  1. UV stability of HMS-PP (High Melt Strength Polypropylene) obtained by radiation process

    International Nuclear Information System (INIS)

    Oliani, W.L.; Parra, Duclerc F.; Lugao, Ademar B.

    2006-01-01

    HMS-PP in grains was synthesized by the gamma irradiation of PP under a crosslinking atmosphere of acetylene, followed by thermal treatment for radical recombination and thermal treatment for annihilation of the remaining radicals. The UV stability of the material was evaluated in reference to grains. Accelerated weathering test of HMS-PP samples were performed in artificial ultraviolet light and condensation chamber apparatus Comexim (C-UV type) in aging conditions of exposure for 120 hours and 240 hours. The results were compared to the deterioration caused by sunlight and dew under natural exposition. This work investigated changes in mechanical proprieties (elongation and rupture strength) behavior, Infrared Spectroscopy (FTIR), Optical Microscopy (MO), Scanning Electronic Microscopy (SEM) and Rheological properties of HMS-PP. The HMS-PP is more fragile than PP and undergoes predominately chain scission in aggressive environment degradation conditions. (author)

  2. Polypropylene obtained through zeolite supported catalysts

    International Nuclear Information System (INIS)

    Bastos, Queli C.; Marques, Maria de Fatima V.

    2004-01-01

    Propylene polymerizations were carried out with φ 2 C(Flu)(Cp)ZrCl 2 and SiMe 2 (Ind)2ZrCl 2 catalysts supported on silica, zeolite sodic mordenite (NaM) and acid mordenite (HM). The polymerizations were performed at different temperatures and varying aluminium/zirconium molar ratios ([Al]/[Zr]). The effect of these reaction parameters on the catalyst activity was investigated using a proposed statistical experimental planning. In the case of f 2 C(Flu)(Cp)ZrCl 2 , SiO 2 and NaM were used as support and the catalyst performance evaluated using toluene and pentane as polymerization solvent. The molecular weight, molecular weight distribution, melting point and crystallinity of the polymers were examined. The results indicate very high activities for the syndiospecific heterogeneous system. Also, the polymers obtained had superior Mw and stereo regularity. (author)

  3. Polypropylene obtained through zeolite supported catalysts

    Directory of Open Access Journals (Sweden)

    Queli C. Bastos

    2004-01-01

    Full Text Available Propylene polymerizations were carried out with f2C(Flu(CpZrCl2 and SiMe2(Ind2ZrCl2 catalysts supported on silica, zeolite sodic mordenite (NaM and acid mordenite (HM. The polymerizations were performed at different temperatures and varying aluminium/zirconium molar ratios ([Al]/[Zr]. The effect of these reaction parameters on the catalyst activity was investigated using a proposed statistical experimental planning. In the case of f2C(Flu(CpZrCl2, SiO2 and NaM were used as support and the catalyst performance evaluated using toluene and pentane as polymerization solvent. The molecular weight, molecular weight distribution, melting point and crystallinity of the polymers were examined. The results indicate very high activities for the syndiospecific heterogeneous system. Also, the polymers obtained had superior Mw and stereoregularity.

  4. Rheological behavior of nanocomposite HMSPP (High Melt Strength Polypropylene) obtained by the addition of clay 'chocolate' organophilizated as reinforcement agent

    International Nuclear Information System (INIS)

    Fermino, D.M.; Valenzuela-Diaz, F.R.; Parra, D.F.; Lugao, A.B.

    2012-01-01

    The objective of this study is to obtain a nanocomposite with a bentonite treated in laboratory in comparison to a commercial bentonite and the study of their rheological behavior. The treatment of the sodium clay organophilic in laboratory it was well succeeded as the result of FTIR testing and there was formation of nanocomposites with intercalated clays as XRD assay. In the rheology assay there was increase in a complex viscosity in all of nanocomposite samples of HMSPP. There were small changes in G' module and G″ for nanocomposites. Only with these rheology results we can not say it is interleaved microcomposite or nanocomposite because the criteria of both were not fully met

  5. Development of foams from linear polypropylene (PP) and high melt strength polypropylene (HMSPP) polymeric blends

    International Nuclear Information System (INIS)

    Cardoso, Elisabeth Carvalho Leite

    2009-01-01

    Foamed polymers are future materials, with a comprehensive application field. They can be used in order to improve appearance of insulation structures, for example, or to reduce costs involving materials. This work address to Isotactic Polypropylene / High Melt Strength Polypropylene blends, for foams production. Rheological behavior of polymer melt, especially referring to viscosity in processing temperature, plays a decisive role in applications where dominates extensional flow, as in case of foaming. If the viscosity is very low, it will correspond to a low melt strength, as in case of linear homopolymer (Isotact PP), and the foam will be prejudiced, due to the impossibility of expansion. Otherwise, if the viscosity is very high, with a high melt strength, the foam will collapse immediately after its formation. In order to get foams with an homogeneous and defined cellular structure, there were accomplished blends, 50% in weight, between linear homopolymer (isotactic PP) and HMSPP, from PP modified as per gamma radiation, in acetylene environment and at a 12.5 kGy doses. Extrusion process used a soluble foaming methodology, according to a processing/dissolution principle, which involves the dissolution of a Physical Blowing Agent (PBA), under 30 bar pressure, homogeneously mixed with polymeric melt. Extrusion conditions, that generally involve temperature, pressure and viscoelastic material flow control were experimentally investigated to define prevalent characteristics for producing foams. Nitrogen was the used PBA and process extrusion parameters were adapted to PP, HMSPP and their 50% in weight mixtures thereof. Major PP and HMSPP characteristics were obtained via melt Index and melt strength and thermal analyses (DSC/TGA), in order to make viable and to reproduce foaming as per extrusion process. Foams cellular morphology of PP, HMSPP and their 50% in weight mixtures thereof was investigated, with and without talc addition, as nucleating agent, by using

  6. Rheology of High-Melt-Strength Polypropylene for Additive Manufacturing

    DEFF Research Database (Denmark)

    Hofstätter, Thomas; Kamleitner, Florian; Jagenteufel, Ralf

    Acrylonitrile butadiene styrene (ABS) is a widely used material for additive manufacturing (AM) fused deposition modeling (FDM). The rheological properties of high-melt-strength polypropylene (HMS-PP) were compared to commercially available ABS 250 filament to study the possibility of using...

  7. Strength of biodegradable polypropylene tapes filled with a modified starch

    Science.gov (United States)

    Vinidiktova, N. S.; Ermolovich, O. A.; Goldade, V. A.; Pinchuk, L. S.

    2006-05-01

    The possibility of creating composite materials with high deformation and strength characteristics based on polypropylene (PP) and a natural polysaccharide in the form of a modified starch (MS) has been studied. The modified starch is shown to interact chemically with functional groups of PP, thereby positively affecting the physicomechanical properties, structure, and water absorption properties of films and oriented flat fibers based on starch-filled PP. The strength characteristics of both oriented and unoriented composites are 1.5-2.0 times as high as those of the initial PP. The water absorption ability of the materials varies symbatically with content of MS, which points to the dominant contribution of interactions at the PP-MS interface. The introduction of MS into synthetic polymers offers a possibility of producing new ecologically safe materials with high strength characteristics.

  8. Influence of chemical treatment of clay to obtain polypropylene nanocomposites

    International Nuclear Information System (INIS)

    Rosa, Jeferson L.S.; Marques, Maria F.V.

    2009-01-01

    Commercial clay was chemically treated to prepare a Ziegler-Natta catalyst containing MgCl 2 and clay for the synthesis of polypropylene nanocomposites by in situ polymerization. The performance of this catalyst and materials obtained in propylene polymerization was compared with a reference catalyst (without clay) and with another, whose composition presents the same clay but without prior chemical treatment. Techniques like differential scanning calorimetry (DSC), X-ray diffractometry (XRD) and melt flow index (MFI) measurements were performed. There was a marked reduction in catalytic activity of clay catalysts in comparison with the reference one, and a slight reduction in melting temperature of the polymers produced from first ones. The melt flow index of polymers obtained with treated clay were notably higher than those synthesized with the untreated clay, so the treated clay caused treated the production of PP's with lower molar mass. The clays showed an increase of spacing and irregular stacking of the lamellas, especially if chemically treated. (author)

  9. Synthesis by irradiation and mechanism and structural characterization study of high melt strength polypropylene

    International Nuclear Information System (INIS)

    Lugao, Ademar Benevolo

    2004-01-01

    Polypropylene molecular structure is made only by linear molecules interacting by weak forces. The resulting PP has very low melt strength (MS). MS is important to make feasible to process PP by all the transformation technologies based on the free expansion of the melt. The aim of this work was to develop a new process to synthesize PP with crosslinks and/or long chain branches, known as High Melt Strength Polypropylene (HMSPP) and to characterize its structure and synthesis mechanism. HMSPP was obtained by the irradiation of PP under a crosslinking (acetylene) atmosphere or inert or oxidative one, followed by thermal treatment for radical recombination and thermal treatment for annihilation of the remaining radicals under reactive or inert atmosphere. The results from rheological characterization showed that the highest levels of MS were obtained by conducting irradiation and thermal treatments under crosslinking atmospheres. The results for the elucidation of reaction mechanism by electron spin resonance (ESR) showed that acetylene irradiation is effective in promoting the creation of double bonds, based on the formation of polyenil radicals. The results of structural unraveling showed that radiation promotes predominantly the degradation of atactic molecules or molecules with atactic defects. These results support the hypothesis of formation of branched PP molecules based on the reaction of those fragments with the double bonds created in the PP molecules. (author)

  10. Properties analysis of tensile strength, crystallinity degree and microstructure of polymer composite polypropylene-sand

    International Nuclear Information System (INIS)

    Sudirman; Karo-Karo, Aloma; Ari-Handayani; Bambang-Sugeng; Rukihati; Mashuri

    2004-01-01

    Materials modification base on polymer toward polymer composite is needed by addition of filler. Mechanical properties such as tensile strength, crystallinity degree and microstructure of polymer composite based on polypropylene with sand filler have been investigated. In this work, the polymer composite has been made by mixing the matrix of polypropylene melt flow 2 (PP MF2) or polypropylene melt flow 10 (PP MF 10) with sand filler in a labo plastomill. The composition of sand filler was varied to 10, 30, 40 and 50 % v/v, a then the composite were casted to the film sheets form. The sheets were characterized mechanically i.e tensile strength, crystallinity degree and microstructure. The result showed that the tensile strength decreased by increasing the volume fraction of sand filler, in accordance with microstructure investigation that the matrix area under zone plastic deformation (more cracks), while the filler experienced elastic deformation, so that the strength mechanism of filler did not achieved with expectation (Danusso and Tieghi theory). For filler more than 30 % of volume fraction, the tensile strength of polypropylene melt flow 10 (PP MF 10) was greater than that polypropylene melt flow 2 (PP MF2). It was caused by plasticities in PP MF 10. The tensile strength of PP MF2 was greater than that PP MF 10 for volume fraction of sand filler less than 30 %. It was caused by PP MF2 to be have more degree of crystallinity

  11. Flexural strength of self compacting fiber reinforced concrete beams using polypropylene fiber: An experimental study

    Science.gov (United States)

    Lisantono, Ade; Praja, Baskoro Abdi; Hermawan, Billy Nouwen

    2017-11-01

    One of the methods to increase the tensile strength of concrete is adding a fiber material into the concrete. While to reduce a noise in a construction project, a self compacting concrete was a good choices in the project. This paper presents an experimental study of flexural behavior and strength of self compacting fiber reinforced concrete (RC) beams using polypropylene fiber. The micro monofilament polypropylene fibers with the proportion 0.9 kg/m3 of concrete weight were used in this study. Four beam specimens were cast and tested in this study. Two beams were cast of self compacting reinforced concrete without fiber, and two beams were cast of self compacting fiber reinforced concrete using polypropylene. The beams specimen had the section of (180×260) mm and the length was 2000 mm. The beams had simple supported with the span of 1800 mm. The longitudinal reinforcements were using diameter of 10 mm. Two reinforcements of Ø10 mm were put for compressive reinforcement and three reinforcements of Ø10 mm were put for tensile reinforcement. The shear reinforcement was using diameter of 8 mm. The shear reinforcements with spacing of 100 mm were put in the one fourth near to the support and the spacing of 150 mm were put in the middle span. Two points loading were used in the testing. The result shows that the load-carrying capacity of the self compacting reinforced concrete beam using polypropylene was a little bit higher than the self compacting reinforced concrete beam without polypropylene. The increment of load-carrying capacity of self compacting polypropylene fiber reinforced concrete was not so significant because the increment was only 2.80 % compare to self compacting non fiber reinforced concrete. And from the load-carrying capacity-deflection relationship curves show that both the self compacting polypropylene fiber reinforced concrete beam and the self compacting non fiber reinforced concrete beam were ductile beams.

  12. Compressive and flexural strength of concrete containing palm oil biomass clinker and polypropylene fibres

    Science.gov (United States)

    Ibrahim, M. H. Wan; Mangi, Sajjad Ali; Burhanudin, M. K.; Ridzuan, M. B.; Jamaluddin, N.; Shahidan, S.; Wong, YH; Faisal, SK; Fadzil, M. A.; Ramadhansyah, P. J.; Ayop, S. S.; Othman, N. H.

    2017-11-01

    This paper presents the effects of using palm oil biomass (POB) clinker with polypropylene (PP) fibres in concrete on its compressive and flexural strength performances. Due to infrastructural development works, the use of concrete in the construction industry has been increased. Simultaneously, it raises the demand natural sand, which causes depletion of natural resources. While considering the environmental and economic benefits, the utilization of industrial waste by-products in concrete will be the alternative solution of the problem. Among the waste products, one of such waste by-product is the palm oil biomass clinker, which is a waste product from burning processes of palm oil fibres. Therefore, it is important to utilize palm oil biomass clinker as partial replacement of fine aggregates in concrete. Considering the facts, an experimental study was conducted to find out the potential usage of palm oil fibres in concrete. In this study, total 48 number of specimens were cast to evaluate the compressive and flexural strength performances. Polypropylene fibre was added in concrete at the rate of 0.2%, 0.4% and 0.6%, and sand was replaced at a constant rate of 10% with palm oil biomass clinker. The flexural strength of concrete was noticed in the range of 2.25 MPa and 2.29 MPa, whereas, the higher value of flexural strength was recorded with 0.4% polypropylene fibre addition. Hence, these results show that the strength performances of concrete containing POB clinker could be improved with the addition of polypropylene fibre.

  13. Thermal degradation and tensile strength of sansevieria trifasciata-polypropylene composites

    Science.gov (United States)

    Abral, H.; Kenedy, E.

    2015-07-01

    The paper exhibits thermal degradation and tensile strength of Sansevieria Trifasciata (ST) fibers and polypropylene (PP) composites. Thermal degradation of ST fibers PP composites was conducted by using thermogravimetry (TGA) instrument, meanwhile tensile strength of the composite was done by using tensile equipment. The results show that the thermal resistance of ST fibers PP composites was higher than that of virgin PP only. Increases in volume fraction of fibers in the composites enhance the tensile strength. Scanning Electron Microscope (SEM) observation exhibits good interface bonding between ST fibers and PP matrix.

  14. Thermal degradation and tensile strength of sansevieria trifasciata-polypropylene composites

    International Nuclear Information System (INIS)

    Abral, H; Kenedy, E

    2015-01-01

    The paper exhibits thermal degradation and tensile strength of Sansevieria Trifasciata (ST) fibers and polypropylene (PP) composites. Thermal degradation of ST fibers PP composites was conducted by using thermogravimetry (TGA) instrument, meanwhile tensile strength of the composite was done by using tensile equipment. The results show that the thermal resistance of ST fibers PP composites was higher than that of virgin PP only. Increases in volume fraction of fibers in the composites enhance the tensile strength. Scanning Electron Microscope (SEM) observation exhibits good interface bonding between ST fibers and PP matrix. (paper)

  15. Study of mechanical, rheological and thermal properties of nanocomposite HMSPP (high melt strength polypropylene) with Brazilian bentonite

    International Nuclear Information System (INIS)

    Fermino, Danilo Marin

    2011-01-01

    This work concerns to the study of the mechanical, thermal and rheological behavior of the nano composite HMSPP - Polypropylene High Melt Strength (obtained at a dose of 12.5 kGy) and a bentonite clay Brazilian Paraiba, known as 'Chocolate' in concentrations of 5 and 10% by weight, comparison of to one American Clay, Cloisite 20A nanocomposite was done. Agent compatibilizer polypropylene-graft, known as maleic anhydride (PP-g-AM) was addict 3% concentration thought technique melt intercalation using a twin-screw extruder and the specimens were prepared by injection process. The mechanical behavior was evaluated by strength, flexural strength and impact tests. The thermal behavior was evaluated by the techniques of differential scanning calorimetry (DSC) and thermogravimetry (TGM). The rheological behavior was evaluated in rheometer. The morphology of the nanocomposites was studied by the technique of scanning electron microscopy (SEM). The organophilic bentonite and the nanocomposites were characterized by X-ray diffraction (XRD) and infrared (FTIR). (author)

  16. EFFECT OF SEA WATER ON THE STRENGTH OF POROUS CONCRETE CONTAINING PORTLAND COMPOSITE CEMENT AND MICROFILAMENT POLYPROPYLENE FIBER

    OpenAIRE

    TJARONGE, M.W

    2011-01-01

    The aim of this research is to study the influence of sea water on the strength of porous concrete containing Portland Composite cement and micro monofilament polypropylene fibre. The specimens of porous concrete were immersed in the sea water up to 28 days. The compressive strength test and flexural strength test were carried out at 3, 7 and 28 days in order to investigate the strength development. The test result indicated that the strength of porous concrete can develop in t...

  17. Study of the weathering of high melt strength polypropylene (HMS-PP)

    Energy Technology Data Exchange (ETDEWEB)

    Oliani, Washington L.; Parra, Duclerc F.; Otaguro, Harumi; Lima, Luis F.C.P.; Lugao, Ademar B. [Instituto de Pesquisas Energeticas e Nucleares (IPEN/CNEN-SP), Sao Paulo, SP (Brazil)], E-mail: dfparra@ipen.br

    2007-07-01

    One of the reasons for the good acceptance of the commercial PP is the fact that market requires products with features of 'engineering plastics' with prices in the range of commodities. High melt strength polypropylene (HMSPP) grades are produced by radiation process and have improved rheology for melt blow processes. The melt strength (MS) properties of a polymer increase with molecular weight and with long chain branching due to the increase in the entanglement level. The main scope of this study was to evaluate the stability of HMS-PP prepared by gamma radiation with doses of 12.5, 20 kGy in comparison with virgin PP. Many variables influence the rate of degradation of polymers by photo-oxidation. The irradiance and permeability to oxygen are the most important factors but other factors such as temperature and moisture have also influenced the degradation rates. Polypropylenes are sensitive to oxidation due to the presence of the tertiary carbon atom. Therefore, effective stabilization against oxidation (thermo and photo oxidation) is required. The samples submitted to the natural aging for a period of six months were characterized by: tensile test, thermogravimetry analysis (TGA), optical microscopy, scanning electronic microscopy (SEM) and infrared spectroscopy (FTIR). SEM analysis showed particular aspects of cracks on the surface. The loss of tensile strength is associated to the presence of fractures. The results showed that pronounced oxidation followed by chain scission occur at the initial periods of weathering exposition of the HMS-PP. (author)

  18. Study of the weathering of high melt strength polypropylene (HMS-PP)

    International Nuclear Information System (INIS)

    Oliani, Washington L.; Parra, Duclerc F.; Otaguro, Harumi; Lima, Luis F.C.P.; Lugao, Ademar B.

    2007-01-01

    One of the reasons for the good acceptance of the commercial PP is the fact that market requires products with features of 'engineering plastics' with prices in the range of commodities. High melt strength polypropylene (HMSPP) grades are produced by radiation process and have improved rheology for melt blow processes. The melt strength (MS) properties of a polymer increase with molecular weight and with long chain branching due to the increase in the entanglement level. The main scope of this study was to evaluate the stability of HMS-PP prepared by gamma radiation with doses of 12.5, 20 kGy in comparison with virgin PP. Many variables influence the rate of degradation of polymers by photo-oxidation. The irradiance and permeability to oxygen are the most important factors but other factors such as temperature and moisture have also influenced the degradation rates. Polypropylenes are sensitive to oxidation due to the presence of the tertiary carbon atom. Therefore, effective stabilization against oxidation (thermo and photo oxidation) is required. The samples submitted to the natural aging for a period of six months were characterized by: tensile test, thermogravimetry analysis (TGA), optical microscopy, scanning electronic microscopy (SEM) and infrared spectroscopy (FTIR). SEM analysis showed particular aspects of cracks on the surface. The loss of tensile strength is associated to the presence of fractures. The results showed that pronounced oxidation followed by chain scission occur at the initial periods of weathering exposition of the HMS-PP. (author)

  19. Effect of Pin Geometry on the Mechanical Strength of Friction-Stir-Welded Polypropylene Composite Plates

    Science.gov (United States)

    Kordestani, F.; Ashenai Ghasemi, F.; Arab, N. B. M.

    2017-09-01

    Friction stir welding (FSW) is a solid-state welding process, which has successfully been applied in aerospace and automotive industries for joining materials. The friction stir tool is the key element in the FSW process. In this study, the effect of four different tool pin geometries on the mechanical properties of two types of polypropylene composite plates, with 30% glass and carbon fiber, respectively, were investigated. For this purpose, four pins of different geometry, namely, a threaded-tapered pin, square pin, four-flute threaded pin, and threaded-tapered pin with a chamfer were made and used to carry out the butt welding of 5-mm-thick plates. The standard tensile and Izod impact tests were performed to evaluate the tensile strength and impact toughness of welded specimens. The results indicated that the threaded-tapered pin with a chamfer produced welds with a better surface appearance and higher tensile and impact strengths. The tests also showed that, with the threaded-tapered pin with a chamfer, the impact strength of the glass- and carbon-fiber composite welds were about 40 and 50%, respectively, of that of the base materials.

  20. Interfacial crystalline structures in injection over-molded polypropylene and bond strength.

    Science.gov (United States)

    Yan, Bowen; Wu, Hong; Jiang, Genjie; Guo, Shaoyun; Huang, Jian

    2010-11-01

    This paper describes interfacial crystalline structures found in injection overmolded polypropylene components and the relationship of these structures to bond strength between the components. The combined effects of the development of hierarchical gradient structures and the particular thermomechanical environment near the interface on the interfacial crystalline structures were investigated in detail by PLM, SEM, DSC, WAXD, and infrared dichroism spectroscopy. The experimental results showed that during molding there was competitive formation of interfacial crystalline structures consisted of "shish-kebab" layer (SKL) and a transcrystalline layers (TCL). Variation in shear stress (controlled by injection pressure and injection speed) plays an important role in the formation of the SKL. The formation of TCL is influenced by the thermal environment, namely melt temperature and mold temperature. Increasing within certain limits, interfacial temperature and the thermal gradient near the interface promotes β-iPP growth. The relationship between interfacial crystalline structures and interfacial bond strength was established by lap shear measurement. The interfacial bond strength is improved by enhancing the formation of TCL, but reduced if SKL predominates.

  1. Polypropylene Nano composites Obtained by In Situ Polymerization Using Metallocenes Catalyst: Influence of the Nanoparticles on the Final Polymer Morphology

    International Nuclear Information System (INIS)

    Zapata, P.; Quijada, R.

    2012-01-01

    Polypropylene nano composites containing silica nanospheres based on the sol-gel methods were produced via in situ polymerization using a rac-Et(Ind) 2 ZrCl 2 /methylaluminoxane (MAO) system. Two different routes were used depending on the interaction between the silica nanoparticles with the catalytic system. In route 1 the nanoparticles were added together with the catalytic system (rac-Et(Ind) 2 ZrCl 2 )/(MAO) directly into the reactor, and in route 2 the metallocenes rac-Et(Ind) 2 ZrCl 2 was supported on silica nanospheres pretreated with (MAO). SEM images show that when the nanospheres were added by both routes, they were replicated in the final polymer particle morphology; this phenomenon was more pronounced for PP obtained by route 2. The polypropylene (PP) nano composites obtained by both routes had a slightly higher percent crystallinity and crystallinity temperatures than pure PP. Transmission electron microscopy (TEM) images show that the nanospheres were well dispersed into the polypropylene matrix, particularly in the nano composites obtained by the support system (route 2).

  2. Polypropylene Nanocomposites Obtained by In Situ Polymerization Using Metallocene Catalyst: Influence of the Nanoparticles on the Final Polymer Morphology

    Directory of Open Access Journals (Sweden)

    Paula Zapata

    2012-01-01

    Full Text Available Polypropylene nanocomposites containing silica nanospheres based on the sol-gel methods were produced via in situ polymerization using a rac-Et(Ind2ZrCl2/methylaluminoxane (MAO system. Two different routes were used depending on the interaction between the silica nanoparticles with the catalytic system. In route 1 the nanoparticles were added together with the catalytic system (rac-Et(Ind2ZrCl2/(MAO directly into the reactor, and in route 2 the metallocene rac-Et(Ind2ZrCl2 was supported on silica nanospheres pretreated with (MAO. SEM images show that when the nanospheres were added by both routes, they were replicated in the final polymer particle morphology; this phenomenon was more pronounced for PP obtained by route 2. The polypropylene (PP nanocomposites obtained by both routes had a slightly higher percent crystallinities and crystallinity temperatures than pure PP. Transmission electron microscopy (TEM images show that the nanospheres were well dispersed into the polypropylene matrix, particularly in the nanocomposites obtained by the support system (route 2.

  3. Tensile strength characteristics of polypropylene composites reinforced with stone groundwood fibers from softwood

    OpenAIRE

    López, Joan Pere; Méndez González, José Alberto; Espinach Orús, Xavier; Julián Pérez, Fernando; Mutjé Pujol, Pere; Vilaseca Morera, Fabiola

    2012-01-01

    The behavior of stone groundwood / polypropylene injection-molded composites was evaluated with and without coupling agent. Stone groundwood (SGW) is a fibrous material commonly prepared in a high yield process and mainly used for papermaking applications. In this work, the use of SGW fibers was explored as a reinforcing element of polypropylene (PP) composites. The surface charge density of the composite components was evaluated, as well as the fiber’s length and diameter inside the composit...

  4. Polypropylene /Aspen/ liquid polybutadienes composites: maximization of impact strength, tensile and modulus by statistical experimental design

    Czech Academy of Sciences Publication Activity Database

    Kokta, B. V.; Fortelný, Ivan; Kruliš, Zdeněk; Horák, Zdeněk; Michálková, Danuše

    2005-01-01

    Roč. 99, - (2005), s. 10-11 ISSN 0009-2770. [International Conference on Polymeric Materials in Automotive , Slovak Rubber Conference /17./. 10.5.2005-12.5.2005, Bratislava] Institutional research plan: CEZ:AV0Z40500505 Keywords : polypropylene * Aspen-PP composite Subject RIV: CD - Macromolecular Chemistry

  5. Rheological behavior of nanocomposite HMSPP (High Melt Strength Polypropylene) obtained by the addition of clay 'chocolate' organophilizated as reinforcement agent; Comportamento reologico de nanocomposito de HMSPP (Polipropileno com alta resistencia do fundido) obtido pela adicao de argila 'chocolate' organofilizada como agente de reforco

    Energy Technology Data Exchange (ETDEWEB)

    Fermino, D. M.; Valenzuela-Diaz, F.R., E-mail: dmfermino@usp.com.br [Universidade de Sao Paulo (USP), Sao Paulo, SP (Brazil). Escola Politecnica. Dept. de Engenharia Metalurgica e de Materiais; Parra, D. F.; Lugao, A. B. [Instituto de Pesquisas Energeticas e Nucleares (IPEN/CNEN-SP), Sao Paulo, SP (Brazil). Centro de Quimica e Meio Ambiente

    2012-07-01

    The objective of this study is to obtain a nanocomposite with a bentonite treated in laboratory in comparison to a commercial bentonite and the study of their rheological behavior. The treatment of the sodium clay organophilic in laboratory it was well succeeded as the result of FTIR testing and there was formation of nanocomposites with intercalated clays as XRD assay. In the rheology assay there was increase in a complex viscosity in all of nanocomposite samples of HMSPP. There were small changes in G' module and G″ for nanocomposites. Only with these rheology results we can not say it is interleaved microcomposite or nanocomposite because the criteria of both were not fully met.

  6. Rheological behavior of nanocomposite HMSPP (High Melt Strength Polypropylene) obtained by the addition of clay 'chocolate' organophilizated as reinforcement agent; Comportamento reologico de nanocomposito de HMSPP (Polipropileno com alta resistencia do fundido) obtido pela adicao de argila 'chocolate' organofilizada como agente de reforco

    Energy Technology Data Exchange (ETDEWEB)

    Fermino, D.M.; Valenzuela-Diaz, F.R., E-mail: dmfermino@usp.com.br [Universidade de Sao Paulo (USP), Sao Paulo, SP (Brazil). Escola Politecnica. Dept. de Engenharia Metalurgica e de Materiais; Parra, D.F.; Lugao, A.B. [Instituto de Pesquisas Energeticas e Nucleares (IPEN/CNEN-SP), Sao Paulo, SP (Brazil). Centro de Quimica e Meio Ambiente

    2012-07-01

    The objective of this study is to obtain a nanocomposite with a bentonite treated in laboratory in comparison to a commercial bentonite and the study of their rheological behavior. The treatment of the sodium clay organophilic in laboratory it was well succeeded as the result of FTIR testing and there was formation of nanocomposites with intercalated clays as XRD assay. In the rheology assay there was increase in a complex viscosity in all of nanocomposite samples of HMSPP. There were small changes in G' module and G″ for nanocomposites. Only with these rheology results we can not say it is interleaved microcomposite or nanocomposite because the criteria of both were not fully met.

  7. Strength and fracture energy of foamed concrete incorporating rice husk ash and polypropylene mega-mesh 55

    Science.gov (United States)

    Jaini, Z. M.; Rum, R. H. M.; Boon, K. H.

    2017-10-01

    This paper presents the utilization of rice husk ash (RHA) as sand replacement and polypropylene mega-mesh 55 (PMM) as fiber reinforcement in foamed concrete. High pozzolanic reaction and the ability to become filler make RHA as a strategic material to enhance the strength and durability of foamed concrete. Furthermore, the presence of PMM optimizes the toughness of foamed concrete in resisting shrinkage and cracking. In this experimental study, cube and cylinder specimens were prepared for the compression and splitting-tensile tests. Meanwhile, notched beam specimens were cast for the three-point bending test. It was found that 40% RHA and 9kg/m3 PMM contribute to the highest strength and fracture energy. The compressive, tensile and flexural strengths are 32MPa, 2.88MPa and 6.68MPa respectively, while the fracture energy achieves 42.19N/m. The results indicate high potential of RHA and PMM in enhancing the mechanical properties of foamed concrete.

  8. High improvement in trap level density and direct current breakdown strength of block polypropylene by doping with a β-nucleating agent

    Science.gov (United States)

    Zhang, Chong; Zha, Jun-Wei; Yan, Hong-Da; Li, Wei-Kang; Dang, Zhi-Min

    2018-02-01

    Polypropylene is one kind of eco-friendly insulating material, which has attracted more attention for use in high voltage direct current (HVDC) insulation due to the long-distance transmission, low loss, and recyclability. In this work, the morphology and thermal and electrical properties of the block polypropylene with various β-nucleating agent (β-NA) contents were investigated. The relative fraction of the β-crystal can reach 64.7% after adding 0.05 wt. % β-NA. The β-NA also greatly reduced the melting point and improved the crystallization temperature. The electrical property results showed that the alternating and direct current breakdown strength and conduction current were obviously improved. In addition, space charge accumulation was significantly suppressed by introducing the β-NA. This work provides an attractive strategy of design and fabrication of polypropylene for HVDC application.

  9. Autoclaved Sand-Lime Products with a Polypropylene Mesh

    Science.gov (United States)

    Kostrzewa, Paulina; Stępień, Anna

    2017-10-01

    The paper presents the results of the research on modifications of silicate bricks with a polypropylene mesh and their influence on physical, mechanical and microstructural properties of such bricks. The main goal of the paper was to determine effects of the polypropylene mesh on sand-lime product parameters. The analysis has focused on compressive strength, water absorption, bulk density and structural features of the material. The obtained product is characterized by improved basic performance characteristics compared to traditional silicate products. Using the polypropylene mesh increased compressive strength by 25% while decreasing the product density. The modified products retain their form and do not disintegrate after losing their bearing capacity.

  10. Influence of polypropylene fibres on the tensile strength and thermal properties of various densities of foamed concrete

    Science.gov (United States)

    Jhatial, Ashfaque Ahmed; Inn, Goh Wan; Mohamad, Noridah; Johnson Alengaram, U.; Mo, Kim Hung; Abdullah, Redzuan

    2017-11-01

    As almost half of the world’s population now lives in the urban areas, the raise in temperature in these areas has necessitated the development of thermal insulating material. Conventional concrete absorbs solar radiation during the daytime while releasing it at night causing raise in temperature in urban areas. The thermal conductivity of 2200 kg/m3 density conventional concrete is 1.6 W/mK. Higher the thermal conductivity value, greater the heat flow through the material. To reduce this heat transfer, the construction industry has turned to lightweight foamed concrete. Foamed concrete, due to its air voids, gives excellent thermal properties and sound absorption apart from fire-resistance and self-leveling properties. But due to limited studies on different densities of foamed concrete, the thermal properties are not understood properly thus limiting its use as thermal insulating material. In this study, thermal conductivity is determined for 1400, 1600 and 1800 kg/m3 densities of foamed concrete. 0.8% of Polypropylene fibres (PP) is used to reinforce the foamed concrete and improve the mechanical properties. Based upon the results, it was found that addition of PP fibres enhances the tensile strength and slightly reduced the thermal conductivity for lower densities, while the reverse affect was noticed in 1800 kg/m3 density.

  11. The use of radiation for the production of high melt strength polypropylene

    International Nuclear Information System (INIS)

    Lugao, A.B.; Cardoso, E.C.L.; Hustzler, B.; Tokumoto, S.; Mendes, A.N.F.

    2001-01-01

    PP suffers from low melt strength, i.e., the melted PP does not exhibits an increase in resistance to stretching during elongation. It is well known that the melt-strength properties of a polymer increase with molecular weight and with long chain branching due to the increase in the entanglement level (high melt strength PP-HMSPP). In spite of been the most fast growing polymeric commodity nowadays those new grades of PP and its development have been barely studied and its general chemical characterization have been even less studied with few exceptions. HMSPP as proposed by Montell patents are produced by low temperature and low dose irradiation of high molecular weight isotatica PP in N 2 atmosphere. So the well-known reactions would be mostly degradation and crosslinking. Degradation however is supposed to be the first and more intense reaction a the initial steps as already shown. So, according to Montell patents, another reaction is likely to occur, branching or T links competing with crosslinkings or H links. Radical are likely to decay very fast in amorphous phase, but under annealing the radicals entrapped in the crystal phase is likely to move to the boundary and react. The group of professor Silverman has already hypothesized in T links formation and also studied the radical decay of PP. It is easy to understand the difficulties in differentiate Hs from Ts links and even these links if in very small amount from the bulk or from virgin polymer, as the Ts links and even these links if in very small amount from the bulk or from virgin polymer, as the chemical groups and links are chemically speaking essentially the same

  12. Study of mechanical, rheological and thermal properties of nanocomposite HMSPP (high melt strength polypropylene) with Brazilian bentonite; Estudo das propriedades mecanicas, reologicas e termicas de nanocomposito de HMSPP (polipropileno com alta resistencia do fundido) com uma bentonita brasileira

    Energy Technology Data Exchange (ETDEWEB)

    Fermino, Danilo Marin

    2011-07-01

    This work concerns to the study of the mechanical, thermal and rheological behavior of the nano composite HMSPP - Polypropylene High Melt Strength (obtained at a dose of 12.5 kGy) and a bentonite clay Brazilian Paraiba, known as 'Chocolate' in concentrations of 5 and 10% by weight, comparison of to one American Clay, Cloisite 20A nanocomposite was done. Agent compatibilizer polypropylene-graft, known as maleic anhydride (PP-g-AM) was addict 3% concentration thought technique melt intercalation using a twin-screw extruder and the specimens were prepared by injection process. The mechanical behavior was evaluated by strength, flexural strength and impact tests. The thermal behavior was evaluated by the techniques of differential scanning calorimetry (DSC) and thermogravimetry (TGM). The rheological behavior was evaluated in rheometer. The morphology of the nanocomposites was studied by the technique of scanning electron microscopy (SEM). The organophilic bentonite and the nanocomposites were characterized by X-ray diffraction (XRD) and infrared (FTIR). (author)

  13. Study of mechanical, rheological and thermal properties of nanocomposite HMSPP (high melt strength polypropylene) with Brazilian bentonite; Estudo das propriedades mecanicas, reologicas e termicas de nanocomposito de HMSPP (polipropileno com alta resistencia do fundido) com uma bentonita brasileira

    Energy Technology Data Exchange (ETDEWEB)

    Fermino, Danilo Marin

    2011-07-01

    This work concerns to the study of the mechanical, thermal and rheological behavior of the nano composite HMSPP - Polypropylene High Melt Strength (obtained at a dose of 12.5 kGy) and a bentonite clay Brazilian Paraiba, known as 'Chocolate' in concentrations of 5 and 10% by weight, comparison of to one American Clay, Cloisite 20A nanocomposite was done. Agent compatibilizer polypropylene-graft, known as maleic anhydride (PP-g-AM) was addict 3% concentration thought technique melt intercalation using a twin-screw extruder and the specimens were prepared by injection process. The mechanical behavior was evaluated by strength, flexural strength and impact tests. The thermal behavior was evaluated by the techniques of differential scanning calorimetry (DSC) and thermogravimetry (TGM). The rheological behavior was evaluated in rheometer. The morphology of the nanocomposites was studied by the technique of scanning electron microscopy (SEM). The organophilic bentonite and the nanocomposites were characterized by X-ray diffraction (XRD) and infrared (FTIR). (author)

  14. Improvement of the T-peel Strength of Polypropylene Adhesion Joints by Surface Photografting Pre-Treatment with Methyl Methacrylate

    Science.gov (United States)

    Balart, R.; Sánchez-Nácher, L.; Balart, J.; Fombuena, V.; España, J. M.

    2010-06-01

    Although polypropylene is one of the most used polymers at industrial level due to good balanced properties, it presents some restrictions in applications that require good adhesion properties as well as coating and painting. These restrictions are related to its non polar nature which leads to low wetting properties. So that, in most cases, it is necessary a previous surface pre-treatment in order to improve adhesion properties. These surface treatments could be physical or chemical. Among the wide variety of physical processes, plasma technologies are useful from both technical and environmental points of view. If we take into account economic considerations, chemical processes are interesting due to low cost equipment and procedures. In particular, we have used photografting of methyl methacrylate (MMA) monomer on polypropylene substrates with UV radiation and initiators. This process is useful to promote chemical modification of polypropylene surface by grafting MMA monomers into polypropylene polymer chains. Due to polarity of some groups in MMA monomers, it is possible to increase surface wettability thus promoting a remarkable increase in adhesion properties of polypropylene. In this work, changes in wettability of polypropylene surfaces in terms of the exposure time to UV radiation in presence of MMA monomers and initiators has been investigated. Furthermore, chemical changes have been characterized by FTIR analysis and mechanical performance of adhesion joints has been evaluated by T-peel tests.

  15. Synthesis and characterization of stimuli-responsive polypropylene containing N-vinylcaprolactam and N-vinylimidazole obtained by ionizing radiation

    Energy Technology Data Exchange (ETDEWEB)

    Zavala-Lagunes, Edgar [Departamento de Química de Radiaciones y Radioquímica, Instituto de Ciencias Nucleares, Universidad Nacional Autónoma de México, Circuito Exterior, Ciudad Universitaria, México, D.F. 04510 (Mexico); Ruiz, Juan-Carlos [División de Ciencias Básicas e Ingeniería, Depto. de Ingeniería de Procesos e Hidráulica, Universidad Autónoma Metropolitana-Iztapalapa, Av. San Rafael Atlixco No. 186, México, D.F. 09340 (Mexico); Varca, Gustavo H.C. [Instituto de Pesquisas Energéticas e Nucleares (IPEN/CNEN-SP), Av. Prof. Lineu Prestes, 2242, Cidade Universitária, 05508-000 São Paulo, SP (Brazil); Bucio, Emilio, E-mail: ebucio@nucleares.unam.mx [Departamento de Química de Radiaciones y Radioquímica, Instituto de Ciencias Nucleares, Universidad Nacional Autónoma de México, Circuito Exterior, Ciudad Universitaria, México, D.F. 04510 (Mexico)

    2016-10-01

    Polypropylene films were grafted with thermo-responsive N-vinylcaprolactam and pH-responsive N-vinylimidazole polymers by means of gamma radiation using pre-irradiation and direct methods, in order to functionalize the films with thermo- and/or pH-responsiveness. The dependence of grafting yield on parameters such as co-monomer concentration, pre-irradiation dose, temperature, and reaction time was evaluated. The samples were characterized by Fourier transform infrared and X-ray photoelectron spectroscopies, differential scanning calorimetry, thermogravimetric analysis, swelling studies in different solvents, and water contact angle. The grafted copolymers presented thermo- and pH-sensitiveness, highlighting their potential as advanced biomaterials, capable of providing adequate environment for hosting and sustained release of antimicrobial drugs bearing cationic moieties, such as groups of diclofenac, while still exhibiting good cytocompatibility. - Highlights: • Development of novel and versatile thermo and/or pH responsive PP based materials • Responsive monomers were grafted by radiation methods to functionalize polypropylene. • Thermo-responsive N-vinylcaprolactam and pH-responsive N-vinylimidazole were selected. • Grafting was performed using gamma irradiation by pre-irradiation and direct methods. • Potential biomedical applications comprise smart biomaterials for drug loading.

  16. The role of testing realism on experimentally obtained stereotype strength.

    Science.gov (United States)

    Hoffmann, Errol R; Whitfield, Richard C

    2011-01-01

    It has been shown (Hoffmann 2009) that pencil-and-paper tests, when used to determine stereotype strength, may yield data quite different to that obtained from hardware tests. The purpose of this research was to determine the level of realism required in order to have stereotypes that are consistent with real-world values. It is surprising that there does not appear to be any published research addressing this problem; all previous researches have considered either paper/pencil or hardware tests or sometimes both, but no level of simulation in between these techniques. In order to determine the effect of level of testing realism, a specific example was chosen to test, that of water tap operation stereotypes. Tests used verbal questioning, photographs of tap arrangements, a partial hardware arrangement and finally a full hardware setup. The results of these four levels of realism were very different and illustrated that, only with a full realistic simulation, did participants respond as might be expected in a real-world environment, illustrating the importance of testing realism when determining population stereotypes. This result has strong implications for product designers when selecting appropriate layouts of displays and controls and the linkages relating these. Copyright © 2010 Elsevier Ltd and The Ergonomics Society. All rights reserved.

  17. Influence of the elastomeric polypropylene addition on the properties of commercial metallocenic polypropylene

    Directory of Open Access Journals (Sweden)

    Marques Maria de Fátima V.

    2001-01-01

    Full Text Available Polypropylene with special properties can be obtained by metallocenic catalysts. These catalytic systems represent the beginning of a new age in polyolefins technology. In this work, the influence of the addition of a syndiotactic polypropylene (s-PP on the processability and mechanical properties of a commercial isotactic polypropylene (i-PP obtained by metallocenic catalysts was evaluated. Increasing addition of s-PP promoted better processability, with an increase in the impact strength and a decrease in the stress at break. A reduction of the crystallinity in the polymeric blends was verified. The more significant influence of the s-PP addition was observed for the mi-PP, compared to the ZNi-PP.

  18. Rheological properties of polypropylene nanocomposites

    International Nuclear Information System (INIS)

    Oliveira, Camila F. de P.; Demarquette, Nicole R.

    2009-01-01

    In this work, composites of polypropylene with a master batch to obtain clay containing nano composites were obtained. The materials were characterized by X ray diffraction, small angle X-ray scattering and by rheological analysis. (author)

  19. Examining the influence of injection speed and mould temperature on the tensile strength of polypropylene and ABS

    DEFF Research Database (Denmark)

    Aarøe, Esben Raahede; Blaimschein, Karl Stephan; Deker, Lasse

    This report is the final task of course “41738 Experimental Plastics Technology” in the three weeks period of June 2009 at DTU, IPL. The aim of this project has been to investigate the ultimate tensile strength behaviour of two different polymers, with different structural composition, by varying...... the injection speed and the mold temperature independently while keeping all other process parameters fixed. In addition the scaling from production of large to small geometries has been investigated by doing two parallel productions and test setups of respectively injection moulded and micro injection moulded...... specimens. After production and tensile testing the specimens were examined with a microscope to underpin conclusions from the tensile test data. It was experienced that the injection speed in general increased the the tensile strength by orienting the polymeric-chains lengthwise in the specimens and thus...

  20. Kenaf/PP and EFB/PP: Effect of fibre loading on the mechanical properties of polypropylene composites

    Science.gov (United States)

    Anuar, N. I. S.; Zakaria, S.; Harun, J.; Wang, C.

    2017-07-01

    Kenaf and empty fruit bunch (EFB) fibre which are the important natural fibres in Malaysia were studied as nonwoven polymer composites. The effect of fibre loading on kenaf polypropylene and EFB polypropylene nonwoven composite was studied at different mixture ratio. Kenaf polypropylene nonwoven composite (KPNC) and EFB polypropylene nonwoven composite (EPNC) were prepared by carding and needle-punching techniques, followed by a compression moulding at 6 mm thickness. This study was conducted to identify the optimum fibre loading of nonwoven polypropylene composite and their effect on the mechanical strength. The study was designed at 40%, 50%, 60% and 70% of fibre content in nonwoven mat and composite. The tensile strength, flexural strength and compression strength were tested to evaluate the composite mechanical properties. It was found that the mechanical properties for both kenaf and EFB nonwoven composites were influenced by the fibre content. KPNC showed higher mechanical strength than EPNC. The highest flexural strength was obtained at 60% KPNC and the lowest value was showed by 40% EPNC. The tensile and flexural strength for both KPNC and EPNC decreased after the fibre loading of 60%.

  1. Study on the effect of testing machine rigidity on strength and ductility temperature dependences obtained

    International Nuclear Information System (INIS)

    Krashchenko, V.P.; Statsenko, V.E.; Rudnitskij, N.P.

    1984-01-01

    Investigation procedures are described for rigidity of testing machines and mechanical properties of tantalum and nickel in the temperature range 293-1873K. Temperature dependences are presented for strength characteristics of the investigated materials obtained with the use of installations of different rigidity. Dependence analysis is carried out and recommendations are given as to the characteristics application

  2. Thermal analysis of polypropylene modified by gamma irradiation composites under outdoor conditions

    International Nuclear Information System (INIS)

    Komatsu, Luiz G.H.; Oliani, Washington L.; Lugao, Ademar B.; Parra, Duclerc F.

    2015-01-01

    This work reports the influence of the clay in the degradation process of the HMSPP.The polypropylene (PP) was irradiated under acetylene atmosphere in gamma irradiation source ( 60 Co) to obtain the HMSPP (high melt strength polypropylene). Composites of HMSPP were processed in twin-screw extruder with clay Cloisite 20A and Maleic Anhydride (PP-g-MA) as coupling agent. The obtained composites were exposed under outdoor conditions for 6 months. The ageing effects were characterized by Differential Scanning Calorimetry (DSC), Thermogravimetry Analysis (TGA). Chemical oxidation was evaluated by Carbonyl Index (IC) through infrared Spectroscopy (FT-IR). The results showed correlation between carbonyl index and ageing time. (author)

  3. Thermal analysis of polypropylene modified by gamma irradiation composites under outdoor conditions

    Energy Technology Data Exchange (ETDEWEB)

    Komatsu, Luiz G.H.; Oliani, Washington L.; Lugao, Ademar B.; Parra, Duclerc F., E-mail: dfparra@ipen.br [Instituto de Pesquisas Energeticas e Nucleares (IPEN/CNEN-SP), Sao Paulo, SP (Brazil)

    2015-07-01

    This work reports the influence of the clay in the degradation process of the HMSPP.The polypropylene (PP) was irradiated under acetylene atmosphere in gamma irradiation source ({sup 60}Co) to obtain the HMSPP (high melt strength polypropylene). Composites of HMSPP were processed in twin-screw extruder with clay Cloisite 20A and Maleic Anhydride (PP-g-MA) as coupling agent. The obtained composites were exposed under outdoor conditions for 6 months. The ageing effects were characterized by Differential Scanning Calorimetry (DSC), Thermogravimetry Analysis (TGA). Chemical oxidation was evaluated by Carbonyl Index (IC) through infrared Spectroscopy (FT-IR). The results showed correlation between carbonyl index and ageing time. (author)

  4. Fracture properties of high-strength concrete obtained by direct modification of structure

    Directory of Open Access Journals (Sweden)

    Solodkyy Serhiy

    2017-01-01

    Full Text Available High-strength concrete is effectively used worldwide in the last three decades, but it is more brittle in comparison with normal strength concretes. Partial substitution of cement in concrete by active mineral additives and usage of chemical admixture of plasticizing and air-entraining action can considerably change their fracture properties. The obtained results show that the increase of the fracture properties is observed in concretes modified with chemical admixtures incorporating mineral additives such as zeolite and limestone due to consolidation of the concrete microstructure. Densification takes place as a result of limiting the amount of calcium hydroxide (CH due to its reaction with active silica included in the zeolite and the formation of larger amounts of hydrated calcium silicates of tobermorite type as well as calcium hydroaluminate and hydrocarboaluminate with the simultaneous adsorption modification of hydrated products by chemical admixtures.

  5. The Effect of Tool Pin Shape of Friction Stir Welding (FSW) on Polypropylene

    Science.gov (United States)

    Nik, Z. C.; Ishak, M.; Othman, N. H.

    2017-09-01

    This experiment deals with similar joining of polypropylene (PP) with thickness of 3 mm was carried out by using friction stir welding (FSW) technique. The process parameters, rotational speed, welding speed and tilt angle were fixed of experiments. The tool geometry shapes were the main parameters which were taken into consideration. The optimum designs of tool geometry shape were determined with reference to tensile strength of the joint. During the tensile testing experiment, the results show that all fractured occurs in the heat-affected zone (HAZ) on the polypropylene (PP). Results show that the optimum design can be obtained with same rotational speed, welding speed and tilt angle.

  6. Study of gel formation in polypropylene modified by gamma irradiation

    International Nuclear Information System (INIS)

    Oliani, W.L.; Parra, D.F.; Fermino, D.M.; Lima, L.F.C.P.; Lugao, A.B.; Riella, H.G.

    2010-01-01

    The linearity of the chains of iPP (isotactic polypropylene) confers to this, low melt strength. This fact limits the use of iPP in processes that demand high stretching. The graft of branches confers improvements in its extensional viscosity, resulting in Polypropylene with High Melt Strength (HMS-PP). Preparation process of the HMS-PP, included iPP in pellets, conditioned in plastic container containing acetylene under pressure of 110 kPa and radiation with γ source of 60 Co in the doses of 5, 12.5 and 20 kGy. The gel fraction of the samples was determined by the extraction of soluble components in xylene under boiling for 12 hours at 138 deg C. The soluble part of the samples was decanted with the total volatilization of the xylene to the room temperature (25 deg C) and deposition in glass blades. These samples had been characterized by Optic Microscopy, Scanning Electron Microscopy and Infrared Spectroscopy. In this study of the morphology, we obtained the formation of gel and microgel of polypropylene with higher incidence in HMS-PP 20 kGy. (author)

  7. Polypropylene and polycarbonate radiosterilization: effects on the stress resistance

    International Nuclear Information System (INIS)

    Musico Filho, W.; Terence, M.C.; Guedes, S.M.L.; Araujo, E.S. de

    1994-01-01

    The gamma radiation effect on polymer sterilization used in the fabrication of medical supplies, national polycarbonate and polypropylene, was studied in function of the tensile strength. During the polycarbonate irradiation occur the scission of polymer chain and the crosslinking/scission of the polypropylene, but in the sterilization dose, 25 kGy, does not occur expressive changes in the tensile strength. After the polypropylene sterilization the tensile strength continues increasing as consequence of the crosslinking. Since the sixth day the oxidation reaction predominates as consequence of the radical migration to the amorphous region. (author). 7 refs, 6 figs

  8. Validity of maximal isometric knee extension strength measurements obtained via belt-stabilized hand-held dynamometry in healthy adults.

    Science.gov (United States)

    Ushiyama, Naoko; Kurobe, Yasushi; Momose, Kimito

    2017-11-01

    [Purpose] To determine the validity of knee extension muscle strength measurements using belt-stabilized hand-held dynamometry with and without body stabilization compared with the gold standard isokinetic dynamometry in healthy adults. [Subjects and Methods] Twenty-nine healthy adults (mean age, 21.3 years) were included. Study parameters involved right side measurements of maximal isometric knee extension strength obtained using belt-stabilized hand-held dynamometry with and without body stabilization and the gold standard. Measurements were performed in all subjects. [Results] A moderate correlation and fixed bias were found between measurements obtained using belt-stabilized hand-held dynamometry with body stabilization and the gold standard. No significant correlation and proportional bias were found between measurements obtained using belt-stabilized hand-held dynamometry without body stabilization and the gold standard. The strength identified using belt-stabilized hand-held dynamometry with body stabilization may not be commensurate with the maximum strength individuals can generate; however, it reflects such strength. In contrast, the strength identified using belt-stabilized hand-held dynamometry without body stabilization does not reflect the maximum strength. Therefore, a chair should be used to stabilize the body when performing measurements of maximal isometric knee extension strength using belt-stabilized hand-held dynamometry in healthy adults. [Conclusion] Belt-stabilized hand-held dynamometry with body stabilization is more convenient than the gold standard in clinical settings.

  9. Effect of Hybrid Fibers on the Mechanical Properties of High Strength Concrete

    Directory of Open Access Journals (Sweden)

    Hamid H. Hussein, Saeed K. Rejeb Hayder T. Abd

    2014-04-01

    Full Text Available In this study, high strength concrete of 75 MPa compressive strength was investigated. The experimental program was designed to study the effect of fibers and hybrid fibers (steel and polypropylene fibers on the fresh (workability and wet density and hardened properties (compressive strength, splitting strength, flexural strength and dry density of high strength concrete. Results show that decreases in slump flow of all concrete mixtures containing steel, polypropylene and hybrid fibers compared with control mix (0% fiber. Hybrid high strength concrete with steel and polypropylene fibers showed superior compressive, splitting, flexural strengths over the others concrete without or with single fibers content. The test results indicate that the maximum increase in compressive and flexural strengths are obtains with the hybridization ratio (70%steel + 30% polypropylene and were equal to 14.54% and 23.34% respectively, compared with the control mix. While, the maximum increase in splitting tensile strength with (100% steel fiber + 0 polypropylene is 21.19%. 

  10. Modelling of Creep and Stress Relaxation Test of a Polypropylene Microfibre by Using Fraction-Exponential Kernel

    Directory of Open Access Journals (Sweden)

    Andrea Sorzia

    2016-01-01

    Full Text Available A tensile test until breakage and a creep and relaxation test on a polypropylene fibre are carried out and the resulting creep and stress relaxation curves are fit by a model adopting a fraction-exponential kernel in the viscoelastic operator. The models using fraction-exponential functions are simpler than the complex ones obtained from combination of dashpots and springs and, furthermore, are suitable for fitting experimental data with good approximation allowing, at the same time, obtaining inverse Laplace transform in closed form. Therefore, the viscoelastic response of polypropylene fibres can be modelled straightforwardly through analytical methods. Addition of polypropylene fibres greatly improves the tensile strength of composite materials with concrete matrix. The proposed analytical model can be employed for simulating the mechanical behaviour of composite materials with embedded viscoelastic fibres.

  11. Monotonic and cyclic responses of impact polypropylene and continuous glass fiber-reinforced impact polypropylene composites at different strain rates

    KAUST Repository

    Yudhanto, Arief

    2016-03-08

    Impact copolymer polypropylene (IPP), a blend of isotactic polypropylene and ethylene-propylene rubber, and its continuous glass fiber composite form (glass fiber-reinforced impact polypropylene, GFIPP) are promising materials for impact-prone automotive structures. However, basic mechanical properties and corresponding damage of IPP and GFIPP at different rates, which are of keen interest in the material development stage and numerical tool validation, have not been reported. Here, we applied monotonic and cyclic tensile loads to IPP and GFIPP at different strain rates (0.001/s, 0.01/s and 0.1/s) to study the mechanical properties, failure modes and the damage parameters. We used monotonic and cyclic tests to obtain mechanical properties and define damage parameters, respectively. We also used scanning electron microscopy (SEM) images to visualize the failure mode. We found that IPP generally exhibits brittle fracture (with relatively low failure strain of 2.69-3.74%) and viscoelastic-viscoplastic behavior. GFIPP [90]8 is generally insensitive to strain rate due to localized damage initiation mostly in the matrix phase leading to catastrophic transverse failure. In contrast, GFIPP [±45]s is sensitive to the strain rate as indicated by the change in shear modulus, shear strength and failure mode.

  12. Additive manufacturing with polypropylene microfibers.

    Science.gov (United States)

    Haigh, Jodie N; Dargaville, Tim R; Dalton, Paul D

    2017-08-01

    The additive manufacturing of small diameter polypropylene microfibers is described, achieved using a technique termed melt electrospinning writing. Sequential fiber layering, which is important for accurate three-dimensional fabrication, was achieved with the smallest fiber diameter of 16.4±0.2μm obtained. The collector speed, temperature and melt flow rate to the nozzle were optimized for quality and minimal fiber pulsing. Of particular importance to the success of this method is appropriate heating of the collector plate, so that the electrostatically drawn filament adheres during the direct-writing process. By demonstrating the direct-writing of polypropylene, new applications exploiting the favorable mechanical, stability and biocompatible properties of this polymer are envisaged. Copyright © 2017. Published by Elsevier B.V.

  13. Development of unfolding method to obtain pin-wise source strength distribution from PWR spent fuel assembly measurement

    International Nuclear Information System (INIS)

    Sitompul, Yos Panagaman; Shin, Hee-Sung; Park, Se-Hwan; Oh, Jong Myeong; Seo, Hee; Kim, Ho Dong

    2013-01-01

    An unfolding method has been developed to obtain a pin-wise source strength distribution of a 14 × 14 pressurized water reactor (PWR) spent fuel assembly. Sixteen measured gamma dose rates at 16 control rod guide tubes of an assembly are unfolded to 179 pin-wise source strengths of the assembly. The method calculates and optimizes five coefficients of the quadratic fitting function for X-Y source strength distribution, iteratively. The pin-wise source strengths are obtained at the sixth iteration, with a maximum difference between two sequential iterations of about 0.2%. The relative distribution of pin-wise source strength from the unfolding is checked using a comparison with the design code (Westinghouse APA code). The result shows that the relative distribution from the unfolding and design code is consistent within a 5% difference. The absolute value of the pin-wise source strength is also checked by reproducing the dose rates at the measurement points. The result shows that the pin-wise source strengths from the unfolding reproduce the dose rates within a 2% difference. (author)

  14. Fracture behavior of polypropylene/clay nanocomposites.

    Science.gov (United States)

    Chen, Ling; Wang, Ke; Kotaki, Masaya; Hu, Charmaine; He, Chaobin

    2006-12-01

    Polypropylene (PP)/clay nanocomposites have been prepared via a reactive compounding approach with an epoxy based masterbatch. Compared with PP and common PP/organoclay nanocomposites, the PP/clay nanocomposites based on epoxy/clay masterbatch have higher impact strength. The phenomenon can be attributed to the epoxy phase dispersed uniformly in the PP matrix, which may act as impact energy absorber and helps to form a large damage zone, thus a higher impact strength value is achieved.

  15. Simple method of obtaining the band strengths in the electronic spectra of diatomic molecules

    International Nuclear Information System (INIS)

    Gowda, L.S.; Balaji, V.N.

    1977-01-01

    It is shown that relative band strengths of diatomic molecules for which the product of Franck-Condon factor and r-centroid is approximately equal to 1 for (0,0) band can be determined by a simple method which is in good agreement with the smoothed array of experimental values. Such values for the Swan bands of the C 2 molecule are compared with the band strengths of the simple method. It is noted that the Swan bands are one of the outstanding features of R- and N-type stars and of the heads of comets

  16. Solid-state drawing of post-consumer isotactic poly(propylene): effect of melt filtration and carbon black on structural and mechanical properties

    NARCIS (Netherlands)

    Luijsterburg, B.J.; Jobse, P.S.; Spoelstra, A.B.; Goossens, J.G.P.

    2016-01-01

    Post-consumer plastic waste obtained via mechanical recycling is usually applied in thick-walled products, because of the low mechanical strength due to the presence of contaminants. In fact, sorted post-consumer isotactic poly(propylene) (i-PP) can be considered as a blend of 95% i-PP and 5%

  17. Conductive polypropylene composites

    International Nuclear Information System (INIS)

    Koszkul, J.

    1997-01-01

    The results of studies on polypropylene composites with three sorts of Polish-made carbon blacks were presented. It was found that composite of 20% black content had properties of an electrically conducting material

  18. Radiation crosslinking of polypropylene

    International Nuclear Information System (INIS)

    Nojiri, A.; Sawasaki, T.

    1984-01-01

    The radiation crosslinking of polypropylene with several kinds of polyfunctional monomers has been examined, and it has been clarified that the enhanced crosslinking may be classified into two types. In particular, the irradiation crosslinking process of polypropylene containing a polyfunctional monomer having an acryloyloxy group giving a specific gel - dose curve has been studied by infrared absorption spectrum and oxygen absorptivity measurement in comparison with the non-enhanced system. (author)

  19. Radiation resistant modified polypropylene

    International Nuclear Information System (INIS)

    Bojarski, J.; Zimek, Z.

    1997-01-01

    Radiation technology for production of radiation resistant polypropylene for medical use has been presented. The method consists in radiation induced copolymerization of polypropylene with ethylene and addition of small amount of copolymer of polyethylene and vinyl acetate. The material of proposed composition has a very good mechanical properties and elevated radiation resistivity decided on possibility of radiosterilization of products made of this material and designed for medical use. 3 figs, 3 tabs

  20. Echo intensity obtained from ultrasonography images reflecting muscle strength in elderly men

    Directory of Open Access Journals (Sweden)

    Watanabe Y

    2013-07-01

    Full Text Available Yuya Watanabe,1 Yosuke Yamada,1,2 Yoshihiro Fukumoto,3 Tatsuro Ishihara,4 Keiichi Yokoyama,1 Tsukasa Yoshida,1 Motoko Miyake,1 Emi Yamagata,5 Misaka Kimura1 1Laboratory of Sports and Health Science, Kyoto Prefectural University of Medicine, Kyoto, Japan; 2Research Fellow, Japan Society for the Promotion of Science, Tokyo, Japan; 3Faculty of Rehabilitation, Kobe Gakuin University, Kobe, Japan; 4Faculty of Health and Sports Science, Doshisha University, Kyoto, Japan; 5Laboratory of Gerontological Nursing, Kyoto Prefectural University of Medicine, Kyoto, Japan Background: It is well known that loss of muscle mass (quantitative change is a major change that occurs with aging. Qualitative changes in skeletal muscle, such as increased intramuscular fat, also occur as one ages. Enhanced echo intensity (EI on ultrasonography images of skeletal muscle is believed to reflect muscle quality. Recent studies evaluating the quality of skeletal muscle using computer-aided gray scale analysis showed that EI is associated with muscle strength independently of age or muscle size in middle-aged and elderly women. The aim of the present study was to investigate whether muscle quality based on EI is associated with muscle strength independently of muscle size for elderly men. Methods: A total of 184 elderly men (65–91 years living independently in Kyoto, Japan, participated in this study. The EI, muscle thickness (MT, and subcutaneous fat thickness (FT of the anterior compartment of the right thigh were determined by assessing ultrasonography images. The maximum isometric torque of knee extension at a knee angle of 90° was measured. Results: The EI showed a significant negative correlation with muscle strength (r = -0.333, P < 0.001. Multivariate regression analysis revealed that the MT and EI of the knee extensor muscle were independently associated with maximum isometric knee extension strength. Even when partial correlation analysis was performed with age

  1. High strength Ni based composite reinforced by solid solution W(Al) obtained by powder metallurgy

    International Nuclear Information System (INIS)

    Zhao Bo; Zhu Changjun; Ma Xianfeng; Zhao Wei; Tang Huaguo; Cai Shuguang; Qiao Zhuhui

    2007-01-01

    The solid-solution-particle reinforced W(Al)-Ni composites were successfully fabricated by using mechanical alloying (MA) and hot-pressing (HP) technique when the content of Ni is between 45 wt% and 55 wt%. Besides, samples of various original component ratio of Al 50 W 50 to Ni have been fabricated, and the corresponding microcomponents and mechanical properties such as microhardness, ultimate tensile strength and elongation were characterized and discussed. The optimum ultimate tensile strength under the experiment conditions is 1868 MPa with elongation of 10.21% and hardness of 6.62 GPa. X-ray diffraction (XRD), FE-SEM and energy dispersive analysis of X-rays (EDS) were given to analysis the components and morphology of the composite bulk specimens

  2. Biodegradation of Polypropylene Nonwovens

    Science.gov (United States)

    Keene, Brandi Nechelle

    The primary aim of the current research is to document the biodegradation of polypropylene nonwovens and filament under composting environments. To accelerate the biodegradat ion, pre-treatments and additives were incorporated into polypropylene filaments and nonwovens. The initial phase (Chapter 2) of the project studied the biodegradation of untreated polypropylene with/without pro-oxidants in two types of composting systems. Normal composting, which involved incubation of samples in food waste, had little effect on the mechanical properties of additive-free spunbond nonwovens in to comparison prooxidant containing spunbond nonwovens which were affected significantly. Modified composting which includes the burial of samples with food and compressed air, the polypropylene spunbond nonwovens with/without pro-oxidants displayed an extreme loss in mechanical properties and cracking on the surface cracking. Because the untreated spunbond nonwovens did not completely decompose, the next phase of the project examined the pre-treatment of gamma-irradiation or thermal aging prior to composting. After exposure to gamma-irradiation and thermal aging, polypropylene is subjected to oxidative degradation in the presence of air and during storage after irradiat ion. Similar to photo-oxidation, the mechanism of gamma radiation and thermal oxidative degradation is fundamentally free radical in nature. In Chapter 3, the compostability of thermal aged spunbond polypropylene nonwovens with/without pro-oxidant additives. The FTIR spectrum confirmed oxidat ion of the polypropylene nonwovens with/without additives. Cracking on both the pro-oxidant and control spunbond nonwovens was showed by SEM imaging. Spunbond polypropylene nonwovens with/without pro-oxidants were also preirradiated by gamma rays followed by composting. Nonwovens with/without pro-oxidants were severely degraded by gamma-irradiation after up to 20 kGy exposure as explained in Chapter 4. Furthermore (Chapter 5), gamma

  3. Can Images Obtained With High Field Strength Magnetic Resonance Imaging Reduce Contouring Variability of the Prostate?

    International Nuclear Information System (INIS)

    Usmani, Nawaid; Sloboda, Ron; Kamal, Wafa; Ghosh, Sunita; Pervez, Nadeem; Pedersen, John; Yee, Don; Danielson, Brita; Murtha, Albert; Amanie, John; Monajemi, Tara

    2011-01-01

    Purpose: The objective of this study is to determine whether there is less contouring variability of the prostate using higher-strength magnetic resonance images (MRI) compared with standard MRI and computed tomography (CT). Methods and Materials: Forty patients treated with prostate brachytherapy were accrued to a prospective study that included the acquisition of 1.5-T MR and CT images at specified time points. A subset of 10 patients had additional 3.0-T MR images acquired at the same time as their 1.5-T MR scans. Images from each of these patients were contoured by 5 radiation oncologists, with a random subset of patients repeated to quantify intraobserver contouring variability. To minimize bias in contouring the prostate, the image sets were placed in folders in a random order with all identifiers removed from the images. Results: Although there was less interobserver contouring variability in the overall prostate volumes in 1.5-T MRI compared with 3.0-T MRI (p < 0.01), there was no significant differences in contouring variability in the different regions of the prostate between 1.5-T MRI and 3.0-T MRI. MRI demonstrated significantly less interobserver contouring variability in both 1.5-T and 3.0-T compared with CT in overall prostate volumes (p < 0.01, p = 0.01), with the greatest benefits being appreciated in the base of the prostate. Overall, there was less intraobserver contouring variability than interobserver contouring variability for all of the measurements analyzed. Conclusions: Use of 3.0-T MRI does not demonstrate a significant improvement in contouring variability compared with 1.5-T MRI, although both magnetic strengths demonstrated less contouring variability compared with CT.

  4. Effect of Mesoporous Silica and Hydroxyapatite Nanoparticles on the Tensile and Dynamic Mechanical Thermal Properties of Polypropylene and Polypropylene Foam

    Directory of Open Access Journals (Sweden)

    Alireza Albooyeh

    2014-12-01

    Full Text Available The main purpose of this paper is the experimental study on the tensile and dynamic - mechanical thermal properties of polypropylene (PP and polypropylene foam reinforced with mesoporous silica (MCM-41, hydroxyapatite (HA and the composite of mesoporous silica and hydroxyapatite (MCM41-HA nanoparticles. Nanocomposites and nanocomposite foams containing PP, maleic anhydride grafted polypropylene, different nanoparticles and chemical blowing agent (for foam samples are mixed using the melt-compounding technique in a twin-screw extruder. The results of the tests show that at the same nanoparticles content, all the nanofillers cause better mechanical properties than neat PP and PP foam. Also, due to the porous structure of the foam samples, these samples have the higher damping characteristics and lower tensile properties than the solid samples. Because of higher rigidity and higher strength of HA nanoparticles, the greatest increase in modulus and tensile strength occurs by adding these nanoparticles to neat PP and PP foam. The highest damping factor is obtained by adding MCM-41-HA nanoparticles to PP and PP foam, because of the porous nature of the MCM-41 particles which were reinforced by HA particles. The results of differential scanning calorimetry show that the addition of different nanoparticles does not have any significant effect on crystallinity and melting behavior of PP. Scanning electron microscopy images show that the nanomaterials were fine and uniformly dispersed within the polymer matrix. Furthermore, the addition of different nanoparticles to PP foam causes to increase the cell density, to reduce the cell sizes and to improve the cell sizes distribution. In this respect, the lowest cell sizes and the highest cell density are created by adding HA and MCM41-HA  nanopaticles to PP foams.

  5. Polypropylene reinforced with organophilic clay and brazilian nut fibers

    International Nuclear Information System (INIS)

    Rocha-Gomes, L.V.; Mondelo-Garcia, F.J.; Vaccioli, K.; Valera, S.T.; Silva-Valenzuela, M.G.; Valenzuela-Diaz, F.R.

    2014-01-01

    Polymer nanocomposites have been shown to possess better properties when compared with traditional composites. This study aims to investigate the effects of the addition of organophilic clay and Brazilian nut fiber on the polypropylene (PP). First, 5%, 10% and 20% PP/compatibilizer maleic anhydride (PP-g-MA) by weight was added to Pure PP, respectively. From the results, 5% PP-g-MA was defined for preparing the nanocomposites. Samples were prepared containing 5% PP / PP-g-MA reinforced with 5% organophilic Brazilian smectite clay and 5%, 10% and 15% Brazilian nut fiber. Specimens were tested for tensile strength and impact. The materials were characterized by laser diffraction particle size and X-ray diffraction, and the nanocomposites, by mechanical strength and impact. The best result was obtained by inserting 15% fiber. (author)

  6. Effect of polybutenes on mechanical and physical properties of polypropylene

    International Nuclear Information System (INIS)

    Nascimento, Uedson A. do; Timoteo, Gustavo Arante V.; Rabello, Marcelo S.

    2009-01-01

    This study investigated the effect of polybutene (PIB) of molecular weights ranging from 480 the 1.600 g/mol in polypropylene homopolymer. Compositions with 0, 3, 5 and 7% of PIB were prepared in internal mixer and compression moulded. The properties evaluated were: tensile strength, scanning electron microscopy (SEM), FTIR, X-ray diffraction (XRD) and melt flow index (IF). The results of mechanical tests showed that the presence of the plasticizer reduced the tensile strength, elastic modulus and hardness. The analysis of XRD showed a drop in the degree of crystallinity of PP/PIB blends. The micrographs obtained by SEM did not reveal the occurrence of the phase separation. The IF analysis confirm the effect of PIB as internal lubricant's, by increasing the rate of flow. (author)

  7. Synthesis And Thermal Characterization Of Polypropylene ...

    African Journals Online (AJOL)

    The present work investigates the heat transfer and specifically, thermal conductivity, diffusivity and specific heat in Aluminium composite materials. The composites were obtained by mixing polypropylene (PP) with oxidized Aluminium (Al) under various volume fractions. Two sizes of filler are used in the sample composite ...

  8. About the possibility of obtaining cementitious soil composites of high strength on the basis of belozems of carbonate composition

    Science.gov (United States)

    Karapetyan, K. A.; Hayroyan, S. G.; Manukyan, E. S.

    2018-04-01

    The problem of manufacturing high strength cementitious soils based on belozems of carbonate composition, which experience compression (no less than 10 MPa), without application of surface active substances is considered. The portland cement of type 400 was used as a binding agent to develop compositions of cementitious soil composites, and the ordinary pipe water was used to obtain solutions of cementitious soils. The chemical and mineralogical composition of the initial ingredients and the granulometric composition of belozems were determined. The measurements showed that the upper and lower plasticity limits, the optimum moisture content, and the maximal density of the skeleton of belozems, as well as the considered compositions of cementitious soils, are insignificant, while the plasticity index of cementitious soils is less than one for belozems. It is experimentally proved that an increase in the portland cement amount lead to an increase in the compressive strength of cementitious soils with a decreasing speed. But for the same amount of portland cement used in the cementitious soil compositions, the values of the strength ratio of the pieces tested at the age of 60 and 28 days remain the same and are approximately equal to 1.2. A comparison of experimental data showed that it seems to be real to manufacture a cementitious soil on the basis of belozems of carbonate composition, which contain 10% of cement of the weight of dry mixture and have strength more than 10 MPa, without adding any surfactants to the material composition.

