Welding of high-strength stainless steel 03Kh12N10MT for cryogenic engineering

International Nuclear Information System (INIS)

Pustovit, A.I.

1989-01-01

Consideration is being given to weld resistance to cold and hot cracking at 93 and 77K and to mechanical properties of welded joints of high-strength stainless steel 03Kh12N10MT, produced under the fluxes AN-17M, AN-18, AN-26, AN-45, ANF-5, 48-OF-6, ANK-45 and ANK-49 in combination with various welding wires. It is shown that welds on 03Kh12N10MT steel meet the requirements only when using 48-OF-6 or ANK-49 flux. It is noted that impact strength of welds at 77K is sufficiently affected by the volume fraction of non-metallic inclusions in weld metal

Nitrogen-containing superlow-carbon austenitic steel 02Kh25N22AM2

Science.gov (United States)

Fe'ldgandler, É. G.; Svistunova, T. V.; Savkina, L. Ya.; Lapshina, O. B.

1996-02-01

At present the equipment for manufacturing carbamide mineral fertilizers is produced from domestic steel 03Kh17N14M3 having "carbamide quality." Imported equipment also used in the industry is produced from steel of the 25-22-2 (Cr -Ni-Mo) type shipped by various firms, namely, 2RE69 (Sandvik, Sweden), 254SFER (Avesta, Sweden), 2522LCN (VDM, Germany), DM 1.4466 (Germany), and X2CrNiMo 25-22-2 (Dalmine, Italy). The imported steels are used because in some units steel 03Khl7Nl4M3 does not provide the requisite corrosion resistance in an intensified process of carbamide manufacturing. We currently possess domestic high-alloyed steel for producing new and repairing imported equipment operating under the severe conditions of carbamide synthesis. The present paper concerns the structure, mechanical properties, and corrosion resistance of industrially produced steel 02Kh25N22AM2 (ChS-108) and the recommended range of its application.

Development of plastic deformations in 12Kh18N10T steel under cyclic symmetrical bending of specimens of various length

Energy Technology Data Exchange (ETDEWEB)

Pisarenko, G.S.; Leonets, V.A.; Bega, N.D. (AN Ukrainskoj SSR, Kiev. Inst. Problem Prochnosti)

1983-08-01

Effect of specimen length on intensity of plastic deformation development and cyclic strength is studied for annealed 12Kh18N10T steel under cyclic symmetrical bending. The intensity of microplastic deformations and cyclic strength of annealed 12Kh18N10T steel in the considered case is due to self-heating.

Features of argon-arc welding of aluminium alloy AD1 to stainless steel 12Kh18N10T

International Nuclear Information System (INIS)

Sadov, I.I.

1982-01-01

Welding of pipes made of the 12Kh18N10T stainless steel and the AD1 aluminium alloy is proposed to perform using one-sided aluminizing. It is recommended to use shields in order to protect internal and external surfaces of pipes, aluminizing of which is impossible. It is shown that developed technological process for welded joints made of aluminium and stainless steel for cryogenic apparatus permits to create light-duty cryostat assembly using aluminium alloys instead of copper alloys, to increase reliability of apparatus (usage of welded joints instead of soldered ones), and to improve labour conditions

Protective effect of KhOSP-10 inhibitor during corrosion, hydrogenadsorption and corrosion cracking of a steel in sulfuric acid

Energy Technology Data Exchange (ETDEWEB)

Mindyuk, A K; Svist, E I; Savitskaya, O P; Goyan, E B; Gopanenko, A N [AN Ukrainskoj SSR, Lvov. Fiziko-Mekhanicheskij Inst.

1975-01-01

The protective propeties of inhibitor KhOSP-10 in the time of corrosion and corrosive cracking of steel 40Kh are higher then those of inhibitors KPI-1, KI-1, I-I-V etc. Its ability to reduce steel hydrogenation is the same as in the case of KPI-1 inhibitor i.e. below that of KI-1. HCl additives enhance the efficiency of inhibitors KPI-1, KI-1, I-1-V etc. up to the protective ability of KhOSP-10. Kinetics of the electrode processes was estimated from polarization curves.

Influence of sulphur and phosphorus impurities on ductility of 25Kh2NMFA steel during forging

International Nuclear Information System (INIS)

Onishchenko, A.K.

1989-01-01

Using cylindrical samples of the 25Kh2NMFA steel with sulfur and phosphorus content in the range of 0.001-0.030%, tensile test with the rate of deformation 10 -3 s -1 at the temperatures of 800-1200 deg C has been conducted. Analysis of fracture foci and plasticity diagrams has shown, that to ensure ductility during forging and high mechanical properties, the content of sulfur and phosphorus impurities in the 25Kh2NMFA steel must not exceed 0.015%

Effect of agressive medium movement of local corrosion of the steel - 12Kh18N10T

International Nuclear Information System (INIS)

Makartsev, V.V.; Pakhomov, V.S.; Abramova, I.M.

1980-01-01

The effect of agressive medium movement on the formation of pitting corrosion of the 12Kh18N10T stainless steel in the acidic chloride-nitrate solution at room temperature is studied. It is established that the agressive medium movement hinders the formation of pitting corrosion at potentials more negative than +0.4 V and practically does not affect it at more positive potentials. The investigations have been carried out on a disc electrode rotating at a speed from 0 to 2000 rot./min

On the protective effect of KhOSP-10 inhibitor during corrosion, hydrogenadsorption and corrosion cracking of a steel in sulfuric acid

International Nuclear Information System (INIS)

Mindyuk, A.K.; Svist, E.I.; Savitskaya, O.P.; Goyan, E.B.; Gopanenko, A.N.

1975-01-01

The protective propeties of inhibitor KhOSP-10 in the time of corrosion and corrosive cracking of steel 40Kh are higher then those of inhibitors KPI-1, KI-1, I-I-V etc. Its ability to reduce steel hydrogenation is the same as in the case of KPI-1 inhibitor i.e. below that of KI-1. HCl additives enhance the efficiency of inhibitors KPI-1, KI-1, I-1-V etc. up to the protective ability of KhOSP-10. Kinetics of the electrode processes was estimated from polarization curves

Peculiarities of welding procedure for the 05Kh12K14N5M5T-VD maraging stainless steel with strength higher 1500 MPa

International Nuclear Information System (INIS)

Pustovit, A.I.

1980-01-01

The effect of welding procedure of 05Kh12K14N5M5T-VD stainless steel on the properties of its welded joints is investigated. A new procedure of welding for pressure vessels made of this steel using Sv-03Kh15K14N5M3T-EL welding wire is suggested [ru

Welding procedure for 06Kh13N7D2 steel

International Nuclear Information System (INIS)

Muromtsev, B.I.; Turkov, I.I.

1990-01-01

Based on the results of investigations into the process strength, mechanical and corrosion properties of 08Kh13N7D2 steel welded joints, the optimal method of its welding and a possibility of applying it for high-strength mounting in nuclear power plants are determined

Corrosion resistance of welded joints in 08Kh22N6T and 08Kh21N6M2T steels made with new electrodes

International Nuclear Information System (INIS)

Sidorkina, Y.S.; Leibzon, V.M.; Mankevich, T.V.; Sidlin, E.A.; Zheltova, G.A.

1986-01-01

This paper examines the corrosion resistance of 08Kh22N6T and 08Kh21N6M2T steels which would make it possible to ensure equal properties of all the zones of the welded joints. The investigations were carried out on the welded joints in the steels produced with new OZL-40 and OZL-41 electrodes and with standard TsL-11 and EA-400/10u electrodes. The chemical compositions of the steels and deposited metal are presented. The tests of the intercrystalline corrosion resistances of the welded joints in the steels in the as-welded condition and after heat treatment showed that the weld metal is not attacked by intercrystalline corrosion. The tests also showed that the welded joints in 08Kh22N6T steel made with the OZL-40 and TsL-11 electrodes are resistant to corrosion in 55% phosphoric acid at 90 C in 1% sulfuric acid, and in 25% formic acid at 80 C. The investigated steels made with the OZL-40 and OZL-41 electrode respectively show that the welded joints are resistant to intercrystalline and general corrosion, have high mechanical and processing properties and the electrodes, and can be used for welding equipment designed for service in alkaline, neutral, and slightly acid media

Effect of smelting method on the austenite grain size and properties of heat-resisting pearlitic steel

International Nuclear Information System (INIS)

Balakhovskaya, M.B.; Khusainova, N.A.; Davlyatova, L.N.

1975-01-01

Influence of smelting method on austenite grain size and properties of refractory perlite steel were studied. An opportunity was found to increase the steel refractoriness without deteriorating its other properties. The steel 12Kh1MF of electric or common open-hearth smelting was used. The dependence of kinetics of austenite grain growth on the smelting method was studied in the temperature range 950 deg - 1200 deg C with 1 hour exposure. The grain size of austenite in steel is supposedly determined by aluminium nitrides and vanadium carbides. In tests of normalized (kept for 20 minutes at 950-980 deg C) and tempered (kept for 3 hours at 730 deg C) transverse (tangential) pipe cross-section samples the electric steel had higher impact viscosity than the open-hearth metal. At working temperatures (540 deg -580 deg C) the difference in viscosity has its minimum. Viscosity of both steels 12Kh1MF begins to sharply decrease from 20 deg C. However, electric steel has rather high viscosity even at - 40 deg C, while the open-hearth one becomes brittle as early as at - 20 deg C. Long-term strength tests at 580 deg C under stresses 10-14 kG/mm 2 show that the coarse-grain steel is more refractory, i.e. time till fracture of open-hearth steel samples is twice as long as that of electric steel samples

Investigation of Creep Processes and Microdamages in 10Kh9V2MFBR-Sh High-Chromium Steel

Science.gov (United States)

Grin', E. A.; Pchelintsev, A. V.

2018-01-01

During the modernization and the new construction of power units at TPPs in Russia, high-chromium martensitic steels with higher heat-resistant properties than the traditional perlite steels are increasingly used as structural materials. High-chromium steels have a necessary regulatory support for their use in domestic power engineering. However, up to the present time, the issue of assessing the quality of these steels at the analysis of their state during long-term operation remains open. The article proposed is one of the first attempts to create a system of quality criteria for martensitic steels based on their microdamage parameters. Tests were carried out on the long-term strength and creep of samples from 10Kh9V2MFBR-Sh steel at high temperatures with the construction of creep curves in relative coordinates "deformation related to the deformation of fracture, current time related to time to failure." For some samples, the tests were interrupted and the metal was subjected to metallographic studies consisting of the analysis of microdamage with reference to the accumulated creep strain. It has been shown experimentally that the deformation curve of high-chromium steel differs from the analogous curve of pearlitic steel by a longer and flat section of steady creep and by a sharper transition to the third accelerated creep stage, which has a very short time period (approximately 10% of the total durability). The tendency to the increase in the microdamage of the structure of steel as the accumulated creep strain increases with time was confirmed. The beginning of transition to the final creep phase is characterized by the formation of contours of future pore chains and by the appearance of individual large pores of up to 6 μm in size, the presence of which in the microstructure of the martensitic steel indicates a very significant accumulation of creep strain, and corresponds to the predestruction stage of metal. It is necessary to continue the research to

Effect of smelting method on the austenite grain size and properties of heat-resisting pearlitic steel

Energy Technology Data Exchange (ETDEWEB)

Balakhovskaya, M B; Khusainova, N A; Davlyatova, L N [Vsesoyuznyj Nauchno-Issledovatel' skij Teplotekhnicheskij Inst., Moscow (USSR)

1975-12-01

Influence of smelting method on austenite grain size and properties of refractory perlite steel were studied. An opportunity was found to increase the steel refractoriness without deteriorating its other properties. The steel 12Kh1MF of electric or common open-hearth smelting was used. The dependence of kinetics of austenite grain growth on the smelting method was studied in the temperature range 950 deg - 1200 deg C with 1 hour exposure. The grain size of austenite in steel is supposedly determined by aluminium nitrides and vanadium carbides. In tests of normalized (kept for 20 minutes at 950-980 deg C) and tempered (kept for 3 hours at 730 deg C) transverse (tangential) pipe cross-section samples the electric steel had higher impact viscosity than the open-hearth metal. At working temperatures (540 deg -580 deg C) the difference in viscosity has its minimum. Viscosity of both steels 12Kh1MF begins to sharply decrease from 20 deg C. However, electric steel has rather high viscosity even at /sup -/40 deg C, while the open-hearth one becomes brittle as early as at /sup -/20 deg C. Long-term strength tests at 580 deg C under stresses 10-14 kG/mm/sup 2/ show that the coarse-grain steel is more refractory, i.e. time till fracture of open-hearth steel samples is twice as long as that of electric steel samples.

Hydrogen degradation of the 26H2MF alloy steel in H2SO4 and hydrocarbon environments

International Nuclear Information System (INIS)

Zielinski, A.; Swieczko-Zurek, B.; Michaliak, P.

2004-01-01

The Polish 26H2M alloy steel has been subjected to different heat treatment resulting in different microstructure and fracture appearance. The slow strain rate tests have been made on smooth round specimens in diluted sulphuric acid, boiler fuel and used mineral machine oil. The 26H2MF steel has become relatively immune in neutral boiler fuel and mineral oil and been heavily suffered from hydrogen degradation in acidic environment. The results demonstrate that the 26H2MF steel is highly susceptible to hydrogen degradation but in absence of stress raisers the increased hydrogen absorption in hydrocarbons can cause only small loss of its plasticity. (author) >>>

Metallographical procedure for detecting carburized layer in the 12Kh18N10T steel tubes

International Nuclear Information System (INIS)

Najmark, S.I.; Shmalenyuk, R.P.

1977-01-01

The various causes of the tendency to intercrystalline corrosion of stainless steel tubing were studied. 12Kh18N10T steel tube specimens were metallographically investigated to reveal the presence and depth of the carburized layer. Unlubricated specimens and specimens with the graphite-saltpeter lubrication applied on them were austenized in the temperature range from 950 to 1250 deg C and then exposed to a provoking anneal at 650 deg C for 24 h. All the lubricated specimens showed a carbide network along grain boundaries and intercrystalline cracks. The specimens treated without lubrication had no cracks. The method offered can differentiate poor tube cleaning and the undesirable effect of other processing steps on the tubes

Heat treatment effect on impact strength of 40Kh steel

International Nuclear Information System (INIS)

Golubev, V.K.; Novikov, S.A.; Sobolev, Yu.S.; Yukina, N.A.

1984-01-01

The paper presents results of studies on the effect of heat treatment on strength and pattern of 40Kh steel impact failure. Loading levels corresponding to macroscopic spalling microdamage initiation in the material are determined for three initial states. Metallographic study on the spalling failure pattern for 40Kh steel in different initial states and data on microhardness measurement are presented

On the low-cycle fracture of chromium-nickel-molybdenum structural steels in seawater

International Nuclear Information System (INIS)

Karpenko, G.V.; Kobzaruk, A.V.; Malyshevskij, V.A.; Shul'te, A.Yu.; Rybin, V.V.; Silaev, I.I.

1977-01-01

The processes of low-cycle fracture of the chrome-nickel-molybdenum steels 15KhN5MF, 12KhN4MF and 15KhN3M in air, and in sea water have been investigated by the optical microscopy method, and electron microscopic examination of thin films. Bringing no change in the fracture character, sea water produces a speeding-up effect on the low-cycle fatigue fracture process. During long-time corrosion fatigue testing considerable importance lies with the electrochemical corrosion factor expediting the occurrence of corrosive pits acting as crack-initiation nuclei, fatigue crack attack, accumulation of corrosion products in fatigue cracks, etc

Long-term strength and allowable stresses of grade 10Kh9MFB and X10CrMoVNb9-1 (T91/P91) chromium heat-resistant steels

Science.gov (United States)

Skorobogatykh, V. N.; Danyushevskiy, I. A.; Schenkova, I. A.; Prudnikov, D. A.

2015-04-01

Currently, grade X10CrMoVNb9-1 (T91, P91) and 10Kh9MFB (10Kh9MFB-Sh) chromium steels are widely applied in equipment manufacturing for thermal power plants in Russia and abroad. Compilation and comparison of tensile, impact, and long-term strength tests results accumulated for many years of investigations of foreign grade X10CrMoVNb9-1, T91, P91, and domestic grade 10Kh9MFB (10Kh9MFB-Sh) steels is carried out. The property identity of metals investigated is established. High strength and plastic properties of steels, from which pipes and other products are made, for operation under creep conditions are confirmed. Design characteristics of long-term strength on the basis of tests with more than one million of hour-samples are determined ( and at temperatures of 500-650°C). The table of recommended allowable stresses for grade 10Kh9MFB, 10Kh9MFB-SH, X10CrMoVNb9-1, T91, and P91 steels is developed. The long-time properties of pipe welded joints of grade 10Kh9MFB+10Kh9MFB, 10Kh9MFB-Sh+10Kh9MFB-Sh, X10CrMoVNb9-1+X10CrMoVNb9-1, P91+P91, T91+T91, 10Kh9MFB (10Kh9MFB-Sh)+X10CrMoVNb9-1(T/P91) steels is researched. The welded joint reduction factor is experimentally determined.

Influence of quantity of non-martensite products of transformation on resistance to fracture of improving structural steel

International Nuclear Information System (INIS)

Gulyaev, A.P.; Golovanenko, Yu.S.; Zikeev, V.N.

1978-01-01

18KhNMFA, low-carbon, alloyed steel and 42KhMFA medium-carbon, alloyed steel have been examined. For the purpose of obtaining different structures in hardening the steel, different cooling rates, different temperatures and isothermal holding times are applied. The following has been shown: on tempering to the same hardness (HV 300), the presence of non-martensite structures in hardened state does not practically influence the standard mechanical properties of steel (sigmasub(B), sigmasub(0.2), delta, PSI). The resistance of steel to the brittle failure is enhanced by the uniform, fine-disperse distribution of the carbide phase in the structure of lower bainite (up to 80 % bainite in martensite for 42KhMF steel to be improved), as well as strongly fragmented packages of rack martensite-bainite (up to 50 % lower bainite in martensite of 18KhNMFA steel). The formation of the upper bainite in the structure of the hardened steels 18KhNMFA and 42KhMF results on tempering in the formation of coarse, non-uniform, branched carbide inclusions, and this, in its turn, leads to raising the cold-shortness threshold and to lowering the amount of work as required for propagation of a crack. The presence of ferritic-pearlitic structures in the structural steels hardened to martensite and bainite results in reducing the resistance of steel to the brittle failure; the presence of every 10 % ferritic-pearlitic component in martensite of the structural steels 18KhNMFA and 42KhMFA to be thermally improved, raises T 50 by 8 deg and 20 deg C, respectively

Study of 16KhSN high strength steel in different structural states and under working conditions

International Nuclear Information System (INIS)

Skudnov, V.A.; Vorob'ev, I.A.; Kutyajkin, V.G.; Bugrov, Yu.V.

1985-01-01

A study was made on the effect of deformation degree (up to 60%) during reducing, drawing and heat treatment (annealing at 750 deg C), quenching from 930 deg C and tempering at 350 deg C) on strength, plasticity, hardening degree, notch sensitivity, density and elasticity characteristics of the steel. The effect of test temperature (from-196 up to 1000 deg C) on tensile strength and plasticity was studied as well. It was established that drawing and reducing of 16KhSN steel in annealed state with strain degrees of up to 60% results to increase of strength characteristics 1.7...2.3 times and decrease of plasticity characteristics by 15...23%, strain hardening coefficient - 2.2 times and the maximum strain energy - by 80 MJ/m 3 . Hardening heat treatment (quenching from 930 deg C+temperating at 350 deg C) affects on mechanical properties of 16KhSN steel in much the same way as cold working, but strength characteristics of heat-treated steel increase 2.6...3.6 times and the maximum strain energy grows by 640 MJ/m 3 . Systematic data on the effect of temperature (-196...1000 deg C) and tensile rate (4 mm/min...5m/s) on strength and plasticity of 16KhSN steel in annealed state were obtained

Additional materials for welding of the EP99 heat resisting alloy with the EI868 alloy and 12Kh18N9T steel

International Nuclear Information System (INIS)

Sorokin, L.I.; Filippova, S.P.; Petrova, L.A.

1978-01-01

Presented are the results of the studies aimed at selecting an additive material for argon-arc welding process involving heat-resistant nickel EP99 alloy to be welded to the EI868 alloy and 12Kh18N9T steel. As the additive material use was made of wire made of nickel-chromium alloys and covered electrodes made of the EP367 alloy with additions of tungsten. It has been established that in order to improve the resistance of metal to hot-crack formation during argon arc welding of the EP99 alloy with the EI868 alloy, it is advisable to use an additive material of the EP533 alloy, and while welding the same alloy with the 12Kh18N9T steel, filler wire of the EP367 alloy is recommended

Effect of metal properties of casts of steel-15Kh1M1FL on the crack resistance at 565 deg C

International Nuclear Information System (INIS)

Gladshtejn, V.I.; Sheshenev, M.F.

1976-01-01

Results are given of prolonged tests of the metal of industrial casts with various fluidity limits. It has been shown experimentally that a quite satisfactory crack resistance is characteristic of a metal with a fluidity limit in the range 30-50 kgf/mm 2 . Metallographic studies have been conducted. Upon variation of the structure and properties of the 15Kh1M1FL steel during operation, the rate of growth of small cracks (up to 2.0 mm) decreases almost by 3 orders of ten (from 1.4x10 -4 to 2.0x10 -7 mm/hour). Subsequent structural changes during prolonged operation (over 50000 hours) result in a gradual increase in the rate of crack growth. At the same time resistance towards appearance of the impermissible high rate of the crack growth, Ksub(10sup(-3)), diminishes monotonically with the operation time. The metal of industrial 15Kh1M1FL steel casts has good crack resistance (Ksub(10sup(-3)) =30-70 kgf/mmsup(3/2) and Vsub(ef) =) kgf/mm 2 ) and a satisfactory local plasticity (critical opening being no more than 0.20 mm for 10 3 hours)

Successive carbon- and boron saturation of KhVG steel in powder mixtures

Energy Technology Data Exchange (ETDEWEB)

Alimov, Yu A; Gordienko, S I

1975-01-01

Method of successive saturation of KhVG steel with carbon and boron in powder mixtures is described. After carbonization of steel in a charcoal carburator at 930 deg C during 3 hrs a domain of equiaxial large grains is formed there the latter representing carbides of Fe/sub 3/C and (Fe, M)/sub 3/C. The increase of duration of carbonization up to 5 hrs and above results in formation of a cement grid greatly impairing the mechanical properties of the metal. Carbonization is followed by borating in powdered technical boron carbide at 900 deg C for 4 hrs which ensures formation on the sample surface of a borated layer with depth up to 65 mkm covering the carbonized zone. As followed from metallographic and x-ray structural analysis, the borated layer consists of boride needles with complex composition (Fe, Cr, Mn)B. Oil hardening of carbonized KhVG steel from 850 deg C and low-temperature tempering at 180 deg C for 1 hr results in formation in the main metal of martensite-carbide structure and, respectively, in the decrease of the microhardness gradient between the diffusion layers, as compared with borated KhVG steel. Operation tests of strengthened matrices of preforming machines under the conditions of application of dynamic pressing forces up to 1500 kg Fce/cm/sup 2/ demonstrated that the cyclical strength of carboborated coverings is 2.0-3.0 times higher than that of borated ones. The method of carboborating is recommended for strengthening the details of stamp and press tools.

Mechanical properties and kinetics of bainite transformation in the 35KhN3MFA and 25KhN3MFA steels

International Nuclear Information System (INIS)

Korotushenko, G.V.; Grigorkin, V.I.; Kozlov, V.I.; Sandomirskij, M.M.; Krivonosova, L.F.

1978-01-01

The mechanical properties and phase composition of the 25KhN3M A and 25KhN3M A bainitic steels have been investigated under austenization temperature varying from 870 to 1180 deg C and quenching cooling rate varying from 1 to 18x10 3 deg/min. Roentgen and quantitative phase analyses were employed. When bainitic steels are subjected to quenching by cooling with slow rate, their structure reveals b.c.c.-bainite with carbon content below the steel average, tetragonal martensite with a higher carbon content, carbon-rich residual austenite and carbides. Decreasing quenching cooling rates increase the concentration of tetragonal martensite and residual austenite and correspondingly reduce the concentration of b.c.c.-bainite. This tends to degrade the structural strength of bainitic steels in cores of large-size forged products

Structural inheritance in cast 30KhGNM-type steel

International Nuclear Information System (INIS)

Sadovskij, V.D.; Bershtejn, L.I.; Mel'nikova, A.A.; Polyakova, A.M.; Schastlivtsev, V.M.

1980-01-01

Structural inheritance in the cast 30KhGNM-type steel depending on the heating rate and the temperature of preliminary tempering is investigated. When eating the cast steel with a beinite structure at the rate of 1-150 deg/min, the restoration of austenite grain and the following recrystallization due to the phase cold work, are observed. Slow heating from room temperature or preliminary tempering hinder grain restoration during heating. A non-monotonous effect of tempering temperature on the structural inheritance is established which can be connected with the kinetics of decomposition of residual austenite in steel

Operational reliability of high pressure steam lines of pearlitic steels after 150-200 thousand h service

International Nuclear Information System (INIS)

Veksler, E.Ya.; Chajkovskij, V.M.; Osasyuk, V.V.

1980-01-01

Usage of both calculational and physical methods is recommended to estimate a service operating life of long-term working steam line materials. Application of these methods is demonstrated when studying steam line bends made of 12MKh and 12Kh1MF pearlitic steels. Good coincidence of results for the determination of residual durability of steam lines is obtained using these two methods [ru

Study of surface layer on 08Kh15N5D2T steel

International Nuclear Information System (INIS)

Tyurin, A.G.; Povolotskij, V.D.; Zhivotovskij, Eh.A.; Berg, B.N.

1986-01-01

08Kh15N5D2T steel phase composition is investigated. Its surface layer was determined by X-ray diffraction analysis method. It is shown, that a subscale appears to be the reason for corrosion of products, made of EhP410 steel. Under the existing smelling technology the carbon content in it is ≥ 0.05%. Therefore to avoid the metal surface depletion with chromium, one must provide for titanium relation to carbon of not less than 4.5 and carry out the rolled product thermal treatment in a protective atmosphere; otherwise, the technology must include not only the removal of scale from steel but the metal subscale layer as well

Strain ageing of the 15Kh2MFA steel at 500 and 550 deg C

International Nuclear Information System (INIS)

Maksimovich, G.G.; Azbukin, V.G.; Krylova, R.P.; Tretyak, I.Yu.; Bardachevskaya, T.V.

1978-01-01

The effect of ageing at high temperatures and under high stresses on strength and plasticity of the 15Kh2MFA steel has been studied. The steel was kept at 500 and at 550 deg C for 100, 1000 and 2500 hours without stress and under stress of 0.5 and 0.9 of the long-term strength limit (sigmasub(ls)). Ageing at 500 deg C without stress and under 0.5 sigmasub(ls) changed neither strength nor plasticity of the steel; under 0.9 sigmasub(ls) the strength somewhat decreased. Ageing at 550 deg C for 1000 hours resulted in an appreciable stress drop

Relationships of quenching stresses to structural transformations in steel

International Nuclear Information System (INIS)

Loshkarev, V.E.

1985-01-01

Technique for accountancy of the effect of stresses on structural transformations in steel when solving problems of thermoplasticity is suggested. It is revealed on the basis of the conducted calculations that accountancy of interrelation of stressed and structural states of 20Kh2MF steel essentially affects forecasting of results of quenching

Structure, mechanical and corrosion properties of powdered stainless steel Kh13

International Nuclear Information System (INIS)

Radomysel'skij, I.D.; Napara-Volgina, S.G.; Orlova, L.N.; Apininskaya, L.M.

1982-01-01

Structure, mechanical and corrosion properties are studied for compact powdered stainless steel, Grade Kh13, produced from prealloyed powder and a mixture of chromium and iron powders by hot vacuum pressing (HVP) following four schemes: HVP of unsintered billets; HVP of presintered billets; HVP of unsintered billets followed by diffusion annealing; HVP of sintered billets followed by diffusion annealing. Analysis of the structure, mechanical and corrosion properties of Kh13 steel produced according to the four schemes confirmed that production of this steel by the HVP method without presintering of porous billets and diffusion annealing of compact stampings is possible only when prealloyed powder of particular composition is used as a starting material

Effect of Heat Treatment on the Structure and Properties of Die Steel 70Kh3G2FTR

Science.gov (United States)

Krylova, S. E.; Kletsova, O. A.; Gryzunov, V. I.; Fot, A. P.; Tavtilov, I. Sh.

2018-01-01

The effect of heat treatment parameters on the properties and structural and phase composition of a promising die steel 70Kh3G2FTR for hot deformation is studied. The temperature-and-stress state of a hammer die under a heat treatment is simulated.

Effect of heat treatment and plastic deformation on the structure and the mechanical properties of nitrogen-bearing 04N9Kh2A steel

Science.gov (United States)

Blinov, V. M.; Bannykh, O. A.; Lukin, E. I.; Kostina, M. V.; Blinov, E. V.

2014-11-01

The effect of the conditions of heat treatment and plastic deformation on the structure and the mechanical properties of low-carbon martensitic nickel steel (9 wt % Ni) with an overequilibrium nitrogen content is studied. The limiting strain to failure of 04N9Kh2A steel is found to be 40% at a rolling temperature of 20°C and 80% at a rolling temperature of 900°C. Significant strengthening of the steel (σ0.2 = 1089 MPa) is obtained after rolling at a reduction of 40% at 20°C. The start and final temperatures of the α → γ transformation on heating and those of the γ → α transformation on cooling are determined by dilatometry. The specific features of the formation of the steel structure have been revealed as functions of the annealing and tempering temperatures. Electron-microscopic studies show that, after quenching from 850°C and tempering at 600°C for 1 h, the structure contains packet martensite with thin interlayers of retained austenite between martensite crystals. The strength of the nitrogen-bearing 04N9Kh2A steel after quenching from 850 and 900°C, cooling in water, and subsequent tempering at 500°C for 1 h is significantly higher than that of carboncontaining 0H9 steel used in cryogenic engineering.

Corrosion of austenitic steels and their components in vanadium-containing chloride melts

Science.gov (United States)

Abramov, A. V.; Polovov, I. B.; Rebrin, O. I.; Lisienko, D. G.

2014-08-01

The corrosion of austenitic 12Kh18N10T, 10Kh17N13M2T, and 03Kh17N14M3 steels and their components (Cr, Fe, Ni, Mo) in NaCl-KCl-VCl2 melts with 5 wt % V at 750°C is studied. The rates and mechanisms of corrosion of the materials under these conditions are determined. The processes that occur during contact of the metals and steels with vanadium-containing chloride electrolytes are investigated.

Effect of helium ion bombardment on hydrogen behaviour in stainless steel

International Nuclear Information System (INIS)

Guseva, M.I.; Stolyarova, V.G.; Gorbatov, E.A.

1987-01-01

The effect of helium ion bombardment on hydrogen behaviour in 12Kh18N10T stainless steel is investigated. Helium and hydrogen ion bombardment was conducted in the ILU-3 ion accelerator; the fluence and energy made up 10 16 -5x10 17 cm -2 , 30 keV and 10 16 -5x10 18 cm -2 , 10 keV respectively. The method of recoil nuclei was used for determination of helium and hydrogen content. Successive implantation of helium and hydrogen ions into 12Kh18N10T stainless steel results in hydrogen capture by defects formed by helium ions

Structural features and properties of the laser-deposited nickel alloy layer on a KhV4F tool steel after heat treatment

Science.gov (United States)

Shcherbakov, V. S.; Dikova, Ts. D.; Stavrev, D. S.

2017-07-01

The study and application of the materials that are stable in the temperature range up to 1000°C are necessary to repair forming dies operating in this range. Nickel-based alloys can be used for this purpose. The structural state of a nickel alloy layer deposited onto a KhV4F tool steel and then heat treated is investigated. KhV4F tool steel (RF GOST) samples are subjected to laser deposition using a pulsed Nd:YAG laser. A nickel-based material (0.02C-73.8Ni-2.5Nb-19.5Cr-1.9Fe-2.8Mn) is employed for laser deposition. After laser deposition, the samples are subjected to heat treatment at 400°C for 5 h, 600°C for 1 h, 800°C for 1 h, and 1000°C for 1 h. The microstructure, the phase composition, and the microhardness of the deposited layer are studied. The structure of the initial deposited layer has relatively large grains (20-40 μm in size). The morphology is characterized by a cellular-dendritic structure in the transition zone. The following two structural constituents with a characteristic dendritic structure are revealed: a supersaturated nickel-based γ solid solution and a chromium-based bcc α solid solution. In the initial state and after heat treatment, the hardness of the deposited material (210-240 HV 0.1) is lower than the hardness of the base material (400-440 HV 0.1). Only after heat treatment at 600°C for 1 h, the hardness increases to 240-250 HV0.1. Structure heredity in the form of a dendritic morphology is observed at temperatures of 400, 600, and 800°C. The following sharp change in the structural state is detected upon heat treatment at 1000°C for 1 h: the dendritic morphology changes into a typical α + γ crystalline structure. The hardness of the base material decreases significantly to 160-180 HV 0.1. The low hardness of the deposited layer implies the use of the layer material in limited volume to repair the forming surfaces of dies and molds for die casting. However, the high ductility of the deposited layer of the nickel

Cyclic crack resistance of anticorrosion cladding-15Kh2MFA steel joint

International Nuclear Information System (INIS)

Zvezdin, Yu.I.; Nikiforchin, G.N.; Timofeev, B.T.; Zima, Yu.V.; Andrusiv, B.N.

1985-01-01

Cyclie crack resistance of transition zone in austenitic cladding steel 15Kh2MFA joint is studied, taking into account the geometry of fatigue cracks, fracture micromechanism and crack closure effect. Kinetics of crack development from the cladding to the basic metal and vice versa is considered. Microstructure of transition zone is investigated. The results obtained are considered as applied to WWER. It is emphasized, that the braking of fatigue cracks is observed at low asymmetry of loading cycle. Increased loading asymmetry accelerates sharply the alloy fracture due to the growth of subcladding crack, at that, the direction of crack propagation and the structure of transition zone are not of great importance

Influence of local microplastic strains on stress corrosion of 08Kh18N10T steel

International Nuclear Information System (INIS)

Moskvin, L.N.; Efimov, A.A.; Sherman, Ya.I.; Fedorova, T.I.

1987-01-01

Study on specific features of microhomogeneous strain in the process of plastic strain development and their role in stress corrosion of 08Kh18N10T steel sheet specimens subject to preliminary strain by 1, 3, 6, 16 and 23% and subsequent tests of stress corrosion in magnesium chloride solution at 150 deg C 140 MPa has been carried out. Analysis of test results has shown that microplastic strain is distributed over a specimen nonuniformly and is accompanied with the slip bands formation which are sources of corrosion crack origination and development. 08Kh18N10T steel manifests the highest trend to stress corrosion under 1% microplastic strain

The influence of heating rate on reheat-cracking in a commercial 2 1/4Cr1Mo steel

International Nuclear Information System (INIS)

Hippsley, C.A.

1983-03-01

The effects of elevated heating rate on stress-relief cracking in a commercial 2 1/4 Cr1Mo steel have been investigated. A SEN bend-specimen stress-relaxation test was used to assess reheat cracking susceptibility and fracture mechanisms for an initial post-weld heating rate of 1000 Kh - 1 . Two factors controlling the influence of heating rate on the final severity of cracking were identified, i.e. the rate of stress-relaxation with respect to temperature, and the time available for crack-growth. The factors were found to counteract each other, but in the case of commercial 2 1/4 Cr1Mo steel, the crack-growth factor outweighed the relaxation factor, resulting in a reduction in the propensity to stress-relief cracking at the elevated heating rate. However, by reference to the results of a separate investigation concerning A508/2 MnMoNiCr steel it was demonstrated that the balance between these two factors may be reversed in other alloy systems, with the consequence that reheat cracking is exacerbated by increasing the initial heating rate. A computer model was addressed to the stress-relaxation test conditions using data from the commercial 2 1/4 Cr1Mo steel. The model predictions exhibited reasonable agreement with experimental test results for both 100 Kh - 1 and 1000 Kh - 1 heating rates. (author)

Ductility of high chromium stainless steels

International Nuclear Information System (INIS)

Peretyat'ko, V.N.; Kazantsev, A.A.

1997-01-01

Aimed to optimize the hot working conditions for high chromium stainless steels the experiments were carried in the temperature range of 800-1300 deg C using hot torsion tests and cylindrical specimens of ferritic and ferritic-martensitic steels 08Kh13, 12Kh13, 20Kh13, 30Kh13 and 40Kh13. Testing results showed that steel plasticity varies in a wide range depending on carbon content. Steels of lesser carbon concentration (08Kh13 and 12Kh13) exhibit a sharp increase in plasticity with a temperature rise, especially in the interval of 1200-1250 deg C. Steels 20Kh13 and 30Kh13 display insignificant plasticity increasing, whereas plastic properties of steel 40Kh13 increase noticeably in the range of 1000-1300 deg C. It is shown that optimal hot working conditions for specific steel must be selected with account of steel phase composition at high temperatures

The Amelioration of Myelofibrosis with Thrombocytopenia by a JAK1/2 Inhibitor, Ruxolitinib, in a Post-polycythemia Vera Myelofibrosis Patient with a JAK2 Exon 12 Mutation.

Science.gov (United States)

Ikeda, Kazuhiko; Ueda, Koki; Sano, Takahiro; Ogawa, Kazuei; Ikezoe, Takayuki; Hashimoto, Yuko; Morishita, Soji; Komatsu, Norio; Ohto, Hitoshi; Takeishi, Yasuchika

2017-01-01

Less than 5% of patients with polycythemia vera (PV) show JAK2 exon 12 mutations. Although PV patients with JAK2 exon 12 mutations are known to develop post-PV myelofibrosis (MF) as well as PV with JAK2V617F, the role of JAK inhibitors in post-PV MF patients with JAK2 exon 12 mutations remains unknown. We describe how treatment with a JAK1/2 inhibitor, ruxolitinib, led to the rapid amelioration of marrow fibrosis, erythrocytosis and thrombocytopenia in a 77-year-old man with post-PV MF who carried a JAK2 exon 12 mutation (JAK2H538QK539L). This case suggests that ruxolitinib is a treatment option for post-PV MF in patients with thrombocytopenia or JAK2 exon 12 mutations.

Radiation embrittlement of WWER 440 pressure vessel steel and of some improved steels by western producers

International Nuclear Information System (INIS)

Koutsky, J.; Vacek, M.; Stoces, B.; Pav, T.; Otruba, J.; Novosad, P.; Brumovsky, M.

1982-01-01

The resistance was studied of Cr-Mo-V type steel 15Kh2MFA to radiation embrittlement at an irradiation temperature of around 288 degC. Studied was the steel used for the manufacture of the pressure vessel of the Paks nuclear reactor in Hungary. The obtained results of radiation embrittlement and hardening of steel 15Kh2MFA were compared with similar values of Mn-Ni-Mo type steels A 533-B and A 508 manufactured by leading western manufacturers within the international research programme coordinated by the IAEA. It was found that the resistance of steel 15Kh2MFA to radiation embrittlement is comparable with steels A 533-B and A 508 by western manufacturers. (author)

Effect of zirconium on the structure and phase composition of steel 03Kh8SYu

International Nuclear Information System (INIS)

Tarzhumanova, V.A.; Ryabchenkov, A.V.; Shatunova, A.V.; Yoganova, S.A.

1986-01-01

Previously, the authors determined the optimum zirconium content providing retention of a fine-grained structure for steel 03Kh8SYu during high-temperature heating. It was suggested that this was caused by separation in the steel of intermetallic phase Fe 3 Zr. This paper presents results of further studies in this direction. X-ray analysis results for the anodic residues of the steels are presented. It can be seen that in steel without zirconium, carbides of the type M 23 C 6 and M 7 C 3 and aluminum nitride are present. On adding 0.05% Zr, zirconium nitride forms in addition to the existing aluminum nitride and carbides of the type M 7 C 3 . The authors also investigated the effect of zirconium on the tendency of the steel toward grain growth at higher temperature; they studied the structure of steel 03Kh8SYu with 0.61% Zr after soaking specimens for 100 h at 950-1100 C. Results are presented

Increasing the brittle fracture resistance in manual arc welding and heat treatment of type 12KhM steels

International Nuclear Information System (INIS)

Tikhonov, V.P.; Bychenkova, G.A.; Gordeev, Y.V.; Ilyuhov, C.V.

1984-01-01

The extensive application of heat-resisting steels is delayed by their poor weldability. Optimum technology has been developed for manual arc welding and heat treatment of structures of type 12KhM steels resulting in high cracking resistance. Trials were conducted to evaluate the efficiency of removing the structural stresses in tempering the structures. On the basis of the experimental results, it may be assumed that the toughness properties of the welded joints produced by manual arc welding can be improved by optimizing the alloying system of the weld metal, with the parent metal treated in the optimum heat treatment conditions. The aim of subsequent investigations was to assess the properties of the weld metal made with vanadium-free electrodes. It was found that the impact toughness increased two to three times; the mean hardness and the maximum hardness were both less than 220. The reduction in hardness and increase of the toughness properties of the metal are caused by the lower degree of hardening of the bulk of the grain and, consequently, by the lower concentration of plastic strain at the grain boundaries

Hydrogen effect on mechanical properties and flake formation in the 10KhSND steel rolled plates

Energy Technology Data Exchange (ETDEWEB)

Muradova, R G; Zakharov, V A; Kuzin, A P; Gol' tsov, V A; Podgajskij, M S [Donetskij Politekhnicheskij Inst. (Ukrainian SSR); Donetskij Nauchno-Issledovatel' skij Inst. Chernoj Metallurgii (Ukrainian SSR))

1982-01-01

The effect of hydrogen on mechanical properties of the 10KhSND steel rolled plates during natural aging is studied. Optimum period of metal acceptance tests, which are advisable to conduct after 5-7 day natural aging of finished products, are found out. The technique is worked out and a safe hydrogen content to prevent flake formation in the 10KhSND steel is determined. It is shown that a safe hydrogen content is dependent on the experiment conditions (sample dimensions, conditions of cooling, and prehistory).

