WorldWideScience

Sample records for steel-x6crni1811

  1. Low and high cycle fatigue behaviour of steel-X6CRNI1811 (Type 304 SS) in air and flowing sodium

    International Nuclear Information System (INIS)

    Huthmann, H.; Jenner, G.

    Strain controlled LCF-tests were performed on X6CrNi1811 steel (Type 304 SS) in air and flowing sodium in a non-isothermal sodium loop. The results measured at 550 deg. C in an upstream position of the sodium loop show an increase in fatigue life in the strain range from about 1.5% to 0.4% for the base material in the as-received condition while the welded joints remain unaffected by the environment. The LCF-behaviour of base material specimens tested at 500 deg. C in a downstream position after a prior pre-exposure to sodium (4058 h, 500 deg. C) is also improved in comparison to parallel specimens tested in air with comparable thermal aging. Load controlled HCF-tests performed on X6CrNi1811 steel at 550 deg. C show a significant increase in fatigue life in the low cycle region (Nsub(f) 6 cycles) and a higher endurance limit for the base material in sodium but no influence of the environment is indicated for the welded joints. (author)

  2. Creep-rupture-strength and creep-behaviour of stainless steel X6CrNi 1811(DIN 1.4948); Comportamiento a la fluencia lenta del acero X6CrNi 1811 (1.4948)

    Energy Technology Data Exchange (ETDEWEB)

    Solano, R R; Schirra, M; Rivas, M de la; Seith, B

    1977-07-01

    The steel X6CrNi 1811 (DIN 1.4948) that will be used as a structure material for the German Fast Breeder Reactor SNR 300 was creep-tested in a temperature range of 550-650 degree centigree under base material condition as well as welded material condition. Tests are foreseen up to 30.000 hours with a continuous measuring of the elongation. The present report describes the test results up to about 4-000 hours. Taking into account the results of other programs carried out with the same material between 550- and 600 degree centigree at similar rupture time, were defined the stresses for the long term tests. The main point of this program (Extrapolation Program) lies in the knowledge of the creep-rupture-strength and creep behaviour of the structure materials up to 3.10{sup 4}h at high temperature in order to extrapolate up to 10{sup 5} h. for reactor operating temperatures. (Author) 14 refs.

  3. Creep-rupture-strength and creep-behaviour of stainless steel X6CrNi 1811 (DIN 1.4948)

    International Nuclear Information System (INIS)

    Solano, R.R.; Rivas, M. de las; Schirra, M.; Seith, B.

    1976-10-01

    The steel X6CrNi 1811 (DIN 1.4948) that will be used as a structure material for the German fast breeder reactor SNR 300 was creep-tested in a temperature range of 550-650 0 C under base material condition as well as welded material condition. Tests are foreseen up to 30.000 hours with a continuous measuring of the elongation. The present report describes the test results up to about 5.000 hours. Taking into account the results of other programs carried out with the same material between 550 and 600 0 C at similar rupture times, were defined the stresses for the long term tests. The main point of this program ('Extrapolation Program') lies in the knowledge of the creep time and creep behaviour of the structure materials up to 3 x 10 4 h at high temperature in order to extrapolate up to 10 5 h for operating temperatures. (orig.) [de

  4. Creep-rupture-strength and creep-behaviour of stainless steel X6CrNi 1811 (DIN 1.4948)

    International Nuclear Information System (INIS)

    Solano, R.R.; Rivas, M. de las; Seith, B.; Schirra, M.

    1977-01-01

    The steel X6CrNi 1811 (DIN 1.4948) that will be used as a structure material for the german fast breder reactor SNR 300, was creep-tested in a temperature range of 550-650 deg C under base material condition as well as welded material condition. Tests are foreseen up to 30.000 hours with a continous measuring of the elongation. The test results up to about 4.000 hours is described. Taking into account the results of other programs carried out with the same material between 550 and 600 deg C at similar rupture time, were defined the stresses for the longterm test. The main point of this program (''Extrapolation Program'') lies in the knowledge of the creep-rupture-strength and creep behaviour of the structure materials up to 3.10 4 h at high temperature in order to extrapolate up to 10 5 h for reactor operating temperatures. (author) [es

  5. Creep-rupture-strength and creep-behaviour of stainless steel X6CrNi 1811(DIN 1.4948)

    International Nuclear Information System (INIS)

    Solano, R. R.; Schirra, M.; Rivas, M. de la; Seith, B.

    1977-01-01

    The steel X6CrNi 1811 (DIN 1.4948) that will be used as a structure material for the German Fast Breeder Reactor SNR 300 was creep-tested in a temperature range of 550-650 degree centigree under base material condition as well as welded material condition. Tests are foreseen up to 30.000 hours with a continuous measuring of the elongation. The present report describes the test results up to about 4-000 hours. Taking into account the results of other programs carried out with the same material between 550- and 600 degree centigree at similar rupture time, were defined the stresses for the long term tests. The main point of this program (Extrapolation Program) lies in the knowledge of the creep-rupture-strength and creep behaviour of the structure materials up to 3.10 4 h at high temperature in order to extrapolate up to 10 5 h. for reactor operating temperatures. (Author) 14 refs

  6. Creep-rupture-tests on thestainless steel X6 CrNi1811 (DIN 1.4948) in the frame of the ''Extrapolation-Program'' Pt. 2

    International Nuclear Information System (INIS)

    Solano, R.R.; Barroso, S.; Rivas, M. de las; Schirra, M.; Seith, B.

    1979-01-01

    The austenitic stainless steel X6 CrNi 1811 (DIN 1.4948) that is used as a structure material for the German Fast Breeder Reactor SNR 300 was creep tested in a temperature range of 550-650 deg under base material condition as well as welded material condition. The main point of this program (''Extrapolation-Program'') lies in the knowledge of the cree-rupture-strength and creep-behaviour up to 3X10 - 4 hours at higher temperatures in order to extrapolate up to (>=)10 5 hours for operating temperatures. In order to study the stress dependency of the minimum creep rate additional tests were carried out over temperature range 550 deg - 750 deg C. The present report describes the state in the running program with test-time up to 35.000 hours. Besides the cree-rupture behaviour it is possible to make a distinct quantitative statement for the creep-behaviour and ductility. Extensive metallographic examinations show the fracture behaviour and changes in structure. (author)

  7. Creep-rupture-test on the stainless steel X6CRNI1811 (DIN 1.4948) in the frame of the ''Extrapolation-Program''. (Part III)

    International Nuclear Information System (INIS)

    Solano, R.; Las Rivas, M. de; Barroso, S.

    1982-01-01

    The austenitic stainless steel X6CrNi1811 (DIN 1.4948) used as a structure material for the German Fast Breeder Reactor SNR 300 was creep tested in a temperature range of 550-650 deg under base material condition as well as welded material condition. The main point of this program (''Extrapolation-Program'') lies in the knowledge of the creep-rupture-strength and creepbehaviour up to 3 x 10 4 hours at higher temperatures in order to extrapolate up to >=10 5 hours for operating temperatures. In order to study the stress dependency of the minimum creep rate additional tests were carried out of 550 deg - 750 deg C. The present report describes the state in the running program with test-times of 23.000 hours and results from tests up to 55.000 hours belonging to other parallel programs are taken into account. Besides the creep-rupture behaviour it is also made a study of ductility between 550 and 750 deg C. Extensive metallographic examinations have been made to study the fracture behaviour and changes in structure. (author)

  8. Creep-rupture-test on the stainless steel X6crni1811 (Din 1.494.8) in the frame of the Extrapolation-Program. (Part III)

    International Nuclear Information System (INIS)

    Solano, R.; Schirra, M.; Rivas, M. de la; Barroso, S.; Seith, B.

    1982-01-01

    The austenitic stainless steel X6crni1811 (Din 1.4948) used as a structure material for the German Fast Breeder Reactor SNR 300 was creep tested in a temperature range of 550-650 degree centigree material condition as well as welded material condition. The main point of this program (Extrapolation-Program) lies in the knowledge of the creep-rupture-strength and creep-behaviour up to 3 x 10 4 hours higher temperatures in order to extrapolated up to ≥10 5 hours for operating temperatures. In order to study the stress dependency of the minimum creep rate additional tests were carried out of 550 degree centigree - 750 degree centigree. The present report describes the state in the running program with test-times of 23.000 hours and results from tests up to 55.000 hours belonging to other parallel programs are taken into account. Besides the creep-rupture behaviour it is also made a study of ductility between 550 and 750 degree centigree. Extensive metallographic examinations have been made to study the fracture behaviour and changes in structure. (Author)

  9. Creep-rupture-test on the stainless steel X6crni1811 (Din 1.494.8) in the frame of the Extrapolation-Program. (Part III); Ensayos de fluencia lenta en el acero inoxidable X6 Cr Ni 1811 (1.4948) en el marco del Programa Extrapolacion

    Energy Technology Data Exchange (ETDEWEB)

    Solano, R; Schirra, M; Rivas, M de la; Barroso, S; Seith, B

    1982-07-01

    The austenitic stainless steel X6crni1811 (Din 1.4948) used as a structure material for the German Fast Breeder Reactor SNR 300 was creep tested in a temperature range of 550-650 degree centigree material condition as well as welded material condition. The main point of this program (Extrapolation-Program) lies in the knowledge of the creep-rupture-strength and creep-behaviour up to 3 x 10{sup 4} hours higher temperatures in order to extrapolated up to {>=}10{sup 5} hours for operating temperatures. In order to study the stress dependency of the minimum creep rate additional tests were carried out of 550 degree centigree - 750 degree centigree. The present report describes the state in the running program with test-times of 23.000 hours and results from tests up to 55.000 hours belonging to other parallel programs are taken into account. Besides the creep-rupture behaviour it is also made a study of ductility between 550 and 750 degree centigree. Extensive metallographic examinations have been made to study the fracture behaviour and changes in structure. (Author)

  10. Electrochemical characterisation of X10CrNi 18-8 steel in artificial plasma

    Directory of Open Access Journals (Sweden)

    J. Przondziono

    2015-01-01

    Full Text Available Quality of applied guide wires conditions the course of treatment and its success to a great extent. In order to simulate conditions that can be found in blood vascular system samples were exposed to artificial blood plasma (T = 37 } 1 oC for the time of 8 h. In order to obtain information regarding physical and chemical properties of modified surface of wire made of X10CrNi 18-8 steel, electrochemical impedance spectroscopy (EIS test and tests of chemical composition of the surface layer X-ray photoelectron spectroscopy (XPS were made. On the ground of performed EIS and XPS tests, favourable impact of steam sterilisation process on corrosion resistance of X10CrNi 18-8 steel was observed only for the case when chemical passivation was applied prior to sterilisation.

  11. Changes in mechanical properties and structure of electrolytic plasma treated X 12 CrNi 18 10 Ti stainless steel

    Energy Technology Data Exchange (ETDEWEB)

    Kurbanbekov, Sherzod; Baklanov, Viktor; Karakozov, Batyrzhan [Republican State Enterprise National Nuclear Center of Kazakhstan, Kurchatov (Kazakhstan). Inst. of Atomic Energy Branch; Skakov, Mazhyn [Republican State Enterprise National Nuclear Center of Kazakhstan, Kurchatov (Kazakhstan)

    2017-05-01

    The paper addresses findings regarding the influence of electrolytic plasma treatment on the mechanical properties as well as structural and phase states of X 12 CrNi 18 10 Ti steel. Electrolytic plasma treatment is based on carburizing of stainless steel heated in electrolytes. Treatment of steel samples has been performed as follows: the samples were heated up to a temperature between 850 and 950 C and then they were cured for 7 minutes in an electrolyte of an aqueous solution containing 10 % glycerol (C{sub 3}H{sub 8}O{sub 3}) and 15 % sodium carbonate (Na{sub 2}CO{sub 3}). It is found that, after plasma electrolytic treatment, the surface of X 12 CrNi 18 10 Ti steel had a modified structure and high hardness. Increasing wear resistance of X 12 CrNi 18 10 Ti steel has been observed after carburizing and the coefficient of friction has been reduced. X-ray analysis showed that retained austenite γ-Fe is a main phase, and there are some diffraction lines of orthorhombic Fe{sub 3}C phase as well as Fe{sub 3}O{sub 4} cubic phase. It has been determined, that, after plasma electrolytic treatment, a carbide phase in the modified surface layer, irrespective of the location in the steel structure has the chemical composition Fe{sub 3}C. High concentration of carbon atoms in a solid solution based on γ- and α-iron, a large dislocation density, presence of particles of carbide phase and retained austenite layers have been found.

  12. Determination of susceptibility to intergranular corrosion of stainless steels type X5CrNi18-10 in field

    Directory of Open Access Journals (Sweden)

    Bore V. Jegdic

    2016-12-01

    Full Text Available In this paper, the DL EPR method (electrochemical potentiokinetic reactivation with double loop was modified and used to study the susceptibility to intergranular corrosion and stress corrosion cracking of a stainless steel type X5CrNi18-10. The tests were performed in a special electrochemical cell, with the electrolyte in the gel form. Modified DL EPR method is characterized by simple and high accuracy measurements as well as repeatability of the test results. The indicator of susceptibility to intergranular corrosion (Qr/QpGBA obtained by modified DL EPR method is in a very good agreement with the same indicator obtained by standard DL EPR method. The modified DL EPR method is quantitative and highly selective method. Small differences in the susceptibility of the stainless steel type CrNi18-10 to intergranular corrosion and stress corrosion cracking can be determined. Test results can be obtained in a short time. The cost of tests performed by modified DL EPR method is much lower than the cost of tests by conventional chemical methods. Modified DL EPR method can be applied in the field on the stainless steels constructions.

  13. Mechanical properties of steel X 6 CrNi 18 11 after creep

    Energy Technology Data Exchange (ETDEWEB)

    Heesen, E te; Lorenz, H; Grosser, E D [INTERATOM, Bergisch Gladbach (Germany)

    1977-07-01

    Test series were conducted to determine the influence of prior creep on the mechanical properties of X 6 CrNi 18 11 base material, weld joint and weld metal. Creep and tensile tests on base and weld joint were performed at 600 degrees C, the weld metal was Investigated at 550, 600, and 650 degrees C. With regard to the base materials, prior creep leads to a significant reduction in tensile ductility combined with an increase of the 0.2 % proof stress. Residual ductility represents a sufficient ductility reserve. For the weld joint tensile strength remains unchanged up to the end of the secondary creep stage. Although tensile elongation and reduction of area decrease, the relative reduction is less compared to the base material. Concerning the weld metal the 0.2 % proof stress reveals a marked decrease due to the test temperature leading to a stress relief heat treatment. Ultimate tensile strength and ductility Indicate little or no deviations from the original values. Thermal exposures in the absence of stress nearly gave the same properties as were found on precrept specimens. (author)

  14. Behavior of X 6 CrNi 18 11 under sequential testing of creep and fatigue

    Energy Technology Data Exchange (ETDEWEB)

    Husslage, W [TNO, Apeldoorn (Netherlands); Breitling, H [INTERATOM, Bergisch Gladbach (Germany)

    1977-07-01

    The behaviour of the austenitic stainless steel X 6 CrNi 18 11 with about 0.05% C, 18% Cr and 11% Ni was investigated under combined creep and cyclic loading at 550 degrees C. Base metal specimens and specimens containing a weld were tested by: prior cyclic loading followed by creep loading to rupture; prior creep loading followed by cyclic loading to rupture; alternating periods of creep and cyclic loading to rupture. The results were evaluated using the linear cumulative fatigue and creep damage rule. The damage factor D determined on basis of the respective behaviour of base material and welds varied between 0.5 and 1.6 if specimens containing a weld defect were not taken into consideration. Weld defects, which had predominantly an influence on fatigue, lowered the damage factor D up to 0.2. Evaluation of the results on welds with the pure creep and fatigue behaviour of base material shows damage factors between 0.4 and 0.9. By the high margins between allowable creep and fatigue life and life measured with specimens, the cumulative damages of base material and welded joints are much better than the allowable values according to CCI 1592 of the ASME Boiler and Pressure Vessel Code. (author)

  15. Formability of high-alloy dual-phase Cr-Ni steels

    International Nuclear Information System (INIS)

    Elfmark, J.

    2004-01-01

    The formability of dual-phase high-alloy Cr-Ni steel within the temperature range from 900 to 1250 C was studied using laboratory tensile and torsion tests. The dual-phase steels on 24% Cr basis are characterized by poor hot formability due to very low stable deformation values and slow recrystallization. Mathematical description of deformation stability exhaustion was derived, as well as a model of formability control based on analysis of the gradual diffuse deformation stability from the stability limit to the moment when the deformation starts to concentrate in a small volume of the test piece. Rolling simulation of dual-phase steel strip was used as an example demonstrating the draught scheme optimization technique which avoids the danger of crack occurrence during the rolling of dual-phase steel strip. (orig.)

  16. Effect of carbon content on microstructure and mechanical properties of hot-rolled low carbon 12Cr-Ni stainless steel

    International Nuclear Information System (INIS)

    Zheng, H.; Ye, X.N.; Li, J.D.; Jiang, L.Z.; Liu, Z.Y.; Wang, G.D.; Wang, B.S.

    2010-01-01

    Research highlights: → Hot-rolled ultra low carbon martensite is characterized by dislocation cells substructure. → The formation of dislocation cells is attributed to high Ms and low interstitial atoms content. → Hot-rolled ultra low carbon 12Cr-Ni stainless steel has excellent impact toughness. → Delta ferrite deteriorates the impact toughness of hot-rolled 12Cr-Ni stainless steel. - Abstract: 12Cr-Ni stainless steels containing different carbon contents from 0.004 wt.% to 0.034 wt.% were hot-rolled and air-cooled. Their corresponding microstructures were observed with optical microscope and transmission electron microscope, and the Vickers hardness, tensile and impact tests were also carried out. It was found that the martensitic morphology was significantly influenced by carbon content. The as-received ultra low carbon martensite in the steel containing 0.004 wt.% C is characterized by dislocation cells substructure. The formation of dislocation cells is attributed to high martensite finishing point (above 400 deg. C) and low interstitial atoms content. On the other hand, the martensite in the steel containing 0.034 wt.% C consists mainly of typical martensite laths because of low martensite finishing point and high interstitial atoms content which hinder dislocation motion. Furthermore, carbon content has an evident effect on the mechanical properties of 12Cr-Ni steels. The hardness and strength of the as-received steels increase with an increase in carbon content, but their elongation and impact toughness decrease with the carbon content. The steel containing 0.004 wt.% C has excellent impact toughness due to the ultra low carbon content in the martensite composed of dislocation cells.

  17. The Effect of Si and Mn on Microstructure and Selected Properties of Cr-Ni Stainless Steels

    Directory of Open Access Journals (Sweden)

    Kalandyk B.

    2017-03-01

    Full Text Available Cast stainless steel of the Cr-Ni duplex type is used, among others, for the cast parts of pumps and valves handling various chemically aggressive media. Therefore, the main problem discussed in this article is the problem of abrasion wear resistance in a mixture of SiC and water and resistance to electrochemical corrosion in a 3% NaCl-H2O solution of selected cast steel grades, i.e. typical duplex cast steel, high silicon and manganese duplex cast steel, and Cr-Ni austenitic cast steel (type AISI 316L. The study shows that the best abrasion wear resistance comparable to Ni-Hart cast iron was obtained in the cast duplex steel, where Ni was partially replaced with Mn and N. This cast steel was also characterized by the highest hardness and matrix microhardness among all the tested cast steel grades. The best resistance to electrochemical corrosion in 3% NaCl-H2O solution showed the cast duplex steel with high content of Cr, Mo and N. The addition of Ni plays rather insignificant role in the improvement of corrosion resistance of the materials tested.

  18. Attempts to improve the fatigue characteristics of the austenitic steel X5CrNi18-10 in the temperature range of 25-600 C by mechanical boundary layer hardening; Zur Verbesserung des Ermuedungsverhaltens des austenitischen Stahls X5CrNi18-10 im Temperaturbereich 25-600 C durch mechanische Randschichtverfestigungsverfahren

    Energy Technology Data Exchange (ETDEWEB)

    Nikitin, Ivan

    2007-01-31

    Pieces of the austenitic steel X5CrNi18-10 whose boundary layers had been hardened by different methods were investigated with a view to their fatigue deformation characteristics in the temperature range of 25-600 degC. Parallel to this, microstructural and X-ray analyses provided deeper understanding of fatigue deformation. The microstructure was characterized, among others, by TEM. Boundary layers were solidified by rolling, by a combination of mechanical and thermal processes, by high-temperature rolling, and by laser shock solidification. The analyses focused on microstructural processes and on the intrinsic stress stability and provided important information on the fabrication of structural components with optimised life. (orig.)

  19. Low-Cycle Fatigue Behavior of 10CrNi3MoV High Strength Steel and Its Undermatched Welds.

    Science.gov (United States)

    Song, Wei; Liu, Xuesong; Berto, Filippo; Razavi, S M J

    2018-04-24

    The use of high strength steel allows the design of lighter, more slender and simpler structures due to high strength and favorable ductility. Nevertheless, the increase of yield strength does not guarantee the corresponding improvement of fatigue resistance, which becomes a major concern for engineering structure design, especially for the welded joints. The paper presents a comparison of the low cycle fatigue behaviors between 10CrNi3MoV high strength steel and its undermatched weldments. Uniaxial tension tests, Push-pull, strain-controlled fatigue tests were conducted on base metal and weldments in the strain range of 0.2⁻1.2%. The monotonic and cyclic stress-strain curves, stress-life, strain-life and energy-life in terms of these materials were analyzed for fatigue assessment of materials discrepancy. The stress-life results of base metal and undermatched weld metal exhibit cyclic softening behaviors. Furthermore, the shapes of 10CrNi3MoV steel hysteresis loops show a satisfactory Masing-type behavior, while the weld metal shows a non-Masing type behavior. Strain, plastic and total strain energy density amplitudes against the number of reversals to failure results demonstrate that the undermatched weld metal presents a higher resistance to fatigue crack initiation than 10CrNi3MoV high strength steel. Finally, fatigue fracture surfaces of specimens were compared by scanning electron microscopy to identify the differences of crack initiation and the propagation between them.

  20. Low-Cycle Fatigue Behavior of 10CrNi3MoV High Strength Steel and Its Undermatched Welds

    Directory of Open Access Journals (Sweden)

    Wei Song

    2018-04-01

    Full Text Available The use of high strength steel allows the design of lighter, more slender and simpler structures due to high strength and favorable ductility. Nevertheless, the increase of yield strength does not guarantee the corresponding improvement of fatigue resistance, which becomes a major concern for engineering structure design, especially for the welded joints. The paper presents a comparison of the low cycle fatigue behaviors between 10CrNi3MoV high strength steel and its undermatched weldments. Uniaxial tension tests, Push-pull, strain-controlled fatigue tests were conducted on base metal and weldments in the strain range of 0.2–1.2%. The monotonic and cyclic stress-strain curves, stress-life, strain-life and energy-life in terms of these materials were analyzed for fatigue assessment of materials discrepancy. The stress-life results of base metal and undermatched weld metal exhibit cyclic softening behaviors. Furthermore, the shapes of 10CrNi3MoV steel hysteresis loops show a satisfactory Masing-type behavior, while the weld metal shows a non-Masing type behavior. Strain, plastic and total strain energy density amplitudes against the number of reversals to failure results demonstrate that the undermatched weld metal presents a higher resistance to fatigue crack initiation than 10CrNi3MoV high strength steel. Finally, fatigue fracture surfaces of specimens were compared by scanning electron microscopy to identify the differences of crack initiation and the propagation between them.

  1. Standard and applied material testing methods of austenitic CrNi stainless steels in different nitric acid media - procedures and results

    International Nuclear Information System (INIS)

    Leistikow, S.; Kraft, R.; Schanz, G.

    1989-07-01

    Extended ASTM Standard Huey Testing has been performed in at 120 0 C boiling 14.4 molar (65%) nitric acid during 15 periods (15x48 = 720 h duration) for quality control of numerous commercial nitric acid resistant austenitic CrNi steels. It was shown how sensitively the chosen testing conditions could differentiate between CrNi steels of the same nominal composition as specified for DIN W.Nr. 1.4306 (AISI Type 304 L), but with varying residual element contents. Within an attempt to differentiate within this group of steels by application of electrochemical methods, potentiostatic tests at 1250 mV in nitric acid of equal concentration and temperature were able to detect remarkable differences in corrosion behaviour already after one hour. Another approach, more typical for the electrochemical potentials during materials application in reprocessing plants of nuclear fuel, gave preference to long-term immersion tests, which were performed in nitric acid of lower concentration and temperature. Reference tests in pure 7 molar, 90 0 C nitric acid could only reveal by surface attack small differences in steel quality by exposures of 720 h duration. To shorten the test time by an increase of the redox potential chromium (VI) ions were added to the nitric acid. In a solution of 0,5 g Gr (VI)/l at 90 0 C remarkable differences in corrosion behavior of the steels - similar to the Huey test results - became measurable by means of gravimetry and metallography already during a short-term exposure of 24-71 h. (orig./MM) [de

  2. A POPULATION OF X-RAY WEAK QUASARS: PHL 1811 ANALOGS AT HIGH REDSHIFT

    International Nuclear Information System (INIS)

    Wu Jianfeng; Brandt, W. N.; Schneider, Donald P.; Hall, Patrick B.; Gibson, Robert R.; Schmidt, Sarah J.; Richards, Gordon T.; Shemmer, Ohad; Just, Dennis W.

    2011-01-01

    We report the results from Chandra and XMM-Newton observations of a sample of 10 type 1 quasars selected to have unusual UV emission-line properties (weak and blueshifted high-ionization lines; strong UV Fe emission) similar to those of PHL 1811, a confirmed intrinsically X-ray weak quasar. These quasars were identified by the Sloan Digital Sky Survey at high redshift (z ∼ 2.2); eight are radio quiet while two are radio intermediate. All of the radio-quiet PHL 1811 analogs, without exception, are notably X-ray weak by a mean factor of ∼13. These sources lack broad absorption lines and have blue UV/optical continua, supporting the hypothesis that they are intrinsically X-ray weak like PHL 1811 itself. However, their average X-ray spectrum appears to be harder than those of typical quasars, which may indicate the presence of heavy intrinsic X-ray absorption. Our sample of radio-quiet PHL 1811 analogs supports a connection between an X-ray weak spectral energy distribution and PHL 1811-like UV emission lines; this connection provides an economical way to identify X-ray weak type 1 quasars. The fraction of radio-quiet PHL 1811 analogs in the radio-quiet quasar population is estimated to be ∼< 1.2%. We have investigated correlations between relative X-ray brightness and UV emission-line properties (e.g., C IV equivalent width and blueshift) for a sample combining our radio-quiet PHL 1811 analogs, PHL 1811 itself, and typical type 1 quasars. These correlation analyses suggest that PHL 1811 analogs may have extreme wind-dominated broad emission-line regions. Observationally, the radio-quiet PHL 1811 analogs appear to be a subset (∼30%) of radio-quiet weak-line quasars (WLQs). The existence of a subset of quasars in which high-ionization 'shielding gas' covers most of the broad emission-line region (BELR), but little more than the BELR, could potentially unify the PHL 1811 analogs and WLQs. The two radio-intermediate PHL 1811 analogs are X-ray bright. X

  3. Al2 O3:Cr,Ni: a possible thermoluminescent dosemeter

    International Nuclear Information System (INIS)

    Mariani R, Francisco; Roman B, Alvaro; Saavedra S, Renato; Ibarra S, Angel

    1996-01-01

    Results from a study on the thermoluminescent (Tl) emission from Al 2 O 3 :Cr,Ni are presented. The measurements were obtained for evaluation of the Al 2 O 3 :Cr,Ni dosimetric properties. Different crystal batches were exposed to two kind of ionizing radiation (X-ray and β - ). The Tl spectrum has a main peak with high thermal and optical stability, deviating from linearity for doses lower than 3.6 Gy. Furthermore, this material shows advantages (thermal resistance, reusability, multiple heating cycles) compared to TLD-100. Measured Al 2 O 3 :Cr,Ni properties indicate that it could be used as a dosemeter. (author)

  4. THE INFLUENCE OF GRINDING CONDITIONS ON THE DISTRIBUTION OF RESIDUAL STRESS IN THE SURFACE LAYER OF 17crni6-6 STEEL AFTER CARBURIZING

    Directory of Open Access Journals (Sweden)

    Jacek Sawicki

    2017-06-01

    Full Text Available This paper presents the results of a study aimed at determining the residual stress which results from developing the surface layer by low-pressure and conventional carburizing and grinding of 17CrNi6-6 steel. A synergistic effect of thermochemical and abrasive treatment was examined on ring samples used to study residual stress by Davidenkov’s method. Samples were subjected to vacuum carburizing and conventional carburizing, which was followed by grinding with a 38A60K8V aloxite grinding wheel and a CBN grinding wheel - RNB80/63B75V. The following cutting fluids were used during the grinding process: oil emulsion 5%, supply rate ca. 20 l/min, Micro5000 oil supplied at the minimum quantity lubrication (MQL of ca. 25 ml/h, dry machining. The study determined the effect of the type of grinding wheel and the cooling and lubricating agent on the distribution of residual stress in the sur-face layer. The best effects of grinding with respect to the residual stress were achieved with flood cooling with oil emulsion and grinding with a CBN grinding wheel.

  5. Impact Strength of Austenitic and Ferritic-Austenitic Cr-Ni Stainless Cast Steel in -40 and +20°C Temperature

    Directory of Open Access Journals (Sweden)

    Kalandyk B.

    2014-10-01

    Full Text Available Studies described in this paper relate to common grades of cast corrosion resistant Cr-Ni steel with different matrix. The test materials were subjected to heat treatment, which consisted in the solution annealing at 1060°C followed by cooling in water. The conducted investigations, besides the microstructural characteristics of selected cast steel grades, included the evaluation of hardness, toughness (at a temperature of -40 and +20oC and type of fracture obtained after breaking the specimens on a Charpy impact testing machine. Based on the results of the measured volume fraction of ferrite, it has been found that the content of this phase in cast austenitic steel is 1.9%, while in the two-phase ferritic-austenitic grades it ranges from 50 to 58%. It has been demonstrated that within the scope of conducted studies, the cast steel of an austenitic structure is characterised by higher impact strength than the two-phase ferritic-austenitic (F-A grade. The changing appearance of the fractures of the specimens reflected the impact strength values obtained in the tested materials. Fractures of the cast austenitic Cr-Ni steel obtained in these studies were of a ductile character, while fractures of the cast ferritic-austenitic grade were mostly of a mixed character with the predominance of brittle phase and well visible cleavage planes.

  6. Cr-Ni ALLOY ELECTRODEPOSITION AND COMPARISON WITH CONVENTIONAL PURE Cr COATING TECHNIQUE

    Directory of Open Access Journals (Sweden)

    M. Moniruzzaman

    2012-12-01

    Full Text Available Cr coating is widely used as the outer surface of precision parts due to its attractive appearance and superior corrosion resistance properties. It is obtained by electrodeposition via a conventional bath with hexavalent Cr ions. This manufacturing technique has many drawbacks, such as very low efficiency and high operating temperature and it is hazardous to health. In this work, we studied a Cr-Ni alloy deposition technique and compared the alloy coating properties to those with conventional Cr coating. Sequential two-step alloy electrodeposition was also compared. We took varying concentrations of Cr, Ni and complexing agents for the electrodeposition of Cr-Ni alloy and sequential Cr-Ni alloy coating on mild steel. Operating parameters, i.e. current density and temperature, were varied to examine their effects on the coating properties. The coatings thus obtained were characterized by visual observation, corrosion test, microhardness measurement, morphology and chemical analysis. The Cr-Ni alloy coating was found to be more corrosion resistant in 5% NaCl solution and harder than the pure Cr coating obtained by conventional electrodeposition. Toxic gas was produced in a much lower extent in the alloy coating than the conventional Cr coating technique. Again, the two-step Cr-Ni alloy coating was found better in terms of corrosion resistance as well as hardness compared to the Cr-Ni alloy coating. The process was also found to be much more environmentally friendly.

  7. Hunting for Intrinsically X-ray Weak Quasars: The Case of PHL 1811 Analogs

    Science.gov (United States)

    Brandt, William

    2009-09-01

    A central dogma of X-ray astronomy is that luminous X-ray emission is a universal property of efficiently accreting supermassive black holes. One interesting challenge to this idea has come from the quasar PHL 1811 which appears to be intrinsically X-ray weak and also has distinctive emission-line properties. We propose to observe a sample of eight SDSS quasars, selected to have similar UV emission-line properties to that of PHL 1811, to test if they are also X-ray weak. Our analyses of the currently available X-ray data appear to support this hypothesis but do not provide a proper test. Our results will have implications for the nature of accretion-disk coronae, emission-line formation, and AGN selection.

  8. Tensile properties of irradiated and fatigue exposed stainless steel DIN X 6 CrNi 1811 (similar to AISI type 304) plate and welded joints

    International Nuclear Information System (INIS)

    Vries, M.I. de; Schaaf, B. van der; Elen, J.D.

    1979-10-01

    Test specimens of plate metal and welded joints of stainless steel DIN 1.4948, which is similar to AISI type 304, have been irradiated at 723 K and 823 K up to fluences of 1.10 23 n.m -2 and 5.10 24 n.m -2 (E > 0.1 MeV). These are representative conditions for the SNR-300 reactor vessel and inner components after 16 years of operation. High-rate (depsilon/dt = 1 s -1 ) tensile tests were performed after fatigue exposure up to various fractions of fatigue life (D) ranging from 5% to 95% at the same temperatures as the nominal temperatures of the irradiation series

  9. Derivation of time dependent design-values for SNR 300 structural material

    International Nuclear Information System (INIS)

    Lorenz, H.; Breitling, H.; de Heesen, E.

    1976-01-01

    Time-dependent design values were derived from long-term creep rupture data for steel X 6 CrNi 1811 in the unwelded and welded condition. The design values had to satisfy the ASME CC 1592 criterea with respect to creep rupture strength, time to reach 1% strain and transition to tertiary creep as well as the requirement of German regulatory rules to properly account for weld bahaviour. For the evaluation and extrapolation 2 proven computer programmes were used. The design data derived under consideration of weld joints show relative good agreement with the values of ASME CC 1592. Consideration of welds leads to lower design values above 550 0 C and 5x10 3 h with the difference between rolled and weld material becoming larger with increasing time and temperature. (author)

  10. Formed electroslag welded joint from austenitic steel 18/10 CrNi

    International Nuclear Information System (INIS)

    Jilek, L.; Kusak, L.; Martinak, A.

    1987-01-01

    The electroslag welded joint from titanium stabilized steel 18/10 CrNi of 150 mm in thickness showed positive results for both nondestructive and destructive testing. Czechoslovak flux VUZ-4F and the optimized welding mode were completely proven. The weldment was subject to deformation by forging with a removal of 20 to 50% and to bending deformation. A 40% to 50% deformation was necessary for breaking the coarse-grain casting structure. The bending deformation resulted in breaking the coarse-grain casting structure in the entire cross-section, it was, however, only acting in a narrow band corresponding to the largest curvature. At the same time, the heat affected zone decayed. Following heat treatment, especially forming, the delta ferrite content in the weld metal decreased, the mechanical properties of the weld metal and the welded joint following welding and heat treatment showed a relatively large scatter. Forming reduced the scatter and improved plastic properties. Machining within 40 and 50% resulted in good echogenicity of the welded joint in ultrasound testing. The welded joint showed equal properties as the base material of the weldment. (author). 15 figs., 2 tabs., 16 refs

  11. Influencia de la soldadura sobre la rotura por tensiones en tubos de acero inoxidable austenitico del tipo 18-11NB(TP347

    Directory of Open Access Journals (Sweden)

    Gutiérrez de Saiz-Solabarria, S.

    2000-06-01

    Full Text Available This work has been undertaken to study the stress cracking failure in various 18Cr11Ni [TP347 (18-11Nb, TP 321 (18-11 Ti, TP304 (18-11 and TP316 (18-11-2] types austenitic stainless steel tubes. The material used was produced hot-rolling at 76,2 mm φ (3"φ x 2,54 mm (1/10" thickness. The study was carried out at 593ºC and applied stress of 50 Ton/in2.

    Se estudia el efecto de la soldadura sobre la rotura por tensiones en tubos de acero inoxidable austenítico estabilizado con Nb o Ti de los tipos 18-11Nb (TP 347 y 18-11Ti (TP 321 así como sin estabilizar del tipo 18-11 (TP 304 y con Mo del tipo 18-11-2 (TP 316. Los tubos, en todos los casos, son de dimensiones 76,2 mm (3” φ x 2,54 mm (1/10” de espesor y la tensión aplicada (σ de 10 Ton/in2, para una temperatura de servicio de 593ºC.

  12. Constant strain rate test and SCC-behaviour of stainless steels

    International Nuclear Information System (INIS)

    Krauss, H.; Speckhardt, H.

    1979-01-01

    In the present work, the stress corrosion cracking behaviour in boiling aqueous 35% magnesium chloride solution under conditions of no external current was investigated as a function of the defined extension rates for the two austenitic steels X 2 CrNi 189 and X 2 CrNiSi 1815, as well as for both ferritic austenitic steels X 6 CrNiMoCu 217 and X 2 CrNiMoN 225. The endurance time found until cracking, the maximum tensile stress, the sample stretching up to cracking and the relative rupture energy were determined for the evaluation, as well as metallographic investigations to describe the crack picture, test surface appearance and attack picture carried out. (orig.) 891 RW/orig. 892 BRE [de

  13. Effect of quenching temperature on martensite multi-level microstructures and properties of strength and toughness in 20CrNi2Mo steel

    Energy Technology Data Exchange (ETDEWEB)

    Long, Shao-lei [College of Materials Science and Metallurgical Engineering, Guizhou University (China); Guizhou Key Laboratory for Mechanical Behavior and Microstructure of Materials (China); National & Local Joint Engineering Laboratory for High-performance Metal Structure Material and Advanced Manufacturing Technology (China); Liang, Yi-long, E-mail: liangyilong@126.com [College of Materials Science and Metallurgical Engineering, Guizhou University (China); Guizhou Key Laboratory for Mechanical Behavior and Microstructure of Materials (China); National & Local Joint Engineering Laboratory for High-performance Metal Structure Material and Advanced Manufacturing Technology (China); Jiang, Yun [Guizhou Key Laboratory for Mechanical Behavior and Microstructure of Materials (China); National & Local Joint Engineering Laboratory for High-performance Metal Structure Material and Advanced Manufacturing Technology (China); Liang, Yu; Yang, Ming; Yi, Yan-liang [College of Materials Science and Metallurgical Engineering, Guizhou University (China); Guizhou Key Laboratory for Mechanical Behavior and Microstructure of Materials (China); National & Local Joint Engineering Laboratory for High-performance Metal Structure Material and Advanced Manufacturing Technology (China)

    2016-10-31

    The martensite multi-level microstructures of 20CrNi2Mo steel, which were quenched at the different temperatures of 900–1200 °C and tempered at 200 °C, were investigated by optical microscope (OM), scanning electron microscopy (SEM), electron backscattering diffraction (EBSD) and transmission electron microscopy (TEM), and the relationship between the microstructures and properties of strength and toughness was discussed by the classic formula of Hall–Petch. The results show that the size of prior austenite grain (d{sub r}), martensite packet (d{sub p}) and block (d{sub b}) increase with increasing of the quenching temperature, while the martensite lath (d{sub l}) size is opposite. On another hand, the confusion degree of the martensite packets changes from disorder to order. The boundaries of prior austenite grain, packet, block and the martensite lath are high angle boundaries (HBs) and low angle boundaries (LBs), respectively, and the ratio of the low angle boundaries increase with the quenching temperature by calculating to the multi-level microstructure size with the mathematical model established by myself. In addition, the relationship between the packet/block and strength follows the classical formula of Hall–Petch, and the size of d{sub b} is far lower than the size of d{sub p}, d{sub b} is the effective control unit of the strength. Meanwhile, d{sub l} is the effective control unit of toughness because it strongly impacts the crack initiation and propagation and follows also the Hall-Petch with toughness in 20CrNi2Mo steel.

  14. Al{sub 2} O{sub 3}:Cr,Ni: a possible thermoluminescent dosemeter; Al{sub 2} O{sub 3}: Cr, Ni un posible dosimetro termoluminiscente

    Energy Technology Data Exchange (ETDEWEB)

    Mariani R, Francisco; Roman B, Alvaro; Saavedra S, Renato [Pontificia Univ. Catolica de Chile, Santiago (Chile). Facultad de Fisica; Ibarra S, Angel [Centro de Investigaciones Energeticas, Medioambientales y Tecnologicas (CIEMAT), Madrid (Spain). Seccion Materiales para Fusion

    1997-12-31

    Results from a study on the thermoluminescent (Tl) emission from Al{sub 2} O{sub 3}:Cr,Ni are presented. The measurements were obtained for evaluation of the Al{sub 2} O{sub 3}:Cr,Ni dosimetric properties. Different crystal batches were exposed to two kind of ionizing radiation (X-ray and {beta}{sup -}). The Tl spectrum has a main peak with high thermal and optical stability, deviating from linearity for doses lower than 3.6 Gy. Furthermore, this material shows advantages (thermal resistance, reusability, multiple heating cycles) compared to TLD-100. Measured Al{sub 2} O{sub 3}:Cr,Ni properties indicate that it could be used as a dosemeter. (author). 5 refs., 4 figs.

  15. Characteristics of modified martensitic stainless steel surfaces under tribocorrosion conditions

    International Nuclear Information System (INIS)

    Rozing, Goran; Marusic, Vlatko; Alar, Vesna

    2017-01-01

    Stainless steel samples were tested in the laboratory and under real conditions of tribocorrosion wear. Electrochemical tests were also carried out to verify the corrosion resistance of modified steel surfaces. Metallographic analysis and hardness testing were conducted on stainless steel samples X20Cr13 and X17CrNi16 2. The possibilities of applications of modified surfaces of the selected steels were investigated by testing the samples under real wear conditions. The results have shown that the induction hardened and subsequently nitrided martensitic steels achieved an average wear resistance of up to three orders of magnitude higher as compared to the delivered condition.

  16. Characteristics of modified martensitic stainless steel surfaces under tribocorrosion conditions

    Energy Technology Data Exchange (ETDEWEB)

    Rozing, Goran [Osijek Univ. (Croatia). Chair of Mechanical Engineering; Marusic, Vlatko [Osijek Univ. (Croatia). Dept. of Engineering Materials; Alar, Vesna [Zagreb Univ. (Croatia). Dept. Materials

    2017-04-01

    Stainless steel samples were tested in the laboratory and under real conditions of tribocorrosion wear. Electrochemical tests were also carried out to verify the corrosion resistance of modified steel surfaces. Metallographic analysis and hardness testing were conducted on stainless steel samples X20Cr13 and X17CrNi16 2. The possibilities of applications of modified surfaces of the selected steels were investigated by testing the samples under real wear conditions. The results have shown that the induction hardened and subsequently nitrided martensitic steels achieved an average wear resistance of up to three orders of magnitude higher as compared to the delivered condition.

  17. The Intrinsically X-Ray-weak Quasar PHL 1811. II. Optical and UV Spectra and Analysis

    Science.gov (United States)

    Leighly, Karen M.; Halpern, Jules P.; Jenkins, Edward B.; Casebeer, Darrin

    2007-11-01

    This is the second of two papers reporting observations and analysis of the unusually bright (mb=14.4), luminous (MB=-25.5), nearby (z=0.192) narrow-line quasar PHL 1811. The first paper reported that PHL 1811 is intrinsically X-ray-weak and presented a spectral energy distribution (SED). Here we present HST STIS optical and UV spectra, and ground-based optical spectra. The optical and UV line emission is very unusual. There is no evidence for forbidden or semiforbidden lines. The near-UV spectrum is dominated by very strong Fe II and Fe III, and unusual low-ionization lines such as Na I D and Ca II H and K are observed. High-ionization lines are very weak; C IV has an equivalent width of 6.6 Å, a factor of ~5 smaller than measured from quasar composite spectra. An unusual feature near 1200 Å can be deblended in terms of Lyα, N V, Si II, and C III* using the blueshifted C IV profile as a template. Photoionization modeling shows that the unusual line emission can be explained qualitatively by the unusually soft SED. Principally, a low gas temperature results in inefficient emission of collisionally excited lines, including the semiforbidden lines generally used as density diagnostics. The emission resembles that of high-density gas; in both cases this is a consequence of inefficient cooling. PHL 1811 is very unusual, but we note that quasar surveys may be biased against finding similar objects. Based on observations made with the NASA/ESA Hubble Space Telescope, obtained at the Space Telescope Science Institute, which is operated by the Association of Universities for Research in Astronomy, Inc., under NASA contract NAS5-26555. These observations are associated with proposal 9181. Based on observations obtained at Kitt Peak National Observatory, a division of the National Optical Astronomy Observatories, which is operated by the Association of Universities for Research in Astronomy, Inc., under cooperative agreement with the National Science Foundation.

  18. Propagation of semi-elliptical surface cracks in ferritic and austenitic steel plates under thermal cyclic loading

    International Nuclear Information System (INIS)

    Bethge, K.

    1989-05-01

    Theoretical and experimental investigations of crack growth under thermal and thermomechanical fatigue loading are presented. The experiments were performed with a ferritic reactor pressure vessel steel 20 MnMoNi 5 5 and an austenitic stainless steel X6 CrNi 18 11. A plate containing a semi-elliptical surface crack is heated up to a homogeneous temperature and cyclically cooled down by a jet of cold water. On the basis of linear elastic fracture mechanics stress-intensity factors are calculated with the weight function method. The prediction of crack growth under thermal fatigue loading using data from mechanical fatigue tests is compared with the experimental result. (orig.) [de

  19. Bulk and surface properties of liquid Al-Cr and Cr-Ni alloys

    International Nuclear Information System (INIS)

    Novakovic, R

    2011-01-01

    The energetics of mixing and structural arrangement in liquid Al-Cr and Cr-Ni alloys has been analysed through the study of surface properties (surface tension and surface segregation), dynamic properties (chemical diffusion) and microscopic functions (concentration fluctuations in the long-wavelength limit and chemical short-range order parameter) in the framework of statistical mechanical theory in conjunction with quasi-lattice theory. The Al-Cr phase diagram exhibits the existence of different intermetallic compounds in the solid state, while that of Cr-Ni is a simple eutectic-type phase diagram at high temperatures and includes the low-temperature peritectoid reaction in the range near a CrNi 2 composition. Accordingly, the mixing behaviour in Al-Cr and Cr-Ni alloy melts was studied using the complex formation model in the weak interaction approximation and by postulating Al 8 Cr 5 and CrNi 2 chemical complexes, respectively, as energetically favoured.

  20. Bulk and surface properties of liquid Al-Cr and Cr-Ni alloys.

    Science.gov (United States)

    Novakovic, R

    2011-06-15

    The energetics of mixing and structural arrangement in liquid Al-Cr and Cr-Ni alloys has been analysed through the study of surface properties (surface tension and surface segregation), dynamic properties (chemical diffusion) and microscopic functions (concentration fluctuations in the long-wavelength limit and chemical short-range order parameter) in the framework of statistical mechanical theory in conjunction with quasi-lattice theory. The Al-Cr phase diagram exhibits the existence of different intermetallic compounds in the solid state, while that of Cr-Ni is a simple eutectic-type phase diagram at high temperatures and includes the low-temperature peritectoid reaction in the range near a CrNi(2) composition. Accordingly, the mixing behaviour in Al-Cr and Cr-Ni alloy melts was studied using the complex formation model in the weak interaction approximation and by postulating Al(8)Cr(5) and CrNi(2) chemical complexes, respectively, as energetically favoured.

  1. The influence of cold work on the oxidation behaviour of stainless steel

    International Nuclear Information System (INIS)

    Langevoort, J.C.

    1985-01-01

    In this thesis the study of the interaction of oxygen gas with stainless steel surfaces is described. Thermogravimetry, microscopy and ellipsometry have been used to follow the oxidation in situ, while EDX, AES and XPS have been used to determine the oxide compositions. The aim of this thesis is to reveal the influence on the oxidation behaviour of stainless steel of i) cold work (rolling, drawing, milling, polishing and Ar ion bombardment) ii) the initially formed oxide and iii) the experimental conditions. Two types of stainless steels have been used (AISI 304 (a 18/8 Cr/Ni steel) and Incoloy 800 H (a 20/30 Cr/Ni steel)). (Auth.)

  2. Estimation of residual stresses in reactor pressure vessel steel specimens clad by stainless steel strip electrodes

    International Nuclear Information System (INIS)

    Schimmoeller, H.A.; Ruge, J.L.

    1978-01-01

    The equations to determine a two-dimensional state of residual stress in flat laminated plates are well known from an earlier work by one of the authors. The derivation of these equations leads to a linear, inhomogeneous system of Volterra's integral equations of the second kind. To ascertain the unknown residual stresses from these equations it is necessary to cut down the thickness of the test plate layer by layer. This results in two-dimensional deformation reactions in the rest of the test plate, which can be measured, e.g. by a strain gauge rosette applied to the opposite side of the plate. The above-mentioned stress analysis has been transferred to 86mm thick reactor pressure vessel steel specimens (Type 22NiMoCr 37, DIN-No. 1.6751, similar to ASTM A508, Class 2) double-run clad by austenitic stainless steel strip electrodes (first layer 24/13 Cr-Ni steel, second layer 21/10 Cr-Ni steel). The overall dimensions of the clad specimens investigated amounted to 200 x 200 x (86+4.5+4.5)mm. At the surface of the austenitic cladding there is a two-dimensional tensile normal stress state of about 200N/mm 2 parallel, and about 300N/mm 2 transverse, to the welding direction. The maximum tensile stress was 8mm below the interface (fusion line, material transition) in the parent material. The stress distributions of the specimens investigated, determined on the basis of the above-mentioned combined experimental mathematical procedure, are presented graphically for the as-welded (as-delivered) and annealed (600 0 C/12hr) conditions. (author)

  3. Comparative studies on ultrasonic, friction, laser and resistance pressure welding of NiTi shape memory alloys with high-alloy steels. Final report; Vergleichende Untersuchungen zum Ultraschall-, Reib-, Laserstrahl- und Widerstandspressschweissen von NiTi-Shape-Memory-Metall mit hochlegierten Staehlen. Abschlussbericht

    Energy Technology Data Exchange (ETDEWEB)

    Zuckschwerdt, K.

    2000-04-01

    The suitability of different welding techniques for welding of NiTi shape memory alloys with high-alloy steel (C12CrNi17-7, X5CrNiNb19-9, X20Cr13) was investigated. The quality of the welds was analyzed using mechanical-technological, fractographic, metallographic and electron microscopy analysis. [German] Ziel dieses Forschungsvorhabens ist es, die Eignung der einzelnen Schweissverfahren fuer das Fuegen von NiTi-Formgedaechtnislegierungen mit hochlegiertem Stahl (X12CrNi17-7, X5CrNiNb19-9, X20Cr13) darzustellen und zu beurteilen. Die Qualitaet der Fuegeverbindungen wird mit Hilfe mechanisch-technologischer, fraktographischer, metallographischer und elektronenmikroskopischer Untersuchungen bewertet.

  4. High-temperature brazing of X5CrNi18 10 and NiCr20TiAl using the atmospherically plasma-sprayed L-Ni2 filler metal

    International Nuclear Information System (INIS)

    Wielage, B.; Drozak, J.

    1992-01-01

    The hybrid-technological combination of the atmospheric plasma spraying for the application of a high-temperature filler metal followed by a brazing process was analyzed in terms of structure and mechanical properties of X5CrNi18 10 and NiCr20TiAl brazing joints. The thickness of the filler metal layer was minimized at [de

  5. Effect of acetic acid on corrosion behavior of AISI 201, 304 and 430 stainless steels

    Energy Technology Data Exchange (ETDEWEB)

    Vashishtha, Himanshu; Taiwade, Ravindra V.; Sharma, Sumitra [Visvesvaraya National Institute of Technology (VNIT), Nagpur (India). Dept. of Metallurgical and Materials Engineering

    2017-05-15

    Austenitic stainless steels are often used to handle organic acids such as acetic acid (CH{sub 3}COOH), which are extensively used in food contact applications and chemical industries for manufacturing medicines, nutrition and various chemical amalgams. In the present investigation an attempt has been made to compare the corrosion behavior of Cr-Ni (AISI type 304), Cr-Mn-Ni (type 201) and Cr (type 430) stainless steel for economical replacement of higher cost Cr-Ni grade. Immersion testing was performed at room temperature and boiling temperature in acetic acid. Atomic absorption spectroscopy was carried out to evaluate metal ion concentration in the immersion solution. The surface morphology of pit formation was characterized using scanning electron microscopy coupled with energy dispersive X-ray spectroscopy. The effect of elemental leaching on electrical conductivity of the immersion solution was evaluated and correlated with pH measurements. A new mechanism has been proposed for the pit formation due to manganese sulfide inclusions. The replacement compatibility was further confirmed with anodic polarization testing and a successful replacement was established for room temperature applications.

  6. Analysis of the austenitic stainless steel's r-value behavior at elevated temperatures

    OpenAIRE

    Dušan Arsić; Milan Djordjević; Srbislav Aleksandrović; Vukić Lazić; Ruzica R. Nikolic; Branislav Hadzima

    2015-01-01

    An analysis of the anisotropy properties of austenitic steel AISI 304 (X5CrNi18-10) at elevated temperatures is presented in this paper. Considerations of the anisotropy problems are presented in the theoretical part of the paper, as well as the procedure for determination of the normal anisotropy coefficient. The experimental part of the paper describes the plan, methodology and equipment for testing of material's normal anisotropy and mechanical characteristics. The objective of conducting ...

  7. Cathode-sputtered Ti-Zr-N-C-O base hard coatings and stability of said coatings on hard metals and working steels. Kathodenzerstaeubte Hartstoffschichten auf Basis Ti-Zr-N-C-O und deren Stabilitaet auf Hartmetall und Gebrauchsstaehlen

    Energy Technology Data Exchange (ETDEWEB)

    Boehmer, M.

    1986-02-26

    This paper deals with the examination of the metallurgical and thermal stability of the resistant material layers of titanium in connection with the substrate material influence. As substrate material were chosen: hard metal (81% WC, 12% TiC+TaC, 7% Co), high speed steel (DIN 1.3343), austenitic nickel chromium steel (X5 CrNi 18 9) and unalloyed tool steel (DIN 1.1545). The hard materials of titanium were deposited by means of cathode evaporation.

  8. Hydrogen Embrittlement Mechanism in Fatigue Behaviour of Austenitic and Martensitic Stainless Steels

    Directory of Open Access Journals (Sweden)

    Brück Sven

    2018-01-01

    Full Text Available In the present study, the influence of hydrogen on the fatigue behaviour of the high strength martensitic stainless steel X3CrNiMo13-4 and the metastable austenitic stainless steels X2Crni19-11 with various nickel contents was examined in the low and high cycle fatigue regime. The focus of the investigations was the changes in the mechanisms of short crack propagation. The aim of the ongoing investigation is to determine and quantitatively describe the predominant processes of hydrogen embrittlement and their influence on the short fatigue crack morphology and crack growth rate. In addition, simulations were carried out on the short fatigue crack growth, in order to develop a detailed insight into the hydrogen embrittlement mechanisms relevant for cyclic loading conditions.

  9. EXPERIMENTAL RESEARCH REGARDING THE INFLUENCE OF CUTTING REGIME ON THE WEAR OF DRILLS AT STEEL PROCESSING

    Directory of Open Access Journals (Sweden)

    Leonard Marius CIUREZU GHERGHE

    2015-05-01

    Full Text Available This paper aims to highlight the influence of cutting regime on the wear drills at steel processing , in particular the processing of stainless steel X17CrNi16-2 SR EN 10088-4 DIN 17440. We are interested in wear of the drill at processing of this type of stainless steel , which has applicability in energy industry given the special characteristics of its. We want a maximum value of 0.2 mm for the wear of the drill, measurement and taking pictures are made using a microscope DigiMicro 2.0 and the software used is MicroCapture. Processing was done on machining center YMC YOUNG TECH 1050, and the tool used was 8 mm drill bit high speed steel.

  10. Small angle neutron scattering study of the damage induced by creep deformation in AISI 304 stainless steel

    International Nuclear Information System (INIS)

    Boeuf, A.; Coppola, R.; Matera, R.; Rustichelli, F.; Zambonardi, F.; Puliti, P.; Melone, S.

    1982-01-01

    In the austenitic stainless steels, a class of materials largely used in the nuclear power plants, creep induces essentially two new microstructural effects: the nucleation and growth of grain boundary cavities and the precipitation of carbides. Carbides precipitate as a consequence of pure thermal treatment, whereas for the occurrence of voids the presence of stress is necessary. It should be noted however, that the kinetics of precipitation and even the precipitate crystal structure are changed by the introduction of dislocations due to straining during creep. The aim of the present study is a quantitative characterization of the creep damage occurring in a stainless steel of the type X 6 CrNi 8 11 (AISI 304). The experimental techniques used are optical and electron microscopy, microprobe analysis and small angle neutron scattering. This latter technique is described in more detail

  11. Study of the Weldability of Austenitic PH Steel for Power Plants

    Directory of Open Access Journals (Sweden)

    Ziewiec A.

    2016-06-01

    Full Text Available The article presents the results of Transvarestraint test of a modern precipitation hardened steel X10CrNiCuNb18-9-3 with copper. For comparison, the results of tests of conventional steel without the addition of copper X5CrNi18-10 are presented. The total length of all cracks and the maximum length of cracks were measured. The study of microstructure (LM, SEM showed that the austenitic stainless steel X10CrNiCuNb18-9-3 is very prone to hot cracking. After performing the Transvarestraint tests three types of cracks were observed: solidification cracks occurring during crystallization, liquation cracks due to segregation in the heat affected zone (HAZ and surface cracks. Niobium carbonitrides dispersed in the bands of segregation are the reason of high susceptibility to liquation cracking. Segregation of copper occurring during solidification causes of surface cracking. A combined effect of copper and stresses contributes to formation of hot microcracks. These microcracks propagate to a depth of 20-30 μm.

  12. Impact of roughness, wettability and hydrodynamic conditions on the incrustation on stainless steel surfaces

    International Nuclear Information System (INIS)

    Bogacz, Wojciech; Lemanowicz, Marcin; Al-Rashed, Mohsen H.; Nakonieczny, Damian; Piotrowski, Tomasz; Wójcik, Janusz

    2017-01-01

    Highlights: • Steel plates (X5CrNi18-10) with different roughness and wettability were prepared. • Incrustation of MgSO 4 ·7H 2 O under laminar flow (Re = 59–178) was investigated. • Influence of surface properties and fluid velocity on incrustation was found. • Wettability and surface roughness cannot be considered separately. • Analysis of heat transfer and incrustation time-lapse videos are presented. - Abstract: The goal of this work was to investigate the influence of the stainless steel surface roughness and wettability on incrustation of MgSO 4 ·7H 2 O from aqueous solutions and resulting heat transfer resistance. The experiments were done for laminar flow (Re = 59–178) which is characteristic for regions of apparatus where fouling usually begin. A series of steel plates (X5CrNi18-10) were prepared and used as a heat transfer surfaces. Their properties, i.e. roughness, wettability and elementary composition of surfaces were determined. The experiments were done using specially designed flow cell equipped with Peltier element. Each incrustation measurement lasted for two hours, during which heat transfer resistance was measured as a function of time. After the experiments the mass of crystalline deposit was weighted. It was proved that wettability as well as surface roughness cannot be considered separately in the case of incrustation phenomenon. The knowledge of surface roughness is insufficient due to the fact, that it is possible to obtain surfaces with similar roughness but substantially different wettability for the same material.

  13. Corrosion processes of alloyed steels in salt solutions

    Energy Technology Data Exchange (ETDEWEB)

    Kienzler, Bernhard [Karlsruher Institut fuer Technologie (KIT), Eggenstein-Leopoldshafen (Germany). Institut fuer Nukleare Entsorgung

    2018-02-15

    A summary is given of the corrosion experiments with alloyed Cr-Ni steels in salt solutions performed at Research Centre Karlsruhe (today KIT), Institute for Nuclear Waste Disposal (INE) in the period between 1980 and 2004. Alloyed steels show significantly lower general corrosion in comparison to carbon steels. However, especially in salt brines the protective Cr oxide layers on the surfaces of these steels are disturbed and localized corrosion takes place. Data on general corrosion rates, and findings of pitting, crevice and stress corrosion cracking are presented.

  14. Parametrical limits of SCC-susceptibility of austenitic and austenitic-ferritic Cr-Ni steels

    International Nuclear Information System (INIS)

    Starosvetskij, D.I.; Baru, R.L.; Bondarenko, A.I.; Bogoyavlenskij, V.L.; Timonin, V.A.

    1990-01-01

    Comparative investigations into corrosion cracking (CC) of austenitic (12Kh18N10T) and austenitic-ferritic (08Kh22N6T) chromium-nickel steels are performed for various chloride media in a wide range of chloride concentrations and temperatures. It is shown that the ratio between steels in terms of their CC-susceptibility is not definite and can undergo a reversal depending on parameters of medium, level and conditions of loading. Differences in mechanisms of corrosion cracking of austenitic and austenitic-ferritic steels are established

  15. Investigation of Cr-Ni duplex stainless steel

    International Nuclear Information System (INIS)

    Lu Shiying

    1985-01-01

    At temperatures of 450 - 750 0 C, a laminate-shaped intermetallic phase Fe3Cr3Mo2Si2 has been observed. Intergranular brittle fracture is due to the precipitation of the Fe3Cr3Mo2SI2 phase, but quasi-cleavage fracture is connected with the precipitation of chi and σ phases. The formation of chi and σ during aging at 750 - 900 0 C results in a drastic decrease of the SCC resistance of Cr18Ni5 steel. In order to avoid a fully ferritic microstructure in Cr18Ni5 duplex steel after heating at high temperature or welding, the K value must be kept to 0.42 for thin wall tube. The decrease in SCC resistance after cold deformation is not due to the formation of strain-induced martensite but is connected with significant reduction in the resistance to pitting corrosion. (author)

  16. Microstructure changes in the low stacking fault energy steel

    International Nuclear Information System (INIS)

    Rodak, K.; Kuc, D.; Niewielski, G.; Hetmanczyk, M.

    1999-01-01

    A Cr-Ni austenitic steel (type 304) was investigated using TEM. It is shown that some structural parameters (dislocations density within the subgrains and the subgrains size) change with temperature and strain rate after hot temperature deformation. The subgrain microstructure was characterized quantitatively for different characteristics. (author)

  17. Resistance Spot Welding of dissimilar Steels

    Directory of Open Access Journals (Sweden)

    Ladislav Kolařík

    2012-01-01

    Full Text Available This paper presents an analysis of the properties of resistance spot welds between low carbon steel and austenitic CrNi stainless steel. The thickness of the welded dissimilar materials was 2 mm. A DeltaSpot welding gun with a process tape was used for welding the dissimilar steels. Resistance spot welds were produced with various welding parameters (welding currents ranging from 7 to 8 kA. Light microscopy, microhardness measurements across the welded joints, and EDX analysis were used to evaluate the quality of the resistance spot welds. The results confirm the applicability of DeltaSpot welding for this combination of materials.

  18. Development of x-ray computed tomographic scanner for iron and steel

    International Nuclear Information System (INIS)

    Taguchi, Isamu; Nakamura, Shigeo.

    1985-01-01

    X-ray computed tomography is extensively used in medicine, but has rarely been applied to non-medical purposes. Steel specimens pose particularly difficult problems-very poor transmission of X-rays and the need for high resolving capability. There has thus been no effective tomographic method of examining steel specimens. Due to the growing need for non-destructive, non-contact methods for observing and analyzing the internal conditions of steel microscopically, however, we have developed an X-ray Computed Tomographic Scanner for Steel (CTS) system, specifically for examination of steel specimens. Its major specifications and functions are as follows. Type: the second-generation CT, 8-channels, Scanning method: 6 0 revolution, 30-times traversing, Slice width: 0.5 mm, Resolving capability: 0.25 x 0.25 mm, X-ray source: 420 kV, 3 mA, X-ray detector: BGO scintillator, Standard specimen shape: 50 mm dia., 100 mm high, Measuring time: 10.5 min. Porosity of a stainless steel (SUS 304) bloom was examined three-dimensionally by the CTS system. Corrosion procedure of a steel slab was also examined. (author)

  19. On the Cutting Performance of Coated HSS Taps When Machining of Austenitic Steel

    Science.gov (United States)

    Sliwkova, Petra; Piska, Miroslav

    2014-12-01

    The paper deals with a quality of the PVD coated HSS taps when cutting the stainless austenitic chromiumnickel non-stabilized steel DIN 1.4301 (X5CrNi 18-10). The main attention is focused on the analysis of loading (cutting moment, specific energy) of the HSS taps by means of pieso-electrical dynamometer Kistler 9272 and the relation between the quality of duplex and triplex PVD coatings and their effects on the quality of machined thread surfaces and tool life of the taps. The results showed a safe and stabilized cutting with acceptable quality of threads for HSSE with the TiN+TiCN+DLC coating.

  20. Effects of Cryogenic Treatment on the Strength Properties of Heat Resistant Stainless Steel (07X16H6)

    Science.gov (United States)

    Nadig, D. S.; Bhat, M. R.; Pavan, V. K.; Mahishi, Chandan

    2017-09-01

    Cryogenic treatment on metals is a well known technology where the materials are exposed to cryogenic temperature for prolonged time duration. The process involves three stages viz. slow cooling, holding at cryogenic temperature and warming to room temperature. During this process, hard and micro sized carbide particles are released within the steel material. In addition, soft and unconverted austenite of steel changes to strong martensite structure. These combined effects increase the strength and hardness of the cryotreated steel. In this experimental study, the effects of cryogenic treatment, austenitising and tempering on the mechanical properties of stainless steel (07X16H6) have been carried. After determining the strength properties of the original material, the specimens were cryotreated at 98K for 24 hours in a specially developed cryotreatment system. The effects of austenitising prior to cryogenic treatment and tempering post cryotreatment on the mechanical properties of steel samples have been experimentally determined and analysed.

  1. Laser Welding Of Finned Tubes Made Of Austenitic Steels

    Directory of Open Access Journals (Sweden)

    Stolecki M.

    2015-09-01

    Full Text Available This paper describes the technology of welding of finned tubes made of the X5CrNi1810 (1.4301 austenitic steel, developed at Energoinstal SA, allowing one to get high quality joints that meet the requirements of the classification societies (PN-EN 15614, and at the same time to significantly reduce the manufacturing costs. The authors described an automatic technological line equipped with a Trumph disc laser and a tube production technological process. To assess the quality of the joints, one performed metallographic examinations, hardness measurements and a technological attempt to rupture the fin. Analysis of the results proved that the laser-welded finned tubes were performed correctly and that the welded joints had shown no imperfections.

  2. OPTICAL MONITORING OF TWO BRIGHTEST NEARBY QUASARS, PHL 1811 AND 3C 273

    International Nuclear Information System (INIS)

    Fan, J. H.; Liu, Y.; Yuan, Y. H.; Kurtanidze, O.; Chanishvili, R.; Richter, G. M.

    2014-01-01

    Variability is one of the most observable characteristics of active galactic nuclei, and it is important when considering the emission mechanism. In this paper, we report optical photometry monitoring of two nearby brightest quasars, PHL 1811 and 3C 273, using the ST-6 camera attached to the Newtonian focus and the Ap6E CCD camera attached to the primary focus of the 70 cm meniscus telescope at the Abastumani Observatory, Georgia. PHL 1811 was monitored during the period from 2002 September to 2012 December, while 3C 273 was monitored during the period from 1998 February to 2008 May. During our monitoring period, the two sources did not show any significant intra-day variability. The largest detected variations are ΔR = 0.112 ± 0.010 mag. for PHL 1811, ΔB = 0.595 ± 0.099 mag, ΔV = 0.369 ± 0.028 mag, ΔR = 0.495 ± 0.076 mag, and ΔI = 0.355 ± 0.009 mag for 3C 273. When the periodicity analysis methods are adopted for the observations of the sources, a period of p = 5.80 ± 1.12 yr is obtained for PHL 1811 in the R light curve in the present work, and periods of p = 21.10 ± 0.14, 10.00 ± 0.14, 7.30 ± 0.09, 13.20 ± 0.09, 2.10 ± 0.06, and 0.68 ± 0.05 yr are obtained for 3C 273 based on the data in the present work combined with historical works

  3. OPTICAL MONITORING OF TWO BRIGHTEST NEARBY QUASARS, PHL 1811 AND 3C 273

    Energy Technology Data Exchange (ETDEWEB)

    Fan, J. H.; Liu, Y.; Yuan, Y. H. [Center for Astrophysics, Guangzhou University, Guangzhou 510006 (China); Kurtanidze, O.; Chanishvili, R. [Abastumani Observatory, Mt. Kanobili, 0301 Abastumani, Georgia (United States); Richter, G. M. [Astrophysikalisches Institut Potsdam, An der Sternwarte 16, D-14482 Potsdam (Germany)

    2014-08-01

    Variability is one of the most observable characteristics of active galactic nuclei, and it is important when considering the emission mechanism. In this paper, we report optical photometry monitoring of two nearby brightest quasars, PHL 1811 and 3C 273, using the ST-6 camera attached to the Newtonian focus and the Ap6E CCD camera attached to the primary focus of the 70 cm meniscus telescope at the Abastumani Observatory, Georgia. PHL 1811 was monitored during the period from 2002 September to 2012 December, while 3C 273 was monitored during the period from 1998 February to 2008 May. During our monitoring period, the two sources did not show any significant intra-day variability. The largest detected variations are ΔR = 0.112 ± 0.010 mag. for PHL 1811, ΔB = 0.595 ± 0.099 mag, ΔV = 0.369 ± 0.028 mag, ΔR = 0.495 ± 0.076 mag, and ΔI = 0.355 ± 0.009 mag for 3C 273. When the periodicity analysis methods are adopted for the observations of the sources, a period of p = 5.80 ± 1.12 yr is obtained for PHL 1811 in the R light curve in the present work, and periods of p = 21.10 ± 0.14, 10.00 ± 0.14, 7.30 ± 0.09, 13.20 ± 0.09, 2.10 ± 0.06, and 0.68 ± 0.05 yr are obtained for 3C 273 based on the data in the present work combined with historical works.

  4. Austenitic chromium nickel steel as standard reference material in measurement of thermal and temperature conductivity

    International Nuclear Information System (INIS)

    Binkele, L.

    1990-01-01

    A niobium-stabilized CrNi steel with the NBS designation SRM 735 is introduced as WLF standard reference material in a report by Hust and Giarratano, for the temperature range 300-1200 K and for thermal conductivities around 20 W/mk. However, its specification does not show it to be a direct member of the DIN family of CrNi steels. This report should be regarded as a continuation and supplement to the above-mentioned efforts in America. On the one hand, a solution of a possibly too-narrow specification is aimed at for the reference material, where it is important how sensitive the thermal conductivity is to changes in the chemical composition and changes of the manufacturing parameters and what accuracy can be reached for the reference values with the best measurement techniques. On the other hand, the data base should be expanded and the accuracy of the reference curve should be improved if possible. (orig./MM) [de

  5. Strengthening of stable Cr-Ni austenitic stainless steel under thermomechanical treatments

    Science.gov (United States)

    Akkuzin, S. A.; Litovchenko, I. Yu.; Tyumentsev, A. N.

    2017-12-01

    The features of microstructure and mechanical properties of stable austenitic steel after thermomechanical treatment consisted of low-temperature deformation, deformation in the temperature range T = 273-873 K, and subsequent annealing were investigated. It is shown that under such treatment direct (γ → α')- and reverse (α'→γ)-martensitic transformations occur in the steel. As a result of the thermomechanical treatment submicrocrystalline structural states with high density of micro- and nanotwins and localized deformation bands are formed. The strength of the steel in these structural states is several times higher than that in the initial state.

  6. Investigations on avoidance of hot cracks during laser welding of austenitic Cr-Ni steels and nickel-based alloys using temperature field tailoring. Final report; Untersuchungen zur Vermeidung von Heissrissen beim Laserstrahlschweissen von austenitischen Cr-Ni-Staehlen und Nickelbasislegierungen mittels Temperaturfeld-Tailoring. Schlussbericht

    Energy Technology Data Exchange (ETDEWEB)

    NONE

    2013-08-08

    The aim of the project was to transfer the developed method of laser beam welding of heat treated machining steels of temperature field tailoring on hot crack endangered austenitic Cr-Ni steels and nickel-based alloys. With this method, transient thermal stresses adjacent to the weld are produced by an travelling induction heating so that the hot cracking is prevented during welding. As test materials the austenitic Cr-Ni steel with sulfur additive 1.4305, the Cr-Ni steels 1.4404 and 1.4435 and the nickel-based alloy Udimet 720 were selected. As a result of the research it was shown that a hot crack-free laser welding in the investigated materials using at least three different welding and material-technical approaches is possible. [German] Das Ziel des Forschungsvorhabens bestand darin, das fuer das Laserstrahlschweissen verguetbarer Automatenstaehle entwickelte Verfahren des Temperaturfeld-Tailorings auf heissrissgefaehrdete austenitische Cr-Ni-Staehle und Nickelbasislegierungen zu uebertragen. Mit diesem Verfahren werden waehrend des Schweissens transiente thermische Spannungen neben der Schweissnaht durch eine mitlaufende induktive Erwaermung so erzeugt, dass die Heissrissbildung verhindert wird. Als Versuchswerkstoffe wurden der austenitische Cr-Ni-Stahl mit Schwefelzusatz 1.4305, die Cr-Ni-Staehle 1.4404 und 1.4435 sowie die Nickelbasislegierung Udimet 720 ausgewaehlt. Im Ergebnis des Forschungsvorhabens konnte gezeigt werden, dass ein heissrissfreies Laserstrahlschweissen bei den untersuchten Werkstoffen unter Nutzung von mindestens drei verschiedenen schweiss- und werkstofftechnischen Ansaetzen moeglich ist: Erstens koennen mit einem Temperaturfeld-Tailoring bei im Stumpfstoss zu verschweissenden Blechen aus austenitischen Staehlen bis mindestens 6 mm Dicke senkrecht zur Naht und parallel zur Blechoberflaeche wirkende transiente Druckspannungen erzeugt werden, die der Bildung von Mittelrippenrissen oder dazu parallel liegenden Heissrissen entgegenwirken

  7. Reduction of emission when applying thermal separation processes in the dismantling of nuclear facilities - oxy-fuel gas and plasma arc cutting

    International Nuclear Information System (INIS)

    Stoiber, H.; Hammer, G.; Schultz, H.

