  1. Soft magnetic moldable composites: Properties and applications

    Energy Technology Data Exchange (ETDEWEB)

    Svensson, Leif, E-mail: leif.svensson@iprod.lth.se [Lund University, Division of Production and Materials Engineering, Box 188, 221 00 Lund (Sweden); Frogner, Kenneth, E-mail: kenneth.frogner@iprod.lth.se [Lund University, Division of Production and Materials Engineering, Box 188, 221 00 Lund (Sweden); Jeppsson, Peter, E-mail: peter.jeppsson@iprod.lth.se [Lund University, Division of Production and Materials Engineering, Box 188, 221 00 Lund (Sweden); Cedell, Tord, E-mail: tord.cedell@iprod.lth.se [Lund University, Division of Production and Materials Engineering, Box 188, 221 00 Lund (Sweden); Andersson, Mats, E-mail: mats.andersson@iprod.lth.se [Lund University, Division of Production and Materials Engineering, Box 188, 221 00 Lund (Sweden)

    2012-09-15

    A new type of electromagnetic soft magnetic material (SMM) is introduced, based on spherical iron powder particles and a suitable polymer binder. A key feature of this material is that it can be cast or molded into almost any 3D shape, hence the denotation soft magnetic moldable composite (SM{sup 2}C). The SM{sup 2}C is compared with a set of reference materials, such as ferrites, laminated steels, and soft magnetic composites, in terms of primary properties such as permeability and loss, and other properties, such as thermal conductivity and manufacturability. The SM{sup 2}C has the obvious disadvantage of relatively low permeability, but offers benefits such as relatively low losses and high potential for close integration into electromagnetic circuits. Some recent SM{sup 2}C applications are illustrated, and design and manufacturing aspects are discussed. - Highlights: Black-Right-Pointing-Pointer A new type of soft magnetic composite is introduced. Black-Right-Pointing-Pointer Properties are compared to other flux core materials. Black-Right-Pointing-Pointer The new material has low losses but also low permeability. Black-Right-Pointing-Pointer Potential benefits in freedom of design and manufacturing issues.

  2. Hysteretic behavior of soft magnetic elastomer composites

    Energy Technology Data Exchange (ETDEWEB)

    Krautz, Maria; Werner, David [Institute for Complex Materials, IFW Dresden, P.O. Box 270116, D-01171 Dresden (Germany); Schrödner, Mario [Thuringian Institute of Textile and Plastics Research e.V., Breitscheidstraße 97, D-07407 Rudolstadt (Germany); Funk, Alexander [Institute for Complex Materials, IFW Dresden, P.O. Box 270116, D-01171 Dresden (Germany); Jantz, Alexander; Popp, Jana [Thuringian Institute of Textile and Plastics Research e.V., Breitscheidstraße 97, D-07407 Rudolstadt (Germany); Eckert, Jürgen [Institute for Complex Materials, IFW Dresden, P.O. Box 270116, D-01171 Dresden (Germany); Erich Schmid Institute of Materials Science, Austrian Academy of Sciences, Jahnstraße 12, A-8700 Leoben (Austria); Department of Materials Physics, Montanuniversität Leoben, Jahnstraße 12, A-8700 Leoben (Austria); Waske, Anja [Institute for Complex Materials, IFW Dresden, P.O. Box 270116, D-01171 Dresden (Germany)

    2017-03-15

    Composites of polymer and micron-sized particles of carbonyl-iron were investigated in terms of their magnetization behavior. Thermoplastic elastomers with varying Young's modulus (E{sub Polymer}=0.14–14.6 MPa) were used as matrix material. Field dependent magnetization curves reveal that the hysteretic behavior of the composites strongly depends on both the particle fraction (7, 10, 14, 21, 31 vol%) and on the mechanical properties of the polymer. It is shown that hysteresis only appears above a certain fraction of magnetic particles which can be accounted to the magnetic exchange between the particles. However, hysteresis is suppressed in the composite with largest Young's modulus of the polymer matrix, even at largest particle fraction. - Highlights: • Composites with soft magnetic Iron Particles show hysteretic magnetization behavior. • Origin of the hysteresis is the alignment of particles along field direction. • Hysteresis depends on both, mechanical properties of matrix and particle fraction.

  3. Three-dimensional magnetic properties of soft magnetic composite materials

    International Nuclear Information System (INIS)

    Lin, Z.W.; Zhu, J.G.

    2007-01-01

    A three-dimensional (3-D) magnetic property measurement system, which can control the three components of the magnetic flux density B vector and measure the magnetic field strength H vector in a cubic sample of soft magnetic material, has been developed and calibrated. This paper studies the relationship between the B and H loci in 3-D space, and the power losses features of a soft magnetic composite when the B loci are controlled to be circles with increasing magnitudes and ellipses evolving from a straight line to circle in three orthogonal planes. It is found that the B and H loci lie in the same magnetization plane, but the H loci and power losses strongly depend on the orientation, position, and process of magnetization. On the other hand, the H vector evolves into a unique locus, and the power loss approaches a unique value, respectively, when the B vector evolves into the round locus with the same magnitude from either a series of circles or ellipses

  4. Magnetically Assisted Bilayer Composites for Soft Bending Actuators

    Directory of Open Access Journals (Sweden)

    Sung-Hwan Jang

    2017-06-01

    Full Text Available This article presents a soft pneumatic bending actuator using a magnetically assisted bilayer composite composed of silicone polymer and ferromagnetic particles. Bilayer composites were fabricated by mixing ferromagnetic particles to a prepolymer state of silicone in a mold and asymmetrically distributed them by applying a strong non-uniform magnetic field to one side of the mold during the curing process. The biased magnetic field induces sedimentation of the ferromagnetic particles toward one side of the structure. The nonhomogeneous distribution of the particles induces bending of the structure when inflated, as a result of asymmetric stiffness of the composite. The bilayer composites were then characterized with a scanning electron microscopy and thermogravimetric analysis. The bending performance and the axial expansion of the actuator were discussed for manipulation applications in soft robotics and bioengineering. The magnetically assisted manufacturing process for the soft bending actuator is a promising technique for various applications in soft robotics.

  5. Magnetically Assisted Bilayer Composites for Soft Bending Actuators.

    Science.gov (United States)

    Jang, Sung-Hwan; Na, Seon-Hong; Park, Yong-Lae

    2017-06-12

    This article presents a soft pneumatic bending actuator using a magnetically assisted bilayer composite composed of silicone polymer and ferromagnetic particles. Bilayer composites were fabricated by mixing ferromagnetic particles to a prepolymer state of silicone in a mold and asymmetrically distributed them by applying a strong non-uniform magnetic field to one side of the mold during the curing process. The biased magnetic field induces sedimentation of the ferromagnetic particles toward one side of the structure. The nonhomogeneous distribution of the particles induces bending of the structure when inflated, as a result of asymmetric stiffness of the composite. The bilayer composites were then characterized with a scanning electron microscopy and thermogravimetric analysis. The bending performance and the axial expansion of the actuator were discussed for manipulation applications in soft robotics and bioengineering. The magnetically assisted manufacturing process for the soft bending actuator is a promising technique for various applications in soft robotics.

  6. Magnetically Assisted Bilayer Composites for Soft Bending Actuators

    OpenAIRE

    Jang, Sung-Hwan; Na, Seon-Hong; Park, Yong-Lae

    2017-01-01

    This article presents a soft pneumatic bending actuator using a magnetically assisted bilayer composite composed of silicone polymer and ferromagnetic particles. Bilayer composites were fabricated by mixing ferromagnetic particles to a prepolymer state of silicone in a mold and asymmetrically distributed them by applying a strong non-uniform magnetic field to one side of the mold during the curing process. The biased magnetic field induces sedimentation of the ferromagnetic particles toward o...

  7. Magnetically assisted bilayer composites for soft bending actuators

    NARCIS (Netherlands)

    Jang, S.H.; Na, Seon Hong; Park, Yong Lae

    2017-01-01

    This article presents a soft pneumatic bending actuator using a magnetically assisted bilayer composite composed of silicone polymer and ferromagnetic particles. Bilayer composites were fabricated by mixing ferromagnetic particles to a prepolymer state of silicone in a mold and asymmetrically

  8. Magnetic and physical-mechanical properties of polymer composites with soft magnetic fillers

    International Nuclear Information System (INIS)

    Usakova, M.; Usak, E.; Olah, V.; Rekosova, J.

    2013-01-01

    In this paper the influence of soft magnetic ferrite fillers on magnetic and physical-mechanical properties of the prepared composite samples based in natural rubber matrix was studied. The soft magnetic ferrite materials with the chemical composition Mn_0_._3_7Zn_0_._5_7Fe_2_._0_6O_4 and Ni_0_._3_3Zn_0_._6_7Fe_2O_4 were used as magnetic filler in various concentrations. Further, the effect of thermo-oxidative ageing on the prepared composite materials was investigated. Magneto-rheological elastomers are solid analogues to magneto-rheological fluids. These materials are considered as smart materials comprising of micro- or submicro-sized magnetic particles dispersed in non-magnetic matrix. (authors)

  9. Determination of 3D magnetic reluctivity tensor of soft magnetic composite material

    International Nuclear Information System (INIS)

    Guo Youguang; Zhu Jianguo; Lin Zhiwei; Zhong Jinjiang; Lu Haiyan; Wang Shuhong

    2007-01-01

    Soft magnetic composite (SMC) materials are especially suitable for construction of electrical machines with complex structures and three-dimensional (3D) magnetic fluxes. In the design and optimization of such 3D flux machines, the 3D vector magnetic properties of magnetic materials should be properly determined, modeled, and applied for accurate calculation of the magnetic field distribution, parameters, and performance. This paper presents the measurement of 3D vector magnetic properties and determination of 3D reluctivity tensor of SMC. The reluctivity tensor is a key factor for accurate numerical analysis of magnetic field in a 3D flux SMC motor

  10. Magnetic measurement of soft magnetic composites material under 3D SVPWM excitation

    Science.gov (United States)

    Zhang, Changgeng; Jiang, Baolin; Li, Yongjian; Yang, Qingxin

    2018-05-01

    The magnetic properties measurement and analysis of soft magnetic material under the rotational space-vector pulse width modulation (SVPWM) excitation are key factors in design and optimization of the adjustable speed motor. In this paper, a three-dimensional (3D) magnetic properties testing system fit for SVPWM excitation is built, which includes symmetrical orthogonal excitation magnetic circuit and cubic field-metric sensor. Base on the testing system, the vector B and H loci of soft magnetic composite (SMC) material under SVPWM excitation are measured and analyzed by proposed 3D SVPWM control method. Alternating and rotating core losses under various complex excitation with different magnitude modulation ratio are calculated and compared.

  11. Steinmetz law in iron–phenolformaldehyde resin soft magnetic composites

    International Nuclear Information System (INIS)

    Kollár, Peter; Vojtek, Vladimír; Birčáková, Zuzana; Füzer, Ján; Fáberová, Mária; Bureš, Radovan

    2014-01-01

    The validity of Steinmetz law describing the dc energy losses as a function of maximum induction has been investigated for iron based soft magnetic composites (SMCs) up to 1.4 T with the effort to find a physical meaning of the coefficients in Steinmetz law. In the Rayleigh region the coefficients were expressed mathematically using the Rayleigh law. Further the “range of validity of Steinmetz law” was found to be from 0.3 T to 1.2 T. The typical “straight” shape of hysteresis loops of SMCs at lower maximum induction was approximated by linear functions in order to express the dc losses in form of Steinmetz law. - Highlights: • The exponent x in Steinmetz law in Rayleigh region for Fe-based SMC is equal to 3. • The validity of Steinmetz law is from 0.3 T to 1.2 T with exponent x=1.5. • The straight shape of hysteresis loop is approximated by linear functions. • This approximation provides the relation for dc losses in form of Steinmetz law

  12. Annealing effects on magnetic properties of silicone-coated iron-based soft magnetic composites

    Science.gov (United States)

    Wu, Shen; Sun, Aizhi; Zhai, Fuqiang; Wang, Jin; Zhang, Qian; Xu, Wenhuan; Logan, Philip; Volinsky, Alex A.

    2012-03-01

    This paper focuses on novel iron-based soft magnetic composites synthesis utilizing high thermal stability silicone resin to coat iron powder. The effect of an annealing treatment on the magnetic properties of synthesized magnets was investigated. The coated silicone insulating layer was characterized by scanning electron microscopy and energy dispersive X-ray spectroscopy. Silicone uniformly coated the powder surface, resulting in a reduction of the imaginary part of the permeability, thereby increasing the electrical resistivity and the operating frequency of the synthesized magnets. The annealing treatment increased the initial permeability, the maximum permeability, and the magnetic induction, and decreased the coercivity. Annealing at 580 °C increased the maximum permeability by 72.5%. The result of annealing at 580 °C shows that the ferromagnetic resonance frequency increased from 2 kHz for conventional epoxy resin coated samples to 80 kHz for the silicone resin insulated composites.

  13. Interplay of domain walls and magnetization rotation on dynamic magnetization process in iron/polymer–matrix soft magnetic composites

    Energy Technology Data Exchange (ETDEWEB)

    Dobák, Samuel, E-mail: samuel.dobak@student.upjs.sk [Institute of Physics, Faculty of Science, Pavol Jozef Šafárik University, Park Angelinum 9, 041 54 Košice (Slovakia); Füzer, Ján; Kollár, Peter [Institute of Physics, Faculty of Science, Pavol Jozef Šafárik University, Park Angelinum 9, 041 54 Košice (Slovakia); Fáberová, Mária; Bureš, Radovan [Institute of Materials Research, Slovak Academy of Sciences, Watsonova 47, 043 53 Košice (Slovakia)

    2017-03-15

    This study sheds light on the dynamic magnetization process in iron/resin soft magnetic composites from the viewpoint of quantitative decomposition of their complex permeability spectra into the viscous domain wall motion and magnetization rotation. We present a comprehensive view on this phenomenon over the broad family of samples with different average particles dimension and dielectric matrix content. The results reveal the pure relaxation nature of magnetization processes without observation of spin resonance. The smaller particles and higher amount of insulating resin result in the prevalence of rotations over domain wall movement. The findings are elucidated in terms of demagnetizing effects rising from the heterogeneity of composite materials. - Highlights: • A first decomposition of complex permeability into domain wall and rotation parts in soft magnetic composites. • A pure relaxation nature of dynamic magnetization processes. • A complete loss separation in soft magnetic composites. • The domain walls activity is considerably suppressed in composites with smaller iron particles and higher matrix content. • The demagnetizing field acts as a significant factor at the dynamic magnetization process.

  14. The effect of compaction parameters and dielectric composition on properties of soft magnetic composites

    Science.gov (United States)

    Xiao, Ling; Sun, Y. H.; Yu, Lie

    2011-07-01

    This paper investigated the effect of compaction parameters and dielectric composition on mechanical, magnetic and electrical properties of iron-organosilicon epoxy resin soft magnetic composites. In this work, iron powders with high purity were covered by an organic material (organosilicon epoxy resin) and then by coupling agent (KH-550). The coated powders were then cold compacted at 600, 800 and 1000 MPa and cured under vacuum respectively. The results show that the saturation magnetic flux density and electrical resistivity are dependent on compaction pressure and resin content. Increase in the organic phase content leads to decrease of the saturation magnetic flux density, while increase of the electrical resistivity. Furthermore, the samples with 0.9 wt% resins + 0.1 wt% coupling agent at compaction pressure of 800 MPa shows better properties than the others.

  15. The effect of compaction parameters and dielectric composition on properties of soft magnetic composites

    International Nuclear Information System (INIS)

    Xiao Ling; Yu Lie; Sun, Y H

    2011-01-01

    This paper investigated the effect of compaction parameters and dielectric composition on mechanical, magnetic and electrical properties of iron-organosilicon epoxy resin soft magnetic composites. In this work, iron powders with high purity were covered by an organic material (organosilicon epoxy resin) and then by coupling agent (KH-550). The coated powders were then cold compacted at 600, 800 and 1000 MPa and cured under vacuum respectively. The results show that the saturation magnetic flux density and electrical resistivity are dependent on compaction pressure and resin content. Increase in the organic phase content leads to decrease of the saturation magnetic flux density, while increase of the electrical resistivity. Furthermore, the samples with 0.9 wt% resins + 0.1 wt% coupling agent at compaction pressure of 800 MPa shows better properties than the others.

  16. Enhanced magnetic properties of Fe soft magnetic composites by surface oxidation

    Energy Technology Data Exchange (ETDEWEB)

    Zhao, Guoliang; Wu, Chen, E-mail: chen_wu@zju.edu.cn; Yan, Mi, E-mail: mse_yanmi@zju.edu.cn

    2016-02-01

    Fe soft magnetic composites (SMCs) with low core loss were fabricated via surface oxidation of the Fe powders by H{sub 2}O and O{sub 2} at elevated temperatures. Surface oxidation prevents magnetic dilution due to the formation of the ferromagnetic iron oxide coating layer, giving rise to high magnetic flux density and effective permeability of the SMCs compared with those fabricated with traditional phosphate coating. Mechanism of the oxidation process has been investigated where Fe{sub 3}O{sub 4} forms by reactions of Fe with H{sub 2}O and O{sub 2}. The Fe{sub 3}O{sub 4} coating layer tends to convert into γ-Fe{sub 2}O{sub 3} with increased oxidation temperature and time. By controlling composition of the coating layer, low core loss of 688.9 mW/cm{sup 3} (measured at 50 mT and 100 kHz) and higher effective permeability of 88.3 can be achieved for the Fe SMCs. - Highlights: • Surface oxidation as a new method to fabricate Fe Soft magnetic composite (SMCs). • Oxidation mechanism revealed where Fe reacts with H2O and O2 at high temperatures. • Evolution of the iron oxide coating with growth temperature and time investigated. • The iron oxide insulation coating results in improved magnetic performance.

  17. EXPERIMENTATION OF THREE PHASE OUTER ROTATING SWITCHED RELUCTANCE MOTOR WITH SOFT MAGNETIC COMPOSITE MATERIALS

    Directory of Open Access Journals (Sweden)

    N. C. LENIN

    2017-01-01

    Full Text Available This paper presents the application of Soft Magnetic Composite (SMC material in Outer Rotating Switched Reluctance Motor (ORSRM. The presented stator core of the Switched Reluctance Motor was made of two types of material, the classical laminated silicon steel sheet and the soft magnetic composite material. First, the stator core made of laminated steel has been analysed. The next step is to analyse the identical geometry SRM with the soft magnetic composite material, SOMALOY for its stator core. The comparisons of both cores include the calculated torque and torque ripple, magnetic conditions, simplicity of fabrication and cost. The finite element method has been used to analyse the magnetic conditions and the calculated torque. Finally, tested results shows that SMC is a better choice for SRM in terms of torque ripple and power density.