  9. Strength and thermal stability of Cu-Al2O3 composite obtained by internal oxidation

    Directory of Open Access Journals (Sweden)

    Jovanovic, M. T.

    2010-12-01

    Full Text Available The objective of the work is to study the effects of the high-energy milling on strengthening, thermal stability and electrical conductivity of Cu-Al2O3 composite. The prealloyed copper powders, atomized in inert gas and containing 3 wt. % Al, were milled up to 20 h in the planetary ball mill to oxidize in situ aluminium with oxygen from the air. Composite compacts were obtained by hot-pressing in an argon atmosphere at 800 °C for 3 h under the pressure of 35MPa. The microstructural characterization was performed by the optical microscope, scanning electron microscope (SEM, transmission electron microscope (TEM and X-ray diffraction analysis (XRD. The microhardness, electrical conductivity and density measurements were also carried out. The effect of internal oxidation and high-energy milling on strengthening of Cu-Al2O3 composite was significant, The increase of the microhardness of composite compacts (292 HV is almost threefold comparing to compacts processed from the as-received Cu-3 wt. % Al powder (102 HV. The grain size of Cu-Al2O3 compacts processed from 5 and 20 h-milled powders was 75 and 45 nm, respectively. The small increase in the grain size and the small microhardness drop indicate the high thermal stability of Cu-Al2O3 composite during high-temperature exposure at 800 °C.El objetivo del trabajo es el estudio de los efectos de la pulverización con altas energías sobre la resistencia, estabilidad térmica y conductividad eléctrica del compuesto Cu-Al2O3. El polvo pre-aleado de cobre, obtenido a través de la atomización con gas inerte y con un contenido de 3wt. % Al, se molió durante 20 h en el molino planetario de bolas dando lugar a la oxidación in situ del aluminio con el oxígeno del aire. El compuesto compactado se ha obtenido mediante prensado en caliente en atmósfera de argón a 800 °C durante 3 h y a una presión de 35MPa. La caracterización microestructural se hizo a través de microscopia óptica, microscopia

  10. Fatigue mechanisms in unidirectional glass-fibre-reinforced polypropylene

    DEFF Research Database (Denmark)

    Gamstedt, E.K.; Berglund, L.A.; Peijs, T.

    1999-01-01

    Polypropylene (PP) and polypropylene modified with maleic anhydride (MA-PP) reinforced by continuous longitudinal glass fibres have been investigated. The most prominent effect of the modification with maleic anhydride in the composite is a stronger fibre/matrix interface. The effects of interfac......Polypropylene (PP) and polypropylene modified with maleic anhydride (MA-PP) reinforced by continuous longitudinal glass fibres have been investigated. The most prominent effect of the modification with maleic anhydride in the composite is a stronger fibre/matrix interface. The effects...... of interfacial strength on fatigue performance and on the underlying micromechanisms have been studied for these composite systems. Tension-tension fatigue tests (R = 0.1) were carried out on 0 degrees glass-fibre/PP and glass-fibre/ MA-PP coupons. The macroscopic fatigue behaviour was characterized in terms...

  11. Enhancement in Mechanical and Electrical Properties of Polypropylene Using Graphene Oxide Grafted with End-Functionalized Polypropylene

    Directory of Open Access Journals (Sweden)

    Patchanee Chammingkwan

    2016-03-01

    Full Text Available Terminally hydroxylated polypropylene (PP synthesized by a chain transfer method was grafted to graphene oxide (GO at the chain end. Thus obtained PP-modified GO (PP-GO was melt mixed with PP without the use of a compatibilizer to prepare PP/GO nanocomposites. Mechanical and electrical properties of the resultant nanocomposites and reference samples that contained graphite nanoplatelets, partially reduced GO, or fully reduced GO were examined. The best improvement in the tensile strength was obtained using PP-GO at 1.0 wt %. The inclusion of PP-GO also led to the highest electrical conductivity, in spite of the incomplete reduction. These observations pointed out that terminally hydroxylated PP covalently grafted to GO prevented GO layers from re-stacking and agglomeration during melt mixing, affording improved dispersion as well as stronger interfacial bonding between the matrix and GO.

  12. Physical and dielectric properties of irradiated polypropylene and poly(ethylene terephthalate)

    International Nuclear Information System (INIS)

    Kita, H.; Okamoto, K.

    1986-01-01

    The effect of high-energy electron irradiation in air and in nitrogen on the physical and dielectric properties of polypropylene and poly(ethylene terephthalate) has been studied by measurements of electric strength, dielectric constant, dissipation factor, tensile strength, gel fraction and molecular weight distribution. Electric strength of polypropylene was improved by irradiation, while dielectric properties of poly(ethylene terephthalate) were virtually unaffected by irradiation of 1.0-20 Mrad. Possible mechanisms for increasing electric strength are discussed from the point of view of degradation and oxidation taking place simultaneously with crosslinking of polypropylene. The maximum dose level to improve the electric strength of polypropylene is determined to be about 5 Mrad. (author)

  13. Preparation of Polypropylene/Montmorillonite Nanocomposites Using Ionizing Radiation

    International Nuclear Information System (INIS)

    Güven, Olgun; Zengin, Fatma

    2011-01-01

    Polymer/clay nanocomposites are new generation materials that bring significant changes in mechanical, thermal and permeation properties of base polymers by low clay loading. In this study, polypropylene/montmorillonite nanocomposites were prepared by melt intercalation method by using batch type mixer. Two polypropylene samples with different melt flow indexes are used as the matrix, maleic anhydride grafted polypropylene (PP-g-MAH), and polypropylene granules oxidized by radiation/ozone are used as compatibilizer and unmodified clay (Na + montmorillonite, MMT) as the filler. Aim of this study is to examine the effect of different compatibilizers in the mechanical properties of polypropylene composite. Firstly, PP/clay samples were prepared and the effect of clay was examined, then 5, 10, 20kGy oxidized/degraded polypropylenes were used as compatibilizer and, 10 kGy was determined to be the most suitable irradiation dose for the best compatibilizing effect. Polypropylene granules were ozonated until they contained carbonyl groups equivalent to 10kGy oxidized PP, which was checked by FTIR-ATR spectroscopy. UV-visible reflectance measurements were also made on film samples and no significant changes were observed in visible region. Nano structures of some nanocomposites were characterized by PALS (Positron Annihilation Lifetime Spectroscopy) where it was observed that the addition of clay decreased the number of free volume holes and free volume hole radia. The dispersion state of MMT within polymer matrix was analyzed by XRD (X-ray diffraction). Tensile tests were made and the effect of the addition of clay and compatibilizers investigated. At low melt flow index PP, 1% MMT of PP/10kGyPP/MMT nanocomposite showed an increase in E-modulus 26% and in tensile strength 8% as compared to those of pristine PP. In conclusion radiation degraded (chain scissioned and oxidized) PP has been found to show very good compatibilizing effect for the natural montmorillonite/polypropylene

  14. Preparation of Polypropylene/Montmorillonite Nanocomposites Using Ionizing Radiation

    Energy Technology Data Exchange (ETDEWEB)

    Güven, Olgun; Zengin, Fatma

    2011-07-01

    Polymer/clay nanocomposites are new generation materials that bring significant changes in mechanical, thermal and permeation properties of base polymers by low clay loading. In this study, polypropylene/montmorillonite nanocomposites were prepared by melt intercalation method by using batch type mixer. Two polypropylene samples with different melt flow indexes are used as the matrix, maleic anhydride grafted polypropylene (PP-g-MAH), and polypropylene granules oxidized by radiation/ozone are used as compatibilizer and unmodified clay (Na{sup +} montmorillonite, MMT) as the filler. Aim of this study is to examine the effect of different compatibilizers in the mechanical properties of polypropylene composite. Firstly, PP/clay samples were prepared and the effect of clay was examined, then 5, 10, 20kGy oxidized/degraded polypropylenes were used as compatibilizer and, 10 kGy was determined to be the most suitable irradiation dose for the best compatibilizing effect. Polypropylene granules were ozonated until they contained carbonyl groups equivalent to 10kGy oxidized PP, which was checked by FTIR-ATR spectroscopy. UV-visible reflectance measurements were also made on film samples and no significant changes were observed in visible region. Nano structures of some nanocomposites were characterized by PALS (Positron Annihilation Lifetime Spectroscopy) where it was observed that the addition of clay decreased the number of free volume holes and free volume hole radia. The dispersion state of MMT within polymer matrix was analyzed by XRD (X-ray diffraction). Tensile tests were made and the effect of the addition of clay and compatibilizers investigated. At low melt flow index PP, 1% MMT of PP/10kGyPP/MMT nanocomposite showed an increase in E-modulus 26% and in tensile strength 8% as compared to those of pristine PP. In conclusion radiation degraded (chain scissioned and oxidized) PP has been found to show very good compatibilizing effect for the natural montmorillonite/polypropylene

  15. Polypropylene/graphite nanocomposites by in situ polymerization

    International Nuclear Information System (INIS)

    Milani, Marceo A.; Galland, Giselda B.; Quijada, Raul

    2011-01-01

    This work presents the synthesis of nanocomposites of polypropylene/graphite by in situ polymerization using metallocene catalyst and graphene nanosheets. Initially was analyzed which of the metallocene catalysts rac-Et(Ind) 2 ZrCl 2 or rac-Me 2 Si(Ind) 2 ZrCl 2 produces polypropylene with mechanical properties more relevant. Then it were performed the in situ polymerization reactions to obtain the nanocomposites. The polymeric materials were characterized by XRD, DSC, GPC and DMTA. (author)

  16. Effect of Mg and Cu on mechanical properties of high-strength welded joints of aluminum alloys obtained by laser welding

    Science.gov (United States)

    Annin, B. D.; Fomin, V. M.; Karpov, E. V.; Malikov, A. G.; Orishich, A. M.

    2017-09-01

    Results of experimental investigations of welded joints of high-strength aluminum-lithium alloys of the Al-Cu-Li and Al-Mg-Li systems are reported. The welded joints are obtained by means of laser welding and are subjected to various types of processing for obtaining high-strength welded joints. A microstructural analysis is performed. The phase composition and mechanical properties of the welded joints before and after heat treatment are studied. It is found that combined heat treatment of the welded joint (annealing, quenching, and artificial ageing) increases the joint strength, but appreciably decreases the alloy strength outside the region thermally affected by the welding process.

  17. Production of the oxidation-resistant polypropylene track membranes

    International Nuclear Information System (INIS)

    Kravets, L.I.; Dmitriev, S.N.; Apel, P.Y.

    1999-01-01

    This paper describes results of the method of manufacturing the polypropylene track membranes produced by physicochemical treatment under irradiation of accelerated heavy ions of polymer films. The developed method allows to produce membranes 0.1 - 0.2 μm in diameter and more with an improved structural and physicochemical properties. Poly-propylene track membranes of a novel sample are characterized by high homogeneity of pore sizes in magnitude, considerable mechanical strength, advanced thermal stability and resistance to oxidation in aggressive media. It opens new fields for their usage

  18. Properties of Recycled Aggregate Concrete Reinforced with Polypropylene Fibre

    Directory of Open Access Journals (Sweden)

    Wan Mohammad Wan Nur Syazwani

    2016-01-01

    Full Text Available This research work is aimed to investigate how the addition of various proportion of polypropylene fibre affects the mechanical strength and permeability characteristics of recycled aggregate concrete (RAC which has been produced with treated coarse recycled concrete aggregate (RCA. Further research on RAC properties and their applications is of great importance as the scarcity of virgin aggregate sources in close proximity to major urban centers is becoming a worldwide problem. In this study, the hardened RAC properties at the curing age of 7 and 28 days such as compressive strength, flexural strength, ultrasonic pulse velocity (UPV, water absorption and total porosity were evaluated and compare with control specimens. Experimental result indicates that although the inclusion of the treated coarse RCA can enhance the mechanical strength and permeability properties of RAC, Further modification by addition of polypropylene fibre can optimize the results.

  19. The radiation degradation of polypropylene

    International Nuclear Information System (INIS)

    De Hollain, G.

    1977-04-01

    Polypropylene is used extensively in the manufacture of disposable medical devices because of its superior properties. Unfortunately this polymer does not lend itself well to radiation sterilization, undergoing serious degradation which affects the mechanical properties of the polymer. In this paper the effects of radiation on the mechanical and physical properties of polypropylene are discussed. A programme of research to minimize the radiation degradation of this polymer through the addition of crosslinking agents to counteract the radiation degradation is proposed. It is furthermore proposed that a process of annealing of the irradiated polymer be investigated in order to minimize the post-irradiation degradation of the polypropylene [af

  20. Maximal isometric muscle strength values obtained By hand-held dynamometry in children between 6 and 15 years of age.

    Science.gov (United States)

    Escobar, Raul G; Munoz, Karin T; Dominguez, Angelica; Banados, Pamela; Bravo, Maria J

    2017-01-01

    In this study we aimed to determine the maximal isometric muscle strength of a healthy, normal-weight, pediatric population between 6 and 15 years of age using hand-held dynamometry to establish strength reference values. The secondary objective was determining the relationship between strength and anthropometric parameters. Four hundred normal-weight Chilean children, split into 10 age groups, separated by 1-year intervals, were evaluated. Each age group included between 35 and 55 children. The strength values increased with increasing age and weight, with a correlation of 0.83 for age and 0.82 for weight. The results were similar to those reported in previous studies regarding the relationships among strength, age, and anthropometric parameters, but the reported strength differed. These results provide normal strength parameters for healthy and normal-weight Chilean children between 6 and 15 years of age and highlight the relevance of ethnicity in defining reference values for muscle strength in a pediatric population. Muscle Nerve 55: 16-22, 2017. © 2016 Wiley Periodicals, Inc.

  1. Effect of nanosilica particles on polypropylene polymer modified asphalt mixture performance

    Directory of Open Access Journals (Sweden)

    Nura Bala

    2018-06-01

    Full Text Available The current study was conducted to investigate the effect of nanosilica particles on the performance characteristics of polymer modified asphalt binders. In this study, control 80/100 binder were modified with polypropylene polymer and nanosilica particles at concentration of 0%–4%. Both nanosilica particles and polypropylene polymer were added by weight of total bitumen content. The asphalt performance tests flexural four point beam fatigue test, indirect tensile strength, indirect tensile stiffness modulus and draindown tests are conducted to evaluate the effect of nanosilica particles. The results of the study shows that nanosilica particles improves the fatigue properties of polypropylene polymer modified binder. This indicates that nanosilica particles have significant effect on improving the performance properties of polymer modified binders. Also, the result reveals that thermoplastic polymer polypropylene with nanosilica particles when used as bitumen modifiers improve the performance and durability of asphalt mixtures. Keywords: Polypropylene, Fatigue cracking, Stiffness modulus, Modified asphalt, Draindown

  2. Test-Retest Reliability of Measurements of Hand-Grip Strength Obtained by Dynamometry from Older Adults: A Systematic Review of Research in the PubMed Database.

    Science.gov (United States)

    Bohannon, R W

    2017-01-01

    A systematic review was performed to summarize literature describing the test-retest reliability of grip strength measures obtained from older adults. Relevant literature was identified via a PubMed search. Seventeen articles were deemed appropriate based on inclusion and exclusion criteria. The relative test-retest reliability of grip strength measures obtained by dynamometry was good to excellent (intra-class correlation coefficients > 0.80) in all but 3 studies, which involved older adults with severe dementia. Absolute reliability, as indicated by summary statistics such as the minimum detectable change (95%), was more variable. As a percentage, that change ranged from 14.5% to 98.5%. Consequently, clinicians can be confident in the relative reliability of grip strength measures obtained from at risk older adults. However, relatively large percentage changes in grip strength may be necessary to conclude with confidence that a real change has occurred over time in some populations.

  3. Preparation and Characterization of Extruded Composites Based on Polypropylene and Chitosan Compatibilized with Polypropylene-Graft-Maleic Anhydride

    Science.gov (United States)

    Carrasco-Guigón, Fernando Javier; Rodríguez-Félix, Dora Evelia; Castillo-Ortega, María Mónica; Santacruz-Ortega, Hisila C.; Burruel-Ibarra, Silvia E.; Encinas-Encinas, Jose Carmelo; Plascencia-Jatomea, Maribel; Herrera-Franco, Pedro Jesus; Madera-Santana, Tomas Jesus

    2017-01-01

    The preparation of composites of synthetic and natural polymers represent an interesting option to combine properties; in this manner, polypropylene and chitosan extruded films using a different proportion of components and polypropylene-graft-maleic anhydride (PPgMA) as compatibilizer were prepared. The effect of the content of the biopolymer in the polypropylene (PP) matrix, the addition of compatibilizer, and the particle size on the properties of the composites was analyzed using characterization by fourier transform-infrared spectroscopy (FT-IR), scanning electron microscopy (SEM), differential scanning calorimetry (DSC), tensile strength, and contact angle, finding that in general, the addition of the compatibilizer and reducing the particle size of the chitosan, favored the physicochemical and morphological properties of the films. PMID:28772464

  4. High strain rate behaviour of polypropylene microfoams

    Directory of Open Access Journals (Sweden)

    Martínez A.B.

    2012-08-01

    Full Text Available Microcellular materials such as polypropylene foams are often used in protective applications and passive safety for packaging (electronic components, aeronautical structures, food, etc. or personal safety (helmets, knee-pads, etc.. In such applications the foams which are used are often designed to absorb the maximum energy and are generally subjected to severe loadings involving high strain rates. The manufacture process to obtain polymeric microcellular foams is based on the polymer saturation with a supercritical gas, at high temperature and pressure. This method presents several advantages over the conventional injection moulding techniques which make it industrially feasible. However, the effect of processing conditions such as blowing agent, concentration and microfoaming time and/or temperature on the microstructure of the resulting microcellular polymer (density, cell size and geometry is not yet set up. The compressive mechanical behaviour of several microcellular polypropylene foams has been investigated over a wide range of strain rates (0.001 to 3000 s−1 in order to show the effects of the processing parameters and strain rate on the mechanical properties. High strain rate tests were performed using a Split Hopkinson Pressure Bar apparatus (SHPB. Polypropylene and polyethylene-ethylene block copolymer foams of various densities were considered.

  5. High strain rate behaviour of polypropylene microfoams

    Science.gov (United States)

    Gómez-del Río, T.; Garrido, M. A.; Rodríguez, J.; Arencón, D.; Martínez, A. B.

    2012-08-01

    Microcellular materials such as polypropylene foams are often used in protective applications and passive safety for packaging (electronic components, aeronautical structures, food, etc.) or personal safety (helmets, knee-pads, etc.). In such applications the foams which are used are often designed to absorb the maximum energy and are generally subjected to severe loadings involving high strain rates. The manufacture process to obtain polymeric microcellular foams is based on the polymer saturation with a supercritical gas, at high temperature and pressure. This method presents several advantages over the conventional injection moulding techniques which make it industrially feasible. However, the effect of processing conditions such as blowing agent, concentration and microfoaming time and/or temperature on the microstructure of the resulting microcellular polymer (density, cell size and geometry) is not yet set up. The compressive mechanical behaviour of several microcellular polypropylene foams has been investigated over a wide range of strain rates (0.001 to 3000 s-1) in order to show the effects of the processing parameters and strain rate on the mechanical properties. High strain rate tests were performed using a Split Hopkinson Pressure Bar apparatus (SHPB). Polypropylene and polyethylene-ethylene block copolymer foams of various densities were considered.

  6. Mechanical properties of pineapple leaf fibre reinforced polypropylene composites

    International Nuclear Information System (INIS)

    Arib, R.M.N.; Sapuan, S.M.; Ahmad, M.M.H.M.; Paridah, M.T.; Zaman, H.M.D. Khairul

    2006-01-01

    Pineapple leaf fibre, which is rich in cellulose, relative inexpensive and abundantly available has the potential for polymer-reinforced composite. The present study investigates the tensile and flexural behaviours of pineapple leaf fibre-polypropylene composites as a function of volume fraction. The tensile modulus and tensile strength of the composites were found to be increasing with fibre content in accordance with the rule of mixtures. The tensile modulus and tensile strength with a volume fraction 10.8% are 687.02 and 37.28 MPa, respectively. The flexural modulus gives higher value at 2.7% volume fraction. The flexural strength of the composites containing 5.4% volume fraction was found to be higher than that of pure polypropylene resin by 5.1%. Scanning electron microscopic studies were carried out to understand the fibre-matrix adhesion and fibre breakage

  7. Mechanical properties of pineapple leaf fibre reinforced polypropylene composites

    Energy Technology Data Exchange (ETDEWEB)

    Arib, R.M.N. [Department of Mechanical and Manufacturing Engineering, Universiti Putra Malaysia, 43400 Serdang, Selangor (Malaysia); Sapuan, S.M. [Department of Mechanical and Manufacturing Engineering, Universiti Putra Malaysia, 43400 Serdang, Selangor (Malaysia)]. E-mail: sapuan@eng.upm.edu.my; Ahmad, M.M.H.M. [Department of Mechanical and Manufacturing Engineering, Universiti Putra Malaysia, 43400 Serdang, Selangor (Malaysia); Paridah, M.T. [Faculty of Forestry, Universiti Putra Malaysia, 43400 Serdang, Selangor (Malaysia); Zaman, H.M.D. Khairul [Radiation Processing Technology Division, Malaysian Institute for Nuclear Technology Research (MINT), Bangi 43000 Kajang, Selangor (Malaysia)

    2006-07-01

    Pineapple leaf fibre, which is rich in cellulose, relative inexpensive and abundantly available has the potential for polymer-reinforced composite. The present study investigates the tensile and flexural behaviours of pineapple leaf fibre-polypropylene composites as a function of volume fraction. The tensile modulus and tensile strength of the composites were found to be increasing with fibre content in accordance with the rule of mixtures. The tensile modulus and tensile strength with a volume fraction 10.8% are 687.02 and 37.28 MPa, respectively. The flexural modulus gives higher value at 2.7% volume fraction. The flexural strength of the composites containing 5.4% volume fraction was found to be higher than that of pure polypropylene resin by 5.1%. Scanning electron microscopic studies were carried out to understand the fibre-matrix adhesion and fibre breakage.

  8. Preparation of organophilic clays and polypropylene nano composites

    International Nuclear Information System (INIS)

    Lima, Martha Fogliato S.; Nascimento, Vinicius G. do; Lenz, Denise M.; Schenato, Flavia

    2011-01-01

    Polypropylene/montmorillonite nano composites were prepared by the melt intercalation technique. The clay was organically modified with different quaternary ammonium salts to obtain the organo clay. The modified clays with the quaternary ammonium salts were introduced in a polypropylene matrix with 3 wt. % of clay. The interlayer distance (d001) of the clay particles were obtained by X- ray diffraction and the thermal stability of the systems were investigated by thermogravimetry. The organo clay presence in the polymer matrix increased the degradation temperature in relation to the pure polymer. (author)

  9. Study of modified polypropylene nanocomposites by gamma irradiation with addition of cloisite clay

    International Nuclear Information System (INIS)

    Komatsu, Luiz G.H.; Oliani, Washington L.; Parra, Duclerc F.; Lugao, Ademar B.

    2011-01-01

    Nanomaterials, and, in particular, nanoreinforcements for polymer composites have been the subject of intense research, development and commercialization. Clay-containing polymeric nanocomposites (CPNCs) are used as either functional or structural materials, large-volume CPNCs with a commodity or engineering polymer as the matrix, where the mechanical behavior is the main concern (followed by gas-vapor barrier properties, flammability, etc.). This work concerns to the study of the mechanical, thermal and morphological behavior nanocomposite, (HMSPP) Polypropylene High Melt Strength (obtained at dose of 12.5 kGy) and addition of 5 and 10 wt% of organoclay with Cloisite 20A nanocomposite. Agent compatibilizer polypropylene-graft, (PP-g-AM) was added at 3% concentration and the clay was dispersed through melt intercalation technique using a twin-screw extruder). We observed an increase in traction rupture. The mechanical behavior was evaluated by strength, the thermal behavior were evaluated by the technique of differential scanning calorimetry, the morphology of the nanocomposites was studied by scanning electron microscopy, melt flow index and Fourier transformed infrared spectroscopy in nanocomposites Cloisite 20 A at 10% wt. (author)

  10. The influence of modified zeolites as nucleating agents on crystallization behavior and mechanical properties of polypropylene

    International Nuclear Information System (INIS)

    Lv, Zhiping; Wang, Kunjun; Qiao, Zhihua; Wang, Wenjie

    2010-01-01

    Polypropylene (PP) composites with unmodified and modified zeolites were prepared by melt blending in single-screw extruder. The modified zeolites, diethoxy (distearoyl) silane (DDS)-zeolite 13X (DDS-13X) and diethoxy (distearoyl) silane-zeolite 5A (DDS-5A), were obtained by grafting diethoxy (distearoyl) silane onto zeolite 13X and 5A, respectively. The influence of the unmodified and modified zeolites as nucleating agents on properties of polypropylene was investigated with X-ray diffraction (XRD), differential scanning calorimetry (DSC), polarized light microscopy (PLM), Vicat softening temperature (VST) and mechanical properties test. The XRD results revealed that zeolite 13X and DDS-13X had a great influence on nucleation of PP compared to zeolite 5A and DDS-5A. The DSC results showed that the addition of small amount of modified zeolites lead to increase in crystallization temperature (T c ), initial crystallization temperature (T onset ) and crystallinity (X c ) of PP composites compared to unmodified zeolites, especially, DDS-13X was more effective than DDS-5A, and the highest crystallinity X c (50.48%) was observed in PP/0.3 wt.% DDS-13X, which was responsible to the higher tensile strength and flexural strength of PP/DDS-13X. The PP/DDS-5A, however, exhibited evident increase in flexural strength and a little change in tensile strength compared to pure PP. Moreover, as the addition amount of DDS-5A or DDS-13X up to 1 wt.%, the impact strength of both PP/DDS-5A and PP/DDS-13X reached 43 kJ/m 2 , which was about 2.8 times greater than that of the pure PP (11.3 kJ/m 2 ). These results were in good agreement with the spherulite morphology observed from PLM micrographs.

  11. Studying the compactibility of the VT22 high-strength alloy powder obtained by the PREP method

    Science.gov (United States)

    Kryuchkov, D. I.; Berezin, I. M.; Nesterenko, A. V.; Zalazinsky, A. G.; Vichuzhanin, D. I.

    2017-12-01

    Compression curves are plotted for VT22 high-strength alloy powder under conditions of uniaxial compression at room temperature. The density of the compacted briquette at the loading and unloading stages is determined. It is demonstrated that strong interparticle bonds are formed in the area of the action of shear deformation. The results are supposed to be used to identify the flow model of the material studied and to perform the subsequent numerical modeling of the compaction process.

  12. Tough and Reinforced Polypropylene/Kaolin Composites using Modified Kaolin

    Science.gov (United States)

    Yao, J. L.; Zhu, H. X.; Qi, Y. B.; Guo, M. J.; Hu, Q.; Gao, L.

    2018-05-01

    Polypropylene (PP)/kaolin composites have been prepared by filling modified kaolin with diethylenetriaminepentaacetic acid (DTPA) into the PP matrix. The surface modification of kaolin particles effectively improves the compatibility between kaolin and PP matrix. It is conducive for uniform dispersion of inorganic particles in the matrix, and enhances the mechanical performance of the composites. Compared with plain kaolin, the mechanical properties of the modified composites exhibit higher tensile strength, bending strength, impact strength and melt index simultaneously. The DTPA modification of kaolin overall enhances the mechanical properties of PP composites. It meets the requirements in various applications, and makes the modified experiment interesting in modern teaching.

  13. Antioxidant action in irradiated polypropylene studied by ultraviolet spectroscopy

    International Nuclear Information System (INIS)

    Milosavljevic, B.H.; Novakovic, Lj.

    1999-01-01

    Ultraviolet spectrum of 0.2 mm thick film of polypropylene containing 0.5% ORGANOX 1010 showed that in the sample prepared by slow cooling about 15% of the antioxidant reacted during the preparation process. The difference in turbidity between the samples obtained in the slow and the fast cooling process is attributed to the degree of crystallinity, which is in agreement with the DSC data. Very pronounced effects of the oxygen concentration and the degree of crystallinity on antioxidant uptake in irradiated polypropylene films were observed and discussed. It was also shown that a Febetron 707 pulsed electron accelerator is capable of producing both the single pulse dose (50 kGy) and the dose rate (2.5 TGy/s) large enough to enable a comparison of dose rate effects and LET effects in the study of the antioxidant reactions in polypropylene

  14. Effects of gamma irradiation on polypropylene, polypropylene + high density polyethylene and polypropylene + high density polyethylene + wood flour

    Energy Technology Data Exchange (ETDEWEB)

    Reyes, J.; Albano, C.; Davidson, E.; Poleo, R. [Universidad Central de Venezuela, Caracas (Venezuela). Escuela de Quimica; Gonzalez, J.; Ichazo, M. [Universidad Simon Bolivar, Dept. de Mecanica, Caracas (Venezuela); Chipara, M. [Research Institute for Electrotechnics, Bucharest (Romania)

    2001-04-01

    The effect of the gamma-irradiation on the mechanical properties of the composites, Polypropylene (PP), PP+high density Polyethylene (HDPE), PP+ HDPE+wood flour, where HDPE is virgin and recycled, was studied. This paper discusses the behavior of the composites after exposure to various doses of gamma irradiation (1-7 MRads) in the presence of oxygen. The dependence of mechanical properties on the integral dose for a constant dose rate of 0.48 MRads/h confirms the influence of the irradiation. Strong effects on the elongation at break and break strength is noticed. The mathematical analysis suggests for the PP+r-HDPE a bimolecular process of the elongation at break. On the order hand, for the PP+HDPE a complex process is represented for a three exponential equation. (orig.)

  15. Effects of gamma irradiation on polypropylene, polypropylene + high density polyethylene and polypropylene + high density polyethylene + wood flour

    International Nuclear Information System (INIS)

    Reyes, J.; Albano, C.; Davidson, E.; Poleo, R.; Chipara, M.

    2001-01-01

    The effect of the gamma-irradiation on the mechanical properties of the composites, Polypropylene (PP), PP+high density Polyethylene (HDPE), PP+ HDPE+wood flour, where HDPE is virgin and recycled, was studied. This paper discusses the behavior of the composites after exposure to various doses of gamma irradiation (1-7 MRads) in the presence of oxygen. The dependence of mechanical properties on the integral dose for a constant dose rate of 0.48 MRads/h confirms the influence of the irradiation. Strong effects on the elongation at break and break strength is noticed. The mathematical analysis suggests for the PP+r-HDPE a bimolecular process of the elongation at break. On the order hand, for the PP+HDPE a complex process is represented for a three exponential equation. (orig.)

  16. Polypropylene Track Membranes for Mikro and Ultrafiltration of Chemically Aggressive Agents

    CERN Document Server

    Kravets, L I; Apel, P Yu

    2000-01-01

    A production process for track membranes on the basis of chemically resistant polymer polypropylene has been developed. Research in all stages of the formation of the polypropylene track membranes has been conducted: the main principles of the process of chemical etching of polypropylene irradiated with accelerated ions have been investigated, the most effective structure of the etchant for a selective etching of the heavy ion tracks has been selected, the parameters of etching have been optimized. A method for sensibilization of latent tracks in polypropylene by effect of solvents has been developed. It helps to reach a significant increase in etching selectivity. A method for destruction of an absorbed chromocontaining layer on the surface of polypropylene track membranes formed during etching has been elaborated. Experimental samples of the membranes for micro and ultrafiltration have been obtained and their properties have been studied in course of their exploitation in chemically aggressive agents. For t...

  17. Modification of bentonite clay and application on polypropylene nano composites

    International Nuclear Information System (INIS)

    Oliveira, Akidauana D.B.; Rodrigues, Andre W.B.; Agrawal, Pankaj; Araujo, Edcleide M.; Melo, Tomas J.A.

    2009-01-01

    This work consisted on the modification of Brasgel PA clay with ionic surfactant Praepagen WB and its incorporation into polypropylene. The results of infrared and DR-X was showed that the intercalation of surfactant in the clay and the incorporation of organoclay in PP matrix resulted in the formation of an intercalated structure. The impact strength of PP increased with the incorporation of organoclay. (author)

  18. Functional Block Copolymers as Compatibilizers for Nanoclays in Polypropylene Nanocomposites

    DEFF Research Database (Denmark)

    Jankova Atanasova, Katja; Daugaard, Anders Egede; Stribeck, Norbert

    2011-01-01

    With the aim of creating tough nanocomposits (NC) [1] based on polypropylene (PP) and nanoclay (NCl) in the framework of the 7th EU program NANOTOUGH we have designed amphiphilic block copolymers utilizing Atom Transfer Radical Polymerization (ATRP) [2]. They consist of a hydrophobic block...... crystallites) is replaced by alien-reinforcement (of the MMT). Furthermore, the results from the impact strength and cyclic test of the prepared PP nanocomposites [3] are promicing....

  19. Comparison of the performance of masterbatch and liquid color concentrates for mass coloration of polypropylene

    DEFF Research Database (Denmark)

    Haastrup, Sonja; Yu, Donghong; Broch, Thomas

    2016-01-01

    The properties of polypropylene (PP) mixed with masterbatch (MB) and liquid color concentrates (LCC), respectively, were compared by preparing samples of PP with MB and PP with LCC and neat PP as a reference material using 1–4 extrusion cycles. Two colors were examined, i.e., a white color...... consisting of pigment white 6, and a green color consisting of pigment white 6, pigment blue 15:3, and pigment green 7. The color difference between PP prepared with MB and LCC was determined and the mechanical, rheological, and crystalline properties of PP prepared with MB and LCC were found to be generic....... The color of PP obtained from MB and LCC were comparable. Further, it was found that the tensile strength, the viscosity, and the crystal structure obtained were similar when using LCC instead of MB. The viscosity of the treated PP generally decreased with increasing extruder retention time due to thermal...

  20. Study of gel formation in polypropylene modified by gamma irradiation; Estudo da formacao de geis em polipropileno modificado por irradiacao gama

    Energy Technology Data Exchange (ETDEWEB)

    Oliani, W.L.; Parra, D.F.; Fermino, D.M.; Lima, L.F.C.P.; Lugao, A.B., E-mail: washoliani@usp.b [Instituto de Pesquisas Energeticas e Nucleares (IPEN/CNEN-SP), Sao Paulo, SP (Brazil); Riella, H.G. [Universidade Federal de Santa Catarina (UFSC), Florianopolis, SC (Brazil)

    2010-07-01

    The linearity of the chains of iPP (isotactic polypropylene) confers to this, low melt strength. This fact limits the use of iPP in processes that demand high stretching. The graft of branches confers improvements in its extensional viscosity, resulting in Polypropylene with High Melt Strength (HMS-PP). Preparation process of the HMS-PP, included iPP in pellets, conditioned in plastic container containing acetylene under pressure of 110 kPa and radiation with {gamma} source of {sup 60}Co in the doses of 5, 12.5 and 20 kGy. The gel fraction of the samples was determined by the extraction of soluble components in xylene under boiling for 12 hours at 138 deg C. The soluble part of the samples was decanted with the total volatilization of the xylene to the room temperature (25 deg C) and deposition in glass blades. These samples had been characterized by Optic Microscopy, Scanning Electron Microscopy and Infrared Spectroscopy. In this study of the morphology, we obtained the formation of gel and microgel of polypropylene with higher incidence in HMS-PP 20 kGy. (author)

  1. Flexure and impact properties of glass fiber reinforced nylon 6-polypropylene composites

    Science.gov (United States)

    Kusaseh, N. M.; Nuruzzaman, D. M.; Ismail, N. M.; Hamedon, Z.; Azhari, A.; Iqbal, A. K. M. A.

    2018-03-01

    In recent years, polymer composites are rapidly developing and replacing the metals or alloys in numerous engineering applications. These polymer composites are the topic of interests in industrial applications such as automotive and aerospace industries. In the present research study, glass fiber (GF) reinforced nylon 6 (PA6)-polypropylene (PP) composite specimens were prepared successfully using injection molding process. Test specimens of five different compositions such as, 70%PA6+30%PP, 65%PA6+30%PP+5%GF, 60%PA6+30%PP+10%GF, 55%PA6+30%PP+15%GF and 50%PA6+30%PP+20%GF were prepared. In the experiments, flexure and impact tests were carried out. The obtained results revealed that flexure and impact properties of the polymer composites were significantly influenced by the glass fiber content. Results showed that flexural strength is low for pure polymer blend and flexural strength of GF reinforced composite increases gradually with the increase in glass fiber content. Test results also revealed that the impact strength of 70%PA6+30%PP is the highest and 55%PA6+30%PP+15%GF composite shows moderate impact strength. On the other hand, 50%PA6+30%PP+20%GF composite shows low toughness or reduced impact strength.

  2. Effect of coupling agent on durian skin fibre nanocomposite reinforced polypropylene

    Science.gov (United States)

    Siti Nur E'zzati, M. A.; Anuar, H.; Siti Munirah Salimah, A. R.

    2018-01-01

    This paper reports on the development of a composite-based natural fiber to reduce the reliance on petroleum-based product in order to amplify environmental awareness. The production of Durian Skin Nanofiber (DSNF) was conducted using biological fermentation method via rhizopus oryzae in order to obtain the nano dimension of the particle size. Polypropylene (PP) and DSNF were produced using Haake internal mixer via melt blending technique. The significant effect of maleic anhydride grafted polypropylene (MAPP) on the properties of PP/DSNF nanocomposite was investigated to study its mechanical properties which are tensile strength and thermal stability using thermogravimetric (TGA) and differential scanning analysis (DSC). The tensile property of PP nanocomposites increased from 33 MPa to 38 MPa with the presence of MAPP. The addition of MAPP also increased the thermal stability of PP/DSNF nanocomposite where the char residue increased by 52%. Besides that, the thermal degradation of PP/DSNF and PP/DSNF-MAPP were higher than PP where they exerted higher amount of weight loss at an elevated temperature. The percentage of crystallinity, %Xc, of PP nanocomposites improved with the addition of MAPP by 35% based on the differential scanning calorimetry (DSC) result. The SEM analysis showed that the PP/DSNF-MAPP exerts ductile fracture while PP/DSNF exerts brittle fracture.

  3. Woodflour as Reinforcement of Polypropylene

    Directory of Open Access Journals (Sweden)

    José Cláudio Caraschi

    2002-10-01

    Full Text Available The effect of the filler content and size, as well as accelerated aging on the mechanical properties of polypropylene composites reinforced with woodflour (WF/PP were evaluated. The composites were prepared by the extrusion of polypropylene with woodflour (Pinus elliotti based on following ratios: 15, 25 and 40 wt% with two different granulometries. The specimens were injection molded according to ASTM standards. The composite properties did not show significant differences as a function of the filler granulometry. We also observed that by increasing the filler content, both the mechanical properties and the melt flow index (MFI decreased, and the elasticity modulus, hardness and density increased. Concerning the accelerated aging, the composite presented a reduction in tensile properties. The results showed that the composite properties are extremely favorable when compared to other commercial systems reinforced by inorganic fillers.

  4. Application of waste bulk moulded composite (BMC) as a filler for isotactic polypropylene composites.

    Science.gov (United States)

    Barczewski, Mateusz; Matykiewicz, Danuta; Andrzejewski, Jacek; Skórczewska, Katarzyna

    2016-05-01

    The aim of this study was to produce isotactic polypropylene based composites filled with waste thermosetting bulk moulded composite (BMC). The influence of BMC waste addition (5, 10, 20 wt%) on composites structure and properties was investigated. Moreover, additional studies of chemical treatment of the filler were prepared. Modification of BMC waste by calcium stearate (CaSt) powder allows to assess the possibility of the production of composites with better dispersion of the filler and more uniform properties. The mechanical, processing, and thermal properties, as well as structural investigations were examined by means of static tensile test, Dynstat impact strength test, differential scanning calorimetry (DSC), wide angle X-ray scattering (WAXS), melt flow index (MFI) and scanning electron microscopy (SEM). Developed composites with different amounts of non-reactive filler exhibited satisfactory thermal and mechanical properties. Moreover, application of the low cost modifier (CaSt) allows to obtain composites with better dispersion of the filler and improved processability.

  5. Study on Welding Mechanism Based on Modification of Polypropylene for Improving the Laser Transmission Weldability to PA66

    Science.gov (United States)

    Liu, Huixia; Jiang, Hairong; Guo, Dehui; Chen, Guochun; Yan, Zhang; Li, Pin; Zhu, Hejun; Chen, Jun; Wang, Xiao

    2015-01-01

    Polypropylene and PA66 are widely used in our daily life, but they cannot be welded by laser transmission welding (LTW) because of polar differences and poor compatibility. In this paper, grafting modification technology is used to improve the welding performance between polypropylene and PA66. Firstly, the strong reactive and polar maleic-anhydride (MAH) is grafted to polypropylene and infrared spectrometer is used to prove that MAH has been grafted to polypropylene. At the same time, the mechanical and thermal properties of the graft modified polypropylene (TGMPP) are tested. The results prove that the grafting modification has little influence on them. Also, the optical properties of TGMPP are measured. Then, the high welding strength between TGMPP and PA66 is found and the mechanism of the weldability is researched, which shows that there are two reasons for the high welding strength. By observing the micro morphology of the welding zone, one reason found is that the modification of polypropylene can improve the compatibility between polypropylene and PA66 and make them easy to diffuse mutually, which causes many locking structures formed in the welding region. The other reason is that there are chemical reactions between TGMPP and PA66 proved by the X-ray photoelectron spectrometer. PMID:28793484

  6. Application to refrigerator plastics by mechanical recycling from polypropylene in waste-appliances

    International Nuclear Information System (INIS)

    Ha, Kyung Ho; Kim, Moon Saeng

    2012-01-01

    Highlights: → Polypropylene is mechanically recycled from waste-appliances. → Recycled polypropylene (RPP) is impact enhanced polypropylene with ethylene-propylene rubber (EPR). → Performance evaluation shows that RPP is applicable to refrigerator plastics. -- Abstract: For the application to refrigerator plastics by mechanical recycling from polypropylene (PP) in waste-appliances, it needs to identify the degradation and heterogeneity of recycled polypropylene (RPP). It is applicable the thermal analysis such as differential scanning calorimetry (DSC), thermo-gravimetric analysis (TGA), spectroscopic analysis such as Fourier Transform Infrared (FTIR) and morphological analysis such as scanning electronic microscope (SEM). The analysis results show that RPP from waste-appliances is the polyethylene (PE) and polypropylene (PP) copolymer enhanced impact property (Impact-PP) and it is possible to apply refrigerator plastics with good impact property at low temperature. Finally, the performance evaluation of RPP is estimated by Gel Permeation Chromatography (GPC) analysis and is performed by the various mechanical and physical testing methods. It shows that RPP has relatively high molecular weight and balanced properties with strength and toughness. It is expected that RPP by the mechanical recycling from waste-appliances will have about 50% cost-merit.

  7. Monotonic and cyclic responses of impact polypropylene and continuous glass fiber-reinforced impact polypropylene composites at different strain rates

    KAUST Repository

    Yudhanto, Arief; Lubineau, Gilles; Wafai, Husam; Mulle, Matthieu; Pulungan, Ditho Ardiansyah; Yaldiz, R.; Verghese, N.

    2016-01-01

    Impact copolymer polypropylene (IPP), a blend of isotactic polypropylene and ethylene-propylene rubber, and its continuous glass fiber composite form (glass fiber-reinforced impact polypropylene, GFIPP) are promising materials for impact

  8. Mechanical Properties of Nanofilled Polypropylene Composites

    Directory of Open Access Journals (Sweden)

    Cristina-Elisabeta PELIN

    2015-06-01

    Full Text Available The paper presents a study concerning mechanical performance of thermoplastic nanocomposites based on isotactic polypropylene matrix, nanofilled with montmorillonite modified with quaternary ammonium salt and carboxyl functionalized carbon nanotubes, respectively, added in the same concentration relative to the matrix. The nanofilled and single polymer materials were obtained by simple melt compounding through extrusion process followed by injection molding into specific shape specimens for mechanical testing of the samples. Mechanical properties were evaluated by tensile and 3 point bending tests. In terms of modulus of elasticity, the results showed overall positive effects concerning the effect of nanofiller addition to the thermoplastic polymer. The fracture cross section of the tested specimens was characterized by FT-IR spectroscopy and SEM microscopy.

  9. Study of microcellular injection-molded polypropylene/waste ground rubber tire powder blend

    International Nuclear Information System (INIS)

    Xin, Zhen Xiang; Zhang, Zhen Xiu; Pal, Kaushik; Byeon, Jong Ung; Lee, Sung Hyo; Kim, Jin Kuk

    2010-01-01

    Microcellular polypropylene/waste ground rubber tire powder blend processing was performed on an injection-molding machine with a chemical foaming agent. The molded samples produced based on the design of experiments (DOE) matrices were subjected to tensile testing and scanning electron microscope (SEM) analyses. Molding conditions and waste ground rubber tire (WGRT) powder have been found to have profound effects on the cell structures and mechanical properties of polypropylene (PP) and waste ground rubber tire powder composite samples. The result shows that microcellular PP/WGRT blend samples exhibit smaller cell size and higher cell density compare with polypropylene resin. Among the molding parameters studied, chemical foaming agent weight percentage has the most significant effect on cell size, cell density, and tensile strength. The results also suggest that tensile strength of microcellular PP/WGRT composites is sensitive to weight reduction, and skin thickness.

  10. Permeation Tests on Polypropylene Fiber Materials

    Science.gov (United States)

    2018-03-16

    Permeation Tests on Polypropylene Fiber Materials Brandy J. White Martin H. Moore Brian J. Melde Laboratory for the Study of Molecular Interfacial...ABSTRACT Permeation Tests on Polypropylene Fiber Materials Brandy J. White, Martin H. Moore, Brian J. Melde Center for Bio/Molecular Science

  11. Effect of processing conditions on the mechanical and thermal properties of high-impact polypropylene nanocomposites

    Energy Technology Data Exchange (ETDEWEB)

    Furlan, L G [Federal Institute of Rio Grande do Sul, IFRS, Campus Restinga, Estrada Joao Antonio da Silveira, 351, Porto Alegre 91790-400 (Brazil); Ferreira, C I; Dal Castel, C; Santos, K S; Mello, A C.E. [Chemistry Institute, Federal University of Rio Grande do Sul, UFRGS, Av. Bento Goncalves, 9500, Porto Alegre 91501-970 (Brazil); Liberman, S A; Oviedo, M A.S. [Braskem S.A., III Polo Petroquimico, Via Oeste, Lote 5, Triunfo 95853-000 (Brazil); Mauler, R.S., E-mail: mauler@iq.ufrgs.br [Chemistry Institute, Federal University of Rio Grande do Sul, UFRGS, Av. Bento Goncalves, 9500, Porto Alegre 91501-970 (Brazil)

    2011-08-25

    Highlights: {yields} Polypropylene montmorillonite (PP-MMT) produced at different processing conditions. {yields} Polypropylene Nanocomposites with higher increase on impact resistance. {yields} Higher enhancement on mechanical properties. - Abstract: Polypropylene montmorillonite (PP-MMT) nanocomposites have been prepared by using a co-rotating twin screw extruder. The effects of processing conditions at fixed clay content (5 wt%) on polymer properties were investigated by means of transmission electron microscopy (TEM), flexural modulus, izod impact, dynamic mechanical analysis (DMA), and differential scanning calorimetry (DSC). It was noticed that the morphology and the mechanical properties of polypropylene nanocomposites were affected by different screw shear configuration. The results showed that the higher enhancement on mechanical properties was obtained by medium shear intensity profile instead of high configuration. An exceptional increase (maximum of 282%) on impact resistance was observed.

  12. Effect of processing conditions on the mechanical and thermal properties of high-impact polypropylene nanocomposites

    International Nuclear Information System (INIS)

    Furlan, L.G.; Ferreira, C.I.; Dal Castel, C.; Santos, K.S.; Mello, A.C.E.; Liberman, S.A.; Oviedo, M.A.S.; Mauler, R.S.

    2011-01-01

    Highlights: → Polypropylene montmorillonite (PP-MMT) produced at different processing conditions. → Polypropylene Nanocomposites with higher increase on impact resistance. → Higher enhancement on mechanical properties. - Abstract: Polypropylene montmorillonite (PP-MMT) nanocomposites have been prepared by using a co-rotating twin screw extruder. The effects of processing conditions at fixed clay content (5 wt%) on polymer properties were investigated by means of transmission electron microscopy (TEM), flexural modulus, izod impact, dynamic mechanical analysis (DMA), and differential scanning calorimetry (DSC). It was noticed that the morphology and the mechanical properties of polypropylene nanocomposites were affected by different screw shear configuration. The results showed that the higher enhancement on mechanical properties was obtained by medium shear intensity profile instead of high configuration. An exceptional increase (maximum of 282%) on impact resistance was observed.

  13. UV protective zinc oxide coating for biaxially oriented polypropylene packaging film by atomic layer deposition

    Energy Technology Data Exchange (ETDEWEB)

    Lahtinen, Kimmo, E-mail: kimmo.lahtinen@lut.fi [ASTRaL, Lappeenranta University of Technology, Sammonkatu 12, FI-50130 Mikkeli (Finland); Kääriäinen, Tommi, E-mail: tommi.kaariainen@colorado.edu [ASTRaL, Lappeenranta University of Technology, Sammonkatu 12, FI-50130 Mikkeli (Finland); Johansson, Petri, E-mail: petri.johansson@tut.fi [Paper Converting and Packaging Technology, Tampere University of Technology, P.O.Box 589, FI-33101 Tampere (Finland); Kotkamo, Sami, E-mail: sami.kotkamo@tut.fi [Paper Converting and Packaging Technology, Tampere University of Technology, P.O.Box 589, FI-33101 Tampere (Finland); Maydannik, Philipp, E-mail: philipp.maydannik@lut.fi [ASTRaL, Lappeenranta University of Technology, Sammonkatu 12, FI-50130 Mikkeli (Finland); Seppänen, Tarja, E-mail: tarja.seppanen@lut.fi [ASTRaL, Lappeenranta University of Technology, Sammonkatu 12, FI-50130 Mikkeli (Finland); Kuusipalo, Jurkka, E-mail: jurkka.kuusipalo@tut.fi [Paper Converting and Packaging Technology, Tampere University of Technology, P.O.Box 589, FI-33101 Tampere (Finland); Cameron, David C., E-mail: david.cameron@miktech.fi [ASTRaL, Lappeenranta University of Technology, Sammonkatu 12, FI-50130 Mikkeli (Finland)

    2014-11-03

    Biaxially oriented polypropylene (BOPP) packaging film was coated with zinc oxide (ZnO) coatings by atomic layer deposition (ALD) in order to protect the film from UV degradation. The coatings were made at a process temperature of 100 °C using diethylzinc and water as zinc and oxygen precursors, respectively. The UV protective properties of the coatings were tested by using UV–VIS and infrared spectrometry, differential scanning calorimetry (DSC) and a mechanical strength tester, which characterised the tensile and elastic properties of the film. The results obtained with 36 and 67 nm ZnO coatings showed that the ZnO UV protective layer is able to provide a significant decrease in photodegradation of the BOPP film under UV exposure. While the uncoated BOPP film suffered a complete degradation after a 4-week UV exposure, the 67 nm ZnO coated BOPP film was able to preserve half of its original tensile strength and 1/3 of its elongation at break after a 6-week exposure period. The infrared analysis and DSC measurements further proved the UV protection of the ZnO coatings. The results show that a nanometre scale ZnO coating deposited by ALD is a promising option when a transparent UV protection layer is sought for polymer substrates. - Highlights: • Atomic layer deposited zinc oxide coatings were used as UV protection layers. • Biaxially oriented polypropylene (BOPP) film was well protected against UV light. • Formation of UV degradation products in BOPP was significantly reduced. • Mechanical properties of the UV exposed BOPP film were significantly improved.

  14. Fabrication of polypropylene/silver nanocomposites for biocidal applications

    Energy Technology Data Exchange (ETDEWEB)

    Oliani, Washington Luiz, E-mail: washoliani@usp.br [Nuclear and Energy Research Institute, IPEN-CNEN/SP, Av. Prof. Lineu Prestes, 2242 – Cidade Universitária – CEP, 05508-000 São Paulo (Brazil); Parra, Duclerc Fernandes; Komatsu, Luiz Gustavo Hiroki [Nuclear and Energy Research Institute, IPEN-CNEN/SP, Av. Prof. Lineu Prestes, 2242 – Cidade Universitária – CEP, 05508-000 São Paulo (Brazil); Lincopan, Nilton [Department of Microbiology, Institute of Biomedical Sciences, University of Sao Paulo, 05508-000, São Paulo (Brazil); Department of Clinical Analysis, School of Pharmacy, University of São Paulo, 05508-000, São Paulo (Brazil); Rangari, Vijaya Kumar [Department of Materials Science and Engineering, Tuskegee University, AL 36088 (United States); Lugao, Ademar Benevolo [Nuclear and Energy Research Institute, IPEN-CNEN/SP, Av. Prof. Lineu Prestes, 2242 – Cidade Universitária – CEP, 05508-000 São Paulo (Brazil)

    2017-06-01

    This paper presents a study on biocidal effect of polymer nanocomposite films of gamma irradiated polypropylene (PP) and silver nanoparticles. The modified polypropylene was obtained from isotactic polypropylene (iPP) in pellets form by irradiation with gamma rays in the presence of acetylene. A new morphology with long chain branching of PP and distinct rheology is obtained by this process. The blend of 50/50 wt% neat PP and PP modified by gamma radiation were further mixed using a twin screw extruder. The AgNPs were infused into this polymer blend at different concentrations of: 0.1%; 0.25%; 0.5%; 1.0%; 1.0% (PVP), 2.0% and 4.0% by wt%. These polymer nanocomposites were characterized by Raman spectroscopy, scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS), thermogravimetric analysis (TG), differential scanning calorimetry (DSC), X-ray diffraction (XRD), transmission electron microscopy (TEM), cytotoxicity test and Kirby-Bauer disk diffusion techniques. The bactericidal effect of Pseudomonas aeruginosa (P. aeruginosa) and Staphylococcus aureus (S. aureus) were assessed in detail. - Highlights: • PP film was obtained from iPP in pellets form by γ rays with acetylene and AgNPs • Bactericidal effect of P aeruginosa and S aureus were assessed.

  15. Effect of bar sealing parameters on OPP/MCPP heat seal strength

    Directory of Open Access Journals (Sweden)

    2007-11-01

    Full Text Available The effect of bar sealing parameters on the heat seal strength of oriented polypropylene (OPP/metallic cast polypropylene (MCPP laminate film was investigated. Based on the results obtained from the parametric study, a bar sealing process window was developed. All points drop within the process window are combinations of platen temperature and dwell time that produce acceptable heat seal. Optimum combinations are indicated by the lower border of the window. The plateau initiation temperature, Tpi of OPP/MCPP laminate film used in the present study occurred before the final melting temperature, Tmf of the sealant material. The highest achievable heat seal strength was at the plateau region, and the corresponding failure modes were delaminating, tearing or combine failure modes (delaminating and tearing. Minimum pressure level of 1.25 bars is necessary to bring the laminate interface into intimate contact in order to effect sealing.

  16. Effect of modified polypropylene on the interfacial bonding of polymer–aluminum laminated films

    International Nuclear Information System (INIS)

    Liang, Chang-Sheng; Lv, Zhong-Fei; Bo, Yang; Cui, Jia-Yang; Xu, Shi-Ai

    2015-01-01

    Highlights: • Aluminium-polymer composite packing material with high T-peel strength was prepared. • Polypropylene was grafted by acrylic acid, glycidyl methacrylate, maleic anhydride. • Grafted polypropylene greatly improved the T-peel strength. • Chemical bonding plays an important role in improving the adhesion strength. - Abstract: The interfacial bonding between functionalized polymers and chromate–phosphate treated aluminum (Al) foil were investigated in this study. Glycidyl methacrylate (GMA), acrylic acid (AA) and maleic anhydride (MAH) were grafted onto polypropylene (PP) to improve its adhesion strength with the treated Al foil. The interfacial peel strength was evaluated by the T-peel test, and the results showed that modification of PP resulted in a significant improvement in the interfacial peel strength from 1 N/15 mm for pure PP to 10–14 N/15 mm for the modified PP. The surface chemistry, topography and surface energy of the modified PP and Al foil after peeling were characterized by time-of-flight secondary ion mass spectrometry (TOF-SIMS), X-ray photoelectron spectroscopy (XPS), attenuated total reflectance Fourier transform infrared spectroscopy (ATR-FTIR), scanning electron microscopy (SEM) and contact angle measurement. The treated Al foil could react with the functional groups of PP, resulting in the formation of new carboxylates. The new chemical bonding rather than the mechanical interlocking contributed to the improvement of adhesion strength

  17. Radiation resistant polypropylene blended with mobilizer,. antioxidants and nucleating agent

    Science.gov (United States)

    Shamshad, A.; Basfar, A. A.

    2000-03-01

    Post-irradiation storage of medical disposables prepared from isotactic polypropylene renders them brittle due to degradation. To avoid this, isotactic polypropylene [(is)PP] was blended with a mobilizer, dioctyl pthallate (DOP), three antioxidants (hindered amines and a secondary antioxidant) and benzoic acid to obtain radiation-resistant, thermally-stable and transparent material. Different formulations prepared were subjected to gamma radiation to doses of 25 and 50 kGy. Tests of breakage on bending after ageing in an oven at 70°C up to 12 months have shown that the addition of DOP and the antioxidants imparts improved radiation and thermal stability as compared to (is)PP alone or its blend with DOP. All the formulations irradiated or otherwise demonstrated excellent colour stability even after accelerated ageing at 70°C for prolonged periods.

  18. Surface modification and micromechanical properties of jute fiber mat reinforced polypropylene composites

    Directory of Open Access Journals (Sweden)

    2007-05-01

    Full Text Available A new treating method using sodium hydroxide (NaOH and Maleic anhydride-grafted polypropylene (MPP emulsion was introduced to treat jute fiber mat in order to enhance the performance of jute/polypropylene (PP composite prepared by film stacking method. The surface modifications of jute fiber mat have been found to be very effective in improving the fiber-matrix adhesion. It was shown that treatments changed not only the surface topography but also the distribution of diameter and strength for the jute fibers, which was analyzed by using a two-parameter Weibull distribution model. Consequently, the interfacial shear strength, flexural and tensile strength of the composites all increased, but the impact strength decreased slightly. These results have demonstrated a new approach to use natural materials to enhance the mechanical performances of composites.

  19. Photo-oxidative degradation of TiO{sub 2}/polypropylene films

    Energy Technology Data Exchange (ETDEWEB)

    García-Montelongo, X.L. [Facultad de Ingeniería Mecánica y Eléctrica, Universidad Autónoma de Nuevo León, Ciudad Universitaria, C.P. 66451 San Nicolás de los Garza, N.L. (Mexico); Martínez-de la Cruz, A., E-mail: azael70@yahoo.com.mx [Facultad de Ingeniería Mecánica y Eléctrica, Universidad Autónoma de Nuevo León, Ciudad Universitaria, C.P. 66451 San Nicolás de los Garza, N.L. (Mexico); Vázquez-Rodríguez, S. [Facultad de Ingeniería Mecánica y Eléctrica, Universidad Autónoma de Nuevo León, Ciudad Universitaria, C.P. 66451 San Nicolás de los Garza, N.L. (Mexico); Torres-Martínez, Leticia M. [Facultad de Ingeniería Civil, Universidad Autónoma de Nuevo León, Ciudad Universitaria, C.P. 66451 San Nicolás de los Garza, N.L. (Mexico)

    2014-03-01

    Graphical abstract: - Highlights: • Photo-oxidative degradation of polypropylene is accelerated by TiO{sub 2} incorporation. • Weight loss, FTIR, SEM and GPC shown high degree of degradation of polypropylene. • A mechanism of the photo-degradation of polypropylene by TiO{sub 2} is proposed. - Abstract: Photo-oxidative degradation of polypropylene films with TiO{sub 2} nanoparticles incorporated was studied in a chamber of weathering with Xenon lamps as irradiation source. TiO{sub 2} powder with crystalline structure of anatase was synthesized by thermal treatments at 400 and 500 °C starting from a precursor material obtained by sol–gel method. Composites of TiO{sub 2}/polypropylene were prepared with 0.1, 0.5 and 1.0 wt% of TiO{sub 2}. The mixture of components was performed using a twin screw extruder, the resulting material was pelletized by mechanical fragmenting and then hot-pressed in order to form polypropylene films with TiO{sub 2} dispersed homogeneously. Photo-oxidative degradation process was followed by visual inspection, weight loss of films, scanning electron microscopy (SEM), infrared spectroscopy with Fourier transformed (FTIR), and gel permeation chromatography (GPC)

  20. Morphological, viscoelastic and mechanical characterization of polypropylene/exfoliated graphite nanocomposites

    Directory of Open Access Journals (Sweden)

    Creusa Iara Ferreira

    2013-01-01

    Full Text Available The viscoelastic, mechanical and morphological properties of polypropylene/exfoliated graphite nanocomposites with different contents of nanofiller were investigated. According to transmission electron microscopy results, the nanofiller particles were homogeneously dispersed in the matrix. The rheological properties indicated that incorporation of graphite improved the matrix stiffness and had a reinforcing effect. Exfoliated graphite had a weak interaction with the polypropylene. The behavior of the nanocomposites was similar to that of polypropylene in terms of the interfacial detachment inferred from the transmission electron microscopy images and of their G' (storage and G'' (loss moduli, and viscosity. The mechanical properties of the nanocomposites compared to the matrix improved significantly for the flexural and storage moduli with little loss of impact strength.

  1. Morphological, viscoelastic and mechanical characterization of polypropylene/exfoliated graphite nanocomposites

    Energy Technology Data Exchange (ETDEWEB)

    Ferreira, Creusa Iara; Oliveira, Ricardo Vinicius Bof de; Mauler, Raquel Santos, E-mail: raquel.mauler@ufrgs.br [Universidade Federal do Rio Grande do Sul (PGCIMAT/IQ/UFRGS), Porto Alegre, RS (Brazil); Bianchi, Otavio [Universidade de Caxias do Sul (PGMAT/CCET/UCS), RS (Brazil); Oviedo, Mauro Alfredo Soto [Braskem S/A, Rio de Janeiro, RJ (Brazil)

    2013-07-01

    The viscoelastic, mechanical and morphological properties of polypropylene/exfoliated graphite nanocomposites with different contents of nanofiller were investigated. According to transmission electron microscopy results, the nanofiller particles were homogeneously dispersed in the matrix. The rheological properties indicated that incorporation of graphite improved the matrix stiffness and had a reinforcing effect. Exfoliated graphite had a weak interaction with the polypropylene. The behavior of the nanocomposites was similar to that of polypropylene in terms of the interfacial detachment inferred from the transmission electron microscopy images and of their G' (storage) and G' (loss) moduli, and viscosity. The mechanical properties of the nanocomposites compared to the matrix improved significantly for the flexural and storage moduli with little loss of impact strength. (author)

  2. Morphological, viscoelastic and mechanical characterization of polypropylene/exfoliated graphite nanocomposites

    Energy Technology Data Exchange (ETDEWEB)

    Ferreira, Creusa Iara; Oliveira, Ricardo Vinicius Bof de; Mauler, Raquel Santos, E-mail: raquel.mauler@ufrgs.br [Universidade Federal do Rio Grande do Sul (PGCIMAT/IQ/UFRGS), Porto Alegre, RS (Brazil); Bianchi, Otavio [Universidade de Caxias do Sul (PGMAT/CCET/UCS), RS (Brazil); Oviedo, Mauro Alfredo Soto [Braskem S/A, Rio de Janeiro, RJ (Brazil)

    2013-07-01

    The viscoelastic, mechanical and morphological properties of polypropylene/exfoliated graphite nanocomposites with different contents of nanofiller were investigated. According to transmission electron microscopy results, the nanofiller particles were homogeneously dispersed in the matrix. The rheological properties indicated that incorporation of graphite improved the matrix stiffness and had a reinforcing effect. Exfoliated graphite had a weak interaction with the polypropylene. The behavior of the nanocomposites was similar to that of polypropylene in terms of the interfacial detachment inferred from the transmission electron microscopy images and of their G' (storage) and G' (loss) moduli, and viscosity. The mechanical properties of the nanocomposites compared to the matrix improved significantly for the flexural and storage moduli with little loss of impact strength. (author)

  3. Chemical modification of flax reinforced polypropylene composites

    CSIR Research Space (South Africa)

    Jacob John, Maya

    2009-04-01

    Full Text Available This paper presents an experimental study on the static and dynamic mechanical properties of nonwoven based flax fibre reinforced polypropylene composites. The effect of zein modification on flax fibres is also reported. Flax nonwovens were treated...

  4. Resterilized Polypropylene Mesh for Inguinal Hernia Repair

    African Journals Online (AJOL)

    2018-04-19

    Apr 19, 2018 ... Conclusion: The use of sterilized polypropylene mesh for the repair of inguinal ... and nonabsorbable materials to reduce the tissue–mesh. INTRODUCTION ... which we have been practicing in our center since we introduced ...

  5. POLYPROPYLENE-MODIFIED KAOLINITE COMPOSITES: EFFECT ...

    African Journals Online (AJOL)

    Meziane O, Bensedira A, Guessoum M and Haddaoui N

    2016-05-01

    May 1, 2016 ... prepared by the melt intercalation method. ... several beneficial variations on stiffness, hardness, toughness and heat ..... Polypropylene/ untreated and treated kaolinite composites have been prepared via direct melt.

  6. Reinforcement of Recycled Foamed Asphalt Using Short Polypropylene Fibers

    Directory of Open Access Journals (Sweden)

    Yongjoo Kim

    2013-01-01

    Full Text Available This paper presents the reinforcing effects of the inclusion of short polypropylene fibers on recycled foamed asphalt (RFA mixture. Short polypropylene fibers of 10 mm length with a 0.15% by weight mixing ratio of the fiber to the asphalt binder were used. The Marshall stability test, the indirect tensile strength test, the resilient modulus test, and wheel tracking test of the RFA mixtures were conducted. The test results were compared to find out the reinforcing effects of the inclusion of the fiber and the other mixtures, which included the conventional recycled foamed asphalt (RFA mixtures; the cement reinforced recycled foamed asphalt (CRFA mixtures; the semihot recycled foamed asphalt (SRFA mixtures; and recycled hot-mix asphalt (RHMA mixtures. It is found that the FRFA mixture shows higher Marshall stability than the RFA and SRFA mixtures, higher indirect tensile strength than the RFA mixture, and higher rut resistance than the RFA, SRFA, and RHMA mixtures as seen from the wheel tracking test.

  7. Irradiation of isotactic polypropylene and polypropylene/ethylene-propylene (diene-monomer) blends

    NARCIS (Netherlands)

    Gisbergen, van J.G.M.; Meijerink, J.I.; Overbergh, N.; Kleintjes, L.; Lemstra, P.J.

    1989-01-01

    The influence of electron beam irradiation on rheological properties and morphology of polypropylene and polypropylene/ethylene-propylene rubber blends was studied. Electron beam irradiation of isotactic PP causes pronounced chain scission (degradation) at dosis = 100 kGy. Melt viscosity can be

  8. Evaluation of Electroless-Nickel Plated Polypropylene under Thermal Cycling and Mechanical Tests

    Directory of Open Access Journals (Sweden)

    O.O. Ajibola

    2016-09-01

    Full Text Available The electroless-nickel composite (ENC consisting of bright metallic electroless-nickel (EN and dull electroless-nickel-phosphorus (EN-P were deposited on the polypropylene (PP substrate from the sodium hypophosphite baths. The ENC plated specimens were subjected to abrasive wear-adhesion test of 1750, 3500, 7000 and 14000 cycles; thermal cycle-adhesion tests, and tensile strength and creep tests. The deposition of ENC influenced the strength and creep strain properties of the PP. The maximum stress σ of 118 (MPa was obtained from EN-PP specimen at strain  of 0.1 mm/mm as compared with the PP having stress σ of 36 (MPa at strain  of 0.07 mm/mm before failure The surface appearances and microstructures of ENC film on PP substrates were examined under the higher resolution metallurgical microscope with digital camera and microscopic camera. The composition of ENC film was characterized using Scanning Electron Microscopy and Energy Dispersive X-Ray analyses (Jeol JSM-7600F Field Emission SEM/EDX, The micrographs and spectra lines data generated were used to interpret the results.

  9. Aksa plans polypropylene joint venture

    International Nuclear Information System (INIS)

    Alperowicz, N.

    1992-01-01

    Turkish acrylic fiber maker Aksa (Yalova), part of the Akkok textile conglomerate, is studying construction of a world-scale polypropylene (PP) plant as part of its diversification plans. The company says it is engaged in discussions with three 'multinations in the PP business' on the possibility of a joint venture. One of the firms is understood to be Amoco. Aksa is looking at three possible locations for the 100,000 m.t.-150,000 m.t./year plant: Yalova, near Istanbul, where its existing plants are located; Zonguldak, on the Black Sea coast; and within one of the existing complexes or a new site belonging to state-owned Petkim. Aksa has not yet discussed that option with Petkim, which recently received approval to build a $2.5-billion petrochemical complex. The Aksa PP plant would cost about $100 million and would use propylene from world markets. The onstream date depends on Aksa's ability to link up with a foreign partner, but it hopes to complete the unit within three years. Turkey has only one PP plant, a 65,000-m.t./year Petkim unit at Aliaga. The domestic market is currently two to three times that amount and is growing. Petkim also plans a 200,000-m.t./year PP plant as part of its new complex

  10. Laboratory Evaluation of Interactions in the Degradation of a Polypropylene Geotextile in Marine Environments

    Directory of Open Access Journals (Sweden)

    José Ricardo Carneiro

    2018-01-01

    Full Text Available The long-term behaviour of geosynthetics applied in coastal engineering structures can be adversely affected by many agents. This paper studies the resistance of a nonwoven polypropylene geotextile against some degradation agents present in marine environments and evaluates the existence of interactions between them. For that purpose, the geotextile was exposed to some laboratory degradation tests: immersion tests (in seawater, deionised water, and sodium chloride 35 g·L−1, thermooxidation, and artificial weathering. The geotextile was (1 exposed separately to each degradation test and (2 exposed successively to combinations of two or three degradation tests. The damage caused by the degradation tests was evaluated by monitoring the tensile properties of the geotextile. Based on the changes occurred in tensile strength, reduction factors were determined. The reduction factors obtained directly in the multiple exposures were compared with those obtained by the traditional methodology for the combined effect of the degradation agents. The results, among other findings, showed the existence of relevant interactions between the degradation agents and showed that the reduction factors obtained by the traditional methodology were unable to represent accurately (by underestimating the degradation occurred in the geotextile.

  11. Polypropylene reinforced with organophilic clay and brazilian nut fibers; Polipropileno reforcado com argila verde lodo e fibra da castanha-do-brasil

    Energy Technology Data Exchange (ETDEWEB)

    Rocha-Gomes, L.V.; Mondelo-Garcia, F.J.; Vaccioli, K.; Valera, S.T.; Silva-Valenzuela, M.G.; Valenzuela-Diaz, F.R., E-mail: leila@ifes.edu.br [Universidade de Sao Paulo (LPSS/PMT/EP/USP), SP (Brazil). Dept. de Engenharia Metalurgica e de Materiais. Lab. de Materiais Nao-Metalicos

    2014-07-01

    Polymer nanocomposites have been shown to possess better properties when compared with traditional composites. This study aims to investigate the effects of the addition of organophilic clay and Brazilian nut fiber on the polypropylene (PP). First, 5%, 10% and 20% PP/compatibilizer maleic anhydride (PP-g-MA) by weight was added to Pure PP, respectively. From the results, 5% PP-g-MA was defined for preparing the nanocomposites. Samples were prepared containing 5% PP / PP-g-MA reinforced with 5% organophilic Brazilian smectite clay and 5%, 10% and 15% Brazilian nut fiber. Specimens were tested for tensile strength and impact. The materials were characterized by laser diffraction particle size and X-ray diffraction, and the nanocomposites, by mechanical strength and impact. The best result was obtained by inserting 15% fiber. (author)

  12. Effect of the interfacial adhesion on the tensile and impact properties of carbon fiber reinforced polypropylene matrices

    Directory of Open Access Journals (Sweden)

    Clara Leal Nogueira

    2005-03-01

    Full Text Available Thermoplastic composites have been applied in a wide variety of industrial products, showing recently a great potential to be used in aeronautical field. The objectives of this work were to evaluate the fiber/matrix interface of carbon fiber reinforced polypropylene-based matrices after tensile and impact tests and also to compare the mechanical test results of the manufactured laminates. The laminates were prepared by stacking carbon fiber fabric style Plain Weave (CF and films of four different polypropylene matrices, described as (a polypropylene-PP, (b polypropylene-polyethylene copolymer-PP-PE, (c PP-PE with an interfacial compatibilizer-AM1 and (d PP-PE containing an elastomeric modifier-AM2. The composites were processed using hot compression molding. The mechanical testing results showed that the CF-AM1 laminate family presented the lowest impact strength and the highest tensile strength values when compared to the other laminates. SEM analysis observations of both tensile and impact fractured specimens of the CF-PP/PE-AM1 specimens revealed a stronger fiber/matrix interface. The CF-PP/PE-AM2 laminate showed a lower tensile strength and higher impact strength values when compared to the CF-PP/PE-AM1 one. PP-PE and PP laminates presented the lowest impact strength values.