    1995-01-01

    Plasma arc cutting and laser beam cutting was used for the studies with the goal of significantly reducing material emission by changing the operating and equipment parameters. Some separations using the oxy-fuel gas cutting process served the purpose of providing a guide for determining which factors can most effectively reduce emission. The separation experiments were carried out with specimens of R-St 37-2, 10 mm thick, as well as of X 6 CrNi 18 10 steel 5, 10, 15 and 20 mm thick. In all cases, lowering speed and the amount of gas proved at first to be effective measures to check material emission. It was also possible to achieve adherence of molten mass and slag on the flank of the joint with excessive icicling. When the plasma separates the CrNi steel, it is possible to increase emission reduction additionally by using an argon/hydrogen mixture instead of nitrogen as a cutting gas. (orig./DG) [de

  8. Active flux tungsten inert gas welding of austenitic stainless steel AISI 304

    Directory of Open Access Journals (Sweden)

    D. Klobčar

    2016-10-01

    Full Text Available The paper presents the effects of flux assisted tungsten inert gas (A-TIG welding of 4 (10 mm thick austenitic stainless steel EN X5CrNi1810 (AISI 304 in the butt joint. The sample dimensions were 300 ´ 50 mm, and commercially available active flux QuickTIG was used for testing. In the planned study the influence of welding position and weld groove shape was analysed based on the penetration depth. A comparison of microstructure formation, grain size and ferrit number between TIG welding and A-TIG welding was done. The A-TIG welds were subjected to bending test. A comparative study of TIG and A-TIG welding shows that A-TIG welding increases the weld penetration depth.

  9. Hydrogen Embrittlement Mechanism in Fatigue Behavior of Austenitic and Martensitic Stainless Steels

    Directory of Open Access Journals (Sweden)

    Sven Brück

    2018-05-01

    Full Text Available In the present study, the influence of hydrogen on the fatigue behavior of the high strength martensitic stainless steel X3CrNiMo13-4 and the metastable austenitic stainless steels X2Crni19-11 with various nickel contents was examined in the low and high cycle fatigue regime. The focus of the investigations were the changes in the mechanisms of short crack propagation. Experiments in laboratory air with uncharged and precharged specimen and uncharged specimen in pressurized hydrogen were carried out. The aim of the ongoing investigation was to determine and quantitatively describe the predominant processes of hydrogen embrittlement and their influence on the short fatigue crack morphology and crack growth rate. In addition, simulations were carried out on the short fatigue crack growth, in order to develop a detailed insight into the hydrogen embrittlement mechanisms relevant for cyclic loading conditions. It was found that a lower nickel content and a higher martensite content of the samples led to a higher susceptibility to hydrogen embrittlement. In addition, crack propagation and crack path could be simulated well with the simulation model.

  10. The research of axial corrosion fatigue on 10Ni3CrMoV steel

    Science.gov (United States)

    Xie, Xing; Yi, Hong; Xu, Jian; Xie, Kun

    2017-09-01

    Fatigue life had been studied with 10CrNi3MoV steel at different load ratios and in different environmental medias. The microstructure and micro-topography had been observed and analyzed by means of SEM, EDS and TEM. Our findings indicated that, the fatigue life of 10Ni3CrMoV steel in seawater was shorter than in air, the difference in longevity was larger with the decreasing of axis stress. Corrosion pits had a great influence on corrosion fatigue life.

  11. Corrosion resistance of premodeled wires made of stainless steel used for heart electrotherapy leaders

    International Nuclear Information System (INIS)

    Przondziono, J; Szatka, W; Walke, W; Młynarski, R

    2012-01-01

    The purpose of the study is to evaluate resistance to electrochemical corrosion of wire made of X10CrNi18-8 stainless steel designed for use in cardiology treatment. The influence of strain formed in the premodeling process and methods of wire surface preparation to corrosive resistance in artificial plasma solution were analysed. Wire corrosion tests were carried out in the solution of artificial plasma. Resistance to electrochemical corrosion was evaluated on the ground of recorded curves of anodic polarization by means of potentiodynamic method. Potentiodynamic tests carried out enabled to determine how the resistance to pitting corrosion of wire changes, depending on strain formed in the premodeling process as well as on the method of wire surface preparation. For evaluation of phenomena occurring on the surface of tested steel, electrochemical impedance spectroscopy (EIS) was applied. Deterioration of corrosive properties of wire along with the increase in the formed strain hardening was observed.

  12. Sodium corrosion tests in the ML 1 circuit

    International Nuclear Information System (INIS)

    Borgstedt, H.U.

    1977-01-01

    In the ML-1 circuit of the 'Juan Vigon' research centre in Madrid, sodium corrosion tests are being carried out on the austenitic steels DIN 1.4970 (X10NiCrMoTiB1515) and DIN 1.4301 (X5CrNi189) at temperatures between 500 and 700 0 C. The exposure time of the samples amounts to 6,000 h by now. Every 1,000 h, the samples were weighed in order to measure corrosion and deposition effects. After 3,000 and 6,000 h, some selected samples were destroyed for inspection. The results are given. (GSC) [de

  13. Weldability of Stainless Steels

    International Nuclear Information System (INIS)

    Saida, Kazuyoshi

    2010-01-01

    It gives an outline of metallographic properties of welding zone of stainless steels, generation and mechanisms of welding crack and decreasing of corrosion resistance of welding zone. It consists of seven chapters such as introduction, some kinds of stainless steels and properties, metallographic properties of welding zone, weld crack, toughness of welding zone, corrosion resistance and summary. The solidification modes of stainless steels, each solidification mode on the cross section of Fe-Cr-Ni alloy phase diagram, each solidification mode of weld stainless steels metal by electron beam welding, segregation state of alloy elements at each solidification mode, Schaeffler diagram, Delong diagram, effects of (P + S) mass content in % and Cr/Ni equivalent on solidification cracking of weld stainless steels metal, solidification crack susceptibility of weld high purity stainless steels metal, effects of trace impurity elements on solidification crack susceptibility of weld high purity stainless steels metal, ductile fracture susceptibility of weld austenitic stainless steels metal, effects of H2 and ferrite content on generation of crack of weld 25Cr-5N duplex stainless steels, effects of O and N content on toughness of weld SUS 447J1 metals, effect of ferrite content on aging toughness of weld austenitic stainless steel metal, corrosion morphology of welding zone of stainless steels, generation mechanism of knife line attack phenomenon, and corrosion potential of some kinds of metals in seawater at room temperature are illustrated. (S.Y.)

  14. Corrosion of X65 Pipeline Steel Under Deposit and Effect of Corrosion Inhibitor

    Directory of Open Access Journals (Sweden)

    XU Yun-ze

    2016-10-01

    Full Text Available Effect of the deposit on the electrochemical parameters of X65 pipeline steel in oxygen contained sodium chloride solution was studied by EIS and PDS methods. The galvanic corrosion behavior under deposit and effect of different concentration of corrosion inhibitor PBTCA were studied by electrical resistance (ER method combined with ZRA. The results show that the corrosion potential of X65 steel shifts negatively as SiO2 covering its surface and the corrosion rate becomes lower. When the galvanic couple specimen with deposit is electrically connected with the specimen without deposit, anodic polarization occurs on X65 steel under deposit and the galvanic current density decreases from 120μA/cm2 to 50μA/cm2 and keeps stable. As 5×10-5, 8×10-5 and 3×10-4 PBTCA were introduced into the solution, the galvanic current density reaches the highest 1300μA/cm2 and then decreases to 610μA/cm2 keeping stable around 610μA/cm2, corrosion rate of X65 steel under deposit reaches 6.11mm/a. PBTCA accelerates the corrosion of X65 steel under deposit in oxygen contained solution. Through the investigation on the surface of the specimens, serious local corrosion occurs on the X65 steel surface under deposit.

  15. Structure of maraging steel after thermomechanical treatment at high temperature

    International Nuclear Information System (INIS)

    Prokoshkina, V.G.; Kaputkina, L.M.; Mozzhukhin, V.E.

    1981-01-01

    Developed polygonized substructure is formed in austenite of maraging Cr-Ni steels under the selected conditions of hot deformation during high temperature mechanical treatment (HTMT). Substructure of hot deformed austenite is inherited by packet martensite during cooling. Presence of developed polygonized substructure in austenite results in grinding and high uniformity of packet sizes of martensite crystals. Substructure of α-phase of the investigated steels after HTMT, as well as the one inherited from hot deformed austenite, is inherited at α→γ-transformation in the process of repetitive austenization, and it can be preserved within a limited temperature-time range of heating in γ-region [ru

  16. Requirements on cast steel for the primary coolant circuit of water cooled reactors

    International Nuclear Information System (INIS)

    The most important requirements placed on the structural components of water cooled nuclear reactors include corrosion resistance and mechanical materials properties. Intercrystalline corrosion resistance was tested using the Strauss Test in compliance with the DIN 50914 Standard. Following sensitization between 600 to 700 degC with a dwell time between 15 minutes and 100 hours, a specimen homogeneously annealed with the casting and rapidly water cooled showed no intercrystalline corrosion. Specimens cooled from 1050 degC at a rate of 100 degC per hour showed no unambiguous tendency for intercrystalline corrosion after sensitization; in some cases, however, an initial attack of intercrystalline corrosion was found. It was found that austenitic Cr-Ni cast steel containing 2.5% Mo and about 15% ferrite showed the sensitive intercrystalline corrosion range at higher temperatures and longer dwell times than rolled Cr-Ni steels. In plating the ferritic cast steel with a corrosion resistant plating material, annealing temperature after welding must not exceed 600 to 620 degC otherwise the resistance of the plated layer against intercrystalline corrosion would not be safeguarded, and following annealing for stress removal at a temperature of 600 to 620 degC all requirements must be satisfied by the weld metal and weld transition placed on the initial material. Martensite materials are used for the manufacture of components which are not used under pressure, such as alloys with 13% Cr and 1% to 6% Ni and alloys with 17% Cr and 4% Ni. Carbon content is maintained below 0.10% to guarantee good weldability and the highest corrosion resistance. Cast steels with 13% Cr and 4% Ni after a dwell of 2500 hours in fully desalinated water without oxygen and with 3600 ppm of boron at a test temperature of 95 to 300 degC showed a surface reduction of 0.005 mm annually. In identical conditions except for the water containing oxygen the reduction in surface was 0.05 mm per year. (J.B.)

  17. The influence of Boron on creep-rupture behaviour of austenitic unstabilized and Nb-stabilized stainless steel X8CrNi 1613 in unirradiated and irradiated condition

    International Nuclear Information System (INIS)

    Sen, Susant Kumar.

    1976-10-01

    The present study deals with influence of boron on creep-rupture behaviour in unirradiated condition at 650 0 C along with precipitation behaviour, heat-treatment and recrystallization of unstabilized and stabilized steel. The results of creep-rupture tests on unirradiated specimens show that boron exerts a beneficial effect on the rupture life and ductility. Boron losses its beneficial effect on creep properties in unstabilized steel by prolong creeping. The magnitude of beneficial effect of Boron on creep properties depends upon the initial boron distribution which influences the number, size and distribution of the precipitates. Boron promotes the precipitation of type M 23 C 6 Carbides in the grain as well as at the grain boundary. Boron segregates in atomic form during slow cooling from austenitizing temperature. The recrystallization will be delayed by the presence of boron. The results of creep tests at 650 0 C shows that boron exerts a beneficial effect on creep life of irradiated steels. (orig./GSC) [de

  18. Rootslased Kärdlas 1811. aastal / Andres Pisa

    Index Scriptorium Estoniae

    Pisa, Andres

    2011-01-01

    1810. aastal tabas Kärdla rootslasi väljasaatmine. Parun Ungern-Sternberg asustas Vormsile 302 Kärdla rootslast. Pärast väljasaatmist 1810-1811 Kärdlasse jäänud ja juurdetulnud rootslastest. Andmete selgitamisel on kasutatud kuuenda ülevenemaalise hingerevisjoni materjale

  19. RF plasma nitriding of severely deformed iron-based alloys

    International Nuclear Information System (INIS)

    Ferkel, H.; Glatzer, M.; Estrin, Y.; Valiev, R.Z.; Blawert, C.; Mordike, B.L.

    2003-01-01

    The effect of severe plastic deformation by cold high pressure torsion (HPT) on radio frequency (RF) plasma nitriding of pure iron, as well as St2K50 and X5CrNi1810 steels was investigated. Nitriding was carried out for 3 h in a nitrogen atmosphere at a pressure of 10 -5 bar and temperatures of 350 and 400 deg. C. Nitrided specimens were analysed by scanning electron microscopy (SEM), X-ray diffraction and micro hardness measurements. It was found that HPT enhances the effect of nitriding leading almost to doubling of the thickness of the nitrided layer for pure iron and the high alloyed steel. The largest increase in hardness was observed when HPT was combined with RF plasma nitriding at 350 deg. C. In the case of pure iron, the X-ray diffraction spectra showed the formation of ε and γ' nitrides in the compound layer, with a preferential formation of γ' at the expense of the α-phase at the higher nitriding temperature. The corresponding surface hardness was up to 950 HV0.01. While the HPT-processed St2K50 exhibits both nitride phases after nitriding at 350 deg. C, only the γ'-phase was observed after nitriding at 400 deg. C. A surface hardness of up to 1050 HV0.01 was measured for this steel. The high alloyed steel X5CrNi1810 exhibited the highest increase in surface hardness when HPT was combined with nitriding at 350 deg. C. The surface hardness of this steel was greater than 1400 HV0.025. The XRD analyses indicate the formation of the expanded austenite (S-phase) in the surface layer as a result of RF plasma nitriding. Furthermore, after HPT X5CrNi1810 was transformed completely into deformation martensite which did not transform back to austenite under thermochemical treatment. However, in the case of nitriding of the HPT-processed high alloyed steel at 400 deg. C, the formation of the S-phase was less pronounced. In view of the observed XRD peak broadening, the formation of nitrides, such as e.g. CrN, cannot be ruled out

  20. Creep and time to rupture of a 16/16 Cr Ni Steel; Comportamiento a la fluencia lenta de la aleacion X 8 Cr Ni Mo Nb 1616 con distintos tratamientos termicos

    Energy Technology Data Exchange (ETDEWEB)

    Solano, R; Garcia, R; Bohm, H; Schirra, M

    1972-07-01

    The influence of different thermal-mechanical treatments on the creep and time to rupture of a 16/16 Cr.Ni steel is studied. The solution treated material after annealing at 700-800 degree centigree did not affect time to rupture. At the contrary a 12% cold-working and annealing at 800 degree centigree improve the time to rupture. This treatment is preserved up to 700 degree centigree 10{sup 4} hours. The ductility is not strongly affected. A metallographic study of the fracture was carried out. (Author) 23 refs.

  1. X-ray analysis in the steel industry

    International Nuclear Information System (INIS)

    Bourke, T.; Turner, K.

    1999-01-01

    Full text: The steel industry makes extensive use of X-ray analysis at all stages of the steelmaking process. XRF and XRD techniques, together with the associated techniques of electron probe microanalysis and electron microscopy are key tools for exploration and mine site and process development where detailed grade and mineralogical data is required. In production X-ray analysis is used to monitor and control: mine product grade (eg iron ore, coal and other raw materials), steel making production processes (eg iron ore sinter, incoming raw materials), waste products (eg coal watery refuse, slags) and final products (eg paint coatings, customer complaints). The demands put on X-ray analysis by the Steel Industry are severe. Iron ore mining and steelmaking is a continuous process, hence instrumentation has to be robust and reliable. In addition, with ever tightening environmental controls there is an increasing demand for trace heavy element analysis in both raw and waste materials. Copyright (1999) Australian X-ray Analytical Association Inc

  2. Development of a high-energy x-ray CT and its application to iron and steel analysis

    International Nuclear Information System (INIS)

    Taguchi, Isamu

    1987-01-01

    X-ray computed tomographic scanners are extensively used in medicine but have rarely been applied to non-medical purposes. Steel specimens pose particularly difficult problems - very poor transmission of X-rays and the need for high resolving capability. There have thus been no effective tomographic methods for examining steel specimens. Due to the growing need for non-destructive, non-contact methods for observing and analyzing the internal conditions of steel and raw materials for steel, however, we have developed a new high-energy computed tomographic scanner for steel (CTS). Its major specifications and functions are as follows. Type : 2nd-generation CT, 8-channel, Scanning method : 6deg revolution, 30-time traversing, Slice width : 0.3 mm, Resolving capability : 0.1 x 0.1 mm X-ray source : 420 kV, 3 mA, X-ray detector : BGO scintillator, Standard sample size : 50 mm dia., 50 mm high, Data collection time : 9.5 or 5 min. The CTS was successfully applied to the observation and the analysis of porosities of stainless steel (SUS 304) bloom, pores of iron ore sinters and metallic phases of the meteirites found in Antarctic Continent. (author)

  3. 22 CFR 181.1 - Purpose and application.

    Science.gov (United States)

    2010-04-01

    ..., will not give rise to a cause of action, and will not affect any public or private rights established... Foreign Relations DEPARTMENT OF STATE INTERNATIONAL AGREEMENTS COORDINATION, REPORTING AND PUBLICATION OF INTERNATIONAL AGREEMENTS § 181.1 Purpose and application. (a) The purpose of this part is to implement the...

  4. Analysis of the austenitic stainless steel's r-value behavior at elevated temperatures

    Directory of Open Access Journals (Sweden)

    Dušan Arsić

    2015-05-01

    Full Text Available An analysis of the anisotropy properties of austenitic steel AISI 304 (X5CrNi18-10 at elevated temperatures is presented in this paper. Considerations of the anisotropy problems are presented in the theoretical part of the paper, as well as the procedure for determination of the normal anisotropy coefficient. The experimental part of the paper describes the plan, methodology and equipment for testing of material's normal anisotropy and mechanical characteristics. The objective of conducting the experiments was to investigate influence of temperature on normal anisotropy, as well as on the mechanical properties of the considered material. The normal anisotropy was monitored by the coefficient – the so-called "r-value". Besides that, the tensile strength, yield stress and elongation at break were monitored, also. The tests were done on the 0.7 mm thick sheet metal within the temperature range 20 to 700°C.

  5. Effect of Solution Annealing on Susceptibility to Intercrystalline Corrosion of Stainless Steel with 20% Cr and 8% Ni

    Science.gov (United States)

    Taiwade, R. V.; Patil, A. P.; Patre, S. J.; Dayal, R. K.

    2013-06-01

    In general, as-received (AR) austenitic stainless steels (ASSs) contain complex carbide precipitates due to manufacturing operations, subsequent annealing treatment, or due to the fabrication processes such as welding. The presence of pre-existing carbides leads to cumulative sensitization and make the steel susceptible to intercrystalline corrosion (ICC)/intergranular corrosion (IGC) which causes premature failure during service. Solution annealing (SA) is one of the ways to deal with such situations. In this present investigation, the AR (hot rolled and mill annealed) chromium-nickel (Cr-Ni) ASS is compared with SA Cr-Ni ASS. The extent of ICC/IGC was evaluated qualitatively and quantitatively by various electrochemical tests including ASTM standard A-262 Practice A and Practice E, double loop electrochemical potentiokinetic reactivation and electrochemical impedance spectroscopy. The degree of sensitization for hot rolled mill annealed AR condition is found to be substantially higher (51.55%) than that of SA condition (26.9%) for thermally aged samples (at 700 °C). The chemical composition across the grain boundary was measured using electron probe micro-analyzer for both (AR and SA) conditions and confirms that the pre-sensitization effect was completely removed after SA treatment.

  6. Research of Technological Properties of Steel X6CRNITI18-10 Welded Joints Exploited in Nitric Acid Medium

    Directory of Open Access Journals (Sweden)

    Gediminas Mikalauskas

    2016-04-01

    Full Text Available The repair of chemical industry equipments often requires to replace long time operated pipes or welded inserts with the simi-lar chemical composition. During the study the joints from corro-sion resistant steel X6CrNiTi18-10 were welded by manual metal arc welding with covered electrodes (MMA process 111 and tungsten inert gas welding (TIG process 141 at different welding parameters. The visual, radiographic, penetrant control and ferrite content analysis were carried out. The transverse tensile and bending samples were produced from welded samples; also the macroscopic and microscopic analyse were carried out.

  7. Corrosion behaviour of the welded steel 1.4313/CA6-NM

    OpenAIRE

    Lovíšek, Martin; Liptáková, Tatiana; Pešlová, Františka

    2014-01-01

    The stainless steel 1.4313/CA6-NM (EN X3CrNiMo13-4) is used for turbine production. The weld joints are therefore very sensitive localities from mechanical and corrosion point of view. The subject of the work is corrosion studying of the steel welded by TIG method with consequent heat treatment. Corrosion resistance of the weld joints and base material are evaluated through potentiodynamic polarization test measured on the surface after heat treatment and on the surface cleaned by grinding an...

  8. Improved hardness of laser alloyed X12CrNiMo martensitic stainless steel

    CSIR Research Space (South Africa)

    Adebiyi, DI

    2011-07-01

    Full Text Available The improvement in hardness of X12CrNiMo martensitic stainless steel laser alloyed with 99.9% pure titanium carbide, stellite 6 and two cases of premixed ratio of titanium carbide and stellite 6 [TiC (30 wt.%)- stellite 6 (70 wt.%) and TiC (70 wt...

  9. Failure investigations in the nuclear materials laboratory

    International Nuclear Information System (INIS)

    Woitscheck, A.

    1982-01-01

    A report is given of damage to hydrostatic floating seals (with a single-stage pressure drop of 155 bar) from pressurized water reactors. The seals were manufactured from the steel X 22 CrNi 17 and plasmacoated with a layer of Cr 2 O 3 . The types of damage occurring (green discoloration and hump formation) are discussed in terms of their mechanistic causes. A further investigation involved metallographic examination with optical and scanning electron microscopes of seven specimens from thin-walled piping made of the finegrained, structural steel 17 MnMoV 6,4 in which cracking had occurred in weld regions, in particular, crack growth and the form of cracking at the weld root were investigated. (orig.) [de

  10. Structural chemistry and magnetic properties of Pr3-xSr1+xCrNiO8

    International Nuclear Information System (INIS)

    Dutton, Sian E.; Bahout, Mona; Battle, Peter D.; Tonus, Florent; Demange, Valerie

    2008-01-01

    Polycrystalline samples of the n=1 Ruddlesden-Popper system Pr 3-x Sr 1+x CrNiO 8 have been synthesized over the composition range 0.0 0.1 adopt the tetragonal space group I4/mmm; Pr 2.9 Sr 1.1 CrNiO 8 adopts the orthorhombic space group Fmmm. There is no evidence of Cr/Ni cation ordering in any composition. A maximum in the zero-field cooled magnetic susceptibility is observed at a temperature T f that decreases with increasing Sr content; 52≤T f (K)≤13. The frequency dependence of T f observed in a.c. susceptibility measurements, together with the analysis of neutron diffraction data, suggests that the atomic magnetic moments in these compositions adopt a spin-glass-like state below T f . - Graphical abstract: The n=1 Ruddlesden-Popper system Pr 3-x Sr 1+x CrNiO 8 (0.0< x≤1.0) has been characterized by diffraction methods and magnetometry. There is no evidence of Cr/Ni cation ordering in any composition. The atomic magnetic moments adopt a spin-glass-like state below a transition temperature that decreases from 52 K (x=0.1) to 13 K (x=1.0)

  11. Damage evolution in TWIP and standard austenitic steel by means of 3D X ray tomography

    Energy Technology Data Exchange (ETDEWEB)

    Fabrègue, D., E-mail: damien.fabregue@insa-lyon.fr [Université de Lyon, CNRS, F-69621 Villeurbanne (France); INSA-Lyon, MATEIS UMR5510, F-69621 Villeurbanne (France); Landron, C. [Université de Lyon, CNRS, F-69621 Villeurbanne (France); INSA-Lyon, MATEIS UMR5510, F-69621 Villeurbanne (France); Bouaziz, O. [ArcelorMittal Research, Voie Romaine-BP30320, F-57283 Maizières les Metz (France); Maire, E. [Université de Lyon, CNRS, F-69621 Villeurbanne (France); INSA-Lyon, MATEIS UMR5510, F-69621 Villeurbanne (France)

    2013-09-01

    The evolution of ductile damage of Fe–22Mn–0.6C austenitic TWIP steel by means of 3D X ray tomography in-situ tensile tests is reported for the first time. The comparison with another fully austenitic steel (316 stainless steel) is also carried out. The damage process of TWIP steel involves intense nucleation of small voids combined with the significant growth of the biggest cavities whereas macroscopical triaxiality remains constant. Due to this high nucleation rate, the average cavity diameter remains constant unlike the 316 stainless steel.

  12. Effect of load ratio and saltwater corrosive environment on the initiation life of fatigue of 10Ni5CrMoV steel

    Science.gov (United States)

    Xie, Xing; Yi, Hong; Xu, Jian; Gen, Liming; Chen, Luyun

    2017-09-01

    Fatigue initiation life has been studied with 10CrNi5MoV steel for use in ocean engineering at different load ratios and in different environmental media. The microstructure and micro-topography have been observed and analyzed by means of SEM, EDS and EBSD. Our findings indicate that, the initiation life of 10Ni5CrMoV steel in seawater is shorter than that in air, and the difference in longevity is larger with the increasing of load ratio. Corrosion pits had a great influence on initial corrosion fatigue life.

  13. Quantitative description of changes in the structure in austenitic steels after hot temperature deformation

    International Nuclear Information System (INIS)

    Kuc, D.; Rodak, K.; Niewielski, G.; Hetmanczyk, M.

    1998-01-01

    An investigation on the structural changes in austenitic hard deformable Cr-Mn and Cr-Ni steels during dynamic recrystallization has been presented in the paper. The influence of the factors (strain rate, deformation, temperature) on the geometric characteristic of grains has been taken into consideration. Investigation of the structure were performed using metallographic microscope and transmission electron microscope. The results of researched should widen the theoretical background in order to the model of phenomena, which accompany the dynamic recovery and dynamic recrystallization. (author)

  14. Creep and time to rupture of a 16/16 Cr Ni Steel

    International Nuclear Information System (INIS)

    Solano, R.; Garcia, R.; Bohm, H.; Schirra, M.

    1972-01-01

    The influence of different thermal-mechanical treatments on the creep and time to rupture of a 16/16 Cr.Ni steel is studied. The solution treated material after annealing at 700-800 degree centigree did not affect time to rupture. At the contrary a 12% cold-working and annealing at 800 degree centigree improve the time to rupture. This treatment is preserved up to 700 degree centigree 10 4 hours. The ductility is not strongly affected. A metallographic study of the fracture was carried out. (Author) 23 refs

  15. Sliding Wear Behaviour and Corosion Resistance to Ringer’s Solution of Uncoated and DLC Coated X46Cr13 Steel

    Directory of Open Access Journals (Sweden)

    Scendo M.

    2016-12-01

    Full Text Available Sliding wear properties and corrosion resistance in Ringer’s solution of uncoated and diamond-like carbon (DLC coated X46Cr13 steel was tested. The Raman spectra showed that the DLC film was successfully coated by plasma assisted CVD method onto the steel surface. The wear test, carried out using a ball-on disk tribometer, revealed that the DLC coating show better resistance to sliding wear and lower friction coefficient against a 100Cr6 steel ball than five times softer X46Cr13 steel. The oxidation kinetic parameters were determined by means of both the gravimetric and electrochemical method. It was found that the DLC coating markedly decreased the rate of corrosion of the X46Cr13 steel, irrespective of the corrosion mechanism involved.

  16. Effect of process parameters on formability of laser melting deposited 12CrNi2 alloy steel

    Science.gov (United States)

    Peng, Qian; Dong, Shiyun; Kang, Xueliang; Yan, Shixing; Men, Ping

    2018-03-01

    As a new rapid prototyping technology, the laser melting deposition technology not only has the advantages of fast forming, high efficiency, but also free control in the design and production chain. Therefore, it has drawn extensive attention from community.With the continuous improvement of steel performance requirements, high performance low-carbon alloy steel is gradually integrated into high-tech fields such as aerospace, high-speed train and armored equipment.However, it is necessary to further explore and optimize the difficult process of laser melting deposited alloy steel parts to achieve the performance and shape control.This article took the orthogonal experiment on alloy steel powder by laser melting deposition ,and revealed the influence rule of the laser power, scanning speed, powder gas flow on the quality of the sample than the dilution rate, surface morphology and microstructure analysis were carried out.Finally, under the optimum technological parameters, the Excellent surface quality of the alloy steel forming part with high density, no pore and cracks was obtained.

  17. Investigation on fracture toughness of laser beam welded steels

    International Nuclear Information System (INIS)

    Riekehr, S.; Cam, G.; Santos, J.F. dos; Kocak, M.; Klein, R.M.; Fischer, R.

    1999-01-01

    Laser beam welding is currently used in the welding of a variety of structural materials including hot and cold rolled steels, high strength low alloy and stainless steels, aluminium and titanium alloys, refractory and high temperature alloys and dissimilar materials. This high power density welding process has unique advantages of cost effectiveness, low distortion, high welding speed, easy automation, deep penetration, narrow bead width, and narrow HAZ compared to the conventional fusion welding processes. However, there is a need to understand the deformation and fracture properties of laser beam weld joints in order to use this cost effective process for fabrication of structural components fully. In the present study, an austenitic stainless steel, X5CrNi18 10 (1.4301) and a ferritic structural steel, RSt37-2 (1.0038), with a thickness of 4 mm were welded by 5 kW CO 2 laser process. Microhardness measurements were conducted to determine the hardness profiles of the joints. Flat micro-tensile specimens were extracted from the base metal, fusion zone, and heat affected zone of ferritic joint to determine the mechanical property variation across the joint and the strength mismatch ratio between the base metal and the fusion zone. Moreover, fracture mechanics specimens were extracted from the joints and tested at room temperature to determine fracture toughness, Crack Tip Opening Displacement (CTOD), of the laser beam welded specimens. The effect of the weld region strength mis-matching on the fracture toughness of the joints have been evaluated. Crack initiation, crack growth and crack deviation processes have also been examined. These results were used to explain the influence of mechanical heterogeneity of the weld region on fracture behaviour. This work is a part of the ongoing Brite-Euram project Assessment of Quality of Power Beam Weld Joints (ASPOW). (orig.)

  18. Effects of Cooling Rate on 6.5% Silicon Steel Ordering

    Energy Technology Data Exchange (ETDEWEB)

    Cui, Jun [Ames Lab. and Iowa State Univ., Ames, IA (United States); Macziewski, Chad [Iowa State Univ., Ames, IA (United States); Jensen, Brandt [Ames Lab., Ames, IA (United States); Ouyang, Gaoyuan [Iowa State Univ., Ames, IA (United States); Zhou, Lin [Ames Lab., Ames, IA (United States); Dennis, Kevin [Ames Lab., Ames, IA (United States); Zarkevich, Nikolai [Ames Lab., Ames, IA (United States); Jiang, Xiujuan [Pacific Northwest National Lab. (PNNL), Richland, WA (United States); Tang, Wei [Ames Lab., Ames, IA (United States); Zhou, Shihuai [Ames Lab., Ames, IA (United States); Simsek, Emrah [Ames Lab., Ames, IA (United States); Napolitano, Ralph [Iowa State Univ., Ames, IA (United States); Kramer, Matt [Ames Lab., Ames, IA (United States)

    2017-03-02

    Increasing Si content improves magnetic and electrical properties of electrical steel, with 6.5% Si as the optimum. Unfortunately, when Si content approaches 5.7%, the Fe-Si alloy becomes brittle. At 6.5%, the steel conventional cold rolling process is no longer applicable. The heterogeneous formation of B2 and D03 ordered phases is responsible for the embrittlement. The formation of these ordered phases can be impeded by rapid cooling. However, only the cooling rates of water and brine water were investigated. A comprehensive study of the effect of rapid cooling rate on the formation of the ordered phases was carried out by varying wheel speed and melt-injection rate. Thermal imaging employed to measure cooling rates while microstructures of the obtained ribbons are characterized using X-ray diffraction and TEM. The electrical, magnetic and mechanical properties are characterized using 4-pt probe, VSM, and macro-indentation methods. The relations between physical properties and ordered phases are established.

  19. Cold metal transfer spot plug welding of AA6061-T6-to-galvanized steel for automotive applications

    International Nuclear Information System (INIS)

    Cao, R.; Huang, Q.; Chen, J.H.; Wang, Pei-Chung

    2014-01-01

    Highlights: • Two Al-to-galvanized steel spot plug welding joints were studied by CMT method. • The optimum process variables for the two joints were gotten by orthogonal test. • Connection mechanism of the two joints were discussed. -- Abstract: In this study, cold metal transfer (CMT) spot plug joining of 1 mm thick Al AA6061-T6 to 1 mm thick galvanized steel (i.e., Q235) was studied. Welding variables were optimized for a plug weld in the center of a 25 mm overlap region with aluminum 4043 wire and 100% argon shielding gas. Microstructures and elemental distributions were characterized by scanning electron microscopy with energy dispersive X-ray spectrometer. Mechanical testing of CMT spot plug welded joints was conducted. It was found that it is feasible to join Al AA6061T6-to-galvanized steel by CMT spot plug welding method. The process variables for two joints with Al AA6061T6-to-galvanized mild steel and galvanized mild steel-to-Al AA6061T6 are optimized. The strength of CMT spot welded Al AA6061T6-to-galvanized mild steel is determined primarily by the strength and area of the brazed interface. While, the strength of the galvanized mild steel-to-Al AA6061T6 joint is mainly dependent upon the area of the weld metal

  20. Development of banded microstructure in 34CrNiMo6 steel

    Directory of Open Access Journals (Sweden)

    A. Nagode

    2016-07-01

    Full Text Available In this paper the development of a banded microstructure in hot-rolled 34CrNiMo6 steel which consisted of bainitic and martensitic bands is explained. The chemical compositions of the bands were measured with energy dispersive x-ray spectroscopy (EDS, which showed that the martensitic bands contained more alloying elements (Mn, Cr, Mo, Si than bainitic bands. By using Oberhoffer reagent, the segregations of phosphorus were also revealed. These phosphorus segregations coincided with the positive segregations of the alloying elements. The continuous cooling transformation (CCT diagrams of steel were calculated. They confirmed the formation of martensite in positive segregations and the formation of bainite in negative segregations.

  1. Galvannealing of (high-)manganese-alloyed TRIP- and X-IP registered -steel

    Energy Technology Data Exchange (ETDEWEB)

    Blumenau, M. [ThyssenKrupp Steel Europe AG, Bamenohler Strasse 211, D-57402 Finnentrop (Germany); Norden, M. [DOC Dortmunder Oberflaechencentrum GmbH, Eberhardstrasse 12, D-44145 Dortmund (Germany); Friedel, F.; Peters, K. [ThyssenKrupp Steel Europe AG, Kaiser-Wilhelm-Strasse 100, D-47166 Duisburg (Germany)

    2010-12-15

    In this study the influence of Mn on galvannealed coatings of 1.7% Mn-1.5% Al TRIP- and 23% Mn X-IP registered -steels was investigated. It is shown that the external selective oxides like Mn, Al and Si of the TRIP steel which occur after annealing at 800 C for 60 s at a dew point (DP) of -25 C (5% H{sub 2}) hamper the Fe/Zn-reaction during subsequent galvannealing. Preoxidation was beneficially utilized to increase the surface-reactivity of the TRIP steel under the same dew point conditions. The influence of Mn on the steel alloy was investigated by using a 23% Mn containing X-IP registered -steel which was bright annealed at 1100 C for 60 s at DP -50 C (5% H{sub 2}) to obtain a mainly oxide free surface prior to hot dip galvanizing (hdg) and subsequent galvannealing. As well known from the literature Mn alloyed to the liquid zinc melt stabilizes {delta}-phase at lower temperatures by participating in the Fe-Zn-phase reactions, it was expected that the metallic Mn of the X-IP registered -steel increases the Fe/Zn-reactivity in the same manner. The approximation of the effective diffusion coefficient (D{sub eff}(Fe)) during galvannealing was found to be higher than compared to a low alloyed steel reference. Contrary to the expectation no increased Fe/Zn-reaction was found by microscopic investigations. Residual {eta}- and {zeta}-phase fractions prove a hampered Fe/Zn-reaction. As explanation for the observed hampered Fe/Zn-reaction the lower Fe-content of the high-Mn-alloyed X-IP registered -steel was suggested as the dominating factor for galvannealing. (Copyright copyright 2010 Wiley-VCH Verlag GmbH and Co. KGaA, Weinheim)

  2. Corrosion effect of Bacillus cereus on X80 pipeline steel in a Beijing soil environment.

    Science.gov (United States)

    Wan, Hongxia; Song, Dongdong; Zhang, Dawei; Du, Cuiwei; Xu, Dake; Liu, Zhiyong; Ding, De; Li, Xiaogang

    2018-06-01

    The corrosion of X80 pipeline steel in the presence of Bacillus cereus (B. cereus) was studied through electrochemical and surface analyses and live/dead staining. Scanning electron microscopy and live/dead straining results showed that a number of B. cereus adhered to the X80 steel. Electrochemical impedance spectroscopy showed that B. cereus could accelerate the corrosion of X80 steel. In addition, surface morphology observations indicated that B. cereus could accelerate pitting corrosion in X80 steel. The depth of the largest pits due to B. cereus was approximately 11.23μm. Many pits were found on the U-shaped bents and cracks formed under stress after 60days of immersion in the presence of B. cereus. These indicate that pitting corrosion can be accelerated by B. cereus. X-ray photoelectron spectroscopy results revealed that NH 4 + existed on the surface of X80 steel. B. cereus is a type of nitrate-reducing bacteria and hence the corrosion mechanism of B. cereus may involve nitrate reduction on the X80 steel. Copyright © 2018 Elsevier B.V. All rights reserved.

  3. Precipitation behaviors of X70 acicular ferrite pipeline steel

    Institute of Scientific and Technical Information of China (English)

    Hao Yu; Yi Sun; Qixiang Chen; Haitao Jiang; Lihong Zhang

    2006-01-01

    The morphology, structure, and chemical composition of precipitates in the final microstructure of Nb-V-Ti microalloyed X70 acicular ferrite pipeline steel were investigated using transmission electron microscopy (TEM) and energy dispersive X-ray spectroscopy (EDS). Precipitates observed by TEM can be classified into two groups. The large precipitates are complex compounds that comprise square-shaped TiN precipitate as core with fine Nb-containing precipitate nucleated on pre-existing TiN precipitate as caps on one or more faces at high temperature. In contrast, the fine and spherical Nb carbides and/or carbonitrides precipitate heterogeneously on dislocations and sub-boundaries at low temperature. From the analysis in terms of thermodynamics, EDS and chemical composition of the steel, NbC precipitation is considered to be the predominant precipitation behavior in the tested steel under the processing conditions of this research.

  4. Experiments for liquid metal embrittlement of fusion reactor materials by liquid lithium

    International Nuclear Information System (INIS)

    Grundmann, M.; Borgstedt, H.U.

    1984-10-01

    The liquid metal embrittlement behaviour of two martensitic-ferritic steels [X22CrMoV121 (Nr. 1.4923) and X18CrMoVNb 121 (Nr. 1,4914)] and one austenite chromium-nickel-steel X5CrNi189 (Nr. 1.4301) was investigated. Tensile tests in liquid lithium at 200 and 250 0 C with two different strain rates on precorroded samples (1000 h at 550 0 C in lithium) were carried out. Reference values were gained from tensile tests in air (RT, 250 0 C). It is concluded that there is sufficient compatibility of the austenitic steel with liquid lithium. The use of the ferritic-martensitic steels in liquid lithium on the other hand, especially at temperatures of about 550 0 C, seems to be problematic. The experimental results led to a better understanding of LME, applying the theory of this material failure. (orig./IHOE) [de

  5. Cutting using the CO laser. Trennen mit dem CO-Laser

    Energy Technology Data Exchange (ETDEWEB)

    Maisenhaelder, F.; Stoehr, M. (DLR, Inst. fuer Technische Physik, Stuttgart (Germany))

    1991-02-01

    Several cutting experiments were performed to investigate the maximum cutting speed when using CO or CO{sub 2} laser radiation. The material which was used for these experiments was mild steel (St 37) and stainless steel (V2A; X5CrNi 189), the material thickness varied from 0.5 mm to 4 mm. The cutting parameters, especially the focal power density and the focal diameter, were equal for both laser wavelengths. The experimental result shows an increased cutting speed with CO laser beams in comparison to CO{sub 2} laser beams.

  6. Passivation process of X80 pipeline steel in bicarbonate solutions

    Science.gov (United States)

    Zhou, Jian-Long; Li, Xiao-Gang; Du, Cui-Wei; Pan, Ying; Li, Tao; Liu, Qian

    2011-04-01

    The passivation process of X80 pipeline steel in bicarbonate solutions was investigated using potentiodynamic, dynamic electrochemical impedance spectroscopy (DEIS), and Mott-Schottky measurements. The results show that the shape of polarization curves changes with HCO{3/-} concentration. The critical `passive' concentration is 0.009 mol/L HCO{3/-} for X80 pipeline steel in bicarbonate solutions. No anodic current peak exists in HCO3/- solutions when the concentration is lower than 0.009 mol/L, whereas there are one and two anodic current peaks when the HCO3/- concentration ranges from 0.009 to 0.05 mol/L and is higher than 0.1 mol/L, respectively. DEIS measurements show that there exist active dissolution range, transition range, pre-passive range, passive layer formation range, passive range, and trans-passive range for X80 pipeline steel in the 0.1 mol/L HCO{3/-} solutions. The results of DEIS measurements are in complete agreement with the potentiodynamic diagram. An equivalent circuit containing three sub-layers is used to explain the Nyquist plots in the passive range. Analyses are well made for explaining the corresponding fitted capacitance and impedance. The Mott-Schottky plots show that the passive film of X80 pipeline steel is an n-type semiconductor, and capacitance measurements are in good accordance with the results of DEIS experiment.

  7. Microstructural stability of 21-6-9 stainless steel

    International Nuclear Information System (INIS)

    Krenzer, R.W.; Sanderson, E.C.

    1978-01-01

    Two experiments were designed to better define parameters for thermomechanical processing of 21-6-9 stainless steel. This steel is one of the nitrogen-strengthened chromium, manganese, and nickel austenitic stainless steels having mechanical properties that can be improved by a combination of plastic deformation and heat treatments. By heat-treating coupons, the time-temperature relationship of the precipitate phase, and the solutionizing, recrystallizing, and stress-relieving temperature ranges in 21-6-9 were established. Secondly, mechanical properties and microstructure as a function of percent deformation and stress-relieving temperature are reported

  8. Effect of Alternating Current on the Cathodic Protection and Interface Structure of X80 Steel

    Directory of Open Access Journals (Sweden)

    Huiru Wang

    2017-07-01

    Full Text Available This study employs potential-monitoring techniques, cyclic voltammetry tests, alternating current (AC voltammetry methods, and surface characterization to investigate the AC corrosion of cathodically protected X80 pipeline steel. In a non-passive neutral solution at pH 7.2, a sufficiently negative potential completely protects steel at an AC current density of 100 A/m2. In an alkaline solution at pH 9.6, more serious AC corrosion occurs at more negative cathodic protection (CP potential, whereas without CP the steel suffers negligible corrosion. In addition, the interface capacitance increases with AC amplitude. Based on these results, the AC corrosion mechanisms that function under various conditions are analyzed and described.

  9. Characterisation of weldment hardness, impact energy and microstructure in API X65 steel

    International Nuclear Information System (INIS)

    Hashemi, S.H.; Mohammadyani, D.

    2012-01-01

    The variation of microstructure and mechanical properties in various sub-zones of double submerged arc welded line pipe steel of grade API X65 was investigated. Instrumented Charpy V-notch tests and Vickers hardness experiments were conducted on the fusion zone, base metal and heat affected zone of the weld joint in 14.3 mm thick, 1219 mm outside diameter spiral pipeline. The lowest impact energy and the highest hardness level (160J and 218 HV, respectively) were recorded in the fusion zone. The low energy and high hardness characteristics of the seam weld can be attributed to its cast microstructure and the presence of grain boundary phases (such as proeutectoid ferrite), confirmed by standard metallographic observation. Despite this, service requirements set by the API 5L industry code (minimum impact energy of 73J, maximum hard spots of 350 HV) were fulfilled by the tested steel. Highlights: ► Experimental study of API X65 steel microstructure. ► Analysis of the relationship between X65 steel microstructure and hardness. ► Analysis of the relationship between X65 steel microstructure and impact energy. ► Presentation of detailed technical information on DSA welding in spiral pipes.

  10. Analysis of a multi pass weld of a thick walled tube made of austenitic stainless steel X6 CrNiNb 18 10

    International Nuclear Information System (INIS)

    Scholtes, B.; Zinn, W.; Ilg, U.; Backfisch, W.; Gibmeier, J.; Kirch, D.

    2006-01-01

    In this paper, microstructure and residual stresses of a multi pass welding of a thick-walled tube made of austenitic stainless steel X6 CrNiNb 18 10 (1.4550) are systematically characterized and assessed. Results of microstructural and phase analyses, residual stress and hardness measurements as well as of a tensile test using micro specimen and SEM analyses are presented. Using these data, plastic deformations occurring during the welding process in the vicinity of the weld seam are evaluated. Finally, consequences of an additional heat treatment at 400 C/24 h are studied. (Abstract Copyright [2006], Wiley Periodicals, Inc.) [de

  11. De Amsterdamse bouwmeester en landmeter Jan Jacobszoon Bolten (1738-na 1811)

    NARCIS (Netherlands)

    von der Dunk, T.H.

    2013-01-01

    The Amsterdam architect and surveyor Jan Jacobszoon Bolten (1738-after 1811) is one of many private architects whose name pops up now and then in the literature. This essay, for the first time, sketches his quite varied career. Since mid-1768 he held the post of architect and surveyor in the

  12. Evolution of surfaces properties for 100Cr6 steel by implantation and ionic mixing

    International Nuclear Information System (INIS)

    Faussemagne, A.

    1996-01-01

    Physico-chemical characterizations performed on samples of 100Cr6 steel implanted both with boron and nitrogen revealed the formation of boron nitride along with the following new phases: Fe 1-x (B, N), Fe 2-x (B, N) and Fe 3-x (B, N). A thorough analysis of boron NITRIDE 5BN) indicates that a low ion current density (3 μA.cm -2 ) in the case of the boron plus nitrogen sequence favours the formation of sp 2 bonds (hexagonal-BN) while a higher ion current density (6μA.cm -2 ) promotes sp 3 bonds cubic-BN) in the opposite sequence. Tribological tests carried out on these samples revealed that nitrogen and boron implantations do not lead to any significant improvement of friction and wear at variance with the results obtained by others authors. However, on a set samples accidentally contaminated with carbon during implantation, we noticed a considerable improvement of these tribological parameters. As this pollution is commonly encountered in surface treatment by ion beams, one can invoke this phenomenon to explain the origin of the discrepancy reported by the literature. Extensive investigations allowed us to conclude that surface carbon, whatever its origin (contamination, ion implantation or ion beam mixed coating), provided that its amount is sufficiently high (≥2 x 10 16 C.cm -2 ), decreases the coefficient of friction by a factor 5 and reduces drastically (∼ 100) the wear. A careful examination of the whole results led us to propose a theoretical model, based on the role of the asperities of the two bodies in contact, to explain the evolution of the coefficient of friction and wear with the amount of surface carbon. This analysis revealed that in order to improve friction and wear of 100Cr6 steel, one needs to coat this material with a well adherent carbon layer having a thickness higher than the asperity heights of the two bodies in contact. Finally, this study allowed us to develop a simple lower-cost process for the improvement of the tribological

  13. X-ray diffraction study of slags forming during corrosion resistant steel production

    International Nuclear Information System (INIS)

    Slavov, V.I.; Zadorozhnaya, V.N.; Shurygina, A.V.

    1990-01-01

    Using X-ray diffraction analysis slags, forming during corrosion-resistant 12Kh18N10T grade steel production by two flowsheets, are studied. Standard two-slag technology of steel production does not provide efficient disintegration of chromospinelides in slags, gives high steel contamination with respect to nonmetallic impurities, coarse structure and, as a consequence, presence of macrodefects on rolled products surface. One-slag steel melting technology with titanium alloying of the steel at vacuum causes fast removal of chromospinelides at the beginning of reduction period, promotes titanium absorption by the steel, refines nonmetallic inclusions, provides more fine structure and steel plasticity, removes surface defects

  14. Correction factors for safe performance of API X65 pipeline steel

    International Nuclear Information System (INIS)

    Hashemi, Sayyed H.

    2009-01-01

    Prediction of required Charpy energy for fracture arrest is vital for safe performance of gas transportation pipelines. This is commonly estimated through failure models calibrated in the past on fracture data from combined Charpy tests and full-thickness burst experiments. Unfortunately, such pipeline failure models are unable to correctly predict the minimum arrest toughness of thermo-mechanical controlled rolled (TMCR) steels. To refine the existing failure models, different empirical adjustments have been proposed in recent years. In this paper, similar correction factors were derived from fracture information of instrumented Charpy impact tests on API X65 steel. The contribution of different fracture mechanisms of impact test specimens was determined through energy partitioning analysis. Parts of the energy contribution were correlated then to the source of uncertainty observed in similar experiments. The applied technique was similar to that of previous studies on X70 and X100 steels, and proved to be encouraging in giving consistent results compared to available test data.

  15. X-ray impact induced desorption of gases from stainless steel surfaces

    International Nuclear Information System (INIS)

    Brumbach, S.; Kaminsky, M.

    1975-01-01

    During the operation of plasma devices the interaction of energetic photons with surfaces can cause gas release by photodesorption, and thereby contribute to plasma contamination. Measurements of gases released from stainless steel surfaces were made in an ultrahigh vacuum environment using x-rays characteristic for a tungsten target bremsstrahlung spectrum for electron energies varying from 15 to 50 keV. The predominant gas species observed mass spectrometically are CO 2 (m/e = 44), CO (m/e = 28), and O 2 (m/e = 32). Mean quantum yields for the release of these species from stainless steel were determined. For example, for fresh stainless steel surfaces irradiated by x-rays produced by 50 keV electrons, a mean quantum yield for molecular CO 2 release of 3 x 10 -4 molecules per photons in a bremsstrahlung spectrum at 50 keV electron energy was observed. Based on such a quantum yield an outgassing rate was determined

  16. Austenite Formation from Martensite in a 13Cr6Ni2Mo Supermartensitic Stainless Steel

    NARCIS (Netherlands)

    Bojack, A.; Zhao, L.; Morris, P.F.; Sietsma, J.

    2016-01-01

    The influence of austenitization treatment of a 13Cr6Ni2Mo supermartensitic stainless steel (X2CrNiMoV13-5-2) on austenite formation during reheating and on the fraction of austenite retained after tempering treatment is measured and analyzed. The results show the formation of austenite in two

  17. Residual stresses determination by neutron diffraction in a 100Cr6 chromium steel bearing ring

    Czech Academy of Sciences Publication Activity Database

    Rogante, M.; Martinat, G.; Mikula, Pavol; Vrána, Miroslav

    2013-01-01

    Roč. 51, č. 5 (2013), s. 275-281 ISSN 0023-432X R&D Projects: GA MŠk(XE) LM2011019 Institutional support: RVO:61389005 Keywords : 100Cr6 steel * rings * martensitic hardening * tempering * residual stress es * neutron diffraction Subject RIV: BM - Solid Matter Physics ; Magnetism Impact factor: 0.546, year: 2013

  18. X-ray diffraction study of microstructural changes during fatigue damage initiation in steel pipes

    Energy Technology Data Exchange (ETDEWEB)

    Pinheiro, B., E-mail: bianca@lts.coppe.ufrj.br [Laboratory of Mechanics of Lille (LML), UMR CNRS 8107, University of Lille 1, Boulevard Paul Langevin, Cite Scientifique, 59655 Villeneuve d' Ascq (France); Lesage, J. [Laboratory of Mechanics of Lille (LML), UMR CNRS 8107, University of Lille 1, Boulevard Paul Langevin, Cite Scientifique, 59655 Villeneuve d' Ascq (France); Pasqualino, I. [Subsea Technology Laboratory (LTS), Ocean Engineering Department, COPPE/Federal University of Rio de Janeiro, PO Box 68508, Cidade Universitaria, CEP 21945-970, Rio de Janeiro/RJ (Brazil); Benseddiq, N. [Laboratory of Mechanics of Lille (LML), UMR CNRS 8107, University of Lille 1, Boulevard Paul Langevin, Cite Scientifique, 59655 Villeneuve d' Ascq (France); Bemporad, E. [Interdepartmental Laboratory of Electron Microscopy (LIME), University of Rome TRE, Via Della Vasca Navale 79, 00146 Rome (Italy)

    2012-01-15

    Highlights: Black-Right-Pointing-Pointer In this work we study the fatigue damage evolution in an API 5L X60 steel. Black-Right-Pointing-Pointer Microstructural changes and residual stresses are evaluated during fatigue tests. Black-Right-Pointing-Pointer Microdeformations and macro residual stresses are estimated by X-ray diffraction. Black-Right-Pointing-Pointer Results are discussed in view of an indicator of fatigue damage initiation. Black-Right-Pointing-Pointer This indicator could allow the prediction of residual life before macrocracking. - Abstract: Steel pipes used in the oil and gas industry undergo the action of cyclic loads that can cause their failure by fatigue. A consistent evaluation of the fatigue damage during the initiation phase should fundamentally be based on a nanoscale approach, i.e., at the scale of the dislocation network, in order to take into account the micromechanisms of fatigue damage that precede macrocrack initiation and propagation until the final fracture. In this work, microstructural changes related to fatigue damage initiation are investigated in the API 5L X60 grade steel, used in pipe manufacturing. Microdeformations and macro residual stress are evaluated using X-ray diffraction in real time during alternating bending fatigue tests performed on samples cut off from an X60 steel pipe. The aim of this ongoing work is to provide ground for further development of an indicator of fatigue damage initiation in X60 steel. This damage indicator could allow a good residual life prediction of steel pipes previously submitted to fatigue loading, before macroscopic cracking, and help to increase the reliability of these structures.

  19. Effect of non-metallic inclusions on hydrogen-induced cracking of API5L X100 steel

    Energy Technology Data Exchange (ETDEWEB)

    Jin, T.Y.; Liu, Z.Y.; Cheng, Y.F. [Department of Mechanical and Manufacturing Engineering, University of Calgary, Calgary, Alberta (Canada)

    2010-08-15

    In this work, the type, composition and distribution of inclusions contained in an API5L X100 steel were characterized by scanning electron microscopy and energy-dispersive x-ray analysis. A hydrogen-charging at various current densities was used to introduce hydrogen into the steel, and the correlation between HIC and the inclusions was established. The microstructure of the steel consists of a leather-like bainitic ferrite matrix, with martensite/austenite as the second phase particles. At least four types of inclusions are contained in API5L X100 steel, elongated MnS inclusions and spherical Al-, Si- and Ca-Al-O-S-enriched inclusions. In particular, the majority of inclusions in the steel are Al-enriched. Upon hydrogen-charging, hydrogen blisters and HIC could be caused in the steel in the absence of external stress. The cracks are primarily associated with the Al- and Si-enriched inclusions, rather than the elongated MnS inclusion. The critical amount of hydrogen resulting in HIC of the tested API5L X100 steel is determined to be 3.24 ppm under condition in this work. (author)

  20. Preparation and properties of Fe{sub 80−x}Ni{sub x}P{sub 14}B{sub 6} bulk metallic glasses

    Energy Technology Data Exchange (ETDEWEB)

    Zhang, Ling; Ma, XiuHua [School of Physics Science and Technology, Xinjiang University, Urumqi, Xinjiang 830046 (China); Li, Qiang, E-mail: qli@xju.edu.cn [School of Physics Science and Technology, Xinjiang University, Urumqi, Xinjiang 830046 (China); Zhang, Jijun [School of Physics Science and Technology, Xinjiang University, Urumqi, Xinjiang 830046 (China); Ningbo Institute of Materials Technology and Engineering, Chinese Academy of Sciences, Ningbo, Zhejiang 315201 (China); Dong, Yaqiang; Chang, Chuntao [Ningbo Institute of Materials Technology and Engineering, Chinese Academy of Sciences, Ningbo, Zhejiang 315201 (China)

    2014-09-01

    Highlights: • Fe{sub 80−x}Ni{sub x}P{sub 14}B{sub 6} (x = 20–50 at.%) BMGs were prepared by fluxing and J-quenching techniques. • The highest GFA is reached at x = 40 and the corresponding critical diameter is up to 2.5 mm. • The present FeNi-based BMGs exhibit very large ε{sub p} and the ε{sub p} of Fe{sub 30}Ni{sub 50}P{sub 14}B{sub 6} BMG is 11.7%. • The present FeNi-based BMGs have much higher corrosion resistance than stainless steel. - Abstract: Bulk Fe{sub 80−x}Ni{sub x}P{sub 14}B{sub 6} (x = 20, 30, 40, 50 at.%) glassy alloy rods with the diameters of 1.0–2.5 mm were synthesized by combining fluxing technique and J-quenching technique. The glassy alloy rods were characterized by X-ray diffraction (XRD), differential scanning calorimetry (DSC) and vibrating sample magnetometer (VSM). It is found that the range of supercooled liquid region (ΔT{sub x}) is 27–32 K. The saturation magnetization of Fe{sub 80−x}Ni{sub x}P{sub 14}B{sub 6} (x = 20, 30, 40, 50 at.%) bulk glassy alloys gradually decreases from 1.13 T to 0.58 T with increasing Ni content from x = 20 to x = 50. More importantly, the present quaternary FeNiPB bulk metallic glasses (BMGs) shows a significant plastic strain, in particular, the plastic strain of Fe{sub 30}Ni{sub 50}P{sub 14}B{sub 6} BMG reaches as high as 11.7%. The corrosion resistance of the present FeNiPB BMGs was studied by weight-loss method, potentiodynamic polarization curves and scanning electron microscopy (SEM). It is shown that the corrosion resistance of the present FeNiPB BMGs in 0.5 M NaCl and 1 M HCl solution increases with Ni content, and further the present FeNiPB BMGs exhibit larger E{sub corr} values and lower I{sub corr} values, i.e. higher corrosion resistances, than that of stainless steel.

  1. AGAINST DARWIN: WILLEM G. BRILL (1811-1896) ON THE ORIGIN OF LANGUAGE

    NARCIS (Netherlands)

    Noordegraaf, J.

    1994-01-01

    The present paper deals with the contribution to the nineteenth-century debate on the origin of language that was made by the Dutch linguist Willem G. Brill (1811-1896). Brill published papers on this question both before and after 'Darwin'. When rejecting Darwin’s point of view Brill can be

  2. A Study on the Fatigue-Fractured Surface of Normalized SS41 Steel and M.E.F. Dual Phase Steel by an X-ray Diffraction Technique

    International Nuclear Information System (INIS)

    Oh, Sae Wook; Park, Young Chul; Park, Soo Young; Kim, Deug Jin; Hue, Sun Chul

    1996-01-01

    This study verified the relationship between fracture mechanics parameters and X-ray parameters for normalized SS41 steel with homogeneous crystal structure and M.E.F. dual phase steel(martensite encapsulated islands of ferrite). The fatigue crack propagation test were carried out and X-ray diffraction technique was applied to fatigue fractured surface. The change in X-ray parameters(residual stress, half-value breadth) according to the depth of fatigue fractured surface were investigated. The depth of maximum plastic zone, W y , were determined on the basis of the distribution of the half-value breadth for normalized SS41 steel and that of the residual stress for M.E.F. dual phase steel. K max could be estimated by the measurement of W y

  3. 49 CFR 661.6 - Certification requirements for procurement of steel or manufactured products.

    Science.gov (United States)

    2010-10-01

    ... § 661.6 Certification requirements for procurement of steel or manufactured products. If steel, iron, or... 49 Transportation 7 2010-10-01 2010-10-01 false Certification requirements for procurement of steel or manufactured products. 661.6 Section 661.6 Transportation Other Regulations Relating to...

  4. Determination of small amounts of aluminum in iron and steel by x-ray fluorescence analysis

    International Nuclear Information System (INIS)

    Ito, Minao; Sato, Shoki; Narita, Masanao

    1981-01-01

    The accuracy of X-ray fluorescence analysis for determining aluminum in steel is generally poor when the aluminum content is below 0.1%. In this study, it is confirmed that the existence of inhomogeneous acid-insoluble aluminum causes the poor accuracy of X-ray fluorescence analysis. The accuracy can be improved by adding granular ferro-zirconium to molten steel when sampling. By using this method, the accuracy of determining aluminum was 0.0024% for low alloy steels and 0.0022% for stainless steels as the standard deviation obtained for a series of differences between an analytical result and a standard value. Corrections for overlapping of the chromium spectrum, and for absorption and enhancement effects of co-existent elements are not necessary for the analysis of low alloy steels, whereas these corrections are necessary for the analysis of stainless steels. (author)

  5. Chemical analysis by X-ray fluorescence, of niobium in high-strength plate steels

    International Nuclear Information System (INIS)

    Iozzi, F.B.; Dias, M.J.P.

    1981-01-01

    The use of X-ray fluorescence spectrometry in quantitative analysis of niobium in steels, as an alternative solution for optical emission spectrometry, in the rapid chemical control of steel fabrication by LD type converters, is presented. (M.C.K.) [pt

  6. Effect of pH Value on the Electrochemical and Stress Corrosion Cracking Behavior of X70 Pipeline Steel in the Dilute Bicarbonate Solutions

    Science.gov (United States)

    Cui, Z. Y.; Liu, Z. Y.; Wang, L. W.; Ma, H. C.; Du, C. W.; Li, X. G.; Wang, X.

    2015-11-01

    In this work, effects of pH value on the electrochemical and stress corrosion cracking (SCC) behavior of X70 pipeline steel in the dilute bicarbonate solutions were investigated using electrochemical measurements, slow strain rate tensile tests and surface analysis techniques. Decrease of the solution pH from 6.8 to 6.0 promotes the anodic dissolution and cathodic reduction simultaneously. Further decrease of the pH value mainly accelerates the cathodic reduction of X70 pipeline steel. As a result, when the solution pH decreases form 6.8 to 5.5, SCC susceptibility decreases because of the enhancement of the anodic dissolution. When the solution pH decreases from 5.5 to 4.0, SCC susceptibility increases gradually because of the acceleration of cathodic reactions.

  7. Effects of C and Si on strain aging of strain-based API X60 pipeline steels

    Science.gov (United States)

    Sung, Hyo Kyung; Lee, Dong Ho; Lee, Sunghak; Lee, Byeong-Joo; Hong, Seung-Pyo; Kim, Young-Woon; Yoo, Jang Yong; Hwang, Byoungchul; Shin, Sang Yong

    2017-05-01

    Four types of strain-based API X60 pipeline steels were fabricated by varying the C and Si contents, and the effects of C and Si on strain aging were investigated. The 0.05 wt% C steels consisted mainly of polygonal ferrite (PF), whereas the 0.08 wt% C steels consisted of acicular ferrite (AF). The volume fraction of AF increased with increasing C content because C is an austenite stabilizer element. The volume fractions of bainitic ferrite (BF) of the 0.15 wt% Si steels were higher than those of the 0.25 wt% Si steels, whereas the volume fractions of the secondary phases were lower. From the tensile properties before and after the aging process of the strainbased API X60 pipeline steels, the yield strength increased and the uniform and total elongation decreased, which is the strain aging effect. The strain aging effect in the strain-based API X60 pipeline steels was minimized when the volume fraction of AF was increased and secondary phases were distributed uniformly. On the other hand, an excessively high C content formed fine precipitates, and the strain aging effect occurred because of the interactions among dislocations and fine precipitates.

  8. X-ray fractography on fatigue fracture surface of high manganese austenitic steel

    International Nuclear Information System (INIS)

    Akita, Koichi; Misawa, Hiroshi; Kodama, Shotaro; Saito, Tetsuro.

    1997-01-01

    Fatigue tests were carried out under constant stress amplitude, using a non-magnetic high manganese Mn-Cr steel. X-ray fractography was applied on the fatigue fractured surface to investigate the relationship between stress intensity factor and residual stress or half-value breadth of the X-ray diffraction profile. The fatigue crack propagation rate of this non-magnetic Mn-Cr steel had the same tendency as in the ordinary structural ferritic steels. The relationship between stress intensity factor and the residual stress or half-value breadth of the steel was almost the same as that of the ferritic cyclic work hardening steels. No stress induced transformation was observed on the fracture surface, but the residual stress on the fractured surface was compressive in the high stress intensity factors range, which is typical in the cyclic work hardening steels. The half-value breadth on the fractured surface increased with increasing effective stress intensity factor range. The relationship between the half-value breadth and stress intensity factor range was represented by a linear line regardless of the stress ratio. Therefore, the acting stress intensity factor range at the time of fracture can be estimated from the half-value breadth. The depth of monotonic plastic zone was estimated from the distribution of half-value breadth beneath the fractured surface. The relationship between the maximum stress intensity factor and half-value breadth was expressed by the equation ω m α(K max /σ y ) 2 , where the value of α was 0.025. This is about one sixth of the value for ferritic steels, and the fact shows the severe work hardening occuring in the plastic zone in this manganese steel. (author)

  9. Creep and precipitation behaviors of AL6XN austenitic steel at elevated temperatures

    Science.gov (United States)

    Meng, L. J.; Sun, J.; Xing, H.

    2012-08-01

    Creep behaviors of the solution-treated AL6XN austenitic stainless steel have been investigated at 873-1023 K and 120-260 MPa. The results showed that the creep stress exponent and activation energy of the AL6XN steel are 5 and 395.4 kJ/mol, respectively in the power-law breakdown regime. TEM observations revealed that dislocations distributed homogenously in grains. The creep deformation mechanism is mainly attributed to viscous dislocation glide. Precipitates in the steel after creep deformation were additionally analyzed by TEM, and the results showed that there are four different types of precipitates, such as M23C6, M6C, σ phase and Laves phase. The M23C6 carbides were observed at grain boundaries in the steel after creep at 873 K. The M6C, σ phase and Laves phase precipitates were found when the creep temperature increases to 923-1023 K. Although the AL6XN steel exhibited low steady state creep rates, a high volume fraction of brittle precipitates of σ and Laves phases reduced the creep lifetime of the steel at elevated temperatures.

  10. Creep and precipitation behaviors of AL6XN austenitic steel at elevated temperatures

    Energy Technology Data Exchange (ETDEWEB)

    Meng, L.J. [School of Materials Science and Engineering, Shanghai Jiaotong University, Dongchuan Road 800, Shanghai 200240 (China); Sun, J., E-mail: jsun@sjtu.edu.cn [School of Materials Science and Engineering, Shanghai Jiaotong University, Dongchuan Road 800, Shanghai 200240 (China); Xing, H. [School of Materials Science and Engineering, Shanghai Jiaotong University, Dongchuan Road 800, Shanghai 200240 (China)

    2012-08-15

    Creep behaviors of the solution-treated AL6XN austenitic stainless steel have been investigated at 873-1023 K and 120-260 MPa. The results showed that the creep stress exponent and activation energy of the AL6XN steel are 5 and 395.4 kJ/mol, respectively in the power-law breakdown regime. TEM observations revealed that dislocations distributed homogenously in grains. The creep deformation mechanism is mainly attributed to viscous dislocation glide. Precipitates in the steel after creep deformation were additionally analyzed by TEM, and the results showed that there are four different types of precipitates, such as M{sub 23}C{sub 6}, M{sub 6}C, {sigma} phase and Laves phase. The M{sub 23}C{sub 6} carbides were observed at grain boundaries in the steel after creep at 873 K. The M{sub 6}C, {sigma} phase and Laves phase precipitates were found when the creep temperature increases to 923-1023 K. Although the AL6XN steel exhibited low steady state creep rates, a high volume fraction of brittle precipitates of {sigma} and Laves phases reduced the creep lifetime of the steel at elevated temperatures.

  11. Fatigue fracture analysis in medium carbon structural steel and austenitic stainless steel by X-ray fractography

    International Nuclear Information System (INIS)

    Rao, N.N.; Azmi bin Rahmat

    1994-01-01

    Apart from the reidual stresses present in the bulk material, a growing fatigue crack may develop its own stress field ahead of the crack tip which in turn could influence the crack propagation behaviour. A fracture surface analysis through measurement of the residual stress of a failed component may provide some additional useful information to that obtained through conventional metallurgical and fracture mechanics investigations. This method of fracture surface analysis using x-ray diffraction technique is known as X -ray Fractography . Residual stress (ρ sub γ) and the full width at half maximum (FWHM) of the x-ray diffraction profile of any reflection are determined at different crack lengths on the fracture surface. These are then corelated to the fracture toughness parameters such as fracture toughness K sub I sub C, the maximum stress intensity factor K sub max and the stress intensity factor range δK. The present investigation aims at detailed x-ray analysis of the fatigue fractured surfaces of the compact tension specimens prepared from ferritic and austenitic stainless steels. The ferritic steel has been subjected to various heat treatments to obtain different microstructures and mechanical properties. The overall observations are analyzed through fatigue (cumulative) damage and material science concepts

  12. X-ray emission from stainless steel foils irradiated by femtosecond petawatt laser pulses

    Science.gov (United States)

    Alkhimova, M. A.; Faenov, A. Ya; Pikuz, T. A.; Skobelev, I. Yu; Pikuz, S. A.; Nishiuchi, M.; Sakaki, H.; Pirozhkov, A. S.; Sagisaka, S.; Dover, N. P.; Kondo, Ko; Ogura, K.; Fukuda, Y.; Kiriyama, H.; Esirkepov, T.; Bulanov, S. V.; Andreev, A.; Kando, M.; Zhidkov, A.; Nishitani, K.; Miyahara, T.; Watanabe, Y.; Kodama, R.; Kondo, K.

    2018-01-01

    We report about nonlinear growth of x-ray emission intensity emitted from plasma generated by femtosecond petawatt laser pulses irradiating stainless steel foils. X-ray emission intensity increases as ˜ I 4.5 with laser intensity I on a target. High spectrally resolved x-ray emission from front and rear surfaces of 5 μm thickness stainless steel targets were obtained at the wavelength range 1.7-2.1 Å, for the first time in experiments at femtosecond petawatt laser facility J-KAREN-P. Total intensity of front x-ray spectra three times dominates to rear side spectra for maximum laser intensity I ≈ 3.2×1021 W/cm2. Growth of x-ray emission is mostly determined by contribution of bremsstrahlung radiation that allowed estimating bulk electron plasma temperature for various magnitude of laser intensity on target.

  13. Investigations of corrosion films formed on API-X52 pipeline steel in acid sour media

    Energy Technology Data Exchange (ETDEWEB)

    Hernandez-Espejel, A. [Instituto Politecnico Nacional, Departamento de Ingenieria Metalurgica, IPN-ESIQIE, UPALM Ed. 7, Zacatenco 07738, Mexico, D.F. (Mexico); Dominguez-Crespo, M.A. [Instituto Politecnico Nacional, CICATA-Unidad Altamira-Tamaulipas, km 14.5, Carretera Tampico-Puerto Industrial Altamira, 89600 Altamira, Tamps (Mexico); Cabrera-Sierra, R. [Instituto Politecnico Nacional, Departamento de Ingenieria Quimica Industrial, IPN-ESIQIE, UPALM Ed. 7, Zacatenco 07738, Mexico, D.F. (Mexico); Rodriguez-Meneses, C. [Instituto Politecnico Nacional, Departamento de Ingenieria Metalurgica, IPN-ESIQIE, UPALM Ed. 7, Zacatenco 07738, Mexico, D.F. (Mexico); Arce-Estrada, E.M., E-mail: earce@ipn.m [Instituto Politecnico Nacional, Departamento de Ingenieria Metalurgica, IPN-ESIQIE, UPALM Ed. 7, Zacatenco 07738, Mexico, D.F. (Mexico)

    2010-07-15

    Corrosion films formed by voltammetry using different switching potentials and by immersion on API-X52 pipeline steel in simulated acid sour media (NACE ID182) have been characterized using Scanning Electron Microscopy (SEM), X-ray Diffraction (XRD), Linear Polarization and Electrochemical Impedance Spectroscopy (EIS) techniques. XRD and EDS analysis showed that the films are mainly composed of sulphide compounds (mackinawite, troilite, marcasite and pyrite) as well as iron oxides, as steel damage increases. Across SEM micrographs the corrosion films formed by potentiodynamic and immersion tests are very similar, covering most of the steel. Polarization and EIS results corroborate poor behavior against corrosion.

