Quasicrystalline and crystalline precipitation during isothermal tempering in a 12Cr-9Ni-4Mo maraging stainless steel

International Nuclear Information System (INIS)

Liu, P.; Stigenberg, A.H.; Nilsson, J.O.

1995-01-01

A thorough microstructural investigation has been performed on a high strength maraging steel of the type 12%Cr-9%Ni-4%Mo-2%Cu-1%Ti. The major precipitate formed during isothermal aging at 475 C is a quasicrystalline phase possessing icosahedral symmetry termed R'-phase with a typical chemical composition of 48%Mo-33%Fe-13%Cr-2%Ni-4%Si. At 550 C the major precipitate is trigonal R-phase with a typical composition of 45%Mo-31%Fe-18%Cr-4%Ni-2%Si. At 550 C also Laves phase with a composition of 48%Mo-35%Fe-13%Cr-2%Ni-2%Si could be observed. At both 475 and 550 C an ordered phase termed L-phase precipitated. This minority phase has an ordered face centered cubic (f.c.c.) structure of type L1 0 . Its composition is typically 9%Fe-4%Cr-52%Ni-15%Mo.-16%Ti-4%Al. R'-phase formed at 475 C transformed to R-phase and Laves phase during aging at 550 C. In an analogous manner, R-phase and Laves phase formed at 550 C transformed to R'-phase during subsequent aging at 475 C. This transformation was rationalized by a strong similarity in crystal structure between quasicrystalline R'-phase of icosahedral symmetry and Frank-Kasper phases such as R-phase and Laves phase

Low-Cycle Fatigue Behavior of 10CrNi3MoV High Strength Steel and Its Undermatched Welds.

Science.gov (United States)

Song, Wei; Liu, Xuesong; Berto, Filippo; Razavi, S M J

2018-04-24

The use of high strength steel allows the design of lighter, more slender and simpler structures due to high strength and favorable ductility. Nevertheless, the increase of yield strength does not guarantee the corresponding improvement of fatigue resistance, which becomes a major concern for engineering structure design, especially for the welded joints. The paper presents a comparison of the low cycle fatigue behaviors between 10CrNi3MoV high strength steel and its undermatched weldments. Uniaxial tension tests, Push-pull, strain-controlled fatigue tests were conducted on base metal and weldments in the strain range of 0.2⁻1.2%. The monotonic and cyclic stress-strain curves, stress-life, strain-life and energy-life in terms of these materials were analyzed for fatigue assessment of materials discrepancy. The stress-life results of base metal and undermatched weld metal exhibit cyclic softening behaviors. Furthermore, the shapes of 10CrNi3MoV steel hysteresis loops show a satisfactory Masing-type behavior, while the weld metal shows a non-Masing type behavior. Strain, plastic and total strain energy density amplitudes against the number of reversals to failure results demonstrate that the undermatched weld metal presents a higher resistance to fatigue crack initiation than 10CrNi3MoV high strength steel. Finally, fatigue fracture surfaces of specimens were compared by scanning electron microscopy to identify the differences of crack initiation and the propagation between them.

Low-Cycle Fatigue Behavior of 10CrNi3MoV High Strength Steel and Its Undermatched Welds

Directory of Open Access Journals (Sweden)

Wei Song

2018-04-01

Full Text Available The use of high strength steel allows the design of lighter, more slender and simpler structures due to high strength and favorable ductility. Nevertheless, the increase of yield strength does not guarantee the corresponding improvement of fatigue resistance, which becomes a major concern for engineering structure design, especially for the welded joints. The paper presents a comparison of the low cycle fatigue behaviors between 10CrNi3MoV high strength steel and its undermatched weldments. Uniaxial tension tests, Push-pull, strain-controlled fatigue tests were conducted on base metal and weldments in the strain range of 0.2–1.2%. The monotonic and cyclic stress-strain curves, stress-life, strain-life and energy-life in terms of these materials were analyzed for fatigue assessment of materials discrepancy. The stress-life results of base metal and undermatched weld metal exhibit cyclic softening behaviors. Furthermore, the shapes of 10CrNi3MoV steel hysteresis loops show a satisfactory Masing-type behavior, while the weld metal shows a non-Masing type behavior. Strain, plastic and total strain energy density amplitudes against the number of reversals to failure results demonstrate that the undermatched weld metal presents a higher resistance to fatigue crack initiation than 10CrNi3MoV high strength steel. Finally, fatigue fracture surfaces of specimens were compared by scanning electron microscopy to identify the differences of crack initiation and the propagation between them.

Substitution of modified 9 Cr-1 Mo steel for austentic stainless steels

International Nuclear Information System (INIS)

Sikka, V.K.

1982-04-01

This report describes the current program to develop a high-strength ferritic-martensitic steel. The alloy is essentially Fe-9% Cr-1% Mo with small additions of V and Nb and is known as modifed 9 Cr-1 Mo steel. Its elevated-temperature properties and design allowable stresses match those of type 304 stainless steel for temperatures up to 600 0 C and exceed those of other ferritic steels by factors of 2 to 3. The improved strength of this alloy permits its use in place of stainless steels for many applications

A Weakest-Link Approach for Fatigue Limit of 30CrNiMo8 Steels (Preprint)

Science.gov (United States)

2011-03-01

34Application of a Weakest-Link Concept to the Fatigue Limit of the Bearing Steel Sae 52100 in a Bainitic Condition," Fatigue and Fracture of...AFRL-RX-WP-TP-2011-4206 A WEAKEST-LINK APPROACH FOR FATIGUE LIMIT OF 30CrNiMo8 STEELS (PREPRINT) S. Ekwaro-Osire and H.V. Kulkarni Texas...2011 4. TITLE AND SUBTITLE A WEAKEST-LINK APPROACH FOR FATIGUE LIMIT OF 30CrNiMo8 STEELS (PREPRINT) 5a. CONTRACT NUMBER In-house 5b. GRANT

Effects of Bond Coating on NiCrBSi-Mo Composite Functional Coating Properties in Plasma Spraying NiCrBSi-Mo/Ni Coating

OpenAIRE

DU Ji-yu; LI Fang-yi; LU Hai-yang; SHANG Jian-tong; LI Zhen

2017-01-01

Nickel-based bond coating and composite functional coating were sprayed on leaf blade steel material FV520B successively by using air plasma spraying system. NiCrBSi-Mo powder deposition rate, coating porosity, bonding strength and surface hardness were tested. The results indicate that, for the NiCrBSi-Mo/Ni coating, bond coating with 180-220μm thickness can improve NiCrBSi-Mo powder deposition rate while the surface coating with lower porosity, higher bonding strength and high hardness is p...

Comparative study of creep behaviour in three Cr Ni 15/15 steel stabilized with Ti and with different contents in W, Mn, Mo and Bor

International Nuclear Information System (INIS)

Solano, R.R.; Rivas, M. de las; Schirra, M.; Seith, B.

1975-01-01

The main difference between the three steels which are tested at temperature range from 650 0 C to 750 0 C is due to the hardening elements pf the matrix and the Boron content: 1. 12R72HV (X10NiCrMoTiB 1515) 2% Mn 1,5% Mo 80 ppmB 2. Vaccutherm (X12CrNiWTi 1613) 3% W 2,5 ppmB 3. RGT 21 (X12CrNiWTi 1613) 3% W 50 ppm B. The investigations of all casts are carried out in two different heat treatments which are suitable for the conditions required for the operation of the reactor. Cond. I: 1150 0 C 30 min, water quenced; 800 0 32 hour, air; 10% cold work. Cond. II: 1150 0 C 30 min, water quenched; 10% cold work. In connection with creep test the condition I irrespective of 3 steels show no remarkable difference. The observation at 750 0 C test temperature and also at condition II above 650 0 C on Boron-free Vaccutherm cast shows an unfavourable behaviour. There is no significant difference in the stress dependence of secondary creep rate and also absolute creep rate. A definite superiority is to be found for 12R72HV when considering the values for time-yield-limit-ratio and ductility compared to the W-steels. The test results shows different fracture behaviour. Transcrystalline fracture is found on cast 12R72HV, whereas RGT 21 and Vaccutherm show transition from transcrystalline to intercrystalline fracture, depending on the rupture time and test temperature. The long term rupture specimens show intercrystalline fracture. (author)

Austenite Formation from Martensite in a 13Cr6Ni2Mo Supermartensitic Stainless Steel

NARCIS (Netherlands)

Bojack, A.; Zhao, L.; Morris, P.F.; Sietsma, J.

2016-01-01

The influence of austenitization treatment of a 13Cr6Ni2Mo supermartensitic stainless steel (X2CrNiMoV13-5-2) on austenite formation during reheating and on the fraction of austenite retained after tempering treatment is measured and analyzed. The results show the formation of austenite in two

Observations on thermally cycled 20% Cr/25% Ni/Nb stabilised stainless steel

International Nuclear Information System (INIS)

Lobb, R.C.

1984-06-01

A variety of optical and electron techniques, such as optical metallography, scanning electron microscopy and electron probe microanalysis, have been used to study the morphology and composition of oxides formed on 20 Cr/25 Ni/Nb stainless steel during oxidation at 850 0 C and subsequent thermal cycling in simulated reactor gas. (author)

Welding and corrosion resistance of the new nitrogen alloyed steel X2 CrNiMnMoN241764

International Nuclear Information System (INIS)

Arit, N.; Henser, H.; GroB, V.

1994-01-01

Remanit 4565 S is a new developed nitrogen alloyed austenitic stainless steel. Characteristic features are: improved strength and toughness, delayed precipitation of carbides and intermetallic phases, improved corrosion resistance. Welding fabrication is possible without the risk of pore formation. TIG-welded joints are as resistant as the base metal, using filler metal SG-NiCr 20 Mo 15 (Thermanit Nimo C) respectively SG-NiCr 28 Mo(Thermanit 30/40 E) according to the area of application. (Author) 8 refs

Resistencia a la corrosión a alta temperatura de recubrimientos NiCrAlY y NiCrFeNbMoTiAl depositados por APS

Directory of Open Access Journals (Sweden)

José Luis Tristancho-Reyes

2014-12-01

Full Text Available La corrosión a alta temperatura de las tuberías utilizadas en equipos generadores de vapor (calderas ha sido reconocida como un grave problema que trae consigo el adelgazamiento de éstas y, por consiguiente, la falla de los equipos. En la última década se han incrementado las investigaciones que involucran recubrimientos protectores que ayudan de alguna manera a prolongar la vida útil de estos equipos. Esta investigación determinó el comportamiento de los recubrimientos NiCrAlY y NiCrFeNbMoTiAl depositados por proyección térmica asistida por plasma (APS sobre la aleación SA213 – T22 (2¼Cr – 1Mo, en un ambiente corrosivo de 80%V2O5–20%K2SO4 a 800°C. Los valores de la cinética de corrosión fueron determinados mediante resistencia a la polarización lineal (RPL y espectroscopia de impedancia electroquímica (EIE. Los resultados obtenidos muestran una menor cinética de corrosión en el recubrimiento NiCrFeNbMoTiAl que la presentada por el recubrimiento NiCrAlY, corroborado por Microscopia Electrónica de Barrido (MEB.

Development of banded microstructure in 34CrNiMo6 steel

Directory of Open Access Journals (Sweden)

A. Nagode

2016-07-01

Full Text Available In this paper the development of a banded microstructure in hot-rolled 34CrNiMo6 steel which consisted of bainitic and martensitic bands is explained. The chemical compositions of the bands were measured with energy dispersive x-ray spectroscopy (EDS, which showed that the martensitic bands contained more alloying elements (Mn, Cr, Mo, Si than bainitic bands. By using Oberhoffer reagent, the segregations of phosphorus were also revealed. These phosphorus segregations coincided with the positive segregations of the alloying elements. The continuous cooling transformation (CCT diagrams of steel were calculated. They confirmed the formation of martensite in positive segregations and the formation of bainite in negative segregations.

Microstructural evolution in 13Cr-8Ni-2.5Mo-2Al martensitic precipitation-hardened stainless steel

International Nuclear Information System (INIS)

Ping, D.H.; Ohnuma, M.; Hirakawa, Y.; Kadoya, Y.; Hono, K.

2005-01-01

The microstructure of 13Cr-8Ni-2.5Mo-2Al martensitic precipitation-hardened (PH) stainless steel has been investigated using transmission electron microscopy, three-dimensional atom probe and small-angle X-ray scattering. A high number density (∼10 23-25 m -3 ) of ultra-fine (1-6 nm) β-NiAl precipitates are formed during aging at 450-620 deg. C, which are spherical in shape and dispersed uniformly with perfect coherency with the matrix. As the annealing temperature increases, the size and concentration of the precipitates increase concurrently while the number density decreases. The Mo and Cr segregation to the precipitate-matrix interface has been detected and is suggested to suppress precipitate coarsening. In the sample aged for 500 h at 450 deg. C, the matrix decomposes into Cr-rich (α') and Cr-poor (α) regions. The decrease in the strength at higher temperature (above 550 deg. C) is attributed to the formation of larger carbides and reverted austenite

Investigation of Cr-Ni duplex stainless steel

International Nuclear Information System (INIS)

Lu Shiying

1985-01-01

At temperatures of 450 - 750 0 C, a laminate-shaped intermetallic phase Fe3Cr3Mo2Si2 has been observed. Intergranular brittle fracture is due to the precipitation of the Fe3Cr3Mo2SI2 phase, but quasi-cleavage fracture is connected with the precipitation of chi and σ phases. The formation of chi and σ during aging at 750 - 900 0 C results in a drastic decrease of the SCC resistance of Cr18Ni5 steel. In order to avoid a fully ferritic microstructure in Cr18Ni5 duplex steel after heating at high temperature or welding, the K value must be kept to 0.42 for thin wall tube. The decrease in SCC resistance after cold deformation is not due to the formation of strain-induced martensite but is connected with significant reduction in the resistance to pitting corrosion. (author)

Effect of Si and Mn additions on ferrite and austenite phase fractions in 25Cr-7Ni-1.5Mo-3W base super duplex stainless steels

International Nuclear Information System (INIS)

Jeong, S.W.; Lee, Z.-H.; Lee, H.M.

2000-01-01

The effect of heat treatment and Si and Mn additions on the ferrite and austenite phase fractions of the super duplex stainless steel (SDSS), Fe-25Cr-7Ni-1.5Mo-3W-Si-Mn-0.25N (numbers are all in wt.% unless specified otherwise), was investigated. The thermodynamic calculations of phase equilibria and phase fractions were performed using the Thermo-Calc program. Based on the calculated results, specific compositions of Si and Mn were selected and alloys with these compositions were analysed by Feritscope, X-ray diffractometry and scanning electron microscopy. The calculated phase fractions and experimentally analysed ones were compared and there was a good agreement between calculations and measurements. The optimum heat treatment condition for Fe-25Cr-7Ni-1.5Mo-3W-0.5Si-0.5Mn-0.25N is to hold at 1050 to 1100 C for 2 h in considering the ferrite to austenite ratio of 50:50 and to avoid second phase precipitation such as the σ phase. It was suggested that an excessive addition of more than 0.8Si and 1.0Mn may induce the σ phase precipitation. (orig.)

Influence of creep ductility on creep-fatigue behaviour of 20%Cr/25%Ni/Nb stainless steel

International Nuclear Information System (INIS)

Gladwin, D.; Miller, D.A.

1985-01-01

The influence of creep ductility on creep-fatigue endurance of 20%Cr/25%Ni/Nb stainless steel has been examined. In order to induce different creep ductilities in the 20/25/Nb stainless steel, three different thermo-mechanical routes were employed. These resulted in a range of ductilities (3-36%) being obtained at the strain rates of interest. Strain controlled slow-fast creep-fatigue cycles were used with strain rates of 10 -6 s -1 , 10 -7 s -1 in tension and 10 -3 s -1 in compression. It was found that creep ductility strongly influenced the creep-fatigue endurance of the 20/25/Nb stainless steel. When failure was creep dominated endurance was found to be directly proportional to the creep ductility. A ductility exhaustion model has been used to successfully predict creep-fatigue endurance when failure was creep dominated. (author)

Creep and time to rupture of a 16/16 Cr Ni Steel; Comportamiento a la fluencia lenta de la aleacion X 8 Cr Ni Mo Nb 1616 con distintos tratamientos termicos

Energy Technology Data Exchange (ETDEWEB)

Solano, R; Garcia, R; Bohm, H; Schirra, M

1972-07-01

The influence of different thermal-mechanical treatments on the creep and time to rupture of a 16/16 Cr.Ni steel is studied. The solution treated material after annealing at 700-800 degree centigree did not affect time to rupture. At the contrary a 12% cold-working and annealing at 800 degree centigree improve the time to rupture. This treatment is preserved up to 700 degree centigree 10{sup 4} hours. The ductility is not strongly affected. A metallographic study of the fracture was carried out. (Author) 23 refs.

Effect of heat treatment on workability of Cr-Ni-Mo steels

International Nuclear Information System (INIS)

Barcal, J.; Macek, K.

1988-01-01

The workability was studied of the new development generation of hardenable martensite Cr-Ni-Mo steels of the 10-10-2 and 6-11-3 types whose application is envisaged in future in nuclear engineering. Attention is paid to identification of inclusions and the phase analysis ofthe structure with respect to heat treatment and steel type. Face milling was used in the test of workability. In addition, tensile strength and impact bending strength testing was performed. The results showed that steel of the 6-11-3 type in the quenched condition was best workable. However, this steel showed a significant reduction in workability when in the hardened condition. Reduced workability can also be presumed for type 10-10-2 steel in the hardened condition when life is considered. Microstructure changes leading to softening of steel by aging had a favourable effect on workability, especially in steels of the 10-10-2 type. Hardened steels of the 6-11-3 type are recommended to be re-quenched. (Z.M.). 7 figs., 3 tabs., 9 refs

Alloying effect on hardening of martensite stainless steels of the Fe-Cr-Ni and Fe-Cr-Co systems

International Nuclear Information System (INIS)

Fel'dgandler, Eh.G.; Savkina, L.Ya.

1975-01-01

The effect of alloying elements is considered on the γ → a-transformation and hardening of certain compositions of the ternary Fe-Cr-Ni- and Fe-Cr-Co alloy systems with the martensite structure. In martensite Fe-(10 to 14)% Cr base steels the elements Co, Cu, W, Ni, Mo, Si, Cr decrease, Mn, Si, Mo, Cu increase, and Cr, Ni, Co decrease the temperature of α → γ-transition. The tempering of martensite steels of the Fe-Cr-Ni- and Fe-Cr-Co-systems containing 10 to 14% Cr, 4 to 9% Ni, and 7 to 12% Co does not lead to hardening. Alloyage of the martensite Fe-Cr-Ni-, Fe-Cr-Co- and Fe-Cr-Ni-Co base separately with Mo, W, Si or Cu leads to a hardening during tempering, the hardening being the higher, the higher is the content of Ni and, especially, of Co. The increase in the content of Mo or Si produces the same effect as the increase in the Co content. In on Fe-Cr-Co or Fe-Cr-Ni-Co based steels alloyed with Mo or Si, two temperature ranges of ageing have been revealed which, evidently, have different hardening natures. The compositions studied could serve as the base material for producing maraging stainless steels having a complex variety of properties

Comparison of the corrosion resistance of DIN W. Nr. 1.4970 (15%Cr-15%Ni-1.2%Mo-Ti and ASTM F-138 (17%Cr-13%Ni-2.5%Mo austenitic stainless steels for biomedical applications

Directory of Open Access Journals (Sweden)

Maysa Terada

2006-09-01

Full Text Available The resistance to localised corrosion of the full austenitic 15%Cr-15%Ni-1.2%Mo titanium stabilized stainless steel (DIN W. Nr. 1.4970 was investigated by electrochemical methods including electrochemical impedance spectroscopy (EIS, potentiodynamic polarization and potentiostatic polarization measurements in a phosphate-buffered solution (PBS. The low carbon and non-stabilized austenitic stainless steel, AISI 316L (ASTM F-138, widely used for surgical implants, was also tested for comparison. The tests were conducted at room temperature after a stable potential had been reached. After the electrochemical measurements, the surfaces of the specimens were observed using SEM to evaluate the presence of pits. Potentiodynamic polarization results showed that both steels are prone to localized corrosion. Larger pits were found on the surface of AISI 316L specimens after the electrochemical tests. EIS response has indicated the duplex structure of the passive oxides. The results showed that the electrochemical behaviour of the DIN W. Nr. 1.4970 is better than of AISI 316L steel. Therefore, their application as an implant material may be considered.

Heterogeneity of structure and properties of 12Cr18Ni10Ti and 08Cr16Ni11Mo3 stainless steels irradiated up to high damaging doses in reactor Bn-350

International Nuclear Information System (INIS)

Maksimkin, O.P.; Tivanova, O.V.; Turubarova, L.G.; Silnyagina, N.S.; Doronina, T.A.

2006-01-01

Full text: Earlier, during investigation of post-operating properties and structure of responsible units of fast neutron reactors there was shown /1, 2/ that depending on character of preliminary treatment of austenite stainless steel (austenization, cold deformation, mechanical and thermal treatment) radiation effects could be different. In /2/ one could observe heterogeneity at swelling of cold- worked hexahedral ducts along perimeter, in particular, the swelling of corners was less than plates'. At the same time after mechanical-thermal treatment the corners swell in 3-5 times of magnitude higher than plates. By the present there are several assumptions about nature of this phenomenon. One of them is a difference of deformation degree of material in corners and plates of the duct. It is known that /3/ external effects (including deformation) induce martensitic γ→α transformation in austenitic steels, due to which the structure and properties of steel are changed. In particular, paramagnetic FCC matrix reveals sites with ferromagnetic BCC structure. Steel heating, containing martensitic α-phase higher than ∼ 450-800 deg C, results in reverse γ→α transformation in material, which in its turn leads to formation of phase phase-hardened austenite. We can expect that only peculiarities of processes of direct and reverse martensitic transformations, which took place during preliminary austenitic steel treatment, will predetermine its behavior under irradiation. Taking into account the above mentioned there have been carried out complex material-scientific investigations of 12Cr18Ni10Ti and 08Cr16Ni11Mo3 steel samples cut off from different sites (both adjacent to corners and far from them) of hexagonal ducts of spent fuel assemblies of BN-350 reactor. There were used samples in the form of plates of different sizes: 5x10x2 mm - for metallographic investigations (microscope Neophot-2) and determination of microhardness (PMT-3); 2x20x0,3 mm - for mechanical

Correlation of yield stress and microhardness in 08Cr16Ni11Mo3 stainless steel irradiated to high dose in the BN-350 fast reactor

International Nuclear Information System (INIS)

Gusev, M.N.; Maksimkin, O.P.; Tivanova, O.V.; Silnaygina, N.S.; Garner, F.A.

2006-01-01

The relationship between the microhardness and the engineering yield stress in 08Cr16Ni11Mo3 steel after irradiation in the BN-350 reactor has been experimentally derived and agrees with a previously published correlation developed by Toloczko for unirradiated 316 in a variety of cold-work conditions. Even more importantly, when the correlation is derived in the K Δ format where the correlation involves changes in the two properties, excellent agreement is found with a universal K Δ correlation developed by Busby and coworkers. Additionally, this report points out that microhardness measurements must take into account that sodium exposure at high temperature and neutron fluence alters the metal surface to produce ferrite, and therefore the altered layers should be removed prior to testing

Precipitation kinetics in austenitic 18Cr-30Ni-Nb cast steel

Directory of Open Access Journals (Sweden)

M. Garbiak

2008-08-01

Full Text Available The study presents the results of investigations on the precipitation kinetics in austenitic 18%Cr-30%Ni cast steel stabilised with an addition of 1.84 wt% niobium. Phase analysis of isolates extracted from the alloy subjected to annealing within the temperature range of 600–1000oC during 10–1000 h was made. The phase constitution of the isolates mainly comprised niobium carbides of the NbC type and complex chromium carbides of the Cr23C6 type. In specimens annealed within the temperature range of 700–900oC, a high-silicon G phase was additionally identified. The highest kinetics of the precipitation process was recorded after annealing at the temperatures of 800 and 900oC.

Improved hardness of laser alloyed X12CrNiMo martensitic stainless steel

CSIR Research Space (South Africa)

Adebiyi, DI

2011-07-01

Full Text Available The improvement in hardness of X12CrNiMo martensitic stainless steel laser alloyed with 99.9% pure titanium carbide, stellite 6 and two cases of premixed ratio of titanium carbide and stellite 6 [TiC (30 wt.%)- stellite 6 (70 wt.%) and TiC (70 wt...

Study of fatigue and fracture behavior of NbCr{sub 2}-based alloys: Phase stability in Nb-Cr-Ni ternary system

Energy Technology Data Exchange (ETDEWEB)

Zhu, J.H.; Liaw, P.K. [Univ. of Tennessee, Knoxville, TN (United States). Dept. of Materials Science and Engineering; Liu, C.T. [Oak Ridge National Lab., TN (United States). Metals and Ceramics Div.

1997-12-01

Phase stability in a ternary Nb-Cr-Ni Laves phase system was studied in this paper. Their previous study in NbCr{sub 2}-based transition-metal Laves phases has shown that the average electron concentration factor, e/a, is the dominating factor in controlling the phase stability of NbCr{sub 2}-based Laves phases when the atomic size ratios are kept identical. Since Ni has ten out-shell electrons, the substitution of Ni for Cr in NbCr{sub 2} will increase the average electron concentration of the alloy, thus leading to the change of the crystal structures from C15 to C14. In this paper, a number of pseudo-binary Nb(Cr,Ni){sub 2} alloys were prepared, and the crystal structures of the alloys after a long heat-treatment at 1000 C as a function of the Ni content were determined by the X-ray diffraction technique. The boundaries of the C15/C14 transition were determined and compared to their previous predictions. It was found that the electron concentration and phase stability correlation is obeyed in the Nb-Cr-Ni system. However, the e/a ratio corresponding to the C15/C14 phase transition was found to move to a higher value than the predicted one. The changes in the lattice constant, Vickers hardness and fracture toughness were also determined as a function of the Ni content, which were discussed in light of the phase stability difference of the alloys.

Precipitation sequences in austenitic Fe-22Cr-21Ni-6Mo-(N) stainless steels

International Nuclear Information System (INIS)

Kim, S.-J.; Lee, T.-H.

1999-01-01

Precipitation sequence of nitrogen containing Fe-22Cr-21Ni-6Mo-N austenitic stainless steel has been investigated after aging at high temperatures, and compared with nitrogen free steel. The σ phases and M 23 C 6 carbides were observed along the grain boundaries as well as in the matrix in both of the solution treated specimens. The M 6 C carbides and chi phase appeared successively in between 3 hours and 24 hours depending on the nitrogen content. Main difference in aging behavior was the precipitation of fine nitrides. Aging for 24 hours and 168 hours of nitrogen containing steel resulted in the formation of fine Cr 2 N and faceted AlN nitrides. The crystallography, structure and morphology were analyzed with analytical electron microscopy. (orig.)

On the corrosion testing of weldments of high alloyed CrNiMo-stainless steels and NiCrMo-alloys

International Nuclear Information System (INIS)

Riedel, G.; Voigt, C.; Werner, H.

1997-01-01

Weldments of high-alloyed CrNiMo stainless steels and NiCrMo alloys can be more susceptible to localized corrosion than the solution annealed basic material owing to segregations and precipitations in the heat affected zone, the high temperature zone and/or in the weld. To investigate these differences the FeCl 3 -test (10% FeCl 3 . 6aq), the test ''green death'' (11.5% H 2 SO 4 , 1.2% HCl, 1% CuCl 2 , 1% FeCl 3 ) as well as chronopotentiostatic tests in artificial sea water or in 3% NaCl-solution are used. In particular for testing the highest alloyed materials a CaCl 2 -test was developed (4.5 M CaCl 2 , chronopotentiostatic test in duration of 8 to 10 hours at + 200 mV (SCE)), which can be carried out to a temperature of 115 C at atmospheric pressure. The aggressivity increases in the range FeCl 3 -test, ''green death''-test, CaCl 2 -test. Matching and graduated over-alloyed weldments (TIG, heat input of 7 and 15.5 kJ/cm) of materials 1.4529, 1.4562, 2.4856, 2.4819 (german materials No.) are comparingly examined in various tests, of materials 1.4406, 1.4539, 1.4439 and 1.4563 (german materials No.) only matching weldments in the FeCl 3 -test. In strongly oxidizing media only a highly over-alloyed performed weldment (filler material 2.4607, german material No.) produces the best corrosion behaviour, measured as the critical temperatures of localized corrosion. Measurements of critical current densities of passivation can be used for investigations of corrosion behaviour of weldments, too. Critical current densities of passivation are showing a tendency to inverse proportion to the critical temperatures of localized corrosion. Suitable electrolytes are among others 0.2 M H 2 SO 4 + 1 M NaCl + 10 -3 % KSCN, N 2 -bubbled, 25 to 60 C and xM H 2 SO 4 + 4 M NaCl + 10 -3 % KSCN (x = 0.05 to 1), 25 C, in contact with air. An influence of heat input at the welding is indicated in the test of localized corrosion, but it is only small. It is sometimes more clearly shown at

Alloy Design and Development of Cast Cr-W-V Ferritic Steels for Improved High-Temperature Strength for Power Generation Applications

Energy Technology Data Exchange (ETDEWEB)

Klueh, R L; Maziasz, P J; Vitek, J M; Evans, N D; Hashimoto, N

2006-09-23

combination in COST CB2. To explore this question, nine more casting test blocks, four 3Cr steels and five 11Cr steels were purchased, and microstructure and mechanical properties studies similar to those described above for the first iteration of test blocks were conducted. Experimental results from the second iteration indicated that 11 Cr steels with excellent properties are possible. The 11Cr-1.5Mo-V-Nb steels were superior to 11Cr-2W-V-Ta steels, and it appears the former class of steels can be developed to have tensile and creep properties exceeding those of COST CB2. The W-Nb combination in an 11Cr-2W-V-Nb steel had tensile and short-time creep properties at 650 C better than the 11Cr-1.5Mo-V-Nb steels, although long-time low-stress properties may not be as good because of Laves phase formation. Based on the results, the next step in the development of improved casting steels involves acquisition of 11Cr-1.5Mo-V-Nb-N-B-C and 11Cr-2W-V-Nb-N-B-C steels on which long-term creep-rupture tests (>10,000 h) be conducted. For better oxidation and corrosion resistance, development of 11Cr steels, as opposed to a 9Cr steels, such as COST CB2, are important for future turbine designs that envision operating temperatures of 650 C.

Creep and Oxidation Behavior of Modified CF8C-Plus with W, Cu, Ni, and Cr

Science.gov (United States)

Unocic, Kinga A.; Dryepondt, Sebastien; Yamamoto, Yukinori; Maziasz, Philip J.

2016-04-01

The microstructures of modified CF8C-Plus (Fe-19Cr-12Ni-0.4W-3.8Mn-0.2Mo-0.6Nb-0.5Si-0.9C) with W and Cu (CF8CPWCu) and CF8CPWCu enhanced with 21Cr + 15Ni or 22Cr + 17.5Ni were characterized in the as-cast condition and after creep testing. When imaged at lower magnifications, the as-cast microstructure was similar among all three alloys as they all contained a Nb-rich interdendritic phase and Mn-based inclusions. Transmission electron microscopy (TEM) analysis showed the presence of nanoscale Cu-rich nanoprecipitates distributed uniformly throughout the matrix of CF8CPWCu, whereas in CF8CPWCu22/17, Cu precipitates were found primarily at the grain boundaries. The presence of these nanoscale Cu-rich particles, in addition to W-rich Cr23C6, nanoscale Nb carbides, and Z-phase (Nb2Cr2N2), improved the creep strength of the CF8CPWCu steel. Modification of CF8CPWCu with Cr and Ni contents slightly decreased the creep strength but significantly improved the oxidation behavior at 1073 K (800 °C). In particular, the addition of 22Cr and 17.5Ni strongly enhanced the oxidation resistance of the stainless steel resulting in a 100 degrees or greater temperature improvement, and this composition provided the best balance between improving both mechanical properties and oxidation resistance.

Effects of air melting on Fe/0.3/3Cr/0.5Mo/2Mn and Fe/0.3C/3Cr/0.5Mo/2Ni structural alloy steels

International Nuclear Information System (INIS)

Steinberg, B.

1979-06-01

Changing production methods of a steel from vacuum melting to air melting can cause an increase in secondary particles, such as oxides and nitrides, which may have detrimental effects on the mechanical properties and microstructure of the alloy. In the present study a base alloy of Fe/0.3C/3Cr/0.5Mo with either 2Mn or 2Ni added was produced by air melting and its mechanical properties and microstructure were compared to an identical vacuum melted steel. Significant differences in mechanical behavior, morphology, and volume fraction of undissolved inclusions have been observed as a function of composition following air melting. For the alloy containing manganese, all properties remained very close to vacuum melted values but the 2Ni alloy displayed a marked loss in Charpy impact toughness and plane strain fracture toughness. This loss is attributed to an increase in volume fraction of secondary particles in the nickel alloy, as opposed to both the Mn alloy and vacuum melted alloys, as well as to substaintially increased incidence of linear coalescence of voids. Microstructural features are discussed

Experimental study and modelling of high temperature creep flow and damage behaviour of 9Cr1Mo-NbV steel weldments

International Nuclear Information System (INIS)

Gaffard, V.

2004-12-01

Chromium martensitic stainless steels are under development since the 70's with the prospect of using them as structural components in thermal and nuclear power plants. The modified 9Cr1Mo-NbV steel is already used, especially in England and Japan, as a material for structural components in thermal power plants where welding is a commonly used joining technique. New generations of chromium martensitic stainless steels with improved mechanical properties for high pressure and temperature use are currently under development. However, observations of several in-service premature failures of welded components in 9Cr1Mo-NbV steel, outline a strong need for understanding the high temperature creep flow and damage behaviour of 9Cr1Mo-NbV steels and weldments. The present study aimed at experimentally determining and then modelling the high temperature creep flow and damage behaviour of both 9Cr1Mo-NbV steels and weldments (typically in the temperature range from 450 C to 650 C). The base metal was first studied as the reference material. It was especially evidenced that tempered chromium martensitic steels exhibit a change in both creep flow and damage behaviour for long term creep exposure. As a consequence, the classically performed extrapolation of 1,000 hours creep data to 100,000 hours creep lifetime predictions might be very hazardous. Based on experimental observations, a new model, integrating and coupling multiple creep flow and damage mechanisms, was developed in the framework of the mechanics of porous media. It was then successfully used to represent creep flow and damage behaviour of the base metal from high to low stress levels even for complex multiaxial loading conditions. Although the high temperature creep properties of the base metal are quite good, the occurrence of premature failure in weldments in high temperature creep conditions largely focused the attention of the scientific community. The lower creep strength of the weld component was also

The effects of minor alloy modifications and heat treatment on the microstructure and creep rupture behavior of 2.25Cr-1Mo Steel

International Nuclear Information System (INIS)

Todd, J.A.; Chung, D.W.; Parker, E.R.

1983-01-01

The effects of alloy additions on the microstructure of simulated cooled and tempered 2.25Cr-1Mo steels have been studied using transmission electron microscopy. Carbide precipitation sequences have been identified in the modification 3Cr-1Mo-1Mn-1Ni and compared to those in 2.25Cr-1Mo steels modified with Mn and Ni and also with Ti, V and B. The influence of minor compositional changes on the creep rupture behavior of 2.25Cr-1Mo steel has been studied at 500 C, 560 C, and 600 C. The most significant effect of alloy modifications on creep properties resulted from additions of Mn and Cr. Preliminary studies show that 1% Mn and 0.5Mn + 1Ni + 0.75Cr additions significantly reduce creep strength at all three temperatures for tests up to 2000 hours duration. The 3Cr-1Mo-1Mn-1Ni steel showed improvements in rupture ductility at all temperatures when compared with the base 2.25Cr-1Mo steel and the manganese-nickel modifications. Plots of the Larson-Miller parameter for both these modifications lay within the scatter band for commercial 2.25Cr-1Mo steels

A new methodology based on ultrasonic attenuation to characterize dynamically recrystallized microstructure in a 15Cr-15Ni-2.2Mo-Ti modified austenitic stainless steel

International Nuclear Information System (INIS)

Mandal, S.; Kumar, A.; Sivaprasad, P.V.; Jayakumar, T.; Baldev Raj; Kumar, S.; Samajdar, I.

2010-01-01

In this study, a C-scan ultrasonic imaging system has been employed for imaging the microstructural variations during dynamic recrystallization (DRX) of a 15Cr-15Ni-2.2Mo-Ti modified austenitic stainless steel. Four specimens were forged at 1273 K for different strains in the range of 0.1-0.5. It has been observed that the specimen with 0.2 strain or lower did not show any variation in the amplitude of the first backwall echo. However, at and above 0.3 strain, a visible variation in the C-scan images has been observed. This variation has been attributed to the evolution of fine grains. The formation of fine grains, on the other hand, was related to DRX, as indicated by electron back scattered diffraction (EBSD). (author)

The creep and stress-rupture behaviour under internal pressure of tubes made from austenitic stainless steel X8 CrNiMoNb 1616 (Material No. 1.4981)

International Nuclear Information System (INIS)

Schaefer, L.; Polifka, F.; Kempe, H.

1979-05-01

Creep and stress rupture tests have been performed at 600, 650, 700 and 750 0 C on tubes made from three different heats from the austenitic stainless steel X8 CrNiMoNb 1616 (Material No. 1.4981). The tubes were loaded by internal pressure and the tangential (hoop) creep strain was measured continuously. The results are presented in form of creep curves, stress-time to rupture curves and curves for a creep limit. The average and minimum creep rates as a function of the applied stress have been evaluated and are described with a creep law analogous to Norton's creep law. An interpolation and extrapolation of the stress-rupture-strength and the creep strength are possible using the time-temperature-parameter-plot after Larson and Miller. (orig.) [de

Microstructure investigation of NiAl-Cr(Mo) interface in a directionally solidified NiAl-Cr(Mo) eutectic alloyed with refractory metal

International Nuclear Information System (INIS)

Chen, Y.X.; Cui, C.Y.; Guo, J.T.; Li, D.X.

2004-01-01

The microstructure of a directionally solidified NiAl-Cr(Mo) eutectic alloyed with refractory metal in as-processed and heat-treated states has been studied by means of scanning electron microscopy and high resolution electron microscopy (HREM). The microstructure of the NiAl-Cr(Mo) eutectic was characterized by lamellar Cr(Mo) phases embedded within NiAl matrix with common growth direction of . The interface between NiAl and lamellar Cr(Mo) did not have any transition layers. Misfit dislocations were observed at the NiAl-Cr(Mo) interface. In addition to lamellar Cr(Mo) phases, coherent Cr(Mo, Ni, Al) precipitates and NiAl precipitates were also observed in the NiAl matrix and lamellar Cr(Mo) phases, respectively. After hot isostatic pressing and heat treatment, the NiAl-Cr(Mo) interfaces became smooth and straight. Square array of misfit dislocations was directly observed at the (0 0 1) interface between NiAl and Cr(Mo, Ni, Al) precipitate. The configuration of misfit dislocation network showed a generally good agreement with prediction based on the geometric O-lattice model

Effects of the Microstructure on Segregation behavior of Ni-Cr-Mo High Strength Low Alloy RPV Steel

Energy Technology Data Exchange (ETDEWEB)

Park, Sang Gyu; Wee, Dang Moon [Korea Advanced Institute of Science and Technology, Daejeon (Korea, Republic of); Kim, Min Chul; Lee, Bong Sang [Korea Atomic Energy Research Institute, Daejeon (Korea, Republic of)

2010-10-15

SA508 Gr.4N Ni-Cr-Mo low alloy steel has an improved fracture toughness and strength, compared to commercial Mn-Mo-Ni low alloy RPV steel SA508 Gr.3. Higher strength and fracture toughness of low alloy steels could be achieved by adding Ni and Cr. So there are several researches on SA508 Gr.4N low alloy steel for a RPV application. The operation temperature and time of a reactor pressure vessel is more than 300 .deg. C and over 40 years. Therefore, in order to apply the SA508 Gr.4N low alloy steel for a reactor pressure vessel, it requires a resistance of thermal embrittlement in the high temperature range including temper embrittlement resistance. S. Raoul reported that the susceptibility to temper embrittlement was increasing a function of the cooling rate in SA533 steel, which suggests the martensitic microstructures resulting from increased cooling rates are more susceptible to temper embrittlement. However, this result has not been proved yet. So the comparison of temper embrittlement behavior was made between martensitic microstructure and bainitic microstructure with a viewpoint of boundary features in SA508 Gr.4N, which have mixture of tempered bainite/martensite. In this study, we have compared temper embrittlement behaviors of SA508 Gr.4N low alloy steel with changing volume fraction of martensite. The mechanical properties of these low alloy steels) were evaluated after a long-term heat treatment(450 .deg. C, 2000hr. Then, the images of the segregated boundaries were observed and segregation behavior was analyzed by AES. In order to compare the misorientation distributions of model alloys, grain boundary structures were measured with EBSD

Effect of Cavitation on Surface Damage of 16.7Cr-10Ni-2Mo Stainless Steel in Marine Environment

Energy Technology Data Exchange (ETDEWEB)

Chong, Sang-Ok; Han, Min-Su; Kim, Seong-Jong [Mokpo National Maritime University, Mokpo (Korea, Republic of)

2015-10-15

Stainless steel is generally known to have characteristics of excellent corrosion resistance and durability, but in a marine environment it can suffer from localized corrosion due to the breakdown of passivity film due to chloride ion in seawater. Furthermore, the damage behaviors are sped up under a cavitation environment because of complex damage from electrochemical corrosion and cavitation-erosion. In this study the characteristics of electrochemical corrosion and cavitation erosion behavior were evaluated on 16.7Cr-10Ni-2Mo stainless steel under a cavitation environment in natural seawater. The electrochemical experiments have been conducted at both static conditions and dynamic conditions inducing cavitation with different current density parameters. The surface morphology and damage behaviors were compared after the experiment. After the cavitation test with time variables morphological examinations on damaged specimens were analyzed by using a scanning electron microscope and a 3D microscope. the galvanostatic experiment gave a cleaner surface morphology presented with less damage depth at high current density regions. It is due to the effect of water cavitation peening under the cavitation condition. In the cavitation experiment, with amplitude of 30 μm and seawater temperature of 25 ℃, weight loss and cavitation-erosion damage depth were dramatically increased after 5 hours inducing cavitation.

NbCl 5 and CrCl 3 catalysts effect on synthesis and hydrogen ...

Indian Academy of Sciences (India)

Two kinds of novel materials, Mg–1.6 mol% Ni–0.4 mol% NiO–2 mol% MCl (MCl = NbCl5, CrCl3), along with Mg–1.6 mol% Ni–0.4 mol% NiO for comparison, were examined for their potential use in hydrogen storage applications, having been fabricated via cryomilling. The effects of NbCl5 and CrCl3 on hydrogen storage ...

Effect of load ratio and saltwater corrosive environment on the initiation life of fatigue of 10Ni5CrMoV steel

Science.gov (United States)

Xie, Xing; Yi, Hong; Xu, Jian; Gen, Liming; Chen, Luyun

2017-09-01

Fatigue initiation life has been studied with 10CrNi5MoV steel for use in ocean engineering at different load ratios and in different environmental media. The microstructure and micro-topography have been observed and analyzed by means of SEM, EDS and EBSD. Our findings indicate that, the initiation life of 10Ni5CrMoV steel in seawater is shorter than that in air, and the difference in longevity is larger with the increasing of load ratio. Corrosion pits had a great influence on initial corrosion fatigue life.

Evaluation of rolling contact fatigue of induction heated 13Cr-2Ni-2Mo Stainless steel bar with Si3N4-ball

Science.gov (United States)

Yadoiwa, Ariyasu; Mizobe, Koshiro; Kida, Katsuyuki

2018-03-01

13Cr % martensitic stainless steels were used in various industry, because they have excellent corrosion resistance and high hardness among other stainless steels. They are also expected as a bearing material, however, the research on rolling contact fatigue (RCF) is not enough. In this study, 13Cr-2Ni-2Mo stainless steels were quenched by induction heating and their RCF lives were evaluated. A Si3N4-ball was used in order to apply higher stress (Pmax = 5.6 GPa) than our previous tests (Pmax=5.3 GPa), in a single-ball RCF testing machine. It was found that the basic life (L10) was 2.20×106 cycles and Median life (L50) was 6.04×106 cycles. In addition, Weibull modulus became higher than the previous tests.

