The influence of cold work on the oxidation behaviour of stainless steel

International Nuclear Information System (INIS)

Langevoort, J.C.

1985-01-01

In this thesis the study of the interaction of oxygen gas with stainless steel surfaces is described. Thermogravimetry, microscopy and ellipsometry have been used to follow the oxidation in situ, while EDX, AES and XPS have been used to determine the oxide compositions. The aim of this thesis is to reveal the influence on the oxidation behaviour of stainless steel of i) cold work (rolling, drawing, milling, polishing and Ar ion bombardment) ii) the initially formed oxide and iii) the experimental conditions. Two types of stainless steels have been used (AISI 304 (a 18/8 Cr/Ni steel) and Incoloy 800 H (a 20/30 Cr/Ni steel)). (Auth.)

Al2 O3:Cr,Ni: a possible thermoluminescent dosemeter

International Nuclear Information System (INIS)

Mariani R, Francisco; Roman B, Alvaro; Saavedra S, Renato; Ibarra S, Angel

1996-01-01

Results from a study on the thermoluminescent (Tl) emission from Al 2 O 3 :Cr,Ni are presented. The measurements were obtained for evaluation of the Al 2 O 3 :Cr,Ni dosimetric properties. Different crystal batches were exposed to two kind of ionizing radiation (X-ray and β - ). The Tl spectrum has a main peak with high thermal and optical stability, deviating from linearity for doses lower than 3.6 Gy. Furthermore, this material shows advantages (thermal resistance, reusability, multiple heating cycles) compared to TLD-100. Measured Al 2 O 3 :Cr,Ni properties indicate that it could be used as a dosemeter. (author)

Attempts to improve the fatigue characteristics of the austenitic steel X5CrNi18-10 in the temperature range of 25-600 C by mechanical boundary layer hardening; Zur Verbesserung des Ermuedungsverhaltens des austenitischen Stahls X5CrNi18-10 im Temperaturbereich 25-600 C durch mechanische Randschichtverfestigungsverfahren

Energy Technology Data Exchange (ETDEWEB)

Nikitin, Ivan

2007-01-31

Pieces of the austenitic steel X5CrNi18-10 whose boundary layers had been hardened by different methods were investigated with a view to their fatigue deformation characteristics in the temperature range of 25-600 degC. Parallel to this, microstructural and X-ray analyses provided deeper understanding of fatigue deformation. The microstructure was characterized, among others, by TEM. Boundary layers were solidified by rolling, by a combination of mechanical and thermal processes, by high-temperature rolling, and by laser shock solidification. The analyses focused on microstructural processes and on the intrinsic stress stability and provided important information on the fabrication of structural components with optimised life. (orig.)

Creep-rupture-tests on thestainless steel X6 CrNi1811 (DIN 1.4948) in the frame of the ''Extrapolation-Program'' Pt. 2

International Nuclear Information System (INIS)

Solano, R.R.; Barroso, S.; Rivas, M. de las; Schirra, M.; Seith, B.

1979-01-01

The austenitic stainless steel X6 CrNi 1811 (DIN 1.4948) that is used as a structure material for the German Fast Breeder Reactor SNR 300 was creep tested in a temperature range of 550-650 deg under base material condition as well as welded material condition. The main point of this program (''Extrapolation-Program'') lies in the knowledge of the cree-rupture-strength and creep-behaviour up to 3X10 - 4 hours at higher temperatures in order to extrapolate up to (>=)10 5 hours for operating temperatures. In order to study the stress dependency of the minimum creep rate additional tests were carried out over temperature range 550 deg - 750 deg C. The present report describes the state in the running program with test-time up to 35.000 hours. Besides the cree-rupture behaviour it is possible to make a distinct quantitative statement for the creep-behaviour and ductility. Extensive metallographic examinations show the fracture behaviour and changes in structure. (author)

Creep-rupture-test on the stainless steel X6CRNI1811 (DIN 1.4948) in the frame of the ''Extrapolation-Program''. (Part III)

International Nuclear Information System (INIS)

Solano, R.; Las Rivas, M. de; Barroso, S.

1982-01-01

The austenitic stainless steel X6CrNi1811 (DIN 1.4948) used as a structure material for the German Fast Breeder Reactor SNR 300 was creep tested in a temperature range of 550-650 deg under base material condition as well as welded material condition. The main point of this program (''Extrapolation-Program'') lies in the knowledge of the creep-rupture-strength and creepbehaviour up to 3 x 10 4 hours at higher temperatures in order to extrapolate up to >=10 5 hours for operating temperatures. In order to study the stress dependency of the minimum creep rate additional tests were carried out of 550 deg - 750 deg C. The present report describes the state in the running program with test-times of 23.000 hours and results from tests up to 55.000 hours belonging to other parallel programs are taken into account. Besides the creep-rupture behaviour it is also made a study of ductility between 550 and 750 deg C. Extensive metallographic examinations have been made to study the fracture behaviour and changes in structure. (author)

Corrosion processes of alloyed steels in salt solutions

Energy Technology Data Exchange (ETDEWEB)

Kienzler, Bernhard [Karlsruher Institut fuer Technologie (KIT), Eggenstein-Leopoldshafen (Germany). Institut fuer Nukleare Entsorgung

2018-02-15

A summary is given of the corrosion experiments with alloyed Cr-Ni steels in salt solutions performed at Research Centre Karlsruhe (today KIT), Institute for Nuclear Waste Disposal (INE) in the period between 1980 and 2004. Alloyed steels show significantly lower general corrosion in comparison to carbon steels. However, especially in salt brines the protective Cr oxide layers on the surfaces of these steels are disturbed and localized corrosion takes place. Data on general corrosion rates, and findings of pitting, crevice and stress corrosion cracking are presented.

Mechanical properties of steel X 6 CrNi 18 11 after creep

Energy Technology Data Exchange (ETDEWEB)

Heesen, E te; Lorenz, H; Grosser, E D [INTERATOM, Bergisch Gladbach (Germany)

1977-07-01

Test series were conducted to determine the influence of prior creep on the mechanical properties of X 6 CrNi 18 11 base material, weld joint and weld metal. Creep and tensile tests on base and weld joint were performed at 600 degrees C, the weld metal was Investigated at 550, 600, and 650 degrees C. With regard to the base materials, prior creep leads to a significant reduction in tensile ductility combined with an increase of the 0.2 % proof stress. Residual ductility represents a sufficient ductility reserve. For the weld joint tensile strength remains unchanged up to the end of the secondary creep stage. Although tensile elongation and reduction of area decrease, the relative reduction is less compared to the base material. Concerning the weld metal the 0.2 % proof stress reveals a marked decrease due to the test temperature leading to a stress relief heat treatment. Ultimate tensile strength and ductility Indicate little or no deviations from the original values. Thermal exposures in the absence of stress nearly gave the same properties as were found on precrept specimens. (author)

Creep-rupture-test on the stainless steel X6crni1811 (Din 1.494.8) in the frame of the Extrapolation-Program. (Part III)

International Nuclear Information System (INIS)

Solano, R.; Schirra, M.; Rivas, M. de la; Barroso, S.; Seith, B.

1982-01-01

The austenitic stainless steel X6crni1811 (Din 1.4948) used as a structure material for the German Fast Breeder Reactor SNR 300 was creep tested in a temperature range of 550-650 degree centigree material condition as well as welded material condition. The main point of this program (Extrapolation-Program) lies in the knowledge of the creep-rupture-strength and creep-behaviour up to 3 x 10 4 hours higher temperatures in order to extrapolated up to ≥10 5 hours for operating temperatures. In order to study the stress dependency of the minimum creep rate additional tests were carried out of 550 degree centigree - 750 degree centigree. The present report describes the state in the running program with test-times of 23.000 hours and results from tests up to 55.000 hours belonging to other parallel programs are taken into account. Besides the creep-rupture behaviour it is also made a study of ductility between 550 and 750 degree centigree. Extensive metallographic examinations have been made to study the fracture behaviour and changes in structure. (Author)

THE INFLUENCE OF GRINDING CONDITIONS ON THE DISTRIBUTION OF RESIDUAL STRESS IN THE SURFACE LAYER OF 17crni6-6 STEEL AFTER CARBURIZING

Directory of Open Access Journals (Sweden)

Jacek Sawicki

2017-06-01

Full Text Available This paper presents the results of a study aimed at determining the residual stress which results from developing the surface layer by low-pressure and conventional carburizing and grinding of 17CrNi6-6 steel. A synergistic effect of thermochemical and abrasive treatment was examined on ring samples used to study residual stress by Davidenkov’s method. Samples were subjected to vacuum carburizing and conventional carburizing, which was followed by grinding with a 38A60K8V aloxite grinding wheel and a CBN grinding wheel - RNB80/63B75V. The following cutting fluids were used during the grinding process: oil emulsion 5%, supply rate ca. 20 l/min, Micro5000 oil supplied at the minimum quantity lubrication (MQL of ca. 25 ml/h, dry machining. The study determined the effect of the type of grinding wheel and the cooling and lubricating agent on the distribution of residual stress in the sur-face layer. The best effects of grinding with respect to the residual stress were achieved with flood cooling with oil emulsion and grinding with a CBN grinding wheel.

Investigation of Cr-Ni duplex stainless steel

International Nuclear Information System (INIS)

Lu Shiying

1985-01-01

At temperatures of 450 - 750 0 C, a laminate-shaped intermetallic phase Fe3Cr3Mo2Si2 has been observed. Intergranular brittle fracture is due to the precipitation of the Fe3Cr3Mo2SI2 phase, but quasi-cleavage fracture is connected with the precipitation of chi and σ phases. The formation of chi and σ during aging at 750 - 900 0 C results in a drastic decrease of the SCC resistance of Cr18Ni5 steel. In order to avoid a fully ferritic microstructure in Cr18Ni5 duplex steel after heating at high temperature or welding, the K value must be kept to 0.42 for thin wall tube. The decrease in SCC resistance after cold deformation is not due to the formation of strain-induced martensite but is connected with significant reduction in the resistance to pitting corrosion. (author)

Microstructure changes in the low stacking fault energy steel

International Nuclear Information System (INIS)

Rodak, K.; Kuc, D.; Niewielski, G.; Hetmanczyk, M.

1999-01-01

A Cr-Ni austenitic steel (type 304) was investigated using TEM. It is shown that some structural parameters (dislocations density within the subgrains and the subgrains size) change with temperature and strain rate after hot temperature deformation. The subgrain microstructure was characterized quantitatively for different characteristics. (author)

Resistance Spot Welding of dissimilar Steels

Directory of Open Access Journals (Sweden)

Ladislav Kolařík

2012-01-01

Full Text Available This paper presents an analysis of the properties of resistance spot welds between low carbon steel and austenitic CrNi stainless steel. The thickness of the welded dissimilar materials was 2 mm. A DeltaSpot welding gun with a process tape was used for welding the dissimilar steels. Resistance spot welds were produced with various welding parameters (welding currents ranging from 7 to 8 kA. Light microscopy, microhardness measurements across the welded joints, and EDX analysis were used to evaluate the quality of the resistance spot welds. The results confirm the applicability of DeltaSpot welding for this combination of materials.

Characteristics of modified martensitic stainless steel surfaces under tribocorrosion conditions

International Nuclear Information System (INIS)

Rozing, Goran; Marusic, Vlatko; Alar, Vesna

2017-01-01

Stainless steel samples were tested in the laboratory and under real conditions of tribocorrosion wear. Electrochemical tests were also carried out to verify the corrosion resistance of modified steel surfaces. Metallographic analysis and hardness testing were conducted on stainless steel samples X20Cr13 and X17CrNi16 2. The possibilities of applications of modified surfaces of the selected steels were investigated by testing the samples under real wear conditions. The results have shown that the induction hardened and subsequently nitrided martensitic steels achieved an average wear resistance of up to three orders of magnitude higher as compared to the delivered condition.

Characteristics of modified martensitic stainless steel surfaces under tribocorrosion conditions

Energy Technology Data Exchange (ETDEWEB)

Rozing, Goran [Osijek Univ. (Croatia). Chair of Mechanical Engineering; Marusic, Vlatko [Osijek Univ. (Croatia). Dept. of Engineering Materials; Alar, Vesna [Zagreb Univ. (Croatia). Dept. Materials

2017-04-01

Stainless steel samples were tested in the laboratory and under real conditions of tribocorrosion wear. Electrochemical tests were also carried out to verify the corrosion resistance of modified steel surfaces. Metallographic analysis and hardness testing were conducted on stainless steel samples X20Cr13 and X17CrNi16 2. The possibilities of applications of modified surfaces of the selected steels were investigated by testing the samples under real wear conditions. The results have shown that the induction hardened and subsequently nitrided martensitic steels achieved an average wear resistance of up to three orders of magnitude higher as compared to the delivered condition.

Estimation of residual stresses in reactor pressure vessel steel specimens clad by stainless steel strip electrodes

International Nuclear Information System (INIS)

Schimmoeller, H.A.; Ruge, J.L.

1978-01-01

The equations to determine a two-dimensional state of residual stress in flat laminated plates are well known from an earlier work by one of the authors. The derivation of these equations leads to a linear, inhomogeneous system of Volterra's integral equations of the second kind. To ascertain the unknown residual stresses from these equations it is necessary to cut down the thickness of the test plate layer by layer. This results in two-dimensional deformation reactions in the rest of the test plate, which can be measured, e.g. by a strain gauge rosette applied to the opposite side of the plate. The above-mentioned stress analysis has been transferred to 86mm thick reactor pressure vessel steel specimens (Type 22NiMoCr 37, DIN-No. 1.6751, similar to ASTM A508, Class 2) double-run clad by austenitic stainless steel strip electrodes (first layer 24/13 Cr-Ni steel, second layer 21/10 Cr-Ni steel). The overall dimensions of the clad specimens investigated amounted to 200 x 200 x (86+4.5+4.5)mm. At the surface of the austenitic cladding there is a two-dimensional tensile normal stress state of about 200N/mm 2 parallel, and about 300N/mm 2 transverse, to the welding direction. The maximum tensile stress was 8mm below the interface (fusion line, material transition) in the parent material. The stress distributions of the specimens investigated, determined on the basis of the above-mentioned combined experimental mathematical procedure, are presented graphically for the as-welded (as-delivered) and annealed (600 0 C/12hr) conditions. (author)

Austenitic chromium nickel steel as standard reference material in measurement of thermal and temperature conductivity

International Nuclear Information System (INIS)

Binkele, L.

1990-01-01

A niobium-stabilized CrNi steel with the NBS designation SRM 735 is introduced as WLF standard reference material in a report by Hust and Giarratano, for the temperature range 300-1200 K and for thermal conductivities around 20 W/mk. However, its specification does not show it to be a direct member of the DIN family of CrNi steels. This report should be regarded as a continuation and supplement to the above-mentioned efforts in America. On the one hand, a solution of a possibly too-narrow specification is aimed at for the reference material, where it is important how sensitive the thermal conductivity is to changes in the chemical composition and changes of the manufacturing parameters and what accuracy can be reached for the reference values with the best measurement techniques. On the other hand, the data base should be expanded and the accuracy of the reference curve should be improved if possible. (orig./MM) [de

Strengthening of stable Cr-Ni austenitic stainless steel under thermomechanical treatments

Science.gov (United States)

Akkuzin, S. A.; Litovchenko, I. Yu.; Tyumentsev, A. N.

2017-12-01

The features of microstructure and mechanical properties of stable austenitic steel after thermomechanical treatment consisted of low-temperature deformation, deformation in the temperature range T = 273-873 K, and subsequent annealing were investigated. It is shown that under such treatment direct (γ → α')- and reverse (α'→γ)-martensitic transformations occur in the steel. As a result of the thermomechanical treatment submicrocrystalline structural states with high density of micro- and nanotwins and localized deformation bands are formed. The strength of the steel in these structural states is several times higher than that in the initial state.

The research of axial corrosion fatigue on 10Ni3CrMoV steel

Science.gov (United States)

Xie, Xing; Yi, Hong; Xu, Jian; Xie, Kun

2017-09-01

Fatigue life had been studied with 10CrNi3MoV steel at different load ratios and in different environmental medias. The microstructure and micro-topography had been observed and analyzed by means of SEM, EDS and TEM. Our findings indicated that, the fatigue life of 10Ni3CrMoV steel in seawater was shorter than in air, the difference in longevity was larger with the decreasing of axis stress. Corrosion pits had a great influence on corrosion fatigue life.

Effect of acetic acid on corrosion behavior of AISI 201, 304 and 430 stainless steels

Energy Technology Data Exchange (ETDEWEB)

Vashishtha, Himanshu; Taiwade, Ravindra V.; Sharma, Sumitra [Visvesvaraya National Institute of Technology (VNIT), Nagpur (India). Dept. of Metallurgical and Materials Engineering

2017-05-15

Austenitic stainless steels are often used to handle organic acids such as acetic acid (CH{sub 3}COOH), which are extensively used in food contact applications and chemical industries for manufacturing medicines, nutrition and various chemical amalgams. In the present investigation an attempt has been made to compare the corrosion behavior of Cr-Ni (AISI type 304), Cr-Mn-Ni (type 201) and Cr (type 430) stainless steel for economical replacement of higher cost Cr-Ni grade. Immersion testing was performed at room temperature and boiling temperature in acetic acid. Atomic absorption spectroscopy was carried out to evaluate metal ion concentration in the immersion solution. The surface morphology of pit formation was characterized using scanning electron microscopy coupled with energy dispersive X-ray spectroscopy. The effect of elemental leaching on electrical conductivity of the immersion solution was evaluated and correlated with pH measurements. A new mechanism has been proposed for the pit formation due to manganese sulfide inclusions. The replacement compatibility was further confirmed with anodic polarization testing and a successful replacement was established for room temperature applications.

Al{sub 2} O{sub 3}:Cr,Ni: a possible thermoluminescent dosemeter; Al{sub 2} O{sub 3}: Cr, Ni un posible dosimetro termoluminiscente

Energy Technology Data Exchange (ETDEWEB)

Mariani R, Francisco; Roman B, Alvaro; Saavedra S, Renato [Pontificia Univ. Catolica de Chile, Santiago (Chile). Facultad de Fisica; Ibarra S, Angel [Centro de Investigaciones Energeticas, Medioambientales y Tecnologicas (CIEMAT), Madrid (Spain). Seccion Materiales para Fusion

1997-12-31

Results from a study on the thermoluminescent (Tl) emission from Al{sub 2} O{sub 3}:Cr,Ni are presented. The measurements were obtained for evaluation of the Al{sub 2} O{sub 3}:Cr,Ni dosimetric properties. Different crystal batches were exposed to two kind of ionizing radiation (X-ray and {beta}{sup -}). The Tl spectrum has a main peak with high thermal and optical stability, deviating from linearity for doses lower than 3.6 Gy. Furthermore, this material shows advantages (thermal resistance, reusability, multiple heating cycles) compared to TLD-100. Measured Al{sub 2} O{sub 3}:Cr,Ni properties indicate that it could be used as a dosemeter. (author). 5 refs., 4 figs.

Weldability of Stainless Steels

International Nuclear Information System (INIS)

Saida, Kazuyoshi

2010-01-01

It gives an outline of metallographic properties of welding zone of stainless steels, generation and mechanisms of welding crack and decreasing of corrosion resistance of welding zone. It consists of seven chapters such as introduction, some kinds of stainless steels and properties, metallographic properties of welding zone, weld crack, toughness of welding zone, corrosion resistance and summary. The solidification modes of stainless steels, each solidification mode on the cross section of Fe-Cr-Ni alloy phase diagram, each solidification mode of weld stainless steels metal by electron beam welding, segregation state of alloy elements at each solidification mode, Schaeffler diagram, Delong diagram, effects of (P + S) mass content in % and Cr/Ni equivalent on solidification cracking of weld stainless steels metal, solidification crack susceptibility of weld high purity stainless steels metal, effects of trace impurity elements on solidification crack susceptibility of weld high purity stainless steels metal, ductile fracture susceptibility of weld austenitic stainless steels metal, effects of H2 and ferrite content on generation of crack of weld 25Cr-5N duplex stainless steels, effects of O and N content on toughness of weld SUS 447J1 metals, effect of ferrite content on aging toughness of weld austenitic stainless steel metal, corrosion morphology of welding zone of stainless steels, generation mechanism of knife line attack phenomenon, and corrosion potential of some kinds of metals in seawater at room temperature are illustrated. (S.Y.)

Structure of maraging steel after thermomechanical treatment at high temperature

International Nuclear Information System (INIS)

Prokoshkina, V.G.; Kaputkina, L.M.; Mozzhukhin, V.E.

1981-01-01

Developed polygonized substructure is formed in austenite of maraging Cr-Ni steels under the selected conditions of hot deformation during high temperature mechanical treatment (HTMT). Substructure of hot deformed austenite is inherited by packet martensite during cooling. Presence of developed polygonized substructure in austenite results in grinding and high uniformity of packet sizes of martensite crystals. Substructure of α-phase of the investigated steels after HTMT, as well as the one inherited from hot deformed austenite, is inherited at α→γ-transformation in the process of repetitive austenization, and it can be preserved within a limited temperature-time range of heating in γ-region [ru

Parametrical limits of SCC-susceptibility of austenitic and austenitic-ferritic Cr-Ni steels

International Nuclear Information System (INIS)

Starosvetskij, D.I.; Baru, R.L.; Bondarenko, A.I.; Bogoyavlenskij, V.L.; Timonin, V.A.

1990-01-01

Comparative investigations into corrosion cracking (CC) of austenitic (12Kh18N10T) and austenitic-ferritic (08Kh22N6T) chromium-nickel steels are performed for various chloride media in a wide range of chloride concentrations and temperatures. It is shown that the ratio between steels in terms of their CC-susceptibility is not definite and can undergo a reversal depending on parameters of medium, level and conditions of loading. Differences in mechanisms of corrosion cracking of austenitic and austenitic-ferritic steels are established

Investigations on avoidance of hot cracks during laser welding of austenitic Cr-Ni steels and nickel-based alloys using temperature field tailoring. Final report; Untersuchungen zur Vermeidung von Heissrissen beim Laserstrahlschweissen von austenitischen Cr-Ni-Staehlen und Nickelbasislegierungen mittels Temperaturfeld-Tailoring. Schlussbericht

Energy Technology Data Exchange (ETDEWEB)

NONE

2013-08-08

The aim of the project was to transfer the developed method of laser beam welding of heat treated machining steels of temperature field tailoring on hot crack endangered austenitic Cr-Ni steels and nickel-based alloys. With this method, transient thermal stresses adjacent to the weld are produced by an travelling induction heating so that the hot cracking is prevented during welding. As test materials the austenitic Cr-Ni steel with sulfur additive 1.4305, the Cr-Ni steels 1.4404 and 1.4435 and the nickel-based alloy Udimet 720 were selected. As a result of the research it was shown that a hot crack-free laser welding in the investigated materials using at least three different welding and material-technical approaches is possible. [German] Das Ziel des Forschungsvorhabens bestand darin, das fuer das Laserstrahlschweissen verguetbarer Automatenstaehle entwickelte Verfahren des Temperaturfeld-Tailorings auf heissrissgefaehrdete austenitische Cr-Ni-Staehle und Nickelbasislegierungen zu uebertragen. Mit diesem Verfahren werden waehrend des Schweissens transiente thermische Spannungen neben der Schweissnaht durch eine mitlaufende induktive Erwaermung so erzeugt, dass die Heissrissbildung verhindert wird. Als Versuchswerkstoffe wurden der austenitische Cr-Ni-Stahl mit Schwefelzusatz 1.4305, die Cr-Ni-Staehle 1.4404 und 1.4435 sowie die Nickelbasislegierung Udimet 720 ausgewaehlt. Im Ergebnis des Forschungsvorhabens konnte gezeigt werden, dass ein heissrissfreies Laserstrahlschweissen bei den untersuchten Werkstoffen unter Nutzung von mindestens drei verschiedenen schweiss- und werkstofftechnischen Ansaetzen moeglich ist: Erstens koennen mit einem Temperaturfeld-Tailoring bei im Stumpfstoss zu verschweissenden Blechen aus austenitischen Staehlen bis mindestens 6 mm Dicke senkrecht zur Naht und parallel zur Blechoberflaeche wirkende transiente Druckspannungen erzeugt werden, die der Bildung von Mittelrippenrissen oder dazu parallel liegenden Heissrissen entgegenwirken

EXPERIMENTAL RESEARCH REGARDING THE INFLUENCE OF CUTTING REGIME ON THE WEAR OF DRILLS AT STEEL PROCESSING

Directory of Open Access Journals (Sweden)

Leonard Marius CIUREZU GHERGHE

2015-05-01

Full Text Available This paper aims to highlight the influence of cutting regime on the wear drills at steel processing , in particular the processing of stainless steel X17CrNi16-2 SR EN 10088-4 DIN 17440. We are interested in wear of the drill at processing of this type of stainless steel , which has applicability in energy industry given the special characteristics of its. We want a maximum value of 0.2 mm for the wear of the drill, measurement and taking pictures are made using a microscope DigiMicro 2.0 and the software used is MicroCapture. Processing was done on machining center YMC YOUNG TECH 1050, and the tool used was 8 mm drill bit high speed steel.

Analysis of the austenitic stainless steel's r-value behavior at elevated temperatures

OpenAIRE

Dušan Arsić; Milan Djordjević; Srbislav Aleksandrović; Vukić Lazić; Ruzica R. Nikolic; Branislav Hadzima

2015-01-01

An analysis of the anisotropy properties of austenitic steel AISI 304 (X5CrNi18-10) at elevated temperatures is presented in this paper. Considerations of the anisotropy problems are presented in the theoretical part of the paper, as well as the procedure for determination of the normal anisotropy coefficient. The experimental part of the paper describes the plan, methodology and equipment for testing of material's normal anisotropy and mechanical characteristics. The objective of conducting ...

Effect of Solution Annealing on Susceptibility to Intercrystalline Corrosion of Stainless Steel with 20% Cr and 8% Ni

Science.gov (United States)

Taiwade, R. V.; Patil, A. P.; Patre, S. J.; Dayal, R. K.

2013-06-01

In general, as-received (AR) austenitic stainless steels (ASSs) contain complex carbide precipitates due to manufacturing operations, subsequent annealing treatment, or due to the fabrication processes such as welding. The presence of pre-existing carbides leads to cumulative sensitization and make the steel susceptible to intercrystalline corrosion (ICC)/intergranular corrosion (IGC) which causes premature failure during service. Solution annealing (SA) is one of the ways to deal with such situations. In this present investigation, the AR (hot rolled and mill annealed) chromium-nickel (Cr-Ni) ASS is compared with SA Cr-Ni ASS. The extent of ICC/IGC was evaluated qualitatively and quantitatively by various electrochemical tests including ASTM standard A-262 Practice A and Practice E, double loop electrochemical potentiokinetic reactivation and electrochemical impedance spectroscopy. The degree of sensitization for hot rolled mill annealed AR condition is found to be substantially higher (51.55%) than that of SA condition (26.9%) for thermally aged samples (at 700 °C). The chemical composition across the grain boundary was measured using electron probe micro-analyzer for both (AR and SA) conditions and confirms that the pre-sensitization effect was completely removed after SA treatment.

Constant strain rate test and SCC-behaviour of stainless steels

International Nuclear Information System (INIS)

Krauss, H.; Speckhardt, H.

1979-01-01

In the present work, the stress corrosion cracking behaviour in boiling aqueous 35% magnesium chloride solution under conditions of no external current was investigated as a function of the defined extension rates for the two austenitic steels X 2 CrNi 189 and X 2 CrNiSi 1815, as well as for both ferritic austenitic steels X 6 CrNiMoCu 217 and X 2 CrNiMoN 225. The endurance time found until cracking, the maximum tensile stress, the sample stretching up to cracking and the relative rupture energy were determined for the evaluation, as well as metallographic investigations to describe the crack picture, test surface appearance and attack picture carried out. (orig.) 891 RW/orig. 892 BRE [de

Behavior of X 6 CrNi 18 11 under sequential testing of creep and fatigue

Energy Technology Data Exchange (ETDEWEB)

Husslage, W [TNO, Apeldoorn (Netherlands); Breitling, H [INTERATOM, Bergisch Gladbach (Germany)

1977-07-01

The behaviour of the austenitic stainless steel X 6 CrNi 18 11 with about 0.05% C, 18% Cr and 11% Ni was investigated under combined creep and cyclic loading at 550 degrees C. Base metal specimens and specimens containing a weld were tested by: prior cyclic loading followed by creep loading to rupture; prior creep loading followed by cyclic loading to rupture; alternating periods of creep and cyclic loading to rupture. The results were evaluated using the linear cumulative fatigue and creep damage rule. The damage factor D determined on basis of the respective behaviour of base material and welds varied between 0.5 and 1.6 if specimens containing a weld defect were not taken into consideration. Weld defects, which had predominantly an influence on fatigue, lowered the damage factor D up to 0.2. Evaluation of the results on welds with the pure creep and fatigue behaviour of base material shows damage factors between 0.4 and 0.9. By the high margins between allowable creep and fatigue life and life measured with specimens, the cumulative damages of base material and welded joints are much better than the allowable values according to CCI 1592 of the ASME Boiler and Pressure Vessel Code. (author)

Cathode-sputtered Ti-Zr-N-C-O base hard coatings and stability of said coatings on hard metals and working steels. Kathodenzerstaeubte Hartstoffschichten auf Basis Ti-Zr-N-C-O und deren Stabilitaet auf Hartmetall und Gebrauchsstaehlen

Energy Technology Data Exchange (ETDEWEB)

Boehmer, M.

1986-02-26

This paper deals with the examination of the metallurgical and thermal stability of the resistant material layers of titanium in connection with the substrate material influence. As substrate material were chosen: hard metal (81% WC, 12% TiC+TaC, 7% Co), high speed steel (DIN 1.3343), austenitic nickel chromium steel (X5 CrNi 18 9) and unalloyed tool steel (DIN 1.1545). The hard materials of titanium were deposited by means of cathode evaporation.

Impact of roughness, wettability and hydrodynamic conditions on the incrustation on stainless steel surfaces

International Nuclear Information System (INIS)

Bogacz, Wojciech; Lemanowicz, Marcin; Al-Rashed, Mohsen H.; Nakonieczny, Damian; Piotrowski, Tomasz; Wójcik, Janusz

2017-01-01

Highlights: • Steel plates (X5CrNi18-10) with different roughness and wettability were prepared. • Incrustation of MgSO 4 ·7H 2 O under laminar flow (Re = 59–178) was investigated. • Influence of surface properties and fluid velocity on incrustation was found. • Wettability and surface roughness cannot be considered separately. • Analysis of heat transfer and incrustation time-lapse videos are presented. - Abstract: The goal of this work was to investigate the influence of the stainless steel surface roughness and wettability on incrustation of MgSO 4 ·7H 2 O from aqueous solutions and resulting heat transfer resistance. The experiments were done for laminar flow (Re = 59–178) which is characteristic for regions of apparatus where fouling usually begin. A series of steel plates (X5CrNi18-10) were prepared and used as a heat transfer surfaces. Their properties, i.e. roughness, wettability and elementary composition of surfaces were determined. The experiments were done using specially designed flow cell equipped with Peltier element. Each incrustation measurement lasted for two hours, during which heat transfer resistance was measured as a function of time. After the experiments the mass of crystalline deposit was weighted. It was proved that wettability as well as surface roughness cannot be considered separately in the case of incrustation phenomenon. The knowledge of surface roughness is insufficient due to the fact, that it is possible to obtain surfaces with similar roughness but substantially different wettability for the same material.

Effect of load ratio and saltwater corrosive environment on the initiation life of fatigue of 10Ni5CrMoV steel

Science.gov (United States)

Xie, Xing; Yi, Hong; Xu, Jian; Gen, Liming; Chen, Luyun

2017-09-01

Fatigue initiation life has been studied with 10CrNi5MoV steel for use in ocean engineering at different load ratios and in different environmental media. The microstructure and micro-topography have been observed and analyzed by means of SEM, EDS and EBSD. Our findings indicate that, the initiation life of 10Ni5CrMoV steel in seawater is shorter than that in air, and the difference in longevity is larger with the increasing of load ratio. Corrosion pits had a great influence on initial corrosion fatigue life.

Propagation of semi-elliptical surface cracks in ferritic and austenitic steel plates under thermal cyclic loading

International Nuclear Information System (INIS)

Bethge, K.

1989-05-01

Theoretical and experimental investigations of crack growth under thermal and thermomechanical fatigue loading are presented. The experiments were performed with a ferritic reactor pressure vessel steel 20 MnMoNi 5 5 and an austenitic stainless steel X6 CrNi 18 11. A plate containing a semi-elliptical surface crack is heated up to a homogeneous temperature and cyclically cooled down by a jet of cold water. On the basis of linear elastic fracture mechanics stress-intensity factors are calculated with the weight function method. The prediction of crack growth under thermal fatigue loading using data from mechanical fatigue tests is compared with the experimental result. (orig.) [de

Quantitative description of changes in the structure in austenitic steels after hot temperature deformation

International Nuclear Information System (INIS)

Kuc, D.; Rodak, K.; Niewielski, G.; Hetmanczyk, M.

1998-01-01

An investigation on the structural changes in austenitic hard deformable Cr-Mn and Cr-Ni steels during dynamic recrystallization has been presented in the paper. The influence of the factors (strain rate, deformation, temperature) on the geometric characteristic of grains has been taken into consideration. Investigation of the structure were performed using metallographic microscope and transmission electron microscope. The results of researched should widen the theoretical background in order to the model of phenomena, which accompany the dynamic recovery and dynamic recrystallization. (author)

Creep and time to rupture of a 16/16 Cr Ni Steel

International Nuclear Information System (INIS)

Solano, R.; Garcia, R.; Bohm, H.; Schirra, M.

1972-01-01

The influence of different thermal-mechanical treatments on the creep and time to rupture of a 16/16 Cr.Ni steel is studied. The solution treated material after annealing at 700-800 degree centigree did not affect time to rupture. At the contrary a 12% cold-working and annealing at 800 degree centigree improve the time to rupture. This treatment is preserved up to 700 degree centigree 10 4 hours. The ductility is not strongly affected. A metallographic study of the fracture was carried out. (Author) 23 refs

Comparative studies on ultrasonic, friction, laser and resistance pressure welding of NiTi shape memory alloys with high-alloy steels. Final report; Vergleichende Untersuchungen zum Ultraschall-, Reib-, Laserstrahl- und Widerstandspressschweissen von NiTi-Shape-Memory-Metall mit hochlegierten Staehlen. Abschlussbericht

Energy Technology Data Exchange (ETDEWEB)

Zuckschwerdt, K.

2000-04-01

The suitability of different welding techniques for welding of NiTi shape memory alloys with high-alloy steel (C12CrNi17-7, X5CrNiNb19-9, X20Cr13) was investigated. The quality of the welds was analyzed using mechanical-technological, fractographic, metallographic and electron microscopy analysis. [German] Ziel dieses Forschungsvorhabens ist es, die Eignung der einzelnen Schweissverfahren fuer das Fuegen von NiTi-Formgedaechtnislegierungen mit hochlegiertem Stahl (X12CrNi17-7, X5CrNiNb19-9, X20Cr13) darzustellen und zu beurteilen. Die Qualitaet der Fuegeverbindungen wird mit Hilfe mechanisch-technologischer, fraktographischer, metallographischer und elektronenmikroskopischer Untersuchungen bewertet.

Effect of process parameters on formability of laser melting deposited 12CrNi2 alloy steel

Science.gov (United States)

Peng, Qian; Dong, Shiyun; Kang, Xueliang; Yan, Shixing; Men, Ping

2018-03-01

As a new rapid prototyping technology, the laser melting deposition technology not only has the advantages of fast forming, high efficiency, but also free control in the design and production chain. Therefore, it has drawn extensive attention from community.With the continuous improvement of steel performance requirements, high performance low-carbon alloy steel is gradually integrated into high-tech fields such as aerospace, high-speed train and armored equipment.However, it is necessary to further explore and optimize the difficult process of laser melting deposited alloy steel parts to achieve the performance and shape control.This article took the orthogonal experiment on alloy steel powder by laser melting deposition ,and revealed the influence rule of the laser power, scanning speed, powder gas flow on the quality of the sample than the dilution rate, surface morphology and microstructure analysis were carried out.Finally, under the optimum technological parameters, the Excellent surface quality of the alloy steel forming part with high density, no pore and cracks was obtained.

Hydrogen Embrittlement Mechanism in Fatigue Behaviour of Austenitic and Martensitic Stainless Steels

Directory of Open Access Journals (Sweden)

Brück Sven

2018-01-01

Full Text Available In the present study, the influence of hydrogen on the fatigue behaviour of the high strength martensitic stainless steel X3CrNiMo13-4 and the metastable austenitic stainless steels X2Crni19-11 with various nickel contents was examined in the low and high cycle fatigue regime. The focus of the investigations was the changes in the mechanisms of short crack propagation. The aim of the ongoing investigation is to determine and quantitatively describe the predominant processes of hydrogen embrittlement and their influence on the short fatigue crack morphology and crack growth rate. In addition, simulations were carried out on the short fatigue crack growth, in order to develop a detailed insight into the hydrogen embrittlement mechanisms relevant for cyclic loading conditions.

Requirements on cast steel for the primary coolant circuit of water cooled reactors

International Nuclear Information System (INIS)

The most important requirements placed on the structural components of water cooled nuclear reactors include corrosion resistance and mechanical materials properties. Intercrystalline corrosion resistance was tested using the Strauss Test in compliance with the DIN 50914 Standard. Following sensitization between 600 to 700 degC with a dwell time between 15 minutes and 100 hours, a specimen homogeneously annealed with the casting and rapidly water cooled showed no intercrystalline corrosion. Specimens cooled from 1050 degC at a rate of 100 degC per hour showed no unambiguous tendency for intercrystalline corrosion after sensitization; in some cases, however, an initial attack of intercrystalline corrosion was found. It was found that austenitic Cr-Ni cast steel containing 2.5% Mo and about 15% ferrite showed the sensitive intercrystalline corrosion range at higher temperatures and longer dwell times than rolled Cr-Ni steels. In plating the ferritic cast steel with a corrosion resistant plating material, annealing temperature after welding must not exceed 600 to 620 degC otherwise the resistance of the plated layer against intercrystalline corrosion would not be safeguarded, and following annealing for stress removal at a temperature of 600 to 620 degC all requirements must be satisfied by the weld metal and weld transition placed on the initial material. Martensite materials are used for the manufacture of components which are not used under pressure, such as alloys with 13% Cr and 1% to 6% Ni and alloys with 17% Cr and 4% Ni. Carbon content is maintained below 0.10% to guarantee good weldability and the highest corrosion resistance. Cast steels with 13% Cr and 4% Ni after a dwell of 2500 hours in fully desalinated water without oxygen and with 3600 ppm of boron at a test temperature of 95 to 300 degC showed a surface reduction of 0.005 mm annually. In identical conditions except for the water containing oxygen the reduction in surface was 0.05 mm per year. (J.B.)

Creep-rupture-test on the stainless steel X6crni1811 (Din 1.494.8) in the frame of the Extrapolation-Program. (Part III); Ensayos de fluencia lenta en el acero inoxidable X6 Cr Ni 1811 (1.4948) en el marco del Programa Extrapolacion

Energy Technology Data Exchange (ETDEWEB)

Solano, R; Schirra, M; Rivas, M de la; Barroso, S; Seith, B

1982-07-01

The austenitic stainless steel X6crni1811 (Din 1.4948) used as a structure material for the German Fast Breeder Reactor SNR 300 was creep tested in a temperature range of 550-650 degree centigree material condition as well as welded material condition. The main point of this program (Extrapolation-Program) lies in the knowledge of the creep-rupture-strength and creep-behaviour up to 3 x 10{sup 4} hours higher temperatures in order to extrapolated up to {>=}10{sup 5} hours for operating temperatures. In order to study the stress dependency of the minimum creep rate additional tests were carried out of 550 degree centigree - 750 degree centigree. The present report describes the state in the running program with test-times of 23.000 hours and results from tests up to 55.000 hours belonging to other parallel programs are taken into account. Besides the creep-rupture behaviour it is also made a study of ductility between 550 and 750 degree centigree. Extensive metallographic examinations have been made to study the fracture behaviour and changes in structure. (Author)

Study of the Weldability of Austenitic PH Steel for Power Plants

Directory of Open Access Journals (Sweden)

Ziewiec A.

2016-06-01

Full Text Available The article presents the results of Transvarestraint test of a modern precipitation hardened steel X10CrNiCuNb18-9-3 with copper. For comparison, the results of tests of conventional steel without the addition of copper X5CrNi18-10 are presented. The total length of all cracks and the maximum length of cracks were measured. The study of microstructure (LM, SEM showed that the austenitic stainless steel X10CrNiCuNb18-9-3 is very prone to hot cracking. After performing the Transvarestraint tests three types of cracks were observed: solidification cracks occurring during crystallization, liquation cracks due to segregation in the heat affected zone (HAZ and surface cracks. Niobium carbonitrides dispersed in the bands of segregation are the reason of high susceptibility to liquation cracking. Segregation of copper occurring during solidification causes of surface cracking. A combined effect of copper and stresses contributes to formation of hot microcracks. These microcracks propagate to a depth of 20-30 μm.

Laser Welding Of Finned Tubes Made Of Austenitic Steels

Directory of Open Access Journals (Sweden)

Stolecki M.

2015-09-01

Full Text Available This paper describes the technology of welding of finned tubes made of the X5CrNi1810 (1.4301 austenitic steel, developed at Energoinstal SA, allowing one to get high quality joints that meet the requirements of the classification societies (PN-EN 15614, and at the same time to significantly reduce the manufacturing costs. The authors described an automatic technological line equipped with a Trumph disc laser and a tube production technological process. To assess the quality of the joints, one performed metallographic examinations, hardness measurements and a technological attempt to rupture the fin. Analysis of the results proved that the laser-welded finned tubes were performed correctly and that the welded joints had shown no imperfections.

On the Cutting Performance of Coated HSS Taps When Machining of Austenitic Steel

Science.gov (United States)

Sliwkova, Petra; Piska, Miroslav

2014-12-01

The paper deals with a quality of the PVD coated HSS taps when cutting the stainless austenitic chromiumnickel non-stabilized steel DIN 1.4301 (X5CrNi 18-10). The main attention is focused on the analysis of loading (cutting moment, specific energy) of the HSS taps by means of pieso-electrical dynamometer Kistler 9272 and the relation between the quality of duplex and triplex PVD coatings and their effects on the quality of machined thread surfaces and tool life of the taps. The results showed a safe and stabilized cutting with acceptable quality of threads for HSSE with the TiN+TiCN+DLC coating.

Small angle neutron scattering study of the damage induced by creep deformation in AISI 304 stainless steel

International Nuclear Information System (INIS)

Boeuf, A.; Coppola, R.; Matera, R.; Rustichelli, F.; Zambonardi, F.; Puliti, P.; Melone, S.

1982-01-01

In the austenitic stainless steels, a class of materials largely used in the nuclear power plants, creep induces essentially two new microstructural effects: the nucleation and growth of grain boundary cavities and the precipitation of carbides. Carbides precipitate as a consequence of pure thermal treatment, whereas for the occurrence of voids the presence of stress is necessary. It should be noted however, that the kinetics of precipitation and even the precipitate crystal structure are changed by the introduction of dislocations due to straining during creep. The aim of the present study is a quantitative characterization of the creep damage occurring in a stainless steel of the type X 6 CrNi 8 11 (AISI 304). The experimental techniques used are optical and electron microscopy, microprobe analysis and small angle neutron scattering. This latter technique is described in more detail

Corrosion resistance of premodeled wires made of stainless steel used for heart electrotherapy leaders

International Nuclear Information System (INIS)

Przondziono, J; Szatka, W; Walke, W; Młynarski, R

2012-01-01

The purpose of the study is to evaluate resistance to electrochemical corrosion of wire made of X10CrNi18-8 stainless steel designed for use in cardiology treatment. The influence of strain formed in the premodeling process and methods of wire surface preparation to corrosive resistance in artificial plasma solution were analysed. Wire corrosion tests were carried out in the solution of artificial plasma. Resistance to electrochemical corrosion was evaluated on the ground of recorded curves of anodic polarization by means of potentiodynamic method. Potentiodynamic tests carried out enabled to determine how the resistance to pitting corrosion of wire changes, depending on strain formed in the premodeling process as well as on the method of wire surface preparation. For evaluation of phenomena occurring on the surface of tested steel, electrochemical impedance spectroscopy (EIS) was applied. Deterioration of corrosive properties of wire along with the increase in the formed strain hardening was observed.

Active flux tungsten inert gas welding of austenitic stainless steel AISI 304

Directory of Open Access Journals (Sweden)

D. Klobčar

2016-10-01

Full Text Available The paper presents the effects of flux assisted tungsten inert gas (A-TIG welding of 4 (10 mm thick austenitic stainless steel EN X5CrNi1810 (AISI 304 in the butt joint. The sample dimensions were 300 ´ 50 mm, and commercially available active flux QuickTIG was used for testing. In the planned study the influence of welding position and weld groove shape was analysed based on the penetration depth. A comparison of microstructure formation, grain size and ferrit number between TIG welding and A-TIG welding was done. The A-TIG welds were subjected to bending test. A comparative study of TIG and A-TIG welding shows that A-TIG welding increases the weld penetration depth.

High-temperature brazing of X5CrNi18 10 and NiCr20TiAl using the atmospherically plasma-sprayed L-Ni2 filler metal

International Nuclear Information System (INIS)

Wielage, B.; Drozak, J.

1992-01-01

The hybrid-technological combination of the atmospheric plasma spraying for the application of a high-temperature filler metal followed by a brazing process was analyzed in terms of structure and mechanical properties of X5CrNi18 10 and NiCr20TiAl brazing joints. The thickness of the filler metal layer was minimized at [de

Creep and time to rupture of a 16/16 Cr Ni Steel; Comportamiento a la fluencia lenta de la aleacion X 8 Cr Ni Mo Nb 1616 con distintos tratamientos termicos

Energy Technology Data Exchange (ETDEWEB)

Solano, R; Garcia, R; Bohm, H; Schirra, M

1972-07-01

The influence of different thermal-mechanical treatments on the creep and time to rupture of a 16/16 Cr.Ni steel is studied. The solution treated material after annealing at 700-800 degree centigree did not affect time to rupture. At the contrary a 12% cold-working and annealing at 800 degree centigree improve the time to rupture. This treatment is preserved up to 700 degree centigree 10{sup 4} hours. The ductility is not strongly affected. A metallographic study of the fracture was carried out. (Author) 23 refs.

Hydrogen Embrittlement Mechanism in Fatigue Behavior of Austenitic and Martensitic Stainless Steels

Directory of Open Access Journals (Sweden)

Sven Brück

2018-05-01

Full Text Available In the present study, the influence of hydrogen on the fatigue behavior of the high strength martensitic stainless steel X3CrNiMo13-4 and the metastable austenitic stainless steels X2Crni19-11 with various nickel contents was examined in the low and high cycle fatigue regime. The focus of the investigations were the changes in the mechanisms of short crack propagation. Experiments in laboratory air with uncharged and precharged specimen and uncharged specimen in pressurized hydrogen were carried out. The aim of the ongoing investigation was to determine and quantitatively describe the predominant processes of hydrogen embrittlement and their influence on the short fatigue crack morphology and crack growth rate. In addition, simulations were carried out on the short fatigue crack growth, in order to develop a detailed insight into the hydrogen embrittlement mechanisms relevant for cyclic loading conditions. It was found that a lower nickel content and a higher martensite content of the samples led to a higher susceptibility to hydrogen embrittlement. In addition, crack propagation and crack path could be simulated well with the simulation model.

Analysis of the austenitic stainless steel's r-value behavior at elevated temperatures

Directory of Open Access Journals (Sweden)

Dušan Arsić

2015-05-01

Full Text Available An analysis of the anisotropy properties of austenitic steel AISI 304 (X5CrNi18-10 at elevated temperatures is presented in this paper. Considerations of the anisotropy problems are presented in the theoretical part of the paper, as well as the procedure for determination of the normal anisotropy coefficient. The experimental part of the paper describes the plan, methodology and equipment for testing of material's normal anisotropy and mechanical characteristics. The objective of conducting the experiments was to investigate influence of temperature on normal anisotropy, as well as on the mechanical properties of the considered material. The normal anisotropy was monitored by the coefficient – the so-called "r-value". Besides that, the tensile strength, yield stress and elongation at break were monitored, also. The tests were done on the 0.7 mm thick sheet metal within the temperature range 20 to 700°C.

Investigation on fracture toughness of laser beam welded steels

International Nuclear Information System (INIS)

Riekehr, S.; Cam, G.; Santos, J.F. dos; Kocak, M.; Klein, R.M.; Fischer, R.

1999-01-01

Laser beam welding is currently used in the welding of a variety of structural materials including hot and cold rolled steels, high strength low alloy and stainless steels, aluminium and titanium alloys, refractory and high temperature alloys and dissimilar materials. This high power density welding process has unique advantages of cost effectiveness, low distortion, high welding speed, easy automation, deep penetration, narrow bead width, and narrow HAZ compared to the conventional fusion welding processes. However, there is a need to understand the deformation and fracture properties of laser beam weld joints in order to use this cost effective process for fabrication of structural components fully. In the present study, an austenitic stainless steel, X5CrNi18 10 (1.4301) and a ferritic structural steel, RSt37-2 (1.0038), with a thickness of 4 mm were welded by 5 kW CO 2 laser process. Microhardness measurements were conducted to determine the hardness profiles of the joints. Flat micro-tensile specimens were extracted from the base metal, fusion zone, and heat affected zone of ferritic joint to determine the mechanical property variation across the joint and the strength mismatch ratio between the base metal and the fusion zone. Moreover, fracture mechanics specimens were extracted from the joints and tested at room temperature to determine fracture toughness, Crack Tip Opening Displacement (CTOD), of the laser beam welded specimens. The effect of the weld region strength mis-matching on the fracture toughness of the joints have been evaluated. Crack initiation, crack growth and crack deviation processes have also been examined. These results were used to explain the influence of mechanical heterogeneity of the weld region on fracture behaviour. This work is a part of the ongoing Brite-Euram project Assessment of Quality of Power Beam Weld Joints (ASPOW). (orig.)

