Development of plastic deformations in 12Kh18N10T steel under cyclic symmetrical bending of specimens of various length

Energy Technology Data Exchange (ETDEWEB)

Pisarenko, G.S.; Leonets, V.A.; Bega, N.D. (AN Ukrainskoj SSR, Kiev. Inst. Problem Prochnosti)

1983-08-01

Effect of specimen length on intensity of plastic deformation development and cyclic strength is studied for annealed 12Kh18N10T steel under cyclic symmetrical bending. The intensity of microplastic deformations and cyclic strength of annealed 12Kh18N10T steel in the considered case is due to self-heating.

Influence of local microplastic strains on stress corrosion of 08Kh18N10T steel

International Nuclear Information System (INIS)

Moskvin, L.N.; Efimov, A.A.; Sherman, Ya.I.; Fedorova, T.I.

1987-01-01

Study on specific features of microhomogeneous strain in the process of plastic strain development and their role in stress corrosion of 08Kh18N10T steel sheet specimens subject to preliminary strain by 1, 3, 6, 16 and 23% and subsequent tests of stress corrosion in magnesium chloride solution at 150 deg C 140 MPa has been carried out. Analysis of test results has shown that microplastic strain is distributed over a specimen nonuniformly and is accompanied with the slip bands formation which are sources of corrosion crack origination and development. 08Kh18N10T steel manifests the highest trend to stress corrosion under 1% microplastic strain

Effect of partial oxygen pressure on physicochemical properties of Kh18N10T steel at isothermal oxidation

International Nuclear Information System (INIS)

Alekseev, V.N.; Oshe, E.K.; Fokin, M.N.; Bogdanova, S.V.; Loskutov, A.I.

1990-01-01

Auger-electron spectroscopy, photoelectric polarization, conductometry methods have been used to analyze chemical and defect composition of surface oxide layers, formed on stainless steel Kh18N10T in vacuum (10 -9 - 10 -2 torr) and at temperatures 593-673 K. The boundary conditions of manifestation of extermal behaviour of the dependence of the surface oxide growth rate at isothermal oxidation of this steel are determined. The relation between passivation properties of the surface oxide and the magnitude of the edge angle of the surface wetting with molten tin is revealed

Effect of preliminary heat treatment on phase transformations and properties of the Kh15N5D2T (VNS-2) steel

International Nuclear Information System (INIS)

Madyanov, S.A.; Voronenko, B.I.; Makhnev, E.S.

1978-01-01

It is shown that preliminary heat treatment has a significant effect on the α→γ transformation kinetics, the quantity of residual austenite, the grain size and mechanical properties of the Kh15N5D2T steel after final heat treatment. The preliminary heat treatment regimes leading to the increase of the quantity of residual austenite and to grain refining increase the work of crack propagation in the finally strengthened state. The optimum properties were obtained after threefold preliminary tempering for 1h at 650 deg C. An approximately constant relation of α- and γ-phases (approximately 50%) is observed at 625 deg C irrespective of the investigated regimes of preliminary heat treatment

Welding of heterogeneous 12Kh2MFSR steels with the Mn-Cr-Si-Ni system

International Nuclear Information System (INIS)

Smirnov, A.N.; Belogolov, E.I.

1978-01-01

The process of welding pipes of the 12Kh2MFSR pearlitic steels and austenitic steels of the Mn-Cr-Si-Ni system was studied. The filler materials were selected, and the working capacity of welded joints was examined in ageing and cyclic heatings. The microhardness of steels was measured, and the ultimate strength of welded joints was determined. The following has been established: the composite joints of steels of the Mn-Cr-Si-Ni system and 12Kh2MFSR steel are advisable to be welded on a coating layer welded by the EhA395/9 electrodes on the surface of a pipe of the 12Kh2MFSR pearlitic steel; this guarantees the sufficient working capacity of welded joints

Cyclic crack resistance of anticorrosion cladding-15Kh2MFA steel joint

International Nuclear Information System (INIS)

Zvezdin, Yu.I.; Nikiforchin, G.N.; Timofeev, B.T.; Zima, Yu.V.; Andrusiv, B.N.

1985-01-01

Cyclie crack resistance of transition zone in austenitic cladding steel 15Kh2MFA joint is studied, taking into account the geometry of fatigue cracks, fracture micromechanism and crack closure effect. Kinetics of crack development from the cladding to the basic metal and vice versa is considered. Microstructure of transition zone is investigated. The results obtained are considered as applied to WWER. It is emphasized, that the braking of fatigue cracks is observed at low asymmetry of loading cycle. Increased loading asymmetry accelerates sharply the alloy fracture due to the growth of subcladding crack, at that, the direction of crack propagation and the structure of transition zone are not of great importance

Simulation of Microdamage and Evaluation of Remaining Life of Steam Conduit Components from New-Generation Refractory Steel 10Kh9MF-Sh

Science.gov (United States)

Gladshtein, V. I.

2018-03-01

The effects of microdamage on the remaining life of high-temperature components of steam conduits from high-chromium steel 10Kh9MF-Sh and low-alloy steel 12Kh1M1F are compared. To simulate the microdamage, specimens with a circular notch and different relative diameters are fabricated. Specimens with a notch simulating the highest degree of microdamage and smooth specimens are tested for long-term strength. The coefficient of the remaining life of a conduit is computed for the range of relative damage presenting practical interest.

Effect of partial oxygen pressure on physicochemical properties of Kh18N10T steel at isothermal oxidation. Vliyanie partsial'nogo davleniya kisloroda na fiziko-khimicheskie svojstva poverkhnosti stali Kh18N10T pri izotermicheskom okislenii

Energy Technology Data Exchange (ETDEWEB)

Alekseev, V N; Oshe, E K; Fokin, M N; Bogdanova, S V; Loskutov, A I [AN SSSR, Moscow (USSR). Inst. Fizicheskoj Khimii

1990-10-01

Auger-electron spectroscopy, photoelectric polarization, conductometry methods have been used to analyze chemical and defect composition of surface oxide layers, formed on stainless steel Kh18N10T in vacuum (10{sup -9} - 10{sup -2} torr) and at temperatures 593-673 K. The boundary conditions of manifestation of extermal behaviour of the dependence of the surface oxide growth rate at isothermal oxidation of this steel are determined. The relation between passivation properties of the surface oxide and the magnitude of the edge angle of the surface wetting with molten tin is revealed.

Neutron diffraction study of a nitrogen martensitic steel 0Kh16N4AB under load

Czech Academy of Sciences Publication Activity Database

Sumin, V. V.; Papushkin, I.V.; Bannykh, O.A.; Blinov, V.M.; Lukáš, Petr

2008-01-01

Roč. 105, č. 1 (2008), s. 88-91 ISSN 0031-918X Institutional research plan: CEZ:AV0Z10480505 Keywords : steel 0Kh16N4AB * neutron diffraction * FSD Subject RIV: BG - Nuclear, Atomic and Molecular Physics , Colliders Impact factor: 0.412, year: 2008

Investigation into the Cyclic Strength of the Bodies of Steam Shutoff Valves from 10Kh9MFB-Sh Steel

Science.gov (United States)

Skorobogatykh, V. N.; Kunavin, S. A.; Prudnikov, D. A.; Shchenkova, I. A.; Bazhenov, A. M.; Zadoinyi, V. A.; Starkovskii, G. L.

2018-02-01

Steam shutoff valves are operated under complex loading conditions at thermal and nuclear power stations. In addition to exposure to high temperature and stresses resulting in fatigue, these valves are subjected to cyclic loads in heating-up-cooling down, opening-closing, etc. cycles. The number of these cycles to be specified in designing the valves should not exceed the maximum allowable value. Hence, the problem of cyclic failure rate of steam shutoff valve bodies is critical. This paper continues the previous publications about properties of the construction material for steam shutoff valve bodies (grade 10Kh9MFB-Sh steel) produced by electroslag melting and gives the results of investigation into the cyclic strength of this material. Fatigue curves for the steal used for manufacturing steam shutoff valve bodies are presented. The experimental data are compared with the calculated fatigue curves plotted using the procedures outlined in PNAE G-002-986 and RD 10-249-98. It is confirmed that these procedures may be used in designing valve bodies from 10Kh9MFB-Sh steel. The effect of the cyclic damage after preliminary cyclic loading of the specimens according to the prescribed load conditions on the high-temperature strength of the steel is examined. The influence of cyclic failure rate on the long-term strength was investigated using cylindrical specimens with a smooth working section in the as-made conditions and after two regimes of preliminary cyclic loading (training) at a working temperature of 570°C and the number of load cycles exceeding the design value, which was 2 × 103 cycles. The experiments corroborated that the material (10Kh9MFB-Sh steel) of the body manufactured by the method of electroslag melting had high resistance to cyclic failure rate. No effect of cyclic damages in the metal of the investigated specimens on the high-temperature strength has been found.

Heat treatment effect on impact strength of 40Kh steel

International Nuclear Information System (INIS)

Golubev, V.K.; Novikov, S.A.; Sobolev, Yu.S.; Yukina, N.A.

1984-01-01

The paper presents results of studies on the effect of heat treatment on strength and pattern of 40Kh steel impact failure. Loading levels corresponding to macroscopic spalling microdamage initiation in the material are determined for three initial states. Metallographic study on the spalling failure pattern for 40Kh steel in different initial states and data on microhardness measurement are presented

Evolution of secondary-phase precipitates during annealing of the 12Kh18N9T steel irradiated with neutrons to a dose of 5 DPA

Science.gov (United States)

Tsai, K. V.; Maksimkin, O. P.; Turubarova, L. G.

2007-03-01

The formation and evolution of thermally-induced secondary precipitates in an austenitic stainless steel 12Kh18N9T irradiated in the core of a laboratory reactor VVR-K to a dose of 5 dpa and subjected to post-radiation isochronous annealings for 1 h in a temperature range from 450 to 1050°C have been studied using transmission electron microscopy (TEM) and microhardness measurements. It has been shown that the formation of stitch (secondary) titanium carbides and M 23C6 carbides at grain and twin boundaries after annealing at 1050°C is preceded by a complex evolution of fineparticles of secondary phases (titanium carbides and nitrides) precipitated at dislocation loops and dislocations during annealing at temperatures above 750°C.

Effect of nonmetallic inclusions on anisotropy of ductility in 35KhN3MFA steel forgings

International Nuclear Information System (INIS)

Shtremel', M.A.; Yavojskij, V.I.; Volkov, V.A.; Chursin, G.M.; Chukhlov, V.I.; Fetisov, G.I.; Mochalin, N.K.; Smol'yaninov, L.V.

1980-01-01

Characteristics of nonmetaltic inclusions and anizotropy of ductility and of impuct strength of forgings of the 35KhN3MFA steel are compared at different variants of melting and outer-furnace treatment. It is shown that method of melting rugulates anisotropy of ductility primarily through deformability of large inclusions during forging. Deformability of inclusions considerably changes due to introduction of silicocalcium in iron mold [ru

Estimation of structural strength of 38KhN3MFA steel, melted using different methods

International Nuclear Information System (INIS)

Kudrya, A.V.; Mochalov, B.V.; Fadeev, Yu.I.

1982-01-01

Quantity of steel melted by different methods using criteria of fracture mechanics is evaluated. Three technological variants of the 38KhN3MFA steel melting: acid Martin steel prepared by the duplex-process (melt 1); the main Martin steel melting with deoxidation and alloying in a ladle by liquid alloy and treatment with synthetic slag with argon purging after production (melt 2) and its electroslag remelt - ESP process (melt 3) are investigated. The analysis of the investigated melts has revealed that crack resistances of the acid Martin steel is higher than that of other melts at practically similar standard mechanical properties with 0.35 probability at 0.05 significance level in the low-tempered state; in the tempered state the best crack resistance is observed in the ESP main Martin steel. Metal of the main Martin melting has lower crack resistance as compared with other meltings at both strength levels. The results of the work point out the necessity of applying the criteria of fracture mechanics for obtaining an objective evaluation of the steel quality

Low-temperature cyclic cracking resistance of Fe-Cr-Ni and Fe-Cr-Mn steels welded joints

International Nuclear Information System (INIS)

Ostash, O.P.; Zhmur-Klimenko, V.T.; Yarema, S.Ya.; Yushchenko, K.A.; Strok, L.P.; Belotserkovets, V.I.

1983-01-01

Results of further investigations into regularities of development of low-temperature fatigue fracture of welded oints in 07Kh13G20AN4 steel are presented, they are compared with analogous data traditional cryogenic 0Kh18N10T and 03Kh13AG19 steels. Welded joints have been prepared by means of automatic V-like level arc Welding of plates; 0Kh18N10T and 07Kh13G20AN4 steels have been welded by means of sv-04Kh19N9 wire, 03Kh13AG19 steel-by means of sv-07Kh13AG19 wire. Tests at almost zero (asymmetry coefficient R=0.05) cycle of extension at 15-20 Hz frequency have been conducted on 5 mm thick disk samples at 20 deg C and - 160 deg C according to the given methods. It is shown that by cyclic crack resistance of welded joint zones of 0Kh18N10T steel and chromium-manganese steels at normal temperature the 07Kh13G20AN4 steel exceeds 0Kh18N10T steel, at low temperature it yields to 0Kh18N10T only by fracture toughness of heat affected zones HAZ and weld metal (ne). 07Kh13G20AN4 steel and its welded joints as most hardened and cheap may be a good substituent for 0Kh18N10T steel. Optimization of WM alloying for increase of its cyclic fracture toughness at cryogenic temperatures is necessary

Ductile fracture of two-phase welds under 77K. [Steel-EhP810, steel-EhP666, steel-08Kh18N10T, steel-EhP659-VI, steel-chP810

Energy Technology Data Exchange (ETDEWEB)

Yushchenko, K.A.; Voronin, S.A.; Pustovit, A.I.; Shavel' , A.V.

The effect of the type of welding and fillers on crack resistance of welded joints high-strength steel EhP810 and its various compounds with steels EhP666, 08Kh18N10T has been studied. For the welding of steel EhP810 with steels EhP810, EhP666, 08Kh18N10T electron-beam, automatic, argon tungsten arc with non-consumable electrode with various fillers, as well as argon metal-arc welding with consumable electrode, were used. It is shown, that for a joint, made by electron-beam welding, parameters sigmasub(u), Ksub(IcJ), KCV are higher than for a joint of a similar phase structure made using filler wire EhP659-VI. It is explained by the fact, that during electron-beam welding joint metal refining takes place, which removes gases. In welded joints of chP810 steel, having joints with austenitic structure, characteristic of crack resistance Ssub(c) increases by more than 0.2 mm in contrast to two-phase joints, which conventional yield strength at 77 K exceeds 1000 MPa. It is worth mentioning, that for other classes of steels formation of two-phase structure of joint increases welded joint resistance to brittle fracture. It is possible to obtain the required structure of joint with assigned level of resistance to brittle fracture by means of the use of different fillers, optimum and welding procedure, regulating the part of the basic metal in joint content.

Effect of metal properties of casts of steel-15Kh1M1FL on the crack resistance at 565 deg C

International Nuclear Information System (INIS)

Gladshtejn, V.I.; Sheshenev, M.F.

1976-01-01

Results are given of prolonged tests of the metal of industrial casts with various fluidity limits. It has been shown experimentally that a quite satisfactory crack resistance is characteristic of a metal with a fluidity limit in the range 30-50 kgf/mm 2 . Metallographic studies have been conducted. Upon variation of the structure and properties of the 15Kh1M1FL steel during operation, the rate of growth of small cracks (up to 2.0 mm) decreases almost by 3 orders of ten (from 1.4x10 -4 to 2.0x10 -7 mm/hour). Subsequent structural changes during prolonged operation (over 50000 hours) result in a gradual increase in the rate of crack growth. At the same time resistance towards appearance of the impermissible high rate of the crack growth, Ksub(10sup(-3)), diminishes monotonically with the operation time. The metal of industrial 15Kh1M1FL steel casts has good crack resistance (Ksub(10sup(-3)) =30-70 kgf/mmsup(3/2) and Vsub(ef) =) kgf/mm 2 ) and a satisfactory local plasticity (critical opening being no more than 0.20 mm for 10 3 hours)

Metallographical procedure for detecting carburized layer in the 12Kh18N10T steel tubes

International Nuclear Information System (INIS)

Najmark, S.I.; Shmalenyuk, R.P.

1977-01-01

The various causes of the tendency to intercrystalline corrosion of stainless steel tubing were studied. 12Kh18N10T steel tube specimens were metallographically investigated to reveal the presence and depth of the carburized layer. Unlubricated specimens and specimens with the graphite-saltpeter lubrication applied on them were austenized in the temperature range from 950 to 1250 deg C and then exposed to a provoking anneal at 650 deg C for 24 h. All the lubricated specimens showed a carbide network along grain boundaries and intercrystalline cracks. The specimens treated without lubrication had no cracks. The method offered can differentiate poor tube cleaning and the undesirable effect of other processing steps on the tubes

Study of 16KhSN high strength steel in different structural states and under working conditions

International Nuclear Information System (INIS)

Skudnov, V.A.; Vorob'ev, I.A.; Kutyajkin, V.G.; Bugrov, Yu.V.

1985-01-01

A study was made on the effect of deformation degree (up to 60%) during reducing, drawing and heat treatment (annealing at 750 deg C), quenching from 930 deg C and tempering at 350 deg C) on strength, plasticity, hardening degree, notch sensitivity, density and elasticity characteristics of the steel. The effect of test temperature (from-196 up to 1000 deg C) on tensile strength and plasticity was studied as well. It was established that drawing and reducing of 16KhSN steel in annealed state with strain degrees of up to 60% results to increase of strength characteristics 1.7...2.3 times and decrease of plasticity characteristics by 15...23%, strain hardening coefficient - 2.2 times and the maximum strain energy - by 80 MJ/m 3 . Hardening heat treatment (quenching from 930 deg C+temperating at 350 deg C) affects on mechanical properties of 16KhSN steel in much the same way as cold working, but strength characteristics of heat-treated steel increase 2.6...3.6 times and the maximum strain energy grows by 640 MJ/m 3 . Systematic data on the effect of temperature (-196...1000 deg C) and tensile rate (4 mm/min...5m/s) on strength and plasticity of 16KhSN steel in annealed state were obtained

Study of cast and thermo-mechanically strengthened chromium-nickel nitrogen-containing steel

International Nuclear Information System (INIS)

Prokoshkina, V.G.; Kaputkina, L.M.; Svyazhin, A.G.

2000-01-01

The effect of nitrogen on the structure and strength of corrosion-resistant chromium-nickel steels after thermal and thermomechanical treatment is studied. The 06Kh15N7AD and 07Kh15N7DAMB steels alloying by nitrogen was accomplished through the basic composition steels remelting in the molecular nitrogen atmosphere under the pressure of 0.1-2.5 MPa. The 02Kh15N5DAF and 05Kh15N5DAM steels ingots were obtained through melting in a plasma furnace under the nitrogen pressure of 0.4MPA. The high-temperature thermomechanical treatment (HTMT) was performed by rolling with preliminary blanks heating up to 1050 deg C and the rolling end temperature not below 950 deg C. It is shown, that the HTMT of the nitrogen-containing steels makes it possible to obtain strength characteristics by 1.5 times exceeding the properties of traditionally applicable corrosion-resistant steels, whereby sufficiently high plasticity of the nitrogen-containing steel is retained [ru

Effect of hydrostatic pressure on phase transformations in Kh17N8 steel during deformation

International Nuclear Information System (INIS)

Eshchenko, R.N.; Teplov, V.A.

1984-01-01

The phase composition and structure of Kh17N8 steel strained to different degrees under atmospheric pressure and 1700 MPa are investigated. It has been found that deformation at 1700 MPa causes α and epsilon-martensite formation, the same deformation under atmospheric pressure - only α-martensite formation. The amount of the formed α-martensite is not changed with application of hydrostatic pressure. Electron-microscopic observations have shown that the dispersion of α-martensite formed under pressure is higher than in the absence of pressure; no interconnection in formation of α and epsilon-martensite in samples strained under pressure has been observed

Structure, mechanical and corrosion properties of powdered stainless steel Kh13

International Nuclear Information System (INIS)

Radomysel'skij, I.D.; Napara-Volgina, S.G.; Orlova, L.N.; Apininskaya, L.M.

1982-01-01

Structure, mechanical and corrosion properties are studied for compact powdered stainless steel, Grade Kh13, produced from prealloyed powder and a mixture of chromium and iron powders by hot vacuum pressing (HVP) following four schemes: HVP of unsintered billets; HVP of presintered billets; HVP of unsintered billets followed by diffusion annealing; HVP of sintered billets followed by diffusion annealing. Analysis of the structure, mechanical and corrosion properties of Kh13 steel produced according to the four schemes confirmed that production of this steel by the HVP method without presintering of porous billets and diffusion annealing of compact stampings is possible only when prealloyed powder of particular composition is used as a starting material

Features of argon-arc welding of aluminium alloy AD1 to stainless steel 12Kh18N10T

International Nuclear Information System (INIS)

Sadov, I.I.

1982-01-01

Welding of pipes made of the 12Kh18N10T stainless steel and the AD1 aluminium alloy is proposed to perform using one-sided aluminizing. It is recommended to use shields in order to protect internal and external surfaces of pipes, aluminizing of which is impossible. It is shown that developed technological process for welded joints made of aluminium and stainless steel for cryogenic apparatus permits to create light-duty cryostat assembly using aluminium alloys instead of copper alloys, to increase reliability of apparatus (usage of welded joints instead of soldered ones), and to improve labour conditions

Changes in structure and phase composition of chromium diffusion layer on stainless steels after long annealing

International Nuclear Information System (INIS)

Knyazev, E.V.; Voshedchenko, B.M.; Voskresenskij, Yu.A.

1985-01-01

A study was made on the effect of elevated temperatures UU and long holdings at heat on structure, phase composition and properties of chromium diffusion layer on austenitic chromium-nickel stainless steels 10Kh18N10TVD, 10Kh15N30M4B, 10Kh11N23T3MR, 10Kh21N28V6M3. The following mechanism of processes taking place in diffusion chromium layer is presented. The steady drop of chromium concentrations is observed after diffusion saturation. Chromium redistribution related with system transformation to more equilibrium state and simultaneous decarburization of steel surfaces takes place in diffusion layers of 10Kh15N30M4B and 10Kh21N28V6M3 steels after annealing at different temperatures and holdings at heat. Decarburization of steel surface layers is practically excluded in diffusion layers of 10Kh18N10T-VD and 10Kh11N23T3MR steels. Diffusion chromium-saturated layer stays effective only on 10Kh18N10T-VD and 10Kh11N23T3MR steels on heating up to 1000 deq C with holding up to 250 h

Effect of agressive medium movement of local corrosion of the steel - 12Kh18N10T

International Nuclear Information System (INIS)

Makartsev, V.V.; Pakhomov, V.S.; Abramova, I.M.

1980-01-01

The effect of agressive medium movement on the formation of pitting corrosion of the 12Kh18N10T stainless steel in the acidic chloride-nitrate solution at room temperature is studied. It is established that the agressive medium movement hinders the formation of pitting corrosion at potentials more negative than +0.4 V and practically does not affect it at more positive potentials. The investigations have been carried out on a disc electrode rotating at a speed from 0 to 2000 rot./min

Effect of neutron irradiation on the properties of the repair welds of the 15Kh2MFA steel

International Nuclear Information System (INIS)

Morozov, A.M.; Khachaturyants, L.V.

1986-01-01

The authors studied the effect of neutron irradiation on the tendency of the metal belonging to the heat affected zone of the weld toward brittle fracture (an increase in the critical temperature of brittleness). For comparison, the authors studied the radiation embrittlement of the original base metal (steel 15Kh2MFA) subjected to the conventional heat treatment of the reactor frames consisting of hardening and high-temperature tempering. Along with these materials, the radiational embrittlement of the base metal in the rehardened condition without tempering was studied. It was concluded that the presence of the regions repaired according to this technology and located in the frame at the level of the reactor core does not pose the problem of decreased resistance to brittle fracture

Effect of preliminary neutron irradiation on helium blistering of 0Kh16N15M3B steel

International Nuclear Information System (INIS)

Chernov, I.I.; Kalin, B.A.; Skorov, D.M.; Shishkin, G.N.; Ivanov, M.V.

1982-01-01

The method of electron microscopy has been applied to investigate the effect of preliminary neutron irradiation on the OKh16N15M3B steel blistering under irradiation by 20 keV helium ions with (1-10)x10 21 ion/m 2 doses at the temperature below 373 K. It is shown that neutron irradiation shifts critical doses of blister formation and intense scaling towards higher doses. But after the incubation period the erosion of steel preliminary neutron irradiated grows with the increase of helium ion dose above 7x10 21 ion/m 2 . Short-term heating of neutron irradiated samples during 15 min at 1173 K does not practically affect the beginning of intense scaling of the surface

Effect of hot rolling on the structure and the mechanical properties of nitrogen-bearing austenitic-martensitic 14Kh15AN4M steel

Science.gov (United States)

Bannykh, O. A.; Betsofen, S. Ya.; Lukin, E. I.; Blinov, V. M.; Voznesenskaya, N. M.; Tonysheva, O. A.; Blinov, E. V.

2016-04-01

The effect of the rolling temperature and strain on the structure and the properties of corrosionresistant austenitic-martensitic 14Kh15AN4M steel is studied. The steel is shown to exhibit high ductility: upon rolling in the temperature range 700-1100°C at a reduction per pass up to 80%, wedge steel specimens are uniformly deformed along and across the rolling direction without cracking and other surface defects. Subsequent cold treatment and low-temperature tempering ensure a high hardness of the steel (50-56 HRC). Austenite mainly contributes to the hardening upon rolling in the temperature range 700-800°C at a reduction of 50-70%, and martensite makes the main contribution at higher temperatures and lower strains. Texture does not form under the chosen deformation conditions, which indicates dynamic recrystallization with the nucleation and growth of grains having no preferential orientation.

Structural inheritance in cast 30KhGNM-type steel

International Nuclear Information System (INIS)

Sadovskij, V.D.; Bershtejn, L.I.; Mel'nikova, A.A.; Polyakova, A.M.; Schastlivtsev, V.M.

1980-01-01

Structural inheritance in the cast 30KhGNM-type steel depending on the heating rate and the temperature of preliminary tempering is investigated. When eating the cast steel with a beinite structure at the rate of 1-150 deg/min, the restoration of austenite grain and the following recrystallization due to the phase cold work, are observed. Slow heating from room temperature or preliminary tempering hinder grain restoration during heating. A non-monotonous effect of tempering temperature on the structural inheritance is established which can be connected with the kinetics of decomposition of residual austenite in steel

Effect of Cr, Ni, and Mo additions on the susceptibility of the 0Kh6n7m7c steel to hot cracking

International Nuclear Information System (INIS)

Tolstykh, L.G.; Pryakhin, A.V.; Popov, A.N.; Usynin, V.F.

1977-01-01

The effect of chromium, molybdenum, and nickel on the tendency of surfacing materials to form hot cracks (Vsub(kp) was studied using the mathematical statistics method. The St3 steel and 38KhN3MFA steel were used in the study. A device facilitating the hot cracking tendency test procedure was developed. It was found that, in the concentration range involved, Ni and Mo produce no effect on Vsub(kp), and Cr enhances it. A new powder wire, PP-OKh7N8M6S, capable of increasing surface material resistance by 1.5-2 times, has been developed

The Kinetics of Bainitic Transformation of Roll Steel 75Kh3MF

Science.gov (United States)

Kletsova, O. A.; Krylova, S. E.; Priymak, E. Yu.; Gryzunov, V. I.; Kamantsev, S. V.

2018-01-01

The critical points of steel 75Kh3MF and the temperature of the start of martensitic transformation are determined by a dilatometric method. The thermokinetic and isothermal diagrams of decomposition of supercooled austenite are plotted. The microstructure and microhardness of steel specimens cooled at different rates are studied. The kinetics of the occurrence of bainitic transformation in the steel is calculated using the Austin-Ricket equation.

Preliminary heat treatment of 4KhM2Fch die steel

International Nuclear Information System (INIS)

Leonidov, V.M.; Berezkin, Y.A.; Nikitenko, E.V.

1986-01-01

To improve the machinability and preparation of the structure for hardening, die steels are given a preliminary treatment which provides a reduction in hardness as a result of separation in the structure of the carbide and ferrite phases, coagulation of the carbides, and acquisition by them of a granular form and also the obtaining of fine grains and a uniform distribution of the structural constituents. The microstructure was evaluated after etching in 4% nital on an MIM-8M microscope. The 4KhM2Fch steel was given a preliminary heat treatment of normalize and anneal. It was concluded that for 4KhM2Fch steel a preliminary heat treatment of normalizing from 950 0 C with a hold of 1.5-2 h, annealing at 750-760 0 C with a hold of 2-3 h, cooling to the isothermal temperature of 670-680 0 C with a hold of 3-4 h, and further air cooling is recommended. The structure after such a heat is granular pearlite with a rating 1-2 and a hardness of 220-250 HB

Steel corrosion in tributyl phosphate in the presence of water and ethyl mercaptan

International Nuclear Information System (INIS)

Pischik, L.M.; Tsinman, A.I.

1979-01-01

Studied is the corrosion of steels St3, 15Kh5M, 08Kh13, 10Kh14G14N4T, 08Kh18G8N2T, 10Kh17N13M2T in TBP, in mixtures of TBP with ethyl mercaptan (EM) and two-phase systems TBP-water and TBP-water-EM at 50-150 deg. In pure TBP St3 corrosion rate is low even at 150 deg. In the presence of water St 3 strongly corrodes at above 50 deg temperature in organic and water layers and also in gas phase. The steel-08Kh18G8N2T at 90 deg in acid TBP is passive and its corrosion rate is lower than 0.01 mm/year. In identical conditions the resistance of stainless steels increases together with chromium content but in TBP with acid number 100 and above at 150 deg all tested steels including steel-10Kh17N13M2T are slightly resistant. Thus, even in absence of corrosion active additions of EM the mixture of TBP-water at higher temperature is agressive in relation not only to carbon steel but also to stainless steels

Investigation of Creep Processes and Microdamages in 10Kh9V2MFBR-Sh High-Chromium Steel

Science.gov (United States)

Grin', E. A.; Pchelintsev, A. V.

2018-01-01

During the modernization and the new construction of power units at TPPs in Russia, high-chromium martensitic steels with higher heat-resistant properties than the traditional perlite steels are increasingly used as structural materials. High-chromium steels have a necessary regulatory support for their use in domestic power engineering. However, up to the present time, the issue of assessing the quality of these steels at the analysis of their state during long-term operation remains open. The article proposed is one of the first attempts to create a system of quality criteria for martensitic steels based on their microdamage parameters. Tests were carried out on the long-term strength and creep of samples from 10Kh9V2MFBR-Sh steel at high temperatures with the construction of creep curves in relative coordinates "deformation related to the deformation of fracture, current time related to time to failure." For some samples, the tests were interrupted and the metal was subjected to metallographic studies consisting of the analysis of microdamage with reference to the accumulated creep strain. It has been shown experimentally that the deformation curve of high-chromium steel differs from the analogous curve of pearlitic steel by a longer and flat section of steady creep and by a sharper transition to the third accelerated creep stage, which has a very short time period (approximately 10% of the total durability). The tendency to the increase in the microdamage of the structure of steel as the accumulated creep strain increases with time was confirmed. The beginning of transition to the final creep phase is characterized by the formation of contours of future pore chains and by the appearance of individual large pores of up to 6 μm in size, the presence of which in the microstructure of the martensitic steel indicates a very significant accumulation of creep strain, and corresponds to the predestruction stage of metal. It is necessary to continue the research to

Successive carbon- and boron saturation of KhVG steel in powder mixtures

Energy Technology Data Exchange (ETDEWEB)

Alimov, Yu A; Gordienko, S I

1975-01-01

Method of successive saturation of KhVG steel with carbon and boron in powder mixtures is described. After carbonization of steel in a charcoal carburator at 930 deg C during 3 hrs a domain of equiaxial large grains is formed there the latter representing carbides of Fe/sub 3/C and (Fe, M)/sub 3/C. The increase of duration of carbonization up to 5 hrs and above results in formation of a cement grid greatly impairing the mechanical properties of the metal. Carbonization is followed by borating in powdered technical boron carbide at 900 deg C for 4 hrs which ensures formation on the sample surface of a borated layer with depth up to 65 mkm covering the carbonized zone. As followed from metallographic and x-ray structural analysis, the borated layer consists of boride needles with complex composition (Fe, Cr, Mn)B. Oil hardening of carbonized KhVG steel from 850 deg C and low-temperature tempering at 180 deg C for 1 hr results in formation in the main metal of martensite-carbide structure and, respectively, in the decrease of the microhardness gradient between the diffusion layers, as compared with borated KhVG steel. Operation tests of strengthened matrices of preforming machines under the conditions of application of dynamic pressing forces up to 1500 kg Fce/cm/sup 2/ demonstrated that the cyclical strength of carboborated coverings is 2.0-3.0 times higher than that of borated ones. The method of carboborating is recommended for strengthening the details of stamp and press tools.

Effect of zirconium on the structure and phase composition of steel 03Kh8SYu

International Nuclear Information System (INIS)

Tarzhumanova, V.A.; Ryabchenkov, A.V.; Shatunova, A.V.; Yoganova, S.A.

1986-01-01

Previously, the authors determined the optimum zirconium content providing retention of a fine-grained structure for steel 03Kh8SYu during high-temperature heating. It was suggested that this was caused by separation in the steel of intermetallic phase Fe 3 Zr. This paper presents results of further studies in this direction. X-ray analysis results for the anodic residues of the steels are presented. It can be seen that in steel without zirconium, carbides of the type M 23 C 6 and M 7 C 3 and aluminum nitride are present. On adding 0.05% Zr, zirconium nitride forms in addition to the existing aluminum nitride and carbides of the type M 7 C 3 . The authors also investigated the effect of zirconium on the tendency of the steel toward grain growth at higher temperature; they studied the structure of steel 03Kh8SYu with 0.61% Zr after soaking specimens for 100 h at 950-1100 C. Results are presented

The effect of thermoplastic treatment regimes on the microplastic strain of nitrogen-containing steel Kh21G10N7MBF

International Nuclear Information System (INIS)

Bannykh, O.A.; Blinov, V.M.; Kostina, M.V.; Grachev, S.V.; Mal'tseva, L.A.

2005-01-01

A study is made into the influence of a percentage reduction during cold rolling and subsequent holdings at heat on development of microplastic deformation when bending sheet specimens of stainless austenitic high-nitrogen steel Kh21G10N7MBF. It is revealed that a maximum value of apparent limit of elasticity (∼1800 MPa) is attained due to plastic deformation by rolling at 20 Deg C with a total percentage reduction of 60 % and subsequent aging at 500 Deg C for 1-4 h [ru

Influence of sulphur and phosphorus impurities on ductility of 25Kh2NMFA steel during forging

International Nuclear Information System (INIS)

Onishchenko, A.K.

1989-01-01

Using cylindrical samples of the 25Kh2NMFA steel with sulfur and phosphorus content in the range of 0.001-0.030%, tensile test with the rate of deformation 10 -3 s -1 at the temperatures of 800-1200 deg C has been conducted. Analysis of fracture foci and plasticity diagrams has shown, that to ensure ductility during forging and high mechanical properties, the content of sulfur and phosphorus impurities in the 25Kh2NMFA steel must not exceed 0.015%

Effect of smelt aluminium on mechanical properties of steels

International Nuclear Information System (INIS)

Ryabov, V.R.; Dykhno, I.S.; Deev, G.F.; Karikh, V.V.

1987-01-01

Effect of smelt aluminium on mechanical properties of armco-iron and 12 Kh18N10T steel is studied. It is stated that in smelt aluminium and aluminium alloy contact with armco-iron the sample ductility is decreased. Corrosion effect of smelt alluminium on (18Kh15N5AM3) steel in the form of reinforced wire in aluminium-steel KAS-1A composite material is investigted. It is stated in experiment that during smelt alluminium-steel contact interaction of heterogeneous phases takes place

Effect of boron control of environment on corrosion and resistance to low-cycle corrosion fatigue in structural steels

International Nuclear Information System (INIS)

Babej, Yu.I.; Zhitkov, V.V.; Zvezdin, Yu.I.; Liskevich, I.Yu.; Nazarov, A.A.

1982-01-01

Tests of the specimens on total, contact and crevice corrosion, corrosion cracking and low-cycle fatigue are conducted for determination of corrosion and corrosion-fatigue characteristics in the 15Kh3NMFA, 10N3MFA, 10Kh16N4B, 05Kh13N6M2 structural steels, used in energetics. The environment is subjected to boron control and contacting with atmosphere for simulation of stop and operation modes of the facility. The experiments are carried out in the distilled water with 12g/l H 3 BO 3 and 10 mg/l Cl' at 25, 60, 100 deg C under contacting with atmosphere. It is established, that the pearlitic steels 15Kh3NMFA, 10N3MFA, as well as transition and martensitic 05Kh13N6M2 and 10Kh16N4B steels are highly stable to total, crevice and contact corrosion at the high parameters of aqueous boron-containing medium. Steel resistance to low-cycle fracture decreases slightly under the conditions similar to the operation ones, in the water with 12 g/l H 3 BO 3 . Durability of the pearlitic steels at the simulation of stop conditions decreases more noticeably, crack formation as a rule, initiating from corrosion spots

Hydrogen effect on mechanical properties and flake formation in the 10KhSND steel rolled plates

Energy Technology Data Exchange (ETDEWEB)

Muradova, R G; Zakharov, V A; Kuzin, A P; Gol' tsov, V A; Podgajskij, M S [Donetskij Politekhnicheskij Inst. (Ukrainian SSR); Donetskij Nauchno-Issledovatel' skij Inst. Chernoj Metallurgii (Ukrainian SSR))

1982-01-01

The effect of hydrogen on mechanical properties of the 10KhSND steel rolled plates during natural aging is studied. Optimum period of metal acceptance tests, which are advisable to conduct after 5-7 day natural aging of finished products, are found out. The technique is worked out and a safe hydrogen content to prevent flake formation in the 10KhSND steel is determined. It is shown that a safe hydrogen content is dependent on the experiment conditions (sample dimensions, conditions of cooling, and prehistory).

Hydrogen effect on mechanical properties and flake formation in the 10KhSND steel rolled plates

International Nuclear Information System (INIS)

Muradova, R.G.; Zakharov, V.A.; Kuzin, A.P.; Gol'tsov, V.A.; Podgajskij, M.S.

1982-01-01

The effect of hydrogen on mechanical properties of the 10KhSND steel rolled plates during natural aging is studied. Optimum period of metal acceptance tests, which are advisable to conduct after 5-7 day natural aging of finished products, are found out. The technique is worked out and a safe hydrogen content to prevent flake formation in the 10KhSND steel is determined. It is shown that a safe hydrogen content is dependent on the experiment conditions (sample dimensions, conditions of cooling, and prehistory)

Protective effect of KhOSP-10 inhibitor during corrosion, hydrogenadsorption and corrosion cracking of a steel in sulfuric acid

Energy Technology Data Exchange (ETDEWEB)

Mindyuk, A K; Svist, E I; Savitskaya, O P; Goyan, E B; Gopanenko, A N [AN Ukrainskoj SSR, Lvov. Fiziko-Mekhanicheskij Inst.

1975-01-01

The protective propeties of inhibitor KhOSP-10 in the time of corrosion and corrosive cracking of steel 40Kh are higher then those of inhibitors KPI-1, KI-1, I-I-V etc. Its ability to reduce steel hydrogenation is the same as in the case of KPI-1 inhibitor i.e. below that of KI-1. HCl additives enhance the efficiency of inhibitors KPI-1, KI-1, I-1-V etc. up to the protective ability of KhOSP-10. Kinetics of the electrode processes was estimated from polarization curves.

Cooling rate and microstructure of surface layers of 5KhNM steel, machined by electroerosion method

International Nuclear Information System (INIS)

Foteev, N.K.; Ploshkin, V.V.; Lyakishev, V.A.; Shirokov, S.V.

1982-01-01

The cooling rate and microstructure of surface layers of steel 5KhNM machined by electroerosion method have been studied. It is shown that the difference in heating rate of the surface layers with electric discharge over the 5KhNM steel samples depth results in the intensive size reduction of the microstructure. In the surface layer alongside with martensite residual austenite is present, the lattice period of which increases with the increase of pulse duration, carbide phase of complex composition appears, and concentrational heterogeneity in alloying elements (except carbon) is absent

Cooling rate and microstructure of surface layers of 5KhNM steel, machined by electroerosion method

Energy Technology Data Exchange (ETDEWEB)

Foteev, N.K.; Ploshkin, V.V.; Lyakishev, V.A.; Shirokov, S.V.

1982-01-01

The cooling rate and microstructure of surface layers of steel 5KhNM machined by electroerosion method have been studied. It is shown that the difference in heating rate of the surface layers with electric discharge over the 5KhNM steel samples depth results in the intensive size reduction of the microstructure. In the surface layer alongside with martensite residual austenite is present, the lattice period of which increases with the increase of pulse duration, carbide phase of complex composition appears, and concentrational heterogeneity in alloying elements (except carbon) is absent.

Quality of austenite chrome-nickel steel made by gas-oxygen refining

International Nuclear Information System (INIS)

Fel'dgandler, Eh.G.; Levin, F.L.; Moshkevich, E.A.; Shifrin, Eh.V.; Movshovich, V.S.; Pargamonov, E.A.

1991-01-01

Properties and structure were investigated of austenitic 03Kh18N11 and 08KhN10T steels melted at gas oxygen refining aggregates. It was established that mechanical and corrosion properties of rolling of such steels were in agreement with standard properties of metal of open melting. Sheet 08Kh18N10T steel has the level of strength and plasticity regulated for 12Kh18N10T steel. As steel of 08Kh18N10T holds the complex of high mechanical and corrosion properties, 08Kh18N10T is recommended to be replace by 12Kh18N10T with the aim of decrease of titanium usage and increase of process efficiency

Coarsening of (Fe, Cr)23C6 carbide phase on the tempering of 14Kh17N2 chromium-nickel steel

International Nuclear Information System (INIS)

Psarev, V.I.

2002-01-01

Paper lists the results of computer analysis of distribution according to sizes (Fe, Cr) 23 C 6 microparticles resulting from 14Kh17N2 steel tempering under 700 Deg C. Data were obtained at the maximum beneficial magnification of a light microscope. The mentioned curves of distribution densities are characterized by more reliable run from most permissible sizes of dispersed particles. Application of general rules of distributions and of previously elaborated procedure to identify experimental histograms with theoretical distributions enables to derive valuable information on dynamics of coarsening of a disperse phase in this case, as well [ru

Radiation embrittlement of WWER 440 pressure vessel steel and of some improved steels by western producers

International Nuclear Information System (INIS)

Koutsky, J.; Vacek, M.; Stoces, B.; Pav, T.; Otruba, J.; Novosad, P.; Brumovsky, M.

1982-01-01

The resistance was studied of Cr-Mo-V type steel 15Kh2MFA to radiation embrittlement at an irradiation temperature of around 288 degC. Studied was the steel used for the manufacture of the pressure vessel of the Paks nuclear reactor in Hungary. The obtained results of radiation embrittlement and hardening of steel 15Kh2MFA were compared with similar values of Mn-Ni-Mo type steels A 533-B and A 508 manufactured by leading western manufacturers within the international research programme coordinated by the IAEA. It was found that the resistance of steel 15Kh2MFA to radiation embrittlement is comparable with steels A 533-B and A 508 by western manufacturers. (author)

Corrosion behaviour of stainless steels by internal friction method

International Nuclear Information System (INIS)

Postnikov, V.S.; Kovalevskij, V.I.

1987-01-01

Corrosion of austenite chromium-nickel stainless steels 12 Kh18N9, 12Kh18N9T, 12Kh18N10 and 12Kh18N10T is investigated. Wire samples 0.7...0.8 mm in diameter before tests were subjected to quenching in water from the temperature of 1050...1100 deg C and part of them - to tempering at 650 deg C for 2 h. Pitting corrosion was brought about by different concentration of iron chloride solutions (C FeCl 3 ). Total corrosion has a slight effect on the character of IF (internal friction) variation that increases without the whole test period up to the moment when mechanical strength of the sample

On the protective effect of KhOSP-10 inhibitor during corrosion, hydrogenadsorption and corrosion cracking of a steel in sulfuric acid

International Nuclear Information System (INIS)

Mindyuk, A.K.; Svist, E.I.; Savitskaya, O.P.; Goyan, E.B.; Gopanenko, A.N.

1975-01-01

The protective propeties of inhibitor KhOSP-10 in the time of corrosion and corrosive cracking of steel 40Kh are higher then those of inhibitors KPI-1, KI-1, I-I-V etc. Its ability to reduce steel hydrogenation is the same as in the case of KPI-1 inhibitor i.e. below that of KI-1. HCl additives enhance the efficiency of inhibitors KPI-1, KI-1, I-1-V etc. up to the protective ability of KhOSP-10. Kinetics of the electrode processes was estimated from polarization curves

Effect of the isothermal transformation temperature on the fine structure of steel-12Kh1MF

International Nuclear Information System (INIS)

Mints, I.I.; Berezina, T.G.; Lanskaya, K.A.

1976-01-01

For detailed analysis of bainite and pearlite in steel 12Kh1MF, homogeneous structures were obtained by isothermal annealing at 350, 450, 500, and 650 0 for 1 h. Isothermal transformation of austenite leads to the formation of bainite at 350-500 0 and pearlite at 650 0 . The austenitizing temperature was 980 0 for both types of samples, with holding for 20 min. For comparison, the plates were quenched from 980 0 and 1050 0 in ice-cold brine. The investigation was conducted with use of light and electron microscopes and x-ray analysis. The long-term strength was also determined. Isothermal treatment of steel 12Kh1MF at 350-500 0 C leads to the formation of a structure consisting of upper and lower bainite. At 500 0 the structure consists primarily of upper bainite, and at 350 0 of lower bainite. With tempering of the steel with a structure of upper and lower bainite at 730 0 for 3 h the dislocations undergo redistribution of the polygonization type within ferrite needles, with development of a cellular substructure. The acicular structure of the matrix is retained in this case. The density and evenness of the distribution of carbides is higher in upper bainite than in lower bainite. Steel 12Kh1MF with a structure of upper bainite is more susceptible to recrystallization as compared with a structure of lower bainite, which is responsible for the higher heat resistance of the latter

Defect accumulation in welded joints of 12Kh1MF steel steam pipelines during creep

International Nuclear Information System (INIS)

Anokhov, A.E.; Alekhova, I.A.