  18. Magnetic properties of soft layer/FePt-MgO exchange coupled composite Perpendicular recording media

    Institute of Scientific and Technical Information of China (English)

    Yin Jin-Hua; Takao Suzuki; Pan Li-Qing

    2008-01-01

    The magnetic properties of exchange coupled composite(ECC)media that are composed of perpendicular magnetic recording media FePt-MgO and two kinds of soft layers have been studied by using an x-ray diffractometer,a polar Kerr magneto-optical system(PMOKE)and a vibrating sample magnetometer(VSM).The results show that ECC media can reduce the coercivities of perpendicular magnetic recording media FePt-MgO.The ECC media with granular-type soft layers have weaker exchange couplings between magnetic grains and the magnetization process,for ECC media of this kind mainly follow the Stoner-Wohlfarth model.

  19. Composite nanoplatelets combining soft-magnetic iron oxide with hard-magnetic barium hexaferrite

    Science.gov (United States)

    Primc, D.; Makovec, D.

    2015-01-01

    By coupling two different magnetic materials inside a single composite nanoparticle, the shape of the magnetic hysteresis can be engineered to meet the requirements of specific applications. Sandwich-like composite nanoparticles composed of a hard-magnetic Ba-hexaferrite (BaFe12O19) platelet core in between two soft-magnetic spinel iron oxide maghemite (γ-Fe2O3) layers were synthesized using a new, simple and inexpensive method based on the co-precipitation of Fe3+/Fe2+ ions in an aqueous suspension of hexaferrite core nanoparticles. The required close control of the supersaturation of the precipitating species was enabled by the controlled release of the Fe3+ ions from the nitrate complex with urea ([Fe((H2N)2C&z.dbd;O)6](NO3)3) and by using Mg(OH)2 as a solid precipitating agent. The platelet Ba-hexaferrite nanoparticles of different sizes were used as the cores. The controlled coating resulted in an exclusively heterogeneous nucleation and the topotactic growth of the spinel layers on both basal surfaces of the larger hexaferrite nanoplatelets. The direct magnetic coupling between the core and the shell resulted in a strong increase of the energy product |BH|max. Ultrafine core nanoparticles reacted with the precipitating species and homogeneous product nanoparticles were formed, which differ in terms of the structure and composition compared to any other compound in the BaO-Fe2O3 system.By coupling two different magnetic materials inside a single composite nanoparticle, the shape of the magnetic hysteresis can be engineered to meet the requirements of specific applications. Sandwich-like composite nanoparticles composed of a hard-magnetic Ba-hexaferrite (BaFe12O19) platelet core in between two soft-magnetic spinel iron oxide maghemite (γ-Fe2O3) layers were synthesized using a new, simple and inexpensive method based on the co-precipitation of Fe3+/Fe2+ ions in an aqueous suspension of hexaferrite core nanoparticles. The required close control of the

  20. Development of Ferrite-Coated Soft Magnetic Composites: Correlation of Microstructure to Magnetic Properties

    Science.gov (United States)

    Sunday, Katie Jo

    Soft magnetic composites (SMCs) comprised of ferrite-coated ferrous powder permit isotropic magnetic flux capabilities, lower core losses, and complex designs through the use of traditional powder metallurgy techniques. Current coating materials and methods are vastly limited by the nonmagnetic properties of organic and some inorganic coatings and their inability to withstand high heat treatments for proper stress relief of core powder after compaction. Ferrite-based coatings are ferrimagnetic, highly resistive, and boast high melting temperatures, thus providing adequate electrical barriers between metallic particles. These insulating layers are necessary for reducing eddy current losses by increasing resistivity in order to improve the overall magnetic efficiency and subsequent frequency range. The goals of this work are to correlate ferrite-coated Fe powder composites microstructure for the coating and core powder to magnetic properties such as permeability, coercivity, and core loss. We first explore the relevant concepts of SMC materials from their composition to processing steps to pertinent properties. This thesis employs a suite of characterization techniques for powder and composite properties. We use X-ray diffraction, scanning electron microscopy, and transmission electron microscopy to provide a complete understanding of the effect of processing conditions on ferrite-coated Fe-based SMCs. Magnetic, mechanical, and electrical properties are then analyzed to correlate microstructural features and determine their effect on such properties. In the second part of this thesis, we present a proof of concept study on Al2O3- and Al2O3- Fe3O4-coated Fe powder composites, illustrating magnetization is highly dependent on ferromagnetic volume. We then expand on previous work to compare an ideal, crystalline state using Fe3O 4-Fe thin film heterostructures to a highly strained state using bulk powder studies. Fe3O4-coated Fe composites are produced via mechanical

  1. Annealing effects on magnetic properties of silicone-coated iron-based soft magnetic composites

    International Nuclear Information System (INIS)

    Wu Shen; Sun Aizhi; Zhai Fuqiang; Wang Jin; Zhang Qian; Xu Wenhuan; Logan, Philip; Volinsky, Alex A.

    2012-01-01

    This paper focuses on novel iron-based soft magnetic composites synthesis utilizing high thermal stability silicone resin to coat iron powder. The effect of an annealing treatment on the magnetic properties of synthesized magnets was investigated. The coated silicone insulating layer was characterized by scanning electron microscopy and energy dispersive X-ray spectroscopy. Silicone uniformly coated the powder surface, resulting in a reduction of the imaginary part of the permeability, thereby increasing the electrical resistivity and the operating frequency of the synthesized magnets. The annealing treatment increased the initial permeability, the maximum permeability, and the magnetic induction, and decreased the coercivity. Annealing at 580 °C increased the maximum permeability by 72.5%. The result of annealing at 580 °C shows that the ferromagnetic resonance frequency increased from 2 kHz for conventional epoxy resin coated samples to 80 kHz for the silicone resin insulated composites. - Highlights: ► Silicone uniformly coated the powder, increased the operating frequency of SMCs. ► The annealing treatment increased the DC properties of SMCs. ► Annealing at 580 °C increased the maximum permeability by 72.5%. ► Compared with epoxy coated, the SMCs had higher resistivity annealing at 580 °C.

  2. Analytical expression for initial magnetization curve of Fe-based soft magnetic composite material

    Energy Technology Data Exchange (ETDEWEB)

    Birčáková, Zuzana, E-mail: zuzana.bircakova@upjs.sk [Institute of Physics, Faculty of Science, Pavol Jozef Šafárik University, Park Angelinum 9, 04154 Košice (Slovakia); Kollár, Peter; Füzer, Ján [Institute of Physics, Faculty of Science, Pavol Jozef Šafárik University, Park Angelinum 9, 04154 Košice (Slovakia); Bureš, Radovan; Fáberová, Mária [Institute of Materials Research, Slovak Academy of Sciences, Watsonova 47, 04001 Košice (Slovakia)

    2017-02-01

    The analytical expression for the initial magnetization curve for Fe-phenolphormaldehyde resin composite material was derived based on the already proposed ideas of the magnetization vector deviation function and the domain wall annihilation function, characterizing the reversible magnetization processes through the extent of deviation of magnetization vectors from magnetic field direction and the irreversible processes through the effective numbers of movable domain walls, respectively. As for composite materials the specific dependences of these functions were observed, the ideas were extended meeting the composites special features, which are principally the much higher inner demagnetizing fields produced by magnetic poles on ferromagnetic particle surfaces. The proposed analytical expression enables us to find the relative extent of each type of magnetization processes when magnetizing a specimen along the initial curve. - Highlights: • Analytical expression of the initial curve derived for SMC. • Initial curve described by elementary magnetization processes. • Influence of inner demagnetizing fields on magnetization process in SMC.

  3. Advances in Powder Metallurgy Soft Magnetic Composite Materials

    Directory of Open Access Journals (Sweden)

    Bureš R.

    2017-06-01

    Full Text Available Powder metallurgy has grown with the expansion of various industry. Automotive industry had the most strong influence. Today, more than 90% of PM products are used in the transportation industry. Development of new materials such as magnetic materials is expected to meet the new trends of automotive industry, electric and hybrid vehicles.

  4. Giant magnetoimpedance in composite wires with insulator layer between non-magnetic core and soft magnetic shell

    International Nuclear Information System (INIS)

    Buznikov, N.A.; Antonov, A.S.; Granovsky, A.B.; Kim, C.G.; Kim, C.O.; Li, X.P.; Yoon, S.S.

    2006-01-01

    A method for calculation of the magnetoimpedance in composite wires having an insulator layer between non-magnetic core and soft magnetic shell is described. It is assumed that the magnetic shell has a helical anisotropy and the driving current flows through the core only. The distribution of eddy currents and expressions for the impedance are found by means of a solution of Maxwell equations taking into account the magnetization dynamics within the shell governed by the Landau-Lifshitz equation. The effect of the insulator layer on the magnetoimpedance is analyzed

  5. Giant magnetoimpedance in composite wires with insulator layer between non-magnetic core and soft magnetic shell

    Energy Technology Data Exchange (ETDEWEB)

    Buznikov, N.A. [Research Center for Advanced Magnetic Materials, Chungnam National University, Daejeon 305-764 (Korea, Republic of); Antonov, A.S. [Institute for Theoretical and Applied Electrodynamics, Russian Academy of Sciences, Moscow 125412 (Russian Federation); Granovsky, A.B. [Faculty of Physics, M.V. Lomonosov Moscow State University, Moscow 119992 (Russian Federation); Kim, C.G. [Research Center for Advanced Magnetic Materials, Chungnam National University, Daejeon 305-764 (Korea, Republic of)]. E-mail: cgkim@cnu.ac.kr; Kim, C.O. [Research Center for Advanced Magnetic Materials, Chungnam National University, Daejeon 305-764 (Korea, Republic of); Li, X.P. [Department of Mechanical Engineering and Division of Bioengineering, National University of Singapore, Singapore 119260 (Singapore); Yoon, S.S. [Department of Physics, Andong National University, Andong 760-749 (Korea, Republic of)

    2006-05-15

    A method for calculation of the magnetoimpedance in composite wires having an insulator layer between non-magnetic core and soft magnetic shell is described. It is assumed that the magnetic shell has a helical anisotropy and the driving current flows through the core only. The distribution of eddy currents and expressions for the impedance are found by means of a solution of Maxwell equations taking into account the magnetization dynamics within the shell governed by the Landau-Lifshitz equation. The effect of the insulator layer on the magnetoimpedance is analyzed.

  6. Preparation of Fe–Si–Ni soft magnetic composites with excellent high-frequency properties

    Energy Technology Data Exchange (ETDEWEB)

    Xu, Wei; Wu, Chen, E-mail: chen_wu@zju.edu.cn; Yan, Mi, E-mail: mse_yanmi@zju.edu.cn

    2015-05-01

    Fe–Si–Ni powders were firstly prepared into soft magnetic composites (SMCs) by ball milling, surface passivation and subsequent compaction. The morphology, phase composition, and magnetic properties of the Fe–Si–Ni powders and their high-frequency performance as SMCs were investigated. The Fe–Si–Ni powders, with saturation magnetization (M{sub s}) of 254.40 emu/g after annealing, were milled down to particle sizes ranging from 40 μm to 150 μm. Surface passivation of the powders was carried out with 0.2–1.0 wt% phosphoric acid solution prior to compaction. Evolution of the high-frequency properties for the Fe–Si–Ni SMCs with the passivator concentration and the molding pressure was studied. With optimized preparation parameters, high saturation flux density (B{sub s}) of 1.23 T, stable permeability, and superior dc-bias property with a percentage permeability above 70% while H=50 Oe were achieved for the Fe–Si–Ni SMC. Minimum core loss (285 mW/cm{sup 3}) was also measured at 50 kHz for B{sub m}=50 mT. - Highlights: • Fe–Si–Ni as a new type of magnetic powder has been prepared into soft magnetic composites. • Effective surface passivation of the Fe–Si–Ni powders can be achieved by phosphate treatment. • Influence of the passivator concentration and molding pressure has been investigated. • The obtained Fe–Si–Ni soft magnetic composites exhibit excellent high-frequency performance.

  7. A facile way to realize exchange coupling interaction in hard/soft magnetic composites

    Energy Technology Data Exchange (ETDEWEB)

    Li, Dongyun, E-mail: lidongyun@cjlu.edu.cn [College of Materials Science and Engineering, China Jiliang University, Hangzhou 310018 (China); Wang, Fan [College of Materials Science and Engineering, China Jiliang University, Hangzhou 310018 (China); Xia, Ailin, E-mail: alxia@126.com [Anhui Key Laboratory of Metal Materials and Processing, School of Materials Science and Engineering, Anhui University of Technology, Maanshan 243032 (China); Zhang, Lijiao [School of Science, Hebei University of Science and Technology, Shijiazhuang 050018 (China); Li, Tingting; Jin, Chuangui; Liu, Xianguo [Anhui Key Laboratory of Metal Materials and Processing, School of Materials Science and Engineering, Anhui University of Technology, Maanshan 243032 (China)

    2016-11-01

    SrFe{sub 12}O{sub 19}/CoFe{sub 2}O{sub 4} and SrFe{sub 12}O{sub 19}/Fe–B hard/soft magnetic composites were obtained by using powders synthesized via a hydrothermal and a molten salt method, respectively. The exchange coupling interaction was found to exist in the composites after a facile grinding according to the results of magnetic hysteresis loops and irreversible sloping recoil loops. It can be found that different grinding time affects their magnetic properties slightly. Our study proves that the conditions of realizing exchange coupling interaction may not be so stringent. - Highlights: • SrM/CFO and SrM/Fe–B with exchange coupling were obtained via a grinding way. • Different grinding time affects their magnetic properties slightly. • The conditions of realizing exchange coupling may not be so stringent.

  8. Magnetic properties and loss separation in FeSi/MnZnFe2O4 soft magnetic composites

    International Nuclear Information System (INIS)

    Lauda, M.; Füzer, J.; Kollár, P.; Strečková, M.; Bureš, R.; Kováč, J.; Baťková, M.; Baťko, I.

    2016-01-01

    We investigated composites that have been prepared from FeSi powders covered with MnZnFe 2 O 4 (MnZn ferrite), which was prepared by sol–gel synthesis accompanied with the auto-combustion process. The aim of this paper is to analyze the complex permeability and core losses of prepared samples with different amount of MnZn ferrite. The microstructure and the powder morphology were examined by scanning electron microscopy. Magnetic measurements on bulk samples were carried out using a vibrating sample magnetometer, an impedance analyzer and hysteresisgraphs. The results indicate that the composites with 2.6 wt% MnZn ferrite show better soft magnetic properties than the composites with about 6 wt% MnZn ferrite. - Highlights: • Successful preparation of soft magnetic composite FeSi/MnZnFe 2 O 4 . • Study of the complex magnetic permeability. • Comparison of different compositions of prepared SMC's. • Determination of parts of magnetic losses.

  9. Formation of soft magnetic high entropy amorphous alloys composites containing in situ solid solution phase

    Science.gov (United States)

    Wei, Ran; Sun, Huan; Chen, Chen; Tao, Juan; Li, Fushan

    2018-03-01

    Fe-Co-Ni-Si-B high entropy amorphous alloys composites (HEAACs), which containing high entropy solid solution phase in amorphous matrix, show good soft magnetic properties and bending ductility even in optimal annealed state, were successfully developed by melt spinning method. The crystallization phase of the HEAACs is solid solution phase with body centered cubic (BCC) structure instead of brittle intermetallic phase. In addition, the BCC phase can transformed into face centered cubic (FCC) phase with temperature rise. Accordingly, Fe-Co-Ni-Si-B high entropy alloys (HEAs) with FCC structure and a small amount of BCC phase was prepared by copper mold casting method. The HEAs exhibit high yield strength (about 1200 MPa) and good plastic strain (about 18%). Meanwhile, soft magnetic characteristics of the HEAs are largely reserved from HEAACs. This work provides a new strategy to overcome the annealing induced brittleness of amorphous alloys and design new advanced materials with excellent comprehensive properties.

  10. Structure and properties of nanocrystalline soft magnetic composite materials with silicon polymer matrix

    International Nuclear Information System (INIS)

    Dobrzanski, L.A.; Nowosielski, R.; Konieczny, J.; PrzybyI, A.; WysIocki, J.

    2005-01-01

    The paper concerns investigation of nanocrystalline composites technology preparation. The composites in the form of rings with rectangular transverse section, and with polymer matrix and nanocrystalline metallic powders fulfillment were made, for obtaining good ferromagnetic properties. The nanocrystalline ferromagnetic powders were manufactured by high-energy ball milling of metallic glasses strips in an as-quenched state. Generally for investigation, Co matrix alloys with the silicon polymer were used. Magnetic properties in the form of hysteresis loop by rings method were measured. Generally composite cores showed lower soft ferromagnetic properties than winded cores of nanocrystalline strips, but composite cores showed interesting mechanical properties. Furthermore, the structure of strips and powders on properties of composites were investigated

  11. Eddy current and total power loss separation in the iron-phosphate-polyepoxy soft magnetic composites

    International Nuclear Information System (INIS)

    Taghvaei, A.H.; Shokrollahi, H.; Janghorban, K.; Abiri, H.

    2009-01-01

    This work investigates the magnetic properties of iron-phosphate-polyepoxy soft magnetic composite materials. FTIR spectra, EDX analysis, distribution maps, X-ray diffraction pattern and density measurements show that the particles surface layer contains a thin layer of nanocrystalline/amorphous phosphate with high coverage of powders surface. In this paper, a formula for calculating the eddy current loss and total loss components by loss separation method is presented and finally the different parts of power losses are calculated. The results show that, the contribution of eddy current in the bulk material for single coating layer (k b = 0.18) is higher in comparison with double coating layer (k b = 0.09). Moreover, iron-phosphate-polyepoxy composites (P = 0.000004f 2 ) have lower power loss in comparison with iron-phosphate composites (P = 0.00002f 2 ).

  12. Visualization of Magnetic Flux Distribution at Soft Magnetic Composite(Special Issue to the Asia-Pacific Symposium on Applied Electromagnetics and Mechanics (APSAEM06))

    OpenAIRE

    Z. W., Lin; J. G., Zhu; Y. G., Guo; J. J., Zhong; W. Y., Yu; Centre for Electrical Machines and Power Electronics, Faculty of Engineering, University of Technology; Centre for Electrical Machines and Power Electronics, Faculty of Engineering, University of Technology; Centre for Electrical Machines and Power Electronics, Faculty of Engineering, University of Technology; Centre for Electrical Machines and Power Electronics, Faculty of Engineering, University of Technology; Baosteel Group Shanghai Iron and Steel Research Institute

    2007-01-01

    Soft magnetic composite (SMC), as one of soft magnetic materials, is being used increasingly in electromagnetic devices due to its magnetic isotropy, high electrical resistivity and easy formation. This paper presents the magnetic field distribution at the compressing surface of SMC by means of magneto-optical imaging technique. It is found that the flux density is non-uniform inside the sample, even within one particle region. Although there are interactions between neighbouring particles, t...