Potential of Aerostats for the Recovery of Disabled Main Battle Tanks and Other Heavy Military Vehicles and Equipment

Science.gov (United States)

2007-08-01

1 Material Notes: Austenitic Cr-Ni stainless steel . More corrosion resistant than Type 301 and because of higher Ni content does not work...or a refrigeration down to extremely low temperatures . To even reduce the pressure to below 2,000 bar, the tank would need to be refrigerated to...investigated for use in the ISO tank design: Stainless Steel Cold Rolled (AISI Type 302 Stainless Steel , cold rolled to 1550 Mpa tensile strength) Titanium

Oxidation and thermal shock behavior of thermal barrier coated 18/10CrNi alloy with coating modifications

Energy Technology Data Exchange (ETDEWEB)

Guergen, Selim [Vocational School of Transportation, Anadolu University, Eskisehir (Turkmenistan); Diltemiz, Seyid Fehmi [Turkish Air Force1st Air Supply and Maintenance Center Command, Eskisehir (Turkmenistan); Kushan, Melih Cemal [Dept. of Mechanical Engineering, Eskisehir Osmangazi University, Eskisehir (Turkmenistan)

2017-01-15

In this study, substrates of 18/10CrNi alloy plates were initially sprayed with a Ni-21Cr-10Al-1Y bond coat and then with an yttria stabilized zirconia top coat by plasma spraying. Subsequently, plasma-sprayed Thermal barrier coatings (TBCs) were treated with two different modification methods, namely, vacuum heat treatment and laser glazing. The effects of modifications on the oxidation and thermal shock behavior of the coatings were evaluated. The effect of coat thickness on the bond strength of the coats was also investigated. Results showed enhancement of the oxidation resistance and thermal shock resistance of TBCs following modifications. Although vacuum heat treatment and laser glazing exhibited comparable results as per oxidation resistance, the former generated the best improvement in the thermal shock resistance of the TBCs. Bond strength also decreased as coat thickness increased.

Failures by stress corrosion of electrical heating accessories, instrument leads and thermoelements of chromium nickel steel

International Nuclear Information System (INIS)

Schwarz, M.

1982-01-01

Measurement and control devices are being increasingly used for process control, monitoring and the safety of chemical plants. Pressure, temperature, through-put, moisture, composition and the like are continuously measured at many positions of the system. The supervision of the measuring equipment and hence the necessary exchanging ability of the devices during operation means good access to the plant. An extensive system of pipelines between the measuring equipment and the product lines to be supervised is the result. Common austenite 18 10 CrNi steel pipes of 12 mm diameter and 1 mm wall thickness are used for assembling and corrosion reasons in these pulse instrument leads. The failure of several instrument leads in a large scale plant at the beginning of the frost period interfers with the control. It was therefore necessary to find the exact cause; this is described in the present work. (orig.) [de

Reduction of emission when applying thermal separation processes in the dismantling of nuclear facilities - oxy-fuel gas and plasma arc cutting

International Nuclear Information System (INIS)

Stoiber, H.; Hammer, G.; Schultz, H.

1995-01-01

Plasma arc cutting and laser beam cutting was used for the studies with the goal of significantly reducing material emission by changing the operating and equipment parameters. Some separations using the oxy-fuel gas cutting process served the purpose of providing a guide for determining which factors can most effectively reduce emission. The separation experiments were carried out with specimens of R-St 37-2, 10 mm thick, as well as of X 6 CrNi 18 10 steel 5, 10, 15 and 20 mm thick. In all cases, lowering speed and the amount of gas proved at first to be effective measures to check material emission. It was also possible to achieve adherence of molten mass and slag on the flank of the joint with excessive icicling. When the plasma separates the CrNi steel, it is possible to increase emission reduction additionally by using an argon/hydrogen mixture instead of nitrogen as a cutting gas. (orig./DG) [de

RF plasma nitriding of severely deformed iron-based alloys

International Nuclear Information System (INIS)

Ferkel, H.; Glatzer, M.; Estrin, Y.; Valiev, R.Z.; Blawert, C.; Mordike, B.L.

2003-01-01

The effect of severe plastic deformation by cold high pressure torsion (HPT) on radio frequency (RF) plasma nitriding of pure iron, as well as St2K50 and X5CrNi1810 steels was investigated. Nitriding was carried out for 3 h in a nitrogen atmosphere at a pressure of 10 -5 bar and temperatures of 350 and 400 deg. C. Nitrided specimens were analysed by scanning electron microscopy (SEM), X-ray diffraction and micro hardness measurements. It was found that HPT enhances the effect of nitriding leading almost to doubling of the thickness of the nitrided layer for pure iron and the high alloyed steel. The largest increase in hardness was observed when HPT was combined with RF plasma nitriding at 350 deg. C. In the case of pure iron, the X-ray diffraction spectra showed the formation of ε and γ' nitrides in the compound layer, with a preferential formation of γ' at the expense of the α-phase at the higher nitriding temperature. The corresponding surface hardness was up to 950 HV0.01. While the HPT-processed St2K50 exhibits both nitride phases after nitriding at 350 deg. C, only the γ'-phase was observed after nitriding at 400 deg. C. A surface hardness of up to 1050 HV0.01 was measured for this steel. The high alloyed steel X5CrNi1810 exhibited the highest increase in surface hardness when HPT was combined with nitriding at 350 deg. C. The surface hardness of this steel was greater than 1400 HV0.025. The XRD analyses indicate the formation of the expanded austenite (S-phase) in the surface layer as a result of RF plasma nitriding. Furthermore, after HPT X5CrNi1810 was transformed completely into deformation martensite which did not transform back to austenite under thermochemical treatment. However, in the case of nitriding of the HPT-processed high alloyed steel at 400 deg. C, the formation of the S-phase was less pronounced. In view of the observed XRD peak broadening, the formation of nitrides, such as e.g. CrN, cannot be ruled out

Cutting using the CO laser. Trennen mit dem CO-Laser

Energy Technology Data Exchange (ETDEWEB)

Maisenhaelder, F.; Stoehr, M. (DLR, Inst. fuer Technische Physik, Stuttgart (Germany))

1991-02-01

Several cutting experiments were performed to investigate the maximum cutting speed when using CO or CO{sub 2} laser radiation. The material which was used for these experiments was mild steel (St 37) and stainless steel (V2A; X5CrNi 189), the material thickness varied from 0.5 mm to 4 mm. The cutting parameters, especially the focal power density and the focal diameter, were equal for both laser wavelengths. The experimental result shows an increased cutting speed with CO laser beams in comparison to CO{sub 2} laser beams.

Development of nitronic 50 fusion welding techniques for 4 K service

International Nuclear Information System (INIS)

Dalder, E.N.C.; Juhas, M.C.

1981-01-01

The Mirror Fusion Test Facility (MFTF-B) is a large magnetic fusion energy experiment in the tandem mirror configuration. The requirement that each pair of Yin-Yang magnets, one pair at each end of the experiment, not undergo excessive lateral motion during seismic events was found to require excessively thick (> 12.7 mm) walled tubing in the support-struts, which accelerated the flow of heat inward to the 4 K magnet case from the nearby 300 K wall of the rector vessel, when any of the Cr-Ni austenite stainless steels, such as Type 304 with a 300 K yield-strength (sigma y) of 307 mpa (min.) was considered. Since the cold end of the lateral restraining strut was to be at or near 4 K, the additional constraints of good austenite stability and resistance to brittle fracture at 4 K existed. After consideration of these constraints against available information on Cr-Ni and Cr-Mn-Ni-N 2 austenitic stainless steels, grade XM-19 (Fe-22 Cr-12 Ni-5 Mn-.04 C-.02 N 2 was chosen. The mechanical properties of these welds were studied

The influence of Boron on creep-rupture behaviour of austenitic unstabilized and Nb-stabilized stainless steel X8CrNi 1613 in unirradiated and irradiated condition

International Nuclear Information System (INIS)

Sen, Susant Kumar.

1976-10-01

The present study deals with influence of boron on creep-rupture behaviour in unirradiated condition at 650 0 C along with precipitation behaviour, heat-treatment and recrystallization of unstabilized and stabilized steel. The results of creep-rupture tests on unirradiated specimens show that boron exerts a beneficial effect on the rupture life and ductility. Boron losses its beneficial effect on creep properties in unstabilized steel by prolong creeping. The magnitude of beneficial effect of Boron on creep properties depends upon the initial boron distribution which influences the number, size and distribution of the precipitates. Boron promotes the precipitation of type M 23 C 6 Carbides in the grain as well as at the grain boundary. Boron segregates in atomic form during slow cooling from austenitizing temperature. The recrystallization will be delayed by the presence of boron. The results of creep tests at 650 0 C shows that boron exerts a beneficial effect on creep life of irradiated steels. (orig./GSC) [de

Dynamic impact response of high-density square honeycombs made of TRIP steel and TRIP matrix composite material

Directory of Open Access Journals (Sweden)

Weigelt C.

2012-08-01

Full Text Available Two designs of square-celled metallic honeycomb structures fabricated by a modified extrusion technology based on a powder feedstock were investigated. The strength and ductility of these cellular materials are achieved by an austenitic CrNi (AISI 304 steel matrix particle reinforced by an MgO partially-stabilized zirconia building up their cell wall microstructure. Similar to the mechanical behaviour of the bulk materials, the strengthening mechanism and the martensitic phase transformations in the cell walls are affected by the deformation temperature and the nominal strain rate. The microstructure evolution during quasi-static and dynamic impact compression up to high strain rates of 103 1/s influences the buckling and failure behaviour of the honeycomb structures. In contrast to bending-dominated quasi-isotropic networks like open-celled metal foams, axial compressive loading to the honeycomb’s channels causes membrane stretching as well as crushing of the vertical cell node elements and cell walls. The presented honeycomb materials differ geometrically in their cell wall thickness-to-cell size-ratio. Therefore, the failure behaviour is predominantly controlled by global buckling and torsional-flexural buckling, respectively, accompanied by plastic matrix flow and strengthening of the cell wall microstructure.

Study of corrosion in metallic coating in steel-carbon by thermal spray; Estudo de corrosao em revestimentos metalicos em aco-carbono obtidos por aspersao termica

Energy Technology Data Exchange (ETDEWEB)

Cruz, Maria C.P.; Cavalcanti, Eliane B.; Rambo, Elisabeth S.M.; Araujo, Paulo M.M. [Instituto de Tecnologia e Pesquisa (IPT), Aracaju, SE (Brazil); Santos, Anderson O. [PETROBRAS S.A., Rio de Janeiro, RJ (Brazil)

2008-07-01

The effect caused for constituent elements of the watery environment of production of the oil on metallic coverings was studied that simulate the artificial rise of the oil (connecting rods of pump mechanic). For in such a way, the techniques of electrochemical analysis had been used, as the method of linear polarization and the extrapolation of the straight line of Tafel of metallic coverings [alloy of Bronze and Aluminum; alloy of CrNi 80/20; NiCr 80/20; 95MXC (Cr: 26.5% - 31.5%, Cr: 26.5% - 31.5%, B: 3.35% - 4.15%, Mn: 1.1% - 2.2%, Itself: 1.1% -2.1%, Faith) and aluminum] on the substratum steel simulating covering in the connecting rods of pump. Oil well had been raised the resistance characteristics the polarization of the metal when submitted to the watery way surrounding it. They had been evaluated the resistance the covering polarization applied on the steel, with the objective to analyze its resistance the corrosion and to verify the possibility of its use as barrier against the problems originated for the degradation in connecting rods of pump. For the calculated Taxes of Corrosion, it can be concluded that the Aluminum coverings (0,003 mm/year) and NiCr 80/20 (0,179 mm/year) had been the ones that had presented a bigger resistance to the corrosive way. (author)

Experiments for liquid metal embrittlement of fusion reactor materials by liquid lithium

International Nuclear Information System (INIS)

Grundmann, M.; Borgstedt, H.U.

1984-10-01

The liquid metal embrittlement behaviour of two martensitic-ferritic steels [X22CrMoV121 (Nr. 1.4923) and X18CrMoVNb 121 (Nr. 1,4914)] and one austenite chromium-nickel-steel X5CrNi189 (Nr. 1.4301) was investigated. Tensile tests in liquid lithium at 200 and 250 0 C with two different strain rates on precorroded samples (1000 h at 550 0 C in lithium) were carried out. Reference values were gained from tensile tests in air (RT, 250 0 C). It is concluded that there is sufficient compatibility of the austenitic steel with liquid lithium. The use of the ferritic-martensitic steels in liquid lithium on the other hand, especially at temperatures of about 550 0 C, seems to be problematic. The experimental results led to a better understanding of LME, applying the theory of this material failure. (orig./IHOE) [de

Failure investigations in the nuclear materials laboratory

International Nuclear Information System (INIS)

Woitscheck, A.

1982-01-01

A report is given of damage to hydrostatic floating seals (with a single-stage pressure drop of 155 bar) from pressurized water reactors. The seals were manufactured from the steel X 22 CrNi 17 and plasmacoated with a layer of Cr 2 O 3 . The types of damage occurring (green discoloration and hump formation) are discussed in terms of their mechanistic causes. A further investigation involved metallographic examination with optical and scanning electron microscopes of seven specimens from thin-walled piping made of the finegrained, structural steel 17 MnMoV 6,4 in which cracking had occurred in weld regions, in particular, crack growth and the form of cracking at the weld root were investigated. (orig.) [de

Alloy development for fast induced radioactivity decay for fusion reactor applications

International Nuclear Information System (INIS)

Klueh, R.L.; Bloom, E.E.

1984-03-01

The Cr-Mo ferritic (martensitic) steels and austenitic stainless steels (primarily type 316 and variations on that composition) are the leading candidates for the structural components for future fusion reactors. However, irradiation of such steels in a fusion environment produces long-lived radioactive isotopes. These isotopes lead to difficult radioactive waste disposal problems once the structure is removed from service. Such problems could be reduced by developing steels that contain only elements that produce radioactive isotopes that decay to low levels in a reasonable time (tens of years instead of hundreds or thousands of years). This report discusses the development of such steels by making elemental substitutions in the steels now under consideration. Molybdenum must be replaced in the Cr-Mo steels; nickel and molybdenum both must be replaced in the austenitic stainless steels (the nitrogen concentration must be limited, and niobium, maintained to extremely low levels). Appropriate substitutions are tungsten for molybdenum in the Cr-Mo steels and manganese for nickel in the austenitic stainless steels. Indications are that suitable ferritic steels can be developed, but development of a nickel-free austenitic stainless steel with properties similar to the Cr-Ni stainless steels appears to be much more complex

Study of regularities in propagation of thermal fatigue cracks

International Nuclear Information System (INIS)

Tachkova, N.G.; Sobolev, N.D.; Egorov, V.I.; Rostovtsev, Yu.V.; Ivanov, Yu.S.; Sirotin, V.L.

1978-01-01

Regularities in the propagation of thermal fatigue cracks in the Cr-Ni steels of the austenite class depending upon deformation conditions in the crack zone, have been considered. Thin-walled tube samples of the Kh16N40, Kh18N20 and Kh16N15 steels have been tested in the 10O reversible 400 deg C and 100 reversible 500 deg C regimes. The samples have possessed a slot-shaped stress concentrator. Stress intensity pseudocoefficient has been calculated for the correlation of experimental data. The formula for determining crack propagation rate has been obtained. The experiments permit to conclude that propagation rate of thermal fatigue cracks in the above steels depends upon the scope of plastic deformation during a cycle and stress intensity pseudocoefficient, and is determined by plastic deformation resistance during thermal cyclic loading

Tensile properties of irradiated and fatigue exposed stainless steel DIN X 6 CrNi 1811 (similar to AISI type 304) plate and welded joints

International Nuclear Information System (INIS)

Vries, M.I. de; Schaaf, B. van der; Elen, J.D.

1979-10-01

Test specimens of plate metal and welded joints of stainless steel DIN 1.4948, which is similar to AISI type 304, have been irradiated at 723 K and 823 K up to fluences of 1.10 23 n.m -2 and 5.10 24 n.m -2 (E > 0.1 MeV). These are representative conditions for the SNR-300 reactor vessel and inner components after 16 years of operation. High-rate (depsilon/dt = 1 s -1 ) tensile tests were performed after fatigue exposure up to various fractions of fatigue life (D) ranging from 5% to 95% at the same temperatures as the nominal temperatures of the irradiation series

High temperature coatings from post processing Fe-based chips and Ni-based alloys as a solution for critical raw materials

Science.gov (United States)

Dudziak, T.; Olbrycht, A.; Polkowska, A.; Boron, L.; Skierski, P.; Wypych, A.; Ambroziak, A.; Krezel, A.

2018-03-01

Due to shortage of natural resources worldwide, it is a need to develop innovative technologies, to save natural resources and secure Critical Raw Materials (CRM). On the other hand, these new technologies should move forward materials engineering in order to develop better materials for extreme conditions. One way to develop new materials is to use post processing chips of austenitic steels (i.e. 304L stainless steel: 18/10 Cr/Ni) and other materials such as Ni-based alloy with high Cr content. In this work, the results of the preliminary study on the High Velocity Oxy Fuel (HVOF) coatings developed from 304L stainless steel chips and Haynes® 282® Ni- based alloys are shown. The study obeys development of the powder for HVOF technology. The produced coatings were exposed at high temperature at 500 and 700 °C for 100 and 300 hours respectively to assess corrosion behaviour.

Development of environmentally compatible tribosystems with PVD-technology

International Nuclear Information System (INIS)

Lugscheider, E.; Hornig, T.; Kienitz, S.; Klocke, F.; Krieg, T.

2001-01-01

PVD coatings offer a wide variety of applications. The focal point of this work is the development of an advanced type of PVD-hardcoating which allows machining with environmentally compatible lubricants. Representative examples for the investigations are the tribological systems 'turning of quenched and tempered steel 42CrMo4 V' and 'austenitic stainless steel X5CrNi18-10'. Ti-Hf-Cr-N and TiAlN/Al 2 O 3 were deposited by AIP- and H.I.S. TM - process respectively. These coating systems showed best results concerning oxidation wear and abrasive wear in former investigations. This was necessary because main cutting-edge life criterias are oxidation wear and abrasive wear at the minor cutting edge. Consequently, a high oxidation stability and a high hardness at high temperatures are required. (author)

Mechanical Properties and Microstructure of Dissimilar Material Welded Joints

Directory of Open Access Journals (Sweden)

Ziewiec A.

2014-10-01

Full Text Available The paper presents results of the mechanical testing and the microstructure analysis of dissimilar welded joint of the R350HT steel and the high-manganese (Hadfield cast steel using Cr-Ni cast steel spacer. The simulation tests of the welded joint surface deformation were carried out. The macroscopic and microscopic investigation were made using light microscopy (LM and scanning electron microscopy (SEM. Content of the magnetic phase was measured using magnetoscope. The quantitative metallographic investigation was used for assessment of ferrite and martensite contents and X-ray diffraction phase analysis was carried out. The results showed that during cooling of the spacer after welding, the transformation of metastable austenite into martensite proceeded. In addition to work hardening, the phase transformation of austenite into martensite occurs during the process of the superficial deformation of the spacer while simulated exploitation. This leads to a substantial increase of hardness, and at the same time, causes the increase of wear resistance of the welded joints of crossovers.

Sodium corrosion tests in the ML 1 circuit

International Nuclear Information System (INIS)

Borgstedt, H.U.

1977-01-01

In the ML-1 circuit of the 'Juan Vigon' research centre in Madrid, sodium corrosion tests are being carried out on the austenitic steels DIN 1.4970 (X10NiCrMoTiB1515) and DIN 1.4301 (X5CrNi189) at temperatures between 500 and 700 0 C. The exposure time of the samples amounts to 6,000 h by now. Every 1,000 h, the samples were weighed in order to measure corrosion and deposition effects. After 3,000 and 6,000 h, some selected samples were destroyed for inspection. The results are given. (GSC) [de

Biofouling of Cr-Nickel Spray Coated Films on Steel Surfaces

International Nuclear Information System (INIS)

Yoshida, Kento; Kanematsu, Hideyuki; Kuroda, Daisuke; Ikigai, Hajime; Kogo, Takeshi; Yokoyama, Seiji

2012-01-01

Nowadays, corrosion of metals brings us serious economic loss and it often reaches several percentage of GNP. Particularly the marine corrosion was serious and the counter measure was very hard to be established, since the number of factors is huge and complicated. One of the complicated factors in marine corrosion is biofouling. Biofouling was classified into two main categories, microfouling and macrofouling. The former is composed of biofilm formation mainly. Marine bacteria are attached to material surfaces, seeking for nutrition in oligotrophic environment and they excrete polysaccharide to form biofilm on metal surfaces. Then larger living matters are attached on the biofilms to develop biofouling on metal surfaces, which often lead loss and failures of metals in marine environments. From the viewpoint of corrosion protection and maintenance of marine structures, biofouling should be mitigated as much as possible. In this study, we applied spray coating to steels and investigated if chromium-nickel spray coating could mitigate the biofouling, being compared with the conventional aluminium-zinc spray coating in marine environments. The specimens used for this investigation are aluminium, zinc, aluminium-zinc, stacked chromium/nickel and those films were formed on carbon steel (JIS SS400). And the pores formed by spray coating were sealed by a commercial reagent for some specimens. All of those specimens were immersed into sea water located at Marina Kawage (854-3, Chisato, Tsu, Mie Prefecture) in Ise Bay for two weeks. The depth of the specimen was two meter from sea water surface and the distance was always kept constant, since they were suspended from the floating pier. The temperature in sea water changed from 10 to 15 degrees Celsius during the immersion test. The biofouling behavior was investigated by low vacuum SEM (Hitachi Miniscope TM1000) and X-ray fluorescent analysis. When the spray coated specimens with and without sealing agents were compared

Microbial-Influenced Corrosion of Corten Steel Compared with Carbon Steel and Stainless Steel in Oily Wastewater by Pseudomonas aeruginosa

Science.gov (United States)

Mansouri, Hamidreza; Alavi, Seyed Abolhasan; Fotovat, Meysam

2015-07-01

The microbial corrosion behavior of three important steels (carbon steel, stainless steel, and Corten steel) was investigated in semi petroleum medium. This work was done in modified nutrient broth (2 g nutrient broth in 1 L oily wastewater) in the presence of Pseudomonas aeruginosa and mixed culture (as a biotic media) and an abiotic medium for 2 weeks. The behavior of corrosion was analyzed by spectrophotometric and electrochemical methods and at the end was confirmed by scanning electron microscopy. The results show that the degree of corrosion of Corten steel in mixed culture, unlike carbon steel and stainless steel, is less than P. aeruginosa inoculated medium because some bacteria affect Corten steel less than other steels. According to the experiments, carbon steel had less resistance than Corten steel and stainless steel. Furthermore, biofilm inhibits separated particles of those steels to spread to the medium; in other words, particles get trapped between biofilm and steel.

Aircraft Steels

Science.gov (United States)

2009-02-19

component usage. PH 13-8Mo is a precipitation-hardenable martensitic stainless steel combining excellent corrosion resistance with strength. Custom 465 is...a martensitic , age-hardenable stainless steel capable of about 1,724 MPa (250 ksi) UTS when peak-aged (H900 condition). Especially, this steel can...NOTES 14. ABSTRACT Five high strength steels (4340, 300M, AerMet 100, Ferrium S53, and Hy-Tuf) and four stainless steels (High Nitrogen, 13

Steel making

CERN Document Server

Chakrabarti, A K

2014-01-01

"Steel Making" is designed to give students a strong grounding in the theory and state-of-the-art practice of production of steels. This book is primarily focused to meet the needs of undergraduate metallurgical students and candidates for associate membership examinations of professional bodies (AMIIM, AMIE). Besides, for all engineering professionals working in steel plants who need to understand the basic principles of steel making, the text provides a sound introduction to the subject.Beginning with a brief introduction to the historical perspective and current status of steel making together with the reasons for obsolescence of Bessemer converter and open hearth processes, the book moves on to: elaborate the physiochemical principles involved in steel making; explain the operational principles and practices of the modern processes of primary steel making (LD converter, Q-BOP process, and electric furnace process); provide a summary of the developments in secondary refining of steels; discuss principles a...

Corrosion engineering in nuclear power industry

International Nuclear Information System (INIS)

Prazak, M.; Tlamsa, J.; Jirousova, D.; Silber, K.

1990-01-01

Corrosion problems in nuclear power industry are discussed from the point of view of anticorrosion measures, whose aim is not only increasing the lifetime of the equipment but, first of all, securing ecological safety. A brief description is given of causes of corrosion damage that occurred at Czechoslovak nuclear power plants and which could have been prevented. These involve the corrosion of large-volume radioactive waste tanks made of the CSN 17247 steel and of waste piping of an ion exchange station made of the same material, a crack in a steam generator collector, contamination of primary circuit water with iron, and corrosion of CrNi corrosion-resistant steel in a spent fuel store. It is concluded that if a sufficient insight into the corrosion relationships exists and a reasonable volume of data is available concerning the corrosion state during the nuclear facility performance, the required safety can be achieved without adopting extremely costly anticorrosion measures. (Z.M.)

The Study on Weldability of Boron Steel and Hot-Stamped Steel by Using Laser Heat Source (Ⅲ) - Comparison on Laser Weldability of Boron Steel and Hot -Stamped Steel-

Energy Technology Data Exchange (ETDEWEB)

Choi, So Young; Kim, Jong Do [Korea Maritime and Ocean University, Busan (Korea, Republic of); Kim, Jong Su [Korea Institute of Machinery and Materials, Daejeon (Korea, Republic of)

2015-01-15

This study was conducted to compare the laser weldability of boron steel and hot-stamped steel. In general, boron steel is used in the hot-stamping process. Hot-stamping is a method for simultaneously forming and cooling boron steel in a press die after heating it to the austenitizing temperature. Hot-stamped steel has a strength of 1500 MPa or more. Thus, in this study, the laser weldability of boron steel and that of hot-stamped steel were investigated and compared. A continuous wave disk laser was used to produce butt and lap joints. In the butt welding, the critical cooling speed at which full penetration was obtained in the hot-stamped steel was lower than that of boron steel. In the lap welding, the joint widths were similar regardless of the welding speed when full penetration was obtained.

The Study on Weldability of Boron Steel and Hot-Stamped Steel by Using Laser Heat Source (Ⅲ) - Comparison on Laser Weldability of Boron Steel and Hot -Stamped Steel-

International Nuclear Information System (INIS)

Choi, So Young; Kim, Jong Do; Kim, Jong Su

2015-01-01

This study was conducted to compare the laser weldability of boron steel and hot-stamped steel. In general, boron steel is used in the hot-stamping process. Hot-stamping is a method for simultaneously forming and cooling boron steel in a press die after heating it to the austenitizing temperature. Hot-stamped steel has a strength of 1500 MPa or more. Thus, in this study, the laser weldability of boron steel and that of hot-stamped steel were investigated and compared. A continuous wave disk laser was used to produce butt and lap joints. In the butt welding, the critical cooling speed at which full penetration was obtained in the hot-stamped steel was lower than that of boron steel. In the lap welding, the joint widths were similar regardless of the welding speed when full penetration was obtained

Connections: Superplasticity, Damascus Steels, Laminated Steels, and Carbon Dating

Science.gov (United States)

Wadsworth, Jeffrey

2016-12-01

In this paper, a description is given of the connections that evolved from the initial development of a family of superplastic plain carbon steels that came to be known as Ultra-High Carbon Steels (UHCS). It was observed that their very high carbon contents were similar, if not identical, to those of Damascus steels. There followed a series of attempts to rediscover how the famous patterns found on Damascus steels blades were formed. At the same time, in order to improve the toughness at room temperature of the newly-developed UHCS, laminated composites were made of alternating layers of UHCS and mild steel (and subsequently other steels and other metals). This led to a study of ancient laminated composites, the motives for their manufacture, and the plausibility of some of the claims relating to the number of layers in the final blades. One apparently ancient laminated composite, recovered in 1837 from the great pyramid of Giza which was constructed in about 2750 B.C., stimulated a carbon dating study of ancient steels. The modern interest in "Bladesmithing" has connections back to many of these ancient weapons.

Current status of stainless steel industry and development of stainless steel

International Nuclear Information System (INIS)

Lee, Yong Deuk; Lee, Chan Soo; Kim Kwang Tae

2000-01-01

Stainless steel is not only clean and smooth in its surface, but also it is superior in quality in terms of corrosion resistance and strength. So that, it is widely in use in the field of construction, chemical installations, and other industries. Growth of stainless steel industry started since the steel technology was developed for mass production in 1960s. Since then stainless steel industry grew rapidly on account of diversified development in this field and growth rate went up to 5.8% per year comparable to 2.3% of steel growth. The rapid growth is attributed to significant industry developments in Europe and Japan in the years of 1970s and 1980s. In addition to these the expansion of stainless steel industry in Korea and Taiwan. Presently Korea produces about 120,000 tons of stainless steel and occupies about 8% of international market. This means Korea become the second largest single country in world in stainless steel production. Moreover Korea is to reinforce its domestic production line by affiliating production companies, increasing of production capability, and specializing in types of stainless steel. This paper is to describe activity of material development, and types of stainless steel for industry use. (Hong, J. S.)

[Factors influencing electrocardiogram results in workers exposed to noise in steel-making and steel-rolling workshops of an iron and steel plant].

Science.gov (United States)

Li, Y H; Yu, S F; Gu, G Z; Chen, G S; Zhou, W H; Wu, H; Jiao, J

2016-02-20

To investigate the factors influencing the electrocardiogram results in the workers exposed to noise in steel-making and steel rolling workshops of an iron and steel plant. From September to December, 2013, cluster sampling was used to select 3 150 workers exposed to noise in the steel-making and steel-rolling workshops of an iron and steel plant, and a questionnaire survey and physical examinations were performed. The number of valid workers was 2 915, consisting of 1 606 workers in the steel-rolling workshop and 1 309 in the steel-making workshop. The electrocardiogram results of the workers in steel-making and steel-rolling workshops were analyzed. The overall abnormal rate of electrocardiogram was 26.35%, and the workers in the steel-making workshop had a significantly higher abnormal rate of electrocardiogram than those in the steel-rolling workshop(32.24% vs 21.54%, Pelectrocardiogram than female workers(27.59% vs 18.61%, Pelectrocardiogram than those who did not drink(28.17% vs 23.75%, Pelectrocardiogram than those who were not exposed to high temperature(29.43% vs 20.14%, Pelectrocardiogram in the workers with cumulative noise exposure levels of electrocardiogram results. High cumulative noise exposure, alcohol consumption, and high temperature may affect the abnormal rate of electrocardiogram in the workers exposed to noise in steel-making and steel-rolling workshops.

Compactibility of atomized high-speed steel and steel 3 powders

International Nuclear Information System (INIS)

Kulak, L.D.; Gavrilenko, A.P.; Pikozh, A.P.; Kuz'menko, N.N.

1985-01-01

Spherical powders and powders of lammellar-scaly shape of high-speed R6M5K5 steel and steel 3 produced by the method of centrifugal atomization of a rotating billet under conditions of cold pressing in steel moulds are studied for thier compactability. Compacting pressure dependnences are establsihed for density of cold-pressed compacts of spherical and scaly powders. The powders of lammellar-scaly shape both of high-speed steel and steel 3 are found to possess better compactibility within a wide range of pressures as compared to powders of spherical shape. Compacts of the lammellar-scaly powders possess also higher mechanical strength

Bond characteristics of steel fiber and deformed reinforcing steel bar embedded in steel fiber reinforced self-compacting concrete (SFRSCC)

Science.gov (United States)

Aslani, Farhad; Nejadi, Shami

2012-09-01

Steel fiber reinforced self-compacting concrete (SFRSCC) is a relatively new composite material which congregates the benefits of the self-compacting concrete (SCC) technology with the profits derived from the fiber addition to a brittle cementitious matrix. Steel fibers improve many of the properties of SCC elements including tensile strength, ductility, toughness, energy absorption capacity, fracture toughness and cracking. Although the available research regarding the influence of steel fibers on the properties of SFRSCC is limited, this paper investigates the bond characteristics between steel fiber and SCC firstly. Based on the available experimental results, the current analytical steel fiber pullout model (Dubey 1999) is modified by considering the different SCC properties and different fiber types (smooth, hooked) and inclination. In order to take into account the effect of fiber inclination in the pullout model, apparent shear strengths ( τ ( app)) and slip coefficient ( β) are incorporated to express the variation of pullout peak load and the augmentation of peak slip as the inclined angle increases. These variables are expressed as functions of the inclined angle ( ϕ). Furthurmore, steel-concrete composite floors, reinforced concrete floors supported by columns or walls and floors on an elastic foundations belong to the category of structural elements in which the conventional steel reinforcement can be partially replaced by the use of steel fibers. When discussing deformation capacity of structural elements or civil engineering structures manufactured using SFRSCC, one must be able to describe thoroughly both the behavior of the concrete matrix reinforced with steel fibers and the interaction between this composite matrix and discrete steel reinforcement of the conventional type. However, even though the knowledge on bond behavior is essential for evaluating the overall behavior of structural components containing reinforcement and steel fibers

Corrosion resistant steel

International Nuclear Information System (INIS)

Zubchenko, A.S.; Borisov, V.P.; Latyshev, V.B.

1980-01-01

Corrosion resistant steel for production of sheets and tubes containing C, Mn, Cr, Si, Fe is suggested. It is alloyed with vanadium and cerium for improving tensile properties and ductility. The steel can be melted by a conventional method in electric-arc or induction furnaces. The mentioned steel is intended to be used as a substitute for nickel-bearing austenitic steels

The steel scrap age.

Science.gov (United States)

Pauliuk, Stefan; Milford, Rachel L; Müller, Daniel B; Allwood, Julian M

2013-04-02

Steel production accounts for 25% of industrial carbon emissions. Long-term forecasts of steel demand and scrap supply are needed to develop strategies for how the steel industry could respond to industrialization and urbanization in the developing world while simultaneously reducing its environmental impact, and in particular, its carbon footprint. We developed a dynamic stock model to estimate future final demand for steel and the available scrap for 10 world regions. Based on evidence from developed countries, we assumed that per capita in-use stocks will saturate eventually. We determined the response of the entire steel cycle to stock saturation, in particular the future split between primary and secondary steel production. During the 21st century, steel demand may peak in the developed world, China, the Middle East, Latin America, and India. As China completes its industrialization, global primary steel production may peak between 2020 and 2030 and decline thereafter. We developed a capacity model to show how extensive trade of finished steel could prolong the lifetime of the Chinese steelmaking assets. Secondary steel production will more than double by 2050, and it may surpass primary production between 2050 and 2060: the late 21st century can become the steel scrap age.

Preparation and characterization of 304 stainless steel/Q235 carbon steel composite material

Directory of Open Access Journals (Sweden)

Wenning Shen

Full Text Available The composite material of 304 stainless steel reinforced Q235 carbon steel has been prepared by modified hot-rolling process. The resulted material was characterized by scanning electron microscope, three-electrode method, fault current impact method, electrochemical potentiodynamic polarization curve measurement and electrochemical impedance spectroscopy. The results showed that metallurgical bond between the stainless steel layer and carbon steel substrate has been formed. The composite material exhibited good electrical conductivity and thermal stability. The average grounding resistance of the composite material was about 13/20 of dip galvanized steel. There has no surface crack and bubbling formed after fault current impact. The composite material led to a significant decrease in the corrosion current density in soil solution, compared with that of hot dip galvanized steel and bare carbon steel. On the basis polarization curve and EIS analyses, it can be concluded that the composite material showed improved anti-corrosion property than hot-dip galvanized steel. Keywords: Stainless steel, Carbon steel, Anti-corrosion, Conductivity, Electrochemical, EIS

Influence of liquid copper-silver brazing alloy on properties of high-strength and heat resistant alloys and steels

International Nuclear Information System (INIS)

Semenov, V.N.

1999-01-01

The influence of temperature, heating rate, microstructure, the duration of Cu-Ag melt attack during brazing, the thickness and the material of barrier coating on properties of materials (Ni-Cr alloys, Cr-Ni steals, a Fe-Ni base EhJ-702 alloy) being brazed is studied. The tests of specimens with a brazing alloy are carried out in the temperature range of 780-1000 deg C. It is revealed that heat resistant alloys under brazing conditions experience brittle fracture. Multiphase structure coarse grain, increased hydrogen content mechanical stress concentrators are found to intensity embrittlement of the materials. The use of barrier coating displaying a chemical affinity to the brazing alloy results in a decrease of the tendency to embrittlement

Plasma nitriding of steels

CERN Document Server

Aghajani, Hossein

2017-01-01

This book focuses on the effect of plasma nitriding on the properties of steels. Parameters of different grades of steels are considered, such as structural and constructional steels, stainless steels and tools steels. The reader will find within the text an introduction to nitriding treatment, the basis of plasma and its roll in nitriding. The authors also address the advantages and disadvantages of plasma nitriding in comparison with other nitriding methods. .

Steel

International Nuclear Information System (INIS)

Zorev, N.N.; Astafiev, A.A.; Loboda, A.S.; Savukov, V.P.; Runov, A.E.; Belov, V.A.; Sobolev, J.V.; Sobolev, V.V.; Pavlov, N.M.; Paton, B.E.

1977-01-01

Steels also containing Al, N and arsenic, are suitable for the construction of large components for high-power nuclear reactors due to their good mechanical properties such as good through-hardening, sufficiently low brittleness conversion temperature and slight displacement of the latter with neutron irradiation. Defined steels and their properties are described. (IHOE) [de

Tool steels

DEFF Research Database (Denmark)

Højerslev, C.

2001-01-01

On designing a tool steel, its composition and heat treatment parameters are chosen to provide a hardened and tempered martensitic matrix in which carbides are evenly distributed. In this condition the matrix has an optimum combination of hardness andtoughness, the primary carbides provide...... resistance against abrasive wear and secondary carbides (if any) increase the resistance against plastic deformation. Tool steels are alloyed with carbide forming elements (Typically: vanadium, tungsten, molybdenumand chromium) furthermore some steel types contains cobalt. Addition of alloying elements...... serves primarily two purpose (i) to improve the hardenabillity and (ii) to provide harder and thermally more stable carbides than cementite. Assuming proper heattreatment, the properties of a tool steel depends on the which alloying elements are added and their respective concentrations....

Atomistic study of the hardening of ferritic iron by Ni-Cr decorated dislocation loops

Science.gov (United States)

Bonny, G.; Bakaev, A.; Terentyev, D.; Zhurkin, E.; Posselt, M.

2018-01-01

The exact nature of the radiation defects causing hardening in reactor structural steels consists of several components that are not yet clearly determined. While generally, the hardening is attributed to dislocation loops, voids and secondary phases (radiation-induced precipitates), recent advanced experimental and computational studies point to the importance of solute-rich clusters (SRCs). Depending on the exact composition of the steel, SRCs may contain Mn, Ni and Cu (e.g. in reactor pressure vessel steels) or Ni, Cr, Si, Mn (e.g. in high-chromium steels for generation IV and fusion applications). One of the hypotheses currently implied to explain their formation is the process of radiation-induced diffusion and segregation of these elements to small dislocation loops (heterogeneous nucleation), so that the distinction between SRCs and loops becomes somewhat blurred. In this work, we perform an atomistic study to investigate the enrichment of loops by Ni and Cr solutes and their interaction with an edge dislocation. The dislocation loops decorated with Ni and Cr solutes are obtained by Monte Carlo simulations, while the effect of solute segregation on the loop's strength and interaction mechanism is then addressed by large scale molecular dynamics simulations. The synergy of the Cr-Ni interaction and their competition to occupy positions in the dislocation loop core are specifically clarified.

Substitution of modified 9 Cr-1 Mo steel for austentic stainless steels

International Nuclear Information System (INIS)

Sikka, V.K.

1982-04-01

This report describes the current program to develop a high-strength ferritic-martensitic steel. The alloy is essentially Fe-9% Cr-1% Mo with small additions of V and Nb and is known as modifed 9 Cr-1 Mo steel. Its elevated-temperature properties and design allowable stresses match those of type 304 stainless steel for temperatures up to 600 0 C and exceed those of other ferritic steels by factors of 2 to 3. The improved strength of this alloy permits its use in place of stainless steels for many applications

Joint research centre fusion materials irradiations in HFR: Present status and prospectives

International Nuclear Information System (INIS)

Casini, G.; Fenici, P.

1989-01-01

First a review is made of the Joint Research Centre experimental activity at HFR-Petten in the frame of the Fusion Technology and Safety Programme. The materials under investigation are: Cr-Ni Austenitic steels (316-L type) and Cr-Mn Austenitic steels (AMCR and FI type) as structural materials and Pb-17Li eutetic as tritium breeding material. The experiments on structural materials comprise: Sample irradiations with post-irradiation tensile tests (FRUST) Sample irradiations under constant load and post-irradiation strain measurement (TRIESTE) On-line creep tests (CRISP). The experiments on Pb-17Li breeder material regard sample irradiations to investigate tritium production and recovery as well as tritium permeation through blanket structures (LIBRETTO Experiment). Both irradiations on structural and breeding materials will be pursued up to the end of the current JRC-Multiannual Programme (1988-1991) and even further. In the last part of the paper expected developments of the testing programme at HFR are discussed. New areas of research should involve materials for divertor applications (NET/ITER) and advanced low activation composite materials for Commercial Power Reactors

Rheological, mechanical and tribological properties of carbon-nanofibre reinforced poly (ether ether ketone composites

Directory of Open Access Journals (Sweden)

Volker Altstaedt

2003-12-01

Full Text Available Poly(ether ether ketone nanocomposites containing vapour-grown carbon nanofibres (CNF were produced using standard polymer processing techniques. At high shear rates no significant increase in resin viscosity was observed. Nevertheless, the addition of the CNFs results in a higher melt strength at 360°C. Electron microscopy confirmed the homogeneous dispersion and alignment of nanofibres in the polymer matrix. Evaluation of the mechanical composite properties revealed a linear increase in tensile stiffness and strength with nanofibre loading fractions up to 15 wt% whilst matrix ductility was maintained up to 10 wt%. An interpretation of the composite performance by short-fibre theory resulted in rather low intrinsic stiffness properties of the vapour-grown CNF. Differential scanning calorimetry was used to investigate crystallization kinetics and degree of crystallinity. The CNFs were found not to act as nucleating sites. Furthermore, unidirectional sliding tests against two different counterpart materials (100Cr6 martensitic bearing steel, X5CrNi18-10 austenitic stainless steel were performed. The carbon nanofibres were found to reduce the wear rate of PEEK significantly.

Preparation and characterization of 304 stainless steel/Q235 carbon steel composite material

Science.gov (United States)

Shen, Wenning; Feng, Lajun; Feng, Hui; Cao, Ying; Liu, Lei; Cao, Mo; Ge, Yanfeng

The composite material of 304 stainless steel reinforced Q235 carbon steel has been prepared by modified hot-rolling process. The resulted material was characterized by scanning electron microscope, three-electrode method, fault current impact method, electrochemical potentiodynamic polarization curve measurement and electrochemical impedance spectroscopy. The results showed that metallurgical bond between the stainless steel layer and carbon steel substrate has been formed. The composite material exhibited good electrical conductivity and thermal stability. The average grounding resistance of the composite material was about 13/20 of dip galvanized steel. There has no surface crack and bubbling formed after fault current impact. The composite material led to a significant decrease in the corrosion current density in soil solution, compared with that of hot dip galvanized steel and bare carbon steel. On the basis polarization curve and EIS analyses, it can be concluded that the composite material showed improved anti-corrosion property than hot-dip galvanized steel.

Compresibility and sinterability of HCx PM steel diluted with stainless steels

Directory of Open Access Journals (Sweden)

Elena Gordo

2003-12-01

Full Text Available HCx powder metallurgy steel contains in its composition high contents of Cr and C, and significant quantities of alloy elements typical of tool steels (Mo, V, W, to provide the corrosion resistance of stainless steel with wear resistance of tool steels. HCx appears to be a suitable material for applications in aggressive environments, as valve seat inserts in automotive engines. However, this steel presents a low compressibility leading to high production costs. In this work, some results carried out to improve the compressibility of HCx are presented. The way to attempt this improvement is the dilution of base material with two stainless steels, the ferritic 430LHC and the austenitic 316L. The powder mixes prepared were uniaxially pressed to study the compressibility. The sinterability was study by determining of density, hardness, transverse rupture strength (TRS and microstructural evolution after vacuum sintering at different temperatures. As a result, better compressibility is observed in the mixes although not all of them present the properties required.

Boron Steel: An Alternative for Costlier Nickel and Molybdenum Alloyed Steel for Transmission Gears

Directory of Open Access Journals (Sweden)

A. Verma

2010-06-01

Full Text Available Case Carburized (CC low carbon steels containing Ni, Cr and Mo alloying elements are widely used for transmission gears in automobile, as it possesses desired mechanical properties. In order to cut cost and save scarce materials like Ni and Mo for strategic applications, steel alloyed with Boron has been developed, which gives properties comparable to Ni-Cr-Mo alloyed steel. In the process of steel development, care was taken to ensure precipitation of boron which results in precipitation hardening. The characterization of the developed boron steel had exhibited properties comparable to Ni-Cr-Mo alloyed steel and superior to conventional boron steel.

Interaction model of steel ladle of continuous caster in steel works

Directory of Open Access Journals (Sweden)

Huang Bang Fu

2016-01-01

Full Text Available For further research on the precondition and interoperability model of interaction ladles among continuous caster, this article takes steel ladle of Y steel works as the object of research. On the basis of turnover number calculation model of single cast steel ladle, the relationship between cast number and the turnover number and turnover times and last turnover number are further analyzed. The simulation of steel ladle turnover rules was taken on the 2 continuous casters with Gantt chart. After that, the relationships between turnover number and last turnover number and non-turnover number are researched deeply. Combining with the Gantt chart, the expressions of start casting time and empty ladle ending time and heavy ladle starting time were put forward. The precondition of steel ladle interaction is obtained, which means the exchange ladle should not undertaking transport task in first stop continuous caster, and the empty ladle end time of exchange ladle of first stop continuous caster should early than the heavy ladle start time of last stop continuous caster. After applying the model to practice, 3 steel ladles of No.2 continuous caster can be reduced. This research results is supplying theoretical basis for steel ladle controlling and production organization optimization, and enriches the theory and method of metallurgical process integration.

Initiation and growth of thermal fatigue crack networks in an AISI 304 L type austenitic stainless steel (X2 CrNi18-09)

International Nuclear Information System (INIS)

Maillot, V.

2004-01-01

We studied the behaviour of a 304 L type austenitic stainless steel submitted to thermal fatigue. Using the SPLASH equipment of CEA/SRMA we tested parallelepipedal specimens on two sides: the specimens are continuously heated by Joule effect, while two opposites faces are cyclically. cooled by a mixed spray of distilled water and compressed air. This device allows the reproduction and the study of crack networks similar to those observed in nuclear power plants, on the inner side of circuits fatigued by mixed pressurized water flows at different temperatures. The crack initiation and the network constitution at the surface were observed under different thermal conditions (Tmax = 320 deg C, ΔT between 125 and 200 deg C). The experiment produced a stress gradient in the specimen, and due to this gradient, the in-depth growth of the cracks finally stopped. The obtained crack networks were studied quantitatively by image analysis, and different parameters were studied: at the surface during the cycling, and post mortem by step-by-step layer removal by grinding. The maximal depth obtained experimentally, 2.5 mm, is relatively coherent with the finite element modelling of the SPLASH test, in which compressive stresses appear at a depth of 2 mm. Some of the crack networks obtained by thermal fatigue were also tested in isothermal fatigue crack growth under 4-point bending, at imposed load. The mechanisms of the crack selection, and the appearance of the dominating crack are described. Compared to the propagation of a single crack, the crack networks delay the propagation, depending on the severity of the crack competition for domination. The dominating crack can be at the network periphery, in that case it is not as shielded by its neighbours as a crack located in the center of the network. It can also be a straight crack surrounded by more sinuous neighbours. Indeed, on sinuous cracks, the loading is not the same all along the crack path, leading to some morphological

Age-hardening susceptibility of high-Cr ODS ferritic steels and SUS430 ferritic steel

Energy Technology Data Exchange (ETDEWEB)

Chen, Dongsheng, E-mail: chen.dongsheng85@gmail.com [Graduate School of Energy Science, Kyoto University, Gokasho, Uji, Kyoto 611-0011 (Japan); Kimura, Akihiko; Han, Wentuo; Je, Hwanil [Institute of Advanced Energy, Kyoto University, Gokasho, Uji, Kyoto 611-0011 (Japan)

2015-10-15

Highlights: • The role of oxide particles in α/α′ phase decomposition behavior; microstructure of phase decomposition observed by TEM. • The characteristics of ductility loss caused by age-hardening. • Correlation of phase decomposition and age-hardening explained by dispersion strengthened models. • Age-hardening susceptibility of ODS steels and SUS430 steel. - Abstract: The effect of aging on high-Cr ferritic steels was investigated with focusing on the role of oxide particles in α/α′ phase decomposition behavior. 12Cr-oxide dispersion strengthened (ODS) steel, 15Cr-ODS steel and commercial SUS430 steel were isothermally aged at 475 °C for up to 10,000 h. Thermal aging caused a larger hardening in SUS430 than 15Cr-ODS, while 12Cr-ODS showed almost no hardening. A characteristic of the ODS steels is that the hardening was not accompanied by the significant loss of ductility that was observed in SUS430 steel. After aging for 2000 h, SUS430 steel shows a larger ductile–brittle transition temperature (DBTT) shift than 15Cr-ODS steel, which suggests that the age-hardening susceptibility is lower in 15Cr-ODS steel than in conventional SUS430 steel. Thermal aging leaded to a large number of Cr-rich α′ precipitates, which were confirmed by transmission electron microscopy (TEM). Correlation of age-hardening and phase decomposition was interpreted by Orowan type strengthening model. Results indicate that oxide particles cannot only suppress ductility loss, but also may influence α/α′ phase decomposition kinetics.

Redemption of asthma pharmaceuticals among stainless steel and mild steel welders

DEFF Research Database (Denmark)

Kristiansen, Pernille; Jørgensen, Kristian Tore; Hansen, Johnni

2015-01-01

PURPOSE: The purpose was to examine bronchial asthma according to cumulative exposure to fume particulates conferred by stainless steel and mild steel welding through a proxy of redeemed prescribed asthma pharmaceuticals. METHODS: A Danish national company-based historical cohort of 5,303 male ever...... was estimated by combining questionnaire data on welding work with a welding exposure matrix. The estimated exposure accounted for calendar time, welding intermittence, type of steel, welding methods, local exhaustion and welding in confined spaces. Hazard ratios (HRs) with 95 % confidence intervals (CIs) were...... nonsignificant increased rate of redemption of asthma medicine was observed among high-level exposed stainless steel welders in comparison with low-level exposed welders (HR 1.54, 95 % CI 0.76-3.13). This risk increase was driven by an increase risk among non-smoking stainless steel welders (HR 1.46, 95 % CI 1...

Derivation of time dependent design-values for SNR 300 structural material

International Nuclear Information System (INIS)

Lorenz, H.; Breitling, H.; de Heesen, E.

1976-01-01

Time-dependent design values were derived from long-term creep rupture data for steel X 6 CrNi 1811 in the unwelded and welded condition. The design values had to satisfy the ASME CC 1592 criterea with respect to creep rupture strength, time to reach 1% strain and transition to tertiary creep as well as the requirement of German regulatory rules to properly account for weld bahaviour. For the evaluation and extrapolation 2 proven computer programmes were used. The design data derived under consideration of weld joints show relative good agreement with the values of ASME CC 1592. Consideration of welds leads to lower design values above 550 0 C and 5x10 3 h with the difference between rolled and weld material becoming larger with increasing time and temperature. (author)

Nitrogen-alloyed martensitic steels

International Nuclear Information System (INIS)

Berns, H.