Hydrogen effect on mechanical properties and flake formation in the 10KhSND steel rolled plates

International Nuclear Information System (INIS)

Muradova, R.G.; Zakharov, V.A.; Kuzin, A.P.; Gol'tsov, V.A.; Podgajskij, M.S.

1982-01-01

The effect of hydrogen on mechanical properties of the 10KhSND steel rolled plates during natural aging is studied. Optimum period of metal acceptance tests, which are advisable to conduct after 5-7 day natural aging of finished products, are found out. The technique is worked out and a safe hydrogen content to prevent flake formation in the 10KhSND steel is determined. It is shown that a safe hydrogen content is dependent on the experiment conditions (sample dimensions, conditions of cooling, and prehistory)

Microstructure and mechanical properties of ZrO{sub 2} particle dispersion strengthened 16MnV steel

Energy Technology Data Exchange (ETDEWEB)

Wang, B.A. [State Key Laboratory of Metastable Materials Science and Technology, Yanshan University, Qinhuangdao 066004 (China); Wang, N. [State Key Laboratory of Metastable Materials Science and Technology, Yanshan University, Qinhuangdao 066004 (China); CNOOC Research Institute of Oil and Petrochemicals (CRI), Beijing 100000 (China); Yang, Y.J.; Zhong, H. [State Key Laboratory of Metastable Materials Science and Technology, Yanshan University, Qinhuangdao 066004 (China); Ma, M.Z., E-mail: mz550509@ysu.edu.cn [State Key Laboratory of Metastable Materials Science and Technology, Yanshan University, Qinhuangdao 066004 (China); Zhang, X.Y.; Liu, R.P. [State Key Laboratory of Metastable Materials Science and Technology, Yanshan University, Qinhuangdao 066004 (China)

2017-04-24

The dispersion strengthened 16MnV steels with 0.5 wt% and 1.2 wt% ZrO{sub 2} particles were prepared using medium frequency induction melting furnace. The ZrO{sub 2} particles mixed with iron powder were added into the 16MnV steel through cored-wire injection process. Optical metallographic microscope (OM), scanning electron microscope (SEM) and transmission electron microscope (TEM) were used to observe and analyze the microstructure, fracture morphology, dislocation configuration and strengthening mechanism of ZrO{sub 2} particle dispersion strengthened 16MnV steel under as-cast, normalizing and quenching states. Results showed that the strength of 16MnV steel under various states increased significantly after the addition of dispersed ZrO{sub 2} particles. Analysis indicates that the dislocation cell formed by high density dislocation around ZrO{sub 2} particles and attractive interaction between those particles are the main strengthening mechanism of dispersion strengthened 16MnV steel. The tensile test results showed that remarkable strengthening effect of ZrO{sub 2} particle on 16MnV steel has been observed. As the addition of 1.2 wt% ZrO{sub 2}, the improvement of strength in ZrO{sub 2}/16MnV is approximately 37.69% for as-casting, 24.2% after normalization and 29.96% after quenching, respectively. The normalized ZrO{sub 2}/16MnV with 1.2 wt% ZrO{sub 2} has the highest strength of 1453 MPa.

Cooling rate and microstructure of surface layers of 5KhNM steel, machined by electroerosion method

International Nuclear Information System (INIS)

Foteev, N.K.; Ploshkin, V.V.; Lyakishev, V.A.; Shirokov, S.V.

1982-01-01

The cooling rate and microstructure of surface layers of steel 5KhNM machined by electroerosion method have been studied. It is shown that the difference in heating rate of the surface layers with electric discharge over the 5KhNM steel samples depth results in the intensive size reduction of the microstructure. In the surface layer alongside with martensite residual austenite is present, the lattice period of which increases with the increase of pulse duration, carbide phase of complex composition appears, and concentrational heterogeneity in alloying elements (except carbon) is absent

Cooling rate and microstructure of surface layers of 5KhNM steel, machined by electroerosion method

Energy Technology Data Exchange (ETDEWEB)

Foteev, N.K.; Ploshkin, V.V.; Lyakishev, V.A.; Shirokov, S.V.

1982-01-01

The cooling rate and microstructure of surface layers of steel 5KhNM machined by electroerosion method have been studied. It is shown that the difference in heating rate of the surface layers with electric discharge over the 5KhNM steel samples depth results in the intensive size reduction of the microstructure. In the surface layer alongside with martensite residual austenite is present, the lattice period of which increases with the increase of pulse duration, carbide phase of complex composition appears, and concentrational heterogeneity in alloying elements (except carbon) is absent.

Estimation of structural strength of 38KhN3MFA steel, melted using different methods

International Nuclear Information System (INIS)

Kudrya, A.V.; Mochalov, B.V.; Fadeev, Yu.I.

1982-01-01

Quantity of steel melted by different methods using criteria of fracture mechanics is evaluated. Three technological variants of the 38KhN3MFA steel melting: acid Martin steel prepared by the duplex-process (melt 1); the main Martin steel melting with deoxidation and alloying in a ladle by liquid alloy and treatment with synthetic slag with argon purging after production (melt 2) and its electroslag remelt - ESP process (melt 3) are investigated. The analysis of the investigated melts has revealed that crack resistances of the acid Martin steel is higher than that of other melts at practically similar standard mechanical properties with 0.35 probability at 0.05 significance level in the low-tempered state; in the tempered state the best crack resistance is observed in the ESP main Martin steel. Metal of the main Martin melting has lower crack resistance as compared with other meltings at both strength levels. The results of the work point out the necessity of applying the criteria of fracture mechanics for obtaining an objective evaluation of the steel quality

Neutron diffraction study of a nitrogen martensitic steel 0Kh16N4AB under load

Czech Academy of Sciences Publication Activity Database

Sumin, V. V.; Papushkin, I.V.; Bannykh, O.A.; Blinov, V.M.; Lukáš, Petr

2008-01-01

Roč. 105, č. 1 (2008), s. 88-91 ISSN 0031-918X Institutional research plan: CEZ:AV0Z10480505 Keywords : steel 0Kh16N4AB * neutron diffraction * FSD Subject RIV: BG - Nuclear, Atomic and Molecular Physics , Colliders Impact factor: 0.412, year: 2008

Molecular genetic tests for JAK2V617F, Exon12_JAK2 and MPLW515K/L are highly informative in the evaluation of patients suspected to have BCR-ABL1-negative myeloproliferative neoplasms.

Science.gov (United States)

dos Santos, Marcos Tadeu; Mitne-Neto, Miguel; Miyashiro, Kozue; Chauffaille, Maria de Lourdes L Ferrari; Rizzatti, Edgar Gil

2014-02-01

Polycythaemia vera (PV), essential thrombocythemia (ET) and idiopathic myelofibrosis (MF), are the most common myeloproliferative neoplasms (MPN) in patients without the BCR-ABL1 gene rearrangement. They are caused by clonal expansion of haematopoietic stem cells and share, as a diagnostic criterion, the identification of JAK2V617F mutation. Classically, when other clinical criteria are present, a JAK2V617F negative case requires the analysis of Exon12_JAK2 for the diagnosis of PV, and of MPL515K/L mutations for the diagnosis of ET and MF. Here, we evaluated 78 samples from Brazilian patients suspected to have MPN, without stratification for PV, ET or MF. We found that 28 (35.9%) are JAK2V617F carriers; from the 50 remaining samples, one (2%) showed an Exon12_JAK2 mutation, and another (2%) was positive for MPLW515L mutation. In summary, the investigation of JAK2V617F, Exon12_JAK2 and MPLW515K/L was relevant for the diagnosis of 38.4% of patients suspected to have BCR-ABL1-negative MPN, suggesting that molecular genetic tests are useful for a quick and unequivocal diagnosis of MPN.

Structural changes in surface layer of steel 08Kh18N10T during machining

International Nuclear Information System (INIS)

Palenik, J.; Vodarek, V.

1989-01-01

The results are reported of a study of the surface layer of steel 08Kh18N10T affected by machining. Structural changes were studied caused by finish turning and by additional roller burnishing. Multiple deformation bands were observed to occur under the given cutting conditions; they mainly consisted of deformation doublets and only in isolated cases of ε-martensite. The presence of α'-martensite was not shown in the specimen surface layer following finish turning. The deformation shear bands in the roller-burnished specimen consisted of both ε-martensite and of deformation doublets. The amount of ε-martensite in the structure was significantly higher than in the specimen worked by turning. Local presence of α'-martensite formations was observed inside the deformation bands. It thus follows that roller burnishing is unsuitable as part of the manufacture of components from steel 08Kh18N10T. (J.B.). 5 figs., 1 tab., 9 refs

The effect of thermal treatment on corrosion properties of 0Kh15N16M3B stainless steel tested in the N2O4 boiling medium

International Nuclear Information System (INIS)

Kamenev, A.Ya.; Kopets, Z.V.; Mel'nikova, N.N.; Dergaj, A.M.; Fedyushin, E.E.

1985-01-01

The experimental data on the effect of thermal treatment on corrosion properties of stainless steel 00Kh16n15m3b tested in the N 2 O 4 boiling medium at 8.0 MPa and 433 K are presented. The electron microscope data on steel microstructure after different heat treatments and phase composition of oxide films emerging at corrosion test are given. It is shown, that the rise of the heat treatment temperature from 823 up to 1023 K increases total corrosion of 00Kh16n15m3b steel under given test conditions and practically does't affect intercrystalline corrosion. Developed oxide layers are of deposited nature and doesn't affect markedly the rate of progress of the corrosive processes. Taking into account high chromium volatility in vacuum one can assume that at the initial stages of the coolant effect, the process of depletion of steel surface by chromium durng heat treatment affects markedly steel corrosion stability

Ultrasound surface treatment of Kh18N10T steel with different structural state. Ul'trazvukovaya poverkhnostnaya obrabotka stali Kh18N10T s razlichnym strukturnym sostoyaniem

Energy Technology Data Exchange (ETDEWEB)

Aksenov, V K; Danilov, P A; Mats, A V; Netesov, V M; Yaes, A A [AN Ukrainskoj SSR, Kharkov (Ukrainian SSR). Fiziko-Tekhnicheskij Inst.

1989-09-01

Ultrasound surface treatment (USST) is studied for its effect on the structure and mechanical-and-physical properties of Kh18N10T steel with different prehistory. It is shown that surface treatment may both increase and decrease steel microhardness.

Evolution of secondary-phase precipitates during annealing of the 12Kh18N9T steel irradiated with neutrons to a dose of 5 DPA

Science.gov (United States)

Tsai, K. V.; Maksimkin, O. P.; Turubarova, L. G.

2007-03-01

The formation and evolution of thermally-induced secondary precipitates in an austenitic stainless steel 12Kh18N9T irradiated in the core of a laboratory reactor VVR-K to a dose of 5 dpa and subjected to post-radiation isochronous annealings for 1 h in a temperature range from 450 to 1050°C have been studied using transmission electron microscopy (TEM) and microhardness measurements. It has been shown that the formation of stitch (secondary) titanium carbides and M 23C6 carbides at grain and twin boundaries after annealing at 1050°C is preceded by a complex evolution of fineparticles of secondary phases (titanium carbides and nitrides) precipitated at dislocation loops and dislocations during annealing at temperatures above 750°C.

Reheat cracking in 1/2 CrMoV steel. Heat affected zones

International Nuclear Information System (INIS)

Batte, A.D.; Miller, R.C.; Murphy, M.C.

1976-01-01

Low alloy creep resisting steels are inherently susceptible to cracking during stress relief heat treatment (reheat cracking) though few welds give rise to problems in manufacture or service. Mechanical tests on simulated affected zone structures in CrMoV forgings have shown that cracking occurs when the high temperature ductility is inadequate to accommodate the residual welding strain. Differences in susceptibility result from differences in heat affected zone grain size if the purity level is sufficiently high; reheat cracking may then be avoided by ensuring complete grain refinement during welding. The susceptibility of a lower purity forging was insensitive to grain size; heat affected zone refinement is unlikely to eliminate cracking in such steel. (orig.) [de

Annealing effect on restoration of irradiation steel properties

International Nuclear Information System (INIS)

Vishkarev, O.M.; Kolesova, T.N.; Myasnikova, K.P.; Pecherin, A.M.; Shamardin, V.K.

1986-01-01

The effect of temperature and annealing time on the restoration of properties of the 15Kh2NMFAA and 15Kh2MFA steels after irradiation at 285 deg with the fluence of 6x10 23 neutr/m 2 (E>0.5 MeV) is studied. Microhardness (H μ ) restoration in the irradiated 15Kh2NMFAA steel is shown to start from 350 deg C annealing temperature. The complete microhardness restoration is observed at the annealing temperature of 500 deg C for 10 hours

Effect of preliminary heat treatment on phase transformations and properties of the Kh15N5D2T (VNS-2) steel

International Nuclear Information System (INIS)

Madyanov, S.A.; Voronenko, B.I.; Makhnev, E.S.

1978-01-01

It is shown that preliminary heat treatment has a significant effect on the α→γ transformation kinetics, the quantity of residual austenite, the grain size and mechanical properties of the Kh15N5D2T steel after final heat treatment. The preliminary heat treatment regimes leading to the increase of the quantity of residual austenite and to grain refining increase the work of crack propagation in the finally strengthened state. The optimum properties were obtained after threefold preliminary tempering for 1h at 650 deg C. An approximately constant relation of α- and γ-phases (approximately 50%) is observed at 625 deg C irrespective of the investigated regimes of preliminary heat treatment

Influence of structure and properties of tubular billets of the 12 Kh 18N10T steel on deformability of tubes at cold-rolling mills

International Nuclear Information System (INIS)

Vil'yams, O.S.; Bol'shova, N.M.; Olejnik, O.V.; Velikotnaya, E.S.

1979-01-01

Metallographic analysis of the defects of the ''oblique cracks'' type on the surface of hot-rolled tubes of the 12Kh18N10T steel has been carried out. Recommended is the complex of mechanical properties and the structure factors (grain size) of conversion hot-rolled tubes, providing the combination of ductility and high rapture strength during rolling at pilger mills. At a grain size not coarser than number 5, a billet must have σsub(T) 5 >=40 %. Hot-rolled coarse-grained billet is not recommended for warm rolng because of high strain hardening

Fatigue resistance of Cr-Ni-Mo-V steel

International Nuclear Information System (INIS)

Naumchenkov, N.E.; Filimonova, O.V.; Borisov, I.A.

1985-01-01

A study was made on the effect of additional alloying (Ni, Ni+Co), stress concentration, surface plastic strain on fatigue resistance of rotor steel of Cr-Ni-Mo-V-composition. It is shown that the steel with decreased carbon content possesses high complex of mechanical properties. Fatigue characteristics are not inferior to similar characteristics of steels of 25KhN3MFA type. Additional alloying of the steel containing 0.11...0.17% C and 4.5...4.7% N:, with niobium separately or niobium and cobalt in combination enabled to improve fatigue resistance of samles up to 25%. Strengthening of stress concentration zones by surface plastic strain is recommended for improving rotor suppporting 'nower under cyclic loading

Quality of austenite chrome-nickel steel made by gas-oxygen refining

International Nuclear Information System (INIS)

Fel'dgandler, Eh.G.; Levin, F.L.; Moshkevich, E.A.; Shifrin, Eh.V.; Movshovich, V.S.; Pargamonov, E.A.

1991-01-01

Properties and structure were investigated of austenitic 03Kh18N11 and 08KhN10T steels melted at gas oxygen refining aggregates. It was established that mechanical and corrosion properties of rolling of such steels were in agreement with standard properties of metal of open melting. Sheet 08Kh18N10T steel has the level of strength and plasticity regulated for 12Kh18N10T steel. As steel of 08Kh18N10T holds the complex of high mechanical and corrosion properties, 08Kh18N10T is recommended to be replace by 12Kh18N10T with the aim of decrease of titanium usage and increase of process efficiency

Heating temperature effect on ferritic grain size of rotor steel

International Nuclear Information System (INIS)

Cheremnykh, V.G.; Derevyankin, E.V.; Sakulin, A.A.

1983-01-01

The heating temperature effect on ferritic grain size of two steels 13Kh1M1FA and 25Kh1M1FA is evaluated. It is shown that exposure time increase at heating temperatures below 1000 deg C up to 10h changes but slightly the size of the Cr-Mo-V ferritic grain of rotor steel cooled with 25 deg C/h rate. Heating up to 1000 deg C and above leads to substantial ferritic grain growth. The kinetics of ferritic grain growth is determined by the behaviour of phases controlling the austenitic grain growth, such as carbonitrides VCsub(0.14)Nsub(0.78) in 13Kh1M1FA steel and VCsub(0.18)Nsub(0.72) in 25Kh1M1FA steel. Reduction of carbon and alloying elements content in steel composition observed at the liquation over rotor length leads to a certain decrease of ferritic grain resistance to super heating

Corrosion of chromium, nickel, titanium and steels in solutions of sodium and ammonium thiosulfates

International Nuclear Information System (INIS)

Grebenshchikova, S.V.; Kochergin, V.P.; Doronina, I.V.

1983-01-01

Results of gravimetric determinatiion of average rate of chromium, nickel, titatnium and steels 12Kh18N10T and VSt.3 corrosion rate in solutions 50 mass.% (NH 4 ) 2 S 2 O 3 and Na 2 S 2 O 3 in the air and nitrogen atmosphere at 333 K have been generalized. Anodic polarization curves are recorded and stationary potentials of metals and steels under the conditions are measured. It is shown that in (NH 4 ) 2 S 2 O 3 solution the rate of metal and steels corrosion is higher than in Na 2 S 2 O 3 solution indepenent of the nature of gaseous medium contacting with solution. In the series Ni → VSt.3 → 12Kh18N10T → VT1 → chromium in (NH 4 ) 2 S 2 O 3 and Na 2 S 2 O 3 solutions at 333 K corrosion resistance increases. Chromium, titanium and chromium-nickel steel 12Kh18N10T possess a high corrosion resistance

Ductile fracture of two-phase welds under 77K. [Steel-EhP810, steel-EhP666, steel-08Kh18N10T, steel-EhP659-VI, steel-chP810

Energy Technology Data Exchange (ETDEWEB)

Yushchenko, K.A.; Voronin, S.A.; Pustovit, A.I.; Shavel' , A.V.

The effect of the type of welding and fillers on crack resistance of welded joints high-strength steel EhP810 and its various compounds with steels EhP666, 08Kh18N10T has been studied. For the welding of steel EhP810 with steels EhP810, EhP666, 08Kh18N10T electron-beam, automatic, argon tungsten arc with non-consumable electrode with various fillers, as well as argon metal-arc welding with consumable electrode, were used. It is shown, that for a joint, made by electron-beam welding, parameters sigmasub(u), Ksub(IcJ), KCV are higher than for a joint of a similar phase structure made using filler wire EhP659-VI. It is explained by the fact, that during electron-beam welding joint metal refining takes place, which removes gases. In welded joints of chP810 steel, having joints with austenitic structure, characteristic of crack resistance Ssub(c) increases by more than 0.2 mm in contrast to two-phase joints, which conventional yield strength at 77 K exceeds 1000 MPa. It is worth mentioning, that for other classes of steels formation of two-phase structure of joint increases welded joint resistance to brittle fracture. It is possible to obtain the required structure of joint with assigned level of resistance to brittle fracture by means of the use of different fillers, optimum and welding procedure, regulating the part of the basic metal in joint content.

Development of production technology and investigation of quality for forged-welded turbine rotors of steel 25Kh2NVFA

International Nuclear Information System (INIS)

Borisov, I.A.; Merinov, G.N.; Slezkina, E.V.

1997-01-01

A study was made into mechanical properties and microstructure of turbine rotor components manufactured by forging and heat treated under various conditions. It is revealed that the optimal heat treatment of forgings must include double quenching with subsequent tempering at 630-640 deg C for 10-20 h. Forged and welded rotors should be tempered at 620-630 deg C for 50-100 h. Microscopic examination and mechanical tests showed that low alloy steel 25Kh2NMF can be successfully used for manufacturing rotors of high-, medium-and low-heat turbines

Studying microstructure of heat resistant steel deoxidized by barium ferrosilicon

Directory of Open Access Journals (Sweden)

A. Z. Issagulov

2016-07-01

Full Text Available The paper examined the nature and distribution of non-metallic inclusions in the heat-resistant steel 12H1MF (0,12 % С, 1 % Сr, 0,5 - 0,6 Mo, 0,5 % V, ferrosilicobarim. As a reference, used by steel, deoxidized silicon. Melting was carried out in a laboratory, research-metallic inclusions, their shape and distribution, pollution index were studied according to conventional methods. Studies have shown that ferrosilicobarim deoxidation in an amount of 0,1 - 0,2 %, reduce the overall pollution index of non-metallic inclusions and change the nature of their distribution.

Nucleation and microstructure development in Cr-Mo-V tool steel during gas atomization

Science.gov (United States)

Behúlová, M.; Grgač, P.; Čička, R.

2017-11-01

Nucleation studies of undercooled metallic melts are of essential interest for the understanding of phase selection, growth kinetics and microstructure development during their rapid non-equilibrium solidification. The paper deals with the modelling of nucleation processes and microstructure development in the hypoeutectic tool steel Ch12MF4 with the chemical composition of 2.37% C, 12.06 % Cr, 1.2% Mo, 4.0% V and balance Fe [wt. %] in the process of nitrogen gas atomization. Based on the classical theory of homogeneous nucleation, the nucleation temperature of molten rapidly cooled spherical particles from this alloy with diameter from 40 μm to 600 μm in the gas atomization process is calculated using various estimations of parameters influencing the nucleation process - the Gibbs free energy difference between solid and liquid phases and the solid/liquid interfacial energy. Results of numerical calculations are compared with experimentally measured nucleation temperatures during levitation experiments and microstructures developed in rapidly solidified powder particles from the investigated alloy.

Long-term behaviour of heat-resistant steels and high-temperature materials

International Nuclear Information System (INIS)

1987-01-01

This book contains 10 lectures with the following subjects: On the effect of thermal pretreatment on the structure and creep behaviour of the alloy 800 H (V. Guttmann, J. Timm); Material properties of heat resistant ferritic and austenitic steels after cold forming (W. Bendick, H. Weber); Investigations for judging the working behaviour of components made of alloy 800 and alloy 617 under creep stress (H.J. Penkalla, F. Schubert); Creep behaviour of gas turbine materials in hot gas (K.H. Kloos et al.); Effect of small cold forming on the creep beahviour of gas turbine blades made of Nimonic 90 (K.H. Keienburg et al.); Investigations on creep fatigue alternating load strength of nickel alloys (G. Raule); Change of structure, creep fatigue behaviour and life of X20 Cr Mo V 12 1 (by G. Eggeler et al.); Investigations on thermal fatigue behaviour (K.H. Mayer et al.); Creep behaviour of similar welds of the steels 13 Cr Mo 4 4, 14 MoV 6 3, 10 Cr Mo 910 and GS-17 Cr Mo V 5 11 (K. Niel et al.); Determining the creep crack behaviour of heat resistant steels with samples of different geometry (K. Maile, R. Tscheuschner). (orig.,/MM) [de

Corrosion behavior of austenitic steels and their components in niobium-containing chloride melts

Science.gov (United States)

Abramov, A. V.; Polovov, I. B.; Rebrin, O. I.; Volkovich, V. A.; Lisienko, D. G.

2014-02-01

The mechanism of corrosion of austenitic steels 12Kh18N10T, 10Kh17N13M2T, and 03Kh17N14M3 and metals Cr, Fe, Ni, and Mo in a NaCl-KCl-NbCl n ( n = 3.5, Nb content is 5 ± 0.1 wt %) melt at 750°C is studied. The metal and steel corrosion rates under these conditions are determined. The character of material fracture and the mechanisms of material corrosion are found.

Microstructural investigations of fatigued 12% Cr-steel 1.4914 (X 18 Cr Mo V Nb 12 1)

International Nuclear Information System (INIS)

Gersinska, R.

1992-10-01

The low cycle fatigue properties of a tempered steel X18 Cr Mo V Nb 12 1 (DIN 1.4914) have been investigated at different temperatures, strain amplitudes, mean strains and strain rates. The role of martensite lath structure and of precipitates and dislocations on the strengthening mechanisms and fatigue damage have been analysed. Plastic deformation results in a slip band formation on the surface and in a cellular dislocation structure in the interior of the specimens. A reduced strain rate is causing lower stress amplitudes and greater cells at higher temperatures. At lower temperatures the influence of strain rate is small. Fatigue mechanisms are soon dominant at lower strain rates. REM-investigations of the specimen surfaces are revealing the development of cracks at slip bands. The cracks start always at the surfaces of the specimen, and they are transcristalline in nature. The influence of the ageing temperature has been investigated. A reduced ageing temperature of 600degC results in a higher dislocation density and a lower martensite lath distance in the undeformed material. Strain ageing was initially observed in tensile experiments. The influence of dynamic strain ageing on the mechanical properties and the microstructure of tempered steel 1.4914 is investigated. A correlation of mechanical and microstructural data has been performed. (orig./MM) [de

On change of vanadium carbide state during 20Kh3MVF steel heat treatment

International Nuclear Information System (INIS)

Gitgarts, M.I.; Maksimenko, V.N.

1975-01-01

The Xray diffraction study of vanadium carbide MC has been made in the steel-20KH3MVF quenched from 970 and 1040 deg and tempered at 660 deg for 210 hrs. It has been found that the constant of the MC crystal lattice regularly varies with the temperature of isothermal hold-up. In the steel tempered after quenching two vanadium carbides of different content could co-exist simultaneously: carbide formed in the quenching process and carbide formed during tempering. The discovered effect of the temperature dependence of the MC content is, evidently, inherent also to other steels containing vanadium

Superheat effect on bainite steel hardenability

International Nuclear Information System (INIS)

Kubachek, V.V.; Sklyuev, P.V.

1978-01-01

The bainite hardenability of 34KhN1M and 35 KhN1M2Ph steels has been investigated by the end-face hardening technique. It is established that, as the temperature of austenitization rises from 900 to 1280 deg C, the temperature of bainite transformation increases and bainite hardenability of the steels falls off. A repeated slow heating to 900 deg C of previously overheated 34KhN1M steel breaks up grain, lowers the temperature of the bainite transformation and raises the hardenability to values obtained with ordinary hardening from 900 deg C. A similar heating of previously overheated 35KhN1M2Ph steel is accompanied by restoration of initial coarse grains and maintenance of both the elevated bainite transformation temperature and to lower hardenability corresponding to hardening from the temperature of previous overheating

Mutation and crystallization of the first KH domain of human polycytosine-binding protein 1 (PCBP1) in complex with DNA

International Nuclear Information System (INIS)

Yoga, Yano M. K.; Traore, Daouda A. K.; Wilce, Jacqueline A.; Wilce, Matthew C. J.

2011-01-01

The successful preparation of a mutant KH domain representing the first KH domain of PCBP1 and its crystallization in complex with a C-rich DNA are reported. This structure is anticipated to provide high-resolution information that will allow better understanding of the basis of cytosine specificity by PCBPs. Polycytosine-binding proteins (PCBPs) are triple KH-domain proteins that play an important role in the regulation of translation of eukaryotic mRNA. They are also utilized by viral RNA and have been shown to interact with ssDNA. Underlying their function is the specific recognition of C-rich nucleotides by their KH domains. However, the structural basis of this recognition is only partially understood. Here, the preparation of a His-tagged KH domain is described, representing the first domain of PCBP1 that incorporates a C54S mutation as well as the addition of a C-terminal tryptophan. This construct has facilitated the preparation of highly diffracting crystals in complex with C-rich DNA (sequence ACCCCA). Crystals of the KH1–DNA complex were grown using the hanging-drop vapour-diffusion method in 0.1 M phosphate–citrate pH 4.2, 40%(v/v) PEG 300. X-ray diffraction data were collected to 1.77 Å resolution and the diffraction was consistent with space group P2 1 , with unit-cell parameters a = 38.59, b = 111.88, c = 43.42 Å, α = γ = 90.0, β = 93.37°. The structure of the KH1–DNA complex will further our insight into the basis of cytosine specificity by PCBPs

Design of the WWER-440 pressurizer

International Nuclear Information System (INIS)

Bednarek, L.

1978-01-01

The main specifications are presented of a pressurizer for the WWER-440 reactor as are factors securing operating reliability and the required life of the equipment. Ferritic-pearlite steel 22K is the basic material for the manufacture of the shell, support and couplings. The internal parts and the heads are manufactured from the 08KH18N10T chromium-nickel austenitic steel, the bolts and nuts of manholes from chromium-molybdenum steels 25KH1MF and 25KH2MFA. Quality testing of basic materials and quality control during the process of manufacture are briefly described. (Z.M.)

On effect of some thermodeformation parameters of welding cycle on tendency of pearlitic heat-resisting steels to fracture in reheating

International Nuclear Information System (INIS)

Prokhorov, N.N.; Bardokin, E.V.

1979-01-01

Studied is the inclination of the 12Kh1MF, 15Kh3M1F and N18K9M5T steels subject to thermodeformation cycle imitating a welding one, to fracture in reheating. A hot-rolled metal then subject to the same thermal treatment was used. The imitation of thermodeformation cycle of the welding permitted to vary maximum heating temperatures, the period during which the metal is kept at temperatures higher than 1100 deg C, and the cooling rate of ajacent zone metal. It is shown that the curve of the dependence of deformation ability and the tendency to fracture at the reheating of adjacent zone metal on the rate of its cooling at welding is U-shaped. Deformation ability has its maximum value at the cooling rate of 30 deg c/s in the range 1300 to 1000 deg C

Comparative assessment of microstructure and texture in the Fe-30.5Mn-8.0Al-1.2C and Fe-30.5Mn-2.1Al-1.2C steels under cold rolling

Directory of Open Access Journals (Sweden)

Fabrício Mendes Souza

Full Text Available Abstract Investigation of microstructure and texture has been done for cold rolled Fe-30.5Mn-8.0Al-1.2C (8Al and Fe-30.5Mn-2.1Al-1.2C (2Al (wt.% steels. They were rolled to a strain of ~0.70. Refinement of a crystallographic slip band substructure in low to medium rolling strain and nucleation of twins on the mature slip bands at a higher strain were suggested as deformation mechanisms in the 8Al steel. Mainly shear banding contributed to the formation of a Copper texture in such steel. Brass-texture development in the 2Al steel is mainly due to deformation twinning and shear banding formation. Detailed images of KAM maps showed that the stored deformation energy was mainly localized in the twinned areas and shear bands, which generated the inhomogeneous deformation microstructures in both steels at a higher strain. Goss and Brass texture intensity decreases and Cu-texture intensity increases as the Al wt.% increases in different cold rolled High-Mn (Mn ~30 wt.% steels.

Effect of partial oxygen pressure on physicochemical properties of Kh18N10T steel at isothermal oxidation

International Nuclear Information System (INIS)

Alekseev, V.N.; Oshe, E.K.; Fokin, M.N.; Bogdanova, S.V.; Loskutov, A.I.

1990-01-01

Auger-electron spectroscopy, photoelectric polarization, conductometry methods have been used to analyze chemical and defect composition of surface oxide layers, formed on stainless steel Kh18N10T in vacuum (10 -9 - 10 -2 torr) and at temperatures 593-673 K. The boundary conditions of manifestation of extermal behaviour of the dependence of the surface oxide growth rate at isothermal oxidation of this steel are determined. The relation between passivation properties of the surface oxide and the magnitude of the edge angle of the surface wetting with molten tin is revealed

Effect of smelt aluminium on mechanical properties of steels

International Nuclear Information System (INIS)

Ryabov, V.R.; Dykhno, I.S.; Deev, G.F.; Karikh, V.V.

1987-01-01

Effect of smelt aluminium on mechanical properties of armco-iron and 12 Kh18N10T steel is studied. It is stated that in smelt aluminium and aluminium alloy contact with armco-iron the sample ductility is decreased. Corrosion effect of smelt alluminium on (18Kh15N5AM3) steel in the form of reinforced wire in aluminium-steel KAS-1A composite material is investigted. It is stated in experiment that during smelt alluminium-steel contact interaction of heterogeneous phases takes place

Smelting of high-quality boiler steel in large-load arc furnaces

Energy Technology Data Exchange (ETDEWEB)

Kablukovskij, A F; Breus, V M; Tyurin, E I; Khristich, V D; Dumchev, Ya P [Tsentral' nyj Nauchno-Issledovatel' skij Inst. Chernoj Metallurgii, Moscow (USSR)

1975-02-01

High-grade steel can be obtained in large-capacity furnaces if the smelting technology used takes account of the size of the aggregates, the course of the metal fusion process, interaction with slag, furnace atmosphere, reducing agents, and other process characteristics. 12Kh1MF boiler steel smelted in a 100-ton electric arc furnace by an oxidizing process with oxygen bath blow and cast by the siphon method into 6.5-ton ingots using a slag-forming mixture (240 mm diameter billets and 219 to 245 mm diameter tubes) is satisfactory with regard to macro and microstructure, oxygen and nonmetallic oxide inclusion content, and mechanical properties. The stress rupture strength of 10/sup 5/ h at 570/sup 0/C is similar to that of open-hearth steel. Sulfides larger than a 3.5 spheroid have been detected in it. The nitrogen content of the electric steel is 0.0090 to 0.0120%, which is somewhat greater than usual in open-hearth metal. Of the oxygen inclusions in the steel, spinel-alumina predominates. Large inclusions were represented mainly by brittle silicates which appeared to be of exogenous origin.

Regulation of Blood Pressure by Targeting CaV1.2-Galectin-1 Protein Interaction.

Science.gov (United States)

Hu, Zhenyu; Li, Guang; Wang, Jiong-Wei; Chong, Suet Yen; Yu, Dejie; Wang, Xiaoyuan; Soon, Jia Lin; Liang, Mui Cheng; Wong, Yuk Peng; Huang, Na; Colecraft, Henry M; Liao, Ping; Soong, Tuck Wah

2018-04-12

Background -L-type Ca V 1.2 channels play crucial roles in regulation of blood pressure. Galectin-1 (Gal-1), has been reported to bind to the I-II loop of Ca V 1.2 channels to reduce their current density. However, the mechanistic understanding for the down-regulation of Ca V 1.2 channels by Gal-1, and whether Gal-1 plays a direct role in blood pressure regulation remain unclear. Methods - In vitro experiments involving co-IP, western blot, patch-clamp recordings, immunohistochemistry and pressure myography were used to evaluate the molecular mechanisms by which Gal-1 down-regulates Ca V 1.2 channel in transfected HEK 293 cells, smooth muscle cells, arteries from Lgasl1 -/- mice, rat and human patients. In vivo experiments involving delivery of Tat-e9c peptide and AAV5-Gal-1 into rats were performed to investigate the effect of targeting Ca V 1.2-Gal-1 interaction on blood pressure monitored by tail cuff or telemetry methods. Results -Our study reveals that Gal-1 is a key regulator for proteasomal degradation of Ca V 1.2 channels. Gal-1 competed allosterically with Ca V β subunit for binding to the I-II loop of Ca V 1.2 channel. This competitive disruption of Ca V β binding led to Ca V 1.2 degradation by exposing the channels to poly-ubiquitination. Notably, we demonstrated that the inverse relationship of reduced Gal-1 and increased Ca V 1.2 protein levels in arteries was associated with hypertension in hypertensive rats and patients, and Gal-1 deficiency induces higher blood pressure in mice due to up-regulated Ca V 1.2 protein level in arteries. To directly regulate blood pressure by targeting the Ca V 1.2-Gal-1 interaction, we administered Tat-e9c, a peptide that competed for binding of Gal-1, by a mini-osmotic pump and this specific disruption of Ca V 1.2-Gal-1 coupling increased smooth muscle Ca V 1.2 currents, induced larger arterial contraction and caused hypertension in rats. In contrasting experiments, over-expression of Gal-1 in smooth muscle by a

Topic 1. Steels for light water reactor pressure vessels

International Nuclear Information System (INIS)

Brumovsky, M.; Brynda, J.; Kepka, M.; Barackova, L.; Vacek, M.; Havel, S.; Cukr, B.; Protiva, K.; Petrman, I.; Tvrdy, M.; Hyspecka, L.; Mazanec, K.; Kupca, L.; Brezina, M.

1980-01-01

Part 1 of the Proceedings consists of papers on the criteria for the selection and comparison of the properties of steel for pressure vessels and on the metallurgy of the said steels, the selection of suitable material for internal tubing systems, the manufacture of high-alloy steels for WWER components, the mechanical and metallurgical properties of steel 22K for WWER 440 pressure components, and of steel 10MnNi2Mo for the WWER primary coolant circuit, and the metallographic assessment of steel 0Kh18N10T. (J.P.)

ANC of 6.92 MeV (2"+) and 7.12 MeV (1"-) states from sub-Coulomb "1"2C("6Li,d) data

International Nuclear Information System (INIS)

Mondal, Ashok; Basu, C.; Adhikari, S.

2016-01-01

The determination of the astrophysical S-factor of the "1"2C(α,γ) reaction at 300 keV requires a R-matrix extrapolation. This is because a direct measurement of this reaction at 300 keV is almost impossible due to the very small cross-section. The R-matrix extrapolation requires as input the asymptotic normalization constant (ANC) of mainly two "1"6O states states viz. 6.92 MeV and 7.12 MeV on which the fit is most sensitive. The ANC of these two states have been determined from indirect measurements, mainly from "1"2C("6Li,d) and "1"2C("7Li,t) alpha transfer reactions. Most of these measurements are done at above barrier energies as cross-sections are larger. In this work, we determine the ANC of the 6.92 MeV and 7.12 MeV states of "1"6O using the "1"2C("6Li,d) data of Heikkinen et al measured at 4.5 to 5.0 MeV incident energies. The data spans over a larger angular span in comparison to Avila though the former data do not cover the very backward angles as in the Avila data. As the Heikkinen data has never been analyzed to extract the ANC we report the results of our analysis of the data

Changes in structure and phase composition of chromium diffusion layer on stainless steels after long annealing

International Nuclear Information System (INIS)

Knyazev, E.V.; Voshedchenko, B.M.; Voskresenskij, Yu.A.

1985-01-01

A study was made on the effect of elevated temperatures UU and long holdings at heat on structure, phase composition and properties of chromium diffusion layer on austenitic chromium-nickel stainless steels 10Kh18N10TVD, 10Kh15N30M4B, 10Kh11N23T3MR, 10Kh21N28V6M3. The following mechanism of processes taking place in diffusion chromium layer is presented. The steady drop of chromium concentrations is observed after diffusion saturation. Chromium redistribution related with system transformation to more equilibrium state and simultaneous decarburization of steel surfaces takes place in diffusion layers of 10Kh15N30M4B and 10Kh21N28V6M3 steels after annealing at different temperatures and holdings at heat. Decarburization of steel surface layers is practically excluded in diffusion layers of 10Kh18N10T-VD and 10Kh11N23T3MR steels. Diffusion chromium-saturated layer stays effective only on 10Kh18N10T-VD and 10Kh11N23T3MR steels on heating up to 1000 deq C with holding up to 250 h

Effect of neutron irradiation on the properties of the repair welds of the 15Kh2MFA steel

International Nuclear Information System (INIS)

Morozov, A.M.; Khachaturyants, L.V.

1986-01-01

The authors studied the effect of neutron irradiation on the tendency of the metal belonging to the heat affected zone of the weld toward brittle fracture (an increase in the critical temperature of brittleness). For comparison, the authors studied the radiation embrittlement of the original base metal (steel 15Kh2MFA) subjected to the conventional heat treatment of the reactor frames consisting of hardening and high-temperature tempering. Along with these materials, the radiational embrittlement of the base metal in the rehardened condition without tempering was studied. It was concluded that the presence of the regions repaired according to this technology and located in the frame at the level of the reactor core does not pose the problem of decreased resistance to brittle fracture

Preliminary tension effect on low-cycle fatigue of 40Kh13 steel in gaseous hydrogen

International Nuclear Information System (INIS)

Romaniv, A.N.

1984-01-01

Comparative bending tests of specimens deformed by tension at 65, 18 and 30% in hydrogen and vacuum were accomplished to reveal the effect of preliminary tension on low-cycle fatigue strength of 40Kh13 martensitic steel. It was found that small amounts of preliminary strains induced a considerable decrease in low-cycle durability in vacuum and hydrogen which was connected with developing defects arising at the early stages of plastic deformation. A rather high degree of preliminary tension promoted steel homogenization, hydrogen embrittlement decrease and service behaviour improvement

Coarsening of (Fe, Cr)23C6 carbide phase on the tempering of 14Kh17N2 chromium-nickel steel

International Nuclear Information System (INIS)

Psarev, V.I.