Microchemistry of neutron irradiated 12%CrMoVNb martensitic steel

International Nuclear Information System (INIS)

Little, E.A.; Morgan, T.S.; Faulkner, R.G.

1992-01-01

Non-equilibrium solute segregation has been studied in a 12%CrMoVNb martensitic steel following fast reactor irradiation at 465 C and correlated with the development of M 6 X η-phase. Cr, Ni, Si, Mo, P and Mn are all shown to exhibit positive segregation to lath boundaries and are subsequently incorporated into M 6 X precipitates. The co-segregation of a combination of these elements which include P and Si, and possibly Cr or Mo, appears to promote M 6 X formation

High Nb, Ta, and Al creep- and oxidation-resistant austenitic stainless steel

Science.gov (United States)

Brady, Michael P [Oak Ridge, TN; Santella, Michael L [Knoxville, TN; Yamamoto, Yukinori [Oak Ridge, TN; Liu, Chain-tsuan [Oak Ridge, TN

2010-07-13

An austenitic stainless steel HTUPS alloy includes, in weight percent: 15 to 30 Ni; 10 to 15 Cr; 2 to 5 Al; 0.6 to 5 total of at least one of Nb and Ta; no more than 0.3 of combined Ti+V; up to 3 Mo; up to 3 Co; up to 1 W; up to 0.5 Cu; up to 4 Mn; up to 1 Si; 0.05 to 0.15 C; up to 0.15 B; up to 0.05 P; up to 1 total of at least one of Y, La, Ce, Hf, and Zr; less than 0.05 N; and base Fe, wherein the weight percent Fe is greater than the weight percent Ni wherein said alloy forms an external continuous scale comprising alumina, nanometer scale sized particles distributed throughout the microstructure, said particles comprising at least one composition selected from the group consisting of NbC and TaC, and a stable essentially single phase fcc austenitic matrix microstructure, said austenitic matrix being essentially delta-ferrite-free and essentially BCC-phase-free.

Fatigue damage evolution of cold-worked austenitic nickel-free high-nitrogen steel X13CrMnMoN18-14-3 (1.4452)

Energy Technology Data Exchange (ETDEWEB)

Tikhovskiy, I.; Weiss, S.; Fischer, A. [Univ. of Duisburg-Essen, Materials Science and Engineering II, Duisburg (Germany)

2004-07-01

Due to the fact that the risk of Ni-allergies becomes more and more important for modern therapies, the necessity of Ni-free implant materials becomes increasingly important. Beside Co- and Ti-base alloys Ni-free high-nitrogen steels may offer an attractive alternative. The present work presents the austenitic high-nitrogen and nickel-free steel X13CrMnMoN18-14-3, (Material No.: 1.4452) after 20% cold-working. In addition this material was deformed under axial cyclic total strain controlled fatigue tests at room temperature. The development of dislocation structure due to different loading amplitudes was compared to none cyclically deformed material. The good mechanical und fatigue properties of these austenitic high-nitrogen steels as well as the better tribological, chemical and biological properties compared to CrNiMo-steels qualify these steels as a promising alternative in medical applications. (orig.)

Effects of nickel and cobalt addition on creep strength and microstructure of the precipitation-strengthened 15Cr ferritic steels

Energy Technology Data Exchange (ETDEWEB)

Shibuya, Masachika; Toda, Yoshiaki; Sawada, Kota; Kushima, Hideaki; Kimura, Kazuhiro [National Inst. for Materials Science, Tsukuba, Ibaraki (Japan)

2010-07-01

Creep strength of 15Cr ferritic steel with ferrite matrix was increased by precipitation strengthening of intermetallic compounds. It was higher than those of 9-12Cr ferritic steels with a tempered martensitic microstructure strengthened by carbide and carbonitride. Addition of nickel was confirmed to improve Charpy impact toughness of the 15Cr steels, however, creep strength was slightly reduced by the addition of nickel. Microstructure of the 15Cr steel changes from ferrite single phase to dual phases of ferrite and martensite with the addition of nickel which is an austenite stabilizing element. The 15Cr steels investigated in the previous study, contain 3mass% of cobalt which is also an austenite stabilizing element, therefore, the influence of nickel and cobalt combination on mechanical properties and microstructure of the 15Cr-1Mo-6W-V-Nb steel is investigated in this study. Creep strength, Charpy impact toughness and microstructure of the steel were strongly influenced by the composition of nickel and cobalt. Design guideline of the 15Cr steel is discussed with respect to a role of microstructure and combination of nickel and cobalt addition. (orig.)

Technology development and production of elongated shell for reactor vessel active zone of WWER-TOI project from steel 15Cr2NiMoVN class 1

International Nuclear Information System (INIS)

Shklyaev, S.Eh.; Titova, T.I.; Ratushev, D.V.; Shul'gan, N.A.; Eroshkin, S.B.; Durynin, V.A.; Efimov, S.V.; Dub, V.S.; Kulikov, A.P.; Romashkin, A.N.

2015-01-01

Production process for the elongated shell blank of the active zone of the reactor pressure vessel made from steel 15Cr2NiMoVN Class 1 with finished sizes Dext=4.655 mm, Dint=4.240 mm, H=4.910 mm (height for heat treatment – 5.750 mm) is presented. For the first time in Russia in production site of OMZ-Special steel LLC a unique elongated shell blank of the reactor vessel active zone was made from ingot 420.0 t for WWER-TOI project fully meeting the specified requirements in terms of metallurgical quality and set of service properties [ru

Impact of saline aquifer water on surface and shallow pit corrosion of martensitic stainless steels during exposure to CO2 environment (CCS)

Science.gov (United States)

Pfennig, Anja; Kranzmann, Axel

2018-05-01

Pipe steels suitable for carbon capture and storage technology (CCS) require resistance against the corrosive environment of a potential CCS-site, e.g. heat, pressure, salinity of the aquifer, CO2-partial pressure. Samples of different mild and high alloyed stainless injection-pipe steels partially heat treated: 42CrMo4, X20Cr13, X46Cr13, X35CrMo4 as well as X5CrNiCuNb16-4 were kept at T=60 °C and ambient pressure as well as p=100 bar for 700 h - 8000 h in a CO2-saturated synthetic aquifer environment similar to possible geological on-shore CCS-sites in the northern German Basin. Main corrosion products are FeCO3 and FeOOH. Corrosion rates obtained at 100 bar are generally much lower than those measured at ambient pressure. Highest surface corrosion rates are 0.8 mm/year for 42CrMo4 and lowest 0.01 mm/year for X5CrNiCuNb16-4 in the vapour phase at ambient pressure. At 100 bar the highest corrosion rates are 0.01 mm/year for 42CrMo4, X20Cr13 (liquid phase), X46Cr13 and less than 0.01 mm/year for X35CrMo4 and X5CrNiCuNb16-4 after 8000 h of exposure with no regard to atmosphere. Martensitic microstructure offers good corrosion resistance.

The influence of cerium and yttrium ion implantation upon the oxidation behaviour of a 20% Cr/25% Ni/Nb stabilised stainless steel, in carbon dioxide, at 8250C

International Nuclear Information System (INIS)

Bennett, M.J.; Dearnaley, G.; Houlton, M.R.; Hawes, R.W.M.

1982-01-01

The influence of cerium and yttrium ion implantation upon the oxidation behaviour of a 20% Cr/25% Ni niobium stabilised stainless steel during up to 7 157h exposure to carbon dioxide, at 825 0 C has been examined. The doses ranged between 5 x 10 14 and 10 17 ions cm -2 . Above thresholds of between 5 x 10 14 and 5 x 10 15 yttrium and between 5 x 10 15 and 10 16 cerium ions cm -2 the implantation of both elements improved the oxidation resistance of the 20/25/Nb steel. Yttrium exerted the greater influence, reducing by a factor of two the attack after 7 157h. Up to 80% of the oxide formed on the 20/25/Nb steel spalled, particularly on thermal cycling. Cerium and yttrium implantation improved oxide adhesion by similar extents, which increased with ion dose such that with the highest doses, no spallation was measurable. The effect of the implanted elements derived from their incorporation within the oxide film. It was initiated by their promotion of the formation of an initial chromium-rich oxide layer, which had a finer grain size than that formed on the 20/25/Nb steel. Reduction in continuing attack was associated in part, with improved oxide adhesion, as this decreased the significant contribution to the attack of the 20/25/Nb steel from the reoxidation of spalled areas. (author)

Creep and time to rupture of a 16/16 Cr Ni Steel

International Nuclear Information System (INIS)

Solano, R.; Garcia, R.; Bohm, H.; Schirra, M.

1972-01-01

The influence of different thermal-mechanical treatments on the creep and time to rupture of a 16/16 Cr.Ni steel is studied. The solution treated material after annealing at 700-800 degree centigree did not affect time to rupture. At the contrary a 12% cold-working and annealing at 800 degree centigree improve the time to rupture. This treatment is preserved up to 700 degree centigree 10 4 hours. The ductility is not strongly affected. A metallographic study of the fracture was carried out. (Author) 23 refs

Studies on the influence of processing methods on the corrosion characteristics of electroslag-tape-plating with NiMo16Cr16Ti. Untersuchungen zum Einfluss der Prozessfuehrung auf die Korrosionseigenschaften beim Elektroschlacke-Bandplattieren mit NiMo16Cr16Ti

Energy Technology Data Exchange (ETDEWEB)

Blum, J

1991-01-01

The aim of the project was to demonstrate an economic possibility of using NiMo16Cr16Ti reliably as a plating material with simple to use methods. For this, the electroslag and submerged arc welding with tape electrodes as a coating technology are compared with each other. As the research showed, it is possible to coat large surface area, thick walled components economically with NiMo16Cr16Ti using electroslag (RES) tape plating. The choice of powder is important for the hot crack freedom and the precipitation poverty and thus the corrosion resistance of the plating. The silicon content was proved to be of importance in the plating. With the right choice of powder, the second layer already possesses the endurance of laminated materials against intercrystalline corrosion in coating tests as well as against pitting in a 10% FeCl{sub 3} solution. The coating capability lies at 0.5 m{sup 2}/h. - In addition the use of video thermography for on-line surveillance of seam on RES plates is documented. The evaluation of the pictures makes possible the targeting of the external magnets and thus the influencing of the melting bath flux. (orig./RHM) With 80 figs., 12 tabs.

Kinetics of steel corrosion in water

International Nuclear Information System (INIS)

Vettegren', V.I.; Bashkarev, A.Ya.; Danchukov, K.G.; Morozov, G.I.

2003-01-01

Kinetics of corrosion damage accumulation in steels of different composition (Cr-Ni-Mo-Ti, Cr-Ni-Mn-N-V, Cr-Ni-N-Mn-Mo, Cr-Ni-Nb, Cr-Ni-Ti, Cr-Mn-Ni, Mn-Al-Nb-Si, Mn-Cr-Al-Si and Mn-Al-Si) in NaCl solution and in sea water was studied. It is shown that degree of corrosion damage relates to time according to the first order reaction expression. The values of corrosion activation energy and of parameter characterizing protection properties of corrosion film are determined [ru

Application of newly developed heat resistant materials for USC boilers

International Nuclear Information System (INIS)

Sato, T.; Tamura, K.; Fukuda, Y.; Matsuda, J.

2004-01-01

This paper describes the research on the development and improvement of new high strength heat resistant steels such as SUPER304H (18Cr-9Ni-3Cu-Nb-N), NF709 (20Cr-25Ni-1.5Mo-Nb-Ti-N) and HR3C (25Cr-20Ni-Nb-N) as boiler tube, and NF616 (9Cr-0.5Mo-1.8W-Nb-V) and HCM12A (11Cr-0.4Mo-2W-Nb-V-Cu) as thick section pipe. The latest manufacturing techniques applied for these steels are introduced. In addition the high temperature strength of Alloy617 (52Ni-22Cr-13Co-9Mo-Ti-Al) that is one of the candidate materials for the next generation 700 □ USC boilers is described. (orig.)

Stress corrosion cracking in repair-welded 3.5 NiCrMoV steel in an actual turbine environment

International Nuclear Information System (INIS)

Hitomi, Itoh; Takashi, Shige; Takashi, Momoo

2001-01-01

Temporary welding repairs are sometimes needed when damage occurs at the teeth of blade grooves in a low-pressure turbine rotor operated at the dry/wet boundary region. When repair welding has been performed for the 3,5 NiCrMoV steel used in low-pressure turbines, the soundness of the weld must be confirmed. For this reason, a laboratory investigation of susceptibility for stress corrosion cracking (SCC) was conducted for test specimens taken from simulated welds, and then an exposure test was conducted in an actual turbine environment for approximately 7,000 hours. As no SCC initiation was detected and also the propagation was extremely small, repair welding is deemed to be applicable. (author)

Hot Deformation Behavior of 1Cr12Ni3Mo2VN Martensitic Stainless Steel

Science.gov (United States)

He, Xiaomao; Jiang, Peng; Zhou, Leyu; Chen, Chao; Deng, Xiaochun

2017-08-01

1Cr12Ni3Mo2VN is a new type of martensitic stainless steel for the last-stage blades of large-capacity nuclear and thermal power turbines. The deformation behavior of this steel was studied by thermal compression experiments that performed on a Gleeble-3500 thermal simulator at a temperature range of 850°C to 1200°C and a strain rate of 0.01s-1 to 20s-1. When the deformation was performed at high temperature and low strain rate, a necklace type of microstructures was observed, the plastic deformation mechanism is grain boundary slip and migration, when at low temperature and lower strain rate, the slip bands were observed, the mechanism is intracrystalline slips, and when at strain rate of 20s-1, twins were observed, the mechanism are slips and twins. The Arrhenius equation was applied to describe the constitutive equation of the flow stress. The accuracy of the equation was verified by using the experimental data and the correlation coefficient R2 = 0.9786, and the equation can provide reasonable data for the design and numerical simulation of the forging process.

Effect of ETA treatment on corrosion fatigue in rotors and blades and stress corrosion cracking in 3.5 NiCrMoV steel low-pressure turbine discs

International Nuclear Information System (INIS)

Hitomi, Itoh; Takashi, Momoo; Takayuki, Shiomi

2001-01-01

In recent years, to increase the reliability and reduce the amount of feed water iron to prevent of fouling of steam generator tubes, ethanolamine (ETA) treatment has been adopted into the secondary system. In this investigation, the authors verified that ethanolamine treatment does not adversely affect the susceptibility of either stress corrosion cracking (SCC) in the turbine discs that are the principal units in the secondary system or corrosion fatigue (CF) in rotors and blades. In the first stage, a laboratory investigation was made of (1) SCC initiation and propagation in 3,5 NiCrMoV steel and (2) CF in 3,5 NiCrMoV steel and blade steels, in both cases using deaerated water to which had been added ethanolamine with few organic acids that is 10 times the estimated concentration. It was confirmed that the ethanolamine treatment had almost no effect. In the second stage, test pieces (removed from the disc steel inserted into the turbine extraction chamber before the ethanolamine treatment was started) were used to observe the initiation and propagation of SCC. Even after long-term observation, ethanolamine treatment into the secondary system was found to have almost no effect on the susceptibility of SCC in discs. (author)

Composition design of superhigh strength maraging stainless steels using a cluster model

Directory of Open Access Journals (Sweden)

Zhen Li

2014-02-01

Full Text Available The composition characteristics of maraging stainless steels were studied in the present work investigation using a cluster-plus-glue-atom model. The least solubility limit of high-temperature austenite to form martensite in basic Fe–Ni–Cr corresponds to the cluster formula [NiFe12]Cr3, where NiFe12 is a cuboctahedron centered by Ni and surrounded by 12 Fe atoms in FCC structure and Cr serves as glue atoms. A cluster formula [NiFe12](Cr2Ni with surplus Ni was then determined to ensure the second phase (Ni3M precipitation, based on which new multi-component alloys [(Ni,Cu16Fe192](Cr32(Ni,Mo,Ti,Nb,Al,V16 were designed. These alloys were prepared by copper mould suction casting method, then solid-solution treated at 1273 K for 1 h followed by water-quenching, and finally aged at 783 K for 3 h. The experimental results showed that the multi-element alloying results in Ni3M precipitation on the martensite, which enhances the strengths of alloys sharply after ageing treatment. Among them, the aged [(Cu4Ni12Fe192](Cr32(Ni8.5Mo2Ti2Nb0.5Al1V1 alloy (Fe74.91Ni8.82Cr11.62Mo1.34Ti0.67Nb0.32Al0.19V0.36Cu1.78 wt% has higher tensile strengths with YS=1456 MPa and UTS=1494 MPa. It also exhibits good corrosion-resistance in 3.5 wt% NaCl solution.

Porous p-NiO/n-Nb{sub 2}O{sub 5} nanocomposites prepared by an EISA route with enhanced photocatalytic activity in simultaneous Cr(VI) reduction and methyl orange decolorization under visible light irradiation

Energy Technology Data Exchange (ETDEWEB)

Hashemzadeh, Fatemeh, E-mail: Fa.hashemzadeh@gmail.com [Young Researchers and Elite Clube, Marand Branch, Islamic Azad University, Marand (Iran, Islamic Republic of); Gaffarinejad, Ali, E-mail: Ghaffarinejad@iust.ac.ir [Department of Chemistry, Iran University of Science and Technology, Tehran 16846-13114 (Iran, Islamic Republic of); Rahimi, Rahmatollah, E-mail: Rahimi_Rah@iust.ac.ir [Department of Chemistry, Iran University of Science and Technology, Tehran 16846-13114 (Iran, Islamic Republic of)

2015-04-09

Highlights: • EISA synthesis of NiO/Nb{sub 2}O{sub 5} composites (NiNbx; x = Ni/Nb = 0.0, 0.4, 0.8, 1.2). • 200–400 nm extension in absorption edge to visible region compared to NiNb0.0. • Simultaneous Cr(VI)–MO redox photoreactions on NiNbx in visible light at pH 2. • NiNb0.4, the most active sample, due to low E{sub g} & e{sup −}–h{sup +} separation by p–n junction. • More efficiency of Cr(VI)–MO system than that of single ones, showing synergism effect. - Abstract: Porous NiO/Nb{sub 2}O{sub 5} nanocomposites with Ni/Nb molar ratio of 0.4, 0.8 and 1.2 have been obtained via the EISA route using P123 copolymer as organic template, and are assigned as NiNb0.4, NiNb0.8 and NiNb1.2, respectively. For comparison, pure Nb{sub 2}O{sub 5} sample assigned as NiNb0.0 was also synthesized by the same method. Structural and textural features of the as prepared samples were investigated by XRD, FTIR, FE-SEM, EDX, UV–vis DRS and BET techniques. The results indicated that the porous p-NiO/n-Nb{sub 2}O{sub 5} junction nanocomposites were formed and coupling of NiO with Nb{sub 2}O{sub 5} resulted a remarkable red shift in the optical response of the nanocomposite samples. The photocatalytic properties of the nanocomposite samples, and also synthesized pure Nb{sub 2}O{sub 5} (NiNb0.0) and commercial Nb{sub 2}O{sub 5} as reference catalysts were evaluated for the first time by simultaneous Cr(VI) reduction and MO decolorization in aqueous suspension under visible light irradiation at pH 2. NiNb0.4 was found to be the most active photocatalyst, which might be attributed to the extended absorption in the visible light region and the effective photogenerated electron–hole separation by the photosynergistic effects of the p-NiO/n-Nb{sub 2}O{sub 5} composite powder. The photocatalytic efficiency of the most active photocatalyst, NiNb0.4, was found to be rather low for either single Cr(VI) solution or single MO solution. However, the photocatalytic reduction of

Effect of Carbide Dissolution on Chlorine Induced High Temperature Corrosion of HVOF and HVAF Sprayed Cr3C2-NiCrMoNb Coatings

Science.gov (United States)

Fantozzi, D.; Matikainen, V.; Uusitalo, M.; Koivuluoto, H.; Vuoristo, P.

2018-01-01

Highly corrosion- and wear-resistant thermally sprayed chromium carbide (Cr3C2)-based cermet coatings are nowadays a potential highly durable solution to allow traditional fluidized bed combustors (FBC) to be operated with ecological waste and biomass fuels. However, the heat input of thermal spray causes carbide dissolution in the metal binder. This results in the formation of carbon saturated metastable phases, which can affect the behavior of the materials during exposure. This study analyses the effect of carbide dissolution in the metal matrix of Cr3C2-50NiCrMoNb coatings and its effect on chlorine-induced high-temperature corrosion. Four coatings were thermally sprayed with HVAF and HVOF techniques in order to obtain microstructures with increasing amount of carbide dissolution in the metal matrix. The coatings were heat-treated in an inert argon atmosphere to induce secondary carbide precipitation. As-sprayed and heat-treated self-standing coatings were covered with KCl, and their corrosion resistance was investigated with thermogravimetric analysis (TGA) and ordinary high-temperature corrosion test at 550 °C for 4 and 72 h, respectively. High carbon dissolution in the metal matrix appeared to be detrimental against chlorine-induced high-temperature corrosion. The microstructural changes induced by the heat treatment hindered the corrosion onset in the coatings.

Shot Peening Effects on Subsurface Layer Properties and Fatigue Performance of Case-Hardened 18CrNiMo7-6 Steel

Directory of Open Access Journals (Sweden)

H. S. Ho

2018-01-01

Full Text Available The present study is conducted with a dual-aim: firstly, to examine the effect of several single shot peening conditions on the subsurface layer properties and fatigue performance of the case-hardened 18CrNiMo7-6 steel, and secondly, to propose an optimized peening condition for improved fatigue performance. By carrying out the subsurface integrity analysis and fatigue testing, the underlying relationships among the peening process, subsurface layer property and fatigue performance are investigated, the way peening conditions affect the fatigue life and its associated scatter for the case-hardened 18CrNiMo7-6 steel is quantitatively assessed. The in-depth study shows that dual peening can be an optimized solution, for it is able to produce a subsurface layer with enhanced properties and eventually gain a significant improvement in fatigue performance.

Phase transformation in a Ni-Mo-Cr alloy

International Nuclear Information System (INIS)

Dymek, S.; Wrobel, M.; Blicharski, M.; Dollar, M.

2001-01-01

The paper gives a characteristic of a nickel-based superalloy containing 25 wt.% Mo and 8 wt.% Cr with particular attention to the influence of a thermochemical and heat treatment on phase transformations. The applied heat treatments are comprised of soaking temperature 1100 o C followed by aging at 650 o C at three conditions: conventional aging for 72 hours, prolonged aging for 4000 hours and prolonged aging for 4000 hours followed by cold working and subsequent aging for 1000 hours. The conventional aging led to the formation of lenticular precipitates of the dispersed metastable Ni 2 (Mo,Cr) phase. The aging for 4000 hours brought about coarsening of the ordered domains without changing their crystallographic and ordering characteristics. The plastic deformation preceded the further aging for 1000 hours accelerated the decomposition of the Ni 2 (Mo,Cr) phase on the mixture of the Ni 3 Mo and Ni 4 Mo-based phases. (author)

Experimental study and modelling of high temperature creep flow and damage behaviour of 9Cr1Mo-NbV steel weldments; Etude experimentale et modelisation, du comportement, de l'endommagement et de la rupture en fluage a haute temperature de joint soudes en acier 9Cr1Mo-NbV

Energy Technology Data Exchange (ETDEWEB)

Gaffard, V

2004-12-15

Chromium martensitic stainless steels are under development since the 70's with the prospect of using them as structural components in thermal and nuclear power plants. The modified 9Cr1Mo-NbV steel is already used, especially in England and Japan, as a material for structural components in thermal power plants where welding is a commonly used joining technique. New generations of chromium martensitic stainless steels with improved mechanical properties for high pressure and temperature use are currently under development. However, observations of several in-service premature failures of welded components in 9Cr1Mo-NbV steel, outline a strong need for understanding the high temperature creep flow and damage behaviour of 9Cr1Mo-NbV steels and weldments. The present study aimed at experimentally determining and then modelling the high temperature creep flow and damage behaviour of both 9Cr1Mo-NbV steels and weldments (typically in the temperature range from 450 C to 650 C). The base metal was first studied as the reference material. It was especially evidenced that tempered chromium martensitic steels exhibit a change in both creep flow and damage behaviour for long term creep exposure. As a consequence, the classically performed extrapolation of 1,000 hours creep data to 100,000 hours creep lifetime predictions might be very hazardous. Based on experimental observations, a new model, integrating and coupling multiple creep flow and damage mechanisms, was developed in the framework of the mechanics of porous media. It was then successfully used to represent creep flow and damage behaviour of the base metal from high to low stress levels even for complex multiaxial loading conditions. Although the high temperature creep properties of the base metal are quite good, the occurrence of premature failure in weldments in high temperature creep conditions largely focused the attention of the scientific community. The lower creep strength of the weld component was also

Crystallography of sigma phase precipitation in superaustenitic Fe-22Cr-21Ni-6Mo-0.3N stainless steels

International Nuclear Information System (INIS)

Lee, Tae Ho; Jung, Yun Chul; Kim, Sung Joon

1999-01-01

The crystallographic features of sigma phase precipitation in super austenitic Fe-22Cr-21Ni-6Mo-(0.3N) stainless steels during isothermal aging were investigated utilizing transmission electron microscopy. The sigma phase precipitated along the austenite grain boundaries even after solution treatment due to higher Mo contents and remained stable throughout aging at 900 .deg. C up to 168 hours. The sigma phase observed in this study was found to be ternary Fe-Cr-Mo sigma phase and had tetragonal structure with lattice parameters of a=9.17A and c=4.74A. The orientation relationships between the sigma phase and austenite were determined from the analyses of selected area diffraction patterns taken by various zone axes and stereo graphic analyses. The orientation relationships between sigma and austenite phases obtained in this study were as follows; 1) (110) γ ll (110) σ , [111] γ ll [001] σ and (112) γ ll (110) σ , [111] γ ll [001] σ and 2) (110) γ ll (110) σ , [112] γ ll [113] σ and (111) γ ll (332) σ , [112] γ ll [113] σ . However, the former orientation relationship was predominant throughout aging and the latter orientation relationship was scarcely observed in very limited aging condition

Low-cost, high-strength Fe--Ni--Cr alloys for high temperature exhaust valve application

Science.gov (United States)

Muralidharan, Govindarajan

2017-09-05

An Fe--Ni--Cr alloy is composed essentially of, in terms of wt. %: 2.4 to 3.7 Al, up to 1.05 Co, 14.8 to 15.9 Cr, 25 to 36 Fe, up to 1.2 Hf, up to 4 Mn, up to 0.6 Mo, up to 2.2 Nb, up to 1.05 Ta, 1.9 to 3.6 Ti, up to 0.08 W, up to 0.03 Zr, 0.18 to 0.27 C, up to 0.0015 N, balance Ni, wherein, in terms of atomic percent: 8.5.ltoreq.Al+Ti+Zr+Hf+Ta.ltoreq.11.5, 0.53.ltoreq.Al/(Al+Ti+Zr+Hf+Ta).ltoreq.0.65, and 0.16.ltoreq.Cr/(Fe+Ni+Cr+Mn).ltoreq.0.21, the alloy being essentially free of Cu, Si, and V.

Soft-martensitic stainless Cr-Ni-Mo steel for turbine rotors in geothermic power stations

International Nuclear Information System (INIS)

Schonfeld, K.; Potthast, E.

1986-01-01

Steel Grade X5 Cr-Ni-Mo 12 6 containing 0.05% carbon, 12% chromium, 6% nickel, and 1.50% molybdenum is an advantageous material for turbine rotors in geothermic power stations because of its excellent strength and toughness properties in combination with good erosion and corrosion resistance. In terms of the phase diagram, this soft-martensitic steel has its place at the martensite/austenite/ferrite interface. Therefore, its chemical composition must be chosen so as to have a completely martensitic structure after hardening. The manufacture of and the mechanical properties of a turbine rotor 1200 mm in diameter by 5600 mm in length with a finished weight of approximately 21.5 tons are described in detail

The Effect of Si and Mn on Microstructure and Selected Properties of Cr-Ni Stainless Steels

Directory of Open Access Journals (Sweden)

Kalandyk B.

2017-03-01

Full Text Available Cast stainless steel of the Cr-Ni duplex type is used, among others, for the cast parts of pumps and valves handling various chemically aggressive media. Therefore, the main problem discussed in this article is the problem of abrasion wear resistance in a mixture of SiC and water and resistance to electrochemical corrosion in a 3% NaCl-H2O solution of selected cast steel grades, i.e. typical duplex cast steel, high silicon and manganese duplex cast steel, and Cr-Ni austenitic cast steel (type AISI 316L. The study shows that the best abrasion wear resistance comparable to Ni-Hart cast iron was obtained in the cast duplex steel, where Ni was partially replaced with Mn and N. This cast steel was also characterized by the highest hardness and matrix microhardness among all the tested cast steel grades. The best resistance to electrochemical corrosion in 3% NaCl-H2O solution showed the cast duplex steel with high content of Cr, Mo and N. The addition of Ni plays rather insignificant role in the improvement of corrosion resistance of the materials tested.

Comparison of the segregation behavior between tempered martensite and tempered bainite in Ni-Cr-Mo high strength low alloy RPV steel

Energy Technology Data Exchange (ETDEWEB)

Park, Sang Gyu; Kim, Min Chul; Kim, Hyung Jun; Lee, Bong Sang [Korea Atomic Energy Research Institute, Daejeon (Korea, Republic of)

2012-05-15

SA508 Gr.4N Ni-Cr-Mo low alloy steel has an superior fracture toughness and strength, compared to commercial Mn-Mo-Ni low alloy RPV steel SA508 Gr.3. Higher strength and fracture toughness of low alloy steels could be obtained by adding Ni and Cr. So several were performed on researches on SA508 Gr.4N low alloy steel for a RPV application. The operation temperature and term of a reactor pressure vessel is more than 300 .deg. C and over 40 years. Therefore, in order to apply the SA508 Gr.4N low alloy steel for a reactor pressure vessel, the resistance of thermal embrittlement in the high temperature range including temper embrittlement is required. S. Raoul reported that the susceptibility to temper embrittlement was increasing a function of the cooling rate in SA533 steel, which suggests the martensitic microstructures resulting from increased cooling rates are more susceptible to temper embrittlement. However, this result has not been proved yet. So the comparison of temper embrittlement behavior was made between martensitic microstructure and bainitic microstructure with a viewpoint of boundary features in SA508 Gr.4N, which have mixture of tempered bainite/martensite. We have compared temper embrittlement behaviors of SA508 Gr.4N low alloy steel with changing volume fraction of martensite. The mechanical properties of these low alloy steels were evaluated after a long-term heat treatment. Then, the the segregated boundaries were observed and segregation behavior was analyzed by AES. In order to compare the misorientation distributions of model alloys, grain boundary structures were measured with EBSD

The influence of heat treatment and process parameters optimization on hardness and corrosion properties of laser alloyed X12CrNiMo steel

CSIR Research Space (South Africa)

Popoola, API

2016-10-01

Full Text Available Martensitic stainless steels are used in the production of steam turbine blades but their application is limited due to low hardness and poor corrosion resistance. Laser surface alloying and heat treatment of X12CrNiMo Martensitic stainless steel...

PLASTIC DEFORMATION ON THE MACHINED SURFACE OF STEEL Cr20Ni10MoTi AT DRILLING

Directory of Open Access Journals (Sweden)

Jozef Jurko

2009-07-01

Full Text Available Information about material machinability is very important for the machining technology. Precise and reliable information on the machinability of a material before it enters the machining process is a necessity, and this brings the verification of technological methods in practice. This article presents the conclusions of machinability tests on austenitic stainless steel according to EN-EU (ISO: steel Cr20Ni10MoTi. This article presents the conclusions of VEGA grant agency at the Ministry of Education SR for supporting research work and co-financing the projects: Grant work #01/3173/2006 with the title „Experimental investigation of cutting zones in drilled and milled stainless steels

Void formation and helium effects in 9Cr-1MoVNb and 12Cr-1MoVW steels irradiated in HFIR and FFTF at 400/degree/C

International Nuclear Information System (INIS)

Maziasz, P.J.; Klueh, R.L.

1988-01-01

Martensitic/ferritic 9Cr-1MoVNb and 12Cr-1MoVW steels doped with up to 2 wt% Ni have up to 450 appm He after HFIR irradiation to /approximately/38 dpa, but only 5 appm He after 47 dpa in FFTF. No fine He bubbles and few or no larger voids were observable in any of these steels after FFTF irradiation at 407/degree/C. By contrast, many voids were found in the undoped steels (30-90 appm He) irradiated in HFIR at 400/degree/C, while voids plus many more fine He bubbles were found in the Ni-doped steels (400-450 appm He). Irradiation in both reactors at /approximately/400/degree/C produced significant changes in the as-tempered lath/subgrain boundary, dislocation, and precipitation structures that were sensitive to alloy composition, including doping with Ni. However, for each specific alloy the irradiation-produced changes were exactly the same comparing samples irradiated in FFTF and HFIR, particularly the Ni-doped steels. Therefore, the increased void formation appears solely due to the increased helium generation found in HFIR. While the levels of void swelling are relatively low after 37-39 dpa in HFIR (0.1-0.4%), details of the microstructural evolution suggest that void nucleation is still progressing, and swelling could increase with dose. The effect of helium on void swelling remains a valid concern for fusion application that requires higher dose experiments. 15 refs., 14 figs., 8 tabs

Tensile properties of the modified 13Cr martensitic stainless steels

Energy Technology Data Exchange (ETDEWEB)

Mabruri, Efendi, E-mail: effe004@lipi.go.id; Anwar, Moch Syaiful, E-mail: moch.syaiful.anwar@lipi.go.id; Prifiharni, Siska, E-mail: siska.prifiharni@lipi.go.id; Romijarso, Toni B.; Adjiantoro, Bintang [Research Center for Metallurgy and Materials, Indonesian Institute of Sciences (LIPI) Kawasan Puspiptek Gd. 470 Serpong, Tangerang Selatan 15314 (Indonesia)

2016-04-19

This paper reports the influence of Mo and Ni on the tensile properties of the modified 13Cr martensitic stainless steels in tempered condition. Four steels with different content of Mo and Ni were prepared by induction melting followed by hot forging, quenching and tempering. The experimental results showed that the addition of about 1% and 3% Mo has a beneficial effect to increase both the tensile strength and the elongation of the steels. On the contrary, the addition of about 3% Ni into the martensitic stainless steel results in decreasing of both the tensile strength and the elongation. Among the alloys investigated the 13Cr3Mo type steel exhibited largest tensile strength of 1348 MPa and largest elongation of 12%. The observation on the tensile fractured surfaces by using scanning electron microscope supported these findings.

Tensile properties of the modified 13Cr martensitic stainless steels

International Nuclear Information System (INIS)

Mabruri, Efendi; Anwar, Moch Syaiful; Prifiharni, Siska; Romijarso, Toni B.; Adjiantoro, Bintang

2016-01-01

This paper reports the influence of Mo and Ni on the tensile properties of the modified 13Cr martensitic stainless steels in tempered condition. Four steels with different content of Mo and Ni were prepared by induction melting followed by hot forging, quenching and tempering. The experimental results showed that the addition of about 1% and 3% Mo has a beneficial effect to increase both the tensile strength and the elongation of the steels. On the contrary, the addition of about 3% Ni into the martensitic stainless steel results in decreasing of both the tensile strength and the elongation. Among the alloys investigated the 13Cr3Mo type steel exhibited largest tensile strength of 1348 MPa and largest elongation of 12%. The observation on the tensile fractured surfaces by using scanning electron microscope supported these findings.

Analysis of High Temperature Deformed Structure and Dynamic Precipitation in W9Mo3Cr4V Steel

Institute of Scientific and Technical Information of China (English)

无

2001-01-01

With TEM、SEM, various high-temperature deformed structures inW9Mo3Cr4V steel were investigated. The sub-structures，recrystallized nuclei, as well as the dynamic precipitation were also studied and analyzed. The relationship between recrystallized structures and dynamic precipitation was discussed. The results showed that the deformed structures in W9Mo3Cr4V steel are more complicated than those in low alloy steels. Because W9Mo3Cr4V steel is a high-speed steel, there are a large number of residual carbides on the matrix. Also, much dynamic precipitating carbides will precipitate during deformation at high temperature.

3D Modelling of Flash Formation in Linear Friction Welded 30CrNiMo8 Steel Chain

Directory of Open Access Journals (Sweden)

Pedro Effertz

2017-10-01

Full Text Available Linear friction welding (LFW is a solid-state welding process that has been thoroughly investigated for chain welding in recent years in order to replace the currently in use Flash Butt Welding (FBW process. Modelling has proven to be an indispensable tool in LFW, thus providing necessary insight to the process, regardless of its final application. This article describes a 3D model developed in the commercial software DEFORM to study the LFW process of 30CrNiMo8 high strength steel in the Hero chain. Hence, a weakly coupled thermal and mechanical model were used, by means of the process experimental input such as displacement histories. The flash morphology and intervening mechanisms were analyzed. A thermal evaluation of different regions in the studied geometry was considered, and a correlation of the modeled and experimental width of the extrusion zone was established.

Thermo-mechanical treatment of the Cr-Mo constructional steel plates with Nb, Ti and B additions

International Nuclear Information System (INIS)

Adamczyk, J.; Opiela, M.

2002-01-01

Results of investigations of the influence of parameters of thermomechanical treatment, carried out by rolling with controlled recrystallization, on the microstructure and mechanical properties of Cr-Mo constructional steel with Nb, Ti and B microadditions, destined for the manufacturing of weldable heavy plates, are presented. These plates show a yield point of over 960 MPa after heat treatment. Two variants of thermomechanical treatment were worked out, based on the obtained results of investigations, when rolling a plate 40 mm thick in several passes to a plate 15 mm thick in a temperature range from 1100 to 900 o C. It was found that the lack of complete recrystallization of the austenite in the first rolling variant, leads to localization of plastic deformation in form of shear bands. There exists a segregation of MC-type carbides and alloying elements in these bands, causing a distinctive reduction of the crack resistance of the steel, as also a disadvantageous anisotropy of plastic properties of plate after tempering. For plates rolled under the same conditions, using a retention shield, a nearly three times higher impact energy in - 40 o C was obtained, as also only a slight anisotropy of plastic properties, saving the required mechanical properties. (author)

Effect of long-term aging on microstructural stabilization and mechanical properties of 20Cr32Ni1Nb steel

Energy Technology Data Exchange (ETDEWEB)

Guo, Xiaofeng; Jia, Xiankai [School of Mechanical and Power Engineering, Nanjing Tech University, Nanjing, Jiangsu 211816 (China); Gong, Jianming, E-mail: gongjm@njtech.edu.cn [School of Mechanical and Power Engineering, Nanjing Tech University, Nanjing, Jiangsu 211816 (China); Key Lab of Design and Manufacture of Extreme Pressure Equipment, Jiangsu Province (China); Geng, Luyang; Tang, Jianqun; Jiang, Yong [School of Mechanical and Power Engineering, Nanjing Tech University, Nanjing, Jiangsu 211816 (China); Key Lab of Design and Manufacture of Extreme Pressure Equipment, Jiangsu Province (China); Ni, Yingying; Yang, Xinyu [School of Mechanical and Power Engineering, Nanjing Tech University, Nanjing, Jiangsu 211816 (China)

2017-04-06

The centrifugally cast 20Cr32Ni1Nb stainless steel aged at 950 ℃ from 200 h up to 5000 h was investigated on the mechanical properties and microstructural evolution using post-aged tensile tests, post-aged Charpy impact tests, Optical microscopy (OM) observations, and field emission-scanning electron microscopy (FE-SEM) examinations. Experimental results indicate that the as-cast microstructure of the steel typically consists of a supersaturated solid solution of austenite matrix with a network of interdendritic primary carbides (NbC and M{sub 23}C{sub 6}). During aging process, the growth and coarsening of NbC carbides and M{sub 23}C{sub 6} carbides as well as the transformation of NbC carbide into G phase take place. Meanwhile, the transformation of NbC into G phase releases C into the matrix during aging exposure. This released C tends to combine with Cr, and forms M{sub 23}C{sub 6} at the dendrite boundaries. Compared with a continuous reduction of the elongation in the whole aging period, the strength parameters (σ{sub ult} and σ{sub ys}) exhibit an initial increase followed by a continuous decrease with the aging time prolonged from 1000 h to 5000 h. Additionally, the variation of Charpy impact absorbed energy is relatively complex during aging process. The microstructural evolution during long-term aging process is consistent with the variation of mechanical properties.

Reversed austenite in 0Cr13Ni4Mo martensitic stainless steels

Energy Technology Data Exchange (ETDEWEB)

Song, Y.Y., E-mail: songyuanyuan@imr.ac.cn [Institute of Metal Research, Chinese Academy of Science, Shenyang 110016 (China); Li, X.Y.; Rong, L.J.; Li, Y.Y. [Institute of Metal Research, Chinese Academy of Science, Shenyang 110016 (China); Nagai, T. [National Institute for Materials Science, Sengen 1-2-1, Tsukuba 305-0047 (Japan)

2014-01-15

The austenite reversion process and the distribution of carbon and other alloying elements during tempering in 0Cr13Ni4Mo martensitic stainless steel have been investigated by in-situ high temperature X-ray diffraction (XRD) and scanning transmission electron microscopy (STEM). The microstructure of the reversed austenite was characterized using transmission electron microscopy (TEM). The results revealed that the amount of the reversed austenite formed at high temperature increased with the holding time. Direct experimental evidence supported carbon partitioning to carbides and Ni to the reversed austenite. The reversed austenite almost always nucleated in contact with lath boundary M{sub 23}C{sub 6} carbides during tempering and the diffusion of Ni promoted its growth. The Ni enrichment and the ultrafine size of the reversed austenite were considered to be the main factors that accounted for the stability of the reversed austenite. - Highlights: • The amount of the reversed austenite formed at high temperature increases with the holding time. • STEM results directly show that carbon is mainly partitioned into the carbides and Ni into the reversed austenite. • The Ni enrichment and the ultrafine size are the main factors leading to the stabilization of the reversed austenite.

The irradiation hardening of Ni-Mo-Cr and Ni-W-Cr alloy under Xe26+ ion irradiation

Science.gov (United States)

Chen, Huaican; Hai, Yang; Liu, Renduo; Jiang, Li; Ye, Xiang-xi; Li, Jianjian; Xue, Wandong; Wang, Wanxia; Tang, Ming; Yan, Long; Yin, Wen; Zhou, Xingtai

2018-04-01

The irradiation hardening of Ni-Mo-Cr and Ni-W-Cr alloy was investigated. 7 MeV Xe26+ ion irradiation was performed at room temperature and 650 °C with peak damage dose from 0.05 to 10 dpa. With the increase of damage dose, the hardness of Ni-Mo-Cr and Ni-W-Cr alloy increases, and reaches saturation at damage dose ≥1 dpa. Moreover, the damage dose dependence of hardness in both alloys can be described by the Makin and Minter's equation, where the effective critical volume of obstacles can be used to represent irradiation hardening resistance of the alloys. Our results also show that Ni-W-Cr alloy has better irradiation hardening resistance than Ni-Mo-Cr alloy. This is ascribed to the fact that the W, instead of Mo in the alloy, can suppress the formation of defects under ion irradiation.