  13. AC magnetic properties of the soft magnetic composites based on Supermalloy nanocrystalline powder prepared by mechanical alloying

    Energy Technology Data Exchange (ETDEWEB)

    Neamtu, B.V., E-mail: bogdan.neamtu@stm.utcluj.ro [Materials Science and Engineering Department, Technical University of Cluj-Napoca, 400614 Cluj-Napoca (Romania); Institut Neel, CNRS/Universite J. Fourier, BP166, 38042 Grenoble, Cedex 9 (France); Geoffroy, O. [Institut Neel, CNRS/Universite J. Fourier, BP166, 38042 Grenoble, Cedex 9 (France); Grenoble Electrical Engineering, University J. Fourier, BP 46, F-38402 Saint-Martin d' Heres Cedex (France); Chicinas, I. [Materials Science and Engineering Department, Technical University of Cluj-Napoca, 400614 Cluj-Napoca (Romania); Isnard, O. [Institut Neel, CNRS/Universite J. Fourier, BP166, 38042 Grenoble, Cedex 9 (France)

    2012-05-25

    Highlights: Black-Right-Pointing-Pointer Nanocrystalline soft magnetic composites were obtained. Black-Right-Pointing-Pointer The cutting frequency of the produced nanocrystalline SMC exceeds 100 kHz. Black-Right-Pointing-Pointer A long annealing at low temperature leads to an improvement of the permeability (12%). - Abstract: The preparation and characterization of the nanocrystalline soft magnetic composite core based on Supermalloy powder obtained via mechanical alloying route are presented. The AC magnetic properties of the compacts were determined in frequency range from 100 Hz to 100 kHz for flux densities of 0.05 and 0.1 T. Composite materials were obtained by covering the Supermalloy particles with a polymer binder, then compacted into toroidal shape and finally polymerized. It is found that an increase of the compacting pressure from 600 MPa to 800 MPa leads to an increase of the compacts permeability by more than 8%. Also, reducing the polymer content from 2 wt.% to 0.5 wt.% leads to an increase of the magnetic losses (at 100 kHz and 0.1 T) by 380%. The removal of the stresses induced during compaction has been accomplished by a heat treatment at 170 Degree-Sign C for 120 h. This leads to a significant increase (12%) of the relative initial permeability of the compacts.

  14. Development of a low-cost double rotor axial flux motor with soft magnetic composite and ferrite permanent magnet materials

    Science.gov (United States)

    Liu, Chengcheng; Zhu, Jianguo; Wang, Youhua; Guo, Youguang; Lei, Gang; Liu, Xiaojing

    2015-05-01

    This paper proposes a low-cost double rotor axial flux motor (DRAFM) with low cost soft magnetic composite (SMC) core and ferrite permanent magnets (PMs). The topology and operating principle of DRAFM and design considerations for best use of magnetic materials are presented. A 905 W 4800 rpm DRAFM is designed for replacing the high cost NdFeB permanent magnet synchronous motor (PMSM) in a refrigerator compressor. By using the finite element method, the electromagnetic parameters and performance of the DRAFM operated under the field oriented control scheme are calculated. Through the analysis, it is shown that that the SMC and ferrite PM materials can be good candidates for low-cost electric motor applications.

  15. New Soft Magnetic Composites for electromagnetic applications with improved mechanical properties

    Science.gov (United States)

    Ferraris, Luca; Pošković, Emir; Franchini, Fausto

    2016-05-01

    The chance to move from 2D to 3D approach in the design of the electrical machines is made possible by the availability of Soft Magnetic Composites (SMC), iron based powders, insulated and pressed to realize shapes otherwise impossible with the traditional lamination sheets technology. Some commercial products are available on the market as "ready to press" powders, which presents good magnetic and energetic properties but are sometimes weak under the mechanical point of view; other products aim at improving this aspect but with considerable process complications and relative cost. The experience of the Authors in the realization of bonded magnets with the adoption of selected organic resins has been partly transferred in the research field of the SMC in order to investigate the possibility to obtain good mechanical properties maintaining the magnetic characteristics of the Insulated Iron Powder Compounds (I.I.P.C.) taken as reference. The paper presents the activity that has been carried out in the realization of SMC mixing iron powders and phenolic resin, in different weight percentages and mold pressures. The obtained results are considered satisfactory under the point of view of the compromise between magnetic and mechanical properties, considering also that the required productive process is simpler. The comparison of the obtained results with those related to commercial products encourages to carry on the research, also because of the reduced cost of the proposed SMC at parity (or better) performance.

  16. Study of AC Magnetic Properties and Core Losses of Fe/Fe3O4-epoxy Resin Soft Magnetic Composite

    Science.gov (United States)

    Laxminarayana, T. A.; Manna, Subhendu Kumar; Fernandes, B. G.; Venkataramani, N.

    Soft Magnetic Composites (SMC) were prepared by coating of nanocrystalline Fe3O4 particles, synthesized by co-precipitation method, on atomized iron powder of particle size less than 53 μm in size using epoxy resin as a binder between iron and Fe3O4. Fe3O4 was chosen, for its high electric resistivity and suitable magnetic properties, to keep the coating layer magnetic and seek improvement to the magnetic properties of SMC. SEM images and XRD patterns were recorded in order to investigate the coatings on the surface of iron powder. A toroid was prepared by cold compaction of coated iron powder at 1050 MPa and subsequently cured at 150˚C for 1 hr in argon atmosphere. For comparison of properties, a toroid of uncoated iron powder was also compacted at 1050 MPa and annealed at 600˚C for 2 hr in argon atmosphere. The coated iron powder composite has a resistivity of greater than 200 μΩm, measured by four probe method. A comparison of Magnetic Hysteresis loops and core losses using B-H Loop tracer in the frequency range 0 to 1500 Hz on the coated and uncoated iron powder is reported.

  17. Losses Approximation for Soft Magnetic Composites Based on a Homogenized Equivalent Conductivity

    Directory of Open Access Journals (Sweden)

    X. Ren

    2016-09-01

    Full Text Available Soft magnetic composites (SMC are a promising alternative to laminated steel in many Electrical Engineering applications. This is largely owing to their low level of eddy current losses. The electromagnetic behavior of SMC in electromagnetic devices cannot be easily predicted using standard numerical techniques such as the finite element method, mostly due to the computational cost required to model the material microstructure. Another difficulty lies in the high property contrast between the matrix and the inclusions. In this paper we propose a homogenization strategy to define the equivalent electromagnetic properties of SMC. For components made of SMC, the equivalent conductivity and permeability can be determined. These equivalent properties can be used to calculate eddy current losses or introduced into structural analysis tools to design electromagnetic devices.

  18. Magnetic and microstructural properties of Fe{sub 3}O{sub 4}-coated Fe powder soft magnetic composites

    Energy Technology Data Exchange (ETDEWEB)

    Jo Sunday, Katie [Department of Materials Science and Engineering, Drexel University, Philadelphia, PA19104 (United States); Hanejko, Francis G. [Hoeganaes Corporation, Cinnaminson, NJ08077 (United States); Taheri, Mitra L., E-mail: mtaheri@coe.drexel.edu [Department of Materials Science and Engineering, Drexel University, Philadelphia, PA19104 (United States)

    2017-02-01

    Soft magnetic composites (SMCs) comprised of ferrite-coated ferrous powder permit isotropic magnetic flux capabilities, lower core losses, and complex designs through the use of traditional powder metallurgy techniques. Current coating materials and methods are vastly limited by the nonmagnetic properties of organic and some inorganic coatings and their inability to withstand high heat treatments for proper stress relief of core powder after compaction. Ferrite-based coatings are ferrimagnetic, highly resistive, and possess high melting temperatures, thus providing adequate electrical barriers between metallic particles. In this work, iron powder was coated with Fe{sub 3}O{sub 4} particles via mechanical milling, then compacted and cured in an inert gas environment. We find density and coercivity to improve with increasing temperatures; however, core loss greatly increases, which is attributed to the formation of a more conductive iron-oxide phase and less resistive Fe volume. Our work begins to exemplify the unique qualities and potential for ferrite-based coatings using traditional powder metallurgy techniques and higher curing temperatures for electromagnetic devices. - Highlights: • Fe{sub 3}O{sub 4}-coated Fe powder was produced via mechanical milling, then compacted and cured into composite form. • SEM/EDS confirm Fe particles are individually isolated with iron-oxide coating material. • Larger particle sizes show improved core loss and coercivity measurements. • We report good magnetic properties for compaction at 800 MPa and a curing temperature of 700 °C.

  19. Magnetic properties measurement of soft magnetic composite material (SOMALOY 700) by using 3-D tester

    Science.gov (United States)

    Asari, Ashraf; Guo, Youguang; Zhu, Jianguo

    2017-08-01

    Core losses of rotating electrical machine can be predicted by identifying the magnetic properties of the magnetic material. The magnetic properties should be properly measured since there are some variations of vector flux density in the rotating machine. In this paper, the SOMALOY 700 material has been measured under x, y and z- axes flux density penetration by using the 3-D tester. The calibrated sensing coils are used in detecting the flux densities which have been generated by the Labview software. The measured sensing voltages are used in obtaining the magnetic properties of the sample such as magnetic flux density B, magnetic field strength H, hysteresis loop which can be used to calculate the total core loss of the sample. The results of the measurement are analyzed by using the Mathcad software before being compared to another material.

  20. Fabrication and Properties of Iron-based Soft Magnetic Composites Coated with NiZnFe2O4

    Directory of Open Access Journals (Sweden)

    WU Shen

    2017-07-01

    Full Text Available This paper focuses on iron-based soft magnetic composites which were synthesized by utilizing the sol-gel method prepared Ni-Zn ferrite particles as insulating compound to coat iron powder, and the influence of NiZnFe2O4 content and molding pressure on the magnetic properties was studied. The morphology, magnetic properties and density of Ni-Zn ferrite insulated compacts were investigated. Scanning electron microscope,line-scan EDX analysis and distribution maps show that the iron particle surface is covered with a thin layer of uniform Ni-Zn ferrites. The existing of the insulating layer can effectively improve the electrical resistivity of soft magnetic composites. Magnetic measurements show that the real part of permeability decreases with the increase of the Ni-Zn ferrite content, and the sample with 3%(mass fraction, the same below Ni-Zn ferrite has an acceptable real part and minimum imaginary part of permeability in comparison with other samples. Results show that the addition of NiZnFe2O4 can dramatically decrease the internal magnetic loss, the magnetic loss of coated samples decreases by 83.8% as compared with that of uncoated samples at 100kHz. The density of the Fe-3%NiZnFe2O4 compacts reaches 7.14g/cm3 and the saturation magnetization is 1.47T when the molding pressure is 1000MPa.

  1. Iron-borosilicate soft magnetic composites: The correlation between processing parameters and magnetic properties for high frequency applications

    Energy Technology Data Exchange (ETDEWEB)

    Gheiratmand, T., E-mail: t.gheiratmand@yahoo.com; Madaah Hosseini, H.R., E-mail: Madaah@sharif.edu; Seyed Reihani, S.M.

    2017-05-01

    Iron-borosilicate soft magnetic composites are suitable magnetic materials for high temperature and high frequency applications. In this research two different techniques have been applied to fabricate these composites: uniaxial pressing following by sintering and spark plasma sintering. Different processing parameters including the content of borosilicate, the amount of compaction pressure and the size of iron particles have been evaluated through the study of microstructure and magnetic properties. The microstructural observations showed that the borosilicate is distributed on the iron grain boundaries enhancing the resistivity and causing the loss of eddy currents. Increasing the compaction pressure was led to the decrease of electrical resistivity. By increasing the frequency both real and imaginary parts of permeability decreased. The use of higher content of borosilicate resulted in the lower decreasing slop of permeability. Best combination of density, permeability and electrical resistivity was obtained in the sample with 2 wt% of borosilicate. In addition, the densification of powders with fine particles was more difficult than coarse particles due to the inter particles friction and bridging effects. Furthermore, as the particles size increases the size of open porosities before sintering where the borosilicate could aggregate enhances. This could yields to the increase in the electrical resistivity. The high ratio of surface to the volume in the powders with fine particles results in the developing the demagnetizing fields and subsequently, decreasing the permeability. The highest relative density (99.99% of theoretical density) with best distribution of borosilicate was achieved in the composites produced by spark plasma sintering (SPS). The relaxation frequency, obtained from imaginary part of permeability, was found as 340 Hz in the composites made by SPS. - Highlights: • Iron-borosilicate SMC was produced for high temperature and frequency

  2. Effect of heat treatment in air on surface composition of iron-phosphate based soft magnetic composite components

    Energy Technology Data Exchange (ETDEWEB)

    Oikonomou, C., E-mail: christos.oikonomou@chalmers.se; Oro, R.; Hryha, E.; Nyborg, L.

    2014-11-15

    Highlights: • Surface morphological and chemical depth profiling analyses of SMC parts. • Effect of annealing at exterior/interior areas for different temperature regimes. • Difference in degree of oxidation/nature of bulk/coating with area and temperature. • Thermodynamic calculations/considerations on the thermal stability of the coating. • Incomplete delubrication and strong bulk oxidation of the samples under 500 °C. - Abstract: Soft magnetic composite materials (SMC) manufactured by conventional powder metallurgical techniques for electromagnetic applications constitute individually encapsulated ferromagnetic powder particles with an insulating surface layer, bonded together into 3D finished structures. The production procedure includes compaction of the SMC base powder mixed with a lubricant substance and a post-annealing treatment that aims to relieve the stresses induced in the component during pressing. In the present study, the effect of the heat treatment process to the nature of the insulating layer was investigated under different temperature regimes using analytical techniques. Its surface chemistry was determined based on the XPS depth profiling technique, and its morphology and structure were evaluated using HR-SEM and XRD. Differences between interior and exterior areas of the samples suggested the development of an oxide scale in the outer regions that prevents its further bulk oxidation at temperatures above 500 °C, while below that temperature incomplete de-lubrication takes place.

  3. Magnetic properties and loss separation in FeSi/MnZnFe{sub 2}O{sub 4} soft magnetic composites

    Energy Technology Data Exchange (ETDEWEB)

    Lauda, M. [Institute of Physics, Faculty of Science, Pavol Jozef Šafárik Univesity, Park Angelinum 9, 04154 Košice (Slovakia); Füzer, J., E-mail: jan.fuzer@upjs.sk [Institute of Physics, Faculty of Science, Pavol Jozef Šafárik Univesity, Park Angelinum 9, 04154 Košice (Slovakia); Kollár, P. [Institute of Physics, Faculty of Science, Pavol Jozef Šafárik Univesity, Park Angelinum 9, 04154 Košice (Slovakia); Strečková, M.; Bureš, R. [Institute of Materials Research, Slovak Academy of Sciences, Watsonova 47, 04001 Košice (Slovakia); Kováč, J.; Baťková, M.; Baťko, I. [Institute of Experimental Physics, Slovak Academy of Sciences, Watsonova 47, 04001 Košice (Slovakia)

    2016-08-01

    We investigated composites that have been prepared from FeSi powders covered with MnZnFe{sub 2}O{sub 4} (MnZn ferrite), which was prepared by sol–gel synthesis accompanied with the auto-combustion process. The aim of this paper is to analyze the complex permeability and core losses of prepared samples with different amount of MnZn ferrite. The microstructure and the powder morphology were examined by scanning electron microscopy. Magnetic measurements on bulk samples were carried out using a vibrating sample magnetometer, an impedance analyzer and hysteresisgraphs. The results indicate that the composites with 2.6 wt% MnZn ferrite show better soft magnetic properties than the composites with about 6 wt% MnZn ferrite. - Highlights: • Successful preparation of soft magnetic composite FeSi/MnZnFe{sub 2}O{sub 4}. • Study of the complex magnetic permeability. • Comparison of different compositions of prepared SMC's. • Determination of parts of magnetic losses.

  4. Fe-based soft magnetic composites coated with NiZn ferrite prepared by a co-precipitation method

    Energy Technology Data Exchange (ETDEWEB)

    Peng, Yuandong; Yi, Yi; Li, Liya; Ai, Hengyu; Wang, Xiaoxu [State Key Laboratory of Powder Metallurgy, Central South University, Changsha 410083 (China); Chen, Lulu [Jiangsu Eagle-globe Group Co., Ltd., Nantong 226600 (China)

    2017-04-15

    Fe powder was coated with NiZn ferrite by a co-precipitation method using chlorate as the raw material. Soft magnetic composites were manufactured via compaction and heat treatment of the coated powder. The coated powder and heat treated powder were analysed using scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS), X-ray diffraction (XRD) and Raman spectroscopy. Their magnetic properties were determined using a Quantum Design-Vibrating Sample Magnetometer (QD-VSM). The composites were analysed with SEM and EDS. The permeability and magnetic loss of the composites were measured with a B-H curve analyzer. The results show that, using the co-precipitation method, the raw precipitate was successfully prepared and coated the pure Fe powder and turned into spinel NiZn ferrite treated at 600 ℃ for 1 h. After heat treatment at 500 ℃ under air, the insulation coating layer of soft magnetic composite (SMC) was not destroyed and containing Fe, Ni, Zn and oxygen. The permeabilities of the SMC are stable at edge of the 2–200 kHz frequency range and the total loss was lower. - Graphical abstract: Scanning electron microscopy (SEM) images of Fe/(NiZn)Fe{sub 2}O{sub 4} composite powder heated at 600 ℃ for 1 h. - Highlights: • Fe particles were coated with (NiZn)Fe{sub 2}O{sub 4} via a co-precipitation and calcined method. • Coating layers were uniform and dense. • The permeabilities of the SMC are stable at edge of the 2–200 kHz frequency range.

  5. Influence of demagnetizing field on the permeability of soft magnetic composites

    International Nuclear Information System (INIS)

    Lin, G.Q.; Li, Z.W.; Chen, Linfeng; Wu, Y.P.; Ong, C.K.

    2006-01-01

    The influence of demagnetizing field on the effective permeability of magnetic composites has been investigated. A theoretical expression of the effective permeability has been obtained and discussed according to four typical composites with spheres, needles, flakes, and aligned prolate ellipsoidal particles. The results indicate that the demagnetizing field within the particles can reduce the effective permeability significantly. In order to increase the effective permeability, it is necessary to decrease the demagnetizing field within the particles. A linear relationship between effective permeability and volume fraction is also observed for composites filled with spherical particles at low volume fraction

  6. Iron-based soft magnetic composites with Mn-Zn ferrite nanoparticles coating obtained by sol-gel method

    Science.gov (United States)

    Wu, Shen; Sun, Aizhi; Xu, Wenhuan; Zhang, Qian; Zhai, Fuqiang; Logan, Philip; Volinsky, Alex A.

    2012-11-01

    This paper focuses on iron-based soft magnetic composites which were synthesized by utilizing Mn-Zn ferrite nanoparticles to coat iron powder. The nanocrystalline iron powders, with an average particle diameter of 20 nm, were obtained via the sol-gel method. Scanning electron microscopy, energy dispersive X-ray spectroscopy and distribution maps show that the iron particle surface is covered with a thin layer of Mn-Zn ferrites. Mn-Zn ferrite uniformly coated the surface of the powder particles, resulting in a reduced imaginary permeability, increased electrical resistivity and a higher operating frequency of the synthesized magnets. Mn-Zn ferrite coated samples have higher permeability and lower magnetic loss when compared with the non-magnetic epoxy resin coated compacts. The real part of permeability increases by 33.5% when compared with the epoxy resin coated samples at 10 kHz. The effects of heat treatment temperature on crystalline phase formation and on the magnetic properties of the Mn-Zn ferrite were investigated via X-ray diffraction and a vibrating sample magnetometer. Ferrites decomposed to FeO and MnO after annealing above 400 °C in nitrogen; thus it is the optimum annealing temperature to attain the desired permeability.