  14. Investigations of corrosion films formed on API-X52 pipeline steel in acid sour media

    International Nuclear Information System (INIS)

    Hernandez-Espejel, A.; Dominguez-Crespo, M.A.; Cabrera-Sierra, R.; Rodriguez-Meneses, C.; Arce-Estrada, E.M.

    2010-01-01

    Corrosion films formed by voltammetry using different switching potentials and by immersion on API-X52 pipeline steel in simulated acid sour media (NACE ID182) have been characterized using Scanning Electron Microscopy (SEM), X-ray Diffraction (XRD), Linear Polarization and Electrochemical Impedance Spectroscopy (EIS) techniques. XRD and EDS analysis showed that the films are mainly composed of sulphide compounds (mackinawite, troilite, marcasite and pyrite) as well as iron oxides, as steel damage increases. Across SEM micrographs the corrosion films formed by potentiodynamic and immersion tests are very similar, covering most of the steel. Polarization and EIS results corroborate poor behavior against corrosion.

  15. The mutual effects of hydrogen and microstructure on hardness and impact energy of SMA welds in X65 steel

    Energy Technology Data Exchange (ETDEWEB)

    Latifi, V. Amin; Miresmaeili, Reza, E-mail: miresmaeili@modares.ac.ir; Abdollah-Zadeh, Amir

    2017-01-02

    Micro-alloy steels are broadly used in gas and petroleum transportation industries. However, application of these steels in pipelines is challenged by hydrogen embrittlement due to presence of hydrogen sulfide in the medium. The present work deals with the interaction of hydrogen with plasticity of X65 steel. Two weld joints produced by common E7010-G and E7018 electrodes via shielded metal arc welding (SMAW) method were also investigated. It was revealed in microhardness test that direct charge of hydrogen to the surface did not lead to meaningful variations due to lamination as well as surface and sub-surface porosities. In fact, the effect of hydrogen on material plasticity was influenced by lamination and porosities. On the other hand, indirect charge on the tested surface led to increase in hardness by 12%, 9% and 6% in base metal as well as in weld metals obtained from E7010-G and E7018 electrodes, respectively. Therefore, hydrogen atoms affected plasticity of X65 steel more harshly than that of weld metals; thus, the base metal is more sensitive to hydrogen embrittlement. Due to high strain rate, impact test does not provide sufficient time for hydrogen diffusion through notch during the test. No observation of any variations in impact energies of charged samples may hence be explained by uniform hydrogen concentration throughout the samples. The base steel was seen to be much more sensitive to hydrogen defects rather than weld metals of both electrodes due to possessing pearlite/ferrite interfaces. According to hydrogen concentration studies, E710-G weld metal had more hydrogen diffusivity than X65 steel and E7018 weld metal by four time and 25%, respectively. This was due to acicular ferritic microstructure of E710-G weld metal and its dislocation tangles that provided many reversible traps for hydrogen.

  16. 1x2M steel performance in the BOR-60 steam generator

    International Nuclear Information System (INIS)

    Golovanov, V.N.; Shamardin, V.K.; Kondratiev, V.I.; Kryukov, F.N.; Chernobrovkin, Yu.V.; Bulanova, T.M.; Bai, V.F.

    The results from studies of 1x2M steel characteristics are presented. This steel was used as the material for the BOR-60 steam generator that had been in operation under the steam generating mode for 18,000 hs (35,000 hs in sodium). It was revealed that the pit corrosion depth on the water/steam side evaporative tube surfaces was about 0.25 μm and less and the total corrosion rate was less than 0.06 mm/y. The mechanical properties of the material were essentially similar both in the evaporator and superheater and met all the requirements imposed on. Based on the analysis of data on the decarbonizaton depth in sodium and on the corrosion damage in water and steam it was concluded that 1x2M steel can be successfully used as the steam generator material at the operating temperatures up to 470 deg. C and had sufficiently longer service-life as compared to 18,000 hs. (author)

  17. Effect of wheel speed on magnetic and mechanical properties of melt spun Fe-6.5 wt.% Si high silicon steel

    Science.gov (United States)

    Ouyang, Gaoyuan; Jensen, Brandt; Tang, Wei; Dennis, Kevin; Macziewski, Chad; Thimmaiah, Srinivasa; Liang, Yongfeng; Cui, Jun

    2018-05-01

    Fe-Si electric steel is the most widely used soft magnetic material in electric machines and transformers. Increasing the silicon content from 3.2 wt.% to 6.5 wt.% brings about large improvement in the magnetic and electrical properties. However, 6.5 wt.% silicon steel is inherited with brittleness owing to the formation of B2 and D03 ordered phase. To obtain ductility in Fe-6.5wt.% silicon steel, the ordered phase has to be bypassed with methods like rapid cooling. In present paper, the effect of cooling rate on magnetic and mechanical properties of Fe-6.5wt.% silicon steel is studied by tuning the wheel speed during melt spinning process. The cooling rate significantly alters the ordering and microstructure, and thus the mechanical and magnetic properties. X-ray diffraction data shows that D03 ordering was fully suppressed at high wheel speeds but starts to nucleate at 10m/s and below, which correlates with the increase of Young's modulus towards low wheel speeds as tested by nanoindentation. The grain sizes of the ribbons on the wheel side decrease with increasing wheel speeds, ranging from ˜100 μm at 1m/s to ˜8 μm at 30m/s, which lead to changes in coercivity.

  18. Recommendations on X80 steel for the design of hydrogen gas transmission pipelines

    International Nuclear Information System (INIS)

    Briottet, L.; Batisse, R.; De Dinechin, G.; Langlois, P.; Thiers, L.

    2012-01-01

    By limiting the pipes thickness necessary to sustain high pressure, high-strength steels could prove economically relevant for transmitting large gas quantities in pipelines on long distance. Up to now, the existing hydrogen pipelines have used lower-strength steels to avoid any hydrogen embrittlement. The CATHY-GDF project, funded by the French National Agency for Research, explored the ability of an industrial X80 grade for the transmission of pressurized hydrogen gas in large diameter pipelines. This project has developed experimental facilities to test the material under hydrogen gas pressure. Indeed, tensile, toughness, crack propagation and disc rupture tests have been performed. From these results, the effect of hydrogen pressure on the size of some critical defects has been analyzed allowing proposing some recommendations on the design of X80 pipe for hydrogen transport. Cost of Hydrogen transport could be several times higher than natural gas one for a given energy amount. Moreover, building hydrogen pipeline using high grade steels could induce a 10 to 40% cost benefit instead of using low grade steels, despite their lower hydrogen susceptibility. (authors)

  19. X-ray photoelectron spectroscopy characterization of high dose carbon-implanted steel and titanium alloys

    Science.gov (United States)

    Viviente, J. L.; García, A.; Alonso, F.; Braceras, I.; Oñate, J. I.

    1999-04-01

    A study has been made of the depth dependence of the atomic fraction and chemical bonding states of AISI 440C martensitic stainless steel and Ti-6Al-4V alloy implanted with 75 keV C + at very high doses (above 10 18 ions cm -2), by means of X-ray photoelectron spectroscopy combined with an Ar + sputtering. A Gaussian-like carbon distribution was observed on both materials at the lowest implanted dose. More trapezoidal carbon depth-profiles were found with increasing implanted doses, and a pure carbon layer was observed only on the titanium alloy implanted at the highest dose. The implanted carbon was combined with both base metal and carbon itself to form metallic carbides and graphitic carbon. Furthermore, carbon-enriched carbides were also found by curve fitting the C 1s spectra. The titanium alloy showed a higher carbidic contribution than the steel implanted at the same C + doses. A critical carbon concentrations of about 33 at.% and 23 at.% were measured for the formation of C-C bonds in Ti-6Al-4V and steel samples, respectively. The carbon atoms were bound with metal to form carbidic compounds until these critical concentrations were reached; when this C concentration was exceeded the proportion of C-C bonds increased and resulted in the growth of carbonaceous layers.

  20. Radiation-induced segregation at grain boundaries in AL-6XN stainless steels irradiated by hydrogen ions

    Science.gov (United States)

    Long, Yunxiang; Zheng, Zhongcheng; Guo, Liping; Zhang, Weiping; Shen, Zhenyu; Tang, Rui

    2018-04-01

    The effect of high concentration of hydrogen on the segregation of radiation-induced segregation (RIS) in AL-6XN stainless steels has been investigated by transmission electron microscopy (TEM) with energy-dispersive X-ray spectroscopy. Specimens were irradiated with 100 keV H2+ ions from 1 dpa to 5 dpa at 380 °C to investigated the dose dependence of grain boundary RIS. A specimen was irradiated to 5 dpa at 290 °C to study the effect of irradiation temperature. The trends of Cr depletion and Ni enrichment with irradiation dose is similar to that of other austenitic steels reported in the literatures, but the higher concentration of hydrogen made the RIS profile wider. An abnormal phenomenon that the degree of RIS increased with decreasing irradiation temperature was found, indicating that with the retention of hydrogen in the steels, temperature dependence of RIS is dominated by the quantity of retained hydrogen, rather than by thermal segregation processes.

  1. Standard practice for X-Ray determination of retained austenite in steel with near random crystallographic orientation

    CERN Document Server

    American Society for Testing and Materials. Philadelphia

    2003-01-01

    1.1 This practice covers the determination of retained austenite phase in steel using integrated intensities (area under peak above background) of X-ray diffraction peaks using chromium Kα or molybdenum Kα X-radiation. 1.2 The method applies to carbon and alloy steels with near random crystallographic orientations of both ferrite and austenite phases. 1.3 This practice is valid for retained austenite contents from 1 % by volume and above. 1.4 If possible, X-ray diffraction peak interference from other crystalline phases such as carbides should be eliminated from the ferrite and austenite peak intensities. 1.5 Substantial alloy contents in steel cause some change in peak intensities which have not been considered in this method. Application of this method to steels with total alloy contents exceeding 15 weight % should be done with care. If necessary, the users can calculate the theoretical correction factors to account for changes in volume of the unit cells for austenite and ferrite resulting from vari...

  2. Investigation of the fabrication process of hot-worked stainless-steel and Mo sheathed PbMo6 S8 wires

    International Nuclear Information System (INIS)

    Yamasaki, H.; Kimura, Y.

    1988-01-01

    Stainless-steel and Mo sheathed PbMo 6 S 8 wires have been fabricated by hot working from modified PbS, Mo, and MoS 2 mixed powders which were prepared by reacting Pb, Mo, and S at 530 0 C. Critical current densities were investigated for different preparation conditions, and it is revealed that obtaining continuous current path between PbMo 6 S 8 grains is the most important factor to achieve high critical current density. The J/sub c/ value of 2.8 x 10 4 Acm 2 (8 T), 7.8 x 10 3 Acm 2 (15 T), and 1.3 x 10 3 Acm 2 (23 T) was observed for the PbMo 6 S/sub 7.0/ wire heat treated at 700 0 C.copic

  3. Development of stress-modified fracture strain criterion for ductile fracture of API X65 steel

    International Nuclear Information System (INIS)

    Oh, Chang Kyun; Kim, Yun Jae; Park, Jin Moo; Kim, Woo Sik; Baek, Jong Hyun

    2005-01-01

    This paper presents a stress-modified fracture strain for API X65 steel used for gas pipeline, as a function of stress triaxiality. To determine the stress-modified fracture strain, tension test of bars with four different notch radii, made of API X65 steel, is firstly performed, from which true fracture strains are determined as a function of notch radius. Then detailed elastic-plastic, large strain Finite Element (FE) analyses are performed to estimate variations of stress triaxiality in the notched bars with load. Combining experimental with FE results provides the true fracture strain as a function of stress triaxiality, which is regarded as a criterion of ductile fracture. Application of the developed stress-modified fracture strain to failure prediction of gas pipes made of API X65 steel with various types of defects is discussed

  4. NEB in Analysis of Optical Flow 4 x 4 and 6 x 6-Patches

    International Nuclear Information System (INIS)

    Xia, Shengxiang; Liang, Di

    2017-01-01

    We apply the nudged elastic band technique to non-lineal high-dimensional datasets, we analyze spaces of 4 x 4 and 6 x 6 optical flow patches and detect their topological properties. We experimentally prove that subsets of 4 x 4 and 6 x 6 optical flow patches can be modeled a circle, which confirm some results of 4 x 4 and 6 x 6 optical flow patches by using a new method-NEB, and expend Adams et al's result to larger patches of optical flow. (paper)

  5. Investigation of intergranular corrosion resistance of Cr16Ni25NMo6 steel

    International Nuclear Information System (INIS)

    Kamenev, Yu.B.; Nazarov, A.A.; Kuusk, L.V.; Majdeburova, T.F.

    1990-01-01

    The effect of 08Kh16N25AM6 steel susceptibility to intergranular corrosion on its intergranular cracking resistance in high-temperature water is investigated. In addition, the performed tests point to the susceptibility of sensibilized Kh16N25AM6 steel to intergranular corrosion in media simulating an agressive environment of power generation equipment; the latter requires a strict control over the resistance of weld joints of the above steel to intergranular corrosion. It is shown that Kh16N25AM6 type steel in sensibilized state is susceptible to intercrystalline corrosion cracking in high-temperature water which correlates with its susceptibility to intergranular corrosion established by AM GOST 6032-84 and potentiodynamic reactivation methods

  6. Sodium alginate: A promising biopolymer for corrosion protection of API X60 high strength carbon steel in saline medium.

    Science.gov (United States)

    Obot, I B; Onyeachu, Ikenna B; Kumar, A Madhan

    2017-12-15

    Sodium alginate (SA), a polysaccharide biopolymer, has been studied as an effective inhibitor against the corrosion of API X60 steel in neutral 3.5% NaCl using gravimetric and electrochemical techniques (OCP, EIS and EFM). The inhibition efficiency of the SA increased with concentration but was lower at higher temperature (70°C). Electrochemical measurements showed that the SA shifted the steel corrosion potential to more positive value and reduced the kinetics of corrosion by forming an adsorbed layer which mitigated the steel surface wetting, based on contact angle measurement. SEM-EDAX was used to confirm the inhibition of SA on API X60 steel surfaces. The SA adsorbs on the steel surface through a physisorption mechanism using its carboxylate oxygen according to UV-vis and ATR-IR measurements, respectively. This phenomena result in decreased localized pitting corrosion of the API X60 steel in 3.5% NaCl solution. Theoretical results using quantum chemical calculations and Monte Carlo simulations provide further atomic level insights into the interaction of SA with steel surface. Copyright © 2017 Elsevier Ltd. All rights reserved.

  7. X-ray analysis on the fatigue fracture surface of stainless steels

    International Nuclear Information System (INIS)

    Yoshioka, Yasuo; Guimard, B.

    1986-01-01

    Several X-ray diffraction parameters were observed on the fatigue fracture surface and its vicinity of both of SUS420J1 martensitic and SUS304 austenitic stainless steels and we discussed the relation between the stress intensity factor and these parameters. Monotonic plastic zone depth determined by the measurement of residual stress distribution proportionals to the squre of the maximum stress intensity factor as well as the case of ferritic steel. However, it is very difficult to find the relation between the stress intensity factor and residual stress or half value breadth of X-ray diffraction profile in the fracture surface for both materials. On the other hand, the amount of martensite induced by the transformation during fatigue process in SUS304 is related to the maximum stress intensity factor in the fracture surface regardless the stress ratio R. (author)

  8. First occurrence of knight rock shrimp, Sicyonia lancifer (Olivier, 1811 (Decapoda: Sicyoniidae in the Mediterranean Sea.

    Directory of Open Access Journals (Sweden)

    A. PATANIA

    2015-01-01

    Full Text Available The occurrence of the non-native species Sicyonia lancifer  (Olivier, 1811 belonging to Sicyoniidae family is reported for the first time in the Mediterranean Sea. In the following  paper  the distinguishing features of the species are provided.

  9. Ciclo de desarrollo de Trigona (Tetragonisca angustula, Latreille 1811 (Hymenoptera, Trigonini

    Directory of Open Access Journals (Sweden)

    María Giomar Nates Parra

    1989-01-01

    Full Text Available Se estudió el ciclo de desarrollo de una abeja sin aguijón: Trigona (Tetragonisca angustula. Latreille 1811 (Hymenoptera. Trigonini. Los resultados fueron los siguientes: El periodo comprendido entre la postura del huevo y la emergencia del imago, es, en las obreras, de 36.5 días en promedio. La duración del ciclo se hace mayor a medida que las celdas se alejan del centro del panal. Se determinaron 3 instares larvales y 5 fases pupales para obreras.

  10. Slow strain rate corrosion and fracture characteristics of X-52 and X-70 pipeline steels

    International Nuclear Information System (INIS)

    Contreras, A.; Albiter, A.; Salazar, M.; Perez, R.

    2005-01-01

    The susceptibility to stress corrosion cracking (SCC) in a NACE solution saturated with H 2 S, of the X-52 and X-70 steels was studied using slow strain rate tests (SSRT) and electrochemical evaluations. SCC tests were performed in samples which include the longitudinal weld bead of the pipeline steels and were carried out in the NACE solution at both room temperature and 50 deg. C. After failure, the fracture surfaces were observed in a scanning electron microscope (SEM) and the chemical analysis were obtained using X-rays energy dispersive (EDXs) techniques. The specimens tested in air, exhibited a ductile type of failure, and whereas, those tested in the corrosive solution showed a brittle fracture. Specimens tested in the NACE solution saturated with H 2 S presented high susceptibility to SCC. Corrosion was found to be an important factor in the initiation of some cracks. In addition, the effect of the temperature on the corrosion attack was explored. The susceptibility to SCC was manifested as a decrease in the mechanical properties. Potentiodynamic polarization curves and hydrogen permeation measurements were made. The diffusion of atomic hydrogen was related to this fracture forms. The hydrogen permeation flux increased with the increasing of temperature

  11. characterization and weldability of plasma nitrided P/M martensitic stainless steel X 20 Cr Ni 172

    International Nuclear Information System (INIS)

    Abdel-Karim, R.A.; El-demellawy, M.A; Waheed, A.F.

    2004-01-01

    stainless steels are widely used in nuclear applications, as a construction material. in these applications stainless steels suffer from corrosion degradation due severe environment and operating conditions. improving the engineering properties of such material prolong the service life time.in the present study, powder metallurgy technique namely plasma rotating electrode process (PREP) was used to produce martensitic steel DIN X 20 Cr Ni 172 with 0.5 % N. this step was followed by hot isostatic pressing process (HIP) . the effect of N on the weldability of this steel has been investigated . this included microstructure characterization, hardness evaluation and ferrite content measurements. the results showed that the presence of high nitrogen content in this steel resulted in a pore free structure with improved the hardness across the welding area. A single phase with few precipitates was detected on the grain boundaries in the heat affected zone. the results were supplemented by x-ray diffraction patterns and EDAX analysis

  12. M-X Environmental Technical Report. Environmental Characteristics of Alternative Designated Deployment Areas, Steel Industry.

    Science.gov (United States)

    1980-12-22

    180,000 Utah Pl’!nouth Nucor Steel (Proposed) 350,000 I 50 175,000 ,rem Unied State Steel Corp. 2,500,000 0 0 Arizona Tempe urathion Steel Co. 180,300 75...allocated to the M-X system construction without disrupting supply to its existing customers. h. Nucor Corporation. Nucor Corporation operates three...amount of this, at least 40 percent to possibly one half, could be in the form of rebar. Nucor will have an obvious freight advantage. i. Ameron, Inc

  13. Design of dual energy x-ray detector for conveyor belt with steel wire ropes

    Science.gov (United States)

    Dai, Yue; Miao, Changyun; Rong, Feng

    2009-07-01

    A dual energy X-ray detector for conveyor belt with steel wire ropes is researched in the paper. Conveyor belt with steel wire ropes is one of primary transfer equipments in modern production. The traditional test methods like electromagnetic induction principle could not display inner image of steel wire ropes directly. So X-ray detection technology has used to detect the conveyor belt. However the image was not so clear by the interference of the rubber belt. Therefore, the dualenergy X-ray detection technology with subtraction method is developed to numerically remove the rubber belt from radiograph, thus improving the definition of the ropes image. The purpose of this research is to design a dual energy Xray detector that could make the operator easier to found the faulty of the belt. This detection system is composed of Xray source, detector controlled by FPGA chip, PC for running image processing system and so on. With the result of the simulating, this design really improved the capability of the staff to test the conveyor belt.

  14. Formation of non-equilibrium structures in R6M5 steel under strong pulse beams action

    International Nuclear Information System (INIS)

    Rusin, Yu.G.; Plotnikov, S.V.

    2001-01-01

    Formation of non-equilibrium structures in R6M5 steel surface layer in the supply state under irradiation by strong pulse beams (SPB) is examined. Cylindric samples with diameter 10 mm and height 15 mm of R6M5 fast-cutting steel with following content (weight %): 0.85% C, 0.4% Mn, 0.5% Si, 4.0 Cr; 2.1% V; 5.3% Mo, 6.0% W; 0.4% Ni, Fe (the rest) were examined. Irradiation by SPB was conducted on the 'TEMP' modified accelerator operating in a technological regime with carbon beams parameters: energy from 0.3 up o 0.4 MeV, beam density in an impulse from 20 to 250 A/cm 2 , pulse duration from 60 tp 100 ns. The beam consists of 70 % carbon ions and 30 % hydrogen ions. Phase identification and its structural phase analysis have been studied on the DRON-3 X-ray diffractometer of common assignment. Topography of metallographic specimen surface has been examined on the REM-200 scanning electron microscope. Doping elements redistribution and phases quantitative characteristics after SPB action were studied with help of the X-ray spectral microanalysis (XRSA) on the MS-46 Camebax microanalyzer. Character of doping elements redistribution in the alloy (XRSA data) show its appreciably redistribution, moreover in the melted zone the increased content of molybdenum, tungsten, vanadium is observing, and in the zone of thermal action its increase relatively to matrix values

  15. Influence of Nitrided Layer on The Properties of Carbon Coatings Produced on X105CrMo17 Steel Under DC Glow-Discharge Conditions

    Directory of Open Access Journals (Sweden)

    Tomasz BOROWSKI

    2016-09-01

    Full Text Available In most cases, machine components, which come in contact with each other, are made of steel. Common steel types include 100Cr6 and X105CrMo17 are widely used in rolling bearings, which are subjected to high static loads. However, more and more sophisticated structural applications require increasingly better performance from steel. The most popular methods for improving the properties of steel is carburisation or nitriding. Unfortunately, when very high surface properties of steel are required, this treatment may be insufficient. Improvement of tribological properties can be achieved by increasing the hardness of the surface, reducing roughness or reducing the coefficient of friction. The formation of composite layers on steel, consisting of a hard nitride diffusion layer and an external carbon coating with a low coefficient of friction, seems to be a prospect with significant potential. The article describes composite layers produced on X105CrMo17 steel and defines their morphology, surface roughness and their functional properties such as: resistance to friction-induced wear, coefficient of friction and corrosion resistance. The layers have been formed at a temperature of 370°C in successive processes of: nitriding in low-temperature plasma followed by deposition of a carbon coating under DC glow-discharge conditions. An evaluation was also made of the impact of the nitrided layers on the properties and morphology of the carbon coatings formed by comparing them to coatings formed on non-nitrided X105CrMo17 steel substrates. A study of the surface topography, adhesion, resistance to friction-induced wear and corrosion shows the significant importance of the substrate type the carbon coatings are formed on.DOI: http://dx.doi.org/10.5755/j01.ms.22.3.7532

  16. Analyse and research of nonmetallic inclusions for steel 100Cr6

    Directory of Open Access Journals (Sweden)

    I. Vitez

    2009-01-01

    Full Text Available Steel 100Cr6 belongs to a group of hardened steels, which are applicable for production of rolling element parts. Because of specific working conditions, a proper chemical composition is required with a minimum content of nonmetallic inclusion. In this paper, the research results of presence the nonmetallic inclusions and their chemical composition are presented for the steel produced in vacuum and open induction electric furnace and their influence on the prescribed properties for this steel. The optical and scanning electronic microscope are used to identify presence and the chemical compositions of nonmetallic inclusions.

  17. Passivation behavior of Type 304 stainless steel in a non-aqueous alkyl carbonate solution containing LiPF6 salt

    International Nuclear Information System (INIS)

    Myung, Seung-Taek; Sasaki, Yusuke; Saito, Takamitsu; Sun, Yang-Kook; Yashiro, Hitoshi

    2009-01-01

    Passivation behavior of type 304 stainless steel in a non-aqueous alkyl carbonate solution containing LiPF 6 salt was studied using electrochemical polarization, X-ray photoelectron spectroscopy (XPS) and time of flight-secondary ion mass spectroscopy (ToF-SIMS). Cathodic polarization to 0 V vs. Li/Li + resulted in most but not complete reduction of the air-formed film from oxides to metal on the stainless steel, as confirmed by XPS. For complete elimination of the air-formed film, the surface of the stainless steel was scratched under anodic polarization conditions. At 3 V vs. Li/Li + where an anodic current peak appeared, only an indistinct layer was recognized on the newly scratched surface, according to ToF-SIMS analysis. Above 4 V vs. Li/Li + , substantial passive films were formed, which were composed of oxides and fluorides of iron and chromium. The origin of oxide was due to water contained in the non-aqueous alkyl carbonate solution, and that of fluorides were the result of the decomposition of electrolytic salt, LiPF 6 , especially at higher potential. The resultant passive films were stable in the non-aqueous alkyl carbonate solution containing LiPF 6 salt.

  18. Microstructural characterization of second phases in X10CrMoVNb9-1 and 12CrMoWCuVNb steels after long steam exposure time at 550 C

    International Nuclear Information System (INIS)

    Rodak, Kinga; Hernas, Adam; Vodarek, Vlastimil

    2015-01-01

    Microstructural changes in high alloy (9-12% Cr) creep resistant martensitic X10CrMoVNb9-1 and 12CrMoW . CuVNb steels after 100 000 h of steam exposure at 550 C have been studied using scanning transmission electron microscopy. Precipitates were identified using electron diffraction patterns and energy dispersive X-ray spectroscopy analysis. After long time exposure, a significant coarsening of M 23 C 6 carbides, and intensive precipitation of the coarse Laves phase were observed. Moreover, in the 12CrMoW . CuVNb steel, a low amount of the modified Z-phase particles was detected. The microstructures of the X10Cr . MoVNb9-1 and 12CrMoWCuVNb steels after 100 000 h of exposure differ in several aspects.

  19. Microstructural characterization of second phases in X10CrMoVNb9-1 and 12CrMoWCuVNb steels after long steam exposure time at 550 C

    Energy Technology Data Exchange (ETDEWEB)

    Rodak, Kinga; Hernas, Adam [Silesian Univ. of Technology, Inst. of Materials Science, Katowice (Poland); Vodarek, Vlastimil [VSB-Technical Univ. of Ostrava (Czech Republic)

    2015-07-15

    Microstructural changes in high alloy (9-12% Cr) creep resistant martensitic X10CrMoVNb9-1 and 12CrMoW . CuVNb steels after 100 000 h of steam exposure at 550 C have been studied using scanning transmission electron microscopy. Precipitates were identified using electron diffraction patterns and energy dispersive X-ray spectroscopy analysis. After long time exposure, a significant coarsening of M{sub 23}C{sub 6} carbides, and intensive precipitation of the coarse Laves phase were observed. Moreover, in the 12CrMoW . CuVNb steel, a low amount of the modified Z-phase particles was detected. The microstructures of the X10Cr . MoVNb9-1 and 12CrMoWCuVNb steels after 100 000 h of exposure differ in several aspects.

  20. Magnetic properties of the HoMn6-xFe xSn6 compounds

    International Nuclear Information System (INIS)

    Cakir, O.; Dincer, I.; Duman, E.; Krenke, T.; Elmali, A.; Elerman, Y.

    2007-01-01

    Intermetallic compounds of HoMn 6-x Fe x Sn 6 (0 ≤ x ≤ 1.2) were studied by means of field-cooled (FC) and zero-field-cooled (ZFC) magnetization measurements in the temperature range 5 K ≤ T ≤ 600 K. The unit cell parameters decrease with the increasing of Fe content. The compounds with x = 0 and 0.3 behave ferrimagnetically in the whole temperature range and spin reorientation transition is observed at 200 and 185 K, respectively. The x = 0.5 and 0.6 compounds show ferrimagnetic-helimagnetic-ferrimagnetic phase transitions with decreasing temperature while the compounds with x = 0.9 and 1.2 only show helimagnetic-ferrimagnetic phase transitions. Additionally, for the x = 0.6 compound the metamagnetic phase transition from helimagnetism to ferrimagnetism is induced by an applied field 20 kOe

  1. Lattice dynamics of cubic Cs2NaLnX6 and CsNaLn1-xLn'xX6 elpasolites

    International Nuclear Information System (INIS)

    Acevedo, R.; Poblete, V.; Alzamora, R.; Venegas, R.; Navarro, G.; Henriquez, C.

    1999-01-01

    Crystal lattice dynamics of stoichiometric Cs 2 NaLnX 6 and nonstoichiometric CsNaLn 1-x Ln' x X 6 , 0.01 ≤ x ≤ 0.10, Ln and Ln' are trivalent positive lanthanide ions and X is chlorine or bromine, were studied.. Phonon dispersion relations were computed for similar compound, Cs 2 UBr 6 , and vibronic absorption spectra with reduced number of required input parameters are considered on the basis of proposed model. (author)

  2. Bright x-ray stainless steel K-shell source development at the National Ignition Facility

    Energy Technology Data Exchange (ETDEWEB)

    May, M. J.; Fournier, K. B.; Colvin, J. D.; Barrios, M. A.; Dewald, E. L.; Moody, J.; Patterson, J. R.; Schneider, M.; Widmann, K. [Lawrence Livermore National Laboratory, P.O. Box 808 L170, Livermore, California 94551 (United States); Hohenberger, M.; Regan, S. P. [Laboratory for Laser Energetics, University of Rochester, Rochester, New York 14623 (United States)

    2015-06-15

    High x-ray conversion efficiency (XRCE) K-shell sources are being developed for high energy density experiments for use as backlighters and for the testing of materials exposed to high x-ray fluxes and fluences. Recently, sources with high XRCE in the K-shell x-ray energy range of iron and nickel were investigated at the National Ignition Facility (NIF). The x-ray conversion efficiency in the 5–9 keV spectral range was determined to be 6.8% ± 0.3%. These targets were 4.1 mm diameter, 4 mm tall hollow epoxy tubes having a 50 μm thick wall supporting a tube of 3 to 3.5 μm thick stainless steel. The NIF laser deposited ∼460 kJ of 3ω light into the target in a 140 TW, 3.3 ns square pulse. The absolute x-ray emission of the source was measured by two calibrated Dante x-ray spectrometers. Time resolved images filtered for the Fe K-shell were recorded to follow the heating of the target. Time integrated high-resolution spectra were recorded in the K-shell range.

  3. Influence of Al on the fatigue crack growth behavior of Fe–22Mn–(3Al)–0.6C TWIP steels

    International Nuclear Information System (INIS)

    Ma, Penghui; Qian, Lihe; Meng, Jiangying; Liu, Shuai; Zhang, Fucheng

    2015-01-01

    The influence of Al on fatigue crack growth (FCG) behavior of the high-Mn austenitic twinning-induced plasticity (TWIP) steel was investigated by conducting FCG tests on Fe–22Mn–0Al–0.6C and Fe–22Mn–3Al–0.6C TWIP steels (hereafter, referred to as 0Al and 3Al TWIP steel, respectively). The FCG tests were performed at stress ratio of 0.1 under the control of stress intensity factor range using three-point bending specimens. Excepting that the traditional two-dimensional (2D) observation methods (optical, scanning and transmission electron microscopes) were used to observe the crack paths, fracture surfaces and microstructure features, a high-resolution synchrotron X-ray computed tomography was also applied to observe the three-dimensional (3-D) crack morphology. The results indicate that the FCG resistance of the 0Al TWIP steel is superior to that of 3Al TWIP steel in the near threshold regime. Observed from the 2D crack paths and 3D crack morphologies, it can be found that the crack surface roughness and crack deflection of the 0Al steel are greater than those of 3Al steel. It is suggested that the degree of roughness-induced crack closure decreases with the addition of Al. And the 0Al steel shows much larger plastic zone sizes ahead of the crack tip than the 3Al steel, suggesting that plasticity-induced crack closure may also play an important role in decreasing the FCG rate in the 0Al steel. By excluding the crack closure effects, the 0Al steel still exhibits a higher effective crack growth threshold value than the 3Al steel; this is considered to be due to the higher planarity of slip in the 0Al steel than in the 3Al steel, and the mechanical twins generated in the 0Al steel reduce the stress concentration at crack tip

  4. 20 cool facts about the New Madrid Seismic Zone-Commemorating the bicentennial of the New Madrid earthquake sequence, December 1811-February 1812 [poster

    Science.gov (United States)

    Williams, R.A.; McCallister, N.S.; Dart, R.L.

    2011-01-01

    This poster summarizes a few of the more significant facts about the series of large earthquakes that struck the New Madrid seismic zone of southeastern Missouri, northeastern Arkansas, and adjacent parts of Tennessee and Kentucky from December 1811 to February 1812. Three earthquakes in this sequence had a magnitude (M) of 7.0 or greater. The first earthquake occurred on December 16, 1811, at 2:15 a.m.; the second on January 23, 1812, at 9 a.m.; and the third on February 7, 1812, at 3:45 a.m. These three earthquakes were among the largest to strike North America since European settlement. The mainshocks were followed by many hundreds of aftershocks that occurred over the next decade. Many of the aftershocks were major earthquakes themselves. The area that was strongly shaken by the three main shocks was 2-3 times as large as the strongly shaken area of the 1964 M9.2 Alaskan earthquake and 10 times as large as that of the 1906 M7.8 San Francisco earthquake. Geologic studies show that the 1811-1812 sequence was not an isolated event in the New Madrid region. The 1811-1812 New Madrid earthquake sequence was preceded by at least two other similar sequences in about A.D. 1450 and A.D. 900. Research also indicates that other large earthquakes have occurred in the region surrounding the main New Madrid seismicity trends in the past 5,000 years or so.

  5. Fatigue behaviour of X70 steel in crude oil

    Czech Academy of Sciences Publication Activity Database

    Gajdoš, Lubomír; Šperl, Martin; Bystrianský, J.

    2015-01-01

    Roč. 49, č. 2 (2015), s. 243-246 ISSN 1580-2949 R&D Projects: GA ČR(CZ) GAP105/10/2052; GA TA ČR(CZ) TE02000162 Institutional support: RVO:68378297 Keywords : corrosion fatigue * S-N curve * X70 steel * crude oil * separated water Subject RIV: JL - Materials Fatigue, Friction Mechanics Impact factor: 0.439, year: 2015 http://mit.imt.si/Revija/izvodi/mit152/gajdos.pdf

  6. Study of hot cracking potential in a 6-ton steel ingot casting

    Science.gov (United States)

    Yang, Jing'an; Liu, Baicheng; Shen, Houfa

    2018-04-01

    A new hot cracking potential (HCP) criterion, for the appearance of hot tearing in steel ingot castings, is proposed. The maximum value of the first principal stress, divided by the dynamic yield strength in the brittle temperature range (BTR), was used to identify the HCP. Experiments were carried out on a 6-ton P91 steel ingot in which severe hot tearing was detected in the upper centerline. Another ingot, with a better heat preservation riser, and without hot tearing, was used for comparison. Samples were obtained from the area of the ingot body with hot tearing, and their morphologies were inspected by a X-ray high energy industrial computed tomography. The carbon and sulfur distributions around the hot tearing were characterized by an infrared spectrometry carbon and sulfur analyzer. High temperature mechanical properties were obtained by a Gleeble thermal simulation machine, under different strain rates. Then, thermo-mechanical simulations using an elasto-viscoplastic finite-element model were conducted to analyze the stress and strain evolution during ingot solidification. The results showed that the hot tearing area, which was rich in both carbon and sulfur, was under excessive tensile stress in the BTR, bearing the highest HCP.

  7. Investigation of surface residual stress profile on martensitic stainless steel weldment with X-ray diffraction

    Directory of Open Access Journals (Sweden)

    I.I. Ahmed

    2018-04-01

    Full Text Available The development of residual stresses during fabrication is inevitable and often neglected with dire consequences during the service life of the fabricated components. In this work, the surface residual stress profile following the martensitic stainless steel (MSS pipe welding was investigated with X-ray diffraction technique. The results revealed the presence of residual stresses equilibrated across the weldment zones. Tensile residual stress observed in weld metal was balanced by compressive residual stresses in the parent material on the opposing sides of weld metal. Keywords: Residual stress, Weld, Stainless steel, X-ray, HAZ

  8. Research of x-ray nondestructive detector for high-speed running conveyor belt with steel wire ropes

    Science.gov (United States)

    Wang, Junfeng; Miao, Changyun; Wang, Wei; Lu, Xiaocui

    2008-03-01

    An X-ray nondestructive detector for high-speed running conveyor belt with steel wire ropes is researched in the paper. The principle of X-ray nondestructive testing (NDT) is analyzed, the general scheme of the X-ray nondestructive testing system is proposed, and the nondestructive detector for high-speed running conveyor belt with steel wire ropes is developed. The hardware of system is designed with Xilinx's VIRTEX-4 FPGA that embeds PowerPC and MAC IP core, and its network communication software based on TCP/IP protocol is programmed by loading LwIP to PowerPC. The nondestructive testing of high-speed conveyor belt with steel wire ropes and network transfer function are implemented. It is a strong real-time system with rapid scanning speed, high reliability and remotely nondestructive testing function. The nondestructive detector can be applied to the detection of product line in industry.

  9. X-ray diffraction study on the evaluation of the damage of steel structures subjected to earthquake

    International Nuclear Information System (INIS)

    Kaneta, Kiyoshi; Nishizawa, Hidekazu; Koshika, Norihide.

    1985-01-01

    The purpose of this study is to investigate the behavior of steel structures subjected to a strong earthquake and to evaluate the damage from a microscopic point of view. For this purpose, the authors have adopted two kinds of research techniques. The first is the ''ON-LINE EARTHQUAKE RESPONSE SIMULATION SYSTEM (ON-LINE SIMULATION SYSTEM)'', which is composed of an electro-hydrauric testing machine controled by a computer and a full scale specimen. Since a term of restoring force in the equation of motion is to be substituted by the actual reaction of a specimen under test, we can obtain the non-linear response of structure without any assumption about the hysteretic characteristics. Based on this method, the dynamic behavior of simple steel structures subjected to an intense earthquakes were simulated. The second technique is the ''X-RAY DIFFRACTION METHOD''. Although this method is usually regarded an experimental technique particular to the material science, we have realized the good applicability for the study of structural engineering. Because X-ray diffraction method is advantageous in investigating the microscopic behavior of steel member such as the plastic deformation and the low cycle fatigue. From the view point stated above, we have adopted this method for the evaluation of low cycle fatigue damage of steel member subjected to an earthquake. The experiment has been performed by radiating the X-ray at several stages of the ON-LINE SIMULATION. As has been expected, the X-ray diffraction patterns have changed in a regular manner depending on the degree of fatigue damage, and the results have shown a good possibility that the X-ray diffraction approach can offer a powerful tool for the detection of the earthquake damage of steel members. (author)

  10. Fatigue behavior of austenitic steels. Subproject. Mechanism oriented investigation of the fatigue behavior of austenitic steel X6CrNiNb1810 in the HCF and VHCF regime. Final report; Ermuedungsverhalten Austenit. Teilprojekt. Mechanismenorientierte Untersuchung des Ermuedungsverhaltens des austenitischen Stahles X6CrNiNb1810 im HCF- und VHCF-Bereich. Abschlussbericht

    Energy Technology Data Exchange (ETDEWEB)

    Sorich, A.; Smaga, M.; Eifler, D.

    2015-01-23

    In addition to load cycles in the Low Cycle Fatigue (LCF)-regime due to start up and shut down procedures of power plants, in some components additional high-frequency loadings in the High Cycle Fatigue (HCF)- and Very High Cycle Fatigue (VHCF)-regime occur. These loadings are induced e.g. by stresses due to thermal cyclic fluctuations and fluid dynamic processes. Therefore it is necessary to characterize experimentally the cyclic deformation behavior of metastable austenitic steels at operating temperature particularly in the HCF- and VHCF-regime and to develop a nondestructive method to detect fatigue processes. This joint research project was conducted in cooperation between the Institute of Materials Science and Engineering (WKK) of the University of Kaiserslautern and the Fraunhofer-Institute for Non-Destructive Testing (IZFP) in Saarbruecken. WKK was focused on experimental investigations to characterize the cyclic deformation behavior of the metastable austenitic steel in the HCF- and VHCF-range, taking into account cyclic hardening and softening processes and in particular to consider fatigue-induced changes in microstructure. The IZFP has focused on the development and application of a testing concept based on electromagnetic ultrasonic measurements. The isothermal cyclic deformation behavior of the metastable austenitic steel X6CrNiNb1810 (1.4550, AISI 347) at 300 C in the HCF-range is characterized by cyclic softening until specimen failure. At strain amplitudes of 0.10 % ≤ ε{sub a,t} ≤ 0.15 % and the stress amplitude σ{sub a} = 160 MPa cyclic softening is followed by cyclic hardening, which results in a significant increase in life time, up to the limiting number of cycles, which was defined at N{sub I} = 10{sup 7} in HCF-regime. The cyclic hardening is determined by a transformation induced phase formation from face-centered cubic (fcc) austenite to body-centered cubic (bcc) α{sup '}-martensite and/or in hexagonal (hcp) ε-martensite. In

  11. Evolution of surfaces properties for 100Cr6 steel by implantation and ionic mixing; Evolution des proprietes de surface de l`acier 100Cr6 par implantation et melange ioniques

    Energy Technology Data Exchange (ETDEWEB)

    Faussemagne, A

    1996-07-09

    Physico-chemical characterizations performed on samples of 100Cr6 steel implanted both with boron and nitrogen revealed the formation of boron nitride along with the following new phases: Fe{sub 1-x}(B, N), Fe{sub 2-x}(B, N) and Fe{sub 3-x}(B, N). A thorough analysis of boron NITRIDE (5BN) indicates that a low ion current density (3 {mu}A.cm{sup -2}) in the case of the boron plus nitrogen sequence favours the formation of sp{sup 2} bonds (hexagonal-BN) while a higher ion current density (6{mu}A.cm{sup -2}) promotes sp{sup 3} bonds (cubic-BN) in the opposite sequence. Tribological tests carried out on these samples revealed that nitrogen and boron implantations do not lead to any significant improvement of friction and wear at variance with the results obtained by others authors. However, on a set samples accidentally contaminated with carbon during implantation, we noticed a considerable improvement of these tribological parameters. As this pollution is commonly encountered in surface treatment by ion beams, one can invoke this phenomenon to explain the origin of the discrepancy reported by the literature. Extensive investigations allowed us to conclude that surface carbon, whatever its origin (contamination, ion implantation or ion beam mixed coating), provided that its amount is sufficiently high ({>=}2 x 10{sup 16} C.cm{sup -2}), decreases the coefficient of friction by a factor 5 and reduces drastically ({approx} 100) the wear. A careful examination of the whole results led us to propose a theoretical model, based on the role of the asperities of the two bodies in contact, to explain the evolution of the coefficient of friction and wear with the amount of surface carbon. This analysis revealed that in order to improve friction and wear of 100Cr6 steel, one needs to coat this material with a well adherent carbon layer having a thickness higher than the asperity heights of the two bodies in contact. Finally, this study allowed us to develop a simple lower

  12. Rheological, mechanical and tribological properties of carbon-nanofibre reinforced poly (ether ether ketone composites

    Directory of Open Access Journals (Sweden)

    Volker Altstaedt

    2003-12-01

    Full Text Available Poly(ether ether ketone nanocomposites containing vapour-grown carbon nanofibres (CNF were produced using standard polymer processing techniques. At high shear rates no significant increase in resin viscosity was observed. Nevertheless, the addition of the CNFs results in a higher melt strength at 360°C. Electron microscopy confirmed the homogeneous dispersion and alignment of nanofibres in the polymer matrix. Evaluation of the mechanical composite properties revealed a linear increase in tensile stiffness and strength with nanofibre loading fractions up to 15 wt% whilst matrix ductility was maintained up to 10 wt%. An interpretation of the composite performance by short-fibre theory resulted in rather low intrinsic stiffness properties of the vapour-grown CNF. Differential scanning calorimetry was used to investigate crystallization kinetics and degree of crystallinity. The CNFs were found not to act as nucleating sites. Furthermore, unidirectional sliding tests against two different counterpart materials (100Cr6 martensitic bearing steel, X5CrNi18-10 austenitic stainless steel were performed. The carbon nanofibres were found to reduce the wear rate of PEEK significantly.

  13. X-ray generation from Bremsstrahlung effect using stainless steel target

    International Nuclear Information System (INIS)

    Siti Aiasah Hashim; Shari Jahar; Leo Kee Wah; Muhammad Zahidee Taat

    2004-01-01

    X-ray radiation is produced when high energy electron interacts with metals. This process is known as Bremsstrahlung. In commercial electron beam irradiator, this process may be utilized to serve irradiation of thick products with lower dose requirement such disinfestation of fruits, delaying ripening and medical product sterilization. Initial experiment was carried out to measure the amount of x-ray radiation produced by using a simple converter. In this experiment, the target material is the stainless steel beam shutter that is normally used to protect the window. The maximum energy for the Eps 3000 is 3 MeV and was used generate the x-ray radiation. The dose was measure using CTA film and analyzed using UV spectrophotometer. The results obtained showed that sufficient amount of x-ray dose can be generated for low dose irradiation by using this simple set up. (Author)

  14. LAB3 Cosmic Ray Test Stand Analysis of Steel Stack Supports

    International Nuclear Information System (INIS)

    Cease, H.

    1998-01-01

    A cosmic ray test stand is being constructed at Lab 3. The stand consists of two stacks of steel plates one resting on top of the other. The top stack is composed of 6 plates of steel making an overall stack size of 34.5-inch x 40-inch x 99-inch. The bottom stack also has 6 layers of plate making an overall size of approximately 49.5-inch x 82-inch x 99-inch. The bottom stack is supported with three support legs. See drawing 3823.000ME-900428 for the individual plate orientation. The minimum support leg size and necessary welds between plates are determined.

  15. Zn(Ta1-xNbx2O6 nanomaterials: Synthesis, characterization and corrosion behaviour

    Directory of Open Access Journals (Sweden)

    Birdeanu Mihaela

    2016-01-01

    Full Text Available Zn(Ta1-xNbx2O6 pseudo-binary oxide nanocrystalline materials (where x = 1; 0.5; 0.1; 0.05 and 0 were obtained through the solid-state method and characterized by X-ray diffraction, Fourier Transform Infrared Spectroscopy and Ultraviolet-visible spectroscopy. In addition, their morphology and topography have been determined by field emission-scanning electron microscopy (SEM and atomic force microscopy (AFM. There is a significant dependence between the rugosity and the uniformity of crystals. The evenly crystals organized in multilayers have the lowest value of rugosity and the non uniform fractal type architectures have the highest value of rugosity. The compounds’ anti-corrosion features were evaluated after deposition on carbon steel (OL in 0.1 M Na2SO4 media by open circuit potential measurement and potentiodynamic polarization technique with Tafel representation. The inhibition efficiency of pseudo-binary oxides deposited on carbon steel electrode was in the range 42.3-52.7 % promising for their further multiple layer deposition with porphyrins in order to improve anticorrosion properties. Due to the high band gap (3.80 - 4.30 eV provided by increasing the tantalum content, four of these pseudo-binary oxides might find applications in photovoltaic cells.

  16. 26 x 6.6 radial-belted aircraft tire performance

    Science.gov (United States)

    Davis, Pamela A.; Martinson, Veloria J.; Yager, Thomas J.; Stubbs, Sandy M.

    1991-01-01

    Preliminary results from testing of 26 x 6.6 radial-belted and bias-ply aircraft tires at NASA Langley's Aircraft Landing Dynamics Facility (ALDF) are reviewed. The 26 x 6.6 tire size evaluation includes cornering performance tests throughout the aircraft ground operational speed range for both dry and wet runway surfaces. Static test results to define 26 x 6.6 tire vertical stiffness properties are also presented and discussed.

  17. Effects of sulphide ion on the corrosion behaviour of X52 steel in a carbon dioxide environment at temperature 40 deg. C

    International Nuclear Information System (INIS)

    Fatah, M.C.; Ismail, M.C.; Ari-Wahjoedi, B.; Kurnia, K.A.

    2011-01-01

    Research highlights: → We study the effect of sulphide ion on the corrosion behaviour of X52 steel. → Increasing sulphide ion concentration will increase the corrosion rate of X52 steel. → Increasing sulphide ion concentration will increase cathodic reaction. → Less protective film, also contribute to the increasing the corrosion rate. - Abstract: The electrochemical behaviour of X52 steel in the presence of sulphide at 40 deg. C in a CO 2 environment was investigated using the methods of linear polarization resistance (LPR), potentiodynamic sweep, electrochemical impedance spectroscopy (EIS). In addition, the surface of X52 steel was also studied using scanning electron microscopy (SEM). The results showed that the corrosion rate of X52 steel increased with increasing concentration of sulphide ion. Potentiodynamic curve showed that there were changes in cathodic branch due to the change in the nature of cathodic reaction in the presence of sulphide ion. EIS analysis showed the higher sulphide ion concentration, the higher adsorbed species on the steel surface that contributed in the cathodic reaction. Furthermore, SEM results showed crevices on the scale which indicated pitting tendency in sulphide ion solutions. The less protective film, probably mackinawite, also contributed to the increase of corrosion rate in the presence of sulphide ion.

  18. Electrochemical testing of passivity state and corrosion resistance of supermartensitic stainless steels

    Directory of Open Access Journals (Sweden)

    S. Lasek

    2010-01-01

    Full Text Available On low interstitial - supermartensitic stainless steels (X1CrNiMo 12-5-1, X2CrNiMo 13-6-2, X1CrNiMo 12-6-2 the electrochemical potentiodynamic polarization tests were carried out and the passive state stability and localized corrosion resistance were compared and evaluated. The effect of quenching and tempering as well as the changes in microstructure on polarisation curves and corrosion properties at room temperature were established. Small differences in chemical composition of steels were also registered on their corrosion parameters changes and resistance.

  19. Potential of Aerostats for the Recovery of Disabled Main Battle Tanks and Other Heavy Military Vehicles and Equipment

    Science.gov (United States)

    2007-08-01

    1 Material Notes: Austenitic Cr-Ni stainless steel . More corrosion resistant than Type 301 and because of higher Ni content does not work...or a refrigeration down to extremely low temperatures . To even reduce the pressure to below 2,000 bar, the tank would need to be refrigerated to...investigated for use in the ISO tank design: Stainless Steel Cold Rolled (AISI Type 302 Stainless Steel , cold rolled to 1550 Mpa tensile strength) Titanium

  20. Feasibility analysis of modified AL-6XN steel for structure component application in supercritical water-cooled reactor

    Institute of Scientific and Technical Information of China (English)

    Xinggang LI; Qingzhi YAN; Rong MA; Haoqiang WANG; Changchun GE

    2009-01-01

    Modified AL-6XN austenite steel was patterned after AL-6XN superaustenitic stainless steel by introducing microalloy elements such as zirconium and titanium in order to adapt to recrystallizing thermo-mechanical treatment and further improve crevice corrosion resistance. Modified AL-6XN exhibited comparable tensile strength, and superior plasticity and impact toughness to commercial AL-6XN steel. The effects of aging behavior on corrosion resistance and impact toughness were measured to evaluate the qualification of modified AL-6XN steel as an in-core component and cladding material in a supercritical water-cooled reactor. Attention should be paid to degradation in corrosion resistance and impact toughness after aging for 50 hours when modified AL-6XN steel is considered as one of the candidate materials for in-core components and cladding tubes in supercritical water-cooled reactors.

  1. Characterizing Grain-Oriented Silicon Steel Sheet Using Automated High-Resolution Laue X-ray Diffraction

    Science.gov (United States)

    Lynch, Peter; Barnett, Matthew; Stevenson, Andrew; Hutchinson, Bevis

    2017-11-01

    Controlling texture in grain-oriented (GO) silicon steel sheet is critical for optimization of its magnetization performance. A new automated laboratory system, based on X-ray Laue diffraction, is introduced as a rapid method for large scale grain orientation mapping and texture measurement in these materials. Wide area grain orientation maps are demonstrated for both macroetched and coated GO steel sheets. The large secondary grains contain uniform lattice rotations, the origins of which are discussed.

  2. Erosion Behaviour of API X100 Pipeline Steel at Various Impact Angles and Particle Speeds

    Directory of Open Access Journals (Sweden)

    Paul C. Okonkwo

    2016-09-01

    Full Text Available Erosion is the gradual removal of material due to solid particle impingement and results in a failure of pipeline materials. In this study, a series of erosion tests were carried out to investigate the influence of particle speed and impact angle on the erosion mechanism of API X100 pipeline steel. A dry erosion machine was used as the test equipment, while the particle speed ranged from 20 to 80 m/s and impact angles of 30° and 90° were used as test parameters. The eroded API X100 steel surface was characterized using scanning electron microscope (SEM and X-ray photoelectron spectroscopy (XPS. The weight loss and erosion rate were also investigated. The results showed that at a 90° impact angle, a ploughing mechanism was occurring on the tested specimens, while material removal through low-angle cutting was the dominant mechanism at lower impact angles. Embedment of alumina particles on the target steel surface, micro-cutting, and low-angle cutting were observed at low impact angles. Therefore, the scratches, cuttings, and severe ploughings observed on some failed oil and gas pipelines could be attributed to the erosion mechanism.

  3. Fracture Characteristics of Structural Steels and Weldments

    Science.gov (United States)

    1975-11-01

    CARACTERISTICS 0F.$ýTRUCTURAL TEL/ - "AD E NTSA .INAL 1 A7 sk S. CONTRACT OR GRANT NUMBER(&) Y.2G. im 9. PERFORMING ORGANIZATION NAME AND ADDRESS -017...36, T- 1,and HY-Y130 Steel and AX. Il 30 15 I Tensile F~racture Surface of A-36 Steel, 12x 31 16 Dimple Rupture in A-6Sel 0X 31 17 Plastic ...sites and the relative plasticity of thle The objective of this study was to use a scanning metal. If many fracture icleation sites initiate mticro

  4. Development of environmentally compatible tribosystems with PVD-technology

    International Nuclear Information System (INIS)

    Lugscheider, E.; Hornig, T.; Kienitz, S.; Klocke, F.; Krieg, T.

    2001-01-01

    PVD coatings offer a wide variety of applications. The focal point of this work is the development of an advanced type of PVD-hardcoating which allows machining with environmentally compatible lubricants. Representative examples for the investigations are the tribological systems 'turning of quenched and tempered steel 42CrMo4 V' and 'austenitic stainless steel X5CrNi18-10'. Ti-Hf-Cr-N and TiAlN/Al 2 O 3 were deposited by AIP- and H.I.S. TM - process respectively. These coating systems showed best results concerning oxidation wear and abrasive wear in former investigations. This was necessary because main cutting-edge life criterias are oxidation wear and abrasive wear at the minor cutting edge. Consequently, a high oxidation stability and a high hardness at high temperatures are required. (author)

  5. Susceptibility to stress corrosion in stainless steels type AISI 321 and 12X18H10T used in PWR type reactors (WWER)

    International Nuclear Information System (INIS)

    Matadamas C, N.

    1995-01-01

    Titanium stabilized stainless steels have been utilized in sovietic pressurized water reactors (VVER) for avoid the susceptibility to Intergranular Corrosion (IGC) present in other austenitic stainless steels. However the Intergranular Corrosion resistance of this kind of materials has been questioned because of Intergranular Stress Corrosion Cracking failures (IGSCC) have been reported. This paper study the electrochemical behavior of the AISI 321 stainless steel in a H 3 BO 3 Solution contaminated with chlorides and its susceptibility to Intergranular Corrosion.Electrochemical prediction diagrams of the stainless steels AISI 321 and 12X18H10T (sovietic) sensitized (600 Centigrade, 3 h.) were compared. Cylindrical and conical samples were used in Slow Strain Rate Tests (SSRT), to determine the susceptibility to Stress Corrosion Cracking (SCC) in AISI 321 and 12X18H10T stainless steels. The results obtained showed that the temperature of the solution is a very important factor to detect this susceptibility. Fractography studies on the fracture surfaces of the samples obtained in the SSRT at high temperature were realized. Corrosion velocities of both AISI 321 and 12X18H10T stainless steels were determined using conical samples in the CERT system at high temperature. E.D.A.X. analysis was employed in both AISI 321 and 12X18H10T stainless steels in order to explain the degree of sensitization. (Author)

  6. Low Temperature Irradiation Embrittlement of Reactor Pressure Vessel Steels

    Energy Technology Data Exchange (ETDEWEB)

    Wang, Jy-An John [Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States)

    2015-08-01

    The embrittlement trend curve development project for HFIR reactor pressure vessel (RPV) steels was carried out with three major tasks. Which are (1) data collection to match that used in HFIR steel embrittlement trend published in 1994 Journal Nuclear Material by Remec et. al, (2) new embrittlement data of A212B steel that are not included in earlier HFIR RPV trend curve, and (3) the adjustment of nil-ductility-transition temperature (NDTT) shift data with the consideration of the irradiation temperature effect. An updated HFIR RPV steel embrittlement trend curve was developed, as described below. NDTT( C) = 23.85 log(x) + 203.3 log (x) + 434.7, with 2- uncertainty of 34.6 C, where parameter x is referred to total dpa. The developed update HFIR RPV embrittlement trend curve has higher embrittlement rate compared to that of the trend curve developed in 1994.

  7. Oxidation and thermal shock behavior of thermal barrier coated 18/10CrNi alloy with coating modifications

    Energy Technology Data Exchange (ETDEWEB)

    Guergen, Selim [Vocational School of Transportation, Anadolu University, Eskisehir (Turkmenistan); Diltemiz, Seyid Fehmi [Turkish Air Force1st Air Supply and Maintenance Center Command, Eskisehir (Turkmenistan); Kushan, Melih Cemal [Dept. of Mechanical Engineering, Eskisehir Osmangazi University, Eskisehir (Turkmenistan)

    2017-01-15

    In this study, substrates of 18/10CrNi alloy plates were initially sprayed with a Ni-21Cr-10Al-1Y bond coat and then with an yttria stabilized zirconia top coat by plasma spraying. Subsequently, plasma-sprayed Thermal barrier coatings (TBCs) were treated with two different modification methods, namely, vacuum heat treatment and laser glazing. The effects of modifications on the oxidation and thermal shock behavior of the coatings were evaluated. The effect of coat thickness on the bond strength of the coats was also investigated. Results showed enhancement of the oxidation resistance and thermal shock resistance of TBCs following modifications. Although vacuum heat treatment and laser glazing exhibited comparable results as per oxidation resistance, the former generated the best improvement in the thermal shock resistance of the TBCs. Bond strength also decreased as coat thickness increased.

  8. Magnetic properties of a stainless steel irradiated with 6 MeV Xe ions

    Science.gov (United States)

    Xu, Chaoliang; Liu, Xiangbing; Qian, Wangjie; Li, Yuanfei

    2017-11-01

    Specimens of austenitic stainless steel were irradiated with 6 MeV Xe ions at room temperature to 2, 7, 15 and 25 dpa. The vibrating sample magnetometer (VSM), grazing incidence X-ray diffraction (GIXRD) and positron annihilation lifetime spectroscopy (PLS) were carried out to analysis the magnetic properties and microstructural variations. The magnetic hysteresis loops indicated that higher irradiation damage causes more significant magnetization phenomenon. The equivalent saturated magnetization Mes and coercive force Hc were obtained from magnetic hysteresis loops. It is indicated that the Mes increases with irradiation damage. While Hc increases first to 2 dpa and then decreases continuously with irradiation damage. The different contributions of irradiation defects and ferrite precipitates on Mes and Hc can explain these phenomena.

  9. Two-dimensional time-resolved X-ray diffraction study of directional solidification in steels

    International Nuclear Information System (INIS)

    Yonemura, Mitsuharu

    2009-01-01

    Full text: The high intensity heat source used for fusion welding creates steep thermal gradients of 100 degree C/s from 1800 degree Celsius. Further, the influence of a preferred orientation is serious for observation of a directional solidification that follows the dendrite growth along the direction toward the moving heat source. Therefore, we observed the rapid solidification of weld metal at a time resolution of 0.01∼0.1seconds by the Two-Dimensional Time-Resolved X-ray Diffraction (2DTRXRD) system for real welding. The diffraction ring was dynamically observed by 2DTRXRD during arc-passing over the irradiation area of X-ray with synchrotron energy of 18 KeV. The arc power output was 10 V - 150 A, and a scan speed of the arc was 1.0 mm/s. The temperature rise of instruments was suppressed by the water-cooled copper plate under the sample. Further, the temperature distribution of the weld metal was measured by the thermocouple and related to the diffraction patterns. Consequently, solidification and solid phase transformation of low carbon steels and stainless steels were observed during rapid cooling by 2DTRXRD. In the low-carbon steel, the microstructure is formed in the 2 step process; (i) formation of crystallites and (ii) increase of crystallinity. In the stainless steel, the irregular interface layer of σ/y in the quenched metal after solidification is expected that it is easy for dendrites to move at the lower temperature. In the carbide precipitation stainless steel, it is easy for NbC to grow on σ phase with a little under cooling. Further, a mist-like pattern, which differs from the halo-pattern, in the fusion zone gave some indication of the possibilities to observe the nucleation and the early solidification by 2DTRXRD. (author)

  10. Post-uniform elongation and tensile fracture mechanisms of Fe-18Mn-0.6C-xAl twinning-induced plasticity steels

    International Nuclear Information System (INIS)

    Yu, Ha-Young; Lee, Sang-Min; Nam, Jae-Hoon; Lee, Seung-Joon; Fabrègue, Damien; Park, Myeong-heom; Tsuji, Nobuhiro; Lee, Young-Kook

    2017-01-01

    The objective of the present study was to elucidate the complicated interrelationship between necking, post-uniform elongation (e_p_u), strain rate sensitivity (SRS), fracture mechanism and Al concentration in Fe-18Mn-0.6C-xAl twinning-induced plasticity steels. Many tensile tests were conducted for in- and ex-situ observations of necking, fracture surfaces, crack propagation and the density and size of micro-voids with the assistance of a high-speed camera and X-ray tomographic equipment. The addition of Al increased e_p_u, SRS and reduction ratios in dimension of the neck part of tensile specimens, and also changed fracture mode from quasi-cleavage to ductile fracture at the edge part. The quasi-cleavage surface of Al-free specimen was induced by edge and side cracks occurring along grain boundary junctions and twin boundaries within the edges and side surfaces where local deformation bands meet. The ductile-fracture surface of 1.5 %Al-added specimen was formed by the coalescence of micro-voids. While the side-to-middle crack propagation occurred in Al-free and 1 %Al-added specimens due to side cracks, the middle-to-side crack propagation was observed in 1.5 %Al-added specimen. The Al-free specimen had the larger size of the 20 largest voids compared to the 1.5 %Al-added specimen despite its lower void density and local strain due to the accelerated growth of voids near the tips of side cracks. Evaluating the negligible e_p_u of Al-free specimen by SRS is not deemed to be reasonable due to its inappreciable necking and side cracks. The improvement of e_p_u in 1.5 %Al-added specimen is primarily due to disappearance of edge and side cracks.

  11. Microstructure, state of internal stress and corrosion resistance of the short-time laser heat-treated nitrogen high-alloyed tool steel X30CrMoN151; Mikrostruktur, Eigenspannungszustand und Korrosionsbestaendigkeit des kurzzeitlaserwaermebehandelten hochstickstofflegierten Werkzeugstahls X30CrMoN151

    Energy Technology Data Exchange (ETDEWEB)

    Bohne, C. (ed.)

    2000-07-01

    This study compares the crystalline structure, state of internal stress and chemical properties of the high-alloyed nitrogen tool steel X30CrMoN15 1 and conventional cold work steel X39CrMo17 1. Transformation points A{sub c}1b and A{sub c}1e were calculated from residual austenite analysis and the c{sub m}/a{sub m} martensite ratios for various heating rates. This was used to generate a TTA (time-temperature-austenitisation) graph for X30CrMoN15 1 for the first time. Transmission electron microscopy and small-angle neutron scattering show that precipitates in nitrogen high-alloyed steel X30CrMoN15 1 can be eliminated completely by short-time laser heat treatment. The corrosion tests show that in contrast to X39CrMo17 1 X30CrMoN15 1 reacts more sensitively to parameter changes during short-time heat treatment in oxidising acid at pH 5-6. [German] Im Rahmen der Arbeit werden die Gefuegeausbildung, Eigenspannungen und chemische Eigenschaften des hochstickstofflegierten Werkzeugstahls X30CrMoN15 1 und des konventionellen Kaltarbeitsstahls X39CrMo17 1 verglichen. Aus den Restaustenitanalysen und den c{sub m}/a{sub m}-Verhaeltnissen des Martensits konnten die Umwandlungspunkte A{sub c1b} und A{sub c1e} fuer verschiedene Aufheizraten bestimmt und daraus ein bisher nicht bekanntes ZTA-Schaubild fuer den X30CrMoN15 1 erstellt werden. Transmissionselektronenmikroskopie und Neutronenkleinwinkelstreuung zeigen, dass sich die Ausscheidungen im hochstickstofflegierten Stahl X30CrMoN14 1 durch die Kurzzeitlaserwaermebehandlung vollstaendig aufloesen koennen. Die Korrosionsversuche zeigen, dass im Gegensatz zum X39CrMo17 1 der X30CrMoN15 1 in oxidierender Saeure bei pH 5-6 empfindlicher auf Parameteraenderungen bei der Kurzzeitwaermebehandlung reagiert. (orig.)

  12. Inhibitory effect of non-ionic surfactants of the TRITON-X series on the corrosion of carbon steel in sulphuric acid

    International Nuclear Information System (INIS)

    Fuchs-Godec, R.

    2007-01-01

    The corrosion inhibition characteristics of non-ionic surfactants of the TRITON-X series, known as TRITON-X-100 and TRITON-X-405, on stainless steel (SS) type X4Cr13 in sulphuric acid were investigated by potentiodynamic polarisation measurements. It was found that these surfactants act as good inhibitors of the corrosion of stainless steel in 2 mol L -1 H 2 SO 4 solution, but the inhibition efficiency strongly depends on the electrode potential. The polarisation data showed that the non-ionic surfactants used in this study acted as mixed-type inhibitors and adsorb on the stainless steel surface, in agreement with the Flory-Huggins adsorption isotherm. Calculated ΔG ads values are -57.79 kJ mol -1 for TRITON-X-100, and -87.5 kJ mol -1 for TRITON-X-405. From the molecular structure it can be supposed that these surfactants adsorb on the metal surface through two lone pairs of electrons on the oxygen atoms of the hydrophilic head group, suggesting a chemisorption mechanism

  13. Corrosion of carbon steel in the [P_1_4_6_6_6][Br] ionic liquid: The effects of γ-radiation and cover gas

    International Nuclear Information System (INIS)

    Morco, Ryan P.; Musa, Ahmed Y.; Momeni, Mojtaba; Wren, J.C.

    2016-01-01

    Highlights: • Carbon steel corrosion in non-aqueous ionic liquid ([P_1_4_6_6_6] [Br]) electrolyte. • Gamma-irradiation results to less corrosion, forming protective oxides. • Substantial corrosion is seen in the absence of gamma-radiation. • A corrosion mechanism is proposed for the observed results. - Abstract: The corrosion of carbon steel in the ionic liquid (IL) [P_1_4_6_6_6] [Br] was studied with the IL in contact with an inert (Ar) or oxidizing (air) cover gas in the presence and absence of γ-radiation. Significant corrosion was observed for the tests performed in the absence of γ-radiation while a protective oxide layer is formed in the presence of γ-radiation. The corrosion is attributed to the presence of impurity H_2O and O_2 dissolved in the IL, and a corrosion mechanism is proposed.

  14. Comparative study on the stress corrosion cracking of X70 pipeline steel in simulated shallow and deep sea environments

    Energy Technology Data Exchange (ETDEWEB)

    Sun, Feilong [Corrosion and Protection Center, University of Science and Technology Beijing, Beijing 100083 (China); Key Laboratory of Corrosion and Protection of Ministry of Education, Beijing 100083 (China); China Building Material Test & Certification Group Co. Ltd., Beijing 100024 (China); Ren, Shuai [Corrosion and Protection Center, University of Science and Technology Beijing, Beijing 100083 (China); Key Laboratory of Corrosion and Protection of Ministry of Education, Beijing 100083 (China); Li, Zhong [Department of Chemical and Materials Engineering, University of Alberta, Edmonton, AB, Canada T6G 2G6 (Canada); Liu, Zhiyong, E-mail: liuzhiyong7804@ustb.edu.cn [Corrosion and Protection Center, University of Science and Technology Beijing, Beijing 100083 (China); Key Laboratory of Corrosion and Protection of Ministry of Education, Beijing 100083 (China); Li, Xiaogang; Du, Cuiwei [Corrosion and Protection Center, University of Science and Technology Beijing, Beijing 100083 (China); Key Laboratory of Corrosion and Protection of Ministry of Education, Beijing 100083 (China)

    2017-02-08

    The stress corrosion cracking (SCC) behavior of X70 steel in simulated shallow and deep sea environments was studied using potentiodynamic polarization measurement, a slow strain rate tensile (SSRT) test and scanning electron microscopy (SEM). The results indicate that the predominant cathodic reaction changes from an oxygen reduction reaction to the hydrogen evolution reaction as the dissolved oxygen (DO) content decreases. In the simulated deep sea environment, the SCC susceptibility of X70 steel decreased first, reached its lowest point at 15 MPa and then increased as the simulated sea hydrostatic pressure (HP) further increased. This is consistent with the regularity for the change of the cathodic hydrogen evolution reaction current density i{sub H} at E{sub corr}, which indicates that the HP may influence the SCC susceptibility of X70 steel by changing the permeated hydrogen concentration.

  15. Mechanical Properties and Microstructure of Dissimilar Material Welded Joints

    Directory of Open Access Journals (Sweden)

    Ziewiec A.

    2014-10-01

    Full Text Available The paper presents results of the mechanical testing and the microstructure analysis of dissimilar welded joint of the R350HT steel and the high-manganese (Hadfield cast steel using Cr-Ni cast steel spacer. The simulation tests of the welded joint surface deformation were carried out. The macroscopic and microscopic investigation were made using light microscopy (LM and scanning electron microscopy (SEM. Content of the magnetic phase was measured using magnetoscope. The quantitative metallographic investigation was used for assessment of ferrite and martensite contents and X-ray diffraction phase analysis was carried out. The results showed that during cooling of the spacer after welding, the transformation of metastable austenite into martensite proceeded. In addition to work hardening, the phase transformation of austenite into martensite occurs during the process of the superficial deformation of the spacer while simulated exploitation. This leads to a substantial increase of hardness, and at the same time, causes the increase of wear resistance of the welded joints of crossovers.

  16. Efficient laser-induced 6-8 keV x-ray production from iron oxide aerogel and foil-lined cavity targets

    Energy Technology Data Exchange (ETDEWEB)

    Pérez, F.; Kay, J. J.; Patterson, J. R.; Kane, J.; Villette, B.; Girard, F.; Reverdin, C.; May, M.; Emig, J.; Sorce, C.; Colvin, J.; Gammon, S.; Jaquez, J.; Satcher, J. H.; Fournier, K. B.

    2012-08-01

    The performance of new iron-based laser-driven x-ray sources has been tested at the OMEGA laser facility for production of x rays in the 6.5–8.5 keV range. Two types of targets were experimentally investigated: low-density iron oxide aerogels (density 6-16 mg/cm36-16 mg/cm3) and stainless steel foil-lined cavity targets (steel thickness 1-5 μm1-5 μm). The targets were irradiated by 40 beams of the OMEGA laser (500 J/beam, 1 ns pulse, wavelength 351 nm). All targets showed good coupling with the laser, with <5%<5% of the incident laser light backscattered by the resulting plasma in all cases (typically <2.5%<2.5%). The aerogel targets produced Te=2Te=2 to 3 keV, ne=0.12-0.2ne=0.12-0.2 critical density plasmas yielding a 40%–60% laser-to-x-ray total conversion efficiency (CE) (1.2%–3% in the Fe K-shell range). The foil cavity targets produced Te~2 keV, Te~2 keV, ne~0.15ne~0.15 critical density plasmas yielding a 60%–75% conversion efficiency (1.6%–2.2% in the Fe K-shell range). Time-resolved images illustrate that the volumetric heating of low-density aerogels allow them to emit a higher K-shell x-ray yield even though they contain fewer Fe atoms. However, their challenging fabrication process leads to a larger shot-to-shot variation than cavity targets.

  17. Corrosion Behavior of X80 Steel with Coupled Coating Defects under Alternating Current Interference in Alkaline Environment.

