electron microscopy was used to observe the microsturcture of the hydrogel. The results of this study demonstrated that the average pore size in the hydrogel was increased significantly (pceramic and chitosan. The composite hydrogel fabricated swell in water and has high potential to be used for bone tissue engineering applications; bioactive glass can substantially improve bioactivity of the bone tissue engineering scaffolds However, further studies are required to investigate the effect of BG on the biocompatibility of the scaffolds. In addition, in vitro cell studies are also required to confirm the suitability of the fabricated scaffold for bone tissue engineering.

  13. Bioactive sol-gel glass added ionomer cement for the regeneration of tooth structure.

    Science.gov (United States)

    Choi, Jung-Young; Lee, Hae-Hyoung; Kim, Hae-Won

    2008-10-01

    Dental cements including the glass ionomer cement (GIC) have found widespread use in restoring tooth structures. In this study, a sol-gel derived glass (SG) with a bioactive composition (70SiO(2).25CaO.5P(2)O(5)) was added to the commercial GIC (GC, Fuji I) to improve the bioactivity and tooth regeneration capability. The SG powders prepared with sizes in the range of a few micrometers were mixed with GIC at SG/GC ratios of 10 and 30 wt%. The setting time, diametral tensile strength, and in vitro bioactivity of the GC-SG cements were examined. The setting time of the GC-SG cements increased with increasing amount of SG. However, the addition of SG did not significantly alter the diametral tensile strength of the GC. GC-SG induced the precipitation of an apatite bone-mineral phase on the surface after immersion in a simulated body fluid (SBF), showing in vitro bone bioactivity. However, no mineral induction in SBF was observed in the commercial GIC after the immersion. The in vitro cell assay confirmed that the GC-SG samples produced higher cell viability than the GC sample with cell culturing for up to 7 days.

  14. Effect of a novel bioactive glass-ceramic on dentinal tubule occlusion: an in vitro study.

    Science.gov (United States)

    Zhong, Y; Liu, J; Li, X; Yin, W; He, T; Hu, D; Liao, Y; Yao, X; Wang, Y

    2015-03-01

    This in vitro study aimed to assess the ability and efficacy of HX-BGC, a novel bioactive glass-ceramic (SiO2-P2 O5-CaO-Na2 O-SrO), to reduce dentine tubule permeability. Dentine discs from human third molars were etched and randomly allocated into five groups: Group 1--distilled water; Group 2--Sensodyne Repair toothpaste (containing NovaMin®); Group 3--HX-BGC toothpaste (containing 7.5% HX-BGC); Group 4--control toothpaste (without HX-BGC); and Group 5--HX-BGC powder. Specimens were treated daily by brushing with an electric toothbrush for 20 seconds. Between daily treatments (7 days total), specimens were immersed in artificial saliva for 24 hours. Dentine permeability was measured at baseline, after the first treatment, after the first 24-hour immersion in artificial saliva and at the end of day 7. Dentine morphology and surface deposits were observed by scanning electron microscopy after one day and 7 days of treatment, respectively. Sensodyne Repair and bioactive glass-ceramic toothpaste significantly and immediately lowered dentine permeability. The HX-BGC powder group showed the highest reduction in dentine permeability after 7 days of treatment. The novel bioactive glass-ceramic material HX-BGC is effective in reducing dentine permeability by occluding open dentine tubules, indicating that HX-BGC may be a potential treatment for dentine hypersensitivity. © 2015 Australian Dental Association.

  15. Drug delivery property, bactericidal property and cytocompatibility of magnetic mesoporous bioactive glass.

    Science.gov (United States)

    Liu, Yi-Zhuo; Li, Yang; Yu, Xi-Bin; Liu, Li-Na; Zhu, Zhen-An; Guo, Ya-Ping

    2014-08-01

    A multifunctional magnetic mesoporous bioactive glass (MMBG) has been widely used for a drug delivery system, but its biological properties have been rarely reported. Herein, the effects of mesopores and Fe3O4 nanoparticles on drug loading-release property, bactericidal property and biocompatibility have been investigated by using mesoporous bioactive glass (MBG) and non-mesoporous bioactive glass (NBG) as control samples. Both MMBG and MBG have better drug loading efficiency than NBG because they possess ordered mesoporous channels, big specific surface areas and high pore volumes. As compared with MBG, the Fe3O4 nanoparticles in MMBG not only provide magnetic property, but also improve sustained drug release property. For gentamicin-loaded MMBG (Gent-MMBG), the sustained release of gentamicin and the Fe3O4 nanoparticles minimize bacterial adhesion significantly and prevent biofilm formation against Staphylococcus aureus (S. aureus) and Staphylococcus epidermidis (S. epidermidis). Moreover, the magnetic Fe3O4 nanoparticles in MMBG can promote crucial cell functions such as cell adhesion, spreading and proliferation. The excellent biocompatibility and drug delivery property of MMBG suggest that Gent-MMBG has great potentials for treatment of implant-associated infections. Copyright © 2014 Elsevier B.V. All rights reserved.

  16. Enhanced Stem Cell Osteogenic Differentiation by Bioactive Glass Functionalized Graphene Oxide Substrates

    Directory of Open Access Journals (Sweden)

    Xiaoju Mo

    2016-01-01

    Full Text Available An unmet need in engineered bone regeneration is to develop scaffolds capable of manipulating stem cells osteogenesis. Graphene oxide (GO has been widely used as a biomaterial for various biomedical applications. However, it remains challenging to functionalize GO as ideal platform for specifically directing stem cell osteogenesis. Herein, we report facile functionalization of GO with dopamine and subsequent bioactive glass (BG to enhance stem cell adhesion, spreading, and osteogenic differentiation. On the basis of graphene, we obtained dopamine functionalized graphene oxide/bioactive glass (DGO/BG hybrid scaffolds containing different content of DGO by loading BG nanoparticles on graphene oxide surface using sol-gel method. To enhance the dispersion stability and facilitate subsequent nucleation of BG in GO, firstly, dopamine (DA was used to modify GO. Then, the modified GO was functionalized with bioactive glass (BG using sol-gel method. The adhesion, spreading, and osteoinductive effects of DGO/BG scaffold on rat bone marrow mesenchymal stem cells (rBMSCs were evaluated. DGO/BG hybrid scaffolds with different content of DGO could influence rBMSCs’ behavior. The highest expression level of osteogenic markers suggests that the DGO/BG hybrid scaffolds have great potential or elicit desired bone reparative outcome.

  17. Simulations reveal the role of composition into the atomic-level flexibility of bioactive glass cements.

    Science.gov (United States)

    Tian, Kun Viviana; Chass, Gregory A; Di Tommaso, Devis

    2016-01-14

    Bioactive glass ionomer cements (GICs), the reaction product of a fluoro-alumino-silicate glass and polyacrylic acid, have been in effective use in dentistry for over 40 years and more recently in orthopaedics and medical implantation. Their desirable properties have affirmed GIC's place in the medical materials community, yet are limited to non-load bearing applications due to the brittle nature of the hardened composite cement, thought to arise from the glass component and the interfaces it forms. Towards helping resolve the fundamental bases of the mechanical shortcomings of GICs, we report the 1st ever computational models of a GIC-relevant component. Ab initio molecular dynamics simulations were employed to generate and characterise three fluoro-alumino-silicate glasses of differing compositions with focus on resolving the atomic scale structural and dynamic contributions of aluminium, phosphorous and fluorine. Analyses of the glasses revealed rising F-content leading to the expansion of the glass network, compression of Al-F bonding, angular constraint at Al-pivots, localisation of alumino-phosphates and increased fluorine diffusion. Together, these changes to the structure, speciation and dynamics with raised fluorine content impart an overall rigidifying effect on the glass network, and suggest a predisposition to atomic-level inflexibility, which could manifest in the ionomer cements they form.

  18. Cytotoxicity assessment of modified bioactive glasses with MLO-A5 osteogenic cells in vitro.

    Science.gov (United States)

    Modglin, Vernon C; Brown, Roger F; Jung, Steven B; Day, Delbert E

    2013-05-01

    The primary objective of this study was to evaluate in vitro responses of MLO-A5 osteogenic cells to two modifications of the bioactive glass 13-93. The modified glasses, which were designed for use as cell support scaffolds and contained added boron to form the glasses 13-93 B1 and 13-93 B3, were made to accelerate formation of a bioactive hydroxyapatite surface layer and possibly enhance tissue growth. Quantitative MTT cytotoxicity tests revealed no inhibition of growth of MLO-A5 cells incubated with 13-93 glass extracts up to 10 mg/ml, moderate inhibition of growth with 13-93 B1 glass extracts, and noticeable inhibition of growth with 13-93 B3 glass extracts. A morphology-based biocompatibility test was also performed and yielded qualitative assessments of the relative biocompatibilities of glass extracts that agree with those obtained by the quantitative MTT test. However, as a proof of concept experiment, when MLO-A5 cells were seeded onto 13-93 B3 scaffolds in a dynamic in vitro environment, cell proliferation occurred as evidenced by qualitative and quantitative MTT labeling of scaffolds. Together these results demonstrate the in vitro toxicity of released borate ion in static experiments; however borate ion release can be mitigated in a dynamic environment similar to the human body where microvasculature is present. Here we argue that despite toxicity in static environments, boron-containing 13-93 compositions may warrant further study for use in tissue engineering applications.

  19. Preparation and characterization of bioactive glass nanoparticles prepared by sol-gel for biomedical applications

    Science.gov (United States)

    Luz, Gisela M.; Mano, João F.

    2011-12-01

    Bioactive glass nanoparticles (BG-NPs), based on both ternary (SiO2-CaO-P2O5) and binary (SiO2-CaO) systems, were prepared via an optimized sol-gel method. The pH of preparation and the effect of heat treatment temperature were evaluated, as well as the effect of suppressing P in the bioactivity ability of the materials. The morphology and composition of the BG-NPs were studied using FTIR, XRD and SEM. The bioactive character of these materials was accessed in vitro by analyzing the ability for apatite formation onto the surface after being immersed in simulated body fluid (SBF). XRD, EDX and SEM were used to confirm the bioactivity of the materials. The BG-NP effect on cell metabolic activity was assessed by seeding L929 cells with their leachables, proving the non-cytotoxicity of the materials. Finally the most bioactive BG-NPs developed (ternary system prepared at pH 11.5 and treated at 700 °C) were successfully combined with chitosan in the production of biomimetic nanocomposite osteoconductive membranes that could have the potential to be used in guided tissue regeneration.

  20. Preparation and characterization of bioactive glass nanoparticles prepared by sol-gel for biomedical applications.

    Science.gov (United States)

    Luz, Gisela M; Mano, João F

    2011-12-09

    Bioactive glass nanoparticles (BG-NPs), based on both ternary (SiO(2)-CaO-P(2)O(5)) and binary (SiO(2)-CaO) systems, were prepared via an optimized sol-gel method. The pH of preparation and the effect of heat treatment temperature were evaluated, as well as the effect of suppressing P in the bioactivity ability of the materials. The morphology and composition of the BG-NPs were studied using FTIR, XRD and SEM. The bioactive character of these materials was accessed in vitro by analyzing the ability for apatite formation onto the surface after being immersed in simulated body fluid (SBF). XRD, EDX and SEM were used to confirm the bioactivity of the materials. The BG-NP effect on cell metabolic activity was assessed by seeding L929 cells with their leachables, proving the non-cytotoxicity of the materials. Finally the most bioactive BG-NPs developed (ternary system prepared at pH 11.5 and treated at 700 °C) were successfully combined with chitosan in the production of biomimetic nanocomposite osteoconductive membranes that could have the potential to be used in guided tissue regeneration.

  1. Synthesis and characterization of cerium- and gallium-containing borate bioactive glass scaffolds for bone tissue engineering.

    Science.gov (United States)

    Deliormanlı, Aylin M

    2015-02-01

    Bioactive glasses are widely used in biomedical applications due to their ability to bond to bone and even to soft tissues. In this study, borate based (13-93B3) bioactive glass powders containing up to 5 wt% Ce2O3 and Ga2O3 were prepared by the melt quench technique. Cerium (Ce+3) and gallium (Ga+3) were chosen because of their low toxicity associated with bacteriostatic properties. Bioactive glass scaffolds were fabricated using the polymer foam replication method. In vitro degradation and bioactivity of the scaffolds were evaluated in SBF under static conditions. Results revealed that the cerium- and gallium-containing borate glasses have much lower degradation rates compared to the bare borate glass 13-93B3. In spite of the increased chemical durability, substituted glasses exhibited a good in vitro bioactive response except when the Ce2O3 content was 5 wt%. Taking into account the high in vitro hydroxyapatite forming ability, borate glass scaffolds containing Ce+3 and Ga+3 therapeutic ions are promising candidates for bone tissue engineering applications.

  2. Preparation of a biomimetic composite scaffold from gelatin/collagen and bioactive glass fibers for bone tissue engineering

    Energy Technology Data Exchange (ETDEWEB)

    Sharifi, Esmaeel; Azami, Mahmoud [Department of Tissue Engineering and Applied Cell Sciences, School of Advanced Technologies in Medicine, Tehran University of Medical Sciences, Tehran (Iran, Islamic Republic of); Kajbafzadeh, Abdol-Mohammad [Department of Tissue Engineering and Applied Cell Sciences, School of Advanced Technologies in Medicine, Tehran University of Medical Sciences, Tehran (Iran, Islamic Republic of); Pediatric Urology Research Center, Section of Tissue Engineering and Stem Cells Therapy, Department of Pediatric Urology, Children' s Hospital Medical Center, Tehran, Iran (IRI) (Iran, Islamic Republic of); Moztarzadeh, Fatollah [Department of Biomedical Engineering, Amirkabir University of Technology (Tehran Polytechnic), Tehran (Iran, Islamic Republic of); Faridi-Majidi, Reza [Department of Medical Nanotechnology, School of Advanced Technologies in Medicine, Tehran University of Medical Sciences, Tehran (Iran, Islamic Republic of); Shamousi, Atefeh; Karimi, Roya [Department of Tissue Engineering and Applied Cell Sciences, School of Advanced Technologies in Medicine, Tehran University of Medical Sciences, Tehran (Iran, Islamic Republic of); Ai, Jafar, E-mail: jafar_ai@tums.ac.ir [Department of Tissue Engineering and Applied Cell Sciences, School of Advanced Technologies in Medicine, Tehran University of Medical Sciences, Tehran (Iran, Islamic Republic of); Brain and Spinal Injury Research Center (BASIR), Imam Khomeini Hospital, Tehran University of Medical Sciences, Tehran (Iran, Islamic Republic of)

    2016-02-01

    Bone tissue is a composite material made of organic and inorganic components. Bone tissue engineering requires scaffolds that mimic bone nature in chemical and mechanical properties. This study proposes a novel method for preparing composite scaffolds that uses sub-micron bioglass fibers as the organic phase and gelatin/collagen as the inorganic phase. The scaffolds were constructed by using freeze drying and electro spinning methods and their mechanical properties were enhanced by using genipin crosslinking agent. Electron microscopy micrographs showed that the structure of composite scaffolds were porous with pore diameters of approximately 70–200 μm, this was again confirmed by mercury porosimetery. These pores are suitable for osteoblast growth. The diameters of the fibers were approximately 150–450 nm. Structural analysis confirmed the formation of desirable phases of sub-micron bioglass fibers. Cellular biocompatibility tests illustrated that scaffolds containing copper ion in the bioglass structure had more cell growth and osteoblast attachment in comparison to copper-free scaffolds. - Highlights: • Fabrication of 45S5 sub-micron bioglass fiber using electrospinning method. • Production of copper doped submicron bioglass fibers on 45S5 bioglass base by electrospinning sol gel route method. • Incorporation of bioglass/Cu-bioglass sub-micron fibers into gelatin/collagen matrix to form biomimetic composite scaffold which were non-cytotoxic according to MTT assay. • Discovering that copper can decrease the glass transition temperatures and enhance osteoblast cell adhesion and viability.

  3. Heat treatment of Na2O-CaO-P2O5-SiO2 bioactive glasses: densification processes and postsintering bioactivity.

    Science.gov (United States)

    Sola, A; Bellucci, D; Raucci, M G; Zeppetelli, S; Ambrosio, L; Cannillo, V

    2012-02-01

    Because of their excellent bioactivity, bioactive glasses are increasingly diffused to produce biomedical devices for bone prostheses, to face the dysfunctions that may be caused by traumatic events, diseases, or even natural aging. However, several processing routes, such as the production of scaffolds or the deposition of coatings, include a thermal treatment to apply or sinter the glass. The exposure to high temperature may induce a devetrification phenomenon, altering the properties and, in particular, the bioactivity of the glass. The present contribution offers an overview of the thermal behavior and properties of two glasses belonging to the Na2O-CaO-P2O5-SiO2 system, to be compared to the standard 45S5 Bioglass(®). The basic goal is to understand the effect of both the original composition and the thermal treatment on the performance of the sintered glasses. The new glasses, the one (BG_Na) with a high content of Na2O, the other (BG_Ca) with a high content of CaO, were fully characterized and sintering tests were performed to define the most interesting firing cycles. The sintered samples, treated at 880°C and 800°C respectively, were investigated from a microstructural point of view and their mechanical properties were compared to those of the bulk (not sintered) glass counterparts. The effect of sintering was especially striking on the BG_Ca material, whose Vickers hardness increased from 598.9 ± 46.7 HV to 1053.4 ± 35.0 HV. The in vitro tests confirmed the ability of the glasses, both in bulk and sintered form, of generating a hydroxyapatite surface layer when immersed in a simulated body fluid. More accurate biological tests performed on the sintered glasses proved the high bioactivity of the CaO-rich composition even after a heat treatment. Copyright © 2011 Wiley Periodicals, Inc.

  4. Bioactive glass particulate filler composite: Effect of coupling of fillers and filler loading on some physical properties.

    Science.gov (United States)

    Oral, Onur; Lassila, Lippo V; Kumbuloglu, Ovul; Vallittu, Pekka K

    2014-05-01

    The aim of this study was to investigate the effect of silanization of biostable and bioactive glass fillers in a polymer matrix on some of the physical properties of the composite. The water absorption, solubility, flexural strength, flexural modulus and toughness of different particulate filler composite resins were studied in vitro. Five different specimen groups were analyzed: A glass-free control, a non-silanized bioactive glass, a silanized bioactive glass, a non-silanized biostable glass and a silanized biostable glass groups. All of these five groups were further divided into sub-groups of dry and water-stored materials, both of them containing groups with 3wt%, 6wt%, 9wt% or 12wt% of glass particles (n=8 per group). The silanization of the glass particles was carried out with 2% of gamma-3-methacryloxyproyltrimethoxysilane (MPS). For the water absorption and solubility tests, the test specimens were stored in water for 60 days, and the percentages of weight change were statistically analyzed. Flexural strength, flexural modulus and toughness values were tested with a three-point bending test and statistically analyzed. Higher solubility values were observed in non-silanized glass in proportion to the percentage of glass particles. Silanization, on the other hand, decreased the solubility values of both types of glass particles and polymer. While 12wt% non-silanized bioactive glass specimens showed -0.98wt% solubility, 12wt% silanized biostable glass specimens were observed to have only -0.34wt% solubility. The three-point bending results of the dry specimens showed that flexural strength, toughness and flexural modulus decreased in proportion to the increase of glass fillers. The control group presented the highest results (106.6MPa for flexural strength, 335.7kPA for toughness, 3.23GPa for flexural modulus), whereas for flexural strength and toughness, 12wt% of non-silanized biostable glass filler groups presented the lowest (70.3MPa for flexural strength

  5. Bioactivity and cytotoxicity of glass and glass-ceramics based on the 3CaO·P₂O₅--SiO₂--MgO system.

    Science.gov (United States)

    Daguano, Juliana K M F; Rogero, Sizue O; Crovace, Murilo C; Peitl, Oscar; Strecker, Kurt; Dos Santos, Claudinei

    2013-09-01

    The mechanical strength of bioactive glasses can be improved by controlled crystallization, turning its use as bulk bone implants viable. However, crystallization may affect the bioactivity of the material. The aim of this study was to develop glass-ceramics of the nominal composition (wt%) 52.75(3CaO·P₂O₅)-30SiO₂-17.25MgO, with different crystallized fractions and to evaluate their in vitro cytotoxicity and bioactivity. Specimens were heat-treated at 700, 775 and 975 °C, for 4 h. The major crystalline phase identified was whitlockite, an Mg-substituted tricalcium phosphate. The evaluation of the cytotoxicity was carried out by the neutral red uptake methodology. Ionic exchanges with the simulated body fluid SBF-K9 acellular solution during the in vitro bioactivity tests highlight the differences in terms of chemical reactivity between the glass and the glass-ceramics. The effect of crystallinity on the rates of hydroxycarbonate apatite (HCA) formation was followed by Fourier transformed infrared spectroscopy. Although all glass-ceramics can be considered bioactive, the glass-ceramic heat-treated at 775 °C (V775-4) presented the most interesting result, because the onset for HCA formation is at about 24 h and after 7 days the HCA layer dominates completely the spectrum. This occurs probably due to the presence of the whitlockite phase (3(Ca,Mg)O·P₂O₅). All samples were considered not cytotoxic.

  6. Freeform extrusion fabrication of titanium fiber reinforced 13-93 bioactive glass scaffolds.

    Science.gov (United States)

    Thomas, Albin; Kolan, Krishna C R; Leu, Ming C; Hilmas, Gregory E

    2017-06-01

    Although implants made with bioactive glass have shown promising results for bone repair, their application in repairing load-bearing long bone is limited due to their poor mechanical properties in comparison to human bone. This work investigates the freeform extrusion fabrication of bioactive silicate 13-93 glass scaffolds reinforced with titanium (Ti) fibers. A composite paste prepared with 13-93 glass and Ti fibers (~16µm in diameter and lengths varying from ~200µm to ~2 mm) was extruded through a nozzle to fabricate scaffolds (0-90° filament orientation pattern) on a heated plate. The sintered scaffolds measured pore sizes ranging from 400 to 800µm and a porosity of ~50%. Scaffolds with 0.4vol% Ti fibers measured fracture toughness of ~0.8MPam 1/2 and a flexural strength of ~15MPa. 13-93 glass scaffolds without Ti fibers had a toughness of ~0.5MPam 1/2 and a strength of ~10MPa. The addition of Ti fibers increased the fracture toughness of the scaffolds by ~70% and flexural strength by ~40%. The scaffolds' biocompatibility and their degradation in mechanical properties in vitro were assessed by immersing the scaffolds in a simulated body fluid over a period of one to four weeks. Copyright © 2016 Elsevier Ltd. All rights reserved.

  7. Fabrication of Bioactive Glass Nanopowder for Replacement of Ossicles in Middle ear

    Directory of Open Access Journals (Sweden)

    Ali Doostmohammadi

    2007-06-01

    Full Text Available Background and Aim: Due to its ability in bonding with hard and soft tissue, healing and repairing of the bone, and proper replacing of the ossicles in middle ear, bioactive glass has come into considera­tion. The aim of this work was preparation, development and characterization of nanopowder bioactive glass obtained by the sol-gel technique. Materials and Methods: Bioglass powder was made by sol-gel technique and the presence of desired ele­ments is tested by X-ray fluorescence analysis. Trans Electronic Microscopic (TEM technique was used to evaluate the powders shape and size. The prepared bioglass powder was immersed in the simu­lated body fluid solution for 30 days. Fourier transform infrared (FTIR spectroscopy was util­ized to recognize and to confirm the formation of apatite layer on prepared bioglass powder. (XRD as a structural characterization technique was used to investigate the microstructure. Results: The glass powder size was less than 100 nanometers. The formation of apatite layer con­firmed the bioactivity of the bioglass powder and tests revealed that all the films had the signs of bioactiv­ity. It was also found that at sintering temperatures above 900 ºC, crystalline phase Ca2SiO4 was formed. Conclusion: The sol-gel nanopowder bioglass can be used as a replacement for small bones such as ossi­cles in middle ear, and it leads to bone osteointegration and growth of the surrounding tissue.

  8. SBA-15 ordered mesoporous silica inside a bioactive glass-ceramic scaffold for local drug delivery.

    Science.gov (United States)

    Cauda, V; Fiorilli, S; Onida, B; Vernè, E; Vitale Brovarone, C; Viterbo, D; Croce, G; Milanesio, M; Garrone, E

    2008-10-01

    The paper reports the synthesis of an ordered silica mesostructure of the SBA-15 type inside a macroporous bioactive glass-ceramic scaffold of the type SiO(2)-CaO-K(2)O, to combine the bioactivity of the latter with the release properties of the former, in view of local drug delivery from implants designed for tissue engineering. The standard procedure for SBA-15 synthesis has been modified to minimize the damage to the scaffold caused by the acidic synthesis medium. The composite system has been characterized by means of Scanning Electron Microscopy (coupled with EDS analysis), Small Angle X-Ray Diffraction, Thermogravimetry analysis and Infrared Spectroscopy: the formation of a well ordered hexagonal mesostructure was confirmed. Ibuprofen has been chosen as model drug. The uploading properties have been investigated of the scaffold-mesoporous silica composite as compared with the scaffold as such, and a five-fold increase in the adsorbing properties toward ibuprofen was found, due to the presence of the ordered mesoporous silica. The ibuprofen release to a SBF solution in vitro is complete in 1 day. Retention of bioactivity from the glass-ceramic scaffold after the silica mesostructure incorporation has been observed.

  9. The Fabrication and Characterization of PCL/Rice Husk Derived Bioactive Glass-Ceramic Composite Scaffolds

    Directory of Open Access Journals (Sweden)

    Farnaz Naghizadeh

    2014-01-01

    Full Text Available The present study was conducted to fabricate a 3D scaffold using polycaprolactone (PCL and silicate based bioactive glass-ceramic (R-SBgC. Different concentrations of R-SBgC prepared from rice husk ash (RHA were combined with PCL to fabricate a composite scaffold using thermally induced phase separation (TIPS method. The products were then characterized using SEM and EDX. The results demonstrated that R-SBgC in PCL matrix produced a bioactive material which has highly porous structure with interconnected porosities. There appears to be a relationship between the increase in R-SBgC concentration and increased material density and compressive modulus; however, increasing R-SBgC concentration result in reduced scaffold porosity. In conclusion, it is possible to fabricate a PCL/bioactive glass-ceramic composite from processed rice husk. Varying the R-SBgC concentrations can control the properties of this material, which is useful in the development of the ideal scaffold intended for use as a bone substitute in nonload bearing sites.

  10. Comparison of the Remineralizing Effects of Sodium Fluoride and Bioactive Glass Using Bioerodible Gel Systems

    Directory of Open Access Journals (Sweden)

    Attiguppe Ramashetty Prabhakar

    2009-12-01

    Full Text Available Background and aims. A carious lesion is the accumulation of numerous episodes of de- and remineralization, rather than a unidirectional demineralization process. Tooth destruction can be arrested or reversed by the frequent delivery of fluoride or calcium/phosphorous ions to the tooth surface. The present study compared and evaluated the remineralization potential of sodium fluoride and bioactive glass delivered through a bioerodible gel system. Materials and methods. Longitudinal sections of artificial carious lesions, created at the gingivofacial surface of 64 primary maxillary incisors were photographed under a polarized light microscope and quantified for demineralization. The sections were repositioned into the tooth form and randomly mounted in sets of four that simulated an arch form. The teeth were divided into 4 groups: 1 sodium fluoride films, 2 bioactive glass films, 3 control films placed interproximally and 4 nontreatment group. Following exposure to artificial saliva for 30 days, the lesions were again photographed and quantified as above. The recorded values were statistically analyzed using Student’s paired t-test for intragroup comparison, one-way ANOVA and Post-Hoc Tukey’s test for pairwise comparison. Results. The sodium fluoride and bioactive gel groups showed significant remineralization compared with the control groups (P < 0.001. Conclusion. Bioerodible gel films can be used to deliver remineralizing agents to enhance remineralization.

  11. Cytocompatibility studies of titania-doped calcium borosilicate bioactive glasses in-vitro.

    Science.gov (United States)

    Samudrala, Rajkumar; Abdul Azeem P; Penugurti, Vasudevarao; Manavathi, Bramanandam

    2017-08-01

    The present study aims to elucidate the applications of Titania (TiO2) doped calcium borosilicate glass as a biocompatible material in regenerative orthopedic applications. In this context, we have examined the bioactivity of various concentrations of TiO2 doped glasses with the help of simulated body fluid (SBF). Cytocompatibility, cell proliferation, and protein expression studies revealed the potential candidature of TiO2 doped glasses on osteoblast cell lines (MG-63). We hypothesized that TiO2 doped calcium borosilicate glasses are most cytocompatible material for bone implants. Glasses with composition 31B2O3-20SiO2-24.5Na2O-(24.5-x) CaO- x TiO2 (x=0,0.5,1,2) have been prepared by the conventional melt-quenching technique. After immersion of glasses in the SBF, formation of hydroxyapatite layer on the surface was confirmed by X-ray Diffractometer (XRD), Fourier Transform Infrared Spectroscopy (FT-IR) and Scanning Electron Microscopy-Energy Dispersive Spectroscopy (SEM-EDS) analysis. Significant change in the pH of the body fluid was observed with the addition of titania. Degradation test was performed as per the ISO 10993. The results showed that partial substitution of TiO2 with CaO negatively influenced bioactivity; it decreased with increase in concentration of TiO2. Vickers hardness tester was used to measure the microhardness values of the prepared glasses. With the increasing of TiO2 content, the microhardness of the glass samples was increased from 545Hv to 576Hv. Cytocompatibility has been evaluated with MG-63 cells by using MTT assay. Further, we observed that there was no change in expressions of cyclin levels even after the incorporation of titania. The antibacterial properties were examined against E. coli and S. aureus. Strong antibacterial efficacy was observed for 2% TiO2 in the system. Hence it can be concluded that titania-doped borosilicate glasses may be used as potential materials in bone tissue engineering. Copyright © 2017 Elsevier B

  12. Influence of Cu doping in borosilicate bioactive glass and the properties of its derived scaffolds

    Energy Technology Data Exchange (ETDEWEB)

    Wang, Hui [School of Materials Science and Engineering, Tongji University, Shanghai 2001804 (China); Zhao, Shichang [Department of Orthopedic Surgery, Shanghai Sixth People' s Hospital, Shanghai Jiao Tong University, Shanghai 200233 (China); Xiao, Wei [Department of Materials Science and Engineering, and Center for Biomedical Science and Engineering, Missouri University of Science and Technology, Rolla, MO 65409-0340 (United States); Xue, Jingzhe [Department of Chemistry, Tongji University, Shanghai 200092 (China); Shen, Youqu [Department of Materials Science and Engineering, and Center for Biomedical Science and Engineering, Missouri University of Science and Technology, Rolla, MO 65409-0340 (United States); Zhou, Jie; Huang, Wenhai [School of Materials Science and Engineering, Tongji University, Shanghai 2001804 (China); Rahaman, Mohamed N. [Department of Materials Science and Engineering, and Center for Biomedical Science and Engineering, Missouri University of Science and Technology, Rolla, MO 65409-0340 (United States); Zhang, Changqing, E-mail: shzhangchangqing@163.com [Department of Orthopedic Surgery, Shanghai Sixth People' s Hospital, Shanghai Jiao Tong University, Shanghai 200233 (China); Wang, Deping, E-mail: wdpshk@tongji.edu.cn [School of Materials Science and Engineering, Tongji University, Shanghai 2001804 (China)

    2016-01-01

    Copper doped borosilicate glasses (BG–Cu) were studied by means of FT-IR, Raman, UV–vis and NMR spectroscopies to investigate the changes that appeared in the structure of borosilicate glass matrix by doping copper ions. Micro-fil and immunohistochemistry analysis were applied to study the angiogenesis of its derived scaffolds in vivo. Results indicated that the Cu ions significantly increased the B–O bond of BO{sub 4} groups at 980 cm{sup −1}, while they decrease that of BO{sub 2}O{sup −} groups at 1440–1470 cm{sup −1} as shown by Raman spectra. A negative shift was observed from {sup 11}B and {sup 29}Si NMR spectra. The {sup 11}B NMR spectra exhibited a clear transformation from BO{sub 3} into BO{sub 4} groups, caused by the agglutination effect of the Cu ions and the charge balance of the agglomerate in the glass network, leading to a more stable glass network and lower ions release rate in the degradation process. Furthermore, the BG–Cu scaffolds significantly enhanced blood vessel formation in rat calvarial defects at 8 weeks post-implantation. Generally, it suggested that the introduction of Cu into borosilicate glass endowed glass and its derived scaffolds with good properties, and the cooperation of Cu with bioactive glass may pave a new way for tissue engineering. - Highlights: • Agglutination effect of Cu{sup 2+} and charge balance of agglomerate lead to more stable glass. • Lower degradability and lower ions release were found in BG-Cu scaffolds. • Excellent angiogenesis and sustain Cu{sup 2+} release were endowed by doping Cu.

  13. Gallium-containing phospho-silicate glasses: synthesis and in vitro bioactivity.

    Science.gov (United States)

    Franchini, Mirco; Lusvardi, Gigliola; Malavasi, Gianluca; Menabue, Ledi

    2012-08-01

    A series of Ga-containing phospho-silicate glasses based on Bioglass 45S5, having molar formula 46.2SiO2·24.3Na2O·26.9CaO·2.6P2O5·xGa2O3 (x=1.0, 1.6, 3.5), were prepared by fusion method. The reference Bioglass 45S5 without gallium was also prepared. The synthesized glasses were immersed in simulated body fluid (SBF) for 30 days in order to observe ion release and hydroxyapatite (HA) formation. All Ga-containing glasses maintain the ability of HA formation as indicated by main X-ray diffractometric peaks and/or electronic scanning microscopy results. HA layer was formed after 1 day of SBF soaking in 45S5 glass containing up to 1.6% Ga2O3 content. Moreover, gallium released by the glasses was found to be partially precipitated on the glass surface as gallium phosphate. Further increase in gallium content reduced the ion release in SBF. The maximum of Ga(3+) concentration measured in solution is ~6 ppm determined for 3.5% Ga2O3 content. This amount is about half of the toxic level (14 ppm) of gallium and the glasses release gallium till 30 days of immersion in SBF. Considering the above results, the studied materials can be proposed as bioactive glasses with additional antimicrobial effect of gallium having no toxic outcome. Copyright © 2012 Elsevier B.V. All rights reserved.

  14. A glass fiber-reinforced composite - bioactive glass cranioplasty implant: A case study of an early development stage implant removed due to a late infection.

    Science.gov (United States)

    Posti, Jussi P; Piitulainen, Jaakko M; Hupa, Leena; Fagerlund, Susanne; Frantzén, Janek; Aitasalo, Kalle M J; Vuorinen, Ville; Serlo, Willy; Syrjänen, Stina; Vallittu, Pekka K

    2015-03-01

    This case study describes the properties of an early development stage bioactive glass containing fiber-reinforced composite calvarial implant with histology that has been in function for two years and three months. The patient is a 33-year old woman with a history of substance abuse, who sustained a severe traumatic brain injury later unsuccessfully treated with an autologous bone flap and a custom-made porous polyethylene implant. She was thereafter treated with developmental stage glass fiber-reinforced composite - bioactive glass implant. After two years and three months, the implant was removed due to an implant site infection. The implant was analyzed histologically, mechanically, and in terms of chemistry and dissolution of bioactive glass. Mechanical integrity of the load bearing fiber-reinforced composite part of the implant was not affected by the in vivo period. Bioactive glass particles demonstrated surface layers of hydroxyapatite like mineral and dissolution, and related increase of pH was considerably less after two and three months period than that for fresh bioactive glass. There was a difference in the histology of the tissues inside the implant areas near to the margin of the implant that absorbed blood during implant installation surgery, showed fibrous tissue with blood vessels, osteoblasts, collagenous fibers with osteoid formation, and tiny clusters of more mature hard tissue. In the center of the implant, where there was less absorbed blood, only fibrous tissue was observed. This finding is in line with the combined positron emission tomography - computed tomography examination with (18F)-fluoride marker, which demonstrated activity of the mineralizing bone by osteoblasts especially at the area near to the margin of the implant 10 months after implantation. Based on these promising reactions found in the bioactive glass containing fiber-reinforced composite implant that has been implanted for two years and three months, calvarial

  15. EFFECT OF SINTERING TEMPERATURE ON MICROSTRUCTURE AND IN-VITRO BEHAVIOR OF BIOACTIVE GLASS-CERAMICS

    Directory of Open Access Journals (Sweden)

    Hashmi M. U.

    2013-12-01

    Full Text Available In this work, powders of the composition (CaO 46- SiO2 34- P2O5 14.5- MgO 4- CaF2 1- MgF2 0.5 (wt. % were thoroughly mixed and melted in a muffle furnace. The melt was quenched in water to form glass. Three glass-ceramics were prepared by sintering glass samples at three different temperatures 850, 900 and 950°C according to the exothermal peaks of DTA. The DTA peaks correspond to the bioactive crystalline phases hydroxyapatite (HA and wollastonite as confirmed by the XRD data. Study of diameter-shrinkage co-efficient and bulk-density of samples revealed higher densification rate for the range 900 - 950°C than that for the range 850 - 900°C.SEM and optical microscope results illustrated a tendency towards closely packed structure and increasing grain size with the increase of sintering temperature. The samples were immersed in SBF for 30 days at room temperature for in-vitro evaluation.EDS analysis, showing the presence of carbon (C along with calcium (Ca and phosphorus (P suggests the formation of hydroxycarbonate-apatite (HCA phase that indicates the bioactivity of the material which increases with the increase of sintering temperature.

  16. Optimization of fluoride-containing bioactive glasses as a novel scolicidal agent adjunct to hydatid surgery.

    Science.gov (United States)

    Rostami, Ali; Mozafari, Masoud; Gholipourmalekabadi, Mazaher; Caicedo, Hector Hugo; Lasjerdi, Zohreh; Sameni, Marzieh; Samadikuchaksaraei, Ali

    2015-08-01

    We have presented a novel scolicidal agent made from fluoride-containing bioactive glass (FBG). The samples were characterized by XRD and the ion release behavior of the samples was evaluated at 37°C. The scolicidal activity, cellular response and antibacterial activity and biocompatibility of the different concentrations of the FBG (ranging from 0.5 to 2 mg ml(-1)) were evaluated in vitro and in vivo. The results showed an easy diffusion of the fluoride through the glass matrix in an F concentration-dependent manner. The FBG showed an intensive scolicidal property, so that toxicity effect begun from 5 min and the samples with 20, 10, 5 and 0% fluoride showed 98±2, 93±5.8, 76.2±6 and 5.8±1.7% scolicidal activity, respectively, after 8h exposing time. Our data revealed that scolicidal activity of the FBG increased with the increase of F ratio and concentrations of the bioactive glass. On the other hand, all the synthesized FBG samples found to be cyto-biocompatible when tested in vitro (MTT and LDH assays) and in vivo (no significant infiltration of inflammatory cells compared with control, p>0.05), and antibacterial against Escherichia coli, Staphylococcus aureus and Pseudomonas aeruginosa. The results demonstrated that the synthesized FBG might have a potential application in prevention of post-surgery infections, especially hydatidosis. Copyright © 2015 Elsevier B.V. All rights reserved.

  17. Fabrication and in vitro characterization of bioactive glass composite scaffolds for bone regeneration.

    Science.gov (United States)

    Poh, Patrina S P; Hutmacher, Dietmar W; Stevens, Molly M; Woodruff, Maria A

    2013-12-01

    Here we fabricate and characterize bioactive composite scaffolds for bone tissue engineering applications. 45S5 Bioglass® (45S5) or strontium-substituted bioactive glass (SrBG) were incorporated into polycaprolactone (PCL) and fabricated into 3D bioactive composite scaffolds utilizing additive manufacturing technology. We show that composite scaffolds (PCL/45S5 and PCL/SrBG) can be reproducibly manufactured with a scaffold morphology highly resembling that of PCL scaffolds. Additionally, micro-CT analysis reveals BG particles were homogeneously distributed throughout the scaffolds. Mechanical data suggested that PCL/45S5 and PCL/SrBG composite scaffolds have higher compressive Young's modulus compared to PCL scaffolds at similar porosity (∼75%). After 1 day in accelerated degradation conditions using 5M NaOH, PCL/SrBG, PCL/45S5 and PCL lost 48.6 ± 3.8%, 12.1 ± 1% and 1.6 ± 1% of the original mass, respectively. In vitro studies were conducted using MC3T3 cells under normal and osteogenic conditions. All scaffolds were shown to be non-cytotoxic, and supported cell attachment and proliferation. Our results also indicate that the inclusion of bioactive glass (BG) promotes precipitation of calcium phosphate on the scaffold surfaces which leads to earlier cell differentiation and matrix mineralization when compared to PCL scaffolds. However, as indicated by alkaline phosphatase activity, no significant difference in osteoblast differentiation was found between PCL/45S5 and PCL/SrBG scaffolds. These results suggest that PCL/45S5 and PCL/SrBG composite scaffolds show potential as next generation bone scaffolds.

  18. Aluminum-free glass-ionomer bone cements with enhanced bioactivity and biodegradability

    Energy Technology Data Exchange (ETDEWEB)

    Gomes, Filipa O.; Pires, Ricardo A., E-mail: rpires@dep.uminho.pt; Reis, Rui L.

    2013-04-01

    Al-free glasses of general composition 0.340SiO{sub 2}:0.300ZnO:(0.250-a-b)CaO:aSrO:bMgO:0.050Na{sub 2}O:0.060P{sub 2}O{sub 5} (a, b = 0.000 or 0.125) were synthesized by melt quenching and their ability to form glass-ionomer cements was evaluated using poly(acrylic acid) and water. We evaluated the influence of the poly(acrylic acid) molecular weight and glass particle size in the cement mechanical performance. Higher compressive strength (25 ± 5 MPa) and higher compressive elastic modulus (492 ± 17 MPa) were achieved with a poly(acrylic acid) of 50 kDa and glass particle sizes between 63 and 125 μm. Cements prepared with glass formulation a = 0.125 and b = 0.000 were analyzed after immersion in simulated body fluid; they presented a surface morphology consistent with a calcium phosphate coating and a Ca/P ratio of 1.55 (similar to calcium-deficient hydroxyapatite). Addition of starch to the cement formulation induced partial degradability after 8 weeks of immersion in phosphate buffer saline containing α-amylase. Micro-computed tomography analysis revealed that the inclusion of starch increased the cement porosity from 35% to 42%. We were able to produce partially degradable Al-free glass-ionomer bone cements with mechanical performance, bioactivity and biodegradability suitable to be applied on non-load bearing sites and with the appropriate physical characteristics for osteointegration upon partial degradation. Zn release studies (concentrations between 413 μM and 887 μM) evidenced the necessity to tune the cement formulations to reduce the Zn concentration in the surrounding environment. Highlights: ► We developed partially degradable, bioactive, Al-free glass-ionomer cements (GICs). ► Enhanced mechanical behavior was achieved using 63–125 μm glass particle size range. ► The highest mechanical resistance was obtained using poly(acrylic acid) of 50 kDa. ► Biodegradation was successfully tuned to start 8 weeks after GIC preparation. ► Zn

  19. Synthesis of bioactive and machinable miserite glass-ceramics for dental implant applications.

    Science.gov (United States)

    Saadaldin, Selma A; Dixon, S Jeffrey; Costa, Daniel O; Rizkalla, Amin S

    2013-06-01

    To synthesize and characterize machinable, bioactive glass-ceramics (GCs) suitable for dental implant applications. A glass in the SiO2-Al2O3-CaO-CaF2-K2O-B2O3-La2O3 system was synthesized by wet chemical methods, followed by calcination, melting and quenching. Crystallization kinetics were determined by differential thermal analysis (DTA). GC discs were produced by cold pressing of the glass powder and sintered using schedules determined by DTA. The crystalline phases and microstructure of GC samples were characterized by X-ray diffraction (XRD) and scanning electron microscopy (SEM), respectively. Dynamic Young's modulus (E), true hardness (Ho), fracture toughness (KIC) and brittleness index (BI) were evaluated. Bioactivity was studied by examining the formation of hydroxyapatite (HA) on the GC surfaces after soaking in simulated body fluid (SBF). Attachment and proliferation of MC3T3-E1 osteoblastic cells were assessed in vitro. Miserite [KCa5(Si2O7)(Si6O15)(OH)F] was the main crystalline phase of the GC with additional secondary phases. Microstructural studies revealed interlocking lath-like crystalline morphology. E, Ho, and KIC values for the GCs were 96±3 GPa, 5.27±0.26 GPa and 4.77±0.27 MPa m(0.5), respectively. The BI was found to be 1.11±0.05 μm(-0.5), indicating outstanding machinability. An HA surface layer was formed on the GC surfaces when soaked in SBF, indicating potential bioactivity. MC3T3-E1 cells exhibited attachment, spreading and proliferation on GC surfaces, demonstrating excellent biocompatibility. We present a novel approach for the synthesis of miserite GC with the physical and biological properties required for non-metallic dental implant applications. Copyright © 2013 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

  20. Preparation of Nanofibrous Structure of Mesoporous Bioactive Glass Microbeads for Biomedical Applications

    Directory of Open Access Journals (Sweden)

    Shiao-Wen Tsai

    2016-06-01

    Full Text Available A highly ordered, mesoporous (pore size 2~50 nm bioactive glass (MBG structure has a greater surface area and pore volume and excellent bone-forming bioactivity compared with traditional bioactive glasses (BGs. Hence, MBGs have been used in drug delivery and bone tissue engineering. MBGs can be developed as either a dense or porous block. Compared with a block, microbeads provide greater flexibility for filling different-shaped cavities and are suitable for culturing cells in vitro. In contrast, the fibrous structure of a scaffold has been shown to increase cell attachment and differentiation due to its ability to mimic the three-dimensional structure of natural extracellular matrices. Hence, the aim of this study is to fabricate MBG microbeads with a fibrous structure. First, a sol-gel/electrospinning technique was utilized to fabricate the MBG nanofiber (MBGNF structure. Subsequently, the MBGNF microbeads (MFBs were produced by an electrospraying technology. The results show that the diameter of the MFBs decreases when the applied voltage increases. The drug loading and release profiles and mechanisms of the MFBs were also evaluated. MFBs had a better drug entrapment efficiency, could reduce the burst release of tetracycline, and sustain the release over 10 days. Hence, the MFBs may be suitable drug carriers. In addition, the cellular attachment of MG63 osteoblast-like cells is significantly higher for MFBs than for glass microbeads after culturing for 4 h. The nanofibrous structure of MFBs could provide an appropriate environment for cellular spreading. Therefore, MFBs have great potential for use as a bone graft material in bone tissue engineering applications.

  1. Influence of Incorporating Fluoroapatite Nanobioceramic on the Compressive Strength and Bioactivity of Glass Ionomer Cement.

    Science.gov (United States)

    M, Khaghani; S, Alizadeh; A, Doostmohammadi

    2016-09-01

    In order to increase the performance of glass ionomer cement, it is reinforced with metal powders, short fibers, bioceramics and other materials. Fluoroapatite (Ca10(PO4)6F2) is found in dental enamel and is usually used in dental materials due to its good chemical and physical properties. In this study, the effects of the addition of synthesized fluoroapatite nanoceramic on the compressive strength and bioactivity of glass ionomer cement were investigated. The synthesized fluoroapatite nanoceramic particles (~ 70 nm) were incorporated into as-prepared glass ionomer powder and were characterized using X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR) and scanning electron microscopy (SEM). Moreover, the compressive strength values of the modified glass ionomer cements with 0, 1, 3 and 5 wt% of fluoroapatite were evaluated. Results showed that glass ionomer cement containing 3 wt% fluoroapatite nanoparticles exhibited the highest compressive strength (102.6 ± 4) compared to the other groups, including control group. Furthermore, FTIR and SEM investigations indicated that after soaking the glass ionomer cement- 3 wt% fluoroapatite composite in the simulated body fluid solution, the intensity of O-H, P-O and C-O absorption bands increased as a result of the formation of apatite layer on the surface of the sample, and the rather flat and homogeneous surface of the cement became more porous and inhomogeneous. Addition of synthesized nano-fluoroapatite to as-prepared glass ionomer cement enhanced the compressive strength as well as nucleation of the calcium phosphate layer on the surface of the composite. This makes it a good candidate for dentistry and orthopedic applications.

  2. Behavior study of the doped castor bean polymer rod with bioactive glass and hidroxyapatite in mice femur medullary canal.

    Science.gov (United States)

    Santos, Viviani Teixeira Dos; Facco, Gilberto Gonçalves; Ortiz, Hudman Cunha; Silva, Iandara Schettert da

    2017-02-01

    Purpose To evaluate the polymer doped rods behavior with bioactive glass and hydroxyapatite for possible application as a fracture fixing method. Methods Twenty eight Rattus norvegicus Wistar underwent bone defect for access to the femoral medullary canal and distributed into three experimental groups: group A - doped castor bean polymer with bioactive glass; group B - castor bean polymer and; group C - castor bean polymer doped with bioactive glass and hydroxyapatite. After 15 and 60 evaluation days, the femurs were removed and sent for histology and scanning electron microscopy. Results Initially mild and moderate inflammatory infiltrate is observed that decreases as time goes by, and the presence of connective tissue capsule around the graft in all groups. Regarding the biomaterials resorption little was observed. The implanted rods did not favor the osteoconductive process in the femoral medullary canal which was observed only in the C15 group. Conclusions The association of castor bean polymer, bioactive glass and hydroxyapatite was biocompatible and osteointegrable. The osteoconductive only occurred in the presence of hydroxyapatite and bioactive glass (C15 Group) and little biodegradation was observed.