  7. A 2D finite element study on the role of material properties on eddy current losses in soft magnetic composites

    Science.gov (United States)

    Ren, Xiaotao; Corcolle, Romain; Daniel, Laurent

    2016-02-01

    The use of soft magnetic composites (SMCs) in electrical engineering applications is growing. SMCs provide an effective alternative to laminated steels because they exhibit a high permeability with low eddy current losses. Losses are a critical feature in the design of electrical machines, and it is necessary to evaluate the role of microstructure and constitutive properties of SMCs during the predesign stage. In this paper we propose a simplified finite element approach to compute eddy current losses in these materials. The computations allow to quantify the role of exciting source and material properties on eddy current losses. This analysis can later be used in the development of homogenization models for SMC. Contribution to the topical issue "Numelec 2015 - Elected submissions", edited by Adel Razek

  8. Fabrication and properties of iron-based soft magnetic composites coated with parylene via chemical vapor deposition polymerization

    International Nuclear Information System (INIS)

    Wu, Shen; Sun, Aizhi; Lu, Zhenwen; Cheng, Chuan

    2015-01-01

    This paper focuses on novel iron-based soft magnetic composites synthesis utilizing low friction factor parylene C films to coat iron powder via chemical vapor deposition polymerization. The morphology, magnetic properties, density, and chemical stability of parylene insulated iron particles were investigated. The coated parylene insulating layer was characterized by scanning electron microscopy and energy dispersive X-ray spectroscopy. The thickness of parylene C film is averagely 300 nm according to the results of transmission electron microscopy. Parylene C film uniformly coated the powder surface resulting in reducing the permeability imaginary part, increasing electrical resistivity and increasing the operating frequency of the synthesized magnets. It was shown that the parylene C coated compacts exhibited noticeably higher density compared to the epoxy resin coated compacts at the same pressure, suppress at 800 MPa increased the density by 17.02%. The result of Tafel curves indicated that the resistance of the iron particles to corrosion by NaCl solution is obviously improved after being insulated with parylene C film. - Highlights: • Parylene C uniformly coated the powder, increased the operating frequency of SMCs. • Compared with epoxy coated, the density of SMCs increased by 17.02% at 800 MPa. • The resistance of the iron particles is obviously improved with parylene film insulated

  9. Iron-based soft magnetic composites with Mn–Zn ferrite nanoparticles coating obtained by sol–gel method

    International Nuclear Information System (INIS)

    Wu, Shen; Sun, Aizhi; Xu, Wenhuan; Zhang, Qian; Zhai, Fuqiang; Logan, Philip; Volinsky, Alex A.

    2012-01-01

    This paper focuses on iron-based soft magnetic composites which were synthesized by utilizing Mn–Zn ferrite nanoparticles to coat iron powder. The nanocrystalline iron powders, with an average particle diameter of 20 nm, were obtained via the sol–gel method. Scanning electron microscopy, energy dispersive X-ray spectroscopy and distribution maps show that the iron particle surface is covered with a thin layer of Mn–Zn ferrites. Mn–Zn ferrite uniformly coated the surface of the powder particles, resulting in a reduced imaginary permeability, increased electrical resistivity and a higher operating frequency of the synthesized magnets. Mn–Zn ferrite coated samples have higher permeability and lower magnetic loss when compared with the non-magnetic epoxy resin coated compacts. The real part of permeability increases by 33.5% when compared with the epoxy resin coated samples at 10 kHz. The effects of heat treatment temperature on crystalline phase formation and on the magnetic properties of the Mn–Zn ferrite were investigated via X-ray diffraction and a vibrating sample magnetometer. Ferrites decomposed to FeO and MnO after annealing above 400 °C in nitrogen; thus it is the optimum annealing temperature to attain the desired permeability. - Highlights: ► Uniformly coated Mn–Zn ferrite powder increased the operating frequency of SMCs. ► Compared with epoxy coated, the permeability of SMCs increased by 33.5% at 10 kHz. ► 400 °C is the optimum annealing temperature to attain the desired permeability.

  10. High performance soft magnetic materials

    CERN Document Server

    2017-01-01

    This book provides comprehensive coverage of the current state-of-the-art in soft magnetic materials and related applications, with particular focus on amorphous and nanocrystalline magnetic wires and ribbons and sensor applications. Expert chapters cover preparation, processing, tuning of magnetic properties, modeling, and applications. Cost-effective soft magnetic materials are required in a range of industrial sectors, such as magnetic sensors and actuators, microelectronics, cell phones, security, automobiles, medicine, health monitoring, aerospace, informatics, and electrical engineering. This book presents both fundamentals and applications to enable academic and industry researchers to pursue further developments of these key materials. This highly interdisciplinary volume represents essential reading for researchers in materials science, magnetism, electrodynamics, and modeling who are interested in working with soft magnets. Covers magnetic microwires, sensor applications, amorphous and nanocrystalli...

  11. Structure and magnetic properties of iron-based soft magnetic composite with Ni-Cu-Zn ferrite-silicone insulation coating

    Science.gov (United States)

    Li, Wangchang; Wang, Wei; Lv, Junjun; Ying, Yao; Yu, Jing; Zheng, Jingwu; Qiao, Liang; Che, Shenglei

    2018-06-01

    This paper investigates the structure and magnetic properties of Ni-Cu-Zn ferrite-silicone coated iron-based soft magnetic composites (SMCs). Scanning electron microscopy coupled with a energy-dispersive spectroscopy (EDS) analysis revealed that the Ni-Cu-Zn ferrite and silicone resin were uniformly coated on the surface of iron powders. By controlling the composition of the coating layer, low total core loss of 97.7 mW/cm3 (eddy current loss of 48 mW/cm3, hysteresis loss of 49.7 mW/cm3, measured at 100 kHz and 0.02 T) and relatively high effective permeability of 72.5 (measured at 100 kHz) were achieved. In addition, the as-prepared SMCs displayed higher electrical resistivity, good magnetic characteristics over a wide range of frequencies (20-200 kHz) and ideal the D-C bias properties (more than 75% at H = 50 Oe). Furthermore, higher elastic modulus and hardness of SMCs, which means that the coating layer has good mechanical properties and is not easily damaged during the pressing process, were obtained in this paper. The results of this work indicate that the Ni-Cu-Zn ferrite-silicone coated SMCs have desirable properties which would make them suitable for application in the fields of the electric-magnetic switching devices, such as inductance coils, transformer cores, synchronous electric motors and resonant inductors.

  12. Magnetic properties of iron-based soft magnetic composites with SiO{sub 2} coating obtained by reverse microemulsion method

    Energy Technology Data Exchange (ETDEWEB)

    Wu, Shen [School of Material Science and Engineering, University of Science and Technology Beijing, Beijing 100083 (China); State Key Laboratory for Advanced Metals and Materials, University of Science and Technology Beijing, Beijing 100083 (China); Sun, Aizhi, E-mail: sunaizhi@126.com [School of Material Science and Engineering, University of Science and Technology Beijing, Beijing 100083 (China); State Key Laboratory for Advanced Metals and Materials, University of Science and Technology Beijing, Beijing 100083 (China); Lu, Zhenwen; Cheng, Chuan [School of Material Science and Engineering, University of Science and Technology Beijing, Beijing 100083 (China); Gao, Xuexu [State Key Laboratory for Advanced Metals and Materials, University of Science and Technology Beijing, Beijing 100083 (China)

    2015-05-01

    In this work, iron-based soft magnetic composites coated with the amorphous SiO{sub 2} layer have been fabricated by utilizing tetraethoxysilane in the reverse microemulsion method, and then the effects of addition amount of SiO{sub 2} and annealing temperature on the magnetic properties were investigated. The results show that the surface of iron powders contains a thin amorphous SiO{sub 2} insulation layer, which effectively decreases the magnetic loss of synthesized magnets. The magnetic loss of coated samples decreased by 87.8% as compared with that of uncoated samples at 150 kHz. Magnetic measurements show that the sample with 1.25 wt% SiO{sub 2} has an acceptable real part and minimum imaginary part of permeability in comparison with other samples. Also, the annealing treatment increased the initial permeability, the maximum permeability and the magnetic induction and decreased the coercivity with increasing temperature in the range 300–600 °C. The results of the loss separation imply that the annealed SMCs have a higher hysteresis loss coefficient (k{sub 2}) and lower eddy current loss coefficient (k{sub 3}) as compared with the pure iron compacts after the same heat treatment due to the preservation of the SiO{sub 2} layer. - Highlights: • SiO{sub 2} coated the iron powder by reverse microemulsion method, decreased the magnetic loss of SMCs. • 25 wt% is the optimum coating amount to attain the desired permeability. • The influence of annealing temperature on the magnetic performance of the core was discussed. • Compare with the pure iron compacts, the annealed SMCs have lower value of eddy current coefficient.

  13. Chemical synthesis of Fe/Fe{sub 3}O{sub 4} core-shell composites with enhanced soft magnetic performances

    Energy Technology Data Exchange (ETDEWEB)

    Yang, Bai, E-mail: byang@buaa.edu.cn [Key Laboratory of Aerospace Advanced Materials and Performance, Ministry of Education, School of Materials Science and Engineering, Beihang University, Beijing 100191 (China); Li, Xiaopan [Key Laboratory of Aerospace Advanced Materials and Performance, Ministry of Education, School of Materials Science and Engineering, Beihang University, Beijing 100191 (China); Yang, Xueying [Hi-tech Industry Standardization Institute, Hubei Standardization and Quality Institution, Wuhan 430061 (China); Yu, Ronghai [Key Laboratory of Aerospace Advanced Materials and Performance, Ministry of Education, School of Materials Science and Engineering, Beihang University, Beijing 100191 (China)

    2017-04-15

    The large-grain Fe/Fe{sub 3}O{sub 4} composite particles with average size of about 1.2 µm have been fabricated by a facile one-step solvothermal method. The formation of high-purity Fe{sub 3}O{sub 4} as the shells (90.14 wt%) and α-Fe as the cores (9.86 wt%) in the Fe/Fe{sub 3}O{sub 4} composites leads to their high saturation magnetization of 119.6 A m{sup 2} Kg{sup -1}. Very low coercivity of 30 Oe is obtained in the composites due to their uniform cubic-shaped morphologies. Compared with Fe-based nanosized particles, these micron-sized magnetic Fe/Fe{sub 3}O{sub 4} composites exhibit high air stability and good compactibility with high compressed density of 5.9 g cm{sup -3}. The fully compacted sample shows good soft magnetic properties including high magnetic induction B{sub 1.2k} {sub (H=1200} {sub A/m)} of 540 mT and good frequency-dependent magnetic properties with operating frequency up to 50 MHz superior to those of the most traditional soft magnetic ferrites, which promotes their potential applications in high-frequency and high-power magnetic devices. - Highlights: • Micron-sized Fe/Fe{sub 3}O{sub 4} composites are prepared by a one-step solvothermal method. • High saturation magnetization and low coercivity are obtained in the composites. • Good air stability and high bulk density occurs in the composites. • High magnetic induction and good frequency-dependent properties are achieved.

  14. Magnetism and metallurgy of soft magnetic materials

    CERN Document Server

    Chen, Chih-Wen

    2011-01-01

    Soft magnetic materials are economically and technologically the most important of all magnetic materials. In particular, the development of new materials and novel applications for the computer and telecommunications industries during the past few decades has immensely broadened the scope and altered the nature of soft magnetic materials. In addition to metallic substances, nonmetallic compounds and amorphous thin films are coming increasingly important. This thorough, well-organized volume - on of the most comprehensive treatments available - offers a coherent, logical presentation of the p

  15. Structure and distribution of cross-links in boron-modified phenol-formaldehyde resins designed for soft magnetic composites: a multiple-quantum 11B-11B MAS NMR correlation spectroscopy study

    Czech Academy of Sciences Publication Activity Database

    Kobera, Libor; Czernek, Jiří; Strečková, M.; Urbanová, Martina; Abbrent, Sabina; Brus, Jiří

    2015-01-01

    Roč. 48, č. 14 (2015), s. 4874-4881 ISSN 0024-9297 R&D Projects: GA MŠk(CZ) LD14010 Grant - others:European Commission(XE) COST Action MP1202 HINT Institutional support: RVO:61389013 Keywords : phenol-formaldehyde polymers * boron crosslinks * soft magnetic composites Subject RIV: CD - Macromolecular Chemistry Impact factor: 5.554, year: 2015

  16. Connection between microstructure and magnetic properties of soft magnetic materials

    International Nuclear Information System (INIS)

    Bertotti, G.

    2008-01-01

    The magnetic behavior of soft magnetic materials is discussed with some emphasis on the connection between macroscopic properties and underlying micromagnetic energy aspects. It is shown that important conceptual gaps still exist in the interpretation of macroscopic magnetic properties in terms of the micromagnetic formulation. Different aspects of hysteresis modeling, power loss prediction and magnetic non-destructive evaluation are discussed in this perspective

  17. Forces Between a Permanent Magnet and a Soft Magnetic Plate

    DEFF Research Database (Denmark)

    Beleggia, Marco; Vokoun, David; De Graef, Marc

    2012-01-01

    Forces between a hard/permanent magnet of arbitrary shape and an ideally soft magnetic plate in close proximity are derived analytically from the image method applied to magnetostatics. We found that the contact force, defined as the force required to detach the hard magnet from the plate, coinci...

  18. Development of High-frequency Soft Magnetic Materials for Power Electronics

    Directory of Open Access Journals (Sweden)

    LIU Jun-chang

    2017-05-01

    Full Text Available The new requirements of high-frequency magnetic properties are put forward for electronic components with the rapid development of power electronics industry and the use of new electromagnetic materials. The properties of magnetic core, which is the key unit of electronic components, determine the performance of electronic components directly. Therefore, it's necessary to study the high-frequency soft magnetic materials. In this paper, the development history of four types of soft magnetic materials was reviewed. The advantages and disadvantages of each kind of soft magnetic materials and future development trends were pointed out. The emphases were placed on the popular soft magnetic composite materials in recent years. The tendency is to develop high-frequency soft magnetic composite materials with the particle size controllable, uniform coating layer on the core and a mass production method from laboratory to industrialization.

  19. Tailoring superelasticity of soft magnetic materials

    Science.gov (United States)

    Cremer, Peet; Löwen, Hartmut; Menzel, Andreas M.

    2015-10-01

    Embedding magnetic colloidal particles in an elastic polymer matrix leads to smart soft materials that can reversibly be addressed from outside by external magnetic fields. We discover a pronounced nonlinear superelastic stress-strain behavior of such materials using numerical simulations. This behavior results from a combination of two stress-induced mechanisms: a detachment mechanism of embedded particle aggregates and a reorientation mechanism of magnetic moments. The superelastic regime can be reversibly tuned or even be switched on and off by external magnetic fields and thus be tailored during operation. Similarities to the superelastic behavior of shape-memory alloys suggest analogous applications, with the additional benefit of reversible switchability and a higher biocompatibility of soft materials.

  20. Forces between a permanent magnet and a soft magnetic plate

    Czech Academy of Sciences Publication Activity Database

    Beleggia, M.; Vokoun, David; DeGraef, M.

    2012-01-01

    Roč. 3, č. 5 (2012), 0500204/1-0500204/4 ISSN 1949-307X R&D Projects: GA ČR GPP108/12/P111 Institutional research plan: CEZ:AV0Z10100520 Keywords : electromagnetics * hard magnetic materials * soft magnetic materials Subject RIV: BM - Solid Matter Physics ; Magnetism http://ieeexplore.ieee.org/stamp/stamp.jsp?tp=&arnumber=6313974

  1. Bat head contains soft magnetic particles: evidence from magnetism.

    Science.gov (United States)

    Tian, Lanxiang; Lin, Wei; Zhang, Shuyi; Pan, Yongxin

    2010-10-01

    Recent behavioral observations have indicated that bats can sense the Earth's magnetic field. To unravel the magnetoreception mechanism, the present study has utilized magnetic measurements on three migratory species (Miniopterus fuliginosus, Chaerephon plicata, and Nyctalus plancyi) and three non-migratory species (Hipposideros armiger, Myotis ricketti, and Rhinolophus ferrumequinum). Room temperature isothermal remanent magnetization acquisition and alternating-field demagnetization showed that the bats' heads contain soft magnetic particles. Statistical analyses indicated that the saturation isothermal remanent magnetization of brains (SIRM(1T_brain)) of migratory species is higher than those of non-migratory species. Furthermore, the SIRM(1T_brain) of migratory bats is greater than their SIRM(1T_skull). Low-temperature magnetic measurements suggested that the magnetic particles are likely magnetite (Fe3O4). This new evidence supports the assumption that some bats use magnetite particles for sensing and orientation in the Earth's magnetic field.

  2. The mechanics of soft biological composites.

    Energy Technology Data Exchange (ETDEWEB)

    Nguyen, Thao D. (Sandia National Laboratories, Livermore, CA); Grazier, John Mark; Boyce, Brad Lee; Jones, Reese E. (Sandia National Laboratories, Livermore, CA)

    2007-10-01

    Biological tissues are uniquely structured materials with technologically appealing properties. Soft tissues such as skin, are constructed from a composite of strong fibrils and fluid-like matrix components. This was the first coordinated experimental/modeling project at Sandia or in the open literature to consider the mechanics of micromechanically-based anisotropy and viscoelasticity of soft biological tissues. We have exploited and applied Sandia's expertise in experimentation and mechanics modeling to better elucidate the behavior of collagen fibril-reinforced soft tissues. The purpose of this project was to provide a detailed understanding of the deformation of ocular tissues, specifically the highly structured skin-like tissue in the cornea. This discovery improved our knowledge of soft/complex materials testing and modeling. It also provided insight into the way that cornea tissue is bio-engineered such that under physiologically-relevant conditions it has a unique set of properties which enhance functionality. These results also provide insight into how non-physiologic loading conditions, such as corrective surgeries, may push the cornea outside of its natural design window, resulting in unexpected non-linear responses. Furthermore, this project created a clearer understanding of the mechanics of soft tissues that could lead to bio-inspired materials, such as highly supple and impact resistant body armor, and improve our design of human-machine interfaces, such as micro-electrical-mechanical (MEMS) based prosthetics.

  3. Anisotropic magnetism in field-structured composites

    International Nuclear Information System (INIS)

    Martin, James E.; Venturini, Eugene; Odinek, Judy; Anderson, Robert A.