1988-01-01

A report is presented on initial results with pressure-nitrided martensitic steels. In heat-resistant steels, thermal stability and toughness are raised by nitrogen. In cold work steel, there is a more favourable corrosion behaviour. (orig./MM) [de

MICROALLOYED STEELS FOR THE AUTOMOTIVE INDUSTRY

Directory of Open Access Journals (Sweden)

Debanshu Bhattacharya

2014-12-01

Full Text Available Two major drivers for the use of newer steels in the automotive industry are fuel efficiency and increased safety performance. Fuel efficiency is mainly a function of weight of steel parts, which in turn, is controlled by gauge and design. Safety is determined by the energy absorbing capacity of the steel used to make the part. All of these factors are incentives for the U.S. automakers to use both Highly Formable and Advanced High Strength Steels (AHSS to replace the conventional steels used to manufacture automotive parts in the past. AHSS is a general term used to describe various families of steels. The most common AHSS is the dual-phase steel that consists of a ferrite-martensite microstructure. These steels are characterized by high strength, good ductility, low tensile to yield strength ratio and high bake hardenability. Another class of AHSS is the complex-phase or multi-phase steel which has a complex microstructure consisting of various phase constituents and a high yield to tensile strength ratio. Transformation Induced Plasticity (TRIP steels is another class of AHSS steels finding interest among the U.S. automakers. These steels consist of a ferrite-bainite microstructure with significant amount of retained austenite phase and show the highest combination of strength and elongation, so far, among the AHSS in use. High level of energy absorbing capacity combined with a sustained level of high n value up to the limit of uniform elongation as well as high bake hardenability make these steels particularly attractive for safety critical parts and parts needing complex forming. A relatively new class of AHSS is the Quenching and Partitioning (Q&P steels. These steels seem to offer higher ductility than the dual-phase steels of similar strengths or similar ductility as the TRIP steels at higher strengths. Finally, martensitic steels with very high strengths are also in use for certain parts. The most recent initiative in the area of AHSS

Notch aspects of RSP steel microstructure

Directory of Open Access Journals (Sweden)

Michal Černý

2012-01-01

Full Text Available For a rather long time, basic research projects have been focused on examinations of mechanical properties for Rapid Solidification Powder (RSP steels. These state-of-art steels are commonly known as “powdered steels“. In fact, they combine distinctive attributes of conventional steel alloys with unusual resistance of construction material manufactured by so called “pseudo-powdered” metallurgy.Choice of suitable materials for experimental verification was carried out based on characteristic application of so called “modern steel”. First, groups of stainless and tool steel types (steel grades ČSN 17 and 19 were selected. These provided representative specimens for the actual comparison experiment. For stainless steel type, two steel types were chosen: hardenable X47Cr14 (ČSN 17 029 stainless steel and non-hardenable X2CrNiMo18-14-3 (ČSN 17 350 steel. They are suitable e.g. for surgical tools and replacements (respectively. For tooling materials, C80U (ČSN 19 152 carbon steel and American D2 highly-alloyed steel (ČSN “equivalent” being 19 572 steel were chosen for the project. Finally, the M390 Böhler steel was chosen as representative of powdered (atomized steels. The goal of this paper is to discuss structural aspects of modern stainless and tool steel types and to compare them against the steel made by the RSP method. Based on the paper's results, impact of powdered steel structural characteristics on the resistance to crack initiation shall be evaluated.

Steel-reinforced concrete-filled steel tubular columns under axial and lateral cyclic loading

Science.gov (United States)

Farajpourbonab, Ebrahim; Kute, Sunil Y.; Inamdar, Vilas M.

2018-03-01

SRCFT columns are formed by inserting a steel section into a concrete-filled steel tube. These types of columns are named steel-reinforced concrete-filled steel tubular (SRCFT) columns. The current study aims at investigating the various types of reinforcing steel section to improve the strength and hysteresis behavior of SRCFT columns under axial and lateral cyclic loading. To attain this objective, a numerical study has been conducted on a series of composite columns. First, FEM procedure has been verified by the use of available experimental studies. Next, eight composite columns having different types of cross sections were analyzed. For comparison purpose, the base model was a CFT column used as a benchmark specimen. Nevertheless, the other specimens were SRCFT types. The results indicate that reinforcement of a CFT column through this method leads to enhancement in load-carrying capacity, enhancement in lateral drift ratio, ductility, preventing of local buckling in steel shell, and enhancement in energy absorption capacity. Under cyclic displacement history, it was observed that the use of cross-shaped reinforcing steel section causes a higher level of energy dissipation and the moment of inertia of the reinforcing steel sections was found to be the most significant parameter affecting the hysteresis behavior of SRCFT columns.

Structural amorphous steels

International Nuclear Information System (INIS)

Lu, Z.P.; Liu, C.T.; Porter, W.D.; Thompson, J.R.

2004-01-01

Recent advancement in bulk metallic glasses, whose properties are usually superior to their crystalline counterparts, has stimulated great interest in fabricating bulk amorphous steels. While a great deal of effort has been devoted to this field, the fabrication of structural amorphous steels with large cross sections has remained an alchemist's dream because of the limited glass-forming ability (GFA) of these materials. Here we report the discovery of structural amorphous steels that can be cast into glasses with large cross-section sizes using conventional drop-casting methods. These new steels showed interesting physical, magnetic, and mechanical properties, along with high thermal stability. The underlying mechanisms for the superior GFA of these materials are discussed

Prospects of structural steels

International Nuclear Information System (INIS)

Bannykh, O.A.

2012-01-01

The current state of world steel production is considered as well as the development strategy of metallurgy industry in the Russian Federation through to 2020. The main factors determining the conservation of steel as perspective material for industry are given: energy expenses on production, the well-proven recirculation technology, the capability of changing steel properties in wide range, temperature range of operation. The conclusion is made that in the immediate future steel will not lose its importance [ru

Mechanical properties and fatigue strength of high manganese non-magnetic steel/carbon steel welded joints

International Nuclear Information System (INIS)

Nakaji, Eiji; Ikeda, Soichi; Kim, You-Chul; Nakatsuji, Yoshihiro; Horikawa, Kosuke.

1997-01-01

The dissimilar materials welded joints of high manganese non-magnetic steel/carbon steel (hereafter referred to as DMW joints), in which weld defects such as hot crack or blowhole are not found, were the good quality. Tensile strength of DMW joints was 10% higher than that of the base metal of carbon steel. In the bend tests, the DMW joints showed the good ductility without crack. Charpy absorbed energy at 0(degC) of the DMW joints was over 120(J) in the bond where it seems to be the lowest. Large hardening or softening was not detected in the heat affected zone. Fatigue strength of the DMW joints is almost the same with that of the welded joints of carbon steel/carbon steel. As the fatigue strength of the DMW joints exceeds the fatigue design standard curve of JSSC for carbon steel welded joints, the DMW joints can be treated the same as the welded joints of carbon steel/carbon steel of which strength is lower than that of high manganese non-magnetic steel, from the viewpoint of the fatigue design. (author)

Damascus steel ledeburite class

Science.gov (United States)

Sukhanov, D. A.; Arkhangelsky, L. B.; Plotnikova, N. V.

2017-02-01

Discovered that some of blades Damascus steel has an unusual nature of origin of the excess cementite, which different from the redundant phases of secondary cementite, cementite of ledeburite and primary cementite in iron-carbon alloys. It is revealed that the morphological features of separate particles of cementite in Damascus steels lies in the abnormal size of excess carbides having the shape of irregular prisms. Considered three hypotheses for the formation of excess cementite in the form of faceted prismatic of excess carbides. The first hypothesis is based on thermal fission of cementite of a few isolated grains. The second hypothesis is based on the process of fragmentation cementite during deformation to the separate the pieces. The third hypothesis is based on the transformation of metastable cementite in the stable of angular eutectic carbide. It is shown that the angular carbides are formed within the original metastable colony ledeburite, so they are called “eutectic carbide”. It is established that high-purity white cast iron is converted into of Damascus steel during isothermal soaking at the annealing. It was revealed that some of blades Damascus steel ledeburite class do not contain in its microstructure of crushed ledeburite. It is shown that the pattern of carbide heterogeneity of Damascus steel consists entirely of angular eutectic carbides. Believe that Damascus steel refers to non-heat-resistant steel of ledeburite class, which have similar structural characteristics with semi-heat-resistant die steel or heat-resistant high speed steel, differing from them only in the nature of excess carbide phase.

Micro-Abrasion Wear Resistance of Borided 316L Stainless Steel and AISI 1018 Steel

Science.gov (United States)

Reséndiz-Calderon, C. D.; Rodríguez-Castro, G. A.; Meneses-Amador, A.; Campos-Silva, I. E.; Andraca-Adame, J.; Palomar-Pardavé, M. E.; Gallardo-Hernández, E. A.

2017-11-01

The 316L stainless steel has high corrosion resistance but low tribological performance. In different industrial sectors (biomedical, chemical, petrochemical, and nuclear engineering), improvement upon wear resistance of 316L stainless steel components using accessible and inexpensive methods is critical. The AISI 1018 steel is widely used in industry, but its tribological performance is not the best among steels. Therefore, in this study the behavior of the borided 316L stainless steel and 1018 steel is evaluated under micro-abrasion wear. The boriding was carried out at 1223 K over 6 h of exposure time, resulting in a biphase layer composed of FeB/Fe2B phases. In order to evaluate Fe2B phase with no influence from FeB phase, AISI 1018 steel samples were borided at 1273 K for over 20 min and then diffusion annealed at 1273 K over 2 h to obtain a Fe2B mono-phase layer. Micro-abrasion wear resistance was evaluated by a commercial micro-abrasion testing rig using a mix of F-1200 SiC particles with deionized water as abrasive slurry. The obtained wear rates for FeB and Fe2B phases and for the 316L stainless steel were compared. Wear resistance of 316L stainless steel increases after boriding. The wear mechanisms for both phases and for the stainless steel were identified. Also, transient conditions for rolling and grooving abrasion were determined for the FeB and Fe2B phases.

Stahlschüssel key to steel

CERN Document Server

Wegst, W S

2016-01-01

The Key to Steel (Stahlschlüssel/Stahlschluessel) cross reference book will help you to decode / decipher steel designations and find equivalent materials worldwide. The 2016 edition includes more than 70,000 standard designations and trade names from approximately 300 steelmakers and suppliers. Presentation is trilingual: English, French, and German. Materials covered include structural steels, tool steels, valve steels, high temperature steels and alloys, stainless and heat-resisting steels, and more. Standards and designations from 25 countries are cross-referenced.

Methods of forging steel

OpenAIRE

Pečoler, Primož

2014-01-01

The following work presents processes of steel forming, challenges when forging steel, forming machines suitable for forging and which choice of machine is most suitable for forging. We can separate steel forming to free forging and drop forging. Free forging can be divided to hand forging and machine forging. The correct choice of furnaces is also very important. We must reach correct temperature in the furnace for raw steel to melt with less scalings. In diploma I mentioned some machine...

Corrosion characteristics of DMR-1700 steel and comparison with different steels in marine environment

International Nuclear Information System (INIS)

Gurrappa, I.; Malakondaiah, G.

2005-01-01

In the present paper, a systematic corrosion study has been carried out on DMR-1700 steel to understand the protective nature of oxide scale that forms on its surface under marine environmental conditions. Further, the studies related to oxide scales as well as pitting and crevice corrosion resistance of both stainless steels and widely used low alloy steel EN24 in marine environment have been studied for comparison purpose. The surface morphologies of corroded steels have been observed under scanning electron microscope (SEM) in order to understand the nature of corrosion. A high performance protective coating that has been developed for protection of low alloy steels DMR-1700 and EN24 against corrosion is presented after stressing the importance of surface engineering in enhancing the life of steels. Based on the studies with different techniques, DMR-1700 steel has been recommended for manufacture of components used in aerospace systems in association with appropriate protective coating for improving their efficiency

Characterization of D2 tool steel friction surfaced coatings over low carbon steel

International Nuclear Information System (INIS)

Sekharbabu, R.; Rafi, H. Khalid; Rao, K. Prasad

2013-01-01

Highlights: • Solid state coating by friction surfacing method. • D2 tool steel is coated over relatively softer low carbon steel. • Defect free interface between tool steel coating and low carbon steel substrate. • D2 coatings exhibited higher hardness and good wear resistance. • Highly refined martensitic microstructure in the coating. - Abstract: In this work D2 tool steel coating is produced over a low carbon steel substrate using friction surfacing process. The process parameters are optimized to get a defect free coating. Microstructural characterization is carried out using optical microscopy, scanning electron microscopy and X-ray diffraction. Infrared thermography is used to measure the thermal profile during friction surfacing of D2 steel. Wear performance of the coating is studied using Pin-on-Disk wear tests. A lower rotational speed of the consumable rod and higher translational speed of the substrate is found to result in thinner coatings. Friction surfaced D2 steel coating showed fine-grained martensitic microstructure compared to the as-received consumable rod which showed predominantly ferrite microstructure. Refinement of carbides in the coating is observed due to the stirring action of the process. The infrared thermography studies showed the peak temperature attained by the D2 coating to be about 1200 °C. The combined effect of martensitic microstructure and refined carbides resulted in higher hardness and wear resistance of the coating

Methods of making bainitic steel materials

Science.gov (United States)

Bakas, Michael Paul; Chu, Henry Shiu-Hung; Zagula, Thomas Andrew; Langhorst, Benjamin Robert

2018-01-16

Methods of making bainitic steels may involve austenitizing a quantity of steel by exposing the quantity of steel to a first temperature. A composition of the quantity of steel may be configured to impede formation of non-bainite ferrite, pearlite, and Widmanstatten ferrite. The quantity of steel may be heat-treated to form bainite by exposing the quantity of steel to a second, lower temperature. The second, lower temperature may be stabilized by exposing the quantity of steel to the second, lower temperature in the presence of a thermal ballast.

Milled Die Steel Surface Roughness Correlation with Steel Sheet Friction

DEFF Research Database (Denmark)

Berglund, J.; Brown, C.A.; Rosén, B.-G.

2010-01-01

This work investigates correlations between the surface topography ofmilled steel dies and friction with steel sheet. Several die surfaces were prepared by milling. Friction was measured in bending under tension testing. Linear regression coefficients (R2) between the friction and texture...

Steels from materials science to structural engineering

CERN Document Server

Sha, Wei

2013-01-01

Steels and computer-based modelling are fast growing fields in materials science as well as structural engineering, demonstrated by the large amount of recent literature. Steels: From Materials Science to Structural Engineering combines steels research and model development, including the application of modelling techniques in steels.  The latest research includes structural engineering modelling, and novel, prototype alloy steels such as heat-resistant steel, nitride-strengthened ferritic/martensitic steel and low nickel maraging steel.  Researchers studying steels will find the topics vital to their work.  Materials experts will be able to learn about steels used in structural engineering as well as modelling and apply this increasingly important technique in their steel materials research and development. 

Microstructural characterisation and corrosion performance of old railway girder bridge steel and modern weathering structural steel

International Nuclear Information System (INIS)

Tewary, N.K.; Kundu, A.; Nandi, R.; Saha, J.K.; Ghosh, S.K.

2016-01-01

Highlights: • Microstructure and corrosion performance are compared for two structural steels. • Microstructure evolution shows primarily ferrite-pearlite in both the steels. • Steels show higher corrosion rate in 1% HCl solution than in 3.5% NaCl solution. • The corrosion products show the presence of oxide, hydroxide and oxy-hydroxides. • The corroded surface reveals morphologies like flowery, cotton balls and rosette. - Abstract: A comparison on microstructure and corrosion performance has been made between the two structural steels used in old railway girder bridge (Sample A) and modern grades of weathering structural steel (Sample B). The microstructures, viewed under optical microscope and scanning electron microscope (SEM), show mainly ferrite-pearlite phase constituents in both the steels, A and B. The phase fraction analysis shows higher amount of pearlite in steel A compared to that of steel B. The grain size of steel A is larger than that of steel B under identical processing condition. The immersion corrosion test in 3.5% NaCl shows that the corrosion rate of steel A increases with time, while the same for steel B decreases with time. On the other hand, corrosion test in 1% HCl shows that the corrosion rate of both steel A and B is higher as compared to that of NaCl which always decreases with time. The XRD analysis of corrosion products show the presence of many oxides, hydroxide and oxy-hydroxide like Lepidocrocite (γ-FeOOH), Goethite (α-FeOOH), Akaganeite (β-FeOOH), Magnetite (Fe_3O_4) and Maghemite (γ-Fe_2O_3) in both the steels. The SEM images of corroded surfaces reveal different morphologies like flowery, cotton balls and rosette etc. which indicate that the corrosion products primarily contain Lepidocrocite (γ-FeOOH), Goethite (α-FeOOH) and Akaganeite (β-FeOOH).

Microstructural characterization in dissimilar friction stir welding between 304 stainless steel and st37 steel

International Nuclear Information System (INIS)

Jafarzadegan, M.; Feng, A.H.; Abdollah-zadeh, A.; Saeid, T.; Shen, J.; Assadi, H.

2012-01-01

In the present study, 3 mm-thick plates of 304 stainless steel and st37 steel were welded together by friction stir welding at a welding speed of 50 mm/min and tool rotational speed of 400 and 800 rpm. X-ray diffraction test was carried out to study the phases which might be formed in the welds. Metallographic examinations, and tensile and microhardness tests were used to analyze the microstructure and mechanical properties of the joint. Four different zones were found in the weld area except the base metals. In the stir zone of the 304 stainless steel, a refined grain structure with some features of dynamic recrystallization was evidenced. A thermomechanically-affected zone was characterized on the 304 steel side with features of dynamic recovery. In the other side of the stir zone, the hot deformation of the st37 steel in the austenite region produced small austenite grains and these grains transformed to fine ferrite and pearlite and some products of displacive transformations such as Widmanstatten ferrite and martensite by cooling the material after friction stir welding. The heat-affected zone in the st37 steel side showed partially and fully refined microstructures like fusion welding processes. The recrystallization in the 304 steel and the transformations in the st37 steel enhanced the hardness of the weld area and therefore, improved the tensile properties of the joint. - Highlights: ► FSW produced sound welds between st37 low carbon steel and 304 stainless steel. ► The SZ of the st37 steel contained some products of allotropic transformation. ► The material in the SZ of the 304 steel showed features of dynamic recrystallization. ► The finer microstructure in the SZ increased the hardness and tensile strength.

Comparison of the performance of concrete-filled steel tubular and hollow steel diagrid buildings

Science.gov (United States)

Peter, Minu Ann; S, Sajith A.; Nagarajan, Praveen

2018-03-01

In the recent construction scenario, diagrid structures are becoming a popular high-rise building structural system. Diagrid structures consist of diagonals in the perimeter and an interior core. The corner and interior vertical columns are not required due to the structural efficiency of diagrid structural systems. Steel and concrete are commonly used material for diagrid. An alternate material for diagrid is concrete-filled steel tube (CFST). CFST incorporates the advantages of both steel and concrete. In CFST, the inward buckling of the steel tube is effectively prevented by the filled concrete. The compressive strength of concrete increases due to the tri-axial state of stress in concrete induced by the steel tube. The longitudinal as well as lateral reinforcement to the concrete core is also provided by the steel tube. This paper compares the performance of CFST and steel diagrid buildings using linear static analysis. For this purpose, a 12 storey and 36 storey building are analysed using finite element method and CFST diagrid building is found to perform better.

Hydrogen gas embrittlement of stainless steels mainly austenitic steels. Volumes 1 and 2

International Nuclear Information System (INIS)

Azou, P.

1988-01-01

Steel behavior in regard to hydrogen is examined especially austenitic steels. Gamma steels are studied particularly the series 300 with various stabilities and gamma steels with improved elasticity limit for intermetallic phase precipitation and nitrogen additions. A two-phase structure γ + α' is also studied. All the samples are tested for mechanical behavior in gaseous hydrogen. Influence of metallurgical effects and of testing conditions on hydrogen embrittlement are evidenced. Microstructure resulting from mechanical or heat treatments, dislocation motion during plastic deformation and influence of deformation rate are studied in detail [fr

Some comments about the situation of the Steel Industry in the Arab Countries (Arab Steel Summit)

International Nuclear Information System (INIS)

Haidar, Y.; Astier, J.

2009-01-01

The Arab Steel Summit, that convened in Abu Dhabi in April, gave us another opportunity to review the situation of the Arab Iron and Steel Industry, with regard to the present World economic context. We will address: - the World situation of steel production, focusing on the Arab Countries; - the related situation of steel consumption; - the steel trade, including imports, exports and prices; - the consequences for technology and economy. (authors)

Challenges in Special Steel Making

Science.gov (United States)

Balachandran, G.

2018-02-01

Special bar quality [SBQ] is a long steel product where an assured quality is delivered by the steel mill to its customer. The bars have enhanced tolerance to higher stress application and it is demanded for specialised component making. The SBQ bars are sought for component making processing units such as closed die hot forging, hot extrusion, cold forging, machining, heat treatment, welding operations. The final component quality of the secondary processing units depends on the quality maintained at the steel maker end along with quality maintained at the fabricator end. Thus, quality control is ensured at every unit process stages. The various market segments catered to by SBQ steel segment is ever growing and is reviewed. Steel mills need adequate infrastructure and technological capability to make these higher quality steels. Some of the critical stages of processing SBQ and the critical quality maintenance parameters at the steel mill in the manufacture has been brought out.

Trends in steel technology

International Nuclear Information System (INIS)

Anon.

1980-01-01

Dual phase steels, composite products, and microalloyed steels are making inroads in the automotive industry applications for bumpers, automotive parts, bodies, mechanical parts, suspension and steering equipment and truck bumpers. New steels are also used to support solar mirrors and cells, in corrosive environments in the oil and gas industry, fusion reactors, and pressure vessels in nuclear power plants

Analysis of the Behaviour of Composite Steel and Steel Fiber Reinforced Concrete Slabs

Directory of Open Access Journals (Sweden)

Mindaugas Petkevičius

2011-04-01

Full Text Available There was a pending influence of steel fiber on the strength and stiffness of composite steel–concrete slabs under statical short–time load. Steel profiled sheeting and steel fiber reinforced concrete were used for specimens. Four composite slabs were made. Experimental investigations into the behaviour and influence of steel fiber reinforced concrete in composite slabs were conducted. Transverse, longitudinal, shear deformation and deflection of the slab were measured. The results indicated that the use of steel fiber in composite slabs was effective: strength was 20–24 % higher and the meanings of deflections under the action of the bending moment were 0,6MR (where MR is the bending moment at failure of the slabs and were 16–18 % lower for slabs with usual concrete. Article in Lithuanian

Ductile fracture of two-phase welds under 77K. [Steel-EhP810, steel-EhP666, steel-08Kh18N10T, steel-EhP659-VI, steel-chP810

Energy Technology Data Exchange (ETDEWEB)

Yushchenko, K.A.; Voronin, S.A.; Pustovit, A.I.; Shavel' , A.V.

The effect of the type of welding and fillers on crack resistance of welded joints high-strength steel EhP810 and its various compounds with steels EhP666, 08Kh18N10T has been studied. For the welding of steel EhP810 with steels EhP810, EhP666, 08Kh18N10T electron-beam, automatic, argon tungsten arc with non-consumable electrode with various fillers, as well as argon metal-arc welding with consumable electrode, were used. It is shown, that for a joint, made by electron-beam welding, parameters sigmasub(u), Ksub(IcJ), KCV are higher than for a joint of a similar phase structure made using filler wire EhP659-VI. It is explained by the fact, that during electron-beam welding joint metal refining takes place, which removes gases. In welded joints of chP810 steel, having joints with austenitic structure, characteristic of crack resistance Ssub(c) increases by more than 0.2 mm in contrast to two-phase joints, which conventional yield strength at 77 K exceeds 1000 MPa. It is worth mentioning, that for other classes of steels formation of two-phase structure of joint increases welded joint resistance to brittle fracture. It is possible to obtain the required structure of joint with assigned level of resistance to brittle fracture by means of the use of different fillers, optimum and welding procedure, regulating the part of the basic metal in joint content.

Steel Industry Wastes.

Science.gov (United States)

Schmidtke, N. W.; Averill, D. W.

1978-01-01

Presents a literature review of wastes from steel industry, covering publications of 1976-77. This review covers: (1) coke production; (2) iron and steel production; (3) rolling operations; and (4) surface treatment. A list of 133 references is also presented. (NM)

Fatigue damage of steel components

DEFF Research Database (Denmark)

Fæster, Søren; Zhang, Xiaodan; Huang, Xiaoxu

2014-01-01

Railway rails and the inner ring in roller bearings in wind turbines are both experiencing steel-to-steel contact in small areas with huge loads resulting in extremely high stresses in the base materials......Railway rails and the inner ring in roller bearings in wind turbines are both experiencing steel-to-steel contact in small areas with huge loads resulting in extremely high stresses in the base materials...

Corrosion of mild steel and stainless steel by marine Vibrio sp.

Digital Repository Service at National Institute of Oceanography (India)

PrabhaDevi; Wagh, A.B.

Microbially induced corrosion (MIC) of stainless steel and mild steel coupons exposed to media with and without a bacterial culture Vibrio sp. was studied using Scanning Electron Microscope (SEM). Pitting type of corrosion was noticed which was more...

The Study for Recycling NORM - Contaminated Steel Scraps from Steel Industry

International Nuclear Information System (INIS)

Tsai, K. F.; Lee, Y. S.; Chao, H. E.

2003-01-01

Since 1994, most of the major steel industries in Taiwan have installed portal monitor to detect the abnormal radiation in metal scrap feed. As a result, the discovery of NORM (Naturally Occurring Radioactive Material) has increased in recent years. In order to save the natural resources and promote radiation protection, an experimental melting process for the NORM contaminated steel scraps was carried out by the Institute of Nuclear Energy Research (INER) Taiwan, ROC. The experimental melting process has a pretreatment step that includes a series of cutting and removal of scales, sludge, as well as combustible and volatile materials on/in the steel scraps. After pretreatment the surface of the steel scraps are relatively clean. Then the scraps are melted by a pilot-type induction furnace. This experiment finally produced seven ingots with a total weight of 2,849 kg and 96.8% recovery. All of the surface dose rates are of the background values. The activity concentrations of these ingots are also below the regulatory criteria. Thus, these NORM-bearing steel scraps are ready for recycling. This study has been granted by the regulatory authority

Steel: Price and Policy Issues

National Research Council Canada - National Science Library

Cooney, Stephen

2006-01-01

Steel prices remain at historically elevated levels. The rapid growth of steel production and demand in China is widely considered as a major cause of the increases in both steel prices and the prices of steelmaking inputs...

5l/h pump for dosing corrosion radioactive liquids

International Nuclear Information System (INIS)

Przybylovich, S.; Shraer, V.; Chermak, R.

1977-01-01

The technical requirements, design and main technical characteristics of the pump for dosing corrosion and radioactive liquids with capacity up to 5 l/h are described. The design is based on the popular sixvertical split casing pump. The pump has four separate pump membrane type blocks with nonstraight hydraulic membrane control. The membranes are made of the cold worked CrNi(18/10)type stainless steel with thickness up to 0.1 mm and have the lifetime up to 3000 hours. The remote pump heads are used for pumping radioactive fluids when the pumping goes behind the safe wall, separating the pump from a hot lab. The tests showed that the pump secures the satisfactory accuracy of dozing and uniformity of pumping and that it is really possible to achieve the required life time of 10000 hours by this pump

In situ 3D monitoring of corrosion on carbon steel and ferritic stainless steel embedded in cement paste

International Nuclear Information System (INIS)

Itty, Pierre-Adrien; Serdar, Marijana; Meral, Cagla; Parkinson, Dula; MacDowell, Alastair A.; Bjegović, Dubravka; Monteiro, Paulo J.M.

2014-01-01

Highlights: • The morphology of the corrosion of steel in cement paste was studied in situ. • During galvanostatic corrosion, carbon steel reinforcement corroded homogeneously. • On ferritic stainless steel, deep corrosion pits formed and caused wider cracks. • The measured rate of steel loss correlated well with Faraday’s law of electrolysis. - Abstract: In a X-ray microcomputed tomography study, active corrosion was induced by galvanostatically corroding steel embedded in cement paste. The results give insight into corrosion product build up, crack formation, leaching of products into the cracks and voids, and differences in morphology of corrosion attack in the case of carbon steel or stainless steel reinforcement. Carbon steel was homogeneously etched away with a homogeneous layer of corrosion products forming at the steel/cement paste interface. For ferritic stainless steel, pits were forming, concentrating the corrosion products locally, which led to more extensive damage on the cement paste cover

Fracture Mechanisms in Steel Castings

Directory of Open Access Journals (Sweden)

Stradomski Z.

2013-09-01

Full Text Available The investigations were inspired with the problem of cracking of steel castings during the production process. A single mechanism of decohesion - the intergranular one - occurs in the case of hot cracking, while a variety of structural factors is decisive for hot cracking initiation, depending on chemical composition of the cast steel. The low-carbon and low-alloyed steel castings crack due to the presence of the type II sulphides, the cause of cracking of the high-carbon tool cast steels is the net of secondary cementite and/or ledeburite precipitated along the boundaries of solidified grains. Also the brittle phosphor and carbide eutectics precipitated in the final stage solidification are responsible for cracking of castings made of Hadfield steel. The examination of mechanical properties at 1050°C revealed low or very low strength of high-carbon cast steels.

On choice of tempered steels

International Nuclear Information System (INIS)

Govorov, A.A.; Pan'shin, I.F.; Rakhmanov, V.I.

1978-01-01

For the purpose of developing a graphical method for choosing structural steels, a change in the propagation work of a crack and in the critical temperature of brittleness of 40, 40Kh, 40KhN, and 40KhNM steels, was examined depending on the hardness after hardening and tempering. A diagram enabling to choose the grade of steel for making an article of known dimensions according to the preset values of its mechanical properties has been plotted. The developed selection scheme takes into account the hardenability of steels and the influence of the hardness after thermal treatment on the cold-shortness of steel

Volatilization from PCA steel alloy

Energy Technology Data Exchange (ETDEWEB)

Hagrman, D.L.; Smolik, G.R.; McCarthy, K.A.; Petti, D.A.

1996-08-01

The mobilizations of key components from Primary Candidate Alloy (PCA) steel alloy have been measured with laboratory-scale experiments. The experiments indicate most of the mobilization from PCA steel is due to oxide formation and spalling but that the spalled particles are large enough to settle rapidly. Based on the experiments, models for the volatization of iron, manganese, and cobalt from PCA steel in steam and molybdenum from PCA steel in air have been derived.

Risk of lung cancer according to mild steel and stainless steel welding

DEFF Research Database (Denmark)

Sørensen, Anita Rath; Thulstrup, Ane Marie; Hansen, Johnni

2007-01-01

OBJECTIVES: Whether the elevated risk of lung cancer observed among welders is caused by welding emissions or by confounding from smoking or asbestos exposure is still not resolved. This question was addressed in a cohort with a long follow-up and quantified estimates of individual exposure.......06-1.70)]. Among the stainless steel welders, the risk increased significantly with increasing accumulative welding particulate exposure, while no exposure-response relation was found for mild steel welders, even after adjustment for tobacco smoking and asbestos exposure. CONCLUSIONS: The study corroborates...... earlier findings that welders have an increased risk of lung cancer. While exposure-response relations indicate carcinogenic effects related to stainless steel welding, it is still unresolved whether the mild steel welding process carries a carcinogenic risk....

Review on Cold-Formed Steel Connections

Science.gov (United States)

Tan, Cher Siang; Mohammad, Shahrin; Md Tahir, Mahmood; Shek, Poi Ngian

2014-01-01

The concept of cold-formed light steel framing construction has been widespread after understanding its structural characteristics with massive research works over the years. Connection serves as one of the important elements for light steel framing in order to achieve its structural stability. Compared to hot-rolled steel sections, cold-formed steel connections perform dissimilarity due to the thin-walled behaviour. This paper aims to review current researches on cold-formed steel connections, particularly for screw connections, storage rack connections, welded connections, and bolted connections. The performance of these connections in the design of cold-formed steel structures is discussed. PMID:24688448

Radiation embrittlement of WWER 440 pressure vessel steel and of some improved steels by western producers

International Nuclear Information System (INIS)

Koutsky, J.; Vacek, M.; Stoces, B.; Pav, T.; Otruba, J.; Novosad, P.; Brumovsky, M.

1982-01-01

The resistance was studied of Cr-Mo-V type steel 15Kh2MFA to radiation embrittlement at an irradiation temperature of around 288 degC. Studied was the steel used for the manufacture of the pressure vessel of the Paks nuclear reactor in Hungary. The obtained results of radiation embrittlement and hardening of steel 15Kh2MFA were compared with similar values of Mn-Ni-Mo type steels A 533-B and A 508 manufactured by leading western manufacturers within the international research programme coordinated by the IAEA. It was found that the resistance of steel 15Kh2MFA to radiation embrittlement is comparable with steels A 533-B and A 508 by western manufacturers. (author)

A comparison of the iraddiated tensile properties of a high-manganese austenitic steel and type 316 stainless steel

International Nuclear Information System (INIS)

Klueh, R.L.; Grossbeck, M.L.

1984-01-01

The USSR steel EP-838 is a high-manganese, low-nickel steel that also has lower chromium and molybdenum than type 316 stainless steel. Tensile specimens of 20%-cold-worked EP-838 and type 316 stainless steel were irradiated in the High Flux Isotope Reactor (HFIR) at the coolant temperature (approx.=50 0 C). A displacement damage level of 5.2 dpa was reached for the EP-838 and up to 9.5 dpa for the type 316 stainless steel. Tensile tests at room temperature and 300 0 C on the two steels indicated that the irradiation led to increased strength and decreased ductility compared to the unirradiated steels. Although the 0.2% yield stress of the type 316 stainless steel in the unirradiated condition was greater than that for the EP-838, after irradiation there was essentially no difference between the strength or ductility of the two steels. The results indicate that the replacement of the majority of the nickel by manganese and a reduction of chromium and molybdenum in an austenitic stainless steel of composition near that for type 316 stainless steel has little effect on the irradiated and unirradiated tensile properties at low temperatures. (orig.)

Ductility of high chromium stainless steels

International Nuclear Information System (INIS)

Peretyat'ko, V.N.; Kazantsev, A.A.

1997-01-01

Aimed to optimize the hot working conditions for high chromium stainless steels the experiments were carried in the temperature range of 800-1300 deg C using hot torsion tests and cylindrical specimens of ferritic and ferritic-martensitic steels 08Kh13, 12Kh13, 20Kh13, 30Kh13 and 40Kh13. Testing results showed that steel plasticity varies in a wide range depending on carbon content. Steels of lesser carbon concentration (08Kh13 and 12Kh13) exhibit a sharp increase in plasticity with a temperature rise, especially in the interval of 1200-1250 deg C. Steels 20Kh13 and 30Kh13 display insignificant plasticity increasing, whereas plastic properties of steel 40Kh13 increase noticeably in the range of 1000-1300 deg C. It is shown that optimal hot working conditions for specific steel must be selected with account of steel phase composition at high temperatures

Steels for nuclear power. I

International Nuclear Information System (INIS)

Bohusova, O.; Brumovsky, M.; Cukr, B.; Hatle, Z.; Protiva, K.; Stefec, R.; Urban, A.; Zidek, M.

1976-01-01

The principles are listed of nuclear reactor operation and the reactors are classified by neutron energy, fuel and moderator designs, purpose and type of moderator. The trend and the development of light-water reactor applications are described. The fundamental operating parameters of the WWER type reactors are indicated. The effect is discussed of neutron radiation on reactor structural materials. The characteristics are described of steel corrosion due to the contact of the steel with steam or sodium in the primary coolant circuit. The reasons for stress corrosion are given and the effects of radiation on corrosion are listed. The requirements and criteria are given for the choice of low-alloy steel for the manufacture of pressure vessels, volume compensators, steam generators, cooling conduits and containment. A survey is given of most frequently used steels for pressure vessels and of the mechanical and structural properties thereof. The basic requirements for the properties of steel used in the primary coolant circuit are as follows: sufficient strength in operating temperature, toughness, good weldability, resistance to corrosion and low brittleness following neutron irradiation. The materials are listed used for the components of light-water and breeder reactors. The production of corrosion-resistant steels is discussed with a view to raw materials, technology, steel-making processes, melting processes, induction furnace steel-making, and to selected special problems of the chemical composition of steels. The effects are mainly discussed of lead, bismuth and tin as well as of some other elements on hot working of high-alloy steels and on their structure. The problems of corrosion-resistant steel welding and of pressure vessel cladding are summed up. Also discussed is the question of the concept and safeguards of the safety of nuclear installation operation and a list is presented of most commonly used nondestructive materials testing methods. The current

The industrial ecology of steel

Energy Technology Data Exchange (ETDEWEB)

Considine, Timothy J.; Jablonowski, Christopher; Considine, Donita M.M.; Rao, Prasad G.

2001-03-26

This study performs an integrated assessment of new technology adoption in the steel industry. New coke, iron, and steel production technologies are discussed, and their economic and environmental characteristics are compared. Based upon detailed plant level data on cost and physical input-output relations by process, this study develops a simple mathematical optimization model of steel process choice. This model is then expanded to a life cycle context, accounting for environmental emissions generated during the production and transportation of energy and material inputs into steelmaking. This life-cycle optimization model provides a basis for evaluating the environmental impacts of existing and new iron and steel technologies. Five different plant configurations are examined, from conventional integrated steel production to completely scrap-based operations. Two cost criteria are used to evaluate technology choice: private and social cost, with the latter including the environmental damages associated with emissions. While scrap-based technologies clearly generate lower emissions in mass terms, their emissions of sulfur dioxide and nitrogen oxides are significantly higher. Using conventional damage cost estimates reported in the literature suggests that the social costs associated with scrap-based steel production are slightly higher than with integrated steel production. This suggests that adopting a life-cycle viewpoint can substantially affect environmental assessment of new technologies. Finally, this study also examines the impacts of carbon taxes on steel production costs and technology choice.

DETERMINANTS OF RETAINED EARNINGS IN PROFITABLE STEEL COMPANIES IN INDIA: A STUDY OF STEEL SECTOR

OpenAIRE

Dr. Sohaib Masood

2018-01-01

In this paper an attempt has been made to identify the important determinants of retained earnings in profitable steel companies in steel sector of India and which have impact on the retention of earnings of steel companies under study. Multiple linear regression is used to identify the determinants of retained earnings for a period of sixteen years. Also the importance of retained earnings as a source of finance for steel sector companies is also studied in the paper.

Advanced cold rolled steels for automotive applications

Energy Technology Data Exchange (ETDEWEB)

Hofmann, Harald; Mattissen, Dorothea; Schaumann, Thomas Wilhelm [ThyssenKrupp Steel AG, Center of Materials Excellence, Dortmund (Germany)

2009-01-15

Advanced high-strength steels offer a great potential for the further development of automobile bodies-in-white due to their combined mechanical properties of high formability and strength. They represent the first choice in material selection for strength and crash-relevant parts with challenging geometries. The intensive development of multiphase steels by ThyssenKrupp Steel has led to hot dip galvanizing concepts with an outstanding forming potential. Hot rolled, hot dip galvanized complex-phase steels are currently produced in addition to cold rolled dual phase (DP) and retained austenite (RA) or transformation induced plasticity (TRIP) steels. New continuously annealed grades of steel are being developed with tensile strength levels of up to 1000 MPa in combination with sufficient ductility for the high demands of structural automobile components. These steels make use of the classic advantages of microalloying as well as the principles of DP steels and RA / TRIP steels. Further improvement of properties will be reached by the new class of high manganese alloyed steels. (orig.)

Processing and refinement of steel microstructure images for assisting in computerized heat treatment of plain carbon steel

Science.gov (United States)

Gupta, Shubhank; Panda, Aditi; Naskar, Ruchira; Mishra, Dinesh Kumar; Pal, Snehanshu

2017-11-01

Steels are alloys of iron and carbon, widely used in construction and other applications. The evolution of steel microstructure through various heat treatment processes is an important factor in controlling properties and performance of steel. Extensive experimentations have been performed to enhance the properties of steel by customizing heat treatment processes. However, experimental analyses are always associated with high resource requirements in terms of cost and time. As an alternative solution, we propose an image processing-based technique for refinement of raw plain carbon steel microstructure images, into a digital form, usable in experiments related to heat treatment processes of steel in diverse applications. The proposed work follows the conventional steps practiced by materials engineers in manual refinement of steel images; and it appropriately utilizes basic image processing techniques (including filtering, segmentation, opening, and clustering) to automate the whole process. The proposed refinement of steel microstructure images is aimed to enable computer-aided simulations of heat treatment of plain carbon steel, in a timely and cost-efficient manner; hence it is beneficial for the materials and metallurgy industry. Our experimental results prove the efficiency and effectiveness of the proposed technique.

Laser cutting of thick steel plates and simulated steel components using a 30 kW fiber laser

International Nuclear Information System (INIS)

Tamura, Koji; Ishigami, Ryoya; Yamagishi, Ryuichiro

2016-01-01

Laser cutting of thick steel plates and simulated steel components using a 30 kW fiber laser was studied for application to nuclear decommissioning. Successful cutting of carbon steel and stainless steel plates up to 300 mm in thickness was demonstrated, as was that of thick steel components such as simulated reactor vessel walls, a large pipe, and a gate valve. The results indicate that laser cutting applied to nuclear decommissioning is a promising technology. (author)

Electrochemical Corrosion Behavior of Carbon Steel and Hot Dip Galvanized Steel in Simulated Concrete Solution with Different pH Values

Directory of Open Access Journals (Sweden)

Wanchen XIE

2017-08-01

Full Text Available Hot dip galvanizing technology is now widely used as a method of protection for steel rebars. The corrosion behaviors of Q235 carbon steel and hot galvanized steel in a Ca(OH2 solution with a pH from 10 to 13 was investigated by electrode potential and polarization curves testing. The results indicated that carbon steel and hot galvanized steel were all passivated in a strong alkaline solution. The electrode potential of hot dip galvanized steel was lower than that of carbon steel; thus, hot dip galvanized steel can provide very good anodic protection for carbon steel. However, when the pH value reached 12.5, a polarity reversal occurred under the condition of a certain potential. Hot dip galvanized coating became a cathode, and the corrosion of carbon steel accelerated. The electrochemical behaviors and passivation abilities of hot dip galvanized steel and carbon steel were affected by pH. The higher the pH value was, the more easily they were passivated.DOI: http://dx.doi.org/10.5755/j01.ms.23.3.16675

Effect of Different Chromium Additions on the Microstructure and Mechanical Properties of Multipass Weld Joint of Duplex Stainless Steel

Science.gov (United States)

Kang, Dong Hoon; Lee, Hae Woo

2012-12-01

The correlation between the mechanical properties and ferrite volume fraction (approximately 40, 50, and 60 Ferrite Number [FN]) in duplex stainless steel weld metals were investigated by changing the Cr content in filler wires with a flux-cored arc-welding (FCAW) process. The interpass temperature was thoroughly maintained under a maximum of 423 K (150 °C), and the heat input was also sustained at a level under 15 KJ/cm in order to minimize defects. The microstructure examination demonstrated that the δ-ferrite volume fraction in the deposited metals increased as the Cr/Ni equivalent ratio increased, and consequently, chromium nitride (Cr2N) precipitation was prone to occur in the ferrite domains due to low solubility of nitrogen in this phase. Thus, more dislocations are pinned by the precipitates, thereby lowering the mobility of the dislocations. Not only can this lead to the strength improvement, but also it can accentuate embrittlement of the weld metal at subzero temperature. Additionally, the solid-solution strengthening by an increase of Cr and Mo content in austenite phase depending on the reduction of austenite proportion also made an impact on the increase of the tensile and yield strength. On the other hand, the impact test (at 293 K, 223 K, and 173 K [20 °C, -50 °C, and -100 °C]) showed that the specimen containing about 40 to 50 FN had the best result. The absorbed energy of about 40 to 50 J sufficiently satisfied the requirements for industrial applications at 223 K (-50 °C), while the ductile-to-brittle transition behavior exhibited in weldment containing 60 FN. As the test temperature decreased under 223 K (-50 °C), a narrow and deep dimple was transformed into a wide and shallow dimple, and a significant portion of the fracture surface was occupied by a flat cleavage facet with river patterns.

Steel alloys

International Nuclear Information System (INIS)

Bloom, E.E.; Stiegler, J.O.; Rowcliffe, A.F.; Leitnaker, J.M.

1977-01-01

The invention deals with a fuel element for fast breeder reactors. It consits essentially of a uranium oxide, nitride, or carbide or a mixture of these fuels with a plutonium or thorium oxide, nitride, or carbide. The fuel elements are coated with an austenitic stainless steel alloy. Inside the fuel elements, vacancies or small cavities are produced by neutron effects which causes the steel coating to swell. According to the invention, swelling is prevented by a modification of type 304, 316, 321, or 12 K 72HV commercial steels. They consist mainly of Fe, Cr, and Ni in a ratio determined by a temary diagram. They may also contain 1.8 to 2.3% by weight of Mo and a fraction of Si (0.7 to 2% by weight) and Ti(0.10 to 0.5% by weight) to prevent cavity formation. They are structurally modified by cold working. (IHOE) [de

Clean steels for fusion

International Nuclear Information System (INIS)

Gelles, D.S.

1995-03-01

Fusion energy production has an inherent advantage over fission: a fuel supply with reduced long term radioactivity. One of the leading candidate materials for structural applications in a fusion reactor is a tungsten stabilized 9% chromium Martensitic steel. This alloy class is being considered because it offers the opportunity to maintain that advantage in the reactor structure as well as provide good high temperature strength and radiation induced swelling and embrittlement resistance. However, calculations indicate that to obtain acceptable radioactivity levels within 500 years after service, clean steel will be required because the niobium impurity levels must be kept below about 2 appm and nickel, molybdenum, nitrogen, copper, and aluminum must be intentionally restricted. International efforts are addressing the problems of clean steel production. Recently, a 5,000 kg heat was vacuum induction melted in Japan using high purity commercial raw materials giving niobium levels less than 0.7 appm. This paper reviews the need for reduced long term radioactivity, defines the advantageous properties of the tungsten stabilized Martensitic steel class, and describes the international efforts to produce acceptable clean steels

Thermal stability of manganese-stabilized stainless steels

International Nuclear Information System (INIS)

Klueh, R.L.; Kenik, E.A.

1993-01-01

Previous work on a series of experimental high-manganese reduced-activation austenitic stainless steels demonstrated that they have improved tensile properties relative to type 316 stainless steel in both the annealed and 20% cold-worked conditions. Steels were tested with an Fe-20Mn-12Cr-0.25C (in weight percent) base composition, to which various combinations of Ti, W, V, P, and B were added. Tensile tests have now been completed on these steels after thermal aging at 600 degrees C. Thermal stability varied with composition, but the alloys were as stable or more stable than type 316 stainless steel. the strength of the annealed steels increased slightly after aging to 5000 h, while a strength decrease occurred for the cold worked steel. In both conditions, a steel containing a combination of all the alloying elements was most stable and had the best strength after thermal aging 5000 h at 600 degrees C. Despite having much higher strength than 316 stainless steel after aging, the ductility of the strongest experimental alloy was still as good as that of 316 stainless steel

Sliding wear characteristics of carburized steels and thermally refined steels implanted with nitrogen ions

International Nuclear Information System (INIS)

Terashima, Keiichi; Koda, Hiroyuki; Takeuchi, Eiichi.

1995-01-01

In order to concretely examine the application of surface reforming by ion implantation, nitrogen ion implantation was applied to the thermally refined steels S45C and SCM440 and the carburized steel SCM415, which are high versatile steels for mechanical structures, and their friction and wear characteristics were examined. The results are summarized as follows. In the surface-reformed material, in which nitrogen was implanted for the purpose of improving the seizure durability of the carburized steel, the load-frictional coefficient curve in lubricated sliding friction was similar to that of the material without implantation, but it was recognized that the load at which seizure occurred reached 2000 kgf or more, and as the amount of implantation was more, the material withstood higher load. In the lubricated sliding friction using a pin-ring type wear testing machine of the thermally refined steels and those to which implantation was applied, it was recognized that the specific wear amount was less in the implanted steels than in those without implantation. The results of the analysis of the implanted surface layers and the friction surfaces are reported. (K.I.)

Larson-Miller Constant of Heat-Resistant Steel

Science.gov (United States)

Tamura, Manabu; Abe, Fujio; Shiba, Kiyoyuki; Sakasegawa, Hideo; Tanigawa, Hiroyasu

2013-06-01

Long-term rupture data for 79 types of heat-resistant steels including carbon steel, low-alloy steel, high-alloy steel, austenitic stainless steel, and superalloy were analyzed, and a constant for the Larson-Miller (LM) parameter was obtained in the current study for each material. The calculated LM constant, C, is approximately 20 for heat-resistant steels and alloys except for high-alloy martensitic steels with high creep resistance, for which C ≈ 30 . The apparent activation energy was also calculated, and the LM constant was found to be proportional to the apparent activation energy with a high correlation coefficient, which suggests that the LM constant is a material constant possessing intrinsic physical meaning. The contribution of the entropy change to the LM constant is not small, especially for several martensitic steels with large values of C. Deformation of such martensitic steels should accompany a large entropy change of 10 times the gas constant at least, besides the entropy change due to self-diffusion.

Properties of hot rolled steels for enamelling

International Nuclear Information System (INIS)

Gavrilovski, Dragica; Gavrilovski, Milorad

2003-01-01

The results of an investigation of the structure and properties of experimental produced hot rolled steels suitable for enamelling are presented in the paper. Hot rolled steels for enamelling represent a special group of the steels for conventional enamelling. Their quality has to be adapted to the method and conditions of enamelling. Therefore, these steels should meet some specific requirements. In addition to usual investigation of the chemical composition and mechanical properties, microstructure and quality of the steel surface also were investigated. The basic aim was to examine steels capability for enamelling, i. e. steels resistance to the fish scales phenomena, by trial enamelling, as well as quality of the steel - enamel contact surface, to evaluate the binding. Also, the changes of the mechanical properties, especially the yield point, during thermal treatment, as a very specific requirement, were investigated, by simplified method. Good results were obtained confirming the steels capability for enamelling. (Original)

Reduced-activation steels: present status and future development

International Nuclear Information System (INIS)

Klueh, R.L.

2007-01-01

Full text of publication follows: Reduced-activation steels for fusion reactor applications were developed in the 1980's to replace the commercial elevated- temperature steels first considered. In the United States, this involved replacing Sandvik HT9 and modified 9Cr-1Mo steels. Reduced-activation steels, which were developed for more rapid radioactivity decay following exposure in a fusion neutron environment, were patterned after the commercial steels they were to replace. The objective for the reduced-activation steels was that they have strengths (yield stress and ultimate tensile strength from room temperature to 600 deg. C) and impact toughness (measured in a Charpy test) comparable to or better than the steels they were replacing. That objective was achieved in reduced-activation steels developed in Japan, Europe, and the United States. Since the reduced-activation steels were developed in the 1980's, reactor designers have been interested designs for increased efficiency of future fusion plants. This means reactors will need to operate at higher temperatures-above 550 deg. C, which is the upper-temperature limit for the reduced-activation steels. Although the tensile and impact toughness of the reduced-activation steels exceed those of the commercial steels they were patterned after, their creep-rupture properties are inferior to some of the commercial steels they replaced. furthermore, they are much inferior to commercial steels that have been developed since the 1980's. Reasons for why the creep-rupture properties for the new commercial ferritic/martensitic steels are superior to the earlier commercial steels and the reduced-activation steels were examined. The reasons involve compositional changes that were made in the earlier commercial steels to give the new commercial steels their superior properties. Computational thermodynamics calculations were carried out to compare the expected equilibrium phases. It appears that similar changes in composition

In situ 3D monitoring of corrosion on carbon steel and ferritic stainless steel embedded in cement paste

KAUST Repository

Itty, Pierre-Adrien

2014-06-01

In a X-ray microcomputed tomography study, active corrosion was induced by galvanostatically corroding steel embedded in cement paste. The results give insight into corrosion product build up, crack formation, leaching of products into the cracks and voids, and differences in morphology of corrosion attack in the case of carbon steel or stainless steel reinforcement. Carbon steel was homogeneously etched away with a homogeneous layer of corrosion products forming at the steel/cement paste interface. For ferritic stainless steel, pits were forming, concentrating the corrosion products locally, which led to more extensive damage on the cement paste cover. © 2014 Elsevier Ltd.