  3. Micro PIXE-RBS for the study of Sr release at bioactive glass scaffolds/biological medium interface

    Energy Technology Data Exchange (ETDEWEB)

    Lacroix, Joséphine; Lao, Jonathan [Clermont Université, Université Blaise Pascal, CNRS/IN2P3, Laboratoire de Physique Corpusculaire, BP 80026, 63171 Aubière Cedex (France); Nedelec, Jean-Marie [Clermont Université, ENSCCF, Institut de Chimie de Clermont-Ferrand, BP 10448, 63000 Clermont-Ferrand (France); CNRS, UMR 6296, ICCF, 63171 Aubière (France); Jallot, Edouard, E-mail: jallot@clermont.in2p3.fr [Clermont Université, Université Blaise Pascal, CNRS/IN2P3, Laboratoire de Physique Corpusculaire, BP 80026, 63171 Aubière Cedex (France)

    2013-07-01

    Strontium is a very interesting element in bone regeneration as it can promote bone formation and limit bone resorption. Bone tissue engineering has a very high potential as a method for bone healing and it requires a 3D macroporous scaffold to serve as a support for cell growth. In that purpose, strontium containing bioactive glass foams made with the sol–gel foaming process are very promising scaffolds as they combine the high bioactivity of bioactive glasses, the beneficial effects of strontium on bone growth and a structure that would allow cell adhesion, cell invasion and vascularization. This paper reports the synthesis of such a material and its in vitro bioactivity study. The release of strontium ions from the material to the biological medium occurs quickly, as shown by ICP-AES results, with the delivery of quantities of Sr ions that should be adequate for bone regeneration. Ion microbeam techniques evidence a very specific behavior of strontium: it is rapidly removed from the inner part of the material but remains in the calcium phosphate layer that is deposited on the surface of the foam pores. It reveals the particular behavior of glass foams compared to other materials suitable for implantation like glass powders of same composition and highlights the interest of ion microbeam techniques in the study of strontium-containing bioactive glass scaffolds.

  4. Mesoporous bioactive glass nanolayer-functionalized 3D-printed scaffolds for accelerating osteogenesis and angiogenesis

    Science.gov (United States)

    Zhang, Yali; Xia, Lunguo; Zhai, Dong; Shi, Mengchao; Luo, Yongxiang; Feng, Chun; Fang, Bing; Yin, Jingbo; Chang, Jiang; Wu, Chengtie

    2015-11-01

    The hierarchical microstructure, surface and interface of biomaterials are important factors influencing their bioactivity. Porous bioceramic scaffolds have been widely used for bone tissue engineering by optimizing their chemical composition and large-pore structure. However, the surface and interface of struts in bioceramic scaffolds are often ignored. The aim of this study is to incorporate hierarchical pores and bioactive components into the bioceramic scaffolds by constructing nanopores and bioactive elements on the struts of scaffolds and further improve their bone-forming activity. Mesoporous bioactive glass (MBG) modified β-tricalcium phosphate (MBG-β-TCP) scaffolds with a hierarchical pore structure and a functional strut surface (~100 nm of MBG nanolayer) were successfully prepared via 3D printing and spin coating. The compressive strength and apatite-mineralization ability of MBG-β-TCP scaffolds were significantly enhanced as compared to β-TCP scaffolds without the MBG nanolayer. The attachment, viability, alkaline phosphatase (ALP) activity, osteogenic gene expression (Runx2, BMP2, OPN and Col I) and protein expression (OPN, Col I, VEGF, HIF-1α) of rabbit bone marrow stromal cells (rBMSCs) as well as the attachment, viability and angiogenic gene expression (VEGF and HIF-1α) of human umbilical vein endothelial cells (HUVECs) in MBG-β-TCP scaffolds were significantly upregulated compared with conventional bioactive glass (BG)-modified β-TCP (BG-β-TCP) and pure β-TCP scaffolds. Furthermore, MBG-β-TCP scaffolds significantly enhanced the formation of new bone in vivo as compared to BG-β-TCP and β-TCP scaffolds. The results suggest that application of the MBG nanolayer to modify 3D-printed bioceramic scaffolds offers a new strategy to construct hierarchically porous scaffolds with significantly improved physicochemical and biological properties, such as mechanical properties, osteogenesis, angiogenesis and protein expression for bone tissue

  5. Pore characterisation and interconnectivity studies on bioactive 58 S sol-gel glass

    Energy Technology Data Exchange (ETDEWEB)

    Cook, R.; Watson, T.; Robinson, P. [Thomas Dental Inst., London (United Kingdom). Microscopy and Imaging Dept.; Fielder, E.; Hench, L.L. [Imperial Coll. of Science, Technology and Medicine, London (United Kingdom). Dept. of Materials

    2001-07-01

    The interconnecting pore network of bioactive 58S sol-gel glass is a vital structural characteristic requiring investigation, as in vivo this will provide the route of tissue fluid ingress and ultimately, the sites for early cell proliferation and osteogenesis. To characterise and visualise micropore (<20A) to macropore (>500A) dimension ranges, five complementary analytical methods were applied to 58S sol-gel monoliths, each resolving different characteristics of the pore network. Nitrogen porosimetry best resolved micro and smaller mesopores (20-500A), supplemented by helium ultra-pycnometry data. Mercury intrusion porosimetry was employed to characterise the meso and small macropores. SEM and confocal microscope imaging of the residual mercury within the matrix provided the first visual evidence of pores within the gel-glass interstices. The network's patency was clearly demonstrated by imaging fluorochrome-labelled command-set dental dentine bonding monomers, traversing the matrix. (orig.)

  6. In vitro study of improved wound-healing effect of bioactive borate-based glass nano-/micro-fibers

    Energy Technology Data Exchange (ETDEWEB)

    Yang, Qingbo [Department of Chemistry, Missouri University of Science and Technology, Rolla, MO 65409 (United States); Center for Biomedical Science and Engineering (CBSE), Missouri University of Science and Technology, Rolla, MO 65409 (United States); Center for Single Nanoparticle, Single Cell and Single Molecule Monitoring (CS3M), Missouri University of Science and Technology, Rolla, MO 65409 (United States); Chen, Sisi [Department of Chemistry, Missouri University of Science and Technology, Rolla, MO 65409 (United States); Center for Biomedical Science and Engineering (CBSE), Missouri University of Science and Technology, Rolla, MO 65409 (United States); Shi, Honglan [Department of Chemistry, Missouri University of Science and Technology, Rolla, MO 65409 (United States); Center for Biomedical Science and Engineering (CBSE), Missouri University of Science and Technology, Rolla, MO 65409 (United States); Center for Single Nanoparticle, Single Cell and Single Molecule Monitoring (CS3M), Missouri University of Science and Technology, Rolla, MO 65409 (United States); Xiao, Hai [Department of Electrical and Computer Engineering, Clemson University, Clemson, SC 29634 (United States); Ma, Yinfa, E-mail: yinfa@mst.edu [Department of Chemistry, Missouri University of Science and Technology, Rolla, MO 65409 (United States); Center for Biomedical Science and Engineering (CBSE), Missouri University of Science and Technology, Rolla, MO 65409 (United States); Center for Single Nanoparticle, Single Cell and Single Molecule Monitoring (CS3M), Missouri University of Science and Technology, Rolla, MO 65409 (United States)

    2015-10-01

    Because of the promising wound-healing capability, bioactive glasses have been considered as one of the next generation hard- and soft-tissue regeneration materials. The lack of understanding of the substantial mechanisms, however, indicates the need for further study on cell–glass interactions to better interpret the rehabilitation capability. In the present work, three bioactive glass nano-/micro-fibers, silicate-based 45S5, borate-based 13-93B3 and 1605 (additionally doped with copper oxide and zinc oxide), were firstly compared for their in vitro soaking/conversion rate. The results of elemental monitoring and electron microscopic characterization demonstrated that quicker ion releasing and glass conversion occurred in borate-based fibers than that of silicate-based one. This result was also reflected by the formation speed of hydroxyapatite (HA). This process was further correlated with original boron content and surrounding rheological condition. We showed that an optimal fiber pre-soaking time (or an ideal dynamic flow rate) should exist to stimulate the best cell proliferation and migration ability. Moreover, 13-93B3 and 1605 fibers showed different glass conversion and biocompatibility properties as well, indicating that trace amount variation in composition can also influence fiber's bioactivity. In sum, our in vitro rheological module closely simulated in vivo niche environment and proved a potentially improved wound-healing effect by borate-based glass fibers, and the results shall cast light on future improvement in bioactive glass fabrication. - Highlights: • Bioactive glass nano-/micro-materials were effectively used for tissue wound healing. • The wound-healing effects of silicate-based 45S5, borate-based 13-93B3 and 1605 fibers were investigated. • Glass conversion rates were compared under either static or dynamic-flow modes. • Glass compositions and flow rates greatly influenced bioactivity and cell migration. • These results can

  7. DISSOLUTION BEHAVIOR OF BIOACTIVE GLASS CERAMICS WITH DIFFERENT CaO/MgO RATIOS

    Directory of Open Access Journals (Sweden)

    MUHAMMAD USMAN HASHMI

    2010-03-01

    Full Text Available In this work, powders of three different compositions, each having 34 SiO2-14.5 P2O5-1 CaF2-0.5 MgF (% wt and ratio of CaO/MgO varying from 11.5:1 to 1:11.5 were thoroughly mixed and melted under oxy-acetylene flame in a fire clay crucible that made the glass formation cheaper in time and cost. The melt of each composition was quenched in water to form three different glasses. Every glass was sintered at 950°C to form three glass ceramics named G1, G2 and G3 respectively. To study the dissolution behavior, each sample was immersed in a simulated body fluid (SBF for 2, 5, 10, 20 and 25 days at room temperature. Thin film XRD analysis revealed that the samples with larger CaO/MgO ratio exhibited better bioactivity. pH of SBF increased efficiently in case of G1 whereas in case of G2 and G3, this increase was slower due to greater amount of MgO. The concentrations of Ca, P, Mg and Si ions were measured by Atomic Absorption Spectroscopy. EDS analysis showed the increase in P and Ca ions and presence of C in G1 after 5 days immersion and after 10 days, in case of G2 indicating the higher formation rate of hydroxycarbonate Apatite layer in G1 as compared to G2 due to greater CaO/MgO ratio whereas in G3 Mg-hydroxycarbonate apatite (Ca(Mg5(CO3(PO43(OH (heneuite layer was recognized after 20 days showing the least bioactivity due to very large amount of Mg and the least CaO/MgO ratio.

  8. Role of glass structure in defining the chemical dissolution behavior, bioactivity and antioxidant properties of zinc and strontium co-doped alkali-free phosphosilicate glasses.

    Science.gov (United States)

    Kapoor, Saurabh; Goel, Ashutosh; Tilocca, Antonio; Dhuna, Vikram; Bhatia, Gaurav; Dhuna, Kshitija; Ferreira, José M F

    2014-07-01

    We investigated the structure-property relationships in a series of alkali-free phosphosilicate glass compositions co-doped with Zn(2+) and Sr(2+). The emphasis was laid on understanding the structural role of Sr(2+) and Zn(2+) co-doping on the chemical dissolution behavior of glasses and its impact on their in vitro bioactivity. The structure of glasses was studied using molecular dynamics simulations in combination with solid state nuclear magnetic resonance spectroscopy. The relevant structural properties are then linked to the observed degradation behavior, in vitro bioactivity, osteoblast proliferation and oxidative stress levels. The apatite-forming ability of glasses has been investigated by X-ray diffraction, infrared spectroscopy and scanning electron microscopy-energy-dispersive spectroscopy after immersion of glass powders/bulk in simulated body fluid (SBF) for time durations varying between 1h and 14 days, while their chemical degradation has been studied in Tris-HCl in accordance with ISO 10993-14. All the glasses exhibit hydroxyapatite formation on their surface within 1-3h of their immersion in SBF. The cellular responses were observed in vitro on bulk glass samples using human osteosarcoma MG63 cell line. The dose-dependent cytoprotective effect of glasses with respect to the concentration of zinc and strontium released from the glasses is also discussed. Copyright © 2014 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

  9. Clinical Applications of S53P4 Bioactive Glass in Bone Healing and Osteomyelitic Treatment: A Literature Review

    Directory of Open Access Journals (Sweden)

    N. A. P. van Gestel

    2015-01-01

    Full Text Available Nowadays, S53P4 bioactive glass is indicated as a bone graft substitute in various clinical applications. This review provides an overview of the current published clinical results on indications such as craniofacial procedures, grafting of benign bone tumour defects, instrumental spondylodesis, and the treatment of osteomyelitis. Given the reported results that are based on examinations, such as clinical examinations by the surgeons, radiographs, CT, and MRI images, S53P4 bioactive glass may be beneficial in the various reported applications. Especially in craniofacial reconstructions like mastoid obliteration and orbital floor reconstructions, in grafting bone tumour defects, and in the treatment of osteomyelitis very promising results are obtained. Randomized clinical trials need to be performed in order to determine whether bioactive glass would be able to replace the current golden standard of autologous bone usage or with the use of antibiotic containing PMMA beads (in the case of osteomyelitis.

  10. Antimicrobial thin films based on ayurvedic plants extracts embedded in a bioactive glass matrix

    Science.gov (United States)

    Floroian, L.; Ristoscu, C.; Candiani, G.; Pastori, N.; Moscatelli, M.; Mihailescu, N.; Negut, I.; Badea, M.; Gilca, M.; Chiesa, R.; Mihailescu, I. N.

    2017-09-01

    Ayurvedic medicine is one of the oldest medical systems. It is an example of a coherent traditional system which has a time-tested and precise algorithm for medicinal plant selection, based on several ethnopharmacophore descriptors which knowledge endows the user to adequately choose the optimal plant for the treatment of certain pathology. This work aims for linking traditional knowledge with biomedical science by using traditional ayurvedic plants extracts with antimicrobial effect in form of thin films for implant protection. We report on the transfer of novel composites from bioactive glass mixed with antimicrobial plants extracts and polymer by matrix-assisted pulsed laser evaporation into uniform thin layers onto stainless steel implant-like surfaces. The comprehensive characterization of the deposited films was performed by complementary analyses: Fourier transformed infrared spectroscopy, glow discharge optical emission spectroscopy, scanning electron microscopy, atomic force microscopy, electrochemical impedance spectroscopy, UV-VIS absorption spectroscopy and antimicrobial tests. The results emphasize upon the multifunctionality of these coatings which allow to halt the leakage of metal and metal oxides into the biological fluids and eventually to inner organs (by polymer use), to speed up the osseointegration (due to the bioactive glass use), to exert antimicrobial effects (by ayurvedic plants extracts use) and to decrease the implant price (by cheaper stainless steel use).

  11. Development of sol-gel bioactive glass for hard tissue regeneration

    Science.gov (United States)

    Noor, Siti Noor Fazliah Mohd; Zain, Nurul Shazwani Mohd; Wei, Poh Yong; Azizan, Nur Syazana; Mohamad, Hasmaliza

    2016-12-01

    The regeneration of hard tissues requires various contributing factors such as cells, scaffolds and growth factors. Bioactive glasses are known for its properties to stimulate hard tissue regeneration. In this study, sol-gel bioactive glasses (BG) were prepared and characterized. Sol-gel BG powders having particle size less than 25 µm were incubated with cell culture medium for 4 hours at 37°C on continuous rolling, and then the medium was filtered using 0.22 µm syringe filters. Prior to use, the SGBG-conditioned media were supplemented with 10% (v/v) fetal bovine serum and 1% (v/v) antibiotic-antimycotic, and were allowed to equilibrate overnight inside a CO2 incubator. The human dental pulp stem cells (DPSC) were incubated with the BG-conditioned media and their viability and proliferation were assessed at day 1, 2, 4 and 7 using Alamar Blue and MTT assays. The results showed that BG at various powders to liquid ratio concentrations promoted DPSC growth. The BG have potential to be used for hard tissue regeneration especially in the field of regenerative dentistry.

  12. MECHANISM OF BIOACTIVITY OF LS2-FA GLASS-CERAMICS IN SBF AND DMEM MEDIUM

    Directory of Open Access Journals (Sweden)

    GABRIELA LUTIŠANOVÁ

    2012-09-01

    Full Text Available In this paper, the results of in vitro bioactivity of glass-ceramics in the Li2O–SiO2–CaO–P2O5–CaF2 (shorthand LS2-FA system immersed in two media (simulated body fluid (SBF and Dulbecco’s modified Eagle’s medium (DMEM are compared. Microprobe (EPMA and Scanning Electron Microscopy (SEM were used to detect the presence of a new phase on the surface and to characterize its layer. Inductively coupled plasma (ICP was used to monitor ion concentration changes in SBF with immersion time. The results show, that during the assay in vitro behaviour tests, the surface of the sample was partially dissolved and released of Si4+, Ca2+ and Li+ ions were released into the SBF medium. The results of surface characterization after in vitro tests revealed difference in the bioactivity of glass-ceramics with various time of immersion in SBF and DMEM. For the formation of an apatite-layer in an earlier testing period (1, 3 and 7 days, a pronounced difference was not observed between SBF and DMEM immersion. In the longer testing period in SBF (28 days, the apatite-layer was developed by periodic deposition of spherical bullets that covers the whole surface. The use of the acellular culture medium DMEM resulted in a delay at the start of precipitation.

  13. Synthesis, characterization and in vitro study of magnetic biphasic calcium sulfate-bioactive glass

    Energy Technology Data Exchange (ETDEWEB)

    Goh, Yi-Fan; Akram, Muhammad; Alshemary, Ammar Z. [Department of Chemistry, Faculty of Science, Universiti Teknologi Malaysia, 81310 UTM Skudai, Johor, Darul Ta' zim (Malaysia); Hussain, Rafaqat, E-mail: rafaqat@kimia.fs.utm.my [Ibnu Sina Institute for Fundamental Science Studies, Universiti Teknologi Malaysia, 81310 UTM Skudai, Johor Darul Ta' zim (Malaysia)

    2015-08-01

    Calcium sulfate-bioactive glass (CSBG) composites doped with 5, 10 and 20 mol% Fe were synthesized using quick alkali sol–gel method. X-ray diffraction (XRD) data of samples heated at 700 °C revealed the presence of anhydrite, while field emission scanning electron microscopy (FESEM) and energy dispersive X-ray (EDX) characterization confirmed the formation of nano-sized CSBGs. The UV–vis studies confirmed that the main iron species in 5% Fe and 10% Fe doped CSBGs were tetrahedral Fe(III) whereas that in 20% Fe doped CSBG were extra-framework FeO{sub x} oligomers or iron oxide phases. Measurement of magnetic properties of the samples by vibrating sample magnetometer (VSM) showed very narrow hysteresis loop with zero coercivity and remanence for 10% Fe and 20% Fe doped CSBG, indicating that they are superparamagnetic in nature. All samples induced the formation of apatite layer with Ca/P ratio close to the stoichiometric HA in simulated body fluid (SBF) assessment. - Highlights: • Biphasic calcium sulphate-bioactive glass containing iron was prepared. • Composite bioglass was superparamagnetic in nature. • All samples promoted the growth of apatite layer with Ca/P close to 1.67.

  14. SYNTHESIS AND CHARACTERIZATION OF BIOACTIVE GLASS/FORSTERITE NANOCOMPOSITES FOR BONE AND DENTAL IMPLANTS

    Directory of Open Access Journals (Sweden)

    REZA KAMALIAN

    2012-12-01

    Full Text Available In this research, bioactive glass (BG of the type CaO–P2O5–SiO2 and nanocrystalline forsterite (NF bioceramic were successfully synthesized via sol–gel processing method. Heat-treatment process was done to obtain phase-pure nanopowders. After characterization of each sample, the nanocomposite samples were prepared by cold pressing method and sintered at 1000°C. The samples were fully characterized by X-ray powder diffraction (XRD, scanning electron microscope (SEM, energy dispersive spectroscopy (EDX, Fourier transform infrared spectroscopy (FTIR analyses. The average nanocrystallite size was determined using the Debye-Scherrer’s formula 19.6 nm. The bioactivity was examined in vitro with respect to the ability of hydroxyapatite (HAp layer to form on the surfaces as a result of contact with simulated body fluid (SBF. According to the obtained results, the prepared nanocomposite enhances the fracture toughness of the BG matrix without deteriorating its intrinsic properties as bioactivity.

  15. New PMMA-co-EHA glass-filled composites for biomedical applications: Mechanical properties and bioactivity.

    Science.gov (United States)

    Lopes, Poliana; Corbellini, Marcelo; Ferreira, Bárbara Leite; Almeida, Nuno; Fredel, Márcio; Fernandes, Maria Helena; Correia, Rui

    2009-01-01

    A bioactive glass of the 3CaO.P(2)O(5)-MgO-SiO(2) system was incorporated as a filler into poly(methylmethacrylate)-co-(ethylhexylacrylate) (PMMA-co-EHA) copolymer. The effect of filler proportion (0, 30, 40 and 50wt.%) on the bending properties was evaluated and a maximum flexural strength of 29MPa coupled with an elastic modulus of 1.1GPa was obtained at an intermediate filler concentration (30wt.%). These values are slightly higher than those usually reported for human cancellous bone. The in vitro bioactivity was assessed by determining the changes in surface morphology and composition after soaking in simulated body fluid (SBF, Kokubo solution). Inductively coupled plasma was used to trace the evolution of ionic concentrations in the SBF solution, namely Ca and P. X-ray diffraction and scanning electron microscopy confirmed the growth of spherical calcium phosphate aggregates on the surface of composites, indicating that the composites are potentially bioactive.

  16. Investigating the addition of SiO₂-CaO-ZnO-Na₂O-TiO₂ bioactive glass to hydroxyapatite: Characterization, mechanical properties and bioactivity.

    Science.gov (United States)

    Yatongchai, Chokchai; Placek, Lana M; Curran, Declan J; Towler, Mark R; Wren, Anthony W

    2015-11-01

    Hydroxyapatite (Ca10(PO4)6(OH)2) is widely investigated as an implantable material for hard tissue restoration due to its osteoconductive properties. However, hydroxyapatite in bulk form is limited as its mechanical properties are insufficient for load-bearing orthopedic applications. Attempts have been made to improve the mechanical properties of hydroxyapatite, by incorporating ceramic fillers, but the resultant composite materials require high sintering temperatures to facilitate densification, leading to the decomposition of hydroxyapatite into tricalcium phosphate, tetra-calcium phosphate and CaO phases. One method of improving the properties of hydroxyapatite is to incorporate bioactive glass particles as a second phase. These typically have lower softening points which could possibly facilitate sintering at lower temperatures. In this work, a bioactive glass (SiO2-CaO-ZnO-Na2O-TiO2) is incorporated (10, 20 and 30 wt%) into hydroxyapatite as a reinforcing phase. X-ray diffraction confirmed that no additional phases (other than hydroxyapatite) were formed at a sintering temperature of 560 ℃ with up to 30 wt% glass addition. The addition of the glass phase increased the % crystallinity and the relative density of the composites. The biaxial flexural strength increased to 36 MPa with glass addition, and there was no significant change in hardness as a function of maturation. The pH of the incubation media increased to pH 10 or 11 through glass addition, and ion release profiles determined that Si, Na and P were released from the composites. Calcium phosphate precipitation was encouraged in simulated body fluid with the incorporation of the bioactive glass phase, and cell culture testing in MC-3T3 osteoblasts determined that the composite materials did not significantly reduce cell viability. © The Author(s) 2015.

  17. Hybrid macroporous gelatin/bioactive-glass/nanosilver scaffolds with controlled degradation behavior and antimicrobial activity for bone tissue engineering.

    Science.gov (United States)

    Yazdimamaghani, M; Vashaee, D; Assefa, S; Walker, K J; Madihally, S V; Köhler, G A; Tayebi, L

    2014-06-01

    A new composition of gelatin/bioactive-glass/silver nanoparticle was synthesized and employed to prepare antibacterial macroporous scaffolds with potential applications in bone tissue engineering. A set of macroporous nanocomposite scaffolds were developed from an aqueous solution of gelatin by freeze-drying and crosslinking using genipin at ambient temperature. Silver nanoparticles were successfully synthesized in situ in gelatin solution by heat treatment reduction as a simple and "green" method in which gelatin acted as a natural reducing and stabilizing agent. The effect of the incorporation of the bioactive-glass and the silver nanoparticle concentration on the physicochemical properties of the scaffolds, such as the gel fraction, porosity, in vitro enzyme degradation, morphology, and swelling behavior was studied. Furthermore, the in vitro viability of human mesenchymal stem cells (hMSC) and the antibacterial activity against gram-negative Escherichia coli and gram-positive Staphylococcus aureus were tested on the scaffolds. It was found that upon the addition of silver nanoparticles the porosity, pore size, swelling, and antibacterial properties were enhanced. The silver nanoparticles increased the in vitro enzyme degradation in samples without bioactive-glass; however, the degradation was remarkably reduced by addition of bioactive-glass. In addition, formation of apatite particles, the main inorganic constituent of the bone, on the surface of the bioactive-glass containing scaffolds were confirmed after immersion in simulated body fluid (SBF). The viability of hMSC on the scaffold suggested that gelatin/bioactive-glass/nanosilver scaffolds can be used as an antibacterial scaffolds.

  18. Development of HydroxyCarbonate Apatite on hybrid polymers used in fixed restorations modified by bioactive glass

    Science.gov (United States)

    Georgantzi, B.; Papadopoulou, L.; Zorba, T.; Garefis, P.; Paraskevopoulos, K.; Koidis, P.

    2004-03-01

    The incorporation of a bioactive glass in the structure of hybrid polymers used in dentistry for the construction of fixed prosthetic restorations could induce the expression of bioactivity, leading to the possibility of periodontal tissues reattachment. Hybrid polymer specimens and polymer specimens modified by bioactive glass were prepared and used as control for the surface morphology examination by Scanning Electron Microscopy with associated Dispersive Spectroscopy Analysis (SEM-EDS) and for surface characterization with Fourier Transform Infrared Spectroscopy (FTIR). Furthermore, hybrid polymer specimens modified by bioactive glass were immersed in simulated body fluid (SBF) at 37 °C for different time intervals and were examined by SEM-EDS and FTIR. After 4 days immersion time a dense and continuous apatite layer covered almost the entire modified surface of the specimens. The molar Ca/P ratio reached the value of 1.79. The apatite layer showed a thickness of 1?m and was attached to the substrate, while bioactive glass particles were still present in polymer mass.

  19. The In Vitro Bioactivity, Degradation, and Cytotoxicity of Polymer-Derived Wollastonite-Diopside Glass-Ceramics

    Science.gov (United States)

    Juraski, Amanda De Castro; Dorion Rodas, Andrea Cecilia; Elsayed, Hamada; Bernardo, Enrico; Oliveira Soares, Viviane; Daguano, Juliana

    2017-01-01

    Ca-Mg silicates are receiving a growing interest in the field of bioceramics. In a previous study, wollastonite-diopside (WD) glass-ceramics were successfully prepared by a new processing route, consisting of the heat treatment of a silicone resin embedding reactive oxide particles and a Ca/Mg-rich glass. The in vitro degradation, bioactivity, and cell response of these new WD glass-ceramics, fired at 900–1100 °C for 1 h, as a function of the Ca/Mg-rich glass content, are the aim of this investigation The results showed that WD glass-ceramics from formulations comprising different glass contents (70–100% at 900 °C, 30% at 1100 °C) exhibit the formation of an apatite-like layer on their surface after immersion in SBF for seven days, thus confirming their surface bioactivity. The XRD results showed that these samples crystallized, mainly forming wollastonite (CaSiO3) and diopside (CaMgSi2O6), but combeite (Na2Ca2Si3O9) crystalline phase was also detected. Besides in vitro bioactivity, cytotoxicity and osteoblast adhesion and proliferation tests were applied after all characterizations, and the formulation comprising 70% glass was demonstrated to be promising for further in vivo studies. PMID:28772783

  20. Investigating in vitro bioactivity and magnetic properties of the ferrimagnetic bioactive glass–ceramic fabricated using soda-lime–silica waste glass

    Energy Technology Data Exchange (ETDEWEB)

    Abbasi, M. [Department of Materials Science and Engineering, School of Engineering, Shiraz University, Zand Street, Shiraz (Iran, Islamic Republic of); Hashemi, B., E-mail: hashemib@shirazu.ac.ir [Department of Materials Science and Engineering, School of Engineering, Shiraz University, Zand Street, Shiraz (Iran, Islamic Republic of); Shokrollahi, H. [Electroceramics Group, Materials Science and Engineering Department, Shiraz University of Technology, Shiraz (Iran, Islamic Republic of)

    2014-04-01

    The main purpose of the current research is the production and characterization of a ferrimagnetic bioactive glass–ceramic prepared through the solid-state reaction method using soda-lime–silica waste glass as the main raw material. In comparison with the conventional route, that is, the melt-quenching and subsequent heat treatment, the present work is an economical technique. Structural, thermal and magnetic properties of the samples were examined by X-ray diffraction (XRD), differential thermal analysis (DTA) and vibrating sample magnetometer (VSM). The in vitro test was utilized to assess the bioactivity level of the samples by Hanks' solution as simulated body fluid (SBF). The apatite surface layer formation was examined by the scanning electron microscopy (SEM) equipped with energy dispersive spectroscopy (EDS). The calcium ion concentration in the solutions was measured by atomic absorption spectroscopy (AAS). VSM results revealed that with the addition of 5–20 wt% strontium hexaferrite to bioactive glass–ceramics, the ferrimagnetic bioactive glass–ceramics with hysteresis losses between 7024 and 75,852 erg/g were obtained. The in vitro test showed that the onset formation time of hydroxyapatite layer on the surface of the samples was 14 days and after 30 days, this layer was completed. - Highlights: • A novel ferrimagnetic bioactive glass–ceramic was synthesized by an incorporation method. • The bioactive part was synthesized by the solid-state reaction method using soda-lime–silica waste glass. • The doping of SrFe{sub 12}O{sub 19} to Bioglass{sup ®} 45S5 glass–ceramic is likely to decrease bioactivity.

  1. Evaluating the critical strain energy release rate of bioactive glass coatings on Ti6Al4V substrates after degradation.

    Science.gov (United States)

    Matinmanesh, A; Li, Y; Nouhi, A; Zalzal, P; Schemitsch, E H; Towler, M R; Papini, M

    2018-02-01

    It has been reported that the adhesion of bioactive glass coatings to Ti6Al4V reduces after degradation, however, this effect has not been quantified. This paper uses bilayer double cantilever (DCB) specimens to determine GIC and GIIC, the critical mode I and mode II strain energy release rates, respectively, of bioactive coating/Ti6Al4V substrate systems degraded to different extents. Three borate-based bioactive glass coatings with increasing amounts of incorporated SrO (0, 15 and 25mol%) were enamelled onto Ti6Al4V substrates and then immersed in de-ionized water for 2, 6 and 24h. The weight loss of each glass composition was measured and it was found that the dissolution rate significantly decreased with increasing SrO content. The extent of dissolution was consistent with the hypothesis that the compressive residual stress tends to reduce the dissolution rate of bioactive glasses. After drying, the bilayer DCB specimens were created and subjected to nearly mode I and mode II fracture tests. The toughest coating/substrate system (one composed of the glass containing 25mol% SrO) lost 80% and 85% of its GIC and GIIC, respectively, in less than 24h of degradation. The drop in GIC and GIIC occurred even more rapidly for other coating/substrate systems. Therefore, degradation of borate bioactive glass coatings is inversely related to their fracture toughness when coated onto Ti6A4V substrates. Finally, roughening the substrate was found to be inconsequential in increasing the toughness of the system as the fracture toughness was limited by the cohesive toughness of the glass itself. Copyright © 2017 Elsevier Ltd. All rights reserved.

  2. Fabrication of 13-93 bioactive glass scaffolds for bone tissue engineering using indirect selective laser sintering.

    Science.gov (United States)

    Kolan, Krishna C R; Leu, Ming C; Hilmas, Gregory E; Brown, Roger F; Velez, Mariano

    2011-06-01

    Bioactive glasses are promising materials for bone scaffolds due to their ability to assist in tissue regeneration. When implanted in vivo, bioactive glasses can convert into hydroxyapatite, the main mineral constituent of human bone, and form a strong bond with the surrounding tissues, thus providing an advantage over polymer scaffold materials. Bone scaffold fabrication using additive manufacturing techniques can provide control over pore interconnectivity during fabrication of the scaffold, which helps in mimicking human trabecular bone. 13-93 glass, a third-generation bioactive material designed to accelerate the body's natural ability to heal itself, was used in the research described herein to fabricate bone scaffolds using the selective laser sintering (SLS) process. 13-93 glass mixed with stearic acid (as the polymer binder) by ball milling was used as the powder feedstock for the SLS machine. The fabricated green scaffolds underwent binder burnout to remove the stearic acid binder and were then sintered at temperatures between 675 °C and 695 °C. The sintered scaffolds had pore sizes ranging from 300 to 800 µm with 50% apparent porosity and an average compressive strength of 20.4 MPa, which is excellent for non-load bearing applications and among the highest reported for an interconnected porous scaffold fabricated with bioactive glasses using the SLS process. The MTT labeling experiment and measurements of MTT formazan formation are evidence that the rough surface of SLS scaffolds provides a cell-friendly surface capable of supporting robust cell growth.

  3. Biofilm formation affects surface properties of novel bioactive glass-containing composites.

    Science.gov (United States)

    Hyun, Hong-Keun; Salehi, Satin; Ferracane, Jack L

    2015-12-01

    This study investigated the effects of bacterial biofilm on the surface properties of novel bioactive glass (BAG)-containing composites of different initial surface roughness. BAG (65 mol% Si; 4% P; 31% Ca) and BAG-F (61% Si; 31% Ca; 4% P; 3% F; 1% B) were synthesized by the sol-gel method and micronized (size ∼0.1-10 μm). Composites with 72wt% total filler load were prepared by replacing 15% of the silanized Sr glass with BAG, BAG-F, or silanized silica. Specimens (n=10/group) were light-cured and divided into 4 subgroups of different surface roughness by wet polishing with 600 and then up to 1200, 2400, or 4000 grit SiC. Surface roughness (SR), gloss, and Knoop microhardness were measured before and after incubating in media with or without a Streptococcus mutans (UA 159) biofilm for 2 weeks. Results were analyzed with ANOVA/Tukey's test (α=0.05). The SR of the BAG-containing composites with the smoothest surfaces (2400/4000 grit) increased in media or bacteria; the SR of the roughest composites (600 grit) decreased. The gloss of the smoothest BAG-containing composites decreased in bacteria and media-only, but more in media-alone. The microhardness of all of the composites decreased with exposure to media or bacteria, with BAG-containing composites affected more than the control. Exposure to bacterial biofilm and its media produced enhanced roughness and reduced gloss and surface microhardness of highly polished dental composites containing a bioactive glass additive, which could affect further biofilm formation, as well as the esthetics, of restorations made from such a material. Copyright © 2015 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

  4. Modifications in Glass Ionomer Cements: Nano-Sized Fillers and Bioactive Nanoceramics.

    Science.gov (United States)

    Najeeb, Shariq; Khurshid, Zohaib; Zafar, Muhammad Sohail; Khan, Abdul Samad; Zohaib, Sana; Martí, Juan Manuel Nuñez; Sauro, Salvatore; Matinlinna, Jukka Pekka; Rehman, Ihtesham Ur

    2016-07-14

    Glass ionomer cements (GICs) are being used for a wide range of applications in dentistry. In order to overcome the poor mechanical properties of glass ionomers, several modifications have been introduced to the conventional GICs. Nanotechnology involves the use of systems, modifications or materials the size of which is in the range of 1-100 nm. Nano-modification of conventional GICs and resin modified GICs (RMGICs) can be achieved by incorporation of nano-sized fillers to RMGICs, reducing the size of the glass particles, and introducing nano-sized bioceramics to the glass powder. Studies suggest that the commercially available nano-filled RMGIC does not hold any significant advantage over conventional RMGICs as far as the mechanical and bonding properties are concerned. Conversely, incorporation of nano-sized apatite crystals not only increases the mechanical properties of conventional GICs, but also can enhance fluoride release and bioactivity. By increasing the crystallinity of the set matrix, apatites can make the set cement chemically more stable, insoluble, and improve the bond strength with tooth structure. Increased fluoride release can also reduce and arrest secondary caries. However, due to a lack of long-term clinical studies, the use of nano-modified glass ionomers is still limited in daily clinical dentistry. In addition to the in vitro and in vivo studies, more randomized clinical trials are required to justify the use of these promising materials. The aim of this paper is to review the modification performed in GIC-based materials to improve their physicochemical properties.

  5. Modifications in Glass Ionomer Cements: Nano-Sized Fillers and Bioactive Nanoceramics

    Science.gov (United States)

    Najeeb, Shariq; Khurshid, Zohaib; Zafar, Muhammad Sohail; Khan, Abdul Samad; Zohaib, Sana; Martí, Juan Manuel Nuñez; Sauro, Salvatore; Matinlinna, Jukka Pekka; Rehman, Ihtesham Ur

    2016-01-01

    Glass ionomer cements (GICs) are being used for a wide range of applications in dentistry. In order to overcome the poor mechanical properties of glass ionomers, several modifications have been introduced to the conventional GICs. Nanotechnology involves the use of systems, modifications or materials the size of which is in the range of 1–100 nm. Nano-modification of conventional GICs and resin modified GICs (RMGICs) can be achieved by incorporation of nano-sized fillers to RMGICs, reducing the size of the glass particles, and introducing nano-sized bioceramics to the glass powder. Studies suggest that the commercially available nano-filled RMGIC does not hold any significant advantage over conventional RMGICs as far as the mechanical and bonding properties are concerned. Conversely, incorporation of nano-sized apatite crystals not only increases the mechanical properties of conventional GICs, but also can enhance fluoride release and bioactivity. By increasing the crystallinity of the set matrix, apatites can make the set cement chemically more stable, insoluble, and improve the bond strength with tooth structure. Increased fluoride release can also reduce and arrest secondary caries. However, due to a lack of long-term clinical studies, the use of nano-modified glass ionomers is still limited in daily clinical dentistry. In addition to the in vitro and in vivo studies, more randomized clinical trials are required to justify the use of these promising materials. The aim of this paper is to review the modification performed in GIC-based materials to improve their physicochemical properties. PMID:27428956

  6. Modifications in Glass Ionomer Cements: Nano-Sized Fillers and Bioactive Nanoceramics

    Directory of Open Access Journals (Sweden)

    Shariq Najeeb

    2016-07-01

    Full Text Available Glass ionomer cements (GICs are being used for a wide range of applications in dentistry. In order to overcome the poor mechanical properties of glass ionomers, several modifications have been introduced to the conventional GICs. Nanotechnology involves the use of systems, modifications or materials the size of which is in the range of 1–100 nm. Nano-modification of conventional GICs and resin modified GICs (RMGICs can be achieved by incorporation of nano-sized fillers to RMGICs, reducing the size of the glass particles, and introducing nano-sized bioceramics to the glass powder. Studies suggest that the commercially available nano-filled RMGIC does not hold any significant advantage over conventional RMGICs as far as the mechanical and bonding properties are concerned. Conversely, incorporation of nano-sized apatite crystals not only increases the mechanical properties of conventional GICs, but also can enhance fluoride release and bioactivity. By increasing the crystallinity of the set matrix, apatites can make the set cement chemically more stable, insoluble, and improve the bond strength with tooth structure. Increased fluoride release can also reduce and arrest secondary caries. However, due to a lack of long-term clinical studies, the use of nano-modified glass ionomers is still limited in daily clinical dentistry. In addition to the in vitro and in vivo studies, more randomized clinical trials are required to justify the use of these promising materials. The aim of this paper is to review the modification performed in GIC-based materials to improve their physicochemical properties.

  7. In vitro bioactivity of SiO{sub 2}, CaO, Na{sub 2}O - based glasses

    Energy Technology Data Exchange (ETDEWEB)

    Lebecq, I.; Desanglois, F.; Follet-Houttemane, C. [Univ. de Valenciennes et du Hainaut Cambresis (Spain). Lab. des Materiaux Avances Ceramiques

    2002-07-01

    Bioactivity of 15 glasses in the system SiO{sub 2}-CaO-Na{sub 2}O was evaluated by examining the formation of apatite in vitro. SiO{sub 2} content is varied between 42 mole% and 55 mole%. Surfaces of glasses soaked in SBF were studied by FTIR. An apatite layer is formed on surfaces in a wide compositional region within 4 days. Hench Bioglass 45S5 is also studied for comparison. (orig.)

  8. Comparison of nanoscale and microscale bioactive glass on the properties of P(3HB)/Bioglass composites.

    Science.gov (United States)

    Misra, Superb K; Mohn, Dirk; Brunner, Tobias J; Stark, Wendelin J; Philip, Sheryl E; Roy, Ipsita; Salih, Vehid; Knowles, Jonathan C; Boccaccini, Aldo R

    2008-04-01

    This study compares the effects of introducing micro (m-BG) and nanoscale (n-BG) bioactive glass particles on the various properties (thermal, mechanical and microstructural) of poly(3hydroxybutyrate) (P(3HB))/bioactive glass composite systems. P(3HB)/bioactive glass composite films with three different concentrations of m-BG and n-BG (10, 20 and 30 wt%, respectively) were prepared by a solvent casting technique. The addition of n-BG particles had a significant stiffening effect on the composites, modulus when compared with m-BG. However, there were no significant differences in the thermal properties of the composites due to the addition of n-BG and m-BG particles. The systematic addition of n-BG particles induced a nanostructured topography on the surface of the composites, which was not visible by SEM in m-BG composites. This surface effect induced by n-BG particles considerably improved the total protein adsorption on the n-BG composites compared to the unfilled polymer and the m-BG composites. A short term in vitro degradation (30 days) study in simulated body fluid (SBF) showed a high level of bioactivity as well as higher water absorption for the P(3HB)/n-BG composites. Furthermore, a cell proliferation study using MG-63 cells demonstrated the good biocompatibility of both types of P(3HB)/bioactive glass composite systems. The results of this investigation confirm that the addition of nanosized bioactive glass particles had a more significant effect on the mechanical and structural properties of a composite system in comparison with microparticles, as well as enhancing protein adsorption, two desirable effects for the application of the composites in tissue engineering.

  9. Therapeutic ion-releasing bioactive glass ionomer cements with improved mechanical strength and radiopacity

    Science.gov (United States)

    Fuchs, Maximilian; Gentleman, Eileen; Shahid, Saroash; Hill, Robert; Brauer, Delia

    2015-10-01

    Bioactive glasses (BG) are used to regenerate bone, as they degrade and release therapeutic ions. Glass ionomer cements (GIC) are used in dentistry, can be delivered by injection and set in situ by a reaction between an acid-degradable glass and a polymeric acid. Our aim was to combine the advantages of BG and GIC, and we investigated the use of alkali-free BG (SiO2-CaO-CaF2-MgO) with 0 to 50% of calcium replaced by strontium, as the beneficial effects of strontium on bone formation are well documented. When mixing BG and poly(vinyl phosphonic-co-acrylic acid), ions were released fast (up to 90% within 15 minutes at pH 1), which resulted in GIC setting, as followed by infrared spectroscopy. GIC mixed well and set to hard cements (compressive strength up to 35 MPa), staying hard when in contact with aqueous solution. This is in contrast to GIC prepared with poly(acrylic acid), which were shown previously to become soft in contact with water. Strontium release from GIC increased linearly with strontium for calcium substitution, allowing for tailoring of strontium release depending on clinical requirements. Furthermore, strontium substitution increased GIC radiopacity. GIC passed ISO10993 cytotoxicity test, making them promising candidates for use as injectable bone cements.

  10. Long term effects of bioactive glass particulates on dental pulp stem cells in vitro

    Directory of Open Access Journals (Sweden)

    Gholami Sanaz

    2017-12-01

    Full Text Available Bioactive glasses (BG are known for their ability to induce bone formation by the action of their dissolution products. Glasses can deliver active ions at a sustained rate, determined by their composition and surface area. Nanoporous sol-gel derived BGs can biodegrade rapidly, which can lead to a detrimental burst release of ions and a pHrise. The addition of phosphate into the glass can buffer the pH during dissolution. Here, dissolution of BG with composition 60 mol% SiO2, 28 mol% CaO and 12 mol% P2O5 at 600 μg/ml were investigated. Initially, the dissolution and apatite formation of the BG particulates were examined in simulated body fluid using FTIR and XRD. BG particulates were indirectly exposed to dental pulp stem cells, and the effect of 14 days continuous ion release on human dental pulp stem cells (hDPSC viability and differentiation was evaluated. Alamar blue assay showed that cell proliferation was not inhibited by the continuous release of Ca, P and soluble silica. In fact, hDPSC in the presence of BG particulate displayed a higher density of mineralized nodules than untreated cells, as assessed by Alizarin red. The results will have a great contribution to the in vivo application of this particular BG.

  11. Bioactive Glass Nanoparticles as a New Delivery System for Sustained 5-Fluorouracil Release: Characterization and Evaluation of Drug Release Mechanism

    Directory of Open Access Journals (Sweden)

    Abeer M. El-Kady

    2015-01-01

    Full Text Available Bioactive glass nanoparticles were synthesized and tested for the first time as a new delivery system for sustained 5-fluorouracil (5-FU release. They were characterized by TEM, DTA, TGA, and FT-IR. The porosity % and specific surface area of glass nanoparticles were 85.59% and 378.36 m2/g, respectively. The in vitro bioactivity evaluation confirmed that bioactive glass disks prepared from these nanoparticles could induce hydroxyapatite layer over their surfaces in simulated body fluid. The in vitro drug release experiment indicated that glass nanoparticles could serve as long-term local delivery vehicles for sustained 5-FU release. The release profile of 5-FU showed an initial fast release stage followed by a second stage of slower release. The initial burst release of 5-FU in the first day was about 23% (28.92 mg·L−1 of the total amount of loaded 5-FU, while the final cumulative percentage of the 5-FU released after 32 days was about 45.6% (57.31 mg·L−1 of the total amount of loaded 5-FU. The application of different mathematical models indicated that 5-FU was released by diffusion controlled mechanism and suggested that its release rate was dependent on glass particles dissolution, changes of surface area as well as diameter of glass particles, and concentration of loaded drug.

  12. Thermogelling chitosan–collagen–bioactive glass nanoparticle hybrids as potential injectable systems for tissue engineering

    Energy Technology Data Exchange (ETDEWEB)

    Moreira, Cheisy D.F.; Carvalho, Sandhra M.; Mansur, Herman S., E-mail: hmansur@demet.ufmg.br; Pereira, Marivalda M., E-mail: mpereira@demet.ufmg.br

    2016-01-01

    Recently, stimuli-responsive nanocomposite-derived hydrogels have gained prominence in tissue engineering because they can be applied as injectable scaffolds in bone and cartilage repair. Due to the great potential of these systems, this study aimed to synthesize and characterize novel thermosensitive chitosan-based composites, chemically modified with collagen and reinforced by bioactive glass nanoparticles (BG) on the development of injectable nanohybrids for regenerative medicine applications. Thus, the composite hydrogels were extensively characterized by structural, morphological, rheological, and biological testing. The composites showed thermosensitive response with the gelation temperature at approximately 37 °C, which is compatible with the human body temperature. In addition, scanning electron microscopy (SEM) analysis indicated that the chitosan hydrogels exhibited 3D-porous structures, and the incorporation of collagen in the system caused increase on the average pore size. Fourier transform infrared spectroscopy (FTIR) analysis indicated the main functional groups of each component of the composite system and their chemical interactions forming the scaffold. Moreover, rheological measurements were employed to assess the viscoelastic behavior of the hydrogels as a function of the temperature. The results demonstrated that the addition of collagen and bioactive glass increases the mechanical properties after the gelation process. The addition of 2 wt.% of BG nanoparticles caused an increase of approximately 39% on stiffness compared to pure chitosan and the addition of 30 wt.% collagen caused a further increase on the stiffness by 95%. The cytotoxicity and cell viability of the hydrogels were assessed by MTT and LIVE/DEAD® assays, where the results demonstrated no toxic effect of the composites on the human osteosarcoma cell culture (SAOS) and kidney cells line of human embryo (HEK 293T). Hence, it can be stated that innovative composites were

  13. Bioactive glass-ceramic coating for enhancing the in vitro corrosion resistance of biodegradable Mg alloy

    Energy Technology Data Exchange (ETDEWEB)

    Ye Xinyu [Key Laboratory for Advanced Ceramics and Machining Technology of Ministry of Education, Tianjin University, Tianjin 300072 (China); Cai Shu, E-mail: caishu@tju.edu.cn [Key Laboratory for Advanced Ceramics and Machining Technology of Ministry of Education, Tianjin University, Tianjin 300072 (China); Dou Ying [Key Laboratory for Advanced Ceramics and Machining Technology of Ministry of Education, Tianjin University, Tianjin 300072 (China); Xu Guohua [Shanghai Changzheng Hospital, Shanghai 200003 (China); Huang Kai; Ren Mengguo; Wang Xuexin [Key Laboratory for Advanced Ceramics and Machining Technology of Ministry of Education, Tianjin University, Tianjin 300072 (China)

    2012-10-15

    Highlights: Black-Right-Pointing-Pointer Sol-gel derived 45S5 glass-ceramic coating was prepared on Mg alloy substrate. Black-Right-Pointing-Pointer The corrosion resistance of glass-ceramic coated Mg alloy was markedly improved. Black-Right-Pointing-Pointer The corrosion behavior of the coated sample varied due to the cracking of coating. - Abstract: In this work, a bioactive 45S5 glass-ceramic coating was synthesized on magnesium (Mg) alloy substrate by using a sol-gel dip-coating method, to improve the initial corrosion resistance of AZ31 Mg alloy. The surface morphology and phase composition of the glass-ceramic coating were characterized by scanning electron microscopy (SEM), X-ray diffraction (XRD) and Fourier transform infrared spectroscopy (FTIR). The coating composed of amorphous phase and crystalline phase Na{sub 2}Ca{sub 2}Si{sub 3}O{sub 9}, with the thickness of {approx}1.0 {mu}m, exhibited a uniform and crack-free surface morphology. The corrosion behavior of the uncoated and coated Mg alloy substrates was investigated by the electrochemical measurements and immersion tests in simulated body fluid (SBF). Potentiodynamic polarization tests recorded an increase of potential (E{sub corr}) form -1.60 V to -1.48 V, and a reduction of corrosion current density (i{sub corr}) from 4.48 {mu}A cm{sup -2} to 0.16 {mu}A cm{sup -2}, due to the protection provided by the glass-ceramic coating. Immersion tests also showed the markedly improved corrosion resistance of the coated sample over the immersion period of 7 days. Moreover, after 14 days of immersion in SBF, the corrosion resistance of the coated sample declined due to the cracking of the glass-ceramic coating, which was confirmed by electrochemical impedance spectroscopy (EIS) analysis. The results suggested that the 45S5 glass-ceramic coated Mg alloy could provide a suitable corrosion behavior for use as degradable implants.

  14. Dental ceramics coated with bioactive glass: Surface changes after exposure in a simulated body fluid under static and dynamic conditions

    Science.gov (United States)

    Papadopoulou, L.; Kontonasaki, E.; Zorba, T.; Chatzistavrou, X.; Pavlidou, E.; Paraskevopoulos, K.; Sklavounos, S.; Koidis, P.