  13. Agave nonwovens in polypropylene composites: mechanical and thermal studies

    CSIR Research Space (South Africa)

    John, MJ

    2015-03-01

    Full Text Available Blends of agave fibres with wool waste, pineapple leaf fibres and polypropylene fibres were manufactured by needle-punching technique. Composites were prepared with polypropylene matrix by the process of compression moulding. The effects of blend...

  14. Rheology of high melt strength polypropylene for additive manufacturing

    DEFF Research Database (Denmark)

    Jagenteufel, Ralf; Hofstätter, Thomas; Kamleitner, Florian

    2017-01-01

    stability, whereas HMS-PP showed a more stable behavior at the investigated temperatures. Hereafter, the material was used in a fused deposition modeling additive manufacturing process, focusing on the investigation of possible improvements of HMS-PP over ABS. Based on the extrusion parameters for ABS...

  15. Kenaf Fibre Reinforced Polypropylene Composites: Effect of Cyclic Immersion on Tensile Properties

    Directory of Open Access Journals (Sweden)

    W. H. Haniffah

    2015-01-01

    Full Text Available This research studied the degradation of tensile properties of kenaf fibre reinforced polypropylene composites due to cyclic immersion into two different solutions, as well as comparison of the developed composites’ tensile properties under continuous and cyclic immersion. Composites with 40% and 60% fibre loadings were immersed in tap water and bleach for 4 cycles. Each cycle consisted of 3 days of immersion and 4 days of conditioning in room temperature (28°C and 55% humidity. The tensile strength and modulus of composites were affected by fibre composition, type of liquid of immersion, and number of cycles. The number of immersion cycles and conditioning caused degradation to tensile strength and modulus of kenaf fibre reinforced polypropylene composites. Continuous and cyclic immersion in bleach caused tensile strength of the composites to differ significantly whereas, for tensile modulus, the difference was insignificant in any immersion and fibre loadings. However, continuous immersion in the bleach reduced the tensile strength of composites more compared to cyclic immersion. These preliminary results suggest further evaluation of the suitability of kenaf fibre reinforced polypropylene composites for potential bathroom application where the composites will be exposed to water/liquid in cyclic manner due to discontinuous usage of bathroom.

  16. Structural characterization and mechanical properties of polypropylene reinforced natural fibers

    Science.gov (United States)

    Karim, M. A. A.; Zaman, I.; Rozlan, S. A. M.; Berhanuddin, N. I. C.; Manshoor, B.; Mustapha, M. S.; Khalid, A.; Chan, S. W.

    2017-10-01

    Recently the development of natural fiber composite instead of synthetics fiber has lead to eco-friendly product manufacturing to meet various applications in the field of automotive, construction and manufacturing. The use of natural fibers offer an alternative to the reinforcing fibers because of their good mechanical properties, low density, renewability, and biodegradability. In this present research, the effects of maleic anhydride polypropylene (MAPP) on the mechanical properties and material characterization behaviour of kenaf fiber and coir fiber reinforced polypropylene were investigated. Different fractions of composites with 10wt%, 20wt% and 30wt% fiber content were prepared by using brabender mixer at 190°C. The 3wt% MAPP was added during the mixing. The composites were subsequently molded with injection molding to prepare the test specimens. The mechanical properties of the samples were investigated according to ISO 527 to determine the tensile strength and modulus. These results were also confirmed by the SEM machine observations of fracture surface of composites and FTIR analysis of the chemical structure. As the results, the presence of MAPP helps increasing the mechanical properties of both fibers and 30wt% kenaf fiber with 3wt% MAPP gives the best result compare to others.

  17. Raman Spectroscopy of Isotactic Polypropylene-Halloysite Nanocomposites

    Directory of Open Access Journals (Sweden)

    Elamin E. Ibrahim

    2012-01-01

    Full Text Available Raman spectroscopy investigations on nanocomposites obtained by dispersing halloysite within isotactic polypropylene are reported. A detailed analysis of the modifications of the regularity band associated to the polymeric matrix is presented. The Raman lines assigned to the polymeric matrix are broadened and weakened as the loading with halloysite is increased. The analysis of Raman lines indicates that the polymeric matrix becomes less crystalline upon the loading with halloysite and that the nanofiller is experiencing a weak dehydration upon dispersion within the polymeric matrix, probably due to the related thermal processing used to achieve the dispersion of halloysite.

  18. Polypropylene-polyethylene blends modified by gamma radiation

    International Nuclear Information System (INIS)

    Terence, Mauro C.; Ruiz, Francisco C.

    2009-01-01

    One way to obtain a better mechanical property of polypropylene and polyethylene is to increasing the number of polymer chains cross-linked by gamma radiation. After irradiation a network is formed as a result of various chemical reactions and the radicals formed are concentrated in the amorphous phase. With the objective to improve the mechanical properties of PP, blends with PE were prepared and irradiated in doses up to 500 kGy, in atmospheric ambient. The molecular characterization of the blends was made by infrared spectroscopy and the data showed an increase in rigidity and a unique behaviour in Izod impact resistance. (author)

  19. Microstructural evolution during tensile deformation of polypropylenes

    International Nuclear Information System (INIS)

    Dasari, A.; Rohrmann, J.; Misra, R.D.K.

    2003-01-01

    Tensile deformation processes occurring at varying strain rates in high and low crystallinity polypropylenes and ethylene-propylene di-block copolymers have been investigated by scanning electron microscopy. This is examined for both long and short chain polymeric materials. The deformation processes in different polymeric materials show striking dissimilarities in spite of the common propylene matrix. Additionally, the deformation behavior of long and their respective short chain polymers was different. Deformation mechanisms include crazing/tearing, wedging, ductile ploughing, fibrillation, and brittle fracture. The different modes of deformation are depicted in the form of strain rate-strain diagrams. At a constant strain rate, the strain to fracture follows the sequence: high crystallinity polypropylenes< low crystallinity polypropylenes< ethylene-propylene di-block copolymers, indicative of the trend in resistance to plastic deformation

  20. Coir dust reinforced recycled polypropylene composites

    International Nuclear Information System (INIS)

    Santos, Bianca B. dos; Costa, Marysilvia F. da; Thire, Rossana M. da S.M.

    2015-01-01

    The environmental impacts caused by disposed plastics encourage the search for new alternatives. Recycling polymers leads to the degradation of their mechanical properties, which can be modified by the addition of fillers. In this paper, recycled polypropylene from plastic cups with 2%, 5% and 10% of coir dust were produced with and without the addition of additives. These composites were characterized by tensile tests, X-ray diffraction, differential scanning calorimetry and scanning electron microscopy on the fracture surface. It was verified the effectiveness of the addition of coir dust in improving the elasticity modulus of recycled polypropylene besides the effectiveness of additives used in promoting the adhesion of the powder to the matrix. However, higher levels of coir dust caused the appearance of air bubbles inside the material, which contributed to its embrittlement. The addition of coir dust promoted a decrease in the degree of polypropylene crystallinity. (author)

  1. Flammability of polypropylene/organoclay nanocomposites

    International Nuclear Information System (INIS)

    Alves, Tatianny Soares; Barbosa, Renata; Carvalho, Laura Hecker de; Canedo, Eduardo Luis

    2014-01-01

    The flammabilities of nanocomposites made with three polypropylene grades (homo and copolymers) with 5 wt % of organoclay (Cloisite 20A), 5 or 15 wt % of maleated polypropylene as compatibilizer, and 0, 0.5 or 1 wt % of cis-13-docosenamide (Erucamide) as co-intercalant, were studied using the horizontal burning test UL94HB. Masterbatches prepared in an internal mixer were diluted in the polypropylene matrix using a corotating twin-screw extruder, with different screw configurations and operating at 240 or 480 rpm. Results indicate that the high burning rate of the composites was not affected by the processing conditions. For all formulations was observed a significant reduction in smoke release, lack of dripping and the formation of a char surface layer, that protected the core of the samples. (author)

  2. Synthesis and characterization of CNTs using polypropylene waste as precursor

    Energy Technology Data Exchange (ETDEWEB)

    Bajad, Ganesh S. [Department of Chemical Engineering, Visvesvaraya National Institute of Technology, Nagpur 440010 (India); Tiwari, Saurabh K. [Department of Chemical Engineering, Indian Institute of Technology Bombay, Powai, Mumbai 400076 (India); Vijayakumar, R.P., E-mail: vijayakumarrp@che.vnit.ac.in [Department of Chemical Engineering, Visvesvaraya National Institute of Technology, Nagpur 440010 (India)

    2015-04-15

    Graphical abstract: - Highlights: • A facile method for producing CNTs from polypropylene waste is proposed. • Optimization of Ni/Mo mole ratio using RSM suggests the adequacy of cubic model. • Process parameters were optimized by RSM using Box–Behnken four factorial design. • Maximum desirability of one suggested that 514% of CNTs would yield over Ni{sub 4}Mo{sub 0.2}MgO{sub 1}. • Increase in Ni/Mo ratio from 0.5 to 20, inner diameter of CNTs decreases from 25 to 2 nm. - Abstract: We study the synthesis of MWCNTs using polypropylene waste as a precursor and Ni/Mo/MgO as a catalyst by the combustion technique. Molar ratios of Ni, Mo and MgO in the Ni/Mo/MgO catalyst were optimized using response surface methodology (RSM) to obtain the maximum yield of CNTs. The mole ratio 4/0.2/1 was found to yield more carbon product. Further, process parameters such as combustion temperature, combustion time, polymer and catalyst weight were optimized by RSM using Box–Behnken three-level and four-factorial design. The best possible combination of process parameters (combustion time of 10 min, combustion temperature of 800 °C, polymer weight of 5 g and catalyst weight of 150 mg) for maximum yield of CNTs was obtained. HRTEM indicates that the diameter of CNTs depends on the catalyst composition used for the synthesis of CNTs. The results of the study indicate a facile method for producing CNTs from polypropylene waste.

  3. Synthesis and characterization of CNTs using polypropylene waste as precursor

    International Nuclear Information System (INIS)

    Bajad, Ganesh S.; Tiwari, Saurabh K.; Vijayakumar, R.P.

    2015-01-01

    Graphical abstract: - Highlights: • A facile method for producing CNTs from polypropylene waste is proposed. • Optimization of Ni/Mo mole ratio using RSM suggests the adequacy of cubic model. • Process parameters were optimized by RSM using Box–Behnken four factorial design. • Maximum desirability of one suggested that 514% of CNTs would yield over Ni 4 Mo 0.2 MgO 1 . • Increase in Ni/Mo ratio from 0.5 to 20, inner diameter of CNTs decreases from 25 to 2 nm. - Abstract: We study the synthesis of MWCNTs using polypropylene waste as a precursor and Ni/Mo/MgO as a catalyst by the combustion technique. Molar ratios of Ni, Mo and MgO in the Ni/Mo/MgO catalyst were optimized using response surface methodology (RSM) to obtain the maximum yield of CNTs. The mole ratio 4/0.2/1 was found to yield more carbon product. Further, process parameters such as combustion temperature, combustion time, polymer and catalyst weight were optimized by RSM using Box–Behnken three-level and four-factorial design. The best possible combination of process parameters (combustion time of 10 min, combustion temperature of 800 °C, polymer weight of 5 g and catalyst weight of 150 mg) for maximum yield of CNTs was obtained. HRTEM indicates that the diameter of CNTs depends on the catalyst composition used for the synthesis of CNTs. The results of the study indicate a facile method for producing CNTs from polypropylene waste

  4. Effect of Surface Modification of Palygorskite on the Properties of Polypropylene/Polypropylene-g-Maleic Anhydride/Palygorskite Nanocomposites

    Directory of Open Access Journals (Sweden)

    David Cisneros-Rosado

    2017-01-01

    Full Text Available The effect of surface modification of palygorskite (Pal on filler dispersion and on the mechanical and thermal properties of polypropylene (PP/polypropylene grafted maleic anhydride (PP-g-MAH/palygorskite (Pal nanocomposites was evaluated. A natural Pal mineral was purified and individually surface modified with hexadecyl tributyl phosphonium bromide and (3-Aminopropyltrimethoxysilane; the pristine and modified Pals were melt-compounded with PP to produce nanocomposites using PP-g-MAH as compatibilizer. The grafting of Pal surface was verified by FT-IR and the change in surface hydrophilicity was estimated by the contact angle of sessile drops of ethylene glycol on Pal tablets. The extent of Pal dispersion and the degree of improvement in both the mechanical and thermal properties were related to the surface treatment of Pal. Modified Pals were better dispersed during melt processing and improved Young’s modulus and strength; however, maximum deformation tended to decrease. The thermal stability of PP/PP-g-MAH/Pal nanocomposites was considerably improved with the content of modified Pals. The degree of crystallinity increased with Pal content, regardless of the surface modification. Surfactant modified Pal exhibited better results in comparison with silane Pal; it is possible that longer alkyl chains from surfactant molecules promoted interactions with polymer chains, thereby improving nanofiller dispersion and enhancing the properties.

  5. Free radicals in irradiated unstabilized polypropylene, as seen by diffuse reflection absorption-spectrophotometry

    International Nuclear Information System (INIS)

    Zagorski, Z.P.; Rafalski, A.

    1998-01-01

    The introduction of UV-Vis absorption spectrophotometry to the study of radiation chemistry of polymers has opened the possibility to investigate even very opaque samples. The virgin powder polypropylene, as obtained from the industrial production line, shows after irradiation unstable products of radiolysis. Until now they were investigated mainly by EPR method. Optical absorption spectra (by diffuse reflection spectrophotometry) contribute to better identification and study of changes in time, temperature and diffusion of reactive gases. Studying the formation of stable compounds, which do not produce EPR signal, we are able to examine these species on the basis of their electronic spectra. The most important results concern the peroxides in irradiated polypropylene

  6. Evaluation of Mechanical Property of Carbon Fiber/Polypropylene Composite According to Carbon Fiber Surface Treatment

    International Nuclear Information System (INIS)

    Han, Song Hee; Oh, Hyun Ju; Kim, Seong Su

    2013-01-01

    In this study, the mechanical properties of a carbon fiber/polypropylene composite were evaluated according to the carbon fiber surface treatment. Carbon fiber surface treatments such as silane coupling agents and plasma treatment were performed to enhance the interfacial strength between carbon fibers and polypropylene. The treated carbon fiber surface was characterized by XP S, Sem, and single-filament tensile test. The interlaminar shear strength (Ilks) of the composite with respect to the surface treatment was determined by a short beam shear test. The test results showed that the Ilks of the plasma-treated specimen increased with the treatment time. The Ilks of the specimen treated with a silane coupling agent after plasma treatment increased by 48.7% compared to that of the untreated specimen

  7. Irradiation and processing of oil palm empty fruit bunch fibres - polypropylene composites

    International Nuclear Information System (INIS)

    Khairul Zaman Mohd Dahlan; Syarifah Hanisah Syed Abdul Aziz

    2000-01-01

    In this study, polypropylene was blended with oil palm empty fruit bunch fibres at a ratio of 60 to 40 by weight, respectively. Trimethylolpropane triacrylate (TMPTA) was used as the crosslinking agent. Homopolymer Polypropylene of MFI 14.0 and EFB fibres of 0.5 -1.0 mm sizes were used through out the experiment. Processing parameters such as temperature, rotor speed and processing time were optimized. Modes of irradiation were established to determine the optimum properties of the composites. The mechanical properties of the composite such as tensile strength, tensile modulus, flexural strength and flexural modulus were measured. The results indicate that temperature, 185 degree C, with a rotor speed of 40 rpm and 9 minutes processing time are sufficient to produce the optimum mechanical properties of PP/EFB composite. Modes of adding TMPTA into the blend and modes of irradiation also have influenced the properties of the composites

  8. Effect of tool geometry on friction stir spot welding of polypropylene sheets

    Directory of Open Access Journals (Sweden)

    M. K. Bilici

    2012-10-01

    Full Text Available The effects of tool geometry and properties on friction stir spot welding properties of polypropylene sheets were studied. Four different tool pin geometries, with varying pin angles, pin lengths, shoulder diameters and shoulder angles were used for friction stir spot welding. All the welding operations were done at the room temperature. Lap-shear tensile tests were carried out to find the weld static strength. Weld cross section appearance observations were also done. From the experiments the effect of tool geometry on friction stir spot weld formation and weld strength were determined. The optimum tool geometry for 4 mm thick polypropylene sheets were determined. The tapered cylindrical pin gave the biggest and the straight cylindrical pin gave the lowest lap-shear fracture load.

  9. Comparison of the mechanical properties between carbon nanotube and nanocrystalline cellulose polypropylene based nano-composites

    International Nuclear Information System (INIS)

    Huang, Jun; Rodrigue, Denis

    2015-01-01

    Highlights: • SWCNT and NCC can effectively improve the mechanical properties of nano-composites. • SWCNT is more effective than NCC to increase modulus and strength. • Longer NCC is more effective to improve the mechanical properties of nano-composites. • It is more economic to use NCC than SWCNT to improve mechanical properties. - Abstract: Using beam and tetrahedron elements to simulate nanocrystalline cellulose (NCC), single wall carbon nanotube (SWCNT) and polypropylene (PP), finite element method (FEM) is used to predict the mechanical properties of nano-composites. The bending, shear and torsion behaviors of nano-composites are especially investigated due to the limited amount of information in the present literature. First, mixed method (MM) and FEM are used to compare the bending stiffness of NCC/PP and SWCNT/PP composites. Second, based on mechanics of materials, the shear moduli of both types of nano-composites are obtained. Finally, fixing the number of fibers and for different volume contents, four NCC lengths are used to determine the mechanical properties of the composites. The bending and shearing performances are also compared between NCC and SWCNT based composites. In all cases, the elastic–plastic analyses are carried out and the stress or strain distributions for specific regions are also investigated. From all the results obtained, an economic analysis shows that NCC is more interesting than SWCNT to reinforce PP

  10. A novel approach in organic waste utilization through biochar addition in wood/polypropylene composites

    Energy Technology Data Exchange (ETDEWEB)

    Das, Oisik [Department of Civil and Environmental Engineering, University of Auckland, Auckland 1142 (New Zealand); Sarmah, Ajit K., E-mail: a.sarmah@auckland.ac.nz [Department of Civil and Environmental Engineering, University of Auckland, Auckland 1142 (New Zealand); Bhattacharyya, Debes [Department of Mechanical Engineering, Center for Advanced Composite Materials, University of Auckland, Auckland 1142 (New Zealand)

    2015-04-15

    Highlights: • Biochar made from waste wood was added with wood polypropylene composites. • 24% biochar gave the best mechanical properties. • 6% biochar had no effect on physico-mechanical properties of composites. • Coupling agent remained unreacted in composites having higher amount of biochar. - Abstract: In an attempt to concurrently address the issues related to landfill gas emission and utilization of organic wastes, a relatively novel idea is introduced to develop biocomposites where biochar made from pyrolysis of waste wood (Pinus radiata) is added with the same wood, plastic/polymer (polypropylene) and maleated anhydride polypropylene (MAPP). Experiments were conducted by manufacturing wood and polypropylene composites (WPCs) mixed with 6 wt%, 12 wt%, 18 wt%, 24 wt%, and 30 wt% biochar. Though 6 wt% addition had similar properties to that of the control (composite without biochar), increasing biochar content to 24 wt% improved the composite’s tensile/flexural strengths and moduli. The biochar, having high surface area due to fine particles and being highly carbonised, acted as reinforcing filler in the biocomposite. Composites having 12 wt% and 18 wt% of biochar were found to be the most ductile and thermally stable, respectively. This study demonstrates that, WPCs added with biochar has good potential to mitigate wastes while simultaneously producing biocomposites having properties that might be suited for various end applications.

  11. A novel approach in organic waste utilization through biochar addition in wood/polypropylene composites

    International Nuclear Information System (INIS)

    Das, Oisik; Sarmah, Ajit K.; Bhattacharyya, Debes

    2015-01-01

    Highlights: • Biochar made from waste wood was added with wood polypropylene composites. • 24% biochar gave the best mechanical properties. • 6% biochar had no effect on physico-mechanical properties of composites. • Coupling agent remained unreacted in composites having higher amount of biochar. - Abstract: In an attempt to concurrently address the issues related to landfill gas emission and utilization of organic wastes, a relatively novel idea is introduced to develop biocomposites where biochar made from pyrolysis of waste wood (Pinus radiata) is added with the same wood, plastic/polymer (polypropylene) and maleated anhydride polypropylene (MAPP). Experiments were conducted by manufacturing wood and polypropylene composites (WPCs) mixed with 6 wt%, 12 wt%, 18 wt%, 24 wt%, and 30 wt% biochar. Though 6 wt% addition had similar properties to that of the control (composite without biochar), increasing biochar content to 24 wt% improved the composite’s tensile/flexural strengths and moduli. The biochar, having high surface area due to fine particles and being highly carbonised, acted as reinforcing filler in the biocomposite. Composites having 12 wt% and 18 wt% of biochar were found to be the most ductile and thermally stable, respectively. This study demonstrates that, WPCs added with biochar has good potential to mitigate wastes while simultaneously producing biocomposites having properties that might be suited for various end applications

  12. Polypropylenes foam consisting of thermally expandable microcapsule as blowing agent

    Science.gov (United States)

    Jeoung, Sun Kyung; Hwang, Ye Jin; Lee, Hyun Wook; Kwak, Sung Bok; Han, In-Soo; Ha, Jin Uk

    2016-03-01

    The structure of thermally expandable microcapsule (TEMs) is consisted of a thermoplastic shell which is filled with liquid hydrocarbon at core. The shell of TEMs becomes soft when the temperature is higher than boiling temperature of liquid hydrocarbon. The shell of TEMs is expanded under the high temperature because the inner pressure of TEMs is increased by vaporization of hydrocarbon core. Therefore, the TEMs are applicable for blowing agents and light weight fillers. In this research, we fabricated the polypropylene (PP) foam by using the TEMs and chemical blowing agents and compared to their physical properties. The density of the specimen was decreased when the contents of chemical blowing agents and TEMs were increased. In addition, the mechanical properties (i.e. tensile strength and impact strength) of specimens were deteriorated with increasing amount of chemical blowing agents and TEMs. However, PP foam produced with TEMs showed higher impact strength than the one with the chemical blowing agent. In order to clarify the dependence of impact strength of PP foam as the blowing agent, the morphology difference of the PP foams was investigated. Expanding properties of PP foams produced with TEMs was changed with TEMs content of PP foams. Processing conditions also influenced the mechanical properties of PP foam containing TEMs.

  13. Laparoscopic Pelvic Floor Repair Using Polypropylene Mesh

    Directory of Open Access Journals (Sweden)

    Shih-Shien Weng

    2008-09-01

    Conclusion: Laparoscopic pelvic floor repair using a single piece of polypropylene mesh combined with uterosacral ligament suspension appears to be a feasible procedure for the treatment of advanced vaginal vault prolapse and enterocele. Fewer mesh erosions and postoperative pain syndromes were seen in patients who had no previous pelvic floor reconstructive surgery.

  14. On clarification of haze in polypropylene

    NARCIS (Netherlands)

    Bernland, K.; Goossens, J.G.P.; Smith, P.; Tervoort, T.A.

    2016-01-01

    The mechanism of reducing light scattering in isotactic polypropylene (i-PP), through the addition of so-called clarifying agents, is studied with small-angle light scattering (SALS) and scanning electron microscopy (SEM). The clarifying agents used in this study depict monotectic phase behavior

  15. Cyclic viscoelastoplasticity of polypropylene/nanoclay composites

    DEFF Research Database (Denmark)

    Drozdov, A.; Christiansen, Jesper de Claville

    2012-01-01

    Observations are reported on isotactic polypropylene/organically modified nanoclay hybrids with concentrations of filler ranging from 0 to 5 wt.% in cyclic tensile tests with a stress–controlled program (oscillations between various maximum stresses and the zero minimum stress). A pronounced effe...

  16. Morphology of Thermoplastic Elastomers:Stereoblock Polypropylene

    Energy Technology Data Exchange (ETDEWEB)

    Pople, John A

    2002-08-06

    The morphologies of low-density (0.86 g/cm{sup 3}), elastomeric polypropylene (ePP) derived from bis(2-arylindenyl) hafnium dichloride were investigated using a combination of polarized optical microscopy (OM), differential scanning calorimetry (DSC), wide angle X-ray scattering (WAXS), Fourier transform infrared (FT-IR) spectroscopy, and tapping mode atomic force microscopy (TMAFM). These low-crystallinity polypropylenes, when crystallized isothermally from the melt, exhibit morphologies reminiscent of classical semi-crystalline polymers. The presence of lamellae, cross-hatching, hedrites, and spherulites was revealed by high resolution TM-AFM. These elastomeric polypropylenes can be fractionated into components of different average tacticities and crystallinities, but similar molecular mass. The analysis of the morphologies of all of the fractions revealed both large hierarchical structures and cross-hatching typical of the {alpha}-modification of crystalline isotactic polypropylene for all but the lowest crystalline ether soluble fraction. Evidence for high-melting crystals in all of the fractions are most consistent with a stereoblock microstructure of atactic and isotactic sequences.

  17. Biomechanical findings in rats undergoing fascial reconstruction with graft materials suggested as an alternative to polypropylene.

    Science.gov (United States)

    Konstantinovic, M L; Ozog, Y; Spelzini, F; Pottier, C; De Ridder, D; Deprest, J

    2010-03-01

    Graft materials used for pelvic floor reinforcement should still be considered as investigational and, therefore, evaluated experimentally and within clinical trials. The present report describes our biomechanical findings in rats implanted with selected novel implant materials, which in recent years have been suggested as alternatives to plain polypropylene (PP) meshes. Full thickness abdominal wall defects were primarily repaired by the implant of interest. Experiments involved eight different implant materials: two partly degradable synthetic implants, that is, a hybrid of polyglactin 910 with PP (Vypro II) and collagen coated PP (Pelvitex); two non-cross linked (Surgisis, InteXēn LP) and two cross-linked materials (Pelvicol, Pelvisoft) and two porous modifications of InteXēn LP and Pelvicol implants. At different time points (7, 14, 30, and 90 days), the implants and surrounding host tissue (explant) were harvested and tensiometry was performed. Tensile strength and location of breakage were recorded. In general resorbable non-cross linked collagen matrices and porous materials were weaker after 90 days; similar behavior was seen for implant materials alone and their construction with the surrounding native tissue. Both non-porous and porous modification of InteXēn LP appeared at 90 days as a very thin layer of collagen that was two-thirds, respectively one-third of the initial thickness. In experimental conditions, sufficient strength was obtained only after 3 months, and PP containing constructs appeared as the strongest though reconstruction with Pelvicol showed comparable outcomes. Lower values for strength of non-cross linked and porous collagen materials are questioning their efficacy for pelvic floor reconstruction. (c) 2009 Wiley-Liss, Inc.

  18. PBI treated polypropylene battery separator

    Science.gov (United States)

    Veryzwyvelt, S. A.

    1981-01-01

    A generalized procedure for fabricating the separator is described. Some of the desired properties considered in fabricating the separator material for nickel-cadmium cells were good mechanical strength, good chemical stability, good wettability to the electrolyte, high electrolyte retention, and gas passage.

  19. Effect of ionizing radiation on polypropylene composites reinforced with coconut fibers

    Energy Technology Data Exchange (ETDEWEB)

    Miranda, Leila F.; Pereira, Nilson C.; Faldini, Sonia B.; Masson, Terezinha J.; Silveira, Luiz H., E-mail: lfmiranda@sti.com.b [Universidade Presbiteriana Mackenzie, Sao Paulo, SP (Brazil). Escola de Engenharia. Curso de Engenharia de Materiais; Silva, Leonardo G. de Andrade e, E-mail: lgasilva@ipen.b [Instituto de Pesquisas Energeticas e Nucleares (IPEN/CNEN-SP), Sao Paulo, SP (Brazil)

    2009-07-01

    The use of the polymeric composite materials has been increasing but these materials have environmental problems related to the discard. To reduce the discard deleterious effect, coconuts, sisal, as well as sugar cane pulp natural based fiber have been studied to replace the synthetic ones. These fibers embedded in a polymeric matrix plays a similar role as the synthetic ones, in terms of mechanical and thermal properties. The natural fibers are environmentally friendly, easy to recycle and biodegradable. The aim of this work is the study of ionizing radiation effects on the properties of recycled polypropylene composites, reinforced with 10%, 15% and 20% of the coconut fibers, using as coupling agent a substance based on maleic anhydride (MAPP) graphitized polypropylene. The samples were molded by injection, irradiated and submitted to thermal and mechanical tests. The mechanical properties (hardness, impact strength and tensile strength), temperature of thermal distortion (HDT) and Vicat softening temperature of the non irradiated and irradiated composites were determined. The irradiation doses were of 30, 50 and 100kGy in a gamma cell. Regarding the thermal and mechanical properties of non-irradiated samples, the incorporation of coconut fibers to polypropylene resulted in a decrease of impact strength, tensile strength and Vicat softening temperature as well as in an increase in hardness and HDT. This result indicates that the coconut fibers do not act like a reinforcement agent but as biodegradable filler. In the irradiated samples, it was observed a decrease in the impact strength, tensile strength, HDT, and thermal distortion temperature and an increase in the hardness and tensile strength. The Vicat softening temperature shows no change. (author)

  20. Effect of ionizing radiation on polypropylene composites reinforced with coconut fibers

    International Nuclear Information System (INIS)

    Miranda, Leila F.; Pereira, Nilson C.; Faldini, Sonia B.; Masson, Terezinha J.; Silveira, Luiz H.

    2009-01-01

    The use of the polymeric composite materials has been increasing but these materials have environmental problems related to the discard. To reduce the discard deleterious effect, coconuts, sisal, as well as sugar cane pulp natural based fiber have been studied to replace the synthetic ones. These fibers embedded in a polymeric matrix plays a similar role as the synthetic ones, in terms of mechanical and thermal properties. The natural fibers are environmentally friendly, easy to recycle and biodegradable. The aim of this work is the study of ionizing radiation effects on the properties of recycled polypropylene composites, reinforced with 10%, 15% and 20% of the coconut fibers, using as coupling agent a substance based on maleic anhydride (MAPP) graphitized polypropylene. The samples were molded by injection, irradiated and submitted to thermal and mechanical tests. The mechanical properties (hardness, impact strength and tensile strength), temperature of thermal distortion (HDT) and Vicat softening temperature of the non irradiated and irradiated composites were determined. The irradiation doses were of 30, 50 and 100kGy in a gamma cell. Regarding the thermal and mechanical properties of non-irradiated samples, the incorporation of coconut fibers to polypropylene resulted in a decrease of impact strength, tensile strength and Vicat softening temperature as well as in an increase in hardness and HDT. This result indicates that the coconut fibers do not act like a reinforcement agent but as biodegradable filler. In the irradiated samples, it was observed a decrease in the impact strength, tensile strength, HDT, and thermal distortion temperature and an increase in the hardness and tensile strength. The Vicat softening temperature shows no change. (author)

  1. Study of the effect of ionizing radiation on composites of wood flour in polypropylene matrix using barium titanate as coupling agent

    International Nuclear Information System (INIS)

    Ulloa, Maritza Eliza Perez

    2007-01-01

    easier to be processed, increasing the mobility among the macromolecules, so that decreasing the viscosity and increasing the flow rate. The results obtained from the essay of the resistance to traction showed an addition of the property. The increase occurred both in the samples with no additives. The radiation modified the composite material occurring the formation of crosslinking. The incorporation of wood flour to the propylene resulted to the decrease of the resistance to the impact. The decrease of this property can be occurred because of the presence of wood flour can act as a tension concentrator, and consequently, reduces the impact strength. There was an addition in the hardness of the composites which had wood flour. The addition in the hardness was meaningful to the composites WF/PP, that because the bigger the amount of load, the bigger the module of hardness. In the irradiated samples, the hardness increase due to the wood oxidation, face to the radiation. It was observed that in some cases the increase in the radiation dose, did not influenced meaningfully in the variation of the temperature of thermal deflection of the composites indicating that there was crosslinking among the molecules promoted by TPDGA, and an improvement in the adhesion among interfaces promoted by the titanate. In the essay of temperature of softening Vicat, results presented were quite closed to pure PP and the results were not meaningful, the temperature of the composites can be considered the same of the pure PP. The ionizing radiation interacted in the composite material crosslinking the PP and oxidant the wood, what shows an increase in some proprieties and decrease in others ones. (author)

  2. Effect of atmospheric pressure plasma treatment condition on adhesion of ramie fibers to polypropylene for composite

    Energy Technology Data Exchange (ETDEWEB)

    Li, Ying [College of Material and Textile Engineering, Jiaxing University, Jiaxing 314033 (China); Center for Plasma-Aided Manufacturing, Madison, WI 53706 (United States); School of Human Ecology, University of Wisconsin-Madison, Madison, WI 53706 (United States); Manolache, Sorin [Center for Plasma-Aided Manufacturing, Madison, WI 53706 (United States); US Forest Products Laboratory, Madison, WI 53726 (United States); Qiu, Yiping, E-mail: ypqiu@dhu.edu.cn [College of Textiles, Donghua University, Shanghai 201620 (China); Sarmadi, Majid, E-mail: majidsar@wisc.edu [Center for Plasma-Aided Manufacturing, Madison, WI 53706 (United States); School of Human Ecology, University of Wisconsin-Madison, Madison, WI 53706 (United States); Materials Science Program, University of Wisconsin-Madison, Madison, WI 53706 (United States)

    2016-02-28

    Graphical abstract: - Highlights: • The continuous ethanol flow technique can successfully modify ramie fiber surface with an increase in IFSS value up to 50%. • Response surface methodology was applied to design the plasma treatment parameters for ramie fiber modification. • The ethanol flow rate was the most influential treatment parameter in plasma modification process. - Abstract: In order to improve the interfacial adhesion between hydrophilic ramie fibers and hydrophobic polypropylene (PP) matrices, ramie fibers are modified by atmospheric pressure dielectric barrier discharge (DBD) plasma with our continuous ethanol flow technique in helium environment. A central composite design of experiments with different plasma processing parameter combinations (treatment current, treatment time and ethanol flow rate) is applied to find the most influential parameter and to obtain the best modification effect. Field emission scanning electron microscope (SEM) shows the roughened surfaces of ramie fibers from the treated groups due to plasma etching effect. Dynamic contact angle analysis (DCAA) demonstrates that the wettability of the treated fibers drastically decreases. Microbond pullout test shows that the interfacial shear strength (IFSS) between treated ramie fibers and PP matrices increases significantly. Residual gas analysis (RGA) confirms the creation of ethyl groups during plasma treatment. This study shows that our continuous ethanol flow technique is effective in the plasma modification process, during which the ethanol flow rate is the most influential parameter but all parameters have simultaneous influence on plasma modification effect of ramie fibers.

  3. Fire retardancy assessment of polypropylene composite filed with nano clay prepared from Iraqi bentonite

    Science.gov (United States)

    Kareem Salih, Watheq

    2018-05-01

    Fire retardants have an extraordinary importance because of their role in saving the people, property and reducing the damages and minimizing the dangers resulting from fires and burning of polymeric composites which are used in different civil and industrial fields. The work in this paper can be divided into two main stages. In first one nano-clay was manufactured from Iraqi bentonite and it was characterized using AFM, XRD, XRF, SEM, and BET. The AFM test showed the particle size of prepared nano clay was about 99.25 nm. In the second stage, polypropylene/nano clay composites at three low loading percents (0%,2%,4%,6%) were formulated via twin screw extruder. The fire retardancy tests included burning rate according to ASTM:D-635 and maximum flame height of flame according to ASTM:D-3014. Besides, the mechanical tests and thermal behavior of prepared samples were investigated. The results showed that (4%) of nano-clay had the maximum fire retardancy and while at (2%) loading, the maximum value of tensile strength and Yong modulus were obtained. The maximum heat of fusion was recorded for 6% nano clay sample. The final results assessment confirmed on the possibility of using low loadings of prepared nano clay to improve the fire retardancy, mechanical and thermal properties successfully.

  4. The Usage Of Nutshell In The Production of Polypropylene Based on Polymer Composite Panels

    Directory of Open Access Journals (Sweden)

    Selçuk Akbaş

    2013-04-01

    Full Text Available Natural fibers have been commonly utilized to reinforced materials for many years. Recently due to advantages of natural fibers such as low cost, high physical and mechanical resistance are produced plastic-composite materials by mixing various proportions. In addition, plastic composites are used natural fibers include agricultural wastes (wheat straw, rice straw, hemp fiber, shells of various dry fruits, etc.. In this study, polymer composites were manufactured using waste nutshell flour as filler and polypropylene (PP as polymer matrix. The nutshell-PP composites were manufactured via extrusion and compression methods. The final product tested to determine their tensile, flexural, impact strength properties as well as some physical features such as thickness swelling and water absorptions. The best results were obtained composites containing 30% nutshell flour. In addition, composites which were produced nutshell provided the values of ASTM D6662 standard. The data collected in our country which waste a large portion of nutshell allows for the evaluation of the production polymer composites. The incorporation of nutshell flour feasible to produce plastic composites when appropriate formulations were used. As a result hazelnut shell which was considered agricultural waste can be utilized in polymer composite production.

  5. Mechanical and thermal properties of polymer composite based on natural fibers: Moroccan hemp fibers/polypropylene

    International Nuclear Information System (INIS)

    Elkhaoulani, A.; Arrakhiz, F.Z.; Benmoussa, K.; Bouhfid, R.; Qaiss, A.

    2013-01-01

    Highlights: ► Moroccan hemp fibers are used as reinforcement in thermoplastic matrix. ► Moroccan hemp fiber was alkali treated to remove waxes and noncellulosic component. ► Fiber–matrix adhesion was assured by the use of a SEBS-g-MA as a compatibilizer. - Abstract: Moroccan hemp is a cellulosic fiber obtained from the north of Morocco. Their use as reinforcement in thermoplastic matrix composite requires a knowledge of their morphology and structure. In this paper the Moroccan hemp fiber was alkali treated to remove waxes and noncellulosic surface components. Fiber/matrix adhesion was assured by the use of a styrene-(ethylene-butene)-styrene three-block copolymer grafted with maleic anhydride (SEBS-g-MA) as a compatibilizer. Scanning electron microscopy (SEM), Fourier transforms infrared spectroscopy (FT-IR), Thermogravimetric analysis (TGA), tensile and torsional tests were carried out for hemp fibers polypropylene composite and the compatibilized composite at different fiber content. Thus, the binary composite PP/hemp fibers (Alk) and ternary system with maleic anhydride indicate clearly an improved adhesion of the fiber to the matrix as results of the good interaction at the interface. A gain of 50% on the Young’s modulus of PP/hemp 25 wt.% without coupling agent and 74% on the PP/hemp 20 wt.% composite with the coupling agent were found. Tensile strength curve shows a remarkable stabilization when the coupling agent was used

  6. Effect of Polypropylene and Basalt Fiber on the Behavior of Mortars for Repair Applications

    Directory of Open Access Journals (Sweden)

    Chaohua Jiang

    2016-01-01

    Full Text Available The fresh, mechanical, and durability properties of the polypropylene fiber-reinforced mortar (PP FRM and the basalt fiber-reinforced mortar (BFRM with various fiber contents were tested in this paper. The test results show that the presence of polypropylene (PP fiber and basalt fiber (BF in the mortar reduces the initial slump flow and increases the slump flow loss rate. The bond strength and flexural strength of fiber-reinforced mortar (FRM are improved, whereas no obvious improvement on the compressive strength has been observed. Compared with the control mortar, the bond strength of PP FRM and BFRM reinforced with 0.6 kg/m3, 1.6 kg/m3, and 2.6 kg/m3 fiber increases by 16.60%–28.80% and 10.60%–21.40%, respectively. Furthermore, FRM shows lower drying shrinkage, superior abrasion resistance, water impermeability, and freeze-thaw resistance compared with the control mortar. The abrasion resistance strength of PP FRM and BFRM is 77.30% and 38.65% more than the control mortar with 2.6 kg/m3 fiber content. Therefore, PP FRM and BFRM are suitable to be utilized as repair materials, especially in repairing hydraulic structures surfaces with excellent bond strength and abrasion resistance.

  7. The influence of antioxidant on positron annihilation in polypropylene

    International Nuclear Information System (INIS)

    Djourelov, N.; He, C.; Suzuki, T.; Ito, Y; Kondo, K.; Ito, Y.; Shantarovich, V.P.

    2003-01-01

    The purpose of this report is to check the influence of the carbonyl groups (CG), created by oxygen naturally dissolved in a polymer matrix and by the source irradiation, on annihilation characteristics of free positrons using the positron annihilation lifetime spectroscopy (PALS) and coincidence Doppler-broadening spectroscopy (CDBS). Positron annihilation in a pure polypropylene (PP) and in an antioxidant-containing polypropylene (PPA) sample at room and low temperatures has been studied by CDBS. PALS has been used as an o-Ps (orth-positronium) formation monitor. The momentum density distributions of electrons obtained by CDBS at the beginning of measurements have been compared to that at the o-Ps intensity saturation level. It has been shown that the initial concentration of carbonyl groups in a PP sample is high, while for an antioxidant-containing sample, PPA, carbonyl groups are not detected by CDBS. CDBS spectra for a PP can be explained by annihilation of free positrons with the oxygen contained in the carbonyl groups. For a PPA sample, no significant contribution of annihilation with oxygen core electrons can be concluded. (Y. Kazumata)

  8. Investigation of Fibres Migration in Cotton/Polypropylene Blended Yarn

    Directory of Open Access Journals (Sweden)

    Dzmitry RYKLIN

    2014-09-01

    Full Text Available This study is devoted to theoretical and experimental research of fibres migration in blended yarns. A hypothesis states that due to fibres migration their tension in yarn becomes equal. On the basis of that hypothesis, we identified the factors that affect the migration. The main factors influencing are differences in Young's modulus and density of fibres. Simulating the fibres migration we obtained the formulae for determining the proportion of fibres in the external and inner layers of blended yarn. These formulae were proved by analysis of cross-section of cotton/polypropylene yarn. Results of blended yarn processing in knitting showed that migration of polypropylene fibres in direction to the yarn surface leads to significant increase of yarn breakages due to growth of its friction coefficient. Reduction of the input yarn tension by 10 % – 15 % helped to stabilize the process of knitting. It was found that the usage of theoretical information about fibres migration allows to draw conclusions about the necessity of adjustments to settings of subsequent processing of blended yarns. DOI: http://dx.doi.org/10.5755/j01.ms.20.3.4610

  9. Investigation of some physical properties of polypropylene irradiated by gamma rays

    International Nuclear Information System (INIS)

    Kattn, M.; Ajji, Z.

    2005-03-01

    Pure polypropylene samples were exposed to different of gamma radiation up to 100 kGy in presence of oxygen or nitrogen. Some physical properties were investigated in relation to the radiation dose: melting point, crystallinity, apparent activation energy; tensile strength,; elongation. The data show that the crystallinity decreases at low doses. In addition, the melting point is shifted to lower temperature with increasing the irradiation dose. The apparent activation energy increases with increasing irradiation dose. The tensile strength increases for low doses up to maximum, and after this value it decreases increasing (Authors)

  10. OPTIMIZATION OF PROCESS PARAMETERS FOR ENHANCED MECHANICAL PROPERTIES OF POLYPROPYLENE TERNARY NANOCOMPOSITES

    Directory of Open Access Journals (Sweden)

    Oladipupo Olaosebikan Ogunleye

    2015-02-01

    Full Text Available Preparation of Polypropylene ternary nanocomposites (PPTN was accomplished by blending multiwall carbon nanotube (MWCNT in polypropylene/clay binary system using a melt intercalation method. The effects of MWCNT loadings (A, melting temperature (B and mixing speed (C were investigated and optimized using central composite design. The analysis of the fitted cubic model clearly indicated that A and B were the main factors influencing the tensile properties at a fixed value of C. However, the analysis of variance showed that the interactions between the process parameters, such as; AB, AC, AB2, A2B and ABC, were highly significant on both tensile strength and Young’s modulus enhancement, while no interaction is significant in all models considered for elongation. The established optimal conditions gave 0.17%, 165 °C, and 120 rpm for A, B and C, respectively. These conditions yielded a percentage increase of 57 and 63% for tensile strength and Young’s modulus respectively compared to the virgin Polypropylene used.

  11. Montmorillonite clay/polypropylene (HMSPP) nanocomposites: evaluation of thermal and mechanical properties

    International Nuclear Information System (INIS)

    Komatsu, L.G.H.; Oliani, W.L.; Lugao, A.B.; Parra, D.F.

    2014-01-01

    The evaluation of HMSPP (high melt strength polypropylene) properties in nanocomposites was done in composites of 0.1; 1; 3; 5; 10 wt% of Cloisite 20A clay. The PP-g-MA (polypropylene graft maleic anhydride) was the compatibilizer agent in the process of extrusion in twin-screw. Mechanical tests performed in the nanocomposites with higher clay content showed higher values of rupture in 5 and 10 wt% of Cloisite. The thermal properties were evaluate utilizing Calorimetry Differential Exploratory (DSC) and in the sample of 10 wt% of Cloisite were observed increase of the melting temperature and increase of crystallinity. The morphology was investigated by the Scanning Electron Microscopy (SEM) and Fourier Transformed Infrared (FTIR), in which the sample with lower clay amount, 1 wt% of Cloisite showed better dispersion of the clay. X-Ray Diffraction reported the clay intercalation in the sample with 5 wt% of clay. (author)

  12. Mechanical and thermal properties of polypropylene composites with curaua fibre irradiated with gamma radiation

    International Nuclear Information System (INIS)

    Egute, Nayara S.; Forster, Pedro L.; Parra, Duclerc F.; Fermino, Danilo M.; Santana, Sebastiao; Lugao, Ademar B.

    2009-01-01

    Thermal and mechanical behavior of polypropylene with curaua fibre composites were investigated. The treatment of the curaua fibres was processed in alkaline solution (10% wt NaOH). A coupling agent was used (maleic anhydride) to increase the adhesion of the fibre/matrix interface. This composite was irradiated with gamma source in the doses of 5, 15 and 30 kGy and the adhesion between the fibres and the polymeric matrix was monitored to observe probable changes. The thermal behavior was evaluated using differential scanning calorimetry (DSC) and Thermogravimetry (TGA). The mechanical behavior was evaluated using tensile strength in comparison with non-reinforced polypropylene resin. The morphology of the composite fracture surface was observed using scanning electron microscopy (SEM). There were no significant changes in the thermal properties neither in the adhesion of irradiated fibres at doses of 5, 15 and 30 kGy of gamma radiation. (author)

  13. Texturing of polypropylene (PP) with nanosecond lasers

    Science.gov (United States)

    Riveiro, A.; Soto, R.; del Val, J.; Comesaña, R.; Boutinguiza, M.; Quintero, F.; Lusquiños, F.; Pou, J.

    2016-06-01

    Polypropylene (PP) is a biocompatible and biostable polymer, showing good mechanical properties that has been recently introduced in the biomedical field for bone repairing applications; however, its poor surface properties due to its low surface energy limit their use in biomedical applications. In this work, we have studied the topographical modification of polypropylene (PP) laser textured with Nd:YVO4 nanosecond lasers emitting at λ = 1064 nm, 532 nm, and 355 nm. First, optical response of this material under these laser wavelengths was determined. The application of an absorbing coating was also studied. The influence of the laser processing parameters on the surface modification of PP was investigated by means of statistically designed experiments. Processing maps to tailor the roughness, and wettability, the main parameters affecting cell adhesion characteristics of implants, were also determined. Microhardness measurements were performed to discern the impact of laser treatment on the final mechanical properties of PP.

  14. Development of polypropylene (PP)/bentonite organoclay nanocomposites; Desenvolvimento de nanocompositos de polipropileno/argila bentonitica organofilica

    Energy Technology Data Exchange (ETDEWEB)

    Oliveira, Carlos Ivan Ribeiro de; Rocha, Marisa Cristina Guimaraes; Verly, Jessica, E-mail: carlosivanr@gmail.com [Universidade do Estado do Rio de Janeiro (UERJ), Nova Friburgo, RJ (Brazil). Instituto Politecnico; Silva, Ana Lucia Nazareth da [Universidade Federal do Rio de Janeiro (UFRJ), RJ (Brazil). Instituto de Macromoleculas Professora Eloisa Mano; Bertolino, Luiz Carlos [Centro de Tecnologia Mineral (CETEM), Rio de Janeiro, RJ (Brazil)

    2016-07-01

    In recent years, a significant number of studies on polymer/clay nanocomposites has been developed due to the improved properties these materials have compared to those of the conventional composites. Among the various clays used for preparing nanocomposites, the bentonite clays have been the most widely used. In this context, the aim of this work is to develop polypropylene/organoclay nanocomposites based on deposits of bentonite clays recently discovered in Cubati, PB. The composites were prepared in a twin screw extruder. The structural characterization of the produced materials indicated a possible intercalation of the polymer chains between the layers of the organoclay. The results of impact strength showed that the addition of clay as well as the initial addition of clay and compatibilizer decreased the impact strength of polypropylene. The Young's modulus and tensile strength of the polymer were not significantly affected by the filler addition. However, an increase of the elongation at break was observed. (author)

  15. Processing and Characterization of a Polypropylene Biocomposite Compounded with Maleated and Acrylated Compatibilizers

    Directory of Open Access Journals (Sweden)

    Brent A. Nerenz

    2012-01-01

    Full Text Available Polypropylene (PP biocomposites containing 20 wt.% sunflower hull as a particulate reinforcement were compounded and tested under tensile, flexural, and impact loadings. The incorporation of the sunflower hull without compatibilizer resulted in diminished tensile strength and impact energy absorption but increased flexural strength and both tensile modulus and flexural modulus when compared to neat PP. Formulations containing three different chemical compatibilizers were tested to determine their effectiveness in improving the interfacial adhesion between the fiber surface and PP chains. Maleic anhydride grafted with PP (MA-g-PP achieved greater improvements in tensile strength but reduced impact strength in comparison to an acrylic-acid-grafted PP compatibilizer (AA-g-PP. The molecular weight, graft level, and the ability to affect strength, modulus, and absorbed impact energy were also investigated for the compatibilizers. A MA-g-PP having high molecular weight and low graft level was most effective in improving the investigated properties of a sunflower hull-reinforced polypropylene biocomposite.

  16. Effect of polypropylene maleic anhydride (PPMAH) on mechanical and morphological properties of polypropylene (PP)/recycled acrylonitrile butadiene rubber (NBRr)/empty fruit bunch (EFB) composites

    Science.gov (United States)

    Othman, Nurul Syazwani; Santiagoo, Ragunathan; Abdillahi, Khalid Mohamed; Ismail, Hanafi

    2017-07-01

    The fabrication of polypropylene (PP)/ recycled acrylonitrile butadiene rubber (NBRr)/ empty fruit bunch (EFB) composites were investigated. The effects of polypropylene maleic anhydride (PPMAH) as a compatibilizer on the mechanical and morphological properties of PP/NBRr/EFB composites were studied. Composites were prepared through melt mixing using heated two roll mill at 180 °C for 9 minutes and rotor speed of 15 rpm. NBRr loading were varied from 0 to 60 phr and PPMAH was fixed for 5 phr. The composites were moulded into a 1 mm thin sheet using hot press machine and then cut into dumbbell shape. The mechanical and morphological properties of composites were examined using universal tensile machine (UTM) and scanning electron microscope (SEM), respectively. Tensile strength and Young's modulus of PP/NBRr/EFB composites decreased with increasing NBRr loading, whilst increasing the elongation at break. However, PPMAH compatibilized composites have resulted 27% to 40% and 25% to 42% higher tensile strength and Young's modulus, respectively, higher compared to uncompatibilized composites. This was due to the better adhesion between PP/NBRr matrices and EFB filler with the presence of maleic anhydride moieties. From the morphological study, the micrograph of PPMAH compatibilized composites has proved the well bonded and good attachments of EFB filler with PP/NBRr matrices which results better tensile strength to the PP/NBRr/EFB composites.

  17. Green aqueous surface modification of polypropylene for novel polymer nanocomposites.

    Science.gov (United States)

    Thakur, Vijay Kumar; Vennerberg, Danny; Kessler, Michael R

    2014-06-25

    Polypropylene is one of the most widely used commercial commodity polymers; among many other applications, it is used for electronic and structural applications. Despite its commercial importance, the hydrophobic nature of polypropylene limits its successful application in some fields, in particular for the preparation of polymer nanocomposites. Here, a facile, plasma-assisted, biomimetic, environmentally friendly method was developed to enhance the interfacial interactions in polymer nanocomposites by modifying the surface of polypropylene. Plasma treated polypropylene was surface-modified with polydopamine (PDA) in an aqueous medium without employing other chemicals. The surface modification strategy used here was based on the easy self-polymerization and strong adhesion characteristics of dopamine (DA) under ambient laboratory conditions. The changes in surface characteristics of polypropylene were investigated using FTIR, TGA, and Raman spectroscopy. Subsequently, the surface modified polypropylene was used as the matrix to prepare SiO2-reinforced polymer nanocomposites. These nanocomposites demonstrated superior properties compared to nanocomposites prepared using pristine polypropylene. This simple, environmentally friendly, green method of modifying polypropylene indicated that polydopamine-functionalized polypropylene is a promising material for various high-performance applications.

  18. Mechanical and thermal properties of eco-friendly poly(propylene carbonate)/cellulose acetate butyrate blends.

    Science.gov (United States)

    Xing, Chenyang; Wang, Hengti; Hu, Qiaoqiao; Xu, Fenfen; Cao, Xiaojun; You, Jichun; Li, Yongjin

    2013-02-15

    The eco-friendly poly(propylene carbonate) (PPC)/cellulose acetate butyrate (CAB) blends were prepared by melt-blending in a batch mixer for the first time. PPC and CAB were partially miscible because of the drastically shifted glass transition temperatures of both PPC and CAB, which originated from the specific interactions between carbonyl groups and hydroxyl groups. The incorporation of CAB into PPC matrix enhanced not only tensile strength and modulus of PPC dramatically, but also improved heat resistance and thermal stability of PPC significantly. The tensile strength and the modulus of PPC/CAB=50/50 blend are 27.7 MPa and 1.24 GPa, which are 21 times and 28 times higher than those of the unmodified PPC, respectively. Moreover, the elongation at break of PPC/CAB=50/50 blend is as high as 117%. In addition, the obtained blends exhibited good transparency, which is very important for the package materials. The results in this work pave new possibility for the massive application of eco-friendly polymer materials. Copyright © 2012 Elsevier Ltd. All rights reserved.

  19. Tissue Engineering Bionanocomposites Based on Poly(propylene fumarate

    Directory of Open Access Journals (Sweden)

    Ana M. Diez-Pascual

    2017-06-01

    Full Text Available Poly(propylene fumarate (PPF is a linear and unsaturated copolyester based on fumaric acid that has been widely investigated for tissue engineering applications in recent years due to its tailorable mechanical performance, adjustable biodegradability and exceptional biocompatibility. In order to improve its mechanical properties and spread its range of practical applications, novel approaches need to be developed such as the incorporation of fillers or polymer blending. Thus, PPF-based bionanocomposites reinforced with different amounts of single-walled carbon nanotubes (SWCNT, multi-walled carbon nanotubes (MWCNT, graphene oxide nanoribbons (GONR, graphite oxide nanoplatelets (GONP, polyethylene glycol-functionalized graphene oxide (PEG-GO, polyethylene glycol-grafted boron nitride nanotubes (PEG-g-BNNTs and hydroxyapatite (HA nanoparticles were synthesized via sonication and thermal curing, and their morphology, biodegradability, cytotoxicity, thermal, rheological, mechanical and antibacterial properties were investigated. An increase in the level of hydrophilicity, biodegradation rate, stiffness and strength was found upon increasing nanofiller loading. The nanocomposites retained enough rigidity and strength under physiological conditions to provide effective support for bone tissue formation, showed antibacterial activity against Gram-positive and Gram-negative bacteria, and did not induce toxicity on human dermal fibroblasts. These novel biomaterials demonstrate great potential to be used for bone tissue engineering applications.

  20. Synthesis and characterization of polypropylene/jigsaw wood ash composite

    International Nuclear Information System (INIS)

    Sudirman; Karo Karo, Aloma; Gunawan, Indra; Handayani, Ari; Hertinvyana, Evi

    2002-01-01

    The composite of polypropylene (PP) polymer with jigsaw wood ash as filler is the alternative composite material. The dispersion of the filler in the composite is random with the jigsaw wood ash composition of 10,30, and 50% by volume. The characterization of composite are done to measure its mechanical properties, physical properties and microstructure by using XRD and SEM. From this research, it is concluded that increasing filler content of the composite will decrease its mechanical and physical properties. The comparation of different composites are found that tensile strength of PP MF 10 is higher 4.24% compared with PP MF 2 as a matrix. It is also found that melting temperature of PP MF 10 is higher 4.09% compared with PP MF 2 as a matrices and the decomposition temperature different is 0.17%. The degree of crystallinity of composite with PP MF 10 as a matrices is 2.55% higher compared with PP MF 2. The higher degree of crystallinity is increasing the tensile strength

  1. The effect of temperature and drawing ratio on the mechanical properties of polypropylene monofilaments

    Science.gov (United States)

    Taheri, Hesam; Nóbrega, João Miguel; Samyn, Pieter; Covas, José Antonio

    2014-05-01

    In this work, the simultaneous effect of both temperature and drawing ratio during processing of polypropylene monofilaments has been investigated. The basis of this work specifically aims at emphasizing the conditions of temperature and drawing ratio applied in the cooling bath, in order to find out under which conditions the named parameters can be applied in a processing line under continuous extrusion. The effects of temperature are studied for a constant total drawing ratio to analyze the influences on mechanical properties and structural differences of the final polypropylene monofilament. The quenched monofilaments were drawn around an adjustable guide assembly in the quench bath and first drawing stage, imparting thermal and mechanical treatments to the filaments. In the heating stage, monofilaments are affected to high-speed draw rolls while passing through the oven. As such, the best conditions to produce a polypropylene monofilament with high tenacity strength were determined. Results of this study show that the monofilament properties are significantly affected by temperature in the cooling zone. The nature of the first drawing had a significant effect on the end properties and monofilaments with modulus of 637 MPa have finally been manufactured. We have also proposed a new hypothesis, which is termed "gap nucleation" and determine this phenomenon in the gap between die and cooling bath.

  2. Study of Tensile Properties and Deflection Temperature of Polypropylene/Subang Pineapple Leaf Fiber Composites

    Science.gov (United States)

    Hafizhah, R.; Juwono, A. L.; Roseno, S.

    2017-05-01

    The development of eco-friendly composites has been increasing in the past four decades because the requirement of eco-friendly materials has been increasing. Indonesia has a lot of natural fiber resources and, pineapple leaf fiber is one of those fibers. This study aimed to determine the influence of weight fraction of pineapple leaf fibers, that were grown at Subang, to the tensile properties and the deflection temperature of polypropylene/Subang pineapple leaf fiber composites. Pineapple leaf fibers were pretreated by alkalization, while polypropylene pellets, as the matrix, were extruded into sheets. Hot press method was used to fabricate the composites. The results of the tensile test and Heat Deflection Temperature (HDT) test showed that the composites that contained of 30 wt.% pineapple leaf fiber was the best composite. The values of tensile strength, modulus of elasticity and deflection temperature were (64.04 ± 3.91) MPa; (3.98 ± 0.55) GPa and (156.05 ± 1.77) °C respectively, in which increased 187.36%, 198.60%, 264.72% respectively from the pristine polypropylene. The results of the observation on the fracture surfaces showed that the failure modes were fiber breakage and matrix failure.

  3. THE FTIR STUDIES OF PHOTO-OXIDATIVE DEGRADATION OF POLYPROPYLENE

    Institute of Scientific and Technical Information of China (English)

    WEN Zaiqing; HU Xingzhou; SHEN Deyan

    1988-01-01

    The photo-oxidative degradation process of polypropylene film containing iron ions was investigated via FTIR and absorbance substraction technique. It is shown that the iron ions play an important role in the decomposition of hydroperoxide and the increase of the degradation rate of polypropylene film. Theamorphous region of PP film undergoes degradation prior to the crystalline one.

  4. Melt rheological properties of natural fiber-reinforced polypropylene

    Science.gov (United States)

    Jarrod J. Schemenauer; Tim A. Osswald; Anand R. Sanadi; Daniel F. Caulfield

    2000-01-01

    The melt viscosities and mechanical properties of 3 different natural fiber-polypropylene composites were investigated. Coir (coconut), jute, and kenaf fibers were compounded with polypropylene at 30% by weight content. A capillary rheometer was used to evaluate melt viscosity. The power-law model parameters are reported over a shear rate range between 100 to 1000 s–1...

  5. Ziegler-Natta catalysts for the preparation of polypropylene clay nanocomposites from magnesium ethoxide

    International Nuclear Information System (INIS)

    Marques, Maria de Fatima V.; Silva, Micheli G. da; Ferreira, Ana Luiza R.

    2009-01-01

    In the present work, the process for the preparation of Ziegler-Natta catalysts based on MgCl 2 /TiCl 4 was evaluated on the synthesis of isotactic polypropylene. The catalysts were produced by the chemical activation process aiming the morphology control, in order to obtain catalyst particles with spherical form. The synthesis of the catalytic support was accomplished from magnesium ethoxide at different preparation conditions. Commercial clays were also added in the preparation of ZN catalysts, which were employed in propylene polymerization. The purpose was to synthesizing polypropylene nanocomposites by in situ polymerization technique. The results indicated that the developed methods of catalyst preparation were effective, since they have shown high activities and they produced PP with high melting temperatures. It was possible to verify by XRD that the catalytic components were inserted in the clays galleries and the polymers obtained by means of those catalysts are possibly exfoliated nanocomposites. (author)

  6. Antifriction basalt-plastics based on polypropylene

    Science.gov (United States)

    Bashtannik, P. I.; Ovcharenko, V. G.

    1997-05-01

    A study is made of the dependence of the mechanical and friction-engineering properties of polypropylene reinforced with basalt fibers on the viscosity of the polymer matrix. It is established that the main factors that determine the mechanical properties of the plastics are the quality of impregnation of the fibers by the binder and the residual length of the reinforcing filler in the composite after extrusion and injection molding. The material that was developed has a low friction coefficient and low rate of wear within a relatively brood range of friction conditions. The basalt-plastics can be used in the rubbing parts of machines and mechanisms subjected to dry friction.

  7. Effect of combined extrusion parameters on mechanical properties of basalt fiber-reinforced plastics based on polypropylene

    Science.gov (United States)

    Bashtannik, P. I.; Ovcharenko, V. G.; Boot, Yu. A.

    1997-11-01

    Basalt fibers are efficient reinforcing fillers for polypropylene because they increase both the mechanical and the tribotechnical properties of composites. Basalt fibers can compete with traditional fillers (glass and asbestos fibers) of polypropylene with respect to technological, economic, and toxic properties. The effect of technological parameters of producing polypropylene-based basalt fiber-reinforced plastics (BFRPs) by combined extrusion on their mechanical properties has been investigated. The extrusion temperature was found to be the main parameter determining the mechanical properties of the BFRPs. With temperature growth from 180 to 240°C, the residual length of the basalt fibers in the composite, as well as the adhesive strength of the polymer-fiber system, increased, while the composite defectiveness decreased. The tensile strength and elastic modulus increased from 35 to 42 MPa and 3.2 to 4.2 GPa, respectively. At the same time, the growth in composite solidity led to its higher brittleness. Thus, a higher temperature of extrusion allows us to produce materials which can be subjected to tensile and bending loads, while the materials produced at a lower temperature of extrusion are impact stable. The effect of the gap size between the extruder body and moving disks on the mechanical properties of the BFRPs is less significant than that of temperature. An increase of the gap size from 2 to 8 mm improves the impregnation quality of the fibers, but the extruder productivity diminishes. The possibility of controling the properties of reinforced polypropylene by varying the technological parameters of combined extrusion is shown. The polypropylene-based BFRPs produced by the proposed method surpass the properties of glass and asbestos fiber-reinforced plastics.

  8. Solid-state drawing of post-consumer isotactic poly(propylene): Effect of melt filtration and carbon black on structural and mechanical properties.

    Science.gov (United States)

    Luijsterburg, B J; Jobse, P S; Spoelstra, A B; Goossens, J G P

    2016-08-01

    Post-consumer plastic waste obtained via mechanical recycling is usually applied in thick-walled products, because of the low mechanical strength due to the presence of contaminants. In fact, sorted post-consumer isotactic poly(propylene) (i-PP) can be considered as a blend of 95% i-PP and 5% poly(ethylene), with traces of poly(ethylene terephthalate) (PET). By applying a treatment such as solid-state drawing (SSD) after melt extrusion, the polymer chains can be oriented in one direction, thereby improving the stiffness and tensile strength. In this research, molecular processes such as crystal break-up and chain orientation of these complex blends were monitored as a function of draw ratio. The melt filter mesh size - used to exclude rigid PET particles - and the addition of carbon black (CB) - often added for coloration in the recycling industry - were varied to investigate their influence on the SSD process. This research shows that despite the blend complexity, the molecular processes during SSD compare to virgin i-PP and that similar draw ratios can be obtained (λmax=20), albeit at reduced stiffness and strength as a result of the foreign polymers present in post-consumer i-PP. It is observed that the process stability improves with decreasing mesh size and that higher draw ratios can be obtained. The addition of carbon black, which resides in the dispersed PE phase, also stabilizes the SSD process. Compared to isotropic post-consumer i-PP, the stiffness can be improved by a factor 10 to over 11GPa, while the tensile strength can be improved by a factor 15-385MPa, which is approx. 70% of the maximum tensile strength achieved for virgin i-PP. Copyright © 2016 Elsevier Ltd. All rights reserved.

  9. The use of maleic anhydride-modified polypropylene for performance enhancement in continuous glass fiber-reinforced polypropylene composites

    NARCIS (Netherlands)

    Rijsdijk, H.A.; Contant, M.; Peijs, A.A.J.M.; Miravete, A.

    1993-01-01

    The influence of maleic anhydride-modified polypropylene (m-PP) on static mech. properties of continuous glass fiber-reinforced polypropylene (PP) composites was studied. M-PP was added to the PP homopolymer to improve the adhesion between the matrix and the glass fiber. Three-point bending tests

  10. Impact of Surface Modification and Nanoparticle on Sisal Fiber Reinforced Polypropylene Nano composites

    International Nuclear Information System (INIS)

    Ibrahim, I. D.; Jamiru, T.; Sadiku, E. R.; Agwuncha, S. Ch.; Kupolati, W. K.

    2016-01-01

    The use of plant fibers, polymer, and nanoparticles for composite has gained global attention, especially in the packaging, automobile, aviation, building, and construction industries. Nano composites materials are currently in use as a replacement for traditional materials due to their superior properties, such as high strength-to-weight ratio, cost effectiveness, and environmental friendliness. Sisal fiber (SF) was treated with 5% NaOH for 2 hours at 70"°C. A mixed blend of sisal fiber and recycled polypropylene (rPP) was produced at four different fiber loadings: 10, 20, 30, and 40 wt.%, while nano clay was added at 1, 3, and 5 wt.%. Maleic anhydride grafted polypropylene (MAPP) was used as the compatibilizer for all composites prepared except the untreated sisal fibers. The characterization results showed that the fiber treatment, addition of MAPP, and nano clay improved the mechanical properties and thermal stability and reduced water absorption of the SF/rPP nano composites. The tensile strength, tensile modulus, and impact strength increased by 32.80, 37.62, and 5.48%, respectively, when compared to the untreated SF/rPP composites. Water absorption was reduced due to the treatment of fiber and the incorporation of MAPP and nano clay.

  11. Effect of surface modified kaolin on properties of polypropylene grafted maleic anhydride

    Science.gov (United States)

    Yang, Ni; Zhang, Zuo-Cai; Ma, Ning; Liu, Huan-Li; Zhan, Xue-Qing; Li, Bing; Gao, Wei; Tsai, Fang-Chang; Jiang, Tao; Chang, Chang-Jung; Chiang, Tai-Chin; Shi, Dean

    To achieve reinforcement of mechanical and thermal performances of polypropylene (PP) product, this work aimed at fabrication of surface modified kaolin (M-kaolin) filled polypropylene grafted maleic anhydride (PP-g-MAH) composites with varying contents of fillers and investigation of their mechanical and thermal properties. And the prepared PP-g-MAH/M-kaolin composites were characterized by means of Fourier transform infrared spectroscopy (FTIR), scanning electron microscopy (SEM) and thermogravimetric analysis (TGA). Fracture analysis by SEM showed M-kaolin particles were well dispersed in the PP-g-MAH matrix. Mechanical behaviors were determined by tensile strength, tensile strain at break and impact strength analysis. Impact strength of PP-g-MAH/2 wt% M-kaolin composites was improved up to 30% comparing with unfilled composites. Thermostability had been found enhanced when M-kaolin added. The results revealed PP-g-MAH/M-kaolin composites showed the optimal thermal and mechanical properties when 2 wt% of M-kaolin was added.

  12. Microstructure and Properties of Polypropylene/Carbon Nanotube Nanocomposites

    Directory of Open Access Journals (Sweden)

    Dimitrios Bikiaris

    2010-04-01

    Full Text Available In the last few years, great attention has been paid to the preparation of polypropylene (PP nanocomposites using carbon nanotubes (CNTs due to the tremendous enhancement of the mechanical, thermal, electrical, optical and structural properties of the pristine material. This is due to the unique combination of structural, mechanical, electrical, and thermal transport properties of CNTs. However, it is well-known that the properties of polymer-based nanocomposites strongly depend on the dispersion of nanofillers and almost all the discussed properties of PP/CNTs nanocomposites are strongly related to their microstructure. PP/CNTs nanocomposites were, mainly, prepared by melt mixing and in situ polymerization. Young’s modulus, tensile strength and storage modulus of the PP/CNTs nanocomposites can be increased with increasing CNTs content due to the reinforcement effect of CNTs inside the polymer matrix. However, above a certain CNTs content the mechanical properties are reduced due to the CNTs agglomeration. The microstructure of nanocomposites has been studied mainly by SEM and TEM techniques. Furthermore, it was found that CNTs can act as nucleating agents promoting the crystallization rates of PP and the addition of CNTs enhances all other physical properties of PP. The aim of this paper is to provide a comprehensive review of the existing literature related to PP/CNTs nanocomposite preparation methods and properties studies.

  13. Functional behaviour of polypropylene/ZnO-soluble starch nanocomposites

    International Nuclear Information System (INIS)

    Chandramouleeswaran, Subramani; Mhaske, S T; Kathe, A A; Varadarajan, P V; Prasad, Virendra; Vigneshwaran, Nadanathangam

    2007-01-01

    ZnO-polypropylene nanocomposites (nano-PP) were prepared using nanoparticles of ZnO stabilized by soluble starch (nano-ZnO) as filler in PP by the melt mixing process. X-ray diffraction (XRD) and other spectroscopic analysis-ultraviolet-visible (UV-vis), Fourier transform infrared (FTIR) and photoluminescence-revealed the presence and characteristics of nano-ZnO in the composites. The presence of ZnO imparts whiteness, while starch increased the yellowing of polymers. The nanocomposites were analyzed for changes in optical, mechanical, electrical and rheological properties, as influenced by the increasing concentration of nano-ZnO. The mechanical properties were marginally increased and the dielectric strength of the nano-PP increased to a notable level. By monitoring the evolution of the carbonyl absorption bands from FTIR analysis, the efficacy of nano-ZnO in the reduction of photo-degradation due to UV irradiation was demonstrated. The excellent antibacterial activity exhibited by nano-ZnO impregnated PP against two human pathogenic bacteria, Staphylococcus aureus and Klebsiella pneumoniae, makes it a suitable candidate for food packaging applications

  14. Functional behaviour of polypropylene/ZnO soluble starch nanocomposites

    Science.gov (United States)

    Chandramouleeswaran, Subramani; Mhaske, S. T.; Kathe, A. A.; Varadarajan, P. V.; Prasad, Virendra; Vigneshwaran, Nadanathangam

    2007-09-01

    ZnO-polypropylene nanocomposites (nano-PP) were prepared using nanoparticles of ZnO stabilized by soluble starch (nano-ZnO) as filler in PP by the melt mixing process. X-ray diffraction (XRD) and other spectroscopic analysis—ultraviolet-visible (UV-vis), Fourier transform infrared (FTIR) and photoluminescence—revealed the presence and characteristics of nano-ZnO in the composites. The presence of ZnO imparts whiteness, while starch increased the yellowing of polymers. The nanocomposites were analyzed for changes in optical, mechanical, electrical and rheological properties, as influenced by the increasing concentration of nano-ZnO. The mechanical properties were marginally increased and the dielectric strength of the nano-PP increased to a notable level. By monitoring the evolution of the carbonyl absorption bands from FTIR analysis, the efficacy of nano-ZnO in the reduction of photo-degradation due to UV irradiation was demonstrated. The excellent antibacterial activity exhibited by nano-ZnO impregnated PP against two human pathogenic bacteria, Staphylococcus aureus and Klebsiella pneumoniae, makes it a suitable candidate for food packaging applications.

  15. Effect of gamma radiation on the performance of jute fabrics-reinforced polypropylene composites

    Energy Technology Data Exchange (ETDEWEB)

    Haydaruzzaman [Department of Physics, Jahangirnagar University, Savar, Dhaka (Bangladesh); Khan, Ruhul A. [Radiation and Polymer Chemistry Laboratory, Institute of Nuclear Science and Technology, Bangladesh Atomic Energy Commission, G. P.O. Box 3787, Dhaka 1000 (Bangladesh); Khan, Mubarak A. [Radiation and Polymer Chemistry Laboratory, Institute of Nuclear Science and Technology, Bangladesh Atomic Energy Commission, G. P.O. Box 3787, Dhaka 1000 (Bangladesh)], E-mail: makhan.inst@gmail.com; Khan, A.H.; Hossain, M.A. [Department of Physics, Jahangirnagar University, Savar, Dhaka (Bangladesh)

    2009-11-15

    Jute fabrics-reinforced polypropylene (PP) composites (50% fiber) were prepared by compression molding. Composites were fabricated with non-irradiated jute fabrics/non-irradiated PP (C-0), non-irradiated jute fabrics/irradiated PP (C-1), irradiated jute fabrics/non-irradiated PP (C-2) and irradiated jute fabrics/irradiated PP (C-3). It was found that C-3 composite performed the best mechanical properties over other composites. Total radiation dose varied from 250-1000 krad and composites made of using 500 krad showed the best results. The optimized values (C-3 composites) for tensile strength (TS), bending strength (BS) and impact strength (IS) were found to be 63 MPa, 73 MPa and 2.93 kJ/m{sup 2}, respectively.