    Science.gov (United States)

    Li, Zhong; Li, Caiyu; Qian, Hongchang; Li, Jun; Huang, Liang; Du, Cuiwei

    2017-06-28

    The corrosion behavior of X80 steel in the presence of coupled coating defects was simulated and studied under the interference of alternating current (AC) in an alkaline environment. The results from electrochemical measurements showed that the electrode potential of the coating defect with the smaller exposed area was lower than that with the larger area, which indicated that the steel with the smaller coating defect was more prone to corrosion. The result of weight loss tests also showed that the smaller coating defect had induced a higher corrosion rate. However, the corrosion rate of X80 steel at the larger coating defect decreased gradually with the increase of the larger defect area at a constant smaller defect area. The corrosion morphology images showed that the coating defects with smaller areas suffered from more severe pitting corrosion.

  18. Characterization of Mechanical Properties and Residual Stress in API 5L X80 Steel Welded Joints

    Science.gov (United States)

    de Sousa Lins, Amilton; de Souza, Luís Felipe Guimarães; Fonseca, Maria Cindra

    2018-01-01

    The use of high-strength and low-alloy steels, high design factors and increasingly stringent safety requirements have increased the operating pressure levels and, consequently, the need for further studies to avoid and prevent premature pipe failure. To evaluate the possibility of improving productivity in manual arc welding of this type of steel, this work characterizes the mechanical properties and residual stresses in API 5L X80 steel welded joints using the SMAW and FCAW processes. The residual stresses were analyzed using x-ray diffraction with the sin2 ψ method at the top and root of the welded joints in the longitudinal and transverse directions of the weld bead. The mechanical properties of the welded joints by both processes were characterized in terms of tensile strength, impact toughness and Vickers microhardness in the welded and shot peening conditions. A predominantly compressive residual stress was found, and shot peening increased the tensile strength and impact toughness in both welded joints.

  19. Microstructure and Hardness of Cold Work Vanadis 6 Steel after Subzero Treatment at −140°C

    Directory of Open Access Journals (Sweden)

    Juraj Ďurica

    2018-01-01

    Full Text Available The microstructure, phase constitution, and hardness of Cr-V ledeburitic tool steel Vanadis 6 subjected to subzero treatment at −140°C and for different soaking times have been investigated. The light microscopy, scanning electron microscopy, and X-ray diffraction have been used for microstructural investigations. The hardness has been evaluated by the Vickers method. The obtained results assist to draw that subzero treatment reduces the retained austenite amount and increases the population density of carbides, compared to conventional heat treatment. The extent of decrease in the retained austenite amount makes around 85%, and the increase in population density of small globular carbides was approximately fivefold. High compressive stresses were identified in the retained austenite, and their values follow the increase in carbide count. This makes a serious support to the theory explaining the formation of “extra” carbides as a by-product of more complete martensitic transformation. As a result of the mentioned microstructural changes, the material hardness increased from 875 ± 16 HV 10 up to 954.6 ± 14 HV 10 for conventionally quenched and SZT steels, respectively.

  20. Precipitation sequences in austenitic Fe-22Cr-21Ni-6Mo-(N) stainless steels

    International Nuclear Information System (INIS)

    Kim, S.-J.; Lee, T.-H.

    1999-01-01

    Precipitation sequence of nitrogen containing Fe-22Cr-21Ni-6Mo-N austenitic stainless steel has been investigated after aging at high temperatures, and compared with nitrogen free steel. The σ phases and M 23 C 6 carbides were observed along the grain boundaries as well as in the matrix in both of the solution treated specimens. The M 6 C carbides and chi phase appeared successively in between 3 hours and 24 hours depending on the nitrogen content. Main difference in aging behavior was the precipitation of fine nitrides. Aging for 24 hours and 168 hours of nitrogen containing steel resulted in the formation of fine Cr 2 N and faceted AlN nitrides. The crystallography, structure and morphology were analyzed with analytical electron microscopy. (orig.)

  1. Rating of the X-ray method of measurement of stresses in steels

    International Nuclear Information System (INIS)

    Skrzypinski, A.

    1977-01-01

    The possibilities of utilization of some dependencies occuring in the X-ray technique of measurement of natural stresses for determination of distances of a between - plane lattice without natural stresses (d 0 ) are discussed. The proposed methodics of determination of d 0 is illustrated with the investigations which were carried-out on bearing steel LH15. (author)

  2. Failures by stress corrosion of electrical heating accessories, instrument leads and thermoelements of chromium nickel steel

    International Nuclear Information System (INIS)

    Schwarz, M.

    1982-01-01

    Measurement and control devices are being increasingly used for process control, monitoring and the safety of chemical plants. Pressure, temperature, through-put, moisture, composition and the like are continuously measured at many positions of the system. The supervision of the measuring equipment and hence the necessary exchanging ability of the devices during operation means good access to the plant. An extensive system of pipelines between the measuring equipment and the product lines to be supervised is the result. Common austenite 18 10 CrNi steel pipes of 12 mm diameter and 1 mm wall thickness are used for assembling and corrosion reasons in these pulse instrument leads. The failure of several instrument leads in a large scale plant at the beginning of the frost period interfers with the control. It was therefore necessary to find the exact cause; this is described in the present work. (orig.) [de

  3. Study of Laser Welding of HCT600X Dual Phase Steels

    Directory of Open Access Journals (Sweden)

    Švec Pavol

    2014-12-01

    Full Text Available The effects of beam power and welding speed on microstructure, microhardnes and tensile strength of HCT600X laser welded steel sheets were evaluated. The welding parameters influenced both the width and the microstructure of the fusion zone and heat affected zone. The welding process has no effect on tensile strength of joints which achieved the strength of base metal and all joints fractured in the base metal.

  4. Diffusion brazing of Ti–6Al–4V and austenitic stainless steel using silver-based interlayer

    International Nuclear Information System (INIS)

    Soltani Tashi, R.; Akbari Mousavi, S.A.A.; Mazar Atabaki, M.

    2014-01-01

    Highlights: • Ti–6Al–4V and stainless steel 316L were successfully joined by diffusion brazing. • The wettability of the filler alloy was escalated by increasing the temperature. • By increasing the brazing temperature various intermetallic compounds were formed. • There is a noteworthy effect of the brazing temperature on the fracture footpath. - Abstract: In the present study, vacuum brazing was applied to join Ti–6Al–4V and stainless steel using AgCuZn filler metal. The bonds were characterized by scanning electron microscopy, energy dispersive spectroscopy and X-ray diffraction analysis. Mechanical strengths of the joints were evaluated by the shear test and microhardness showed that shear strength decreased with increasing the brazing temperature and time. The results showed that the wettability of the filler alloy was increased by enhancing the wetting test temperature. It was shown that by increasing the brazing temperature various intermetallic compounds were formed in the bond area. These intermetallic compounds were mainly a combination of CuTi and Fe–Cu–Ti. The shear test results verified the influence of the bonding temperature on the strength of the joints based on the formation of different intermetallics in the bond zone. The fracture analysis also revealed different fracture footpath and morphology for the different brazing temperatures

  5. Characterization by X ray diffraction of deleterious phases precipitated in a super duplex stainless steel

    International Nuclear Information System (INIS)

    Pardal, Juan M.; Tavares, Sergio S. Maior; Fonseca, Maria P. Cindra; Montenegro, Talles Ribeiro; Dias, Antonio Jose N.; Almeida, Sergio L. de

    2010-01-01

    In this work the identification and quantification of deleterious phases in two super duplex stainless steels grade UNS S32750, with quite different grain sizes, was performed by X-ray diffraction. The materials were isothermally aged in the 800 . 950 deg C range. Direct comparison method was used to quantify the ferrite phase in each sample. The amount of deleterious phases (σ, χ and γ2) formed was calculated by the difference of the amount of ferrite phase measured in each specimen to the amount of ferrite initially measured in the un-aged steel. The results obtained give an useful contribution to the understanding of kinetics of deleterious phases precipitation in super duplex steels. (author)

  6. Electrochemical corrosion behaviors of the X90 linepipe steel in NS4 solution

    Directory of Open Access Journals (Sweden)

    Jinheng Luo

    2016-10-01

    Full Text Available Oil and gas line pipes are laid underground and run through different areas in the laying process, so they will be subjected to different degrees of corrosion and even crack, leading to enormous casualties and economic losses. In order to guarantee the safe operation of line pipes, therefore, it is significant to investigate the electrochemical corrosion behaviors of pipe steel in a simulated soil environment. In this paper, the electrochemical corrosion behaviors of the base metals and welding materials of API 5L X90 steel longitudinally submerged arc welding pipes in near-neutral simulated soil solution (NS4 were studied by means of the electrochemical impedance spectroscopy (EIS and the potentiodynamic polarization testing technology. It is shown that the typical characteristic of anodic dissolution is presented but with no passivation phenomenon when X90 linepipe steel is put in NS4 solution. The base material is thermodynamically more stable than the seam weld material. The base material and seam weld samples were polarized under −850 mV polarization potential for different durations. It is demonstrated that with the proceeding of polarization, the polarization resistance and the corrosion resistance increase while the corrosion current density decreases. And the corrosion resistance of base material is better than that of seam weld material.

  7. Grazing incidence synchrotron X-ray diffraction and Moessbauer spectroscopy analyses of plasma nitrided ASTM F138 stainless steel

    Energy Technology Data Exchange (ETDEWEB)

    Souza, Danilo Olzon Dionysio de; Ardisson, Jose Domingos, E-mail: dolzon@gmail.com [Centro de Desenvolvimento da Tecnologia Nuclear (CDTN/CNEN-MG), Belo Horizonte, MG (Brazil); Silva, Edilaine Honorio [Studiecentrum voor Kernenergie (Belgium); Olzon-Dionysio, Maristela; Souza, Sylvio Dionysio de; Fabris, Jose Domingos [Universidade Federal dos Vales do Jequitinhonha e Mucuri (UFVJM), Diamantina, MG (Brazil); Martinez, L.G. [Instituto de Pesquisas Energeticas e Nucleares (IPEN/CNEN-SP), Sao Paulo, SP (Brazil)

    2016-07-01

    Full text: systematic investigation of samples of plasma-nitriding austenitic stainless steels ASTM F138 and AISI 316L is reported. The surface treatment of the steels through plasma-nitriding was used to improve further the hardness, wear and corrosion resistance of these stainless steels. The resulting layered crystallographic structure actually corresponds to several phases with close cell parameters, making their identification and quantification a real experimental challenge. The ASTM F138 and AISI 316L stainless steel disks were plasma nitrided for 4 h at 400 deg C in a 80% H{sub 2} -20% N2 atmosphere at 6 torr, using plasma current frequencies between 6 and 100 kHz. Data of Moessbauer (CEMS and CXMS) and grazing incidence synchrotron X-ray diffraction (XRD-SR) were systematically collected. The nitrided layer thickness were not in general influenced by the plasma frequency, except at 12 kHz, which produced a layer thickness of approximately 8.0 mm, being in average 40% thicker than for the other samples. CXMS and CEMS Moessbauer spectra for this 12 kHz-sample show a much more pronounced magnetic resonance lines than for the other samples. The Fe{sub 4}N phase presents a single magnetic hyperfine interaction; the other two (Fe{sub 2-3}N and the expanded austenite) present both paramagnetic and magnetic components, even though their hyperfine parameters may not be safely separated. We also present the results of XRD-SR that were probed at several depths. The data from these techniques may be consistently correlated and this leads to an improved model to explain the structure of the nitrided layers. (author)

  8. Hydrogen degradation of 21-6-9 and medium carbon steel by disc pressure test

    International Nuclear Information System (INIS)

    Zhou, D.H.; Zhou, W.X.; Xu, Z.L.

    1986-01-01

    This paper reports the method of disc pressure test and the results for 21-6-9 stainless steel and medium carbon steel in hydrogen gas with different pressures and time of storage. The results show the hydrogen induced degradation of these two kinds of steel. An attempt was made to establish an index which uses variation of area of deformed disc to determine the degradation of ductility in a hydrogen environment. (orig.)

  9. Microstructure of steel X 20 Cr 13 in the electron microscopical picture

    International Nuclear Information System (INIS)

    Gesatzke, W.

    1982-01-01

    The tempered microstructure of the steel X 20 Cr 13 is described by an electron microscopical overall picture and additional information is gained which would not be possible with the optical microscope. The large transmission area permits one to quantitatively evaluate a microstructure component which due to its small size can only be measured with electron microscope pictures. (orig.) [de

  10. Nanostructure of protective rust layer on weathering steel examined using synchrotron radiation x-rays

    International Nuclear Information System (INIS)

    Yamashita, Masato; Uchida, Hitoshi; Konishi, Hiroyuki; Mizuki, Jun'ichiro

    2004-01-01

    The X-ray absorption fine structure (XAFS) spectrum of pure goethite around the Fe K absorption edge and that of the protective rust layer formed on weathering steel exposed for 17 years in an atmospheric environment around the Cr K edge, have been examined using synchrotron radiation X-rays. It was found that the rust layer on the weathering steel mainly consisted of Cr-goethite. By examining the fine structure at the Cr K edge and the Fe K edge, we concluded that Cr 3+ in the rust layer is coordinated with O 2- and is positioned in the double chains of vacant sites in the network of FeO 3 (OH) 3 octahedra in the goethite crystal. This Cr 3+ site indicates that the protective effect of the rust layer is due to the dense aggregation of fine crystals of Cr-goethite with cation selectivity. (author)

  11. Microstructure and wear behavior of stellite 6 cladding on 17-4 PH stainless steel

    Energy Technology Data Exchange (ETDEWEB)

    Gholipour, A. [Department of Materials Engineering, Isfahan University of Technology, Isfahan 84156-83111 (Iran, Islamic Republic of); Shamanian, M., E-mail: shamanian@cc.iut.ac.ir [Department of Materials Engineering, Isfahan University of Technology, Isfahan 84156-83111 (Iran, Islamic Republic of); Ashrafizadeh, F. [Department of Materials Engineering, Isfahan University of Technology, Isfahan 84156-83111 (Iran, Islamic Republic of)

    2011-04-07

    Research highlights: > The microstructure of the surface layer consisted of carbides embedded in a Co-rich solid solution with dendritic structure. Primary phases formed during the process were identified as Co(FCC) and lamellar eutectic phases (M{sub 23}C{sub 6}, M{sub 6}C, Cr{sub 7}C{sub 3}). > Microhardness profiles showed that hardness increases from interface to the coating surface. This is due to the finer size of the grains at coating surface in comparison to that at interface and also diffusion of Fe adjacent to the interface. > The delamination was suggested as the dominant mechanism of the wear. In this regard, plate-like wear debris consisted of voids and cracks. In addition, due to increase in surface temperature, Cr{sub 2}O{sub 3} oxide phase was formed during wear tests. - Abstract: This paper deals with the investigation of the microstructure and wear behavior of the stellite 6 cladding on precipitation hardening martensitic stainless steel (17-4PH) using gas tungsten arc welding (GTAW) method. 17-4 PH stainless steel is widely used in oil and gas industries. Optical metallography, scanning electron microscopy (SEM) and energy dispersive spectroscopy (EDS) were employed to study the microstructure and wear mechanisms. X-ray diffraction analysis was also used to identify phases formed in the coating. The results showed that the microstructure of the surface layer consisted of carbides embedded in a Co-rich solid solution with a dendritic structure. In addition, the dendritic growth in the coating was epitaxial. Primary phases formed during the process were Co (fcc), Co (hcp), lamellar eutectic phases, M{sub 23}C{sub 6} and Cr{sub 7}C{sub 3} type carbides. The results of the wear tests indicated that the delamination was the dominant mechanism. So, it is necessary to apply an inter-layer between the substrate and top coat.

  12. Dissimilar friction welding of 6061-T6 aluminum and AISI 1018 steel: Properties and microstructural characterization

    International Nuclear Information System (INIS)

    Taban, Emel; Gould, Jerry E.; Lippold, John C.

    2010-01-01

    Joining of dissimilar materials is of increasing interest for a wide range of industrial applications. The automotive industry, in particular, views dissimilar materials joining as a gateway for the implementation of lightweight materials. Specifically, the introduction of aluminum alloy parts into a steel car body requires the development of reliable, efficient and economic joining processes. Since aluminum and steel demonstrate different physical, mechanical and metallurgical properties, identification of proper welding processes and practices can be problematic. In this work, inertia friction welding has been used to create joints between a 6061-T6 aluminum alloy and a AISI 1018 steel using various parameters. The joints were evaluated by mechanical testing and metallurgical analysis. Microstructural analyses were done using metallography, microhardness testing, scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS), X-ray elemental mapping, focused ion beam (FIB) with ultra high resolution SEM and transmission electron microscopy (TEM) in TEM and STEM modes. Results of these analysis first suggested that joint strengths on the order of 250 MPa could be achieved. In addition, failures were seen in the plasticized layer on the aluminum side of the joint. Further, bond lines were characterized by a thin layer of formed Al-Fe intermetallic. This intermetallic layer averaged roughly 250 nm thick and compositionally appears related to the FeAl and Fe 2 Al 5 phases.

  13. Interaction between molten corium UO2+x-ZrO2-FeOy and VVER vessel steel

    International Nuclear Information System (INIS)

    Bechta, S. V.; Granovsky, V. S.; Khabensky, V. B.; Krushinov, E. V.; Vitol, S. A.; Sulatsky, A. A.; Gusarov, V. V.; Almiashev, V. I.; Lopukh, D. B.; Bottomley, D.; Fischer, M.; Piluso, P.; Miassoedov, A.; Tromm, W.; Altstadt, E.; Fichot, F.; Kymalainen, O.

    2010-01-01

    In case of in-vessel corium retention during a severe accident in a light water reactor, weakening of the vessel wall and deterioration of the vessel steel properties can be caused both by the melting of the steel and by its physicochemical interaction with corium. The interaction behavior has been studied in medium-scale experiments with prototypic corium. The experiments yielded data for the steel corrosion rate during interaction with UO 2+x -ZrO 2 -FeO y melt in air and steam at different steel surface temperatures and heat fluxes from the corium to the steel. It has been observed that the corrosion rates in air and steam atmosphere are almost the same. Further, if the temperature at the interface increases beyond a certain level, corrosion intensifies. This is explained by the formation of liquid phases in the interaction Zone. The available experimental data have been used to develop a correlation for the corrosion rate as a function of temperature and heat flux. (authors)

  14. Microstructure and Mechanical Properties of ASTM A743 CA6NM Steel Welded by FCAW Process

    OpenAIRE

    Silva, Rafael de Paula; Faria, Maria Ismenia Sodero Toledo; Almeida, Luiz Fernando Cursino Briet de; Nunes, Carlos Angelo; Vieira, Décio; Borges Júnior, Wanderlei

    2017-01-01

    CA6NM steel is widely used in the manufacture of hydraulic turbines metallic parts, due to its resistance to corrosion and cavitation damage, combined with good weldability and fatigue properties. However, welding of this type of steel is complex and to ensure a minimum residual stress after welding it is necessary perform a post welding heat treatment (PWHT) of the part. This study aims to analyze the effect of a PWHT on the microstructure and mechanical properties of CA6NM steel weld joint ...

  15. Corrosion study of API 5L x-series pipeline steels in 3.5% NaCl solution under varying conditions

    International Nuclear Information System (INIS)

    Shahid, M.; Qureshi, M.I.; Farooq, M.U.; Khan, M.I.

    2003-01-01

    Pipelines provide convenient and efficient means for mass transportation of variety of fluids, such as oil and gas, over varying distances. In the last two decades or so, pipeline designers focused mainly on the usage of larger sizes and higher operating pressures for achieving higher transportation efficiency. This has been accomplished through the provision of steels with progressive increase in yield strength coupled with good weldability and sufficient toughness to restrict crack propagation. In addition to higher strength and toughness, developing pipeline technologies have required improved resistance to corrosion, which has been tried with specific alloy additions and special control over non-metallic inclusions. Corrosion investigations were carried out on various grades of pipeline steels (API 5L X-46, X-52, X-56, X-60 and X- 70) under varying environmental conditions. This paper describes the results pertaining to corrosion behavior of the steels in 3.5% NaCl solutions in stagnant, turbulent and deaerated conditions. It was found that all grades corrode in this solution and their corrosion potentials and corrosion currents are in close vicinity of each other. Turbulent solutions, however, have shown an increase in corrosion rates whereas deaeration has revealed a relative decrease in aggressivity of the electrolyte. (author)

  16. Effect of welding thermal cycles on the structure and properties of simulated heat-affected zone areas in X10CrMoVNb9-1 (T91) steel at a state after 100,000 h of operation

    Energy Technology Data Exchange (ETDEWEB)

    Łomozik, Mirosław, E-mail: miroslaw.lomozik@is.gliwice.pl [Instytut Spawalnictwa, Testing of Materials Weldability and Welded Constructions Department, 44-100 Gliwice, Bł. Czesława 16-18 (Poland); Hernas, Adam, E-mail: adam.hernas@polsl.pl [Silesian University of Technology, Faculty of Materials Engineering and Metallurgy, 40-019 Katowice, Krasińskiego 8 str. (Poland); Zeman, Marian L., E-mail: marian.zeman@is.gliwice.pl [Instytut Spawalnictwa, Testing of Materials Weldability and Welded Constructions Department, 44-100 Gliwice, Bł. Czesława 16-18 (Poland)

    2015-06-18

    The article presents results of structural tests (light, scanning electron and scanning transmission electron microscopy) of X10CrMoVNb9-1 (T91) creep-resisting steel after approximately 100,000 h of operation. It was ascertained that the parent metal of T91 steel is characterized by the microstructure of tempered martensite with M{sub 23}C{sub 6} carbide precipitates and few dispersive precipitates of MX-type niobium and vanadium carbonitrides. The most inconvenient change in T91 steel precipitate morphology due to long-term operation is the appearance of the Laves Fe{sub 2}Mo phase which along with M{sub 23}C{sub 6} carbide particles forms elongated blocks and conglomerates on grain boundaries. The article also presents results of tests related to the effect of simulated welding thermal cycles on selected properties of X10CrMoVNb9-1 (T91) grade steel at a state after approximately 100,000 h of operation. The tests involved the determination of the chemical composition of the steel tested as well as impact tests, hardness measurements and microscopic metallographic examination (based on light microscopy) of simulated heat-affected zone (HAZ) areas for a cooling time (t{sub 8/5}) restricted within a range between 3 s and 120 s, with and without heat treatment. The tests revealed that, among other results, hardness values of simulated HAZ areas in X10CrMoVNb9-1 (T91) steel do not guarantee cold crack safety of the steel at the state without additional heat treatment. It was also observed that simulated welding thermal cycles of cooling times t{sub 8/5}=3, 12, 60 and 120 s do not significantly affect the toughness and hardness of simulated HAZ areas of the steel tested.

  17. Effect of black clay soil moisture on the electrochemical behavior of API X70 pipeline steel

    Science.gov (United States)

    Hendi, R.; Saifi, H.; Belmokre, K.; Ouadah, M.; Smili, B.; Talhi, B.

    2018-03-01

    The effect of moisture content variation (20–100 wt.%) on the electrochemical behavior of API X70 pipeline steel buried in the soil of Skikda (East of Algeria) was studied using electrochemical techniques, scanning electron microscopy (SEM), X ray diffraction analysis (XRD) and weight loss measurement. The electrochemical measurements showed that the corrosion current Icorr is directly proportional to the moisture content up to 50 wt.%, beyond this content, this value becomes almost constant. The result were confirmed by electrochemical impedance spectroscopy; the capacitance of the double layer formed on the surface is the highest at 50 wt.%. A single time constant was detected by plotting the Bode diagrams. The steel surface degradation has been appreciated using the scanning electron microscopy observations. A few pitting corrosion at 20 wt.% moisture, followed by more degradation at 50 wt.% have been revealed. However, when the moisture amount exceeded 50 wt.%, the surface became entirely covered by a corrosion product. XRD analysis revealed the dominance of FeOOH and Fe3O4 phases on steel surface for a moisture content of 50 wt.%.

  18. Ex situ characterization of metallurgical inclusions in X100 pipeline steel before and after immersion in a neutral pH bicarbonate solution

    International Nuclear Information System (INIS)

    Li, Yingbo; Liu, Jie; Deng, Yida; Han, Xiaopeng; Hu, Wenbin; Zhong, Cheng

    2016-01-01

    The initiation of corrosion pits in pipeline steels plays an important role in the development of stress corrosion cracking. In order to reveal the effect of inclusions on corrosion initiation sites and also to clarify contradictory results from previous literature, we proposed an ex situ characterization method that is allowed to characterize exactly the same inclusion or location of the surface of steel before and after corrosion tests. The time-dependent corrosion behaviour of the inclusions and the surrounding X100 steel matrix at the same area before and after early stage immersion in a near-neutral pH bicarbonate solution was investigated by ex situ scanning electron microscopy (SEM), energy-dispersive X-ray (EDX) analysis and localized electrochemical impedance spectroscopy (LEIS). The sizes of most inclusions in X100 steel are below 3 μm. The results challenge the long-held opinion of previous work that corrosion pit initiations are related with the inclusions. It has been found that most of the inclusions remain stable (intact) during the whole testing time although severe corrosion occurs on the matrix of the steel. The chemical composition of the inclusion greatly affects the chemical stability of the inclusion. SiO_2 inclusions and complex inclusions with a high SiO_2 content remain intact although obvious general corrosion occurs on the steel matrix under the investigated immersion period. Inclusions with little Si, such as Al–Mg–Ca–O enriched inclusions, totally disappear after certain immersion time. During the immersion, the corrosion product tends to deposit at the interstice between the inclusion and steel matrix. - Highlights: • Ex situ characterization of metallurgical inclusions in X100 pipeline steel. • The pipeline steel was immersed in neutral pH bicarbonate solution. • Majority of inclusions remain stable during the whole testing time. • The chemical stability of metallurgical inclusions depends on the SiO_2 content.

  19. Ex situ characterization of metallurgical inclusions in X100 pipeline steel before and after immersion in a neutral pH bicarbonate solution

    Energy Technology Data Exchange (ETDEWEB)

    Li, Yingbo; Liu, Jie [Key Laboratory of Advanced Ceramics and Machining Technology (Ministry of Education), School of Materials Science and Engineering, Tianjin University, Tianjin 300072 (China); Deng, Yida [Tianjin Key Laboratory of Composite and Functional Materials, Tianjin University, Tianjin 300072 (China); Han, Xiaopeng [Key Laboratory of Advanced Ceramics and Machining Technology (Ministry of Education), School of Materials Science and Engineering, Tianjin University, Tianjin 300072 (China); Hu, Wenbin [Key Laboratory of Advanced Ceramics and Machining Technology (Ministry of Education), School of Materials Science and Engineering, Tianjin University, Tianjin 300072 (China); Tianjin Key Laboratory of Composite and Functional Materials, Tianjin University, Tianjin 300072 (China); Zhong, Cheng, E-mail: cheng.zhong@tju.edu.cn [Key Laboratory of Advanced Ceramics and Machining Technology (Ministry of Education), School of Materials Science and Engineering, Tianjin University, Tianjin 300072 (China)

    2016-07-15

    The initiation of corrosion pits in pipeline steels plays an important role in the development of stress corrosion cracking. In order to reveal the effect of inclusions on corrosion initiation sites and also to clarify contradictory results from previous literature, we proposed an ex situ characterization method that is allowed to characterize exactly the same inclusion or location of the surface of steel before and after corrosion tests. The time-dependent corrosion behaviour of the inclusions and the surrounding X100 steel matrix at the same area before and after early stage immersion in a near-neutral pH bicarbonate solution was investigated by ex situ scanning electron microscopy (SEM), energy-dispersive X-ray (EDX) analysis and localized electrochemical impedance spectroscopy (LEIS). The sizes of most inclusions in X100 steel are below 3 μm. The results challenge the long-held opinion of previous work that corrosion pit initiations are related with the inclusions. It has been found that most of the inclusions remain stable (intact) during the whole testing time although severe corrosion occurs on the matrix of the steel. The chemical composition of the inclusion greatly affects the chemical stability of the inclusion. SiO{sub 2} inclusions and complex inclusions with a high SiO{sub 2} content remain intact although obvious general corrosion occurs on the steel matrix under the investigated immersion period. Inclusions with little Si, such as Al–Mg–Ca–O enriched inclusions, totally disappear after certain immersion time. During the immersion, the corrosion product tends to deposit at the interstice between the inclusion and steel matrix. - Highlights: • Ex situ characterization of metallurgical inclusions in X100 pipeline steel. • The pipeline steel was immersed in neutral pH bicarbonate solution. • Majority of inclusions remain stable during the whole testing time. • The chemical stability of metallurgical inclusions depends on the SiO{sub 2

  20. Assembling x-ray sources by carbon nanotubes

    Science.gov (United States)

    Sessa, V.; Lucci, M.; Toschi, F.; Orlanducci, S.; Tamburri, E.; Terranova, M. L.; Ciorba, A.; Rossi, M.; Hampai, D.; Cappuccio, G.

    2007-05-01

    By the use of a chemical vapour deposition technique a series of metal wires (W, Ta, Steel ) with differently shaped tips have been coated by arrays of single wall carbon nanotubes (SWNT). The field emission properties of the SWNT deposits have been measured by a home made apparatus working in medium vacuum (10 -6- 10 -7 mbar) and the SWNT-coated wires have been used to fabricate tiny electron sources for X-ray tubes. To check the efficiency of the nanotube coated wires for X-ray generation has, a prototype X-ray tube has been designed and fabricated. The X-ray tube works at pressures about 10 -6 mbar. The target ( Al film) is disposed on a hole in the stainless steel sheath: this configuration makes unnecessary the usual Be window and moreover allows us to use low accelerating potentials (< 6 kV).

  1. X-ray stress analysis of residual stress gradients in surface layers of steel

    International Nuclear Information System (INIS)

    Ganev, N.; Kraus, I.; Gosmanova, G.; Pfeiffer, L.; Tietz, H.-D.

    2001-01-01

    The aim of the contribution is to present the theoretical possibilities of X-ray non-destructive identification of stress gradients within the penetration depth of used radiation and its utilization for experimental stress analysis. Practical usefullness of outlined speculations is illustrated with results of stress measurements on cut and shot-penned steel samples. (author)

  2. Characteristics of thermochemical treated EN10090 X50 steel

    International Nuclear Information System (INIS)

    Schmitz, S.; Graf, K.; Scheid, A.; Moreno, A.

    2014-01-01

    EN10090 X50 steel is commonly used for engine valves to withstand severe operation conditions involving high temperature and corrosion from fuel and combustion gas. Usually, to enhance wear performance, valves undergo nitriding thermochemical treatment by salt baths. The aim of this work is to produce diffusion layers at least 20μm thick with hardness higher than 700HV by plasma surface treatment with no continuous compounds layer using nitrogen and methane based atmospheres. Samples were characterized by laser Confocal and scanning electron microscopy, X-ray diffraction and Vickers hardness. Salt bath treatment induced formation of undesirable compounds layer at the surface and a diffusion layer thicker than 40μm, with hardness arising 1280HV_0_,_0_1_0. Plasma surface treatment produced diffusion layer thicker than 40μm with no continuous compounds layer and mean hardness varying from 750 to 960HV_0_,_0_1_0. (author)

  3. Compositional analysis of steels by x-ray fluorescence spectrometry

    International Nuclear Information System (INIS)

    Kutty, K.V.G.; Rajagopalan, S.; Ananthakrishnan, S.K.; Asuvatharaman, R.

    1988-01-01

    The x-ray fluorescence spectrometric method of determining Ni, Cr, Mn, Mo, T i, Si and Co in austenitic, ferritic, titanium-stabilised and low alloy steels is described. Samples in the bulk solid form (25-50 mm diameter and upto 50 mm height) or very small samples having a flat surface at least 5 mm in diameter are analysed as received after a brief surface treatment. The complex matrix effects affecting the determination of the various elements are discussed. The direct calibration method as well as the mathematical method of empirical coefficients of overcoming the matrix effects is described. The precision and accuracy of the analyses are discussed. (author). 10 refs

  4. Microstructure and mechanical properties of unirradiated low activation ferritic steel

    International Nuclear Information System (INIS)

    Hsu, C.Y.; Lechtenberg, T.A.

    1986-01-01

    Transmission electron micrographs of normalized and tempered 9Cr-2.5W-0.3V-0.15C low activation ferritic steel showed tempered lath-type martensite with precipitation of rod and plate-like carbides at lath and grain boundaries. X-ray diffraction analysis of the extracted replicas revealed nearly 100% M 23 C 6 carbides (a=1.064 nm), with no indication of Fe 2 W-type Laves phase even after thermal aging at 600 0 C/1000 h. Thermal aging increased the number density of rod-like M 23 C 6 along prior austenite grain boundaries and martensite lath boundaries. The elevated-temperature tensile strengths of this steel are about 10% higher than the average strengths of commercial heats of 9Cr-1Mo and modified 9Cr-1Mo steels up to 650 0 C, with equivalent uniform elongation and ∝50% decrease in total elongation. The DBTT was determined to be -25 0 C which is similar to other 9Cr-1Mo steels. Fractographic examination of tensile tested specimens shows a mixed mode of equiaxed and elongated dimples at test temperatures above 400 0 C. Modification of the Ga3X alloy composition for opimization of materials properties is discussed. However, the proposed low activation ferritic steel shows the promise of improved mechanical properties over 9Cr-1Mo steels. (orig.)

  5. Ion irradiation-induced precipitation of Cr23C6 at dislocation loops in austenitic steel

    International Nuclear Information System (INIS)

    Jin, Shuoxue; Guo, Liping; Luo, Fengfeng; Yao, Zhongwen; Ma, Shuli; Tang, Rui

    2013-01-01

    The irradiation-induced precipitates in argon ion-irradiated austenitic stainless steel at 550 °C were examined via transmission electron microscopy. The selected-area electron diffraction patterns of precipitates indicated unambiguously that the precipitates were Cr 23 C 6 carbides. It was observed directly for the first time that irradiation-induced Cr 23 C 6 precipitates formed at dislocation loops in austenitic stainless steel, and coarsened with increasing irradiation dose.

  6. Sensitivity and statistical analysis within the elaboration of steel plated girder resistance

    Czech Academy of Sciences Publication Activity Database

    Melcher, J.; Škaloud, Miroslav; Kala, Z.; Karmazínová, M.

    2009-01-01

    Roč. 5, č. 2 (2009), s. 120-126 ISSN 1816-112X. [International conf. on steel and aluminium structures /6./. Oxford, 24.06.2007-27.06.2007] Institutional research plan: CEZ:AV0Z20710524 Keywords : steel structures * fatigue * sensitivity * imperfection * plated girder Subject RIV: JM - Building Engineering

  7. Microchemistry of neutron irradiated 12%CrMoVNb martensitic steel

    International Nuclear Information System (INIS)

    Little, E.A.; Morgan, T.S.; Faulkner, R.G.

    1992-01-01

    Non-equilibrium solute segregation has been studied in a 12%CrMoVNb martensitic steel following fast reactor irradiation at 465 C and correlated with the development of M 6 X η-phase. Cr, Ni, Si, Mo, P and Mn are all shown to exhibit positive segregation to lath boundaries and are subsequently incorporated into M 6 X precipitates. The co-segregation of a combination of these elements which include P and Si, and possibly Cr or Mo, appears to promote M 6 X formation

  8. Two-dimensional time-resolved x-ray diffraction study of dual phase rapid solidification in steels

    Science.gov (United States)

    Yonemura, Mitsuharu; Osuki, Takahiro; Terasaki, Hidenori; Komizo, Yuichi; Sato, Masugu; Toyokawa, Hidenori; Nozaki, Akiko

    2010-01-01

    The high intensity heat source used for fusion welding creates steep thermal gradients of 100 °C/s from 1800 °C. Further, the influence of preferred orientation is important for the observation of a directional solidification that follows the dendrite growth along the ⟨100⟩ direction toward the moving heat source. In the present study, we observed the rapid solidification of weld metal at a time resolution of 0.01-0.1 s by a two-dimensional time-resolved x-ray diffraction (2DTRXRD) system for real welding. The diffraction rings were dynamically observed by 2DTRXRD with synchrotron energy of 18 keV while the arc passes over the irradiation area of the x-rays. The arc power output was 10 V-150 A, and the scan speed of the arc was 1.0 mm/s. The temperature rise in instruments was suppressed by a water-cooled copper plate under the specimen. Further, the temperature distribution of the weld metal was measured by a thermocouple and correlated with the diffraction patterns. Consequently, solidification and solid phase transformation of low carbon steels and stainless steels were observed during rapid cooling by 2DTRXRD. In the low carbon steel, the microstructure is formed in a two step process, (i) formation of crystallites and (ii) increase of crystallinity. In stainless steel, the irregular interface layer of δ/γ in the quenched metal after solidification is expected to show the easy movement of dendrites at a lower temperature. In carbide precipitation stainless steel, it is easy for NbC to grow on δ phase with a little undercooling. Further, a mistlike pattern, which differs from the halo pattern, in the fusion zone gave some indication of the possibilities to observe the nucleation and the early solidification by 2DTRXRD.

  9. Cracking resistance study of steel for gas pipelines; Badania odpornosci stali przeznaczonej na rurociagi gazowe

    Energy Technology Data Exchange (ETDEWEB)

    Wasiak, J.; Bilous, W.; Hajewska, E.; Szteke, W.; Wagner, T. [Institute of Atomic Energy, Otwock-Swierk (Poland)

    1996-12-31

    The results of cracking resistance of steel tubes for gas pipelines have been performed. The temperature dependence of mechanical properties of X56 steel used as tube material have been shown. 2 refs, 6 figs, 4 tabs.

  10. Interpretation and significance of reverse chevron-shaped markings on fracture surfaces of API X100 pipeline steels

    International Nuclear Information System (INIS)

    Sowards, Jeffrey W.; McCowan, Chris N.; Drexler, Elizabeth S.

    2012-01-01

    Highlights: ► We investigated fractures of X100 steel linepine produced during fracture mechanics testing. ► Fractures exhibited a unique chevron pattern that points in the direction of crack propagation. ► A qualitative model is proposed to explain the fracture pattern formation. ► Findings indicate that careful interpretation of ductile material fractures is necessary. - Abstract: Fracture surfaces of X100 pipeline steels were examined with optical and electron microscopy after crack tip opening angle fracture testing. Some fracture surfaces exhibited chevron-shaped fracture patterns that are markedly different from classic chevron fracture. The chevron-shaped markings on the X100 fracture surfaces point in the direction of crack growth, rather than towards the location of fracture initiation, as observed in classic cases of chevron fracture. Existing models, predicting formation of chevron fracture patterns, do not explain the fracture behavior observed for X100 steel. A mechanism is proposed where reverse chevron-shaped patterns are developed due to the shape of the crack front itself. The chevron shape forms as a result of crack tunneling, and the overall pattern is developed on the fracture surface due to intermittent crack growth, resulting in alternating regions (bands) of fast fracture and slower, more ductile fracture. The contrast between these bands of alternating fracture defines the chevron. Care should be taken during interpretation of intermittent chevron markings on fractures of ductile materials, as they may point away from rather than towards the origin of fracture.

  11. X-ray photoelectron spectroscopy studies of hard coatings formed by titanium on 304 stainless steel

    International Nuclear Information System (INIS)

    Nair, M.R.; Kothari, D.C.; Rangwala, A.A.; Lal, K.B.; Prabhawalkar, P.D.; Raole, P.M.

    1986-01-01

    Titanium ions are implanted (at 30 keV) in 304 stainless steel to a dose of 1.8x10 17 ions cm -2 using 15 μA cm -2 and 5 μA cm -2 beam current densities for specimens 2 and 3 respectively. X-ray photoelectron spectroscopy (XPS) measurements are performed at different temperatures. The microhardness of implanted and unimplanted specimens is also measured. In specimen 2 the microhardness does not increase significantly and XPS measurements give evidence of carburized surface alloy formation. At 250 0 C TiO 2 is detected on the surface and it migrates into the bulk phase above 350 0 C. In specimen 3 the XPS measurements exhibit an absence of iron owing to the radiation-induced segregation of titanium on the surface. This specimen shows an increase in microhardness. The XPS measurements reveal a layer of (TiC x -C) on the surface which is suggested to be responsible for the increase in microhardness. Upon heating, TiC x is seen to move into the bulk phase and the carbon concentration is increased. These changes occurring at higher temperatures are suggested as having an effect on the wear-resistant properties of titanium-implanted 304 stainless steel. (orig.)

  12. Corrosive effect of oil's accompanying water polluted with H2S over steel (API 5L X-52)

    International Nuclear Information System (INIS)

    Cueli Corugedo, Alexander; Adames Montero, Yosmari; Rivera Beltran, Yischy; Davis Harriet, Juan

    2013-01-01

    The corrosion from the steel to the carbon in the sale oil pipage conduction, is a serious problem, due to the material and economical looses they cause, damaging even in some cases the productive field. The purpose of this study is to determine the aggressiveness of the oil's water layer, polluted with H 2 S ( g) , over the steel of pipelines' construction (API 5L X-52), taking into account the temperature variations which take place during the transportation of the oil, using the electrochemical techniques of polarisation resistance (LPR) and electrochemical noise. It is pretended to determine the velocity of steel corrosion in the oil's water layer polluted with H 2 S through electrochemical techniques. It was shown that the temperature increases and the concentration of H 2 S to 500 ppm in the oil's accompanying water emphasizes the corrosion phenomenon experienced by the steel (9, 188 0 mm/year to 70℃).The results of the electrochemical noise spectrums and the values of the localisation ?s index calculated, shown the presence of corrosion on the steel surface (API 5L X-52).This result was complemented through optic Microscopy which permits to corroborate the poor adherence of the sulphur layers deposited on the metal that increase the appearance of events found with the temperature increase and the concentration of H 2 S in the environment studied

  13. Tribological Behavior of Multilayered WC-Ti1-xAlxN Coatings Deposited by Cathodic Arc Deposition Process on High Speed Steel

    International Nuclear Information System (INIS)

    Kim, Jung Gu; Hwang, Woon Suk

    2006-01-01

    Recently, much of the current development in surface modification engineering are focused on multilayered coatings. Multilayered coatings have the potential to improve the tribological properties. Four different multilayered coatings were deposited on AISI D2 steel. The prepared samples are designed as WC-Ti 0.6 Al 0.4 N, WC-Ti 0.53 Al 0.47 N, WC-Ti 0.5 Al 0.5 N and WC-Ti 0.43 Al 0.57 N. The multilayered coatings were investigated with respect to coating surface and cross-sectional morphology, roughness, adhesion, hardness, porosity and tribological behavior. Especially, wear tests of four multilayered coatings were preformed by using a ball-on-disc configuration with a linear sliding speed of 0.017 m/sec, 5.38 N load. The tests were carried out at room temperature in air by employing AISI 52100 steel ball (H R = 66) having a diameter of 10 mm. The surface morphology, and topography of the wear scars of samples and balls have been determined by using scanning electron spectroscopy (SEM). Results have showed an improved wear resistance of the WC-Ti 1-x 6Al x N coatings with increasing of Al concentration. WC-Ti 0.43 Al 0.57 N coating with the lower surface roughness and porosity with good adhesion enhanced wear resistance

  14. Elevated temperature mechanical properties of line pipe steels

    Science.gov (United States)

    Jacobs, Taylor Roth

    The effects of test temperature on the tensile properties of four line pipe steels were evaluated. The four materials include a ferrite-pearlite line pipe steel with a yield strength specification of 359 MPa (52 ksi) and three 485 MPa (70 ksi) yield strength acicular ferrite line pipe steels. Deformation behavior, ductility, strength, strain hardening rate, strain rate sensitivity, and fracture behavior were characterized at room temperature and in the temperature range of 200--350 °C, the potential operating range for steels used in oil production by the steam assisted gravity drainage process. Elevated temperature tensile testing was conducted on commercially produced as-received plates at engineering strain rates of 1.67 x 10 -4, 8.33 x 10-4, and 1.67 x 10-3 s-1. The acicular ferrite (X70) line pipe steels were also tested at elevated temperatures after aging at 200, 275, and 350 °C for 100 h under a tensile load of 419 MPa. The presence of serrated yielding depended on temperature and strain rate, and the upper bound of the temperature range where serrated yielding was observed was independent of microstructure between the ferrite-pearlite (X52) steel and the X70 steels. Serrated yielding was observed at intermediate temperatures and continuous plastic deformation was observed at room temperature and high temperatures. All steels exhibited a minimum in ductility as a function of temperature at testing conditions where serrated yielding was observed. At the higher temperatures (>275 °C) the X52 steel exhibited an increase in ductility with an increase in temperature and the X70 steels exhibited a maximum in ductility as a function of temperature. All steels exhibited a maximum in flow strength and average strain hardening rate as a function of temperature. The X52 steel exhibited maxima in flow strength and average strain hardening rate at lower temperatures than observed for the X70 steels. For all steels, the temperature where the maximum in both flow

  15. Measurement of erosion of stainless steel by molten lead-free solder using micro-focus x-ray CT system

    International Nuclear Information System (INIS)

    Nishikawa, Hiroshi; Takemoto, Tadashi; Kang, Songai

    2009-01-01

    The severe erosion damage, which is caused by a molten lead-free solder, of wave solder equipment made into stainless steel has been encountered in operation. Then, the higher maintenance frequency and reduced life time of wave solder machine component is a serious issue in a manufacturing process. In this study, the evaluation method of erosion of stainless steel by molten lead-free solders was investigated using micro-focus X-ray systems for fluoroscopic and computed tomography (CT). As a result, it was found that the fluoroscopic image could truly reconstruct the cross-shape of the stainless steel sample after immersion test without destruction. In the case of X-ray systems for fluoroscopic and CT used in this study, three-dimensional data can be obtained. Therefore, it was possible to easily check the whole picture of the test sample after immersion test and to decide the maximum erosion depth of test sample. (author)

  16. EBSD study of hydrogen-induced cracking in API-5 L-X46 pipeline steel

    International Nuclear Information System (INIS)

    Venegas, V.; Caleyo, F.; Gonzalez, J.L.; Baudin, T.; Hallen, J.M.; Penelle, R.

    2005-01-01

    The spatial distribution of plastic deformation and grain orientation surrounding hydrogen-induced cracks (HIC) is investigated in samples of API-5L-X46 pipeline steel using scanning electron microscopy and electron backscattering diffraction (EBSD). This work shows direct experimental evidence of the influence of microstructure, microtexture and mesotexture on HIC crack path

  17. Effect of Strength and Microstructure on Stress Corrosion Cracking Behavior and Mechanism of X80 Pipeline Steel in High pH Carbonate/Bicarbonate Solution

    Science.gov (United States)

    Zhu, Min; Du, Cuiwei; Li, Xiaogang; Liu, Zhiyong; Wang, Shengrong; Zhao, Tianliang; Jia, Jinghuan

    2014-04-01

    The stress corrosion cracking (SCC) behaviors and mechanisms of X80 pipeline steels with different strength and microstructure in high pH carbonate/bicarbonate solution were investigated by slow strain rate testing and electrochemical test. The results showed that the cracking mode of low strength X80 steel composed of bulky polygonal ferrite and granular bainite in high pH solution was intergranular (IGSCC), and the SCC mechanism was anodic dissolution (AD). While the mixed cracking mode of high strength X80 steel consisted of fine acicular ferrite and granular bainite was intergranular (IGSCC) in the early stage, and transgranular (TGSCC) in the later stage. The decrease of pH value of crack tip was probably the key reason for the occurrence of TGSCC. The SCC mechanism may be a mixed mode of AD and hydrogen embrittlement (HE), and the HE mechanism may play a significant role in the deep crack propagation at the later stage. The cracking modes and SCC mechanisms of the two X80 steels were associated with its microstructure and strength.

  18. On the measurement of austenite in supermartensitic stainless steel by X-ray diffraction

    Energy Technology Data Exchange (ETDEWEB)

    Tolchard, Julian Richard, E-mail: tolchard@material.ntnu.no [Department of Materials Science and Engineering, Norwegian University of Science and Technology, Trondheim (Norway); Sømme, Astri; Solberg, Jan Ketil [Department of Materials Science and Engineering, Norwegian University of Science and Technology, Trondheim (Norway); Solheim, Karl Gunnar [Statoil, Stavanger (Norway)

    2015-01-15

    Sections of a 13Cr supermartensitic stainless steel were investigated to determine the optimum sample preparation for measurement of the austenite content by X-ray diffraction. The surface of several samples was mechanically ground or polished using media of grit sizes in the range 1–120 μm. The strained surface layer was afterwards removed stepwise by electropolishing, and the austenite content measured at each step. It was found that any level of mechanical grinding or polishing results in a reduction of the measured austenite fraction relative to the true bulk value, and that coarser grinding media impart greater damage and greater reduction in the measured austenite content. The results thus highlight the importance of the electropolishing step in preparation of such samples, but suggest that the American Society for Testing and Materials standard E975-03 substantially overestimates the amount of material which needs to be removed to recover the true “bulk” content. - Highlights: • Quantitative Rietveld analysis of austenite/martensite ratio in supermartensitic stainless steels • Critical evaluation of sample preparation for residual austenite measurements by X-ray diffraction • Highlighting of the importance of electropolishing as a final preparation step.

  19. Effect of Pipe Flattening in API X65 Linepipe Steels Having Bainite vs. Ferrite/Pearlite Microstructures

    Directory of Open Access Journals (Sweden)

    Singon Kang

    2018-05-01

    Full Text Available The influence of microstructure on pipe flattening response was assessed using two different commercially produced U-ing, O-ing, and expansion (UOE pipes from API X65 steels having either a bainitic microstructure (steel B or a ferrite/pearlite microstructure (steel FP. A four-point bending apparatus and distinctive procedure were used to minimize strain localization during flattening. The flattened specimens were sectioned at different positions through the thickness, and tensile tested in both the longitudinal (LD and transverse directions (TD to assess the through-thickness variation in properties. Yield strength (YS distributions in the LD show V-shaped profiles through thickness in both steels, whereas the YS in the TD nearest the outside diameter (OD surface is reduced. These variations in YS are due to the Bauschinger effect associated with the compressive flattening pre-strain. The uniform elongation (UE of steel FP is almost independent of specimen position through the thickness, but for steel B there is a substantial reduction of the UE at both the inside and outside diameter positions and this reduction is greater in the LD. This work confirms that flattened pipe mechanical properties exhibit an important dependence on their microstructure type and it is postulated that the flattening procedure also influences the mechanical properties.

  20. Study of the temperature effect on the surface of stainless steel using fission track technique

    Energy Technology Data Exchange (ETDEWEB)

    Dhawan, M M; Nagpaul, K K [Kurukshetra Univ. (India). Dept. of Physics

    1977-01-01

    Solid state track technique has been used to determine trace amounts of uranium in steel. Steel samples of the size 1 cm x 1 cm x 0.6 cm were ground, polished, heated to various temperatures ranging from room temperature to 900 deg C and then packed alternately with lexan detectors in an aluminium capsule for thermal neutron irradiation. After irradiation, lexan discs were removed and etched. Their surfaces were scanned under an optical microscope for measurement of track density. Uranium contents of the samples was found to vary from 6 ppm to 9 ppm.

  1. X-ray Radiographic Study of Simulated Voids-like Defects in Al-Castings and Welded in Steel

    International Nuclear Information System (INIS)

    Mahrok, M.; Juma, Th.; Saeed, F.

    2013-01-01

    the detection and evaluation of imperfections in internal structures of casting and welded joints by x - ray radiography were studied.Optimum radiography conditions that improved the radiographic detection were attempted.Mathematical equations for radiography were used to calculate the size and depth of defects in casting were tested for validity to a wide range of parameters commonly used in radiography and for variable density and shape of the defects with respect to surrounding.Two kinds of samples are prepared.The first is aluminum casting through which two different sizes of a regular steel spheres are included and then radio graphed from two opposite sides to estimate their dimensional information from the radiographs.The second sample is steel plates which are welded and then radio graphed by x - rays.Imperfections such as incomplete root penetration, undercut and porosity were detected in the radiographs.

  2. Semisolid forming of 44MnSiV6 microalloyed steel

    Science.gov (United States)

    Plata, Gorka; Lozares, Jokin; Hurtado, Iñaki; Azpilgain, Zigor; Idoyaga, Zuriñe

    2018-05-01

    Globalisation is forcing many sectors to be more cost-effective due to the low manpower cost of developing countries. This, in combination with European trends of green production and reduction of emissions, enhances the necessity of advanced technologies to remain at the forefront of the market. It is precisely in this field where the Semisolid forming (SSF) exhibits a great potential. In Mondragon Unibertsitatea, it has been demonstrated the capability of producing sound components of 42CrMo4 and S48C steels by saving material, energy and attaining as hot forged properties. To make the process even more cost-effective, it has also been proved the capacity of SSF 44MnSiV6 microalloyed steel that enables the striking of the post processing heat treatment.

  3. Influence of surface mechanical activation of the X40Cr13 steel on roughness after ion and gas nitriding

    International Nuclear Information System (INIS)

    Jasinski, J.; Wojtal, A.; Jeziorski, L.; Radecki, A.; Ucieklak, S.

    2003-01-01

    The article describes the problem of the thermal and mechanical activation of the surface of the X40Cr13 steel on the state of the ion and gas nitriding. in order to determine the nitriding influence and make the analysis of results, the steel was subjected to: soft annealing, hardening with subsequent tempering at T = 550 o C and also mechanical activation of the surface consisting in peripheral grinding with abrasive papers of the grain size 60, 360, 1000 and mechanical polishing. The main aim of this work was to establish the influence of different surface geometrical structure, depending on X40Cr13 steel structure, on the roughness profile after ion and gas nitriding. With regard to the above, the examinations of basic roughness parameters prior to and after thermochemical processes and the analysis of utilitarian usefulness of activations applied were carried out. (author)

  4. Effect of pre-deformation on the fatigue crack initiation life of X60 pipeline steel

    International Nuclear Information System (INIS)

    Zheng, M.; Luo, J.H.; Zhao, X.W.; Bai, Z.Q.; Wang, R.

    2005-01-01

    It is impossible to keep petroleum and natural gas transmission pipelines free from defects in the manufacturing, installation and servicing processes. The damage might endanger the safety of pipelines and even shorten their service life; gas or petroleum release due to defects may jeopardise the surrounding ecological environments with associated economic and life costs. Pre-tensile deformation of X60 steel is employed to experimentally simulate the influence of dents on the fatigue crack initiation life. The investigation indicates that the fatigue crack initiation life of pre-deformed X60 pipeline steel can be assessed by a previously proposed energetic approach. The threshold for crack initiation increases with the pre-deformation due to a strain hardening effect, while the fatigue resistant factor exhibits a maximum with pre-deformation owing to its special dependence on fracture strain and fracture strength. The result is expected to be beneficial to the understanding of the effect of damage on the safety of pipelines and fatigue life prediction

  5. Stress corrosion cracking of X80 pipeline steel exposed to high pH solutions with different concentrations of bicarbonate

    Science.gov (United States)

    Fan, Lin; Du, Cui-wei; Liu, Zhi-yong; Li, Xiao-gang

    2013-07-01

    Susceptibilities to stress corrosion cracking (SCC) of X80 pipeline steel in high pH solutions with various concentrations of HCO{3/-} at a passive potential of -0.2 V vs. SCE were investigated by slow strain rate tensile (SSRT) test. The SCC mechanism and the effect of HCO{3/-} were discussed with the aid of electrochemical techniques. It is indicated that X80 steel shows enhanced susceptibility to SCC with the concentration of HCO{3/-} increasing from 0.15 to 1.00 mol/L, and the susceptibility can be evaluated in terms of current density at -0.2 V vs. SCE. The SCC behavior is controlled by the dissolution-based mechanism in these circumstances. Increasing the concentration of HCO{3/-} not only increases the risk of rupture of passive films but also promotes the anodic dissolution of crack tips. Besides, little susceptibility to SCC is found in dilute solution containing 0.05 mol/L HCO{3/-} for X80 steel. This can be attributed to the inhibited repassivation of passive films, manifesting as a more intensive dissolution in the non-crack tip areas than at the crack tips.

  6. Circumferential welding of API X80 steel pipes; Soldagem circunferencial em tubos de aco da classe API X80

    Energy Technology Data Exchange (ETDEWEB)

    Castello Branco, J.F.; Bott, Ivani de S. [Pontificia Univ. Catolica do Rio de Janeiro, RJ (Brazil). Dept. de Ciencia dos Materiais e Metalurgia]. E-mails: joaofcb@uol.com.br; bott@dcmm.puc-rio.br; Fedele, R.A. [Boehler Thyssen Welding, Sao Paulo, SP (Brazil)]. E-mail: engenharia@btwbr.com.br; Souza, Luis Felipe G. de [Centro Federal de Educacao Tecnologica Celso Suckow da Fonseca (CEFET-RJ), Rio de Janeiro, RJ (Brazil). Dept. de Engenharia Industrial Mecanica]. E-mail: lfelipe@cefet-rj.br

    2003-07-01

    The present work is a part of an extensive program for the development of API 5L Gr.X80 grade steel , produced by the well-known UOE production process, for pipeline fabrication. The current stage of this program involves the characterization and performance evaluation/qualification of girth welds produced by Shield Metal Arc Weld (SMAW) under simulated field conditions, with tubes fixed in the horizontal position. Three types of electrodes were utilized for the basic tasks; the root pass, the hot pass and fill and cap passes. The root pass was carried out with an E-6010 electrode to avoid incomplete joint penetration. The hot pass, applied over the root pass, was performed with an E-9010-G electrode. The fill and cap passes were executed with E-10018-G electrodes. The welded joints produced were evaluated according to the API 1104 specification, which requires: side bend, nick- break and tensile tests. Additionally, non-destructive tests, Charpy-V impact tests and metallographic characterization were undertaken. It was verified that this welding procedure, based on three types of electrodes, could produce welded joints in accordance to the API 1104 specification. These results ensure the applicability of the API 5L Gr. X80 steel developed in this research project for use in pipeline construction. (author)

  7. Residual stress evaluation by X-Ray diffraction and hole-drilling in an API 5L X70 steel pipe bent by hot induction

    International Nuclear Information System (INIS)

    Ceglias, Rodrigo Braga; Alves, Juciane Maria; Botelho, Ramon Alves; Baeta Junior, Eustaquio de Souza; Santos, Igor Cuzzuol dos; Moraes, Nicki Robbers Darciano Cajueiro de; Oliveira, Rebeca Vieira de; Diniz, Saulo Brinco; Brandao, Luiz Paulo

    2016-01-01

    The API 5L X70 steel is used in high-pressure gas transmission pipelines. Because of this, knowledge of presence of residual stress and their magnitude is important to assess the material integrity in service. For the pipeline manufacturing, tubes need to be curved which is often made using the hot induction bending process. This process can introduce different residual stress depending of tube position. For this research, in order to evaluate the residual stress, was used an API 5L X70 tube that was previously curved by hot induction process. Samples were taken from the extrados, intrados, neutral line and straight section of the curved tube. Residual stresses were studied by two conventional methods: X-Ray Diffraction (XRD) and Hole-Drilling, which are destructive and non-destructive methods, respectively, in order to assess their qualitative responses. Each of these methods presents particular methodologies in sample preparation and material analysis, but also they differ in factors such time consumption and cost of the analysis. The qualitative responses obtained by the two different methods were comparable and satisfactory and pointed out the existence of a compressive residual stress state in steel pipe. (author)

  8. Residual stress evaluation by X-Ray diffraction and hole-drilling in an API 5L X70 steel pipe bent by hot induction

    Energy Technology Data Exchange (ETDEWEB)

    Ceglias, Rodrigo Braga; Alves, Juciane Maria; Botelho, Ramon Alves; Baeta Junior, Eustaquio de Souza; Santos, Igor Cuzzuol dos; Moraes, Nicki Robbers Darciano Cajueiro de; Oliveira, Rebeca Vieira de; Diniz, Saulo Brinco; Brandao, Luiz Paulo, E-mail: brandao@ime.eb.br [Instituto Militar de Engenharia (IME), Rio de Janeiro, RJ (Brazil). Secao de Engenharia Mecanica e de Materiais

    2016-09-15

    The API 5L X70 steel is used in high-pressure gas transmission pipelines. Because of this, knowledge of presence of residual stress and their magnitude is important to assess the material integrity in service. For the pipeline manufacturing, tubes need to be curved which is often made using the hot induction bending process. This process can introduce different residual stress depending of tube position. For this research, in order to evaluate the residual stress, was used an API 5L X70 tube that was previously curved by hot induction process. Samples were taken from the extrados, intrados, neutral line and straight section of the curved tube. Residual stresses were studied by two conventional methods: X-Ray Diffraction (XRD) and Hole-Drilling, which are destructive and non-destructive methods, respectively, in order to assess their qualitative responses. Each of these methods presents particular methodologies in sample preparation and material analysis, but also they differ in factors such time consumption and cost of the analysis. The qualitative responses obtained by the two different methods were comparable and satisfactory and pointed out the existence of a compressive residual stress state in steel pipe. (author)

  9. X-ray impact induced desorption of gases from surfaces

    International Nuclear Information System (INIS)

    Brumbach, S.; Kaminsky, M.

    1976-02-01

    Measurements of gases released from 302 stainless steel and gold surfaces before and after discharge cleaning were made in ultrahigh vacuum using x-rays with an energy distribution typical of a tungsten bremsstrahlung spectrum. Similar measurements were also made for Al 2 O 3 surfaces which had not been discharge cleaned. For the non-discharge-cleaned surfaces of stainless steel, Al 2 O 3 , and gold the predominant gas species observed mass spectrometrically was CO 2 . For some stainless steel and Al 2 O 3 surfaces CO and O 2 were also readily observed. Mean quantum yields for CO, O 2 and CO 2 release from such stainless steel surfaces, for example, ranged from less than 6 x 10 -5 to 9 x 10 -4 molecules per photons in the bremsstrahlung spectrum characteristic for 50 keV electron energy. After discharge cleaning a decrease in the mean quantum yields was observed for the stainless steel and gold surfaces

  10. Optimization of Thixoforging Parameters for C70S6 Steel Connecting Rods

    Science.gov (United States)

    Özkara, İsa Metin; Baydoğan, Murat

    2016-11-01

    A microalloyed steel, C70S6, with a solidification interval of 1390-1479 °C, was thixoforged in the semisolid state in a closed die at temperatures in the range 1400-1475 °C to form a 1/7 scaled-down model of a passenger vehicle connecting rod. Die design and an optimized thixoforging temperature eliminated the excessive flash and other problems during forging. Tension test samples from connecting rods thixoforged at the optimum temperature of 1440 °C exhibited nearly the same hardness, yield strength, and ultimate tensile strength as conventional hot forged samples but ductility decreased by about 45% due to grain boundary ferrite network formed during cooling from the thixoforging temperature. Thus, C70S6-grade steel can be thixoforged at 1440 °C to form flash-free connecting rods. This conclusion was also validated using FEA analysis.

  11. Nitrogen plasma immersion ion implantation for surface treatment and wear protection of austenitic stainless steel X6CrNiTi1810

    International Nuclear Information System (INIS)

    Blawert, C.; Mordike, B.L.

    1999-01-01

    Plasma immersion ion implantation is an effective surface treatment for stainless steels. The influence of treatment parameters (temperature, plasma density and pressure) on the sliding wear resistance are studied here. At moderate temperatures, nitrogen remains in solid solution without forming nitrides. This increases the surface hardness and the wear resistance without affecting the passivation of the steel. This may allow the use of such steels in applications where their poor wear resistance would normally prohibit their use. (orig.)

  12. X-ray fractographic study on fatigue fracture surface of structural steels

    International Nuclear Information System (INIS)

    Ogura, Keiji; Miyoshi, Yoshio; Kawaguchi, Masahiro; Kayama, Masahiro.

    1985-01-01

    An X-ray fractographic study was made on the fatigue fracture surface of the structural steels with various strength levels. An emphasis was put on examining the effect of strength level on the residual stress and half-value breadth on and under the fracture surface. It was found that the residual stress on the fracture surface was controlled by Ksub(max) in a low Ksub(max) or ΔK region (Region I), while it was controlled by ΔK rather than Ksub(max) in a high Ksub(max) or ΔK region (Region III). It was also found that another transitional region (Region II) was observed between these two regions in SNCM 815 steel. An explanation for all these behavior was discussed by a proposed model. The distribution of the residual stress and half-value breadth under the fracture surface was found to be usefull for estimating the value of Ksub(max), although the distribution itself was strongly influenced by strength level, particularly the work-softening behavior, of the materials. (author)

  13. Gaseous hydrogen embrittlement of an API X80 ferrito-pearlitic steel; Fragilisation par l'hydrogene gazeux d'un acier ferrito-perlitique de grade API X80

    Energy Technology Data Exchange (ETDEWEB)

    Moro, I.

    2009-11-15

    This work deals with hydrogen embrittlement, at ambient temperature and under a high pressure gaseous way, of an API X80 high elasticity limit steel used for pipelines construction, and with the understanding of the associated physical mechanisms of the embrittlement. At first has been described a bibliographic study of the adsorption, absorption, diffusion, transport and trapping of hydrogen in the steels. Then has been carried out an experimental and numerical study concerning the implantation in the finite element code CASTEM3M of a hydrogen diffusion model coupled to mechanical fields. The hydrogen influence on the mechanical characteristics of the X80 steel, of a ferrito-pearlitic microstructure has been studied with tensile tests under 300 bar of hydrogen and at ambient temperature. The sensitivity of the X80 steel to hydrogen embrittlement has been analyzed by tensile tests at different deformation velocities and under different hydrogen pressures on axisymmetrical notched test specimens. These studies show that the effect of the hydrogen embrittlement vary effectively with the experimental conditions. Moreover, correlated with the results of the tests simulations, it has been shown too that in these experimental conditions and for that steel, the hydrogen embrittlement is induced by three different hydrogen populations: the hydrogen trapped at the ferrite/perlite interfaces, the hydrogen adsorbed on surface and the reticular hydrogen trapped in the material volume. At last, the tensile and rupture tests of specimens, during which atmosphere changes have been carried out, have shown a strong reversibility of the hydrogen embrittlement, associated with its initiation as soon as hydrogen is introduced in the atmosphere. At last, three hydrogen mechanisms, depending of the different hydrogen populations are presented and discussed. (O.M.)

  14. Corrosion resistance of welded joints in 08Kh22N6T and 08Kh21N6M2T steels made with new electrodes

    International Nuclear Information System (INIS)

    Sidorkina, Y.S.; Leibzon, V.M.; Mankevich, T.V.; Sidlin, E.A.; Zheltova, G.A.

    1986-01-01

    This paper examines the corrosion resistance of 08Kh22N6T and 08Kh21N6M2T steels which would make it possible to ensure equal properties of all the zones of the welded joints. The investigations were carried out on the welded joints in the steels produced with new OZL-40 and OZL-41 electrodes and with standard TsL-11 and EA-400/10u electrodes. The chemical compositions of the steels and deposited metal are presented. The tests of the intercrystalline corrosion resistances of the welded joints in the steels in the as-welded condition and after heat treatment showed that the weld metal is not attacked by intercrystalline corrosion. The tests also showed that the welded joints in 08Kh22N6T steel made with the OZL-40 and TsL-11 electrodes are resistant to corrosion in 55% phosphoric acid at 90 C in 1% sulfuric acid, and in 25% formic acid at 80 C. The investigated steels made with the OZL-40 and OZL-41 electrode respectively show that the welded joints are resistant to intercrystalline and general corrosion, have high mechanical and processing properties and the electrodes, and can be used for welding equipment designed for service in alkaline, neutral, and slightly acid media

  15. Phase transformations in low-carbon manganese steel 6Mn16

    Directory of Open Access Journals (Sweden)

    J. Lis

    2009-01-01

    Full Text Available The kinetics of phase transformations of the austenite of 6Mn16 steel during continuous cooling are presented in a CCT diagram. Manganese partitioning between ferrite and austenite during intercritical annealing is enhanced by prior soft annealing. Due to the increased Mn concentration in austenite, the temperatures BS and MS have decreased, as compared to those achieved during cooling from the complete austenite region.

  16. High Ni austenite stainless steel resistant to neutron irradiation degradation

    International Nuclear Information System (INIS)

    Yonezawa, Toshio; Iwamura, Toshihiko; Kanasaki, Hiroshi; Fujimoto, Koji; Nakata, Shizuo; Ajiki, Kazuhide; Nakamura, Mitsuhiro.

    1997-01-01

    The composition of the stainless steel of the present invention comprises from 0.005 to 0.08% of C, up to 3% of Mn, up to 0.2% of Si+P+S, from 25 to 40% of Ni, from 25 to 40% of Cr, up to 3% of Mo, up to 0.3% of Nb+Ta, up to 0.3% of Ti, up to 0.001% of B and the balance of Fe. A solid solubilization treatment at a temperature of from 1,000 to 1,150degC is applied to the stainless steel having the composition. The stainless steel is excellent in stress corrosion cracking-resistance at a working circumstance of a LWR type reactor (high temperature and high pressure water at from 270 to 350degC/from 70 to 160 atm even after undergoing neutron irradiation of about 1 x 10 22 n/cm 2 (E>1 MeV) which is a maximum neutron irradiation amount undergone till the final stage of the working life of the LWR-type reactor. In addition, the average thermal expansion coefficient at from room temperature to 400degC ranges from 15x10 -6 - 19x10 -6 /K. (I.N.)

  17. X-Ray diffraction application in studying the nitrogen fixing and aging in stainless steel AISI 304

    International Nuclear Information System (INIS)

    Ramos, L.F.V.

    1973-01-01

    Solid solutions of N in AISI-304 stainless steels were aged to different degrees. The aging was monitored through X-Ray difraction measurement of the lattice parameter 'a'. The increases in 'a', due to the increase of N in solid solution were determined experimentally

  18. Thermal stability of retained austenite in TRIP steels studied by synchrotron X-ray diffraction during cooling

    International Nuclear Information System (INIS)

    Dijk, N.H. van; Butt, A.M.; Zhao, L.; Sietsma, J.; Offerman, S.E.; Wright, J.P.; Zwaag, S. van der

    2005-01-01

    We have performed in situ X-ray diffraction measurements at a synchrotron source in order to study the thermal stability of the retained austenite phase in transformation induced plasticity steels during cooling from room temperature to 100 K. A powder analysis of the diffraction data reveals a martensitic transformation of part of the retained austenite during cooling. The fraction of austenite that transforms during cooling is found to depend strongly on the bainitic holding time and the composition of the steel. It is shown that that austenite grains with a lower average carbon concentration have a lower stability during cooling

  19. Microstructure and Mechanical Properties of Dissimilar Friction Stir Spot Welding Between St37 Steel and 304 Stainless Steel

    Science.gov (United States)

    Khodadadi, Ali; Shamanian, Morteza; Karimzadeh, Fathallah

    2017-05-01

    In the present study, St37 low-carbon steel and 304 stainless steel were welded successfully, with the thickness of 2 mm, by a friction stir spot welding process carried out at the tool dwell time of 6 s and two different tool rotational speeds of 630 and 1250 rpm. Metallographic examinations revealed four different zones including SZ and HAZ areas of St37 steel and SZ and TMAZ regions of 304 stainless steel in the weld nugget, except the base metals. X-ray diffraction and energy-dispersive x-ray spectroscopy experiments were used to investigate the possible formation of such phases as chromium carbide. Based on these experiments, no chromium carbide precipitation was found. The recrystallization of the weld nugget in the 304 steel and the phase transformations of the weld regions in the St37 steel enhanced the hardness of the weld joint. Hardness changes of joint were acceptable and approximately uniform, as compared to the resistance spot weld. In this research, it was also observed that the tensile/shear strength, as a crucial factor, was increased with the rise in the tool rotational speed. The bond length along the interface between metals, as an effective parameter to increase the tensile/shear strength, was also determined. At higher tool rotational speeds, the bond length was found to be improved, resulting in the tensile/shear strength of 6682 N. Finally, two fracture modes were specified through the fracture mode analysis of samples obtained from the tensile/shear test consisting of the shear fracture mode and the mixed shear/tensile fracture mode.

  20. Annealing effect on restoration of irradiation steel properties

    International Nuclear Information System (INIS)

    Vishkarev, O.M.; Kolesova, T.N.; Myasnikova, K.P.; Pecherin, A.M.; Shamardin, V.K.