In situ 3D monitoring of corrosion on carbon steel and ferritic stainless steel embedded in cement paste

KAUST Repository

Itty, Pierre-Adrien; Serdar, Marijana; Meral, Cagla; Parkinson, Dula; MacDowell, Alastair A.; Bjegović, Dubravka; Monteiro, Paulo J.M.

2014-01-01

In a X-ray microcomputed tomography study, active corrosion was induced by galvanostatically corroding steel embedded in cement paste. The results give insight into corrosion product build up, crack formation, leaching of products into the cracks and voids, and differences in morphology of corrosion attack in the case of carbon steel or stainless steel reinforcement. Carbon steel was homogeneously etched away with a homogeneous layer of corrosion products forming at the steel/cement paste interface. For ferritic stainless steel, pits were forming, concentrating the corrosion products locally, which led to more extensive damage on the cement paste cover. © 2014 Elsevier Ltd.

Scientific and Technological Principles of Development of New Cold-Resistant Arc-Steels (Steels for Arctic Applications)

Science.gov (United States)

Sych, O. V.; Khlusova, E. I.; Yashin, E. A.

2017-12-01

The paper presents the results of quantitative analysis of C, Mn, Ni and Cu content on strength and cold-resistance of rolled plates. Relations between the ferritic-bainitic structure morphology and anisotropy and steel performance characteristics have been established. Influence of thermal and deformation rolling patterns on steel structure has been studied. The steel chemical composition has been improved and precision thermomechanical processing conditions for production of cold-resistant Arc-steel plates have been developed.

Irradiation embrittlement of pressure vessel steels

International Nuclear Information System (INIS)

Brumovsky, M.; Vacek, M.

1975-01-01

A Standard Research Programme on Irradiation Embrittlement of Pressure Vessel Steels was approved by the Coordinating Meeting on the 12th May 1972 at the Working Group on Engineering Aspects of Irradiation Embrittlement of Pressure Vessel Steels. This Working Group was set up by the International Atomic Energy Agency in Vienna. Seven countries with their research institutes agreed on doing irradiation experiments according to the approved programme on steel A533 B from the U.S. HSST Programme. The Czechoslovak contribution covering tensile and impact testing of non-irradiated steel and steel irradiated at 280degC to 1.3 x 10 23 n/m 2 (E above 1 MeV) is presented in this report. As an additional part the same set of experiments was carried out on two additional steels - A 542 and A 543, made in SKODA Works for comparison of their irradiation embrittlement and hardening with A533 B steel. (author)

Heat treatments in a conventional steel to reproduce the microstructure of a nuclear grade steel

International Nuclear Information System (INIS)

Rosalio G, M.

2014-01-01

The ferritic steels used in the manufacture of pressurized vessels of Boiling Water Reactors (BWR) suffer degradation in their mechanical properties due to damage caused by the neutron fluxes of high energy bigger to a Mega electron volt (E> 1 MeV) generated in the reactor core. The materials with which the pressurized vessels of nuclear reactors cooled by light water are built correspond to low alloy ferritic steels. The effect of neutron irradiation on these steels is manifested as an increase in hardness, mechanical strength, with the consequent decrease in ductility, fracture toughness and an increase in temperature of ductile-brittle transition. The life of a BWR is 40 years, its design must be considered sufficient margin of safety because pressure forces experienced during operation, maintenance and testing of postulated accident conditions. It is necessary that under these conditions the vessel to behave ductile and likely to propagate a fracture is minimized. The vessels of light water nuclear reactors have a bainite microstructure. Specifically, the reactor vessels of the nuclear power plant of Laguna Verde (Veracruz, Mexico) are made of a steel Astm A-533, Grade B Class 1. At present they are carrying out some welding tests for the construction of a model of a BWR, however, to use nuclear grade steel such as Astm A-533 to carry out some of the welding tests, is very expensive; perform these in a conventional material provides basic information. Although the microstructure present in the conventional material does not correspond exactly to the degree of nuclear material, it can take of reference. Therefore, it is proposed to conduct a pilot study to establish the thermal treatment that reproduces the microstructure of nuclear grade steel, in conventional steel. The resulting properties of the conventional steel samples will be compared to a JRQ steel, that is a steel Astm A-533, Grade B Class 1, provided by IAEA. (Author)

Controlling DC permeability in cast steels

Energy Technology Data Exchange (ETDEWEB)

Sumner, Aaran, E-mail: aaran.sumner@nottingham.ac.uk [University of Nottingham, Nottingham University Park Campus, Nottingham NG7 2RD, England (United Kingdom); Gerada, Chris, E-mail: chris.gerada@nottingham.ac.uk [Electrical Machines, University of Nottingham, Tower Building, Nottingham NG7 2RD, England (United Kingdom); Brown, Neil, E-mail: neil.brown@cummins.com [Advanced Electrical Machines Research and Technology at Cummins Power Generation, Peterborough PE2 6FZ, England (United Kingdom); Clare, Adam, E-mail: adam.clare@nottingham.ac.uk [Advanced Manufacturing, University of Nottingham, University Park Campus, Nottingham NG7 2RD, England (United Kingdom)

2017-05-01

Annealing (at multiple cooling rates) and quenching (with tempering) was performed on specimens of cast steel of varying composition. The aim was to devise a method for selecting the steel with the highest permeability, from any given range of steels, and then increasing the permeability by heat treatment. Metallographic samples were imaged using optical microscopy to show the effect of the applied heat treatments on the microstructure. Commonly cast steels can have DC permeability altered by the careful selection of a heat treatment. Increases of up to 381% were achieved by annealing using a cooling rate of 6.0 °C/min. Annealing was found to cause the carbon present in the steel to migrate from grain boundaries and from within ferrite crystals into adjacent pearlite crystals. The migration of the carbon resulted in less carbon at grain boundaries and within ferrite crystals reducing the number of pinning sites between magnetic domains. This gives rise to a higher permeability. Quenching then tempering was found to cause the formation of small ferrite crystals with the carbon content of the steel predominately held in the martensitic crystal structures. The results show that with any given range of steel compositions the highest baseline DC permeability will be found with the steel that has the highest iron content and the lowest carbon content. For the samples tested in this paper a cooling rate of 4.5 °C/min resulted in the relative permeability of the sample with the highest baseline permeability, AS4, increasing from 783 to 1479 at 0.5 T. This paper shows how heat treatments commonly applied to hypoeutectoid cast steels, to improve their mechanical performance, can be used to also enhance electromagnetic properties of these alloys. The use of cast steels allows the creation of DC components for electrical machines not possible by the widely used method of stacking of electrical grade sheet steels. - Highlights: • A range of structural steels had their

Controlling DC permeability in cast steels

International Nuclear Information System (INIS)

Sumner, Aaran; Gerada, Chris; Brown, Neil; Clare, Adam

2017-01-01

Annealing (at multiple cooling rates) and quenching (with tempering) was performed on specimens of cast steel of varying composition. The aim was to devise a method for selecting the steel with the highest permeability, from any given range of steels, and then increasing the permeability by heat treatment. Metallographic samples were imaged using optical microscopy to show the effect of the applied heat treatments on the microstructure. Commonly cast steels can have DC permeability altered by the careful selection of a heat treatment. Increases of up to 381% were achieved by annealing using a cooling rate of 6.0 °C/min. Annealing was found to cause the carbon present in the steel to migrate from grain boundaries and from within ferrite crystals into adjacent pearlite crystals. The migration of the carbon resulted in less carbon at grain boundaries and within ferrite crystals reducing the number of pinning sites between magnetic domains. This gives rise to a higher permeability. Quenching then tempering was found to cause the formation of small ferrite crystals with the carbon content of the steel predominately held in the martensitic crystal structures. The results show that with any given range of steel compositions the highest baseline DC permeability will be found with the steel that has the highest iron content and the lowest carbon content. For the samples tested in this paper a cooling rate of 4.5 °C/min resulted in the relative permeability of the sample with the highest baseline permeability, AS4, increasing from 783 to 1479 at 0.5 T. This paper shows how heat treatments commonly applied to hypoeutectoid cast steels, to improve their mechanical performance, can be used to also enhance electromagnetic properties of these alloys. The use of cast steels allows the creation of DC components for electrical machines not possible by the widely used method of stacking of electrical grade sheet steels. - Highlights: • A range of structural steels had their

STEFINS: a steel freezing integral simulation program

International Nuclear Information System (INIS)

Frank, M.V.

1980-09-01

STEFINS (STEel Freezing INtegral Simulation) is a computer program for the calculation of the rate of solidification of molten steel on solid steel. Such computations arize when investigating core melt accidents in fast reactors. In principle this problem involves a coupled two-dimensional thermal and hydraulic approach. However, by physically reasonable assumptions a decoupled approach has been developed. The transient solidification of molten steel on a cold wall is solved in the direction normal to the molten steel flow and independent from the solution for the molten steel temperature and Nusselt number along the direction of flow. The solutions to the applicable energy equations have been programmed in cylindrical and slab geometries. Internal gamma heating of steel is included

Nitrogen-containing steels and thermomechanical treatment

International Nuclear Information System (INIS)

Kaputkina, L.; Prokoshkina, V.G.; Svyazhin, G.

2004-01-01

The strengthening of nitrogen-containing corrosion-resistant steels resulting from alloying and thermomechanical treatment have been investigated using X-ray diffraction analysis, light microscopy, hardness measurements and tensile testing. Combined data have been obtained for nitrogen interaction with alloying elements , peculiarities of deformed structure and short-range of nitrogen-containing steels of various structural classes. The higher nitrogen and total alloying element contents, the higher deformation strengthening. Prospects of use the steels with not high nitrogen content and methods of their thermomechanical strengthening are shown. High temperature thermomechanical treatment (HTMT) is very effective for obtaining high and thermally stable constructional strength of nitrogen-containing steels of all classes. The HTMT is most effective if used in a combination with dispersion hardening for aging steels or in the case of mechanically unstable austenitic steels. (author)

Automated Steel Cleanliness Analysis Tool (ASCAT)

Energy Technology Data Exchange (ETDEWEB)

Gary Casuccio (RJ Lee Group); Michael Potter (RJ Lee Group); Fred Schwerer (RJ Lee Group); Dr. Richard J. Fruehan (Carnegie Mellon University); Dr. Scott Story (US Steel)

2005-12-30

The objective of this study was to develop the Automated Steel Cleanliness Analysis Tool (ASCATTM) to permit steelmakers to evaluate the quality of the steel through the analysis of individual inclusions. By characterizing individual inclusions, determinations can be made as to the cleanliness of the steel. Understanding the complicating effects of inclusions in the steelmaking process and on the resulting properties of steel allows the steel producer to increase throughput, better control the process, reduce remelts, and improve the quality of the product. The ASCAT (Figure 1) is a steel-smart inclusion analysis tool developed around a customized next-generation computer controlled scanning electron microscopy (NG-CCSEM) hardware platform that permits acquisition of inclusion size and composition data at a rate never before possible in SEM-based instruments. With built-in customized ''intelligent'' software, the inclusion data is automatically sorted into clusters representing different inclusion types to define the characteristics of a particular heat (Figure 2). The ASCAT represents an innovative new tool for the collection of statistically meaningful data on inclusions, and provides a means of understanding the complicated effects of inclusions in the steel making process and on the resulting properties of steel. Research conducted by RJLG with AISI (American Iron and Steel Institute) and SMA (Steel Manufactures of America) members indicates that the ASCAT has application in high-grade bar, sheet, plate, tin products, pipes, SBQ, tire cord, welding rod, and specialty steels and alloys where control of inclusions, whether natural or engineered, are crucial to their specification for a given end-use. Example applications include castability of calcium treated steel; interstitial free (IF) degasser grade slag conditioning practice; tundish clogging and erosion minimization; degasser circulation and optimization; quality assessment/steel

Automated Steel Cleanliness Analysis Tool (ASCAT)

International Nuclear Information System (INIS)

Gary Casuccio; Michael Potter; Fred Schwerer; Richard J. Fruehan; Dr. Scott Story

2005-01-01

The objective of this study was to develop the Automated Steel Cleanliness Analysis Tool (ASCATTM) to permit steelmakers to evaluate the quality of the steel through the analysis of individual inclusions. By characterizing individual inclusions, determinations can be made as to the cleanliness of the steel. Understanding the complicating effects of inclusions in the steelmaking process and on the resulting properties of steel allows the steel producer to increase throughput, better control the process, reduce remelts, and improve the quality of the product. The ASCAT (Figure 1) is a steel-smart inclusion analysis tool developed around a customized next-generation computer controlled scanning electron microscopy (NG-CCSEM) hardware platform that permits acquisition of inclusion size and composition data at a rate never before possible in SEM-based instruments. With built-in customized ''intelligent'' software, the inclusion data is automatically sorted into clusters representing different inclusion types to define the characteristics of a particular heat (Figure 2). The ASCAT represents an innovative new tool for the collection of statistically meaningful data on inclusions, and provides a means of understanding the complicated effects of inclusions in the steel making process and on the resulting properties of steel. Research conducted by RJLG with AISI (American Iron and Steel Institute) and SMA (Steel Manufactures of America) members indicates that the ASCAT has application in high-grade bar, sheet, plate, tin products, pipes, SBQ, tire cord, welding rod, and specialty steels and alloys where control of inclusions, whether natural or engineered, are crucial to their specification for a given end-use. Example applications include castability of calcium treated steel; interstitial free (IF) degasser grade slag conditioning practice; tundish clogging and erosion minimization; degasser circulation and optimization; quality assessment/steel cleanliness; slab, billet

Corrosion of carbon steel and low-alloy steel in diluted seawater containing hydrazine under gamma-rays irradiation

International Nuclear Information System (INIS)

Nakano, Junichi; Yamamoto, Masahiro; Tsukada, Takashi

2014-01-01

Seawater was injected into reactor cores of Units 1, 2, and 3 in the Fukushima Daiichi nuclear power station as an urgent coolant. It is considered that the injected seawater causes corrosion of steels of the reactor pressure vessel and primary containment vessel. To investigate the effects of gamma-rays irradiation on weight loss in carbon steel and low-alloy steel, corrosion tests were performed in diluted seawater at 50°C under gamma-rays irradiation. Specimens were irradiated with dose rates of 4.4 kGy/h and 0.2 kGy/h. To evaluate the effects of hydrazine (N 2 H 4 ) on the reduction of oxygen and hydrogen peroxide, N 2 H 4 was added to the diluted seawater. In the diluted seawater without N 2 H 4 , weight loss in the steels irradiated with 0.2 kGy/h was similar to that in the unirradiated steels, and weight loss in the steels irradiated with 4.4 kGy/h increased to approximate 1.7 times of those in the unirradiated steels. Weight loss in the steels irradiated in the diluted seawater containing N 2 H 4 was similar to that in the diluted seawater without N 2 H 4 . When N 2 was introduced into the gas phase in the flasks during gamma-rays irradiation, weight loss in the steels decreased. (author)

Study on cementitious properties of steel slag

Directory of Open Access Journals (Sweden)

Zhu G.

2013-01-01

Full Text Available The converter steel slag chemical and mineral components in China’s main steel plants have been analysed in the present paper. The electronic microscope, energy spectrum analysis, X-ray diffraction analysis confirmed the main mineral compositions in the converter slag. Converter slag of different components were grounded to obtain a powder with specific surface area over 400m2/kg, making them to take place some part of the cement in the concrete as the admixture and carry out the standard tests. The results indicate that the converter slag can be used as cementitious materials for construction. Furthermore, physical mechanic and durability tests on the concrete that certain amount of cement be substituted by converter steel slag powder from different steel plants are carried out, the results show that the concrete with partial substitution of steel slag powder has the advantages of higher later period strength, better frost resistance, good wear resistance and lower hydration heat, etc. This study can be used as the technical basis for “Steel Slag Powder Used For Cement And Concrete”, “Steel Slag Portland Cement”, “Low Heat Portland Steel Slag Cement”, “Steel Slag Road Cement” in China, as well as a driving force to the works of steel slag utilization with high-value addition, circular economy, energy conservation and discharge reduction in the iron and steel industry.

Modern steels for light automobiles (review)

Science.gov (United States)

Tikhonov, A. K.

1994-10-01

The article considers the directions of work at VAZ together with metallurgists of the CIS for creating highly efficient economically-alloyed and microalloyed steels; highly ductile forged steels with improved corrosion resistance coated with zinc and with good stamping, welding, and painting capacity. Steels are created for petrol tanks with aluminum-zinc coatings instead of lead, and new heat and corrosion-resistant steels are developed for automobile exhaust gas systems.

Inclusion control in high-performance steels

International Nuclear Information System (INIS)

Holappa, L.E.K.; Helle, A.S.

1995-01-01

Progress of clean steel production, fundamentals of oxide and sulphide inclusions as well as inclusion morphology in normal and calcium treated steels are described. Effects of cleanliness and inclusion control on steel properties are discussed. In many damaging constructional and engineering applications the nonmetallic inclusions have a quite decisive role in steel performance. An example of combination of good mechanical properties and superior machinability by applying inclusion control is presented. (author)

Steel fiber reinforced concrete

International Nuclear Information System (INIS)

Baloch, S.U.

2005-01-01

Steel-Fiber Reinforced Concrete is constructed by adding short fibers of small cross-sectional size .to the fresh concrete. These fibers reinforce the concrete in all directions, as they are randomly oriented. The improved mechanical properties of concrete include ductility, impact-resistance, compressive, tensile and flexural strength and abrasion-resistance. These uniqlte properties of the fiber- reinforcement can be exploited to great advantage in concrete structural members containing both conventional bar-reinforcement and steel fibers. The improvements in mechanical properties of cementitious materials resulting from steel-fiber reinforcement depend on the type, geometry, volume fraction and material-properties of fibers, the matrix mix proportions and the fiber-matrix interfacial bond characteristics. Effects of steel fibers on the mechanical properties of concrete have been investigated in this paper through a comprehensive testing-programme, by varying the fiber volume fraction and the aspect-ratio (Lid) of fibers. Significant improvements are observed in compressive, tensile, flexural strength and impact-resistance of concrete, accompanied by marked improvement in ductility. optimum fiber-volume fraction and aspect-ratio of steel fibers is identified. Test results are analyzed in details and relevant conclusions drawn. The research is finally concluded with future research needs. (author)

Development of nuclear grade stainless steels at KCSSL

International Nuclear Information System (INIS)

Balachandran, G.; Dhere, M.; Mahadik, A.; Hinge, N.M.; Balasubramanian, V.

2011-01-01

Kalyani Carpenter Special Steels Ltd is an alloy steel plant, where a variety of alloy steel grades are produced for automotive, defence, nuclear and aerospace applications. The plant has developed expertise in processing of several alloy steel grades of superior quality that meets stringent specifications. Primary steel is processed through a combination of electric arc furnace, ladle furnace and vacuum degassing where stringent control over dephosphorisation, desulphurization, deoxidation is effected to get a refined high quality steel. The molten steel is cast through continuous casting of slabs or ingot casting. In grades specific to nuclear application, the primary cast products are further subjected to electroslag remelting to achieve further freedom from inclusions and to achieve a favourable solidification grain structure, which ultimately improve the hot workability of the alloy steel. Appropriate choice of slag and operating parameters are needed for realising the required ingot quality. The present study would examine the processing and quality aspects of some important grades of steels used in nuclear industry namely ferritic 9Cr-1Mo steel, martensitic stainless steels 403, 410, precipitation hardenable 17-4 PH stainless steel and austenitic 321, 316LN stainless steel, which were made and supplied for applications to Indian nuclear industry. The expertise developed in processing the steels in terms of melting, heat treatment and their relationship to structural features and mechanical properties would be highlighted. (author)

Fatigue behaviour of friction welded medium carbon steel and austenitic stainless steel dissimilar joints

International Nuclear Information System (INIS)

Paventhan, R.; Lakshminarayanan, P.R.; Balasubramanian, V.

2011-01-01

Research highlights: → Fusion welding of dissimilar metals is a problem due to difference in properties. → Solid state welding process such as friction welding is a solution for the above problem. → Fatigue life of friction welded carbon steel and stainless steel joints are evaluated. → Effect of notch on the fatigue life of friction welded dissimilar joints is reported. → Formation of intermetallic is responsible for reduction in fatigue life of dissimilar joints. -- Abstract: This paper reports the fatigue behaviour of friction welded medium carbon steel-austenitic stainless steel (MCS-ASS) dissimilar joints. Commercial grade medium carbon steel rods of 12 mm diameter and AISI 304 grade austenitic stainless steel rods of 12 mm diameter were used to fabricate the joints. A constant speed, continuous drive friction welding machine was used to fabricate the joints. Fatigue life of the joints was evaluated conducting the experiments using rotary bending fatigue testing machine (R = -1). Applied stress vs. number of cycles to failure (S-N) curve was plotted for unnotched and notched specimens. Basquin constants, fatigue strength, fatigue notch factor and notch sensitivity factor were evaluated for the dissimilar joints. Fatigue strength of the joints is correlated with microstructure, microhardness and tensile properties of the joints.

Life after Steel

Science.gov (United States)

Mangan, Katherine

2013-01-01

Bobby Curran grew up in a working-class neighborhood in Baltimore, finished high school, and followed his grandfather's steel-toed bootprints straight to Sparrows Point, a 3,000-acre sprawl of industry on the Chesapeake Bay. College was not part of the plan. A gritty but well-paying job at the RG Steel plant was Mr. Curran's ticket to a secure…

Development of new high-performance stainless steels

International Nuclear Information System (INIS)

Park, Yong Soo

2002-01-01

This paper focused on high-performance stainless steels and their development status. Effect of nitrogen addition on super-stainless steel was discussed. Research activities at Yonsei University, on austenitic and martensitic high-performance stainless, steels, and the next-generation duplex stainless steels were introduced

Ferritic/martensitic steels: Promises and problems

International Nuclear Information System (INIS)

Klueh, R.L.; Ehrlich, K.; Abe, F.

1992-01-01

Ferritic/martensitic steels are candidate structural materials for fusion reactors because of their higher swelling resistance, higher thermal conductivity, lower thermal expansion, and better liquid-metal compatibility than austenitic steels. Irradiation effects will ultimately determine the applicability of these steels, and the effects of irradiation on microstructure and swelling, and on the tensile, fatigue, and impact properties of the ferritic/martensitic steels are discussed. Most irradiation studies have been carried out in fast reactors, where little transmutation helium forms. Helium has been shown to enhance swelling and affect tensile and fracture behavior, making helium a critical issue, since high helium concentrations will be generated in conjunction with displacement damage in a fusion reactor. These issues are reviewed to evaluate the status of ferritic/martensitic steels and to assess the research required to insure that such steels are viable candidates for fusion applications

Evaluation criteria of structural steel reliability

International Nuclear Information System (INIS)

Zav'yalov, A.S.

1980-01-01

Different low-carbon and medium-carbon structural steels are investigated. It is stated that steel reliability evaluation criteria depend on the fracture mode, steel suffering from the brittle fracture under the influence of the stresses (despite their great variety) arising in articles during the production and operation. Fibrous steel fracture at the given temperature and article thickness says about its high ductility and toughness and brittle fractures are impossible. Brittle fractures take place in case of a crystalline and mixed fracture with a predominant crystalline component. Evaluation methods of article and sample steel structural strength differing greatly from real articles in a thickness (diameter) or used at temperatures higher than possible operation temperatures cannot be reliability evaluation criteria because at a great thickness (diameter) and lower operation temperatures steel fracture and its strain mode can change resulting in a sharp reliability degradation

Development of PWR pressure vessel steels

International Nuclear Information System (INIS)

Druce, S.; Edwards, B.

1982-01-01

Requirements to be met by vessel steels for pressurized water reactors are analyzed. Chemicat composition of low-alloyed steels, mechanical properties of sheets and forgings made of these steels and changes in the composition and properties over the wall thickness of the reactor vessel are presented. Problems of the vessel manufacturing including welding and heat treatment processes of sheets and forgings are considered. Special attention is paid to steel embrittlement during vessel fabrication and operation (radiation embrittlement, thermal embrittlement). The role of non-metal inclusions and their effect on anisotropy of fracture toughness is discussed. Possible developments of vessel steels and procedures for producing reactor vessels are reviewed

Development of PWR pressure vessel steels

Energy Technology Data Exchange (ETDEWEB)

Druce, S.; Edwards, B.

1982-01-01

Requirements to be met by vessel steels for pressurized water reactors are analyzed. Chemicat composition of low-alloyed steels, mechanical properties of sheets and forgings made of these steels and changes in the composition and properties over the wall thickness of the reactor vessel are presented. Problems of the vessel manufacturing including welding and heat treatment processes of sheets and forgings are considered. Special attention is paid to steel embrittlement during vessel fabrication and operation (radiation embrittlement, thermal embrittlement). The role of non-metal inclusions and their effect on anisotropy of fracture toughness is discussed. Possible developments of vessel steels and procedures for producing reactor vessels are reviewed.

Influence of steel-making process and heat-treatment temperature on the fatigue and fracture properties of pressure vessel steels

International Nuclear Information System (INIS)

Koh, S. K.; Na, E. G.; Baek, T. H.; Won, S. Y.; Park, S. J.; Lee, S. W.

2001-01-01

In this paper, high strength pressure vessel steels having the same chemical compositions were manufactured by the two different steel-making processes, such as Vacuum Degassing(VD) and Electro-Slag Remelting(ESR) methods. After the steel-making process, they were normalized at 955 deg. C, quenched at 843 .deg. C, and finally tempered at 550 .deg. C or 450 deg. C, resulting in tempered martensitic microstructures with different yielding strengths depending on the tempering conditions. Low-Cycle Fatigue(LCF) tests, Fatigue Crack Growth Rate(FCGR) tests, and fracture toughness tests were performed to investigate the fatigue and fracture behaviors of the pressure vessel steels. In contrast to very similar monotonic, LCF, and FCGR behaviors between VD and ESR steels, a quite difference was noticed in the fracture toughness. Fracture toughness of ESR steel was higher than that of VD steel, being attributed to the removal of impurities in steel-making process

Development of High Heat Input Welding High Strength Steel Plate for Oil Storage Tank in Xinyu Steel Company

Science.gov (United States)

Zhao, Hemin; Dong, Fujun; Liu, Xiaolin; Xiong, Xiong

This essay introduces the developed high-heat input welding quenched and tempered pressure vessel steel 12MnNiVR for oil storage tank by Xinyu Steel, which passed the review by the Boiler and Pressure Vessel Standards Technical Committee in 2009. The review comments that compared to the domestic and foreign similar steel standard, the key technical index of enterprise standard were in advanced level. After the heat input of 100kJ/cm electro-gas welding, welded points were still with excellent low temperature toughness at -20°C. The steel plate may be constructed for oil storage tank, which has been permitted by thickness range from 10 to 40mm, and design temperature among -20°C-100°C. It studied microstructure genetic effects mechanical properties of the steel. Many production practices indicated that the mechanical properties of products and the steel by stress relief heat treatment of steel were excellent, with pretreatment of hot metal, converter refining, external refining, protective casting, TMCP and heat treatment process measurements. The stability of performance and matured technology of Xinyu Steel support the products could completely service the demand of steel constructed for 10-15 million cubic meters large oil storage tank.

Corrosion behavior of 2205 duplex stainless steel.

Science.gov (United States)

Platt, J A; Guzman, A; Zuccari, A; Thornburg, D W; Rhodes, B F; Oshida, Y; Moore, B K

1997-07-01

The corrosion of 2205 duplex stainless steel was compared with that of AISI type 316L stainless steel. The 2205 stainless steel is a potential orthodontic bracket material with low nickel content (4 to 6 wt%), whereas the 316L stainless steel (nickel content: 10 to 14 wt%) is a currently used bracket material. Both stainless steels were subjected to electrochemical and immersion (crevice) corrosion tests in 37 degrees C, 0.9 wt% sodium chloride solution. Electrochemical testing indicates that 2205 has a longer passivation range than 316L. The corrosion rate of 2205 was 0.416 MPY (milli-inch per year), whereas 316L exhibited 0.647 MPY. When 2205 was coupled to 316L with equal surface area ratio, the corrosion rate of 2205 reduced to 0.260 MPY, indicating that 316L stainless steel behaved like a sacrificial anode. When 316L is coupled with NiTi, TMA, or stainless steel arch wire and was subjected to the immersion corrosion test, it was found that 316L suffered from crevice corrosion. On the other hand, 2205 stainless steel did not show any localized crevice corrosion, although the surface of 2205 was covered with corrosion products, formed when coupled to NiTi and stainless steel wires. This study indicates that considering corrosion resistance, 2205 duplex stainless steel is an improved alternative to 316L for orthodontic bracket fabrication when used in conjunction with titanium, its alloys, or stainless steel arch wires.

ABOUT RATIONING MAXIMUM ALLOWABLE DEFECT DEPTH ON THE SURFACE OF STEEL BILLETS IN PRODUCTION OF HOT-ROLLED STEEL

Directory of Open Access Journals (Sweden)

PARUSOV E. V.

2017-01-01

Full Text Available Formulation of the problem. Significant influence on the quality of rolled steel have various defects on its surface, which in its turn inherited from surface defects of billet and possible damage to the surface of rolled steel in the rolling mill line. One of the criteria for assessing the quality indicators of rolled steel is rationing of surface defects [1; 2; 3; 6; 7]. Current status of the issue. Analyzing the different requirements of regulations to the surface quality of the rolled high-carbon steels, we can conclude that the maximum allowable depth of defects on the surface of billet should be in the range of 2.0...5.0 mm (depending on the section of the billet, method of its production and further the destination Purpose. Develop a methodology for calculating the maximum allowable depth of defects on the steel billet surface depending on the requirements placed on the surface quality of hot-rolled steel. Results. A simplified method of calculation, allowing at the rated depth of defects on the surface of the hot-rolled steel to make operatively calculation of the maximum allowable depth of surface defects of steel billets before heating the metal in the heat deformation was developed. The findings shows that the maximum allowable depth of surface defects is reduced with increasing diameter rolled steel, reducing the initial section steel billet and degrees of oxidation of the metal in the heating furnace.

The reactor vessel steels

International Nuclear Information System (INIS)

Bilous, W.; Hajewska, E.; Szteke, W.; Przyborska, M.; Wasiak, J.; Wieczorkowski, M.

2005-01-01

In the paper the fundamental steels using in the construction of pressure vessel water reactor are discussed. The properties of these steels as well as the influence of neutron irradiation on its degradation in the time of exploitation are also done. (authors)

Heat Treatment and Properties of Iron and Steel

National Research Council Canada - National Science Library

Digges, Thomas

1966-01-01

.... Chemical compositions, heat treatments, and some properties and uses are presented for structural steels, tool steels, stainless and heat-resisting steels, precipitation-hardenable stainless steels...

Performance Steel Castings

Science.gov (United States)

2012-09-30

system components to be built. Figure la shows the machine design . PSC-2012 Page 94 Glue Application Sheet Transfer Feed Elevator Figure la...Department of Defense such as cleats, ejection chutes , control arms, muzzle brakes, mortar components, clevises, tow bar clamps, ammo conveyor elements...Foundry and the members of Steel Founders’ Society of America. Abstract Weapon system designers and builders need advanced steel casting technology

High temperature oxidation behavior of ODS steels

Science.gov (United States)

Kaito, T.; Narita, T.; Ukai, S.; Matsuda, Y.

2004-08-01

Oxide dispersion strengthened (ODS) steels are being developing for application as advanced fast reactor cladding and fusion blanket materials, in order to allow increased operation temperature. Oxidation testing of ODS steel was conducted under a controlled dry air atmosphere to evaluate the high temperature oxidation behavior. This showed that 9Cr-ODS martensitic steels and 12Cr-ODS ferritic steels have superior high temperature oxidation resistance compared to 11 mass% Cr PNC-FMS and 17 mass% Cr ferritic stainless steel. This high temperature resistance is attributed to earlier formation of the protective α-Cr 2O 3 on the outer surface of ODS steels.

Fragmentation of armor piercing steel projectiles upon oblique perforation of steel plates

Directory of Open Access Journals (Sweden)

Aizik F.

2012-08-01

Full Text Available In this study, a constitutive strength and failure model for a steel core of a14.5 mm API projectile was developed. Dynamic response of a projectile steel core was described by the Johnson-Cook constitutive model combined with principal tensile stress spall model. In order to obtain the parameters required for numerical description of projectile core material behavior, a series of planar impact experiments was done. The parameters of the Johnson-Cook constitutive model were extracted by matching simulated and experimental velocity profiles of planar impact. A series of oblique ballistic experiments with x-ray monitoring was carried out to study the effect of obliquity angle and armor steel plate thickness on shattering behavior of the 14.5 mm API projectile. According to analysis of x-ray images the fragmentation level increases with both steel plate thickness and angle of inclination. The numerical modeling of the ballistic experiments was done using commercial finite element code, LS-DYNA. Dynamic response of high hardness (HH armor steel was described using a modified Johnson-Cook strength and failure model. A series of simulations with various values of maximal principal tensile stress was run in order to capture the overall fracture behavior of the projectile’s core. Reasonable agreement between simulated and x-ray failure pattern of projectile core has been observed.

On high temperature strength of carbon steels

International Nuclear Information System (INIS)

Ichinose, Hiroyuki; Tamura, Manabu; Kanero, Takahiro; Ihara, Yoshihito

1977-01-01

In the steels for high temperature use, the oxidation resistance is regarded as important, but carbon steels show enough oxidation resistance to be used continuously at the temperature up to 500 deg. C if the strength is left out of consideration, and up to 450 deg. C even when the strength is taken into account. Moreover, the production is easy, the workability and weldability are good, and the price is cheap in carbon steels as compared with alloy steels. In the boilers for large thermal power stations, 0.15-0.30% C steels are used for reheater tubes, main feed water tubes, steam headers, wall water tubes, economizer tubes, bypass pipings and others, and they account for 70% of all steel materials used for the boilers of 350 MW class and 30% in 1000 MW class. The JIS standard for the carbon steels for high temperature use and the related standards in foreign countries are shown. The high temperature strength of carbon steels changes according to the trace elements, melting and heat treatment as well as the main compositions of C, Si and Mn. Al and N affect the high temperature strength largely. The characteristics of carbon steels after the heating for hours, the factors controlling the microstructure and high temperature strength, and the measures to improve the high temperature strength of carbon steels are explained. (Kako, I.)

East/west steels for reactor pressure vessels

International Nuclear Information System (INIS)

Davies, M.; Kryukov, A.; Nikolaev, Y.; English, C.

1997-01-01

The report consist of three parts dealing with comparison of the irradiation behaviour of 'Eastern' and 'Western' steels, mechanisms of irradiation embrittlement and the role of compositional variations on the irradiation sensitivity of pressure vessels. Nickel, copper and phosphorus are the elements rendering the most essential influence on behaviour of pressure vessel steels under irradiation and subsequent thermal annealing. For WWER-440 reactor pressure vessel (RPV) steels in which nickel content does nor exceed 0.3% the main affecting factors are phosphorous and copper. For WWER-1000 RPV welds in which nickel content generally exceed 1.5% the role of nickel in radiation embrittlement is decisive. In 'Western' type steels main influencing elements are nickel and copper. The secondary role of phosphorus in radiation embrittlement of 'Western' steels is caused by lower relative content compared to 'Eastern' steels. The process of how copper, phosphorus and nickel contents affect the irradiation sensitivity of both types of steel seem to be similar. Some distinctions between the observed radiation effects is apparently caused by differences in the irradiation conditions and ratios of the contents of above mentioned elements in both types of steel. For 'Eastern' RPV steels the dependence of the recovery degree of irradiated steels due to postirradiation thermal annealing id obviously dependent on phosphorus contents and the influence of nickel contents on this process is detectable

Development of ferritic steels for fusion reactor applications

Energy Technology Data Exchange (ETDEWEB)

Klueh, R.L.; Maziasz, P.J.; Corwin, W.R.

1988-08-01

Chromium-molybdenum ferritic (martensitic) steels are leading candidates for the structural components for future fusion reactors. However, irradiation of such steels in a fusion environment will produce long-lived radioactive isotopes that will lead to difficult waste-disposal problems. Such problems could be reduced by replacing the elements in the steels (i.e., Mo, Nb, Ni, N, and Cu) that lead to long-lived radioactive isotopes. We have proposed the development of ferritic steels analogous to conventional Cr-Mo steels, which contain molybdenum and niobium. It is proposed that molybdenum be replaced by tungsten and niobium be replaced by tantalum. Eight experimental steels were produced. Chromium concentrations of 2.25, 5, 9, and 12% were used (all concentrations are in wt %). Steels with these chromium compositions, each containing 2% W and 0.25% V, were produced. To determine the effect of tungsten and vanadium, 2.25 Cr steels were produced with 2% W and no vanadium and with 0.25% V and O and 1% W. A 9Cr steel containing 2% W, 0.25 V, and 0.07% Ta was also studied. For all alloys, carbon was maintained at 0.1%. Tempering studies on the normalized steels indicated that the tempering behavior of the new Cr-W steels was similar to that of the analogous Cr-Mo steels. Microscopy studies indicated that 2% tungsten was required in the 2.25 Cr steels to produce 100% bainite in 15.9-mm-thick plate during normalization. The 5Cr and 9Cr steels were 100% martensite, but the 12 Cr steel contained about 75% martensite with the balance delta-ferrite. 33 refs., 35 figs., 5 tabs.

Development of ferritic steels for fusion reactor applications

International Nuclear Information System (INIS)

Klueh, R.L.; Maziasz, P.J.; Corwin, W.R.

1988-08-01

Chromium-molybdenum ferritic (martensitic) steels are leading candidates for the structural components for future fusion reactors. However, irradiation of such steels in a fusion environment will produce long-lived radioactive isotopes that will lead to difficult waste-disposal problems. Such problems could be reduced by replacing the elements in the steels (i.e., Mo, Nb, Ni, N, and Cu) that lead to long-lived radioactive isotopes. We have proposed the development of ferritic steels analogous to conventional Cr-Mo steels, which contain molybdenum and niobium. It is proposed that molybdenum be replaced by tungsten and niobium be replaced by tantalum. Eight experimental steels were produced. Chromium concentrations of 2.25, 5, 9, and 12% were used (all concentrations are in wt %). Steels with these chromium compositions, each containing 2% W and 0.25% V, were produced. To determine the effect of tungsten and vanadium, 2.25 Cr steels were produced with 2% W and no vanadium and with 0.25% V and O and 1% W. A 9Cr steel containing 2% W, 0.25 V, and 0.07% Ta was also studied. For all alloys, carbon was maintained at 0.1%. Tempering studies on the normalized steels indicated that the tempering behavior of the new Cr-W steels was similar to that of the analogous Cr-Mo steels. Microscopy studies indicated that 2% tungsten was required in the 2.25 Cr steels to produce 100% bainite in 15.9-mm-thick plate during normalization. The 5Cr and 9Cr steels were 100% martensite, but the 12 Cr steel contained about 75% martensite with the balance delta-ferrite. 33 refs., 35 figs., 5 tabs

Hydrogen effects in stainless steel

International Nuclear Information System (INIS)

Caskey, G.R. Jr.

1983-01-01

The effects of hydrogen on stainless steels have been reviewed and are summarized in this paper. Discussion covers hydrogen solution and transport in stainless steels as well as the effects of hydrogen on deformation and fracture under various loading conditions. Damage is caused also by helium that arises from decay of the hydrogen isotope tritium. Austenitic, ferritic, martensite, and precipitation-hardenable stainless steels are included in the discussion. 200 references

Occupational Profiles in the European Steel Industry.

Science.gov (United States)

Franz, Hans-Werner; And Others

The steel industry in Europe has faced great changes, with resulting layoffs and restructuring. Now that the most basic changes seem to be over, it has become evident that the remaining steel industry requires more highly trained workers than was the case previously. Although steel maintenance employees were always highly skilled, steel production…

Cold-formed steel design

CERN Document Server

Yu, Wei-Wen

2010-01-01

The definitive text in the field, thoroughly updated and expanded Hailed by professionals around the world as the definitive text on the subject, Cold-Formed Steel Design is an indispensable resource for all who design for and work with cold-formed steel. No other book provides such exhaustive coverage of both the theory and practice of cold-formed steel construction. Updated and expanded to reflect all the important developments that have occurred in the field over the past decade, this Fourth Edition of the classic text provides you with more of the detailed, up-to-the-minute techni

Performance of Retrofitted Self-Compacting Concrete-Filled Steel Tube Beams Using External Steel Plates

Directory of Open Access Journals (Sweden)

Ahmed A. M. AL-Shaar

2018-01-01

Full Text Available Self-compacting concrete-filled steel tube (SCCFST beams, similar to other structural members, necessitate retrofitting for many causes. However, research on SCCFST beams externally retrofitted by bolted steel plates has seldom been explored in the literature. This paper aims at experimentally investigating the retrofitting performance of square self-compacting concrete-filled steel tube (SCCFST beams using bolted steel plates with three different retrofitting schemes including varied configurations and two different steel plate lengths under flexure. A total of 18 specimens which consist of 12 retrofitted SCCFST beams, three unretrofitted (control SCCFST beams, and three hollow steel tubes were used. The flexural behaviour of the retrofitted SCCFST beams was examined regarding flexural strength, failure modes, and moment versus deflection curves, energy absorption, and ductility. Experimental results revealed that the implemented retrofitting schemes efficiently improve the moment carrying capacity and stiffness of the retrofitted SCCFST beams compared to the control beams. The increment in flexural strength ranged from 1% to 46%. Furthermore, the adopted retrofitting schemes were able to restore the energy absorption and ductility of the damaged beams in the range of 35% to 75% of the original beam ductility. Furthermore, a theoretical model was suggested to predict the moment capacity of the retrofitted SCCFST beams. The theoretical model results were in good agreement with the test results.

ESF GROUND SUPPORT - STRUCTURAL STEEL ANALYSIS

Energy Technology Data Exchange (ETDEWEB)

T. Misiak

1996-06-26

The purpose and objective of this analysis are to expand the level of detail and confirm member sizes for steel sets included in the Ground Support Design Analysis, Reference 5.20. This analysis also provides bounding values and details and defines critical design attributes for alternative configurations of the steel set. One possible configuration for the steel set is presented. This analysis covers the steel set design for the Exploratory Studies Facility (ESF) entire Main Loop 25-foot diameter tunnel.

Characterization of friction stir welded joint of low nickel austenitic stainless steel and modified ferritic stainless steel

Science.gov (United States)

Mondal, Mounarik; Das, Hrishikesh; Ahn, Eun Yeong; Hong, Sung Tae; Kim, Moon-Jo; Han, Heung Nam; Pal, Tapan Kumar

2017-09-01

Friction stir welding (FSW) of dissimilar stainless steels, low nickel austenitic stainless steel and 409M ferritic stainless steel, is experimentally investigated. Process responses during FSW and the microstructures of the resultant dissimilar joints are evaluated. Material flow in the stir zone is investigated in detail by elemental mapping. Elemental mapping of the dissimilar joints clearly indicates that the material flow pattern during FSW depends on the process parameter combination. Dynamic recrystallization and recovery are also observed in the dissimilar joints. Among the two different stainless steels selected in the present study, the ferritic stainless steels shows more severe dynamic recrystallization, resulting in a very fine microstructure, probably due to the higher stacking fault energy.

Utilization of structural steel in buildings.

Science.gov (United States)

Moynihan, Muiris C; Allwood, Julian M

2014-08-08

Over one-quarter of steel produced annually is used in the construction of buildings. Making this steel causes carbon dioxide emissions, which climate change experts recommend be reduced by half in the next 37 years. One option to achieve this is to design and build more efficiently, still delivering the same service from buildings but using less steel to do so. To estimate how much steel could be saved from this option, 23 steel-framed building designs are studied, sourced from leading UK engineering firms. The utilization of each beam is found and buildings are analysed to find patterns. The results for over 10 000 beams show that average utilization is below 50% of their capacity. The primary reason for this low value is 'rationalization'-providing extra material to reduce labour costs. By designing for minimum material rather than minimum cost, steel use in buildings could be drastically reduced, leading to an equivalent reduction in 'embodied' carbon emissions.

Corrosion fatigue of pressure vessel steels in PWR environments--influence of steel sulfur content

International Nuclear Information System (INIS)

Scott, P.M.; Druce, S.G.; Truswell, A.E.

1984-01-01

Large effects of simulated light water reactor environments at 288 C on fatigue crack growth in low alloy pressure vessel steels are observed only when specific mechanical, metallurgical, and electrochemical conditions are satisfied simultaneously. In this paper, the relative importance of three key variables--steel impurity content, water chemistry, and flow rate--and their interaction with loading rate or strain rate are examined. In particular, the results of a systematic examination of the influence of a steel's sulfur content are described

Corrosion fatigue of pressure vessel steels in PWR environments--influence of steel sulfur content

Energy Technology Data Exchange (ETDEWEB)

Scott, P.M.; Druce, S.G.; Truswell, A.E.

1984-07-01

Large effects of simulated light water reactor environments at 288 C on fatigue crack growth in low alloy pressure vessel steels are observed only when specific mechanical, metallurgical, and electrochemical conditions are satisfied simultaneously. In this paper, the relative importance of three key variables--steel impurity content, water chemistry, and flow rate--and their interaction with loading rate or strain rate are examined. In particular, the results of a systematic examination of the influence of a steel's sulfur content are described.

Aerosol measurements from plasma torch cuts on stainless steel, carbon steel, and aluminum

International Nuclear Information System (INIS)

Novick, V.J.; Brodrick, C.J.; Crawford, S.; Nasiatka, J.; Pierucci, K.; Reyes, V.; Sambrook, J.; Wrobel, S.; Yeary, J.

1996-01-01

The main purpose of this project is to quantify aerosol particle size and generation rates produced by a plasma torch whencutting stainless steel, carbon steel and aluminum. the plasma torch is a common cutting tool used in the dismantling of nuclear facilities. Eventually, other cutting tools will be characterized and the information will be compiled in a user guide to aid in theplanning of both D ampersand D and other cutting operations. The data will be taken from controlled laboratory experiments on uncontaminated metals and field samples taken during D ampersand D operations at ANL nuclear facilities. The plasma torch data was collected from laboratory cutting tests conducted inside of a closed, filtered chamber. The particle size distributions were determined by isokinetically sampling the exhaust duct using a cascade impactor. Cuts on different thicknesses showed there was no observable dependence of the aerosol quantity produced as a function of material thickness for carbon steel. However, data for both stainless steel and aluminum revealed that the aerosol mass produced for these materials appear to have some dependance on thickness, with thinner materials producing tmore aerosols. The results of the laboratory cutting tests show that most measured particle size distributions are bimodal with one mode at about 0.2 μm and the other at about 10 μm. The average Mass Median Aerodynamic Diameters (MMAD's) for these tests are 0.36 ±0.08 μm for stainless steel, 0.48 ±0.17μm for aluminum and 0.52±0.12 μm for carbon steel

Kawasaki Steel Giho, Vol. 27, No. 4, 1995. Special issue on steel structure

Energy Technology Data Exchange (ETDEWEB)

NONE

1995-12-31

;Contents (Partial): Vertical Gust Prediction of Cable-Stayed Bridges in Yawed Wind; Design and Construction of a Super Platform Structure Made of Steel; Prefabricated Steel Deck of Battledeck Floor Type for Redecking; Aesthetic Design of Structures; and Lift-up Construction Method for Multi-layer Building.

Data for a steel industry model

OpenAIRE

Mæstad, Ottar

2000-01-01

SNF has recently developed a new model of the steel market and some of the major factor markets connected to the steel industry. The aim of the model has been to study how regulations of the emissions of carbon dioxide (CO2) in the steel industry might affect the structure of the industry. It has also been an objective to investigate how structural changes in the steel industry might influence on the industry’s demand for transport services. This paper outlines the details about the data that...

Symbolic aesthetics in steel structural systems

Directory of Open Access Journals (Sweden)

Usama Abdul-Mun'em Khuraibet

2015-02-01

Full Text Available The aesthetic expression and its orders are important for steel structures forming. Steel structures are a compilation of structural elements, where its shapes have standard dimensions and pre-fabricated. As the steel construction systems not only aim to achieve the functional requirements for users, but must also have the symbolic aesthetics which provides visually and cognitive expression for viewers. In this sense the research interested in expressional aesthetics in these systems and highlights the importance of attention as structural items. Therefore the visual items which related with steel structures contain some of the most powerful forms of modern architecture, steel structures with a glass cladding, agility and accuracy in manufacture of structural elements as visual items, structural interest in the forms of spaces which have long span systems or in high buildings are different forms of expression and influence. So the research focuses on the study of those expressive patterns related with the steel construction properties, including the advantages of these systems at the level of strength and firmness, flexibility and economy as well as aesthetic and expression. Accordingly, the research problem concentrated on educational shortage in the study of the structural steel system aspects concerning constructional characteristic, expressive and aesthetic features, and how to deal with them as a language bearing the symbols and meanings which have clear structural style, because it the best ways to make those systems as communication means with users, by premise that the use of expressional symbol in steel construction increases the aesthetic value. Therefore the research aims to reveal the most structural and expressive patterns by analysis the expressional means and steel structural aesthetics.

Future directions for ferritic/martensitic steels for nuclear applications

International Nuclear Information System (INIS)

Klueh, R.L.; Swindeman, R.W.

2000-01-01

High-chromium (7-12% Cr) ferritic/martensitic steels are being considered for nuclear applications for both fission and fusion reactors. Conventional 9-12Cr Cr-Mo steels were the first candidates for these applications. For fusion reactors, reduced-activation steels were developed that were patterned on the conventional steels but with molybdenum replaced by tungsten and niobium replaced by tantalum. Both the conventional and reduced-activation steels are considered to have an upper operating temperature limit of about 550degC. For improved reactor efficiency, higher operating temperatures are required. For ferritic/martensitic steels that could meet such requirements, oxide dispersion-strengthened (ODS) steels are being considered. In this paper, the ferritic/martensitic steels that are candidate steels for nuclear applications will be reviewed, the prospect for ODS steel development and the development of steels produced by conventional processes will be discussed. (author)

Stress corrosion cracking of austenitic stainless steels in high temperature water and alternative stainless steel

International Nuclear Information System (INIS)

Yonezawa, T.