Quantitative evaluation of safety use limit for crevice corrosion in Ni-Cr-Mo alloys

International Nuclear Information System (INIS)

Fukaya, Yuichi; Akashi, Masatsune; Sasaki, Hidetsugu; Tsujikawa, Shigeo

2007-01-01

The most important problem with corrosion-resistant alloys such as stainless steels is localized corrosion. Crevice corrosion, which is a typical localized corrosion, occurs under the mildest environmental conditions. Consequently, whether crevice corrosion occurs or not is an important issue in structural material selection. This study investigated highly corrosion-resistant Ni-Cr-Mo alloys whose resistance for crevice corrosion is difficult to evaluate with the JIS G 0592 standard for common strainless steels. The optimized procedures for determining the critical potential and temperature for crevice corrosion of the alloys were developed based on the JIS method. The limits of safety usage of various Ni-Cr-Mo alloys were evaluated quantitatively in chloride solution environments. (author)

Surface Nb-ALLOYING on 0.4C-13Cr Stainless Steel: Microstructure and Tribological Behavior

Science.gov (United States)

Yu, Shengwang; You, Kai; Liu, Xiaozhen; Zhang, Yihui; Wang, Zhenxia; Liu, Xiaoping

2016-02-01

0.4C-13Cr stainless steel was alloyed with niobium using double glow plasma surface alloying and tribological properties of Nb-alloyed steel such as hardness, friction and wear were measured. Effects of the alloying temperature on microstructure and the tribological behavior of the alloyed steel were investigated compared with untreated steel. Formation mechanisms of Nb-alloyed layers and increased wear resistance were also studied. The result shows that after surface Nb-alloying treatment, the 0.4C-13Cr steel exhibits a diffusion adhesion at the alloyed layer/substrate interface and improved tribological property. The friction coefficient of Nb-alloyed steel is decreased by about 0.3-0.45 and the wear rate after Nb-alloying is only 2-5% of untreated steel.

Effect of ageing on the microstructural stability of cold-worked titanium-modified 15Cr-15Ni-2.5Mo austenitic stainless steel

International Nuclear Information System (INIS)

Venkadesan, S.; Bhaduri, A.K.; Rodriguez, P.; Padmanabhan, K.A.

1992-01-01

A titanium-modified 15Cr-15Ni-2.5Mo austenitic stainless steel conforming to ASTM A 771 (UNS S 38660), commercially called Alloy D9, is being indigenously developed for application as material for the fuel clad and the hexagonal wrapper for fuel subassemblies of the Prototype Fast Breeder Reactor. As this material would be used in the cold-worked condition and would be subjected to prolonged exposure to elevated service temperatures, the effect of ageing on the microstructural stability was studied as a function of the amount of cold work. The material was given 2.5-30% prior cold work and then aged at temperatures in the range 923 to 1173 K for times ranging from 0.25 to 1000 h. Hardness measurements made before and after ageing were correlated with the Larson-Miller parameter to determine the highest stable prior cold-work level. Optical microscopy was used to study the microstructural changes. The influence of prolonged exposure for two and three years at the operating temperatures of clad and wrapper, on the elevated temperature tensile properties of a 20% prior cold-worked Alloy D9 was also studied through accelerated ageing treatments based on the present parametric approach. (orig.)

Metallographical investigations on cavitation erosion of the steel X 2 CrNiMoN 22 5 3

International Nuclear Information System (INIS)

Pohl, M.; Goecke, A.

1989-01-01

The development of erosion-resistant material, however, presupposes a precise knowledge of the mechanism and progress of the destruction. For this reason, cavitation erosion was studied in this investigation using optical microscopy (OM), scanning electron microscopy (SEM), transmission electron microscopy (TEM) and ultra-microhardness tests (UMHT) - as well as gravimetry. A Cr-Ni-Mo steel with a ferritic-austenitic structure was investigated. This material was selected to provide information about the possible interaction between the phases within such a structure and about the damage mechanism of the individual phases. The experimental material was modified by a heat treatment to precipitate the σ-phase so that a three-phase model material could be obtained as well as the two-phase alloy. (orig./MM) [de

Long term properties and microstructural evolution of 18Cr-10Ni-3Cu-Ti-Nb austenitic stainless steel for boiler tube application

Energy Technology Data Exchange (ETDEWEB)

Minami, Y.; Fukui, T.; Ono, T. [TenarisNKK Tubes, Kawasaki, Kanagawa (Japan); Caminada, S. [TenarisDalmine, Dalmine, BG (Italy)

2010-07-01

The allowable tensile stress of 0.1C-18Cr-10Ni-3Cu-Ti-Nb steel (TEMPALOY AA-1; ASME C.C. 2512) is more than 30% higher compared with that of ASME SA-213 Grade TP347H in the temperature range 600-700 C. This high creep rupture strength is obtained by the precipitation of MC and M{sub 23}C{sub 6} carbides, and Cu-rich phase. Long term creep rupture tests over 10{sup 5}h enabled to verify the superior creep rupture strength of this steel. The investigation of microstructural evolution on the creep ruptured and aged specimens has shown the high structural stability of this material. Hardness and impact properties after high temperature aging reveal similar performance as conventional 18-8 stainless steels. Excellent steam oxidation resistance can be achieved by a shot-blasting method. The scale thickness of shot-blasted tube after 1000h at 750 C is below a few micron meters. These results have revealed that the mechanical properties and environmental resistance of this steel enable the use of TEMPALOY AA-1 in the latest generation of advanced USC boiler. (orig.)

Effect of Cr3C2 content on the microstructure and properties of Mo2NiB2-based cermets

International Nuclear Information System (INIS)

Xie, Lang; Li, XiaoBo; Zhang, Dan; Yang, ChengMing; Yin, FuCheng; Xiangtan Univ., Hunan; Xiangtan Univ., Hunan; Xiao, YiFeng

2015-01-01

Four series of Mo 2 NiB 2 -based cermets with Cr 3 C 2 addition of between 0 and 7.5 wt.% in 2.5 wt.% increments were studied by means of scanning electron microscopy, energy dispersive X-ray analysis and X-ray diffractometry. The transverse rupture strength and hardness were also measured. It was found that Cr 3 C 2 completely dissolved in Mo 2 NiB 2 -based cermets. Cr 3 C 2 addition improved the wettability of the Ni binder phase on the Mo 2 NiB 2 hard phase, which resulted in a decrease in the porosity and an increase in the phase uniformity. The cermets with 2.5 wt.% Cr 3 C 2 content showed relatively fine grains and almost full density. A high Cr 3 C 2 content resulted in the formation of M 6 C (M = Mo, Cr, Ni) phase. In addition, energy dispersive X-ray spectroscopy results showed that the content of Mo in the binder decreased with increasing Cr 3 C 2 content. The cermets with 2.5 wt.% Cr 3 C 2 addition exhibited the highest transverse rupture strength of 2210 MPa, whereas the cermets without Cr 3 C 2 addition exhibited the highest hardness.

Hydrogen effect on different melts of steel 03Cr10Ni10Mo2(Ti,Al)

International Nuclear Information System (INIS)

Hruby, J.; Novosad, P.; Axamit, R.

1984-01-01

The effect of hydrogen on martensitic 03Cr10Ni10Mo2(Ti,Al) steel was studied following vacuum induction melting and electroslag remelting with and without the effect of radiation. Under the influence of hydrogen and under the same parameters of catodic hydrogen charging of steel after vacuum induction melting shows a 20 - 30% reduction in total ductility. Steels after electroslag remelting show a higher reduction in total ductility - within the range of 26 - 33%, i.e., 33 - 43% for different melts, and contraction Z shows a reduction of 23 - 59%. Electroslag remelted steels show a greater reduction in plasticity owing to hydrogen than steels melted in vacuum induction furnaces. The reduction of the yield point and the breaking strength owing to hydrogen are more explicit than in steel after vacuum melting. In non-irradiated hydrogenated samples a higher yield point was evident. (B.S.)

Effect of Molybdenum on the Corrosion Behavior of High-Entropy Alloys CoCrFeNi2 and CoCrFeNi2Mo0.25 under Sodium Chloride Aqueous Conditions

Directory of Open Access Journals (Sweden)

Alvaro A. Rodriguez

2018-01-01

Full Text Available The corrosion behavior of high-entropy alloys (HEAs CoCrFeNi2 and CoCrFeNi2Mo0.25 was investigated in 3.5 wt. percent sodium chloride (NaCl at 25°C by electrochemical methods. Their corrosion parameters were compared to those of HASTELLOY® C-276 (UNS N10276 and stainless steel 316L (UNS 31600 to assess the suitability of HEAs for potential industrial applications in NaCl simulating seawater type environments. The corrosion rates were calculated using corrosion current determined from electrochemical experiments for each of the alloys. In addition, potentiodynamic polarization measurements can indicate active, passive, and transpassive behavior of the metal as well as potential susceptibility to pitting corrosion. Cyclic voltammetry (CV can confirm the alloy susceptibility to pitting corrosion. Electrochemical impedance spectroscopy (EIS elucidates the corrosion mechanism under studied conditions. The results of the electrochemical experiments and scanning electron microscopy (SEM analyses of the corroded surfaces revealed general corrosion on alloy CoCrFeNi2Mo0.25 and HASTELLOY C-276 and pitting corrosion on alloy CoCrFeNi2 and stainless steel 316L.

Comparison of SA508 Gr.3 and SA508 Gr.4N Low Alloy Steels for Reactor Pressure Vessel Steel

Energy Technology Data Exchange (ETDEWEB)

Kim, Min Chul; Lee, B. S

2009-12-15

The microstructural characteristics and mechanical properties of SA508 Gr.3 Mn-Mo-Ni low alloy steel and SA508 Gr.4N Ni-Mo-Cr low alloy steel were investigated. The differences in the stable phases between these two low alloy steels were evaluated by means of a thermodynamic calculation using ThermoCalc. They were then compared to microstructural features and correlated with mechanical properties. Mn-Mo-Ni low alloy steel shows the upper bainite structure which has the coarse cementite in the lath boundaries. However, Ni-Mo-Cr low alloy steel shows the mixture of lower bainite and tempered martensite structure that homogeneously precipitates the small carbides such as M{sub 23}C{sub 6} and M{sub 7}C{sub 3} due to an increase of hardenability and Cr addition. In the mechanical properties, Ni-Mo-Cr low alloy steel has higher strength and toughness than Mn-Mo-Ni low alloy steel. Ni and Cr additions increase the strength by solid solution hardening. Besides, microstructural changes from upper bainite to tempered martensite improve the strength of the low alloy steel by grain refining effect. And the changes in the precipitation behavior by Cr addition improve the ductile-brittle transition behavior along with a toughening effect of Ni addition.

Effect of chemical composition on irradiation embrittlement and annealing in Ni-Cr-Mo-V reactor pressure vessel steel

Energy Technology Data Exchange (ETDEWEB)

Novosad, P [Czech Nuclear Society, Prague (Czech Republic)

1994-12-31

Results concerning copper and phosphorus influence on radiation-induced changes in the Ni-Cr-Mo-V steel mechanical properties, are presented. Correlations between different mechanical properties for steels with different chemical composition, are presented. A comparison of transition temperature shifts obtained for static and dynamic fracture toughness tests and Charpy impact tests, is discussed. Recovery of radiation hardening, measured by hardness test after isochronal annealing of steels with different compositions, is also shown. Copper content strongly affects irradiation-induced changes of mechanical properties, but phosphorus content in connection with variable copper content has only a small effect. (author). 4 refs., 4 figs., 4 tabs.

Nondestructive testing for microstructural characterization in 9Cr-1Mo ferritic steel towards assessment of fabrication quality and in-service degradation

Energy Technology Data Exchange (ETDEWEB)

Jayakumar, T.; Rao, K.B.S.; Raj, Baldev [Indira Gandhi Centre for Atomic Research, Kalpakkam (India)

1999-07-01

The paper discusses the usefulness of non destructive testing for microstructural characterization in 9Cr-1Mo ferritic steel. Ultrasonic velocity and attenuation measurements and spectral analysis have been used in a complementary way for characterizing Ac{sub 1} and Ac{sub 3} temperatures, amount of martensite and ferrite, dissolution of V{sub 4}C{sub 3} and NbC and formation of {delta}-ferrite. The microstructural degradation occurring due to thermal ageing and creep has also been studied by ultrasonic velocity measurements. Magnetic Barkhausen noise technique has been used for estimating the extent of various regions in heat affected zone (HAZ) of 9Cr-1Mo ferritic steel weldment. The same technique has been used for the assessment of low cycle fatigue damage in 9Cr-1Mo steel. The study establishes that non destructive methods can be used for the assessment of fabrication quality and in service degradation of the components. (author)

Liquidus projection of the Nb-Cr-Al system near the Al3(Nb,Cr) + Cr(Al,Nb) eutectic region

International Nuclear Information System (INIS)

Souza, S.A.; Ferrandini, P.L.; Nunes, C.A.; Coelho, A.A.; Caram, R.

2006-01-01

The system Nb-Cr-Al was investigated in the region near the Al 3 (Nb,Cr) + Cr(Al,Nb) eutectic and the liquidus projection of that region was determined based on the microstructural characterization of arc melted alloys. The characterization utilized scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS), differential thermal analysis (DTA) and X-ray diffraction (XRD). The results allowed one to determine three primary solidification liquidus surfaces ((Cr,Al) 2 Nb, Cr(Al,Nb) and Al 3 (Nb,Cr)), that are originated from the binary systems Cr-Nb, Cr-Al and Al-Nb. It is proposed the occurrence of the invariant reaction L + (Cr,Al) 2 Nb ↔ Al 3 (Nb,Cr) + Cr(Al,Nb) and of a point of minimum, which involves a three phase reaction, L ↔ Al 3 (Nb,Cr) + Cr(Al,Nb). All alloys studied showed formation of the Al 3 (Nb,Cr) + Cr(Al,Nb) eutectic as the last solidification step with Al(Nb)Cr 2 precipitating from Cr(Al,Nb)

Effect of plastic deformation on the supercooled austenite transformations of the Cr-Mo steel with Nb, Ti and B microadditions

International Nuclear Information System (INIS)

Adamczyk, J.; Opiela, M.

1998-01-01

Effect of plastic deformation at austenizing temperature was investigated on phase transformations, structure and hardness of the supercooled austenite transformation products of the Cr-Mo constructional steel with Nb, Ti and B microadditions. Basing on the analysis of the phase transformation plots of the supercooled undeformed austenite and of the supercooled and plastically deformed one, it was found out that direct cooling of specimens after completing their plastic deformation in the above mentioned conditions, results in significant acceleration of the α→β, and ferritic and pearlitic transformations, and in the decrease of transformation products hardness. These phenomena are of great importance for working out of the thermo-mechanical treatment of products made from the heat-treated microalloyed steel. (author)

The effect of spheroidizing by thermal cycling in low concentration Cr-Mo alloy steel

International Nuclear Information System (INIS)

Yun, H.S.; Kang, C.Y.

1979-01-01

An intensive study was carried out on spheroidizing of pearlite (Sph) and number of spherical carbide in proeutectoid ferrite (No/100) of low concentration Cr-Mo steel with thermal cycling. Physical and mechanical properties of steel containing 0.33 % C with thermal cycling were compared with those of low concentration Cr-Mo steel with thermal cycling. The effect of normal heat treatment and cooling rate on spheroidizing of pearlite and precipitation of fine spherical carbide in the steels were investigated. The results obtained were as follows: 1) Thermal cycling of low concentration Cr-Mo steel promoted the spheroidizing of pearlite compared with that of steel without Cr and Mo to steel had significant effect on spheroidizing of pearlite. 2) Number of fine spherical carbides of low concentration Cr-Mo steel with thermal cycling was over 5 times to that of fine spherical carbides of hypoeutectoid steel with thermal cycling. 3) Spheroidizing of pearlite and number of fine spherical carbide in proeutectoid ferrite of low concentration Cr-Mo steel with increasing thermal cycle and cooling rate. 4) Hardness of steel with thermal cycling was decreased. However, low concentration Cr-Mo steel had little decreasing rate in hardness with increasing thermal cycle on the basis of 100 times in thermal cycle. Therefore, toughness was considered to be increased with increasing spheroidizing of pearlite without changing mechanical properties. (author)

Role of Nb in low interstitial 13Cr super martensitic stainless steel

Energy Technology Data Exchange (ETDEWEB)

Ma, X.P.; Wang, L.J. [Key Laboratory for Anisotropy and Texture of Materials, Northeastern University, Shenyang 110004 (China); Liu, C.M., E-mail: cmliu@mail.neu.edu.cn [Key Laboratory for Anisotropy and Texture of Materials, Northeastern University, Shenyang 110004 (China); Subramanian, S.V. [Department of Materials Science and Engineering, McMaster University, Hamilton, L8S-4L7 (Canada)

2011-08-25

Highlights: {yields} Nb retards the kinetics of reversed austenite formation. {yields} Nb suppresses the occurrence of Cr rich precipitates. {yields} Nano-scale precipitates contribute to the significant increase in strength. - Abstract: The effect of adding 0.1 wt% Nb to low interstitial (N 0.01 wt%, C 0.01 wt%) 13Cr super martensitic stainless steel (SMSS) on solid phase transformation and microstructures achieved by normalizing and tempering was investigated using dilatometer, electron backscattered diffraction (EBSD), transmission electron microscope (TEM), X-ray diffraction (XRD), and its consequence on mechanical properties was examined to clarify the role of Nb in low interstitial martensitic stainless steel. Nb was found to retard kinetics of reversed austenite formation during tempering and to suppress the occurrence of Cr rich precipitates. The measurement of mechanical properties shows that while the strength properties were significantly increased by nano-scale precipitates enriched in Nb in the steel with 0.10 wt% Nb, the ductility and toughness properties were restored by optimum volume fraction of retained austenite. Excellent strength and adequate toughness properties were obtained by tempering the steel with 0.10 wt% Nb and low interstitial (N 0.01 wt%, C 0.01 wt%) steel at 600 deg. C.

The integrity of 9Cr-1Mo to stainless steel transition joints in AGR steam generators

International Nuclear Information System (INIS)

James, D.W.; Neumann, P.; Soo, J.

1982-01-01

The metallurgical aspects of the transition joint between 9Cr-1Mo and 316 stainless steel boiler tube sections are reviewed. A large minimum superheat margin (106 0 C) between the dryout zone and the 9Cr-1Mo to stainless steel transition joint was specified in the original design to eliminate the risk of wetting the stainless steel which is susceptible to stress corrosion cracking. However, small defects were discovered in the welds between the 9Cr-1Mo and Sanicro (72%Ni-16%Cr-10%Fe) transition piece, resulting from dilution of the weld pool by nickel from the transition piece. This led to the possibility of weld failure as a result of creep crack growth in service, and any significant reduction in operating temperature would mean that the large superheat margin could not be sustained. The creep properties of the joints, together with the transition joint temperature distribution, enabled tube failure rates to be determined as a function of operating temperature. A probabilistic model was developed so that the transition joint could be operated within a temperature 'window', the lower temperature limit being determined by stress corrosion considerations and the upper limit being set by creep rate limitations. This allows full load performance from the boilers throughout the anticipated life of the plant. (author)

Long-term Stability of 9- to 12 % Cr Steels

DEFF Research Database (Denmark)

Hald, John

2004-01-01

In the recent 25 years creep rupture strength of 9- to 12 %Cr steels for steam pipes and turbines has been doubled by development of new alloys. This development has formed a basis for improved efficiency of fossil fired steam power plants by introduction of advanced steam temperatures...... and pressures. Newly developed steam pipe steels are based on modifications of well-established steels like the X 20CrMoV12 1. Balanced addition of V, Nb and N to a 9Cr 1 Mo steel led to the Modified 9 Cr steel P 91. Addition of 1% W to a 9Cr 1 MoVNbN base composition led to steel E 911 and partial replacement...... of Mo with 1.8 % W combined with a slight amount of Boron led to steel P 92. The creep rupture strength of these new alloys are now secured with long-term tests up to 100,000 hours, which demonstrate improvements of 50% (P 91), 75 % (E 911) and 100 % (P 92) in strength compared to X 20CrMoV12 1....

Soft zone formation in dissimilar welds between two Cr-Mo steels

International Nuclear Information System (INIS)

Albert, S.K.; Gill, T.P.S.; Tyagi, A.K.; Mannan, S.L.; Rodriguez, P.; Kulkarni, S.D.

1997-01-01

Two dissimilar weldments between 9Cr-1Mo and 2.25Cr-1Mo ferritic steels have been characterized for their microstructural stability during various postweld heat treatments (PWHTs). The samples for the investigation were extracted from bead-on-plate weldments made by depositing 2.25Cr-1Mo weld metal on 9Cr-1Mo base plate and vice versa. Subsequent application of PWHT resulted in the formation of a soft zone in the low Cr ferritic steel weld or base plate. A carbide-rich hard zone, adjoining the soft zone, was also detected in the high Cr side of the weldment. Unmixed zones in the weld metal provided additional soft and hard zones in the weld metals. The migration of carbon from low-Cr steel to high-Cr steel, driven by the carbon activity gradient, has been shown to be responsible for the formation of soft and hard zones. A carbon activity diagram for 2.25Cr-1Mo/9Cr-1Mo weldments has been proposed to aid in the selection of welding consumables for reducing or preventing the soft zone formation

Cladding nuclear steels - the application of plasma-arc hot wire surfacing

International Nuclear Information System (INIS)

Trarbach, K.O.

1981-01-01

The effect of one and two layer plasma-arc hot wire cladding on the HAZ microstructure of the fine grained structural steel 22 NiMoCr 3 7, which is similar to ASTM A 508, class 2, and steel 20 MnMoNi 5 5, similar to ASTM A 533, grade B, class 1 is determined. Attention is directed particularly to the behaviour of the susceptible region, and the consumables considered are cladding materials X 2 CrNiNb 19 9, similar to ER 347 Elc, and S-NiCr 20 Nb, similar to ER NiCr-3 (Inconel 82). Results of corrosion resistance tests show that this cladding technique can be recommended for manufacture of equipment for the chemical industry to avoid corrosion failure. Plasma-arc hot wire surfacing is also shown to be capable of depositing single or double clad layers to meet the highest safety requirements and could be applied to nuclear power plants for the special manufacture of wear resistant parts and for protection of equipment subject to a variety of corrosive environments. (U.K.)

Alumina-Forming Austenitic Stainless Steels Strengthened by Laves Phase and MC Carbide Precipitates

Science.gov (United States)

Yamamoto, Y.; Brady, M. P.; Lu, Z. P.; Liu, C. T.; Takeyama, M.; Maziasz, P. J.; Pint, B. A.

2007-11-01

Creep strengthening of Al-modified austenitic stainless steels by MC carbides or Fe2Nb Laves phase was explored. Fe-20Cr-15Ni-(0-8)Al and Fe-15Cr-20Ni-5Al base alloys (at. pct) with small additions of Nb, Mo, W, Ti, V, C, and B were cast, thermally-processed, and aged. On exposure from 650 °C to 800 °C in air and in air with 10 pct water vapor, the alloys exhibited continuous protective Al2O3 scale formation at an Al level of only 5 at. pct (2.4 wt pct). Matrices of the Fe-20Cr-15Ni-5Al base alloys consisted of γ (fcc) + α (bcc) dual phase due to the strong α-Fe stabilizing effect of the Al addition and exhibited poor creep resistance. However, adjustment of composition to the Fe-15Cr-20Ni-5Al base resulted in alloys that were single-phase γ-Fe and still capable of alumina scale formation. Alloys that relied solely on Fe2Nb Laves phase precipitates for strengthening exhibited relatively low creep resistance, while alloys that also contained MC carbide precipitates exhibited creep resistance comparable to that of commercially available heat-resistant austenitic stainless steels. Phase equilibria studies indicated that NbC precipitates in combination with Fe2Nb were of limited benefit to creep resistance due to the solution limit of NbC within the γ-Fe matrix of the alloys studied. However, when combined with other MC-type strengtheners, such as V4C3 or TiC, higher levels of creep resistance were obtained.

Effect of Cr and Mo on strain ageing behaviour of low carbon steel

International Nuclear Information System (INIS)

Pereloma, E.V.; Bata, V.; Scott, R.I.; Smith, R.M.

2010-01-01

This work explores the effects of Cr (0.26-0.74 wt%) and Mo (0.09-0.3 wt%) additions on the kinetics of strain ageing process in low carbon steel. The strain ageing behaviour of the steels was investigated by using tensile tests and transmission electron microscopy. The results have shown that Mo-alloyed steels undergo the same four stages of ageing as unalloyed low carbon steel, whereas Cr-alloyed steels exhibit only three stages of ageing. At the same time, the addition of Mo accelerates the ageing response, while alloying with Cr reduces the rate of strain ageing by ∼3 times in comparison with non-alloyed low carbon steel. It especially delays the offset of Stage III. This is explained by the reduction of carbon content in ferrite due to the enrichment of cementite with Cr leading to the reduction of its equilibrium solubility in ferrite.

Effect of Cr and Mo on strain ageing behaviour of low carbon steel

Energy Technology Data Exchange (ETDEWEB)

Pereloma, E.V., E-mail: elenap@uow.edu.au [School of Mechanical, Materials and Mechatronic Engineering, University of Wollongong, Northfields Avenue, Wollongong, NSW 2522 (Australia); Bata, V. [Department of Materials Engineering, Monash University (Australia); Scott, R.I.; Smith, R.M. [BlueScope Steel Limited, Port Kembla (Australia)

2010-04-25

This work explores the effects of Cr (0.26-0.74 wt%) and Mo (0.09-0.3 wt%) additions on the kinetics of strain ageing process in low carbon steel. The strain ageing behaviour of the steels was investigated by using tensile tests and transmission electron microscopy. The results have shown that Mo-alloyed steels undergo the same four stages of ageing as unalloyed low carbon steel, whereas Cr-alloyed steels exhibit only three stages of ageing. At the same time, the addition of Mo accelerates the ageing response, while alloying with Cr reduces the rate of strain ageing by {approx}3 times in comparison with non-alloyed low carbon steel. It especially delays the offset of Stage III. This is explained by the reduction of carbon content in ferrite due to the enrichment of cementite with Cr leading to the reduction of its equilibrium solubility in ferrite.

Microstructural investigations of fatigued 12% Cr-steel 1.4914 (X 18 Cr Mo V Nb 12 1)

International Nuclear Information System (INIS)

Gersinska, R.

1992-10-01

The low cycle fatigue properties of a tempered steel X18 Cr Mo V Nb 12 1 (DIN 1.4914) have been investigated at different temperatures, strain amplitudes, mean strains and strain rates. The role of martensite lath structure and of precipitates and dislocations on the strengthening mechanisms and fatigue damage have been analysed. Plastic deformation results in a slip band formation on the surface and in a cellular dislocation structure in the interior of the specimens. A reduced strain rate is causing lower stress amplitudes and greater cells at higher temperatures. At lower temperatures the influence of strain rate is small. Fatigue mechanisms are soon dominant at lower strain rates. REM-investigations of the specimen surfaces are revealing the development of cracks at slip bands. The cracks start always at the surfaces of the specimen, and they are transcristalline in nature. The influence of the ageing temperature has been investigated. A reduced ageing temperature of 600degC results in a higher dislocation density and a lower martensite lath distance in the undeformed material. Strain ageing was initially observed in tensile experiments. The influence of dynamic strain ageing on the mechanical properties and the microstructure of tempered steel 1.4914 is investigated. A correlation of mechanical and microstructural data has been performed. (orig./MM) [de

Experiences with new and improved oil quenched CrMoV rotor materials

International Nuclear Information System (INIS)

Ewald, J.; Keienburg, K.H.; Wiemann, W.; Sauer, D.L.

1987-01-01

The improvement gained with 1% CrMoNiV rotors of modern manufacturing processes are described. It was possible to raise the creep strength as well as the toughness level. The aim of this paper is to present representative data from older 1% CrMoNiV rotors and to compare them with test results from rotors of modern steel making technology and with improved chemical composition. The results prove, that the todays oil quenched version of the 1% CrMoNiV rotor material represents a good compromise with respect to creep rupture and (fracture) toughness behaviour. In addition the 1% CrMoNiV-steels have a stable microstructure which implements minor changes of properties during long term service

Diffusion complex layers of TiC-Ni-Mo type produced on steel during vacuum titanizing process combined with the electrolytic deposition

International Nuclear Information System (INIS)

Kasprzycka, E.; Krolikowski, A.

1999-01-01

Diffusion carbide layers produced on steel surface by means of vacuum titanizing process have been studied. A new technological process combining a vacuum titanizing with an electrolytic deposition of Ni-Mo alloy has been proposed to increase of corrosion resistance of carbide layers. The effect of preliminary electrolytic deposition of Ni-Mo alloy on the NC10 steel surface on the titanized layer structure and its corrosion resistance has ben investigated. As a result, diffusion complex layers of TiC-Ni-Mo type on NC10 steel surface have been obtained. An X-ray structural analysis of titanized surfaces on NC10 steel precovered with an electrolytic Ni-Mo alloy coating (70%Ni+30%Mo) revealed a presence of titanium carbide TiC, NiTi, MoTi and trace quantity of austenite. The image of the TiC-Ni-Mo complex layer on NC10 steel surface obtained by means of joined SEM+TEM method and diagrams of elements distribution in the layer diffusion zone have been shown. Concentration of depth profiles of Ti, Ni, Mo, Cr and Fe in the layer diffusion zone obtained by means of the joined EDS+TEM method are shown. Concentration depth profiles of Ti, Ni, Mo, Cr and Fe in the layer diffusion zone obtained by means of the X r ay microanalysis and microhardness of the layer are shown. An X-ray structural analysis of titanized surfaces on the NC10 steel, without Ni-Mo alloy layer, revealed only a substantial presence of titanium carbide TiC. For corrosion resistance tests the steel samples with various diffusion layers and without layers were used: (i) the TiC-Ni-Mo titanized complex layers on NC10 steel, (ii) the TiC titanized carbide layers on the NC10 steel, (iii) the NC10 steel without layers. Corrosion measurements of sample under test have been performed in 0.1 M H 2 SO 4 by means of potentiodynamic polarization and electrochemical impedance tests. It has been found that the corrosion resistance of titanized steel samples with the TiC and TiC-Ni-Mo layers is higher than for the steel

Relationship of bainitic microstructure to impact toughness in Cr-Mo and Cr-W steels

International Nuclear Information System (INIS)

Klueh, R.L.; Alexander, D.J.

1992-01-01

Non-classical bainite microstructures can develop during continuous cooling of low-carbon alloy steels. These differ from classical upper and lower bainite developed by isothermal transformation. Two non-classical bainite microstructures were produced in a 3Cr-1.5Mo0.25V-0.lC steel using different cooling rates after austenitizing--water quenching and air cooling. The carbide-free acicular bainite formed in the quenched steel had a lower ductile-brittle transition temperature (DBTT) than the granular bainite formed in the air-cooled steel. With increasing tempering parameter (defined bv tempering time and temperature), the DBTT of both decreased and approached a common value, although the final value occurred at a much lower tempering parameter for the quenched steel than for the air-cooled steel. The upper-shelf enery was similarly affected by microstructure. These observations along with similar observations in two Cr-W steels indicate that control of the bainite microstructure can be used to optimize strength and toughness

Structural evolution of Fe-18Ni-16Cr-4Al steel during aging at 950 .deg. C

Energy Technology Data Exchange (ETDEWEB)

Wang, Man; Jang, Jinsung [Korea Atomic Energy Research Institute, Daejeon (Korea, Republic of); Zhou, Zhangjian [School of Materials Science and Engineering, USTB, Beijing (China)

2015-05-15

Austenitic stainless steels are also among important structural materials for in-core components of nuclear reactors, and the performance, the oxidation resistance as well as the mechanical strength at high temperature are further expected after Fukushima accident. Alumina-forming austenitic (AFA) steel was first developed by Y. Yamamoto et al. , which showed a good combination of oxidation resistance and creep resistance. The strengthening is achieved through nano-sized MX and Laves. Microstructural evolution of Fe-18Ni-16Cr-4Al during aging at 950 .deg. C was studied. This steel consists of two phases of austenite and ferrite. During aging, needle-shaped NiAl precipitates in austenite, while round shaped NiAl form in ferrite, which is supposed to be due to different crystal structural parameters.

Effect of Cr, Ni, and Mo additions on the susceptibility of the 0Kh6n7m7c steel to hot cracking

International Nuclear Information System (INIS)

Tolstykh, L.G.; Pryakhin, A.V.; Popov, A.N.; Usynin, V.F.

1977-01-01

The effect of chromium, molybdenum, and nickel on the tendency of surfacing materials to form hot cracks (Vsub(kp) was studied using the mathematical statistics method. The St3 steel and 38KhN3MFA steel were used in the study. A device facilitating the hot cracking tendency test procedure was developed. It was found that, in the concentration range involved, Ni and Mo produce no effect on Vsub(kp), and Cr enhances it. A new powder wire, PP-OKh7N8M6S, capable of increasing surface material resistance by 1.5-2 times, has been developed

On mechanism of austenite chromium-nickel-molybdenum steels intercrystalline corrosion in weak and strong oxidizing media

International Nuclear Information System (INIS)

Plaskeev, A.V.; Savkina, L.Ya.; Knyazheva, V.M.; Kolotyrkin, Ya.M.; Fil'dgandler, Eh.G.; Rodin, N.N.

1975-01-01

Wide possibilities γ-spectrometry for kinetic investigation of intercrystalline corrosion (ICC) and also for recognizing the nature of the selectively soluble structural components at the stages of their initiation and development has been determined using 00Cr16Ni15Mo steel, containing 0,05 and 0,03%C. It is shown by γ-spectrometry, autoradiography, electrochemistry, optical and electron metallography in combination with (Cr,Fe,Mo) 23 C 6 carbide properties investigation, that ICC of sensitized 00Cr16Ni15Mo3 steel, is determined by selective dissolution of chromium and molybdenum depleted boundary regions of solid solutions. At potentials of passivation region (imitation of D method) the main cause of ICC is the selective dissolution of (Cr;Fe;Mo) 23 C 6 carbides arranged at grain boundaries. This process is facilitated in the presence of molybdenum in carbide

Residual stress determination by neutron diffraction in a car gear-shaft made of 20NiCrMo2 alloyed case hardening steel

Czech Academy of Sciences Publication Activity Database

Rogante, M.; Mazzanti, M.; Mikula, Pavol; Vrána, Miroslav

2012-01-01

Roč. 50, č. 4 (2012), s. 213-220 ISSN 0023-432X R&D Projects: GA ČR(CZ) GAP204/12/1360 Institutional support: RVO:61389005 Keywords : 20NiCrMo2 steel * gear-shaft * caser hardening * residual stress * neutron diffraction Subject RIV: BG - Nuclear, Atomic and Molecular Physics, Colliders Impact factor: 0.687, year: 2012

Hyperfine interaction and some thermomagnetic properties of amorphous and partially crystallized Fe70−xMxMo5Cr4Nb6B15 (M = Co or Ni, x = 0 or 10 alloys

Directory of Open Access Journals (Sweden)

Rzącki Jakub

2015-03-01

Full Text Available As revealed by Mössbauer spectroscopy, replacement of 10 at.% of iron in the amorphous Fe70Mo5Cr4Nb6B15 alloy by cobalt or nickel has no effect on the magnetic structure in the vicinity of room temperature, although the Curie point moves from 190 K towards ambient one. In the early stages of crystallization, the paramagnetic crystalline Cr12Fe36Mo10 phase appears before α-Fe or α-FeCo are formed, as is confirmed by X-ray diffractometry and transmission electron microscopy. Creation of the crystalline Cr12Fe36Mo10 phase is accompanied by the amorphous ferromagnetic phase formation at the expense of amorphous paramagnetic one.

Corrosion resistance of Ni-Cr-Mo alloys. Chemical composition and metallurgical condition's effects

International Nuclear Information System (INIS)

Zadorozne, N.S.; Rebak, Raul B.

2009-01-01

Ni-Cr-Mo alloys offer an outstanding corrosion resistance in a wide variety of highly-corrosive environments. This versatility is due to the excellent performance of nickel in hot alkaline solutions and the beneficial effect of chromium and molybdenum in oxidizing and reducing conditions, respectively. Alloy C-22 (22 % Cr-13 % Mo-3% W) is a well known versatile member of this family. Due to its excellent corrosion resistance in a wide variety of environments, Alloy C-22 has been selected for the fabrication of the corrosion-resistant outer shell of the high-level nuclear waste container. The increasing demand of the industry for corrosion resistant alloys with particular properties of corrosion and mechanical resistance has led to the development of new alloys. Alloy C-22HS (Ni-21 % Cr-17 % Mo) is a new high-strength corrosion resistant material recently developed and introduced into the market. This alloy provides a corrosion resistance comparable with that of other C-type alloys, and it can also be age hardened to effectively double its yield strength. HASTELLOY HYBRID-BC1 (Ni-22 % Mo-15 % Cr) is a new development intended for filling the gap between Ni-Mo and Ni-Cr-Mo alloys. This novel alloy is able to withstand HCl and H 2 SO 4 , even in the presence of dissolved oxygen and other oxidizing species. Its resistance to chloride-induced pitting corrosion, crevice corrosion and stress corrosion cracking is also remarkable. Thermal aging of Ni-Cr-Mo alloys leads to microstructure changes depending on the temperature range and exposure time at temperature. A Long Range Ordering (LRO) reaction can occur in the range of 350 C degrees to 600 C degrees, producing an ordered Ni 2 (Cr,Mo) phase. This ordering reaction does not seem to affect the corrosion resistance and produces only a slight loss in ductility. LRO transformation is homogeneous and has proven to be useful to fabricate the age-hard enable Alloy C22-HS. Tetrahedral Close Packed (TCP) phases, like μ, σ and

Crystal structure and ion conducting properties of La5NbMo2O16

KAUST Repository

Vu, T.D.

2016-01-29

The new compound La5NbMo2O16 with high ionic conduction has been discovered during the study of the ternary phase diagram of La2O3-MoO3-Nb2O5. The material crystallizes in the cubic space group Pn 3n (no 222) with the unit cell parameter a=11.2250(1) Å. La5NbMo2O16 is a new analogue of the R5Mo3O16 series (R=Pr, Nd). The structure was refined from a combined data X-ray and neutron powder diffraction. The ionic conductivity of the compound is then measured on sintered pellets, by means of complex impedance spectroscopy. © 2016 Elsevier Inc. All rights reserved.

Modelling and characterization of chi-phase grain boundary precipitation during aging of Fe-Cr-Ni-Mo stainless steel

International Nuclear Information System (INIS)

Xu, W.; San Martin, D.; Rivera Diaz del Castillo, P.E.J.; Zwaag, S. van der

2007-01-01

High molybdenum stainless steels may contain the chi-phase precipitate (χ, Fe 36 Cr 12 Mo 10 ) which may lead to undesirable effects on strength, toughness and corrosion resistance. In the present work, specimens of a 12Cr-9Ni-4Mo wt% steel are heat treated at different temperatures and times, and the average particle size and particle size distribution of chi-phase precipitate are studied quantitatively. A computer model based on the KWN framework has been developed to describe the evolution of chi-phase precipitation. The kinetic model takes advantage of the KWN model to describe the precipitate particle size distribution, and is coupled with the thermodynamic software ThermoCalc for calculating the instantaneous local thermodynamic equilibrium condition at the interface and the driving force for nucleation. A modified version of Zener's theory accounting for capillarity effects at early growth stages is implemented in this model. The prediction of the model for chi-phase precipitation at a grain boundary is compared to experimental results and both the average particle size and the particle size distribution are found to be in good agreement with experimental observations at late precipitation stages

Electron beam welding of heavy section 3Cr-1.5Mo alloy

International Nuclear Information System (INIS)

King, J.F.; David, S.A.; Nasreldin, A.

1986-01-01

Welding of thick section steels is a common practice in the fabrication of pressure vessels for energy systems. The fabrication cost is strongly influenced by the speed at which these large components can be welded. Conventional welding processes such as shielded metal arc (SMA) and submerged arc (SA) are time-consuming and expensive. Hence there is a great need to reduce welding time and the tonnage of weld metal deposited. Electron beam welding (EBW) is a process that potentially could be used to achieve dramatic reduction in the welding time and costs. The penetrating ability of the beam produces welds with high depth-to-width ratios at relatively high travel speeds, making it possible to weld thick sections with one or two passes without filler metals and other consumables. The paper describes a study that was undertaken to investigate the feasibility of using a high power electron beam welding machine to weld heavy section steel. The main emphasis of this work was concentrated on determining the mechanical properties of the resulting weldment, characterizing the microstructure of the various weldment regions, and comparing these results with those from other processes. One of the steels selected for the heavy section electron beam welding study was a new 3 Cr-1.5 Mo-0.1 V alloy. The steel was developed at the AMAX Materials Research Center by Wada and co-workers for high temperature, high pressure hydrogen service as a possible improved replacement for 2-1/4 Cr-1 Mo steels. The excellent strength and toughness of this steel make it a promising candidate for future pressure vessels such as those for coal gasifiers. The work was conducted on 102 mm (4 in.) thick plates of this material in the normalized-and-tempered condition

Molybdenum depletion around P-phases Ni-Cr-Mo-W weld metals

International Nuclear Information System (INIS)

Silva, Cleiton Carvalho; Miranda, Helio Cordeiro de; Farias, Jesualdo Pereira

2010-01-01

This work evaluated the local chemical composition in matrix/precipitate interface in a Ni-Cr-Mo-W alloy weld metals deposited on substrate of C-Mn steel. The microstructural characterization was carried out through optical microscopy, scanning electron microscopy (SEM), transmission electron microscopy (TEM) and energy dispersive X-ray spectroscopy (EDS). The results had shown that the presence of secondary phases precipitates in the interdendritic region. Through SEM analysis were observed indications of depletion of Mo around these phases. These precipitates were identified as P-phase by TEM analysis. The Mo depletion indications were confirmed through EDS. The Mo depletion was a result of a reheating due to several welding heat cycles deposited to promote the coating layer. (author)

Precipitation in 20 Cr-25 Ni type stainless steel irradiated at low temperatures in a thermal reactor (AGR)

International Nuclear Information System (INIS)

Taylor, C.

1983-01-01

The effects of irradiation on the microstructure of AGR fuel rod cladding have been studied by analytical electron microscopy. Two alloys were investigated, the standard 20 Cr-25 Ni steel stabilised with Nb and a variant containing less Nb but strengthened with a dispersion of TiN precipitates. Irradiation at 360 deg C to 480 deg C produced (Ni, Si)-rich precipitates in both alloys; additionally the standard alloy contained (Ni, Nb, Si)-rich precipitates when irradiated at 440 deg C to 640 deg C. While similar features have been observed in other austenitic stainless steels irradiated in fast reactors, where the lattice-damage rate is greater than in a thermal reactor, their formation is not predicted by isothermal equilibrium diagrams. It is suggested here that the phases are irradiation-induced and that the total displacement damage is the controlling factor. Cladding solution-treated above 1050 deg C then irradiated at 2 -based reactor coolant occurred in cladding with low levels of cold-work at the outer surface, also resulting in Cr-rich carbide formation. (author)

Abrasive wear resistance and microstructure of Ni-Cr-B-Si hardfacing alloys with additions of Al, Nb, Mo, Fe, Mn and C

International Nuclear Information System (INIS)

Berns, H.; Fischer, A.; Theisen, W.

1987-01-01

The development of new Ni-base hardfacing alloys for filler wire welding or metal spraying should result in materials with a good resistance against high temperature corrosion and abrasive wear. The first step is to design microstructures, which obtain a satisfactory abrasive wear behaviour at room temperature. Thus, different alloys are melted and scrutinized as to their microstructure and their abrasive wear resistance in laboratory. Compared to commercial Ni-base hardfacing alloys they show a higher volume fraction of coarse hard phases due to the additional, initial solidification of Nb-carbides and Cr-, and Mo-borides. Thus, the abrasive wear resistance is improved. For hard abrasive particles, such as corundum, the Ni-base alloys are more wear resistant than harder Fe-base alloys investigate earlier. This is due to the tougher Ni metal matrix that results in microcracking not to be the most significantly acting wear mechanism

Creep Rupture Analysis and Life Estimation of 1.25Cr-0.5Mo, 2.25Cr-1Mo and Modified 9Cr-1Mo Steel: A Comparative Study

Science.gov (United States)

Roy, Prabir Kumar

2018-04-01

This paper highlights a comparative assessment of creep life of 1.25Cr-0.5Mo, 2.25Cr-1Mo and modified 9Cr-1Mo steels based on accelerated creep rupture tests. Creep rupture test data have been analysed and creep life of the above mentioned materials have been assessed using Larson Miller parameter at the stress levels of 60 and 42 MPa for different temperatures. Limiting steam temperatures for minimum design life of 105 h at 42 and 60 MPa for the above mentioned steels have also been calculated. Microstructural studies for the three above mentioned steels are also done.