    1986-01-01

    The effect of temperature and annealing time on the restoration of properties of the 15Kh2NMFAA and 15Kh2MFA steels after irradiation at 285 deg with the fluence of 6x10 23 neutr/m 2 (E>0.5 MeV) is studied. Microhardness (H μ ) restoration in the irradiated 15Kh2NMFAA steel is shown to start from 350 deg C annealing temperature. The complete microhardness restoration is observed at the annealing temperature of 500 deg C for 10 hours

  1. Apoptosis in Postovulatory Follicles of Chalcalburnus tarichi Pallas, 1811.

    Directory of Open Access Journals (Sweden)

    Burak Kaptaner

    2015-12-01

    Full Text Available İnci kefali Chalcalburnus tarichi, Pallas, 1811 postovulasyon foliküllerinde apoptoz. Bu çalışmada, inci kefali (Chalcalburnus tarichi postovulasyon foliküllerinde apoptoz, TUNEL boyama ve agaroz jel elektroforez metodları ile araştırıldı ve plazma 17β-estradiol (E2 seviyesi ovulasyondan sonra 1., 3. ve 5. günlerde belirlendi. Postovulasyon foliküllerinde apoptotik hücreler, histolojik kesitlerde, ovulasyondan sonra 1. günde işaretlendi ve apoptozun çoğunlukla granuloza nadiren de teka hücrelerinde meydana geldiği belirlendi. Apoptozun işareti olan oligonükleozomal büyüklükteki DNA parçalanması ovulasyondan sonra 1., 3. ve 5. günlerde gözlendi. Ovulasyon anında oligonükleozomal DNA parçalanması gözlenmezken, 3. ve 5. günlerde bu parçalanmanın belirgin olduğu görüldü. Plazma E2 seviyesi ovulasyondan sonra dereceli olarak düştü. Bu düşüş 3. ve 5. günlerde önemliydi (P

  2. Avaliação de diferentes modelos de colméias para abelhas jataí (Tetragonisca angustula Latreille, 1811 Evaluation of different types of stingless bees hives (Tetragonisca angustula Latreille, 1811

    Directory of Open Access Journals (Sweden)

    Maria Claudia Colla Ruvolo-Takasusuki

    2002-04-01

    Full Text Available O objetivo deste trabalho foi avaliar o desempenho de colônias de abelhas jataís, Tetragonisca angustula Latreille, 1811 (Hymenoptera, Meliponinae na região de Maringá, Estado do Paraná, alojadas nos seguintes modelos de colméia: Fritzen, Guiliani, Nogueira-Neto e Antonio Carlos Farias (ACF. O experimento foi realizado no período de dezembro de 1999 a dezembro de 2000, com 20 colônias. Mensalmente, as colméias foram pesadas e obtendo-se o peso da colônia. Os dados foram analisados estatisticamente utilizando o mês como co-variável e o teste de Scheffe para comparação das médias. As colônias alojadas em colméias dos modelos Guiliani e Nogueira-Neto apresentaram um melhor desenvolvimento diferindo (p = 0,0004 das colônias alojadas nos modelos Fritzen e ACF. O peso médio das colônias foi de 387,3 ± 92,2g, 375,8 ± 72,6g, 241,2 ± 137,1g e 230,9 ± 55,3g, respectivamente, para as alojadas nos modelos Guiliani, Nogueira-Neto, ACF e Fritzen. Os meses críticos foram março e maio de 2000, nos quais ocorreram oito mortes e oito abandonos. Pode-se verificar que as colônias mantidas nas colméias Guiliani e Nogueira-Neto apresentaram uma maior uniformidade no peso. Portanto, pode-se concluir que os modelos de colméias Guiliani e Nogueira-Neto seriam os mais recomendados para a região de Maringá, Estado do Paraná.This research was carried out to evaluate the performance of stingless bees' colonies, Tetragonisca angustula Latreille, 1811 (Hymenoptera, Meliponinae, in Maringá region in the south of Brazil. Twenty colonies were settled in the following types of hives: Fritzen, Guiliani, Nogueira-Neto, and Antonio Carlos Farias (ACF, with five replications each type. The experimental season was from December, 1999 to December 2000. Monthly, the hives were weighed in order to get the colony weight. Data were analyzed statistically using the month as co variable and Scheffes’s test to compare the means. The colonies settled in

  3. X-Ray diffraction technique applied to study of residual stresses after welding of duplex stainless steel plates

    International Nuclear Information System (INIS)

    Monin, Vladimir Ivanovitch; Assis, Joaquim Teixeira de; Lopes, Ricardo Tadeu; Turibus, Sergio Noleto; Payao Filho, Joao C.

    2014-01-01

    Duplex stainless steel is an example of composite material with approximately equal amounts of austenite and ferrite phases. Difference of physical and mechanical properties of component is additional factor that contributes appearance of residual stresses after welding of duplex steel plates. Measurements of stress distributions in weld region were made by X-ray diffraction method both in ferrite and austenite phases. Duplex Steel plates were joined by GTAW (Gas Tungsten Arc Welding) technology. There were studied longitudinal and transverse stress components in welded butt joint, in heat affected zone (HAZ) and in points of base metal 10 mm from the weld. Residual stresses measured in duplex steel plates jointed by welding are caused by temperature gradients between weld zone and base metal and by difference of thermal expansion coefficients of ferrite and austenite phases. Proposed analytical model allows evaluating of residual stress distribution over the cross section in the weld region. (author)

  4. The fatigue behavior of X 6 CrNi 18 11 under sodium corrosion conditions

    International Nuclear Information System (INIS)

    Huthmann, H.; Menken, G.; Husslage, W.

    1977-01-01

    To carry out fatigue tests in sodium the experience gained in an ongoing program on irradiation effects was used for the definition of the test procedure and sample conditions, i.e. strain controlled experiments with an hour glass sample and axial strain measurement. In order to allow sodium corrosion to take place during the test, the samples were welded into a bellow and connected to a dynamic sodium loop. Due to the restricted test capacities, INTERATOM and the Metaalinstituut TNO (MI-TNO) pursued in a combined experimental program two different concepts with regard to the corrosion conditions. INTERATOM tested the samples during exposure in flowing sodium within a nonisothermal loop. The MI-TNO tested the samples after a precorrosion in a nonisothermal sodium loop. During the test at TNO the bellow-sealed samples were surrounded by static sodium

  5. The fatigue behavior of X 6 CrNi 18 11 under sodium corrosion conditions

    Energy Technology Data Exchange (ETDEWEB)

    Huthmann, H; Menken, G [INTERATOM, Bergisch Gladbach (Germany); Husslage, W [TNO, Apeldoorn (Netherlands)

    1977-07-01

    To carry out fatigue tests in sodium the experience gained in an ongoing program on irradiation effects was used for the definition of the test procedure and sample conditions, i.e. strain controlled experiments with an hour glass sample and axial strain measurement. In order to allow sodium corrosion to take place during the test, the samples were welded into a bellow and connected to a dynamic sodium loop. Due to the restricted test capacities, INTERATOM and the Metaalinstituut TNO (MI-TNO) pursued in a combined experimental program two different concepts with regard to the corrosion conditions. INTERATOM tested the samples during exposure in flowing sodium within a nonisothermal loop. The MI-TNO tested the samples after a precorrosion in a nonisothermal sodium loop. During the test at TNO the bellow-sealed samples were surrounded by static sodium.

  6. Moessbauer spectroscopic study of rust formed on a weathering steel and a mild steel exposed for a long term in an industrial environment

    International Nuclear Information System (INIS)

    Kamimura, Takayuki; Nasu, Saburo; Tazaki, Takashi; Kuzushita, Kaori; Morimoto, Shotaro

    2002-01-01

    The rusts formed on mild steel (15-year exposure) and weathering steel (32-year exposure) exposed to an industrial environment have been characterized by means of X-ray diffraction technique and 57 Fe Moessbauer spectroscopy. By using an X-ray diffraction method, it is suggested that the rusts formed on both steels consist of the crystalline α-FeOOH, γ-FeOOH and an X-ray amorphous phase, which gives no peak to X-ray diffraction pattern. The amount of the X-ray amorphous phase exceeds 50% of the total amount of the rust. The 57 Fe Moessbauer spectra observed at 10K indicate that the rust contains only α-FeOOH, γ-FeOOH and Fe 3-δ O 4 (γ-Fe 2 O 3 ) for mild steel, and only α-FeOOH and γ-FeOOH for weathering steel. The X-ray amorphous substance in the rust payer formed on mild steel possesses the structures of mainly α-FeOOH showing superparamagnetism owing to its small particle size, and Fe 3-δ O 4 (γ-Fe 2 O 3 ). They are contained both in the inner rust layer and in the outer rust layer. The X-ray amorphous phase in the rust layer formed on weathering steel is mainly α-FeOOH. (author)

  7. Microstructure of the Transitional Area of the Connection of a High-temperature Ni-based Brazing Alloy and Stainless Steel AISI 321 (X6CrNiTi 18–10

    Directory of Open Access Journals (Sweden)

    R. Augustin

    2010-01-01

    Full Text Available This paper presents a detailed examination of the structure of the transitional area between a brazing alloy and the parent material, the dimensions of the diffusion zones that are created, and the influence on them of a change in the brazing parameters. Connections between Ni-based brazing alloys (NI 102 with a small content of B and AISI 321 stainless steel (X6CrNiTi 18–10 were created in a vacuum (10−2 Pa at various brazing temperatures and for various holding times at the brazing temperature. Various specimens were tested. First, the brazing alloys were wetted and the dependence of the wetting on the brazing parameters was assessed. Then a chemical microanalysis was made of the interface between the brazing alloy and the parent material. The individual diffusion zones were identified on pictures from a light microscope and REM, and their dimensions, together with their dependence on the brazing parameters, were determined.

  8. Failure analysis of natural gas buried X65 steel pipeline under deflection load using finite element method

    International Nuclear Information System (INIS)

    Liu, P.F.; Zheng, J.Y.; Zhang, B.J.; Shi, P.

    2010-01-01

    A 3D parametric finite element model of the pipeline and soil is established using finite element method to perform the failure analysis of natural gas buried X65 steel pipeline under deflection load. The pipeline is assumed to be loaded in a parabolic deflection displacement along the axial direction. Based on the true stress-strain constitutive relationship of X65 steel, the elastic-plastic finite element analysis employs the arc-length algorithm and non-linear stabilization algorithm respectively to simulate the strain softening properties of pipeline after plastic collapse. Besides, effects of the soil types and model sizes on the maximum deflection displacement of pipeline are investigated. The proposed finite element method serves as a base available for the safety design and evaluation as well as engineering acceptance criterion for the failure of pipeline due to deflection.

  9. SCC growth behavior of cast stainless steels in high-temperature water. Influences of corrosion potential, steel type, thermal aging and cold-work

    International Nuclear Information System (INIS)

    Yamada, Takuyo; Terachi, Takumi; Miyamoto, Tomoki; Arioka, Koji

    2011-01-01

    Recent studies on crack growth rate (CGR) measurement in oxygenated high-temperature pure water conditions, such as normal water chemistry (NWC) in BWRs, using compact tension (CT) type specimens have shown that stainless steel weld metal are susceptible to stress corrosion cracking (SCC). On the other hand, the authors reported that no significant SCC growth was observed on stainless steel weld metals in PWR primary water at temperatures from 250degC to 340degC. Cast austenitic stainless steels are widely used in light water reactors, and there is a similarity between welded and cast stainless steels in terms of the microstructure of the ferrite/austenite duplex structure. However, there are a few reports giving CGR data on cast stainless steels in the BWRs and PWRs. The principal purpose of this study was to examine the SCC growth behavior of cast stainless steels in simulated PWR primary water. A second objective was to examine the effects on SCC growth in hydrogenated and oxygenated water environments at 320degC of: (1) corrosion potential; (2) steels type (Mo in alloy); (3) thermal-aging (up to 400degC x 40 kh); and (4) cold-working (10%). The results were as follows: (1) No significant SCC growth was observed on all types of cast stainless steels: aged (400degC x 40 kh) of SCS14A and SCS13A and 10% cold-working, in hydrogenated (low-potential) water at 320degC. (2) Aging at 400degC x 40 kh SCS14A (10%CW) markedly accelerated the SCC growth of cast material in high-potential water at 320degC, but no significant SCC growth was observed in the hydrogenated water, even after long-term thermal aging (400degC x 40 kh). (3) Thus, cast stainless steels have excellent SCC resistance in PWR primary water. (4) On the other hand, significant SCC growth was observed on all types of cast stainless steels: 10%CW SCS14A and SCS13A, in 8 ppm-oxygenated (high-potential) water at 320degC. (5) No large difference in SCC growth was observed between SCS14A (Mo) and SCS13A. (6) No

  10. In-service thermal ageing of martensitic stainless steels

    International Nuclear Information System (INIS)

    Tampigny, R.; Molinie, E.; Foct, F.; Dignocourt, P.

    2011-01-01

    Martensitic stainless steels are largely used in Nuclear Power Plants (NPPs) mainly as valve stems, bolts or nuts due to their high mechanical properties and their good resistance to corrosion in primary water. At the end of the eighties, research studies have demonstrated a thermal ageing irreversible embrittlement due to the precipitation of a chromium-rich phase for X6 CrNiCu 17-04, X6 CrNiMo 16.04 and X12 Cr 13 martensitic stainless steels and a semi-empirical modeling has been proposed. Numerous metallurgical examinations have been performed in hot laboratories to consolidate the good correlation between in-service experience and the modeling developed by EDF RD. According to the feedback analysis, thermal ageing embrittlement can appear at different in-service temperatures or do not appear in relation with chemical composition of martensitic stainless steels and end of manufacturing heat treatments associated. A new campaign of metallurgical examinations has been proposed to consolidate previous studies and to contribute to maintenance policy for the next ten years after the third decennial outages for 900 MWe NPP. Influence of real in-service temperatures and end of manufacturing heat treatments have been examined to understand reasons why in some cases thermal ageing embrittlement does not occur or occur with a lowest intensity. These new results have contributed to reinforce EDF RD modeling validity and technical specifications defined in RCC-M for new valve stems, bolts or nuts. (authors)

  11. The influence of heat treatment and process parameters optimization on hardness and corrosion properties of laser alloyed X12CrNiMo steel

    CSIR Research Space (South Africa)

    Popoola, API

    2016-10-01

    Full Text Available Martensitic stainless steels are used in the production of steam turbine blades but their application is limited due to low hardness and poor corrosion resistance. Laser surface alloying and heat treatment of X12CrNiMo Martensitic stainless steel...

  12. High energy x-ray synchrotron radiation analysis of residual stress distribution of shot-peened steels

    International Nuclear Information System (INIS)

    Tanaka, Keisuke; Akiniwa, Yoshiaki; Kimachi, Hirohisa; Suzuki, Kenji; Yanase, Etsuya; Nishio, Kouji; Kusumi, Yukihiro

    2001-01-01

    A high energy X-ray beam from synchrotron radiation source SPring-8 was used to determine the residual stress distribution beneath the shot-peened surface of carbon steel plates. By using the monochromatic X-ray beam with an energy of 72 keV, the relation between 2θ and sin 2 ψ was obtained by the side-inclination method upto sin 2 ψ = 0.9. The distribution of the residual stress was determined from the non-linearity of the relation between 2θ and sin 2 ψ. (author)

  13. Comparative Study of API 5L X60 and ASTM 572 Gr50 Steel Exposed to Crude Oil and Seawater

    Directory of Open Access Journals (Sweden)

    Marcy Viviana Chiquillo Márquez

    2018-04-01

    Full Text Available In the petroleum industry, the biphasic conditions in storage and separation tanks allow that the material to remain exposed to two different environments, causing its deterioration. In this article, an evaluation is made of the corrosive behavior and Vickers microhardness (HV of two high strength low alloy (HSLA steels and how their surfaces are characterized. The ASTM 572 Gr50 steel showed a lower corrosion rate in all systems after being immersed for 720 and 1440 hours. Characterizing the surface by means of Scanning Electron Microscopy (SEM showed uniform and localized corrosion for the both steels, and revealed that the ASTM 572 Gr50 steel shows pitting corrosion in crude oil systems. The electrochemical results revealed that the corrosion potential of API X60 steel was more negative; however the ASTM 572 Gr50 steel had a higher current density and a lower polarization resistance when immersed in an oil/seawater mixture. It also observed that, after being immersed in the corrosive fluids, the microstructures of the steels were not modified and variations in their microhardness (HV were minute.

  14. SAE 1045 steel/WC-Co/Ni-Cu-Ni/SAE 1045 steel joints prepared by dynamic diffusion bonding: Microelectrochemical studies in 0.6 M NaCl solution

    International Nuclear Information System (INIS)

    Andreatta, Francesco; Matesanz, Laura; Akita, Adriano H.; Paussa, Luca; Fedrizzi, Lorenzo; Fugivara, Cecilio S.; Gomez de Salazar, Jose M.; Benedetti, Assis V.

    2009-01-01

    Corrosion of SAE 1045 steel/WC-Co/Ni-Cu-Ni/SAE 1045 steel interfaces was investigated in 0.6 M NaCl solution using an electrochemical microcell, which enables local electrochemical characterization at the micrometer scale. Two pieces of steel, one with a WC-Co coating covered with Ni (12 μm) and Cu (5 μm) layers, and the other with a Ni (15 μm) layer, were welded by dynamic diffusion bonding. A WC-Co coating was applied to the steel by the high velocity oxygen-fuel process, and Ni-Cu and Ni layers by electroplating. Polarization curves were recorded using an electrochemical microcell. Different regions of welded samples were investigated, including steel, cermet coating, and steel/cermet and steel/Ni-Cu-Ni/cermet interfaces. Optical and electronic microscopes were employed to study the corroded regions. Potentiodynamic polarization curves obtained using the microcell revealed that the base metal was more susceptible to corrosion than the cermet. In addition, cermet steel/cermet and steel/Ni-Cu-Ni/cermet joints exhibited different breakdown potentials. Steel was strongly corroded in the regions adjacent to the interfaces, while the cermet was less corroded. Iron oxides/hydroxides and chloride salts were the main corrosion products of steel. After removal of the superficial layer of corrosion products, iron oxides were mainly observed. Chloride ions were detected mainly on a copper-enriched layer placed between two Ni-enriched layers.

  15. Comportamiento parabólico del crecimiento de capas boradas en los aceros Y8A y X12M // Parabolic behavior of boriding layers growth in Y8A and X12M steels

    Directory of Open Access Journals (Sweden)

    C. Figueroa Hernández

    1999-01-01

    Full Text Available Se determina la influencia que tienen los principales parámetros tecnológicos del borado en el crecimiento de las capas y secorrobora el cumplimiento de la ley parabólica para predecir este comportamiento en los aceros Y8A y X12M.El proceso de borado se aplica en una mezcla de carburo de silicio y bórax (70 y 30 % a la temperatura de 850, 900 y 950 oCdurante un tiempo de 2, 4 y 6 horas. Como variable dependiente se seleccionó la profundidad del recubrimiento, a partir de lacual se obtuvieron los coeficientes del crecimiento parabólico y la energía de activación en función de la temperatura, el tiempodel proceso y el tipo de acero.La caracterización metalográfica reveló la presencia de la fase Fe2BPalabras claves: Borado, recubrimiento superf icial , t ecnología de recubrimiento.__________________________________________________________________________AbstractIt was determined the influence of the main technological parameters of the boriding process, and a mathematical model thatallows to predict this conduct on the steels Y8A and X12M steels was obtained.The boriding process is applied in a mixture of silicon carbide and borax (70 and 30% at 850, 900 and 950 oC temperatureduring a period of time 2, 4 and 6 hours. As an independent variable the depth of the coat was selected.It was obtained the parabolic growth coefficients, and the activation energy according to temperature, time and the chemicalcomposition of steel.Metallografic analysis reveals the presence of Fe2B phase.Key words: Boriding process, superf icial coat , coat technology.

  16. Initiation and growth of thermal fatigue crack networks in an AISI 304 L type austenitic stainless steel (X2 CrNi18-09)

    International Nuclear Information System (INIS)

    Maillot, V.

    2004-01-01

    We studied the behaviour of a 304 L type austenitic stainless steel submitted to thermal fatigue. Using the SPLASH equipment of CEA/SRMA we tested parallelepipedal specimens on two sides: the specimens are continuously heated by Joule effect, while two opposites faces are cyclically. cooled by a mixed spray of distilled water and compressed air. This device allows the reproduction and the study of crack networks similar to those observed in nuclear power plants, on the inner side of circuits fatigued by mixed pressurized water flows at different temperatures. The crack initiation and the network constitution at the surface were observed under different thermal conditions (Tmax = 320 deg C, ΔT between 125 and 200 deg C). The experiment produced a stress gradient in the specimen, and due to this gradient, the in-depth growth of the cracks finally stopped. The obtained crack networks were studied quantitatively by image analysis, and different parameters were studied: at the surface during the cycling, and post mortem by step-by-step layer removal by grinding. The maximal depth obtained experimentally, 2.5 mm, is relatively coherent with the finite element modelling of the SPLASH test, in which compressive stresses appear at a depth of 2 mm. Some of the crack networks obtained by thermal fatigue were also tested in isothermal fatigue crack growth under 4-point bending, at imposed load. The mechanisms of the crack selection, and the appearance of the dominating crack are described. Compared to the propagation of a single crack, the crack networks delay the propagation, depending on the severity of the crack competition for domination. The dominating crack can be at the network periphery, in that case it is not as shielded by its neighbours as a crack located in the center of the network. It can also be a straight crack surrounded by more sinuous neighbours. Indeed, on sinuous cracks, the loading is not the same all along the crack path, leading to some morphological

  17. Fragmentation of armor piercing steel projectiles upon oblique perforation of steel plates

    Directory of Open Access Journals (Sweden)

    Aizik F.

    2012-08-01

    Full Text Available In this study, a constitutive strength and failure model for a steel core of a14.5 mm API projectile was developed. Dynamic response of a projectile steel core was described by the Johnson-Cook constitutive model combined with principal tensile stress spall model. In order to obtain the parameters required for numerical description of projectile core material behavior, a series of planar impact experiments was done. The parameters of the Johnson-Cook constitutive model were extracted by matching simulated and experimental velocity profiles of planar impact. A series of oblique ballistic experiments with x-ray monitoring was carried out to study the effect of obliquity angle and armor steel plate thickness on shattering behavior of the 14.5 mm API projectile. According to analysis of x-ray images the fragmentation level increases with both steel plate thickness and angle of inclination. The numerical modeling of the ballistic experiments was done using commercial finite element code, LS-DYNA. Dynamic response of high hardness (HH armor steel was described using a modified Johnson-Cook strength and failure model. A series of simulations with various values of maximal principal tensile stress was run in order to capture the overall fracture behavior of the projectile’s core. Reasonable agreement between simulated and x-ray failure pattern of projectile core has been observed.

  18. Mechanical and environmental effects on stress corrosion cracking of low carbon pipeline steel in a soil solution

    International Nuclear Information System (INIS)

    Contreras, A.; Hernández, S.L.; Orozco-Cruz, R.; Galvan-Martínez, R.

    2012-01-01

    Highlights: ► Mechanical and environmental effects on SCC of X52 steel were investigated. ► Slow strain rate tests (SSRT) were performed in a soil solution (NS4). ► Different levels of polarization potentials were applied to mitigating SCC. ► SSRT results indicate that X52 pipeline steel was susceptible to SCC. ► SCC susceptibility increase as the yielding and ultimate tensile stress increase. -- Abstract: Mechanical and environmental effects on stress corrosion cracking (SCC) susceptibility of X52 pipeline steel were investigated using slow strain rate tests (SSRT) performed in a glass autoclave containing a soil solution at strain rate of 1 × 10 −6 in./s at room temperature. Polarization potentials of −100, −200 and −400 mV referred to open circuit potential (OCP) was applied in order to establish the effectiveness of cathodic protection in mitigating SCC of X52 pipeline steel. Electrochemical impedance spectroscopy (EIS) tests and scanning electron microscopy (SEM) observations were done in order to analyze the SCC process. SSRT results indicate that X52 pipeline steel was susceptible to SCC. Susceptibility to SCC increase as the yielding stress (YS) and ultimate tensile stress (UTS) increase. The EIS results showed that the highest corrosion of the steel sample was obtained when the highest cathodic over potential was applied. SEM observations of these specimens showed a brittle type of fracture with transgranular appearance. The failure and SCC of X52 steel in soil solution was explained by hydrogen mechanism.

  19. Plasma nitriding of CA-6NM steel: effect of H2 + N2 gas mixtures in nitride layer formation for low N2 contents at 500 ºC

    Directory of Open Access Journals (Sweden)

    Angela Nardelli Allenstein

    2010-12-01

    Full Text Available This work aims to characterize the phases, thickness, hardness and hardness profiles of the nitride layers formed on the CA-6NM martensitic stainless steel which was plasma nitrided in gas mixtures containing different nitrogen amounts. Nitriding was performed at 500 ºC temperature, and 532 Pa (4 Torr pressure, for gas mixtures of 5% N2 + 95% H2, 10% N2 + 90% H2, and 20% N2 + 80% H2, and 2 hours nitriding time. A 6 hours nitriding time condition for gas mixture of 5% N2 + 95% H2 was also studied. Nitrided samples results were compared with non-nitrided condition. Thickness and microstructure of the nitrided layers were characterized by optical microscopy (OM, using Villela and Nital etchants, and the phases were identified by X-ray diffraction. Hardness profiles and hardness measured on surface steel were determined using Vickers hardness and nanoindentation tester, respectively. It was verified that nitrided layer produced in CA-6NM martensitc stainless steel is constituted of compound layer, being that formation of the diffusion zone was not observed for the studied conditions. The higher the nitrogen amounts in gas mixture the higher is the thickness of the nitrided layer and the probability to form different nitride phases, in the case γ'-Fe4N, ε-Fe2-3N and CrN phases. Intrinsic hardness of the nitrided layers produced in the CA-6NM stainless steel is about 12-14 GPa (~1200-1400 HV.

  20. Gradient microstructure and microhardness in a nitrided 18CrNiMo7-6 gear steel

    Science.gov (United States)

    Yang, R.; Wu, G. L.; Zhang, X.; Fu, W. T.; Huang, X.

    2017-07-01

    A commercial gear steel (18CrNiMo7-6) containing a tempered martensite structure was nitrided using a pressurized gas nitriding process under a pressure of 5 atm at 530 °C for 5 hours. The mechanical properties and microstructure of the nitrided sample were characterized by Vickers hardness measurements, X-ray diffraction, and backscatter electron imaging in a scanning electron microscope. A micro-hardness gradient was identified over a distance of 500 μm with hardness values of 900 HV at the top surface and 300 HV in the core. This micro-hardness gradient corresponds to a gradient in the microstructure that changes from a nitride compound layer at the top surface (∼ 20 μm thick) to a diffusion zone with a decreasing nitrogen concentration and precipitate density with distance from the surface, finally reaching the core matrix layer with a recovered martensite structure.

  1. Examination of the X-ray piping diagnostic system using EGS4 (measuring the thickness of a steel pipe with rust)

    International Nuclear Information System (INIS)

    Kajiwara, G.

    2001-01-01

    In a series of papers entitled 'Examination of the X-ray piping diagnostic system using EGS4' presented the proceedings of the EGS4 users' meetings, I discussed the possibility of measuring the thickness of piping walls with rust. In the present paper, I describe, based on our earlier results, how the thickness of steel pipes with rust can be measured. I conducted EGS4 simulation to measure the thickness of a combination of steel and rust and made an energy absorption diagram for this combination. The equivalent thickness of steel was obtained through experiments and the system operation. The thickness of the steel determined by using the diagram agreed well with the actual steel thickness obtained by the experiments. In the future, we will focus on how to automate this measurement procedure and how to use the same procedure to measure the thickness of pipes filled with water. (author)

  2. Ab-initio study of the structural, magnetic and electric properties of NixCr1-x x={0.125, 0.25, 0.375, 0.5, 0.625, 0.75, 0.875}

    Directory of Open Access Journals (Sweden)

    R. Golsorkhtabar

    2007-03-01

    Full Text Available  We investigated the structural, magnetic and electronic properties of NixCr1-x alloy in the range 0.125≤ x ≤0.875 by using FP-LAPW method to solve Kohn-Sham equations. In structural study, we calculated the formation energy, lattice parameter and bulk modulus for bcc and fcc structures within ferromagnetic, ferromagnetic and paramagnetic phases. Our results indicate that the system preference for alloy formation is higher in the range of x=0.625 – 0.75 compared to other studied concentrations. Moreover, by investigation of the values obtained for the lattice parameter and bulk modulus we found out that Cr-Ni bond is weaker than Ni-Ni and Cr-Cr bonds. Additionally, our magnetic results indicate that the magnetic interactions among atoms in bcc structures have probably RKKY behavior. Finally, our results show that the Ni0.75Cr0.25 alloy with fcc structure ans spin polarization of 90% has the highest magnetic and structural stability.

  3. Laves intermetallics in stainless steel-zirconium alloys

    International Nuclear Information System (INIS)

    Abraham, D.P.; McDeavitt, S.M.; Richardson, J.W. Jr.

    1997-01-01

    Laves intermetallics have a significant effect on properties of metal waste forms being developed at Argonne National Laboratory. These waste forms are stainless steel-zirconium alloys that will contain radioactive metal isotopes isolated from spent nuclear fuel by electrometallurgical treatment. The baseline waste form composition for stainless steel-clad fuels is stainless steel-15 wt.% zirconium (SS-15Zr). This article presents results of neutron diffraction measurements, heat-treatment studies and mechanical testing on SS-15Zr alloys. The Laves intermetallics in these alloys, labeled Zr(Fe,Cr,Ni) 2+x , have both C36 and C15 crystal structures. A fraction of these intermetallics transform into (Fe,Cr,Ni) 23 Zr 6 during high-temperature annealing; the authors have proposed a mechanism for this transformation. The SS-15Zr alloys show virtually no elongation in uniaxial tension, but exhibit good strength and ductility in compression tests. This article also presents neutron diffraction and microstructural data for a stainless steel-42 wt.% zirconium (SS-42Zr) alloy

  4. Evolution of microstructure in 100Cr6 steel after cooling from a thixoforming temperature to bainitic transformation ranges

    Energy Technology Data Exchange (ETDEWEB)

    Rogal, Łukasz, E-mail: l.rogal@imim.pl [Institute of Metallurgy and Materials Science, Polish Academy of Sciences, 25 Reymonta Street, 30-059 Krakow (Poland); Korpala, Grzegorz [Institut für Metallformung, TU Bergakademie Freiberg, 4 Bernhard-von-Cotta-Straße, 09596 Freiberg (Germany); Dutkiewicz, Jan [Institute of Metallurgy and Materials Science, Polish Academy of Sciences, 25 Reymonta Street, 30-059 Krakow (Poland)

    2015-01-29

    A new concept for the isothermal heat treatment of thixo-elements, consisting of controlled cooling from a semi-solid metal processing (SSM) range, was proposed. 100Cr6 steel (0.97% C, 1.4% Cr, 0.4% Si, 0.4% Mn bal. Fe) after forging was used as the starting material. The DSC analysis was used to determine the liquid phase fraction vs temperature in the solidus–liquidus range. The temperatures and kinetics of bainite transformation after cooling the steel in the semi-solid state were calculated based on the Chester and Bhadeshia models. The steel was heated up to 1425 °C in order to obtain about 25% of the liquid fraction. Then it was cooled in oil at three different temperatures: 135 °C, 235 °C and 335 °C, at which the samples were held for 5 h. The microstructure of the samples annealed at 135 °C consisted of globular grains (the average size of 323 µm), where coarse needles of martensite were observed. They were surrounded by an eutectic mixture of chemical composition different from that of the globular grains. The electron diffraction pattern (SAEDP) showed reflections from α′-Fe and from Fe{sub 3}C carbides. The X-ray diffraction confirmed the presence of martensite, austenite and carbides to the amount of 74.5%, 22% and 3.5% respectively. The average hardness of samples was 735HV{sub 10}, while the compression strength attained 3810 MPa at the plastic strain of 8.6%. The samples cooled down to 235 °C also showed globular grains surrounded by the eutectic mixture. The TEM studies allowed researchers to identify lower bainite with a plate thickness of about 500 nm (SAEDP from that area showed reflections from α-Fe and Fe{sub 3}C carbides). X-ray diffraction confirmed the presence of 90% ferrite, 6% austenite and 4% carbide. The average hardness of samples annealed at 235 °C decreased to 627HV{sub 10}, while the compression strength decreased to 3100 MPa. The plastic strain increased to 32%. The microstructure of the samples after cooling and

  5. Soberanía, representación e independencia en Caracas, 1808-1811

    Directory of Open Access Journals (Sweden)

    Inés Quintero

    2009-06-01

    Full Text Available El artículo analiza el impacto que la crisis política de la monarquía española sus- citó en Caracas, en donde tuvo lugar un intenso debate. En noviembre de 1808 se intentó erigir una junta, sin éxito. El 19 de abril de 1810 se constituyó la Junta Conservadora de los Derechos del Rey Fernando VII y, finalmente, el 5 de julio de 1811 se declaró la Independencia. El artículo analiza el contenido del debate acerca del ejercicio de la soberanía, así como la manera en que organizaron la representación política quienes tuvieron a su cargo la conducción de este pro- ceso histórico, desde el inicio del movimiento juntista hasta la declaración de la indepedencia.

  6. X-ray diffraction study of microstructural changes during fatigue damage initiation in pipe steels: Role of the initial dislocation structure

    International Nuclear Information System (INIS)

    Pinheiro, B.; Lesage, J.; Pasqualino, I.; Bemporad, E.; Benseddiq, N.

    2013-01-01

    The present work is the second part of an ongoing study of microstructural changes during fatigue damage initiation in pipe steels [B. Pinheiro et al., Mat. Sci. Eng., A 532 (2012) 158–166]. Microdeformations and residual stresses (macrostresses) are evaluated by X-ray diffraction during alternating bending fatigue tests on samples taken from an API 5L X60 grade steel pipe. Microdeformations are evaluated from the full width at half maximum (FWHM) of the diffraction peak and residual stresses are estimated from the peak shift. Here, to understand the role of the initial dislocation structure, annealed samples are considered. As previously found for as-machined samples, the evolution of microdeformations shows three regular successive stages, but now with an increase during the first stage. The amplitude of each stage is accentuated with increasing stress amplitude, while its duration is reduced. Residual stresses show a similar trend, with stages of the same durations than those observed for FWHM, respectively. Additionally, changes in density and distribution of dislocations are observed by transmission electron microscopy combined with the technique of focused ion beam. The results are very encouraging for the development of a future indicator of fatigue damage initiation for pipe steels based on microstructural changes measured by X-ray diffraction

  7. X-ray diffraction study of microstructural changes during fatigue damage initiation in pipe steels: Role of the initial dislocation structure

    Energy Technology Data Exchange (ETDEWEB)

    Pinheiro, B., E-mail: bianca@lts.coppe.ufrj.br [Laboratory of Mechanics of Lille (LML), UMR CNRS 8107, University Lille 1, Boulevard Paul Langevin, Cité Scientifique, 59655 Villeneuve d' Ascq (France); Lesage, J. [Laboratory of Mechanics of Lille (LML), UMR CNRS 8107, University Lille 1, Boulevard Paul Langevin, Cité Scientifique, 59655 Villeneuve d' Ascq (France); Pasqualino, I. [Subsea Technology Laboratory (LTS), Ocean Engineering Department, COPPE/Federal University of Rio de Janeiro, PO Box 68508, Cidade Universitária, CEP 21945-970, Rio de Janeiro/RJ (Brazil); Bemporad, E. [University of Rome “ROMA TRE”, Mechanical and Industrial Eng. Dept., Via Vasca Navale 79, 00146 Rome (Italy); Benseddiq, N. [Laboratory of Mechanics of Lille (LML), UMR CNRS 8107, University Lille 1, Boulevard Paul Langevin, Cité Scientifique, 59655 Villeneuve d' Ascq (France)

    2013-09-15

    The present work is the second part of an ongoing study of microstructural changes during fatigue damage initiation in pipe steels [B. Pinheiro et al., Mat. Sci. Eng., A 532 (2012) 158–166]. Microdeformations and residual stresses (macrostresses) are evaluated by X-ray diffraction during alternating bending fatigue tests on samples taken from an API 5L X60 grade steel pipe. Microdeformations are evaluated from the full width at half maximum (FWHM) of the diffraction peak and residual stresses are estimated from the peak shift. Here, to understand the role of the initial dislocation structure, annealed samples are considered. As previously found for as-machined samples, the evolution of microdeformations shows three regular successive stages, but now with an increase during the first stage. The amplitude of each stage is accentuated with increasing stress amplitude, while its duration is reduced. Residual stresses show a similar trend, with stages of the same durations than those observed for FWHM, respectively. Additionally, changes in density and distribution of dislocations are observed by transmission electron microscopy combined with the technique of focused ion beam. The results are very encouraging for the development of a future indicator of fatigue damage initiation for pipe steels based on microstructural changes measured by X-ray diffraction.

  8. The procurement and testing of the stainless steel in-vessel panels of the Wendelstein 7-X Stellarator

    International Nuclear Information System (INIS)

    Peacock, A.; Girlinger, A.; Vorkoeper, A.; Boscary, J.; Greuner, H.; Hurd, F.; Mendelevitch, B.; Pirsch, H.; Stadler, R.; Zangl, G.

    2011-01-01

    320 In-vessel water cooled stainless steel panels, poloidal closure plates and pumping gap panels, covering an area of approximately 100 m 2 , are used in Wendelstein7-X to protect the plasma vessel. The panels are manufactured at Deggendorf, Germany by MAN Diesel and Turbo SE. The panels consist of a laser welded sandwich of stainless steel plates together with a labyrinth of cooling channels and have a complicated geometry to fit the plasma vessel of Wendelstein 7-X. The hydraulic and mechanical stability requirements whilst maintaining the tight tolerances for the shape of the components are very demanding. The panels are designed to operate at up to an average heat load of 100 kW/m 2 and a maximum heat load of 200 kW/m 2 with a water velocity of approximately 2 m s -1 . High heat flux testing of an un-cooled panel at a time averaged load of 200 kW/m 2 for 10 s were successfully performed to support the start up phase of Wendelstein 7-X operation. Extensive testing both during manufacture and after delivery to IPP-Garching demonstrates the suitability of the delivered panels for their purpose.

  9. Pendulum impact tests of wooden and steel highway guardrail posts

    Science.gov (United States)

    Charles J. Gatchell; Jarvis D. Michie

    1974-01-01

    Impact strength characteristics of southern pine, red oak, and steel highway guardrail posts were evaluated in destructive impact testing with a 4,000-pound pendulum at the Southwest Research Institute. Effects were recorded with high-speed motion-picture equipment. Comparisons were based on reactions to the point of major post failure. Major comparisons of 6x6-inch...

  10. The influence of biosurfactant adsorption on the physicochemical behaviour of carbon steel surfaces using contact angle measurements and X-ray photoelectron spectroscopy

    Energy Technology Data Exchange (ETDEWEB)

    Shubina, V., E-mail: varvara.shubina2014@gmail.com [LUNAM Université, IFSTTAR, MAST, SMC, F-44340 Bouguenais (France); Gaillet, L. [LUNAM Université, IFSTTAR, MAST, SMC, F-44340 Bouguenais (France); Ababou-Girard, S. [Institut de Physique de Rennes, Département Matériaux et Nanosciences, UMR 6251 CNRS, Université Rennes 1, 35000 Rennes-Cedex (France); Gaudefroy, V. [LUNAM Université, IFSTTAR, MAST, SMC, F-44340 Bouguenais (France); Chaussadent, T.; Farças, F. [Université Paris-Est, IFSTTAR, MAST, CPDM, F-77447 Marne-la-Vallée (France); Meylheuc, T. [INRA, UMR1319 Micalis, F-78352 Jouy-en-Josas (France); AgroParisTech, UMR Micalis, F-78352 Jouy-en-Josas (France); Dagbert, C. [2 Chemin de la Grand’côte, 36270 Éguzon-Chantôme (France); Creus, J. [LaSIE, UMR7356, Université de La Rochelle, Pôle Sciences et Technologie, Bâtiment Marie Curie, Avenue Michel Crépeau, 17000 La Rochelle (France)

    2015-10-01

    Highlights: • Surface modifications to carbon steel surfaces due to the adsorption of a biosurfactant derived from Pseudomonas fluorescens bacteria cells were investigated using contact angle measurements (CAM) and X-ray photoelectron spectroscopy (XPS). • CAM allowed to establish an increase of electron-donating properties of steel surface due to the biosurfactant adsorption. • XPS demonstrated that biosurfactant molecules change the stoichiometry of mixted-oxide layer and the new outer layer mostly composed of magnetite. • Thickness and density of adsorbed biosurfactants layers were highlighted using a semiquantitative approach for 3 different concentrations of biomolecules. - Abstract: We investigated modifications to carbon steel surfaces due to the adsorption of a biosurfactant derived from Pseudomonas fluorescens bacteria cells using contact angle measurements (CAM) and X-ray photoelectron spectroscopy (XPS). After conditioning carbon steel in solutions with three different concentrations of biosurfactant molecules: 0.05, 0.3 and 1 g L{sup −1}, the average thickness of the biosurfactant layer on the carbon steel specimens was 7.9 ± 0.3, 12.1 ± 0.5 and 16.4 ± 0.7 Å, respectively. The biosurfactants changed the composition of both the Fe{sup 2+} and Fe{sup 3+} mixed-oxide layer and the outer layer, mostly composed of Fe{sup 3+} associated with magnetite. Contact angle measurements indicate decreased hydrophobic properties after the carbon steel was modified by biosurfactant. It was shown that the carbon steel surface free energy depends on the biosurfactant concentration, due to an acquisition of strong electron-donating properties.

  11. The influence of biosurfactant adsorption on the physicochemical behaviour of carbon steel surfaces using contact angle measurements and X-ray photoelectron spectroscopy

    International Nuclear Information System (INIS)

    Shubina, V.; Gaillet, L.; Ababou-Girard, S.; Gaudefroy, V.; Chaussadent, T.; Farças, F.; Meylheuc, T.; Dagbert, C.; Creus, J.

    2015-01-01

    Highlights: • Surface modifications to carbon steel surfaces due to the adsorption of a biosurfactant derived from Pseudomonas fluorescens bacteria cells were investigated using contact angle measurements (CAM) and X-ray photoelectron spectroscopy (XPS). • CAM allowed to establish an increase of electron-donating properties of steel surface due to the biosurfactant adsorption. • XPS demonstrated that biosurfactant molecules change the stoichiometry of mixted-oxide layer and the new outer layer mostly composed of magnetite. • Thickness and density of adsorbed biosurfactants layers were highlighted using a semiquantitative approach for 3 different concentrations of biomolecules. - Abstract: We investigated modifications to carbon steel surfaces due to the adsorption of a biosurfactant derived from Pseudomonas fluorescens bacteria cells using contact angle measurements (CAM) and X-ray photoelectron spectroscopy (XPS). After conditioning carbon steel in solutions with three different concentrations of biosurfactant molecules: 0.05, 0.3 and 1 g L −1 , the average thickness of the biosurfactant layer on the carbon steel specimens was 7.9 ± 0.3, 12.1 ± 0.5 and 16.4 ± 0.7 Å, respectively. The biosurfactants changed the composition of both the Fe 2+ and Fe 3+ mixed-oxide layer and the outer layer, mostly composed of Fe 3+ associated with magnetite. Contact angle measurements indicate decreased hydrophobic properties after the carbon steel was modified by biosurfactant. It was shown that the carbon steel surface free energy depends on the biosurfactant concentration, due to an acquisition of strong electron-donating properties

  12. Notch aspects of RSP steel microstructure

    Directory of Open Access Journals (Sweden)

    Michal Černý

    2012-01-01

    Full Text Available For a rather long time, basic research projects have been focused on examinations of mechanical properties for Rapid Solidification Powder (RSP steels. These state-of-art steels are commonly known as “powdered steels“. In fact, they combine distinctive attributes of conventional steel alloys with unusual resistance of construction material manufactured by so called “pseudo-powdered” metallurgy.Choice of suitable materials for experimental verification was carried out based on characteristic application of so called “modern steel”. First, groups of stainless and tool steel types (steel grades ČSN 17 and 19 were selected. These provided representative specimens for the actual comparison experiment. For stainless steel type, two steel types were chosen: hardenable X47Cr14 (ČSN 17 029 stainless steel and non-hardenable X2CrNiMo18-14-3 (ČSN 17 350 steel. They are suitable e.g. for surgical tools and replacements (respectively. For tooling materials, C80U (ČSN 19 152 carbon steel and American D2 highly-alloyed steel (ČSN “equivalent” being 19 572 steel were chosen for the project. Finally, the M390 Böhler steel was chosen as representative of powdered (atomized steels. The goal of this paper is to discuss structural aspects of modern stainless and tool steel types and to compare them against the steel made by the RSP method. Based on the paper's results, impact of powdered steel structural characteristics on the resistance to crack initiation shall be evaluated.

  13. S-N Fatigue and Fatigue Crack Propagation Behaviors of X80 Steel at Room and Low Temperatures

    Science.gov (United States)

    Jung, Dae-Ho; Kwon, Jae-Ki; Woo, Nam-Sub; Kim, Young-Ju; Goto, Masahiro; Kim, Sangshik

    2014-02-01

    In the present study, the S-N fatigue and the fatigue crack propagation (FCP) behaviors of American Petroleum Institute X80 steel were examined in the different locations of the base metal (BM), weld metal (WM), and heat-affected zone (HAZ) at 298 K, 223 K, and 193 K (25 °C, -50 °C, and -80 °C). The resistance to S-N fatigue of X80 BM specimen increased greatly with decreasing temperature from 298 K to 193 K (25 °C to -80 °C) and showed a strong dependency on the flow strength (½(yield strength + tensile strength)). The FCP rates of X80 BM specimen were substantially reduced with decreasing temperature from 298 K to 223 K (25 °C to -50 °C) over the entire ∆ K regime, while further reduction in FCP rates was not significant with temperature from 223 K to 193 K (-50 °C to -80 °C). The FCP rates of the X80 BM and the WM specimens were comparable with each other, while the HAZ specimen showed slightly better FCP resistance than the BM and the WM specimens over the entire ∆K regime at 298 K (25 °C). Despite the varying microstructural characteristics of each weld location, the residual stress appeared to be a controlling factor to determine the FCP behavior. The FCP behaviors of high strength X80 steel were discussed based on the microstructural and the fractographic observations.

  14. Burnout experiments with 6 x 6, 8 x 8 and 7 x 7 rod bundle test sections using freon as model fluid

    International Nuclear Information System (INIS)

    Fulfs, H.; Katsaounis, A.; Minden, C.v.

    1976-01-01

    This paper reports on burnout experiments at staedy state condition using Freon12 as model fluid. The experiments were carried out with three test sections with 6 x 6, 8 x 8 and 7 x 7 rod bundles. The axial flux distribution of the rods is either constant or reactor like. The transformed measured points using STEVENS and BOURE scaling factors to equivalent water conditions respectively, were compared to the burnout correlation W3 using the reactor layout program DYNAMIT. The DYNAMIT code is a thermohydraulic lay-out reactor program without consideration of mixing flow between the subchannels. (orig.) [de

  15. Corrosion Cyclic Voltammetry of Two Types of Heat-Affected Zones (HAZs) of API-X100 Steel in Bicarbonate Solutions

    Science.gov (United States)

    Eliyan, Faysal Fayez; Alfantazi, Akram

    2014-12-01

    This paper examined the electrochemical corrosion behavior and corrosion products of two types of heat-affected HAZs made from API-X100 steel. Cyclic voltammetry, with different scan rates and potential ranges at 10 cycles, was applied to analyze the interdependent corrosion reactions of cathodic reduction, anodic dissolution, passivation, and transpassivation. The HAZ cooled at 60 K/s, from a peak temperature of 1470 K (1197 °C) that was held for 15 seconds, exhibited better passivation and lower cathodic activity than the HAZ cooled at 10 K/s. Increasing bicarbonate concentration, from 0.05 and 0.2 to 0.6 M, increases the anodic activity and cathodic reduction, but accordingly protects the active surfaces and enhances passivation.

  16. Long-term strength and allowable stresses of grade 10Kh9MFB and X10CrMoVNb9-1 (T91/P91) chromium heat-resistant steels

    Science.gov (United States)

    Skorobogatykh, V. N.; Danyushevskiy, I. A.; Schenkova, I. A.; Prudnikov, D. A.

    2015-04-01

    Currently, grade X10CrMoVNb9-1 (T91, P91) and 10Kh9MFB (10Kh9MFB-Sh) chromium steels are widely applied in equipment manufacturing for thermal power plants in Russia and abroad. Compilation and comparison of tensile, impact, and long-term strength tests results accumulated for many years of investigations of foreign grade X10CrMoVNb9-1, T91, P91, and domestic grade 10Kh9MFB (10Kh9MFB-Sh) steels is carried out. The property identity of metals investigated is established. High strength and plastic properties of steels, from which pipes and other products are made, for operation under creep conditions are confirmed. Design characteristics of long-term strength on the basis of tests with more than one million of hour-samples are determined ( and at temperatures of 500-650°C). The table of recommended allowable stresses for grade 10Kh9MFB, 10Kh9MFB-SH, X10CrMoVNb9-1, T91, and P91 steels is developed. The long-time properties of pipe welded joints of grade 10Kh9MFB+10Kh9MFB, 10Kh9MFB-Sh+10Kh9MFB-Sh, X10CrMoVNb9-1+X10CrMoVNb9-1, P91+P91, T91+T91, 10Kh9MFB (10Kh9MFB-Sh)+X10CrMoVNb9-1(T/P91) steels is researched. The welded joint reduction factor is experimentally determined.

  17. The effect of hot strip mill processing parameters and alloy addition on low temperature toughness of API-X70 steel

    Energy Technology Data Exchange (ETDEWEB)

    Ro, Kwang Seop; Al-Shammary, Saad; Al-Butairi, Adel A. [QA and PTS, SAUDI IRON and STEEL COMAPNY, Al-Jubail, (Saudi Arabia); Al-Hajeri, Khaled F. [Saudi Basic Industries Corporation, Jubail, (Saudi Arabia)

    2010-07-01

    The design of high strength steel grade is based on stringent specifications in terms of chemistry, mechanical properties and surface requirements. This study investigated the effect of alloy addition on low temperature toughness of API X70 pipeline steel. Seven different chemical compositions have been selected for experimental testing. Ni, Cr and Cu were added in various quantities to the tested material without deteriorating the phase transformation to acicular ferrite. A tensile test, Charpy impact test, DWTT pressed notch test and microstructural observations using optical microscope and SEM were carried out. Statistical analyses were done to identify the relationship between chemical composition and DWTT shear area. The following equation showed excellent agreement with the experimental test data: Pct Shear aero of DWTT (-10 degrees C) = 954 - 0.3*SRT + 0.5*TBT - 0.4*FRT + 0.04*CT - 306*C - 60*(Mn+Ni+Cu) + 38*(Mo+Cr) - 791*(Ti+Nb+V) - 4*MA. The results showed that it is possible to design high strength API X 70 steel grades with good DWTT toughness by using the statistical equation that was developed.

  18. INFLUENCE OF MODIFICATION ON THE STRUCTURE AND CHARACTERISTICS OF THE STAINLESS STEEL 12X18H10TL

    Directory of Open Access Journals (Sweden)

    I. V. Zemskov

    2004-01-01

    Full Text Available There are given the results of investigation of influence of modification by ferrocerium, FS30RZM30B, FSMG, modifier MN, developed in BNTU, ferromolybdenum on the structure and characteristics of the steel 12X18H10TL.

  19. Irradiation Effects at 160-240 deg C in Some Swedish Pressure Vessel Steels

    Energy Technology Data Exchange (ETDEWEB)

    Grounes, M [AB Atomenergi, Nykoeping (Sweden); Myers, H P [Chalmers Institute of Technology, Goeteborg (Sweden); Hannerz, N E [Motala Verkstads AB, Motala (Sweden)

    1967-09-15

    Tensile specimens, Charpy impact specimens and miniature impact specimens of six steels in different conditions were irradiated to 2.8 x 10{sup 18} and 5.6 x 10{sup 18} n/cm{sup 2} (> 1 MeV) at 160-240 deg C. The steels investigated were SIS 142103, 2103/R3, NO 345, Fortiweld, Fortiweld HS and OK 54 P. There is no correlation between the increase in transition temperature and initial transition temperature. However, changes in strength and ductility can be correlated to the initial yield strength. The increases in transition temperature due to strain aging and irradiation are approximately additive. The irradiation-induced changes in 2103/R3 and Fortiweld HS steels do not vary with position in the thickness of the plate. Different tempering treatments in Fortiweld HS steel do not change the extent of irradiation effects. Normal Charpy V-notch impact specimens and miniature specimens give the same irradiation-induced increase in transition temperature.

  20. Irradiation Effects at 160-240 deg C in Some Swedish Pressure Vessel Steels

    International Nuclear Information System (INIS)

    Grounes, M.; Myers, H.P.; Hannerz, N.E.

    1967-09-01

    Tensile specimens, Charpy impact specimens and miniature impact specimens of six steels in different conditions were irradiated to 2.8 x 10 18 and 5.6 x 10 18 n/cm 2 (> 1 MeV) at 160-240 deg C. The steels investigated were SIS 142103, 2103/R3, NO 345, Fortiweld, Fortiweld HS and OK 54 P. There is no correlation between the increase in transition temperature and initial transition temperature. However, changes in strength and ductility can be correlated to the initial yield strength. The increases in transition temperature due to strain aging and irradiation are approximately additive. The irradiation-induced changes in 2103/R3 and Fortiweld HS steels do not vary with position in the thickness of the plate. Different tempering treatments in Fortiweld HS steel do not change the extent of irradiation effects. Normal Charpy V-notch impact specimens and miniature specimens give the same irradiation-induced increase in transition temperature

  1. Biofouling of Cr-Nickel Spray Coated Films on Steel Surfaces

    International Nuclear Information System (INIS)

    Yoshida, Kento; Kanematsu, Hideyuki; Kuroda, Daisuke; Ikigai, Hajime; Kogo, Takeshi; Yokoyama, Seiji

    2012-01-01

    Nowadays, corrosion of metals brings us serious economic loss and it often reaches several percentage of GNP. Particularly the marine corrosion was serious and the counter measure was very hard to be established, since the number of factors is huge and complicated. One of the complicated factors in marine corrosion is biofouling. Biofouling was classified into two main categories, microfouling and macrofouling. The former is composed of biofilm formation mainly. Marine bacteria are attached to material surfaces, seeking for nutrition in oligotrophic environment and they excrete polysaccharide to form biofilm on metal surfaces. Then larger living matters are attached on the biofilms to develop biofouling on metal surfaces, which often lead loss and failures of metals in marine environments. From the viewpoint of corrosion protection and maintenance of marine structures, biofouling should be mitigated as much as possible. In this study, we applied spray coating to steels and investigated if chromium-nickel spray coating could mitigate the biofouling, being compared with the conventional aluminium-zinc spray coating in marine environments. The specimens used for this investigation are aluminium, zinc, aluminium-zinc, stacked chromium/nickel and those films were formed on carbon steel (JIS SS400). And the pores formed by spray coating were sealed by a commercial reagent for some specimens. All of those specimens were immersed into sea water located at Marina Kawage (854-3, Chisato, Tsu, Mie Prefecture) in Ise Bay for two weeks. The depth of the specimen was two meter from sea water surface and the distance was always kept constant, since they were suspended from the floating pier. The temperature in sea water changed from 10 to 15 degrees Celsius during the immersion test. The biofouling behavior was investigated by low vacuum SEM (Hitachi Miniscope TM1000) and X-ray fluorescent analysis. When the spray coated specimens with and without sealing agents were compared

  2. Susceptibility to stress corrosion in stainless steels type AISI 321 and 12X18H10T used in PWR type reactors (WWER); Susceptibilidad a la corrosion bajo esfuerzo de barras de acero inoxidable AISI 321 y 12X18H10T en ambientes utilizados en reactores VVER

    Energy Technology Data Exchange (ETDEWEB)

    Matadamas C, N

    1996-12-31

    Titanium stabilized stainless steels have been utilized in sovietic pressurized water reactors (VVER) for avoid the susceptibility to Intergranular Corrosion (IGC) present in other austenitic stainless steels. However the Intergranular Corrosion resistance of this kind of materials has been questioned because of Intergranular Stress Corrosion Cracking failures (IGSCC) have been reported. This paper study the electrochemical behavior of the AISI 321 stainless steel in a H{sub 3}BO{sub 3} Solution contaminated with chlorides and its susceptibility to Intergranular Corrosion.Electrochemical prediction diagrams of the stainless steels AISI 321 and 12X18H10T (sovietic) sensitized (600 Centigrade, 3 h.) were compared. Cylindrical and conical samples were used in Slow Strain Rate Tests (SSRT), to determine the susceptibility to Stress Corrosion Cracking (SCC) in AISI 321 and 12X18H10T stainless steels. The results obtained showed that the temperature of the solution is a very important factor to detect this susceptibility. Fractography studies on the fracture surfaces of the samples obtained in the SSRT at high temperature were realized. Corrosion velocities of both AISI 321 and 12X18H10T stainless steels were determined using conical samples in the CERT system at high temperature. E.D.A.X. analysis was employed in both AISI 321 and 12X18H10T stainless steels in order to explain the degree of sensitization. (Author).

  3. Microstructure and mechanical properties of hard zone in friction stir welded X80 pipeline steel relative to different heat input

    Energy Technology Data Exchange (ETDEWEB)

    Aydin, Hakan, E-mail: hakanay@uludag.edu.tr [Engineering and Architecture Faculty, Mechanical Engineering Department, Uludag University, 16059 Gorukle-Bursa (Turkey); Nelson, Tracy W. [Mechanical Engineering Department, Brigham Young University, 435 CTB, Provo, UT 84602 (United States)

    2013-12-01

    The study was conducted to investigate the microstructure and mechanical properties of the hard zone in friction stir welded X80 pipeline steel at different heat inputs. Microstructural analysis of the welds was carried out using optical microscopy, transmission electron microscopy, and microhardness. Heat input during friction stir welding process had a significant influence on the microstructure and mechanical properties in the hard zone along the advancing side of the weld nugget. Based on the results, the linear relationships between heat input and post-weld microstructures and mechanical properties in the hard zone of friction stir welded X80 steels were established. It can be concluded that with decrease in heat input the bainitic structure in the hard zone becomes finer and so hard zone strength increases.

  4. Microstructure and mechanical properties of hard zone in friction stir welded X80 pipeline steel relative to different heat input

    International Nuclear Information System (INIS)

    Aydin, Hakan; Nelson, Tracy W.

    2013-01-01

    The study was conducted to investigate the microstructure and mechanical properties of the hard zone in friction stir welded X80 pipeline steel at different heat inputs. Microstructural analysis of the welds was carried out using optical microscopy, transmission electron microscopy, and microhardness. Heat input during friction stir welding process had a significant influence on the microstructure and mechanical properties in the hard zone along the advancing side of the weld nugget. Based on the results, the linear relationships between heat input and post-weld microstructures and mechanical properties in the hard zone of friction stir welded X80 steels were established. It can be concluded that with decrease in heat input the bainitic structure in the hard zone becomes finer and so hard zone strength increases

  5. Characterization by X ray diffraction of deleterious phases precipitated in a super duplex stainless steel; Caracterizacao por difracao de raios X de fases deleterias precipitadas em aco inoxidavel superduplex

    Energy Technology Data Exchange (ETDEWEB)

    Pardal, Juan M.; Tavares, Sergio S. Maior; Fonseca, Maria P. Cindra; Montenegro, Talles Ribeiro, E-mail: juanpardal@vm.uff.b [Universidade Federal Fluminense (PGEMEC/UFF), Niteroi, RJ (Brazil). Programa de Pos-graduacao em Engenharia Mecanica; Dias, Antonio Jose N.; Almeida, Sergio L. de [Instituto Nacional de Tecnologia (INT), Rio de Janeiro, RJ (Brazil). Div. de Materiais Ceramicos e Metalicos. Lab. de Tecnologia de Materiais

    2010-07-01

    In this work the identification and quantification of deleterious phases in two super duplex stainless steels grade UNS S32750, with quite different grain sizes, was performed by X-ray diffraction. The materials were isothermally aged in the 800 . 950 deg C range. Direct comparison method was used to quantify the ferrite phase in each sample. The amount of deleterious phases ({sigma}, {chi} and {gamma}2) formed was calculated by the difference of the amount of ferrite phase measured in each specimen to the amount of ferrite initially measured in the un-aged steel. The results obtained give an useful contribution to the understanding of kinetics of deleterious phases precipitation in super duplex steels. (author)

  6. Effect of Ni content on stainless steel fabricated by laser melting deposition

    Science.gov (United States)

    Zhang, H.; Zhang, C. H.; Wang, Q.; Wu, C. L.; Zhang, S.; Chen, J.; Abdullah, Adil O.

    2018-05-01

    The novel stainless steel + x wt.% Ni (x = 0, 3.05, 6.10, 9.15) specimens were successfully fabricated by laser melting deposition, aiming at investigating the influence of Ni content on stainless steel structure and property. The effects of Ni content on phase compositions, microstructure, microhardness, wear and electrochemical corrosion resistance of as-deposited stainless steel were studied systematically using XRD, OM, SEM, microhardness tester, friction-wear tester and potentiodynamic polarization measurement, respectively. Experimental results showed that with the increase of Ni content, the constituent phase of the as-deposited specimen changed from ferrite phase (specimen for x = 0) to austenite phase (specimen for x = 9.15). The microstructure growth followed the principle of dendrite growth. However, the dominant microstructure varied from equiaxed dendrite to columnar dendrite with increasing Ni content. Phase transition from ferrite phase to austenite phase with the addition of Ni content resulted in the decrease of microhardness value from 643HV to 289HV. Meanwhile, the wear resistance of as-deposited specimens decreased gradually with the increasing of Ni content, which might be attributed to the fact that the wear resistance is proportional to microhardness according to Archard's law. It was noted that corrosion resistance of as-deposited stainless steel was extremely improved with the increase of Ni content. The higher Ni content specimen (specimen for x = 9.15) exhibited the best corrosion resistance among the tested specimens based on corrosion rate, which was one order of magnitude lower than that of the lower Ni content specimens (specimens for x = 0, 3.05).

  7. Performance of steel wool fiber reinforced geopolymer concrete

    Science.gov (United States)

    Faris, Meor Ahmad; Abdullah, Mohd Mustafa Al Bakri; Ismail, Khairul Nizar; Muniandy, Ratnasamy; Ariffin, Nurliayana

    2017-09-01

    In this paper, performance of geopolymer concrete was studied by mixing of Class F fly ash from Manjung power station, Lumut, Perak, Malaysia with alkaline activator which are combination of sodium hydroxide and sodium silicate. Steel wool fiber were added into the geopolymer concrete as reinforcement with different weight percentage vary from 0 % - 5 %. Chemical compositions of Malaysian fly ash was first analyzed by using X-ray fluorescence. All geopolymer concrete reinforced with steel wool fiber with different weight percentage were tested in terms of density, workability, and compression. Result shows Malaysian fly ash identified by using XRF was class F. Density of geopolymer concrete close to density of OPC which is approximately 2400 kg/m3 and the density was increase gradually with the additions of steel fiber. However, the inclusions of steel fibers also shows some reduction to the workability of geopolymer concrete. Besides, the compressive strength was increased with the increasing of fibers addition until maximum of 18.6 % improvement at 3 % of steel fibers.

  8. Monitoring of stainless-steel slag carbonation using X-ray computed microtomography.

    Science.gov (United States)

    Boone, Marijn A; Nielsen, Peter; De Kock, Tim; Boone, Matthieu N; Quaghebeur, Mieke; Cnudde, Veerle

    2014-01-01

    Steel production is one of the largest contributors to industrial CO2 emissions. This industry also generates large amounts of solid byproducts, such as slag and sludge. In this study, fine grained stainless-steel slag (SSS) is valorized to produce compacts with high compressive strength without the use of a hydraulic binder. This carbonation process is investigated on a pore-scale level to identify how the mineral phases in the SSS react with CO2, where carbonates are formed, and what the impact of these changes is on the pore network of the carbonated SSS compact. In addition to conventional research techniques, high-resolution X-ray computed tomography (HRXCT) is applied to visualize and quantify the changes in situ during the carbonation process. The results show that carbonates mainly precipitate at grain contacts and in capillary pores and this precipitation has little effect on the connectivity of the pore space. This paper also demonstrates the use of a custom-designed polymer reaction cell that allows in situ HRXCT analysis of the carbonation process. This shows the distribution and influence of water and CO2 in the pore network on the carbonate precipitation and, thus, the influence on the compressive strength development of the waste material.

  9. An X-ray diffraction study of corrosion products from low carbon steel

    International Nuclear Information System (INIS)

    Morales, A. L.

    2003-01-01

    It was found in earlier work a decrease in the corrosion rate from low carbon steel when it was subjected to the action of a combined pollutant concentration (SO 4 ''2-=10''-4 M+Cl=1.5x 10''-3 M). It was also found that large magnetic content of the rust was related to higher corrosion rates. In the present study corrosion products are further analyzed by means of X-ray diffraction to account for composition changes during the corrosion process. it is found that lepidocrocite and goethite are the dominant components for the short-term corrosion in all batches considered while for log-term corrosion lepidocrite and goethite dominates if the corrosion rates is low and magnetite dominates if the corrosion rate is high. The mechanism for decreasing the corrosion rate is related to the inhibition of magnetite production at this particular concentration. (Author) 15 refs

  10. Development of nitronic 50 fusion welding techniques for 4 K service

    International Nuclear Information System (INIS)

    Dalder, E.N.C.; Juhas, M.C.

    1981-01-01

    The Mirror Fusion Test Facility (MFTF-B) is a large magnetic fusion energy experiment in the tandem mirror configuration. The requirement that each pair of Yin-Yang magnets, one pair at each end of the experiment, not undergo excessive lateral motion during seismic events was found to require excessively thick (> 12.7 mm) walled tubing in the support-struts, which accelerated the flow of heat inward to the 4 K magnet case from the nearby 300 K wall of the rector vessel, when any of the Cr-Ni austenite stainless steels, such as Type 304 with a 300 K yield-strength (sigma y) of 307 mpa (min.) was considered. Since the cold end of the lateral restraining strut was to be at or near 4 K, the additional constraints of good austenite stability and resistance to brittle fracture at 4 K existed. After consideration of these constraints against available information on Cr-Ni and Cr-Mn-Ni-N 2 austenitic stainless steels, grade XM-19 (Fe-22 Cr-12 Ni-5 Mn-.04 C-.02 N 2 was chosen. The mechanical properties of these welds were studied

  11. Aqueous stress-corrosion cracking of high-toughness D6AC steel

    Science.gov (United States)

    Gilbreath, W. P.; Adamson, M. J.

    1976-01-01

    The crack growth behavior of D6AC steel as a function of stress intensity, stress and corrosion history, and test technique, under sustained load in filtered natural seawater, 3.3 per cent sodium chloride solution, and distilled water, was investigated. Reported investigations of D6AC were considered in terms of the present study with emphasis on thermal treatment, specimen configuration, fracture toughness, crack-growth rates, initiation period, and threshold. Both threshold and growth kinetics were found to be relatively insensitive to these test parameters. The apparent incubation period was dependent on technique, both detection sensitivity and precracking stress intensity level.

  12. Surface modification of hydroturbine steel using friction stir processing

    Science.gov (United States)

    Grewal, H. S.; Arora, H. S.; Singh, H.; Agrawal, A.

    2013-03-01

    Friction stir processing (FSP) has proved to be a viable tool for enhancing the mechanical properties of materials, however, the major focus has been upon improving the bulk properties of light metals and their alloys. Hydroturbines are susceptible to damage owing to slurry and cavitation erosion. In this study, FSP of a commonly employed hydroturbine steel, 13Cr4Ni was undertaken. Microstructural characterization of the processed steel was conducted using optical microscopy (OM), scanning electron microscopy (SEM) equipped with energy dispersive spectroscopy (EDS), X-ray diffraction (XRD) and electron back scatter diffraction (EBSD) techniques. Mechanical characterization of the steel was undertaken in terms of microhardness and resistance to cavitation erosion (CE). FSP resulted in the refinement of the microstructure with reduction in grain size by a factor of 10. EBSD results confirmed the existence of submicron and ultrafine grained microstructure. The microhardness of the steel was found to enhance by 2.6 times after processing. The processed steel also showed 2.4 times higher resistance against cavitation erosion in comparison to unprocessed steel. The primary erosion mechanism for both the steels was identical in nature, with plastic deformation responsible for the loss of material.

  13. Cold-rolled steel strip X-ray thickness gauge

    International Nuclear Information System (INIS)

    Tong Jianmin; Cong Peng; Li Litao

    2010-01-01

    This paper introduces a cold-rolled steel strip X-ray thickness gauge. This gauge uses two-detector construction including penetrating ionization chamber and measuring ionization chamber. Standard magazine box is composed of three rotating plates driving by stepper motor, including 13 pieces of standard sample to build up 154 thickness value, obtaining standard sample curve covering thickness range of 0.1 mm to 5 mm. Automation system include Siemens S7-200 PLC as key controlling unit, embedded controlling system for data acquisition and computing, and PC as man-machine interface, and employ Ethernet (TCP/IP) or RS485/232 as communication protocol. Reversing Cold mill AGC closed-loop control operation test demonstrates that the gauge can adapt to the severe production environment, operate stably and reliably, measurement precision can reached to ±0.19%, reproducibility to ±0.09%, and stability to ±0.06%, response time range from 4 ms to 200 ms and be adjustable. So it can meet the high demanding of cold-rolled plate/strip production. (authors)

  14. Analysis of Anti-Bullet Resistance of Armored Steels of Foreign Manufacture

    Directory of Open Access Journals (Sweden)

    V. N. Zuzov

    2017-01-01

    Full Text Available The paper studies penetrating armour plates from the steel alloys such as Armox 560T, Domex protect 500, Weldox 700 E, Hardox 400, and Armstal 500, which are used for armour protection. In all tests for five different thick (6 mm, 8 mm, 10 mm, 6 + 6 mm, and 8 + 8mm plates was used one of the most common bullets, i.e. a 7.62 mm "APM2" (hard steel core bullet with an impact velocity of 830 m / s and 920 m / s. The article presents the developed rational finite element models of plates and bullets, which allow us to obtain results with acceptable accuracy and minimum time of solution using the LS-DYNA solver. Predicts the rational thickness values and the steel properties to ensure protection according to the European standard EN1063 ("BR7". Also conducts analysis of influence of the friction coefficient on the results of numerical simulation.The main results of calculations include the residual velocity and kinetic energy of the bullet after penetrating and the pattern of the plate fracture mechanism (for each plate type and thickness. As a result of the studies, it was found that the monolayer 6 mm, 8 mm and 10 mm thick plates from all the investigated steel alloys do not provide a protection level of "BR7" (with an initial bullet velocity of 830 m / s and, on the other hand, the two-layer plates from the alloys Armox 560T, Domex protect 500, and Armstal 500 with a total thickness of 12 mm provide such level of protection. It was also revealed that the influence of the coefficient of friction on the resistance to the bullet penetration is very small, so friction can be neglected.At an initial velocity of 920 m / s a bullet penetrated two-layer 6x2 mm thick plates from all the steel alloys under consideration, while with a thickness of 8x2 mm the bullet could not penetrate (except the Weldox 700E alloy plate.

  15. Microstructure and Mechanical Properties of 21-6-9 Stainless Steel Electron Beam Welds

    Science.gov (United States)

    Elmer, John W.; Ellsworth, G. Fred; Florando, Jeffrey N.; Golosker, Ilya V.; Mulay, Rupalee P.

    2017-04-01

    Welds can either be stronger or weaker than the base metals that they join depending on the microstructures that form in the fusion and heat-affected zones of the weld. In this paper, weld strengthening in the fusion zone of annealed 21-6-9 stainless steel is investigated using cross-weld tensile samples, hardness testing, and microstructural characterization. Due to the stronger nature of the weld, the cross-weld tensile tests failed in the base metal and were not able to generate true fusion zone mechanical properties. Nanoindentation with a spherical indenter was instead used to predict the tensile behavior for the weld metal. Extrapolation of the nanoindentation results to higher strains was performed using the Steinberg-Guinan and Johnson-Cook strength models, and the results can be used for weld strength modeling purposes. The results illustrate how microstructural refinement and residual ferrite formation in the weld fusion zone can be an effective strengthener for 21-6-9 stainless steel.

  16. A two-stage constitutive model of X12CrMoWVNbN10-1-1 steel during elevated temperature

    Science.gov (United States)

    Zhu, Luobei; He, Jianli; Zhang, Ying

    2018-02-01

    In order to clarify the competition between work hardening (WH) caused by dislocation movements and the dynamic softening result from dynamic recovery (DRV) and dynamic recrystallization (DRX), a new two-stage flow stress model of X12CrMoWVNbN10-1-1 (X12) ferrite heat-resistant steel was established to describe the whole hot deformation behavior. And the parameters were determined by the experimental data operated on a Gleeble-3800 thermo- mechanical simulation. In this constitutive model, a single internal variable dislocation density evolution model is used to describe the influence of WH and DRV to flow stress. The DRX kinetic dynamic model can express accurately the contribution of DRX to the decline of flow stress, which was established on the Avrami equation. Furthermore, The established new model was compared with Fields-Bachofen (F-B) model and experimental data. The results indicate the new two-stage flow stress model can more accurately represent the hot deformation behavior of X12 ferrite heat-resistant steel, and the average error is only 0.0995.

  17. Corrosion Resistance and Pitting Behaviour of Low-Carbon High-Mn Steels in Chloride Solution

    Directory of Open Access Journals (Sweden)

    Grajcar A.

    2016-06-01

    Full Text Available Corrosion resistance of the X4MnSiAlNbTi27-4-2 and X6MnSiAlNbTi26-3-3 type austenitic steels, after hot deformation as well as after cold rolling, were evaluated in 3.5% NaCl solution using potentiodynamic polarization tests. A type of nonmetallic inclusions and their pitting corrosion behaviour were investigated. Additionally, the effect of cold deformation on the corrosion resistance of high-Mn steels was studied. The SEM micrographs revealed that corrosion damage formed in both investigated steels is characterized by various shapes and an irregular distribution at the metallic matrix, independently on the steel state (thermomechanically treated or cold worked. Corrosion pits are generated both in grain interiors, grain boundaries and along the deformation bands. Moreover, corrosion damage is stronger in cold deformed steels in comparison to the thermomechanically treated specimens. EDS analysis revealed that corrosion pits preferentially nucleated on MnS and AlN inclusions or complex oxysulphides. The morphology of corrosion damage in 3.5% NaCl supports the data registered in potentiodynamic tests.