    2000-01-01

    Magnetic field-structured composites (FSCs) are made by structuring magnetic particle suspensions in uniaxial or biaxial (e.g., rotating) magnetic fields, while polymerizing the suspending resin. A uniaxial field produces chainlike particle structures, and a biaxial field produces sheetlike particle structures. In either case, these anisotropic structures affect the measured magnetic hysteresis loops, with the magnetic remanence and susceptibility increased significantly along the axis of the structuring field, and decreased slightly orthogonal to the structuring field, relative to the unstructured particle composite. The coercivity is essentially unaffected by structuring. We present data for FSCs of magnetically soft particles, and demonstrate that the altered magnetism can be accounted for by considering the large local fields that occur in FSCs. FSCs of magnetically hard particles show unexpectedly large anisotropies in the remanence, and this is due to the local field effects in combination with the large crystalline anisotropy of this material. (c) 2000 The American Physical Society

  4. Soft magnetic tweezers: a proof of principle.

    Science.gov (United States)

    Mosconi, Francesco; Allemand, Jean François; Croquette, Vincent

    2011-03-01

    We present here the principle of soft magnetic tweezers which improve the traditional magnetic tweezers allowing the simultaneous application and measurement of an arbitrary torque to a deoxyribonucleic acid (DNA) molecule. They take advantage of a nonlinear coupling regime that appears when a fast rotating magnetic field is applied to a superparamagnetic bead immersed in a viscous fluid. In this work, we present the development of the technique and we compare it with other techniques capable of measuring the torque applied to the DNA molecule. In this proof of principle, we use standard electromagnets to achieve our experiments. Despite technical difficulties related to the present implementation of these electromagnets, the agreement of measurements with previous experiments is remarkable. Finally, we propose a simple way to modify the experimental design of electromagnets that should bring the performances of the device to a competitive level.

  5. MFM study of magnetic interaction between recording and soft magnetic layers

    International Nuclear Information System (INIS)

    Honda, Yukio; Tanahashi, Kiwamu; Hirayama, Yoshiyuki; Kikukawa, Atsushi; Futamoto, Masaaki

    2001-01-01

    Magnetic force microscopy was used to study the magnetic interaction between the recording and the soft magnetic layers in double-layer perpendicular media by observing the magnetization structure from the soft magnetic layer side. There was a strong magnetic interaction between the recording and the soft magnetic layers. Introducing a thin nonmagnetic intermediate layer between the two layers greatly reduced the magnetic interaction and drastically reduced the medium noise

  6. Magnetic characterization of soft and hard magnetic materials

    International Nuclear Information System (INIS)

    Groessinger, R.; Mehmood, N.; Sato Turtelli, R.; Keplinger, F.

    2008-01-01

    Full text: For industrial applications many materials are used which are magnetic such as various kind of steels, but also soft respectively hard magnetic materials are applied in order to solve a certain technical problem. For this purpose the magnetic properties of these materials have to be known or even optimized. In solid state physics the magnetic characterization is often performed at low temperatures, which means from 4.2 K up to room temperature. Contrary, for industrial application the range of environmental temperatures (-20 o C - 120 o C) where such systems are used is of interest. Additionally ranges the shape and size between few mm up to several cm. It is the purpose of this paper to summarize measuring systems which are mainly suited for an industrial characterizations. The most important hysteresis measurement methods which are applicable for industrial purpose are summarized. Special emphasis is laid on the difference between soft or hard magnetic materials. Practical examples for each method are given. Additionally a strain gauge method which is useful for magnetostriction measurement is shown. (author)

  7. Synthesis and magnetic properties of hard magnetic (CoFe{sub 2}O{sub 4})-soft magnetic (Fe{sub 3}O{sub 4}) nano-composite ceramics by SPS technology

    Energy Technology Data Exchange (ETDEWEB)

    Fei Chunlong [Key Laboratory of Artificial Micro- and Nano-structures of Ministry of Education and School of Physics and Technology, Hubei Key Laboratory on Organic and Polymeric Opto-electronic Materials, Wuhan University, Wuhan 430072 (China); Zhang Yue [Key Laboratory of Artificial Micro- and Nano-structures of Ministry of Education and School of Physics and Technology, Hubei Key Laboratory on Organic and Polymeric Opto-electronic Materials, Wuhan University, Wuhan 430072 (China); Key Laboratory for the Green Preparation and Application of Functional Materials of Ministry of Education, Hubei University, Wuhan 430062 (China); Yang Zhi; Liu Yong [Key Laboratory of Artificial Micro- and Nano-structures of Ministry of Education and School of Physics and Technology, Hubei Key Laboratory on Organic and Polymeric Opto-electronic Materials, Wuhan University, Wuhan 430072 (China); Xiong Rui, E-mail: wudawujiron@163.co [Key Laboratory of Artificial Micro- and Nano-structures of Ministry of Education and School of Physics and Technology, Hubei Key Laboratory on Organic and Polymeric Opto-electronic Materials, Wuhan University, Wuhan 430072 (China) and Key Laboratory for the Green Preparation and Application of Functional Materials of Ministry of Education, Hubei University, Wuhan 430062 (China); Shi Jing [Key Laboratory of Artificial Micro- and Nano-structures of Ministry of Education and School of Physics and Technology, Hubei Key Laboratory on Organic and Polymeric Opto-electronic Materials, Wuhan University, Wuhan 430072 (China); International Center for Materials Physics, Shen Yang 110015 (China); Ruan Xuefeng [Key Laboratory of Artificial Micro- and Nano-structures of Ministry of Education and School of Physics and Technology, Hubei Key Laboratory on Organic and Polymeric Opto-electronic Materials, Wuhan University, Wuhan 430072 (China)

    2011-07-15

    CoFe{sub 2}O{sub 4}/Fe{sub 3}O{sub 4} nano-composite ceramics were synthesized by Spark Plasma Sintering. The X-ray diffraction patterns show that all samples are composed of CoFe{sub 2}O{sub 4} and Fe{sub 3}O{sub 4} phases when the sintering temperature is below 900 {sup o}C. It is found that the magnetic properties strongly depend on the sintering temperature. The two-step hysteresis loops for samples sintered below 500 {sup o}C are observed, but when sintering temperature reaches 500 {sup o}C, the step disappears, which indicates that the CoFe{sub 2}O{sub 4} and Fe{sub 3}O{sub 4} are well exchange coupled. As the sintering temperature increases from 500 to 800 {sup o}C, the results of X-ray diffractometer indicate the constriction of crystalline regions due to the ion diffusion at the interfaces of CoFe{sub 2}O{sub 4}/Fe{sub 3}O{sub 4} phases, which have great impact on the magnetic properties. - Research highlights: In this work, a series of CoFe{sub 2}O{sub 4}/Fe{sub 3}O{sub 4} nano-composite ceramics were prepared through SPS. The magnetic properties of these ceramics have been studied in detail. It is found that the magnetic properties strongly depend on the sintering temperature.

  8. Composite magnetic particles

    International Nuclear Information System (INIS)

    Davies, G.E.; Janata, J.

    1981-01-01

    This patent claim on behalf of I.C.I. Ltd., relates to the preparation and use of composite magnetic particles, comprising a low density core, and having a magnetic coating over at least a proportion of the surface. The density of such particles can be chosen to suit a range of applications, e.g. in affinity chromatography, in radioimmunoassay, in the transport of the associated component, such as a drug or enzyme, to a specific site in a living organism. (U.K.)

  9. Incorporation of the Fe3O4 and SiO2 nanoparticles in epoxy-modified silicone resin as the coating for soft magnetic composites with enhanced performance

    Science.gov (United States)

    Luo, Dahao; Wu, Chen; Yan, Mi

    2018-04-01

    Three inorganic-organic hybrids have been designed by incorporating epoxy-modified silicone resin (ESR) with SiO2, Fe3O4 and their mixture in the application as the coating of Fe soft magnetic composites (SMCs). The introduced SiO2 nanoparticles are well dispersed in the ESR, while the Fe3O4 tends to agglomerate or even separate from the ESR. Simultaneous addition of the SiO2 and Fe3O4 gives rise to satisfactory distribution of both nanoparticles and optimized magnetic performance of the SMCs with high permeability (124.6) and low loss (807.8 mW/cm3). On one hand, introduction of the ferromagnetic Fe3O4 reduces the magnetic dilution effect, which is beneficial for improved magnetization and permeability. On the other hand, SiO2 incorporation prevents the agglomeration of the Fe3O4 nanoparticles and gives rise to increased electrical resistivity for reduced core loss as well as enhanced mechanical strength of the SMCs.

  10. Eddy current effect in soft magnetic backlayer for PMR media

    International Nuclear Information System (INIS)

    Tanaka, T.; Yamamoto, S.; Kurisu, H.; Matsuura, M.

    2005-01-01

    Flux density distributions in the recording layer and soft magnetic backlayer of a perpendicular magnetic recording medium were calculated up to 5 GHz using a three-dimensional finite element method electromagnetic field analysis simulator, where eddy current effects in the high-frequency recording process were considered. It is presented that the flux density distribution in a recording layer hardly depends on the eddy current effect, although flux density distribution in a soft magnetic backlayer changes depending on the recording frequency and resistivity of the soft magnetic backlayer

  11. Soft Magnetic Multilayered Thin Films for HF Applications

    Science.gov (United States)

    Loizos, George; Giannopoulos, George; Serletis, Christos; Maity, Tuhin; Roy, Saibal; Lupu, Nicoleta; Kijima, Hanae; Yamaguchi, Masahiro; Niarchos, Dimitris

    Multilayered thin films from various soft magnetic materials were successfully prepared by magnetron sputtering in Ar atmosphere. The magnetic properties and microstructure were investigated. It is found that the films show good soft magnetic properties: magnetic coercivity of 1-10 Oe and saturation magnetization higher than 1T. The initial permeability of the films is greater than 300 and flattens up to 600 MHz. The multilayer thin film properties in combination with their easy, fast and reproducible fabrication indicate that they are potential candidates for high frequency applications.

  12. Superconducting composite for magnetic bearings

    International Nuclear Information System (INIS)

    Rigney, T.K. II.

    1995-01-01

    A composite includes granules of Type II superconducting material and granules of rare-earth permanent magnets that are distributed in a binder. The composite is a two-phase structure that combines the properties of the superconductor and magnets with the flexibility and toughness of a polymeric material. A bearing made from this composite has the load capacity and stiffness of a permanent magnet bearing with added stability from a Type II superconducting material. 7 figs

  13. Photocatalytic/Magnetic Composite Particles

    Science.gov (United States)

    Wu, Chang-Yu; Goswami, Yogi; Garretson, Charles; Andino, Jean; Mazyck, David

    2007-01-01

    Photocatalytic/magnetic composite particles have been invented as improved means of exploiting established methods of photocatalysis for removal of chemical and biological pollutants from air and water. The photocatalytic components of the composite particles are formulated for high levels of photocatalytic activity, while the magnetic components make it possible to control the movements of the particles through the application of magnetic fields. The combination of photocatalytic and magnetic properties can be exploited in designing improved air- and water treatment reactors.

  14. Soft X-ray resonant scattering from magnetic heterostructures

    International Nuclear Information System (INIS)

    Grabis, J.

    2005-01-01

    Heterogenous magnetic multilayers are of great interest both because of their relevance for technological applications and since they provide model systems to understand magnetic behavior and interactions. Soft x-ray resonant magnetic scattering (XRMS) allows to determine element-specific and depth-resolving information of the local magnetic order of such systems. Within the framework of the present thesis the diffractometer ALICE for soft XRMS has been constructed. XRMS measurements of two different physical systems are presented in this thesis: The antiferromagnetic and ferromagnetic order in interlayer exchange-coupled Fe/Cr(001) superlattices are studied as a function of the applied field by measuring the reflected intensity at different positions in reciprocal space. Thin films and multilayers of the Heusler compound Co 2 MnGe are studied by means of soft x-ray absorption spectroscopy, magnetic circular dichroism and resonant magnetic scattering

  15. Development of soft magnetic materials with special properties

    International Nuclear Information System (INIS)

    Mager, A.

    1979-01-01

    New steps in the development of soft magnetic alloys are based on a better understanding of the magnetizing processes in close connection with the development of magnetic forms and components for different applications. New result on the influence of crystal grains, inclusions, and mechanical stresses on the soft magnetic properties of Ni-Fe-alloys with ca. 50 to 75% Nickel-contents are given. Special soft magnetic alloys were developed and improved for low temperature applications, for small temperature coefficients, for different shapes of hysteresis loops, or for high wear resistance - and moreover forms, components, and basic designs of chokes for RFI suppression, of transformers for electronic power supplies, of transformers for ground-fault interrupters, and for magnetic shielding equipments. (orig.) 891 GSC/orig. 892 AV [de

  16. Cluster-Assembled Soft Magnets for Power Electronics Applications

    National Research Council Canada - National Science Library

    Leslie-Pelecky, Diandra L

    2006-01-01

    This project used inert-gas condensation (IGC) to fabricate model nanostructured systems with the goal of better understanding the mechanisms responsible for decreasing the coercivity in soft magnetic materials...

  17. Synthesis, structural and magnetic characterization of soft magnetic nanocrystalline ternary FeNiCo particles

    Energy Technology Data Exchange (ETDEWEB)

    Toparli, Cigdem [Department of Metallurgical & Materials Eng., Istanbul Technical University, 34469 Istanbul (Turkey); Max-Planck-Institut für Eisenforschung GmbH, Düsseldorf (Germany); Ebin, Burçak [Department of Metallurgical & Materials Eng., Istanbul Technical University, 34469 Istanbul (Turkey); Nuclear Chemistry and Industrial Material Recycling, Department of Chemistry and Chemical Engineering, Chalmers University of Technology, S-412 96 Gothenburg (Sweden); Gürmen, Sebahattin, E-mail: gurmen@itu.edu.tr [Department of Metallurgical & Materials Eng., Istanbul Technical University, 34469 Istanbul (Turkey)

    2017-02-01

    The present study focuses on the synthesis, microstructural and magnetic properties of ternary FeNiCo nanoparticles. Nanocrystalline ternary FeNiCo particles were synthesized via hydrogen reduction assisted ultrasonic spray pyrolysis method in single step. The effect of precursor concentration on the morphology and the size of particles was investigated. The syntheses were performed at 800 °C. Structure, morphology and magnetic properties of the as-prepared products were characterized through X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM) and vibrating sample magnetometer (VSM) studies. Scherer calculation revealed that crystallite size of the ternary particles ranged between 36 and 60 nm. SEM and TEM investigations showed that the particle size was strongly influenced by the precursor concentration and Fe, Ni, Co elemental composition of individual particles was homogeneous. Finally, the soft magnetic properties of the particles were observed to be a function of their size. - Highlights: • Ternary FeNiCo alloy nanocrystalline particles were synthesized in a single step. • Cubic crystalline structure and spherical morphology was observed by XRD, SEM and TEM investigations. • The analysis of magnetic properties indicates the soft magnetic features of particles.

  18. Design-based modeling of magnetically actuated soft diaphragm materials

    Science.gov (United States)

    Jayaneththi, V. R.; Aw, K. C.; McDaid, A. J.

    2018-04-01

    Magnetic polymer composites (MPC) have shown promise for emerging biomedical applications such as lab-on-a-chip and implantable drug delivery. These soft material actuators are capable of fast response, large deformation and wireless actuation. Existing MPC modeling approaches are computationally expensive and unsuitable for rapid design prototyping and real-time control applications. This paper proposes a macro-scale 1-DOF model capable of predicting force and displacement of an MPC diaphragm actuator. Model validation confirmed both blocked force and displacement can be accurately predicted in a variety of working conditions i.e. different magnetic field strengths, static/dynamic fields, and gap distances. The contribution of this work includes a comprehensive experimental investigation of a macro-scale diaphragm actuator; the derivation and validation of a new phenomenological model to describe MPC actuation; and insights into the proposed model’s design-based functionality i.e. scalability and generalizability in terms of magnetic filler concentration and diaphragm diameter. Due to the lumped element modeling approach, the proposed model can also be adapted to alternative actuator configurations, and thus presents a useful tool for design, control and simulation of novel MPC applications.

  19. Nanomodified composite magnetic materials and their molding technologies

    Directory of Open Access Journals (Sweden)

    I. Timoshkov

    2018-05-01

    Full Text Available Advanced electro-magnetic machines and systems require new materials with improved properties. Heterogeneous 3D nanomodified soft magnetic materials could be efficiently applied. Multistage technology of iron particle surface nanomodification by sequential oxidation and Si-organic coatings will be reported. The thickness of layers is 0.5-5 nm. Compaction and annealing are the final steps of magnetic parts and components shaping. The soft magnetic composite material shows the features: resistivity is controlled by insulating coating thickness and equals up to ρ =10-4 Ω⋅m for metallic state and ρ =104 Ω⋅m for insulator state, maximum magnetic permeability is μm = 2500 and μm = 300 respectively, induction is up to Bm=2.1 T. These properties of composite soft magnetic material allow applying for transformers, throttles, stator-rotor of high-efficient and powerful electric machines in 10 kHz–1MGz frequency range. For microsystems and microcomponents application, good opportunity to improve their reliability is the use of nanocomposite materials. Electroplating technology of nanocomposite magnetic materials into the ultra-thick micromolds will be presented. Co-deposition of the soft magnetic alloys with inert hard nanoparticles allows obtaining materials with magnetic permeability up to μm=104, magnetic induction of Bs=(0.62–1.3 T. Such LIGA-like technology will be applied in MEMS to produce high reliable devices with advanced physical properties.

  20. Nanomodified composite magnetic materials and their molding technologies

    Science.gov (United States)

    Timoshkov, I.; Gao, Q.; Govor, G.; Sakova, A.; Timoshkov, V.; Vetcher, A.

    2018-05-01

    Advanced electro-magnetic machines and systems require new materials with improved properties. Heterogeneous 3D nanomodified soft magnetic materials could be efficiently applied. Multistage technology of iron particle surface nanomodification by sequential oxidation and Si-organic coatings will be reported. The thickness of layers is 0.5-5 nm. Compaction and annealing are the final steps of magnetic parts and components shaping. The soft magnetic composite material shows the features: resistivity is controlled by insulating coating thickness and equals up to ρ =10-4 Ωṡm for metallic state and ρ =104 Ωṡm for insulator state, maximum magnetic permeability is μm = 2500 and μm = 300 respectively, induction is up to Bm=2.1 T. These properties of composite soft magnetic material allow applying for transformers, throttles, stator-rotor of high-efficient and powerful electric machines in 10 kHz-1MGz frequency range. For microsystems and microcomponents application, good opportunity to improve their reliability is the use of nanocomposite materials. Electroplating technology of nanocomposite magnetic materials into the ultra-thick micromolds will be presented. Co-deposition of the soft magnetic alloys with inert hard nanoparticles allows obtaining materials with magnetic permeability up to μm=104, magnetic induction of Bs=(0.62-1.3) T. Such LIGA-like technology will be applied in MEMS to produce high reliable devices with advanced physical properties.