Kinetics of Cr/Mo-rich precipitates formation for 25Cr-6.9Ni-3.8Mo-0.3N super duplex stainless steel

Science.gov (United States)

Byun, Sang-Ho; Kang, Namhyun; Lee, Tae-Ho; Ahn, Sang-Kon; Lee, Hae Woo; Chang, Woong-Seong; Cho, Kyung-Mox

2012-04-01

The amount and composition of Cr-rich (σ) and Mo-rich (χ) precipitates in super duplex stainless steels was analyzed. An isothermal heat treatment was conducted at temperatures ranging from 700 °C to 1000 °C for up to 10 days. A time-temperature transformation (TTT) diagram was constructed for the mixture of σ and χ phases. The mixture of the σ and χ phases exhibited the fastest rate of formation at approximately 900 °C. Minor phases, such as Cr2N, M23C6, and M7C3, were also detected using a transmission electron microscopy (TEM). Also, a continuous cooling transformation (CCT) diagram was constructed for the mixture of σ and χ phases using the Johnson-Mehl-Avrami equation. Compared with the known CCT diagram of the σ phase, this study revealed faster kinetics with an order of magnitude difference and a new CCT diagram was also developed for a mixture of σ and χ phases. The calculated fraction of σ and χ phases obtained at a cooling speed of 0.5 °C/s was in good agreement with the experimental data.

Establishment of Wear Resistant HVOF Coatings for 50CrMo4 Chromium Molybdenum Alloy Steel as an Alternative for Hard Chrome Plating

Science.gov (United States)

Karuppasamy, S.; Sivan, V.; Natarajan, S.; Kumaresh Babu, S. P.; Duraiselvam, M.; Dhanuskodi, R.

2018-05-01

High cost imported components of seamless steel tube manufacturing plants wear frequently and need replacement to ensure the quality of the product. Hard chrome plating, which is time consuming and hazardous, is conventionally used to restore the original dimension of the worn-out surface of the machine components. High Velocity Oxy-Fuel (HVOF) thermal spray coatings with NiCrBSi super alloy powder and Cr3C2 NiCr75/25 alloy powder applied on a 50CrMo4 (DIN-1.7228) chromium molybdenum alloy steel, the material of the wear prone machine component, were evaluated for use as an alternative for hard chrome plating in this present work. The coating characteristics are evaluated using abrasive wear test, sliding wear test and microscopic analysis, hardness test, etc. The study results revealed that the HVOF based NiCrBSi and Cr3C2NiCr75/25 coatings have hardness in the range of 800-900 HV0.3, sliding wear rate in the range of 50-60 µm and surface finish around 5 microns. Cr3C2 NiCr75/25 coating is observed to be a better option out of the two coatings evaluated for the selected application.

Characteristics of centrifugally cast GX25CrNiSi18-9 steel

Directory of Open Access Journals (Sweden)

R. Zapała

2011-07-01

Full Text Available The paper presents the results of microstructural examinations of the industrial heat-resistant centrifugally cast GX25CrNiSi18-9 steel characterised by increased content of Cu. The study included changes in the microstructure of base cast steel respective of the steel held at a temperature of 900 and 950°C for 48 hours. Based on the results obtained, an increase in microhardness of the examined cast steel matrix with increasing temperature was stated, which was probably caused by fine precipitates enriched in Cr, Mo, and C forming inside the matrix grains.The layer of scale formed on the tested cast steel oxidised in the atmosphere of air at 900 and 950°C was characterised by an increased tendency to degradation with increasing temperature of the conducted tests.

Corrosion resistance of amorphous NiCrZr and NiCrMoZr alloys

International Nuclear Information System (INIS)

Naka, M.; Miyake, M.; Okamoto, I.

1987-01-01

One of the authors has reported that the corrosion resistance of chromium containing amorphous alloys is extremely improved by alloying phosphorus among metalloids. Two factors operate for the improvement of corrosion resistance of the amorphous alloys. First, phosphorus serves for the rapid formation of protective passive film. Second, the compositional and structural homogeneity in amorphous state also account for the formation of protective film. The latter factor has been clearly seen in the high corrosion resistance of CoCrMoZr and CoCrWZr alloys without metalloids. In order to clarify the separately two factors in the corrosion resistance of amorphous alloys, the corrosion resistance of amorphous alloys without metalloids has to be further investigated. This paper also deals with the corrosion resistance and electrochemical behavior of NiCrZr and NiCrMoZr alloys in 1N HCl, and compare them with the corrosion behavior of the crystalline alloys containing the same composition as that of the amorphous alloys

Precipitation hardening in a 12%Cr-9%Ni-4%Mo-2%Cu stainless steel

International Nuclear Information System (INIS)

Haettestrand, Mats; Nilsson, Jan-Olof; Stiller, Krystyna; Liu Ping; Andersson, Marcus

2004-01-01

A combination of complementary techniques including one-dimensional and three-dimensional atom probe, energy-filtered transmission electron microscopy and conventional transmission electron microscopy has been used to assess the precipitation reactions at 475 deg. C in a 12%Cr-9%Ni-4%Mo-2%Cu precipitation hardening stainless steel. The continuous hardening up to at least 1000 h of ageing was attributed to a sequence of precipitation reactions involving nickel-rich precipitates nucleating at copper clusters followed by molybdenum-rich quasicrystalline precipitates and nickel-rich precipitates of type L1 0 . An estimate of the relative contributions to the strength increment during tempering based on measurements of particle densities was performed. Nickel-rich precipitates were found to play the most important role up to about 40 h of ageing after which the effect of quasicrystalline particles became increasingly important

Ion backscattering, channeling and nuclear reaction analysis study of passive films formed on FeCrNi and FeCrNiMo (100) single crystals

Energy Technology Data Exchange (ETDEWEB)

Cohen, C; Schmaus, D [Paris-7 Univ., 75 (France). Groupe de Physique des Solides de l' ENS; Elbiache, A; Marcus, P [Ecole Nationale Superieure de Chimie, 75 - Paris (France)

1990-01-01

The compositions of passive films formed on Fe-17Fr-13Ni (at. %) and Fe-18.5Cr-14Ni-1.5Mo (100) single crystals have been determined and the structure of the alloy under the film has been investigated. The alloys were passivated in 0.05M H{sub 2}SO{sub 4} at 250 mV/SHE for 30 min. The oxygen content was measured by nuclear microanalysis using the {sup 16}O(d,p) {sup 17}O* reaction. The oxygen content in the passive film is similar for the two alloys and equal to (12{plus minus}2) 10{sup 15} O/cm{sup 2}. The cationic compositions of the passive films have been determined by {sup 4}He channeling at two incident beam energies: 0.8 and 2.0 MeV. For the two alloys studied, a total cation content of (5{plus minus}2)10{sup 15} at/cm{sup 2} is found in the passive films. The corresponding thickness is about 12 A. There is an excess of oxygen, which can be attributed to the presence of hydroxyls and sulfate. A strong chromium enrichment is found in the passive film formed on both alloys: chromium represents about 50% of the cations. There is no evidence of molybdenum enrichment in the passive film formed on the Mo-alloyed stainless steel. The comparison of the results obtained at the two different incident beam energies (0.8MeV and 2MeV) reveals the existence of defects at the alloy/passive film interface. (author).

Effect of Mo contents on corrosion behaviors of welded duplex stainless steel

Science.gov (United States)

Bae, Seong Han; Lee, Hae Woo

2013-05-01

The corrosion behaviour and change of the phase fraction in welded 24Cr Duplex stainless steel was investigated for different chemical composition ranges of Mo contents. Filler metal was produced by fixing the contents of Cr, Ni, N, and Mn while adjusting the Mo content to 0.5, 1.4, 2.5, 3.5 wt%. The δ-ferrite fraction was observed to increase as the content of Mo increased. A polarisation test conducted in a salt solution, indicated the pitting corrosion potential increased continuously to 3.5 wt% Mo, while the corrosion potential changed most between 0.5 and 1.41 wt% Mo. The location of the pitting corrosion in 0.5 wt% Mo steel was randomly distributed, but it occurred selectively at the grain boundary between the γ- and δ-ferrite phases in 1.4, 2.5 and 3.5 wt% Mo steel. Energy dispersive X-ray spectroscopy mapping analysis showed that areas deficient in Cr, Mo, and Ni occurred around the grain boundary of the γ- and δ-ferrite phases. Non-metallic inclusions are thought to act as initiation points for the pitting corrosion that occurs in the salt solution initially as a result of the potential difference between the matrix structure and the incoherent inclusions.

Stress corrosion cracking in 3,5 NiCrMoV steel in a 403 K potential-PH diagram

International Nuclear Information System (INIS)

Hitomi, Itoh; Takashi, Momoo

2001-01-01

3,5 NiCrMoV steel is used in low-pressure turbine rotors and discs. It has been pointed out that intergranular stress corrosion cracking may occur in this material in the wet region at temperatures of about 400 K. Accordingly, the authors focused on the environmental conditions under which stress corrosion cracking (SCC) occurs. A potential-pH diagram was used to investigate the region in which SCC occurs in the high strength materials that are particularly susceptible to SCC. The investigation found that SCC is initiated in this material not only in the high caustic region but in the neutral region as well. The investigation also found that initiation and propagation were accelerated in dissolved oxygen environments with increased chemical potential in the neutral region. Since careful observation of the starting point of cracks has shown that corrosion pits trigger SCC, subsequent immersion tests under constant potential were conducted. The results showed that corrosion pits are generated at the high potential range. These results led to the development of an acceleration test environment for laboratory to determine the susceptibility of SCC in field turbine disc and rotor materials. (author)

Effects of Microalloying on the Microstructures and Mechanical Properties of Directionally Solidified Ni-33(at.%)Al-31Cr-3Mo Eutectic Alloys Investigated

Science.gov (United States)

Whittenberger, J. Daniel; Raj, Sai V.; Locci, Ivan E.; Salem, Jonathan A.

2002-01-01

Despite nickel aluminide (NiAl) alloys' attractive combination of oxidation and thermophysical properties, their development as replacements for superalloy airfoils in gas turbine engines has been largely limited by difficulties in developing alloys with an optimum combination of elevated-temperature creep resistance and room-temperature fracture toughness. Alternatively, research has focused on developing directionally solidified NiAl-based in situ eutectic composites composed of NiAl and (Cr,Mo) phases in order to obtain a desirable combination of properties a systematic investigation was undertaken at the NASA Glenn Research Center to examine the effects of small additions of 11 alloying elements (Co, Cu, Fe, Hf, Mn, Nb, Re, Si, Ta, Ti, and Zr) in amounts varying from 0.25 to 1.0 at.% on the elevated-temperature strength and room-temperature fracture toughness of directionally solidified Ni-33Al-31Cr-3Mo eutectic alloy. The alloys were grown at 12.7 mm/hr, where the unalloyed eutectic base alloy exhibited a planar eutectic microstructure. The different microstructures that formed because of these fifth-element additions are included in the table. The additions of these elements even in small amounts resulted in the formation of cellular microstructures, and in some cases, dendrites and third phases were observed. Most of these elemental additions did not improve either the elevated-temperature strength or the room-temperature fracture toughness over that of the base alloy. However, small improvements in the compression strength were observed between 1200 and 1400 K when 0.5 at.% Hf and 0.25 at.% Ti were added to the base alloy. The results of this study suggest that the microalloying of Ni-33Al-31Cr-3Mo will not significantly improve either its elevatedtemperature strength or its room-temperature fracture toughness. Thus, any improvements in these properties must be acquired by changing the processing conditions.

Atomic displacements in dilute alloys of Cr, Nb and Mo

Indian Academy of Sciences (India)

physics pp. 497–514. Atomic displacements in dilute alloys of Cr, Nb and Mo ... used to calculate dynamical matrix and the impurity-induced forces up to second nearest ... origin, the lattice is strained, and the host atoms get displaced to new ...

A comparison of low-chromium and high-chromium reduced-activation steels for fusion applications

International Nuclear Information System (INIS)

Klueh, R.L.; Maziasz, P.J.; Alexander, D.J.

1996-01-01

Ferritic steels have been considered candidate structural materials for first wall and blanket structures for fusion power plants since the late 1970s. The first steels considered in the United States were the conventional Cr-Mo steels Sandvik HT9 (nominally 12Cr-1Mo-0.25V-0.5W-0.5Ni-0.2C, here designated l2Cr-1MoVW), modified 9Cr-1Mo steel (9Cr-1Mo-0.2V-0.06Nb-0. IC, designated 9Cr-1MoVNb) and, to a lesser extent, 2 1/4Cr-1Mo steel (2.25Cr-Mo-0.1C). All compositions are in wt. %. The normalized-and-tempered 9 and 12Cr steels had a tempered martensite microstructure, and the normalized-and-tempered 2 1/4 Cr steel had a tempered bainite microstructure. This report describes chromium steels tested in normalized and tempered conditions. Miniature tensile and Charpy specimens were tested

Impact behavior of 9-Cr and 12-Cr ferritic steels after low-temperature irradiation

International Nuclear Information System (INIS)

Klueh, R.L.; Vitek, J.M.; Corwin, W.R.; Alexander, D.J.

1987-01-01

Miniature Charpy impact specimens of 9Cr-1MoVNb and 12Cr-1MoVW steels and these steels with 1 and 2% Ni were irradiated in the High-Flux Isotope Reactor (HFIR) at 50 0 C to displacement damage levels of up to 9 dpa. Nickel was added to study the effect of transmutation helium. Irradiation caused an increase in the ductile-brittle transition temperature (DBTT). The 9Cr-1MoVNb steels, with and without nickel, showed a larger shift than the 12Cr-1MoVW steels, with and without nickel. The results indicated that helium also increased the DBTT. The same steels were previously irradiated at higher temperatures. From the present and past tests, the effect of irradiation temperature on the DBTT behavior can be evaluated. For the 9Cr-1MoVNb steel, there is a continuous decrease in the magnitude of the DBTT increase up to an irradiation temperature of about 400 0 C, after which the shift drops rapidly to zero at about 450 0 C. The DBTT of the 12Cr-1MoVW steel shows a maximum increase at an irradiation temperature of about 400 0 C and less of an increase at either higher or lower irradiation temperatures

Correlation of Yield Stress And Microhardness in 08cr16ni11mo3 Irradiated To High Dose In The Bn-350 Fast Reactor

International Nuclear Information System (INIS)

Maksimkin, O.P.; Gusev, M.N.; Tivanova, O.S.; Silnaygina, N.S.; Garner, Francis A.

2006-01-01

The relationship between values of the microhardness and the engineering yield stress in steel 08Cr16Ni11Mo3 (Russian analog of AISI 316) heavily irradiated in the BN-350 reactor has been experimentally derived. It agrees very well with the previously published correlation developed by Toloczko for unirradiated 316 in a variety of cold-work conditions. Even more importantly, when the correlation is derived in the K δ format where the correlation involves changes in the two properties, we find excellent agreement with a universal K δ correlation developed by Busby and coworkers. With this K δ correlation, one can predict the value of yield stress in irradiated material based on measured values of microhardness. The technique is particularly suitable when the material of interest is in an inconvenient location or configuration, or when significant gradients in mechanical properties are anticipated over small dimensions. This approach makes it possible to reduce the labor input and risk when conducting such work. It appears that the derived correlation is equally applicable to both Russian and Western austenitic steel, and also in both irradiated and unirradiated conditions. Additionally, this report points out that microhardness measurements must take into account that high temperature sodium exposure alters the metal surface to produce ferrite, and therefore the altered layers should be removed prior to testing

Supercritical water corrosion of high Cr steels and Ni-base alloys

International Nuclear Information System (INIS)

Jang, Jin Sung; Han, Chang Hee; Hwang, Seong Sik

2004-01-01

High Cr steels (9 to 12% Cr) have been widely used for high temperature high pressure components in fossil power plants. Recently the concept of SCWR (supercritical water-cooled reactor) has aroused a keen interest as one of the next generation (Generation IV) reactors. Consequently Ni-base (or high Ni) alloys as well as high Cr steels that have already many experiences in the field are among the potential candidate alloys for the cladding or reactor internals. Tentative inlet and outlet temperatures of the anticipated SCWR are 280 and 510 .deg. C respectively. Among many candidate alloys there are austenitic stainless steels, Ni base alloys, ODS alloys as well as high Cr steels. In this study the corrosion behavior of the high Cr steels and Ni base (or high Ni) alloys in the supercritical water were investigated. The corrosion behavior of the unirradiated base metals could be used in the near future as a guideline for the out-of-pile or in-pile corrosion evaluation tests

Sintering behaviour and mechanical properties of Cr3C2–NiCr ...

Indian Academy of Sciences (India)

fracture toughness. Keywords. Cermet; Cr3C2–NiCr; sintering; mechanical properties. ... et al investigated the mechanical properties of VC, Cr3C2 and NbC doped ..... Huang S G, Li L, Van der Biest O and Vleugels J 2008 J. Alloys. Compds.

Toughness of 2,25Cr-1Mo steel and weld metal

Science.gov (United States)

Acarer, Mustafa; Arici, Gökhan; Acar, Filiz Kumdali; Keskinkilic, Selcuk; Kabakci, Fikret

2017-09-01

2,25Cr-1Mo steel is extensively used at elevated temperature structural applications in fossil fire power plants for steam pipes, nozzle chambers and petrochemical industry for hydrocracking unit due to its excellent creep resistance and good redundant to oxidation. Also they should have acceptable weldability and toughness. The steels are supplied in quenched and tempered condition and their welded components are subjected to post-weld heat treatment (PWHT). Tempering process is carried out at 690-710°C to improve toughness properties. However they are sensitive to reheat cracking and temper embrittlement. To measure temper embrittlement of the steels and their weld metal, temper embrittlement factor and formula (J factor - Watanabe and X formula- Bruscato) are used. Step cooling heat treatment is also applied to determine temper embrittlement. In this study, toughness properties of Cr Mo (W) steels were reviewed. Also transition temperature curves of 2,25Cr-1Mo steel and its weld metal were constructed before and after step cool heat treatment as experimental study. While 2,25Cr-1Mo steel as base metal was supplied, all weld metal samples were produced in Gedik Welding Company. Hardness measurements and microstructure evaluation were also carried out.

Ternary alloying study of MoSi2

International Nuclear Information System (INIS)

Yi, D.; Li, C.; Akselsen, O.M.; Ulvensoen, J.H.

1998-01-01

Ternary alloying of MoSi 2 with adding a series of transition elements was investigated by X-ray diffraction (XRD), scanning electron microscopy, transmission electron microscopy (TEM), and energy dispersive spectroscopy (EDS). Iron, Co, Ni, Cr, V, Ti, and Nb were chosen as alloying elements according to the AB 2 structure map or the atomic size factor. The studied MoSi 2 base alloys were prepared by the arc melting process from high-purity metals. The EDS analysis showed that Fe, Co, and Ni have no solid solubility in as-cast MoSi 2 , while Cr, V, Ti, and Nb exhibit limited solid solubilities, which were determined to be 1.4 ± 0.7, 1.4 ± 0.4, 0.4 ± 0.1, and 0.8 ± 0.1. Microstructural characterization indicated that Mo-Si-M VIII (M VIII = Fe, Co, Ni) and Mo-Si-Cr alloys have a two-phase as-cast microstructure, i.e., MoSi 2 matrix and the second-phase FeSi 2 , CoSi, NiSi 2 , and CrSi 2 , respectively. In as-cast Mo-Si-V, Mo-Si-Ti, and Mo-Si-Nb alloys, besides MoSi 2 and C40 phases, the third phases were observed, which have been identified to be (Mo, V) 5 Si 3 , TiSi 2 , and (Mo, Nb) 5 Si 3

Corrosion Study of Super Ferritic Stainless Steel UNS S44660 (26Cr-3Ni-3Mo) and Several Other Stainless Steel Grades (UNS S31603, S32101, and S32205) in Caustic Solution Containing Sodium Sulfide

Science.gov (United States)

Chasse, Kevin R.; Singh, Preet M.

2013-11-01

Electrochemical techniques, scanning electron microscopy (SEM), and X-ray photoelectron spectroscopy (XPS) were used in this study to show how the corrosion mechanism of several commercial grades of stainless steel in hot caustic solution is strongly influenced by the presence of sodium sulfide. Experimental results from super ferritic stainless steel UNS S44660 (26Cr-3Ni-3Mo) were compared to austenitic stainless steel UNS S31603, lean duplex stainless steel (DSS) UNS S32101, and standard DSS UNS S32205 in caustic solution, with and without sodium sulfide, at 443 K (170 °C). Weight loss measurements indicated that corrosion rates of UNS44660 were much lower than the other grades of stainless steel in the presence of the sodium sulfide. Potentiodynamic polarization and linear polarization resistance measurements showed that the electrochemical behavior was altered by the adhesion of sulfur species, which reduced the polarization resistances and increased the anodic current densities. SEM and XPS results imply that the surface films that formed in caustic solution containing sodium sulfide were defective due to the adsorption of sulfide, which destabilized the passive film and led to the formation of insoluble metal sulfide compounds.

Effect of heat treatment on pitting corrosion of austenitic Cr-Ni-Mo steels in sodium chloride solution

International Nuclear Information System (INIS)

Stefec, R.; Franz, F.; Holecek, A.

1979-01-01

The pitting corrosion resistance of Cr17Ni12Mo2,5 type steel under potentiostatic polarization in a sodium chloride solution is adversely affected by previous annealing. The data obtained were systematically dependent on annealing temperature, time and surface roughness. The corrosion current, the number of pits or the mean area of pit opening and the corrosion rate within the pits were increased by previous annealing at 550 to 750 0 C for 1-100 hrs. The highest corrosion rate estimated corresponded to heat treatments provoking severe sensitization to intergranular corrosion. The paercentage area of corrosion pit openings and the estimated pit penetration rates were several times higher for as-machined than for polished surfaces. It can be assumed that pitting corrosion is little affected by the carbon content and that molybdenum depletion of grain-boundary zones is responsible for the reduced pitting resistance of annealed steels. (orig./HP) [de

Effect of various heat treatments on microstructure and mechanical properties of 34CrNiMo6 steel

International Nuclear Information System (INIS)

Abd El-Azim, M.E.; Ghoneim, M.M.; Nasreldin, A.M.; Soliman, S.

1997-01-01

Three different austenitization treatments were applied to high strength 34CrNiMo6 steel: conventional austenitization (CAT), high temperature austenitization (HTA) and duplex treatment (DT). It was found that DT structure has finer prior austenite grain size (30 μm) than those of HTA (200 μm) and CAT (70 μm) structures. DT and HTA structures have coarser lath size for martensite than CAT structure. DT results in higher room temperature impact toughness than HTA and CAT structures and shifts the ductile-brittle transition to lower temperatures by 14 K and 32 K in comparison with HTA and CAT structures, respectively. However, DT structure has intermediate values of room temperature yield stress and ultimate tensile strength between those of CAT and HTA structures. When this steel was tempered at 300 and 400 C it underwent tempered martensite embrittlement associated with intergranular fracture. (orig.)

Binary and tertiary reaction cross-sections of V, Cr, Mn, Fe, Ni, Cu, Zr, Nb, Mo, Ta, W, Pt and their isotopes

International Nuclear Information System (INIS)

Garg, S.B.

1982-01-01

Neutron induced binary and tertiary reaction cross-sections have been evaluated for V, Cr, Mn, Fe, Ni, Cu, Zr, Nb, Mo, Ta, W, Pt and their isotopes in the 'energy range 0.5 MeV to 20 MeV using the nuclear statistical empirical model. The reactions considered are (n,n'), (n,2n), (n,3n), (n,p), (n,d), (n,t), (n, 3 He), (n,α), (n,np), (n,nd), (n,nt), (n,n 3 He), (n,nα), (n,pn), (n,2p), (n,ν), (n,αp), (n,dn) and (n,pα). Most of the above mentioned elements are used as structural materials in nuclear reactors and the measured cross-section data for the above listed reactions are seldom available for the radiation damage and safety analysis. With a view to providing these data, this nuclear model based evaluation has been undertaken. The associated uncertainties in the cross-sections and their fission averages have also been evaluated. (author)

The Structure and Mechanical Properties of Ni-Mo PM Steels with Addition of Mn And Cu

Science.gov (United States)

Lichańska, E.; Kulecki, P.; Pańcikiewicz, K.

2017-12-01

The aim of the study was to evaluate the effect of chemical composition on the structure and mechanical properties of Mn-Ni-Mo and Ni-Mo-Cu PM steels. Pre-alloyed powder Astaloy 85Mo, diffusion alloyed powders Distaloy AQ and Distaloy AB produced by Höganäs, low carbon ferromanganese, carbonyl nickel powder T255 with three-dimensional filamentary structure and graphite CU-F have been used as the basic powders. Three mixtures with compositions of Fe-1%Mn-(0.5/1.75)%Ni-(0.5/0.85)%Mo-0.8%C and Fe-1.75%Ni-0.5%Mo-1.5%Cu-0.8%C were prepared in a Turbula mixer. Green compacts were single pressed in a steel die at 660 MPa according to PN-EN ISO 2740 standard. Sinterhardening was carried out at 1250°C in a mixture of 95% N2+5% H2 for 60 minutes. Mechanical tests (tensile, bend, hardness) and microstructural investigations were performed. Additionally, XRD and EDS analysis, fractographic investigations were carried out. The microstructures of steels investigated were mainly bainitic or bainitic-martensitic. Addition 1% Mn to Distaloy AQ based steel caused increase of tensile properties (YS from 422 to 489 MPa, UTS from 522 to 638 MPa, TRS from 901 to 1096 MPa) and decrease of plasticity (elongation from 3.65 to 2.84%).

Estimation of the Temperature-Dependent Nitrogen Solubility in Stainless Fe-Cr-Mn-Ni-Si-C Steel Melts During Processing

Science.gov (United States)

Wendler, Marco; Hauser, Michael; Sandig, Eckhard Frank; Volkova, Olena

2018-04-01

The influence of chemical composition, temperature, and pressure on the nitrogen solubility of various high alloy stainless steel grades, namely Fe-14Cr-(0.17-7.77)Mn-6Ni-0.5Si-0.03C [wt pct], Fe-15Cr-3Mn-4Ni-0.5Si-0.1C [wt pct], and Fe-19Cr-3Mn-4Ni-0.5Si-0.15C [wt pct], was studied in the melt. The temperature-dependent N-solubility was determined using an empirical approach proposed by Wada and Pehlke. The thus calculated N-concentrations overestimate the actual N-solubility of all the studied Fe-Cr-Mn-Ni-Si-C steel melts at a given temperature and pressure. Consequently, the calculation model has to be modified by Si and C because both elements are not recognized in the original equation. The addition of the 1st and 2nd order interaction parameters for Si and C to the model by Wada and Pehlke allows a precise estimation of the temperature-dependent nitrogen solubility in the liquid steel bath, and fits very well with the measured nitrogen concentrations during processing of the steels. Moreover, the N-solubility enhancing effect of Cr- and Mn-additions has been demonstrated.

Creep and creep fatigue crack behavior of 1Cr- and 9Cr-steels

International Nuclear Information System (INIS)

Maile, K.; Klenk, A.; Schellenberg, G.; Granacher, J.; Tramer, M.

2000-01-01

A large database for creep crack initiation and propagation under constant load conditions is available on conventional power plant steels of types 1%Cr and 12%Cr. Modern plants are often used in the medium and peak load regime, thus the dominant loading situation in high temperature components is creep fatigue. For life assessment data about crack initiation and growth under creep fatigue loading are required. These characteristics can not be substituted by pure fatigue or creep crack data. Therefore, a comprehensive test programme was started to investigate the creep fatigue crack behaviour of a 1%CrMoNiV turbine rotor steel (30CrMoNiV 4 11) at 550 C and a new 9%CrMoVNb pipe steel (type P 9 1) at 600 C. DENT-specimen with 15 and 60 mm thickness as well as side grooved CT-specimen with 25 and 50 mm thickness have been tested to determine possible influences of geometry and thus to check the transferability of the data to components. The creep fatigue crack growth results of tests with dwell times between t H = 0,32h and 10 h lie in the scatterbands given by creep crack growth results. Nevertheless a higher crack growth rate under creep fatigue conditions can be stated. An increase in crack growth rate due to creep fatigue is clearly visible. Loading situations with frequencies higher than 1.10 -4 Hz should be not assessed with pure creep crack results or sufficient safety margins have to be applied. (orig.)

Effect of combined addition of N and Nb on the high temperature behavior of a 25Cr-20Ni stainless steel

International Nuclear Information System (INIS)

Park, In Duck; Nam, Ki Woo

2002-01-01

In order to clarify the effect of precipitates on creep strength at high temperature in 25Cr-20Ni stainless steels, threshold stress and void-hardening stress have been measured and compared each others. The value of threshold stress for high temperature, measured by stress abruptly loading test, is about 130 MPa. Threshold stress must be measured by the function of stress loading time in the combination hardening steel of solution hardening and precipitate hardening. Average diameter and inter-partial distance of precipitates from TEM microstructure can determine void-hardening stress. The value of void-hardening stress, evaluated by using Scattergood and Bacon's equation, was from 101 to 130 MPa. The ratio of average void hardening to threshold stress is 1.13 and both values are not equal. The result from analyzing the electron diffraction pattern shows that the dispersed precipitates in SUS310J1TB is NbCrN nitrides. Mechanism of the interaction between dislocations and precipitate particles in SUS310J1TB is Srolovitz mechanism, which is a gravitation-type interaction

Heat treatment for improvement in lower temperature mechanical properties of 0.40 pct C-Cr-Mo ultrahigh strength steel

Science.gov (United States)

Tomita, Yoshiyuki; Okabayashi, Kunio

1983-11-01

In the previous paper, it was reported that isothermal heat treatment of a commercial Japanese 0.40 pct C-Ni-Cr-Mo ultrahigh strength steel (AISI 4340 type) at 593 K for a short time followed by water quenching, in which a mixed structure of 25 vol pct lower bainite and 75 vol pct martensite is produced, results in the improvement of low temperature mechanical properties (287 to 123 K). The purpose of this paper is to study whether above new heat treatment will still be effective in commercial practice for improving low temperature mechanical properties of the ultrahigh strength steel when applied to a commercial Japanese 0.40 pct C-Cr-Mo ultrahigh strength steel which is economical because it lacks the expensive nickel component (AISI 4140 type). At and above 203 K this new heat treatment, as compared with the conventional 1133 K direct water quenching treatment, significantly improved the strength, tensile ductility, and notch toughness of the 0.40 pct C-Cr-Mo ultrahigh strength steel. At and above 203 K the new heat treatment also produced superior fracture ductility and notch toughness results at similar strength levels as compared to those obtained by using γ α' repetitive heat treatment for the same steel. However, the new heat treatment remarkably decreased fracture ductility and notch toughness of the 0.40 pct C-Cr-Mo ultrahigh strength steel below 203 K, and thus no significant improvement in the mechanical properties was noticeable as compared with the properties produced by the conventional 1133 K direct water quenching treatment and the γ α' repetitive heat treatment. This contrasts with the fact that the new heat treatment, as compared with the conventional 1133 K direct water quenching treatment and the γ α' repetitive heat treatment, dramatically improved the notch toughness of the 0.40 pct C-Ni-Cr-Mo ultrahigh strength steel, providing a better combination of strength and ductility throughout the 287 to 123 K temperature range. The difference

Effect of ion plating TiN on the oxidation of sputtered NiCrAlY-coated Ti3Al-Nb in air at 850-950 C

International Nuclear Information System (INIS)

Rizzo, F.C.; Zeng, C.; Chinese Academy of Sciences, Shenyang; Wu, W.

1998-01-01

A single sputtered NiCrAlY coating and a complex coating of inner ion-plated TiN and outer sputtered NiCrAlY were prepared on the intermetallic compound Ti 3 Al-Nb. Their oxidation behavior was examined at 850, 900, and 950 C in air by thermal gravimetry combined with XRD, SEM, and EDAX. The results showed that Ti 3 Al-Nb followed approximately parabolic oxidation, forming an outer thin Al 2 O 3 -rich scale and an inner TiO 2 -rich layer doped with Nb at the three temperatures. The TiO 2 -rich layer doped with Nb dominated the oxidation reaction. The single NiCrAlY coating did not follow parabolic oxidation exactly at 850 and 950 C, but oxidized approximately in a parabolic manner, because the instantaneous parabolic constants changed slightly with time. Besides the Al 2 O 3 scale, TiO 2 formed from the coating surface at the coating-substrate interface. The deterioration of the coating accelerated with increasing temperature. The NiCrAlY-TiN coating showed two-stage parabolic oxidation at 850 and 900 C, and an approximate parabolic oxidation at 950 C. The TiN layer was effective as a barrier to inhibit coating-alloy interdiffusion

The role of Ti, Zr and Ce in shaping of the Cr-Ni-Nb cast steel resistance to carburising

Directory of Open Access Journals (Sweden)

G. Tęcza

2008-08-01

Full Text Available From the centrifugally cast Cr-Ni-Nb steel pipes, specimens were cut out and subjected to carburising for 100 hours in a mixture of charcoal (90% and Na2CO3 (10% at the temperatures of 950 and 1150°C. The specimens were cut in direction normal to the pipe axis and were examined by optical and scanning microscopy. As a parameter describing the resistance of the examined alloy to the carburising effect, the thickness of a carburised layer was accepted. It has been observed that additions of Ti and Zr, and of Ti+Zr+Ce introduced jointly, increase the thickness of the carburised layer, while the addition of Ce improves the alloy resistance to carburising. On the alloy surface, a layer composed of oxides, mainly of chromium, silicon and iron, has been formed. Changes in the chemical composition of the surface layer were examined by scanning microscopy.

Effects of sodium environment on the mechanical properties of Fe-2 1/4Cr-1Mo steel

International Nuclear Information System (INIS)

Chopra, O.K.

1983-09-01

Mechanical property data on isothermally annealed, thermally aged, and sodium-exposed Fe-2 1/4Cr-1Mo steel are analyzed to evaluate the influence of the sodium environment as well as the effects of the microstructural and compositional changes that occur in the steel during long-term exposure to sodium. Correlations are developed to predict the environmental effects on tensile, creep, fatigue, and creep-fatigue properties of Fe-2 1/4Cr-1Mo steel in sodium. The results indicate that at temperatures 0 C), degradation of mechanical properties is essentially due to thermal aging. Loss of carbon from the steel reduces both the tensile and creep-rupture strength, but has little or no effect on the fatigue properties. The cyclic properties of Fe-2 1/4Cr-1Mo steel in sodium are superior to those in air. The creep-fatigue behavior in sodium is significantly different from that in an air environment. The creep-fatigue data are analyzed using the interactive damage rate equations to predict the time-dependent fatigue behavior of isothermally annealed Fe-2 1/4Cr-1Mo steel in sodium. 15 references, 7 figures, 1 table

Monotonic and Cyclic Behavior of DIN 34CrNiMo6 Tempered Alloy Steel

Directory of Open Access Journals (Sweden)

Ricardo Branco

2016-04-01

Full Text Available This paper aims at studying the monotonic and cyclic plastic deformation behavior of DIN 34CrNiMo6 high strength steel. Monotonic and low-cycle fatigue tests are conducted in ambient air, at room temperature, using standard 8-mm diameter specimens. The former tests are carried out under position control with constant displacement rate. The latter are performed under fully-reversed strain-controlled conditions, using the single-step test method, with strain amplitudes lying between ±0.4% and ±2.0%. After the tests, the fracture surfaces are examined by scanning electron microscopy in order to characterize the surface morphologies and identify the main failure mechanisms. Regardless of the strain amplitude, a softening behavior was observed throughout the entire life. Total strain energy density, defined as the sum of both tensile elastic and plastic strain energies, was revealed to be an adequate fatigue damage parameter for short and long lives.

High Ni austenite stainless steel resistant to neutron irradiation degradation

International Nuclear Information System (INIS)

Yonezawa, Toshio; Iwamura, Toshihiko; Kanasaki, Hiroshi; Fujimoto, Koji; Nakata, Shizuo; Ajiki, Kazuhide; Nakamura, Mitsuhiro.

1997-01-01

The composition of the stainless steel of the present invention comprises from 0.005 to 0.08% of C, up to 3% of Mn, up to 0.2% of Si+P+S, from 25 to 40% of Ni, from 25 to 40% of Cr, up to 3% of Mo, up to 0.3% of Nb+Ta, up to 0.3% of Ti, up to 0.001% of B and the balance of Fe. A solid solubilization treatment at a temperature of from 1,000 to 1,150degC is applied to the stainless steel having the composition. The stainless steel is excellent in stress corrosion cracking-resistance at a working circumstance of a LWR type reactor (high temperature and high pressure water at from 270 to 350degC/from 70 to 160 atm even after undergoing neutron irradiation of about 1 x 10 22 n/cm 2 (E>1 MeV) which is a maximum neutron irradiation amount undergone till the final stage of the working life of the LWR-type reactor. In addition, the average thermal expansion coefficient at from room temperature to 400degC ranges from 15x10 -6 - 19x10 -6 /K. (I.N.)

Evaluating Strengthening and Impact Toughness Mechanisms for Ferritic and Bainitic Microstructures in Nb, Nb-Mo and Ti-Mo Microalloyed Steels

Directory of Open Access Journals (Sweden)

Gorka Larzabal

2017-02-01

Full Text Available Low carbon microalloyed steels show interesting commercial possibilities by combining different “micro”-alloying elements when high strength and low temperature toughness properties are required. Depending on the elements chosen for the chemistry design, the mechanisms controlling the strengths and toughness may differ. In this paper, a detailed characterization of the microstructural features of three different microalloyed steels, Nb, Nb-Mo and Ti-Mo, is described using mainly the electron backscattered diffraction technique (EBSD as well as transmission electron microscopy (TEM. The contribution of different strengthening mechanisms to yield strength and impact toughness is evaluated, and its relative weight is computed for different coiling temperatures. Grain refinement is shown to be the most effective mechanism for controlling both mechanical properties. As yield strength increases, the relative contribution of precipitation strengthening increases, and this factor is especially important in the Ti-Mo microalloyed steel where different combinations of interphase and random precipitation are detected depending on the coiling temperature. In addition to average grain size values, microstructural heterogeneity is considered in order to propose a new equation for predicting ductile–brittle transition temperature (DBTT. This equation considers the wide range of microstructures analyzed as well as the increase in the transition temperature related to precipitation strengthening.

Influence of Normalizing Temperature on the Microstructure and Hardness of 9Cr-1Mo ODS Steel

Energy Technology Data Exchange (ETDEWEB)

Jang, Ki Nam; Kim, Tae Kyu [Korea Atomic Energy Research Institute, Daejeon (Korea, Republic of); Kim, Kyu Tae [Dongguk University, Gyeongju (Korea, Republic of)

2016-10-15

Oxide dispersion strengthened(ODS) steel has superior high-temperature strength and creep properties because fine oxide particles having an excellent stability at high temperatures are uniformly distributed in the matrix. ODS steel has being developed for structure materials of sodium fast cooled reactor(SFR) because of its excellent irradiation resistance and mechanical properties. 9Cr-1Mo ODS steel has better high temperature strength and irradiation resistance than common 9Cr-1Mo steel because Y{sub 2}O{sub 3} nano-sized particles which interrupt dislocation movement and grain boundary slip are uniformly dispersed in the martensite matrix. The mechanical properties of the ODS steels are mainly determined by their microstructures, and the microstructure is considerably decided by the heat-treatment conditions. This study focused on the effect of normalizing temperature on microstructure and hardness of 9Cr-1Mo martensitic ODS steel so as to optimize the heat-treatment condition. In this study, the effect of normalizing temperature on mechanical property and microstructures of 9Cr-1Mo martensitic ODS steel was investigated. It was shown that the microhardness was steadily increased with increasing of the normalizing temperature. According to TEM observation, mechanical property of 9Cr-1Mo ODS steel was significantly affected by lath width. These observations, could be useful to understand the relationship between normalizing temperature and microstructure.

The influence of heating rate on reheat-cracking in a commercial 2 1/4Cr1Mo steel

International Nuclear Information System (INIS)

Hippsley, C.A.

1983-03-01

The effects of elevated heating rate on stress-relief cracking in a commercial 2 1/4 Cr1Mo steel have been investigated. A SEN bend-specimen stress-relaxation test was used to assess reheat cracking susceptibility and fracture mechanisms for an initial post-weld heating rate of 1000 Kh - 1 . Two factors controlling the influence of heating rate on the final severity of cracking were identified, i.e. the rate of stress-relaxation with respect to temperature, and the time available for crack-growth. The factors were found to counteract each other, but in the case of commercial 2 1/4 Cr1Mo steel, the crack-growth factor outweighed the relaxation factor, resulting in a reduction in the propensity to stress-relief cracking at the elevated heating rate. However, by reference to the results of a separate investigation concerning A508/2 MnMoNiCr steel it was demonstrated that the balance between these two factors may be reversed in other alloy systems, with the consequence that reheat cracking is exacerbated by increasing the initial heating rate. A computer model was addressed to the stress-relaxation test conditions using data from the commercial 2 1/4 Cr1Mo steel. The model predictions exhibited reasonable agreement with experimental test results for both 100 Kh - 1 and 1000 Kh - 1 heating rates. (author)

Research on 16Mo3 (16M Steel Pipes Overlaid with Haynes Nicro625 Alloy Using MIG (131 Method / Badania Rur Ze Stali 16Mo3 (16M Napawanych Metodą MIG (131 Stopem Haynes Nicro625

Directory of Open Access Journals (Sweden)

Golański G.

2015-12-01

Full Text Available The paper presents the research on the microstructure and mechanical properties of a pipe made of 16Mo3 steel, overlaid with superalloy based on Haynes NiCro625 nickel. The overlay weld was overlaid using the MIG (131 method. The performed macro - and microscopic tests have shown the correct structure of the overlay weld without any welding unconformities. The examined overlay weld was characterized by a dendritic structure of the primary crystals accumulating towards the heat removal. It has been proved that the content of iron in the surface zone does not exceed 7%, and the steel-superalloy joint shows the highest properties in comparison with the materials joined.

Analysis of a multi pass weld of a thick walled tube made of austenitic stainless steel X6 CrNiNb 18 10

International Nuclear Information System (INIS)

Scholtes, B.; Zinn, W.; Ilg, U.; Backfisch, W.; Gibmeier, J.; Kirch, D.

2006-01-01

In this paper, microstructure and residual stresses of a multi pass welding of a thick-walled tube made of austenitic stainless steel X6 CrNiNb 18 10 (1.4550) are systematically characterized and assessed. Results of microstructural and phase analyses, residual stress and hardness measurements as well as of a tensile test using micro specimen and SEM analyses are presented. Using these data, plastic deformations occurring during the welding process in the vicinity of the weld seam are evaluated. Finally, consequences of an additional heat treatment at 400 C/24 h are studied. (Abstract Copyright [2006], Wiley Periodicals, Inc.) [de

The role of Zr and Nb in oxidation/sulfidation behavior of Fe-Cr-Ni alloys

Energy Technology Data Exchange (ETDEWEB)

Natesan, K. (Argonne National Lab., IL (USA)); Baxter, D.J. (Argonne National Lab., IL (USA) INCO Alloy Ltd., Hereford, England (UK))

1990-11-01

05Structural Fe-Cr-Ni alloys may undergo rapid degradation at elevated temperatures unless protective surface oxide scales are formed and maintained. The ability of alloys to resist rapid degradation strongly depends on their Cr content and the chemistry of the exposure environment. Normally, 20 wt % Cr is required for service at temperatures up to 1000{degree}C; the presence of sulfur, however, inhibits formation of a protective surface oxide scale. The oxidation and sulfidation behavior of Fe-Cr-Ni alloys is examined over a wide temperature range (650 to 1000{degree}C), with particular emphasis on the effects of alloy Cr content and the radiation of reactive elements such as Nb and Zr. Both Nb and Zr are shown to promote protective oxidation behavior on the 12 wt % Cr alloy in oxidizing environments and to suppress sulfidation in mixed oxygen/sulfur environments. Additions of Nb and Zr at 3 wt % level resulted in stabilization of Cr{sub 2}O{sub 3} scale and led to a barrier layer of Nb- or Zr-rich oxide at the scale/metal interface, which acted to minimize the transport of base metal cations across the scale. Oxide scales were preformed in sulfur-free environments and subsequently exposed to oxygen/sulfur mixed-gas atmospheres. Preformed scales were found to delay the onset of breakaway corrosion. Corrosions test results obtained under isothermal and thermal cycling conditions are presented. 58 refs., 55 figs., 8 tabs.