  18. The procurement and testing of the stainless steel in-vessel panels of the Wendelstein 7-X Stellarator

    Energy Technology Data Exchange (ETDEWEB)

    Peacock, A., E-mail: alan.peacock@ipp.mpg.de [European Commission c/o Max-Planck-Institut fuer Plasmaphysik, EURATOM Association, 85748 Garching (Germany); Girlinger, A. [MAN Diesel and Turbo SE D-94469 Deggendorf (Germany); Vorkoeper, A. [Max-Planck-Institut fuer Plasmaphysik, EURATOM Association, 17491 Greifswald (Germany); Boscary, J.; Greuner, H. [Max-Planck-Institut fuer Plasmaphysik, EURATOM Association, 85748 Garching (Germany); Hurd, F. [European Commission c/o Max-Planck-Institut fuer Plasmaphysik, EURATOM Association, 85748 Garching (Germany); Mendelevitch, B.; Pirsch, H.; Stadler, R.; Zangl, G. [Max-Planck-Institut fuer Plasmaphysik, EURATOM Association, 85748 Garching (Germany)

    2011-10-15

    320 In-vessel water cooled stainless steel panels, poloidal closure plates and pumping gap panels, covering an area of approximately 100 m{sup 2}, are used in Wendelstein7-X to protect the plasma vessel. The panels are manufactured at Deggendorf, Germany by MAN Diesel and Turbo SE. The panels consist of a laser welded sandwich of stainless steel plates together with a labyrinth of cooling channels and have a complicated geometry to fit the plasma vessel of Wendelstein 7-X. The hydraulic and mechanical stability requirements whilst maintaining the tight tolerances for the shape of the components are very demanding. The panels are designed to operate at up to an average heat load of 100 kW/m{sup 2} and a maximum heat load of 200 kW/m{sup 2} with a water velocity of approximately 2 m s{sup -1}. High heat flux testing of an un-cooled panel at a time averaged load of 200 kW/m{sup 2} for 10 s were successfully performed to support the start up phase of Wendelstein 7-X operation. Extensive testing both during manufacture and after delivery to IPP-Garching demonstrates the suitability of the delivered panels for their purpose.

  19. An Investigation of Aging Behaviour in Microalloyed Steel (X70) UOE Pipe

    Science.gov (United States)

    Wiskel, J. B.; Ma, J.; Ivey, D. G.; Henein, H.

    Aging of microalloyed steel pipe can occur at relatively low temperatures associated with the pipe coating process and/or during long term storage or use. The aging phenomenon is primarily attributed to C diffusion to dislocations and subsequent pinning of these dislocations. Important factors in the aging process include time, temperature, chemical composition and plastic deformation (arising from the pipe forming process). The work presented in this paper uses a Box-Behnken experimental design to determine the effect of time, temperature, location in the UOE pipe (90° or 180° to the weld), position through the pipe wall thickness (ID, CL or OD) and the steel's C/Nb ratio (0.60, 1.25 and 1.80) on the change in yield strength of three (uncoated) X70 UOE pipes. Quantitative microstructure analysis is undertaken to determine the grain size and microconstituent fractions of the as-received pipe material. Quadratic equations and response surface(s) correlating the significant aging variables with changes in the longitudinal yield stress of the pipe are developed. Both through thickness position and the C/Nb ratio, followed by aging temperature, had the largest effect on the change in longitudinal yield strength.

  20. Synthesis and luminescent properties of Sr{sub 2}Gd{sub 6.8}Eu{sub 1.2}Si{sub 6(1−x)}P{sub 6x}O{sub 26} oxyapatites

    Energy Technology Data Exchange (ETDEWEB)

    Ishchenko, A.V., E-mail: a-v-i@mail.ru [Ural Federal University, 620002 Ekaterinburg (Russian Federation); Zuev, M.G. [Ural Federal University, 620002 Ekaterinburg (Russian Federation); Institute of Solid State Chemistry, Ural Branch of the Russian Academy of Sciences, 620990 Ekaterinburg (Russian Federation); Vasin, A.A. [Institute of Solid State Chemistry, Ural Branch of the Russian Academy of Sciences, 620990 Ekaterinburg (Russian Federation); Yagodin, V.V.; Viktorov, L.V.; Shulgin, B.V. [Ural Federal University, 620002 Ekaterinburg (Russian Federation)

    2016-01-15

    The solid solutions Sr{sub 2}Gd{sub 6.8}Eu{sub 1.2}Si{sub 6(1−x)}P{sub 6x}O{sub 26−δ} (where x=0–0.15 and δ is oxygen nonstoichiometry) were synthesized. The structural properties of the crystal lattice of the solid solutions and the peculiarities of Eu{sup 3+} and P{sup 5+} dopants substitution for matrix ions have been considered. The photo-, X-ray and pulsed cathode luminescence properties have been studied. It has been found that substitution of (SiO{sub 4}){sup 4−} by (PO{sub 4}){sup 3−} tetrahedron in Eu{sup 3+}-doped oxyapatites does not bring significant changes to bands structure Eu{sup 3+} in luminescence spectra under different excitation (UV, X-ray, pulse cathode beam). However, the increase of P{sup 5+} concentration in Sr{sub 2}Gd{sub 6.8}Eu{sub 1.2}Si{sub 6(1−x)}P{sub 6x}O{sub 26–δ} compounds leads to a decrease of integral intensity of Eu{sup 3+} luminescence bands due to local environment symmetry modifications and covalency degree changes. Two nonequivalent optical Eu{sup 3+} centers have been found. These compounds are of interest for efficient X-ray phosphors, display devices and LED engineering material creation. - Highlights: • The luminescence properties were studied upon UV, X-ray and pulse cathode beam. • P{sup 5+} doping of Sr{sub 2}Gd{sub 6.8}Eu{sub 1.2}Si{sub 6}O{sub 26} leads to luminescence intensity reduction. • At least two types of optical centers formed by Eu{sup 3+} ions were found. • The structural features of Sr{sub 2}Gd{sub 6.8}Eu{sub 1.2}Si{sub 6(1−x)}P{sub 6x}O{sub 26} were reported. • Partial replacement of Si by P does not change the Sr{sub 2}Gd{sub 6.8}Eu{sub 1.2}Si{sub 6}O{sub 26} structure.

  1. Precipitation behavior of carbides in high-carbon martensitic stainless steel

    Energy Technology Data Exchange (ETDEWEB)

    Zhu, Qin-tian; Li, Jing; Shi, Cheng-bin; Yu, Wen-tao; Shi, Chang-min [University of Science and Technology, Beijing (China). State Key Laboratory of Advanced Metallurgy; Li, Ji-hui [Yang Jiang Shi Ba Zi Group Co., Ltd, Guangdong (China)

    2017-01-15

    A fundamental study on the precipitation behavior of carbides was carried out. Thermo-calc software, scanning electron microscopy, electron probe microanalysis, transmission electron microscopy, X-ray diffractometry and high-temperature confocal laser scanning microscopy were used to study the precipitation and transformation behaviors of carbides. Carbide precipitation was of a specific order. Primary carbides (M7C3) tended to be generated from liquid steel when the solid fraction reached 84 mol.%. Secondary carbides (M7C3) precipitated from austenite and can hardly transformed into M23C6 carbides with decreasing temperature in air. Primary carbides hardly changed once they were generated, whereas secondary carbides were sensitive to heat treatment and thermal deformation. Carbide precipitation had a certain effect on steel-matrix phase transitions. The segregation ability of carbon in liquid steel was 4.6 times greater that of chromium. A new method for controlling primary carbides is proposed.

  2. Alfinated coating structure on HS6-5-2 (SW7M high speed steel

    Directory of Open Access Journals (Sweden)

    T. Szymczak

    2010-10-01

    Full Text Available The paper presents the results of immersion alfinated coating structure in AlSi5 silumin on HS6-5-2 (SW7M high speed steel. Alfinating bath temperature was 750 ± 5 ° C, time of sample immersion was τ = 180s. Thickness of obtained coating under specified conditions was g = 150μm. Manufactured coating consists of three layers of different construction phase. The first layer from the substrate „g1`” constructed with a AlFe phase consist of alloy additives constituents of HS6-5-2 (SW7M steel: W, Mo, V, Cr and Si. On it crystallizes the second layer „g1``” of AlFeWMoCr intermetallic phases also containing Si and small amount of V. Last, the outer layer „g2” of the coating is composed with silumin including AlFeWMoCrVSi intermetallic phases. Within all layers of the coating occurs carbides. Penetration of carbides to individual coating layers is mainly due to steel surface partial melting and crystallizing layers „g1`” and „g1``” by alfinating liquid and shifting into her of carbides as well as partial carbides rejection by crystallization front of intermetallic phases occurs in coating.

  3. Yb-fibre Laser Welding of 6 mm Duplex Stainless Steel 2205

    Science.gov (United States)

    Bolut, M.; Kong, C. Y.; Blackburn, J.; Cashell, K. A.; Hobson, P. R.

    Duplex stainless steel (DSS) is one of the materials of choice for structural and nuclear applications, having high strength and good corrosion resistance when compared with other grades of stainless steel. The welding process used to join these materials is critical as transformation of the microstructure during welding directly affects the material properties. High power laser welding has recently seen an increase in research interest as it offers both speed and flexibility. This paper presents an investigation into the important parameters affecting laser welding of DSS grade 2205, with particular focus given to the critical issue of phase transformation during welding. Bead-on-plate melt-run trials without filler material were performed on 6mm thick plates using a 5 kW Yb-fibre laser. The laser beam was characterized and a Design of Experiment approach was used to quantify the impact of the process parameters. Optical metallographic methods were used to examine the resulting microstructures.

  4. The Role of Hydrogen-Enhanced Strain-Induced Lattice Defects on Hydrogen Embrittlement Susceptibility of X80 Pipeline Steel

    Science.gov (United States)

    Hattori, M.; Suzuki, H.; Seko, Y.; Takai, K.

    2017-08-01

    Studies to date have not completely determined the factors influencing hydrogen embrittlement of ferrite/bainite X80 pipeline steel. Hydrogen embrittlement susceptibility was evaluated based on fracture strain in tensile testing. We conducted a thermal desorption analysis to measure the amount of tracer hydrogen corresponding to that of lattice defects. Hydrogen embrittlement susceptibility and the amount of tracer hydrogen significantly increased with decreasing crosshead speed. Additionally, a significant increase in the formation of hydrogen-enhanced strain-induced lattice defects was observed immediately before the final fracture. In contrast to hydrogen-free specimens, the fracture surface of the hydrogen-charged specimens exhibited shallower dimples without nuclei, such as secondary phase particles. These findings indicate that the presence of hydrogen enhanced the formation of lattice defects, particularly just prior to the occurrence of final fracture. This in turn enhanced the formation of shallower dimples, thereby potentially causing premature fracture of X80 pipeline steel at lower crosshead speeds.

  5. Determination of residual stresses in steel 20 comparison of the results obtained by the Barkhausen noise and X-ray diffraction

    International Nuclear Information System (INIS)

    Fernandez, L. M.; Herrera, V.; Suarez, J.C.; Merino, F.J.

    1997-01-01

    During a heat treatment (quenching, surface hardening, Thermochemical treatment) the metallic alloys undergo temperature variations and phase transformation. The resulting changes give rise to internal stresses in the piece. Phase transformation modifies the thermomechanical behavior of the material through the change of mechanical properties ( hardness, fatigue-behaviour, corrosion resistance, electric resistivity, etc.) The aim of this paper is residual stress measurements in specimens of steel-20 submitted to different heat treatment, by two non destructive methods: Barkhausen and X-ray diffraction. Brakhausen Effects utilizes the magnetic properties of ferromagnetic materials such as ferritic and perlitic steels and provides a practical tool for surface streets evaluation. X-ray streets analysis is based on the measurement of lattice strains in different directions of specimen The results obtained by two techniques are compared, avowing a good agreement

  6. Interaction between molten corium UO{sub 2+x}-ZrO{sub 2}-FeO{sub y} and VVER vessel steel

    Energy Technology Data Exchange (ETDEWEB)

    Bechta, S. V.; Granovsky, V. S.; Khabensky, V. B.; Krushinov, E. V.; Vitol, S. A.; Sulatsky, A. A. [Alexandrov Sci Res Technol Inst, Sosnovyi Bor (Russian Federation); Gusarov, V. V.; Almiashev, V. I. [Russian Acad Sci, Inst Silicate Chem, St Petersburg (Russian Federation); Lopukh, D. B. [SPb State Electrotech Univ LETI SPbGETU, St Petersburg (Russian Federation); Bottomley, D. [Joint Res Ctr, Inst Transurane, Karlsruhe (Germany); Fischer, M. [AREVA NP GmbH, Erlangen (Germany); Piluso, P. [CEA Saclay, DEN, DSNI, Saclay (France); Miassoedov, A.; Tromm, W. [Forschungszentrum Karlsruhe, D-76021 Karlsruhe (Germany); Altstadt, E. [Forschungszentrum Dresden Rossendorf, Dresden (Germany); Fichot, F. [CEA Cadarache, SEMCA, DPAM, IRSN, St Paul Les Durance (France); Kymalainen, O. [FORTUM Nucl Serv Ltd, Espoo (Finland)

    2010-07-01

    In case of in-vessel corium retention during a severe accident in a light water reactor, weakening of the vessel wall and deterioration of the vessel steel properties can be caused both by the melting of the steel and by its physicochemical interaction with corium. The interaction behavior has been studied in medium-scale experiments with prototypic corium. The experiments yielded data for the steel corrosion rate during interaction with UO{sub 2+x}-ZrO{sub 2}-FeO{sub y} melt in air and steam at different steel surface temperatures and heat fluxes from the corium to the steel. It has been observed that the corrosion rates in air and steam atmosphere are almost the same. Further, if the temperature at the interface increases beyond a certain level, corrosion intensifies. This is explained by the formation of liquid phases in the interaction Zone. The available experimental data have been used to develop a correlation for the corrosion rate as a function of temperature and heat flux. (authors)

  7. Effect of Deformation Parameters on Microstructure and Properties During DIFT of X70HD Pipeline Steel

    Science.gov (United States)

    Wang, Jian; Zhu, Wei; Xiao, Hong; Zhang, Liang-liang; Qin, Hao; Yu, Yue

    2018-02-01

    Grain refinement is a critical approach to improve the strength of materials without damaging the toughness. The grains of deformation-induced ferrite are considerably smaller than those of proeutectoid ferrite. Grain refinement is crucial to the application of deformation-induced ferrite. The composition of ferrite and bainite or martensite is important in controlling the performance of X70HD pipeline steel, and cooling significantly influences the control of their ratio and grain size. By analyzing the static and dynamic phase-transition points using Gleeble-3800 thermal simulator, thermal simulations were performed through two-stage deformations in the austenite zone. Ferrite transformation rules were studied with thermal simulation tests under different deformation and cooling parameters based on the actual production of cumulative deformation. The influence of deformation parameters on the microstructure transformation was analyzed. Numerous fine-grain deformation-induced ferrites were obtained by regulating various parameters, including deformation temperature, strain rate, cooling rate, final cooling temperature and other parameters. Results of metallographic observation and microtensile testing revealed that the selection of appropriate parameters can refine the grains and improve the performance of the X70HD pipeline steel.

  8. Development of Continuous Galvanization-compatible Martensitic Steel

    Energy Technology Data Exchange (ETDEWEB)

    Gong, Y. F.; Song, T. J.; Kim, Han S.; De Cooman [Pohang Univ. of Science and Technology, Pohang (Korea, Republic of); Kwak, J. H. [POSCO Gwangyang Works, Gwangyang (Korea, Republic of)

    2012-01-15

    The development of martensitic grades which can be processed in continuous galvanizing lines requires the reduction of the oxides formed on the steel during the hot dip process. This reduction mechanism was investigated in detail by means of High Resolution Transmission Electron Microscopy (HR-TEM) of cross-sectional samples. Annealing of a martensitic steel in a 10% H{sub 2} + N{sub 2} atmosphere with the dew point of -35 .deg. C resulted in the formation of a thin c-xMno.SiO{sub 2} (x>1) oxide film and amorphous a-xMnO.SiO{sub 2} oxide particles on the surface. During the hot dip galvanizing in Zn-0.13%Al, the thin c-xMnO.SiO{sub 2} (x>1) oxide films was reduced by the Al. The a-xMnO.SiO{sub 2} (x<0.9) and a-SiO{sub 2} (x>1) oxide film was also reduced and the amorphous a-xMnO.SiO{sub 2} and a-SiO{sub 2} particles were embedded in the Fe{sub 2}Al{sub 5-x}Zn{sub x} inhibition layer formed at the steel/coating interface during hot dipping. The results clearly show that Al in the liquid Zn bath can reduce the crystalline c-xMn.SiO{sub 2} (x>1) oxides but not the amorphous a-xMnO.SiO{sub 2} (x<0.9) and a-SiO{sub 2} oxides. These oxides remain embedded in the Zn layer or in the inhibition layer, making it possible to apply a Zn or Zn-alloy coating on martensitic steel by hot dipping. The hot dipping process was also found to deteriorate the mechanical properties, independently of the Zn bath composition.

  9. Quantitative analysis of inclusions in high-strength steels by x-ray computed tomography using ultra-bright synchrotron radiation

    International Nuclear Information System (INIS)

    Shiozawa, Daiki; Nakai, Yoshikazu; Morikage, Yasushi; Tanaka, Hiroshi; Okado, Hideki; Miyashita, Takuya

    2006-01-01

    The observation of internal microstructures in materials is important to elucidate the mechanisms of ultra-long life fatigue of high-strength steels, and to ensure the integrity of structures. By conventional techniques, such as laboratory X-ray and ultrasonic imaging, the size and shape of subsurface non-metallic inclusions and cracks, those are smaller than 100 μm, cannot be measured. Then, in the present study, the ultra-bright synchrotron radiation X-ray was applied to the imaging of subsurface inclusion. To obtain basic data for the measurement, the penetration depth of synchrotron radiation wave in a free-cutting steel was examined. It was found that the depths where the transmitted wave cannot be observed are 100 μm for 15 keV, 200 μm for 20 keV, 600 μm for 25 keV, and 800 μm for 30 keV. For the measurement of size and shape of inclusion, synchrotron radiation computed tomography method (SR-CT) was employed. Metallographic structures can be observed in a free-cutting steel, and the diameter of these structures is about 7 - 10 μm. They are considered to be inclusions, which mainly contain manganese sulfide (MnS) or pearlitic phase. To investigate the possibility of detection of pearlitic phase, SR-CT was applied to observe the metallographic structures in carbon steel (S35C), which contains a lot of pearlitic phase and a little inclusion. In this case, no metallographic structure was observed inside specimen. These results indicate that the microstructures those were observed by SR-CT method was inclusions, not pearlitic phase. (author)

  10. Determination of Ni and Cu content of steel and pig iron samples by Si/Li/X-ray spectrometer

    International Nuclear Information System (INIS)

    Kis-Varga, M.; Bacso, J.

    1976-01-01

    Results connected with concentration measurements of Ni and Cu in low alloy steel and pig iron samples are presented. The samples were analysed by a Si(Li) detector X-ray spectrometer developed by the authors. The characteristic X-rays of elements were excited by a 5 mCi activity ring-shaped 125 I radioisotope source which emits the K-X-rays of Te and a weak γ-line of 35 keV energy. The semiconductor detector X-ray spectrometer can be used even more advantageously for analysis of major components of metallurgical samples. The method for quantitative analysis needed only one or a small number of standards. The interelement disturbing effects were mathematically corrected with computer

  11. The Effect of Stepped Austempering on Phase Composition and Mechanical Properties of Nanostructured X37CrMoV5-1 Steel

    Directory of Open Access Journals (Sweden)

    Marciniak S.

    2015-04-01

    Full Text Available This paper presents the results of studies of X37CrMoV5-1 steel subjected to quenching processes with a one-step and a two-step isothermal annealing. The TEM observation revealed that steel after one-step treatment led is composed of carbide-free bainite with nanometric thickness of ferrite plates and of high volume fraction of retained austenite in form of thin layers or large blocks. In order to improve the strength parameters an attempt was made to reduce the austenite content by use of quenching with the two-step isothermal annealing. The temperature and time of each step were designed on the basis of dilatometric measurements. It was shown, that the two-step heat treatment led to increase of the bainitic ferrite content and resulted in improvement of steel's strength with no loss of steel ductility.

  12. Quantitative characterization of the atomic-scale structure of oxyhydroxides in rusts formed on steel surfaces

    International Nuclear Information System (INIS)

    Saito, M.; Suzuki, S.; Kimura, M.; Suzuki, T.; Kihira, H.; Waseda, Y.

    2005-01-01

    Quantitative X-ray structural analysis coupled with anomalous X-ray scattering has been used for characterizing the atomic-scale structure of rust formed on steel surfaces. Samples were prepared from rust layers formed on the surfaces of two commercial steels. X-ray scattered intensity profiles of the two samples showed that the rusts consisted mainly of two types of ferric oxyhydroxide, α-FeOOH and γ-FeOOH. The amounts of these rust components and the realistic atomic arrangements in the components were estimated by fitting both the ordinary and the environmental interference functions with a model structure calculated using the reverse Monte Carlo simulation technique. The two rust components were found to be the network structure formed by FeO 6 octahedral units, the network structure itself deviating from the ideal case. The present results also suggest that the structural analysis method using anomalous X-ray scattering and the reverse Monte Carlo technique is very successful in determining the atomic-scale structure of rusts formed on the steel surfaces

  13. Study on tempering behaviour of AISI 410 stainless steel

    International Nuclear Information System (INIS)

    Chakraborty, Gopa; Das, C.R.; Albert, S.K.; Bhaduri, A.K.; Thomas Paul, V.; Panneerselvam, G.; Dasgupta, Arup

    2015-01-01

    Martensitic stainless steels find extensive applications due to their optimum combination of strength, hardness and wear-resistance in tempered condition. However, this class of steels is susceptible to embrittlement during tempering if it is carried out in a specific temperature range resulting in significant reduction in toughness. Embrittlement of as-normalised AISI 410 martensitic stainless steel, subjected to tempering treatment in the temperature range of 673–923 K was studied using Charpy impact tests followed by metallurgical investigations using field emission scanning electron and transmission electron microscopes. Carbides precipitated during tempering were extracted by electrochemical dissolution of the matrix and identified by X-ray diffraction. Studies indicated that temper embrittlement is highest when the steel is tempered at 823 K. Mostly iron rich carbides are present in the steel subjected to tempering at low temperatures of around 723 K, whereas chromium rich carbides (M 23 C 6 ) dominate precipitation at high temperature tempering. The range 773–823 K is the transition temperature range for the precipitates, with both Fe 2 C and M 23 C 6 types of carbides coexisting in the material. The nucleation of Fe 2 C within the martensite lath, during low temperature tempering, has a definite role in the embrittlement of this steel. Embrittlement is not observed at high temperature tempering because of precipitation of M 23 C 6 carbides, instead of Fe 2 C, preferentially along the lath and prior austenite boundaries. Segregation of S and P, which is widely reported as one of the causes for temper embrittlement, could not be detected in the material even through Auger electron spectroscopy studies. - Highlights: • Tempering behaviour of AISI 410 steel is studied within 673–923 K temperature range. • Temperature regime of maximum embrittlement is identified as 773–848 K. • Results show that type of carbide precipitation varies with

  14. Stress corrosion cracking of 350 maraging steel in 3.5 Wt. % NaCl solution

    International Nuclear Information System (INIS)

    Hussain, I.; Hussain, T.; Tauqir, A.; Hashmi, F.H.; Khan, A.Q.

    1993-01-01

    Stress corrosion behavior of 350 maraging steel in 3.5 wt.% NaCl solution was investigated. The results suggest that the steel is susceptible to stress corrosion cracking as the time to failure was always considerably shorter, as compared to those in air at the same stress level. The fracture mode was nearly intergranular and occasionally transgranular. There was no definite trend for the different modes of failure. The strain rate effect was also considered and the results show that the stress corrosion cracks were absent at strain rate high than 1.97 x 10/sup -4/S/sup -1/ and lower than 1.29 x 10/sup -7/S/sup -1/. The critical strain rate range was found to be between 6.4 x 10/sup -7/ to 3.24 x10/sup -5/S /sup -1/. (author)

  15. Comparison on mechanical anisotropies of selective laser melted Ti-6Al-4V alloy and 304 stainless steel

    Energy Technology Data Exchange (ETDEWEB)

    Yu, Hanchen; Yang, Jingjing; Yin, Jie; Wang, Zemin, E-mail: zmwang@hust.edu.cn; Zeng, Xiaoyan

    2017-05-17

    Near-fully dense Ti-6Al-4V and 304 stainless steel samples have been produced applying selective laser melting (SLM) in the present work. The microstructures, textures and microhardnesses on horizontal and vertical cross sections, as well as the tensile properties of horizontally and vertically SLMed samples are investigated. It is found that the microstructures of the two SLMed alloys are mainly composed of hexagonal close-packed (HCP) martensitic phase or face-centered cubic (FCC) austenitic phase within columnar structures in Ti-6Al-4V alloy and 304 stainless steel, respectively. For both SLMed alloys, the tensile properties and microhardnesses show anisotropic though the textures are weak. Especially, the Ti-6Al-4V samples show even stronger anisotropic mechanical properties compared with 304 stainless steel. The higher length-width ratios of the columnar structures, rather than the weaker textures or the less symmetry of HCP crystal structure in SLMed Ti-6Al-4V are believed to be responsible for the stronger mechanical anisotropies. As expected, heat treatment is an effective method to eliminate columnar structures and leads to nearly isotropic mechanical properties.

  16. Improved corrosion resistance of cast carbon steel in sulphur oxides by Alonizing

    International Nuclear Information System (INIS)

    Holtzer, M.; Dzioba, Z.

    1992-01-01

    The results of studies on the Alonizing of cast steel and of testing the corrosion resistance of this cast steel in an atmosphere containing 5 to 6% SO 2 + 50% SO 3 at 853 K are described and compared with the results obtained with unalonized cast carbon steel and high-alloy 23Cr-8Ni-2Mo cast steel. The duration of the corrosion tests was 336 hours. The aluminium diffusion layer on cast carbon steel was obtained by holding the specimens in a mixture containing 99% of powered Fe-Al and 1% of NH 4 Cl at 1323 ± 20 K. The holding time was 10 and 20 hours, respectively. The aluminium layer formed on the cast carbon steel was examined by optical microscopy and an X-ray microanalysis. After Alonizing for 10 h the layer had reached a thickness of 950 μm, and contained up to 35% Al. In a mixture of sulphur oxides corrosion rate of the alonized cast carbon steel was by about 600 times lower than of the unalonized cast carbon steel, and by about 50 times lower than that of the 23Cr-8Ni-2Mo cast steel. (orig.) [de

  17. X-ray photoelectron spectroscopy and electrochemical studies of mild steel FeE500 passivation in concrete simulated water

    Science.gov (United States)

    Miserque, F.; Huet, B.; Azou, G.; Bendjaballah, D.; L'Hostis, V.

    2006-11-01

    In the context of the prediction of the long-term behaviour of reinforced concrete structures involved in the nuclear waste storage, the corrosion mechanisms of steels have to be assessed. When mild steel rebars are embedded in concrete, the chemical environment of the reinforcement is progressively modified, due to the carbonation of the concrete matrix. This modification leads to the variation of iron oxides properties formed at the steel/concrete interface, and the active corrosion can be initiated. The aim of this study is to evaluate the passivation behaviour and to provide insights into the depassivation of mild steel in concrete pore solution. In a young concrete, due to the alkalinity of the interstitial solution, steel reinforcement remains passive. Immersion tests of mild steel substrate in various alkaline solutions (from pH 13 to 10) have been performed. Due to the low thickness of the corrosion layers formed, X-ray photoelectron spectroscopy has been used to characterize them. In the passive domain, the corrosion products are similar for the various solutions. The corrosion layer is composed of a mixture of Fe3+ and Fe2+. A similar approach is used to determine the depassivation mechanism. The effect of various components such as carbonates, sulfates and silicates resulting from the dissolution of minerals of cement during the carbonation process is investigated. In addition to the surface analysis, the evolution of the electrochemical behaviour as function of the solution nature (pH) is evaluated with the help of electrochemical measurements (free corrosion potential, cyclic voltamperometry).

  18. Energy spectrum measurement of high power and high energy(6 and 9 MeV) pulsed x-ray source for industrial use

    Energy Technology Data Exchange (ETDEWEB)

    Takagi, Hiroyuki [Hitachi, Ltd. Power Systems Company, Ibaraki (Japan); Murata, Isao [Graduate School of Engineering, Osaka University, Osaka (Japan)

    2016-06-15

    Industrial X-ray CT system is normally applied to non-destructive testing (NDT) for industrial product made from metal. Furthermore there are some special CT systems, which have an ability to inspect nuclear fuel assemblies or rocket motors, using high power and high energy (more than 6 MeV) pulsed X-ray source. In these case, pulsed X-ray are produced by the electron linear accelerator, and a huge number of photons with a wide energy spectrum are produced within a very short period. Consequently, it is difficult to measure the X-ray energy spectrum for such accelerator-based X-ray sources using simple spectrometry. Due to this difficulty, unexpected images and artifacts which lead to incorrect density information and dimensions of specimens cannot be avoided in CT images. For getting highly precise CT images, it is important to know the precise energy spectrum of emitted X-rays. In order to realize it we investigated a new approach utilizing the Bayesian estimation method combined with an attenuation curve measurement using step shaped attenuation material. This method was validated by precise measurement of energy spectrum from a 1 MeV electron accelerator. In this study, to extend the applicable X-ray energy range we tried to measure energy spectra of X-ray sources from 6 and 9 MeV linear accelerators by using the recently developed method. In this study, an attenuation curves are measured by using a step-shaped attenuation materials of aluminum and steel individually, and the each X-ray spectrum is reconstructed from the measured attenuation curve by the spectrum type Bayesian estimation method. The obtained result shows good agreement with simulated spectra, and the presently developed technique is adaptable for high energy X-ray source more than 6 MeV.

  19. Cluster-enhanced X-O-2 photochemistry (X=CH3I, C3H6, C6H12, and Xe)

    NARCIS (Netherlands)

    Baklanov, A.V.; Bogdanchikov, G.A.; Vidma, K.V.; Chestakov, D.A.; Parker, D.H.

    2007-01-01

    The effect of a local environment on the photodissociation of molecular oxygen is investigated in the van der Waals complex X-O-2 (X=CH3I, C3H6, C6H12, and Xe). A single laser operating at wavelengths around 226 nm is used for both photodissociation of the van der Waals complex and simultaneous

  20. In situ 3D monitoring of corrosion on carbon steel and ferritic stainless steel embedded in cement paste

    KAUST Repository

    Itty, Pierre-Adrien

    2014-06-01

    In a X-ray microcomputed tomography study, active corrosion was induced by galvanostatically corroding steel embedded in cement paste. The results give insight into corrosion product build up, crack formation, leaching of products into the cracks and voids, and differences in morphology of corrosion attack in the case of carbon steel or stainless steel reinforcement. Carbon steel was homogeneously etched away with a homogeneous layer of corrosion products forming at the steel/cement paste interface. For ferritic stainless steel, pits were forming, concentrating the corrosion products locally, which led to more extensive damage on the cement paste cover. © 2014 Elsevier Ltd.

  1. In situ 3D monitoring of corrosion on carbon steel and ferritic stainless steel embedded in cement paste

    KAUST Repository

    Itty, Pierre-Adrien; Serdar, Marijana; Meral, Cagla; Parkinson, Dula; MacDowell, Alastair A.; Bjegović, Dubravka; Monteiro, Paulo J.M.

    2014-01-01

    In a X-ray microcomputed tomography study, active corrosion was induced by galvanostatically corroding steel embedded in cement paste. The results give insight into corrosion product build up, crack formation, leaching of products into the cracks and voids, and differences in morphology of corrosion attack in the case of carbon steel or stainless steel reinforcement. Carbon steel was homogeneously etched away with a homogeneous layer of corrosion products forming at the steel/cement paste interface. For ferritic stainless steel, pits were forming, concentrating the corrosion products locally, which led to more extensive damage on the cement paste cover. © 2014 Elsevier Ltd.

  2. Anodized Steel Electrodes for Supercapacitors.

    Science.gov (United States)

    Sagu, Jagdeep S; Wijayantha, K G Upul; Bohm, Mallika; Bohm, Siva; Kumar Rout, Tapan

    2016-03-09

    Steel was anodized in 10 M NaOH to enhance its surface texture and internal surface area for application as an electrode in supercapacitors. A mechanism was proposed for the anodization process. Field-emission gun scanning electron microscopy (FEGSEM) studies of anodized steel revealed that it contains a highly porous sponge like structure ideal for supercapacitor electrodes. X-ray photoelectron spectroscopy (XPS) measurements showed that the surface of the anodized steel was Fe2O3, whereas X-ray diffraction (XRD) measurements indicated that the bulk remained as metallic Fe. The supercapacitor performance of the anodized steel was tested in 1 M NaOH and a capacitance of 18 mF cm(-2) was obtained. Cyclic voltammetry measurements showed that there was a large psueudocapacitive contribution which was due to oxidation of Fe to Fe(OH)2 and then further oxidation to FeOOH, and the respective reduction of these species back to metallic Fe. These redox processes were found to be remarkably reversible as the electrode showed no loss in capacitance after 10000 cycles. The results demonstrate that anodization of steel is a suitable method to produce high-surface-area electrodes for supercapacitors with excellent cycling lifetime.

  3. Fatigue damage evolution of cold-worked austenitic nickel-free high-nitrogen steel X13CrMnMoN18-14-3 (1.4452)

    Energy Technology Data Exchange (ETDEWEB)

    Tikhovskiy, I.; Weiss, S.; Fischer, A. [Univ. of Duisburg-Essen, Materials Science and Engineering II, Duisburg (Germany)

    2004-07-01

    Due to the fact that the risk of Ni-allergies becomes more and more important for modern therapies, the necessity of Ni-free implant materials becomes increasingly important. Beside Co- and Ti-base alloys Ni-free high-nitrogen steels may offer an attractive alternative. The present work presents the austenitic high-nitrogen and nickel-free steel X13CrMnMoN18-14-3, (Material No.: 1.4452) after 20% cold-working. In addition this material was deformed under axial cyclic total strain controlled fatigue tests at room temperature. The development of dislocation structure due to different loading amplitudes was compared to none cyclically deformed material. The good mechanical und fatigue properties of these austenitic high-nitrogen steels as well as the better tribological, chemical and biological properties compared to CrNiMo-steels qualify these steels as a promising alternative in medical applications. (orig.)

  4. Crystallographic orientation study of silicon steels using X-ray diffraction, electrons diffraction and the Etch Pit method

    International Nuclear Information System (INIS)

    Santos, Hamilta de Oliveira

    1999-01-01

    The aim of the present study is the microstructural and crystallographic orientation of Fe-3%Si steel. The silicon steel shows good electrical properties and it is used in the nuclear and electrical power fields. The studied steel was supplied by Cia. Acos Especiais Itabira S/A - ACESITA. The material was received in the hot compressed condition, in one or two passes. The hot compressing temperatures used were 900, 1000 and 1100 deg C with soaking times ranging from 32 to 470 s. The material preferential crystallographic orientation was evaluated in every grain of the samples. The characterization techniques used were: scanning electron microscopy (SEM) using the etch pit method; X ray diffraction using the Laue back-reflection method; orientation imaging microscopy (OIM). Microstructural characterization in terms of grain size measurement and mean number of grains in the sample were also undertaken. The Laue method was found an easy technique to access crystallographic orientation of this work polycrystalline samples 2.5 mm average grain size. This was due to the inability to focus the X-rays on a single grain of the material. The scanning electron microscopy showed microcavities left by the etch pit method, which allowed the observation of the crystallographic orientation of each grain from the samples. No conclusive grain crystallographic orientation was possible to obtain by the OIM technique due to the non-existing rolling direction. A more extensive work with the OIM technique must be undertaken on the Fe-3%Si with oriented grains and non oriented grains. (author)

  5. X-ray stress measurement of ferritic steel using fourier analysis of Debye-Scherrer ring

    International Nuclear Information System (INIS)

    Fujimoto, Yohei; Sasaki, Toshihiko; Miyazaki, Toshiyuki

    2015-01-01

    In this study, X-ray stress measurements of ferritic steel based on Fourier analysis are conducted. Taira et al. developed the cosα method for X-ray stress measurements using a two-dimensional X-ray detector. Miyazaki et al. reported that the cosα method can be described more concisely by developing the Fourier series (the Fourier analysis method). The Fourier analysis method is expected to yield the stress measurement with an imperfect Debye-Scherrer ring and there is a possibility that the materials evaluation is different compared with the conventional method, that is, the sin 2 ψ method. In the Fourier analysis method, the strain measured by X-rays is developed as a Fourier series, and all the plane-stress components can be calculated from the Fourier series. In this study, the normal stress calculation was confirmed. In addition, the Fourier-analysis and cosα methods were used for X-ray stress measurements during a four-point bending test on a S45C test piece, and the effectiveness of the Fourier analysis method was confirmed. It was found that the experimental results from the Fourier analysis and cosα methods were nearly identical. In addition, the measurement accuracies of both the methods were equivalent. (author)

  6. Measurements of the residual stresses in the welded steel columns based on the x-ray diffraction method, 2

    International Nuclear Information System (INIS)

    Kaneta, Kiyoshi; Nishizawa, Hidekazu; Arashiyama, Masaki.

    1982-01-01

    In order to evaluate the applicability of two kinds of techniques of the X-ray stress analysis, namely, the standard sin 2 psi method and the newly developed phi-sin 2 psi method, bending tests have been performed. The test results have proved that the values of the stresses measured by means of the mechanical devices and of those measured by the two kinds of the X-ray techniques coincide each other. Then, these two methods have been applied to measure the surface residual stresses of the box-typed, welded steel columns and the following conclusions have been drawn. 1. The principal stress of the surface residural stresses is, in most cases, oriented to the rolled directions at the center of the steel plates, and it tends to rotate in the neighborhood of the heat affected zones. 2. Tensile residual stresses of a large magnitude have been observed in the direction parallel to the beads of the weld, and the moderate compressive residual stresses can be detected in the direction normal to the beads. (author)

  7. Dynamic impact response of high-density square honeycombs made of TRIP steel and TRIP matrix composite material

    Directory of Open Access Journals (Sweden)

    Weigelt C.

    2012-08-01

    Full Text Available Two designs of square-celled metallic honeycomb structures fabricated by a modified extrusion technology based on a powder feedstock were investigated. The strength and ductility of these cellular materials are achieved by an austenitic CrNi (AISI 304 steel matrix particle reinforced by an MgO partially-stabilized zirconia building up their cell wall microstructure. Similar to the mechanical behaviour of the bulk materials, the strengthening mechanism and the martensitic phase transformations in the cell walls are affected by the deformation temperature and the nominal strain rate. The microstructure evolution during quasi-static and dynamic impact compression up to high strain rates of 103 1/s influences the buckling and failure behaviour of the honeycomb structures. In contrast to bending-dominated quasi-isotropic networks like open-celled metal foams, axial compressive loading to the honeycomb’s channels causes membrane stretching as well as crushing of the vertical cell node elements and cell walls. The presented honeycomb materials differ geometrically in their cell wall thickness-to-cell size-ratio. Therefore, the failure behaviour is predominantly controlled by global buckling and torsional-flexural buckling, respectively, accompanied by plastic matrix flow and strengthening of the cell wall microstructure.

  8. X pinch a point x-ray source

    International Nuclear Information System (INIS)

    Garg, A.B.; Rout, R.K.; Shyam, A.; Srinivasan, M.

    1993-01-01

    X ray emission from an X pinch, a point x-ray source has been studied using a pin-hole camera by a 30 kV, 7.2 μ F capacitor bank. The wires of different material like W, Mo, Cu, S.S.(stainless steel) and Ti were used. Molybdenum pinch gives the most intense x-rays and stainless steel gives the minimum intensity x-rays for same bank energy (∼ 3.2 kJ). Point x-ray source of size (≤ 0.5 mm) was observed using pin hole camera. The size of the source is limited by the size of the pin hole camera. The peak current in the load is approximately 150 kA. The point x-ray source could be useful in many fields like micro lithography, medicine and to study the basic physics of high Z plasmas. (author). 4 refs., 3 figs

  9. The Mechanism of High Ductility for Novel High-Carbon Quenching-Partitioning-Tempering Martensitic Steel

    Science.gov (United States)

    Qin, Shengwei; Liu, Yu; Hao, Qingguo; Wang, Ying; Chen, Nailu; Zuo, Xunwei; Rong, Yonghua

    2015-09-01

    In this article, a novel quenching-partitioning-tempering (Q-P-T) process was applied to treat Fe-0.6C-1.5Mn-1.5Si-0.6Cr-0.05Nb hot-rolled high-carbon steel and the microstructures including retained austenite fraction and the average dislocation densities in both martensite and retained austenite were characterized by X-ray diffraction, scanning electron microscopy, and transmission electron microscopy, respectively. The Q-P-T steel exhibits high strength (1950 MPa) and elongation (12.4 pct). Comparing with the steel treated by traditional quenching and tempering (Q&T) process, the mechanism of high ductility for high-carbon Q-P-T steel is revealed as follows. Much more retained austenite existing in Q-P-T steel than in Q&T one remarkably enhances the ductility by the following two effects: the dislocation absorption by retained austenite effect and the transformation-induced plasticity effect. Besides, lower dislocation density in martensite matrix produced by Q-P-T process plays an important role in the improvement of ductility. However, some thin plates of twin-type martensite embedded in dislocation-type martensite matrix in high-carbon Q-P-T steel affect the further improvement of ductility.

  10. Mechanical Characteristics of Submerged Arc Weldment in API Gas Pipeline Steel of Grade X65

    International Nuclear Information System (INIS)

    Hashemi, S. H.; Mohammadyani, D.

    2011-01-01

    The mechanical properties of submerged arc weldment (SAW) in gas transportation pipeline steel of grade API X65 (65 ksi yield strength) were investigated. This steel is produced by thermo mechanical control rolled (TMC), and is largely used in Iran gas piping systems and networks. The results from laboratory study on three different regions; i.e. base metal (BM), fusion zone (FZ) and heat affected zone (HAZ) were used to compare weldment mechanical characteristics with those specified by API 5L (revision 2004) standard code. Different laboratory experiments were conducted on test specimens taken from 48 inch outside diameter and 14.3 mm wall thickness gas pipeline. The test results showed a gradient of microstructure and Vickers hardness data from the centerline of FZ towards the unaffected MB. Similarly, lower Charpy absorbed energy (compared to BM) was observed in the FZ impact specimens. Despite this, the API specifications were fulfilled in three tested zones, ensuring pipeline structural integrity under working conditions.

  11. Microstructural Evolution and the Precipitation Behavior in X90 Linepipe Steel During Isothermal Processing

    Science.gov (United States)

    Tian, Y.; Wang, H. T.; Wang, Z. D.; Misra, R. D. K.; Wang, G. D.

    2018-03-01

    Thermomechanical controlled processing of 560-MPa (X90) linepipe steel was simulated in the laboratory using a thermomechanical simulator to study the microstructural evolution and precipitation behavior during isothermal holding. The results indicated that martensite was obtained when the steels were isothermally held for 5 s at 700 °C. Subsequently, granular bainite and acicular ferrite transformation occurred with increased holding time. Different amount of polygonal ferrite formed after isothermally holding for 600-3600 s. Pearlite nucleated after isothermally holding for 3600 s. Precipitation occurred after isothermal holding for 5 s and continuous precipitation occurred at grain boundaries after isothermally holding for 600 s. After isothermally holding for 3600 s, large Nb/Ti carbide precipitated. The presence of MX-type precipitates was confirmed by diffraction pattern. The interphase precipitation (IP) occurred between 5 and 30 s. Maximum hardness was obtained after isothermally holding for 600 s when IP occurred and rapidly decreased to a low value, mainly because polygonal ferrite dominated the microstructure after isothermally holding for 3600 s.

  12. Thermal Stability of Nanocrystalline Structure In X37CrMoV5-l Steel

    Directory of Open Access Journals (Sweden)

    Skołek E.

    2015-04-01

    Full Text Available The aim of the study was to investigate the thermal stability of the nanostructure produced in X37CrMoV5-1 tool steel by austempering heat treatment consisted of austenitization and isothermal quenching at the range of the bainitic transformation. The nanostructure was composed of bainitic ferrite plates of nanometric thickness separated by thin layers of retained austenite. It was revealed, that the annealing at the temperature higher than temperature of austempering led to formation of cementite precipitations. At the initial stage of annealing cementite precipitations occurred in the interfaces between ferritic bainite and austenite. With increasing temperature of annealing, the volume fraction and size of cementite precipitations also increased. Simultaneously fine spherical Fe7C3 carbides appeared. At the highest annealing temperature the large, spherical Fe7C3 carbides as well as cementite precipitates inside the ferrite grains were observed. Moreover the volume fraction of bainitic ferrite and of freshly formed martensite increased in steel as a result of retained austenite transformation during cooling down to room temperature.

  13. Crystal structures of the double perovskites Ba2Sr1-x Ca x WO6

    International Nuclear Information System (INIS)

    Fu, W.T.; Akerboom, S.; IJdo, D.J.W.

    2007-01-01

    Structures of the double perovskites Ba 2 Sr 1- x Ca x WO 6 have been studied by the profile analysis of X-ray diffraction data. The end members, Ba 2 SrWO 6 and Ba 2 CaWO 6 , have the space group I2/m (tilt system a 0 b - b - ) and Fm3-barm (tilt system a 0 a 0 a 0 ), respectively. By increasing the Ca concentration, the monoclinic structure transforms to the cubic one via the rhombohedral R3-bar phase (tilt system a - a - a - ) instead of the tetragonal I4/m phase (tilt system a 0 a 0 c - ). This observation supports the idea that the rhombohedral structure is favoured by increasing the covalency of the octahedral cations in Ba 2 MM'O 6 -type double perovskites, and disagrees with a recent proposal that the formation of the π-bonding, e.g., d 0 -ion, determines the tetragonal symmetry in preference to the rhombohedral one. - Graphical abstract: Enlarged sections showing the evolution of the basic (222) and (400) reflections in Ba 2 Sr 1- x Ca x WO 6 . Tick marks below are the positions of Bragg's reflections calculated using the space groups I2/m (x=0), R3-bar (x=0.25, 0.5 and 0.75) and Fm3-barm (x=1), respectively

  14. Hot ductility testing and weld simulation tests

    International Nuclear Information System (INIS)

    Weber, G.; Schick, M.

    1999-01-01

    The objective of the project was to enhance the insight into the causes of intergranular cracks detected in austenitic circumferential welds at BWR pipes. The susceptibility of a variety of austenitic pipe materials to hot cracking during welding and in-service intergranular crack corrosion was examined. The assumption was cracking in the root area of the HAZ of a multiple-layer weld. Hot-ductility tests and weld simulation tests specifically designed for the project were performed with the austenitic LWR pipe materials 1.4553 (X6 CrNiNb 18 10 S), 1.4550 (X10 CrNiNb 18 9), 1.4533 (X6 CrNiTi 18 9, two weld pools), and a non-stabilized TP 304 (X5 CrNi 18 10). (orig./CB) [de

  15. Residual stress studies of austenitic and ferritic steels

    International Nuclear Information System (INIS)

    Chrenko, R.M.

    1978-01-01

    Residual studies have been made on austenitic and ferritic steels of the types used as structural materials. The residual stress results presented here will include residual stress measurements in the heat-affected zone on butt welded Type 304 stainless steel pipes, and the stresses induced in Type 304 austenitic stainless steel and Type A508 ferritic steel by several surface preparations. Such surface preparation procedures as machining and grinding can induce large directionality effects in the residual stresses determined by X-ray techniques and some typical data will be presented. A brief description is given of the mobile X-ray residual stress apparatus used to obtain most of the data in these studies. (author)

  16. Precipitation behavior in austenitic and ferritic steels during fast neutron irradiation and thermal aging

    International Nuclear Information System (INIS)

    Kawanishi, H.; Hajima, R.; Sekimura, N.; Arai, Y.; Ishino, S.

    1988-01-01

    Precipitation behavior has been studied using a carbon extraction replica technique in Ti-modified Type 316 stainless steels (JPCA-2) and 9Cr-2Mo ferritic/martensitic steels (JFMS) irradiated to 8.1x10 24 n/m 2 at 873 and 673 K, respectively, in the experimental fast breeder reactor JOYO. Precipitate identification and compositional analysis were carried out on extracted replicas. The results were compared to those from the as-received steel and a control which had been given the same thermal as-treatment as the specimens received during irradiations. Carbides, Ti-sulphides and phosphides were precipitated in JPCA-2. Precipitate observed in JFMS included carbides, Laves-phases and phosphides. The precipitates in both steels were concluded to be stable under irradiation except for MC and M 6 C in JPCA-2. Small MC particles were found precipitated in JPCA-2 during both irradiation and aging. Irradiation proved to promote the precipitation of M 6 C in JPCA-2. (orig.)

  17. Carbide precipitation in the heat affected zone of a GTA weld in 21-6-9 stainless steel

    International Nuclear Information System (INIS)

    Carr, M.J.; Thorvaldson, W.G.

    1979-01-01

    Grain boundary precipitation was observed in a multipass GTA weld in 21-6-9 stainless steel. The precipitate was identified by electron diffraction as M 23 C 6 -type carbide. The presence of these carbide particles did not cause intergranular attack in standard corrosion tests

  18. Mechanical properties of API X80 steel pipe joints welded by Flux Core Arc Weld Process; Propriedades mecanicas de juntas de tubos de aco API X80 soldadas com arame tubulares

    Energy Technology Data Exchange (ETDEWEB)

    Ordonez, Robert E. Cooper; Silva, Jose Hilton F.; Trevisan, Roseana E. [Universidade Estadual de Campinas, SP (Brazil). Faculdade de Engenharia Mecanica. Dept. de Engenharia de Fabricacao

    2003-07-01

    Flux Core Arc Welding processes (FCAW) are beginning to be applied in pipeline welds, however, very limited experimental data regarding mechanical properties of pipeline weld joints with these processes are available in the literature. In this paper, the effects of preheat temperature and type of FCAW on mechanical properties (microhardness and tensile strength) of API X80 weld joint steel are presented. FCAW processes with gas protection and self-shielded were used. Multipasses welding were applied in 30'' diameter and 0,625'' thickness tubes. Influence factors were: FCAW type and preheat temperature. Acceptance criteria of welded joints were evaluated by API 1104 standard for tensile strength test and ASTM E384-99 for microhardness test. The results obtained showed that FCAW type and preheat temperature have no influence on mechanical properties of API X80 joint steel. (author)

  19. Evaluation of Creep Strength of Heterogeneous Welded Joint in HR6W Alloy and Sanicro 25 Steel

    Directory of Open Access Journals (Sweden)

    Zieliński A.

    2017-12-01

    Full Text Available This article presents the results of investigations on HR6W alloy and Sanicro 25 steel and the dissimilar welded joint made of them. The characteristic images of microstructure of the investigated materials in the as-received condition and following the creep test, observed with a scanning electron microscope (SEM, are shown. The X-ray analysis of phase composition of the existing precipitates was carried out. The method for evaluation of creep strength based on abridged creep tests carried out at a temperature higher than the design one is presented. The obtained results do not deviate from the values of creep strength determined in long-term creep tests. The maximum difference in creep strength of the investigated materials is ±20%, which is in compliance with the acceptable scatter band. The methodology presented can be used for verification of creep strength (life time of the material of finished components to be operated under creep conditions.

  20. Microstructure and properties of high chrome steel roller after laser surface melting

    International Nuclear Information System (INIS)

    Li Meiyan; Wang Yong; Han Bin; Zhao Weimin; Han Tao

    2009-01-01

    Laser surface melting of high chrome steels was achieved by a 5 kW continuous wave CO 2 laser. The microstructure of the laser surface-melted steels was investigated by scanning electron microscopy, transmission electron microscopy and X-ray diffractometry, and the hardness profiles were determined by a Vickers hardness tester. The corrosion behavior in 3.5% NaCl solution was studied by electrochemical corrosion equipment. The large carbides of high chrome steels are completely dissolved and ultrafine dendrites of austenite with submicroscopic M 23 C 6 carbides precipitation are formed in the melted zone. The austenite in the melted zone has a high tempering stability. The corrosion resistance of the laser surface-melted steels is significantly improved due to the dissolution of carbides and the increase of the alloying elements in the solid solution as well as the large amount of austenite.

  1. Study of corrosion in metallic coating in steel-carbon by thermal spray; Estudo de corrosao em revestimentos metalicos em aco-carbono obtidos por aspersao termica

    Energy Technology Data Exchange (ETDEWEB)

    Cruz, Maria C.P.; Cavalcanti, Eliane B.; Rambo, Elisabeth S.M.; Araujo, Paulo M.M. [Instituto de Tecnologia e Pesquisa (IPT), Aracaju, SE (Brazil); Santos, Anderson O. [PETROBRAS S.A., Rio de Janeiro, RJ (Brazil)

    2008-07-01

    The effect caused for constituent elements of the watery environment of production of the oil on metallic coverings was studied that simulate the artificial rise of the oil (connecting rods of pump mechanic). For in such a way, the techniques of electrochemical analysis had been used, as the method of linear polarization and the extrapolation of the straight line of Tafel of metallic coverings [alloy of Bronze and Aluminum; alloy of CrNi 80/20; NiCr 80/20; 95MXC (Cr: 26.5% - 31.5%, Cr: 26.5% - 31.5%, B: 3.35% - 4.15%, Mn: 1.1% - 2.2%, Itself: 1.1% -2.1%, Faith) and aluminum] on the substratum steel simulating covering in the connecting rods of pump. Oil well had been raised the resistance characteristics the polarization of the metal when submitted to the watery way surrounding it. They had been evaluated the resistance the covering polarization applied on the steel, with the objective to analyze its resistance the corrosion and to verify the possibility of its use as barrier against the problems originated for the degradation in connecting rods of pump. For the calculated Taxes of Corrosion, it can be concluded that the Aluminum coverings (0,003 mm/year) and NiCr 80/20 (0,179 mm/year) had been the ones that had presented a bigger resistance to the corrosive way. (author)

  2. The Beam Line X NdFe-steel hybrid wiggler for SSRL

    International Nuclear Information System (INIS)

    Hoyer, E.; Halbach, K.; Humphries, D.; Marks, S.; Plate, D.; Shuman, D.; Karpenko, V.P.; Kulkarni, S.; Tirsell, K.G.

    1987-01-01

    A wiggler magnet with 15 periods, each 12.85 cm long, which achieves 1.40 T at a 2.1 cm gap (2.26T at 0.8 cm) has been designed and is now in fabrication at LBL. This wiggler will be the radiation source of the high intensity synchrotron radiation beam line for the Beam Line X PRT facility at SSRL. The magnet utilizes Neodymium-Iron (NdFe) material and Vanadium Permendur (steel) in the hybrid configuration to achieve simultaneously a high magnetic field and short period. Magnetic field adjustment is with a driven chain and ball screw drive system. The magnetic structure is external to an s.s. vacuum chamber which has thin walls, 0.76 mm thickness, at each pole tip for higher field operation. Magnetic design, construction details and magnetic measurements are presented

  3. Irradiation creep in ferritic steels

    International Nuclear Information System (INIS)

    Vandermeulen, W.; Bremaecker, A. de; Burbure, S. de; Huet, J.J.; Asbroeck, P. van

    Pressurized and non-pressurized capsules of several ferritic steels have been irradiated in Rapsodie between 400 and 500 0 C up to 3.7 x 10 22 n/cm 2 (E>0.1 MeV). Results of the diameter measurements are presented and show that the total in-pile deformation is lower than for austenitic steels

  4. Microstructural aspects of crack formation and propagation in the austenitic steel X6CrNiNb18-10 under low cycle fatigue loading

    International Nuclear Information System (INIS)

    Soppa, E.; Kohler, C.; Roos, E.; Schuler, X.

    2012-01-01

    The understanding of the crack initiation mechanisms and crack growth in apparently monolithic materials like X6CrNiNb18-10 stainless steel under cyclic loading requires the explicit analysis of the phenomena underlying fatigue on both atomistic and microscopic levels. The permanent delivery of mechanical energy through cyclic loading evokes changes in the microstructure that can lead to a martensitic transformation. The transformation of a metastable cubic face centered austenite and formation of a cubic body centered α'-martensite under cyclic loading at room temperature was found, both, in the experiment and in molecular dynamics simulations. The martensite nucleates prevalently at grain boundaries, triple points and at the specimen free surface and forms small (∝ 1 μm) differently oriented grains, also in the same parent austenitic grain. By a combination of interrupted low cycle fatigue tests (LCF) and electron backscatter diffraction (EBSD) measurements the martensitic transformation and subsequent fatigue crack formation were observed at the same area in the microstructure at different stages of the specimen lifetime. The EBSD measurements showed the following crack initiation scenarios: Cracks started (a) at the phase boundary between austenite and α'-martensite, (b) inside fully martensitic areas in the matrix, (c) at broken or debonded coarse NbCs. It is obvious that formation of a hard α'-martensite in a ductile and soft austenite and forming two-phase material causes a heterogeneous stress and strain distribution on the microscopic level. α'-martensite enhances locally the stress amplitude whereas in a soft austenite the plastic strain amplitude increases. Strain concentration in the austenite along the phase boundary is connected with a stress increase along the interface and can initiate fatigue crack there. Also at the crack tip, a permanent martensitic transformation occurs, so that the growth of the fatigue cracks at room temperature seems

  5. In-situ observation of crack propagation in thermally sprayed coatings

    Czech Academy of Sciences Publication Activity Database

    Mušálek, R.; Kovářík, O.; Matějíček, Jiří

    2010-01-01

    Roč. 205, č. 7 (2010), s. 1807-1811 ISSN 0257-8972 R&D Projects: GA MŠk ME 901 Institutional research plan: CEZ:AV0Z20430508 Keywords : coating fracture * in-situ observation * alumina * stainless steel * plasma spraying Subject RIV: JL - Materials Fatigue, Friction Mechanics Impact factor: 2.135, year: 2010 http://www.sciencedirect.com/science?_ob=GatewayURL&_method=citationSearch&_uoikey=B6TVV-4YTFBCY-5&_origin=SDEMFRHTML&_version=1&md5=896533bcc989ebaa374ff209558fbcf1

  6. Phase stability of high manganese austenitic steels for cryogenic applications

    CERN Document Server

    Couturier, K

    2000-01-01

    The aim of this work is to study the austenitic stability against a' martensitic transformation of three non-magnetic austenitic steels : a new stainless steel X2CrMnNiMoN 19-12-11-1 grade, a traditional X8CrMnNiN 19-11-6 grade and a high manganese X8MnCrNi 28-7-1 grade. Measurements of relative magnetic susceptibility at room temperature are performed on strained tensile specimens at 4.2 K. A special extensometer for high precision strain measurements at low temperature has been developed at CERN to test specimens up to various levels of plastic strain. Moreover, the high precision strain recording of the extensometer enables a detailed study of the serrated yield phenomena associated with 4.2 K tensile testing and their influence on the evolution of magnetic susceptibility. The results show that high Mn contents increase the stability of the austenitic structure against a' martensitic transformation, while keeping high strength at cryogenic temperature. Moreover, proper elaboration through primary and possi...

  7. Compactibility of atomized high-speed steel and steel 3 powders

    International Nuclear Information System (INIS)

    Kulak, L.D.; Gavrilenko, A.P.; Pikozh, A.P.; Kuz'menko, N.N.

    1985-01-01

    Spherical powders and powders of lammellar-scaly shape of high-speed R6M5K5 steel and steel 3 produced by the method of centrifugal atomization of a rotating billet under conditions of cold pressing in steel moulds are studied for thier compactability. Compacting pressure dependnences are establsihed for density of cold-pressed compacts of spherical and scaly powders. The powders of lammellar-scaly shape both of high-speed steel and steel 3 are found to possess better compactibility within a wide range of pressures as compared to powders of spherical shape. Compacts of the lammellar-scaly powders possess also higher mechanical strength

  8. Joining of pressureless-sintered SiC to stainless steel using Ag-Cu alloy and insert-metals

    International Nuclear Information System (INIS)

    Yano, Toyohiko; Takada, Naohiro; Iseki, Takayoshi

    1987-01-01

    Brazing of pressureless-sintered SiC to stainless steel using Ag-28 wt% Cu alloy was studied. In SiC plate joined to stainless steel rod (6 mm in diameter) using an Ag-Cu alloy powder containing 1.5 wt% Ti, the bond strength increased with decreasing brazing temperature and holding time. When the increased size of stainless steel plate (10 x 10 x 4 mm), joining was unsuccessful by the method mentioned above and even with Ti insert-metal. However, simultaneous use of Ti and Mo as insert-metal gave a good bonding in the order SiC/Ti/Mo/stainless steel, because of relaxation of residual stress due to thermal expansion mismatch. The shear strength was 30 - 50 MPa. A thin layer, probably Ti 3 SiC 2 , was observed at the interface between SiC and brazing filler immediately after melting. But with increasing both temperature and time, Ti 5 Si 3 (C) and TiC x were formed if Ti was continuously provided from the brazing filler. Since the interface of Ti 3 SiC 2 and either Ti 5 Si 3 (C) or TiC x seemed to be brittle, the formation of Ti 5 Si 3 (C) and TiC x decreased the bond strength. At lower temperature and short time, a high bond strength is expected when Ti was inserted in contact with SiC. (author)

  9. Fe3Nb3N precipitates of the Fe3W3C type in Nb stabilized ferritic stainless steel

    International Nuclear Information System (INIS)

    Malfliet, A.; Van den Broek, W.; Chassagne, F.; Mithieux, J.-D.; Blanpain, B.; Wollants, P.

    2011-01-01

    Highlights: → The precipitation in Nb stabilized ferritic stainless steel at 950 deg. C is investigated. → We characterized the Fe 3 Nb 3 X precipitates with SAED, EELS, WDS and AES. → We found that Fe 3 Nb 3 X precipitates are stabilized by N and not by C or O. → This insight is new and important for future development of this type of steel grade. - Abstract: A Nb stabilized ferritic stainless steel with 0.45 wt.%Nb, 82 ppm C and 170 ppm N is investigated to reveal the nature of the precipitates present at 950 deg. C. In particular, Fe 3 Nb 3 X precipitates of the Fe 3 W 3 C type are analyzed with WDS and EELS to determine the light elements X stabilizing this phase in the steel. According to WDS on large precipitates after 500 h at 950 deg. C, the Fe 3 Nb 3 X phase contains 10.4 at.% N, 1.2 at.% O and 1.0 at.% C. Auger Electron Spectroscopy on the same precipitates confirms the presence of N. In addition, it is revealed that the C and O peaks observed with WDS result from surface contamination as they disappear after Ar sputtering. The presence of a N peak in the EELS spectra of small Fe 3 Nb 3 X precipitates which have formed after 6 min at 950 deg. C indicate that N stabilizes this phase already from the initial precipitation stage. With this analysis it is demonstrated that N is an effective stabilizer of Fe 3 Nb 3 X precipitates in ferritic stainless steels. The formation of this phase should therefore be considered when predicting the precipitation behavior of Nb in industrial Nb stabilized ferritic stainless steels containing residual N.

  10. Study on tempering behaviour of AISI 410 stainless steel

    Energy Technology Data Exchange (ETDEWEB)

    Chakraborty, Gopa, E-mail: gopa_mjs@igcar.gov.in [Metallurgy & Materials Group, Indira Gandhi Center for Atomic Research, Kalpakkam 603102 (India); Das, C.R.; Albert, S.K.; Bhaduri, A.K.; Thomas Paul, V. [Metallurgy & Materials Group, Indira Gandhi Center for Atomic Research, Kalpakkam 603102 (India); Panneerselvam, G. [Chemistry Group, Indira Gandhi Center for Atomic Research, Kalpakkam 603102 (India); Dasgupta, Arup [Metallurgy & Materials Group, Indira Gandhi Center for Atomic Research, Kalpakkam 603102 (India)

    2015-02-15

    Martensitic stainless steels find extensive applications due to their optimum combination of strength, hardness and wear-resistance in tempered condition. However, this class of steels is susceptible to embrittlement during tempering if it is carried out in a specific temperature range resulting in significant reduction in toughness. Embrittlement of as-normalised AISI 410 martensitic stainless steel, subjected to tempering treatment in the temperature range of 673–923 K was studied using Charpy impact tests followed by metallurgical investigations using field emission scanning electron and transmission electron microscopes. Carbides precipitated during tempering were extracted by electrochemical dissolution of the matrix and identified by X-ray diffraction. Studies indicated that temper embrittlement is highest when the steel is tempered at 823 K. Mostly iron rich carbides are present in the steel subjected to tempering at low temperatures of around 723 K, whereas chromium rich carbides (M{sub 23}C{sub 6}) dominate precipitation at high temperature tempering. The range 773–823 K is the transition temperature range for the precipitates, with both Fe{sub 2}C and M{sub 23}C{sub 6} types of carbides coexisting in the material. The nucleation of Fe{sub 2}C within the martensite lath, during low temperature tempering, has a definite role in the embrittlement of this steel. Embrittlement is not observed at high temperature tempering because of precipitation of M{sub 23}C{sub 6} carbides, instead of Fe{sub 2}C, preferentially along the lath and prior austenite boundaries. Segregation of S and P, which is widely reported as one of the causes for temper embrittlement, could not be detected in the material even through Auger electron spectroscopy studies. - Highlights: • Tempering behaviour of AISI 410 steel is studied within 673–923 K temperature range. • Temperature regime of maximum embrittlement is identified as 773–848 K. • Results show that type of

  11. X particle effect for 6Li reaction rates calculations

    International Nuclear Information System (INIS)

    Kocak, G.; Balantekin, A. B.

    2009-01-01

    The inferred primordial 6 L i-7 L i abundances are different from standard big bang nucleosynthesis results, 6 L i is 1000 times larger and 7 L i is 3 times smaller than the big bang prediction. In big bang nucleosynthesis, negatively charged massive X particles a possible solution to explain this primordial Li abundances problem [1]. In this study, we consider only X particle effect for nuclear reactions to obtain S-factor and reaction rates for Li. All S-factors calculated within the Optical Model framework for d(α,γ)6 L i system. We showed that the enhancement effect of massive negatively charged X particle for 6 L i system reaction rate.(author)

  12. In situ 3D monitoring of corrosion on carbon steel and ferritic stainless steel embedded in cement paste

    International Nuclear Information System (INIS)

    Itty, Pierre-Adrien; Serdar, Marijana; Meral, Cagla; Parkinson, Dula; MacDowell, Alastair A.; Bjegović, Dubravka; Monteiro, Paulo J.M.

    2014-01-01

    Highlights: • The morphology of the corrosion of steel in cement paste was studied in situ. • During galvanostatic corrosion, carbon steel reinforcement corroded homogeneously. • On ferritic stainless steel, deep corrosion pits formed and caused wider cracks. • The measured rate of steel loss correlated well with Faraday’s law of electrolysis. - Abstract: In a X-ray microcomputed tomography study, active corrosion was induced by galvanostatically corroding steel embedded in cement paste. The results give insight into corrosion product build up, crack formation, leaching of products into the cracks and voids, and differences in morphology of corrosion attack in the case of carbon steel or stainless steel reinforcement. Carbon steel was homogeneously etched away with a homogeneous layer of corrosion products forming at the steel/cement paste interface. For ferritic stainless steel, pits were forming, concentrating the corrosion products locally, which led to more extensive damage on the cement paste cover

  13. Effects of Non-metallic Inclusions on Hot Ductility of High Manganese TWIP Steels Containing Different Aluminum Contents

    Science.gov (United States)

    Wang, Yu-Nan; Yang, Jian; Wang, Rui-Zhi; Xin, Xiu-Ling; Xu, Long-Yun

    2016-06-01

    The characteristics of inclusions in Fe-16Mn- xAl-0.6C ( x = 0.002, 0.033, 0.54, 2.10 mass pct) steels have been investigated and their effects on hot ductility of the high manganese TWIP steels have been discussed. Ductility is very poor in the steel containing 0.54 mass pct aluminum, which is lower than 20 pct in the temperature range of 873 K to 1473 K (600 °C to 1200 °C). For the steels containing 0.002 and 2.10 mass pct aluminum, ductility is higher than 40 pct in the same temperature range. The hot ductility of steel containing 0.033 mass pct aluminum is higher than 30 pct throughout the temperature range under examination. With increasing aluminum content, the main inclusions in the steels change along the route of MnO/(MnO + MnS) → MnS/(Al2O3 + MnS) → AlN/(Al2O3 + MnS)/(MgAl2O4 + MnS) → AlN. The thermodynamic results of inclusion types calculated with FactSage software are in agreement with the experimental observation results. The inclusions in the steels containing 0.002 mass pct aluminum do not deteriorate the hot ductility. MnS inclusions whose average size, number density, and volume ratio are 1.12 μm, 15.62 mm-2, and 2.51 × 10-6 in the steel containing 0.033 mass pct aluminum reduce the ductility. In the steel containing 0.54 mass pct aluminum, AlN inclusions whose average size, number density, and volume ratio are 0.878 μm, 16.28 mm-2 and 2.82 × 10-6 can precipitate at the austenite grain boundaries, prevent dynamic recrystallization and deteriorate the hot ductility. On the contrary, in the steel containing 2.10 mass pct aluminum, the average size, number density and volume ratio of AlN inclusions change to 2.418 μm, 35.95 mm-2, and 2.55 × 10-5. They precipitate in the matrix, which do not inhibit dynamic recrystallization and thereby do not lead to poor hot ductility.

  14. Characterization and corrosion behavior of F6NM stainless steel treated in high temperature water

    Science.gov (United States)

    Li, Zheng-yang; Cai, Zhen-bing; Yang, Wen-jin; Shen, Xiao-yao; Xue, Guo-hong; Zhu, Min-hao

    2018-03-01

    F6NM martensitic stainless steel was exposed to 350 °C water condition for 500, 1500, and 2500 h to simulate pressurized water reactor (PWR) condition. The characterization and corrosion behavior of the oxide film were investigated. Results indicate that the exposed steel surface formed a double-layer oxide film. The outer oxide film is Fe-rich and contains two type oxide particles. However, the inner oxide film is Cr-rich, and two oxide films, whose thicknesses increase with increasing exposure time. The oxide film reduces the corrosion behavior because the outer oxide film has many crack and pores. Finally, the mechanism and factors affecting the formation of the oxide film were investigated.

  15. Study of effect of austenite prehistory of 03Ch20N16AG6 steel on it structure and properties

    Energy Technology Data Exchange (ETDEWEB)

    Demchuk, I S; Krakhmalev, V I; Manninen, A I [Leningradskij Politekhnicheskij Inst. (USSR)

    1981-01-01

    Effect of preliminary cold working and different procedures of thermal treatment on structure and mechanical properties of stable austenite of 03Kh20N16AG6 steel is found out. It is shown that the degree of defectability of initial austenite structure predetermines the further deformation behaviour of the steel (level of strength characteristics, plasticity storage, hardening degree etc.) in the wide temperature range. Close connection of structural changes with properties should determine the choice of preliminary treatment of stable austenitic steel as applied to concrete condition of operation.

  16. An X-ray diffraction study of microstructural deformation induced by cyclic loading of selected steels

    International Nuclear Information System (INIS)

    Fourspring, P.M.; Pangborn, R.N.

    1996-06-01

    X-ray double crystal diffractometry (XRDCD) was used to assess cyclic microstructural deformation in a face centered cubic (fcc) steel (AISI304) and a body centered cubic (bcc) steel (SA508 class 2). The first objective of the investigation was to determine if XRDCD could be used to effectively monitor cyclic microstructural deformation in polycrystalline Fe alloys. A second objective was to study the microstructural deformation induced by cyclic loading of polycrystalline Fe alloys. The approach used in the investigation was to induce fatigue damage in a material and to characterize the resulting microstructural deformation at discrete fractions of the fatigue life of the material. Also, characterization of microstructural deformation was carried out to identify differences in the accumulation of damage from the surface to the bulk, focusing on the following three regions: near surface (0--10 microm), subsurface (10--300 microm), and bulk. Characterization of the subsurface region was performed only on the AISI304 material because of the limited availability of the SA508 material. The results from the XRDCD data indicate a measurable change induced by fatigue from the initial state to subsequent states of both the AISI304 and the SA508 materials. Therefore, the XRDCD technique was shown to be sensitive to the microstructural deformation caused by fatigue in steels; thus, the technique can be used to monitor fatigue damage in steels. In addition, for the AISI304 material, the level of cyclic microstructural deformation in the bulk material was found to be greater than the level in the near surface material. In contrast, previous investigations have shown that the deformation is greater in the near surface than the bulk for Al alloys and bcc Fe alloys

  17. The temperature dependence of void swelling of fast reactor irradiated 316 stainless steel

    International Nuclear Information System (INIS)

    Bramman, J.I.; Brown, C.