  16. Study on the formation of the nanogel and microgels polypropylene modified by gamma radiation and incorporation of silver nanoparticles to biocides activity

    International Nuclear Information System (INIS)

    Oliani, Washington Luiz

    2013-01-01

    The study consists of the synthesis of HMSPP (polypropylene with high melt strength), also called polypropylene modified by gamma irradiation from iPP (isotactic polypropylene) in presence of acetylene at 110 kPa pressure and irradiated with γ of 60 Co source at doses of 5, 12.5 and 20 kGy. The gel fraction of the samples was determined by extracting in xylene. The soluble portion of the samples was decanted to deposition on glass substrate until complete volatilization of xylene at room temperature of 25 °C. On the soluble portion of 12.5 kGy irradiated sample were added silver nanoparticles (AgNPs) in proportions of 0.25, 0.5, 1.0, 2.0 and 4.0 wt%. These gel samples were characterized by: scanning electron microscopy/energy dispersive spectroscopy (SEM / EDS), infrared spectroscopy (FTIR), scanning electron microscopy with field emission (FE-SEM), atomic force microscopy (AFM), differential scanning calorimetry (DSC), X-ray diffraction (XRD), reduction of colony forming unit (CFU) (%) and cytotoxicity assay. In this study of the morphology, it has been observed the formation of microgels in polypropylene increasing with the dose PP 5 kGy < PP 12.5 kGy < 20 kGy. Nanoscale structures of gels polypropylene (nanogels and nanofibers) were found in samples of PP 12.5 kGy and 20 kGy. The nanogels are formation of crosslinking, branching and entanglement that are nucleated in regions of high energy concentration (spurs) of one irradiated sample. Efficiency in tests of bactericide activity of the gels with AgNPs was observed versus E. coli and S. aureus from 1% AgNPs and non cytotoxicity were characterized in those samples for mammalian cells. In a second stage of this work films of the blend of PP and modified PP (50/50) were produced in a twin screw extruder. AgNPs were added to the extrusion processing in proportions of 0.1; 0.25; 0.5; 1.0; 1.0 PVP; 2.0 and 4.0 wt%. The films obtained were characterized by differential scanning calorimetry (DSC), thermogravimetry

  17. Evaluation of the acquirement of nano composites of polypropylene and a bentonite organophilized by different methodologies

    International Nuclear Information System (INIS)

    Paiva, Lucilene B. de; Morales, Ana R.; Branciforti, Marcia C.; Bretas, Rosario E.S.

    2009-01-01

    This work describes the organophilization of an argentinean sodium bentonite with a quaternary ammo nium salt, by two methodologies: cation exchange in aqueous dispersion and intercalation in semi-solid medium. The modified samples were used in the preparation of nano composites, with polypropylene as a matrix and polypropylene-graft-maleic anhydride as a coupling agent, through melt intercalation by using a twin-screw micro extruder. The organophilic bentonites were characterized by the swelling capacity test in water and in xylene and by X-ray diffraction, and the nano composites were characterized by X-ray diffraction and transmission electronic microscopy. The results showed that were obtained nano composites with structures partially intercalated and exfoliated. (author)

  18. Polyfunctional monomers as additives for enhancing the radiation copolymerization of styrene with polyethylene, polypropylene, and PVC

    International Nuclear Information System (INIS)

    Ang, C.H.; Garnett, J.L.; Levot, R.; Long, M.A.

    1982-01-01

    Additives which can increase the yield in the radiation grafting of monomers to polymers are useful. The use of polyfunctional monomers as additives (approx. = 1% v/v) are shown to enhance significantly the copolymerization yields of styrene in methanol to films of polyethylene and polypropylene under certain radiation conditions. The results obtained when the polyolefins are replaced by PVC as backbone polymer in these accelerated grafting reactions are reported. Divinylbenzene (DVB) and trimethylolpropane triacrylate (TMPTA) were used as representative polyfunctional monomers for the enhancement effect. When polypropylene was used as backbone polymer, the inclusion of DVB significantly enhanced the radiation grafting of styrene in methanol at all monomer concentrations studied above 35%. At certain monomer concentrations (50% , 60%), the yield of graft copolymer was almost doubled by the addition of DVB. 3 tables. (DP)

  19. Non-isothermal kinetic studies on co-processing of olive residue and polypropylene

    International Nuclear Information System (INIS)

    Aboulkas, A.; El Harfi, K.; El Bouadili, A.

    2008-01-01

    Co-processing of olive residue with polypropylene was performed in a thermogravimetric analyzer (TGA) reaction system in a nitrogen atmosphere with a view to comparing the process of the mixture with those of the individual components. Experiments were conducted at different heating rates of 2, 10, 20 and 50 K min -1 in the temperature range of 300-975 K based on the results obtained, three thermal stages were identified during the thermal degradation. The first two were dominated by olive residue pyrolysis, while the third was linked to polypropylene pyrolysis, which occurred at much higher temperatures. Discrepancies between the experimental and calculated TG/DTG profiles were considered as a measurement of the extent of interactions occurring on co-pyrolysis. The maximum degradation temperature of each component in the mixture was higher than those of the individual components alone; thus, an increase in thermal stability was expected. The kinetic processing of thermogravimetric data was conducted using the Friedman method

  20. Mechanical Properties of Isotactic Polypropylene Modified with Thermoplastic Potato Starch

    Science.gov (United States)

    Knitter, M.; Dobrzyńska-Mizera, M.

    2015-05-01

    In this paper selected mechanical properties of isotactic polypropylene (iPP) modified with potato starch have been presented. Thermoplastic starch (TPS) used as a modifier in the study was produced from potato starch modified with glycerol. Isotactic polypropylene/thermoplastic potato starch composites (iPP/TPS) that contained 10, 30, 50 wt.% of modified starch were examined using dynamic mechanical-thermal analysis, static tensile, Brinell hardness, and Charpy impact test. The studies indicated a distinct influence of a filler content on the mechanical properties of composites in comparison with non-modified polypropylene.

  1. Determination of Partition Coefficients of Selected Model Migrants between Polyethylene and Polypropylene and Nanocomposite Polypropylene

    Directory of Open Access Journals (Sweden)

    Pablo Otero-Pazos

    2016-01-01

    Full Text Available Studies on nanoparticles have focused the attention of the researchers because they can produce nanocomposites that exhibit unexpected hybrid properties. Polymeric materials are commonly used in food packaging, but from the standpoint of food safety, one of the main concerns on the use of these materials is the potential migration of low molecular substances from the packaging into the food. The key parameters of this phenomenon are the diffusion and partition coefficients. Studies on migration from food packaging with nanomaterials are very scarce. This study is focused on the determination of partition coefficients of different model migrants between the low-density polyethylene (LDPE and polypropylene (PP and between LDPE and nanocomposite polypropylene (naPP. The results show that the incorporation of nanoparticles in polypropylene increases the mass transport of model migrants from LDPE to naPP. This quantity of migrants absorbed into PP and naPP depends partially on the nature of the polymer and slightly on the chemical features of the migrant. Relation (RPP/naPP between partition coefficient KLDPE/PP and partition coefficient KLDPE/naPP at 60°C and 80°C shows that only BHT at 60°C has a RPP/naPP less than 1. On the other hand, bisphenol A has the highest RPP/naPP with approximately 50 times more.

  2. Sorption of heavy metals on a chitosan-grafted-polypropylene nonwoven geotextile

    Directory of Open Access Journals (Sweden)

    Vandenbossche M.

    2013-04-01

    Full Text Available This work describes the development of an environmental friendly functionalized polypropylene nonwoven geotextile (PP in order to trap heavy metals in sediments and sludges. Chitosan was chosen as the sorbent because of its ability to trap heavy metals, of its natural origin (from shells, and of its low cost. PP was first functionalized with acrylic acid using a cold plasma process, in order to bring some reactive carboxylic functions onto the surface. Chitosan was then covalently grafted on the acrylic acid modified polypropylene. The functionalized surfaces were characterized by FTIR (Fourier Transform InfraRed and chitosan was thus proven to be grafted. The ability of the functionalized textile to trap heavy metals was then investigated. Copper was chosen as the model heavy metal, and artificial solutions of CuSO4 were prepared for the experiments. Sorption studies among the concentration of copper in polluted solutions at 20°C were carried out with PP-g-AA-chitosan (Polypropylene-grafted-Acrylic acid-chitosan in order to evaluate the maximum of absorption of this surface: the textile can chelate copper increasingly with the initial copper concentration until 800 ppm where it reaches a plateau at about 30 mg/L. The effects of pH and of the ionic strength (absorption in a NaCl containing solution were finally investigated. The trapping of Cu2+ decreases slowly when the ionic strength increases. For a seawater-like NaCl concentration of 30g/L, the textile still chelates about 20 mg/L of Cu2+. Finally, the optimum pH to trap the maximum amount of copper was determined to be 4.75, which corresponds to the optimum pH for the solubility of the chitosan.

  3. A Combined Self-Consistent Method to Estimate the Effective Properties of Polypropylene/Calcium Carbonate Composites

    Directory of Open Access Journals (Sweden)

    Zhongqiang Xiong

    2018-01-01

    Full Text Available In this work, trying to avoid difficulty of application due to the irregular filler shapes in experiments, self-consistent and differential self-consistent methods were combined to obtain a decoupled equation. The combined method suggests a tenor γ independent of filler-contents being an important connection between high and low filler-contents. On one hand, the constant parameter can be calculated by Eshelby’s inclusion theory or the Mori–Tanaka method to predict effective properties of composites coinciding with its hypothesis. On the other hand, the parameter can be calculated with several experimental results to estimate the effective properties of prepared composites of other different contents. In addition, an evaluation index σ f ′ of the interactional strength between matrix and fillers is proposed based on experiments. In experiments, a hyper-dispersant was synthesized to prepare polypropylene/calcium carbonate (PP/CaCO3 composites up to 70 wt % of filler-content with dispersion, whose dosage was only 5 wt % of the CaCO3 contents. Based on several verifications, it is hoped that the combined self-consistent method is valid for other two-phase composites in experiments with the same application progress as in this work.

  4. Decontamination of polypropylene fabrics by dry cleaning

    International Nuclear Information System (INIS)

    Severa, J.; Knajfl, J.

    1983-01-01

    Polypropylene fabrics can efficiently be decontaminated by dry cleaning in benzine or perchloroethylene, this also in case the fabric was greased in addition to radioactive contamination. For heavily soiled fabric, it is advantageous to first dry clean it and then wash it. The positive effect was confirmed of intensifiers on the cleaning process, especially of benzine soap. In practice, its concentration should be selected within 1 and 10 g.dm - 3 . Decontamination by dry cleaning and subsequent washing is advantageous in that that the resulting activity of waste water from the laundry is low. Radioactive wastes from the dry cleaning process have a low weight and can be handled as solid waste. (M.D.)

  5. Flexural creep behaviour of jute polypropylene composites

    Science.gov (United States)

    Chandekar, Harichandra; Chaudhari, Vikas

    2016-09-01

    Present study is about the flexural creep behaviour of jute fabric reinforced polypropylene (Jute-PP) composites. The PP sheet and alkali treated jute fabric is stacked alternately and hot pressed in compression molding machine to get Jute-PP composite laminate. The flexural creep study is carried out on dynamic mechanical analyzer. The creep behaviour of the composite is modeled using four-parameter Burgers model. Short-term accelerated creep testing is conducted which is later used to predict long term creep behaviour. The feasibility of the construction of a master curve using the time-temperature superposition (TTS) principle to predict long term creep behavior of unreinforced PP and Jute-PP composite is investigated.

  6. Mechanical and rheological response of polypropylene/boehmite nanocomposites

    CSIR Research Space (South Africa)

    Pedrazzoli, D

    2014-01-01

    Full Text Available In this work the influence of synthetic boehmite alumina (BA) nanoparticles with various surface treatments on the morphology, crystallization behavior and mechanical properties of polypropylene copolymer (PP) nanocomposites was studied...

  7. The effects of normal paraffins mobilizers on irradiated polypropylene

    International Nuclear Information System (INIS)

    Chen Wenxiu; Gao Ling

    1995-01-01

    The n-paraffins blended with polypropylene (PP) as mobilizer had been investigated. The effectiveness of mobilizer (n-paraffins) on irradiated polypropylene is dependent on the molecular weight of mobilizer and its content on polypropylene. The n-docosame (n-C 22 ) possesses the best effectiveness of radiation tolerance on PP among the mobilizer paraffins: n-decane (n-C 10 ), n-hexadecane (n-C 16 ), n-docosane (n-C 22 ) and n-hexatriacontane (n-C 36 ). The 2% (w/w) content of a given mobilizer is the most effective at reducing the embrittlement of irradiated PP as evidenced by the elongation at break. The physical properties of polypropylene with mobilizers such as density, Young's modulus, the Fraction of free volume and the weight swelling ratio in p-xylene at room temperature were measured. Above phenomena are related with the constructive of blended PP and demonstrated by its physical properties

  8. Graft copolimerization of hydrophilic monomers onto irradiated polypropylene fibers

    International Nuclear Information System (INIS)

    Sundardi, F.

    1978-01-01

    A method of graft copolymerization of hydrophilic monomers, such as 1-vinyl-2-pyrrolidone, acrylonitrile, acrylic acid, and acrylamide, onto irradiated polypropylene fibers has been studied. γ ray as well as electron beam were employed for the irradiation processes. Graft-copolymerization kinetics and the properties of grafted fibers have been investigated. Moisture regain, dyes absorption, and melting point of the grafted fibers were found to increase with the increasing of the degree of grafting. Polypropylene for 1-vinyl-2-pyrrolidone grafted fibers showed excellent dye absorption for almost all kinds of dyes such as direct, basic, acid, reactive, disper, and naphthol dyes. However, for polypropylene acrylic acid grafted fibers, the colorfastness to washing was found to be unsatisfactory. The colorfastness to washing for polypropylene 1-vinyl-2-pyrrolidone grafted fibers was found to be fairly good for certain types of dyes such as vat and naphthol dyes. (author)

  9. Effect of ultraviolet radiation (300-400 nanometers) on polypropylene

    International Nuclear Information System (INIS)

    Lerman, S.

    1983-01-01

    Polypropylene discs and shavings were exposed to simulated ambient ultraviolet (UV) radiation (lambda 300-400 nm) for a period equivalent to at least two years of wear within the eye, assuming the eye to be exposed to ambient UV radiation for four hours per day at 1 mW/cm2. The polypropylene and the incubation media were measured by several forms of optical spectroscopy, and there was no photochemical change in either. Where polypropylene discs were exposed to a very high level of UV radiation (greater than 500 W/cm2), they became brittle and discolored within five to ten days. This level of exposure, however, was equivalent to a total of over 20 million joules/cm2, which is at least one million times levels for expected ambient UV exposure to polypropylene within the eye

  10. Influence of Interleaved Films on the Mechanical Properties of Carbon Fiber Fabric/Polypropylene Thermoplastic Composites

    Directory of Open Access Journals (Sweden)

    Jong Won Kim

    2016-05-01

    Full Text Available A laminated composite was produced using a thermoplastic prepreg by inserting an interleaved film with the same type of matrix as the prepreg during the lay-up process to improve the low interlaminar properties, which is a known weakness of laminated composites. Carbon fiber fabric (CFF and polypropylene (PP were used to manufacture the thermoplastic prepregs. Eight prepregs were used to produce the laminated composites. Interleaved films with different thicknesses were inserted into each prepreg. The physical properties of the composite, such as thickness, density, fiber volume fraction (Vf, and void content (Vc, were examined. The tensile strength, flexural strength, interlaminar shear strength (ILSS, impact property, and scanning electron microscopy (SEM were used to characterize the mechanical properties. Compared to the composite without any inserted interleaved film, as the thickness of the inserted interleaved resin film was increased, Vc decreased by 51.45%. At the same time, however, the tensile strength decreased by 8.75%. Flexural strength increased by 3.79% and flexural modulus decreased by 15.02%. Interlaminar shear strength increased by 11.05% and impact strength increased by 15.38%. Fracture toughness of the laminated composite was improved due to insertion of interleaved film.

  11. Influence of Interleaved Films on the Mechanical Properties of Carbon Fiber Fabric/Polypropylene Thermoplastic Composites.

    Science.gov (United States)

    Kim, Jong Won; Lee, Joon Seok

    2016-05-06

    A laminated composite was produced using a thermoplastic prepreg by inserting an interleaved film with the same type of matrix as the prepreg during the lay-up process to improve the low interlaminar properties, which is a known weakness of laminated composites. Carbon fiber fabric (CFF) and polypropylene (PP) were used to manufacture the thermoplastic prepregs. Eight prepregs were used to produce the laminated composites. Interleaved films with different thicknesses were inserted into each prepreg. The physical properties of the composite, such as thickness, density, fiber volume fraction ( V f ), and void content ( V c ), were examined. The tensile strength, flexural strength, interlaminar shear strength (ILSS), impact property, and scanning electron microscopy (SEM) were used to characterize the mechanical properties. Compared to the composite without any inserted interleaved film, as the thickness of the inserted interleaved resin film was increased, V c decreased by 51.45%. At the same time, however, the tensile strength decreased by 8.75%. Flexural strength increased by 3.79% and flexural modulus decreased by 15.02%. Interlaminar shear strength increased by 11.05% and impact strength increased by 15.38%. Fracture toughness of the laminated composite was improved due to insertion of interleaved film.

  12. A novel technique for distal fingertip replantation: Polypropylene suture guided interpositional vein graft.

    Science.gov (United States)

    Dadaci, Mehmet; Ince, Bilsev; Altuntas, Zeynep; Bitik, Ozan; Uzun, Hakan; Bilgen, Fatma

    2015-05-04

    Despite current advances in microsurgery, fingertip replantation is still controversial, mainly due to its difficulty and cost. The purpose of this study is to describe a new technique of interposition vein graft guided by polypropylene suture in distal fingertip replantation. A total of eight consecutive Tamai zone 1 fingertip replantations performed by the same author were included. All replantations were performed using interposition vein graft guided by polypropylene suture. This technique involved a vein graft of ∼ 2 cm, with appropriate calibration, obtained from the volar part of the forearm and a 2-0 polyprolene suture passed through the interposition vein graft. Then, a polypropylene suture guide carrying the vein graft was inserted into the artery. The anastomosis was easily performed with the aid of 10-0 or 11-0 nylon in a bloodless medium and without encountering the posterior wall problem. Average surgery time was 2.5 hours (range = 2-3 hours). Among eight Tamai zone 1 replantations, six were successful (75%). There were two replantations lost because of arterial failure. This technique may ease fingertip replantations and increase the success rate for Tamai zone 1 injuries.

  13. Radiation oxidation of polypropylene: A solid-state 13C NMR study using selective isotopic labeling

    International Nuclear Information System (INIS)

    Mowery, Daniel M.; Assink, Roger A.; Derzon, Dora K.; Klamo, Sara B.; Bernstein, Robert; Clough, Roger L.

    2007-01-01

    Polypropylene samples, in which the three different carbon atoms along the chain were selectively labeled with carbon-13, were subjected to radiation under inert and air atmospheres, and to post-irradiation exposure in air at various temperatures. By using solid-state 13 C NMR measurements at room temperature, we have been able to identify and quantify the oxidation products. The isotopic labeling provides insight into chemical reaction mechanisms, since oxidation products can be traced back to their positions of origin on the macromolecule. The major products include peroxides and alcohols, both formed at tertiary carbon sites along the chain. Other products include methyl ketones, acids, esters, peresters, and hemiketals formed from reaction at the tertiary carbon, together with in-chain ketones and esters from reaction at the secondary chain carbon. No evidence is found of products arising from reactions at the methyl side chain. Significant temperature-dependent differences are apparent; for example much higher yields of chain-end methyl ketones, which are the indicator product of chain scission, are generated for both elevated temperature irradiation and for post-irradiation treatment at elevated temperatures. Time-dependent plots of yields of the various oxidation products have been obtained under a wide range of conditions, including the post-irradiation oxidation of a sample at room temperature in air that has been monitored for 2 years. Radiation-oxidation products of polypropylene are contrasted to products measured for 13 C-labeled polyethylene in an earlier investigation: the peroxides formed in irradiated polypropylene are remarkably longer lived, the non-peroxidic products are significantly different, and the overall ratios of oxidation products in polypropylene change relatively little as a function of the extent of oxidation

  14. Mechanical, Thermal Degradation, and Flammability Studies on Surface Modified Sisal Fiber Reinforced Recycled Polypropylene Composites

    Directory of Open Access Journals (Sweden)

    Arun Kumar Gupta

    2012-01-01

    Full Text Available The effect of surface treated sisal fiber on the mechanical, thermal, flammability, and morphological properties of sisal fiber (SF reinforced recycled polypropylene (RPP composites was investigated. The surface of sisal fiber was modified with different chemical reagent such as silane, glycidyl methacrylate (GMA, and O-hydroxybenzene diazonium chloride (OBDC to improve the compatibility with the matrix polymer. The experimental results revealed an improvement in the tensile strength to 11%, 20%, and 31.36% and impact strength to 78.72%, 77%, and 81% for silane, GMA, and OBDC treated sisal fiber reinforced recycled Polypropylene (RPP/SF composites, respectively, as compared to RPP. The thermogravimetric analysis (TGA, differential scanning calorimeter (DSC, and heat deflection temperature (HDT results revealed improved thermal stability as compared with RPP. The flammability behaviour of silane, GMA, and OBDC treated SF/RPP composites was studied by the horizontal burning rate by UL-94. The morphological analysis through scanning electron micrograph (SEM supports improves surface interaction between fiber surface and polymer matrix.

  15. Novel polypropylene biocomposites reinforced with carbon nanotubes and hydroxyapatite nanorods for bone replacements

    Energy Technology Data Exchange (ETDEWEB)

    Liao, Cheng Zhu; Li, Kai [Department of Physics and Materials Science, City University of Hong Kong, Tat Chee Avenue, Kowloon (Hong Kong); Wong, Hoi Man; Tong, Wing Yin; Yeung, Kelvin Wai Kwok [Department of Orthopedics and Traumatology, The University of Hong Kong (Hong Kong); Tjong, Sie Chin, E-mail: aptjong@cityu.edu.hk [Department of Physics and Materials Science, City University of Hong Kong, Tat Chee Avenue, Kowloon (Hong Kong)

    2013-04-01

    Multi-walled carbon nanotubes (MWNTs) of 0.1 and 0.3 wt.% and hydoxyapatite nanorods (nHAs) of 8–20 wt.% were incorporated into polypropylene (PP) to form biocomposites using melt-compounding and injection molding techniques. The structural, mechanical, thermal and in vitro cell responses of the PP/MWNT–nHA hybrids were investigated. Tensile and impact tests demonstrated that the MWNT additions are beneficial in enhancing the stiffness, tensile strength and impact toughness of the PP/nHA nanocomposites. According to thermal analysis, the nHA and MWNT fillers were found to be very effective to improve dimensional and thermal stability of PP. The results of osteoblast cell cultivation and dimethyl thiazolyl diphenyl tetrazolium (MTT) tests showed that the PP/MWNT–nHA nanocomposites are biocompatible. Such novel PP/MWNT–nHA hybrids are considered to be potential biomaterials for making orthopedic bone implants. - Highlights: ► Multiwalled carbon nanotubes (MWNTs) and hydroxyapatite nanorods (nHA) are used as hybrid fillers to reinforce polypropylene. ► MWNT additions are beneficial in enhancing tensile strength and stiffness of PP/nHA composites. ► Hybridizing MWNT with nHA fillers enhance thermal and dimensional stability of PP significantly. ► Hybridizing MWNT with nHA greatly enhance osteoblast adhesion and proliferation. ► PP/MWNT–nHA composites show attractive applications as load-bearing materials in orthopedics.

  16. Bio-composites fabricated by sandwiching sisal fibers with polypropylene (PP)

    International Nuclear Information System (INIS)

    Sosiati, H.; Nahyudin, A.; Fauzi, I.; Wijayanti, D. A.; Triyana, K.

    2016-01-01

    Sisal fibers reinforced polypropylene (PP) composites were successfully fabricated using sandwiching sisal fibers with PP sheets. The ratio of fiber and polymer matrix was 50:50 (wt. %). Untreated short and long sisal fibers, and alkali treated short sisal fibers in 6% NaOH at 100°C for 1 and 3 h were used as reinforcement or fillers. A small amount (3 wt. %) of maleic anhydride grafted polypropylene (MAPP) was added as a coupling agent. Scanning electron microscopy (SEM) and Fourier transform infrared (FTIR) spectroscopy were used to characterize the surface morphology and chemical composition of the fibers, respectively. Flexural test of sisal/PP composites was done according to ASTM D 790-02. The results showed that flexural strength of untreated long fiber reinforced composite is much higher than that of the untreated and alkali treated short fibers reinforced composites with and without the addition of MAPP. Alkalization related to fiber surface modification, fiber length/fiber orientation and a composite fabrication technique are important factors in contributing to the fiber distribution within the matrix, the bonding between the fiber and the matrix and the enhancement of flexural strength of the bio-composite.

  17. Bio-composites fabricated by sandwiching sisal fibers with polypropylene (PP)

    Science.gov (United States)

    Sosiati, H.; Nahyudin, A.; Fauzi, I.; Wijayanti, D. A.; Triyana, K.

    2016-04-01

    Sisal fibers reinforced polypropylene (PP) composites were successfully fabricated using sandwiching sisal fibers with PP sheets. The ratio of fiber and polymer matrix was 50:50 (wt. %). Untreated short and long sisal fibers, and alkali treated short sisal fibers in 6% NaOH at 100°C for 1 and 3 h were used as reinforcement or fillers. A small amount (3 wt. %) of maleic anhydride grafted polypropylene (MAPP) was added as a coupling agent. Scanning electron microscopy (SEM) and Fourier transform infrared (FTIR) spectroscopy were used to characterize the surface morphology and chemical composition of the fibers, respectively. Flexural test of sisal/PP composites was done according to ASTM D 790-02. The results showed that flexural strength of untreated long fiber reinforced composite is much higher than that of the untreated and alkali treated short fibers reinforced composites with and without the addition of MAPP. Alkalization related to fiber surface modification, fiber length/fiber orientation and a composite fabrication technique are important factors in contributing to the fiber distribution within the matrix, the bonding between the fiber and the matrix and the enhancement of flexural strength of the bio-composite.

  18. Bio-composites fabricated by sandwiching sisal fibers with polypropylene (PP)

    Energy Technology Data Exchange (ETDEWEB)

    Sosiati, H., E-mail: hsosiati@gmail.com [Nanomaterials Research Group, LPPT Universitas Gadjah Mada (Indonesia); Nahyudin, A., E-mail: ahmadnahyudin@yahoo.co.id; Fauzi, I., E-mail: ikhsannurfauzi@gmail.com; Wijayanti, D. A., E-mail: wijayantidwiastuti@gmail.com [Department of Physics, Faculty of Mathematics and Natural Sciences, Gadjah Mada University (Indonesia); Triyana, K., E-mail: triyana@ugm.ac.id [Nanomaterials Research Group, LPPT Universitas Gadjah Mada (Indonesia); Department of Physics, Faculty of Mathematics and Natural Sciences, Gadjah Mada University (Indonesia)

    2016-04-19

    Sisal fibers reinforced polypropylene (PP) composites were successfully fabricated using sandwiching sisal fibers with PP sheets. The ratio of fiber and polymer matrix was 50:50 (wt. %). Untreated short and long sisal fibers, and alkali treated short sisal fibers in 6% NaOH at 100°C for 1 and 3 h were used as reinforcement or fillers. A small amount (3 wt. %) of maleic anhydride grafted polypropylene (MAPP) was added as a coupling agent. Scanning electron microscopy (SEM) and Fourier transform infrared (FTIR) spectroscopy were used to characterize the surface morphology and chemical composition of the fibers, respectively. Flexural test of sisal/PP composites was done according to ASTM D 790-02. The results showed that flexural strength of untreated long fiber reinforced composite is much higher than that of the untreated and alkali treated short fibers reinforced composites with and without the addition of MAPP. Alkalization related to fiber surface modification, fiber length/fiber orientation and a composite fabrication technique are important factors in contributing to the fiber distribution within the matrix, the bonding between the fiber and the matrix and the enhancement of flexural strength of the bio-composite.

  19. Mechanical properties of unidirectional and randomly oriented kenaf bast fibre composites using polypropylene resin matrix

    International Nuclear Information System (INIS)

    Sharifah Hanisah Syed Abd Aziz; Khairul Zaman Mohd Dahlan

    2004-01-01

    Fibres are known to confer strength and rigidity to the weak and brittle matrix and currently, research in composite materials is being directed at using natural fibers instead of synthetic fibres. In this work long and random kenaf fibers were used in the as-received condition and alkalized with a 0.06M NaOH solution. They were combined with polypropylene thin sheets and hot-pressed to form natural fibre composites. The mechanical properties of the composites were investigated to observe the effect of fibre alignment, fibre treatment, and the method of moulding technique used. A general trend was observed whereby alkalized and long fibre composites give higher flexural modulus and flexural strength compared with random mat and untreated fibres. The long fibre composites also gave a higher work of fracture. However, the correlation between fibre surface treatment and the work of fracture was less clear. The method of moulding used also need to be improved to optimize the performance of the composites manufactured as the overall mechanical test result showed some irregularities. Pre-irradiation on the polypropylene pellets before the composite is manufactured will be considered as one of the mechanism in enhancing the mechanical performance of the composites in future work. (Author)

  20. Application of gas chromatography to the investigations on polypropylene radiolysis

    International Nuclear Information System (INIS)

    Zagorski, Z.P.; Gluszewski, W.

    2006-01-01

    Refinement of the gas chromatography (GC) instrumental approach permitted not only improvement of investigation in basic research, but also development of a new kind of polypropylene blends, more suitable for the production of medical devices and radiation sterilization. It has been shown, that using the GC method not only methane and carbon dioxide can be measured, but also the consumption of oxygen which reacts with free radicals on the polypropylene chain

  1. Radiation resistant modified polypropylene; Polipropylen modyfikowany odporny radiacyjnie

    Energy Technology Data Exchange (ETDEWEB)

    Bojarski, J; Zimek, Z [Institute of Nuclear Chemistry and Technology, Warsaw (Poland)

    1997-10-01

    Radiation technology for production of radiation resistant polypropylene for medical use has been presented. The method consists in radiation induced copolymerization of polypropylene with ethylene and addition of small amount of copolymer of polyethylene and vinyl acetate. The material of proposed composition has a very good mechanical properties and elevated radiation resistivity decided on possibility of radiosterilization of products made of this material and designed for medical use. 3 figs, 3 tabs.

  2. Selective laser vaporization of polypropylene sutures and mesh

    Science.gov (United States)

    Burks, David; Rosenbury, Sarah B.; Kennelly, Michael J.; Fried, Nathaniel M.

    2012-02-01

    Complications from polypropylene mesh after surgery for female stress urinary incontinence (SUI) may require tedious surgical revision and removal of mesh materials with risk of damage to healthy adjacent tissue. This study explores selective laser vaporization of polypropylene suture/mesh materials commonly used in SUI. A compact, 7 Watt, 647-nm, red diode laser was operated with a radiant exposure of 81 J/cm2, pulse duration of 100 ms, and 1.0-mm-diameter laser spot. The 647-nm wavelength was selected because its absorption by water, hemoglobin, and other major tissue chromophores is low, while polypropylene absorption is high. Laser vaporization of ~200-μm-diameter polypropylene suture/mesh strands, in contact with fresh urinary tissue samples, ex vivo, was performed. Non-contact temperature mapping of the suture/mesh samples with a thermal camera was also conducted. Photoselective vaporization of polypropylene suture and mesh using a single laser pulse was achieved with peak temperatures of 180 and 232 °C, respectively. In control (safety) studies, direct laser irradiation of tissue alone resulted in only a 1 °C temperature increase. Selective laser vaporization of polypropylene suture/mesh materials is feasible without significant thermal damage to tissue. This technique may be useful for SUI procedures requiring surgical revision.

  3. Effect of Nano-clay on Rheological and Extrusion Foaming Process of a Block-Copolymerized Polypropylene

    Directory of Open Access Journals (Sweden)

    Wang Mingyi

    2016-01-01

    Full Text Available The effects of nano-clay and the corresponding coupling agent maleic anhydride grafted polypropylene (PP-g-MAH on thermal properties, rheological properties and extrusion foaming process of a block-copolymerized polypropylene (B-PP were studied. Supercritical CO2 (SC CO2 was used as the foaming agent with a concentration of 5wt%. Each step of foamed B-PP/ PP-g-MAH/ nano-clay composites processing is addressed, including mixing of the composites, manufacture of the composites, foaming process of the composites and characterization of the cell structure. The results showed that incorporation of nano-clay and PP-g-MAH caused reduced melt strength and complex viscosity of B-PP. However, the heterogeneous nucleation induced by nano-clay and PP-g-MAH improved the maximum foaming expansion ratio and cell-population density of B-PP foam.

  4. Study on the Properties of Microcapsulated Chlorocyclophosphazene Polypropylene Composites%三聚氯化磷腈微胶囊阻燃剂/聚丙烯复合材料的性能研究

    Institute of Scientific and Technical Information of China (English)

    刘亚青; 赵贵哲

    2007-01-01

    Microcapsulated chlorocyclophosphazenes were synthesized, and then microcapsulated chlorocyclophosphazene/polypropylene(PP) composites were prepared.The results showed that microcapsulated chlorocyclophosphazene had good high thermal stability through thermogravimetric analysis (TGA).The flammability and mechanical properties of microcapsulated chlorocyclophosphazene/polypropylene composites were investigated by limiting oxygen index experiment, UL 94V flame retardancy test, cone calorimetry, tensile experiment, and impact test, respectively.It was shown that the microcapsulated chlorocyclophosphazene/PP composites had better tensile strength, impact strength, flame retardant properties and smoke suppress properties compared with chlorocyclophosphazene/PP composites.

  5. Short Jute Fiber Reinforced Polypropylene Composites: Effect of Nonhalogenated Fire Retardants

    Directory of Open Access Journals (Sweden)

    Sk. Sharfuddin Chestee

    2017-01-01

    Full Text Available Short jute fiber reinforced polypropylene (PP composites were prepared using a single screw extrusion moulding. Jute fiber content in the composites is optimized with the extent of mechanical properties, and composites with 20% jute show higher mechanical properties. Dissimilar concentrations of several fire retardants (FRs, such as magnesium oxide (MO, aluminum oxide (AO, and phosphoric acid (PA, were used in the composites. The addition of MO, AO, and PA improved the fire retardancy properties (ignition time, flame height, and total firing time of the composites. Ignition time for 30% MO, flame height for 30% PA, and total firing time for 20% MO content composites showed good results which were 8 sec, 1 inch, and 268 sec, respectively. Mechanical properties (tensile strength, tensile modulus, bending strength, bending modulus, and elongation at break, degradation properties (soil test, weathering test, and percentage of weight loss, and water uptake were studied.

  6. Influence of Rubber Powders on Foaming Behavior and Mechanical Properties of Foamed Polypropylene Composites

    Directory of Open Access Journals (Sweden)

    HE Yue

    2017-02-01

    Full Text Available Polypropylene/rubber powders composites with different kinds of rubber powders were foamed by injection molding machine equipped with volume-adjustable cavity. The effect of dispersity of rubber powders and crystallization behavior of composites on the foaming behavior and mechanical properties was investigated. The results show that the addition of rubber powders can improve the cell structure of foamed PP with fine and uniform cell distribution. And cell density and size of PP/PP-MAH/NBR foams are 7.64×106cell/cm3 and 29.78μm respectively, which are the best among these foams. Combining cell structures with mechanical properties, notch impact strength of PP/PP-MAH/CNBR composites increases approximately by 2.2 times while tensile strength is reduced just by 26% compared with those of the pure PP. This indicates that PP/PP-MAH/CNBR composites are ideal foamed materials.

  7. THE EFFECT OF HIGH TEMPERATURES ON CONCRETE INCORPORATING ULTRAFINE SILICA AND POLYPROPYLENE FIBERS

    Directory of Open Access Journals (Sweden)

    M. Benkaddour

    2016-05-01

    Full Text Available In recent years, lots of studies have attempted to examine the possible causes for the thermal instability of ordinary concrete and high performance. However, we still do not know the exact terms of phenomena taking place during exposure to high temperature and the technological solutions that exist (polypropylene fibres, thermal reported are not always well controlled.In this work, several concrete formulations have been tested and multi-scale observation of high-temperature behavior of ordinary concrete (compressive strength of 48 MPa and HPC (compressive strength 75 MPa were adopted. On the scale of the material, the identification of trends with temperature data such as porosity and particularly the mechanical properties allow us to better understand the behaviour of concrete at high temperature differential thermal analysis have been also made.

  8. Design and synthesis of structurally well-defined functional polypropylenes via transition metal-mediated olefin polymerization chemistry

    Institute of Scientific and Technical Information of China (English)

    Dong Jinyong

    2006-01-01

    Functionalization of polyolefins is an industrially important yet scientifically challenging research subject.This paper summarizes our recent effort to access structurally well-defined functional polypropylenes via transition metal-mediated olefin polymerization.In one approach,polypropylenes containing side chain functional groups of controlled concentrations were obtained by Ziegler-Natta-catalyzed copolymerization of propylene in combination with either living anionic or controlled radical polymerization of polar monomers.The copolymerization of propylene with 1,4-divinylbenzene using an isospecific MgC12-supported TIC14 catalyst yielded potypropylenes containing pendant styrene moieties.Both metalation reaction with n-butyllithium and hydrochlorination reaction with dry hydrogen chloride selectively and quantitatively occurred at the pendant reactive sites,generating polymeric benzyllithium and 1-chloroethylbenzene species.These species initiated living anionic polymerization of styrene(S)and atom transfer radical polymerization(in the presence of CuC1 and pentamethyldiethylenetriamine) of methyl methacrylate(MMA),respectively,resulting in functional polypropylene graft copolymers(PP-g-PS and PP-g-PMMA)with controllable graft lengths.In another approach,chain end-functionalized polypropylenes containing a terminal OH-group with controlled molecular weights were directly prepared by propylene polymerization with a metaUocene catalyst through a selective aluminum chain transfer reaction.Both approaches proved to be desirable polyolefin functionalization routes in terms of efficiency and polymer structure controllability.

  9. Effect of Polypropylene Fibers on Self-Healing and Dynamic Modulus of Elasticity Recovery of Fiber Reinforced Concrete

    Directory of Open Access Journals (Sweden)

    Adham El-Newihy

    2018-02-01

    Full Text Available This study aims to evaluate self-healing properties and recovered dynamic moduli of engineered polypropylene fiber reinforced concrete using non-destructive resonant frequency testing. Two types of polypropylene fibers (0.3% micro and 0.6% macro and two curing conditions have been investigated: Water curing (at ~25 Celsius and air curing. The Impact Resonance Method (IRM has been conducted in both transverse and longitudinal modes on concrete cylinders prior/post crack induction and post healing of cracks. Specimens were pre-cracked at 14 days, obtaining values of crack width in the range of 0.10–0.50 mm. Addition of polypropylene fibers improved the dynamic response of concrete post-cracking by maintaining a fraction of the original resonant frequency and elastic properties. Macro fibers showed better improvement in crack bridging while micro fiber showed a significant recovery of the elastic properties. The results also indicated that air-cured Polypropylene Fiber Reinforced Concrete (PFRC cylinders produced ~300 Hz lower resonant frequencies when compared to water-cured cylinders. The analyses showed that those specimens with micro fibers exhibited a higher recovery of dynamic elastic moduli.

  10. Mapping physicochemical surface modifications of flame-treated polypropylene

    Directory of Open Access Journals (Sweden)

    S. Farris

    2014-04-01

    Full Text Available The aim of this work was to investigate how the surface morphology of polypropylene (PP is influenced by the surface activation mediated by a flame obtained using a mixture of air and propane under fuel-lean (equivalence ratio φ = 0.98 conditions. Morphological changes observed on flamed samples with smooth (S, medium (M, and high (H degree of surface roughness were attributed to the combined effect of a chemical mechanism (agglomeration and ordering of partially oxidized intermediate-molecular-weight material with a physical mechanism (flattening of the original roughness by the flame’s high temperature. After two treatments, the different behavior of the samples in terms of wettability was totally reset, which made an impressive surface energy of ~43 mJ•m–2 possible, which is typical of more hydrophilic polymers (e.g., polyethylene terephthalate – PET. In particular, the polar component was increased from 1.21, 0.08, and 0.32 mJ•m–2 (untreated samples to 10.95, 11.20, and 11.17 mJ•m–2 for the flamed samples S, M, and H, respectively, an increase attributed to the insertion of polar functional groups (hydroxyl and carbonyl on the C–C backbone, as demonstrated by the X-ray photoelectron spectroscopy results.

  11. Energy harvesting from vibration with cross-linked polypropylene piezoelectrets

    Directory of Open Access Journals (Sweden)

    Xiaoqing Zhang

    2015-07-01

    Full Text Available Piezoelectret films are prepared by modification of the microstructure of polypropylene foam sheets cross-linked by electronic irradiation (IXPP, followed by proper corona charging. Young’s modulus, relative permittivity, and electromechanical coupling coefficient of the fabricated films, determined by dielectric resonance spectra, are about 0.7 MPa, 1.6, and 0.08, respectively. Dynamic piezoelectric d33 coefficients up to 650 pC/N at 200 Hz are achieved. The figure of merit (FOM, d33 ⋅ g33 for a more typical d33 value of 400 pC/N is about 11.2 GPa−1. Vibration-based energy harvesting with one-layer and two-layer stacks of these films is investigated at various frequencies and load resistances. At an optimum load resistance of 9 MΩ and a resonance frequency of 800 Hz, a maximum output power of 120 μW, referred to the acceleration g due to gravity, is obtained for an energy harvester consisting of a one-layer IXPP film with an area of 3.14 cm2 and a seismic mass of 33.7 g. The output power can be further improved by using two-layer stacks of IXPP films in electric series. IXPP energy harvesters could be used to energize low-power electronic devices, such as wireless sensors and LED lights.

  12. Energy harvesting from vibration with cross-linked polypropylene piezoelectrets

    Energy Technology Data Exchange (ETDEWEB)

    Zhang, Xiaoqing [Shanghai Key Laboratory of Special Artificial Microstructure Materials and Technology & School of Physics Science and Engineering, Tongji University, Shanghai 200092 (China); Institute for Telecommunications Technology, Merckstrasse 25, 64283 Darmstadt (Germany); Wu, Liming [Shanghai Key Laboratory of Special Artificial Microstructure Materials and Technology & School of Physics Science and Engineering, Tongji University, Shanghai 200092 (China); Sessler, Gerhard M., E-mail: g.sessler@nt.tu-darmstadt.de [Institute for Telecommunications Technology, Merckstrasse 25, 64283 Darmstadt (Germany)

    2015-07-15

    Piezoelectret films are prepared by modification of the microstructure of polypropylene foam sheets cross-linked by electronic irradiation (IXPP), followed by proper corona charging. Young’s modulus, relative permittivity, and electromechanical coupling coefficient of the fabricated films, determined by dielectric resonance spectra, are about 0.7 MPa, 1.6, and 0.08, respectively. Dynamic piezoelectric d{sub 33} coefficients up to 650 pC/N at 200 Hz are achieved. The figure of merit (FOM, d{sub 33} ⋅ g{sub 33}) for a more typical d{sub 33} value of 400 pC/N is about 11.2 GPa{sup −1}. Vibration-based energy harvesting with one-layer and two-layer stacks of these films is investigated at various frequencies and load resistances. At an optimum load resistance of 9 MΩ and a resonance frequency of 800 Hz, a maximum output power of 120 μW, referred to the acceleration g due to gravity, is obtained for an energy harvester consisting of a one-layer IXPP film with an area of 3.14 cm{sup 2} and a seismic mass of 33.7 g. The output power can be further improved by using two-layer stacks of IXPP films in electric series. IXPP energy harvesters could be used to energize low-power electronic devices, such as wireless sensors and LED lights.

  13. Electromagnetic interference shielding effectiveness of polypropylene/conducting fiber composites

    International Nuclear Information System (INIS)

    Lee, Pyoung-Chan; Kim, Bo-Ram; Jeoung, Sun Kyoung; Kim, Yeung Keun

    2016-01-01

    Electromagnetic released from the automotive electronic parts is harmful to human body. Electromagnetic interference (EMT) shielding refers to the reflection and/or adsorption of electromagnetic radiation by a material, which thereby acts as a shield against the penetration of the radiation through the shield. Polypropylene (PP)/conductive micro fiber composites containing various fiber contents and fiber length were injection-molded. The effect of fiber content and length on electrical properties of the composites was studied by electrical resistivity and EMT shielding measurements. The through-plane electrical conductivity and dielectric permittivity were obtained by measuring dielectric properties. The EMT shielding effectiveness (SE) was investigated by using S-parameter in the range of 100 ~ 1500 MHz. Reflection, absorption and multiple-reflection are the EMT attenuation mechanisms. From the measurement of S-Parameters, the absorption coefficient, reflection coefficient, and the shielding efficiency of the materials were calculated. The EMT SE of PP/conducing fiber composites is 40 dB over a wide frequency range up to 1.5 GHz, which is higher than that of PP/talc composite used automotive parts, viz. 0 dB.

  14. Improved Mechanical Properties of Compatibilized Polypropylene/Polyamide-12 Blends

    Directory of Open Access Journals (Sweden)

    Nora Aranburu

    2015-01-01

    Full Text Available Compatibilized blends of polypropylene (PP and polyamide-12 (PA12 as a second component were obtained by direct injection molding having first added 20% maleic anhydride-modified copolymer (PP-g-MA to the PP, which produced partially grafted PP (gPP. A nucleating effect of the PA12 took place on the cooling crystallization of the gPP, and a second crystallization peak of the gPP appeared in the PA12-rich blends, indicating changes in the crystalline morphology. There was a slight drop in the PA12 crystallinity of the compatible blends, whereas the crystallinity of the gPP increased significantly in the PA12-rich blends. The overall reduction in the dispersed phase particle size together with the clear increase in ductility when gPP was used instead of PP proved that compatibilization occurred. Young’s modulus of the blends showed synergistic behavior. This is proposed to be both due to a change in the crystalline morphology of the blends on the one hand and, on the other, in the PA12-rich blends, to the clear increase in the crystallinity of the gPP phase, which may, in turn, have been responsible for the increase in its continuity and its contribution to the modulus.

  15. Radiation-induced grafting of styrene on polypropylene pellets

    International Nuclear Information System (INIS)

    Souza, Camila P.; Ferreira, Henrique P.; Parra, Duclerc F.; Lugao, Ademar B.

    2009-01-01

    The changes of radiation-induced in polypropylene (PP) pellets exposed to gamma irradiation in inert atmosphere were investigated in correlation with the applied doses (10 and 50 kGy). Also, results from the grafting of styrene onto PP pellets using simultaneous irradiation at the same doses are presented. The grafting reaction was carried out using toluene as solvent, under nitrogen atmosphere and at room temperature. The properties of the irradiated and grafted PP pellets were studied using Melt Flow Index, thermal analysis (TG and DSC), and ATR-IR. The degree of grafting (DOG) for the grafted pellets was gravimetrically determined. The results showed that radiation-induced graft polymerization on pellets were successfully obtained and the influence of dose irradiated did not change the thermal properties in spite of the increase in the MFI and consequently this increase in the viscosity results an decrease the molecular mass. The MFI for grafted pellets was not achievable because the high degree of viscosity of polymer, even arising the test temperature, the polymer was not flow enough. (author)

  16. Some Exploitation Properties of Wood Plastic Hybrid Composites Based on Polypropylene and Plywood Production Waste

    Science.gov (United States)

    Kajaks, Janis; Kalnins, Karlis; Uzulis, Sandris; Matvejs, Juris

    2015-12-01

    During the last 20-30 years many researchers have paid attention to the studies of properties of thewood polymer composites (WPC). A lot of works are closely related to investigations of exploitation properties of wood fibres or wood flour containing polyolefine composites [1, 2]. The most useful from wide selection of polyolefines are polypropylenes, but timber industry waste materials comprising lignocellulose fibres are often used as reinforcement of WPC [3-12]. Plywood industry is not an exception - part of waste materials (by-products) are used for heat energy, i.e. burned. In this work we have approbated reinforcing of polypropylene (PP) with one of the plywood industry by-products, such as birch plywood sawdust (PSWD),which containswood fibre fractions with different length [13]. The main fraction (50%) includes fibres with length l = 0.5 - 1 mm. Our previous study [13] has confirmed that PSWD is a promising filler for PP reinforcing. Addition of PSWD up to 40-50 wt.% has increased WPC tensile and flexural modulus, but decreased deformation ability of PP matrix, impact strength, water resistance and fluidity of composite melts. It was shown [13] that modification of the composites with interfacial modifier - coupling agent maleated polypropylene (MAPP content up to 5-7 wt.%) considerably improved all the abovementioned properties. SEM investigations also confirmed positive action of coupling agent on strengthening of adhesion interaction between components wood and PP matrix. Another way how to make better properties of the WPC is to form hybridcomposites [1, 14-24]. Very popular WPC modifiers are nanoparticle additions like organonanoclays, which increase WPC physical-mechanical properties - microhardness, water resistance and diminish barrier properties and combustibility [1, 2, 14-17, 19, 20]. The goal of this study was to investigate organonanoclays influence on plywood production industry by-product birch plywood sawdust (PSWD) containing

  17. Magnetic fluids stabilized by polypropylene glycol

    Energy Technology Data Exchange (ETDEWEB)

    Lebedev, A.V., E-mail: lav@icmm.r [Institute of Continuous Media Mechanics, UB RAS, Academic Korolev Str. 1, Perm 614013 (Russian Federation); Lysenko, S.N. [Institute of Technical Chemistry, UB RAS, Academic Korolev Str. 3, Perm 614013 (Russian Federation)

    2011-05-15

    A series of samples of magnetic fluids stabilized with low-molecular weight polypropylene glycol (PPG) of different molecular masses were synthesized. The use of PPG allowed the maximum extension of the carrier fluid range to include ethyl- and butyl-acetate, ethanol, butanol, acetone, carbon tetrachloride, toluene, kerosene and PPG itself. Magnetic and rheological properties of the samples were investigated. Based on the results of investigation it has been concluded that magnetic nanoparticles are covered by a monolayer of surfactant molecules. At low temperatures the propanol-based sample preserves fluidity up to -115 {sup o}C. Measurement of critical temperatures of other base fluids showed that alcohols are the best carrier medium. Coagulation stability of the ethanol-based ferrocolloid with respect to water and kerosene was explored. It has been found that kerosene, whose fraction by weight exceeds 22.5%, does not mix with the colloid. This effect can be used to produce magneto-controllable extractors of ethyl alcohol. Under the action of water the colloid coagulates, which allows one to substitute the carrier fluid and to separate the colloid into fractions. - Research highlights: PPG stabilizes the magnetic particles in the polar and non-polar media. The minimum operating temperature reaches -115 {sup o}C. Alcohols are the best environment for PPG-stabilized particles. PPG magnetic fluids can be used as magnetic extractors of alcohol. PPG MF can be divided into fractions by partial coagulation with water.

  18. OLED-polypropylene bio-CD sensor

    Science.gov (United States)

    Vengasandra, Srikanth; Cai, Yuankun; Grewell, David; Shinar, Joseph; Shinar, Ruth

    2008-08-01

    With the goal of developing microfluidic platforms for sensing applications, flash-free micro patterns were embossed in polypropylene surfaces with ultrasonic heating for a biosensing lab-on-CD application. The embossed features were designed to act as reservoirs, valves, and reaction chambers to allow, in combination with a compact sensing platform, the monitoring of analyte levels using a standard PC-CD player. To generate the compact sensor, as an example, we chose the photoluminescence (PL)-based detection of lactate and glucose using an OLED-based sensing platform. Once embossed, the surface energy of the plastic substrate was chemically modified to make it hydrophilic. Reagents, placed in separate reservoirs, were directed through burst valves towards a reaction chamber via CD rotation. Lactate or glucose were monitored by measuring the effect of the related dissolved oxygen level on the PL decay time of an oxygen-sensitive dye, following analyte oxidation catalyzed by a suitable specific oxidase enzyme. The results demonstrate the potential of integrating OLEDs as excitation sources in PL-based sensors with microfluidic CD-based platforms, including for simultaneous multiple analyses.

  19. Needleless Melt-Electrospinning of Polypropylene Nanofibres

    Directory of Open Access Journals (Sweden)

    Jian Fang

    2012-01-01

    Full Text Available Polypropylene (PP nanofibres have been electrospun from molten PP using a needleless melt-electrospinning setup containing a rotary metal disc spinneret. The influence of the disc spinneret (e.g., disc material and diameter, operating parameters (e.g., applied voltage, spinning distance, and a cationic surfactant on the fibre formation and average fibre diameter were examined. It was shown that the metal material used for making the disc spinneret had a significant effect on the fibre formation. Although the applied voltage had little effect on the fibre diameter, the spinning distance affected the fibre diameter considerably, with shorter spinning distance resulting in finer fibres. When a small amount of cationic surfactant (dodecyl trimethyl ammonium bromide was added to the PP melt for melt-electrospinning, the fibre diameter was reduced considerably. The finest fibres produced from this system were 400±290 nm. This novel melt-electrospinning setup may provide a continuous and efficient method to produce PP nanofibres.

  20. Storing of Extracts in Polypropylene Microcentrifuge Tubes Yields Contaminant Peak During Ultra-flow Liquid Chromatographic Analysis.

    Science.gov (United States)

    Kshirsagar, Parthraj R; Hegde, Harsha; Pai, Sandeep R

    2016-05-01

    This study was designed to understand the effect of storage in polypropylene microcentrifuge tubes and glass vials during ultra-flow liquid chromatographic (UFLC) analysis. One ml of methanol was placed in polypropylene microcentrifuge tubes (PP material, Autoclavable) and glass vials (Borosilicate) separately for 1, 2, 4, 8, 10, 20, 40, and 80 days intervals stored at -4°C. Contaminant peak was detected in methanol stored in polypropylene microcentrifuge tubes using UFLC analysis. The contaminant peak detected was prominent, sharp detectable at 9.176 ± 0.138 min on a Waters 250-4.6 mm, 4 μ, Nova-Pak C18 column with mobile phase consisting of methanol:water (70:30). It was evident from the study that long-term storage of biological samples prepared using methanol in polypropylene microcentrifuge tubes produce contaminant peak. Further, this may mislead in future reporting an unnatural compound by researchers. Long-term storage of biological samples prepared using methanol in polypropylene microcentrifuge tubes produce contaminant peakContamination peak with higher area under the curve (609993) was obtained in ultra-flow liquid chromatographic run for methanol stored in PP microcentrifuge tubesContamination peak was detected at retention time 9.113 min with a lambda max of 220.38 nm and 300 mAU intensity on the given chromatographic conditionsGlass vials serve better option over PP microcentrifuge tubes for storing biological samples. Abbreviations used: UFLC: Ultra Flow Liquid Chromatography; LC: Liquid Chromatography; MS: Mass spectrometry; AUC: Area Under Curve.

  1. Strength Characteristics of Fiber Reinforced Quarry Dust Stabilized Fly Ash

    OpenAIRE

    Akshaya Kumar Sabat; Bidula Bose

    2015-01-01

    Effects of quarry dust and polypropylene fiber on compaction properties, shear strength parameters, and California bearing ratio (CBR) of a fly ash have been discussed in this paper. Quarry dust was added to a fly ash from 0 to 60% at an increment of 10%, compaction and soaked CBR tests were conducted on fly ash-quarry dust mixes and the optimum percentage of quarry dust was found out to be 40%. Polypropylene fiber was added to fly ash stabilized with optimum percentage of quarry dust, from 0...

  2. Co-60 gamma radiation assisted diffusion of iodine in polypropylene

    Energy Technology Data Exchange (ETDEWEB)

    Mathakari, N.L.; Bhoraskar, V.N. [Microtron Accelerator Laboratory, Department of Physics, University of Pune, Pune, Maharashtra 411007 (India); Dhole, S.D., E-mail: sanjay@physics.unipune.ernet.i [Microtron Accelerator Laboratory, Department of Physics, University of Pune, Pune, Maharashtra 411007 (India)

    2010-09-15

    Thin films of polypropylene having dimensions 50 mm x 15 mm x 350 {mu}m were immersed in 1 N iodine solution and then irradiated with Co-60 gamma radiation for the periods of 48, 96 and 144 h at the doses varying from 14.4 to 43.2 kGy. The films were also kept immersed in iodine solution for similar periods but without irradiation. Furthermore, the films were also directly-irradiated with Co-60 gamma radiation for similar periods and doses. The radiation-iodinated, plain-iodinated and directly-irradiated samples were characterized by using various techniques such as weight gain EDS, SEM, FTIR, UV-visible spectroscopy, contact angle and XRD. Weight gain, EDS and SEM collectively reveal that gamma irradiation enhances iodine intake in polypropylene. FTIR, EDS and contact angle measurements indicate that presence of iodine during irradiation resists radiation induced carbonylation of polypropylene. FTIR also shows presence of HOI (Hypoiodous acid) species instead of expected C-I bonds. UV-visible analysis unambiguously shows that presence of iodine enhances radiation induced band gap reduction process of polypropylene. XRD indicates that iodine decreases the crystallinity of polypropylene.

  3. The Effect of Size and Crumb Rubber Composition as a Filler with Compatibilizer Pp-G-Ma in Polypropylene Blends and Sir-20 Compound on Mechanical and Thermal Properties

    Directory of Open Access Journals (Sweden)

    Erna Frida

    2013-04-01

    Full Text Available Having been researched the development of thermoplastic elastomer material of polypropylene and natural rubber SIR-20 compound with Crumb Rubber as the filler. Reinforced polypropylene with size 60 mesh with 1 mm, and the composition of the Crumb rubber (30, 40, and 50 wt%. Observed mechanical properties are tensile strength, fracture elongation, Young's modulus, tear strength and impact strength. Thermal properties are analyzed by DSC and DTA/TGA. It is acquired that for the size of 60 mesh crumb rubber tensile strength, fracture elongation, Young’s modulus, tear strength and impact strength are bigger than 1mm size. The addition of 60 mesh crumb rubber increases but it decreases by adding of 50 weight%. While for crumb rubber 1 mm tensile strength, fracture elongation, tear strength and impact strength decreas. Based on analysis of DSC that the addition of crumb rubber does not make a difference boiling point significantly between samples containing crumb rubber and polypropylene Analysis TGA/DTA to an increase in enthalpy and decomposition temperature with the addition of crumb rubber used and thermal stability.

  4. Effect of material and processing parameters on mechanical properties of Polypropylene/Ethylene-Propylene-Diene-Monomer/clay nanocomposites

    International Nuclear Information System (INIS)

    Hejazi, Iman; Sharif, Farhad; Garmabi, Hamid

    2011-01-01

    Highlights: → Improved mechanical properties over a broad range of processing conditions. → Moderate levels of clay and processing parameters lead to higher toughness of TPO. → Significant improvement of tensile strength and modulus of TPO materials. -- Abstract: Polypropylene/Ethylene-Propylene-Diene-Monomer (PP/EPDM) blends are well known for having a combination of favourable mechanical properties. In this paper, addition of organoclay to PP/EPDM to make PP/EPDM nanocomposites with enhanced mechanical properties is studied. PP/EPDM/organoclay nanocomposites were prepared using a lab scale twin-screw extruder. Maleic anhydride grafted polypropylene (PP-g-MA) was used to enhance the intercalation/exfoliation process and to create good adhesion at the polymer/polymer and polymer/filler interfaces. Taguchi method was employed to deign the experiments and optimize material and processing parameters for optimized mechanical properties. Organoclay (NC) and compatibilizer content were selected as material parameters and the main processing variables were feeding rate and average shear rate (RPM). X-ray diffraction (XRD), Transmission Electron Microscopy (TEM) and Scanning Electron Microscopy (SEM) were used to study the microstructure of the nanocomposites samples. It was observed that NC content and shear rate in extruder improved the tensile strength and modulus. Another important result was the insignificant effect of NC content on impact strength while increasing shear rate first increased and then decreased the impact strength.

  5. Plasma modification of polypropylene surfaces and its alloying with styrene in situ

    Energy Technology Data Exchange (ETDEWEB)

    Ma Guiqiu, E-mail: magq@tju.edu.cn [School of Materials Science and Engineering, Tianjin Key Laboratory of Composite and Functional Materials, Tianjin University, Tianjin, 300072 (China); Liu Ben; Li Chen; Huang Dinghai; Sheng Jing [School of Materials Science and Engineering, Tianjin Key Laboratory of Composite and Functional Materials, Tianjin University, Tianjin, 300072 (China)

    2012-01-15

    The treatment of polypropylene surfaces has been studied by dielectric barrier discharges plasma of Ar. The structure and morphology of polypropylene surfaces of Ar plasma modification are characterized by X-ray photoelectron spectroscopy, Fourier transform infrared spectrometers and scanning electron microscope. The modified by plasma treatment of iPP (isotactic polypropylene) surface properties have been examined in a determination of free radicals. The modified active surfaces of polypropylene can induce grafting copolymerization of styrene onto polypropylene. The structure of grafting copolymer is characterized and the grafting percent of styrene onto polypropylene is calculated. The homopolymer of styrene can be formed under grafting copolymerization of styrene onto polypropylene, which follows that the alloying of polypropylene with styrene is achieved in situ.

  6. Combined Performance of Polypropylene Fibre and Weld Slag in High Performance Concrete

    Science.gov (United States)

    Ananthi, A.; Karthikeyan, J.

    2017-12-01

    The effect of polypropylene fibre and weld slag on the mechanical properties of High Performance Concrete (HPC) containing silica fume as the mineral admixtures was experimentally verified in this study. Sixteen series of HPC mixtures(70 MPa) were designed with varying fibre fractions and Weld Slag (WS). Fibre added at different proportion (0, 0.1, 0.3 and 0.6%) to the weight of cement. Weld slag was substituted to the fine aggregate (0, 10, 20 and 30%) at volume. The addition of fibre decreases the slump at 5, 9 and 14%, whereas the substitution of weld slag decreases by about 3, 11 and 21% with respect to the control mixture. Mechanical properties like compressive strength, split tensile strength, flexural strength, Ultrasonic Pulse Velocity test (UPV) and bond strength were tested. Durability studies such as Water absorption and Sorptivity test were conducted to check the absorption of water in HPC. Weld slag of 10% and fibre dosage of 0.3% in HPC, attains the maximum strength and hence this combination is most favourable for the structural applications.

  7. Studies on improvement of mechanical properties of Kenaf-reinforced polypropylene composites

    International Nuclear Information System (INIS)

    Sarifah Hanisah Syed Abd Aziz; Khairul Zaman Mohd Dahlan

    2006-01-01

    At present, research in composite materials is being directed at using natural fibres instead of synthetic fibres. Kenaf which is extensively grown in the Far East including Malaysia, has been identified as a bast (stem) fibre with significant market potential. In this work, long and random kenaf fibres were used in the as-received condition and alkalized with a 0.06 M NaOH solution. They were combined with polypropylene thin sheets, sandwiched between layers of kenaf fibres and hot-pressed to form natural fibre composites. The mechanical properties of the composites were investigated to observe the effect of fibre alignment, fibre treatment, the addition of coupling agent and pre-irradiation method used. A general trend was observed whereby alkalized and long fibre composites gave higher flexural modulus and flexural strength compared with random mat and untreated fibres. The long fibre composites also gave a higher work of fracture. However, the correlation between fibre surface treatment and the work of fracture was less clear. The addition of coupling agent at 1% showed a slight improvement on the mechanical performance of the composites whereas pre-irradiation on the polypropylene pellets and fibres before the composite is manufactured showed significant improvement on the mechanical properties. However, the method of moulding used need to be improved to optimize the performance of the composites. (Author)

  8. Physicomechanical evaluation of polypropylene, polyester, and polytetrafluoroethylene meshes for inguinal hernia repair.

    Science.gov (United States)

    Deeken, Corey R; Abdo, Michael S; Frisella, Margaret M; Matthews, Brent D

    2011-01-01

    For meshes to be used effectively for hernia repair, it is imperative that engineers and surgeons standardize the terminology and techniques related to physicomechanical evaluation of these materials. The objectives of this study were to propose standard techniques, perform physicomechanical testing, and classify materials commonly used for inguinal hernia repair. Nine meshes were evaluated: 4 polypropylene, 1 polyester, 1 polytetrafluoroethylene, and 3 partially absorbable. Physical properties were determined through image analysis, laser micrometry, and density measurements. Biomechanical properties were determined through suture retention, tear resistance, uniaxial, and ball burst testing with specimens tested in 2 different orientations. A 1-way ANOVA with Tukey's post-test or a t-test were performed, with p INFINIT (WL Gore & Associates) did not resist tearing as effectively as the others. All meshes exhibited supraphysiologic burst strengths except INFINIT and ULTRAPRO. Significant differences exist between the physicomechanical properties of polypropylene, polyester, polytetrafluoroethylene, and partially absorbable mesh prostheses commonly used for inguinal hernia repair. Orientation of the mesh was also shown to be critical for the success of meshes, particularly those demonstrating anisotropy. Copyright © 2011 American College of Surgeons. Published by Elsevier Inc. All rights reserved.

  9. Super Oxygen and Improved Water Vapor Barrier of Polypropylene Film with Polyelectrolyte Multilayer Nanocoatings.

    Science.gov (United States)

    Song, Yixuan; Tzeng, Ping; Grunlan, Jaime C

    2016-06-01

    Biaxially oriented polypropylene (BOPP) is widely used in packaging. Although its orientation increases mechanical strength and clarity, BOPP suffers from a high oxygen transmission rate (OTR). Multilayer thin films are deposited from water using layer-by-layer (LbL) assembly. Polyethylenimine (PEI) is combined with either poly(acrylic acid) (PAA) or vermiculite (VMT) clay to impart high oxygen barrier. A 30-bilayer PEI/VMT nanocoating (226 nm thick) improves the OTR of 17.8 μm thick BOPP by more than 30X, rivaling most inorganic coatings. PEI/PAA multilayers achieve comparable barrier with only 12 bilayers due to greater thickness, but these films exhibit increased oxygen permeability at high humidity. The PEI/VMT coatings actually exhibit improved oxygen barrier at high humidity (and also improve moisture barrier by more than 40%). This high barrier BOPP meets the criteria for sensitive food and some electronics packaging applications. Additionally, this water-based coating technology is cost effective and provides an opportunity to produce high barrier polypropylene film on an industrial scale. © 2016 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

  10. Effects of Particle Size and Surface Chemistry on the Dispersion of Graphite Nanoplates in Polypropylene Composites

    Directory of Open Access Journals (Sweden)

    Raquel M. Santos

    2018-02-01

    Full Text Available Carbon nanoparticles tend to form agglomerates with considerable cohesive strength, depending on particle morphology and chemistry, thus presenting different dispersion challenges. The present work studies the dispersion of three types of graphite nanoplates (GnP with different flake sizes and bulk densities in a polypropylene melt, using a prototype extensional mixer under comparable hydrodynamic stresses. The nanoparticles were also chemically functionalized by covalent bonding polymer molecules to their surface, and the dispersion of the functionalized GnP was studied. The effects of stress relaxation on dispersion were also analyzed. Samples were removed along the mixer length, and characterized by microscopy and dielectric spectroscopy. A lower dispersion rate was observed for GnP with larger surface area and higher bulk density. Significant re-agglomeration was observed for all materials when the deformation rate was reduced. The polypropylene-functionalized GnP, characterized by increased compatibility with the polymer matrix, showed similar dispersion effects, albeit presenting slightly higher dispersion levels. All the composites exhibit dielectric behavior, however, the alternate current (AC conductivity is systematically higher for the composites with larger flake GnP.

  11. Polypropylene fumarate/phloroglucinol triglycidyl methacrylate blend for use as partially biodegradable orthopaedic cement.

    Science.gov (United States)

    Jayabalan, M; Thomas, V; Rajesh, P N

    2001-10-01

    Polypropylene fumarate/phloroglucinol triglycidyl methacrylate oligomeric blend-based bone cement was studied. Higher the percentage of phloroglucinol triglycidyl methacrylate, lesser the setting time. An optimum setting time could be arrived with 50:50 blend composition of the two oligomers. Composite cement of 50:50 blend prepared with hydroxyapatite granules of particle size 125 microm binds bovine rib bones. The tensile strength of this adhesive bond was found to be 1.11 kPa. The thermal studies suggest the onset of cross-linking reaction in the cured blend if the blend is heated. The absence of softening endotherm in the cured blend shows the thermosetting-like amorphous nature of blend system, which may restrict the changes in creep properties. The in vitro biodegradation studies reveal possible association of calcium ions with negatively charged units of degrading polymer chain resulting in slow down of degradation. Relatively slow degradation was observed in Ringer's solution. The study reveals the potential use of polypropylene fumarate/phloroglucinol triglycidyl methacrylate as partially degradable polymeric cement for orthopaedic applications.

  12. Adsorption of chromium (Vi) on radiation grafted N,N-dimethylaminoethylmethacrylate onto polypropylene, from aqueous solutions

    International Nuclear Information System (INIS)

    Burillo, G.; Serrano G, J.; Bonifacio M, J.

    2013-01-01

    Polypropylene (Pp) grafted with dimethylaminoethylmethacrylate (DMAEMA), was prepared by irradiation with a 60 Co γ source. The obtained Pp-g-DMAEMA was used to study the Cr(Vi) ion adsorption as a function of contact time, initial ph, initial concentration of metal ion and temperature. Chromium adsorption data on Pp-g-DMAEMA at various initial concentration fit well the Freundlich and Langmuir isotherms. The maximum adsorption capacity (a max ) was found to be 0.3103 x 0 -4 mol g -1 . The thermodynamic parameters ΔH 0 , ΔG 0 and ΔS 0 were estimated showing the adsorption process to be exothermic and spontaneous. (Author)

  13. Micromechanical Characterization of Complex Polypropylene Morphologies by HarmoniX AFM

    Directory of Open Access Journals (Sweden)

    S. Liparoti

    2017-01-01

    Full Text Available This paper examines the capability of the HarmoniX Atomic Force Microscopy (AFM technique to draw accurate and reliable micromechanical characterization of complex polymer morphologies generally found in conventional thermoplastic polymers. To that purpose, injection molded polypropylene samples, containing representative morphologies, have been characterized by HarmoniX AFM. Mapping and distributions of mechanical properties of the samples surface are determined and analyzed. Effects of sample preparation and test conditions are also analyzed. Finally, the AFM determination of surface elastic moduli has been compared with that obtained by indentation tests, finding good agreement among the results.

  14. Mechanical properties in polypropylene-polyethylene blends modified by gamma radiation

    International Nuclear Information System (INIS)

    Ruiz, F.C.; Terence, M.C.

    2008-01-01

    One of the way to obtain a better mechanical property of polypropylene and polyethylene is related to increase the number polymer chains cross-linked by gamma radiation. After irradiation a network is formed which is the result of various chemical reactions occurred during this process, where the radicals formed are concentrated in the amorphous phase. With the objective to increase the mechanical properties of PP, blends with PE were prepared and irradiated in doses up to 100kGy, in atmospheric ambient. The tests showed increase in rigidity and a particular behaviour in Izod impact resistance. (author)

  15. New fillers in the synthesis of polypropylene nano composites with Ziegler-Natta catalysts

    International Nuclear Information System (INIS)

    Rosa, Jeferson L.S.; Silva, Marcelo C.V.; Marques, Maria F.V.

    2011-01-01

    In this study, Ziegler-Natta catalysts bi-supported on MgCl 2 and natural clays were prepared in order to synthesize polypropylene nanocomposites. The employed clays were bentonite, as reference, as well as halloysite, vermiculite and mica. Propylene polymerizations were carried out using those catalysts and the properties of the obtained materials were analyzed using techniques of thermogravimetric analysis X-ray diffraction, dynamic mechanical thermal analysis e scanning electronic microscopy. Results showed the production of nanocomposites with higher thermal degradation temperature. (author)

  16. Influence of the chemical modification and content of the clay on the mechanical properties of polypropylene and national bentonite composites

    International Nuclear Information System (INIS)

    Libano, Elaine V.D.G.; Pacheco, Elen B.A.V.; Visconte, Leila L.Y.