  1. Core–shell structured FeSiAl/SiO{sub 2} particles and Fe{sub 3}Si/Al{sub 2}O{sub 3} soft magnetic composite cores with tunable insulating layer thicknesses

    Energy Technology Data Exchange (ETDEWEB)

    Fan, Xi’an, E-mail: groupfxa@163.com [The State Key Laboratory of Refractories and Metallurgy, Wuhan University of Science and Technology, Wuhan, Hubei 430081 (China); Key Laboratory for Ferrous Metallurgy and Resources Utilization of Ministry of Education, Wuhan University of Science and Technology, Wuhan, Hubei 430081 (China); Wang, Jian, E-mail: snove418562@163.com [The State Key Laboratory of Refractories and Metallurgy, Wuhan University of Science and Technology, Wuhan, Hubei 430081 (China); Key Laboratory for Ferrous Metallurgy and Resources Utilization of Ministry of Education, Wuhan University of Science and Technology, Wuhan, Hubei 430081 (China); Wu, Zhaoyang, E-mail: wustwuzhaoyang@163.com [The State Key Laboratory of Refractories and Metallurgy, Wuhan University of Science and Technology, Wuhan, Hubei 430081 (China); Key Laboratory for Ferrous Metallurgy and Resources Utilization of Ministry of Education, Wuhan University of Science and Technology, Wuhan, Hubei 430081 (China); Li, Guangqiang, E-mail: ligq-wust@mail.wust.edu.cn [The State Key Laboratory of Refractories and Metallurgy, Wuhan University of Science and Technology, Wuhan, Hubei 430081 (China); Key Laboratory for Ferrous Metallurgy and Resources Utilization of Ministry of Education, Wuhan University of Science and Technology, Wuhan, Hubei 430081 (China)

    2015-11-15

    Graphical abstract: - Highlights: • FeSiAl/SiO{sub 2} core–shell particles and Fe{sub 3}Si/Al{sub 2}O{sub 3} composite cores were prepared. • SiO{sub 2} surrounding FeSiAl were replaced by Al{sub 2}O{sub 3} during sintering process. • Fe{sub 3}Si particles were separated by Al{sub 2}O{sub 3} with tunable thickness in composite cores. • Fe{sub 3}Si/Al{sub 2}O{sub 3} had lower core loss and better frequency stability than FeSiAl core. • The insulating layer between ferromagnetic particles can reduce core loss. - Abstract: FeSiAl/SiO{sub 2} core–shell particles and Fe{sub 3}Si/Al{sub 2}O{sub 3} composite cores with tunable insulating layer thicknesses have been synthesized via a modified Stöber method combined with following high temperature sintering process. Most of the conductive FeSiAl particles could be coated by insulating SiO{sub 2} using the modified Stöber method. During the sintering process, the reaction 4Al + 3SiO{sub 2} ≣ 2α-Al{sub 2}O{sub 3} + 3Si took place and the new Fe{sub 3}Si/Al{sub 2}O{sub 3} composite was formed. The Fe{sub 3}Si/Al{sub 2}O{sub 3} composite cores displayed more excellent soft magnetic properties, better frequency stability at high frequencies, much higher resistivity and lower core loss than the raw FeSiAl core. Based on this, several types of FeSiAl/SiO{sub 2} particles and Fe{sub 3}Si/Al{sub 2}O{sub 3} composite cores with tunable insulating layer thicknesses were selectively prepared by simply varying TEOS contents. The thickness of Al{sub 2}O{sub 3} insulating layer and resistivity of Fe{sub 3}Si/Al{sub 2}O{sub 3} composite cores increased with increasing the TEOS contents, while the permeability and core loss changed in the opposite direction.

  2. Soft magnetic properties of FeRuGaSi alloy films: SOFMAX

    International Nuclear Information System (INIS)

    Hayashi, K.; Hayakawa, M.; Ishikawa, W.; Ochiai, Y.; Iwasaki, Y.; Aso, K.

    1988-01-01

    To advance new soft magnetic materials of an FeGaSi alloy into the commercial world, improvements on various properties were designed by introducing additive elements without sacrificing its high saturation magnetic induction. The detailed studies on the diversified properties, such as saturation magnetic induction, film internal stress, wear resistivity, and so on, were performed. High-frequency permeability of the laminated structure film was also investigated. As a result, the Ru-added FeRuGaSi alloy films, whose typical compositions are Fe 72 Ru 4 Ga 7 Si 17 and Fe 68 Ru 8 Ga 7 Si 17 (at. %), prove to be excellent soft magnetic materials especially appropriate for the magnetic recording/playback head core use

  3. Synthesis, microstructure and magnetic properties of Fe{sub 3}Si{sub 0.7}Al{sub 0.3}@SiO{sub 2} core–shell particles and Fe{sub 3}Si/Al{sub 2}O{sub 3} soft magnetic composite core

    Energy Technology Data Exchange (ETDEWEB)

    Wang, Jian, E-mail: snove418562@163.com [The State Key Laboratory of Refractories and Metallurgy, Wuhan University of Science and Technology, Wuhan, Hubei 430081 (China); Key Laboratory for Ferrous Metallurgy and Resources Utilization of Ministry of Education, Wuhan University of Science and Technology, Wuhan, Hubei 430081 (China); Fan, Xi’an, E-mail: groupfxa@163.com [The State Key Laboratory of Refractories and Metallurgy, Wuhan University of Science and Technology, Wuhan, Hubei 430081 (China); Key Laboratory for Ferrous Metallurgy and Resources Utilization of Ministry of Education, Wuhan University of Science and Technology, Wuhan, Hubei 430081 (China); Wu, Zhaoyang, E-mail: wustwuzhaoyang@163.com [The State Key Laboratory of Refractories and Metallurgy, Wuhan University of Science and Technology, Wuhan, Hubei 430081 (China); Key Laboratory for Ferrous Metallurgy and Resources Utilization of Ministry of Education, Wuhan University of Science and Technology, Wuhan, Hubei 430081 (China); Li, Guangqiang [The State Key Laboratory of Refractories and Metallurgy, Wuhan University of Science and Technology, Wuhan, Hubei 430081 (China); Key Laboratory for Ferrous Metallurgy and Resources Utilization of Ministry of Education, Wuhan University of Science and Technology, Wuhan, Hubei 430081 (China)

    2015-11-15

    Fe{sub 3}Si{sub 0.7}Al{sub 0.3}@SiO{sub 2} core–shell particles and Fe{sub 3}Si/Al{sub 2}O{sub 3} soft magnetic composite core have been synthesized via a modified stöber method combined with following high temperature sintering process. Most of conductive Fe{sub 3}Si{sub 0.7}Al{sub 0.3} particles could be uniformly coated by insulating SiO{sub 2} using the modified stöber method. The Fe{sub 3}Si{sub 0.7}Al{sub 0.3}@SiO{sub 2} core–shell particles exhibited good soft magnetic properties with low coercivity and high saturation magnetization. The reaction 4Al+3SiO{sub 2}=2α-Al{sub 2}O{sub 3}+3Si took place during the sintering process. As a result the new Fe{sub 3}Si/Al{sub 2}O{sub 3} composite was formed. The Fe{sub 3}Si/Al{sub 2}O{sub 3} composite core displayed more excellent soft magnetic properties, better frequency stability at high frequencies, much higher electrical resistivity and lower core loss than the pure Fe{sub 3}Si{sub 0.7}Al{sub 0.3} core. The method of introducing insulating layers surrounding magnetic particles provides a promising route to develop new and high compact soft magnetic materials with good magnetic and electric properties. - Graphical abstract: In Fe{sub 3}Si/Al{sub 2}O{sub 3} composite, Fe{sub 3}Si phases are separated by Al{sub 2}O{sub 3} layers and the eddy currents are confined in Fe{sub 3}Si phases, thus increasing resistivity and reducing core loss. - Highlights: • Fe{sub 3}Si{sub 0.7}Al{sub 0.3}@SiO{sub 2} core–shell particles and Fe{sub 3}Si/Al{sub 2}O{sub 3} cores were prepared. • Fe{sub 3}Si{sub 0.7}Al{sub 0.3} particles could be uniformly coated by nano-sized SiO{sub 2} clusters. • Fe{sub 3}Si{sub 0.7}Al{sub 0.3}@SiO{sub 2} particles and Fe{sub 3}Si/Al{sub 2}O{sub 3} cores showed good soft magnetic properties. • Fe{sub 3}Si/Al{sub 2}O{sub 3} had lower core loss and better frequency stability than Fe{sub 3}Si{sub 0.7}Al{sub 0.3} cores.

  4. The recording characteristics of particulate double layers with hard-magnetic and soft-magnetic underlayers

    NARCIS (Netherlands)

    Lalbahadoersing, S.; Groenland, J.P.J.; Luitjens, S.B.; Lodder, J.C.

    2002-01-01

    Particulate double-layer tape samples with magnetic underlayers have been investigated by performing magnetic recording measurements and by computer simulation.The presence of soft-magnetic underlayers resulted in decreased signal output and better overwrite behavior. Hard-magnetic underlayers

  5. Magnetic losses in composite materials

    International Nuclear Information System (INIS)

    Ramprecht, J; Sjoeberg, D

    2008-01-01

    We discuss some of the problems involved in homogenization of a composite material built from ferromagnetic inclusions in a nonmagnetic background material. The small signal permeability for a ferromagnetic spherical particle is combined with a homogenization formula to give an effective permeability for the composite material. The composite material inherits the gyrotropic structure and resonant behaviour of the single particle. The resonance frequency of the composite material is found to be independent of the volume fraction, unlike dielectric composite materials. The magnetic losses are described by a magnetic conductivity which can be made independent of frequency and proportional to the volume fraction by choosing a certain bias. Finally, some concerns regarding particles of small size, i.e. nanoparticles, are treated and the possibility of exciting exchange modes are discussed. These exchange modes may be an interesting way to increase losses in composite materials

  6. Synthesis of FeSiBPNbCu nanocrystalline soft-magnetic alloys with high saturation magnetization

    Energy Technology Data Exchange (ETDEWEB)

    Li, Zongzhen [China Iron and Steel Research Institute Group, Advanced Technology and Materials Co., Ltd., Beijing 100081 (China); Wang, Anding; Chang, Chuntao [Key Laboratory of Magnetic Materials and Devices, Ningbo Institute of Materials Technology and Engineering, Chinese Academy of Sciences, 519 Zhuangshi Road, Zhenhai District, Ningbo, Zhejiang 315201 (China); Wang, Yanguo [Institute of Physics, Chinese Academy of Sciences, PO Box 603, Beijing 100080 (China); Dong, Bangshao [China Iron and Steel Research Institute Group, Advanced Technology and Materials Co., Ltd., Beijing 100081 (China); Zhou, Shaoxiong, E-mail: sxzhou@atmcn.com [China Iron and Steel Research Institute Group, Advanced Technology and Materials Co., Ltd., Beijing 100081 (China)

    2014-10-25

    Highlights: • Thermal stability of the FeSiBPNbCu alloys is strongly dependent on the Fe content. • The FeSiBPNbCu alloys with high Fe content exhibit good soft magnetic properties. • The coexistence of Cu, P and Nb leads to the excellent soft magnetic properties. - Abstract: A series of [Fe{sub 0.76+x}(Si{sub 0.4}B{sub 0.4}P{sub 0.2}){sub 0.24−x}]{sub 98.25}Nb{sub 1}Cu{sub 0.75} (x = 0–0.08) nanocrystalline soft-magnetic alloys with high saturation magnetization were synthesized by adjusting Fe content and improving the crystallization behavior, soft-magnetic properties and microstructure. It is found that the temperature interval between the two crystallization peaks is significantly enlarged from 50 to 180 °C when the Fe content of the alloys increases from x = 0 to x = 0.08, which greatly expands the optimum annealing temperature range. The alloys with higher Fe content are prone to form more uniform nanocomposite microstructure with better thermal stability and soft magnetic properties. The Fe-rich FeSiBPNbCu nanocrystalline alloys with x = 0.08 exhibit excellent soft-magnetic properties, including the high saturation magnetic flux density of up to 1.74 T, low coercivity of about 3.3 A/m and high effective permeability of more than 2.2 × 10{sup 4} at 1 kHz under a field of 1 A/m. The combination of excellent soft-magnetic properties, low cost and good productivity makes the FeSiBPNbCu alloys to be a kind of promising soft-magnetic materials for electrical and electronic industry applications.

  7. Frequency and Magnetic Field Dependence of the Skin Depth in Co-rich Soft Magnetic Microwires

    Directory of Open Access Journals (Sweden)

    A. Zhukov

    2016-11-01

    Full Text Available We studied giant magnetoimpedance (GMI effect in magnetically soft amorphous Co-rich microwires in the extended frequency range. From obtained experimentally dependences of GMI ratio on magnetic field and different frequencies we estimated the penetration depth and its dependence on applied magnetic field and frequency

  8. Developing bulk exchange spring magnets

    Science.gov (United States)

    Mccall, Scott K.; Kuntz, Joshua D.

    2017-06-27

    A method of making a bulk exchange spring magnet by providing a magnetically soft material, providing a hard magnetic material, and producing a composite of said magnetically soft material and said hard magnetic material to make the bulk exchange spring magnet. The step of producing a composite of magnetically soft material and hard magnetic material is accomplished by electrophoretic deposition of the magnetically soft material and the hard magnetic material to make the bulk exchange spring magnet.

  9. Microfluidic magnetic separator using an array of soft magnetic elements

    DEFF Research Database (Denmark)

    Smistrup, Kristian; Lund-Olesen, Torsten; Hansen, Mikkel Fougt

    2006-01-01

    We present the design, fabrication, characterization, and demonstration of a new passive magnetic bead separator. The device operates in an effective state when magnetized by an external magnetic field of only 50 mT, which is available from a tabletop electromagnet. We demonstrate the complete...... capture of 1.0 mu m fluorescent magnetic beads from a 7.5 mu L sample volume traveling at an average linear fluid velocity of 5 mm/s....

  10. Analysis of soft magnetic materials by electron backscatter diffraction as a powerful tool

    Directory of Open Access Journals (Sweden)

    David Schuller

    2018-04-01

    Full Text Available The current work demonstrates that electron backscatter diffraction (EBSD is a powerful and versatile characterization technique for investigating soft magnetic materials. The properties of soft magnets, e.g., magnetic losses strongly depend on the materials chemical composition and microstructure, including grain size and shape, texture, degree of plastic deformation and elastic strain. In electrical sheet stacks for e-motor applications, the quality of the machined edges/surfaces of each individual sheet is of special interest. Using EBSD, the influence of the punching process on the microstructure at the cutting edge is quantitatively assessed by evaluating the crystallographic misorientation distribution of the deformed grains. Using an industrial punching process, the maximum affected deformation depth is determined to be 200 - 300 μm. In the case of laser cutting, the affected deformation depth is determined to be approximately zero. Reliability and detection limits of the developed EBSD approach are evaluated on non-affected sample regions and model samples containing different indentation test bodies. A second application case is the investigation of the recrystallization process during the annealing step of soft magnetic composites (SMC toroids produced by powder metallurgy as a function of compaction pressure, annealing parameters and powder particle size. With increasing pressure and temperature, the recrystallized area fraction (e.g., grains with crystallographic misorientations 3°.

  11. Magnetoelectric coupling characteristics in multiferroic heterostructures with different thickness of nanocrystalline soft magnetic alloy

    Science.gov (United States)

    Chen, Lei; Wang, Yao

    2016-05-01

    Magnetoelectric(ME) coupling characteristics in multiferroic heterostructures with different thickness of nanocrystalline soft magnetic alloy has been investigated at low frequency. The ME response with obvious hysteresis, self-biased and dual-peak phenomenon is observed for multiferroic heterostructures, which results from strong magnetic interactions between two ferromagnetic materials with different magnetic properties, magnetostrictions and optimum bias magnetic fields Hdc,opti. The proposed multiferroic heterostructures not only enhance ME coupling significantly, but also broaden dc magnetic bias operating range and overcomes the limitations of narrow bias range. By optimizing the thickness of nanocrystalline soft magnetic alloy Tf, a significantly zero-biased ME voltage coefficient(MEVC) of 14.8mV/Oe (185 mV/cmṡ Oe) at Tf = 0.09 mm can be obtained, which is about 10.8 times as large as that of traditional PZT/Terfenol-D composite with a weak ME coupling at zero bias Hdc,zero. Furthermore, when Tf increases from 0.03 mm to 0.18 mm, the maximum MEVC increases nearly linearly with the increased Tf at Hdc,opti. Additionally, the experimental results demonstrate the ME response for multiferroic heterostructures spreads over a wide magnetic dc bias operating range. The excellent ME performance provides a promising and practicable application for both highly sensitive magnetic field sensors without bias and ME energy harvesters.

  12. Controllable helical deformations on printed anisotropic composite soft actuators

    Science.gov (United States)

    Wang, Dong; Li, Ling; Serjouei, Ahmad; Dong, Longteng; Weeger, Oliver; Gu, Guoying; Ge, Qi

    2018-04-01

    Helical shapes are ubiquitous in both nature and engineering. However, the development of soft actuators and robots that mimic helical motions has been hindered primarily due to the lack of efficient modeling approaches that take into account the material anisotropy and the directional change of the external loading point. In this work, we present a theoretical framework for modeling controllable helical deformations of cable-driven, anisotropic, soft composite actuators. The framework is based on the minimum potential energy method, and its model predictions are validated by experiments, where the microarchitectures of the soft composite actuators can be precisely defined by 3D printing. We use the developed framework to investigate the effects of material and geometric parameters on helical deformations. The results show that material stiffness, volume fraction, layer thickness, and fiber orientation can be used to control the helical deformation of a soft actuator. In particular, we found that a critical fiber orientation angle exists at which the twist of the actuator changes the direction. Thus, this work can be of great importance for the design and fabrication of soft actuators with tailored deformation behavior.

  13. Magnetic resonance imaging of pediatric soft-tissue vascular anomalies

    International Nuclear Information System (INIS)

    Navarro, Oscar M.

    2016-01-01

    Magnetic resonance (MR) imaging can be used in the management of pediatric soft-tissue vascular anomalies for diagnosing and assessing extent of lesions and for evaluating response to therapy. MR imaging studies often involve a combination of T1- and T2-weighted images in addition to MR angiography and fat-suppressed post-contrast sequences. The MR imaging features of these vascular anomalies when combined with clinical findings can aid in diagnosis. In cases of complex vascular malformations and syndromes associated with vascular anomalies, MR imaging can be used to evaluate accompanying soft-tissue and bone anomalies. This article reviews the MR imaging protocols and appearances of the most common pediatric soft-tissue vascular anomalies. (orig.)