HAZ microstructure in joints made of X13CrMoCoVNbNB9-2-1 (PB2 steel welded with and without post-weld heat treatment

Directory of Open Access Journals (Sweden)

M. Łomozik

2016-07-01

Full Text Available The article presents the results of research butt welded joints made of X13CrMoCoVNbNB9-2-1 steel. The joints were welded with post-weld heat treatment PWHT and without PWHT, using the temper bead technique TBT. After welding the joint welded with PWHT underwent stress-relief annealing at 770 °C for 3 hours. The scope of structural tests included the microstructural examination of the coarse-grained heat affected zone (HAZ areas of the joints, the comparison of the morphology of these areas and the determination of carbide precipitate types of the coarse grain heat affected zone (CGHAZ of the joints welded with and without PWHT.

Gradient microstructure and microhardness in a nitrided 18CrNiMo7-6 gear steel

Science.gov (United States)

Yang, R.; Wu, G. L.; Zhang, X.; Fu, W. T.; Huang, X.

2017-07-01

A commercial gear steel (18CrNiMo7-6) containing a tempered martensite structure was nitrided using a pressurized gas nitriding process under a pressure of 5 atm at 530 °C for 5 hours. The mechanical properties and microstructure of the nitrided sample were characterized by Vickers hardness measurements, X-ray diffraction, and backscatter electron imaging in a scanning electron microscope. A micro-hardness gradient was identified over a distance of 500 μm with hardness values of 900 HV at the top surface and 300 HV in the core. This micro-hardness gradient corresponds to a gradient in the microstructure that changes from a nitride compound layer at the top surface (∼ 20 μm thick) to a diffusion zone with a decreasing nitrogen concentration and precipitate density with distance from the surface, finally reaching the core matrix layer with a recovered martensite structure.

Irradiation-induced precipitation in a SUS316 stainless steel using three-dimensional atom probe

International Nuclear Information System (INIS)

Hatakeyama, M.; Yamagata, I.

2013-01-01

Precipitation and segregation were investigated in a compositionally modified 316 austenitic stainless steel, neutron-irradiated at 862 K using a three-dimensional atom probe. In the solution-annealed specimen, Mo, Ti, Nb, C and P enrichment were observed in a silicide, with nominal composition Fe 3 Cr 2 Ni 2 Mo 2 Si 2 . In a Ti-rich carbide, nominaling Fe 5 Cr 8 Ni 10 Mo 2 Ti 11 Si 2 C 6 , enrichment of Mo, Si, O, and Nb was observed. Radiation-induced segregation (RIS) at the precipitate–matrix interface was also investigated at an atomic scale. RIS of Ni and P atoms, which are undersized in Fe, was also analyzed around the interface of the Ti-rich carbide and matrix. Results suggest that the carbide–matrix interface is a sink with an interstitial bias. In the cold-worked specimen, complex-precipitates consisting of silicide and carbide were formed

Microstructure, state of internal stress and corrosion resistance of the short-time laser heat-treated nitrogen high-alloyed tool steel X30CrMoN151; Mikrostruktur, Eigenspannungszustand und Korrosionsbestaendigkeit des kurzzeitlaserwaermebehandelten hochstickstofflegierten Werkzeugstahls X30CrMoN151

Energy Technology Data Exchange (ETDEWEB)

Bohne, C. (ed.)

2000-07-01

This study compares the crystalline structure, state of internal stress and chemical properties of the high-alloyed nitrogen tool steel X30CrMoN15 1 and conventional cold work steel X39CrMo17 1. Transformation points A{sub c}1b and A{sub c}1e were calculated from residual austenite analysis and the c{sub m}/a{sub m} martensite ratios for various heating rates. This was used to generate a TTA (time-temperature-austenitisation) graph for X30CrMoN15 1 for the first time. Transmission electron microscopy and small-angle neutron scattering show that precipitates in nitrogen high-alloyed steel X30CrMoN15 1 can be eliminated completely by short-time laser heat treatment. The corrosion tests show that in contrast to X39CrMo17 1 X30CrMoN15 1 reacts more sensitively to parameter changes during short-time heat treatment in oxidising acid at pH 5-6. [German] Im Rahmen der Arbeit werden die Gefuegeausbildung, Eigenspannungen und chemische Eigenschaften des hochstickstofflegierten Werkzeugstahls X30CrMoN15 1 und des konventionellen Kaltarbeitsstahls X39CrMo17 1 verglichen. Aus den Restaustenitanalysen und den c{sub m}/a{sub m}-Verhaeltnissen des Martensits konnten die Umwandlungspunkte A{sub c1b} und A{sub c1e} fuer verschiedene Aufheizraten bestimmt und daraus ein bisher nicht bekanntes ZTA-Schaubild fuer den X30CrMoN15 1 erstellt werden. Transmissionselektronenmikroskopie und Neutronenkleinwinkelstreuung zeigen, dass sich die Ausscheidungen im hochstickstofflegierten Stahl X30CrMoN14 1 durch die Kurzzeitlaserwaermebehandlung vollstaendig aufloesen koennen. Die Korrosionsversuche zeigen, dass im Gegensatz zum X39CrMo17 1 der X30CrMoN15 1 in oxidierender Saeure bei pH 5-6 empfindlicher auf Parameteraenderungen bei der Kurzzeitwaermebehandlung reagiert. (orig.)

Boron-bearing Influences of 9Cr-0.5Mo-2W-V-Nb Ferritic/Martensitic Steels for a SFR Fuel Cladding

International Nuclear Information System (INIS)

Baek, Jong-Hyuk; Han, Chang-Hee; Kim, Woo-Gon; Kim, Sung-Ho; Lee, Chan-Bock

2008-01-01

modification, the influences of B-bearing 9Cr-0.5Mo-2W-V-Nb ferritic/ martensitic steels on the microstructural and mechanical properties were systematically investigated in order to evaluate the applicable validity as a cladding material for the Gen-IV SFR fuel

Evaluation of microstructure and mechanical properties of 50Cr5NiMoV steel for forged backup roll

Energy Technology Data Exchange (ETDEWEB)

Song, X.Y.; Zhang, X.J.; Fu, L.C.; Yang, H.B.; Yang, K.; Zhu, L., E-mail: zl508@126.com

2016-11-20

The microstructure and mechanical properties of forged 50Cr5NiMoV steel backup roll were evaluated in this study. The microstructure characteristics from surface to center along radial direction of the backup roll were carefully observed by optical microscopy (OM), scanning electron microscopy (SEM) and transmission electron microscopy (TEM), and the chemical composition, hardness, tensile property, impact and fracture toughness in different position of the backup roll were also examined. The results indicate that the finely precipitated carbides at different matrix during heat treatment process strongly influence mechanical properties of the backup roll. Especially, the spheroidized pearlite at the inner regions which consists of large globular or rod-like M{sub 7}C{sub 3} and a little of small globular M{sub 23}C{sub 6} possesses much better toughness and fracture resistance properties than those of the lamellar pearlite with lamellar M{sub 23}C{sub 6} and a little of globular M{sub 7}C{sub 3}.

Development of LP turbine rotor steels resistant to stress corrosion cracking

International Nuclear Information System (INIS)

Nakayama, Takenori; Sugie, Kiyoshi; Fujiwara, Kazuo; Takano, Masayoshi; Kinoshita, Shushi

1988-01-01

The effect of various alloying elements on caustic SCC of 3.5 NiCrMoV steel for turbine rotor forgings was studied. From the results, low P (≤ 0.005 %) steel and low P (≤ 0.005 %) - Nb (0.02/0.03 %) steel has been developed as a rotor material, resistant to SCC. It is confirmed that the developed steel has a higher resistance to SCC and to temper embrittlement, and has equivalent other mechanical properties to those of conventional rotor steel. In addition, the role of P and Nb in SCC was also discussed. (author)

Comparison of low-cycle fatigue data of 2 1/4%CrMo steels

International Nuclear Information System (INIS)

Sanderson, S.J.; Petrequin, P.; Nieuwland, H.C.D.

Data files have been produced on international strain-controlled fatigue information available for 2 1/4%CrMo steels; data assessment from these files is treated in three categories viz: annealed and isothermally annealed 2 1/4%Cr1%Mo steel; normalised and tempered and quenched and tempered 2 1/4%Cr1%Mo steel; and 2 1/4%CrMo variants. The available data have been considered generally in terms of total strain range vs. cycles to failure (Nsub(f)), tensile stress at Nsub(f)/2 vs. cycles to failure and time to failure vs. cycles to failure. Where possible the continuous cycling data have been statistically analysed in terms of the elastic and plastic strain components and cycles to failure to yield best-fit equations over defined temperature (T) regimes viz: T <= 427 deg. C, 427 deg. C < T <= 550 deg. C. and 550 deg. C < T <= 600 deg. C. The behaviour of the steels within the various classifications is discussed. (author)

CoCr double-layered media with NiFe and CoZrNb soft-magnetic layers (invited)

International Nuclear Information System (INIS)

Bernards, J.P.C.; Schrauwen, C.P.G.; Zieren, V.; Luitjens, S.B.

1988-01-01

The magnetic, structural, and recording properties of CoCr double-layered media are investigated. The underlayer materials NiFe (crystalline) and CoZrNb (amorphous) were combined with two different kinds of intermediate layers: Ti (crystalline) and Ge (amorphous). Applying a bias voltage during sputtering of NiFe results in a low coercivity of the NiFe layer and in a high coercivity of the CoCr layer. The structure of the NiFe layer influences the structure of the CoCr layer. A Ti layer between the NiFe and CoCr layers decreases the in-plane remanence of the CoCr layer. The coercivity of all CoZrNb layers is low, independent of the application of a bias voltage. The orientation and structure of CoCr on CoZrNb can be improved by using a Ge intermediate layer, which results in a low coercivity of the CoCr. A Ti intermediate layer increases the coercivity. Ring heads show a dependence of spike noise on the underlayer coercivity and on the applied normal force. A probe-type head shows a dependence of its output on the CoCr coercivity, which may be understood in terms of demagnetization and writing depth

Microstructure evolution and mechanical properties of X12CrMoWVNbN10-1-1 steel during quenching and tempering process

Directory of Open Access Journals (Sweden)

Xingang Tao

2016-01-01

Full Text Available The effect of heat treatments was investigated on the microstructure evolution and mechanical properties of X12CrMoWVNbN10-1-1 steel. The as-received steel was austenitized at 1080 °C for 16 h and cooled in furnace, following tempered in two steps, i.e. at 570 °C for 18 h and then at 690 °C for 24 h. The austenitized sample had a typical lath martensite structure with some retained austenite and no delta ferrite was observed after austenitization. After the first tempering at 570 °C, there was no retained austenite remained but it resulted in the forming of precipitates, such as Cr-rich M7C3, Cr-rich M23C6, Cr-rich M2N, Nb-rich MN, and the subgrain, as well as the reduction in dislocation density. However, microstructure observation after secondary tempering proved the further arrangement of dislocation, subgrain growth and the coarsening of precipitates. Hardness and impact tests were carried out for establishing a correlation between microstructure and mechanical properties. Finally, a careful fractographic analysis of impact samples had been done using SEM and EDS.

Corrosive sliding wear behavior of laser clad Mo2Ni3Si/NiSi intermetallic coating

International Nuclear Information System (INIS)

Lu, X.D.; Wang, H.M.

2005-01-01

Many ternary metal silicides such as W 2 Ni 3 Si, Ti 2 Ni 3 Si and Mo 2 Ni 3 Si with the topologically closed-packed (TCP) hP12 MgZn 2 type Laves phase crystal structure are expected to have outstanding wear and corrosion resistance due to their inherent high hardness and sluggish temperature dependence and strong atomic bonds. In this paper, Mo 2 Ni 3 Si/NiSi intermetallic coating was fabricated on substrate of an austenitic stainless steel AISI321 by laser cladding using Ni-Mo-Si elemental alloy powders. Microstructure of the coating was characterized by optical microscopy (OM), scanning electron microscopy (SEM), X-ray diffraction (XRD) and energy dispersive X-ray analysis (EDS). Wear resistance of the coating is evaluated under corrosive sliding wear test condition. Influence of corrosion solutions on the wear resistance of the coating was studied and the wear mechanism was discussed based on observations of worn surface morphology. Results showed that the laser clad Mo 2 Ni 3 Si/NiSi composite coating have a fine microstructure of Mo 2 Ni 3 Si primary dendrites and the interdendritic Mo 2 Ni 3 Si/NiSi eutectics. The coating has excellent corrosive wear resistance compared with austenitic stainless steel AISI321 under acid, alkaline and saline corrosive environments

Welding repair of the high-intermediate pressure steam casings made of Cr-Mo and Cr-Mo-V steel

International Nuclear Information System (INIS)

Mazur, Z.; Cristalinas, V.; Kubiak, J.

1996-01-01

An analysis of typical failure causes and their location at high-intermediate pressure steam turbine casing, and weldability analysis of the Cr-Mo and Cr-Mo-V steels, is carried out. basing on the steam turbine of 158 MW capacity, the internal high pressure casing failures and development of in situ repair welding technology is described. After repair, the casing was put back into service

The study of tribological and corrosion behavior of plasma nitrided 34CrNiMo6 steel under hot and cold wall conditions

International Nuclear Information System (INIS)

Maniee, A.; Mahboubi, F.; Soleimani, R.

2014-01-01

Highlights: • 34CrNiMo6 steel was plasma nitrided under hot and cold wall conditions. • The amount of ε phase in hot wall condition was more than that of cold wall condition. • Wear resistance of hot wall nitrided samples was more than cold wall treated ones. • Hot wall nitriding provides better corrosion behavior than cold wall nitriding. - Abstract: This paper reports on a comparative study of tribological and corrosion behavior of plasma nitrided 34CrNiMo6 low alloy steel under modern hot wall condition and conventional cold wall condition. Plasma nitriding was carried out at 500 °C and 550 °C with a 25% N 2 + 75% H 2 gas mixture for 8 h. The wall temperature of the chamber in hot wall condition was set to 400 °C. The treated specimens were characterized by using scanning electron microscopy (SEM), X-ray diffraction (XRD), microhardness and surface roughness techniques. The wear test was performed by pin-on-disc method. Potentiodynamic polarization and electrochemical impedance spectroscopy (EIS) tests were also used to evaluate the corrosion resistance of the samples. The results demonstrated that in both nitriding conditions, wear and corrosion resistance of the treated samples decrease with increasing temperature from 500 °C to 550 °C. Moreover, nitriding under hot wall condition at the same temperature provided slightly better tribological and corrosion behavior in comparison with cold wall condition. In consequence, the lowest friction coefficient, and highest wear and corrosion resistance were found on the sample treated under hot wall condition at 500 °C, which had the maximum surface hardness and ε-Fe 2–3 N phase

Effect of normalization heat treatment on creep and tensile properties of modified 9Cr-1Mo steel

International Nuclear Information System (INIS)

Panneer Selvi, S.; Sakthivel, T.; Parameswaran, P.; Laha, K.

2016-01-01

Creep and tensile properties have been investigated on modified 9Cr-1Mo steel subjected to single and double normalization heat treatments. Optical, scanning and transmission electron microscopic investigation revealed the presence of refined prior austenite grain size and fine M 23 C 6 precipitates in the double normalized steel compared to the steel subjected to single normalization heat treatment. Increased creep strain and significant reduction in creep rupture life were observed with the double normalized steel in comparison with single normalized steel. Increased tensile ductility coupled with marginal decrease in tensile strength at higher test temperature was observed with double normalized steel compared to single normalized steel. It has been attributed to the presence of refined prior austenite grain size and coarsening of Nb rich MX precipitates in double normalized steel. (author)

Highly corrosive and high strength Cr-Mn series austenite sintered steel, method of manufacturing the same and the usage

International Nuclear Information System (INIS)

Arai, Masahiko; Hirano, Tatsumi; Aono, Yasuhisa; Kato, Takahiko; Kondo, Yasuo; Inagaki, Masatoshi

1998-01-01

The steel of the present invention comprises a highly corrosive and high strength Cr-Mn series austenite sintered steel containing up to 0.1% of C, up to 1% of Si, up to 0.4% of N, from 9 to 25% of (Mn + Ni) within a range of more than 2% and up to 15% of Mn and from 14 to 20% of Cr, and it has an average crystal grain size of 1μm or less and comprises at least 90 vol% of an austenite phase. In addition, the alloy is incorporated with one or more elements of up to 3% of Mo, 1.0% of Ti, up to 2.0% of Zr and up to 1.0% of Nb in an amount of up to 2.0% in total of Ti, Zr and Nb. When these materials are used under the circumstance where materials are generally deteriorated in grain boundaries, since they are excellent in corrosion resistance and strength, remarkable effects can be attained in the improvement of the safety and the reliability of products. In addition, they are applied not only to a reactor core but also to a water-cooled circumstance and a circumstance where hydrogen exists, thereby capable of exhibiting remarkable effects. (T.M.)

[Studies on the tolerance of the organism to X 5 CrNiMo 18.10 steel (Königsee). II. Light microscopic studies of the surrounding tissue of metal implants (X 5 CrNiMo 18.10 steel) in guinea pigs].

Science.gov (United States)

Höhndorf, H; Drössler, K; Stiehl, P

1977-06-01

The tissue around X 5 CrNiMo 18.10-steel implantates with different surfaces was examined in 72 guinea-pigs. Aside from controls, these animals were preoperatively sensibilized against chromium and nickel. The results can be summarized since the histologic findings showed no different peculiarities. The authors describe an intussusception of the implantate in connective tissue which evidently depends on time and surface. Further the spreading of alien material in the surrounding of the implantate, and morphologic findings are reported. The morphologic evidences are described and discussed in detail, since they are interpreted as signs of cell-mediated immune reactions. The presence of lymphocytes, lymphoblasts, histiocytes (mostly carrying alien material), and granulocytes, as well as proliferations at the arterioles suggest an overlapping of immune reactions.

Effect of Alloy 625 Buffer Layer on Hardfacing of Modified 9Cr-1Mo Steel Using Nickel Base Hardfacing Alloy

Science.gov (United States)

Chakraborty, Gopa; Das, C. R.; Albert, S. K.; Bhaduri, A. K.; Murugesan, S.; Dasgupta, Arup

2016-04-01

Dashpot piston, made up of modified 9Cr-1Mo steel, is a part of diverse safety rod used for safe shutdown of a nuclear reactor. This component was hardfaced using nickel base AWS ER NiCr-B alloy and extensive cracking was experienced during direct deposition of this alloy on dashpot piston. Cracking reduced considerably and the component was successfully hardfaced by application of Inconel 625 as buffer layer prior to hardface deposition. Hence, a separate study was undertaken to investigate the role of buffer layer in reducing the cracking and on the microstructure of the hardfaced deposit. Results indicate that in the direct deposition of hardfacing alloy on modified 9Cr-1Mo steel, both heat-affected zone (HAZ) formed and the deposit layer are hard making the thickness of the hard layer formed equal to combined thickness of both HAZ and deposit. This hard layer is unable to absorb thermal stresses resulting in the cracking of the deposit. By providing a buffer layer of Alloy 625 followed by a post-weld heat treatment, HAZ formed in the modified 9Cr-1Mo steel is effectively tempered, and HAZ formed during the subsequent deposition of the hardfacing alloy over the Alloy 625 buffer layer is almost completely confined to Alloy 625, which does not harden. This reduces the cracking susceptibility of the deposit. Further, unlike in the case of direct deposition on modified 9Cr-1Mo steel, dilution of the deposit by Ni-base buffer layer does not alter the hardness of the deposit and desired hardness on the deposit surface could be achieved even with lower thickness of the deposit. This gives an option for reducing the recommended thickness of the deposit, which can also reduce the risk of cracking.

Phase Composition of a CrMo0.5NbTa0.5TiZr High Entropy Alloy: Comparison of Experimental and Simulated Data

Directory of Open Access Journals (Sweden)

Fan Zhang

2013-09-01

Full Text Available Microstructure and phase composition of a CrMo0.5NbTa0.5TiZr high entropy alloy were studied in the as-solidified and heat treated conditions. In the as-solidified condition, the alloy consisted of two disordered BCC phases and an ordered cubic Laves phase. The BCC1 phase solidified in the form of dendrites enriched with Mo, Ta and Nb, and its volume fraction was 42%. The BCC2 and Laves phases solidified by the eutectic-type reaction, and their volume fractions were 27% and 31%, respectively. The BCC2 phase was enriched with Ti and Zr and the Laves phase was heavily enriched with Cr. After hot isostatic pressing at 1450 °C for 3 h, the BCC1 dendrites coagulated into round-shaped particles and their volume fraction increased to 67%. The volume fractions of the BCC2 and Laves phases decreased to 16% and 17%, respectively. After subsequent annealing at 1000 °C for 100 h, submicron-sized Laves particles precipitated inside the BCC1 phase, and the alloy consisted of 52% BCC1, 16% BCC2 and 32% Laves phases. Solidification and phase equilibrium simulations were conducted for the CrMo0.5NbTa0.5TiZr alloy using a thermodynamic database developed by CompuTherm LLC. Some discrepancies were found between the calculated and experimental results and the reasons for these discrepancies were discussed.

Metallurgical aspects of the weldability of Cr-Mo stabilised ferritic steels

International Nuclear Information System (INIS)

Colombe, Gerard; Petrequin, Pierre; Donati, J.R.; Zacharie, C.

1977-01-01

Results of tests performed to compare the tendency of 2.25 Cr-Mo and 9 Cr-2 Mo steels stabilised with niobium and niobium + vanadium, to different cracking phenomena susceptible to occur during welding, stress-relieving and service in the conditions of fast breeder reactors are presented

Microstructural characterization of second phases in X10CrMoVNb9-1 and 12CrMoWCuVNb steels after long steam exposure time at 550 C

International Nuclear Information System (INIS)

Rodak, Kinga; Hernas, Adam; Vodarek, Vlastimil

2015-01-01

Microstructural changes in high alloy (9-12% Cr) creep resistant martensitic X10CrMoVNb9-1 and 12CrMoW . CuVNb steels after 100 000 h of steam exposure at 550 C have been studied using scanning transmission electron microscopy. Precipitates were identified using electron diffraction patterns and energy dispersive X-ray spectroscopy analysis. After long time exposure, a significant coarsening of M 23 C 6 carbides, and intensive precipitation of the coarse Laves phase were observed. Moreover, in the 12CrMoW . CuVNb steel, a low amount of the modified Z-phase particles was detected. The microstructures of the X10Cr . MoVNb9-1 and 12CrMoWCuVNb steels after 100 000 h of exposure differ in several aspects.

Microstructural characterization of second phases in X10CrMoVNb9-1 and 12CrMoWCuVNb steels after long steam exposure time at 550 C

Energy Technology Data Exchange (ETDEWEB)

Rodak, Kinga; Hernas, Adam [Silesian Univ. of Technology, Inst. of Materials Science, Katowice (Poland); Vodarek, Vlastimil [VSB-Technical Univ. of Ostrava (Czech Republic)

2015-07-15

Microstructural changes in high alloy (9-12% Cr) creep resistant martensitic X10CrMoVNb9-1 and 12CrMoW . CuVNb steels after 100 000 h of steam exposure at 550 C have been studied using scanning transmission electron microscopy. Precipitates were identified using electron diffraction patterns and energy dispersive X-ray spectroscopy analysis. After long time exposure, a significant coarsening of M{sub 23}C{sub 6} carbides, and intensive precipitation of the coarse Laves phase were observed. Moreover, in the 12CrMoW . CuVNb steel, a low amount of the modified Z-phase particles was detected. The microstructures of the X10Cr . MoVNb9-1 and 12CrMoWCuVNb steels after 100 000 h of exposure differ in several aspects.

Corrosion behavior of austenitic steels and their components in niobium-containing chloride melts

Science.gov (United States)

Abramov, A. V.; Polovov, I. B.; Rebrin, O. I.; Volkovich, V. A.; Lisienko, D. G.

2014-02-01

The mechanism of corrosion of austenitic steels 12Kh18N10T, 10Kh17N13M2T, and 03Kh17N14M3 and metals Cr, Fe, Ni, and Mo in a NaCl-KCl-NbCl n ( n = 3.5, Nb content is 5 ± 0.1 wt %) melt at 750°C is studied. The metal and steel corrosion rates under these conditions are determined. The character of material fracture and the mechanisms of material corrosion are found.

Influence of Mo addition on the tempered properties of 13Cr martensitic stainless steel

International Nuclear Information System (INIS)

Jung, Byong Ho; Ahn, Yong Sik

1998-01-01

In order to investigate the effect of Mo addition on the mechanical properties of 13Cr-0.2C martensitic stainless steel, tensile test and Charpy V-notch test were performed after tempering at the temperature range of 200∼700 .deg. C following austenitizing at 1100 .deg. C. The yield strength and hardness of the steel were increased with the increase of Mo content at all tempering conditions, because Mo causes retardation of precipitation and coarsening of carbides and solid solution strengthening of matrix. Except 500 .deg. C of tempering temperature, the Charpy impact energy was significantly increased with Mo content and showed the highest value at 1.5 wt% addition. The increase of impact energy of the steel containing Mo is thought to be caused by δ-ferrite formed in the tempered martensitic matrix. At 500 .deg. C tempering, Charpy impact energy was decreased drastically due to temper embrittlement and it was not possible to prevent it even though Mo was added up to 1.5 wt%

High temperature strength and aging behavior of 12%Cr-15%Mn austenitic steels

International Nuclear Information System (INIS)

Miyahara, Kazuya; Bae, Dong-Su; Sakai, Hidenori; Hosoi, Yuzo

1993-01-01

High Mn-Cr austenitic steels are still considered to be an important high temperature structural material from the point of view of reduced radio-activation. The objective of the present study is to make a fundamental research of mechanical properties and microstructure of 12%Cr-15%Mn austenitic steels. Especially the effects of alloying elements of V and Ti on the mechanical properties and microstructure evolution of high Mn-Cr steels were studied. Precipitation behaviors of carbides, nitrides and σ phase are investigated and their remarkable effects on the high temperature strength are found. The addition of V was very effective for strengthening the materials with the precipitation of fine VN. Ti was also found to be beneficial for the improvement of high temperature strength properties. The results of high temperature strengths of the 12Cr-15Mn austenitic steels were compared with those of the other candidate and/or reference materials, for example, JFMS (modified 9Cr-2Mo ferritic stainless steel) and JPCAs (modified 316 austenitic stainless steels). (author)

Microstructure of Precipitation Hardenable Powder Metallurgical Ni Alloys Containing 35 to 45 pct Cr and 3.5 to 6 pct Nb

DEFF Research Database (Denmark)

Bihlet, Uffe Ditlev; Dahl, Kristian Vinter; Somers, Marcel A. J.

2014-01-01

the additional presence of metastable γ'' (Ni3Nb). A co-dependent growth morphology was found, where the preferred growth direction of γ'', the {001} planes of γ-Ni, caused precipitates of both α-Cr and d to appear in the form of mutually perpendicular oriented disks or plates. Solution heat treatment at 1373 K...

Irradiation-induced precipitation in a SUS316 stainless steel using three-dimensional atom probe

Energy Technology Data Exchange (ETDEWEB)

Hatakeyama, M., E-mail: hatake@imr.tohoku.ac.jp [International Research Center for Nuclear Materials Science, IMR/Tohoku University, Narita, Oarai, Ibaraki 311-1313 (Japan); Yamagata, I. [Japan Atom Energy Agency, Narita, Oarai, Ibaraki 311-1393 (Japan)

2013-11-15

Precipitation and segregation were investigated in a compositionally modified 316 austenitic stainless steel, neutron-irradiated at 862 K using a three-dimensional atom probe. In the solution-annealed specimen, Mo, Ti, Nb, C and P enrichment were observed in a silicide, with nominal composition Fe{sub 3}Cr{sub 2}Ni{sub 2}Mo{sub 2}Si{sub 2}. In a Ti-rich carbide, nominaling Fe{sub 5}Cr{sub 8}Ni{sub 10}Mo{sub 2}Ti{sub 11}Si{sub 2}C{sub 6}, enrichment of Mo, Si, O, and Nb was observed. Radiation-induced segregation (RIS) at the precipitate–matrix interface was also investigated at an atomic scale. RIS of Ni and P atoms, which are undersized in Fe, was also analyzed around the interface of the Ti-rich carbide and matrix. Results suggest that the carbide–matrix interface is a sink with an interstitial bias. In the cold-worked specimen, complex-precipitates consisting of silicide and carbide were formed.

Characterization on the Microstructure Evolution and Toughness of TIG Weld Metal of 25Cr2Ni2MoV Steel after Post Weld Heat Treatment

Directory of Open Access Journals (Sweden)

Xia Liu

2018-03-01

Full Text Available The microstructure and toughness of tungsten inert gas (TIG backing weld parts in low-pressure steam turbine welded rotors contribute significantly to the total toughness of the weld metal. In this study, the microstructure evolution and toughness of TIG weld metal of 25Cr2Ni2MoV steel low-pressure steam turbine welded rotor under different post-weld heat treatment (PWHT conditions are investigated. The fractography and microstructure of weld metal after PWHT are characterized by optical microscope, SEM, and TEM, respectively. The Charpy impact test is carried out to evaluate the toughness of the weld. The optical microscope and SEM results indicate that the as-welded sample is composed of granular bainite, acicular ferrite and blocky martensite/austenite (M-A constituent. After PWHT at 580 °C, the blocky M-A decomposes into ferrite and carbides. Both the number and size of precipitated carbides increase with holding time. The impact test results show that the toughness decreases dramatically after PWHT and further decreases with holding time at 580 °C. The precipitated carbides are identified as M23C6 carbides by TEM, which leads to the dramatic decrease in the toughness of TIG weld metal of 25Cr2Ni2MoV steel.

The rate(time)- dependent mechanical behavior modified 9Cr-1Mo steel, 3

International Nuclear Information System (INIS)

Moosbrugger, J.C.

1991-01-01

In this paper, constitutive equations are presented for the nonisothermal small strain behavior of modified 9Cr-1Mo steel between 25degC - 600degC. The basic framework uses the superposition of nonlinear kinematic hardening rules as proposed by Chaboche and coworkes. A framework for accounting for isotropic softening is presented wherein this softening can be included in a drag stress, in a yield stress or as a decrease in the saturation level of kinematic hardening or some combination of these; a single isotropic softening equation is used as determined from experiments. The behavior of modified 9Cr-1Mo steel between 25degC - 600degC has been investigated by Swindeman, and Majors et. al. and many important features have been discussed. Here, model parameters are determined from available isothermal uniaxial data and some correlations with isothermal and nonisothermal tests are presented. (J.P.N.)

Microstructure and properties of 13Cr5Ni1Mo0.025Nb0.09V0.06N super martensitic stainless steel

International Nuclear Information System (INIS)

Ma, X.P.; Wang, L.J.; Liu, C.M.; Subramanian, S.V.

2012-01-01

Highlights: ► Characterization of the microstructures of a commercial martenistic stainless steel. ► Excess N content causes the occurrence of coarse carbo-nitride and Cr 2 N. ► Correlation of microstructures with mechanical and corrosion properties. ► The poor pitting resistance is due to Cr rich precipitates. - Abstract: The morphological microstructure, the density and dispersion of high angle boundaries, morphology and micro chemical composition of precipitates and the volume fraction of retained austenite of a commercial super martensitic stainless steel (SMSS) normalized and tempered at various temperatures were characterized by optical microscope, scanning electron microscope (SEM), electron backscattered diffraction (EBSD), transmission electron microscope (TEM) and X-ray diffraction (XRD) in the light of equilibrium phase diagram of the alloy calculated using Thermo-Calc software. The mechanical properties and pitting corrosion resistance were determined to correlate with microstructures. Two kinds of morphology of precipitate were observed in tempered commercial super martensitic stainless. Besides the globular Nb and V rich carbo-nitride precipitates, rod-like Cr rich nitrides were formed due to excess N content. While high density of high angle boundaries and precipitates contribute to strength properties, the dislocation softening of the matrix and retained austenite from tempering restore the ductility and impact toughness properties. The poor resistance to pitting corrosion is attributed to the occurrence of Cr rich precipitates. It is demonstrated that by lowering the nitrogen content and adding niobium, the Cr rich precipitates can be suppressed and the mechanical properties and resistance to pitting corrosion can be significantly improved.

Role of Nb in glass formation of Fe–Cr–Mo–C–B–Nb BMGs

Energy Technology Data Exchange (ETDEWEB)

Zhai, Fuqiang, E-mail: fuqiangzhai@gmail.com [Departament Física Aplicada, EETAC, Universitat Politècnica Catalunya-BarcelonaTech, Esteve Terradas 5, 08860 Castelldefels (Spain); Pineda, Eloi [Departament Física i Enginyeria Nuclear, ESAB, Universitat Politècnica Catalunya- BarcelonaTech, Esteve Terradas 8, 08860 Castelldefels (Spain); Duarte, M. Jazmín [Max-Planck-Institut für Eisenforschung GmbH, Max-Planck-Strasse 1, 40237 Düsseldorf (Germany); Crespo, Daniel [Departament Física Aplicada, EETAC, Universitat Politècnica Catalunya-BarcelonaTech, Esteve Terradas 5, 08860 Castelldefels (Spain)

2014-08-01

Highlights: • The Fe{sub 46}Cr{sub 15}Mo{sub 14}C{sub 15}B{sub 6}Nb{sub 4} BMG of 3 mm Ø was produced for the first time. • The compressive strength of Fe–Cr–Mo–C–B–Nb BMG is reported. • The fragility parameter of Fe–Cr–Mo–C–B–Nb BMG was studied. • The microscopic mechanism is explained by E{sub g}, E{sub x}, E{sub p} and m parameters. - Abstract: A new Fe-based bulk metallic glass with superior glass-forming ability (GFA), Fe{sub 46}Cr{sub 15}Mo{sub 14}C{sub 15}B{sub 6}Nb{sub 4}, was developed based on the Fe–Cr–Mo–C–B alloy system by minor addition of Nb. The effects of Nb addition on glass formation of the Fe{sub 50−x}Cr{sub 15}Mo{sub 14}C{sub 15}B{sub 6}Nb{sub x} (x = 0, 2, 4 and 6 at.%) alloys were investigated. The optimum addition content of Nb was determined as 4 at.% by X-ray diffraction and differential scanning calorimeter analysis. A fully amorphous rod sample with 3 mm in diameter was produced by using commercial-grade raw materials and a copper mold casting technique. This alloy shows an ultimate compressive strength of 1920 MPa and Vicker’s hardness 1360 H{sub V}, which is two to three times that of conventional high strength steel and suggests a promising potential for applications combining outstanding corrosion and wear resistance properties. The crystallization kinetics studies found that the activation energies for glass transition, onset of crystallization and crystallization peak were higher than those of other reported Fe-based bulk metallic glasses. The value of the fragility parameter m for the Fe{sub 46}Cr{sub 15}Mo{sub 14}C{sub 15}B{sub 6}Nb{sub 4} alloy was calculated to be 34, indicating that the Fe–Cr–Mo–C–B–Nb alloy system is a strong glass former according to the Angell’s classification scheme. It is inferred that the more sequential change in the atomic size, the generation of new atomic pairs with large negative heats of mixing and the amount of oxygen in the molten liquid

Density of liquid NiCrAlMo quarternary alloys measured by a modified sessile drop method

International Nuclear Information System (INIS)

Fang, L.; Wang, Y.F.; Xiao, F.; Tao, Z.N.; MuKai, K.

2006-01-01

The densities of liquid NiCrAlMo quaternary alloys with a fixed molar ratio of Ni:Cr:Al (approximately as 73:14:13) and molybdenum concentration from 0 to 10 mass% were measured by a modified sessile drop method (MSDM). It was found that the density of the liquid NiCrAlMo quaternary alloys decreases with increasing temperature, but increases with the increase of molybdenum concentration. The molar volume of liquid NiCrAlMo quaternary alloys increases with the increase of temperature and molybdenum concentration. The density of liquid NiCrAlMo quaternary alloys calculated from the partial molar volumes of nickel, chromium, aluminum and molybdenum in the corresponding Ni-based binary alloys are in good agreement with the experimental results, means, within the error tolerance range the density of liquid Ni-based multi-component alloys can be predicted from the partial volumes of elements in Ni-based binary alloys in liquid state

Erosion-oxidation behavior of thermal sprayed Ni20Cr alloy and WC and Cr3C2 cermet coatings

Directory of Open Access Journals (Sweden)

Clarice Terui Kunioshi

2005-06-01

Full Text Available An apparatus to conduct high temperature erosion-oxidation studies up to 850 °C and with particle impact velocities up to 15 m.s-1 was designed and constructed in the Corrosion Laboratories of IPEN. The erosion-oxidation behavior of high velocity oxy fuel (HVOF sprayed alloy and cermet coatings of Ni20Cr, WC 20Cr7Ni and Cr3C2 Ni20Cr on a steel substrate has been studied. Details of this apparatus and the erosion-oxidation behavior of these coatings are presented and discussed. The erosion-oxidation behavior of HVOF coated Cr3C2 25(Ni20Cr was better than that of WC 20Cr7Ni, and the erosion-oxidation regimes have been identified for these coatings at particle impact velocity of 3.5 m.s-1, impact angle of 90° and temperatures in the range 500 to 850 °C.

Effect of shot peening on the residual stress and mechanical behaviour of low-temperature and high-temperature annealed martensitic gear steel 18CrNiMo7-6

DEFF Research Database (Denmark)

Yang, R.; Zhang, X.; Mallipeddi, D.

2017-01-01

A martensitic gear steel (18CrNiMo7-6) was annealed at 180 degrees C for 2h and at similar to 750 degrees C for 1h to design two different starting microstructures for shot peening. One maintains the original as-transformed martensite while the other contains irregular-shaped sorbite together...... with ferrite. These two materials were shot peened using two different peening conditions. The softer sorbite + ferrite microstructure was shot peened using 0.6 mm conditioned cut steel shots at an average speed of 25 m/s in a conventional shot peening machine, while the harder tempered martensite steel...

Measurement of high temperature elastic moduli of an 18Cr-9Ni-2.95 Cu-0.58 Nb-0.1C (Wt %) austenitic stainless steel

Science.gov (United States)

Tripathy, Haraprasanna; Hajra, Raj Narayan; Sudha, C.; Raju, S.; Saibaba, Saroja

2018-04-01

The Young's modulus (E) and Shear modulus (G) of an indigenously developed 18Cr-9Ni-0.1C-2.95 Cu-0.58Nb (wt %) austenitic stainless steel has been evaluated in the temperature range 298 K to 1273 K (25 °C to 1000 °C), using Impulse excitation technique (IET). The Bulk modulus (K) and the poison's ratio have been estimated from the measured values of E and G. It is observed that the elastic constants (E, G and K) are found to decrease in a nonlinear fashion with increase in temperature. The Cu precipitation is found to influence the elastic moduli of the steel in the cooling cycle. The observed elastic moduli are fitted to 3rd order polynomial equations in order to describe the temperature dependence of E, G, K moduli in the temperature range 298-1273 K (25 °C to 1000 °C). The room temperature values of E,G and K moduli is found to be 207, 82 and 145 GPa respectively for the present steel.

Behaviour and microstructure of stainless steels irradiated in the french fast breeder reactors

International Nuclear Information System (INIS)

Dubuisson, P.; Gilbon, D.

1991-01-01

The burn-up of Fast Breeder Reactors is limited by the irradiation induced dimensional changes and mechanical properties of structural materials used for replaceable in-core components. This paper describes the behaviour improvements and also the radiation-induced microstructures of the different steels used for fuel pin cladding and wrapper tubes in French reactors. Materials of fuel pin cladding are austenitic steels whose main problem is swelling. Improvements in swelling resistance by cold-working, titanium additions and modifications of matrix (Fe-Cr-Ni) from SA 316 to CW 15-15 Ti are shown. These improvements are correlated with a best stability of microstructure under irradiation. Beneficial effects of phosphorus addition and multistabilisation (NbVTi) on radiation induced microstructure and swelling resistance are also shown. Austenitic steels used for wrapper tubes are limited both by swelling and by void embrittlement. The ferritic F17 (17Cr), ferritic-martensitic EM12 (9Cr-2MoNbV) and martensitic EM10 (9Cr-1Mo) steels present high swelling resistance. Nevertheless radiation-induced embrittlement is observed in EM12 and especially in F17. This embrittlement results from a fine and uniform radiation enhanced precipitation in ferrite grains. By contrast, the microstructure of fully martensitic EM10 steel is mush more stable and its ductile-brizzle transition temperature stays below 0 0 C. 12 figs

XHM-1 alloy as a promising structural material for water-cooled fusion reactor components

International Nuclear Information System (INIS)

Solonin, M.I.; Alekseev, A.B.; Kazennov, Yu.I.; Khramtsov, V.F.; Kondrat'ev, V.P.; Krasina, T.A.; Rechitsky, V.N.; Stepankov, V.N.; Votinov, S.N.

1996-01-01

Experience gained in utilizing austenitic stainless steel components in water-cooled power reactors indicates that the main cause of their failure is the steel's propensity for corrosion cracking. In search of a material immune to this type of corrosion, different types of austenitic steels and chromium-nickel alloys were investigated and tested at VNIINM. This paper presents the results of studying physical and mechanical properties, irradiation and corrosion resistance in a water coolant at <350 C of the alloy XHM-1 as compared with austenitic stainless steels 00Cr16Ni15Mo3Nb, 00Cr20Ni25Nb and alloy 00Cr20Ni40Mo5Nb. Analysis of the results shows that, as distinct from the stainless steels studied, the XHM-1 alloy is completely immune to corrosion cracking (CC). Not a single induced damage was encountered within 50 to 350 C in water containing different amounts of chlorides and oxygen under tensile stresses up to the yield strength of the material. One more distinctive feature of the alloy compared to steels is that no change in the strength or total elongation is encountered in the alloy specimens irradiated to 32 dpa at 350 C. The XHM-1 alloy has adequate fabricability and high weldability characteristics. As far as its properties are concerned, the XHM-1 alloy is very promising as a material for water-cooled fusion reactor components. (orig.)

Effect of laser absorption on picosecond laser ablation of Cr12MoV mold steel, 9Cr18 stainless steel and H13A cemented carbide

Science.gov (United States)

Wu, Baoye; Liu, Peng; Wang, Xizhao; Zhang, Fei; Deng, Leimin; Duan, Jun; Zeng, Xiaoyan

2018-05-01

Due to excellent properties, Cr12MoV mold steel, 9Cr18 stainless steel and H13A cemented carbide are widely used in industry. In this paper, the effect of absorption of laser light on ablation efficiency and roughness have been studied using a picosecond pulse Nd:YVO4 laser. The experimental results reveal that laser wavelength, original surface roughness and chemical composition play an important role in controlling ablation efficiency and roughness. Firstly, higher ablation efficiency with lower surface roughness is achieved on the ablation of 9Cr18 at 532, comparing with 1064 nm. Secondly, the ablation efficiency increases while the Ra of the ablated region decreases with the decrease of original surface roughness on ablation of Cr12MoV mold steel at 532 nm. Thirdly, the ablation efficiency of H13A cemented carbide is much higher than 9Cr18 stainless steel and Cr12MoV mold steel at 1064 nm. Scanning electron microscopy images reveals the formation of pores on the surface of 9Cr18 stainless steel and Cr12MoV mold steel at 532 nm while no pores are formed at 1064 nm. As to H13A cemented carbide, worm-like structure is formed at 1064 nm. The synergetic effects of the heat accumulation, plasma shielding and ablation threshold on laser ablation efficiency and machining quality were analyzed and discussed systematically in this paper.

Effect of nitrogen alloying of stainless steels on their corrosion stability

International Nuclear Information System (INIS)

Chigal, V.; Knyazheva, V.M.; Pitter, Ya.; Babich, S.G.; Bogolyubskij, S.D.