2002-01-01

Paper lists the results of computer analysis of distribution according to sizes (Fe, Cr) 23 C 6 microparticles resulting from 14Kh17N2 steel tempering under 700 Deg C. Data were obtained at the maximum beneficial magnification of a light microscope. The mentioned curves of distribution densities are characterized by more reliable run from most permissible sizes of dispersed particles. Application of general rules of distributions and of previously elaborated procedure to identify experimental histograms with theoretical distributions enables to derive valuable information on dynamics of coarsening of a disperse phase in this case, as well [ru

Reliability of non-heated tube bends of boilers

International Nuclear Information System (INIS)

Bugaj, N.V.; Akhremenko, V.L.; Zamotaev, V.S.

1984-01-01

Bend failures are described for non-heated boiler tubes of 12Kh1MF and 20 steels. Methods of reliability evaluations are presented which permit revealing and replacing the bends with inadequate resources. Influences of operation conditions on bend durability is shown as well as the factors which are dominating at bend failures

Long-term Stability of 9- to 12 % Cr Steels

DEFF Research Database (Denmark)

Hald, John

2004-01-01

In the recent 25 years creep rupture strength of 9- to 12 %Cr steels for steam pipes and turbines has been doubled by development of new alloys. This development has formed a basis for improved efficiency of fossil fired steam power plants by introduction of advanced steam temperatures...... and pressures. Newly developed steam pipe steels are based on modifications of well-established steels like the X 20CrMoV12 1. Balanced addition of V, Nb and N to a 9Cr 1 Mo steel led to the Modified 9 Cr steel P 91. Addition of 1% W to a 9Cr 1 MoVNbN base composition led to steel E 911 and partial replacement...... of Mo with 1.8 % W combined with a slight amount of Boron led to steel P 92. The creep rupture strength of these new alloys are now secured with long-term tests up to 100,000 hours, which demonstrate improvements of 50% (P 91), 75 % (E 911) and 100 % (P 92) in strength compared to X 20CrMoV12 1....

Effect of boron control of environment on corrosion and resistance to low-cycle corrosion fatigue in structural steels

International Nuclear Information System (INIS)

Babej, Yu.I.; Zhitkov, V.V.; Zvezdin, Yu.I.; Liskevich, I.Yu.; Nazarov, A.A.

1982-01-01

Tests of the specimens on total, contact and crevice corrosion, corrosion cracking and low-cycle fatigue are conducted for determination of corrosion and corrosion-fatigue characteristics in the 15Kh3NMFA, 10N3MFA, 10Kh16N4B, 05Kh13N6M2 structural steels, used in energetics. The environment is subjected to boron control and contacting with atmosphere for simulation of stop and operation modes of the facility. The experiments are carried out in the distilled water with 12g/l H 3 BO 3 and 10 mg/l Cl' at 25, 60, 100 deg C under contacting with atmosphere. It is established, that the pearlitic steels 15Kh3NMFA, 10N3MFA, as well as transition and martensitic 05Kh13N6M2 and 10Kh16N4B steels are highly stable to total, crevice and contact corrosion at the high parameters of aqueous boron-containing medium. Steel resistance to low-cycle fracture decreases slightly under the conditions similar to the operation ones, in the water with 12 g/l H 3 BO 3 . Durability of the pearlitic steels at the simulation of stop conditions decreases more noticeably, crack formation as a rule, initiating from corrosion spots

Corrosion behaviour of stainless steels by internal friction method

International Nuclear Information System (INIS)

Postnikov, V.S.; Kovalevskij, V.I.

1987-01-01

Corrosion of austenite chromium-nickel stainless steels 12 Kh18N9, 12Kh18N9T, 12Kh18N10 and 12Kh18N10T is investigated. Wire samples 0.7...0.8 mm in diameter before tests were subjected to quenching in water from the temperature of 1050...1100 deg C and part of them - to tempering at 650 deg C for 2 h. Pitting corrosion was brought about by different concentration of iron chloride solutions (C FeCl 3 ). Total corrosion has a slight effect on the character of IF (internal friction) variation that increases without the whole test period up to the moment when mechanical strength of the sample

Effect of Cr, Ni, and Mo additions on the susceptibility of the 0Kh6n7m7c steel to hot cracking

International Nuclear Information System (INIS)

Tolstykh, L.G.; Pryakhin, A.V.; Popov, A.N.; Usynin, V.F.

1977-01-01

The effect of chromium, molybdenum, and nickel on the tendency of surfacing materials to form hot cracks (Vsub(kp) was studied using the mathematical statistics method. The St3 steel and 38KhN3MFA steel were used in the study. A device facilitating the hot cracking tendency test procedure was developed. It was found that, in the concentration range involved, Ni and Mo produce no effect on Vsub(kp), and Cr enhances it. A new powder wire, PP-OKh7N8M6S, capable of increasing surface material resistance by 1.5-2 times, has been developed

Development and industrial mastering hot rolling procedure for low-ductile steels and alloys

International Nuclear Information System (INIS)

Degterenko, V.K.; Sokolov, V.A.

1980-01-01

The technique for the development of the sheet hot rolling procedure for low-ductile steels and alloys (0Kh17N14M2, 12Kh21N5T, 20Kh25N20C2,40Kh13, 36NKhTYu etc.) is proposed, using plastometer which permits to obtain the data on the deformation resistance in the wide range of temperatures (800-1300 deg C), of deformation degrees (0.1-0.3) and deformation rates (0.001-300 c -1 ). With the help of the plastometric data processed on the computer the calculation of the rolling regimes for the sheet with improved surface quality is carried out at the more uniform loading on the mill stands

Investigation into the Cyclic Strength of the Bodies of Steam Shutoff Valves from 10Kh9MFB-Sh Steel

Science.gov (United States)

Skorobogatykh, V. N.; Kunavin, S. A.; Prudnikov, D. A.; Shchenkova, I. A.; Bazhenov, A. M.; Zadoinyi, V. A.; Starkovskii, G. L.

2018-02-01

Steam shutoff valves are operated under complex loading conditions at thermal and nuclear power stations. In addition to exposure to high temperature and stresses resulting in fatigue, these valves are subjected to cyclic loads in heating-up-cooling down, opening-closing, etc. cycles. The number of these cycles to be specified in designing the valves should not exceed the maximum allowable value. Hence, the problem of cyclic failure rate of steam shutoff valve bodies is critical. This paper continues the previous publications about properties of the construction material for steam shutoff valve bodies (grade 10Kh9MFB-Sh steel) produced by electroslag melting and gives the results of investigation into the cyclic strength of this material. Fatigue curves for the steal used for manufacturing steam shutoff valve bodies are presented. The experimental data are compared with the calculated fatigue curves plotted using the procedures outlined in PNAE G-002-986 and RD 10-249-98. It is confirmed that these procedures may be used in designing valve bodies from 10Kh9MFB-Sh steel. The effect of the cyclic damage after preliminary cyclic loading of the specimens according to the prescribed load conditions on the high-temperature strength of the steel is examined. The influence of cyclic failure rate on the long-term strength was investigated using cylindrical specimens with a smooth working section in the as-made conditions and after two regimes of preliminary cyclic loading (training) at a working temperature of 570°C and the number of load cycles exceeding the design value, which was 2 × 103 cycles. The experiments corroborated that the material (10Kh9MFB-Sh steel) of the body manufactured by the method of electroslag melting had high resistance to cyclic failure rate. No effect of cyclic damages in the metal of the investigated specimens on the high-temperature strength has been found.

Low-temperature cyclic cracking resistance of Fe-Cr-Ni and Fe-Cr-Mn steels welded joints

International Nuclear Information System (INIS)

Ostash, O.P.; Zhmur-Klimenko, V.T.; Yarema, S.Ya.; Yushchenko, K.A.; Strok, L.P.; Belotserkovets, V.I.

1983-01-01

Results of further investigations into regularities of development of low-temperature fatigue fracture of welded oints in 07Kh13G20AN4 steel are presented, they are compared with analogous data traditional cryogenic 0Kh18N10T and 03Kh13AG19 steels. Welded joints have been prepared by means of automatic V-like level arc Welding of plates; 0Kh18N10T and 07Kh13G20AN4 steels have been welded by means of sv-04Kh19N9 wire, 03Kh13AG19 steel-by means of sv-07Kh13AG19 wire. Tests at almost zero (asymmetry coefficient R=0.05) cycle of extension at 15-20 Hz frequency have been conducted on 5 mm thick disk samples at 20 deg C and - 160 deg C according to the given methods. It is shown that by cyclic crack resistance of welded joint zones of 0Kh18N10T steel and chromium-manganese steels at normal temperature the 07Kh13G20AN4 steel exceeds 0Kh18N10T steel, at low temperature it yields to 0Kh18N10T only by fracture toughness of heat affected zones HAZ and weld metal (ne). 07Kh13G20AN4 steel and its welded joints as most hardened and cheap may be a good substituent for 0Kh18N10T steel. Optimization of WM alloying for increase of its cyclic fracture toughness at cryogenic temperatures is necessary

Evaluation of the material in creep-exposed critical 12Cr-1Mo-V ferritic steel components of the pressure section of power plant steam boilers

International Nuclear Information System (INIS)

Dobrzanski, J.

2002-01-01

Metallographic examinations were carried out on ferritic 12Cr-1Mo-V steel with tempered martensite structure after 68,000 - 145,000 hr service in creep conditions. Structural evolution related to the form of martensite, carbide precipitation and internal damage due to long-term action of thermally activated processes was discussed. A generalised scheme of structural evolution and progress of the internal damage was developed in correlation with the life exhaustion ratio. Principles of the classification for ferritic 12Cr-1Mo-V steel after long-term-service were proposed together with the method for evolution of the state of the material for the industrial practice. (author)

Nitrogen effect on the tendency of Cr-Ni-MN steels to delayed fracture under stress and hydrogen effects

International Nuclear Information System (INIS)

Suvorova, S.O.; Fillipov, G.A.

1996-01-01

Austenitic steels types 03Kh17N16G10AM5, 03Kh6N12G10AM5 and 07Kh13AG20 with various nitrogen contents were studied for their tendency to delayed fracture using mechanical tests, fractography and X ray diffraction analysis. The steel type 07Kh13G20 exhibited the highest strength in the initial state but showed an increase tendency to delayed fracture after hydrogenation. It is underlined that nitrogen additions essentially intensify the tendency of cold worked steels to delayed fracture. This fact should be taken into account when using nitrogen-containing Cr-Ni-Mn steels under severe operational conditions. 4 refs., 2 tabs

Plasticity of low carbon stainless steels

International Nuclear Information System (INIS)

Bulat, S.I.; Fel'dgandler, Eh.G.; Kareva, E.N.

1975-01-01

In the temperature range 800-1200 0 C and with strain rates of from 10 -3 to 3 s -1 , austenitic (000Kh18N12) and austenitic-ferrite (000Kh26N6) very low carbon stainless steels containing 0.02-0.03% C exhibit no higher resilience than corresponding ordinary steels containing 0.10-0.12% C. However, the plasticity of such steels (particularly two-phase steels) at 900-1100 0 C is appreciably inferior owing to the development of intergranular brittle fracture. Pressure treatment preceded by partial cooling of the surface to 850 0 C yields rolled and forged products with acceptable indices but is inconvenient technically. At the Zlatoustovsk and Ashin metallurgical plants successful tests have been performed involving the forging and rolling of such steels heated to 1280-1300 0 C without partial cooling; it was necessary to improve the killing conditions, correct the chemical composition (increasing the proportion of ferrite) and take measures against heat loss. (author)

Tantalum-containing Z-phase in 12%Cr martensitic steels

DEFF Research Database (Denmark)

Danielsen, Hilmar Kjartansson; Hald, John

2009-01-01

Z-phases in tantalum-containing 12%Cr steels have been investigated. In 12%Cr steel without any Nb or V, the formation of CrTaN Z-phases was observed. In 12%Cr steel which also contained V, the Ta entered Z-phase as a minor element, Cr(V,Ta)N. The crystal structure of Cr(V,Ta)N seems to be identi......Z-phases in tantalum-containing 12%Cr steels have been investigated. In 12%Cr steel without any Nb or V, the formation of CrTaN Z-phases was observed. In 12%Cr steel which also contained V, the Ta entered Z-phase as a minor element, Cr(V,Ta)N. The crystal structure of Cr(V,Ta)N seems...

Analysis of nature of brazed joints fracture under operating conditions

International Nuclear Information System (INIS)

Orlov, A.V.; Gura, P.M.

1985-01-01

Technique establishing causes leading to brazed joint fracture in pressure boundary components, operating under heavy conditions of high temperature and corrosive medium is described. Some cases of tube brazed joint fractures in a superheater of 12Kh1MF and 08Kh18N10T steels are considered. The attention is paid on using metallography for determination of mechanical or corrosion fracture properties. The diagram is developed permitting to take into account the interrelation between the fracture area in the given zone and its strength

Appi - tarbijast võlgnik kolis välismaale! : kommentaar Riigikohtu lahenditele asjades 3-2-1-114-12 ja 3-2-1-123-12 / Karin Sein

Index Scriptorium Estoniae

Sein, Karin, 1974-

2013-01-01

Riigikohtu lahendist 3-2-1-114-12, milles vaieldi füüsilisest isikust võlgniku pankroti väljakuulutamise kohtualluvuse üle. Lahendist 3-2-1-123-12, milles vaieldi, kas ja millistel tingimustel on Eesti kohus pädev läbi vaatama hagi Eestist lahkunud tarbijast krediidisaaja vastu

Effect of heat treatment on the impact properties of a 12Cr-1Mo-V-W steel

International Nuclear Information System (INIS)

Chin, B.A.; Wilcox, R.C.

1983-01-01

This paper describes the effects of austenitization and tempering treatments on the strength and impact properties of a 12Cr-1Mo-V-W steel. Data are reported for austenitization temperatures covering the range 900 to 1250 0 C and tempering treatments of 600 to 800 0 C. A 50 0 C improvement in the ductile brittle transition temperature is achieved through heat treatment. This is found to result from elimination of delta ferrite and associated carbides at the delta ferrite-matrix interface. 17 figures

Durability of bends in high-temperature steam lines under the conditions of long-term operation

Science.gov (United States)

Katanakha, N. A.; Semenov, A. S.; Getsov, L. B.

2015-04-01

The article presents the results of stress-strain state computations and durability of bent and steeply curved branches of high-temperature steam lines carried out on the basis of the finite element method using the modified Soderberg formula for describing unsteady creep processes with taking the accumulation of damage into account. The computations were carried out for bends made of steel grades that are most widely used for manufacturing steam lines (12Kh1MF, 15Kh1M1F, and 10Kh9MFB) and operating at different levels of inner pressure and temperature. The solutions obtained using the developed creep model are compared with those obtained using the models widely used in practice.

On the adsorption-induced fatigue of structural steels in the presence of alcohols

International Nuclear Information System (INIS)

Loboiko, V.I.; Karpenko, G.V.; Vasilenko, I.I.

1976-01-01

The purpose of the work was to study he effect of anhydrous alcohols on the cyclic fatigue of steels in the absence of contact of the alcohol with atmospheric moisture during the testing process. A vacuum was created in the operating space and then the vacuum annealing was carried out in a bath with the sample and through metal vacuum connection the bath was filled with anhydrous alcohol. Studies were made on several construction steels (20Kh, 40Kh, 50Kh, and ShKh15); steels 40Kh, 50Kh, and ShKh15 were quenched from 840-860 0 C in oil and then tempered at 200 0 C (2 h), steel 20Kh was studied in the as-received state. It was shown that with increase in the carbon content of steel with a martensite structure, the decrease in strength in the presence of anhydrous alcohol was greater than in dry air. Experiments showed that anhydrous alcohol causes an adsorption decrease in the strength both of samples with preliminarily formed cracks and V-shaped stress concentrators and of smooth samples. The greatest adsorption effect of alcohols in our case, as in static fatigue, was observed in samples with cracks. A dependence was shown between the length of the carbon chain and the fatigue limit. This dependence indicates the monotone nature of the decrease in the fatigue limit with transfer from methyl to butyl and then to octyl alcohol

Dielectron spectroscopy at 1-2 AGeV with HADES

International Nuclear Information System (INIS)

Spataro, S.; Agakishiev, G.; Destefanis, M.; Gilardi, C.; Kirschner, D.; Kuehn, W.; Lange, J.S.; Metag, V.; Mishra, D.; Novotny, R.; Pechenov, V.; Pechenova, O.; Perez Cavalcanti, T.; Spruck, B.; Wen, H.; Agodi, C.; Bellia, G.; Finocchiaro, P.; Balanda, A.; Dybczak, A.; Kozuch, A.; Michalska, B.; Otwinowski, J.; Przygoda, W.; Salabura, P.; Trebacz, R.; Wisniowski, M.; Wojcik, T.; Belver, D.; Cabanelas, P.; Castro, E.; Garzon, J.A.; Lamas-Valverde, J.; Marin, J.; Belyaev, A.; Chernenko, S.; Fateev, O.; Ierusalimov, A.; Zanevsky, Y.; Blanco, A.; Fonte, P.; Lopes, L.; Mangiarotti, A.; Boehmer, M.; Christ, T.; Eberl, T.; Fabbietti, L.; Friese, J.; Gernhaeuser, R.; Jurkovic, M.; Kruecken, R.; Maier, L.; Sailer, B.; Boyard, J.L.; Hennino, T.; Moriniere, E.; Ramstein, B.; Roy-Stephan, M.; Braun-Munzinger, P.; Galatyuk, T.; Gonzalez-Diaz, D.; Holzmann, R.; Koenig, I.; Koenig, W.; Kolb, B.W.; Lang, S.; Palka, M.; Pietraszko, J.; Rustamov, A.; Schmah, A.; Simon, R.; Sudol, M.; Traxler, M.; Yurevich, S.; Zumbruch, P.; Diaz, J.; Gil, A.; Dohrmann, F.; Grosse, E.; Kaempfer, B.; Kanaki, K.; Kotte, R.; Naumann, L.; Wuestenfeld, J.; Zhou, P.; Froehlich, I.; Heilmann, M.; Lorenz, M.; Markert, J.; Micel, J.; Muentz, C.; Pachmayer, Y.C.; Stroebele, H.; Sturm, C.; Tarantola, A.; Teilab, K.; Golubeva, M.; Guber, F.; Ivashkin, A.; Karavicheva, T.; Kurepin, A.; Lapidus, K.; Reshetin, A.; Sadovsky, A.; Veretenkin, I.; Iori, I.; Krasa, A.; Krizek, F.; Kugler, A.; Sobolev, Yu.G.; Tlusty, P.; Wagner, V.; Mousa, J.; Parpottas, Y.; Tsertos, H.; Stroth, J.

2008-01-01

The HADES spectrometer at GSI (Darmstadt) is investigating the e + e - pair production in p+p, p+A and A+A collisions. In this contribution we would like to highlight the physics motivations and the experiments performed so far, focusing mainly on the first results coming from 12 C+ 12 C collisions at 1 and 2 AGeV, and on preliminary results from p+p/d+p collisions at 1.25 AGeV. (orig.)

Structural steels for power generating equipment and heat and chemical heat treatments

International Nuclear Information System (INIS)

Astaf'ev, A.A.

1979-01-01

Development of structural steels for power generating equipment and for reactor engineering, in particular, is elucidated. Noted is utilization of the 15Kh2NMFA steels for the WWER-1000 reactor vessels, the 10GN2MFA steels for steam generators, pressurizers, vessels of the automatic emergency shut down and safety system; the 00Kh12N3DL steel for cast pump vessels and main locking bars. The recommendations on heat treatment of big forgings, for instance, ensuring the necessary complex of mechanical properties are given. Diffusion chromizing with subsequent nitriding of austenitic steels which increase durability of the components in BN reactors more than 4 times, is practised on a large scale

Regridded Harmonized World Soil Database v1.2

Data.gov (United States)

National Aeronautics and Space Administration — This data set describes select global soil parameters from the Harmonized World Soil Database (HWSD) v1.2, including additional calculated parameters such as area...

Effect of partial oxygen pressure on physicochemical properties of Kh18N10T steel at isothermal oxidation. Vliyanie partsial'nogo davleniya kisloroda na fiziko-khimicheskie svojstva poverkhnosti stali Kh18N10T pri izotermicheskom okislenii

Energy Technology Data Exchange (ETDEWEB)

Alekseev, V N; Oshe, E K; Fokin, M N; Bogdanova, S V; Loskutov, A I [AN SSSR, Moscow (USSR). Inst. Fizicheskoj Khimii

1990-10-01

Auger-electron spectroscopy, photoelectric polarization, conductometry methods have been used to analyze chemical and defect composition of surface oxide layers, formed on stainless steel Kh18N10T in vacuum (10{sup -9} - 10{sup -2} torr) and at temperatures 593-673 K. The boundary conditions of manifestation of extermal behaviour of the dependence of the surface oxide growth rate at isothermal oxidation of this steel are determined. The relation between passivation properties of the surface oxide and the magnitude of the edge angle of the surface wetting with molten tin is revealed.

Effect of nonmetallic inclusions on anisotropy of ductility in 35KhN3MFA steel forgings

International Nuclear Information System (INIS)

Shtremel', M.A.; Yavojskij, V.I.; Volkov, V.A.; Chursin, G.M.; Chukhlov, V.I.; Fetisov, G.I.; Mochalin, N.K.; Smol'yaninov, L.V.

1980-01-01

Characteristics of nonmetaltic inclusions and anizotropy of ductility and of impuct strength of forgings of the 35KhN3MFA steel are compared at different variants of melting and outer-furnace treatment. It is shown that method of melting rugulates anisotropy of ductility primarily through deformability of large inclusions during forging. Deformability of inclusions considerably changes due to introduction of silicocalcium in iron mold [ru

Dielectron spectroscopy at 1-2 AGeV with HADES

Energy Technology Data Exchange (ETDEWEB)

Spataro, S. [Istituto Nazionale di Fisica Nucleare, Lab. Nazionali del Sud, Catania (Italy)]|[Justus Liebig Univ. Giessen, II.Physikalisches Institut, Giessen (Germany); Agakishiev, G.; Destefanis, M.; Gilardi, C.; Kirschner, D.; Kuehn, W.; Lange, J.S.; Metag, V.; Mishra, D.; Novotny, R.; Pechenov, V.; Pechenova, O.; Perez Cavalcanti, T.; Spruck, B.; Wen, H. [Justus Liebig Univ. Giessen, II.Physikalisches Inst., Giessen (Germany); Agodi, C.; Bellia, G.; Finocchiaro, P. [Istituto Nazionale di Fisica Nucleare, Lab. Nazionali del Sud, Catania (Italy); Balanda, A.; Dybczak, A.; Kozuch, A.; Michalska, B.; Otwinowski, J.; Przygoda, W.; Salabura, P.; Trebacz, R.; Wisniowski, M.; Wojcik, T. [Jagiellonian Univ. of Cracow, Smoluchowski Inst. of Physics, Krakow (Poland); Belver, D.; Cabanelas, P.; Castro, E.; Garzon, J.A.; Lamas-Valverde, J.; Marin, J. [Univ. of Santiago de Compostela, Dept. de Fisica de Particulas, Santiago de Compostela (Spain); Belyaev, A.; Chernenko, S.; Fateev, O.; Ierusalimov, A.; Zanevsky, Y. [Joint Inst. of Nuclear Research, Dubna (Russian Federation); Blanco, A.; Fonte, P.; Lopes, L.; Mangiarotti, A. [LIP-Lab. de Instrumentacao e Fisica Experimental de Particulas, Coimbra (Portugal); Boehmer, M.; Christ, T.; Eberl, T.; Fabbietti, L.; Friese, J.; Gernhaeuser, R.; Jurkovic, M.; Kruecken, R.; Maier, L.; Sailer, B. [Technische Univ. Muenchen, Physik Department E12, Muenchen (Germany); Boyard, J.L.; Hennino, T.; Moriniere, E.; Ramstein, B.; Roy-Stephan, M. [Univ. Paris Sud, Inst. de Physique Nucleaire (UMR 8608), CNRS/IN2P3, Orsay Cedex (France); Braun-Munzinger, P.; Galatyuk, T.; Gonzalez-Diaz, D.; Holzmann, R.; Koenig, I.; Koenig, W.; Kolb, B.W.; Lang, S.; Palka, M.; Pietraszko, J.; Rustamov, A.; Schmah, A.; Simon, R.; Sudol, M.; Traxler, M.; Yurevich, S.; Zumbruch, P. [Gesellschaft fuer Schwerionenforschung mbH, Darmstadt (Germany); Diaz, J.; Gil, A. [Univ. de Valencia-CSIC, Inst. de Fisica Corpuscular, Valencia (Spain)] [and others

2008-11-15

The HADES spectrometer at GSI (Darmstadt) is investigating the e {sup +}e{sup -} pair production in p+p, p+A and A+A collisions. In this contribution we would like to highlight the physics motivations and the experiments performed so far, focusing mainly on the first results coming from {sup 12}C+{sup 12}C collisions at 1 and 2 AGeV, and on preliminary results from p+p/d+p collisions at 1.25 AGeV. (orig.)

Chromium surface alloying of structural steels during laser treatment

International Nuclear Information System (INIS)

Kurov, I.E.; Nagornykh, S.N.; Sivukhin, G.A.; Solenov, S.V.

1987-01-01

Results of matrix alloying from the surface layer and creation of considerably increased chromium concentration in the depth which permits to increase the efficiency of laser treatment of steels (12Kh18N10T and 38KhN3M) in the process of their further mechanical polishing, are presented. The treatment was realized by continuous CO 2 -laser at different power densities and scanning rates are presented. A model describing the creation of anomalous distributions of the alloying element in steels is plotted

Study of cast and thermo-mechanically strengthened chromium-nickel nitrogen-containing steel

International Nuclear Information System (INIS)

Prokoshkina, V.G.; Kaputkina, L.M.; Svyazhin, A.G.

2000-01-01

The effect of nitrogen on the structure and strength of corrosion-resistant chromium-nickel steels after thermal and thermomechanical treatment is studied. The 06Kh15N7AD and 07Kh15N7DAMB steels alloying by nitrogen was accomplished through the basic composition steels remelting in the molecular nitrogen atmosphere under the pressure of 0.1-2.5 MPa. The 02Kh15N5DAF and 05Kh15N5DAM steels ingots were obtained through melting in a plasma furnace under the nitrogen pressure of 0.4MPA. The high-temperature thermomechanical treatment (HTMT) was performed by rolling with preliminary blanks heating up to 1050 deg C and the rolling end temperature not below 950 deg C. It is shown, that the HTMT of the nitrogen-containing steels makes it possible to obtain strength characteristics by 1.5 times exceeding the properties of traditionally applicable corrosion-resistant steels, whereby sufficiently high plasticity of the nitrogen-containing steel is retained [ru

Investigation of fretting corrosion of vacuum-chrome-plated vt3-1 titanium alloy in pair with unprotected vt3-1 alloy and 40khnma steel

International Nuclear Information System (INIS)

Rojkh, I.L.; Koltunova, L.N.; Vejtsman, M.G.; Birman, Ya.N.; Skosarev, A.V.; Kogan, I.S.

1978-01-01

The character of destruction of contacting surfaces in the process of fretting corrosion of titanium alloy VT3-1 chromized in vacuum in pair with unprotected alloy VT3-1 and steel 40KhNMA has been studied by scanning electron microscopy, electronography, and recording the surface profile. The specific load was 200 kg/cm 2 , vibration amplitude 50 mkm and frequency 500 Hz. It has been established that pairs unprotected with coating are subjected to intensive fretting corrosion especially when they are made of titanium alloy. For the pair chromized alloy VT3-1 - unprotected alloy VT3-1 no destruction of a chromized surface is observed. Vacuum chromium coating in the pair with steel 40KhNMA reveals similar properties as in pair with a titanium alloy. The surface of a steel sample is destroyed because of fretting corrosion, though the intensity of corrosion is lower than in the case of unprotected pairs. Vacuum chromium coating is recommended for protection of titanium alloy VT3-1 from fretting corrosion in pair with steel 40KhNMA or an alloy VT3-1 especially in those cases when various organic coatings are unsuitable

Application of experiment planning during investigation of cementation process in solid carburizers

International Nuclear Information System (INIS)

Lisenkov, A.N.; Denisov, V.M.; Prigozhina, E.L.

1981-01-01

A mathematical model of cementation process in solid carburizirs is obtained, the most effective contents of carburizers are chosen. Specimens are produced out of St20, 12KhN3A, 40Kh13, KhVG steels. It is shown that specimens of St20 and 12KhN3A steels have the higher depth of cementated layer, specimens made of 40Kh13 and KhVG steels-the lower depth. It is shown that the quality of cementated layer structure at recommended regimes improved, cementated layer depth for low-carbon steels changed a little and for tool steels increased infficiently: for KhVG steel in 2-3 times for 40Kh13 steel in 1.5-2.5 times

Electroplastic drawing of stainless steels

International Nuclear Information System (INIS)

Troitskij, O.A.; Spitsyn, V.I.; Sokolov, N.V.; Ryzhkov, V.G.

1977-01-01

Effect of electroplastic drawing on mechanical, magnetic and electrical properties of wire of 12Kh18N10T and Kh13N13M2 steels was studied. Pulse, direct and alternating currents were used. Direct and alternating current densities were 400 A/mm 2 , mean density of pulse current was 200 A/mm 2 . The investigations have shown that the current density increase results in decreasing the wire strengthening intensity though in increasing plastic properties. As a result of electroplastic drawing the growth of magnetic characteristics of wire occurs

55-mW, 1.2-V, 12-bit, 100-MSPS Pipeline ADCs for Wireless Receivers

Science.gov (United States)

Ito, Tomohiko; Kurose, Daisuke; Ueno, Takeshi; Yamaji, Takafumi; Itakura, Tetsuro

For wireless receivers, low-power 1.2-V 12-bit 100-MSPS pipeline ADCs are fabricated in 90-nm CMOS technology. To achieve low-power dissipation at 1.2V without the degradation of SNR, the configuration of 2.5bit/stage is employed with an I/Q amplifier sharing technique. Furthermore, single-stage pseudo-differential amplifiers are used in a Sample-and-Hold (S/H) circuit and a 1st Multiplying Digital-to-Analog Converter (MDAC). The pseudo-differential amplifier with two-gain-stage transimpedance gain-boosting amplifiers realizes high DC gain of more than 90dB with low power. The measured SNR of the 100-MSPS ADC is 66.7dB at 1.2-V supply. Under that condition, each ADC dissipates only 55mW.

Stationary potentials and corrosion of metals and steels in sodium and potassium chloride eutectic melts saturated with hydrogen chloride

International Nuclear Information System (INIS)

Belov, V.N.; Ershova, T.K.; Kochergin, V.P.

1978-01-01

Stationary potentials have been measured at 850 deg C and corrosion rates found gravimetrically for a number of metals and steels in the eutectic NaCl-KCl melt saturated with HCl. Periodic shifts of the stationary potentials towards positive values have been established in the Ti-V-Cr-Fe-Ni, Cu-Zr-Nb-Mo, Ag-Ta-W-Pt systems, with the corrosion rate of metals decreasing in them. The stationary potentials are shown to shift towards positive values in the series: st.08 KP, st.3, Kh17N2, Kh22N6T, Kh13NChG9, 1Kh18N10T, Kh17N13M2T, OKh17N16M3T, Kh23N18, Kh25N16G7, Kh23N28M3D3T, with corrosive resistance in this series increasing

Creep cavity and carbide studies during creep of a 12%CrMoV-steel

Energy Technology Data Exchange (ETDEWEB)

Andersson, Henrik; Storesund, J.; Seitisleam, F.

1997-03-01

Uniaxial creep tests of a X20CrMoV 12 1 steel has been carried out. The work was performed as a follow-up on earlier investigations on a similar steel with lower creep ductility. A comparison with this previous work is included. Both interrupted and rupture tests were performed and studies were made of cavity formation processes and carbide transformations. The creep curves could be reproduced using an analytical model. No secondary creep was observed. Cavities were found to form already at a strain of 1%. The cavity density, mean diameter and cavitated area fraction were found to have a linear relationship with the strain for strains up to about 10%. The mean carbide diameter was observed to be a function of time at temperature. A small decrease in carbide density with strain was detected 12 refs, 28 figs, 6 tabs

Effect of silicon on the structure, tribological behaviour, and mechanical properties of nitrogen-containing chromium-manganese austenitic steels

International Nuclear Information System (INIS)

Korshunov, L.G.; Chernenko, N.L.; Gojkhenberg, Yu.N.

2003-01-01

The effect of silicon in quantity of 3.5-4.5 mass. % on tribological behaviour is studied for nitrogen-bearing (0.20-0.52 mass. % of nitrogen) chromium-manganese austenitic steels (10Kh15G23S4A0.20, 10Kh16G17N3S4A0.30, 10Kh19G20NS4A0.50, 12Kh19G19NS2A0.50, 10Kh18G19A0.50, 08Kh16G8N10S4A0.18). Mechanical properties and corrosion resistance of the steels are determined. Using metallographic, x-ray diffraction and electron microscopical methods a study is made into structural transformations running in the steels considered under friction and static tension. It is shown that additional silicon alloying of nitrogen-bearing chromium-manganese austenitic steels results in an essential increase of adhesion wear resistance of the materials on retention of low friction coefficient (f=0.25-0.33). A strong silicon effect on steel tribological behaviour is related with planar slip activation and with an increase of austenite strength and heat resistance [ru

Role of a guanine nucleotide-binding protein in α1-adrenergic receptor-mediated Ca2+ mobilization in DDT1 MF-2 cells

International Nuclear Information System (INIS)

Cornett, L.E.; Norris, J.S.

1987-01-01

In this study the mechanisms involved in α 1 -adrenergic receptor-mediated Ca 2+ mobilization at the level of the plasma membrane were investigated. Stimulation of 45 Ca 2+ efflux from saponin-permeabilized DDT 1 MF-2 cells was observed with the addition of either the α 1 -adrenergic agonist phenylephrine and guanosine-5'-triphosphate or the nonhydrolyzable guanine nucleotide guanylyl-imidodiphosphate. In the presence of [ 32 P] NAD, pertussis toxin was found to catalyze ADP-ribosylation of a M/sub r/ = 40,500 (n = 8) peptide in membranes prepared from DDT 1 , MF-2 cells, possibly the α-subunit of N/sub i/. However, stimulation of unidirectional 45 Ca 2+ efflux by phenylephrine was not affected by previous treatment of cells with 100 ng/ml pertussis toxin. These data suggest that the putative guanine nucleotide-binding protein which couples the α 1 -adrenergic receptor to Ca 2+ mobilization in DDT 1 MF-2 cells is not a pertussis toxin substrate and may possibly be an additional member of guanine nucleotide binding protein family

Local corrosion of high alloy steels under biodeposits

International Nuclear Information System (INIS)

Korovyakova, M.D.; Nikitin, V.M.; Speshneva, N.V.

1999-01-01

Impact of the bacteriozenosis different structural-functional state under biodeposits on corrosion resistance of the 12Kh18N10T and Kh18N10T high-alloy steels in the natural seawater is studied. It is shown that saturation of natural micro communities by separate aerobic and facultative-anaerobic bacterial monocultures increases corrosion resistance of these steels by their overgrow with biodeposits [ru

The effect of laser treatment on the wear resistance of steel in corrosive media

International Nuclear Information System (INIS)

Plyatsko, G.V.; Porter, A.I.; Prejs, G.A.; Mojsa, M.I.

1975-01-01

The corrosion mechanical wearing properties of steel 45 treated with a laser beam (H 100 =7800 Mn/sq.m) under friction with nitrated steel 40KhNMA (HV=7000 Mn/sq.m), chrome cast iron Kh15M (hardened and low-temperature tempered, modified), perlite cast iron and bronze are studied. The aqueous buffers with pH=6 and 11 are used as a corrosion active media. In a weakly acid medium the most intensive wearing of steel 40KhNMA is observed at P=8 Mn/sq.m. Its wearing reduces due to increase of pressure to 12 Mn/sq.m. Extent of steel 45 wearing increases with pressure increase from 8 to 12 Mn/sg.m. Friction coefficient of this pair changes by jumps at an increase of normal pressure and its variation range is smaller than that observed in an alkaline medium. The maximum value of friction coefficient is shifted to the higher pressure. The wearing of cast iron Kh15M-steel 45 pair has an alternative pattern. In an alkaline medium the cast iron wearing intensity shows a linear increase with the normal contact pressure but that of the steel changes jumpwise attaining extreme at 8 and 12 Mn/sq.m. In a weak acid medium the intensity of grasping and graphitization at the friction surface of cast iron Kh15M-steel 45 pair is higher than that in the alkaline medium. Experiments demonstrate an effectiveness of the laser beam treatment of steel 45 for its friction in the alkaline medium with nitrated steel 40KhNMA and with hardened low-temperature tempered cast iron 45 under friction contact pressure as high as 8 Mn/sq.m, and in acid medium at 12 and 8 Mn/sq.m respectively. The laser treatment provides high corrosion-mechanical stability of steel 45 and the counterbodies described, as well as the low friction coefficient of these pairs

Specific features of precipitation hardening of austenitic steels with various base. 2. Kinetics and mechanism of carbide precipitation

International Nuclear Information System (INIS)

Kositsyna, I.I.; Sagaradze, V.V.; Khakimova, O.N.

1997-01-01

Electron microscopic studies were carried out to determine the kinetics and mechanisms of precipitation hardening in Fe-Mn, Fe-Mn-Cr, Fe-Cr-Mn-N, Fe-Cr-Ni and Fe-Ni base stainless steels (45G20M2F2, 50Kh16G15N6M2F2, 45Kh18N10G10M2F2, 40Kh18Ni18M2F2, 45N26M2F2). The steels were heat treated under various conditions. It is revealed that in manganese steels the particles of vanadium carbide nucleate according to homogeneous mechanism at all aging temperatures (600-750 deg C). The presence of chromium in the matrix promotes the transition to heterogeneous mechanism of carbide nucleation and growth. With nickel content increasing the plasticity of precipitation hardened steels gets better due to more intense diffusion of atoms and vacancies to grain boundaries and, hence, the widening of near-boundary zones free of carbide particles

Effect of austenitization conditions on kinetics of isothermal transformation of austenite of structural steels

International Nuclear Information System (INIS)

Konopleva, E.V.; Bayazitov, V.M.; Abramov, O.V.; Kozlova, A.G.

1987-01-01

Effect of austenization of kinetics of pearlite and bainite transformations for steels with different carbon content differing by alloying character and degree has been investigated. Austenization temperature increase is shown to leads to retardation of ferrite-pearlite transformation in low- and medium-carbon alloyed steels. Step-like holding in the region of austenite stable state (850, 950 deg) after high-temperature heating (1100 deg C) increases the rate of transformation partially recovering its kinetics and decomposition velocity after low-temperature heating in steels alloyed advantageously with carbide-forming elements (08Kh2G2F, 30Kh3) and does not affect kinetics in the 35Kh, 30KhGSN2A, 45N5 steels. Increase of heating temperature and growth of an austenite grain cause considerable acceleration of bainite transformation, increase of the temperaure of bainite transformation beginning and increase of the transformation amplitude in the 08Kh2G2F, 30Kh3 steels and affect weakly kinetics in steels with mixed alloying (30KhGSN2A) or low-alloy one (35Kh). The bainite transformation rate in the 45N5 steelite does not depend on austenization. The effect of additional acceleration of bainite transformation as a result holding after high-temperature heating in those steels, where activation of transformation occurs with increase of heating temperature

Optimal control of conditions of deformation during rolling the bar alloy from alloy steel

International Nuclear Information System (INIS)

Inatovich, Yu.V.; Shilov, V.A.; Shvarts, D.L.; Kudelin, S.P.

2001-01-01

A complex of programs for determining the optimal gaps between rollers during rolling of simple merchant sections of alloy steels of a wide brand assortment (12KhN3A, Kh17N2, Kh18N10T) was elaborated. Experience in calculations made according to the programs suggests advisability of their use in the automated design systems for roller calibration and for adjustment of section mills [ru

Steel corrosion in tributyl phosphate in the presence of water and ethyl mercaptan

International Nuclear Information System (INIS)

Pischik, L.M.; Tsinman, A.I.

1979-01-01

Studied is the corrosion of steels St3, 15Kh5M, 08Kh13, 10Kh14G14N4T, 08Kh18G8N2T, 10Kh17N13M2T in TBP, in mixtures of TBP with ethyl mercaptan (EM) and two-phase systems TBP-water and TBP-water-EM at 50-150 deg. In pure TBP St3 corrosion rate is low even at 150 deg. In the presence of water St 3 strongly corrodes at above 50 deg temperature in organic and water layers and also in gas phase. The steel-08Kh18G8N2T at 90 deg in acid TBP is passive and its corrosion rate is lower than 0.01 mm/year. In identical conditions the resistance of stainless steels increases together with chromium content but in TBP with acid number 100 and above at 150 deg all tested steels including steel-10Kh17N13M2T are slightly resistant. Thus, even in absence of corrosion active additions of EM the mixture of TBP-water at higher temperature is agressive in relation not only to carbon steel but also to stainless steels

Effect of laser absorption on picosecond laser ablation of Cr12MoV mold steel, 9Cr18 stainless steel and H13A cemented carbide

Science.gov (United States)

Wu, Baoye; Liu, Peng; Wang, Xizhao; Zhang, Fei; Deng, Leimin; Duan, Jun; Zeng, Xiaoyan

2018-05-01

Due to excellent properties, Cr12MoV mold steel, 9Cr18 stainless steel and H13A cemented carbide are widely used in industry. In this paper, the effect of absorption of laser light on ablation efficiency and roughness have been studied using a picosecond pulse Nd:YVO4 laser. The experimental results reveal that laser wavelength, original surface roughness and chemical composition play an important role in controlling ablation efficiency and roughness. Firstly, higher ablation efficiency with lower surface roughness is achieved on the ablation of 9Cr18 at 532, comparing with 1064 nm. Secondly, the ablation efficiency increases while the Ra of the ablated region decreases with the decrease of original surface roughness on ablation of Cr12MoV mold steel at 532 nm. Thirdly, the ablation efficiency of H13A cemented carbide is much higher than 9Cr18 stainless steel and Cr12MoV mold steel at 1064 nm. Scanning electron microscopy images reveals the formation of pores on the surface of 9Cr18 stainless steel and Cr12MoV mold steel at 532 nm while no pores are formed at 1064 nm. As to H13A cemented carbide, worm-like structure is formed at 1064 nm. The synergetic effects of the heat accumulation, plasma shielding and ablation threshold on laser ablation efficiency and machining quality were analyzed and discussed systematically in this paper.