1982-01-01

Technique for investigation of micropore accumulation in 12Kh1MF steel welded joints is proposed. The micropore density in different zones of welded joints in non-uniform. It is shown that failure localization in welded joint in the softening zone during the creep takes place due to the micropore priority accumulation in this zone. It is found out that accumulation of residual deformations in different zones of 12Kh1MF welded joints under creep runs more uniformly as the level of working stresses decreases and test duration increases

On change of vanadium carbide state during 20Kh3MVF steel heat treatment

International Nuclear Information System (INIS)

Gitgarts, M.I.; Maksimenko, V.N.

1975-01-01

The Xray diffraction study of vanadium carbide MC has been made in the steel-20KH3MVF quenched from 970 and 1040 deg and tempered at 660 deg for 210 hrs. It has been found that the constant of the MC crystal lattice regularly varies with the temperature of isothermal hold-up. In the steel tempered after quenching two vanadium carbides of different content could co-exist simultaneously: carbide formed in the quenching process and carbide formed during tempering. The discovered effect of the temperature dependence of the MC content is, evidently, inherent also to other steels containing vanadium

Superheat effect on bainite steel hardenability

International Nuclear Information System (INIS)

Kubachek, V.V.; Sklyuev, P.V.

1978-01-01

The bainite hardenability of 34KhN1M and 35 KhN1M2Ph steels has been investigated by the end-face hardening technique. It is established that, as the temperature of austenitization rises from 900 to 1280 deg C, the temperature of bainite transformation increases and bainite hardenability of the steels falls off. A repeated slow heating to 900 deg C of previously overheated 34KhN1M steel breaks up grain, lowers the temperature of the bainite transformation and raises the hardenability to values obtained with ordinary hardening from 900 deg C. A similar heating of previously overheated 35KhN1M2Ph steel is accompanied by restoration of initial coarse grains and maintenance of both the elevated bainite transformation temperature and to lower hardenability corresponding to hardening from the temperature of previous overheating

Effect of silicon on the structure, tribological behaviour, and mechanical properties of nitrogen-containing chromium-manganese austenitic steels

International Nuclear Information System (INIS)

Korshunov, L.G.; Chernenko, N.L.; Gojkhenberg, Yu.N.

2003-01-01

The effect of silicon in quantity of 3.5-4.5 mass. % on tribological behaviour is studied for nitrogen-bearing (0.20-0.52 mass. % of nitrogen) chromium-manganese austenitic steels (10Kh15G23S4A0.20, 10Kh16G17N3S4A0.30, 10Kh19G20NS4A0.50, 12Kh19G19NS2A0.50, 10Kh18G19A0.50, 08Kh16G8N10S4A0.18). Mechanical properties and corrosion resistance of the steels are determined. Using metallographic, x-ray diffraction and electron microscopical methods a study is made into structural transformations running in the steels considered under friction and static tension. It is shown that additional silicon alloying of nitrogen-bearing chromium-manganese austenitic steels results in an essential increase of adhesion wear resistance of the materials on retention of low friction coefficient (f=0.25-0.33). A strong silicon effect on steel tribological behaviour is related with planar slip activation and with an increase of austenite strength and heat resistance [ru

Manufacture of rings of 08Kh18N10T sheet for internal structures of WWER type reactors

International Nuclear Information System (INIS)

Fojta, A.; Nitka, B.

1984-01-01

Technology is presented of the manufacture of rings for the jacket, shaft, core catcher and shaft bottom of WWER-440 reactors produced by Vitkovice Steel Works. The rings are manufactured from sheets of austenitic steel 08Kh18N10T. The materials and technology problems are discussed of sheet production, ring welding technology and annealing following welding. The plastic properties are assessed of the welded joints and problems are outlined of ring production for WWER-1000 reactors. (B.S.)

Influence of structure and properties of tubular billets of the 12 Kh 18N10T steel on deformability of tubes at cold-rolling mills

International Nuclear Information System (INIS)

Vil'yams, O.S.; Bol'shova, N.M.; Olejnik, O.V.; Velikotnaya, E.S.

1979-01-01

Metallographic analysis of the defects of the ''oblique cracks'' type on the surface of hot-rolled tubes of the 12Kh18N10T steel has been carried out. Recommended is the complex of mechanical properties and the structure factors (grain size) of conversion hot-rolled tubes, providing the combination of ductility and high rapture strength during rolling at pilger mills. At a grain size not coarser than number 5, a billet must have σsub(T) 5 >=40 %. Hot-rolled coarse-grained billet is not recommended for warm rolng because of high strain hardening

On the low-cycle fracture of chromium-nickel-molybdenum structural steels in seawater

International Nuclear Information System (INIS)

Karpenko, G.V.; Kobzaruk, A.V.; Malyshevskij, V.A.; Shul'te, A.Yu.; Rybin, V.V.; Silaev, I.I.

1977-01-01

The processes of low-cycle fracture of the chrome-nickel-molybdenum steels 15KhN5MF, 12KhN4MF and 15KhN3M in air, and in sea water have been investigated by the optical microscopy method, and electron microscopic examination of thin films. Bringing no change in the fracture character, sea water produces a speeding-up effect on the low-cycle fatigue fracture process. During long-time corrosion fatigue testing considerable importance lies with the electrochemical corrosion factor expediting the occurrence of corrosive pits acting as crack-initiation nuclei, fatigue crack attack, accumulation of corrosion products in fatigue cracks, etc

[Gao Jingyi. Han yu yu bei Ou yu yan : Han yu yu Wula'er yu yan ji Yin Ou yu yan tong yuan tan jiu] / Ago Künnap

Index Scriptorium Estoniae

Künnap, Ago, 1941-

2010-01-01

Arvustus: Gao Jingyi. Han yu yu bei Ou yu yan : Han yu yu Wula'er yu yan ji Yin Ou yu yan tong yuan tan jiu = Chinese language and languages of northern Europe. Beijing : Zhongguo she hui ke xue chu ban she, 2008

Annealing effect on restoration of irradiation steel properties

International Nuclear Information System (INIS)

Vishkarev, O.M.; Kolesova, T.N.; Myasnikova, K.P.; Pecherin, A.M.; Shamardin, V.K.

1986-01-01

The effect of temperature and annealing time on the restoration of properties of the 15Kh2NMFAA and 15Kh2MFA steels after irradiation at 285 deg with the fluence of 6x10 23 neutr/m 2 (E>0.5 MeV) is studied. Microhardness (H μ ) restoration in the irradiated 15Kh2NMFAA steel is shown to start from 350 deg C annealing temperature. The complete microhardness restoration is observed at the annealing temperature of 500 deg C for 10 hours

On choice of tempered steels

International Nuclear Information System (INIS)

Govorov, A.A.; Pan'shin, I.F.; Rakhmanov, V.I.

1978-01-01

For the purpose of developing a graphical method for choosing structural steels, a change in the propagation work of a crack and in the critical temperature of brittleness of 40, 40Kh, 40KhN, and 40KhNM steels, was examined depending on the hardness after hardening and tempering. A diagram enabling to choose the grade of steel for making an article of known dimensions according to the preset values of its mechanical properties has been plotted. The developed selection scheme takes into account the hardenability of steels and the influence of the hardness after thermal treatment on the cold-shortness of steel

Effect of melting technique on grain size and heat resistance of the 12Kh1MF steel

International Nuclear Information System (INIS)

Lanskaya, K.A.; Kulikova, L.V.; Butneva, N.I.

1978-01-01

Investigated are the 12Kh1MF steel melted in open-hearth and arc furnaces (deoxidation by aluminium in 1.0 kg/t quantity) and then subjected to electroslag melting. The size of an austenitic grain depends on the residual contents of nitrogen and aluminium in steel. The open-hearth metal subjected to electroslag melting and containing a small quantity of nitrogen (0.006%) and aluminium (0.013%) has coarse austenitic grains and higher heat resistance compared to the steel melted in an arc furnace and also sub ected to electroslag melting. The nitride analysis of steel is carried out

Specific features of precipitation hardening of austenitic steels with various base. 2. Kinetics and mechanism of carbide precipitation

International Nuclear Information System (INIS)

Kositsyna, I.I.; Sagaradze, V.V.; Khakimova, O.N.

1997-01-01

Electron microscopic studies were carried out to determine the kinetics and mechanisms of precipitation hardening in Fe-Mn, Fe-Mn-Cr, Fe-Cr-Mn-N, Fe-Cr-Ni and Fe-Ni base stainless steels (45G20M2F2, 50Kh16G15N6M2F2, 45Kh18N10G10M2F2, 40Kh18Ni18M2F2, 45N26M2F2). The steels were heat treated under various conditions. It is revealed that in manganese steels the particles of vanadium carbide nucleate according to homogeneous mechanism at all aging temperatures (600-750 deg C). The presence of chromium in the matrix promotes the transition to heterogeneous mechanism of carbide nucleation and growth. With nickel content increasing the plasticity of precipitation hardened steels gets better due to more intense diffusion of atoms and vacancies to grain boundaries and, hence, the widening of near-boundary zones free of carbide particles

Structural steels for power generating equipment and heat and chemical heat treatments

International Nuclear Information System (INIS)

Astaf'ev, A.A.

1979-01-01

Development of structural steels for power generating equipment and for reactor engineering, in particular, is elucidated. Noted is utilization of the 15Kh2NMFA steels for the WWER-1000 reactor vessels, the 10GN2MFA steels for steam generators, pressurizers, vessels of the automatic emergency shut down and safety system; the 00Kh12N3DL steel for cast pump vessels and main locking bars. The recommendations on heat treatment of big forgings, for instance, ensuring the necessary complex of mechanical properties are given. Diffusion chromizing with subsequent nitriding of austenitic steels which increase durability of the components in BN reactors more than 4 times, is practised on a large scale

Metastable structure formation during high velocity grinding

International Nuclear Information System (INIS)

Samarin, A.N.; Klyuev, M.M.

1984-01-01

Metastable structures in surface layers of samples are; investigated during force high-velocity abrasive grinding. Samples of martensitic (40Kh13), austenitic (12Kh18N10T), ferritic (05Kh23Yu5) steels and some alloys, in particular KhN77TYuR (EhI437B), were grinded for one pass at treatment depth from 0.17 up to 2.6 mm. It is established that processes of homogenizing, recrystallization and coagulation are; developed during force high-velocity grinding along with polymorphic transformations in the zone of thermomechanical effect, that leads to changes of physical and mechanical properties of the surface

Preliminary tension effect on low-cycle fatigue of 40Kh13 steel in gaseous hydrogen

International Nuclear Information System (INIS)

Romaniv, A.N.

1984-01-01

Comparative bending tests of specimens deformed by tension at 65, 18 and 30% in hydrogen and vacuum were accomplished to reveal the effect of preliminary tension on low-cycle fatigue strength of 40Kh13 martensitic steel. It was found that small amounts of preliminary strains induced a considerable decrease in low-cycle durability in vacuum and hydrogen which was connected with developing defects arising at the early stages of plastic deformation. A rather high degree of preliminary tension promoted steel homogenization, hydrogen embrittlement decrease and service behaviour improvement

Methods for protection of high-strength welded stainless steel from corrosion cracking

International Nuclear Information System (INIS)

Lashchevskij, V.B.; Gurvich, L.Ya.; Batrakov, V.P.; Kozheurova, N.S.; Molotova, V.A.; Shvarts, M.M.

1978-01-01

The efficiency of protection from corrosion cracking under a bending stress of 100 kgf/mm 2 in a salt mist and in a sulphur dioxide atmosphere, of welded joints of steel 08Kh15N5D2T with metallizing, galvanic and varnish coatings and lubricants, and of steel 1Kh15N4AM3 with sealing compounds has been investigated. Metallization of welded joints with aluminium and zinc efficiently increases corrosion resistance in a salt mist. Galvanic coatings of Cd, Zn, and Cr increase the time to cracking in a salt mist from 2-3 to 60-80 days. The protective properties of varnishes under the effect of a salt mist decrease in the following sequence: epoxy-polyamide enamel EP-140, acrylic enamel C-38, silicone enamels KO-834, KO-811, and KO-814. In an atmosphere containing SO 2 0.15 vol.% at 100% relative humidity, the varnishes investigated, with the exception of the inhibited coating XC-596, show lower protective properties than in a salt mist. The high efficiency of protection from corrosion cracking in a salt mist of slots of steel 1Kh15N4AM3 when using organic sealing compounds U4-21 and U5-21, and also slushing lubricants and oils PVK, TsIATIM-201, K17, and AMS3 was established

Effect of reactor irradiation on long-term strength and creep of 0Kh16N15M3B steel under plane stressed state

International Nuclear Information System (INIS)

Khristov, G.P.; Kosov, B.D.

1982-01-01

The paper deals with analysis of results of experimental studies in creep of the austenitic OKh16n15m3b steel with various size of initial-structure grain under conditions of high-intensity reactor irradiation and control tests. It is suggested to consider the material initial structure effect on intensity of minimum creep rates both under ordinary and intrareactor conditions of loading by means of the function grain size effect on the equivalent stress. It is shown that the criterial expression previously suggested by the authors is invariant to the type of stressed and structural states and relative to intensity of minimal creep rates. It is established that the creep rate of the irradiated steel may be calculated from dependence for nonirradiated steel using as an argument a certain reduced equivalent stress which is a function of the acting stress and irradiation parameter

Stationary potentials and corrosion of metals and steels in sodium and potassium chloride eutectic melts saturated with hydrogen chloride

International Nuclear Information System (INIS)

Belov, V.N.; Ershova, T.K.; Kochergin, V.P.

1978-01-01

Stationary potentials have been measured at 850 deg C and corrosion rates found gravimetrically for a number of metals and steels in the eutectic NaCl-KCl melt saturated with HCl. Periodic shifts of the stationary potentials towards positive values have been established in the Ti-V-Cr-Fe-Ni, Cu-Zr-Nb-Mo, Ag-Ta-W-Pt systems, with the corrosion rate of metals decreasing in them. The stationary potentials are shown to shift towards positive values in the series: st.08 KP, st.3, Kh17N2, Kh22N6T, Kh13NChG9, 1Kh18N10T, Kh17N13M2T, OKh17N16M3T, Kh23N18, Kh25N16G7, Kh23N28M3D3T, with corrosive resistance in this series increasing

Effect of Heat Treatment on the Structure and Properties of Die Steel 70Kh3G2FTR

Science.gov (United States)

Krylova, S. E.; Kletsova, O. A.; Gryzunov, V. I.; Fot, A. P.; Tavtilov, I. Sh.

2018-01-01

The effect of heat treatment parameters on the properties and structural and phase composition of a promising die steel 70Kh3G2FTR for hot deformation is studied. The temperature-and-stress state of a hammer die under a heat treatment is simulated.

Corrosion failure of a bolt made of the 25Kh1MF material

International Nuclear Information System (INIS)

Liska, V.; Cechova, D.; Velkoborsky, J.

1989-01-01

M36x4 bolts, of which there are 222 at each nuclear power plant unit, are made of the 25Kh1MF or 38KhN3MFA steel. They are located in an environment with elevated temperature, with damp air and with boric acid. Corrosion of these bolts is due to the rather poor metallurgical quality of the steel. No inadmissible inhomogeneities of the type of lines of inclusions occur in the bolt material produced by cold rolling but defects of the type of laps were found on the threads. It is suggested that if the cold rolling technology were obviated, corrosion failure of the bolts might not occur. (M.D.). 7 figs., 3 refs

Ductility of high chromium stainless steels

International Nuclear Information System (INIS)

Peretyat'ko, V.N.; Kazantsev, A.A.

1997-01-01

Aimed to optimize the hot working conditions for high chromium stainless steels the experiments were carried in the temperature range of 800-1300 deg C using hot torsion tests and cylindrical specimens of ferritic and ferritic-martensitic steels 08Kh13, 12Kh13, 20Kh13, 30Kh13 and 40Kh13. Testing results showed that steel plasticity varies in a wide range depending on carbon content. Steels of lesser carbon concentration (08Kh13 and 12Kh13) exhibit a sharp increase in plasticity with a temperature rise, especially in the interval of 1200-1250 deg C. Steels 20Kh13 and 30Kh13 display insignificant plasticity increasing, whereas plastic properties of steel 40Kh13 increase noticeably in the range of 1000-1300 deg C. It is shown that optimal hot working conditions for specific steel must be selected with account of steel phase composition at high temperatures

Effect of nickel and MnS inclusions in the metal on the pitting corrosion of low-carbon stainless steels

International Nuclear Information System (INIS)

Frejman, L.I.; Nguen, The Dong; Volkov, D.E.; Konnov, Yu.P.

1986-01-01

The resistance to pitting corrosion of steels on the 03Kh17-03Kh18 base containing up to 20 % Ni at different levels of S and Mn impurities contamination is investigated. It is shown that up to 50 % of nickel introduced into ordinary steels with 5-6 % Ni is spent to compensate the resistance decrease caused by MnS inclusions. Full compensation is not attained even in the 10-20 %. Ni range in which nickel practically does not affect the resistance of neither ordinary, nor pure (without MnS) steels. Titanium introduction into ordinary steel on the Kh22N6 base permits to surpass the level of 03Kh17N3 pure steel resistance and attain the level of 03Kh17N6 pure steel almost by all characteristics (including passivated characteristics in sulfuric acid) besides pitting repassivity. In this property pure steels with Ni >or approx. 3 % surpass even the molybdenum containing 03Kh21NbM2T ordinary steel though they by far concede by passivation in sulfuric acid

Effect of austenitization conditions on kinetics of isothermal transformation of austenite of structural steels

International Nuclear Information System (INIS)

Konopleva, E.V.; Bayazitov, V.M.; Abramov, O.V.; Kozlova, A.G.

1987-01-01

Effect of austenization of kinetics of pearlite and bainite transformations for steels with different carbon content differing by alloying character and degree has been investigated. Austenization temperature increase is shown to leads to retardation of ferrite-pearlite transformation in low- and medium-carbon alloyed steels. Step-like holding in the region of austenite stable state (850, 950 deg) after high-temperature heating (1100 deg C) increases the rate of transformation partially recovering its kinetics and decomposition velocity after low-temperature heating in steels alloyed advantageously with carbide-forming elements (08Kh2G2F, 30Kh3) and does not affect kinetics in the 35Kh, 30KhGSN2A, 45N5 steels. Increase of heating temperature and growth of an austenite grain cause considerable acceleration of bainite transformation, increase of the temperaure of bainite transformation beginning and increase of the transformation amplitude in the 08Kh2G2F, 30Kh3 steels and affect weakly kinetics in steels with mixed alloying (30KhGSN2A) or low-alloy one (35Kh). The bainite transformation rate in the 45N5 steelite does not depend on austenization. The effect of additional acceleration of bainite transformation as a result holding after high-temperature heating in those steels, where activation of transformation occurs with increase of heating temperature

Comments on Yu N Parkhomenko's paper 'Role of aberration effects in dispersive cavities'

International Nuclear Information System (INIS)

Anokhov, S P

1999-01-01

The legitimacy of the approach, proposed by Yu N Parkhomenko for dealing with the operation of solid-state lasers with dispersive cavities, is discussed. Additional information is provided on the neodymium glass laser, used in the present author's experiment. Comment on A Yu N Parkhomenko 1998 Quantum Electron. 28 1102. (discussion)

Local corrosion of high alloy steels under biodeposits

International Nuclear Information System (INIS)

Korovyakova, M.D.; Nikitin, V.M.; Speshneva, N.V.

1999-01-01

Impact of the bacteriozenosis different structural-functional state under biodeposits on corrosion resistance of the 12Kh18N10T and Kh18N10T high-alloy steels in the natural seawater is studied. It is shown that saturation of natural micro communities by separate aerobic and facultative-anaerobic bacterial monocultures increases corrosion resistance of these steels by their overgrow with biodeposits [ru

Influence of isothermal thermomechanical treatment on structure and properties of structural steels

International Nuclear Information System (INIS)

Smirnov, M.A.; Kaletin, A.Yu.; Schastlivthev, V.M.; Kaletina, Yu.V.

1997-01-01

A study is made into the structure and mechanical properties of steel 35KhGSA and 37KhN3A after isothermal hardening resulting in bainitic structure formation as well as after low-temperature thermomechanical treatment (LTTMT) combining the plastic deformation at the temperature of bainitic transformation and subsequent isothermal hardening. It is shown that LTTMT permits and essential enhancement of strength properties in steel 35KhGSA, high plasticity and impact strength being reserved. This is associated with bainitic structure refinement. In steel 37KhN3A the process of carbide formation takes place along with bainitic transformation, and LTTMT results in lesser strengthening. LTTMT is fount to not practically affect the tendency of structural steels to bainitic brittleness. This treatment promotes some shift of brittleness manifestation to lower temperatures

On the adsorption-induced fatigue of structural steels in the presence of alcohols

International Nuclear Information System (INIS)

Loboiko, V.I.; Karpenko, G.V.; Vasilenko, I.I.

1976-01-01

The purpose of the work was to study he effect of anhydrous alcohols on the cyclic fatigue of steels in the absence of contact of the alcohol with atmospheric moisture during the testing process. A vacuum was created in the operating space and then the vacuum annealing was carried out in a bath with the sample and through metal vacuum connection the bath was filled with anhydrous alcohol. Studies were made on several construction steels (20Kh, 40Kh, 50Kh, and ShKh15); steels 40Kh, 50Kh, and ShKh15 were quenched from 840-860 0 C in oil and then tempered at 200 0 C (2 h), steel 20Kh was studied in the as-received state. It was shown that with increase in the carbon content of steel with a martensite structure, the decrease in strength in the presence of anhydrous alcohol was greater than in dry air. Experiments showed that anhydrous alcohol causes an adsorption decrease in the strength both of samples with preliminarily formed cracks and V-shaped stress concentrators and of smooth samples. The greatest adsorption effect of alcohols in our case, as in static fatigue, was observed in samples with cracks. A dependence was shown between the length of the carbon chain and the fatigue limit. This dependence indicates the monotone nature of the decrease in the fatigue limit with transfer from methyl to butyl and then to octyl alcohol

Corrosion behavior of austenitic steels and their components in niobium-containing chloride melts

Science.gov (United States)

Abramov, A. V.; Polovov, I. B.; Rebrin, O. I.; Volkovich, V. A.; Lisienko, D. G.

2014-02-01

The mechanism of corrosion of austenitic steels 12Kh18N10T, 10Kh17N13M2T, and 03Kh17N14M3 and metals Cr, Fe, Ni, and Mo in a NaCl-KCl-NbCl n ( n = 3.5, Nb content is 5 ± 0.1 wt %) melt at 750°C is studied. The metal and steel corrosion rates under these conditions are determined. The character of material fracture and the mechanisms of material corrosion are found.

Corrosion of austenitic steels and their components in vanadium-containing chloride melts

Science.gov (United States)

Abramov, A. V.; Polovov, I. B.; Rebrin, O. I.; Lisienko, D. G.

2014-08-01

The corrosion of austenitic 12Kh18N10T, 10Kh17N13M2T, and 03Kh17N14M3 steels and their components (Cr, Fe, Ni, Mo) in NaCl-KCl-VCl2 melts with 5 wt % V at 750°C is studied. The rates and mechanisms of corrosion of the materials under these conditions are determined. The processes that occur during contact of the metals and steels with vanadium-containing chloride electrolytes are investigated.

Damping capacity of unstable steels on chromium-nickel-manganese base

Energy Technology Data Exchange (ETDEWEB)

Kochkin, L.I.; Rudakov, A.A. (Kirovskij Politekhnicheskij Inst. (USSR))

1982-02-01

The paper deals with results of a study on the energy scattering in OKh13N3G8, 20Kh13N3G4 and 30Kh13N3G4 unstable steels. It is shown that the development of microplastic strains most easily occurs in low-carbon steel having a two-phase structure in the initial state. The proceeding of microplastic deformations in carbon unstable steels is limited by the interstitial atom effect on the dislocation movement. It is established that in OKh13N3G8 steel the martensite ..cap alpha --> gamma..- transformation begins under the cyclic stress amplitudes below the yield point of this steel. The steels studied possess a high vibrostrength.

Effect of heat treatment and rotor steels composition on hydrogen solubility

International Nuclear Information System (INIS)

Ivanov, A.I.; Samojlenko, L.V.; Gorovaya, O.N.; Najdovskij, A.G.; Bilik, I.; Kret, Ya.

1988-01-01

Measurements of equilibrium hydrogen adsorption in samples of 27KhN3MFA and 25Kh2NMFA steels were conducted. Carbide inclusions and doping additions, typical for rotor steels, don't produce noticeable effect on hydrogen solubility in

Investigation of intergranular corrosion resistance of Cr16Ni25NMo6 steel

International Nuclear Information System (INIS)

Kamenev, Yu.B.; Nazarov, A.A.; Kuusk, L.V.; Majdeburova, T.F.

1990-01-01

The effect of 08Kh16N25AM6 steel susceptibility to intergranular corrosion on its intergranular cracking resistance in high-temperature water is investigated. In addition, the performed tests point to the susceptibility of sensibilized Kh16N25AM6 steel to intergranular corrosion in media simulating an agressive environment of power generation equipment; the latter requires a strict control over the resistance of weld joints of the above steel to intergranular corrosion. It is shown that Kh16N25AM6 type steel in sensibilized state is susceptible to intercrystalline corrosion cracking in high-temperature water which correlates with its susceptibility to intergranular corrosion established by AM GOST 6032-84 and potentiodynamic reactivation methods

Investigation of 12Kh1MF steel resistance to brittle fractures

International Nuclear Information System (INIS)

Bologov, G.A.; Rushchits, T.Yu.

1977-01-01

The metal of hot-rolled steam pipe made of 12Kh1MF steel, which has been subjected to thermal treatment under laboratory conditions, and metal samples from acting steam pipes after different exploitation periods at 510-565 deg C have been investigated. The dependence of impact viscosity and its constituents on conditions of thermal treatment has been established. The energy consumed by the developing crack has been used as an impact viscosity criterion. Appropriate thermal treatment is capable of rehabilitating the impact viscosity of embrittled metal. Cold plastic deformation increases crack propagation rate in the initial metal and promotes embrittlement during exploitation. Ageing of the working metal reduces its capacity of stopping the developing crack and shifts the temperature threshold of brittleness towards positive temperature

Influence of chemical heterogeneity of solid solutions on brittleness in chromium steels

International Nuclear Information System (INIS)

Madyanov, S.A.; Sedov, V.K.; Apaev, B.A.

1985-01-01

The role of chemical heterogeneity of solid solutions in formation of mechanical properties of Kh09, Kh15, Kh20, Kh19N2G5T chromium steels has been investigated. It is established that besides the known regioA of chemical heterogeneity in the vicinity of 475 deg C exists a high-temperature region (1000-1050 deg C), where maximum heteroge=- neity of chromium distribution in solid solution, is observed. Both types of chemical heterogeneity cause essential hardening of alloys, which becomes apparent in abrupt change of capability to microplastic deformation The mechanism of occurrence of the given temper brittleness consists in carbon diffusion into microvolunes enriched in carbide-forming elements

Mechanical and fracture properties at impact loading of selected steels for nuclear power engineering

International Nuclear Information System (INIS)

Buchar, J.; Bilek, Z.

1988-01-01

The possibilities are briefly characterized of experimental research of mechanical and fracture properties of steels used in nuclear power engineering. Attention is paid to plastic deformation and the assessment of fracture formation during impact loading. The results are reported for steels 15Kh2MFA and 10GN2MFA. For steel 15Kh2MFA the effect was also studied of neutron radiation at different temperatures. From the theory developed for non-irradiated material 10GN2MFA, a prediction is made within the original model of the fracture stress value for steel 15Kh2MFA in both non-irradiated and irradiated states. The conclusion is arrived at that the existing methods of assessing steel properties at impact load allow obtaining knowledge of all significant effects during actual stress, this using only small specimens of the materials. (Z.M.). 4 figs., 8 refs

Damping capacity of unstable steels on chromium-nickel-manganese base

International Nuclear Information System (INIS)

Kochkin, L.I.; Rudakov, A.A.

1982-01-01

The paper deals with results of a study on the energy scattering in OKh13N3G8, 20Kh13N3G4 and 30Kh13N3G4 unstable steels. It is shown that the development of microplastic strains most easily occurs in low-carbon steel having a two-phase structure in the initial state. The proceeding of microplastic deformations in carbon unstable steels is limited by the interstitial atom effect on the dislocation movement. It is established that in OKh13N3G8 steel the martensite α→γ- transformation begins under the cyclic stress amplitudes below the yield point of this steel. The steels studied possess a high vibrostrength [ru

Nitrogen effect on the tendency of Cr-Ni-MN steels to delayed fracture under stress and hydrogen effects

International Nuclear Information System (INIS)

Suvorova, S.O.; Fillipov, G.A.

1996-01-01

Austenitic steels types 03Kh17N16G10AM5, 03Kh6N12G10AM5 and 07Kh13AG20 with various nitrogen contents were studied for their tendency to delayed fracture using mechanical tests, fractography and X ray diffraction analysis. The steel type 07Kh13G20 exhibited the highest strength in the initial state but showed an increase tendency to delayed fracture after hydrogenation. It is underlined that nitrogen additions essentially intensify the tendency of cold worked steels to delayed fracture. This fact should be taken into account when using nitrogen-containing Cr-Ni-Mn steels under severe operational conditions. 4 refs., 2 tabs

Yuánmíng Yuán en el siglo XVIII: Arte entre la diplomacia y la filosofía; entre Europa y Pekín

Directory of Open Access Journals (Sweden)

Pedro Luengo

2016-01-01

Full Text Available Este estudio pretende probar que el Yuánmíng Yuán fue diseñado como una representación del macrocosmos imperial a partir de la filosofía de la China de Qianlong. Para ello se valorará la función simbólica de los palacios de estilo europeo a partir de las descripciones de embajadas orientales y occidentales. Esta información se pondrá en relación con las diferentes representaciones pictóricas del jardín, conservadas tanto en grabados o acuarelas como en pinturas murales. A partir de toda esta información se pretende valorar su utilización en las visitas de diferentes legados diplomáticos extranjeros. En concreto, se intenta comprobar que los palacios europeos se utilizaron eminentemente para impresionar a las misiones orientales, y no tanto a las occidentales.

The effect of laser treatment on the wear resistance of steel in corrosive media

International Nuclear Information System (INIS)

Plyatsko, G.V.; Porter, A.I.; Prejs, G.A.; Mojsa, M.I.

1975-01-01

The corrosion mechanical wearing properties of steel 45 treated with a laser beam (H 100 =7800 Mn/sq.m) under friction with nitrated steel 40KhNMA (HV=7000 Mn/sq.m), chrome cast iron Kh15M (hardened and low-temperature tempered, modified), perlite cast iron and bronze are studied. The aqueous buffers with pH=6 and 11 are used as a corrosion active media. In a weakly acid medium the most intensive wearing of steel 40KhNMA is observed at P=8 Mn/sq.m. Its wearing reduces due to increase of pressure to 12 Mn/sq.m. Extent of steel 45 wearing increases with pressure increase from 8 to 12 Mn/sg.m. Friction coefficient of this pair changes by jumps at an increase of normal pressure and its variation range is smaller than that observed in an alkaline medium. The maximum value of friction coefficient is shifted to the higher pressure. The wearing of cast iron Kh15M-steel 45 pair has an alternative pattern. In an alkaline medium the cast iron wearing intensity shows a linear increase with the normal contact pressure but that of the steel changes jumpwise attaining extreme at 8 and 12 Mn/sq.m. In a weak acid medium the intensity of grasping and graphitization at the friction surface of cast iron Kh15M-steel 45 pair is higher than that in the alkaline medium. Experiments demonstrate an effectiveness of the laser beam treatment of steel 45 for its friction in the alkaline medium with nitrated steel 40KhNMA and with hardened low-temperature tempered cast iron 45 under friction contact pressure as high as 8 Mn/sq.m, and in acid medium at 12 and 8 Mn/sq.m respectively. The laser treatment provides high corrosion-mechanical stability of steel 45 and the counterbodies described, as well as the low friction coefficient of these pairs

Structural changes IN THE Kh20N45M4B nickel alloys and THE Kh16N15M3B steel due to helium ion bombardment

International Nuclear Information System (INIS)

Kalin, B.A.; Chernikov, U.N.; Chernov, I.I.; Kozhevnikov, O.A.; Shishkin, G.N.; Yakushin, V.L.

1986-01-01

Using transmission electron microscopy, x-ray structural analysis, and the thermal desorption techniques, the authors carried out a detailed study of the structural and phase changes, defect formation, and helium accumulation in the He + -bombarded 16-15 austenitic steels and 20-45 nickel alloys. Microstructure of the bombarded specimens was studied using the methods of transmission electron microscopy of thin foils in the EVM-100, and EM-301G electron microscopes. Results of x-ray studies on the bombarded specimens are presented. The conducted studies show that bombardment of structural materials with light ions can lead to significant structural damages and changes in the chemical and phase composition of the surface layer. The possible mechanisms of the changes in the chemical and phase composition include selective sputtering and radiation-induced accelerated diffusion of elements in the field of internal lateral stresses developing during the He + implantation process

Welding wires for high-tensile steels

International Nuclear Information System (INIS)

Laz'ko, V.E.; Starova, L.L.; Koval'chuk, V.G.; Maksimovich, T.L.; Labzina, I.E.; Yadrov, V.M.

1993-01-01

Strength of welded joints in arc welding of high-tensile steels of mean and high thickness by welding wires is equal to approximately 1300 MPa in thermohardened state and approximately 600 MPa without heat treatment. Sv-15Kh2NMTsRA-VI (EhK44-VI) -Sv-30Kh2NMTsRA-VI (EkK47-VI) welding wires are suggested for welding of medium-carbon alloyed steels. These wires provide monotonous growth of ultimate strength of weld metal in 1250-1900 MPa range with increase of C content in heat-treated state

The permeation behavior of deuterium through 1Cr18Ni9Ti stainless steel with TiN+TiC-TiN multiple films

International Nuclear Information System (INIS)

Xiong, Y.; Song, J.; Luo, D.; Lei, Q.; Chen, C.

2015-01-01

The prevention of tritium losses via permeation through structure components is an important issue in fusion technology. The production of thin layers on materials with low diffusivity and/or low surface recombination constants (so-called permeation barriers) seems to be the most practical method to reduce or hinder the permeation of tritium through materials. TiN+TiC+TiN multiple films are deposited on the surface of 1Cr18Ni9Ti stainless steel by ion-beam assisted deposition technology. The characteristics of films are tested by XPS ASEM and XRD, which shows that the film are compact and uniform with a thickness of about 15 μm, and have a good adherence with the substrate below 773 K. The diffraction peaks in the XRD patterns for TiC and TiN are broadened, implying that the multiple films are deposited on the surface of 1Cr18Ni9Ti stainless steel. Meanwhile, the C-H bonded CH 4 -appears in the infrared spectra of multiple films, suggesting that the CH 4 - is in a static state, so hydrogen atom cannot migrate from the site bonded with carbon to a neighboring site. The measured deuterium permeability in 1Cr18Ni9Ti stainless steel coated with multiple films is 2-3 orders of magnitude lower than that of pure 1Cr18Ni9Ti stainless steel substrate from 473 K to 773 K. However, this barrier is partly destroyed above 773 K

Boron effect on fabrication properties and service behaviour of complex corrosion-resistant steels

International Nuclear Information System (INIS)

Gol'dshtejn, Ya.E.; Piskunova, A.I.; Shmatko, M.N.

1978-01-01

In order to determine the optimum boron admixtures for the improvement of the technological plasticity without the considerable reduction in the corrosion resistance of the complex alloy Cr-Ni-Mo steels, industrial heats of the 03KH16N15M3, 03KH17N14M3 and other steels, containing 0.0005-0.003% boron, have been researched. The plasticity, corrosion resistance and microstructure of certain steels have been determined. It is shown that small additions of boron enhance the technological plasticity during the ingot rolling. In order to prevent a sharp reduction in the corrosion resistance, the boron content should be confined to 0.0015% and the quenching temperature raised to 1,120-1,150 deg C. The positive effect of the quenching temperature increase is accounted for by the solution of the excess phases and by the reduction of the dislocation density in the near-the-boundary zones

Pipes out of the chromium-molybdenum 12Kh2M1 steel intended for power units

International Nuclear Information System (INIS)

Saf'yanov, A.V.; Plyatskovskij, O.A.; Khokhlov-Nekrasov, O.G.; Palatnikova, E.S.; Karpenko, N.P.

1977-01-01

Vanadiumless steel 12Kh2M1 (2.25%Cr, 1%Mo) known to be applied abroad has been used for production of 325x60 mm tubes. The technology involves heating of the blanks to 1270-1300 deg C, their piercing in a double-roller mill, rolling on a pilger mill 8-16'' in thick wall caliber rolls, thermal treatment (normalizing at 930-960 deg C for 1 hour and tempering at 730+-10 deg C for 4 hours and etching (12-22% H 2 SO 4 and up to 143 g/l FeSO 4 ) for 3-4 hours at 55-65 deg C. Good technological properties of the steel and its capacity of working at 540-580 deg C are confirmed. Vanadium alloying of boiler steels does not provide for essential improvement of oxydation resistance and long term strength, but decreases the workability and enhances scatter of working parameters on account of minor variations of chemical composition

Chemical heat treatment of low alloyed maraging steels

Energy Technology Data Exchange (ETDEWEB)

Malinov, L S; Korotich, I K [Zhdanovskij Metallurgicheskij Inst. (Ukrainian SSR)

1979-09-01

The investigation concerned the nitriding, cementation, chromizing, borating of economically alloyed maraging grade 04Kh2N5MFYu steel. The investigated methods of chemothermal treatment were found to considerably increase the hardness of the surface layer of the maraging steel. The high tempering of the grade 04Kh2N5MFYu cemented and hardened steel was found to produce secondary hardening. On chromizing, the diffusion layer is an alloyed ferrite which strengthens because of the dispersion hardening on ageing. The formation of the plastic low-carbon martensite at relatively small cooling rates greatly decreases the tendency of the boride layer to cracking.

LOCATING THE TRAILING EDGE OF THE CIRCUMBINARY RING IN THE KH 15D SYSTEM

International Nuclear Information System (INIS)

Capelo, Holly L.; Herbst, William; Leggett, S. K.; Hamilton, Catrina M.; Johnson, John A.

2012-01-01

Following two years of complete occultation of both stars in the binary T Tauri star KH 15D by its opaque circumbinary ring, KH 15D has abruptly brightened again during apastron phases, reaching I = 15 mag. Here, we show that the brightening is accompanied by a change in spectral class from K6/K7 (the spectral class of star A) to ∼K1, and a bluing of the system in V – I by about 0.3 mag. A radial velocity measurement confirms that, at apastron, we are now seeing direct light from star B, which is more luminous and of earlier spectral class than star A. Evidently, the trailing edge of the occulting screen has just become tangent to one anse of star B's projected orbit. This confirms a prediction of the precession models, supports the view that the tilted ring is self-gravitating, and ushers in a new era of the system's evolution that should be accompanied by the same kind of dramatic phenomena observed from 1995 to 2009. It also promotes KH 15D from a single-lined to a double-lined eclipsing binary, greatly enhancing its value for testing pre-main-sequence models. The results of our study strengthen the case for truncation of the outer ring at around 4 AU by a sub-stellar object such as an extremely young giant planet. The system is currently at an optimal configuration for detecting the putative planet and we urge expedient follow-up observations.

Analytical description of changes in the magnetic states of chromium-nickel steel under uniaxial elastic deformation

Science.gov (United States)

Gorkunov, E. S.; Yakushenko, E. I.; Zadvorkin, S. M.; Mushnikov, A. N.

2017-12-01

Dependences of magnetization and magnetic permeability of the 15KhN4D structural steel on the value of uniaxial stresses and magnetic field strength are obtained. A polynomial approximation fairly accurately describing the observed changes is proposed on the basis of experimental data.

Chromium surface alloying of structural steels during laser treatment

International Nuclear Information System (INIS)

Kurov, I.E.; Nagornykh, S.N.; Sivukhin, G.A.; Solenov, S.V.

1987-01-01

Results of matrix alloying from the surface layer and creation of considerably increased chromium concentration in the depth which permits to increase the efficiency of laser treatment of steels (12Kh18N10T and 38KhN3M) in the process of their further mechanical polishing, are presented. The treatment was realized by continuous CO 2 -laser at different power densities and scanning rates are presented. A model describing the creation of anomalous distributions of the alloying element in steels is plotted

Low-temperature nitriding of austenitic steel in a vibrofluidized bed

Science.gov (United States)

Baraz, V. R.; Grachev, S. V.

1999-11-01

The prospects for use of a vibrofluidized bed (VFB) for low-temperature nitrogen saturation of high-strength austenitic steel based on Cr-Ni-Mn (12Kh17N8G2S2MF) are considered. The positive effect of preliminary plastic deformation on the intensity of nitriding is described. The temperature and time parameters of nitriding in a VFB for strain-aging austenitic steel 12Kh17N8G2S2MF are shown to be adequate for the regimes of the final heat-treatment operation of aging. This creates the possibility of combining the operations of surface alloying and strain aging into a single cycle. This combined treatment increases substantially the resistance of the steel to cyclic loads while preserving the strength parameters. It is shown that the presented method of low-temperature nitriding in a VFB is expedient for improving the service characteristics of austenitic steel 12Kh17N8G2S2MF used for production of force springs of automobile brake systems.

Hot working effect on austenite transformations in structural steel in continuous cooling

International Nuclear Information System (INIS)

Zajmovskij, V.A.; Kisteh, N.V.; Samedov, O.V.

1979-01-01

Austenite transformations in 40, 40Kh, 40KhN and 40KhNMA steels under hot working at 900 deg C with 20% reduction degree and continuous cooling with 1,7-16 0 /s are investigated. Changing of cooling rate in various ways affects the temperature range of austenite transformation in pearlite and bainite regions. Regulating the cooling rate after hot working one can essentially change the impact strength and steel ductility as a result of high temperature thermomechanical treatment effect

Parametrical limits of SCC-susceptibility of austenitic and austenitic-ferritic Cr-Ni steels

International Nuclear Information System (INIS)

Starosvetskij, D.I.; Baru, R.L.; Bondarenko, A.I.; Bogoyavlenskij, V.L.; Timonin, V.A.

1990-01-01

Comparative investigations into corrosion cracking (CC) of austenitic (12Kh18N10T) and austenitic-ferritic (08Kh22N6T) chromium-nickel steels are performed for various chloride media in a wide range of chloride concentrations and temperatures. It is shown that the ratio between steels in terms of their CC-susceptibility is not definite and can undergo a reversal depending on parameters of medium, level and conditions of loading. Differences in mechanisms of corrosion cracking of austenitic and austenitic-ferritic steels are established

Plasticity of low carbon stainless steels

International Nuclear Information System (INIS)

Bulat, S.I.; Fel'dgandler, Eh.G.; Kareva, E.N.

1975-01-01

In the temperature range 800-1200 0 C and with strain rates of from 10 -3 to 3 s -1 , austenitic (000Kh18N12) and austenitic-ferrite (000Kh26N6) very low carbon stainless steels containing 0.02-0.03% C exhibit no higher resilience than corresponding ordinary steels containing 0.10-0.12% C. However, the plasticity of such steels (particularly two-phase steels) at 900-1100 0 C is appreciably inferior owing to the development of intergranular brittle fracture. Pressure treatment preceded by partial cooling of the surface to 850 0 C yields rolled and forged products with acceptable indices but is inconvenient technically. At the Zlatoustovsk and Ashin metallurgical plants successful tests have been performed involving the forging and rolling of such steels heated to 1280-1300 0 C without partial cooling; it was necessary to improve the killing conditions, correct the chemical composition (increasing the proportion of ferrite) and take measures against heat loss. (author)

Optimal control of conditions of deformation during rolling the bar alloy from alloy steel

International Nuclear Information System (INIS)

Inatovich, Yu.V.; Shilov, V.A.; Shvarts, D.L.; Kudelin, S.P.

2001-01-01

A complex of programs for determining the optimal gaps between rollers during rolling of simple merchant sections of alloy steels of a wide brand assortment (12KhN3A, Kh17N2, Kh18N10T) was elaborated. Experience in calculations made according to the programs suggests advisability of their use in the automated design systems for roller calibration and for adjustment of section mills [ru

Close toleranoe forging of chromium steel blades for powerful steam turbines

International Nuclear Information System (INIS)

Shastin, Eh.G.; Kositskij, Yu.N.; Lyubchits, G.A.

1989-01-01

Work on simulating technological process on die-forging hammer was performed in order to reduce the preparation period bringing technology of close tolerance forging of turbine blades to a commercial level. A special attention was paid to development of accurate forming of forgings of 20Kh13Sh, 12Kh13 and 15Kh11MFSh steels on screw presses with nominal effort equal to 80 and 144 MN

Effect of heat treatment regime on structural lamination in ferritic-austenitic steels

International Nuclear Information System (INIS)

Sizov, R.A.; Zakharova, M.I.; Novikov, I.I.; Bannykh, O.A.

1983-01-01

The effect of preliminary thermal treatment on lamination and viscosity of EhP-53 and KO-3 steels after durable aging at the temperature of 350 is studied. It is shown that preliminary heat treatment considerably affects lamination processes in the result of aging of 0Kh18G8N2T steel. The lowest rate of lamination and higher impact strength after aging at 350 deg C for 4500 hours corresponds to the following heat treatment: 10 hour aging at 650 deg C with cooling in the air, then quenching in water from 950 deg C after aging for 30 min and the following tempering (650 deg C, 5 hours). Unlike the 0Kh18G8N2T steel, lamination parameters of steel 0Kh22N6T practically do not change after the application of heat treatment. Nevertherless, taking into account results of impact strength, it is advisable to have thermal treatment according to the regime: quenching in water at 950 deg C after aging for 30 min

Tendency of the 18-8 type corrosion-resistant steel to cracking in automatic building-up of copper and copper base alloys in argon

International Nuclear Information System (INIS)

Abramovich, V.R.; Andronik, V.A.