1986-01-01

Results of corrosion tests and structural investigations of 03Cr18Ni10 and 03Cr18Ni10Mo3 steels without nitrogen and with nitrogen content of 0.15-0.3% are presented. Corrosion-electrochemical behaviour of Cr20Ni20 steel with ultralow carbon content (0.004-0.006%) and nitrogen content with 0-0.5% as well as Cr 2 N nitride behaviour are investigated. A conclusion is made on nitrogen and excessive nitride phase effect on corrosion stability of steel in corrosive media with different reduction-oxidation properties

Characteristics of Modified 9Cr-1Mo Steel for Reactor Pressure Vessel of Very High Temperature Gas Cooled Reactor

Energy Technology Data Exchange (ETDEWEB)

Kim, Sung Ho; Ryu, W. S.; Han, Chang Hee; Yoon, J. H.; Chang, Jong Hwa

2004-11-15

Many researches and developments have been progressed for the construction of VHTR by 2020 in Korea. Modified 9Cr-1Mo steel has been receiving attention for the application to the reactor pressure vessel material of VHTR. We collected and analyzed the research data for modified 9Cr-1Mo steel in order to understand the characteristics of modified 9Cr-1Mo steel. The modified 9Cr-1Mo steel is a modified alloy system similar to conventional 9Cr-1Mo grade ferritic steel. Modifications include additions of vanadium, niobium, and nitrogen, as well as lower carbon content. In this report, we summarized the change of microstructure and mechanical properties after tempering, thermal aging, and irradiation. Modified 9Cr-1Mo steel has high strength and thermal conductivity, low thermal expansion, and good resistance to corrosion. But the irradiation embrittlement behavior of modified 9Cr-1Mo steel should be evaluated and the evaluation methodology also should be developed. At the same time, the characteristics of weldment which is the weak part in pressure vessel should be evaluated.

High-Temperature Oxidation Behavior and Kinetics of Forged 12Cr-MoVW Steel

Directory of Open Access Journals (Sweden)

Kim Yong Hwan

2017-06-01

Full Text Available The oxidation kinetics of forged 12Cr-MoVW steel was investigated in an air (N2+O2 atmosphere at 873-1073 K (Δ50 K using thermogravimetric analysis. The oxidized samples were characterized using X-ray diffraction, and the surface and cross-sectional morphologies were examined using scanning electron microscopy coupled with energy-dispersive X-ray spectroscopy. The forged 12Cr-MoVW steel samples exhibited parabolic behavior and a low oxidation rate compared with their as-cast counterparts. A protective oxide layer was uniformly formed at relatively low temperature (≤973 K for the forged samples, which thus exhibited better oxidation resistance than the as-cast ones. These oxides are considered solid-solution compounds such as (Fe, Cr2O3.

A New Method to Produce Ni-Cr Ferroalloy Used for Stainless Steel Production

Science.gov (United States)

Chen, Pei-Xian; Chu, Shao-Jun; Zhang, Guo-Hua

2016-08-01

A new electrosilicothermic method has been proposed in the present paper to produce Ni-Cr ferroalloy, which can be used for the production of 300 series stainless steel. Based on this new process, the Ni-Si ferroalloy is first produced as the intermediate alloy, and then the desiliconization process of Ni-Si ferroalloy melt with chromium concentrate is carried out to generate Ni-Cr ferroalloy. The silicon content in the Ni-Si ferroalloy produced in the submerged arc furnace should be more than 15 mass% (for the propose of reducing dephosphorization), in order to make sure the phosphorus content in the subsequently produced Ni-Cr ferroalloy is less than 0.03 mass%. A high utilization ratio of Si and a high recovery ratio of Cr can be obtained after the desiliconization reaction between Ni-Si ferroalloy and chromium concentrate in the electric arc furnace (EAF)-shaking ladle (SL) process.

Multiaxial creep of fine grained 0.5Cr-0.5Mo-0.25V and coarse grained 1Cr-0.5Mo steels

International Nuclear Information System (INIS)

Browne, R.J.; Flewitt, P.E.J.; Lonsdale, D.

1991-01-01

To explore the multiaxial creep response of materials used for electrical power generating plant, two steels, a fine grained 0.5Cr-0.5Mo-0.25V steel in a normalised and tempered condition with high creep ductility and a coarse grained 1Cr-0.5Mo steel in a quenched and tempered condition with low uniaxial creep ductility, have been selected. A range of multiaxial stress testing techniques which span the stress states that would allow identification of any technique dependent variables has been used. The deformation and failure of the normalised and tempered 0.5Cr-0.5Mo-0.25V steel for a range of multiaxial test techniques and, therefore, stress states may be described by an equivalent stress criterion. The results from the multiaxial tests carried out on the fully bainitic 1Cr-0.5Mo steel show that the multiaxial stress rupture criterion (MSRC) varies with stress state; at high triaxiality (notch), it is controlled by the maximum principal stress, whereas at low triaxiality (shear) it is dependent on both maximum principal stress and equivalent stress. Furthermore, a simple description of stress state based on maximum principal and equivalent stress does not define this uniquely, since the MSRC derived from uniaxial and torsion testing does not describe the failure of notch, tube, or double shear tests. (author)

Application of NiMoNb adhesion layer on plasma-treated polyimide substrate for flexible electronic devices

Energy Technology Data Exchange (ETDEWEB)

Bang, S.-H.; Kim, K.-K.; Jung, H.-Y.; Kim, T.-H.; Jeon, S.-H. [Metal and Material Technology Group, R and D Center, LS Mtron Ltd., Gyeonggi 431-080 (Korea, Republic of); Seol, Jae-Bok, E-mail: zptkfm20@hanmail.net [Max-Planck-Insititut für Eisenforschung, Max-Planck-Str. 1, D-40237 Düsseldorf (Germany)

2014-05-02

A thin film, NiMoNb, was introduced as an adhesion layer between the Cu metal and the insulator polyimide substrate in a flexible Cu-clad laminated structure. Using 90° peel test, we evaluated the peel strength of the system as a function of the thickness of the adhesion layer. An increase in the NiMoNb thickness from 7 to 40 nm enhanced the peel strength of the deposited systems. After plasma treatment by the roll-to-roll method, the multilayer structure showed an outstanding peel strength of ∼ 529 N/m, even after thermal annealing at 150 °C for 168 h. We also studied the role of plasma treatment of the polyimide substrate on the adhesion strength and microstructure of a flexible Cu-clad laminated structure by peel strength, atomic force microscopy, X-ray photoelectron spectroscopy, and transmission electron microscopy. These experimental observations showed that the plasma-treated polyimide substrate with the deposition of NiMoNb showed the enhanced adhesion of ∼ 656 N/m, because of the change of functional groups, which affected the bonding force and crystallinity of the thin films deposited on polyimide, rather than an increase in the surface roughness. - Highlights: • NiMoNb film on polyimide substrate was employed for higher peel strength. • Plasma-treated substrate enhances the peel strength of multilayer. • Even when annealed at 150 °C, plasma-treated films showed enhanced peel strength.

Application of NiMoNb adhesion layer on plasma-treated polyimide substrate for flexible electronic devices

International Nuclear Information System (INIS)

Bang, S.-H.; Kim, K.-K.; Jung, H.-Y.; Kim, T.-H.; Jeon, S.-H.; Seol, Jae-Bok

2014-01-01

A thin film, NiMoNb, was introduced as an adhesion layer between the Cu metal and the insulator polyimide substrate in a flexible Cu-clad laminated structure. Using 90° peel test, we evaluated the peel strength of the system as a function of the thickness of the adhesion layer. An increase in the NiMoNb thickness from 7 to 40 nm enhanced the peel strength of the deposited systems. After plasma treatment by the roll-to-roll method, the multilayer structure showed an outstanding peel strength of ∼ 529 N/m, even after thermal annealing at 150 °C for 168 h. We also studied the role of plasma treatment of the polyimide substrate on the adhesion strength and microstructure of a flexible Cu-clad laminated structure by peel strength, atomic force microscopy, X-ray photoelectron spectroscopy, and transmission electron microscopy. These experimental observations showed that the plasma-treated polyimide substrate with the deposition of NiMoNb showed the enhanced adhesion of ∼ 656 N/m, because of the change of functional groups, which affected the bonding force and crystallinity of the thin films deposited on polyimide, rather than an increase in the surface roughness. - Highlights: • NiMoNb film on polyimide substrate was employed for higher peel strength. • Plasma-treated substrate enhances the peel strength of multilayer. • Even when annealed at 150 °C, plasma-treated films showed enhanced peel strength

Microstructure and properties of 13Cr5Ni1Mo0.025Nb0.09V0.06N super martensitic stainless steel

Energy Technology Data Exchange (ETDEWEB)

Ma, X.P.; Wang, L.J. [Key Laboratory for Anisotropy and Texture of Materials, Northeastern University, Shenyang 110819 (China); Liu, C.M., E-mail: cmliu@mail.neu.edu.cn [Key Laboratory for Anisotropy and Texture of Materials, Northeastern University, Shenyang 110819 (China); Subramanian, S.V. [Department of Materials Science and Engineering, McMaster University, Hamilton, L8S-4L7 (Canada)

2012-03-30

Highlights: Black-Right-Pointing-Pointer Characterization of the microstructures of a commercial martenistic stainless steel. Black-Right-Pointing-Pointer Excess N content causes the occurrence of coarse carbo-nitride and Cr{sub 2}N. Black-Right-Pointing-Pointer Correlation of microstructures with mechanical and corrosion properties. Black-Right-Pointing-Pointer The poor pitting resistance is due to Cr rich precipitates. - Abstract: The morphological microstructure, the density and dispersion of high angle boundaries, morphology and micro chemical composition of precipitates and the volume fraction of retained austenite of a commercial super martensitic stainless steel (SMSS) normalized and tempered at various temperatures were characterized by optical microscope, scanning electron microscope (SEM), electron backscattered diffraction (EBSD), transmission electron microscope (TEM) and X-ray diffraction (XRD) in the light of equilibrium phase diagram of the alloy calculated using Thermo-Calc software. The mechanical properties and pitting corrosion resistance were determined to correlate with microstructures. Two kinds of morphology of precipitate were observed in tempered commercial super martensitic stainless. Besides the globular Nb and V rich carbo-nitride precipitates, rod-like Cr rich nitrides were formed due to excess N content. While high density of high angle boundaries and precipitates contribute to strength properties, the dislocation softening of the matrix and retained austenite from tempering restore the ductility and impact toughness properties. The poor resistance to pitting corrosion is attributed to the occurrence of Cr rich precipitates. It is demonstrated that by lowering the nitrogen content and adding niobium, the Cr rich precipitates can be suppressed and the mechanical properties and resistance to pitting corrosion can be significantly improved.

Effect of quenching temperature on martensite multi-level microstructures and properties of strength and toughness in 20CrNi2Mo steel

Energy Technology Data Exchange (ETDEWEB)

Long, Shao-lei [College of Materials Science and Metallurgical Engineering, Guizhou University (China); Guizhou Key Laboratory for Mechanical Behavior and Microstructure of Materials (China); National & Local Joint Engineering Laboratory for High-performance Metal Structure Material and Advanced Manufacturing Technology (China); Liang, Yi-long, E-mail: liangyilong@126.com [College of Materials Science and Metallurgical Engineering, Guizhou University (China); Guizhou Key Laboratory for Mechanical Behavior and Microstructure of Materials (China); National & Local Joint Engineering Laboratory for High-performance Metal Structure Material and Advanced Manufacturing Technology (China); Jiang, Yun [Guizhou Key Laboratory for Mechanical Behavior and Microstructure of Materials (China); National & Local Joint Engineering Laboratory for High-performance Metal Structure Material and Advanced Manufacturing Technology (China); Liang, Yu; Yang, Ming; Yi, Yan-liang [College of Materials Science and Metallurgical Engineering, Guizhou University (China); Guizhou Key Laboratory for Mechanical Behavior and Microstructure of Materials (China); National & Local Joint Engineering Laboratory for High-performance Metal Structure Material and Advanced Manufacturing Technology (China)

2016-10-31

The martensite multi-level microstructures of 20CrNi2Mo steel, which were quenched at the different temperatures of 900–1200 °C and tempered at 200 °C, were investigated by optical microscope (OM), scanning electron microscopy (SEM), electron backscattering diffraction (EBSD) and transmission electron microscopy (TEM), and the relationship between the microstructures and properties of strength and toughness was discussed by the classic formula of Hall–Petch. The results show that the size of prior austenite grain (d{sub r}), martensite packet (d{sub p}) and block (d{sub b}) increase with increasing of the quenching temperature, while the martensite lath (d{sub l}) size is opposite. On another hand, the confusion degree of the martensite packets changes from disorder to order. The boundaries of prior austenite grain, packet, block and the martensite lath are high angle boundaries (HBs) and low angle boundaries (LBs), respectively, and the ratio of the low angle boundaries increase with the quenching temperature by calculating to the multi-level microstructure size with the mathematical model established by myself. In addition, the relationship between the packet/block and strength follows the classical formula of Hall–Petch, and the size of d{sub b} is far lower than the size of d{sub p}, d{sub b} is the effective control unit of the strength. Meanwhile, d{sub l} is the effective control unit of toughness because it strongly impacts the crack initiation and propagation and follows also the Hall-Petch with toughness in 20CrNi2Mo steel.

Structure change in 25 Cr - 20 Ni steels as a function of their Cr, Ni, Si and W content

International Nuclear Information System (INIS)

Gribaudo, L.M.; Durand, F.; Durand-Charre, M.

1983-01-01

The influence of varying the Cr, Ni, Si and W concentrations on the type and composition of the carbides of solidification and on the phase shift temperature is studied with 18 alloys of composition close to stainless steel-25-20 (AISI 310) composition. Experimental techniques used are differential thermal analysis, microprobe and scanning electron microscope. Crystallization is interpreted with the equilibrium diagram Ni-Cr-C. The formation of the interdendritic σ phase for a chromium rich alloys is interpreted with the phase equilibrium diagram of Fe-Ni-Cr-C. Mechanical properties and corrosion resistance are dependent on the morphology of the carbides M 7 C 3 and M 23 C 6 [fr

Creep-fatigue life prediction method using Diercks equation for Cr-Mo steel

International Nuclear Information System (INIS)

Sonoya, Keiji; Nonaka, Isamu; Kitagawa, Masaki

1990-01-01

For dealing with the situation that creep-fatigue life properties of materials do not exist, a development of the simple method to predict creep-fatigue life properties is necessary. A method to predict the creep-fatigue life properties of Cr-Mo steels is proposed on the basis of D. Diercks equation which correlates the creep-fatigue lifes of SUS 304 steels under various temperatures, strain ranges, strain rates and hold times. The accuracy of the proposed method was compared with that of the existing methods. The following results were obtained. (1) Fatigue strength and creep rupture strength of Cr-Mo steel are different from those of SUS 304 steel. Therefore in order to apply Diercks equation to creep-fatigue prediction for Cr-Mo steel, the difference of fatigue strength was found to be corrected by fatigue life ratio of both steels and the difference of creep rupture strength was found to be corrected by the equivalent temperature corresponding to equal strength of both steels. (2) Creep-fatigue life can be predicted by the modified Diercks equation within a factor of 2 which is nearly as precise as the accuracy of strain range partitioning method. Required test and analysis procedure of this method are not so complicated as strain range partitioning method. (author)

Crystal structure and ion conducting properties of La5NbMo2O16

KAUST Repository

Vu, T.D.; Krichen, F.; Barre, M.; Busselez, R.; Adil, Karim; Jouanneaux, A.; Suard, E.; Goutenoire, F.

2016-01-01

.2250(1) Å. La5NbMo2O16 is a new analogue of the R5Mo3O16 series (R=Pr, Nd). The structure was refined from a combined data X-ray and neutron powder diffraction. The ionic conductivity of the compound is then measured on sintered pellets, by means of complex

Polymorphism in the Laves-phase precipitates of a quinternary Nb-Mo-Cr-Al-Si alloy

International Nuclear Information System (INIS)

Hu Yanling; Vasiliev, Alexandre; Zhang Lichun; Song, Kai; Aindow, Mark

2009-01-01

Transmission electron microscopy has been used to study the precipitates that develop in the A2 phase of an Nb-Mo-Cr-Al-Si alloy upon heat treatment. The precipitates include a Laves-phase that adopts the cubic C15 structure initially and the hexagonal C14 structure in the later stages of precipitation. The morphologies, orientation relationships and defect microstructures indicate that the metastable C15 phase arises due to tensile coherency stresses and that a synchroshear polymorphic transformation to the equilibrium C14 phase occurs as these relax

Corrosion behavior of steels in liquid lead bismuth with low oxygen concentrations

Science.gov (United States)

Kurata, Yuji; Futakawa, Masatoshi; Saito, Shigeru

2008-02-01

Corrosion tests in pots were conducted to elucidate corrosion behavior of various steels in liquid lead-bismuth for 3000 h under the condition of an oxygen concentration of 5 × 10 -8 wt% at 450 °C and an oxygen concentration of 3 × 10 -9 wt% at 550 °C, respectively. Significant corrosion was not observed at 450 °C for ferritic/martensitic steels, F82H, Mod.9Cr-1Mo steel, 410SS, 430SS except 2.25Cr-1Mo steel. Pb-Bi penetration into steels and dissolution of elements into Pb-Bi were severe at 550 °C even for ferritic/martensitic steels. Typical dissolution attack occurred for pure iron both at 550 °C without surface Fe 3O 4 and at 450 °C with a thin Fe 3O 4 film. Ferritization due to dissolution of Ni and Cr, and Pb-Bi penetration were recognized for austenitic stainless steels, 316SS and 14Cr-16Ni-2Mo steel at both temperatures of 450 °C and 550 °C. The phenomena were mitigated for 18Cr-20Ni-5Si steel. In some cases oxide films could not be a corrosion barrier in liquid lead-bismuth.

Development of ferritic steels for fusion reactor applications

Energy Technology Data Exchange (ETDEWEB)

Klueh, R.L.; Maziasz, P.J.; Corwin, W.R.

1988-08-01

Chromium-molybdenum ferritic (martensitic) steels are leading candidates for the structural components for future fusion reactors. However, irradiation of such steels in a fusion environment will produce long-lived radioactive isotopes that will lead to difficult waste-disposal problems. Such problems could be reduced by replacing the elements in the steels (i.e., Mo, Nb, Ni, N, and Cu) that lead to long-lived radioactive isotopes. We have proposed the development of ferritic steels analogous to conventional Cr-Mo steels, which contain molybdenum and niobium. It is proposed that molybdenum be replaced by tungsten and niobium be replaced by tantalum. Eight experimental steels were produced. Chromium concentrations of 2.25, 5, 9, and 12% were used (all concentrations are in wt %). Steels with these chromium compositions, each containing 2% W and 0.25% V, were produced. To determine the effect of tungsten and vanadium, 2.25 Cr steels were produced with 2% W and no vanadium and with 0.25% V and O and 1% W. A 9Cr steel containing 2% W, 0.25 V, and 0.07% Ta was also studied. For all alloys, carbon was maintained at 0.1%. Tempering studies on the normalized steels indicated that the tempering behavior of the new Cr-W steels was similar to that of the analogous Cr-Mo steels. Microscopy studies indicated that 2% tungsten was required in the 2.25 Cr steels to produce 100% bainite in 15.9-mm-thick plate during normalization. The 5Cr and 9Cr steels were 100% martensite, but the 12 Cr steel contained about 75% martensite with the balance delta-ferrite. 33 refs., 35 figs., 5 tabs.

Development of ferritic steels for fusion reactor applications

International Nuclear Information System (INIS)

Klueh, R.L.; Maziasz, P.J.; Corwin, W.R.

1988-08-01

Chromium-molybdenum ferritic (martensitic) steels are leading candidates for the structural components for future fusion reactors. However, irradiation of such steels in a fusion environment will produce long-lived radioactive isotopes that will lead to difficult waste-disposal problems. Such problems could be reduced by replacing the elements in the steels (i.e., Mo, Nb, Ni, N, and Cu) that lead to long-lived radioactive isotopes. We have proposed the development of ferritic steels analogous to conventional Cr-Mo steels, which contain molybdenum and niobium. It is proposed that molybdenum be replaced by tungsten and niobium be replaced by tantalum. Eight experimental steels were produced. Chromium concentrations of 2.25, 5, 9, and 12% were used (all concentrations are in wt %). Steels with these chromium compositions, each containing 2% W and 0.25% V, were produced. To determine the effect of tungsten and vanadium, 2.25 Cr steels were produced with 2% W and no vanadium and with 0.25% V and O and 1% W. A 9Cr steel containing 2% W, 0.25 V, and 0.07% Ta was also studied. For all alloys, carbon was maintained at 0.1%. Tempering studies on the normalized steels indicated that the tempering behavior of the new Cr-W steels was similar to that of the analogous Cr-Mo steels. Microscopy studies indicated that 2% tungsten was required in the 2.25 Cr steels to produce 100% bainite in 15.9-mm-thick plate during normalization. The 5Cr and 9Cr steels were 100% martensite, but the 12 Cr steel contained about 75% martensite with the balance delta-ferrite. 33 refs., 35 figs., 5 tabs

Developing of complex for hot plastic deformation modeling of steel type 20-30CrNiMoV for heavy forging

Directory of Open Access Journals (Sweden)

Dub Vladimir

2017-01-01

Full Text Available Production of heavy forging of bars weighing more then 235 tons for such products as rotors made of steel type 20-30CrNiMoV is a critical independent work, failure to perform which entails high costs related to repeated production (in case of defective product and untimely launch of production plants. One of the frequent causes of a defective product is the impossibility of ultrasonic testing in the barrel-gate zones on the rotor workpiece, which is due to the microstructure of the metal, namely the grain size. Determing the stages of deformation process wich causes such defects in structure is the main goal of this work.

Effect of cloric acid concentration on corrosion behavior of Ni/Cr coated on carbon steel

Science.gov (United States)

Desiati, Resetiana Dwi; Sugiarti, Eni; Thosin, K. A. Zaini

2018-05-01

Corrosion is one of the causes of metal degradation. Carbon steel (Fe) is easy to corrode in the extreme environment. Coating on carbon steel is required to improve corrosion resistance owing to protection or hindrance to extreme environmental conditions. In this present work, carbon steel was coated by electroplating techniques for nickel and pack cementation for chrome. The corrosion rate test was performed by Weight Loss method on FeNiCr, FeNi, FeCr and uncoated Fe as comparator which was dyed in 37% HCl and 25% HCl which had previously been measured dimension and mass. The immersion test result of FeNiCr and FeNi specimen were better than FeCr and uncoated Fe in terms of increasing corrosion resistance. The corrosion rate for 56 hours in 37% HCl for FeNiCr was 1.592 mm/y and FeNi was 3.208 mm/y, FeCr only lasted within 32 hours with corrosion rate was 6.494 mm/y. Surface of the sample after the corrosion test there was pitting, crevice corrosion and alloy cracking caused by chloride. The higher the concentration of HCl the faster the corrosion rate.

The causes of relaxation- and hot cracking in the heat-affected zone of 22 NiMoCr 37 and 20 MnMoNi 55

International Nuclear Information System (INIS)

Schellhammer, W.

1977-01-01

Non-destructive and metallographic investigations with a view to relaxation cracking and hot cracking were carried out in 53 component-specific welds with wall thicknesses of 40 to 360 mm and 21 experimental welds with wall thicknesses of 140 to 275 mm of high-temperature, fine-grained structural steel 22 NiMoCr 37 as well as in 27 component-specific welds of high-strength, fine-grained structural steel 20 MnMoNi 55. Non-destructive tests and conventional metallographic analyses by means of transverse structure micrography were unable to give a sufficiently accurate picture of the two types of cracks in the micro- and millimeter range, a 'volumetric' method was employed (tangential structure micrography with stepwise abrasion) which permitted semi-automatic and fast evaluation. The experimental results showed the selective influence of several elements and led to the development of a method to evaluate the cumulative effect of the chemical elements on relaxation cracking and hot cracking by addition of the selective influence. The method gives quantitative data on material optimisation with regard to the reduction of brittle and crack-prone states and confirms the findings of welding simulation tests. (orig./IHOE) 891 IHOE/orig.- 892 HIS [de

Study of the microstructure and of microhardness variation of a Ni-Fe-Cr austenitic alloy by niobium

International Nuclear Information System (INIS)

Carvalho e Camargo, M.U. de; Lucki, G.

1979-01-01

The mechanisms of hardening and corrosion resistance increase in Ni-Fe-Cr austenitic stainless steels by Nb additions are of interest to nuclear technology Niobium additions to a 321 type stainless steel were made in order to study the microhardness, electrical resistivity and metallography. Experimental measurements results are shown. The effect of Nb additions as a micro-alloying element and the thermal and mechanical processes (cold working in particular) in the microstructure and microhardness properties of the 11% Ni - 70%Fe - 17% Cr austenitic alloys were studied. (Author) [pt

The Influence of Cr on the Solidification Behavior of Polycrystalline γ(Ni)/ γ'(Ni3Al)- δ(Ni3Nb) Eutectic Ni-Base Superalloys

Science.gov (United States)

Xie, Mengtao; Helmink, Randolph; Tin, Sammy

2012-04-01

In the current investigation, the effect of Cr on the solidification characteristics and as-cast microstructure of pseudobinary γ- δ eutectic alloys based on a near-eutectic composition (Ni-5.5Al-13.5Nb at. pct) was investigated. It was found that Cr additions promote the formation of a higher volume fraction of γ- δ eutectic microstructure in the interdendritic region. Increasing levels of Cr also triggered morphological changes in the γ- δ eutectic and the formation of γ- γ'- δ ternary eutectic during the last stage of solidification. A detailed characterization of the as-cast alloys also revealed that Cr additions suppressed the liquidus, solidus, and γ' precipitation temperature of these γ/ γ'- δ eutectic alloys. A comparison of the experimental results with thermodynamic calculations using the CompuTherm Pandat database (CompuTherm LLC, Madison, WI) showed qualitative agreement.

Influence of microstructural development during annealing at 780oC on creep resistance of ferritic-martensitic T91 (9%Cr-1%Mo-V-Nb) steel

International Nuclear Information System (INIS)

De Cicco, H; Zavaleta Gutierrez, N; Marrero, J; Luppo, M.I; Danon, C.A

2006-01-01

Due to its good properties of creep resistance, toughness and rust resistance, martensitic-ferritic 9%Cr-1%Mo steels are widely used for the production of heating plant components, boilers, heat exchangers, piping and tubing, etc. The effectiveness in steels of MX carbonitrides such as (Nb,V) (C,N) on improving creep resistance at high temperatures is well known. Controlling the behavior of the MX phases to precipitation, during annealing, is essential for obtaining a stable microstructure that can resist high temperatures. This study investigates the relationship between creep resistance and the microstructural changes that occur at different annealing times at a temperature of 780 o C -used industrially during the production and post-welding- in T91 steel. Creep trials were carried out at 600 o C and 190 MPa, and the samples were characterized using optic microscopy (OM), inductively coupled plasma-atomic emission spectrometry (ICP-AES) and transmission electron microscopy (TEM), the latter including a facility for energy dispersive spectroscopy (EDS). Based on its morphological characteristics, the MX precipitates are classified into three types, types I, II and III. Tempering time at 780 o C has been found to be one of the factors that determines which MX is dominant in the annealed steel. The presence of type MX-III, formed by the secondary precipitation of a VN particle adhering to a NbX, commonly called 'wing', seems to favor creep resistance in these steels. This type of of precipitate, then, fills an effective role in the anchoring of dislocations during creep (cw)

Supporting data for senary refractory high-entropy alloy CrxMoNbTaVW

Directory of Open Access Journals (Sweden)

B. Zhang

2015-12-01

Full Text Available This data article is related to the research paper entitled “senary refractory high-entropy alloy CrxMoNbTaVW [1]”. In this data article, the pseudo-binary Cr-MoNbTaVW phase diagram is presented to show the impact of Cr content to the senary Cr-MoNbTaVW alloy system; the sub-lattice site fractions are presented to show the disordered property of the Cr-MoNbTaVW BCC structures; the equilibrium and Scheil solidification results with the actual sample elemental compositions are presented to show the thermodynamic information of the melted/solidified CrxMoNbTaVW samples; and the raw EDS scan data of the arc-melted CrxMoNbTaVW samples are also provided.

Influence of Nb content on grain size and mechanical properties of 18 wt% Cr ferritic stainless steel

Energy Technology Data Exchange (ETDEWEB)

Kang, Y. [School of Materials Science and Engineering, University of Science and Technology Beijing, Beijing 100083 (China); Mao, W.M., E-mail: weiminmao@263.net [School of Materials Science and Engineering, University of Science and Technology Beijing, Beijing 100083 (China); Chen, Y.J. [School of Materials Science and Engineering, University of Science and Technology Beijing, Beijing 100083 (China); Jing, J.; Cheng, M. [Taizhou Xinyu Precision Manufacture Company Limited, Jiangyan 225500, Jiangsu (China)

2016-11-20

The influence of Nb contents between 0.20 and 1.20 wt% on the grain size and mechanical properties of 18 wt% Cr ferritic stainless steel produced by investment casting was investigated. The average grain sizes of the three steels decreased apparently with increasing Nb content mainly due to the increasing number of pre-existing oxides formed at higher temperature, which were more likely to be the nuclei of heterogeneous nucleation. The thermodynamic analysis of Nb(C,N) formation was in conformity to the experimental result that the Nb(C,N) precipitates became larger with increasing Nb content. The as-cast specimen with the smallest grain size of steel C had the worse tensile strength and elongation in comparison with the as-cast specimens of steels A and B, mostly owing to the catenarian and dendritic Nb(C,N) particles distributed densely at the grain boundaries. The mechanical properties of specimens were not improved remarkably through high temperature solid-solution, whereas the mechanical properties of normalized specimens in the three steels were improved to different degrees. The coalescence and sparse distribution of smaller precipitates at grain boundaries after normalizing effectively weakened the local stress concentration arising from the reticular distribution of particles. The normalized specimen of steel A with 0.24 wt% Nb still showed good mechanical properties. Normalizing at 850 °C for 2 h is the appropriate heat treatment for the 18 wt% Cr ferritic stainless steel. The comparatively rational Nb content of the ferritic stainless steel is between 0.20 and 0.40 wt% for investment casting production.

Stress-relieving annealing of Cr-Mo steel for high temperature pressure vessels and the quality change in use

International Nuclear Information System (INIS)

Makioka, Minoru; Hirano, Hiromichi

1976-01-01

The securing of good mechanical properties is difficult in thick plates for large pressure vessels because cooling rate is insufficient and time is prolonged in heat treatment. Cr-Mo steel plates are usually used in the state of improved notch toughness though somewhat reduced strength by normalizing or accelerated cooling and tempering. If the time for heat treatment is prolonged, the embrittlement occurs. The effects of temperature, holding time, and cooling rate in stress-relieving treatment on the mechanical properties of 1-1/4Cr - 1/2Mo, 2-1/4Cr - 1Mo, 3Cr - 1Mo, and 5Cr - 1/2Mo steels were investigated. The tensile strength lowered almost linearly as the hollomon-Jaffe parameter of heat treatment condition increased in all the steels. The transition temperature shifted continuously to high temperature side in 1-1/4Cr - 1/2Mo steel, but the notch toughness was improved up to certain values and then the tendency turning to brittleness was shown in the other steels, as the H-J parameter increased. When the holding time became longer, the transition temperature shifted to higher temperature side, but the cooling rate showed no effect. The condition for stress relieving treatment must be selected so that the ferrite bands observed in welded metal do not arise. The embrittlement at the operation temperature of 400 - 450 0 C for a long time is evaluated by the comparison with that by stepped cooling method. (Kako, I.)

Dry sliding wear behavior and corrosion resistance of NiCrBSi coating deposited by activated combustion-high velocity air fuel spray process

International Nuclear Information System (INIS)

Liu, Shenglin; Zheng, Xueping; Geng, Gangqiang

2010-01-01

NiCrBSi is a Ni-based superalloy widely used to obtain high wear and corrosion resistant coatings. This Ni-based alloy coating has been deposited onto 0Cr13Ni5Mo stainless steel using the AC-HVAF technique. The structure and morphologies of the Ni-based coatings were investigated by X-ray diffraction (XRD), scanning electron microscopy (SEM) and energy-dispersive spectrometer (EDS). The wear resistance and corrosion resistance were studied. The tribological behaviors were evaluated using a HT-600 wear test rig. The wear resistance of the Ni-based coating was shown to be higher than that of the 0Cr13Ni5Mo stainless steel because Fe 3 B, with high hardness, was distributed in the coating so the dispersion strengthening in the Ni-based coating was obvious and this increased the wear resistance of the Ni-based coating in a dry sliding wear test. Under the same conditions, the worn volume of 0Cr13Ni5Mo stainless steel was 4.1 times greater than that of the Ni-based coating. The wear mechanism is mainly fatigue wear. A series of the electrochemical tests was carried out in a 3.5 wt.% NaCl solution in order to examine the corrosion behavior. The mechanisms for corrosion resistance are discussed.

Heat treatment effects on impact toughness of 9Cr-1MoVNb and 12Cr-1MoVW steels irradiated to 100 dpa

Energy Technology Data Exchange (ETDEWEB)

Klueh, R.L.; Alexander, D.J. [Oak Ridge National Lab., TN (United States)

1997-08-01

Plates of 9Cr-1MoVNb and 12Cr-1MoVW steels were given four different heat treatments: two normalizing treatments were used and for each normalizing treatment two tempers were used. Miniature Charpy specimens from each heat treatment were irradiated to {approx}19.5 dpa at 365{degrees}C and to {approx}100 dpa at 420{degrees}C in the Fast Flux Test Facility (FFTF). In previous work, the same materials were irradiated to 4-5 dpa at 365{degrees}C and 35-36 dpa at 420{degrees}C in FFTF. The tests indicated that prior austenite grain size, which was varied by the different normalizing treatments, had a significant effect on impact behavior of the 9Cr-1MoVNb but not on the 12Cr-1MoVW. Tempering treatment had relatively little effect on the shift in DBTT for both steels. Conclusions are presented on how heat treatment can be used to optimize impact properties.

Heat treatment effects on impact toughness of 9Cr-1MoVNb and 12Cr-1MoVW steels irradiated to 100 dpa

International Nuclear Information System (INIS)

Klueh, R.L.; Alexander, D.J.

1997-01-01

Plates of 9Cr-1MoVNb and 12Cr-1MoVW steels were given four different heat treatments: two normalizing treatments were used and for each normalizing treatment two tempers were used. Miniature Charpy specimens from each heat treatment were irradiated to ∼19.5 dpa at 365 degrees C and to ∼100 dpa at 420 degrees C in the Fast Flux Test Facility (FFTF). In previous work, the same materials were irradiated to 4-5 dpa at 365 degrees C and 35-36 dpa at 420 degrees C in FFTF. The tests indicated that prior austenite grain size, which was varied by the different normalizing treatments, had a significant effect on impact behavior of the 9Cr-1MoVNb but not on the 12Cr-1MoVW. Tempering treatment had relatively little effect on the shift in DBTT for both steels. Conclusions are presented on how heat treatment can be used to optimize impact properties

Corrosion Performance of Fe-Cr-Ni Alloys in Artificial Saliva and Mouthwash Solution

Science.gov (United States)

Porcayo-Calderon, J.; Casales-Diaz, M.; Salinas-Bravo, V. M.; Martinez-Gomez, L.

2015-01-01

Several austenitic stainless steels suitable for high temperature applications because of their high corrosion resistance and excellent mechanical properties were investigated as biomaterials for dental use. The steels were evaluated by electrochemical techniques such as potentiodynamic polarization curves, cyclic polarization curves, measurements of open circuit potential, and linear polarization resistance. The performance of steels was evaluated in two types of environments: artificial saliva and mouthwash solution at 37°C for 48 hours. In order to compare the behavior of steels, titanium a material commonly used in dental applications was also tested in the same conditions. Results show that tested steels have characteristics that may make them attractive as biomaterials for dental applications. Contents of Cr, Ni, and other minor alloying elements (Mo, Ti, and Nb) determine the performance of stainless steels. In artificial saliva steels show a corrosion rate of the same order of magnitude as titanium and in mouthwash have greater corrosion resistance than titanium. PMID:26064083

Resistivity, hysteresis, and magnetization of 9% Cr stainless steel as a function of temperature and its electromagnetic shielding effects in cylindrical structures

International Nuclear Information System (INIS)

Praeg, W.F.

1979-01-01

Ferromagnetic stainless steels may offer significantly greater wall life-times for first wall/blanket and vacuum vessel structures than commonly used non-magnetic stainless steels. One steel under consideration has the following composition, in wt %, Fe(86.24), Cr(9), Mo(2), Mn(1), Si(0.75), Nb(0.50), V(0.30), C(0.15), P(0.3), S(0.30). There appears to be no literature on the electromagnetic properties of this material. Therefore, the resistivity, the hysteresis loops, and magnetization were measured as a function of temperature up to the Curie point

Excellent corrosion resistance of 18Cr-20Ni-5Si steel in liquid Pb-Bi

International Nuclear Information System (INIS)

Kurata, Y.; Futakawa, M.

2004-01-01

The corrosion properties of three austenitic steels with different Si contents were studied under oxygen-saturated liquid Pb-Bi condition for 3000 h. The three austenitic steels did not exhibit appreciable dissolution of Ni and Cr at 450 deg. C. At 550 deg. C, the thick ferrite layer produced by dissolution of Ni and Cr was found in JPCA and 316SS with low Si contents while the protective oxide film composed of Si and O was formed on 18Cr-20Ni-5Si steel and prevented dissolution of Ni and Cr

Boron Steel: An Alternative for Costlier Nickel and Molybdenum Alloyed Steel for Transmission Gears

Directory of Open Access Journals (Sweden)

A. Verma

2010-06-01

Full Text Available Case Carburized (CC low carbon steels containing Ni, Cr and Mo alloying elements are widely used for transmission gears in automobile, as it possesses desired mechanical properties. In order to cut cost and save scarce materials like Ni and Mo for strategic applications, steel alloyed with Boron has been developed, which gives properties comparable to Ni-Cr-Mo alloyed steel. In the process of steel development, care was taken to ensure precipitation of boron which results in precipitation hardening. The characterization of the developed boron steel had exhibited properties comparable to Ni-Cr-Mo alloyed steel and superior to conventional boron steel.

Phase Evolution in and Creep Properties of Nb-Rich Nb-Si-Cr Eutectics

Science.gov (United States)

Gang, Florian; Kauffmann, Alexander; Heilmaier, Martin

2018-03-01

In this work, the Nb-rich ternary eutectic in the Nb-Si-Cr system has been experimentally determined to be Nb-10.9Si-28.4Cr (in at. pct). The eutectic is composed of three main phases: Nb solid solution (Nbss), β-Cr2Nb, and Nb9(Si,Cr)5. The ternary eutectic microstructure remains stable for several hundred hours at a temperature up to 1473 K (1200 °C). At 1573 K (1300 °C) and above, the silicide phase Nb9(Si,Cr)5 decomposes into α-Nb5Si3, Nbss, and β-Cr2Nb. Under creep conditions at 1473 K (1200 °C), the alloy deforms by dislocation creep while the major creep resistance is provided by the silicide matrix. If the silicide phase is fragmented and, thus, its matrix character is destroyed by prior heat treatment [ e.g., at 1773 K (1500 °C) for 100 hours], creep is mainly controlled by the Laves phase β-Cr2Nb, resulting in increased minimum strain rates. Compared to state of the art Ni-based superalloys, the creep resistance of this three-phase eutectic alloy is significantly higher.

Stress-controlled inelastic behavior of modified 9 Cr-1 Mo steel at elevated temperatures

International Nuclear Information System (INIS)

Taguchi, Kosei.

1989-01-01

Interest in the ferritic steels of higher chromium concentration has increased recently because of an economical combination of mechanical and corrosion properties at elevated temperatures. A modified 9 Cr-1 Mo ferritic steel, developed in the United States, has been expected as an alternative structural material for fast breeder reactor components, in which Type 304 stainless steel or 2.25 Cr-1 Mo steel is currently used. For application of this material to the structural components, a lot of work has been done to develop evaluation methods for the deformation behavior and strength properties. The authors have studied the inelastic behavior and the creep-fatigue properties of modified 9 Cr-1 Mo steel at elevated temperatures, and proposed a constitutive equation and a creep-fatigue damage equation based on the overstress concept. In this paper, the applicability is discussed of the constitutive equation to stress-controlled inelastic behavior, such as creep strain hardening and stress cycling

In-situ Raman and X-ray photoelectron spectroscopic studies on the pitting corrosion of modified 9Cr-1Mo steel in neutral chloride solution

Science.gov (United States)

Ramya, S.; Nanda Gopala Krishna, D.; Mudali, U. Kamachi

2018-01-01

In-situ Raman and X-ray photoelectron spectroscopic studies were performed for the identification of native and corroded surface oxide layers of modified 9Cr-1Mo steel. The Raman data obtained for native oxide layer of modified 9Cr-1Mo steel revealed that it was mainly composed of oxides of Fe and Cr. The presence of alloying element Mo was found to be less significant in the native oxide film. The oxides of Cr were dominant at the surface and were found to be decreasing closer to metal/oxide layer interface. The changes in the chemical composition of the native films upon in-situ pitting during potentiostatic polarization experiment were characterized by in-situ Raman analysis. The corrosion products of potentiostatically polarized modified 9Cr-1Mo steel was composed of dominant Fe (III) phases viz., γ- Fe2O3, α and γ - FeOOH along with the oxides of chromium. The results from Raman analysis were corroborated with the XPS experiments on as received and pitted samples of modified 9Cr-1Mo steel specimens. It was observed that the oxides of Cr and Mo contributed for the stability of the surface layer by forming Cr2O3 and MoO3. Also, the study attempted to find out the intermediate corrosion products inside the metastable pits to account for the pseudo passive behavior of modified 9Cr-1Mo steel in 0.1 M NaCl solution.

Neutron irradiation effects on the ductile-brittle transition of ferritic/martensitic steels

Energy Technology Data Exchange (ETDEWEB)

Klueh, R.L.; Alexander, D.J. [Oak Ridge National Lab., TN (United States)

1997-08-01

Ferritic/martensitic steels such as the conventional 9Cr-1MoVNb (Fe-9Cr-1Mo-0.25V-0.06Nb-0.1C) and 12Cr-1MoVW (Fe-12Cr-1Mo-0.25V-0.5W-0.5Ni-0.2C) steels have been considered potential structural materials for future fusion power plants. The major obstacle to their use is embrittlement caused by neutron irradiation. Observations on this irradiation embrittlement is reviewed. Below 425-450{degrees}C, neutron irradiation hardens the steels. Hardening reduces ductility, but the major effect is an increase in the ductile-brittle transition temperature (DBTT) and a decrease in the upper-shelf energy, as measured by a Charpy impact test. After irradiation, DBTT values can increase to well above room temperature, thus increasing the chances of brittle rather than ductile fracture.

Microstructure and elevated temperature stability of 9-12% Cr steels

Energy Technology Data Exchange (ETDEWEB)

Dogan, Omer N.; Hawk, Jeffrey A.

2005-02-01

Medium Cr steels have been used in fossil fired power plants for many years because of their excellent high temperature stability and mechanical properties. As the desire to increase the efficiency of power plants continues, the operating temperature (>650C) continues to go up. Currently available low and medium Cr containing steels will not withstand the new operating temperature and must be reassessed in terms of their solid-solution and precipitation strengthening schemes. Three medium Cr steels were developed to investigate high temperature alloy strengthening strategies: 0.08C-(9-12)Cr-1.2Ni-0.7Mo-3.0Cu-3.0Co-0.5Ti. The microstructure of the alloy will be described in the as-cast and thermo-mechanically worked states. In addition, the effect on microstructure from long-term high temperature exposure will also be discussed. Finally, the overall stability of these steels will be compared against currently available power plant steels.