    2003-07-01

    Bioactive materials develop a strong bond with living tissues through a carbonate-containing hydroxyapatite layer, similar to that of bone. The fabrication of a thin bioactive glass coating on dental ceramics used in metal-ceramic restorations, could provide a bioactive surface, which in combination with a tissue regenerative technique could lead to periodontal tissues attachment. The aim of this study was the in vitro investigation of the surface structure changes of dental ceramics used in metal-ceramic restorations, coated with a bioactive glass heat-treated at 950 °C, after exposure in a simulated body fluid (SBF) under two different soaking conditions. Coating of dental ceramics with a bioactive glass resulted in the formation of a stable and well bonded with the ceramic substrate thin layer. The growth of a well-attached carbonate apatite layer on their surface after immersion in a simulated body fluid is well evidenced under both experimental conditions, although in static environment the rate of apatite growth is constant and the grown layers seem to be more dense and compact compared with the respective layers observed on specimens under dynamic conditions.

  15. Effect of wollastonite ceramics and bioactive glass on the formation of a bonelike apatite layer on a cobalt base alloy.

    Science.gov (United States)

    Cortés, D A; Medina, A; Escobedo, J C; Escobedo, S; López, M A

    2004-08-01

    A biomimetic method was used to promote a bioactive surface on a cobalt base alloy (ASTM F-75). The metallic substrates were alkali treated and some of the samples were subsequently heat treated. The treated samples were immersed in simulated body fluid (SBF) on granular particles of either bioactive glass or wollastonite. For comparative purposes, no bioactive system was used in some tests. Three different methods were used for the immersion of the samples in SBF: 1) 21 days in SBF, 2) 21 days in 1.5 SBF, and 3) 7 days in SBF followed by 14 days in 1.5 SBF (re-immersion method). A bonelike apatite layer was formed on all the samples placed on wollastonite and bioactive glass particles. The morphology of the apatite layer formed by using the re-immersion method and wollastonite closely resembled the existing bioactive systems. No apatite layer was observed on the samples treated without bioactive material and soaked for 21 days in SBF or 1.5 SBF, apart from the substrates treated by using the re-immersion method. The heat treatment delayed the apatite formation in all the cases studied. Copyright 2004 Wiley Periodicals, Inc. J Biomed Mater Res 70A: 341-346, 2004

  16. In vitro study of improved wound-healing effect of bioactive borate-based glass nano-/micro-fibers.

    Science.gov (United States)

    Yang, Qingbo; Chen, Sisi; Shi, Honglan; Xiao, Hai; Ma, Yinfa

    2015-10-01

    Because of the promising wound-healing capability, bioactive glasses have been considered as one of the next generation hard- and soft-tissue regeneration materials. The lack of understanding of the substantial mechanisms, however, indicates the need for further study on cell-glass interactions to better interpret the rehabilitation capability. In the present work, three bioactive glass nano-/micro-fibers, silicate-based 45S5, borate-based 13-93B3 and 1605 (additionally doped with copper oxide and zinc oxide), were firstly compared for their in vitro soaking/conversion rate. The results of elemental monitoring and electron microscopic characterization demonstrated that quicker ion releasing and glass conversion occurred in borate-based fibers than that of silicate-based one. This result was also reflected by the formation speed of hydroxyapatite (HA). This process was further correlated with original boron content and surrounding rheological condition. We showed that an optimal fiber pre-soaking time (or an ideal dynamic flow rate) should exist to stimulate the best cell proliferation and migration ability. Moreover, 13-93B3 and 1605 fibers showed different glass conversion and biocompatibility properties as well, indicating that trace amount variation in composition can also influence fiber's bioactivity. In sum, our in vitro rheological module closely simulated in vivo niche environment and proved a potentially improved wound-healing effect by borate-based glass fibers, and the results shall cast light on future improvement in bioactive glass fabrication. Copyright © 2015 Elsevier B.V. All rights reserved.

  17. PROCESSING AND CHARACTERISATION OF HIGH-VELOCITY SUSPENSION FLAME SPRAYED (HVSFS BIOACTIVE GLASS COATINGS

    Directory of Open Access Journals (Sweden)

    GIOVANNI BOLELLI

    2010-03-01

    Full Text Available The High-Velocity Suspension Flame Spraying (HVSFS technique was employed in order to deposit bioactive glass coatings onto titanium substrates. Two different glass compositions were examined: the classical 45S5 Bioglass and a newly-developed SiO2–CaO–K2O–P2O5 glass, labelled as “Bio-K”. Suitable raw materials were melted in a furnace and fritted by casting into water. The frit was dry-milled in a porcelain jar and subsequently attrition-milled in isopropanol. The resulting micronsized powders were dispersed in a water+isopropanol mixture, in order to prepare suitable suspensions for the HVSFS process. The deposition parameters were varied; however, all coatings were obtained by performing three consecutive torch cycles in front of the substrate. The thickness and porosity of the coatings were significantly affected by the chosen set of deposition parameters; however, in all cases, the layer produced during the third torch cycle was thicker and denser than the one produced during the first cycle. As the system temperature increases during the spraying process, the particles sprayed during the last torch cycle remain at T > Tg while they spread, so that interlamellar viscous flow sintering takes place, favouring the formation of such denser microstructure. Both coatings are entirely glassy; however, micro-Raman spectroscopy reveals that, whereas the 45S5 coating is structurally identical to the corresponding bulk glass, the “Bio-K” coating is somewhat different from the bulk one.

  18. Synthesis of functionally graded bioactive glass-apatite multistructures on Ti substrates by pulsed laser deposition

    Energy Technology Data Exchange (ETDEWEB)

    Tanaskovic, D.; Jokic, B. [Faculty of Technology and Metallurgy, Karnegijeva 4, 11000 Belgrade (Serbia); Socol, G.; Popescu, A. [National Institute for Lasers, Plasma and Radiation Physics, Box MG-54, Bucharest-Magurele, RO-77125 (Romania); Mihailescu, I.N. [National Institute for Lasers, Plasma and Radiation Physics, Box MG-54, Bucharest-Magurele, RO-77125 (Romania)], E-mail: ion.mihailescu@inflpr.ro; Petrovic, R.; Janackovic, Dj. [Faculty of Technology and Metallurgy, Karnegijeva 4, 11000 Belgrade (Serbia)

    2007-12-15

    Functionally graded glass-apatite multistructures were synthesized by pulsed laser deposition on Ti substrates. We used sintered targets of hydroxyapatite Ca{sub 10}(PO{sub 4}){sub 6}(OH){sub 2}, or bioglasses in the system SiO{sub 2}-Na{sub 2}O-K{sub 2}O-CaO-MgO-P{sub 2}O{sub 5} with SiO{sub 2} content of either 57 wt.% (6P57) or 61 wt.% (6P61). A UV KrF* ({lambda} = 248 nm, {tau} > 7 ns) excimer laser source was used for the multipulse laser ablation of the targets. The hydroxyapatite thin films were obtained in H{sub 2}O vapors, while the bioglass layers were deposited in O{sub 2}. Thin films of 6P61 were deposited in direct contact with Ti, because Ti and this glass have similar thermal expansion behaviors, which ensure good bioglass adhesion to the substrate. This glass, however, is not bioactive, so yet more depositions of 6P57 bioglass and/or hydroxyapatite thin films were performed. All structures with hydroxyapatite overcoating were post-treated in a flux of water vapors. The obtained multistructures were characterized by various techniques. X-ray investigations of the coatings found small amounts of crystalline hydroxyapatite in the outer layers. The scanning electron microscopy analyses revealed homogeneous coatings with good adhesion to the Ti substrate. Our studies showed that the multistructures we had obtained were compatible with further use in biomimetic metallic implants with glass-apatite coating applications.

  19. Effect of various additives on microstructure, mechanical properties, and in vitro bioactivity of sodium oxide-calcium oxide-silica-phosphorus pentoxide glass-ceramics.

    Science.gov (United States)

    Li, H C; Wang, D G; Hu, J H; Chen, C Z

    2013-09-01

    The partial substitution of MgO, TiO2, or CaF2 for CaO in the Na2O-CaO-SiO2-P2O5 (45S5) system was conducted by the sol-gel method and a comparative study on structural, mechanical properties, and bioactivity of the glasses was reported. Based on thermogravimetric and differential thermal analysis, the gels were sintered with a suitable heat treatment procedure. The glass-ceramic properties were characterized by X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR), scanning electron microscopy (SEM), energy dispersive spectrometer (EDS) and so on, and the bioactivity of the glass-ceramic was evaluated by in vitro assays in simulated body fluid (SBF). Results indicate that with the partial substitution of MgO, TiO2, CaF2 for CaO in glass composition, the mechanical properties of the glass-ceramics have been significantly improved. Furthermore, CaF2 promotes glass crystallization and the crystallization does not inhibit the glass-ceramic bioactivity. All samples possess bioactivity; however, the bioactivity of these glass-ceramics is quite different. Compared with 45S5, the introduction of MgO decreases the ability of apatite induction. The addition of TiO2 does not significantly improve the bioactivity, and the replacement of CaO by CaF2 shows a higher bioactivity. Copyright © 2013 Elsevier Inc. All rights reserved.

  20. Ag-loaded mesoporous bioactive glasses against Enterococcus faecalis biofilm in root canal of human teeth.

    Science.gov (United States)

    Fan, Wei; Wu, Daming; Ma, Tengjiao; Fan, Bing

    2015-01-01

    Ag-loaded mesoporous bioactive glass (Ag-MBG) powders were synthesized and characterized. The ions release of Ag-MBGs in Tris-HCl and the pH stability of simulated body fluids after immersing Ag-MBGs were tested. Root canals were inoculated with Enterococcus faecalis for 4 weeks, and the antibacterial activity of MBGs, Ag-MBGs and calcium hydroxide against E. faecalis biofilm were evaluated. Results showed that Ag-MBGs possessed highly ordered mesoporous structure with silver nanoparticles deposited in the mesopores, which enabled a sustained Ag ions released. The biofilms treated with Ag-MBGs showed a significant structural disruption compared with MBGs. These results indicated that Ag-MBGs possess a potent antibacterial effect against E.faecalis biofilm in root canal, and the antibacterial activity was induced by the release of Ag ions from Ag-MBGs.

  1. Composite bone cements loaded with a bioactive and ferrimagnetic glass-ceramic. Part I: Morphological, mechanical and calorimetric characterization.

    Science.gov (United States)

    Bruno, Matteo; Miola, Marta; Bretcanu, Oana; Vitale-Brovarone, Chiara; Gerbaldo, Roberto; Laviano, Francesco; Verné, Enrica

    2014-08-01

    Hyperthermia is a technique for destroying cancer cells which involves the exposition of body's tissue to a controlled heat, normally between 41℃ and 46℃. It has been reported that ferro- or ferrimagnetic materials can heat locally, if they are placed (after being implanted) under an alternating magnetic field, damaging only tumoral cells and not the healthy ones. The power loss produced by the magnetic materials can be dissipated in the form of heat. This phenomenon has to be regulated in order to obtain a controlled temperature inside the tissues. The material that was produced and characterized in this work is composed of two phases: a polymethylmethacrylate (PMMA) matrix in which a ferrimagnetic biocompatible/bioactive glass ceramic is dispersed. This composite material is intended to be applied as bone filler for the hyperthermic treatment of bone tumors. The ferrimagnetic bioactive glass-ceramic belongs to the system SiO 2 -Na 2 O-CaO-P 2 O 5 -FeO-Fe 2 O 3 and contains magnetite (FeO*Fe 2 O 3 ) inside an amorphous bioactive residual phase. The composite material possesses structural, magnetic and bioactivity properties. The structural ones are conferred by PMMA which acts as filler for the bone defect or its damaged area. Bioactivity is conferred by the composition of the residual amorphous phase of the glass-ceramic and magnetic properties are conferred by magnetite crystals embedded in the bioactive glass-ceramic. The characterization involved the following tests: morphological and chemical characterization (scanning electron microscopy-energy dispersion spectrometry-micro computed tomography analysis), calorimetric tests and mechanical test (compression and flexural four point test). In vitro assessment of biological behavior will be the object of the part II of this work. © The Author(s) 2014 Reprints and permissions: sagepub.co.uk/journalsPermissions.nav.

  2. Neocellularization and neovascularization of nanosized bioactive glass-coated decellularized trabecular bone scaffolds

    KAUST Repository

    Gerhardt, Lutz Christian

    2012-09-11

    In this study, the in vivo recellularization and neovascularization of nanosized bioactive glass (n-BG)-coated decellu-larized trabecular bone scaffolds were studied in a rat model and quantified using stereological analyses. Based on the highest amount of vascular endothelial growth factor (VEGF) secreted by human fibroblasts grown on n-BG coatings (0-1.245 mg/cm 2), decellularized trabecular bone samples (porosity: 43-81%) were coated with n-BG particles. Grown on n-BG particles at a coating density of 0.263 mg/cm2, human fibroblasts produced 4.3 times more VEGF than on uncoated controls. After 8 weeks of implantation in Sprague-Dawley rats, both uncoated and n-BG-coated samples were well infiltrated with newly formed tissue (47-48%) and blood vessels (3-4%). No significant differences were found in cellularization and vascularization between uncoated bone scaffolds and n-BG-coated scaffolds. This finding indicates that the decellularized bone itself may exhibit growth-promoting properties induced by the highly interconnected pore microarchitecture and/or proteins left behind on decellularized scaffolds. Even if we did not find proangiogenic effects in n-BG-coated bone scaffolds, a bioactive coating is considered to be beneficial to impart osteoinductive and osteoconductive properties to decellularized bone. n-BG-coated bone grafts have thus high clinical potential for the regeneration of complex tissue defects given their ability for recellularization and neovascularization. © 2012 Wiley Periodicals, Inc.

  3. Hydrogel/bioactive glass composites for bone regeneration applications: synthesis and characterisation.

    Science.gov (United States)

    Killion, John A; Kehoe, Sharon; Geever, Luke M; Devine, Declan M; Sheehan, Eoin; Boyd, Daniel; Higginbotham, Clement L

    2013-10-01

    Due to the deficiencies of current commercially available biological bone grafts, alternative bone graft substitutes have come to the forefront of tissue engineering in recent times. The main challenge for scientists in manufacturing bone graft substitutes is to obtain a scaffold that has sufficient mechanical strength and bioactive properties to promote formation of new tissue. The ability to synthesise hydrogel based composite scaffolds using photopolymerisation has been demonstrated in this study. The prepared hydrogel based composites were characterised using techniques including Fourier Transform Infrared Spectroscopy (FTIR), X-ray diffraction (XRD), scanning electron microscopy (SEM), Energy-dispersive X-ray spectrometry (EDX), rheological studies and compression testing. In addition, gel fraction, differential scanning calorimetry (DSC), thermogravimetric analysis (TGA), porosity and swelling studies of the composites were carried out. It was found that these novel hydrogel bioglass composite formulations did not display the inherent brittleness that is typically associated with bioactive glass based bone graft materials and exhibited enhanced biomechanical properties compared to the polyethylene glycol hydrogel scaffolds along. Together, the combination of enhanced mechanical properties and the deposition of apatite on the surface of these hydrogel based composites make them an ideal candidate as bone graft substitutes in cancellous bone defects or low load bearing applications. © 2013 Elsevier B.V. All rights reserved.

  4. Electrophoretic deposition of gentamicin-loaded bioactive glass/chitosan composite coatings for orthopaedic implants.

    Science.gov (United States)

    Pishbin, Fatemehsadat; Mouriño, Viviana; Flor, Sabrina; Kreppel, Stefan; Salih, Vehid; Ryan, Mary P; Boccaccini, Aldo R

    2014-06-11

    Despite their widespread application, metallic orthopaedic prosthesis failure still occurs because of lack of adequate bone-bonding and the incidence of post-surgery infections. The goal of this research was to develop multifunctional composite chitosan/Bioglass coatings loaded with gentamicin antibiotic as a suitable strategy to improve the surface properties of metallic implants. Electrophoretic deposition (EPD) was applied as a single-step technology to simultaneously deposit the biopolymer, bioactive glass particles, and the antibiotic on stainless steel substrate. The microstructure and composition of the coatings were characterized using SEM/EDX, XRD, FTIR, and TGA/DSC, respectively. The in vitro bioactivity of the coatings was demonstrated by formation of hydroxyapatite after immersion in simulated body fluid (SBF) in a short period of 2 days. High-performance liquid chromatography (HPLC) measurements indicated the release of 40% of the loaded gentamicin in phosphate buffered saline (PBS) within the first 5 days. The developed composite coating supported attachment and proliferation of MG-63 cells up to 10 days. Moreover, disc diffusion test showed improved bactericidal effect of gentamicin-loaded composite coatings against S. aureus compared to control non-gentamicin-loaded coatings.

  5. Assessment of polymer/bioactive glass-composite microporous spheres for tissue regeneration applications.

    Science.gov (United States)

    Keshaw, Hussila; Georgiou, George; Blaker, Jonny J; Forbes, Alastair; Knowles, Jonathan C; Day, Richard M

    2009-07-01

    Conformable scaffold materials capable of rapid vascularization and tissue infiltration would be of value in the therapy of inaccessible wounds. Microporous spheres of poly(D,L-lactide-co-glycolide) (PLGA) containing bioactive glass (BG) were prepared using a thermally induced phase separation (TIPS) technique, and the bioactivity, in vitro degradation, and tissue integration of the microporous spheres were assessed. Microporous spheres containing 10% (w/w) BG stimulated a significant increase in vascular endothelial growth factor secretion from myofibroblasts consistently over a 10-day period (p microporous spheres. The microporous spheres degraded steadily in vitro over a 16-week period, with the neat PLGA microporous spheres retaining 82% of their original weight and microporous spheres containing 10% (w/w) BG retaining 77%. Both types of microporous spheres followed a similar pattern of size reduction throughout the degradation study, resulting in a 23% and 20% reduction after 16 weeks for the neat PLGA microporous spheres and PLGA microporous spheres containing 10% (w/w) BG, respectively (p microporous spheres became rapidly integrated (interspherically and intraspherically) with host tissue, including vascularization of voids inside the microporous sphere. The unique properties of TIPS microporous spheres make them ideally suited for regenerative medicine applications where tissue augmentation is required.

  6. Effect of Bioactive Glass air Abrasion on Shear Bond Strength of Two Adhesive Resins to Decalcified Enamel.

    Directory of Open Access Journals (Sweden)

    Alireza Eshghi

    2014-12-01

    Full Text Available Bioactive glass air abrasion is a conservative technique to remove initial decalcified tissue and caries. This study examined the shear bond strength of composite resin to sound and decalcified enamel air-abraded by bioactive glass (BAG or alumina using etch-and-rinse and self-etch adhesives.Forty-eight permanent molars were root-amputated and sectioned mesiodistally. The obtained 96 specimens were mounted in acrylic resin; the buccal and lingual surfaces remained exposed. A demineralizing solution was used to decalcify half the specimens. Both sound and decalcified specimens were divided into two groups of alumina and bioactive glass air abrasion. In each group, the specimens were subdivided into two subgroups of Clearfil SE Bond or OptiBond FL adhesives (n=12. Composite resin cylinders were bonded on enamel surfaces cured and underwent thermocycling. The specimens were tested for shear bond strength. Data were analyzed using SPSS 16.0 and three-way ANOVA (α=0.05. Similar to the experimental groups, the enamel surface of one specimen underwent SEM evaluation.No significant differences were observed in composite resin bond strength subsequent to alumina or bioactive glass air abrasion preparation techniques (P=0.987. There were no statistically significant differences between the bond strength of etch-and-rinse and self-etch adhesive groups (P=1. Also, decalcified or intact enamel groups had no significant difference (P=0.918. However, SEM analysis showed much less enamel irregularities with BAG air abrasion compared to alumina air abrasion.Under the limitations of this study, preparation of both intact and decalcified enamel surfaces with bioactive glass air abrasion results in similar bond strength of composite resin in comparison with alumina air abrasion using etch-&-rinse or self-etch adhesives.

  7. In situ reduction of antibacterial silver ions to metallic silver nanoparticles on bioactive glasses functionalized with polyphenols

    Energy Technology Data Exchange (ETDEWEB)

    Ferraris, S., E-mail: sara.ferraris@polito.it [Department of Applied Science and Technology, Politecnico di Torino, C.so Duca degli Abruzzi 24, 10129, Torino (Italy); Miola, M. [Department of Applied Science and Technology, Politecnico di Torino, C.so Duca degli Abruzzi 24, 10129, Torino (Italy); Department of Health Sciences, Università del Piemonte Orientale UPO, Via Solaroli 17, 28100, Novara (Italy); Cochis, A.; Azzimonti, B.; Rimondini, L. [Department of Health Sciences, Università del Piemonte Orientale UPO, Via Solaroli 17, 28100, Novara (Italy); Prenesti, E. [Department of Chemistry, Università degli Studi di Torino, Via Pietro Giuria 7, Torino, 10125 (Italy); Vernè, E. [Department of Applied Science and Technology, Politecnico di Torino, C.so Duca degli Abruzzi 24, 10129, Torino (Italy)

    2017-02-28

    Highlights: • Gallic acid and natural polyphenols were grafted onto bioactive glasses. • Grafting ability was dependent on glass reactivity. • In situ reduction of silver nanoparticles was performed onto functionalized glasses. • Bioactive glasses decorated with silver nanoparticles showed antibacterial activity. - Abstract: The realization of surfaces with antibacterial properties due to silver nanoparticles loaded through a green approach is a promising research challenge of the biomaterial field. In this research work, two bioactive glasses have been doubly surface functionalized with polyphenols (gallic acid or natural polyphenols extracted from red grape skins and green tea leaves) and silver nanoparticles deposited by in situ reduction from a silver nitrate aqueous solution. The presence of biomolecules – showing reducing ability to directly obtain in situ metallic silver – and silver nanoparticles was investigated by means of UV–vis spectroscopy, X-Ray Photoelectron Spectroscopy (XPS) and Field Emission Scanning Electron Microscopy (FESEM). The antibacterial activity of the modified surfaces was tested against a multidrug resistant Staphylococcus aureus bacterial strain.

  8. Bactericidal strontium-releasing injectable bone cements based on bioactive glasses

    Science.gov (United States)

    Brauer, Delia S.; Karpukhina, Natalia; Kedia, Gopal; Bhat, Aditya; Law, Robert V.; Radecka, Izabela; Hill, Robert G.

    2013-01-01

    Strontium-releasing injectable bone cements may have the potential to prevent implant-related infections through the bactericidal action of strontium, while enhancing bone formation in patients suffering from osteoporosis. A melt-derived bioactive glass (BG) series (SiO2–CaO–CaF2–MgO) with 0–50% of calcium substituted with strontium on a molar base were produced. By mixing glass powder, poly(acrylic acid) and water, cements were obtained which can be delivered by injection and set in situ, giving compressive strength of up to 35 MPa. Strontium release was dependent on BG composition with increasing strontium substitution resulting in higher concentrations in the medium. Bactericidal effects were tested on Staphylococcus aureus and Streptococcus faecalis; cell counts were reduced by up to three orders of magnitude over 6 days. Results show that bactericidal action can be increased through BG strontium substitution, allowing for the design of novel antimicrobial and bone enhancing cements for use in vertebroplasty or kyphoplasty for treating osteoporosis-related vertebral compression fractures. PMID:23097502

  9. In vitro osteogenesis by intracellular uptake of strontium containing bioactive glass nanoparticles.

    Science.gov (United States)

    Naruphontjirakul, Parichart; Porter, Alexandra E; Jones, Julian R

    2018-01-15

    Monodispersed strontium containing bioactive glass nanoparticles (Sr-BGNPs) with two compositions were synthesised, through a modified sol-gel Stöber process, wherein silica nanoparticles (SiO2-NPs) were formed prior to incorporation of calcium and strontium, with diameters of 90 ± 10 nm. The osteogenic response of a murine preosteoblast cell line, MC3T3-E1, was investigated in vitro for a nanoparticle concentration of 250 µg/mL with compositions of 87 mol% SiO2, 7 mol% CaO, 6 mol% SrO and 83 mol% SiO2, 3 mol% CaO, 14 mol% SrO. Dissolution studies in minimum essential media (α-MEM) at pH 7.4 and artificial lysosomal fluid (ALF) at pH 4.5 showed that the particles dissolved and that Sr2+ ions were released from Sr-BGNPs in both environments. Both particle compositions and their ionic dissolution products enhanced the alkaline phosphatase (ALP) activity of the cells and calcium deposition. Immunohistochemistry (IHC) staining of Col1a1, osteocalcin (OSC) and osteopontin (OSP) showed that these proteins were expressed in the MC3T3-E1 cells following three weeks of culture. In the basal condition, the late osteogenic differentiation markers, OSC and OSP, were more overtly expressed by cells cultured with Sr-BGNPs with 14 mol% SrO and their ionic release products than in the control condition. Col1a1 expression was only slightly enhanced in the basal condition, but was enhanced further by the osteogenic supplements. These data demonstrate that Sr-BGNPs accelerate mineralisation without osteogenic supplements. Sr-BGNPs were internalised into MC3T3-E1 cells by endocytosis and stimulated osteogenic differentiation of the pre-osteoblast cell line. Sr-BGNPs are likely to be beneficial for bone regeneration and the observed osteogenic effects of these particles can be attributed to their ionic release products. We report, for the first time, that monodispersed bioactive glass nanoparticles (∼90 nm) are internalised into preosteoblast cells by

  10. Role of magnesium oxide and strontium oxide as modifiers in silicate-based bioactive glasses: Effects on thermal behaviour, mechanical properties and in-vitro bioactivity.

    Science.gov (United States)

    Bellucci, Devis; Sola, Antonella; Salvatori, Roberta; Anesi, Alexandre; Chiarini, Luigi; Cannillo, Valeria

    2017-03-01

    The composition of a CaO-rich silicate bioglass (BG_Ca-Mix, in mol%: 2.3 Na2O; 2.3 K2O; 45.6 CaO; 2.6 P2O5; 47.2 SiO2) was modified by replacing a fixed 10mol% of CaO with MgO or SrO or fifty-fifty MgO-SrO. The thermal behaviour of the modified glasses was accurately evaluated via differential thermal analysis (DTA), heating microscopy and direct sintering tests. The presence of MgO and/or SrO didn't interfere with the thermal stability of the parent glass, since all the new glasses remained completely amorphous after sintering (treatment performed at 753°C for the glass with MgO; at 750°C with SrO; at 759°C with MgO and SrO). The sintered samples achieved good mechanical properties, with a Young's modulus ranging between 57.9±6.7 for the MgO-SrO modified composition and 112.6±8.0GPa for the MgO-modified one. If immersed in a simulated body fluid (SBF), the modified glasses after sintering retained the strong apatite forming ability of the parent glass, in spite of the presence of MgO and/or SrO. Moreover, the sintered glasses, tested with MLO-Y4 osteocytes by means of a multi-parametrical approach, showed a good bioactivity in vitro, since neither the glasses nor their extracts caused any negative effect on cell viability or any inhibition on cell growth. The best results were achieved by the MgO-modified glasses, both BGMIX_Mg and BGMIX_MgSr, which were able to exert a strong stimulating effect on the cell growth, thus confirming the beneficial effect of MgO on the glass bioactivity. Copyright © 2016 Elsevier B.V. All rights reserved.

  11. Influence of biofilm formation on the optical properties of novel bioactive glass-containing composites.

    Science.gov (United States)

    Hyun, Hong-Keun; Ferracane, Jack L

    2016-09-01

    Bioactive glass (BAG) has been suggested as a possible additive for dental restorative materials because of its antimicrobial effect and potential for promoting apatite formation in body fluids. The purpose of this study was to investigate the effects of bacterial biofilm on the change of colorimetric value and translucency of novel BAG-containing composites having different initial surface roughness. Composites with 72wt% total filler load were prepared by replacing 15% of the silanized Sr glass with BAG (65 mol % Si; 4% P; 31% Ca), BAG-F (61% Si; 31% Ca; 4% P; 3% F; 1% B), or silanized silica. Light-cured discs of 2-mm thickness (n=10/group) were divided into 4 different surface roughness subgroups produced by wet polishing with 600 and then up to 1200, 2400, or 4000 grit SiC. CIE L*a*b* were measured and the color difference and translucency parameter (TP) were calculated before and after incubating in media with or without a Streptococcus mutans (UA 159) biofilm for 2 wks (no agitation). Results were analyzed using ANOVA/Tukey's test (α=0.05). All the color differences for BAG and BAG-F composite showed significant decreases with bacterial biofilm compared to media-only. The mean TP (SD) of BAG and BAG-F composite before aging [10.0 (2.8) and 8.5 (1.4)] was higher than that of the control composite [4.9 (0.8)], while the change in TP with aging was greater compared to the control with or without bacteria. BAG-F composites with the smoothest surfaces showed a greater decrease in TP under bacterial biofilm compared to the BAG composite. Highly polished dental composites containing bioactive glass additives may become slightly rougher and show reduced translucency when exposed to bacterial biofilms, but do not discolor any more than control composites that do not contain the BAG. Copyright © 2016 The Academy of Dental Materials. All rights reserved.

  12. Ion release from, and fluoride recharge of a composite with a fluoride-containing bioactive glass.

    Science.gov (United States)

    Davis, Harry B; Gwinner, Fernanda; Mitchell, John C; Ferracane, Jack L

    2014-10-01

    Materials that are capable of releasing ions such as calcium and fluoride, that are necessary for remineralization of dentin and enamel, have been the topic of intensive research for many years. The source of calcium has most often been some form of calcium phosphate, and that for fluoride has been one of several metal fluoride or hexafluorophosphate salts. Fluoride-containing bioactive glass (BAG) prepared by the sol-gel method acts as a single source of both calcium and fluoride ions in aqueous solutions. The objective of this investigation was to determine if BAG, when added to a composite formulation, can be used as a single source for calcium and fluoride ion release over an extended time period, and to determine if the BAG-containing composite can be recharged upon exposure to a solution of 5000ppm fluoride. BAG 61 (61% Si; 31% Ca; 4% P; 3% F; 1% B) and BAG 81 (81% Si; 11% Ca; 4% P; 3% F; 1% B) were synthesized by the sol-gel method. The composite used was composed of 50/50 Bis-GMA/TEGDMA, 0.8% EDMAB, 0.4% CQ, and 0.05% BHT, combined with a mixture of BAG (15%) and strontium glass (85%) to a total filler load of 72% by weight. Disks were prepared, allowed to age for 24h, abraded, then placed into DI water. Calcium and fluoride release was measured by atomic absorption spectroscopy and fluoride ion selective electrode methods, respectively, after 2, 22, and 222h. The composite samples were then soaked for 5min in an aqueous 5000ppm fluoride solution, after which calcium and fluoride release was again measured at 2, 22, and 222h time points. Prior to fluoride recharge, release of fluoride ions was similar for the BAG 61 and BAG 81 composites after 2h, and also similar after 22h. At the four subsequent time points, one prior to, and three following fluoride recharge, the BAG 81 composite released significantly more fluoride ions (p0.05) for the two composites. These results show that, when added to a composite formulation, fluoride-containing bioactive glass

  13. Bioactivity studies on TiO₂-bearing Na₂O-CaO-SiO₂-B₂O₃ glasses.

    Science.gov (United States)

    Jagan Mohini, G; Sahaya Baskaran, G; Ravi Kumar, V; Piasecki, M; Veeraiah, N

    2015-12-01

    Soda lime silica borate glasses mixed with different concentrations of TiO2 are synthesized by the melt-quenching technique. As a part of study on bioactivity of these glasses, the samples were immersed in simulated body fluid (SBF) solution for prolonged times (~21 days) during which weight loss along with pH measurements is carried out at specific intervals of time. The XRD and SEM analyses of post-immersed samples confirm the formation of crystalline hydroxyapatite layer (HA) on the surface of the samples. To assess the role of TiO2 on the formation of HA layer and degradability of the samples the spectroscopic studies viz. optical absorption and IR spectral studies on post- and pre-immersed samples have been carried out. The analysis of the results of degradability together with spectroscopic studies as a function of TiO2 concentration indicated that about 6.0 mol% of TiO2 is the optimal concentration for achieving better bioactivity of these glasses. The presence of the maximal concentration octahedral titanium ions in this glass that facilitates the formation of HA layer is found to be the reason for such a higher bioactivity. Copyright © 2015 Elsevier B.V. All rights reserved.

  14. Sol-gel derived manganese-releasing bioactive glass as a therapeutical approach for bone tissue engineering

    Energy Technology Data Exchange (ETDEWEB)

    Barrioni, B.R.; Oliveira, A.C.; Leite, M.F.; Pereira, M.M. [Universidade Federal de Minas Gerais (UFMG), MG (Brazil)

    2016-07-01

    Full text: Bioactive glasses (BG) have been highlighted in tissue engineering, due to their high bioactivity and biocompatibility, being potential materials for bone tissue repair. Its composition is variable and quite flexible, allowing the incorporation of therapeutic metallic ions, which has been regarded as a promising approach in the development of BG with superior properties for tissue engineering. These ions can be released in a controlled manner during the dissolution process of the glass, having the advantage of being released at the exactly implant site where they are needed, thus optimizing the therapeutic efficacy and reducing undesired side effects in the patient. Among several ions that have been studied, Manganese (Mn) has been shown to favor osteogenic differentiation. Besides, this ion is also a cofactor for several enzymes involved in remodeling of extracellular matrix, presenting an important role in cell adhesion. Therefore, it is very important to study the Mn role in the BG network and its influence on the glass bioactivity. In this context, new bioactive glass compositions derived from the 58S (60%SiO2-36%CaO-4%P2O5, mol%) were synthesized in this work, using the sol-gel method, by the incorporation of Mn into their structure. FTIR and Raman spectra showed the presence of typical BG chemical groups, whereas the amorphous structure typical of these materials was confirmed by XRD analysis, which also indicated that the Mn incorporation in the glass network was well succeeded, as its precursor did not recrystallize. The role of Mn in the glass network was also evaluated by XPS. The influence of Mn on carbonated hydroxyapatite layer formation after different periods of immersion of the BG powder in Simulated Body Fluid was evaluated using zeta potential, SEM, EDS and FTIR, whereas the controlled ion release was measured through ICP-OES. MTT assay revealed that Mn-containing BG showed no cytotoxic effect on cell culture. All these results indicate

  15. In Vitro Degradation of Borosilicate Bioactive Glass and Poly(l-lactide-co-ε-caprolactone Composite Scaffolds

    Directory of Open Access Journals (Sweden)

    Jenna Tainio

    2017-11-01

    Full Text Available Composite scaffolds were obtained by mixing various amounts (10, 30 and 50 weight % [wt %] of borosilicate bioactive glass and poly(l-lactide-co-ε-caprolactone (PLCL copolymer. The composites were foamed using supercritical CO2. An increase in the glass content led to a decrease in the pore size and density. In vitro dissolution/reaction test was performed in simulated body fluid. As a function of immersion time, the solution pH increased due to the glass dissolution. This was further supported by the increasing amount of Ca in the immersing solution with increasing immersion time and glass content. Furthermore, the change in scaffold mass was significantly greater with increasing the glass content in the scaffold. However, only the scaffolds containing 30 and 50 wt % of glasses exhibited significant hydroxyapatite (HA formation at 72 h of immersion. The compression strength of the samples was also measured. The Young’s modulus was similar for the 10 and 30 wt % glass-containing scaffolds whereas it increased to 90 MPa for the 50 wt % glass containing scaffold. Upon immersion up to 72 h, the Young’s modulus increased and then remained constant for longer immersion times. The scaffold prepared could have great potential for bone and cartilage regeneration.

  16. Antibacterial effect of bioactive glass in combination with powdered enamel and dentin

    Directory of Open Access Journals (Sweden)

    Prabhakar A

    2010-01-01

    Full Text Available Background and Objectives: In endodontics, various intracanal medications have been advocated to eliminate bacteria after root canal instrumentation. A recent study has revealed that addition of powdered dentin to bioactive glass (BAG led to increased glass dissolution, and an increased antibacterial efficacy. Therefore, the present study was undertaken to compare the effect of enamel and dentin powder on the antibacterial efficacy of a commercially available BAG. Materials and Methods: Dentin blocks (dbs were prepared from single rooted human teeth. These dbs were infected with Enterococcus faecalis for two weeks in Tryptic Soy Broth (TSB, while negative controls were kept in sterile TSB. In group I, the infected dbs were filled with BAG, in group II with BAG + Enamel powder and group III with BAG + Dentin powder. Dentin samples were harvested from the dbs and cultured. Statistical Analysis: Kruskal-Wallis ANOVA was used for multiple group comparison followed by Scheffe′s post hoc test for pair-wise comparisons. Results: All the combinations of BAG evaluated significantly reduced the bacterial counts compared to the control group. However, at the end of 24 hours, three days, and five days BAG + Dentin powder showed significant reduction ( P < 0.01 in bacterial counts compared to the other experimental groups. Conclusion: Among the various materials evaluated, it appeared that though BAG exhibits antimicrobial efficacy, the addition of powdered enamel and dentin in aqueous suspension definitely enhanced this property. However, the addition of enamel powder BAG did not significantly alter its antimicrobial efficacy compared to BAG + dentin powder.

  17. Hypoxia-mimicking bioactive glass regenerative effects on dental stem cells

    Science.gov (United States)

    Noor, Siti Noor Fazliah Mohd; Azevedo, Maria; Mohamad, Hasmaliza; Autefage, Hélène

    2016-12-01

    Vascularization is an important aspect of tissue regeneration. Hypoxia, low oxygen concentration, is a known stimulus for the release of vascular endothelial growth factors (VEGF) which play important roles in vascularization. The current study aimed to assess the effect of a cobalt-containing bioactive glass (BG) in stimulating hypoxia and promoting vascularization. To incorporate cobalt into BG, 1 mol% of calcium was substituting with cobalt, and this formulation was compared to the one without cobalt. Both BGs were processed via melt-derived method. The BG powders with particle size less than 38 µm were incubated with cell culture medium for 4 hours at 37°C on continuous rolling, and then the medium was filtered using 0.22 µm syringe filters. Prior to use, the BG-conditioned media were supplemented with 10% (v/v) fetal bovine serum and 1% (v/v) antibiotic-antimycotic, and were allowed to equilibrate overnight inside a CO2 incubator. The conditioned media were used on human dental stem cells (stem cells from permanent (DPSC) and deciduous (SHED) teeth) and assessed for their capacity to stimulate the release of angiogenic factors from the cells. The results showed that cobalt ions were released from the cobalt-containing BG, following partial dissolution of the glasses in cell culture medium, and promoted VEGF release from the cells. In conclusion, the incorporation of cobalt in BG may have potential to be used for tissue regeneration by promoting vascularization through the activation of hypoxia pathway and the release of VEGF.

  18. Data for accelerated degradation of calcium phosphate surface-coated polycaprolactone and polycaprolactone/bioactive glass composite scaffolds

    Directory of Open Access Journals (Sweden)

    Patrina S.P. Poh

    2016-06-01

    Full Text Available Polycaprolactone (PCL-based composite scaffolds containing 50 wt% of 45S5 bioactive glass (45S5 or strontium-substituted bioactive glass (SrBG particles were fabricated into scaffolds using melt-extrusion based additive manufacturing technique. Additionally, the PCL scaffolds were surface coated with a layer of calcium phosphate (CaP. For a comparison of the scaffold degradation, the scaffolds were then subjected to in vitro accelerated degradation by immersion in 5 M sodium hydroxide (NaOH solution for up to 7 days. The scaffold׳s morphology was observed by means of SEM imaging and scaffold mass loss was recorded over the experimental period.

  19. Data for accelerated degradation of calcium phosphate surface-coated polycaprolactone and polycaprolactone/bioactive glass composite scaffolds.

    Science.gov (United States)

    Poh, Patrina S P; Hutmacher, Dietmar W; Holzapfel, Boris M; Solanki, Anu K; Woodruff, Maria A

    2016-06-01

    Polycaprolactone (PCL)-based composite scaffolds containing 50 wt% of 45S5 bioactive glass (45S5) or strontium-substituted bioactive glass (SrBG) particles were fabricated into scaffolds using melt-extrusion based additive manufacturing technique. Additionally, the PCL scaffolds were surface coated with a layer of calcium phosphate (CaP). For a comparison of the scaffold degradation, the scaffolds were then subjected to in vitro accelerated degradation by immersion in 5 M sodium hydroxide (NaOH) solution for up to 7 days. The scaffold׳s morphology was observed by means of SEM imaging and scaffold mass loss was recorded over the experimental period.

  20. Fabrication and in vitro evaluation of a sponge-like bioactive-glass/gelatin composite scaffold for bone tissue engineering

    Energy Technology Data Exchange (ETDEWEB)

    Nadeem, Danish [Biomaterials Engineering Group, School of Oral and Dental Sciences, University of Bristol, BS1 2LY (United Kingdom); Kiamehr, Mostafa [Biomaterials and Tissue Engineering Group, Leeds Dental Institute, University of Leeds, LS2 9LU (United Kingdom); Yang, Xuebin [Biomaterials and Tissue Engineering Group, Leeds Dental Institute, University of Leeds, LS2 9LU (United Kingdom); NIHR Leeds Musculoskeletal Biomedical Research Unit, Chapel Allerton Hospital, Leeds LS7 4SA (United Kingdom); Su, Bo, E-mail: b.su@bristol.ac.uk [Biomaterials Engineering Group, School of Oral and Dental Sciences, University of Bristol, BS1 2LY (United Kingdom)

    2013-07-01

    In this work a bioactive composite scaffold, comprised of bioactive-glass and gelatin, is introduced. Through direct foaming a sponge-like composite of a sol–gel derived bioactive-glass (70S30C; 70% SiO{sub 2}, 30% CaO) and porcine gelatin was developed for use as a biodegradable scaffold for bone tissue engineering. The composite was developed to provide a suitable alternative to synthetic polymer based scaffolds, allowing directed regeneration of bone tissue. The fabricated scaffold was characterised through X-ray microtomography, scanning electron and light microscopy demonstrating a three dimensionally porous and interconnected structure, with an average pore size (170 μm) suitable for successful cell proliferation and tissue ingrowth. Acellular bioactivity was assessed through apatite formation during submersion in simulated body fluid (SBF) whereby the rate and onset of apatite nucleation was found to be comparable to that of bioactive-glass. Modification of dehydrothermal treatment parameters induced varying degrees of crosslinking, allowing the degradation of the composite to be tailored to suit specific applications and establishing its potential for a wide range of applications. Use of genipin to supplement crosslinking by dehydrothermal treatment provided further means of modifying degradability. Biocompatibility of the composite was qualified through successful cultures of human dental pulp stem cells (HDPSCs) on samples of the composite scaffold. Osteogenic differentiation of HDPSCs and extracellular matrix deposition were confirmed through positive alkaline phosphatase staining and immunohistochemistry. - Highlights: ► Optimised composition and fabrication produced sponge-like porosity (pore size ∼ 170 μm). ► Maximum aqueous stability via dehydrothermal treatment at 145 °C, for 48 h ► Biocompatibility and osteogenic potential confirmed via successful HDPSC cultures. ► Minimal toxicity exhibited in optimally crosslinked samples (10 m

  1. A new sol-gel synthesis of 45S5 bioactive glass using an organic acid as catalyst.

    Science.gov (United States)

    Faure, J; Drevet, R; Lemelle, A; Ben Jaber, N; Tara, A; El Btaouri, H; Benhayoune, H

    2015-02-01

    In this paper a new sol-gel approach was explored for the synthesis of the 45S5 bioactive glass. We demonstrate that citric acid can be used instead of the usual nitric acid to catalyze the sol-gel reactions. The substitution of nitric acid by citric acid allows to reduce strongly the concentration of the acid solution necessary to catalyze the hydrolysis of silicon and phosphorus alkoxides. Two sol-gel powders with chemical compositions very close to that of the 45S5 were obtained by using either a 2M nitric acid solution or either a 5mM citric acid solution. These powders were characterized and compared to the commercial Bioglass®. The surface properties of the two bioglass powders were assessed by scanning electron microscopy (SEM) and by Brunauer-Emmett-Teller method (BET). The Fourier transformed infrared spectroscopy (FTIR) and the X-ray diffraction (XRD) revealed a partial crystallization associated to the formation of crystalline phases on the two sol-gel powders. The in vitro bioactivity was then studied at the key times during the first hours of immersion into acellular Simulated Body Fluid (SBF). After 4h immersion into SBF we clearly demonstrate that the bioactivity level of the two sol-gel powders is similar and much higher than that of the commercial Bioglass®. This bioactivity improvement is associated to the increase of the porosity and the specific surface area of the powders synthesized by the sol-gel process. Moreover, the nitric acid is efficiently substituted by the citric acid to catalyze the sol-gel reactions without alteration of the bioactivity of the 45S5 bioactive glass. Copyright © 2014 Elsevier B.V. All rights reserved.

  2. Electrophoretic deposition of ZnO/alginate and ZnO-bioactive glass/alginate composite coatings for antimicrobial applications

    Energy Technology Data Exchange (ETDEWEB)

    Cordero-Arias, L.; Cabanas-Polo, S.; Goudouri, O.M. [Institute of Biomaterials, Department of Materials Science and Engineering, University of Erlangen-Nuremberg, Cauerstrasse 6, D-91058 Erlangen (Germany); Misra, S.K. [Materials Science and Engineering, Indian Institute of Technology Gandhinagar, Ahmedabad 382424 (India); Gilabert, J. [Institute of Ceramics Materials (ITC), University Jaume I, Avenida Vicent SosBaynat, 12006 Castellon (Spain); Valsami-Jones, E. [School of Geography, Earth and Environmental Sciences, University of Birmingham, Edgbaston, Birmingham B15 2TT (United Kingdom); Sanchez, E. [Institute of Ceramics Materials (ITC), University Jaume I, Avenida Vicent SosBaynat, 12006 Castellon (Spain); Virtanen, S. [Institute for Surface Science and Corrosion (LKO, WW4), Department of Materials Science and Engineering, University of Erlangen-Nuremberg, Martensstrasse 7, D-91058 Erlangen (Germany); Boccaccini, A.R., E-mail: aldo.boccaccini@ww.uni-erlangen.de [Institute of Biomaterials, Department of Materials Science and Engineering, University of Erlangen-Nuremberg, Cauerstrasse 6, D-91058 Erlangen (Germany)

    2015-10-01

    Two organic/inorganic composite coatings based on alginate, as organic matrix, and zinc oxide nanoparticles (n-ZnO) with and without bioactive glass (BG), as inorganic components, intended for biomedical applications, were developed by electrophoretic deposition (EPD). Different n-ZnO (1–10 g/L) and BG (1–1.5 g/L) contents were studied for a fixed alginate concentration (2 g/L). The presence of n-ZnO was confirmed to impart antibacterial properties to the coatings against gram-negative bacteria Escherichia coli, while the BG induced the formation of hydroxyapatite on coating surfaces thereby imparting bioactivity, making the coating suitable for bone replacement applications. Coating composition was analyzed by thermogravimetric analysis (TG), Fourier transform infrared spectroscopy (FTIR), X-ray diffraction (XRD) and energy dispersive X-ray spectroscopy (EDS) analyses. Scanning electron microscopy (SEM) was employed to study both the surface and the cross section morphology of the coatings. Polarization curves of the coated substrates made in cell culture media at 37 °C confirmed the corrosion protection function of the novel organic/inorganic composite coatings. - Highlights: • Organic–inorganic nanocomposite coatings fabricated by electrophoretic deposition • nZnO and bioactive glass containing alginate coatings exhibit antibacterial effect. • Bioactive character and anticorrosion function of coatings demonstrated.

  3. Genotoxicity effects of nano bioactive glass and Novabone bioglass on gingival fibroblasts using single cell gel electrophoresis (comet assay: An in vitro study

    Directory of Open Access Journals (Sweden)

    Mohammad Tavakoli

    2012-01-01

    Conclusion: The findings of this study have demonstrated that novel nano bioactive glass had no genotoxicity in concentrations lower than 4 mg/ml. Nanoparticles have a higher surface area in comparison to microparticles and thus, the amount and rate of ion release for nanoparticles are extremely higher. This difference is the main reason for the different genotoxicity of nano bioactive glass and micro Novabone bioglass in the concentrations higher than 4 mg/ml.

  4. The pro-angiogenic properties of multi-functional bioactive glass composite scaffolds

    KAUST Repository

    Gerhardt, Lutz Christian

    2011-06-01

    The angiogenic properties of micron-sized (m-BG) and nano-sized (n-BG) bioactive glass (BG) filled poly(D,L lactide) (PDLLA) composites were investigated. On the basis of cell culture work investigating the secretion of vascular endothelial growth factor (VEGF) by human fibroblasts in contact with composite films (0, 5, 10, 20 wt %), porous 3D composite scaffolds, optimised with respect to the BG filler content capable of inducing angiogenic response, were produced. The in vivo vascularisation of the scaffolds was studied in a rat animal model and quantified using stereological analyses. The prepared scaffolds had high porosities (81-93%), permeability (k = 5.4-8.6 × 10-9 m2) and compressive strength values (0.4-1.6 MPa) all in the range of trabecular bone. On composite films containing 20 wt % m-BG or n-BG, human fibroblasts produced 5 times higher VEGF than on pure PDLLA films. After 8 weeks of implantation, m-BG and n-BG containing scaffolds were well-infiltrated with newly formed tissue and demonstrated higher vascularisation and percentage blood vessel to tissue (11.6-15.1%) than PDLLA scaffolds (8.5%). This work thus shows potential for the regeneration of hard-soft tissue defects and increased bone formation arising from enhanced vascularisation of the construct. © 2011 Elsevier Ltd.

  5. Effects of Chemically Doped Bioactive Borate Glass on Neuron Regrowth and Regeneration.

    Science.gov (United States)

    Gupta, Brinda; Papke, Jason B; Mohammadkhah, Ali; Day, Delbert E; Harkins, Amy B

    2016-12-01

    Peripheral nerve injuries present challenges to regeneration. Currently, the gold standard for nerve repair is an autograft that results in another region of the body suffering nerve damage. Previously, bioactive borate glass (BBG) has been studied in clinical trials to treat patients with non-healing wounds, and we have reported that BBG is conducive for soft tissue repair. BBG provides structural support, degrades in a non-cytotoxic manner, and can be chemically doped. Here, we tested a wide range of chemical compounds that are reported to have neuroprotective characteristics to promote regeneration of peripheral neurons after traumatic injury. We hypothesized that chemical dopants added in trace amounts to BBG would improve neuronal survival and neurite outgrowth from dorsal root ganglion (DRG) explants. We measured neurite outgrowth from whole DRG explants, and survival rates of dissociated neurons and support cells that comprise the DRG. Results show that chemically doped BBGs have differentially variable effects on neuronal survival and outgrowth, with iron, gallium, and zinc improving outgrowth of neurons, and iodine causing the most detriment to neurons. Because chemically doped BBGs support increased nerve regrowth and survival, they show promise for use in peripheral nerve regeneration.