1978-01-01

Studied was the tendency of the 18-8 type corrosion-resistant steel to cracking during automatic building-up of copper and bronze in argon. The investigation was carried out on the 0kh18n10t steel in argon. It had been established, that the degree of copper penetration into the steel inceases with the increase in the time of the 0Kh18n10t steel contact with liquid copper. Liquid copper and copper base alloys have a detrimental effect on mechanical properties of the steel under external tensile load during intercontant. It is shown that in building-up of copper base alloys on the steel-0Kh18n10t, tendency of the steel to cracking decreases with increase in stiffness of a surfaced weld metal plate and with decrease in building-up energy per unit length. The causes of macrocracking in steel at building-up non-ferrous metals are explained. The technological procedures to avoid cracking are suggested

Wear resistance and structural changes in nitrogen-containing high-chromium martensitic steels under conditions of abrasive wear and sliding friction

International Nuclear Information System (INIS)

Makarov, A.V.; Korshunov, L.G.; Schastlivtsev, V.M.; Chernenko, N.L.

1998-01-01

Martensitic nitrogen-containing steels Kh17N2A0.14, Kh13A0.14, Kh14G4A0.22 as well as steel 20Kh13 were studied for their wear resistance under conditions of friction and abrasion. Metallography, X ray diffraction analysis and electron microscopy were used to investigate the structural changes taking place in a thin surface layer on wearing. It is shown that an increase of nitrogen content of 0.14 to 0.22% promotes an enhancement of steel resistance to abrasive and adhesive wear, especially after tempering in the range of 500-550 deg C. Typically, the nitrogen-containing steels exhibit lower resistance to various types of wear in comparison with the steels with high-carbon martensite due to their lower deformability under conditions of friction loading

Electroplastic drawing of stainless steels

International Nuclear Information System (INIS)

Troitskij, O.A.; Spitsyn, V.I.; Sokolov, N.V.; Ryzhkov, V.G.

1977-01-01

Effect of electroplastic drawing on mechanical, magnetic and electrical properties of wire of 12Kh18N10T and Kh13N13M2 steels was studied. Pulse, direct and alternating currents were used. Direct and alternating current densities were 400 A/mm 2 , mean density of pulse current was 200 A/mm 2 . The investigations have shown that the current density increase results in decreasing the wire strengthening intensity though in increasing plastic properties. As a result of electroplastic drawing the growth of magnetic characteristics of wire occurs

Corrosion of chromium, nickel, titanium and steels in solutions of sodium and ammonium thiosulfates

International Nuclear Information System (INIS)

Grebenshchikova, S.V.; Kochergin, V.P.; Doronina, I.V.

1983-01-01

Results of gravimetric determinatiion of average rate of chromium, nickel, titatnium and steels 12Kh18N10T and VSt.3 corrosion rate in solutions 50 mass.% (NH 4 ) 2 S 2 O 3 and Na 2 S 2 O 3 in the air and nitrogen atmosphere at 333 K have been generalized. Anodic polarization curves are recorded and stationary potentials of metals and steels under the conditions are measured. It is shown that in (NH 4 ) 2 S 2 O 3 solution the rate of metal and steels corrosion is higher than in Na 2 S 2 O 3 solution indepenent of the nature of gaseous medium contacting with solution. In the series Ni → VSt.3 → 12Kh18N10T → VT1 → chromium in (NH 4 ) 2 S 2 O 3 and Na 2 S 2 O 3 solutions at 333 K corrosion resistance increases. Chromium, titanium and chromium-nickel steel 12Kh18N10T possess a high corrosion resistance

Determination of constant of chemical reaction rate in the process of steel treatment in the endothermal atmosphere

International Nuclear Information System (INIS)

Gyulikhandanov, E.L.; Kislenkov, V.V.

1978-01-01

The high-temperature method was applied to measuring a relative variation in the electrical resistance of a thin steel foil prepared from the 12KhN3A, 18Kh2N4VA, 20KhGNR, and 20Kh3MVF steels during its carburization and decarburization, and determined was the temperature dependence of the reaction rate of the interaction of the endothermal atmosphere of different compositions with the analloyed γ-Fe. A connection has been established between the reaction rate constant and the thermodynamic activity of carbon in the alloyed austenite at the temperature of about 925 deg C, corresponding to the cementation temperature. This provides the quantitative estimation of the above value for any alloyed steels and with the presence of numerical values of diffusion coefficients; this also enables one to carry out an accurate calculation of the distribution of carbon throughout the depth of a layer when effecting the cementation in the endothermal atmosphere

Investigation of thermal fatigue of chromium-molybdenum steels, used for calcining and agglomeration constructions

International Nuclear Information System (INIS)

Sinyavskij, D.P.; Gorkalo, A.P.

1979-01-01

The technique for investigating thermal fatigue of materials is described. The data on sample stress deformed state and current temperature values are taken from the local volume of the material studied. Results of investigating thermal fatigue of the 15KhMl and 20KhMl steels are presented

Investigation programme and procedure for creep and long-term rupture strength in materials with accounting for stress deviator and loading history

International Nuclear Information System (INIS)

Mozharovskaya, T.N.

1984-01-01

A programme and procedure are given to study 08Kh18N9 steel at 600 deg C and 15Kh2MFA steel at 550 deg C for creep and long-term strength at different parameters of proportional loading as well as at different parameters under loading in two-link irregular trajectories. This makes it possible to estimate the effect of the kind of a stress deviator, history and prehistory of loading on plastic deformation in creep and on failure under long-term loading

Investigation programme and procedure for creep and long-term rupture strength in materials with accounting for stress deviator and loading history

Energy Technology Data Exchange (ETDEWEB)

Mozharovskaya, T N [AN Ukrainskoj SSR, Kiev. Inst. Problem Prochnosti

1984-11-01

A programme and procedure are given to study 08Kh18N9 steel at 600 deg C and 15Kh2MFA steel at 550 deg C for creep and long-term strength at different parameters of proportional loading as well as at different parameters under loading in two-link irregular trajectories. This makes it possible to estimate the effect of the kind of a stress deviator, history and prehistory of loading on plastic deformation in creep and on failure under long-term loading.

Effect of helium ion bombardment on hydrogen behaviour in stainless steel

International Nuclear Information System (INIS)

Guseva, M.I.; Stolyarova, V.G.; Gorbatov, E.A.

1987-01-01

The effect of helium ion bombardment on hydrogen behaviour in 12Kh18N10T stainless steel is investigated. Helium and hydrogen ion bombardment was conducted in the ILU-3 ion accelerator; the fluence and energy made up 10 16 -5x10 17 cm -2 , 30 keV and 10 16 -5x10 18 cm -2 , 10 keV respectively. The method of recoil nuclei was used for determination of helium and hydrogen content. Successive implantation of helium and hydrogen ions into 12Kh18N10T stainless steel results in hydrogen capture by defects formed by helium ions

Experimental verification of the statistical theories of scaling factor effect in fatigue fracture of steel

International Nuclear Information System (INIS)

Svistun, R.P.; Babej, Yu.I.; Tkachenko, N.N.

1976-01-01

Statistical theories of the scale effect in the fatigue failure of 40KH18N9T, 10 and 20 steels have been verified. The theories are shown to be not invariably suitable for a satisfactory exlanation of the fatigue strength of the samples with respect to their dimensions. One of the main reasons for displaying the scale effect in the process of steel fatigue is the sample self-heating, i.e. a temperature factor which in many cases overlaps a statistical one

Experimental verification of the statistical theories of scaling factor effect in fatigue fracture of steel

Energy Technology Data Exchange (ETDEWEB)

Svistun, R P; Babei, Yu I; Tkachenko, N N [AN Ukrainskoj SSR, Lvov. Fiziko-Mekhanicheskij Inst.; L' vovskij Lesotekhnicheskij Inst. (Ukrainian SSR))

1976-01-01

Statistical theories of the scale effect in the fatigue failure of 40KH18N9T, 10 and 20 steels have been verified. The theories are shown to be not invariably suitable for a satisfactory exlanation of the fatigue strength of the samples with respect to their dimensions. One of the main reasons for displaying the scale effect in the process of steel fatigue is the sample self-heating, i.e. a temperature factor which in many cases overlaps a statistical one.

KH in Paraffin - KH(P): A Useful Base for Organic Synthesis

Science.gov (United States)

Taber, Douglass F.; Nelson, Christopher G.

2011-01-01

The preparation of KH as a one:one homogenate with paraffin, termed KH(P), is reported. KH(P), a solid at room temperature, is stable without special handling. On suspension in THF with a phosphonium salt, KH(P) rapidly generates the ylide. Wittig condensation with aromatic, aliphatic and α, β-unsaturated aldehydes proceeds with high Z-selectivity. KH(P) should be a generally useful base for organic synthesis. PMID:17081034

Quality of the KhN73MBTYu alloy after electroslag remelting and vacuum arc remelting

International Nuclear Information System (INIS)

Shelgaeva, A.V.; Krichevets, M.I.; Shinkina, N.S.; Komissarov, A.I.

1978-01-01

The structure and properties of the heat-resisting KhN73MBTYu alloy are investigated after electroslag remelting (ESR) and vacuum arc (VAR) remelting in commercial furnaces. The complex investigations of the casted metal were carried out by modern methods along with the standard acceptance tests, and a number of service properties were determined. It is established that the ESR metal contains magnesium and has the reduced sulphur concentration; the alloy has more fine-grained structure at high isotropy of the properties at room and operating temperatures; higher endurance is achieved under reversal rotational bending; no laminated fractures are observed. According to the basic quality factors the ESR metal satisfies all requirements for the VAR metal. Due to exclusion of strippling of ESR electrodes and ingots the yield of steel forgings increases by 20-25% and the prime cost decreases in comparison with the industrial production of VAR metal

Z-phase in 9-12% Cr Steels

DEFF Research Database (Denmark)

Danielsen, Hilmar; Hald, John

2004-01-01

The complex nitride Z-phase, Cr(V,Nb)N, has recently been identified as a major cause for premature breakdown in creep strength of a number of new 9-12%Cr martensitic steels. A thermodynamic model of the Z-phase has been created based on the Thermo-Calc software. The model predicts the Z-phase to......The complex nitride Z-phase, Cr(V,Nb)N, has recently been identified as a major cause for premature breakdown in creep strength of a number of new 9-12%Cr martensitic steels. A thermodynamic model of the Z-phase has been created based on the Thermo-Calc software. The model predicts the Z......-phase to be stable in all of the new 9-12%Cr martensitic steels. This has generally been confirmed by the performed experiments. Z-phase precipitation seems to be a kinetic problem, and drivning force calculations using Thermo-Calc with the developed model have been used to predict steel compositions, which...

Development of production technology and investigation of quality for forged-welded turbine rotors of steel 25Kh2NVFA

International Nuclear Information System (INIS)

Borisov, I.A.; Merinov, G.N.; Slezkina, E.V.

1997-01-01

A study was made into mechanical properties and microstructure of turbine rotor components manufactured by forging and heat treated under various conditions. It is revealed that the optimal heat treatment of forgings must include double quenching with subsequent tempering at 630-640 deg C for 10-20 h. Forged and welded rotors should be tempered at 620-630 deg C for 50-100 h. Microscopic examination and mechanical tests showed that low alloy steel 25Kh2NMF can be successfully used for manufacturing rotors of high-, medium-and low-heat turbines

Electron beam welding of flanges with tubular shafts of steel 40KhNMA

International Nuclear Information System (INIS)

Leskov, G.I.; Zhivaga, L.I.; Shipitsyn, B.N.; Savichev, R.V.

1975-01-01

The results are presented of elaborating the technological process for the electron beam welding of flanges with a tube of the 40KhNMA steel and of investigation into the quality of the welded joints. A welded piece has been fabricated conforming to the technology suggested observing the parameters worked-out in the following sequence: assembling the piece; pre-welding of the edges in some points; welding; high tempering; welds quality control; removal of the seam reinforcement inside of the tube and the weld root to the depth of 2 mm; quenching; tempering; welds quality control; finishing. The welds quality control consists in visual inspection, ultrasonic testing, magnetic flaw detection, as well as X-ray and metallographic analyses. The mechanical properties are studied on notched samples cut out of the welded joints. The test results have shown that the mechanical properties of the welded joints meet the requirements on the same level with the base metal

Long-term Stability of 9- to 12 % Cr Steels

DEFF Research Database (Denmark)

Hald, John

2004-01-01

In the recent 25 years creep rupture strength of 9- to 12 %Cr steels for steam pipes and turbines has been doubled by development of new alloys. This development has formed a basis for improved efficiency of fossil fired steam power plants by introduction of advanced steam temperatures...... and pressures. Newly developed steam pipe steels are based on modifications of well-established steels like the X 20CrMoV12 1. Balanced addition of V, Nb and N to a 9Cr 1 Mo steel led to the Modified 9 Cr steel P 91. Addition of 1% W to a 9Cr 1 MoVNbN base composition led to steel E 911 and partial replacement...... of Mo with 1.8 % W combined with a slight amount of Boron led to steel P 92. The creep rupture strength of these new alloys are now secured with long-term tests up to 100,000 hours, which demonstrate improvements of 50% (P 91), 75 % (E 911) and 100 % (P 92) in strength compared to X 20CrMoV12 1....

Development and industrial mastering hot rolling procedure for low-ductile steels and alloys

International Nuclear Information System (INIS)

Degterenko, V.K.; Sokolov, V.A.

1980-01-01

The technique for the development of the sheet hot rolling procedure for low-ductile steels and alloys (0Kh17N14M2, 12Kh21N5T, 20Kh25N20C2,40Kh13, 36NKhTYu etc.) is proposed, using plastometer which permits to obtain the data on the deformation resistance in the wide range of temperatures (800-1300 deg C), of deformation degrees (0.1-0.3) and deformation rates (0.001-300 c -1 ). With the help of the plastometric data processed on the computer the calculation of the rolling regimes for the sheet with improved surface quality is carried out at the more uniform loading on the mill stands

On effect of some thermodeformation parameters of welding cycle on tendency of pearlitic heat-resisting steels to fracture in reheating

International Nuclear Information System (INIS)

Prokhorov, N.N.; Bardokin, E.V.

1979-01-01

Studied is the inclination of the 12Kh1MF, 15Kh3M1F and N18K9M5T steels subject to thermodeformation cycle imitating a welding one, to fracture in reheating. A hot-rolled metal then subject to the same thermal treatment was used. The imitation of thermodeformation cycle of the welding permitted to vary maximum heating temperatures, the period during which the metal is kept at temperatures higher than 1100 deg C, and the cooling rate of ajacent zone metal. It is shown that the curve of the dependence of deformation ability and the tendency to fracture at the reheating of adjacent zone metal on the rate of its cooling at welding is U-shaped. Deformation ability has its maximum value at the cooling rate of 30 deg c/s in the range 1300 to 1000 deg C

Effects of Ti element on the microstructural stability of 9Cr–WVTiN reduced activation martensitic steel under ion irradiation

Energy Technology Data Exchange (ETDEWEB)

Luo, Fengfeng [Key Laboratory of Artificial Micro- and Nano-Structures of Ministry of Education, Hubei Nuclear Solid Physics Key Laboratory and School of Physics and Technology, Wuhan University, Wuhan 430072 (China); Guo, Liping, E-mail: guolp@whu.edu.cn [Key Laboratory of Artificial Micro- and Nano-Structures of Ministry of Education, Hubei Nuclear Solid Physics Key Laboratory and School of Physics and Technology, Wuhan University, Wuhan 430072 (China); Jin, Shuoxue; Li, Tiecheng; Chen, Jihong [Key Laboratory of Artificial Micro- and Nano-Structures of Ministry of Education, Hubei Nuclear Solid Physics Key Laboratory and School of Physics and Technology, Wuhan University, Wuhan 430072 (China); Suo, Jinping; Yang, Feng [State Key Laboratory of Mould Technology, Institute of Materials Science and Engineering, Huazhong University of Science and Technology, Wuhan 430074 (China); Yao, Z. [Department of Mechanical and Materials Engineering, Queen’s University, Kingston K7L 3N6, ON (Canada)

2014-12-15

Microstructure of 9Cr–WVTiN reduced-activation martensitic steels with two different Ti concentrations irradiated with Fe{sup +}, He{sup +} and H{sup +} at 300 °C was studied with transmission electron microscopy. Small dislocation loops were observed in the irradiated steels. The mean size and number density of dislocation loops decreased with the increase of Ti concentration. The segregation of Cr and Fe in carbides was observed in both irradiated steels, and the enrichment of Cr and depletion of Fe were more severe in the low Ti-concentration 9Cr–WVTiN steel.

Experience manufacturing and properties of the high-strength corrosion-resistant magnetic 03Kh12K12D2 steel

International Nuclear Information System (INIS)

Fel'dgandler, Eh.G.; Moshkevich, E.I.; Bakuma, S.F.; Bulat, S.I.; Tikhonenko, V.D.

1976-01-01

In industrial conditions, steel 03Kh12K12D2 (DI48-VD) was melted in a 7-tinduction furnace with subsequent vacuum arc remelting. Ingots of dia 500 and 630 mm were forged into slabs and forgings. The slabs were rolled into sheets, 40 mm thick, and the forgings were rolled into sectional shapes. To obtain the optimum mechanical, corrosion, and magnetic properties, the metal was annealed at 600 deg C (10 hr) and 650 deg C (5 and 10 hr). The developed melting and remelting process enabled to obtain steel meeting all the requirements as for the chemical composition, workability, and mechanical magnetic properties. On testing in water with high parameters (200 deg C, 16 kgf/cm 2 ) and in synthetic sea water (70-90 deg C) the corrosion rate did not exceed 1 μm per year

Study of effect of austenite prehistory of 03Ch20N16AG6 steel on it structure and properties

Energy Technology Data Exchange (ETDEWEB)

Demchuk, I S; Krakhmalev, V I; Manninen, A I [Leningradskij Politekhnicheskij Inst. (USSR)

1981-01-01

Effect of preliminary cold working and different procedures of thermal treatment on structure and mechanical properties of stable austenite of 03Kh20N16AG6 steel is found out. It is shown that the degree of defectability of initial austenite structure predetermines the further deformation behaviour of the steel (level of strength characteristics, plasticity storage, hardening degree etc.) in the wide temperature range. Close connection of structural changes with properties should determine the choice of preliminary treatment of stable austenitic steel as applied to concrete condition of operation.

Quality of structural steel melted by single-slag process

International Nuclear Information System (INIS)

Levin, A.M.; Andreev, V.I.; Monastyrskij, A.V.; Drozdova, M.F.; Pashchenko, V.E.; Orzhekh, M.B.

1982-01-01

The 40Kh and 12KhN3A steels were used to compare the quality of the metal manufactured according to several variants of a single-slag process with the metal of a conventional melting technology. Investigation results show, that a single-slag process metal has higher sulfides and oxides contents as well as an increased anisotropy of mechanical properties while its tendency to flake formation is weaker due to a less degree of gas saturation. It is marked that anisotropy in the properties and a sulfide content may be decreased by out-of-furnace treatment of steels

Properties of structural steels melted out of high-purity charge

International Nuclear Information System (INIS)

Marchenko, V.N.; Sergeeva, T.K.; Kondakova, N.K.; Morozov, V.P.; Madorskij, L.L.

1993-01-01

A comparative evaluation has been made of impurities, mechanical properties and hydrogen embirittlement parameters for steels type 40Kh and 40KhS produced by electrometallurgical method with the use of direct reduced charge (DR-steels) and melted in an open-hearth furnace. Investigation results have shown that 40Kh and 40KhS Dr-steels have more coarse austenitic grains and experience more complete transformation of martensite into ferritic-pearlitic mixture on tempering. Threshold stresses increase 2.5 times due to purity enhancement at the expense of application of direct reduced charge

Behaviour of Z phase in 9–12%Cr steels

DEFF Research Database (Denmark)

Danielsen, Hilmar Kjartansson; Hald, John

2006-01-01

The literature on the behaviour of modified Z phase Cr(V,Nb)N in creep resistant martensitic 9–12%Cr steels is briefly reviewed. Ten different 9–12%Cr steels were investigated after prolonged exposure at 600–660uC; the modified Z phase was found in all of them. In steels with high Cr content (11......–12%), Z phase precipitates much faster than in 9%Cr steels. Precipitation of Z phase is associated with dissolution of MX carbonitrides, and causes a breakdown in long term creep strength in 9–12%Cr steels. High Cr steels show creep instabilities accompanied with Z phase precipitation, whereas low Cr...... steels show good long term creep stability. A niobium free CrVN variant of the modified Z phase was observed for the first time during the course of this work. The solution temperature of the Cr(V,Nb)N and CrVN modified Z phases was found to be close to 800uC for 11–12%Cr steels, much lower than the 1200...

Measurements of nitrogen depth distribution in the surface of steel with the 14N(d,p0)15N reaction

International Nuclear Information System (INIS)

Didriksson, R.; Goenczi, L.; Sundqvist, B.

1980-01-01

The 14 N(d,p 0 ) 15 N nuclear reaction has been used to measure the nitrogen depth distribution in the surface of steel samples. With a beam energy of 2.5 MeV a depth of 15μm could be analyzed. The depth resolution was 0.7 μm (FWHM) and nitrogen contents down to 0.02 percent could be determined. (author)

Annealing dislocation loops in OKh16N15M3T steel implanted by helium

International Nuclear Information System (INIS)

Utkelbaev, B.D.; Reutov, V.F.; Zhdan, G.T.

1993-01-01

With the use of electron microscopy a study was made into the influence of preliminary thermomechanical treatment on the process of dislocation loop development in austenitic stainless steel type OKh16N15M3T with helium on annealing. Preliminary treatment was shown to prevent dislocation loop formation to a greater or lesser extent. Preliminary 'cold' working and thermal ageing of the material are the most effective ways to suppress radiation defect formation when annealing helium implanted steel

Reliability and durability of the 12Kh1MF steel tubes of electroslag remelting and their welded joints

International Nuclear Information System (INIS)

Lanskaya, K.A.; Kulikova, L.V.; Mazel', R.E.; Khromchenko, F.A.; Strizhenova, V.F.

1978-01-01

Results of investigating the positive effect of electrolag remelting (ESR) on the properties of the base metal and welded joint of the 12Kh1MF steel steam pipes with the aim of increasing their durability up to 20,000 hrs, are presented. To estimate the quality and properties of tube billet metal, microstructure, content and nature of nonmetallic inclusions, content of gases, austenite grain size, austenite transformations during continuous cooling, metal ductility, mechanical properties at different temperatures and heat resisting properties, have been investigated. It is established, that the base metal in tubes of electroslag remelting possess higher heat resistance, while welded joints besides, have high deformability and resistance to brittle fracture

Stainless austenitic steels strengthened due to reversible phase transformations and by ageing

International Nuclear Information System (INIS)

Sagaradze, V.V.; Kositsyna, I.I.; Ozhiganov, A.V.

1981-01-01

The effect of the reversible phase transformations, consisting in the conduction of the direct and reverse martensite transformations and aging, during which the intermetallide γ'-phase of the composition Ni 3 Ti is formed, on the streng-thening of alloys in the Fe-Cr-Ni-Ti system is considered. Stainless austenitic steels Kh12N12T3 and Kh12N14T3, which acquire high mechanical properties: σsub(0.2)=685-785 MPa, σsub(B)=1275 MPa, delta >= 20%, as a result of reversible phase transformations and aging, are suggested. After the reversible phase transformations and ageing the steels possess a high resistance to γ-α-transformation during cold treatment [ru

Improving composition of protective coatings for steel casting

International Nuclear Information System (INIS)

Kuz'kina, N.N.; Pegov, V.G.; Bogatenkov, V.F.; Shub, L.G.; Raspopova, N.A.

1983-01-01

A radically new fuel-free slag-forming mixture used as protective coating for steel casting is introduced. The lack of combustible powders precludes explosion and fire Lazard in mixture preparation. Usage of the new mixture in stainless steel casting of Kh18N10T type permitted to improve the ingot surface quality and reduce spoilage from 1.16 to 0.66%

Influence of quantity of non-martensite products of transformation on resistance to fracture of improving structural steel

International Nuclear Information System (INIS)

Gulyaev, A.P.; Golovanenko, Yu.S.; Zikeev, V.N.

1978-01-01

18KhNMFA, low-carbon, alloyed steel and 42KhMFA medium-carbon, alloyed steel have been examined. For the purpose of obtaining different structures in hardening the steel, different cooling rates, different temperatures and isothermal holding times are applied. The following has been shown: on tempering to the same hardness (HV 300), the presence of non-martensite structures in hardened state does not practically influence the standard mechanical properties of steel (sigmasub(B), sigmasub(0.2), delta, PSI). The resistance of steel to the brittle failure is enhanced by the uniform, fine-disperse distribution of the carbide phase in the structure of lower bainite (up to 80 % bainite in martensite for 42KhMF steel to be improved), as well as strongly fragmented packages of rack martensite-bainite (up to 50 % lower bainite in martensite of 18KhNMFA steel). The formation of the upper bainite in the structure of the hardened steels 18KhNMFA and 42KhMF results on tempering in the formation of coarse, non-uniform, branched carbide inclusions, and this, in its turn, leads to raising the cold-shortness threshold and to lowering the amount of work as required for propagation of a crack. The presence of ferritic-pearlitic structures in the structural steels hardened to martensite and bainite results in reducing the resistance of steel to the brittle failure; the presence of every 10 % ferritic-pearlitic component in martensite of the structural steels 18KhNMFA and 42KhMFA to be thermally improved, raises T 50 by 8 deg and 20 deg C, respectively

Topic 1. Steels for light water reactor pressure vessels

International Nuclear Information System (INIS)

Brumovsky, M.; Brynda, J.; Kepka, M.; Barackova, L.; Vacek, M.; Havel, S.; Cukr, B.; Protiva, K.; Petrman, I.; Tvrdy, M.; Hyspecka, L.; Mazanec, K.; Kupca, L.; Brezina, M.

1980-01-01

Part 1 of the Proceedings consists of papers on the criteria for the selection and comparison of the properties of steel for pressure vessels and on the metallurgy of the said steels, the selection of suitable material for internal tubing systems, the manufacture of high-alloy steels for WWER components, the mechanical and metallurgical properties of steel 22K for WWER 440 pressure components, and of steel 10MnNi2Mo for the WWER primary coolant circuit, and the metallographic assessment of steel 0Kh18N10T. (J.P.)

Fouling and biocorrosion of a high-alloy steel in the Golden Horn bay

International Nuclear Information System (INIS)

Koryakova, M.D.; Nikitin, V.M.; Suponina, A.P.; Kharchenko, U.V.; Zvyagintsev, A.Yu.

2002-01-01

The studies on the effect of contamination of the Golden Horn bay waters (the Peter the Great Bay in the Japanese Sea) on formation of the community of the bacterio- and macrofouling and corrosion resistance of the Kh18N10T high-alloy steel are continued. The dissolved and chemically absorbed oxygen, pH, saprophytes, oil-oxidizing, sulfate-reducing bacteria and heavy metals are among the medium indicators, characterizing the level of pollution of the regions of the samples testing. It is shown, that the obtained experimental data extend our understanding of the dependent effect of three factors: the sea medium → fouling → corrosion resistance of the Kh18N10T high-alloy steel [ru

The effect of chromium diffusion redistribution on wear resistance of carburized 3Kh13 steel

International Nuclear Information System (INIS)

Shcherbedinskij, G.V.; Shumakov, A.I.; Zemskij, S.V.; Pereverzev, V.M.

1977-01-01

The redistribution of chromium in steel 3Kh13 on carburization in a high-activity carburizer and the wear-resistance of the steel have been investigated. Surface layers with an increased chromium concentration show the highest wear-resistance. The chromium content in the surface layer increases due to its diffusion from the interior. The distribution of carbon and chromium in the carburized layers has been studied with the aid of the radioactive isotope 14 C by the method of layer-by-layer spectral analysis on a vacuum quantometer, layer-by-layer chemical and X-ray structure analysis. The composition of the carbides has been determined by physicochemical analysis. It has been established that the carburized layer can be divided into four zones with respect to its phase composition: first zone - hematite and spinal with 0.5-2.0% C; second zone - solid carbides (Fe,Cr) 7 C 3 ; up to 5% C; third zone - globular carbides in a troostite matrix (Cr,Fe) 7 C 3 and Cr 23 C 6 ; up to 3.5% C; fourth, transitional, zone - troostite carbide mixture Cr 23 C 6 ; up to 1% C. The chromium diffusion in the carburized layer is faster than in the initial austenite. The chromium counterdiffusion is due to the development of a zone of solid carbides M 7 C 3

Heating temperature effect on ferritic grain size of rotor steel

International Nuclear Information System (INIS)

Cheremnykh, V.G.; Derevyankin, E.V.; Sakulin, A.A.

1983-01-01

The heating temperature effect on ferritic grain size of two steels 13Kh1M1FA and 25Kh1M1FA is evaluated. It is shown that exposure time increase at heating temperatures below 1000 deg C up to 10h changes but slightly the size of the Cr-Mo-V ferritic grain of rotor steel cooled with 25 deg C/h rate. Heating up to 1000 deg C and above leads to substantial ferritic grain growth. The kinetics of ferritic grain growth is determined by the behaviour of phases controlling the austenitic grain growth, such as carbonitrides VCsub(0.14)Nsub(0.78) in 13Kh1M1FA steel and VCsub(0.18)Nsub(0.72) in 25Kh1M1FA steel. Reduction of carbon and alloying elements content in steel composition observed at the liquation over rotor length leads to a certain decrease of ferritic grain resistance to super heating

The effects of N+ implantation on the wear and friction of type 304 and 15-5 PH stainless steels

International Nuclear Information System (INIS)

Yost, F.G.; Picraux, S.T.; Follstaedt, D.M.; Pope, L.E.; Knapp, J.A.

1983-01-01

Ion implantation of N + into mechanically polished type 304 and 15-5 PH stainless steels was studied to determine its effect on dry wear and friction behavior. Implantation of 4.0 X 10 17 N + cm -2 at 50 keV yielded a depth profile with a peak concentration of about 45 at.% at a depth of 70 nm which dropped to about 10 at.% at 120 nm. Wear and friction were studied in an unlubricated pin-on-disc configuration using type 304 and 440C stainless steel pins. Both N + -implanted steels exhibited reduced wear at low loads but no significant reduction in the coefficient of friction was found. At the lowest normal load studied (12.3 gf), the average maximum wear depth of the implanted 15-5 PH stainless steel disc (about 0.1 μm) was reduced to approximately 10% of that for the corresponding unimplanted pin-on-disc pair after 1000 cycles. At normal loads of 50 gf or above (corresponding to hertzian stresses of 1160 MPa or higher) all beneficial effects were gone. Vacuum heat treatment at 923 K for 1.8 ks of an identically implanted type 304 stainless steel specimen eradicated the beneficial effects of the nitrogen implantation. The N + -implanted discs show similar reductions in wear to discs implanted with titanium and carbon, but the N + -implanted discs do not exhibit the reductions in the coefficient of friction seen with the discs implanted with titanium and carbon. (Auth.)

Comparison of mechanical behavior of TiN, TiNC, CrN/TiNC, TiN/TiNC films on 9Cr18 steel by PVD

Science.gov (United States)

Feng, Xingguo; Zhang, Yanshuai; Hu, Hanjun; Zheng, Yugang; Zhang, Kaifeng; Zhou, Hui

2017-11-01

TiN, TiNC, CrN/TiNC and TiN/TiNC films were deposited on 9Cr18 steel using magnetron sputtering technique. The morphology, composition, chemical state and crystalline structure of the films were observed and analyzed by X-ray photoelectron spectroscopy (XPS), X-ray diffraction (XRD) and scanning electron microscopy (SEM). Hardness and adhesion force were tested by nanoindentation and scratch tester, respectively. The friction and wear behavior of TiN, TiNC, CrN/TiNC and TiN/TiNC films sliding against GCr15 balls were investigated and compared synthetically using ball-on-disk tribometer. It was found that Tisbnd N, Tisbnd C, Tisbnd Nsbnd C and Csbnd C bonds were formed. The TiN/TiNC film was composed of TiN, TiC and TiNC phases. Hardness and adhesion force results indicated that although the TiN film possessed the highest hardness, its adhesion force was lowest among all the films. Tribological test results showed that the friction coefficient of TiN/TiNC was much lower than that of TiN and the wear rate decreases remarkably from 2.3 × 10-15 m3/Nm to 7.1 × 10-16 m3/Nm, which indicated the TiN/TiNC film has better wear resistance.

Influence of cold work on the diffusion of ion-implanted nitrogen in D9 steel using nuclear reaction analysis

International Nuclear Information System (INIS)

Arunkumar, J.; David, C.; Panigrahi, B.K.; Nair, K.G.M.

2014-01-01

D9 steels and their modified versions are envisaged for use as fuel cladding and wrapper materials in the Indian fast breeder reactor (FBR) programme. The role played by interstitially dissolved nitrogen in steel matrices for the stabilization of austenitic phase, increase of strength and corrosion resistance is well known. Various factors: the role of grain boundaries and the their orientation, stress mediation, grain fragmentation and production of short circuit paths as a result of compressive stress are known to affect the diffusion of nitrogen. Basically, cold working produces plethora of defects throughout the sample as compared to its solution annealed state. Our earlier studies on 1 x10"1"5 and 5x10"1"5 N"1"5 implanted Solution Annealed D9 (SAD9) showed significant vacancy-nitrogen complexes for higher fluence. Hence, thermal diffusion behaviour of nitrogen was studied in 5 x10"1"5 -N"1"5 implanted samples in solution annealed state. In the present study, to understand the influence of cold work, similar thermal diffusion behaviour of nitrogen has been studied in Cold Worked D9 steel (CWD9) using nuclear reaction analysis

Fatigue resistance of Cr-Ni-Mo-V steel

International Nuclear Information System (INIS)

Naumchenkov, N.E.; Filimonova, O.V.; Borisov, I.A.

1985-01-01

A study was made on the effect of additional alloying (Ni, Ni+Co), stress concentration, surface plastic strain on fatigue resistance of rotor steel of Cr-Ni-Mo-V-composition. It is shown that the steel with decreased carbon content possesses high complex of mechanical properties. Fatigue characteristics are not inferior to similar characteristics of steels of 25KhN3MFA type. Additional alloying of the steel containing 0.11...0.17% C and 4.5...4.7% N:, with niobium separately or niobium and cobalt in combination enabled to improve fatigue resistance of samles up to 25%. Strengthening of stress concentration zones by surface plastic strain is recommended for improving rotor suppporting 'nower under cyclic loading

Study of radiation damage of steels for light water pressure vessels at UJV

International Nuclear Information System (INIS)

Vacek, N.; Stoces, B.

1980-01-01

Preoperational determination of radiation resistance of pressure vessel steels is performed at accelerated neutron exposure in a test or materials research reactor. The results obtained at accelerated and operating exposure are not fully identical and surveillance bodies are therefore used manufactured from the pressure vessel material. Currently, the following steels are used for the manufacture of light water reactor pressure vessels: Mn-Mo-Ni (ASTM-A533-B, ASTM-A508), Cr-Mo-V (15Kh2M1FA). At UJV Rez, for irradiation Chanca-M probes imported from France are used featuring electric temperature control. Almost identical radiation embrittlement was measured for all three steels after irradiation with a neutron fluence of 3x10 23 n.m -2 at a temperature of 290 degC. (H.S.)

Increasing the brittle fracture resistance in manual arc welding and heat treatment of type 12KhM steels

International Nuclear Information System (INIS)

Tikhonov, V.P.; Bychenkova, G.A.; Gordeev, Y.V.; Ilyuhov, C.V.

1984-01-01

The extensive application of heat-resisting steels is delayed by their poor weldability. Optimum technology has been developed for manual arc welding and heat treatment of structures of type 12KhM steels resulting in high cracking resistance. Trials were conducted to evaluate the efficiency of removing the structural stresses in tempering the structures. On the basis of the experimental results, it may be assumed that the toughness properties of the welded joints produced by manual arc welding can be improved by optimizing the alloying system of the weld metal, with the parent metal treated in the optimum heat treatment conditions. The aim of subsequent investigations was to assess the properties of the weld metal made with vanadium-free electrodes. It was found that the impact toughness increased two to three times; the mean hardness and the maximum hardness were both less than 220. The reduction in hardness and increase of the toughness properties of the metal are caused by the lower degree of hardening of the bulk of the grain and, consequently, by the lower concentration of plastic strain at the grain boundaries

Rupture of the steel-12KH1MF under creep at temperatures close to 0,5 Tsub(melt)

International Nuclear Information System (INIS)

Berezina, T.G.; Ashikhmina, L.A.; Karasev, V.V.

1976-01-01

Optical and transmission microscopy and fractography techniques have been employed in studying the peculiarities of nucleation and growth of micropores in steel 12Kh1MF at creep. The nucleation of micropores occurs at the initial stages of creep at stress concentration points, predominantly following the retarded shear mechanism. Micropores grow by the way of diffusion, as well as following the deslocation mechanism. An important role in the process of micropore growth is played by pore opening through grain-boundary slip. Pores of 1 to 5 microns in size can be formed along grain boundaries both due to the growth of individual micropores and by coalescence of micropores at points of their concentration. Transition of the creep to the critical phase coincides with the process of the pores blending together to

Fracture of ledeburitic steel during hot plastic deformation

International Nuclear Information System (INIS)

Nikitin, V.P.; Borisov, Yu.A.; Bulat, S.I.; Zajtsev, V.V.

1977-01-01

The mechanisms of the high-temperature failure of high-carbon chromium Kh6F1, Kh6T2 and Kh6VF steels and a possibility to avoid their overheating have been investigated. At 1190 deg C and over the failure occurs along boundaries of grains at points of formation of the initial portions of the liquid phase as carbides are dissolved. If after a holding at 1190-1210 deg C the steels are cooled to 1120-1150 deg C and held for a sufficiently long time, secondary carbides are formed in the eutectic areas and, if the steels are deformed, the discontinuities present a rounded shape. Holding of an overheated steel at 1120-1150 deg C ensures its satisfactory workability in rolling. By choosing adequate overheating and subsequent slight cooling conditions, it is possible not only to retain, but even to improve the plasticity of carbide high-carbon steels. The results of laboratory tests have been confirmed under industrial conditions

Corrosion cracking of 03N18K1M3TYu and 02N12Kh5M3 maraging steels in chloride solutions

Energy Technology Data Exchange (ETDEWEB)

Pavlov, V.N.; Chumalo, G.V.; Vereshchagin, A.N.; Melekhov, R.K.

1987-07-01

The authors investigate the electrochemical behavior in 0.5% NaCl solution and 42% MgCl/sub 2/ solution and the tendency toward corrosion cracking was determined in boiling 0.5% chloride solution of the cobalt-containing maraging steels in the title. Weld specimens and specimens of the base metal of 03N18K1M3TYu steel were tested in 3% NaCl solution for resistance to corrosion cracking. Additional investigations were made of specimens of that steel with previously created fatigue cracks of the base metal and the weld specimens in 3% NaCl solutions, since that steel is a promising material for structures operating in sea water and low concentration chloride solutions.

Positron annihilation and Moessbauer studies of neutron irradiated reactor pressure vessel steels

International Nuclear Information System (INIS)

Brauer, G.; Matz, W.; Liszkay, L.; Molnar, B.

1990-11-01

Positron annihilation (lifetime, Doppler broadening) and Moessbauer studies on unirradiated, neutron irradiated and neutron irradiated plus annealed reactor pressure vessel steels (Soviet type 15Kh2NMFA) are presented. The role of microstructural properties and the formation of irradiation-induced precipitates is discussed. (orig.) [de

Application of experiment planning during investigation of cementation process in solid carburizers

International Nuclear Information System (INIS)

Lisenkov, A.N.; Denisov, V.M.; Prigozhina, E.L.

1981-01-01

A mathematical model of cementation process in solid carburizirs is obtained, the most effective contents of carburizers are chosen. Specimens are produced out of St20, 12KhN3A, 40Kh13, KhVG steels. It is shown that specimens of St20 and 12KhN3A steels have the higher depth of cementated layer, specimens made of 40Kh13 and KhVG steels-the lower depth. It is shown that the quality of cementated layer structure at recommended regimes improved, cementated layer depth for low-carbon steels changed a little and for tool steels increased infficiently: for KhVG steel in 2-3 times for 40Kh13 steel in 1.5-2.5 times

Influence of heating temperature on bainite transformation proceeding in chromium-nickel-molybdenum steels

International Nuclear Information System (INIS)

Kaletin, Yu.M.; Kaletin, A.Yu.

1983-01-01

The purpose of the present paper is to investigate the effect of heating and cooling from austenization temperature on development of bainite transformation in 37KhN3MFA and 18Kh2N4MA structural alloyed steels. The metallographical analysis of specimens has revealed that first crystals of bainite under slow heating up to 770-790 deg C appear at the temperature of about 500 deg C and at 475 deg C there has been much bainite over the whole cross section of the specimen. It is revealed that an increase of heating temperature and cooling rate replace the starting point of bainite transformation upwards. The strongest displacement of the point Bsub(S) into hogh-temperature range takes place after heating steel with the initial bainite structure in intercritical temperature range

Studies on adsorption and corrosion inhibitive properties of quinoline derivatives on N80 steel in 15% hydrochloric acid

Directory of Open Access Journals (Sweden)

K.R. Ansari

2016-12-01

Full Text Available This paper deals with the N80 steel corrosion protection study in 15% HCl which was carried by three quinoline derivatives namely 3-acetyl-1-(4-methylbenzylideneamino quinolin-2-one (AQ-1, 3-acetyl-1-(4 hydroxy benzylideneamino quinolin-2-one (AQ-2, 3-acetyl-1-(3-nitrobenzylideneamino quinolin-2(1H-one (AQ-3 using gravimetric, electrochemical, and quantum chemical studies. Tafel polarization showed that AQs are mixed type inhibitors but dominantly affect cathodic reaction more. The observed results reveal that AQ-1 is the best inhibitor. All the three inhibitors were found to obey the Langmuir adsorption isotherm. Scanning electron microscopy (SEM micrographs supports the protection of the N80 steel by AQs. Quantum chemical study reveals that the inhibitors have a tendency to get protonated and this protonated form has greater tendency to get adsorbed onto the N80 steel surface.

Strength of low-carbon rotor steel

International Nuclear Information System (INIS)

Voropaev, V.I.; Filimonov, O.V.; Borisov, I.A.

1988-01-01

The results of studying the effect of chemical composition and thermal treatment regimes on the structural strength of steels of the 25KhN3MFA type are presented. It is shown that alloying with niobium from 0.01 to 0.08% steels with the increased nickel content (4.2-4.5%) contributes to the increase of structural strength and reduction of semibrittleness temperature. To obtain high values of strength and plastic properties cooling with the rate of 10 3 -10 5 K/hr is recommended

SCC growth behavior of cast stainless steels in high-temperature water. Influences of corrosion potential, steel type, thermal aging and cold-work

International Nuclear Information System (INIS)

Yamada, Takuyo; Terachi, Takumi; Miyamoto, Tomoki; Arioka, Koji

2011-01-01

Recent studies on crack growth rate (CGR) measurement in oxygenated high-temperature pure water conditions, such as normal water chemistry (NWC) in BWRs, using compact tension (CT) type specimens have shown that stainless steel weld metal are susceptible to stress corrosion cracking (SCC). On the other hand, the authors reported that no significant SCC growth was observed on stainless steel weld metals in PWR primary water at temperatures from 250degC to 340degC. Cast austenitic stainless steels are widely used in light water reactors, and there is a similarity between welded and cast stainless steels in terms of the microstructure of the ferrite/austenite duplex structure. However, there are a few reports giving CGR data on cast stainless steels in the BWRs and PWRs. The principal purpose of this study was to examine the SCC growth behavior of cast stainless steels in simulated PWR primary water. A second objective was to examine the effects on SCC growth in hydrogenated and oxygenated water environments at 320degC of: (1) corrosion potential; (2) steels type (Mo in alloy); (3) thermal-aging (up to 400degC x 40 kh); and (4) cold-working (10%). The results were as follows: (1) No significant SCC growth was observed on all types of cast stainless steels: aged (400degC x 40 kh) of SCS14A and SCS13A and 10% cold-working, in hydrogenated (low-potential) water at 320degC. (2) Aging at 400degC x 40 kh SCS14A (10%CW) markedly accelerated the SCC growth of cast material in high-potential water at 320degC, but no significant SCC growth was observed in the hydrogenated water, even after long-term thermal aging (400degC x 40 kh). (3) Thus, cast stainless steels have excellent SCC resistance in PWR primary water. (4) On the other hand, significant SCC growth was observed on all types of cast stainless steels: 10%CW SCS14A and SCS13A, in 8 ppm-oxygenated (high-potential) water at 320degC. (5) No large difference in SCC growth was observed between SCS14A (Mo) and SCS13A. (6) No

Theoretical study of [Li(H2O)n]+ and [K(H2O)n]+ (n = 1-4) complexes

International Nuclear Information System (INIS)

Wojcik, M.J.; Mains, G.J.; Devlin, J.P.

1995-01-01

The geometries, successive binding energies, vibrational frequencies, and infrared intensities are calculated for the [Li(H 2 O) n ] + and [K(H 2 O) n ] + (n = 1-4) complexes. The basis sets used are 6-31G * and LANL1DZ (Los Alamos ECP+DZ) at the SCF and MP2 levels. There is an agreement for calculated structures and frequencies between the MP2/6-31G * and MP2/LANL1DZ basis sets, which indicates that the latter can be used for calculations of water complexes with heavier ions. Our results are in a reasonable agreement with available experimental data and facilitate experimental study of these complexes. 19 refs., 4 figs., 6 tabs

Precipitation process of Z-phase in 9-12%CR steels

DEFF Research Database (Denmark)

Danielsen, Hilmar Kjartansson

2014-01-01

Precipitation of Z-phase, Cr(V,Nb)N, is known to negatively affect creep properties of 9-12%Cr steels for power plant applications as it dissolves finely distributed MX particles, (V,Nb)N, especially in high Cr steels. As the Z-phase precipitates slowly as large particles, this causes a net drop ...... and crystallographically into Z-phase CrTaN particles. Copyright © 2014 Electric Power Research Institute, Inc. Distributed by ASM International®. All rights reserved....