Stainless austenitic steels strengthened due to reversible phase transformations and by ageing

International Nuclear Information System (INIS)

Sagaradze, V.V.; Kositsyna, I.I.; Ozhiganov, A.V.

1981-01-01

The effect of the reversible phase transformations, consisting in the conduction of the direct and reverse martensite transformations and aging, during which the intermetallide γ'-phase of the composition Ni 3 Ti is formed, on the streng-thening of alloys in the Fe-Cr-Ni-Ti system is considered. Stainless austenitic steels Kh12N12T3 and Kh12N14T3, which acquire high mechanical properties: σsub(0.2)=685-785 MPa, σsub(B)=1275 MPa, delta >= 20%, as a result of reversible phase transformations and aging, are suggested. After the reversible phase transformations and ageing the steels possess a high resistance to γ-α-transformation during cold treatment [ru

Water vapor pressure over molten KH2PO4 and demonstration of water electrolysis at ∼300ºC

DEFF Research Database (Denmark)

Berg, Rolf W.; Nikiforov, Aleksey Valerievich; Petrushina, Irina

2016-01-01

A new potentially high-efficiency electrolyte for water electrolysis: molten monobasic potassium phosphate, KH2PO4 or KDP has been investigated at temperatures ∼275–325 °C. At these temperatures, KH2PO4 was found to dissociate into H2O gas in equilibrium with a melt mixture of KH2PO4—K2H2P2O7—KPO3...... of water and methane or hydrogen to be 0.40 ± 0.02 or 1.2 ± 0.03. At equilibrium the vapor pressure was much lower than the vapor pressure above liquid water at the same temperature. Electrolysis was realized by passing current through closed ampoules (vacuum sealed quartz glass electrolysis cells...... with platinum electrodes and the electrolyte melt). The formation of mixtures of hydrogen and oxygen gases as well as the water vapor was detected by Raman spectroscopy. In this way it was demonstrated that water is present in the new electrolyte: molten KH2PO4 can be split by electrolysis via the reaction 2H2O...

Effect of aging on the tribological and mechanical properties of a high-nitrogen stainless austenitic steel

International Nuclear Information System (INIS)

Korshunov, L.G.; Chernenko, N.L.; Tereshchenko, N.A.; Uvarov, A.I.

2005-01-01

The effect of aging, associated with predominant precipitation of vanadium nitrides (VN), on tribological and mechanical properties of austenitic steel 10Kh18AG18N5MF hardened from 1100 Deg C is studied. Metallographic, X-ray diffraction and electron microscopical methods are used to study structural transformations proceeding in the steel on aging as well as on friction loading under conditions of dry slipping friction in steel-abrasive and steel-steel pairs. It is shown that the aging at temperatures of 600-700 Deg C resulting in a considerable increase of strength properties of the steel demonstrates a relatively weak positive effect on steel resistance to abrasive and adhesive wear. It is stated that the use of aging by continuous mechanism permits attaining favourable mechanical and tribological properties in vanadium-alloying nitrogen-bearing austenitic steels [ru

Influence of prolonged service of steam turbines on the properties of materials of rotor and vessel components

International Nuclear Information System (INIS)

Anfimov, V.M.; Artamonov, V.V.; Chizhik, T.A.

1984-01-01

The structure and mechanical properties of steam turbine elements of 25Kh1MF, 25Kh1M1FA (rotors), 15Kh1M1FL (vessel components) steels have been investigated both in initial state and after 200 000 h operation. The structure stability and phase composition of rotor steels providing conservation of heat resistance at a required level was established. Examination of vessel components showed a decrease in the yield strength by 15-20% and durability - by 10% as compared to initial ones. The conclusion on a possible prolongation of the steam turbine service life to 200 000 h is drawn. The nominal service life equals 100 000 h

The effect of chromium diffusion redistribution on wear resistance of carburized 3Kh13 steel

International Nuclear Information System (INIS)

Shcherbedinskij, G.V.; Shumakov, A.I.; Zemskij, S.V.; Pereverzev, V.M.

1977-01-01

The redistribution of chromium in steel 3Kh13 on carburization in a high-activity carburizer and the wear-resistance of the steel have been investigated. Surface layers with an increased chromium concentration show the highest wear-resistance. The chromium content in the surface layer increases due to its diffusion from the interior. The distribution of carbon and chromium in the carburized layers has been studied with the aid of the radioactive isotope 14 C by the method of layer-by-layer spectral analysis on a vacuum quantometer, layer-by-layer chemical and X-ray structure analysis. The composition of the carbides has been determined by physicochemical analysis. It has been established that the carburized layer can be divided into four zones with respect to its phase composition: first zone - hematite and spinal with 0.5-2.0% C; second zone - solid carbides (Fe,Cr) 7 C 3 ; up to 5% C; third zone - globular carbides in a troostite matrix (Cr,Fe) 7 C 3 and Cr 23 C 6 ; up to 3.5% C; fourth, transitional, zone - troostite carbide mixture Cr 23 C 6 ; up to 1% C. The chromium diffusion in the carburized layer is faster than in the initial austenite. The chromium counterdiffusion is due to the development of a zone of solid carbides M 7 C 3

Specific features of the occurrence, development, and re-compaction of spall and shear fractures in spherically-convergent shells made of unalloyed iron and some steels under their spherical explosive loading

International Nuclear Information System (INIS)

Kozlov, E.A.; Brichikov, S.A.; Gorbachev, D.M.; Brodova, I.G.; Yablonskikh, T.I.

2007-01-01

Results of comparative metallographic examination of recovered shells exposed to explosive loading in two modes (with and without a heavy casing confining explosion products scatter) are presented. The shells were made of high-purity and technical-grade unalloyed iron with the initial grain size 250 and 125 μm, steel 30KhGSA in delivery state and quenched up to HR C 35...40, austenitic stainless steel 12Kh18N10T. The heavy casing used in experiments is demonstrated to ensure a rather compact convergence of shells destroyed at high radii. In the described comparative experiments, one managed to compile the 12Kh18N10T steel shell, after it was spalled at high radii and exposed to shear fracture and spallation layer fragmentation at medium radii, into a compact sphere but failed to do the same with the 30KhGSA quenched steel shell after it was fractured according to spall and shear mechanisms at high and medium radii. Polar zones of this steel shell have obvious undercompressed areas due to significant dissipative losses to overcome the shear strength. Occurrence, development, and re-compaction of spall and shear fractures in spherically-convergent shells made of materials, which were already carefully investigated in 1D- and 2D-geometry experiments, were systematically studied in order to verify and validate new physical models of dynamic fractures, as well as up-to-date used in 1D-, 2D- and 3D-numerical algorithms [ru

Electron beam welding of flanges with tubular shafts of steel 40KhNMA

International Nuclear Information System (INIS)

Leskov, G.I.; Zhivaga, L.I.; Shipitsyn, B.N.; Savichev, R.V.

1975-01-01

The results are presented of elaborating the technological process for the electron beam welding of flanges with a tube of the 40KhNMA steel and of investigation into the quality of the welded joints. A welded piece has been fabricated conforming to the technology suggested observing the parameters worked-out in the following sequence: assembling the piece; pre-welding of the edges in some points; welding; high tempering; welds quality control; removal of the seam reinforcement inside of the tube and the weld root to the depth of 2 mm; quenching; tempering; welds quality control; finishing. The welds quality control consists in visual inspection, ultrasonic testing, magnetic flaw detection, as well as X-ray and metallographic analyses. The mechanical properties are studied on notched samples cut out of the welded joints. The test results have shown that the mechanical properties of the welded joints meet the requirements on the same level with the base metal

Properties of structural steels melted out of high-purity charge

International Nuclear Information System (INIS)

Marchenko, V.N.; Sergeeva, T.K.; Kondakova, N.K.; Morozov, V.P.; Madorskij, L.L.

1993-01-01

A comparative evaluation has been made of impurities, mechanical properties and hydrogen embirittlement parameters for steels type 40Kh and 40KhS produced by electrometallurgical method with the use of direct reduced charge (DR-steels) and melted in an open-hearth furnace. Investigation results have shown that 40Kh and 40KhS Dr-steels have more coarse austenitic grains and experience more complete transformation of martensite into ferritic-pearlitic mixture on tempering. Threshold stresses increase 2.5 times due to purity enhancement at the expense of application of direct reduced charge

Fracture of ledeburitic steel during hot plastic deformation

International Nuclear Information System (INIS)

Nikitin, V.P.; Borisov, Yu.A.; Bulat, S.I.; Zajtsev, V.V.

1977-01-01

The mechanisms of the high-temperature failure of high-carbon chromium Kh6F1, Kh6T2 and Kh6VF steels and a possibility to avoid their overheating have been investigated. At 1190 deg C and over the failure occurs along boundaries of grains at points of formation of the initial portions of the liquid phase as carbides are dissolved. If after a holding at 1190-1210 deg C the steels are cooled to 1120-1150 deg C and held for a sufficiently long time, secondary carbides are formed in the eutectic areas and, if the steels are deformed, the discontinuities present a rounded shape. Holding of an overheated steel at 1120-1150 deg C ensures its satisfactory workability in rolling. By choosing adequate overheating and subsequent slight cooling conditions, it is possible not only to retain, but even to improve the plasticity of carbide high-carbon steels. The results of laboratory tests have been confirmed under industrial conditions

Microstructure-based modelling of the long-term monotonic and cyclic creep of the martensitic steel X 20(22) CrMoV 12 1

International Nuclear Information System (INIS)

Henes, D.; Straub, S.; Blum, W.; Moehlig, H.; Granacher, J.; Berger, C.

1999-01-01

The current state of development of the composite model of deformation of the martensitic steel X 20(22) CrMoV 12 1 under conditions of creep is briefly described. The model is able to reproduce differences in monotonic creep strength of different melts with slightly different initial microstructures and to simulate cyclic creep with alternating phases of tension and compression. (orig.)

Effect of hydrostatic pressure on phase transformations in Kh17N8 steel during deformation

International Nuclear Information System (INIS)

Eshchenko, R.N.; Teplov, V.A.

1984-01-01

The phase composition and structure of Kh17N8 steel strained to different degrees under atmospheric pressure and 1700 MPa are investigated. It has been found that deformation at 1700 MPa causes α and epsilon-martensite formation, the same deformation under atmospheric pressure - only α-martensite formation. The amount of the formed α-martensite is not changed with application of hydrostatic pressure. Electron-microscopic observations have shown that the dispersion of α-martensite formed under pressure is higher than in the absence of pressure; no interconnection in formation of α and epsilon-martensite in samples strained under pressure has been observed

Reliability of nondestructive testing of metal strength properties for power equipment

International Nuclear Information System (INIS)

Bugaj, N.V.; Lebedev, A.A.; Sharko, A.V.

1985-01-01

Ultrasonic control which is a constituent part of a complex control system which includes specimen-free (by hardness) tests, random breaking tests and acoustic measurements is stUdied for its reliability with respect to strength properties of power-equipment metal. Quantitative and alternative criteria are developed to estimate quality of elements for power-equipment according to results of metal strength properties. Acoustic control results are presented for ultimate strength in 12Kh1MF-steel

The effect of thermoplastic treatment regimes on the microplastic strain of nitrogen-containing steel Kh21G10N7MBF

International Nuclear Information System (INIS)

Bannykh, O.A.; Blinov, V.M.; Kostina, M.V.; Grachev, S.V.; Mal'tseva, L.A.

2005-01-01

A study is made into the influence of a percentage reduction during cold rolling and subsequent holdings at heat on development of microplastic deformation when bending sheet specimens of stainless austenitic high-nitrogen steel Kh21G10N7MBF. It is revealed that a maximum value of apparent limit of elasticity (∼1800 MPa) is attained due to plastic deformation by rolling at 20 Deg C with a total percentage reduction of 60 % and subsequent aging at 500 Deg C for 1-4 h [ru

Determination of constant of chemical reaction rate in the process of steel treatment in the endothermal atmosphere

International Nuclear Information System (INIS)

Gyulikhandanov, E.L.; Kislenkov, V.V.

1978-01-01

The high-temperature method was applied to measuring a relative variation in the electrical resistance of a thin steel foil prepared from the 12KhN3A, 18Kh2N4VA, 20KhGNR, and 20Kh3MVF steels during its carburization and decarburization, and determined was the temperature dependence of the reaction rate of the interaction of the endothermal atmosphere of different compositions with the analloyed γ-Fe. A connection has been established between the reaction rate constant and the thermodynamic activity of carbon in the alloyed austenite at the temperature of about 925 deg C, corresponding to the cementation temperature. This provides the quantitative estimation of the above value for any alloyed steels and with the presence of numerical values of diffusion coefficients; this also enables one to carry out an accurate calculation of the distribution of carbon throughout the depth of a layer when effecting the cementation in the endothermal atmosphere

Weakly coupled S=1/2 quantum Heisenberg antiferromagnetic chains in an effective staggered field

International Nuclear Information System (INIS)

Sato, Masahiro; Oshikawa, Masaki

2002-01-01

We study weakly coupled S=1/2 quantum Heisenberg antiferromagnetic chains in an effective staggered field. Applying mean-field (MF) theory, spin-wave theory and chain MF (CMF) theory, we can see analytically some effects of the staggered field in this higher dimensional spin system. In particular, when the staggered field and the inter-chain inter-action compete with each other, we conjecture from the MF theory that a nontrivial phase is present. The spin wave theory predicts that the behavior of the gaps induced by a staggered field is different between the competitive case and the non-competitive case. When the inter-chain interactions are weak enough, we can improve the MF phase diagram by using CMF theory and the analytical results of field theories. The ordered phase region predicted by the CMF theory is fairly smaller than one of the MF theory. Cu-benzoate, CuCl 2 · 2DMSO (dimethylsulphoxide), BaCu 2 (Si 1-x Ge x ) 2 O 7 , etc., could be described by our model in enough low temperature. (author)

Quantum state-to-state dynamics for the quenching process of Br(2P1/2) + H2(v(i) = 0, 1, j(i) = 0).

Science.gov (United States)

Xie, Changjian; Jiang, Bin; Xie, Daiqian; Sun, Zhigang

2012-03-21

Quantum state-to-state dynamics for the quenching process Br((2)P(1/2)) + H(2)(v(i) = 0, 1, j(i) = 0) → Br((2)P(3/2)) + H(2)(v(f), j(f)) has been studied based on two-state model on the recent coupled potential energy surfaces. It was found that the quenching probabilities have some oscillatory structures due to the interference of reflected flux in the Br((2)P(1/2)) + H(2) and Br((2)P(3/2)) + H(2) channels by repulsive potential in the near-resonant electronic-to-vibrational energy transfer process. The final vibrational state resolved integral cross sections were found to be dominated by the quenching process Br((2)P(1/2)) + H(2)(v) → Br((2)P(3/2)) + H(2)(v+1) and the nonadiabatic reaction probabilities for Br((2)P(1/2)) + H(2)(v = 0, 1, j(i) = 0) are quite small, which are consistent with previous theoretical and experimental results. Our calculated total quenching rate constant for Br((2)P(1/2)) + H(2)(v(i) = 0, j(i) = 0) at room temperature is in good agreement with the available experimental data. © 2012 American Institute of Physics

SCC growth behavior of cast stainless steels in high-temperature water. Influences of corrosion potential, steel type, thermal aging and cold-work

International Nuclear Information System (INIS)

Yamada, Takuyo; Terachi, Takumi; Miyamoto, Tomoki; Arioka, Koji

2011-01-01

Recent studies on crack growth rate (CGR) measurement in oxygenated high-temperature pure water conditions, such as normal water chemistry (NWC) in BWRs, using compact tension (CT) type specimens have shown that stainless steel weld metal are susceptible to stress corrosion cracking (SCC). On the other hand, the authors reported that no significant SCC growth was observed on stainless steel weld metals in PWR primary water at temperatures from 250degC to 340degC. Cast austenitic stainless steels are widely used in light water reactors, and there is a similarity between welded and cast stainless steels in terms of the microstructure of the ferrite/austenite duplex structure. However, there are a few reports giving CGR data on cast stainless steels in the BWRs and PWRs. The principal purpose of this study was to examine the SCC growth behavior of cast stainless steels in simulated PWR primary water. A second objective was to examine the effects on SCC growth in hydrogenated and oxygenated water environments at 320degC of: (1) corrosion potential; (2) steels type (Mo in alloy); (3) thermal-aging (up to 400degC x 40 kh); and (4) cold-working (10%). The results were as follows: (1) No significant SCC growth was observed on all types of cast stainless steels: aged (400degC x 40 kh) of SCS14A and SCS13A and 10% cold-working, in hydrogenated (low-potential) water at 320degC. (2) Aging at 400degC x 40 kh SCS14A (10%CW) markedly accelerated the SCC growth of cast material in high-potential water at 320degC, but no significant SCC growth was observed in the hydrogenated water, even after long-term thermal aging (400degC x 40 kh). (3) Thus, cast stainless steels have excellent SCC resistance in PWR primary water. (4) On the other hand, significant SCC growth was observed on all types of cast stainless steels: 10%CW SCS14A and SCS13A, in 8 ppm-oxygenated (high-potential) water at 320degC. (5) No large difference in SCC growth was observed between SCS14A (Mo) and SCS13A. (6) No

Corrosion cracking of 03N18K1M3TYu and 02N12Kh5M3 maraging steels in chloride solutions

Energy Technology Data Exchange (ETDEWEB)

Pavlov, V.N.; Chumalo, G.V.; Vereshchagin, A.N.; Melekhov, R.K.

1987-07-01

The authors investigate the electrochemical behavior in 0.5% NaCl solution and 42% MgCl/sub 2/ solution and the tendency toward corrosion cracking was determined in boiling 0.5% chloride solution of the cobalt-containing maraging steels in the title. Weld specimens and specimens of the base metal of 03N18K1M3TYu steel were tested in 3% NaCl solution for resistance to corrosion cracking. Additional investigations were made of specimens of that steel with previously created fatigue cracks of the base metal and the weld specimens in 3% NaCl solutions, since that steel is a promising material for structures operating in sea water and low concentration chloride solutions.

Water vapor pressure over molten KH_2PO_4 and demonstration of water electrolysis at ∼300 °C

International Nuclear Information System (INIS)

Berg, R.W.; Nikiforov, A.V.; Petrushina, I.M.; Bjerrum, N.J.

2016-01-01

Highlights: • The vapor pressure over molten KH_2PO_4 was measured by Raman spectroscopy to be about 8 bars at ∼300 °C. • Raman spectroscopy shows that molten KH_2PO_4 under its own vapor pressure contains much dissolved water. • It is demonstrated spectroscopically that water electrolysis is possible in KH_2PO_4 electrolyte forming H_2 and O_2 at 300 °C. • Molten KH_2PO_4 is a possible electrolyte for water electrolysis. - Abstract: A new potentially high-efficiency electrolyte for water electrolysis: molten monobasic potassium phosphate, KH_2PO_4 or KDP has been investigated at temperatures ∼275–325 °C. At these temperatures, KH_2PO_4 was found to dissociate into H_2O gas in equilibrium with a melt mixture of KH_2PO_4−K_2H_2P_2O_7−KPO_3−H_2O. The water vapor pressure above the melt, when contained in a closed ampoule, was determined quantitatively vs. temperature by use of Raman spectroscopy with methane or hydrogen gas as an internal calibration standard, using newly established relative ratios of Raman scattering cross sections of water and methane or hydrogen to be 0.40 ± 0.02 or 1.2 ± 0.03. At equilibrium the vapor pressure was much lower than the vapor pressure above liquid water at the same temperature. Electrolysis was realized by passing current through closed ampoules (vacuum sealed quartz glass electrolysis cells with platinum electrodes and the electrolyte melt). The formation of mixtures of hydrogen and oxygen gases as well as the water vapor was detected by Raman spectroscopy. In this way it was demonstrated that water is present in the new electrolyte: molten KH_2PO_4 can be split by electrolysis via the reaction 2H_2O → 2H_2 + O_2 at temperatures ∼275–325 °C. At these temperatures, before the start of the electrolysis, the KH_2PO_4 melt gives off H_2O gas that pressurizes the cell according to the following dissociations: 2KH_2PO_4 ↔ K_2H_2P_2O_7 + H_2O ↔ 2KPO_3 + 2H_2O. The spectra show however that the water by

Effect of heat treatment and rotor steels composition on hydrogen solubility

International Nuclear Information System (INIS)

Ivanov, A.I.; Samojlenko, L.V.; Gorovaya, O.N.; Najdovskij, A.G.; Bilik, I.; Kret, Ya.

1988-01-01

Measurements of equilibrium hydrogen adsorption in samples of 27KhN3MFA and 25Kh2NMFA steels were conducted. Carbide inclusions and doping additions, typical for rotor steels, don't produce noticeable effect on hydrogen solubility in

In vitro characterization of gE negative bovine herpesvirus types 1.1 (BHV-1.1 and 1.2a (BHV-1.2a Caracterização in vitro de herpes vírus bovino tipos 1.1 (BHV-1.1 e 1.2a (BHV-1.2a gE negativos

Directory of Open Access Journals (Sweden)

Fernando R. Spilki

2004-09-01

Full Text Available This study aimed the in vitro growth characterization of a previously constructed Brazilian bovine herpesvirus 1.2a with a deletion in the glycoprotein E gene (BHV-1.2a gE-. The plaque sizes, penetration and growth kinetics of the Brazilian BHV-1.2a gE- were studied and compared with the parental virus, as well as with a BHV-1.1 gE- recombinant derived from an European BHV-1.1 strain. No statistical differences were observed between the gE- recombinants and the respective parental viruses penetration assays were performed. When single step growth curves were studied, no statistical differences were observed between gE- and parental viruses. However, it was observed that both gE- viruses were excreted from cells in significantly higher titres at 11 hours post infection in comparison with parental viruses. No statistical differences were observed when plaque sizes of parental viruses or gE- viruses we analyzed separately in each cell type. However, both gE- recombinants displayed a significantly reduced plaque areas on three different cell cultures, in comparison with parental viruses, indicating that the lack of gE had the same effect on both BHV-1 subtypes, manifested by a restricted cell-to-cell spread in infected cells.O presente estudo teve como objetivo a caracterização das propriedades de crescimento in vitro de uma amostra brasileira de herpesvírus bovino tipo 1.2a que apresenta uma deleção no gene que codifica a glicoproteína E (BHV-1.2a gE-. Os tamanhos de placa, cinética de penetração e cinética de multiplicação do vírus BHV-1.2a gE- foram estudados e comparados com o vírus parental, bem como com um vírus BHV-1.1 gE- recombinante, o qual é derivado de uma amostra européia de BHV-1.1. Em termos de cinética de penetração, não foram observadas diferenças significativas quando comparados os vírus gE- com os parentais. A determinação da cinética de multiplicação não demonstrou diferenças significativas entre os

On choice of tempered steels

International Nuclear Information System (INIS)

Govorov, A.A.; Pan'shin, I.F.; Rakhmanov, V.I.

1978-01-01

For the purpose of developing a graphical method for choosing structural steels, a change in the propagation work of a crack and in the critical temperature of brittleness of 40, 40Kh, 40KhN, and 40KhNM steels, was examined depending on the hardness after hardening and tempering. A diagram enabling to choose the grade of steel for making an article of known dimensions according to the preset values of its mechanical properties has been plotted. The developed selection scheme takes into account the hardenability of steels and the influence of the hardness after thermal treatment on the cold-shortness of steel

Parametrical limits of SCC-susceptibility of austenitic and austenitic-ferritic Cr-Ni steels

International Nuclear Information System (INIS)

Starosvetskij, D.I.; Baru, R.L.; Bondarenko, A.I.; Bogoyavlenskij, V.L.; Timonin, V.A.

1990-01-01

Comparative investigations into corrosion cracking (CC) of austenitic (12Kh18N10T) and austenitic-ferritic (08Kh22N6T) chromium-nickel steels are performed for various chloride media in a wide range of chloride concentrations and temperatures. It is shown that the ratio between steels in terms of their CC-susceptibility is not definite and can undergo a reversal depending on parameters of medium, level and conditions of loading. Differences in mechanisms of corrosion cracking of austenitic and austenitic-ferritic steels are established

Close toleranoe forging of chromium steel blades for powerful steam turbines

International Nuclear Information System (INIS)

Shastin, Eh.G.; Kositskij, Yu.N.; Lyubchits, G.A.

1989-01-01

Work on simulating technological process on die-forging hammer was performed in order to reduce the preparation period bringing technology of close tolerance forging of turbine blades to a commercial level. A special attention was paid to development of accurate forming of forgings of 20Kh13Sh, 12Kh13 and 15Kh11MFSh steels on screw presses with nominal effort equal to 80 and 144 MN

Elastic scattering of deuterons from hydrogen at 2.0, 1.6 and 1.2 GeV, and search for critical opalescence in inelastic scattering of proton from carbon-12 at 800 MeV

International Nuclear Information System (INIS)

Haji-Saeid, S.M.

1980-01-01

Large deuteron vector and tensor asymmetries have been measured for the first time at intermediate energies. The polarized deuteron beam whose tensor and vector components were 0.75 and 0.25, respectively, were used at energies of 2.0, 1.6 and 1.2 GeV. The tensor and vector quantities Pyy and Py were extracted from the data obtained within beam polarization normal to the scattering plane, and Pxx was obtained when the polarization was precessed into the scattering plane. Analysis of the data using multiple scattering theory demonstrates the importance of the non-eikonal correction to the Glauber Model and also the sensitivity of the data to double-spin flip components of the NN amplitudes. In another experiment the differential cross section for the 12C(P,P')12C*(15.11 MeV, 1 + T = 1) reaction has been measured at 800 MeV; the range of the angular distribution corresponds to momentum transfers of 0.7 to 2.4 fm -1 (1 to 3.3 mπ). The cross section decreases almost exponentially at large angles; no maximum is observed in the region where nuclear critical opalescence might be expected. The cross sections which measured in parallel to the 15.11 MeV state were for the levels at 11.83 (2 - ), 12.71 (1 + ), 13.35 (2 - ), 16.1 (2 + ) and 16.58 (2 - ) MeV

Study of Ionospheric Indexes T and MF2 related to R12 for Solar Cycles 19-21

Science.gov (United States)

Villanueva, Lucia

2013-04-01

Modern worldwide communications are mainly based on satellite systems, remote communication networks, and advanced technologies. The most important space weather "meteorological" events produce negative effects on signal transmissions. Magnetic storm conditions that follow coronal mass ejections are particularly of great importance for radio communication at HF frequencies (3-30 MHz range), because the Ionization increase (or decrease), significantly over (or below), the Average Values. Nowadays new technologies make possible to establish Geophysical Observatories and monitor the sun almost in real time giving information about geomagnetic indices. Space Weather programs have interesting software predictions of foF2 producing maps and plots, every some minutes. The Average Values of the ionospheric parameters mainly depend on the position, hour, season and the phase of the 11-year cycle of the solar activity. Around 1990´s several ionospheric indexes were suggested to better predict the state of the foF2 monthly media, as: IF2, G, T and MF2, based on foF2 data from different latitude ionospheric observatories. They really show better seasonal changes than monthly solar indexes of solar flux F10.7 or the international sunspot numbers Ri. The main purpose of this paper is to present an analogic model for the ionospheric index MF2, to establish the average long term predictions of this index. Changes of phase from one cycle to the other of one component of the model is found to fit the data. The usefulness of this model could be the prediction of the ionospheric normal conditions for one entire solar cycle having just the prediction of the maximum of the next smooth sunspot number R12. In this presentation, comparisons of the Australian T index and and the Mikhailov MF2 index show an hysteresis variation with the solar monthly index Ri, such dependence is quite well represented by a polynomial fit of degree 6 for rising and decaying fases for solar cycles 19, 20 and

Mechanical properties and microstructure changes of low-activation 3Cr-2W-V-Ti ferritic steels developed for nuclear applications

International Nuclear Information System (INIS)

Asakura, Kentaro; Kohyama, Akira; Yamada, Takemi.

1990-01-01

The effects of alloying elements such as Cr, W, V and Mn on tensile strength at elevated temperatures, creep-rupture properties and toughness of low activation (2.25-3)Cr-(2-2.5)W-V-Ti steels were investigated together with their microstructure change during high temperature exposure. These steels were normalized to produce bainitic structures in the same manner as that for a conventional 2.25Cr-1Mo steel. They presented superior tensile strength at elevated temperatures and creep-rupture strength in comparison with a conventional 2.25Cr-1Mo steel. The creep-rupture strength of the steels at 500degC for 100 000 h demonstrated about twice that of the conventional 2.25Cr-1Mo steel. The 3Cr-2.5W-0.2V-0.01Ti steel is recommended as a potential low activation ferritic steel for nuclear applications with well optimized mechanical properties, such as tensile strength at elevated temperatures, creep-rupture strength and toughness. The effects of alloying elements were discussed with correlating microstructural and mechanical aspects. (author)

Z-phase in 9-12% Cr Steels

DEFF Research Database (Denmark)

Danielsen, Hilmar; Hald, John

2004-01-01

The complex nitride Z-phase, Cr(V,Nb)N, has recently been identified as a major cause for premature breakdown in creep strength of a number of new 9-12%Cr martensitic steels. A thermodynamic model of the Z-phase has been created based on the Thermo-Calc software. The model predicts the Z-phase to......The complex nitride Z-phase, Cr(V,Nb)N, has recently been identified as a major cause for premature breakdown in creep strength of a number of new 9-12%Cr martensitic steels. A thermodynamic model of the Z-phase has been created based on the Thermo-Calc software. The model predicts the Z......-phase to be stable in all of the new 9-12%Cr martensitic steels. This has generally been confirmed by the performed experiments. Z-phase precipitation seems to be a kinetic problem, and drivning force calculations using Thermo-Calc with the developed model have been used to predict steel compositions, which...

Behaviour of Z phase in 9–12%Cr steels

DEFF Research Database (Denmark)

Danielsen, Hilmar Kjartansson; Hald, John

2006-01-01

The literature on the behaviour of modified Z phase Cr(V,Nb)N in creep resistant martensitic 9–12%Cr steels is briefly reviewed. Ten different 9–12%Cr steels were investigated after prolonged exposure at 600–660uC; the modified Z phase was found in all of them. In steels with high Cr content (11......–12%), Z phase precipitates much faster than in 9%Cr steels. Precipitation of Z phase is associated with dissolution of MX carbonitrides, and causes a breakdown in long term creep strength in 9–12%Cr steels. High Cr steels show creep instabilities accompanied with Z phase precipitation, whereas low Cr...... steels show good long term creep stability. A niobium free CrVN variant of the modified Z phase was observed for the first time during the course of this work. The solution temperature of the Cr(V,Nb)N and CrVN modified Z phases was found to be close to 800uC for 11–12%Cr steels, much lower than the 1200...

Glycosylation of alpha(2)delta(1) subunit: a sweet talk with Ca(v)1.2 channels

Czech Academy of Sciences Publication Activity Database

Lazniewska, Joanna; Weiss, Norbert

2016-01-01

Roč. 35, č. 3 (2016), s. 239-242 ISSN 0231-5882 R&D Projects: GA ČR GA15-13556S; GA MŠk 7AMB15FR015 Institutional support: RVO:61388963 Keywords : calcium channel * Ca(v)1.2 channel * ancillary subunit * alpha(2)delta(1) subunit * glycosylation * trafficking Subject RIV: CE - Biochemistry Impact factor: 1.170, year: 2016

Effect of nickel and MnS inclusions in the metal on the pitting corrosion of low-carbon stainless steels

International Nuclear Information System (INIS)

Frejman, L.I.; Nguen, The Dong; Volkov, D.E.; Konnov, Yu.P.

1986-01-01

The resistance to pitting corrosion of steels on the 03Kh17-03Kh18 base containing up to 20 % Ni at different levels of S and Mn impurities contamination is investigated. It is shown that up to 50 % of nickel introduced into ordinary steels with 5-6 % Ni is spent to compensate the resistance decrease caused by MnS inclusions. Full compensation is not attained even in the 10-20 %. Ni range in which nickel practically does not affect the resistance of neither ordinary, nor pure (without MnS) steels. Titanium introduction into ordinary steel on the Kh22N6 base permits to surpass the level of 03Kh17N3 pure steel resistance and attain the level of 03Kh17N6 pure steel almost by all characteristics (including passivated characteristics in sulfuric acid) besides pitting repassivity. In this property pure steels with Ni >or approx. 3 % surpass even the molybdenum containing 03Kh21NbM2T ordinary steel though they by far concede by passivation in sulfuric acid

Analysis of the THAI Iod-11 and Iod-12 tests: Advancements and limitations of ASTEC V2.0R3p1 and MELCOR V2.1.4803

International Nuclear Information System (INIS)

Gonfiotti, Bruno; Paci, Sandro

2015-01-01

Highlights: • The I 2 transport in a multi-compartment vessel was analysed. • ASTEC and MELCOR codes were employed. • Same nodalisation for the code-to-code comparison. • The I 2 concentrations were quite well simulated in ASTEC. • Numerical issues on MELCOR. - Abstract: This work is related to the application of the ASTEC V2.0R3p1 and MELCOR V2.1.4803 codes to the analysis of the THAI Iod-11 and Iod-12 containment tests characterised by an iodine release. The main scope of these two tests was to investigate the steel interaction on dry and wet surfaces, with an interaction supposed to be a two-steps process: an initial faster and reversible physisorption followed by a slower, and irreversible, chemisorption of the physisorbed I 2 . The aim of the present work is to highlight advancements and limitations of the current ASTEC and MELCOR code versions respect to the older code versions employed during the European SARNET projects. The investigation was carried out as a code-to-code comparison vs. the experimental THAI data, focusing on the evaluation of the code models treating the iodine behaviour. A similar spatial nodalisation was employed for both codes. As main result, ASTEC had shown an overall good agreement compared to the iodine related experimental data while, on contrary, MELCOR had shown poor results, probably due to unsolved numerical issues and unsatisfactory iodine modellisation

A new 1-2 GeV/c separated beam for BNL

Energy Technology Data Exchange (ETDEWEB)

Pile, P.H.; Beavis, D.; Brown, R.L.; Chrien, R.; Danby, G.; Jackson, J.; Lazarus, D.M.; Leonhardt, W.; Pearson, C.; Pendzick, A.; Montemurro, P.; Russo, T.; Sandberg, J.; Sawafta, R.; Spataro, C.; Walker, J. (Brookhaven National Lab. Associated Universities, Inc., Upton, NY (United States)); Enge, H.A. (Massachusetts Inst. of Tech., Cambridge, MA (United States))

1992-09-15

A 1-2 GeV/c beam line has been constructed at the Brookhaven National Laboratory alternating gradient synchrotron (BNL AGS). The beam line is optimized to deliver an intense clean beam of 1.8 GeV/c negative kaons for an H particle search experiment and incorporates two stages of velocity selection with the magnetic optics corrected to third order. Details of the beam line design as well as results of the commissioning will be discussed. (orig.).

Elastic scattering of polarized deuterons from hydrogen at 2.0, 1.6, and 1.2 GeV and search for critical opalescence in inelastic scattering of protons from carbon-12 at 800 MeV

International Nuclear Information System (INIS)

Haji-Saeid, S.M.

1981-01-01

Large deuteron vector and tensor asymmetries were measured for the first time at intermediate energies. The polarized deuteron beam (with tensor and vector components of 0.75 and 0.25, respectively) was used at energies of 2.0, 1.6, and 1.2 GeV. The tensor and vector quantities P/sub yy/ and P/sub y/ were extracted from the data obtained within beam polarization normal to the scattering plane, and P/sub xx/ was obtained when the polarization was precessed into the scattering plane. Analysis of the data using multiple scattering theory demonstrates the importance of the noneikona correction to the Glauber Model and also the sensitivity of the data to double-spin flip components of the NN amplitudes. The differential cross section for the 12 C(p,p') 12 C* (15.11 MeV, 1 + , T=1) reaction was measured at 800 MeV; the range of the angular distribution corresponds to momentum transfers of 0.7 to 2.4 fm -1 (1 to 3.3 m/sub π/). The cross section decreases almost exponentially at large angles; no maximum is observed in the region where nuclear critical opalescence might be expected. Cross sections measured in parallel to the 15.11-MeV state were for the levels at 11.83 (2 - ), 12.71 (1 + ), 13.35 (2 - ), 16.1 (2 + ), and 16.58 (2 - ) MeV. 86 figures 18 tables

Immunogenicity and safety of cell-derived MF59®-adjuvanted A/H1N1 influenza vaccine for children

Science.gov (United States)

Knuf, Markus; Leroux-Roels, Geert; Rümke, Hans; Rivera, Luis; Pedotti, Paola; Arora, Ashwani Kumar; Lattanzi, Maria; Kieninger, Dorothee; Cioppa, Giovanni Della

2015-01-01

Mass immunization of children has the potential to decrease infection rates and prevent the transmission of influenza. We evaluated the immunogenicity, safety, and tolerability of different formulations of cell-derived MF59-adjuvanted and nonadjuvanted A/H1N1 influenza vaccine in children and adolescents. This was a randomized, single-blind, multicenter study with a total of 666 healthy subjects aged 6 months–17 y in one of 3 vaccination groups, each receiving formulations containing different amounts of influenza A/H1N1 antigen with or without MF59. A booster trivalent seasonal MF59 vaccine was administered one year after primary vaccinations. Antibody titers were assessed by hemagglutination inhibition (HI) and microneutralization assays obtained on days 1, 22, 43, 366, and 387 (3 weeks post booster). Safety was monitored throughout the study. One vaccination with 3.75 μg of A/H1N1 antigen formulated with 50% MF59 (3.75_halfMF59) or 7.5 μg of A/H1N1 antigen formulated with 100% MF59 (7.5_fullMF59) induced an HI titer ≥1:40 in >70% of children in the 1–vaccinations with nonadjuvanted 15 μg A/H1N1 antigen were needed to achieve this response in the 1–children aged 6–11 months, 1 dose of 7.5_fullMF59 resulted in an HI titer ≥1:40 in >70% while 2 doses of 3.75_halfMF59 were required to achieve this result. All vaccines were well tolerated. Our findings support the immunogenicity and safety of the 3.75_halfMF59 (2 doses for children vaccine formulations for use in children and adolescents aged 6 months to 17 y The use of the 3.75_halfMF59 could have the benefit of antigen and adjuvant sparing, increasing the available vaccine doses allowing vaccination of more people. PMID:25621884

The analysis of ion nitriding and nitrogen ion implantation on tribological properties of steels 33H3MF and 36H3M

International Nuclear Information System (INIS)

Zandecki, R.

1993-01-01

Surface properties of two kinds of steel 33H3MF and 36H3M have been investigated. Three different methods of steel surface treatment have been used: ion nitriding, nitrogen ion implantation and mixing method being the sum of the first and second ones. The microstructure, microhardness distribution, fatigue strength, friction coefficient and other tribological properties have been measured and compared. 60 refs, 74 figs, 19 tabs

On the improvement of quality of tubes for steam generator collectors of thermal power plants

International Nuclear Information System (INIS)

Dolinskaya, L.A.; Gulyaev, G.I.; Kholyavko, Z.I.; Khanina, M.M.; Khotomlyanskij, G.L.

1978-01-01

Pipes from 12Kh1MF steel were strengthened by a method which makes it possible, in subsequent manufacture of items from said pipes, to weld and temper the steel without any substantial prejudice to its structure and strength properties. It was shown that cooling in air from the austenitization temperature down to 820-850 deg C, an accelerated cooling in a bath with water on the temperature range between 850 and 500 deg C and subsequent air cooling enhances both the initial long-time strength and its values after tempering during erection. The high strength properties in this case result from the fragmentation of the bainite ferrite

Quality of structural steel melted by single-slag process

International Nuclear Information System (INIS)

Levin, A.M.; Andreev, V.I.; Monastyrskij, A.V.; Drozdova, M.F.; Pashchenko, V.E.; Orzhekh, M.B.

1982-01-01

The 40Kh and 12KhN3A steels were used to compare the quality of the metal manufactured according to several variants of a single-slag process with the metal of a conventional melting technology. Investigation results show, that a single-slag process metal has higher sulfides and oxides contents as well as an increased anisotropy of mechanical properties while its tendency to flake formation is weaker due to a less degree of gas saturation. It is marked that anisotropy in the properties and a sulfide content may be decreased by out-of-furnace treatment of steels

Hot Deformation Behavior of 1Cr12Ni3Mo2VN Martensitic Stainless Steel

Science.gov (United States)

He, Xiaomao; Jiang, Peng; Zhou, Leyu; Chen, Chao; Deng, Xiaochun

2017-08-01

1Cr12Ni3Mo2VN is a new type of martensitic stainless steel for the last-stage blades of large-capacity nuclear and thermal power turbines. The deformation behavior of this steel was studied by thermal compression experiments that performed on a Gleeble-3500 thermal simulator at a temperature range of 850°C to 1200°C and a strain rate of 0.01s-1 to 20s-1. When the deformation was performed at high temperature and low strain rate, a necklace type of microstructures was observed, the plastic deformation mechanism is grain boundary slip and migration, when at low temperature and lower strain rate, the slip bands were observed, the mechanism is intracrystalline slips, and when at strain rate of 20s-1, twins were observed, the mechanism are slips and twins. The Arrhenius equation was applied to describe the constitutive equation of the flow stress. The accuracy of the equation was verified by using the experimental data and the correlation coefficient R2 = 0.9786, and the equation can provide reasonable data for the design and numerical simulation of the forging process.