    The swelling versus temperature profile for cold-worked M316 stainless steel irradiated in DFR to fluences around 6.5 x 10 22 n.cm -2 (E > 0.1 MeV) is singly-peaked with maximum swelling at just below 600 0 C. The underlying microstructural features are discussed

  18. PORTUGUESE AND LUSO BRASÍLICOS COLONOS IN TRAINING OF FAMILY GROUPS IN THE OF THE SERIDÓ (1788-1811

    Directory of Open Access Journals (Sweden)

    HELDER ALEXANDRE MEDEIROS DE MACEDO

    2011-12-01

    Full Text Available This article objective is to trace the origin of the Portuguese in family pools constructed in the territory of the Freguesia da Gloriosa Senhora Santa Ana do Seridó, which was formed by riversides by Capitanias of Rio Grande and Paraíba, occupied by livestock since the end of the 17th century in the context of Westernization. Part of a regional literature review dedicated to the research of the Seridó genealogical trunks and takes as priority source records of baptisms, marriages and burials of the parish, in the period 1788 to 1811, analysed by the method of historical demography and clipping of analysis as the family groupings formed by settlers of Portuguese origin

  19. Microstructure and properties of high chrome steel roller after laser surface melting

    Energy Technology Data Exchange (ETDEWEB)

    Li Meiyan, E-mail: lmy_102411@163.com [College of Electromechanical Engineering, China University of Petroleum, 271 Bei' er Road, Dongying 257061 (China); Wang Yong; Han Bin; Zhao Weimin; Han Tao [College of Electromechanical Engineering, China University of Petroleum, 271 Bei' er Road, Dongying 257061 (China)

    2009-06-15

    Laser surface melting of high chrome steels was achieved by a 5 kW continuous wave CO{sub 2} laser. The microstructure of the laser surface-melted steels was investigated by scanning electron microscopy, transmission electron microscopy and X-ray diffractometry, and the hardness profiles were determined by a Vickers hardness tester. The corrosion behavior in 3.5% NaCl solution was studied by electrochemical corrosion equipment. The large carbides of high chrome steels are completely dissolved and ultrafine dendrites of austenite with submicroscopic M{sub 23}C{sub 6} carbides precipitation are formed in the melted zone. The austenite in the melted zone has a high tempering stability. The corrosion resistance of the laser surface-melted steels is significantly improved due to the dissolution of carbides and the increase of the alloying elements in the solid solution as well as the large amount of austenite.

  20. Quantum percolation transition in Eu{sub 1-x}Ca{sub x}B{sub 6}

    Energy Technology Data Exchange (ETDEWEB)

    Glushkov, V.V. [A.M.Prokhorov General Physics Institute of RAS, 38, Vavilov str., Moscow 119991 (Russian Federation); Moscow Institute of Physics and Technology, 9, Institutskii per., Dolgoprudny, Moscow Region 141700 (Russian Federation); Anisimov, M.A. [Moscow Institute of Physics and Technology, 9, Institutskii per., Dolgoprudny, Moscow Region 141700 (Russian Federation); Bogach, A.V.; Demishev, S.V.; Sluchanko, N.E. [A.M.Prokhorov General Physics Institute of RAS, 38, Vavilov str., Moscow 119991 (Russian Federation); Filipov, V.B.; Levchenko, A.V.; Shitsevalova, N.Yu. [Institute for Problems of Materials Science NAS, 3, Krzhyzhanovsky str., Kiev 03680 (Ukraine); Flachbart, K. [Centre of Low Temperature Physics, IEP SAS and IPS FS UPJS, Kosice SK-04001 (Slovakia); Kuznetsov, A.V. [Moscow Engineering Physics Institute, 31, Kashirskoe Shosse, Moscow 115409 (Russian Federation)

    2010-03-15

    The study of transport and magnetic properties performed on Eu{sub 1-x}Ca{sub x}B{sub 6} single crystals with nominal Ca content 0 {<=} x {<=} 0.4 at temperatures 1.8-300 K in magnetic fields up to 80 kOe provides the direct experimental evidence of metal-to-insulator transition (MIT) earlier proposed for the system by V. M. Pereira et al. [Phys. Rev. Lett., 93, 147202 (2004)]. A giant enhancement of magnetoresistance up to the values of ({rho}(0) - {rho}(H))/{rho}(H) {proportional_to} 7 x 10{sup 7}% was detected for x = 0.4 in the wide vicinity of the ferromagnetic insulating state. The field induced crossover from hole-like to electron-like regime of charge transport observed for the first time in the paramagnetic phase of Eu{sub 0.6}Ca{sub 0.4}B{sub 6} is discussed in terms of quantum percolation transition predicted for this low carrier density system within double exchange model. (Abstract Copyright [2010], Wiley Periodicals, Inc.)

  1. Quantitative analysis of inclusions in low carbon free cutting steel using small-angle X-ray and neutron scattering

    International Nuclear Information System (INIS)

    Oba, Yojiro; Koppoju, Suresh; Ohnuma, Masato; Kinjo, Yuki; Tomota, Yo; Morooka, Satoshi; Suzuki, Jun-ichi; Yamaguchi, Daisuke; Koizumi, Satoshi; Sato, Masugu; Shiraga, Tetsuo

    2012-01-01

    The microstructure of inclusions in low carbon free cutting steel without lead addition was investigated using small-angle X-ray scattering (SAXS) coupled with small-angle neutron scattering (SANS). The two-dimensional (2D) SAXS pattern shows clear scattering due to inclusions composed of large elongated particles aligned along the rolling direction, and small isotropic particles. From a comparison of the simulated and experimental 2D SAXS patterns, the shapes of the inclusions are regarded as ellipsoid for the larger inclusions and spherical for the smaller inclusions. The length of the minor axis in the large inclusion is 6.9 μm, while the diameter of the small inclusion is 0.50 μm. The aspect ratio of the large inclusion is estimated to be 3.8 in the lower q region, and is reduced slightly to 3.5 in the higher q region from the azimuthal plots. The results of an alloy contrast variation (ACV) analysis using both the SAXS and SANS data indicate that the chemical composition of the inclusions is almost NaCl-type manganese sulfide, and that the amount of iron sulfide is low. The volume fractions are 1.4% for the large inclusions and 0.2% for the small inclusions. This is consistent with the area fraction estimated using an optical microscope, and indicates that nearly all of the sulfur in the steel sample forms the manganese sulfide inclusions. (author)

  2. Precipitation behavior of Laves phase and its effect on toughness of 9Cr-2Mo ferritic-martensitic steel

    International Nuclear Information System (INIS)

    Hosoi, Y.; Wade, N.; Kunimitsu, S.; Urita, T.

    1986-01-01

    This study clarified the relationship between the toughness of a 9Cr-2Mo dual phase steel and precipitates formed during aging, with special attention to the Laves phase (Fe 2 Mo). The ductile-brittle transition temperature (DBTT) is increased and the upper shelf energy decreased when the Laves phase begins to precipitate during aging. Electron microscopy and X-ray diffraction indicate that elimination of Si in the steel reduces the precipitation of the Laves phase and results in maintaining good toughness. It is also noted that the toughness of the steel is controlled by the total amount of precipitates (Laves + carbides) in the aging at 873 K for more than 3.6x10 3 ks. A time-temperature-precipitation diagram for the Laves phase is established and it clearly shows that the precipitation of the Laves phase is markedly retarded by the decrease of Si content. In Si-free steel, no Laves phase is observed in the temperature and time range investigated. (orig.)

  3. Nitrogen-containing steels and thermomechanical treatment

    International Nuclear Information System (INIS)

    Kaputkina, L.; Prokoshkina, V.G.; Svyazhin, G.

    2004-01-01

    The strengthening of nitrogen-containing corrosion-resistant steels resulting from alloying and thermomechanical treatment have been investigated using X-ray diffraction analysis, light microscopy, hardness measurements and tensile testing. Combined data have been obtained for nitrogen interaction with alloying elements , peculiarities of deformed structure and short-range of nitrogen-containing steels of various structural classes. The higher nitrogen and total alloying element contents, the higher deformation strengthening. Prospects of use the steels with not high nitrogen content and methods of their thermomechanical strengthening are shown. High temperature thermomechanical treatment (HTMT) is very effective for obtaining high and thermally stable constructional strength of nitrogen-containing steels of all classes. The HTMT is most effective if used in a combination with dispersion hardening for aging steels or in the case of mechanically unstable austenitic steels. (author)

  4. Synthesis of silicated hydroxyapatite Ca10(PO4)6-x(SiO4)x(OH)2-x

    International Nuclear Information System (INIS)

    Palard, Mickael; Champion, Eric; Foucaud, Sylvie

    2008-01-01

    The preparation of silicated hydroxyapatite Ca 10 (PO 4 ) 6-x (SiO 4 ) x (OH) 2-x (SiHA) with 0≤x≤2 was investigated using a wet precipitation method followed by a heat treatment. X-ray diffraction and Rietveld refinement, Fourier transformed IR (FTIR) spectroscopy, elemental analyses, transmission electron microscopy and thermal analyses were used to characterize the samples. The raw materials were composed of a partially silicated and carbonated apatite and a secondary minor phase containing the excess silicon. Single phase silicated hydroxyapatites, with 0≤x≤1, could be synthesized after a thermal treatment of the raw powders above 700 deg. C. The presence of carbonate groups in the raw apatite played an important role in the incorporation of silicates during heating. From the different results, the mechanisms of formation of SiHA are discussed. - Graphical abstract: The preparation of pure silicated hydroxyapatite Ca 10 (PO 4 ) 6-x (SiO 4 ) x (OH) 2-x powders with controlled silicon content was investigated. The synthesis route included a precipitation in aqueous media. It required an additional high temperature solid-state reaction to fully incorporate the silicon into the apatite crystals

  5. Notch and hydrogen effects on sensitized 21-6-9 stainless steel

    International Nuclear Information System (INIS)

    Caskey, C.R. Jr.

    1979-01-01

    Type 21-6-9 stainless steel alloy is slightly notch sensitive in the solution annealed condition, a behavior that is aggravated by sensitization anneal at 920 0 K. The lower toughness of the sensitized alloy is a measure of microstructural embrittlement associated with carbide precipitation in grain boundaries. The tendency toward grain boundary fracture in the sensitized alloy is accentuated by stress concentration at the notch. Also, there is an increase in notch sensitivity when the alloy is tested in a high pressure (69 MPa) hydrogen environment, due to susceptibility of the grain boundaries to hydrogen embrittlement

  6. Long-term Stability of 9- to 12 % Cr Steels

    DEFF Research Database (Denmark)

    Hald, John

    2004-01-01

    In the recent 25 years creep rupture strength of 9- to 12 %Cr steels for steam pipes and turbines has been doubled by development of new alloys. This development has formed a basis for improved efficiency of fossil fired steam power plants by introduction of advanced steam temperatures...... and pressures. Newly developed steam pipe steels are based on modifications of well-established steels like the X 20CrMoV12 1. Balanced addition of V, Nb and N to a 9Cr 1 Mo steel led to the Modified 9 Cr steel P 91. Addition of 1% W to a 9Cr 1 MoVNbN base composition led to steel E 911 and partial replacement...... of Mo with 1.8 % W combined with a slight amount of Boron led to steel P 92. The creep rupture strength of these new alloys are now secured with long-term tests up to 100,000 hours, which demonstrate improvements of 50% (P 91), 75 % (E 911) and 100 % (P 92) in strength compared to X 20CrMoV12 1....

  7. Investigating pitting in X65 carbon steel using potentiostatic polarisation

    Science.gov (United States)

    Mohammed, Sikiru; Hua, Yong; Barker, R.; Neville, A.

    2017-11-01

    Although pitting corrosion in passive materials is generally well understood, the growth of surface pits in actively-corroding materials has received much less attention to date and remains poorly understood. One of the key challenges which exists is repeatedly and reliably generating surface pits in a practical time-frame in the absence of deformation and/or residual stress so that studies on pit propagation and healing can be performed. Another pertinent issue is how to evaluate pitting while addressing general corrosion in low carbon steel. In this work, potentiostatic polarisation was employed to induce corrosion pits (free from deformation or residual stress) on actively corroding X65 carbon steel. The influence of applied potential (50 mV, 100 mV and 150 mV vs open circuit potential) was investigated over 24 h in a CO2-saturated, 3.5 wt.% NaCl solution at 30 °C and pH 3.8. Scanning electron microscopy (SEM) was utilised to examine pits, while surface profilometry was conducted to measure pit depth as a function of applied potential over the range considered. Analyses of light pitting (up to 120 μm) revealed that pit depth increased linearly with increase in applied potential. This paper relates total pit volume (measured using white light interferometry) to dissipated charge or total mass loss (using the current response for potentiostatic polarisation in conjunction with Faraday's law). By controlling the potential of the surface (anodic) the extent of pitting and general corrosion could be controlled. This allowed pits to be evaluated for their ability to continue to propagate after the potentiostatic technique was employed. Linear growth from a depth of 70 μm at pH 3.8, 80 °C was demonstrated. The technique offers promise for the study of inhibition of pitting.

  8. Study of sulphate-reducing bacteria corrosion in the weld joint for API X-70 steel

    Energy Technology Data Exchange (ETDEWEB)

    Flores, J. E.; Patino-Carachure, C.; Alfonso, I.; Rodriguez, J. A.; Rosas, G.

    2012-11-01

    The corrosion behavior originated by sulfate-reducing bacteria (SRB) was studied in two regions of welded API X-70 steel pipeline. The studies were focused on base material (BM) and heat affected zone (HAZ), from the internal region of the pipe. SRB were extracted from oil and grown in a Postgate medium. Corrosion was evaluated at 60 degree centigrade for times between 5 and 64 days. Potentiodynamic polarization curves, obtained by electrochemical techniques, indicated surface activation at short times. Structural and morphological characterizations were carried out by scanning electron microscopy (SEM) and optical microscopy (OM). H{sub 2}S concentration and pH were also measured. Results showed an important increase in the corrosion damage up to 20 days, influenced by the SRB activity, which lead to a maximum of H{sub 2}S (pH minimum). It was found a localized corrosion attack in the HAZ in a higher quantity compared to BM; and the formation of a thin film on the steel surface, originated by corrosion products and bacterial activity. (Author) 15 refs.

  9. The structure of the alphinizing coat on alloy steels

    Directory of Open Access Journals (Sweden)

    S. Pietrowski

    2008-12-01

    Full Text Available In this paper results of the structure of the coat alphinizing in AlSi5 silumin on alloy steels: acid-proof 1H18N9T (X6CrNiTi18-10 and high speed SW18 (HS18-0-1 were presented. The temperature of the alphinizing bath was amounts to750±5°C, and immersion time of the element τ = 180s. It was shown, that there is the different “g” coat thickness on testing steels. On the 1H18N9T steel it amounts to g = 52μm, and on the SW18 steel – g = 203μm. Regardless of a grade of testing alloy steels the coat consist of three layers with diversified phasic structure. There is different chemical composition of coat layers on testing steels. The first layer from the base consist of AlFe phase containing alloy addictions of steels: Cr and Ni (1H18N9T and W, V and Cr (SW18. On this layer crystallize the second layer of intermetallic phases. It is the phase containing the main alloy addiction of steels: AlFeCr (1H18N9T and AlFeW (SW18. The last, outside layer consist of silumin containing AlFeNi intermetallic phases on the 1H18N9T steel and AlFeW on the SW18 steel. Regardless of the grade of testing steels there is Si element in all layers of the coat. There are morphological differences in tested layers. The second layer (AlFeW phase inside the coat on the SW18 steel consist of faced crystals growing into in outside silumin layer. On the 1H18N9T steel a boundary between transient and outside layer is more uniform. Free separations of intermetallic phases inside silumin layer on the 1H18N9T steel have lamellar and on the SW18 steel – faced form.

  10. Effect of Co deposition on oxidation behavior and electrical properties of ferritic steel for solid oxide fuel cell interconnects

    Energy Technology Data Exchange (ETDEWEB)

    Kruk, A.; Adamczyk, A.; Gil, A. [AGH University of Science and Technology, Faculty of Materials Science and Ceramics, al. Mickiewicza 30, 30-059 Krakow (Poland); Kąc, S. [AGH University of Science and Technology, Faculty of Metals Engineering and Industrial Computer Science, al. Mickiewicza 30, 30-059 Krakow (Poland); Dąbek, J.; Ziąbka, M. [AGH University of Science and Technology, Faculty of Materials Science and Ceramics, al. Mickiewicza 30, 30-059 Krakow (Poland); Brylewski, T., E-mail: brylew@agh.edu.pl [AGH University of Science and Technology, Faculty of Materials Science and Ceramics, al. Mickiewicza 30, 30-059 Krakow (Poland)

    2015-09-01

    In this work, a Co layer deposited on DIN 50049 steel by means of pulsed laser deposition was applied for the protection of solid oxide fuel cell (SOFC) interconnects operating on the cathode side. The coated and uncoated steel samples were oxidized in air at 1073 K for 500 h, and their microstructures as well as electrical resistances were evaluated using X-ray diffraction, atomic force microscopy, scanning electron microscopy coupled with energy-dispersive X-ray spectroscopy, and the 2-probe 4-point direct current method. It was demonstrated that the Co coating had reduced the oxidation rate of the steel by nearly a half. The area-specific resistance value of the coated steel was 5 × 10{sup −6} Ω·m{sup 2}, which was significantly lower than that of bare steel after 350 h of oxidation at 1073 K. Cr vaporization tests showed that the Co coating was efficient at blocking the outward diffusion of Cr. The obtained results prove that steel coated with a thin film of cobalt was suitable for use as metallic interconnect material in SOFCs operating at intermediate temperatures. - Highlights: • Co layer was deposited on ferritic steel by means of pulsed laser deposition. • Coated and bare ferritic steel samples were exposed to air at 1073 K for 500 h. • Scale growth rate on bare steel is higher than that on coated steel. • Electrical resistance for oxidized coated steel was lower than for bare steel. • Co-coated steel effectively reduced the formation of volatile Cr species.

  11. Analysis of ductile-brittle transition shifts for standard and miniature bending specimens of irradiated steel

    International Nuclear Information System (INIS)

    Korshunov, M.E.; Korolev, Yu.N.; Krasikov, E.A.; Gabuev, N.N.; Tykhmeev, D.Yu.

    1996-01-01

    A study is made to reveal if there is a correlation between shifts in temperature curves obtained when testing thin plates and standard specimens on impact bending and fracture toughness. The tests were carried out using steel 25Kh3NM specimens irradiated by 6 x 10 19 cm -2 neutron fluence. A conclusion is made about the possibility to evaluate the degree of radiation-induced embrittlement of reactor steels on the basis of thin plate testing under quasistatic loads [ru

  12. Characterization of sensitization and stress corrosion cracking behavior of stabilized stainless steels under BWR conditions

    International Nuclear Information System (INIS)

    Kilian, R.; Ilg, U.; Meier, V.; Teichmann, H.; Wachter, O.

    1995-01-01

    Stress corrosion cracking occurs if the three parameters -- material condition, tensile stress and water chemistry -- are in a critical range. In this study the material conditions especially of Ti- and Nb-stabilized steels are considered. The purpose of this work is to show the influence of the degree of sensitization of Ti- and Nb-stabilized stainless steels on stress corrosion cracking susceptibility in BWR water chemistry. This is an on-going research program. Preliminary results will be presented. Different types of stabilized, and for comparison unstabilized, stainless steels are examined in various heat treatment conditions with regard to their sensitization behavior by EPR tests (double loop) and TEM. The results are plotted in sensitization diagrams. The sensitization behavior depends on many parameters such as carbon content, stabilization element, stabilization ratio and materials history, e.g. solution heat treatment or cold working. The obtained EPR sensitization diagrams are compared with the well known sensitization diagrams from the literature, which were determined by standard IC test according to e.g. German standard DIN 50914 (equivalent to ASTM A 262, Pract. E). Based on the obtained EPR sensitization diagrams material conditions for SSRT tests were selected. The EPR values (Ir/Ia x 100%) of the tested Ti-stabilized stainless steel are in the range of ∼ 0.1--20%. The SSRT tests are carried out in high-temperature water with 0.4 ppm O 2 , a conductivity of 0.5 microS/cm and a strain rate of 1x10 -6-1 . The test temperature is 280 C. Ti-stabilized stainless steel with Ir/Ia x 100% > 1% suffered intergranular stress corrosion cracking under these conditions. The SCC tests for Nb-stabilized stainless steel are still in progress. The correlation between EPR value, chromium depletion and SSRT result will be shown for a selected material condition of sensitized Ti-stabilized stainless steel

  13. Effect of zirconium on the structure and phase composition of steel 03Kh8SYu

    International Nuclear Information System (INIS)

    Tarzhumanova, V.A.; Ryabchenkov, A.V.; Shatunova, A.V.; Yoganova, S.A.

    1986-01-01

    Previously, the authors determined the optimum zirconium content providing retention of a fine-grained structure for steel 03Kh8SYu during high-temperature heating. It was suggested that this was caused by separation in the steel of intermetallic phase Fe 3 Zr. This paper presents results of further studies in this direction. X-ray analysis results for the anodic residues of the steels are presented. It can be seen that in steel without zirconium, carbides of the type M 23 C 6 and M 7 C 3 and aluminum nitride are present. On adding 0.05% Zr, zirconium nitride forms in addition to the existing aluminum nitride and carbides of the type M 7 C 3 . The authors also investigated the effect of zirconium on the tendency of the steel toward grain growth at higher temperature; they studied the structure of steel 03Kh8SYu with 0.61% Zr after soaking specimens for 100 h at 950-1100 C. Results are presented

  14. Boron steel. I Part. Preparation

    International Nuclear Information System (INIS)

    Jaraiz Franco, E.; Esteban Hernandez, J. A.

    1960-01-01

    With the advent of the first nuclear reactors arise the need for control rods and shielding duties for some types of radiations. One of the materials used for this purpose has been the high boron steel. This paper describes the melting and casting procedures employed for the production, at laboratory scale, of steels with Boron content ranging from 1 to 4 per cent, as well as the metallographic and X-Ray techniques used for the identification of the present phases. The electrolytic technique employed for the isolation of the Fe 2 B phase and its subsequent X-Ray identification has proved to be satisfactory. (Author) 11 refs

  15. Microstructure evolution and mechanical properties of X12CrMoWVNbN10-1-1 steel during quenching and tempering process

    Directory of Open Access Journals (Sweden)

    Xingang Tao

    2016-01-01

    Full Text Available The effect of heat treatments was investigated on the microstructure evolution and mechanical properties of X12CrMoWVNbN10-1-1 steel. The as-received steel was austenitized at 1080 °C for 16 h and cooled in furnace, following tempered in two steps, i.e. at 570 °C for 18 h and then at 690 °C for 24 h. The austenitized sample had a typical lath martensite structure with some retained austenite and no delta ferrite was observed after austenitization. After the first tempering at 570 °C, there was no retained austenite remained but it resulted in the forming of precipitates, such as Cr-rich M7C3, Cr-rich M23C6, Cr-rich M2N, Nb-rich MN, and the subgrain, as well as the reduction in dislocation density. However, microstructure observation after secondary tempering proved the further arrangement of dislocation, subgrain growth and the coarsening of precipitates. Hardness and impact tests were carried out for establishing a correlation between microstructure and mechanical properties. Finally, a careful fractographic analysis of impact samples had been done using SEM and EDS.

  16. Research on atmospheric corrosion of steel using synchrotron radiation

    International Nuclear Information System (INIS)

    Yamashita, M.; Uchida, H.; Konishi, H.; Mizuki, J.

    2004-01-01

    Correlation between local structure around Cr in the protective rust layer on weathering steel and protective performance of the rust layer is presented as an example of corrosion research using synchrotron radiation which has recently been applied in various research fields as a useful tool. In addition, in situ observation of initial process of rust formation on steel is also mentioned. It was pointed out by considering the X-ray absorption fine structure spectra that the nanostructure of the protective rust layer on weathering steel primarily comprises of small Cr-goethite crystals containing surface adsorbed and/or intergranular CrO x 3-2X complex anions. This CrO x 3-2X explains the protective performance of the rust layer originated by dense aggregation of fine crystals with cation selectivity of the Cr-goethite. It is very advantageous to employ white X-rays for in situ observation of rusting process of a carbon steel covered with electrolyte thin films because rust structure might change very quickly. This in situ observation revealed the effect of ion species on the change in rust phase during wet/dry repeating. It can be said that application of synchrotron radiation on corrosion research is so useful to understand the nanostructure of surface oxides which closely relate to corrosion behavior of metals and alloys. (author)

  17. Stress corrosion (Astm G30-90 standard) in 08x18H10T stainless steel of nuclear fuel storage pool in WWER reactors

    International Nuclear Information System (INIS)

    Herrera, V.; Zamora R, L.

    1997-01-01

    At the water storage of the irradiated nuclear fuel has been an important factor in its management. The actual pools have its walls covered with inoxidable steel and heat exchangers to dissipate the residual heat from fuel. It is essential to control the water purity to eliminate those conditions which aid to the corrosion process in fuel and at related components. The steel used in this research was obtained from an austenitic inoxidizable steel standardized with titanium 08x18H10T (Type 321) similar to one of the two steel coatings used to cover walls and the pools floor. the test consisted in the specimen deformation through an U ply according to the Astm G30-90 standard. The exposition of the deformed specimen it was realized in simulated conditions to the chemical regime used in pools. (Author)

  18. Laser cladding of Colmonoy 6 powder on AISI316L austenitic stainless steel

    International Nuclear Information System (INIS)

    Zhang, H.; Shi, Y.; Kutsuna, M.; Xu, G.J.

    2010-01-01

    Stainless steels are widely used in nuclear power plant due to their good corrosion resistance, but their wear resistance is relatively low. Therefore, it is very important to improve this property by surface treatment. This paper investigates cladding Colmonoy 6 powder on AISI316L austenitic stainless steel by CO 2 laser. It is found that preheating is necessary for preventing cracking in the laser cladding procedure and 450 o C is the proper preheating temperature. The effects of laser power, traveling speed, defocusing distance, powder feed rate on the bead height, bead width, penetration depth and dilution are investigated. The friction and wear test results show that the friction coefficient of specimens with laser cladding is lower than that of specimens without laser cladding, and the wear resistance of specimens has been increased 53 times after laser cladding, which reveals that laser cladding layer plays roles on wear resistance. The microstructures of laser cladding layer are composed of Ni-rich austenitic, boride and carbide.

  19. Evaluation of stresses generated in steel finger joint of bridge by X-ray stress measurement

    International Nuclear Information System (INIS)

    Kohri, Ami; Kawano, Yutaka; Nishido, Takayuki

    2017-01-01

    In a steel bridge, the evaluation of the stress generated in the finger joint without a gap to absorb temperature change can be an index when evaluating the remaining life. This study chose as the object the finger joint of a diagonal bridge, where the generated stress state is considered to be more complicated, prepared a finger joint test specimen that simulated an actual part, and performed a load test. For judgment, FEM analysis, non-destructive X-ray stress measurement, and measurement of the generated stress using strain gauge were applied. Compared with the FEM analysis results, the difference in the stress value was generated due to the difference in the contact state, but the trends of the stress distribution were equivalent. In addition, the same measurement value as the strain gauge was obtained, and the validity of the X-ray stress measurement method was confirmed. As a result, it was found that the stress measurement method by X-ray is effective for measuring the generated stress including the residual stress of the finger joint without gap at a bridge. (A.O.)

  20. Study on Sintering Mechanism of Stainless Steel Fiber Felts by X-ray Computed Tomography

    Directory of Open Access Journals (Sweden)

    Jun Ma

    2016-01-01

    Full Text Available The microstructure evolution of Fe-17 wt. % Cr-12 wt. % Ni-2 wt. % Mo stainless steel fiber felts during the fast sintering process was investigated by the synchrotron radiation X-ray computed tomography technique. The equation of dynamics of stable inter-fiber neck growth was established for the first time based on the geometry model of sintering joints of two fibers and Kucsynski’s two-sphere model. The specific evolutions of different kinds of sintering joints were observed in the three-dimensional images. The sintering mechanisms during sintering were proposed as plastic flow and grain boundary diffusion, the former leading to a quick growth of sintering joints.

  1. Relações de reciprocidade: o desempenho militar na lógica de arrecadação de recursos-guerra contra artigas (1811-1820 = Relations of reciprocity: the military perfomance in the logic of raise of resources - war against artigas (1811-1820

    Directory of Open Access Journals (Sweden)

    Corrêa, Mariana Milbradt

    2014-01-01

    Full Text Available Este artigo é um estudo de correspondências que narravam enfrentamentos armados durante o período relativo à Guerra contra Artigas (1811-1820 nos confins meridionais do Império Português na América. O trabalho é feito através da análise de correspondências pertencente ao Fundo Guerra do Arquivo Nacional do Rio de Janeiro. Selecionamos ofícios em que os comandantes de campo narravam às vitórias obtidas contra as tropas de Artigas. Interrogamos as implicações da presença nesses relatos de uma exaltação dos comandantes e regimentos militares vitoriosos. Diante da endemia bélica que vivia essa região à época analisada, consideramos que um estudo dos sucessos militares, que permitiram ao Império Português se estender, conquistar e garantir o domínio de suas fronteiras é essencial para compreender uma das formas de conquista de poder nessa sociedade, e as relações que se fundavam no bom desempenho na guerra. Mais do que um procedimento comum, as consagrações presentes nas cartas parecem ter um sentido, inserindo-se em uma lógica de relações de reciprocidade, na qual a elite militar ao mesmo tempo em que lutava em nome de Sua Majestade e sustentava a fronteira do império português angariava para si terras e prestígio que permitiam a reprodução da mesma lógica regionalmente. Essa analise parte do projeto financiado pelo CNPQ: Potentados regionais, sociedade e construção do Estado no Brasil: um estudo a partir da fronteira meridional (1811-1865, coordenado por Luís A. Farinatti

  2. Development and evaluation of a cleanable high efficiency steel filter

    International Nuclear Information System (INIS)

    Bergman, W.; Larsen, G.; Weber, F.; Wilson, P.; Lopez, R.; Valha, G.; Conner, J.; Garr, J.; Williams, K.; Biermann, A.; Wilson, K.; Moore, P.; Gellner, C.; Rapchun, D.; Simon, K.; Turley, J.; Frye, L.; Monroe, D.

    1993-01-01

    We have developed a high efficiency steel filter that can be cleaned in-situ by reverse air pulses. The filter consists of 64 pleated cylindrical filter elements packaged into a 6l0 x 6l0 x 292 mm aluminum frame and has 13.5 m 2 of filter area. The filter media consists of a sintered steel fiber mat using 2 μm diameter fibers. We conducted an optimization study for filter efficiency and pressure drop to determine the filter design parameters of pleat width, pleat depth, outside diameter of the cylinder, and the total number of cylinders. Several prototype cylinders were then built and evaluated in terms of filter cleaning by reverse air pulses. The results of these studies were used to build the high efficiency steel filter. We evaluated the prototype filter for efficiency and cleanability. The DOP filter certification test showed the filter has a passing efficiency of 99.99% but a failing pressure drop of 0.80 kPa at 1,700 m 3 /hr. Since we were not able to achieve a pressure drop less than 0.25 kPa, the steel filter does not meet all the criteria for a HEPA filter. Filter loading and cleaning tests using AC Fine dust showed the filter could be repeatedly cleaned by reverse air pulses. The next phase of the prototype evaluation consisted of installing the unit and support housing in the exhaust duct work of a uranium grit blaster for a field evaluation at the Y-12 Plant in Oak Ridge, TN. The grit blaster is used to clean the surface of uranium parts and generates a cloud of UO 2 aerosols. We used a 1,700 m 3 /hr slip stream from the 10,200 m 3 /hr exhaust system

  3. Elastic-plastic fracture analysis of carbon steel piping using the latest CEGB R6 approach

    International Nuclear Information System (INIS)

    Kanno, S.; Hasegawa, K.; Shimizu, T.; Kobayashi, H.

    1991-01-01

    The elastic-plastic fracture of carbon steel piping having various pipe diameters and circumferential crack angles and subjected to a bending moment is analyzed using the latest United Kingdom Central Electricity Generating Board R6 approach. The elastic-plastic fracture criterion must be applied instead of the plastic collapse criterion with increase of the pipe diameter and the crack angle. A simplified elastic-plastic fracture analysis procedure based on the R6 approach is proposed. (author)

  4. The effect of nickel on the mechanical behavior of molybdenum P/M steels

    International Nuclear Information System (INIS)

    Gething, B.A.; Heaney, D.F.; Koss, D.A.; Mueller, T.J.

    2005-01-01

    This study has examined the effects of nickel alloying additions on the microstructural characteristics and mechanical properties of Fe-xNi-0.85Mo-0.4C-base steels that were powder processed using double-press double-sinter processing to maximize density. The steels were examined in the as-processed condition as well as in a quench-and-temper heat treated condition. Tensile behavior indicates that while nickel content (at levels of 2,4, and 6%) increased tensile strength in the as-sintered condition, it did not significantly affect tensile strength in the quenched and tempered condition. In both conditions increasing Ni content decreased elongation to fracture. The 4% Ni steel, which tended to have the smallest maximum pore size, also exhibited the greatest fatigue strength

  5. Czochralski growth and optical properties of Li 6Gd 1-xEu x(BO 3) 3 ( x=0-1) single crystals

    Science.gov (United States)

    Yavetskiy, R. P.; Dolzhenkova, E. F.; Dubovik, M. F.; Korshikova, T. I.; Tolmachev, A. V.

    2005-04-01

    It was shown that a continuous series of Li 6Gd 1-xEu x(BO 3) 3 solid solutions exist within the whole concentration range ( x=0-1). Li 6Gd 1-xEu x(BO 3) 3 ( x=0-0.03; 1) single crystals up to 25 mm in length and up to 20 mm in diameter have been grown by the Czochralski method. The structural perfection of the crystals has been estimated from etch patterns and XPA analysis results. The optical absorption and thermally stimulated luminescence of the grown crystals has been studied.

  6. The Role of the Bainitic Packet in Control of Impact Toughness in a Simulated CGHAZ of X90 Pipeline Steel

    Directory of Open Access Journals (Sweden)

    Bin Guo

    2016-10-01

    Full Text Available X90 pipeline steel was processed with the simulated coarse grain heat affect zone (CGHAZ thermal cycle with heat input varying from 30 kJ/cm to 60 kJ/cm, the microstructures were investigated by means of optical microscope (OM, scanning electron microscope (SEM, electron backscattering diffraction (EBSD, and transmission electron microscope (TEM, and the impact properties were evaluated from the welding thermal cycle treated samples. The results indicate that the microstructure is primarily composed of lath bainite. When decreasing the heat input, both bainite packet and block are significantly refined, and the toughness has an increased tendency due to the grain refinement. The fracture surfaces all present cleavage fracture for the samples with different heat inputs. Moreover, the average cleavage facet size for the CGHAZ is nearly equal to the average bainite packet size, and the bainitic packet boundary can strongly impede the crack propagation, indicating that the bainitic packet is the most effective unit in control of impact toughness in the simulated CGHAZ of X90 pipeline steel.

  7. Polymorphism of perovskite compounds Ba/sub 2/SEsub(0. 67)Wsup(VI)O/sub 6/. 2. The systems Ba/sub 2/Ndsub(0. 67(1-x))Ysub(0. 67x)WO/sub 6/ and Ba/sub 2/Ndsub(0. 67)Wsub(1-x)Usub(x)O/sub 6/

    Energy Technology Data Exchange (ETDEWEB)

    Schnittenhelm, H J; Kemmler-Sack, S [Tuebingen Univ. (Germany, F.R.). Inst. fuer Chemie

    1977-06-01

    In the system Ba/sub 2/Ndsub(0.67(1-x))Ysub(0.67x)WO/sub 6/ the formation of a continuous series of mixed crystals with cubic 1:1 ordered perovskite structure is observed. The existence of a hexagonal modification is confined to the Y-rich side (x => 0.9). In the Ba/sub 2/Ndsub(0.67)Wsub(1-x)Usub(x)O/sub 6/ series only for x =< 0.25 homogeneous cubic perovskites are obtained. In contrast to systems with other rare earths the Nd series show uncommon optical properties.

  8. Soft-martensitic stainless Cr-Ni-Mo steel for turbine rotors in geothermic power stations

    International Nuclear Information System (INIS)

    Schonfeld, K.; Potthast, E.

    1986-01-01

    Steel Grade X5 Cr-Ni-Mo 12 6 containing 0.05% carbon, 12% chromium, 6% nickel, and 1.50% molybdenum is an advantageous material for turbine rotors in geothermic power stations because of its excellent strength and toughness properties in combination with good erosion and corrosion resistance. In terms of the phase diagram, this soft-martensitic steel has its place at the martensite/austenite/ferrite interface. Therefore, its chemical composition must be chosen so as to have a completely martensitic structure after hardening. The manufacture of and the mechanical properties of a turbine rotor 1200 mm in diameter by 5600 mm in length with a finished weight of approximately 21.5 tons are described in detail

  9. Irradiation embrittlement of pressure vessel steels

    International Nuclear Information System (INIS)

    Brumovsky, M.; Vacek, M.

    1975-01-01

    A Standard Research Programme on Irradiation Embrittlement of Pressure Vessel Steels was approved by the Coordinating Meeting on the 12th May 1972 at the Working Group on Engineering Aspects of Irradiation Embrittlement of Pressure Vessel Steels. This Working Group was set up by the International Atomic Energy Agency in Vienna. Seven countries with their research institutes agreed on doing irradiation experiments according to the approved programme on steel A533 B from the U.S. HSST Programme. The Czechoslovak contribution covering tensile and impact testing of non-irradiated steel and steel irradiated at 280degC to 1.3 x 10 23 n/m 2 (E above 1 MeV) is presented in this report. As an additional part the same set of experiments was carried out on two additional steels - A 542 and A 543, made in SKODA Works for comparison of their irradiation embrittlement and hardening with A533 B steel. (author)

  10. Moessbauer spectroscopy and X-ray diffraction study of 304 L stainless steel thin films

    International Nuclear Information System (INIS)

    Boubeker, B.; Eymery, J.P.; Goudeau, P.; Sayouty, E.H.

    1994-01-01

    304 L stainless steel films (SS) were elaborated using an ion-beam sputtering technique. The target material was a sheet of commercial grade 304 L SS. The starting material was first analysed by both conversion electron Moessbauer spectroscopy (CEMS) and X-ray diffraction. The nonmagnetic state and f.c.c. structure of this material were confirmed. The films were deposited on various substrates with thicknesses in the 175-800 nm range. The films are found to have both b.c.c. structure and ferromagnetic character. X-ray diffraction technique was also used in order to determine the residual stresses developed during the deposition process. The second stage of the work is devoted to the evolution of the film structure as a function of annealing treatments. So isochronal and isothermal kinetics at temperatures higher than 913 K have allowed to follow the alpha --> gamma phase transformation using X-ray diffraction and CEMS technique.The X-ray diffractograms reveal the existence of both b.c.c. and f.c.c. phases. Similar results can be deduced from Moessbauer spectra due to the single line coming from the non-magnetic phase and the sextet coming from the ferromagnetic phase. In addition the CEMS spectra reveal that the ferromagnetic component is split into two parts which indicates the existence of two iron sites. 1 fig., 4 refs.(author)

  11. Progress in measurement of (n,x) cross sections at HST in 1995

    Energy Technology Data Exchange (ETDEWEB)

    Bangjiao, Ye; Zhongmin, Wang; Yangmei, Fan; Rongdian, Han; Xiaoqi, Yu; Huaijiang, Du [Department of Modern Physics, Univ. of Sci. and Tech. of China (China)

    1996-06-01

    The measurement of energy spectrum and angular distributions of protons emission from reaction induced by 14.6 MeV neutron bombarding stainless steel has been performed at Univ. of Sci. and Tech. of China, Hefei (HST) by using multitelescope system. 14.6 MeV neutrons were produced by 150 KeV Cockcroft-Walton accelerator. The 1Cr18Ni9Ti (type 321) stainless steel target with 0.8 mm thick and 40 mm height was used. The progress on measurement of {sup nat}Ni(n,x{alpha}) reaction cross sections are introduced. (2 figs.).

  12. Passivating action of an organic inhibitor on the steel of reinforced concrete

    International Nuclear Information System (INIS)

    Anzola, E.; Malave, R.; Barrios, V.; Villarroel, D.; Tiso, A.; Parra, M.

    2003-01-01

    An electrochemical evaluation has been made on a concrete mix with an organic inhibitor added, in order to establish its contribution to the formation of a protective film on the steel surface. Concrete cylinders (6''x ), each with a 3/8 steel bar and two graphite electrodes embedded, with two water/cement ratios (0.40 and 0.55) were used as testing samples. Reinforced steel bars, both chemically cleaned and in the as rolled condition, embedded in salted and unsalted concrete mixes, were used to test if chemical adsorption occurs in each condition. Samples were soaked into brine solution during 365 days as to simulate a sea environment. During exposure period readings of potential, corrosion rate and potentiodynamical cyclic curves were made. It can be, concluded that the organic inhibitor needs a low water(cement ratio mix (0.40) in order to react via a chemical adsorption on the steel, being more effective on cleaned surfaces. (Author) 10 refs

  13. Effect of silicon ion implantation upon the structure and corrosion resistance of the surface layer of stainless steel 316L, Vitalium and titanium alloy Ti6Al14V

    International Nuclear Information System (INIS)

    Baszkiewicz, J.; Kaminski, M.; Krupa, D.; Kozubowski, J.; Barcz, A.; Gawlik, A.; Jagielski, J.

    1995-01-01

    Samples of 316L stainless steel, Vitalium and Ti6A14V titanium alloy have been implanted with doses of 1.5, 3, and 4.5 x 10 17 Si + /cm 2 . Transmission electron microscopy shows that during ion implantation amorphous layers are formed. When samples of titanium alloy were implanted with a dose of 0.5 x 10 17 Si + /cm 2 , the implanted layer consisted of a dispersion of fine silicide crystallites instead of being amorphous. The corrosion resistance was analyzed by electrochemical techniques in 0.9% NaCl at the temperature of 37 C. The increase of corrosion resistance has been observed as a result of structural modifications of the surface layer. (author). 7 refs, 4 tabs

  14. USAGE OF PRESSURE OSCILLATIONS OF FLUCTUATING GAS FLOW FOR HANDLING OF 40X HARDENED STEEL SAMPLES

    Directory of Open Access Journals (Sweden)

    E. E. Il'ina

    2016-07-01

    Full Text Available Subject of Research. The paper deals with experience in the use of advanced technology of aeroacoustic treatment of materials for impact toughness improvement of the 40X type constructional steel samples. The method is based on the influence of pulsating air stream with oscillating shock-wave structures on the sample. As a result, the so-called Maxwell's waves are generated in the sample, that can lead to a beneficial transformation in the micro- and substructure and also in the phase structure of hardened steels. Obtained changes may be enough to improve impact toughness and decrease the residual stresses that arise in the course of previous treatments. Distortion of components decreases in this case, and failure probability becomes lower at the further treatment and operation. The advantage of technology is elimination of the additional heat treatment, for example, of the relaxation annealing that serves to reduce the residual stresses. This can be useful, particularly, for the preservation of high hardness and wear resistance, obtained by hardening and low-temperature tempering (about 200 ° C, as the relaxation annealing has typically a higher temperature and will result in their reduction. The toughness increase of the samples is assumed as an indicator of the positive impact of the considered treatment. Main Results. We have defined characteristics and modes of experimental acoustic transducer implementing the aeroacoustic processing. Experiments have been carried out on the impact assessment of aeroacoustic effects on the toughness of widely used 40X type steel. The obtained results enable to suggest that the application of aeroacoustic treatment for samples hardened by heat treatment leads to the toughness increasing of the investigated material. In this case an increased value of hardness obtained after heat treatment is maintained. Practical Relevance. The results supplement previously obtained experimental data for aeroacoustic

  15. Combined Effect of Alternating Current Interference and Cathodic Protection on Pitting Corrosion and Stress Corrosion Cracking Behavior of X70 Pipeline Steel in Near-Neutral pH Environment

    Directory of Open Access Journals (Sweden)

    Liwei Wang

    2018-03-01

    Full Text Available Influence of alternating current (AC on pitting corrosion and stress corrosion cracking (SCC behavior of X70 pipeline steel in the near-neutral pH environment under cathodic protection (CP was investigated. Both corrosion and SCC are inhibited by −0.775 VSCE CP without AC interference. With the superimposition of AC current (1–10 mA/cm2, the direct current (DC potential shifts negatively under the CP of −0.775 VSCE and the cathodic DC current decreases and shifts to the anodic direction. Under the CP potential of −0.95 VSCE and −1.2 VSCE, the applied AC current promotes the cathodic reaction and leads to the positive shift of DC potential and increase of cathodic current. Local anodic dissolution occurs attributing to the generated anodic current transients in the positive half-cycle of the AC current, resulting in the initiation of corrosion pits (0.6–2 μm in diameter. AC enhances the SCC susceptibility of X70 steel under −0.775 VSCE CP, attributing to the promotion of anodic dissolution and hydrogen evolution. Even an AC current as low as 1 mA/cm2 can enhance the SCC susceptibility.

  16. Nitrogen effect on the tendency of Cr-Ni-MN steels to delayed fracture under stress and hydrogen effects

    International Nuclear Information System (INIS)

    Suvorova, S.O.; Fillipov, G.A.

    1996-01-01

    Austenitic steels types 03Kh17N16G10AM5, 03Kh6N12G10AM5 and 07Kh13AG20 with various nitrogen contents were studied for their tendency to delayed fracture using mechanical tests, fractography and X ray diffraction analysis. The steel type 07Kh13G20 exhibited the highest strength in the initial state but showed an increase tendency to delayed fracture after hydrogenation. It is underlined that nitrogen additions essentially intensify the tendency of cold worked steels to delayed fracture. This fact should be taken into account when using nitrogen-containing Cr-Ni-Mn steels under severe operational conditions. 4 refs., 2 tabs

  17. Characterization of D2 tool steel friction surfaced coatings over low carbon steel

    International Nuclear Information System (INIS)

    Sekharbabu, R.; Rafi, H. Khalid; Rao, K. Prasad

    2013-01-01

    Highlights: • Solid state coating by friction surfacing method. • D2 tool steel is coated over relatively softer low carbon steel. • Defect free interface between tool steel coating and low carbon steel substrate. • D2 coatings exhibited higher hardness and good wear resistance. • Highly refined martensitic microstructure in the coating. - Abstract: In this work D2 tool steel coating is produced over a low carbon steel substrate using friction surfacing process. The process parameters are optimized to get a defect free coating. Microstructural characterization is carried out using optical microscopy, scanning electron microscopy and X-ray diffraction. Infrared thermography is used to measure the thermal profile during friction surfacing of D2 steel. Wear performance of the coating is studied using Pin-on-Disk wear tests. A lower rotational speed of the consumable rod and higher translational speed of the substrate is found to result in thinner coatings. Friction surfaced D2 steel coating showed fine-grained martensitic microstructure compared to the as-received consumable rod which showed predominantly ferrite microstructure. Refinement of carbides in the coating is observed due to the stirring action of the process. The infrared thermography studies showed the peak temperature attained by the D2 coating to be about 1200 °C. The combined effect of martensitic microstructure and refined carbides resulted in higher hardness and wear resistance of the coating

  18. Stress corrosion evaluation on stainless steel 304 pipes in Laguna Verde Nuclear Power Plant

    International Nuclear Information System (INIS)

    Arganis J, C.R.

    1996-01-01

    Inside the frame of the project IAEA/MEX-41044 'Stress corrosion as a starting event of accidents in nuclear plants', and of the institutional project IA-252 under the same name, it was required from the Laguna Verde Nuclear Plant, material equivalent to the one employed in the piping of the primary recycling system. Laguna Verde Nuclear Plant granted two tracks of tubes, that could be used to substitute the ones that are in operation, as is the tube SA-358TP304 CL-QC with transversal welding, designated as ER-316-LQA. According to the report entitles 'Revision of the operational experience related to corrosion in the nuclear plants' it was found that the stress corrosion is the principal mechanism of corrosion present in the nuclear plants. Previous records indicate that sensitized stainless steels are resistant to stress corrosion in testings of constant loading in sea water (3.5% of chlorides approximately) to 80 Centigrade and to 80% of the limit of conveyance and that a solution of 22% of NaCl to 90 Centigrade, produces cracking due to stress corrosion in highly sensitized steels, in tests of speed of slow extension (SSRT), to a speed of 1x10 -6 s -1 . Daniels reports that there is a direct relation between the speed limit of detection of the SSRT test and the concentration of chlorides, for stainless steels tested to 100 Centigrade. The minimum detection speed of susceptibility to stress corrosion for solution to 20% of NaCl, is of 1x10 -7 s -1 . Taking into account these considerations, the employment of a solution with 22% of NaCl to 90 Centigrade to a speed of 1x10 -6 s -1 seems a good choice for the evaluation of stainless steel. (Author)

  19. Fatigue properties of X80 pipeline steels with ferrite/bainite dual-phase microstructure

    Energy Technology Data Exchange (ETDEWEB)

    Zhao, Zuo-peng [Key Lab of Metastable Materials Science & Technology and College of Materials Science & Engineering, Yanshan University, Qinhuangdao 066004 (China); Qiao, Gui-ying [Key Lab of Metastable Materials Science & Technology and College of Materials Science & Engineering, Yanshan University, Qinhuangdao 066004 (China); Key Lab of Applied Chemistry of Hebei Province and School of Environment and Chemical Engineering, Yanshan University, Qinhuangdao 066004 (China); Tang, Lei [Key Lab of Applied Chemistry of Hebei Province and School of Environment and Chemical Engineering, Yanshan University, Qinhuangdao 066004 (China); Zhu, Hong-wei; Liao, Bo [Key Lab of Metastable Materials Science & Technology and College of Materials Science & Engineering, Yanshan University, Qinhuangdao 066004 (China); Xiao, Fu-ren, E-mail: frxiao@ysu.edu.cn [Key Lab of Metastable Materials Science & Technology and College of Materials Science & Engineering, Yanshan University, Qinhuangdao 066004 (China)

    2016-03-07

    Fatigue properties are important parameters for the safety design and security evaluation of gas transmission pipelines. In this work, the fatigue life at different stresses of full-thickness X80 pipeline steel plates with a ferrite/bainite dual-phase microstructure was investigated using a MTS servo-hydraulic universal testing machine; the fatigue crack propagation rate was examined with CT specimens by using an INSTRON 8874 testing machine. Results indicate that fatigue life increases as maximum stress decreases; as the maximum stress decreases to the maximum operating stress (440 MPa), the fatigue life is approximately 4.2×10{sup 5} cycles. The fatigue crack of the full-thickness fatigue life specimens is generated at the surface of rolled steel plates and then the crack propagates and grows inward until a fracture is formed. During fatigue crack growth, a transitional turning point appears in the curve of da/dN with ΔK in the Paris region. The transitional turning point that divides the Paris region to two stages is approximately ΔK≅30 MPa m{sup 1/2}. The change in the growth rate (da/dN) is related to the variation of the crack path and in the fracture mode because of the possible microstructural sensitivity of fatigue crack propagation behavior. This study also discussed the effect of duple phase ferrite/bainite microstructure on fatigue crack initiation and propagation.

  20. Fatigue properties of X80 pipeline steels with ferrite/bainite dual-phase microstructure

    International Nuclear Information System (INIS)

    Zhao, Zuo-peng; Qiao, Gui-ying; Tang, Lei; Zhu, Hong-wei; Liao, Bo; Xiao, Fu-ren

    2016-01-01

    Fatigue properties are important parameters for the safety design and security evaluation of gas transmission pipelines. In this work, the fatigue life at different stresses of full-thickness X80 pipeline steel plates with a ferrite/bainite dual-phase microstructure was investigated using a MTS servo-hydraulic universal testing machine; the fatigue crack propagation rate was examined with CT specimens by using an INSTRON 8874 testing machine. Results indicate that fatigue life increases as maximum stress decreases; as the maximum stress decreases to the maximum operating stress (440 MPa), the fatigue life is approximately 4.2×10"5 cycles. The fatigue crack of the full-thickness fatigue life specimens is generated at the surface of rolled steel plates and then the crack propagates and grows inward until a fracture is formed. During fatigue crack growth, a transitional turning point appears in the curve of da/dN with ΔK in the Paris region. The transitional turning point that divides the Paris region to two stages is approximately ΔK≅30 MPa m"1"/"2. The change in the growth rate (da/dN) is related to the variation of the crack path and in the fracture mode because of the possible microstructural sensitivity of fatigue crack propagation behavior. This study also discussed the effect of duple phase ferrite/bainite microstructure on fatigue crack initiation and propagation.

  1. Creep-Rupture Properties and Corrosion Behaviour of 21/4 Cr-1 Mo Steel and Hastelloy X-Alloys in Simulated HTGR Environment

    DEFF Research Database (Denmark)

    Lystrup, Aage; Rittenhouse, P. L.; DiStefano, J. R.

    Hastelloy X and 2/sup 1///sub 4/ Cr-1 Mo steel are being considered as structural alloys for components of a High-Temperature Gas-Cooled Reactor (HTGR) system. Among other mechanical properties, the creep behavior of these materials in HTGR primary coolant helium must be established to form part...

  2. Monitoring of Fatigue Degradation in Austenitic Stainless Steels

    International Nuclear Information System (INIS)

    Kalkhof, D.; Niffenegger, M.; Leber, H.J.

    2004-01-01

    During cyclic loading of austenitic stainless steel, it was observed that microstructural changes occurred; these affect both the mechanical and physical properties of the material. For certain steels, a strain-induced martensite phase transformation was seen. The investigations showed that, for the given material and loading conditions, the volume fraction of martensite depends on the cycle number, temperature and initial material state. It was also found that the martensite content continuously increased with the cycle number. Therefore, the volume fraction of martensite was used as an indication of fatigue usage. It was noted that the temperature dependence of the martensite formation could be described by a Boltzmann function, and that the martensite content decreased with increasing temperature. Two different heats of the austenitic stainless steel X6CrNiTi18-10 (AISI 321, DIN 1.4541) were investigated. It was found that the martensite formation rate was much higher for the cold-worked than for the solution-annealed material. All applied techniques - neutron diffraction and advanced magnetic methods - were successful in detecting the presence of martensite in the differently fatigued specimens. (author)

  3. Kinetics of electrochemical boriding of low carbon steel

    International Nuclear Information System (INIS)

    Kartal, G.; Eryilmaz, O.L.; Krumdick, G.; Erdemir, A.; Timur, S.

    2011-01-01

    In this study, the growth kinetics of the boride layers forming on low carbon steel substrates was investigated during electrochemical boriding which was performed at a constant current density of 200 mA/cm 2 in a borax based electrolyte at temperatures ranging from 1123 K to 1273 K for periods of 5-120 min. After boriding, the presence of both FeB and Fe 2 B phases were confirmed by the X-ray diffraction method. Cross-sectional microscopy revealed a very dense and thick morphology for both boride phases. Micro hardness testing of the borided steel samples showed a significant increase in the hardness of the borided surfaces (i.e., up to (1700 ± 200) HV), while the hardness of un-borided steel samples was approximately (200 ± 20) HV. Systematic studies over a wide range of boriding time and temperature confirmed that the rate of the boride layer formation is strongly dependent on boriding duration and has a parabolic character. The activation energy of boride layer growth for electrochemical boriding was determined as (172.75 ± 8.6) kJ/mol.

  4. Initiation and growth of thermal fatigue crack networks in an AISI 304 L type austenitic stainless steel (X2 CrNi18-09); Amorcage et propagation de reseaux de fissures de fatigue thermique dans un acier inoxydable austenitique de type X2 CrNi18-09 (AISI 304 L)

    Energy Technology Data Exchange (ETDEWEB)

    Maillot, V

    2004-07-01

    We studied the behaviour of a 304 L type austenitic stainless steel submitted to thermal fatigue. Using the SPLASH equipment of CEA/SRMA we tested parallelepipedal specimens on two sides: the specimens are continuously heated by Joule effect, while two opposites faces are cyclically. cooled by a mixed spray of distilled water and compressed air. This device allows the reproduction and the study of crack networks similar to those observed in nuclear power plants, on the inner side of circuits fatigued by mixed pressurized water flows at different temperatures. The crack initiation and the network constitution at the surface were observed under different thermal conditions (Tmax = 320 deg C, {delta}T between 125 and 200 deg C). The experiment produced a stress gradient in the specimen, and due to this gradient, the in-depth growth of the cracks finally stopped. The obtained crack networks were studied quantitatively by image analysis, and different parameters were studied: at the surface during the cycling, and post mortem by step-by-step layer removal by grinding. The maximal depth obtained experimentally, 2.5 mm, is relatively coherent with the finite element modelling of the SPLASH test, in which compressive stresses appear at a depth of 2 mm. Some of the crack networks obtained by thermal fatigue were also tested in isothermal fatigue crack growth under 4-point bending, at imposed load. The mechanisms of the crack selection, and the appearance of the dominating crack are described. Compared to the propagation of a single crack, the crack networks delay the propagation, depending on the severity of the crack competition for domination. The dominating crack can be at the network periphery, in that case it is not as shielded by its neighbours as a crack located in the center of the network. It can also be a straight crack surrounded by more sinuous neighbours. Indeed, on sinuous cracks, the loading is not the same all along the crack path, leading to some

  5. Laser surface pretreatment of 100Cr6 bearing steel – Hardening effects and white etching zones

    International Nuclear Information System (INIS)

    Buling, Anna; Sändker, Hendrik; Stollenwerk, Jochen; Krupp, Ulrich; Hamann-Steinmeier, Angela

    2016-01-01

    Highlights: • Laser surface pretreatment of the bearing steel 100Cr6 is performed. • Microstructural changes of the surface are examined by light microscopy and SEM. • Topographical changes are observed using white light interferometry. • Micro-hardness testing show the existence of very hard white etching zones (WEZ). • WEZ are attributed to near-surface reaustenitization and rapid quenching. • Dark etching zones (DEZ) are found at the laser path edges after laser pretreatment. - Abstract: In order to achieve a surface pretreatment of the bearing steel 100Cr6 (1–1.5 wt.% Cr) a laser-based process was used. The obtained modification may result in an optimization of the adhesive properties of the surface with respect to an anticorrosion polymer coating on the basis of PEEK (poly-ether-ether-ketone), which is applied on the steel surface by a laser melting technique. This work deals with the influence of the laser-based pretreatment regarding the surface microstructure and the micro-hardness of the steel, which has been examined by scanning electron microscopy (SEM), light microscopy and automated micro-hardness testing. The most suitable parameter set for the laser-based pretreatment leads to the formation of very hard white etching zones (WEZ) with a thickness of 23 μm, whereas this pretreatment also induces topographical changes. The occurrence of the white etching zones is attributed to near-surface re-austenitization and rapid quenching. Moreover, dark etching zones (DEZ) with a thickness of 32 μm are found at the laser path edges as well as underneath the white etching zones (WEZ). In these areas, the hardness is decreased due to the formation of oxides as a consequence of re-tempering.

  6. Laser surface pretreatment of 100Cr6 bearing steel – Hardening effects and white etching zones

    Energy Technology Data Exchange (ETDEWEB)

    Buling, Anna, E-mail: a.buling@hs-osnabrueck.de [Faculty of Engineering and Computer Science, University of Applied Sciences, 49009 Osnabrück (Germany); Sändker, Hendrik; Stollenwerk, Jochen [Fraunhofer Institute for Laser Technology ILT, Steinbachstrasse 15, 52074 Aachen (Germany); Krupp, Ulrich; Hamann-Steinmeier, Angela [Faculty of Engineering and Computer Science, University of Applied Sciences, 49009 Osnabrück (Germany)

    2016-08-15

    Highlights: • Laser surface pretreatment of the bearing steel 100Cr6 is performed. • Microstructural changes of the surface are examined by light microscopy and SEM. • Topographical changes are observed using white light interferometry. • Micro-hardness testing show the existence of very hard white etching zones (WEZ). • WEZ are attributed to near-surface reaustenitization and rapid quenching. • Dark etching zones (DEZ) are found at the laser path edges after laser pretreatment. - Abstract: In order to achieve a surface pretreatment of the bearing steel 100Cr6 (1–1.5 wt.% Cr) a laser-based process was used. The obtained modification may result in an optimization of the adhesive properties of the surface with respect to an anticorrosion polymer coating on the basis of PEEK (poly-ether-ether-ketone), which is applied on the steel surface by a laser melting technique. This work deals with the influence of the laser-based pretreatment regarding the surface microstructure and the micro-hardness of the steel, which has been examined by scanning electron microscopy (SEM), light microscopy and automated micro-hardness testing. The most suitable parameter set for the laser-based pretreatment leads to the formation of very hard white etching zones (WEZ) with a thickness of 23 μm, whereas this pretreatment also induces topographical changes. The occurrence of the white etching zones is attributed to near-surface re-austenitization and rapid quenching. Moreover, dark etching zones (DEZ) with a thickness of 32 μm are found at the laser path edges as well as underneath the white etching zones (WEZ). In these areas, the hardness is decreased due to the formation of oxides as a consequence of re-tempering.

  7. Morphological and microstructural studies on aluminizing coating of carbon steel

    Energy Technology Data Exchange (ETDEWEB)

    Samsu, Zaifol; Othman, Norinsan Kamil; Daud, Abd Razak; Hussein, Hishammuddin [School of Applied Physics, Faculty of Science and Technology, Universiti Kebangsaan Malaysia, 43600 Bangi, Selangor (Malaysia)

    2013-11-27

    Hot dip aluminizing is one of the most effective methods of surface protection for steels and is gradually gaining popularity. The morphology and microstructure of an inter-metallic layer form on the surface of low carbon steel by hot dip aluminization treatment had been studied in detail. This effect has been investigated using optical and scanning electron microscopy, and X-ray diffraction. The result shows that the reaction between the steel and the molten aluminium leads to the formation of Fe–Al inter-metallic compounds on the steel surface. X-ray diffraction and electron microscopic studies showed that a two layer coating was formed consisting of an external Al layer and a (Fe{sub 2}Al{sub 5}) inter metallic on top of the substrate after hot dip aluminizing process. The inter-metallic layer is ‘thick’ and exhibits a finger-like growth into the steel. Microhardness testing shown that the intermetallic layer has high hardness followed by steel substrate and the lowest hardness was Al layer.

  8. Properties of half metallic (Ba0.8Sr0.2)2-x La2x/3x/3FeMoO6 double perovskites

    International Nuclear Information System (INIS)

    Serrate, D.; De Teresa, J.M.; Blasco, J.; Morellon, L.; Ibarra, M.R.

    2005-01-01

    Previous work in (Ba 0.8 Sr 0.2 ) 2- x La x FeMoO 6 and Ba 1+ x Sr 1-3 x La 2 x FeMoO 6 have stated electron doping as the most important parameter in terms of T c enhancement. Here we report complementary structural, magnetic and transport properties, say a series where there is no doping and only structural parameters are changed: (Ba 0.8 Sr 0.2 ) 2- x La 2 x /3 x /3 FeMoO 6 . We propose a complete phase diagram where structural and bandfilling impact on the Curie temperature is clearly evidenced

  9. Construction and assembly of pipelines using API 5L grade X80 tubes - considerations to be observed with high-strength steels; Construcao e montagem de dutos terrestres utilizando tubos API 5L Gr. X80

    Energy Technology Data Exchange (ETDEWEB)

    Oliveira, Ailton C. de; Rabello, Jose Mauricio B. [PETROBRAS S.A., Rio de Janeiro, RJ (Brazil)

    2005-07-01

    The use of line pipes API 5L Grade X80, at the point of view of designer allows: reduction of wall thickness and pipe weight or increase of design pressure. In the pipeline construction point of view, the use of line pipes API 5L Grade X80 provide some advantages, however some difficulties must be expected in several stages of the construction and assembly. The implications in cost, productivity, inspection and integrity, with the application of these high resistance steels, complying with PETROBRAS Standard N - 464 Construcao, Montagem e Condicionamento de Dutos Terrestres (Rev. H - 2004 Dec) and the experience consolidated in pipelines construction abroad were presented. At the design stage, a comparison between pipelines designed using API 5L-X70 and API 5L-X80 was carried out approaching the aspects of variation of thickness, pressure design and design factor. An evaluation of the expected gains when choosing API 5L Grade X80 steels were done, regarding reduction of costs and pipe weight. Regarding API 5L-X80 pipe fabrication, the obtained results were reported, proving that this aspect was already overcome, showing the viability of its production in Brazil. Difficulties were detected regarding construction and assembly stage and showing the need of revision of PETROBRAS standard N-464. (author)

  10. Creep rupture of mild steel compact tension test pieces

    International Nuclear Information System (INIS)

    Priddle, E.K.

    1978-10-01

    Creep rupture lives have been determined for compact tension and unnotched tensile test pieces of mild steel at 450 0 C. Three sizes of compact tension specimens were used in which the ratios of reference stress to elastic stress intensity factor were 2.76, 4.78 and 6.6 (msup(-1/2)). The analysis of results in terms of either initial reference stress or stress intensity was unable to reduce the data to a single failure curve. An empirical correlation was found between rupture time and a reference stress/crack length combination where t = 2.46 x 10 20 sub(σref) sup(-8.96) asup(-1.56) (units hours, MPa and metres). This equation has no valid application to materials or specimens other than those from which it was derived. Reported data for 1/2Cr Mo V and 2 1/4Cr Mo steels at 565 0 C were also correlated by this approach. (author)

  11. An influence of active additives on the formation of selected indicators of the condition of the X10CrNi18-8 stainless steel surface layer in MQCL conditions

    Czech Academy of Sciences Publication Activity Database

    Maruda, R. W.; Legutko, S.; Krolczyk, G.; Hloch, Sergej

    2015-01-01

    Roč. 9, č. 5 (2015), s. 452-465 ISSN 1749-785X Institutional support: RVO:68145535 Keywords : emulsion mist * anti-wear modifiers * surface roughness * wear mechanism * MQCL Subject RIV: JQ - Machines ; Tools Impact factor: 0.440, year: 2015 http://www.inderscience.com/jhome.php?jcode=ijsurfse#issue

  12. A study on the redox, spectroscopic, and photophysical characteristics of a series of octahedral hexamolybdenum(ii) clusters: [{Mo6X8}Y6]2- (X, Y = Cl, Br, or I).

    Science.gov (United States)

    Akagi, Soichiro; Fujii, Sho; Kitamura, Noboru

    2018-01-23

    We report a systematic study on the redox, spectroscopic, and photophysical properties of a series of [{Mo 6 X 8 }Y 6 ] 2- (X, Y = Cl, Br, or I. 1-9). All of the [{Mo 6 X 8 }Y 6 ] 2- clusters show intense and long-lived phosphorescence in both CH 3 CN and crystalline phases at 298 K. We found that the emission quantum yields (Φ em ) of 1-9 increase in the sequences X = Cl Br Br Br < Cl for given {Mo 6 X 8 } 4+ -core clusters. The present data demonstrate that arbitrary combinations of X and Y in [{Mo 6 X 8 }Y 6 ] 2- could tune τ em and Φ em in the ranges of 85-300 μs and 0.09-0.47, respectively. Both capping (X) and terminal ligand (Y) effects on the photophysical properties of the clusters are discussed on the basis of the energy gap (i.e., emission energy) dependence of the nonradiative decay rate constant.

  13. Charpy impact behavior of manganese-stabilized martensitic steels

    International Nuclear Information System (INIS)

    Hu, W.L.; Gelles, D.S.

    1986-05-01

    Tests were conducted to evaluate the irradiation-induced shift in ductile-to-brittle transition behavior of two manganese stabilized martensitic steels. Miniature Charpy specimens were fabricated from two heats of steel similar in composition to HT-9 but with 0.1% C and Mn contents ranging from 3.3 to 6.6.%. The 3.3% Mn steel showed a transition temperature similar to that of HT-9 in both the unirradiated condition and in specimens irradiated to 11.3 dpa. The steel containing 6.6% Mn exhibited a higher transition temperature after irradiation than the steel containing 3.3% Mn. The upper shelf energy (USE) after irradiation for the manganese stabilized alloys was much higher than for HT-9. 6 refs., 3 figs., 2 tabs

  14. TEM characterization on new 9% Cr advanced steels thermomechanical treated after tempering

    Science.gov (United States)

    Fernández, P.; Hoffmann, J.; Rieth, M.; Roldán, M.; Gómez-Herrero, A.

    2018-03-01

    Phase transformation on new six reduced activation ferritic/martensitic steels (RAFMs) was investigated to provide the basis for the design and development of advanced steels to maintain adequate strength and creep resistance above 500 °C. The new alloys are designed to increase the amount of fine MX precipitates and reduce coarse M23C6 carbides through alloy composition refinement and the application of thermomechanical treatments. The microstructural investigations by TEM have shown M23C6, M2X, and MX precipitation after tempering at 700 °C/2h with low dislocation recovery, while at 825 °C/2h the martensite developed to subgrain formation and growth. At this stage, only M23C6 and MX were detected. Preliminary results demonstrate that it is feasible to produce fine MX strengthened particles dispersed in the matrix with further optimization of tempering treatments.

  15. Kinetics analysis of two-stage austenitization in supermartensitic stainless steel

    DEFF Research Database (Denmark)

    Nießen, Frank; Villa, Matteo; Hald, John

    2017-01-01

    The martensite-to-austenite transformation in X4CrNiMo16-5-1 supermartensitic stainless steel was followed in-situ during isochronal heating at 2, 6 and 18 K min−1 applying energy-dispersive synchrotron X-ray diffraction at the BESSY II facility. Austenitization occurred in two stages, separated...... that the austenitization kinetics is governed by Ni-diffusion and that slow transformation kinetics separating the two stages is caused by soft impingement in the martensite phase. Increasing the lath width in the kinetics model had a similar effect on the austenitization kinetics as increasing the heating-rate....

  16. The influence of remelting parameters of the electric arc and conventional tempering on the tribological resistance of high speed steel HS 6-5-2

    Directory of Open Access Journals (Sweden)

    A. Dziedzic

    2011-07-01

    Full Text Available The present thesis depicts the results of the research of tribological high speed steel HS 6-5-2 remelted with the electric arc. Steel was remelted with different parameters. The amperage of electric arc was changed, the scanning speed was changed and the single, overlapping remeltings were used. There was also the influence of conventional tempering defined, which was conducted after remelting on the tribological resistance of hardened steel. For the previously mentioned processing variants, the intensity of tribological wear was defined and the linear wear were presented, and the friction coefficients. The type of tribological wear was also given, present during the friction, technically dry, of the hardened steel. The lower intensity of tribological wear was received for the single remelting by electric arc of 50 and 70A. Using the overlapping remeltings for the strengening of the surface layer of the high speed steel HS 6-5-2 causes the increase of the intensity of tribological wear in comparison to the steel with the single remelting. The conventional tempering leads to the decrease of the intensity of tribological wear.

  17. X-ray photoelectron spectroscopy investigation of the carburization of 310 stainless steel

    International Nuclear Information System (INIS)

    Tabet, N.; Allam, I.; Yin, R.C.

    2003-01-01

    The surface of 310 stainless steel (310SS) samples was investigated by X-ray photoelectron spectroscopy (XPS) after 500 h cyclic exposure to two carburizing atmospheres: CH 4 (2%)-H 2 (98%) at 800 deg. C, and CH 4 (10%)-H 2 (90%) at 1100 deg. C. The depth distribution of various elements in the surface region was obtained by XPS after successive cycles of argon etching. The microstructure of the alloy was observed by scanning electron microscopy (SEM) and the phases formed during the exposure were analyzed by X-ray diffraction (XRD). The results showed that the major phases that were formed within few micrometer depth during exposure at 800 deg. C include both iron and chromium carbides. (Mn, Cr) oxide was also formed as a result of the reaction with the residual oxygen of the atmosphere. A region of few microns width that was relatively depleted of chromium was formed under the surface as a result of the outwards diffusion of chromium. The exposure to the reducing atmosphere at 1100 deg. C led to the formation of various iron and chromium carbides. No oxide was formed during exposure. In all exposed samples, the surface was Cr enriched while nickel remained buried under the surface region that reacted with the atmosphere

  18. Two-dimensional and three-dimensional analyses of sigma precipitates and porosity in a superaustenitic stainless steel

    DEFF Research Database (Denmark)

    Fonda, Richard Warren; Lauridsen Mejdal, Erik; Ludwig, W.

    2007-01-01

    X-ray micro-tomography revealed not only the true three-dimensional (3-D) distribution, interconnectivity, and morphology of coarse sigma precipitates in an AL-6XN superaustenitic stainless steel, but also the presence of an internal void network associated with these precipitates. The voids were...

  19. The Microstructure and Properties of Super Martensitic Stainless Steel Microalloyed with Tungsten and Copper

    Science.gov (United States)

    Ye, Dong; Li, Jun; Liu, Yu-Rong; Yong, Qi-Long; Su, Jie; Cao, Jian-Chun; Tao, Jing-Mei; Zhao, Kun-Yu

    2011-06-01

    The microstructure and properties of super martensitic stainless steel (SMSS) microalloyed with tungsten and copper were studied by means of optical microscopy, dilatometer, X-ray diffraction, and tensile tests. The results showed that the microstructure of SMSS, after quenching and tempering, was a typical biphase structure with tempered martensite and reversed austenite dispersedly distributed in the martensite matrix. W and Cu were added into the SMSS to reduce the transformation temperature (Ms) and improve the strength and hardness of the matrix by grain refining and solid solution strengthening. Thermocalc calculations confirmed that M23C6 compound and Laves phase were precipitated during tempering in the investigated steel. Compared with the traditional SMSS, the steel microalloyed with W and Cu performed better mechanical properties.