On the ways of improving mechanical properties of boiler steels subject to hydrogen effect

International Nuclear Information System (INIS)

Tkachev, V.I.; Litvin, A.K.; Zvezdin, Yu.I.

1975-01-01

The effect of oxygen on the strength properties of boiler steels Kh15M2 and 48TS subjected to heat treatment and preliminary plastic deformation has been studied. It is shown that changes in the strength properties of the steel are determined by the heterogeneity of its structure. Treatment which contributes to homogenization of the metal structure increases the resistance of the steel to detrimental effect of hydrogen. Absorption of hydrogen during cathode polarization at various current densities is shown

Role of grain refinement in hardening of structural steels at preliminary thermomechanical treatment

International Nuclear Information System (INIS)

Bukhvalov, A.B.; Grigor'eva, E.V.; Davydova, L.S.; Degtyarev, M.V.; Levit, V.I.; Smirnova, N.A.; Smirnov, L.V.

1981-01-01

The hardening mechanism during preliminary thermomechanical treatment with deformation by cold rolling or hydroextrusion is studied on structural 37KhN3M1 and 38KhN3MFA steels. Specimens have been tested on static tension, impact strength and fracture toughness. It is shown that hydroextrusion application instead of rolling does not change the hardening effect of preliminary thermomechanical treatment (PTMT). It is established that the increase of preliminary deformation degree and the use of accelerated short term hardening heating provides a bett er grain refinement and the increase of PTMT hardening effect [ru

Structural features and properties of the laser-deposited nickel alloy layer on a KhV4F tool steel after heat treatment

Science.gov (United States)

Shcherbakov, V. S.; Dikova, Ts. D.; Stavrev, D. S.

2017-07-01

The study and application of the materials that are stable in the temperature range up to 1000°C are necessary to repair forming dies operating in this range. Nickel-based alloys can be used for this purpose. The structural state of a nickel alloy layer deposited onto a KhV4F tool steel and then heat treated is investigated. KhV4F tool steel (RF GOST) samples are subjected to laser deposition using a pulsed Nd:YAG laser. A nickel-based material (0.02C-73.8Ni-2.5Nb-19.5Cr-1.9Fe-2.8Mn) is employed for laser deposition. After laser deposition, the samples are subjected to heat treatment at 400°C for 5 h, 600°C for 1 h, 800°C for 1 h, and 1000°C for 1 h. The microstructure, the phase composition, and the microhardness of the deposited layer are studied. The structure of the initial deposited layer has relatively large grains (20-40 μm in size). The morphology is characterized by a cellular-dendritic structure in the transition zone. The following two structural constituents with a characteristic dendritic structure are revealed: a supersaturated nickel-based γ solid solution and a chromium-based bcc α solid solution. In the initial state and after heat treatment, the hardness of the deposited material (210-240 HV 0.1) is lower than the hardness of the base material (400-440 HV 0.1). Only after heat treatment at 600°C for 1 h, the hardness increases to 240-250 HV0.1. Structure heredity in the form of a dendritic morphology is observed at temperatures of 400, 600, and 800°C. The following sharp change in the structural state is detected upon heat treatment at 1000°C for 1 h: the dendritic morphology changes into a typical α + γ crystalline structure. The hardness of the base material decreases significantly to 160-180 HV 0.1. The low hardness of the deposited layer implies the use of the layer material in limited volume to repair the forming surfaces of dies and molds for die casting. However, the high ductility of the deposited layer of the nickel

X-ray diffraction study of slags forming during corrosion resistant steel production

International Nuclear Information System (INIS)

Slavov, V.I.; Zadorozhnaya, V.N.; Shurygina, A.V.

1990-01-01

Using X-ray diffraction analysis slags, forming during corrosion-resistant 12Kh18N10T grade steel production by two flowsheets, are studied. Standard two-slag technology of steel production does not provide efficient disintegration of chromospinelides in slags, gives high steel contamination with respect to nonmetallic impurities, coarse structure and, as a consequence, presence of macrodefects on rolled products surface. One-slag steel melting technology with titanium alloying of the steel at vacuum causes fast removal of chromospinelides at the beginning of reduction period, promotes titanium absorption by the steel, refines nonmetallic inclusions, provides more fine structure and steel plasticity, removes surface defects

Creep and long-term strength of heat-resistant steels with different structures with the account taken of the type of stress deviator

International Nuclear Information System (INIS)

Giginyak, F.F.; Dragunov, Yu.G.; Mozharovskaya, T.N.; Titov, V.F.

1993-01-01

The results of the experimental investigations into creep and long-term strength of heat-resistant steels 15Kh2MFA and 15Kh2NMFA in the initial state and after heat-treatment simulating the metal irradiation embrittlement at the end of the product service date under static loading at the complex stress state and at high temperatures are presented. The experimentally substantiated equations of state describing creep and long-term stability of materials taking into account the type of the stress state are derived. (author)

Joint formation of dissimilar steels in pressure welding with superposition of ultrasonic oscillations

Energy Technology Data Exchange (ETDEWEB)

Surovtsev, A P; Golovanenko, S A; Sukhanov, V E; Kazantsev, V F

1983-12-01

Investigation results of kinetics and quality of carbon steel joints with the steel 12Kh18N10T, obtained by pressure welding with superposition of ultrasonic oscillations with the frequency 16.5-18.0 kHz are given. The effect of ultrasonic oscillations on the process of physical contact development of the surfaces welded, formation of microstructure and impact viscosity of the compound, is shown.

Mechanical properties of irradiated 9Cr-2WVTa steel

International Nuclear Information System (INIS)

Klueh, R.L.; Alexander, D.J.; Rieth, M.

1998-01-01

An Fe-9Cr-2W-0.25V-0.07Ta-0.1C (9Cr-2WVTa) steel has excellent strength and impact toughness before and after irradiation in the Fast Flux Test Facility and the High Flux Reactor (HFR). The ductile-brittle transition temperature (DBTT) increased only 32 C after 28 dpa at 365 C in FFTF, compared to a shift of ∼60 C for a 9Cr-2WV steel--the same as the 9Cr-2WVTa steel but without tantalum. This difference occurred despite the two steels having similar tensile but without tantalum. This difference occurred despite the two steels having similar tensile properties before and after irradiation. The 9Cr-2WVTa steel has a smaller prior-austenite grain size, but otherwise microstructures are similar before irradiation and show similar changes during irradiation. The irradiation behavior of the 9Cr-2WVTa steel differs from the 9Cr-2WV steel and other similar steels in two ways: (1) the shift in DBTT of the 9Cr-2WVTa steel irradiated in FFTF does not saturate with fluence by ∼28 dpa, whereas for the 9Cr-2WV steel and most similar steels, saturation occurs at <10 dpa, and (2) the shift in DBTT for 9Cr-2WVTa steel irradiated in FFTF and HFR increased with irradiation temperature, whereas it decreased for the 9Cr-2WV steel, as it does for most similar steels. The improved properties of the 9Cr-2WVTa steel and the differences with other steels were attributed to tantalum in solution

Study of regularities in propagation of thermal fatigue cracks

International Nuclear Information System (INIS)

Tachkova, N.G.; Sobolev, N.D.; Egorov, V.I.; Rostovtsev, Yu.V.; Ivanov, Yu.S.; Sirotin, V.L.

1978-01-01

Regularities in the propagation of thermal fatigue cracks in the Cr-Ni steels of the austenite class depending upon deformation conditions in the crack zone, have been considered. Thin-walled tube samples of the Kh16N40, Kh18N20 and Kh16N15 steels have been tested in the 10O reversible 400 deg C and 100 reversible 500 deg C regimes. The samples have possessed a slot-shaped stress concentrator. Stress intensity pseudocoefficient has been calculated for the correlation of experimental data. The formula for determining crack propagation rate has been obtained. The experiments permit to conclude that propagation rate of thermal fatigue cracks in the above steels depends upon the scope of plastic deformation during a cycle and stress intensity pseudocoefficient, and is determined by plastic deformation resistance during thermal cyclic loading

Specific features of the occurrence, development, and re-compaction of spall and shear fractures in spherically-convergent shells made of unalloyed iron and some steels under their spherical explosive loading

International Nuclear Information System (INIS)

Kozlov, E.A.; Brichikov, S.A.; Gorbachev, D.M.; Brodova, I.G.; Yablonskikh, T.I.

2007-01-01

Results of comparative metallographic examination of recovered shells exposed to explosive loading in two modes (with and without a heavy casing confining explosion products scatter) are presented. The shells were made of high-purity and technical-grade unalloyed iron with the initial grain size 250 and 125 μm, steel 30KhGSA in delivery state and quenched up to HR C 35...40, austenitic stainless steel 12Kh18N10T. The heavy casing used in experiments is demonstrated to ensure a rather compact convergence of shells destroyed at high radii. In the described comparative experiments, one managed to compile the 12Kh18N10T steel shell, after it was spalled at high radii and exposed to shear fracture and spallation layer fragmentation at medium radii, into a compact sphere but failed to do the same with the 30KhGSA quenched steel shell after it was fractured according to spall and shear mechanisms at high and medium radii. Polar zones of this steel shell have obvious undercompressed areas due to significant dissipative losses to overcome the shear strength. Occurrence, development, and re-compaction of spall and shear fractures in spherically-convergent shells made of materials, which were already carefully investigated in 1D- and 2D-geometry experiments, were systematically studied in order to verify and validate new physical models of dynamic fractures, as well as up-to-date used in 1D-, 2D- and 3D-numerical algorithms [ru

Special Features of Induction Annealing of Friction Stir Welded Joints of Medium-Alloy Steels

Science.gov (United States)

Priymak, E. Yu.; Stepanchukova, A. V.; Bashirova, E. V.; Fot, A. P.; Firsova, N. V.

2018-01-01

Welded joints of medium-alloy steels XJY750 and 40KhN2MA are studied in the initial condition and after different variants of annealing. Special features of the phase transformations occurring in the welded steels are determined. Optimum modes of annealing are recommended for the studied welded joints of drill pipes, which provide a high level of mechanical properties including the case of impact loading.

Corrosion resistance of heat exchange equipment in hydrotreating Orenburg Condensate

International Nuclear Information System (INIS)

Teslya, B.M.; Burlov, V.V.; Parputs, I.V.; Parputs, T.P.

1986-01-01

The authors study the corrosion resistance of materials of construction and select appropriate materials for the fabrication of heat exchange equipment that will be serviceable under hydrotreating conditions. This paper discusses the Orenburg condensate hydrotreating unit which has been shut down repeatedly for repair because of corrosion damage to components of heat exchangers in the reactor section: tube bundles (08Kh18N10T steel), corrugated compensators (12Kh18N10T steel), and pins of the floating heads (37Kh13N8G8MFB steel). The authors recommend that the tube bundles and the compensators in heat exchangers in the reaction section should be fabricated of 08Kh21N6M2T or 10Kh17N13M2T steel. The pins have been replaced by new pins made of 10Kh17N13 X M2T steel, increasing the service life from 6-12 months to 2 years

Optimum conditions for aging of stainless maraging steels

International Nuclear Information System (INIS)

Mironenko, P.A.; Krasnikova, S.I.; Drobot, A.V.

1980-01-01

Aging kinetics of two 0Kh11N10M2T type steels in which 3 % Mo (steel 1), and 3 % Mo and 11 % Co (steel 2) had been additionally introduced instead of titanium were investigated. Electron microscopy and X-ray methods were used. It was ascertained that the process of steel aging proceeded in 3 stages. Steel 2 was hardened more intensively during the aging, had a higher degree of hardness and strength after the aging, weakened more slowly if overaged than steel 1. The intermetallide hcp-phase Fe 2 Mo was the hardening phase on steels extended aging. Optimum combination of impact strength and strength was was achieved using two-stage aging: the first stage - maximum strength aging was achieved, the second stage - aging at minimum temperatures of two-phase α+γ region

Corrosion-electrochemical behavior of metals in alkali solutions

International Nuclear Information System (INIS)

Levin, V.A.; Levina, E.Eh.

1995-01-01

Results of an investigation into corrosion-electrochemical behaviour of 12Kh18N10T, 10Kh17N13M2T, 08Kh21N6M2T and 15Kh25T steels, 06KhN28MDT and KhN78T alloys as well as NP-2 nickel in sodium, potassium and lithium hydroxide solutions at 95-180 deg C temperatures are considered. It is ascertained, that anode polarization curves of all metals irrespective of hydroxide nature, concentration, temperature, presence of chloride and chlorate additions, are of identic character. The movement of anode polarization curves in the direction of lower current of hydroxide type in NaOH-KOH-LiOH series, temperature and solution concentration reduction at other equal terms. 12 refs.; 6 figs

Microstructure of a high boron 9-12% chromium steel

Energy Technology Data Exchange (ETDEWEB)

Andren, H.O. [Chalmers Univ. of Technology, Goeteborg (Sweden). Dept. of Applied Physics

2008-07-01

Additions of small amounts of boron (10-100 ppm) to 9-12% chromium steels are often made since they have been found to be beneficial for the creep strength up to and above 600 C. The effect of boron is to restrict the coarsening of M{sub 23}C{sub 6} precipitates during service. It was found that increasing the boron content from 9 to 40 ppm gave a decrease in coarsening constant at 600 C by a factor of 2. The present understanding of boron solution, non-equilibrium grain boundary segregation, incorporation into M{sub 23}C{sub 6}, and diffusion is reviewed in the paper. A very high boron addition (300 ppm) was made in the trial TAF steel already in the 1950'ies. The microstructure of a similar trial steel, FT3B, has been studied detail. In this steel large Mo, Cr, Fe and V containing metal borides are formed rather than the expected BN, with the crystal structure M{sub 2}B{sub 2}. Nitrogen is therefore still available for the formation of VN. Due to tempering at a low temperature (690 C) to a high strength (830 MPa), this steel contained a dense distribution of very small VN precipitates, 5-15 nm in size. A similar VN distribution is probably the cause of the still unsurpassed creep strength of the TAF steel. (orig.)

Influence of heat treatment on microstructure and properties of GX12CrMoVNbN9-1 cast steel

Directory of Open Access Journals (Sweden)

G. Golański

2010-07-01

Full Text Available The paper presents results of research on the influence of multistage heat treatment on microstructure and properties of high-chromiummartensitic GX12CrMoVNbN9 – 1 (GP91 steel. The material under investigation were samples taken out from a test coupon. Heattreatment of GP91 cast steel was performed at the parameters of temperature and time typical of treatment for multi-ton steel casts. The research has proved that in the as-received condition (as-cast state GP91 cast steel was characterized by a coarse grain, martensitic microstructure which provided the required standard mechanical properties. The heat treatment of GP91 cast steel contributed to obtainment of a fine grain microstructure of high tempered martensite with numerous precipitations of carbides of diverse size. The GP91 cast steel structure received through heat treatment made it possible to obtain high plastic properties, particularly impact strength, maintaining strength properties on the level of the required minimum.

History of the formerly top secret KH-9 Hexagon spy satellite

Science.gov (United States)

Pressel, Phil

2014-12-01

This paper is about the development, design, fabrication and use of the KH-9 Hexagon spy in the sky satellite camera system that was finally declassified by the National Reconnaissance Office on September 17, 2011 twenty five years after the program ended. It was the last film based reconnaissance camera and was known by experts in the field as "the most complicated system ever put up in orbit." It provided important intelligence for the United States government and was the reason that President Nixon was able to sign the SALT treaty, and when President Reagan said "Trust but Verify" it provided the means of verification. Each satellite weighed 30,000 pounds and carried two cameras thereby permitting photographs of the entire landmass of the earth to be taken in stereo. Each camera carried up to 30 miles of film for a total of 60 miles of film. Ultra-complex mechanisms controlled the structurally "wimpy" film that traveled at speeds up to 204 inches per second at the focal plane and was perfectly synchronized to the optical image.

Composition of the spheroidal objects in KhN77TYuR-VD alloy

International Nuclear Information System (INIS)

Kotkis, M.A.; Nabutovskii, L.S.; Ostrov, A.E.; Zil'berman, A.G.

1986-01-01

The authors make an element analysis of the spheroidal objects in KhN77TYuR-VD alloy with the use of the energy dispersion microanalyzer with which the Stereoscan S-180 scanning electron microscope is equipped. Examples of the qualitative element analysis are shown. The results of the investigations show that the composition of the spheroidal inclusions includes nickel, chromium, titanium, iron, and also silicon and sulfur. The information obtained makes it possible to make an assumption on the mechanism of origin of these objects

Stainless steel phase detector for the 15 UD Pelletron at Nuclear Science Centre

International Nuclear Information System (INIS)

Ghosh, S.; Ahuja, R.; Rao, S.; Sarkar, A.; Avasthi, D.K.; Kanjilal, D.; Roy, A.; Bhowmik, R.K.

1995-01-01

A spiral resonant cavity has been installed at Nuclear Science Centre to monitor the phase of the accelerated pulsed beam from the 15 UD Pelletron. The cavity, made of stainless steel, is optimised for particles with β 0 similar 0.08. The unloaded Q-factor of the cavity is similar 2000 at a resonant frequency of 48 MHz. The measured sensitivity of the cavity pickup for 161.5 MeV 58 Ni pulsed beam is 5.9 μV (peak to peak) per nA of average beam current. The cavity signal can be used for average beam current down to 1 nA. ((orig.))

Elastic and inelastic scattering of {sup 15}N ions by {sup 9}Be at 84 MeV

Energy Technology Data Exchange (ETDEWEB)

Rudchik, A.T., E-mail: rudchik@kinr.kiev.ua [Institute for Nuclear Research, Ukrainian Academy of Sciences, Prospect Nauki 47, 03680 Kyiv (Ukraine); Chercas, K.A. [Institute for Nuclear Research, Ukrainian Academy of Sciences, Prospect Nauki 47, 03680 Kyiv (Ukraine); Kemper, K.W. [Physics Department, Florida State University, Tallahassee, FL 32306-4350 (United States); Rusek, K. [Heavy Ion Laboratory of Warsaw University, ul. L. Pasteura 5A, PL-02-093 Warsaw (Poland); Rudchik, A.A.; Herashchenko, O.V. [Institute for Nuclear Research, Ukrainian Academy of Sciences, Prospect Nauki 47, 03680 Kyiv (Ukraine); Koshchy, E.I. [Kharkiv National University, pl. Svobody 4, 61077 Kharkiv (Ukraine); Pirnak, Val.M. [Institute for Nuclear Research, Ukrainian Academy of Sciences, Prospect Nauki 47, 03680 Kyiv (Ukraine); Piasecki, E.; Trzcińska, A. [Heavy Ion Laboratory of Warsaw University, ul. L. Pasteura 5A, PL-02-093 Warsaw (Poland); Sakuta, S.B. [Russian Research Center “Kurchatov Institute”, Kurchatov Sq. 1, 123182 Moscow (Russian Federation); Siudak, R. [H. Niewodniczański Institute of Nuclear Physics, Polish Academy of Sciences, ul. Radzikowskiego 152, PL-31-342 Cracow (Poland); Strojek, I. [National Center for Nuclear Researches, ul. Hoża 69, PL-00-681 Warsaw (Poland); Stolarz, A. [Heavy Ion Laboratory of Warsaw University, ul. L. Pasteura 5A, PL-02-093 Warsaw (Poland); Ilyin, A.P.; Ponkratenko, O.A.; Stepanenko, Yu.M.; Shyrma, Yu.O. [Institute for Nuclear Research, Ukrainian Academy of Sciences, Prospect Nauki 47, 03680 Kyiv (Ukraine); Szczurek, A. [H. Niewodniczański Institute of Nuclear Physics, Polish Academy of Sciences, ul. Radzikowskiego 152, PL-31-342 Cracow (Poland); Uleshchenko, V.V. [Institute for Nuclear Research, Ukrainian Academy of Sciences, Prospect Nauki 47, 03680 Kyiv (Ukraine)

2016-03-15

Angular distributions of the {sup 9}Be + {sup 15}N elastic and inelastic scattering were measured at E{sub lab}({sup 15}N) = 84 MeV (E{sub c.m.} = 31.5 MeV) for the 0–6.76 MeV states of {sup 9}Be and 0–6.32 MeV states of {sup 15}N. The data were analyzed within the optical model and coupled-reaction-channels method. The elastic and inelastic scattering, spin reorientations of {sup 9}Be in ground and excited states and {sup 15}N in excited states as well as the most important one- and two-step transfer reactions were included in the channels-coupling scheme. The parameters of the {sup 9}Be + {sup 15}N optical potential of Woods–Saxon form as well as deformation parameters of these nuclei were deduced. The analysis showed that the {sup 9}Be + {sup 15}N pure potential elastic scattering dominates at the forward angles whereas the ground state spin reorientation of {sup 9}Be gives a major contribution to the elastic scattering cross sections at the large angles. Contributions from particle transfers are found to be negligible for the present scattering system.

Substitution of modified 9 Cr-1 Mo steel for austentic stainless steels

International Nuclear Information System (INIS)

Sikka, V.K.

1982-04-01

This report describes the current program to develop a high-strength ferritic-martensitic steel. The alloy is essentially Fe-9% Cr-1% Mo with small additions of V and Nb and is known as modifed 9 Cr-1 Mo steel. Its elevated-temperature properties and design allowable stresses match those of type 304 stainless steel for temperatures up to 600 0 C and exceed those of other ferritic steels by factors of 2 to 3. The improved strength of this alloy permits its use in place of stainless steels for many applications

Unit rupture work as a criterion for quantitative estimation of hardenability in steel

International Nuclear Information System (INIS)

Kramarov, M.A.; Orlov, E.D.; Rybakov, A.B.

1980-01-01

Shown is possible utilization of high sensitivity of resistance to fracture of structural steel to the hardenability degree in the course of hardening to find the quantitative estimation of the latter one. Proposed is a criterion kappa, the ratio of the unit rupture work in the case of incomplete hardenability (asub(Tsub(ih))) under investigation, and the analoguc value obtained in the case of complete hardenability Asub(Tsub(Ch)) at the testing temperature corresponding to the critical temperature Tsub(100(M). Confirmed is high criterion sensitivity of the hardened steel structure on the basis of experimental investigation of the 40Kh, 38KhNM and 38KhNMFA steels after isothermal hold-up at different temperatures, corresponding to production of various products of austenite decomposition

Nontoxic corrosion inhibitors for N80 steel in hydrochloric acid

OpenAIRE

M. Yadav; Debasis Behera; Usha Sharma

2016-01-01

The purpose of this paper is to evaluate the protective ability of 1-(2-aminoethyl)-2-oleylimidazoline (AEOI) and 1-(2-oleylamidoethyl)-2-oleylimidazoline (OAEOI) as corrosion inhibitors for N80 steel in 15% hydrochloric acid, which may find application as eco-friendly corrosion inhibitors in acidizing processes in petroleum industry. Different concentrations of synthesized inhibitors AEOI and OAEOI were added to the test solution (15% HCl) and the corrosion inhibition of N80 steel in hydroch...

The genome and structural proteome of YuA, a new Pseudomonas aeruginosa phage resembling M6.

Science.gov (United States)

Ceyssens, Pieter-Jan; Mesyanzhinov, Vadim; Sykilinda, Nina; Briers, Yves; Roucourt, Bart; Lavigne, Rob; Robben, Johan; Domashin, Artem; Miroshnikov, Konstantin; Volckaert, Guido; Hertveldt, Kirsten

2008-02-01

Pseudomonas aeruginosa phage YuA (Siphoviridae) was isolated from a pond near Moscow, Russia. It has an elongated head, encapsulating a circularly permuted genome of 58,663 bp, and a flexible, noncontractile tail, which is terminally and subterminally decorated with short fibers. The YuA genome is neither Mu- nor lambda-like and encodes 78 gene products that cluster in three major regions involved in (i) DNA metabolism and replication, (ii) host interaction, and (iii) phage particle formation and host lysis. At the protein level, YuA displays significant homology with phages M6, phiJL001, 73, B3, DMS3, and D3112. Eighteen YuA proteins were identified as part of the phage particle by mass spectrometry analysis. Five different bacterial promoters were experimentally identified using a promoter trap assay, three of which have a sigma54-specific binding site and regulate transcription in the genome region involved in phage particle formation and host lysis. The dependency of these promoters on the host sigma54 factor was confirmed by analysis of an rpoN mutant strain of P. aeruginosa PAO1. At the DNA level, YuA is 91% identical to the recently (July 2007) annotated phage M6 of the Lindberg typing set. Despite this level of DNA homology throughout the genome, both phages combined have 15 unique genes that do not occur in the other phage. The genome organization of both phages differs substantially from those of the other known Pseudomonas-infecting Siphoviridae, delineating them as a distinct genus within this family.

Effect of temperature on the mechanical characteristics of cold-worked steel OKh16N15M3B with active tension and creep

International Nuclear Information System (INIS)

Erasov, V.S.; Konoplenko, V.P.; Pirogov, E.N.

1986-01-01

Steel OKh16N15M3B is used extensively for the manufacture of atomic reactor fuel-element shells. The aim of this work is a study of the mechanical characteristics of this steel cold-worked by 20% with active tension and creep in the temperature range 973-1323 0 K, which is necessary for predicting the behavior of fuel-element shells in critical situations. It is found that above 973 0 K there is active loss of strength for cold-worked steel OKh16N15M3B. Strength characteristics in the region 973-1323 0 K decrease by more than a factor of six. Thermal activation analysis of the plastic deformation process, showing a sharp increase in activation energy above 1073 0 K, suggests a change in the mechanisms of plastic deformation taking place. For active tension and creep the same temperature range is obtained for a marked change in activation energy

Effect of operational conditions of electroerosion machining on the surface microgeometry parameters of steels and alloys

International Nuclear Information System (INIS)

Foteev, N.K.

1976-01-01

Studies the influence of pulse duration and a series of operating conditions of a ShGI-40-440 spark-machining generator on changes in the basic surface microgeometry characteristics of components of stainless steel 1Kh18N10T, steel St 45 and hard alloy T14K8. The microgeometry characteristics of spark-machined surfaces differ significantly from the corresponding characteristics of surfaces machined by cutting and vibro-rolling

Cooling intensification during quenching of power plant components - the way to increase reliability

International Nuclear Information System (INIS)

Borisov, I.A.

1989-01-01

To enchance the complex of mechanical properties and to increase operation time of large components of power facilities, regimes of accelerated cooling are developed. Results of heat treatment with accelerated cooling of turbine rotor of steel 26KhN3M2FAA, disks of turbine welded rotor of steel 20KhN2MFAA, components of steel 35KhN3MFA, are given. Special steels with carbon content less than 0.30% for details of power machine-building are developed

X-ray spectrum microanalysis of copper and stainless steel surface layer after electroerosion machining

International Nuclear Information System (INIS)

Abdukarimov, Eh.T.; Saidinov, S.Ya.

1989-01-01

The results of experimental investigations of the surface layer of copper and steel 12Kh18N10T after electroerrosion treatment by a rotating tungsten electrode in natural and distilled water are presented. It is established that the quantity of electrode material transferred to the surface of the steel treated grows with the spark discharge energy increase. Tungsten concentration in the surface layer reaches 5-10% with the average depth of penetration 40-50 μm

High temperature strength and aging behavior of 12%Cr-15%Mn austenitic steels

International Nuclear Information System (INIS)

Miyahara, Kazuya; Bae, Dong-Su; Sakai, Hidenori; Hosoi, Yuzo

1993-01-01

High Mn-Cr austenitic steels are still considered to be an important high temperature structural material from the point of view of reduced radio-activation. The objective of the present study is to make a fundamental research of mechanical properties and microstructure of 12%Cr-15%Mn austenitic steels. Especially the effects of alloying elements of V and Ti on the mechanical properties and microstructure evolution of high Mn-Cr steels were studied. Precipitation behaviors of carbides, nitrides and σ phase are investigated and their remarkable effects on the high temperature strength are found. The addition of V was very effective for strengthening the materials with the precipitation of fine VN. Ti was also found to be beneficial for the improvement of high temperature strength properties. The results of high temperature strengths of the 12Cr-15Mn austenitic steels were compared with those of the other candidate and/or reference materials, for example, JFMS (modified 9Cr-2Mo ferritic stainless steel) and JPCAs (modified 316 austenitic stainless steels). (author)

Helium-induced weld degradation of HT-9 steel

International Nuclear Information System (INIS)

Wang, Chin-An; Chin, B.A.; Lin, Hua T.; Grossbeck, M.L.

1992-01-01

Helium-bearing Sandvik HT-9 ferritic steel was tested for weldability to simulate the welding of structural components of a fusion reactor after irradiation. Helium was introduced into HT-9 steel to 0.3 and 1 atomic parts per million (appm) by tritium doping and decay. Autogenous single pass full penetration welds were produced using the gas tungsten arc (GTA) welding process under laterally constrained conditions. Macroscopic examination showed no sign of any weld defect in HT-9 steel containing 0.3 appm helium. However, intergranular micro cracks were observed in the HAZ of HT-9 steel containing 1 appm helium. The microcracking was attributed to helium bubble growth at grain boundaries under the influence of high stresses and temperatures that were present during welding. Mechanical test results showed that both yield strength (YS) and ultimate tensile strength (UTS) decreased with increasing temperature, while the total elongation increased with increasing temperature for all control and helium-bearing HT-9 steels

Parameter optimization for steel quenching by C02-laser irradiation

International Nuclear Information System (INIS)

Moryashchev, S.F.; Kislitsyn, A.A.; Kosyrev, F.K.

1984-01-01

The dependence of average absorption factor on maximal temperature of the article surface during quenching by CO 2 -laser irradiation was determined empirically. The calculations of depth of a hardening zone and process productivity in 40 Kh, 4Kh13 steels and Armco-iron with regard to this dependence were conducted

Sàng khôn as A Theorizing Tool in Mobility Education

Directory of Open Access Journals (Sweden)

Ngoc Ba Doan

2017-02-01

Full Text Available The current virtual and physical mobility of humans, ideas, knowledge and epistemologies has major implications for education, especially in settings where English is seen as the default medium of instruction. While diversity is inherent in mobility, English-only pedagogy is a denial of the richness and potential of diverse resources learners bring with them through their mobility. This paper reports a philosophical stance and pedagogical practices employed by a lecturer in English language education at an Australian university. It argues that students’ full linguistic resources and epistemologies, known as sàng khôn, contribute to their agency and can be used as tools to theorise new knowledge in the context of their mobility education.

Nontoxic corrosion inhibitors for N80 steel in hydrochloric acid

Directory of Open Access Journals (Sweden)

M. Yadav

2016-11-01

Full Text Available The purpose of this paper is to evaluate the protective ability of 1-(2-aminoethyl-2-oleylimidazoline (AEOI and 1-(2-oleylamidoethyl-2-oleylimidazoline (OAEOI as corrosion inhibitors for N80 steel in 15% hydrochloric acid, which may find application as eco-friendly corrosion inhibitors in acidizing processes in petroleum industry. Different concentrations of synthesized inhibitors AEOI and OAEOI were added to the test solution (15% HCl and the corrosion inhibition of N80 steel in hydrochloric acid medium containing inhibitors was tested by weight loss, potentiodynamic polarization and AC impedance measurements. Influence of temperature (298–323 K on the inhibition behavior was studied. Surface studies were performed by using FTIR spectra and SEM. Both the inhibitors, AEOI and OAEOI at 150 ppm concentration show maximum efficiency 90.26% and 96.23%, respectively at 298 K in 15% HCl solution. Both the inhibitors act as mixed corrosion inhibitors. The adsorption of the corrosion inhibitors at the surface of N80 steel is the root cause of corrosion inhibition.

Fatigue Resistance of GX12CrMoVNbN9-1 Cast Steel after Ageing Process

Directory of Open Access Journals (Sweden)

Stanisław MROZIŃSKI

2014-12-01

Full Text Available In the present paper, low cycle fatigue behaviour of GX12CrMoVNbN9-1 (GP91 cast steel is presented. Fatigue tests were performed under isothermal conditions at room temperature and at 550 and 600oC, on five levels of total strain amplitude value ɛac = 0.25÷0.60%. The cast steel subject to investigation was in the as-received condition (after heat treatment and after 8000 hours of ageing at the temperature of 600oC. Performed research has shown an insignificant influence of the ageing process on mechanical properties of GP91 cast steel, determined with the static test of tension. Analysis of the performed tests has proved that GP91 cast steel in the as-received condition and after ageing process was characterized by strong cyclic softening without a clear period of stabilization of the hysteresis loop parameters. The fatigue lifetime curves at each temperature were obtained based on Basquin and Coffin – Manson equations. The process of ageing of GP91 cast steel contributed to a decrease in its fatigue life Nf from a few to a few dozen percent, and the level of fatigue life was dependent on the value of strain amplitude ɛac. It has also been stated that the fatigue life Nf of GP91 cast steel is determined by its plastic properties, and the degree of changes in fatigue life Nf was dependent not only on the temperature of testing, but also on the value of strain amplitude ɛac. DOI: http://dx.doi.org/10.5755/j01.ms.20.4.6077

Non-destructive automated express method for determining the inclination of chromium-nickel steels IGC

International Nuclear Information System (INIS)

Nazarov, A.A.; Kamenev, Yu.B.; Kuusk, L.V.; Kormin, E.G.; Vasil'ev, A.N.; Sumbaeva, T.E.

1986-01-01

Methods of automated control of 18-10-type steel inclination to IGC are developed and a corresponding automated testing complex (ATS) is created. 08Kh18N10T steel samples had two variants of thermal treatment: 1) 1200 deg (5 h), 600 deg (50 h); 2) 1200 deg (5 h). Methods of non-destructive automated control of 18-10-type steel inclination to IGC are developed on the basis of potentiodynamic reactivation (PR) principle. Automated testing complex is developed, which has undergone experimental running and demonstrated a high confidence of results, reliability and easy operation

Nitrogen ion implantation effect on friction coefficient of tool steel

International Nuclear Information System (INIS)

Velichko, N.I.; Udovenko, V.F.; Markus, A.M.; Presnyakova, G.N.; Gamulya, G.D.

1988-01-01

Effect of nitrogen molecular ion implantation into KhVSG steel on the friction coefficient in the air and vacuum is investigated. Irradiation is carried out by the N 2 + beam with energy 120 keV and flux density 5 μ/cm 2 at room temperature in vacuum 5x10 -4 Pa. The integral dose of irradiation is 10 17 particle/cm 2 . Nitrogen ion implantation is shown to provide the formation of the modified layer changing friction properties of steel. The friction coefficient can either increase or decrease depending on implantation and test conditions. 4 refs.; 2 figs

Estimation of the Ultimate Tensile Strength of Steel from Its HB and HV Hardness Numbers and Coercive Force

Science.gov (United States)

Sandomirskii, S. G.

2017-11-01

A formula is derived to accurately describe the tabulated relation between the Brinell ( HB) and Vickers ( HV) hardnesses of steel over the entire range of their possible variation. This formula and the formulas describing the relation between the HB hardness of chromium-molybdenum and chromium-nickel steels and their ultimate tensile strength σu are used to analyze the change in σu of 38KhNM steel upon quenching and tempering. The data that reveal a relation between σu of 38KhNM steel and its coercive force are obtained.

KH 2PO4 as a novel catalyst for regioselective monobromination of aralkyl ketones using N-bromosuccinimide: a green methodology

Directory of Open Access Journals (Sweden)

P. Md. Khaja Mohinuddin

2015-08-01

Full Text Available A simple, regioselective and green method has been developed for the preparation of monobrominated ketones from various aralkyl ketones by using N-bromosuccinimide in presence of KH 2PO 4 in EtOH at reflux temperature. The present method is of short reaction time and simple with excellent isolated yields of products. The use of eco-friendly solvent, reuse of organic waste (succinimide and recyclable catalyst used for 4 times without loss of activity are advantageous. This is the first example of the use of KH 2PO 4 as a useful catalyst in organohalogen chemistry and the present method meets reduce-reuse-recycle (RRR principle towards development of green protocol.

Structural changes in complex steels with 12 % Cr during welding thermal cycle

International Nuclear Information System (INIS)

Ul'yanova, N.V.; Kurnosova, N.D.

1981-01-01

The structural changes in the heat affected zones of welded steam tubes of the 12Kh11V2MF and 18Kh12VMBFR steels, are investigated. A short-time heating of thin samples up to 1300-900 deg C with the aim of imitating the thermal welding cycle permits to determine temperatures of specific region formation in heat affeced zones of 12% Cr steels. The difference in the amounts and structure of σ-ferrite and γ-phase in these regions is established. A ''tongue'' nature of γ-phase grain growth is found in the temperature range of 1150-1100 deg C, while at 1300-1250 deg C σ-ferrite growth with the formation of saw-shape boundaries is observed. It is shown that tensile properties of imitated heat affected zone of 12Kh12VMBFP steel increase with heating temperature with the insignificant plasticity decrease. Impact strength on longitudinal samples decreases but remains higher than that determined by specifications [ru

Thermal conductivity and thermal expansion of stainless steels D9 and HT9

International Nuclear Information System (INIS)

Leibowitz, L.; Blomquist, R.A.

1988-01-01

Renewed interest in the use of metallic fuels in liquid-metal fast breeder reactors has prompted study of the thermodynamic and transport properties of its materials. Two stainless steels are of particular interest because of their good performance under irradiation. These are D9, an austenitic steel, and HT9, a ferritic steel. Thermal conductivity and thermal expansion data for these alloys are of particular interest in assessing in-reactor behavior. Because literature data were inadequate, measurements of these two properties for the two steels were performed and are reported to 1200 K. Of particular interest is the influence on these properties of a phase transition in HT9

Crustal Structure of Khövsgöl, Mongolia

Science.gov (United States)

Scott, A. M.; Meltzer, A.; Stachnik, J.; Russo, R.; Munkhuu, U.; Tsagaan, B.

2017-12-01

Mongolia is part of the Central Asian Orogenic Belt, an accretionary event that spanned 800 million years from the mid-Proterozoic to mid-Phanerozoic. As a result of the past collisional and rifting events, the modern Khövsgöl rift system of northern Mongolia contains a heterogeneous lithospheric structure. The current rift system has three parallel N-S trending basins that roughly align with terrane boundaries. Structures inherited during the accretionary events may be a factor influencing regional deformation. The forces that drive local deformation are not well understood, but varying processes have been proposed: far-field effects of India-Eurasian plate convergence, westward subduction of the Pacific plate, magmatic underplating at the base of the crust, mantle plume activity, and asthenospheric mantle convection. Determining the nature of crustal features within this poorly understood region may illuminate processes that control rifting within intracontinental settings. A network of 26 broadband seismic stations encompassing 200 square kilometers of the Khövsgöl rift system were deployed from August 2014 to June 2016. More than 2100 events were detected, and most earthquakes were concentrated near rift structures. Events between Busiin-Gol and Darkhad, the westernmost and central basins of the Khövsgöl rift system, are distributed within the crust. An active fault is outlined along the eastern border of the Darkhad basin. Khövsgöl earthquakes bound both sides of the rift. Along the northern border of Lake Khövsgöl, seismic events define a shallow active fault orthogonal to the basin. The largest event recorded within the network was a magnitude ml=5.2 located near the northeastern border of Lake Khövsgöl on 12-05-2014. The focal mechanism of this earthquake is predominantly strike-slip, but also includes an extensional component. This work focuses on earthquake relocation and calculating moment tensors and focal mechanisms of larger regional

Corrosion resistance of chromium-nickel steel containing rare earths

International Nuclear Information System (INIS)

Asatiani, G.N.; Mandzhgaladze, S.N.; Tavadze, L.F.; Chuvatina, S.N.; Saginadze, D.I.

1983-01-01

Effect of additional out-of-furnace treatment with complex alloy (foundry alloy) calcite-silicon-magnesium-rare earth metal on corrosion resistance of the 03Kh18N20M3D3C3B steel has been studied. It is shown that introduction of low additions of rare earths improves its corrosion resistance improves its corrosion resistance in agressive media (in 70% - sulfuric acid) in the range of transition from active to passive state. Effect of additional introduction of rare earth metals is not considerable, if potential of steel corrosion is in the range of stable passive state (32% - sulfuric acid). Additional out-of-furnace treatment with complex foundry alloy, containing rare earth metals, provides a possibility to use a steel with a lower content of Cr, Ni, Mo, than in conventional acid-resistant steels in highly agressive media

Effects of nickel and cobalt addition on creep strength and microstructure of the precipitation-strengthened 15Cr ferritic steels

Energy Technology Data Exchange (ETDEWEB)

Shibuya, Masachika; Toda, Yoshiaki; Sawada, Kota; Kushima, Hideaki; Kimura, Kazuhiro [National Inst. for Materials Science, Tsukuba, Ibaraki (Japan)

2010-07-01

Creep strength of 15Cr ferritic steel with ferrite matrix was increased by precipitation strengthening of intermetallic compounds. It was higher than those of 9-12Cr ferritic steels with a tempered martensitic microstructure strengthened by carbide and carbonitride. Addition of nickel was confirmed to improve Charpy impact toughness of the 15Cr steels, however, creep strength was slightly reduced by the addition of nickel. Microstructure of the 15Cr steel changes from ferrite single phase to dual phases of ferrite and martensite with the addition of nickel which is an austenite stabilizing element. The 15Cr steels investigated in the previous study, contain 3mass% of cobalt which is also an austenite stabilizing element, therefore, the influence of nickel and cobalt combination on mechanical properties and microstructure of the 15Cr-1Mo-6W-V-Nb steel is investigated in this study. Creep strength, Charpy impact toughness and microstructure of the steel were strongly influenced by the composition of nickel and cobalt. Design guideline of the 15Cr steel is discussed with respect to a role of microstructure and combination of nickel and cobalt addition. (orig.)

Chemical Composition and Anti-Biofilm Activity of Burdock (Arctium ...

African Journals Online (AJOL)

formation for cultures treated with burdock leaf fraction, thus confirming the inhibitory efficiency of .... subjected three times to 1 min of sonication ..... 15. Lee K-H, Kim B-S, KeumK-S, Yu H-H, Kim Y-H. Essential. Oil of Curcuma longa Inhibits ...

PENDIDIKAN KARAKTER MENURUT KH. WAHID HASYIM

Directory of Open Access Journals (Sweden)

Rangga Sa’adillah S. A. P.

2015-11-01

Full Text Available This library research examined two research questions. They are what thoughts of KH. Wahid Hasyim about the character education are and how the concept of character education by KH. Wahid Hasyim is relevant to the current condition of education in Indonesia. This study reveals two findings through an inductive analysis. The chief finding of this study is that there are eight characteristic values taught by KH.Wahid Hasyim including religious, tolerant, independent, democratic, patriotic, nasionalist, communicative, and keen on reading. Second, this study disclosed that the thought of character education by KH. Wahid Hasyim is in line with the goal of character education. He strove to build a multicultural national life, educate an intelligent civilization, build a noble character, encourage people to contribute to the development of human life, and develop the potential of having kind hearts, positive thoughts and good behavior as well as exemplary models. He also sought to generate enthusiasm of citizens to keep the peace, creativity, independence, and to be able to coexist with other nations in a harmony.

Choice of corrosion-resistant metal for fluotitanic acid

International Nuclear Information System (INIS)

Reingeverts, M.D.; Lapchenko, E.P.; Semenyuk, E.Y.

1986-01-01

The authors investigate the corrosion and anodic behavior of steels 12Kh18N10T, 08Kh21N6M2T, and 06KhN28MDT, nickel, and molybdenum in 10-40% naturally aerated solutions of H 2 TiF 6 at 20 and 50 degrees C. The authors found that in solutions of fluotitanic acid, as also in tetrafluoroboric and hydrofluoric acids, the most stable alloys are chromium-nickel-molybdenum alloy of type 06KhN28MDT and (for acid concentrations above 20%) copper-nickel-alloys of the monel metal type. Steels 12Kh18N10T and 08Kh21N6M2T can be used in acid concentrations of less than 10% and temperatures up to 20 degrees C with anodic protection

Production of 15N-enriched nitric acid (H15NO3

Directory of Open Access Journals (Sweden)

C. R. Sant Ana Filho

2008-12-01

Full Text Available Techniques that employ 15N have proved to be an important tool in many areas of the agronomic and biomedical sciences. Nevertheless, their use is limited by methodological difficulties and by the price of compounds in the international market. Nitric compounds (15NO3- have attracted the interest of researchers. However, these compounds are not currently produced in Brazil. Thus, in the present work H15NO3 was obtained from the oxidation of anhydrous 15NH3. The method we used differs from the industrial process in that the absorption tower is replaced with a polytetrafluoroethylene-lined, stainless-steel hydration reactor. The process output was evaluated based on the following parameters: reaction temperature; ratio of reagents; pressure and flow of 15NH3(g through the catalyst (Pt/Rh. The results showed that, at the best conditions (500 ºC; 50 % excess O2; 0.4 MPa; and 3.39 g.min-1 of 15NH3, a conversion percentage (N-15NH3 to N-15NO3- of 62.2 %, an overall nitrogen balance (N-15NH3 + N-15NO3- of 86.8 %, and purity higher than 99 % could be obtained.

Review of Z phase precipitation in 9–12 wt-%Cr steels

DEFF Research Database (Denmark)

Danielsen, Hilmar Kjartansson

2016-01-01

For high temperature applications, 9–12 wt-%Cr steels in fossil fired power plants rely upon precipitate strengthening from (V,Nb)N MX nitrides for long term creep strength. During prolonged exposure at service temperature, another nitride precipitates: Cr(V,Nb)NZ phase. The Z phases lowly replace......MX, eventually causing a breakdown in creep strength. The present paper reviews the Z phase and its behaviour in 9–12 wt-%Cr steels including thermodynamic modelling, crystal structure, nucleation process and precipitation rate as a function of chemical composition. The influence of Z phase precipitation upon...

Development of oxide dispersion strengthened 9Cr ferritic-martensitic steel clad tube for fast reactor

International Nuclear Information System (INIS)

Laha, K.; Saroja, S.; Mathew, M.D.; Jayakumar, T.; Vijay, R.; Venugopal Reddy, A.; Lakshminarayana, B.; Kapoor, Komal; Jha, S.K.; Tonpe, S.S.