    2011-01-01

    The polypropylene/national clay composite was prepared by melt intercalation in a counter-rotating twin screw extruder, using bentonite as filler either in the natural (BENT) form or modified with the ammonium salt, cetyltrimethylammonium chloride (BENT-org). The clay was used in 1, 3 and 5%w. The influence of the modification and content of clay on the mechanical properties of this system was analysed. The analyses of infrared spectroscopy (FTIR) and X-ray diffraction (XRD) showed that clay organophilization did occur. The tensile modulus and the tensile strength at the yield point were not affected by chemical modification (BENT and BENT-org) or clay content. On the other hand, it was evidenced that the elongation at the yield point decreased with the addition of BENT and BENT-org to polypropylene. According to the thermogravimetric results, it was evidenced that the incorporation of clay into polypropylene improved thermal stability of the polymer in the composites with 5%w of BENT and 3 and 5%w of BENT-org. (author)

  17. Extraction of Micro- and Nano-Fibrils from Nylon 6/Polypropylene Grafted with Maleic Anhydride/Polypropylene Blended Films

    Directory of Open Access Journals (Sweden)

    E. Bagheban Kochak

    2013-01-01

    Full Text Available Atechnical feasibility study has been conducted on production of nano- and micro-fibrils from nylon 6/polypropylene grafted with maleic anhydride/polypropylene blended films. Fibrils are prepared in four consecutive steps.In the first step the polymers melt blended in an extruder with and without compatibilizers to produce chips; in the second step films are extruded from polymer blends chips, in the third step films are cold drawn with different draw ratios at room temperature and in the forth step fibrils are extracted by Soxhlet extraction with formic acid as solvent for nylon 6.  The films and fibrils were examined by scanning electron microscope and FTIR spectroscopy. It is found that the polypropylene dispersed phase deforms and coalesces into elongated fibrils during drawing  operation. The  fibrils’ diameters in the blends containing compatibilizer are more uniform and are smaller than those from films without compatibilizers. The thinnest polypropylene fibril observed has a diameter around 300 nm with the aspect ratio above 150. The stress-elongation curves show three distinctive regions, elastic, yield and hardening-leading to breakage. The elastic region is short and follows by necking and yield, i.e., elongation without increase in load. The hardening region is accompanied by the increase in the slope. The deformations of the polypropylene particles are noticed during the last regions of the extension; the fibril deformations seem to be more severe during breakage.

  18. Modification of polypropylene with radiation-treated wood fiber

    International Nuclear Information System (INIS)

    Czvikovszky, T.; Tapolcai, I.

    1983-01-01

    The dispersed wood material is used not only as filler for thermosetting polymers but also as a new type of fibrous additive for thermoplastics e.g. polypropylene. Benefit of this additive (filler or reinforcement) is determined by the coupling between the wood and the synthetic resin. Fibrous, dispersed wood material was preirradiated in air, treated with vinyl monomer containing polyester resin and then mixed in polypropylene. Processability of such thermoplastic blends as well as reactivity of the mixed components were followed by measuring energy, absorbed during the kneading of the melt. The vinylmonomer vinylmonomer - polyester additive, activated at higher temperature by the radiation-formed peroxy groups on the wood fiber, results in good processability of the thermoplastic blend, and gives interesting mechanical properties. Calandering, extrusion, pressmoulding and mechanical testing demonstrated good workability and practical value of the polypropylene composite material containing radiation-treated wood fiber. (author)

  19. High-voltage pulsed life of multistressed polypropylene capacitor dielectric

    International Nuclear Information System (INIS)

    Laghari, J.R.

    1992-01-01

    High-voltage polypropylene capacitors were aged under singular as well as simultaneous multiple stresses (electrical, thermal, and radiation) at the University of Buffalo's 2 MW thermal nuclear reactor. These stresses were combined neutron-gamma radiation with a total dose of 1.6 x 10 6 rad, electrical stress at 40 V rms /μm, and thermal stress at 90 degrees C. After exposure, the polypropylene dielectric was tested for life (number of pulses to fail) under high-voltage high-repetition-rate (100 pps) pulses. Pulsed life data were also compared with ac life data. Results show that radiation stress causes the most degradation in life, either acting alone or in combination with other stresses. The largest reduction in life occurs when polypropylene is aged under simultaneous multiple stresses (electrical, thermal, and radiation). In this paper, it is shown that pulsed life can be equivalently compared with ac life

  20. Anomalous behavior of secondary dielectric relaxation in polypropylene glycols

    Energy Technology Data Exchange (ETDEWEB)

    Grzybowska, K; Grzybowski, A; Ziolo, J; Rzoska, S J; Paluch, M [Institute of Physics, Silesian University, Uniwersytecka 4, 40-007 Katowice (Poland)

    2007-09-19

    A surprising slow down in the dielectric secondary {gamma}-relaxation with temperature increasing near the glass transition is confirmed for several polypropylene glycols. The peculiar behavior diminishes as the molecular weight grows. The minimal model (Dyre and Olsen 2003 Phys. Rev. Lett. 91 155703) is applied successfully to describe the temperature dependences of the {gamma}-relaxation times. The minimal model parameters are analyzed for different molecular weights. A molecular explanation of the {gamma}-process anomaly for polypropylene glycols is proposed on the basis of the minimal model prediction.

  1. Flexural behaviour of reinforced concrete beams with discrete steel – polypropylene fibres

    Directory of Open Access Journals (Sweden)

    Amizah Wan Jusoh Wan

    2017-01-01

    Full Text Available This paper discusses the experimental results on the flexural test of concrete containing different proportions of steel fibre (SF and polypropylene fibre (PPF. The flexural test was carried out under 4-point bending load and followed the relevant standards to FRC. Hooked-end deformed SF fibre with 60 mm length and fibrillated virgin PPF fibre with 19 mm length were used in this study. Meanwhile, the concrete was designed for high strength concrete of C60. The mixture included both single SF and PPF, and also the combination of both fibres; Control beam (PC, beam with 75%SF, beam with 75%SF + 25%PPF and beam with 25%PPF. The total fibre volume fraction (Vf was fixed at 1.5%. The experimental results show that the percentage proportion of combined SF-PPF at 75-25% had the best performance for its flexural capacity. Mixture with single PPF was also found not effective in delaying the onset of tension cracks and to increase the tensile strength of the concrete. Experimental result also shows beam with 75%SF +25%PPF had their structural stiffness improved the most as compared with the others. For the compressive strength, beam with 75%SF + 25%PPF also revealed comparable performance with the control for high strength composite concrete.

  2. Bond Characteristics of Macro Polypropylene Fiber in Cementitious Composites Containing Nanosilica and Styrene Butadiene Latex Polymer

    Directory of Open Access Journals (Sweden)

    Jae-Woong Han

    2015-01-01

    Full Text Available This study evaluated the bond properties of polypropylene (PP fiber in plain cementitious composites (PCCs and styrene butadiene latex polymer cementitious composites (LCCs at different nanosilica contents. The bond tests were evaluated according to JCI SF-8, in which the contents of nanosilica in the cement were 0, 2, 4, 6, 8, and 10 wt%, based on cement weight. The addition of nanosilica significantly affected the bond properties between macro PP fiber and cementitious composites. For PCCs, the addition of 0–2 wt% nanosilica enhanced bond strength and interface toughness, whereas the addition of 4 wt% or more reduced bond strength and interface toughness. The bond strength and interfacial toughness of LCCs also increased with the addition of up to 6% nanosilica. The analysis of the relative bond strength showed that the addition of nanosilica affects the bond properties of both PCC and LCC. This result was confirmed via microstructural analysis of the macro PP fiber surface after the bond tests, which revealed an increase in scratches due to frictional forces and fiber tearing.

  3. Studies on Poly(propylene fumarate-co-caprolactone diol Thermoset Composites towards the Development of Biodegradable Bone Fixation Devices

    Directory of Open Access Journals (Sweden)

    M. Jayabalan

    2009-01-01

    Full Text Available The effect of reinforcement in the cross-linked poly(propylene fumarate-co-caprolactone diol thermoset composites based on Kevlar fibres and hydroxyapatite was studied. Cross-linked poly(propylene fumarate-co-caprolactone diol was also studied without any reinforcement for comparison. The reinforcing fibre acts as a barrier for the curing reaction leading to longer setting time and lesser cross-link density. The fibre and HA reinforced composites have almost the same compressive strength. Nonreinforced material undergoes greater degree of swelling. Among the reinforced materials, the hydroxyapatite reinforced composite has a much higher swelling percentage than the fibre reinforced one. The studies on in vitro degradation of the cured materials reveal hydrolytic degradation in Ringer's solution and PBS medium during aging. All the three materials are found to swell initially in Ringer's solution and PBS medium during aging and then undergo gradual degradation. Compression properties of these cross-linked composites increase with aging; HA reinforced composite has the highest compressive strength and compressive modulus, whereas the aged fibre-reinforced composite has the least compressive strength and modulus.

  4. Studies on Poly(propylene fumarate-co-caprolactone diol) Thermoset Composites towards the Development of Biodegradable Bone Fixation Devices.

    Science.gov (United States)

    Jayabalan, M

    2009-01-01

    The effect of reinforcement in the cross-linked poly(propylene fumarate-co-caprolactone diol) thermoset composites based on Kevlar fibres and hydroxyapatite was studied. Cross-linked poly(propylene fumarate-co-caprolactone diol) was also studied without any reinforcement for comparison. The reinforcing fibre acts as a barrier for the curing reaction leading to longer setting time and lesser cross-link density. The fibre and HA reinforced composites have almost the same compressive strength. Nonreinforced material undergoes greater degree of swelling. Among the reinforced materials, the hydroxyapatite reinforced composite has a much higher swelling percentage than the fibre reinforced one. The studies on in vitro degradation of the cured materials reveal hydrolytic degradation in Ringer's solution and PBS medium during aging. All the three materials are found to swell initially in Ringer's solution and PBS medium during aging and then undergo gradual degradation. Compression properties of these cross-linked composites increase with aging; HA reinforced composite has the highest compressive strength and compressive modulus, whereas the aged fibre-reinforced composite has the least compressive strength and modulus.

  5. Interactive transport of guanidinylated poly(propylene imine)-based dendrimers through liposomal and cellular membranes.

    Science.gov (United States)

    Tsogas, Ioannis; Sideratou, Zili; Tsiourvas, Dimitris; Theodossiou, Theodossis A; Paleos, Constantinos M

    2007-10-15

    The ability of guanidinylated poly(propylene imine) dendrimers to translocate across lipid bilayers was assessed by employing either a model phosphate-bearing liposomal membrane system or A549 human lung carcinoma cells. Two dendrimer generations, differing in the number of surface guanidinium groups, were employed, while surface acetylation or the use of spacers affected the binding of the guanidinium group to the phosphate moiety and finally the transport efficiency. Following adhesion of dendrimers with liposomes, fusion or transport occurred. Transport through the liposomal bilayer was observed at low guanidinium/phosphate molar ratios, and was enhanced when the bilayer was in the liquid-crystalline phase. For effective transport through the liposomal membrane, an optimum balance between the binding strength and the degree of hydrophobicity of the guanidinylated dendrimer is required. In experiments performed in vitro with cells, efficient penetration and internalization in subcellular organelles and cytosol was observed.

  6. Crystalline structure of polypropylene in blends with thermoplastic elastomers after electron beam irradiation

    International Nuclear Information System (INIS)

    Steller, Ryszard; Zuchowska, Danuta; Meissner, Wanda; Paukszta, Dominik; Garbarczyk, Jozef

    2006-01-01

    Isotactic polypropylene (PP) was blended in extruder with 0-50% addition of styrene-ethylene/butylene-styrene (SEBS) and styrene-butadiene-styrene (SBS) block copolymers. Granulated blends were irradiated with electron beam (60 kGy) and 1 week later processed with injection molding machine. Properties of samples molded from irradiated and non-irradiated granulates were investigated using DSC, WAXS, MFR, SEM and mechanical and solubility tests. It was found that the SEBS based systems are more resistant to irradiation in comparison to similar blends with SBS copolymer. Such behavior can be explained by the presence of double bonds in elastic SBS block. Irradiation of PP-SBS blends leads to considerable structure changes of crystalline and amorphous PP phases and elastic SBS phase. It indicates creation of new (inter)phase consisting of products of grafting and cross-linking reactions. Irradiated PP-SBS blends show significant improvement of impact strength at low temperatures

  7. Polypropylene/elastomers/organophilic bentonite nanocomposites. Influence of elastomer content on morphology and mechanical properties

    International Nuclear Information System (INIS)

    Ferreira, K.R.M.; Braga, C.R.C.; Andrade, D.L.A.C.S.; Carvalho, L.H.; Silva, S.M.L.

    2010-01-01

    In this study, the effect of the elastomer terpolymer ethylene-propylene-diene (EPDM) content on the morphology and mechanical properties of polypropylene PP/EPDM/organophilic bentonite nanocomposite was evaluated. The bentonite, supplied by Bentonit Uniao Nordeste, was purified and organically modified with cetyl trimethyl quaternary ammonium (cetremide) before the incorporation in PP/EPDM blend. The blends with various amounts of EPDM (10, 20, 30 and 40 wt%) and 1 phr of organoclay were prepared by melt-blending at 180 deg C and 50 rpm for 15 min with an internal mixer (Haake). The blends were characterized by X-ray diffraction and mechanical properties (tensile strength). According to the results, we concluded that the content of EPDM affected the morphology and mechanical properties of nanocomposites resulting in improvement in mechanical and morphological properties when a content of 30 wt% of EPDM was used. (author)

  8. Liquid fuel obtain from polypropylene (PP-5) and high density polyethylene (HDPE-2) waste plastics mixture

    Energy Technology Data Exchange (ETDEWEB)

    Sarker, Moinuddin; Rashid, Mohammad Mamunor; Rahman, Md. Sadikur; Molla, Mohammed [Department of Research and Development, Natural State Research Inc, Stamford, (United States)

    2011-07-01

    Plastics are made by combination of small based molecules to form monomers. The monomers are then joined together by chemical polymerization mechanism to form polymers also known as plastics. These plastics contain various elements such as carbon, hydrogen, oxygen, nitrogen, chlorine and sul fur. The use of plastics is vastly expanded and it is being used in every sector of the world. However, using plastics does have a negative aspect, after use they end up in our landfill as waste causing numerous health and environmental problems. Landfill waste plastics release harmful gases due to the presence of carbon, chlorine and sul fur in them into the atmosphere causing climates to change drastically, equivalent to the effects of greenhouse gases (GHG) emission. To overcome these environmental issues, scientists have already developed many methods to converting these waste plastics into energy and fuel . We developed one new methods thermal cracking conversion to convert these waste plastics into usable liquid fuel . Thermal cracking conversion is a process to shorten the long chain hydrocarbons to produce liquid fuel in the absence of a catalyst. The thermal degradation process of the waste plastics long chain hydrocarbon to makes short chain hydrocarbon fuel. The fuel produced has been analyzed and tested according to standard methods. Key words: fuel , hydrocarbon, waste plastic, thermal degradation, conversion, GC/MS.

  9. Liquid fuel obtain from polypropylene (PP-5) and high density polyethylene (HDPE-2) waste plastics mixture

    International Nuclear Information System (INIS)

    Sarker, Moinuddin; Rashid, Mohammad Mamunor; Rahman, Md. Sadikur; Molla, Mohammed

    2011-01-01

    Plastics are made by combination of small based molecules to form monomers. The monomers are then joined together by chemical polymerization mechanism to form polymers also known as plastics. These plastics contain various elements such as carbon, hydrogen, oxygen, nitrogen, chlorine and sul fur. The use of plastics is vastly expanded and it is being used in every sector of the world. However, using plastics does have a negative aspect, after use they end up in our landfill as waste causing numerous health and environmental problems. Landfill waste plastics release harmful gases due to the presence of carbon, chlorine and sul fur in them into the atmosphere causing climates to change drastically, equivalent to the effects of greenhouse gases (GHG) emission. To overcome these environmental issues, scientists have already developed many methods to converting these waste plastics into energy and fuel . We developed one new methods thermal cracking conversion to convert these waste plastics into usable liquid fuel . Thermal cracking conversion is a process to shorten the long chain hydrocarbons to produce liquid fuel in the absence of a catalyst. The thermal degradation process of the waste plastics long chain hydrocarbon to makes short chain hydrocarbon fuel. The fuel produced has been analyzed and tested according to standard methods. Key words: fuel , hydrocarbon, waste plastic, thermal degradation, conversion, GC/MS

  10. An in-depth analysis of the physico-mechanical properties imparted by agricultural fibers and food processing residues in polypropylene biocomposites

    International Nuclear Information System (INIS)

    Murdy, Rachel Campbell; Mak, Michelle; Misra, Manjusri; Mohanty, Amar K.

    2015-01-01

    The use of agricultural and food processing residues as potential reinforcements in plastics has been extensively studied. However, there is a large variation in the mechanical performance of agricultural fiber-based biocomposites due to different processing materials and parameters. An in-depth comparison of the resulting effect of the agricultural filler on the matrix is often not possible given the discrepancy in processing conditions. This study seeks to determine the intrinsic properties of agricultural fibers and food processing residues for their use in polypropylene biocomposites based on a standardization of experimental design. The effect of 25wt% loading of miscanthus, fall-and spring-harvest switchgrass, wheat straw, oat hull, soy hull, soy stalk, hemp and flax on the physico-mechanical properties of polypropylene biocomposites was investigated. The addition of fiber led to an improvement in flexural strength, flexural modulus, and tensile modulus, and a general decrease in tensile strength at yield, elongation at break and Izod impact strength. Scanning electron microscopy highlighted the interfacial adhesion, orientation and distribution of the fibers within the matrix, confirming that fiber length and dispersion within the matrix are positively correlated with mechanical properties. The crystallization of the polypropylene phase and a compositional analysis of the agricultural fibers and processing residues were also compared to offer insight into the effect of the filler’s intrinsic properties on the resulting material performance

  11. An in-depth analysis of the physico-mechanical properties imparted by agricultural fibers and food processing residues in polypropylene biocomposites

    Energy Technology Data Exchange (ETDEWEB)

    Murdy, Rachel Campbell; Mak, Michelle [Bioproducts Discovery and Development Centre, Department of Plant Agriculture, Crop Science Building, University of Guelph, Guelph, ON N1G 2W1 (Canada); Misra, Manjusri; Mohanty, Amar K. [Bioproducts Discovery and Development Centre, Department of Plant Agriculture, Crop Science Building, University of Guelph, Guelph, ON N1G 2W1 (Canada); School of Engineering, Thornbrough Building, University of Guelph, ON N1G 2W1 (Canada)

    2015-05-22

    The use of agricultural and food processing residues as potential reinforcements in plastics has been extensively studied. However, there is a large variation in the mechanical performance of agricultural fiber-based biocomposites due to different processing materials and parameters. An in-depth comparison of the resulting effect of the agricultural filler on the matrix is often not possible given the discrepancy in processing conditions. This study seeks to determine the intrinsic properties of agricultural fibers and food processing residues for their use in polypropylene biocomposites based on a standardization of experimental design. The effect of 25wt% loading of miscanthus, fall-and spring-harvest switchgrass, wheat straw, oat hull, soy hull, soy stalk, hemp and flax on the physico-mechanical properties of polypropylene biocomposites was investigated. The addition of fiber led to an improvement in flexural strength, flexural modulus, and tensile modulus, and a general decrease in tensile strength at yield, elongation at break and Izod impact strength. Scanning electron microscopy highlighted the interfacial adhesion, orientation and distribution of the fibers within the matrix, confirming that fiber length and dispersion within the matrix are positively correlated with mechanical properties. The crystallization of the polypropylene phase and a compositional analysis of the agricultural fibers and processing residues were also compared to offer insight into the effect of the filler’s intrinsic properties on the resulting material performance.

  12. An in-depth analysis of the physico-mechanical properties imparted by agricultural fibers and food processing residues in polypropylene biocomposites

    Science.gov (United States)

    Murdy, Rachel Campbell; Mak, Michelle; Misra, Manjusri; Mohanty, Amar K.

    2015-05-01

    The use of agricultural and food processing residues as potential reinforcements in plastics has been extensively studied. However, there is a large variation in the mechanical performance of agricultural fiber-based biocomposites due to different processing materials and parameters. An in-depth comparison of the resulting effect of the agricultural filler on the matrix is often not possible given the discrepancy in processing conditions. This study seeks to determine the intrinsic properties of agricultural fibers and food processing residues for their use in polypropylene biocomposites based on a standardization of experimental design. The effect of 25wt% loading of miscanthus, fall-and spring-harvest switchgrass, wheat straw, oat hull, soy hull, soy stalk, hemp and flax on the physico-mechanical properties of polypropylene biocomposites was investigated. The addition of fiber led to an improvement in flexural strength, flexural modulus, and tensile modulus, and a general decrease in tensile strength at yield, elongation at break and Izod impact strength. Scanning electron microscopy highlighted the interfacial adhesion, orientation and distribution of the fibers within the matrix, confirming that fiber length and dispersion within the matrix are positively correlated with mechanical properties. The crystallization of the polypropylene phase and a compositional analysis of the agricultural fibers and processing residues were also compared to offer insight into the effect of the filler's intrinsic properties on the resulting material performance.

  13. Removal of light petroleum hydrocarbons from water sources using polypropylene and titanium dioxide nano-composite

    Directory of Open Access Journals (Sweden)

    H. Karyab

    2016-08-01

    Full Text Available Background: Petroleum hydrocarbons are the most important pollutants which threat human health and aquatics. Adsorbents are one of the common equipment in water pollution management; however, their applications have been associated with limitations. Objective: To evaluate the potential of polypropylene/titanium dioxide Nano-composite in adsorption of light petroleum hydrocarbons from water sources. Methods: This experimental study was conducted at school of health, Qazvin University of Medical Sciences in 2014-15. Activation of polypropylene fibers, with 1 cm length and 300 microns diameters, was achieved with wet heating. To synthesize of nano-composite the fibers were coated with nano-titanium dioxide with 20 nm diameter. The sonication was performed at 26 kHz and 100 W of power in 40ºc. The morphology of the fractured surfaces of impact specimens was examined by FESEM. The adsorption rate of petrol and gasoline, as surrogate of TPH, was evaluated in different retention time within polyamide mesh aperture diameter of 250 nm. Average of TPH adsorbing, per unit weight of adsorbent, were analyzed with analysis of variance and Scheffe post hoc tests. Findings: The FESEM micrographs showed that the dispersion of the nano-Tio2 particles was relatively good and only few aggregations exist. The maximum adsorption capacity of petrol and gasoline was obtained in 30 minute. The adsorption rate of gasoline was 6.49±0.10 g/g and oil was 7.01±0.13 g/g. Conclusion: According to the results and in comparison with commercial imported adsorbents, the synthesized Nano-composite had favorable performance. The results show that the polypropylene/Tio2 Nano-composite can be used effectively in light petroleum hydrocarbons removal from polluted water sources.

  14. Colorimetry analysis of polypropylene-polyethylene base copoliners

    International Nuclear Information System (INIS)

    Sunol, J. J.; Saurina, J.; Carrasco, F.; Pages, P.

    1998-01-01

    In this paper, crystallisation process study has been performed, from the molten material, in polypropylene-polyethylene (PP-PE) copolymers rich in PP (∼ 95 wgh.%), using different additives. Some samples have been artificially aged. Calorimetric analysis has been performed by different scanning calorimetry (DSC), from which crystallisation kinetics has been studied under dynamic conditions. (Author) 22 refs

  15. Coir fiber reinforced polypropylene composite panel for automotive interior applications

    Science.gov (United States)

    Nadir Ayrilmis; Songklod Jarusombuti; Vallayuth Fueangvivat; Piyawade Bauchongkol; Robert H. White

    2011-01-01

    In this study, physical, mechanical, and flammability properties of coconut fiber reinforced polypropylene (PP) composite panels were evaluated. Four levels of the coir fiber content (40, 50, 60, and 70 % based on the composition by weight) were mixed with the PP powder and a coupling agent, 3 wt % maleic anhydride grafted PP (MAPP) powder. The water resistance and the...

  16. Environmental and Cost Assessment of a Polypropylene Nanocomposite

    NARCIS (Netherlands)

    Roes, A.L.|info:eu-repo/dai/nl/303022388; Marsili, E.; Nieuwlaar, E.|info:eu-repo/dai/nl/073931373; Patel, M.K.|info:eu-repo/dai/nl/18988097X

    2007-01-01

    This paper describes a study on the use of a polypropylene (PP)/layered silicate nanocomposite as packaging film, agricultural film, and automotive panels. The study’s main question was “Are the environmental impacts and costs throughout the life cycle of nanocomposite products lower than those of

  17. The mechanical properties of unidirectional all-polypropylene composites

    NARCIS (Netherlands)

    Alcock, B.; Cabrera, N.O.; Barkoula, N.M.; Loos, J.; Peijs, A.A.J.M.

    2006-01-01

    The creation of highly oriented, co-extruded polypropylene (PP) tapes allows the production of recyclable ‘all-polypropylene’ composites, with a large temperature processing window (>30 °C) and a high volume fraction of highly oriented PP (>90%). These composites show little deviation of mechanical

  18. PLASTIC SHRINKAGE CONTROLLING EFFECT BY POLYPROPYLENE SHORT FIBER WITH HYDROPHILY

    Science.gov (United States)

    Hosoda, Akira; Sadatsuki, Yoshitomo; Oshima, Akihiro; Ishii, Akina; Tsubaki, Tatsuya

    The aim of this research is to clarify the mechanism of controlling plastic shrinkage crack by adding small amout of synthetic short fiber, and to propose optimum polypropylene short fiber to control plastic shrinkage crack. In this research, the effect of the hydrophily of polypropylene fiber was investigated in the amount of plastic shrinkage of mortar, total area of plastic shrinkage crack, and bond properties between fiber and mortar. The plastic shrinkage test of morar was conducted under high temperature, low relative humidity, and constant wind velocity. When polypropylene fiber had hydrophily, the amount of plastic shrinkage of mortar was restrained, which was because cement paste in morar was captured by hydrophilic fiber and then bleeding of mortar was restrained. With hydrophily, plastic shrinkage of mortar was restrained and bridging effect was improved due to better bond, which led to remarkable reduction of plastic shrinkage crack. Based on experimental results, the way of developing optimum polypropylene short fiber for actual construction was proposed. The fiber should have large hydrophily and small diameter, and should be used in as small amount as possible in order not to disturb workability of concrete.

  19. Packing parameters effect on injection molding of polypropylene nanostructured surfaces

    DEFF Research Database (Denmark)

    Calaon, Matteo; Tosello, Guido; Hansen, Hans Nørgaard

    2012-01-01

    having a diameter of 500 nm was employed. The tool insert surface was produced using chemical-based-batch techniques such aluminum anodization and nickel electroplating. During the injection molding process, polypropylene (PP) was employed as material and packing phase parameters (packing time, packing...

  20. Comparison of polypropylene and silicone Ahmed Glaucoma Valves.

    Science.gov (United States)

    Ishida, Kyoko; Netland, Peter A; Costa, Vital P; Shiroma, Lineu; Khan, Baseer; Ahmed, Iqbal Ike K

    2006-08-01

    To evaluate and compare the clinical outcomes after implantation of the silicone plate and the polypropylene plate Ahmed Glaucoma Valves. Prospective, multicenter, comparative series. A total of 132 patients with uncontrolled glaucoma were treated with either the silicone or polypropylene Ahmed Glaucoma Valve implant. Success was defined according to 2 criteria: (1) intraocular pressure (IOP) of 6 mmHg or more or 21 mmHg or less, and (2) IOP reduction of at least 30% relative to preoperative values. Eyes requiring further glaucoma surgery, including cyclophotocoagulation, or showing loss of light perception were classified as failures. Average follow-up was 12.8 months (range, 6-30 months) for the silicone plate group and 14.5 months (range, 6-30 months) for the polypropylene plate group (P = 0.063). At the last follow-up examination, the mean IOP was 13.8+/-3.9 mmHg and 17.3+/-6.5 mmHg (PAhmed Glaucoma Valve (model FP7) showed improved IOP reduction compared with the polypropylene (model S2) implant. Differences observed in mean IOP, success rate, and complications suggest that plate material may influence clinical outcome.

  1. Polypropylene/organoclay/SEBS nanocomposites with toughness-stiffness properties

    DEFF Research Database (Denmark)

    Sanporean (nee Potarniche), Catalina-Gabriela; Vuluga, Zina; Radovici, Constantin

    2014-01-01

    Polypropylene nanocomposites with a different amount of styrene-ethylene-butylene-styrene block copolymer (SEBS)/clay were prepared via a melt mixing technique. To improve the dispersion of commercial organoclay (denoted as OMMT), various amounts of SEBS were incorporated. At a fixed content of O...

  2. Impact of UV radiation on the physical properties of polypropylene ...

    African Journals Online (AJOL)

    The purpose of this study was to analyse the influence of simulated sun light radiation (xenon lamp) on physical properties of polypropylene (PP) nonwoven material, which is used for the production of agrotextiles. The research showed that the properties of row cover change when radiated with UV light. Tensile, tearing ...

  3. Rapid disintegrating tablets of simvastatin dispersions in polyoxyethylene–polypropylene block copolymer for maximized disintegration and dissolution

    Science.gov (United States)

    Balata, Gehan F; Zidan, Ahmad S; Abourehab, Mohamad AS; Essa, Ebtessam A

    2016-01-01

    The objective of this research was to improve the dissolution of simvastatin and to incorporate it in rapid disintegrating tablets (RDTs) with an optimized disintegration and dissolution characteristics. Polyoxyethylene–polypropylene block copolymer (poloxamer 188) was employed as a hydrophilic carrier to prepare simvastatin solid dispersions (SDs). Fourier transform infrared spectroscopy, differential scanning calorimetry (DSC) and X-ray diffractometry were employed to understand the interaction between the drug and the carrier in the solid state. The results obtained from Fourier transform infrared spectroscopy showed absence of any chemical interaction between the drug and poloxamer. The results of differential scanning calorimetry and X-ray diffractometry confirmed the conversion of simvastatin to distorted crystalline state. The SD of 1:2 w/w drug to carrier ratio showed the highest dissolution; hence, it was incorporated in RDT formulations using a 32 full factorial design and response surface methodology. The initial assessments of RDTs demonstrated an acceptable flow, hardness, and friability to indicate good mechanical strength. The interaction and Pareto charts indicated that percentage of croscarmellose sodium incorporated was the most important factor affecting the disintegration time and dissolution parameter followed by the hardness value and their interaction effect. Compression force showed a superior influence to increase RDT’s porosity and to fasten disintegration rather than swelling action by croscarmellose sodium. On the other hand, croscarmellose sodium was most important for the initial simvastatin release. The results suggest the potential use of poloxamer 188-based SD in RDT for the oral delivery of poor water-soluble antihyperlipidemic drug, simvastatin. PMID:27757012

  4. Rapid disintegrating tablets of simvastatin dispersions in polyoxyethylene-polypropylene block copolymer for maximized disintegration and dissolution.

    Science.gov (United States)

    Balata, Gehan F; Zidan, Ahmad S; Abourehab, Mohamad As; Essa, Ebtessam A

    2016-01-01

    The objective of this research was to improve the dissolution of simvastatin and to incorporate it in rapid disintegrating tablets (RDTs) with an optimized disintegration and dissolution characteristics. Polyoxyethylene-polypropylene block copolymer (poloxamer 188) was employed as a hydrophilic carrier to prepare simvastatin solid dispersions (SDs). Fourier transform infrared spectroscopy, differential scanning calorimetry (DSC) and X-ray diffractometry were employed to understand the interaction between the drug and the carrier in the solid state. The results obtained from Fourier transform infrared spectroscopy showed absence of any chemical interaction between the drug and poloxamer. The results of differential scanning calorimetry and X-ray diffractometry confirmed the conversion of simvastatin to distorted crystalline state. The SD of 1:2 w/w drug to carrier ratio showed the highest dissolution; hence, it was incorporated in RDT formulations using a 3 2 full factorial design and response surface methodology. The initial assessments of RDTs demonstrated an acceptable flow, hardness, and friability to indicate good mechanical strength. The interaction and Pareto charts indicated that percentage of croscarmellose sodium incorporated was the most important factor affecting the disintegration time and dissolution parameter followed by the hardness value and their interaction effect. Compression force showed a superior influence to increase RDT's porosity and to fasten disintegration rather than swelling action by croscarmellose sodium. On the other hand, croscarmellose sodium was most important for the initial simvastatin release. The results suggest the potential use of poloxamer 188-based SD in RDT for the oral delivery of poor water-soluble antihyperlipidemic drug, simvastatin.

  5. Poly(propylene carbonate): Insight into the Microstructure and Enantioselective Ring-Opening Mechanism

    KAUST Repository

    Salmeia, Khalifah A.

    2012-11-13

    Different poly(propylene carbonate) (PPC) microstructures have been synthesized from the alternating copolymerization of CO 2 with both racemic propylene oxide (PO) and various mixtures of PO enantiomers using chiral salen catalysts. The microstructures of the obtained copolymers as a function of polymerization time have been analyzed by a combination of chiral GC and high-resolution NMR spectroscopy. The 13C NMR spectra of selected poly(propylene carbonate) samples were recorded using a 900 MHz ( 1H) spectrometer, showing a previously unreported fine splitting of the carbonate resonances. This allowed a detailed assignment of signals for various copolymer microstructures taking into account the specifics in their stereo- and regioirregularities. For example, the enantioselectivity preference of the (R,R-salen)Co catalyst for (S)-PO at the beginning of the copolymerization leads predominantly to (S)-PO insertion, with any (R)-PO misinsertion being followed by incorporation of (S)-PO, so that the microstructure features isolated stereoerrors. K rel calculations for the copolymerization showed around 5-fold enantioselectivity for (S)-PO over (R)-PO at short reaction time. Analysis of the copolymer microstructures obtained under various reaction conditions appears to be an additional approach to differentiate the occurrence of bimetallic and bifunctional copolymerization mechanisms that are widely discussed in the literature. © 2012 American Chemical Society.

  6. Poly(propylene carbonate): Insight into the Microstructure and Enantioselective Ring-Opening Mechanism

    KAUST Repository

    Salmeia, Khalifah A.; Vagin, Sergei; Anderson, Carly E.; Rieger, Bernhard

    2012-01-01

    Different poly(propylene carbonate) (PPC) microstructures have been synthesized from the alternating copolymerization of CO 2 with both racemic propylene oxide (PO) and various mixtures of PO enantiomers using chiral salen catalysts. The microstructures of the obtained copolymers as a function of polymerization time have been analyzed by a combination of chiral GC and high-resolution NMR spectroscopy. The 13C NMR spectra of selected poly(propylene carbonate) samples were recorded using a 900 MHz ( 1H) spectrometer, showing a previously unreported fine splitting of the carbonate resonances. This allowed a detailed assignment of signals for various copolymer microstructures taking into account the specifics in their stereo- and regioirregularities. For example, the enantioselectivity preference of the (R,R-salen)Co catalyst for (S)-PO at the beginning of the copolymerization leads predominantly to (S)-PO insertion, with any (R)-PO misinsertion being followed by incorporation of (S)-PO, so that the microstructure features isolated stereoerrors. K rel calculations for the copolymerization showed around 5-fold enantioselectivity for (S)-PO over (R)-PO at short reaction time. Analysis of the copolymer microstructures obtained under various reaction conditions appears to be an additional approach to differentiate the occurrence of bimetallic and bifunctional copolymerization mechanisms that are widely discussed in the literature. © 2012 American Chemical Society.

  7. The preparation of layered double hydroxide wrapped carbon nanotubes and their application as a flame retardant for polypropylene

    International Nuclear Information System (INIS)

    Du Baoxian; Fang Zhengping

    2010-01-01

    Carbon nanotubes (CNTs) wrapped with layered double hydroxide (LDH-w-CNTs) were facilely obtained through in situ introduction of CNTs into the hydrothermal reaction system of LDH, with the goal of combining their unique physical and chemical characteristics to meet new advanced applications. Morphological observations indicated that LDH lamellae enwrapped the surface of CNTs and the wrapping degree was dependent on the functionalization of CNTs. ζ-potential measurements showed that the interaction between the positive charge of LDH and the negative charge of CNTs was the main driving force of the wrapping process. Both hybrids led to a reduction in the peak heat release rate (PHRR) of polypropylene, indicating that they could confer better flame retardancy on polypropylene with respect to LDH and CNTs.

  8. Study of the effect of ionizing radiation on composites of wood flour in polypropylene matrix using barium titanate as coupling agent; Estudo do efeito da radiacao ionizante em compositos de polipropileno/po de madeira usando titanato de bario como agente de acoplagem

    Energy Technology Data Exchange (ETDEWEB)

    Ulloa, Maritza Eliza Perez

    2007-07-01

    sample easier to be processed, increasing the mobility among the macromolecules, so that decreasing the viscosity and increasing the flow rate. The results obtained from the essay of the resistance to traction showed an addition of the property. The increase occurred both in the samples with no additives. The radiation modified the composite material occurring the formation of crosslinking. The incorporation of wood flour to the propylene resulted to the decrease of the resistance to the impact. The decrease of this property can be occurred because of the presence of wood flour can act as a tension concentrator, and consequently, reduces the impact strength. There was an addition in the hardness of the composites which had wood flour. The addition in the hardness was meaningful to the composites WF/PP, that because the bigger the amount of load, the bigger the module of hardness. In the irradiated samples, the hardness increase due to the wood oxidation, face to the radiation. It was observed that in some cases the increase in the radiation dose, did not influenced meaningfully in the variation of the temperature of thermal deflection of the composites indicating that there was crosslinking among the molecules promoted by TPDGA, and an improvement in the adhesion among interfaces promoted by the titanate. In the essay of temperature of softening Vicat, results presented were quite closed to pure PP and the results were not meaningful, the temperature of the composites can be considered the same of the pure PP. The ionizing radiation interacted in the composite material crosslinking the PP and oxidant the wood, what shows an increase in some proprieties and decrease in others ones. (author)

  9. Sensitivity of the polypropylene to the strain rate: experiments and modeling

    International Nuclear Information System (INIS)

    Abdul-Latif, A.; Aboura, Z.; Mosleh, L.

    2002-01-01

    , i.e. to describe the elastic-viscoplastic behavior of the polypropylene for other loading paths which did not use during the identification process. Finally, the obtained model being devoted to describe the stress-strain behavior of the polypropylene, is able to fairly well reproduce the strain rate dependent deformation of such a material under several loading conditions (uniaxial tensile load at different strain rates, strain rate jumping and relaxation phenomenon). It is important to keep in mind that the final objective will be to model the damaged behavior of women fibbers glass composite materials with thermoplastic matrix

  10. Flame Retardancy and Mechanical Properties of Kenaf Filled Polypropylene (PP) Containing Ammonium Polyphosphate (APP)

    International Nuclear Information System (INIS)

    Atikah Ismail; Azman Hassan; Aznizam Abu Bakar; Jawaid, M.

    2013-01-01

    The effects of ammonium polyphosphate (APP) as flame retardant and kenaf as fillers on flammability, thermal and mechanical properties of polypropylene (PP) composites were determined. Test specimens were prepared by using a co-rotating twin screw extruder for the compounding process followed by injection molding. The flame retardancy of the composites was determined by using limiting oxygen index (LOI) test. Addition of flame retardant into kenaf-PP composites significantly increased the LOI values that indicated the improvement of flame retardancy. Thermogravimetric analysis was done to examine the thermal stability of the composites. The addition of kenaf fiber in PP composites decreased the thermal stability significantly but the influence of APP on thermal properties of the kenaf-filled PP composites was not significant. The flexural strength and modulus of composites increased with the addition of APP into kenaf filled PP composite. The addition of APP into kenaf filled PP causes increase in the impact strength while increasing the APP content in the kenaf filled PP composite show decrease in impact strength. (author)

  11. Nuclear magnetic resonance study of the effect of the addition of clay on polypropylene

    International Nuclear Information System (INIS)

    Nogueira, Regina F.; San Gil, Rosane A.S.; Tavares, Maria Ines B.

    2001-01-01

    Polypropylene (PP) samples and polypropylene (PP)/clay (M) composite prepared by melting mixing have been characterized by solution and solid state nuclear magnetic resonance spectroscopy (NMR). The monomer sequences distribution and the influence of time and temperature of mechanical mix on the modifications in the PP structure were investigated by 13 C solution NMR. The solid state NMR investigation showed that the 13 C routine spectra such as MAS and CPMAS allowed obtaining information on the molecular domains of chains, and also permits to evaluate the domains mobility. 29 Si and 27 Al solid state NMR were used to characterize the clay and the PP/M composite samples. The results showed that the heating and friction in the range of temperature and time used in the sample preparation did not affect the distribution of configurational sequence in the PP chains. The effect of clay in the PP/M composite structure could be detected, using both 13 C solution and in 29 Si solid state NMR spectra. (author)

  12. The influence of temperature on the formation of liquid fuel from Polypropylene plastic wastes

    Science.gov (United States)

    Martynis, M.; Mulyazmi; Praputri, E.; Witri, R.; Putri, N.

    2018-03-01

    The current trend of municipal waste management in urban areas is caused by rapid changes in social, economic, political and cultural life. As a non-biodegradable polymers that have become essential materials, plastic wastes have created a very serious environmental challenge because of the huge quantities and their disposal problems. Recycling of plastics is seen as one method for reducing environmental and resource depletion. The most attractive technique of plastics recycling is pyrolysis involving the degradation of the polymeric materials by heating in the absence of oxygen. This study investigated the characteristics of pyrolysis liquid fuel (PLF) produced from polypropylene plastic wastes with temperature variations. Pyrolisis was carried out on 200 grams of polypropylene waste plastics at the operating temperature of 200°C, 250°C, 300 °C and 350 °C for 45 minutes. The liquid products were found to have carbon chain length in the range of C8-C9, similar with gasoline. The maximum density, volume and calorific value of the oil obtained were 0.8 g/cm3, 61 ml and 1307 cal/gr, respectively.

  13. On crystallization of polypropylene on atomically flat silicate substrate and relationship to mechanical properties

    International Nuclear Information System (INIS)

    Huang, H.Z.; Yuan, Q.; Misra, R.D.K.

    2011-01-01

    Research highlights: → Phyllosilicate was used to probe the nucleation and chain organization in thin films. → Crystal morphology was altered from leaf-like structure to fully developed spherulites. → The lamellae structure changed from well-oriented to cross-hatched implying epitaxial growth. → The good interfacial bonding favored by epitaxial crystallization is beneficial for toughness. - Abstract: Phyllosilicates including mica offer one of the easiest methods to obtain atomically flat surface of macroscopic size by cleavage. Thus, thin films of polypropylene crystallized at different pressure and as a function of polypropylene concentration were investigated. The objective was to probe the nucleation and chain organization in thin films on basal plane surface from the view point of relating the nucleation and growth process to the intergallery space between the clay layers. The crystal morphology was altered from leaf-like structure at high undercooling to fully developed spherulites at low undercooling. Furthermore, the lamellae structure change from well-oriented to cross-hatched with increase in the crystallization pressure was indicative of epitaxial growth between polymer matrix and mica surface. The possible epitaxial mechanism is discussed here. The study provides a method to explore the macro- and microstructure of polymer and epitaxy between polymer matrix and inorganic particle surface. The good interfacial bonding favored by epitaxial crystallization is beneficial for toughness.

  14. Tension free monofilament macropore polypropylene mesh (Gynemesh PS in female genital prolapse repair

    Directory of Open Access Journals (Sweden)

    Vicente Sola

    2006-08-01

    Full Text Available OBJECTIVES: To review intraoperative and postoperative complications associated to the correction of cystocele and rectocele with polypropylene mesh macropore monofilament (Gynemesh PS using transvaginal free tension technique. MATERIALS AND METHODS: Prospective study of patients that have been submitted to correction of cystocele and/or rectocele between November 2004 and August 2005 in the Urogynecology and Vaginal Surgery Unit of Gynecology and Obstetrics Department, Las Condes Clinic. Mesh was used in 31 patients: 9 for cystocele, 11 for rectocele, and 11 for concomitant meshes. Total mesh used 42. Media age 55 years old, weight 64 kilograms. In 7 patients we used a third mesh for correction of urinary incontinence by TVT-O technique. RESULTS: They did not present intraoperative complications, neither in immediate or delayed postoperative time. We did not observe hematoma, infection, erosion or exposition mesh. Healing of cystocele and rectocele was obtained in 100% of patients, with a pursuit between 1 and 8 months. DISCUSSION: The use of prosthetic polypropylene monofilament macropore mesh in the correction of cystocele and/or rectocele, by transvaginal route with tension free technique seems to be a safe and effective surgery procedure.

  15. Transparent Low Electrostatic Charge Films Based on Carbon Nanotubes and Polypropylene. Homopolymer Cast Films

    Directory of Open Access Journals (Sweden)

    Zoe Vineth Quiñones-Jurado

    2018-01-01

    Full Text Available Use of multi-wall carbon nanotubes (MWCNTs in external layers (A-layers of ABA-trilayer polypropylene films was investigated, with the purpose of determining intrinsic and extrinsic factors that could lead to antistatic behavior of transparent films. The incorporation of 0.01, 0.1, and 1 wt % of MWCTNs in the A-layers was done by dilution through the masterbatch method. Masterbatches were fabricated using isotactic polypropylene (iPP with different melt flow indexes 2.5, 34, and 1200 g/10 min, and using different ultrasound assist methods. It was found that films containing MWCNTs show surface electrical resistivity of 1012 and 1016 Ω/sq, regardless of the iPP melt flow index (MFI and masterbatch fabrication method. However, electrostatic charge was found to depend upon the iPP MFI, the ultrasound assist method and MWCNT concentration. A percolation electron transport mechanism was determined most likely responsible for this behavior. Optical properties for films containing MWCNTs do not show significant differences compared to the reference film at MWCNT concentrations below 0.1 wt %. However, an enhancement in brightness was observed, and it was attributed to ordered iPP molecules wrapping the MWCNTs. Bright transparent films with low electrostatic charge were obtained even for MWCNTs concentrations as low as 0.01 wt %.

  16. Rheological, Colour and Processing Properties of Polypropylene Masterbatches for Nanocomposite Fibre Preparation

    Directory of Open Access Journals (Sweden)

    Štefan Krivoš

    2017-12-01

    Full Text Available Asia’s current dominance of the global production of standard types of chemical fibres requires the sophistication of European fibre and textile products. Modifying the mass or surface of materials using nanotechnologies is one of the most promising ways to ensure the special, mono- and multi-functionally modified fibre properties of clothing and technical textiles. The permanent antimicrobial treatment of fibre mass represents one the most desired functional modifi cations of chemical fibres. It involves the use of an antimicrobial additive masterbatch with the appropriate rheological, colour and processing properties required for the preparation of antimicrobial modified fibres. This article presents the results of our study of the effect of two types of nanoadditives (nanosilica and nanocalcium carbonate as potential carriers of an AMB active ingredient, and the effect of stearic acid, polyethylene glycol and propylene oxide as various dispersing systems on the rheological, colour and processing properties of polypropylene nanoadditive masterbatches. The obtained experimental results are evaluated in terms of the suitability of the properties of prepared nanoadditive masterbatches for the preparation of nanocomposite polypropylene fibres.

  17. The effect of temperature and strain rate on the mechanical properties of highly oriented polypropylene tapes and all-polypropylene composites

    NARCIS (Netherlands)

    Alcock, B.; Cabrera, N.O.; Barkoula, N.M.; Reynolds, C.T.; Govaert, L.E.; Peijs, A.A.J.M.

    2007-01-01

    The creation of highly oriented, co-extruded polypropylene (PP) tapes allows the production of recyclable "all-polypropylene" (all-PP) composites, with a large temperature processing window and a high volume fraction of highly oriented PP (>90%). The wholly thermoplastic nature of these

  18. Surface functionalisation of polypropylene hernia-repair meshes by RF-activated plasma polymerisation of acrylic acid and silver nanoparticles

    Energy Technology Data Exchange (ETDEWEB)

    Nisticò, Roberto, E-mail: roberto.nistico@unito.it [University of Torino, Department of Chemistry and NIS Research Centre, Via P. Giuria 7, 10125 Torino (Italy); Rosellini, Andrea [University of Torino, Department of Chemistry and NIS Research Centre, Via P. Giuria 7, 10125 Torino (Italy); Rivolo, Paola [Politecnico di Torino, Dipartimento di Scienza Applicata e Tecnologia, C.so Duca degli Abruzzi 24, 10129 Torino (Italy); Faga, Maria Giulia [CNR-IMAMOTER, Strada delle Cacce 73, 10135 Torino (Italy); Lamberti, Roberta; Martorana, Selanna [Herniamesh S.r.l., Via F.lli Meliga 1/C, 10034 Chivasso (Italy); Castellino, Micaela [Center for Space Human Robotics, Istituto Italiano di Tecnologia, Corso Trento 21, 10129 Torino (Italy); Virga, Alessandro; Mandracci, Pietro [Politecnico di Torino, Dipartimento di Scienza Applicata e Tecnologia, C.so Duca degli Abruzzi 24, 10129 Torino (Italy); Malandrino, Mery; Magnacca, Giuliana [University of Torino, Department of Chemistry and NIS Research Centre, Via P. Giuria 7, 10125 Torino (Italy)

    2015-02-15

    Graphical abstract: - Highlights: • Polypropylene meshes for hernioplasty were surface functionalised via plasma-polymerisation to confer adhesive properties. • Subsequently, silver nanoparticles were loaded to add antibacterial activity. • Materials were physico-chemical characterised and adhesive properties evaluated. - Abstract: Hernia diseases are among the most common and diffuse causes of surgical interventions. Unfortunately, still nowadays there are different phenomena which can cause the hernioplasty failure, for instance post-operative prostheses displacements and proliferation of bacteria in the surgical site. In order to limit these problems, commercial polypropylene (PP) and polypropylene/Teflon (PP/PTFE) bi-material meshes were surface functionalised to confer adhesive properties (and therefore reduce undesired displacements) using polyacrylic acid synthesized by plasma polymerisation (PPAA). A broad physico-chemical and morphological characterisation was carried out and adhesion properties were investigated by means of atomic force microscopy (AFM) used in force/distance (F/D) mode. Once biomedical devices surface was functionalised by PPAA coating, metallic silver nanoparticles (AgNPs) with antimicrobial properties were synthesised and loaded onto the polymeric prostheses. The effect of the PPAA, containing carboxylic functionalities, adhesive coating towards AgNPs loading capacity was verified by means of X-ray photoelectron spectroscopy (XPS). Preliminary measurement of the Ag loaded amount and release in water were also investigated via inductively coupled plasma atomic emission spectroscopy (ICP-AES). Promising results were obtained for the functionalised biomaterials, encouraging future in vitro and in vivo tests.

  19. Production of sorption-active polypropylene fibers by radiation-induce grafting of glycidyl methacrylate as a precursor monomer

    International Nuclear Information System (INIS)

    Bondar, Yu.V.; Kim, H.J.; Lim, Y.J.; Kravets, L.I.

    2004-01-01

    Full text: Two types of sorption-active polypropylene fiber carrying strong-acid sulfonate groups and amino groups have been synthesized by radiation-induced graft polymerization of glycidyl methacrylate (GMA) with subsequent chemical modification of the epoxy groups of poly-GMA graft chains. The effect of various polymerization parameters on the GMA grafting degree was investigated in detail. The epoxy ring-opening of poly-GMA graft chains with introduction of strong-acid sulfonate groups was carried out with sodium hydrogen sulfite in water-dimethylformamide solution at 70 o C. The main peculiarities of the sulfonation reaction in depending on the reaction time and GMA grafting degree have been investigated. It was shown that for the samples with GMA grafting degree more than 50% two simultaneous processes take place during the sulfonation reaction, namely the incorporation of the sulfonate groups via opening of the GMA epoxy-rings as well as hydrolysis of the GMA epoxy-rings with the formation of α-glycol groups. Amine groups were incorporated by treatment of GMA-grafted polypropylene fibers with excess of diethylene triamine reagent. The conversion of the epoxy groups into the functional groups was investigated as a function of the degree of GMA grafting and reaction time. The ion-exchange characteristics of obtained sorption-active polypropylene fibers were determined

  20. Production of sorption-active polypropylene fiber by radiation-induce grafting of glycidyl methacrylate as a precursor monomer

    International Nuclear Information System (INIS)

    Bondar, Yu.V.; Kim, H.J.; Lim, Y.J.; Kravets, L.I.

    2004-01-01

    Two types of sorption-active polypropylene fiber carrying strong-acid sulfonate groups and amino groups have been synthesized by radiation-induced graft polymerization of glycidyl methacrylate (GMA) with subsequent chemical modification of the epoxy groups of poly-GMA graft chains. The effect of various polymerization parameters on the GMA grafting degree was investigated in detail. The epoxy ring-opening of poly-GMA graft chains with introduction of strong-acid sulfonate groups was carried out with sodium hydrogen sulfite in water-dimethylformamide solution at 70 o C. The main peculiarities of the sulfonation reaction in depending on the reaction time and GMA grafting degree have been investigated. It was shown that for the samples with GMA grafting degree more than 50% two simultaneous processes take place during the sulfonation reaction, namely the incorporation of the sulfonate groups via opening of the GMA epoxy-rings as well as hydrolysis of the GMA epoxy-rings with the formation of α-glycol groups. Amine groups were incorporated by treatment of GMA-grafted polypropylene fibers with excess of diethylene triamine reagent. The conversion of the epoxy groups into the functional groups was investigated as a function of the degree of GMA grafting and reaction time. The ion-exchange characteristics of obtained sorption-active polypropylene fibers were determined. (author)

  1. INFLUENCE OF KENAF AND POLYPROPYLENE FIBRES ON MECHANICAL AND DURABILITY PROPERTIES OF FIBRE REINFORCED LIGHTWEIGHT FOAMED CONCRETE

    Directory of Open Access Journals (Sweden)

    H. AWANG

    2015-04-01

    Full Text Available This paper investigates the mechanical and durability properties of lightweight foamed concrete (LFC with the inclusion of kenaf and polypropylene fibres. A density of 1000kg/m3 foamed concrete was used for all the tested specimens. The ratio of cement, sand and water used was 1:1.5:0.45. Polypropylene and kenaf fibres were used as additives at 0.25% and 0.4% by volume of the total mix. A 30% cement replacement by fly ash was used with each type of additive. All the experiments were set up in accordance with International standard methods of testing. Scanning electron microscopy (SEM analysis is included to have a better view of the concrete behavior with fibre inclusions. In reference to the analysis and discussion, the types of fibre used were proven to have a lesser contribution towards compressive strength or might even have reduced the result. However, the integration of fly ash enhanced the compressive strength. In addition, a higher percentage of fiber inclusions had been recorded to have a positive contribution towards flexural, tensile spiltting and shrinkage properties of LFC.

  2. Fabrication and characterization of jute fabrics reinforced polypropylene-based composites: effects of ionizing radiation and disaccharide (sucrose)

    Science.gov (United States)

    Sahadat Hossain, Md.; Uddin, Muhammad B.; Razzak, Md.; Sarwaruddin Chowdhury, A. M.; Khan, Ruhul A.

    2017-12-01

    Composites were prepared successfully by compression molding technique using jute fabrics (reinforcing agent) and polypropylene (matrix). Jute fabrics were treated with disaccharide (sucrose) solution and composites were fabricated with the treated fabric and polypropylene. The fiber content of the prepared composites was 40% by weight. It was found that the sucrose (2% solution) decreased the tensile strength (TS) and elongation at break about 6% and 37%, respectively, but tensile modulus and impact strength improved about 27% and 32%, respectively. When gamma radiation was applied through the untreated and treated composites the mechanical properties were improved much higher in non-treated Jute/PP-based composites than that of sucrose treated composites. For 5.0 kGy gamma dose the highest mechanical properties were observed for non-treated composites. At 5.0 kGy gamma dose the improvement of TS was 14% and 2% for non-treated and sucrose treated composites, respectively. The water uptake property of the sucrose treated composites was performed up to 10 days and composites absorbed 18% water. The functional groups of the both composites were analyzed by Fourier transform infrared spectroscopy machine. The scanning electron microscopic images of the both composites were taken for the surface and fiber adhesion analysis.

  3. Processing and characterization of halloysite nanotubes filled polypropylene nanocomposites based on a masterbatch route: effect of halloysites treatment on structural and mechanical properties

    Directory of Open Access Journals (Sweden)

    2011-04-01

    Full Text Available Halloysites/polypropylene nanocomposites with different nanotubes contents were prepared by diluting a masterbatch containing 30 wt.% halloysites with polypropylene (PP. Unmodified (HNTs and quaternary ammonium salt treated (QM-HNTs halloysite nanotubes were used. Both degree of crystallinity and crystallization temperature increase upon addition of halloysites into PP, thus indicating a potential nucleation effect induced by the nanotubes. An homogeneous distribution and dispersion of nanotubes was observed throughout the PP matrix, with a slightly better dispersion in the case of modified QM-HNTs compared to unmodified HNTs. Mechanical tests in tension, bending and notched impact demonstrated that strength and modulus of the nanocomposites significantly increase with addition of halloysites without significant loss of ductility. An halloysite content of 6 wt.% appears as an optimum. Modified halloysites (QM-HNTs lead to globally better performances due to strong interfacial interaction between the polymer matrix and the nanotubes.

  4. Functionalization of silica nanoparticles for polypropylene nanocomposites applications

    International Nuclear Information System (INIS)

    Bracho, Diego; Palza, Humberto; Quijada, Raul; Dougnac, Vivianne

    2011-01-01

    Synthetic silica nanospheres of different diameters produced via the sol-gel method were used in order to enhance the barrier properties of the polypropylene-silica nanocomposites. Modification of the silica surface by reaction with organic chlorosilanes was performed in order to improve the particles interaction with the polypropylene matrix and its dispersion. Unmodified and modified silica nanoparticles were characterized using electronic microscopy (TEM), elemental analysis, thermo gravimetric analysis (TGA), and solid state nuclear magnetic resonance (NMR) spectroscopy. Preliminary permeability tests of the polymer-silica nanocomposite films showed no significant change at low particles load (3 wt%) regardless its size or surface functionality, mainly because of the low aspect ratio of the silica nanospheres. However, it is expected that at a higher concentration of silica particles differences will be observed. (author)

  5. Carbon ion irradiation induced surface modification of polypropylene

    International Nuclear Information System (INIS)

    Saha, A.; Chakraborty, V.; Dutta, R.K.; Chintalapudi, S.N.

    2001-01-01

    Polypropylene was irradiated with 12 C ions of 3.6 and 5.4 MeV energies in the fluence range of 5x10 13 -5x10 14 ions/cm 2 using 3 MV tandem accelerator. Ion penetration was limited to a few microns and surface modifications were investigated by scanning electron microscopy. At the lowest ion fluence only blister formation of various sizes (1-6 μm) were observed, but at higher fluence (1x10 14 ions/cm 2 ) a three-dimensional network structure was found to form. A gradual degradation in the network structure was observed with further increase in the ion fluence. The dose dependence of the changes on surface morphology of polypropylene is discussed

  6. Carbon ion irradiation induced surface modification of polypropylene

    Energy Technology Data Exchange (ETDEWEB)

    Saha, A. E-mail: abhijit@alpha.iuc.res.in; Chakraborty, V.; Dutta, R.K.; Chintalapudi, S.N

    2001-12-01

    Polypropylene was irradiated with {sup 12}C ions of 3.6 and 5.4 MeV energies in the fluence range of 5x10{sup 13}-5x10{sup 14} ions/cm{sup 2} using 3 MV tandem accelerator. Ion penetration was limited to a few microns and surface modifications were investigated by scanning electron microscopy. At the lowest ion fluence only blister formation of various sizes (1-6 {mu}m) were observed, but at higher fluence (1x10{sup 14} ions/cm{sup 2}) a three-dimensional network structure was found to form. A gradual degradation in the network structure was observed with further increase in the ion fluence. The dose dependence of the changes on surface morphology of polypropylene is discussed.

  7. Ziegler-Natta catalyst for polypropylene and polyethylene nanocomposites preparation

    International Nuclear Information System (INIS)

    Silvino, Alexandre C.; Dias, Marcos L.; Bezerra, Ana Beatriz F.

    2009-01-01

    Polypropylene and polyethylene nanocomposites are well known for their improved properties when compared with the neat polymers. In this work we report the preparation, characterization and the activity studies of a fourth generation Ziegler-Natta catalyst for the preparation of polyolefin/clay nanocomposites. The catalyst was prepared treating an organo-modified silicate with magnesium and titanium compounds. The content of titanium and that of the magnesium of the catalyst were determined by UV-vis spectroscopy and atomic absorption respectively. The first results show that the catalyst is active for propylene polymerization being suitable for polypropylene/clay nanocomposite preparation. The catalyst activity for ethylene polymerization was also investigated. The X-ray diffraction patterns of the polyethylene samples suggest the clay exfoliation occurs in the in situ polymerization, even with high clay loading (about 9 %) indicating that a nanocomposite was formed. (author)

  8. Rheological and Thermal Behavior of Polypropylene-Kaolin Composites

    International Nuclear Information System (INIS)

    Teng, S.T.; Nor Azura Abdul Rahim; Lan, D.N.U

    2014-01-01

    Kaolins effect on rheological behaviour of polypropylene-kaolin composites was investigated. The research found that not only the kaolin content influence the rheological behaviour but also the compounding using internal mixer and twin screw extruder. In details, viscosity and shear stress increased with addition of kaolin content. These characteristics also exhibited higher in polypropylene-kaolin composite suspensions compounded using twin screw extruder than using internal mixer. Chain scission was assumed to occur and affect the melt properties. Further justification characterized by Differential Scanning Calorimeter (DSC) showed that the effect of kaolin and loading content were more evident on the onset melting temperature and crystallinity. Besides, due to the different cooling operation in both processes, the effect of compounding on melting characteristic was conspicuous. (author)

  9. Development of Anti-Insect Microencapsulated Polypropylene Films Using a Large Scale Film Coating System.

    Science.gov (United States)

    Song, Ah Young; Choi, Ha Young; Lee, Eun Song; Han, Jaejoon; Min, Sea C

    2018-04-01

    Films containing microencapsulated cinnamon oil (CO) were developed using a large-scale production system to protect against the Indian meal moth (Plodia interpunctella). CO at concentrations of 0%, 0.8%, or 1.7% (w/w ink mixture) was microencapsulated with polyvinyl alcohol. The microencapsulated CO emulsion was mixed with ink (47% or 59%, w/w) and thinner (20% or 25%, w/w) and coated on polypropylene (PP) films. The PP film was then laminated with a low-density polyethylene (LDPE) film on the coated side. The film with microencapsulated CO at 1.7% repelled P. interpunctella most effectively. Microencapsulation did not negatively affect insect repelling activity. The release rate of cinnamaldehyde, an active repellent, was lower when CO was microencapsulated than that in the absence of microencapsulation. Thermogravimetric analysis exhibited that microencapsulation prevented the volatilization of CO. The tensile strength, percentage elongation at break, elastic modulus, and water vapor permeability of the films indicated that microencapsulation did not affect the tensile and moisture barrier properties (P > 0.05). The results of this study suggest that effective films for the prevention of Indian meal moth invasion can be produced by the microencapsulation of CO using a large-scale film production system. Low-density polyethylene-laminated polypropylene films printed with ink incorporating microencapsulated cinnamon oil using a large-scale film production system effectively repelled Indian meal moth larvae. Without altering the tensile and moisture barrier properties of the film, microencapsulation resulted in the release of an active repellent for extended periods with a high thermal stability of cinnamon oil, enabling commercial film production at high temperatures. This anti-insect film system may have applications to other food-packaging films that use the same ink-printing platform. © 2018 Institute of Food Technologists®.

  10. Surface modification of polypropylene membrane by polyethylene glycol graft polymerization

    Energy Technology Data Exchange (ETDEWEB)

    Abednejad, Atiye Sadat, E-mail: atiyeabednejad@gmail.com [Department of Biomedical Engineering, Faculty of New Sciences and Technologies, University of Tehran, P.O. Box 14395-1561, Tehran (Iran, Islamic Republic of); Amoabediny, Ghasem [Department of Life Science Engineering, Faculty of New Sciences and Technologies, University of Tehran, P.O. Box 14395-1561, Tehran (Iran, Islamic Republic of); Research Center for New Technologies in Life Science Engineering, University of Tehran, P.O. Box 63894-14179, Tehran (Iran, Islamic Republic of); Ghaee, Azadeh [Department of Biomedical Engineering, Faculty of New Sciences and Technologies, University of Tehran, P.O. Box 14395-1561, Tehran (Iran, Islamic Republic of)

    2014-09-01

    Polypropylene hollow fiber microporous membranes have been used in a wide range of applications, including blood oxygenator. The hydrophobic feature of the polypropylene surface causes membrane fouling. To minimize fouling, a modification consisting of three steps: surface activation in H{sub 2} and O{sub 2} plasma, membrane immersion in polyethylene glycol (PEG) and plasma graft polymerization was performed. The membranes were characterized by contact angle measurement, Fourier transform infrared spectroscopy (FTIR), X-ray photoelectron spectroscopy (XPS), tensile test, scanning electron microscopy (SEM) and atomic force microscopy (AFM). Oxygen transfer of modified membranes was also tested. The stability of grafted PEG was measured in water and in phosphate buffer saline (PBS) at 37 °C. Blood compatibility of modified surfaces was evaluated by the platelet adhesion method. Water contact angel reduction from 110° to 72° demonstrates the enhanced hydrophilicity, and XPS results verify the presence of oxygenated functional groups due to the peak existence in 286 eV as a result of PEG grafting. The results clearly indicate that plasma graft-polymerization of PEG is an effective way for antifouling improvement of polypropylene membranes. Also, the results show that oxygen transfer changes in PEG grafted membranes are not significant. - Highlights: • H{sub 2} and O{sub 2} plasma graft polymerization of PEG on polypropylene membrane was carried out. • Changes in surface properties were investigated by FTIR, XPS, SEM, and AFM. • Surface wettability enhanced as a result of poly ethylene glycol grafting. • PEG grafting degree increase causes reduction of fouling and adhesion.

  11. Quality evaluation of polypropylene packaged corn yogurt during storage

    Science.gov (United States)

    Aini, Nur; Prihananto, V.; Sustriawan, B.; Astuti, Y.; Maulina, M. R.

    2018-01-01

    Packaging is an important factor to control the process of quality decrease of any food product, including to determine the shelf life. The objective of this study was to determine changes quality of corn yogurt packaged using polypropylene. The method were using was package yogurt polypropylene, then it was stored in a refrigerator at 5, 10, or 15°C during 21 days. The yogurt was analysed every 7 days over a 21-day period. The results indicate that protein content decreased during storage, while the lactic acid bacteria, total acid, pH, viscosity, and total solids were increased. At the end of storage, the amount of lactic acid bacteria still fulfil the minimum requirements of a probiotic food, with a count of 6.407 log CFU/g. Overal scoring by panelist (scores ranged from 0 to 5) have a 4.78 at the beginning of storage. By the 21st day of storage, yogurt was packaging using transparent polypropylene having a score of 3.85, and that stored in opaque white packaging having a value of 3.95.

  12. Property Relationship in Organosilanes and Nanotubes Filled Polypropylene Hybrid Composites

    Directory of Open Access Journals (Sweden)

    Alejandra J. Monsiváis-Barrón

    2014-10-01

    Full Text Available Polypropylene composites with different filler contents were prepared by creating a masterbatch containing 3 wt%. filler. A variety of silanol groups were used to synthetized three compounds in different media trough a sol-gel process with acetic acid, formic acid and ammonium hydroxide as catalysts. Besides, four different nanotubular fillers were also used to analyze their behavior and compare it with the effect caused by the silanol groups. These tubular structures comprise: unmodified halloysite, carbon nanotubes and functionalized halloysite and carbon nanotubes. Morphological characterization in SEM and STEM/TEM showed dispersion in the polypropylene matrix. According to TGA and DSC measurements thermal behavior remain similar for all the composites. Mechanical test in tension demonstrate that modulus of the composites increases for all samples with a major impact for materials containing silanol groups synthetized in formic acid. Rheological measurements show a significantly increment in viscosity for samples containing unmodified and modified carbon nanotubes. No difference was found for samples containing silanol groups and halloysite when compared to neat polypropylene. Finally, the oxygen transmission rate increased for all samples showing high barrier properties only for samples containing natural and functionalized halloysite nanotubes.

  13. Development and characterisation of injection moulded, all-polypropylene composites

    Directory of Open Access Journals (Sweden)

    A. Kmetty

    2013-02-01

    Full Text Available In this work, all-polypropylene composites (all-PP composites were manufactured by injection moulding. Prior to injection moulding, pre-impregnated pellets were prepared by a three-step process (filament winding, compression moulding and pelletizing. A highly oriented polypropylene multifilament was used as the reinforcement material, and a random polypropylene copolymer (with ethylene was used as the matrix material. Plaque specimens were injection moulded from the pellets with either a film gate or a fan gate. The compression moulded sheets and injection moulding plaques were characterised by shrinkage tests, static tensile tests, dynamic mechanical analysis and falling weight impact tests; the fibre distribution and fibre/matrix adhesion were analysed with light microscopy and scanning electron microscopy. The results showed that with increasing fibre content, both the yield stress and the perforation energy significantly increased. Of the two types of gates used, the fan gate caused the mechanical properties of the plaque specimens to become more homogeneous (i.e., the differences in behaviour parallel and perpendicular to the flow direction became negligible.

  14. Degradation of Polypropylene Membranes Applied in Membrane Distillation Crystallizer

    Directory of Open Access Journals (Sweden)

    Marek Gryta

    2016-03-01

    Full Text Available The studies on the resistance to degradation of capillary polypropylene membranes assembled in a membrane crystallizer were performed. The supersaturation state of salt was achieved by evaporation of water from the NaCl saturated solutions using membrane distillation process. A high feed temperature (363 K was used in order to enhance the degradation effects and to shorten the test times. Salt crystallization was carried out by the application of batch or fluidized bed crystallizer. A significant membrane scaling was observed regardless of the method of realized crystallization. The SEM-EDS, DSC, and FTIR methods were used for investigations of polypropylene degradation. The salt crystallization onto the membrane surface accelerated polypropylene degradation. Due to a polymer degradation, the presence of carbonyl groups on the membranes’ surface was identified. Besides the changes in the chemical structure a significant mechanical damage of the membranes, mainly caused by the internal scaling, was also found. As a result, the membranes were severely damaged after 150 h of process operation. A high level of salt rejection was maintained despite damage to the external membrane surface.

  15. Property Relationship in Organosilanes and Nanotubes Filled Polypropylene Hybrid Composites.

    Science.gov (United States)

    Monsiváis-Barrón, Alejandra J; Bonilla-Rios, Jaime; Sánchez-Fernández, Antonio

    2014-10-20

    Polypropylene composites with different filler contents were prepared by creating a masterbatch containing 3 wt%. filler. A variety of silanol groups were used to synthetized three compounds in different media trough a sol-gel process with acetic acid, formic acid and ammonium hydroxide as catalysts. Besides, four different nanotubular fillers were also used to analyze their behavior and compare it with the effect caused by the silanol groups. These tubular structures comprise: unmodified halloysite, carbon nanotubes and functionalized halloysite and carbon nanotubes. Morphological characterization in SEM and STEM/TEM showed dispersion in the polypropylene matrix. According to TGA and DSC measurements thermal behavior remain similar for all the composites. Mechanical test in tension demonstrate that modulus of the composites increases for all samples with a major impact for materials containing silanol groups synthetized in formic acid. Rheological measurements show a significantly increment in viscosity for samples containing unmodified and modified carbon nanotubes. No difference was found for samples containing silanol groups and halloysite when compared to neat polypropylene. Finally, the oxygen transmission rate increased for all samples showing high barrier properties only for samples containing natural and functionalized halloysite nanotubes.

  16. Stabilization of polypropylene, polypropylene blends with poly (styrene-b-(ethylene-co-butylene)-b-styrene) under irradiation: A comparative investigation

    International Nuclear Information System (INIS)

    Luan Shifang; Yang Huawei; Shi Hengchong; Zhao Jie; Wang Jianwei; Yin Jinghua

    2011-01-01

    The aim of this paper is to investigate the stabilization of polypropylene in the poly (styrene-b-(ethylene-co-butylene)-b-styrene) (SEBS)/polypropylene (PP) blends under irradiation with respect to PP. The PP films, SEBS/PP films were subjected to electron beam irradiation and characterized by wide angle X-ray diffraction (WAXD), differential scanning calorimetry (DSC), gel permeation chromatography (GPC), and dynamic mechanical thermal analysis (DMTA). It demonstrated that upon irradiation, the molecular weight of PP had a pronounced decrease due to the major chain scission, and the minor chain cross-linking or chain branching occurred at the higher irradiation dose. Stabilization of PP was improved in the presence of SEBS, exhibiting an enhanced irradiation resistance.

  17. Stabilization of polypropylene, polypropylene blends with poly (styrene-b-(ethylene-co-butylene)-b-styrene) under irradiation: A comparative investigation

    Energy Technology Data Exchange (ETDEWEB)

    Luan Shifang; Yang Huawei; Shi Hengchong; Zhao Jie [State Key Laboratory of Polymer Physics and Chemistry, Changchun Institute of Applied Chemistry, Chinese Academy of Sciences, Changchun 130022 (China); Wang Jianwei [Shandong Weigao Group Medical Polymer Company Limited, Weihai 264209 (China); Yin Jinghua, E-mail: yinjh@ciac.jl.c [State Key Laboratory of Polymer Physics and Chemistry, Changchun Institute of Applied Chemistry, Chinese Academy of Sciences, Changchun 130022 (China)

    2011-01-15

    The aim of this paper is to investigate the stabilization of polypropylene in the poly (styrene-b-(ethylene-co-butylene)-b-styrene) (SEBS)/polypropylene (PP) blends under irradiation with respect to PP. The PP films, SEBS/PP films were subjected to electron beam irradiation and characterized by wide angle X-ray diffraction (WAXD), differential scanning calorimetry (DSC), gel permeation chromatography (GPC), and dynamic mechanical thermal analysis (DMTA). It demonstrated that upon irradiation, the molecular weight of PP had a pronounced decrease due to the major chain scission, and the minor chain cross-linking or chain branching occurred at the higher irradiation dose. Stabilization of PP was improved in the presence of SEBS, exhibiting an enhanced irradiation resistance.