2015-01-01

In order to clarify the effect of SFE on SCC resistance of austenitic stainless steels and to develop the alternative material of Type 316LN stainless steel for BWR application, the effect of chemical composition and heat treatment on SFE value and SCCGR in oxygenated high temperature water were studied. The correlation factors between SFE values for 54 heats of materials and their chemical compositions for nickel, molybdenum, chromium, manganese, nitrogen, silicon and carbon were obtained. From these correlation factors, original formulae for SFE values calculation of austenitic stainless steels in the SHTWC, SHTFC and AGG conditions were established. The maximum crack length, average crack length and cracked area of the IGSCC for 33 heats were evaluated as IGSCC resistance in oxygenated high temperature water. The IGSCC resistance of strain hardened nonsensitized austenitic stainless steels in oxygenated high temperature water increases with increasing of nickel contents and SFE values. From this study, it is suggested that the SFE value is a key parameter for the IGSCC resistance of non-sensitized strain hardened austenitic stainless steels. As an alternative material of Type 316LN stainless steel, increased SFE value material, which is high nickel, high chromium, low silicon and low nitrogen material, is recommendable. (author)

National steel tries wheeling

International Nuclear Information System (INIS)

Dudak, J.R.

1992-01-01

In 1989, National Steel felt the need to take the next step to make its Detroit-based division, Great Lakes Steel, more competitive in the world flat-rolled steel market. In 1988, Great Lakes Steel started flowing natural gas through the first fully litigated bypass (Competitive Sourcing Option) of a local distribution company. In 1989, the second connection with the new supply route for gas transportation, Panhandle Eastern had started flowing and the LDC, Michigan Consolidated Gas Co. (MichCon) had pulled out their piping previously serving the plants. Since we had been able to structure a fully reliable supply route, storage and balancing program for gas in the face of such strong opposition by the LDC, the author felt it was time to attack the next singularly sourced major commodity, electricity. Electricity, at this major integrated steel plant, represented approximately 7% of plant cost yearly. Yet being monopolized, Great Lakes Division (GLD) could not multiple source this commodity like it does with its other 93% of costs, except for labor (25% of the 93%). Multiple sourcing is done to bring competitive pressure to suppliers and to diversify supplies and protect plant operation in the event of failure by one supplier. This paper describes National Steel's strategy to reduce the cost of power, at the minimum of capital costs, the most expedient way possible, that does not sacrifice any major long-term potential cost improvements. The results show that competitively priced power is available across the mid-west, at prices well below many state regulated electric utilities, for at least 5 to 15 years, but with major obstacles in obtaining transmission access

Auburn Steel Company radioactive contamination incident

International Nuclear Information System (INIS)

Bradley, F.J.; Cabasino, L.; Kelly, R.; Awai, A.; Kasyk, G.

1986-04-01

On February 21, 1983, workers at the Auburn Steel Company, Auburn, New York discovered that about 120 tons of steel poured that day had become contaminated with 60 Co. In addition to the steel, the air cleaning system and portions of the mill used in casting the steel were contaminated. Approximately 25 curies of 60 Co were involved. Decontamination and disposal of the contamination cost in excess of $2,200,000. This report details the discovery of the contamination, decontamination of the plant and disposal of the contamination

Steeling and Resilience in Art Education

Science.gov (United States)

Heise, Donalyn

2014-01-01

Steel is an incredibly strong alloy of iron and carbon. Due to its incredible strength and durability, this resilient material is commonly used for constructing buildings. The transitive verb "steeling" is defined in Miriam-Webster dictionary as "to fill with resolution or determination, as in, she 'steeled herself to face the…

Development of commercial nitrogen-rich stainless steels

International Nuclear Information System (INIS)

Liljas, M.

1999-01-01

This paper reviews the development of nitrogen alloyed stainless steels. Nitrogen alloying of austenitic stainless steels started at an early stage and was to a large extent caused by nickel shortage. However, direct technical advantages such as increased strength of the nitrogen alloyed steels made them attractive alternatives to the current steels. It was not until the advent of the AOD (argon oxygen decarburisation) process in the late 1960s that nitrogen alloying could be controlled to such accuracy that it became successful commercially on a broader scale. The paper describes production aspects and how nitrogen addition influences microstructure and the resulting properties of austenitic and duplex stainless steels. For austenitic steels there are several reasons for nitrogen alloying. Apart from increasing strength nitrogen also improves structural stability, work hardening and corrosion resistance. For duplex steels nitrogen also has a decisive effect in controlling the microstructure during thermal cycles such as welding. (orig.)

Damascus steels: history, processing, properties and carbon dating

International Nuclear Information System (INIS)

Wadsworth, J.

2007-01-01

In the mid-1970s, a class of steels containing high levels of carbon (∼ 1-2 wt% C) was developed for superplastic characteristics - that is, the ability to plastically deform to an extraordinary degree in tension at intermediate temperatures. Because these steels also had excellent room temperature properties, they were developed for their commercial potential. In the late 1970s, we became aware of the striking compositional similarities between these modern steels and the ancient steels of Damascus. This observation led us to revisit the history and metallurgy of Damascus steels and related steels. The legends and origins of Damascus steel date back to the time of Alexander the Great (323 BC) and the medieval Crusades (11th and 12th century AD), and this material has also been the subject of scrutiny by famous scientist in Europe, including Michael Faraday. Modern attempts to reproduce the legendary surface patterns which famously characterized Damascus steels are described. The extend to which the characteristics of Damascus steels are unusual is discussed. Finally, a program on radiocarbon dating was initiated to directly determine the age of about 50 ancient steels, including a Damascus knife, and the results are summarized. (author)

Designing of the chemical composition of steels basing on the hardenability of constructional steels

International Nuclear Information System (INIS)

Dobrzanski, L.A.; Sitek, W.

2003-01-01

The paper presents the original method of modelling of the relationships between chemical composition of alloy constructional steel and its hardenability, employing neural networks. Basing on the experimental results of the hardenability investigations, which employed Jominy method, the model of the neural networks was developed and fully verified experimentally. The model makes it possible to obtain Jominy hardenability curves basing on the steel chemical composition. The model of neural networks, making it possible to design the steel chemical composition, basing on the known Jominy hardenability curve shape, was developed also and fully verified numerically. (author)

Mechanical properties of irradiated 9Cr-2WVTa steel

International Nuclear Information System (INIS)

Klueh, R.L.; Alexander, D.J.; Rieth, M.

1998-01-01

An Fe-9Cr-2W-0.25V-0.07Ta-0.1C (9Cr-2WVTa) steel has excellent strength and impact toughness before and after irradiation in the Fast Flux Test Facility and the High Flux Reactor (HFR). The ductile-brittle transition temperature (DBTT) increased only 32 C after 28 dpa at 365 C in FFTF, compared to a shift of ∼60 C for a 9Cr-2WV steel--the same as the 9Cr-2WVTa steel but without tantalum. This difference occurred despite the two steels having similar tensile but without tantalum. This difference occurred despite the two steels having similar tensile properties before and after irradiation. The 9Cr-2WVTa steel has a smaller prior-austenite grain size, but otherwise microstructures are similar before irradiation and show similar changes during irradiation. The irradiation behavior of the 9Cr-2WVTa steel differs from the 9Cr-2WV steel and other similar steels in two ways: (1) the shift in DBTT of the 9Cr-2WVTa steel irradiated in FFTF does not saturate with fluence by ∼28 dpa, whereas for the 9Cr-2WV steel and most similar steels, saturation occurs at <10 dpa, and (2) the shift in DBTT for 9Cr-2WVTa steel irradiated in FFTF and HFR increased with irradiation temperature, whereas it decreased for the 9Cr-2WV steel, as it does for most similar steels. The improved properties of the 9Cr-2WVTa steel and the differences with other steels were attributed to tantalum in solution

Technical features of steel structure construction by Kawasaki Steel; Kawasaki Seitetsu no kokozo gijutsu no tokucho

Energy Technology Data Exchange (ETDEWEB)

Kaneko, T.; Urata, I.; Okata, S. [Kawasaki Steel Corp., Tokyo (Japan)

1996-03-01

In the steel structure technology of Kawasaki Steel, the joint technique (e.g., welding) is added to them while developing or improving the products that meet the social needs as a material supplier. Moreover, the execution technique that manufactures materials or constructs them as an integrated structure, the structural analysis that conforms to the function and application of a structure, and the design technique on dynamic properties or durability such as earthquake resistance, fatigue, and corrosion resistance are synthetically expanded for engineering. In this paper, a building steel frame, non-residence building, bridge, and harbor structure as steel structure in the building and construction fields were described for each structure genre. The structural technology of a building steel frame is summarized to the products of pillar materials. An earthquake brace, using a dead soft steel, with high earthquake energy absorption capability and a damping wall were also developed. The design and execution technique of a large roof was systematized. The exchange technique of a road bridge RC floor and the technique of an unstiffened suspension bridge for pipeline were developed. A new technique was also developed for a suspension monorail track and offshore structure. 30 refs., 5 figs.

Simple Heat Treatment for Production of Hot-Dip Galvanized Dual Phase Steel Using Si-Al Steels

Science.gov (United States)

Equihua-Guillén, F.; García-Lara, A. M.; Muñíz-Valdes, C. R.; Ortíz-Cuellar, J. C.; Camporredondo-Saucedo, J. E.

2014-01-01

This work presents relevant metallurgical considerations to produce galvanized dual phase steels from low cost aluminum-silicon steels which are produced by continuous strip processing. Two steels with different contents of Si and Al were austenized in the two-phase field ferrite + austenite (α + γ) in a fast manner to obtain dual phase steels, suitable for hot-dip galvanizing process, under typical parameters of continuous annealing processing line. Tensile dual phase properties were obtained from specimens cooled from temperature below Ar3, held during 3 min, intermediate cooling at temperature above Ar1 and quenching in Zn bath at 465 °C. The results have shown typical microstructure and tensile properties of galvanized dual phase steels. Finally, the synergistic effect of aluminum, silicon, and residual chromium on martensite start temperature ( M s), critical cooling rate ( C R), volume fraction of martensite, and tensile properties has been studied.

Corrosion behaviour of laser clad stainless steels

International Nuclear Information System (INIS)

Damborenea, J.J. de; Weerasinghe, V.M.; West, D.R.F.

1993-01-01

The present paper is focussed in the study of the properties of a clad layer of stainless steel on a mild steel. By blowing powder of the alloy into a melt pool generated by a laser of 2 KW, an homogeneous layer of 316 stainless steel can be obtained. Structure, composition and corrosion behaviour are similar to those of a stainless steel in as-received condition. (Author)

Ion-nitriding of austenitic stainless steels

International Nuclear Information System (INIS)

Pacheco, O.; Hertz, D.; Lebrun, J.P.; Michel, H.

1995-01-01

Although ion-nitriding is an extensively industrialized process enabling steel surfaces to be hardened by nitrogen diffusion, with a resulting increase in wear, seizure and fatigue resistance, its direct application to stainless steels, while enhancing their mechanical properties, also causes a marked degradation in their oxidation resistance. However, by adaption of the nitriding process, it is possible to maintain the improved wear resistant properties while retaining the oxidation resistance of the stainless steel. The controlled diffusion permits the growth of a nitrogen supersaturated austenite layer on parts made of stainless steel (AISI 304L and 316L) without chromium nitride precipitation. The diffusion layer remains stable during post heat treatments up to 650 F for 5,000 hrs and maintains a hardness of 900 HV. A very low and stable friction coefficient is achieved which provides good wear resistance against stainless steels under diverse conditions. Electrochemical and chemical tests in various media confirm the preservation of the stainless steel characteristics. An example of the application of this process is the treatment of Reactor Control Rod Cluster Assemblies (RCCAs) for Pressurized Water Nuclear Reactors

High - speed steel for precise cased tools

International Nuclear Information System (INIS)

Karwiarz, J.; Mazur, A.

2001-01-01

The test results of high-vanadium high - speed steel (SWV9) for precise casted tools are presented. The face -milling cutters of NFCa80A type have been tested in industrial operating conditions. An average life - time of SWV9 steel tools was 3-10 times longer compare to the conventional high - speed milling cutters. Metallography of SWB9 precise casted steel revealed beneficial for tool properties distribution of primary vanadium carbides in the steel matrix. Presented results should be a good argument for wide application of high - vanadium high - speed steel for precise casted tools. (author)

Thermochemical surface engineering of steels

DEFF Research Database (Denmark)

Thermochemical Surface Engineering of Steels provides a comprehensive scientific overview of the principles and different techniques involved in thermochemical surface engineering, including thermodynamics, kinetics principles, process technologies and techniques for enhanced performance of steels...

The problems of high-nitrogen steels production

International Nuclear Information System (INIS)

Svyazhin, A.G.; Kaputkina, L.M.; Efimenko, S.P.

1999-01-01

Analysis of existing technologies of high-nitrogen steel production shows that rational nitrogen content in mass production corresponds to moderate high values. Such steels can be smelted under normal or slightly elevated pressure in steelmaking units, using processes of mass- and special metallurgy. High-nitrogen steels with ''overequilibrium'' nitrogen content are promising, but technology and equipment for production of them are complicated, and production of such steels is therefore limited. (orig.)

Investigation of special capsule technologies for material in-pile irradiation test and development plan in HANARO

Energy Technology Data Exchange (ETDEWEB)

Cho, M. S.; Son, J. M.; Kim, D. S.; Park, S. J.; Cho, Y. G.; Seo, C. K.; Kang, Y. H. [KAERI, Taejon (Korea, Republic of)

2002-10-01

In-pile test for several materials such as Zr alloy, stainless steel, Cr-Ni steel etc. which are used as structural material of the advanced reactor and KNGR(Korea Next Generation Reactor) like SMART, is necessary to produce the design data for developing new reactor materials. Advanced countries like USA, Europe and Japan etc. are not only performing the simple irradiation test for materials, but developing many kinds of special capsule to perform in-pile test having special purpose. For the special test items of fuel rod, fission products, total heat generation, swelling, deformation, sweep gas, temperature ramping and BOCA etc. are being actively concerned. There are capsules measuring creep, fatigue, crack growth, and controlling fluence etc. for special irradiation test of materials. In addition, the advanced countries are developing several instrument technologies suitable for the special capsules. In HANARO, non-instrumented, instrumented material capsules and non-instrumented fuel capsule have been developed and they have been utilized in the irradiation test for users, and creep capsule loading single specimen was made and is planned to test in the reactor soon. For some forthcoming years, special capsules not only measuring creep deformation with multi-specimens, fatigue, controlling fluence but crack propagation and gas sweep considering the requirements of users will be developed in HANARO.

Behaviour of steels in natural environments: focus on stainless steels in natural sea water

International Nuclear Information System (INIS)

Feron, D.

2005-01-01

Corrosion behaviour of steels and alloys in natural environments is not only dependent to material parameters and environmental chemistry, but also to micro-organisms which may be there. The global approach used to investigate the behaviour of alloys in natural environments is illustrated by the work done on stainless steels in seawater. In aerated seawater, studies led to the proposal of an 'enzymatic model' based on the enzymatic catalyze of the cathodic reaction and which allows reproducing the electrochemical behaviour of stainless steels in natural seawater and the crevice corrosion phenomena observed in natural sea waters. Coupling areas under aerobic and anaerobic conditions leads to the worst situation for stainless steel behaviour: the catalysis of the cathodic reaction on aerobic exposed surfaces and the decrease of the corrosion resistance of anaerobic surfaces due to sulphides. These results lead to the concept of electro-active bio-films. (author)

Structure of three Zlatoust bulats (Damascus-steel blades)

Science.gov (United States)

Schastlivtsev, V. M.; Gerasimov, V. Yu.; Rodionov, D. P.

2008-08-01

Chemical composition, structure, and hardness of samples of three Zlatoust bulats (Damascus steels), namely, an Anosov bulat blade (1841), Obukhov bulat blade (1859), and a Shvetsov forged bulat-steel blank (crucible steel) have been investigated. The Anosov bulat possesses all signs of the classical Damascus steel; this is a hypereutectoid carbon steel with a structure formed from chains of carbides against the background of fine pearlite (troostite). A banded pattern is revealed on the surface of the blade. The Obukhov blade cannot be referred to classical Damascus steel. The pattern on the surface of the blade is absent, despite the fact that the initial steel is hypereutectoid. The structure of the blade does not correspond to the structure of classical Damascus steel; this is bainite with numerous cementite particles. The Shvetsov sample cannot be regarded as Damascus steel since it is made from a hypereutectoid steel alloyed by managanese and tungsten. The pattern on the surface of the metal is a consequence of the dendritic structure of the ingot which is developed during forging. The structure of this pattern differs from classical damascene pattern, since the latter is formed due to a specific arrangement of a variety of carbide particles against the pearlitic or some other background obtained during heat treatment.

Cold formability of steels

International Nuclear Information System (INIS)

Lafond, G.; Leclerq, G.; Moliexe, F.; Namdar, R.; Roesch, L.; Sanz, G.

1977-01-01

This work was essentially aimed to the study of the following three questions. Is it possible to assess the cold formability of steels using simple material properties as criteria. What values of mechanical properties can one expect to reach in cold formed parts. Are there simple ways of characterizing the speroidization treatments carried out on steels before cold forming operations. The present report describes the results obtained during this investigation. It is logically divided into three separate parts. Experimental study of cold formability in wire drawing. Influence of metallurgical variables on mechanical properties of high carbon cold drawn wires. Contribution to the study of characterization methods of cold forming steels subjected to a spheroidization heat treatment

High yttria ferritic ODS steels through powder forging

Science.gov (United States)

Kumar, Deepak; Prakash, Ujjwal; Dabhade, Vikram V.; Laha, K.; Sakthivel, T.

2017-05-01

Oxide dispersion strengthened (ODS) steels are being developed for future nuclear reactors. ODS Fe-18%Cr-2%W-0.2%Ti steels with 0, 0.35, 0.5, 1 and 1.5% Y2O3 (all compositions in weight%) dispersion were fabricated by mechanical alloying of elemental powders. The powders were placed in a mild steel can and forged in a stream of hydrogen gas at 1473 K. The steels were forged again to final density. The strength of ODS steel increased with yttria content. Though this was accompanied by a decrease in tensile elongation, all the steels showed significant ductility. The ductility in high yttria alloys may be attributed to improved inter-particle bonding between milled powders due to reduction of surface oxides by hydrogen. This may permit development of ODS steels with yttria contents higher than the conventional limit of 0.5%. It is suggested that powder forging is a promising route to fabricate ODS steels with high yttria contents and improved ductility.

Behaviour of carbon steel and chromium steels in CO2 environments

International Nuclear Information System (INIS)

Lefebvre, B.; Bounie, P.; Guntz, G.; Prouheze, J.C.; Renault, J.J.

1984-01-01

The behavior in aqueous CO 2 environments of steel with chromium content between 0 and 22% has been studied by autoclave tests. The influence of chromium and molybdenum contents has been investigated particularly on 13 Cr steel. Conventional electrochemical test results are related to the CO 2 autoclave test results. The influence of the environment: temperature, chloride concentration, partial pressure of CO 2 and some amount of H 2 S on the corrosion resistance are discussed

Microstructural Development during Welding of TRIP steels

NARCIS (Netherlands)

Amirthalingam, M.

2010-01-01

The Advanced High Strength Steels (AHSS) are promising solutions for the production of lighter automobiles which reduce fuel consumption and increase passenger safety by improving crash-worthiness. Transformation Induced Plasticity Steel (TRIP) are part of the advanced high strength steels which

Tribological Response of Heat Treated AISI 52100 Steels Against Steel and Ceramic Counterparts

Directory of Open Access Journals (Sweden)

Türedi E.

2017-09-01

Full Text Available AISI 52100 bearing steels are commonly used in applications requiring high hardness and abrasion resistance. The bearing steels are working under dynamic loads in service conditions and their toughness properties become important. In order to provide the desired mechanical properties, various heat treatments (austenizing, quenching and tempering are usually applied. In this study, AISI 52100 bearing steel samples were austenized at 900°C for ½ h and water quenched to room temperature. Then tempering was carried out at 795°C, 400°C and 200°C for ½ h. In order to investigate the effect of heat treatment conditions on wear behavior, dry friction tests were performed according to ASTM G99-05 Standard with a ‘ball-on-disk’ type tribometer. The samples were tested against steel and ceramic counterparts using the parameters of 100 m distance and 30 N load and 0.063 m/s rotational speed. After wear test, the surface characterization was carried out using microscopy. Wear loss values were calculated using a novel optical method on both flat and counterpart specimens.

Precaution against radioactive contamination of steel products in Germany

International Nuclear Information System (INIS)

Ewers, E.; Schulz-Klemp, V.; Steffen, R.

1999-01-01

Regulations for handling of radioactive materials in Germany. Engagement of the Germany Iron and Steel Institute (VDEh) since the end of the eighties and measures taken. Level of radioactivity in uncontaminated steel products. Agreements between steel industry and scrap supplying industry as well as terms of delivery. Actual status of equipment for detection of radioactivity in the German steel plants. Demands of steel users for clean steel. (author)

Anodized Steel Electrodes for Supercapacitors.

Science.gov (United States)

Sagu, Jagdeep S; Wijayantha, K G Upul; Bohm, Mallika; Bohm, Siva; Kumar Rout, Tapan

2016-03-09

Steel was anodized in 10 M NaOH to enhance its surface texture and internal surface area for application as an electrode in supercapacitors. A mechanism was proposed for the anodization process. Field-emission gun scanning electron microscopy (FEGSEM) studies of anodized steel revealed that it contains a highly porous sponge like structure ideal for supercapacitor electrodes. X-ray photoelectron spectroscopy (XPS) measurements showed that the surface of the anodized steel was Fe2O3, whereas X-ray diffraction (XRD) measurements indicated that the bulk remained as metallic Fe. The supercapacitor performance of the anodized steel was tested in 1 M NaOH and a capacitance of 18 mF cm(-2) was obtained. Cyclic voltammetry measurements showed that there was a large psueudocapacitive contribution which was due to oxidation of Fe to Fe(OH)2 and then further oxidation to FeOOH, and the respective reduction of these species back to metallic Fe. These redox processes were found to be remarkably reversible as the electrode showed no loss in capacitance after 10000 cycles. The results demonstrate that anodization of steel is a suitable method to produce high-surface-area electrodes for supercapacitors with excellent cycling lifetime.

Corrosion of steel in concrete

International Nuclear Information System (INIS)

Preece, C.M.

1982-10-01

A comparative study has been made of those properties of Massiv and Standard cements which are considered to determine their ability to protect steel reinforcement from corroding. Saturated Massiv cement has a higher evaporabel water content, but a significantly finer pore structure than has saturated Standard cement. This fine structure resulted in an electrical resistivity ten times higher and chloride diffusivity ten times lower than those of Standard cement. Electrochemical measurements have shown that the passive current density of steel in Massiv mortar is higher than that of steel in Standard mortar, but the higher current should lead to a more rapid decrease in potential to a level at which neither chloride attack of hydrogen evolution will occur. Whereas steel in Standard mortar was found to be highly susceptible to crevice corrosion, no such attack has been observed in Massiv mortar. Moreover, the initiation of chloride induced corrosion and the subsequent rates of corrosion were both lower in Massiv mortar than in Standard mortar. Thus, it may be predicted that Massiv cement would provide greater protection for steel reinforcement in underground structures exposed to chloride containing ground water than would Standard cement. (author)

46 CFR 56.60-5 - Steel (High temperature applications).

Science.gov (United States)

2010-10-01

....A.) Upon prolonged exposure to temperatures above 775 °F (412 °C), the carbide phase of plain carbon steel, plain nickel-alloy steel, carbon-manganese-alloy steel, manganese-vanadium-alloy steel, and carbon-silicon steel may convert to graphite. (b) (Reproduces 124.2.B.) Upon prolonged exposure to...

Austenitic stainless steels with cryogenic resistance

International Nuclear Information System (INIS)

Tarata, Daniela Florentina

1999-01-01

The most used austenitic stainless steels are alloyed with chromium and nickel and have a reduced carbon content, usually lower than 0.1 % what ensures corresponding properties for processing by plastic deformation at welding, corrosion resistance in aggressive environment and toughness at low temperatures. Steels of this kind alloyed with manganese are also used to reduce the nickel content. By alloying with manganese which is a gammageneous element one ensures the stability of austenites. Being cheaper these steels may be used extensively for components and equipment used in cryogenics field. The best results were obtained with steels of second group, AMnNi, in which the designed chemical composition was achieved, i.e. the partial replacement of nickel by manganese ensured the toughness at cryogenic temperatures. If these steels are supplementary alloyed, their strength properties may increase to the detriment of plasticity and toughness, although the cryogenic character is preserved

Micropurity in stainless steel making

International Nuclear Information System (INIS)

Motloch, Z.

1981-01-01

New technologies were developed by the Vitkovice research institutes in response to high requirements for the quality of high-alloy steels for nuclear power, viz., duplex technology with double vacuum degassing at the DH unit and oxidation vacuum degassing using the VAKUVIT equipment. The steel produced shows low contents of impurities and high micropurity. A study was conducted into changes in carbon content and the formation of titanium nitrides and carbonitrides in austenitic steels during their production, and optimum technological parameters were found for eliminating their formation in forgings. (author)

Water requirements of the iron and steel industry

Science.gov (United States)

Walling, Faulkner B.; Otts, Louis Ethelbert

1967-01-01

Twenty-nine steel plants surveyed during 1957 and 1958 withdrew from various sources about 1,400 billion gallons of water annually and produced 40.8 million tons of ingot steel. This is equivalent to about 34,000 gallons of water per ton of steel. Fifteen iron ore mines and fifteen ore concentration plants together withdrew annually about 89,000 million gallons to produce 15 million tons of iron ore concentrate, or 5,900 gallons per ton of concentrate. About 97 percent of the water used in the steel plants came from surface sources, 2.2 percent was reclaimed sewage, and 1.2 percent was ground water. Steel plants supplied about 96 percent of their own water requirements, although only three plants used self-supplied water exclusively. Water used by the iron ore mines and concentration plants was also predominantly self supplied from surface source. Water use in the iron and steel industry varied widely and depended on the availability of water, age and condition of plants and equipment, kinds of processes, and plant operating procedures. Gross water use in integrated steel plants ranged from 11,200 to 110,000 gallons per ton of steel ingots, and in steel processing plants it ranged from 4,180 to 26,700 gallons per ton. Water reuse also varied widely from 0 to 18 times in integrated steel plants and from 0 to 44 times in steel processing plants. Availability of water seemed to be the principal factor in determining the rate of reuse. Of the units within steel plants, a typical (median) blast furnace required 20,500 gallons of water per ton of pig iron. At the 1956-60 average rate of pig iron consumption, this amounts to about 13,000 gallons per ton of steel ingots or about 40 percent of that required by a typical integrated steel plant 33,200 gallons per ton. Different processes of iron ore concentration are devised specifically for the various kinds of ore. These processes result in a wide range of water use from 124 to 11,300 gallons of water per ton of iron ore

Spark Plasma Co-Sintering of Mechanically Milled Tool Steel and High Speed Steel Powders.

Science.gov (United States)

Pellizzari, Massimo; Fedrizzi, Anna; Zadra, Mario

2016-06-16

Hot work tool steel (AISI H13) and high speed steel (AISI M3:2) powders were successfully co-sintered to produce hybrid tool steels that have properties and microstructures that can be modulated for specific applications. To promote co-sintering, which is made difficult by the various densification kinetics of the two steels, the particle sizes and structures were refined by mechanical milling (MM). Near full density samples (>99.5%) showing very fine and homogeneous microstructure were obtained using spark plasma sintering (SPS). The density of the blends (20, 40, 60, 80 wt % H13) was in agreement with the linear rule of mixtures. Their hardness showed a positive deviation, which could be ascribed to the strengthening effect of the secondary particles altering the stress distribution during indentation. A toughening of the M3:2-rich blends could be explained in view of the crack deviation and crack arrest exerted by the H13 particles.

Spark Plasma Co-Sintering of Mechanically Milled Tool Steel and High Speed Steel Powders

Directory of Open Access Journals (Sweden)

Massimo Pellizzari

2016-06-01

Full Text Available Hot work tool steel (AISI H13 and high speed steel (AISI M3:2 powders were successfully co-sintered to produce hybrid tool steels that have properties and microstructures that can be modulated for specific applications. To promote co-sintering, which is made difficult by the various densification kinetics of the two steels, the particle sizes and structures were refined by mechanical milling (MM. Near full density samples (>99.5% showing very fine and homogeneous microstructure were obtained using spark plasma sintering (SPS. The density of the blends (20, 40, 60, 80 wt % H13 was in agreement with the linear rule of mixtures. Their hardness showed a positive deviation, which could be ascribed to the strengthening effect of the secondary particles altering the stress distribution during indentation. A toughening of the M3:2-rich blends could be explained in view of the crack deviation and crack arrest exerted by the H13 particles.

Metallurgy of steels for PWR pressure vessels

International Nuclear Information System (INIS)

Kepka, M.; Mocek, J.; Barackova, L.

1980-01-01

A survey and the chemical compositions are presented of reactor pressure vessel steels. The metallurgy is described of steel making for pressure vessels in Japan and the USSR. Both acidic and alkaline open-hearth steel is used for the manufacture of ingots. The leading world manufacturers of forging ingots for pressure vessels, however, exclusively use electric steel. Vacuum casting techniques are exclusively used. Experience is shown gained with the introduction of the manufacture of forging ingots for pressure vessels at SKODA, Plzen. The metallurgical procedure was tested utilizing alkaline open hearths, electric arc furnaces and facilities for vacuum casting of steel. Pure charge raw materials should be used for securing high steel purity. Prior to forging pressure vessel rings, not only should sufficiently big bottoms and heads be removed but also the ingot middle part should be scrapped showing higher contents of impurities and nonhomogeneous structure. (B.S.)

Metallurgy of steels for PWR pressure vessels

Energy Technology Data Exchange (ETDEWEB)

Kepka, M; Mocek, J; Barackova, L [Skoda, Plzen (Czechoslovakia)

1980-09-01

A survey and the chemical compositions are presented of reactor pressure vessel steels. The metallurgy is described of steel making for pressure vessels in Japan and the USSR. Both acidic and alkaline open-hearth steel is used for the manufacture of ingots. The leading world manufacturers of forging ingots for pressure vessels, however, exclusively use electric steel. Vacuum casting techniques are exclusively used. Experience is shown gained with the introduction of the manufacture of forging ingots for pressure vessels at SKODA, Plzen. The metallurgical procedure was tested utilizing alkaline open hearths, electric arc furnaces and facilities for vacuum casting of steel. Pure charge raw materials should be used for securing high steel purity. Prior to forging pressure vessel rings, not only should sufficiently big bottoms and heads be removed but also the ingot middle part should be scrapped showing higher contents of impurities and nonhomogeneous structure.

Metadynamic recrystallization in C steels

Indian Academy of Sciences (India)

Unknown

EN24 and EN2 steels, a drop from 4000 s to 6 s for similar temperature rise was observed. Metadynamic ... carbon–manganese or silicon–manganese steels, but stops after a reduction at ... growth by strain-induced grain boundary migration;.

A Tale of Wootz Steel

Indian Academy of Sciences (India)

manufacture of steel in south India by a crucible process at ... indicates that the production of wootz steel was almost on an industrial scale in ... in an Age of Design marked by ... The Russian Anasoff also studied the process of manufacturing.

Optimum conditions for aging of stainless maraging steels

International Nuclear Information System (INIS)

Mironenko, P.A.; Krasnikova, S.I.; Drobot, A.V.

1980-01-01

Aging kinetics of two 0Kh11N10M2T type steels in which 3 % Mo (steel 1), and 3 % Mo and 11 % Co (steel 2) had been additionally introduced instead of titanium were investigated. Electron microscopy and X-ray methods were used. It was ascertained that the process of steel aging proceeded in 3 stages. Steel 2 was hardened more intensively during the aging, had a higher degree of hardness and strength after the aging, weakened more slowly if overaged than steel 1. The intermetallide hcp-phase Fe 2 Mo was the hardening phase on steels extended aging. Optimum combination of impact strength and strength was was achieved using two-stage aging: the first stage - maximum strength aging was achieved, the second stage - aging at minimum temperatures of two-phase α+γ region

An Experimental Study on the Shear Hysteresis and Energy Dissipation of the Steel Frame with a Trapezoidal-Corrugated Steel Plate.

Science.gov (United States)

Shon, Sudeok; Yoo, Mina; Lee, Seungjae

2017-03-06

The steel frame reinforced with steel shear wall is a lateral load resisting system and has higher strength and shear performance than the concrete shear wall system. Especially, using corrugated steel plates in these shear wall systems improves out-of-plane stiffness and flexibility in the deformation along the corrugation. In this paper, a cyclic loading test of this steel frame reinforced with trapezoidal-corrugated steel plate was performed to evaluate the structural performance. The hysteresis behavior and the energy dissipation capacity of the steel frame were also compared according to the corrugated direction of the plate. For the test, one simple frame model without the wall and two frame models reinforced with the plate are considered and designed. The test results showed that the model reinforced with the corrugated steel plate had a greater accumulated energy dissipation capacity than the experimental result of the non-reinforced model. Furthermore, the energy dissipation curves of two reinforced frame models, which have different corrugated directions, produced similar results.

Radiation induced microstructural evolution in ferritic/martensitic steels

International Nuclear Information System (INIS)

Kohno, Y.; Kohyama, A.; Asakura, K.; Gelles, D.S.

1993-01-01

R and D of ferritic/martensitic steels as structural materials for fusion reactor is one of the most important issues of fusion technology. The efforts to characterize microstructural evolution under irradiation in the conventional Fe-Cr-Mo steels as well as newly developed Fe-Cr-Mn or Fe-Cr-W low activation ferritic/ martensitic steels have been continued. This paper provides some of the recent results of heavy irradiation effects on the microstructural evolution of ferritic/martensitic steels neutron irradiated in the FFTF/MOTA (Fast Flux Test Facility/Materials Open Test Assembly). Materials examined are Fe-10Cr-2Mo dual phase steel (JFMS: Japanese Ferritic/Martensitic Steel), Fe-12Cr-XMn-1Mo manganese stabilized martensitic steels and Fe-8Cr-2W Tungsten stabilized low activation martensitic steel (F82H). JFMS showed excellent void swelling resistance similar to 12Cr martensitic steel such as HT-9, while the manganese stabilized steels and F82H showed less void swelling resistance with small amount of void swelling at 640-700 K (F82H: 0.14% at 678 K). As for irradiation response of precipitate behavior, significant formation of intermetallic χ phase was observed in the manganese stabilized steels along grain boundaries which is though to cause mechanical property degradation. On the other hand, precipitates identified were the same type as those in unirradiated condition in F82H with no recognition of irradiation induced precipitates, which suggested satisfactory mechanical properties of F82H after the irradiation. (author)

Corrosion fatigue crack growth in clad low-alloy steels: Part 1, medium-sulfur forging steel

International Nuclear Information System (INIS)

James, L.A.; Poskie, T.J.; Auten, T.A.; Cullen, W.H.

1996-01-01

Corrosion fatigue crack propagation tests were conducted on a medium- sulfur ASTM A508-2 forging steel overlaid with weld-deposited Alloy EN82H cladding. The specimens featured semi-elliptical surface cracks penetrating approximately 6.3 mm of cladding into the underlying steel. The initial crack sizes were relatively large with surface lengths of 30.3--38.3 mm, and depths of 13.1--16.8 mm. The experiments were conducted in a quasi-stagnant low-oxygen (O 2 < 10 ppb) aqueous environment at 243 degrees C, under loading conditions (ΔK, R, and cyclic frequency) conductive to environmentally-assisted cracking (EAC) in higher-sulfur steels under quasi-stagnant conditions. Earlier experiments on unclad compact tension specimens of this heat of steel did not exhibit EAC, and the present experiments on semi-elliptical surface cracks penetrating cladding also did not exhibit EAC

A model for TRIP steel constitutive behaviour

NARCIS (Netherlands)

Perdahcioglu, Emin Semih; Geijselaers, Hubertus J.M.; Menari, G

2011-01-01

A constitutive model is developed for TRIP steel. This is a steel which contains three or four different phases in its microstructure. One of the phases in TRIP steels is metastable austenite (Retained Austenite) which transforms to martensite upon deformation. The accompanying transformation strain

Reinforcement steel corrosion in passive state and by carbonation: Consideration of galvanic currents and interface steel - concrete defaults

International Nuclear Information System (INIS)

Nasser, A.

2010-01-01

This thesis aims to study the durability of nuclear waste deep storage structures. The work carried out is essentially an experimental study, and focuses on the corrosion of steel in the passive state with aerated or non-aerated conditions on the one hand, and the corrosion of steel in carbonated concrete during the propagation phase on the other hand. Indeed, the pore solution of concrete in contact with the metal is alkaline (pH between 12 and 13). Under these conditions, steel reinforced concrete remains passive by forming a stable and protective oxide layer (corrosion of steel in the passive state). This passive layer limits the steel corrosion rate at very low values (negligible on a short life time) but not null. For the nuclear waste storage structures due to a very long life time (up to several hundred years), this low corrosion rate can become a risk. Therefore, it is necessary to study the evolution of the oxide layer growth over time. The objectives of the thesis are to study the influence of the steel-concrete interface quality on reinforcement corrosion in passive and active state, and the possible occurrence of galvanic corrosion currents between different reinforcement steel areas. (author)

An evaluation of corrosion resistant alloys by field corrosion test in Japanese refuse incineration plants

International Nuclear Information System (INIS)

Kawahara, Yuuzou; Nakamura, Masanori; Shibuya, Eiichi; Yukawa, Kenichi

1995-01-01

As the first step for development of the corrosion resistant superheater tube materials of 500 C, 100 ata used in high efficient waste-to-energy plants, field corrosion tests of six conventional alloys were carried out at metal temperatures of 450 C and 550 C for 700 and 3,000 hours in four typical Japanese waste incineration plants. The test results indicate that austenitic alloys containing approximately 80 wt% [Cr+Ni] show excellent corrosion resistance. When the corrosive environment is severe, intergranular corrosion of 40∼200 microm depth occurs in stainless steel and high alloyed materials. It is confirmed quantitatively that corrosion behavior is influenced by environmental corrosion factors such as Cl concentration and thickness of deposits on tube surface, metal temperature, and flue gas temperature. The excellent corrosion resistance of high [Cr+Ni+Mo] alloys such as Alloy 625 is explained by the stability of its protective oxide, such that the time dependence of corrosion nearly obeys the parabolic rate law

Wear Resistance of Piston Sleeve Made of Layered Material Structure: MMC A356R, Anti-Abrasion Layer and FGM Interface

Directory of Open Access Journals (Sweden)

Hernik Szymon

2016-09-01

Full Text Available The aim of this paper is the numerical analysis of the one of main part of car engine – piston sleeve. The first example is for piston sleeve made of metal matrix composite (MMC A356R. The second improved material structure is layered. Both of them are comparison to the classical structure of piston sleeve made of Cr-Ni stainless steel. The layered material structure contains the anti-abrasion layer at the inner surface of piston sleeve, where the contact and friction is highest, FGM (functionally graded material interface and the layer of virgin material on the outer surface made of A356R. The complex thermo-elastic model with Archard's condition as a wear law is proposed. The piston sleeve is modelling as a thin walled cylindrical axisymmetric shell. The coupled between the formulation of thermo-elasticity of cylindrical axisymmetric shell and the Archard’s law with functionally changes of local hardness is proposed.

Tensile-property characterization of thermally aged cast stainless steels

International Nuclear Information System (INIS)

Michaud, W.F.; Toben, P.T.; Soppet, W.K.; Chopra, O.K.

1994-02-01

The effect of thermal aging on tensile properties of cast stainless steels during service in light water reactors has been evaluated. Tensile data for several experimental and commercial heats of cast stainless steels are presented. Thermal aging increases the tensile strength of these steels. The high-C Mo-bearing CF-8M steels are more susceptible to thermal aging than the Mo-free CF-3 or CF-8 steels. A procedure and correlations are presented for predicting the change in tensile flow and yield stresses and engineering stress-vs.-strain curve of cast stainless steel as a function of time and temperature of service. The tensile properties of aged cast stainless steel are estimated from known material information, i.e., chemical composition and the initial tensile strength of the steel. The correlations described in this report may be used for assessing thermal embrittlement of cast stainless steel components

Chemical analysis of steel by optical emission spectrometry

International Nuclear Information System (INIS)

Hayakawa, M.O.; Kajita, T.; Jeszensky, G.

1981-01-01

The development of the chemical analysis for special steels by optical emission spectrometry direct reading method with computer, at the Siderurgica N.S. Aparecida S.A. is presented. Results are presented for the low alloy steels and high speed steel. Also, the contribution of this method to the special steel preparation is commented. (Author) [pt

Steamside Oxidation Behavior of Experimental 9%Cr Steels

Energy Technology Data Exchange (ETDEWEB)

Dogan, O.N.; Holcomb, G.R.; Alman, D.E.; Jablonski, P.D.

2007-10-01

Reducing emissions and increasing economic competitiveness require more efficient steam power plants that utilize fossil fuels. One of the major challenges in designing these plants is the availability of materials that can stand the supercritical and ultra-supercritical steam conditions at a competitive cost. There are several programs around the world developing new ferritic and austenitic steels for superheater and reheater tubes exposed to the advanced steam conditions. The new steels must possess properties better than current steels in terms of creep strength, steamside oxidation resistance, fireside corrosion resistance, and thermal fatigue resistance. This paper introduces a series of experimental 9%Cr steels containing Cu, Co, and Ti. Stability of the phases in the new steels is discussed and compared to the phases in the commercially available materials. The steels were tested under both the dry and moist conditions at 650ºC for their cyclical oxidation resistance. Results of oxidation tests are presented. Under the moist conditions, the experimental steels exhibited significantly less mass gain compared to the commercial P91 steel. Microstructural characterization of the scale revealed different oxide compositions.

Plasticity of low carbon stainless steels

International Nuclear Information System (INIS)

Bulat, S.I.; Fel'dgandler, Eh.G.; Kareva, E.N.

1975-01-01

In the temperature range 800-1200 0 C and with strain rates of from 10 -3 to 3 s -1 , austenitic (000Kh18N12) and austenitic-ferrite (000Kh26N6) very low carbon stainless steels containing 0.02-0.03% C exhibit no higher resilience than corresponding ordinary steels containing 0.10-0.12% C. However, the plasticity of such steels (particularly two-phase steels) at 900-1100 0 C is appreciably inferior owing to the development of intergranular brittle fracture. Pressure treatment preceded by partial cooling of the surface to 850 0 C yields rolled and forged products with acceptable indices but is inconvenient technically. At the Zlatoustovsk and Ashin metallurgical plants successful tests have been performed involving the forging and rolling of such steels heated to 1280-1300 0 C without partial cooling; it was necessary to improve the killing conditions, correct the chemical composition (increasing the proportion of ferrite) and take measures against heat loss. (author)

Comparison of the hot-stamped boron-alloyed steel and the warm-stamped medium-Mn steel on microstructure and mechanical properties

International Nuclear Information System (INIS)

Li, Xiaodong; Chang, Ying; Wang, Cunyu; Hu, Ping; Dong, Han

2017-01-01

The application of high strength steels (HSS) for automotive structural parts is an effective way to realize lightweight and enhance safety. Therefore, improvements in mechanical properties of HSS are needed. In the present study, the warm stamping process of the third generation automotive medium-Mn steel was discussed, the characteristics of martensitic transformation were investigated, as well as the microstructure and mechanical properties were analyzed, compared to the popular hot-stamped 22MnB5 steel in the automotive industry. The results are indicated as follows. Firstly, the quenching rate of the medium-Mn steel can be selected in a wide range based on its CCT curves, which is beneficial to the control of forming process. Secondly, the influence of stamping temperature and pressure on the M s temperature of the medium-Mn steel is not obvious and can be neglected, which is favorable to the even distribution of martensitic microstructure and mechanical properties. Thirdly, the phenomenon of decarbonization is hardly found on the surface of the warm-stamped medium-Mn steel, and the ultra-fine-grained microstructure is found inside the medium-Mn steel after warm stamping. Besides, the warm-stamped medium-Mn steel holds the better comprehensive properties, such as a lower yield ratio, higher total elongation and higher tear toughness than the hot-stamped 22MnB5 steel. Furthermore, an actual warm-stamped B-pillar of medium-Mn steel is stamped and ultra-fine-grained martensitic microstructure is obtained. The mechanical properties are evenly distributed. As a result, this paper proves that the warm-stamped medium-Mn steel part can meet the requirements of lightweight and crash safety, and is promising for the industrial production of automotive structural parts.

Comparison of the hot-stamped boron-alloyed steel and the warm-stamped medium-Mn steel on microstructure and mechanical properties

Energy Technology Data Exchange (ETDEWEB)

Li, Xiaodong [School of Automotive Engineering, State Key Lab of Structural Analysis for Industrial Equipment, Dalian University of Technology, Dalian 116024 (China); Chang, Ying, E-mail: yingc@dlut.edu.cn [School of Automotive Engineering, State Key Lab of Structural Analysis for Industrial Equipment, Dalian University of Technology, Dalian 116024 (China); Wang, Cunyu [East China Branch of Central Iron & Steel Research Institute (CISRI), Beijing 100081 (China); Hu, Ping [School of Automotive Engineering, State Key Lab of Structural Analysis for Industrial Equipment, Dalian University of Technology, Dalian 116024 (China); Dong, Han [East China Branch of Central Iron & Steel Research Institute (CISRI), Beijing 100081 (China)

2017-01-02

The application of high strength steels (HSS) for automotive structural parts is an effective way to realize lightweight and enhance safety. Therefore, improvements in mechanical properties of HSS are needed. In the present study, the warm stamping process of the third generation automotive medium-Mn steel was discussed, the characteristics of martensitic transformation were investigated, as well as the microstructure and mechanical properties were analyzed, compared to the popular hot-stamped 22MnB5 steel in the automotive industry. The results are indicated as follows. Firstly, the quenching rate of the medium-Mn steel can be selected in a wide range based on its CCT curves, which is beneficial to the control of forming process. Secondly, the influence of stamping temperature and pressure on the M{sub s} temperature of the medium-Mn steel is not obvious and can be neglected, which is favorable to the even distribution of martensitic microstructure and mechanical properties. Thirdly, the phenomenon of decarbonization is hardly found on the surface of the warm-stamped medium-Mn steel, and the ultra-fine-grained microstructure is found inside the medium-Mn steel after warm stamping. Besides, the warm-stamped medium-Mn steel holds the better comprehensive properties, such as a lower yield ratio, higher total elongation and higher tear toughness than the hot-stamped 22MnB5 steel. Furthermore, an actual warm-stamped B-pillar of medium-Mn steel is stamped and ultra-fine-grained martensitic microstructure is obtained. The mechanical properties are evenly distributed. As a result, this paper proves that the warm-stamped medium-Mn steel part can meet the requirements of lightweight and crash safety, and is promising for the industrial production of automotive structural parts.

From the TRIP effect and Quenching and Partitioning steels concepts to the development of new high-performance, lean powder metallurgy steels

International Nuclear Information System (INIS)

Torralba, José M.; Navarro, Alfonso; Campos, Mónica

2013-01-01

A new method of developing lean powder metallurgy steel is proposed. The microstructure of the steel is tailored by combining two different prealloyed steel grades. These materials open a new niche in steel grades for high-performance applications by using a low-cost method of production. Moreover, an alternative route to developing microstructures suitable for manufacturing TRIP and/or Q and P steels is proposed avoiding some of the complex steps that must otherwise be taken to obtain the proper starting microstructure

From the TRIP effect and Quenching and Partitioning steels concepts to the development of new high-performance, lean powder metallurgy steels

Energy Technology Data Exchange (ETDEWEB)

Torralba, José M., E-mail: josemanuel.torralba@imdea.org [IMDEA Materials Institute, C/Eric Kandel 2, 28906 - Getafe, Madrid (Spain); Department of Materials Science and Engineering, Universidad Carlos III Av. Universidad, 30, Leganés (Spain); Navarro, Alfonso; Campos, Mónica [Department of Materials Science and Engineering, Universidad Carlos III Av. Universidad, 30, Leganés (Spain)

2013-06-20

A new method of developing lean powder metallurgy steel is proposed. The microstructure of the steel is tailored by combining two different prealloyed steel grades. These materials open a new niche in steel grades for high-performance applications by using a low-cost method of production. Moreover, an alternative route to developing microstructures suitable for manufacturing TRIP and/or Q and P steels is proposed avoiding some of the complex steps that must otherwise be taken to obtain the proper starting microstructure.

Japan steel mill perspective

Energy Technology Data Exchange (ETDEWEB)

Murase, K. [Kobe Steel Ltd., Tokyo (Japan)

2004-07-01

The international and Japan's steel industry, the coking coal market, and Japan's expectations from Canada's coal industry are discussed. Japan's steel mills are operating at full capacity. Crude steel production for the first half of 2004 was 55.8 million tons. The steel mills are profitable, but costs are high, and there are difficulties with procuring raw materials. Japan is trying to enhance the quality of coke, in order to achieve higher productivity in the production of pig iron. Economic growth is rising disproportionately in the BRICs (Brazil, Russia, India, and China), with a large increase in coking coal demand from China. On the supply side, there are several projects underway in Australia and Canada to increase production. These include new developments by Elk Valley Coal Corporation, Grande Cache Coal, Western Canadian Coal, and Northern Energy and Mining in Canada. The Elga Mine in the far eastern part of Russia is under development. But the market is expected to remain tight for some time. Japan envisions Canadian coal producers will provide a stable coal supply, expansion of production and infrastructure capabilities, and stabilization of price. 16 slides/overheads are included.

Clean Cast Steel Technology, Phase IV

Energy Technology Data Exchange (ETDEWEB)

Charles E. Bates

2003-02-24

The objective of the Clean Cast Steel Technology Program was to improve casting product quality by removing or minimizing oxide defects and to allow the production of higher integrity castings for high speed machining lines. Previous research has concentrated on macro-inclusions that break, chip, or crack machine tool cutters and drills and cause immediate shutdown of the machining lines. The overall goal of the project is to reduce the amount of surface macro-inclusions and improve the machinability of steel castings. Macro-inclusions and improve the machinability of steel castings. Macro-inclusions have been identified by industrial sponsors as a major barrier to improving the quality and marketability of steel castings.

Mechanical properties of CO2/MIG welded structural rolled steel and stainless steel

International Nuclear Information System (INIS)

Lim, Jong Young; Yoon, Myong Jin; Kim, Sang Youn; Kim, Tae Gyu; Shin, Hyeon Seung

2015-01-01

To accomplish long-term use of specific parts of steel, welding technology is widely applied. In this study, to compare the efficiency in improving mechanical properties, rolled steel (SS400) was welded with stainless steel (STS304) by both CO 2 welding method and MIG (metal inert gas) welding method, respectively. Multi-tests were conducted on the welded specimen, such as X-ray irradiation, Vickers' Hardness, tensile test, fatigue test and fatigue crack growth test. Based on the fatigue crack growth test performed by two different methods, the relationship of da/dN was analyzed. Although the hardness by the two methods was similar, tensile test and fatigue properties of MIG welded specimen are superior to CO 2 welded one.