2012-01-01

One of the key issues in the economical operation of FBR is to achieve high burn-up of fuel (200-250 GWd/t) which considerably reduces the fuel cycle cost. This imposes stringent requirements of void swelling resistance upto 200 dpa for the core structural materials. Presently used alloy 09 (a modified austenitic stainless steel, 15Cr-15Ni-Ti) for PFBR has void swelling limit less than 150 dpa. Because of the inherent void swelling resistance, 9-12Cr steels ferritic/martensitic steels are qualified for irradiation upto 200 dpa but their low creep strength at temperatures above 600 deg C restricts their application as a clad material. Oxide dispersion strengthening is found to be promising means of extending the creep resistance of ferritic/martensitic steels beyond 650 deg C without sacrificing the inherent advantages of high thermal conductivity and low swelling of ferritic steels

Supercavitation Advances and Perspectives A collection dedicated to the 70th jubilee of YuN Savchenko

CERN Document Server

2012-01-01

This collection is dedicated to the 70th jubilee of Yu. N. Savchenko, and presents experimental, theoretical, and numerical investigations written by an international group of well-known authors. The contributions solve very important problems of the high-speed hydrodynamics, such as supersonic motion in water, drag diminishing, dynamics and stability of supercavitating vehicles, water entry and hydrodynamic performances of hydrofoils, ventilated cavities after a disc and under the ship bottom. The  book is written for researches, scientists, engineers, and students interested in problems of hydromechanics.

Enhancement of strength properties of hot rolled 10KHSND steel

International Nuclear Information System (INIS)

Nasibov, A.G.; Popova, L.V.; Pikulin, S.A.; Globa, N.I.

1989-01-01

To find out the reasons of low hot rolling yield for 10KhSND steel sheets in mechanical properties, titanium effect in the range of 0.008-0.03% concentrations is studied. It is established that the titanium content in a solid solution is conserved within 0.003-0.005%, the rest of titanium is bound to carbonitrides Ti(C, N). It is shown that alloys with 0.025-0.03% titanium content possess the increased values of ultimate and yield strength the necessary level of impact strength and good wealdability. The good steel yield, when the titanium content is sustained at the given level, increases from 40 to 85%

Microstructural characterization of 5-9% chromium reduced-activation steels

International Nuclear Information System (INIS)

Jayaram, R.; Klueh, R.L.

1997-01-01

The microstructures of a 9Cr-2W-0.25-0.1C (9Cr-2WV), a 9Cr-2W-0.25V-0.07Ta-0.1C (9Cr-2WVTa), a 7Cr-2W-0.25V-0.07Ta-0.1C (7Cr-2WVTa), and a 5Cr-2W-0.25V-0.07Ta-0.1C (5Cr-2WVTa) steel (all compositions are in weight percent) have been characterized by Analytical Electron Microscopy (AEM) and Atom Probe Field Ion Microscopy (APFIM). The matrix in all four reduced-activation steels was 100% martensite. In the two 9Cr steels, the stable precipitates were blocky M 23 C 6 and small spherical MC. The two lower-chromium steels contained blocky M 7 C 3 and small needle-shaped carbonitrides in addition to M 23 C 6 . AEM and APFIM analysis revealed that in the steels containing tantalum, the majority of the tantalum was in solid solution. The experimental observations were in good agreement with phases and compositions predicted by phase equilibria calculations

Quaternary (liquid + liquid) equilibria of aqueous two-phase polyethylene glycol, poly-N-vinylcaprolactam, and KH{sub 2}PO{sub 4}: Experimental and the generalized Flory-Huggins theory

Energy Technology Data Exchange (ETDEWEB)

Foroutan, Masumeh [Department of Physical Chemistry, Faculty of Chemistry, College of Science, University of Tehran, Enghelab Ave., Tehran 14155-6455 (Iran, Islamic Republic of)], E-mail: foroutan@khayam.ut.ac.ir; Zarrabi, Mona [Department of Physical Chemistry, Faculty of Chemistry, College of Science, University of Tehran, Enghelab Ave., Tehran 14155-6455 (Iran, Islamic Republic of)

2008-06-15

A quaternary (liquid + liquid) equilibrium study was performed to focus attention on the interaction parameters between poly-N-vinylcaprolactam (PVCL) and poly-ethylene glycol (PEG) as well as between other species. At first, the new experimental data of (liquid + liquid) equilibria for aqueous two-phase systems containing PEG, KH{sub 2}PO{sub 4}, and PVCL at T = 303.15 K have been determined. Then the Flory-Huggins theory with two electrostatic terms (the Debye-Huckel and the Pitzer-Debye-Huckel equations) has been generalized to correlate the phase behavior of the quaternary system. Good agreement has been found between experimental and calculated data from both models especially from the Pitzer-Debye-Huckel equation. Also an effort was done to compare the effect of temperature as well as addition of PVCL on the binodal curves of PEG, KH{sub 2}PO{sub 4}, and water. The effect of the type of salt on the binodals has been also studied, and the salting out power of the salts has been determined.

Interaction of steel, titanium and zirconium with melted chlorides containing copper and zinc

International Nuclear Information System (INIS)

Ozeryanaya, I.N.; Manukhina, T.I.; Shibanov, B.S.

1976-01-01

Cu and Zn coatings were obtained by contact displacement of their molten chlorides. Cu was deposited on Kh18N10T stainless steel, and Zn was deposited on Ti or Zr at 400-550 0 . Cu was displaced from the electrolyte by all components in the steel. A smooth coating exhibited high adhesion. According to metallography there was a transition layer of a Ni-Cr solid solution between the surface Cu layer and steel. With electronegetiol Ti and Zr, contact deposition of Zn or Cu from chloride melts was possible. The coatings were multilayer and exhibited adequate adhesion. The coating consisted of an intermetallic compound of Ti or Zr with Zn

Effect of aging on the tribological and mechanical properties of a high-nitrogen stainless austenitic steel

International Nuclear Information System (INIS)

Korshunov, L.G.; Chernenko, N.L.; Tereshchenko, N.A.; Uvarov, A.I.

2005-01-01

The effect of aging, associated with predominant precipitation of vanadium nitrides (VN), on tribological and mechanical properties of austenitic steel 10Kh18AG18N5MF hardened from 1100 Deg C is studied. Metallographic, X-ray diffraction and electron microscopical methods are used to study structural transformations proceeding in the steel on aging as well as on friction loading under conditions of dry slipping friction in steel-abrasive and steel-steel pairs. It is shown that the aging at temperatures of 600-700 Deg C resulting in a considerable increase of strength properties of the steel demonstrates a relatively weak positive effect on steel resistance to abrasive and adhesive wear. It is stated that the use of aging by continuous mechanism permits attaining favourable mechanical and tribological properties in vanadium-alloying nitrogen-bearing austenitic steels [ru

Microstructural stability of 21-6-9 stainless steel

International Nuclear Information System (INIS)

Krenzer, R.W.; Sanderson, E.C.

1978-01-01

Two experiments were designed to better define parameters for thermomechanical processing of 21-6-9 stainless steel. This steel is one of the nitrogen-strengthened chromium, manganese, and nickel austenitic stainless steels having mechanical properties that can be improved by a combination of plastic deformation and heat treatments. By heat-treating coupons, the time-temperature relationship of the precipitate phase, and the solutionizing, recrystallizing, and stress-relieving temperature ranges in 21-6-9 were established. Secondly, mechanical properties and microstructure as a function of percent deformation and stress-relieving temperature are reported

On superplasticity of corrosion resistant ferritic-austenitic chromium-nickel steels

Energy Technology Data Exchange (ETDEWEB)

Surovtsev, A P; Sukhanov, V E

1988-01-01

The deformability of corrosion resistant chromium-nickel ferritic austenitic steel type O8Kh22N6T under tension, upsetting and torsion in the 600-1200 deg C temperature range is studied. For the deformation rate of the order of 10/sup -3/ s/sup -1/ the effect of superelasticity reveals itself at 850 deg C in the process of ferrite dynamic polymerization, in the 925-950 deg C range, at initial stages of dynamic recrystallization - the dynamic polygonization controlled by chromium carbide dissolving in steel and maximum at 1050 deg C in the process of development of austenite dynamic recrystallization with grain refinement with F/A ratio equalling 1. After upsetting in the elasticity mode at 1050 deg C the impact strength of the above steel is maximum.

Relationships of quenching stresses to structural transformations in steel

International Nuclear Information System (INIS)

Loshkarev, V.E.

1985-01-01

Technique for accountancy of the effect of stresses on structural transformations in steel when solving problems of thermoplasticity is suggested. It is revealed on the basis of the conducted calculations that accountancy of interrelation of stressed and structural states of 20Kh2MF steel essentially affects forecasting of results of quenching

Microstructural characterization of 5-9% chromium reduced-activation steels

Energy Technology Data Exchange (ETDEWEB)

Jayaram, R. [Univ. of Pittsburgh, PA (United States); Klueh, R.L. [Oak Ridge National Lab., TN (United States)

1997-08-01

The microstructures of a 9Cr-2W-0.25-0.1C (9Cr-2WV), a 9Cr-2W-0.25V-0.07Ta-0.1C (9Cr-2WVTa), a 7Cr-2W-0.25V-0.07Ta-0.1C (7Cr-2WVTa), and a 5Cr-2W-0.25V-0.07Ta-0.1C (5Cr-2WVTa) steel (all compositions are in weight percent) have been characterized by Analytical Electron Microscopy (AEM) and Atom Probe Field Ion Microscopy (APFIM). The matrix in all four reduced-activation steels was 100% martensite. In the two 9Cr steels, the stable precipitates were blocky M{sub 23}C{sub 6} and small spherical MC. The two lower-chromium steels contained blocky M{sub 7}C{sub 3} and small needle-shaped carbonitrides in addition to M{sub 23}C{sub 6}. AEM and APFIM analysis revealed that in the steels containing tantalum, the majority of the tantalum was in solid solution. The experimental observations were in good agreement with phases and compositions predicted by phase equilibria calculations.

High-cycle fatigue characteristics of weldable steel for light-water reactors

International Nuclear Information System (INIS)

Klesnil, M.; Polak, J.; Obrtlik, K.; Troshchenko, V.T.; Mishchenko, Yu.I.; Khamaza, L.A.

1982-01-01

Czechoslovak and Soviet 15Kh2NMFA steel was used for running fatigue tests at temperatures of 20, 350 and 400 degC in the high-cycle range with various loading regimes. The results show that at the given temperatures in this type of steel a cyclic softening occurs. The fatigue characteristics were measured with great dispersion of results, but within this dispersion they are almost identical for various steels at the same temperature. Increased temperature results in the decrease in the amplitude of cyclic deformation stress and in the increase in the amplitude of plastic deformation. The diversity in the values of cyclic plasticity and stress response measured in the given mode may be explained by the lower level of softening and the non-homogeneous cyclic plastic deformation of material under the given constant conditions. (J.B.)

Influence of Z-phase on long-term creep stability of martensitic 9-12% Cr steels

Energy Technology Data Exchange (ETDEWEB)

Danielsen, Hilmar K. [Technical Univ. of Denmark, Lyngby (Denmark). Dept. of Mechanical Engineering; Hald, John [DONG Energy A/S (Denmark); Vattenfall (Denmark)

2010-07-01

The long-term creep strength of the new generation of martensitic creep resistant 9-12%Cr steels since the well-known steel Grade 91 relies strongly on particle strengthening by fine Mn nitrides based on V and Nb. During long-term high-temperature exposures the Mn nitrides may be replaced by the thermodynamically more stable Z-phases (Cr(V,Nb)N) causing a breakdown in creep strength. Cr contents above 10.5% strongly accelerate Z-phase precipitation, which explains the lack of success for all attempts to develop martensitic creep resistant steels with high Cr content for oxidation protection. However 9%Cr steels do not seem to be affected by the Z-phase. Careful control of the Z-phase precipitation process has led to the design of experimental 12%Cr martensitic steels strengthened by fine Z-phase nitrides based on Nb or Ta. Such steels may again enable the combination of high strength and oxidation resistance in the same alloy. This opens a new pathway for further alloy development of the heat resistant martensitic steels. (orig.)

Kankaan tuotekehittäminen erikoisolosuhteisiin K&H Annala Oy:lle

OpenAIRE

Koski, Marjo

2017-01-01

Opinnäytetyö tehtiin yhteistyössä Suomen ainoan huonekalukankaita valmistavan yrityksen K&H Annala Oy:n kanssa. Työn aiheena oli suunnitella ja tuotteistaa kangasmallisto erikoisolosuhteisiin innovatiivisesta, Italiassa valmistettavasta Flyer-langasta. Projektin lähtökohtana oli opinnäytetyöntekijän kasvava kiinnostuneisuus kudottuja tekstiilejä kohtaan ja kankaan suunnitteluprosessin vieminen teollisen tuotannon puolelle. Projektissa tähdättiin uudentyyppiseen kankaaseen ilmeen ja materiaali...

Influence of ion implanted helium on deuterium trapping in Kh18N10T stainless steel

International Nuclear Information System (INIS)

Tolstolutskaya, G.D.; Ruzhitskij, V.V.; Kopanets, I.E.

2004-01-01

The results are presented on evolution of distribution profiles and helium and deuterium thermal desorption ion implanted in steel 18Cr10NiTi. Accumulation, trapping, retention and microstructure evolution are studied; effect helium and hydrogen simultaneous implantation on these processes is also studied

Optimum alloy compositions in reduced-activation martensitic 9Cr steels for fusion reactor

International Nuclear Information System (INIS)

Abe, F.; Noda, T.; Okada, M.

1992-01-01

In order to obtain potential reduced-activation ferritic steels suitable for fusion reactor structures, the effect of alloying elements W and V on the microstructural evolution, toughness, high-temperature creep and irradiation hardening behavior was investigated for simple 9Cr-W and 9Cr-V steels. The creep strength of the 9Cr-W steels increased but their toughness decreased with increasing W concentration. The 9Cr-V steels exhibited poor creep rupture strength, far below that of a conventional 9Cr-1MoVNb steel and poor toughness after aging at 873 K. It was also found that the Δ-ferrite should be avoided, because it degraded both the roughness and high-temperature creep strength. Based on the results on the simple steels, optimized martensitic 9Cr steels were alloy-designed from a standpoint of enough thoughness and high-temperature creep strength. Two kinds of optimized 9Cr steels with low and high levels of W were obtained; 9Cr-1WVTa and 9Cr-3WVTa. These steels indeed exhibited excellent toughness and creep strength, respectively. The 9Cr-1WVTa steel exhibiting an excellent roughness was shown to be the most promising for relatively low-temperature application below 500deg C, where irradiation embrittlement is significant. The 9Cr-3WVTa steel was the most promising for high temperature application above 500deg C from the standpoint of enough high-temperature strength. (orig.)

Creep constitutive equation of dual phase 9Cr-ODS steel

International Nuclear Information System (INIS)

Sakasegawa, Hideo; Ukai, Shigeharu; Tamura, Manabu; Ohtsuka, Satoshi; Tanigawa, Hiroyasu; Ogiwara, Hiroyuki; Kohyama, Akira; Fujiwara, Masayuki

2008-01-01

9Cr-ODS (oxide dispersion strengthened) steels developed by JAEA (Japan Atomic Energy Agency) have superior creep properties compared with conventional heat resistant steels. The ODS steels can enormously contribute to practical applications of fast breeder reactors and more attractive fusion reactors. Key issues are developments of material processing procedures for mass production and creep life prediction methods in present R and D. In this study, formulation of creep constitutive equation was performed against the backdrop. The 9Cr-ODS steel displaying an excellent creep property is a dual phase steel. The ODS steel is strengthened by the δ ferrite which has a finer dispersion of oxide particles and shows a higher hardness than the α' martensite. The δ ferrite functions as a reinforcement in the dual phase 9Cr-ODS steel. Its creep behavior is very unique and cannot be interpreted by conventional theories of heat resistant steels. Alternative qualitative model of creep mechanism was formulated at the start of this study using the results of microstructural observations. Based on the alternative creep mechanism model, a novel creep constitutive equation was formulated using the exponential type creep equation extended by a law of mixture

Specific Features of Structural-Phase State and Properties of Reactor Pressure Vessel Steel at Elevated Irradiation Temperature

Directory of Open Access Journals (Sweden)

E. A. Kuleshova

2017-01-01

Full Text Available This paper considers influence of elevated irradiation temperature on structure and properties of 15Kh2NMFAA reactor pressure vessel (RPV steel. The steel is investigated after accelerated irradiation at 300°C (operating temperature of VVER-1000-type RPV and 400°C supposed to be the operating temperature of advanced RPVs. Irradiation at 300°C leads to formation of radiation-induced precipitates and radiation defects-dislocation loops, while no carbide phase transformation is observed. Irradiation at a higher temperature (400°C neither causes formation of radiation-induced precipitates nor provides formation of dislocation loops, but it does increase the number density of the main initial hardening phase—of the carbonitrides. Increase of phosphorus concentration in grain boundaries is more pronounced for irradiation at 400°C as compared to irradiation at 300°C due to influence of thermally enhanced diffusion at a higher temperature. The structural-phase changes determine the changes of mechanical properties: at both irradiation temperatures irradiation embrittlement is mainly due to the hardening mechanism with some contribution of the nonhardening one for irradiation at 400°C. Lack of formation of radiation-induced precipitates at T = 400°C provides a small ΔTK shift (17°C. The obtained results demonstrate that the investigated 15Kh2NMFAA steel may be a promising material for advanced reactors with an elevated operating temperature.

Hot deformation effect on the kinetics of austenite transformation under continuous cooling conditions

International Nuclear Information System (INIS)

Bernshtejn, M.L.; Zajmovskij, V.A.; Kisteh, N.V.; Samedov, O.V.; Faldin, S.A.

1979-01-01

The effect of hot deformation on the kinetics of austenite transformations in the commercial 4040Kh 40KhN, and 40KhNMA steels on continuous cooling was studied. The transformations were studied using a dilatometer of a special design which permits a specimen to be fixed quickly in holders after hot deformation. It is stated that in hot-deformed austenite the pearlite transformation proceeds at higher temperatures and in a narrower temperature range. Austenite deformation provides an opportunity to obtain a more fine ferrite-pearlite structure and ensures a uniform distribution of a structurally free ferrite in the steel bulk. The effect of hot deformation on the structure of ferrite decomposition products in the 40KhN and 40KhNMA steels is more complicated, which is connected with a substantial change in the kinetics of pearlite and intermediate transformations

Long-term behaviour of heat-resistant steels and high-temperature materials

International Nuclear Information System (INIS)

1987-01-01

This book contains 10 lectures with the following subjects: On the effect of thermal pretreatment on the structure and creep behaviour of the alloy 800 H (V. Guttmann, J. Timm); Material properties of heat resistant ferritic and austenitic steels after cold forming (W. Bendick, H. Weber); Investigations for judging the working behaviour of components made of alloy 800 and alloy 617 under creep stress (H.J. Penkalla, F. Schubert); Creep behaviour of gas turbine materials in hot gas (K.H. Kloos et al.); Effect of small cold forming on the creep beahviour of gas turbine blades made of Nimonic 90 (K.H. Keienburg et al.); Investigations on creep fatigue alternating load strength of nickel alloys (G. Raule); Change of structure, creep fatigue behaviour and life of X20 Cr Mo V 12 1 (by G. Eggeler et al.); Investigations on thermal fatigue behaviour (K.H. Mayer et al.); Creep behaviour of similar welds of the steels 13 Cr Mo 4 4, 14 MoV 6 3, 10 Cr Mo 910 and GS-17 Cr Mo V 5 11 (K. Niel et al.); Determining the creep crack behaviour of heat resistant steels with samples of different geometry (K. Maile, R. Tscheuschner). (orig.,/MM) [de

Yu Kilchun’s Concept of Reform of the Tax System in the Korean Empire

Directory of Open Access Journals (Sweden)

Jinah Yang

2016-08-01

Full Text Available Yu Kilchun in “Semubu (Tax Department” criticizes the trend of the tax system, in which the authority to impose and collect taxes had been taken away from the local magistrates and the isŏ class (composed of hyangni, local functionaries, and sŏri, petty clerks during the Kabo Reform was once again returned to them. Yu Kilchun devised a concept of tax system reform on the premise of the reorganization of the administrative districts into the chu-kun-hyang-ri (state-county-district-village system. Yu’s idea was to make myŏn (hyang, district a governing administrative unit, placed under direct government control. To fund the operation of local governments, Yu proposed to create local taxes, chu taxes and hyang. Tax amounts were to be determined by local assemblies, chuhoe and hyanghoe, which were given the authority to deliberate on budget. The authority to review tax sources, levy and collect taxes was given to hyang, a small unit of administrative division. By imbuing this authority to hyang, Yu Kilchun planned to exclude local magistrates and the isŏ class in the tax collection process. Since “Semubu” discusses the reorganization of administrative divisions and local tax administration, as well as local tax system reform, the discovery of this text is significant, as it expands the range of the reform ideas proposed by Yu Kilchun, and furthermore the Enlightenment Party.

[Textual research on Guang dong xin yu (New Sayings of Guangdong) quoted in Ben cao gang mu shi yi (Supplements to Compendium of Materia Medica].

Science.gov (United States)

Zhang, Ruixian; Zhang, Wei; Li, Jian; Liang, Fei

2014-05-01

Altogether 15 terms for Guang dong xin yu (New Sayings of Guangdong) were used in Ben cao gang mu shi yi (Supplements to Compendium of Materia Medica), including Yue yu (Cantonese sayings), Chong yu (Sayings from Insect Drug), Jie yu (Sayings from Crustacean Drug), Xin yu (New Sayings), Yue hai xiang yu (Fragrant Sayings from Cantonese Region), Yue zhi mu yu (Sayings from Plants in Cantonese Annals), Guang dong suo yu (Trivial Sayings from Guangdong), Yue shan lu (Records of Cantonese Mountains), Yue lu (Cantonese Records), Jiao guang lu (Joint Guangdong Records), Yue cao zhi (Records of Cantonese Grasses), Guang guo lu (Records of Guangdong Fruits), Nan yue suo ji (Trivial Records of Southern Canton), Guang zhi (Guangdong Records), Yue zhi (Cantonese Records) etc. dealing with 57 sorts of drugs (with individual overlapping ones), the author of Xin yu was Qu Dajun, a surviving fogy of the Ming Dynasty actively involved in the activities to restore the old dynasty and resist the Qing Dynasty, and was persecuted in the literary inquisition in which his works were burnt so that Zhao Xuemin, when quoting his texts, had to go in a roundabout way.

Bubble formation upon crystallization of high nitrogen iron base alloys

International Nuclear Information System (INIS)

Svyazhin, A.G.; Sivka, E.; Skuza, Z.

2000-01-01

A study is made into the conditions of nitrogen bubble formation during crystallization of unalloyed iron, alloys of Fe-O, Fe-O-S systems, steels 1Kh13, 0Kh18N9 and a two-phase Fe-11%Cr-1%Mo-0.2%V steel. It is revealed that the amount of bubbles in a high nitrogen steel casting increases with a degree of nitrogen supersaturation and decreases with a cooling rate growth and with a rise of surfactant concentration in the metal. In sound castings a nitrogen content can be increased due to a cooling rate growth, nitrogen dilution with inert gas, an increase of nitrogen pressure during crystallization as well as due to the introduction of such surfactants as sulphur, selenium, tellurium, tin [ru

Electroexcitation of 15N levels from 9.7 to 14.7 MeV

International Nuclear Information System (INIS)

Ansaldo, E.J.; Bergstrom, J.C.; Caplan, H.S.; Yen, R.

1977-01-01

The electromagnetic form factors of five transitions in 15 N have been measured for momentum transfers between 0.48 and 1.27 fm -1 . The transitions observed were identified with levels at 9.76, 10.80, 11.88, 12.50, and 14.7 MeV excitation energy. Ground state radiative widths have been extracted by a Helm model analysis. (author)

Evolution of the structure and the phase composition of a bainitic structural steel during plastic deformation

Science.gov (United States)

Nikitina, E. N.; Glezer, A. M.; Ivanov, Yu. F.; Aksenova, K. V.; Gromov, V. E.; Kazimirov, S. A.

2017-10-01

The evolution of the phase composition and the imperfect substructure of the 30Kh2N2MFA bainitic structural steel subjected to compressive deformation by 36% is quantitatively analyzed. It is shown that deformation is accompanied by an increase in the scalar dislocation density, a decrease in the longitudinal fragment sizes, an increase in the number of stress concentrators, the dissolution of cementite particles, and the transformation of retained austenite.

Austenite strengthening and softening during hot deformation

International Nuclear Information System (INIS)

Tushinskij, L.I.; Vlasov, V.S.; Kazimirova, I.E.; Tokarev, A.O.

1981-01-01

Processes of formation of austenite structure of 20 and 12Kh18N10T steels during hot deformation and postdeformation isothermal holdings have been investigated by the methods of analysis of curves of hot deformation, high-temperature metallography and light microscopy. Deformation has been exercised by extention in vacuum with average 4x10 -2 s -1 rate. Deformation temperatures of steel 20 are 930 and 1000 deg C, of steel 12Kh18N10T - 1100 deg C. It is stated that dynamic recrystallization takes place in both investigated steels during hot deformation. In the carbonic steel it is developed by shifting sections of high-angular boundaries, flow stress in this case remains constant. Recrystallization is developed by subgrain coalescence in austenite steel, that brings about preservation of increased defect density in recrystallized volumes. As a result strengthening of steel is continued up to fracture during the increase of the deformation degree. Postdeformation weakening of 12Kh18N10T steel is slowed down as compared with weakening of carbonic steel [ru

Inhibitor effect on corrosion of titanium alloys in muriatic solutions of titanium-magnesium production

International Nuclear Information System (INIS)

Dobrunov, Yu.V.; Volynskij, V.V.; Kolobov, G.A.; Kuznetsov, S.I.

1977-01-01

Corrosion tests of titanium alloys VTI-0, OT4, VT5-1 and steel Kh18N1OT in 10% and 18% HCl with additions of carnallite at 40 deg C have been carried out. It has been established that titanium alloys in 10% and 18% HCl containing 5 and 10% carnallite are sufficiently corrosion resistant in the presence of 0.1-1% FeCl or HNO 3 and can be used for manufacturing the equipment of recirculation gas scrubbers. Steel Kh18N10T is unstable in all the media tested. It is subjected to intensive pitting. Specimens of steel Kh18N10T have also revealed edge cracking

Steamside Oxidation Behavior of Experimental 9%Cr Steels

Energy Technology Data Exchange (ETDEWEB)

Dogan, O.N.; Holcomb, G.R.; Alman, D.E.; Jablonski, P.D.

2007-10-01

Reducing emissions and increasing economic competitiveness require more efficient steam power plants that utilize fossil fuels. One of the major challenges in designing these plants is the availability of materials that can stand the supercritical and ultra-supercritical steam conditions at a competitive cost. There are several programs around the world developing new ferritic and austenitic steels for superheater and reheater tubes exposed to the advanced steam conditions. The new steels must possess properties better than current steels in terms of creep strength, steamside oxidation resistance, fireside corrosion resistance, and thermal fatigue resistance. This paper introduces a series of experimental 9%Cr steels containing Cu, Co, and Ti. Stability of the phases in the new steels is discussed and compared to the phases in the commercially available materials. The steels were tested under both the dry and moist conditions at 650ºC for their cyclical oxidation resistance. Results of oxidation tests are presented. Under the moist conditions, the experimental steels exhibited significantly less mass gain compared to the commercial P91 steel. Microstructural characterization of the scale revealed different oxide compositions.

Properties of cast Ti-stabilised stainless steel after long-term ageing

International Nuclear Information System (INIS)

Ehrnsten, U.; Karjalainen-Roikonen, P.; Nenonen, P.; Ahlstrand, R.; Hietanen, O.; Timofeev, B.T.; Bloomin, A.A.

2000-01-01

Mechanical properties and microstructure are studied and compared for two kinds of specimens of cast Ti-stabilized stainless steel 08Kh18N10T used for manufacturing of valves and pumps in nuclear power plants. One set of specimens represents the main gate valve material after 106000 h (∼ 12 years) operation at 270 deg C. The comparison is made with reference specimens in as-fabricated state. The results of impact tests, hardness measurements and microscopic examination show that 12 year operation gives rise to the shift of ductile-brittle transition temperature to higher values (from - 68 deg C - 103 deg C). The microstructure of both materials is similar. The microhardness of δ-ferrite in the steel after long-term operation is slightly higher [ru

Manufacture of tube billets for fuel cans by vacuum centrifugal casting

International Nuclear Information System (INIS)

Zelenskij, V.F.; Neklyudov, I.M.; Chernyj, B.P.

1989-01-01

Vacuum device for induction melting with centrifugal casting in the ingot mold with rotation vertical or horisontal axis is presented. Removing and grinding of nonmetallic inclusions are realized by selection of casting conditions and of chemically active reducer, sound metal with high ductility is obtained. Data on micro- and macrostructure of casted tube billets made of 08Kh18N10T and 06Kh16H15M3B stainless steels, designed for manufacture of fuel cans are presented

Experimental and computational studies of naphthyridine derivatives as corrosion inhibitor for N80 steel in 15% hydrochloric acid

Science.gov (United States)

Ansari, K. R.; Quraishi, M. A.

2015-05-01

The inhibition effect of three naphthyridine derivatives namely 2-amino-4-(4-methoxyphenyl)-1,8-naphthyridine-3-carbonitrile (ANC-1), 2-amino-4-(4-methylphenyl)-1,8-naphthyridine-3-carbonitrile (ANC-2) and 2-amino-4-(3-nitrophenyl)-1,8-naphthyridine-3-carbonitrile (ANC-3) as corrosion inhibitors for N80 steel in 15% HCl by using gravimetric, electrochemical techniques (EIS and potentiodynamic polarization), SEM, EDX and quantum chemical calculation. The order of inhibition efficiency is ANC-1>ANC-2>ANC-3. Potentiodynamic polarization reveals that these inhibitors are mixed type with predominant cathodic control. Studied inhibitors obey the Langmuir adsorption isotherm. The quantum calculation is in good agreement with experimental results.

Structure and phase composition of titanium nitride coating on austenitic steel

International Nuclear Information System (INIS)

Dubovitskaya, N.V.; Kolenchenko, L.D.; Larikov, L.N.

1989-01-01

Structure and phase composition of titanium nitride coating deposited on 08Kh18N10T steel substrate using ''Bulat'' device are studied. Use of complex investigation methods permitted despite small coating thickness (1μm) to aquire information on hardness, porosity, to study phase composition in all coating thickness. The surface layer (∼0.1 μm) consists of ε-Ti 2 N, TiN 0.6 , TiC 0.35 , that is formed with carbon participation from oil vacuum. In more deeper layers beside ε-Ti 2 N TiC 0.14 N 0.77 is present. Effect of carbon diffusion from substrate to forming coating is stated. Gradient of element concentrations in the substrate-coating interface causes recrystallization of austenite

Durability of bends in high-temperature steam lines under the conditions of long-term operation

Science.gov (United States)

Katanakha, N. A.; Semenov, A. S.; Getsov, L. B.

2015-04-01

The article presents the results of stress-strain state computations and durability of bent and steeply curved branches of high-temperature steam lines carried out on the basis of the finite element method using the modified Soderberg formula for describing unsteady creep processes with taking the accumulation of damage into account. The computations were carried out for bends made of steel grades that are most widely used for manufacturing steam lines (12Kh1MF, 15Kh1M1F, and 10Kh9MFB) and operating at different levels of inner pressure and temperature. The solutions obtained using the developed creep model are compared with those obtained using the models widely used in practice.

Estimation of work capacity of welded mounting joints of pipelines of heat resisting steel

International Nuclear Information System (INIS)

Gorynin, I.V.; Ignatov, V.A.; Timofeev, B.T.; Blyumin, A.A.

1982-01-01

The analysis of a work capacity of circular welds made for the Dsub(y)850 pipeline connection with high pressure vessels of heat resisting steel of the 15Kh1NMFA type has been carried out on the base of test results with small samples and real units. Welds were performed using the manual electric arc welding without the following heat treatment. It has been shown that residual stresses in such welds do not produce an essential effect on the resistance of weld metal and heat affected zone on the formation and developments of cracks

Slag inclusions in vacuum-melted ingots of the KhN73MBTYu nickel base alloy

International Nuclear Information System (INIS)

Gorin, V.A.; Kleshchev, A.S.; Kazharskaya, L.P.

1977-01-01

Three types of slag inclusions in ingots of the vacuum-arc-remelted nickel alloy KhN73MBTYu are considered. Type 1 inclusions are those in the surface zone; type 2 inclusions are agglomerations of nitrides and oxides formed due to the fall of lining slag; type 3 inclusions consist of agglomerations of nitrides and oxides as a result of interaction of dissolved oxygen and nitrogen with melt components. The inclusions are removed by machining of the lateral surface. It should be noted that the presence of a large amount of slag on the surface of the molten pool adversely affects the stability of the electrical regime of melting. Strict adherence to the recommendations on the melting and pouring of the initial metal reduces the pollution of the consumable electrode with nonmetallic inclusions

Behavior of helium gas atoms and bubbles in low activation 9Cr martensitic steels

Science.gov (United States)

Hasegawa, Akira; Shiraishi, Haruki; Matsui, Hideki; Abe, Katsunori

1994-09-01

The behavior of helium-gas release from helium-implanted 9Cr martensitic steels (500 appm implanted at 873 K) during tensile testing at 873 K was studied. Modified 9Cr-1Mo, low-activation 9Cr-2W and 9Cr-0.5V were investigated. Cold-worked AISI 316 austenitic stainless steel was also investigated as a reference which was susceptible helium embrittlement at high temperature. A helium release peak was observed at the moment of rupture in all the specimens. The total quantity of helium released from these 9Cr steels was in the same range but smaller than that of 316CW steel. Helium gas in the 9Cr steels should be considered to remain in the matrix at their lath-packets even if deformed at 873 K. This is the reason why the martensitic steels have high resistance to helium embrittlement.

Behavior of helium gas atoms and bubbles in low activation 9Cr martensitic steels

International Nuclear Information System (INIS)

Hasegawa, Akira; Shiraishi, Haruki; Matsui, Hideki; Abe, Katsunori

1994-01-01

The behavior of helium-gas release from helium-implanted 9Cr martensitic steels (500 appm implanted at 873 K) during tensile testing at 873 K was studied. Modified 9Cr-1Mo, low-activation 9Cr-2W and 9Cr-0.5V were investigated. Cold-worked AISI 316 austenitic stainless steel was also investigated as a reference which was susceptible helium embrittlement at high temperature. A helium release peak was observed at the moment of rupture in all the specimens. The total quantity of helium released from these 9Cr steels was in the same range but smaller than that of 316CW steel. Helium gas in the 9Cr steels should be considered to remain in the matrix at their lath-packets even if deformed at 873 K. This is the reason why the martensitic steels have high resistance to helium embrittlement. ((orig.))

Boron content effect on the high-temperature plasticity of corrosion resistant low-carbon austenite type steels

International Nuclear Information System (INIS)

Gol'dshtejn, Ya.E.; Shmatko, M.N.; Chuvatina, S.N.

1976-01-01

With the concept that the state of grain and subgrain boundaries influences the hot plasticity of corrosion resistant steel as a starting point, the study was undertaken of the effect of boron microalloying up on the intergranular strength and of the action boron exerts upon the distribution (redistribution) of other phases present in austenitic 03Kh16N14M3 steels. An electron microscope study of the composition of redundant phases and that of the fine structure of steel have shown the effect of small additions of boron upon the hot plasticity of steel to be linked directly to its influence upon austenite disintegration and the precipitation along the boundaries of crystals of redundant phases in the course of hot plastic deformation. The action of boron upon the process plasticity of steel depends on the temperature and the rate of deformation which govern the kinetics of the precipitation of the redundant phases

SEEING THROUGH THE RING: NEAR-INFRARED PHOTOMETRY OF V582 MON (KH 15D)

Energy Technology Data Exchange (ETDEWEB)

Arulanantham, Nicole A.; Herbst, William [Astronomy Department, Wesleyan University, Middletown, CT 06459 (United States); Cody, Ann Marie [NASA Ames Research Center, Moffett Field, CA 94035 (United States); Stauffer, John R.; Rebull, Luisa M. [Spitzer Science Center, California Institute of Technology, Pasadena, CA 91125 (United States); Agol, Eric; Windemuth, Diana [Department of Astronomy, University of Washington, Seattle, WA 98195-1580 (United States); Marengo, Massimo [Department of Physics and Astronomy, Iowa State University, Ames, IA 50011 (United States); Winn, Joshua N. [Department of Physics and Kavli Institute for Astrophysics and Space Research, Massachusetts Institute of Technology, Cambridge, MA 02139 (United States); Hamilton, Catrina M. [Physics and Astronomy Department, Dickinson College, Carlisle, PA 17013 (United States); Mundt, Reinhard [Max Planck Institute for Astronomy, D-69117 Heidelberg (Germany); Johns-Krull, Christopher M. [Department of Physics and Astronomy, Rice University, Houston, TX 77005 (United States); Gutermuth, Robert A. [Department of Astronomy, University of Massachusetts, Amherst, MA 01002 (United States)

2016-04-15

We examine the light and color evolution of the T Tauri binary KH 15D through photometry obtained at wavelengths between 0.55 and 8.0 μm. The data were collected with A Novel Dual Imaging CAMera (ANDICAM) on the 1.3 m SMARTS telescope at Cerro-Tololo Inter-American Observatory and with InfraRed Array Camera on the Spitzer Space Telescope. We show that the system’s circumbinary ring, which acts as a screen that covers and uncovers different portions of the binary orbit as the ring precesses, has reached an orientation where the brighter component (star B) fully or nearly fully emerges during each orbital cycle. The fainter component (star A) remains fully occulted by the screen at all phases. The leading and trailing edges of the screen move across the sky at the same rate of ∼15 m s{sup −1}, consistent with expectation for a ring with a radius and width of ∼4 au and a precession period of ∼6500 years. Light and color variations continue to indicate that the screen is sharp edged and opaque at VRIJH wavelengths. However, we find an increasing transparency of the ring edge at 2.2, 3.6, and 4.5 μm. Reddening seen at the beginning of the eclipse that occurred during the CSI 2264 campaign particularly suggests selective extinction by a population of large dust grains. Meanwhile, the gradual bluing observed while star B is setting is indicative of forward scattering effects at the edge of the ring. The spectral energy distribution of the system at its bright phase shows no evidence of infrared excess emission that can be attributed to radiation from the ring or other dust component out to 8 μm.

On the nature of anomalies in temperature dependence of the OKh18N1OT steel yield strength after thermal cycling in the low temperature range

International Nuclear Information System (INIS)

Medvedev, E.M.; Lavrent'ev, F.F.; Kurmanova, T.N.

1978-01-01

Investigated were structural transformations in 0Kh18N10T steel as a result of heating and cooling and of deformation within the range of temperatures between 300 and 77 K, the quantity relationships between the said transformations and the variation of the yield limit with the temperature. The studies were conducted by metallography and mechanical test methods. It was shown that an increase in the number of heating and cooling cycles correlates with a loss in strength of the steel while deformation at 77 K. This anomaly in the temperature relationship of the yield limit is related to the appearance in the course of deformation of α-martensite with a BCC lattice. Deformation at 300 K increases the amount ea of epsilon-martensite, a decrses the effectve size of grain and, in consequence, increases the yield limit. The relationship between the yield limit and the grain size at the temperature of 300 K is described adequately by the Hall-Petch equation

Effect of smelting method on the austenite grain size and properties of heat-resisting pearlitic steel

International Nuclear Information System (INIS)

Balakhovskaya, M.B.; Khusainova, N.A.; Davlyatova, L.N.

1975-01-01

Influence of smelting method on austenite grain size and properties of refractory perlite steel were studied. An opportunity was found to increase the steel refractoriness without deteriorating its other properties. The steel 12Kh1MF of electric or common open-hearth smelting was used. The dependence of kinetics of austenite grain growth on the smelting method was studied in the temperature range 950 deg - 1200 deg C with 1 hour exposure. The grain size of austenite in steel is supposedly determined by aluminium nitrides and vanadium carbides. In tests of normalized (kept for 20 minutes at 950-980 deg C) and tempered (kept for 3 hours at 730 deg C) transverse (tangential) pipe cross-section samples the electric steel had higher impact viscosity than the open-hearth metal. At working temperatures (540 deg -580 deg C) the difference in viscosity has its minimum. Viscosity of both steels 12Kh1MF begins to sharply decrease from 20 deg C. However, electric steel has rather high viscosity even at - 40 deg C, while the open-hearth one becomes brittle as early as at - 20 deg C. Long-term strength tests at 580 deg C under stresses 10-14 kG/mm 2 show that the coarse-grain steel is more refractory, i.e. time till fracture of open-hearth steel samples is twice as long as that of electric steel samples

Irradiation hardening of Mod.9Cr-1Mo steel

International Nuclear Information System (INIS)

Ryu, Woo-Seog; Kim, Sung-Ho; Choo, Kee-Nam; Kim, Do-Sik

2009-01-01

An irradiation test of Mod.9Cr-1Mo steel was carried out in the OR5 test hole of HANARO of a 30 MW thermal power at 390±10degC up to a fast neutron fluence of 4.4x10 19 (n/cm 2 ) (E > 1.0 MeV). The dpa of the irradiated specimens was evaluated to be 0.034 - 0.07. Tensile and impact tests of the irradiated Mod.9Cr-1Mo were done in the hot cell of the IMEF. The change of the tensile strength by irradiation was similar to the change of the yield strength. The increase of the yield and tensile strengths was up to 18% and 10% respectively. The elongation reduction of the weldment was up to 65%. (author)

Stress corrosion cracking properties of 15-5PH steel

Science.gov (United States)

Rosa, Ferdinand

1993-01-01

Unexpected occurrence of failures, due to stress corrosion cracking (SCC) of structural components, indicate a need for improved characterization of materials and more advanced analytical procedures for reliably predicting structures performance. Accordingly, the purpose of this study was to determine the stress corrosion susceptibility of 15-5PH steel over a wide range of applied strain rates in a highly corrosive environment. The selected environment for this investigation was a highly acidified sodium chloride (NaCl) aqueous solution. The selected alloy for the study was a 15-5PH steel in the H900 condition. The slow strain rate technique was selected to test the metals specimens.

Fundamental modelling of particle strengthened 9-12% Cr steels

Energy Technology Data Exchange (ETDEWEB)

Magnusson, Hans; Sandstroem, Rolf [Royal Inst. of Tech., Stockholm (Sweden). Dept. of Materials Science and Engineering; Royal Inst. of Tech., Stockholm (Sweden). Brinell Centre

2010-07-01

Creep strength of particle strengthened 9-12% Cr steels can be predicted by fundamental modelling. The creep strength is evaluated from the state of the microstructure during creep. Particle hardening at high temperatures can be predicted by taking dislocation climb across particles into account. Work hardening is calculated from immobile dislocations in subgrain interiors and at boundaries using the composite theory. Subgrain coarsening will lower the influence of the mechanically hard boundaries. Recovery in dislocation density is predicted through static recovery by climb and dynamic recovery by locking and dipole formation. Solid solution hardening is needed in order to explain the difference in creep strength between different 9-12% Cr steels. The accumulation of large atoms such as Mo and W will slow down the dislocation climb velocity, and thereby the microstructure recovery rate. 100000h rupture strength is predicted for X20, P91, P92 steels without any use of fitting parameters. The creep strength of P91 steel with different microstructure due to Al additions. Z-phase transformation and heat affected material is presented. (orig.)

Development of ferritic steels for fusion reactor applications

Energy Technology Data Exchange (ETDEWEB)

Klueh, R.L.; Maziasz, P.J.; Corwin, W.R.

1988-08-01

Chromium-molybdenum ferritic (martensitic) steels are leading candidates for the structural components for future fusion reactors. However, irradiation of such steels in a fusion environment will produce long-lived radioactive isotopes that will lead to difficult waste-disposal problems. Such problems could be reduced by replacing the elements in the steels (i.e., Mo, Nb, Ni, N, and Cu) that lead to long-lived radioactive isotopes. We have proposed the development of ferritic steels analogous to conventional Cr-Mo steels, which contain molybdenum and niobium. It is proposed that molybdenum be replaced by tungsten and niobium be replaced by tantalum. Eight experimental steels were produced. Chromium concentrations of 2.25, 5, 9, and 12% were used (all concentrations are in wt %). Steels with these chromium compositions, each containing 2% W and 0.25% V, were produced. To determine the effect of tungsten and vanadium, 2.25 Cr steels were produced with 2% W and no vanadium and with 0.25% V and O and 1% W. A 9Cr steel containing 2% W, 0.25 V, and 0.07% Ta was also studied. For all alloys, carbon was maintained at 0.1%. Tempering studies on the normalized steels indicated that the tempering behavior of the new Cr-W steels was similar to that of the analogous Cr-Mo steels. Microscopy studies indicated that 2% tungsten was required in the 2.25 Cr steels to produce 100% bainite in 15.9-mm-thick plate during normalization. The 5Cr and 9Cr steels were 100% martensite, but the 12 Cr steel contained about 75% martensite with the balance delta-ferrite. 33 refs., 35 figs., 5 tabs.

Development of ferritic steels for fusion reactor applications

International Nuclear Information System (INIS)

Klueh, R.L.; Maziasz, P.J.; Corwin, W.R.

1988-08-01

Chromium-molybdenum ferritic (martensitic) steels are leading candidates for the structural components for future fusion reactors. However, irradiation of such steels in a fusion environment will produce long-lived radioactive isotopes that will lead to difficult waste-disposal problems. Such problems could be reduced by replacing the elements in the steels (i.e., Mo, Nb, Ni, N, and Cu) that lead to long-lived radioactive isotopes. We have proposed the development of ferritic steels analogous to conventional Cr-Mo steels, which contain molybdenum and niobium. It is proposed that molybdenum be replaced by tungsten and niobium be replaced by tantalum. Eight experimental steels were produced. Chromium concentrations of 2.25, 5, 9, and 12% were used (all concentrations are in wt %). Steels with these chromium compositions, each containing 2% W and 0.25% V, were produced. To determine the effect of tungsten and vanadium, 2.25 Cr steels were produced with 2% W and no vanadium and with 0.25% V and O and 1% W. A 9Cr steel containing 2% W, 0.25 V, and 0.07% Ta was also studied. For all alloys, carbon was maintained at 0.1%. Tempering studies on the normalized steels indicated that the tempering behavior of the new Cr-W steels was similar to that of the analogous Cr-Mo steels. Microscopy studies indicated that 2% tungsten was required in the 2.25 Cr steels to produce 100% bainite in 15.9-mm-thick plate during normalization. The 5Cr and 9Cr steels were 100% martensite, but the 12 Cr steel contained about 75% martensite with the balance delta-ferrite. 33 refs., 35 figs., 5 tabs

Design of the WWER-440 pressurizer

International Nuclear Information System (INIS)

Bednarek, L.