  14. Dual-tip magnetic force microscopy with suppressed influence on magnetically soft samples

    International Nuclear Information System (INIS)

    Precner, Marián; Fedor, Ján; Šoltýs, Ján; Cambel, Vladimír

    2015-01-01

    Standard magnetic force microscopy (MFM) is considered as a powerful tool used for magnetic field imaging at nanoscale. The method consists of two passes realized by the magnetic tip. Within the first one, the topography pass, the magnetic tip directly touches the magnetic sample. Such contact perturbs the magnetization of the sample explored. To avoid the sample touching the magnetic tip, we present a new approach to magnetic field scanning by segregating the topological and magnetic scans with two different tips located on a cut cantilever. The approach minimizes the disturbance of sample magnetization, which could be a major problem in conventional MFM images of soft magnetic samples. By cutting the cantilever in half using the focused ion beam technique, we create one sensor with two different tips—one tip is magnetized, and the other one is left non-magnetized. The non-magnetized tip is used for topography and the magnetized one for the magnetic field imaging. The method developed we call dual-tip magnetic force microscopy (DT-MFM). We describe in detail the dual-tip fabrication process. In the experiments, we show that the DT-MFM method reduces significantly the perturbations of the magnetic tip as compared to the standard MFM method. The present technique can be used to investigate microscopic magnetic domain structures in a variety of magnetic samples and is relevant in a wide range of applications, e.g., data storage and biomedicine. (paper)

  15. The influence of the surface topography on the magnetization dynamics in soft magnetic thin films

    NARCIS (Netherlands)

    Craus, CB; Palasantzas, G; Chezan, AR; De Hosson, JTM; Boerma, DO; Niesen, L

    2005-01-01

    In this work we study the influence of surface roughness on the magnetization dynamics of soft magnetic nanocrystalline Fe-Zr-N thin films deposited (under identical conditions) onto a Si oxide, a thin polymer layer, and a thin Cu layer. The substrate temperature during deposition was approximately

  16. Insulator coated magnetic nanoparticulate composites with reduced core loss and method of manufacture thereof

    Science.gov (United States)

    Zhang, Yide (Inventor); Wang, Shihe (Inventor); Xiao, Danny (Inventor)

    2004-01-01

    A series of bulk-size magnetic/insulating nanostructured composite soft magnetic materials with significantly reduced core loss and its manufacturing technology. This insulator coated magnetic nanostructured composite is comprises a magnetic constituent, which contains one or more magnetic components, and an insulating constituent. The magnetic constituent is nanometer scale particles (1-100 nm) coated by a thin-layered insulating phase (continuous phase). While the intergrain interaction between the immediate neighboring magnetic nanoparticles separated by the insulating phase (or coupled nanoparticles) provide the desired soft magnetic properties, the insulating material provides the much demanded high resistivity which significantly reduces the eddy current loss. The resulting material is a high performance magnetic nanostructured composite with reduced core loss.

  17. The Characterization of the Magnetic Properties of Soft Magnetic Materials

    DEFF Research Database (Denmark)

    Larsen, Raino Michael

    1996-01-01

    The hysteresis curve and magnetic properties such as permeability, saturation induction, residual induction, coercive force and hysteresis losses are presented. The design and construction of equipment making it possible to measure true DC-values as well as AC-properties of toroid rings and cylin......The hysteresis curve and magnetic properties such as permeability, saturation induction, residual induction, coercive force and hysteresis losses are presented. The design and construction of equipment making it possible to measure true DC-values as well as AC-properties of toroid rings...

  18. Beam loss reduction by magnetic shielding using beam pipes and bellows of soft magnetic materials

    Science.gov (United States)

    Kamiya, J.; Ogiwara, N.; Hotchi, H.; Hayashi, N.; Kinsho, M.

    2014-11-01

    One of the main sources of beam loss in high power accelerators is unwanted stray magnetic fields from magnets near the beam line, which can distort the beam orbit. The most effective way to shield such magnetic fields is to perfectly surround the beam region without any gaps with a soft magnetic high permeability material. This leads to the manufacture of vacuum chambers (beam pipes and bellows) with soft magnetic materials. A Ni-Fe alloy (permalloy) was selected for the material of the pipe parts and outer bellows parts, while a ferritic stainless steel was selected for the flanges. An austenitic stainless steel, which is non-magnetic material, was used for the inner bellows for vacuum tightness. To achieve good magnetic shielding and vacuum performances, a heat treatment under high vacuum was applied during the manufacturing process of the vacuum chambers. Using this heat treatment, the ratio of the integrated magnetic flux density along the beam orbit between the inside and outside of the beam pipe and bellows became small enough to suppress beam orbit distortion. The outgassing rate of the materials with this heat treatment was reduced by one order magnitude compared to that without heat treatment. By installing the beam pipes and bellows of soft magnetic materials as part of the Japan Proton Accelerator Research Complex 3 GeV rapid cycling synchrotron beam line, the closed orbit distortion (COD) was reduced by more than 80%. In addition, a 95.5% beam survival ratio was achieved by this COD improvement.

  19. Effect of soft underlayer magnetic anisotropy on perpendicular recording process

    International Nuclear Information System (INIS)

    Lim, C.K.; Kim, E.S.; Yoon, S.Y.; Kong, S.H.; Lee, H.S.; Oh, H.S.; Kim, Y.S.

    2007-01-01

    The presence of the soft magnetic underlayer (SUL) in perpendicular magnetic recording (PMR) media is essential for the application. It is commonly understood that the SUL provides the return flux path and enhances the writing field by enhancing the recording field from the write pole. However, SUL increases the magnetic noise during the read back process due to magnetic domain walls in the SUL. Hence, it is common to grow SUL with large uniaxial or unidirectional magnetic anisotropy field (H k ) to reduce domain wall noise. In this paper, we explore the effect of increasing SUL H k on the recording process. We studied this effect by using the finite element micromagnetic simulation. Our simulation results show that the contribution of SUL to the writing field amplitude is reduced with increasing H k . This reduction in magnetic field from high H k SUL actually improves the recording performance due to the better field gradient at SUL. The simulation results are qualitatively consistent with the actual experimental data obtained from the Guzik measurement

  20. Investigations on the magnetization behavior of magnetic composite particles

    Energy Technology Data Exchange (ETDEWEB)

    Eichholz, Christian [Process Research and Chemical Engineering, BASF SE, Ludwigshafen (Germany); Knoll, Johannes, E-mail: johannes.knoll@kit.edu [Institute of Mechanical Engineering and Mechanics, Karlsruhe Institute of Technology, Karlsruhe (Germany); Lerche, Dietmar [L.U.M. GmbH, Berlin (Germany); Nirschl, Hermann [Institute of Mechanical Engineering and Mechanics, Karlsruhe Institute of Technology, Karlsruhe (Germany)

    2014-11-15

    In life sciences the application of surface functionalized magnetic composite particles is establishing in diagnostics and in downstream processing of modern biotechnology. These magnetic composite particles consist of non-magnetic material, e.g. polystyrene, which serves as a matrix for the second magnetic component, usually colloidal magnetite. Because of the multitude of magnetic cores these magnetic beads show a complex magnetization behavior which cannot be described with the available approaches for homogeneous magnetic material. Therefore, in this work a new model for the magnetization behavior of magnetic composite particles is developed. By introducing an effective magnetization and considering an overall demagnetization factor the deviation of the demagnetization of homogeneously magnetized particles is taken into account. Calculated and experimental results show a good agreement which allows for the verification of the adapted model of particle magnetization. Besides, a newly developed magnetic analyzing centrifuge is used for the characterization of magnetic composite particle systems. The experimental results, also used for the model verification, give both, information about the magnetic properties and the interaction behavior of particle systems. By adding further components to the particle solution, such as salts or proteins, industrial relevant systems can be reconstructed. The analyzing tool can be used to adapt industrial processes without time-consuming preliminary tests with large samples in the process equipments. - Highlights: • New model for magnetizability calculation of magnetic composite particles. • New method for particle bulk characterization relating to their magnetizability. • Model verification due to experimental data.

  1. Investigations on the magnetization behavior of magnetic composite particles

    International Nuclear Information System (INIS)

    Eichholz, Christian; Knoll, Johannes; Lerche, Dietmar; Nirschl, Hermann

    2014-01-01

    In life sciences the application of surface functionalized magnetic composite particles is establishing in diagnostics and in downstream processing of modern biotechnology. These magnetic composite particles consist of non-magnetic material, e.g. polystyrene, which serves as a matrix for the second magnetic component, usually colloidal magnetite. Because of the multitude of magnetic cores these magnetic beads show a complex magnetization behavior which cannot be described with the available approaches for homogeneous magnetic material. Therefore, in this work a new model for the magnetization behavior of magnetic composite particles is developed. By introducing an effective magnetization and considering an overall demagnetization factor the deviation of the demagnetization of homogeneously magnetized particles is taken into account. Calculated and experimental results show a good agreement which allows for the verification of the adapted model of particle magnetization. Besides, a newly developed magnetic analyzing centrifuge is used for the characterization of magnetic composite particle systems. The experimental results, also used for the model verification, give both, information about the magnetic properties and the interaction behavior of particle systems. By adding further components to the particle solution, such as salts or proteins, industrial relevant systems can be reconstructed. The analyzing tool can be used to adapt industrial processes without time-consuming preliminary tests with large samples in the process equipments. - Highlights: • New model for magnetizability calculation of magnetic composite particles. • New method for particle bulk characterization relating to their magnetizability. • Model verification due to experimental data

  2. Soft Multifunctional Composites and Emulsions with Liquid Metals.

    Science.gov (United States)

    Kazem, Navid; Hellebrekers, Tess; Majidi, Carmel

    2017-07-01

    Binary mixtures of liquid metal (LM) or low-melting-point alloy (LMPA) in an elastomeric or fluidic carrier medium can exhibit unique combinations of electrical, thermal, and mechanical properties. This emerging class of soft multifunctional composites have potential applications in wearable computing, bio-inspired robotics, and shape-programmable architectures. The dispersion phase can range from dilute droplets to connected networks that support electrical conductivity. In contrast to deterministically patterned LM microfluidics, LMPA- and LM-embedded elastomer (LMEE) composites are statistically homogenous and exhibit effective bulk properties. Eutectic Ga-In (EGaIn) and Ga-In-Sn (Galinstan) alloys are typically used due to their high conductivity, low viscosity, negligible nontoxicity, and ability to wet to nonmetallic materials. Because they are liquid-phase, these alloys can alter the electrical and thermal properties of the composite while preserving the mechanics of the surrounding medium. For composites with LMPA inclusions (e.g., Field's metal, Pb-based solder), mechanical rigidity can be actively tuned with external heating or electrical activation. This progress report, reviews recent experimental and theoretical studies of this emerging class of soft material architectures and identifies current technical challenges and opportunities for further advancement. © 2017 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

  3. Analysis of soft magnetic materials by electron backscatter diffraction as a powerful tool

    Science.gov (United States)

    Schuller, David; Hohs, Dominic; Loeffler, Ralf; Bernthaler, Timo; Goll, Dagmar; Schneider, Gerhard

    2018-04-01

    The current work demonstrates that electron backscatter diffraction (EBSD) is a powerful and versatile characterization technique for investigating soft magnetic materials. The properties of soft magnets, e.g., magnetic losses strongly depend on the materials chemical composition and microstructure, including grain size and shape, texture, degree of plastic deformation and elastic strain. In electrical sheet stacks for e-motor applications, the quality of the machined edges/surfaces of each individual sheet is of special interest. Using EBSD, the influence of the punching process on the microstructure at the cutting edge is quantitatively assessed by evaluating the crystallographic misorientation distribution of the deformed grains. Using an industrial punching process, the maximum affected deformation depth is determined to be 200 - 300 μm. In the case of laser cutting, the affected deformation depth is determined to be approximately zero. Reliability and detection limits of the developed EBSD approach are evaluated on non-affected sample regions and model samples containing different indentation test bodies. A second application case is the investigation of the recrystallization process during the annealing step of soft magnetic composites (SMC) toroids produced by powder metallurgy as a function of compaction pressure, annealing parameters and powder particle size. With increasing pressure and temperature, the recrystallized area fraction (e.g., grains with crystallographic misorientations particle boundaries or areas with existing plastic deformation. The progress of recrystallization is visualized as a function of time and of different particle to grain size distributions. Here, large particles with coarse internal grain structures show a favorable recrystallization behavior which results in large bulk permeability of up to 600 - 700 and lower amount of residual misorientations (>3°).

  4. Discontinuous spring magnet-type magnetostrictive Terfecohan/YFeCo multilayers: A novel nanostructured material principle for excellent magnetic softness

    International Nuclear Information System (INIS)

    Duc, N.H.; Huong Giang, D.T.

    2007-01-01

    Novel physics and reversal mechanisms of the whole system switching (WS) and individual switching (IS) type are reported for hard/soft TbFeCo/YFeCo exchange-spring multilayers. The WS type usually occurs in multilayered systems, in which the magnetic anisotropy of hard TbFeCo layers is neglectable. For such a system, the ferrimagnetically coupled hard/soft multilayered state is recovered after removing applied fields from the magnetized state. At low negative fields, the magnetization switching occurs collectively for all magnetic moments in the whole system. In this case, the low-coercivity mechanism is discussed on the basis of a hard/soft interfacial point contact. This configuration is realized for TbFeCo/YFeCo discontinuous exchange-spring multilayers, in which the magnetic (Fe,Co) nanograins coexist with non-magnetic amorphous phase in the soft layers. In this state, a magnetic coercivity as small as 0.4 mT is achieved. It is considered as an excellent magnetic softness of rare-earth-based systems. Enhancing the magnetic anisotropy in the hard TbFeCo layers, the magnetization switching follows the IS type at low temperatures. Starting to decrease the applied magnetic field from the high-field state, one observes the first reversal of the magnetic moments in the soft high-magnetization YFeCo-layers in positive magnetic fields. This is the reason for the observation of the negative coercivity as well as negative-biasing phenomena

  5. Stress induced anisotropy in CoFeMn soft magnetic nanocomposites

    Energy Technology Data Exchange (ETDEWEB)

    Leary, A. M., E-mail: leary@cmu.edu; Keylin, V.; McHenry, M. E. [Materials Science and Engineering Department, Carnegie Mellon University, 5000 Forbes Ave., Pittsburgh, Pennsylvania 15213 (United States); Ohodnicki, P. R. [Functional Materials Development Division, National Energy Technology Laboratory (NETL), 626 Cochrans Mill Road, Pittsburgh, Pennsylvania 15236 (United States)

    2015-05-07

    The use of processing techniques to create magnetic anisotropy in soft magnetic materials is a well-known method to control permeability and losses. In nanocomposite materials, field annealing below the Curie temperature results in uniaxial anisotropy energies up to ∼2 kJ/m{sup 3}. Higher anisotropies up to ∼10 kJ/m{sup 3} result after annealing Fe-Si compositions under stress due to residual stress in the amorphous matrix acting on body centered cubic crystals. This work describes near zero magnetostriction Co{sub 80−x−y}Fe{sub x}Mn{sub y}Nb{sub 4}B{sub 14}Si{sub 2} soft magnetic nanocomposites, where x and y < 8 at.% with close packed crystalline grains that show stress induced anisotropies up to ∼50 kJ/m{sup 3} and improved mechanical properties with respect to Fe-Si compositions. Difference patterns measured using transmission X-ray diffraction show evidence of affine strain with respect to the stress axis.

  6. Studies of SmCo5/Fe nanocomposite magnetic bilayers with magnetic soft x-ray transmission microscopy

    Energy Technology Data Exchange (ETDEWEB)

    Shahzad, F.; Siddiqi, S. A.; Im, M.-Y.; Avallone, A.; Fischer, P.; Hussain, Z.; Siddiqi, I.; Hellman, F.; Zhao, J.

    2009-12-04

    A hard/soft SmCo{sub 5}/Fe nanocomposite magnetic bilayer system has been fabricated on X-ray transparent 100-200 nm thin Si{sub 3}N{sub 4} membranes by magnetron sputtering. The microscopic magnetic domain pattern and its behavior during magnetization reversal in the hard and soft magnetic phases have been individually studied by element specific magnetic soft x-ray microscopy at a spatial resolution of better than 25nm. We observe that the domain patterns for soft and hard phases switch coherently throughout the full hysteresis cycle upon applying external magnetic fields. We derived local M(H) curves from the images for Fe and SmCo5 separately and found switching for both hard and soft phases same.

  7. Dynamical Origin of Highly Efficient Energy Dissipation in Soft Magnetic Nanoparticles for Magnetic Hyperthermia Applications

    Science.gov (United States)

    Kim, Min-Kwan; Sim, Jaegun; Lee, Jae-Hyeok; Kim, Miyoung; Kim, Sang-Koog

    2018-05-01

    We explore robust magnetization-dynamic behaviors in soft magnetic nanoparticles in single-domain states and find their related high-efficiency energy-dissipation mechanism using finite-element micromagnetic simulations. We also make analytical derivations that provide deeper physical insights into the magnetization dynamics associated with Gilbert damping parameters under applications of time-varying rotating magnetic fields of different strengths and frequencies and static magnetic fields. Furthermore, we find that the mass-specific energy-dissipation rate at resonance in the steady-state regime changes remarkably with the strength of rotating fields and static fields for given damping constants. The associated magnetization dynamics are well interpreted with the help of the numerical calculation of analytically derived explicit forms. The high-efficiency energy-loss power can be obtained using soft magnetic nanoparticles in the single-domain state by tuning the frequency of rotating fields to the resonance frequency; what is more, it is controllable via the rotating and static field strengths for a given intrinsic damping constant. We provide a better and more efficient means of achieving specific loss power that can be implemented in magnetic hyperthermia applications.

  8. Soft-matter composites with electrically tunable elastic rigidity

    International Nuclear Information System (INIS)

    Shan, Wanliang; Lu, Tong; Majidi, Carmel

    2013-01-01

    We use a phase-changing metal alloy to reversibly tune the elastic rigidity of an elastomer composite. The elastomer is embedded with a sheet of low-melting-point Field’s metal and an electric Joule heater composed of a serpentine channel of liquid-phase gallium–indium–tin (Galinstan ® ) alloy. At room temperature, the embedded Field’s metal is solid and the composite remains elastically rigid. Joule heating causes the Field’s metal to melt and allows the surrounding elastomer to freely stretch and bend. Using a tensile testing machine, we measure that the effective elastic modulus of the composite reversibly changes by four orders of magnitude when powered on and off. This dramatic change in rigidity is accurately predicted with a model for an elastic composite. Reversible rigidity control is also accomplished by replacing the Field’s metal with shape memory polymer. In addition to demonstrating electrically tunable rigidity with an elastomer, we also introduce a new technique to rapidly produce soft-matter electronics and multifunctional materials in several minutes with laser-patterned adhesive film and masked deposition of liquid-phase metal alloy. (paper)

  9. Soft-matter composites with electrically tunable elastic rigidity

    Science.gov (United States)

    Shan, Wanliang; Lu, Tong; Majidi, Carmel

    2013-08-01

    We use a phase-changing metal alloy to reversibly tune the elastic rigidity of an elastomer composite. The elastomer is embedded with a sheet of low-melting-point Field’s metal and an electric Joule heater composed of a serpentine channel of liquid-phase gallium-indium-tin (Galinstan®) alloy. At room temperature, the embedded Field’s metal is solid and the composite remains elastically rigid. Joule heating causes the Field’s metal to melt and allows the surrounding elastomer to freely stretch and bend. Using a tensile testing machine, we measure that the effective elastic modulus of the composite reversibly changes by four orders of magnitude when powered on and off. This dramatic change in rigidity is accurately predicted with a model for an elastic composite. Reversible rigidity control is also accomplished by replacing the Field’s metal with shape memory polymer. In addition to demonstrating electrically tunable rigidity with an elastomer, we also introduce a new technique to rapidly produce soft-matter electronics and multifunctional materials in several minutes with laser-patterned adhesive film and masked deposition of liquid-phase metal alloy.