Microstructure Evolution and Chemical Analysis on Carbon Steels and Fe-Cr-Mo Alloys after FAC Simulation Tests

International Nuclear Information System (INIS)

Kim, Seunghyun; Kim, Taeho; Lee, Yun Ju; Kim, Ji Hyun

2017-01-01

Flow-accelerated corrosion (FAC) is an environment assisted degradation of structural materials, which usually occurs in pipelines of power plants. There have been many studies to investigate the fundamental mechanism and corresponding countermeasures against FAC, and recently the carbon steels have been replaced by ASTM A 335 P22, which contains approximately 2.2 wt.% of Cr and 1 wt.% of Mo. By enhancing passivity of P22 by Cr, it is reported that FAC rate has been greatly reduced. However, while corrosion behavior of Fe-based alloys is relatively well known, their behavior under high-temperature flowing water is not well investigated. In other words, effects of Cr and its corrosion and oxidation behavior is not clearly revealed. Furthermore, it is known that Mo enhances the pitting corrosion resistance of alloys however its mechanism is not clearly investigated. Recently, replacement of Mo in alloy contents has been widely studied because of the cost of Mo. Carbon steels undergo severe environmental-assisted degradation behavior so called FAC, and as its countermeasure the carbon steel has been replaced by P22 which contains Cr and Mo. It is generally known that Cr and Mo enhances passivity of Fe-based alloys however their corrosion and oxidation behavior has not been fully investigated especially in high-temperature flowing water environments. In this study, we employed HRTEM and synchrotron XAS techniques in order to investigate detailed microstructure evolution and chemical bonding of the commercialized carbon steel and the Fe-Cr-Mo alloys. From the analysis, it is found that while carbon steels exhibit porous oxide P22 exhibit oxide structures with thin Cr-rich oxide and spinel. Therefore, carbon steel undergoes severe FAC compared to P22 however effects of Cr and Mo and their behavior in high-temperature flowing water will be investigated.

Microstructures and room temperature fracture toughness of Nb/Nb5Si3 composites alloyed with W, Mo and W–Mo fabricated by spark plasma sintering

International Nuclear Information System (INIS)

Xiong, Bowen; Cai, Changchun; Wang, Zhenjun

2014-01-01

Highlights: • Microstructure of Nb/Nb 5 Si 3 composite alloyed with W and Mo is change obviously. • W and Mo elements can solid solution in Nb and Nb 5 Si 3 phase respectively. • Alloyed with W and Mo together, the solid solubility of Nb 5 Si 3 phases is undetected. • The Nb/Nb 5 Si 3 composite alloyed with W and Mo together has high fracture toughness. - Abstract: Microstructures and room temperature fracture toughness of Nb/Nb 5 Si 3 composites alloyed with W, Mo and W–Mo fabricated by spark plasma sintering were investigated. The microstructures were examined using scanning electron microscope (SEM). X-ray diffraction (XRD) was performed on the bulk specimens for identification of phases. The chemical species were analyzed using electron-probe micro-analysis (EPMA). Results indicated that the microstructures of Nb/Nb 5 Si 3 composites alloyed with W or Mo is unaltered, including primary Nb and eutectic mixtures of Nb and Nb 5 Si 3 , and the coarse and fine eutectic mixtures. The W and Mo elements solid solution in Nb and Nb 5 Si 3 phase are detected. But that alloyed with W and Mo together, The microstructures are change obviously, including Nb phase, the solid solubility phases of W and Mo atoms in Nb, and the solid solubility phases of Nb atoms in W are also found, but the solid solubility phenomenon of Nb 5 Si 3 phases is not detected. The microhardness of Nb and Nb 5 Si 3 phases increases obviously because of solid solution strengthening. The Nb/Nb 5 Si 3 composite alloyed with W and Mo together hashing high fracture toughness is attributable to the big eutectic Nb and interface of eutectic phases, which can bear large deformation to absorb the crack energy and form the decohesion between eutectic phases

Creep rupture properties of oxidised 20%Cr austenitic stainless steels

International Nuclear Information System (INIS)

Lobb, R.C.; Ecob, R.C.

1989-02-01

Sheet specimens of stabilised 20%Cr/25%Ni/Nb and nitrided 20%Cr/25%Ni/Ti stainless steels, both used as fuel cladding materials in CAGRs, have been oxidised in simulated reactor gas (Co 2 /1-2%CO) for up to l.9kh at 850 0 C, including intermediate thermal cycles to room temperature. The oxidised specimens have been creep tested subsequently at 750 0 C, under conditions of constant stress. The creep rupture properties are affected differently for the two materials. For 20%Cr/25%Ni/Nb stainless steel, there was no effect of oxidation on the intrinsic microstructure, when compared with thermally aged, non-oxidised material. Any differences in creep ductility were ascribed to geometric effects in specimens of this alloy. Lower ductilities were associated with an increased incidence of pitting attack (higher oxide spallation) and it was concluded that the extent of local, rather than general, loss of section controlled the ductility. For nitrided 20%Cr/25%Ni/Ti stainless steel, the intrinsic microstructure was affected by oxidation, such that increased grain boundary precipitation of M 23 C 6 occurred. The resultant effect was for a greater tendency for intergranular failure at lower ductility than for the thermally aged material. The magnitude of this reduction could not be quantified because the specimen geometry was also changed by oxidation. In this instance, the oxidation mode that produced the most severe loss of section was grain boundary, rather than pitting, attack. This mode of attack was not linked directly to oxide fracture/spallation, but to the period of oxidation. (author)

Prediction of Ductile Fracture Behaviors for 42CrMo Steel at Elevated Temperatures

Science.gov (United States)

Lin, Y. C.; Liu, Yan-Xing; Liu, Ge; Chen, Ming-Song; Huang, Yuan-Chun

2015-01-01

The ductile fracture behaviors of 42CrMo steel are studied by hot tensile tests with the deformation temperature range of 1123-1373 K and strain rate range of 0.0001-0.1 s-1. Effects of deformation temperature and strain rate on the flow stress and fracture strain of the studied steel are discussed in detail. Based on the experimental results, a ductile damage model is established to describe the combined effects of deformation temperature and strain rate on the ductile fracture behaviors of 42CrMo steel. It is found that the flow stress first increases to a peak value and then decreases, showing an obvious dynamic softening. This is mainly attributed to the dynamic recrystallization and material intrinsic damage during the hot tensile deformation. The established damage model is verified by hot forging experiments and finite element simulations. Comparisons between the predicted and experimental results indicate that the established ductile damage model is capable of predicting the fracture behaviors of 42CrMo steel during hot forging.

Study of 13Cr-4Ni-(Mo (F6NM Steel Grade Heat Treatment for Maximum Hardness Control in Industrial Heats

Directory of Open Access Journals (Sweden)

Massimo De Sanctis

2017-09-01

Full Text Available The standard NACE MR0175 (ISO 15156 requires a maximum hardness value of 23 HRC for 13Cr-4Ni-(Mo steel grade for sour service, requiring a double tempering heat treatment at temperature in the range 648–691 °C for the first tempering and 593–621 °C for the second tempering. Difficulties in limiting alloy hardness after the tempering of forged mechanical components (F6NM are often faced. Variables affecting the thermal behavior of 13Cr-4Ni-(Mo during single and double tempering treatments have been studied by means of transmission electron microscopy (TEM observations, X-ray diffraction measurements, dilatometry, and thermo-mechanical simulations. It has been found that relatively low Ac1 temperatures in this alloy induce the formation of austenite phase above 600 °C during tempering, and that the formed, reverted austenite tends to be unstable upon cooling, thus contributing to the increase of final hardness via transformation to virgin martensite. Therefore, it is necessary to increase the Ac1 temperature as much as possible to allow the tempering of martensite at the temperature range required by NACE without the detrimental formation of virgin martensite upon final cooling. Attempts to do so have been carried out by reducing both carbon (<0.02% C and nitrogen (<100 ppm levels. Results obtained herein show final hardness below NACE limits without an unacceptable loss of mechanical strength.

Microstructure of laser cladded martensitic stainless steel

CSIR Research Space (South Africa)

Van Rooyen, C

2006-08-01

Full Text Available and martensite with 10% ferrite for Material B. Table 7 - Proposed martensitic stainless steel alloys for laser cladding Material C* Cr Ni Mn Si Mo Co Ms (ºC)* Cr eq Ni eq Material A 0.4 13 - 1 0.5 2.5 5.5 120 16.5 12.5 Material B 0.2 15 2 1 0.7 2.5 5.5 117... dilution, low heat input, less distortion, increased mechanical and corrosion properties excellent repeatability and control of process parameters. Solidification of laser cladded martensitic stainless steel is primarily austenitic. Microstructures...

The Phase Transformations in Hypoeutectoid Steels Mn-Cr-Ni

Directory of Open Access Journals (Sweden)

RoŻniata E.

2015-04-01

Full Text Available The results of a microstructure and hardness investigations of the hypoeutectoid steels Mn-Cr-Ni, imitating by its chemical composition toughening steels, are presented in the paper. The analysis of the kinetics of phase transformations of undercooled austenite of steels containing different amounts of alloying elements in their chemical composition, constitutes the aim of investigations.

Interface bonding of NiCrAlY coating on laser modified H13 tool steel surface

Science.gov (United States)

Reza, M. S.; Aqida, S. N.; Ismail, I.

2016-06-01

Bonding strength of thermal spray coatings depends on the interfacial adhesion between bond coat and substrate material. In this paper, NiCrAlY (Ni-164/211 Ni22 %Cr10 %Al1.0 %Y) coatings were developed on laser modified H13 tool steel surface using atmospheric plasma spray (APS). Different laser peak power, P p, and duty cycle, DC, were investigated in order to improve the mechanical properties of H13 tool steel surface. The APS spraying parameters setting for coatings were set constant. The coating microstructure near the interface was analyzed using IM7000 inverted optical microscope. Interface bonding of NiCrAlY was investigated by interfacial indentation test (IIT) method using MMT-X7 Matsuzawa Hardness Tester Machine with Vickers indenter. Diffusion of atoms along NiCrAlY coating, laser modified and substrate layers was investigated by energy-dispersive X-ray spectroscopy (EDXS) using Hitachi Tabletop Microscope TM3030 Plus. Based on IIT method results, average interfacial toughness, K avg, for reference sample was 2.15 MPa m1/2 compared to sample L1 range of K avg from 6.02 to 6.96 MPa m1/2 and sample L2 range of K avg from 2.47 to 3.46 MPa m1/2. Hence, according to K avg, sample L1 has the highest interface bonding and is being laser modified at lower laser peak power, P p, and higher duty cycle, DC, prior to coating. The EDXS analysis indicated the presence of Fe in the NiCrAlY coating layer and increased Ni and Cr composition in the laser modified layer. Atomic diffusion occurred in both coating and laser modified layers involved in Fe, Ni and Cr elements. These findings introduce enhancement of coating system by substrate surface modification to allow atomic diffusion.

Structure and magnetic properties of NdFeB thin films with Cr, Mo, Nb, Ta, Ti, and V buffer layers

International Nuclear Information System (INIS)

Jiang, H.; O'Shea, M.J.

2000-01-01

Layers of NdFeB of the form A(20 nm)/NdFeB(d nm)/A(20 nm) where A represents Cr, Mo, Nb, Ta, Ti, V were prepared on a silicon substrate by magnetron sputtering. The purpose is to determine how (i) the chosen buffer layer and (ii) NdFeB layer thickness d (especially d 2 Fe 14 B with no preferred crystalline orientation. Our highest coercivities occur for buffer layer elements from row five of the periodic table, 20 kOe (1600 kA/m) in a Nb buffered sample with d of 180 nm and 17 kOe (1350 kA/m) in a Mo buffered sample with d of 180 nm. Buffer layers from row four (Ti, V, and Cr) and row six (Ta) all give lower coercivities. Our largest energy product, 10.3 MG-Oe (82 kJ/m 3 ), is obtained for the Mo buffered sample. Average Nd 2 Fe 14 B crystallite size for this sample is 27 nm. Only the Cr and Ti buffered films show a large coercivity (≥2 kOe) for d of 54 nm with the Cr films showing the highest coercivity, 2.7 kOe (215 kA/m). In films subjected to a rapid thermal anneal (anneal time 30 s) we find that both the coercivity and energy product are larger than in samples subjected to a 20 min anneal. In our Nb buffered systems we obtain coercivities as high as 26.3 kOe (2090 kA/m) after a rapid thermal anneal

Phase transformation and tribological properties of Ag-MoO3 contained NiCrAlY based composite coatings fabricated by laser cladding

Science.gov (United States)

Wang, Lingqian; Zhou, Jiansong; Xin, Benbin; Yu, Youjun; Ren, Shufang; Li, Zhen

2017-08-01

Ag-MoO3 contained NiCrAlY based composite coating was successfully prepared on GH4169 stainless steel substrate by high energy ball milling and laser cladding. The microstructure and phase transformation were investigated by scanning electron microscopy (SEM) equipped with energy dispersive spectroscopy (EDS) and X-ray diffraction spectrum (XRD). The tribological behavior and mechanism from room temperature to 800 °C were investigated. Results showed that MoO3 in the composite powders transformed to Mo2C reinforcement under the high energy density of laser, and a series of opposite transformation occurred during friction process. The coating showed the lowest friction coefficient and low wear rate at 600 °C and 800 °C due to the generation of Ag2MoO4 during tribo-chemical reactions and the formation of lubrication glaze on the worn surface. Ag made effective lubrication when the temperature rose up to 200 °C. The coating displayed a relatively high friction coefficient (about 0.51) at 400 °C, because though MoO3 (oxidation products of Mo2C) and Ag2MoO4 were detected on the worn surface, they could not realize effective lubrication at this temperature. Abrasive wear, adhesive wear and plastic deformation contributed to the increased friction and wear.

Análisis mecánico y tribológico de los recubrimientos fe-cr-ni-c y ni-al-mo

Directory of Open Access Journals (Sweden)

JORGE E. MUÑOZ

2007-01-01

Full Text Available En este trabajo de investigación se evaluaron dos recubrimientos aplicados por medio de la técnica de rociado térmico por combustión, la aleación: Ni=89%, Al = 5,5%, Mo=5,5% y la aleación Fe=81,8%, Cr=16%, Ni=2%, C=0,2. La preparación superficial de las probetas se realizó usando chorro de arena. Se realizaron pruebas de resistencia al cortante, adherencia, desgaste abrasivo, desgaste por deslizamiento y flexión en cuatro puntos. El recubrimiento Fe-Cr-Ni-C presentó menor pérdida de masa, tanto para desgaste abrasivo como para el desgaste por deslizamiento. La multicapa presentó una mayor porosidad en el recubrimiento Ni-Al- Mo usado como capa base y la capa exterior de Fe-Cr-Ni-C presentó mayor cantidad de partículas no fundidas y óxidos. La falla ocurrida en el ensayo de adherencia para las probetas con recubrimiento multicapa fue de característica adhesiva y cohesiva. El esfuerzo en el que se presenta la fisura por flexión en el recubrimiento multicapa disminuyó con el aumento del espesor

Hydrogen induced plastic damage in pressure vessel steel of 2.25Cr-1Mo

International Nuclear Information System (INIS)

Han, G.W.; Song, Y.J.

1995-01-01

2.25Cr-1Mo steel is generally employed as a hydrogenation reaction vessel material used at elevated temperature and in a hydrogen containing environment. During service of the reaction vessel, a large number of hydrogen atoms would enter its wall. When the reaction vessel is shutdown and the temperature reduces to about ambient temperature, the hydrogen atoms remaining in the wall would induce plastic damage in the steel. The mechanism of hydrogen induced plastic damage is different for various materials with different microstructures. Investigations have demonstrated that the hydrogen induced plastic damage in carbide annealed carbon steels is caused by hydrogen accelerating the initiating and growing of microvoids from the carbide particles. However, SEM examination on the fracture surface of hydrogen charged tensile specimen of 2.25Cr-1Mo steel show that a large number of fisheyes appear on the fracture surface. This indicates that hydrogen induced plastic damage in 2.25Cr-1Mo steel is related to the occurrence of fisheye cracks during plastic deformation. By means of micro-fracture mechanics to analyze fisheye crack occurrence from the first generation microvoid, the mechanism of hydrogen induced plastic damage in the pressure vessel steel is investigated

Room and elevated temperature Mechanical Behavior of 9-12% Cr Steels

Energy Technology Data Exchange (ETDEWEB)

Dogan, Omer N.; Hawk, Jeffrey A.; Schrems, Karol K.

2005-02-01

The mechanical properties of medium Cr steels used in fossil fired power plants are very good because of their excellent high temperature microstructural stability. However, as the desire to increase the operating temperature (>650C) of the plant goes up, the need for steels that maintain their strength at these temperatures also increases. The mechanical properties of three medium Cr steels (0.08C-(9-12)Cr-1.2Ni-0.7Mo-3.0Cu-3.0Co-0.5Ti) were investigated through hardness, hot hardness and tensile measurements. The strength of the 9-12%Cr steels at room temperature after long-term isothermal aging (750C; 1000 hours) compares favorably with that of other power plant steels (e.g., P91). In addition, the elevated temperature strength and hot hardness also behave similarly. The mechanical behavior will be discussed in terms of the strength, elongation and tensile fracture characteristics.

Caustic cracking of 2 1/4 CrMo steel

International Nuclear Information System (INIS)

Cowen, H.C.; Thorley, A.W.

1983-12-01

Stress corrosion cracking tests performed on the 21/4 Cr Mo ferritic steel are described. The principal environments studied were strong, aqueous caustic soda, molten anhydrous caustic soda, and caustic soda with an addition of sodium. Emphasis has been placed on material in the quenched-hardened condition. (author)

Microstructure and tribological properties of NiMo/Mo2Ni3Si intermetallic 'in-situ' composites

International Nuclear Information System (INIS)

Gui Yongliang; Song Chunyan; Yang Li; Qin Xiaoling

2011-01-01

Research highlights: → Wear resistant NiMo/Mo 2 Ni 3 Si intermetallic 'in-situ' composites was fabricated successfully with Mo-Ni-Si powder blends as the starting materials. Microstructure of the NiMo/Mo 2 Ni 3 Si composites consists of Mo 2 Ni 3 Si primary dendrites, binary intermetallic phase NiMo and small amount of Ni/NiMo eutectics structure. The NiMo/Mo 2 Ni 3 Si composites exhibited high hardness and outstanding tribological properties under room-temperature dry-sliding wear test conditions which were attributed to the covalent-dominant strong atomic bonds and excellent combination of strength and ductility and toughness. - Abstract: Wear resistant NiMo/Mo 2 Ni 3 Si intermetallic 'in-situ' composites with a microstructure of ternary metal silicide Mo 2 Ni 3 Si primary dendritic, the long strip-like NiMo intermetallic phase, and a small amount of Ni/NiMo eutectics structure were designed and fabricated using molybdenum, nickel and silicon elemental powders. Friction and wear properties of NiMo/Mo 2 Ni 3 Si composites were evaluated under different contact load at room-temperature dry-sliding wear test conditions. Microstructure, worn surface morphologies and subsurface microstructure were characterized by OM, XRD, SEM and EDS. Results indicate that NiMo/Mo 2 Ni 3 Si composites have low fiction coefficient, excellent wear resistance and sluggish wear-load dependence. The dominant wear mechanisms of NiMo/Mo 2 Ni 3 Si composites are soft abrasion and slightly superficial oxidative wear.

Microstructure, crystallography of phase transformations and multiple precipitations in PH 15-7Mo stainless steel

International Nuclear Information System (INIS)

Liu, Hongwei; Liu, Jiangwen; Luo, Chengping; Liu, Zhijian

2016-01-01

The microstructure and crystallographic features of a semi-austenitic precipitation hardening steel PH 15-7Mo during solution treatment, roddrawing and aging were investigated by means of optical microscope, X-ray diffraction analyzer and transmission electron microscope. It was found that the microstructure of the steel was consist of dominant austenite, small amount of martensite and 10–15 vol.% δ-ferrite after solution treatment at 1050 °C followed by cooling in water at room temperature. The austenite transformed into lath martensite during tensile roddrawing about 60% deforming companied with some coherent fine β-NiAl particles precipitated within martensite. With higher aging temperature and longer holding time, tiny carbide M_2_3C_6 particles precipitated from martensite, which kept the cubic–cubic orientation relationship (OR) with austenite and G-T OR with martensite which is different with all the reported orientations. The OR between tiny carbide M_2_3C_6 particles G-T OR with martensite was discussed in terms of crystallography of phase transformations. - Highlights: • Microstructure changes of austenitic steel PH15-7Mo were due to alloying elements, service condition and carbide M_2_3C_6. • Lath-shape martensitic laths keep pseudo {112} twinning relationship. • β-NiAl particles hold a typical cubic-to-cubic orientation relationship with martensite. • M_2_3C_6 carbide kept a cubic–cubic orientation relationship (OR) with austenite and an unusual G-T OR with martensite. • Multiple orientation relationship between M_2_3C_6 and austenite is correlative with their structural similarity.

Passive behaviour of alloy corrosion-resistant steel Cr10Mo1 in simulating concrete pore solutions with different pH

International Nuclear Information System (INIS)

Ai, Zhiyong; Jiang, Jinyang; Sun, Wei; Song, Dan; Ma, Han; Zhang, Jianchun; Wang, Danqian

2016-01-01

Highlights: • A new alloy corrosion-resistant steel Cr10Mo1 is developed for reinforcing rebar of concrete in severe environments. • The effects of pH on the passive behaviour of Cr10Mo1 steel compared with plain carbon steel were studied systematically by electrochemical techniques and surface analysis. • The mechanism for self-reinforcing passivity against carbonation of the corrosion-resistant steel is revealed. - Abstract: The passive behaviour of new alloy corrosion-resistant steel Cr10Mo1 and plain carbon steel (as a comparison) in simulating concrete pore solutions of different pH (ranging from 13.5 to 9.0) under open circuit potential conditions, was evaluated by various electrochemical techniques: potentiodynamic polarization, capacitance measurements and electrochemical impedance spectroscopy. The chemical composition and structure of passive films were investigated by X-ray photoelectron spectroscopy (XPS) and secondary ion mass spectroscopy (SIMS). The electrochemical responses of passive films show that Cr10Mo1 steel has an increasing passivity with pH decreasing while carbon steel dose conversely, revealing carbonation does no negative effect on passivation of the corrosion-resistant steel. SIMS reveals that the passive film on the corrosion-resistant steel presents a bilayer structure: an outer layer mainly consisting of Fe oxides and hydroxides, and an inner layer enriched in Cr species, while only a Fe-concentrated layer for carbon steel. According to the XPS analysis results, as the pH decreases, more stable and protective Cr oxides are enriched in the film on Cr10Mo1 steel while Fe oxides gradually decompose. Higher content of Cr oxides in the film layer provides Cr10Mo1 corrosion-resistant steel more excellent passivity at lower pH.

Passive behaviour of alloy corrosion-resistant steel Cr10Mo1 in simulating concrete pore solutions with different pH

Energy Technology Data Exchange (ETDEWEB)

Ai, Zhiyong, E-mail: 230139452@seu.edu.cn [School of Materials Science and Engineering, Southeast University, Nanjing 211189, Jiangsu (China); Jiangsu Key Laboratory of Construction Materials, Nanjing 211189, Jiangsu (China); Jiang, Jinyang, E-mail: jiangjinyang16@163.com [School of Materials Science and Engineering, Southeast University, Nanjing 211189, Jiangsu (China); Jiangsu Key Laboratory of Construction Materials, Nanjing 211189, Jiangsu (China); Sun, Wei, E-mail: sunwei@seu.edu.cn [School of Materials Science and Engineering, Southeast University, Nanjing 211189, Jiangsu (China); Jiangsu Key Laboratory of Construction Materials, Nanjing 211189, Jiangsu (China); Song, Dan, E-mail: songdancharls@hhu.edu.cn [School of Materials Science and Engineering, Southeast University, Nanjing 211189, Jiangsu (China); Jiangsu Key Laboratory of Construction Materials, Nanjing 211189, Jiangsu (China); College of Mechanics and Materials, Hohai University, Nanjing 210098, Jiangsu (China); Ma, Han, E-mail: mahan-iris@shasteel.cn [Research Institute of Jiangsu Shasteel Iron and Steel, Zhangjiagang 215625, Jiangsu (China); Zhang, Jianchun, E-mail: Zhangjc-iris@shasteel.cn [Research Institute of Jiangsu Shasteel Iron and Steel, Zhangjiagang 215625, Jiangsu (China); Wang, Danqian, E-mail: wonderbaba@126.com [School of Materials Science and Engineering, Southeast University, Nanjing 211189, Jiangsu (China); Jiangsu Key Laboratory of Construction Materials, Nanjing 211189, Jiangsu (China)

2016-12-15

Highlights: • A new alloy corrosion-resistant steel Cr10Mo1 is developed for reinforcing rebar of concrete in severe environments. • The effects of pH on the passive behaviour of Cr10Mo1 steel compared with plain carbon steel were studied systematically by electrochemical techniques and surface analysis. • The mechanism for self-reinforcing passivity against carbonation of the corrosion-resistant steel is revealed. - Abstract: The passive behaviour of new alloy corrosion-resistant steel Cr10Mo1 and plain carbon steel (as a comparison) in simulating concrete pore solutions of different pH (ranging from 13.5 to 9.0) under open circuit potential conditions, was evaluated by various electrochemical techniques: potentiodynamic polarization, capacitance measurements and electrochemical impedance spectroscopy. The chemical composition and structure of passive films were investigated by X-ray photoelectron spectroscopy (XPS) and secondary ion mass spectroscopy (SIMS). The electrochemical responses of passive films show that Cr10Mo1 steel has an increasing passivity with pH decreasing while carbon steel dose conversely, revealing carbonation does no negative effect on passivation of the corrosion-resistant steel. SIMS reveals that the passive film on the corrosion-resistant steel presents a bilayer structure: an outer layer mainly consisting of Fe oxides and hydroxides, and an inner layer enriched in Cr species, while only a Fe-concentrated layer for carbon steel. According to the XPS analysis results, as the pH decreases, more stable and protective Cr oxides are enriched in the film on Cr10Mo1 steel while Fe oxides gradually decompose. Higher content of Cr oxides in the film layer provides Cr10Mo1 corrosion-resistant steel more excellent passivity at lower pH.

Evaluation of dynamic fracture toughness of cold worked 9Cr-1Mo steel

International Nuclear Information System (INIS)

Sathyanarayanan, S.; Sasikala, G.; Ray, S.K.

2004-01-01

Dynamic J-R curves for cold worked 9Cr-1Mo steel have been estimated from instrumented impact test data at ambient temperature on pre-cracked Charpy specimens using three methods of analysis, namely those by Ray et al., Schindler, and Sreenivasan and Mannan. It is concluded that of these three, Schindler's method is the best suited for the purpose since it gives consistent variations with cold work of dynamic J-R curves and dynamic fracture toughness. Cold work results in substantial degradation in dynamic fracture toughness of 9Cr-1Mo steel

Changes in mechanical properties and structure of electrolytic plasma treated X 12 CrNi 18 10 Ti stainless steel

Energy Technology Data Exchange (ETDEWEB)

Kurbanbekov, Sherzod; Baklanov, Viktor; Karakozov, Batyrzhan [Republican State Enterprise National Nuclear Center of Kazakhstan, Kurchatov (Kazakhstan). Inst. of Atomic Energy Branch; Skakov, Mazhyn [Republican State Enterprise National Nuclear Center of Kazakhstan, Kurchatov (Kazakhstan)

2017-05-01

The paper addresses findings regarding the influence of electrolytic plasma treatment on the mechanical properties as well as structural and phase states of X 12 CrNi 18 10 Ti steel. Electrolytic plasma treatment is based on carburizing of stainless steel heated in electrolytes. Treatment of steel samples has been performed as follows: the samples were heated up to a temperature between 850 and 950 C and then they were cured for 7 minutes in an electrolyte of an aqueous solution containing 10 % glycerol (C{sub 3}H{sub 8}O{sub 3}) and 15 % sodium carbonate (Na{sub 2}CO{sub 3}). It is found that, after plasma electrolytic treatment, the surface of X 12 CrNi 18 10 Ti steel had a modified structure and high hardness. Increasing wear resistance of X 12 CrNi 18 10 Ti steel has been observed after carburizing and the coefficient of friction has been reduced. X-ray analysis showed that retained austenite γ-Fe is a main phase, and there are some diffraction lines of orthorhombic Fe{sub 3}C phase as well as Fe{sub 3}O{sub 4} cubic phase. It has been determined, that, after plasma electrolytic treatment, a carbide phase in the modified surface layer, irrespective of the location in the steel structure has the chemical composition Fe{sub 3}C. High concentration of carbon atoms in a solid solution based on γ- and α-iron, a large dislocation density, presence of particles of carbide phase and retained austenite layers have been found.

Ferritic stainless steels: corrosion resistance + economy

International Nuclear Information System (INIS)

Remus, A.L.

1976-01-01

Ferritic stainless steels provide corrosion resistance at lower cost. They include Type 409, Type 439, 18SR, 20-Mo (1.6 Mo), 18-2 (2 Mo), 26-1S, E-Brite 26-1, 29 Cr-4 Mo, and 29 Cr-4 Mo-2 Ni. Their corrosion and mechanical properties are examined. Resistance to stress-corrosion cracking is an advantage compared to austenitic types

The effect of molybdenum on the corrosion behaviour of the high-entropy alloys Co1.5CrFeNi1.5Ti0.5Mox in aqueous environments

International Nuclear Information System (INIS)

Chou, Y.L.; Yeh, J.W.; Shih, H.C.

2010-01-01

The purpose of this study is to investigate the electrochemical properties of the Co 1.5 CrFeNi 1.5 Ti 0.5 Mo x high-entropy alloys in three aqueous environments which simulate acidic, marine, and basic environments at ambient temperature (∼25 o C). The potentiodynamic polarisation curves of the Co 1.5 CrFeNi 1.5 Ti 0.5 Mo x alloys, obtained in aqueous solutions of H 2 SO 4 and NaOH, clearly revealed that the corrosion resistance of the Mo-free alloy was superior to that of the Mo-containing alloys. On the other hand, the lack of hysteresis in cyclic polarisation tests and SEM micrographs confirmed that the Mo-containing alloys are not susceptible to pitting corrosion in NaCl solution.

Effects of Ni and Mo on the microstructure and some other properties of Co-Cr dental alloys

International Nuclear Information System (INIS)

Matkovic, Tanja; Matkovic, Prosper; Malina, Jadranka

2004-01-01

Influences of adding Ni and Mo on the microstructure and properties of as-cast Co-Cr base alloys have been investigated in order to determine the region of their optimal characteristics for biomedical application. The alloys were produced by arc-melting technique under argon atmosphere. Using optical metallography and scanning electron micro analyser it has been established that among 10 samples of Co-Cr-Ni alloys only samples 5 and 9 with the composition Co 55 Cr 40 Ni 5 and Co 60 Cr 30 Ni 10 have appropriate dendritic solidification microstructure. This microstructure, typical for commercial dental alloys, appears and beside greater number of as-cast Co-Cr-Mo alloys. The results of hardness and corrosion resistance measurements revealed the strong influence of different alloy chemistry and of as-cast microstructure. Hardness of alloys decreases with nickel content, but increases with chromium content. Therefore all Co-Cr-Ni alloys have significantly lower hardness than Co-Cr-Mo alloys. Corrosion resistance of alloys in artificial saliva was evaluated on the base of pitting potential. Superior corrosion characteristics have the samples with typical dendritic microstructure and higher chromium content, until nickel content have not significant effect. According to this, in ternary Co-Cr-Ni phase diagram was located the small concentration region (about samples 5 and 9) in them alloy properties can satisfied the high requirements for biomedical applications. This region is considerably larger in Co-Cr-Mo phase diagram

Chemical diffusion of Cr, Ni and Si in welded joints. II

International Nuclear Information System (INIS)

Kucera, J.; Ciha, K.

1987-01-01

The results are given of a study in chemical diffusion in welded joints P2/A and P3/A. P2 stands for the steel (Fe-17.48 Cr-8.15 Ni-0.14 Si), P3 for (Fe-18.52 Cr-8.20 Ni-1.78 Si) and A for the Fe-Arema. Triadic sandwiche-like samples were diffusion heated at temperatures from 920 to 1170 degC. The concentration distributions N(x,t) of the given elements were measured with microprobe JXA-3A. The evaluation of the experimental data was carried out either by Grube's method, or in some cases by the spline-polynomial method. The evaluated diffusivities D-bar satisfy the Arrhenius relation and yield the standard diffusion characteristics D 0 and H. The diffusivities D-bar of Cr, Ni and Si in P1/A, in P2/A and P3/A welded joints vary with Si content in P1, P2 and P3 alloys, similar to the Cr-51 and Ni-63 self-diffusivities in Fe-18 Cr-12 Ni-X Si steels, and tend to increase with increasing Si content. The values D-bar measured in the vicinity of grain boundaries are higher than the bulk diffusion coefficients. The most rapid diffusant is Si and the slowest one Ni. Thus, the relations D-bar Si :D-bar Cr :D-bar Ni ≅ 6:3:1 (P3/A) and D-bar Si :D-bar Cr :D-bar Ni ≅ 1.7:1.4:1 (P3/A) are valid at 1050 degC. Comparing the results with those published if can be noted that the Cr-51 and Ni-63 self-diffusion in Fe-18 Cr-12 Ni-X Si steels is faster than chemical diffusion of these elements in the said steel welded joints P2/A and P3/A; X varies from 0.14 to 1.98. (author). 7 tabs., 7 figs., 20 refs

On phase equilibria in duplex stainless steels

Energy Technology Data Exchange (ETDEWEB)

Wessman, S. [Swerea KIMAB AB, Stockholm (Sweden); Pettersson, R. [Outokumpu Stainless AB, Avesta Research Centre, Avesta (Sweden); Hertzman, S. [Outokumpu Stainless Research Foundation, Stockholm (Sweden)

2010-05-15

The equilibrium conditions of four duplex stainless steels; Fe-23Cr-4.5Ni-0.1N, Fe-22Cr-5.5Ni-3Mo-0.17N, Fe-25Cr-7Ni-4Mo-0.27N and Fe-25Cr-7Ni-4Mo-1W-1.5Cu-0.27N were studied in the temperature region from 700 to 1000 C. Phase compositions were determined with SEM EDS and the phase fractions using image analysis on backscattered SEM images. The results showed that below 1000 C the steels develop an inverse duplex structure with austenite and sigma phase, of which the former is the matrix phase. With decreasing temperature, the microstructure will be more and more complex and finely dispersed. The ferrite is, for the higher alloyed steels, only stable above 1000 C and at lower temperatures disappears in favour of intermetallic phases. The major intermetallic phase is sigma phase with small amounts of chi phase, the latter primarily in high Mo and W grades. Nitrides, not a focus in this investigation, were present as rounded particles and acicular precipitates at lower temperatures. The results were compared to theoretical predictions using the TCFE5 and TCFE6 databases. (Abstract Copyright [2010], Wiley Periodicals, Inc.)

Effect of niobium on the embrittlement of 2.25 Cr and 2.25 Cr-1Mo steels by phosphous

International Nuclear Information System (INIS)

Antunes, J.L.B.

1985-01-01

The influence of niobium on the temper embrittlement of 2.25Cr and 2.25 Cr-1Mo steels doped with phosphorus is evaluated. The transition temperatures of the samples tempered at 650 0 C and aged at different temperatures for niobium steels. (M.J.C.) [pt

Characteristics of Ni-Cr-Fe laser clad layers on EA4T steel

Science.gov (United States)

Chen, Wenjing; Chen, Hui; Wang, Yongjing; Li, Congchen; Wang, Xiaoli

2017-07-01

The Ni-Cr-Fe metal powder was deposited on EA4T steel by laser cladding technology. The microstructure and chemical composition of the cladding layer were analyzed by optical microscopy (OM), scanning electron microscopy (SEM) and X-ray diffraction (XRD). The bonding ability between the cladding layer and the matrix was measured. The results showed that the bonding between the cladding layer and the EA4T steel was metallurgical bonding. The microstructure of cladding layer was composed of planar crystals, columnar crystals and dendrite, which consisted of Cr2Ni3, γ phase, M23C6 and Ni3B phases. When the powder feeding speed reached 4 g/min, the upper bainite occurred in the heat affected zone (HAZ). Moreover, the tensile strength of the joint increased, while the yield strength and the ductility decreased.

Assessment of the integrity of ferritic-austenitic dissimilar weld joints of different grades of Cr-Mo ferritic steels

Energy Technology Data Exchange (ETDEWEB)

Laha, K.; Chandravathi, K.S.; Parameswaran, P.; Goyal, Sunil; Mathew, M.D. [Indira Gandhi Centre for Atomic Research, Kalpakkam (India). Metallurgy and Materials Group

2010-07-01

Integrity of the 2.25 Cr-1Mo / Alloy 800, 9Cr-1Mo / Alloy 800 and 9Cr-1Mo-VNb / Alloy 800 ferritic-austenitic dissimilar joints, fusion welded employing Inconel 182 electrode, has been assessed under creep conditions at 823 K. The dissimilar weld joints displayed lower creep rupture strength than their respective ferritic steel base metals. The strength reduction was more for 2.25Cr-1Mo steel joint and least for 9Cr-1Mo steel joint. The failure location in the joints was found to shift from the ferritic steel base metal to the intercritical region of heat-affected zone (HAZ) in ferritic steel (type IV cracking) with decrease in stress. At still lower stresses the failure occurred at the ferritic / austenitic weld interface. Localized creep deformation and cavitation in the soft intercritical HAZ induced type IV failure whereas creep cavitation at the weld interface particles induced ferritic / austenitic interface cracking due to high creep strength mismatch across it. Micromechanisms of type IV failure and interface cracking in the ferritic / austenitic joints and different susceptibility to failure for different grades of ferritic steels are discussed based on microstructural investigation, mechanical testing and finite element analysis. (Note from indexer: paper contains many typographical errors.)

Effect of Carbon Content on the Microstructure and Mechanical Properties of NbC-Ni Based Cermets

Directory of Open Access Journals (Sweden)

Shuigen Huang

2018-03-01

Full Text Available The aim of this work was to correlate the overall carbon content in NbC-Ni, NbC-Ni-VC and NbC-Ni-Mo starting powders with the resulting microstructure, hardness, and fracture toughness of Ni-bonded NbC cermets. A series of NbC-Ni, NbC-Ni-VC and NbC-Ni-Mo cermets with different carbon content were prepared by conventional liquid phase sintering for 1 h at 1420 °C in vacuum. Microstructural analysis of the fully densified cermets was performed by electron probe microanalysis (EPMA to assess the effect of carbon and VC or Mo additions on the NbC grain growth and morphology. A decreased carbon content in the starting powder mixtures resulted in increased dissolution of Nb, V, and Mo in the Ni binder and a decreased C/Nb ratio in the NbC based carbide phase. The Vickers hardness (HV30 and Palmqvist indentation toughness were found to decrease significantly with an increasing carbon content in the Mo-free cermets, whereas an antagonistic correlation between hardness and toughness was obtained as a function of the Mo-content in Mo-modified NbC cermets. To obtain optimized mechanical properties, methods to control the total carbon content of NbC-Ni mixtures were proposed and the prepared cermets were investigated in detail.

Overview of research trends and problems on Cr-Mo low alloy steels for pressure vessel

International Nuclear Information System (INIS)

Chi, Byung Ha; Kim, Jeong Tae

2000-01-01

Cr-Mo low alloy steels have been used for a long time for pressure vessel due to its excellent corrosion resistance, high temperature strength and toughness. The paper reviewed the latest trends on material development and some problems on Cr-Mo low alloy steel for pressure vessel, such as elevated temperature strength, hardenability, synergetic effect between temper and hydrogen embrittlement, hydrogen attack and hydrogen induced disbonding of overlay weld-cladding

Phase stability, crystal structure and magnetism in (U1-xNbx)2 Ni21B6 and (UyNb1-y)3Ni20B6

Science.gov (United States)

Provino, Alessia; Bhattacharya, Amitava; Dhar, Sudesh K.; Pani, Marcella; Gatti, Flavio; Paudyal, Durga; Manfrinetti, Pietro

Ternary phases with composition T2M21X6 and T3M20X6 (T = transition metal; M = 3 d metal; X = B, C, P) are reported to crystallize with the W2Cr21C6-type and Mg3Ni20B6-type, respectively (ternary ordered derivatives of the cubic Cr23C6-type, cF116). They attract interest due to their refractory, mechanical, and peculiar magnetic properties. Literature data on these compounds only concern apparently stoichiometric 2:21:6 and 3:20:6 phases. Often only nominal composition has been reported, with few structural refinements and no measurements of physical properties. Lack of detailed stoichiometry and crystallographic data does not allow sufficient understanding of the crystal chemistry and properties of these compounds. We studied stability, crystal structure and magnetism of (U1-xNbx)2 Ni21B6 and (UyNb1-y)3Ni20B6; stable phases are U2Ni21B6 and Nb3Ni20B6, as also confirmed by theoretical calculations. The two pristine compounds solubilize Nb and U, respectively, up to a given extent. The substitution of U by Nb leads to a structural change from the W2Cr21C6- to the Mg3Ni20B6-type. While U2Ni21B6 is a Pauli paramagnet (itinerant non-magnetic state of U-5 f electrons), in agreement with literature, magnetization data for (UyNb1-y)3 Ni20B6 show itinerant ferromagnetism with TC >300 K.

Effect of Nb Addition to Ti-Bearing Super Martensitic Stainless Steel on Control of Austenite Grain Size and Strengthening

Science.gov (United States)

Ma, Xiaoping; Langelier, Brian; Gault, Baptiste; Subramanian, Sundaresa

2017-05-01

The role of Nb in normalized and tempered Ti-bearing 13Cr5Ni2Mo super martensitic stainless steel is investigated through in-depth characterization of the bimodal chemistry and size of Nb-rich precipitates/atomic clusters and Nb in solid solution. Transmission electron microscopy and atom probe tomography are used to analyze the samples and clarify precipitates/atom cluster interactions with dislocations and austenite grain boundaries. The effect of 0.1 wt pct Nb addition on the promotion of (Ti, Nb)N-Nb(C,N) composite precipitates, as well as the retention of Nb in solution after cooling to room temperature, are analyzed quantitatively. (Ti, Nb)N-Nb(C,N) composite precipitates with average diameters of approximately 24 ± 8 nm resulting from epitaxial growth of Nb(C,N) on pre-existing (Ti,Nb)N particles, with inter-particle spacing on the order of 205 ± 68 nm, are found to be associated with mean austenite grain size of 28 ± 10 µm in the sample normalized at 1323 K (1050 °C). The calculated Zener limiting austenite grain size of 38 ± 13 µm is in agreement with the experimentally observed austenite grain size distribution. 0.08 wt pct Nb is retained in the as-normalized condition, which is able to promote Nb(C, N) atomic clusters at dislocations during tempering at 873 K (600 °C) for 2 hours, and increases the yield strength by 160 MPa, which is predicted to be close to maximum increase in strengthening effect. Retention of solute Nb before tempering also leads to it preferentially combing with C and N to form Nb(C, N) atom clusters, which suppresses the occurrence of Cr- and Mo-rich carbides during tempering.

Determination of the Fe-Cr-Ni and Fe-Cr-Mo Phase Diagrams at Intermediate Temperatures using a Novel Dual-Anneal Diffusion-Multiple Approach

Science.gov (United States)

Cao, Siwei

Phase diagrams at intermediate temperatures are critical both for alloy design and for improving the reliability of thermodynamic databases. There is a significant shortage of experimental data for phase diagrams at the intermediate temperatures which are defined as around half of the homologous melting point (in Kelvin). The goal of this study is to test a novel dual-anneal diffusion multiple (DADM) methodology for efficient determination of intermediate temperature phase diagrams using both the Fe-Cr-Ni and Fe-Cr-Mo systems as the test beds since both are very useful for steel development. Four Fe-Cr-Ni-Mo-Co diffusion multiples were made and annealed at 1200 °C for 500 hrs. One sample was used directly for evaluating the isothermal sections at 1200 ° C. The other samples (and cut slices) were used to perform a subsequent dual annealing at 900 °C (500 hrs), 800 °C (1000 hrs), 700 °C (1000 hrs), and 600 °C (4500 hrs), respectively. The second annealing induced phase precipitation from the supersaturated solid solutions that were created during the first 1200 °C annealing. Scanning electron microscopy (SEM), electron probe microanalysis (EPMA), electron backscatter diffraction (EBSD), and transmission electron microscopy (TEM) were used to identify the phases and precipitation locations in order to obtain the compositions to construct the isothermal sections of both ternary systems at four different temperatures. The major results obtained from this study are isothermal sections of the Fe-Cr-Ni and Fe-Cr-Mo systems at 1200 °C, 900 °C, 800 °C, and 700 °C. For the Fe-Cr-Ni system, the results from DADMs agree with the majority of the literature results except for results at both 800 °C and 700 °C where the solubility of Cr in the fcc phase was found to be significantly higher than what was computed from thermodynamic calculations using the TCFE5 database. Overall, it seems that the Fe-Cr-Ni thermodynamic assessment only needs slight improvement to

Effects of sodium environment on the mechanical properties of Fe-2 1/4Cr-1Mo steel

International Nuclear Information System (INIS)

Chopra, O.K.