1978-01-01

The main specifications are presented of a pressurizer for the WWER-440 reactor as are factors securing operating reliability and the required life of the equipment. Ferritic-pearlite steel 22K is the basic material for the manufacture of the shell, support and couplings. The internal parts and the heads are manufactured from the 08KH18N10T chromium-nickel austenitic steel, the bolts and nuts of manholes from chromium-molybdenum steels 25KH1MF and 25KH2MFA. Quality testing of basic materials and quality control during the process of manufacture are briefly described. (Z.M.)

Dr. Yu Wang, Director, Natural Science Division, National Science Council, Taiwan

CERN Document Server

Patrice Loïez

2001-01-01

Photo 01: L. to r.: Dr. Philippe Bloch, CERN CMS ECAL Deputy Project Manager, Dr. Yu Wang, Dr. Etiennette Auffray, CERN, responsible of the CERN ECAL Regional Centre. Photo 02: L. to r.: Dr. Yu Wang, Dr. Philippe Bloch, Dr. Apollo GO, National Central University, Taiwan, Dr. Etiennette Auffray.

Influence of prolonged service of steam turbines on the properties of materials of rotor and vessel components

International Nuclear Information System (INIS)

Anfimov, V.M.; Artamonov, V.V.; Chizhik, T.A.

1984-01-01

The structure and mechanical properties of steam turbine elements of 25Kh1MF, 25Kh1M1FA (rotors), 15Kh1M1FL (vessel components) steels have been investigated both in initial state and after 200 000 h operation. The structure stability and phase composition of rotor steels providing conservation of heat resistance at a required level was established. Examination of vessel components showed a decrease in the yield strength by 15-20% and durability - by 10% as compared to initial ones. The conclusion on a possible prolongation of the steam turbine service life to 200 000 h is drawn. The nominal service life equals 100 000 h

The influence of heating rate on reheat-cracking in a commercial 2 1/4Cr1Mo steel

International Nuclear Information System (INIS)

Hippsley, C.A.

1983-03-01

The effects of elevated heating rate on stress-relief cracking in a commercial 2 1/4 Cr1Mo steel have been investigated. A SEN bend-specimen stress-relaxation test was used to assess reheat cracking susceptibility and fracture mechanisms for an initial post-weld heating rate of 1000 Kh - 1 . Two factors controlling the influence of heating rate on the final severity of cracking were identified, i.e. the rate of stress-relaxation with respect to temperature, and the time available for crack-growth. The factors were found to counteract each other, but in the case of commercial 2 1/4 Cr1Mo steel, the crack-growth factor outweighed the relaxation factor, resulting in a reduction in the propensity to stress-relief cracking at the elevated heating rate. However, by reference to the results of a separate investigation concerning A508/2 MnMoNiCr steel it was demonstrated that the balance between these two factors may be reversed in other alloy systems, with the consequence that reheat cracking is exacerbated by increasing the initial heating rate. A computer model was addressed to the stress-relaxation test conditions using data from the commercial 2 1/4 Cr1Mo steel. The model predictions exhibited reasonable agreement with experimental test results for both 100 Kh - 1 and 1000 Kh - 1 heating rates. (author)

PREFACE: SANS-YuMO User Meeting at the Start-up of Scientific Experiments on the IBR-2M Reactor: Devoted to the 75th anniversary of Yu M Ostanevich's birth

Science.gov (United States)

Gordely, Valentin; Kuklin, Alexander; Balasoiu, Maria

2012-03-01

The Second International Workshop 'SANS-YuMO User Meeting at the Start-up of Scientific Experiments on the IBR-2M Reactor', devoted to the 75th anniversary of the birth of Professor Yu M Ostanevich (1936-1992), an outstanding neutron physicist and the founder of small-angle neutron scattering (field, group, and instrument) at JINR FLNPh, was held on 27-30 May at the Frank Laboratory of Neutron Physics. The first Workshop was held in October 2006. Research groups from different neutron centers, universities and research institutes across Europe presented more than 35 oral and poster presentations describing scientific and methodological results. Most of them were obtained with the help of the YuMO instrument before the IBR-2 shutdown in 2006. For the last four years the IBR-2 reactor has been shut down for refurbishment. At the end of 2010 the physical launch of the IBR-2M reactor was finally realized. Nowadays the small-angle neutron scattering (SANS) technique is applied to a wide range of scientific problems in condensed matter, soft condensed matter, biology and nanotechnology, and despite the fact that there are currently over 30 SANS instruments in operation worldwide at both reactor and spallation sources, the demand for beam-time is considerably higher than the time available. It must be remembered, however, that as the first SANS machine on a steady-state reactor was constructed at the Institute Laue Langevin, Grenoble, the first SANS instrument on a 'white' neutron pulsed beam was accomplished at the Joint Institute for Nuclear Research at the IBR-30 reactor, beamline N5. During the meeting Yu M Ostanevich's determinative and crucial contribution to the construction of spectrometers at the IBR-2 high-pulsed reactor was presented, as well as his contribution to the development of the time-of-flight (TOF) small-angle scattering technique, and a selection of other scientific areas. His leadership and outstanding scientific achievements in applications of the

Damage development in 9%Cr steels

International Nuclear Information System (INIS)

Rauch, M.; Maile, K.

2003-01-01

Modern 9-11% martensitic steels are candidate materials to be used in modern fossil fired power plants with high efficiency rates. The focus of the R and D work is put on the further development and optimisation, the determination of material characteristics but also on the identification and quantification of damage mechanisms and the damage evolution. For this purpose extensive experiments such as long creep tests on specimens under internal pressure, metallurgical examinations and theoretical investigations for determination of stress-strain state which have been conducted. The laboratory tests are completed by examination of real components. As a result an empirical description of the creep cavity density as a function of deformation and multiaxiality of stress state has been carried out which can be used in further FE-calculations determining the damage state. The results of all metallographical examinations on specimens with different heat treatments and service loads are summarised in a structure atlas and are published for further usage. Damage development, martensitic 9 % Cr steels, creep cavity density, creep tests under multiaxial load, metallographical investigations, and measurements on pipe bends. (author)

Heat treatment effects on structure and proerties of the alloy type KhN73MBNYu (EhJ 698)

International Nuclear Information System (INIS)

Maslenkov, S.B.; Maslenkova, E.A.; Solov'ev, Yu.V.; Zryumov, V.P.

1994-01-01

Influence of quenching temperature and various ageing conditions on tensile properties and impact strength of wrought alloy type KhN73MBTYu has been investigated at room temperature and in the range of 500-850 deg C. Two-step quenching followed by ageing at 700-750 deg C. Two-step quenching followed by ageing at 700-750 deg C is shown to assure needed heat resistance of the alloy. Due to the whole complex of structural changes during heat treatments mechanical properties of the alloy preserv high level up to 750 deg C. This temperature is limiting value in the case of long-term operation

[Autobiography of modern acupuncturist Yu Shu-zhuang].

Science.gov (United States)

Li, Jia-jian' i; Guo, Jing; Yu, Zhen-zhong; Wang, Lin-peng

2014-11-01

Professor YU Shu-zhuang is a distinguished acupuncturist in China. He has practiced the TCM acupuncture-moxibustion clinical, educational and scientific research for 60 years in his life. In clinic, he summarized the experiences "five-ming first"; in treatment, he insisted "dredging" and "regulating", protecting the function of spleen and stomach, and needles should be less but specific. In the meanwhile, he made a deep study on the function and clinical effects of specific acupoints, and used the research results of propagated sensation along channel to guide clinical treatment, forming his special academic points. Professor YU has educated a great number of acupuncture-moxibustion talents in China and foreign countries, making great contribution to the popularization of acupuncture-moxibustion in the worldwide.

The structure of the alphinizing coat on alloy steels

Directory of Open Access Journals (Sweden)

S. Pietrowski

2008-12-01

Full Text Available In this paper results of the structure of the coat alphinizing in AlSi5 silumin on alloy steels: acid-proof 1H18N9T (X6CrNiTi18-10 and high speed SW18 (HS18-0-1 were presented. The temperature of the alphinizing bath was amounts to750±5°C, and immersion time of the element τ = 180s. It was shown, that there is the different “g” coat thickness on testing steels. On the 1H18N9T steel it amounts to g = 52μm, and on the SW18 steel – g = 203μm. Regardless of a grade of testing alloy steels the coat consist of three layers with diversified phasic structure. There is different chemical composition of coat layers on testing steels. The first layer from the base consist of AlFe phase containing alloy addictions of steels: Cr and Ni (1H18N9T and W, V and Cr (SW18. On this layer crystallize the second layer of intermetallic phases. It is the phase containing the main alloy addiction of steels: AlFeCr (1H18N9T and AlFeW (SW18. The last, outside layer consist of silumin containing AlFeNi intermetallic phases on the 1H18N9T steel and AlFeW on the SW18 steel. Regardless of the grade of testing steels there is Si element in all layers of the coat. There are morphological differences in tested layers. The second layer (AlFeW phase inside the coat on the SW18 steel consist of faced crystals growing into in outside silumin layer. On the 1H18N9T steel a boundary between transient and outside layer is more uniform. Free separations of intermetallic phases inside silumin layer on the 1H18N9T steel have lamellar and on the SW18 steel – faced form.

Elevated temperature tensile properties of P9 steel towards ferritic steel wrapper development for sodium cooled fast reactors

Energy Technology Data Exchange (ETDEWEB)

Choudhary, B.K., E-mail: bkc@igcar.gov.in; Mathew, M.D.; Isaac Samuel, E.; Christopher, J.; Jayakumar, T.

2013-11-15

Tensile deformation and fracture behaviour of the three developmental heats of P9 steel for wrapper applications containing varying silicon in the range 0.24–0.60% have been examined in the temperature range 300–873 K. Yield and ultimate tensile strengths in all the three heats exhibited gradual decrease with increase in temperature from room to intermediate temperatures followed by rapid decrease at high temperatures. A gradual decrease in ductility to a minimum at intermediate temperatures followed by an increase at high temperatures has been observed. The fracture mode remained transgranular ductile. The steel displayed signatures of dynamic strain ageing at intermediate temperatures and dominance of recovery at high temperatures. No significant difference in the strength and ductility values was observed for varying silicon in the range 0.24–0.60% in P9 steel. P9 steel for wrapper application displayed strength and ductility values comparable to those reported in the literature.

Elevated temperature tensile properties of P9 steel towards ferritic steel wrapper development for sodium cooled fast reactors

Science.gov (United States)

Choudhary, B. K.; Mathew, M. D.; Isaac Samuel, E.; Christopher, J.; Jayakumar, T.

2013-11-01

Tensile deformation and fracture behaviour of the three developmental heats of P9 steel for wrapper applications containing varying silicon in the range 0.24-0.60% have been examined in the temperature range 300-873 K. Yield and ultimate tensile strengths in all the three heats exhibited gradual decrease with increase in temperature from room to intermediate temperatures followed by rapid decrease at high temperatures. A gradual decrease in ductility to a minimum at intermediate temperatures followed by an increase at high temperatures has been observed. The fracture mode remained transgranular ductile. The steel displayed signatures of dynamic strain ageing at intermediate temperatures and dominance of recovery at high temperatures. No significant difference in the strength and ductility values was observed for varying silicon in the range 0.24-0.60% in P9 steel. P9 steel for wrapper application displayed strength and ductility values comparable to those reported in the literature.

Elevated temperature tensile properties of P9 steel towards ferritic steel wrapper development for sodium cooled fast reactors

International Nuclear Information System (INIS)

Choudhary, B.K.; Mathew, M.D.; Isaac Samuel, E.; Christopher, J.; Jayakumar, T.

2013-01-01

Tensile deformation and fracture behaviour of the three developmental heats of P9 steel for wrapper applications containing varying silicon in the range 0.24–0.60% have been examined in the temperature range 300–873 K. Yield and ultimate tensile strengths in all the three heats exhibited gradual decrease with increase in temperature from room to intermediate temperatures followed by rapid decrease at high temperatures. A gradual decrease in ductility to a minimum at intermediate temperatures followed by an increase at high temperatures has been observed. The fracture mode remained transgranular ductile. The steel displayed signatures of dynamic strain ageing at intermediate temperatures and dominance of recovery at high temperatures. No significant difference in the strength and ductility values was observed for varying silicon in the range 0.24–0.60% in P9 steel. P9 steel for wrapper application displayed strength and ductility values comparable to those reported in the literature

The rate(time)- dependent mechanical behavior modified 9Cr-1Mo steel, 3

International Nuclear Information System (INIS)

Moosbrugger, J.C.

1991-01-01

In this paper, constitutive equations are presented for the nonisothermal small strain behavior of modified 9Cr-1Mo steel between 25degC - 600degC. The basic framework uses the superposition of nonlinear kinematic hardening rules as proposed by Chaboche and coworkes. A framework for accounting for isotropic softening is presented wherein this softening can be included in a drag stress, in a yield stress or as a decrease in the saturation level of kinematic hardening or some combination of these; a single isotropic softening equation is used as determined from experiments. The behavior of modified 9Cr-1Mo steel between 25degC - 600degC has been investigated by Swindeman, and Majors et. al. and many important features have been discussed. Here, model parameters are determined from available isothermal uniaxial data and some correlations with isothermal and nonisothermal tests are presented. (J.P.N.)

Investigation of fretting corrosion of vacuum-chrome-plated vt3-1 titanium alloy in pair with unprotected vt3-1 alloy and 40khnma steel

International Nuclear Information System (INIS)

Rojkh, I.L.; Koltunova, L.N.; Vejtsman, M.G.; Birman, Ya.N.; Skosarev, A.V.; Kogan, I.S.

1978-01-01

The character of destruction of contacting surfaces in the process of fretting corrosion of titanium alloy VT3-1 chromized in vacuum in pair with unprotected alloy VT3-1 and steel 40KhNMA has been studied by scanning electron microscopy, electronography, and recording the surface profile. The specific load was 200 kg/cm 2 , vibration amplitude 50 mkm and frequency 500 Hz. It has been established that pairs unprotected with coating are subjected to intensive fretting corrosion especially when they are made of titanium alloy. For the pair chromized alloy VT3-1 - unprotected alloy VT3-1 no destruction of a chromized surface is observed. Vacuum chromium coating in the pair with steel 40KhNMA reveals similar properties as in pair with a titanium alloy. The surface of a steel sample is destroyed because of fretting corrosion, though the intensity of corrosion is lower than in the case of unprotected pairs. Vacuum chromium coating is recommended for protection of titanium alloy VT3-1 from fretting corrosion in pair with steel 40KhNMA or an alloy VT3-1 especially in those cases when various organic coatings are unsuitable

On abnormal decomposition of supercooled austenite in carbon and alloy steels

International Nuclear Information System (INIS)

Parusov, V.V.; Dolzhenkov, I.I.; Podobedov, L.V.; Vakulenko, I.A.

1980-01-01

Residual stresses which appear as a result of thermal cycling in the temperature range of 300-700 deg C are investigated in an austenitic class steel (03Kh18N11) to ground the assumption on the effect of plastic deformation, appearing due to thermal stresses, on the mechanism of supercooled austenite decomposition. The determination of residual stresses is carried out with the help of X-ray diffraction analysis. It is established that the deformation brings about an increase in density of dislocation the interaction of which leads to the formation of a typical austenite substructure which conditions the proceeding of the eutectoid transformation according to an abnormal mechanism. It is noted, that the grain pearlite formation due to plastic and microplastic deformation of supercooled austenite induced by thermal stresses should be taken into account when developing steel heat treatment shedules [ru

Alloy spreading and filling of gaps in brazing of VDU-2 and KhN50VMTYuB heat resistant nickel alloys with VPr3K and VPr10 alloys

International Nuclear Information System (INIS)

Shapiro, A.E.; Podol'skij, B.A.; Lepisko, M.R.; Borzyak, A.G.; Moryakov, V.F.; Rostislavskaya, T.T.

1984-01-01

A study was made on contact interaction of VDU-2 and KhN50VMTYuB alloys with VPr3K and VPr10 alloys at 1325 and 1220 deg C in argon and industrial vacuum. The contact angles and wettability indexes were determined. The solders fill the vertical gaps of up to 0.25 mm width through 80 mm height. Spreading and filling of gaps proceeds better during soldering in argon with boron trifluoride addition as compared to soldering in industrial vacuum. VPr10 alloy is divided into two phases when wetting KhN50VMTYuB alloy: fusible one on the base of nickel-chromium-manganese solution and infusible one on the base of nickel-niobium eutectics. The square of fusible phase spreading is 2.5...3 times larger as compared to infusible one

Gas metal arc weldability of 1.5 GPa grade martensitic steels

Science.gov (United States)

Hwang, Insung; Yun, Hyeonsang; Kim, Dongcheol; Kang, Munjin; Kim, Young-Min

2018-01-01

The gas metal arc weldability of 1.5 GPa grade martensitic (MART) steel was evaluated using both inverter direct current (DC) and DC pulse power type welders, under conditions of different welding currents, welding speeds, and shielding gasses. By investigating the bead appearance, tensile strength, and arc stability, it was determined that DC pulse power is better than inverter DC power for arc welding of 1.3 mm thick 1.5 GPa grade MART steel. Further, from the results of the weldability for various shielding gases, it was determined that mixed shielding gas is more effective for welding 1.5 GPa grade MART steel than is pure inert gas (Ar) or active (CO2) gas. In the case of pure shielding gas, no sound bead was formed under any conditions. However, when the mixed shielding gas was used, sound and fine beads were obtained.

Effect of smelting method on the austenite grain size and properties of heat-resisting pearlitic steel

Energy Technology Data Exchange (ETDEWEB)

Balakhovskaya, M B; Khusainova, N A; Davlyatova, L N [Vsesoyuznyj Nauchno-Issledovatel' skij Teplotekhnicheskij Inst., Moscow (USSR)

1975-12-01

Influence of smelting method on austenite grain size and properties of refractory perlite steel were studied. An opportunity was found to increase the steel refractoriness without deteriorating its other properties. The steel 12Kh1MF of electric or common open-hearth smelting was used. The dependence of kinetics of austenite grain growth on the smelting method was studied in the temperature range 950 deg - 1200 deg C with 1 hour exposure. The grain size of austenite in steel is supposedly determined by aluminium nitrides and vanadium carbides. In tests of normalized (kept for 20 minutes at 950-980 deg C) and tempered (kept for 3 hours at 730 deg C) transverse (tangential) pipe cross-section samples the electric steel had higher impact viscosity than the open-hearth metal. At working temperatures (540 deg -580 deg C) the difference in viscosity has its minimum. Viscosity of both steels 12Kh1MF begins to sharply decrease from 20 deg C. However, electric steel has rather high viscosity even at /sup -/40 deg C, while the open-hearth one becomes brittle as early as at /sup -/20 deg C. Long-term strength tests at 580 deg C under stresses 10-14 kG/mm/sup 2/ show that the coarse-grain steel is more refractory, i.e. time till fracture of open-hearth steel samples is twice as long as that of electric steel samples.

15 CFR 9.9 - Consumer education.

Science.gov (United States)

2010-01-01

... 15 Commerce and Foreign Trade 1 2010-01-01 2010-01-01 false Consumer education. 9.9 Section 9.9 Commerce and Foreign Trade Office of the Secretary of Commerce PROCEDURES FOR A VOLUNTARY LABELING PROGRAM FOR HOUSEHOLD APPLIANCES AND EQUIPMENT TO EFFECT ENERGY CONSERVATION § 9.9 Consumer education. The...

Room and elevated temperature Mechanical Behavior of 9-12% Cr Steels

Energy Technology Data Exchange (ETDEWEB)

Dogan, Omer N.; Hawk, Jeffrey A.; Schrems, Karol K.

2005-02-01

The mechanical properties of medium Cr steels used in fossil fired power plants are very good because of their excellent high temperature microstructural stability. However, as the desire to increase the operating temperature (>650C) of the plant goes up, the need for steels that maintain their strength at these temperatures also increases. The mechanical properties of three medium Cr steels (0.08C-(9-12)Cr-1.2Ni-0.7Mo-3.0Cu-3.0Co-0.5Ti) were investigated through hardness, hot hardness and tensile measurements. The strength of the 9-12%Cr steels at room temperature after long-term isothermal aging (750C; 1000 hours) compares favorably with that of other power plant steels (e.g., P91). In addition, the elevated temperature strength and hot hardness also behave similarly. The mechanical behavior will be discussed in terms of the strength, elongation and tensile fracture characteristics.

The influence of grain size on the strain-induced martensite formation in tensile straining of an austenitic 15Cr–9Mn–Ni–Cu stainless steel

International Nuclear Information System (INIS)

Kisko, A.; Misra, R.D.K.; Talonen, J.; Karjalainen, L.P.

2013-01-01

In order to improve understanding on the behavior of ultrafine-grained austenitic stainless steels during deformation, the influence of the austenite grain size and microstructure on the strain-induced martensite transformation was investigated in an austenitic 15Cr–9Mn–Ni–Cu (Type 204Cu) stainless steel. By different reversion treatments of the 60% cold-rolled sheet, varying grain sizes from ultrafine (0.5 μm), micron-scale (1.5 μm), fine (4 μm) to coarse (18 μm) were obtained. Some microstructures also contained a mixture of ultrafine or micron-scale and coarse initially cold-worked austenite grains. Samples were tested in tensile loading and deformation structures were analyzed after 2%, 10% and 20% engineering strains by means of martensite content measurements, scanning electron microscope together with a electron backscatter diffraction device and transmission electron microscope. The results showed that the martensite nucleation sites and the rate of transformation vary. In ultrafine grains strain-induced α′-martensite nucleates at grain boundaries and twins, whereas in coarser grains as well as in coarse-grained retained austenite, α′-martensite formation occurs at shear bands, sometimes via ε-martensite. The transformation rate of strain-induced α′-martensite decreases with decreasing grain size to 1.5 μm. However, the rate is fastest in the microstructure containing a mixture of ultrafine and retained cold-worked austenite grains. There the ultrafine grains transform quite readily to martensite similarly as the coarse retained austenite grains, where the previous cold-worked microstructure is still partly remaining

Effect of Cu addition on microstructure and mechanical properties of 15%Cr super martensitic stainless steel

International Nuclear Information System (INIS)

Ye, Dong; Li, Jun; Jiang, Wen; Su, Jie; Zhao, Kunyu

2012-01-01

Highlights: ► Cu contributes to refine the grains. ► Cu solutes in matrix under quenching and precipitates as ε-Cu during tempering. ► Cu promotes the kinetics of reversed austenite formation. ► Mechanical properties are significantly influenced by austenite amount. ► Cu alloyed super martensitic stainless steel exhibits greatly improved mechanical properties. -- Abstract: The effect of adding different content of Cu (0 wt.%, 1.5 wt.% and 3 wt.%) to the 15%Cr super martensitic stainless steel (SMSS) was investigated using optical microscope, scanning electron microscope (SEM), transmission electron microscope (TEM) and X-ray diffraction (XRD). Its consequence on mechanical properties was examined to clarify the role of Cu in the tested steels. The experimental results indicate that the microstructures of three tested steels are tempered martensite, retained austenite and reversed austenite; two kinds of austenites are dispersedly distributed among martensite matrix. Cu can solute in matrix under quenching condition and can precipitate as Cu-rich nanometer phase (ε-Cu) during tempering. Cu is helpful for the grain refinement and to promote the formation of reversed austenite during tempering. The maximum volume fraction of austenite is 55.9% in the steel with 3 wt.% Cu, which is responsible for the improvement of ductility. The results of the mechanical properties tests reveal that the mechanical properties are significantly influenced by the volume fraction of austenite. Cu can cause solid solution strengthening, precipitation strengthening and grain refinement strengthening in SMSS. Cu alloyed super martensitic stainless steel exhibits greatly improved mechanical properties.

Influence of thermo-mechanical treatment on the tensile properties of a modified 14Cr–15Ni stainless steel

Energy Technology Data Exchange (ETDEWEB)

Vijayanand, V.D., E-mail: vdvijayanand@igcar.gov.in; Laha, K.; Parameswaran, P.; Nandagopal, M.; Panneer Selvi, S.; Mathew, M.D.

2014-10-15

The titanium modified 14Cr–15Ni austenitic stainless steel is used as clad and wrapper material for fast breeder nuclear reactor. Thermo-mechanical treatments consisting of solution annealing at two different temperatures of 1273 and 1373 K followed by cold-work and thermal ageing have been imparted to the steel to tailor its microstructure for enhancing strength. Tensile tests have been carried out on the thermo-mechanically treated steel at nominal strain rate of 1.6 × 10{sup −4} s{sup −1} over a temperature range of 298–1073 K. The yield stress and the ultimate tensile strength of the steel increased with increase in solution treatment temperature and this has been attributed to the fine and higher density of Ti(C,N) precipitate. Tensile flow behaviour of the steel has been analysed using Ludwigson and Voce constitutive equations. The steel heat treated at higher solution temperature exhibited earlier onset of cross slip during tensile deformation. The rate of recovery at higher test temperatures was also influenced by variations in solution heat treatment temperature. In addition, dynamic recrystallization during tensile deformation at higher temperatures was profound for steel solution heat-treated at lower temperature. The differences in flow behaviour and softening mechanisms during tensile testing of the steel after different heat treated conditions have been attributed to the nature of Ti(C,N) precipitation.

Influence of thermo-mechanical treatment on the tensile properties of a modified 14Cr–15Ni stainless steel

International Nuclear Information System (INIS)

Vijayanand, V.D.; Laha, K.; Parameswaran, P.; Nandagopal, M.; Panneer Selvi, S.; Mathew, M.D.

2014-01-01

The titanium modified 14Cr–15Ni austenitic stainless steel is used as clad and wrapper material for fast breeder nuclear reactor. Thermo-mechanical treatments consisting of solution annealing at two different temperatures of 1273 and 1373 K followed by cold-work and thermal ageing have been imparted to the steel to tailor its microstructure for enhancing strength. Tensile tests have been carried out on the thermo-mechanically treated steel at nominal strain rate of 1.6 × 10 −4 s −1 over a temperature range of 298–1073 K. The yield stress and the ultimate tensile strength of the steel increased with increase in solution treatment temperature and this has been attributed to the fine and higher density of Ti(C,N) precipitate. Tensile flow behaviour of the steel has been analysed using Ludwigson and Voce constitutive equations. The steel heat treated at higher solution temperature exhibited earlier onset of cross slip during tensile deformation. The rate of recovery at higher test temperatures was also influenced by variations in solution heat treatment temperature. In addition, dynamic recrystallization during tensile deformation at higher temperatures was profound for steel solution heat-treated at lower temperature. The differences in flow behaviour and softening mechanisms during tensile testing of the steel after different heat treated conditions have been attributed to the nature of Ti(C,N) precipitation

Certain peculiarities of structural inheritance in phase recrystallization of steel

International Nuclear Information System (INIS)

Mukhamedov, A.A.

1978-01-01

The structural inheritance in phase recrystallization of previously overheated to various temperatures industrially melted 40Kh steel and of Armco-iron has been investigated. The steels have been heated to 100O, 11O0, 1200 and 1260 deg C and cooled in the air, and in some instances, hardened (quenched) in water. The physical broadening of X-ray lines points to a nonmonotonous variation of fine structure parameters as a function of the temperature and the heating time. The inheritance effect of fine structure defects affects the steel properties obtained in a final heat treatment. The structural inheritance effect has an important bearing upon the wear resistance of steel. A purpose-oriented use of the structural inheritance effect can enhance service properties of steel parts

Development and use of data base on mechanical properties of materials in power engineering

International Nuclear Information System (INIS)

Popov, A.A.; Shchukina, E.G.; Karaev, A.B.

1987-01-01

The structure of a data base on the properties of materials used in reactor engineering is considered. The data base presents a factographic automated data retrieval system, containing test results on the 15Kh2NMFA, 15Kh2NMFA-A, 15Kh2MFA, 10GN2MFA, 22K reactor vessel steels and also the data on the A533, A508 and A304 steels taken from literature. The system is realized using the VAN6 minicomputer and operates in a dialogue mode. Software of the system is arranged by module scheme and realized using the BASIC language. Results of tensile, impact, hardness, fatigue, brittle hardness, radiation resistance, high-temperature strength and heat-resistance tests and data on the thermal properties of the alloys are introduced into the system. Prior to the input in the system the information is subjected to additional expert analysis for completeness and authenticity. The main function of the data base considered consists in the systematization of a large volume of experimental data, which envisages arbitrary retrieval and subsequent analysis using statistical methods. The system contains approximately 15 thousand records on magnetic discs. The total volume of the store is 20 M byte. The system capabilities are demonstrated when analyzing the effects of aalloying additions on mechanical properties of the 15Kh2NMFA steel

15N Hyperpolarization of Imidazole-15N2 for Magnetic Resonance pH Sensing via SABRE-SHEATH.

Science.gov (United States)

Shchepin, Roman V; Barskiy, Danila A; Coffey, Aaron M; Theis, Thomas; Shi, Fan; Warren, Warren S; Goodson, Boyd M; Chekmenev, Eduard Y

2016-06-24

15 N nuclear spins of imidazole- 15 N 2 were hyperpolarized using NMR signal amplification by reversible exchange in shield enables alignment transfer to heteronuclei (SABRE-SHEATH). A 15 N NMR signal enhancement of ∼2000-fold at 9.4 T is reported using parahydrogen gas (∼50% para-) and ∼0.1 M imidazole- 15 N 2 in methanol:aqueous buffer (∼1:1). Proton binding to a 15 N site of imidazole occurs at physiological pH (p K a ∼ 7.0), and the binding event changes the 15 N isotropic chemical shift by ∼30 ppm. These properties are ideal for in vivo pH sensing. Additionally, imidazoles have low toxicity and are readily incorporated into a wide range of biomolecules. 15 N-Imidazole SABRE-SHEATH hyperpolarization potentially enables pH sensing on scales ranging from peptide and protein molecules to living organisms.

Comparative estimation of weld-ability of medium-alloy steels

International Nuclear Information System (INIS)

Makarov, Eh.L.; Laz'ko, V.E.

1977-01-01

Weldability of various industrial steels has been investigated as affected by mutual presence of carbon and alloying elements in a wide range of concentrations. Mechanical properties and technological strength of medium alloyed steel welded joints have been compared. Technological strength parameters have been found to sharply decrease with increasing carbon content, the decrease depending on the alloying system. Resistance to hot and cold cracking is somewhat decreased by nickel and increased by molibdenum and tungsten. The best mechanical properties are displayed by steels of the Kh2GSNVM type. Industrial evidence on argon arc welding of different constructions made of steels 1.5-20 mm thick is compared to laboratory results. Accordingly, the high strength steels are divided into three groups, i.e. those manifesting good, satisfactory and poor weldability

Microstructure-based assessment of creep rupture strength in 9Cr steels

International Nuclear Information System (INIS)

Spigarelli, S.

2013-01-01

A microstructure-based model to assess the long-term creep strength in 9Cr steels is proposed. The model takes into account a number of different key issues, including the presence and evolution of the most important families of precipitates (M 23 C 6 , MX, Laves and Z phases), the subgrain recovery process, the different strengthening mechanisms (solid solution strengthening and particle strengthening), and is able to give realistic values of the long-term creep strength in P9, P91 and P911 steels. If properly tuned to describe the mid/long-term precipitation of the Z-phase, and the concurrent dissolution of MX precipitates, the model can also predict the sigmoidal behaviour which leads to the early rupture of single heats of P91 steel. Highlights: ► Creep response at 600 °C of 9% Cr steels. ► Important effect of the different families of precipitates. ► The effect is described by introducing the grain size term in a previously developed model. ► Degradation of particle strengthening effect is considered by calculating the coarsening of the particles.

Heat treatment effect on the properties of the EhP767 maraging steel welded joints

International Nuclear Information System (INIS)

Taver, E.I.; Piskarev, M.N.; Yushchenko, K.A.; Pustovit, A.I.; Anisimova, M.S.

1977-01-01

Heat treatment effect on properties of welded joints of maraging 03Kh13N4K13M3T (EhP767) steel with yield strength over 150 kgs/mm 2 has been investigated. It is shown, that change in impact strength of aged joints at - 196 deg C depends on the amount of residual austenite and grain size. To stabilize 20-40 % residual austenite heat treatment regimes have been developed. Recommended are quenching at 1030-1050 deg C, sub-zero treatment and aging at 520 deg C for 16 hrs

New method for NPP sodium coolant pipeline austenization

International Nuclear Information System (INIS)

Malashonok, V.A.; Rotshtejn, A.V.; Gotshalk, A.L.; Miryushchenko, E.F.

1980-01-01

Heat treatment technology is considered for pipelines intended for the NPP cooling systems employing sodium coolant. Various techniques are discussed which are used for protecting the pipeline internal surfaces against oxidation in the process of heat treatment. It is noted that the austenite formation of welded joints of steel 12Kh18N9 and steel Kh16N11M3 at temperatures of 1050 and 1100 deg C releases welding-induced stresses and reduces a possibility of local damages. Evacuation down to 1 mm Hg appears to be the most rational protective technique. The considered procedure of the pipeline heat treatment has been utilized for mounting the equipment of the BN-600 reactor at the Beloyarskaya NPP. The economic gain resulting from the use of the procedure, owing to decrease in argon consumption and reduction of labour input, makes up 150 000 roubles

Influence of Z-phase on long-term creep stability of martensitic 9-12%Cr steels

Energy Technology Data Exchange (ETDEWEB)

Hald, J. [DONG Energy (Denmark)]|[Vattenfall Europe AG, Berlin (Germany)]|[DTU Mechanical Engineering (Denmark); Danielsen, H.K. [DTU Mechanical Engineering (Denmark)

2008-07-01

The long-term creep strength of the new generation of martensitic creep resistant 9- 12% Cr steels since the well-known steel Grade 91 relies strongly on particle strengthening by fine MN nitrides based on V and Nb. During long-term hightemperature exposures the MN nitrides may be replaced by the thermodynamically more stable Z-phases (Cr(V,Nb)N) causing a breakdown in creep strength. Cr contents above 10.5% strongly accelerate Z-phase precipitation, which explains the lack of success for all attempts to develop martensitic creep resistant steels with high Cr content for oxidation protection. The Z-phase nucleation process by Cr-diffusion into pre-existing MN nitrides is rate controlling for the Z-phase transformation. More work is needed before effects of chemical composition on the nucleation process can be reliably modeled. Careful control of the Z-phase precipitation process has led to the design of experimental 12%Cr martensitic steels strengthened by Z-phase. Such steels may again enable the combination of high strength and oxidation resistance in the same alloy. This opens a new pathway for further alloy development of the heat resistant martensitic steels. (orig.)

Synthesis of 15N-enriched urea (CO(15NH22 from 15NH3, CO, and S in a discontinuous process

Directory of Open Access Journals (Sweden)

C. R. Sant Ana Filho

2012-12-01

Full Text Available CO(15NH22 enriched with the stable isotope 15N was synthesized based on a reaction involving CO, 15NH3, and S in the presence of CH3OH. The method differs from the industrial method; a stainless steel reactor internally lined with polytetrafluoroethylene (PTFE was used in a discontinuous process under low pressure and temperature. The yield of the synthesis was evaluated as a function of the parameters: the amount of reagents, reaction time, addition of H2S, liquid solution and reaction temperature. The results showed that under optimum conditions (1.36, 4.01, and 4.48 g of 15NH3, CO, and S, respectively, 40 ml CH3OH, 40 mg H2S, 100 ºC and 120 min of reaction 1.82 g (yield 76.5% of the compound was obtained per batch. The synthesized CO(15NH22 contained 46.2% N, 0.55% biuret, melting point of 132.55 ºC and did not exhibit isotopic fractionation. The production cost of CO(15NH22 with 90.0 at. % 15N was US$ 238.60 per gram.

Creep strength and ductility of 9 to 12% chromium steels

DEFF Research Database (Denmark)

Hald, John

2004-01-01

The present paper focuses in on long-term creep properties of parent material of the new 9-12%Cr creep resistant steels, P91, E911 and P92 developed for use in advanced ultrasupercritical power plants. These steels have been at the center of activities in the ECCC Working Group 3A (WG3A) "Ferriti...

Caracterización de los aceros sinterizados obtenidos a partir de polvos prealeados Fe-1,5% Mo

Directory of Open Access Journals (Sweden)

Torralba, J. M.

1995-02-01

Full Text Available Sintered molybdenum-, copper-, nickel- alloyed steels, have been studied through the influence of the Chemical composition on different mechanical and physical properties. In all the studied steels, a constant percentage of carbon has been used, as well Fe-Mo prealloyed powders, with a 1,5% Mo content. Selected sintering conditions were close to those used in the P/M industry, potential consumer of the studied steels.

Se estudian los aceros aleados sinterizados con molibdeno, cobre, níquel y grafito, a partir de la influencia de su composición sobre distintas propiedades mecánicas y físicas. En todos los aceros, se utilizó una composición de carbono constante, así como polvos prealeados de Fe-Mo, con 1,5% Mo. Las condiciones de sinterización elegidas han sido las más próximas a las utilizadas en la industria pulvimetalúrgica, que es el usuario potencial de los materiales estudiados.

Evaluación de la capacidad de reproducción vegetativa de variedades de morera (Morus alba L.

Directory of Open Access Journals (Sweden)

G Martín

Full Text Available Con el objetivo de evaluar el efecto de la variedad y de la parte de la rama en la brotación foliar y radicular de los propágulos, se estudiaron cinco variedades de morera (tigreada, yu-12, yu-62, murcia y universidad. Las ramas se dividieron en tres partes (basal, media y apical, lo que originó un total de 15 tratamientos. Se evaluó la cantidad y el porcentaje de propágulos brotados y arraigados, el número de ramas, el número de hojas y el peso de las raíces. Yu-12 y tigreada tuvieron la mayor brotación (100 y 98 %, respectivamente. Sin embargo, tigreada se destacó en el arraigamiento (70 % del total de esquejes plantados y el peso de las raíces (2,67 g, en lo que difirió significativamente (p < 0,05 del resto de las variedades. Además, al utilizar la parte basal y la media se obtuvo el mayor porcentaje de brotación (93 y 90 %, respectivamente. La interacción de la variedad y la parte de la rama fue significativa; los mejores resultados se obtuvieron en la tigreada parte basal, en cuanto al número de ramas y de hojas. Tigreada mostró el mejor comportamiento morfoagronómico durante el periodo experimental; mientras que yu-12, yu-62, universidad y murcia no respondieron eficientemente a la reproducción a partir de propágulos. La parte basal y la media fueron determinantes en la brotación foliar y radicular y en el peso de las raíces. Se recomienda repetir estos experimentos en vivero, en diferentes meses del año, y utilizar productos que estimulen el enraizamiento de los propágulos.

Impact behavior of 9-Cr and 12-Cr ferritic steels after low-temperature irradiation

International Nuclear Information System (INIS)

Klueh, R.L.; Vitek, J.M.; Corwin, W.R.; Alexander, D.J.

1987-01-01

Miniature Charpy impact specimens of 9Cr-1MoVNb and 12Cr-1MoVW steels and these steels with 1 and 2% Ni were irradiated in the High-Flux Isotope Reactor (HFIR) at 50 0 C to displacement damage levels of up to 9 dpa. Nickel was added to study the effect of transmutation helium. Irradiation caused an increase in the ductile-brittle transition temperature (DBTT). The 9Cr-1MoVNb steels, with and without nickel, showed a larger shift than the 12Cr-1MoVW steels, with and without nickel. The results indicated that helium also increased the DBTT. The same steels were previously irradiated at higher temperatures. From the present and past tests, the effect of irradiation temperature on the DBTT behavior can be evaluated. For the 9Cr-1MoVNb steel, there is a continuous decrease in the magnitude of the DBTT increase up to an irradiation temperature of about 400 0 C, after which the shift drops rapidly to zero at about 450 0 C. The DBTT of the 12Cr-1MoVW steel shows a maximum increase at an irradiation temperature of about 400 0 C and less of an increase at either higher or lower irradiation temperatures

High temperature oxidation of 9% and 12% Cr steel: effect of water vapour; Oxidation haute temperature d'un acier 9% et 12% de teneur Cr. Effet de la vapeur d'eau

Energy Technology Data Exchange (ETDEWEB)

Evin, H.; Heritier, D.; Chevalier, S. [Universite de Bourgogne, Institut Carnot de Bourgogne UMR 5209 CNRS, 21 - Dijon (France); Fojer, C. [OCAS N.V. ArcelorMittal Research Industry Gent, Zelzate (Belgium)

2008-07-01

Isothermal tests were performed on commercial 9%Cr and 12%Cr steels between 600 and 750 deg C in air under atmospheric pressure. The same steels were also tested in oxidizing atmosphere enriched with 12% H{sub 2}O at 700 deg C for 24 hours. Kinetics data were registered and the corrosion products were analyzed using different characterization tools such as scanning electron microscope, x-ray diffraction and secondary ions mass spectrometry. 9%Cr steels showed very limited high temperature corrosion behavior in air, because a breakaway appeared after less than 80 hours at 750 deg C. Spinel oxides composed of iron, chromium and manganese (Mn{sub 1.5}Cr{sub 1.5}O{sub 4} and MnFe{sub 2}O{sub 4}) were identified over the surfaces of both steel grades after oxidation. (Cr,Fe){sub 2}O{sub 3} was also identified especially at 700 deg C and 750 deg C, whereas Fe{sub 2}O{sub 3} mainly grew at 600 and 650 deg C. Differences in oxide morphology and composition were noticed between the samples oxidized under air and air + 12 % water vapor. (authors)

Conversion of MX Nitrides to Modified Z-Phase in 9-12%Cr Ferritic Steels

DEFF Research Database (Denmark)

Cipolla, Leonardo

for Z-phase formation was highlighted during the studies. Several 9-12%Cr commercial steels with prolonged high-temperature exposures have been investigated, too. The same mechanism of Z-phase formation observed in 12%Cr model alloys was identified in industrial 9-12%Cr steels after thousands of hours......The 9-12%Cr ferritic steels are extensively used in modern steam power plants at service temperature up to 620°C. Currently the best perform ing ferritic creep resistance steel is the ASTM Grade 92, whose high temperature strength has recently been assessed by European Creep Collaborative Committee...... in 2005 as 600°C/113MPa/10 5h. All previous attempts made in the last twenty years to develop ferritic steels for 650°C applications have failed due to the incapacity to combine the superior oxidation resistance, given by 12%Cr content, with excellent creep resistance of high-alloyed ferritic steels...

N7- and N9-substituted purine derivatives: a N-15 NMR study

Czech Academy of Sciences Publication Activity Database

Marek, R.; Brus, Jiří; Toušek, J.; Kovács, L.; Hocková, Dana

2002-01-01

Roč. 40, č. 5 (2002), s. 353-360 ISSN 0749-1581 R&D Projects: GA ČR GA203/98/P026; GA MŠk LN00A016 Institutional research plan: CEZ:AV0Z4050913 Keywords : NMR * H-1 NMR * N-15 NMR Subject RIV: CE - Biochemistry Impact factor: 0.994, year: 2002

Tribological properties of CrN coatings deposited by nitro-chromizing treatment on AISI D2 steel

Energy Technology Data Exchange (ETDEWEB)

Durmaz, M., E-mail: mdurmaz@sakarya.edu.tr; Abakay, E.; Sen, U.; Sen, S. [Department of Metallurgical and Materials Engineering, Engineering Faculty, Sakarya University, Esentepe Campus, 54187 Sakarya (Turkey); Kilinc, B. [Department of Metallurgical and Materials Engineering, Institute of Arts and Sciences, Sakarya University, Esentepe Campus, 54187 Sakarya (Turkey)

2015-03-30

In this work, the wear test of uncoated and chromium nitride coated AISI D2 cold work tool steel against alumina ball realized at 0.1 m/s sliding speeds and under the loads of 2.5N, 5N and 10N. Steel samples were nitrided at 575°C for 8 h in the first step of the coating process, and then chromium nitride coating was performed thermo-reactive deposition technique (TRD) in a powder mixture consisting of ferro-chromium, ammonium chloride and alumina at 1000°C for 2 h. Nitro-chromized samples were characterized by X-Ray diffraction analysis (XRD), scanning electron microscopy (SEM), micro-hardness and ball on disk wear tests. The coating layer formed on the AISI D2 steel was compact and homogeneous. X-ray studies showed that the phase formed in the coated layer is Cr{sub 2}N. The depth of the layer was 8.15 µm. The average hardness of the layer was 2160±15 HV{sub 0.025}. For uncoated and chromium nitride materials, wear rate increased with increasing load. The results of friction coefficient and wear rate of the tested materials showed that the CrN coating presents the lowest results.

Tribological properties of CrN coatings deposited by nitro-chromizing treatment on AISI D2 steel

International Nuclear Information System (INIS)

Durmaz, M.; Abakay, E.; Sen, U.; Sen, S.; Kilinc, B.

2015-01-01

In this work, the wear test of uncoated and chromium nitride coated AISI D2 cold work tool steel against alumina ball realized at 0.1 m/s sliding speeds and under the loads of 2.5N, 5N and 10N. Steel samples were nitrided at 575°C for 8 h in the first step of the coating process, and then chromium nitride coating was performed thermo-reactive deposition technique (TRD) in a powder mixture consisting of ferro-chromium, ammonium chloride and alumina at 1000°C for 2 h. Nitro-chromized samples were characterized by X-Ray diffraction analysis (XRD), scanning electron microscopy (SEM), micro-hardness and ball on disk wear tests. The coating layer formed on the AISI D2 steel was compact and homogeneous. X-ray studies showed that the phase formed in the coated layer is Cr 2 N. The depth of the layer was 8.15 µm. The average hardness of the layer was 2160±15 HV 0.025 . For uncoated and chromium nitride materials, wear rate increased with increasing load. The results of friction coefficient and wear rate of the tested materials showed that the CrN coating presents the lowest results

Tribological properties of CrN coatings deposited by nitro-chromizing treatment on AISI D2 steel

Science.gov (United States)

Durmaz, M.; Kilinc, B.; Abakay, E.; Sen, U.; Sen, S.