  6. Bioactive glass and hydroxyapatite thin films obtained by pulsed laser deposition

    Energy Technology Data Exchange (ETDEWEB)

    Gyorgy, E. [National Institute for Lasers, Plasma and Radiation Physics, P.O. Box MG 36, 77125 Bucharest (Romania) and Consejo Superior de Investigaciones Cientificas, Instituto de Ciencia de Materiales de Barcelona, Campus UAB, 08193 Bellaterra (Spain)]. E-mail: egyorgy@icmab.es; Grigorescu, S. [National Institute for Lasers, Plasma and Radiation Physics, P.O. Box MG 36, 77125 Bucharest (Romania); Socol, G. [National Institute for Lasers, Plasma and Radiation Physics, P.O. Box MG 36, 77125 Bucharest (Romania); Mihailescu, I.N. [National Institute for Lasers, Plasma and Radiation Physics, P.O. Box MG 36, 77125 Bucharest (Romania); Janackovic, D. [Faculty of Technology and Metallurgy, University of Belgrade, Karnegijeva 4, 11000 Belgrade (Serbia); Dindune, A. [Institute of Inorganic Chemistry of the Riga Technical University (Latvia); Plasma and Ceramic Technologies Ltd. (PCT Ltd.) (Latvia); Kanepe, Z. [Institute of Inorganic Chemistry of the Riga Technical University (Latvia); Plasma and Ceramic Technologies Ltd. (PCT Ltd.) (Latvia); Palcevskis, E. [Plasma and Ceramic Technologies Ltd. (PCT Ltd.) (Latvia); Zdrentu, E.L. [Institute of Biochemistry, Splaiul Independentei 296, Bucharest (Romania); Petrescu, S.M. [Institute of Biochemistry, Splaiul Independentei 296, Bucharest (Romania)

    2007-07-31

    Bioactive glass (BG), calcium hydroxyapatite (HA), and ZrO{sub 2} doped HA thin films were grown by pulsed laser deposition on Ti substrates. An UV KrF{sup *} ({lambda} = 248 nm, {tau} {>=} 7 ns) excimer laser was used for the multi-pulse irradiation of the targets. The substrates were kept at room temperature or heated during the film deposition at values within the (400-550 deg. C) range. The depositions were performed in oxygen and water vapor atmospheres, at pressure values in the range (5-40 Pa). The HA coatings were heat post-treated for 6 h in a flux of hot water vapors at the same temperature as applied during deposition. The surface morphology, chemical composition, and crystalline quality of the obtained thin films were studied by scanning electron microscopy, atomic force microscopy, and X-ray diffractometry. The films were seeded for in vitro tests with Hek293 (human embryonic kidney) cells that revealed a good adherence on the deposited layers. Biocompatibility tests showed that cell growth was better on HA than on BG thin films.

  7. One-pot synthesis of magnetic, macro/mesoporous bioactive glasses for bone tissue engineering

    Directory of Open Access Journals (Sweden)

    Dan Wang, Huiming Lin, Jingjie Jiang, Xiao Han, Wei Guo, Xiaodan Wu, Yingxue Jin and Fengyu Qu

    2013-01-01

    Full Text Available Magnetic and macro/mesoporous bioactive glasses were synthesized by a one-pot method via a handy salt leaching technique. It was identified to be an effective and simple synthetic strategy. The non-ionic triblock copolymer, poly(ethylene glycol-block-poly(propylene glycol-block-poly(ethylene glycol (P123, was used as the structure directing agent for mesoporous structure but also as the reductant to reduce the iron source into magnetic iron oxide. The prepared materials exhibited excellent super-paramagnetic property with interconnected macroporous (200–300 μm and mesoporous (3.4 nm structure. Furthermore, their outstanding drug storage/release properties and rapid (5 induction of hydroxyapatite growth ability were investigated after immersing in simulated body fluid solution at 37 °C. Notably, the biocompatibility assessment confirmed that the materials obtained presented good biocompatibility and enhanced adherence of HeLa cells. Herein, the novel materials are expected to have potential application for bone tissue engineering.

  8. Evaluation of antimicrobial properties of bioactive glass used in regenerative periodontal therapy

    Directory of Open Access Journals (Sweden)

    Ram Sabarish Chandrasekar

    2015-01-01

    Full Text Available Context: Bone grafting materials which have an inherent anti-microbial property against initial colonizers of plaque bacteria would be useful in regenerative periodontal surgical procedures. Aims: This study was performed to analyze the antibacterial property of a Perioglas™ against a common oral commensal Streptococcus salivarius (early colonizer. Settings and Design: In vitro observational study. Materials and Methods: Perioglas™ (in various concentrations was assessed for its antibacterial property against the ATCC 13419 strain of S. salivarius. The anti-microbial activity was analyzed in terms of reduction in colony-forming units in culture plates and smear following a 24 h incubation at 37°C. Statistical Analysis Used: Observational study - No statistical analysis applicable. Results: The bioactive glass (BAG exerted an antibacterial effect against the S. salivarius in the suspending media and smear. The antibacterial activity of BAG increased in proportion with its concentration. Conclusions: Perioglas™ demonstrated a considerable antibacterial effect against S. salivarius at 50 mg/mL concentration.

  9. Effect of nano-sized bioactive glass particles on the angiogenic properties of collagen based composites.

    Science.gov (United States)

    Vargas, Gabriela E; Haro Durand, Luis A; Cadena, Vanesa; Romero, Marcela; Mesones, Rosa Vera; Mačković, Mirza; Spallek, Stefanie; Spiecker, Erdmann; Boccaccini, Aldo R; Gorustovich, Alejandro A

    2013-05-01

    Angiogenesis is essential for tissue regeneration and repair. A growing body of evidence shows that the use of bioactive glasses (BG) in biomaterial-based tissue engineering (TE) strategies may improve angiogenesis and induce increased vascularization in TE constructs. This work investigated the effect of adding nano-sized BG particles (n-BG) on the angiogenic properties of bovine type I collagen/n-BG composites. Nano-sized (20-30 nm) BG particles of nominally 45S5 Bioglass® composition were used to prepare composite films, which were characterized by scanning electron microscopy (SEM) and transmission electron microscopy (TEM). The in vivo angiogenic response was evaluated using the quail chorioallantoic membrane (CAM) as an model of angiogenesis. At 24 h post-implantation, 10 wt% n-BG containing collagen films stimulated angiogenesis by increasing by 41 % the number of blood vessels branch points. In contrast, composite films containing 20 wt% n-BG were found to inhibit angiogenesis. This experimental study provides the first evidence that addition of a limited concentration of n-BG (10 wt%) to collagen films induces an early angiogenic response making selected collagen/n-BG composites attractive matrices for tissue engineering and regenerative medicine.

  10. Femtosecond laser induced surface modification for prevention of bacterial adhesion on 45S5 bioactive glass

    Science.gov (United States)

    Shaikh, Shazia; Singh, Deepti; Subramanian, Mahesh; Kedia, Sunita; Singh, Anil Kumar; Singh, Kulwant; Gupta, Nidhi; Sinha, Sucharita

    2018-02-01

    Bacterial attachment and biofilm formation on implant surface has been a major concern in hospital and industrial environment. Prevention of bacterial infections of implant surface through surface treatment could be a potential solution and hence this has become a key area of research. In the present study, the antibacterial and biocompatible properties of femtosecond laser surface treated 45S5 bioactive glass (BG) have been investigated. Adhesion and sustainability of both gram positive S. aureus and gram negative P.aeruginosa and E. coli nosocomial bacteria on untreated and laser treated BG samples has been explored. An imprint method has been used to visualize the growth of bacteria on the sample surface. We observed complete bacterial rejection potentially reducing risk of biofilm formation on laser treated surface. This was correlated with surface roughness, wettability and change in surface chemical composition of the samples before and after laser treatment. Biocompatibility of the laser treated BG was demonstrated by studying the anchoring and growth of human cervix cell line INT407. Our results demonstrate that, laser surface modification of BG enables enhanced bacterial rejection without affecting its biocompatibility towards growth of human cells on it. These results open a significantly potential approach towards use of laser in successfully imparting desirable characteristics to BG based bio-implants and devices.

  11. Electrophoretic Deposition as a New Bioactive Glass Coating Process for Orthodontic Stainless Steel

    Directory of Open Access Journals (Sweden)

    Kyotaro Kawaguchi

    2017-11-01

    Full Text Available This study investigated the surface modification of orthodontic stainless steel using electrophoretic deposition (EPD of bioactive glass (BG. The BG coatings were characterized by spectrophotometry, scanning electron microscopy with energy dispersive X-ray spectrometry, and X-ray diffraction. The frictional properties were investigated using a progressive load scratch test. The remineralization ability of the etched dental enamel was studied according to the time-dependent mechanical properties of the enamel using a nano-indentation test. The EPD process using alternating current produced higher values in both reflectance and lightness. Additionally, the BG coating was thinner than that prepared using direct current, and was completely amorphous. All of the BG coatings displayed good interfacial adhesion, and Si and O were the major components. Most BG-coated specimens produced slightly higher frictional forces compared with non-coated specimens. The hardness and elastic modulus of etched enamel specimens immersed with most BG-coated specimens recovered significantly with increasing immersion time compared with the non-coated specimen, and significant acid-neutralization was observed for the BG-coated specimens. The surface modification technique using EPD and BG coating on orthodontic stainless steel may assist the development of new non-cytotoxic orthodontic metallic appliances having satisfactory appearance and remineralization ability.

  12. Characterization of nodules induced by bioactive glass on cultured periodontal-ligament fibroblasts.

    Science.gov (United States)

    Kubo, K; Kamada, T; Matsuyama, T; Tsukasa, N; Uehara, M; Izumi, Y; Kitano, M; Ogino, M; Sueda, T

    1995-04-01

    We previously reported that materials leached from bioactive glass (BG) and vitamin D3 induced the formation of nodules on cultured periodontal-ligament fibroblasts (PLF). In this study, we have investigated the relationship between the conditions of the materials and nodule formation, analyzed morphologically, and also studied whether the production of nodules was specific to cultured PLF. PLF and skin fibroblasts were cultured in the presence or absence of BG. The amounts of calcium, phosphate, sodium and silicon in the culture medium and the number of nodules were measured at the 55th day. The nodules were observed microscopically and analyzed using an X-ray microanalyzer. In PLF, nodules were formed regardless of the presence or absence of BG; however, they were more numerous in the presence of BG. In skin fibroblasts, nodules were not observed. The amounts of calcium and silicon were higher in the presence of BG, while the amount of phosphate was lower. The nodules appeared crystalline with a spongy structure and contained calcium and phosphorus. Our results show that the nodules were associated with PLF and precipitated by the materials (higher concentrations of calcium and silicon), and they were spongy crystal composed of calcium and phosphorus.

  13. Periodontal Regeneration Using Strontium-Loaded Mesoporous Bioactive Glass Scaffolds in Osteoporotic Rats

    Science.gov (United States)

    Zhang, Yufeng; Wei, Lingfei; Wu, Chengtie; Miron, Richard J.

    2014-01-01

    Recent studies demonstrate that the rate of periodontal breakdown significantly increased in patients compromised from both periodontal disease and osteoporosis. One pharmacological agent used for their treatment is strontium renalate due to its simultaneous ability to increase bone formation and halt bone resorption. The aim of the present study was to achieve periodontal regeneration of strontium-incorporated mesoporous bioactive glass (Sr-MBG) scaffolds in an osteoporotic animal model carried out by bilateral ovariectomy (OVX). 15 female Wistar rats were randomly assigned to three groups: control unfilled periodontal defects, 2) MBG alone and 3) Sr-MBG scaffolds. 10 weeks after OVX, bilateral fenestration defects were created at the buccal aspect of the first mandibular molar and assessed by micro-CT and histomorphometric analysis after 28 days. Periodontal fenestration defects treated with Sr-MBG scaffolds showed greater new bone formation (46.67%) when compared to MBG scaffolds (39.33%) and control unfilled samples (17.50%). The number of TRAP-positive osteoclasts was also significantly reduced in defects receiving Sr-MBG scaffolds. The results from the present study suggest that Sr-MBG scaffolds may provide greater periondontal regeneration. Clinical studies are required to fully characterize the possible beneficial effect of Sr-releasing scaffolds for patients suffering from a combination of both periodontal disease and osteoporosis. PMID:25116811

  14. Enamel matrix derivative alone or in combination with a bioactive glass in wide intrabony defects.

    Science.gov (United States)

    Kuru, Bahar; Yilmaz, Selçuk; Argin, Kiliçaslan; Noyan, Ulkü

    2006-09-01

    This controlled clinical study investigated the clinical and radiographic outcome of wide intrabony periodontal defects treated by enamel matrix derivatives alone or in combination with a bioactive glass over a period of 8 months. Twenty-three chronic periodontitis patients, who received initial therapy and had radiographical interproximal defects with an associated probing depth of 6 mm or more and an intrabony component of at least 4 mm, were included. Each of the patients, contributing at least one intrabony defect, was treated with either enamel matrix derivative alone (group 1, n=10) or the combination (group 2, n=13). In both groups, all clinical and radiographical parameters were improved. Groups 1 and 2 presented a mean pocket reduction of 5.03+/-0.89 and 5.73+/-0.80 mm, recession of 0.97+/-0.24 and 0.56+/-0.18 mm, relative attachment gain of 4.06+/-1.06 and 5.17+/-0.85 mm, and radiographic bone gain of 2.15+/-0.42 and 2.76+/-0.69 mm, respectively. An intergroup comparison revealed significant differences for all of the parameters, yielding a more favorable outcome towards the combined approach. Within the limits of the study, both treatments resulted in marked clinical and radiographical improvements, but combined treatment seemed to enhance the results in the treatment of wide intrabony defects.

  15. Alternating Current Electrophoretic Deposition of Antibacterial Bioactive Glass-Chitosan Composite Coatings

    Directory of Open Access Journals (Sweden)

    Sigrid Seuss

    2014-07-01

    Full Text Available Alternating current (AC electrophoretic deposition (EPD was used to produce multifunctional composite coatings combining bioactive glass (BG particles and chitosan. BG particles of two different sizes were used, i.e., 2 μm and 20–80 nm in average diameter. The parameter optimization and characterization of the coatings was conducted by visual inspection and by adhesion strength tests. The optimized coatings were investigated in terms of their hydroxyapatite (HA forming ability in simulated body fluid (SBF for up to 21 days. Fourier transform infrared (FTIR spectroscopy results showed the successful HA formation on the coatings after 21 days. The first investigations were conducted on planar stainless steel sheets. In addition, scaffolds made from a TiAl4V6 alloy were considered to show the feasibility of coating of three dimensional structures by EPD. Because both BG and chitosan are antibacterial materials, the antibacterial properties of the as-produced coatings were investigated using E. coli bacteria cells. It was shown that the BG particle size has a strong influence on the antibacterial properties of the coatings.

  16. Remineralization Property of an Orthodontic Primer Containing a Bioactive Glass with Silver and Zinc

    Directory of Open Access Journals (Sweden)

    Seung-Min Lee

    2017-10-01

    Full Text Available White spot lesions (WSLs are irreversible damages in orthodontic treatment due to excessive etching or demineralization by microorganisms. In this study, we conducted a mechanical and cell viability test to examine the antibacterial properties of 0.2% and 1% bioactive glass (BAG and silver-doped and zinc-doped BAGs in a primer and evaluated their clinical applicability to prevent WSLs. The microhardness statistically significantly increased in the adhesive-containing BAG, while the other samples showed no statistically significant difference compared with the control group. The shear bond strength of all samples increased compared with that of the control group. The cell viability of the control and sample groups was similar within 24 h, but decreased slightly over 48 h. All samples showed antibacterial properties. Regarding remineralization property, the group containing 0.2% of the samples showed remineralization properties compared with the control group, but was not statistically significant; further, the group containing 1% of the samples showed a significant difference compared with the control group. Among them, the orthodontic bonding primer containing 1% silver-doped BAG showed the highest remineralization property. The new orthodontic bonding primer used in this study showed an antimicrobial effect, chemical remineralization effect, and WSL prevention as well as clinically applicable properties, both physically and biologically.

  17. 3D cell culture to determine in vitro biocompatibility of bioactive glass in association with chitosan.

    Science.gov (United States)

    Bédouin, Y; Pellen Mussi, P; Tricot-Doleux, S; Chauvel-Lebret, D; Auroy, P; Ravalec, X; Oudadesse, H; Perez, F

    2015-01-01

    This study reports the in vitro biocompatibility of a composite biomaterial composed of 46S6 bioactive glass in association with chitosan (CH) by using 3D osteoblast culture of SaOS2. The 46S6 and CH composite (46S6-CH) forms small hydroxyapatite crystals on its surface after only three days immersion in the simulated body fluid. For 2D osteoblast culture, a significant increase in cell proliferation was observed after three days of contact with 46S6 or 46S6-CH-immersed media. After six days, 46S6-CH led to a significant increase in cell proliferation (128%) compared with pure 46S6 (113%) and pure CH (122%). For 3D osteoblast culture, after six days of culture, there was an increase in gene expression of markers of the early osteoblastic differentiation (RUNX2, ALP, COL1A1). Geometric structures corresponding to small apatite clusters were observed by SEM on the surface of the spheroids cultivated with 46S6 or 46S6-CH-immersed media. We showed different cellular responses depending on the 2D and 3D cell culture model. The induction of osteoblast differentiation in the 3D cell culture explained the differences of cell proliferation in contact with 46S6, CH or 46S6-CH-immersed media. This study confirmed that the 3D cell culture model is a very promising tool for in vitro biological evaluation of bone substitutes' properties.

  18. Management of radicular cysts using platelet-rich fibrin and bioactive glass: a report of two cases.

    Science.gov (United States)

    Zhao, Jiing-Huei; Tsai, Chung-Hung; Chang, Yu-Chao

    2014-07-01

    Platelet-rich fibrin (PRF) created by Choukroun's protocol concentrates most platelets and leukocytes from a blood harvest into a single autologous fibrin biomaterial. However, no current data is available concerning the use of PRF for the treatment of periapical lesions. Two cases of radicular cysts were reported using an interdisciplinary approach, including regular endodontic therapy followed by surgical management with PRF and bioactive glass. Two cases of radicular cysts presented as an incidental radiographic finding, appearing as an apical radiolucency with well-circumscribed sclerotic borders. After regular endodontic retreatment, cystic lining/granulation tissues were enucleated and the periradicular bony defect was grafted using PRF and bioactive glass. Then, PRF was applied to serve as a membrane over the grafted defects. Recall periapical radiographs of Case 1 and cone beam computer tomography of Case 2 showed satisfactory healing of the periapical pathosis. In Case 2, the bony defect appeared completely healed at 4 months surgical reentry and the new bone was clinically very dense and mature. The results of these case reports show that the combination of PRF and bioactive glass is an effective modality of regenerative treatment for radicular cysts. Copyright © 2012. Published by Elsevier B.V.

  19. Management of radicular cysts using platelet-rich fibrin and bioactive glass: A report of two cases

    Directory of Open Access Journals (Sweden)

    Jiing-Huei Zhao

    2014-07-01

    Full Text Available Platelet-rich fibrin (PRF created by Choukroun’s protocol concentrates most platelets and leukocytes from a blood harvest into a single autologous fibrin biomaterial. However, no current data is available concerning the use of PRF for the treatment of periapical lesions. Two cases of radicular cysts were reported using an interdisciplinary approach, including regular endodontic therapy followed by surgical management with PRF and bioactive glass. Two cases of radicular cysts presented as an incidental radiographic finding, appearing as an apical radiolucency with well-circumscribed sclerotic borders. After regular endodontic retreatment, cystic lining/granulation tissues were enucleated and the periradicular bony defect was grafted using PRF and bioactive glass. Then, PRF was applied to serve as a membrane over the grafted defects. Recall periapical radiographs of Case 1 and cone beam computer tomography of Case 2 showed satisfactory healing of the periapical pathosis. In Case 2, the bony defect appeared completely healed at 4 months surgical reentry and the new bone was clinically very dense and mature. The results of these case reports show that the combination of PRF and bioactive glass is an effective modality of regenerative treatment for radicular cysts.

  20. Teicoplanin-loaded borate bioactive glass implants for treating chronic bone infection in a rabbit tibia osteomyelitis model.

    Science.gov (United States)

    Zhang, Xin; Jia, Weitao; Gu, Yifei; Xiao, Wei; Liu, Xin; Wang, Deping; Zhang, Changqing; Huang, Wenhai; Rahaman, Mohamed N; Day, Delbert E; Zhou, Nai

    2010-08-01

    The treatment of chronic osteomyelitis (bone infection) remains a clinical challenge. In this work, pellets composed of a chitosan-bonded mixture of borate bioactive glass particles (teicoplanin powder (antibiotic), were evaluated in vitro and in vivo for treating chronic osteomyelitis induced by methicillin-resistant Staphylococcus aureus (MRSA) in a rabbit model. When immersed in phosphate-buffered saline, the pellets showed sustained release of teicoplanin over 20-30 days, while the bioactive glass converted to hydroxyapatite (HA) within 7 days, eventually forming a porous HA structure. Implantation of the teicoplanin-loaded pellets in a rabbit tibia osteomyelitis model resulted in the detection of teicoplanin in the blood for about 9 days. The implants converted to a bone-like HA graft, and supported the ingrowth of new bone into the tibia defects within 12 weeks of implantation. Microbiological, histological and scanning electron microscopy techniques showed that the implants provided a cure for the bone infection. The results indicate that the teicoplanin-loaded borate bioactive glass implant, combining sustained drug release with the ability to support new bone ingrowth, could provide a method for treating chronic osteomyelitis. Copyright 2010 Elsevier Ltd. All rights reserved.

  1. Effect of sintering temperature variations on fabrication of 45S5 bioactive glass-ceramics using rice husk as a source for silica.

    Science.gov (United States)

    Leenakul, Wilaiwan; Tunkasiri, Tawee; Tongsiri, Natee; Pengpat, Kamonpan; Ruangsuriya, Jetsada

    2016-04-01

    45S5 bioactive glass is a highly bioactive substance that has the ability to promote stem cell differentiation into osteoblasts--the cells that create bone matrix. The aim of this work is to analyze physical and mechanical properties of 45S5 bioactive glass fabricated by using rice husk ash as its silica source. The 45S5 bioactive glass was prepared by melting the batch at 1300 °C for 3h. The samples were sintered at different temperatures ranging from 900 to 1050 °C with a fixed dwell-time of 2h. The phase transitions, density, porosity and microhardness values were investigated and reported. DTA analysis was used to examine the crystallization temperatures of the glasses prepared. We found that the sintering temperature had a significant effect on the mechanical and physical properties of the bioactive glass. The XRD showed that when the sintering temperature was above 650 °C, crystallization occurred and bioactive glass-ceramics with Na2Ca2Si3O9, Na2Ca4(PO4)2SiO4 and Ca3Si2O7 were formed. The optimum sintering temperature resulting in maximum mechanical values was around 1050 °C, with a high density of 2.27 g/cm(3), 16.96% porosity and the vicker microhardness value of 364HV. Additionally, in vitro assay was used to examine biological activities in stimulated body fluid (SBF). After incubation in SBF for 7 days, all of the samples showed formations of apatite layers indicating that the 45S5 bioactive glasses using rice husk as a raw material were also bioactive. Copyright © 2015 Elsevier B.V. All rights reserved.

  2. Kinetics of a bioactive compound (caffeine) mobility at the vicinity of the mechanical glass transition temperature induced by gelling polysaccharide.

    Science.gov (United States)

    Jiang, Bin; Kasapis, Stefan

    2011-11-09

    An investigation of the diffusional mobility of a bioactive compound (caffeine) within the high-solid (80.0% w/w) matrices of glucose syrup and κ-carrageenan plus glucose syrup exhibiting distinct mechanical glass transition properties is reported. The experimental temperature range was from 20 to -60 °C, and the techniques of modulated differential scanning calorimetry, small deformation dynamic oscillation in shear, and UV spectrometry were employed. Calorimetric and mechanical measurements were complementary in recording the relaxation dynamics of high-solid matrices upon controlled heating. Predictions of the reaction rate theory and the combined WLF/free volume framework were further utilized to pinpoint the glass transition temperature (T(g)) of the two matrices in the softening dispersion. Independent of composition, calorimetry yielded similar T(g) predictions for both matrices at this level of solids. Mechanical experimentation, however, was able to detect the effect of adding gelling polysaccharide to glucose syrup as an accelerated pattern of vitrification leading to a higher value of T(g). Kinetic rates of caffeine diffusion within the experimental temperature range were taken with UV spectroscopy. These demonstrated the pronounced effect of the gelling κ-carrageenan/glucose syrup mixture to retard diffusion of the bioactive compound near the mechanical T(g). Modeling of the diffusional mobility of caffeine produced activation energy and fractional free-volume estimates, which were distinct from those of the carbohydrate matrix within the glass transition region. This result emphasizes the importance of molecular interactions between macromolecular matrix and small bioactive compound in glass-related relaxation phenomena.

  3. Efficacy of Modified Bioactive Glass for Dentin Remineralization and Obstruction of Dentinal Tubules

    Directory of Open Access Journals (Sweden)

    Mahshid Saffarpour

    2017-10-01

    Full Text Available Objectives: This study assessed the efficacy of modified bioactive glass (MBG for dentin remineralization and obstruction of dentinal tubules.Materials and Methods: Thirty-six dentin discs were made from 20 third molars and were stored in 12% lactic acid solution for two weeks to induce demineralization. The samples were divided into three groups (n=12: 1- BG, 2- BG modified with 5% strontium (Sr and 3- BG modified with 10% Sr. After applying the BG, the samples were stored in artificial saliva for 7, 14 and 21 days. Attenuated Total Reflection-Fourier Transform Infrared Spectroscopy (ATR-FTIR, X-ray Diffraction (XRD analysis, Scanning Electron Microscopy (SEM, and Energy-Dispersive X-ray (EDX analysis were used to assess remineralization. Also, 6 dentin discs were divided into three groups of BG, BG modified with 5% Sr and BG modified with 10% Sr, to examine tubular occlusion. The discs were etched using 0.5M of EDTA for two minutes and were stored in artificial saliva for 7 days. Changes in dentin surface morphology were evaluated under SEM.Results: Group 3 showed high rates of remineralization at days 7 and 14, although the rate decreased at day 21. Group 2 exhibited high rates of remineralization at days 7, 14 and 21. Dentinal tubules were partially occluded by BG and BG modified with 5% Sr, while they were almost completely obstructed after the use of BG modified with 10% Sr.Conclusions: Strontium increases remineralization. Addition of 10% Sr to BG enhances apatite formation; however, the apatite dissolves over time. Addition of 5% Sr to BG stabilizes the apatite lattice and increases the remineralization.

  4. Bioactive glass-reinforced bioceramic ink writing scaffolds: sintering, microstructure and mechanical behavior.

    Science.gov (United States)

    Shao, Huifeng; Yang, Xianyan; He, Yong; Fu, Jianzhong; Liu, Limin; Ma, Liang; Zhang, Lei; Yang, Guojing; Gao, Changyou; Gou, Zhongru

    2015-09-10

    The densification of pore struts in bioceramic scaffolds is important for structure stability and strength reliability. An advantage of ceramic ink writing is the precise control over the microstructure and macroarchitecture. However, the use of organic binder in such ink writing process would heavily affect the densification of ceramic struts and sacrifice the mechanical strength of porous scaffolds after sintering. This study presents a low-melt-point bioactive glass (BG)-assisted sintering strategy to overcome the main limitations of direct ink writing (extrusion-based three-dimensional printing) and to produce high-strength calcium silicate (CSi) bioceramic scaffolds. The 1% BG-added CSi (CSi-BG1) scaffolds with rectangular pore morphology sintered at 1080 °C have a very small BG content, readily induce apatite formation, and show appreciable linear shrinkage (∼21%), which is consistent with the composite scaffolds with less or more BG contents sintered at either the same or a higher temperature. These CSi-BG1 scaffolds also possess a high elastic modulus (∼350 MPa) and appreciable compressive strength (∼48 MPa), and show significant strength enhancement after exposure to simulated body fluid-a performance markedly superior to those of pure CSi scaffolds. Particularly, the honeycomb-pore CSi-BG1 scaffolds show markedly higher compressive strength (∼88 MPa) than the scaffolds with rectangular, parallelogram, and Archimedean chord pore structures. It is suggested that this approach can potentially facilitate the translation of ceramic ink writing and BG-assisted sintering of bioceramic scaffold technologies to the in situ bone repair.

  5. A Novel Injectable Borate Bioactive Glass Cement as an Antibiotic Delivery Vehicle for Treating Osteomyelitis

    Science.gov (United States)

    Cui, Xu; Gu, Yi-Fei; Jia, Wei-Tao; Rahaman, Mohamed N.; Wang, Yang; Huang, Wen-Hai; Zhang, Chang-Qing

    2014-01-01

    Background A novel injectable cement composed of chitosan-bonded borate bioactive glass (BG) particles was evaluated as a carrier for local delivery of vancomycin in the treatment of osteomyelitis in a rabbit tibial model. Materials and Methods The setting time, injectability, and compressive strength of the borate BG cement, and the release profile of vancomycin from the cement were measured in vitro. The capacity of the vancomycin-loaded BG cement to eradicate methicillin-resistant Staphylococcus aureus (MRSA)-induced osteomyelitis in rabbit tibiae in vivo was evaluated and compared with that for a vancomycin-loaded calcium sulfate (CS) cement and for intravenous injection of vancomycin. Results The BG cement had an injectability of >90% during the first 3 minutes after mixing, hardened within 30 minutes and, after hardening, had a compressive strength of 18±2 MPa. Vancomycin was released from the BG cement into phosphate-buffered saline for up to 36 days, and the cumulative amount of vancomycin released was 86% of the amount initially loaded into the cement. In comparison, vancomycin was released from the CS cement for up 28 days and the cumulative amount released was 89%. Two months post-surgery, radiography and microbiological tests showed that the BG and CS cements had a better ability to eradicate osteomyelitis when compared to intravenous injection of vancomycin, but there was no significant difference between the BG and CS cements in eradicating the infection. Histological examination showed that the BG cement was biocompatible and had a good capacity for regenerating bone in the tibial defects. Conclusions These results indicate that borate BG cement is a promising material both as an injectable carrier for vancomycin in the eradication of osteomyelitis and as an osteoconductive matrix to regenerate bone after the infection is cured. PMID:24427311

  6. Bioactive glass combined with bisphosphonates provides protection against biofilms formed by the periodontal pathogen Aggregatibacter actinomycetemcomitans.

    Science.gov (United States)

    Hiltunen, Anna K; Skogman, Malena E; Rosenqvist, Kirsi; Juvonen, Helka; Ihalainen, Petri; Peltonen, Jouko; Juppo, Anne; Fallarero, Adyary

    2016-03-30

    Biofilms play a pivotal role in the progression of periodontitis and they can be treated with antiseptics (i.e. chlorhexidine) or antibiotics, but these therapeutic alternatives are unable of ameliorating periodontal alveolar bone loss, which has been, on the other hand, successfully treated with bone-preserving agents. The improved bone formation achieved in animal models by the combination of two such agents: bioactive glass (BAG) and bisphosphonates has attracted the interest for further exploring dental applications. However, the antimicrobial effects that may result from combining them have not been yet investigated. Here, our aim was to explore the anti-biofilm effects that could result from combining BAG with bisphosphonates, particularly in a dental biofilm model. The experiments were performed with an oral cavity single-specie (Aggregatibacter actinomycetemcomitans) biofilm assay, which was optimized in this contribution. Risedronate displayed an intrinsic anti-biofilm effect, and all bisphosphonates, except clodronate, reduced biofilm formation when combined with BAG. In particular, the anti-biofilm activity of risedronate was significantly increased by the combination with BAG. Since it has been proposed that some of the antimicrobial effects of BAG are caused by local pH changes, studies of pH variations were performed to gain a mechanistic understanding. However, the observed anti-biofilm effects could not be explained with lowered pHs. Overall, these results do provide further support for the promising use of bisphosphonate-BAG combinations in dental applications. These findings are particularly relevant for patients undergoing cancer chemotherapy, or osteoporotic patients, which are known to be more vulnerable to periodontitis. In such cases, bisphosphonate treatment could play a double positive effect: local treatment of periodontitis (in combination with BAG) and systemic treatment of osteoporosis, prevention of hypercalcemia and metastases

  7. Review and the state of the art: Sol-gel and melt quenched bioactive glasses for tissue engineering.

    Science.gov (United States)

    Kaur, Gurbinder; Pickrell, Gary; Sriranganathan, Nammalwar; Kumar, Vishal; Homa, Daniel

    2016-08-01

    Biomaterial development is currently the most active research area in the field of biomedical engineering. The bioglasses possess immense potential for being the ideal biomaterials due to their high adaptiveness to the biological environment as well as tunable properties. Bioglasses like 45S5 has shown great clinical success over the past 10 years. The bioglasses like 45S5 were prepared using melt-quenching techniques but recently porous bioactive glasses have been derived through sol-gel process. The synthesis route exhibits marked effect on the specific surface area, as well as degradability of the material. This article is an attempt to provide state of the art of the sol-gel and melt quenched bioactive bioglasses for tissue regeneration. Fabrication routes for bioglasses suitable for bone tissue engineering are highlighted and the effect of these fabrication techniques on the porosity, pore-volume, mechanical properties, cytocompatibilty and especially apatite layer formation on the surface of bioglasses is analyzed in detail. Drug delivery capability of bioglasses is addressed shortly along with the bioactivity of mesoporous glasses. © 2015 Wiley Periodicals, Inc. J Biomed Mater Res Part B: Appl Biomater, 104B: 1248-1275, 2016. © 2015 Wiley Periodicals, Inc.

  8. Acid Neutralizing Ability and Shear Bond Strength Using Orthodontic Adhesives Containing Three Different Types of Bioactive Glass

    Science.gov (United States)

    Yang, Song-Yi; Kim, Seong-Hwan; Choi, Se-Young; Kim, Kwang-Mahn

    2016-01-01

    The objective of the study was to compare the acid neutralizing ability and shear bond strength (SBS) of three different types of orthodontic adhesives containing bioactive glasses (BAGs). 45S5, 45S5F and S53P4 BAGs were prepared using the melting technique and ground to fine particles. Orthodontic adhesives containing three types of BAGs were prepared as follows: 52.5% 45S5 BAG + 17.5% glass (45S5_A); 61.25% 45S5 BAG + 8.75% glass (45S5_B); 52.5% 45S5F BAG + 17.5% glass (45S5F_A); 61.25% 45S5F BAG + 8.75% glass (45S5F_B); 52.5% S53P4 BAG + 17.5% glass (S53P4_A); 61.25% S53P4 BAG + 8.75% glass (S53P4_B); and 70.0% glass (BAG_0). To evaluate the acid neutralizing properties, specimens were immersed in lactic acid solution, and pH changes were measured. SBS was measured with a universal testing machine. For all of the BAG-containing adhesives, the one with 61.25% of BAG showed a significantly greater increase of pH than the one with 52.5% of BAG (p 0.05). The adhesive containing 61.25% of 45S5F BAG exhibited clinically acceptable SBS and acid neutralizing properties. Therefore, this composition is a suitable candidate to prevent white spot lesions during orthodontic treatment. PMID:28773250

  9. Acid Neutralizing Ability and Shear Bond Strength Using Orthodontic Adhesives Containing Three Different Types of Bioactive Glass

    Directory of Open Access Journals (Sweden)

    Song-Yi Yang

    2016-02-01

    Full Text Available The objective of the study was to compare the acid neutralizing ability and shear bond strength (SBS of three different types of orthodontic adhesives containing bioactive glasses (BAGs. 45S5, 45S5F and S53P4 BAGs were prepared using the melting technique and ground to fine particles. Orthodontic adhesives containing three types of BAGs were prepared as follows: 52.5% 45S5 BAG + 17.5% glass (45S5_A; 61.25% 45S5 BAG + 8.75% glass (45S5_B; 52.5% 45S5F BAG + 17.5% glass (45S5F_A; 61.25% 45S5F BAG + 8.75% glass (45S5F_B; 52.5% S53P4 BAG + 17.5% glass (S53P4_A; 61.25% S53P4 BAG + 8.75% glass (S53P4_B; and 70.0% glass (BAG_0. To evaluate the acid neutralizing properties, specimens were immersed in lactic acid solution, and pH changes were measured. SBS was measured with a universal testing machine. For all of the BAG-containing adhesives, the one with 61.25% of BAG showed a significantly greater increase of pH than the one with 52.5% of BAG (p < 0.05. Groups with 61.25% of BAG showed lower SBS than samples with 52.5% of BAG. 45S5F_A showed no significant difference of SBS compared to BAG_0 (p > 0.05. The adhesive containing 61.25% of 45S5F BAG exhibited clinically acceptable SBS and acid neutralizing properties. Therefore, this composition is a suitable candidate to prevent white spot lesions during orthodontic treatment.

  10. Osseointegration properties of titanium dental implants modified with a nanostructured coating based on ordered porous silica and bioactive glass nanoparticles

    Energy Technology Data Exchange (ETDEWEB)

    Covarrubias, Cristian, E-mail: ccovarrubias@odontologia.uchile.cl [Laboratory of Nanobiomaterials, Institute for Research in Dental Sciences, Faculty of Dentistry, University of Chile, Santiago (Chile); Mattmann, Matías [Laboratory of Nanobiomaterials, Institute for Research in Dental Sciences, Faculty of Dentistry, University of Chile, Santiago (Chile); Von Marttens, Alfredo [Department of Prosthesis, Faculty of Dentistry, University of Chile, Santiago (Chile); Caviedes, Pablo; Arriagada, Cristián [Laboratory of Cell Therapy, ICBM, Faculty of Medicine, University of Chile (Chile); Valenzuela, Francisco [Laboratory of Nanobiomaterials, Institute for Research in Dental Sciences, Faculty of Dentistry, University of Chile, Santiago (Chile); Rodríguez, Juan Pablo [Laboratory of Cell Biology, INTA, University of Chile, Santiago (Chile); Corral, Camila [Department of Restorative Dentistry, Faculty of Dentistry, University of Chile, Santiago (Chile)

    2016-02-15

    Graphical abstract: - Highlights: • The fabrication of a coating for osseointegration of titanium implant is presented. • The coating consists of nanoporous silica loaded with bioactive glass nanoparticles. • Coating accelerates the in vitro formation of apatite in simulated body fluid. • Coating promotes the osteogenic differentiation of stem cells. • Coating accelerates the formation of bone tissue in the periphery of the implant. - Abstract: The fabrication of a nanoporous silica coating loaded with bioactive glass nanoparticles (nBG/NSC) on titanium dental implant surface and its in vitro and in vivo evaluation is presented. The coating was produced by a combined sol–gel and evaporation induced self-assembly process. In vitro bioactivity was assessed in simulated body fluid (SBF) and investigating the osteogenic differentiation of human bone marrow mesenchymal stem cells (hBMSCs). A rat tibial model was employed to analyze the bone response to nBG/NSC-modified titanium implant surface in vivo. The nBG/NSC coating was confirmed at nano level to be constituted by a highly ordered nanoporous silica structure. The coating nanotopography in conjunction with the bioactivity of the BG particles accelerate the in vitro apatite formation and promote the osteogenic differentiation of hBMSCs in absence of osteogenic supplements. These properties accelerate the formation of bone tissue in the periphery of the implant after 3 weeks of implantation. Backscattered scanning electron microscopy images revealed the presence of gaps and soft tissue in the unmodified implant after 6 weeks, whereas the nBG/NSC-modified implant showed mature bone in intimate contact with the implant surface. The nBG/NSC coating appears promising for accelerating the osseointegration of dental implants.

  11. Photocurable bioactive bone cement based on hydroxyethyl methacrylate-poly(acrylic/maleic) acid resin and mesoporous sol gel-derived bioactive glass

    Energy Technology Data Exchange (ETDEWEB)

    Hesaraki, S., E-mail: S-hesaraki@merc.ac.ir

    2016-06-01

    This paper reports on strong and bioactive bone cement based on ternary bioactive SiO{sub 2}-CaO-P{sub 2}O{sub 5} glass particles and a photocurable resin comprising hydroxyethyl methacrylate (HEMA) and poly(acrylic/maleic) acid. The as-cured composite represented a compressive strength of about 95 MPa but it weakened during soaking in simulated body fluid, SBF, qua its compressive strength reached to about 20 MPa after immersing for 30 days. Biodegradability of the composite was confirmed by reducing its initial weight (~ 32%) as well as decreasing the molecular weight of early cured resin during the soaking procedure. The composite exhibited in vitro calcium phosphate precipitation in the form of nanosized carbonated hydroxyapatite, which indicates its bone bonding ability. Proliferation of calvarium-derived newborn rat osteoblasts seeded on top of the composite was observed during incubation at 37 °C, meanwhile, an adequate cell supporting ability was found. Consequently, it seems that the produced composite is an appropriate alternative for bone defect injuries, because of its good cell responses, high compressive strength and ongoing biodegradability, though more in vivo experiments are essential to confirm this assumption. - Highlights: • Light cure cement based on SiO{sub 2}-CaO-P{sub 2}O{sub 5} glass and polymer-like matrix was formed. • The matrix includes poly(acrylic/maleic acid) and poly(hydroxyethyl methacrylate). • The cement is as strong as polymethylmethacrylate bone cement. • The cement exhibits apatite formation ability in simulated body fluid. • The cement is biodegradable and supports proliferation of osteoblastic cells.

  12. Mechanical properties of bioactive glass (13-93) scaffolds fabricated by robotic deposition for structural bone repair.

    Science.gov (United States)

    Liu, Xin; Rahaman, Mohamed N; Hilmas, Gregory E; Bal, B Sonny

    2013-06-01

    There is a need to develop synthetic scaffolds to repair large defects in load-bearing bones. Bioactive glasses have attractive properties as a scaffold material for bone repair, but data on their mechanical properties are limited. The objective of the present study was to comprehensively evaluate the mechanical properties of strong porous scaffolds of silicate 13-93 bioactive glass fabricated by robocasting. As-fabricated scaffolds with a grid-like microstructure (porosity 47%, filament diameter 330μm, pore width 300μm) were tested in compressive and flexural loading to determine their strength, elastic modulus, Weibull modulus, fatigue resistance, and fracture toughness. Scaffolds were also tested in compression after they were immersed in simulated body fluid (SBF) in vitro or implanted in a rat subcutaneous model in vivo. As fabricated, the scaffolds had a strength of 86±9MPa, elastic modulus of 13±2GPa, and a Weibull modulus of 12 when tested in compression. In flexural loading the strength, elastic modulus, and Weibull modulus were 11±3MPa, 13±2GPa, and 6, respectively. In compression, the as-fabricated scaffolds had a mean fatigue life of ∼10(6) cycles when tested in air at room temperature or in phosphate-buffered saline at 37°C under cyclic stresses of 1-10 or 2-20MPa. The compressive strength of the scaffolds decreased markedly during the first 2weeks of immersion in SBF or implantation in vivo, but more slowly thereafter. The brittle mechanical response of the scaffolds in vitro changed to an elasto-plastic response after implantation for longer than 2-4weeks in vivo. In addition to providing critically needed data for designing bioactive glass scaffolds, the results are promising for the application of these strong porous scaffolds in loaded bone repair. Copyright © 2013 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

  13. A highly bioactive poly (amido amine)/70S30C bioactive glass hybrid with photoluminescent and antimicrobial properties for bone regeneration.

    Science.gov (United States)

    Akbari Dourbash, Fakhraddin; Alizadeh, Parvin; Nazari, Shahram; Farasat, Alireza

    2017-09-01

    The field of tissue engineering constantly calls for novel biomaterials that possess intrinsically multifunctional properties such as bioactivity, bioimaging ability and antibacterial properties. In this paper, poly (amido amine) generation 5/bioactive glass inorganic-organic hybrids have been developed through direct hybridization by 3-glycidoxypropyltrimethoxysilane (GPTMS) as coupling agent. Results indicated that the degree of covalent coupling by GPTMS and the weight percent of inorganic and organic constituents highly influence hybrids properties. It was found that nanoscale integration of inorganic and organic chains by GPTMS significantly endows hybrids with high thermal stability. Furthermore, hybrids exhibited photoluminescent ability (emission 400-600nm and 700nm) without incorporating of any organic dyes or quantum dots. In addition, hydrophilicity of our hybrids indicated good cell/material interaction. The biological apatite was formed on the surface of calcium containing hybrids when soaked in simulated body fluid (SBF) for 1week. Hybrids also showed linear biodegradation behavior in SBF that could be controlled by the degree of covalent crosslinking which was indicative of their stable biodegradation ability. High inherent antibacterial properties against Staphylococcus aureus was also observed from poly (amido amine)/silica hybrids. No adverse cytotoxicity for human gingival fibroblast cell lines (HGF) was detected after 4days. It is envisaged that our novel multifunctional hybrid system will confer intriguing potential in advancing the field of tissue engineering. Copyright © 2017 Elsevier B.V. All rights reserved.

  14. Genotoxicity effects of nano bioactive glass and Novabone bioglass on gingival fibroblasts using single cell gel electrophoresis (comet assay): An in vitro study.

    Science.gov (United States)

    Tavakoli, Mohammad; Bateni, Ensiyeh; Rismanchian, Mansour; Fathi, Mohammadhossein; Doostmohammadi, Ali; Rabiei, Azim; Sadeghi, Hojat; Etebari, Mahmood; Mirian, Mina

    2012-05-01

    The greater surface of bioactive glass nanoparticles presents an incomparable and promising feature similar to the biological apatite. Nanoparticles improve cellular adhesion, enhance osteoblast proliferation and differentiation, and increase biomineralization for periodontal regeneration and dental implants. Considering the fact that interaction between periodontal cells and bone graft materials are important for periodontal lesion regeneration, the present study was undertaken to investigate the genotoxicity of a novel synthesized nanoscale bioactive glass and compared it with Novabone bioglass in periodontal fibroblasts cells, in order to approve the biocompatibility of nano bioactive glass. In this in vitro experimental study, periodontal C165 fibroblasts cells were cultured in their logarithmic phase and the genotoxicity of novel synthesized bioactive glass nanoparticles and Novabone bioglass was studied in different concentrations and a control group using Comet assay test. By using Autocomet software, three parameters (Tail length, %DNA in tail, Tail moment) were analyzed; the genotoxicity of mentioned biomaterials and control group. Obtained data were analyzed by SPSS 11.5 software, Kruskal Wallis H and Mann Whitney tests (P = 0.05). No statistically significant difference was observed between the concentrations of Novabone bioglass (P value = 0.085) with control group and novel nano bioactive glass (P value = 0.437) with control group in the evaluation of %DNA in tail parameter. There was significant difference between genotoxicity of novel nano bioactive glass and control, and between Novabone bioglass and control group in concentrations of 4 and 5 mg/ml. According to significance of the mean difference, novel nano bioactive glass showed higher genotoxicity compared to Novabone bioglass in the concentration of 5 mg/ml (P ≤ 0.05). The findings of this study have demonstrated that novel nano bioactive glass had no genotoxicity in concentrations lower than

  15. Resin bonding using etch-and-rinse and self-etch adhesives to decalcified deciduous enamel after bioactive glass air abrasion.

    Science.gov (United States)

    Eshghi, Alireza; Khoroushi, Maryam; Rezvani, Alireza

    2014-09-01

    Bioactive glass air abrasion is a conservative technique for removal of initial decalcified enamel superficial layer and caries vs alumina air abrasion. This study evaluated shear bond strength of composite resin to sound and decalcified deciduous enamel using etch-and-rinse and self-etch adhesives after alumina and bioactive glass air abrasion. Ninety-six fat enamel surfaces, mounted in acrylic resin, were prepared from 48 deciduous molars. Half of the specimens were decalcified with a demineralizing solution. Both intact and decalcified specimens were assigned to two groups for alumina and bioactive glass air abrasion. In each group, the specimens were subdivided into two groups for application of Clearfil SE Bond or Optibond FL adhesives (n = 12). After composite resin bonding, the specimens underwent shear bond test. Data were analyzed using three-way analysis of variance (ANOVA), linear regression model and independent-sample t-test (α = 0.05). No significant differences were noted in bond strength of composite resin after alumina or bioactive glass air abrasion (p = 0.272). Optibond FL adhesive and enamel decalcification produced higher bond strength (p = 0.000, p = 0.001 respectively). In this study, bioactive glass air abrasion produced bond strength comparable to the conventional method. This technique might be an alternative method for preparation of normal and/or decalcified enamel of deciduous teeth for resin bonding.

  16. 3D nanocomposite chitosan/bioactive glass scaffolds obtained using two different routes: an evaluation of the porous structure and mechanical properties

    Directory of Open Access Journals (Sweden)

    Elke M. F. Lemos

    2016-05-01

    Full Text Available Porous synthetic substrates are developed through tissue engineering technologies to grow new tissue, restoring the function of tissue or an organ. For bone regeneration, these scaffolds must support the dynamic load exerted on this tissue, achieved primarily by increasing their compression strength, as established in the literature. The aim of this paper was to incorporate an inorganic composite bioactive glass (60%SiO2 - 36%CaO - 4%P2O5 as a reinforcing agent in mechanical 3D scaffolds that must remain porous. Two strategies were adopted: a co-precipitation method to obtain a nanoparticulate dispersion of bioactive glass (BGNP and a sol-gel method to combine a bioactive glass solution (BG with a previously prepared chitosan polymer solution. Moreover, a lyophilization process was also used, generating highly porous scaffolds. Various aspects of the scaffold were evaluated, including the morphology, orientation and size of the pores, and mechanical strength, as obtained using the two synthetic methods. The data for compressive strength revealed increased strength after the incorporation of bioactive glass, which was more pronounced when utilizing the nanoscale bioactive glass.