IMPACT STRENGTH AND FAILURE ANALYSIS OF WELDED DAMASCUS STEEL

Directory of Open Access Journals (Sweden)

Rastislav Mintách

2012-01-01

Full Text Available The aim of this work was the experimental research of damascus steel from point of view of the structural analyze, impact strength and failure analyzes. The damascus steel was produced by method of forged welding from STN 41 4260 spring steel and STN 41 9312 tool steel. The damascus steel consisted of both 84 and 168 layers. The impact strength was experimentally determined for original steels and damascus steels after heat treatment in dependence on temperature in the range from -60 to 160 °C. It has been found that the impact strength of experimental steels decreased with decreasing temperature behind with correlated change of damage mode. In the case of experimental tests performed at high temperature ductile fracture was revealed and with decreasing temperature proportion of cleavage facets increased. Only the STN 41 9312 steel did not show considerable difference in values of the impact strength with changing temperature.

Mechanics in Steels through Microscopy

NARCIS (Netherlands)

Tirumalasetty, G.K.

2013-01-01

The goal of the study consolidated in this thesis is to understand the mechanics in steels using microscopy. In particular, the mechanical response of Transformation Induced Plasticity (TRIP) steels is correlated with their microstructures. Chapter 1 introduces the current state of the art of TRIP

High-strength maraging steels

International Nuclear Information System (INIS)

Grachev, S.V.; Shejn, A.S.

1989-01-01

Analysis of data on technological and operation properties of maraging steels on Fe-Cr-Ni, Fe-Ni, Fe-Cr-Co-Mo bases is given. Their advantages and drawbacks are pointed out. The scheme of strengthening heat treatment is considered. The fields of the most effective application of maraging steels for instance, for products operating under conditions of low-cycle and shock cyclic loading are mentioned

Parallel between steels alloyed with chrome-nickel and Fe-Mn-Al-C steels, in their response to fracture and wear (Review)

International Nuclear Information System (INIS)

Ramos, J; Perez, G.A

2008-01-01

The big worldwide demand for chrome-nickel alloy steels ('conventional steel') leads to the need for advanced materials for applications in different engineering systems that operate at high temperatures and in aggressive environmental conditions, favoring research and development in alternate alloys. In this technological race in search of these new materials, the FeMnAlC alloys ('new steels') have attracted attention for their excellent mechanical and tribological properties as well as for their good performance in corrosive-oxide environments, which make them similar to conventional steel. There are two important similarities between these two steels. First, an agent that causes the passive film to become stainless appears in both steels: chrome in the conventional steel, and aluminum in the FeMnAl alloy. The second similarity is that a stabilizing agent of the austenitic phase (FCC) appears in both, so that excellent mechanical properties can be obtained: nickel in the conventional steel, and manganese in the FeMnAl alloy. In certain sectors, such as aeronautics, conventional steel is rarely used because it is a very heavy material. This conventional steel is almost three times heavier that aluminum (7.85/2.7). Two advantages that the new FeMnAIC steels have compared to the conventional steels are that they are about 13% lighter in weight and they are less expensive. The FeMnAl also have excellent mechanical properties and good corrosion-oxidation resistance, which generates big expectations for their application in a broad scientific spectrum. This work reports the state of the information currently available about FeMnAlC alloys, comparing the mechanical and tribological behaviors of conventional alloy steels with chrome and nickel alloys, specifying the scopes of their application. A condition that favors the steels' fragility is the high speed of deformation and impact, where the FCC crystalline structure materials do not have a fragile ductile transition

Development of structural steels for nuclear application

Energy Technology Data Exchange (ETDEWEB)

Hong, Jun Hwa; Chi, S. H.; Ryu, W. S.; Lee, B. S.; Kim, D. H.; Kim, J. H.; Oh, Y. J.; Byun, T. S.; Yoon, J. H.; Park, D. K.; Oh, J. M.; Cho, H. D.; Kim, H.; Kim, H. D.; Kang, S. S.; Kim, J. W.; Ahn, S. B.

1997-08-01

To established the bases of nuclear structural material technologies, this study was focused on the localization and improvement of nuclear structural steels, the production of material property data, and technology developments for integrity evaluation. The important test and analysis technologies for material integrity assessment were developed, and the materials properties of the pressure vessel steels were evaluated systematically on the basis of those technologies, they are microstructural characteristics, tensile and indentation deformation properties, impact properties, and static and dynamic fracture toughness, fatigue and corrosion fatigue etc. Irradiation tests in the research reactors were prepared or completed to obtain the mechanical properties of irradiated materials. The improvement of low alloy steel was also attempted through the comparative study on the manufacturing processes, computer assisted alloy and process design, and application of the inter critical heat treatment. On the other hand, type 304 stainless steels for reactor internals were developed and tested successfully. High strength type 316LN stainless steels for reactor internals were developed and the microstructural characteristics, corrosion resistance, mechanical properties at high temperatures, low cycle fatigue property etc. were tested and analyzed in the view point of the effect of nitrogen. Type 347 stainless steels with high corrosion resistance and toughness for pipings and tubes and low-activated Cr-Mn steels were also developed and their basic properties were evaluated. Finally, the martensitic stainless steels for turbine blade were developed and tests. (author). 242 refs., 100 tabs., 304 figs.

Development of structural steels for nuclear application

International Nuclear Information System (INIS)

Hong, Jun Hwa; Chi, S. H.; Ryu, W. S.; Lee, B. S.; Kim, D. H.; Kim, J. H.; Oh, Y. J.; Byun, T. S.; Yoon, J. H.; Park, D. K.; Oh, J. M.; Cho, H. D.; Kim, H.; Kim, H. D.; Kang, S. S.; Kim, J. W.; Ahn, S. B.

1997-08-01

To established the bases of nuclear structural material technologies, this study was focused on the localization and improvement of nuclear structural steels, the production of material property data, and technology developments for integrity evaluation. The important test and analysis technologies for material integrity assessment were developed, and the materials properties of the pressure vessel steels were evaluated systematically on the basis of those technologies, they are microstructural characteristics, tensile and indentation deformation properties, impact properties, and static and dynamic fracture toughness, fatigue and corrosion fatigue etc. Irradiation tests in the research reactors were prepared or completed to obtain the mechanical properties of irradiated materials. The improvement of low alloy steel was also attempted through the comparative study on the manufacturing processes, computer assisted alloy and process design, and application of the inter critical heat treatment. On the other hand, type 304 stainless steels for reactor internals were developed and tested successfully. High strength type 316LN stainless steels for reactor internals were developed and the microstructural characteristics, corrosion resistance, mechanical properties at high temperatures, low cycle fatigue property etc. were tested and analyzed in the view point of the effect of nitrogen. Type 347 stainless steels with high corrosion resistance and toughness for pipings and tubes and low-activated Cr-Mn steels were also developed and their basic properties were evaluated. Finally, the martensitic stainless steels for turbine blade were developed and tests. (author). 242 refs., 100 tabs., 304 figs

Use of ferritic steels in breeder reactors worldwide

International Nuclear Information System (INIS)

Patriarca, P.

1983-01-01

The performance of LMFBR reactor steam generator materials is reviewed. Tensile properties of stainless steel-304, stainless steel-316, chromium-molybdenum steels, and Incoloy 800H are presented for elevated temperatures

Comparison of SA508 Gr.3 and SA508 Gr.4N Low Alloy Steels for Reactor Pressure Vessel Steel

Energy Technology Data Exchange (ETDEWEB)

Kim, Min Chul; Lee, B. S

2009-12-15

The microstructural characteristics and mechanical properties of SA508 Gr.3 Mn-Mo-Ni low alloy steel and SA508 Gr.4N Ni-Mo-Cr low alloy steel were investigated. The differences in the stable phases between these two low alloy steels were evaluated by means of a thermodynamic calculation using ThermoCalc. They were then compared to microstructural features and correlated with mechanical properties. Mn-Mo-Ni low alloy steel shows the upper bainite structure which has the coarse cementite in the lath boundaries. However, Ni-Mo-Cr low alloy steel shows the mixture of lower bainite and tempered martensite structure that homogeneously precipitates the small carbides such as M{sub 23}C{sub 6} and M{sub 7}C{sub 3} due to an increase of hardenability and Cr addition. In the mechanical properties, Ni-Mo-Cr low alloy steel has higher strength and toughness than Mn-Mo-Ni low alloy steel. Ni and Cr additions increase the strength by solid solution hardening. Besides, microstructural changes from upper bainite to tempered martensite improve the strength of the low alloy steel by grain refining effect. And the changes in the precipitation behavior by Cr addition improve the ductile-brittle transition behavior along with a toughening effect of Ni addition.

76 FR 2708 - Porcelain-on-Steel Cooking Ware From Taiwan; Top-of-the-Stove Stainless Steel Cooking Ware From...

Science.gov (United States)

2011-01-14

.... 701- TA-267 and 731-TA-304 (Third Review)] Porcelain-on-Steel Cooking Ware From Taiwan; Top-of-the-Stove Stainless Steel Cooking Ware From Korea AGENCY: United States International Trade Commission...-steel cooking ware from Taiwan and the antidumping and countervailing duty orders on imports of top-of...

Solubility and diffusivity of hydrogen in enameling steel

Energy Technology Data Exchange (ETDEWEB)

De Gregorio, P.; Valentini, R.; Solina, A.; Gastaldo, F. (Centro Sviluppo Materiali, Rome (Italy) Pisa Univ. (Italy). Dip. di Ingegneria Chimica, Chimica Industriale e Scienza dei Materiali)

1991-06-01

In recent years, continuous casting has almost expelled conventional ingot casting from the steel-making process by its much higher productivity. However, enameling steel sheets doesn't give the steel sufficient resistance to fishscale, as that which is achieved by the inclusions in case of ingot capped steel. Fishscales are caused by hydrogen gas building up pressure at the interface between enamel and steel, resulting in the rupture of enamel. Object of this study, was not only to correlate fishscale susceptibility with metallurgical parameters, but to define the effect of reversible and irreversible traps on hydrogen solubility and diffusivity in enameling steel. Hydrogen permeation was studied, in low carbon enameling steel, with an electrochemical technique developed by Devanathan and co-workers. This method was used to calculate concentrations of irreversibly adsorbed hydrogen and evaluate hydrogen diffusion coefficients. The results on reversible traps correlated with micro-voids formations around the carbide precipitate, while the irreversible traps correlated with inclusions and precipitate content.

Topic 1. Steels for light water reactor pressure vessels

International Nuclear Information System (INIS)

Brumovsky, M.; Brynda, J.; Kepka, M.; Barackova, L.; Vacek, M.; Havel, S.; Cukr, B.; Protiva, K.; Petrman, I.; Tvrdy, M.; Hyspecka, L.; Mazanec, K.; Kupca, L.; Brezina, M.

1980-01-01

Part 1 of the Proceedings consists of papers on the criteria for the selection and comparison of the properties of steel for pressure vessels and on the metallurgy of the said steels, the selection of suitable material for internal tubing systems, the manufacture of high-alloy steels for WWER components, the mechanical and metallurgical properties of steel 22K for WWER 440 pressure components, and of steel 10MnNi2Mo for the WWER primary coolant circuit, and the metallographic assessment of steel 0Kh18N10T. (J.P.)

Welding Metallurgy and Weldability of Stainless Steels

Science.gov (United States)

Lippold, John C.; Kotecki, Damian J.

2005-03-01

Welding Metallurgy and Weldability of Stainless Steels, the first book in over twenty years to address welding metallurgy and weldability issues associated with stainless steel, offers the most up-to-date and comprehensive treatment of these topics currently available. The authors emphasize fundamental metallurgical principles governing microstructure evolution and property development of stainless steels, including martensistic, ferric, austenitic, duplex, and precipitation hardening grades. They present a logical and well-organized look at the history, evolution, and primary uses of each stainless steel, including detailed descriptions of the associated weldability issues.

Selected properties of new „duplex” cast steel

Directory of Open Access Journals (Sweden)

S. Pietrowski

2011-10-01

Full Text Available In this paper selected properties of new „duplex” cast steel are presented. The new cast steel was devised in HYDRO-VACUUM company in Grudziądz, where “duplex” cast steel for pump elements is smelted. The goal was to devise a new grade of “duplex” cast steel of better physicochemical properties and cheaper than now applied. It was demonstrated, that there is the possibility of devising the new grade of “duplex” cast steel. It is characterized by higher mechanical properties, similar wear resistance and greater corrosion resistance in 15% water solution of H2SO4 in comparison to now applied “duplex” cast steel. The chemical composition was selected to obtain in microstructure about of 50% ferrite and 50% austenite. It guarantee the highest properties and the lowest costs of its smelting.In the paper results of: the microstructure, Rm, Rp0,2, A5, HB, wear resistance and corrosion resistance in water solution of 15% HCl and H2SO4 acids of new cast steel was presented. They were compared with now applied in HYDRO-VACUUM company “duplex” cast steel.

The structure of the alphinizing coat on alloy steels

Directory of Open Access Journals (Sweden)

S. Pietrowski

2008-12-01

Full Text Available In this paper results of the structure of the coat alphinizing in AlSi5 silumin on alloy steels: acid-proof 1H18N9T (X6CrNiTi18-10 and high speed SW18 (HS18-0-1 were presented. The temperature of the alphinizing bath was amounts to750±5°C, and immersion time of the element τ = 180s. It was shown, that there is the different “g” coat thickness on testing steels. On the 1H18N9T steel it amounts to g = 52μm, and on the SW18 steel – g = 203μm. Regardless of a grade of testing alloy steels the coat consist of three layers with diversified phasic structure. There is different chemical composition of coat layers on testing steels. The first layer from the base consist of AlFe phase containing alloy addictions of steels: Cr and Ni (1H18N9T and W, V and Cr (SW18. On this layer crystallize the second layer of intermetallic phases. It is the phase containing the main alloy addiction of steels: AlFeCr (1H18N9T and AlFeW (SW18. The last, outside layer consist of silumin containing AlFeNi intermetallic phases on the 1H18N9T steel and AlFeW on the SW18 steel. Regardless of the grade of testing steels there is Si element in all layers of the coat. There are morphological differences in tested layers. The second layer (AlFeW phase inside the coat on the SW18 steel consist of faced crystals growing into in outside silumin layer. On the 1H18N9T steel a boundary between transient and outside layer is more uniform. Free separations of intermetallic phases inside silumin layer on the 1H18N9T steel have lamellar and on the SW18 steel – faced form.

Marine corrosion of mild steel at Lumut, Perak

Science.gov (United States)

Ting, Ong Shiou; Potty, Narayanan Sambu; Liew, Mohd. Shahir

2012-09-01

The corrosion rate of structural steels in the adverse marine and offshore environments affects the economic interest of offshore structures since the loss of steel may have significant impact on structural safety and performance. With more emphasis to maintain existing structures in service for longer time and hence to defer replacement costs, there is increasing interest in predicting corrosion rate at a given location for a given period of exposure once the protection coating or cathodic protection is lost. The immersion depth, salinity, steel composition and water pollution will be taken into account. Various corrosion allowances are prescribed for structural members by different standards. There are no studies to determine the appropriate corrosion allowance for steel structures in marine environment in Malaysia. The objectives of the research are to determine the nature and rate of corrosion in mm/year for steel structures in marine environment. It also tries to identify whether the corrosion rate is affected by differences in the chemical composition of the steels, and microalgae. Two sets of corrosion coupons of Type 3 Steel consisting of mild steel were fabricated and immersed in seawater using steel frames. The corrosion rate of the coupon in mm/ per year is estimated based on the material weight loss with time in service. The results are compared with recommendations of the code.

A methodology for replacement of conventional steel by microalloyed steel in bus tubular structures

International Nuclear Information System (INIS)

Cruz, Magnus G.H.; Viecelli, Alexandre

2008-01-01

The aim of this article is to show the use of a methodology that allows, in a trustful way and without the need to build up a complete physical model, the replacement of conventional steel by structural microalloyed steel (HSLA) in tubular structure, concerning passengers transport in vehicles with capacity of more than 20 people. The validation of the methodology is based on the ECE R66-00 regulation and on the Brazilian CONTRAN 811/96 resolution, which regulate minimal conditions of safety for this kind of vehicle. The methodology has four sequential and dependent stages, where the main focus is related to the experimental tests through the models that are simplified initially for later calibration using finite element method. Modular structures made of two different materials were tested and analyzed to confirm the present methodology, first the structure made of steel that is used by the bus industry in Brazil was tested and then it was compared with the new microalloyed steel. Experimental values are compared with calculated ones, foreseeing parametric optimisation and keeping the security levels according to legislation

A methodology for replacement of conventional steel by microalloyed steel in bus tubular structures

Energy Technology Data Exchange (ETDEWEB)

Cruz, Magnus G.H. [Marcopolo S.A., Unidade Ana Rech, Av. Rio Branco, 4889, Ana Rach, 95060-650 Caxias do Sul (Brazil)], E-mail: magnus@verbonet.com.br; Viecelli, Alexandre [Mechanical Engineering Department, Universidade de Caxias do Sul, Rua Francisco Getulio Vargas, 1130, 95070-560 Caxias do Sul, RS (Brazil)], E-mail: avieceli@ucs.br

2008-07-01

The aim of this article is to show the use of a methodology that allows, in a trustful way and without the need to build up a complete physical model, the replacement of conventional steel by structural microalloyed steel (HSLA) in tubular structure, concerning passengers transport in vehicles with capacity of more than 20 people. The validation of the methodology is based on the ECE R66-00 regulation and on the Brazilian CONTRAN 811/96 resolution, which regulate minimal conditions of safety for this kind of vehicle. The methodology has four sequential and dependent stages, where the main focus is related to the experimental tests through the models that are simplified initially for later calibration using finite element method. Modular structures made of two different materials were tested and analyzed to confirm the present methodology, first the structure made of steel that is used by the bus industry in Brazil was tested and then it was compared with the new microalloyed steel. Experimental values are compared with calculated ones, foreseeing parametric optimisation and keeping the security levels according to legislation.

High yttria ferritic ODS steels through powder forging

Energy Technology Data Exchange (ETDEWEB)

Kumar, Deepak [Department of Metallurgical and Materials Engineering, I.I.T-Roorkee, Uttarakhand 247667 (India); Prakash, Ujjwal, E-mail: ujwalfmt@iitr.ac.in [Department of Metallurgical and Materials Engineering, I.I.T-Roorkee, Uttarakhand 247667 (India); Dabhade, Vikram V. [Department of Metallurgical and Materials Engineering, I.I.T-Roorkee, Uttarakhand 247667 (India); Laha, K.; Sakthivel, T. [Mechanical Metallurgy Group, IGCAR, Kalpakkam, Tamilnadu 603102 (India)

2017-05-15

Oxide dispersion strengthened (ODS) steels are being developed for future nuclear reactors. ODS Fe-18%Cr-2%W-0.2%Ti steels with 0, 0.35, 0.5, 1 and 1.5% Y{sub 2}O{sub 3} (all compositions in weight%) dispersion were fabricated by mechanical alloying of elemental powders. The powders were placed in a mild steel can and forged in a stream of hydrogen gas at 1473 K. The steels were forged again to final density. The strength of ODS steel increased with yttria content. Though this was accompanied by a decrease in tensile elongation, all the steels showed significant ductility. The ductility in high yttria alloys may be attributed to improved inter-particle bonding between milled powders due to reduction of surface oxides by hydrogen. This may permit development of ODS steels with yttria contents higher than the conventional limit of 0.5%. It is suggested that powder forging is a promising route to fabricate ODS steels with high yttria contents and improved ductility. - Highlights: •ODS steels with yttria contents beyond the conventional limit of 0.5 wt% were fabricated by powder forging in a hydrogen atmosphere. •All the alloys exhibited significant ductility. •This may be attributed to improved inter-particle bonding due to reduction of surface oxides by hydrogen. •Strength in excess of 300 MPa was obtained at 973 K for 0.5%, 1% and 1.5% yttria ODS alloys. •Powder forging is a promising route to fabricate ODS steels and permits development of compositions with up to 1.5% yttria.

75 FR 62144 - Porcelain-on-Steel Cooking Ware From China and Taiwan; Top-of-the-Stove Stainless Steel Cooking...

Science.gov (United States)

2010-10-07

...); (Investigation Nos. 701-TA-267 and 731-TA-304 (Third Review))] Porcelain-on-Steel Cooking Ware From China and Taiwan; Top-of- the-Stove Stainless Steel Cooking Ware From Korea AGENCY: United States International... porcelain-on-steel cooking ware from China and Taiwan and the antidumping and countervailing duty orders on...

Transition welds in welding of two-ply steels

International Nuclear Information System (INIS)

Fartushnyj, V.G.; Evsyukov, Yu.G.

1977-01-01

Studied were physico-mechanical properties of welds made by various welding wires of chromium-nickel and nickel-chromium steels in submerged arc welding of double-layer steels with main layer of the VSt.3sp. carbon steel. It is shown that service-reliable structures welded of two-layer steels are obtained by providing the content from 11 to 20 % Ni in the automatically welded transition layer

Fire-induced collapses of steel structures

DEFF Research Database (Denmark)

Dondera, Alexandru; Giuliani, Luisa

Single-story steel buildings such as car parks and industrial halls are often characterised by stiff beams and flexible columns and may experience an outward (sway) collapse during a fire, endangering people and properties outside the building. It is therefore a current interest of the research...... to investigate the collapse behaviour of single-story steel frames and identify relevant structural characteristics that influence the collapse mode. In this paper, a parametric study on the collapse a steel beam-column assembly with beam hinged connection and fixed column support is carried out under...... on the beam. By means of those tables, a simple method for the assessment and the countermeasure of unsafe collapse mode of single-story steel buildings can be derived....

Stainless Steel to Titanium Bimetallic Transitions

Energy Technology Data Exchange (ETDEWEB)

Kaluzny, J. A. [Fermilab; Grimm, C. [Fermilab; Passarelli, D. [Fermilab

2015-01-01

In order to use stainless steel piping in an LCLS-II (Linac Coherent Light Source Upgrade) cryomodule, stainless steel to titanium bimetallic transitions are needed to connect the stainless steel piping to the titanium cavity helium vessel. Explosion bonded stainless steel to titanium transition pieces and bimetallic transition material samples have been tested. A sample transition tube was subjected to tests and x-ray examinations between tests. Samples of the bonded joint material were impact and tensile tested at room temperature as well as liquid helium temperature. The joint has been used successfully in horizontal tests of LCLS-II cavity helium vessels and is planned to be used in LCLS-II cryomodules. Results of material sample and transition tube tests will be presented.

Experimental studies of Steel Corrugated Constructions

Directory of Open Access Journals (Sweden)

Lazarev Yuriy

2016-01-01

Full Text Available The purpose of this particular article is to assess existing calculations of steel corrugated constructions. Steel Corrugated Construction is a perspective type of constructions, which is exhibiting numerous advantages in comparison with one that currently applied in automobile and railroad networks (reinforced concrete water-throughput pipes, reinforced concrete frame bridges. The evaluation of experimental data on models of constructions of this particular type has been carried out in order to improve calculations of Steel Corrugated Constructions.

The development of EUROFER reduced activation steel

Energy Technology Data Exchange (ETDEWEB)

Schaaf, B. van der E-mail: vanderschaaf@nrg-nl.com; Tavassoli, F.; Fazio, C.; Rigal, E.; Diegele, E.; Lindau, R.; LeMarois, G

2003-09-01

Ferritic martensitic steels show limited swelling and susceptibility to helium effects and can be made with low activation chemical compositions. These properties make them the reference steel for the development of breeding blankets in fusion power plants. EUROFER97 is the European implementation of such a steel, where experience gained from an IEA co-operation with Japan and the US is also implemented. Results obtained so far show that EUROFER steel has attractive mechanical properties even after long ageing times. Compatibility tests in water and PbLi17 are in progress. Oxidised aluminium is the most effective protective layer in PbLi17. The displacement damage and helium formation strongly influence the hydrogen transport in the steel. Present experiments should be backed by tests in a more fusion relevant environment, e.g. IFMIF. The 2.5 dpa neutron irradiations at low temperatures result in a higher DBTT. High dose irradiations, up to 80 dpa, are underway. The early results of ODS grades with EUROFER steel composition show potential of these grades for increasing the operating temperature with 100-150 K.

Assessing the national steel-making problem: the demand for steel products in Brazil (1901-1940

Directory of Open Access Journals (Sweden)

Gustavo Barros

2017-12-01

Full Text Available This paper examines the demand for steel products inBrazil between 1901 and 1940, considering its dimension, its composition and its evolution, as well as the contemporaries’ perception on the issue. In order to do this, a wide array of primary sources is used, including original disaggregated foreign exchange data. Based on these sources, it is observed that the dimension of the potential domestic market exhibited a certain stability along the more than three decades during which the steel-making debate took place, and that this reflected on the contemporary estimates of the size of the market. This relative stability of the market size was accompanied by a diversification process of the demand for steel products. Furthermore, the share of iron and steel products on the value of imports showed a growth trend along the period, highlighting the importance the external constraint had in the shaping of this market in the country.

Corrosion behaviour of dissimilar welds between martensitic stainless steel and carbon steel from secondary circuit of candu npp

International Nuclear Information System (INIS)

Popa, L.; Fulger, M.; Tunaru, M.; Velciu, L.; Lazar, M.

2015-01-01

Corrosion damages of welds occur in spite of the fact that the proper base metal and filler metal have been correctly selected, industry codes and standards have been followed and welds have been realized with full weld penetration and have proper shape and contour. It is not unusual to find that, although the base metal or alloy is resistant to corrosion in a particular environment, the welded counterpart is not resistant. In secondary circuit of a Nuclear Power Station there are some components which have dissimilar welds. Our experiments were performed in chloride environmental on two types of samples: non-welded (420 martensitic steel and 52.2k carbon steel) and dissimilar welds (dissimilar metal welds: joints beetween 420 martensitic steel and 52.2k carbon steel). To evaluate corrosion susceptibility of dissimilar welds was used electrochemical method (potentiodynamic method) and metallography microscopy (microstructural analysis). The present paper follows the localized corrosion behaviour of dissimilar welds between austenitic stainless steel and carbon steel in solutions containing chloride ions. We have been evaluated the corrosion rates of samples (welded and non-welded) by electrochemically. (authors)

Aging degradation of cast stainless steel

International Nuclear Information System (INIS)

Chopra, O.K.; Chung, H.M.

1985-10-01

A program is being conducted to investigate the significance of in-service embrittlement of cast-duplex stainless steels under light-water reactor operating conditions. Data from room-temperature Charpy-impact tests for several heats of cast stainless steel aged up to 10,000 h at 350, 400, and 450 0 C are presented and compared with results from other studies. Microstructures of cast-duplex stainless steels subjected to long-term aging either in the laboratory or in reactor service have been characterized. The results indicate that at least two processes contribute to the low-temperature embrittleent of duplex stainless steels, viz., weakening of the ferrite/austenite phase boundary by carbide precipitation and embrittlement of ferrite matrix by the formation of additional phases such as G-phase, Type X, or the α' phase. Carbide precipitation has a significant effect on the onset of embrittlement of CF-8 and -8M grades of stainless steels aged at 400 or 450 0 C. The existing correlations do not accurately represent the embrittlement behavior over the temperature range 300 to 450 0 C. 18 refs., 13 figs

Iron and steel research at CENIM

International Nuclear Information System (INIS)

Medina, S. F.; Lopez, F.; Morcillo, M.

2003-01-01

In 2002 the National Centre for Metallurgical Research (CENIM) celebrated its 39th anniversary. During this time, steel has been the most studied material of all the metals and alloys researched in the different projects funded by national science and technology plans, European metallurgical research programmes, and by the iron and steel making companies who over the years have placed their trust in the research work undertaken at CENIM. Two generations of researchers have dedicated their careers to studying the different aspects of steel, from primary metallurgy considering iron ores and enrichment processes, the thermodynamics of reactions in the blast furnace and in the ladle, thermal and thermomechanical treatments, the physical metallurgy of steels, their mechanical properties, and finally their deterioration in a wide range of media of different aggressivities. CENIM maintains its commitment to iron and steel research, drawing attention to the vast amount of research work undertaken and financed within the framework of the ECSC programme since Spain joined the European Community in January 1986. (Author) 3 refs

The Vibration Based Fatigue Damage Assessment of Steel and Steel Fiber Reinforced Concrete (SFRC Composite Girder

Directory of Open Access Journals (Sweden)

Xu Chen

2015-01-01

Full Text Available The steel-concrete composite girder has been usually applied in the bridge and building structures, mostly consisting of concrete slab, steel girder, and shear connector. The current fatigue damage assessment for the composite girder is largely based on the strain values and concrete crack features, which is time consuming and not stable. Hence the vibration-based fatigue damage assessment has been considered in this study. In detail, a steel-steel fiber reinforced concrete (SFRC composite girder was tested. The steel fiber reinforced concrete is usually considered for dealing with the concrete cracks in engineering practice. The composite girder was 3.3m long and 0.45m high. The fatigue load and impact excitation were applied on the specimen sequentially. According to the test results, the concrete crack development and global stiffness degradation during the fatigue test were relatively slow due to the favourable performance of SFRC in tension. But on the other hand, the vibration features varied significantly during the fatigue damage development. Generally, it confirmed the feasibility of executing fatigue damage assessment of composite bridge based on vibration method.

Ultrahigh Ductility, High-Carbon Martensitic Steel

Science.gov (United States)

Qin, Shengwei; Liu, Yu; Hao, Qingguo; Zuo, Xunwei; Rong, Yonghua; Chen, Nailu

2016-10-01

Based on the proposed design idea of the anti-transformation-induced plasticity effect, both the additions of the Nb element and pretreatment of the normalization process as a novel quenching-partitioning-tempering (Q-P-T) were designed for Fe-0.63C-1.52Mn-1.49Si-0.62Cr-0.036Nb hot-rolled steel. This high-carbon Q-P-T martensitic steel exhibits a tensile strength of 1890 MPa and elongation of 29 pct accompanied by the excellent product of tensile and elongation of 55 GPa pct. The origin of ultrahigh ductility for high-carbon Q-P-T martensitic steel is revealed from two aspects: one is the softening of martensitic matrix due to both the depletion of carbon in the matensitic matrix during the Q-P-T process by partitioning of carbon from supersaturated martensite to retained austenite and the reduction of the dislocation density in a martensitic matrix by dislocation absorption by retained austenite effect during deformation, which significantly enhances the deformation ability of martensitic matrix; another is the high mechanical stability of considerable carbon-enriched retained austenite, which effectively reduces the formation of brittle twin-type martensite. This work verifies the correctness of the design idea of the anti-TRIP effect and makes the third-generation advanced high-strength steels extend to the field of high-carbon steels from low- and medium-carbon steels.

Steel structures for nuclear facilities

International Nuclear Information System (INIS)

1993-01-01

In the guide the requirements concerning design and fabrication of steel structures for nuclear facilities and documents to be submitted to the Finnish Centre for Radiation and Nuclear Safety (STUK) are presented. Furthermore, regulations concerning inspection of steel structures during construction of nuclear facilities and during their operation are set forth

Stainless steel electrochemical behaviour - application to the decontamination of steel parts contaminated by tritium

International Nuclear Information System (INIS)

Bellanger, G.

1991-01-01

This purpose of this work is the study of an electrochemical decontamination process of stainless steel in which tritium is present on the surface of the metal, in the oxide layer and in the metal. We have first investigated the behaviour of the oxide layer. Then we have studied the hydrogen evolution, its diffusion and retrodiffusion in the metal. The results are applied to the decontamination of steel parts contamined by tritium. Part of the tritium can be eliminated by reducing the oxyde layer, which contains large amounts of tritium. However, it is more beneficial to electrolyse at the potential at which the H + ions are reduced. The hydrogen on the steel surface enters in the metal and displaces most of tritium located in the metallic layers near the surface. The tritium surface elimination rate is about 95%. The tritium eliminated through electrolysis is only a small fraction of all the tritium contained in the metal. However, according to conservation experiments of parts after electrolysis, it can be concluded that hydrogen, probably more strongly bound than tritium to steel, forms near the surface a barrier that prevents tritium retrodiffusion. Electrolysis appears as a satisfactory process for the surface decontamination of slightly tritiated steel parts. A decontamination automaton based on the preceding results is described using a pad electrolyser. This type of decontamination is little polluting, and the parts can be recycled after the in situ treatment [fr

The effect of intermediate stop and ball size in fabrication of recycled steel powder using ball milling from machining steel chips

International Nuclear Information System (INIS)

Fitri, M.W.M.; Shun, C.H.; Rizam, S.S.; Shamsul, J.B.

2007-01-01

A feasibility study for producing recycled steel powder from steel scrap by ball milling was carried out. Steel scrap from machining was used as a raw material and was milled using planetary ball milling. Three samples were prepared in order to study the effect of intermediate stop and ball size. Sample with intermediate stop during milling process showed finer particle size compared to the sample with continuous milling. Decrease in the temperature of the vial during the intermediate stop milling gives less ductile behaviour to the steel powder, which is then easily work-hardened and fragmented to fine powder. Mixed small and big size ball give the best production of recycled steel powder where it gives higher impact force to the scrap and accelerate the fragmentation of the steel scrap into powder. (author)

Austenitic stainless steel-to-ferritic steel transition joint welding for elevated temperature service

International Nuclear Information System (INIS)

King, J.F.; Goodwin, G.M.; Slaughter, G.M.

1978-01-01

Transition weld joints between ferritic steels and austenitic stainless steels are required for fossil-fired power plants and proposed nuclear plants. The experience with these dissimilar-metal transition joints has been generally satisfactory, but an increasing number of failures of these joints is occurring prematurely in service. These concerns with transition joint service history prompted a program to develop more reliable joints for application in proposed nuclear power plants

Electrochemical Determination of Hydrogen Entry to HSLA Steel during Pickling

Directory of Open Access Journals (Sweden)

Jari Aromaa

2018-01-01

Full Text Available Pickling with hydrochloric acid is a standard method to clean steel surfaces before hot-dip galvanizing. When normal low strength steels are pickled, hydrogen formed in pickling reactions does not have any significant harmful effect on the mechanical properties of steel. However, in pickling of steels with higher strength, the penetration of hydrogen into the steel may cause severe damages. The effect of pickling of high-strength low-alloy (HSLA steels was investigated using a cell construction based on the Devanathan-Stachurski method with modified anodic surface treatment and hydrogen production using acid. The penetration and the permeability of hydrogen were measured using an electrochemical cell with hydrochloric acid on the one side of the steel sample and a solution of NaOH on the other side. No protective coating, for example, palladium on the anodic side of the sample, is needed. The penetration rate of hydrogen into the steel and exit rate from the steel were lower for higher strength steel.

Applications of electron beam to precoated steel

International Nuclear Information System (INIS)

Koshiishi, K.; Masuhara, K.

1992-01-01

Applications of EB to precoated steel started with paint cure and have expanded to film lamination and surface modification. These applications can offer precoated steel some advantages which are difficult or impossible to gain by thermal methods. But there are also such problems as adhesion, formability and paintability in EB processing. In practice, using EB technologies along with thermal technologies cannot be avoided for precoated steel at the present. Future development of EB applications to precoated steel will depend on how we can seek superiority and distinction of EB technology against conventional and competitive technologies. (author)

Mechanism of creep in stainless steel

International Nuclear Information System (INIS)

Monteiro, S.N.; Silveira, T.L.

In the present work the creep criterions to identify the deformation mechanisms through the exponent of the strain rate versus stress relationship are presented. When applied to several stainless steels these criterions show an apparent contradiction for the proper mechanism acting at Σ/D above 10 9 /cm 2 . Microstructural aspects interfering in different manners with the fracture of these steels could be a reason for rationalizing the contradictory behavior. This is discussed in suggested deformation maps for the steels investigated [pt

MERGER FOR MONOPOLY: THE FORMATION OF U.S. STEEL

Directory of Open Access Journals (Sweden)

Charles S. Reback

2007-01-01

Full Text Available Scholars have posited three reasons as to why U.S. Steel Corporation was formed: to swindle the public, to monopolize the steel industry, or to become a more efficient firm. The evidence from a stock market event study shows that from its inception, U.S. Steel was viewed as a monopolistic competitor. The stock prices of component and competing firms reacted positively to the announcement of the company’s formation. This is consistent with the theory that U.S. Steel was formed to monopolize the domestic steel industry, inconsistent with the theory that U.S. Steel was formed to become a more efficient firm, and inconsistent with the theory that US. Steel was formed in order to sell overpriced stock to an unsuspecting public. These results confirm Stigler’s conclusions in his classic paper “The Dominant Firm and the Inverted Umbrella,” despite that paper’s empirical flaws. Further, this conclusion is supported by much of the recent literature on U:S. Steel.

Radioisotope methods of investigations of phenomenons at phases border of steel - atmosphere in gaseous processes of thermochemical treatment of steel

International Nuclear Information System (INIS)

L'utse-Birk, A.; Bel'ski, V.; Vez'ranovski, Eh.; Valis', L.

1979-01-01

Radioisotope methods of investigations of the processes of thermochemical treatment of steels are valuable, and in some cases, the only means for analysis of complicated mechanisms of diffusion, absorption and chemical reactions, going on in some technological processes. New specific methods are stated for investigation of processes on the border between steel and gaseous atmosphere. Quantative method nas been developed for investigation of the kinetics of carbon transfere (labelled by carbon-14) from steel into gases. Hydrocarbons and their derivatives are adsorbed selectivelly and beta-activity of the compound is measured in the presence of liquid scintillators. Limiting detectable amount of carbon equals to 0.5μg. Application of labelled (by radioisotope iron-59) iron in steel has ensured a possibility to determine its participation in reactions with chromium and titanum coating atmospheres. Application of hydrocarbons labelled by carbon-14 in the composition of titanum coating atmosphere has permitted to determine, in comparison with investigation of carbon diffusion in steel, participation of two different carbon sources in the forming of the TiC layer on steel and has led to the optimization of processes, especially for low-carbon steels [ru

Prospects of weldable steels for nuclear power engineering

International Nuclear Information System (INIS)

Pilous, V.

1985-01-01

In nuclear power plants with WWER reactors a medium-alloyed CrNiMoV steel is considered for the pressure vessel and a MnNiMoV steel for the primary pipes, the pressurizer and other systems. The chemical composition of both steels is given and briefly discussed are the results of tests carried out within a study of the weldability of the steels. Attention is also devoted to the causes of cracks under austenite-based overlays occurring when medium-alloyed CrNiMoV steels are overlaid with strip electrodes using high thermal input submerged arc welding, and in the process of heat treatment. It appears that austenitic overlays reduce the life span by 5 to 15% as compared with the basic steel. If, however, the overlay is not part of the cross section critical with regard to strength, the reduced life span need not be considered and both types of steel will be suitable for primary circuits of nuclear power plants because they guarantee the required mechanical and physical properties of the welded joints. (Z.M.)

Distribution of Stress in Deformation Zone of Niobium Microalloyed Steel

Science.gov (United States)

Jandrlić, Ivan; Rešković, Stoja; Brlić, Tin

2018-07-01

Microalloyed steels today represent a significant part of total world production and processing of steel. Although widely used, there are scarce data on the stress distribution in the deformation zone of these steels. Research was carried out on two steel grades, both low-carbon structural steels with the same basic chemical composition, with one of them additionally microalloyed with niobium. Differences in the stress distribution in the deformation zone between two tested steels were continuously observed and measured using the methods of digital image correlation and thermography. It has been found out that niobium microalloyed steel has significantly more complex material flow and stress distribution in the deformation zone when compared to the plain low carbon steel.

Distribution of Stress in Deformation Zone of Niobium Microalloyed Steel

Science.gov (United States)

Jandrlić, Ivan; Rešković, Stoja; Brlić, Tin

2018-03-01

Microalloyed steels today represent a significant part of total world production and processing of steel. Although widely used, there are scarce data on the stress distribution in the deformation zone of these steels. Research was carried out on two steel grades, both low-carbon structural steels with the same basic chemical composition, with one of them additionally microalloyed with niobium. Differences in the stress distribution in the deformation zone between two tested steels were continuously observed and measured using the methods of digital image correlation and thermography. It has been found out that niobium microalloyed steel has significantly more complex material flow and stress distribution in the deformation zone when compared to the plain low carbon steel.

TiC reinforced cast Cr steels

Energy Technology Data Exchange (ETDEWEB)

Dogan, O.N.; Hawk, J.A.; Schrems, K.K.

2006-06-01

A new class of materials, namely TiC-reinforced cast chromium (Cr) steels, was developed for applications requiring high abrasion resistance and good fracture toughness. The research approach was to modify the carbide structure of commercial AISI 440C steel for better fracture resistance while maintaining the already high abrasion resistance. The new alloys contained 12Cr, 2.5–4.5Ti, and 1–1.5C (wt.%) and were melted in a vacuum induction furnace. Their microstructure was composed primarily of a martensitic matrix with a dispersion of TiC precipitates. Modification of TiC morphology was accomplished through changing the cooling rate during solidification. Wear rates of the TiC-reinforced Cr steels were comparable to that of AISI 440C steel, but the impact resistance was much improved.

TiC-reinforced cast Cr steels

Science.gov (United States)

Doğan, Ö. N.; Hawk, J. A.; Schrems, K. K.

2006-06-01

A new class of materials, namely TiC-reinforced cast chromium (Cr) steels, was developed for applications requiring high abrasion resistance and good fracture toughness. The research approach was to modify the carbide structure of commercial AISI 440C steel for better fracture resistance while maintaining the already high abrasion resistance. The new alloys contained 12Cr, 2.5-4.5Ti, and 1-1.5C (wt.%) and were melted in a vacuum induction furnace. Their microstructure was composed primarily of a martensitic matrix with a dispersion of TiC precipitates. Modification of TiC morphology was accomplished through changing the cooling rate during solidification. Wear rates of the TiC-reinforced Cr steels were comparable to that of AISI 440C steel, but the impact resistance was much improved.

Volatility Spillover in Chinese Steel Markets

Science.gov (United States)

Fang, Wen

2018-03-01

This paper examines volatility spillover in Chinese steel markets by comparing spillover effects before and after steel futures market established and finds some interesting change. Volatility spillover method based on multi-GARCH model are proposed. The results show that there is significant proof for spillover effects from B2B electronic market to spot market, and two-way effects between futures and spot market. Market policy planners and practitioners could make decisions according to the master of spillovers. We also find that B2B e-market and futures market can both provide efficient protection against steel price volatility risk, B2B e-market offer a broad-based platform for trading steel commodities over time and space since e-market role in information flow process is dominant.

GRAPHITIZED STEELS IN MACHINE-BUILDING

Directory of Open Access Journals (Sweden)

I. V. Akimov

2010-01-01

Full Text Available It is shown that graphitized steels in some cases due to its intermediate disposition by structure and characteristics among low-carbon steels and cast irons, can provide the necessary combination of characteristics of construction material and consequently to increase safety and durability of details of metallurgical and machinebuilding industry machines.

78 FR 11090 - Steel Import Monitoring and Analysis System

Science.gov (United States)

2013-02-15

... tariffs on these steel imports and providing the steel industry time to restructure. The monitoring system... submissions were received from a coalition of eight steel trade groups (referred to as the ``industry''), a... that helps the industry to closely monitor steel imports. The comments are summarized below. The three...

Ferritic steels for French LMFBR steam generators

International Nuclear Information System (INIS)

Aubert, M.; Mathieu, B.; Petrequin, P.

1983-06-01

Austenitic stainless steels have been widely used in many components of the French LMFBR. Up to now, ferritic steels have not been considered for these components, mainly due to their relatively low creep properties. Some ferritic steels are usable when the maximum temperatures in service do not exceed about 530 0 C. It is the case of the steam generators of the Phenix plant, where the exchange tubes of the evaporator are made of 2,25% Cr-1% Mo steel, stabilized or not by addition of niobium. These ferritic alloys have worked successfully since the first steam production in October 1973. For the SuperPhenix power plant, an ''all austenitic stainless alloy'' apparatus has been chosen. However, for the future, ferritic alloys offer potential for use as alternative materials in the evaporators: low alloys steels type 2,25% Cr-1% Mo (exchange tubes, tube-sheets, shells), or at higher chromium content type 9% Cr-2% Mo NbV (exchange tubes) or 12M Cr-1% Mo-V (tube-sheets). Most of these steels have already an industrial background, and are widely used in similar applications. The various potential applications of these steels are reviewed with regards to the French LMFBR steam generators, indicating that some points need an effort of clarification, for instance the properties of the heterogeneous ferritic/austenitic weldments

Thermal stability study for candidate stainless steels of GEN IV reactors

International Nuclear Information System (INIS)

Simeg Veternikova, J.; Degmova, J.; Pekarcikova, M.; Simko, F.; Petriska, M.; Skarba, M.; Mikula, P.; Pupala, M.

2016-01-01

Highlights: • Thermal resistance of advanced stainless steels were observed at 1000 °C. • GEN IV candidate steels were confronted to classic AISI steels. • ODS AISI 316 has weaker thermal resistance than classic AISI steel. • Ferritic ODS steels and NF 709 has better thermal resistance than AISI steels. - Abstract: Candidate stainless steels for GEN IV reactors were investigated in term of thermal and corrosion stability at high temperatures. New austenitic steel (NF 709), austenitic ODS steel (ODS 316) and two ferritic ODS steels (MA 956 and MA 957) were exposed to around 1000 °C in inert argon atmosphere at pressure of ∼8 MPa. The steels were further studied in a light of vacancy defects presence by positron annihilation spectroscopy and their thermal resistance was confronted to classic AISI steels. The thermal strain supported a creation of oxide layers observed by scanning electron microscopy (SEM).

Thermal stability study for candidate stainless steels of GEN IV reactors

Energy Technology Data Exchange (ETDEWEB)

Simeg Veternikova, J., E-mail: jana.veternikova@stuba.sk [Institute of Nuclear and Physical Engineering, Faculty of Electrical and Information Technology, Slovak University of Technology, Ilkovicova 3, 812 19 Bratislava (Slovakia); Degmova, J. [Institute of Nuclear and Physical Engineering, Faculty of Electrical and Information Technology, Slovak University of Technology, Ilkovicova 3, 812 19 Bratislava (Slovakia); Pekarcikova, M. [Institute of Materials Science, Faculty of Materials Science and Technology, Slovak University of Technology, Paulinska 16, 917 24 Trnava (Slovakia); Simko, F. [Department of Molten Salts, Institute of Inorganic Chemistry, Slovak Academy of Sciences, Dubravska cesta 9, 845 36 Bratislava (Slovakia); Petriska, M. [Institute of Nuclear and Physical Engineering, Faculty of Electrical and Information Technology, Slovak University of Technology, Ilkovicova 3, 812 19 Bratislava (Slovakia); Skarba, M. [Slovak University of Technology, Vazovova 5, 812 43 Bratislava (Slovakia); Mikula, P. [Institute of Nuclear and Physical Engineering, Faculty of Electrical and Information Technology, Slovak University of Technology, Ilkovicova 3, 812 19 Bratislava (Slovakia); Pupala, M. [Department of Molten Salts, Institute of Inorganic Chemistry, Slovak Academy of Sciences, Dubravska cesta 9, 845 36 Bratislava (Slovakia)

2016-11-30

Highlights: • Thermal resistance of advanced stainless steels were observed at 1000 °C. • GEN IV candidate steels were confronted to classic AISI steels. • ODS AISI 316 has weaker thermal resistance than classic AISI steel. • Ferritic ODS steels and NF 709 has better thermal resistance than AISI steels. - Abstract: Candidate stainless steels for GEN IV reactors were investigated in term of thermal and corrosion stability at high temperatures. New austenitic steel (NF 709), austenitic ODS steel (ODS 316) and two ferritic ODS steels (MA 956 and MA 957) were exposed to around 1000 °C in inert argon atmosphere at pressure of ∼8 MPa. The steels were further studied in a light of vacancy defects presence by positron annihilation spectroscopy and their thermal resistance was confronted to classic AISI steels. The thermal strain supported a creation of oxide layers observed by scanning electron microscopy (SEM).

Elevated temperature mechanical properties of line pipe steels

Science.gov (United States)

Jacobs, Taylor Roth

The effects of test temperature on the tensile properties of four line pipe steels were evaluated. The four materials include a ferrite-pearlite line pipe steel with a yield strength specification of 359 MPa (52 ksi) and three 485 MPa (70 ksi) yield strength acicular ferrite line pipe steels. Deformation behavior, ductility, strength, strain hardening rate, strain rate sensitivity, and fracture behavior were characterized at room temperature and in the temperature range of 200--350 °C, the potential operating range for steels used in oil production by the steam assisted gravity drainage process. Elevated temperature tensile testing was conducted on commercially produced as-received plates at engineering strain rates of 1.67 x 10 -4, 8.33 x 10-4, and 1.67 x 10-3 s-1. The acicular ferrite (X70) line pipe steels were also tested at elevated temperatures after aging at 200, 275, and 350 °C for 100 h under a tensile load of 419 MPa. The presence of serrated yielding depended on temperature and strain rate, and the upper bound of the temperature range where serrated yielding was observed was independent of microstructure between the ferrite-pearlite (X52) steel and the X70 steels. Serrated yielding was observed at intermediate temperatures and continuous plastic deformation was observed at room temperature and high temperatures. All steels exhibited a minimum in ductility as a function of temperature at testing conditions where serrated yielding was observed. At the higher temperatures (>275 °C) the X52 steel exhibited an increase in ductility with an increase in temperature and the X70 steels exhibited a maximum in ductility as a function of temperature. All steels exhibited a maximum in flow strength and average strain hardening rate as a function of temperature. The X52 steel exhibited maxima in flow strength and average strain hardening rate at lower temperatures than observed for the X70 steels. For all steels, the temperature where the maximum in both flow

Quest for steel quality: the role of metallurgical chemistry

Energy Technology Data Exchange (ETDEWEB)

McLean, A. [Toronto Univ., ON (Canada). Dept. of Metallurgy and Materials Science

2000-10-01

Improvements in the quality of steels and the role played by metallurgical chemistry to bring about those improvements are discussed. The particular emphasis is on the chemical behaviour of solutes in molten steel and the reaction between steel, slag and refractory materials and the manner in which they influence the physical properties and performance of the steel product. As an illustration of the contribution of chemistry to steel making the case of the steel plates used in the construction of the Titanic is cited. In 1911 when the Titanic was constructed by Harland and Wolff at their Belfast shipyard, the steel plates used in the hull met all then current specifications. In 1992 when a number of steel samples recovered from the Titanic were examined, it was found that the hull of the vessel was constructed of low carbon, semi-killed steel, produced in the open-hearth process. Microstructural analysis showed extensive carbon banding, typical of hot rolled 0.2 per cent carbon steel. Also found were long manganese sulphide inclusions elongated in the rolling direction, some of which exceeded 25 mm in length. It was determined that as a consequence of these inclusions, at a seawater temperature of 0 degree C, the hull plates of the Titanic had essentially no resistance to fracture. Today's high quality steels used in applications such as Arctic pipelines, offshore platforms, icebreakers and ships for the transportation of natural gas, oxygen and sulphur concentrations are frequently less than 10 ppm. These elements have a profound influence of the quality of the final steel products by virtue of their effect of hindering the formation of inclusions. 2 refs., 3 figs.