KH in Paraffin - KH(P): A Useful Base for Organic Synthesis

Science.gov (United States)

Taber, Douglass F.; Nelson, Christopher G.

2011-01-01

The preparation of KH as a one:one homogenate with paraffin, termed KH(P), is reported. KH(P), a solid at room temperature, is stable without special handling. On suspension in THF with a phosphonium salt, KH(P) rapidly generates the ylide. Wittig condensation with aromatic, aliphatic and α, β-unsaturated aldehydes proceeds with high Z-selectivity. KH(P) should be a generally useful base for organic synthesis. PMID:17081034

Theoretical study of [Li(H2O)n]+ and [K(H2O)n]+ (n = 1-4) complexes

International Nuclear Information System (INIS)

Wojcik, M.J.; Mains, G.J.; Devlin, J.P.

1995-01-01

The geometries, successive binding energies, vibrational frequencies, and infrared intensities are calculated for the [Li(H 2 O) n ] + and [K(H 2 O) n ] + (n = 1-4) complexes. The basis sets used are 6-31G * and LANL1DZ (Los Alamos ECP+DZ) at the SCF and MP2 levels. There is an agreement for calculated structures and frequencies between the MP2/6-31G * and MP2/LANL1DZ basis sets, which indicates that the latter can be used for calculations of water complexes with heavier ions. Our results are in a reasonable agreement with available experimental data and facilitate experimental study of these complexes. 19 refs., 4 figs., 6 tabs

The AKAP Cypher/Zasp contributes to β-adrenergic/PKA stimulation of cardiac CaV1.2 calcium channels.

Science.gov (United States)

Yu, Haijie; Yuan, Can; Westenbroek, Ruth E; Catterall, William A

2018-06-04

Stimulation of the L-type Ca 2+ current conducted by Ca V 1.2 channels in cardiac myocytes by the β-adrenergic/protein kinase A (PKA) signaling pathway requires anchoring of PKA to the Ca V 1.2 channel by an A-kinase anchoring protein (AKAP). However, the AKAP(s) responsible for regulation in vivo remain unknown. Here, we test the role of the AKAP Cypher/Zasp in β-adrenergic regulation of Ca V 1.2 channels using physiological studies of cardiac ventricular myocytes from young-adult mice lacking the long form of Cypher/Zasp (LCyphKO mice). These myocytes have increased protein levels of Ca V 1.2, PKA, and calcineurin. In contrast, the cell surface density of Ca V 1.2 channels and the basal Ca 2+ current conducted by Ca V 1.2 channels are significantly reduced without substantial changes to kinetics or voltage dependence. β-adrenergic regulation of these L-type Ca 2+ currents is also significantly reduced in myocytes from LCyphKO mice, whether calculated as a stimulation ratio or as net-stimulated Ca 2+ current. At 100 nM isoproterenol, the net β-adrenergic-Ca 2+ current conducted by Ca V 1.2 channels was reduced to 39 ± 12% of wild type. However, concentration-response curves for β-adrenergic stimulation of myocytes from LCyphKO mice have concentrations that give a half-maximal response similar to those for wild-type mice. These results identify Cypher/Zasp as an important AKAP for β-adrenergic regulation of cardiac Ca V 1.2 channels. Other AKAPs may work cooperatively with Cypher/Zasp to give the full magnitude of β-adrenergic regulation of Ca V 1.2 channels observed in vivo. This is a work of the U.S. Government and is not subject to copyright protection in the United States. Foreign copyrights may apply.

Welding wires for high-tensile steels

International Nuclear Information System (INIS)

Laz'ko, V.E.; Starova, L.L.; Koval'chuk, V.G.; Maksimovich, T.L.; Labzina, I.E.; Yadrov, V.M.

1993-01-01

Strength of welded joints in arc welding of high-tensile steels of mean and high thickness by welding wires is equal to approximately 1300 MPa in thermohardened state and approximately 600 MPa without heat treatment. Sv-15Kh2NMTsRA-VI (EhK44-VI) -Sv-30Kh2NMTsRA-VI (EkK47-VI) welding wires are suggested for welding of medium-carbon alloyed steels. These wires provide monotonous growth of ultimate strength of weld metal in 1250-1900 MPa range with increase of C content in heat-treated state

Power cables with extruded insulation and their accessories for rated voltages from 1 kV (Um = 1,2 kV) up to 30 kV (Um = 36 kV) : Part 2: cables for rated voltages from 6 kV (Um = 7,2 kV) up to 30 kV (Um = 36 kV)

CERN Document Server

International Electrotechnical Commission. Geneva

2005-01-01

Power cables with extruded insulation and their accessories for rated voltages from 1 kV (Um = 1,2 kV) up to 30 kV (Um = 36 kV) : Part 2: cables for rated voltages from 6 kV (Um = 7,2 kV) up to 30 kV (Um = 36 kV)

[Effect of KH2PO4 on the odonto- and osteogenic differentiation potential of human stem cells from apical papillae].

Science.gov (United States)

Wang, Yan-ping; Wu, Jin-tao; Wang, Zi-lu; Zheng, Yang-yu; Zhang, Guang-dong; Yu, Jin-hua

2013-01-01

To determine the effects of KH2PO4 on the odonto- and osteogenic differentiation potential of human stem cells from apical papillae (SCAP) in vitro. SCAP were isolated and cultured respectively in alpha minimum essential medium (α-MEM) or α-MEM containing 1.8 mmol/L KH2PO4. Alkaline phosphatase (ALP) activity, alizarin red staining, real-time reverse transcription polymerase chain reaction (RT-PCR) and Western blotting were used to examine the odonto and osteogenic potential of SCAP in the two media. SCAP cultured in α-MEM containing 1.8 mmol/L KH2PO4 exhibited a higher ALP activity [(0.370 ± 0.013) Sigma unit×min(-1)×mg(-1)] at day 3 than control group [(0.285 ± 0.008) Sigma unit×min(-1)×mg(-1)] and KH2PO4-treated SCAP formed more calcified nodules at day 5 [(0.539 ± 0.007) µg/g] and day 7 [(1.617 ± 0.042) µg/g] than those in normal medium [(0.138 ± 0.037) µg/g, P odonto- and osteogenic markers were significantly up-regulated after the stimulation of KH2PO4 at day 3 and 7 respectively, as compared with control group. 1.8 mmol/L KH2PO4 can promote the odonto and osteogenic differentiation potential of human SCAP.

Determination of {sup 55}Mn(n,γ){sup 56}Mn reaction cross-section at the neutron energies of 1.12, 2.12, 3.12 and 4.12 MeV

Energy Technology Data Exchange (ETDEWEB)

Vansola, Vibha; Mukherjee, Surjit [M.S. University of Baroda, Vadodara (India). Dept. of Physics; Naik, Haladhara [Bhabha Atomic Research Center, Mumbai (India). Radiochemistry Div.; Suryanarayana, Saraswatula Venkata [Bhabha Atomic Research Center, Mumbai (India). Nuclear Physics Div.; Ghosh, Reetuparna; Badwar, Sylvia; Lawriniang, Bioletty Mary [North Eastern Hill Univ., Meghalaya (India). Dept. of Physics; Sheela, Yerraguntla Santhi [Manipal Univ. (India). Dept. of Statistics

2016-07-01

The {sup 55}Mn(n,γ){sup 56}Mn reaction cross-sections at the neutron energies of 1.12, 2.12, 3.12 and 4.12 MeV were determined by using activation and off-line γ-ray spectrometric technique. The neutron energies of 1.12 and 2.12 MeV were generated from the {sup 7}Li(p,n) reaction by using the proton energies of 3 and 4 MeV from the folded tandem ion beam accelerator (FOTIA) at BARC. For the neutron energies of 3.12 and 4.12 MeV, the proton energies used were 5 and 6 MeV from the Pelletron facility at TIFR, Mumbai. The {sup 115}In(n,γ){sup 116m}In reaction cross-section was used as the neutron flux monitor. The {sup 55}Mn(n,γ){sup 56}Mn reaction cross-section at the neutron energies of 4.12 MeV are reported for the first time, whereas at 1.12, 2.12 and 3.12 MeV, they are in between the literature data. The {sup 55}Mn(n,γ){sup 56}Mn reaction cross-section was also calculated theoretically by using the computer code TALYS 1.6 and EMPIRE 3.2.2. The experimental data of present work are found to be in between the theoretical values of TALYS and EMPIRE.

Mechanical and fracture properties at impact loading of selected steels for nuclear power engineering

International Nuclear Information System (INIS)

Buchar, J.; Bilek, Z.

1988-01-01

The possibilities are briefly characterized of experimental research of mechanical and fracture properties of steels used in nuclear power engineering. Attention is paid to plastic deformation and the assessment of fracture formation during impact loading. The results are reported for steels 15Kh2MFA and 10GN2MFA. For steel 15Kh2MFA the effect was also studied of neutron radiation at different temperatures. From the theory developed for non-irradiated material 10GN2MFA, a prediction is made within the original model of the fracture stress value for steel 15Kh2MFA in both non-irradiated and irradiated states. The conclusion is arrived at that the existing methods of assessing steel properties at impact load allow obtaining knowledge of all significant effects during actual stress, this using only small specimens of the materials. (Z.M.). 4 figs., 8 refs

Investigations on grain boundary segregation energy of phosphorus in 12Cr1MoV steel under elastic stress

Czech Academy of Sciences Publication Activity Database

Zheng, L.; Fu, Y.; Lejček, Pavel; Song, S.; Schmitz, G.; Meng, Y.

2016-01-01

Roč. 18, č. 4 (2016), 506-510 ISSN 1438-1656 R&D Projects: GA ČR GAP108/12/0144 Institutional support: RVO:68378271 Keywords : grain boundary segregation, * stress effect, * phosphorus, * steel Subject RIV: BM - Solid Matter Physics ; Magnetism Impact factor: 2.319, year: 2016

Nitrogen ion implantation effect on friction coefficient of tool steel

International Nuclear Information System (INIS)

Velichko, N.I.; Udovenko, V.F.; Markus, A.M.; Presnyakova, G.N.; Gamulya, G.D.

1988-01-01

Effect of nitrogen molecular ion implantation into KhVSG steel on the friction coefficient in the air and vacuum is investigated. Irradiation is carried out by the N 2 + beam with energy 120 keV and flux density 5 μ/cm 2 at room temperature in vacuum 5x10 -4 Pa. The integral dose of irradiation is 10 17 particle/cm 2 . Nitrogen ion implantation is shown to provide the formation of the modified layer changing friction properties of steel. The friction coefficient can either increase or decrease depending on implantation and test conditions. 4 refs.; 2 figs

Simulation of 200-400 MeV/u "1"2C + "1"2C elastic scattering on SHARAQ spectrometer

International Nuclear Information System (INIS)

Yu Lei; Zhang Gaolong; Terashima, S.; Le Xiaoyun; Tanihata, I.

2015-01-01

In order to further obtain the information of three-body force (TBF) from 200-400 MeV/u "1"2C + "1"2C elastic scattering, we plan to perform this experiment on a SHARAQ spectrometer. Based on the experimental condition of the Radioactive Ion Beam Factory (RIBF)-SHARAQ facility, a simulation is given to find a compromise between the better energy and angular resolutions, and higher yield by optimizing the target thickness, beam transport mode, beam intensity and angular step. From the simulation, we found that the beam quality mainly limits the improvements of energy and angular resolutions. A beam tracking system as well as a lateral and angular dispersion-matching technique are adopted to reduce the influence of beam quality. According to the two angular settings of SHARAQ as well as the expected cross sections on the basis of the theoretical model, the energy and angular resolutions, and statistical accuracy are estimated. (authors)

Study of some properties of 's' neutron resonance parameters for target nuclei I = 1/2 and I = 3/2 in function of spin value J = I + 1/2 in the energy range 1 {yields} 5000 eV; Etude de quelques proprietes des parametres de resonances des neutrons ''s'' pour des noyaux cibles I = 1/2 et I = 3/2 en fonction de la valeur du spin J = I + 1/2 dans le domaine d'energie 1 eV {yields} 5000 eV

Energy Technology Data Exchange (ETDEWEB)

Julien, J [Commissariat a l' Energie Atomique, Saclay (France). Centre d' Etudes Nucleaires

1967-05-15

Different kinds of experiments and analysis methods allowing to achieve neutron resonances parameters in the low energy range (1 eV {yields} 5000 eV) are described. A great deal of effort to improve experimental conditions and data processing in order to know the spin value J = I {+-} 1/2 has been spent. The time of flight method was used. A few target nuclei I = 3/2 and 1 = 1/2 have been studied. For I = 3/2 (Ga, As, 3r, Au) we find S{sub o} J = 2 {approx_equal} 2 S{sub o} J = 1 and S{sub o} J = 1 {approx_equal} S{sub o} J = 0 for I = 1/2 (Tm, Pt) but {sup 77}Se. Fluctuations of the total radiative width {gamma}{sub {gamma}} depend on the spin value I = I {+-} 1/2 when E1 transition, are enhanced for one of the both spin states. The magnitude of these fluctuations can be explained of the strength of E1 transitions (E{sub {gamma}} {approx} 7 MeV) is supposed to be proportional to E{sup 5}{sub {gamma}} instead of E{sup 3}{sub {gamma}}. The distribution of levels spacings against spin value J are considered and are compared to theoretical predictions. (author) [French] On decrit les differentes methodes d'analyse permettant d'obtenir les parametres des resonances de neutron dans le domaine d'energie 1 eV {yields} 5000 eV. Un effort particulier a ete fait pour connaitre la valeur du spin J = I {+-} 1/2. Les types d'experience et les analyses des donnees, developpes et ameliores pour determiner J sont decrits. Les resultats obtenus ont permis l'etude de differentes proprietes en fonction du spin J. On trouve: S{sub o} J 2 {approx_equal} 2 S{sub o} J = 1 pour les noyaux I = 3/2 etudies (Ga, As, Br, Au) et S{sub o} J = 1 {approx_equal} S{sub o} J = 0 Pour le Tm et {sup 195}Pt de spin I = 1/2. On constate que les largeurs radiatives totales {gamma}{sub {gamma}} fluctuent si des transitions E1 aux premiers etats excites sont favorisees. Ces fluctuations peuvent etre expliquees si on suppose que les intensites de ces transitions sont proportionnelles a E{sup 5}{sub {gamma

A CACNA1C variant associated with reduced voltage-dependent inactivation, increased CaV1.2 channel window current, and arrhythmogenesis.

Directory of Open Access Journals (Sweden)

Jessica A Hennessey

Full Text Available Mutations in CACNA1C that increase current through the CaV1.2 L-type Ca2+ channel underlie rare forms of long QT syndrome (LQTS, and Timothy syndrome (TS. We identified a variant in CACNA1C in a male child of Filipino descent with arrhythmias and extracardiac features by candidate gene sequencing and performed functional expression studies to electrophysiologically characterize the effects of the variant on CaV1.2 channels. As a baby, the subject developed seizures and displayed developmental delays at 30 months of age. At age 5 years, he displayed a QTc of 520 ms and experienced recurrent VT. Physical exam at 17 years of age was notable for microcephaly, short stature, lower extremity weakness and atrophy with hyperreflexia, spastic diplegia, multiple dental caries and episodes of rhabdomyolysis. Candidate gene sequencing identified a G>C transversion at position 5731 of CACNA1C (rs374528680 predicting a glycine>arginine substitution at residue 1911 (p.G1911R of CaV1.2. The allele frequency of this variant is 0.01 in Malays, but absent in 984 Caucasian alleles and in the 1000 genomes project. In electrophysiological analyses, the variant decreased voltage-dependent inactivation, thus causing a gain of function of CaV1.2. We also observed a negative shift of V1/2 of activation and positive shift of V1/2 of channel inactivation, resulting in an increase of the window current. Together, these suggest a gain-of-function effect on CaV1.2 and suggest increased susceptibility for arrhythmias in certain clinical settings. The p.G1911R variant was also identified in a case of sudden unexplained infant death (SUID, for which an increasing number of clinical observations have demonstrated can be associated with arrhythmogenic mutations in cardiac ion channels. In summary, the combined effects of the CACNA1C variant to diminish voltage-dependent inactivation of CaV1.2 and increase window current expand our appreciation of mechanisms by which a gain of

Overexpression of MfPIP2-7 from Medicago falcata promotes cold tolerance and growth under NO3 (-) deficiency in transgenic tobacco plants.

Science.gov (United States)

Zhuo, Chunliu; Wang, Ting; Guo, Zhenfei; Lu, Shaoyun

2016-06-14

Plasma membrane intrinsic proteins (PIPs), which belong to aquaporins (AQPs) superfamily, are subdivided into two groups, PIP1 and PIP2, based on sequence similarity. Several PIP2s function as water channels, while PIP1s have low or no water channel activity, but have a role in water permeability through interacting with PIP2. A cold responsive PIP2 named as MfPIP2-7 was isolated from Medicago falcata (hereafter falcata), a forage legume with great cold tolerance, and transgenic tobacco plants overexpressing MfPIP2-7 were analyzed in tolerance to multiple stresses including freezing, chilling, and nitrate reduction in this study. MfPIP2-7 transcript was induced by 4 to 12 h of cold treatment and 2 h of abscisic acid (ABA) treatment. Pretreatment with inhibitor of ABA synthesis blocked the cold induced MfPIP2-7 transcript, indicating that ABA was involved in cold induced transcription of MfPIP2-7 in falcata. Overexpression of MfPIP2-7 resulted in enhanced tolerance to freezing, chilling and NO3 (-) deficiency in transgenic tobacco (Nicotiana tabacum L.) plants as compared with the wild type. Moreover, MfPIP2-7 was demonstrated to facilitate H2O2 diffusion in yeast. Higher transcript levels of several stress responsive genes, such as NtERD10B, NtERD10C, NtDREB1, and 2, and nitrate reductase (NR) encoding genes (NtNIA1, and NtNIA2) were observed in transgenic plants as compared with the wild type with dependence upon H2O2. In addition, NR activity was increased in transgenic plants, which led to alterations in free amino acid components and concentrations. The results suggest that MfPIP2-7 plays an important role in plant tolerance to freezing, chilling, and NO3 (-) deficiency by promoted H2O2 diffusion that in turn up-regulates expression of NIAs and multiple stress responsive genes.

Hot working effect on austenite transformations in structural steel in continuous cooling

International Nuclear Information System (INIS)

Zajmovskij, V.A.; Kisteh, N.V.; Samedov, O.V.

1979-01-01

Austenite transformations in 40, 40Kh, 40KhN and 40KhNMA steels under hot working at 900 deg C with 20% reduction degree and continuous cooling with 1,7-16 0 /s are investigated. Changing of cooling rate in various ways affects the temperature range of austenite transformation in pearlite and bainite regions. Regulating the cooling rate after hot working one can essentially change the impact strength and steel ductility as a result of high temperature thermomechanical treatment effect

Effect of hot rolling on the structure and the mechanical properties of nitrogen-bearing austenitic-martensitic 14Kh15AN4M steel

Science.gov (United States)

Bannykh, O. A.; Betsofen, S. Ya.; Lukin, E. I.; Blinov, V. M.; Voznesenskaya, N. M.; Tonysheva, O. A.; Blinov, E. V.

2016-04-01

The effect of the rolling temperature and strain on the structure and the properties of corrosionresistant austenitic-martensitic 14Kh15AN4M steel is studied. The steel is shown to exhibit high ductility: upon rolling in the temperature range 700-1100°C at a reduction per pass up to 80%, wedge steel specimens are uniformly deformed along and across the rolling direction without cracking and other surface defects. Subsequent cold treatment and low-temperature tempering ensure a high hardness of the steel (50-56 HRC). Austenite mainly contributes to the hardening upon rolling in the temperature range 700-800°C at a reduction of 50-70%, and martensite makes the main contribution at higher temperatures and lower strains. Texture does not form under the chosen deformation conditions, which indicates dynamic recrystallization with the nucleation and growth of grains having no preferential orientation.

Fracture characteristic in creep of a 5 Cr-1/2 Mo steel at 600 and 6500C

International Nuclear Information System (INIS)

Paiva, R.L.C. de; Monteiro, S.N.; Silveira, T.L.

The creep behavior of a 5 Cr-1/2 Mo steel was studied at 600 and 650 0 C. The caracteristics of fracture, observed by optical and scanning metallography, displayed a transition from intergranular to transgranular mode of rupture in the range of temperatures and stresses studied. This behavior was dicussed based upon the possible mechanisms for creep deformation taking place in this material [pt

Chemical heat treatment of low alloyed maraging steels

Energy Technology Data Exchange (ETDEWEB)

Malinov, L S; Korotich, I K [Zhdanovskij Metallurgicheskij Inst. (Ukrainian SSR)

1979-09-01

The investigation concerned the nitriding, cementation, chromizing, borating of economically alloyed maraging grade 04Kh2N5MFYu steel. The investigated methods of chemothermal treatment were found to considerably increase the hardness of the surface layer of the maraging steel. The high tempering of the grade 04Kh2N5MFYu cemented and hardened steel was found to produce secondary hardening. On chromizing, the diffusion layer is an alloyed ferrite which strengthens because of the dispersion hardening on ageing. The formation of the plastic low-carbon martensite at relatively small cooling rates greatly decreases the tendency of the boride layer to cracking.

Study of radiation damage of steels for light water pressure vessels at UJV

International Nuclear Information System (INIS)

Vacek, N.; Stoces, B.

1980-01-01

Preoperational determination of radiation resistance of pressure vessel steels is performed at accelerated neutron exposure in a test or materials research reactor. The results obtained at accelerated and operating exposure are not fully identical and surveillance bodies are therefore used manufactured from the pressure vessel material. Currently, the following steels are used for the manufacture of light water reactor pressure vessels: Mn-Mo-Ni (ASTM-A533-B, ASTM-A508), Cr-Mo-V (15Kh2M1FA). At UJV Rez, for irradiation Chanca-M probes imported from France are used featuring electric temperature control. Almost identical radiation embrittlement was measured for all three steels after irradiation with a neutron fluence of 3x10 23 n.m -2 at a temperature of 290 degC. (H.S.)

Mechanical behavior of 9Cr-1Mo-1V steel due to creep fatigue deformation

International Nuclear Information System (INIS)

Kim, Sang Tae; Kim, Jae Kyoung; Lee, Hak Sun; Oh, Sang Hyun; Kwun, Sook In; Kim, Chung Seok

2005-01-01

Creep-fatigue tests with trapezoid load wave were performed on a 9Cr-1Mo-1V steel at high temperature(550 .deg. C). Trapezoid load wave is considering about hold time for creep effects. we could find out some information in the relationship between number of cycles to failure and hold time. The number of cycles to failure depended on hold time. The cyclic behavior of 9Cr-1Mo-1V steel was characterized by cyclic softening with increasing number of cycles in high temperature. Also we could observe some cavity in the specimens. The size of cavity was different from each hold time

Prospects for Martensitic 12 % Cr Steels for Advanced Steam Power Plants

DEFF Research Database (Denmark)

Hald, John

2016-01-01

and FB2 are now used in power plants up to 600–620 °C steam temperature. For higher steam temperatures up to 650 °C steels with 11–12 % Cr are needed for better resistance against steam oxidation. However, fine V and Nb based nitrides may transform to coarse Z-phase [Cr(V,Nb)N] nitrides in steels...

Structural characterization of Li1.2v3o8 insertion electrodes by single-crystal x-ray-diffraction

CSIR Research Space (South Africa)

De Picciotto, LA

1993-08-01

Full Text Available The crystal structures of Li1.2V3O8 and a lithiated product Li4.0V3O8 have been determined by single-crystal X-ray diffraction methods. The structure refinement of Li1.2V308 confirms that of Li1+xV3O8(x almost-equal-to 0) reported by Wadsley thirty...

Wear resistance and structural changes in nitrogen-containing high-chromium martensitic steels under conditions of abrasive wear and sliding friction

International Nuclear Information System (INIS)

Makarov, A.V.; Korshunov, L.G.; Schastlivtsev, V.M.; Chernenko, N.L.

1998-01-01

Martensitic nitrogen-containing steels Kh17N2A0.14, Kh13A0.14, Kh14G4A0.22 as well as steel 20Kh13 were studied for their wear resistance under conditions of friction and abrasion. Metallography, X ray diffraction analysis and electron microscopy were used to investigate the structural changes taking place in a thin surface layer on wearing. It is shown that an increase of nitrogen content of 0.14 to 0.22% promotes an enhancement of steel resistance to abrasive and adhesive wear, especially after tempering in the range of 500-550 deg C. Typically, the nitrogen-containing steels exhibit lower resistance to various types of wear in comparison with the steels with high-carbon martensite due to their lower deformability under conditions of friction loading

Corrosion resistance of heat exchange equipment in hydrotreating Orenburg Condensate

International Nuclear Information System (INIS)

Teslya, B.M.; Burlov, V.V.; Parputs, I.V.; Parputs, T.P.

1986-01-01

The authors study the corrosion resistance of materials of construction and select appropriate materials for the fabrication of heat exchange equipment that will be serviceable under hydrotreating conditions. This paper discusses the Orenburg condensate hydrotreating unit which has been shut down repeatedly for repair because of corrosion damage to components of heat exchangers in the reactor section: tube bundles (08Kh18N10T steel), corrugated compensators (12Kh18N10T steel), and pins of the floating heads (37Kh13N8G8MFB steel). The authors recommend that the tube bundles and the compensators in heat exchangers in the reaction section should be fabricated of 08Kh21N6M2T or 10Kh17N13M2T steel. The pins have been replaced by new pins made of 10Kh17N13 X M2T steel, increasing the service life from 6-12 months to 2 years

Effect of cyclic electron irradiation on mechanical properties of austenite steel

International Nuclear Information System (INIS)

Tsepelev, A.B.; Sadykhov, S.I.O.; Chernov, A.I.; Sevost'yanov, M.A.

2006-01-01

To check the supposition on the possibility of radiation-stimulated process enhancement under cyclic irradiation conditions an experimental investigation is carried out to elucidate the effect of the mode of irradiation (continuous or cyclic) on mechanical properties of chromium-manganese austenitic stainless steel type 10Kh12G20V. The effect of some radiation hardening is observed under cyclic irradiation, however, the data obtained cannot be considered as good evidence for the validity of proposed model of dynamic preference if the scatter in experimental data is taken into account [ru

The effect of alloying and treatment on martensite transformation during deformation in Fe-Cr-Mn steels with unstable austenite

International Nuclear Information System (INIS)

Malinov, L.S.; Konop, V.I.; Sokolov, K.N.

1977-01-01

The effect is studied of alloying with chromium (6-10%), silicon (1-2%), molybdenum (1-3%), and copper (2%), the heat treatment conditions, and the deformation conditions, or the martensitic transformation and mechanical properties of Fe-Cr-Mn steels of the transitional class based on 0G8AM2S. It is shown that appropriate alloying and treatment, taking into account the degree of stability of the austenite, can ensure a complex of high mechanical properties of the steels investigated. For instance, the treatment of steel 0Kh10AG8MD2S by the technique: hardening+ 40% deformation at 400 deg C + 10% deformation at room temperature has yielded the following mechanical properties: sigmasub(B)=150 kgf/mm 2 , sigmasub(T)=110 kgf/mm 2 , sigma=18%, psi=32%

Creep-fatigue-environment interaction of 9Cr-1Mo-V-Nb steel

International Nuclear Information System (INIS)

Shibata, Hiroyuki; Ishikawa, Akiyoshi; Asada, Yasuhide

1996-01-01

An extension of the creep-fatigue damage model has been conducted in the present study. The original damage model has been developed to the predict the creep-fatigue life of 9Cr-1Mo-V-Nb steel (Modified 9Cr-1Mo steel) in a very high vacuum environment. The present study is to extend an applicability of the model to the creep-fatigue damage accumulation in the air environment. (orig.)

Transcriptional and electrophysiological consequences of KChIP2-mediated regulation of CaV1.2

DEFF Research Database (Denmark)

Thomsen, Morten B; Foster, Erika; Nguyen, Katherine H

2009-01-01

previous finding. Using gene-chip and real-time PCR techniques, we find that KChIP2(-/-) mice have an increased transcriptional activity of the calcium channel beta(2) subunit, CACNB2, whereas the expression of Ca(V)1.2 is preserved. Although I(to,f) is absent and I(Ca,L) is decreased in myocytes from KCh...

Polarisation parameter measurement in the proton-proton elastic scattering from 0.5 to 1.2 GeV

International Nuclear Information System (INIS)

Ducros, Yves

1970-01-01

The angular distribution of the polarisation parameter was measured in the proton-proton elastic - scattering at seven energies between 0.5 and 1.2 GeV. A polarized proton target was used. The results show a maximum of the polarisation parameter of 0.6, at 0.73 GeV. This maximum is due to the important increase of the total cross section between 0.6 and 0.73 GeV. At 1.2 GeV the angular distribution of the polarisation shows a minimum for a momentum transfer value of -1 (GeV/c) 2 . A phase shift analysis was done at 0.66 GeV, using all available experimental data at this energy. There is no evidence of a di-baryonic resonance in the 1 D 2 phase. (author) [fr

microstructure change in 12 % Cr steel during creep

International Nuclear Information System (INIS)

Winatapura, D. S.; Panjaitan, E.; Arslan, A.; Sulistioso, G.S.

1998-01-01

The microstructure change in steel containing of 12% Cr or DIN X20CrMoV 12 1 during creep has been studied by means of optical microscopy and Transmission Electron Microscope (TEM). The creep testing at 650 o C was conducted under constant load of 650 Mpa. The heat treatment of the specimen before creep testing was austenization, followed by tempering for 2 hours. The obtained microstructure was tempered martensitic. This microstructure consisted of the martensite laths, and distributed randomly in the matrix. During tempering, chromium carbide particles of Cr 7 C 6 less than 0,2 μmin-size were precipitated on or and in the subgrain and lath martensite grain boundary. During creep testing those particles transformed and precipitated as chrome carbide precipitates of Cr 23 C 6 . At the secondary creep stage, the void formation occurred, and then it developed into the creep cracks. At tertiary creep stage for 3554 hours, the specimen was failure. The creep cracks were informs of transgranular and intergranular modes which propagated almost perpendicular to the stress axis. From this observation, it is suggested that tempering caused the ductility of martensitic microstructure, which increased the creep resistant or Cr 12% steel

Optimum conditions for aging of stainless maraging steels

International Nuclear Information System (INIS)

Mironenko, P.A.; Krasnikova, S.I.; Drobot, A.V.

1980-01-01

Aging kinetics of two 0Kh11N10M2T type steels in which 3 % Mo (steel 1), and 3 % Mo and 11 % Co (steel 2) had been additionally introduced instead of titanium were investigated. Electron microscopy and X-ray methods were used. It was ascertained that the process of steel aging proceeded in 3 stages. Steel 2 was hardened more intensively during the aging, had a higher degree of hardness and strength after the aging, weakened more slowly if overaged than steel 1. The intermetallide hcp-phase Fe 2 Mo was the hardening phase on steels extended aging. Optimum combination of impact strength and strength was was achieved using two-stage aging: the first stage - maximum strength aging was achieved, the second stage - aging at minimum temperatures of two-phase α+γ region

Aberrant Splicing Induced by Dysregulated Rbfox2 Produces Enhanced Function of CaV1.2 Calcium Channel and Vascular Myogenic Tone in Hypertension.

Science.gov (United States)

Zhou, Yingying; Fan, Jia; Zhu, Huayuan; Ji, Li; Fan, Wenyong; Kapoor, Isha; Wang, Yue; Wang, Yuan; Zhu, Guoqing; Wang, Juejin

2017-12-01

Calcium influx from activated voltage-gated calcium channel Ca V 1.2 in vascular smooth muscle cells is indispensable for maintaining myogenic tone and blood pressure. The function of Ca V 1.2 channel can be optimized by alternative splicing, one of post-transcriptional modification mechanisms. The splicing factor Rbfox2 is known to regulate the Ca V 1.2 pre-mRNA alternative splicing events during neuronal development. However, Rbfox2's roles in modulating the key function of vascular Ca V 1.2 channel and in the pathogenesis of hypertension remain elusive. Here, we report that the proportion of Ca V 1.2 channels with alternative exon 9* is increased by 10.3%, whereas that with alternative exon 33 is decreased by 10.5% in hypertensive arteries. Surprisingly, the expression level of Rbfox2 is increased ≈3-folds, presumably because of the upregulation of a dominant-negative isoform of Rbfox2. In vascular smooth muscle cells, we find that knockdown of Rbfox2 dynamically increases alternative exon 9*, whereas decreases exon 33 inclusion of Ca V 1.2 channels. By patch-clamp studies, we show that diminished Rbfox2-induced alternative splicing shifts the steady-state activation and inactivation curves of vascular Ca V 1.2 calcium channel to hyperpolarization, which makes the window current potential to more negative. Moreover, siRNA-mediated knockdown of Rbfox2 increases the pressure-induced vascular myogenic tone of rat mesenteric artery. Taken together, our data indicate that Rbfox2 modulates the functions of vascular Ca V 1.2 calcium channel by dynamically regulating the expressions of alternative exons 9* and 33, which in turn affects the vascular myogenic tone. Therefore, our work suggests a key role for Rbfox2 in hypertension, which provides a rational basis for designing antihypertensive therapies. © 2017 American Heart Association, Inc.

RSCAT_LEVEL_2B_OWV_COMP_12_V1.1:1

Data.gov (United States)

National Aeronautics and Space Administration — This dataset contains the RapidScat Level 2B 12.5km Version 1.1 science-quality ocean surface wind vectors. The Level 2B wind vectors are binned on a 12.5 km Wind...

High temperature strength and aging behavior of 12%Cr-15%Mn austenitic steels

International Nuclear Information System (INIS)

Miyahara, Kazuya; Bae, Dong-Su; Sakai, Hidenori; Hosoi, Yuzo

1993-01-01

High Mn-Cr austenitic steels are still considered to be an important high temperature structural material from the point of view of reduced radio-activation. The objective of the present study is to make a fundamental research of mechanical properties and microstructure of 12%Cr-15%Mn austenitic steels. Especially the effects of alloying elements of V and Ti on the mechanical properties and microstructure evolution of high Mn-Cr steels were studied. Precipitation behaviors of carbides, nitrides and σ phase are investigated and their remarkable effects on the high temperature strength are found. The addition of V was very effective for strengthening the materials with the precipitation of fine VN. Ti was also found to be beneficial for the improvement of high temperature strength properties. The results of high temperature strengths of the 12Cr-15Mn austenitic steels were compared with those of the other candidate and/or reference materials, for example, JFMS (modified 9Cr-2Mo ferritic stainless steel) and JPCAs (modified 316 austenitic stainless steels). (author)

Hydrogen storage in TiCr1.2(FeV)x BCC solid solutions

International Nuclear Information System (INIS)

Santos, Sydney F.; Huot, Jacques

2009-01-01

The Ti-V-based BCC solid solutions have been considered attractive candidates for hydrogen storage due to their relatively large hydrogen absorbing capacities near room temperature. In spite of this, improvements of some issues should be achieved to allow the technological applications of these alloys. Higher reversible hydrogen storage capacity, decreasing the hysteresis of PCI curves, and decrease in the cost of the raw materials are needed. In the case of vanadium-rich BCC solid solutions, which usually have large hydrogen storage capacities, the search for raw materials with lower cost is mandatory since pure vanadium is quite expensive. Recently, the substitutions of vanadium in these alloys have been tried and some interesting results were achieved by replacing vanadium by commercial ferrovanadium (FeV) alloy. In the present work, this approach was also adopted and TiCr 1.2 (FeV) x alloy series was investigated. The XRD patterns showed the co-existence of a BCC solid solution and a C14 Laves phase in these alloys. SEM analysis showed the alloys consisted of dendritic microstructure and C14 colonies. The amount of C14 phase increases when the amount of (FeV) decreases in these alloys. Concerning the hydrogen storage, the best results were obtained for the TiCr 1.2 (FeV) 0.4 alloy, which achieved 2.79 mass% of hydrogen storage capacity and 1.36 mass% of reversible hydrogen storage capacity

PDGF-induced migration of synthetic vascular smooth muscle cells through c-Src-activated L-type Ca2+ channels with full-length CaV1.2 C-terminus.

Science.gov (United States)

Guo, Xiaoguang; Kashihara, Toshihide; Nakada, Tsutomu; Aoyama, Toshifumi; Yamada, Mitsuhiko

2018-06-01

In atherosclerosis, vascular smooth muscle cells (VSMC) migrate from the media toward the intima of the arteries in response to cytokines, such as platelet-derived growth factor (PDGF). However, molecular mechanism underlying the PDGF-induced migration of VSMCs remains unclear. The migration of rat aorta-derived synthetic VSMCs, A7r5, in response to PDGF was potently inhibited by a Ca V 1.2 channel inhibitor, nifedipine, and a Src family tyrosine kinase (SFK)/Abl inhibitor, bosutinib, in a less-than-additive manner. PDGF significantly increased Ca V 1.2 channel currents without altering Ca V 1.2 protein expression levels in A7r5 cells. This reaction was inhibited by C-terminal Src kinase, a selective inhibitor of SFKs. In contractile VSMCs, the C-terminus of Ca V 1.2 is proteolytically cleaved into proximal and distal C-termini (PCT and DCT, respectively). Clipped DCT is noncovalently reassociated with PCT to autoinhibit the channel activity. Conversely, in synthetic A7r5 cells, full-length Ca V 1.2 (Ca V 1.2FL) is expressed much more abundantly than truncated Ca V 1.2. In a heterologous expression system, c-Src activated Ca V 1.2 channels composed of Ca V 1.2FL but not truncated Ca V 1.2 (Ca V 1.2Δ1763) or Ca V 1.2Δ1763 plus clipped DCT. Further, c-Src enhanced the coupling efficiency between the voltage-sensing domain and activation gate of Ca V 1.2FL channels by phosphorylating Tyr1709 and Tyr1758 in PCT. Compared with Ca V 1.2Δ1763, c-Src could more efficiently bind to and phosphorylate Ca V 1.2FL irrespective of the presence or absence of clipped DCT. Therefore, in atherosclerotic lesions, phenotypic switching of VSMCs may facilitate pro-migratory effects of PDGF on VSMCs by suppressing posttranslational Ca V 1.2 modifications.

Bimetallic MOFs (H₃O)_x[Cu(MF₆)(pyrazine)₂]·(4 - x)H₂O (M = V⁴⁺, x = 0; M = Ga³⁺, x = 1)

DEFF Research Database (Denmark)

Manson, Jamie L.; Schlueter, John A.; Garrett, Kerry E.

2016-01-01

The title compounds are bimetallic MOFs containing [Cu(pyz)2]2+ square lattices linked by MF6 n- octahedra. In each, only the Cu2+ spins exhibit long-range magnetic order below 3.5 K (M = V4+) and 2.6 K (M = Ga3+). The V4+ spins remain disordered down to 0.5 K....

Measurement of {sup 197}Au(n,γ){sup 198g}Au reaction cross-section at the neutron energies of 1.12, 2.12, 3.12 and 4.12 MeV

Energy Technology Data Exchange (ETDEWEB)

Vansola, Vibha [M.S. Univ., Baroda (India). Dept. of Physics; Ghosh, Reetuparna; Badwar, Sylvia [North Eastern Hill Univ., Meghalaya (India). Dept. of Physics; and others

2015-07-01

The {sup 197}Au(n,γ){sup 198}Au reaction cross-sections at the neutron energies of 1.12, 2.12, 3.12 and 4.12 MeV were determined by using activation and off-line γ-ray spectrometric technique. The mono-energetic neutron energies of 1.12-4.12 MeV were generated from the {sup 7}Li(p,n) reaction by using the proton energies of 3 and 4 MeV from the folded tandem ion beam accelerator (FOTIA) at BARC as well as 5 and 6 MeV from the Pelletron facility at TIFR, Mumbai. The {sup 115}In(n,γ){sup 116m}In reaction cross-section was used as the neutron flux monitor. The {sup 197}Au(n,γ){sup 198}Au reaction cross-section at the neutron energies of 3.12 and 4.12 MeV are reported for the first time. The {sup 197}Au(n,γ){sup 198}Au reaction cross-sections at 1.12 and 2.12 MeV are close to the literature data of in between neutron energies. The {sup 197}Au(n,γ){sup 198}Au cross-section was also calculated theoretically by using the computer code TALYS 1.6 and found to be higher than the experimental data of present work and literature data within the neutron energies of 0.8 to 4 MeV.

Photoproduction of eta mesons from threshold to 1.2 GeV

International Nuclear Information System (INIS)

Rigney, A.; Breuer, M.; Hoffman-Rothe, P.; Anton, G.; Arends, J.; Berrier-Ronsin, G.; Beulertz, W.; Blanpied, G.; Bock, A.; Bruns, M.; Didelez, J.; Djaladi, C.; Edel, G.; Frascaria, R.; Maass, R.; Helbing, K.; Hey, J.; Noeldeke, G.; Hourani, E.; Mayers, M.; Preedom, B.; Ritchie, B.; Rosier, L.; Saghai, B.; Schumacher, M.; Smend, F.; Whisnant, S.