  17. A new sol–gel synthesis of 45S5 bioactive glass using an organic acid as catalyst

    Energy Technology Data Exchange (ETDEWEB)

    Faure, J., E-mail: joel.faure@univ-reims.fr [Université de Reims Champagne-Ardenne, Laboratoire Ingénierie et Sciences des Matériaux, LISM EA 4695, 21 rue Clément ADER, 51685 REIMS Cedex 2 (France); Drevet, R., E-mail: richard.drevet@univ-reims.fr [Université de Reims Champagne-Ardenne, Laboratoire Ingénierie et Sciences des Matériaux, LISM EA 4695, 21 rue Clément ADER, 51685 REIMS Cedex 2 (France); Lemelle, A.; Ben Jaber, N.; Tara, A. [Université de Reims Champagne-Ardenne, Laboratoire Ingénierie et Sciences des Matériaux, LISM EA 4695, 21 rue Clément ADER, 51685 REIMS Cedex 2 (France); El Btaouri, H. [Université de Reims Champagne-Ardenne UMR CNRS MEDyC, EA 7369, Campus Moulin de la Housse, 51687 REIMS Cedex 2 (France); Benhayoune, H. [Université de Reims Champagne-Ardenne, Laboratoire Ingénierie et Sciences des Matériaux, LISM EA 4695, 21 rue Clément ADER, 51685 REIMS Cedex 2 (France)

    2015-02-01

    In this paper a new sol–gel approach was explored for the synthesis of the 45S5 bioactive glass. We demonstrate that citric acid can be used instead of the usual nitric acid to catalyze the sol–gel reactions. The substitution of nitric acid by citric acid allows to reduce strongly the concentration of the acid solution necessary to catalyze the hydrolysis of silicon and phosphorus alkoxides. Two sol–gel powders with chemical compositions very close to that of the 45S5 were obtained by using either a 2 M nitric acid solution or either a 5 mM citric acid solution. These powders were characterized and compared to the commercial Bioglass®. The surface properties of the two bioglass powders were assessed by scanning electron microscopy (SEM) and by Brunauer–Emmett–Teller method (BET). The Fourier transformed infrared spectroscopy (FTIR) and the X-ray diffraction (XRD) revealed a partial crystallization associated to the formation of crystalline phases on the two sol–gel powders. The in vitro bioactivity was then studied at the key times during the first hours of immersion into acellular Simulated Body Fluid (SBF). After 4 h immersion into SBF we clearly demonstrate that the bioactivity level of the two sol–gel powders is similar and much higher than that of the commercial Bioglass®. This bioactivity improvement is associated to the increase of the porosity and the specific surface area of the powders synthesized by the sol–gel process. Moreover, the nitric acid is efficiently substituted by the citric acid to catalyze the sol–gel reactions without alteration of the bioactivity of the 45S5 bioactive glass. - Highlights: • Citric acid is employed as a catalyzer of the sol–gel process. • This catalyzer is used at a very low concentration for the hydrolysis reaction. • The chemical composition of the bioglass synthesized by the sol–gel process is optimized. • The properties of two sol–gel bioglasses are compared with those of the commercial

  18. [Effects of bioactive glass and extracted dentin proteins on human dental pulp cells].

    Science.gov (United States)

    Xin, Y; Wang, S N; Cui, C Y; Dong, Y M

    2017-04-18

    To investigate the proliferation, odontogenic differentiation and mineralization of human dental pulp cells (HDPCs) on bioactive glass(BG) and extracted dentin proteins(EDP). Primary HDPCs were isolated from third molars by enzyme digestion and were cultured in Dulbecco's minimum essential medium (DMEM). Then the 4th generation of HDPCs was cultured with DMEM, which contained BG-EDP, BG, and EDP, respectively. Meanwhile HDPCs were cultured in DMEM as control group. Proliferation of HDPCs was evaluated by 3-(4,5-dimethyl-2-thiazolyl)-2,5-diphenyl-2-H-tetrazolium bromide (MTT) colorimetric assay. Odontogenic differentiation was determined by alkaline phosphatase (ALP) activity assay and real-time PCR. Mineralization was investigated by Alizarin red staining and cetylpyridinium chloride (CPC) assay. The proliferation of HDPCs was increased significantly in BG-EDP group on 3,7,and 9 d (optical density value: 1.36±0.06, 2.52±0.20, 2.72±0.29) compared with BG (optical density value: 1.20±0.26, 2.33±0.26, 2.50±0.30), EDP(optical density value: 1.13±0.15, 2.10±0.13, 2.38±0.22) and control group (optical density value: 0.84±0.17, 1.84±0.18, 1.95±0.19), PEDP group had no statistical difference compared with EDP group and control group; the expression of odontogenic differentiation genes (DSPP, DMP-1) showed no difference among all the groups(P>0.05). After 14 days, ALP activity of BG-EDP group (56.67±1.83) was significantly upregulated compared with EDP group (41.98±9.71) and control group (30.82±6.70), P0.05; DSPP gene expression was upregulated significantly in BG-EDP group (5.79±1.94) compared with the other groups (PEDP group (3.87±1.87) increased but had no statistical difference compared with the other groups (P>0.05). The alizarin red staining showed more mineral nodules in BG-EDP group, the cetylpyridinium chloride semi-quantification presented higher calcification in BG-EDP group (0.27±0.01) compared with the other groups (PEDP, BG

  19. Understanding the composition-structure-bioactivity relationships in diopside (CaO·MgO·2SiO₂)-tricalcium phosphate (3CaO·P₂O₅) glass system.

    Science.gov (United States)

    Kapoor, Saurabh; Semitela, Ângela; Goel, Ashutosh; Xiang, Ye; Du, Jincheng; Lourenço, Ana H; Sousa, Daniela M; Granja, Pedro L; Ferreira, José M F

    2015-03-01

    The present work is an amalgamation of computation and experimental approach to gain an insight into composition-structure-bioactivity relationships of alkali-free bioactive glasses in the CaO-MgO-SiO2-P2O5 system. The glasses have been designed in the diopside (CaO·MgO·2SiO2; Di)-tricalcium phosphate (3CaO·P2O5; TCP) binary join by varying the Di/TCP ratio. The melt-quenched glasses have been investigated for their structure by molecular dynamic (MD) simulations as well as by nuclear magnetic resonance spectroscopy (NMR). In all the investigated glasses silicate and phosphate components are dominated by Q(2) (Si) and Q(0) (P) species, respectively. The apatite forming ability of the glasses was investigated using X-ray diffraction (XRD), infrared spectroscopy after immersion of glass powders in simulated body fluid (SBF) for time durations varying between 1 h and 14 days, while their chemical degradation has been studied in Tris-HCl in accordance with ISO 10993-14. All the investigated glasses showed good bioactivity without any substantial variation. A significant statistical increase in metabolic activity of human mesenchymal stem cells (hMSCs) when compared to the control was observed for Di-60 and Di-70 glass compositions under both basal and osteogenic conditions. Copyright © 2015 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

  20. Bioactivity of ferrimagnetic glass-ceramics in the system FeO-Fe2O3-CaO-SiO2.

    Science.gov (United States)

    Ebisawa, Y; Miyaji, F; Kokubo, T; Ohura, K; Nakamura, T

    1997-10-01

    Bioactive and ferrimagnetic glass-ceramics are useful as thermoseeds for hyperthermia treatment of cancer. A heat treatment of a 40(FeO, Fe2O3)-60CaO x SiO2 wt% glass gives a ferrimagnetic glass-ceramic containing 36 wt% magnetite in a CaO x SiO2 matrix. However, it does not show bioactivity since a small amount of iron ion remains in the matrix. In the present study, bioactivities of ferrimagnetic glass-ceramics which were prepared by heat treatment of glasses of the composition 40(FeO, Fe2O3)-60CaO x SiO2 (wt%) with various components added at 100:3 weight ratio were evaluated in vitro by examining bone-like apatite formation on their surfaces in a simulated body fluid. It was found that glass-ceramics with Na2O or B2O3 added in combination with P2O5 show bioactivity.

  1. EFFECT OF DIFFERENT CaO/MgO RATIOS ON THE STRUCTURAL AND MECHANICAL PROPERTIES OF BIOACTIVE GLASS-CERAMICS

    Directory of Open Access Journals (Sweden)

    M. U. Hashmi

    2012-12-01

    Full Text Available The aim of present work is to study the relationship between crystalline phases, microstructure and mechanical properties of bioactive glass-ceramics. For this purpose, glasses of composition (50-x CaO–34SiO2–14.5P2O5–1CaF2–0.5MgF2– xMgO (wt. % (where x = 4, 25 and 46 respectively were synthesized by conventional melt-quench method. Each glass was sintered according to the endothermal and exothermal peaks of differential scanning calorimetric (DSC data to form three glass ceramics termed G1, G2 and G3 respectively. X-ray diffraction (XRD revealed crystalline phases of hydroxyapatite and wollastonite in G1 and G2, whereas in G3, a new phase ‘whitlockite’ was observed probably due to a greater concentration of MgO in this sample. Bulk density of the samples was determined by Archimedes principle. Scanning electron microscope (SEM data illustrated that the rate of densification of materials increased with the decrease of CaO/MgO ratio. Analysis of mechanical properties revealed that micro-hardness and bending strength of the samples increased with the increase in MgO content, which is in accordance with the results of XRD, SEM and bulk density.

  2. Synthesis, characterization and bioactivity of a calcium-phosphate glass-ceramics obtained by the sol-gel processing method.

    Science.gov (United States)

    Jmal, Nouha; Bouaziz, Jamel

    2017-02-01

    In this work, a calcium-phosphate glass-ceramics was successfully obtained by heat treatment of a mixture of 26.52 in wt.% of fluorapatite (Fap) and 73.48 in wt.% of 77S (77 SiO214 CaO9 P2O5 in wt.%) gel. The calcium phosphate-glass-ceramics was prepared by sol-gel process with tetraethyl orthosilicate (TEOS), triethyl phosphate (TEP), calcium nitrate and fluorapatite. The synthesized powders were characterized by some commonly used tools such as X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR), 31P magic angle spinning nuclear magnetic resonance (MAS-NMR), scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS), and thin-film X-ray diffraction (TF-XRD). The obtained results seemed to confirm the nucleation and growth of hydroxyapatite (Hap) nano-phase in the glass. Moreover, an in-vitro evaluation of the glass-ceramic was performed. In addition, to assess its bioactive capacity, it was soaked in simulated body fluid (SBF) at different time intervals. The SEM, EDS and TF-XRD analyses showed the deposition of hydroxyapatite on the surface of the specimens after three days of immersion in SBF solution. The mechanical properties of the obtained material such as rupture strength, Vickers hardness and elastic modulus were measured. In addition, the friction coefficient of calcium phosphate-glass-ceramics was tested. The values of the composite of rupture strength (24MPa), Vickers hardness (214Hv), Young's modulus (52.3GPa), shear modulus (19GPa) and friction coefficient (0.327) were obtained. This glass-ceramics can have useful applications in dental prostheses. Indeed, this material may have promising applications for implants because of its content of fluorine, the effective protector against dental caries. Copyright © 2016 Elsevier B.V. All rights reserved.

  3. Evaluation of optical density of bone defects filled with calcium phosphate cement and bioactive glass in rats.

    Science.gov (United States)

    Biancon Filho, Luiz Alberto; Primo, Bruno Tochetto; Gassen, Humberto Thomazi; Fontanella, Vânia Regina Camargo; Silva, Aurelício Novaes

    2011-02-01

    To evaluate new bone formation, by the analysis of optical density, in rat femoral defects filled with calcium phosphate cement (CPC) and bioactive glass (BG). Twenty-one rats were divided into three groups, Group I (CPC), Group II (BG), and Group III (control), and assessed after 7, 15, and 30 days. Three bone cavities were made in the left femur and filled with CPC, BG, and no material (control). Digital images were obtained and the results were subjected to statistical analysis of variance (ANOVA), complemented by the Friedman and Kruskal-Wallis nonparametric tests, with a significance level of 5%. Regarding optical density, Group I showed statistical values significantly higher than Group III and also higher, although not statistically significant, than Group II, in all observation periods. When Groups II and III were compared, Group II showed higher optical density values, without statistically significant differences, in all periods. The biomaterials analyzed showed higher optical density in relation to the control group in all observation periods, calcium phosphate cement being the best option in the repair of bone defects, but without statistically significant differences in relation to bioactive glass.

  4. An Amperometric Acetylcholinesterase Sensor Based on the Bio-templated Synthesis of Hierarchical Mesoporous Bioactive Glass Microspheres

    Science.gov (United States)

    Lv, Zhuo; Luo, Ruiping; Xi, Lijuan; Chen, Yang; Wang, Hongsu

    2017-11-01

    This work describes the synthesis of three-dimensional hollow hierarchical mesoporous bioactive glass (HMBG) microspheres based on Herba leonuri pollen grains via a hydrothermal method. The HMBG microspheres perfectly copied the hierarchical porous structure and inner hollow structure constituting the double-layer surface of the natural Herba leonuri pollen grains. This structural mimicry of the pollen grains resulted in a higher degree of adsorption of acetylcholinesterase (AChE) on HMBG microspheres in comparison with mesoporous bioactive glass. Subsequently, an amperometric biosensor for the detection of Malathion was fabricated by immobilizing AChE onto an HMBG microspheres-modified carbon paste electrode. The biosensor response exhibited two good linear ranges during an incubation time of 10 min in the malathion concentration ranges of 0.02-50 ppb and 50-600 ppb, with a detection limit of 0.0135 ppb ( S/ N = 3). Overall, the prepared enzymatic biosensor showed high sensitivity in the rapid detection of Malathion and could be applied to detect pesticide residues in vegetable matter.

  5. Nano-sized 58S bioactive glass enhances proliferation and osteogenic genes expression of osteoblast-like cells.

    Science.gov (United States)

    Gong, Wei Yu; Dong, Yan Mei; Chen, Xiao Feng; Karabucak, Bekir

    2012-01-01

    To observe the effects of ionic dissolution products on nano-sized 58S bioactive glass (nano-58S) on proliferation and specific osteogenic genes expression in MG-63 cells. Ionic dissolution products were prepared by incubating nano-58S or sol-gel bioactive glass 58S (58S) particulates in Dulbecco's modified Eagle's medium (DMEM) at 1% w/v for 24 hr and filtrated through 0.22 µm filters to remove the particulates. MG-63 cells were cultured in the nano-58S extraction, 58S extraction, and DMEM, respectively, for different time periods to assay the proliferation, mRNA expression of alkaline phosphatase (ALP), Cbfa1, Collagen type I (Col-I) and osteocalcin (OCN), as well as ALP staining, activity and matrix mineralisation. In the nano-58S group, cell proliferation and mRNA expression of ALP, Cbfa1 and OCN were significantly enhanced in a time-dependent manner compared with the control group. mRNA expression of Cbfa1 on day 4 and OCN on day 7 was significantly higher than that in the 58S group. Moreover, there was significantly more ALP protein expression and mineralisation in the nano-58S group than in the 58S group. The nano-58S enhanced proliferation, osteogenic markers expression in MG-63 cells and induced stronger mineralization than 58S.

  6. Cutaneous and Labyrinthine Tolerance of Bioactive Glass S53P4 in Mastoid and Epitympanic Obliteration Surgery: Prospective Clinical Study

    Directory of Open Access Journals (Sweden)

    Daniele Bernardeschi

    2015-01-01

    Full Text Available Objective. To evaluate the cutaneous and the inner ear tolerance of bioactive glass S53P4 when used in the mastoid and epitympanic obliteration for chronic otitis surgery. Material and Methods. Forty-one cases have been included in this prospective study. Cutaneous tolerance was clinically evaluated 1 week, 1 month, and 3 months after surgery with a physical examination of the retroauricular and external auditory canal (EAC skin and the presence of otalgia; the inner ear tolerance was assessed by bone-conduction hearing threshold 1 day after surgery and by the presence of vertigo or imbalance. Results. All surgeries but 1 were uneventful: all patients maintained the preoperative bone-conduction hearing threshold except for one case in which the round window membrane was opened during the dissection of the cholesteatoma in the hypotympanum and this led to a dead ear. No dizziness or vertigo was reported. Three months after surgery, healing was achieved in all cases with a healthy painless skin. No cases of revision surgery for removal of the granules occurred in this study. Conclusion. The bioactive glass S53P4 is a well-tolerated biomaterial for primary or revision chronic otitis surgery, as shown by the local skin reaction which lasted less than 3 months and by the absence of labyrinthine complications.

  7. Synthesis of copper-containing bioactive glass nanoparticles using a modified Stöber method for biomedical applications.

    Science.gov (United States)

    Zheng, Kai; Dai, Xinyi; Lu, Miao; Hüser, Norbert; Taccardi, Nicola; Boccaccini, Aldo R

    2017-02-01

    Copper (Cu)-containing bioactive glasses (BGs) are attracting attention for bone regeneration and wound healing since they have bone-bonding capability and potential osteogenesis and angiogenesis properties. In this study, highly dispersed and spherical Cu-containing bioactive glass nanoparticles (Cu-BGNs) were successfully synthesized via a modified Stöber method. The content of incorporated Cu in the particles could be tailored by adjusting the amount of the added Cu precursor, a procedure that had no significant effects on the morphological and structural characteristics of the nanoparticles. Cu-BGNs exhibited satisfactory apatite-forming ability, as a large quantity of apatite could form on Cu-BGNs pellets after immersion in simulated body fluid for just 3days. The incorporation of Cu exhibited positive effects on the apatite formation. In addition, both Si and Cu ions were released from the Cu-BGN in a sustained manner for at least 14days in cell culture medium, indicating the potential of the BGN as promising carriers for delivering therapeutic Cu ions. Moreover, Cu-BGNs showed no significant cytotoxicity towards human mesenchymal stem cells and fibroblast cells at concentrations of 100, 10 and 1μg/mL. Taken together, the results suggest that Cu-BGNs are promising nanoparticulate fillers to develop nanocomposites for biomedical applications especially in bone regeneration and wound healing. Copyright © 2016 Elsevier B.V. All rights reserved.

  8. Evaluation of La-Doped Mesoporous Bioactive Glass as Adsorbent and Photocatalyst for Removal of Methylene Blue from Aqueous Solution

    Directory of Open Access Journals (Sweden)

    Liying Li

    2015-01-01

    Full Text Available A series of La-doped mesoporous bioactive glass (BG-La materials with excellent biosafety and hypotoxicity have been prepared and tested as adsorbent. The study was aimed to evaluate the possibility of utilizing BG-La for the adsorptive removal of methylene blue (MB from aqueous solution and test the adsorption and desorption behavior of this new material. The process parameters affecting adsorption behaviors such as pH, contact time, and initial concentration and the photocatalytic degradation of MB were systematically investigated. The result showed that BG-La had excellent removal rate (R of MB, and BG-La showed better photocatalytic effect than undoped mesoporous bioactive glass (BG. Furthermore, the MB loaded BG-La was easily desorbed with acid solution due to its electronegativity and mesoporous structure. The result indicated that these materials can be employed as candidates for removal of dye pollutant owing to their high removal rate, excellent photocatalytic effect, desorption performance, and their reusability.

  9. Mechanical Behavior of Nanostructured Hybrids Based on Poly(Vinyl Alcohol/Bioactive Glass Reinforced with Functionalized Carbon Nanotubes

    Directory of Open Access Journals (Sweden)

    H. S. Mansur

    2012-01-01

    Full Text Available This study reports the synthesis and characterization of novel tridimensional porous hybrids based on PVA combined with bioactive glass and reinforced by chemically functionalized carbon nanotubes (CNT for potential use in bone tissue engineering. The functionalization of CNT was performed by introducing carboxylic groups in multiwall nanotubes. This process aimed at enhancing the affinity of CNTs with the water-soluble PVA polymer derived by the hydrogen bonds formed among alcohol (PVA and carboxylic groups (CNT–COOH. In the sequence, the CNT–COOH (0.25 wt% were used as the nanostructure modifier for the hybrid system based on PVA associated with the bioactive glass (BaG. The mechanical properties of the nanostructured hybrids reinforced with CNT–COOH were evaluated by axial compression tests, and they were compared to reference hybrid. The averaged yield stresses of macroporous hybrids were (2.3 ± 0.9 and (4.4 ± 1.0 MPa for the reference and the CNT reinforced materials, respectively. Moreover, yield strain and Young's modulus were significantly enhanced by about 30% for the CNT–COOH hybrids. Hence, as far as the mechanical properties are concerned, the results have clearly showed the feasibility of utilizing these new hybrids reinforced with functionalized CNT in repairing cancellous bone tissues.

  10. Development of injectable biocomposites from hyaluronic acid and bioactive glass nano-particles obtained from different sol-gel routes.

    Science.gov (United States)

    Sohrabi, Mehri; Hesaraki, Saeed; Kazemzadeh, Asghar; Alizadeh, Masoud

    2013-10-01

    Bioactive glass nano-powders with the same chemical composition and different particle characteristics were synthesized by acid-catalyzed (the glass is called BG1) and acid-base catalyzed (BG2) sol-gel processes. Morphological characteristics of powders were determined by TEM and BET methods. The powders were separately mixed with 3% hyaluronic acid solution to form a paste. In vitro reactivity of pastes was determined by soaking them in simulated body fluid. Rheological behaviors of paste in both rotation and oscillation modes were also measured. The results showed that BG1 particles was microporous with mean pore diameter of 1.6 nm and particle size of ~300 nm while BG2 was mesoporous with average pore diameter of 8 and 17 nm and particle size of 20-30 nm. The paste made of BG2 revealed better washout resistance and in vitro apatite formation ability than BG1. According to the rheological evaluations, both pastes exhibited shear thinning but non-thixotropic behavior, meanwhile paste of BG2 had higher viscosity than BG1. The oscillatory tests revealed that the pastes were viscoelastic materials with more viscous nature. Both pastes could be completely injected through standard syringe using low compressive load of 5-50 N. Overall, The biocomposites can potentially be used as bioactive paste for the treatment of hard and even soft tissues. Copyright © 2013 Elsevier B.V. All rights reserved.

  11. Osseointegration properties of titanium dental implants modified with a nanostructured coating based on ordered porous silica and bioactive glass nanoparticles

    Science.gov (United States)

    Covarrubias, Cristian; Mattmann, Matías; Von Marttens, Alfredo; Caviedes, Pablo; Arriagada, Cristián; Valenzuela, Francisco; Rodríguez, Juan Pablo; Corral, Camila

    2016-02-01

    The fabrication of a nanoporous silica coating loaded with bioactive glass nanoparticles (nBG/NSC) on titanium dental implant surface and its in vitro and in vivo evaluation is presented. The coating was produced by a combined sol-gel and evaporation induced self-assembly process. In vitro bioactivity was assessed in simulated body fluid (SBF) and investigating the osteogenic differentiation of human bone marrow mesenchymal stem cells (hBMSCs). A rat tibial model was employed to analyze the bone response to nBG/NSC-modified titanium implant surface in vivo. The nBG/NSC coating was confirmed at nano level to be constituted by a highly ordered nanoporous silica structure. The coating nanotopography in conjunction with the bioactivity of the BG particles accelerate the in vitro apatite formation and promote the osteogenic differentiation of hBMSCs in absence of osteogenic supplements. These properties accelerate the formation of bone tissue in the periphery of the implant after 3 weeks of implantation. Backscattered scanning electron microscopy images revealed the presence of gaps and soft tissue in the unmodified implant after 6 weeks, whereas the nBG/NSC-modified implant showed mature bone in intimate contact with the implant surface. The nBG/NSC coating appears promising for accelerating the osseointegration of dental implants.

  12. Bioactive glass 45S5 powders: effect of synthesis route and resultant surface chemistry and crystallinity on protein adsorption from human plasma.

    Science.gov (United States)

    Bahniuk, Markian S; Pirayesh, Hamidreza; Singh, Harsh D; Nychka, John A; Unsworth, Larry D

    2012-12-01

    Despite its medical applications, the mechanisms responsible for the osseointegration of bioactive glass (45S5) have yet to be fully understood. Evidence suggests that the strongest predictor for osseointegration of bioactive glasses, and ceramics, with bone tissue as the formation of an apatitic calcium phosphate layer atop the implanted material, with osteoblasts being the main mediator for new bone formation. Most have tried to understand the formation of this apatitic calcium phosphate layer, and other bioresponses between the host and bioactive glass 45S5 using Simulated Body Fluid; a solution containing ion concentrations similar to that found in human plasma without the presence of proteins. However, it is likely that cell attachment is probably largely mediated via the adsorbed protein layer. Plasma protein adsorption at the tissue bioactive glass interface has been largely overlooked. Herein, we compare crystalline and amorphous bioactive glass 45S5, in both melt-derived as well as sol-gel forms. Thus, allowing for a detailed understanding of both the role of crystallinity and powder morphology on surface ions, and plasma protein adsorption. It was found that sol-gel 45S5 powders, regardless of crystallinity, adsorbed 3-5 times as much protein as the crystalline melt-derived counterpart, as well as a greater variety of plasma proteins. The devitrification of melt-cast 45S5 resulted in only small differences in the amount and variety of the adsorbed proteome. Surface properties, and not material crystallinity, play a role in directing protein adsorption phenomena for bioactive glasses given the differences found between crystalline melt-cast 45S5 and sol-gel derived 45S5.

  13. Nanogel-based scaffolds fabricated for bone regeneration with mesoporous bioactive glass and strontium: In vitro and in vivo characterization.

    Science.gov (United States)

    Zhang, Qiao; Chen, Xiaohui; Geng, Shinan; Wei, Lingfei; Miron, Richard J; Zhao, Yanbing; Zhang, Yufeng

    2017-04-01

    The delivery of novel bioactive scaffolds for the repair of bone defects remains a prominent challenge worldwide. Currently osteoporosis, a disease caused by low bone mineral density affects over 200 million people worldwide with up to half of this population experiencing at least one fracture within their lifetime. Recently temperature-sensitive p(N-isopropylacrylamide-co-butyl methylacrylate) nanogel (PIB nanogel) scaffolds have emerged as biomaterial candidate for regenerative therapies. It has the advantage of being injected from syringes as a soluble gel form (capable of delivering growth and/or living progenitor cells) yet hardens once it reaches body temperatures. Although this material demonstrates optimal clinical delivery of scaffolds, its main drawback is its low osteoconductivity and bioactivity. Recently we have demonstrated that mesoporous bioactive glass (MBG) loaded with strontium was able to regenerate osteoporotic defects in vivo and enhance osteoblast differentiation in vitro. The aim of this study was to combine the advantages of these two therapies and prepare PIB-nanogel scaffolds containing Sr-MBG and investigate their ability to regenerate femur defects created in ovarectamized rats. The results demonstrate that groups containing Sr-MBG within the nanogel formulation had significantly higher new bone formation when compared with other modalities. We further demonstrate that although nanogel demonstrated poor osteogenic ability, the addition of osteoblasts worked synergistically with Sr-MBG particles to enhance the regeneration of the created femur defects in osteoporotic animals. In conclusion, PIB nanogel scaffolds are a viable treatment modality for bone tissue engineering and may serve as a carrier-scaffold for osteogenic cells and/or bioactive scaffolds such as Sr-MBG. © 2017 Wiley Periodicals, Inc. J Biomed Mater Res Part A: 105A: 1175-1183, 2017. © 2017 Wiley Periodicals, Inc.

  14. Porous and strong bioactive glass (13–93) scaffolds prepared by unidirectional freezing of camphene-based suspensions

    Science.gov (United States)

    Liu, Xin; Rahaman, Mohamed N.; Fu, Qiang; Tomsia, Antoni P.

    2011-01-01

    Scaffolds of 13–93 bioactive glass (6Na2O, 12K2O, 5MgO, 20CaO, 4P2O5, 53SiO2; wt %) with an oriented pore architecture were formed by unidirectional freezing of camphene-based suspensions, followed by thermal annealing of the frozen constructs to grow the camphene crystals. After sublimation of the camphene, the constructs were sintered (1 h at 700 °C) to produce a dense glass phase with oriented macropores. The objective of this work was to study how constant freezing rates (1–7 °C/min) during the freezing step influenced the pore orientation and mechanical response of the scaffolds. When compared to scaffolds prepared by freezing the suspensions on a substrate kept at a constant temperature of 3 °C (time-dependent freezing rate), higher freezing rates resulted in better pore orientation, a more homogeneous microstructure, and a marked improvement in the mechanical response of the scaffolds in compression. Scaffolds fabricated using a constant freezing rate of 7 °C/min (porosity = 50 ± 4%; average pore diameter = 100 μm), had a compressive strength of 47 ± 5 MPa and an elastic modulus of 11 ± 3 GPa (in the orientation direction). In comparison, scaffolds prepared by freezing on the constant-temperature substrate had strength and modulus values of 35 ± 11 MPa and 8 ± 3 GPa, respectively. These oriented bioactive glass scaffolds prepared by the constant freezing rate route could potentially be used for the repair of defects in load-bearing bones, such as segmental defects in the long bones. PMID:21855661

  15. In vitro performance of 13-93 bioactive glass fiber and trabecular scaffolds with MLO-A5 osteogenic cells.

    Science.gov (United States)

    Modglin, Vernon C; Brown, Roger F; Fu, Qiang; Rahaman, Mohamed N; Jung, Steven B; Day, Delbert E

    2012-10-01

    This in vitro study was performed to evaluate the ability of two types of porous bioactive glass scaffolds to support the growth and differentiation of an established osteogenic cell line. The two scaffold types tested included 13-93 glass fiber and trabecular-like scaffolds seeded with murine MLO-A5 cells and cultured for intervals of 2 to 12 days. Culture in MTT-containing medium showed metabolically active cells both on the surface and within the interior of the scaffolds. Scanning electron microscopy revealed well-attached cells on both types of scaffolds with a continual increase in cell density over a 6-day period. Protein measurements also showed a linear increase in cell density during the incubation. Activity of alkaline phosphatase, a key indicator of osteoblast differentiation, increased about 10-fold during the 6-day incubation with both scaffold types. The addition of mineralization media to MLO-A5 seeded scaffolds triggered extensive formation of alizarin red-positive mineralized extracellular material, additional evidence of cell differentiation and completion of the final step of bone formation on the constructs. Collectively, the results indicate that the 13-93 glass fiber and trabecular scaffolds promote the attachment, growth, and differentiation of MLO-A5 osteogenic cells and could potentially be used for bone tissue engineering applications. Copyright © 2012 Wiley Periodicals, Inc.

  16. Sol-gel-derived bioactive glass nanoparticle-incorporated glass ionomer cement with or without chitosan for enhanced mechanical and biomineralization properties.

    Science.gov (United States)

    Kim, Dong-Ae; Lee, Jung-Hwan; Jun, Soo-Kyung; Kim, Hae-Won; Eltohamy, Mohamed; Lee, Hae-Hyoung

    2017-07-01

    This study investigated the mechanical and in vitro biological properties (in immortalized human dental pulp stem cells (ihDPSCs)) of bioactive glass nanoparticle (BGN)-incorporated glass ionomer cement (GIC) with or without chitosan as a binder. After the BGNs were synthesized and characterized, three experimental GICs and a control (conventional GIC) that differed in the additive incorporated into a commercial GIC liquid (Hy-bond, Shofu, Japan) were produced: BG5 (5wt% of BGNs), CL0.5 (0.5wt% of chitosan), and BG5+CL0.5 (5wt% of BGNs and 0.5wt% of chitosan). After the net setting time was determined, weight change and bioactivity were analyzed in simulated body fluid (SBF) at 37°C. Mechanical properties (compressive strength, diametral tensile strength, flexural strength and modulus) were measured according to the incubation time (up to 28 days) in SBF. Cytotoxicity (1day) and biomineralization (14 days), assessed by alizarin red staining, were investigated using an extract from GIC and ihDPSCs. Data were analyzed using one-way analysis of variance (ANOVA) followed by Tukey's post hoc test; pmechanical properties were increased in the BGN-incorporated GICs compared to those in the control (pmechanical properties such as compressive, diametral tensile and flexural strength as well as in vitro biomineralization properties in ihDPSCs without cytotoxicity. Therefore, the developed BGN-incorporated GIC is a promising restorative dental material, although further in vivo investigation is needed before clinical application. Copyright © 2017 The Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

  17. Proliferation, differentiation and gene expression of osteoblasts in boron-containing associated with dexamethasone deliver from mesoporous bioactive glass scaffolds.

    Science.gov (United States)

    Wu, Chengtie; Miron, Richard; Sculean, Anton; Kaskel, Stefan; Doert, Thomas; Schulze, Renate; Zhang, Yufeng

    2011-10-01

    Boron is one of the trace elements in the human body which plays an important role in bone growth. Porous mesopore bioactive glass (MBG) scaffolds are proposed as potential bone regeneration materials due to their excellent bioactivity and drug-delivery ability. The aims of the present study were to develop boron-containing MBG (B-MBG) scaffolds by sol-gel method and to evaluate the effect of boron on the physiochemistry of B-MBG scaffolds and the response of osteoblasts to these scaffolds. Furthermore, the effect of dexamethasone (DEX) delivery in B-MBG scaffold system was investigated on the proliferation, differentiation and bone-related gene expression of osteoblasts. The composition, microstructure and mesopore properties (specific surface area, nano-pore volume and nano-pore distribution) of B-MBG scaffolds have been characterized. The effect of boron contents and large-pore porosity on the loading and release of DEX in B-MBG scaffolds were also investigated. The results have shown that the incorporation of boron into MBG scaffolds slightly decreases the specific surface area and pore volume, but maintains well-ordered mesopore structure and high surface area and nano-pore volume compared to non-mesopore bioactive glass. Boron contents in MBG scaffolds did not influence the nano-pore size distribution or the loading and release of DEX. B-MBG scaffolds have the ability to maintain a sustained release of DEX in a long-term span. Incorporating boron into MBG glass scaffolds led to a controllable release of boron ions and significantly improved the proliferation and bone-related gene expression (Col I and Runx2) of osteoblasts. Furthermore, the sustained release of DEX from B-MBG scaffolds significantly enhanced alkaline phosphatase (ALP) activity and gene expressions (Col I, Runx2, ALP and BSP) of osteoblasts. These results suggest that boron plays an important role in enhancing osteoblast proliferation in B-MBG scaffold system and DEX-loaded B-MBG scaffolds

  18. Preparation of copper-containing bioactive glass/eggshell membrane nanocomposites for improving angiogenesis, antibacterial activity and wound healing.

    Science.gov (United States)

    Li, Jinyan; Zhai, Dong; Lv, Fang; Yu, Qingqing; Ma, Hongshi; Yin, Jinbo; Yi, Zhengfang; Liu, Mingyao; Chang, Jiang; Wu, Chengtie

    2016-05-01

    Effectively stimulating angiogenesis and avoiding wound infection are great challenges in wound care management. Designing new healing dressings with requisite angiogenic capacity and antibacterial performance is of particular significance. In order to achieve this aim, we prepared a copper (Cu)-containing bioactive glass nanocoating (40-50nm) with uniform nanostructure on natural eggshell membrane (Cu-BG/ESM) by the pulsed laser deposition (PLD) technique. The surface physicochemical properties including hydrophilicity and hardness of ESM were significantly improved after depositing Cu-BG nanocoatings. Meanwhile, 5Cu-BG/ESM films containing 5mol% Cu stimulated proangiogenesis by improving vascular endothelial growth factor (VEGF) and hypoxia-inducible factor (HIF)-1α protein secretion as well as angiogenesis-related gene expression (VEGF, HIF-1α, VEGF receptor 2 (KDR) and endothelial nitric oxide (eNos)) of human umbilical vein endothelial cells (HUVECs). When used to treat full-thickness skin defects in mice, 5Cu-BG/ESM films enhanced the healing quality as confirmed by the significantly improved angiogenesis (as indicated by CD31 expression) and formation of continuous and uniform epidermis layer in vivo. Furthermore, 5Cu-BG/ESM films could maintain a sustained release of Cu(2+) ions and distinctly inhibited the viability of bacteria (Escherichia coli). The results indicate that Cu(2+) ions released from Cu-BG/ESM nanocomposite films play an important role for improving both angiogenesis and antibacterial activity and the prepared nanocomposite films combined Cu-containing BG nanocoatings with ESM are a promising biomaterial for wound healing application. Designing new healing dressings with requisite angiogenic capacity and antibacterial performance is of particular significance in wound care management. In our study, we successfully prepared copper-containing bioactive glass/eggshell membrane (Cu-BG/ESM) nanocomposites with uniform bioactive glass

  19. [Scintigraphic detection of osteoblast activity after implantation of BAS-0 bioactive glass-ceramic material into long bone defects].

    Science.gov (United States)

    Sponer, P; Urban, K; Urbanová, E

    2006-06-01

    The aim of the study was to demonstrate, by three-phase bone scintigraphy, radionuclide uptake at the site of defects in long bones filled with the non-resorbable bioactive glass-ceramic material BAS-0 at a long follow-up. Twenty patients, 14 men and 6 women, operated on between 1990 and 2000 for benign bone tumors or tumor-like lesions localized in the femur, tibia or humerus were comprised in the study. Their average age at the time of operation was 14 years (range, 8 to 24). The diagnoses based on histological examination included juvenile bone cysts in 11, aneurysmal bone cyst in five, non-ossifying fibroma in two, and fibrous dysplasia in two patients. The lesions were localized in the femur, humerus and tibia in 11, five and four patients, respectively. The metaphysis was affected in eight and the diaphysis in 12 patients. Clinical, radiological and scintigraphic examinations were carried out at 2 to 12 years (7 years on average) after surgery. The clinical evaluation included subjective complaints and objective findings. Radiographs were made in standard projections and the osteo-integration of glass-ceramic material was investigated. Three-phase bone scans were made and the healthy and the affected limbs in each patient were compared by means of an index. Radionuclide uptake was considered normal when the index value was equal to 1.0, mildly increased at an index value of 1.2, moderately increased at 1.2-1.5 and markedly increased at an index value higher than 1.5. The clinical evaluation showed that, in the patients with glass-ceramic filling of metaphyses, six had no subjective complaints and two reported transient pain. In the patients with implants in diaphyses, subjective complaints were recorded in nine and no complaints in three patients. No inflammatory changes in soft tissues were found. No restriction in weightbearing of the limb treated was reported by any of the patients. On radiography, 18 patients were free from any disease residue or

  20. Development of a novel bioactive glass suitable for osteosarcoma-related bone grafts.

    Science.gov (United States)

    Rahimnejad Yazdi, Alireza; Torkan, Lawrence; Waldman, Stephen D; Towler, Mark R

    2017-05-31

    In this study, zinc borate-based glasses with increasing gallium content (0, 2.5, 5, 10, and 15 wt % Ga) were synthesized and their effect on the viability and proliferation of preosteoblasts and osteosarcoma cancer cells were investigated. Methyl thiazolyl tetrazolium (MTT) cell viability assays using glass degradation extracts revealed that the extracts from glasses with lower Ga contents could enhance the viability of preosteoblasts, while extracts from the glass composition with 15 wt % Ga caused statistically significant reduction of their viability. MTT cell viability assays using the extracts and osteosarcoma cells showed that only extracts from the glass composition with 5 wt % Ga (G3) did not cause a statistically significant increase in the viability of cancer cells for all degradation periods (1 day, 7 days, and 28 days). G3 was selected as the most suitable composition for the osteosarcoma-related graft operations as it could improve the viability of preosteoblasts without increasing the viability of cancer cells. The viability of preosteoblasts and osteosarcoma cells in contact with the glass powders were also investigated using MTT assays. The results showed that the G3 powders could enhance the viability of preosteoblasts while decreasing the viability of osteosarcoma cells. Finally, live/dead assays revealed that suppression of proliferation appeared to be the mechanism causing the observed reductions in the viability of osteosarcoma cells exposed to G3 powders. © 2017 Wiley Periodicals, Inc. J Biomed Mater Res Part B: Appl Biomater, 2017. © 2017 Wiley Periodicals, Inc.

  1. Clinical and histologic evaluation of an enamel matrix protein derivative combined with a bioactive glass for the treatment of intrabony periodontal defects in humans.

    NARCIS (Netherlands)

    Sculean, A.; Windisch, P.; Keglevich, T.; Gera, I.

    2005-01-01

    The present study clinically and histologically evaluated healing of human intrabony defects following treatment with a combination of enamel matrix derivative (EMD) and bioactive glass (BG) or BG alone. Six patients displaying either combined one- and two-walled (five patients) or three-walled (one

  2. One-pot synthesis of macro-mesoporous bioactive glasses/polylactic acid for bone tissue engineering.

    Science.gov (United States)

    Han, Xiao; Wang, Dan; Chen, Xiang; Lin, Huiming; Qu, Fengyu

    2014-10-01

    The macro-mesoporous bioactive glasses/polylactic acid nanofibers were synthesized via electrospun method followed by acid treatment processing. It was identified to be an effective and simple synthetic strategy to form the uniform nanofibers about 350 nm in size. The non-ionic triblock copolymer, poly(ethylene glycol)-block-poly(propylene glycol)-block-poly(ethylene glycol) (P123), was used as the template for mesoporous structure (5 nm) and the macroporous structure about 10 μm in size derived from the overlapping of the nanofibers. Furthermore, the surface hydrophilic-hydrophobic property can be adjusted by varying the amount of mesoporous bioglass precursor (MBG-p). With the outstanding structure characters and the suitable hydrophilic property, these nanofiber composites show controlled drug release and the fast hydroxyapatite (HAP) mineralization performance. Herein, the novel materials are expected to have potential application for bone tissue engineering. Copyright © 2014 Elsevier B.V. All rights reserved.

  3. In situ reduction of antibacterial silver ions to metallic silver nanoparticles on bioactive glasses functionalized with polyphenols

    Science.gov (United States)

    Ferraris, S.; Miola, M.; Cochis, A.; Azzimonti, B.; Rimondini, L.; Prenesti, E.; Vernè, E.

    2017-02-01

    The realization of surfaces with antibacterial properties due to silver nanoparticles loaded through a green approach is a promising research challenge of the biomaterial field. In this research work, two bioactive glasses have been doubly surface functionalized with polyphenols (gallic acid or natural polyphenols extracted from red grape skins and green tea leaves) and silver nanoparticles deposited by in situ reduction from a silver nitrate aqueous solution. The presence of biomolecules - showing reducing ability to directly obtain in situ metallic silver - and silver nanoparticles was investigated by means of UV-vis spectroscopy, X-Ray Photoelectron Spectroscopy (XPS) and Field Emission Scanning Electron Microscopy (FESEM). The antibacterial activity of the modified surfaces was tested against a multidrug resistant Staphylococcus aureus bacterial strain.

  4. Sol-gel derived nanoscale bioactive glass (NBG) particles reinforced poly(ε-caprolactone) composites for bone tissue engineering.

    Science.gov (United States)

    Lei, Bo; Shin, Kwan-Ha; Noh, Da-Young; Jo, In-Hwan; Koh, Young-Hag; Kim, Hyoun-Ee; Kim, Sung Eun

    2013-04-01

    This study investigated the effect of the addition of sol-gel derived nanoscale bioactive glass (NBG) particles on the mechanical properties and biological performances of PCL polymer, in order to evaluate the potential applications of PCL/NBG composites for bone tissue regeneration. Regardless of the NBG contents (10, 20, and 30 wt.%), the NBG particles, which were synthesized through the sol-gel process using polyethylene glycol (PEG) polymer as a template, could be uniformly dispersed in the PCL matrix, while generating pores in the PCL/NBG composites. The elastic modulus of the PCL/NBG composites increased remarkably from 89±11 MPa to 383±50 MPa with increasing NBG content from 0 to 30 wt.%, while still showing good ultimate tensile strength in the range of 15-19 MPa. The hydrophilicity, water absorption and degradation behavior of the PCL/NBG composites were also enhanced by the addition of the NBG particles. Furthermore, the PCL/NBG composite with a NBG content of 30 wt.% showed significantly enhanced in vitro bioactivity and cellular response compared to those of the pure PCL. Copyright © 2012 Elsevier B.V. All rights reserved.

  5. The Biomineralization of a Bioactive Glass-Incorporated Light-Curable Pulp Capping Material Using Human Dental Pulp Stem Cells

    Directory of Open Access Journals (Sweden)

    Soo-Kyung Jun

    2017-01-01

    Full Text Available The aim of this study was to investigate the biomineralization of a newly introduced bioactive glass-incorporated light-curable pulp capping material using human dental pulp stem cells (hDPSCs. The product (Bioactive® [BA] was compared with a conventional calcium hydroxide-incorporated (Dycal [DC] and a light-curable (Theracal® [TC] counterpart. Eluates from set specimens were used for investigating the cytotoxicity and biomineralization ability, determined by alkaline phosphatase (ALP activity and alizarin red staining (ARS. Cations and hydroxide ions in the extracts were measured. An hDPSC viability of less than 70% was observed with 50% diluted extract in all groups and with 25% diluted extract in the DC. Culturing with 12.5% diluted BA extract statistically lowered ALP activity and biomineralization compared to DC (p0.05. Ca (~110 ppm and hydroxide ions (pH 11 were only detected in DC and TC. Ionic supplement-added BA, which contained similar ion concentrations as TC, showed similar ARS mineralization compared to TC. In conclusion, the BA was similar to, yet more cytotoxic to hDPSCs than, its DC and TC. The BA was considered to stimulate biomineralization similar to DC and TC only when it released a similar amount of Ca and hydroxide ions.

  6. In vitro and in vivo evaluation of a polylactic acid-bioactive glass composite for bone fixation devices.

    Science.gov (United States)

    Vergnol, Gwenaelle; Ginsac, Nathalie; Rivory, Pascaline; Meille, Sylvain; Chenal, Jean-Marc; Balvay, Sandra; Chevalier, Jérôme; Hartmann, Daniel J

    2016-01-01

    Poly(lactic acid) is nowadays among the most used bioabsorbable materials for medical devices. To promote bone growth on the material surface and increase the degradation rate of the polymer, research is currently focused on organic-inorganic composites by adding a bioactive mineral to the polymer matrix. The purpose of this study was to investigate the ability of a poly(L,DL-lactide)-Bioglass® (P(L,DL)LA-Bioglass(®) 45S5) composite to be used as a bone fixation device. In vitro cell viability testing of P(l,dl)LA based composites containing different amounts of Bioglass(®) 45S5 particles was investigated. According to the degradation rate of the P(L,DL)LA matrix and the cytocompatibility experiments, the composite with 30 wt % of Bioglass® particles seemed to be the best candidate for further investigation. To study its behavior after immersion in simulated physiological conditions, the degradation of the composite was analyzed by measuring its weight loss and mechanical properties and by proceeding with X-ray tomography. We demonstrated that the presence of the bioactive glass significantly accelerated the in vitro degradation of the polymer. A preliminary in vivo investigation on rabbits shows that the addition of 30 wt % of Bioglass(®) in the P(L,DL)LA matrix seems to trigger bone osseointegration especially during the first month of implantation. This composite has thus strong potential interest for health applications. © 2015 Wiley Periodicals, Inc.

  7. Bio-active glass air-abrasion has the potential to remove resin composite restorative material selectively

    Energy Technology Data Exchange (ETDEWEB)

    Milly, Hussam [Biomaterials, Biomimetics and Biophotonics Research Group, Kings College London Dental Institute at Guy' s Hospital, King' s Health Partners, London (United Kingdom); Andiappan, Manoharan [Unit of Dental Public Health, Kings College London Dental Institute at Guy' s Hospital, King' s Health Partners, London (United Kingdom); Thompson, Ian [Biomaterials, Biomimetics and Biophotonics Research Group, Kings College London Dental Institute at Guy' s Hospital, King' s Health Partners, London (United Kingdom); Banerjee, Avijit, E-mail: avijit.banerjee@kcl.ac.uk [Biomaterials, Biomimetics and Biophotonics Research Group, Kings College London Dental Institute at Guy' s Hospital, King' s Health Partners, London (United Kingdom); Unit of Conservative Dentistry, King' s College London Dental Institute at Guy' s Hospital, King' s Health Partners, London (United Kingdom)

    2014-06-01

    The aims of this study were to assess: (a) the chemistry, morphology and bioactivity of bio-active glass (BAG) air-abrasive powder, (b) the effect of three air-abrasion operating parameters: air pressure, powder flow rate (PFR) and the abrasive powder itself, on the selective removal of resin composite and (c) the required “time taken”. BAG abrasive particles were characterised using scanning electron microscopy-energy dispersive X-ray spectrometry (SEM-EDX) and Fourier-transform infrared spectroscopy (FTIR). Standardised resin composite restorations created within an enamel analogue block (Macor™) in vitro, were removed using air-abrasion undersimulated clinical conditions. 90 standardised cavities were scanned before and after resin composite removal using laser profilometry and the volume of the resulting 3D images calculated. Multilevel linear model was used to identify the significant factors affecting Macor™ removal. BAG powder removed resin composite more selectively than conventional air-abrasion alumina powder using the same operating parameters (p < 0.001) and the effect of altering the unit's operating parameters was significant (p < 0.001). In conclusion, BAG powder is more efficient than alumina in the selective removal of resin composite particularly under specific operating parameters, and therefore may be recommended clinically as a method of preserving sound enamel structure when repairing and removing defective resin composite restorations.

  8. The Biomineralization of a Bioactive Glass-Incorporated Light-Curable Pulp Capping Material Using Human Dental Pulp Stem Cells.

    Science.gov (United States)

    Jun, Soo-Kyung; Lee, Jung-Hwan; Lee, Hae-Hyoung

    2017-01-01

    The aim of this study was to investigate the biomineralization of a newly introduced bioactive glass-incorporated light-curable pulp capping material using human dental pulp stem cells (hDPSCs). The product (Bioactive® [BA]) was compared with a conventional calcium hydroxide-incorporated (Dycal [DC]) and a light-curable (Theracal® [TC]) counterpart. Eluates from set specimens were used for investigating the cytotoxicity and biomineralization ability, determined by alkaline phosphatase (ALP) activity and alizarin red staining (ARS). Cations and hydroxide ions in the extracts were measured. An hDPSC viability of less than 70% was observed with 50% diluted extract in all groups and with 25% diluted extract in the DC. Culturing with 12.5% diluted BA extract statistically lowered ALP activity and biomineralization compared to DC (p 0.05). Ca (~110 ppm) and hydroxide ions (pH 11) were only detected in DC and TC. Ionic supplement-added BA, which contained similar ion concentrations as TC, showed similar ARS mineralization compared to TC. In conclusion, the BA was similar to, yet more cytotoxic to hDPSCs than, its DC and TC. The BA was considered to stimulate biomineralization similar to DC and TC only when it released a similar amount of Ca and hydroxide ions.

  9. Preparation and in vitro characterization of scaffolds of poly(L-lactic acid) containing bioactive glass ceramic nanoparticles.