  20. Diffusion Brazing of Ti-6Al-4V and Stainless Steel 316L Using AgCuZn Filler Metal

    Directory of Open Access Journals (Sweden)

    R. Soltani Tashi

    2013-09-01

    Full Text Available In the present study, vacuum brazing was applied to join Ti-6Al-4V and stainless steel using AgCuZn filler metal. The bonds were characterized by scanning electron microscopy, energy dispersive spectroscopy and X-ray diffraction analysis. Mechanical strengths of the joints were evaluated by the shear test and microhardness. It has been shown that shear strength decreased with increasing the brazing temperature and time. The wettability of the filler alloy was increased by enhancing the wetting test temperature. By increasing the brazing temperature various intermetallic compounds were formed in the bond area. These intermetallic compounds were mainly a combination of CuTi and Fe-Cu-Ti. The shear test results verified the influence of the bonding temperature on the strength of the joints based on the formation of different intermetallics in the bond zone. The fracture analysis also revealed different fracture footpath and morphology for different brazing temperatures.

  1. Combined Synchrotron X-ray Diffraction and Digital Image Correlation Technique for Measurement of Austenite Transformation with Strain in TRIP-assisted Steels

    Energy Technology Data Exchange (ETDEWEB)

    Poling, Whitney A.; Savic, Vesna; Hector, Louis G.; Sachdev, Anil K.; Hu, Xiaohua; Devaraj, Arun; Abu-Farha, Fadi

    2016-04-05

    The strain-induced, diffusionless shear transformation of retained austenite to martensite during straining of transformation induced plasticity (TRIP) assisted steels increases strain hardening and delays necking and fracture leading to exceptional ductility and strength, which are attractive for automotive applications. A novel technique that provides the retained austenite volume fraction variation with strain in TRIP-assisted steels with improved precision is presented. Digital images of the gauge section of tensile specimens were first recorded up to selected plastic strains with a stereo digital image correlation (DIC) system. The austenite volume fraction was measured by synchrotron X-ray diffraction from small squares cut from the gage section. Strain fields in the squares were then computed by localizing the strain measurement to the corresponding region of a given square during DIC post-processing of the images recorded during tensile testing. Results obtained for a QP980 steel are used to study the influence of initial volume fraction of austenite and the austenite transformation with strain on tensile mechanical behavior.

  2. Effects of heat input on mechanical properties of metal inert gas welded 1.6 mm thick galvanized steel sheet

    International Nuclear Information System (INIS)

    Rafiqul, M I; Ishak, M; Rahman, M M

    2012-01-01

    It is usually a lot easier and less expensive to galvanize steel before it is welded into useful products. Galvanizing afterwards is almost impossible. In this research work, Galvanized Steel was welded by using the ER 308L stainless steel filler material. This work was done to find out an alternative way of welding and investigate the effects of heat input on the mechanical properties of butt welded joints of Galvanized Steel. A 13.7 kW maximum capacity MIG welding machine was used to join 1.6 mm thick sheet of galvanized steel with V groove and no gap between mm. Heat inputs was gradually increased from 21.06 to 25.07 joules/mm in this study. The result shows almost macro defects free welding and with increasing heat input the ultimate tensile strength and welding efficiency decrease. The Vickers hardness also decreases at HAZ with increasing heat input and for each individual specimen; hardness was lowest in heat affected zone (HAZ), intermediate in base metal and maximum in welded zone. The fracture for all specimens was in the heat affected zone while testing in the universal testing machine.

  3. Effects of heat input on mechanical properties of metal inert gas welded 1.6 mm thick galvanized steel sheet

    Science.gov (United States)

    Rafiqul, M. I.; Ishak, M.; Rahman, M. M.

    2012-09-01

    It is usually a lot easier and less expensive to galvanize steel before it is welded into useful products. Galvanizing afterwards is almost impossible. In this research work, Galvanized Steel was welded by using the ER 308L stainless steel filler material. This work was done to find out an alternative way of welding and investigate the effects of heat input on the mechanical properties of butt welded joints of Galvanized Steel. A 13.7 kW maximum capacity MIG welding machine was used to join 1.6 mm thick sheet of galvanized steel with V groove and no gap between mm. Heat inputs was gradually increased from 21.06 to 25.07 joules/mm in this study. The result shows almost macro defects free welding and with increasing heat input the ultimate tensile strength and welding efficiency decrease. The Vickers hardness also decreases at HAZ with increasing heat input and for each individual specimen; hardness was lowest in heat affected zone (HAZ), intermediate in base metal and maximum in welded zone. The fracture for all specimens was in the heat affected zone while testing in the universal testing machine.

  4. Strain rate effects in nuclear steels at room and higher temperatures

    Energy Technology Data Exchange (ETDEWEB)

    Solomos, G. E-mail: george.solomos@jrc.it; Albertini, C.; Labibes, K.; Pizzinato, V.; Viaccoz, B

    2004-04-01

    An investigation of strain rate, temperature and size effects in three nuclear steels has been conducted. The materials are: ferritic steel 20MnMoNi55 (vessel head), austenitic steel X6CrNiNb1810 (upper internal structure), and ferritic steel 26NiCrMo146 (bolting). Smooth cylindrical tensile specimens of three sizes have been tested at strain rates from 0.001 to 300 s{sup -1}, at room and elevated temperatures (400-600 deg. C). Full stress-strain diagrams have been obtained, and additional parameters have been calculated based on them. The results demonstrate a clear influence of temperature, which amounts into reducing substantially mechanical strengths with respect to RT conditions. The effect of strain rate is also shown. It is observed that at RT the strain rate effect causes up shifting of the flow stress curves, whereas at the higher temperatures a mild downshifting of the flow curves is manifested. Size effect tendencies have also been observed. Some implications when assessing the pressure vessel structural integrity under severe accident conditions are considered.

  5. Effect of gas atoms on swelling of austenitic stainless steel

    International Nuclear Information System (INIS)

    Igata, N.; Eguchi, N.; Nishibe, E.; Naito, A.

    1994-01-01

    There have been many studies on the effect of He on swelling, however not so many on the effect of nitrogen on swelling. In this study the effect of nitrogen on swelling of 316 steel was investigated under HVEM irradiation for establishing a model of swelling. The nitrogen content was changed from 0.083 to 0.002 wt%, and for the comparison 321 steel containing Ti was used. Irradiation was performed by HVEM at 500 C under 2x10 -3 dpa/s. The dislocation loop number density in the early stage was nearly equal to the cavity number density formed later and both increased with nitrogen content. The swelling increased and decreased through the maximum as the nitrogen content increased. The result was explained by the model of swelling. As for 321 steel, no cavities were found under HVEM until 6 dpa at 500 C. This suggests the effect of scavenging of nitrogen by Ti. ((orig.))

  6. Damage mechanism of piping welded joints made from austenitic Steel for the type RBMK reactor

    International Nuclear Information System (INIS)

    Karzov, G.; Timofeev, B.; Gorbakony, A.; Petrov, V.; Chernaenko, T.

    1999-01-01

    In the process of operation of RBMK reactors the damages were taking place on welded piping, produced from austenitic stainless steel of the type 08X18H10T. The inspection of damaged sections in piping has shown that in most cases crack-like defects are of corrosion and mechanical character. The paper considers in details the reasons of damages appearance and their development for this type of welded joints of downcomers 325xl6 mm, which were fabricated from austenitic stainless steel using TlG and MAW welding methods. (author)

  7. Electron-beam welding of 21-6-9 (Cr--Ni--Mn) stainless steel: effect of machine parameters on weldability

    International Nuclear Information System (INIS)

    Casey, H.

    1975-04-01

    The high-manganese, nitrogen-strengthened 21-6-9 (Cr--Ni--Mn) austenitic stainless steel has a weldability rating similar to that of more common austenitic stainless steels in terms of cracking, porosity, etc. However, weld pool disruption problems may occur with this alloy that can be related to instability within the molten weld pool. Selection of machine parameters is critical to achieving weld pool quiescence as this report confirms from recent tests. Test samples came from heats of air-melted, vacuum-arc remelted, and electroslag remelted material. Low- and high-voltage machine parameters are discussed, and effects of parameter variation on weld pool behavior are given. Data relate weld pool behavior to weld fusion-zone geometry. Various weld parameters are recommended for the 21-6-9 alloy, regardless of its source or chemistry. (auth)

  8. Microstructural aspects of crack formation and propagation in the austenitic steel X6CrNiNb18-10 under low cycle fatigue loading

    Energy Technology Data Exchange (ETDEWEB)

    Soppa, E.; Kohler, C.; Roos, E.; Schuler, X. [Stuttgart Univ. (Germany). MPA

    2012-07-01

    The understanding of the crack initiation mechanisms and crack growth in apparently monolithic materials like X6CrNiNb18-10 stainless steel under cyclic loading requires the explicit analysis of the phenomena underlying fatigue on both atomistic and microscopic levels. The permanent delivery of mechanical energy through cyclic loading evokes changes in the microstructure that can lead to a martensitic transformation. The transformation of a metastable cubic face centered austenite and formation of a cubic body centered α'-martensite under cyclic loading at room temperature was found, both, in the experiment and in molecular dynamics simulations. The martensite nucleates prevalently at grain boundaries, triple points and at the specimen free surface and forms small (∝ 1 μm) differently oriented grains, also in the same parent austenitic grain. By a combination of interrupted low cycle fatigue tests (LCF) and electron backscatter diffraction (EBSD) measurements the martensitic transformation and subsequent fatigue crack formation were observed at the same area in the microstructure at different stages of the specimen lifetime. The EBSD measurements showed the following crack initiation scenarios: Cracks started (a) at the phase boundary between austenite and α'-martensite, (b) inside fully martensitic areas in the matrix, (c) at broken or debonded coarse NbCs. It is obvious that formation of a hard α'-martensite in a ductile and soft austenite and forming two-phase material causes a heterogeneous stress and strain distribution on the microscopic level. α'-martensite enhances locally the stress amplitude whereas in a soft austenite the plastic strain amplitude increases. Strain concentration in the austenite along the phase boundary is connected with a stress increase along the interface and can initiate fatigue crack there. Also at the crack tip, a permanent martensitic transformation occurs, so that the growth of the fatigue cracks at room

  9. Boundary condition effect on response modification factor of X-braced steel frames

    Directory of Open Access Journals (Sweden)

    Walid A. Attia

    2018-04-01

    Full Text Available Design of the structures to resist seismic force depends on the theory of dissipation in elastic energy that already exists in response modification factor “R-factor”. The main problem in codes gives a constant value for R-factor, since change in boundary conditions of building change in behavior of braced steel frame structures and that effects on R-factor. This study is an attempt to assess overstrength, ductility and response modification factor of X-braced steel frame under change in boundary conditions, as change in the direction of strong axis of column and connection support type of column besides variation in storey and bays numbers to be 21 frames and each frame has 8 different boundary conditions as sum of 168 cases for analysis. These frames were analyzed by using nonlinear static “pushover” analysis. As results of this study change in support type and direction of strong axis of column give large change in value of R-factor; the minimum value was 4.37 and maximum value 10.97. Minimum value is close to code value that’s mean the code is more conservative in suggesting of R-factor and gives a large factor of safety. Change in the location of bracing gives change in value of R-factor for all boundary conditions. Change in direction of strong axis of columns and support type didn’t give change in value of fundamental period, all boundary conditions. Keywords: Response modification factor, Ductility reduction factor, Overstrength factor, Boundary conditions, Brace frame, Nonlinear static analysis “Pushover”

  10. Multiferroic Double Perovskites ScFe1-xCrxO3 (1 /6x ≤5 /6 ) for Highly Efficient Photovoltaics and Spintronics

    Science.gov (United States)

    Cai, Tian-Yi; Liu, Shi-Chen; Ju, Sheng; Liu, Cheng-You; Guo, Guang-Yu

    2017-09-01

    Ferroelectric oxides are attractive materials for constructing efficient solar cells. Nevertheless, a wide band gap of nearly 3.0 eV in these ferroelectric oxides would result in poor overall sunlight absorption and, hence, low energy conversion efficiency. Here, by systematic first-principles density-functional calculations, we demonstrate that double-perovskite semiconductors ScFe1-xCrxO3 (1 /6x ≤5 /6 ) with a narrow band gap of approximately 1.8 eV would simultaneously exhibit large ferroelectric polarization (100 μ C /cm2 ) and ferrimagnetic magnetization (170 emu/cm3 ). Within a Schottky-based model for a typical sandwich solar-cell structure, a power-conversion efficiency of 9.0% can be reached by neglecting all other sources of photovoltaicity in ferroelectric materials. This value is larger than the largest value of 8.1% observed in ferroelectric oxides. Furthermore, these double perovskites are found to be single-spin semiconductors, and the obtained photocurrent is fully spin polarized over almost the entire Sun spectrum. These fascinating advantages would make ScFex Cr1 -xO3 (1 /6x ≤5 /6 ) semiconductors promising candidates for highly efficient solar cells and spin photovoltaic devices.

  11. High-cycle fatigue behavior of ultrafine-grained austenitic stainless and TWIP steels

    Energy Technology Data Exchange (ETDEWEB)

    Hamada, A.S. [Materials Engineering Laboratory (4KOMT), Box 4200, University of Oulu, 90014 Oulu (Finland); Metallurgical and Materials Engineering Department, Faculty of Petroleum and Mining Engineering, Suez Canal University, Box 43721, Suez (Egypt); Karjalainen, L.P., E-mail: pentti.karjalainen@oulu.fi [Materials Engineering Laboratory (4KOMT), Box 4200, University of Oulu, 90014 Oulu (Finland)

    2010-08-20

    High-cycle fatigue behavior of ultrafine-grained (UFG) 17Cr-7Ni Type 301LN austenitic stainless and high-Mn Fe-22Mn-0.6C TWIP steels were investigated in a reversed plane bending fatigue and compared to the behavior of steels with conventional coarse grain (CG) size. Optical, scanning and transmission electron microscopy were used to examine fatigue damage mechanisms. Testing showed that the fatigue limits leading to fatigue life beyond 4 x 10{sup 6} cycles were about 630 MPa for 301LN while being 560 MPa for TWIP steel, and being 0.59 and 0.5 of the tensile strength respectively. The CG counterparts were measured to have the fatigue limits of 350 and 400 MPa. The primary damage caused by fatigue took place by grain boundary cracking in UFG 301LN, while slip band cracking occurred in CG 301LN. However, in the case of TWIP steel, the fatigue damage mechanism is similar in spite of the grain size. In the course of cycling neither the formation of a martensite structure nor mechanical twinning occurs, but intense slip bands are created with extrusions and intrusions. Fatigue crack initiates preferentially on grain and twin boundaries, and especially in the intersection sites of slip bands and boundaries.

  12. Metallurgical study of low-temperature plasma carbon diffusion treatments for stainless steels

    International Nuclear Information System (INIS)

    Lewis, D.B.; Leyland, A.; Stevenson, P.R.; Cawley, J.; Matthews, A.

    1993-01-01

    We recently reported a novel low-temperature carbon diffusion technique for surface hardening of stainless steels. The treatment was shown to provide benefits in terms of abrasive wear resistance. There is also evidence to suggest that by performing diffusion treatments at low temperatures (i.e. below 400 C), these benefits can be achieved without compromising corrosion resistance. Here a variety of surface analysis and depth profiling techniques have been used to determine the physical and mechanical properties of carbon-rich layers produced on a range of stainless steel substrate materials. X-ray diffraction (XRD) was employed to determine the crystallographic structure, whilst wavelength dispersive X-ray analysis (WDX) and glow discharge optical spectroscopy (GDOS) gave information on the concentration and distribution of the diffused species within the treated layers. A variety of carbide-based structures was detected, including the expected M 23 C 6 and, more surprisingly, M 3 C. Optical and electron microscopy techniques were used to provide information on layer morphology. The surfaces produced by the low-temperature carbon-diffusion process generally exhibit a distinct diffusion layer of between 1 and 20 μm, depending on the material and the treatment conditions. Austenitic stainless steels appear to give the best response to treatment, however other types of stainless steel can be treated, particularly if the microstructure contains above 5% retained austenite. Here we discuss the changes in mechanical and metallurgical properties provided by this technique and its potential value for treatment of both austenitic and other stainless steel substrate materials. (orig.)

  13. Laser cutting of steel plates up to 100 mm in thickness with a 6-kW fiber laser for application to dismantling of nuclear facilities

    Science.gov (United States)

    Shin, Jae Sung; Oh, Seong Yong; Park, Hyunmin; Chung, Chin-Man; Seon, Sangwoo; Kim, Taek-Soo; Lee, Lim; Lee, Jonghwan

    2018-01-01

    A cutting study with a high-power ytterbium-doped fiber laser was conducted for the dismantling of nuclear facilities. Stainless steel and carbon steel plates of various thicknesses were cut at a laser power of 6-kW. Despite the use of a low output of 6-kW, the cutting was successful for both stainless steel and carbon steel plates of up to 100 mm in thickness. In addition, the maximum cutting speeds against the thicknesses were obtained to evaluate the cutting performance. As representative results, the maximum cutting speeds for a 60-mm thickness were 72 mm/min for the stainless steel plates and 35 mm/min for the carbon steel plates, and those for a 100-mm thickness were 7 mm/min for stainless steel and 5 mm/min for carbon steel plates. These results show an efficient cutting capability of about 16.7 mm by kW, whereas other groups have shown cutting capabilities of ∼10 mm by kW. Moreover, the maximum cutting speeds were faster for the same thicknesses than those from other groups. In addition, the kerf widths of 60-mm and 100-mm thick steels were also obtained as another important parameter determining the amount of secondary waste. The front kerf widths were ∼1.0 mm and the rear kerf widths were larger than the front kerf widths but as small as a few millimeters.

  14. Chevrel-phase solid solution Mo 6Se 8- xTe x. Study of its superconducting, magnetic and NMR properties

    Science.gov (United States)

    Hamard1a, C.; Auffret, V.; Peña, O.; Le Floch, M.; Nowak, B.; Wojakowski, A.

    2000-09-01

    The Chevrel-phase solid solution Mo 6Se 8-Mo 6Te 8 was studied by X-ray diffraction, AC and DC magnetic susceptibility and 77Se and 125Te NMR spectroscopy. From the smooth evolution of the lattice parameters and superconducting critical temperatures, a progressive substitution of selenium atoms by tellurium is shown, on the whole range of composition 0⩽ x⩽8, in the formulation Mo 6Se 8- xTe x: the unit-cell volume increases linearly because of the larger ionic size of tellurium, while Tc decreases rapidly (from 6.45 down to 0 K) because of the different formal oxidation states of the anions and a probable evolution of the Fermi level in the density of states. Results of magnetic susceptibility support this model and suggest the inhibition of the intrinsic metallic behavior with increasing x. The NMR spectra of the binaries Mo 6Se 8 and Mo 6Te 8 reveal two significant features, attributed to two different chalcogen positions in the R 3¯ symmetry. At low Se contents in Mo 6Se 8- xTe x ( x=7.5, 7 and 6), selenium first fills the two X(2) sites along the three-fold axis (2c positions), and then it becomes statistically distributed over the general 6f positions, leading to broad 77Se NMR lines. On the other hand, substitution of Te atoms in Mo 6Se 8 seems to occur in a random way, creating large perturbations on the 125Te NMR spectra, over the whole range of x. Theoretical analysis based on the presence of two anisotropic lines (of axial and non-axial symmetries, respectively) allowed us to estimate their anisotropy factors and to perfectly simulate the frequency response of both Mo 6Se 8 and Mo 6Te 8 binaries. Analysis of the Knight shift anisotropy leads us to conclude about the importance of the molybdenum z 2 molecular orbital contribution which controls the Mo-X dipolar interactions.

  15. Diamond deposition on siliconized stainless steel

    International Nuclear Information System (INIS)

    Alvarez, F.; Reinoso, M.; Huck, H.; Rosenbusch, M.

    2010-01-01

    Silicon diffusion layers in AISI 304 and AISI 316 type stainless steels were investigated as an alternative to surface barrier coatings for diamond film growth. Uniform 2 μm thick silicon rich interlayers were obtained by coating the surface of the steels with silicon and performing diffusion treatments at 800 deg. C. Adherent diamond films with low sp 2 carbon content were deposited on the diffused silicon layers by a modified hot filament assisted chemical vapor deposition (HFCVD) method. Characterization of as-siliconized layers and diamond coatings was performed by energy dispersive X-ray analysis, scanning electron microscopy, X-ray diffraction and Raman spectroscopy.

  16. X-ray diffraction analysis of rust layer on a weathering steel bridge with surface treatment using synchrotron radiation

    International Nuclear Information System (INIS)

    Yamashita, Masato; Hara, Shuichi; Kamimura, Takayuki; Miyuki, Hideaki; Sato, Masugu

    2007-01-01

    We have examined the structure of rust layer formed on a weathering steel bridge, to which the surface treatment, employing the effect of Cr 2 (SO 4 ) 3 sophisticatedly designed to form the protective goethite (α-FeOOH) rust layer which contains a certain amount of Cr, Cr-goethite, was applied in 1996, using X-ray diffraction at SPring-8 synchrotron radiation facility. It was shown that the formation of α-FeOOH was promoted and/or crystal growth of γ-FeOOH was suppressed by the surface treatment. The increase in the protective ability index (PAI) of the rust layer indicates that the protective goethite was predominantly formed under the effect of the surface treatment. In conclusion, it can be said that the surface treatment worked well to promote the formation of the protective goethite rust layer on the weathering steel bridge during the 10-year exposure. (author)

  17. Static tensile deformation behavior of a lean duplex stainless steel studied by in situ neutron diffraction and synchrotron radiation white x-rays

    International Nuclear Information System (INIS)

    Tsuchida, Noriyuki; Kawahata, Taiji; Ishimaru, Eiichiro; Takahashi, Akihiko; Suzuki, Hiroshi; Shobu, Takahisa

    2013-01-01

    To investigate the tensile deformation behavior of a lean duplex stainless steel (S32101) from the viewpoints of plastic deformability among phases or grains, we performed static tensile tests, in situ neutron diffraction, and white x-ray diffraction experiments at room temperature. In the static tensile tests, the S32101 steel displayed a larger uniform elongation and a better tensile strength-uniform elongation balance than a commercial SUS329J4L duplex stainless steel. A larger uniform elongation of S32101 is associated with the macroscopic work hardening behavior that a work hardening rate higher than the flow stress can maintain up until high true strains. From the experimental results of synchrotron radiation white x-ray diffraction experiments, the hard phase of S32101 was changed from the ferrite (α) phase to austenite (γ) one during tensile deformation. This led to a larger stress partitioning between the phases at the latter stage of deformation. From the experimental results of in situ neutron diffraction, it was found that the stress partitioning of the γ phase in the S32101 was the largest among the present results. Therefore, the larger work hardening rate of S32101 can be explained by the large stress partitioning of the γ phase, that between γ and α phases and γ volume fraction. (author)

  18. Mechanical properties of CO2/MIG welded structural rolled steel and stainless steel

    International Nuclear Information System (INIS)

    Lim, Jong Young; Yoon, Myong Jin; Kim, Sang Youn; Kim, Tae Gyu; Shin, Hyeon Seung

    2015-01-01

    To accomplish long-term use of specific parts of steel, welding technology is widely applied. In this study, to compare the efficiency in improving mechanical properties, rolled steel (SS400) was welded with stainless steel (STS304) by both CO 2 welding method and MIG (metal inert gas) welding method, respectively. Multi-tests were conducted on the welded specimen, such as X-ray irradiation, Vickers' Hardness, tensile test, fatigue test and fatigue crack growth test. Based on the fatigue crack growth test performed by two different methods, the relationship of da/dN was analyzed. Although the hardness by the two methods was similar, tensile test and fatigue properties of MIG welded specimen are superior to CO 2 welded one.

  19. Evaluation of welding by MIG in martensitic stainless steel

    International Nuclear Information System (INIS)

    Fernandes, M.A.; Mariano, N.A.; Marinho, D.H.C. Marinho

    2010-01-01

    This work evaluated structure's characterization and mechanical properties after the welding process of the stainless steel CA6NM. The employed welding process was the metal active gas with tubular wire. The control of the thermal cycle in the welding process has fundamental importance regarding the properties of the welded joint, particularly in the thermally affected zone. The mechanical properties were appraised through impact resistance tests and the hardness and microstructure through metallographic characterization and Ray-X diffraction. The parameters and the process of welding used promoted the hardness and toughness appropriate to the applications of the steel. Welding energy's control becomes an essential factor that can affect the temperature of carbide precipitation and the nucleation of the retained austenite in the in the region of the in the thermally affected zone. (author)

  20. Study of API 5L X70 steel corrosion processes when in contact with some Brazilian soils

    International Nuclear Information System (INIS)

    Jesus, Sergio Luis de

    2007-01-01

    Pipelines, fuel storage tanks and other metallic structures are in permanent contact and exposed to different types of soils, of horizons or layers, or of soil aggressiveness. This interaction may cause expressive damages to the environment and to the planned work. Contamination may occur due to leakage of stored products, splitting during transportation, accidents caused by pipelines without extensive maintenance. The result of these accidents could be, among others, some financial losses. In order to recognize the dynamic interactions between metallic surfaces and the environment it is crucial to have preventive actions and to develop better-applied materials. API steel 5L X70 has been used in structures of low and high pressure with high mechanical strength and corrosion and, even so, it is susceptible to etching corrosion since it is in contact with different environments from mangrove regions to industrial environments. The present case evaluated the role of 5L X70 API steel in contact with different soil horizons representative of the Brazilian soil. This investigation correlated chemical species with solute ions in soil solution, secondary and primary phase minerals besides physical and chemical characteristics as pH, electric conductivity, total dissolved solids, among others, to the results of corrosion resistance and ways of corrosion. The evaluation was carried out using x-ray diffractometry, scanning electron microscopy, total reflection x-ray fluorescence, fuel injection flow besides texture and gravimetric analyses to soil characterization and mineralogy, identification of corrosion products, soil solution analyses, evaluation of tested materials and classification of ways and types of corrosion. This was an attempt to integrate the data to a better understanding of the process involving reagents and products. The results showed that different soil horizons such as different types of analyzed soils produce specific etching in metallic structures

  1. Parametric Study of Slurry-Erosion of Hydroturbine Steels with and without Detonation Gun Spray Coatings using Taguchi Technique

    Science.gov (United States)

    Grewal, Harpreet Singh; Bhandari, Sanjeev; Singh, Harpreet

    2012-09-01

    WC-Co-Cr coatings were deposited on some hydroturbine 13Cr4Ni and 16Cr5Ni steels by the detonation-gun spray process. An in-depth characterization of the as-sprayed coating was done using X-ray diffraction (XRD) and scanning electron microscopy (SEM)/energy-dispersive X-ray spectroscopy (EDS) techniques. Microhardness and porosity measurements were also made. The coating was found to have a typical splat-like morphology with some indications of unmelted carbide particles. The XRD results showed the presence of WC as the primary phase along with W2C and Co6W6C as secondary phases. Furthermore, the slurry erosion behavior of the coatings was investigated to ascertain the usefulness of the coatings to reduce the slurry erosion of the steels. The effect of four operating factors viz. the velocity, impact angle, concentration, and particle size on the slurry erosion of coated and bare steels has been studied using a high-speed jet-type test rig. The sand used as an erodent was collected from a power plant to replicate the actual turbine conditions. It has been observed that the given cermet coating can enhance the erosion resistance of the steel. Velocity was found to be the most significant factor affecting the erosion behavior of the coating, whereas it was the erodent particle size in the case of uncoated steel. As evidenced from the SEM images, the platelet mechanism of erosion seemed to be the prominent one, causing the removal of material from the surface of the steel, whereas for the coating, the formation and interlinking of cracks resulted in the removal of material.

  2. A study on magnetoelastic properties of Tb3 (Fe28-xCox) V1.0 (x=0, 3, 6) compounds

    International Nuclear Information System (INIS)

    Gholizadeh, A.; Tajabor, N.; Pourarian, F.

    2012-01-01

    In this work, The magnetoelastic properties of polycrystalline samples of Tb 3 (Fe 28-x Co x ) V 1.0 (x=0, 3, 6) intermetallic compounds are investigated by means of linear thermal expansion and magnetostriction measurements in the temperature range of 77-515 K under applied magnetic fields up to 1.5 T. The linear thermal expansion increases with the Co content. The well-defined anomalies observed in the linear thermal expansion coefficients for Tb 3 (Fe 28-x Co x ) V 1.0 (x=0, 3, 6) compounds are associated with the magnetic ordering temperature for x=0 and spin reorientation temperatures for x=3, 6. Below transition temperatures, the value of the longitudinal magnetostriction (λ Pa ) at 1.6 T increases with Co content.

  3. Low carbon manganese-nickel-niobium steel

    International Nuclear Information System (INIS)

    Heisterkamp, F.; Hulka, K.

    1983-11-01

    Experimental heats of a low carbon-manganese-0.5% nickel-0.15% niobium steel have been rolled to plates between 13.5 and 50 mm thickness and to a 16 mm hot strip. Various combinations of soaking temperatures form 1100 0 C to 1300 0 C and of finish rolling temperatures between 710 0 C and 930 0 C have been investigated. From mechanical properties obtained, one can conclude that the investigated steel composition provides very good properties e.g. for pipe steels X65 to X75. In particular, the toughness at low temperature is outstanding despite relaxed rolling conditions. Metalographic and special investigations such as electron microscopy, texture evaluation and chemical extraction, correlated with applied rolling schedules and the mechanical properties obtained resulted in a comprehensive understanding about the benefits of high niobium metallurgy combined with nickel addition. All practically applied welding processes generated mechanical properties, in particular toughness of the weldment, that meet arctic specifications.(Author) [pt

  4. LaCu6-xAgx: A promising host of an elastic quantum critical point

    Energy Technology Data Exchange (ETDEWEB)

    Poudel, Lekh [ORNL; Dela Cruz, Clarina R. [ORNL; Koehler, Michael R. [University of Tennessee, Knoxville (UTK); McGuire, Michael A. [ORNL; Keppens, Veerle [University of Tennessee, Knoxville (UTK); Mandrus, David [ORNL; Christianson, Andrew D. [ORNL

    2018-05-01

    Structural properties of LaCu6-xAgx have been investigated using neutron and x-ray diffraction, and resonant ultrasound spectroscopy (RUS) measurements. Diffraction measurements indicate a continuous structural transition from orthorhombic (Pnma) to monoclinic (P2₁/C) structure. RUS measurements show softening of natural frequencies at the structural transition, consistent with the elastic nature of the structural ground state. The structural transition temperatures in LaCu6-xAgx decrease with Ag composition until the monoclinic phase is completely suppressed at xc=0.225. All of the evidence is consistent with the presence of an elastic quantum critical point in LaCu6-xAgx.

  5. Mechanical properties of phases in austeno-ferritic duplex stainless steel-Surface stresses studied by X-ray diffraction

    International Nuclear Information System (INIS)

    Dakhlaoui, Rim; Braham, Chedly; Baczmanski, Andrzej

    2007-01-01

    In this work the parameters characterizing the individual elastoplastic mechanical behaviour of each phase in austeno-ferritic duplex stainless steels are determined by using X-ray diffraction during a uniaxial tensile test. The interpretation of the experimental data is based on the diffraction elastic constants calculated by the self-consistent model taking the anisotropy of the studied materials into account. The elastoplastic model is used to predict the evolution of the internal stresses during loading, and to identify the critical resolved shear stresses and strain hardening parameters of the material. The effect of the chemical composition on the individual elastoplastic behaviour of the studied phases is established by comparing results from three different samples. Finally, the X-ray diffraction results are compared with those previously obtained by using neutron radiation

  6. On the System of Diophantine Equations x2-6y2=-5 and x=az2-b

    Directory of Open Access Journals (Sweden)

    Silan Zhang

    2014-01-01

    Full Text Available Mignotte and Pethö used the Siegel-Baker method to find all the integral solutions (x,y,z of the system of Diophantine equations x2-6y2=-5 and x=2z2-1. In this paper, we extend this result and put forward a generalized method which can completely solve the family of systems of Diophantine equations x2-6y2=-5 and x=az2-b for each pair of integral parameters a,b. The proof utilizes algebraic number theory and p-adic analysis which successfully avoid discussing the class number and factoring the ideals.

  7. Phase structures and morphologies of tempered CA6NM stainless steel welded by hybrid laser-arc process

    Energy Technology Data Exchange (ETDEWEB)

    Mirakhorli, F., E-mail: Fatemeh.mirakhorli.1@ens.etsmtl.ca [École de Technologie Supérieure, Montréal, Québec H3C 1K3 (Canada); National Research Council Canada – Aerospace, Montréal, Québec H3T 2B2 (Canada); Cao, X., E-mail: Xinjin.cao@cnrc-nrc.gc.ca [National Research Council Canada – Aerospace, Montréal, Québec H3T 2B2 (Canada); Pham, X-T., E-mail: Tan.pham@etsmtl.ca [École de Technologie Supérieure, Montréal, Québec H3C 1K3 (Canada); Wanjara, P., E-mail: Priti.wanjara@cnrc-nrc.gc.ca [National Research Council Canada – Aerospace, Montréal, Québec H3T 2B2 (Canada); Fihey, J.L., E-mail: jean-luc.fihey@etsmtl.ca [École de Technologie Supérieure, Montréal, Québec H3C 1K3 (Canada)

    2017-01-15

    The post-weld tempered microstructure of hybrid laser-arc welded CA6NM, a cast low carbon martensitic stainless steel, was investigated. The microstructural evolutions from the fusion zone to the base metal were characterized in detail using optical microscopy, scanning electron microscopy (SEM), electron backscatter diffraction (EBSD), X-ray diffraction (XRD) and microhardness techniques. The fusion zone, in its post-weld tempered condition, consisted of tempered lath martensite, residual delta-ferrite with various morphologies, reversed austenite and chromium carbides. The reversed austenite, which can be detected through both EBSD and XRD techniques, was found to be finely dispersed along the martensite lath boundaries, particularly at triple junctions. Based on the EBSD analysis, the orientation relationship between the reversed austenite and the adjacent martensite laths seemed to follow the Kurdjumov-Sachs (K-S) model. The results also revealed the presence of the reversed austenite in the different regions of the heat affected zone after post-weld tempering. The microindentation hardness distribution was measured, and correlated to the evolution of the corresponding microstructure across the welds. - Highlights: •The EBSD analysis was performed on hybrid laser-arc welded CA6NM. •The FZ consisted of tempered lath martensite, reversed austenite, carbides and δ ferrite after tempering. •The reversed γ was formed along the α′ lath boundaries, particularly at triple junctions.

  8. Stainless Steel to Titanium Bimetallic Transitions

    Energy Technology Data Exchange (ETDEWEB)

    Kaluzny, J. A. [Fermilab; Grimm, C. [Fermilab; Passarelli, D. [Fermilab

    2015-01-01

    In order to use stainless steel piping in an LCLS-II (Linac Coherent Light Source Upgrade) cryomodule, stainless steel to titanium bimetallic transitions are needed to connect the stainless steel piping to the titanium cavity helium vessel. Explosion bonded stainless steel to titanium transition pieces and bimetallic transition material samples have been tested. A sample transition tube was subjected to tests and x-ray examinations between tests. Samples of the bonded joint material were impact and tensile tested at room temperature as well as liquid helium temperature. The joint has been used successfully in horizontal tests of LCLS-II cavity helium vessels and is planned to be used in LCLS-II cryomodules. Results of material sample and transition tube tests will be presented.

  9. Fracture toughness behavior of irradiated stainless steel in PWR systems

    Energy Technology Data Exchange (ETDEWEB)

    Xu, H.; Fyfitch, S. [AREVA NP Inc., Lynchburg, Pennsylvania (United States); Tang, H.T. [Electric Power Research Inst., Palo Alto, California (United States)

    2007-07-01

    Data from available research programs were collected and evaluated by the Electric Power Research Institute (EPRI) Materials Reliability Program (MRP) to determine the relationship between fracture toughness and neutron fluence for conditions representative of pressurized water reactor (PWR) conditions. It is shown that the reduction of fracture toughness with increasing neutron dose in both boiling water reactors (BWRs) and PWRs is consistent with that observed in fast reactors. The lower bound fracture toughness observed for irradiated stainless steels in PWRs is 38 MPa{radical}m (34.6 ksi{radical}in) at neutron exposures greater than 6.7 X 10{sup 21} n/cm{sup 2} (E > 1.0 MeV) or approximately 10 dpa. For such levels of fracture toughness, it is recommended that linear-elastic fracture mechanics (LEFM) analyses be considered for design and operational analyses. The results from this study can be used by the nuclear industry to assess the effects of irradiation on stainless steels in PWR systems. (author)

  10. Heavy-Section Steel Irradiation Program: Progress report for April--September 1995. Volume 6, Number 2

    International Nuclear Information System (INIS)

    Corwin, W.R.

    1996-08-01

    The goal of the Heavy-Section Steel Irradiation Program is to provide a thorough, quantitative assessment of effects of neutron irradiation on material behavior, and in particular the fracture toughness properties, of typical pressure vessel steels as they relate to light-water reactor pressure-vessel integrity. Effects of specimen size, material chemistry, product form and microstructure, irradiation fluence, flux, temperature and spectrum, and post-irradiation annealing are being examined on a wide range of fracture properties. The HSSI Program is arranged into 14 tasks: (1) program management, (2) fracture toughness (K Ic ) curve shift in high-copper welds, (3) crack-arrest toughness (K Ia ) curve shift in high-copper welds, (4) irradiation effects on cladding, (5) K Ic and K Ia curve shifts in low upper-shelf welds, (6) annealing effects in low upper-shelf welds, (7) irradiation effects in a commercial low upper-shelf weld, (8) microstructural analysis of irradiation effects, (9) in-service aged material evaluations, (10) correlation monitor materials, (11) special technical assistance, (12) JPDR steel examination, (13) technical assistance for JCCCNRS Working Groups 3 and 12, and (14) additional requirements for materials. This report provides an overview of the activities within each of these task from April through September 1995

  11. Type IIA string theory on T"6/(Z_2 x Z_6 x ΩR). Model building and string phenomenology with intersecting D6-branes

    International Nuclear Information System (INIS)

    Ecker, Jill

    2016-01-01

    In this doctoral thesis, various aspects of string model building and phenomenology are investigated within the framework of Type IIA string theory on the T"6/(Z_2 x Z_6 x ΩR) orbifold with discrete torsion. The aim is the reproduction of supersymmetric versions of well-known particle physics models using intersecting rigid D6-branes wrapped on fractional three-cycles. The models analyzed include the minimal supersymmetric Standard Model as well as supersymmetric Pati-Salam models, left-right symmetric models and SU(5) models. Systematic computer scans test numerous combinations of intersecting D6-branes in order to detect those that give rise to the correct chiral particle content of the considered models. For each type of the afore mentioned models, concrete examples will be found which satisfy the constraints on the particle spectrum and fulfill all consistency conditions. Finally, the thesis focuses on phenomenological aspects of the particle physics models found, including the detection of massless U(1) combinations, discrete Z_n-symmetries and cubic couplings such as the Yukawa couplings.

  12. Optimum conditions for aging of stainless maraging steels

    International Nuclear Information System (INIS)

    Mironenko, P.A.; Krasnikova, S.I.; Drobot, A.V.

    1980-01-01

    Aging kinetics of two 0Kh11N10M2T type steels in which 3 % Mo (steel 1), and 3 % Mo and 11 % Co (steel 2) had been additionally introduced instead of titanium were investigated. Electron microscopy and X-ray methods were used. It was ascertained that the process of steel aging proceeded in 3 stages. Steel 2 was hardened more intensively during the aging, had a higher degree of hardness and strength after the aging, weakened more slowly if overaged than steel 1. The intermetallide hcp-phase Fe 2 Mo was the hardening phase on steels extended aging. Optimum combination of impact strength and strength was was achieved using two-stage aging: the first stage - maximum strength aging was achieved, the second stage - aging at minimum temperatures of two-phase α+γ region

  13. Fatigue crack growth rate of API X70 steel pipelines under spectrum loading

    International Nuclear Information System (INIS)

    Beden, S.M.; Abdullah, S.; Ariffin, A.K.

    2012-01-01

    Pipelines offer the most efficient way to transport bulk quantities of gas and oil, either from points of production to storage locations or from storage locations to distributed points of end use. As one of the main materials of west–east gas transmission pipes, X70 pipelines usually serve under variable amplitude loading (VAL). Base on the importance of in-service API X70 pipelines, it is important for the safe operation of this system to know its behaviour under VAL. This paper focuses on the ability of using the NASGRO model to predict the fatigue crack growth (FCG), based on investigation with the modified Wheeler model and experimental data. The results show that the NASGRO model give a fatigue life near by to that published in literatures and also showed the FCG rate response of X70 pipeline steels when exposed to VAL with different overload values. Extra modification to the NASGRO model may lead to better representing of FCG rate. Highlights: ► The assessment of fatigue crack propagation under different load histories are proposed and presented in this paper. ► Due to lack of knowledge in the related area, as yet no universal model exists. ► The output was based on both simulation and experiments. The simulation part was carried out based on the NASGRO model. ► This work focus on fatigue crack growth (FCG) and fatigue life based on the comparison with the previous work.

  14. Marble waste characterization as a desulfurizing slag component for steel

    International Nuclear Information System (INIS)

    Coleti, J.L.; Grillo, F.F.; Tenorio, J.A.S.; De Oliveira, J.R.

    2014-01-01

    The current steel market requires from steel plants better quality of its products. As a result, steel plants need to search for improvements and costs reduction in its process. Hence, the residue of marble containing significant quantities of calcium and magnesium carbonates, raw materials of steel refining slag, was characterized in order to replace the conventional lime used. Therefore, it will be possible to reduce the cost and volume of waste produced by the ornamental rock industry. The following methods were applied to test the waste potential: SEM with EDS, x-ray diffraction, x-ray fluorescence (EDX), Thermogravimetry (TG) and analysis of surface area and particle size by the BET method using dispersion leisure. The results indicated the feasibility of waste as raw material in the composition of desulfurizing slags. (author)

  15. Interaction of uranium with in situ anoxically generated magnetite on steel

    International Nuclear Information System (INIS)

    Rovira, Miquel; El Aamrani, Souad; Duro, Lara; Gimenez, Javier; Pablo, Joan de; Bruno, Jordi

    2007-01-01

    In the high level nuclear waste repository concept, spent nuclear fuel is designed to be encapsulated in steel canisters. Thus, it is necessary to study the influence of the steel and/or its corrosion products on the behaviour of the radionuclides released from the fuel. In this sense, the main objective of this work is to contribute to the knowledge of the influence of the steel and/or its corrosion products on the uranium(VI) retention. To this aim, magnetite (Fe 3 O 4 ) has been generated by anaerobic steel corrosion in an autoclave reactor at an overpressure of 8 atm of H 2 (g). After characterisation by X-ray diffraction (XRD), the obtained corroded steel coupons were contacted, at two different H 2 (g) pressures (1 atm and 7.6 atm), with a U(VI) solution. The evolution of the uranium concentration in solution is determined and a study of the composition of the coupons at the end of the experiments is carried out. The main conclusion obtained from this work is that magnetite generated on a steel coupon is able not only to retain uranium via sorption, but also to reduce hexavalent to tetravalent uranium in a higher extent than commercial magnetite, thus, providing an effective retardation path to the migration of uranium (and, potentially, other actinides) out of the repository

  16. Chemistry conditions in crevices of carbon steel and stainless steel: a comparative study

    International Nuclear Information System (INIS)

    Pushpalata, R.; Veena, S.; Chandran, Sinu; Mohan, T.V.K.; Rangarajan, S.; Narasimhan, S.V.

    2008-01-01

    Occurrence of crevice corrosion in the steam generator tubes of nuclear power plants may lead to transport of radioactivity to the secondary side. It is expected that effect of crevice corrosion will be more pronounced in a passive material like stainless steel (SS) as compared to carbon steel (CS). Theoretical modeling of the dynamics of crevice chemistry calls for experimental data with respect to various water chemistry parameters like pH, conductivity and concentrations of the ionic species in typical crevices of different geometry (aspect ratio of length and width). This paper presents the experimental results obtained with crevices in CS -106 B, SS-304 (nano grain) and SS 316 blocks (varying dimensions) exposed to a medium containing 1 ppm of lithium and chloride ion each for 10 days in static autoclave at 245 deg C. The bulk solution pH showed a reduction in alkalinity and slight increase in conductivity. In case of CS about 58 times increase in Cl - was observed in the smaller crevice of dimension 1 mm (width) x 25 mm (depth) whereas it was only ∼ 12 times in the bigger crevice (2 mm x 39 mm). Other anionic impurities like SO 4 2- and Br - present as impurities in NaCI were also found to be concentrated in the crevices whereas not much increase in cationic impurities was observed. In a similar experiment with SS blocks with crevice dimension comparable to diffusion layer thickness, appreciable increase in chloride concentration was observed. Electrochemical experiments were also carried out in deaerated NaCI (3.5%) solution at 25 deg C with CS, SS-304 (nano grain) and SS-316 (normal-grain) coupons. The OCP was -297 mV for SS-316 whereas for SS-304 coupon the OCP was -339 mV. Potentiodynamic anodic polarization curve showed a passive behavior up to 0.0V and then a sudden increase in anodic current. On nano-grained SS, a yellowish film on the surface was observed with a large number of pits whereas severe general corrosion was observed in the normal

  17. Carbon steel protection in G.S. (Girlder sulfide) plants. CITROSOLV process influence. Pt. 6

    International Nuclear Information System (INIS)

    Lires, O.A.; Burkart, A.L.; Delfino, C.A.; Rojo, E.A.

    1988-01-01

    In order to protect carbon steel towers and piping of Girlder sulfide (G.S.) experimental heavy water plants against corrosion produced by the action of aqueous solutions of hydrogen sulfides, a method, previously published, was developed. Carbon steel, exposed to saturated aqueous solutions of hydrogen sulfide, forms iron sulfide scales. In oxygen free solutions evolution of corrosion follows the sequence: mackinawite → cubic ferrous sulfide → troilite → pyrrotite → pyrite. Scales formed by pyrrotite-pyrite or pyrite are the most protective layers (these are obtained at 130 deg C, 2 MPa, for periods of 14 days). CITROSOLV Process (Pfizer) is used to descaling and passivating stainless steel plant's components. This process must be used in mixed (carbon steel - stainless steel) circuits and may cause the formation of magnetite scales over the carbon steel. The influence of magnetite in the pyrrotite-pyrite scales formation is studied in this work. (Author) [es

  18. Study of the M23C6 precipitation in AISI 304 stainless steel by small angle neutron scattering

    International Nuclear Information System (INIS)

    Boeuf, A.; Caciuffo, R.G.M.; Institut Max von Laue - Paul Langevin, 38 - Grenoble; Ancona Univ.; Melone, S.; Puliti, P.; Rustichelli, F.; Institut Max von Laue - Paul Langevin, 38 - Grenoble; Ancona Univ.; Coppola, R.

    1985-01-01

    The results of some small-angle neutron scattering (SANS) experiments on M 23 C 6 (M=Fe, Cr) carbide precipitation in AISI 304 stainless steel, aged at different temperatures during different times, are presented. The total volume fraction, the total surface of precipitates per unit sample volume and the size distribution functions of the M 23 C 6 carbides were determined. (orig.)

  19. Heat treatment temperature influence on ASTM A890 GR 6A super duplex stainless steel microstructure

    International Nuclear Information System (INIS)

    Martins, Marcelo; Casteletti, Luiz Carlos

    2005-01-01

    Duplex and super duplex stainless steels are ferrous alloys with up to 26% chromium, 8% nickel, 5% molybdenum and 0.3% nitrogen, which are largely used in applications in media containing ions from the halogen family, mainly the chloride ion (Cl - ). The emergence of this material aimed at substituting Copper-Nickel alloys (Cupro-Nickel) that despite presenting good corrosion resistance, has mechanical properties quite inferior to steel properties. The metallurgy of duplex and super duplex stainless steel is complex due to high sensitiveness to sigma phase precipitation that becomes apparent, due to the temperatures they are exposed on cooling from solidification as well as from heat treatment processes. The objective of this study was to verify the influence of heat treating temperatures on the microstructure and hardness of ASTM A890/A890M Gr 6A super duplex stainless steel type. Microstructure control is of extreme importance for castings, as the chemical composition and cooling during solidification inevitably provide conditions for precipitation of sigma phase. Higher hardness in these materials is directly associated to high sigma phase concentration in the microstructure, precipitated in the ferrite/austenite interface. While heat treatment temperature during solution treatment increases, the sigma phase content in the microstructure decreases and consequently, the material hardness diminishes. When the sigma phase was completely dissolved by the heat treatment, the material hardness was influenced only due to ferrite and austenite contents in the microstructure

  20. The failure behavior of duplex 316 L steel-TA6V titanium alloy spherical pressure vessels

    International Nuclear Information System (INIS)

    Miannay, D.

    1980-05-01

    The purpose of this paper is to compare the experimental residual stresses of spherical vessels made of TA6V alloy which exhibits plasticity before failure in toughness testing and cracked with several configurations, with stresses estimated according to the afore mentioned theories. An internal austenitic 316 L steel is used to prevent 'leak before break' [fr

  1. Metallurgy of high-silicon steel parts produced using Selective Laser Melting

    International Nuclear Information System (INIS)

    Garibaldi, Michele; Ashcroft, Ian; Simonelli, Marco; Hague, Richard

    2016-01-01

    The metallurgy of high-silicon steel (6.9%wt.Si) processed using Selective Laser Melting (SLM) is presented for the first time in this study. High-silicon steel has great potential as a soft magnetic alloy, but its employment has been limited due to its poor workability. The effect of SLM-processing on the metallurgy of the alloy is investigated in this work using microscopy, X-Ray Diffraction (XRD) and Electron Backscatter Diffraction (EBSD). XRD analysis suggests that the SLM high-silicon steel is a single ferritic phase (solid solution), with no sign of phase ordering. This is expected to have beneficial effects on the material properties, since ordering has been shown to make silicon steels more brittle and electrically conductive. For near-fully dense samples, columnar grains with a high aspect ratio and oriented along the build direction are found. Most importantly, a <001> fibre-texture along the build direction can be changed into a cube-texture when the qualitative shape of the melt-pool is altered (from shallow to deep) by increasing the energy input of the scanning laser. This feature could potentially open the path to the manufacture of three-dimensional grain-oriented high-silicon steels for electromechanical applications.

  2. Alloy development for fast induced radioactivity decay for fusion reactor applications

    International Nuclear Information System (INIS)

    Klueh, R.L.; Bloom, E.E.

    1984-03-01

    The Cr-Mo ferritic (martensitic) steels and austenitic stainless steels (primarily type 316 and variations on that composition) are the leading candidates for the structural components for future fusion reactors. However, irradiation of such steels in a fusion environment produces long-lived radioactive isotopes. These isotopes lead to difficult radioactive waste disposal problems once the structure is removed from service. Such problems could be reduced by developing steels that contain only elements that produce radioactive isotopes that decay to low levels in a reasonable time (tens of years instead of hundreds or thousands of years). This report discusses the development of such steels by making elemental substitutions in the steels now under consideration. Molybdenum must be replaced in the Cr-Mo steels; nickel and molybdenum both must be replaced in the austenitic stainless steels (the nitrogen concentration must be limited, and niobium, maintained to extremely low levels). Appropriate substitutions are tungsten for molybdenum in the Cr-Mo steels and manganese for nickel in the austenitic stainless steels. Indications are that suitable ferritic steels can be developed, but development of a nickel-free austenitic stainless steel with properties similar to the Cr-Ni stainless steels appears to be much more complex

  3. Microstructural evolution in warm-rolled and cold-rolled strip cast 6.5 wt% Si steel thin sheets and its influence on magnetic properties

    Energy Technology Data Exchange (ETDEWEB)

    Wang, Xianglong, E-mail: 215454278@qq.com; Liu, Zhenyu, E-mail: zyliu@mail.neu.edu.cn; Li, Haoze; Wang, Guodong

    2017-07-01

    Highlights: • The experimental materials used in the study are based on strip casting. • Magnetic properties between warm rolled and cold rolled sheets are investigated. • Cold rolled 6.5% Si sheet has better magnetic properties than warm rolled sheet. • The γ and λ-fiber recrystallization textures can be optimized after cold rolling. • Cold rolling should be more suitable for fabricating 6.5% Si steel thin sheets. - Abstract: 6.5 wt% Si steel thin sheets were usually fabricated by warm rolling. In our previous work, 6.5 wt% Si steel thin sheets with good magnetic properties had been successfully fabricated by cold rolling based on strip casting. In the present work, the main purposes were to find out the influences of warm rolling and cold rolling on microstructures and magnetic properties of the thin sheets with the thickness of 0.2 mm, and to confirm which rolling method was more suitable for fabricating 6.5 wt% Si steel thin sheets. The results showed that the cold rolled sheet could obtain good surface quality and flatness, while the warm rolled sheet could not. The intensity of γ-fiber rolling texture (<1 1 1>//ND) of cold rolled specimen was weaker than that of the warm rolled specimen, especially for the {1 1 1}<1 1 2> component at surface layer and {1 1 1}<1 1 0> component at center layer. After the same annealing treatment, the cold rolled specimen, which had higher stored energy and weaker intensity of γ-fiber rolling texture, could obtain smaller recrystallization grain size, weaker intensity of γ-fiber recrystallization texture and stronger intensity of λ-fiber recrystallization texture. Therefore, due to the good surface quality, smaller recrystallization grain size and optimum recrystallization texture, the cold rolled specimen possessed improved magnetic properties, and cold rolling should be more suitable for fabricating 6.5 wt% Si steel thin sheets.

  4. Structural and tribological properties of carbon steels modified by plasma pulses

    International Nuclear Information System (INIS)

    Sartowska, B.; Walis, L.; Piekoszewski, J.; Senatorski, J.; Stanislawski, J.; Nowicki, L.; Ratajczak, R.; Barlak, M.; Kopcewicz, M.; Kalinowska, J.; Prokert, F.

    2006-01-01

    Carbon steels with different concentration of carbon and heat (Armco-iron, steels 20, 45, 65 and N9) were treated according to the standard procedures: they were irradiated with five intense (about 5 J/cm 2 ), short (μs range) argon or nitrogen plasma pulses generated in a rod plasma injector (RPI) type of plasma generator. Samples were characterized by the following methods: nuclear reaction analysis (NRA) 14 N(d,α) 12 C , scanning electron microscopy (SEM), conversion electron Moessbauer spectroscopy (CEMS), X-ray diffraction analysis (GXRD), and Amsler wear tests. SEM observations shown that the morphology of the pulse treated samples, both argon and nitrogen plasma are identical. It has been found, that nitrogen is much more efficient than argon in ausenitization of carbon steel. The craters and droplets are uniformly distributed over the surface, which is typical of melted and rapidly recrystallized top layers. The thickness of the modified layers is in the range of 1.2-1.6 μm

  5. Perovskite phases of the system Ba/sub 2/Ysub(0. 67)Usub(1-x)Wsub(x)O/sub 6/

    Energy Technology Data Exchange (ETDEWEB)

    Schittenhelm, H J; Kemmler-Sack, S [Tuebingen Univ. (Germany, F.R.). Inst. fuer Anorganische Chemie

    1976-08-01

    A solid solution series is formed between the polymorphic perovskites Ba/sub 2/Ysub(0.67)UO/sub 6/ and Ba/sub 2/Ysub(0.67)WO/sub 6/ (cubic: a = 8.37 A; hexagonal: a = 4x5.88 A and c = 4x7.77 A). The structure is cubic between x = 0.1 and 0.99 and for x > 0.95 hexagonal as well. Strong deviations from the ideal behaviour are detectable with spectroscopic methods. The shape of the UO/sub 6/ and WO/sub 6/ octahedrons experiences only minor changes within the series.

  6. Size-dependent characteristics of ultra-fine oxygen-enriched nanoparticles in austenitic steels

    Energy Technology Data Exchange (ETDEWEB)

    Miao, Yinbin, E-mail: ymiao@anl.gov [Argonne National Laboratory, Lemont, IL 60439 (United States); University of Illinois at Urbana-Champaign, Urbana, IL 61801 (United States); Mo, Kun [Argonne National Laboratory, Lemont, IL 60439 (United States); Zhou, Zhangjian [University of Science and Technology Beijing, Beijing 100082 (China); Liu, Xiang; Lan, Kuan-Che [University of Illinois at Urbana-Champaign, Urbana, IL 61801 (United States); Zhang, Guangming [University of Illinois at Urbana-Champaign, Urbana, IL 61801 (United States); University of Science and Technology Beijing, Beijing 100082 (China); Miller, Michael K.; Powers, Kathy A. [Oak Ridge National Laboratory, Oak Ridge, TN 37830 (United States); Stubbins, James F. [University of Illinois at Urbana-Champaign, Urbana, IL 61801 (United States); International Institute for Carbon-Neutral Energy Research (I2CNER), Kyushu University, Fukuoka 819-0395 (Japan)

    2016-11-15

    Here, a coordinated investigation of the elemental composition and morphology of ultra-fine-scale nanoparticles as a function of size within a variety of austenitic oxide dispersion-strengthened (ODS) steels is reported. Atom probe tomography was utilized to evaluate the elemental composition of these nanoparticles. Meanwhile, the crystal structures and orientation relationships were determined by high-resolution transmission electron microscopy. The nanoparticles with sufficient size (>4 nm) to maintain a Y{sub 2}Ti{sub 2−x}O{sub 7−2x} stoichiometry were found to have a pyrochlore structure, whereas smaller Y{sub x}Ti{sub y}O{sub z} nanoparticles lacked a well-defined structure. The size-dependent characteristics of the nanoparticles in austenitic ODS steels differ from those in ferritic/martensitic ODS steels. - Highlights: • The structural and chemical characteristics of nanoparticles are revealed. • Nanoparticles' crystal structure and elemental composition are size-dependent. • Characteristics of austenitic ODS steels are compared to that of an F/M ODS steel. • Hypothesis about the formation mechanism of nanoparticles is proposed accordingly.

  7. The ANL X6B beamline at NSLS: A versatile facility

    International Nuclear Information System (INIS)

    Huang, K.G.; Ramanathan, M.; Montano, P.A.; Illinois Univ., Chicago, IL

    1994-07-01

    We have described the x-ray optics and beamline performance of the ANL X6B beam line at the NSLS. Considerable flexibility has been built into the beam line to accommodate a wide range of x-ray diffraction, scattering, and spectroscopy experiments with various requirements. We presented selected examples of experimental results and showed that with the high intensity, high energy resolution, high-q resolution, and energy tunability, the X6B beam line has become a versatile facility

  8. Study of regularities in propagation of thermal fatigue cracks

    International Nuclear Information System (INIS)

    Tachkova, N.G.; Sobolev, N.D.; Egorov, V.I.; Rostovtsev, Yu.V.; Ivanov, Yu.S.; Sirotin, V.L.

    1978-01-01

    Regularities in the propagation of thermal fatigue cracks in the Cr-Ni steels of the austenite class depending upon deformation conditions in the crack zone, have been considered. Thin-walled tube samples of the Kh16N40, Kh18N20 and Kh16N15 steels have been tested in the 10O reversible 400 deg C and 100 reversible 500 deg C regimes. The samples have possessed a slot-shaped stress concentrator. Stress intensity pseudocoefficient has been calculated for the correlation of experimental data. The formula for determining crack propagation rate has been obtained. The experiments permit to conclude that propagation rate of thermal fatigue cracks in the above steels depends upon the scope of plastic deformation during a cycle and stress intensity pseudocoefficient, and is determined by plastic deformation resistance during thermal cyclic loading

  9. Effect of Microstructure on HIC Susceptibility of API X70MS Linepipe Steel

    Energy Technology Data Exchange (ETDEWEB)

    Sung, Joon-Ho; Sim, Ho-Seop; Park, Byung-Gyu [Dongkuk Steel R and D Center, Pohang (Korea, Republic of); Cho, Kyung-Mox [Pusan National University, Busan (Korea, Republic of)

    2017-06-15

    The resistance of hydrogen induced cracking (HIC) was investigated with different microstructures of API X70MS steel. Ferrite/acicular ferrite (F/AF), deformed ferrite/acicular ferrite, ferrite/bainite (F/B) and single acicular ferrite (AF) were obtained by thermo-mechanical controlled process (TMCP) with changing rolling and cooling conditions. HIC resistance was found to be affected by the type as well as morphology of the microstructure, and thus the behavior of crack initiation and propagation could be analyzed. It was found that single AF and deformed F/AF with uniformly distributed dislocation reduced HIC initiation. Banded microstructure with a hardness value below 250 HV, such as AF, showed good HIC propagation resistance due to high toughness. AF generally exhibited excellent crack initiation and propagation resistance, namely the best HIC susceptibility performance. AF might redeem the HIC resistance for the banded microstructure also.

  10. Dissimilar laser welding of AISI 316L stainless steel to Ti6–Al4–6V alloy via pure vanadium interlayer

    Energy Technology Data Exchange (ETDEWEB)

    Tomashchuk, I., E-mail: iryna.tomashchuk@u-bourgogne.fr; Grevey, D.; Sallamand, P.

    2015-01-12

    Successful continuous laser joining of AISI 316L stainless steel with Ti6Al4V titanium alloy through pure vanadium interlayer has been performed. Three welding configurations were tested: one-pass welding involving all three materials and two pass and double spot welding involving creation of two melted zones separated by remaining solid vanadium. For the most relevant welds, the investigation of microstructure, phase content and mechanical properties has been carried out. In case of formation of a single melted zone, the insertion of steel elements into V-based solid solution embrittles the weld. In case of creation of two separated melted zones, the mechanical resistance of the junction is determined by annealing of remaining vanadium interlayer, which can be witnessed by observing the increase of grain size and decrease of UTS. The two pass configuration allows attain highest mechanical resistance: 367 MPa or 92% of UTS of annealed vanadium. Double spot configuration produces excessive heat supply to vanadium interlayer, which results in important decrease of tensile strength down to 72% of UTS of annealed vanadium. It was found that undesirable σ phase which forms between Fe and V is not created during the laser welding process because of high cooling rates. However, the zones whose composition corresponds to σ homogeneity range are crack-susceptible, so the best choice is to reduce the V content in steel/vanadium melted zone below σ phase formation limit. In the same time, the proportion between V and Ti in Ti6Al4V/vanadium melted zones does not influence mechanical properties as these elements form ideal solid solution.

  11. X-ray diffraction and Moessbauer study of (Fe1-xNi x)4N (0.2 ≤ x ≤ 0.6) films

    International Nuclear Information System (INIS)

    El Khiraoui, S.; Sajieddine, M.; Vergnat, M.; Sahlaoui, M.; Bauer, Ph.; Mabrouki, M.

    2007-01-01

    Single phase (Fe 1-x Ni x ) 4 N compounds (0.2 ≤ x ≤ 0.6) have been synthesized by reactive evaporation and investigated by X-ray diffraction and Moessbauer spectrometry. The lattice parameters of the nitrides decrease from 3.796 to 3.774 A with increasing Ni concentration. The fitting results of Moessbauer spectra indicate that the average hyperfine field have the same changing tendency with lattice parameter and the nickel atoms have a tendency to be located at the corner site

  12. X-ray photoelectron spectroscopy study of radiofrequency-sputtered refractory compound steel interfaces

    Science.gov (United States)

    Wheeler, D. R.; Brainard, W. A.

    1978-01-01

    Radiofrequency sputtering was used to deposit Mo2C, Mo2B5, and MoSi2 coatings on 440C steel substrates. Both sputter etched and preoxidized substrates were used, and the films were deposited with and without a substrate bias of -300 V. The composition of the coatings was measured as a function of depth by X-ray photoelectron spectroscopy combined with argon ion etching. In the interfacial region there was evidence that bias produced a graded interface in Mo2B5 but not in Mo2C. Oxides of iron and of all film constituents except carbon were presented in all cases but the iron oxide concentration was higher and the layer thicker on the preoxidized substrates. The film and iron oxides were mixed in the MoSi2 and Mo2C films but layered in the Mo2B5 film. The presence of mixed oxides correlates with enhanced film adhesion.

  13. Effects of cathodic protection on cracking of high-strength pipeline steels

    Energy Technology Data Exchange (ETDEWEB)

    Elboujdaini, M.; Revie, R. W.; Attard, M. [CANMET Materials Technology Laboratory, Ottawa, ON(Canada)], email: melboujd@nrcan.gc.ca

    2010-07-01

    Four strength levels of pipeline steels, ranging from X-70 to X-120, were compared to determine whether higher strength materials are more susceptible to hydrogen embrittlement under cathodic protection. Ductility was measured in a solution at four protection levels, going from no cathodic protection to 500 mV of overprotection. All four steels showed loss of ductility under cathodic protection. Under cathodic polarization, the loss of ductility increased with the strength of the steel and the activity of the potential. After slow-strain-rate experiments conducted in air and examination of fracture surfaces, it is concluded that application of cathodic potentials, cathodic overprotection, higher strength of steel, and exposure to aqueous solution are factors that decrease the ductility of steel. Hydrogen reduction seems to be an important factor in ductility reduction and fractures. Observations suggest that high-strength pipelines need better control of cathodic protection than lower-strength pipelines.

  14. Enhancing Ductility of 1045 Nanoeutectic Steel Prepared by Aluminothermic Reaction through Annealing at 873 K

    Directory of Open Access Journals (Sweden)

    Zhengning Li

    2017-01-01

    Full Text Available The 1045 steel with lamellar spacing of pearlite in nanometer was prepared by aluminothermic reaction casting and annealed at 873 K (600°C with different time. Microstructures of steels were investigated by X-ray diffraction (XRD, scanning electron microscope (SEM, and transmission electron microscope (TEM. Tensile properties of the steels were measured. The results showed that the lamellar spacing of the pearlite increased with the annealing time. It was found that the microstructure of steels consisted of nanocrystalline-ferrite matrix and laminar pearlite phase. The average grain sizes of the ferrite were 26.9, 27.0, 26.1, and 34.9 nm for the cast steel and samples annealed for 2, 4, and 6 h, respectively. As the annealing time increased, the volume fraction of the pearlite almost remained constant, while the laminar spacing of pearlite increased from 146 to 300 nm. The tensile and yield strength varied slightly; the elongation obviously improved. After annealing for 4 h, the elongation increased to be 33%, which was the reported highest value for the steel up to now and about twice of the conventional 1045 steel.

  15. Microstructures of cast-duplex stainless steel after long-term aging

    International Nuclear Information System (INIS)

    Chung, H.M.; Chopra, O.K.

    1985-10-01

    Microstructures of cast-duplex stainless steels subjected to long-term aging either in the laboratory or during in-reactor service have been characterized and compared by TEM, SEM, and optical microscopy. The microstructural characteristics have been correlated with the impact failure behavior of the material. G-phase, α', and an unidentified Type X precipitate were responsible for the ferrite-phase embrittlement. Precipitation of M 23 C 6 carbides on austenite-ferrite boundaries further degraded the reactor-aged material

  16. Topological superconductor in quasi-one-dimensional Tl2 -xMo6Se6

    Science.gov (United States)

    Huang, Shin-Ming; Hsu, Chuang-Han; Xu, Su-Yang; Lee, Chi-Cheng; Shiau, Shiue-Yuan; Lin, Hsin; Bansil, Arun

    2018-01-01

    We propose that the quasi-one-dimensional molybdenum selenide compound Tl2 -xMo6Se6 is a time-reversal-invariant topological superconductor induced by intersublattice pairing, even in the absence of spin-orbit coupling (SOC). No noticeable change in superconductivity is observed in Tl-deficient (0 ≤x ≤0.1 ) compounds. At weak SOC, the superconductor prefers the triplet d vector lying perpendicular to the chain direction and two-dimensional E2 u symmetry, which is driven to a nematic order by spontaneous rotation symmetry breaking. The locking energy of the d vector is estimated to be weak and hence the proof of its direction would rely on tunneling or phase-sensitive measurements.

  17. Normal Strength Steel Fiber Reinforced Concrete Subjected to Explosive Loading

    OpenAIRE

    Mohammed Alias Yusof; Norazman Norazman; Ariffin Ariffin; Fauzi Mohd Zain; Risby Risby; CP Ng

    2011-01-01

    This paper presents the results of an experimental investigation on the behavior of plain reinforced concrete and Normal strength steel fiber reinforced concrete panels (SFRC) subjected to explosive loading. The experiment were performed by the Blast Research Unit Faculty of Engineering, University Pertahanan Nasional Malaysia A total of 8 reinforced concrete panels of 600mm x 600mm x 100mm were tested. The steel fiber reinforced concrete panels incorporated three different volume fraction, 0...

  18. Microstructural characterization in dissimilar friction stir welding between 304 stainless steel and st37 steel

    International Nuclear Information System (INIS)

    Jafarzadegan, M.; Feng, A.H.; Abdollah-zadeh, A.; Saeid, T.; Shen, J.; Assadi, H.

    2012-01-01

    In the present study, 3 mm-thick plates of 304 stainless steel and st37 steel were welded together by friction stir welding at a welding speed of 50 mm/min and tool rotational speed of 400 and 800 rpm. X-ray diffraction test was carried out to study the phases which might be formed in the welds. Metallographic examinations, and tensile and microhardness tests were used to analyze the microstructure and mechanical properties of the joint. Four different zones were found in the weld area except the base metals. In the stir zone of the 304 stainless steel, a refined grain structure with some features of dynamic recrystallization was evidenced. A thermomechanically-affected zone was characterized on the 304 steel side with features of dynamic recovery. In the other side of the stir zone, the hot deformation of the st37 steel in the austenite region produced small austenite grains and these grains transformed to fine ferrite and pearlite and some products of displacive transformations such as Widmanstatten ferrite and martensite by cooling the material after friction stir welding. The heat-affected zone in the st37 steel side showed partially and fully refined microstructures like fusion welding processes. The recrystallization in the 304 steel and the transformations in the st37 steel enhanced the hardness of the weld area and therefore, improved the tensile properties of the joint. - Highlights: ► FSW produced sound welds between st37 low carbon steel and 304 stainless steel. ► The SZ of the st37 steel contained some products of allotropic transformation. ► The material in the SZ of the 304 steel showed features of dynamic recrystallization. ► The finer microstructure in the SZ increased the hardness and tensile strength.

  19. Phase transitions and electrical properties of Bi2W1−xNbxO6−y and Bi2W1−xTaxO6−y

    International Nuclear Information System (INIS)

    Kharitonova, E.P.; Voronkova, V.I.; Gagor, A.B.; Pietraszko, A.P.; Alekseeva, O.A.

    2013-01-01

    Highlights: •The limit of Bi 2 W 1−x Me x O 6−y solid solutions is at x = 0.1, 0.15 for Me = Nb, Ta. •Ta and Nb substitutions for W suppress the reconstructive phase transition. •Bi 2 W 0.9 Nb 0.1 O 6−y samples belong to Aurivillius-type structure up to their melting. •Nb and Ta doping shifts ferroelectric transition to low temperatures up to 200 °C. •The highest conductivity reaches 10 −1 S/cm at 800 °C (x = 0.05, 0.1; Me = Nb, Ta). -- Abstract: Polycrystalline samples of Bi 2 W 1−x Me x O 6−y (Me = Nb, Ta) solid solutions have been prepared by solid-state reactions, and the influence of Nb and Ta substitutions for W on the polymorphism and electrical properties of Bi 2 WO 6 has been studied. The limit of the solid solutions is at x = 0.1 for Me = Nb and at x = 0.15 for Me = Ta. The distinctive features of the polymorphism of the Nb- and Ta-doped materials have been identified. According to differential scanning calorimetry data, tantalum and niobium substitutions for tungsten increase the temperature of the high-temperature, orthorhombic-to-monoclinic reconstructive phase transition and suppress the transition starting at x = 0.05 for Me = Nb and x = 0.10 for Me = Ta. As a result, the Bi 2 W 1−x Nb x O 6−y samples have an orthorhombic Aurivillius-type structure up to their melting point. The Bi 2 W 1−x Ta x O 6−y solid solutions at high temperatures consist of a mixture of an orthorhombic and a monoclinic phase. Nb and Ta doping shifts the ferroelectric phase transition to lower temperatures by more than 200 °C, thus markedly extending the stability range of the nonpolar orthorhombic paraelectric phase, which exists in a temperature range as narrow as 930–960 °C in the case of undoped Bi 2 WO 6 . The increase in oxygen vacancy concentration due to heterovalent substitutions of Nb 5+ and Ta 5+ for W 6+ leads to an increase in conductivity by two orders of magnitude relative to the unsubstituted compound

  20. Design of duplex low carbon steels for improved strength: weight applications

    Energy Technology Data Exchange (ETDEWEB)

    Koo, J.

    1977-08-01

    Duplex ferrite-martensite (DFM) steels with excellent combinations of strength and formability have been selected from first principles, and their microstructure-property relationships established through a systematic investigation of a series of ternary Fe/X/0.1 C steels (X being varying amount of Cr and Si). Duplex processing consists of initial austenitization and quenching to form 100% martensite, followed by annealing in the (..cap alpha.. + ..gamma..) range and subsequent quenching. The resultant DFM morphology is controlled by the type and amount of alloying element X.