  18. Effect of fibre treatment using fluorosilane on Sansevieria Trifasciata/Polypropylene composite

    Science.gov (United States)

    Aref, Yanzur Mohd; Baharum, Azizah

    2018-04-01

    Recently, there is an increasing interest in the development of wood-plastic composites (WPC) due to their advantages such as wide availability, low cost, environment friendliness and sustainability. However, some major factors limiting the large scales production of WPC including the tendency of natural fibres to absorb water and the poor compatibility between fibre and matrix. In this study, we investigated the effectiveness of natural fibre treatment using fluorosilane in imparting hydrophobicity to the polypropylene (PP) matrix composite reinforced with Sansevieria Trifasciata (ST) fibres. ST fibres are subjected to silane treatment with 1H,1H,2H,2H-perfluorooctyltriethoxsysilane (POTS) at 1, 3 and 5% for a period of 2 hours. Influence of POTS treatment on the physical and mechanical properties of composites was studied to determine the optimum condition of silane treatment. The water contact angle (WCA) of WPC increased after POTS treatment where the highest value of 115° was shown by 3% POTS treated ST/PP composite. Based on mechanical properties results, incorporation of POTS treated ST fibre improves the mechanical properties with the enhancement of flexural and impact strength. The treatment with 3% POTS revealed statistically higher flexural strength and modulus compared to 1 and 5%. The water absorption test of ST/PP composites also gives the best result for 3% POTS treatment with 20.90% water uptake.

  19. Effect of carboxylic acids as compatibilizer agent on mechanical properties of thermoplastic starch and polypropylene blends.

    Science.gov (United States)

    Martins, Andréa Bercini; Santana, Ruth Marlene Campomanes

    2016-01-01

    In this work, polypropylene/thermoplastic starch (PP/TPS) blends were prepared as an alternative material to use in disposable packaging, reducing the negative polymeric environmental impact. Unfortunately, this material displays morphological characteristics typical of immiscible polymer blends and a compatibilizer agent is needed. Three different carboxyl acids: myristic (C14), palmitic (C16) and stearic acids (C18) were used as natural compatibilizer agent (NCA). The effects of NCA on the mechanical, physical, thermal and morphological properties of PP/TPS blends were investigated and compared against PP/TPS with and without PP-grafted maleic anhydride (PPgMA). When compared to PP/TPS, blends with C18, PPgMA and C14 presented an improvement of 25, 22 and 17% in tensile strength at break and of 180, 194 and 259% in elongation at break, respectively. The highest increase, 54%, in the impact strength was achieved with C14 incorporation. Improvements could be seen, through scanning electron microscopy (SEM) images, in the compatibility between the immiscible components by acids incorporation. These results showed that carboxylic acids, specifically C14, could be used as compatibilizer agent and could substitute PPgMA. Copyright © 2015 Elsevier Ltd. All rights reserved.

  20. Isothermal crystallization kinetics of isotactic polypropylene with inorganic fullerene-like WS2 nanoparticles

    International Nuclear Information System (INIS)

    Naffakh, Mohammed; Martin, Zulima; Marco, Carlos; Gomez, Marian A.; Jimenez, Ignacio

    2008-01-01

    Nanometric-sized inorganic fullerene-like tungsten disulfide particles (IF-WS 2 ) were used to produce new isotactic polypropylene (iPP) nanocomposites. A remarkable increase of the crystallization rate of iPP in the nanocomposites was observed by DSC and X-ray diffraction techniques using synchrotron radiation. This fact was related to the high nucleation efficiency of IF-WS 2 nanoparticles on the α-form crystals of iPP. Other parameters such as the Avrami exponent, the equilibrium melting temperature, and the fold surface free energy of crystallization of iPP chains in the nanocomposites were obtained from the calorimetric data in order to determine the effect of the nanoparticles on them. A decrease in the fold surface free energy was calculated with increasing IF-WS 2 content

  1. Radiation-chemical synthesis of polypropylene fabrics with sulfonic acid functional groups

    Energy Technology Data Exchange (ETDEWEB)

    Cho, Hyun Kug; Park, Jung Soo; Han, Do Hung, E-mail: dhhan@yumail.ac.kr; Bondar, Iuliia, E-mail: juliavad@yahoo.co

    2011-04-01

    A sorption-active material carrying sulfonic acid groups was synthesized by the radiation-induced graft polymerization of styrene monomer onto the surface of non-woven polypropylene fabric, followed by sulfonation of the grafted polystyrene chains. The effect of the main experimental parameters (absorbed dose, monomer concentration, reaction time) on the styrene degree of grafting was investigated. The sulfonation process with 5% chlorosulfonic acid at room temperature was investigated in detail and the optimal sulfonation conditions for the samples with a medium degree of grafting (70-140%) were determined. Densities of 3.5-5 meq/g were obtained by applying those sorption-active PP fabrics with a sulfonic acid group.

  2. Thermal degradation behaviors of polyethylene and polypropylene. Part I: Pyrolysis kinetics and mechanisms

    International Nuclear Information System (INIS)

    Aboulkas, A.; El harfi, K.; El Bouadili, A.

    2010-01-01

    Study of the decomposition kinetics is an important tool for the development of polymer recycling in industrial scale. In this work, the activation energy and the reaction model of the pyrolysis of high density polyethylene (HDPE), low density polyethylene (LDPE) and polypropylene (PP) have been estimated from non-isothermal kinetic results. Firstly, the activation energy values obtained by Friedman, Kissinger-Akahira-Sunose and Flynn-Wall-Ozawa isoconversional methods, are 238-247 kJ/mol for HDPE, 215-221 kJ/mol for LDPE and 179-188 kJ/mol for PP. Secondly, the appropriate conversion model of the process was determined by Coats-Redfern and Criado methods. The pyrolysis reaction models of HDPE and LDPE are accounted for by 'Contracting Sphere' model, whereas that of PP by 'Contracting Cylinder' model.

  3. Grafting of acrylic acid on etched latent tracks induced by swift heavy ions on polypropylene films

    International Nuclear Information System (INIS)

    Mazzei, R.; Fernandez, A.; Garcia Bermudez, G.; Torres, A.; Gutierrez, M.C.; Magni, M.; Celma, G.; Tadey, D.

    2008-01-01

    In order to continue with a systematic study that include different polymers and monomers, the residual active sites produced by heavy ion beams, that remain after the etching process, were used to start the grafting process. To produce tracks, foils of polypropylene (PP) were irradiated with 208 Pb of 25.62 MeV/n. Then, these were etched and grafted with acrylic acid (AA) monomers. Experimental curves of grafting yield as a function of grafting time with the etching time as a parameter were measured. Also, the grating yield as a function of the fluence and etching time was obtained. In addition, the permeation of solutions, with different pH, through PP grafted foils was measured

  4. Mechanical Properties and Weathering Behavior of Polypropylene-Hemp Shives Composites

    Directory of Open Access Journals (Sweden)

    Marcel Ionel Popa

    2013-01-01

    Full Text Available This paper presents the obtaining and the characterization of composites with polypropylene matrix and hemp shives as filler in different ratios and containing poly(propylene-co maleic anhydride (MAH-PP 3% wt as compatibility agent. The weathering behavior of the composite enclosing 60% hemp shives, performed after the exposure to UV radiations at different exposure times, was evaluated. The changes in the chemical and morphological structures were investigated by FT-IR and RAMAN spectroscopies and AFM microscopy. The mechanical characteristics of the composites were determined before and after an artificial aging process, and they are within the limits of the values reported for polyolefin-based composites and materials with natural fillers. During the accelerated weathering process, the correlation between the chemical degradation of the main components of the composite and the modification of the mechanical properties after the process of aging has been observed.

  5. A novel thermoplastic elastomer based on dynamically vulcanized polypropylene/acrylic rubber blends

    Directory of Open Access Journals (Sweden)

    2008-08-01

    Full Text Available Thermoplastic elastomer based on polypropylene (PP and acrylic rubber (ACM was investigated, with special attention on the compatibilization and dynamic vulcanization. ACM component contains chlorine and carboxyl groups along the backbone, which act as center for the curing and reactive compatibilization. The last event was carried out by adding a combination of maleic anhydride-modified PP (PP-g-MA and triethylene tetramine (TETA, which act as interfacial agents between PP and ACM phases. The effectiveness of the compatibilization was suggested from mixing torque and viscosity, determined from rheological measurements. Outstanding mechanical performance, especially elongation at break, and better tensile set (lower values were obtained with the compatibilization. The dynamic vulcanization also resulted in good mechanical properties for compatibilized blends, but the performance was inferior to that observed for non vulcanized blends. The effect of the compatibilization and/or dynamic vulcanization on the dynamic mechanical, thermal, morphological and stress relaxation properties was investigated.

  6. Reinforced poly(propylene oxide): a very soft and extensible dielectric electroactive polymer

    International Nuclear Information System (INIS)

    Goswami, K; Mazurek, P; Daugaard, A E; Skov, A L; Galantini, F; Gallone, G

    2013-01-01

    Poly(propylene oxide) (PPO), a novel soft elastomeric material, and its composites were investigated as a new dielectric electroactive polymer (EAP). The PPO networks were obtained from thiol-ene chemistry by photochemical crosslinking of α,ω-diallyl PPO with a tetra-functional thiol. The elastomer was reinforced with hexamethylenedisilazane treated fumed silica to improve the mechanical properties of PPO. The mechanical properties of PPO and composites thereof were investigated by shear rheology and stress–strain measurements. It was found that incorporation of silica particles improved the stability of the otherwise mechanically weak pure PPO network. Dielectric spectroscopy revealed high relative dielectric permittivity of PPO at 10 3 Hz of 5.6. The relative permittivity was decreased slightly upon addition of fillers, but remained higher than the commonly used acrylic EAP material VHB4910. The electromechanical actuation performance of both PPO and its composites showed properties as good as VHB4910 and a lower viscous loss. (paper)

  7. Reinforced poly(propylene oxide)- a very soft and extensible dielectric electroactive polymer

    DEFF Research Database (Denmark)

    Goswami, Kaustav; Galantini, F.; Mazurek, Piotr Stanislaw

    2013-01-01

    Poly(propylene oxide) (PPO), a novel soft elastomeric material, and its composites were investigated as a new dielectric electroactive polymer (EAP). The PPO networks were obtained from thiol-ene chemistry by photochemical crosslinking of ,!-diallyl PPO with a tetra-functional thiol. The elastomer...... was reinforced with hexamethylenedisilazane treated fumed silica to improve the mechanical properties of PPO. The mechanical properties of PPO and composites thereof were investigated by shear rheology and stress–strain measurements. It was found that incorporation of silica particles improved the stability...... of the otherwise mechanically weak pure PPO network. Dielectric spectroscopy revealed high relative dielectric permittivity of PPO at 103 Hz of 5.6. The relative permittivity was decreased slightly upon addition of fillers, but remained higher than the commonly used acrylic EAP material VHB4910...

  8. Adsorption of chromium (Vi) on radiation grafted N,N-dimethylaminoethylmethacrylate onto polypropylene, from aqueous solutions

    Energy Technology Data Exchange (ETDEWEB)

    Burillo, G. [UNAM, Instituto de Ciencias Nucleares, Departamento de Quimica, Ciudad Universitaria, 04510 Mexico D. F. (Mexico); Serrano G, J.; Bonifacio M, J., E-mail: juan.serrano@inin.gob.mx [ININ, Carretera Mexico-Toluca s/n, 52750 Ocoyoacac, Estado de Mexico (Mexico)

    2013-08-01

    Polypropylene (Pp) grafted with dimethylaminoethylmethacrylate (DMAEMA), was prepared by irradiation with a {sup 60}Co {gamma} source. The obtained Pp-g-DMAEMA was used to study the Cr(Vi) ion adsorption as a function of contact time, initial ph, initial concentration of metal ion and temperature. Chromium adsorption data on Pp-g-DMAEMA at various initial concentration fit well the Freundlich and Langmuir isotherms. The maximum adsorption capacity (a{sub max}) was found to be 0.3103 x 0{sup -4} mol g{sup -1}. The thermodynamic parameters {Delta}H{sup 0}, {Delta}G{sup 0} and {Delta}S{sup 0} were estimated showing the adsorption process to be exothermic and spontaneous. (Author)

  9. Effect of processing conditions on the mechanical properties of polypropylene/bentonite nano composites

    International Nuclear Information System (INIS)

    Alves, Tatianny S.; Cipriano, Pamela B.; Lira, Vanize F.; Canedo, Eduardo L.; Carvalho, Laura H. de

    2009-01-01

    This work dealt with the effect of processing conditions on the properties of polypropylene/bentonite compounds, using natural clay and an organoclay prepared with hexadecyl trimethyl ammonium bromide. Compounds with 1% clay were prepared by melt compounding in a single-screw extruder and in a counter-rotating twin-screw extruder, and characterized x-ray diffraction; tensile and impact mechanical tests. X ray diffraction results on clays and compounds show that the surfactant was incorporated within the clay galleries and that intercalated nano composites were obtained with the organoclay processed in either the single or the twin-screw extruder. The data also indicated that, without the addition of a compatibilizer, no significant variation of mechanical properties was observed for the composites processed in either extruder. (author)

  10. Conversion of Mixed Plastic Wastes (High Density Polyethylene and Polypropylene) into Liquid Fuel

    International Nuclear Information System (INIS)

    Chaw Su Su Hmwe; Tint Tint Kywe; Moe Moe Kyaw

    2010-12-01

    In this study, mixed plastic wastes were converted into liquid fuels. Mixed plastic wastes used were high density polyethylene (HDPE) and polypropylene (PP). The pyrolysis of mixed plastic waste to liquid fuel was carried out with and without prepared zeolite catalyst.The catalyst was characterized by X-ray Diffraction (XRD). This catalyst was pre-treated for activation. The experiments were carried out at temperature range of 350-410C.Physical properties (density, kinematic, viscosity,refractive index)of prepared liquid fuel samples were measured. From this study, yields of liquid fuel and gas fuel were found to be 41-64% and 15-35% respectively. As for by products, char was obtained as the yield percentages from 9 to 14% and wax (yield% - 1 to 14) was formed during pyrolysis.

  11. The effect of organoclay type on morphology and mechanical properties of polypropylene films: comparative study

    International Nuclear Information System (INIS)

    Gama, D.B.; Calado, J.F.; Duarte, I.S.; Silva, S.M.L.; Andrade, D.L.A.C.S.

    2012-01-01

    This paper aims to compare the effect of the type of organoclay on morphological and mechanical properties of polypropylene films. Thus, were employed two organobentonite synthesized by NanoPol/UFCG (APOC and APOCF) and a organo montmorillonite Cloisite 20A (C20A) from Southern Clay Products (Texas/USA). The PP films and the PP/organoclay hybrids were prepared in a ChillRoll extruder - 16 AX Plastics and characterized by X-ray diffraction and mechanical properties. The results indicate that the incorporation of organobentonite (APOC and APOCF) and organo montmorillonite (C20A) resulted in the formation of PP nanocomposites with predominantly intercalated morphologies. Also indicate that the mechanical behavior of the films obtained with the three clays (APOC APOCF and C20A) was similar suggesting that the organobentonite, modified with national technology, raw material of low cost when compared to commercial organo montmorillonite, can be a viable alternative in the preparation of PP films. (author)

  12. [Quantification of Wood Flour and Polypropylene in Chinese Fir/Polypropylene Composites by FTIR].

    Science.gov (United States)

    Lao, Wan-li; Li, Gai-yun; Zhou, Qun; Qin, Te-fu

    2015-06-01

    The ratio of wood and plastic in Wood Plastic Composites (WPCss) influences quality and price, but traditional thermochemical methods cannot rapidly and accurately quantify the ratio of wood/PP in WPCss. This paper was addressed to investigate the feasibility of quantifying the wood flour content and plastic content in WPCss by Fourier Transform Infrared (FTIR) spectroscopy. With Chinese fir, polypropylene (PP) and other additives as raw materials, 13 WPCs samples with different wood flour contents, ranging from 9.8% to 61.5%, were prepared by modifying wood flour, mixing materials and extrusion pelletizing. The samples were analyzed by FTIR with the KBr pellets technique. The absorption peaks of WPCss at 1059, 1 033 and 1 740 cm(-1) are considered as characteristic of Chinese fir, and the absorption peaks at 1 377, 2 839 and 841 cm(-1) are typical of PP by comparing the spectra of WPCss with that of Chinese fir, PP and other additives. The relationship between the wood flour content, PP content in WPCss and their characteristic IR peaks height ratio was established. The results show that there is a strong linear correlation between the wood flour content in WPCss and I1 059/l 1 377/I1 033, /I1377, R2 are 0.992 and 0.993 respectively; there is a high linear correlation between the PP content in WPCss and I1 377/I1 740, I2 839 /I1 740 R2 are 0.985 and 0.981, respectively. Quantitative methods of the wood flour content and PP content in WPCss by FTIR were developed, the predictive equations of the wood flour content in WPCss are y = 53.297x-9. 107 and y = 55.922x-10.238, the predictive equations of the PP content in WPCss are y = 6.828 5x+5.403 6 and y = 8.719 7x+3.295 8. The results of the accuracy test and precision test show that the method has strong repeatability and high accuracy. The average prediction relative deviations of the wood flour content and PP content in WPCss are about 5%. The prediction accuracy has been improved remarkably, compared to

  13. Growth of ZnO nanowires on polypropylene membrane surface—Characterization and reactivity

    Energy Technology Data Exchange (ETDEWEB)

    Bojarska, Marta, E-mail: m.bojarska@ichip.pw.edu.pl [Warsaw University of Technology, Faculty of Chemical and Process Engineering, Waryńskiego 1, 00-645 Warsaw (Poland); Lehrstuhl für Technische Chemie II, Universität Duisburg-Essen, Essen 45117 (Germany); Nowak, Bartosz, E-mail: novakbartosz@gmail.com [Warsaw University of Technology, Faculty of Chemical and Process Engineering, Waryńskiego 1, 00-645 Warsaw (Poland); Skowroński, Jarosław, E-mail: jaroslaw.skowronski@itee.radom.pl [Institute for Sustainable Technologies—National Research Institute, Pułaskiego 6/10, 26-600 Radom (Poland); Piątkiewicz, Wojciech, E-mail: w.piatkiewicz@polymemtech.com [Institute for Sustainable Technologies—National Research Institute, Pułaskiego 6/10, 26-600 Radom (Poland); PolymemTech Sp. z o.o., al. Niepodległości 118/90, 02-577 Warsaw (Poland); Gradoń, Leon, E-mail: l.gradon@ichip.pw.edu.pl [Warsaw University of Technology, Faculty of Chemical and Process Engineering, Waryńskiego 1, 00-645 Warsaw (Poland)

    2017-01-01

    Highlights: • ZnO nanowires were grown on a polypropylene microfiltration capillary membrane. • Plasma treatment was used for membrane activation and hydrophilization. • The photocatalytic/antibacterial properties were studied upon light irradiation. • PP/ZnO nanowires membrane show good photocatalytic and antibacterial activity. • We report a new method for obtaining reactive membranes with ZnO nanowires. - Abstract: Need for a new membrane is clearly visible in recent studies, mostly due to the fouling phenomenon. Authors, focused on problem of biofouling caused by microorganisms that are present in water environment. An attempt to form a new membrane with zinc oxide (ZnO) nanowires was made; where plasma treatment was used as a first step of modification followed by chemical bath deposition. Such membrane will exhibit additional reactive properties. ZnO, because of its antibacterial and photocatalytic properties, is more and more often used in commercial applications. The authors used SEM imaging, measurement of the contact angle, XRD and the FT–IR analysis for membrane characterization. Amount of ZnO deposited on membrane surface was also investigated by dithizone method. Photocatalytic properties of such membranes were examined through methylene blue and humic acid degradation in laboratory scale modules with LEDs as either: wide range white or UV light source. Antibacterial and antifouling properties of polypropylene membranes modified with ZnO nanowires were examined through a series of tests involving microorganisms: model gram-positive and −negative bacteria. The obtained results showed that it is possible to modify the membrane surface in such a way, that additional reactive properties will be given. Thus, not only did the membrane become a physical barrier, but also turned out to be a reactive one.

  14. Analysis physical properties of composites polymer from cocofiber and polypropylene plastic waste with maleic anhydrate as crosslinking agent

    Science.gov (United States)

    Pelita, E.; Hidayani, T. R.; Akbar, A.

    2017-07-01

    This research was conducted with the aim to produce composites polymer with polypropylene plastic waste materials and cocofiber which aims to produce wood replacement material in the home furnishings industry. This research was conducted with several stages. The first stage is the process of soaking coco fiber with detergent to remove oil and 2% NaOH. The second stage is to combine the polypropylene plastic waste with cocofiber is a chemical bond, modification by adding maleic anhydride as a crosslinking agent and benzoyl peroxide as an initiator each as much as 1%. Mixing materials done by reflux method using xylene solvent. In this study, carried out a wide range of weight variation of coco fiber are added to the 10, 20, 30, 40 and 50%. The third stage is a polymer composite molding process using hot press at a temperature of 158°C. The results of polymer composites Showed optimum condition on the addition of 40% cocofiber with supple tensile strength value of 90.800 kgf /cm2 and value of elongation break at 3.6726 x 104 (kgf/cm2), melting point at 160.02°C, burning point 463.43°C, residue of TGA is 19%, the density of 0.84 g/mL. From these data, conclude that the resulting polymer composites meet the SNI 03-2105-2006 about ordinary composite polymer and polymer composite structural type 8 regular types from 17.5 to 10.5.

  15. Calcium carbonate interaction analysis in polypropylene compounds and their impact on the formation of beta crystalline phase of this polymer

    International Nuclear Information System (INIS)

    Sakahara, Rogerio M.; Hui, Wang S.

    2011-01-01

    The insertion of calcium carbonate (CaCO 3 ) in polypropylene compound is a thoroughly known technique widely studied in the academic area and in the industry. Its wide application is due, mainly, to increase mechanical properties with low manufacturing cost. These improvements in this polymer make it more versatile and competitive compared to other expensive polymers. In this study, the incorporation of four types of CaCO3 from the same manufacturer were compared and the focus was on the size of this mineral filler. Furthermore, it was analyzed the interaction of graphitized polypropylene with maleic anhydride (PP-g-MA) in the same samples. All these samples were analyzed by WAXS and SEM. The physical properties of tensile strength and impact were also analyzed. It was observed from this study that the smallest CaCO3 produced with PP-g-MA resulted in better physical properties with the formation of a crystalline phase beta, as originally studied by other authors using other raw materials. (author)

  16. Study of alteration in the mechanical properties in hybrid nanocomposite of polypropylene/sisal fibers/mineral clay irradiated with gamma rays

    Energy Technology Data Exchange (ETDEWEB)

    Pereira, Nilson C.; Terence, Mauro C.; Miranda, Leila F., E-mail: nilpereira@mackenzie.com.b [Universidade Presbiteriana Mackenzie, Sao Paulo, SP (Brazil). Escola de Engenharia. Curso de Engenharia de Materiais

    2009-07-01

    A new material class formed with reinforced filler, hybrid of organic and inorganic materials provides the technological development of materials with modified properties. And among great numbers of properties that can be modified by presence of hybrid filler to stand out the tension resistance. Polymer shows behavior of tensions and deformation that are not related of simple form. The answer of this material at mechanicals solicitations depends of structural factors and externals variables. As structural factors can be, for example, molecular weight, ramifications and crosslink. As external variables can be, for example, temperature, time or velocity of deformation, kind of solicitation and others. This work was possible to verify as nanostructures materials behavior, mechanically, after were submitted gamma radiation. This work utilized as polymeric matrix, recycled polypropylene, and as hybrid filler, a mixture of montimorillonite mineral clay with natural sisal fibers. It is known that form to magnify the tensile resistance is increase the number of crosslink of principal chain for gamma radiation. After irradiation the polypropylene was crosslinked structures that are result recombination of radicals formed during process of irradiation. It.s known that radicals formed occur preferentially in the amorphous region of polymer. Considering that polymeric matrix polypropylene, without addition fillers suffer strong structural influence when irradiated, was possible verify change in the extension, tensile strength and also maxim tensile in rupture, when this matrix was incorporated with fillers hybrids. (author)

  17. Study of alteration in the mechanical properties in hybrid nanocomposite of polypropylene/sisal fibers/mineral clay irradiated with gamma rays

    International Nuclear Information System (INIS)

    Pereira, Nilson C.; Terence, Mauro C.; Miranda, Leila F.

    2009-01-01

    A new material class formed with reinforced filler, hybrid of organic and inorganic materials provides the technological development of materials with modified properties. And among great numbers of properties that can be modified by presence of hybrid filler to stand out the tension resistance. Polymer shows behavior of tensions and deformation that are not related of simple form. The answer of this material at mechanicals solicitations depends of structural factors and externals variables. As structural factors can be, for example, molecular weight, ramifications and crosslink. As external variables can be, for example, temperature, time or velocity of deformation, kind of solicitation and others. This work was possible to verify as nanostructures materials behavior, mechanically, after were submitted gamma radiation. This work utilized as polymeric matrix, recycled polypropylene, and as hybrid filler, a mixture of montimorillonite mineral clay with natural sisal fibers. It is known that form to magnify the tensile resistance is increase the number of crosslink of principal chain for gamma radiation. After irradiation the polypropylene was crosslinked structures that are result recombination of radicals formed during process of irradiation. It.s known that radicals formed occur preferentially in the amorphous region of polymer. Considering that polymeric matrix polypropylene, without addition fillers suffer strong structural influence when irradiated, was possible verify change in the extension, tensile strength and also maxim tensile in rupture, when this matrix was incorporated with fillers hybrids. (author)

  18. The effect of impact modifier and of nucleating agent on the radiation tolerance of polypropylene

    Energy Technology Data Exchange (ETDEWEB)

    Liu Dongyuan (Beijing Normal Univ., BJ (China)); Czvikovszky, T.; Dobo, J.; Somogyi, A. (Research Inst. for the Plastics Industry, Budapest (Hungary))

    1990-01-01

    The effect of two types of additives was investigated with respect to the oxidative post-irradiation stability of polypropylene: SBS thermoplastic rubbers as impact modifiers and benzoic acid as nucleating agent. Testing was performed by ultimate deformation on bending. The thermoplastic rubber additive increased the post-irradiation stability of polypropylene substantially. (author).

  19. The effect of impact modifier and of nucleating agent on the radiation tolerance of polypropylene

    International Nuclear Information System (INIS)

    Liu Dongyuan; Czvikovszky, T.; Dobo, J.; Somogyi, A.

    1990-01-01

    The effect of two types of additives was investigated with respect to the oxidative post-irradiation stability of polypropylene: SBS thermoplastic rubbers as impact modifiers and benzoic acid as nucleating agent. Testing was performed by ultimate deformation on bending. The thermoplastic rubber additive increased the post-irradiation stability of polypropylene substantially. (author)

  20. Modification of low density polyethylene, isostatic polypropylene and their blends by gamma radiation

    International Nuclear Information System (INIS)

    Santos Rosa, D. dos

    1991-01-01

    The effects of the gamma radiation (of a 60 Co source), over low density polyethylene, isostatic polypropylene and their blends of low density polyethylene / polypropylene were studied. The structures modifications were attended by infrared spectrometry (IV), differential scanning calorimeter (DSC), strain-strain measurement, density measurement and scanning electron microscope (SEM). (author)

  1. Use of polypropylene mesh in hernioplasty by Lichtenstein's technique

    International Nuclear Information System (INIS)

    Montejo Sainz, Jesus Enrique; Pisonero Socias, Juan Jose

    2011-01-01

    INTRODUCTION. The aim of present study was to assess the benefit using the prosthesis (polypropylene mesh) in the hernioplasty using the Lichtenstein's technique in the 'Joaquin Albarran' Clinical Surgical Hospital. METHODS. A prospective study (with an interval of 14 months) was conducted in 140 surgical interventions carried out using the Lichtenstein's technique in patients presenting with inguinal hernia. One hundred and ten patients were excluded due to interventions were of ambulatory method. The following data were studied: type of hernia found in the physical examination, age, sex, and race, type of job, intervention's date, and technique used as well as the complications during the immediate postoperative time. Also, the hernia's relapse after operation, surgical complications and tolerance to polypropylene mesh were taking into account. RESULTS. There was predominance of male sex confirming a direct influence among types of jobs requiring a strong physical effort and the appearance of inguinal hernias (63,3 %). There were only three complications: a hematoma and two seromas. There were not relapses and any case of infection, both local and systemic. The use of prophylactic antibiotics showed an appropriate cost-benefit relationship. CONCLUSIONS. The old age, the male sex and a sustained physical effort have a directly proportional relation to appearance of inguinal hernias. The feasibility of Lichtenstein's hernioplasty, the null incidence of hernia relapses and no appearance of complications including the rejection to prosthetic material, favoured the use of polypropylene in this plasty. Authors recommended the use of perioperative prophylactic antibiotic therapy to avoid wound's infection and thus to secure the result of surgical intervention and its durability. (author)

  2. Surface modifications of polypropylene by high energy carbon ions

    International Nuclear Information System (INIS)

    Saha, A.; Chakraborty, V.; Dutta, R.K.; Chintalapudi, S.N.

    2000-01-01

    Polypropylene was irradiated with 12 C ions of 3.6 and 5.4 MeV energies using 3 MV tandem accelerator. The surface modification was investigated by Scanning Electron Microscopy (SEM). Optical changes were monitored by UV-VIS and FTIR spectroscopy. At the lowest ion fluence, only blister formation of various sizes (1-6 μm) was observed. Polymer when irradiated at a fluence of 1x10 14 ions/cm 2 exhibited a network structure. A comparative study on dose dependence of surface and bulk modification has been described. (author)

  3. The method of polymer compositions manufacturing on the base of polypropylene[Radiation processing]; Sposob wytwarzania kompozycji polimerow na bazie polipropylenu

    Energy Technology Data Exchange (ETDEWEB)

    Zimek, Z; Bulhak, Z; Bojarski, J; Stachowicz, W [Warsaw (Poland); Mirkowski, K [Legionowo (Poland)

    1966-06-28

    The method of manufacturing of radiation resistant polymer composition of medical quality have been proposed. The raw material consisted of polypropylene homopolymer with propylene-ethylene copolymer, ethylene-vinyl acetate copolymer and polystyrene suspension have been mixed and extruded during heating at 190-270{sup o}C. Then obtained mixture have been granulated. The material structure with microagglomerates is responsible for elevated radiation resistance of material being destinated for medical devices production and radiosterilization.

  4. Permanent hydrophilic modification of polypropylene and poly(vinyl alcohol) films by vacuum ultraviolet radiation

    Energy Technology Data Exchange (ETDEWEB)

    Belmonte, Guilherme Kretzmann [Instituto de Química, Universidade Federal do Rio Grande do Sul (UFRGS), Avenida Bento Gonçalves 9500, 91501-970 Porto Alegre, RS (Brazil); Charles, German [Centro de Química Aplicada (CEQUIMAP), Facultad de Ciencias Químicas, Unversidad Nacional de Córdoba, Haya de la Torre y Medina Allende, Edificio de Ciencias II, Ciudad Universitaria, Córdoba 5000 (Argentina); Strumia, Miriam Cristina [Departamento de Química Orgánica, Facultad de Ciencias Químicas, Universidad Nacional de Córdoba, IPQA-Conicet, Haya de la Torre y Medina Allende, Edificio de Ciencias II, Ciudad Universitaria, Córdoba 5000 (Argentina); Weibel, Daniel Eduardo, E-mail: danielw@iq.ufrgs.br [Instituto de Química, Universidade Federal do Rio Grande do Sul (UFRGS), Avenida Bento Gonçalves 9500, 91501-970 Porto Alegre, RS (Brazil)

    2016-09-30

    Highlights: • Polypropylene and Poly(vinyl alcohol) were surface modified by vacuum ultraviolet (VUV) irradiation. • The hydrophilicity of the treated films was permanent and resisted aging for several months. • Grafting of styrene monomer was only observed in the VUV irradiated regions. • The obtained results showed the potential in the use of VUV treatment for surface modification and processing of polymers which lack chromophores in the UV region. - Abstract: Polypropylene (PP) and Poly(vinyl alcohol) (PVA) both synthetics polymers but one of them biodegradable, were surface modified by vacuum ultraviolet (VUV) irradiation. After VUV irradiation in an inert nitrogen atmosphere, the films were exposed to oxygen gas. The treated films were characterized by water contact angle measurements (WCA), optical profilometry, FTIR-ATR, XPS, UPS and NEXAFS techniques. PP and PVA VUV-treated films reached superhydrophilic conditions (WCAs <10°) in about 30 min of irradiation under our experimental conditions. It was observed that when the WCAs reached about 35–40° the hydrophilicity was permanent in both polymers. These results contrasted with typical plasma treatments were a rapid hydrophobic recovery with aging time is usually observed. UPS and XPS data showed the presence of new functionalities on the PP and PVA surfaces that were assigned to COO, C=O, C−O and C=C functional groups. Finally, grafting of styrene (ST) as a typical monomer was tested on PP films. It was confirmed that only in the VUV irradiated region an efficient grafting of ST or polymerized ST was found. Outside the irradiated regions no ST grafted was observed. Our results showed the potential use of VUV treatment for surface modification and processing of polymers which lack chromophores in the UV region.

  5. Polypropylene compositional evolution under 3.5 MeV He{sup +} ion irradiation

    Energy Technology Data Exchange (ETDEWEB)

    Abdesselam, M., E-mail: abdesselam_m@yahoo.fr [Faculte de Physique, USTHB, BP32, El Alia, 16111 BEZ (Algeria); Muller, D. [InESS, UMR7163, 23 rue du Loess, BP20, F-67037 Strasbourg Cedex 02 (France); Djebara, M.; Chami, A.C. [Faculte de Physique, USTHB, BP32, El Alia, 16111 BEZ (Algeria); Montgomery, P. [InESS, UMR7163, 23 rue du Loess, BP20, F-67037 Strasbourg Cedex 02 (France)

    2012-05-01

    A helium beam at 3.5 MeV was used to induce damage in thin polypropylene film of 5.1 {mu}m in thickness. The fluence ranges from 2 Multiplication-Sign 10{sup 12} to 3.5 Multiplication-Sign 10{sup 15} cm{sup -2}. The evolution of the atomic composition (C and H) as a function of the fluence was investigated in situ by forward elastic scattering (C({alpha}, {alpha})C) and hydrogen elastic recoil detection (H({alpha}, H){alpha}), respectively. The helium beam was used at the same time for irradiation and analysis. In respect to the high sensitivity of the polypropylene to radiation damage, the beam current was kept at very low intensity of 0.5 nA. The mass loss becomes significant above a fluence of {approx}5 Multiplication-Sign 10{sup 13} He{sup +} cm{sup -2}. The carbon depletion levels off at a fluence of {approx}5 Multiplication-Sign 10{sup 14} He{sup +} cm{sup -2} approximately while hydrogen loss continues to be present along the whole of the studied fluence range. The final carbon and hydrogen losses, at the highest fluence, are around 17% and 48% of their initial contents, respectively. Satisfactory fits to the release curves have been obtained in the framework of the bulk molecular recombination model (BMR). The deduced hydrogen and carbon release cross sections are 7.8 and 65.2 Multiplication-Sign 10{sup -16} cm{sup 2}, respectively. A comparison with our previous measurements of polyethylene terephthalate (PET) film irradiated with 3.7 MeV He{sup +} beam is made.

  6. Polypropylene compositional evolution under 3.5 MeV He+ ion irradiation

    International Nuclear Information System (INIS)

    Abdesselam, M.; Muller, D.; Djebara, M.; Chami, A.C.; Montgomery, P.

    2012-01-01

    A helium beam at 3.5 MeV was used to induce damage in thin polypropylene film of 5.1 μm in thickness. The fluence ranges from 2 × 10 12 to 3.5 × 10 15 cm −2 . The evolution of the atomic composition (C and H) as a function of the fluence was investigated in situ by forward elastic scattering (C(α, α)C) and hydrogen elastic recoil detection (H(α, H)α), respectively. The helium beam was used at the same time for irradiation and analysis. In respect to the high sensitivity of the polypropylene to radiation damage, the beam current was kept at very low intensity of 0.5 nA. The mass loss becomes significant above a fluence of ∼5 × 10 13 He + cm −2 . The carbon depletion levels off at a fluence of ∼5 × 10 14 He + cm −2 approximately while hydrogen loss continues to be present along the whole of the studied fluence range. The final carbon and hydrogen losses, at the highest fluence, are around 17% and 48% of their initial contents, respectively. Satisfactory fits to the release curves have been obtained in the framework of the bulk molecular recombination model (BMR). The deduced hydrogen and carbon release cross sections are 7.8 and 65.2 × 10 −16 cm 2 , respectively. A comparison with our previous measurements of polyethylene terephthalate (PET) film irradiated with 3.7 MeV He + beam is made.

  7. Polypropylene compositional evolution under 3.5 MeV He+ ion irradiation

    Science.gov (United States)

    Abdesselam, M.; Muller, D.; Djebara, M.; Chami, A. C.; Montgomery, P.

    2012-05-01

    A helium beam at 3.5 MeV was used to induce damage in thin polypropylene film of 5.1 μm in thickness. The fluence ranges from 2 × 1012 to 3.5 × 1015 cm-2. The evolution of the atomic composition (C and H) as a function of the fluence was investigated in situ by forward elastic scattering (C(α, α)C) and hydrogen elastic recoil detection (H(α, H)α), respectively. The helium beam was used at the same time for irradiation and analysis. In respect to the high sensitivity of the polypropylene to radiation damage, the beam current was kept at very low intensity of 0.5 nA. The mass loss becomes significant above a fluence of ˜5 × 1013 He+ cm-2. The carbon depletion levels off at a fluence of ˜5 × 1014 He+ cm-2 approximately while hydrogen loss continues to be present along the whole of the studied fluence range. The final carbon and hydrogen losses, at the highest fluence, are around 17% and 48% of their initial contents, respectively. Satisfactory fits to the release curves have been obtained in the framework of the bulk molecular recombination model (BMR). The deduced hydrogen and carbon release cross sections are 7.8 and 65.2 × 10-16 cm2, respectively. A comparison with our previous measurements of polyethylene terephthalate (PET) film irradiated with 3.7 MeV He+ beam is made.

  8. Functionalization of polypropylene by radiation grafting of acryloyl chloride and sterification with disperse red

    International Nuclear Information System (INIS)

    Bucio, E.; Burillo, G.; Carreon, M.P.; Ogawa, T.

    2002-01-01

    Complete text of publication follows. A practical method for obtaining films containing functional groups on the surface, is the gamma ray-induced grafting of acryloyl or methacryloyl chloride on the films, followed by the reaction of hydroxy or amino groups of the functional compounds. Direct grafting of acrylates or methacrylates with bulky functional groups onto films of polyethylene, polypropylene, polycarbonate, etc, is often encounter difficulty in polymerization of bulky monomers, loss due to homopolymerization, etc. In this work, polypropylene (PP) films were irradiated by gamma rays of Co-60 (Gamma Beam 651 PT source) and grafted with acryloyl chloride; grafting was carried out by direct and phase vapor direct method, at a dose rate of 5.1 kGy/h, different acryloyl concentration on toluene, and doses from 1 to 5 kGy, at room temperature. The unreacted acryloyl chloride and its homopolymer were removed by chloroform extraction. The grafted poly(acryloyl chloride) was then reacted with Disperse Red 1,2-[4-(4-nitrophenylazo)-N-ethylphenylamino] ethanol. The grafted films were characterized by NMR, FTIR-ATR, Visible Spectroscopy, DSC, X-ray diffractometry, SEM, AFM, NMR of solids and Elemental Analysis. Scanning electron micrographs of fractured surfaces indicated that grafting took place not only on the surface of PP film, but the grafted polymer penetrated into the PP films. Thermochromic properties of the films were observed by FTIR and UV-VIS spectrophotometers at different temperatures. AFM showed depth profiles and average rough for samples with different percentage of graft

  9. Rapid disintegrating tablets of simvastatin dispersions in polyoxyethylene–polypropylene block copolymer for maximized disintegration and dissolution

    Directory of Open Access Journals (Sweden)

    Balata GF

    2016-10-01

    Full Text Available Gehan F Balata,1,2 Ahmad S Zidan,2 Mohamad AS Abourehab,1,3 Ebtessam A Essa4 1Department of Pharmaceutics, Faculty of Pharmacy, Umm Al-Qura University, Makkah, Saudi Arabia; 2Department of Pharmaceutics, Faculty of Pharmacy, Zagazig University, Zagazig, 3Department of Pharmaceutics, Faculty of Pharmacy, El-Minia University, El-Minia, 4Department of Pharmaceutics, Faculty of Pharmacy, Tanta University, Tanta, Egypt Abstract: The objective of this research was to improve the dissolution of simvastatin and to incorporate it in rapid disintegrating tablets (RDTs with an optimized disintegration and dissolution characteristics. Polyoxyethylene–polypropylene block copolymer (poloxamer 188 was employed as a hydrophilic carrier to prepare simvastatin solid dispersions (SDs. Fourier transform infrared spectroscopy, differential scanning calorimetry (DSC and X-ray diffractometry were employed to understand the interaction between the drug and the carrier in the solid state. The results obtained from Fourier transform infrared spectroscopy showed absence of any chemical interaction between the drug and poloxamer. The results of differential scanning calorimetry and X-ray diffractometry confirmed the conversion of simvastatin to distorted crystalline state. The SD of 1:2 w/w drug to carrier ratio showed the highest dissolution; hence, it was incorporated in RDT formulations using a 32 full factorial design and response surface methodology. The initial assessments of RDTs demonstrated an acceptable flow, hardness, and friability to indicate good mechanical strength. The interaction and Pareto charts indicated that percentage of croscarmellose sodium incorporated was the most important factor affecting the disintegration time and dissolution parameter followed by the hardness value and their interaction effect. Compression force showed a superior influence to increase RDT’s porosity and to fasten disintegration rather than swelling action by

  10. The mechanisms of reinforcement of polypropylene by graphene nanoplatelets

    Energy Technology Data Exchange (ETDEWEB)

    Ahmad, Siti Rohana; Xue, Chengzhe; Young, Robert J., E-mail: robert.young@manchester.ac.uk

    2017-02-15

    Highlights: • The thermal stability of the polypropylene is improved significantly with the GNPs. • The melting temperature and degree of crystallinity of the PP are both increased. • The effective Young’s modulus of the GNP reinforcement is 100 GPa. • The same effective Young’s modulus is found from Raman band shifts. - Abstract: A detailed analysis has been undertaken of the mechanisms of reinforcement of polypropylene (PP) by the addition of graphene nanoplatelets (GNP). The PP/GNP nanocomposites were processed by melt mixing followed by injection moulding and microstructure was fully characterized. It was found that the GNPs increased the thermal stability of the PP and aided crystal nucleation. The mechanical properties of the nanocomposites were evaluated using both tensile testing and dynamic mechanical thermal analysis. The addition of GNPs led to a significant increase in the Young’s modulus of the PP, coupled with a decrease in the yield stress and a reduction in the elongation to failure. Stress transfer from the PP matrix to the GNP reinforcement was followed from stress-induced shifts of the 2D Raman band and the effective Young’s modulus of the GNPs in the nanocomposites was found to be about 100 GPa, shown to be consistent with the expected value.

  11. Stability of erythropoietin repackaging in polypropylene syringes for clinical use

    Directory of Open Access Journals (Sweden)

    Angela Marsili

    2017-02-01

    Full Text Available Introduction: Epoetin alfa (Eprex® is a subcutaneous, injectable formulation of short half-life recombinant human erythropoietin (rHuEPO. To current knowledge there are no published studies regarding the stability of rHuEPO once repackaging occurs (r-EPO for clinical trial purposes. Materials and methods: We assessed EPO concentration in Eprex® and r-EPO syringes at 0, 60, 90, and 120 days after repackaging in polypropylene syringes. R-EPO was administered to 56 patients taking part in a clinical trial in Friedreich Ataxia. Serum EPO levels were measured at baseline and 48 h after r-EPO administration. Results: No differences were found between r-EPO and Eprex® syringes, but both globally decreased in total EPO content during storage at 4 °C. Patients receiving r-EPO had similar levels in EPO content as expected from previous trials in Friedreich Ataxia and from pharmacokinetics studies in healthy volunteers. Discussion: We demonstrate that repackaging of EPO does not alter its concentration if compared to the original product (Eprex®. This is true both for repackaging procedures and for the stability in polypropylene tubes. The expiration date of r-EPO can be extended from 1 to 4 months after repackaging, in accordance with pharmacopeia rules.

  12. Acoustic properties of polypropylene composites reinforced with stone groundwood

    Directory of Open Access Journals (Sweden)

    Joan Pere López

    2012-11-01

    Full Text Available Currently, acoustic isolation is one of the problems raised with building construction in Spain. The publication of the Basic Document for the protection against noise of the Technical Building Code has increased the demand of comfort for citizens. This has created the need to seek new composite materials that meet the new required acoustical building codes. In this paper we report the results of the newly developed composites that are able to improve the acoustic isolation of airborne noise. These composites were prepared from polypropylene (PP reinforced with mechanical pulp fibers from softwood (Pinus radiata. Mechanical and acoustical properties of the composites from mechanical pulp (MP and polypropylene (PP have been investigated and compared to fiberglass (FG composites. MP composites had lower tensile properties compared with FG composites, although these properties can be improved by incorporation of a coupling agent. The results of acoustical properties of MP composites were reported and compared with the conventional composites based on fiberglass and gypsum plasterboards. Finally, we suggest the application of MP composites as a light-weight building material to reduce acoustic transmitions.

  13. Morphology and properties of recycled polypropylene/bamboo fibers composites

    International Nuclear Information System (INIS)

    Phuong, Nguyen Tri; Guinault, Alain; Sollogoub, Cyrille; Chuong, Bui

    2011-01-01

    Polypropylene (PP) is among the most widely used thermoplastics in many industrial fields. However, like other recycled polymers, its properties usually decrease after recycling process and sometimes are degraded to poor properties level for direct re-employment. The recycled products, in general, need to be reinforced to have competitive properties. Short bamboo fibers (BF) have been added in a recycled PP (RPP) with and without compatibilizer type maleic anhydride polypropylene (MAPP). Several properties of composite materials, such as helium gas permeability and mechanical properties before and after ageing in water, were examined. The effects of bamboo fiber content and fiber chemical treatment have been also investigated. We showed that the helium permeability increases if fiber content is higher than 30% because of a poor adhesion between untreated bamboo fiber and polymer matrix. The composites reinforced by acetylated bamboo fibers show better helium permeability due to grafting of acetyl groups onto cellulose fibers surface and thus improves compatibility between bamboo fibers and matrix, which has been shown by microscopic observations. Besides, mechanical properties of composite decrease with ageing in water but the effect is less pronounced with low bamboo fiber content.

  14. Chemical modification of polypropylene induced by high energy carbon ions

    Energy Technology Data Exchange (ETDEWEB)

    Saha, A.; Chakraborty, V.; Chintalapudi, S.N. E-mail: snc@gamma.iuc.res.in

    2000-06-01

    Polypropylene was irradiated with {sup 12}C{sup +} ions of 3.6 and 5.4 MeV energy using 3 MV Pelletron. The spectral changes owing to ion bombardment were investigated by UV-VIS and Fourier-transform infrared (FTIR) spectroscopy. A gradual increase in absorbance was observed around visible and near visible region with increase in fluence of bombarding ions. The difference absorption spectra show formation of chromophoric groups with wavelength maximum near 380 nm at lower fluence, but at high fluence a shift in peak is observed. The chromophoric groups are likely to be the extended conjugated polyene system and the red shift in peak position at high fluence may be attributed to the greater degree of conjugation. The formation of unsaturated linkage is confirmed by the FTIR spectra with observed stretching band around 1650 cm{sup -1} and its intensity was found to increase with increase in ion fluence studied. The gases (in the range 2-80 amu) which were evolved due to interaction of polypropylene with {sup 12}C{sup +} ions were measured with Residual Gas Analyzer (RGA). A large number of gaseous components were detected. This shows that polymer chains break into some smaller fragments which concomitantly leads to extended conjugation.

  15. Effect of Reinforcement of Hydrophobic Grade Banana (Musa ornata Bark Fiber on the Physicomechanical Properties of Isotactic Polypropylene

    Directory of Open Access Journals (Sweden)

    Md. Mamunur Rashid

    2016-01-01

    Full Text Available This research studied the physicomechanical as well as morphological properties of alkali treated (NaOH and KMnO4 and untreated banana bark fiber (BBF reinforced polypropylene composites. A detailed structural and morphological characterization was performed using Fourier transform infrared spectroscopy (FTIR, scanning electron microscopy (SEM, and mechanical properties testing (tensile strength, flexural strength, and microhardness. Chemical treatments improved the hydrophobic property of the fiber and it is found to be better for KMnO4 treatment. Composites with 0, 5, 10, and 15 wt.% loadings were then compared for water uptake studies and revealed that KMnO4 treated fiber composites absorb less water compared to others. KMnO4 treatment with 15% fiber loading improved the tensile strength, flexural strength, and microhardness of the composites compared to raw and NaOH treated fiber loadings. TGA analysis also shows onset temperature at 400~500°C that is associated with the decomposition of the banana fibers constituents including lignin, cellulose, and hemicelluloses which suggests better thermomechanical stability. All of the values suggest that 15% KMnO4 treated banana bark fiber (BBF/PP composites were found to be better than those of the raw and NaOH treated ones.

  16. Production of sorption-active polypropylene fibers by radiation-induced grafting of glycidyl methacrylate as a precursor monomer

    International Nuclear Information System (INIS)

    Bondar, Yu.V.; Kim, H.J.; Lim, Y.J.

    2006-01-01

    The design and development of sorption-active natural and synthetic polymer fibers and textile materials is of great scientific and practical interest. The advantages of that type of polymeric adsorbents, as their highly developed specific surface, excellent ion-exchange and adsorption parameters and ease of their use especially under continuous conditions, allow them to find a great application in the chemical, biomedical, ecological and industrial fields. To obtain functional polymer materials with the desired performance, the non-active polymer surface have to be modified. Among different innovative techniques used for the introduction of graft chains, the radiation-chemical method of initiation has some economical and ecological preferences over others. It allows to introduce into inert polymeric matrix chains of a monomer already containing a desirable functional group, or to graft chains of a precursor-monomer and subsequently its chemical modification to form required functional groups. At present an epoxy-group containing monomer, glycidyl methacrylate (GMA), is successfully used as a precursor-monomer for production of polymeric adsorbents of variety applications on the base of membranes, films, fibers and fabrics. Two types of sorption-active polypropylene fiber carrying strong-acid sulfonate groups and amino groups have been synthesized by radiation-induced graft polymerization of GMA, with subsequent chemical modification of the epoxy groups of poly-GMA graft chains. The effect of various polymerization parameters on the GMA grafting degree was investigated in detail. The epoxy ring-opening of poly-GMA graft chains with introduction of strong-acid sulfonate groups was carried out with sodium hydrogen sulfite in water-dimethylformamide solution at 70 deg C. The main peculiarities of the sulfonation reaction in depending on the reaction time and GMA grafting degree have been investigated. Amine groups were incorporated by treatment of the GMA

  17. Influence of nonmetals recycled from waste printed circuit boards on flexural properties and fracture behavior of polypropylene composites

    International Nuclear Information System (INIS)

    Zheng Yanhong; Shen Zhigang; Cai Chujiang; Ma Shulin; Xing Yushan

    2009-01-01

    Flexural strength and flexural modulus of the composites can be successfully improved by filling nonmetals recycled from waste printed circuit boards (PCBs) into polypropylene (PP). By using scanning electron microscopy (SEM), the influence of nonmetals on fracture behavior of PP composites is investigated by in situ flexural test. Observation results show that the particles can effectively lead to mass micro cracks instead of the breaking crack. The process of the crack initiation, propagation and fiber breakage dissipate a great amount of energy. As a result, the flexural properties of the composites can be reinforced significantly. Results of the in situ SEM observation and analysis to the dynamic flexural process supply effective test evidence for the reinforcing mechanism of the nonmetals/PP composites on the basis of the energy dissipation theory

  18. Improvement of Thermo-Mechanical Properties of Short Natural Fiber Reinforced Recycled Polypropylene Composites through Double Step Grafting Process

    Science.gov (United States)

    Saputra, O. A.; Rini, K. S.; Susanti, T. D.; Mustofa, R. E.; Prameswari, M. D.; Pramono, E.

    2017-07-01

    This study focused on the effect of a compatibilizer addition, maleic anhydrides (MAH) on mechanical, thermal and water absorption properties of oil palm empty fruit bunches (EFB) fiber reinforced recycled polypropylene (rPP) biocomposites. The double steps grafting process were conducted by incorporated MAH on both rPP and EFB to improve the surface adhesion between these materials, to result in a good mechanical properties as well as biocompatibility to nature. The chemical test was carried out using FTIR (Fourier Transform Infra-Red) spectroscopy technique to evaluated grafting process. The mechanical test was investigated and found that the addition of 10 phr MAH to both rPP and EFB improved mechanical strength of the biocomposites higher than another formulas. In this study, thermal properties of biocomposites also characterized. Water absorption (WA) analysis showed the presence of EFB fiber increased the water uptake of the material.

  19. Evaluation of elevated temperature influence on mechanical properties of a commercial unrefined bagasse fiber-polypropylene composite

    Directory of Open Access Journals (Sweden)

    Foroogh Dastoorian

    2014-11-01

    Full Text Available An experimental investigation was conducted to evaluate the effect of elevated temperatures, ranging from room temperature to 80oC, on mechanical characteristics of a commercial bagasse fiber/polypropylene composite. The test results were used to determine the temperature dependencies of the mechanical properties of the studied composite material at temperatures up to 80°C in order to develop temperature adjustment factors for the use in structural applications. The results have shown that as temperature increases, the material become more ductile due to increased plastic deformation gets lower stiffness and fails at higher strains. The resulted adjustment factors were different for each loading mode and the results also have indicated that the influence of elevated temperatures on values of modulus was higher than that on strengths.

  20. Development of advanced antimicrobial and sterilized plasma polypropylene grafted muga (Antheraea assama) silk as suture biomaterial.

    Science.gov (United States)

    Gogoi, Dolly; Choudhury, Arup Jyoti; Chutia, Joyanti; Pal, Arup Ratan; Khan, Mojibur; Choudhury, Manash; Pathak, Pallabi; Das, Gouranga; Patil, Dinkar S

    2014-04-01

    Surface modification of silk fibroin (SF) materials using environmentally friendly and non-hazardous process to tailor them for specific application as biomaterials has drawn a great deal of interest in the field of biomedical research. To further explore this area of research, in this report, polypropylene (PP) grafted muga (Antheraea assama) SF (PP-AASF) suture is developed using plasma treatment and plasma graft polymerization process. For this purpose, AASF is first sterilized in argon (Ar) plasma treatment followed by grafting PP onto its surface. AASF is a non-mulberry variety having superior qualities to mulberry SF and is still unexplored in the context of suture biomaterial. AASF, Ar plasma treated AASF (AASFAr) and PP-AASF are subjected to various characterization techniques for better comparison and the results are attempted to correlate with their observed properties. Excellent mechanical strength, hydrophobicity, antibacterial behavior, and remarkable wound healing activity of PP-AASF over AASF and AASFAr make it a promising candidate for application as sterilized suture biomaterial. Copyright © 2013 Wiley Periodicals, Inc.

  1. Mechanical and thermal properties of polypropylene (PP) composites filled with modified shell waste

    Energy Technology Data Exchange (ETDEWEB)

    Yao, Z.T., E-mail: sxyzt@126.com [College of Materials Science and Environmental Engineering, Hangzhou Dianzi University, Hangzhou 310018 (China); Chen, T. [Department of Ocean Science and Engineering, Zhejiang University, Hangzhou 310058 (China); Li, H.Y. [Zhoushan Ocean Research Institute, Zhejiang University, Zhoushan 316021 (China); Xia, M.S., E-mail: msxia@zju.edu.cn [Department of Ocean Science and Engineering, Zhejiang University, Hangzhou 310058 (China); Ye, Y.; Zheng, H. [Department of Ocean Science and Engineering, Zhejiang University, Hangzhou 310058 (China)

    2013-11-15

    Highlights: • Adding modified shell powder could significantly increase the properties of PP. • The modified shell powder could act as a nucleating agent in PP matrix. • The modified shell powder has a potential to be used as a bio-filler. -- Abstract: Shell waste, with its high content of calcium carbonate (CaCO{sub 3}) plus organic matrix, has a potential to be used as a bio-filler. In this work, shell waste was modified by furfural and then incorporated to reinforce polypropylene (PP). The shell waste and modified powder were characterized by means of X-ray diffraction (XRD), scanning electron microscopy equipped with an energy dispersive spectrometer (SEM-EDS), X-ray photoelectronic spectroscopy (XPS), and Fourier transformed infrared spectroscopy (FTIR). The mechanical and thermal properties of neat PP and PP composites were investigated as well. Thermal gravimetric (TG) analyses confirmed the reinforcing role of modified powder in PP composites. The mechanical properties studied showed that adding modified powder could significantly increase the impact strength, elongation at break point and flexural modulus of composites. The maximum incorporation content could reach 15 wt.% with a good balance between toughness and stiffness of PP composites. Differential scanning calorimetry (DSC) results showed that the modified powder could act as a nucleating agent and thus increase the crystallization temperature of PP. Polarized optical microscopy (POM) observation also indicated that the introduction of modified powder could promote the heterogeneous nucleation of PP matrix.

  2. Mechanical and dielectric characterization of hemp fibre reinforced polypropylene (HFRPP by dry impregnation process

    Directory of Open Access Journals (Sweden)

    2010-03-01

    Full Text Available Natural fibres such as jute, coir, sisal, bamboo and pineapple are known to have high specific strength and can be effectively used in composites in various applications. The use of hemp fibres to reinforce the polymer aroused great interest and expectations amongst scientists and materials engineers. In this paper, composites with isotactic polypropylene (iPP matrix and hemp fibres were studied. These materials were manufactured via the patented FIBROLINE process based on the principle of the dry impregnation of a fibre assembly with a thermoplastic powder (iPP, using an alternating electric field. The aim of this paper is to show the influence of fibre/matrix interfaces on dielectric properties coupled with mechanical behaviours. Fibres or more probably the fibre/matrix interfaces allow the diffusion of electric charges and delocalise the polarisation energy. In this way, damages are limited during mechanical loading and the mechanical properties of the composites increase. The structure of composite samples was investigated by X-ray and FTIR analysis. The mechanical properties were analysed by quasistatic and dynamic tests. The dielectric investigations were carried out using the SEMME (Scanning Electron Microscope Mirror Effect method coupled with the measurement of the induced current (ICM.

  3. Bio composites from polypropylene/ clay/eva polymers and kenaf natural fiber

    International Nuclear Information System (INIS)

    Siti Hasnah Kamarudin; Khalina Abdan; Bernard Maringgal; Wan Mohd Zin Wan Yunus

    2009-01-01

    Full text: There is an increasing need to investigate more environmental friendly, sustainable materials to replace existing materials as industry attempts to lessen dependence on petroleum based fuels and products. The natural fiber composites offer specific properties comparable to those of conventional fiber composites. In this experiment, mixing process of polymer/nano clay composites from polypropylene, organo clay and ethylene vinyl acetate were prepared using a Brabender twin screw compounder. The composites sheets were then laminated with kenaf fibers and subjected to hot and cold press machine to form a bio composite. The mechanical properties such as flexural and impact strength are compare favourably between polymers reinforced kenaf fiber and polymers without kenaf fiber. In addition, various analysis techniques were used to characterize the dispersion and the properties of nano composites, using scanning electron micrograph (SEM), differential scanning calorimetry (DSC) and thermogravimetric analysis (TGA). These results suggest that kenaf fibers are a viable alternative to inorganic mineral-based reinforcing fibers as long as the right processing conditions are used and they are used in applications where the higher water absorption is not critical. (author)

  4. Influence of injection temperatures and fiberglass compositions on mechanical properties of polypropylene

    Science.gov (United States)

    Keey, Tony Tiew Chun; Azuddin, M.

    2017-06-01

    Injection molding process appears to be one of the most suitable mass and cost efficiency manufacturing processes for polymeric parts nowadays due to its high efficiency of large scale production. When down-scaling the products and components, the limits of conventional injection molding process are reached. These constraints had initiated the development of conventional injection molding process into a new era of micro injection molding technology. In this study, fiberglass reinforced polypropylenes (PP) with various glass fiber percentage materials were used. The study start with fabrication of micro tensile specimens at three different injection temperature, 260°C, 270°C and 280°C for different percentage by weight of fiberglass reinforced PP. Then evaluate the effects of various injection temperatures on the tensile properties of micro tensile specimens. Different percentage by weight of fiberglass reinforced PP were tested as well and it was found that 20% fiberglass reinforced PP possessed the greatest percentage increase of tensile strength with increasing temperatures.

  5. Tribological performance of paddy straw reinforced polypropylene (PSRP and unidirectional glass-pultruded-kenaf (UGPK composites

    Directory of Open Access Journals (Sweden)

    R.M. Nasir

    2014-06-01

    Full Text Available In standard preparation and fabrication of natural-fibre embedded composites, 5 wt. % of natural fibre is enough to strengthen and homogenized in parental matrix as the mechanical strength was observed to increase by more than 25% of pure matrix. Hence, paddy straw and kenaf has been a potential candidate in northern region of Malaysia due to its abundance and easily replenished. A unidirectional glass-pultruded-kenaf (UGPK and paddy straws reinforced polypropylene (PSRP was studied focusing on its tribological performance. Meanwhile, friction and wear properties were examined using pin-on-disc machine under ambient temperature with dry contact condition. The tests were conducted at various sliding velocities (1.178-2.749m/s and applied normal loads (9.82-19.64N. The results showed that specific wear rate and friction coefficient decreased with increasing applied normal load and sliding velocity, but the applied normal load was more influential. The coefficient of friction ranges from 0.5 to 4 and wear rate varies from 0.5 to 4 x 10-5 mm3/Nm for PSRP. The friction coefficient of UGPK is within a range of 2.76 to 4.54 at the given test parameters while its wear rate ranging from 0.8 to 1.79 x 10-5mm3/Nm. The failure mode observed during the test was micro-buckling and followed by splitting while fiber-matrix interfacial failure occurred.

  6. Smart Natural Fiber Reinforced Plastic (NFRP) Composites Based On Recycled Polypropylene in The Presence Kaolin

    Science.gov (United States)

    Suharty, N. S.; Ismail, H.; Diharjo, K.; Handayani, D. S.; Lestari, W. A.

    2017-07-01

    Composites contain double filler material which act as reinforcement and flame retardants of recycled polypropylene (rPP)/kaolin(Kao)/palm oil empty bunch fiber (PEBF) have been succesfully prepared. The composites were synthesized through reactively solution method, using coupling agent PP-g-AA and compatibilizer DVB. The effect of double filler [Kao/PEBF] were investigated flexural strength (FS), inflammability, and morphology. Mechanical testing result in accordance to ASTM D790, the FS of rPP/DVB/PP-g-AA/Kao+ZB/PEBF composite was 48% higher than that of rPP matrix. Moreover, flexural modulus (FM) was significantly improved by 56% as compared to that of rPP matrix. The scanning electron images (SEM) shown good dispersion of [Ka/PEBF] and good filler-matrix interaction. The inflammability testing result which is tested using ASTM D635, showed that the flame resistance of rPP/DVB/PP-g-AA/Kao+ZB/PEBF composite was improve by increasing of time to ignition (TTI) about 857% and burning rate (BR) decreasing to 66% compared to the raw material rPP matrix. In the same time, the addition of 20% (w/w) PEBF as a second filler to form rPP/DVB/PP-g-AA/Kao+ZB/PEBF composites (F5) is able to increase: the FS by 17.5%, the FM by 19%, the TTI by 7.6% and the BR by 3.7% compared to the composite without PEBF (F2).

  7. A Comprehensive Study of the Polypropylene Fiber Reinforced Fly Ash Based Geopolymer.

    Directory of Open Access Journals (Sweden)

    Navid Ranjbar

    Full Text Available As a cementitious material, geopolymers show a high quasi-brittle behavior and a relatively low fracture energy. To overcome such a weakness, incorporation of fibers to a brittle matrix is a well-known technique to enhance the flexural properties. This study comprehensively evaluates the short and long term impacts of different volume percentages of polypropylene fiber (PPF reinforcement on fly ash based geopolymer composites. Different characteristics of the composite were compared at fresh state by flow measurement and hardened state by variation of shrinkage over time to assess the response of composites under flexural and compressive load conditions. The fiber-matrix interface, fiber surface and toughening mechanisms were assessed using field emission scan electron microscopy (FESEM and atomic force microscopy (AFM. The results show that incorporation of PPF up to 3 wt % into the geopolymer paste reduces the shrinkage and enhances the energy absorption of the composites. While, it might reduce the ultimate flexural and compressive strength of the material depending on fiber content.

  8. Stability study of polyacrylic acid films plasma-polymerized on polypropylene substrates at medium pressure

    Energy Technology Data Exchange (ETDEWEB)

    Morent, Rino, E-mail: Rino.Morent@Ugent.be [Department of Applied Physics, Research Unit Plasma Technology, Faculty of Engineering, Ghent University, Jozef Plateaustraat 22, 9000 Ghent (Belgium); De Geyter, Nathalie [Department of Applied Physics, Research Unit Plasma Technology, Faculty of Engineering, Ghent University, Jozef Plateaustraat 22, 9000 Ghent (Belgium); Trentesaux, Martine; Gengembre, Leon [Unite de Catalyse et Chimie du Solide, UMR CNRS 8181, Universite des Sciences et Technologies de Lille, Bat. C3, Cite Scientifique, 59655 Villeneuve d' Ascq (France); Dubruel, Peter [Department of Organic Chemistry, Polymer Chemistry and Biomaterials Research Group, Faculty of Sciences, Ghent University, Krijgslaan 281, 9000 Ghent (Belgium); Leys, Christophe [Department of Applied Physics, Research Unit Plasma Technology, Faculty of Engineering, Ghent University, Jozef Plateaustraat 22, 9000 Ghent (Belgium); Payen, Edmond [Unite de Catalyse et Chimie du Solide, UMR CNRS 8181, Universite des Sciences et Technologies de Lille, Bat. C3, Cite Scientifique, 59655 Villeneuve d' Ascq (France)

    2010-11-01

    Plasma polymerization of acrylic acid has become an interesting research subject, since these coatings are expected to be beneficial for biomedical applications due to their high surface density of carboxylic acid functional groups. However, the application of these monomers is counteracted by their low stability in humid environments, since a high stability is a required characteristic for almost any biological application. The present work investigates whether it is possible to obtain stable deposits with a high retention of carboxylic acid functions by performing plasma polymerization on polypropylene substrates with a dielectric barrier discharge operating at medium pressure. In order to obtain coatings with the desired properties, the plasma parameters need to be optimized. Therefore, in this paper, the influence of discharge power and location of the substrate in the discharge chamber is examined in detail. The properties of the deposited films are studied using contact angle measurements, X-ray photoelectron spectroscopy, atomic force microscopy and Fourier transform infrared spectroscopy. Moreover, to determine whether the obtained deposits are soluble in water, the coatings are once again analyzed after rinsing in water. This paper will clearly show that stable COOH-rich surfaces can be obtained at high discharge power and close to the monomer inlet, which might open perspectives for future biomedical applications.

  9. Study on the formation of the nanogel and microgels polypropylene modified by gamma radiation and incorporation of silver nanoparticles to biocides activity; Estudo da formacao de nanogeis e microgeis de polipropileno modificado por radiacao gama e incorporacao de nanoparticulas de prata visando a acao biocida

    Energy Technology Data Exchange (ETDEWEB)

    Oliani, Washington Luiz

    2013-07-01

    The study consists of the synthesis of HMSPP (polypropylene with high melt strength), also called polypropylene modified by gamma irradiation from iPP (isotactic polypropylene) in presence of acetylene at 110 kPa pressure and irradiated with γ of {sup 60}Co source at doses of 5, 12.5 and 20 kGy. The gel fraction of the samples was determined by extracting in xylene. The soluble portion of the samples was decanted to deposition on glass substrate until complete volatilization of xylene at room temperature of 25 °C. On the soluble portion of 12.5 kGy irradiated sample were added silver nanoparticles (AgNPs) in proportions of 0.25, 0.5, 1.0, 2.0 and 4.0 wt%. These gel samples were characterized by: scanning electron microscopy/energy dispersive spectroscopy (SEM / EDS), infrared spectroscopy (FTIR), scanning electron microscopy with field emission (FE-SEM), atomic force microscopy (AFM), differential scanning calorimetry (DSC), X-ray diffraction (XRD), reduction of colony forming unit (CFU) (%) and cytotoxicity assay. In this study of the morphology, it has been observed the formation of microgels in polypropylene increasing with the dose PP 5 kGy < PP 12.5 kGy < 20 kGy. Nanoscale structures of gels polypropylene (nanogels and nanofibers) were found in samples of PP 12.5 kGy and 20 kGy. The nanogels are formation of crosslinking, branching and entanglement that are nucleated in regions of high energy concentration (spurs) of one irradiated sample. Efficiency in tests of bactericide activity of the gels with AgNPs was observed versus E. coli and S. aureus from 1% AgNPs and non cytotoxicity were characterized in those samples for mammalian cells. In a second stage of this work films of the blend of PP and modified PP (50/50) were produced in a twin screw extruder. AgNPs were added to the extrusion processing in proportions of 0.1; 0.25; 0.5; 1.0; 1.0 PVP; 2.0 and 4.0 wt%. The films obtained were characterized by differential scanning calorimetry (DSC

  10. Radiation-induced grafting of acrylic acid onto polypropylene film and its biodegradability

    Science.gov (United States)

    Mandal, Dev K.; Bhunia, Haripada; Bajpai, Pramod K.; Chaudhari, C. V.; Dubey, K. A.; Varshney, L.

    2016-06-01

    Polypropylene based commodity polyolefins are widely used in packaging, manufacturing, electrical, pharmaceutical and other applications. The aim of the present work is to study the effect of grafting of acrylic acid on the biodegradability of acrylic acid grafted polypropylene. The effect of different conditions showed that grafting percentage increased with increase in monomer concentration, radiation dose and inhibitor concentration but decreased with increase in radiation dose rate. The maximum grafting of 159.4% could be achieved at optimum conditions. The structure of grafted polypropylene films at different degree of grafting was characterized by EDS, FTIR, TGA, DSC, SEM and XRD. EDS studies showed that the increase in acrylic acid grafting percentage increased the hydrophilicity of the grafted films. FTIR studies indicated the presence of acrylic acid on the surface of polypropylene film. TGA studies revealed that thermal stability decreased with increase in grafting percentage. DSC studies showed that melting temperature and crystallinity of the grafted polypropylene films lower than polypropylene film. SEM studies indicated that increase in acrylic acid grafting percentage increased the wrinkles in the grafted films. The maximum biodegradability could be achieved to 6.85% for 90.5% grafting. This suggested that microorganisms present in the compost could biodegrade acrylic acid grafted polypropylene.

  11. Susceptibility to scratch surface damage of wollastonite- and talc-containing polypropylene micrometric composites

    International Nuclear Information System (INIS)

    Hadal, R.; Dasari, A.; Rohrmann, J.; Misra, R.D.K.

    2004-01-01

    The paper describes the effect of wollastonite and talc on the scratch deformation behavior of low and high crystallinity polypropylenes under identical test conditions. The vertical resolution of atomic force microscopy and lateral resolution of scanning electron microscopy is utilized to examine the characteristics of scratch damage. Contrary to the expectations that high crystallinity and stiffness of polypropylene composites should increase resistance to scratch deformation, the susceptibility to mechanical deformation depends on bonding of mineral particles to the polymer matrix. Scratch deformed regions in neat polypropylenes were free of voids and grooves, while reinforced-polypropylenes exhibited voids and debonding/detachment of filler particles. The severity of plastic deformation in reinforced polypropylenes is a function of debonding/detachment of mineral particles, which is comparatively more for talc-reinforced polypropylenes than wollastonite-reinforced polypropylenes because of the layered structure of talc that encourages delamination. Usage of coating and coupling agents improved the resistance to scratch deformation by promoting adhesion and bonding between the reinforcement and matrix

  12. Thermal degradation kinetics and estimation of lifetime of radiation grafted polypropylene films

    International Nuclear Information System (INIS)

    Mandal, Dev K.; Bhunia, Haripada; Bajpai, Pramod K.; Bhalla, Vinod Kumar

    2017-01-01

    In this research work, thermal stability and degradation behavior of acrylic acid grafted polypropylene (PP-g-PAAc) films were investigated by using thermogravimetric (TGA) analysis at four different heating rates 5, 10, 15 and 20 °C/min over a temperature range of 40–550 °C in nitrogen atmosphere. The kinetic parameters namely activation energy (E a ), reaction order (n) and frequency factor (Z) were calculated by three multiple heating rate methods. The thermal stability of PP-g-PAAc films is found to decrease with increase in degree of grafting. The TGA data and thermal kinetic parameters were also used to predict the lifetime of grafted PP films. The estimated lifetime of neat PP as well as grafted PP decreased with increase in temperature by all the three methods. Studies also indicated that E a and lifetime of PP-g-PAAc films decreased with increase in degree of grafting, which may also be helpful in biodegradation of grafted PP films. - Highlights: • Thermal stability of grafted polypropylene films have been observed lower than for neat polypropylene film. • Multiple heating rate methods have been used for determination of activation energy. • Activation energies of grafted polypropylene films were lower than polypropylene film. • The lifetimes of grafted polypropylene films were shorter than for neat polypropylene film.