    Science.gov (United States)

    Hong, Zhongkui; Reis, Rui L; Mano, João F

    2008-09-01

    Porous nanocomposite scaffolds of poly(l-lactic acid) (PLLA) containing different quantities of bioactive glass ceramic (BGC) nanoparticles (SiO(2):CaO:P(2)O(5) approximately 55:40:5 (mol)) were prepared by a thermally induced phase-separation method. Dioxane was used as the solvent for PLLA. Introduction of less than 20wt.% of BGC nanoparticles did not remarkably affect the porosity of PLLA foam. However, as the BGC content increased to 30wt.%, the porosity of the composite was observed to decrease rapidly. The compressive modulus of the scaffolds increased from 5.5 to 8.0MPa, while the compressive strength increased from 0.28 to 0.35MPa as the BGC content increased from 0 to 30wt.%. The in vitro bioactivity and biodegradability of nanocomposites were investigated by incubation in simulated body fluid (SBF) and phosphate-buffered saline, respectively. Scanning electron microscopy, energy dispersive X-ray spectroscopy, Fourier transform infrared spectroscopy and X-ray diffraction were employed to monitor the surface variation of neat PLLA and PLLA/BGC porous scaffolds during incubation. PLLA/(20wt.%)BGC composite exhibited the best mineralization property in SBF, while the PLLA/(10wt.%)BGC composite showed the highest water absorption ability.

  10. In vitro bioactivity behavior of modified multicomponent borate glasses containing dopants of Ag2O, CuO, CeO2 or V2O5

    Science.gov (United States)

    Marzouk, M. A.; ElBatal, F. H.; Ghoneim, N. A.

    2018-02-01

    Some multi-component borate glasses containing dopants of Ag2O, CuO, CeO2 or V2O5 were prepared. Multi-characterization techniques were carried out to investigate their bioactivity, corrosion weight loss after immersion in phosphate solution. Controlled thermal heat-treatment by two-step technique was done to convert the prepared glasses to their corresponding glass-ceramic derivatives. X-ray diffraction analysis was performed to identify the crystalline phases formed by thermal treatment. Infrared absorption of glasses and glass-ceramics reveal vibrational bands due to combined main triangular and tetrahedral borate groups in their specific wavenumbers besides some sharing of phosphate group. After immersion in the phosphate solution, two extra characteristic peaks are generated indicating the bioactivity of the studied glasses and glass-ceramics through the formation of calcium phosphate (hydroxyapatite). X-ray diffraction data indicate the formation of crystalline phases which are variable with the introduced dopants. The main crystalline phase identified is calcium borate together with some other phases some of which contain phosphate ions. These data indicate that the presence of CaO and P2O5 initiates phase separation and subsequent crystallization of the parent and doped glasses. Weight loss data indicate that glass-ceramics are obviously durable than the parent glasses. SEM micrographs of glass-ceramics before immersion show multiconstituent crystalline phases due to the basic chemical composition consisting of multicomponent mixed alkali and alkaline earth oxides beside P2O5 and with the main B2O3 constituent. After immersion, the crystalline phases are identified to be more distinct in different shapes because of the multi-composition involved.

  11. Toughening and functionalization of bioactive ceramic and glass bone scaffolds by biopolymer coatings and infiltration: a review of the last 5 years.

    Science.gov (United States)

    Philippart, Anahí; Boccaccini, Aldo R; Fleck, Claudia; Schubert, Dirk W; Roether, Judith A

    2015-01-01

    Inorganic scaffolds with high interconnected porosity based on bioactive glasses and ceramics are prime candidates for applications in bone tissue engineering. These materials however exhibit relatively low fracture strength and high brittleness. A simple and effective approach to improve the toughness is to combine the basic scaffold structure with polymer coatings or through the formation of interpenetrating polymer-bioactive ceramic microstructures. The polymeric phase can additionally serve as a carrier for growth factors and therapeutic drugs, thus adding biological functionalities. The present paper reviews the state-of-the art in the field of polymer coated and infiltrated bioactive inorganic scaffolds. Based on the notable combination of bioactivity, improved mechanical properties and drug or growth factor delivery capability, this scaffold type is a candidate for bone and osteochondral regeneration strategies. Remaining challenges for the improvement of the materials are discussed and opportunities to broaden the application potential of this scaffold type are also highlighted.

  12. Evaluation of bioactive glass and demineralized freeze dried bone allograft in the treatment of periodontal intraosseous defects: A comparative clinico-radiographic study

    Directory of Open Access Journals (Sweden)

    Kishore Kumar Katuri

    2013-01-01

    Full Text Available Aim: The purpose of this study was to evaluate the efficacy of demineralized freeze dried bone allograft (DFDBA and bioactive glass by clinically and radiographically in periodontal intrabony defects for a period of 12 months. Materials and Methods: Ten systemically healthy patients diagnosed with chronic periodontitis, with radiographic evidence of at least a pair of contralateral vertical osseous defects were included in this study. Defect on one-side is treated with DFDBA and the other side with bioactive glass. Clinical and radiographic measurements were made at baseline 6 month and 12 month after the surgery. Results: Compared to baseline, the 12 month results indicated that both treatment modalities resulted in significant changes in all clinical parameters (gingival index, probing depth, clinical attachment level (CAL and radiographic parameters (bone fill; P < 0.001FNx01. However, sites treated with DFDBA exhibited statistically significantly more changes compared to the bioactive glass in probing depth reduction (2.5 ± 0.1 mm vs. 1.8 ± 0.1 mm CAL gain 2.4 ± 0.1 mm versus 1.7 ± 0.2 mm; ( P < 0.001FNx01. At 12 months, sites treated with bioactive glass exhibited 56.99% bone fill and 64.76% bone fill for DFDBA sites, which is statistically significant ( P < 0.05FNx01. Conclusion: After 12 months, there was a significant difference between the two materials with sites grafted with DFDBA showing better reduction in probing pocket depth, gain in CAL and a greater percentage of bone fill when compared to that of bioactive glass.

  13. Effect of airborne-particle abrasion on dentin with experimental niobophosphate bioactive glass on the microtensile bond strength of resin cements.

    Science.gov (United States)

    Carvalho, Edilausson Moreno; Lima, Darlon Martins; Carvalho, Ceci Nunes; Loguercio, Alessandro Dourado; Martinelli, José Roberto; Bauer, José

    2015-04-01

    The objective of this study was to evaluate the microtensile bond strength (μTBS) of two resin cements bonded to dentin pre-treated with experimental niobophosphate bioactive glass (NBG). The experimental bioactive glass was prepared by mixing different amounts of NbO5; (NH4)2HP4; CaO; Na2CO3. The particle size distribution and composition of the bioactive glass powder were determined. Twenty flat dentin surfaces from sound extracted human molars were polished with 600-grit SiC paper and air-abraded using experimental bioactive glass niobium powder. The bonding procedures were accomplished by the application of two resin cements: self-etching Panavia F or self-adhesive RelyX U-100. The resin-bonded specimens were cut and the μTBS test was performed after 24h. The failure mode was determined with a stereomicroscope at 40× magnification. The results were statistically analyzed by two-way ANOVA and Tukey tests (α=0.05). The two-way ANOVA did not detect interactions between factors, but only a difference between the self-etching and self-adhesive cement (p=0.001). The self-etching resin cement Panavia F obtained a higher μTBS than the self-adhesive cement Relyx U-100. The predominant failure mode of the cements was adhesive/mixed between the resin cement and dentin. A new bioactive glass containing niobium did not interfere with the immediate bonding performance of self-etching and self-adhesive cements. Copyright © 2015 Japan Prosthodontic Society. Published by Elsevier Ltd. All rights reserved.

  14. Production and Characterization of Glass-Ceramic Materials for Potential Use in Dental Applications: Thermal and Mechanical Properties, Microstructure, and In Vitro Bioactivity

    Directory of Open Access Journals (Sweden)

    Francesco Baino

    2017-12-01

    Full Text Available Multicomponent silicate glasses and their corresponding glass-ceramic derivatives were prepared and tested for potential applications in dentistry. The glasses were produced via a melting-quenching process, ground and sieved to obtain fine-grained powders that were pressed in the form of small cylinders and thermally treated to obtain sintered glass-ceramic samples. X-ray diffraction investigations were carried out on the materials before and after sintering to detect the presence of crystalline phases. Thermal analyses, mechanical characterizations (assessment of bending strength, Young’s modulus, Vickers hardness, fracture toughness, and in vitro bioactivity tests in simulated body fluid were performed. On the basis of the acquired results, different potential applications in the dental field were discussed for the proposed glass-ceramics. The use of such materials can be suggested for either restorative dentistry or dental implantology, mainly depending on their peculiar bioactive and mechanical properties. At the end of the work, the feasibility of a novel full-ceramic bilayered implant was explored and discussed. This implant, comprising a highly bioactive layer expected to promote osteointegration and another one mimicking the features of tooth enamel, can have an interesting potential for whole tooth substitution.

  15. Influence of single and binary doping of strontium and lithium on in vivo biological properties of bioactive glass scaffolds

    Science.gov (United States)

    Khan, Pintu Kumar; Mahato, Arnab; Kundu, Biswanath; Nandi, Samit K.; Mukherjee, Prasenjit; Datta, Someswar; Sarkar, Soumya; Mukherjee, Jayanta; Nath, Shalini; Balla, Vamsi K.; Mandal, Chitra

    2016-09-01

    Effects of strontium and lithium ion doping on the biological properties of bioactive glass (BAG) porous scaffolds have been checked in vitro and in vivo. BAG scaffolds were prepared by conventional glass melting route and subsequently, scaffolds were produced by evaporation of fugitive pore formers. After thorough physico-chemical and in vitro cell characterization, scaffolds were used for pre-clinical study. Soft and hard tissue formation in a rabbit femoral defect model after 2 and 4 months, were assessed using different tools. Histological observations showed excellent osseous tissue formation in Sr and Li + Sr scaffolds and moderate bone regeneration in Li scaffolds. Fluorochrome labeling studies showed wide regions of new bone formation in Sr and Li + Sr doped samples as compared to Li doped samples. SEM revealed abundant collagenous network and minimal or no interfacial gap between bone and implant in Sr and Li + Sr doped samples compared to Li doped samples. Micro CT of Li + Sr samples showed highest degree of peripheral cancellous tissue formation on periphery and cortical tissues inside implanted samples and vascularity among four compositions. Our findings suggest that addition of Sr and/or Li alters physico-chemical properties of BAG and promotes early stage in vivo osseointegration and bone remodeling that may offer new insight in bone tissue engineering.

  16. Bioactivity of gel-glass powders in the CaO-SiO2 system: a comparison with ternary (CaO-P2O5-SiO2) and quaternary glasses (SiO2-CaO-P2O5-Na2O).

    Science.gov (United States)

    Saravanapavan, Priya; Jones, Julian R; Pryce, Russell S; Hench, Larry L

    2003-07-01

    Bioactive glasses react chemically with body fluids in a manner that is compatible with the repair processes of the tissues. This results in the formation of an interfacial bond between the glasses and living tissue. Bioactive glasses also stimulate bone-cell proliferation. This behavior is dependent on the chemical composition as well as the surface texture of the glasses. It has been recently reported that gel-derived monolith specimens in the binary SiO2 - CaO are bioactive over a similar molar range of SiO2 content as the previously studied ternary CaO-P2O5-SiO2 system. In this report, the preparation and bioactivity of the binary gel-glass powder with 70 mol % SiO2 is discussed and its bioactivity is compared with the melt-derived 45S5 (quaternary) Bioglass and sol-gel-derived 58S (ternary) bioactive gel-glass compositions. Dissolution kinetic parameters K(1) and K(2) were also computed based on the silicon release for all glass powders. It was shown that the simple two-component SiO2-CaO gel-glass powder is bioactive with comparable dissolution rates as the clinically used melt-derived 45S5 Bioglass powder and extensively studied sol-gel-derived 58S gel-glass powder. Copyright 2003 Wiley Periodicals, Inc.

  17. Biocompatible and bioactive nanostructured glass coatings synthesized by pulsed laser deposition: In vitro biological tests

    Energy Technology Data Exchange (ETDEWEB)

    Popescu, A.C.; Sima, F.; Duta, L.; Popescu, C.; Mihailescu, I.N. [National Institute for Lasers, Plasma, and Radiation Physics, PO Box MG-54, RO-77125, Bucharest-Magurele (Romania); Capitanu, D. [S.C. Medical SRL, Nasta Hospital, Bucharest (Romania); Mustata, R.; Sima, L.E.; Petrescu, S.M. [Institute of Biochemistry, Romanian Academy, Splaiul Independentei 296, Bucharest (Romania); Janackovic, D. [Faculty of Technology and Metallurgy, Karnegijeva 4, 11000 Belgrade (Serbia)

    2009-03-01

    We report on the synthesis by pulsed laser deposition with a KrF* excimer laser source ({lambda} = 248 nm, {tau} = 25 ns) of bioglass thin films of 6P57 and 6P61 types. Physiology, viability, and proliferation of human osteoblast cells were determined by quantitative in vitro tests performed by flow cytometry on primary osteoblasts cultured on pulsed laser deposited bioglasses. Both types of glass films proved to be appropriate mediums for cell survival and proliferation. In a parallel investigation, cell morphology and adhesion to the surface was studied by fluorescence microscopy and scanning electron microscopy. Strong bonds between the materials and cells were found in both cases, as osteoblast pseudopodes penetrated deep into the material. According to our observations, the 6P57 glass films were superior with respect to viability and proliferation performances.

  18. Treatment of tooth fracture by medium-energy CO2 laser and DP-bioactive glass paste: the interaction of enamel and DP-bioactive glass paste during irradiation by CO2 laser.

    Science.gov (United States)

    Lin, C P; Tseng, Y C; Lin, F H; Liao, J D; Lan, W H

    2001-03-01

    Acute trauma or trauma associated with occlusal disturbance can produce tooth crack or fracture. Although several methods are proposed to treat the defect, however, the prognosis is generally poor. If the fusion of a tooth fracture by laser is possible, it will offer an alternative to extraction or at least serve as an adjunctive treatment in the reconstruction. We have tried to use a continuous-wave CO2 laser and a newly developed DP-bioactive glass paste (DPGP) to fuse or bridge tooth crack or fracture lines. Both the DP-bioactive glass paste and tooth enamel have strong absorption bands at the wavelength of 10.6 microm. Therefore, under CO2 laser, DPGP and enamel should have an effective absorption and melt together. The interface between DPGP and enamel could be regarded as a mixture of DPGP and enamel (DPG-E). The study focused on the phase transformation, microstructure, functional group and thermal behavior of DPG-E with or without CO2 laser irradiation, by the analytical techniques of XRD, FTIR, DTA/TGA, and SEM. The results of XRD showed that the main crystal phase in the DPG-E was dicalcium phosphate dihydrate (CaHPO4.2H2O). It changed into CaHPO4, gamma-Ca2P2O7, beta-Ca2P2O7 and finally alpha-Ca2P2O7 with increasing temperature. In the FTIR analysis, the 720 cm(-1) absorption band ascribed to the P-O-P linkage in pyrophosphate rose up and the intensities of the OH- bands reduced after laser irradiation. In regard to the results of DTA/TGA after irradiation, the weight loss decreased due to the removal of part of absorption water and crystallization water by the CO2 laser. SEM micrographs revealed that the melted masses and the plate-like crystals formed a tight chemical bond between the enamel and DPGP. We expect that DPGP with the help of CO2 laser can be an alternative to the treatment of tooth crack or fracture.

  19. Bioactive Glass-Ceramic Scaffolds from Novel ‘Inorganic Gel Casting’ and Sinter-Crystallization

    Science.gov (United States)

    Elsayed, Hamada; Rincón Romero, Acacio; Ferroni, Letizia; Gardin, Chiara; Zavan, Barbara; Bernardo, Enrico

    2017-01-01

    Highly porous wollastonite-diopside glass-ceramics have been successfully obtained by a new gel-casting technique. The gelation of an aqueous slurry of glass powders was not achieved according to the polymerization of an organic monomer, but as the result of alkali activation. The alkali activation of a Ca-Mg silicate glass (with a composition close to 50 mol % wollastonite—50 mol % diopside, with minor amounts of Na2O and P2O5) allowed for the obtainment of well-dispersed concentrated suspensions, undergoing progressive hardening by curing at low temperature (40 °C), owing to the formation of a C–S–H (calcium silicate hydrate) gel. An extensive direct foaming was achieved by vigorous mechanical stirring of partially gelified suspensions, comprising also a surfactant. The open-celled structure resulting from mechanical foaming could be ‘frozen’ by the subsequent sintering treatment, at 900–1000 °C, causing substantial crystallization. A total porosity exceeding 80%, comprising both well-interconnected macro-pores and micro-pores on cell walls, was accompanied by an excellent compressive strength, even above 5 MPa. PMID:28772531

  20. New generation poly(ε-caprolactone)/gel-derived bioactive glass composites for bone tissue engineering: Part I. Material properties

    Energy Technology Data Exchange (ETDEWEB)

    Dziadek, Michal, E-mail: dziadek@agh.edu.pl [AGH University of Science and Technology, Faculty of Materials Science and Ceramics, Department of Glass Technology and Amorphous Coatings, 30 Mickiewicza Ave., 30-059 Krakow (Poland); Menaszek, Elzbieta, E-mail: elzbieta.menaszek@uj.edu.pl [Jagiellonian University, Collegium Medicum, Department of Cytobiology, 9 Medyczna St., 30-688 Krakow (Poland); Zagrajczuk, Barbara, E-mail: b.zagrajczuk@gmail.com [AGH University of Science and Technology, Faculty of Materials Science and Ceramics, Department of Glass Technology and Amorphous Coatings, 30 Mickiewicza Ave., 30-059 Krakow (Poland); Pawlik, Justyna, E-mail: pawlikj@agh.edu.pl [AGH University of Science and Technology, Faculty of Materials Science and Ceramics, Department of Glass Technology and Amorphous Coatings, 30 Mickiewicza Ave., 30-059 Krakow (Poland); Cholewa-Kowalska, Katarzyna, E-mail: cholewa@agh.edu.pl [AGH University of Science and Technology, Faculty of Materials Science and Ceramics, Department of Glass Technology and Amorphous Coatings, 30 Mickiewicza Ave., 30-059 Krakow (Poland)

    2015-11-01

    Poly(ε-caprolactone) (PCL) based composite films containing 12 and 21 vol.% bioactive glass (SBG) microparticles were prepared by solvent casting method. Two gel-derived SBGs of SiO{sub 2}–CaO–P{sub 2}O{sub 5} system differing in SiO{sub 2} and CaO contents were applied (mol%): S2: 80SiO{sub 2}, 16CaO, 4P{sub 2}O{sub 5} and A2: 40SiO{sub 2}, 54CaO, 6P{sub 2}O{sub 5}. The surfaces of the films in contact with Petri dish and exposed to the gas phase during casting were denoted as GS and AS, respectively. Both surfaces of films were characterised in terms of their morphology, micro- and nano-topography as well as wettability. Also mechanical properties (tensile strength, Young's modulus) and PCL matrix crystallinity (degree of crystallinity, crystal size) were evaluated. Degradation behaviour was examined by incubation of materials in UHQ-water at 37 °C for 56 weeks. The crystallinity, melting temperature and mass loss of incubated materials and pH changes of water were monitored. Furthermore, proliferation of MG-63 osteoblastic cells by direct contact and cytotoxic effect of obtained materials were investigated. Results showed that opposite surfaces of the same polymer and composite films differ in studied surface parameters. The addition of SBG particles into PCL matrix improves nano- and micro-roughness of both surfaces, enhances the hydrophilicity of GS surfaces (~ 67° for 21A2-PCL compared to ~ 78° for pure PCL) and also makes AS surface more hydrophobic (~ 94° for 21S2-PCL compared to ~ 86° for pure PCL). The nucleation density of PCL was increased with increasing content of SBG particles, which results in the large number of fine spherulites on composite AS surfaces observed using polarized optical (POM), scanning electron (SEM), and atomic force (AFM) microscopies. Higher content of SBG particles causes a notable increase of Young's modulus (from 0.38 GPa for pure PCL, 0.90 GPa for 12A2-PCL to 1.31 GPa for 21A2-PCL), which also depends on

  1. Bioactive Copper-Doped Glass Scaffolds Can Stimulate Endothelial Cells in Co-Culture in Combination with Mesenchymal Stem Cells

    Science.gov (United States)

    Rath, Subha N.; Brandl, Andreas; Hiller, Daniel; Hoppe, Alexander; Gbureck, Uwe; Horch, Raymund E.; Boccaccini, Aldo R.; Kneser, Ulrich

    2014-01-01

    Bioactive glass (BG) scaffolds are being investigated for bone tissue engineering applications because of their osteoconductive and angiogenic nature. However, to increase the in vivo performance of the scaffold, including enhancing the angiogenetic growth into the scaffolds, some researchers use different modifications of the scaffold including addition of inorganic ionic components to the basic BG composition. In this study, we investigated the in vitro biocompatibility and bioactivity of Cu2+-doped BG derived scaffolds in either BMSC (bone-marrow derived mesenchymal stem cells)-only culture or co-culture of BMSC and human dermal microvascular endothelial cells (HDMEC). In BMSC-only culture, cells were seeded either directly on the scaffolds (3D or direct culture) or were exposed to ionic dissolution products of the BG scaffolds, kept in permeable cell culture inserts (2D or indirect culture). Though we did not observe any direct osteoinduction of BMSCs by alkaline phosphatase (ALP) assay or by PCR, there was increased vascular endothelial growth factor (VEGF) expression, observed by PCR and ELISA assays. Additionally, the scaffolds showed no toxicity to BMSCs and there were healthy live cells found throughout the scaffold. To analyze further the reasons behind the increased VEGF expression and to exploit the benefits of the finding, we used the indirect method with HDMECs in culture plastic and Cu2+-doped BG scaffolds with or without BMSCs in cell culture inserts. There was clear observation of increased endothelial markers by both FACS analysis and acetylated LDL (acLDL) uptake assay. Only in presence of Cu2+-doped BG scaffolds with BMSCs, a high VEGF secretion was demonstrated by ELISA; and typical tubular structures were observed in culture plastics. We conclude that Cu2+-doped BG scaffolds release Cu2+, which in turn act on BMSCs to secrete VEGF. This result is of significance for the application of BG scaffolds in bone tissue engineering approaches. PMID

  2. Bioactive copper-doped glass scaffolds can stimulate endothelial cells in co-culture in combination with mesenchymal stem cells.

    Directory of Open Access Journals (Sweden)

    Subha N Rath

    Full Text Available Bioactive glass (BG scaffolds are being investigated for bone tissue engineering applications because of their osteoconductive and angiogenic nature. However, to increase the in vivo performance of the scaffold, including enhancing the angiogenetic growth into the scaffolds, some researchers use different modifications of the scaffold including addition of inorganic ionic components to the basic BG composition. In this study, we investigated the in vitro biocompatibility and bioactivity of Cu2+-doped BG derived scaffolds in either BMSC (bone-marrow derived mesenchymal stem cells-only culture or co-culture of BMSC and human dermal microvascular endothelial cells (HDMEC. In BMSC-only culture, cells were seeded either directly on the scaffolds (3D or direct culture or were exposed to ionic dissolution products of the BG scaffolds, kept in permeable cell culture inserts (2D or indirect culture. Though we did not observe any direct osteoinduction of BMSCs by alkaline phosphatase (ALP assay or by PCR, there was increased vascular endothelial growth factor (VEGF expression, observed by PCR and ELISA assays. Additionally, the scaffolds showed no toxicity to BMSCs and there were healthy live cells found throughout the scaffold. To analyze further the reasons behind the increased VEGF expression and to exploit the benefits of the finding, we used the indirect method with HDMECs in culture plastic and Cu2+-doped BG scaffolds with or without BMSCs in cell culture inserts. There was clear observation of increased endothelial markers by both FACS analysis and acetylated LDL (acLDL uptake assay. Only in presence of Cu2+-doped BG scaffolds with BMSCs, a high VEGF secretion was demonstrated by ELISA; and typical tubular structures were observed in culture plastics. We conclude that Cu2+-doped BG scaffolds release Cu2+, which in turn act on BMSCs to secrete VEGF. This result is of significance for the application of BG scaffolds in bone tissue engineering

  3. Effect of size of bioactive glass nanoparticles on mesenchymal stem cell proliferation for dental and orthopedic applications

    Energy Technology Data Exchange (ETDEWEB)

    Ajita, J.; Saravanan, S.; Selvamurugan, N., E-mail: selvamurugan.n@ktr.srmuniv.ac.in

    2015-08-01

    Bioactive glass nanoparticles (nanostructured bioglass ceramics or nBGs) have been widely employed as a filler material for bone tissue regeneration. The physical properties of nBG particles govern their biological actions. In this study, the impact of the size of nBG particles on mouse mesenchymal stem cell (mMSC) proliferation was investigated. Three different sizes of nBG particles were prepared via the sol–gel method with varying concentrations of the surfactant and polyethylene glycol (PEG), and the particles were characterized. Increased concentrations of PEG decreased the size of nBG particles (nBG-1: 74.7 ± 0.62 nm, nBG-2: 43.25 ± 1.5 nm, and nBG-3: 37.6 ± 0.81 nm). All three nBGs were non-toxic at a concentration of 20 mg/mL. Increased proliferation was observed in mMSCs treated with smaller nBG particles. Differential mRNA expression of cyclin A2, B2, D1, and E1 genes induced by nBG particles was noticed in the mMSCs. nBG-1 and nBG-3 particles promoted cells in the G0/G1 phase to enter the S and G2/M phases. nBG particles activated ERK, but prolonged activation was achieved with nBG-3 particles. Among the prepared nBG particles, nBG-3 particles showed enhanced mMSC proliferation via the sustained activation of ERKs, upregulation of cyclin gene(s) expression, and promotion of cell transition from the G0/G1 phase to the S and G2/M phases. Thus, this study indicates that small nBG particles have clinical applications in dental and bone treatments as fillers or bone-tissue bond forming materials. - Highlights: • Three different sizes of bioactive glass nanoparticles (nBGs) were prepared via the sol–gel method. • Increased concentrations of polyethylene glycol decreased the size of nBG particles. • All three nBGs were non-toxic at a concentration of 20 mg/mL. • Cell number, cell cycle phase analysis, cyclin gene expression and ERK activation were studied. • Increased proliferation was observed in mMSCs treated with smaller nBG particles.

  4. Silicate, borosilicate, and borate bioactive glass scaffolds with controllable degradation rate for bone tissue engineering applications. I. Preparation and in vitro degradation.

    Science.gov (United States)

    Fu, Qiang; Rahaman, Mohamed N; Fu, Hailuo; Liu, Xin

    2010-10-01

    Bioactive glass scaffolds with a microstructure similar to that of dry human trabecular bone but with three different compositions were evaluated for potential applications in bone repair. The preparation of the scaffolds and the effect of the glass composition on the degradation and conversion of the scaffolds to a hydroxyapatite (HA)-type material in a simulated body fluid (SBF) are reported here (Part I). The in vitro response of osteogenic cells to the scaffolds and the in vivo evaluation of the scaffolds in a rat subcutaneous implantation model are described in Part II. Scaffolds (porosity = 78-82%; pore size = 100-500 microm) were prepared using a polymer foam replication technique. The glasses consisted of a silicate (13-93) composition, a borosilicate composition (designated 13-93B1), and a borate composition (13-93B3), in which one-third or all of the SiO2 content of 13-93 was replaced by B2O3, respectively. The conversion rate of the scaffolds to HA in the SBF increased markedly with the B2O3 content of the glass. Concurrently, the pH of the SBF also increased with the B2O3 content of the scaffolds. The compressive strengths of the as-prepared scaffolds (5-11 MPa) were in the upper range of values reported for trabecular bone, but they decreased markedly with immersion time in the SBF and with increasing B2O3 content of the glass. The results show that scaffolds with a wide range of bioactivity and degradation rate can be achieved by replacing varying amounts of SiO(2) in silicate bioactive glass with B2O3. Copyright 2010 Wiley Periodicals, Inc. J Biomed Mater Res Part A, 2010.

  5. Gallic acid grafting modulates the oxidative potential of ferrimagnetic bioactive glass-ceramic SC-45.

    Science.gov (United States)

    Corazzari, Ingrid; Tomatis, Maura; Turci, Francesco; Ferraris, Sara; Bertone, Elisa; Prenesti, Enrico; Vernè, Enrica

    2016-12-01

    Magnetite-containing glass-ceramics are promising bio-materials for replacing bone tissue after tumour resection. Thanks to their ferrimagnetic properties, they generate heat when subjected to an alternated magnetic field. In virtue of this they can be employed for the hyperthermic treatment of cancer. Moreover, grafting anti-cancer drugs onto their surface produces specific anti-neoplastic activity in these biomaterials. Gallic acid (GA) exhibits antiproliferative activity which renders it a promising candidate for anticancer applications. In the present paper, the reactivity of ferrimagnetic glass-ceramic SC-45 grafted with GA (SC-45+GA) was studied in terms of ROS release, rupture of the C-H bond of the formate molecule and Fenton reactivity by EPR/spin trapping in acellular systems. The ability of these materials to cause lipid peroxidation was assessed by UV-vis/TBA assay employing linoleic acid as a model of membrane lipid. The results, compared to those obtained with SC-45, showed that GA grafting (i) significantly enhanced the Fenton reactivity and (ii) restored the former reactivity of SC-45 towards both the C-H bond and linoleic acid which had been completely suppressed by prolonged contact with water. Fe 2+ centres at the surface are probably implicated. GA, acting as a pro-oxidant, reduces Fe 3+ to Fe 2+ by maintaining a supply of Fe 2+ at the surface of SC-45+GA. Copyright © 2016 Elsevier B.V. All rights reserved.

  6. Effect of ZrO(2) additions on the crystallization, mechanical and biological properties of MgO-CaO-SiO(2)-P(2)O(5)-CaF(2) bioactive glass-ceramics.

    Science.gov (United States)

    Li, H C; Wang, D G; Meng, X G; Chen, C Z

    2014-06-01

    A series of ZrO(2) doped MgO-CaO-SiO(2)-P(2)O(5)-CaF(2) bioactive glass-ceramics were obtained by sintering method. The crystallization behavior, phase composition, morphology and structure of glass-ceramics were characterized. The bending strength, elastic modulus, fracture toughness, micro-hardness and thermal expansion coefficient (TEC) of glass-ceramics were investigated. The in vitro bioactivity and cytotoxicity tests were used to evaluate the bioactivity and biocompatibility of glass-ceramics. The sedimentation mechanism and growth process of apatites on sample surface were discussed. The results showed that the mainly crystalline phases of glass-ceramics were Ca(5)(PO4)3F (fluorapatite) and β-CaSiO(3). (β-wollastonite). m-ZrO(2) (monoclinic zirconia) declined the crystallization temperatures of glasses. t-ZrO(2) (tetragonal zirconia) increased the crystallization temperature of Ca(5)(PO4)(3)F and declined the crystallization temperature of β-CaSiO(3). t-ZrO(2) greatly increased the fracture toughness, bending strength and micro-hardness of glass-ceramics. The nanometer apatites were induced on the surface of glass-ceramic after soaking 28 days in SBF (simulated body fluid), indicating the glass-ceramic has good bioactivity. The in vitro cytotoxicity test demonstrated the glass-ceramic has no toxicity to cell. Copyright © 2014 Elsevier B.V. All rights reserved.

  7. Bioactivity and cell proliferation in radiopaque gel-derived CaO-P2O5-SiO2-ZrO2 glass and glass-ceramic powders.

    Science.gov (United States)

    Montazerian, Maziar; Yekta, Bijan Eftekhari; Marghussian, Vahak Kaspari; Bellani, Caroline Faria; Siqueira, Renato Luiz; Zanotto, Edgar Dutra

    2015-10-01

    In this study, 10 mol% ZrO2 was added to a 27CaO-5P2O5-68SiO2 (mol%) base composition synthesized via a simple sol-gel method. This composition is similar to that of a frequently investigated bioactive gel-glass. The effects of ZrO2 on the in vitro bioactivity and MG-63 cell proliferation of the glass and its derivative polycrystalline (glass-ceramic) powder were investigated. The samples were characterized using thermo-gravimetric and differential thermal analysis (TG/DTA), X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR), and scanning electron microscopy (SEM) coupled to energy dispersive X-ray spectroscopy (EDS). Release of Si, Ca, P and Zr into simulated body fluid (SBF) was determined by inductively coupled plasma (ICP). Upon heat treatment at 1000 °C, the glass powder crystallized into an apatite-wollastonite-zirconia glass-ceramic powder. Hydroxycarbonate apatite (HCA) formation on the surface of the glass and glass-ceramic particles containing ZrO2 was confirmed by FTIR and SEM. Addition of ZrO2 to the base glass composition decreased the rate of HCA formation in vitro from one day to three days, and hence, ZrO2 could be employed to control the rate of apatite formation. However, the rate of HCA formation on the glass-ceramic powder containing ZrO2 crystal was equal to that in the base glassy powder. Tests with a cultured human osteoblast-like MG-63 cells revealed that the glass and glass-ceramic materials stimulated cell proliferation, indicating that they are biocompatible and are not cytotoxic in vitro. Moreover, zirconia clearly increased osteoblast proliferation over that of the Zr-free samples. This increase is likely associated with the lower solubility of these samples and, consequently, a smaller variation in the media pH. Despite the low solubility of these materials, bioactivity was maintained, indicating that these glassy and polycrystalline powders are potential candidates for bone graft substitutes and bone cements with

  8. Effect of Alumina Incorporation on the Surface Mineralization and Degradation of a Bioactive Glass (CaO-MgO-SiO₂-Na₂O-P₂O₅-CaF₂)-Glycerol Paste.

    Science.gov (United States)

    Tulyaganov, Dilshat; Abdukayumov, Khasan; Ruzimuradov, Olim; Hojamberdiev, Mirabbos; Ionescu, Emanuel; Riedel, Ralf

    2017-11-18

    This study investigates the dissolution behavior as well as the surface biomineralization in simulated body fluid (SBF) of a paste composed of glycerol (gly) and a bioactive glass in the system CaO-MgO-SiO₂-Na₂O-P₂O₅-CaF₂ (BG). The synthesis of the bioactive glass in an alumina crucible has been shown to significantly affect its bioactivity due to the incorporation of aluminum (ca. 1.3-1.4 wt %) into the glass network. Thus, the kinetics of the hydroxyapatite (HA) mineralization on the glass prepared in the alumina crucible was found to be slower than that reported for the same glass composition prepared in a Pt crucible. It is considered that the synthesis conditions lead to the incorporation of small amount of aluminum into the BG network and thus delay the HA mineralization. Interestingly, the BG-gly paste was shown to have significantly higher bioactivity than that of the as-prepared BG. Structural analysis of the paste indicate that glycerol chemically interacts with the glass surface and strongly alter the glass network architecture, thus generating a more depolymerized network, as well as an increased amount of silanol groups at the surface of the glass. In particular, BG-gly paste features early intermediate calcite precipitation during immersion in SBF, followed by hydroxyapatite formation after ca. seven days of SBF exposure; whereas the HA mineralization seems to be suppressed in BG, probably a consequence of the incorporation of aluminum into the glass network. The results obtained within the present study reveal the positive effect of using pastes based on bioactive glasses and organic carriers (here alcohols) which may be of interest not only due to their advantageous visco-elastic properties, but also due to the possibility of enhancing the glass bioactivity upon surface interactions with the organic carrier.

  9. Effect of Alumina Incorporation on the Surface Mineralization and Degradation of a Bioactive Glass (CaO-MgO-SiO2-Na2O-P2O5-CaF2-Glycerol Paste

    Directory of Open Access Journals (Sweden)

    Dilshat Tulyaganov

    2017-11-01

    Full Text Available This study investigates the dissolution behavior as well as the surface biomineralization in simulated body fluid (SBF of a paste composed of glycerol (gly and a bioactive glass in the system CaO-MgO-SiO2-Na2O-P2O5-CaF2 (BG. The synthesis of the bioactive glass in an alumina crucible has been shown to significantly affect its bioactivity due to the incorporation of aluminum (ca. 1.3–1.4 wt % into the glass network. Thus, the kinetics of the hydroxyapatite (HA mineralization on the glass prepared in the alumina crucible was found to be slower than that reported for the same glass composition prepared in a Pt crucible. It is considered that the synthesis conditions lead to the incorporation of small amount of aluminum into the BG network and thus delay the HA mineralization. Interestingly, the BG-gly paste was shown to have significantly higher bioactivity than that of the as-prepared BG. Structural analysis of the paste indicate that glycerol chemically interacts with the glass surface and strongly alter the glass network architecture, thus generating a more depolymerized network, as well as an increased amount of silanol groups at the surface of the glass. In particular, BG-gly paste features early intermediate calcite precipitation during immersion in SBF, followed by hydroxyapatite formation after ca. seven days of SBF exposure; whereas the HA mineralization seems to be suppressed in BG, probably a consequence of the incorporation of aluminum into the glass network. The results obtained within the present study reveal the positive effect of using pastes based on bioactive glasses and organic carriers (here alcohols which may be of interest not only due to their advantageous visco-elastic properties, but also due to the possibility of enhancing the glass bioactivity upon surface interactions with the organic carrier.

  10. Mesoporous bioactive glass surface modified poly(lactic-co-glycolic acid) electrospun fibrous scaffold for bone regeneration

    Science.gov (United States)

    Chen, Shijie; Jian, Zhiyuan; Huang, Linsheng; Xu, Wei; Liu, Shaohua; Song, Dajiang; Wan, Zongmiao; Vaughn, Amanda; Zhan, Ruisen; Zhang, Chaoyue; Wu, Song; Hu, Minghua; Li, Jinsong

    2015-01-01

    A mesoporous bioactive glass (MBG) surface modified with poly(lactic-co-glycolic acid) (PLGA) electrospun fibrous scaffold for bone regeneration was prepared by dip-coating a PLGA electrospun fibrous scaffold into MBG precursor solution. Different surface structures and properties were acquired by different coating times. Surface morphology, chemical composition, microstructure, pore size distribution, and hydrophilicity of the PLGA-MBG scaffold were characterized. Results of scanning electron microscopy indicated that MBG surface coating made the scaffold rougher with the increase of MBG content. Scaffolds after MBG modification possessed mesoporous architecture on the surface. The measurements of the water contact angles suggested that the incorporation of MBG into the PLGA scaffold improved the surface hydrophilicity. An energy dispersive spectrometer evidenced that calcium-deficient carbonated hydroxyapatite formed on the PLGA-MBG scaffolds after a 7-day immersion in simulated body fluid. In vitro studies showed that the incorporation of MBG favored cell proliferation and osteogenic differentiation of human mesenchymal stem cells on the PLGA scaffolds. Moreover, the MBG surface-modified PLGA (PLGA-MBG) scaffolds were shown to be capable of providing the improved adsorption/release behaviors of bone morphogenetic protein-2 (BMP-2). It is very significant that PLGA-MBG scaffolds could be effective for BMP-2 delivery and bone regeneration. PMID:26082632

  11. Improved dimensional stability with bioactive glass fibre skeleton in poly(lactide-co-glycolide) porous scaffolds for tissue engineering.

    Science.gov (United States)

    Haaparanta, Anne-Marie; Uppstu, Peter; Hannula, Markus; Ellä, Ville; Rosling, Ari; Kellomäki, Minna

    2015-11-01

    Bone tissue engineering requires highly porous three-dimensional (3D) scaffolds with preferable osteoconductive properties, controlled degradation, and good dimensional stability. In this study, highly porous 3D poly(d,l-lactide-co-glycolide) (PLGA) - bioactive glass (BG) composites (PLGA/BG) were manufactured by combining highly porous 3D fibrous BG mesh skeleton with porous PLGA in a freeze-drying process. The 3D structure of the scaffolds was investigated as well as in vitro hydrolytic degradation for 10weeks. The effect of BG on the dimensional stability, scaffold composition, pore structure, and degradation behaviour of the scaffolds was evaluated. The composites showed superior pore structure as the BG fibres inhibited shrinkage of the scaffolds. The BG was also shown to buffer the acidic degradation products of PLGA. These results demonstrate the potential of these PLGA/BG composites for bone tissue engineering, but the ability of this kind of PLGA/BG composites to promote bone regeneration will be studied in forthcoming in vivo studies. Copyright © 2015 Elsevier B.V. All rights reserved.

  12. Influence of Porous Spherical-Shaped Hydroxyapatite on Mechanical Strength and Bioactive Function of Conventional Glass Ionomer Cement

    Directory of Open Access Journals (Sweden)

    Szu-Yu Chiu

    2017-01-01

    Full Text Available Glass-ionomer-cement (GIC is helpful in Minimal Intervention Dentistry because it releases fluoride ions and is highly biocompatible. The aim of this study is to investigate the mechanisms by which hydroxyapatite (HAp improves the mechanical strength and bioactive functioning of GIC when these materials are combined to make apatite ionomer cement (AIC. A conventional GIC powder was mixed with porous, spherical-HAp particles (HApS, crystalline HAp (HAp200 or one of two types of cellulose. The micro-compressive strengths of the additive particles were measured, and various specimens were evaluated with regard to their compressive strengths (CS, fluoride release concentrations (fluoride electrode and multi-element release concentrations. The AIC was found to release higher concentrations of fluoride (1.2 times and strontium ions (1.5 times compared to the control GIC. It was detected the more release of calcium originated from HApS than HAp200 in AIC. The CS of the AIC incorporating an optimum level of HAp was also significantly higher than that of the GIC. These results suggest that adding HAp can increase the release concentration of ions required for remineralization while maintaining the CS of the GIC. This effect does not result from a physical phenomenon, but rather from chemical reactions between the HAp and polyacrylic acid of GIC.

  13. A clinical study on the efficacy of hydroxyapatite - Bioactive glass composite granules in the management of periodontal bony defects

    Directory of Open Access Journals (Sweden)

    Tirthankar Debnath

    2014-01-01

    Full Text Available Background: In periodontal regeneration, several alloplastic materials are being used with a goal to reconstruct new osseous tissue in the infrabony defect sites. The present study was undertaken to evaluate the efficacy of hydroxyapatite-bioactive glass (HA:BG composite granules in the management of periodontal bony defects. Materials and Methods: A randomized control study was conducted. Subjects with infrabony defects were divided into three groups. Test Group 1 (n = 10: Defect site was treated with HA:BG, with a biodegradable membrane. Test Group 2 (n = 10: Defect site was treated with HAP, with a biodegradable membrane. Control group (n = 10: Defect site was treated with open flap debridement with a biodegradable membrane Results: The healing of defects was uneventful and free of any biological complications. The gain in clinical attachment level, reduction of probing pocket depth, and defect fill were statistically significant in all three groups. TG1 sites showed significant defect fill than TG2 and CG sites. Conclusion: The performance of HA:BG was better compared to HAP and open flap debridement for the reconstruction of infrabony defects.

  14. Platelet-rich plasma plus bioactive glass in the treatment of intra-bony defects: a study in dogs

    Directory of Open Access Journals (Sweden)

    Marcelo Diniz Carvalho

    2011-02-01

    Full Text Available OBJECTIVE: This study was designed to evaluate, histomorphometrically, the association of platelet-rich plasma (PRP and bioactive glass (BG in the treatment of periodontal intrabony defects. MATERIAL AND METHODS: Nine mongrel dogs were included in the study. Three-wall intrabony defects were surgically created at the mesial and distal aspect of first mandibular molar and exposed to plaque accumulation for 1 month. The defects were randomly assigned to the groups: control, BG, PRP, PRP+BG. Dogs were sacrificed 90 days after the surgeries. The histometric parameters evaluated were: length of sulcular and junctional epithelium, connective tissue adaptation, new cementum, new bone, defect extension and area of new bone filling the defect. RESULTS: A superior area of new bone was observed in PRP+BG and BG (13.80±2.32 mm² and 15.63±2.64 mm², respectively when compared to the other groups (8.19±1.46 mm² and 8.81±1.47 mm² for control and PRP, respectively. No statistically significant differences were observed in the remaining parameters. CONCLUSIONS: Within the limits of this study, it may be concluded that PRP failed to provide statistically significant improvements in the histometric parameters.

  15. Surface functionalization of bioactive glasses with natural molecules of biological significance, part II: Grafting of polyphenols extracted from grape skin

    Science.gov (United States)

    Zhang, Xin; Ferraris, Sara; Prenesti, Enrico; Verné, Enrica

    2013-12-01

    Polyphenols, as one of the most important family of phytochemicals protective substances from grape fruit, possess various biological activities and health-promoting benefits, for example: inhibition of some degenerative diseases, cardiovascular diseases and certain types of cancers, reduction of plasma oxidative stress and slowing aging. The combination of polyphenols and biomaterials may have good potential to reach good bioavailability and controlled release, as well as to give biological signaling properties to the biomaterial surfaces. In this research, conventional solvent extraction was developed for obtaining polyphenols from dry grape skins. The Folin&Ciocalteu method was used to determine the amount of total polyphenols in the extracts. Surface functionalization of two bioactive glasses (SCNA and CEL2) was performed by grafting the extracted polyphenols on their surfaces. The effectiveness of the functionalization was tested by UV spectroscopy, which analyzes the amount of polyphenols in the uptake solution (before and after functionalization) and on solid samples, and XPS, which analyzes the presence of phenols on the material surface.

  16. Surface properties and ion release from fluoride-containing bioactive glasses promote osteoblast differentiation and mineralization in vitro.

    Science.gov (United States)

    Gentleman, E; Stevens, M M; Hill, R G; Brauer, D S

    2013-03-01

    Bioactive glasses (BG) are suitable for bone regeneration applications as they bond with bone and can be tailored to release therapeutic ions. Fluoride, which is widely recognized to prevent dental caries, is efficacious in promoting bone formation and preventing osteoporosis-related fractures when administered at appropriate doses. To take advantage of these properties, we created BG incorporating increasing levels of fluoride whilst holding their silicate structure constant, and tested their effects on human osteoblasts in vitro. Our results demonstrate that, whilst cell proliferation was highest on low-fluoride-containing BG, markers for differentiation and mineralization were highest on BG with the highest fluoride contents, a likely effect of a combination of surface effects and ion release. Furthermore, osteoblasts exposed to the dissolution products of fluoride-containing BG or early doses of sodium fluoride showed increased alkaline phosphatase activity, a marker for bone mineralization, suggesting that fluoride can direct osteoblast differentiation. Taken together, these results suggest that BG that can release therapeutic levels of fluoride may find use in a range of bone regeneration applications. Copyright © 2012 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

  17. Acid neutralizing, mechanical and physical properties of pit and fissure sealants containing melt-derived 45S5 bioactive glass.

    Science.gov (United States)

    Yang, Song-Yi; Piao, Yin-Zhu; Kim, Sung-Min; Lee, Yong-Keun; Kim, Kyoung-Nam; Kim, Kwang-Mahn

    2013-12-01

    The aim of this study was to examine the effects of 45S5 bioactive glass (BAG) on the acid neutralizing, mechanical and physical properties of pit and fissure sealants. 45S5BAG (properties, specimens were immersed in lactic acid solution (pH 4.0). Then, the change in pH and the time required to raise the pH from 4.0 to 5.5 were measured. In addition, flexural strength, water sorption and solubility were analyzed. The acid neutralizing properties of each group exhibited increasing pH values as more 45S5BAG was added, and the time required to raise the pH from 4.0 to 5.5 became shorter as the proportion of 45S5BAG increased (P0.05), except for BAG50. The novel pit and fissure sealants neutralized the acid solution (pH 4.0) and exhibited appropriate mechanical and physical properties. Therefore, these compounds are suitable candidates for caries-inhibiting dental materials. Copyright © 2013 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

  18. Three dimensional printing of calcium sulfate and mesoporous bioactive glass scaffolds for improving bone regeneration in vitro and in vivo

    Science.gov (United States)

    Qi, Xin; Pei, Peng; Zhu, Min; Du, Xiaoyu; Xin, Chen; Zhao, Shichang; Li, Xiaolin; Zhu, Yufang

    2017-02-01

    In the clinic, bone defects resulting from infections, trauma, surgical resection and genetic malformations remain a significant challenge. In the field of bone tissue engineering, three-dimensional (3D) scaffolds are promising for the treatment of bone defects. In this study, calcium sulfate hydrate (CSH)/mesoporous bioactive glass (MBG) scaffolds were successfully fabricated using a 3D printing technique, which had a regular and uniform square macroporous structure, high porosity and excellent apatite mineralization ability. Human bone marrow-derived mesenchymal stem cells (hBMSCs) were cultured on scaffolds to evaluate hBMSC attachment, proliferation and osteogenesis-related gene expression. Critical-sized rat calvarial defects were applied to investigate the effect of CSH/MBG scaffolds on bone regeneration in vivo. The in vitro results showed that CSH/MBG scaffolds stimulated the adhesion, proliferation, alkaline phosphatase (ALP) activity and osteogenesis-related gene expression of hBMSCs. In vivo results showed that CSH/MBG scaffolds could significantly enhance new bone formation in calvarial defects compared to CSH scaffolds. Thus 3D printed CSH/MBG scaffolds would be promising candidates for promoting bone regeneration.

  19. Physicochemical Properties and Volumetric Change of Silicone/Bioactive Glass and Calcium Silicate-based Endodontic Sealers.

    Science.gov (United States)

    Tanomaru-Filho, Mario; Torres, Fernanda Ferrari Esteves; Chávez-Andrade, Gisselle Moraima; de Almeida, Madelise; Navarro, Luciana Guilherme; Steier, Liviu; Guerreiro-Tanomaru, Juliane Maria

    2017-12-01

    This study evaluated setting time (ST), radiopacity, pH, flow, solubility, and volumetric change (VC) of a silicone, gutta-percha, and bioactive glass-based sealer, GuttaFlow Bioseal (GFB), and a calcium silicate-based sealer, TotalFill BC Sealer (TFBC), in comparison with AH Plus. ST and flow were evaluated in accordance with the ISO 6876 Standard. pH was evaluated after different time intervals (1, 3, 7, 14, 21, and 28 days). Radiopacity was evaluated by radiographic analysis in millimeters of aluminum. Solubility was evaluated by means of mass loss (%) after 7 and 30 days of immersion in distilled water. VC was evaluated by micro-computed tomography, by using cavities 3 mm deep and 1 mm in diameter in acrylic resin, filled with the materials. The materials were evaluated after setting and after 7 and 30 days of immersion in distilled water. The data were submitted to analysis of variance and Tukey statistical tests (P physicochemical properties. Micro-computed tomography complements the physicochemical analysis of endodontic sealers. Copyright © 2017 American Association of Endodontists. Published by Elsevier Inc. All rights reserved.