1995-01-01

We have measured total and differential cross sections for η-meson photo-production on 7 cm thick 1 H, 2 D, and 14 N liquid targets from threshold to 1.2 GeV, using the tagged Bremsstrahlung photon beam produced by the electrons extracted from the ELSA storage ring at Bonn. The photoreaction was identified by detecting the η decay products in the neutral meson spectrometer SPES0-2π, while the recoil baryons (proton, neutron, or deuteron) were detected by a variety of large angle scintillator detectors. Some of our recent preliminary results, both theoretical and experimental, will be discussed. copyright 1995 American Institute of Physics

Methods for protection of high-strength welded stainless steel from corrosion cracking

International Nuclear Information System (INIS)

Lashchevskij, V.B.; Gurvich, L.Ya.; Batrakov, V.P.; Kozheurova, N.S.; Molotova, V.A.; Shvarts, M.M.

1978-01-01

The efficiency of protection from corrosion cracking under a bending stress of 100 kgf/mm 2 in a salt mist and in a sulphur dioxide atmosphere, of welded joints of steel 08Kh15N5D2T with metallizing, galvanic and varnish coatings and lubricants, and of steel 1Kh15N4AM3 with sealing compounds has been investigated. Metallization of welded joints with aluminium and zinc efficiently increases corrosion resistance in a salt mist. Galvanic coatings of Cd, Zn, and Cr increase the time to cracking in a salt mist from 2-3 to 60-80 days. The protective properties of varnishes under the effect of a salt mist decrease in the following sequence: epoxy-polyamide enamel EP-140, acrylic enamel C-38, silicone enamels KO-834, KO-811, and KO-814. In an atmosphere containing SO 2 0.15 vol.% at 100% relative humidity, the varnishes investigated, with the exception of the inhibited coating XC-596, show lower protective properties than in a salt mist. The high efficiency of protection from corrosion cracking in a salt mist of slots of steel 1Kh15N4AM3 when using organic sealing compounds U4-21 and U5-21, and also slushing lubricants and oils PVK, TsIATIM-201, K17, and AMS3 was established

Structural basis for the differential effects of CaBP1 and calmodulin on Ca(V)1.2 calcium-dependent inactivation.

Science.gov (United States)

Findeisen, Felix; Minor, Daniel L

2010-12-08

Calcium-binding protein 1 (CaBP1), a calmodulin (CaM) homolog, endows certain voltage-gated calcium channels (Ca(V)s) with unusual properties. CaBP1 inhibits Ca(V)1.2 calcium-dependent inactivation (CDI) and introduces calcium-dependent facilitation (CDF). Here, we show that the ability of CaBP1 to inhibit Ca(V)1.2 CDI and induce CDF arises from interaction between the CaBP1 N-lobe and interlobe linker residue Glu94. Unlike CaM, where functional EF hands are essential for channel modulation, CDI inhibition does not require functional CaBP1 EF hands. Furthermore, CaBP1-mediated CDF has different molecular requirements than CaM-mediated CDF. Overall, the data show that CaBP1 comprises two structural modules having separate functions: similar to CaM, the CaBP1 C-lobe serves as a high-affinity anchor that binds the Ca(V)1.2 IQ domain at a site that overlaps with the Ca²+/CaM C-lobe site, whereas the N-lobe/linker module houses the elements required for channel modulation. Discovery of this division provides the framework for understanding how CaBP1 regulates Ca(V)s. Copyright © 2010 Elsevier Ltd. All rights reserved.

Diagnostics of metal state in steam lines

International Nuclear Information System (INIS)

Gofman, Yu.M.; Kazantseva, N.S.; Losev, L.Ya.; Nevolina, G.S.

1986-01-01

A series of micropore detection methods is suggested: light microscopy, electron microscopy, hydrostatic weighing; and comparative investigations of pore-formation processes in 12Kh1MF steel steam lines, which have operated for about 100 thousand hours at t=550 deg C and 47-55 MPa stresses are conducted using these methods. It is shown, that electron microscpy method can be applied at the early stages damaging, when embrionic micropores of 0.1 μm in size appear. Optical metallography allows one to detect pores of about 1 μm in size. Damage in density using the hydrostatic weighing method is estimated in the following way: at creep stages 1-2-0.1; at stage 3-0.4-0.6; at predestruction stage the degree of damage equals to 0.7-0.8

Multiple C-terminal tail Ca(2+)/CaMs regulate Ca(V)1.2 function but do not mediate channel dimerization.

Science.gov (United States)

Kim, Eun Young; Rumpf, Christine H; Van Petegem, Filip; Arant, Ryan J; Findeisen, Felix; Cooley, Elizabeth S; Isacoff, Ehud Y; Minor, Daniel L

2010-12-01

Interactions between voltage-gated calcium channels (Ca(V)s) and calmodulin (CaM) modulate Ca(V) function. In this study, we report the structure of a Ca(2+)/CaM Ca(V)1.2 C-terminal tail complex that contains two PreIQ helices bridged by two Ca(2+)/CaMs and two Ca(2+)/CaM-IQ domain complexes. Sedimentation equilibrium experiments establish that the complex has a 2:1 Ca(2+)/CaM:C-terminal tail stoichiometry and does not form higher order assemblies. Moreover, subunit-counting experiments demonstrate that in live cell membranes Ca(V)1.2s are monomers. Thus, contrary to previous proposals, the crystallographic dimer lacks physiological relevance. Isothermal titration calorimetry and biochemical experiments show that the two Ca(2+)/CaMs in the complex have different properties. Ca(2+)/CaM bound to the PreIQ C-region is labile, whereas Ca(2+)/CaM bound to the IQ domain is not. Furthermore, neither of lobes of apo-CaM interacts strongly with the PreIQ domain. Electrophysiological studies indicate that the PreIQ C-region has a role in calcium-dependent facilitation. Together, the data show that two Ca(2+)/CaMs can bind the Ca(V)1.2 tail simultaneously and indicate a functional role for Ca(2+)/CaM at the C-region site.

Specific electrical conductivity in molten potassium dihydrogen phosphate KH2PO4 - An electrolyte for water electrolysis at ∼300°C

DEFF Research Database (Denmark)

Nikiforov, Aleksey Valerievich; Berg, Rolf W.; Petrushina, Irina

2016-01-01

The conductivity of pure molten KH2PO4 salt and four mixtures with more or less water (KH2PO4-H2O and KH2PO4-KPO3 systems, respectively) were measured at temperatures of 240-320°C and under their own water vapor pressures. Molten KH2PO4 has been proven to be a promising electrolyte for an elevated...... temperature pressurized water electrolyzer demonstrating high conductivity of ∼0.30Scm-1 at 300°C. The conductivity data are given as polynomial functions of temperature and composition. The melting point of the pure salt under its own water vapor pressure was determined to be ∼272°C....

Measurement of the 115In(n,γ)116 m In reaction cross-section at the neutron energies of 1.12, 2.12, 3.12 and 4.12 MeV

Science.gov (United States)

Lawriniang, Bioletty Mary; Badwar, Sylvia; Ghosh, Reetuparna; Jyrwa, Betylda; Vansola, Vibha; Naik, Haladhara; Goswami, Ashok; Naik, Yeshwant; Datrik, Chandra Shekhar; Gupta, Amit Kumar; Singh, Vijay Pal; Pol, Sudir Shibaji; Subramanyam, Nagaraju Balabenkata; Agarwal, Arun; Singh, Pitambar

2015-08-01

The 115In(n,γ)116 m In reaction cross section at neutron energies of 1.12, 2.12, 3.12 and 4.12 MeV was determined by using an activation and off-line γ-ray spectrometric technique. The monoenergetic neutron energies of 1.12 - 4.12 MeV were generated from the 7Li(p,n) reaction by using proton beam with energies of 3 and 4 MeV from the folded tandem ion beam accelerator (FOTIA) at Bhabha Atomic Research Centre (BARC) and with energies of 5 and 6 MeV from the Pelletron facility at Tata Institute of Fundamental Research (TIFR), Mumbai. The 197Au(n,γ)198Au reaction cross-section was used as the neutron flux monitor.The 115In(n,γ)116 m In reaction cross section at neutron energies of 1.12, 2.12, 3.12 and 4.12 MeV was determined by using an activation and off-line γ-ray spectrometric technique. The monoenergetic neutron energies of 1.12 - 4.12 MeV were generated from the 7Li(p,n) reaction by using proton beam with energies of 3 and 4 MeV from the folded tandem ion beam accelerator (FOTIA) at Bhabha Atomic Research Centre (BARC) and with energies of 5 and 6 MeV from the Pelletron facility at Tata Institute of Fundamental Research (TIFR), Mumbai. The 197Au(n,γ)198 Au reaction cross-section was used as the neutron flux monitor. The 115In(n,γ)116 m In reaction cross-sections at neutron energies of 1.12 - 4.12 MeV were compared with the literature data and were found to be in good agreement with one set of data, but not with others. The 115In(n,γ)116 m In cross-section was also calculated theoretically by using the computer code TALYS 1.6 and was found to be slightly lower than the experimental data from the present work and the literature.)198Au reaction cross-section was used as the neutron flux monitor. The 115In(n,γ)116 m In reaction cross-sections at neutron energies of 1.12 - 4.12 MeV were compared with the literature data and were found to be in good agreement with one set of data, but not with others. The 115In(n,γ)116 m In cross-section was also calculated

Effects of niobium addition on the structure and properties of medium and high carbon steels. v. 1,2

International Nuclear Information System (INIS)

Mei, P.R.

1983-01-01

An evaluation about the use of niobium in medium and high carbon steels, with ferritic-pearlitic structure, through the understanding of niobium actuaction mechanism in the structure, and consequently in the mechanical properties of those steels is done. (E.G.) [pt

Parameter optimization for steel quenching by C02-laser irradiation

International Nuclear Information System (INIS)

Moryashchev, S.F.; Kislitsyn, A.A.; Kosyrev, F.K.

1984-01-01

The dependence of average absorption factor on maximal temperature of the article surface during quenching by CO 2 -laser irradiation was determined empirically. The calculations of depth of a hardening zone and process productivity in 40 Kh, 4Kh13 steels and Armco-iron with regard to this dependence were conducted

Influence of isothermal thermomechanical treatment on structure and properties of structural steels

International Nuclear Information System (INIS)

Smirnov, M.A.; Kaletin, A.Yu.; Schastlivthev, V.M.; Kaletina, Yu.V.

1997-01-01

A study is made into the structure and mechanical properties of steel 35KhGSA and 37KhN3A after isothermal hardening resulting in bainitic structure formation as well as after low-temperature thermomechanical treatment (LTTMT) combining the plastic deformation at the temperature of bainitic transformation and subsequent isothermal hardening. It is shown that LTTMT permits and essential enhancement of strength properties in steel 35KhGSA, high plasticity and impact strength being reserved. This is associated with bainitic structure refinement. In steel 37KhN3A the process of carbide formation takes place along with bainitic transformation, and LTTMT results in lesser strengthening. LTTMT is fount to not practically affect the tendency of structural steels to bainitic brittleness. This treatment promotes some shift of brittleness manifestation to lower temperatures

Material physical properties of 12 chromium ferritic steel

International Nuclear Information System (INIS)

Ando, Masanori; Wakai, Takashi; Aoto, Kazumi

2003-09-01

High chromium ferritic steel is an attractive candidate for structural material of the next Fast Breeder Reactor, since both of thermal properties and high temperature strength of the steel are superior to those of conventional austenitic stainless steels. In this study, physical properties of 12Cr steels are measured and compared to those obtained in the previous studies to discuss about stochastic dispersions. The effect of measurement technique on Young's modulus and the influence of the specimen size on coefficient of thermal expansion are also investigated. The following conclusions are obtained. (1) Young's modulus of 12Cr steels obtained in this study tends to larger than those obtained in the previous studies especially in high temperature. Such a discrepancy is resulted from the difference in measurement technique. It was clarified that Young's modulus obtained by free vibration method is more adequate those obtained by the cantilever characteristic vibration method. Therefore, the authors recommend using the values obtained by free vibration method as Young's modulus of 12Cr steels. (2) Both instant and mean coefficient of thermal expansion of 12Cr steels obtained in this study is in a good agreement with those obtained in the previous studies. However, the obviously different values are obtained from the measurement by large size specimens. Such a discrepancy is resulted from heterogeneous during heating process of the specimens. Therefore, the authors recommend using the values obtained by φ4 x 20 mm specimens as instant and mean coefficient of thermal expansion of 12Cr steels. (3) Specific heat of 12Cr steels obtained in this study agree with those obtained in the previous studies with a few exceptions. (4)Thermal conductivity of 12Cr steels obtained in this study agree with those obtained in the previous studies. (5) It was confirmed that instant and mean coefficient of thermal expansion, density, specific heat and thermal conductivity of 12Cr steels

Phase 1/2 study of pacritinib, a next generation JAK2/FLT3 inhibitor, in myelofibrosis or other myeloid malignancies

Directory of Open Access Journals (Sweden)

Srdan Verstovsek

2016-12-01

Full Text Available Abstract Background Pacritinib (SB1518 is a highly selective kinase inhibitor with specificity for JAK2, FLT3, IRAK1, and CFS1R. This multicenter phase 1/2 study evaluated the maximum tolerated dose (MTD, safety, and clinical activity of pacritinib in patients with myelofibrosis (MF and other advanced myeloid malignancies. Methods In the phase 1 dose-escalation part of the study, 43 adults with advanced myeloid malignancies received pacritinib 100 to 600 mg once daily (QD. In the phase 2 part of the study, 31 adults with refractory or intermediate- or high-risk newly diagnosed MF and any degree of cytopenia received pacritinib 400 mg QD. The primary endpoint is a ≥35% reduction in spleen volume at week 24 as determined by magnetic resonance imaging. Results Five patients (11.6% experienced a dose-limiting toxicity during cycle 1 of phase 1. The clinical benefit rate was 86.0% (13 patients achieving clinical improvement and 24 patients having stable disease. The MTD was established at 500 mg QD, and the recommended phase 2 dose was 400 mg QD. In phase 2, the primary endpoint was achieved by 23.5% of evaluable patients (4/17, with 47.4% (9/19 achieving a ≥50% spleen length reduction at week 24 as measured by physical examination. At week 24, 38.9% of evaluable patients (7/18 achieved a ≥50% decrease in MF Quality of Life and Symptom Assessment total score. Gastrointestinal toxicities were the most common adverse events and were predominantly grade 1/2 in severity. Grade 3/4 anemia was reported in 5/31 patients and grade 3/4 thrombocytopenia was reported in 3/31 patients. The most frequent AEs considered to be treatment related were diarrhea (28/31, nausea (15/31, vomiting (9/31, and fatigue (4/31. Grade 3 treatment-related AEs were reported in seven patients (22.6%, four of whom had diarrhea. No grade 4/5 treatment-related AEs were reported. No leukopenia, neutropenia, or lymphopenia were reported. Conclusions Pacritinib was well

Distal C terminus of CaV1.2 channels plays a crucial role in the neural differentiation of dental pulp stem cells.

Directory of Open Access Journals (Sweden)

Jianping Ge

Full Text Available L-type voltage-dependent CaV1.2 channels play an important role in the maintenance of intracellular calcium homeostasis, and influence multiple cellular processes. C-terminal cleavage of CaV1.2 channels was reported in several types of excitable cells, but its expression and possible roles in non-excitable cells is still not clear. The aim of this study was to determine whether distal C-terminal fragment of CaV1.2 channels is present in rat dental pulp stem cells and its possible role in the neural differentiation of rat dental pulp stem cells. We generated stable CaV1.2 knockdown cells via short hairpin RNA (shRNA. Rat dental pulp stem cells with deleted distal C-terminal of CaV1.2 channels lost the potential of differentiation to neural cells. Re-expression of distal C-terminal of CaV1.2 rescued the effect of knocking down the endogenous CaV1.2 on the neural differentiation of rat dental pulp stem cells, indicating that the distal C-terminal of CaV1.2 is required for neural differentiation of rat dental pulp stem cells. These results provide new insights into the role of voltage-gated Ca(2+ channels in stem cells during differentiation.

Effect of heat treatment regime on structural lamination in ferritic-austenitic steels

International Nuclear Information System (INIS)

Sizov, R.A.; Zakharova, M.I.; Novikov, I.I.; Bannykh, O.A.

1983-01-01

The effect of preliminary thermal treatment on lamination and viscosity of EhP-53 and KO-3 steels after durable aging at the temperature of 350 is studied. It is shown that preliminary heat treatment considerably affects lamination processes in the result of aging of 0Kh18G8N2T steel. The lowest rate of lamination and higher impact strength after aging at 350 deg C for 4500 hours corresponds to the following heat treatment: 10 hour aging at 650 deg C with cooling in the air, then quenching in water from 950 deg C after aging for 30 min and the following tempering (650 deg C, 5 hours). Unlike the 0Kh18G8N2T steel, lamination parameters of steel 0Kh22N6T practically do not change after the application of heat treatment. Nevertherless, taking into account results of impact strength, it is advisable to have thermal treatment according to the regime: quenching in water at 950 deg C after aging for 30 min

Energy distributions study of spallation neutrons produced at 0 deg. by proton beams (0.8 GeV and 1.6 GeV) and deuteron beams (1.2 and 1.6 GeV)

International Nuclear Information System (INIS)

Martinez, Eugenie

1997-01-01

We are studying the energy distributions of spallation neutrons produced at 0 deg. by protons of 0.8 GeV up to 1.6 GeV and deuterons of 1.2 and 1.6 GeV with two complementary experimental techniques: the time of flight measurement with tagged incident protons for low energy neutrons (3-400 MeV) and the use of a magnetic spectrometer at high energy (E ≥ 200 MeV). These measurements enable us to measure for the first time the neutron spectra for incident energies higher than 800 MeV. We have compared the double differential cross sections produced with 1.2 GeV protons on several thin targets (Al, Fe, Zr, W, Pb and Th). The neutron production obtained for a lead target is also studied for various energies (0.8 up to 1.6 GeV) and incident particles (p, d). Data are compared with theoretical simulations carried out using the TIERCE system and the intranuclear cascade model of J. Cugnon associated to the decay code of D. Durand. The neutron spectra calculated by using the HETC and MCNP codes, included in TIERCE, are significantly higher than the measured distributions. A better agreement is observed with the results of the Cugnon's cascade model. (author) [fr

Effect of heat treatment and irradiation temperature on mechanical properties and structure of reduced-activation Cr-W-V steels of bainitic, martensitic, and martensitic-ferritic classes

International Nuclear Information System (INIS)

Gorynin, I.V.; Rybin, V.V.; Kursevich, I.P.; Lapin, A.N.; Nesterova, E.V.; Klepikov, E.Yu.

2000-01-01

Effects of molybdenum replacement by tungsten in steels of the bainitic, martensitic, and martensitic-ferritic classes containing 2.5%, 8% and 11% Cr, respectively, were investigated. The phase composition and structure of the bainitic steels were varied by changing the cooling rates from the austenitization temperature (from values typical for normalization up to V=3.3 x 10 -2 deg. C/s) and then tempering. The steels were irradiated to a fluence of 4x10 23 n/m 2 (≥0.5 MeV) at 270 deg. C and to fluences of 1.3x10 23 and 1.2x10 24 n/m 2 (≥0.5 MeV) at 70 deg. C. The 2.5Cr-1.4WV and 8Cr-1.5WV steels have shown lower values of the shifts in ductile-brittle transition temperature (DBTT) under irradiation in comparison with corresponding Cr-Mo steels. Radiation embrittlement at elevated irradiation temperature was lowest in bainitic 2.5Cr-1.4WV steel and martensitic-ferritic 11Cr-1.5WV steel. The positive effect of molybdenum replacement by tungsten at irradiation temperature ∼300 deg. C is reversed at T irr =70 deg. C

Austenite strengthening and softening during hot deformation

International Nuclear Information System (INIS)

Tushinskij, L.I.; Vlasov, V.S.; Kazimirova, I.E.; Tokarev, A.O.

1981-01-01

Processes of formation of austenite structure of 20 and 12Kh18N10T steels during hot deformation and postdeformation isothermal holdings have been investigated by the methods of analysis of curves of hot deformation, high-temperature metallography and light microscopy. Deformation has been exercised by extention in vacuum with average 4x10 -2 s -1 rate. Deformation temperatures of steel 20 are 930 and 1000 deg C, of steel 12Kh18N10T - 1100 deg C. It is stated that dynamic recrystallization takes place in both investigated steels during hot deformation. In the carbonic steel it is developed by shifting sections of high-angular boundaries, flow stress in this case remains constant. Recrystallization is developed by subgrain coalescence in austenite steel, that brings about preservation of increased defect density in recrystallized volumes. As a result strengthening of steel is continued up to fracture during the increase of the deformation degree. Postdeformation weakening of 12Kh18N10T steel is slowed down as compared with weakening of carbonic steel [ru

Effect of explosion hardening on the properties of the near-surface layer of glow-discharged nitrided 33H3MF steel

International Nuclear Information System (INIS)

Rudnicki, J.; Fleszar, A.; Wierzchon, T.; Maranda, A.; Nowaczewski, J.

1999-01-01

The study was concerned with the effect of explosion hardening of 33H3MF steel, realized by the impact of the detonation products of a metallic plate driven by the detonation of an explosive plastic material, upon the microhardness and thickness of the nitrided layers forming during the glow discharge assisted nitridation process. Nitrided layers containing a compound zone, diffusion layers and layers with braunite content were formed on explosion-hardened steel surfaces. The corrosion resistance of the nitrided layers thus obtained was compared with that of the layers formed on non-hardened surfaces and on non-hardened and nitrided surfaces. The layers examined have a higher corrosion resistance than the starting material, but lower than the nitrided layers formed without the explosive load. The impact strength of the steel samples was examined before and after the explosion hardening and also after glow discharge assisted nitriding. It has been found that the explosion hardening followed by nitriding increases the impact strength, which is an advantageous effect. This also gives evidence that the changes in the hardness and structure of the samples examined, which are only observed in the layers whose thickness falls between 0.1 and 1.5 mm do not affect the notch present on the sample surface and thus have no influence upon the character of the sample fracture. (author)

Ergonomic assessment of brake and accelerator mechanisms of MF285 and MF399 tractors using electromyography method

Directory of Open Access Journals (Sweden)

A Nikkhah

2016-04-01

Full Text Available Introduction: Too many people are working in the agricultural sector and therefore, pay more attention to the safety and health at work in the agricultural sector is important. This issue is more important in developing industrial countries where the level of the ergonomic working condition is less than that of developed countries. Attention to ergonomic condition of agricultural machinery drivers is one of the goals of agricultural mechanization. Therefore, in this study the ergonomic conditions of brake and accelerator mechanisms for MF285 and MF399 tractor's drivers were investigated using a new method. Materials and Methods: 25 people were selected for experiment. The electrical activity of Medialis gastrocnemius, Lateralis gastrocnemius, Vastus medialis, Vastus lateralis, Quadratus Lumborum and Trapezius muscles of drivers before and during pressing the pedal and after rest time were recorded using Biovision device. Measurements were performed for each person on each muscle 30 seconds before pressing the pedal, 60 seconds after pressing the pedal and after 60 seconds of rest. For all drivers, the muscles on the right side (brake and accelerator side have been selected and tested. The measurements were performed in compliance with appropriate time intervals between the measurements. Results and Discussion: Ergonomic assessment of brake pedal: The results showed that the RMS electrical activity of muscles of Vastus medialis and Medial gastrocnemius, during 60 seconds braking were 2.47 and 1.97. So, Vastus medialis and Medial gastrocnemius had the highest stress during pressing the MF399 tractor's brake pedal. Moreover, the Medial gastrocnemius and Lateral gastrocnemius with RMS electrical activity ratio of 2.47 and 1.74 had the highest RMS electrical activity ratio respectively, during 60 seconds braking compared to before braking of MF285 tractor. The comparison of results showed that the Vastus medialis and Trapezius had the higher stress

Substitution of modified 9 Cr-1 Mo steel for austentic stainless steels

International Nuclear Information System (INIS)

Sikka, V.K.

1982-04-01

This report describes the current program to develop a high-strength ferritic-martensitic steel. The alloy is essentially Fe-9% Cr-1% Mo with small additions of V and Nb and is known as modifed 9 Cr-1 Mo steel. Its elevated-temperature properties and design allowable stresses match those of type 304 stainless steel for temperatures up to 600 0 C and exceed those of other ferritic steels by factors of 2 to 3. The improved strength of this alloy permits its use in place of stainless steels for many applications

Measurement of neutron captured cross-sections in 1-2 MeV

Energy Technology Data Exchange (ETDEWEB)

Kim, Gi Dong; Kim, Young Sek; Kim, Jun Kon; Yang, Tae Keun [Korea Institutes of Geoscience and Mineral Resources, Taejeon (Korea)

2001-04-01

The measurement of neutron captured reaction cross sections was performed to build the infra system for the production of nuclear data. MeV neutrons were produced with TiT target and {sup 3}T(p,n){sup 3}He reaction. The characteristics of TiT thin film was analyzed with ERD-TOF and RBS. The results was published at Journal of the Korea Physical Society (SCI registration). The energy, the energy spread and the flux of the produced neutron were measured. The neutron excitation functions of {sup 12}C and {sup 16}O were obtained to confirm the neutron energy and neutron energy spread. The neutron energy spread found to be 1.3 % at the neutron energy of 2.077 MeV. The {sup 197}Au(n,{gamma}) reaction was performed to obtain the nerutron flux. The maximum neutron flux found to be 1 x 10{sup 8} neutrons/sec at the neutron energy of 2 MeV. The absolute efficiency of liquid scintillation detector was obtained in the neutron energy of 1 - 2 MeV. The fast neutron total reaction cross sections of Cu, Fe, and Au were measured with sample in-out method. Also the neutron captured reaction cross sections of {sup 63}Cu were measured with fast neutron activation method. The measurement of neutron total reaction cross sections and the neutron captured reaction cross sections with fast neutrons were first tried in Korea. The beam pulsing system was investigated and the code of calculating the deposition spectrums for primary gamma rays was made to have little errors at nuclear data. 25 refs., 28 figs., 14 tabs. (Author)

Fireside corrosion and steamside oxidation of 9-12% Cr martensitic steels exposed for long term testing

DEFF Research Database (Denmark)

Montgomery, Melanie; Jensen, S. A.; Rasmussen, F.

2009-01-01

MoV121 and HCM12 for the 12% Cr steels. The test tubes were welded in as part of the existing final superheaters in actual plants and exposure has been conducted over a ten year period (1994-2005). Compared to the older steel types, T92 and HCM12 utilise tungsten to improve their creep strength. From......To obtain long term corrosion and steam oxidation data for the 9-12%Cr ferritic steels, test tube sections have been exposed in Amager 3 and Avedore 1 coal fired power plants in Denmark (formerly run by ENERGI E2). Thus direct comparisons can be made for T91 and T92 for the 9% Cr steels and X20Cr...... Avedore I testing, T91 and T92 can be compared for exposure times up to similar to 48 000 h exposure. From Amager 3 testing, X20, HCM12 and T92 were tested; T92 has been exposed for up to 31 000 h and X20 and HCM12 have had 84 500 h exposure. Tube sections were removed for various exposure durations...

Structural basis for the differential effects of CaBP1 and calmodulin on CaV1.2 calcium-dependent inactivation

Science.gov (United States)

Findeisen, Felix; Minor, Daniel L.

2010-01-01

Calcium-binding protein 1 (CaBP1), a calmodulin (CaM) homolog, endows certain voltage-gated calcium channels (CaVs) with unusual properties. CaBP1 inhibits CaV1.2 calcium-dependent inactivation (CDI) and introduces calcium-dependent facilitation (CDF). Here, we show that the ability of CaBP1 to inhibit CaV1.2 CDI and induce CDF arises from interaction between the CaBP1 N-lobe and interlobe linker residue Glu94. Unlike CaM, where functional EF hands are essential for channel modulation, CDI inhibition does not require functional CaBP1 EF-hands. Furthermore, CaBP1-mediated CDF has different molecular requirements than CaM-mediated CDF. Overall, the data show that CaBP1 comprises two structural modules having separate functions: similar to CaM, the CaBP1 C-lobe serves as a high-affinity anchor that binds the CaV1.2 IQ domain at a site that overlaps with the Ca2+/CaM C-lobe site, whereas the N-lobe/linker module houses the elements required for channel modulation. Discovery of this division provides the framework for understanding how CaBP1 regulates CaVs. PMID:21134641

The relation between experiments and modeling of rapidly solidified 12Cr-Mo-V stainless steel

DEFF Research Database (Denmark)

Pryds, Nini; Hattel, Jesper Henri

1998-01-01

Solidification during melt spinning of a 12Cr-Mo-V stainless steel has been experimentally studied and numerically simulated. The resulting microstructures have been related to the unknown parameter h, i.e. the heat transfer coefficient between the substrate and the melt, by fitting the heat flow...... of metastable austenite as the primary phase near the chill side of the ribbon. Upon quenching to room temperature, this austenite transformed into martensite. At a distance of about 15 mu m from the chill surface, the growth velocity of the solid/liquid interface decreased (

The LBL 1-2 GeV synchrotron radiation source

International Nuclear Information System (INIS)

Selph, F.B.

1987-06-01

The design of the 1 to 2 GeV Synchrotron Radiation Source to be built at the Lawrence Berkeley Laboratory is described. The goal of this facility is to provide very high brightness photon beams in the ultraviolet and soft x-ray regions. The photon energy range to be served is from 0.5 eV to 10 keV, with the brightest beams available in the 1 eV to 1 keV interval. For time-resolved experiments, beam pulses of a few tens of picoseconds will be available. Emphasis will be on the use of undulators and wigglers to produce high quality, intense beams. Initially, four of the former and one of the latter devices will be installed, with six long straight sections left open for future installations. In addition, provision is being made for 48 beamlines from bending magnets. The storage ring is optimized for operation at 1.5 GeV, with a maximum energy of 1.9 GeV. The injection system includes a 1.5 GeV booster synchrotron for full energy injection at the nominal operating energy of the storage ring. Filling time for the maximum storage ring intensity of 400 mA is about 2 minutes, and beam lifetime will be about 6 hours. Attention has been given to the extraordinary requirements for beam stability, and to the need to independently control photon beam alignment. Typical rms beam size in insertion regions is 201 μm horizontal, and 38 μm vertical. The manner in which this design achieves very high spectral brightness from undulators and wigglers, while maintaining a modest value for the beam current, will be described. Primarily, this requires that the design of the lattice, the arrangement of bending magnets, focusing quadrupoles and straight sections, be done with this in mind

Effect of preliminary neutron irradiation on helium blistering of 0Kh16N15M3B steel

International Nuclear Information System (INIS)

Chernov, I.I.; Kalin, B.A.; Skorov, D.M.; Shishkin, G.N.; Ivanov, M.V.

1982-01-01

The method of electron microscopy has been applied to investigate the effect of preliminary neutron irradiation on the OKh16N15M3B steel blistering under irradiation by 20 keV helium ions with (1-10)x10 21 ion/m 2 doses at the temperature below 373 K. It is shown that neutron irradiation shifts critical doses of blister formation and intense scaling towards higher doses. But after the incubation period the erosion of steel preliminary neutron irradiated grows with the increase of helium ion dose above 7x10 21 ion/m 2 . Short-term heating of neutron irradiated samples during 15 min at 1173 K does not practically affect the beginning of intense scaling of the surface

The influence of welding and post heat treatment parameters on the diffusion and precipitation processes in dissimilar metal joints of a 1% and a 12% Cr-steel

International Nuclear Information System (INIS)

Kullik, M.; Katerbau, K.H.

1989-05-01

The influences of different weld metals, welding processes and post weld heat treatments (PWHT) on mechanical properties, carbon diffusion and precipitation processes were investigated by studying dissimilar metal welds between the cast steel GS-17 CrMoV 5 11 (1% Cr) and the steel X 20 CrMoV 12 1 (12% Cr). By means of tensile and impact tests, metallographic investigation, hardness measurements, electron beam X-ray microanalysis and transmission electron microscope examination changes in the welded joints were shown after different PWHT's as well as after creep tests. It was found that the joint with a 5% CrMoV-weld metal shows higher yield and rupture strength than the joint with a 12% CrMoV-weld metal. With increasing heat input during PWHT the strength decreases for both welds, but always remains higher than the values of the base materials. During PWTH as well as during service at elevated temperatures carbon diffuses from the lower chromium material to the higher chromium material. Width and carbon concentration of the carburized and decarburized zones depend on the heat input. A simple diffusion model was developed to describe the carbon profile for any annealing time and temperature. The consequence of the decarburization is a microstructural change in the heat effected zone of the cast steel. During longer annealing the fine M 2 C-carbides dissolve and coarse M 6 C-crbides form, resulting in a lower creep ductility of this zone. (orig.) With 19 refs., 15 tabs., 104 figs [de

Precipitation process of Z-phase in 9-12%CR steels

DEFF Research Database (Denmark)

Danielsen, Hilmar Kjartansson

2014-01-01

Precipitation of Z-phase, Cr(V,Nb)N, is known to negatively affect creep properties of 9-12%Cr steels for power plant applications as it dissolves finely distributed MX particles, (V,Nb)N, especially in high Cr steels. As the Z-phase precipitates slowly as large particles, this causes a net drop ...... and crystallographically into Z-phase CrTaN particles. Copyright © 2014 Electric Power Research Institute, Inc. Distributed by ASM International®. All rights reserved....

Study of the interaction{pi}{sup +}p at 1.2 GeV/c {pi}{sup +} laboratory momentum; Estudio de la inteeraccion {pi}{sup +} p a 1,2 GeV/c

Energy Technology Data Exchange (ETDEWEB)

Ladron de Guevara, P

1973-07-01

We present the main results of a 0.33 events/urban experiment of {pi}{sup +} interactions in hydrogen at 1.2 GeV/c, using the 80 cm Saclay bubble chamber. the partial cross sections of the different reactions and the elastic differential cross section are computed by normalizing to the total cross section obtained by other groups. (Author) 34 refs.

Effect of rhenium and osmium on mechanical properties of a 9Cr-2W-0.25V-0.07Ta-0.1C steel

International Nuclear Information System (INIS)

Klueh, R.L.; Alexander, D.J.; Sokolov, M.A.

2000-01-01

The nuclear transmutation of tungsten to rhenium and osmium in a tungsten-containing steel irradiated in a fission or fusion reactor will change the chemical composition of the steel. To determine the possible consequences of such compositional changes on the mechanical properties, tensile and Charpy impact properties were measured on five 9Cr-2W-0.25V-0.07Ta-0.1C steels that contained different amounts of rhenium, osmium, and tungsten. The mechanical properties changes caused by these changes in composition were minor. Observations were also made on the effect of carbon concentration. The effect of carbon on tensile behavior was minor, but there was a large effect on Charpy properties. Several of the steels showed little effect of tempering temperature on the Charpy transition temperature, a behavior that was tentatively attributed to the low silicon and/or manganese concentration of the experimental steels

Microstructure of a high boron 9-12% chromium steel

Energy Technology Data Exchange (ETDEWEB)

Andren, H.O. [Chalmers Univ. of Technology, Goeteborg (Sweden). Dept. of Applied Physics

2008-07-01

Additions of small amounts of boron (10-100 ppm) to 9-12% chromium steels are often made since they have been found to be beneficial for the creep strength up to and above 600 C. The effect of boron is to restrict the coarsening of M{sub 23}C{sub 6} precipitates during service. It was found that increasing the boron content from 9 to 40 ppm gave a decrease in coarsening constant at 600 C by a factor of 2. The present understanding of boron solution, non-equilibrium grain boundary segregation, incorporation into M{sub 23}C{sub 6}, and diffusion is reviewed in the paper. A very high boron addition (300 ppm) was made in the trial TAF steel already in the 1950'ies. The microstructure of a similar trial steel, FT3B, has been studied detail. In this steel large Mo, Cr, Fe and V containing metal borides are formed rather than the expected BN, with the crystal structure M{sub 2}B{sub 2}. Nitrogen is therefore still available for the formation of VN. Due to tempering at a low temperature (690 C) to a high strength (830 MPa), this steel contained a dense distribution of very small VN precipitates, 5-15 nm in size. A similar VN distribution is probably the cause of the still unsurpassed creep strength of the TAF steel. (orig.)

Differential cross sections of proton Compton scattering at photon laboratory energies between 1.2 and 1.7 GeV

International Nuclear Information System (INIS)

Duda, J.; Hoefner, F.W.; Jung, M.; Kleissler, R.; Kueck, H.; Leu, P.; Marne, K.D. de; Munk, B.; Vogl, W.; Wedemeyer, R.

1982-11-01

Differential cross sections of proton Compton scattering have been measured at the Bonn 2.5 GeV synchrotron. The experiment covers photon laboratory energies between 1.2 GeV and 1.7 GeV and the square of the four-momentum transfer ranges from t = -0.17 GeV 2 to -0.98 GeV 2 corresponding to c.m. scattering angles between 35 0 and 80 0 . The cross sections exhibit a forward peak followed by a monotone fall-off up to the largest measured vertical stroketvertical stroke-values. Fits of the form dsigma/dt = A.exp(Bt) to the data points with vertical stroketvertical stroke 2 yield forward cross sections A, which are consistent with the 0 0 cross sections calculated from the measured total photon-proton cross section. The average slope is B = 5.6 +- 0.14 GeV 2 . (orig.)

X-ray diffraction study of slags forming during corrosion resistant steel production

International Nuclear Information System (INIS)

Slavov, V.I.; Zadorozhnaya, V.N.; Shurygina, A.V.

1990-01-01

Using X-ray diffraction analysis slags, forming during corrosion-resistant 12Kh18N10T grade steel production by two flowsheets, are studied. Standard two-slag technology of steel production does not provide efficient disintegration of chromospinelides in slags, gives high steel contamination with respect to nonmetallic impurities, coarse structure and, as a consequence, presence of macrodefects on rolled products surface. One-slag steel melting technology with titanium alloying of the steel at vacuum causes fast removal of chromospinelides at the beginning of reduction period, promotes titanium absorption by the steel, refines nonmetallic inclusions, provides more fine structure and steel plasticity, removes surface defects

Effect of KH2PO4 on gene expression, morphological and biochemical characteristics of stevia rebaudiana Bertoni under in vitro conditions.

Science.gov (United States)

Kahrizi, D; Ghari, S M; Ghaheri, M; Fallah, F; Ghorbani, T; Beheshti Ale Agha, A; Kazemi, E; Ansarypour, Z

2017-08-15

Stevia rebaudiana is one of the most important biologically sourced and low-calorie sweeteners Bertoni that has a lot of steviol glycosides. Tissue culture is the best for propagation of stevia and micro nutrients can affect both morphological traits and steviol glycosides production. Therefore, the effect of different concentrations of KH2PO4on stevia growth factors and gene expression had been studied by tissue culture methods, RT-PCR and HPLC. According the results, bud numbers had increased significantly in MS + 0.034 mMKH2PO4 media and the highest measured length was seen in plants grown under MS + 0.034 mM KH2PO4 treatment. Also, the highest growth rate (1.396 mm/d) was observed in MS + 0.034 mMKH2PO4.The best concentration of KH2PO4 for expression of UGT74G1 was 0.00425mMand the best one for UGT76G1 expression was 0.017mM. Interestingly, the best media for both stevioside and rebaudioside A accumulation was 0.017mM KH2PO4containing media. There was positive correlation between the best media for gene expression and the best one for steviol glycosides production.

Joint formation of dissimilar steels in pressure welding with superposition of ultrasonic oscillations

Energy Technology Data Exchange (ETDEWEB)

Surovtsev, A P; Golovanenko, S A; Sukhanov, V E; Kazantsev, V F

1983-12-01

Investigation results of kinetics and quality of carbon steel joints with the steel 12Kh18N10T, obtained by pressure welding with superposition of ultrasonic oscillations with the frequency 16.5-18.0 kHz are given. The effect of ultrasonic oscillations on the process of physical contact development of the surfaces welded, formation of microstructure and impact viscosity of the compound, is shown.

Quasi-exclusive measurement of /sup 12/C(/sup 12/C, 3. cap alpha. )X at 2. 1 GeV/nucleon

Energy Technology Data Exchange (ETDEWEB)

Engelage, J; Baumgartner, M; Greiner, D E; Lindstrom, P J; Olson, D L; Wada, R; Crawford, H J; Webb, M L

1986-05-29

A study of the reaction /sup 12/C(/sup 12/C,3..cap alpha..)X at 2.1 GeV/nucleon has been completed. The energy and momentum transferred to the /sup 12/C projectile and the cross section for the dissociation of /sup 12/C into three alpha particles have been measured, 9.7 (+5.0/-2.5) millibarns. It is found that the results from this analysis are inconsistent with the predictions of current theoretical models for peripheral relativistic heavy ion collisions.

Dielectron production in {sup 12}C+{sup 12}C collisions at 1 GeV per nucleon; Dielektronenproduktion in {sup 12}C+{sup 12}C Kollisionen bei 1 GeV pro Nukleon

Energy Technology Data Exchange (ETDEWEB)

Pachmayer, Yvonne C.