  13. Preparation, characterization and properties of nano-hydroxyapatite/polypropylene carbonate biocomposite

    Energy Technology Data Exchange (ETDEWEB)

    Liao, Jianguo, E-mail: liaojianguo10@hpu.edu.cn [School of Materials Science and Engineering, Henan Polytechnic University, Jiaozuo 454000 (China); Li, Yanqun [School of Materials Science and Engineering, Henan Polytechnic University, Jiaozuo 454000 (China); Zou, Qin [Analytical & Testing Center, Sichuan University, Chengdu 610064 (China); Duan, Xingze; Yang, Zhengpeng; Xie, Yufen [School of Materials Science and Engineering, Henan Polytechnic University, Jiaozuo 454000 (China); Liu, Haohuai [School of Chemistry and Chemical Engineering, Analytical and Testing Center, Guangzhou University, Guangzhou 510006 (China)

    2016-06-01

    The combination of nano-hydroxyapatite (n-HA) and polypropylene carbonate (PPC) was used to make a composite materials by a coprecipitation method. The physical and chemical properties of the composite were tested. Scanning electron microscope (SEM) observation indicated that the biomimetic n-HA crystals were uniformly distributed in the polymer matrix. As the n-HA content increased in the composite, the fracture mechanism of the composites changes from gliding fracture to gliding and brittle fracture. Furthermore, the chemical interaction between inorganic n-HA and polypropylene carbonate was also investigated and discussed in detail. The hydrogen bonds might be formed between –OH/CO{sub 3}{sup 2−} of n-HA crystal and the ester group (–COO–) of PPC. The tensile strength of n-HA/PPC (40/60) was similar to that of the cancellous bone, and reached ca 58 MPa. The osteoblasts were cultured for up to 7 days, and then the adhesion and proliferation of osteoblasts were measured by Methyl thiazolyl tetrazolium (MTT) colorimetry assay and SEM. The cells proliferated, grew normally in fusiform shape and well attached. The in vitro test confirmed that the n-HA/PPC composites were biocompatible and showed undetectable negative effect on osteoblasts. In vivo implantation of the composite in New Zealand white rabbits was performed. It can stimulate the growth of a new bone, and at the same time the material begins to degrade. These results suggested that the composite may be suitable for the reparation or replacement of bone defects and possessed the potential for clinical applications. - Graphical abstract: SEM micrographs of the induced osteoblasts cultured on the n-HA/PC (40/60) composite. After 2 day cell culture (a), after 4 days (b) hematoxylin/eosin-stained sections of n-HA/PPC (40/60) composite materials. In the photos, M denotes n-HA/PPC (40/60) composite materials, B denotes bone, while NB denotes newly formed bone tissue. - Highlights: • A novel method, co

  14. Pulse NMR-spectroscopy of structural changes of chemically modified polypropylene

    International Nuclear Information System (INIS)

    Gafarov, A.M.; Galibeev, S.S.; Kochnev, A.M.; Sukhanov, P.P.; Arkhireev, V.P.

    2004-01-01

    The structure of polypropylene compositions is studied by the method of pulse NMR-spectroscopy. The polypropylene compositions are derived by means of the modification by multicomponent systems. The analysis of relaxation times in a wide temperature range is carried out. Character of changes going on at a level of supermolecular structures is described. It is shown that the amplifications that manifest themselves under the polypropylene modification by the mixtures based on 2,4-tolyilendiisocyanate and e-caprolactam, are related to the change in the intermolecular interaction and formation of a more ordered polymer structure. (authors)

  15. Thermal Stability, Combustion Behavior, and Mechanical Property in a Flame-Retardant Polypropylene System

    Directory of Open Access Journals (Sweden)

    Lili Wang

    2017-01-01

    Full Text Available In order to comprehensively improve the strength, toughness, flame retardancy, smoke suppression, and thermal stability of polypropylene (PP, layered double hydroxide (LDH Ni0.2Mg2.8Al–LDH was synthesized by a coprecipitation method coupled with the microwave-hydrothermal treatment. The X-ray diffraction (XRD, morphology, mechanical, thermal, and fire properties for PP composites containing 1 wt %–20 wt % Ni0.2Mg2.8Al–LDH were investigated. The cone calorimeter tests confirm that the peak heat release rate (pk–HRR of PP–20%LDH was decreased to 500 kW/m2 from the 1057 kW/m2 of PP. The pk–HRR, average mass loss rate (AMLR and effective heat of combustion (EHC analysis indicates that the condensed phase fire retardant mechanism of Ni0.2Mg2.8Al–LDH in the composites. The production rate and mean release yield of CO for composites gradually decrease as Ni0.2Mg2.8Al–LDH increases in the PP matrix. Thermal analysis indicates that the decomposition temperature for PP–5%LDH and PP–10%LDH is 34 °C higher than that of the pure PP. The mechanical tests reveal that the tensile strength of PP–1%LDH is 7.9 MPa higher than that of the pure PP. Furthermore, the elongation at break of PP–10%LDH is 361% higher than PP. In this work, the synthetic LDH Ni0.2Mg2.8Al–LDH can be used as a flame retardant, smoke suppressant, thermal stabilizer, reinforcing, and toughening agent of PP products.

  16. Histologic and biomechanical evaluation of a novel macroporous polytetrafluoroethylene knit mesh compared to lightweight and heavyweight polypropylene mesh in a porcine model of ventral incisional hernia repair.

    Science.gov (United States)

    Melman, L; Jenkins, E D; Hamilton, N A; Bender, L C; Brodt, M D; Deeken, C R; Greco, S C; Frisella, M M; Matthews, B D

    2011-08-01

    To evaluate the biocompatibility of heavyweight polypropylene (HWPP), lightweight polypropylene (LWPP), and monofilament knit polytetrafluoroethylene (mkPTFE) mesh by comparing biomechanics and histologic response at 1, 3, and 5 months in a porcine model of incisional hernia repair. Bilateral full-thickness abdominal wall defects measuring 4 cm in length were created in 27 Yucatan minipigs. Twenty-one days after hernia creation, animals underwent bilateral preperitoneal ventral hernia repair with 8 × 10 cm pieces of mesh. Repairs were randomized to Bard(®)Mesh (HWPP, Bard/Davol, http://www.davol.com), ULTRAPRO(®) (LWPP, Ethicon, http://www.ethicon.com), and GORE(®)INFINIT Mesh (mkPTFE, Gore & Associates, http://www.gore.com). Nine animals were sacrificed at each timepoint (1, 3, and 5 months). At harvest, a 3 × 4 cm sample of mesh and incorporated tissue was taken from the center of the implant site and subjected to uniaxial tensile testing at a rate of 0.42 mm/s. The maximum force (N) and tensile strength (N/cm) were measured with a tensiometer, and stiffness (N/mm) was calculated from the slope of the force-versus-displacement curve. Adjacent sections of tissue were stained with hematoxylin and eosin (H&E) and analyzed for inflammation, fibrosis, and tissue ingrowth. Data are reported as mean ± SEM. Statistical significance (P 0.05 for all comparisons). However, for each mesh type, the maximum strength at 5 months was significantly lower than that at 1 month (P 0.05 for all comparisons). No significant differences with regard to inflammation, fibrosis, or tissue ingrowth were detected between mesh types at any time point (P > 0.09 for all comparisons). However, over time, inflammation decreased significantly for all mesh types (P 0.09). The maximum tensile strength of mesh in the abdominal wall decreased over time for HWPP, LWPP, and mkPTFE mesh materials alike. This trend may actually reflect inability to adequately grip specimens at later time points

  17. Surface treated polypropylene (PP) fibres for reinforced concrete

    Energy Technology Data Exchange (ETDEWEB)

    López-Buendía, Angel M., E-mail: buendia@uv.es [AIDICO Technological Institute of Construction, Benjamin Franklin 17, 46380 Paterna, Valencia (Spain); Romero-Sánchez, María Dolores [AIDICO Technological Institute of Construction, Marble Technical Unit, Camí de Castella 4, 03660 Novelda. Alicante (Spain); Climent, Verónica [Lafarge Cementos, Polígono Sepes, Isaac Newton s/n, 46500 Sagunto, Valencia (Spain); Guillem, Celia [AIDICO Technological Institute of Construction, Marble Technical Unit, Camí de Castella 4, 03660 Novelda. Alicante (Spain)

    2013-12-15

    Surface treatments on a polypropylene (PP) fibre have contributed to the improvement of fibre/concrete adhesion in fibre-reinforced concrete. The treatments to the PP fibre were characterized by contact angle measurements, ATR-IR and XPS to analyse chemical alterations. The surface topography and fibre/concrete interaction were analysed by several microscopic techniques, namely optical petrographic, and scanning electron microscopy. Treatment modified the surface chemistry and topography of the fibre by introducing sodium moieties and created additional fibre surface roughness. Modifications in the fibre surface led to an increase in the adhesion properties between the treated fibres and concrete and an improvement in the mechanical properties of the fibre-reinforced concrete composite as compared to the concrete containing untreated PP fibres. Compatibility with the concrete and increased roughness and mineral surface was also improved by nucleated portlandite and ettringite mineral association anchored on the alkaline PP fibre surface, which is induced during treatment.

  18. Broad line NMR study of modified polypropylene fibres

    International Nuclear Information System (INIS)

    Olcak, D.; Sevcovic, L.; Mucha, L.

    1999-01-01

    Study of drawn fibres prepared from an isostatic polypropylene modified by an ethylene aminoalkylacrylate copolymer has been done using the broad line of 1 H NMR. NMR spectra were measured on the set of fibres prepared with a draw ratio λ from 1 to 5.5 at two temperatures, one of them corresponding to the onset of segmental motion and the other one is the minddle of the temperature interval as determined by decrease of the second moment M 2 . Decomposition of the spectra into elementary components related to the amorphous, intermediate and crystalline regions of partially crystalline polymers has been made. The drawing of the fibres was found to enhance the chain mobility in the amorphous region and to restrain the molecular motion in the intermediate region. Such behaviour well supports conclusions predicted in the earlier study based on the spin-lattice relaxation time T 1 and dynamic mechanical data treated using the WLF theory. (Authors)

  19. Investigation reactor D-2201 polypropylene production unit using nuclear technique

    International Nuclear Information System (INIS)

    Wibisono; Sugiharto; Jefri Simanjuntak

    2016-01-01

    D-2201 reactor is a unit in the polypropylene production process at Pertamina Refinery Unit III Plaju. Reactor with a capacity of 45 kilo liter is not operated in normal operation condition. The validity of liquid level indicator on the unit is doubtful when refers to the production quality. Gamma source of 150 mCi Cobalt-60 and a scintillation detector had been used to scan the outer wall of the reactor to detect the liquid level during operation with a capacity of 40 %. Measurements were made along the reactor walls with 25 mm scan resolution and 5 seconds time sampling. Experiment result shows that the liquid level at the position of 40 % and at normal level position are not observed. Investigation did not find the liquid level above normal. D-2201 is diagnose not normal operating condition diagnosed with liquid abundant passed the recommended limits. Investigation advised to repair or to calibrate the liquid level indicator which is currently installed. (author)

  20. Evaluation of Environmental Aging of Polypropylene Irradiated Versus Pristine

    Science.gov (United States)

    Romano, Rebeca S. Grecco; Oliani, Washington Luiz; Parra, Duclerc Fernandes; Lugao, Ademar Benevolo

    Polypropylene (PP) is the most common thermoplastic resin of the plastic market due to its very interesting physical, chemical and processing properties at very low market price, however after its use the resin does not degrade in the environment or it degrades at very low rate. This study has the objective of comparing the environmental exposure of PP irradiated with 20 kGy and pristine PP. Dumbbell samples were manufactured by injection molding and exposed to the environment during 90 days; another one set was subjected to gamma irradiation at 20 kGy total dose and exposed at the same conditions too. The samples were characterized by mechanical testing, visual inspection, infrared spectroscopy (IR), scanning electron microscopy (SEM) and differential scanning calorimetry (DSC). The irradiated samples, after environmental aging, showed oxidation and presence of cracks in samples of the PP 20 kGy.

  1. An experimental study on stabilization of Pekan clay using polyethylene and polypropylene

    Science.gov (United States)

    Zukri, Azhani; Nazir, Ramli; Mender, Fatin Nabilah

    2017-10-01

    Many countries are expressing concern over the growing issues of polyethylene terephthalate (PET) bottles and polypropylene (PP) products made by the household sector. The rapid increase in the generation of plastic waste all around the world is due to the economic development and population growth. PP is the world's second-most widely produced synthetic plastic, after polyethylene. Statistics show that nearly 50% of the municipal solid waste in Malaysia comes from the institutional, industrial, residential, and construction waste. This paper presents the results of an investigation on the utilisation of fibres as products of PET bottles and PP products in order to improve the engineering properties of clay soil in Pekan. The soil samples were taken from Kampung Tanjung Medang, Pekan, Pahang. The basic properties of the clay soil were determined as follows; optimum moisture content: 32.5%, maximum dry density: 13.43 kN/m3, specific gravity: 2.51, liquid limit: 74.67%, plastic limit: 45.98%, and plasticity index: 28.69%. This investigation concentrates on the shear strength of the reinforced clay soils with PET and PP in random orientation. The reinforced soil samples were subjected to unconfined compression test (UCT) to differentiate their shear strength with that of the unreinforced soil. The tests found that the waste fibres (PET and PP) improved the strength properties of the Pekan clayey soils. The unconfined compressive strength (UCS) value increased with the increasing percentage of PET fibre and reached the optimum content at 10% reinforcement, where it showed the highest improvement of 365 kN/m2 from 325 kN/m2 and depleted when the optimum content reached 20% reinforcement. For PP fibre, the reinforced soil showed the highest UCS at 20% reinforcement with the improvement of 367 kN/m2. The study concluded that the PET and PP fibres can be utilised successfully as reinforcement materials for the stabilisation of clayey soils. The use of these waste compounds

  2. Studies on the flammability of polypropylene/ammonium polyphosphate and montmorillonite by using the cone calorimeter test

    Directory of Open Access Journals (Sweden)

    Hanna A.A.

    2018-03-01

    Full Text Available Fire performance of polypropylene (PP containing different percentages of ammonium polyphosphate (APP with montmorillonite (Mt or treated montmorillonite (MtT was carried out by using the cone calorimeter test (CCT. Different samples from ammonium polyphosphate and montmorillonite were mixed with 90% polypropylene. The characterization of the prepared samples indicates that there is incorporation between the components of the samples. Heat release rate (HRR, peak heat release rate (PHRR, average heat release rate (Av-HRR, and time to ignition (TTI of the samples were obtained from the cone calorimeter test. Also, the fire performance index (FPI and the fire growth rate (FIGRA were calculated. The interpretation of the curves and the parameters results from the cone calorimeter test which indicates that the addition of montmorillonite to APP increases its action as a flame retardant for PP. Moreover, the samples contain acid treatment montmorillonite showed an increase in the efficiency of ammonium polyphosphate when used. This result may be due to an increase in the SiO2 content by acid treatment.

  3. Polypropylene/ hydrocarbon resin blends nanocomposites; Blendas de polipropileno e resina hidrocarbonica com adicao de nanoparticulas de argila

    Energy Technology Data Exchange (ETDEWEB)

    Costa, Marlon W.M. da; Chinellato, Anne C.; Vidotti, Suel E., E-mail: suel.vidotti@ufabc.edu.br [Universidade Federal do ABC (CECS/UFABC), Santo Andre, SP (Brazil). Centro de Engenharia, Modelagem e Ciencias Sociais Aplicadas

    2015-07-01

    This work dealt with a study on the incorporation of hydrocarbon resin (HC) (Sukorez-120) and organoclay nanoparticles (MMT) (Cloisite 20A) to a homopolymer polypropylene (PP) matrix. The mixtures were done using a twin screw extruder and after molded into thin films. The films were characterized by differential scanning calorimetry (DSC), melt flow index (MFI), X-ray diffraction (DRX) and water vapor permeability. In general, the addition of the hydrocarbon resin led to an increase on the polypropylene crystallinity and a reduction on the water vapor permeability, when compared to the pristine PP. Although it was not possible to perceive synergism by the addition of the organoclay, once the samples containing both HC and MMT presented similar crystallinity but higher permeation values than those obtained by the mixtures prepared without the organoclay. This behavior could be attributed to the lack of the organoclay dispersion, as demonstrated by X-ray, as well as to interface defects that could result in worst barrier properties. (author)

  4. Radiation-grafting of 2-hydroxyethylmethacrylate and oligo (ethylene glycol) methyl ether methacrylate onto polypropylene films by one step method

    Energy Technology Data Exchange (ETDEWEB)

    Ramirez-Jimenez, Alejandro [Departamento de Quimica de Radiaciones y Radioquimica, Instituto de Ciencias Nucleares, Universidad Nacional Autonoma de Mexico, Circuito Exterior, Ciudad Universitaria, Mexico DF 04510 (Mexico); Alvarez-Lorenzo, Carmen; Concheiro, Angel [Departamento de Farmacia y Tecnologia Farmaceutica, Universidad de Santiago de Compostela, 15782-Santiago de Compostela (Spain); Bucio, Emilio, E-mail: ebucio@nucleares.unam.mx [Departamento de Quimica de Radiaciones y Radioquimica, Instituto de Ciencias Nucleares, Universidad Nacional Autonoma de Mexico, Circuito Exterior, Ciudad Universitaria, Mexico DF 04510 (Mexico)

    2012-01-15

    Polypropylene films were modified with 2-hydroxyethylmethacrylate (HEMA) and oligo (ethylene glycol) methyl ether methacrylate (OEGMA) using the pre-irradiation method with gamma-rays (one step method). The effect of absorbed dose from 10 to 100 kGy, temperature (50, 60, and 70 {sup o}C), monomer concentration between 12.5% and 62.5%, monomers ratio from 10% to 90% and reaction time from 5 to 50 h; on the degree of grafting was determined. The grafted samples were analyzed by FTIR-ATR, TGA, DSC, swelling, and contact angle. Grafts onto polymeric films between 3% and 109% were obtained at doses from 10 to 100 kGy and a dose rate around 7.4 kGy/h. The graft percent increased with the content in HEMA in the HEMA:OEGMA feed mixture, which indicates a lower reactivity of OEGMA compared to HEMA. The hydrogel layer grafted on the polypropylene substrate increases the hydrophilicity of the surface and also provides certain temperature-responsiveness, which may be of interest for biomedical applications. - Highlights: > PP was grafted with a hydrogel layer applying the {gamma}-ray pre-irradiation method. > Effects of radiation dose, time, temperature and monomers concentration were evaluated. > Grafted layer increases the hydrophilicity of PP films. > HEMA and OEGMA grafted onto PP may be of interest for biomedical applications.

  5. Variation and Grey GM(1, 1) Prediction of Melting Peak Temperature of Polypropylene During Ultraviolet Radiation Aging

    Science.gov (United States)

    Chen, K.; Y Zhang, T.; Zhang, F.; Zhang, Z. R.

    2017-12-01

    Grey system theory regards uncertain system in which information is known partly and unknown partly as research object, extracts useful information from part known, and thereby revealing the potential variation rule of the system. In order to research the applicability of data-driven modelling method in melting peak temperature (T m) fitting and prediction of polypropylene (PP) during ultraviolet radiation aging, the T m of homo-polypropylene after different ultraviolet radiation exposure time investigated by differential scanning calorimeter was fitted and predicted by grey GM(1, 1) model based on grey system theory. The results show that the T m of PP declines with the prolong of aging time, and fitting and prediction equation obtained by grey GM(1, 1) model is T m = 166.567472exp(-0.00012t). Fitting effect of the above equation is excellent and the maximum relative error between prediction value and actual value of T m is 0.32%. Grey system theory needs less original data, has high prediction accuracy, and can be used to predict aging behaviour of PP.

  6. Environmental Particle Emissions due to Automated Drilling of Polypropylene Composites and Nanocomposites Reinforced with Talc, Montmorillonite and Wollastonite

    Science.gov (United States)

    Starost, K.; Frijns, E.; Laer, J. V.; Faisal, N.; Egizabal, A.; Elizextea, C.; Nelissen, I.; Blazquez, M.; Njuguna, J.

    2017-05-01

    In this study, the effect on nanoparticle emissions due to drilling on Polypropylene (PP) reinforced with 20% talc, 5% montmorillonite (MMT) and 5% Wollastonite (WO) is investigated. The study is the first to explore the nanoparticle release from WO and talc reinforced composites and compares the results to previously researched MMT. With 5% WO, equivalent tensile properties with a 10 % weight reduction were obtained relative to the reference 20% talc sample. The materials were fabricated through injection moulding. The nanorelease studies were undertaken using the controlled drilling methodology for nanoparticle exposure assessment developed within the European Commission funded SIRENA Life 11 ENV/ES/506 project. Measurements were taken using CPC and DMS50 equipment for real-time characterization and measurements. The particle number concentration (of particles <1000nm) and particle size distribution (4.87nm - 562.34nm) of the particles emitted during drilling were evaluated to investigate the effect of the silicate fillers on the particles released. The nano-filled samples exhibited a 33% decrease (MMT sample) or a 30% increase (WO sample) on the average particle number concentration released in comparison to the neat polypropylene sample. The size distribution data displayed a substantial percentage of the particles released from the PP, PP/WO and PP/MMT samples to be between 5-20nm, whereas the PP/talc sample emitted larger particle diameters.

  7. Improvement of radiation resistance of polypropylene by blending with polyethylene and polystyrene

    International Nuclear Information System (INIS)

    Al Aji, Z.

    2001-01-01

    The use of polypropylene in production of medical component and packaging materials makes it an interesting material for applied research. Since the use of ethylene oxide for sterilization of medical components will be forbidden in the next future because of its carcinogens effect. Therefore, another alternative sterilization methods are required. The use of Gamma radiation is already established for sterilization of some medical components, this technique causes change in the physical mechanical properties of polypropylene, which makes the addition of stabilizers necessary. In this work, blends of domestically used polymers, polypropylene, linear low-density polyethylene, and polystyrene/butadiene were prepared in order to improve the radiation resistance of polypropylene; naphthalene was also used as an additive

  8. Mechanisms of Contact Electrification at Aluminum-Polytetrafluoroethylene and Polypropylene-Water

    KAUST Repository

    Nauruzbayeva, Jamilya

    2017-01-01

    of electrons, but a comprehensive understanding of contact electrification at interfaces of electrical insulators, such as air, water, polytetrafluoroethylene (PTFE), polypropylene remains incomplete. In fact, a variety of mechanisms responsible for transfer

  9. Process monitoring of glass reinforced polypropylene laminates using fiber Bragg gratings

    KAUST Repository

    Mulle, Matthieu; Wafai, Husam; Yudhanto, Arief; Lubineau, Gilles; Yaldiz, R.; Schijve, W.; Verghese, N.

    2015-01-01

    Hot-press molding of glass-fiber-reinforced polypropylene (GFPP) laminates was monitored using longitudinally and transversely embedded fiber Bragg gratings (FBGs) at different locations in unidirectional laminates. The optical sensors proved

  10. Evaluation of endoscopic laser excision of polypropylene mesh/sutures following anti-incontinence procedures.

    LENUS (Irish Health Repository)

    Davis, N F

    2012-11-01

    We reviewed our experience with and outcome of the largest series to our knowledge of patients who underwent endoscopic laser excision of eroded polypropylene mesh or sutures as a complication of previous anti-incontinence procedures.

  11. Morphology and crystalline-phase-dependent electrical insulating properties in tailored polypropylene for HVDC cables

    Science.gov (United States)

    Zha, Jun-Wei; Yan, Hong-Da; Li, Wei-Kang; Dang, Zhi-Min

    2016-11-01

    Polypropylene (PP) has become one promising material to potentially replace the cross-link polyethylene used for high voltage direct current cables. Besides the isotactic polypropylene, the block polypropylene (b-PP) and random polypropylene (r-PP) can be synthesized through the copolymerization of ethylene and propylene molecules. In this letter, the effect of morphology and crystalline phases on the insulating electrical properties of PP was investigated. It was found that the introduction of polyethylene monomer resulted in the formation of β and γ phases in b-PP and r-PP. The results from the characteristic trap energy levels indicated that the β and γ phases could induce deep electron traps which enable to capture the carriers. And the space charge accumulation was obviously suppressed. Besides, the decreased electrical conductivity was observed in b-PP and r-PP. It is attributed to the existence of deep traps which can effectively reduce the carrier mobility and density in materials.

  12. High Efficiency Particulate Air (HEPA) filters from polyester and polypropylene fibre nonwovens

    CSIR Research Space (South Africa)

    Boguslavsky, L

    2010-10-01

    Full Text Available filtration efficiency. Glass fibres are more harmful to human, compared to polypropylene and polyester fibre which are chemically inert. Hydroentanglement and chemical bonding techniques were utilised in manufacturing nonwovens for dry filtration. Acrylic...

  13. Raman structural study of melt-mixed blends of isotactic polypropylene with polyethylene of various densities

    Science.gov (United States)

    Prokhorov, K. A.; Nikolaeva, G. Yu; Sagitova, E. A.; Pashinin, P. P.; Guseva, M. A.; Shklyaruk, B. F.; Gerasin, V. A.

    2018-04-01

    We report a Raman structural study of melt-mixed blends of isotactic polypropylene with two grades of polyethylene: linear high-density and branched low-density polyethylenes. Raman methods, which had been suggested for the analysis of neat polyethylene and isotactic polypropylene, were modified in this study for quantitative analysis of polyethylene/polypropylene blends. We revealed the dependence of the degree of crystallinity and conformational composition of macromolecules in the blends on relative content of the blend components and preparation conditions (quenching or annealing). We suggested a simple Raman method for evaluation of the relative content of the components in polyethylene/polypropylene blends. The degree of crystallinity of our samples, evaluated by Raman spectroscopy, is in good agreement with the results of analysis by differential scanning calorimetry.

  14. Comparison of polypropylene and silicone Ahmed® glaucoma valves in the treatment of neovascular glaucoma: A 2-year follow-up.

    Science.gov (United States)

    Lubiński, Wojciech; Krzystolik, Karol; Gosławski, Wojciech; Kuprjanowicz, Leszek; Mularczyk, Maciej

    2018-01-01

    Inflammation associated with biomaterials of Ahmed® glaucoma drainage devices may cause the formation of a capsule around the device and can thus have a significant influence on the level of intraocular pressure reduction. The objective of this study was to compare the clinical outcomes after the implantation of a polypropylene or silicone Ahmed® glaucoma valve in patients with neovascular glaucoma. In the study, 27 eyes with neovascular glaucoma (group 1) received silicon Ahmed® valves and 23 eyes (group 2) received polypropylene valves. The best corrected distance visual acuity (BCDVA), intraocular pressure (IOP) and number of anti-glaucomatous drugs were recorded preoperatively and during a follow-up period of 24 months after surgery. Success was defined by the following criteria: 1) intraocular pressure in the rage of 6-21 mm Hg; 2) IOP reduction of at least 30% relative to preoperative values. All complications were registered. One month postoperatively, the mean BCDVA increased significantly in both groups compared to preoperative values (p glaucoma, the implantation of a silicone valve is associated with a significantly higher probability of long-term reduction of IOP below 21 mm Hg and with a lower risk of valve encapsulation in comparison to polypropylene valves. The obtained results suggest that silicone Ahmed® valves are more effective in the treatment of patients with neovascular glaucoma.

  15. Characteristic of Irradiation Result Film of Poly-Propylene-Co-Ethylene/Poly-ε-Caprolactone and Poly-Propylene Grafted Maleic Anhydrate Blend

    International Nuclear Information System (INIS)

    Nikham

    2004-01-01

    The effect of gamma rays irradiation to film of melt-blending polypropylene-co-ethylene (CPP) and poly-ε-caprolactone (PCL) with polypropylene grafted maleic anhydride (PP-g-MAH) blend as compatibilizer has been studied. The objective of the research is to prepare the biodegradable polyblend. The composition blend of CPP/PCL with 0, 10, 15, 20 wt % PP-g-MAH i.e. 100/0, 75/25, 50/50, 25/75 and 0/100 were irradiated by using gamma rays 60 Co with activity 420 kCi at doses; 0, 50, 100, 150, 200 kGy, at dose rate 8.2 kGy/hrs and temperature 90 o C. The elongation at break, tensile strength, gel fraction, enzymatic degradation and heat resistance were evaluated. The results showed that the compatibility of PP-g-MAH to reach good enough polyblend is 20 % weight. Elongation at break film of CPP/PCL 50/50 blend which irradiated at dose 200 kGy decreased, whereas the tensile strength increased. Gel fraction and heat resistance of the film irradiated increased. Enzyme of lipase AK can degraded either without irradiated or irradiated film. Thus quality of the polyblend can be called as biodegradable plastic material. (author)

  16. Recycling effects on the rheological and thermomechanical properties of polypropylene-based composites

    International Nuclear Information System (INIS)

    Bahlouli, Nadia; Pessey, Daniel; Raveyre, Claude; Guillet, Jacques; Ahzi, Said; Dahoun, Abdessalam; Hiver, Jean Marie

    2012-01-01

    Highlights: → Recycling effect on high impact PP with or without talc for automotive industries. → Rheological/mechanical tests, effect of molecular weight, deformation and damage. → Embrittlement of the amorphous matrix by chain scissions and growth of cavitation. → Better stability for talc filled HiPP, but decreased failure stress. → Interfaces talc/PP matrix and EPDM droplets/PP matrix are degraded. -- Abstract: As recycled materials are increasingly used in design of structural components, it is necessary to understand the effect of recycling on the properties and durability of these materials. In this work, the recycling effects on two high impact polypropylenes (HiPP) are studied. The recycling process was simulated by performing several extrusion runs with the same material in order to get a better understanding of the multi recycling effects. These effects were identified not only on the molecular weight and the rheological properties but also on the mechanical properties and the deformation mechanisms. The volume strain has been also measured as a damage indicator in the studied polymers. For both materials, the analysis of the different results showed that the rheological and the mechanical properties were affected by the thermomechanical recycling process. In particular, this process led to the decrease of the molecular weight, the decrease of the failure stress and the decrease of the impact energy. Moreover, Scanning Electronic Micoscopy (SEM) pictures showed a modification of the deformation process due to the embrittlement of the amorphous matrix by the chain scission and by cavitation. Moreover, a better stability for talc filled HiPP was observed but a decrease of the failure stress was obtained because the interfaces talc/polypropylene (PP) matrix and ethylene propylene diene monomer (EPDM) droplets/PP matrix were degraded. Indeed, the knowledge of the molecular characteristics as well as the rheological and mechanical properties of

  17. Effect of Mixing Process on Polypropylene Modified Bituminous Concrete Mix Properties

    OpenAIRE

    Noor Zainab Habib; Ibrahim Kamaruddin; Madzalan Napiah; Isa Mohd Tan

    2011-01-01

    This paper presents a research conducted to investigate the effect of mixing process on polypropylene (PP) modified bitumen mixed with well graded aggregate to form modified bituminous concrete mix. Two mode of mixing, namely dry and wet with different concentration of polymer polypropylene was used with 80/100 pen bitumen, to evaluate the bituminous concrete mix properties. Three percentages of polymer varying from 1-3% by the weight of bitumen was used in this study. Three mixes namely cont...

  18. Properties of residual marine fuel produced by thermolysis from polypropylene waste

    Directory of Open Access Journals (Sweden)

    Linas Miknius

    2015-06-01

    Full Text Available Thermal degradation of waste plastics with the aim of producing liquid fuel is one of the alternative solutions to landfill disposal or incineration. The paper describes thermal conversion of polypropylene waste and analysis of produced liquid fuel that would satisfy ISO 8217-2012 requirements for a residual marine fuel. Single pass batch thermolysis processes were conducted at different own vapour pressures (20-80 barg that determined process temperature, residence time of intermediates what resulted in different yields of the liquid product. Obtained products were stabilized by rectification to achieve required standard flash point. Gas chromatography and 1H NMR spectrometry show aliphatic nature of the liquid product where majority of the compounds are isoalkanes and isoalkenes. Only lightest fractions boiling up to a temperature of 72 oC have significant amount of n-pentane. Distribution of aromatic hydrocarbons is not even along the boiling range. The fractions boiling at a temperature of 128 oC and 160 oC have the highest content of monocyclic arenes – 3.16 % and 4.09 % respectively. The obtained final liquid residual product meets all but one requirements of ISO 8217-2012 for residual marine fuels.DOI: http://dx.doi.org/10.5755/j01.ms.21.2.6105

  19. The stopping power and energy straggling of heavy ions in silicon nitride and polypropylene

    Energy Technology Data Exchange (ETDEWEB)

    Mikšová, R., E-mail: miksova@ujf.cas.cz [Nuclear Physics Institute of the Academy of Science of the Czech Republic v.v. i., 250 68 Rez (Czech Republic); Department of Physics, Faculty of Science, J. E. Purkinje University, Ceske Mladeze 8, 400 96 Usti nad Labem (Czech Republic); Hnatowicz, V. [Nuclear Physics Institute of the Academy of Science of the Czech Republic v.v. i., 250 68 Rez (Czech Republic); Macková, A.; Malinský, P. [Nuclear Physics Institute of the Academy of Science of the Czech Republic v.v. i., 250 68 Rez (Czech Republic); Department of Physics, Faculty of Science, J. E. Purkinje University, Ceske Mladeze 8, 400 96 Usti nad Labem (Czech Republic); Slepička, P. [Department of Solid State Engineering, Institute of Chemical Technology, 166 28 Prague (Czech Republic)

    2015-07-01

    The stopping power and energy straggling of {sup 12}C{sup 3+} and {sup 16}O{sup 3+} ions with energies between 4.5 and 7.8 MeV in a 0.166-μm-thin silicon nitride and in 4-μm-thin polypropylene foils were measured by means of an indirect transmission method using a half-covered PIPS detector. Ions scattered from a thin gold layer under a scattering angle of 150° were used. The energy spectra of back-scattered and decelerated ions were registered and evaluated simultaneously. The measured stopping powers were compared with the theoretical predictions simulated by SRIM-2008 and MSTAR codes. SRIM prediction of energy stopping is reasonably close to the experimentally obtained values comparing to MSTAR values. Better agreement between experimental and predicted data was observed for C{sup 3+} ion energy losses comparing to O{sup 3+} ions. The experimental data from Paul’s database and our previous experimental data were also discussed. The obtained experimental energy-straggling data were compared to those calculated by using Bohr’s, Yang’s models etc. The predictions by Yang are in good agreement with our experiment within a frame of uncertainty of 25%.

  20. The stopping power and energy straggling of heavy ions in silicon nitride and polypropylene

    International Nuclear Information System (INIS)

    Mikšová, R.; Hnatowicz, V.; Macková, A.; Malinský, P.; Slepička, P.

    2015-01-01

    The stopping power and energy straggling of 12 C 3+ and 16 O 3+ ions with energies between 4.5 and 7.8 MeV in a 0.166-μm-thin silicon nitride and in 4-μm-thin polypropylene foils were measured by means of an indirect transmission method using a half-covered PIPS detector. Ions scattered from a thin gold layer under a scattering angle of 150° were used. The energy spectra of back-scattered and decelerated ions were registered and evaluated simultaneously. The measured stopping powers were compared with the theoretical predictions simulated by SRIM-2008 and MSTAR codes. SRIM prediction of energy stopping is reasonably close to the experimentally obtained values comparing to MSTAR values. Better agreement between experimental and predicted data was observed for C 3+ ion energy losses comparing to O 3+ ions. The experimental data from Paul’s database and our previous experimental data were also discussed. The obtained experimental energy-straggling data were compared to those calculated by using Bohr’s, Yang’s models etc. The predictions by Yang are in good agreement with our experiment within a frame of uncertainty of 25%

  1. A new constitutive model for prediction of impact rates response of polypropylene

    Directory of Open Access Journals (Sweden)

    Buckley C.P.

    2012-08-01

    Full Text Available This paper proposes a new constitutive model for predicting the impact rates response of polypropylene. Impact rates, as used here, refer to strain rates greater than 1000 1/s. The model is a physically based, three-dimensional constitutive model which incorporates the contributions of the amorphous, crystalline, pseudo-amorphous and entanglement networks to the constitutive response of polypropylene. The model mathematics is based on the well-known Glass-Rubber model originally developed for glassy polymers but the arguments have herein been extended to semi-crystalline polymers. In order to predict the impact rates behaviour of polypropylene, the model exploits the well-known framework of multiple processes yielding of polymers. This work argues that two dominant viscoelastic relaxation processes – the alpha- and beta-processes – can be associated with the yield responses of polypropylene observed at low-rate-dominant and impact-rates dominant loading regimes. Compression test data on polypropylene have been used to validate the model. The study has found that the model predicts quite well the experimentally observed nonlinear rate-dependent impact response of polypropylene.

  2. Effect of compatibilization and reprocessing on the isothermal crystallization kinetics of polypropylene/wood flour composites

    Directory of Open Access Journals (Sweden)

    Arieny Rodrigues

    2013-01-01

    Full Text Available Numerous studies have focused on polymer mixtures aimed at the potential applications of these materials. This work analyzed the effect of polymer reprocessing and the type and concentration of compatibilizer on the isothermal crystallization kinetics of polypropylene/wood flour composites. The composites, which were polypropylene grafted with acrylic acid (PP-g-AA and maleic anhydride (PP-g-MA, were processed in a twin screw extruder with and without compatibilizer. Reprocessed polypropylene reached complete crystallization in less time than the composites with virgin polypropylene. The addition of wood flour to the composites did not change the kinetics significantly compared to that of the pure polymers, but the compatibilizers did, particularly PP-g-AA. The nucleation exponent (n and crystallization rate (K were calculated from Avrami plots. The values of n ranged from 2 to 3, indicating instantaneous to sporadic nucleation. The crystallization half-time of reprocessed polypropylene was shorter than that of virgin polypropylene and of the compositions containing PP-g-AA compatibilizer. The activation energy of crystallization and the equilibrium melting temperature were calculated, respectively, from Arrhenius and Hoffman-Weeks plots. Both of these parameters showed lower values in the composites, particularly in the ones containing compatibilizers.

  3. Radiation modification and interaction mechanism of polypropylene and polyethylene by protons and electrons

    International Nuclear Information System (INIS)

    Wang Guanghou

    1988-10-01

    A systematic investigation of radiation effects on isotactic polypropylene (PP) and low-density polyethylene (PE) films by protons and electrons is reported. Electrons can make polyethylene cross-linked and polypropylene crached while protons can improve the PP mechanical properties and deteriorate polyethylene with increasing the irradiation dose. The structural analysis shows that conversion between α and β phases occurs and the crystallinity remains constant in the electron-irradiated polypropylene whereas the network structure is formed by allyl-type radicals in the e - -irradiated polyethylene. The infrared spectra indicate that conformational changes have taken place in the polypropylene under proton bombardment, such as the transition from an ordered to a disordered state in the crystalline region, the formation of double bonds as well as trans-conformations. This leads to the cross-linking between macromolecules of polypropylene at the proper irradiation doses, thus enhancing its mechanical properties. The cross-linking of polypropylene by proton bombardment observed and its properties may have some potential applications

  4. Thermal and mechanical properties of polypropylene/titanium dioxide nanocomposite fibers

    International Nuclear Information System (INIS)

    Esthappan, Saisy Kudilil; Kuttappan, Suma Kumbamala; Joseph, Rani

    2012-01-01

    Highlights: ► Wet synthesis method was used for the synthesis of TiO 2 nano particles. ► Mechanical properties of polypropylene fibers were increased by the addition of TiO 2 nanoparticles. ► Thermal stability of polypropylene fiber was improved significantly by the addition of TiO 2 nano particles. ► TiO 2 nanoparticles dispersed well in polypropylene fibers. -- Abstract: Titanium dioxide nanoparticles were prepared by wet synthesis method and characterized by transmission electron microscopy and X-ray diffraction studies. The nanotitanium dioxide then used to prepare polypropylene/titanium dioxide composites by melt mixing method. It was then made into fibers by melt spinning and subsequent drawing. Mechanical properties of the fibers were studied using Favimat tensile testing machine with a load cell of 1200 cN capacity. Thermal behavior of the fibers was studied using differential scanning calorimetry and thermogravimetric analysis. Scanning electron microscope studies were used to investigate the titanium dioxide surface morphology and crosssection of the fiber. Mechanical properties of the polypropylene fiber was improved by the addition of titanium dioxide nanoparticles. Incorporation of nanoparticles improves the thermal stability of polypropylene. Differential scanning calorimetric studies revealed an improvement in crystallinity was observed by the addition of titanium dioxide nanoparticles.

  5. Surface oxygenation of polypropylene using an air dielectric barrier discharge: the effect of different electrode-platen combinations

    International Nuclear Information System (INIS)

    Upadhyay, D.J.; Cui, N.-Y.; Anderson, C.A.; Brown, N.M.D.

    2004-01-01

    Polypropylene film has been modified in an air dielectric barrier discharge using two different electrode-platen configurations: stainless steel wire electrode-rubber platen or ceramic electrode-aluminium platen combinations. Modified films were characterised by static contact angle measurements, X-ray photoelectron spectroscopy (XPS), secondary ion mass spectrometry (SIMS) and Fourier transform infrared spectroscopy (ATR-FT-IR). Surface hydrophilic modification appears to be governed by the presence of low-molecular weight oxidised functionalities using XPS and SIMS techniques. Irrespective of the type of electrode-platen combination used to obtain the discharge, oxygenated functionalities of identical nature are formed on the polymer surface. However, the degree of oxidation obtained by the discharge using the wire electrodes with the rubber platen was considerably greater. Further increase in the observed hydrophilicity due to molecular rearrangement and development of stable oxygenated functionalities was evident after 1 month of post-processing analysis

  6. Restrained Shrinkage Cracking of Fiber-Reinforced High-Strength Concrete

    Directory of Open Access Journals (Sweden)

    Ashkan Saradar

    2018-02-01

    Full Text Available Concrete shrinkage and volume reduction happens due to the loss of moisture, which eventually results in cracks and more concrete deformation. In this study, the effect of polypropylene (PP, steel, glass, basalt, and polyolefin fibers on compressive and flexural strength, drying shrinkage, and cracking potential, using the ring test at early ages of high-strength concrete mixtures, was investigated. The restrained shrinkage test was performed on concrete ring specimens according to the ASTM C1581 standard. The crack width and age of restrained shrinkage cracking were the main parameters studied in this research. The results indicated that the addition of fiber increases the compressive strength by 16%, 20%, and 3% at the age of 3, 7, and 28 days, respectively, and increases the flexural toughness index up to 7.7 times. Steel and glass fibers had a better performance in flexural strength, but relatively poor action in the velocity reduction and cracking time of the restrained shrinkage. Additionally, cracks in all concrete ring specimens except for the polypropylene-containing mixture, was developed to a full depth crack. The mixture with polypropylene fiber indicated a reduction in crack width up to 62% and an increasing age cracking up to 84%.

  7. Graft copolymers of polypropylene films. 1. radiation induced grafting of mixed monomers. Vol. 3

    International Nuclear Information System (INIS)

    El-Salmawi, K.M.; El-Naggar, A.M.; Said, H.M.; Zahran, A.H.

    1996-01-01

    Radiation graft copolymerization of co monomer mixtures of acrylic acid (AAC), and styrene (S) onto polypropylene (PP) film by mutual method has been investigated. The effects of different factors that may affect the grafting yield such as inhibitor concentration (Mohr's salt), solvent composition (MeOH and H 2 O), radiation dose and dose rate were considered. It was found that the role of Mohr's salt is very effective when the ratio of AAC in the co monomer mixtures was at lower values. However, the addition of 1.25 Wt% of Mohr's salt reduced the homo polymer formation and enhances the grafting process. Graft copolymerization in presence of solvent mixture composed of methanol and water was found to afford higher grafting than in pure methanol regardless of the composition of the co monomer mixture used. However, the highest degree of grafting was obtained at a solvent composition of 20% H 2 O:80%MeOH and a co monomer mixture of 20%AAC:80%sty. An attempt was made to determine each PAAC and PS fractions in the total graft yield obtained. Two methods of analysis based on using the reactivity ratios reported in literature, elemental analysis and IR spectroscopy. The determination of poly (acrylic acid) and polystyrene fractions by elemental analysis is believed more accurate than these by reactivity ratio. The precise results obtained by elemental analysis with respect to the chemical structure of known polymer prepared under identical conditions. The results obtained by IR measurements go well with that obtained with the reactivity ratio methods. 5 figs., 3 tabs

  8. Graft copolymers of polypropylene films. 1. radiation induced grafting of mixed monomers. Vol. 3

    Energy Technology Data Exchange (ETDEWEB)

    El-Salmawi, K M; El-Naggar, A M; Said, H M; Zahran, A H [Radiation Chemistry Department, National Center for Radiation Research and Technology, Atomic Energy Authority, Cairo, (Egypt)

    1996-03-01

    Radiation graft copolymerization of co monomer mixtures of acrylic acid (AAC), and styrene (S) onto polypropylene (PP) film by mutual method has been investigated. The effects of different factors that may affect the grafting yield such as inhibitor concentration (Mohr`s salt), solvent composition (MeOH and H{sub 2} O), radiation dose and dose rate were considered. It was found that the role of Mohr`s salt is very effective when the ratio of AAC in the co monomer mixtures was at lower values. However, the addition of 1.25 Wt% of Mohr`s salt reduced the homo polymer formation and enhances the grafting process. Graft copolymerization in presence of solvent mixture composed of methanol and water was found to afford higher grafting than in pure methanol regardless of the composition of the co monomer mixture used. However, the highest degree of grafting was obtained at a solvent composition of 20% H{sub 2} O:80%MeOH and a co monomer mixture of 20%AAC:80%sty. An attempt was made to determine each PAAC and PS fractions in the total graft yield obtained. Two methods of analysis based on using the reactivity ratios reported in literature, elemental analysis and IR spectroscopy. The determination of poly (acrylic acid) and polystyrene fractions by elemental analysis is believed more accurate than these by reactivity ratio. The precise results obtained by elemental analysis with respect to the chemical structure of known polymer prepared under identical conditions. The results obtained by IR measurements go well with that obtained with the reactivity ratio methods. 5 figs., 3 tabs.

  9. Geopolymer obtained from coal ash

    International Nuclear Information System (INIS)

    Conte, V.; Bissari, E.S.; Uggioni, E.; Bernardin, A.M.

    2011-01-01

    Geopolymers are three-dimensional alumino silicates that can be rapidly formed at low temperature from naturally occurring aluminosilicates with a structure similar to zeolites. In this work coal ash (Tractebel Energy) was used as source of aluminosilicate according a full factorial design in eight formulations with three factors (hydroxide type and concentration and temperature) and two-levels. The ash was dried and hydroxide was added according type and concentration. The geopolymer was poured into cylindrical molds, cured (14 days) and subjected to compression test. The coal ash from power plants belongs to the Si-Al system and thus can easily form geopolymers. The compression tests showed that it is possible to obtain samples with strength comparable to conventional Portland cement. As a result, temperature and molarity are the main factors affecting the compressive strength of the obtained geopolymer. (author)

  10. Storing of Extracts in Polypropylene Microcentrifuge Tubes Yields Contaminant Peak During Ultra-flow Liquid Chromatographic Analysis

    OpenAIRE

    Kshirsagar, Parthraj R.; Hegde, Harsha; Pai, Sandeep R.

    2016-01-01

    Background and Aim: This study was designed to understand the effect of storage in polypropylene microcentrifuge tubes and glass vials during ultra-flow liquid chromatographic (UFLC) analysis. Materials and Methods: One ml of methanol was placed in polypropylene microcentrifuge tubes (PP material, Autoclavable) and glass vials (Borosilicate) separately for 1, 2, 4, 8, 10, 20, 40, and 80 days intervals stored at ?4?C. Results: Contaminant peak was detected in methanol stored in polypropylene m...

  11. Multiphasic Reaction Modeling for Polypropylene Production in a Pilot-Scale Catalytic Reactor

    Directory of Open Access Journals (Sweden)

    Mohammad Jakir Hossain Khan

    2016-06-01

    Full Text Available In this study, a novel multiphasic model for the calculation of the polypropylene production in a complicated hydrodynamic and the physiochemical environments has been formulated, confirmed and validated. This is a first research attempt that describes the development of the dual-phasic phenomena, the impact of the optimal process conditions on the production rate of polypropylene and the fluidized bed dynamic details which could be concurrently obtained after solving the model coupled with the CFD (computational fluid dynamics model, the basic mathematical model and the moment equations. Furthermore, we have established the quantitative relationship between the operational condition and the dynamic gas–solid behavior in actual reaction environments. Our results state that the proposed model could be applied for generalizing the production rate of the polymer from a chemical procedure to pilot-scale chemical reaction engineering. However, it was assumed that the solids present in the bubble phase and the reactant gas present in the emulsion phase improved the multiphasic model, thus taking into account that the polymerization took place mutually in the emulsion besides the bubble phase. It was observed that with respect to the experimental extent of the superficial gas velocity and the Ziegler-Natta feed rate, the ratio of the polymer produced as compared to the overall rate of production was approximately in the range of 9%–11%. This is a significant amount and it should not be ignored. We also carried out the simulation studies for comparing the data of the CFD-dependent dual-phasic model, the emulsion phase model, the dynamic bubble model and the experimental results. It was noted that the improved dual-phasic model and the CFD model were able to predict more constricted and safer windows at similar conditions as compared to the experimental results. Our work is unique, as the integrated developed model is able to offer clearer ideas

  12. Hand grip strength

    DEFF Research Database (Denmark)

    Frederiksen, Henrik; Gaist, David; Petersen, Hans Christian

    2002-01-01

    in life is a major problem in terms of prevalence, morbidity, functional limitations, and quality of life. It is therefore of interest to find a phenotype reflecting physical functioning which has a relatively high heritability and which can be measured in large samples. Hand grip strength is known......-55%). A powerful design to detect genes associated with a phenotype is obtained using the extreme discordant and concordant sib pairs, of whom 28 and 77 dizygotic twin pairs, respectively, were found in this study. Hence grip strength is a suitable phenotype for identifying genetic variants of importance to mid...

  13. Study of polypropylene irradiation to ensure the control of its environmental degradation

    International Nuclear Information System (INIS)

    Romano, Rebeca da Silva Grecco

    2017-01-01

    UV light, heat, and pollutants can interact with Polypropylene (PP) molecules, mainly with the tertiary carbon producing free radicals which can react with oxygen producing changes in its properties. PP has outstanding chemical and physical properties and a good processability at very low market price. In addition, PP is extensively used for manufacturing various kinds of products, however due to its large-scale consumption a lot of waste is generated at the end of their life cycle to the environment with low rate degradation. Controlled degradation of PP can be achieved by exposing the polymers to well defined parameters, such as absorbed dose, intemperies, oxygen, etc. In this study, structural changes in PP macro-molecule are created upon exposure to ionizing radiation such as: main chain scission, crosslinking and peroxidation (in presence of air). This study has the objective of comparing the environmental and accelerated exposures of PP neat, PP irradiated with 12,5 kGy and 20 kGy and the incorporation of the commercial pro-degradant d2w®. Dumbbell samples were manufactured by injection molding and exposed to the environment during 180 days and to accelerated aging to 192 days. The samples were characterized by Mechanical Testing, Fourier Transform Infrared Spectroscopy (FTIR), Scanning Electron Microscopy (SEM), X-ray Diffraction (DRX) and Differential Scanning Calorimetry (DSC). The samples previously irradiated, PP 20 kGy, after environmental aging showed higher oxidation and presence of surface cracks than the PP d2w® and PP neat. They also showed presence of carbonyl groups, decreases in elongation at break, increase in Strength Modulus and decrease of melting temperature corroborating with degradation. (author)

  14. Digital micromirror device (DMD)-based 3D printing of poly(propylene fumarate) scaffolds.

    Science.gov (United States)

    Mott, Eric J; Busso, Mallory; Luo, Xinyi; Dolder, Courtney; Wang, Martha O; Fisher, John P; Dean, David

    2016-04-01

    Our recent investigations into the 3D printing of poly(propylene fumarate) (PPF), a linear polyester, using a DMD-based system brought us to a resin that used titanium dioxide (TiO2) as an ultraviolet (UV) filter for controlling cure depth. However, this material hindered the 3D printing process due to undesirable lateral or "dark" curing (i.e., in areas not exposed to light from the DMD chip). Well known from its use in sunscreen, another UV filter, oxybenzone, has previously been used in conjunction with TiO2. In this study we hypothesize that combining these two UV filters will result in a synergistic effect that controls cure depth and avoids dark cure. A resin mixture (i.e., polymer, initiator, UV filters) was identified that worked well. The resin was then further characterized through mechanical testing, cure testing, and cytotoxicity testing to investigate its use as a material for bone tissue engineering scaffolds. Results show that the final resin eliminated dark cure as shown through image analysis. Mechanically the new scaffolds proved to be far weaker than those printed from previous resins, with compressive strengths of 7.8 ± 0.5 MPa vs. 36.5 ± 1.6 MPa, respectively. The new scaffolds showed a 90% reduction in elastic modulus and a 74% increase in max strain. These properties may be useful in tissue engineering applications where resorption is required. Initial cytotoxicity evaluation was negative. As hypothesized, the use of TiO2 and oxybenzone showed synergistic effects in the 3D printing of PPF tissue engineering scaffolds. Copyright © 2015 Elsevier B.V. All rights reserved.

  15. Carbon nanotube induced structural and physical property transitions of syndiotactic polypropylene

    International Nuclear Information System (INIS)

    Gorrasi, Giuliana; Romeo, Valentina; Sannino, Diana; Sarno, Maria; Ciambelli, Paolo; Vittoria, Vittoria; De Vivo, Biagio; Tucci, Vincenzo

    2007-01-01

    In this paper we have studied the effect of increasing carbon multi-walled nanotube (CNT) concentration in composites of syndiotactic polypropylene (sPP) having the same crystalline form but different morphologies. The attention was focused on the form I of sPP with different degrees of perfection (in terms of percentages of chains in helical conformation, crystal dimensions and crystallinity) obtained using two different quenching temperatures from the melt, i.e. 25 and 100 deg. C. We observed a decreasing effect of the crystallization temperature on increasing the nanotube content up to the samples with 10% of CNT, that show a very similar structural organization independent of the undercooling. Only the amorphous phase turns out more relaxed in the samples crystallized at the highest temperature. Either the thermal or the mechanical properties are improved on increasing the CNT content in both series of samples. The electrical conductivity increases in a similar manner in both series of samples and between 1 and 3 wt% it shows a sizable step of about eight orders of magnitude, a phenomenon that can be regarded as the onset of a percolating structure for which charge transport may take place

  16. Electrical and dielectric properties of foam injection-molded polypropylene/multiwalled carbon nanotube composites

    Energy Technology Data Exchange (ETDEWEB)

    Ameli, A.; Nofar, M.; Saniei, M.; Hossieny, N.; Park, C. B. [Microcellular Plastics Manufacturing Laboratory, Department of Mechanical and Industrial Engineering, University of Toronto, 5 King’s College Road, Toronto, Ontario, Canada M5S 3G8 (Canada); Pötschke, P. [Leibniz-Institut für Polymerforschung Dresden e.V. (IPF), Hohe Strasse 6, D-01069 Dresden (Germany)

    2015-05-22

    A combination of high dielectric permittivity (ε′) and low dielectric loss (tan δ) is required for charge storage applications. In percolative systems such as conductive polymer composites, however, obtaining high ε′ and low tan δ is very challenging due to the sharp insulation-conduction transition near the threshold region. Due to the particular arrangement of conductive fillers induced by both foaming and injection molding processes, they may address this issue. Therefore, this work evaluates the application of foam injection molding process in fabricating polymer nanocomposites for energy storage. Polypropylene-multiwalled carbon nanotubes (PP-MWCNT) composites were prepared by melt mixing and foamed in an injection molding process. Electrical conductivity (σ), ε′ and tan δ were then characterized. Also, scanning and transmission electron microscopy (SEM and TEM) was used to investigate the carbon nanotube’s arrangement as well as cellular morphology. The results showed that foam injection-molded composites exhibited highly superior dielectric properties to those of solid counterparts. For instance, foamed samples had ε′=68.3 and tan δ =0.05 (at 1.25 vol.% MWCNT), as opposed to ε′=17.8 and tan δ=0.04 in solid samples (at 2.56 vol.% MWCNT). The results of this work reveal that high performance dielectric nanocomposites can be developed using foam injection molding technologies for charge storage applications.

  17. Fluorinated cellular polypropylene films with time-invariant excellent surface electret properties by post-treatments

    International Nuclear Information System (INIS)

    An Zhenlian; Mao Mingjun; Yao Junlan; Zhang Yewen; Xia Zhongfu

    2010-01-01

    In this work, to improve the electret properties of cellular polypropylene films, they were fluorinated and post-treated with nitrous oxide and by isothermal crystallization. Surface electret properties of the samples were investigated by thermally stimulated discharge current measurements, and their compositions and structures were analysed by attenuated total reflection infrared spectroscopy and wide angle x-ray diffraction, respectively. Time-dependent deterioration of surface electret properties was observed for the fluorinated samples without the nitrous oxide post-treatment. However, deterioration did not occur for the fluorinated samples post-treated with nitrous oxide, and time-invariant excellent surface electret properties or deep surface charge traps were obtained by the combined post-treatments of the fluorinated samples with nitrous oxide and by isothermal crystallization. Based on the analyses of composition and structure of the treated samples, the deterioration was clarified to be due to a trace of oxygen in the reactive mixture, which led to the formation of peroxy RO 2 . radicals in the fluorinated surface layer. The time invariability of surface electret properties was owing to the rapid termination of the peroxy RO 2 . radicals by nitrous oxide. And the deep surface charge traps resulted from the isothermal crystallization treatment which led to an increase in the efficient charging interface between the crystallite and amorphous region and its property change.

  18. Mechanical Properties Distribution within Polypropylene Injection Molded Samples: Effect of Mold Temperature under Uneven Thermal Conditions

    Directory of Open Access Journals (Sweden)

    Sara Liparoti

    2017-11-01

    Full Text Available The quality of the polymer parts produced by injection molding is strongly affected by the processing conditions. Uncontrolled deviations from the proper process parameters could significantly affect both internal structure and final material properties. In this work, to mimic an uneven temperature field, a strong asymmetric heating is applied during the production of injection-molded polypropylene samples. The morphology of the samples is characterized by optical and atomic force microscopy (AFM, whereas the distribution of mechanical modulus at different scales is obtained by Indentation and HarmoniX AFM tests. Results clearly show that the temperature differences between the two mold surfaces significantly affect the morphology distributions of the molded parts. This is due to both the uneven temperature field evolutions and to the asymmetric flow field. The final mechanical property distributions are determined by competition between the local molecular stretch and the local structuring achieved during solidification. The cooling rate changes affect internal structures in terms of relaxation/reorganization levels and give rise to an asymmetric distribution of mechanical properties.

  19. Co-pyrolysis of rice straw and polypropylene using fixed-bed pyrolyzer

    Science.gov (United States)

    Izzatie, N. I.; Basha, M. H.; Uemura, Y.; Mazlan, M. A.; Hashim, M. S. M.; Amin, N. A. M.; Hamid, M. F.

    2016-11-01

    The present work encompasses the impact of temperature (450, 500, 550, 600 °C) on the properties of pyrolysis oil and on other product yield for the co-pyrolysis of Polypropylene (PP) plastics and rice straw. Co-pyrolysis of PP plastic and rice straw were conducted in a fixed-bed drop type pyrolyzer under an inert condition to attain maximum oil yield. Physically, the pyrolysis oil is dark-brown in colour with free flowing and has a strong acrid smell. Copyrolysis between these typically obtained in maximum pyrolysis oil yields up to 69% by ratio 1:1 at a maximum temperature of 550 °C. From the maximum yield of pyrolysis oil, characterization of pyrolysis product and effect of biomass type of the composition were evaluated. Pyrolysis oil contains a high water content of 66.137 wt.%. Furfural, 2- methylnaphthalene, tetrahydrofuran (THF), toluene and acetaldehyde were the major organic compounds found in pyrolysis oil of rice straw mixed with PP. Bio-char collected from co-pyrolysis of rice straw mixed with PP plastic has high calorific value of 21.190 kJ/g and also carbon content with 59.02 wt.% and could contribute to high heating value. The non-condensable gases consist of hydrogen, carbon monoxide, and methane as the major gas components.

  20. Influence of MCM-41 particle on mechanical and morphological behavior of polypropylene

    International Nuclear Information System (INIS)

    Wang Na; Shao Yawei; Shi Zhaoxin; Zhang Jing; Li Hongwei

    2008-01-01

    This study investigates the effects of different types of nanoparticles and amount of nanoparticles on morphology and mechanical performance of polypropylene (PP) composites. Three different types of nanoparticles, namely mesoporous MCM-41 (without template), mesoporous MCM-41 (with template), and mesoporous MCM-41, whose pore channels were filled with different flexible polymer inside the pore channels with the aid of supercritical CO 2 are considered. PP composites containing (0.5-5 wt.%) mesoporous MCM-41 were prepared by compounding. The tensile properties of the composites determined as a function of the filler loading and the different types of nanoparticles are found to vary with the different interface between different fillers and the matrix. The results of tensile tests showed that different flexible polymer filled mesoporous MCM-41 nanoparticles could simultaneously provide PP with strengthening and toughening effects at rather low filler content (0.5 wt.%). Scanning electron microscopy studies revealed a good dispersion of the MCM-41-S-PMMA and MCM-41-S-PS particles in the PP matrix and the enhancement of the interface between PP and MCM-41 are obtained

  1. Studies of polypropylene membrane fouling during microfiltration of broth with Citrobacter freundii bacteria

    Directory of Open Access Journals (Sweden)

    Gryta Marek

    2015-12-01

    Full Text Available In this work a fouling study of polypropylene membranes used for microfiltration of glycerol solutions fermented by Citrobacter freundii bacteria was presented. The permeate free of C. freundii bacteria and having a turbidity in the range of 0.72–1.46 NTU was obtained. However, the initial permeate flux (100–110 L/m2h at 30 kPa of transmembrane pressure was decreased 3–5 fold during 2–3 h of process duration. The performed scanning electron microscope observations confirmed that the filtered bacteria and suspensions present in the broth formed a cake layer on the membrane surface. A method of periodical module rinsing was used for restriction of the fouling influence on a flux decline. Rinsing with water removed most of the bacteria from the membrane surface, but did not permit to restore the initial permeate flux. It was confirmed that the irreversible fouling was dominated during broth filtration. The formed deposit was removed using a 1 wt% solution of sodium hydroxide as a rinsing solution.

  2. Degradation behavior of polymer blend of isotactic polypropylenes with and without unsaturated chain end group

    International Nuclear Information System (INIS)

    Nakatani, Hisayuki; Kurniawan, Dodik; Taniike, Toshiaki; Terano, Minoru

    2008-01-01

    In this work, the relationship between the unsaturated chain end group content and the thermal oxidative degradation rate was systematically studied with binary polymer blends of isotactic polypropylene (iPP) with and without the unsaturated chain end group. The iPPs with and without the unsaturated chain end group were synthesized by a metallocene catalyst in the absence of hydrogen and by a Ziegler catalyst in the presence of one, respectively. The thermal oxidative degradation rate of the binary iPP blends was estimated from the molecular weight and the apparent activation energy (ΔE), which were obtained through size exclusion chromatography (SEC) and thermogravimetric analysis (TGA) measurements, respectively. These values exhibited a negative correlation against the mole content of the unsaturated chain end group. The thermal oxidative degradation rate apparently depends on the content of the unsaturated chain end group. This tendency suggests that the unsaturated chain end acts as a radical initiator of the iPP degradation reaction.

  3. Design and properties of a novel nucleating agent for isotactic polypropylene

    International Nuclear Information System (INIS)

    Lv, Zhiping; Yang, Yunfei; Wu, Ran; Tong, Yuchao

    2012-01-01

    Highlights: ► Three new nucleating agents which is structurally similar to Al-PTBBA were prepared. ► These three nucleating agents were very effective in increasing T c and X c of iPP. ► Great improvement of mechanical properties of nucleated iPP was also obtained. ► Nucleating agent TSD was the most effective nucleating agent for iPP. -- Abstract: Three new nucleating agents TB, TD and TSD (titanate of benzoate or 4-tert-Butylbenzoate) were prepared. Isotactic polypropylene (iPP) nucleated were studied by using thermogravimetry analysis (TGA), X-ray diffraction analysis (XRD), differential scanning calorimetry (DSC) and polarized light microscopy (PLM). The mechanical properties and Vicat softening temperature (VST) of iPP were also tested. The results indicated that these three nucleating agents were very effective in increasing the crystallization temperature (T c ) and crystallinity (X c ) of iPP. Mechanical properties of nucleated iPP were improved remarkably, especially nucleating agent TSD.

  4. Polypropylene (PP) based proton exchange membrane for use in fuel cell

    International Nuclear Information System (INIS)

    Zen, Heloisa Augusto

    2008-01-01

    The radiation-induced graft of styrene onto polypropylene (PP) films was carried out by simultaneous irradiation method in a cobalt-60 source. The PP films were immersed in a solution of styrene with toluene (1:1 and 4:1, v/v) under inert atmosphere and at room temperature and then submitted at 20, 40, 80 and 100 kGy. After graft reaction the films were kept at room temperature under inert atmosphere for periods of 7, 14, 21 and 28 days in order to evaluate the degree of grafting. At the end of each period the films were sulfonated to provide the hydrophilic property to PP. The degree of grafting (DOG) was gravimetric determined and the chemical changes in the grafted and sulfonated films were characterized by Infrared Spectroscopy, Thermogravimetric Analysis (TGA), Differential Scanning Calorimetry and the Ion Exchange Capacity (IEC) was calculated. The greatest DOG was obtained after 21 days of post-irradiation. By TGA the grafted films exhibited a decrease in the thermal stability, while the sulfonated exhibited an increase. By DSC was possible to verify that matrix polymeric did not suffer any drastic change in the melting temperature after grafting and sulfonation reactions. The IEC calculated shows that the new membrane developed has ionic conductivity property. (author)

  5. Skin compatibility and antimicrobial studies on biofunctionalized polypropylene fabric

    Energy Technology Data Exchange (ETDEWEB)

    Anjum, Sadiya [Bioengineering Laboratory, Department of Textile Technology, Indian Institute of Technology, New Delhi 110016 (India); Gupta, Amlan; Sharma, Deepika [Department of Pathology, Sikkim Manipal Institute of Medical Sciences, Sikkim Manipal University, Gangtok 737102 (India); Dalal, Prashansa [Bioengineering Laboratory, Department of Textile Technology, Indian Institute of Technology, New Delhi 110016 (India); Gupta, Bhuvanesh, E-mail: bgupta@textile.iitd.ernet.in [Bioengineering Laboratory, Department of Textile Technology, Indian Institute of Technology, New Delhi 110016 (India)

    2016-12-01

    The aim of this study was the development of antimicrobial fabric which can be used as skin contacting material. The nanosilver loaded bioactive nanogels of polyacrylamide were prepared by gamma irradiation process and the particle size was observed to be in the range of 10–50 nm. In this study, we used polyethylene glycol as carrier for the combination of functional nanogel and essential oils together. Plasma functionalized polypropylene fabric was used as the base material for the bio-immobilization. Bioactive emulsion was coated on the fabric which exhibited excellent antimicrobial activity against Staphylococcus aureus and Escherichia coli. Skin irritation studies were carried out over a period of 3 d on Swiss albino mice. Histopathology studies of the fabric did not show adverse inflammatory response in contact with the skin. The biofunctionalized fabric offers appear to be promising material for skin contacting applications. - Highlights: • Antimicrobial processing of PP fabric for skin contacting material • Polyethylene glycol is used for the carrier of bioactive nanogels. • Synergistic effect of functional nanosilver and essential oil has been investigated. • Skin compatibility and histopathological studies of material have been observed.

  6. Benzothiazole sulfide compatibilized polypropylene/halloysite nanotubes composites

    Energy Technology Data Exchange (ETDEWEB)

    Liu Mingxian [Department of Polymer Materials and Engineering, South China University of Technology, Guangzhou 510640 (China); Guo Baochun, E-mail: psbcguo@scut.edu.cn [Department of Polymer Materials and Engineering, South China University of Technology, Guangzhou 510640 (China); Lei Yanda; Du Mingliang; Jia Demin [Department of Polymer Materials and Engineering, South China University of Technology, Guangzhou 510640 (China)

    2009-02-15

    Clay-philic benzothiazole sulfide, capable of donating electrons, is grafted onto polypropylene (PP) backbones when N-cyclohexyl-2-benzothiazole sulfonamide (CBS), a commonly used accelerator in the tire industry, is included in the processing of PP/halloysite nanotubes (HNTs) composites. CBS decomposes at elevated temperature and yields benzothiazole sulfide radicals, which react with the PP polymeric free radicals generated during the processing of the composites. On the other hand, the benzothiazole group of CBS is reactive to HNTs via electron transferring. The compatibilization between HNTs and PP is thus realized via interfacial grafting and electron transferring mechanism. The interfacial interactions in the compatibilized systems were fully characterized. Compared with the control sample, the dispersion of HNTs and the interfacial bonding are enhanced substantially in the compatibilized composites. The significantly improved mechanical properties and thermal properties of benzothiazole sulfide compatibilized PP/HNTs composites are correlated to the enhanced interfacial property. The present work demonstrates a novel interfacial design via interfacial grafting/electron transferring for the compatibilization of PP/clay composites.

  7. Bacterial Growth on Chitosan-Coated Polypropylene Textile

    Science.gov (United States)

    Erben, D.; Hola, V.; Jaros, J.; Rahel, J.

    2012-01-01

    Biofouling is a problem common in all systems where microorganisms and aqueous environment meet. Prevention of biofouling is therefore important in many industrial processes. The aim of this study was to develop a method to evaluate the ability of material coating to inhibit biofilm formation. Chitosan-coated polypropylene nonwoven textile was prepared using dielectric barrier discharge plasma activation. Resistance of the textile to biofouling was then tested. First, the textile was submerged into a growth medium inoculated with green fluorescein protein labelled Pseudomonas aeruginosa. After overnight incubation at 33°C, the textile was observed using confocal laser scanning microscopy for bacterial enumeration and biofilm structure characterisation. In the second stage, the textile was used as a filter medium for prefiltered river water, and the pressure development on the in-flow side was measured to quantify the overall level of biofouling. In both cases, nontreated textile samples were used as a control. The results indicate that the chitosan coating exhibits antibacterial properties. The developed method is applicable for the evaluation of the ability to inhibit biofilm formation. PMID:23724330

  8. Positron states in polypropylene and polystyrene at low temperature

    International Nuclear Information System (INIS)

    Djourelov, N.; Dauwe, C.; Palacio, C.A.; Laforest, N.; Bas, C.

    2007-01-01

    The increase of the positronium (Ps) yield as a function of the positron (e + ) source exposure time at 20 K was monitored in polypropylene and polystyrene by positron annihilation lifetime (PAL) and Doppler broadening (DB) spectroscopy. The contributions of the different e + and Ps states as extracted from the PAL analysis were used to reproduce the behaviour of the sharpness parameter (S) as a function of the wing parameter (W) of the annihilation line as measured by DB spectroscopy. We find a remarkable non-linearity in the S -W plots, which seems to be related to the existence of a third component (C 3 ) in a four-component exponential analysis. We discuss the origin of C 3 in the frame of a ''blob'' analysis of the PAL spectra. It is shown that the simulated S-W dependence can satisfactorily fit the observed non-linearity only on the assumption that C 3 characterizes a e + -molecule complex. (copyright 2007 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim) (orig.)

  9. Effect of isotacticity on radiation stability of polypropylene

    International Nuclear Information System (INIS)

    Qiao Jinliang; Zhang Fengru; Wei Genshuan; Zhang Juhong; Wu Jilan.

    1995-01-01

    The relationship between radiation stability and isotacticity of polypropylene(PP), such as isotactic pentad ratio, was studied in this paper. It was found that the higher isotacticity, the better radiation stability. Compared with normal PP powder which has normal isotacticity, the special PP powder with higher isotacticity, such as, isotactic pentad ratio > 98%, can keep the Melting Index change less than normal PP after UV-light-oxygen aging or γ-irradiation in air. Furthermore, the special PP powder with higher isotacticity has lower intention of crosslinking or branching after 1KGy γ-irradiation in vacuum and has lower intention of degradation after 5KGy γ-irradiation in vacuum. The special PP powder with higher isotacticity also has lower content of carbonyl after 25KGy γ-irradiation in air. These demonstrated that the special PP with higher isotacticity made from 'special catalyst' is more suitable as the material for radiation sterilization than normal PP, because there are less 'week points' in PP with higher isotacticity than that in PP with lower isotacticity. The random copolymer with 2.7% ethylene units made from the 'special catalyst' mentioned above is even more stable in irradiation sterilization than homopolypropylene with higher isotacticity; therefore, it is reasonable that a random copolypropylene with about 4%wt ethylene made from the 'special catalyst' should be the much more suitable PP material than normal PP for irradiation sterilization. (author)

  10. Radiation-induced grafting of TMPM onto polypropylene

    International Nuclear Information System (INIS)

    Wang Huiliang; Li Hong; Chen Wenxiu

    1995-01-01

    The gamma radiation-induced graft copolymerization of 2,2,6,6-tetramethyl-4-piperidinyl-methacrylate (TMPM), a very effective hindered amine light stabilizer (HALS), onto polypropylene was investigated by simultaneous- irradiation technique. The various synthesis conditions on the graft content was studied. It was found that benzene, CCl 4 and petroleum ether are more effective than other solvents, the percent grafting reached 7.1% for benzene. The percent grafting is higher when graft copolymerization is carried out in argon atmosphere than those in air. For all the grafting copolymerization carried out in benzene and CCl 4 , percent grafting increase linearly from 1 to 5 Mrad and beyond 5 Mrad, a tendency to level off appeared. At a constant dose, the percent grafting was found to be higher at high dose rate until 228 rad/s. Percent grafting also increased continuously with increasing monomer concentration up to 2.85 mol/L, but significant increase in grafting was observed only up to 1.14 mol/L

  11. Functionalization of Silica Nanoparticles for Polypropylene Nanocomposite Applications

    Directory of Open Access Journals (Sweden)

    Diego Bracho

    2012-01-01

    Full Text Available Synthetic silica nanospheres of 20 and 100 nm diameter were produced via the sol-gel method to be used as filler in polypropylene (PP composites. Modification of the silica surface was further performed by reaction with organic chlorosilanes in order to improve the particles interaction with the hydrophobic polyolefin matrix. These nanoparticles were characterized using transmission electronic microscopy (TEM, elemental analysis, thermogravimetric analysis (TGA, and solid-state nuclear magnetic resonance (NMR spectroscopy. For unmodified silica, it was found that the 20 nm particles have a greater effect on both mechanical and barrier properties of the polymeric composite. In particular, at 30 wt%, Young's modulus increases by 70%, whereas water vapor permeability (WVP increases by a factor of 6. Surface modification of the 100 nm particles doubles the value of the composite breaking strain compared to unmodified particles without affecting Young's modulus, while 20 nm modified particles presented a slight increase on both Young's modulus and breaking strain. Modified 100 nm particles showed a higher WVP compared to the unmodified particles, probably due to interparticle condensation during the modification step. Our results show that the addition of nanoparticles on the composite properties depends on both particle size and surface modifications.