  20. Mesoporous bioactive glass surface modified poly(lactic-co-glycolic acid) electrospun fibrous scaffold for bone regeneration.

    Science.gov (United States)

    Chen, Shijie; Jian, Zhiyuan; Huang, Linsheng; Xu, Wei; Liu, Shaohua; Song, Dajiang; Wan, Zongmiao; Vaughn, Amanda; Zhan, Ruisen; Zhang, Chaoyue; Wu, Song; Hu, Minghua; Li, Jinsong

    2015-01-01

    A mesoporous bioactive glass (MBG) surface modified with poly(lactic-co-glycolic acid) (PLGA) electrospun fibrous scaffold for bone regeneration was prepared by dip-coating a PLGA electrospun fibrous scaffold into MBG precursor solution. Different surface structures and properties were acquired by different coating times. Surface morphology, chemical composition, microstructure, pore size distribution, and hydrophilicity of the PLGA-MBG scaffold were characterized. Results of scanning electron microscopy indicated that MBG surface coating made the scaffold rougher with the increase of MBG content. Scaffolds after MBG modification possessed mesoporous architecture on the surface. The measurements of the water contact angles suggested that the incorporation of MBG into the PLGA scaffold improved the surface hydrophilicity. An energy dispersive spectrometer evidenced that calcium-deficient carbonated hydroxyapatite formed on the PLGA-MBG scaffolds after a 7-day immersion in simulated body fluid. In vitro studies showed that the incorporation of MBG favored cell proliferation and osteogenic differentiation of human mesenchymal stem cells on the PLGA scaffolds. Moreover, the MBG surface-modified PLGA (PLGA-MBG) scaffolds were shown to be capable of providing the improved adsorption/release behaviors of bone morphogenetic protein-2 (BMP-2). It is very significant that PLGA-MBG scaffolds could be effective for BMP-2 delivery and bone regeneration.

  1. Negative effect of rapidly resorbing properties of bioactive glass-ceramics as bone graft substitute in a rabbit lumbar fusion model.

    Science.gov (United States)

    Lee, Jae Hyup; Ryu, Hyun-Seung; Seo, Jun-Hyuk; Lee, Do-Yoon; Chang, Bong-Soon; Lee, Choon-Ki

    2014-03-01

    Bioactive glass-ceramics have the ability to directly bind to bones and have been widely used as bone graft substitutes due to their high osteoconductivity and biocompatibility. CaO-SiO2-P2O5-B2O3 glass-ceramics are known to have good osteoconductivity and are used as bone graft extenders. This study aimed to evaluate the effects of the resorbing properties of glass-ceramics in bone fusion after producing and analyzing three types of CaO-SiO2-P2O5-B2O3 glass-ceramics with high osteoconductivity that had enhanced resorption by having an increased B2O3 content. The three types of CaO-SiO2-P2O5-B2O3 glass-ceramics with B2O3 contents of 8.0, 9.0, and 9.5 weight % were designated and grouped as P20B80, P10B90, and P5B95, respectively. Glass-ceramic types were tested for fusion rates and bone formation by employing the lumbar 5-6 intertransverse process fusion model in 51 New Zealand male rabbits. Bioactivity was assessed by soaking in simulated body fluid (SBF). In vitro study results showed sufficient hydroxycarbonate apatite layer formation occurred for P20B80 in1 day, for P10B90 in 3 days, and for P5B95 in 5 days after soaking in SBF. For the rabbit lumbar spine posterolateral fusion model, the autograft group recorded a 100% fusion rate with levels significantly higher than those of P20B80 (29.4%), P10B90 (0%), and P5B95 (14.3%), with high resorbing properties. Resorbing property differences among the three glass-ceramic groups were not significant. Histological results showed new bone formation confirming osteoconductivity in all three types of glass-ceramics. Radiomorphometric results also confirmed the resorbing properties of the three glass-ceramic types. The high resorbing properties and osteoconductivity of porous glass-ceramics can be advantageous as no glass-ceramics remain in the body. However, their relatively fast rate of resorption in the body negatively affects their role as an osteoconductive scaffold as glass-ceramics are resorbed before bony fusion.

  2. Effect of Aminated Mesoporous Bioactive Glass Nanoparticles on the Differentiation of Dental Pulp Stem Cells.

    Directory of Open Access Journals (Sweden)

    Jung-Hwan Lee

    Full Text Available Mesoporous bioactive nanoparticles (MBNs have been developed as promising additives to various types of bone or dentin regenerative material. However, biofunctionality of MBNs as dentin regenerative additive to dental materials have rarely been studied. We investigated the uptake efficiency of MBNs-NH2 with their endocytosis pathway and the role of MBNs-NH2 in odontogenic differentiation to clarify inherent biofunctionality. MBNs were fabricated by sol-gel synthesis, and 3% APTES was used to aminate these nanoparticles (MBNs-NH2 to reverse their charge from negative to positive. To characterize the MBNs-NH2, TEM, XRD, FTIR, zeta(ξ-potential measurements, and Brunauer-Emmett-Teller analysis were performed. After primary cultured rat dental pulp stem cells (rDPSCs were incubated with various concentrations of MBNs-NH2, stem cell viability (24 hours with or without differentiated media, internalization of MBNs-NH2 in rDPSCs (~4 hours via specific endocytosis pathway, intra or extracellular ion concentration and odontoblastic differentiation (~28 days were investigated. Incubation with up to 50 μg/mL of MBNs-NH2 had no effect on rDPSCs viability with differentiated media (p>0.05. The internalization of MBNs-NH2 in rDPSCs was determined about 92% after 4 hours of incubation. Uptake was significantly decreased with ATP depletion and after 1 hour of pre-treatment with the inhibitor of macropinocytosis (p<0.05. There was significant increase of intracellular Ca and Si ion concentration in MBNs-NH2 treated cells compared to no-treated counterpart (p<0.05. The expression of odontogenic-related genes (BSP, COL1A, DMP-1, DSPP, and OCN and the capacity for biomineralization (based on alkaline phosphatase activity and alizarin red staining were significantly upregulated with MBNs-NH2. These results indicate that MBNs-NH2 induce odontogenic differentiation of rDPSCs and may serve as a potential dentin regenerative additive to dental material for promoting

  3. Theoretical and Experimental Studies of the Controlled Release of Tetracycline Incorporated into Bioactive Glasses.

    Science.gov (United States)

    Andrade, Ângela L; Militani, Isabela A; de Almeida, Katia J; Belchior, Jadson C; Dos Reis, Sérgio C; Costa E Silva, Rosangela M F; Domingues, Rosana Z

    2018-01-09

    Several authors have studied the release profile of drugs incorporated in different devices. However, to the best of our knowledge, although many studies have been done on the release of tetracycline, in these release devices, no study has investigated if the released compound is actually the tetracycline, or, instead, a degraded product. This approach is exploited here. In this work, we analyse the influence of two drying methods on the tetracycline delivery behaviour of synthesised glasses using the sol-gel process. We compare the drying methods results using both theoretical models and practical essays, and analyse the chemical characteristic of the released product in order to verify if it remains tetracycline. Samples were freeze-dried or dried in an oven at 37°C and characterised by several methods such as Fourier transform infrared spectroscopy (FTIR), scanning electron microscopy (SEM), thermogravimetric analysis (TG), differential thermogravimetric analysis (DTG), differential thermal analyses (DTA) and gas adsorption analysis (BET). The released concentration of tetracycline hydrochloride was studied as a function of time, and it was measured by ultraviolet spectrophotometry in the tetracycline wavelength. The drug delivery profiles were reasonably consistent with a diffusion model analysis. In addition, we observed higher release rates for the freeze-dried compared to those dried in an oven at 37°C. This higher release can be attributed to larger pore size for the freeze-dried sample systems with tetracycline, which promoted more water penetration, improving the drug diffusion. The analysis of the solution obtained in the release tests using high-performance liquid chromatography- mass spectrometry (HPLC-MS) confirmed that tetracycline was being released.

  4. Compósitos Bioativos Obtidos a Partir da Inserção de Vidro Bioativo em Matriz de Poli(Metacrilato de Metila Bioactive Composites Obtained from Bioactive Glass Particles into Poly(Methyl Methacrylate

    Directory of Open Access Journals (Sweden)

    Paulo E. Silva Junior

    2001-09-01

    materials in a wider range of applications. The goal of this research is to synthesize and characterize polymer matrices reinforced with bioactive glass particles that potentially can combine ability to bond to tissues (bioactivity, with mechanical properties comparable to damage tissues. The composites were produced by bulk polymerization of methyl methacrylate in the presence of bioactive glass particles and an initiator at 60ºC. Bioactive glass particles were added to the monomer in several concentrations to modify the mechanical properties and bioactivity of the composites. The bioactivity of the materials was evaluated by in vitro tests performed at 37ºC in a simulated body fluid for periods of time ranging from 1 hour to 30 days. The composites submitted to in vitro tests were characterized by infrared spectroscopy. The results revealed the deposition of a hidroxy-carbonate-apatite layer on the surface of the composites, confirming their bioactivity. It was also observed that the fraction of the bioactive phase in the composites can be used to control the overall kinetics of the bioactivity process.

  5. Enhanced bone regeneration in rat calvarial defects implanted with surface-modified and BMP-loaded bioactive glass (13-93) scaffolds

    Science.gov (United States)

    Liu, Xin; Rahaman, Mohamed N.; Liu, Yongxing; Bal, B. Sonny; Bonewald, Lynda F.

    2013-01-01

    The repair of large bone defects, such as segmental defects in the long bones of the limbs, is a challenging clinical problem. Our recent work has shown the ability to create porous scaffolds of silicate 13-93 bioactive glass by robocasting which have compressive strengths comparable to human cortical bone. The objective of this study was to evaluate the capacity of those strong porous scaffolds with a grid-like microstructure (porosity = 50%; filament width = 330 μm; pore width = 300 μm) to regenerate bone in a rat calvarial defect model. Six weeks postimplantation, the amount of new bone formed within the implants was evaluated using histomorphometric analysis. The amount of new bone formed in implants composed of the as-fabricated scaffolds was 32% of the available pore space (area). Pretreating the as-fabricated scaffolds in an aqueous phosphate solution for 1, 3, and 6 days, to convert a surface layer to hydroxyapatite prior to implantation, enhanced new bone formation to 46%, 57%, and 45%, respectively. New bone formation in scaffolds pretreated for 1, 3, and 6 days and loaded with bone morphogenetic protein-2 (BMP-2) (1 μg/defect) was 65%, 61%, and 64%, respectively. The results show that converting a surface layer of the glass to hydroxyapatite or loading the surface-treated scaffolds with BMP-2 can significantly improve the capacity of 13-93 bioactive glass scaffolds to regenerate bone in an osseous defect. Based on their mechanical properties evaluated previously and their capacity to regenerate bone found in this study, these 13-93 bioactive glass scaffolds, pretreated or loaded with BMP-2, are promising in structural bone repair. PMID:23567939

  6. Ionic extraction of a novel nano-sized bioactive glass enhances differentiation and mineralization of human dental pulp cells.

    Science.gov (United States)

    Gong, Weiyu; Huang, Zhiwei; Dong, Yanmei; Gan, Yehua; Li, Shenglin; Gao, Xuejun; Chen, Xiaofeng

    2014-01-01

    This study aimed to investigate the effects of a novel nano-sized 58S bioactive glass (nano-58S BG) on the odontogenic differentiation and mineralization of human dental pulp cells (hDPCs) in vitro. Extractions were prepared by incubating nano-58S BG, 45S5 BG, or 58S BG particulates in Dulbecco modified Eagle medium at 1% w/v for 24 hours and were filtrated through 0.22-μm filters. The supernatants were used as BG extractions. The hDPCs were cultured in nano-58S BG, 45S5 BG, and 58S BG extractions. The proliferation of hDPCs was evaluated using the methylthiazol tetrazolium assay. Odontogenic differentiation was evaluated based on the real-time polymerase chain reaction of differentiation- and mineralization-related genes, namely, alkaline phosphatase (ALP), collagen type I, dentin sialophosphoprotein (DSPP), and dentin matrix protein 1. The gene expressions were verified using ALP activity assessment, immunocytochemistry staining of osteocalcin and DSPP, and mineralization assay using alizarin red S stain. All BG extractions up-regulated the expression of odontogenic genes, and the most significant enhancement was in the nano-58S BG group. All BG extractions, especially nano-58S, increased ALP activity, osteocalcin and DSPP protein production, and mineralized nodules formation. Compared with regular BG, the novel nano-58S BG can induce the differentiation and mineralization of hDPCs more efficiently and might be a better potential candidate for dentin-pulp complex regeneration. Copyright © 2014 American Association of Endodontists. Published by Elsevier Inc. All rights reserved.

  7. Surface pre-conditioning with bioactive glass air-abrasion can enhance enamel white spot lesion remineralization.

    Science.gov (United States)

    Milly, Hussam; Festy, Frederic; Andiappan, Manoharan; Watson, Timothy F; Thompson, Ian; Banerjee, Avijit

    2015-05-01

    To evaluate the effect of pre-conditioning enamel white spot lesion (WSL) surfaces using bioactive glass (BAG) air-abrasion prior to remineralization therapy. Ninety human enamel samples with artificial WSLs were assigned to three WSL surface pre-conditioning groups (n=30): (a) air-abrasion with BAG-polyacrylic acid (PAA-BAG) powder, (b) acid-etching using 37% phosphoric acid gel (positive control) and (c) unconditioned (negative control). Each group was further divided into three subgroups according to the following remineralization therapy (n=10): (I) BAG paste (36 wt.% BAG), (II) BAG slurry (100 wt.% BAG) and (III) de-ionized water (negative control). The average surface roughness and the lesion step height compared to intra-specimen sound enamel reference points were analyzed using non-contact profilometry. Optical changes within the lesion subsurface compared to baseline scans were assessed using optical coherence tomography (OCT). Knoop microhardness evaluated the WSLs' mechanical properties. Raman micro-spectroscopy measured the v-(CO3)(2-)/v1-(PO4)(3-) ratio. Structural changes in the lesion were observed using confocal laser scanning microscopy (CLSM) and scanning electron microscopy-energy dispersive X-ray spectrometry (SEM-EDX). All comparisons were considered statistically significant if pair-abrasion removed 5.1 ± 0.6 μm from the lesion surface, increasing the WSL surface roughness. Pre-conditioning WSL surfaces with PAA-BAG air-abrasion reduced subsurface light scattering, increased the Knoop microhardness and the mineral content of the remineralized lesions (pconditioning WSL surfaces with PAA-BAG air-abrasion modified the lesion surface physically and enhanced remineralization using BAG 45S5 therapy. Copyright © 2015 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

  8. In vitro study of root fracture treated by CO2 laser and DP-bioactive glass paste.

    Science.gov (United States)

    Wang, Yin-Lin; Lee, Bor-Shiunn; Tseng, Ching-Li; Lin, Feng-Huei; Lin, Chun-Pin

    2008-01-01

    An ideal material has yet to be discovered that can successfully treat vertical root fracture. Therefore, the purpose of this study was to use a continuous-wave CO2 laser of medium-energy density to fuse DP-bioactive glass paste (DPGP) to vertical root fracture. The DP-bioglass powder was based on a Na2O-CaO-SiO2-P2O5 system and it was mixed with phosphoric acid (65% concentration) with a powder/liquid ratio of 2 g/4 mL to form DPGP. The interaction of DPGP and dentin was analyzed by means of X-ray diffractometer (XRD) and differential thermal analysis/thermogravimetric analysis (DTA/TGA). Root fracture line was filled with DPGP followed by CO2 laser irradiation and the result was examined by scanning electron microscopy (SEM). The main crystal phase of DPGP was monocalcium phosphate monohydrate (Ca(H2PO4)2.H2O) and the phase transformed to dicalcium phosphate dihydrate (CaHPO4.2H2O) after mixing DPGP with dentin powder (DPG-D). Additionally, gamma-Ca2P2O7 and beta-Ca2P2O7 were identified when DPG-D was lased by CO2 laser. The reaction temperature was between 500 degrees C and 1100 degrees C. SEM results demonstrated that the fracture line was effectively sealed by DPGP. The chemical reaction of DPGP and dentin indicated that DPGP combined with CO2 laser is a potential regimen for the treatment of vertical root fracture.

  9. Clinical and histologic evaluation of bone-replacement grafts in the treatment of localized alveolar ridge defects. Part 2: bioactive glass particulate.

    Science.gov (United States)

    Knapp, Charles I; Feuille, Frank; Cochran, David L; Mellonig, James T

    2003-04-01

    The purpose of this study was to evaluate the feasibility of using a bioactive alloplast and a physical barrier to augment localized alveolar ridge defects for the subsequent placement of dental implants. Twelve systemically healthy patients (aged 29 to 55 years) with inadequate dental alveolar ridge widths were selected for study. All patients completed initial therapy, which included scaling, root planing, and oral hygiene instruction. All ridge defects were augmented with a bioactive glass alloplast and a titanium-reinforced e-PTFE barrier. Vertical (height) and horizontal (width) hard tissue measurements were taken the day of ridge augmentation surgery (baseline) and at the 6-month reentry surgery. The change in ridge width varied from a loss of 1 mm to a gain of 4.5 mm, with a mean gain of 1.1 mm (P .08). Mean ridge width gain was 1.1 mm for both maxillary and mandibular sites. There was a loss in bone height of 0.3 mm from baseline. Four implants in four patients could not be placed because of inadequate ridge width augmentation. Histologic examination of the grafted sites revealed connective tissue encapsulation of most residual graft particles. In this study, bioactive glass particulate and an e-PTFE barrier did not consistently augment localized ridge defects for dental implant placement.

  10. Mechanical properties and drug release behavior of PCL/zein coated 45S5 bioactive glass scaffolds for bone tissue engineering application.

    Science.gov (United States)

    Fereshteh, Zeinab; Nooeaid, Patcharakamon; Fathi, Mohammadhossein; Bagri, Akbar; Boccaccini, Aldo R

    2015-09-01

    This article presents data related to the research article entitled "The effect of coating type on mechanical properties and controlled drug release of PCL/zein coated 45S5 bioactive glass scaffolds for bone tissue engineering" [1]. We provide data on mechanical properties, in vitro bioactivity and drug release of bioactive glass (BG) scaffolds coated by poly (ε-caprolactone) (PCL) and zein used as a controlled release device for tetracycline hydrochloride (TCH). By coating the BG scaffolds with PCL or PCL/zein blend the mechanical properties of the scaffolds were substantially improved, i.e., the compressive strength increased from 0.004±0.001 MPa (uncoated BG scaffolds) to 0.15±0.02 MPa (PCL/zein coated BG scaffolds). A dense bone-like apatite layer formed on the surface of PCL/zein coated scaffolds immersed for 14 days in simulated body fluid (SBF). The data describe control of drug release and in vitro degradation behavior of coating by engineering the concentration of zein. Thus, the developed scaffolds exhibit attractive properties for application in bone tissue engineering research.

  11. Research on the biological activity and doxorubicin release behavior in vitro of mesoporous bioactive SiO2-CaO-P2O5 glass nanospheres

    Science.gov (United States)

    Wang, Xiang; Wang, Gen; Zhang, Ying

    2017-10-01

    Mesoporous bioactive glass (MBG) nanospheres have been synthesized by a facile method of sacrificing template using cetyl trimethyl ammonium bromide (CTAB) as surfactant. The prepared MBG nanospheres possess high specific surface area (632 m2 g-1) as well as uniform size (∼100 nm). In addition, MBG nanospheres exhibited a quick in vitro bioactive response in simulated body fluids (SBF) and excellent bioactivity of inducing hydroxyapatite (HA) forming on the surface of MBG nanospheres. Furthermore, MBG nanospheres can sustain release of doxorubicin (DOX) with a higher encapsulation efficiency (63.6%) and show distinct degradation in PBS by releasing Si and Ca ions. The encapsulation efficiency and DOX release of MBG nanospheres could be controlled by mesoporous structure and local pH environment. The greater surface area and pore volumes of prepared MBG nanospheres are conducive to bioactive response and drug release in vitro. The amino groups in DOX can be easily protonated at acidic medium to become positively charged NH+3, which allow these drug molecules to be desorbed from the surface of MBG nanospheres via electrostatic effect. Therefore, the synthesized MBG nanospheres have a pH-sensitive drug release capability. In addition, the cytotoxicity of MBG nanospheres was assessed using a cell counting kit-8 (CCK-8), and results showed that the synthesized MBG nanospheres had no significant cytotoxicity to MC3T3 cells. These all indicated that as-prepared MBG nanospheres are promising candidates for bone tissue engineering.

  12. Comparing the Air Abrasion Cutting Efficacy of Dentine Using a Fluoride-Containing Bioactive Glass versus an Alumina Abrasive: An In Vitro Study

    Directory of Open Access Journals (Sweden)

    Melissa H. X. Tan

    2015-01-01

    Full Text Available Air abrasion as a caries removal technique is less aggressive than conventional techniques and is compatible for use with adhesive restorative materials. Alumina, while being currently the most common abrasive used for cutting, has controversial health and safety issues and no remineralisation properties. The alternative, a bioactive glass, 45S5, has the advantage of promoting hard tissue remineralisation. However, 45S5 is slow as a cutting abrasive and lacks fluoride in its formulation. The aim of this study was to compare the cutting efficacy of dentine using a customised fluoride-containing bioactive glass Na0SR (38–80 μm versus the conventional alumina abrasive (29 μm in an air abrasion set-up. Fluoride was incorporated into Na0SR to enhance its remineralisation properties while strontium was included to increase its radiopacity. Powder outflow rate was recorded prior to the cutting tests. Principal air abrasion cutting tests were carried out on pristine ivory dentine. The abrasion depths were quantified and compared using X-ray microtomography. Na0SR was found to create deeper cavities than alumina (p<0.05 despite its lower powder outflow rate and predictably reduced hardness. The sharper edges of the Na0SR glass particles might improve the cutting efficiency. In conclusion, Na0SR was more efficacious than alumina for air abrasion cutting of dentine.

  13. Silicate, borosilicate, and borate bioactive glass scaffolds with controllable degradation rate for bone tissue engineering applications. II. In vitro and in vivo biological evaluation.

    Science.gov (United States)

    Fu, Qiang; Rahaman, Mohamed N; Bal, B Sonny; Bonewald, Lynda F; Kuroki, Keiichi; Brown, Roger F

    2010-10-01

    In Part I, the in vitro degradation of bioactivAR52115e glass scaffolds with a microstructure similar to that of human trabecular bone, but with three different compositions, was investigated as a function of immersion time in a simulated body fluid. The glasses consisted of a silicate (13-93) composition, a borosilicate composition (designated 13-93B1), and a borate composition (13-93B3), in which one-third or all of the SiO2 content of 13-93 was replaced by B2O3, respectively. This work is an extension of Part I, to investigate the effect of the glass composition on the in vitro response of osteogenic MLO-A5 cells to these scaffolds, and on the ability of the scaffolds to support tissue infiltration in a rat subcutaneous implantation model. The results of assays for cell viability and alkaline phosphatase activity showed that the slower degrading silicate 13-93 and borosilicate 13-93B1 scaffolds were far better than the borate 13-93B3 scaffolds in supporting cell proliferation and function. However, all three groups of scaffolds showed the ability to support tissue infiltration in vivo after implantation for 6 weeks. The results indicate that the required bioactivity and degradation rate may be achieved by substituting an appropriate amount of SiO2 in 13-93 glass with B2O3, and that these trabecular glass scaffolds could serve as substrates for the repair and regeneration of contained bone defects. Copyright 2010 Wiley Periodicals, Inc. J Biomed Mater Res Part A, 2010.

  14. On the dissolution/reaction of small-grain Bioglass ® 45S5 and F-modified bioactive glasses in artificial saliva (AS)

    Science.gov (United States)

    Aina, Valentina; Bertinetti, Luca; Cerrato, Giuseppina; Cerruti, Marta; Lusvardi, Gigliola; Malavasi, Gianluca; Morterra, Claudio; Tacconi, Linda; Menabue, Ledi

    2011-02-01

    The reaction of small-grain Bioglass® 45S5 in artificial saliva (AS), to produce a layer of hydroxy-apatite (HA) and/or hydroxy-carbonate apatite (HCA), has been studied and compared to the results obtained in a simple buffered solution (TRIS). Some potentially bioactive glasses based on the composition of Bioglass® and containing CaF2 (HCaCaF2 5% and HNaCaF2 5%) have also been studied, in order to analyze the effects/changes produced when a F-containing glass surface is contacted with AS. The insertion of fluorine has been proposed to improve bioactive glass bone-bonding ability, and to parallel fluorine-containing glass-ceramics currently used in dentistry. ICP-OES analysis of the solution, and FTIR spectroscopy of the solid samples provided compositional information on the stages of reaction. These data were integrated with XRD and the textural and morphological data, obtained by specific surface areas determination and TEM-EDS measurements. In the case of Bioglass® 45S5, a comparison at corresponding reaction times indicates that the precipitation of an amorphous Ca-phosphate phase is faster in AS, but the crystallization of HA/HCA is delayed in AS with respect to the TRIS solution. For fluoride-containing glasses, the sample HCaCaF2 5%, in which CaF2 replaces part of CaO, possesses the fastest rate for HA/HCA crystallization (1 week) in AS. Some lines of interpretation for these results are proposed.

  15. Influence of ZnO/MgO substitution on sintering, crystallisation, and bio-activity of alkali-free glass-ceramics

    Energy Technology Data Exchange (ETDEWEB)

    Kapoor, Saurabh [Department of Materials and Ceramics Engineering, University of Aveiro, CICECO, 3810-193 Aveiro (Portugal); Goel, Ashutosh [Department of Materials Science and Engineering, Rutgers, The State University of New Jersey, Piscataway, NJ 08854-8065 (United States); Correia, Ana Filipa [Department of Materials and Ceramics Engineering, University of Aveiro, CICECO, 3810-193 Aveiro (Portugal); Pascual, Maria J. [Instituto de Cerámica y Vidrio (CSIC), Kelsen 5, Campus de Cantoblanco, 28049 Madrid (Spain); Lee, Hye-Young; Kim, Hae-Won [Institute of Tissue Regeneration Engineering (ITREN) & College of Dentistry, Dankook University, Cheonan 330714 (Korea, Republic of); Department of Nanobiomedical Science & BK21 PLUS NBM Global Research Centre for Regenerative Medicine, Dankook University, Cheonan 330714 (Korea, Republic of); Ferreira, José M.F., E-mail: jmf@ua.pt [Department of Materials and Ceramics Engineering, University of Aveiro, CICECO, 3810-193 Aveiro (Portugal)

    2015-08-01

    The present study reports on the influence of partial replacement of MgO by ZnO on the structure, crystallisation behaviour and bioactivity of alkali-free bioactive glass-ceramics (GCs). A series of glass compositions (mol%): 36.07 CaO–(19.24 − x) MgO–x ZnO–5.61 P{sub 2}O{sub 5}–38.49 SiO{sub 2}–0.59 CaF{sub 2} (x = 2–10) have been synthesised by melt–quench technique. The structural changes were investigated by solid-state magic angle spinning nuclear magnetic resonance (MAS-NMR), X-ray diffraction and differential thermal analysis. The sintering and crystallisation behaviours of glass powders were studied by hot-stage microscopy and differential thermal analysis, respectively. All the glass compositions exhibited good densification ability resulting in well sintered and mechanically strong GCs. The crystallisation and mechanical behaviour were studied under non-isothermal heating conditions at 850 °C for 1 h. Diopside was the primary crystalline phase in all the GCs followed by fluorapatite and rankinite as secondary phases. Another phase named petedunnite was identified in GCs with ZnO content > 4 mol. The proliferation of mesenchymal stem cells (MSCs) and their alkaline phosphatase activity (ALP) on GCs was revealed to be Zn-dose dependent with the highest performance being observed for 4 mol% ZnO. - Highlights: • The addition of zinc to glasses decreased T{sub g} and promoted crystallisation. • Zinc enhanced the sintering ability and increased mechanical strength by 36%. • The apatite formation ability decreased with increasing Zn contents. • Zinc stimulated mesenchymal stem cell proliferation in a dose dependent manner.

  16. Synthesis and Characterization of Poly(lactic-co-glycolic Acid Nanoparticles-Loaded Chitosan/Bioactive Glass Scaffolds as a Localized Delivery System in the Bone Defects

    Directory of Open Access Journals (Sweden)

    K. Nazemi

    2014-01-01

    Full Text Available The functionality of tissue engineering scaffolds can be enhanced by localized delivery of appropriate biological macromolecules incorporated within biodegradable nanoparticles. In this research, chitosan/58S-bioactive glass (58S-BG containing poly(lactic-co-glycolic acid (PLGA nanoparticles has been prepared and then characterized. The effects of further addition of 58S-BG on the structure of scaffolds have been investigated to optimize the characteristics of the scaffolds for bone tissue engineering applications. The results showed that the scaffolds had high porosity with open pores. It was also shown that the porosity decreased with increasing 58S-BG content. Furthermore, the PLGA nanoparticles were homogenously distributed within the scaffolds. According to the obtained results, the nanocomposites could be considered as highly bioactive bone tissue engineering scaffolds with the potential of localized delivery of biological macromolecules.

  17. Influence of 45S5 Bioactive Glass in A Standard Calcium Phosphate Collagen Bone Graft Substitute on the Posterolateral Fusion of Rabbit Spine.

    Science.gov (United States)

    Pugely, Andrew J; Petersen, Emily B; DeVries-Watson, Nicole; Fredericks, Douglas C

    2017-01-01

    Spinal fusion surgery is an effective but costly treatment for select spinal pathology. Historically iliac crest bone graft (ICBG) has remained the gold standard for achieving successful arthrodesis. Given well-established morbidity autograft harvest, multiple bone graft replacements, void fillers, and extenders have been developed. The objective of this study was to evaluate the in vivo efficacy and safety of two mineralized collagen bone void filler materials similar in composition. Both bone void fillers were composed of hydroxyapatite (HA), tricalcium phosphate (TCP) and bovine collagen. The first test article (Bi-Ostetic bioactive glass foam or "45S5") also contained 45S5 bioactive glass particles while the second test article (Formagraft or "FG") did not. 45S5 and FG were combined with bone marrow aspirate and iliac crest autograft and compared to ICBG in an established posterolateral spine fusion rabbit model. Sixty-nine mature New Zealand White rabbits were divided into 3 test cohorts: ICBG, 45S5, and FG. A Posterolateral fusion model previous validated was utilized to assess fusion efficacy. The test groups were evaluated for spine fusion rate, new bone formation, graft resorption and inflammatory response using radiographic, μCT, biomechanical and histological endpoints at 4, 8 and 12 weeks following implantation. There were 4 clinical complications unrelated to the graft materials and were evenly split between groups (ICBG graft harvest complications; hind limb mobility, chronic pain) and were euthanized. These omissions did not affect the overall outcome of the study. Radiographic scoring of the fusion sites indicated a normal healing response in all test groups, with no adverse reactions and similar progressions of new bone formation observed over time. All groups demonstrated significantly less range of motion in both flexion/extension and lateral bending compared to normal not-fused controls, which supports fusion results observed in the other

  18. Fabrication of nanocomposite mat through incorporating bioactive glass particles into gelatin/poly(ε-caprolactone) nanofibers by using Box–Behnken design

    Energy Technology Data Exchange (ETDEWEB)

    Gönen, Seza Özge, E-mail: gonens@itu.edu.tr; Erol Taygun, Melek; Aktürk, Ayşen; Küçükbayrak, Sadriye

    2016-10-01

    The current research was conducted to propose a nanocomposite material, which could be suitable to be used as a scaffold for bone tissue engineering applications. For this purpose, nanocomposite fibers of gelatin, poly(ε-caprolactone) (PCL), and bioactive glass were successfully fabricated via electrospinning process. In this context, response surface methodology based on a three-level, four-variable Box-Behnken design was adopted as an optimization tool to choose the most appropriate parameter settings to obtain the desired fiber diameter. The investigation, based on a second order polynomial model, focused on the analysis of the effect of both solution and processing parameters on the fiber diameter and its standard deviation. In optimum conditions (bioactive glass content of 7.5% (w/v), applied voltage of 25 kV, tip-to-collector distance of 12.5 cm, and flow rate of 1 mL/h), the fiber diameter was found to be 584 ± 337 nm which was in good agreement with the predicted value by the developed models (523 ± 290 nm). Analytical tools such as scanning electron microscopy, X-ray diffraction analysis, Fourier transform infrared spectroscopy, and differential thermal analyzer were used for further evaluation of the optimized nanocomposite mat. The overall results showed that nanocomposite scaffolds could be promising candidates for tissue engineering applications. - Highlights: • Nanocomposite fibers of gelatin, PCL, and bioactive glass were successfully fabricated. • Three-level, four-variable Box-Behnken design was adopted as an optimization tool. • The individual and interactive effects of the electrospinning parameters were determined. • Quadratic models were used to adjust the fiber diameter and its standard deviation.

  19. The Encapsulation of Organic Molecules and Enzymes in Sol-Gel Glasses: Novel Photoactive, Optical, Sensing and Bioactive Materials. A Review

    Science.gov (United States)

    1992-01-01

    al. (26) have been ahlc to demonstrate invertase activity in aggregates of whole yeast cells trapped in thin sol-gel films, whereas films with cell...the sol-gel proc,:ss, first in’:%ducci i-i 19F,4, opened the road for a whole new class of materials anJ to ja. :. activity in many laboratories. rhc...developed based on the doping idea, namely, chemically active sol-gel glasses Catalysts, sensors and the exciting group of bioactive materials, are some

  20. Delivery of dimethyloxallyl glycine in mesoporous bioactive glass scaffolds to improve angiogenesis and osteogenesis of human bone marrow stromal cells.

    Science.gov (United States)

    Wu, Chengtie; Zhou, Yinghong; Chang, Jiang; Xiao, Yin

    2013-11-01

    Development of hypoxia-mimicking bone tissue engineering scaffolds is of great importance in stimulating angiogenesis for bone regeneration. Dimethyloxallyl glycine (DMOG) is a cell-permeable, competitive inhibitor of hypoxia-inducible factor prolyl hydroxylase (HIF-PH), which can stabilize hypoxia-inducible factor 1α (HIF-1α) expression. The aim of this study was to develop hypoxia-mimicking scaffolds by delivering DMOG in mesoporous bioactive glass (MBG) scaffolds and to investigate whether the delivery of DMOG could induce a hypoxic microenvironment for human bone marrow stromal cells (hBMSC). MBG scaffolds with varied mesoporous structures (e.g. surface area and mesopore volume) were prepared by controlling the contents of mesopore-template agent. The composition, large-pore microstructure and mesoporous properties of MBG scaffolds were characterized. The effect of mesoporous properties on the loading and release of DMOG in MBG scaffolds was investigated. The effects of DMOG delivery on the cell morphology, cell viability, HIF-1α stabilization, vascular endothelial growth factor (VEGF) secretion and bone-related gene expression (alkaline phosphatase, ALP; osteocalcin, OCN; and osteopontin, OPN) of hBMSC in MBG scaffolds were systematically investigated. The results showed that the loading and release of DMOG in MBG scaffolds can be efficiently controlled by regulating their mesoporous properties via the addition of different contents of mesopore-template agent. DMOG delivery in MBG scaffolds had no cytotoxic effect on the viability of hBMSC. DMOG delivery significantly induced HIF-1α stabilization, VEGF secretion and bone-related gene expression of hBMSC in MBG scaffolds in which DMOG counteracted the effect of HIF-PH and stabilized HIF-1α expression under normoxic condition. Furthermore, it was found that MBG scaffolds with slow DMOG release significantly enhanced the expression of bone-related genes more than those with instant DMOG release. The results

  1. Atomic-scale models of early-stage alkali depletion and SiO2-rich gel formation in bioactive glasses.

    Science.gov (United States)

    Tilocca, Antonio

    2015-01-28

    Molecular dynamics simulations of Na(+)/H(+)-exchanged 45S5 Bioglass® models reveal that a large fraction of the hydroxyl groups introduced into the proton-exchanged, hydrated glass structure do not initially form covalent bonds with Si and P network formers but remain free and stabilised by the modifier metal cations, whereas substantial Si-OH and P-OH bonding is observed only at higher Na(+)/H(+) exchange levels. The strong affinity between free OH groups and modifier cations in the highly fragmented 45S5 glass structure appears to represent the main driving force for this effect. This suggests an alternative direct route for the formation of a repolymerised silica-rich gel in the early stages of the bioactive mechanism, not considered before, which does not require sequential repeated breakings of Si-O-Si bonds and silanol condensations.

  2. New generation poly(ε-caprolactone)/gel-derived bioactive glass composites for bone tissue engineering: Part I. Material properties.

    Science.gov (United States)

    Dziadek, Michal; Menaszek, Elzbieta; Zagrajczuk, Barbara; Pawlik, Justyna; Cholewa-Kowalska, Katarzyna

    2015-11-01

    Poly(ε-caprolactone) (PCL) based composite films containing 12 and 21vol.% bioactive glass (SBG) microparticles were prepared by solvent casting method. Two gel-derived SBGs of SiO2-CaO-P2O5 system differing in SiO2 and CaO contents were applied (mol%): S2: 80SiO2, 16CaO, 4P2O5 and A2: 40SiO2, 54CaO, 6P2O5. The surfaces of the films in contact with Petri dish and exposed to the gas phase during casting were denoted as GS and AS, respectively. Both surfaces of films were characterised in terms of their morphology, micro- and nano-topography as well as wettability. Also mechanical properties (tensile strength, Young's modulus) and PCL matrix crystallinity (degree of crystallinity, crystal size) were evaluated. Degradation behaviour was examined by incubation of materials in UHQ-water at 37°C for 56weeks. The crystallinity, melting temperature and mass loss of incubated materials and pH changes of water were monitored. Furthermore, proliferation of MG-63 osteoblastic cells by direct contact and cytotoxic effect of obtained materials were investigated. Results showed that opposite surfaces of the same polymer and composite films differ in studied surface parameters. The addition of SBG particles into PCL matrix improves nano- and micro-roughness of both surfaces, enhances the hydrophilicity of GS surfaces (~67° for 21A2-PCL compared to ~78° for pure PCL) and also makes AS surface more hydrophobic (~94° for 21S2-PCL compared to ~86° for pure PCL). The nucleation density of PCL was increased with increasing content of SBG particles, which results in the large number of fine spherulites on composite AS surfaces observed using polarized optical (POM), scanning electron (SEM), and atomic force (AFM) microscopies. Higher content of SBG particles causes a notable increase of Young's modulus (from 0.38GPa for pure PCL, 0.90GPa for 12A2-PCL to 1.31GPa for 21A2-PCL), which also depends on SBG chemical composition. After 56-week degradation test, considerably higher

  3. Compositional and microstructural design of highly bioactive P2O5-Na2O-CaO-SiO2 glass-ceramics.

    Science.gov (United States)

    Peitl, Oscar; Zanotto, Edgar D; Serbena, Francisco C; Hench, Larry L

    2012-01-01

    Bioactive glasses having chemical compositions between 1Na(2)O-2CaO-3SiO(2) (1N2C3S) and 1.5Na(2)O-1.5CaO-3SiO(2) (1N1C2S) containing 0, 4 and 6 wt.% P(2)O(5) were crystallized through two stage thermal treatments. By carefully controlling these treatments we separately studied the effects on the mechanical properties of two important microstructural features not studied before, crystallized volume fraction and crystal size. Fracture strength, elastic modulus and indentation fracture toughness were measured as a function of crystallized volume fraction for a constant crystal size. Glass-ceramics with a crystalline volume fraction between 34% and 60% exhibited a three-fold improvement in fracture strength and an increase of 40% in indentation fracture toughness compared with the parent glass. For the optimal crystalline concentration (34% and 60%) these mechanical properties were then measured for different grain sizes, from 5 to 21 μm. The glass-ceramic with the highest fracture strength and indentation fracture toughness was that with 34% crystallized volume fracture and 13 μm crystals. Compared with the parent glass, the average fracture strength of this glass-ceramic was increased from 80 to 210 MPa, and the fracture toughness from 0.60 to 0.95 MPa.m(1/2). The increase in indentation fracture toughness was analyzed using different theoretical models, which demonstrated that it is due to crack deflection. Fortunately, the elastic modulus E increased only slightly; from 60 to 70 GPa (the elastic modulus of biomaterials should be as close as possible to that of cortical bone). In summary, the flexural strength of our best material (215 MPa) is significantly greater than that of cortical bone and comparable with that of apatite-wollastonite (A/W) bioglass ceramics, with the advantage that it shows a much lower elastic modulus. These results thus provide a relevant guide for the design of bioactive glass-ceramics with improved microstructure. Copyright © 2011 Acta

  4. In vivo evaluation of bioactive glass-based coatings on dental implants in a dog implantation model

    NARCIS (Netherlands)

    Oirschot, B.A.J.A. van; Alghamdi, H.S.A.; Narhi, T.O.; Anil, S.; Al Farraj Aldosari, A.; Beucken, J.J.J.P van den; Jansen, J.A.

    2014-01-01

    OBJECTIVES: Although titanium is commonly used as a favorable bone implant material due to its mechanical properties, its bioactive and osteoconductive capacity is relatively low. Calcium phosphate ceramics, predominantly hydroxyapatite (HA), have been frequently used for coating purposes to improve

  5. Quantifying the mode II critical strain energy release rate of borate bioactive glass coatings on Ti6Al4V substrates.

    Science.gov (United States)

    Matinmanesh, A; Li, Y; Clarkin, O; Zalzal, P; Schemitsch, E H; Towler, M R; Papini, M

    2017-11-01

    Bioactive glasses have been used as coatings for biomedical implants because they can be formulated to promote osseointegration, antibacterial behavior, bone formation, and tissue healing through the incorporation and subsequent release of certain ions. However, shear loading on coated implants has been reported to cause the delamination and loosening of such coatings. This work uses a recently developed fracture mechanics testing methodology to quantify the critical strain energy release rate under nearly pure mode II conditions, G IIC , of a series of borate-based glass coating/Ti6Al4V alloy substrate systems. Incorporating increasing amounts of SrCO 3 in the glass composition was found to increase the G IIC almost twofold, from 25.3 to 46.9J/m 2 . The magnitude and distribution of residual stresses in the coating were quantified, and it was found that the residual stresses in all cases distributed uniformly over the cross section of the coating. The crack was driven towards, but not into, the glass/Ti6Al4V substrate interface due to the shear loading. This implied that the interface had a higher fracture toughness than the coating itself. Copyright © 2017 Elsevier Ltd. All rights reserved.

  6. Glasses

    DEFF Research Database (Denmark)

    Dyre, Jeppe

    2004-01-01

    The temperature dependence of the viscosity of most glassforming liquids is known to depart significantly from the classical Arrhenius behaviour of simple fluids. The discovery of an unexpected correlation between the extent of this departure and the Poisson ratio of the resulting glass could lead...... to new understanding of glass ageing and viscous liquid dynamics....

  7. Developing surface pre-treatments for electrophoretic deposition of biofunctional chitosan-bioactive glass coatings on a WE43 magnesium alloy

    Science.gov (United States)

    Höhlinger, Michael; Heise, Svenja; Wagener, Victoria; Boccaccini, Aldo R.; Virtanen, Sannakaisa

    2017-05-01

    The use of Mg alloys as biodegradable implants requires optimizing the surface performance. A high number of surface modification and coating approaches have been previously explored, for instance to make magnesium and its alloys more corrosion resistant. The current study focuses on developing surface pre-treatments as a corrosion protection and primer for further surface modifications by electrophoretic deposition (EPD) of bioadaptive chitosan-bioactive glass coatings. For this, different surface treatments were tested on a WE43 Mg alloy. These treatments include immersion in Dulbecco's Modified Eagle's Medium (DMEM), a calcium phosphate treatment, immersion in hydrofluoric acid, and a hydrothermal procedure in NaOH. The resulting coatings were analyzed in view of the surface morphology and composition by SEM/EDX, as well as in view of their short-term corrosion protection ability by electrochemistry. Finally, the suitability of the different pre-treatments as an interfacial protection layer for subsequent EPD of a chitosan/bioactive glass-coating was explored.

  8. Multifunctional Chitosan-45S5 Bioactive Glass-Poly(3-hydroxybutyrate-co-3-hydroxyvalerate) Microsphere Composite Membranes for Guided Tissue/Bone Regeneration.

    Science.gov (United States)

    Li, Wei; Ding, Yaping; Yu, Shanshan; Yao, Qingqing; Boccaccini, Aldo R

    2015-09-23

    Novel multifunctional chitosan-45S5 bioactive glass-poly(3-hydroxybutyrate-co-3-hydroxyvalerate) (PHBV) microsphere (CS-BG-MS) composite membranes were developed with applicability in guided tissue/bone regeneration (GTR/GBR). The incorporation of 45S5 BG and PHBV MS into CS membranes not only provided the membranes with favorable surface roughness, hydrophilicity, and flexibility but also slowed down their degradation rate. Moreover, the CS membranes became bioactive after the incorporation of 45S5 BG and capable of releasing drugs of different physicochemical properties in a controlled and sustained manner with the addition of PHBV MS. Cell culture tests showed that osteoblast-like MG-63 human osteosarcoma cells had significantly higher adhesion, cell proliferation, and alkaline phosphatase (ALP) activity on CS-BG and CS-BG-MS membranes than on neat CS membranes. Therefore, the developed bioactive CS-BG-MS membranes with potential multidrug (e.g., antibacterial and antiosteoporosis drugs) delivery capability are promising candidate membranes for GTR/GBR applications.

  9. Gene delivery nanocarriers of bioactive glass with unique potential to load BMP2 plasmid DNA and to internalize into mesenchymal stem cells for osteogenesis and bone regeneration

    Science.gov (United States)

    Kim, Tae-Hyun; Singh, Rajendra K.; Kang, Min Sil; Kim, Joong-Hyun; Kim, Hae-Won

    2016-04-01

    The recent development of bioactive glasses with nanoscale morphologies has spurred their specific applications in bone regeneration, for example as drug and gene delivery carriers. Bone engineering with stem cells genetically modified with this unique class of nanocarriers thus holds great promise in this avenue. Here we report the potential of the bioactive glass nanoparticle (BGN) system for the gene delivery of mesenchymal stem cells (MSCs) targeting bone. The composition of 15% Ca-added silica, proven to be bone-bioactive, was formulated into surface aminated mesoporous nanospheres with enlarged pore sizes, to effectively load and deliver bone morphogenetic protein-2 (BMP2) plasmid DNA. The enlarged mesopores were highly effective in loading BMP2-pDNA with an efficiency as high as 3.5 wt% (pDNA w.r.t. BGN), a level more than twice than for small-sized mesopores. The BGN nanocarriers released the genetic molecules in a highly sustained manner (for as long as 2 weeks). The BMP2-pDNA/BGN complexes were effectively internalized to rat MSCs with a cell uptake level of ~73%, and the majority of cells were transfected to express the BMP2 protein. Subsequent osteogenesis of the transfected MSCs was demonstrated by the expression of bone-related genes, including bone sialoprotein, osteopontin, and osteocalcin. The MSCs transfected with BMP2-pDNA/BGN were locally delivered inside a collagen gel to the target calvarium defects. The results showed significantly improved bone regeneration, as evidenced by the micro-computed tomographic, histomorphometric and immunohistochemical analyses. This study supports the excellent capacity of the BGN system as a pDNA-delivery nanocarrier in MSCs, and the engineered system, BMP2-pDNA/BGN with MSCs, may be considered a new promising candidate to advance the therapeutic potential of stem cells through genetic modification, targeting bone defects and diseases.The recent development of bioactive glasses with nanoscale morphologies has

  10. SYNTHESIS, CHARACTERIZATION AND BIOLOGICAL EVALUATION OF SOL–GEL DERIVED NANOMATERIAL IN THE TERNARY SYSTEM 64 % SiO2 - 31 % CaO - 5 % P2O5 AS A BIOACTIVE GLASS: IN VITRO STUDY

    Directory of Open Access Journals (Sweden)

    Bizari D.

    2013-09-01

    Full Text Available In this study, we performed a new bioactive glass formulation with the molar composition 64 % SiO2 - 31 % CaO - 5 % P2O5 by the sol-gel method. Sol-gel derived bioglass material was produced in nanopowder using planetary milling machine, followed by sintering at 700°C, for applications as bioactive material in bioactive scaffolds or in orthopaedic. The obtained material was evaluated by X-ray powder diffraction (XRD, thermal gravimetric analysis (TGA, differential scanning calorimetry (DSC analyses, Fourier transform infrared spectroscopy (FTIR, scanning electron microscope (SEM and nitrogen adsorption pore size. The biocompatibility evaluation of the formed glass was assessed through in vitro cell culture by evaluation of alkaline phosphatase activity of osteoblasts and immersion studies in simulated body fluid (SBF for different time intervals while monitoring the pH changes and the concentration of calcium, phosphorus and silicon in the SBF medium as key factors in the rapid bonding of this bioactive glass to bone tissue as a high bioactive glass. The present investigation revealed that the sol-gel derived ternary bioglass system has the ability to support the growth of human fetal osteoblastic cells (hFOB 1.19. Finally, this material proved to be non-toxic and compatible for the proposed work in segmental defects in the goat model in vivo.

  11. In vitro bioactivity of soda lime borate glasses with substituted SrO in sodium phosphate solution

    Directory of Open Access Journals (Sweden)

    Mohamed A. Marzouk

    2014-09-01

    Full Text Available Borate glasses with the basic composition 0.6B2O3·0.2Na2O·0.2CaO and SrO progressively substituting CaO were prepared and characterized for their bone-bonding ability. The obtained glasses were thermally treated and converted to their glass-ceramic derivatives. In this study, FTIR spectral analyses were done for the prepared glasses and glass-ceramics before and after immersion in a sodium phosphate solution for extended times. The appearance of two IR bands within the spectral range 550–680 cm-1 after immersion confirms the formation of hydroxyapatite. X-ray diffraction studies and scanning electron microscope analysis supported the obtained infrared spectroscopy results. The solubility test (measurements of the weight loss in aqueous sodium phosphate solution was conducted for measuring the dissolution of both glassy and crystalline derivatives to find out the role of SrO. The corrosion behaviour of the glasses and glass-ceramics indicate the increase of weight loss with the increase of SrO content. Different suggested proposals were introduced to explain this abnormal behaviour.