CHARACTERIZATION OF NEW TOOL STEEL FOR ALUMINUM EXTRUSION DIES

OpenAIRE

José Britti Bacalhau; Fernanda Moreno Rodrigues; Rafael Agnelli Mesquita

2014-01-01

Aluminum extrusion dies are an important segment of application on industrial tools steels, which are manufactured in steels based on AISI H13 steel. The main properties of steels applied to extrusion dies are: wear resistance, impact resistance and tempering resistance. The present work discusses the characteristics of a newly developed hot work steel to be used on aluminum extrusion dies. The effects of Cr and Mo contents with respect to tempering resistance and the Al addition ...

Comparison of Corrosion Behavior of Low-Alloy Steel Containing Copper and Antimony with 409L Stainless Steel for a Flue Gas Desulfurization System

Energy Technology Data Exchange (ETDEWEB)

Park, Sun-Ah; Shin, Su-Bin; Kim, Jung-Gu [Sungkyunkwan University, Suwon (Korea, Republic of)

2016-07-15

The corrosion behavior of low alloy steel containing Cu, Sb and 409L stainless steel was investigated for application in the low-temperature section of a flue gas desulfurization (FGD) system. The electrochemical properties were evaluated by potentiodynamic polarization testing and electrochemical impedance spectroscopy (EIS) in 16.9 vol% H{sub 2}SO{sub 4} + 0.35 vol% HCl at 60 ℃. The inclusions in these steels ere identified by electron probe microanalyzer (EPMA). The corrosion products of the steels were analyzed using scanning electron microscope (SEM) with energy dispersive spectroscopy (EDS) and transmission electron microscopy (TEM). The corrosion rate of the low alloy steel containing Cu, Sb was about 100 times lower than that of 409L stainless steel. For stainless steel without passivation, active corrosion behavior was shown. In contrast, in the low alloy steel, the Cu, Sb compounds accumulated on the surface improved the corrosion resistance by suppressing the anodic dissolution reaction.

Evaluation of Flash Bainite in 4130 Steel

Science.gov (United States)

2011-07-01

Technical Report ARWSB-TR-11011 Evaluation of Flash Bainite in 4130 Steel G. Vigilante M. Hespos S. Bartolucci...4. TITLE AND SUBTITLE Evaluation of Flash Bainite in 4130 Steel 5a. CONTRACT NUMBER 5b. GRANT NUMBER 5c. PROGRAM ELEMENT...need to be addressed, the Flash Bainite processing of 4130 steel demonstrates promise for applications needing a combination of high strength with

Thermal embrittlement of reactor vessel steels

International Nuclear Information System (INIS)

Corwin, W.R.; Nanstad, R.K.; Alexander, D.J.; Stoller, R.E.; Wang, J.A.; Odette, G.R.

1995-01-01

As a result of observations of possible thermal embrittlement from recent studies with welds removed from retired steam generators of the Palisades Nuclear Plant (PNP), an assessment was made of thermal aging of reactor pressure vessel (RPV) steels under nominal reactor operating conditions. Discussions are presented on (1) data from the literature regarding relatively low-temperature thermal embrittlement of RPV steels; (2)relevant data from the US power reactor-embrittlement data base (PR-EDB); and (3)potential mechanisms of thermal embrittlement in low-alloy steels

Diffusion zinc plating of structural steels

International Nuclear Information System (INIS)

Kazakovskaya, Tatiana; Goncharov, Ivan; Tukmakov, Victor; Shapovalov, Vyacheslav

2004-01-01

The report deals with the research on diffusion zinc plating of structural steels when replacing their cyanide cadmium plating. The results of the experiments in the open air, in vacuum, in the inert atmosphere, under various temperatures (300 - 500 deg.C) for different steel brands are presented. It is shown that diffusion zinc plating in argon or nitrogen atmosphere ensures obtaining the qualitative anticorrosion coating with insignificant change of mechanical properties of steels. The process is simple, reliable, ecology pure and cost-effective. (authors)

The behaviour of concrete under attack of liquid steel

International Nuclear Information System (INIS)

Schneider, U.; Ehm, C.; Diederichs, U.

1983-01-01

Investigations were carried out to study the interaction between concrete and liquid steel. Different types and different forms of concrete were investigated at temperatures of liquid steel between 1.600 and 2.600 0 C. The liquid steel of 1.600 0 C was produced in an induction furnace, the liquid steel of 2.600 0 C was produced in concrete crucibles by metallothermic reactions. The reactions occuring during the interaction of concrete and liquid steel may be summarized as follows: - Concrete reacts violently upon sudden loading with high temperatures and high heat fluxes. Great quantities of steam and gases are generated. The mechanical strength decreases rapidly with increasing temperature. -At about 1.200 0 C concrete begins to melt. First the cement matrix melts, than the aggregates melt. The melts of different concretes consist of different constituents and their reactions with liquid steel vary. The temperature of the liquid steel significantly influences the intensity of the reactions and the erosion rates. - The erosion rates amounted to 30 mm/min, when liquid steel was produced in concrete crucibles. When cylindrical concrete specimens were immersed in molten steel the rate of melting off amounted up to 66 mm/min. - The dissipation of heat during the interaction brings about that the reactions between concrete and liquid steel vanish gradually, if no additional energy is fed into the system. (orig.)

Comparative Research of Extra-large-span Cable-stayed Bridge with Steel Truss Girder and Steel Box Girder

Directory of Open Access Journals (Sweden)

Tan Manjiang

2015-01-01

Full Text Available To research structural performance of extra-large-span cable-stayed bridge under different section forms, with the engineering background of a 800m main-span cable-stayed bridge with steel truss girder, the cable-stayed bridge with steel box girder is designed according to the current bridge regulations when two bridges are designed in an ultimate state of the carrying capacity, so the maximum stress and minimum stress of the stress envelope diagram are substantially the same. A comprehensive comparison is given to two types of bridge on the aspect of static force, natural vibration frequency, stability, economic performance and so on. Analysis results provide future reference for the large-span cable-stayed bridge to select between the steel truss girder and the steel box girder.

Material physical properties of 12 chromium ferritic steel

International Nuclear Information System (INIS)

Ando, Masanori; Wakai, Takashi; Aoto, Kazumi

2003-09-01

High chromium ferritic steel is an attractive candidate for structural material of the next Fast Breeder Reactor, since both of thermal properties and high temperature strength of the steel are superior to those of conventional austenitic stainless steels. In this study, physical properties of 12Cr steels are measured and compared to those obtained in the previous studies to discuss about stochastic dispersions. The effect of measurement technique on Young's modulus and the influence of the specimen size on coefficient of thermal expansion are also investigated. The following conclusions are obtained. (1) Young's modulus of 12Cr steels obtained in this study tends to larger than those obtained in the previous studies especially in high temperature. Such a discrepancy is resulted from the difference in measurement technique. It was clarified that Young's modulus obtained by free vibration method is more adequate those obtained by the cantilever characteristic vibration method. Therefore, the authors recommend using the values obtained by free vibration method as Young's modulus of 12Cr steels. (2) Both instant and mean coefficient of thermal expansion of 12Cr steels obtained in this study is in a good agreement with those obtained in the previous studies. However, the obviously different values are obtained from the measurement by large size specimens. Such a discrepancy is resulted from heterogeneous during heating process of the specimens. Therefore, the authors recommend using the values obtained by φ4 x 20 mm specimens as instant and mean coefficient of thermal expansion of 12Cr steels. (3) Specific heat of 12Cr steels obtained in this study agree with those obtained in the previous studies with a few exceptions. (4)Thermal conductivity of 12Cr steels obtained in this study agree with those obtained in the previous studies. (5) It was confirmed that instant and mean coefficient of thermal expansion, density, specific heat and thermal conductivity of 12Cr steels

Stability of ferritic steel to higher doses: Survey of reactor pressure vessel steel data and comparison with candidate materials for future nuclear systems

International Nuclear Information System (INIS)

Blagoeva, D.T.; Debarberis, L.; Jong, M.; Pierick, P. ten

2014-01-01

This paper is illustrating the potential of the well-known low alloyed clean steels, extensively used for the current light water Reactor Pressure Vessels (RPV) steels, for a likely use as a structural material also for the new generation nuclear systems. This option would provide, especially for large components, affordable, easily accessible and a technically more convenient solution in terms of manufacturing and joining techniques. A comprehensive comparison between several sets of surveillance and research data available for a number of RPV clean steels for doses up to 1.5 dpa, and up to 12 dpa for 9%Cr steels, is carried out in order to evaluate radiation stability of the currently used RPV clean steels even at higher doses. Based on the numerous data available, positive preliminary conclusions are drawn regarding the eventual use of clean RPV steels for the massive structural components of the new reactor systems. - Highlights: • Common embrittlement trend between RPV and advanced steels till intermediate doses. • For doses >1.5 dpa, damage rate saturation tendency is observed for RPV steels. • RPV steels might be conveniently utilised also outside their foreseen dose range

Neutron irradiation creep in stainless steel alloys

Energy Technology Data Exchange (ETDEWEB)

Schuele, Wolfgang (Commission of the European Union, Institute for Advanced Materials, I-21020 Ispra (Vatican City State, Holy See) (Italy)); Hausen, Hermann (Commission of the European Union, Institute for Advanced Materials, I-21020 Ispra (Vatican City State, Holy See) (Italy))

1994-09-01

Irradiation creep elongations were measured in the HFR at Petten on AMCR steels, on 316 CE-reference steels, and on US-316 and US-PCA steels varying the irradiation temperature between 300 C and 500 C and the stress between 25 and 300 MPa. At the beginning of an irradiation a type of primary'' creep stage is observed for doses up to 3-5 dpa after which dose the secondary'' creep stage begins. The primary'' creep strain decreases in cold-worked steel materials with decreasing stress and decreasing irradiation temperature achieving also negative creep strains depending also on the pre-treatment of the materials. These primary'' creep strains are mainly attributed to volume changes due to the formation of radiation-induced phases, e.g. to the formation of [alpha]-ferrite below about 400 C and of carbides below about 700 C, and not to irradiation creep. The secondary'' creep stage is found for doses larger than 3 to 5 dpa and is attributed mainly to irradiation creep. The irradiation creep rate is almost independent of the irradiation temperature (Q[sub irr]=0.132 eV) and linearly dependent on the stress. The total creep elongations normalized to about 8 dpa are equal for almost every type of steel irradiated in the HFR at Petten or in ORR or in EBR II. The negative creep elongations are more pronounced in PCA- and in AMCR-steels and for this reason the total creep elongation is slightly smaller at 8 dpa for these two steels than for the other steels. ((orig.))

Steel Housing - The Reinvention of the Square Wheel?

NARCIS (Netherlands)

Willems, M.H.P.M.

2002-01-01

Steel housing has some remarkable resemblance with a square wheel. Both combine a simple concept, uncommon appearance and lack of appreciation. The title furthermore refers to the repeated stubborn efforts over the last decennia to develop prefabricated steel-based housing systems. Steel has

Steel Creek primary producers: Periphyton and seston, L-Lake/Steel Creek Biological Monitoring Program, January 1986--December 1991

Energy Technology Data Exchange (ETDEWEB)

Bowers, J.A. [Westinghouse Savannah River Co., Aiken, SC (United States); Toole, M.A.; van Duyn, Y. [Normandeau Associates Inc., New Ellenton, SC (United States)

1992-02-01

The Savannah River Site (SRS) encompasses 300 sq mi of the Atlantic Coastal Plain in west-central South Carolina. Five major tributaries of the Savannah River -- Upper Three Runs Creek, Four Mile Creek, Pen Branch, Steel Creek, and Lower Three Runs Creek -- drain the site. In 1985, L Lake, a 400-hectare cooling reservoir, was built on the upper reaches of Steel Creek to receive effluent from the restart of L-Reactor and to protect the lower reaches from thermal impacts. The Steel Creek Biological Monitoring Program was designed to assess various components of the system and identify and changes due to the operation of L-Reactor or discharge from L Lake. An intensive ecological assessment program prior to the construction of the lake provided baseline data with which to compare data accumulated after the lake was filled and began discharging into the creek. The Department of Energy must demonstrate that the operation of L-Reactor will not significantly alter the established aquatic ecosystems. This report summarizes the results of six years` data from Steel Creek under the L-Lake/Steel Creek Monitoring Program. L Lake is discussed separately from Steel Creek in Volumes NAI-SR-138 through NAI-SR-143.

Steel Creek primary producers: Periphyton and seston, L-Lake/Steel Creek Biological Monitoring Program, January 1986--December 1991

International Nuclear Information System (INIS)

Bowers, J.A.; Toole, M.A.; van Duyn, Y.

1992-02-01

The Savannah River Site (SRS) encompasses 300 sq mi of the Atlantic Coastal Plain in west-central South Carolina. Five major tributaries of the Savannah River -- Upper Three Runs Creek, Four Mile Creek, Pen Branch, Steel Creek, and Lower Three Runs Creek -- drain the site. In 1985, L Lake, a 400-hectare cooling reservoir, was built on the upper reaches of Steel Creek to receive effluent from the restart of L-Reactor and to protect the lower reaches from thermal impacts. The Steel Creek Biological Monitoring Program was designed to assess various components of the system and identify and changes due to the operation of L-Reactor or discharge from L Lake. An intensive ecological assessment program prior to the construction of the lake provided baseline data with which to compare data accumulated after the lake was filled and began discharging into the creek. The Department of Energy must demonstrate that the operation of L-Reactor will not significantly alter the established aquatic ecosystems. This report summarizes the results of six years' data from Steel Creek under the L-Lake/Steel Creek Monitoring Program. L Lake is discussed separately from Steel Creek in Volumes NAI-SR-138 through NAI-SR-143

Interphase and intergranular stress generation in carbon steels

International Nuclear Information System (INIS)

Oliver, E.C.; Daymond, M.R.; Withers, P.J.

2004-01-01

Neutron diffraction spectra have been acquired during tensile straining of high and low carbon steels, in order to compare the evolution of internal stress in ferritic steel with and without a reinforcing phase. In low carbon steel, the generation of intergranular stresses predominates, while in high carbon steel similar intergranular stresses among ferrite grain families are superposed upon a large redistribution of stress between phases. Comparison is made to calculations using elastoplastic self-consistent and finite element methods

Enhanced Inclusion Removal from Steel in the Tundish

Energy Technology Data Exchange (ETDEWEB)

R. C. Bradt; M.A.R. Sharif

2009-09-25

The objective of this project was to develop an effective chemical filtering system for significantly reducing the content of inclusion particles in the steel melts exiting the tundish for continuous casting. This project combined a multi-process approach that aimed to make significant progress towards an "inclusion free" steel by incorporating several interdependent concepts to reduce the content of inclusions in the molten steel exiting the tundish for the caster. The goal is to produce "cleaner" steel.

Enhanced Incluison Removal from Steel in the Tundish

Energy Technology Data Exchange (ETDEWEB)

R.C. Bradt; M.A.R. Sharif

2009-09-25

The objective of this project was to develop an effective chemical filtering system for significantly reducing the content of inclusion particles in the steel melts exiting the tundish for continuous casting. This project combined a multi-process approach that aimed to make significant progress towards an "inclusion free" steel by incorporating several interdependent concepts to reduce the content of inclusions in the molten steel exiting the tundish for the caster. The goal is to produce "cleaner" steel.

Durability of light steel framing in residential applications

OpenAIRE

Lawson, RM; Popo-Ola, S.O.; Way, A.; Heatley, T; Pedreschi, Remo

2010-01-01

This paper presents a summary and analysis of research findings on the durability of galvanised cold-formed steel sections used in housing in order to deduce their design life. These cold-formed sections are produced from pre-galvanised strip steel. It reviews reports and publications from research projects carried out by Corus and the Steel Construction Institute on zinc-coated, cold-formed steel products. New data have also been gathered from measurements on houses and similar buildings tha...

Chemical decontamination of stainless steel

International Nuclear Information System (INIS)

Onuma, Tsutomu; Akimoto, Hidetoshi

1991-01-01

The present invention concerns a method for chemical decontamination of radioactive metal waste materials contaminated with radioactive materials on the surface, generated in radioactive materials-handling facilities. The invention is comprised of a method of chemical decontamination of stainless steel, characterized by comprising a first process of immersing a stainless steel-based metal waste material contaminated by radioactive materials on the surface in a sulfuric acid solution and second process of immersing in an aqueous solution of sulfuric acid and oxidizing metal salt, in which a portion of the surface of the stainless steel to be decontaminated is polished mechanically to expose a portion of the base material before the above first and second processes. 1 figs., 2 tabs

Corrosion of carbon steel welds

International Nuclear Information System (INIS)

Daniel, B.

1988-09-01

This report assesses the factors which cause preferential attack to occur in carbon steel fusion welds. It was concluded that the main factors were: the inclusion content of the weld metal, the potential of the weld metal being less noble than that of the parent, and the presence of low-temperature transformation products in the heat-affected zone of the weld. These factors should be minimized or eliminated as appropriate so that the corrosion allowances determined for carbon steel waste drums is also adequate for the welds. An experimental/theoretical approach is recommended to evaluate the relative corrosion resistance of welds prepared from BS 4360 grade 43A steel to that of the parent material. (author)

Tensile behavior of irradiated manganese-stabilized stainless steel

Energy Technology Data Exchange (ETDEWEB)

Klueh, R.L. [Oak Ridge National Lab., TN (United States)

1996-10-01

Tensile tests were conducted on seven experimental, high-manganese austenitic stainless steels after irradiation up to 44 dpa in the FFTF. An Fe-20Mn-12Cr-0.25C base composition was used, to which various combinations of Ti, W, V, B, and P were added to improve strength. Nominal amounts added were 0.1% Ti, 1% W, 0.1% V, 0.005% B, and 0.03% P. Irradiation was carried out at 420, 520, and 600{degrees}C on the steels in the solution-annealed and 20% cold-worked conditions. Tensile tests were conducted at the irradiation temperature. Results were compared with type 316 SS. Neutron irradiation hardened all of the solution-annealed steels at 420, 520, and 600{degrees}C, as measured by the increase in yield stress and ultimate tensile strength. The steel to which all five elements were added to the base composition showed the least amount of hardening. It also showed a smaller loss of ductility (uniform and total elongation) than the other steels. The total and uniform elongations of this steel after irradiation at 420{degrees}C was over four times that of the other manganese-stabilized steels and 316 SS. There was much less difference in strength and ductility at the two higher irradiation temperatures, where there was considerably less hardening, and thus, less loss of ductility. In the cold-worked condition, hardening occured only after irradiation at 420{degrees}C, and there was much less difference in the properties of the steels after irradiation. At the 420{degrees}C irradiation temperature, most of the manganese-stabilized steels maintained more ductility than the 316 SS. After irradiation at 420{degrees}C, the temperature of maximum hardening, the steel to which all five of the elements were added had the best uniform elongation.

A comparison of the tribological behaviour of steel/steel, steel/DLC and DLC/DLC contact when lubricated with mineral and biodegradable oils

OpenAIRE

Kalin, Mitjan; Vižintin, Jože

2015-01-01

Diamond-like carbon (DLC) coatings, which can nowadays be applied to many highly loaded mechanical components, sometimes need to operate under lubricated conditions. It is reasonable to expect that in steel/DLC contacts, at least the steel counter body will behave according to conventional lubrication mechanisms and will interact with lubricants and additives in the contact. However, in DLC/DLC contacts, such mechanisms are still unclear. For example, the "inertness" of DLC coatings raises se...

Industrial investigations of the liquid steel filtration

Directory of Open Access Journals (Sweden)

K. Janiszewski

2014-07-01

Full Text Available Hitherto existing investigations concerning the ceramic filter use in the steel making processes have given good results. The obtained results of filtration have proved that this method may be used as an effective and cheap way of steel filtration from non-metallic inclusions. Placing filters in the tundish is the best location considering the limitation of the possibility of secondary pollution of steel. Yet, the results presented in this paper, of an experiment prepared and carried out in the industrial environment, are the only positive results obtained, which are connected with so much quantities of liquid steel processed with use of the multi-hole ceramic filters.

Advanced high strength steels for automotive industry

Energy Technology Data Exchange (ETDEWEB)

Galan, J.; Samek, L.; Verleysen, P.; Verbeken, K.; Houbert, Y.

2012-11-01

The car industry is facing pressure because of the growing demand for more fuel-efficient passenger cars. In order to limit energy consumption and air pollution the weight of the car body has to be reduced. At the same time, high levels of safety have to be guaranteed. In this situation, the choice of material becomes a key decision in car design. As a response to the requirements of the automotive sector, high strength steels and advanced high strength steels have been developed by the steel industry. These modern steel grades offer an excellent balance of low cost, light weight and mechanical properties. (Author) 48 refs.

Deformation mechanism maps for pure iron, corrosion resistant austenitic steels and a low-alloy carbon steel

International Nuclear Information System (INIS)

Frost, H.Y.; Ashby, M.F.

1980-01-01

Principles of construction of deformation mechanisms charts for iron base alloys are presented. Deformation mechanisms charts for pure iron, 316 and 314 stainless steels, a ferritic steel with 1% Cr, Mo, V are given, examples of the charts application being provided. The charts construction is based, when it is possible, on the state equations, deduced from theoretical models and satisfying experimental data. The charts presented should be considered as an attempt to unite the main regularities of the theory of dislocations and diffusion with the observed experimental picture of plastic deformation and creep of commercial steels [ru

Dual-phase ULCB steels thermomechanically processed

International Nuclear Information System (INIS)

Lis, A.K.; Lis, J.

2001-01-01

The design philosophy of the processing of dual-phase (D-P) ultra low carbon steels (ULCB) by thermomechanical treatment has been briefly discussed. Modelling of the structure evolution during thermomechanical rolling of ULCB steel was based upon the established empirical equations for yield flow at different conditions of: deformation temperatures, strain rates and stresses for applied amount of deformation during hot deformation compression tests. The critical amount of deformation needed for the occurrence of dynamic or static recrystallization was determined. The dependence of grain refinement of the acicular bainitic and polygonal ferrite of the accelerated cooling and amount of stored energy of deformation in steel has been evaluated. Effect of the decreasing of the finishing temperature of thermomechanical processing on the increase of the impact toughness of dual-phase microstructure consisted of the bainitie-martensite islands in the ferrite matrix has been shown. The effect of ageing process after thermomechanical rolling of heavy plates on fracture toughness values of J 0.2 for ULCB-Ni steels has been established from cod tests measurements. New low cost technology of rolling of ULCB steels dual-phase is proposed. (author)

Nanostructuring steel for injection molding tools

International Nuclear Information System (INIS)

Al-Azawi, A; Smistrup, K; Kristensen, A

2014-01-01

The production of nanostructured plastic items by injection molding with ridges down to 400 nm in width, which is the smallest line width replicated from nanostructured steel shims, is presented. Here we detail a micro-fabrication method where electron beam lithography, nano-imprint lithography and ion beam etching are combined to nanostructure the planar surface of a steel wafer. Injection molded plastic parts with enhanced surface properties, like anti-reflective, superhydrophobic and structural colors can be achieved by micro- and nanostructuring the surface of the steel molds. We investigate the minimum line width that can be realized by our fabrication method and the influence of etching angle on the structure profile during the ion beam etching process. Trenches down to 400 nm in width have been successfully fabricated into a 316 type electro-polished steel wafer. Afterward a plastic replica has been produced by injection molding with good structure transfer fidelity. Thus we have demonstrated that by utilizing well-established fabrication techniques, nanostructured steel shims that are used in injection molding, a technique that allows low cost mass fabrication of plastic items, are produced. (paper)

Stainless steels low temperature nitriding

International Nuclear Information System (INIS)

Roux, T.; Darbeida, A.; Von Stebut, J.; Michel, H.; Lebrun, J.P.; Hertz, D.

1995-01-01

Nitrogen ions implantation of 316L stainless steel leads to monophasic diffusion layers, which are constituted of a solid solution (γ N ) fcc, metastable, nitrogen sur-saturated, and without order. This article shows that for 316L stainless steels,these layers improve the tribological properties without degradation of the corrosion resistance. (A.B.). 13 refs. 6 figs

Irradiation creep in ferritic steels

International Nuclear Information System (INIS)

Vandermeulen, W.; Bremaecker, A. de; Burbure, S. de; Huet, J.J.; Asbroeck, P. van

Pressurized and non-pressurized capsules of several ferritic steels have been irradiated in Rapsodie between 400 and 500 0 C up to 3.7 x 10 22 n/cm 2 (E>0.1 MeV). Results of the diameter measurements are presented and show that the total in-pile deformation is lower than for austenitic steels

Manufacture of Damascus steel: Metallographic study

International Nuclear Information System (INIS)

Criado, A.J.; Martinez, J.A.; Calabres, R.; Arias, D.

1997-01-01

Damascus Steel is the denomination that the Europeans gave to the material with which the musulman swords were manufactured during the Era of the Crusades. This hypereutectoid steel presents a high content in carbon more than 0.8%, and in some cases up to 2% in weight. The secret of its good mechanical characteristics is based in the hot forging process in the temperatures interval between 650 and 850 degree centigree. The final quenching in water brine or other aqueous solutions, confers to the swords manufactured with this steel a good resistance to its cutting edge and a high toughness. In the present investigation, the manufacture processes of this type of steel are studied. Electronic scanning microscopy has been applied to the study of materials manufactured by the authors following the ancient craftsmen methods of forging and quenching. (Author) 16 refs

Superheat effect on bainite steel hardenability

International Nuclear Information System (INIS)

Kubachek, V.V.; Sklyuev, P.V.

1978-01-01

The bainite hardenability of 34KhN1M and 35 KhN1M2Ph steels has been investigated by the end-face hardening technique. It is established that, as the temperature of austenitization rises from 900 to 1280 deg C, the temperature of bainite transformation increases and bainite hardenability of the steels falls off. A repeated slow heating to 900 deg C of previously overheated 34KhN1M steel breaks up grain, lowers the temperature of the bainite transformation and raises the hardenability to values obtained with ordinary hardening from 900 deg C. A similar heating of previously overheated 35KhN1M2Ph steel is accompanied by restoration of initial coarse grains and maintenance of both the elevated bainite transformation temperature and to lower hardenability corresponding to hardening from the temperature of previous overheating

Nanostructuring steel for injection molding tools

DEFF Research Database (Denmark)

Al-Azawi, A.; Smistrup, Kristian; Kristensen, Anders

2014-01-01

The production of nanostructured plastic items by injection molding with ridges down to 400 nm in width, which is the smallest line width replicated from nanostructured steel shims, is presented. Here we detail a micro-fabrication method where electron beam lithography, nano-imprint lithography...... and ion beam etching are combined to nanostructure the planar surface of a steel wafer. Injection molded plastic parts with enhanced surface properties, like anti-reflective, superhydrophobic and structural colors can be achieved by micro-and nanostructuring the surface of the steel molds. We investigate...... the minimum line width that can be realized by our fabrication method and the influence of etching angle on the structure profile during the ion beam etching process. Trenches down to 400 nm in width have been successfully fabricated into a 316 type electro-polished steel wafer. Afterward a plastic replica...

Radiation-induced sensitisation of stainless steels

International Nuclear Information System (INIS)

Norris, D.I.R.

1987-01-01

The book contains the proceedings of a symposium on radiation-induced sensitization of stainless steels, which took place at Berkeley, United Kingdom, 1986. The purpose of the symposium was to examine the mechanism leading to inter-granular corrosion of 20%Cr/25% Ni/Nb stainless steel cladding of AGR fuel following irradiation. Nine papers are presented, of which three are theoretical, two papers are based upon corrosion studies of 20%Cr/25%Ni/Nb steel, and the remaining are concerned with compositional redistribution and its measurement. (U.K.)

Validation of constitutive equations for steel

International Nuclear Information System (INIS)

Valentin, T.; Magain, P.; Quik, M.; Labibes, K.; Albertini, C.

1997-01-01

High strain rate mechanical properties are a major concern for each steel manufacturer, especially with respect to thin sheet steel used in the automotive branch. We began to study this topic by starting a project with the following goals: acquiring reliable experimental data, understanding in depth the energy absorption in thin sheet steel and finding the right constitutive material equation. The first part of the project has been presented in. In this paper we present data computation and comparison with the existing material model theories to exploit the experimental data. (orig.)

The Climate for Steel. Actions for, and conditions to, a Copenhagen climate agreement from the perspective of the EU steel sector

International Nuclear Information System (INIS)

Slingerland, S.; Werring, L.; De Bruijn, S.; Korteland, M.

2009-02-01

A position paper discussing the relationship between climate change policies and competitiveness in the global steel sector. Question is how the need for effective action to confront global climate change can be combined with a level playing field for competition in the global steel sector, taking into account the position of Corus Netherlands as a European steel producer. More specifically; what conditions in an international agreement could provide such a level playing field? Chapter 2 of this paper briefly outlines some essential characteristics of the global and European steel sector. Chapter 3 outlines the present status quo of the multilateral climate change negotiation process towards the December 2009 Copenhagen conference. Chapter 4 gives a view on climate and competitiveness for the EU steel sector. Chapter 5 finally provides conclusions and recommendations for provisions in an international agreement that could provide for a competitive level playing field in the steel sector

Corrosion-resistant coating technique for oxide-dispersion-strengthened ferritic/martensitic steel

International Nuclear Information System (INIS)

Sakasegawa, Hideo; Tanigawa, Hiroyasu; Ando, Masami

2014-01-01

Oxide-dispersion-strengthened (ODS) steels are attractive materials for application as fuel cladding in fast reactors and first-wall material of fusion blanket. Recent studies have focused more on high-chromium ferritic (12-18 wt% Cr) ODS steels with attractive corrosion resistance properties. However, they have poor material workability, require complicated heat treatments for recrystallization, and possess anisotropic microstructures and mechanical properties. On the other hand, low-chromium ferritic/martensitic (8-9 wt% Cr) ODS steels have no such limitations; nonetheless, they have poor corrosion resistance properties. In our work, we developed a corrosion-resistant coating technique for a low-chromium ferritic/martensitic ODS steel. The ODS steel was coated with the 304 or 430 stainless steel, which has better corrosion resistances than the low-chromium ferritic/martensitic ODS steels. The 304 or 430 stainless steel was coated by changing the canning material from mild steel to stainless steel in the conventional material processing procedure for ODS steels. Microstructural observations and micro-hardness tests proved that the stainless steels were successfully coated without causing a deterioration in the mechanical property of the low-chromium ferritic/martensitic ODS steel. (author)

Lung cancer mortality in stainless steel and mild steel welders: a nested case-referent study

DEFF Research Database (Denmark)

Lauritsen, Jens; Hansen, K S

1996-01-01

. Analysis was based on 439 deceased referents and 94 deceased cases. There was a 70% excess of lung cancer associated with "welding exposure ever" (OR +/- 95% C.I.: 1.68, 1.02-2.78). Overall OR for "mild steel (MS) welding ever" was 1.64, 0.99-2.72. The risk estimates for welding exposures showed...... an increasing tendency up to 15 years of exposure. The pattern of stainless steel (SS) welding resembles that of mild steel with an estimated OR of 1.65, 0.88-3.0. The general conclusion is that MS welding as well as SS welding seems to be associated with an increased risk of lung cancer. Further followup...

Plastic deformation and fracture behaviors of nitrogen-alloyed austenitic stainless steels

International Nuclear Information System (INIS)

Wang Songtao; Yang Ke; Shan Yiyin; Li Laifeng

2008-01-01

The plastic deformation and fracture behaviors of two nitrogen-alloyed austenitic stainless steels, 316LN and a high nitrogen steel (Fe-Cr-Mn-0.66% N), were investigated by tensile test and Charpy impact test in a temperature range from 77 to 293 K. The Fe-Cr-Mn-N steel showed ductile-to-brittle transition (DBT) behavior, but not for the 316LN steel. X-ray diffraction (XRD) confirmed that the strain-induced martensite occurred in the 316LN steel, but no such transformation in the Fe-Cr-Mn-N steel. Tensile tests showed that the temperature dependences of the yield strength for the two steels were almost the same. The ultimate tensile strength of the Fe-Cr-Mn-N steel displayed less significant temperature dependence than that of the 316LN steel. The strain-hardening exponent increased for the 316LN steel, but decreased for the Fe-Cr-Mn-N steel, with decreasing temperature. Based on the experimental results and the analyses, a modified scheme was proposed to explain the fracture behaviors of austenitic stainless steels

Recent trend of titanium-clad steel plate/sheet (NKK)

International Nuclear Information System (INIS)

Kimura, Hideto

1997-01-01

The roll-bonding process for titanium-clad steel production enabled the on-line manufacturing and quality control of the products which are usually applied for the production of steel plate and sheet by the steel producers. The recent trend of roll-bonded titanium-clad steel which has an excellent corrosion resistance together with the advantage in cost-saving are mainly described in this article as to the demand, production technique and new application aspects. Though the predominant usage of titanium-clad steel plate has been in power-generating plants, enlargeing utilization in the chemical plants such as terephthalic acid production plants is leading the growth in the market of titanium-clad steel plate. Also, the application of titanium-clad steel plates and sheets for the lining the marine structures is expected as one of the best solution to long-term surface protection for their outstanding corrosion resistance against sea water. (author)

49 CFR 192.55 - Steel pipe.

Science.gov (United States)

2010-10-01

... Other Regulations Relating to Transportation (Continued) PIPELINE AND HAZARDOUS MATERIALS SAFETY ADMINISTRATION, DEPARTMENT OF TRANSPORTATION (CONTINUED) PIPELINE SAFETY TRANSPORTATION OF NATURAL AND OTHER GAS BY PIPELINE: MINIMUM FEDERAL SAFETY STANDARDS Materials § 192.55 Steel pipe. (a) New steel pipe is...

Stainless steel fabrications: past and present

International Nuclear Information System (INIS)

Daniels, R.

1986-01-01

The paper deals with stainless steel fabrications of Fairey Engineering Company for the nuclear industry. The manufacture of stainless steel containers for Magnox and Advanced Gas Cooled Reactors, flexible fabrication facility, and welding development, are all briefly described. (U.K.)

Water corrosion resistance of ODS ferritic-martensitic steel tubes

International Nuclear Information System (INIS)

Narita, Takeshi; Ukai, Shigeharu; Kaito, Takeji; Ohtsuka, Satoshi; Matsuda, Yasuji

2008-01-01

Oxide dispersion strengthened (ODS) ferritic-martensitic steels have superior radiation resistance; it is possible to achieve a service temperature of up to around 973 K because of their superior creep strength. These advantages of ODS steels facilities their application to long-life cladding tubes in advanced fast reactor fuel elements. In addition to neutron radiation resistance, sufficient general corrosion resistance to maintain the strength of the cladding, and the stress corrosion cracking (SCC) resistance for spent-fuel-pool cooling systems and high-temperature oxidation for the fuel-clad chemical interaction (FCCI) of ODS ferritic steel are required. Although the addition of Cr to ODS is effective in preventing water corrosion and high-temperature oxidation, an excessively high amount of Cr leads to embrittlement due to the formation of a Cr-rich α' precipitate. The Cr content in 9Cr-ODS martensite and 12Cr-ODS ferrite, the ODS steels developed by the Japan Atomic Energy Agency (JAEA), is controlled. In a previous paper, it has been demonstrated that the resistances of 9Cr- and 12Cr-ODS ferritic-martensitic steels for high-temperature oxidation are superior to those of conventional 12Cr ferritic steel. However, the water corrosion data of ODS ferritic-martensitic steels are very limited. In this study, a water corrosion test was conducted on ODS steels in consideration of the spent-fuel-pool cooling condition, and the results were compared with those of conventional austenitic stainless steel and ferritic-martensitic stainless steel. (author)

Research and tests of steel-concrete-steel sandwich composite shear wall in reactor containment of HTR-PM

International Nuclear Information System (INIS)

Sun Yunlun; Huang Wen; Zhang Ran; Zhang Pei; Tian Chunyu

2014-01-01

By quasi-static test of 8 specimens of steel-concrete-steel sandwich composite shear wall, the bearing capacity, hysteretic behavior, failure mode of the specimens was studied. So was the effect of the shear-span ratios, steel ratios and spacing of studs on the properties of the specimens. The failure patterns of all specimens with different shear-span ratios between 1.0 and 1.5 were compression-bending failure. The hysteretic curves of all specimens were relatively plump, which validated the well deformability and energy dissipation capacity of the specimens. When shear-span ratio less than 1.5, the shear property of the steel plate was well played, and so was the deformability of the specimens. The bigger the steel ratio was, the better the lateral resistance capacity and the deformability was. Among the spacing of studs in the test, the spacing of studs had no significant effect on the bearing capacity, deformability and ductility of the specimens. Based on the principle of superposition an advised formula for the compression-bending capacity of the shear wall was proposed, which fitted well with the test result and had a proper safety margin. (author)

The Cracking Mechanism of Ferritic-Austenitic Cast Steel

Directory of Open Access Journals (Sweden)

Stradomski G.

2016-12-01

Full Text Available In the high-alloy, ferritic - austenitic (duplex stainless steels high tendency to cracking, mainly hot-is induced by micro segregation processes and change of crystallization mechanism in its final stage. The article is a continuation of the problems presented in earlier papers [1 - 4]. In the range of high temperature cracking appear one mechanism a decohesion - intergranular however, depending on the chemical composition of the steel, various structural factors decide of the occurrence of hot cracking. The low-carbon and low-alloy cast steel casting hot cracking cause are type II sulphide, in high carbon tool cast steel secondary cementite mesh and / or ledeburite segregated at the grain solidified grains boundaries, in the case of Hadfield steel phosphorus - carbide eutectic, which carrier is iron-manganese and low solubility of phosphorus in high manganese matrix. In duplex cast steel the additional factor increasing the risk of cracking it is very “rich” chemical composition and related with it processes of precipitation of many secondary phases.

Study of non-metallic inclusion sources in steel

International Nuclear Information System (INIS)

Khons, Ya.; Mrazek, L.

1976-01-01

A study of potential inclusion sources was carried out at the Tvinec steel plant using an unified labelling procedure for different sources. A lanthanum oxide labelling method has been used for refractories with the subsequent La determination in steel by the neutron activation analysis. Samarium and cerium oxides and the 141 Ce radionuclide have been used in conjunction with the testing. The following sources of exogenous inclusions have been studied: 1)Refractory material comprising fireclay and corundum for steel-teeming trough in open-heart furnaces; 2) Fireclay bottom-pouring refractories; 3) Steel-teeming laddle lining; 4) Heat-insulating and exothermic compounds for steel ingots; 5) Vacuum treatment plant lining; 6) Open-hearth and electric arc furnace slag. The major oxide inclusion source in steel was found to be represented by the furnace slag, since it forms about 40 p.c. of all oxide inclusions. The contributions of the remaining sources did not exceede 5 p.c. each

The interaction between nitride uranium and stainless steel

Science.gov (United States)

Shornikov, D. P.; Nikitin, S. N.; Tarasov, B. A.; Baranov, V. G.; Yurlova, M. S.

2016-04-01

Uranium nitride is most popular nuclear fuel for Fast Breeder Reactor New Generation. In-pile experiments at reactor BOR-60 was shown an interaction between nitride fuel and stainless steel in the range of 8-11% burn up (HA). In order to investigate this interaction has been done diffusion tests of 200 h and has been shown that the reaction occurs in the temperature range 1000-1100 ° C. UN interacted with steel in case of high pollution oxygen (1000-2000 ppm). Also has been shown to increase interaction UN with EP-823 steel in the presence of cesium. In this case the interaction layer had a thickness about 2-3 μm. Has been shown minimal interaction with new ODS steel EP-450. The interaction layer had a thickness less then 2 μm. Did not reveal the influence of tellurium and iodine increased interaction. It was show compatibility at 1000 °C between UN and EP-450 ODS steel, chrome steel, alloying aluminium and silicium.

Microstructure-property relationship in microalloyed high-strength steel welds

International Nuclear Information System (INIS)

Zhang, Lei

2017-01-01

High-strength steels are favoured materials in the industry for production of safe and sustainable structures. The main technology used for joining the components of such steel is fusion welding. Steel alloy design concepts combined with advanced processing technologies have been extensively investigated during the development of High-Strength Low-Alloy (HSLA) steels. However, very few studies have addressed the issue of how various alloy designs, even with limited microalloy addition, can influence the properties of high-strength steel welds. In high-strength steel welding practices, the challenges regarding microstructure evolution and the resulting mechanical properties variation, are of great interest. The main focus is the debate regarding the role of microalloy elements on phase transformation and weld performance. Limited Heat Affected Zone (HAZ) softening and limited austenite grain coarsening are significant design essentials, but the primary goal is to ensure excellent toughness and tensile properties in the steel weld. To achieve this purpose, microalloy elements such as Ti, Nb, or V were intentionally added to modern high-strength steels. The focus of this work was to understand the mechanical properties of HSLA steels resulting from differences in alloy design after joining by modern welding processes. To begin, three microalloyed S690QL steels (Nb, Ti, and Ti+V addition) were investigated. Optical microscopy confirmed that similar mixtures of tempered bainite and martensite predominated the parent microstructure in the three steels, different types of coarse microalloy precipitates were also visible. These precipitates were analysed by using a thermodynamic-based software and then identified by Transmission Electron Microscopy (TEM). Results of mechanical testing revealed that all three steels performed above the standard toughness and tensile strength values, but with varied yielding phenomena. During the welding operation, each of the three steels

Microstructure-property relationship in microalloyed high-strength steel welds

Energy Technology Data Exchange (ETDEWEB)

Zhang, Lei

2017-04-01

High-strength steels are favoured materials in the industry for production of safe and sustainable structures. The main technology used for joining the components of such steel is fusion welding. Steel alloy design concepts combined with advanced processing technologies have been extensively investigated during the development of High-Strength Low-Alloy (HSLA) steels. However, very few studies have addressed the issue of how various alloy designs, even with limited microalloy addition, can influence the properties of high-strength steel welds. In high-strength steel welding practices, the challenges regarding microstructure evolution and the resulting mechanical properties variation, are of great interest. The main focus is the debate regarding the role of microalloy elements on phase transformation and weld performance. Limited Heat Affected Zone (HAZ) softening and limited austenite grain coarsening are significant design essentials, but the primary goal is to ensure excellent toughness and tensile properties in the steel weld. To achieve this purpose, microalloy elements such as Ti, Nb, or V were intentionally added to modern high-strength steels. The focus of this work was to understand the mechanical properties of HSLA steels resulting from differences in alloy design after joining by modern welding processes. To begin, three microalloyed S690QL steels (Nb, Ti, and Ti+V addition) were investigated. Optical microscopy confirmed that similar mixtures of tempered bainite and martensite predominated the parent microstructure in the three steels, different types of coarse microalloy precipitates were also visible. These precipitates were analysed by using a thermodynamic-based software and then identified by Transmission Electron Microscopy (TEM). Results of mechanical testing revealed that all three steels performed above the standard toughness and tensile strength values, but with varied yielding phenomena. During the welding operation, each of the three steels

Initiation and growth of thermal fatigue crack networks in an AISI 304 L type austenitic stainless steel (X2 CrNi18-09); Amorcage et propagation de reseaux de fissures de fatigue thermique dans un acier inoxydable austenitique de type X2 CrNi18-09 (AISI 304 L)

Energy Technology Data Exchange (ETDEWEB)

Maillot, V

2004-07-01

We studied the behaviour of a 304 L type austenitic stainless steel submitted to thermal fatigue. Using the SPLASH equipment of CEA/SRMA we tested parallelepipedal specimens on two sides: the specimens are continuously heated by Joule effect, while two opposites faces are cyclically. cooled by a mixed spray of distilled water and compressed air. This device allows the reproduction and the study of crack networks similar to those observed in nuclear power plants, on the inner side of circuits fatigued by mixed pressurized water flows at different temperatures. The crack initiation and the network constitution at the surface were observed under different thermal conditions (Tmax = 320 deg C, {delta}T between 125 and 200 deg C). The experiment produced a stress gradient in the specimen, and due to this gradient, the in-depth growth of the cracks finally stopped. The obtained crack networks were studied quantitatively by image analysis, and different parameters were studied: at the surface during the cycling, and post mortem by step-by-step layer removal by grinding. The maximal depth obtained experimentally, 2.5 mm, is relatively coherent with the finite element modelling of the SPLASH test, in which compressive stresses appear at a depth of 2 mm. Some of the crack networks obtained by thermal fatigue were also tested in isothermal fatigue crack growth under 4-point bending, at imposed load. The mechanisms of the crack selection, and the appearance of the dominating crack are described. Compared to the propagation of a single crack, the crack networks delay the propagation, depending on the severity of the crack competition for domination. The dominating crack can be at the network periphery, in that case it is not as shielded by its neighbours as a crack located in the center of the network. It can also be a straight crack surrounded by more sinuous neighbours. Indeed, on sinuous cracks, the loading is not the same all along the crack path, leading to some

Corrosion of steels in sour gas environments

International Nuclear Information System (INIS)

Twigg, R.J.

1984-03-01

This report presents a study on the effects of sour gas environments on steels. Emphasis is placed on alloys commonly used in the heavy water, sour gas and refining industries. In addition, 'high strength, low alloy' steels, known as 'oil country tubular goods', are included. Reference is made to the effects of hydrogen sulphide environments on austenitic steels and on certain specialty steels. Theories of hydrogen-related cracking mechanisms are outlined with emphasis placed on sulphide stress cracking and hydrogen induced cracking in carbon and low alloy steels. Methods of controlling sulphide stress cracking and hydrogen induced cracking are addressed separately. Case histories from the heavy water, refining, and sour gas industries are used to illustrate operating experience and failure mechanisms. Finally, recommendations, based largely on the author's industrial experience, are made with respect to quality assurance and inspection requirements for sour service components. Only published literature was surveyed. Abstracts were made of all references, reviewing the major sources in detail

Low-temperature creep of austenitic stainless steels

Science.gov (United States)

Reed, R. P.; Walsh, R. P.

2017-09-01

Plastic deformation under constant load (creep) in austenitic stainless steels has been measured at temperatures ranging from 4 K to room temperature. Low-temperature creep data taken from past and unreported austenitic stainless steel studies are analyzed and reviewed. Creep at cryogenic temperatures of common austenitic steels, such as AISI 304, 310 316, and nitrogen-strengthened steels, such as 304HN and 3116LN, are included. Analyses suggests that logarithmic creep (creep strain dependent on the log of test time) best describe austenitic stainless steel behavior in the secondary creep stage and that the slope of creep strain versus log time is dependent on the applied stress/yield strength ratio. The role of cold work, strain-induced martensitic transformations, and stacking fault energy on low-temperature creep behavior is discussed. The engineering significance of creep on cryogenic structures is discussed in terms of the total creep strain under constant load over their operational lifetime at allowable stress levels.

Design Solutions for Sustainable Construction of Pre Engineered Steel Buildings

Directory of Open Access Journals (Sweden)

Muhammad Umair Saleem

2018-05-01

Full Text Available Sustainable construction of ecofriendly infrastructure has been the priority of worldwide researchers. The induction of modern technology in the steel manufacturing industry has enabled designers to get the desired control over the steel section shapes and profiles resulting in efficient use of construction material and manufacturing energy required to produce these materials. The current research study is focused on the optimization of steel building costs with the use of pre-engineered building construction technology. Construction of conventional steel buildings (CSB incorporates the use of hot rolled sections, which have uniform cross-section throughout the length. However, pre-engineered steel buildings (PEB utilize steel sections, which are tailored and profiled based on the required loading effects. In this research study, the performance of PEB steel frames in terms of optimum use of steel sections and its comparison with the conventional steel building is presented in detail. A series of PEB and CSB steel frames is selected and subjected to various loading conditions. Frames were analyzed using Finite Element Based analysis tool and design was performed using American Institute of Steel Construction design specifications. Comparison of the frames has been established in terms of frame weights, lateral displacements (sway and vertical displacements (deflection of the frames. The results have clearly indicated that PEB steel frames are not only the most economical solution due to lesser weight of construction but also have shown better performance compared to CSB frames.

Consequences of Globalisation for the Belgian Steel Industry

OpenAIRE

DE GROOTE, Patrick

2008-01-01

Since a few years the worldwide steel industry has been under the spell of a great consolidation wave and enhanced competition. 2006 was a peak year with the merger of the European group Arcellor Mittal Steel to ArcellorMittal. With this merger, ArcellorMittal became the greatest steel group in the world with a market share of more than 10%. Thanks to the consolidation trend, the steel industry has changed from an obsolete and loss-making industry to a modern, attractive and profitable busine...

Stainless steel in contact with food and bevarage

Directory of Open Access Journals (Sweden)

Sveto Cvetkovski

2012-12-01

Full Text Available Stainless steels are probably the most important materials in the food and beverage industries. The main reason for such broad implementation of stainless steel in contact with food are excellent properties which they possess such as corrosion resistance, resistance to high and low temperatures, very good mechanical and physical properties, aesthetic appeal, inertness of surface, durability, easy cleaning and recycling. Low thermal conductivity of these steels produces steeper temperature coefficient provoking an increased distortion, shrinkage and stresses compared with carbon steel.

Charpy impact behavior of manganese-stabilized martensitic steels

International Nuclear Information System (INIS)

Hu, W.L.; Gelles, D.S.

1986-05-01

Tests were conducted to evaluate the irradiation-induced shift in ductile-to-brittle transition behavior of two manganese stabilized martensitic steels. Miniature Charpy specimens were fabricated from two heats of steel similar in composition to HT-9 but with 0.1% C and Mn contents ranging from 3.3 to 6.6.%. The 3.3% Mn steel showed a transition temperature similar to that of HT-9 in both the unirradiated condition and in specimens irradiated to 11.3 dpa. The steel containing 6.6% Mn exhibited a higher transition temperature after irradiation than the steel containing 3.3% Mn. The upper shelf energy (USE) after irradiation for the manganese stabilized alloys was much higher than for HT-9. 6 refs., 3 figs., 2 tabs

Tantalum-containing Z-phase in 12%Cr martensitic steels

DEFF Research Database (Denmark)

Danielsen, Hilmar Kjartansson; Hald, John

2009-01-01

Z-phases in tantalum-containing 12%Cr steels have been investigated. In 12%Cr steel without any Nb or V, the formation of CrTaN Z-phases was observed. In 12%Cr steel which also contained V, the Ta entered Z-phase as a minor element, Cr(V,Ta)N. The crystal structure of Cr(V,Ta)N seems to be identi......Z-phases in tantalum-containing 12%Cr steels have been investigated. In 12%Cr steel without any Nb or V, the formation of CrTaN Z-phases was observed. In 12%Cr steel which also contained V, the Ta entered Z-phase as a minor element, Cr(V,Ta)N. The crystal structure of Cr(V,Ta)N seems...