Mechanical property data on isothermally annealed, thermally aged, and sodium-exposed Fe-2 1/4Cr-1Mo steel are analyzed to evaluate the influence of the sodium environment as well as the effects of the microstructural and compositional changes that occur in the steel during long-term exposure to sodium. Correlations are developed to predict the environmental effects on tensile, creep, fatigue, and creep-fatigue properties of Fe-2 1/4Cr-1Mo steel in sodium. The results indicate that at temperatures <823 K (550 deg. C), degradation of mechanical properties is essentially due to thermal aging. Loss of carbon from the steel reduces both the tensile and creep-rupture strength, but has little or no effect on the fatigue properties. The cyclic properties of Fe-2 1/4Cr-1Mo steel in sodium are superior to those in air. The creep-fatigue behaviour in sodium is significantly different from that in an air environment. The creep-fatigue data are analyzed using the interactive damage rate equations to predict the time-dependent fatigue bahaviour of isothermally annealed Fe-2 1/4Cr-1Mo steel in sodium. (author)

Improvement of NiMoNb to polyimide adhesion by inductively coupled nitrogen plasma treatment

Energy Technology Data Exchange (ETDEWEB)

Bang, S.-H., E-mail: zxclucy@snu.ac.kr

2016-01-01

Graphical abstract: - Highlights: • NiMoNb was introduced as the adhesion layer for flexible Cu-clad laminate structure. • The effect of sputtering and plasma power on the peel strength was studied. • Plasma pretreatment in inductively coupled plasma greatly affects the peel strength. • FCCL with NiMoNb adhesion layer show outstanding peel strength. - Abstract: In this study, the effect of sputtering power on the peel strength of the flexible copper clad laminate (FCCL) was evaluated before and after heat treatment using 180° peel test. An increase in the sputtering powers from 200 W to 600 W increased film density and improved peel strength. To enhance peel strength much more, an inductively coupled plasma (ICP) was treated on the PI surface using N{sub 2} gas with Ar as a function of RF power. A dramatic enhancement of the peel strength, 923 N/m was achieved, especially after heat treatment by changing ICP power from 200 W to 900 W. The reduction ratio of the peel strength for the 900 W plasma-treated FCCL was only 12%, whereas that for the 200 W plasma-treated FCCL was 43%. The root mean square (RMS) surface roughness with PIs exposed to both 200 W and 900 W plasma treatments was rarely changed, while X-ray photoelectron spectroscopy (XPS) showed the substantial increase of C–N functional groups. To obtain insight the film characteristics, the NiMoNb/PI interfaces were investigated by a high resolution transmission electron microscopy (HR-TEM).

Design of Novel Precipitate-Strengthened Al-Co-Cr-Fe-Nb-Ni High-Entropy Superalloys

Science.gov (United States)

Antonov, Stoichko; Detrois, Martin; Tin, Sammy

2018-01-01

A series of non-equiatomic Al-Co-Cr-Fe-Nb-Ni high-entropy alloys, with varying levels of Co, Nb and Fe, were investigated in an effort to obtain microstructures similar to conventional Ni-based superalloys. Elevated levels of Co were observed to significantly decrease the solvus temperature of the γ' precipitates. Both Nb and Co in excessive concentrations promoted the formation of Laves and NiAl phases that formed either during solidification and remained undissolved during homogenization or upon high-temperature aging. Lowering the content of Nb, Co, or Fe prevented the formation of the eutectic type Laves. In addition, lowering the Co content resulted in a higher number density and volume fraction of the γ' precipitates, while increasing the Fe content led to the destabilization of the γ' precipitates. Various aging treatments were performed which led to different size distributions of the strengthening phase. Results from the microstructural characterization and hardness property assessments of these high-entropy alloys were compared to a commercial, high-strength Ni-based superalloy RR1000. Potentially, precipitation-strengthened high-entropy alloys could find applications replacing Ni-based superalloys as structural materials in power generation applications.

Nitrided steel 38CrN3MAFA for supporting elements in nuclear power plants; Vysokoazotistaya stal` tipa 38HN3MAFA dlya krepezhnikh detajlej reaktorov AEhS

Energy Technology Data Exchange (ETDEWEB)

Rasheva, I; Argirov, Kh; Stojchev, T [Bylgarska Akademiya na Naukite, Sofia (Bulgaria). Inst. po Metaloznanie i Tekhnologiya na Metalite

1996-12-31

Nitride doping of steel at different concentrations is achieved by counter-pressure casting in nitrogen ambience. A new type of steel is developed containing 0.05-0.2% N{sub 2}. It is compared to a standard 34NiCrMoV145 steel (DIN). The mechanical properties are improved significantly after a two-stage thermal treatment and are as follows: fluidity limit R{sub 0}.2>=1045 MPa, relative elongation A>=15%, relative shortening Z>=62%, impact viscosity KCU >= 1 MJ/m{sup 2}. The quench hardening consists of heating to 800-850{sup o} C in oil and cooling to 600{sup o} C in air. The steel is suitable for rotors, turbines, compressor shafts and reactor supporting elements in nuclear power plants. 3 refs., 6 figs., 6 tabs.

Precipitation Kinetics in a Nb-stabilized Ferritic Stainless Steel

Science.gov (United States)

Labonne, M.; Graux, A.; Cazottes, S.; Danoix, F.; Cuvilly, F.; Chassagne, F.; Perez, M.; Massardier, V.

2017-08-01

The precipitation occurring in a Nb-stabilized ferritic stainless steel, containing initially Nb(C, N) carbonitrides and Fe3Nb3X precipitates, was investigated during aging treatments performed between 923 K and 1163 K (650 °C and 890 °C) by combining different techniques, (thermoelectric power (TEP), scanning/transmission electron microscopy (SEM/TEM), and atom probe tomography (APT)), in order to determine the precipitation kinetics, the nature and morphology of the newly formed precipitates as well as the chemistry of the initial Fe3Nb3X precipitates, where X stands for C or N. The following composition was proposed for these precipitates: (Fe0.81 Cr0.19)3 (Nb0.85 Si0.08 Mo0.07)3 (N0.8 C0.2), highlighting the simultaneous presence of N and C in the precipitates. With regard to the precipitation in the investigated temperature range, two main phenomena, associated with a hardness decrease, were clearly identified: (i) the precipitation of Fe2Nb precipitates from the niobium initially present in solution or coming from the progressive dissolution of the Fe3Nb3X precipitates and (ii) the precipitation of the χ-phase at grain boundaries for longer aging times. From the TEP kinetics, a time-temperature-precipitation diagram has been proposed.

PERSISTENT CURRENT EFFECT IN 15-16 T NB3SN ACCELERATOR DIPOLES AND ITS CORRECTION

Energy Technology Data Exchange (ETDEWEB)

Kashikhin, V. V. [Fermilab; Zlobin, A. V. [Fermilab

2016-11-08

Nb3Sn magnets with operating fields of 15-16 T are considered for the LHC Energy Doubler and a future Very High Energy pp Collider. Due to large coil volume, high critical current density and large superconducting (SC) filament size the persistent current effect is very large in Nb3Sn dipoles al low fields. This paper presents the results of analysis of the persistent current effect in the 15 T Nb3Sn dipole demonstrator being developed at FNAL, and describes different possibilities of its correction including passive SC wires, iron shims and coil geometry.

Creep behaviour of the alloys NiCr22Co12Mo and 10CrMo9 10 under static and cyclic load conditions

International Nuclear Information System (INIS)

Wolf, H.

1990-01-01

The creep behaviour of NiCr20Co12Mo is investigated under static strain and at 800deg C, with stresses applied ranging from 105 MPa to 370 MPa. The ferritic steel 10CrMo 9 10 is tested for its creep behaviour under static strain and at the temperatures of 600deg C and 550deg C, with stresses applied between 154 MPa and 326 MPa (at 600deg C), or between 250 MPa and 458 MPa (at 550deg C). The experiments are made to determine the effects of changes in strain on the materials' deformation behaviour, placing emphasis on transient creep and elastic or anelastic response. The mean internal stress is determined from changes in strain. Cyclic creep is analysed as a behaviour directly responding to the pattern of change in strain. Effects of certain strain changes not clarified so far are analysed. The cyclic strain experiments are analysed according to the velocity factor concept. The usual models of creep deformation (theta projection concept) are compared with the model of effective strain, which is based on the fundamental equation of plastic deformation by dislocation motion (Orowan equation). (MM) [de

Martensite shear phase reversion-induced nanograined/ultrafine-grained Fe-16Cr-10Ni alloy: The effect of interstitial alloying elements and degree of austenite stability on phase reversion

Energy Technology Data Exchange (ETDEWEB)

Misra, R.D.K., E-mail: dmisra@louisiana.edu [Center for Structural and Functional Materials, University of Louisiana at Lafayette, Madison Hall Room 217, P.O. Box 44130, Lafayette, LA 70504-1430 (United States); Zhang, Z.; Venkatasurya, P.K.C. [Center for Structural and Functional Materials, University of Louisiana at Lafayette, Madison Hall Room 217, P.O. Box 44130, Lafayette, LA 70504-1430 (United States); Somani, M.C.; Karjalainen, L.P. [Department of Mechanical Engineering, University of Oulu, P.O. Box 4200, Oulu 90014 (Finland)

2010-11-15

Research highlights: {yields} Development of a novel process involving phase-reversion annealing process. {yields} Austensite stability strongly influences development of nanograined structure. {yields} Interstitial elements influence microstructural evolution during annealing. - Abstract: We describe here an electron microscopy study of microstructural evolution associated with martensitic shear phase reversion-induced nanograined/ultrafine-grained (NG/UFG) structure in an experimental Fe-16Cr-10Ni alloy with very low interstitial content. The primary objective is to understand and obtain fundamental insights on the influence of degree of austenite stability (Fe-16Cr-10Ni, 301LN, and 301 have different austenite stability index) and interstitial elements (carbon and nitrogen) in terms of phase reversion process, microstructural evolution during reversion annealing, and temperature-time annealing sequence. A relative comparison of Fe-16Cr-10Ni alloy with 301LN and 301 austenitic stainless steels indicated that phase reversion in Fe-16Cr-10Ni occurred by shear mechanism, which is similar to that observed for 301, but is different from the diffusional mechanism in 301LN steel. While the phase reversion in the experimental Fe-16Cr-10Ni alloy and 301 austenitic stainless steel occurred by shear mechanism, there were fundamental differences between these two alloys. The reversed strain-free austenite grains in Fe-16Cr-10Ni alloy were characterized by nearly same crystallographic orientation, where as in 301 steel there was evidence of break-up of martensite laths during reversion annealing resulting in several regions of misoriented austenite grains in 301 steel. Furthermore, a higher phase reversion annealing temperature range (800-900 deg. C) was required to obtain a fully NG/UFG structure of grain size 200-600 nm. The difference in the phase reversion and the temperature-time sequence in the three stages is explained in terms of Gibbs free energy change that

On the effect of niobium on the properties of welded joints in the 2.25% Cr-1% Mo type steel with nickel and niobium additions

International Nuclear Information System (INIS)

Matusek, P.; Gladis, R.; Walder, V.

The effects were studied of the chemical composition of the base material and of welding parameters on the properties of welded joints of steel 08Cr2.25Mo1NiNb for fast reactor steam generators. Welding was done using Boehler-Fox electrodes and electrodes developed in Czechoslovakia. Testing revealed that the welded joint hardened and embrittled depending on the content of free niobium. The occurrence of eutectic formation of a general composition of Nbsub(m)Xsub(n) and possible of the Fe 2 Nb phase was considered to be one of the possible unfavourable microstructural factor which affects the mechanical properties of the thermally affected zone. The effect of the cooling rate Δtausub(8/5), ie., the effect of welding technologies was also found to be a function of the free niobium content. The results of welded joint creep to the fracture showed that until the 2x10 4 fracture time no negative effect of the welding cycle on the welded joint refractoriness was found. (B.S.)

Structure and delayed failure behaviour of 0.25C-Ni-Cr-Mo-V steel

International Nuclear Information System (INIS)

Kang, C.H.; Maeng, S.C.

1980-01-01

Delayed failure behaviour of the different transformation structures of 0.25C-2.5Ni-2.5Cr-0.5Mo-0.1V low alloy steel has been studied. The studied microstructures are martensite, lower bainite, and mixed structure of 50% martensite and 50% lower bainite. All these structures have been tempered at 450 deg C for 40 min to have the same tensile strength level of 143 kg/mm 2 . Delayed failure testing has been carried out with cantilever bend tester, in distilled water at 25 deg C. By comparing K 1 sub(scc) values, lower bainitic structure has shown the highest value, although it is only slightly higher than that of the martensitic structure. Mixed structure has the lowest resistance to delayed failure. The fracture modes of both martensitic and mixed structures have been observed as intergranular. In the martensitic structure, however, it is noticeable that there is a larger amount of ductile tearing between intergranular facets. The fracture mode of lower bainitic structure is the mixed topography of microplastic tearing and microvoid coalescence. The above experimental results are discussed in terms of Oriani's decohesion theory of hydrogen embrittlement. The lowest resistance of the mixed structure to delayed failure may be due to the enhanced decohesion by hydrogen at the phase boundaries of martensite and lower bainite. (author)

Corrosion resistance of stainless steels and high Ni-Cr alloys to acid fluoride wastes

International Nuclear Information System (INIS)

Smith, H.D.; Mackey, D.B.; Pool, K.H.; Schwenk, E.B.

1992-04-01

TRUEX processing of Hanford Site waste will utilize potentially corrosive acid fluoride processing solutions. Appropriate construction materials for such a processing facility need to be identified. Toward this objective, candidate stainless steels and high Ni-Cr alloys have been corrosion tested in simulated acid fluoride process solutions at 333K. The high Ni-Cr alloys exhibited corrosion rates as low as 0.14 mm/y in a solution with an HF activity of about 1.2 M, much lower than the 19 to 94 mm/y observed for austenitic stainless steels. At a lower HF activity (about 0.008 M), stainless steels display delayed passivation while high Ni-Cr alloys display essentially no reaction

Microstructure and Properties of the Interface Area in the Laser Cladded Ni Based Coatings on the 1Cr10Mo1NiWVNbN Steel

Directory of Open Access Journals (Sweden)

Yunxia Chen

2017-05-01

Full Text Available The Ni-based coatings were deposited on the 1Cr10Mo1NiWVNbN steel by using laser cladding process. The microstructure and properties of the coatings interface area were investigated by OM (Optical Microscopy, SEM (Scanning Electron Microscope, XRD (X-Ray Diffraction microhardness test and EDS (Energy Spectrum Analysis analysis. The results show that the bonding condition of the coatings interface is different in the monolayer and the trilayer. The monolayer coatings have a small dilution area. The dilution rate in a coating layer increases by layers. The scale of ferrite (α phase increases with the layer increases. The surface cladding quality of a monolayer is better than that of the trilayer coatings. The width of the interface increases with the increase of the layer. The width of the interface region in the trilayer coatings increases significantly. The microhardness of the interface zone is much higher than that in the coatings zone and the substrate zone. The microhardness of trilayer coatings is higher than that of the monolayer.

Properties of the passive films on Ni-Cr-Mo alloys

International Nuclear Information System (INIS)

Lloyd, A.C.; Noel, J.J.; McIntyre, N.S.; Shoesmith, D.W.

2003-01-01

Ni-Cr-Mo alloys are among the most corrosion resistant materials known, showing exceptional localized corrosion resistance under extreme industrial conditions. Accordingly, one such alloy, Alloy-22. is a candidate material for the outer sheathing of nuclear waste packages for the Yucca Mountain repository. Nevada, USA. We briefly report our results on the passive behaviour for a series of Ni-Cr-Mo alloys, with the emphasis on determining if there is a temperature dependence associated with it. The change of passive corrosion rate with temperature is a critical parameter required for long-term performance assessment calculations. The results show that alloy C22 performed better than the other members of the C-series of alloys under acidic conditions. This indicates that its selection as a waste package material is appropriate, and that it possess the potential for long-term containment of radio-nuclides. (author)

A survey of the mechanical properties of uranium alloys U-5Mo-3Nb wt.% and U-3Mo-3Nb wt.%

Energy Technology Data Exchange (ETDEWEB)

Dupont, G.

1969-04-15

In a continuing program on the development of soft and ductile uranium alloys for armament applications, two compositions were studied. These gamma extruded uranium alloys were U-5Mo-3Nb wt.% and U-3Mo-3Nb wt.%. This study was carried out to determine the influence of tempering heat treatments associated with extrusion on the ductility of these uranium alloys. The mechanical properties of both alloys were measured in the extruded condition, in the extruded and annealed condition and in the quenched and tempered condition. A maximum elongation of 13.7% in tension with a low amount of work hardening was obtained for the U-3Mo-3Nb wt.% alloy after 1 1/2 hours anneal at 1200 deg F (650 deg C) followed by a rapid cooling in water at 70 deg F (21 deg C). A maximum elongation of 17.3% with a large amount of work hardening was obtained for alloy U-5Mo-3Nb wt.% after vacuum annealing, normalizing, gamma phase solubilizing at 1500 deg F (815 deg C) and quenching in water at 700 deg F (210 deg C). The maximum ductility achieved in these two alloys by our approaches is low compared with the ductility of Armco Iron employed for the same applications in the field of ballistics.

Effect of heat treatment on the microstructure change and mechanical properties for the Ni-19Si-3Nb-0.15B intermetallic alloy

International Nuclear Information System (INIS)

Jang, J.S.C.; Chang, L.J.

2003-01-01

The microstructural change of the Ni-19Si-3Nb-0.15B alloys after different heat treatment was examined by scanning electron microscopy with energy dispersive spectrum. In addition, Vickers's hardness test was used to measure the variation of mechanical properties for each heat-treated alloy. The results reveal that the typical dendritic microstructure of the heat-treated alloys (comprised of dendritic β-phase, α-β eutectic, and the Nb-rich precipitates) remained almost the same microstructure as the as-cast alloy. However, the morphology of the sharp-edged Nb-rich precipitate (identified to be the cubic Nb 3 Ni 2 Si by electron diffraction of TEM) would be blunted by homogenization. In addition, the size of precipitates seemed to grow with increased aging temperature and aging time. Correlating the result of microhardness measurement with the microstructure observation, an aging temperature of 700 deg. C and an aging time of 10 h is found to be the optimum treating condition for the Ni-19Si-3Nb-0.15B alloy. In addition, the precipitate growth is revealed dominating by an interfacial-controlled kinetics with a thermal activation process of Arrhenius type. The strengthening effect of the heat treatment is not obvious from the hardness test. However, the effect of heat treatment exhibited significant improvement on the ductility of the Ni-19Si-3Nb-0.15B alloy (ε ∼3% for as-cast alloy and 12% for heat-treated alloy)

The use of extraction and electronic diffraction replicas for precipitates characterization in welded Cr-Mo Steels

International Nuclear Information System (INIS)

Gutierrez de Saiz-Solabarria, S.; San Juan Nunez, J.M.

1997-01-01

The precipitates and phases found in the structure of welded joints of Heat Interchanges Tubes were studied and identified. The base material satisfied the requirements of ASME Sec II, SA 213 Gr T22 (2 1/4 Cr 1 Mo). Compositions of Filler Metals were: 2 1/4 Cr 1 Mo and 2 1/4 Cr 1 Mo 1/4 Nb. The chemical composition of base and weld materials were analyzed by atomic emission spectroscopy in high vacuum electric discharge and by inductive plasma coupled. For the constituents characterization extraction and diffraction microscopy replicas were used. (Author) 65 refs

Tantalum-containing Z-phase in 12%Cr martensitic steels

DEFF Research Database (Denmark)

Danielsen, Hilmar Kjartansson; Hald, John

2009-01-01

Z-phases in tantalum-containing 12%Cr steels have been investigated. In 12%Cr steel without any Nb or V, the formation of CrTaN Z-phases was observed. In 12%Cr steel which also contained V, the Ta entered Z-phase as a minor element, Cr(V,Ta)N. The crystal structure of Cr(V,Ta)N seems to be identi......Z-phases in tantalum-containing 12%Cr steels have been investigated. In 12%Cr steel without any Nb or V, the formation of CrTaN Z-phases was observed. In 12%Cr steel which also contained V, the Ta entered Z-phase as a minor element, Cr(V,Ta)N. The crystal structure of Cr(V,Ta)N seems...

Fe3Nb3N precipitates of the Fe3W3C type in Nb stabilized ferritic stainless steel

International Nuclear Information System (INIS)

Malfliet, A.; Van den Broek, W.; Chassagne, F.; Mithieux, J.-D.; Blanpain, B.; Wollants, P.

2011-01-01

Highlights: → The precipitation in Nb stabilized ferritic stainless steel at 950 deg. C is investigated. → We characterized the Fe 3 Nb 3 X precipitates with SAED, EELS, WDS and AES. → We found that Fe 3 Nb 3 X precipitates are stabilized by N and not by C or O. → This insight is new and important for future development of this type of steel grade. - Abstract: A Nb stabilized ferritic stainless steel with 0.45 wt.%Nb, 82 ppm C and 170 ppm N is investigated to reveal the nature of the precipitates present at 950 deg. C. In particular, Fe 3 Nb 3 X precipitates of the Fe 3 W 3 C type are analyzed with WDS and EELS to determine the light elements X stabilizing this phase in the steel. According to WDS on large precipitates after 500 h at 950 deg. C, the Fe 3 Nb 3 X phase contains 10.4 at.% N, 1.2 at.% O and 1.0 at.% C. Auger Electron Spectroscopy on the same precipitates confirms the presence of N. In addition, it is revealed that the C and O peaks observed with WDS result from surface contamination as they disappear after Ar sputtering. The presence of a N peak in the EELS spectra of small Fe 3 Nb 3 X precipitates which have formed after 6 min at 950 deg. C indicate that N stabilizes this phase already from the initial precipitation stage. With this analysis it is demonstrated that N is an effective stabilizer of Fe 3 Nb 3 X precipitates in ferritic stainless steels. The formation of this phase should therefore be considered when predicting the precipitation behavior of Nb in industrial Nb stabilized ferritic stainless steels containing residual N.

Kinetics of phase transformations of undercooled austenite in 18CrNiMo7-6 steel applied for toothed wheels

Directory of Open Access Journals (Sweden)

J. Krawczyk

2010-07-01

Full Text Available Toothed wheels constitute essential part of the steel structural elements market. The most often hypereutectoid structural steels forcarburizing are used for toothed wheels. The final producers of toothed wheels are not demanding regarding a microstructure, providedthat the determined requirements will be fulfilled (e.g. metallurgical purity determined by ultrasounds. Therefore delivered forgings can be in an annealed or quenched state. This results from the situation that the final heat treatment or heat-chemical one is being done at one of the last stages of the toothed wheel production. An essential factor allowing to develop the proper heat treatment is the knowledge of the kinetics of phase transformations of undercooled austenite and its relating to technological conditions, being at the producer disposal, as well as to forging dimensions. Such investigations should be carried out on real melts used for forgings for toothed wheels production together with an analysis of microstructure changes on the forging cross-section. They should be based on calculation methods determining the distribution of cooling rates on its cross-section in dependence of an applied cooling medium.The mentioned above problems in relation to 18CrNiMo7-6 steel - are elucidated in this paper. The aim of the investigations wasthe description of the kinetics of phase transformations of undercooled austenite in this steel. The CCT diagram was constructed for the austenitizing temperature determined on the basis of phase transformations temperatures (the so-called critical points.

Corrosion critique of the 2 1/4 Cr--1 Mo steel for LMFBR steam generation system applications

International Nuclear Information System (INIS)

Zima, G.E.

1977-07-01

The unstabilized ferritic steel of nominal composition, 2 1 / 4 Cr-1Mo, has been proposed for critical structural assignments in LMFBR powerplants, specifically: the tubing, tubesheet and shell of the evaporator and superheater components. The interest in this steel has been based on a presumably favorable general corrosion property spectrum, acceptable mechanical properties and fabricability, and certain economies associated with the low alloy content. This report is an attempt at a general corrosion assessment for the 2 1 / 4 Cr-1Mo steel and an identification of corrosion problem areas potential to this steel from the sodium and water/steam systems of the proposed working environment. There is a considerable area of uncertainty in the sodium-side response of 2 1 / 4 Cr-1Mo steel, centered in the loss and redisposition of carbon during long-term exposure to sodium of various impurity backgrounds. It is submitted that present evidence relating to the water/steam-side corrosion behavior of the 2 1 / 4 Cr-1Mo steel, under nominal and conceivable perturbed environmental conditions, constitutes the principal concern for the proposed LMFBR powerplant applications of this steel. It is suggested that this unfavorable corrosion aspect represents an inherent limitation of the low alloy content of this steel, probably largely independent of melting and processing recourses, and it is a sufficient basis to question the incentive for a continuation of the collateral studies of this steel for the proposed LMFBR steam generation system assignments

Study on elevated-temperature flow behavior of Ni-Cr-Mo-B ultra-heavy-plate steel via experiment and modelling

Science.gov (United States)

Gao, Zhi-yu; Kang, Yu; Li, Yan-shuai; Meng, Chao; Pan, Tao

2018-04-01

Elevated-temperature flow behavior of a novel Ni-Cr-Mo-B ultra-heavy-plate steel was investigated by conducting hot compressive deformation tests on a Gleeble-3800 thermo-mechanical simulator at a temperature range of 1123 K–1423 K with a strain rate range from 0.01 s‑1 to10 s‑1 and a height reduction of 70%. Based on the experimental results, classic strain-compensated Arrhenius-type, a new revised strain-compensated Arrhenius-type and classic modified Johnson-Cook constitutive models were developed for predicting the high-temperature deformation behavior of the steel. The predictability of these models were comparatively evaluated in terms of statistical parameters including correlation coefficient (R), average absolute relative error (AARE), average root mean square error (RMSE), normalized mean bias error (NMBE) and relative error. The statistical results indicate that the new revised strain-compensated Arrhenius-type model could give prediction of elevated-temperature flow stress for the steel accurately under the entire process conditions. However, the predicted values by the classic modified Johnson-Cook model could not agree well with the experimental values, and the classic strain-compensated Arrhenius-type model could track the deformation behavior more accurately compared with the modified Johnson-Cook model, but less accurately with the new revised strain-compensated Arrhenius-type model. In addition, reasons of differences in predictability of these models were discussed in detail.

High Temperature Behavior of Cr3C2-NiCr Coatings in the Actual Coal-Fired Boiler Environment

Science.gov (United States)

Bhatia, Rakesh; Sidhu, Hazoor Singh; Sidhu, Buta Singh

2015-03-01

Erosion-corrosion is a serious problem observed in steam-powered electricity generation plants, and industrial waste incinerators. In the present study, four compositions of Cr3C2-(Ni-20Cr) alloy coating powder were deposited by high-velocity oxy-fuel spray technique on T-91 boiler tube steel. The cyclic studies were performed in a coal-fired boiler at 1123 K ± 10 K (850 °C ± 10 °C). X-ray diffraction, scanning electron microscopy/energy dispersive X-ray analysis and elemental mapping analysis techniques were used to analyze the corrosion products. All the coatings deposited on T-91 boiler tube steel imparted hot corrosion resistance. The 65 pctCr3C2 -35 pct (Ni-20Cr)-coated T-91 steel sample performed better than all other coated samples in the given environment.

Formability of high-alloy dual-phase Cr-Ni steels

International Nuclear Information System (INIS)

Elfmark, J.

2004-01-01

The formability of dual-phase high-alloy Cr-Ni steel within the temperature range from 900 to 1250 C was studied using laboratory tensile and torsion tests. The dual-phase steels on 24% Cr basis are characterized by poor hot formability due to very low stable deformation values and slow recrystallization. Mathematical description of deformation stability exhaustion was derived, as well as a model of formability control based on analysis of the gradual diffuse deformation stability from the stability limit to the moment when the deformation starts to concentrate in a small volume of the test piece. Rolling simulation of dual-phase steel strip was used as an example demonstrating the draught scheme optimization technique which avoids the danger of crack occurrence during the rolling of dual-phase steel strip. (orig.)

Irradiation hardening of Mod.9Cr-1Mo steel

International Nuclear Information System (INIS)

Ryu, Woo-Seog; Kim, Sung-Ho; Choo, Kee-Nam; Kim, Do-Sik

2009-01-01

An irradiation test of Mod.9Cr-1Mo steel was carried out in the OR5 test hole of HANARO of a 30 MW thermal power at 390±10degC up to a fast neutron fluence of 4.4x10 19 (n/cm 2 ) (E > 1.0 MeV). The dpa of the irradiated specimens was evaluated to be 0.034 - 0.07. Tensile and impact tests of the irradiated Mod.9Cr-1Mo were done in the hot cell of the IMEF. The change of the tensile strength by irradiation was similar to the change of the yield strength. The increase of the yield and tensile strengths was up to 18% and 10% respectively. The elongation reduction of the weldment was up to 65%. (author)

Comparative studies on ultrasonic, friction, laser and resistance pressure welding of NiTi shape memory alloys with high-alloy steels. Final report; Vergleichende Untersuchungen zum Ultraschall-, Reib-, Laserstrahl- und Widerstandspressschweissen von NiTi-Shape-Memory-Metall mit hochlegierten Staehlen. Abschlussbericht

Energy Technology Data Exchange (ETDEWEB)

Zuckschwerdt, K.

2000-04-01

The suitability of different welding techniques for welding of NiTi shape memory alloys with high-alloy steel (C12CrNi17-7, X5CrNiNb19-9, X20Cr13) was investigated. The quality of the welds was analyzed using mechanical-technological, fractographic, metallographic and electron microscopy analysis. [German] Ziel dieses Forschungsvorhabens ist es, die Eignung der einzelnen Schweissverfahren fuer das Fuegen von NiTi-Formgedaechtnislegierungen mit hochlegiertem Stahl (X12CrNi17-7, X5CrNiNb19-9, X20Cr13) darzustellen und zu beurteilen. Die Qualitaet der Fuegeverbindungen wird mit Hilfe mechanisch-technologischer, fraktographischer, metallographischer und elektronenmikroskopischer Untersuchungen bewertet.

Microstructure and phase transformations in laser clad CrxSy/Ni coating on H13 steel

Science.gov (United States)

Lei, Yiwen; Sun, Ronglu; Tang, Ying; Niu, Wei

2015-03-01

Laser cladding was carried out onto H13 steel with preplaced NiCrBSi+Ni/MoS2 powders using CO2 laser under the optimized experimental parameters of laser power 2 kW, scanning velocity 6 mm/s and laser beam diameter 3 mm. An X-ray diffractometer and scanning electron microscope with energy dispersive spectroscopy were applied to analyze the microstructure and phase compositions of the coating. Thermodynamic calculation was performed with Thermo-Calc software on the basis of a commercially available Ni-based Alloys' database. The experimental results show that MoS2 decomposed and S reacted with Cr to form nonstoichiometric CrxSy during the laser cladding process. The coating consists of spherical CrxSy particles, primary γ-Ni dendrite, interdendritic eutectic (γ-Ni+NiMo) and precipitated NiMo. The precipitated NiMo was fine and uniformly distributed in primary γ-Ni dendrite. The calculated results and experimental data indicate that the solidification process in the coating during laser cladding process was liquid→liquid+CrxSy→ liquid+CrxSy+γ-Ni→liquid+CrxSy+γ-Ni+ eutectic (γ-Ni+NiMo). A solid state phase transformation (fine and uniformly distributed NiMo precipitated from γ-Ni) occurred after the solidification process. The calculations agree well with the experimental data and it is helpful to understand the phase transformation and microstructure evolution in the coating.

Alloying and heat treatment optimization of Fe/Cr/C steels for improved mechanical properties

International Nuclear Information System (INIS)

Sarikaya, M.

1979-06-01

The effects of alloying elements and heat treatments on the microstructural changes and strength-toughness properties were investigated in optimization of vacuum melted Fe/Cr/C base steels. The structure of the steels in the as-quenched conditions consisted of highly dislocated autotempered lath martensite (strong phase) and thin continuous interlath films of retained austenite (tough phase). It has been emphasized again that the mechanical properties of the steels are sensitive to the amount and the stability of retained austenite. To increase the stability of retained austenite in the as-quenched condition 2 w/o Mn or 2 w/o Ni was added to the base steel, viz., Fe/3Cr/0.3C. Partial replacement of Cr by about 0.5 w/o Mo did not alter the beneficial microstructure

Investigation on hole manufacture in 42CrMo4 steel using 3-flute carbide drills and 6-flute cermet reamers

DEFF Research Database (Denmark)

Müller, Pavel; De Chiffre, Leonardo

2009-01-01

An investigation on cutting forces and hole quality using carbide 3-flute self-centering drills and 6-flute cermet reamers was performed on 42CrMo4 alloy steel. Different depths of cuts were analyzed with respect to cutting thrust and cutting torque, hole diameter, form and surface integrity. Goo...

Effect of titanium on the creep deformation behaviour of 14Cr-15Ni-Ti stainless steel

Science.gov (United States)

Latha, S.; Mathew, M. D.; Parameswaran, P.; Nandagopal, M.; Mannan, S. L.

2011-02-01

14Cr-15Ni-Ti modified stainless steel alloyed with additions of phosphorus and silicon is a potential candidate material for the future cores of Prototype Fast Breeder Reactor. In order to optimise the titanium content in this steel, creep tests have been conducted on the heats with different titanium contents of 0.18, 0.23, 0.25 and 0.36 wt.% at 973 K at various stress levels. The stress exponents indicated that the rate controlling deformation mechanism was dislocation creep. A peak in the variation of rupture life with titanium content was observed around 0.23 wt.% titanium and the peak was more pronounced at lower stresses. The variation in creep strength with titanium content was correlated with transmission electron microscopic investigations. The peak in creep strength exhibited by the material with 0.23 wt.% titanium is attributed to the higher volume fraction of fine secondary titanium carbide (TiC) precipitates.

Effect of titanium on the creep deformation behaviour of 14Cr-15Ni-Ti stainless steel

Energy Technology Data Exchange (ETDEWEB)

Latha, S. [Metallurgy and Materials Group, Indira Gandhi Centre for Atomic Research, Kalpakkam, Tamil Nadu 603 102 (India); Mathew, M.D., E-mail: mathew@igcar.gov.in [Metallurgy and Materials Group, Indira Gandhi Centre for Atomic Research, Kalpakkam, Tamil Nadu 603 102 (India); Parameswaran, P.; Nandagopal, M. [Metallurgy and Materials Group, Indira Gandhi Centre for Atomic Research, Kalpakkam, Tamil Nadu 603 102 (India); Mannan, S.L. [National Engineering College, Kovilpatti, Tamil Nadu 628 503 (India)

2011-02-28

14Cr-15Ni-Ti modified stainless steel alloyed with additions of phosphorus and silicon is a potential candidate material for the future cores of Prototype Fast Breeder Reactor. In order to optimise the titanium content in this steel, creep tests have been conducted on the heats with different titanium contents of 0.18, 0.23, 0.25 and 0.36 wt.% at 973 K at various stress levels. The stress exponents indicated that the rate controlling deformation mechanism was dislocation creep. A peak in the variation of rupture life with titanium content was observed around 0.23 wt.% titanium and the peak was more pronounced at lower stresses. The variation in creep strength with titanium content was correlated with transmission electron microscopic investigations. The peak in creep strength exhibited by the material with 0.23 wt.% titanium is attributed to the higher volume fraction of fine secondary titanium carbide (TiC) precipitates.

Effect of titanium on the creep deformation behaviour of 14Cr-15Ni-Ti stainless steel

International Nuclear Information System (INIS)

Latha, S.; Mathew, M.D.; Parameswaran, P.; Nandagopal, M.; Mannan, S.L.

2011-01-01

14Cr-15Ni-Ti modified stainless steel alloyed with additions of phosphorus and silicon is a potential candidate material for the future cores of Prototype Fast Breeder Reactor. In order to optimise the titanium content in this steel, creep tests have been conducted on the heats with different titanium contents of 0.18, 0.23, 0.25 and 0.36 wt.% at 973 K at various stress levels. The stress exponents indicated that the rate controlling deformation mechanism was dislocation creep. A peak in the variation of rupture life with titanium content was observed around 0.23 wt.% titanium and the peak was more pronounced at lower stresses. The variation in creep strength with titanium content was correlated with transmission electron microscopic investigations. The peak in creep strength exhibited by the material with 0.23 wt.% titanium is attributed to the higher volume fraction of fine secondary titanium carbide (TiC) precipitates.

Strain rate effects in nuclear steels at room and higher temperatures

Energy Technology Data Exchange (ETDEWEB)

Solomos, G. E-mail: george.solomos@jrc.it; Albertini, C.; Labibes, K.; Pizzinato, V.; Viaccoz, B

2004-04-01

An investigation of strain rate, temperature and size effects in three nuclear steels has been conducted. The materials are: ferritic steel 20MnMoNi55 (vessel head), austenitic steel X6CrNiNb1810 (upper internal structure), and ferritic steel 26NiCrMo146 (bolting). Smooth cylindrical tensile specimens of three sizes have been tested at strain rates from 0.001 to 300 s{sup -1}, at room and elevated temperatures (400-600 deg. C). Full stress-strain diagrams have been obtained, and additional parameters have been calculated based on them. The results demonstrate a clear influence of temperature, which amounts into reducing substantially mechanical strengths with respect to RT conditions. The effect of strain rate is also shown. It is observed that at RT the strain rate effect causes up shifting of the flow stress curves, whereas at the higher temperatures a mild downshifting of the flow curves is manifested. Size effect tendencies have also been observed. Some implications when assessing the pressure vessel structural integrity under severe accident conditions are considered.

Potentiodynamic polarization studies of bulk amorphous alloy Zr57Cu15.4Ni12.6Al10Nb5 and Zr59Cu20Ni8Al10Ti3 in aqueous HNO3 media

International Nuclear Information System (INIS)

Sharma, Poonam; Dhawan, Anil; Jayraj, J.; Kamachi Mudali, U.

2013-01-01

The potentiodynamic polarization studies were carried out on Zr based bulk amorphous alloy Zr 57 Cu 15.4 Ni 12.6 Al 10 Nb 5 and Zr 59 Cu 20 Ni 8 Al 10 Ti 3 in solutions of 1 M, 6 M and 11.5 M HNO 3 aqueous media at room temperature. As received specimens of Zr 57 Cu 15.4 Ni 12.6 Al 10 Nb 5 (5 mm diameter rod) and Zr 59 Cu 20 Ni 8 Al 10 Ti 3 (3 mm diameter rod) were polished with SiC paper before testing them for potentiodynamic polarization studies. The amorphous nature of the specimens was checked by X-ray diffraction. The bulk amorphous alloy Zr 59 Cu 20 Ni 8 Al 10 Ti 3 shows the better corrosion resistance than Zr 57 Cu 15.4 Ni 12.6 Al 10 Nb 5 alloy in the aqueous HNO 3 media as the value of the corrosion current density (I corr ) for Zr 57 Cu 15.4 Ni 12.6 Al 10 Nb 5 alloy were found to be more than Zr 59 Cu 20 Ni 8 Al 10 Ti 3 alloy in aqueous HNO 3 media. The improved corrosion resistance of Zr 59 Cu 20 Ni 8 Al 10 Ti 3 alloy is possibly due to the presence of Ti and formation of TiO 2 during anodic oxidation. Both Zr based bulk amorphous alloys shows wider passive range at lower concentration of nitric acid and the passive region gets narrowed down with the increase in concentration. A comparison of data obtained from both the Zr-based bulk amorphous alloys is made and results are discussed in the paper. (author)

Carbon transfer between 2 1/4 Cr 1 Mo alloy and austenitic steels (experiments in anisothermal loops)

International Nuclear Information System (INIS)

Baque, P.; Besson, M.; Champeix, L.; Donati, J.R.; Oberlin, C.; Saint-Paul, P.

1976-01-01

Studies on carbon transfer between the ferritic steel 2 1/4 Cr 1 Mo and the austenitic steels 316L and 321H have shown that there is not any measurable carbon transfer in the operating conditions of the secondary circuit of PHENIX (475 deg C was the maximal temperature of the 2 1/4 Cr 1 Mo steel). A significant carbon transfer has been observed between the ferritic steel and the 316L steel when the 321H was replaced by the 2 1/4 Cr 1 Mo steel in the same thermohydraulic conditions (the ferritic steel was then used up to 545 deg C). This experiment has demonstrated the importance of the temperature and the initial carbon content of the ferritic steel as parameters in the decarburization process. It appears that decarburization may not be sensitive to the thermohydraulic conditions at least in the range investigated in those experiments. In the other hand the 316L steel is observed to have been carburized, the degree of carburization remaining appreciably constant and independent on the temperature between 400 deg C and 550 deg C [fr

Reheat cracking susceptibility of P23 (7CrWVMoNb9-6) steel welds made using matching and mis-matching filler metals

Energy Technology Data Exchange (ETDEWEB)

Nevasmaa, Pekka; Salonen, Jorma; Auerkari, Pertti; Rantala, Juhani; Holmstroem, Stefan [VTT Technical Research Centre of Finland, Espoo (Finland)

2010-07-01

Reheat cracking sensitivity of 7CrWVMoNb9-6 (P23) thick-section multipass welds has been investigated by Gleeble simulation, mechanical testing, fractography and metallography. The results demonstrate that the experimental weld metal made using a high-Nb-W-Ti-B type filler metal was sensitive to reheat cracking, with a reduction of area no more than 2-3% in the BWI reheat cracking (RC) test. Welds made using a high-W -low-Ti type filler metal with Nb content similar to the parent steel, as well as welds make using a Ni-Nb-Ti-free-(W-free) type filler metal with the chemical composition closer to P24 grade material, were more ductile and crack-resistant, though with reduced cross-weld creep strength. Fractography of RC test specimens showed evidence of pronounced localisation of damage at the prior austenite grain boundaries of the thermally reheated, experimental P23 weld metal. The reheat cracking susceptibility of the less ductile weld metal was apparently related both to the chemical composition (higher B, Nb and Ti content) and sub-structural features of the coarse-grained reheated weld metal microstructure. Appropriate single- and multi-cycle thermal Gleeble simulations to produce representative HAY and reheated weld metal microstructures (as function of peak temperature), in conjunction with the BWI RC test were successfully applied to characterise the reheat cracking sensitivity of the candidate weld metals and parent steel HAZ. (orig.)

Creep-fatigue evaluation method for modified 9Cr-1Mo steel

International Nuclear Information System (INIS)

Wada, Y.; Aoto, K.

1997-01-01

As creep-fatigue evaluation methods on normalized and tempered Modified 9Cr-1Mo steel for design use, the time fraction rule and the simplified conventional ductility exhaustion rule are investigated for the prediction of tension strain hold creep-fatigue damage of this material. For the above investigation, stress relaxation behaviour during strain hold has to be analyzed using stress-strain-time relation. The initial value of stress relaxation was determined by cyclic stress-strain curves in continuous cycling fatigue tests. Cyclic stress-strain behaviour of Mod.9Cr-1Mo(NT) steel is different from that of austenitic stainless steels, so this effect was considered. Stress relaxation analysis was performed using static creep strain-time relation and conventional hardening rule. The time fraction by using the above stress relaxation analysis results can give good prediction for creep-fatigue life of Mod.9Cr-1Mo(NT) steel. For design use it is practical to be able to estimate creep damages conservatively by both strain behaviour of cyclic plastic (in continuous cycling fatigue tests) and monotonic creep (in standard creep tests). The life reduction by strain hold at the minimum peak of compressive stress in creep-fatigue tests was examined, and this effects can be evaluated by the relationship between the location of oxidation and the effective deformation at crack tip. In an accelerated oxidation environment, for example in high temperature and high pressure steam, a different approach for life reduction should be developed based on the mechanism of growth of oxide and crack growth with oxidation. However, in the creep damage dominant region, its effect is saturated and the effect of cavity growth along grain boundary becomes dominant for long-term strain hold in the high temperature conditions. (author). 6 refs, 6 figs