  12. glasses

    Indian Academy of Sciences (India)

    several applications. Some of the possible applications are optical amplifiers in telecommunication,7 phosphorescence materials and electrochemical batteries.8 Rare earth metal ions when added to borate act as network modifiers and change the properties of glasses .... where R is the universal gas constant. 3.3 Electrical ...

  13. Systematic evaluation of the osteogenic capacity of low-melting bioactive glass-reinforced 45S5 Bioglass porous scaffolds in rabbit femoral defects.

    Science.gov (United States)

    Zhang, Lei; Ke, Xiurong; Lin, Lingzhi; Xiao, Jun; Yang, Xianyan; Wang, Juncheng; Yang, Guojing; Xu, Sanzhong; Gou, Zhongru; Shi, Zhanjun

    2017-06-07

    Due to the low strength and high brittleness of 45S5 Bioglass ® , it is still a great challenge for the three-dimensional porous 45S5 Bioglass ® to treat mechanically required loaded bone defects. Therefore, 45S5 Bioglass ® -derived bioactive glass-ceramic (BGC) porous scaffolds were fabricated at a low temperature sintering condition with and without the addition of 4% low-melting ZnO/B 2 O 3 (ZB) bioactive glass as a reinforcing agent and using 350- or 500 μm paraffin microspheres as a porogen. The pore structure characterization for the scaffolds indicated that the scaffolds containing 4% ZB had very good macroporous structures of ∼313 and ∼448 μm in pore size and over 70% porosity with appreciable strength (>15 MPa), which was about four times higher than that those manufactured without ZB and with 350 μm porogen scaffolds. The open porosity was decreased with the addition of 4% ZB but the interconnected pore percentage (>50 μm) was increased with increasing the porogen size from 350 to 500 μm. In vivo investigations revealed that the stronger scaffolds containing 4% ZB and 500 μm porogen were particularly beneficial for osteogenic capacity in critical size femoral bone defects, accompanied with an accelerated bone ingrowth (6-18 weeks) and the material itself experiencing mild resorption. In contrast, both the scaffolds with smaller pore sizes exhibited a low level of new bone ingrowth (Bioglass ® -derived BGC scaffolds in a clinical setting, especially for mechanically loaded bone defects.

  14. Inhibition of enamel demineralization and bond-strength properties of bioactive glass containing 4-META/MMA-TBB-based resin adhesive.

    Science.gov (United States)

    Kohda, Naohisa; Iijima, Masahiro; Kawaguchi, Kyotaro; Toshima, Hirokazu; Muguruma, Takeshi; Endo, Kazuhiko; Mizoguchi, Itaru

    2015-06-01

    We investigated the enamel demineralization-prevention ability and shear bond strength (SBS) properties of 4-methacryloxyethyl trimellitic anhydride/methyl methacrylate-tri-n-butyl borane (4-META/MMA-TBB)-based resin containing various amounts (0-50%) of bioactive glass (BG). Disk-shaped specimens were immersed in distilled water and ions released were analysed by inductively coupled plasma atomic-emission spectroscopy. Samples were also immersed in lactic acid solution (pH 4.6) to estimate acid-neutralizing ability. Brackets were bonded to human premolars with BG-containing resins and the bonded teeth were alternately immersed in demineralizing (pH 4.55) and remineralizing (pH 6.8) solutions for 14 d. The enamel hardness was determined by nanoindentation testing at twenty equidistant distances from the external surface. The SBS for each sample was examined. The amounts of ions released [calcium (Ca), sodium (Na), silicon (Si), and boron (B)] and the acid-neutralizing ability increased with increasing BG content. After alternating immersion, the specimens bonded with the BG-containing resin with high BG content were harder than those in the other groups in some locations 1-18.5 μm from the enamel surface. Bioactive glass-containing (10-40%) resin had bond strength equivalent to the control specimen. Thus, the SBS obtained for BG-containing resin (6.5-9.2 MPa) was clinically acceptable, suggesting that this material has the ability to prevent enamel demineralization. © 2015 Eur J Oral Sci.

  15. The influence of polymeric component of bioactive glass-based nanocomposite paste on its rheological behaviors and in vitro responses: hyaluronic acid versus sodium alginate.

    Science.gov (United States)

    Sohrabi, Mehri; Hesaraki, Saeed; Kazemzadeh, Asghar

    2014-04-01

    Different biocomposite pastes were prepared from a solid phase that was nanoparticles of sol-gel-derived bioactive glass and different liquid phases including 3% hyaluronic acid solution, sodium alginate solutions (3% and 10 %) or mixtures of hyaluronic acid and sodium alginate (3% or 10 %) solutions in 50:50 volume ratio. Rheological properties of the pastes were measured in both rotatory and oscillatory modes. The washout behavior and in vitro apatite formation of the pastes were determined by soaking them in simulated body fluid under dynamic situation for 14 days. The proliferation and alkaline phosphatase activity of MG-63 osteoblastic cells were also determined using extracts of the pastes. All pastes could be easily injected from the standard syringes with different tip diameters. All pastes exhibited visco-elastic character, but a nonthixotropic paste was obtained using hyaluronic acid in which the loss modulus was higher than the storage modulus. The thixotropy and storage modulus were increasingly improved by adding/using sodium alginate as mixing liquid. Moreover, the pastes in which the liquid phase was sodium alginate or mixture of hyaluronic acid and 10% sodium alginate solution revealed better apatite formation ability and washout resistance than that made of hyaluronic acid alone. No cytotoxicity effects were observed by extracts of the pastes on osteoblasts but better alkaline phosphatase activity was found for the pastes containing hyaluronic acid. Overall, injectable biocomposites can be produced by mixing bioactive glass nanoparticles and sodium alginate/hyaluronic acid polymers. They are potentially useful for hard and even soft tissues treatments. Copyright © 2013 Wiley Periodicals, Inc.

  16. Strontium-containing mesoporous bioactive glass scaffolds with improved osteogenic/cementogenic differentiation of periodontal ligament cells for periodontal tissue engineering.

    Science.gov (United States)

    Wu, Chengtie; Zhou, Yinghong; Lin, Chucheng; Chang, Jiang; Xiao, Yin

    2012-10-01

    To achieve the ultimate goal of periodontal tissue engineering, it is of great importance to develop bioactive scaffolds which can stimulate the osteogenic/cementogenic differentiation of periodontal ligament cells (PDLCs) for the favorable regeneration of alveolar bone, root cementum and periodontal ligament. Strontium (Sr) and Sr-containing biomaterials have been found to induce osteoblast activity. However, there has been no systematic report about the interaction between Sr or Sr-containing biomaterials and PDLCs for periodontal tissue engineering. The aims of this study were to prepare Sr-containing mesoporous bioactive glass (Sr-MBG) scaffolds and investigate whether the addition of Sr could stimulate osteogenic/cementogenic differentiation of PDLCs in a tissue-engineering scaffold system. The composition, microstructure and mesopore properties (specific surface area, nanopore volume and nanopore distribution) of Sr-MBG scaffolds were characterized. The proliferation, alkaline phosphatase (ALP) activity and osteogenesis/cementogenesis-related gene expression (ALP, Runx2, Col I, OPN and CEMP1) of PDLCs on different kinds of Sr-MBG scaffolds were systematically investigated. The results show that Sr plays an important role in influencing the mesoporous structure of MBG scaffolds in which high contents of Sr decreased the well-ordered mesopores as well as their surface area/pore volume. Sr(2+) ions could be released from Sr-MBG scaffolds in a controlled way. The incorporation of Sr into MBG scaffolds has significantly stimulated ALP activity and osteogenesis/cementogenesis-related gene expression of PDLCs. Furthermore, Sr-MBG scaffolds in a simulated body fluid environment still maintained excellent apatite-mineralization ability. The study suggests that the incorporation of Sr into MBG scaffolds is a viable way to stimulate the biological response of PDLCs. Sr-MBG scaffolds are a promising bioactive material for periodontal tissue-engineering applications

  17. Preparation and In Vitro Biological Evaluation of Octacalcium Phosphate/Bioactive Glass-Chitosan/ Alginate Composite Membranes Potential for Bone Guided Regeneration.

    Science.gov (United States)

    Xu, Sanzhong; Chen, Xiaoyi; Yang, Xianyan; Zhang, Lei; Yang, Guojing; Shao, Huifeng; He, Yong; Gou, Zhongru

    2016-06-01

    The chitosan/alginate-trace element-codoped octacalcium phosphate/nano-sized bioactive glass (CS/ALG-teOCP/nBG) composite membranes were prepared by a layer-by-layer coating method for the functional requirement of guided bone regeneration (GBR). The morphology, mechanical properties and moisture content of the membranes was studied by scanning electron microscopy (SEM) observation, mechanical and swelling test. The results showed that the teOCP/nBG distributed uniformly in the composite membranes, and such as-prepared composite membrane exhibited an excellent tensile strength, accompanying with mechanical decay with immersion in aqueous medium. Cell culture and MTT assays showed that the surface microstructure and the ion dissolution products from teOCP/nBG components could enhance the cell proliferation, and especially the composite membranes was suitable for supporting the adhesion and growth behavior of human bone marrow mesenchymal stem cells (hBMSCs) in comparison with the CS/ALG pure polymer membranes. These results suggest that the new CS/ALG-teOCP/nBG composite membrane is highly bioactive and biodegradable, and favorable for guiding bone regeneration.

  18. In vitro investigations on CoO doped CaF2sbnd CaOsbnd B2O3sbnd P2O5-MO bioactive glasses by means of spectroscopic studies

    Science.gov (United States)

    Sobhanachalam, P.; Ravi Kumar, V.; Raghavaiah, B. V.; Ravi Kumar, Valluri; Sahaya Baskaran, G.; Gandhi, Y.; Syam Prasad, P.; Veeraiah, N.

    2017-11-01

    In this investigation we have synthesized CaF2sbnd CaOsbnd B2O3sbnd P2O5: CoO glasses mixed with different therapeutically active ions viz., Ba2+, Sr2+, Mg2+ and Zn2+ (that play a vital role in the normal functioning of human body) and performed in vitro bioactivity studies by immersing them in simulated body fluid (SBF) for a period of about a month and the obtained results were analyzed using spectroscopic studies. Due to immersion in SBF solution, a thin layer of hydroxy apatite (HAp) is developed on the surface of the samples. The results of XRD, SEM and also IR spectra have confirmed that the layer deposited on the surface of the samples is crystalline HAp mixed with cobalt ions. The quantitative analysis of the results in vitro bioactive studies with the help of optical absorption and IR spectral studies have indicated that BaO is an efficient modifier in accelerating the HAp growth. The cobalt ions are found to be in tetrahedral positions and participated in the glass network with BO4 and PO4 structural units in larger quantities in CoZn and CoMg glasses and such occupancy is found to be the reason for the relatively low bioactive efficiency of these glasses when compared with that of CoBa glass.

  19. In vitro response of human osteoblasts to multi-step sol–gel derived bioactive glass nanoparticles for bone tissue engineering

    Energy Technology Data Exchange (ETDEWEB)

    Fan, Jian Ping, E-mail: jian.fan@ucl.ac.uk [Department of Mechanical Engineering, University College London, London WC1E 7JE (United Kingdom); Kalia, Priya; Di Silvio, Lucy [Biomaterials, Tissue Engineering and Imaging, The Dental Institute, King' s College London, Guy' s Hospital, London SE1 9BT (United Kingdom); Huang, Jie [Department of Mechanical Engineering, University College London, London WC1E 7JE (United Kingdom)

    2014-03-01

    A multi-step sol–gel process was employed to synthesize bioactive glass (BG) nanoparticles. Transmission electron microscopy (TEM) revealed that the BG nanoparticles were spherical and ranged from 30 to 60 nm in diameter. In vitro reactivity of the BG nanoparticles was tested in phosphate buffer saline (PBS), Tris-buffer (TRIS), simulated body fluid (SBF), and Dulbecco's modified Eagle's medium (DMEM), in comparison with similar sized hydroxyapatite (HA) and silicon substituted HA (SiHA) nanoparticles. Bioactivity of the BG nanoparticles was confirmed through Fourier transform infrared spectroscopy (FTIR) analysis. It was found that bone-like apatite was formed after immersion in SBF at 7 days. Solutions containing BG nanoparticles were slightly more alkaline than HA and SiHA, suggesting that a more rapid apatite formation on BG was related to solution-mediated dissolution. Primary human osteoblast (HOB) cell model was used to evaluate biological responses to BG nanoparticles. Lactate dehydrogenase (LDH) cytotoxicity assay showed that HOB cells were not adversely affected by the BG nanoparticles throughout the 7 day test period. Interestingly, MTS assay results showed an enhancement in cell proliferation in the presence of BG when compared to HA and SiHA nanoparticles. Particularly, statistically significant (p < 0.05) alkaline phosphatase (ALP) activity of HOB cells was found on the culture containing BG nanoparticles, suggesting that the cell differentiation might be promoted by BG. Real-time quantitative PCR analysis (qPCR) further confirmed this finding, as a significantly higher level of RUNX2 gene expression was recorded on the cells cultured in the presence of BG nanoparticles when compared to those with HA and SiHA. - Highlights: • Spherical bioactive glass nanoparticles (BG) under 60 nm were synthesized. • An alkali morphological catalyst was used in the synthesis. • Cytotoxicity assays demonstrated that BG was not cytotoxic towards HOB

  20. Bioactive glass-ceramic coatings prepared by pulsed laser deposition from RKKP targets (sol-gel vs melt-processing route)

    Energy Technology Data Exchange (ETDEWEB)

    Rau, J.V., E-mail: giulietta.rau@ism.cnr.it [Istituto di Struttura della Materia, Consiglio Nazionale delle Ricerche, Via del Fosso del Cavaliere, 100-00133 Rome (Italy); Teghil, R. [Universita della Basilicata, Dipartimento di Chimica ' A.M. Tamburro' , Via dell' Ateneo Lucano, 10-85100 Potenza (Italy); CNR-IMIP U.O.S. di Potenza, Zona Industriale di Tito scalo (PZ) (Italy); Fosca, M. [Istituto di Struttura della Materia, Consiglio Nazionale delle Ricerche, Via del Fosso del Cavaliere, 100-00133 Rome (Italy); Universita di Roma ' La Sapienza' , Dipartimento di Chimica, Piazzale Aldo Moro, 5-00185 Rome (Italy); De Bonis, A. [Universita della Basilicata, Dipartimento di Chimica ' A.M. Tamburro' , Via dell' Ateneo Lucano, 10-85100 Potenza (Italy); CNR-IMIP U.O.S. di Potenza, Zona Industriale di Tito scalo (PZ) (Italy); Cacciotti, I.; Bianco, A. [Universita di Roma ' Tor Vergata' , Dipartimento di Ingegneria Industriale, UR INSTM ' Roma Tor Vergata' , Via del Politecnico, 1-00133 Rome (Italy); Albertini, V. Rossi [Istituto di Struttura della Materia, Consiglio Nazionale delle Ricerche, Via del Fosso del Cavaliere, 100-00133 Rome (Italy); Caminiti, R. [Universita di Roma ' La Sapienza' , Dipartimento di Chimica, Piazzale Aldo Moro, 5-00185 Rome (Italy); Ravaglioli, A. [Parco Torricelli delle Arti e delle Scienze, Via Granarolo, 64-48018 Faenza (Ra) (Italy)

    2012-05-15

    Highlights: Black-Right-Pointing-Pointer Bioactive glass-ceramic coatings for bone tissue repair and regeneration. Black-Right-Pointing-Pointer Pulsed Lased Deposition allowed congruent transfer of target composition to coating. Black-Right-Pointing-Pointer Target was prepared by sol-gel process suitable for compositional tailoring. Black-Right-Pointing-Pointer Titanium, widely used for orthopaedics and dental implants, was used as substrate. Black-Right-Pointing-Pointer The physico-chemical properties of the prepared coatings are reported. -- Abstract: The deposition of innovative glass-ceramic composition (i.e. RKKP) coatings by Pulsed Lased Deposition (PLD) technique is reported. RKKP was synthesised following two methodologies: melt-processing and sol-gel, the latter being particularly suitable to tailor the compositional range. The PLD advantage with respect to other deposition techniques is the congruent transfer of the target composition to the coating. The physico-chemical properties of films were investigated by Scanning Electron and Atomic Force Microscopies, Fourier Transform Infrared Spectroscopy, Angular and Energy Dispersive X-ray Diffraction, and Vickers microhardness. The deposition performed at 12 J/cm{sup 2} and 500 Degree-Sign C allows to prepare crystalline films with the composition that replicates rather well that of the initial targets. The 0.6 {mu}m thin melt-processing RKKP films, possessing the hardness of 25 GPa, and the 4.3 {mu}m thick sol-gel films with the hardness of 17 GPa were obtained.

  1. In vitro and in vivo bone formation potential of surface calcium phosphate-coated polycaprolactone and polycaprolactone/bioactive glass composite scaffolds.

    Science.gov (United States)

    Poh, Patrina S P; Hutmacher, Dietmar W; Holzapfel, Boris M; Solanki, Anu K; Stevens, Molly M; Woodruff, Maria A

    2016-01-01

    In this study, polycaprolactone (PCL)-based composite scaffolds containing 50wt% of 45S5 Bioglass(®) (45S5) or strontium-substituted bioactive glass (SrBG) particles were fabricated into scaffolds using an additive manufacturing technique for bone tissue engineering purposes. The PCL scaffolds were surface coated with calcium phosphate (CaP) to enable further comparison of the osteoinductive potential of different scaffolds: PCL (control), PCL/CaP-coated, PCL/50-45S5 and PCL/50-SrBG scaffolds. The PCL/50-45S5 and PCL/50-SrBG composite scaffolds were reproducibly manufactured with a morphology highly resembling that of PCL only scaffolds. However, 50wt% loading of the bioactive glass (BG) particles into the PCL bulk decreased the scaffold's compressive Young's modulus. Coating of PCL scaffolds with CaP had a negligible effect on the scaffold's porosity and compressive Young's modulus. When immersed in culture media, BG dissolution ions (Si and Sr) were detected for up to 10weeks in the immersion media and surface precipitates were formed on both PCL/50-45S5 and PCL/50-SrBG scaffolds' surfaces, indicating good in vitro bioactivity. In vitro cell studies were conducted using sheep bone marrow stromal cells (BMSCs) under non-osteogenic or osteogenic conditioned media, and under static or dynamic culture environments. All scaffolds were able to support cell adhesion, growth and proliferation. However, when cultured in non-osteogenic media, only PCL/CaP, PCL/50-45S5 and PCL/50-SrBG scaffolds showed an up-regulation of osteogenic gene expression. Additionally, under a dynamic culture environment, the rate of cell growth, proliferation and osteoblast-related gene expression was enhanced across all scaffold groups. Subsequently, PCL/CaP, PCL/50-45S5 and PCL/50-SrBG scaffolds, with or without seeded cells, were implanted subcutaneously into nude rats for the evaluation of osteoinductivity potential. After 8 and 16weeks, host tissue infiltrated well into the scaffolds, but

  2. Investigation of bioactivity, biocompatibility and thermal behavior of sol–gel silica glass containing a high PEG percentage

    Energy Technology Data Exchange (ETDEWEB)

    Catauro, M., E-mail: michelina.catauro@unina2.it [Department of Industrial and Information Engineering, Second University of Naples, Via Roma 29, 81031 Aversa (Italy); Renella, R.A.; Papale, F. [Department of Industrial and Information Engineering, Second University of Naples, Via Roma 29, 81031 Aversa (Italy); Vecchio Ciprioti, S. [Department of Basic and Applied Science for Engineering, Sapienza University of Rome, Via del Castro Laurenziano 7, Building RM017, I-00161 Rome (Italy)

    2016-04-01

    SiO{sub 2}/PEG organic–inorganic hybrid materials, which contain 60 or 70 weight percentage of PEG, were synthesized by the sol–gel technique. The materials were characterized and subjected to various tests to assess their application in the biomedical field. The evaluation of their morphology by scanning electron microscopy (SEM) confirms the homogeneity of the samples on the nanometer scale. Fourier transform infrared spectroscopy (FT-IR) indicated that the two components of the hybrids (SiO{sub 2} and PEG) are linked by hydrogen bonds. This feature makes them class I hybrids. Simultaneous thermogravimetry/differential thermal analysis (TG/DTA) was used to investigate their thermal behavior and to establish the best temperatures for their pre-treatment. The fundamental properties that a material must have to be used in the biomedical field are biocompatibility and bioactivity. The formation of a hydroxyapatite layer was observed on the hybrid surface by SEM/EDX and FTIR after soaking in simulated body fluid. This indicates that the materials are able to bond to bone tissue. Moreover, the biocompatibility of SiO{sub 2}/PEG hybrids was assessed by performing WST-8 cytotoxicity tests on fibroblast cell NIH 3T3 after 24 h of exposure. The cytotoxicity tests highlight that the cell viability is affected by the polymer percentage. The results showed that the synthesized materials were bioactive and biocompatible. Therefore, the results obtained are encouraging for the use of the obtained hybrids in dental or orthopedic applications. - Highlights: • SiO{sub 2}/PEG hybrid biomaterials synthesized by sol–gel method at high PEG percentage • Chemical, thermal and morphological characterization of hybrid materials • Biological characterizations with WST-8 cytotoxicity tests • Bioactivity characterizations of hybrid materials with high PEG percentage.

  3. Electrophoretic deposition of a bioactive Si, Ca-rich glass coating on 316L stainless steel for biomedical applications

    Directory of Open Access Journals (Sweden)

    H. H. Rodríguez

    2011-12-01

    Full Text Available This work consisted in the development and characterization of a vitroceramic coating on 316L stainless steel bymeans of electrophoretic deposition (EPD. This vitroceramic coating was obtained through a Si-, Ca-rich glas coating crystallization. The electrophoretic deposition tests were performed on 316L stainless steel mechanically polished substrates. The results suggest that the electrophoretic coatings adhered well to the metallic surfaces. Theresults demonstrate that the crystallized coatings are potentially bioactive, because a dense and homogeneous apatite layer, similar to a bone, makes up.

  4. Investigating the influence of Na+ and Sr2+ on the structure and solubility of SiO2-TiO2-CaO-Na2O/SrO bioactive glass.

    Science.gov (United States)

    Li, Y; Placek, L M; Coughlan, A; Laffir, F R; Pradhan, D; Mellott, N P; Wren, A W

    2015-02-01

    This study was conducted to determine the influence that network modifiers, sodium (Na+) and strontium (Sr2+), have on the solubility of a SiO2-TiO2-CaO-Na2O/SrO bioactive glass. Glass characterization determined each composition had a similar structure, i.e. bridging to non-bridging oxygen ratio determined by X-ray photoelectron spectroscopy. Magic angle spinning nuclear magnetic resonance (MAS-NMR) confirmed structural similarities as each glass presented spectral shifts between -84 and -85 ppm. Differential thermal analysis and hardness testing revealed higher glass transition temperatures (Tg 591-760 °C) and hardness values (2.4-6.1 GPa) for the Sr2+ containing glasses. Additionally the Sr2+ (~250 mg/L) containing glasses displayed much lower ion release rates than the Na+ (~1,200 mg/L) containing glass analogues. With the reduction in ion release there was an associated reduction in solution pH. Cytotoxicity and cell adhesion studies were conducted using MC3T3 Osteoblasts. Each glass did not significantly reduce cell numbers and osteoblasts were found to adhere to each glass surface.

  5. Long-term conversion of 45S5 bioactive glass-ceramic microspheres in aqueous phosphate solution.

    Science.gov (United States)

    Fu, Hailuo; Rahaman, Mohamed N; Day, Delbert E; Huang, Wenhai

    2012-05-01

    The conversion of 45S5 glass and glass-ceramics to a hydroxyapatite (HA)-like material in vitro has been studied extensively, but only for short reaction times (typically glass-ceramic microspheres (designated 45S5c) in an aqueous phosphate solution. Microspheres of 45S5c (75-150 μm) were immersed for 10 years at room temperature (~25 °C) in K(2)HPO(4) solution with a concentration of 0.01 M or 1.0 M, and with a starting pH of 7.0 or 9.5. The reacted 45S5c microspheres and solutions were analyzed using structural and analytical techniques. Only 25-45 vol% of the 45S5c microspheres were converted to an HA-like material after the 10 year reaction. In solutions with a starting pH of 9.5, an increase in the K(2)HPO(4) concentration from 0.01 to 1.0 M resulted in a doubling of the volume of the microspheres converted to an HA-like material but had little effect on the composition of the HA-like product. In comparison, reaction of the 45S5c microspheres in the solution with a starting pH of 7.0 resulted in an HA-like product in the 0.01 M K(2)HPO(4) solution but a calcium pyrophosphate product, Ca(10)K(4)(P(2)O(7))(6).9H(2)O, in the 1.0 M solution. The consequences of these results for the long-term use of 45S5 glass-ceramics in biomedical applications are discussed.

  6. Effect of material, process parameters, and simulated body fluids on mechanical properties of 13-93 bioactive glass porous constructs made by selective laser sintering.

    Science.gov (United States)

    Kolan, Krishna C R; Leu, Ming C; Hilmas, Gregory E; Velez, Mariano

    2012-09-01

    The effect of particle size distribution, binder content, processing parameters, and sintering schedule on the microstructure and mechanical properties of porous constructs was investigated. The porous constructs were produced by indirect selective laser sintering (SLS) of 13-93 bioactive glass using stearic acid as a polymeric binder. The binder content and d(50) particle size in the feedstock powders were simultaneously reduced from 22 to 12 wt% and from 20 to 11 μm, respectively, to identify the minimum binder content required for the SLS fabrication. An average particle size of ∼16 μm with a binder content of 15 wt% significantly reduced post-processing time and improved mechanical properties. Increasing the laser power and scan speed at the energy density of 1 cal/cm² maintained the feature sharpness of the parts during the fabrication of green parts and could almost double the mechanical properties of the sintered parts. Changes in the heating rates, ranging from 0.1 to 2 °C/min, during the post-processing of the fabricated "green" scaffolds showed that the heating rate significantly affects the densification and mechanical properties of the sintered scaffolds. The compressive strength of the scaffolds manufactured with the optimized parameters varied from 41 MPa, for a scaffold with a porosity of ∼50%, to 157 MPa, for a dense part. The bioactive scaffolds soaked in simulated body fluids for durations up to 6 weeks were used to evaluate the change in mechanical properties in vitro. Copyright © 2012 Elsevier Ltd. All rights reserved.

  7. Study of the mechanical stability and bioactivity of Bioglass(®) based glass-ceramic scaffolds produced via powder metallurgy-inspired technology.

    Science.gov (United States)

    Boccardi, Elena; Melli, Virginia; Catignoli, Gabriele; Altomare, Lina; Jahromi, Maryam Tavafoghi; Cerruti, Marta; Lefebvre, Louis-Philippe; De Nardo, Luigi

    2016-02-02

    Large bone defects are challenging to heal, and often require an osteoconductive and stable support to help the repair of damaged tissue. Bioglass-based scaffolds are particularly promising for this purpose due to their ability to stimulate bone regeneration. However, processing technologies adopted so far do not allow for the synthesis of scaffolds with suitable mechanical properties. Also, conventional sintering processes result in glass de-vitrification, which generates concerns about bioactivity. In this work, we studied the bioactivity and the mechanical properties of Bioglass(®) based scaffolds, produced via a powder technology inspired process. The scaffolds showed compressive strengths in the range of 5-40 MPa, i.e. in the upper range of values reported so far for these materials, had tunable porosity, in the range between 55 and 77%, and pore sizes that are optimal for bone tissue regeneration (100-500 μm). We immersed the scaffolds in simulated body fluid (SBF) for 28 d and analyzed the evolution of the scaffold mechanical properties and microstructure. Even if, after sintering, partial de-vitrification occurred, immersion in SBF caused ion release and the formation of a Ca-P coating within 2 d, which reached a thickness of 10-15 μm after 28 d. This coating contained both hydroxyapatite and an amorphous background, indicating microstructural amorphization of the base material. Scaffolds retained a good compressive strength and structural integrity also after 28 d of immersion (6 MPa compressive strength). The decrease in mechanical properties was mainly related to the increase in porosity, caused by its dissolution, rather than to the amorphization process and the formation of a Ca-P coating. These results suggest that Bioglass(®) based scaffolds produced via powder metallurgy-inspired technique are excellent candidates for bone regeneration applications.

  8. Characterization of Hybrid Bioactive Glass-polyvinyl Alcohol Scaffolds Containing a PTHrP-derived Pentapeptide as Implants for Tissue Engineering Applications

    Science.gov (United States)

    Coletta, D.J.; Lozano, D.; Rocha-Oliveira, A.A.; Mortarino, P.; Bumaguin, G.E.; Vitelli, E.; Vena, R.; Missana, L.; Jammal, M. V.; Portal-Núñez, S.; Pereira, M.; Esbrit, P.; Feldman, S.

    2014-01-01

    Hybrid foam (BG-PVA) with 50 % Bioactive glass (BG) and 50 % polyvinyl alcohol (PVA) was prepared by sol-gel process to produce scaffolds for bone tissue engineering. The pore structure of hydrated foams was evaluated by 3-D confocal microscopy, confirming 70% porosity and interconnected macroporous network. In this study, we assessed the putative advantage of coating with osteostatin pentapeptide into BG-PVA hybrid scaffolds to improve their bioactivity. In vitro cell culture experiments were performed using mouse pre-osteoblastic MC3T3-E1 cell line. The exposure to osteostatin loaded-BG-PVA scaffolds increase cell proliferation in contrast with the unloaded scaffolds. An in vivo study was selected to implant BG-PVA scaffolds, non-coated (Group A) or coated (Group B) with osteostatin into non critical bone defect at rabbit femur. Both groups showed new compact bone formation on implant surface, with lamellae disposed around a haversian canal forming osteons-like structure. We observed signs of inflammation around the implanted unloaded scaffold at one month, but resolved at 3 months. This early inflammation did not occur in Group B; supporting the notion that osteostatin may act as anti-inflammatory inhibitor. On the other hand, Group B showed increased bone formation, as depicted by many new trabeculae partly mineralized in the implant regenerating area, incipient at 1 month and more evident at 3 months after implantation. PVA/BG hybrid scaffolds present a porous structure suitable to support osteoblast proliferation and differentiation. Our in vitro and in vivo findings indicate that osteostatin coating improves the osteogenic features of these scaffolds PMID:24772196

  9. Bioactivity of Y2O3 and CeO2 doped SiO2-SrO-Na2O glass-ceramics.

    Science.gov (United States)

    Placek, L M; Keenan, T J; Wren, A W

    2016-08-01

    The bioactivity of yttrium and cerium are investigated when substituted for Sodium (Na) in a 0.52SiO2-0.24SrO-0.24-xNa2O-xMO glass-ceramics (where x = 0.08 and MO = Y2O3 or CeO2). Bioactivity is monitored through pH and inductively coupled plasma-optical emission spectrometry where pH of simulated body fluid ranged from 7.5 to 7.6 and increased between 8.2 and 10.0 after 14-day incubation with the glass-ceramic disks. Calcium (Ca) and phosphorus (P) levels in simulated body fluid after incubation with yttrium and cerium containing disks show a continual decline over the 14-day period. In contrast, Con disks (not containing yttrium or cerium) caused the elimination of Ca in solution after 1 day and throughout the incubation period, and initially showed a decline in P levels followed by an increase at 14 days. Scanning electron microscopy and energy dispersive spectroscopy confirmed the presence of Ca and P on the surface of the simulated body fluid-incubated disks and showed precipitates on Con and HCe (8 mol% cerium) samples. Cell viability of MC3T3 osteoblasts was not significantly affected at a 9% extract concentration. Optical microscopy after 24 h cell incubation with disks showed that Con samples do not support osteoblast or Schwann cell growth, while all yttrium and cerium containing disks have direct contact with osteoblasts spread across the wells. Schwann cells attached in all wells, but only showed spreading with the HY-S (8 mol% yttrium, heated to sintering temperature) and YCe (4 mol% yttrium and cerium) disks. Scanning electron microscopy of the compatible disks shows osteoblast and sNF96.2 Schwann cells attachment and spreading directly on the disk surfaces. © The Author(s) 2016.

  10. Influence of heat treatments upon the mechanical properties and in vitro bioactivity of ZrO2-toughened MgO-CaO-SiO2-P2O5-CaF2 glass-ceramics.

    Science.gov (United States)

    Li, Huan-Cai; Wang, Dian-Gang; Meng, Xiang-Guo; Chen, Chuan-Zhong

    2014-09-01

    Zirconia-toughened MgO-CaO-SiO2-P2O5-CaF2 glass-ceramics are prepared using sintering techniques, and a series of heat treatment procedures are designed to obtain a glass-ceramic with improved properties. The crystallization behavior, phase composition, and morphology of the glass-ceramics are characterized. The bending strength, elastic modulus, fracture toughness, and microhardness of the glass-ceramics are investigated, and the effect mechanism of heat treatments upon the mechanical properties is discussed. The bioactivity of glass-ceramics is then evaluated using the in vitro simulated body fluid (SBF) soaking test, and the mechanism whereby apatite forms on the glass-ceramic surfaces in the SBF solution is discussed. The results indicate that the main crystal phase of the G-24 sample undergoing two heat treatment procedures is Ca5(PO4)3F (fluorapatite), and those of the G-2444 sample undergoing four heat treatment procedures are Ca5(PO4)3F and β-CaSiO3 (β-wollastonite). The heat treatment procedures are found to greatly influence the mechanical properties of the glass-ceramic, and an apatite layer is induced on the glass-ceramic surface after soaking in the SBF solution.

  11. Development of fish collagen/bioactive glass/chitosan composite nanofibers as a GTR/GBR membrane for inducing periodontal tissue regeneration.

    Science.gov (United States)

    Zhou, Tian; Liu, Xin; Sui, Baiyan; Liu, Chao; Mo, Xiumei; Sun, Jiao

    2017-09-13

    The development of a guided tissue or bone regeneration (GTR/GBR) membrane with excellent performance has been a major challenge in the biomedical field. The present study was designed to prepare a biomimetic electrospun fish collagen/bioactive glass/chitosan (Col/BG/CS) composite nanofiber membrane and determine its structure, mechanical property, antibacterial activity, and biological effects on human periodontal ligament cells (HPDLCs). The effects of this composite membrane on inducing periodontal tissue regeneration were evaluated using a dog class II furcation defect model. It was found that the composite membrane had a biomimetic structure with good hydrophilicity (the contact angle was 12.83 ± 3°) and a tensile strength of 13.1 ± 0.43 Mpa. Compared to the pure fish collagen membrane, the composite membrane showed some degree of antibacterial activity on Streptococcus mutans. The composite membrane not only enhanced the cell viability and osteogenic gene expression of the HPDLCs, but also promoted the expression of RUNX-2 and OPN protein. Further animal experiments confirmed that the composite membrane was able to promote bone regeneration in the furcation defect of dogs. In conclusion, a biomimetic fish Col/BG/CS composite membrane has been developed in the present study, which can induce tissue regeneration with a certain degree antibacterial activity, providing a basis for potential application as a GTR/GBR membrane.

  12. Bioactive glass microspheres as reinforcement for improving the mechanical properties and biological performance of poly(ε-caprolactone) polymer for bone tissue regeneration.

    Science.gov (United States)

    Lei, Bo; Shin, Kwan-Ha; Noh, Da-Young; Koh, Young-Hag; Choi, Won-Young; Kim, Hyoun-Ee

    2012-05-01

    This study examined the utility of sol-gel-derived bioactive glass microspheres (BGMs) as a reinforcement to improve the mechanical properties and biological performance of poly(ε-caprolactone) (PCL) polymer. All of the PCL-BGMs composites produced, with a variety of BGMs contents (10, 20, and 30 wt %), showed a uniform distribution of the BGMs in the PCL matrix, particularly owing to their spherical shape and small size. This led to a considerable increase in the elastic modulus from 93 ± 12 MPa to 635 ± 179 MPa with increasing BGMs content from 0 to 30 wt %. Furthermore, the addition of the BGMs to the PCL polymer significantly increased the hydrophilicity of the PCL-BGMs composites, which led to a higher water absorption and degradation rate. The PCL-BGMs composite with a BGMs content of 30 wt % showed vigorous growth of apatite crystals with a high aspect ratio on its surface after soaking in the simulated body fluid for 7 days, resulting in the creation of a porous carbonate hydroxyapatite layer. Copyright © 2012 Wiley Periodicals, Inc.

  13. Effect of Desensitization Using Bioactive Glass, Hydroxyapatite, and Diode Laser on the Shear Bond Strength of Resin Composites Measured at Different Time Intervals: An In vitro Study.

    Science.gov (United States)

    Gupta, Timsi; Nagaraja, Shruthi; Mathew, Sylvia; Narayana, Indiresha H; Madhu, K S; Dinesh, K

    2017-01-01

    Dentin desensitizers may change the properties of smear layer and have adverse effects on the bonding performance of adhesive systems. The aim of this study was to compare the effect of bioactive glass (BG), hydroxyapatite, and diode laser desensitization on shear bond strength of resin composites to dentin at different time intervals. Seventy-two caries-free maxillary premolars were selected. Buccal surfaces were flattened to expose dentin. Teeth were divided into four groups (Groups 1, 2, 3, and 4) according to treatment modality (control with no pretreatment, Sensodyne Repair and Protect, Teethmate Desensitizer, diode laser). Bonding was performed using self-etch adhesive followed by composite buildup. Universal testing machine was used to determine shear bond strengths immediately after bonding, after 3 months, and 5 months storage in artificial saliva. Pretreatment with BG and hydroxyapatite desensitizers increased, whereas diode laser decreased mean shear bond strength of composite to dentin as compared to control group. No statistical significant difference in shear bond strength values was seen in groups after storage. Desensitizing toothpastes incorporating remineralizing agents not only occluded open dentinal tubules but also increased shear bond strength of composite to dentin.

  14. Effect of desensitization using bioactive glass, hydroxyapatite, and diode laser on the shear bond strength of resin composites measured at different time intervals: An In vitro Study

    Directory of Open Access Journals (Sweden)

    Timsi Gupta

    2017-01-01

    Full Text Available Background: Dentin desensitizers may change the properties of smear layer and have adverse effects on the bonding performance of adhesive systems. Aim: The aim of this study was to compare the effect of bioactive glass (BG, hydroxyapatite, and diode laser desensitization on shear bond strength of resin composites to dentin at different time intervals. Materials and Methods: Seventy-two caries-free maxillary premolars were selected. Buccal surfaces were flattened to expose dentin. Teeth were divided into four groups (Groups 1, 2, 3, and 4 according to treatment modality (control with no pretreatment, Sensodyne Repair and Protect, Teethmate Desensitizer, diode laser. Bonding was performed using self-etch adhesive followed by composite buildup. Universal testing machine was used to determine shear bond strengths immediately after bonding, after 3 months, and 5 months storage in artificial saliva. Results: Pretreatment with BG and hydroxyapatite desensitizers increased, whereas diode laser decreased mean shear bond strength of composite to dentin as compared to control group. No statistical significant difference in shear bond strength values was seen in groups after storage. Conclusion: Desensitizing toothpastes incorporating remineralizing agents not only occluded open dentinal tubules but also increased shear bond strength of composite to dentin.

  15. Influence of Mg doping on the early steps of physico-chemical reactivity of sol-gel derived bioactive glasses in biological medium.

    Science.gov (United States)

    Soulié, J; Nedelec, J M; Jallot, E

    2009-11-28

    The aim of this study is to highlight the influence of magnesium doping on the surface reactivity of binary (SiO(2)-CaO) and ternary (SiO(2)-CaO-P(2)O(5)) bioactive glasses, prepared by sol-gel chemistry, in biological conditions. These materials were produced in powder form, and their compositional and textural properties characterized. They were then soaked in biological fluids for different delays from 0 to 4 days. The surface changes were characterized using Particles Induced X-ray Emission (PIXE) associated with Rutherford Backscattering Spectroscopy (RBS), which are efficient methods for multi-elemental analysis. Elemental maps of major and trace elements were obtained at a micrometer scale and revealed the formation of a calcium phosphate-rich layer after a few days of interaction. We demonstrate that the presence of magnesium in the material has an impact on the development and the formation rate of the bone-like apatite layer.

  16. Engineered Hybrid Scaffolds of Poly(vinyl alcohol/Bioactive Glass for Potential Bone Engineering Applications: Synthesis, Characterization, Cytocompatibility, and Degradation

    Directory of Open Access Journals (Sweden)

    Hermes S. Costa

    2012-01-01

    Full Text Available The synthesis, characterization, preliminary cytocompatibility, and degradation behavior of the hybrids based on 70% Poly(vinyl alcohol and 30% bioactive glass (58SiO2–33CaO–9P2O5, BaG with macroporous tridimensional structure is reported for the first time. The effect of glutaraldehyde covalent crosslinker in the organic-inorganic nanostructures produced and, as a consequence, tailoring the hybrids properties was investigated. The PVA/BaG hybrids scaffolds are characterized by Fourier transform infrared spectroscopy (FTIR, scanning electron microscopy (SEM, X-ray diffraction (XRD, and X-ray Microcomputed tomography analysis (μCT. Cytotoxicity assessment is performed by the MTT method with VERO cell culture. Additionally, the hybrid in vitro degradation assay is conducted by measuring the mass loss by soaking in deionized water at 37°C for up to 21 days. The results have clearly shown that it is possible to modify the PVA/BaG hybrids properties and degradation behavior by engineering the structure using different concentrations of the chemical crosslinker. Moreover, these hybrid crosslinked nanostructures have presented 3D hierarchical pore size architecture varying within 10–450 μm and a suitable cytocompatibility for potential use in bone tissue engineering applications.

  17. In vitro and in vivo Biocompatibility of Alginate Dialdehyde/Gelatin Hydrogels with and without Nanoscaled Bioactive Glass for Bone Tissue Engineering Applications

    Directory of Open Access Journals (Sweden)

    Ulrike Rottensteiner

    2014-03-01

    Full Text Available In addition to good mechanical properties needed for three-dimensional tissue engineering, the combination of alginate dialdehyde, gelatin and nano-scaled bioactive glass (45S5 is supposed to combine excellent cellular adhesion, proliferation and differentiation properties, good biocompatibility and predictable degradation rates. The goal of this study was to evaluate the in vitro and in vivo biocompatibility as a first step on the way to its use as a scaffold in bone tissue engineering. In vitro evaluation showed good cell adherence and proliferation of bone marrow derived mesenchymal stem cells seeded on covalently crosslinked alginate dialdehyde-gelatin (ADA-GEL hydrogel films with and without 0.1% nano-Bioglass® (nBG. Lactate dehydrogenase (LDH- and mitochondrial activity significantly increased in both ADA-GEL and ADA-GEL-nBG groups compared to alginate. However, addition of 0.1% nBG seemed to have slight cytotoxic effect compared to ADA-GEL. In vivo implantation did not produce a significant inflammatory reaction, and ongoing degradation could be seen after four weeks. Ongoing vascularization was detected after four weeks. The good biocompatibility encourages future studies using ADA-GEL and nBG for bone tissue engineering application.

  18. One-step method for the preparation of poly(methyl methacrylate) modified titanium-bioactive glass three-dimensional scaffolds for bone tissue engineering.

    Science.gov (United States)

    Han, Xiao; Lin, Huiming; Chen, Xiang; Li, Xin; Guo, Gang; Qu, Fengyu

    2016-04-01

    A novel three-dimensional (3D) titanium (Ti)-doping meso-macroporous bioactive glasses (BGs)/poly(methyl methacrylate) (PMMA) composite was synthesised using PMMA and EO20PO70EO20 (P123) as the macroporous and mesoporous templates, respectively. Unlike the usual calcination method, the acid steam technique was used to improve the polycondensation of Ti-BGs, and then PMMA was partially extracted via chloroform to induce the macroporous structure. Simultaneously, the residual PMMA which remained in the wall enhanced the compressive strength to 2.4 MPa (0.3 MPa for pure BGs). It is a simple and green method to prepare the macro-mesoporous Ti-BGs/PMMA. The materials showed the 3D interconnected hierarchical structure (250 and 3.4 nm), making the fast inducing-hydroxyapatite growth and the controlled drug release. Besides mentioned above, the good antimicrobial property and biocompatible of the scaffold also ensure it is further of clinical use. Herein, the fabricated materials are expected to have potential application on bone tissue regeneration.

  19. Poly (d/l) lactide/polycaprolactone/bioactive glasss nanocomposites materials for anterior cruciate ligament reconstruction screws: The effect of glass surface functionalization on mechanical properties and cell behaviors.

    Science.gov (United States)

    Esmaeilzadeh, Javad; Hesaraki, Saeed; Hadavi, Seyed Mohammad-Mehdi; Ebrahimzadeh, Mohammad Hosein; Esfandeh, Masoud

    2017-08-01

    In this paper, different nanocomposites made of a polymer blend (80% of PDLLA and 20% of PCL in w/w) and various amounts of a sol-gel derived bioactive glass nanoparticles (0, 1, 3 and 6wt%) were prepared using a solvent-evaporation technique. The morphology, mechanical properties and osteoblastic cell behaviors of the nanocomposites were evaluated. According to the early results, addition of bioactive glass nanoparticles to the polymer matrix reduced the tensile and flexural strength because of a non-uniform distribution of the nanoparticles. Thus, a homogeneous dispersion was obtained by surface modification of the glass nanoparticles using (3-aminopropyl)triethoxysilane as a coupling agent. The results showed that the tensile and flexural strength of the nanocomposite were improved by the nanoparticle functionalization, however the glass content was a crucial factor. The maximum tensile and flexural strength values of 38MPa and 94MPa were obtained for the polymer matrix loaded with 3wt% of the modified nanofiller and further increase of filler content led to sever agglomeration and hence a reduction of the mechanical properties. The obtained mechanical properties are favorable for anterior cruciate ligament reconstruction screws. Besides, the results of cell culture using human osteoblastic cells illustrated better cell attachment and cell growth of the nanocomposites compared to the neat polymer blend. Copyright © 2017 Elsevier B.V. All rights reserved.

  20. Porous bioactive materials

    Science.gov (United States)

    Zhang, Kai

    Bioactive materials chemically bond to tissues through the development of biologically active apatite. Porous structures in biomaterials are designed to enhance bioactivity, grow artificial tissues and achieve better integration with host tissues in the body. The goal of this research is to design, fabricate and characterize novel porous bioactive materials. 3D ordered macroporous bioactive glasses (3DOM-BGs, pore size: 200--1000 nm) were prepared using a sol-gel process and colloidal crystal templates. 3DOM-BGs are more bioactive and degradable than mesoporous (pore size periodontal fillers, and drugs and biological factors delivery agents. Anchoring artificial soft tissues (e.g., cartilage) to native bone presents a challenge. Porous polymer/bioactive glass composites are candidate materials for engineering artificial soft tissue/bone interfaces. Porous composites consisting of polymer matrices (e.g., polysulfone, polylactide, and polyurethane) and bioactive glass particles were prepared by polymer phase separation techniques adapted to include ceramic particles. Composites (thickness: 200--500 mum) have asymmetric structures with dense top layers and porous structures beneath. Porous structures consist of large pores (>100 mum) in a network of smaller (<10 mum) interconnected pores. Dense layers can be removed and large pores exposed by abrasion or salt leaching techniques. Composite modulus was enhanced with the increase of glass content, due to the change in composition and pore content. The growth of bone-like apatite on and inside composites after soaking in SBF demonstrated their potential for integration with bone. Cell culture studies revealed that composite surfaces were suitable for attachment, spreading and proliferation of chondrocytes.

  1. Effect of the substitution of Y2O3 for CaO on the bioactivity of 2.5CaO.2SiO2 glass.

    Science.gov (United States)

    Costantini, A; Fresa, R; Buri, A; Branda, F

    1997-03-01

    Glasses were prepared whose composition is defined by the following general formula: (2.5-x)CaO.x/3Y2O3.2SiO2 (0 < or = x < or = 1). Their behaviour when they were soaked in a simulated body fluid (SBF) and their thermal properties (glass transformation and softening temperatures, Tg and Ts respectively) were studied Tg and Ts increase with the Y2O3 content. The trend can be explained on the basis of the increased structural rigidity when Ca2+ ions are substituted by Y2+ ions, because of the formation of stronger bonds to the oxygen. The bioactivity was studied by means of electron microscopy equipped with an energy dispersive system for elemental analysis and IR spectroscopy. All the glasses studied except the one with the greatest amount of Y2O3. x = 1.0, reacted with SBF by forming a calcium phosphate layer. The experimental results suggest that the bioactivity is negatively influenced by the Y2O3 content: the tendency to form a calcium phosphate layer is reduced the greater the amount of CaO substituted. A comparison with literature data indicates that the amount of Y2O3 that can be substituted depends on the CaO content of the base CaO-SiO2 glass. The experimental results are in good agreement with the mechanism reported in the literature. After 7 days soaking, crystalline hydroxyapatite is formed in the Y2O3-free glass and in the glasses of low Y2O3 content (x-0.2).

  2. Comparison of in vitro dentinal tubule occluding efficacy of two different methods using a nano-scaled bioactive glass-containing desensitising agent.

    Science.gov (United States)

    Ma, Qian; Wang, Tianda; Meng, Qingfei; Xu, Xiao; Wu, Huaying; Xu, Dongjing; Chen, Yaming

    2017-05-01

    This study aimed to compare the in vitro dentinal tubule occluding efficacy of two different methods using a nano-scaled bioactive glass (BG)-containing desensitising agent. Citric acid treated dentine discs were randomly divided into 7 groups (n=8). Group A1, A2 and A3: dentine discs coated with BG desensitising paste; Group B1, B2 and B3: dentine discs coated with BG desensitising paste and covered with matched transparent trays; and control group (GroupC): dentine discs treated with deionised water. Field Emission Scanning Electron Microscopy (FE-SEM) was used to capture topographical images of each dentine discs after they were immersed in artificial saliva for corresponding treatment time and dentinal tubules exposure rates were thus measured. Elemental compositions of dentine discs were identified using Energy-Dispersive X-ray Spectroscopy (EDX). FE-SEM revealed better tubule occluding effects in Group B. Dentinal tubules in Group B3 were totally occluded with continuous homogeneous minerals to a depth of 20.6-24.7μm. Dentinal tubule exposure rates in Group B1, Group B2 and Group B3 were lower than that in Group A1, Group A2 and Group A3. EDX indicated that occluding deposits observed in each gro