Corrosion behavior of Al-Fe-sputtering-coated steel, high chromium steels, refractory metals and ceramics in high temperature Pb-Bi

International Nuclear Information System (INIS)

Abu Khalid, Rivai; Minoru, Takahashi

2007-01-01

Corrosion tests of Al-Fe-coated steel, high chromium steels, refractory metals and ceramics were carried out in high temperature Pb-Bi at 700 C degrees. Oxygen concentrations in this experiment were 6.8*10 -7 wt.% for Al-Fe-coated steels and 5*10 -6 wt.% for high chromium steels, refractory metals and ceramics. All specimens were immersed in molten Pb-Bi in a corrosion test pot for 1.000 hours. Coating was done with using the unbalanced magnetron sputtering (UBMS) technique to protect the steel from corrosion. Sputtering targets were Al and SUS-304. Al-Fe alloy was coated on STBA26 samples. The Al-Fe alloy-coated layer could be a good protection layer on the surface of steel. The whole of the Al-Fe-coated layer still remained on the base surface of specimen. No penetration of Pb-Bi into this layer and the matrix of the specimen. For high chromium steels i.e. SUS430 and Recloy10, the oxide layer formed in the early time could not prevent the penetration of Pb-Bi into the base of the steels. Refractory metals of tungsten (W) and molybdenum (Mo) had high corrosion resistance with no penetration of Pb-Bi into their matrix. Penetration of Pb-Bi into the matrix of niobium (Nb) was observed. Ceramic materials were SiC and Ti 3 SiC 2 . The ceramic materials of SiC and Ti 3 SiC 2 had high corrosion resistance with no penetration of Pb-Bi into their matrix. (authors)

Tensile property improvement of TWIP-cored three-layer steel sheets fabricated by hot-roll-bonding with low-carbon steel or interstitial-free steel

Science.gov (United States)

Park, Jaeyeong; Kim, Jung-Su; Kang, Minju; Sohn, Seok Su; Cho, Won Tae; Kim, Hyoung Seop; Lee, Sunghak

2017-01-01

TWIP-cored three-layer steel sheets were newly fabricated by hot rolling of TWIP steel sheet surrounded by low-carbon (LC) or interstitial-free (IF) steel sheets. TWIP/LC or TWIP/IF interfaces were well bonded without pores or voids, while a few pearlites were thinly formed along the interfaces. The strengths and elongation of the TWIP-cored sheets increased as the volume fraction of TWIP-cored region increased, and were also well matched with the ones calculated by a rule of mixtures based on volume fraction or force fraction. According to digital image correlation and electron back-scatter diffraction analyses, very high strain hardening effect in the initial deformation stage and active twin formation in the interfacial region beneficially affected the overall homogeneous deformation in the TWIP-cored sheets without any yield point phenomenon occurring in the LC sheet and serrations occurring in the TWIP sheet, respectively. These TWIP-cored sheets can cover a wide range of yield strength, tensile strength, and ductility levels, e.g., 320~498 MPa, 545~878 MPa, and 48~54%, respectively, by controlling the volume fraction of TWIP-cored region, and thus present new applications to multi-functional automotive steel sheets requiring excellent properties.

Reaction of uranium and plutonium carbides with austenitic steels

International Nuclear Information System (INIS)

Mouchnino, M.

1967-01-01

The reaction of uranium and plutonium carbides with austenitic steels has been studied between 650 and 1050 deg. C using UC, steel and (UPu)C, steel diffusion couples. The steels are of the type CN 18.10 with or without addition of molybdenum. The carbides used are hyper-stoichiometric. Tests were also carried out with UCTi, UCMo, UPuCTi and UPuCMo. Up to 800 deg. C no marked diffusion of carbon into stainless steel is observed. Between 800 and 900 deg. C the carbon produced by the decomposition of the higher carbides diffuses into the steel. Above 900 deg. C, decomposition of the monocarbide occurs according to a reaction which can be written schematically as: (U,PuC) + (Fe,Ni,Cr) → (U,Pu) Fe 2 + Cr 23 C 6 . Above 950 deg. C the behaviour of UPuCMo and that of the titanium (CN 18.12) and nickel (NC 38. 18) steels is observed to be very satisfactory. (author) [fr

Compatibility tests of steels in flowing liquid lead-bismuth

International Nuclear Information System (INIS)

Barbier, F.; Benamati, G.; Fazio, C.; Rusanov, A.

2001-01-01

The behaviour of steels exposed to flowing Pb-55Bi was evaluated. The materials tested are the two austenitic steels AISI 316L and 1.4970, and the six martensitic steels Optifer IVc, T91, Batman 27, Batman 28, EP823 and EM10 which were exposed to flowing Pb-55Bi for 1000, 2000 and 3000 h and at two temperatures (573 and 743 K). The corrosion tests were conducted in the non-isothermal loop of IPPE-Obninsk under a controlled oxygen level (10 -6 wt%). The compatibility study showed that at a lower temperature, a very thin oxide layer (<1 μm) was formed on the steels. At higher temperature, austenitic steels also exhibited a thin oxide layer sufficient to prevent their dissolution in the melt. A thicker oxide, which grew according to a parabolic law, was observed on the surface of the martensitic steels. The oxidation resistance behaviour of the martensitic steels was correlated with their alloying elements

CHARACTERIZATION OF NEW TOOL STEEL FOR ALUMINUM EXTRUSION DIES

Directory of Open Access Journals (Sweden)

José Britti Bacalhau

2014-06-01

Full Text Available Aluminum extrusion dies are an important segment of application on industrial tools steels, which are manufactured in steels based on AISI H13 steel. The main properties of steels applied to extrusion dies are: wear resistance, impact resistance and tempering resistance. The present work discusses the characteristics of a newly developed hot work steel to be used on aluminum extrusion dies. The effects of Cr and Mo contents with respect to tempering resistance and the Al addition on the nitriding response have been evaluated. From forged steel bars, Charpy impact test and characterization via EPMA have been conducted. The proposed contents of Cr, Mo, and Al have attributed to the new VEX grade a much better tempering resistance than H13, as well as a deeper and harder nitrided layer. Due to the unique characteristics, this new steel provides an interesting alternative to the aluminum extrusion companies to increase their competitiveness.

Corrosion resistance testing of high-boron-content stainless steels

International Nuclear Information System (INIS)

Petrman, I.; Safek, V.

1994-01-01

Boron steels, i.e. stainless steels with boron contents of 0.2 to 2.25 wt.%, are employed in nuclear engineering for the manufacture of baskets or wells in which radioactive fissile materials are stored, mostly spent nuclear fuel elements. The resistance of such steels to intergranular corrosion and uniform corrosion was examined in the Strauss solution and in boric acid; the dependence of the corrosion rate of the steels on their chemical composition was investigated, and their resistance was compared with that of AISI 304 type steel. Corrosion resistance tests in actual conditions of ''wet'' compact storage (demineralized water or a weak boric acid solution) gave evidence that boron steels undergo nearly no uniform corrosion and, as electrochemical measurements indicated, match standard corrosion-resistant steels. Corrosion resistance was confirmed to decrease slightly with increasing boron content and to increase somewhat with increasing molybdenum content. (Z.S.). 3 tabs., 4 figs., 7 refs

Engineering Performance of High Strength Concrete Containing Steel Fibre Reinforcement

Directory of Open Access Journals (Sweden)

Md Azree Othuman Mydin

2013-09-01

Full Text Available The development and utilization of the high strength concrete in the construction industry have been increasing rapidly. Fiber reinforced concrete is introduced to overcome the weakness of the conventional concrete because concrete normally can crack under a low tensile force and it is known to be brittle. Steel fibre is proved to be the popular and best combination in the high strength concrete to result the best in the mechanical and durability properties of high strength concrete with consideration of curing time, steel fibre geometry, concrete grade and else more. The incorporation of steel fibre in the mortar mixture is known as steel fibre reinforced concrete have the potential to produce improvement in the workability, strength, ductility and the deformation of high strength concrete. Besides that, steel fibre also increases the tensile strength of concrete and improves the mechanical properties of the steel fibre reinforced concrete. The range for any high strength concrete is between 60MPa-100MPa. Steel fibre reinforced concrete which contains straight fibres has poorer physical properties than that containing hooked end stainless steel fibre due to the length and the hooked steel fibre provide a better effective aspects ratio. Normally, steel fibre tensile strength is in the range of 1100MPa-1700MPa. Addition of less steel fibre volumes in the range of 0.5% to 1.0% can produce better increase in the flexural fatigue strength. The strength can be increased with addition of steel fibre up to certain percentage. This paper will review and present some basic properties of steel fibre reinforced concrete such as mechanical, workability and durability properties.

Experimental and numerical simulation of carbon manganese steel ...

African Journals Online (AJOL)

Experimental and numerical simulation of carbon manganese steel for cyclic plastic behaviour. J Shit, S Dhar, S Acharyya. Abstract. The paper deals with finite element modeling of saturated low cycle fatigue and the cyclic hardening phenomena of the materials Sa333 grade 6 carbon steel and SS316 stainless steel.

Crack stability analysis of low alloy steel primary coolant pipe

Energy Technology Data Exchange (ETDEWEB)

Tanaka, T.; Kameyama, M. [Kansai Electric Power Company, Osaka (Japan); Urabe, Y. [Mitsubishi Heavy Industries, Ltd., Takasago (Japan)] [and others

1997-04-01

At present, cast duplex stainless steel has been used for the primary coolant piping of PWRs in Japan and joints of dissimilar material have been applied for welding to reactor vessels and steam generators. For the primary coolant piping of the next APWR plants, application of low alloy steel that results in designing main loops with the same material is being studied. It means that there is no need to weld low alloy steel with stainless steel and that makes it possible to reduce the welding length. Attenuation of Ultra Sonic Wave Intensity is lower for low alloy steel than for stainless steel and they have advantageous inspection characteristics. In addition to that, the thermal expansion rate is smaller for low alloy steel than for stainless steel. In consideration of the above features of low alloy steel, the overall reliability of primary coolant piping is expected to be improved. Therefore, for the evaluation of crack stability of low alloy steel piping to be applied for primary loops, elastic-plastic future mechanics analysis was performed by means of a three-dimensioned FEM. The evaluation results for the low alloy steel pipings show that cracks will not grow into unstable fractures under maximum design load conditions, even when such a circumferential crack is assumed to be 6 times the size of the wall thickness.

Tensile behavior of borated stainless steels

International Nuclear Information System (INIS)

Stephens, J.J. Jr.; Sorenson, K.B.

1991-01-01

Borated stainless steel tensile testing is being conducted at Sandia National Laboratories (SNL). The goal of the test program is to provide data to support a code case inquiry to the ASME Boiler and Pressure Vessel Code, Section III. The adoption by ASME facilitates a material's qualification for structural use in transport cask applications. For transport cask basket applications, the potential advantage to using borated stainless steel arises from the fact that the structural and criticality control functions can be combined into one material. This can result in a decrease in net section thickness of the basket web (increased payload capacity) and eliminates the fabrication process and cost of attaching a discrete boron poison material to the basket web. In addition, adding borate stainless steel to the inventory of acceptable structural material provides the Department of Energy (DOE) and its cask contractors an alternative to current proposed materials which have not been qualified for structural service. The test program at SNL involves procuring material, machining test specimens, and conducting the tensile tests. From test measurements obtained so far, general trends indicate that tensile properties (yield strength and ultimate strength) increase with boron content and are in all cases superior to the minimum required properties established in A-240, Type 304, a typical grade of austenitic stainless steel. Therefore, in a designed basket, web thicknesses using borated stainless steel would be comparable to or thinner tan an equivalent basket manufactured from a typical stainless steel without boron additions. General trends from test results indicate that ductilities decrease with increasing boron content

Development of low-chromium, chromium-tungsten steels for fusion

International Nuclear Information System (INIS)

Klueh, R.L.; Alexander, D.J.; Kenik, E.A.

1995-01-01

High-chromium (9-12% Cr) Cr-Mo and Cr-W ferritic steels are favored as candidates for fusion applications. In early work to develop reduced-activation steels, an Fe-2.25Cr-2W-0.25V-0.1C steel (designated 2.25Cr-2WV) had better strength than an Fe-9Cr-2W-0.25V-0.07Ta-0.1C (9Cr-2WVTa) steel (compositions are in weight percent). However, the 2.25Cr-2WV had poor impact properties, as determined by the ductile-brittle transition temperature and upper-shelf energy of subsize Charpy impact specimens. Because low-chromium steels have some advantages over high-chromium steels, a program to develop low-chromium steels is in progress. Microstructural analysis indicated that the reason for the inferior impact toughness of the 2.25Cr-2WV was the granular bainite obtained when the steel was normalized. Properties can be improved by developing an acicular bainite microstructure by increasing the cooling rate after austenitization. Alternatively, acicular bainite can be promoted by increasing the hardenability. Hardenability was changed by adding small amounts of boron and additional chromium to the 2.25Cr-2WV composition. A combination of B, Cr, and Ta additions resulted in low-chromium reduced-activation steels with mechanical properties comparable to those of 9Cr-2WVTa. (orig.)

Erosion behaviour of hydro turbine steels

Indian Academy of Sciences (India)

WINTEC

creases grain size hardening (Ikegami and Nemoto 1996). Nitrogen solubility ... 116. Table 1. Chemical composition of 13/4 martensitic and 21–4–N nitronic steel (wt %). Steel. C. Si Mn. Cr. Ni. N. S ..... In Fe–Cr–Ni alloys, Schramm and Reed ...

Problems in development of pressure vessel steels

International Nuclear Information System (INIS)

McMahon, C.Y.

1980-01-01

The tendency of steels to intercrystalline fracture at low stresses is the main factor, limiting fracture resistance of steels in agressive media at conventional and elevated temperatures. The reasons for the phenomenon are analyzed. In particular, the role of grain boundary segregations of non-metallic impurities is pointed out. The ways of the problem solving both at the expense of corresponding microstructure control and by means of selection of the steel chemical composition are considered

Properties of Mo-alloyed sintered manganese steels

International Nuclear Information System (INIS)

Romanski, A.; Cias, A.

1998-01-01

Sintered alloy steels are needed for mostly PM structural parts. Powder metallurgy techniques provide a means of fabricating high quality steel parts with tailored mechanical properties. It is now possible to produce sintered steel parts with properties equal to an even superior to those of parts made by more traditional routes. Challenges arise both with the material selection and component fabrication. This work outlines the processing for high performance structural application. (author)

Experimental investigations on steel-concrete composite columns for varying parameters

Science.gov (United States)

Aparna, V.; Vivek, D.; Neelima, Kancharla; Karthikeyan, B.

2017-07-01

In this study, the experimental investigations on steel tubes filled with different types of concrete are presented. Steel tubes filled with fibre reinforced concrete using lathe waste and steel tube with concerned confined with steel mesh were investigated. The combinations were compared with steel tubes with conventional concrete. A total of 4 concrete filled steel tube (CFST) combinations were made with tubes of diameter 100 mm with wall thickness 1.6 mm and a height of 300 mm. Axial compression test to examine the resisting capacity of the columns and push-out test for noting the bond strength were performed. Coupon tests were also conducted to determine the mechanical properties of steel. The structural behaviour of the composite columns was evaluated from on the test results. It was observed that steel tube filled fibre reinforced possessed better bond strength and resistance to axial load.

Tritiated Water Interaction with Stainless Steel

International Nuclear Information System (INIS)

Glen R. Longhurst

2007-01-01

Experiments conducted to study tritium permeation of stainless steel at ambient and elevated temperatures revealed that HT converts relatively quickly to HTO. Further, the HTO partial pressure contributes essentially equally with elemental tritium gas in driving permeation through the stainless steel. Such permeation appears to be due to dissociation of the water molecule on the hot stainless steel surface. There is an equilibrium concentration of HTO vapor above adsorbed gas on the walls of the experimental apparatus evident from freezing transients. The uptake process of tritium from the carrier gas involves both surface adsorption and isotopic exchange with surface bound water

Quenching simulation of steel grinding balls

Energy Technology Data Exchange (ETDEWEB)

Zapata-Hernandez, O.; Reyes, L. A.; Camurri, C.; Carrasco, C.; Garza-Monte-de-Oca, F.; Colas, R.

2015-07-01

The phase transformations of high carbon steel during quenching and equalizing were modelled using commercial computer packages based on the finite element method and the kinetic transformation of steel. The model was used to predict the temperature and microstructural changes taking place within balls of two different sizes that are used for grinding mineral ores. A good correlation between the temperatures measured by inserted thermocouples and those predicted by the model was obtained after modifying the thermal conductivity of the steel within the temperature domain at which mixed phases are present. The phase transformations predicted were confirmed by metallographic analyses. (Author)

Dynamic characteristics of automotive steel sheets

Directory of Open Access Journals (Sweden)

M. Mihaliková

2016-10-01

Full Text Available The aim of this experimental research was to perform an analysis of deformation characteristics on two different types of steel: IF steel, and micro-alloyed steel were used automotive industry. For that purpose changes of properties of these materials were carried out by static 10-3 · s-1 and dynamic 103 · s-1 strain rate assess its plastic properties. Vickers micro hardness test was carried out by the static and dynamic loading condition and describes different hardness distribution. The higher strain hardening of materials was obtained too that was confirmed by distribution of dislocations.

Hydrogen transport in iron and steel

International Nuclear Information System (INIS)

Louthan, M.R. Jr.; Derrick, R.G.; Donovan, J.A.; Caskey, G.R. Jr.

1975-01-01

The permeabilities of protium, deuterium, and tritium in iron and T-1 steel at temperatures as low as 260 0 K are in agreement with the equation proposed by Gonzalez. However, the permeabilities of HP-9-4-20 and 4130 steel to hydrogen are typically lower than predicted. The present data also show that, within experimental accuracy, the isotope effect on the permeability of hydrogen in HP-9-4-20, 4130 and T-1 steel, and high purity iron can be estimated by an inverse square root of mass correction. Trapping effects prevent the development of diffusivity and solubility equations. (auth)

Problems in steel industry for power engineering

International Nuclear Information System (INIS)

Dolbenko, E.T.; Kryanin, I.R.

1979-01-01

The main problems of steel industry in power engineering are considered. The effect of charge materials upon steel quality is analyzed. Radical dicision of the problem is the ensurance of power engineering plants with high quality original charge materials, which are quite pure according to impurities such as: iron melted from metallized charge or prereduced pellets. The usage of such materials considerably improves the complex of technological and service properties and structure of large responsible products: vessels of the reactor core, especially large shafts and others. For the most responsible power engineering dies it is necessary to smelt steel of 150-200 tons and above. The main direction of steel melting industry is quality steel melting in large 150-200 tons arc furnaces which are equipped with magnetic stirrer installations. It is marked that the branch of power engineering is equipped with unique installations of out-of-furnace steel refining. It is shown that further increase in the metal quality is possible when vacuum and electroslag technique of melting is used. It permits to reduce considerably the amount of sulphur, gases, nonmetallic inclusions, to increase the metal density, to remove zonal segregation in large steel ingots. The main problem in the field of usage of material, produced by new melting methods is the expansion of the product nomenclature and the development of technical conditions, reflecting the increase in material properties as a result of new technique application. Importance of development and introduction of new automation and testing methods in metallurgical processes is marked

Nuclear energy and the steel industry

International Nuclear Information System (INIS)

Barnes, R.S.

1977-01-01

Fossil fuels represent a large part of the cost of iron and steel making and their increasing cost has stimulated investigation of methods to reduce the use of fossil fuels in the steel industry. Various iron and steel making routes have been studied by the European Nuclear Steelmaking Club (ENSEC) and others to determine to what extent they could use energy derived from a nuclear reactor to reduce the amount of fossil fuel consumed. The most promising concept is a High-Temperature Gas-Cooled Nuclear Reactor heating helium to a temperature sufficient to steam reform hydrocarbons into reducing gases for the direct reduction of iron ores. It is proposed that the reactor/reformer complex should be separate from the direct-reduction plant/steelworks and should provide reducing gas by pipeline, not only to a number of steel works but to other industrial users. The composition of suitable reducing gases and the methods of producing them from various feedstocks are discussed. Highly industrialised countries with large steel and chemical industries have shown greatest interest in the concept, but those countries with large iron-ore reserves and growing direct capacity should consider the future value of the High-Temperature Gas-Cooled Reactor as a means of extending the life of their gas reserves. (author)

Joining uranium to steel

International Nuclear Information System (INIS)

Perkins, M.A.

1976-05-01

A method has been devised which will allow the joining of uranium to steel by fusion welding through the use of an intermediate material. Uranium-0.5 titanium was joined to AISI 304L stainless steel by using a vanadium insert. Also, a method is now available for selecting possible filler metals when two entirely dissimilar metals need to be joined. This method allows a quantitative ranking to be made of the possible filler metals and thus the most likely candidate can be selected

Influence of titanium on the tempering structure of austenitic steels

International Nuclear Information System (INIS)

Ghuezaiel, M.J.

1985-10-01

The microstructure of titanium-stabilized and initially deformed (approximately 20%) austenitic stainless steels used in structures of fast neutrons reactors has been studied after one hour duration annealings (500 0 C) by X-ray diffraction, optical microscopy, microhardness and transmission electron microscopy. The studied alloys were either of industrial type CND 17-13 (0.23 to 0.45 wt% Ti) or pure steels (18% Cr, 14% Ni, 0 or 0.3 wt% Ti). During tempering, the pure steels presented some restauration before recristallization. In the industrial steels, only recristallization occurred, and this only in the most deformed steel. Precipitation does not occur in the titanium-free pure steel. In industrial steels, many intermetallic phases are formed when recristallization starts [fr

Stainless steels: general considerations and rates of crack growth

International Nuclear Information System (INIS)

Chator, T.

1992-05-01

This report describes the different types of stainless steels, and presents the laws governing the rates of crack growth for several stainless steels extensively used for the manufacture of structures in nuclear power plants. The laws are not discussed in detail in the report. After a brief review of the development of stainless steels, the main categories of stainless steels, their mechanical characteristics and corrosion resistance, are presented. Finally, the rates of crack growth are presented for various stainless steels, mainly austenitic. The study overall aim is an investigation of the cracking in the 900 MWe primary pump thermal barriers and shafts

Three-Sheet Spot Welding of Advanced High-Strength Steels

DEFF Research Database (Denmark)

Nielsen, Chris Valentin; Friis, Kasper Storgaard; Zhang, W.

2011-01-01

The automotive industry has introduced the three-layer weld configuration, which represents new challenges compared to normal two-sheet lap welds. The process is further complicated by introducing high-strength steels in the joint. The present article investigates the weldability of thin, low....... The weld mechanisms are analyzed numerically and compared with metallographic analyses showing how the primary bonding mechanism between the thin, low-carbon steel sheet and the thicker sheet of high-strength steel is solid-state bonding, whereas the two high-strength steels are joined by melting, forming...... a weld nugget at their mutual interface. Despite the absence of the typical fusion nugget through the interface between the low-carbon steel and high-strength steel, the weld strengths obtained are acceptable. The failure mechanism in destructive testing is ductile fracture with plug failure....

Properties of 40N3M powder structural steel

International Nuclear Information System (INIS)

Moskvina, T.P.; Gulyaev, A.P.; Gulyaev, I.A.; Byakov, S.V.; Melent'ev, I.V.; Morgun, G.N.

1984-01-01

Effect of the fabrication technique of compact slabs made of the 40N3M powder structural steel on mechanical properties with determination of a cold brittleness threshold was studied. It is established that after a thermal treatment at a density close to 100% a powder steel is sufficiently close to steel, rolled of an ingot, but is second in reference to steel in its ductility and impact strength. Properties of powder steel obtained by the method of dynamic hot forming (DHF) and hot extrusion are practically equal, but the first method has definite advantages as it allows to obtain details with a definitive form. The above investigation permits to recommend an application of the 40N3M powder steel fabricated by the DHF methods. The optimum thermal treatment course is: quenching+high annealing

Behavior of the elements in the mechanically alloyed and cast ferritic steels and a type 316 stainless steel in a flowing sodium environment

International Nuclear Information System (INIS)

Suzuki, T.; Mutoh, I.

1988-01-01

Sodium corrosion behavior of a mechanically alloyed ferritic steel, dispersion-strengthened with addition of Y 2 0 3 and Ti, two kinds of melted/cast ferritic steels and a Type 316 stainless steel was examined by using a non-isothermal sodium loop system, constructed of another Type 316 stainless steel, with a direct resistance electrical heater. The sodium conditions were 675 0 C, 4.0 m/s in velocity and 1-2 ppm oxygen concentration and a cumulative exposure time of the specimens was about 3000 h. The absorption of Ni and selective dissolution of Cr played an important role in the corrosion of the mechanically alloyed ferritic steel as in the case of the cast ferritic steels. However, the region of Ni absorption and Cr diminution was deeper than that of the cast ferritic steels. Peculiar finding for the mechanically alloyed ferritic steel was the corroded surface with irregularly shaped protuberance, that might be related with formation of sodium titanate, and the absorption of carbon and nitrogen to form carbide and nitride of titanium. It seems that these facts resulted in the irregular weight loss of the specimens, which depended on the downstream position and the cumulative exposure time. However, the tensile properties of the mechanically alloyed ferritic steel did not noticeably change by the sodium exposure

Low temperature gaseous surface hardening of stainless steel

DEFF Research Database (Denmark)

Christiansen, Thomas; Somers, Marcel A. J.

2010-01-01

The present contribution gives an overview of some of the technological aspects of low temperature thermochemical treatment of stainless steel. Examples of low temperature gaseous nitriding, carburising and nitrocarburising of stainless steel are presented and discussed. In particular......, the morphology, microstructure and characteristics of so-called expanite “layers” on stainless steel are addressed....

Corrosion behavior of sensitized duplex stainless steel.

Science.gov (United States)

Torres, F J; Panyayong, W; Rogers, W; Velasquez-Plata, D; Oshida, Y; Moore, B K

1998-01-01

The present work investigates the corrosion behavior of 2205 duplex stainless steel in 0.9% NaCl solution after various heat-treatments, and compares it to that of 316L austenitic stainless steel. Both stainless steels were heat-treated at 500, 650, and 800 degrees C in air for 1 h, followed by furnace cooling. Each heat-treated sample was examined for their microstructures and Vickers micro-hardness, and subjected to the X-ray diffraction for the phase identification. Using potentiostatic polarization method, each heat-treated sample was corrosion-tested in 37 degrees C 0.9% NaCl solution to estimate its corrosion rate. It was found that simulated sensitization showed an adverse influence on both steels, indicating that corrosion rates increased by increasing the sensitization temperatures.

Evolution of stainless steels in nuclear industry

International Nuclear Information System (INIS)

Tavassoli, Farhad

2010-01-01

Starting with the stainless steels used in the conventional industry, their adoption and successive evolutions in the nuclear industry, from one generation of nuclear reactors to another, is presented. Specific examples for several steels are given, covering fabrication procedures, qualification methods, property databases and design allowable stresses, to show how the ever-increasing demands for better performance and reliability, in particular under neutron irradiation, have been met. Particular attention is paid to the austenitic stainless steels types 304L, 316L, 316L(N), 316L(N)-IG, titanium stabilized grade 321, precipitation strengthened alloy 800, conventional and low activation ferritic/martensitic steels and their oxygen dispersion strengthening (ODS) derivatives. For each material, the evolution of the associated filler metal and welding techniques are also presented. (author)

Utilizing steel slag in environmental application - An overview

Science.gov (United States)

Lim, J. W.; Chew, L. H.; Choong, T. S. Y.; Tezara, C.; Yazdi, M. H.

2016-06-01

Steel slags are generated as waste material or byproduct every day from steel making industries.The potential environmental issues which are related with the slag dump or reprocessing for metal recovery are generally being focused in the research. However the chemistry and mineralogy of slag depends on metallurgical process which is able to determine whether the steel slag can be the reusable products or not. Nowadays, steel slag are well characterized by using several methods, such as X-ray Diffraction, ICP-OES, leaching test and many more. About the industrial application, it is mainly reused as aggregate for road construction, as armour stones for hydraulic engineering constructions and as fertilizers for agricultural purposes. To ensure the quality of steel slag for the end usage, several test methods are developed for evaluating the technical properties of steel slag, especially volume stability and environmental behaviour. In order to determine its environmental behaviour, leaching tests have been developed. The focus of this paper however is on those applications that directly affect environmental issues including remediation, and mitigation of activities that negatively impact the environment.

Solidification behavior of austenitic stainless steel filler metals

International Nuclear Information System (INIS)

David, S.A.; Goodwin, G.M.; Braski, D.N.

1980-02-01

Thermal analysis and interrupted solidification experiments on selected austenitic stainless steel filler metals provided an understanding of the solidification behavior of austenitic stainless steel welds. The sequences of phase separations found were for type 308 stainless steel filler metal, L + L + delta + L + delta + γ → γ + delta, and for type 310 stainless steel filler metal, L → L + γ → γ. In type 308 stainless steel filler metal, ferrite at room temperature was identified as either the untransformed primary delta-ferrite formed during the initial stages of solidification or the residual ferrite after Widmanstaetten austenite precipitation. Microprobe and scanning transmission electron microscope microanalyses revealed that solute extensively redistributes during the transformation of primary delta-ferrite to austenite, leading to enrichment and stabilization of ferrite by chromium. The type 310 stainless steel filler metal investigated solidifies by the primary crystallization of austenite, with the transformation going to completion at the solidus temperature. In our samples residual ferrite resulting from solute segregation was absent at the intercellular or interdendritic regions

Rotation capacity of self-compacting steel fibre reinforced concrete beams

NARCIS (Netherlands)

Schumacher, P.; Walraven, J.C.; Den Uijl, J.A.; Bigaj-van Vliet, A.

2009-01-01

Steel fibres are known to enhance the toughness of concrete in compression and in tension. Steel fibres also improve the bond properties between concrete matrix and reinforcing steel bars. In order to investigate the effect of steel fibres on the rotation capacity of reinforced concrete members,

Lightweight Steel Solutions for Automotive Industry

International Nuclear Information System (INIS)

Lee, Hong Woo; Kim, Gyosung; Park, Sung Ho

2010-01-01

Recently, improvement in fuel efficiency and safety has become the biggest issue in worldwide automotive industry. Although the regulation of environment and safety has been tightened up more and more, the majority of vehicle bodies are still manufactured from stamped steel components. This means that the optimized steel solutions enable to demonstrate its ability to reduce body weight with high crashworthiness performance instead of expensive light weight materials such as Al, Mg and composites. To provide the innovative steel solutions for automotive industry, POSCO has developed AHSS and its application technologies, which is directly connected to EVI activities. EVI is a technical cooperation program with customer covering all stages of new car project from design to mass production. Integrated light weight solutions through new forming technologies such as TWB, hydroforming and HPF are continuously developed and provided for EVI activities. This paper will discuss the detailed status of these technologies especially light weight steel solutions based on innovative technologies.

Cubic martensite in high carbon steel

Science.gov (United States)

Chen, Yulin; Xiao, Wenlong; Jiao, Kun; Ping, Dehai; Xu, Huibin; Zhao, Xinqing; Wang, Yunzhi

2018-05-01

A distinguished structural characteristic of martensite in Fe-C steels is its tetragonality originating from carbon atoms occupying only one set of the three available octahedral interstitial sites in the body-centered-cubic (bcc) Fe lattice. Such a body-centered-tetragonal (bct) structure is believed to be thermodynamically stable because of elastic interactions between the interstitial carbon atoms. For such phase stability, however, there has been a lack of direct experimental evidence despite extensive studies of phase transformations in steels over one century. In this Rapid Communication, we report that the martensite formed in a high carbon Fe-8Ni-1.26C (wt%) steel at room temperature induced by applied stress/strain has actually a bcc rather than a bct crystal structure. This finding not only challenges the existing theories on the stability of bcc vs bct martensite in high carbon steels, but also provides insights into the mechanism for martensitic transformation in ferrous alloys.

Development of a new dual phase steel with laminated microstructural morphology

Energy Technology Data Exchange (ETDEWEB)

Saeidi, N., E-mail: navidsae@gmail.com [Department of Materials Engineering, Isfahan University of Technology, Isfahan, 4156–83111 (Iran, Islamic Republic of); Karimi, M. [Department of Materials Science and Engineering, Shahrood University of Technology, Shahrood, 3619995161 (Iran, Islamic Republic of); Toroghinejad, M.R. [Department of Materials Engineering, Isfahan University of Technology, Isfahan, 4156–83111 (Iran, Islamic Republic of)

2017-05-01

The development of dual phase steels to meet the current world demands, for the purpose of decreasing the fuel consumption with increasing the strength to weight ratio, requires certain microstructural modifications. In the present research, a new morphology of DP steel, known as Laminated–DP steel, as well as its unique production method has been introduced. The new process developed involved properly selecting low carbon steels, stacking them in a laminated manner and performing a roll bonding process followed by short austenitization treatment. The martensite volume fraction was designed and obtained to be 24%. Scanning electron microscopy (SEM) was employed for microstructural examination. Moreover, deformation and tensile behavior of the newly developed steel were studied and compared with those of some ordinary DP steel (ODP). Room temperature uniaxial tensile tests also revealed mechanical properties comparable with those of the commercial DP600 steel, a kind of structural automotive steel. - Highlights: • A new method for producing dual phase steels was introduced. • Employing a new thermo-mechanical process a laminated microstructure was obtained. • Mechanical properties of the new laminated DP steel were studied. • Tensile properties of the new DP steel were comparable with those of the commercial DP600 steel.

Analysis of polypyrrole-coated stainless steel electrodes

Indian Academy of Sciences (India)

Analysis of polypyrrole-coated stainless steel electrodes - Estimation of specific ... is carried out on stainless steel electrodes using -toluene sulphonic acid. ... The feasibility of the electrode for supercapacitor applications is investigated.

Effect of Heat Input on Geometry of Austenitic Stainless Steel Weld Bead on Low Carbon Steel

Science.gov (United States)

Saha, Manas Kumar; Hazra, Ritesh; Mondal, Ajit; Das, Santanu

2018-05-01

Among different weld cladding processes, gas metal arc welding (GMAW) cladding becomes a cost effective, user friendly, versatile method for protecting the surface of relatively lower grade structural steels from corrosion and/or erosion wear by depositing high grade stainless steels onto them. The quality of cladding largely depends upon the bead geometry of the weldment deposited. Weld bead geometry parameters, like bead width, reinforcement height, depth of penetration, and ratios like reinforcement form factor (RFF) and penetration shape factor (PSF) determine the quality of the weld bead geometry. Various process parameters of gas metal arc welding like heat input, current, voltage, arc travel speed, mode of metal transfer, etc. influence formation of bead geometry. In the current experimental investigation, austenite stainless steel (316) weld beads are formed on low alloy structural steel (E350) by GMAW using 100% CO2 as the shielding gas. Different combinations of current, voltage and arc travel speed are chosen so that heat input increases from 0.35 to 0.75 kJ/mm. Nine number of weld beads are deposited and replicated twice. The observations show that weld bead width increases linearly with increase in heat input, whereas reinforcement height and depth of penetration do not increase with increase in heat input. Regression analysis is done to establish the relationship between heat input and different geometrical parameters of weld bead. The regression models developed agrees well with the experimental data. Within the domain of the present experiment, it is observed that at higher heat input, the weld bead gets wider having little change in penetration and reinforcement; therefore, higher heat input may be recommended for austenitic stainless steel cladding on low alloy steel.

Fatigue characteristics of dual-phase steel sheets

Energy Technology Data Exchange (ETDEWEB)

Onn, Irwan Herman; Ahmad, Norhayati; Tamin, Mohd Nasir [Universiti Teknologi Malaysia, Skudai (Malaysia)

2015-01-15

Fatigue characteristics of dual-phase steel sheets, commonly used in automobile body construction were established. For this purpose, a series of fatigue tests, each at constant stress amplitude were conducted on 1.2 mm-thick, dual-phase DP600 steel sheet specimens with two different load ratios of minimum-to-maximum stress, R = 0.1 and -1. The resulting fatigue behavior is expressed in terms of fatigue strength-life (S-N) curves. Fatigue behavior of the steel sheets in the high-cycle fatigue region can be represented by Basquin's equation with coefficient and exponent value of 921.2 and 0.093, respectively. An endurance limit of 255 MPa is observed. In addition, fatigue strengths of the dual-phase steel sheets display lower magnitude than their bulk counterparts. Effect of mean stress on fatigue behavior of the steel sheets is well predicted by Walker's model. Exponential calibration factor is introduced to the models by SWT, Goodman and Morrow with comparable prediction to the Walker's model.

Development of Next Generation Heating System for Scale Free Steel Reheating

Energy Technology Data Exchange (ETDEWEB)

Dr. Arvind C. Thekdi

2011-01-27

The work carried out under this project includes development and design of components, controls, and economic modeling tools that would enable the steel industry to reduce energy intensity through reduction of scale formation during the steel reheating process. Application of scale free reheating offers savings in energy used for production of steel that is lost as scale, and increase in product yield for the global steel industry. The technology can be applied to a new furnace application as well as retrofit design for conversion of existing steel reheating furnaces. The development work has resulted in the knowledge base that will enable the steel industry and steel forging industry us to reheat steel with 75% to 95% reduction in scale formation and associated energy savings during the reheating process. Scale reduction also results in additional energy savings associated with higher yield from reheat furnaces. Energy used for steel production ranges from 9 MM Btu/ton to 16.6 MM Btu/ton or the industry average of approximately 13 MM Btu/ton. Hence, reduction in scale at reheating stage would represent a substantial energy reduction for the steel industry. Potential energy savings for the US steel industry could be in excess of 25 Trillion Btu/year when the technology is applied to all reheating processes. The development work has resulted in new design of reheating process and the required burners and control systems that would allow use of this technology for steel reheating in steel as well as steel forging industries.

Control of radioactivity at the Luxembourg steel-making facilities

International Nuclear Information System (INIS)

Werner, C.

1999-01-01

The Luxembourg steel industry has a yearly capacity of close to 3 million tonnes of raw steel produced from scrap at three electric arc furnace steel-making plants. It has introduced in 1994 a comprehensive system of measuring devices to prevent radioactive material from being introduced into its meltshops. Detection equipment has been installed at the road and railroad accesses to the three plants. Further to the controls of incoming scrap, radioactivity is monitored on both the steel and the slag samples of each heat produced at the plants. This measure is taken in order to detect any incident involving the melting of a radioactive source that might have escaped the controls of incoming material as soon as possible. The triple purpose of these controls is: (i) to protect the personnel of the steel making plants from radiation hazards; (ii) to maintain the integrity of the equipment; and (iii) to assure integrity of the products. The presentation describes the possible origins of radioactive contamination in steel scrap as well as the behaviour in the steel making process of the different radionuclides that can be expected to be introduced into the steel making vessels through steel scrap. Together with the government agency for radiation protection, procedures have been developed for the management of any event of detection of radioactivity in the plants and to assure optimum availability of the measuring equipment. These procedures are described and commented in the presentation. The presentation includes also a report on the experience from 4 years of monitoring, during which more than 10 million tonnes of scrap have passed the gates of the steel-making plants of ProfilARBED and ARES. (author)

Passivation condition of carbon steel in bentonite/sand mixture

International Nuclear Information System (INIS)

Taniguchi, Naoki; Kawakami, Susumu

2002-03-01

It is essential to understand the corrosion type of carbon steel under the repository conditions for the lifetime assessment of carbon steel overpack used for geological isolation of high-level radioactive waste. According to the previous study, carbon steel is hard to passivate in buffer material assuming a chemical condition range of groundwater in Japan. However, concrete support will be constructed around the overpack in the case of repository in the soft rock system and groundwater having a higher pH may infiltrate to buffer material. There is a possibility that the corrosion type of carbon steel will be influenced by the rise of the pH in groundwater. In this study, anodic polarization experiments were performed to understand the passivation condition of carbon steel in buffer material saturated with water contacted with concrete. An ordinary concrete an a low-alkalinity concrete were used in the experiment. The results of the experiments showed that the carbon steel can passivate under the condition that water having pH > 13 infiltrate to the buffer material assuming present property of buffer material. If the low-alkalinity concrete is selected as the support material, passivation can not occur on carbon steel overpack. The effect of the factors of buffer material such as dry density and mixing ratio of sand on the passivation of carbon steel was also studied. The results of the study showed that the present property of buffer material is enough to prevent passivation of carbon steel. (author)

Formability Characterization of a New Generation High Strength Steels

Energy Technology Data Exchange (ETDEWEB)

Sriram Sadagopan; Dennis Urban; Chris Wong; Mai Huang; Benda Yan

2003-05-16

Advanced high strength steels (AHSS) are being progressively explored by the automotive industry all around the world for cost-effective solutions to accomplish vehicle lightweighting, improve fuel economy, and consequently reduce greenhouse emissions. Because of their inherent high strength, attractive crash energy management properties, and good formability, the effective use of AHSS such as Duel Phase and TRIP (Transformation Induced Plasticity) steels, will significantly contribute to vehicle lightweighting and fuel economy. To further the application of these steels in automotive body and structural parts, a good knowledge and experience base must be developed regarding the press formability of these materials. This project provides data on relevant intrinsic mechanical behavior, splitting limits, and springback behavior of several lots of mild steel, conventional high strength steel (HSS), advanced high strength steel (AHSS) and ultra-high strength steel (UHSS), supplied by the member companies of the Automotive Applications Committee (AAC) of the American Iron and Steel Institute (AISI). Two lots of TRIP600, which were supplied by ThyssenKrupp Stahl, were also included in the study. Since sheet metal forming encompasses a very diverse range of forming processes and deformation modes, a number of simulative tests were used to characterize the forming behavior of these steel grades. In general, it was found that formability, as determined by the different tests, decreased with increased tensile strength. Consistant with previous findings, the formability of TRIP600 was found to be exceptionally good for its tensile strength.

Study on Fatigue Characteristics of High-Strength Steel Welds

Energy Technology Data Exchange (ETDEWEB)

Chang, Hong Suk; Yoo, Seung Won; Park, Jong Chan [Hyundai Motor Group, Seoul (Korea, Republic of)

2015-03-15

High-strength steel has replaced mild steel as the material of choice for truck decks or frames, owing to the growing demand for lightweight vehicles. Although studies on the weld fatigue characteristics of mild steel are available, studies on high-strength steels have been seldom conducted. In this study, firstly, we surveyed a chosen number of approaches and selected the Radaj method, which uses the notch factor approach, as the one suitable for evaluating the fatigue life of commercial vehicles. Secondly, we obtained the S-N curves of HARDOX and ATOS60 steel welds, and the F-N curves of the T-weld and overlapped-weld structures. Thirdly, we acquired a general S-N curve of welded structures made of high-strength steel from the F-N curve, using the notch factor approach. Fourthly, we extracted the weld fatigue characteristics of high-strength steel and incorporated the results in the database of a commercial fatigue program. Finally, we compared the results of the fatigue test and the CAE prediction of the example case, which demonstrated sufficiently good agreement.

Structure of steel reactor building and construction method therefor

International Nuclear Information System (INIS)

Yamakawa, Toshikimi.

1997-01-01

The building of the present invention contains a reactor pressure vessel, and has double steel plate walls endurable to elevation of inner pressure and keeping airtightness, and shielding concretes are filled between the double steel plate walls. It also has empty double steel plate walls not filled with concretes and has pipelines, vent ducts, wirings and a support structures for attaching them between the double steel plate walls. It is endurable to a great inner pressure satisfactory and keeps airtightness by the two spaced steel plates. It can be greatly reduced in the weight, and can be manufactured efficiently with high quality in a plant by so called module construction, and the dimension of the entire of the reactor building can be reduced. It is constructed in a dock, transported on the sea while having the space between the two steel plate walls as a ballast tanks, placed in the site, and shielding concretes are filled between the double steel plate walls. The term for the construction can be reduced, and the cost for the construction can be saved. (N.H.)

Long-term Stability of 9- to 12 % Cr Steels

DEFF Research Database (Denmark)

Hald, John

2004-01-01

In the recent 25 years creep rupture strength of 9- to 12 %Cr steels for steam pipes and turbines has been doubled by development of new alloys. This development has formed a basis for improved efficiency of fossil fired steam power plants by introduction of advanced steam temperatures...... and pressures. Newly developed steam pipe steels are based on modifications of well-established steels like the X 20CrMoV12 1. Balanced addition of V, Nb and N to a 9Cr 1 Mo steel led to the Modified 9 Cr steel P 91. Addition of 1% W to a 9Cr 1 MoVNbN base composition led to steel E 911 and partial replacement...... of Mo with 1.8 % W combined with a slight amount of Boron led to steel P 92. The creep rupture strength of these new alloys are now secured with long-term tests up to 100,000 hours, which demonstrate improvements of 50% (P 91), 75 % (E 911) and 100 % (P 92) in strength compared to X 20CrMoV12 1....

Electrolytic plasma processing of steel surfaces

International Nuclear Information System (INIS)

Bejar, M.A; Araya, R.N; Baeza, B

2006-01-01

The thermo-chemical treatments of steels with plasma is normally carried out in low-pressure ionized gaseous atmospheres. Among the treatments used most often are: nitruration, carburization and boronized. A plasma can also generate at atmospheric pressure. One way to produce it is with an electrochemical cell that works at a relatively high inter-electrode voltage and under conditions of heavy gas generation. This type of plasma is known as electrolytic plasma. This work studies the feasibility of using electrolytic plasma for the surface processing of steels. Two processes were selected: boronized and nitruration., for the hardening of two types of steel: one with low carbon (1020) and one with low alloy (4140). In the case of the nitruration, the 1020 steel was first aluminized. The electrolytes were aqueous solutions of borax for the boronizing and urea for the nitruration. The electrolytic plasmas were classified qualitatively, in relation with their luminosity by low, medium and high intensity. The boronizing was carried out with low intensity plasmas for a period of one hour. The nitruration was performed with plasmas of different intensities and for period of a few minutes to half an hour. The test pieces processed by electrolytic plasma were characterized by micro-hardness tests and X-ray diffraction. The maximum surface hardnesses obtained for the 1020 and 4140 steels were the following: 300 and 700 HV for the boronizing, and 1650 and 1200 HV for the nitruration, respectively. The utilization of an electrolytic plasma permits the surface processing of steels, noticeably increasing their hardness. With this type of plasma some thermo-chemical surface treatments can be done very rapidly as well (CW)

Recent advances in creep-resistant steels for power plant applications

Indian Academy of Sciences (India)

M. Senthilkumar (Newgen Imaging) 1461 1996 Oct 15 13:05:22

that the martensitic transformation in these three steels produces high dislocation density that confers ... impact and economics have focussed attention on the development of high efficiency, low emission systems. .... programme of Nippon Steel led to the steel NF616 (Nippon Steel 1991), which is now designated P92 in the ...

Low temperature plasma carburizing of AISI 316L austenitic stainless steel and AISI F51 duplex stainless steel

OpenAIRE

Pinedo,Carlos Eduardo; Tschiptschin,André Paulo

2013-01-01

In this work an austenitic AISI 316L and a duplex AISI F51 (EN 1.4462) stainless steel were DC-Plasma carburized at 480ºC, using CH4 as carbon carrier gas. For the austenitic AISI 316L stainless steel, low temperature plasma carburizing induced a strong carbon supersaturation in the austenitic lattice and the formation of carbon expanded austenite (γC) without any precipitation of carbides. The hardness of the carburized AISI 316L steel reached a maximum of 1000 HV due to ∼13 at% c...

Low temperature plasma carburizing of AISI 316L austenitic stainless steel and AISI F51 duplex stainless steel

OpenAIRE

Pinedo, Carlos Eduardo; Tschiptschin, André Paulo

2013-01-01

In this work an austenitic AISI 316L and a duplex AISI F51 (EN 1.4462) stainless steel were DC-Plasma carburized at 480ºC, using CH4 as carbon carrier gas. For the austenitic AISI 316L stainless steel, low temperature plasma carburizing induced a strong carbon supersaturation in the austenitic lattice and the formation of carbon expanded austenite (γC) without any precipitation of carbides. The hardness of the carburized AISI 316L steel reached a maximum of 1000 HV due to ∼13 at% carbon super...

Steel refining possibilities in LF

Science.gov (United States)

Dumitru, M. G.; Ioana, A.; Constantin, N.; Ciobanu, F.; Pollifroni, M.

2018-01-01

This article presents the main possibilities for steel refining in Ladle Furnace (LF). These, are presented: steelmaking stages, steel refining through argon bottom stirring, online control of the bottom stirring, bottom stirring diagram during LF treatment of a heat, porous plug influence over the argon stirring, bottom stirring porous plug, analysis of porous plugs disposal on ladle bottom surface, bottom stirring simulation with ANSYS, bottom stirring simulation with Autodesk CFD.

EIS Response of MIC on Carbon Steel

DEFF Research Database (Denmark)

Hilbert, Lisbeth Rischel; Maahn, Ernst

1998-01-01

Abstract Microbially influenced corrosion of carbon steel under sulphate reducing (sulphide-producing) bacterial activity (SRB) results in the formation of both ferrous sulphides as well as biofilm on the metal surface. The electrochemical characteristics of the ferrous sulphide/steel interface...... as compared to the biofilm/ferrous sulphide/steel interface has been studied with EIS, DC polarisations (Tafel, LPR) and a potentiostatic step technique. The electrochemical response is related to a threshold sulphide concentration above which very characteristic changes such as indications of finite...

HIGH TEMPERATURE TENSILE PROPERTIES OF NEW FE-CR-MN DEVELOPED STEEL

Directory of Open Access Journals (Sweden)

M. Mahmoudiniya

2017-03-01

Full Text Available Nowadays, Ni-free austenitic stainless steels are being developed rapidly and high price of nickel is one of the most important motivations for this development. At present research a new FeCrMn steel was designed and produced based on Fe-Cr-Mn-C system. Comparative studies on microstructure and high temperature mechanical properties of  new steel and AISI 316 steel were done. The results showed that new FeCrMn developed steel has single austenite phase microstructure, and its tensile strength and toughness were higher than those of 316 steel at 25, 200,350 and 500°C. In contrast with 316 steel, the new FeCrMn steel did not show strain induced transformation and dynamic strain aging phenomena during tensile tests that represented higher austenite stability of new developed steel. Lower density and higher strength of the new steel caused higher specific strength in comparison with the 316 one that can be considered as an important advantage in structural applications but in less corrosive environment

Steel fiber replacement of mild steel in prestressed concrete beams

Science.gov (United States)

2010-10-01

In traditional prestressed concrete beams, longitudinal prestressed tendons serve to resist bending moment and : transverse mild steel bars (or stirrups) are used to carry shear forces. However, traditional prestressed concrete I-beams : exhibit earl...

Steel fiber replacement of mild steel in prestressed concrete beams.

Science.gov (United States)

2011-01-01

In traditional prestressed concrete beams, longitudinal prestressed tendons serve to resist bending moment and transverse mild : steel bars (or stirrups) are used to carry shear forces. However, traditional prestressed concrete I-beams exhibit early-...

Properties of Reinforced Concrete Steel Rebars Exposed to High Temperatures

Directory of Open Access Journals (Sweden)

İlker Bekir Topçu

2008-01-01

Full Text Available The deterioration of the mechanical properties of yield strength and modulus of elasticity is considered as the primary element affecting the performance of steel structures under fire. In this study, hot-rolled S220 and S420 reinforcement steel rebars were subjected to high temperatures to investigate the fire performance of these materials. It is aimed to determine the remaining mechanical properties of steel rebars after elevated temperatures. Steels were subjected to 20, 100, 200, 300, 500, 800, and 950∘C temperatures for 3 hours and tensile tests were carried out. Effect of temperature on mechanical behavior of S220 and S420 were determined. All mechanical properties were reduced due to the temperature increase of the steel rebars. It is seen that mechanical properties of S420 steel was influenced more than S220 steel at elevated temperatures.

On the corrosion resistance of 01Kh25 ferritic steel

International Nuclear Information System (INIS)

Eremeeva, R.A.; Koval', E.K.