2008-08-22

This thesis contains the experimental results on dielectron production in {sup 12}C+{sup 12}C collisions at 1 GeV/u recorded with HADES. Within this work, the analysis is demonstrated, showing that leptons are efficiently reconstructed and hadrons very well discriminated. The described pair analysis shows that the combinatorial background is successfully reduced and the amount of true electron-positron pairs is not decreased. After subtracting the combinatorial background, the efficiency-corrected and normalized invariant-mass, transverse momentum and rapidity distributions of the dileptons are investigated. In the invariant-mass region 0.2-0.6 GeV/c{sup 2} the measured pair yield shows a strong excess above the contribution expected from hadron decays after freeze-out according to predictions. Together with the results obtained in {sup 12}C+{sup 12}C at 2 GeV/u it becomes evident that the overshoot of the data increases with decreasing beam energy. A detailed analysis shows that the beam energy dependence of the excess yield, i.e. the pair yield above the known eta contribution, integrated over the 0.15-0.5 GeV/c{sup 2} mass range, scales like pion production. (orig.)

Calculation of radiation loss of 1.2 GeV-electrons in a thick silicon monocrystal

International Nuclear Information System (INIS)

Keshtova, S.V.; Komarov, F.F.

1988-01-01

The angular distribution of radiation loss of different fractions of 1.2 GeV-electrons during axial channeling in a Si monocrystal of 1.6 mm thickness is discussed. The results of the numerical calculations are compared with the experimental data. (author)

Celecoxib induces proliferation and Amphiregulin production in colon subepithelial myofibroblasts, activating erk1-2 signaling in synergy with EGFR.

Science.gov (United States)

Benelli, Roberto; Venè, Roberta; Minghelli, Simona; Carlone, Sebastiano; Gatteschi, Beatrice; Ferrari, Nicoletta

2013-01-01

The COX-2 inhibitor Celecoxib, tested in phase III trials for the prevention of sporadic colon adenomas, reduced the appearance of new adenomas, but was unable to affect the incidence of colon cancer. Moreover the 5years follow-up showed that patients discontinuing Celecoxib treatment had an increased incidence of adenomas as compared to the placebo arm. In the APC(min/+) mouse model short term treatment with Celecoxib reduced gut adenomas, but a prolonged administration of the drug induced fibroblast activation and intestinal fibrosis with a final tumor burden. The way Celecoxib could directly activate human colon myofibroblasts (MF) has not yet been investigated. We found that MF are activated by non toxic doses of Celecoxib. Celecoxib induces erk1-2 and Akt phosphorylation within 5'. This short term activation is apparently insufficient to cause phenotypic changes, but the contemporary triggering of EGFR causes an impressive synergic effect inducing MF proliferation and the neo-expression and release of Amphiregulin (AREG), a well known EGFR agonist involved in colon cancer progression. As a confirm to these observations, the erk inhibitor U0126 and the EGFR inhibitors Tyrphostin and Cetuximab were able to contrast AREG induction. Our data provide evidence that Celecoxib directly activates MF empowering EGFR signaling. According to these results the association with EGFR (or erk1-2) inhibitors could abolish the off-target activity of Celecoxib, possibly extending the potential of this drug for colon cancer prevention. Copyright © 2012 Elsevier Ireland Ltd. All rights reserved.

Proteolytic cleavage and PKA phosphorylation of α1C subunit are not required for adrenergic regulation of CaV1.2 in the heart.

Science.gov (United States)

Katchman, Alexander; Yang, Lin; Zakharov, Sergey I; Kushner, Jared; Abrams, Jeffrey; Chen, Bi-Xing; Liu, Guoxia; Pitt, Geoffrey S; Colecraft, Henry M; Marx, Steven O

2017-08-22

Calcium influx through the voltage-dependent L-type calcium channel (Ca V 1.2) rapidly increases in the heart during "fight or flight" through activation of the β-adrenergic and protein kinase A (PKA) signaling pathway. The precise molecular mechanisms of β-adrenergic activation of cardiac Ca V 1.2, however, are incompletely known, but are presumed to require phosphorylation of residues in α 1C and C-terminal proteolytic cleavage of the α 1C subunit. We generated transgenic mice expressing an α 1C with alanine substitutions of all conserved serine or threonine, which is predicted to be a potential PKA phosphorylation site by at least one prediction tool, while sparing the residues previously shown to be phosphorylated but shown individually not to be required for β-adrenergic regulation of Ca V 1.2 current (17-mutant). A second line included these 17 putative sites plus the five previously identified phosphoregulatory sites (22-mutant), thus allowing us to query whether regulation requires their contribution in combination. We determined that acute β-adrenergic regulation does not require any combination of potential PKA phosphorylation sites conserved in human, guinea pig, rabbit, rat, and mouse α 1C subunits. We separately generated transgenic mice with inducible expression of proteolytic-resistant α 1C Prevention of C-terminal cleavage did not alter β-adrenergic stimulation of Ca V 1.2 in the heart. These studies definitively rule out a role for all conserved consensus PKA phosphorylation sites in α 1C in β-adrenergic stimulation of Ca V 1.2, and show that phosphoregulatory sites on α 1C are not redundant and do not each fractionally contribute to the net stimulatory effect of β-adrenergic stimulation. Further, proteolytic cleavage of α 1C is not required for β-adrenergic stimulation of Ca V 1.2.

Specific electrical conductivity in molten potassium dihydrogen phosphate KH2PO4 - An electrolyte for water electrolysis at ∼300°C

DEFF Research Database (Denmark)

Nikiforov, Aleksey Valerievich; Berg, Rolf W.; Petrushina, Irina

2016-01-01

The conductivity of pure molten KH2PO4 salt and four mixtures with more or less water (KH2PO4-H2O and KH2PO4-KPO3 systems, respectively) were measured at temperatures of 240-320°C and under their own water vapor pressures. Molten KH2PO4 has been proven to be a promising electrolyte for an elevated...

Investigation of intergranular corrosion resistance of Cr16Ni25NMo6 steel

International Nuclear Information System (INIS)

Kamenev, Yu.B.; Nazarov, A.A.; Kuusk, L.V.; Majdeburova, T.F.

1990-01-01

The effect of 08Kh16N25AM6 steel susceptibility to intergranular corrosion on its intergranular cracking resistance in high-temperature water is investigated. In addition, the performed tests point to the susceptibility of sensibilized Kh16N25AM6 steel to intergranular corrosion in media simulating an agressive environment of power generation equipment; the latter requires a strict control over the resistance of weld joints of the above steel to intergranular corrosion. It is shown that Kh16N25AM6 type steel in sensibilized state is susceptible to intercrystalline corrosion cracking in high-temperature water which correlates with its susceptibility to intergranular corrosion established by AM GOST 6032-84 and potentiodynamic reactivation methods

Anion-sensitive regions of L-type CaV1.2 calcium channels expressed in HEK293 cells.

Directory of Open Access Journals (Sweden)

Norbert Babai

2010-01-01

Full Text Available L-type calcium currents (I(Ca are influenced by changes in extracellular chloride, but sites of anion effects have not been identified. Our experiments showed that CaV1.2 currents expressed in HEK293 cells are strongly inhibited by replacing extracellular chloride with gluconate or perchlorate. Variance-mean analysis of I(Ca and cell-attached patch single channel recordings indicate that gluconate-induced inhibition is due to intracellular anion effects on Ca(2+ channel open probability, not conductance. Inhibition of CaV1.2 currents produced by replacing chloride with gluconate was reduced from approximately 75%-80% to approximately 50% by omitting beta subunits but unaffected by omitting alpha(2delta subunits. Similarly, gluconate inhibition was reduced to approximately 50% by deleting an alpha1 subunit N-terminal region of 15 residues critical for beta subunit interactions regulating open probability. Omitting beta subunits with this mutant alpha1 subunit did not further diminish inhibition. Gluconate inhibition was unchanged with expression of different beta subunits. Truncating the C terminus at AA1665 reduced gluconate inhibition from approximately 75%-80% to approximately 50% whereas truncating it at AA1700 had no effect. Neutralizing arginines at AA1696 and 1697 by replacement with glutamines reduced gluconate inhibition to approximately 60% indicating these residues are particularly important for anion effects. Expressing CaV1.2 channels that lacked both N and C termini reduced gluconate inhibition to approximately 25% consistent with additive interactions between the two tail regions. Our results suggest that modest changes in intracellular anion concentration can produce significant effects on CaV1.2 currents mediated by changes in channel open probability involving beta subunit interactions with the N terminus and a short C terminal region.

Extinction of Contextual Cocaine Memories Requires Cav1.2 within D1R-Expressing Cells and Recruits Hippocampal Cav1.2-Dependent Signaling Mechanisms.

Science.gov (United States)

Burgdorf, Caitlin E; Schierberl, Kathryn C; Lee, Anni S; Fischer, Delaney K; Van Kempen, Tracey A; Mudragel, Vladimir; Huganir, Richard L; Milner, Teresa A; Glass, Michael J; Rajadhyaksha, Anjali M

2017-12-06

Exposure to cocaine-associated contextual cues contributes significantly to relapse. Extinction of these contextual associations, which involves a new form of learning, reduces cocaine-seeking behavior; however, the molecular mechanisms underlying this process remain largely unknown. We report that extinction, but not acquisition, of cocaine conditioned place preference (CPP) in male mice increased Ca v 1.2 L-type Ca 2+ channel mRNA and protein in postsynaptic density (PSD) fractions of the hippocampus, a brain region involved in drug-context associations. Moreover, viral-mediated deletion of Ca v 1.2 in the dorsal hippocampus attenuated extinction of cocaine CPP. Molecular studies examining downstream Ca v 1.2 targets revealed that extinction recruited calcium/calmodulin (Ca 2+ /CaMK)-dependent protein kinase II (CaMKII) to the hippocampal PSD. This occurred in parallel with an increase in phosphorylation of the AMPA GluA1 receptor subunit at serine 831 (S831), a CaMKII site, along with an increase in total PSD GluA1. The necessity of S831 GluA1 was further demonstrated by the lack of extinction in S831A GluA1 phosphomutant mice. Of note hippocampal GluA1 levels remained unaltered at the PSD, but were reduced near the PSD and at perisynaptic sites of dendritic spines in extinction-resistant S831A mutant mice. Finally, conditional knock-out of Ca v 1.2 in dopamine D1 receptor (D1R)-expressing cells resulted in attenuation of cocaine CPP extinction and lack of extinction-dependent changes in hippocampal PSD CaMKII expression and S831 GluA1 phosphorylation. In summary, we demonstrate an essential role for the hippocampal Ca v 1.2/CaMKII/S831 GluA1 pathway in cocaine CPP extinction, with data supporting contribution of hippocampal D1R-expressing cells in this process. These findings demonstrate a novel role for Ca v 1.2 channels in extinction of contextual cocaine-associated memories. SIGNIFICANCE STATEMENT Continued drug-seeking behavior, a defining characteristic of

[Effects of different amounts of phosphate fertilizers on copper, zinc transfer in red soil under the application of KH2PO4].

Science.gov (United States)

Guo, Liang; Li, Zhong-wu; Huang, Bin; Wang, Yan; Zhang, Yan

2014-09-01

In order to study the effects of different phosphate addition amounts on migration and transformation of heavy metals (Cu, Zn) in soil, an indoor leaching experiment using soil columns was carry out to study the leaching behavior of Cu and Zn. The KH2PO4 was chosen as the fertilizer application at the doses of 5 mg.kg-1, 15 mg.kg-1 and 25 mg.kg-1. The results showed that KH2PO4, could reduce the leachate pH, but different phosphate amounts had little effect on leachate pH, pH in leachate kept rising in the whole leaching process. With the application of KH2PO4, Cu migration was mainly in the surface layer while Zn migrated into deeper soil. Concentrations of Cu, Zn in deep soil leachate were low indicating that it was harmless to the shallow groundwater. After leaching, heavy metals mainly existed in the residual form in soil, the proportion of residual form of Cu was around 60% and the proportion of residual form of Zn was around 40%. High concentration of KH2PO4 helps the transformation of Zn from residual organic combination state to exchange state.

Catalytic oxidation of 1,2-DCBz over V2O5/TiO2-CNTs: effect of CNT diameter and surface functional groups.

Science.gov (United States)

Du, Cuicui; Wang, Qiulin; Peng, Yaqi; Lu, Shengyong; Ji, Longjie; Ni, Mingjiang

2017-02-01

A series of V 2 O 5 /TiO 2 -carbon nanotube (CNT) catalysts were prepared and tested to decompose gaseous 1,2-dichlorobenzene (1,2-DCBz). Several physicochemical methods, including nitrogen adsorption, scanning electron microscopy (SEM), transmission electron microscopy (TEM), X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS) and H 2 temperature-programmed reduction (TPR) were employed to characterise their physicochemical properties. To better understand the effect of CNT properties on the reactivity of V 2 O 5 /TiO 2 -CNT catalysts, the 1,2-DCBz residue remaining in the off-gas and on the catalyst surface were both collected and analysed. The results indicate that the outer diameter and the surface functional groups (hydroxide radical and carboxyl) of CNTs significantly influence upon the catalytic activity of CNT-containing V 2 O 5 /TiO 2 catalysts: the CNT outer diameter mainly affects the aggregation of CNTs and the π-π interaction between the benzene ring and CNTs, while the introduction of -OH and -COOH groups by acid treatment can further enlarge specific surface area (SSA) and contribute to a higher average oxidation state of vanadium (V aos ) and supplemental surface chemisorbed oxygen (O ads ). In addition, the enhanced mobility of lattice oxygen (O latt) also improves the oxidation ability of the catalysts.

Crucial factors of the inflammatory microenvironment (IL-1β/TNF-α/TIMP-1) promote the maintenance of the malignant hemopoietic clone of myelofibrosis: an in vitro study.

Science.gov (United States)

Sollazzo, Daria; Forte, Dorian; Polverelli, Nicola; Romano, Marco; Perricone, Margherita; Rossi, Lara; Ottaviani, Emanuela; Luatti, Simona; Martinelli, Giovanni; Vianelli, Nicola; Cavo, Michele; Palandri, Francesca; Catani, Lucia

2016-07-12

Along with molecular abnormalities (mutations in JAK2, Calreticulin (CALR) and MPL genes), chronic inflammation is the major hallmark of Myelofibrosis (MF). Here, we investigated the in vitro effects of crucial factors of the inflammatory microenvironment (Interleukin (IL)-1β, Tumor Necrosis Factor (TNF)-α, Tissue Inhibitor of Metalloproteinases (TIMP)-1 and ATP) on the functional behaviour of MF-derived circulating CD34+ cells.We found that, regardless mutation status, IL-1β or TNF-α increases the survival of MF-derived CD34+ cells. In addition, along with stimulation of cell cycle progression to the S-phase, IL-1β or TNF-α ± TIMP-1 significantly stimulate(s) the in vitro clonogenic ability of CD34+ cells from JAK2V617 mutated patients. Whereas in the JAK2V617F mutated group, the addition of IL-1β or TNF-α + TIMP-1 decreased the erythroid compartment of the CALR mutated patients. Megakaryocyte progenitors were stimulated by IL-1β (JAK2V617F mutated patients only) and inhibited by TNF-α. IL-1β + TNF-α + C-X-C motif chemokine 12 (CXCL12) ± TIMP-1 highly stimulates the in vitro migration of MF-derived CD34+ cells. Interestingly, after migration toward IL-1β + TNF-α + CXCL12 ± TIMP-1, CD34+ cells from JAK2V617F mutated patients show increased clonogenic ability.Here we demonstrate that the interplay of these inflammatory factors promotes and selects the circulating MF-derived CD34+ cells with higher proliferative activity, clonogenic potential and migration ability. Targeting these micro-environmental interactions may be a clinically relevant approach.

Choice of corrosion-resistant metal for fluotitanic acid

International Nuclear Information System (INIS)

Reingeverts, M.D.; Lapchenko, E.P.; Semenyuk, E.Y.

1986-01-01

The authors investigate the corrosion and anodic behavior of steels 12Kh18N10T, 08Kh21N6M2T, and 06KhN28MDT, nickel, and molybdenum in 10-40% naturally aerated solutions of H 2 TiF 6 at 20 and 50 degrees C. The authors found that in solutions of fluotitanic acid, as also in tetrafluoroboric and hydrofluoric acids, the most stable alloys are chromium-nickel-molybdenum alloy of type 06KhN28MDT and (for acid concentrations above 20%) copper-nickel-alloys of the monel metal type. Steels 12Kh18N10T and 08Kh21N6M2T can be used in acid concentrations of less than 10% and temperatures up to 20 degrees C with anodic protection

Wastage-resistant characteristics of 12Cr steel tube material. Small leak sodium-water reaction test

International Nuclear Information System (INIS)

Shimoyama, Kazuhito

2004-03-01

In the water leak accident of a steam generator designed for a sodium cooled reactor in the Feasibility Study, the localization of tube failure propagation by using an advanced water leak detector will be required from the viewpoints of the safety and economical efficiency of the plant. So far, the conventional knowledge and analytical tools have been used in the investigation and evaluation of water leak phenomenon; nevertheless, there was neither test data nor the study of quantitative evaluation on the corrosion behavior, so-called wastage-resistant characteristics, of 12Cr steel tube material in sodium-water reactions. Wastage tests for the 12Cr steel tube material were conducted in small water leaks by use of the Sodium-Water Reaction Test Rig (SWAT-1R), and the data of wastage rate were obtained in the parameter of water leak rate under the constant sodium temperature and distance between leak and target tubes. The test results lead to the following conclusions: (1) The wastage-resistibility of 12Cr steel is 1.6 times greater than that of 9Cr steel and is 2.7 times greater than that of 2.25Cr-1Mo steel. (2)The wastage-resistibility of 12Cr steel increases in smaller water leaks; especially in water leak rates of 1 g/sec or less, it is more excellent than that of SUS321 stainless steel used as Monju superheater tube material. (3) Based on the correlation of wastage rate for the 9Cr steel, the correlation for the 12Cr steel has been obtained to be used for the evaluation of tube failure propagation. As the correlation of wastage rate for the 12Cr steel is based on the correlation for the 9Cr steel, it gives enough conservatism in smaller water leaks. To serve in accurately evaluating the tube failure propagation in smaller water leaks, it is necessary to obtain new correlation of wastage rate for the 12Cr steel based on the data in the wide range of water leak rates. (author)

A theory of piezoelectric, elastic, and dielectric properties of the KH2PO4 family crystals under the strain u6. Phase transition and the piezoelectric effect in the KH2PO4 crystal

International Nuclear Information System (INIS)

Levits'kij, R.R.; Lyisnij, B.M.

2003-01-01

In order to study the dielectric, piezoelectric and elastic properties of ferroelectrics and antiferroelectrics of the KH 2 PO 4 family, we consider an extended proton tunneling model that takes into account the shear strain u 6 . In the four-particle cluster approximation for the short-range interactions and the mean field approximation for the long-range interaction we calculate the transverse components of the dielectric susceptibility tensor of the KH 2 PO 4 family ferroelectrics

[JAK2 V617F and exon 12 genetic variations in Korean patients with BCR/ABL1-negative myeloproliferative neoplasms].

Science.gov (United States)

Kim, Jeong Tae; Cho, Yong Gon; Choi, Sam Im; Lee, Young Jin; Kim, Hye Ran; Jang, Sook Jin; Moon, Dae Soo; Park, Young Jin; Park, Geon

2010-12-01

JAK2 genetic variations have been described in a high proportion of patients with BCR/ABL1-negative myeloproliferative neoplasms (MPN). This study was designed to analyze the frequencies of JAK2 V617F and exon 12 variations, and their correlations with clinical characteristics of Korean patients with BCR/ABL1-negative MPN. We examined a total of 154 patients with BCR/ABL1-negative MPN that included 24, 26, 89, and 15 patients with polycythemia vera (PV), primary myelofibrosis (PMF), essential thrombocythemia (ET), and unclassified myeloproliferative neoplasms (MPNU), respectively. We performed allele-specific PCR to detect V617F in all BCR/ABL1-negative patients, and performed direct sequencing to detect exon 12 variations in 47 V617F-negative MPN patients. JAK2 c.1641+179_183del5 variation was detected by restriction fragment length polymorphism assay in 176 healthy subjects. JAK2 V617F was detected in 91 patients (59.1%): PV (91.6%), PMF (46.2%), ET (52.8%), and MPNU (66.7%). In V617F-negative MPN patients, no mutations were found in exon 12. The c.1641+179_183del5 was detected in 68.1% of V617F-negative MPN patients and 45.4% of healthy subjects (P=0.008). JAK2 V617F was closely correlated with age and leukocytosis in BCR/ABL1-negative MPN patients (P<0.05). However, c.1641+179_183del5 was not related to age, sex, or complete blood cell count parameters in V617F-negative MPN patients and healthy subjects. The c.1641+179_183del5 was associated with an increased odds ratio for MPN (odds ratio, 2.6; 95% confidences interval, 1.3-5.1; P=0.007). Frequencies of V617F are similar to reported results. JAK2 exon 12 mutations may be rare and c.1641+179_183del5 may influence the occurrence of MPN in Korean patients with V6 17F-negative MPN.

Measurement of charged pions in {sup 12}C+{sup 12}C collisions at 1A GeV and 2A GeV with HADES

Energy Technology Data Exchange (ETDEWEB)

Agakishiev, G.; Destefanis, M.; Gilardi, C.; Kirschner, D.; Kuehn, W.; Lange, J.S.; Metag, V.; Novotny, R.; Pechenov, V.; Pechenova, O.; Perez Cavalcanti, T.; Spataro, S.; Spruck, B. [Justus Liebig Universitaet Giessen, II. Physikalisches Institut, Giessen (Germany); Agodi, C.; Coniglione, R.; Finocchiaro, P.; Maiolino, C.; Piattelli, P.; Sapienza, P. [Laboratori Nazionali del Sud, Istituto Nazionale di Fisica Nucleare, Catania (Italy); Balanda, A.; Kozuch, A.; Przygoda, W. [Jagiellonian University of Cracow, Smoluchowski Institute of Physics, Krakow (Poland); Panstwowa Wyzsza Szkola Zawodowa, Nowy Sacz (Poland); Bellia, G. [Laboratori Nazionali del Sud, Istituto Nazionale di Fisica Nucleare, Catania (Italy); Universita di Catania, Dipartimento di Fisica e Astronomia, Catania (Italy); Belver, D.; Cabanelas, P.; Duran, I.; Garzon, J.A.; Lamas-Valverde, J.; Marin, J. [University of Santiago de Compostela, Departamento de Fisica de Particulas, Santiago de Compostela (Spain); Belyaev, A.; Chernenko, S.; Fateev, O.; Ierusalimov, A.; Zanevsky, Y. [Joint Institute of Nuclear Research, Dubna (Russian Federation); Bielcik, J.; Braun-Munzinger, P.; Galatyuk, T.; Gonzalez-Diaz, D.; Heinz, T.; Holzmann, R.; Koenig, I.; Koenig, W.; Kolb, B.W.; Lang, S.; Muench, M.; Palka, M.; Pietraszko, J.; Rustamov, A.; Schroeder, C.; Schwab, E.; Simon, R.S.; Traxler, M.; Yurevich, S.; Zumbruch, P. [GSI Helmholtzzentrum fuer Schwerionenforschung, Darmstadt (Germany); Blanco, A.; Lopes, L.; Mangiarotti, A. [LIP-Laboratorio de Instrumentacao e Fisica Experimental de Particulas, Coimbra (Portugal); Bortolotti, A.; Michalska, B. [Sezione di Milano, Istituto Nazionale di Fisica Nucleare, Milano (Italy); Boyard, J.L.; Hennino, T.; Moriniere, E.; Ramstein, B.; Roy-Stephan, M.; Sudol, M. [CNRS/IN2P3 - Universite Paris Sud, Institut de Physique Nucleaire, Orsay Cedex (France); Christ, T.; Eberl, T.; Fabbietti, L.; Friese, J.; Gernhaeuser, R.; Jurkovic, M.; Kruecken, R. [and others

2009-04-15

We present the results of a study of charged-pion production in {sup 12}C+{sup 12}C collisions at incident beam energies of 1A GeV and 2A GeV using the HADES spectrometer at GSI. The main emphasis of the HADES program is on the dielectron signal from the early phase of the collision. Here, however, we discuss the data with respect to the emission of charged hadrons, specifically the production of {pi}{sup {+-}} mesons, which are related to neutral pions representing a dominant contribution to the dielectron yield. We have performed the first large-angular-range measurement of the distribution of {pi}{sup {+-}} mesons for the {sup 12}C+{sup 12}C collision system covering a fairly large rapidity interval. The pion yields, transverse-mass and angular distributions are compared with calculations done within a transport model, as well as with existing data from other experiments. The anisotropy of pion production is systematically analyzed. (orig.)

A comparison of low-chromium and high-chromium reduced-activation steels for fusion applications

International Nuclear Information System (INIS)

Klueh, R.L.; Maziasz, P.J.; Alexander, D.J.

1996-01-01

Ferritic steels have been considered candidate structural materials for first wall and blanket structures for fusion power plants since the late 1970s. The first steels considered in the United States were the conventional Cr-Mo steels Sandvik HT9 (nominally 12Cr-1Mo-0.25V-0.5W-0.5Ni-0.2C, here designated l2Cr-1MoVW), modified 9Cr-1Mo steel (9Cr-1Mo-0.2V-0.06Nb-0. IC, designated 9Cr-1MoVNb) and, to a lesser extent, 2 1/4Cr-1Mo steel (2.25Cr-Mo-0.1C). All compositions are in wt. %. The normalized-and-tempered 9 and 12Cr steels had a tempered martensite microstructure, and the normalized-and-tempered 2 1/4 Cr steel had a tempered bainite microstructure. This report describes chromium steels tested in normalized and tempered conditions. Miniature tensile and Charpy specimens were tested

Damping capacity of unstable steels on chromium-nickel-manganese base

Energy Technology Data Exchange (ETDEWEB)

Kochkin, L.I.; Rudakov, A.A. (Kirovskij Politekhnicheskij Inst. (USSR))

1982-02-01

The paper deals with results of a study on the energy scattering in OKh13N3G8, 20Kh13N3G4 and 30Kh13N3G4 unstable steels. It is shown that the development of microplastic strains most easily occurs in low-carbon steel having a two-phase structure in the initial state. The proceeding of microplastic deformations in carbon unstable steels is limited by the interstitial atom effect on the dislocation movement. It is established that in OKh13N3G8 steel the martensite ..cap alpha --> gamma..- transformation begins under the cyclic stress amplitudes below the yield point of this steel. The steels studied possess a high vibrostrength.

Experimental verification of lifetime of bolting joints for WWER reactor pressure vessels

International Nuclear Information System (INIS)

Brumovsky, M.; Polachova, H.

1992-01-01

This paper presents results from experimental verification of cyclic lifetime of bolting joints of M 140x6 mm type used for WWER-440 MW reactor pressure vessels. Bolting joints or real dimensions were tested in a special testing equipment ZS 1000 in Skoda Concern. Stud bolts are made from 25Kh1MF or 38KhN3MFA type of steels. Tests were carried out at operating as well as at room temperatures with coefficient of asymmetry equal to 0.1; one tests was realized with given bending moment. Experimental results have been compared with calculated lifetimes according to ASME, Soviet and CMEA Codes. In all cases calculations give conservative assessments. (orig.)

Dielectron production in 12C+12C collisions at 1 GeV per nucleon

International Nuclear Information System (INIS)

Pachmayer, Yvonne C.

2008-01-01

This thesis contains the experimental results on dielectron production in 12 C+ 12 C collisions at 1 GeV/u recorded with HADES. Within this work, the analysis is demonstrated, showing that leptons are efficiently reconstructed and hadrons very well discriminated. The described pair analysis shows that the combinatorial background is successfully reduced and the amount of true electron-positron pairs is not decreased. After subtracting the combinatorial background, the efficiency-corrected and normalized invariant-mass, transverse momentum and rapidity distributions of the dileptons are investigated. In the invariant-mass region 0.2-0.6 GeV/c 2 the measured pair yield shows a strong excess above the contribution expected from hadron decays after freeze-out according to predictions. Together with the results obtained in 12 C+ 12 C at 2 GeV/u it becomes evident that the overshoot of the data increases with decreasing beam energy. A detailed analysis shows that the beam energy dependence of the excess yield, i.e. the pair yield above the known eta contribution, integrated over the 0.15-0.5 GeV/c 2 mass range, scales like pion production. (orig.)

Study of the /sup 12/N 2. 43 MeV level. [Differential cross sections; 44 MeV /sup 3/He; 52 MeV p

Energy Technology Data Exchange (ETDEWEB)

Cecil, F E; Shepard, J R; Sercely, R R; Peterson, R J [Colorado Univ., Boulder (USA). Nuclear Physics Lab.; King, N S.P. [California Univ., Davis (USA). Crocker Nuclear Lab.

1976-10-11

The differential cross sections have been measured for the reactions /sup 12/C(/sup 3/He, /sup 3/He')/sup 12/C(17.77 MeV 0/sup +/ T = 1) and /sup 12/C(/sup 3/He, t)/sup 12/N(2.43 MeV) at Esub(/sup 3/He) = 44 MeV. The similar shapes of the angular distributions and the relative magnitudes of the cross sections suggest that the /sup 12/N 2.43 MeV level is the 0/sup +/ T = 1 analog to the /sup 12/C 17.77 MeV level. The reaction /sup 14/N(p, t)/sup 12/N(2.43 MeV) at Esub(p) = 52 MeV is also studied. The strength with which this level is excited in this reaction is consistent with reasonable two-step calculations assuming the 2.43 MeV level to have Jsup(..pi..) = 0/sup +/.

"1"2C fragmentation on thin targets at 95 MeV/A study for hadrontherapy

International Nuclear Information System (INIS)

Dudouet, Jeremie

2014-01-01

The nuclear models need to be improved in order to reach the required accuracy for a reference simulation code for hadrontherapy. In this context, two experiments have been performed by our collaboration on May 2011 and September 2013 at GANIL to study nuclear reactions of 95 MeV/u "1"2C ions on thin targets of medical interest to measure the double differential fragmentation cross sections of each produced isotope. These experimental data have been compared with Monte-Carlo simulations. Different nuclear models provided by the GEANT4 simulation toolkit have firstly been tested. These simulations revealed discrepancies up to one order of magnitude. The phenomenological model HIPSE has then been used and has shown that the overlapping region of two colliding nuclei needs to be taken into account in order to reproduce the kinematics of the emitted fragments at intermediates energies. Due to the difficulties encountered by these models in the data reproduction, a new model is currently under development: SLIIPIE. This one is a semi-microscopic model, built from a participant-spectator geometrical approach. This model was also compared to the experimental data for "1"2C+"1"2C reactions at 95 MeV/A giving promising results. (author) [fr

A Study on Structural, Corrosion, and Sensitization Behavior of Ultrafine and Coarse Grain 316 Stainless Steel Processed by Multiaxial Forging and Heat Treatment

Science.gov (United States)

Kiahosseini, Seyed Rahim; Mohammadi Baygi, Seyyed Javad; Khalaj, Gholamreza; Khoshakhlagh, Ali; Samadipour, Razieh

2018-01-01

Cubic specimens from AISI 316 stainless steel were multiaxially forged to 15 passes and annealed at 1200 °C for 1, 2, and 3 h and finally sensitized at 700 °C for 24 h. Examination of samples indicated that the hardness of the annealed samples was reduced from 153 to 110, 81, and 74 HV for as-received sample and under 1, 2, and 3 h of annealing, and increased from 245 to 288 HV for samples forged at 3 and 7 passes. However, no significant changes were observed in a large number of passes and at about 300 HV. Degree of sensitization of samples was increased to approximately 27.3% at 3-h annealing but reduced to 1.23% by 15 passes of MF. The potentiodynamic polarization test shows that the breakdown potentials decreased with annealing time from 0.6 to - 102 (mV/SCE) for as-received and 3-h annealed specimen. These potentials increased to approximately - 16.5 mV with the increase in MF passes to 15. These observations indicated that the chromium carbide deposition affects Cr-depleted zone, which can subsequently affect the degree of sensitization and pitting corrosion resistance of AISI 316 austenitic stainless steel.

Review of Z phase precipitation in 9–12 wt-%Cr steels

DEFF Research Database (Denmark)

Danielsen, Hilmar Kjartansson

2016-01-01

For high temperature applications, 9–12 wt-%Cr steels in fossil fired power plants rely upon precipitate strengthening from (V,Nb)N MX nitrides for long term creep strength. During prolonged exposure at service temperature, another nitride precipitates: Cr(V,Nb)NZ phase. The Z phases lowly replace......MX, eventually causing a breakdown in creep strength. The present paper reviews the Z phase and its behaviour in 9–12 wt-%Cr steels including thermodynamic modelling, crystal structure, nucleation process and precipitation rate as a function of chemical composition. The influence of Z phase precipitation upon...

Crustal Structure of Khövsgöl, Mongolia

Science.gov (United States)

Scott, A. M.; Meltzer, A.; Stachnik, J.; Russo, R.; Munkhuu, U.; Tsagaan, B.

2017-12-01

Mongolia is part of the Central Asian Orogenic Belt, an accretionary event that spanned 800 million years from the mid-Proterozoic to mid-Phanerozoic. As a result of the past collisional and rifting events, the modern Khövsgöl rift system of northern Mongolia contains a heterogeneous lithospheric structure. The current rift system has three parallel N-S trending basins that roughly align with terrane boundaries. Structures inherited during the accretionary events may be a factor influencing regional deformation. The forces that drive local deformation are not well understood, but varying processes have been proposed: far-field effects of India-Eurasian plate convergence, westward subduction of the Pacific plate, magmatic underplating at the base of the crust, mantle plume activity, and asthenospheric mantle convection. Determining the nature of crustal features within this poorly understood region may illuminate processes that control rifting within intracontinental settings. A network of 26 broadband seismic stations encompassing 200 square kilometers of the Khövsgöl rift system were deployed from August 2014 to June 2016. More than 2100 events were detected, and most earthquakes were concentrated near rift structures. Events between Busiin-Gol and Darkhad, the westernmost and central basins of the Khövsgöl rift system, are distributed within the crust. An active fault is outlined along the eastern border of the Darkhad basin. Khövsgöl earthquakes bound both sides of the rift. Along the northern border of Lake Khövsgöl, seismic events define a shallow active fault orthogonal to the basin. The largest event recorded within the network was a magnitude ml=5.2 located near the northeastern border of Lake Khövsgöl on 12-05-2014. The focal mechanism of this earthquake is predominantly strike-slip, but also includes an extensional component. This work focuses on earthquake relocation and calculating moment tensors and focal mechanisms of larger regional

Role of Al in Zn bath on the formation of the inhibition layer during hot-dip galvanizing for a 1.2Si-1.5Mn transformation-induced plasticity steel

Science.gov (United States)

Wang, Kuang-Kuo; Hsu, Chiung-Wen; Chang, Liuwen; Gan, Dershin; Yang, Kuo-Cheng

2013-11-01

This study investigated the interaction between the Al in the Zn bath and the surface oxides formed by selective oxidation on a 1.2Si-1.5Mn TRIP steel during hot-dip galvanizing. XPS and TEM were employed for characterization. The results indicated that the amorphous xMnO·SiO2 oxide could react with Al to form a Si-Mn-Al-containing oxide. The crystalline MnSiO3 and Mn2SiO4 oxides could be largely reduced by Al to form holes in the oxide film. Consequently, the steel covered by a layer of mixed xMnO·SiO2 and MnSiO3 could form a continuous Fe2Al5 inhibition layer and showed the highest galvanizability among the three samples examined.

K-n and K-p elastic scattering in K-d collisions from 1.2 to 2.2 GeV/c

International Nuclear Information System (INIS)

Declais, Y.; Duchon, J.; Louvel, M.; Patry, J.-P.; Seguinot, J.; Baillon, P.; Bruman, C.; Ferro-Luzzi, M.; Perreau, J.-M.; Ypsilantis, T.

1977-01-01

This report contains the detailed description of an experiment which has determined the differential cross section of the K - n→K - n elastic scattering reaction. The results are 12 angular distributions spanning the K - n c.m. energy interval from approximately 1.86 to approximately 2.32 GeV. The measurements have been performed at the CERN PS using a beam of negative kaons with momenta from 1.2 to 2.2 GeV/c incident on a liquid deuterium target. By means of electronic apparatus the process K - d→K - n psub(s) was identified and recorded; this process is basically the same as the K - n elastic reaction insofar as the spectator proton psub(s) has low momentum. The elastic reaction was derived from the above process by taking into account the Fermi motion of the target neutron and by introducing the appropriate corrections to compensate for the effects due to the composite nature of the neutron (double-scattering, final state interaction). These results, constituting the first extensive collection of data on the pure isospin 1 anti KN state have been used in conjunction with other data in a preliminary partial wave analysis of the anti KN elastic system over the c.m. energy range from 1.84 to 2.23 GeV. Mainly for testing purposes, a similar amount of data has been collected for the K - p elastic reaction also from K - d collisions (K - d→K - p nsub(s)). (Auth.)

L-type calcium channel CaV 1.2 in transgenic mice overexpressing human AbetaPP751 with the London (V717I) and Swedish (K670M/N671L) mutations.

Science.gov (United States)

Willis, Michael; Kaufmann, Walter A; Wietzorrek, Georg; Hutter-Paier, Birgit; Moosmang, Sven; Humpel, Christian; Hofmann, Franz; Windisch, Manfred; Knaus, Hans-Günther; Marksteiner, Josef

2010-01-01

Cumulative evidence indicates that amyloid-beta peptides exert some of their neurodegenerative effects through modulation of L-type voltage gated calcium channels, which play key roles in a diverse range of CNS functions. In this study we examined the expression of CaV1.2 L-type voltage gated calcium channels in transgenic mice overexpressing human AbetaPP751 with the London (V717I) and Swedish (K670M/N671L) mutations by immunohistochemistry in light and electron microscopy. In hippocampal layers of wild type and transgenic mice, CaV1.2 channels were predominantly localized to somato-dendritic domains of neurons, and to astrocytic profiles with an age-dependent increase in labeling density. In transgenic animals, CaV1.2-like immunoreactive clusters were found in neuronal profiles in association with amyloid-beta plaques. Both the number and density of these clusters depended upon age of animals and number of plaques. The most striking difference between wild type and transgenic mice was the age-dependent expression of CaV1.2 channels in reactive astrocytes. At the age of 6 month, CaV1.2 channels were rarely detected in reactive astrocytes of transgenic mice, but an incremental number of CaV1.2 expressing reactive astrocytes was found with increasing age of animals and number of amyloid-beta plaques. This study demonstrates that CaV1.2 channels are highly expressed in reactive astrocytes of 12-months of age transgenic mice, which might be a consequence of the increasing amyloid burden. Further studies should clarify which functional implications are associated with the higher availability of CaV1.2 channels in late stage Alzheimer's disease.

An Overview of the Effects of Alloying Elements on the Properties of Lightweight Fe-(15-35) Mn-(5-12) Al-(0.3-1.2) C Steel

Science.gov (United States)

Xing, Jia; Wei, Yinghui; Hou, Lifeng

2018-04-01

In this review, the influences of alloying elements on the phase constitution, density, and stacking fault energy of Fe-(15-35) Mn-(5-12) Al-(0.3-1.2) C lightweight steel are discussed. The mechanical properties of austenite single-phase and austenite-ferrite dual-phase Fe-Mn-Al-C steels processed by different procedures are also statistically analyzed. The austenite single-phase steel was found to possess superior strength and plasticity. Three reasonable explanations for the mechanism of plastic deformation are presented, namely, shear band-induced plasticity, microband-induced plasticity, and slip band refinement-induced plasticity.

Corrosion Fatigue Characteristics of 12Cr Alloy Steel in Na2SO4 Solution

Science.gov (United States)

Bae, D. H.; Cho, S. Y.

In order to estimate reliability of 12Cr alloy steel using as the turbine blade material of the steam power plant, its corrosion fatigue characteristics in Na2SO4 solution considering its percentage and temperature that were determined from the polarization test results were investigated, and compared with the results in air. The corrosion characteristic of 12Cr alloy steel was remarkably susceptible in 12.7wt.% (IM) Na2SO4 solution, and its susceptibility increased with the solution temperature increase. The corrosion fatigue characteristics in 12.7wt.% Na2SO4 solution were similar to that of in air at 25°C. The crack growth rate was however increased with the temperature of solution increase. The reasons showing such results are due to the difference of the crack growth mechanism according to the electro-chemical activity of the corrosion factors.

Creep behaviour of heat resistant steels. Pt. 2

International Nuclear Information System (INIS)

Kloos, K.H.; Granacher, J.; Oehl, M.