2015-03-01

In this work, the wear test of uncoated and chromium nitride coated AISI D2 cold work tool steel against alumina ball realized at 0.1 m/s sliding speeds and under the loads of 2.5N, 5N and 10N. Steel samples were nitrided at 575°C for 8 h in the first step of the coating process, and then chromium nitride coating was performed thermo-reactive deposition technique (TRD) in a powder mixture consisting of ferro-chromium, ammonium chloride and alumina at 1000°C for 2 h. Nitro-chromized samples were characterized by X-Ray diffraction analysis (XRD), scanning electron microscopy (SEM), micro-hardness and ball on disk wear tests. The coating layer formed on the AISI D2 steel was compact and homogeneous. X-ray studies showed that the phase formed in the coated layer is Cr2N. The depth of the layer was 8.15 µm. The average hardness of the layer was 2160±15 HV0.025. For uncoated and chromium nitride materials, wear rate increased with increasing load. The results of friction coefficient and wear rate of the tested materials showed that the CrN coating presents the lowest results.

Phosphorus effect on fracture properties of structural steels

International Nuclear Information System (INIS)

Goritskij, V.M.; Guseva, I.A.

1985-01-01

Phosphorus content is studied for its effect on fracture peculiarities and fracture toughness. It is supposed that the phosphorus effect on ductile fractures is associated with phosphorus segregation on the ferrite-carbide interfaces. An increase of the phosphorus content in heat-treated 10KhSND steel from 0.020 up to 0.043 wt.% results in a decrease of the pore size and asub(p) value. Close linear correlation is established between critical temperature of embrittlement T 50 and √ asub(p) or √ KC values for a number of structural steels with different phosphorus content

Estimate of production of gaseous nitrogen in the human body based on (15)N analysis of breath N2 after administration of [(15)N2]urea.

Science.gov (United States)

Junghans, Peter

2013-01-01

After oral administration of [(15)N2]urea (1.5 mmol, 95 atom% (15)N), we found that breath N2 was significantly (15)N-labelled. The result suggests that molecular nitrogen in breath must be partly produced endogenously. Based on a metabolic model, the endogenous N2 production was estimated to be 0.40±0.25 mmol kg(-1) d(-1) or 2.9±1.8 % of the total (urinary and faecal) N excretion in fasted healthy subjects (n=4). In patients infected with Helicobacter pylori (n=5), the endogenous N2 production was increased to 1.24±0.59 mmol kg(-1) d(-1) or 9.0±4.3 % of the total N excretion compared to the healthy controls (pexchange measurements may be affected by endogenously produced nitrogen, especially in metabolic situations with elevated nitrosation, for instance in oxidative and nitrosative stress-related diseases such as H. pylori infections.

THE PRODUCTION OF STEEL CORD IN BELARUS IS 15 YEARS OLD

Directory of Open Access Journals (Sweden)

A. N. Savenok

2004-01-01

Full Text Available In this article there is briefly narrated about the history of the steel wire cord production, the development of its production at Belorussian metallurgical works, perspectives of the further increase of the Belorussian steel wire cord production volume. The information on the dynamics of the production of wire RVD, wire of bead rings of tires and steel wire cord at RUP “BMZ” for the last 15 years is given. The tendencies of the development of the tires reinforcing materials for the nearest future are considered.

Structural sensitivity of cyclic crack resistance of rotor steel in gaseous hydrogen

International Nuclear Information System (INIS)

Romaniv, O.N.; Nikiforchin, G.N.; Kozak, L.Yu.

1984-01-01

Comparative evaluation of cyclic crack resistance of hardened rotor set steel 35KhN3MFA in different cstructural states during tesis in agea geseous hydrogen, in the air and in vacuum, has been mde made. It is shown, that structural sensitivity of near-threshold crack resistance of the studied rotor steel in gaseous hydrogen is to a high extent determined by the closing and morphology of fatigue crack. The decrease in crack closing (CC) observed during tests in hydrogen in low-strenght and crack branching in high-strength steels results in the fact, that in contrast to well-known notions on a higher sensitivity to hydrogen embrittlement of high-strenght alloys the negative effect of hydrogen on the near-threshold cyclic crack resistance is manifested only in steel in low-strenght state. The considered regularities in crack growth in low-alloyed steel under the effect of gaseous hydrogen are just only for high-frequency loading. In all probability in the case of fatigue crack growth (GCG) at low frequencies of loading not only the medium activity, but also the role o, closing and crack geometty in the kinetics of fatigue fracture, the clarifying of which requires further studieds, will change

UNTANGLING THE NEAR-IR SPECTRAL FEATURES IN THE PROTOPLANETARY ENVIRONMENT OF KH 15D

Energy Technology Data Exchange (ETDEWEB)

Arulanantham, Nicole A.; Herbst, William; Gilmore, Martha S.; Cauley, P. Wilson [Astronomy Department, Wesleyan University, Middletown, CT 06459 (United States); Leggett, S. K., E-mail: nicole.arulanantham@colorado.edu [Gemini Observatory (North), Hilo, HI 96720 (United States)

2017-01-10

We report on Gemini/GNIRS observations of the binary T Tauri system V582 Mon (KH 15D) at three orbital phases. These spectra allow us to untangle five components of the system: the photosphere and magnetosphere of star B, the jet, scattering properties of the ring material, and excess near-infrared (near-IR) radiation previously attributed to a possible self-luminous planet. We confirm an early-K subgiant classification for star B and show that the magnetospheric He i emission line is variable, possibly indicating increased mass accretion at certain times. As expected, the H{sub 2} emission features associated with the inner part of the jet show no variation with orbital phase. We show that the reflectance spectrum for the scattered light has a distinctive blue slope and spectral features consistent with scattering and absorption by a mixture of water and methane ice grains in the 1–50 μ m size range. This suggests that the methane frost line is closer than ∼5 au in this system, requiring that the grains be shielded from direct radiation. After correcting for features from the scattered light, jet, magnetosphere, and photosphere, we confirm the presence of leftover near-IR light from an additional source, detectable near minimum brightness. A spectral emission feature matching the model spectrum of a 10 M {sub J}, 1 Myr old planet is found in the excess flux, but other expected features from this model are not seen. Our observations, therefore, tentatively support the picture that a luminous planet is present within the system, although they cannot yet be considered definitive.

The Use of 32P and 15N to Estimate Fertilizer Efficiency in Oil Palm

International Nuclear Information System (INIS)

Sisworo, Elsje L; Sisworo, Widjang H; Havid-Rasjid; Haryanto; Syamsul-Rizal; Poeloengan, Z; Kusnu-Martoyo

2004-01-01

Oil palm has become an important commodity for Indonesia reaching an area of 2.6 million ha at the end of 1998. It is mostly cultivated in highly weathered acid soil usually Ultisols and Oxisols which are known for their low fertility, concerning the major nutrients like N and P. This study most conducted to search for the most active root-zone of oil palm and applied urea fertilizer at such soils to obtain high N-efficiency. Carrier free KH 2 32 PO 4 solution was used to determine the active root-zone of oil palm by applying 32 P around the plant in twenty holes. After the most active root-zone have been determined, urea in one, two and three splits were respectively applied at this zone. To estimate N-fertilizer efficiency of urea labelled 15 N Ammonium Sulphate was used by adding them at the same amount of 16 g 15 N plan -1 . This study showed that the most active root-zone was found at a 1.5 m distance from the plant-stem and at 5 cm soil depth. For urea the highest N-efficiency was obtained from applying it at two splits. The use of 32 P was able to distinguish several root zones: 1.5 m - 2.5 m from the plant-stem at a 5 cm and 15 cm soil depth. Urea placed at the most active root-zone, which was at a 1.5 m distance from the plant-stem and at a 5 cm depth in one, two, and three splits respectively showed difference N-efficiency. The highest N-efficiency of urea was obtained when applying it in two splits at the most active root-zone. (author)

MARTENSITIC CREEP RESISTANT STEEL STRENGTHENED BY Z-PHASE

DEFF Research Database (Denmark)

2008-01-01

The present invention relates to steel alloys having a martensitic or martensitic- ferritic structure and comprising Z-phase (CrXN) particles, where X is one or more of the elements V, Nb, Ta, and where the Z-phase particles have an average size of less than 400 nm. The alloy comprises by wt...... % the following components: 9 to 15% Cr, 0.01-0.20% N, C in an amount less than 0.1%, one or more of: 0.01- 0.5%V,0.01-1%Nb, 0.01-2%Ta, and a balance being substantially iron and inevitable impurities. The invention further relates to a method of manufacturing such a steel alloy, a component comprising...... such a steel alloy, and to the use of such a steel alloy for high temperature components....

Resistivity, hysteresis, and magnetization of 9% Cr stainless steel as a function of temperature and its electromagnetic shielding effects in cylindrical structures

International Nuclear Information System (INIS)

Praeg, W.F.

1979-01-01

Ferromagnetic stainless steels may offer significantly greater wall life-times for first wall/blanket and vacuum vessel structures than commonly used non-magnetic stainless steels. One steel under consideration has the following composition, in wt %, Fe(86.24), Cr(9), Mo(2), Mn(1), Si(0.75), Nb(0.50), V(0.30), C(0.15), P(0.3), S(0.30). There appears to be no literature on the electromagnetic properties of this material. Therefore, the resistivity, the hysteresis loops, and magnetization were measured as a function of temperature up to the Curie point

15 N separation in the Nitrox system under pressure

International Nuclear Information System (INIS)

Axente, D.; Baldea, A.; Teaca, C.; Horga, R.; Abrudean, M.

1999-01-01

The basic isotope exchange reaction responsible for the separation of 15 N in Nitrox system is that between gaseous nitrogen oxides and aqueous nitric acid with single stage separation factor α = 1.055 for M.l -1 nitric acid, at 25 deg. C and atmospheric pressure. The rate of nitrogen isotope exchange between NO and HNO 3 has been measured as a function of nitric oxide pressure 0.1 - 0.4 MPa for 1 and 2 M.l -1 . It is concluded that 15 N/ 14 N exchange rate in NO-HNO 3 system has a linear dependence on NO pressure as indicated by rate measurements at different NO partial pressure and constant overall pressure, by adding helium in reactor. Using the rate law: R = [HNO 3 ] 2 [N 2 O 3 ] the 15 N/ 14 N exchange rates for nitric acid concentrations 1.5 - 10 M.l -1 were calculated. In order to know what happens in 15 N separation at higher pressure, when the isotopic transport between two phases is improved, a stainless steel laboratory experimental setup with 1000 mm long x 18 mm i,d. column, packed with triangular wire springs 1.8 x 1.8 x 0.2 mm was utilised. At 0.15 MPA and 2.36 ml.cm -2 . min -1 flow rate HETP was 7% smaller than at atmospheric pressure and 1.5 times smaller flow rate. HETP at 3.14 ml . cm -2 . min -1 flow rate and 0.18 MPa is practically equal with that obtained at atmospheric pressure and 2 times smaller flow rate. The operation of the 15 N separation setup at 0.18 MPa, instead of atmospheric pressure, will permit to double the 10 M.l -1 nitric acid flow rate and of 15 N production of the given column. (authors)

Properties of 40N3M powder structural steel

International Nuclear Information System (INIS)

Moskvina, T.P.; Gulyaev, A.P.; Gulyaev, I.A.; Byakov, S.V.; Melent'ev, I.V.; Morgun, G.N.

1984-01-01

Effect of the fabrication technique of compact slabs made of the 40N3M powder structural steel on mechanical properties with determination of a cold brittleness threshold was studied. It is established that after a thermal treatment at a density close to 100% a powder steel is sufficiently close to steel, rolled of an ingot, but is second in reference to steel in its ductility and impact strength. Properties of powder steel obtained by the method of dynamic hot forming (DHF) and hot extrusion are practically equal, but the first method has definite advantages as it allows to obtain details with a definitive form. The above investigation permits to recommend an application of the 40N3M powder steel fabricated by the DHF methods. The optimum thermal treatment course is: quenching+high annealing

Properties of 15/2- states in 215Ra and 217Th; evaluation of the 15/2- to 9/2+ E3 strength in N=127 isotones

International Nuclear Information System (INIS)

Dracoulis, G.D.; Riess, R.; Stuchbery, A.E.; Bark, R.A.; Gupta, S.L.; Baxter, A.M.; Kruse, M.

1988-01-01

The lifetime of the yrast 15/2 - state in 215 Ra was measured using pulsed beams and γ-ray and electron techniques. Transition multipolarities were established from measured conversion coefficients. The B(E3) of the 15/2 - → 9/2 + transition is found to be considerably larger than previously reported. A candidate for the corresponding transition in 217 Th was also observed. The E3 strength of the 15/2 - → 9/2 + transition in the N=127 isotones is evaluated in the light of these and other recent results. Interpretation in the framework of particle-octupole vibration coupling requires a systematic lowering of the core 3 - vibration as proton pairs are added to 208 Pb

Creep-fatigue-environment interaction of 9Cr-1Mo-V-Nb steel

International Nuclear Information System (INIS)

Shibata, Hiroyuki; Ishikawa, Akiyoshi; Asada, Yasuhide

1996-01-01

An extension of the creep-fatigue damage model has been conducted in the present study. The original damage model has been developed to the predict the creep-fatigue life of 9Cr-1Mo-V-Nb steel (Modified 9Cr-1Mo steel) in a very high vacuum environment. The present study is to extend an applicability of the model to the creep-fatigue damage accumulation in the air environment. (orig.)

Study of nitrogen solubility in multicomponent iron alloys at its pressure in gaseous phase up to 1000kPa

International Nuclear Information System (INIS)

Pomarin, Yu.M.; Grigorenko, G.M.; Latash, Yu.V.; Kanibolotskij, S.A.

1983-01-01

A facility in which metal is melted in a weighed state and nitrogen partical pressure during relting may be charge from 0 to 1000 kPa is developed to investigate nitrogen solubility is liquim metals and alloys. Investigation of nitrogen solubility was performed using samples of 03Kh25N5AM3 steel and Kh20N5, Kh20N10, Kh40N10, Kh40N20 alloys. Positive deflection of [N]=f(√Psub(Nsub(2))) dependence from the Henry law is shown to be observed in the Kh40N10 alloy in the 100-1000 kPa pressure range. In this case the vatue of positive deflection decreases with temperature growth and at T=2273 K nitrogen solubility in the alloy submits to the law of square root. An equation permitting to calculate nitrogen solubility in alloys of Fe-Cr-Ni and Fe-Cr-Mn systems in the 0 to 1000 kPa range of nitrogen partial pressures is obtained

Microstructure and elevated temperature stability of 9-12% Cr steels

Energy Technology Data Exchange (ETDEWEB)

Dogan, Omer N.; Hawk, Jeffrey A.

2005-02-01

Medium Cr steels have been used in fossil fired power plants for many years because of their excellent high temperature stability and mechanical properties. As the desire to increase the efficiency of power plants continues, the operating temperature (>650C) continues to go up. Currently available low and medium Cr containing steels will not withstand the new operating temperature and must be reassessed in terms of their solid-solution and precipitation strengthening schemes. Three medium Cr steels were developed to investigate high temperature alloy strengthening strategies: 0.08C-(9-12)Cr-1.2Ni-0.7Mo-3.0Cu-3.0Co-0.5Ti. The microstructure of the alloy will be described in the as-cast and thermo-mechanically worked states. In addition, the effect on microstructure from long-term high temperature exposure will also be discussed. Finally, the overall stability of these steels will be compared against currently available power plant steels.

Cold-rolled sheets production of stainless martensite-ageing steel smelted by vacuum arc and electroslag techniques

Energy Technology Data Exchange (ETDEWEB)

Rivkin, A A; Grishkov, A I; Suslin, A P; Nesterenko, A A; Lola, V N [Tsentral' nyj Nauchno-Issledovatel' skij Inst. Chernoj Metallurgii, Moscow (USSR)

1975-05-01

In cooperation with a number of metallurgical works the production of a high strength sheet stainless maraging steel EHP678 (000KH11N10M2T) has been tested by rolling cylindrical ingots of vacuum arc smelting at the blooming (the mass of rough ingots was 5.1 to 6.0 t, that of cleaned ingots - 3.8 to 5.1 t) or rectangular ingots of electroslag smelting (13 t) at the slabbing. The recommended regimes of heating and deformation are much similar to those used for the steel-KH18N10T. The output of valid cold-rolled sheets proved to be rather low (0.24 t/t for the vacuum arc smelting and 0.30 t/t for the electroslag smelting) mainly due to the losses on cleaning and a considerable portion of wrong-size slabs. The data are presented on the steel-EHP678 properties after various heat treatments. For the production of wide cold-rolled sheets of the steel EHP678 it is recommended to use steelmaking procedure with electroslag smelting including open-hearth melting in arc furnaces, rolling of ingots at the slabbing with heating up to 1260-1280 deg C (hold-up of 4.5 to 5 hrs); electroslag smelting for rectangular section slabs, rolling of ingots of electroslag smelting at the slabbing with their heating up to 1250 deg C (hold-up of 5.5 to 6 hrs), rolling at the 1680-type mill with heating up to 1250-1260 deg C (hold-up of 4 to 4.5 hrs ensuring the rolling temperature after a rough group not below 1100 deg C), quenching of hot-rolled sheets heating up to 920-940 deg C (hold-up of 3 to 3.5 min/mm), shot peening of sheets for descaling (provided the respective equipment is available) with a subsequent short-time pickling in an acid solution and cold rolling with a summary deformation of 35 to 45 %. The steelmaking with the electroslag smelting is much more profitable as regards to the fine technology of number of the main procedures, convenient cooperation of the works and a considerably greater output of the final products out of one ton of the steel produced.

Microstructure refinement and strengthening mechanisms of a 9Cr oxide dispersion strengthened steel by zirconium addition

International Nuclear Information System (INIS)

Xu, Hai Jian; Lu, Zheng; Wang, Dong Mei; Liu, Chunming

2017-01-01

To study the effects of zirconium (Zr) addition on the microstructure, hardness and the tensile properties of oxide dispersion strengthened (ODS) ferritic-martensitic steels, two kinds of 9Cr-ODS ferritic-martensitic steels with nominal compositions (wt.%) of Fe-9Cr-2W-0.3Y_2O-3 and Fe-9Cr-2W-0.3Zr-0.3Y_2O_3 were fabricated by the mechanical alloying (MA) of premixed powders and then consolidated by hot isostatic pressing (HIP) techniques. The experimental results showed that the average grain size decreases with Zr addition. The trigonal δ-phase Y_4Zr_3O_1_2 oxides and body-centered cubic Y_2O_3 oxides are formed in the 9Cr-Zr-ODS steel and 9Cr non-Zr ODS steel, respectively, and the average size of Y_4Zr_3O_1_2 particles is much smaller than that of Y_2O_3. The dispersion morphology of the oxide particles in 9Cr-Zr-ODS steel is significantly improved and the number density is 1.1 x 10"2"3/m"3 with Zr addition. The 9Cr-Zr-ODS steel shows much higher tensile ductility, ultimate tensile strength and Vickers hardness at the same time

Surface finishing and levelling of thermomechanically hardened rolled steel

International Nuclear Information System (INIS)

Grosval'd, V.G.; Bashchenko, A.P.; Grishkov, A.I.; Gutnik, M.V.; Kanevskij, B.L.; Nikozov, A.I.; Sedov, N.D.; Prosin, K.A.; Safonov, L.I.

1975-01-01

The finishing of high-strength merchant shapes from alloy steel was tried out under industrial conditions with the equipment of metallurgical plants. After thermomechanical hardening in the production line of the rolling mill, 30KhGSN2A and 40Kh1NVA steel rounds 32 and 31 mm in diameter were straightened on a two-roller straightening machine designed by the All-Union Scientific Research Institute for Metallurgical Machinery (VNII Metmash). This made possible subsequent turning and grinding of the rods. The conditions of straightening, turning and grinding have been worked so as to obtain thermomechanically strengthened and ground rolled products approximating the gauged and ground metal in shape geometry and surface finish. It is shown that the labour-consuming operation of turning can be eliminated by reducing the machining pass of the rolled product, and this lowers the labour required for the finishing operations by 75%. After grinding with 40- and 25-grain abrasive wheels, high strength rolled shapes were obtained with a diameter of 30-0.20 mm and a surface finish of class 6-5 satisfying the technical specifications. (author)

Study on the process of calibration and deep centring of blanks

International Nuclear Information System (INIS)

Potapov, I.N.; Romantsev, B.A.; Popov, V.A.; Volodin, V.V.; Goncharuk, A.V.

1985-01-01

Process of calibration and deep centring of blanks before broaching is developed and studied. Investigations are performed at a semi-industrial screw rolling mill MISiS-100 T. Blanks made of 40Kh, 60, 50, 45KhN2MFA, 30KhGSNA steels 80, 85, and 90 mm in diameter and 300 mm long were calibrated and centered after heating in a furnace to a depth of 200 mm at shafts and faces with different calibration. 30KhN2MFA steel is chosen for face material; heat treatment is conducted under the following conditions: heating up to 950-1000 deg C and hold-up during 30-35 min with the following cooling in the air. The above experimental investigations reveal that the process of calibration and deep centring accomplished at a three-shaft screw rolling mill is rather stable and provides a high accuracy of centering hollow marking

Influence of Normalizing Temperature on the Microstructure and Hardness of 9Cr-1Mo ODS Steel

Energy Technology Data Exchange (ETDEWEB)

Jang, Ki Nam; Kim, Tae Kyu [Korea Atomic Energy Research Institute, Daejeon (Korea, Republic of); Kim, Kyu Tae [Dongguk University, Gyeongju (Korea, Republic of)

2016-10-15

Oxide dispersion strengthened(ODS) steel has superior high-temperature strength and creep properties because fine oxide particles having an excellent stability at high temperatures are uniformly distributed in the matrix. ODS steel has being developed for structure materials of sodium fast cooled reactor(SFR) because of its excellent irradiation resistance and mechanical properties. 9Cr-1Mo ODS steel has better high temperature strength and irradiation resistance than common 9Cr-1Mo steel because Y{sub 2}O{sub 3} nano-sized particles which interrupt dislocation movement and grain boundary slip are uniformly dispersed in the martensite matrix. The mechanical properties of the ODS steels are mainly determined by their microstructures, and the microstructure is considerably decided by the heat-treatment conditions. This study focused on the effect of normalizing temperature on microstructure and hardness of 9Cr-1Mo martensitic ODS steel so as to optimize the heat-treatment condition. In this study, the effect of normalizing temperature on mechanical property and microstructures of 9Cr-1Mo martensitic ODS steel was investigated. It was shown that the microhardness was steadily increased with increasing of the normalizing temperature. According to TEM observation, mechanical property of 9Cr-1Mo ODS steel was significantly affected by lath width. These observations, could be useful to understand the relationship between normalizing temperature and microstructure.

Hot ductility of structural steels melted with the use of direct reduction charge

International Nuclear Information System (INIS)

Marchenko, V.N.; Bulat, S.I.; Litvinenko, D.A.

1982-01-01

A possibility of the use of direct reduction charge during the open arc melting of the 40Kh2N2MA steel with the subsequent electroslag remelting was investigated. It is shown that the use of such charge free from non-ferrous metal admixtures permits to increase an alloy hot ductility in the hot-brittleness range from 900 up to 1500 deg C. An increase of the deformation rate from 0.1 up to 1 s - 1 increases 1.5-3 times a level of minimum ductility within this temperature range. It is established that antimony and bismuth impurities considerably decrease hot ductility

Language Personality of the Publicist: Rhetorical and Stylistic Canon (Yu. Senkevich “To “Ra” Across the Atlantic”

Directory of Open Access Journals (Sweden)

Olga V. Shatalova

2017-10-01

Full Text Available In article the communicative and linguistic parameters of the speech of the publicist of the XX century Yu. Senkevich which are declared as a sample for formation of the language personality in the conditions of development of the modern information and communicative environment are designated. On the example of the analysis of the book «On “Ra” through Atlantic» locates the fact of that Yu.N. Senkevich’s creativity corresponds to the main criteria of popular scientific journalism: high degree of reliability, authoritativeness of the publicist; dynamism, dramatic nature, intelligence of a statement. The unostentatious enlightenment based on updating of scientific knowledge for the addressee and a dialogization of a publicistic discourse, the high level of psychological and philosophical generality, the declaration of humanistic values form specific rhetoric which is supported by the formal and grammatical organization of the speech of the publicist. Priority of syntactic designs of a certain type, stylistic ladders and figures – dynamism of a statement and scale of representation of material define. The humour and easy self-irony as significant characteristics of the language personality define a basis of the rhetorical and stylistic canon realized in publicistic works Yu.N. Senkevich – «the human view of people and society» that in the modern information and communicative environment becomes a necessary reference point.

Effect of carbides on erosion resistance of 23-8-N steel

Indian Academy of Sciences (India)

8-N nitronic steel, carbides present in the form of bands are observed to accelerate the erosion rate. Coarse ... lar carbides, precipitating at random boundaries, were more likely to ... 23-8-N nitronic steel is basically austenitic stainless steel.

Creep and creep fatigue crack behavior of 1Cr- and 9Cr-steels

International Nuclear Information System (INIS)

Maile, K.; Klenk, A.; Schellenberg, G.; Granacher, J.; Tramer, M.

2000-01-01

A large database for creep crack initiation and propagation under constant load conditions is available on conventional power plant steels of types 1%Cr and 12%Cr. Modern plants are often used in the medium and peak load regime, thus the dominant loading situation in high temperature components is creep fatigue. For life assessment data about crack initiation and growth under creep fatigue loading are required. These characteristics can not be substituted by pure fatigue or creep crack data. Therefore, a comprehensive test programme was started to investigate the creep fatigue crack behaviour of a 1%CrMoNiV turbine rotor steel (30CrMoNiV 4 11) at 550 C and a new 9%CrMoVNb pipe steel (type P 9 1) at 600 C. DENT-specimen with 15 and 60 mm thickness as well as side grooved CT-specimen with 25 and 50 mm thickness have been tested to determine possible influences of geometry and thus to check the transferability of the data to components. The creep fatigue crack growth results of tests with dwell times between t H = 0,32h and 10 h lie in the scatterbands given by creep crack growth results. Nevertheless a higher crack growth rate under creep fatigue conditions can be stated. An increase in crack growth rate due to creep fatigue is clearly visible. Loading situations with frequencies higher than 1.10 -4 Hz should be not assessed with pure creep crack results or sufficient safety margins have to be applied. (orig.)

Initial study on Z-phase strengthened 9-12% Cr steels by atom probe tomography

Energy Technology Data Exchange (ETDEWEB)

Liu, Fang; Andren, Hans-Olof [Chalmers Univ. of Technology, Goeteborg (Sweden). Dept. of Applied Physics

2010-07-01

The microstructure of two different types of Z-phase strengthened experimental steels, CrNbN-based or CrTaN-based, was investigated. Both steels underwent aging at 650 C for relatively short period of time, 24 hours or 1005 hours. Atom probe tomography was used to study the chemical composition of the matrix and precipitates, and the size and number density of the small precipitates. Both steels contain Laves phase at prior austenite grain boundaries and martensitic lath boundaries. The CrTaN-based steel was found more promising due to its finer and more densely distributed precipitates after 1005 hour aging. (orig.)

[Effects of different amounts of phosphate fertilizers on copper, zinc transfer in red soil under the application of KH2PO4].

Science.gov (United States)

Guo, Liang; Li, Zhong-wu; Huang, Bin; Wang, Yan; Zhang, Yan

2014-09-01

In order to study the effects of different phosphate addition amounts on migration and transformation of heavy metals (Cu, Zn) in soil, an indoor leaching experiment using soil columns was carry out to study the leaching behavior of Cu and Zn. The KH2PO4 was chosen as the fertilizer application at the doses of 5 mg.kg-1, 15 mg.kg-1 and 25 mg.kg-1. The results showed that KH2PO4, could reduce the leachate pH, but different phosphate amounts had little effect on leachate pH, pH in leachate kept rising in the whole leaching process. With the application of KH2PO4, Cu migration was mainly in the surface layer while Zn migrated into deeper soil. Concentrations of Cu, Zn in deep soil leachate were low indicating that it was harmless to the shallow groundwater. After leaching, heavy metals mainly existed in the residual form in soil, the proportion of residual form of Cu was around 60% and the proportion of residual form of Zn was around 40%. High concentration of KH2PO4 helps the transformation of Zn from residual organic combination state to exchange state.

Microstructure refinement and strengthening mechanisms of a 9Cr oxide dispersion strengthened steel by zirconium addition

Energy Technology Data Exchange (ETDEWEB)

Xu, Hai Jian; Lu, Zheng; Wang, Dong Mei; Liu, Chunming [Key Laboratory for Anisotropy and Texture of Materials (Ministry of Education), School of Materials Science and Engineering, Northeastern University, Shenyang (China)

2017-02-15

To study the effects of zirconium (Zr) addition on the microstructure, hardness and the tensile properties of oxide dispersion strengthened (ODS) ferritic-martensitic steels, two kinds of 9Cr-ODS ferritic-martensitic steels with nominal compositions (wt.%) of Fe-9Cr-2W-0.3Y{sub 2}O-3 and Fe-9Cr-2W-0.3Zr-0.3Y{sub 2}O{sub 3} were fabricated by the mechanical alloying (MA) of premixed powders and then consolidated by hot isostatic pressing (HIP) techniques. The experimental results showed that the average grain size decreases with Zr addition. The trigonal δ-phase Y{sub 4}Zr{sub 3}O{sub 12} oxides and body-centered cubic Y{sub 2}O{sub 3} oxides are formed in the 9Cr-Zr-ODS steel and 9Cr non-Zr ODS steel, respectively, and the average size of Y{sub 4}Zr{sub 3}O{sub 12} particles is much smaller than that of Y{sub 2}O{sub 3}. The dispersion morphology of the oxide particles in 9Cr-Zr-ODS steel is significantly improved and the number density is 1.1 x 10{sup 23}/m{sup 3} with Zr addition. The 9Cr-Zr-ODS steel shows much higher tensile ductility, ultimate tensile strength and Vickers hardness at the same time.

Starting of H9ANFNb(P91) steel tubing production for energetics in domestic steel-works; Uruchomienie w krajowych hutach produkcji rur ze stali H9AMFNb(P91) przeznaczonych dla energetyki

Energy Technology Data Exchange (ETDEWEB)

Wiedermann, J. [Instytut Metalurgii Zelaza, Gliwice (Poland); Bieniek, K. [Huta Jednosc, Siemianowice Slaskie (Poland); Pogoda, K. [Huta Batory, Chorzow (Poland)

1996-12-31

The results of primary investigations and attempt of ferritic steel H9AMFNb production in domestic steel-works have been reported. The prototype series of tubes for energetic boilers have been tested and their mechanical properties determined. It has been found the applicability of the material for use in energetics. 9 refs, 4 figs, 3 tabs.

Thermal creep properties of alloy D9 stainless steel and 316 stainless steel fuel clad tubes

International Nuclear Information System (INIS)

Latha, S.; Mathew, M.D.; Parameswaran, P.; Bhanu Sankara Rao, K.; Mannan, S.L.

2008-01-01

Uniaxial thermal creep rupture properties of 20% cold worked alloy D9 stainless steel (alloy D9 SS) fuel clad tubes for fast breeder reactors have been evaluated at 973 K in the stress range 125-250 MPa. The rupture lives were in the range 90-8100 h. The results are compared with the properties of 20% cold worked type 316 stainless steel (316 SS) clad tubes. Alloy D9 SS were found to have higher creep rupture strengths, lower creep rates and lower rupture ductility than 316 SS. The deformation and damage processes were related through Monkman Grant relationship and modified Monkman Grant relationship. The creep damage tolerance parameter indicates that creep fracture takes place by intergranular cavitation. Precipitation of titanium carbides in the matrix and chromium carbides on the grain boundaries, dislocation substructure and twins were observed in transmission electron microscopic investigations of alloy D9 SS. The improvement in strength is attributed to the precipitation of fine titanium carbides in the matrix which prevents the recovery and recrystallisation of the cold worked microstructure

Correlation of hot-microhardness with elevated-temperature tensile properties of low activation ferritic steel

International Nuclear Information System (INIS)

Hsu Chenyih

1986-01-01

Hot microhardness and elevated temperature tensile tests have been performed on 9Cr-2.5W-0.3V-0.15C(GA3X) low activation ferritic steel at temperatures from 20 0 C to 650 0 C. The uniform elongation of the tensile test correlated well with the ductility parameter of the microhardness test. The hot-microhardness test showed a sensitive response to the softening and changes in ductility of the GA3X steel. The ultimate tensile strength and 0.2% yield strength of this steel correlated well with hot microhardness data at test temperatures up to 400 0 C using Cahoon's expressions σ uts = (H/2.9)(n/0.217) n and σ ys = (H/3)(0.1) n , respectively, where H is the diamond pyramid hardness and n is the strain hardening exponent. A 20-30% underestimate of tensile strengths were obtained using Cahoon's expressions at temperatures above 400 0 C, which is probably attributed to creep deformation and may be improved by selecting a proper loading condition during the hardness test. (orig.)

Ultra low carbon bainitic (ULCB) steels after quenching and tempering

International Nuclear Information System (INIS)

Lis, A.K.; Lis, J.; Kolan, C.; Jeziorski, L.

1998-01-01

The mechanical and Charpy V impact strength properties of new advanced ultra low carbon bainitic (ULBC) steels after water quenching and tempering (WQT) have been investigated. Their chemical compositions are given. The nine continuous cooling transformation diagrams (CCT) of the new ULCB steel grades have been established. The CCT diagrams for ULCB N i steels containing 9% Ni - grade 10N9 and 5% Ni - grade HN5MVNb are given. The comparison between CCT diagrams of 3.5%Ni + 1.5%Cu containing steels grade HSLA 100 and HN3MCu is shown. The effect of the increase in carbon and titanium contents in the chemical composition of ULCB M n steels 04G3Ti, 06G3Ti and 09G3Ti on the kinetics of phase transformations during continuous cooling is presented by the shifting CCT diagrams. The Charpy V impact strength and brittle fracture occurence curves are shown. The effect of tempering temperature on tensile properties of WQT HN3MCu steel is shown and Charpy V impact strength curves after different tempering conditions are shown. The optimum tempering temperatures region of HN3MCu steel for high Charpy V impact toughness at law temperatures - 80 o C(193 K) and -120 o C(153 K) is estimated. The effect of tempering temperature on mechanical properties of HN5MVNb steel is given. The low temperature impact Charpy V toughness of HN5MVNb steel is shown. The optimum range of tempering temperature during 1 hour for high toughness of WQT HN5MVNb steel is given. HN3MCu and HN5MVNb steels after WQT have high yield strength YS≥690 MPa and high Charpy V impact toughness KV≥80 J at -100 o C (173K) and KCV≥50 J/cm 2 at - 120 o C (153K) so they may be used for cryogenic applications

Development of the SONIX software for the YuMO instrument at the IBR-2 reactor

International Nuclear Information System (INIS)

Kirilov, A.S.; Litvinenko, E.I.; Astakhova, N.V.; Murashevich, S.M.; Petukhova, T.B.; Yudin, V.E.; Gordelij, V.I.; Islamov, A.Kh.; Kuklin, A.I.

2003-01-01

The main results of the modernization of the software complex of the YuMO spectrometer are described. The comparison of the previous MS-DOS based software and new OS-9 based one is carried out. The advantages and disadvantages of each program are described. The main features of the new software complex and the results of its long-term operation are presented. It is shown that the software upgrade essentially improved the spectrometer control. (author)

Konsep Pendidikan Akhlak dan Dakwah dalam Perspektif Dr. KH. Zakky Mubarak, MA

Directory of Open Access Journals (Sweden)

Muchtar Muchtar

2017-09-01

Full Text Available Research aims to understand role, and the concept of education and dakwah in perspective Dr. KH. Zakky Mubarak, MA. This research departs from looking at the phenomenon of human life is increasingly complex, entered the modern life and globalization present and the future, wich is characterized by technical and professional paced lives, is forecast to many people ignore the moral and religious in individual and social life. The concept of moral education in the perspective of Dr. KH. Zakky Mubarak, MA that establishes the character of the learners, provide good role models, develop the moral high level, and then apply the knowledge of good character and exemplary in real life so it can become an ingrained habit. The concept of dakwah in perspective Dr. KH. Zakky Mubarak, MA at least two steps that need to be understood by a preacher, first that of bringing the wisdom, it means explaining the wisdoms contained in worship and other Islamic activities without patronizing impression, meaning a preacher should put the words and appropriate sentence appropriate to the circumstances . The second is to mau'idlah hasanah , means giving advice that touch the heart so that the message can be embedded in the memories of audience. Dr. KH. Zakky Mubarak, MA is one of the Nahdlatul Ulama cleric who spend their time preaching, either through a lecture or through scientific papers, scientific papers written contains a lot of moral education that can be used as a reference.  Keywords: Concept of Education and Dakwah, Zakky Mubarak, Nahdlatul Ulama Abstrak Penelitian ini bertujuan untuk mengetahui peran, serta konsep pendidikan akhlak dan dakwah dalam perspektif Dr. KH. Zakky Mubarak, MA. Kesimpulan penelitian ini bahwa Konsep pendidikan akhlak dalam perspektif Dr. KH. Zakky Mubarak, MA yaitu menanamkan pemahaman tentang akhlak terhadap peserta didik, memberikan keteladanan yang baik, mengembangkan pada akhlak tingkat tinggi, dan kemudian mengaplikasikan

Characteristics of Modified 9Cr-1Mo Steel for Reactor Pressure Vessel of Very High Temperature Gas Cooled Reactor

Energy Technology Data Exchange (ETDEWEB)

Kim, Sung Ho; Ryu, W. S.; Han, Chang Hee; Yoon, J. H.; Chang, Jong Hwa

2004-11-15

Many researches and developments have been progressed for the construction of VHTR by 2020 in Korea. Modified 9Cr-1Mo steel has been receiving attention for the application to the reactor pressure vessel material of VHTR. We collected and analyzed the research data for modified 9Cr-1Mo steel in order to understand the characteristics of modified 9Cr-1Mo steel. The modified 9Cr-1Mo steel is a modified alloy system similar to conventional 9Cr-1Mo grade ferritic steel. Modifications include additions of vanadium, niobium, and nitrogen, as well as lower carbon content. In this report, we summarized the change of microstructure and mechanical properties after tempering, thermal aging, and irradiation. Modified 9Cr-1Mo steel has high strength and thermal conductivity, low thermal expansion, and good resistance to corrosion. But the irradiation embrittlement behavior of modified 9Cr-1Mo steel should be evaluated and the evaluation methodology also should be developed. At the same time, the characteristics of weldment which is the weak part in pressure vessel should be evaluated.

Study of strength of Dsub(y)150 gate valve case, manufactured by centrifugal casting

International Nuclear Information System (INIS)

Umanskaya, L.G.; Semenov, P.V.; Tinyakov, V.G.; Babkina, R.I.; Khatuntsev, Eh.V.

1982-01-01

A process for manufacturing centrifugal-cast gate valve body is developed. Structural strength of such items, homogeneity, ductile and strength properties over the cross section as well as the metal susceptibility to embrittlement have been investigated. Three cast gate valve bodies have been taken: one - of 20GSL steel - for hydraulic testing, and two - of 15Kh1MFL steel - for investigation into the metal properties across the valve thickness. The strength properties of the centrifugal-cast gate valve body of 15Kh1M1FL steel are stated to meet the specifications. The gate valve metal ductility (delta and PSI) is twice as high as that of a sand-cast valve. The microstructure, strength and ductility are uniform both over wall thickness and over different body cross sections

Mechanical properties of permeable materials with an organized structure on the base of continuous metal fibers

International Nuclear Information System (INIS)

Karpinos, D.M.; Rutkovskij, A.E.; Zorin, V.A.; Ivanchuk, A.A.

1979-01-01

The mechanical properties were studied for permeable fibrous materials with an organized structure on the base of continuous metal fibers (from Kh18N9T steel) subjected to preliminary reprocessing volumetric net half-finished products. The effect of geometrical parameters of the net half-finished products and of their orientation in packing are shown to affect the mechanical properties within a wide range of porosities

9% Cr steel high temperature oxidation. Solutions investigated for improving corrosion resistance of the steel

Energy Technology Data Exchange (ETDEWEB)

Evin, Harold Nicolas; Heintz, Olivier; Chevalier, Sebastien [UMR 5209 CNRS-Bourgogne Univ. (France). Lab. Interdisciplinaire Carnot de Bourgogne; Foejer, Cecilia; Jakani, Saad; Dhont, Annick; Claessens, Serge [OCAS N.V. ArcelorMittal Global R and D, Gent (Belgium)

2010-07-01

The improvement of high temperature oxidation resistance of low chromium content steels, such as T/P91, is of great interest in regards with their application in thermal power generating plants. Indeed, they possess good creep properties, but are facing their limits of use at temperature higher than 600 C, due to accelerated corrosion phenomena. Good knowledge of the mechanisms involved during their oxidation process is needed to prevent the degradation of the materials and to extend life time of the power plants components. Oxide layers thermally grown, on 9% Cr steels (provided by OCAS N.V), during isothermal tests between 600 C and 750 C in laboratory air under atmospheric pressure were investigated, by Scanning Electron Microscopy (SEM) and X-ray diffraction (XRD). The oxidation behaviour appeared very limited at 750 C, due to the presence of a breakaway, which can be linked to iron porous oxide grown over the surface of the samples. ''In situ'' X-ray Photoelectron spectroscopy (XPS) analyses were performed in air at 600 C after short exposures (between 5 min and 25 h). A complex mixture of iron oxide, Cr{sub 2}O{sub 3} and Cr (VI) species were characterized in the scales. The in-situ analyses were compared and related to XPS analyses performed on thick oxide scales formed on samples oxidized in air at 600 C for 100h. An oxidation mechanism is then proposed to understand the oxide scale growth in the temperature range 600 - 750 C. The second step of this study consists in improving the high temperature corrosion resistance of these steels without modifying their mechanical properties. Thus several solutions were investigated such as MOCVD coatings, pack cementation coatings, and tested in cycle conditions prior. (orig.)

Fertilizer-n uptake and distribution in rice plants using 15N tracer technique

International Nuclear Information System (INIS)

Yan Juan; Shen Qirong; Yin Bin; Wan Xinjun

2009-01-01

Fertilizer-nitrogen (N) uptake and distribution in rice were studied using 15 N tracer technique. The results obtained were as follows. At the tillering, jointing and booting, and anthesis stages, 23.1%, 8.3% and 19.9% of N were taken from fertilizer applied in base (N1), tillering (N2) and jointing and booting (N3), respectively. The 15 N translocation from anthesis to maturity was in the order of N3>N1>N2, but the 15 N translocation efficiency was higher in N1 (base fertilizer treatment) than in the other two treatments. At maturity, the 15 N distribution in straw in the treatments of N1, N2 and N3 was only 24.3%, 26.7% and 30.4%, respectively. No matter what time the N fertilizer was applied, the 15 N uptake was mostly distributed in leaves, then in the sheath, the least in stem, and 15 N distribution in spike increased with the increased 15 N translocation from nutritional organs to spike after anthesis. The study also showed that the 15 N uptake at maturity in N1, N2 and N3 treatments was 10.3%, 5.9% and 12.4%, respectively. The results indicated that (1) when soil N content was not high, the base fertilizer application was important to rice growth, and optimal increment might help increase tillering, and improve rice quality; (2) the initiation fertilizer significantly promoted quantities during grain filling, and thus application of N fertilizer in initiation was of considerable advance in increasing N harvest index (NHI); (3) the rice plants absorbed less N applied in tillering stage due to a big N loss in that period. Therefore a little bit increase of base N fertilizer with no or very small amount of tillering fertilizer, together with some topdressing of N fertilizer during initiation could improve N uptake by rice. (authors)

Microstructural Stability and Oxidation Resistance of 9-12 Chromium Steels at Elevated Temperatures

Energy Technology Data Exchange (ETDEWEB)

Dogan, O.N.; Alman, D.E.; Jablonski, P.D.; Hawk, J.A.

2006-05-01

Various martensitic 9-12 Cr steels are utilized currently in fossil fuel powered energy plants for their good elevated temperature properties such as creep strength, steam side oxidation resistance, fire side corrosion resistance, and thermal fatigue resistance. Need for further improvements on the properties of 9-12 Cr steels for higher temperature (>600oC) use is driven by the environmental concerns (i.e., improve efficiency to reduce emissions and fossil fuel consumption). In this paper, we will discuss the results of the research done to explore new subsitutional solute solution and precipitate hardening mechanisms for improved strength of 9-12 Cr martensitic steels. Stability of the phases present in the steels will be evaluated for various temperature and time exposures. A comparison of microstructural properties of the experimental steels and commercial steels will also be presented.

The influence of a Ce surface treatment on oxidation behavior of a commercial (P91) and several experimental steels containing 9 to 12 weight percent Cr was examined at 650ºC in flowing dry and moist air. The oxidation behavior of all the alloys without the Ce modification was significantly degraded by the presence of moisture in the air during testing. For instance the weight gain for P91 was two orders of magnitude greater in moist air than in dry air. This was accompanied by a change in oxide scale from the formation of Cr-based scales in dry air to the formation of Fe-based scales in moist air. The Ce surface treatment was very effective in improving the oxidation resistance of the experimental steels in both moist and dry air. For instance, after exposure to moist air at 650ºC for 2000 hours, an experimental alloy with the cerium surface modification had a weight gain three orders of magnitude lower than the alloy without the Ce modification and two orders of magnitude lower than P91. The Ce surface treatment suppressed the formation of Fe-based scales and

On the hypothesis of agressive environment effect evaluation on the cyclic cracking resistance in metals and alloys

International Nuclear Information System (INIS)

Romaniv, O.N.; Gladkij, Ya.N.; Nikiforchin, G.N.