  12. Mechanical properties of polypropylene/calcium carbonate nanocomposites

    Directory of Open Access Journals (Sweden)

    Daniel Eiras

    2009-01-01

    Full Text Available The aim of this work was to study the influence of calcium carbonate nanoparticles in both tensile and impact mechanical properties of a polypropylene homopolymer. Four compositions of PP/CaCO3 nanocomposites were prepared in a co-rotational twin screw extruder machine with calcium carbonate content of 3, 5, 7 and 10 wt. (% The tests included SEM analyzes together with EDS analyzer and FTIR spectroscopy for calcium carbonate, tensile and impact tests for PP and the nanocomposites. The results showed an increase in PP elastic modulus and a little increase in yield stress. Brittle-to-ductile transition temperature was reduced and the impact resistance increased with the addition of nanoparticles. From the stress-strain curves we determined the occurrence of debonding process before yielding leading to stress softening. Debonding stress was determined from stress-strain curves corresponding to stress in 1% strain. We concluded that the tensile properties depend on the surface contact area of nanoparticles and on their dispersion. Finally we believe that the toughening was due to the formation of diffuse shear because of debonding process.

  13. Effect of Nanosilica Filled Polyurethane Composite Coating on Polypropylene Substrate

    Directory of Open Access Journals (Sweden)

    Yern Chee Ching

    2013-01-01

    Full Text Available Acrylic based polyurethane (PU coatings with various amounts of nanosilica contents were prepared using solution casting method. The nanosilica (SiO2 particles used are around 16 nm in diameter. The friction and wear test was conducted using the reciprocating wear testing machine. The tests were performed at rotary speed of 100 rpm and 200 rpm with load of 0.1 kg to 0.4 kg under 1 N interval. The effect of the PU/nano-SiO2 composite coating on friction and wear behavior of polypropylene substrate was investigated and compared. The worn surface of coating film layer after testing was investigated by using an optical microscope. The introduction of PU/nanosilica composite coating containing 3 wt% of nano-SiO2 content gives the lowest friction coefficient and wear rate to PP substrate. Both the friction and wear rate of PP substrate coated with >3 wt% of nano-SiO2 filled PU coating would increase with the increasing of applied load and sliding time.

  14. Wear resistance of polypropylene-SiC composite

    Science.gov (United States)

    Abenojar, J.; Enciso, B.; Martínez, MA; Velasco, F.

    2017-05-01

    In this work, the wear resistance of thermoplastic composites with a high amount of ceramic is evaluated. Composites made of polypropylene (PP) and silicon carbide (SiC) powder at 50 wt% were used with the final objective of manufacturing ablative materials. This is the first part of a project studying the wear resistance and the mechanical properties of those composites, to be used in applications like habitat industry. In theory, the exposure to high temperature of ablative materials involves the elimination of thermal energy by the sacrifice of surface polymer. In our case, PP will act as a heat sink, up to the reaction temperature (melting or sublimation), where endothermic chemical decomposition into charred material and gaseous products occurs. As the surface is eroded, it is formed a SiC like-foam with improved insulation performance. Composites were produced by extrusion and hot compression. The wear characterization was performed by pin-on-disk test. Wear test was carried out under standard ASTM G99. The parameters were 120 rpm speed, 15 N load, a alumina ball with 6 mm as pin and 1000 m sliding distance. The tracks were also observed by opto-digital microscope.

  15. Anticoagulant and antimicrobial finishing of non-woven polypropylene textiles

    International Nuclear Information System (INIS)

    Degoutin, S; Jimenez, M; Casetta, M; Bellayer, S; Chai, F; Blanchemain, N; Neut, C; Kacem, I; Traisnel, M; Martel, B

    2012-01-01

    The aim of this work is to prepare non-woven polypropylene (PP) textile functionalized with bioactive molecules in order to improve its anticoagulation and antibacterial properties. This paper describes the optimization of the grafting process of acrylic acid (AA) on low-pressure cold-plasma pre-activated PP, the characterization of the modified substrates and the effect of these modifications on the in vitro biological response towards cells. Then, the immobilization of gentamicin (aminoglycoside antibiotic) and heparin (anticoagulation agent) has been carried out on the grafted samples by either ionic interactions or covalent linkages. Their bioactivity has been investigated and related to the nature of their interactions with the substrate. For gentamicin-immobilized AA-grafted samples, an inhibition radius and a reduction of 99% of the adhesion of Escherichia coli have been observed when gentamicin was linked by ionic interactions, allowing the release of the antibiotic. By contrast, for heparin-immobilized AA-grafted PP samples, a strong increase of the anticoagulant effect up to 35 min has been highlighted when heparin was covalently bonded on the substrate, by contact with the blood drop. (paper)

  16. Morphological, rheological and mechanical characterization of polypropylene nanocomposite blends.

    Science.gov (United States)

    Rosales, C; Contreras, V; Matos, M; Perera, R; Villarreal, N; García-López, D; Pastor, J M

    2008-04-01

    In the present work, the effectiveness of styrene/ethylene-butylene/styrene rubbers grafted with maleic anhydride (MA) and a metallocene polyethylene (mPE) as toughening materials in binary and ternary blends with polypropylene and its nanocomposite as continuous phases was evaluated in terms of transmission electron microscopy (TEM), scanning electron microscopy (SEM), oscillatory shear flow and dynamic mechanical thermal analysis (DMA). The flexural modulus and heat distortion temperature values were determined as well. A metallocene polyethylene and a polyamide-6 were used as dispersed phases in these binary and ternary blends produced via melt blending in a corotating twin-screw extruder. Results showed that the compatibilized blends prepared without clay are tougher than those prepared with the nanocomposite of PP as the matrix phase and no significant changes in shear viscosity, melt elasticity, flexural or storage moduli and heat distortion temperature values were observed between them. However, the binary blend with a nanocomposite of PP as matrix and metallocene polyethylene phase exhibited better toughness, lower shear viscosity, flexural modulus, and heat distortion temperature values than that prepared with polyamide-6 as dispersed phase. These results are related to the degree of clay dispersion in the PP and to the type of morphology developed in the different blends.

  17. Potential safe termination by injection of polypropylene pellets in JET

    International Nuclear Information System (INIS)

    Schmidt, G.L.; Ali-Arshad, S.; Bartlett, D.

    1995-01-01

    Thermal energy and the magnetic field energy associated with the plasma current must be dissipated safely when a tokamak discharge is terminated in a disruption. Magnetic energy can be dissipated by impurity radiation if position control is maintained. Prior to the dissipation of magnetic energy, thermal energy is usually conducted to the plasma contact points on a 1ms time scale in a thermal quench. A resistive, highly radiating plasma formed prior to the thermal quench, might dissipate both the thermal and magnetic energy by radiation minimizing damage due to local deposition. High speed injection of a low Z material can produce a resistive, highly radiating plasma on a 1ms time scale. Neon has recently been used in such an application on JT60-U. A large carbon pellet producing dilution temperatures < 1 keV is a possible alternative. This paper summarizes the results of an initial experiment performed in JET using carbon injected at high speed, as a 6mm polypropylene pellet, to investigate this potential approach to a safe plasma termination

  18. Wear resistance of polypropylene-SiC composite

    International Nuclear Information System (INIS)

    Abenojar, J; Enciso, B; Martínez, MA; Velasco, F

    2017-01-01

    In this work, the wear resistance of thermoplastic composites with a high amount of ceramic is evaluated. Composites made of polypropylene (PP) and silicon carbide (SiC) powder at 50 wt% were used with the final objective of manufacturing ablative materials. This is the first part of a project studying the wear resistance and the mechanical properties of those composites, to be used in applications like habitat industry. In theory, the exposure to high temperature of ablative materials involves the elimination of thermal energy by the sacrifice of surface polymer. In our case, PP will act as a heat sink, up to the reaction temperature (melting or sublimation), where endothermic chemical decomposition into charred material and gaseous products occurs. As the surface is eroded, it is formed a SiC like-foam with improved insulation performance. Composites were produced by extrusion and hot compression. The wear characterization was performed by pin-on-disk test. Wear test was carried out under standard ASTM G99. The parameters were 120 rpm speed, 15 N load, a alumina ball with 6 mm as pin and 1000 m sliding distance. The tracks were also observed by opto-digital microscope. (paper)

  19. Preparation and Characterization of Polypropylene Non-woven Fabrics Prepared by Melt-blown Spinning for Filtration Membranes

    Energy Technology Data Exchange (ETDEWEB)

    Chu, Konghee; Park, Mira; Kim, Hakyong [Chonbuk National Univ., Jeonju (Korea, Republic of); Jin, Fanlong; Park, Soojin [Inha Univ., Incheon (Korea, Republic of)

    2014-06-15

    PP non-woven fabrics were prepared by melt-blown spinning, followed by heat and plasma treatments. After heat treatment, the PP non-woven fabrics displayed decreased water flux, increased tensile strength, decreased elongation, and an average pore size of 0.7 μm. The hydrophilicity of the PP non-woven fabrics was improved by plasma treatment. The water flux of the PP non-woven fabrics increased about two fold after the plasma treatment. The particle removal efficiency was determined to be 97.2-99.4% for 1-3 μm sized particles, demonstrating a high particle removal efficiency. Polypropylene (PP) non-woven fabrics have been widely used as filtration membranes in wastewater purification with industrial applications due to their low cost, good mechanical strength, and high thermal and chemical stability. The membrane fouling behavior depends strongly on the physical and mechanical properties of the membrane, including pore size, porosity, morphology, and hydrophilicity. In general, PP non-woven fabrics have poor hydrophilicity; this has limited their application in the biomedical field. It is therefore necessary to develop PP non-woven fabrics with improved surface hydrophilicity to increase the scope of their use. Plasma treatment, an environmentally friendly alternative to traditional chemical activation, only changes the uppermost atomic layers of a membrane surface without affecting the bulk properties of the polymer.

  20. Attitude Strength.

    Science.gov (United States)

    Howe, Lauren C; Krosnick, Jon A

    2017-01-03

    Attitude strength has been the focus of a huge volume of research in psychology and related sciences for decades. The insights offered by this literature have tremendous value for understanding attitude functioning and structure and for the effective application of the attitude concept in applied settings. This is the first Annual Review of Psychology article on the topic, and it offers a review of theory and evidence regarding one of the most researched strength-related attitude features: attitude importance. Personal importance is attached to an attitude when the attitude is perceived to be relevant to self-interest, social identification with reference groups or reference individuals, and values. Attaching personal importance to an attitude causes crystallizing of attitudes (via enhanced resistance to change), effortful gathering and processing of relevant information, accumulation of a large store of well-organized relevant information in long-term memory, enhanced attitude extremity and accessibility, enhanced attitude impact on the regulation of interpersonal attraction, energizing of emotional reactions, and enhanced impact of attitudes on behavioral intentions and action. Thus, important attitudes are real and consequential psychological forces, and their study offers opportunities for addressing behavioral change.

  1. Silver nanoparticle deposition on inverse opal SiO2 films embedded in protective polypropylene micropits for SERS applications

    Science.gov (United States)

    Ammosova, Lena; Ankudze, Bright; Philip, Anish; Jiang, Yu; Pakkanen, Tuula T.; Pakkanen, Tapani A.

    2018-01-01

    Common methods to fabricate surface enhanced Raman scattering (SERS) substrates with controlled micro-nanohierarchy are often complex and expensive. In this study, we demonstrate a simple and cost effective method to fabricate SERS substrates with complex geometries. Microworking robot structuration is used to pattern a polypropylene (PP) substrate with micropits, facilitating protective microenvironment for brittle SiO2 inverse opal (IO) structure. Hierarchical SiO2 IO patterns were obtained using polystyrene (PS) spheres as a sacrificial template, and were selectively embedded into the hydrophilized PP micropits. The same microworking robot technique was subsequently used to deposit silver nanoparticle ink into the SiO2 IO cavities. The fabricated multi-level micro-nanohierarchy surface was studied to enhance Raman scattering of the 4-aminothiophenol (4-ATP) analyte molecule. The results show that the SERS performance of the micro-nanohierarchical substrate increases significantly the Raman scattering intensity compared to substrates with structured 2D surface geometries.

  2. Development of thermoplastic elastomers based on maleated ethylene propylene rubber (m-EPM and polypropylene (PP by dynamic vulcanization

    Directory of Open Access Journals (Sweden)

    2007-08-01

    Full Text Available Dicumyl peroxide (DCP-cured thermoplastic vulcanizates (TPVs based on blends of maleated ethylene propylene rubber (m-EPM and polypropylene (PP using maleated-PP as a compatibilizer have been developed. Physical properties of these TPVs change significantly with concentrations of DCP and rubber/plastic blend ratios. Important correlations were obtained from rheometer delta torque values with various physical properties of the TPVs like tension set and crosslink density etc. Wide angle X-ray diffraction study confirms that concentration of DCP has a strong influence on the crystallinity of PP, which might affect the final physical properties of TPVs. The recyclability and ageing characteristics of these TPVs are also found excellent.

  3. Reduction of the Early Autogenous Shrinkage of High Strength Concrete

    Directory of Open Access Journals (Sweden)

    Drago Saje

    2015-01-01

    Full Text Available The results of a laboratory investigation on the early autogenous shrinkage of high strength concrete, and the possibilities of its reduction, are presented. Such concrete demonstrates significant autogenous shrinkage, which should, however, be limited in the early stages of its development in order to prevent the occurrence of cracks and/or drop in the load-carrying capacity of concrete structures. The following possibilities for reducing autogenous shrinkage were investigated: the use of low-heat cement, a shrinkage-reducing admixture, steel fibres, premoistened polypropylene fibres, and presoaked lightweight aggregate. In the case of the use of presoaked natural lightweight aggregate, with a fraction from 2 to 4 mm, the early autogenous shrinkage of one-day-old high strength concrete decreased by about 90%, with no change to the concrete's compressive strength in comparison with that of the reference concrete.

  4. Thermal Stability of Clay's Galleries in Polypropylene - Clay (montmorillonite Nanocomposites using Polypropylene-gMaleic Anhydride as Compatibilizer

    Directory of Open Access Journals (Sweden)

    Sotya Astutiningsih

    2010-10-01

    Full Text Available Superior properties of food packaging can be achieved using nanocomposite technology. However, fabrication of this materials are complex and expensive. Long term objectives of this research is the synthesis of low cost polypropylene clay nanocomposites (PPCN via a short-cut method known as ‘cascade engineering’. Cascade engineering principle in PPCN fabrication is performed by using compatibilizer (to enable the mixing of PP and clay masterbatch, and PPCN in one pot process using melt mixer. This paper present the experimental results using small-angle x-ray diffraction (XRD on the thermal stability of the PPCN. Results from the XRD analysis showed that the clay was intercalated, however no significant changes were observed as a result of variation in mixing time. XRD patterns of the annealed PPCN showed reduction of MMT’s gallery (deintercalation These phenomenon was probably caused by insufficient bonding and lack of compatibility between PP-g-MA and MMT.

  5. Radiation-modified blends of the basis of polyethylene terephthalate and polypropylene

    International Nuclear Information System (INIS)

    Mery-Meri, R.; Revyakin, O.; Zicans, J.

    2000-01-01

    The binary composite systems on the basis of post-consumer poly-(ethylene terephthalate) and polypropylene have been investigated. Mechanical properties of the compositions were studied in detail in order to expand the application possibilities of tested binary composites. Structural changes of the poly (ethylene terephthalate) / polypropylene blends depending on the concentration of the components were investigated also. Additionally, the optimum processing conditions were established. Particular attention was paid to study the influence of the ionizing γ-radiation on the structural and mechanical properties of the composition systems tested. The magnitude of the adsorbed dose od γ-radiation was established to affect differently the structure of poly(ethylene terephalate) and polypropylene. At small absorbed doses (50 kGy) crosslinking of the polymer was observed for both poly(ethylene terephthalate) and polypropylene resulting in the increase of some mechanical properties of pure materials as well of their compositions, whereas the absorbed dose of 300 kGy caused the destruction of the tested materials. It is important to mention that the rate of radiation-chemical destruction of polypropylene is higher than poly(ethylene terephthalate) destruction rate. (author)

  6. Role of carbon nanotubes (CNTs) in improving wear properties of polypropylene (PP) in dry sliding condition

    International Nuclear Information System (INIS)

    Ashok Gandhi, R.; Palanikumar, K.; Ragunath, B.K.; Paulo Davim, J.

    2013-01-01

    Highlights: ► Role of carbon nanotubes (CNTs) on wear behaviour of polypropylene (PP) is evaluated. ► Effect of applied pressure and composition against a steel counter face is investigated. ► Microstructure and worn surfaces of samples are observed by scanning electron microscope. ► The wear phenomenon has been discussed based on wear losses and worn surfaces. ► The coefficient of friction (μ) and sliding time for PP and PP/CNT blend is investigated. - Abstract: Polymers are widely used for sliding couples against metals and other materials. Polypropylene is a polymer used in variety of applications includes packaging, laboratory equipments, automotive components, etc. Polypropylene is often desirable automotive material due to its low cost, colorability, chemical resistance and UV stability. In addition the range of potential polypropylene uses is nearly unlimited through the use of modifiers, additives and fillers. In the present work, the sliding wear of polypropylene (PP) and carbon nanotube (CNT) blends are evaluated as a function of applied load and composition against a steel counter face in dry condition. The addition of CNT in PP in wear performance is investigated and presented in detail. Microstructure and worn surfaces of samples were observed by scanning electron microscope. The wear phenomenon has been discussed based on wear losses and worn surfaces

  7. Multi-walled carbon nanotube filled polypropylene nanocomposites based on masterbatch route: Improvement of dispersion and mechanical properties through PP-g-MA addition

    Directory of Open Access Journals (Sweden)

    2008-10-01

    Full Text Available Multi-wall carbon nanotubes (MWNTs filled polypropylene (PP nanocomposites were prepared through diluting a PP/MWNT masterbatch in a PP matrix by melt compounding with a twin screw extruder. Polypropylene grafted maleic anhydride (PP-g-MA was used to promote the carbon nanotubes dispersion. The effect of PP-g-MA addition on the rheological, mechanical and morphological properties of the nanocomposites was assessed for different MWNTs loadings. Scanning electron microscopy (SEM has shown that nanotubes are distributed reasonably uniformly. A better dispersion and good adhesion between the nanotubes and the PP matrix is caused by wrapping of PP-g-MA on MWNTs. When PP-g-MA is added, dynamic moduli and viscosity further increases compared to PP/MWNT nanocomposites. The rheological percolation threshold drops significantly. Tensile and flexural moduli and Charpy impact resistance of the nanocomposites also increases by the addition of PP-g-MA. The present study confirms that PP-g-MA is efficient to promote the dispersion of MWNTs in PP matrix and serves as an adhesive to increase their interfacial strength, hence greatly improving the rheological percolation threshold and mechanical properties of PP/MWNT nanocomposites.

  8. Comparative study between polypropylene and polypropylene/poliglecaprone meshes used in the correction of abdominal wall defect in rats Estudo comparativo entre as telas de polipropileno e polipropileno/poliglecaprone utilizadas na correção de defeito na parede abdominal ventral de ratos

    Directory of Open Access Journals (Sweden)

    Carlos Alberto Lima Utrabo

    2012-04-01

    Full Text Available PURPOSE: To evaluate the healing process of a defect in the ventral abdominal wall of rats, comparing the polypropylene and polypropylene/poliglecaprone meshes on the 30th and 60th postoperative day. METHODS: Thirty two Wistar rats were submitted to a ventral abdominal wall defect, with integrity of the parietal peritoneum. In the repair, were used polypropylene (group A and polypropylene/poliglecaprone (group B meshes. The groups were subdivided into four subgroups of eight animals euthanized on the 30th (A30 and B30 and 60th postoperative day (A60 and B60. Fragments of the abdominal wall of the animals were submitted to macroscopic, tensiometric and histological evaluations. RESULTS: The tensiometry on subgroup A30 showed a mean average break point of 0.78 MPa and in A60, 0.66 Mpa. In subgroup B30 it was 0.84 MPa and in B60, 1.27 Mpa. The score of the inflammatory process showed subacute phase on A30 and B30 sub-groups and chronic inflammatory process in subgroups A30 and 60B. CONCLUSIONS: The tensile strength was higher on the wall repaired by polypropylene/poliglecaprone mesh in the 60th post-operative day. Histology showed higher concentration of fibrosis on the surface of the polypropylene mesh with a tendency to encapsulation. In polypropylene/poliglecaprone subgroups the histology showed higher concentration of fibrosis on the surface of mesh filaments.OBJETIVO: Avaliar a cicatrização de um defeito, na parede abdominal ventral de ratos, comparando-se as telas de polipropileno e polipropileno/poliglecaprone no 30º e 60º dia do pós-operatório. MÉTODOS: Trinta e dois ratos Wistar foram submetidos à produção de defeito na parede abdominal ventral, com integridade do peritônio parietal. Na correção foram utilizadas as telas de polipropileno (grupo A e polipropileno/poliglecaprone (grupo B. Houve subdivisão em quatro subgrupos (A30, A60, B30 e B60 de oito animais que foram submetidos à eutanásia no 30º e 60º dia do p

  9. New fillers in the synthesis of polypropylene nano composites with Ziegler-Natta catalysts; Novas cargas na sintese de nanocompositos de polipropileno com catalisadores Ziegler-Natta

    Energy Technology Data Exchange (ETDEWEB)

    NONE

    2011-07-01

    In this study, Ziegler-Natta catalysts bi-supported on MgCl{sub 2} and natural clays were prepared in order to synthesize polypropylene nanocomposites. The employed clays were bentonite, as reference, as well as halloysite, vermiculite and mica. Propylene polymerizations were carried out using those catalysts and the properties of the obtained materials were analyzed using techniques of thermogravimetric analysis X-ray diffraction, dynamic mechanical thermal analysis e scanning electronic microscopy. Results showed the production of nanocomposites with higher thermal degradation temperature. (author)

  10. Antimicrobial Carvacrol-Containing Polypropylene Films: Composition, Structure and Function

    Directory of Open Access Journals (Sweden)

    Max Krepker

    2018-01-01

    Full Text Available Significant research has been directed toward the incorporation of bioactive plant extracts or essential oils (EOs into polymers to endow the latter with antimicrobial functionality. EOs offer a unique combination of having broad antimicrobial activity from a natural source, generally recognized as safe (GRAS recognition in the US, and a volatile nature. However, their volatility also presents a major challenge in their incorporation into polymers by conventional high-temperature-processing techniques. Herein, antimicrobial polypropylene (PP cast films were produced by incorporating carvacrol (a model EO or carvacrol, loaded into halloysite nanotubes (HNTs, via melt compounding. We studied the composition-structure-property relationships in these systems, focusing on the effect of carvacrol on the composition of the films, the PP crystalline phase and its morphology and the films’ mechanical and antimicrobial properties. For the first time, molecular dynamics simulations were applied to reveal the complex interactions between the components of these carvacrol-containing systems. We show that strong molecular interactions between PP and carvacrol minimize the loss of this highly-volatile EO during high-temperature polymer processing, enabling semi-industrial scale production. The resulting films exhibit outstanding antimicrobial properties against model microorganisms (Escherichia coli and Alternaria alternata. The PP/(HNTs-carvacrol nanocomposite films, containing the carvacrol-loaded HNTs, display a higher level of crystalline order, superior mechanical properties and prolonged release of carvacrol, in comparison to PP/carvacrol blends. These properties are ascribed to the role of HNTs in these nanocomposites and their effect on the PP matrix and retained carvacrol content.

  11. Laser-induced selective copper plating of polypropylene surface

    Science.gov (United States)

    Ratautas, K.; Gedvilas, M.; Stankevičiene, I.; JagminienÄ--, A.; Norkus, E.; Li Pira, N.; Sinopoli, S.; Emanuele, U.; Račiukaitis, G.

    2016-03-01

    Laser writing for selective plating of electro-conductive lines for electronics has several significant advantages, compared to conventional printed circuit board technology. Firstly, this method is faster and cheaper at the prototyping stage. Secondly, material consumption is reduced, because it works selectively. However, the biggest merit of this method is potentiality to produce moulded interconnect device, enabling to create electronics on complex 3D surfaces, thus saving space, materials and cost of production. There are two basic techniques of laser writing for selective plating on plastics: the laser-induced selective activation (LISA) and laser direct structuring (LDS). In the LISA method, pure plastics without any dopant (filler) can be used. In the LDS method, special fillers are mixed in the polymer matrix. These fillers are activated during laser writing process, and, in the next processing step, the laser modified area can be selectively plated with metals. In this work, both methods of the laser writing for the selective plating of polymers were investigated and compared. For LDS approach, new material: polypropylene with carbon-based additives was tested using picosecond and nanosecond laser pulses. Different laser processing parameters (laser pulse energy, scanning speed, the number of scans, pulse durations, wavelength and overlapping of scanned lines) were applied in order to find out the optimal regime of activation. Areal selectivity tests showed a high plating resolution. The narrowest width of a copper-plated line was less than 23 μm. Finally, our material was applied to the prototype of the electronic circuit board on a 2D surface.

  12. Effect of boron and phosphate compounds on physical, mechanical, and fire properties of wood-polypropylene composites

    Science.gov (United States)

    Nadir Ayrilmis; Turgay Akbulut; Turker Dundar; Robert H. White; Fatih Mengeloglu; Umit Buyuksari; Zeki Candan; Erkan Avci

    2012-01-01

    Physical, mechanical, and fire properties of the injection-molded wood flour/polypropylene composites incorporated with different contents of boron compounds; borax/boric acid and zinc borate, and phosphate compounds; mono and diammonium phosphates were investigated. The effect of the coupling agent content, maleic anhydride-grafted polypropylene, on the properties of...

  13. Evaluation of Properties of Unidirectional Hemp/Polypropylene Composites: Influence of Fiber Content and Fiber/Matrix Interface Variables

    DEFF Research Database (Denmark)

    Plackett, David; Løgstrup Andersen, Tom; Lilholt, Hans

    2002-01-01

    Flament-wound textile hemp yarn was used in combination with unmodified or maleated polypropylene (PP) films to produce plates of unidirectional composites.......Flament-wound textile hemp yarn was used in combination with unmodified or maleated polypropylene (PP) films to produce plates of unidirectional composites....

  14. Analysis of Nanodomain Composition in High-Impact Polypropylene by Atomic Force Microscopy-Infrared.

    Science.gov (United States)

    Tang, Fuguang; Bao, Peite; Su, Zhaohui

    2016-05-03

    In this paper, compositions of nanodomains in a commercial high-impact polypropylene (HIPP) were investigated by an atomic force microscopy-infrared (AFM-IR) technique. An AFM-IR quantitative analysis method was established for the first time, which was then employed to analyze the polyethylene content in the nanoscopic domains of the rubber particles dispersed in the polypropylene matrix. It was found that the polyethylene content in the matrix was close to zero and was high in the rubbery intermediate layers, both as expected. However, the major component of the rigid cores of the rubber particles was found to be polypropylene rather than polyethylene, contrary to what was previously believed. The finding provides new insight into the complicated structure of HIPPs, and the AFM-IR quantitative method reported here offers a useful tool for assessing compositions of nanoscopic domains in complex polymeric systems.

  15. Essential work of fracture analysis for starch filled poly(propylene carbonate) composites

    International Nuclear Information System (INIS)

    Wang, X.L.; Li, R.K.Y.; Cao, Y.X.; Meng, Y.Z.

    2007-01-01

    Starch filled poly(propylene carbonate) composites are environmental friendly materials. In this study, the fracture toughness of composites under mode I loading was determined by the essential work of fracture concept. The specific essential fracture work of the poly(propylene carbonate)/starch composites decreases with increasing the starch content, while the non-essential work term, βw p increases with increasing the starch content. In addition, the morphologies, thermal properties, thermo-mechanical properties were studied by scanning electron microscope, thermogravimetric analysis, dynamic mechanical analysis, and differential scanning calorimetry, respectively. The thermal and thermo-mechanical measurements revealed that increasing starch content led to an increase in glass transition temperature and thermal stability. Morphology observation indicates that poly(propylene carbonate) and starch have weak interfacial adhesion

  16. Analysis and optimization of machining parameters of laser cutting for polypropylene composite

    Science.gov (United States)

    Deepa, A.; Padmanabhan, K.; Kuppan, P.

    2017-11-01

    Present works explains about machining of self-reinforced Polypropylene composite fabricated using hot compaction method. The objective of the experiment is to find optimum machining parameters for Polypropylene (PP). Laser power and Machining speed were the parameters considered in response to tensile test and Flexure test. Taguchi method is used for experimentation. Grey Relational Analysis (GRA) is used for multiple process parameter optimization. ANOVA (Analysis of Variance) is used to find impact for process parameter. Polypropylene has got the great application in various fields like, it is used in the form of foam in model aircraft and other radio-controlled vehicles, thin sheets (∼2-20μm) used as a dielectric, PP is also used in piping system, it is also been used in hernia and pelvic organ repair or protect new herrnis in the same location.

  17. Influence of procedure variables in formation and properties of polypropylene/bentonite nanocomposites

    International Nuclear Information System (INIS)

    Andrade, Daniela de Lourdes Anjos Coutinho Simoes

    2009-01-01

    The purpose of this work is to prepare nanocomposites of polypropylene/compatibilizer/bentonite, by melting intercalation, with a commercial sodium clay - Argel - as filler. This clay was organically purified and modified by different methods, with a quaternary ammonium salt. The clays were characterized by X-Ray diffraction (XRD), infrared spectroscopy (FTIR) and thermogravimetric analyses (TG) to determine the most efficient preparation method. Before that, in the second stage of this study, the influence of the type and contend of organoclay in the properties of the polypropylene films was measured; the same was done for the compatibilizer. The preliminary results indicate that the nanocomposites film with 1% of organoclay and 15% of polypropylene grafted with maleic anhydride show promise as packing materials and may be used, in the near future, as a new product by the national industry. (author)

  18. Flammability of polypropylene/organoclay nanocomposites; Inflamabilidade de nanocompositos de polipropileno/argila organofilica

    Energy Technology Data Exchange (ETDEWEB)

    Alves, Tatianny Soares; Barbosa, Renata [Universidade Federal do Piaui (UFPI), Teresina (Brazil); Carvalho, Laura Hecker de [Universidade Federal de Campina Grande (UFCG), PB (Brazil); Canedo, Eduardo Luis [Instituto de Tecnologia de Pernambuco, Recife (Brazil)

    2014-11-01

    The flammabilities of nanocomposites made with three polypropylene grades (homo and copolymers) with 5 wt % of organoclay (Cloisite 20A), 5 or 15 wt % of maleated polypropylene as compatibilizer, and 0, 0.5 or 1 wt % of cis-13-docosenamide (Erucamide) as co-intercalant, were studied using the horizontal burning test UL94HB. Masterbatches prepared in an internal mixer were diluted in the polypropylene matrix using a corotating twin-screw extruder, with different screw configurations and operating at 240 or 480 rpm. Results indicate that the high burning rate of the composites was not affected by the processing conditions. For all formulations was observed a significant reduction in smoke release, lack of dripping and the formation of a char surface layer, that protected the core of the samples. (author)

  19. Nickel-titanium wire in circumferential suture of a flexor tendon repair: a comparison to polypropylene.

    Science.gov (United States)

    Karjalainen, T; He, M; Chong, A K S; Lim, A Y T; Ryhanen, J

    2010-07-01

    Nickel-titanium (NiTi) has been proposed as an alternative material for flexor tendon core suture. To our knowledge, its suitability as a circumferential suture of flexor tendon repair has not been investigated before. The purpose of this ex vivo study was to investigate the biomechanical properties of NiTi circumferential repairs and to compare them with commonly used polypropylene. Forty porcine flexor tendons were cut and repaired by simple running or interlocking mattress technique using 100 microm NiTi wire or 6-0 polypropylene. The NiTi circumferential repairs showed superior stiffness, gap resistance, and load to failure when compared to polypropylene repairs with both techniques. Nickel-titanium wire seems to be a potential material for circumferential repair of flexor tendons. Copyright 2010 American Society for Surgery of the Hand. Published by Elsevier Inc. All rights reserved.

  20. Effects of gamma irradiation on food contact polyethylene, polypropylene and polystyrene. Volatiles

    International Nuclear Information System (INIS)

    Kawamura, Yoko; Sayama, Kayo; Yamada, Takashi

    2000-01-01

    The effects of gamma irradiation on the generation of volatiles from food contact polyethylene and polypropylene were investigated using head space (HS)/GC/MS. All samples generated volatiles such as acetic acid, propionic acid, butanoic acid, 2,2-dimethylpropionic acid, acetone, 2-butanone, 2-propanol, 2-methyl-2-propanol, hydrocarbons, etc., due to the gamma irradiation. Especially, acetic acid and acetone were formed in greatest amounts. Since these volatiles did not exist before irradiation and their amounts increased with increasing irradiation dose, they should be degradation products from the polymer or additives by irradiation. Polypropylene generated more kinds and larger amounts of volatiles than polyethylene, which showed that polypropylene is more sensitive to irradiation. Polystyrene contained styrene and ethylbenzene as monomers before irradiation and their amounts decreased after irradiation. Polystyrene generated few degradation products during the irradiation. (author)

  1. Interfacial enhancement of polypropylene composites modified with sorbitol derivatives and siloxane-silsesquioxane resin

    Science.gov (United States)

    Dobrzyńska-Mizera, Monika; Dutkiewicz, Michał; Sterzyński, Tomasz; Di Lorenzo, Maria Laura

    2015-12-01

    Composites based on polypropylene (iPP) modified with a sorbitol derivative (NX8000) and siloxane-silsesquioxane resin (SiOPh) containing maleated polypropylene (MAPP) as compatibilizer were prepared by melt extrusion. Calorimetric investigations were carried out using differential scanning calorimetry (DSC), whereas the morphological and mechanical properties were investigated by scanning electron microscopy (SEM) and static tensile tests. DSC measurements revealed no influence of SiOPh and a slight effect of MAPP addition on the crystallization kinetics of polypropylene. Additionally, the introduction of MAPP into the iPP+NX8000+SiOPh composites increased plastic properties of the samples. All the above was attributed to the compatibilizing effect of MAPP which improved interfacial adhesion between iPP, NX8000 and SiOPh. This phenomenon was also confirmed by the SEM images illustrating more homogenous distribution of the filler in the compatibilized samples.

  2. Coir dust reinforced recycled polypropylene composites; Compositos de polipropileno reciclado e po de coco

    Energy Technology Data Exchange (ETDEWEB)

    Santos, Bianca B. dos; Costa, Marysilvia F. da; Thire, Rossana M. da S.M., E-mail: bianca@metalmat.ufrj.br [Universidade Federal do Rio de Janeiro (UFRJ), Rio de Janeiro, RJ (Brazil)

    2015-07-01

    The environmental impacts caused by disposed plastics encourage the search for new alternatives. Recycling polymers leads to the degradation of their mechanical properties, which can be modified by the addition of fillers. In this paper, recycled polypropylene from plastic cups with 2%, 5% and 10% of coir dust were produced with and without the addition of additives. These composites were characterized by tensile tests, X-ray diffraction, differential scanning calorimetry and scanning electron microscopy on the fracture surface. It was verified the effectiveness of the addition of coir dust in improving the elasticity modulus of recycled polypropylene besides the effectiveness of additives used in promoting the adhesion of the powder to the matrix. However, higher levels of coir dust caused the appearance of air bubbles inside the material, which contributed to its embrittlement. The addition of coir dust promoted a decrease in the degree of polypropylene crystallinity. (author)

  3. Vibration behaviour of foamed concrete floor with polypropylene and rise husk ash fibre

    Science.gov (United States)

    Azaman, N. A. Mohd; Ghafar, N. H. Abd; Ayub, N.; Ibrahim, M. Z.

    2017-11-01

    In the history of the construction industry, lightweight concrete or foamed concrete is a special concrete which can very useful in the construction sector because it is very lightweight and it can compact by itself at each angle of foamwork. Foamed concrete is one of lightweight concrete which widely used for floor construction due to its light weight and economic. The significant challenges in the floor design process are considering the vibration that needs improvements for the poor dynamic behaviour insulation. An alternative material to replace sand with certain amount of rice husk ash (RHA) and polypropylene was introduced. Research was determine the dynamic behavior of foam-polypropylene and foam-RHA concrete by using impact hammer test. The natural frequency for normal foamed concrete, 0.5 % of Polypropylene and 15% of RHA is 29.8 Hz, 29.3 Hz and 29.5 Hz respectively.

  4. Reel-to-Reel Atmospheric Pressure Dielectric Barrier Discharge (DBD Plasma Treatment of Polypropylene Films

    Directory of Open Access Journals (Sweden)

    Lukas JW Seidelmann

    2017-03-01

    Full Text Available Atmospheric pressure plasma treatment of the surface of a polypropylene film can significantly increase its surface energy and, thereby improve the printability of the film. A laboratory-scale dielectric barrier discharge (DBD system has therefore been developed, which simulates the electrode configuration and reel-to-reel web transport mechanism used in a typical industrial-scale system. By treating the polypropylene in a nitrogen discharge, we have shown that the water contact angle could be reduced by as much as 40° compared to the untreated film, corresponding to an increase in surface energy of 14 mNm−1. Ink pull-off tests showed that the DBD plasma treatment resulted in excellent adhesion of solvent-based inks to the polypropylene film.

  5. an experimental study on the use of polypropylene waste

    African Journals Online (AJOL)

    HOD

    5.5% and could satisfy strength and durability requirements of heavy traffic situation. Keywords: High .... the durability of the mix. ..... Perspective to the Management of Federal Roads in ... Pavement Failure Induced by Poor Soil Properties.

  6. Development of hemp fibre reinforced polypropylene composite - Journal Article

    CSIR Research Space (South Africa)

    Hargitai, H

    2005-06-01

    Full Text Available strong decrease in three point bending properties was noticed after immersing the composite samples in the distilled water for 19 days, while the impact strength increased. Double carding of raw materials resulted into decreased anisotropy in composite...

  7. The effect of modified ijuk fibers to crystallinity of polypropylene composite

    Science.gov (United States)

    Prabowo, I.; Nur Pratama, J.; Chalid, M.

    2017-07-01

    Nowadays, plastics becomes concern associated with its degradation and environmental issues. It has led studies to develop an environmental-friendly material. To minimize the impact of those problems, recently the usage of natural fibers as a filler are introduced because of biodegradability and availability. The promising natural fiber is “ijuk” fiber from Arenga pinnata plant as a filler and polypropylene (PP) polymer as a matrix. Unfortunately, the natural fibers and polymers have the different properties on which polymers are polar while natural fibers are non-polar so that reducing the compatibility and resulting the poor crystallinity. To enhance the compatibility and crystallinity, ijuk fibers were prepared by multistage treatments including alkalinization with 5 and 10% sodium hydroxide (NaOH), oxidation with 3 and 6% sodium hypochlorite (NaClO) and hydrolysis with 20% sulphuric acid (H2SO4) in sequences. The purposes of multistage treatments are to remove the components such as lignin, wax, hemicellulose, to cause an oxidative fragmentation of remaining lignin and to annihilate the amorphous parts respectively. Fourier-Transform Infrared (FTIR) confirms the compatibility meanwhile Differential Scanning Calorimetry (DSC) reveals the crystallinity and Scanning Electron Microscope (SEM) displays surface morphology of polypropylene. The experiments were revealing that the effects of “ijuk” fibers by the multistage treatments of 5 and 10% NaOH resulting the crystallinity of polypropylene around 31.2 and 27.64% respectively compared to the crystallinity before adding the “ijuk” fibers for 16.8%. It indicates that the entire treatments increasing the compatibility and crystallinity of polypropylene. In addition, the use of 5% NaOH offers the better crystallinity than non-treated polypropylene. The experiments conclude that by adding alkalinized “ijuk” fibers of multistage treatments can increase the compatibility and crystallinity of polypropylene.

  8. Effect of pulse repetition rate and number of pulses in the analysis of polypropylene and high density polyethylene by nanosecond infrared laser induced breakdown spectroscopy

    Energy Technology Data Exchange (ETDEWEB)

    Leme, Flavio O. [Laboratorio de Quimica Analitica ' Henrique Bergamin Filho' , Centro de Energia Nuclear na Agricultura, Universidade de Sao Paulo, Av. Centenario 303, 13416-000 Piracicaba, SP (Brazil); Godoi, Quienly [Laboratorio de Quimica Analitica ' Henrique Bergamin Filho' , Centro de Energia Nuclear na Agricultura, Universidade de Sao Paulo, Av. Centenario 303, 13416-000 Piracicaba, SP (Brazil); Departamento de Quimica, Universidade Federal de Sao Carlos, Rod. Washington Luis, km 235, 13565-905 Sao Carlos, SP (Brazil); Kiyataka, Paulo H.M. [Centro de Tecnologia de Embalagens, Instituto de Tecnologia de Alimentos, Av. Brasil 2880, 13070-178 Campinas, SP (Brazil); Santos, Dario [Departamento de Ciencias Exatas e da Terra, Universidade Federal de Sao Paulo, Rua Prof. Artur Riedel 275, 09972-270 Diadema, SP (Brazil); Agnelli, Jose A.M. [Departamento de Engenharia de Materiais, Universidade Federal de Sao Carlos, Rod. Washington Luis, km 235, 13565-905 Sao Carlos, SP (Brazil); and others

    2012-02-01

    Pulse repetition rates and the number of laser pulses are among the most important parameters that do affect the analysis of solid materials by laser induced breakdown spectroscopy, and the knowledge of their effects is of fundamental importance for suggesting analytical strategies when dealing with laser ablation processes of polymers. In this contribution, the influence of these parameters in the ablated mass and in the features of craters was evaluated in polypropylene and high density polyethylene plates containing pigment-based PbCrO{sub 4}. Surface characterization and craters profile were carried out by perfilometry and scanning electron microscopy. Area, volume and profile of craters were obtained using Taylor Map software. A laser induced breakdown spectroscopy system consisted of a Q-Switched Nd:YAG laser (1064 nm, 5 ns) and an Echelle spectrometer equipped with ICCD detector were used. The evaluated operating conditions consisted of 10, 25 and 50 laser pulses at 1, 5 and 10 Hz, 250 mJ/pulse (85 J cm{sup -2}), 2 {mu}s delay time and 6 {mu}s integration time gate. Differences in the topographical features among craters of both polymers were observed. The decrease in the repetition rate resulted in irregular craters and formation of edges, especially in polypropylene sample. The differences in the topographical features and ablated masses were attributed to the influence of the degree of crystallinity, crystalline melting temperature and glass transition temperature in the ablation process of the high density polyethylene and polypropylene. It was also observed that the intensities of chromium and lead emission signals obtained at 10 Hz were two times higher than at 5 Hz by keeping the number of laser pulses constant.

  9. Enhancing the Dyeability of Polypropylene Fibers by Melt Blending with Polyethylene Terephthalate

    Directory of Open Access Journals (Sweden)

    Fereshteh Mirjalili

    2013-01-01

    Full Text Available Attempts were made to modify polypropylene fibers by melt blending with polyethylene terephthalate in order to enhance the dyeability of the resultant fiber. Five blends of polypropylene/polyethylene terephthalate/compatibilizer were prepared and subsequently spun into fibers. Three disperse dyes were used to dye such modified fibers at boiling and 130°C. The dyeing performance of the blend fibers, as well as the morphological, chemical, thermal, and mechanical properties, of the corresponding blends was characterized by means of spectrophotometry, polarized optical microscopy, scanning electron microscopy (SEM, FT-IR spectroscopy, differential scanning calorimetry (DSC, and tensile testing.

  10. Physicochemical Study of Irradiated polypropylene/Organo :Modified Montmorillonite Composites by Using Electron Beam Irradiation Technique

    International Nuclear Information System (INIS)

    Hassan, M.S.

    2008-01-01

    Polypropylene/ Organo modified montmorillonite composites (PP/ OMMT) were prepared by melt blending with a twin screw extruder. The thermal properties by thermo gravimetric analysis (TGA), the dispersion of OMMT of macromolecules by X-ray diffraction (XRD), mechanical properties and the morphology by scanning electron microscopy (SEM) were investigated. The effect of electron beam irradiation on these properties was also studied. The results showed an intercalation between the silicate layers and the PP polymer matrix. The (PP/ OMMT) composites exhibit higher thermal stability and lower mechanical properties than pure polypropylene

  11. Development of a Halogen Free Flame Retardant Masterbatch for Polypropylene Fibers

    Directory of Open Access Journals (Sweden)

    François Rault

    2015-02-01

    Full Text Available The efficiency of new phosphinates, in combination with melamine cyanurate, was studied using different polypropylene textile structures. The influence of different ratios up to a total amount of 6 wt% in the polypropylene fiber was investigated using the limiting oxygen index (LOI and cone calorimeter method for research purposes, while the performances were correlated to the standards FMVSS 302 (Federal Motor Vehicle Safety Standards and DIN 4102-l (Deutsches Institut für Normung used more specifically for automotive and building sector.

  12. The relationship between compressive strength and flexural strength of pavement geopolymer grouting material

    Science.gov (United States)

    Zhang, L.; Han, X. X.; Ge, J.; Wang, C. H.

    2018-01-01

    To determine the relationship between compressive strength and flexural strength of pavement geopolymer grouting material, 20 groups of geopolymer grouting materials were prepared, the compressive strength and flexural strength were determined by mechanical properties test. On the basis of excluding the abnormal values through boxplot, the results show that, the compressive strength test results were normal, but there were two mild outliers in 7days flexural strength test. The compressive strength and flexural strength were linearly fitted by SPSS, six regression models were obtained by linear fitting of compressive strength and flexural strength. The linear relationship between compressive strength and flexural strength can be better expressed by the cubic curve model, and the correlation coefficient was 0.842.

  13. Electrolytic Hydrogen obtaining by a photovoltaic source

    International Nuclear Information System (INIS)

    Pasculete, E.; Condrea, F.; Stanoiu, L.

    2005-01-01

    At present, the developed countries allocate large funds for the financing of some global programs for fundamental and applicative research for development of hydrogen non-conventional production technologies. One of these technologies is the photo-assisted electrolysis. This technology is adopted in the research, which results are presented in this paper. The experimental model includes as basic equipment 100 W photovoltaic source, electrolysis battery press filter type, control unit of the electric energy discharged, accumulator, hydrogen storage unit. Five types of material have been tested for the electrolysis cell diaphragm: asbestos; Netrom- unwoven material from fibers of polypropylene; ion changing composite membrane - polysulfone support with an active layer of sulfonated poly-sulfone (PSS/PSJ) and poly-sulfone support with an active layer of sulfonated poly-eter cetone (SPEEK/PSf); ion-exchange membrane made from sulfonated poly-eter cetone (SPEEK). The graphics and results from the test system are presented. The analysis of the experimental results lead to the establishment of the optimal configuration of battery and of the operational conditions of the assembly. The experimental results give the opportunity to obtain electrolytic hydrogen with a photovoltaic source, in an efficient system, and promote the Romanian research at a level of a demonstrative installation

  14. Characterization of liquid products from the co-cracking of ternary and quaternary mixture of petroleum vacuum residue, polypropylene, Samla coal and Calotropis Procera

    Energy Technology Data Exchange (ETDEWEB)

    M. Ahmaruzzaman; D.K. Sharma [Indian Institute of Technology Delhi, New Delhi (India). Centre for Energy Studies

    2008-08-15

    The co-cracking of the petroleum vacuum residue (XVR) with polypropylene (PP), Samla coal (SC) and Calotropis procera (CL) has been carried out in a batch reactor under isothermal conditions at atmospheric pressure. The liquids obtained by co-cracking have been characterized by Fourier transform infrared spectroscopy, high performance liquid chromatography, {sup 1}H nuclear magnetic resonance (NMR), {sup 13}C NMR, gel permeation chromatography (GPC), and inductively coupled argon plasma analyses. It was found that the liquid products obtained from the co-cracking of ternary and quaternary mixtures of the petroleum vacuum residue with polypropylene, coal and C. procera contained less than 1 ppm of Ni and V. The HPLC analyses indicates that the liquids obtained from the cracking of ternary mixture of XVR+PP+CL were mainly aliphatic in nature (saturates content 87.4%). NMR analyses showed that the aromatic carbon contents decreased (15.0%) in the liquid products derived from the co-cracking of quaternary mixtures of XVR+PP+SC+CL compared to their theoretical averages (taking the averages of aromatic carbon contents of the liquids from XVR, PP, SC and CL individually). The overall results indicated that there exists a definite interaction of reactive species when XVR, PP, SC and CL were co-cracked together. 27 refs., 5 tabs.

  15. Effect Of RPC Compositions On: Compressive Strength and Absorption

    Directory of Open Access Journals (Sweden)

    Ahmed Sultan Ali

    2016-03-01

    Full Text Available Concrete is a critical material for the construction of infrastructure facilities throughout the world. A new material known as Reactive Powder Concrete (RPC, or sometimes called Ultra-High Performance Concrete (UHPC, is becoming available that differs significantly from traditional concretes. It is an ultra high strength and high ductility composite material with advanced mechanical properties. It consists of special concrete whose microstructure is optimized by precise gradation of all particles in the mix to yield maximum density. Different RPC mixes in the experimental investigation of the present study the mechanical properties of RPC including compressive strength, density and absorption. The main variables used in the production of the different RPC mixes of the present research are three, namely, type of pozzolanic admixture (metakaolin, micro silica, and silica fume, type of fibers (steel and polypropylene fibers and volume fraction of fibers (1.0,1.5, and 2.0%. The experimental results indicated that RPC mixes with silica fume gave the highest values of compressive strength and density and lowest value of absorption in comparison with RPC using micro silica or metakaolin where metakaolin was the third in such comparisons. However the RPC mixes used in the present investigation gave group compressive strength ranging between 164 -195 MPa. It was also found that the use of steel fibers with high volume fraction (2% in an RPC mix increases the compressive strength by 8% and density of the concrete by 2.5% and reduces its absorption by 13%, unlike an RPC mix using polypropylene fibers of lesser volume fraction.

  16. Evaluation of in-place concrete strength by core testing.

    Science.gov (United States)

    2016-11-01

    The overall objective of the work contained in this report is to develop an ALDOT procedure to evaluate core strength results obtained under various conditions. Since there are many factors that influence the apparent strength of cores, strength corr...

  17. Bond strength of masonry

    NARCIS (Netherlands)

    Pluijm, van der R.; Vermeltfoort, A.Th.

    1992-01-01

    Bond strength is not a well defined property of masonry. Normally three types of bond strength can be distinguished: - tensile bond strength, - shear (and torsional) bond strength, - flexural bond strength. In this contribution the behaviour and strength of masonry in deformation controlled uniaxial

  18. Chondrocyte behavior on nanostructured micropillar polypropylene and polystyrene surfaces

    Energy Technology Data Exchange (ETDEWEB)

    Prittinen, Juha [Department of Applied Physics, University of Eastern Finland, Kuopio (Finland); Jiang, Yu [Department of Chemistry, University of Eastern Finland, Joensuu (Finland); Ylärinne, Janne H. [Department of Applied Physics, University of Eastern Finland, Kuopio (Finland); Pakkanen, Tapani A. [Department of Chemistry, University of Eastern Finland, Joensuu (Finland); Lammi, Mikko J., E-mail: mikko.lammi@uef.fi [Department of Applied Physics, University of Eastern Finland, Kuopio (Finland); Qu, Chengjuan [Department of Applied Physics, University of Eastern Finland, Kuopio (Finland)

    2014-10-01

    This study was aimed to investigate whether patterned polypropylene (PP) or polystyrene (PS) could enhance the chondrocytes' extracellular matrix (ECM) production and phenotype maintenance. Bovine primary chondrocytes were cultured on smooth PP and PS, as well as on nanostructured micropillar PP (patterned PP) and PS (patterned PS) for 2 weeks. Subsequently, the samples were collected for fluorescein diacetate-based cell viability tests, for immunocytochemical assays of types I and II collagen, actin and vinculin, for scanning electronic microscopic analysis of cell morphology and distribution, and for gene expression assays of Sox9, aggrecan, procollagen α{sub 1}(II), procollagen α{sub 1}(X), and procollagen α{sub 2}(I) using quantitative RT-PCR assays. After two weeks of culture, the bovine primary chondrocytes had attached on both patterned PP and PS, while practically no adhesion was observed on smooth PP. However, the best adhesion of the cells was on smooth PS. The cells, which attached on patterned PP and PS surfaces synthesized types I and II collagen. The chondrocytes' morphology was extended, and an abundant ECM network formed around the attached chondrocytes on both patterned PP and PS. Upon passaging, no significant differences on the chondrocyte-specific gene expression were observed, although the highest expression level of aggrecan was observed on the patterned PS in passage 1 chondrocytes, and the expression level of procollagen α{sub 1}(II) appeared to decrease in passaged chondrocytes. However, the expressions of procollagen α{sub 2}(I) were increased in all passaged cell cultures. In conclusion, the bovine primary chondrocytes could be grown on patterned PS and PP surfaces, and they produced extracellular matrix network around the adhered cells. However, neither the patterned PS nor PP could prevent the dedifferentiation of chondrocytes. - Highlights: • Methods to avoid chondrocyte dedifferentiation would be useful for cartilage

  19. Effects of Polypropylene Orientation on Mechanical and Heat Seal Properties of Polymer-Aluminum-Polymer Composite Films for Pouch Lithium-Ion Batteries

    Directory of Open Access Journals (Sweden)

    Fangxinyu Zeng

    2018-01-01

    Full Text Available In this study, polyamide-aluminum foil-polypropylene (PA-Al-PP composite films with different orientation status of the PP layer were prepared, and their morphology, tensile, peeling and heat seal behavior were studied. The comparative study of tensile and fracture behaviors of single-layer film of PA, Al and PP, as well as the composite films of PA-Al, PP-Al and PA-Al-PP revealed that in PA-Al-PP composite film, the PA layer with the highest tensile strength can share the tensile stress from the Al layer during stretching, while the PP layer with the lowest tensile strength can prevent further development of the small cracks on boundary of the Al layer during stretching. Moreover, the study of heat seal behavior suggested that both the orientation status and the heat seal conditions were important factors in determining the heat seal strength (HSS and failure behavior of the sample. Four failure types were observed, and a clear correspondence between HSS and failure types was found. The results also elucidated that for the composite film, only in the cases where the tensile stress was efficiently released by each layer during HSS measurement could the composite film exhibit desired high HSS that was even higher than its tensile strength.

  20. Alumina/Phenolphthalein Polyetherketone Ceramic Composite Polypropylene Separator Film for Lithium Ion Power Batteries

    International Nuclear Information System (INIS)

    Wang, Jing; Hu, Zhiyu; Yin, Xiunan; Li, Yunchao; Huo, Hong; Zhou, Jianjun; Li, Lin

    2015-01-01

    Highlights: • PEK-C (T g : ∼230 °C) was used as binder to prepare ceramic coated composite PP separator. • The composite PP separator was stable and showed low thermal shrinkage in the electrolyte solvent. • The composite PP separator was helpful for high current density discharge. • The composite PP separator improved the safety performance of the coin cells. - Abstract: One way to obtain the lithium ion power battery with better safety performance was to increase the thermal shrinkage resistance of the separator at higher temperature. Phenolphthalein polyetherketone (PEK-C) is a polymer that can withstand high temperature to about 230 °C. Here, we developed a new Al 2 O 3 coated composite polypropylene (PP) separator with PEK-C as binder. The coating layer was formed on the surface of the PP separator and both ceramic particles and binder did not infiltrated into the separator along the thickness direction. The composite separator with 4 μm coating layer provided balanced permeability and thermal shrinkage properties. The composite separator was stable at the electrochemical window for lithium ion battery. The coin cells with composite separator showed better charge/discharge performance than that of the cells with the PP separator. It seemed that the composite separator was helpful for high current density discharge. Also, the battery safety performance test had verified that the Al 2 O 3 coated composite separator with PEK-C as binder had truly improved the safety performance of the coin cells. So, the newly developed Al 2 O 3 coated composite PP separator was a promising safety product for lithium ion power batteries with high energy density

  1. Fracture resistance improvement of polypropylene by joint action of core-shell particles and nucleating agent

    International Nuclear Information System (INIS)

    Yang Gang; Han Liang; Ding Haifeng; Wu Haiyan; Huang Ting; Li Xiaoxi; Wang Yong

    2011-01-01

    Research highlights: →The core-shell particles, which were prepared from melt blending of POE and nano-CaCO 3 , and different nucleating agents (α-form NA or β-form NA) were first introduced into PP to prepare the super toughened PP materials. →NAs control the crystalline structures of PP matrix including the spherulites diameter and the crystal form. →NAs and core-shell particles exhibit apparent joint effect in improving the fracture resistance of PP. - Abstract: As a serial work about the fracture resistance improvement of polypropylene (PP), this work reports the joint effect of core-shell particles and nucleating agent (NA) on the microstructure and fracture resistance of PP. Core-shell particles were prepared through melt blending of ethylene-octene copolymer (POE) and calcium carbonate (CaCO 3 ). Different NA, i.e. α-form NA (P-tert-butylbenzoic acid-Al, MD-NA-28) and β-form NA (aryl amides compound, TMB-5) were introduced into PP matrix to control the crystalline structure. The phase morphology of POE and the distribution of CaCO 3 were characterized by using scanning electron microscope (SEM), and the crystallization behavior of PP matrix were investigated by using differential scanning calorimetry (DSC), wide angle X-ray diffraction (WAXD) and polarization optical microscope (POM). The mechanical properties were obtained through universal tensile measurement and notched Izod impact measurement. Surprisingly, the results show that through addition of so-called core-shell particles and NA simultaneously, the fracture resistance of PP can be dramatically improved.

  2. Experimental and analytical study of the DC breakdown characteristics of polypropylene laminated paper with a butt gap condition considering the insulation design of superconducting cable

    Science.gov (United States)

    Seo, In-jin; Choi, Won; Seong, Jae-gyu; Lee, Bang-wook; Koo, Ja-yoon

    2014-08-01

    It has been reported that the insulation design under DC stress is considered as one of the critical factors in determining the performance of high-voltage direct current (HVDC) superconducting cable. Therefore, it is fundamentally necessary to investigate the DC breakdown characteristics of the composite insulation system consisting of liquid nitrogen (LN2)/polypropylene-laminated-paper (PPLP). In particular, the insulation characteristics under DC polarity reversal condition should be verified to understand the polarity effect of the DC voltage considering the unexpected incidents taking place at line-commutated-converters (LCC) under service at a DC power grid. In this study, to examine the variation of DC electric field strength, the step voltage and polarity reversal breakdown tests are performed under DC stress. Also, we investigate the electric field distributions in a butt gap of the LN2/PPLP condition considering the DC polarity reversal by using simulation software.

  3. Obtaining of inulin acetate

    OpenAIRE

    Khusenov, Arslonnazar; Rakhmanberdiev, Gappar; Rakhimov, Dilshod; Khalikov, Muzaffar

    2014-01-01

    In the article first obtained inulin ester inulin acetate, by etherification of inulin with acetic anhydride has been exposed. Obtained product has been studied using elementary analysis and IR spectroscopy.

  4. Supercritical CO2 foaming of radiation crosslinked polypropylene/high-density polyethylene blend: Cell structure and tensile property

    Science.gov (United States)

    Yang, Chenguang; Xing, Zhe; Zhang, Mingxing; Zhao, Quan; Wang, Mouhua; Wu, Guozhong

    2017-12-01

    A blend of isotactic polypropylene (PP) with high-density polyethylene (HDPE) in different PP/HDPE ratios was irradiated by γ-ray to induce cross-linking and then foamed using supercritical carbon dioxide (scCO2) as a blowing agent. Radiation effect on the melting point and crystallinity were analyzed in detail. The average cell diameter and cell density were compared for PP/HDPE foams prepared under different conditions. The optimum absorbed dose for the scCO2 foaming of PP/HDPE in terms of foaming ability and cell structure was 20 kGy. Tensile measurements showed that the elongation at break and tensile strength at break of the crosslinked PP/HDPE foams were higher than the non-crosslinked ones. Of particular interest was the increase in the foaming temperature window from 4 ℃ for pristine PP to 8-12 ℃ for the radiation crosslinked PP/HDPE blends. This implies much easier handling of scCO2 foaming of crosslinked PP with the addition of HDPE.

  5. Effects of electron beam radiation dose on the compatibilization behaviour in recycled polypropylene/microcrystalline cellulose composites

    Science.gov (United States)

    Samat, N.; Motsidi, S. N. R.; Lazim, N. H. M.

    2018-01-01

    The purpose of this research was to evaluate the influence of dose level of electron beam on the compatibilization behavior of recycled polypropylene (rPP) in rPP/microcrystalline cellulose (MCC) composites. Initially, the rPP was irradiated with various dose of electron beam (5 kGy up to 250 kGy) which then mixed with unirradiated rPP (u-rPP) at a ratio of 30:70 respectively. The composites were prepared by incorporating a series wt% of MCC fibers into rPP (u-rPP : i-rPP) using extruder and finally moulded with an injection moulding machine. The compatibility behavior of irradiated rPP (i-rPP) were analysed with mechanical tensile and thermal methods. The results of mechanical analysis showed great improvement in tensile modulus but an increase in radiation dosage gradually decreased this property. Nevertheless, the tensile strength exhibited a minor effect. The thermal stability of composites is lowered with increase in the absorbed dose, more significantly at higher content of MCC. Fracture surface observations reveal adhesion between the cellulose and rPP matrix.

  6. The impact of the amount of polypropylene fibres on spalling behaviour and residual mechanical properties of Reactive Powder Concretes

    Directory of Open Access Journals (Sweden)

    Hager I.

    2013-09-01

    Full Text Available In this paper, an experimental study on the spalling behaviour and mechanical properties of Reactive Powder Concretes (RPCs in high temperature are presented. The research program was established to evaluate the impact of low melting temperature polypropylene fibres PP on mechanical properties evolution with temperature but also to verify the effectiveness of their addition to prevent spalling. Three sets of RPC specimens were prepared for this study with different amount of PP fibres (no fibres, 1.0 kg/m3 and 2.0 kg/m3. The addition of PP fibres reduces the initial compressive strength of the RPC material by approx. 14% no significant influence on modulus of elasticity was observed. Addition of 1 kg/m3 of PP fibres in RPC, seem not to give a sufficient protection against occurrence of spalling phenomenon. By adding 2 kg/m3 of PP fibres the risk of spalling is significantly reduced.

  7. Effect of cellulose nanocrystals (CNC) particle morphology on dispersion and rheological and mechanical properties of polypropylene/CNC nanocomposites.

    Science.gov (United States)

    Khoshkava, Vahid; Kamal, Musa R

    2014-06-11

    Polypropylene (PP) nanocomposites containing spray-dried cellulose nanocrystals (CNC), freeze-dried CNC, and spray-freeze-dried CNC (CNCSFD) were prepared via melt mixing in an internal batch mixer. Polarized light, scanning electron, and atomic force microscopy showed significantly better dispersion of CNCSFD in PP/CNC nanocomposites compared with the spray-dried and freeze-dried CNCs. Rheological measurements, including linear and nonlinear viscoelastic tests, were performed on PP/CNC samples. The microscopy results were supported by small-amplitude oscillatory shear tests, which showed substantial rises in the magnitudes of key rheological parameters of PP samples containing CNCSFD. Steady-shear results revealed a strong shear thinning behavior of PP samples containing CNCSFD. Moreover, PP melts containing CNCSFD exhibited a yield stress. The magnitude of the yield stress and the degree of shear thinning behavior increased with CNCSFD concentration. It was found that CNCSFD agglomerates with a weblike structure were more effective in modifying the rheological properties. This effect was attributed to better dispersion of the agglomerates with the weblike structure. Dynamic mechanical analysis showed considerable improvement in the modulus of samples containing CNCSFD agglomerates. The percolation mechanical model with modified volume percolation threshold and filler network strength values and the Halpin-Kardos model were used to fit the experimental results.

  8. Thermoplastic polyolefins as formaldehyde free binders in highly filled lignocellulosic panel boards: using glycerine as a processing aid in kenaf fiber polypropylene boards

    Directory of Open Access Journals (Sweden)

    Anand Ramesh Sanadi

    2008-12-01

    Full Text Available A new technique was developed to make highly loaded (up to 95% formaldehyde free natural fiber boards. The purpose of the paper is to report a broad study on 85% kenaf boards using linear thermoplastic polymers as the binder in preparing the boards to determine if these materials have potential in commercial applications by comparing them to other commercial materials. In these materials, linear thermoplastic polymer chains act as an adhesive and the product resembles a typical wood based panel (e.g., phenol formaldehyde fiber board. The process involved the use of small amount of glycerine in the fiber to enhance processibility in a thermo-kinetic mixer followed by hot pressing. In this paper, we report the properties of 85% by weight kenaf fiber boards using polypropylene as the adhesive. A maleated polypropylene was used to improve the adhesion and stress transfer between the adhesive and kenaf fiber. The addition of 2% by weight of glycerine based on the dry weight of kenaf fiber resulted in the best properties of the boards. Differential scanning calorimetric studies suggested that the glycerine had a little effect on the percent crystallinity of the matrix. Dynamic mechanical tests of the 85% boards showed some differences compared to conventional 60% by weight kenaf-PP composites. The 85% kenaf boards had a flexural strength of 75 MPa and a flexural modulus of 6.8 GPa with a specific gravity of 1.24. These properties are comparable to standard formaldehyde free high density hardboards with flexural strengths of 48.3 MPa and flexural modulus of 5.5 GPa, and a specific gravity of 1.28. This paper gives a broad overview of an initial study of these new materials.

  9. Mechanical performance of hemp fiber polypropylene composites at different operating temperatures

    Science.gov (United States)

    Mehdi Tajvidi; Nazanin Motie; Ghonche Rassam; Robert H. Falk; Colin Felton

    2010-01-01

    In order to quantify the effect of temperature on the mechanical properties of hemp fiber polypropylene composites, formulations containing 25% and 40% (by weight) hemp fiber were produced and tested at three representative temperatures of 256, 296, and 336 K. Flexural, tensile, and impact tests, as well as dynamic mechanical analysis, were performed and the reduction...

  10. Spatially Resolved Characterization of Cellulose Nanocrystal-Polypropylene Composite by Confocal Raman Microscopy

    Science.gov (United States)

    Umesh P. Agarwal; Ronald Sabo; Richard S. Reiner; Craig M. Clemons; Alan W. Rudie

    2012-01-01

    Raman spectroscopy was used to analyze cellulose nanocrystal (CNC)–polypropylene (PP) composites and to investigate the spatial distribution of CNCs in extruded composite filaments. Three composites were made from two forms of nanocellulose (CNCs from wood pulp and the nanoscale fraction of microcrystalline cellulose) and two of the three composites investigated used...

  11. Properties and Semicrystalline Structure Evolution of Polypropylene/Montmorillonite Nanocomposites under Mechanical Load

    DEFF Research Database (Denmark)

    Stribeck, Norbert; Zeinolebadi, Ahmad; Ganjaee Sari, Morteza

    2012-01-01

    Small-angle X-ray scattering (SAXS) monitors tensile and load-cycling tests of metallocene isotactic polypropylene (PP), a blend of PP and montmorillonite (MMT), and two block copolymer compatibilized PP/MMT nanocomposites. Mechanical properties of the materials are similar, but the semicrystalline......%. Other results concern the evolution of Strobl’s block structure and void formation during tensile loading....

  12. Influence of postdrawing temperature on mechanical properties of melt-spun isotactic polypropylene

    NARCIS (Netherlands)

    Schimanski, T.; Peijs, A.A.J.M.; Lemstra, P.J.; Loos, J.

    2004-01-01

    Mech. properties of melt-spun and postdrawn isotactic polypropylene (iPP) are studied to examine the dependence on the temp. in the postdrawing stage. In accordance with the literature, the Young's modulus is uniquely detd. by the applied draw ratio. However, we found that the overall mech. behavior

  13. Modification of polycarbonate and polypropylene surfaces by argon ion cluster beams

    Czech Academy of Sciences Publication Activity Database

    Biederman, H.; Slavinská, D.; Boldyreva, H.; Lehmberg, H.; Takaoka, G.; Matsuo, J.; Kinpara, H.; Zemek, Josef

    2001-01-01

    Roč. 19, č. 6 (2001), s. 2050-2056 ISSN 0734-2101 R&D Projects: GA MŠk ME 177 Institutional research plan: CEZ:AV0Z1010914; CEZ:MSM113200002 Keywords : polycarbonate * polypropylene * surfometer * atomic force microscop * X-ray photoelectron spectroscopy Subject RIV: BM - Solid Matter Physics ; Magnetism Impact factor: 1.448, year: 2001

  14. Influence of Wind Speed on Heat Flow through Polypropylene Insulating Material

    Institute of Scientific and Technical Information of China (English)

    SUN Yu-chai; CHENG Zhong-hao; FENG Xun-wei

    2006-01-01

    The heat transfer properties of polypropylene insulation at different ambient temperature against wind were analysed.A theoretical model of the combined conductive, convective and radiative heat flow through fibrous insulating material was presented. Detail study was carried out by using the finite element method. The theoretical results are in accordance to the experimental results which were accomplished in an artificial climate chamber.

  15. Polypropylene Darning: A New Alternative for Reconstruction of Orbital Floor after Total Maxillectomy.

    Science.gov (United States)

    Sharma, Prashant

    2015-06-01

    Removal of orbital floor is an integral part of total (radical) maxillectomy (type IIIa), which if not managed properly, may lead to some eye related distressing complications like diplopia, eyelid malposition, epiphora, dacryocystitis, enopthalmos and ectoprion. Among all, diplopia is the most distressing complication which hampers daily activity. Various options for orbital floor reconstruction are available like titanium sheet, polypropylene mesh, non-vascularized or vascularized bone graft, pedicled flaps, micro-vascular free flaps, prosthesis placement, and split skin graft followed by obturator placement. Till date no-body has tried stabilization of eye ball by 'darning' the orbital floor using non-absorbable suture. 'Polypropylene suture darning' is an easy to learn, novel method with equally good results. Five patients with potentially resectable tumors underwent total maxillectomy. I used polypropylene 3-0 round body suture and 'darning' was done at orbital floor, incorporating periosteum (if remaining) and peri-orbital fat into the sutures. Muscle flaps were done to provide bulk and palatal reconstruction. Assessment of patients was done post-operatively at day-5 i.e., before discharge and at 1 month after surgery, and also in further follow up visits. The results were very good in terms of clear vision & eye movements (directly related to 'darning'), and the aesthetic look of patients and bilateral symmetry were satisfactory (not related to darning). Darning of orbital floor by polypropylene after total maxillectomy is an easy to learn and cost-effective method of reconstruction with good results.

  16. Prediction of yield and long-term failure of oriented polypropylene: kinetics and anisotropy

    NARCIS (Netherlands)

    van Erp, T.B.; Reynolds, C.T.; Peijs, T.; van Dommelen, J.A.W.; Govaert, L.E.

    2009-01-01

    The time-dependent yield and failure behavior of off-axis loaded uniaxially oriented polypropy-lene tape is investigated. The yield and failure behavior is described with an anisotropic vis-coplastic model. A viscoplastic flow rule is used with an equivalent stress, based on Hill’sanisotropic yield

  17. Rate-, temperature-, and structure-dependent yield kinetics of isotactic polypropylene

    NARCIS (Netherlands)

    Erp, van T.B.; Cavallo, D.; Peters, G.W.M.; Govaert, L.E.

    2012-01-01

    The influence of cooling rate on the structure and resulting mechanical performance is explored for a set of isotactic polypropylenes with varying molecular weight, insertion of counits, and addition of a nucleating agent. A continuous variation of crystal type (a–mesomorphic phase competition) and

  18. Flow-induced solidification of high-impact polypropylene copolymer compositions : morphological and mechanical effects

    NARCIS (Netherlands)

    Drongelen, van M.; Gahleitner, M.; Spoelstra, A.B.; Govaert, L.E.; Peters, G.W.M.

    2015-01-01

    Polypropylene-based impact copolymers are a complex composition of matrix material, a dispersed phase and many optional modifiers. The final heterophasic morphology of such systems is influenced significantly by the processing step, adding an additional level of complexity to understanding the

  19. Origin of toughness in .beta.-polypropylene: the effect of molecular mobility in the amorphous phase

    Czech Academy of Sciences Publication Activity Database

    Policianová, Olivia; Hodan, Jiří; Brus, Jiří; Kotek, Jiří

    2015-01-01

    Roč. 60, 9 March (2015), s. 107-114 ISSN 0032-3861 R&D Projects: GA ČR(CZ) GA13-29009S Institutional support: RVO:61389013 Keywords : isotactic polypropylene * β-modification * toughness Subject RIV: JI - Composite Materials Impact factor: 3.586, year: 2015

  20. Interfacial interactions of poly(urethane-urea) based primers with polypropylene

    NARCIS (Netherlands)

    Villani, M.; Scheerder, J. (Jeroen); Benthem, van R.A.T.M.; With, de G.

    2014-01-01

    Good adhesion to polypropylene is required in a number of technologies including printing, painting and food packaging technology. However, for good adhesion between polyolefins and other materials it is usually necessary to pretreat and prime the polyolefinic substrate. In this paper waterborne