1993-01-01

Creep data scatter bands of steels 2.25 Cr-1 Mo and 12 Cr-1 Mo-0.3 V were evaluated with the aid of model functions based on time temperature parameters. From the times to reach given strain values, mean isostrain curves in the stress time diagramme were calculated and therefrom, mean creep curves were derived. On this basis, creep equations were established, which include primary-, secondary- and tertiary-creep and are valid in the main range of application of each steel. Further, mean stress strain curves from hot tensile tests were used to describe the initial plastic strain in the creep equations. The values calculated with the established creep equations agreed relatively well with the correspondent original scatter band values from the creep tests. (orig.) [de

Layered P2-Na 2/3 Co 1/2 Ti 1/2 O 2 as a high-performance cathode material for sodium-ion batteries

Energy Technology Data Exchange (ETDEWEB)

Sabi, Noha; Doubaji, Siham; Hashimoto, Kazuki; Komaba, Shinichi; Amine, Khalil; Solhy, Abderrahim; Manoun, Bouchaib; Bilal, Essaid; Saadoune, Ismael

2017-02-01

Layered oxides are regarded as promising cathode materials for sodium-ion batteries. We present Na2/3Co1/2Ti1/2O2 as a potential new cathode material for sodium-ion batteries. The crystal features and morphology of the pristine powder were characterized by X-ray diffraction (XRD) and scanning electron microscopy (SEM). The cathode material is evaluated in galvanostatic charge-discharge and galvanostatic intermittent titration tests, as well as ex-situ X-ray diffraction analysis. Synthesized by a high-temperature solid state reaction, Na2/3Co1/2Ti1/2O2 crystallizes in P2-type structure with P6(3)/mmc space group. The material presents reversible electrochemical behavior and delivers a specific discharge capacity of 100 mAh g(-1) when tested in Na half cells between 2.0 and 4.2 V (vs. Na+/Na), with capacity retention of 98% after 50 cycles. Furthermore, the electrochemical cycling of this titanium-containing material evidenced a reduction of the potential jumps recorded in the NaxCoO2 parent phase, revealing a positive impact of Ti substitution for Co. The ex-situ XRD measurements confirmed the reversibility and stability of the material. No structural changes were observed in the XRD patterns, and the P2-type structure was stable during the charge/discharge process between 2.0 and 4.2 V vs. Na+/Na. These outcomes will contribute to the progress of developing low cost electrode materials for sodium-ion batteries. (C) 2017 Elsevier B.V. All rights reserved.

Improving composition of protective coatings for steel casting

International Nuclear Information System (INIS)

Kuz'kina, N.N.; Pegov, V.G.; Bogatenkov, V.F.; Shub, L.G.; Raspopova, N.A.

1983-01-01

A radically new fuel-free slag-forming mixture used as protective coating for steel casting is introduced. The lack of combustible powders precludes explosion and fire Lazard in mixture preparation. Usage of the new mixture in stainless steel casting of Kh18N10T type permitted to improve the ingot surface quality and reduce spoilage from 1.16 to 0.66%

Development of ferritic steels for fusion reactor applications

Energy Technology Data Exchange (ETDEWEB)

Klueh, R.L.; Maziasz, P.J.; Corwin, W.R.

1988-08-01

Chromium-molybdenum ferritic (martensitic) steels are leading candidates for the structural components for future fusion reactors. However, irradiation of such steels in a fusion environment will produce long-lived radioactive isotopes that will lead to difficult waste-disposal problems. Such problems could be reduced by replacing the elements in the steels (i.e., Mo, Nb, Ni, N, and Cu) that lead to long-lived radioactive isotopes. We have proposed the development of ferritic steels analogous to conventional Cr-Mo steels, which contain molybdenum and niobium. It is proposed that molybdenum be replaced by tungsten and niobium be replaced by tantalum. Eight experimental steels were produced. Chromium concentrations of 2.25, 5, 9, and 12% were used (all concentrations are in wt %). Steels with these chromium compositions, each containing 2% W and 0.25% V, were produced. To determine the effect of tungsten and vanadium, 2.25 Cr steels were produced with 2% W and no vanadium and with 0.25% V and O and 1% W. A 9Cr steel containing 2% W, 0.25 V, and 0.07% Ta was also studied. For all alloys, carbon was maintained at 0.1%. Tempering studies on the normalized steels indicated that the tempering behavior of the new Cr-W steels was similar to that of the analogous Cr-Mo steels. Microscopy studies indicated that 2% tungsten was required in the 2.25 Cr steels to produce 100% bainite in 15.9-mm-thick plate during normalization. The 5Cr and 9Cr steels were 100% martensite, but the 12 Cr steel contained about 75% martensite with the balance delta-ferrite. 33 refs., 35 figs., 5 tabs.

Development of ferritic steels for fusion reactor applications

International Nuclear Information System (INIS)

Klueh, R.L.; Maziasz, P.J.; Corwin, W.R.

1988-08-01

Chromium-molybdenum ferritic (martensitic) steels are leading candidates for the structural components for future fusion reactors. However, irradiation of such steels in a fusion environment will produce long-lived radioactive isotopes that will lead to difficult waste-disposal problems. Such problems could be reduced by replacing the elements in the steels (i.e., Mo, Nb, Ni, N, and Cu) that lead to long-lived radioactive isotopes. We have proposed the development of ferritic steels analogous to conventional Cr-Mo steels, which contain molybdenum and niobium. It is proposed that molybdenum be replaced by tungsten and niobium be replaced by tantalum. Eight experimental steels were produced. Chromium concentrations of 2.25, 5, 9, and 12% were used (all concentrations are in wt %). Steels with these chromium compositions, each containing 2% W and 0.25% V, were produced. To determine the effect of tungsten and vanadium, 2.25 Cr steels were produced with 2% W and no vanadium and with 0.25% V and O and 1% W. A 9Cr steel containing 2% W, 0.25 V, and 0.07% Ta was also studied. For all alloys, carbon was maintained at 0.1%. Tempering studies on the normalized steels indicated that the tempering behavior of the new Cr-W steels was similar to that of the analogous Cr-Mo steels. Microscopy studies indicated that 2% tungsten was required in the 2.25 Cr steels to produce 100% bainite in 15.9-mm-thick plate during normalization. The 5Cr and 9Cr steels were 100% martensite, but the 12 Cr steel contained about 75% martensite with the balance delta-ferrite. 33 refs., 35 figs., 5 tabs

Caveolin-1 down-regulation is required for Wnt5a-Frizzled 2 signalling in Ha-RasV12 -induced cell transformation.

Science.gov (United States)

Lin, Hsiu-Kuan; Lin, Hsi-Hui; Chiou, Yu-Wei; Wu, Ching-Lung; Chiu, Wen-Tai; Tang, Ming-Jer

2018-05-01

Caveolin-1 (Cav1) is down-regulated during MK4 (MDCK cells harbouring inducible Ha-Ras V12 gene) transformation by Ha-Ras V12 . Cav1 overexpression abrogates the Ha-Ras V12 -driven transformation of MK4 cells; however, the targeted down-regulation of Cav1 is not sufficient to mimic this transformation. Cav1-silenced cells, including MK4/shCav1 cells and MDCK/shCav1 cells, showed an increased cell area and discontinuous junction-related proteins staining. Cellular and mechanical transformations were completed when MDCK/shCav1 cells were treated with medium conditioned by MK4 cells treated with IPTG (MK4+I-CM) but not with medium conditioned by MK4 cells. Nanoparticle tracking analysis showed that Ha-Ras V12 -inducing MK4 cells increased exosome-like microvesicles release compared with their normal counterparts. The cellular and mechanical transformation activities of MK4+I-CM were abolished after heat treatment and exosome depletion and were copied by exosomes derived from MK4+I-CM (MK4+I-EXs). Wnt5a, a downstream product of Ha-Ras V12 , was markedly secreted by MK4+I-CM and MK4+I-EXs. Suppression of Wnt5a expression and secretion using the porcupine inhibitor C59 or Wnt5a siRNA inhibited the Ha-Ras V12 - and MK4+I-CM-induced transformation of MK4 cells and MDCK/shCav1 cells, respectively. Cav1 down-regulation, either by Ha-Ras V12 or targeted shRNA, increased frizzled-2 (Fzd2) protein levels without affecting its mRNA levels, suggesting a novel role of Cav1 in negatively regulating Fzd2 expression. Additionally, silencing Cav1 facilitated the internalization of MK4+I-EXs in MDCK cells. These data suggest that Cav1-dependent repression of Fzd2 and exosome uptake is potentially relevant to its antitransformation activity, which hinders the activation of Ha-Ras V12 -Wnt5a-Stat3 pathway. Altogether, these results suggest that both decreasing Cav1 and increasing exosomal Wnt5a must be implemented during Ha-Ras V12 -driven cell transformation. © 2018 The Authors

Damping capacity of unstable steels on chromium-nickel-manganese base

International Nuclear Information System (INIS)

Kochkin, L.I.; Rudakov, A.A.

1982-01-01

The paper deals with results of a study on the energy scattering in OKh13N3G8, 20Kh13N3G4 and 30Kh13N3G4 unstable steels. It is shown that the development of microplastic strains most easily occurs in low-carbon steel having a two-phase structure in the initial state. The proceeding of microplastic deformations in carbon unstable steels is limited by the interstitial atom effect on the dislocation movement. It is established that in OKh13N3G8 steel the martensite α→γ- transformation begins under the cyclic stress amplitudes below the yield point of this steel. The steels studied possess a high vibrostrength [ru

Alloy Design and Development of Cast Cr-W-V Ferritic Steels for Improved High-Temperature Strength for Power Generation Applications

Energy Technology Data Exchange (ETDEWEB)

Klueh, R L; Maziasz, P J; Vitek, J M; Evans, N D; Hashimoto, N

2006-09-23

-Nb combination in COST CB2. To explore this question, nine more casting test blocks, four 3Cr steels and five 11Cr steels were purchased, and microstructure and mechanical properties studies similar to those described above for the first iteration of test blocks were conducted. Experimental results from the second iteration indicated that 11 Cr steels with excellent properties are possible. The 11Cr-1.5Mo-V-Nb steels were superior to 11Cr-2W-V-Ta steels, and it appears the former class of steels can be developed to have tensile and creep properties exceeding those of COST CB2. The W-Nb combination in an 11Cr-2W-V-Nb steel had tensile and short-time creep properties at 650 C better than the 11Cr-1.5Mo-V-Nb steels, although long-time low-stress properties may not be as good because of Laves phase formation. Based on the results, the next step in the development of improved casting steels involves acquisition of 11Cr-1.5Mo-V-Nb-N-B-C and 11Cr-2W-V-Nb-N-B-C steels on which long-term creep-rupture tests (>10,000 h) be conducted. For better oxidation and corrosion resistance, development of 11Cr steels, as opposed to a 9Cr steels, such as COST CB2, are important for future turbine designs that envision operating temperatures of 650 C.

Cyclic deformation behavior and microstructural changes of 12Cr-WMoV martensitic stainless steel at elevated temperature

International Nuclear Information System (INIS)

Song, X.L.; Yang, G.X.; Zhou, S.L.; Fan, H.; Yang, S.S.; Zhu, J.W.; Liu, Y.N.

2008-01-01

Strain-controlled uniaxial push-pull low-cycle fatigue tests were performed on 12Cr-WMoV martensitic stainless steel at room temperature and 600 deg. C. Specimens were tested at total strain amplitudes of 1.5% and 0.8% with a constant strain rate of 0.004 s -1 . The microstructures of the specimens subjected to different cycles were studied using transmission electron microscopy (TEM). Cyclic softening was observed at room temperature and 600 deg. C. TEM investigations revealed that cellular structures of dislocations were formed in the fatigued specimens at both room and elevated temperatures. Dynamic recovery has a very significant effect on the dislocation structure of specimens tested at elevated temperature. The thickness and density of the dislocation cell walls formed in specimens cycled at 600 deg. C are less than that at room temperature. Cellular dislocation structures formed during cycling are annihilated in the specimens subjected to 1 h annealing at 600 deg. C

Fasciola spp: Mapping of the MF6 epitope and antigenic analysis of the MF6p/HDM family of heme-binding proteins.

Directory of Open Access Journals (Sweden)

Victoria Martínez-Sernández

Full Text Available MF6p/FhHDM-1 is a small cationic heme-binding protein which is recognized by the monoclonal antibody (mAb MF6, and abundantly present in parenchymal cells and secreted antigens of Fasciola hepatica. Orthologs of this protein (MF6p/HDMs also exist in other causal agents of important foodborne trematodiasis, such as Clonorchis sinensis, Opisthorchis viverrini and Paragonimus westermani. Considering that MF6p/FhHDM-1 is relevant for heme homeostasis in Fasciola and was reported to have immunomodulatory properties, this protein is expected to be a useful target for vaccination. Thus, in this study we mapped the epitope recognized by mAb MF6 and evaluated its antigenicity in sheep. The sequence of the MF6p/FhHDM-1 ortholog from F. gigantica (MF6p/FgHDM-1 was also reported. By means of ELISA inhibitions with overlapping synthetic peptides, we determined that the epitope recognized by mAb MF6 is located within the C-terminal moiety of MF6p/FhHDM-1, which is the most conserved region of MF6p/HDMs. By immunoblotting analysis of parasite extracts and ELISA inhibitions with synthetic peptides we also determined that mAb MF6 reacted with the same intensity with F. hepatica and F. gigantica, and in decreasing order of intensity with C. sinensis, O.viverrini and P. westermani orthologs. On the contrary, mAb MF6 showed no reactivity against Dicrocoelium dendriticum and Schistosoma mansoni. The study of the recognition of peptides covering different regions of MF6p/FhHDM-1 by sera from immunized sheep revealed that the C-terminal moiety is the most antigenic, thus being of potential interest for vaccination. We also demonstrated that the production of antibodies to MF6p/FhHDM-1 in sheep infected by F. hepatica occurs relatively early and follows the same pattern as those produced against L-cathepsins.

Room and elevated temperature Mechanical Behavior of 9-12% Cr Steels

Energy Technology Data Exchange (ETDEWEB)

Dogan, Omer N.; Hawk, Jeffrey A.; Schrems, Karol K.

2005-02-01

The mechanical properties of medium Cr steels used in fossil fired power plants are very good because of their excellent high temperature microstructural stability. However, as the desire to increase the operating temperature (>650C) of the plant goes up, the need for steels that maintain their strength at these temperatures also increases. The mechanical properties of three medium Cr steels (0.08C-(9-12)Cr-1.2Ni-0.7Mo-3.0Cu-3.0Co-0.5Ti) were investigated through hardness, hot hardness and tensile measurements. The strength of the 9-12%Cr steels at room temperature after long-term isothermal aging (750C; 1000 hours) compares favorably with that of other power plant steels (e.g., P91). In addition, the elevated temperature strength and hot hardness also behave similarly. The mechanical behavior will be discussed in terms of the strength, elongation and tensile fracture characteristics.

Effect of elevated temperature on the composition, structure, and mechanical properties of diffusion chromized steel

International Nuclear Information System (INIS)

Osintsev, V.D.

1986-01-01

The author studies the effect of operating temperature for equipment in contact sections of sulfuric acid workshops on the structure and mechanical properties of the chromized coatings and core of chromized articles. The ferrite lattice spacing was determined in a DRON-0.5 diffractometer according to the line in copper K /sub alpha/ radiation exposure was carried out after layer-by-layer anodic etching of the coating in an aqueous solution. It was shown that diffusion chromizing may lead to a reduction in strength properties compared with those of unchromized steel. As a base for chromized articles intended for operation at temperatures up to 475 0 C it is desirable to use steels 09G2 or 09G25, or for operation at temperatures up to 540 0 C, steels 12KhM and 12MKh

TRANSCRIPTIONAL UPREGULATION OF α2δ-1 ELEVATES ARTERIAL SMOOTH MUSCLE CELL CAV1.2 CHANNEL SURFACE EXPRESSION AND CEREBROVASCULAR CONSTRICTION IN GENETIC HYPERTENSION

Science.gov (United States)

Bannister, John P.; Bulley, Simon; Narayanan, Damodaran; Thomas-Gatewood, Candice; Luzny, Patrik; Pachuau, Judith; Jaggar, Jonathan H.

2012-01-01

A hallmark of hypertension is an increase in arterial myocyte voltage-dependent Ca2+ (CaV1.2) currents that induces pathological vasoconstriction. CaV1.2 channels are heteromeric complexes comprising a pore forming CaV1.2α1 with auxiliary α2δ and β subunits. Molecular mechanisms that elevate CaV1.2 currents during hypertension and the potential contribution of CaV1.2 auxiliary subunits are unclear. Here, we investigated the pathological significance of α2δ subunits in vasoconstriction associated with hypertension. Age-dependent development of hypertension in spontaneously hypertensive rats (SHR) was associated with an unequal elevation in α2δ-1 and CaV1.2α1 mRNA and protein in cerebral artery myocytes, with α2δ-1 increasing more than CaV1.2α1. Other α2δ isoforms did not emerge in hypertension. Myocytes and arteries of hypertensive SHR displayed higher surface-localized α2δ-1 and CaV1.2α1 proteins, surface α2δ-1 to CaV1.2α1 ratio (α2δ-1:CaV1.2α1), CaV1.2 current-density and non-inactivating current, and pressure- and - depolarization-induced vasoconstriction than those of Wistar-Kyoto controls. Pregabalin, an α2δ-1 ligand, did not alter α2δ-1 or CaV1.2α1 total protein, but normalized α2δ-1 and CaV1.2α1 surface expression, surface α2δ-1:CaV1.2α1, CaV1.2 current-density and inactivation, and vasoconstriction in myocytes and arteries of hypertensive rats to control levels. Genetic hypertension is associated with an elevation in α2δ-1 expression that promotes surface trafficking of CaV1.2 channels in cerebral artery myocytes. This leads to an increase in CaV1.2 current-density and a reduction in current inactivation that induces vasoconstriction. Data also suggest that α2δ-1 targeting is a novel strategy that may be used to reverse pathological CaV1.2 channel trafficking to induce cerebrovascular dilation in hypertension. PMID:22949532

Influence of chemical heterogeneity of solid solutions on brittleness in chromium steels

International Nuclear Information System (INIS)

Madyanov, S.A.; Sedov, V.K.; Apaev, B.A.

1985-01-01

The role of chemical heterogeneity of solid solutions in formation of mechanical properties of Kh09, Kh15, Kh20, Kh19N2G5T chromium steels has been investigated. It is established that besides the known regioA of chemical heterogeneity in the vicinity of 475 deg C exists a high-temperature region (1000-1050 deg C), where maximum heteroge=- neity of chromium distribution in solid solution, is observed. Both types of chemical heterogeneity cause essential hardening of alloys, which becomes apparent in abrupt change of capability to microplastic deformation The mechanism of occurrence of the given temper brittleness consists in carbon diffusion into microvolunes enriched in carbide-forming elements

The RAG1 and RAG2 proteins establish the 12/23 rule in V(D)J recombination

NARCIS (Netherlands)

D.C. van Gent (Dik)

1996-01-01

textabstractV(D)J recombination requires a pair of signal sequences with spacer lengths of 12 and 23 base pairs. Cleavage by the RAG1 AND RAG2 proteins was previously shown to demand only a single signal sequence. Here, we established conditions where 12- and 23-spacer signal

An analysis of a set of creep data for a 9Cr-1Mo-0.2V (P91 type) steel

International Nuclear Information System (INIS)

Cadek, J.; Sustek, V.; Pahutova, M.

1997-01-01

Recently published creep data for a 9Cr-1Mo-0.2V steel are analysed and an attempt is made to interpret them applying the concept of thermally activated detachment of dislocations from carbide particles as the rate controlling process. For the data, very high and stress dependent apparent activation energy of creep, Q c , and very high and temperature dependent apparent stress exponent, m c , are characteristic. The modelling of creep behavior applying the above mentioned concept is shown to fail to account for this temperature and applied stress dependence of minimum creep strain rate and/or the values of Q c and m c following from the data analysis. It is suggested that the behavior of the dislocation substructure, which is affected by the presence of carbide particles, must be introduced into any model to adequately describe the unusual creep behavior of the steel of interest. (orig.)

Comparative estimation of weld-ability of medium-alloy steels

International Nuclear Information System (INIS)

Makarov, Eh.L.; Laz'ko, V.E.

1977-01-01

Weldability of various industrial steels has been investigated as affected by mutual presence of carbon and alloying elements in a wide range of concentrations. Mechanical properties and technological strength of medium alloyed steel welded joints have been compared. Technological strength parameters have been found to sharply decrease with increasing carbon content, the decrease depending on the alloying system. Resistance to hot and cold cracking is somewhat decreased by nickel and increased by molibdenum and tungsten. The best mechanical properties are displayed by steels of the Kh2GSNVM type. Industrial evidence on argon arc welding of different constructions made of steels 1.5-20 mm thick is compared to laboratory results. Accordingly, the high strength steels are divided into three groups, i.e. those manifesting good, satisfactory and poor weldability

Microstructure and elevated temperature stability of 9-12% Cr steels

Energy Technology Data Exchange (ETDEWEB)

Dogan, Omer N.; Hawk, Jeffrey A.

2005-02-01

Medium Cr steels have been used in fossil fired power plants for many years because of their excellent high temperature stability and mechanical properties. As the desire to increase the efficiency of power plants continues, the operating temperature (>650C) continues to go up. Currently available low and medium Cr containing steels will not withstand the new operating temperature and must be reassessed in terms of their solid-solution and precipitation strengthening schemes. Three medium Cr steels were developed to investigate high temperature alloy strengthening strategies: 0.08C-(9-12)Cr-1.2Ni-0.7Mo-3.0Cu-3.0Co-0.5Ti. The microstructure of the alloy will be described in the as-cast and thermo-mechanically worked states. In addition, the effect on microstructure from long-term high temperature exposure will also be discussed. Finally, the overall stability of these steels will be compared against currently available power plant steels.

Solidification Segregation and Homogenization Behavior of 1Cr-1.25Mo-0.25V Steel Ingot

Energy Technology Data Exchange (ETDEWEB)

Kim, Dong-Bae [Dae-gu Mechatronics and Materials Institute, Daegu (Korea, Republic of); Na, Young-Sang; Seo, Seong-Moon [Korea Institute of Materials Science, Changwon (Korea, Republic of); Lee, Je-Hyun [Changwon National University, Changwon (Korea, Republic of)

2016-09-15

As a first step to optimizing the homogenization heat treatment following high temperature upset forging, the solidification segregation and the homogenization behaviors of solute elements were quantitatively analyzed for 1Cr-1.25Mo-0.25V steel ingot by electron probe micro-analysis (EPMA). The random sampling approach, which was designed to generate continuous compositional profiles of each solute element, was employed to clarify the segregation and homogenization behaviors. In addition, ingot castings of lab-scale and a 16-ton-sized 1Cr-1.25Mo-0.25V steel were simulated using the finite element method in three dimensions to understand the size effect of the ingot on the microsegregation and its reduction during the homogenization heat treatment. It was found that the microsegregation in a large-sized ingot was significantly reduced by the promotion of solid state diffusion due to the extremely low cooling rate. On the other hand, from the homogenization point of view, increasing the ingot size causes a dramatic increase in the dendrite arm spacing, and hence the homogenization of microsegregation in a large-sized ingot appears to be practically difficult.

Unit rupture work as a criterion for quantitative estimation of hardenability in steel

International Nuclear Information System (INIS)

Kramarov, M.A.; Orlov, E.D.; Rybakov, A.B.

1980-01-01

Shown is possible utilization of high sensitivity of resistance to fracture of structural steel to the hardenability degree in the course of hardening to find the quantitative estimation of the latter one. Proposed is a criterion kappa, the ratio of the unit rupture work in the case of incomplete hardenability (asub(Tsub(ih))) under investigation, and the analoguc value obtained in the case of complete hardenability Asub(Tsub(Ch)) at the testing temperature corresponding to the critical temperature Tsub(100(M). Confirmed is high criterion sensitivity of the hardened steel structure on the basis of experimental investigation of the 40Kh, 38KhNM and 38KhNMFA steels after isothermal hold-up at different temperatures, corresponding to production of various products of austenite decomposition

Influence of Z-phase on long-term creep stability of martensitic 9-12% Cr steels

Energy Technology Data Exchange (ETDEWEB)

Danielsen, Hilmar K. [Technical Univ. of Denmark, Lyngby (Denmark). Dept. of Mechanical Engineering; Hald, John [DONG Energy A/S (Denmark); Vattenfall (Denmark)

2010-07-01

The long-term creep strength of the new generation of martensitic creep resistant 9-12%Cr steels since the well-known steel Grade 91 relies strongly on particle strengthening by fine Mn nitrides based on V and Nb. During long-term high-temperature exposures the Mn nitrides may be replaced by the thermodynamically more stable Z-phases (Cr(V,Nb)N) causing a breakdown in creep strength. Cr contents above 10.5% strongly accelerate Z-phase precipitation, which explains the lack of success for all attempts to develop martensitic creep resistant steels with high Cr content for oxidation protection. However 9%Cr steels do not seem to be affected by the Z-phase. Careful control of the Z-phase precipitation process has led to the design of experimental 12%Cr martensitic steels strengthened by fine Z-phase nitrides based on Nb or Ta. Such steels may again enable the combination of high strength and oxidation resistance in the same alloy. This opens a new pathway for further alloy development of the heat resistant martensitic steels. (orig.)

Study on Creep Damage Model of 1Cr1Mo1/4V Steel for Turbine Rotor

International Nuclear Information System (INIS)

Choi, Woo Sung; Song, Gee Wook; Kim, Bum Shin; Chang, Sung Ho; Fleury, Eric

2011-01-01

It is well known that the dominant damage mechanisms in high-temperature steam turbine facilities such as rotor and casing are creep and fatigue damages. Even though coupling of creep and fatigue should be considered while predicting the life of turbine facilities, the remaining life of large steam turbine facilities is generally determined on the basis of creep damage because the turbines must generate stable base-load power and because they are operated at a high temperature and pressure for a long time. Almost every large steam turbine in Korea has been operated for more than 20 years and is made of steel containing various amounts of principal alloying elements nickel, chromium, molybdenum, and vanadium. In this study, creep damage model of 1Cr1Mo1/4V steel for turbine rotor is proposed and that can assess the high temperature creep life of large steam turbine facilities is proposed

X-ray spectrum microanalysis of copper and stainless steel surface layer after electroerosion machining

International Nuclear Information System (INIS)

Abdukarimov, Eh.T.; Saidinov, S.Ya.

1989-01-01

The results of experimental investigations of the surface layer of copper and steel 12Kh18N10T after electroerrosion treatment by a rotating tungsten electrode in natural and distilled water are presented. It is established that the quantity of electrode material transferred to the surface of the steel treated grows with the spark discharge energy increase. Tungsten concentration in the surface layer reaches 5-10% with the average depth of penetration 40-50 μm

Impact behavior of 9-Cr and 12-Cr ferritic steels after low-temperature irradiation

International Nuclear Information System (INIS)

Klueh, R.L.; Vitek, J.M.; Corwin, W.R.; Alexander, D.J.

1987-01-01

Miniature Charpy impact specimens of 9Cr-1MoVNb and 12Cr-1MoVW steels and these steels with 1 and 2% Ni were irradiated in the High-Flux Isotope Reactor (HFIR) at 50 0 C to displacement damage levels of up to 9 dpa. Nickel was added to study the effect of transmutation helium. Irradiation caused an increase in the ductile-brittle transition temperature (DBTT). The 9Cr-1MoVNb steels, with and without nickel, showed a larger shift than the 12Cr-1MoVW steels, with and without nickel. The results indicated that helium also increased the DBTT. The same steels were previously irradiated at higher temperatures. From the present and past tests, the effect of irradiation temperature on the DBTT behavior can be evaluated. For the 9Cr-1MoVNb steel, there is a continuous decrease in the magnitude of the DBTT increase up to an irradiation temperature of about 400 0 C, after which the shift drops rapidly to zero at about 450 0 C. The DBTT of the 12Cr-1MoVW steel shows a maximum increase at an irradiation temperature of about 400 0 C and less of an increase at either higher or lower irradiation temperatures

The creep-fatigue crack growth behaviour of a 1CrMoV rotor steel

International Nuclear Information System (INIS)

Priest, R.H.; Miller, D.A.; Gladwin, D.N.; Maguire, J.

1989-01-01

Crack growth rates under simultaneous creep-fatigue conditions have been quantified for a 1CrMoV rotor steel. Measured growth rates were partitioned into cyclic and hold period contributions and these characterized by the relevant fracture mechanics parameters K and C. Cyclic growth rates measured in the creep-fatigue tests were enhanced compared with pure fatigue rates. This observation is compared with the behaviour of other steels and explained by quantitative metallography. The resulting crack growth equation can be used during integrity assessments for plant components containing cracks which are subject to thermal fatigue

Effect of cerium addition on microstructure and mechanical properties of high-strength Fe85Cr4Mo8V2C1 cast steel

Energy Technology Data Exchange (ETDEWEB)

Hufenbach, J., E-mail: j.k.hufenbach@ifw-dresden.de [IFW Dresden, Institute for Complex Materials, P.O. Box 270116, D-01171 Dresden (Germany); Helth, A. [IFW Dresden, Institute for Complex Materials, P.O. Box 270116, D-01171 Dresden (Germany); Lee, M.-H. [Korea Institute of Industrial Technology, Gaetbeol-ro 156, Yeonsu-gu, Incheon 406-840 (Korea, Republic of); Wendrock, H.; Giebeler, L. [IFW Dresden, Institute for Complex Materials, P.O. Box 270116, D-01171 Dresden (Germany); Choe, C.-Y.; Kim, K.-H. [Korea Institute of Industrial Technology, Gaetbeol-ro 156, Yeonsu-gu, Incheon 406-840 (Korea, Republic of); Kühn, U. [IFW Dresden, Institute for Complex Materials, P.O. Box 270116, D-01171 Dresden (Germany); Kim, T.-S. [Korea Institute of Industrial Technology, Gaetbeol-ro 156, Yeonsu-gu, Incheon 406-840 (Korea, Republic of); Eckert, J. [IFW Dresden, Institute for Complex Materials, P.O. Box 270116, D-01171 Dresden (Germany); TU Dresden, Institute of Materials Science, D-01062 Dresden (Germany)

2016-09-30

This work presents an investigation on the influence of rare earth additions (Ce) on the microstructure and mechanical properties of a cast Fe85Cr4Mo8V2C1 (element contents in wt%) tool steel. The applied relatively high solidification rate during the casting process promotes the formation of non-equilibrium phases such as martensite, retained austenite as well as a fine network-like structure of complex carbides. This combination of phases and their morphology results in excellent mechanical properties already in the as-cast state. Cerium additions induce a change in phase formation and resulting mechanical properties. Besides morphological and quantitative changes of the main constituent phases, novel carbo-oxide and carbide phases are formed. To investigate this microstructural phenomenon, X-ray diffraction (XRD), transmission electron microscopy (TEM) and scanning electron microscopy (SEM) combined with energy dispersive X-ray spectroscopy (EDX) were applied. Altogether, the addition of small amounts of the rare earth element cerium together with a tailored casting process results in enhanced mechanical properties compared to the Fe85Cr4Mo8V2C1 alloy and offers new possibilities to obtain high-strength and simultaneously adequate ductile cast steels for advanced tool design.

Comparison of the corrosion resistance of DIN W. Nr. 1.4970 (15%Cr-15%Ni-1.2%Mo-Ti and ASTM F-138 (17%Cr-13%Ni-2.5%Mo austenitic stainless steels for biomedical applications

Directory of Open Access Journals (Sweden)

Maysa Terada

2006-09-01

Full Text Available The resistance to localised corrosion of the full austenitic 15%Cr-15%Ni-1.2%Mo titanium stabilized stainless steel (DIN W. Nr. 1.4970 was investigated by electrochemical methods including electrochemical impedance spectroscopy (EIS, potentiodynamic polarization and potentiostatic polarization measurements in a phosphate-buffered solution (PBS. The low carbon and non-stabilized austenitic stainless steel, AISI 316L (ASTM F-138, widely used for surgical implants, was also tested for comparison. The tests were conducted at room temperature after a stable potential had been reached. After the electrochemical measurements, the surfaces of the specimens were observed using SEM to evaluate the presence of pits. Potentiodynamic polarization results showed that both steels are prone to localized corrosion. Larger pits were found on the surface of AISI 316L specimens after the electrochemical tests. EIS response has indicated the duplex structure of the passive oxides. The results showed that the electrochemical behaviour of the DIN W. Nr. 1.4970 is better than of AISI 316L steel. Therefore, their application as an implant material may be considered.

[Assessment of the MF59-adjuvanted pandemic influenza A/H1N1 vaccine. Systematic review of literature].

Science.gov (United States)

Ruiz-Aragón, J; Grande Tejada, A M; Márquez-Peláez, S; Molina Linde, J M; Yang, R

2013-10-01

To assess the efficacy and safety of MF59-adjuvanted pandemic influenza A/H1N1 vaccine in children. A systematic review of the literature was performed after searching the MedLine and Embase electronic databases, and manual search in specialties journals, with MeSH terms and and free terms. Inclusion criteria were clinical trials with children vaccinated with MF59-adjuvanted influenza A/H1N1 vaccine, compared with other vaccines doses with/without MF59-adjuvanted. The immunogenicity and safety of the vaccine was recorded. The quality of the studies included was assessed by CASPe checklist. Four clinical trials with moderate quality were selected. The local and systemic adverse effects were rare and mild, with no differences between groups. Seroconversion and seroprotection levels were higher with MF59-adjuvanted vaccines. Antibody titres were also higher with the adjuvant vaccines. The adjuvant vaccine has a good efficacy and safety profile. The adverse effects that may occur are common and appear similarly in both vaccination groups. Copyright © 2012 Asociación Española de Pediatría. Published by Elsevier Espana. All rights reserved.

Study of the interactionπ+p at 1.2 GeV/c π+ laboratory momentum

International Nuclear Information System (INIS)

Ladron de Guevara, P.

1973-01-01

We present the main results of a 0.33 events/urban experiment of π + interactions in hydrogen at 1.2 GeV/c, using the 80 cm Saclay bubble chamber. the partial cross sections of the different reactions and the elastic differential cross section are computed by normalizing to the total cross section obtained by other groups. (Author) 34 refs

Synthesis and two-electron redox behavior of diazuleno[2,1-a:1,2-c]naphthalenes.

Science.gov (United States)

Ito, Shunji; Nomura, Akiko; Morita, Noboru; Kabuto, Chizuko; Kobayashi, Hirokazu; Maejima, Seiko; Fujimori, Kunihide; Yasunami, Masafumi

2002-10-18

The Diels-Alder reaction of di-2-azulenylacetylene with tetraphenylcyclopentadienone afforded 7,8,9,10-tetraphenyldiazuleno[2,1-a:1,2-c]naphthalene in one pot via autoxidation of the presumed 1,2-di-2-azulenylbenzene derivative. In contrast, a similar reaction of bis(1-methoxycarbonyl-2-azulenyl)acetylene with tetraphenylcyclopentadienone gave the 1,2-di-2-azulenylbenzene derivative. The following cyclodehydrogenation reaction of the benzene derivative with iron(III) chloride afforded diazuleno[2,1-a:1,2-c]naphthalene 6,11-bismethoxycarbonyl derivative. The redox behavior of these novel diazuleno[2,1-a:1,2-c]naphthalenes was examined by cyclic voltammetry (CV). These compounds exhibited two-step oxidation waves at +0.22 to +0.71 V upon CV, which revealed the formation of a radical cation and dication stabilized by the fused two azulene rings under the electrochemical oxidation conditions. Since the 1,2-di-2-azulenylbenzene derivative was oxidized at higher oxidation potentials (+0.83 and +1.86 V), the fusion of the two azulene rings to naphthalene increased electron-donating properties because of the formation of a closed-shell dicationic structure. Formation of the radical cation was characterized by UV-vis spectroscopy under the electrochemical oxidation conditions, although no evidence was obtained for the presumed dication under the conditions of the UV-vis spectroscopy measurement.

Using R in Taverna: RShell v1.2

Science.gov (United States)

Wassink, Ingo; Rauwerda, Han; Neerincx, Pieter BT; Vet, Paul E van der; Breit, Timo M; Leunissen, Jack AM; Nijholt, Anton

2009-01-01

Background R is the statistical language commonly used by many life scientists in (omics) data analysis. At the same time, these complex analyses benefit from a workflow approach, such as used by the open source workflow management system Taverna. However, Taverna had limited support for R, because it supported just a few data types and only a single output. Also, there was no support for graphical output and persistent sessions. Altogether this made using R in Taverna impractical. Findings We have developed an R plugin for Taverna: RShell, which provides R functionality within workflows designed in Taverna. In order to fully support the R language, our RShell plugin directly uses the R interpreter. The RShell plugin consists of a Taverna processor for R scripts and an RShell Session Manager that communicates with the R server. We made the RShell processor highly configurable allowing the user to define multiple inputs and outputs. Also, various data types are supported, such as strings, numeric data and images. To limit data transport between multiple RShell processors, the RShell plugin also supports persistent sessions. Here, we will describe the architecture of RShell and the new features that are introduced in version 1.2, i.e.: i) Support for R up to and including R version 2.9; ii) Support for persistent sessions to limit data transfer; iii) Support for vector graphics output through PDF; iv)Syntax highlighting of the R code; v) Improved usability through fewer port types. Our new RShell processor is backwards compatible with workflows that use older versions of the RShell processor. We demonstrate the value of the RShell processor by a use-case workflow that maps oligonucleotide probes designed with DNA sequence information from Vega onto the Ensembl genome assembly. Conclusion Our RShell plugin enables Taverna users to employ R scripts within their workflows in a highly configurable way. PMID:19607662

Role of PKC and CaV1.2 in detrusor overactivity in a model of obesity associated with insulin resistance in mice.

Directory of Open Access Journals (Sweden)

Luiz O Leiria

Full Text Available Obesity/metabolic syndrome are common risk factors for overactive bladder. This study aimed to investigate the functional and molecular changes of detrusor smooth muscle (DSM in high-fat insulin resistant obese mice, focusing on the role of protein kinase C (PKC and Ca(v1.2 in causing bladder dysfunction. Male C57BL/6 mice were fed with high-fat diet for 10 weeks. In vitro functional responses and cystometry, as well as PKC and Ca(v1.2 expression in bladder were evaluated. Obese mice exhibited higher body weight, epididymal fat mass, fasting glucose and insulin resistance. Carbachol (0.001-100 µM, α,β-methylene ATP (1-10 µM, KCl (1-300 mM, extracellular Ca(2+ (0.01-100 mM and phorbol-12,13-dibutyrate (PDBu; 0.001-3 µM all produced greater DSM contractions in obese mice, which were fully reversed by the Ca(v1.2 blocker amlodipine. Cystometry evidenced augmented frequency, non-void contractions and post-void pressure in obese mice that were also prevented by amlodipine. Metformin treatment improved the insulin sensitivity, and normalized the in vitro bladder hypercontractility and cystometric dysfunction in obese mice. The PKC inhibitor GF109203X (1 µM also reduced the carbachol induced contractions. PKC protein expression was markedly higher in bladder tissues from obese mice, which was normalized by metformin treatment. The Ca(v1.2 channel protein expression was not modified in any experimental group. Our findings show that Ca(v1.2 blockade and improvement of insulin sensitization restores the enhanced PKC protein expression in bladder tissues and normalizes the overactive detrusor. It is likely that insulin resistance importantly contributes for the pathophysiology of this urological disorder in obese mice.

Fatigue of materials and structures. v. 1,2

International Nuclear Information System (INIS)

1989-01-01

Published in two volumes, the conference proceedings contain 82 contributions, 9 of which have been inputted in INIS. These were concerned with the measurement and evaluation of fatigue characteristics during low-cycle load of materials such as steels for nuclear reactor pressure vessels and other components. (B.S.)

Modeling the influence of the parameters the diffusion of chromium plating on operational and physical and mechanical properties of steels for stamping tool

Directory of Open Access Journals (Sweden)

Олександр Петрович Чейлях

2015-03-01

Full Text Available The diffusion hardening steel can be produced in any plant having a thermal equipment, besides, it is more economical than obtaining an alloy steel with similar properties. The influence of the parameters of the diffusion of chromium plating (the composition of the steel, powder mixture on the structure and mechanical properties of structural and tool steels was investigated. Results of X-ray analysis showed that the diffusion zone in the samples consists of two layers. First layer is predominantly carbides Cr7C3, Cr23C6, Fe3C. An intermediate layer composed of carbon-free solid solution of chromium in the iron. The maximum total thickness of the diffusion zone is observed in the steel 130Cr12V1 and 130Cr12Mo1 (~80 µm, minimum – in carbon steels 45, U10 (~10-30 µm. The thickness of carbide layer is approximately the same – 1-3 µm. Analyzing of data micro-hardness measurement across the thickness of the diffusion zone it must be noted that the diffusion layers of the samples of the tool steels have a high micro-hardness 6000-10000. The maximum HV=10200 was in steel 30Cr2W8V1. Chromium saturation of steel surface significantly increases its wear resistance. A much greater effect of increase of coefficient of relative wear resistance (3 fold increase was observed in steels 30Cr2W8V1, 130Cr12V1 and 130Cr12Mo1. The mathematical models relating the micro-hardness, wear resistance, the thickness of the diffusion layer were obtained. In view of the analytical relationships ascertained that the wear resistance of hardened steels substantially depend on the thickness of the diffusion coating, the micro-hardness of the layer and the core of steel and alloy steels has increased more than two times. For hardening steel punching tool 30Cr2W8V1 can be recommended composition of the powder mixture: 50% FeCr + 48% Al2O3 + 2% NaF, and for steel 130Cr12V1 preferably used as activator NH4F

Non-destructive automated express method for determining the inclination of chromium-nickel steels IGC

International Nuclear Information System (INIS)

Nazarov, A.A.; Kamenev, Yu.B.; Kuusk, L.V.; Kormin, E.G.; Vasil'ev, A.N.; Sumbaeva, T.E.

1986-01-01

Methods of automated control of 18-10-type steel inclination to IGC are developed and a corresponding automated testing complex (ATS) is created. 08Kh18N10T steel samples had two variants of thermal treatment: 1) 1200 deg (5 h), 600 deg (50 h); 2) 1200 deg (5 h). Methods of non-destructive automated control of 18-10-type steel inclination to IGC are developed on the basis of potentiodynamic reactivation (PR) principle. Automated testing complex is developed, which has undergone experimental running and demonstrated a high confidence of results, reliability and easy operation

Manufacture of rings of 08Kh18N10T sheet for internal structures of WWER type reactors

International Nuclear Information System (INIS)