1978-01-01

Experimental data on studying static and cyclic cracking resistances of steels in water and inert gaseous media are given. Presented are experimental values of threshold coefficients of stress intensities for a series of the systems: metal (the 4340 steel of the 45KhN2MFA type, 12Ni-5Cr-3Mo steel, 9Ni-4Co-0.25C steel and others)-medium. On the base of the above data analysis and representations on the mechanism of crack growth under conditions of permanent and variable load effects the conclusion is drawn on the groundlessness of the hypothesis of contribution superposition resulted from pure fatigue and corrosion-static factors when estimating cracking resistance of metals and alloys

Creep Strength of Dissimilar Welded Joints Using High B-9Cr Steel for Advanced USC Boiler

Science.gov (United States)

Tabuchi, Masaaki; Hongo, Hiromichi; Abe, Fujio

2014-10-01

The commercialization of a 973 K (700 °C) class pulverized coal power system, advanced ultra-supercritical (A-USC) pressure power generation, is the target of an ongoing research project initiated in Japan in 2008. In the A-USC boiler, Ni or Ni-Fe base alloys are used for high-temperature parts at 923 K to 973 K (650 °C to 700 °C), and advanced high-Cr ferritic steels are planned to be used at temperatures lower than 923 K (650 °C). In the dissimilar welds between Ni base alloys and high-Cr ferritic steels, Type IV failure in the heat-affected zone (HAZ) is a concern. Thus, the high B-9Cr steel developed at the National Institute for Materials Science, which has improved creep strength in weldments, is a candidate material for the Japanese A-USC boiler. In the present study, creep tests were conducted on the dissimilar welded joints between Ni base alloys and high B-9Cr steels. Microstructures and creep damage in the dissimilar welded joints were investigated. In the HAZ of the high B-9Cr steels, fine-grained microstructures were not formed and the grain size of the base metal was retained. Consequently, the creep rupture life of the dissimilar welded joints using high B-9Cr steel was 5 to 10 times longer than that of the conventional 9Cr steel welded joints at 923 K (650 °C).

Characteristics of centrifugally cast GX25CrNiSi18-9 steel

Directory of Open Access Journals (Sweden)

R. Zapała

2011-07-01

Full Text Available The paper presents the results of microstructural examinations of the industrial heat-resistant centrifugally cast GX25CrNiSi18-9 steel characterised by increased content of Cu. The study included changes in the microstructure of base cast steel respective of the steel held at a temperature of 900 and 950°C for 48 hours. Based on the results obtained, an increase in microhardness of the examined cast steel matrix with increasing temperature was stated, which was probably caused by fine precipitates enriched in Cr, Mo, and C forming inside the matrix grains.The layer of scale formed on the tested cast steel oxidised in the atmosphere of air at 900 and 950°C was characterised by an increased tendency to degradation with increasing temperature of the conducted tests.

The Near-Earth Encounter of Asteroid 308635 (2005 YU55): Thermal IR Observations

Science.gov (United States)

Lim, Lucy F.; Emery, J. P.; Moskovitz, N. A.; Busch, M. W.; Yang, B.; Granvik, M.

2012-10-01

The near-Earth approach (0.00217 AU, or 0.845 lunar distances) of the C-type asteroid 308635 (2005 YU55) in November 2011 presented a rare opportunity for detailed observations of a low-albedo NEA in this size range. As part of a multi-telescope campaign to measure visible and infrared spectra and photometry, we obtained mid-infrared ( 8 to 22 micron) photometry and spectroscopy of 2005 YU55 using Michelle [1] on the Gemini North telescope on UT November 9 and 10, 2011. An extensive radar campaign [2] together with optical lightcurves [3,4] established the rotation state of YU55. In addition, the radar imaging resulted in a shape model for the asteroid, detection of numerous boulders on its surface, and a preliminary estimate of its equatorial diameter at 380 +/- 20 m. In a preliminary analysis, applying the radar and lightcurve-derived parameters to a rough-surface thermophysical model fit to the Gemini/Michelle thermal emission photometry results in a thermal inertia range of approximately 500 to 1500 J m-2 s-1/2 K-1, with the low-thermal-inertia solution corresponding to the small end of the radar size range and vice versa. Updates to these results will be presented and modeling of the thermal contribution to the measured near-infrared spectra from Palomar/Triplespec and IRTF/SpeX will also be discussed. The authors gratefully acknowledge the assistance of observatory staff and the support of the NASA NEOO program (LFL and JPE), the Carnegie fellowship (NAM), and NASA AES, NSF, and the NRAO Jansky Fellowship (MWB). [1] De Buizer, J. and R. Fisher, Proc. Hris (2005), pp. 84-87. [2] Busch, M.W. et al., ACM (2012), abstract #6179. [3] Warner, B., MPBull 39 (2), 84 [4] Pravec, P.

Swelling and irradiation creep of neutron irradiated 316Ti and 15-15Ti steels

International Nuclear Information System (INIS)

Maillard, A.; Touron, H.; Seran, J.L.; Chalony, A.

1992-01-01

The global behavior, the swelling and irradiation creep resistances of cold worked 316Ti and 15-15Ti, two variants of austenitic steels in use as core component materials of the French fast reactors, are compared. The 15-15Ti leads to a significant improvement due to an increase in the incubation dose swelling. The same phenomena observed on 316Ti are found on 15-15Ti. All species without fuel like samples, wrappers or empty clad swell and creep less than fuel pin cladding irradiated in the same conditions. To explain the swelling difference, as for 316Ti, thermal gradient is also invoked but the irradiation creep difference is not yet clearly understood. To predict the behavior of clads it is indispensable to study the species themselves and to use specific rules. All results confirm the good behavior of 15-15Ti, the best behavior being obtained with the 1% Si doped version irradiated up to 115 dpa

Microstructure and mechanical properties of friction stir welded 9Cr ODS steel

International Nuclear Information System (INIS)

Min, Hyoung Kee; Kang, Suk Hoon; Noh, Sanghoon; Lee, Jung Gu; Jang, Jinsung; Kim, Tae Kyu

2013-01-01

It is well known that the welding of ODS steel with a conventional melting.solidification process is not adequate to reserve nano-oxide particles in the matrix homogeneously. To reserve nano-oxide particles in the matrix homogeneously, friction stir welding (FSW) is the most promising technique to join ODS alloys. In this study, the effects of FSW on the microstructure and mechanical properties of a ODS steel were studied to apply the FSW process to 9Cr ODS steels. Microstructures were observed by means of optical microscopy, electron backscatter diffraction (EBSD) and transmission electron microscopy (TEM). A tensile test and hardness test were carried out to the investigate mechanical properties. FSW could successfully produce defect-free welds on ODS plates. FSW produced a fine grain structure consisting of ferrite and martensite. Tensile strengths and elongations of the SZs were excellent at 298 K, compared to those of the BM. This study suggests that FSW might be an appropriate welding method of ODS steels. Oxide dispersion strengthened (ODS) ferritic-martensitic (FM) steel containing 9 wt%Cr is a promising candidate material for high temperature components operating in aggressive environments such as nuclear fusion and fission systems because of the excellent elevated temperature strength, corrosion and radiation resistance. These characteristics come from microstructures consisting of fine grains and nano-oxide particles dispersed in high number density. However, for more applications of ODS steel in nuclear systems, its weldability is the one of the barrier to be solved

Microstructures and mechanical properties of 9Cr oxide dispersion strengthened steel produced by spark plasma sintering

Energy Technology Data Exchange (ETDEWEB)

Xie, Rui [Key Laboratory for Anisotropy and Texture of Materials (Ministry of Education), School of Materials Science and Engineering, Northeastern University, Shenyang 110819 (China); School of Metallurgy, Northeastern University, Shenyang 110819 (China); Lu, Zheng, E-mail: luz@atm.neu.edu.cn [Key Laboratory for Anisotropy and Texture of Materials (Ministry of Education), School of Materials Science and Engineering, Northeastern University, Shenyang 110819 (China); Lu, Chenyang; Li, Zhengyuan [Key Laboratory for Anisotropy and Texture of Materials (Ministry of Education), School of Materials Science and Engineering, Northeastern University, Shenyang 110819 (China); Ding, Xueyong [School of Metallurgy, Northeastern University, Shenyang 110819 (China); Liu, Chunming [Key Laboratory for Anisotropy and Texture of Materials (Ministry of Education), School of Materials Science and Engineering, Northeastern University, Shenyang 110819 (China)

2017-02-15

Highlights: • A 9Cr-ODS steel was produced by mechanical alloying and spark plasma sintering. • Bimodal grain size distribution was observed. • Formation mechanism of bimodal grain size distribution was discussed. • The size and number density of nanoscale particles were obtained by SAXS and HRTEM. • The contribution of nano-sized particles to yield strength is dominating. - Abstract: 9Cr oxide dispersion strengthened (ODS) steel was fabricated by mechanical alloying (MA) and spark plasma sintering (SPS). The nano-sized particles, grain size distribution and mechanical properties of 9Cr-ODS steel sintered at 950 °C were studied by synchrotron radiation small angle X-ray scattering (SAXS), high-resolution transmission electron microscopy (HRTEM), electron backscatter diffraction (EBSD) and tensile experiment. The results showed that bimodal grain size distribution in the matrix is observed, which is attributed to the heterogeneous recrystallization process during the SPS. High-density nano-sized Y{sub 2}Ti{sub 2}O{sub 7} and some large oxides of Cr{sub 2}Mn(Ti)O{sub 4} are formed in 9Cr-ODS steel. The number density and average size of Y{sub 2}Ti{sub 2}O{sub 7} obtained from SAXS are 4.72 × 10{sup 22}/m{sup 3} and 4.4 nm, respectively. The yield strengths of 9Cr-ODS steel fabricated by SPS are compared with the typical 9Cr-ODS steel produced by HIP.

Safety conditions of using structural steels under high temperature and pressures in hydrogen containing environment

International Nuclear Information System (INIS)

Asviyan, M.B.

1984-01-01

The method for establishing full-strength conditions was suggested on the base of results of creep-rupture test of tube samples under hydrogen pressure and according to permissible stresses in neutral medium. Applicability of the method was considered taking St3 and 12KhM steels as examples. It was shown that the use of suggested dependences and special efficiency factors enables to forecast endurance limit for the given steel grade and assigned partial hydrogen pressure without labour-intensive test conducting

Analysis of ductile-brittle transition shifts for standard and miniature bending specimens of irradiated steel

International Nuclear Information System (INIS)

Korshunov, M.E.; Korolev, Yu.N.; Krasikov, E.A.; Gabuev, N.N.; Tykhmeev, D.Yu.

1996-01-01

A study is made to reveal if there is a correlation between shifts in temperature curves obtained when testing thin plates and standard specimens on impact bending and fracture toughness. The tests were carried out using steel 25Kh3NM specimens irradiated by 6 x 10 19 cm -2 neutron fluence. A conclusion is made about the possibility to evaluate the degree of radiation-induced embrittlement of reactor steels on the basis of thin plate testing under quasistatic loads [ru

Stress-controlled inelastic behavior of modified 9 Cr-1 Mo steel at elevated temperatures

International Nuclear Information System (INIS)

Taguchi, Kosei.

1989-01-01

Interest in the ferritic steels of higher chromium concentration has increased recently because of an economical combination of mechanical and corrosion properties at elevated temperatures. A modified 9 Cr-1 Mo ferritic steel, developed in the United States, has been expected as an alternative structural material for fast breeder reactor components, in which Type 304 stainless steel or 2.25 Cr-1 Mo steel is currently used. For application of this material to the structural components, a lot of work has been done to develop evaluation methods for the deformation behavior and strength properties. The authors have studied the inelastic behavior and the creep-fatigue properties of modified 9 Cr-1 Mo steel at elevated temperatures, and proposed a constitutive equation and a creep-fatigue damage equation based on the overstress concept. In this paper, the applicability is discussed of the constitutive equation to stress-controlled inelastic behavior, such as creep strain hardening and stress cycling

TRANSFORMASI KURIKULUM PESANTREN: Telaah Pemikiran KH. MA. Sahal Mahfudh dan Nurcholish Madjid

OpenAIRE

Mukhlison Effendi; Suradi Suradi

2016-01-01

Abstract; Islamic boarding school is an indigenous Indonesia. Some contribution that given in the Islamization process, create a good community literacy and culture are very large. One reason, because there are Islamic boarding school curriculum transformation. Most influential enticement are KH. MA. Sahal Mahfudh and Nurcholish Madjid enticement. To knowing and determine the transformation both of those figures, the researcher take focus of study as: 1) the speculation of KH. MA. Sahal Mahfu...

Metodologi Fatwa K.H. Muhammad Syaf’i Hadzami

Directory of Open Access Journals (Sweden)

Muhammad Ardiansyah

2018-01-01

Full Text Available Fatwa is one of the heavy mandates on the shoulders of Moslem scholars. There are some conditions that must be fulflled before the fatwa could be used to solve the problems of the people. Basically, the fatwa replaces the task of the Prophet in conveying the shari’a law, then the scholars did not dare to be reckless in declaring any fatwa. Therefore, being a mufti is not only required by reading the translation of al-Qur’an or Hadith, or by searching on the google, or by copying broadcasts in social media. According to al-Shirazi, the intellectual condition that must be required to be a mufti is deep understanding toward al-Qur’an and Hadith, also understanding sources of speech such as ḥaqîqah-majâz, ‘âmm-khâṣṣ, Arabic language, nâsikh-mansûkh, ijmâ’, ikhtilaf, and tartîb al-adillah. While the moral requirements to be a mufti according to Imam Ahmad bin Hanbal are having pure intention, having broad knowledge, patience, and soul, having strong mentality to fulfl the task, having suffciency of life to avoid being influenced by others, and understanding the condition of society. This paper attempts to examine the fatwas of a mufti from Betawi who had lived in the modern era known as Mu’allim Syaf’i Hadzami. The fatwas were collected in a work entitled Tawḍîḥ al-Adillah. In this article, the author has concluded that Mu’allim uses eight complementary and relevant fatwa methodologies to solve today’s problems

Effect of N+Cr alloying on the microstructures and tensile properties of Hadfield steel

International Nuclear Information System (INIS)

Chen, C.; Zhang, F.C.; Wang, F.; Liu, H.; Yu, B.D.

2017-01-01

The microstructures and tensile behaviors of traditional Hadfield steel, named Mn12 steel, and Hadfield steel alloyed with N+Cr, named Mn12CrN steel were studied through optical microscopy, transmission electron microscopy, and scanning electron microscopy, among others. Three different tensile strain rates of 5×10 −4 , 5×10 −3 , and 5×10 −2 s −1 were selected in the tensile test. The deformation microstructures and fracture morphologies of the two steels after fracture in the tensile test were observed to analyze the tensile deformation response to different tensile strain rates. Results showed that the grain size of Mn12CrN steel was evidently refined after alloying with N+Cr. The grain would not become abnormally coarse even with increasing austenitizing temperature. During tensile deformation, the strength and plasticity of Mn12CrN steel were superior to those of Mn12 steel at the same strain rate. With increasing the strain rate, the changes in strength and plasticity of Mn12CrN steel were less sensitive to tensile strain rate compared with Mn12 steel. The effects of grain refinement and N+Cr alloying on dynamic strain aging and deformation twining behaviors were responsible for this lack of sensitivity to strain rate.

Development of ferritic-martensitic P9 steel for wrapper application in future SFRs

International Nuclear Information System (INIS)

Choudhary, B.K.; Mathew, M.D.; Isaac Samuel, E.; Moitra, A.

2011-01-01

The paper deals with the outcome of the research and development efforts directed towards the development of ferritic-martensitic P9 steel for wrapper application in future sodium cooled fast reactors with an objective to achieve high fuel burnup and more economical nuclear energy. The important and critical issues involved for the development of P9 wrappers such as optimisation of chemical composition in terms of trace elements like sulphur and phosphorous and appropriate thermo-mechanical treatments along with thermal ageing and irradiation effects on fracture properties have been discussed. Tensile properties evaluated at temperatures ranging from 300 to 873 K on the experimental three heats of P9 steel with different silicon contents and made using primary vacuum induction melting followed by secondary electro slag refining route, have been presented. Fracture behaviour examined mainly in terms of ductile to brittle transition temperature and upper shelf energy provided encouraging results. Based on these investigations, a roadmap has been drawn to make experimental P9 steel wrappers for tests in fast breeder test reactor and prototype fast breeder reactor. (author)

Analysis of High Temperature Deformed Structure and Dynamic Precipitation in W9Mo3Cr4V Steel

Institute of Scientific and Technical Information of China (English)

无

2001-01-01

With TEM、SEM, various high-temperature deformed structures inW9Mo3Cr4V steel were investigated. The sub-structures，recrystallized nuclei, as well as the dynamic precipitation were also studied and analyzed. The relationship between recrystallized structures and dynamic precipitation was discussed. The results showed that the deformed structures in W9Mo3Cr4V steel are more complicated than those in low alloy steels. Because W9Mo3Cr4V steel is a high-speed steel, there are a large number of residual carbides on the matrix. Also, much dynamic precipitating carbides will precipitate during deformation at high temperature.

YU Ren-cun(郁仁存)——A Famous Oncologist in Integrative Medicine

Institute of Scientific and Technical Information of China (English)

2008-01-01

@@ YU Ren-cun was born on August 1,1934.After graduating from Jiangxi Medical College in 1955,he took part in the very first Western Doctors' Class for Learning Traditional Chinese Medicine (TCM) held in Beijing from March 1959 to December 1961.Prof.YU systematically learned TCM while taking this class.Since 1962,he has been working in the Beijing Hospital of Traditional Chinese Medicine,eventually being promoted to a Chief Physician by the Beijing Municipal Government in May of 1981.In 1997,Prof.YU was selected as a well-known veteran for the National TCM Doctor Inheritance Work by the State Administration of Traditional Chinese Medicine (SATCM).The State Council of China has awarded him a special subsidy every month for his excellent work.

Praktik Pemikiran Inklusif-Sosial KH M Sholeh Bahruddin Ngalah sebagai Manifestasi Pendidikan Multikultural Pesantren

Directory of Open Access Journals (Sweden)

M Anang Sholikhudin

2016-12-01

Full Text Available Dalam sejarah hidupnya, praktik pemikiran inklusif-sosial Kiai Sholeh sangat dipengaruhi oleh beberapa hal. Pertama, atas perintah ayahanda dengan pesan seperti berikut: “sak temene dek pasar, dek masjid, dek dalan, kabeh iku dulurmu (sesungguhnya baik di pasar, di masjid, maupun di jalanan, di seluruh tempat itu ada saudaramu.” Kedua, penerapan teori Abraham, yakni mencontoh perilaku ayahanda KH M Bahruddin Kalam (almarhum dan juga perilaku kakek KH M Kalam (almarhum. Ketiga, praktik dari rukun Tarekat Naqshabandiyah pada poin kelima dan keenam, yakni “ambugusi kabeh konco, cilik gede, lanang wadon, enom tuo, lan ambagusi kabeh makhluk (bergaul secara baik dengan semua teman, baik kecil maupun besar, laki-laki maupun perempuan, muda maupun tua, dan bergaul secara baik dengan semua makhluk.” Penelitian ini memfokuskan pada praktik pemikiran inklusif-sosial KH M Sholeh Bahruddin dengan model studi kasus, pendekatan yang dipakai adalah expose facto. Data diambil melalui observasi, wawancara serta dokumentasi. Penelitian menyimpulkan bahwa praktik pemikiran inklusif-sosial KH.. M. Sholeh Bahruddin sebenarnya mempertemukan misi perintah masing-masing agama (Islam, Kristen, Katolik, Budha dan Konghucu untuk membangun perdamaian, keamanan dan memelihara kasih sayang bersama-sama dan meminimalisir terjadinya konflik agama. || In the history of his life, the practice of inclusive social thought by Kiai Sholeh greatly influenced by several things. First, on the orders of his father with the following message: “In the markets, in the mosques, as well as on the streets, all over the places there are your brothers.” Secondly, the application of Abraham’s theory, which was practiced by KH M Bahruddin Kalam, the father (deceased of Kiai Sholeh, as well as KH M Kalam, the grandfather (deceased of Kiai Sholeh. Third, the practice of the Naqshabandi pillars that say: “being good with all friends, both small and great, both men and women, young

Acoustic emission under biaxial stresses in unflawed 21-6-9 and 304 stainless steel

International Nuclear Information System (INIS)

Hamstad, M.A.; Leon, E.M.; Mukherjee, A.K.

1980-01-01

Acoustic emission (AE) testing has been carried out with uniaxial and biaxial (2:1 stress ratio) stressing of smooth samples of 21-6-9 and 304 stainless steel (SS). Uniaxial testing was done with simple tensile and compression samples as well as with the special biaxial specimens. Biaxial tensile stressing was accomplished with a specially designed specimen, which had been used previously to characterize AE in 7075 aluminum under biaxial stressing. Results were obtained for air-melt and for vacuum-melt samples of 21-6-9 SS. The air-melt samples contain considerably more inclusion particles than the vacuum-melt samples. For the 304 SS, as received material was examined. To allow AE correlations with microstructure, extensive characterization of the 21-6-9 microstructure was carried out. Significant differences in AE occur in biaxially stressed specimens as compared to uniaxially stressed samples. 15 figures, 3 tables

Seasonal changes in nitrogen availability, and root and microbial uptake of ¹⁵N¹³C₉-phenylalanine and ¹⁵N-ammonium in situ at a temperate heath

DEFF Research Database (Denmark)

Andresen, Louise C.; Michelsen, Anders; Jonasson, Sven Evert

2011-01-01

In the plant biosynthesis of secondary compounds, phenylalanine is a precursor of condensed tannins. Tannins are deposited into the soil in plant root exudates and dead plant material and have been suggested to precipitate some soil nutrients and hence reduce nutrient availability for plants. Free...... amino acid,inorganic and microbial N concentration during the growing season was investigated in an ecosystem with a natural tannin chemosphere. The influence of tannins on the uptake of nitrogen in plants and microbes was followed by injecting tannic acid (TA), ammonium-15N and phenylalanine-15N/13C9...

Influence of crystallization conditions on formation and distribution of nonmetallic inclusions in steels

International Nuclear Information System (INIS)

Efimov, V.A.

1977-01-01

The processes were studied of the formation and the distribution of nonmetallic inclusions and the chemical inhomogeneity formation during the solidification of h steel. The variation of the character of oxides and sulfides across ingots was shown by considering st 25 and 20 Kh steels. To improve the distribution of inclusions and the stability of properties throughout the body of ingots, it is recommended to throughly deoxidize the metal, to raise the rate of solidification, to reduce the temperature gradient, to employ powder cooling agents, to use casting under a blanket of slag, to modify steel by active elements (r.e.e., Ca, Ba, Zr, B) which affect favourably the nature and the shape of the nonmetallic phase

MTS-MD of Biomolecules Steered with 3D-RISM-KH Mean Solvation Forces Accelerated with Generalized Solvation Force Extrapolation.

Science.gov (United States)

Omelyan, Igor; Kovalenko, Andriy

2015-04-14

with explicit solvent. We have been able to fold the miniprotein from a fully denatured, extended state in about 60 ns of quasidynamics steered with 3D-RISM-KH mean solvation forces, compared to the average physical folding time of 4-9 μs observed in experiment.

Effect of N+Cr alloying on the microstructures and tensile properties of Hadfield steel

Energy Technology Data Exchange (ETDEWEB)

Chen, C. [State Key Laboratory of Metastable Materials Science and Technology, Yanshan University, Qinhuangdao 066004 (China); Zhang, F.C., E-mail: zfc@ysu.edu.cn [State Key Laboratory of Metastable Materials Science and Technology, Yanshan University, Qinhuangdao 066004 (China); National Engineering Research Center for Equipment and Technology of Cold Strip Rolling, Yanshan University, Qinhuangdao 066004 (China); Wang, F. [State Key Laboratory of Metastable Materials Science and Technology, Yanshan University, Qinhuangdao 066004 (China); Liu, H.; Yu, B.D. [China Railway Shanhaiguan Bridge Group Co. LTD, Qinhuangdao 066205 (China)

2017-01-02

The microstructures and tensile behaviors of traditional Hadfield steel, named Mn12 steel, and Hadfield steel alloyed with N+Cr, named Mn12CrN steel were studied through optical microscopy, transmission electron microscopy, and scanning electron microscopy, among others. Three different tensile strain rates of 5×10{sup −4}, 5×10{sup −3}, and 5×10{sup −2} s{sup −1} were selected in the tensile test. The deformation microstructures and fracture morphologies of the two steels after fracture in the tensile test were observed to analyze the tensile deformation response to different tensile strain rates. Results showed that the grain size of Mn12CrN steel was evidently refined after alloying with N+Cr. The grain would not become abnormally coarse even with increasing austenitizing temperature. During tensile deformation, the strength and plasticity of Mn12CrN steel were superior to those of Mn12 steel at the same strain rate. With increasing the strain rate, the changes in strength and plasticity of Mn12CrN steel were less sensitive to tensile strain rate compared with Mn12 steel. The effects of grain refinement and N+Cr alloying on dynamic strain aging and deformation twining behaviors were responsible for this lack of sensitivity to strain rate.

Comparison of congener profiles of polychlorinated biphenyls between Yu-cheng children and a potential food source

Energy Technology Data Exchange (ETDEWEB)

Lung Shih-Chun Candice [Research Center for Environmental Changes, Academia Sinica, Taipei (Taiwan); Guo Yu-Liang Leon; Chang Ho-Yuan [Dept. of Environmental and Occupational Health, Coll. of Medicine, National Cheng Kung Univ., Tainan (Taiwan)

2004-09-15

In 1979, about two thousand people in central Taiwan were intoxicated by consumption of the rice oil that was contaminated with polychlorinated biphenyls (PCBs). This ''Yu-cheng'' incident was one of the two human tragedies which people ingested substantial amounts of PCBs within a short period of time. Some of the follow-up epidemiological studies focused on the children born to the exposed mothers, the Yu-cheng children, since they could be exposed to PCBs via breast-feeding or transplacental transfer. This report presents the results of the serum PCB levels of the 21 Yu-cheng children with a congener-specific analysis. On the other hand, fish consumption is thought to be the single most important exposure route to PCBs to the general public; thus, it is crucial to understand PCB exposure from fish consumption. In a separated study to assess PCB contamination in fish, PCB congener concentrations in tilapia (Oreochromis hybrids), the most popular fish in Taiwan, were evaluated. The consumption quantity of tilapia is the highest throughout the Island. It is mostly farmed in fresh water but can also be bred in saltwater. This report presents the concentrations and profiles in the serums of the Yu-cheng children. The congener profile is compared with PCB profile in the serum of Yu-cheng women reported previously and that in one of the potentially significant exposure source, tilapia, conducted in a separated work. Remarkable similarity between the profile of Yu-cheng children and that of the tilapia is revealed and discussed.

Structure and properties of joints of two-ply steel using ''elastic'' explosives

International Nuclear Information System (INIS)

Gel'man, A.S.; Savel'ev, S.A.; Kulakevich, Ya.S.; Sharypov, N.A.; Drogovejko, I.Z.; Domolego, I.E.

1980-01-01

Some experimental data on structure and properties of compounds during cladding of sheets made of St3 with sheets of nichrome and steel 12Kh18N10T with the use of ''elastic'' explosives are presented. It is shown that the use of ''elastic'' explosives permits to decrease r parameter sufficiently, (where r - is the ratio of explosive mass to the mass of throwen phate) that reduces considerably the specific consumption explosives in comparison with the consumption conventional mixture explosives. Peculiarities of tested ''elastic'' explosives make their application perspective in two cases - at cladding of complex curved surfaces (drums, tube blanks etc.), as sell as at applications of burst chambers, where explosive mass limits dimensions of cladding blanks and details [ru

Effect of Al and N on the toughness of heavy section steel plates

International Nuclear Information System (INIS)

Kikutake, Tetsuo; Tokunaga, Yoshikuni; Nakao, Hitoji; Ito, Kametaro; Takaishi, Shogo.

1988-01-01

The effect of Al and N on the notch toughness and tensile strength of heavy section pressure vessel steel plates is investigated. Notch toughness of steel A533B (Mn-Mo-Ni), which has mixed microstructure of ferrite and bainite, is drastically changed by the ratio of sol.N/sol.Al. With metallurgical observations, it is revealed that AlN morphology is influenced by the ratio of sol.N/sol.Al through the level of solute Al(C Al ). At the heat treatment of heavy section steel plate, AlN shows OSTWALD ripening and its speed depends upon C Al . When Al is added (Al ≥ 0.010%) in steel and sol.N/sol.Al ≤ 0.5, C Al remains low. This prevents AlN ripening, and brings fine austenite grain size and high toughness. On the other hand, when sol.N/sol.Al Al becomes high and this gives poor toughness through coarse AlN precipitates and coarse austenite grain. Therefore, controll of sol.N/sol.Al over 0.5 is favorable to keep high toughness in A533B steel. In steel A387-22 (Cr-Mo) which has full bainitic microstructure, too fine austenite grain brings about poor hardenability, and polygonal ferrite, which brings about both poor strength and tughness, appears in microstructure. Then sol.N/sol.Al < 0.5 is better to give high hardenability in steel A387-22. (author)

Killing Effects of an Isolated Serratia marcescens KH-001 on Diaphorina citri via Lowering the Endosymbiont Numbers

Directory of Open Access Journals (Sweden)

Wei Hu

2018-05-01

Full Text Available Huanglongbing (HLB is the most devastating citrus disease worldwide, and suppression of the Asian citrus psyllid (Diaphorina citri is regarded as an effective method to inhibit the spread of HLB. In this study, we isolated a strain named as Serratia marcescens KH-001 from D. citri nymphs suffering from disease, and evaluated its killing effect on D. citri via toxicity test and effect on microbial community in D. citri using high-throughput sequencing. Our results indicated that S. marcescens KH-001 could effectively kill 83% of D. citri nymphs, while the fermentation products of S. marcescens KH-001 only killed 40% of the D. citrinymphs. High-throughput sequencing results indicated that the S. marcescens KH-001 increased the OTU numbers from 62.5 (PBS buffer to 81.5, while significantly lowered the Shannon index compared with Escherichia coli DH5α (group E (p < 0.05. OTU analysis showed that the S. marcescens KH-001 had significantly reduced the relative abundance of endosymbionts Wolbachia, Profftella, and Carsonella in group S compared with that in other groups (p < 0.05. Therefore, the direct killing effect of the fermentation products of S. marcescens KH-001 and the indirect effect via reducing the numbers of endosymbionts (Wolbachia, Profftella, and Carsonella of D. citri endow S. marcescens KH-001 a sound killing effect on D. citri. Further work need to do before this strain is used as a sound biological control agents.

Microhardness of boron, titanium, and nitrogen implanted steel

International Nuclear Information System (INIS)

Sowa, M.; Szyszko, W.; Sielanko, J.; Glusiec, L.

1989-01-01

Mechanically polished steel (1H18N9T) and (15GTM) samples are implanted with boron, titanium, and nitrogen ions, with dose ranging from 10 16 to 10 17 ions/cm 2 . The implantation energy varied from 100 to 250 keV. Implanted samples are heat-treated at 400 to 800 0 C in vacuum. The microhardness of implanted samples is measured by using a Hanneman tester with loads ranging from 2 to 40 g. The influence of annealing temperature on microhardness of the implanted layers is determined. The diffusion of boron from the implanted layers is also investigated by using the secondary ion mass spectrometer. The diffusion coefficients of boron in steel are determined. (author)

Diffusion bonding of 9Cr ODS ferritic/martensitic steel with a phase transformation

Energy Technology Data Exchange (ETDEWEB)

Noh, Sanghoon, E-mail: shnoh@kaeri.re.kr [Nuclear Materials Division, Korea Atomic Energy Research Institute, Yuseong-gu, Daejeon (Korea, Republic of); Kimura, Akihiko [Institute of Advanced Energy, Kyoto University, Gokasho, Uji, Kyoto (Japan); Kim, Tae Kyu [Nuclear Materials Division, Korea Atomic Energy Research Institute, Yuseong-gu, Daejeon (Korea, Republic of)

2014-10-15

Highlights: • Diffusion bonding was employed to join 9Cr oxide dispersion strengthened ferritic/martensitic steel under uniaxial hydrostatic pressure, and the microstructure and tensile properties of the joints were investigated. • ODS steel was successfully diffusion bonded at an austenization temperature to migrate a residual diffusion bonding interface. • The tensile properties of the joint region were comparable with that of the base metal with a ductile fracture occurred far from the bonding interface. • It is considered that diffusion bonding with a phase transformation can be a very useful joining method for fabricating components in next-generation nuclear systems using 9Cr ODS ferritic/martensitic steel. - Abstract: Diffusion bonding was employed to join oxide-dispersion-strengthened ferritic/martensitic steel under uniaxial hydrostatic pressure using a high vacuum hot press, and the microstructure and tensile properties of the joints were investigated. 9Cr oxide dispersion strengthened (ODS) steel was successfully diffusion bonded at 1150 °C for 1 h to migrate a residual bonding interface. Following heat treatment, including normalising at 1050 °C and tempering at 800 °C for 1 h, comparable results without inclusions or micro-voids at the bonding interface, or degradation in the base metal were achieved. Transmission electron microscopy (TEM) observation revealed that the nano-oxide particles in the bonding region were uniformly distributed in the matrix. At room temperature, the joint had nearly the same tensile properties with that of the base metal. The tensile strength of the joint region at elevated temperatures was comparable with that of the base metal. The total elongation of the joint region decreased slightly, but reached 80% of the base metal at 700 °C, and a ductile fracture occurred far from the bonding interface. Therefore, it is considered that diffusion bonding with a phase transformation can be a very useful joining method for

Consideration of the oxide particle-dislocation interaction in 9Cr-ODS steel

Science.gov (United States)

Ijiri, Yuta; Oono, N.; Ukai, S.; Yu, Hao; Ohtsuka, S.; Abe, Y.; Matsukawa, Y.

2017-05-01

The interaction between oxide particles and dislocations in a 9Cr-ODS ferritic steel is investigated by both static and in situ TEM observation under dynamic straining conditions and room temperature. The measured obstacle strength (?) of the oxide particles was no greater than 0.80 and the average was 0.63. The dislocation loops around some coarsened particles were also observed. The calculated obstacle strength by a stress formula of the Orowan interaction is nearly equaled to the average experimental value. Not only cross-slip system but also the Orowan interaction should be considered as the main interaction mechanism between oxide particles and dislocation in 9CrODS ferritic steel.

Evaluation of dynamic fracture toughness of cold worked 9Cr-1Mo steel

International Nuclear Information System (INIS)

Sathyanarayanan, S.; Sasikala, G.; Ray, S.K.

2004-01-01

Dynamic J-R curves for cold worked 9Cr-1Mo steel have been estimated from instrumented impact test data at ambient temperature on pre-cracked Charpy specimens using three methods of analysis, namely those by Ray et al., Schindler, and Sreenivasan and Mannan. It is concluded that of these three, Schindler's method is the best suited for the purpose since it gives consistent variations with cold work of dynamic J-R curves and dynamic fracture toughness. Cold work results in substantial degradation in dynamic fracture toughness of 9Cr-1Mo steel

Effect of laser absorption on picosecond laser ablation of Cr12MoV mold steel, 9Cr18 stainless steel and H13A cemented carbide

Science.gov (United States)

Wu, Baoye; Liu, Peng; Wang, Xizhao; Zhang, Fei; Deng, Leimin; Duan, Jun; Zeng, Xiaoyan

2018-05-01

Due to excellent properties, Cr12MoV mold steel, 9Cr18 stainless steel and H13A cemented carbide are widely used in industry. In this paper, the effect of absorption of laser light on ablation efficiency and roughness have been studied using a picosecond pulse Nd:YVO4 laser. The experimental results reveal that laser wavelength, original surface roughness and chemical composition play an important role in controlling ablation efficiency and roughness. Firstly, higher ablation efficiency with lower surface roughness is achieved on the ablation of 9Cr18 at 532, comparing with 1064 nm. Secondly, the ablation efficiency increases while the Ra of the ablated region decreases with the decrease of original surface roughness on ablation of Cr12MoV mold steel at 532 nm. Thirdly, the ablation efficiency of H13A cemented carbide is much higher than 9Cr18 stainless steel and Cr12MoV mold steel at 1064 nm. Scanning electron microscopy images reveals the formation of pores on the surface of 9Cr18 stainless steel and Cr12MoV mold steel at 532 nm while no pores are formed at 1064 nm. As to H13A cemented carbide, worm-like structure is formed at 1064 nm. The synergetic effects of the heat accumulation, plasma shielding and ablation threshold on laser ablation efficiency and machining quality were analyzed and discussed systematically in this paper.

Radiation damage structure in irradiated and annealed 440 WWER-Type reactor pressure vessel steels

International Nuclear Information System (INIS)

Kocik, J.; Keilova, E.

1993-01-01

A review of irradiation damages in WWER-type RPV steels based on conventional Transmission Electron Microscopy investigations in a power reactor and a research reactor, is presented; the samples consist in Cr-Mo-V ferritic steel (15Kh2MFA type). The visible part of radiation-induced defects consists of very fine vanadium carbide precipitates, small dislocation loops and black dots (presumably corresponding to clusters and particle embryos formed from vacancies and solute-atoms (vanadium, copper, phosphorus) and carbon associated with vanadium. Radiation-induced defects are concentrated at dislocation substructure during irradiation in a power reactor, revealing the role of radiation-enhanced diffusion in damage structure forming process. Contrarily, the distribution of defects resulting from annealing of specimens irradiated in the research reactor is pre-determined by an homogenous distribution of radiation-induced defects prior to annealing. Increasing the number of re-irradiation and annealing cycles, the amount of dislocation loops among all defects seems to be growing. Simultaneously, the dislocation substructure recovers considerably. (authors). 14 refs., 11 figs., 3 tabs

Radiation damage structure in irradiated and annealed 440 WWER-Type reactor pressure vessel steels

Energy Technology Data Exchange (ETDEWEB)

Kocik, J; Keilova, E [Czech Nuclear Society, Prague (Czech Republic)

1994-12-31

A review of irradiation damages in WWER-type RPV steels based on conventional Transmission Electron Microscopy investigations in a power reactor and a research reactor, is presented; the samples consist in Cr-Mo-V ferritic steel (15Kh2MFA type). The visible part of radiation-induced defects consists of very fine vanadium carbide precipitates, small dislocation loops and black dots (presumably corresponding) to clusters and particle embryos formed from vacancies and solute-atoms (vanadium, copper, phosphorus) and carbon associated with vanadium. Radiation-induced defects are concentrated at dislocation substructure during irradiation in a power reactor, revealing the role of radiation-enhanced diffusion in damage structure forming process. Contrarily, the distribution of defects resulting from annealing of specimens irradiated in the research reactor is pre-determined by an homogenous distribution of radiation-induced defects prior to annealing. Increasing the number of re-irradiation and annealing cycles, the amount of dislocation loops among all defects seems to be growing. Simultaneously, the dislocation substructure recovers considerably. (authors). 14 refs., 11 figs., 3 tabs.

Mechanism of the reactions 14N(d,p)15N and 14N(d,n)15O by Doppler shift line shape method

International Nuclear Information System (INIS)

Abdel-Moneim, A.M.

1976-06-01

In this investigation the total and the differential absolute cross sections of the 14 N(d,p) 15 N reaction leading to excited states at 7.3, 8.3 and 9.05 MeV levels in 15 N and the 14 N(d,n) 15 O reaction leading to the 6.79 MeV level in 15 O, have been studied over the energy range from 0.5 MeV to 3 MeV. Doppler shift line shape method as well as γ-ray yield measurements have been used. The absolute cross sections are determined relative to the known 14 N(p,p) elastic differential cross sections. A comparison with previously determined values for the same reactions at selected energies shows good agreement in angular distribution as well as in absolute values. The total cross section for the d,p reaction shows a general energy dependence which is typical for direct reactions, but with minor contribution from compound nucleus formation at certain energy ranges. For the 14 N(d,n) 15 N reaction, the method applied is unique, since it allows the differential cross section to be studied all the way down to the threshold energy of deuterons at 2 MeV, with a detectorsystem efficiency which is constant over the entire range of neutron energies. The larger part of the energy range that has been investigated is dominated by a resonance at 2.55 π+ 0.05 MeV deuteron energy and a halfwidth depending on the amount of contribution from the direct reaction of the order of 200-400 keV. (JIW)

Evaluation of properties of low activation Mn-Cr steel (2). Physical properties and aging properties

Energy Technology Data Exchange (ETDEWEB)

Saito, Shigeru; Fukaya, Kiyoshi [Japan Atomic Energy Research Inst., Tokai, Ibaraki (Japan). Tokai Research Establishment; Ishiyama, Shintaro [Japan Atomic Energy Research Inst., Oarai, Ibaraki (Japan). Oarai Research Establishment; Sato, Ikuo; Kusuhashi, Mikio; Hatakeyama, Takeshi [Japan Steel Works Ltd., Muroran, Hokkaido (Japan). Muroran Plant; Takahashi, Heishichiro [Hokkaido Univ., Sapporo (Japan); Kikuchi, Mitsuru [Japan Atomic Energy Research Inst., Naka, Ibaraki (Japan). Naka Fusion Research Establishment

2000-08-01

The JT-60SU (Super Upgrade) program is under discussion at JAERI. Its design optimization activity requires the vacuum vessel material to be non-magnetic, very strong and with low induced activation. However, there is no suitable material available to fulfill all the requirements. JAERI started to develop a new material for the vacuum vessel together with the Japan Steel Works LTD. (JSW). Chemical composition and metallurgical processes were optimized and a new steel named VC9, which has the composition of Cr :16wt%, Mn :15.5wt%, C :0.2wt%, N :0.2wt% with nonmagnetic single {gamma} phase, was selected as a candidate material. Here, physical properties and aging properties of VC9 were studied and the results were compared with those of 316L stainless steel. (author)

Comparative assessment of filler wires for argon-arc welding of refractory alloys

International Nuclear Information System (INIS)

Sorokin, L.I.; Bagdasarov, Yu.S.; Tupikin, V.I.

1993-01-01

It is recommended to use wires of similar composition as filler material during argon-arc welding of heat resisting alloys, and Sv-08Kh20N57M8V8T3R wire - for welding of dispersion hardening alloys. Sv-06Kh15N60M15, Sv-KhN64KBMYuVF or Kh11N60M23 wires should be used as filler materials to decrease tendency of welded joints to cracking during welding and heat treatment

An Experimental Investigation on Hardness and Microstructure of Heat Treated EN 9 Steel

Science.gov (United States)

Biswas, Palash; Kundu, Arnab; Mondal, Dhiraj

2017-08-01

In the modern engineering world, extensive research has led to the development of some special grades of steel, often suited for enhanced functions. EN 9 steel is one such grade, having major applications in power plants, automobile and aerospace industry. Different heat treatment processes are employed to achieve high hardness and high wear resistance, but machinability subsequently decreases. Existing literature is not sufficient to achieve a balance between hardness and machinability. The aim of this experimental work is to determine the hardness values and observe microstructural changes in EN9 steel, when it is subjected to annealing, normalizing and quenching. Finally, the effects of tempering after each of these heat treatments on hardness and microstructure have also been shown. It is seen that the tempering after normalizing the specimen achieved satisfactory results. The microstructure was also observed to be consisting of fine grains.

Hydrogen degradation of 21-6-9 and medium carbon steel by disc pressure test

International Nuclear Information System (INIS)

Zhou, D.H.; Zhou, W.X.; Xu, Z.L.

1986-01-01

This paper reports the method of disc pressure test and the results for 21-6-9 stainless steel and medium carbon steel in hydrogen gas with different pressures and time of storage. The results show the hydrogen induced degradation of these two kinds of steel. An attempt was made to establish an index which uses variation of area of deformed disc to determine the degradation of ductility in a hydrogen environment. (orig.)

Creep-fatigue evaluation method for modified 9Cr-1Mo steel

International Nuclear Information System (INIS)

Wada, Y.; Aoto, K.

1997-01-01

As creep-fatigue evaluation methods on normalized and tempered Modified 9Cr-1Mo steel for design use, the time fraction rule and the simplified conventional ductility exhaustion rule are investigated for the prediction of tension strain hold creep-fatigue damage of this material. For the above investigation, stress relaxation behaviour during strain hold has to be analyzed using stress-strain-time relation. The initial value of stress relaxation was determined by cyclic stress-strain curves in continuous cycling fatigue tests. Cyclic stress-strain behaviour of Mod.9Cr-1Mo(NT) steel is different from that of austenitic stainless steels, so this effect was considered. Stress relaxation analysis was performed using static creep strain-time relation and conventional hardening rule. The time fraction by using the above stress relaxation analysis results can give good prediction for creep-fatigue life of Mod.9Cr-1Mo(NT) steel. For design use it is practical to be able to estimate creep damages conservatively by both strain behaviour of cyclic plastic (in continuous cycling fatigue tests) and monotonic creep (in standard creep tests). The life reduction by strain hold at the minimum peak of compressive stress in creep-fatigue tests was examined, and this effects can be evaluated by the relationship between the location of oxidation and the effective deformation at crack tip. In an accelerated oxidation environment, for example in high temperature and high pressure steam, a different approach for life reduction should be developed based on the mechanism of growth of oxide and crack growth with oxidation. However, in the creep damage dominant region, its effect is saturated and the effect of cavity growth along grain boundary becomes dominant for long-term strain hold in the high temperature conditions. (author). 6 refs, 6 figs

Microstructure and long-term creep properties of 9–12% Cr steels

DEFF Research Database (Denmark)

Hald, John

2008-01-01

Advanced microstructure characterisation and microstructure modelling has demonstrated that long-term microstructure stability in 9–12% Cr steels under technical loading conditions is equivalent to precipitate stability. Mo and W can have a positive influence on long-term creep strength of 9–12% Cr...

Microstructure of warm rolling and pearlitic transformation of ultrafine-grained GCr15 steel

International Nuclear Information System (INIS)

Sun, Jun-Jie; Lian, Fu-Liang; Liu, Hong-Ji; Jiang, Tao; Guo, Sheng-Wu; Du, Lin-Xiu; Liu, Yong-Ning

2014-01-01