  10. Excited eigenmodes in magnetic vortex states of soft magnetic half-spheres and spherical caps

    Energy Technology Data Exchange (ETDEWEB)

    Yoo, Myoung-Woo; Lee, Jae-Hyeok; Kim, Sang-Koog, E-mail: sangkoog@snu.ac.kr [National Creative Research Initiative Center for Spin Dynamics and Spin-Wave Devices, Nanospinics Laboratory, Research Institute of Advanced Materials, Department of Materials Science and Engineering, Seoul National University, Seoul 151-744 (Korea, Republic of)

    2014-12-14

    We studied the magnetization dynamics of excitation modes in special geometrical confinements of soft magnetic half-spheres and spherical caps in magnetic vortex states using finite-element micromagnetic numerical calculations. We found additional fine features of the zeroth- and first-order gyrotropic modes and asymmetric m = +1 and m = −1 azimuthal spin-wave modes, which detailed information is unobtainable from two-dimensional mesh-cell based numerical calculations. Moreover, we examined the perpendicular bias field dependence of the excited eigenmodes, which data provide for an efficient means of control over the excited modes. Such numerical calculations offer additional details or new underlying physics on dynamic features in arbitrary-shape magnetic nano-elements such as half-spheres and spherical caps in magnetic vortex states.

  11. Resonant magnetic scattering of polarized soft x rays

    Energy Technology Data Exchange (ETDEWEB)

    Sacchi, M. [Centre Universitaire Paris-Sud, Orsay (France); Hague, C.F. [Universite Pierre et Marie Curie, Paris (France); Gullikson, E.M.; Underwood, J. [Ernest Orlando Lawrence Berkeley National Lab., CA (United States)

    1997-04-01

    Magnetic effects on X-ray scattering (Bragg diffraction, specular reflectivity or diffuse scattering) are a well known phenomenon, and they also represent a powerful tool for investigating magnetic materials since it was shown that they are strongly enhanced when the photon energy is tuned across an absorption edge (resonant process). The resonant enhancement of the magnetic scattering has mainly been investigated at high photon energies, in order to match the Bragg law for the typical lattice spacings of crystals. In the soft X-ray range, even larger effects are expected, working for instance at the 2p edges of transition metals of the first row or at the 3d edges of rare earths (300-1500 eV), but the corresponding long wavelengths prevent the use of single crystals. Two approaches have been recently adopted in this energy range: (i) the study of the Bragg diffraction from artificial structures of appropriate 2d spacing; (ii) the analysis of the specular reflectivity, which contains analogous information but has no constraints related to the lattice spacing. Both approaches have their own specific advantages: for instance, working under Bragg conditions provides information about the (magnetic) periodicity in ordered structures, while resonant reflectivity can easily be related to electronic properties and absorption spectra. An important aspect common to all the resonant X-ray scattering techniques is the element selectivity inherent to the fact of working at a specific absorption edge: under these conditions, X-ray scattering becomes in fact a spectroscopy. Results are presented for films of iron and cobalt.

  12. Composite Microdiscs with a Magnetic Belt

    DEFF Research Database (Denmark)

    Knaapila, Matti; Høyer, Henrik; Helgesen, Geir

    2015-01-01

    , the spontaneous aggregation of composite particles is suppressed when dispersed into liquid, which is attributed to the increased particle size, reduced magnetic susceptibility, and the shape of the magnetic domain distribution within the particles (spherical versus a belt). When the composite particles...

  13. High-frequency behavior of magnetic composites

    International Nuclear Information System (INIS)

    Lagarkov, Andrey N.; Rozanov, Konstantin N.

    2009-01-01

    The paper reviews recent progress in the field of microwave magnetic properties of composites. The problem under discussion is developing composites with high microwave permeability that are needed in many applications. The theory of magnetic composites is briefly sketched with the attention paid to the laws governing the magnetic frequency dispersion in magnetic materials and basic mixing rules for composites. Recent experimental reports on the microwave performance of magnetic composites, as well as data on the agreement of the mixing rules with the measured permeability of composites that are available from the literature are discussed. From the data, a conclusion is made that the validity of a mixing rule is determined by the permeability contrast in the composite, i.e., the difference between permeability of inclusions and that of the host matrix. When the contrast is low, the Maxwell Garnet mixing rule is frequently valid. When the contrast is high, which is of the most interest for obtaining high microwave permeability of a composite, no conventionally accepted theory is capable of accurately predicting the permeability of the composites. Therefore, the mixing rules do not allow the microwave properties of magnetic composites to be predicted when the permeability of inclusions is high, that is the case of the most interest. Because of that, general limitations to the microwave performance of composites are of importance. In particular, an important relation constraining the microwave permeability of composites follows from Kittel's theory of ferromagnetic resonance and analytical properties of frequency dependence of permeability. Another constraint concerning the bandwidth of electromagnetic wave absorbers follows from the Kramers-Kronig relations for the reflection coefficient. The constraints are of importance in design and analysis of electromagnetic wave absorbers and other devices that employ the microwave magnetic properties of composites, such as

  14. Periodate oxidation of nanoscaled magnetic dextran composites

    International Nuclear Information System (INIS)

    Hong Xia; Guo Wei; Yuan Hang; Li Jun; Liu Yanmei; Ma Lan; Bai Yubai; Li Tiejin

    2004-01-01

    Highly hydrophilic, uniform and nontoxic magnetic fluids consisting of magnetite (Fe 3 O 4 ) and dextran were prepared. A periodate oxidation method was used to further activate the magnetic dextran, forming magnetic polyaldehyde-dextran, which could be conjugated to biomolecules such as proteins or antibodies. Oxidated Magnetic dextran composites were characterized by TEM, XRD and SQUID magnetometry. Moreover, a flexible, rapid and simple method to detect aldehydes was introduced to the magnetic composite system by utilizing 2,4-dinitrophenylhydrazine reagent. The result of the quantitative analysis of aldehyde was given by thermogravimetric analysis and elemental analysis

  15. Temperature-dependent magnetic properties of a magnetoactive elastomer: Immobilization of the soft-magnetic filler

    Science.gov (United States)

    Bodnaruk, Andrii V.; Brunhuber, Alexander; Kalita, Viktor M.; Kulyk, Mykola M.; Snarskii, Andrei A.; Lozenko, Albert F.; Ryabchenko, Sergey M.; Shamonin, Mikhail

    2018-03-01

    The magnetic properties of a magnetoactive elastomer (MAE) filled with μm-sized soft-magnetic iron particles have been experimentally studied in the temperature range between 150 K and 310 K. By changing the temperature, the elastic modulus of the elastomer matrix was modified, and it was possible to obtain magnetization curves for an invariable arrangement of particles in the sample and in the case when the particles were able to change their position within the MAE under the influence of magnetic forces. At low (less than 220 K) temperatures, when the matrix becomes rigid, the magnetization of the MAE does not show a hysteresis behavior, and it is characterized by a negative value of the Rayleigh constant. At room temperature, when the polymer matrix is compliant, a magnetic hysteresis exists where the dependence of the differential magnetic susceptibility on the magnetic field exhibits local maxima. The appearance of these maxima is explained by the elastic resistance of the matrix to the displacement of particles under the action of magnetic forces.

  16. Optimizing the field distribution of a Halbach type permanent magnet cylinder using the soft iron and superhard magnet

    Science.gov (United States)

    Xu, Xiaonong; Lu, Dingwei; Xu, Xibin; Yu, Yang; Gu, Min

    2018-01-01

    When a conventional Halbach type Hollow Cylindrical Permanent Magnet Array (HCPMA) is used to generate magnetic induction over the magnitude of coercivity μ0Hc, some detrimental parasitic magnetic phenomena, such as the demagnetization, magnetization reversal, and vortexes of magnetization, can appear in the interior of the magnets. We present a self-consistent quantitative analysis of the magnetization and magnetic induction distributions inside the magnetic array by considering the anisotropic and nonlinear magnetization functions of the materials consisting of the array. These numeric simulations reveal novel magnetization structures resulted from the self-field of array. We demonstrate that both the field uniformity and magnetic flux in the pole gap can be modulated by partially substituting the magnets of high energy products with the soft irons and the superhard magnets. We also show how the optimized substitution parameters can be obtained for a HCPMA achieving the best field uniformity or the maximum magnetic flux.

  17. Magnetic resonance imaging appearance of soft-tissue metastases: our experience at an orthopedic oncology center

    International Nuclear Information System (INIS)

    Sammon, Jennifer; Jain, Abhishek; Bleakney, Robert; Mohankumar, Rakesh

    2017-01-01

    To assess the prevalence and magnetic resonance imaging appearance of metastasis presenting as a soft-tissue mass. A retrospective chart review was performed on 51 patients who presented to an orthopedic oncology center with soft-tissue masses, with a histology-proven diagnosis of soft-tissue metastasis, over a 14-year period. Their magnetic resonance imaging, primary origin, and follow-up have been assessed. Soft-tissue metastasis was identified in patients ranging from 18 to 85 years old. Most (80%) of the masses were located deep to the deep fascia. In our cohort of patients, melanoma was the most common primary malignancy contributing to soft-tissue metastasis (21.8%). Among soft-tissue metastasis from solid organs, breast and lung were the most frequent (9.1% each). Five patients had soft-tissue metastases from an unknown primary. Imaging diagnosis of soft-tissue metastases is challenging as it can demonstrate imaging appearances similar to primary soft-tissue sarcoma. The presence of a known malignancy may not be evident in everyone, and even if available, histopathology will be necessary for diagnosis if this is the only site of recurrence/metastasis to differentiate from a primary soft-tissue sarcoma. Moreover, soft-tissue metastasis may be the initial presentation of a malignancy. Primary malignancies with soft-tissue metastasis carry a poor prognosis; hence, prompt diagnosis and management in essential. (orig.)

  18. Magnetic resonance imaging appearance of soft-tissue metastases: our experience at an orthopedic oncology center

    Energy Technology Data Exchange (ETDEWEB)

    Sammon, Jennifer; Jain, Abhishek; Bleakney, Robert; Mohankumar, Rakesh [Mount Sinai Hospital and University of Toronto, Division of Musculoskeletal Imaging, Joint Department of Medical Imaging, Toronto, Ontario (Canada)

    2017-04-15

    To assess the prevalence and magnetic resonance imaging appearance of metastasis presenting as a soft-tissue mass. A retrospective chart review was performed on 51 patients who presented to an orthopedic oncology center with soft-tissue masses, with a histology-proven diagnosis of soft-tissue metastasis, over a 14-year period. Their magnetic resonance imaging, primary origin, and follow-up have been assessed. Soft-tissue metastasis was identified in patients ranging from 18 to 85 years old. Most (80%) of the masses were located deep to the deep fascia. In our cohort of patients, melanoma was the most common primary malignancy contributing to soft-tissue metastasis (21.8%). Among soft-tissue metastasis from solid organs, breast and lung were the most frequent (9.1% each). Five patients had soft-tissue metastases from an unknown primary. Imaging diagnosis of soft-tissue metastases is challenging as it can demonstrate imaging appearances similar to primary soft-tissue sarcoma. The presence of a known malignancy may not be evident in everyone, and even if available, histopathology will be necessary for diagnosis if this is the only site of recurrence/metastasis to differentiate from a primary soft-tissue sarcoma. Moreover, soft-tissue metastasis may be the initial presentation of a malignancy. Primary malignancies with soft-tissue metastasis carry a poor prognosis; hence, prompt diagnosis and management in essential. (orig.)

  19. FeSiBP bulk metallic glasses with high magnetization and excellent magnetic softness

    Energy Technology Data Exchange (ETDEWEB)

    Makino, Akihiro [Institute for Materials Research, Tohoku University, 2-1-1 Katahira, Sendai 980-8577 (Japan)], E-mail: amakino@imr.tohoku.ac.jp; Kubota, Takeshi; Chang, Chuntao [Institute for Materials Research, Tohoku University, 2-1-1 Katahira, Sendai 980-8577 (Japan); Makabe, Masahiro [Makabe R and D Co., Ltd., 3-1-25 Nagatake, Sendai 983-0036 (Japan); Inoue, Akihisa [Tohoku University, 2-1-1 Katahira, Sendai 980-8577 (Japan)

    2008-10-15

    Fe-based amorphous alloy ribbons are one of the major soft magnetic materials, because of their superior magnetic properties such as the relatively high saturation magnetization (J{sub s}) of 1.5-1.6 T and good magnetic softness. However, the preparation of the ordinary amorphous magnetic alloys requires cooling rates higher than 10{sup 4} K/s due to the low glass-forming ability (GFA) and thus restricts the material outer shape. Recently, Fe-metalloid-based bulk metallic glasses (BMGs) containing glass-forming elements such as Al, Ga, Nb, Mo, Y and so forth have been developed. These alloys have high GFA, leading to the formation of BMG rod with diameters of mm-order. However, the glass-forming metal elements in BMGs result in a remarkable decrease in magnetization. Basically, J{sub s} depends on Fe content; hence, high J{sub s} requires high Fe content in the Fe-based amorphous alloys or BMGs. On the other hand, high GFA requires a large amount of glass-forming elements in the alloys, which results in lower Fe content. Therefore, in substances, the coexistence of high J{sub s} and high GFA is difficult. Since this matter should be immensely important from academia to industry in the material field, a great deal of effort has been devoted; however, it has remained unsolved for many years. In this paper, we present a novel Fe-rich FeSiBP BMG with high J{sub s} of 1.51 T comparable to the ordinary Fe-Si-B amorphous alloy now in practical use as well as with high GFA leading to a rod-shaped specimen of 2.5 mm in diameter, obtained by Cu-mold casting in air.

  20. Effect of magnetic soft phase on the magnetic properties of bulk anisotropic Nd2Fe14B/α-Fe nanocomposite permanent magnets

    Science.gov (United States)

    Li, Yuqing; Yue, Ming; Zhao, Guoping; Zhang, Hongguo

    2018-01-01

    The effects of soft phase with different particle sizes and distributions on the Nd2Fe14B/α-Fe nanocomposite magnets have been studied by the micro-magnetism simulation. The calculated results show that smaller and/or scattered distribution of soft phase can benefit to the coercivity (H ci) of the nanocomposite magnets. The magnetization moment evolution during magnetic reversal is systematically analyzed. On the other hand, magnetic properties of anisotropic Nd-Fe-B/α-Fe nanocomposite magnets prepared by hot pressing and hot deformation methods also provide evidences for the calculated results.

  1. Designing magnetic composite materials using aqueous magnetic fluids

    CERN Document Server

    Galicia, J A; Cousin, F; Guemghar, D; Menager, C; Cabuil, V

    2003-01-01

    In this paper, we report on how to take advantage of good knowledge of both the chemistry and the stability of an aqueous magnetic colloidal suspension to realize different magnetic composites. The osmotic pressure of the magnetic nanoparticles is set prior to the realization of the composite to a given value specially designed for the purpose for each hybrid material: magnetic particles in polymer networks, particles as probes for studying the structure of clay suspensions and shape modification of giant liposomes. First, we show that the introduction of magnetic particles in polyacrylamide gels enhances their Young modulus and reduces the swelling caused by water. The particles cause both a mechanical and an osmotic effect. The latter is strongly dependent on the ionic strength and is attributed to an attraction between particles and the polymeric matrix. In the second part, we determine the microscopic structure of suspensions of laponite as a function of concentration, by combining SANS and magneto-optica...

  2. Magnetic nanofluids and magnetic composite fluids in rotating seal systems

    International Nuclear Information System (INIS)

    Borbath, T; Borbath, I; Boros, T; Bica, D; Vekas, L; Potencz, I

    2010-01-01

    Recent results are presented concerning the development of magnetofluidic leakage-free rotating seals for vacuum and high pressure gases, evidencing significant advantages compared to mechanical seals. The micro-pilot scale production of various types of magnetizable sealing fluids is shortly reviewed, in particular the main steps of the chemical synthesis of magnetic nanofluids and magnetic composite fluids with light hydrocarbon, mineral oil and synthetic oil carrier liquids. The behavior of different types of magnetizable fluids in the rotating sealing systems is analyzed. Design concepts, some constructive details and testing procedures of magnetofluidic rotating seals are presented such as the testing equipment. The main characteristics of several magnetofluidic sealing systems and their applications will be presented: vacuum deposition systems and liquefied gas pumps applications, mechanical and magnetic nanofluid combined seals, gas valves up to 40 bar equipped by rotating seal with magnetic nanofluids and magnetic composite fluids.

  3. FORC-study of magnetization reversal of L10-FePt based exchange coupled composite films

    Directory of Open Access Journals (Sweden)

    Gongyuan Situ

    2017-05-01

    Full Text Available Perpendicular exchange coupled composite structures were prepared, utilizing L10-FePt as hard layer and [Co/Ni]N multilayer as soft layer. Magnetic characteristics revealed the gradually change of the magnetization reversal mechanism from incoherent rotational mode to dominant wall motion as the thickness of soft layer increases. Furthermore, FORC analysis were employed to characterize the interactions of our ECC magnetic system, the result indicates that the exchange coupling interaction were enhanced with the increasing thickness of soft layer.

  4. Improving Mechanical Properties of Molded Silicone Rubber for Soft Robotics Through Fabric Compositing.

    Science.gov (United States)

    Wang, Yue; Gregory, Cherry; Minor, Mark A

    2018-06-01

    Molded silicone rubbers are common in manufacturing of soft robotic parts, but they are often prone to tears, punctures, and tensile failures when strained. In this article, we present a fabric compositing method for improving the mechanical properties of soft robotic parts by creating a fabric/rubber composite that increases the strength and durability of the molded rubber. Comprehensive ASTM material tests evaluating the strength, tear resistance, and puncture resistance are conducted on multiple composites embedded with different fabrics, including polyester, nylon, silk, cotton, rayon, and several blended fabrics. Results show that strong fabrics increase the strength and durability of the composite, valuable in pneumatic soft robotic applications, while elastic fabrics maintain elasticity and enhance tear strength, suitable for robotic skins or soft strain sensors. Two case studies then validate the proposed benefits of the fabric compositing for soft robotic pressure vessel applications and soft strain sensor applications. Evaluations of the fabric/rubber composite samples and devices indicate that such methods are effective for improving mechanical properties of soft robotic parts, resulting in parts that can have customized stiffness, strength, and vastly improved durability.

  5. Sensor Applications of Soft Magnetic Materials Based on Magneto-Impedance, Magneto-Elastic Resonance and Magneto-Electricity

    Directory of Open Access Journals (Sweden)

    Alfredo García-Arribas

    2014-04-01

    Full Text Available The outstanding properties of selected soft magnetic materials make them successful candidates for building high performance sensors. In this paper we present our recent work regarding different sensing technologies based on the coupling of the magnetic properties of soft magnetic materials with their electric or elastic properties. In first place we report the influence on the magneto-impedance response of the thickness of Permalloy films in multilayer-sandwiched structures. An impedance change of 270% was found in the best conditions upon the application of magnetic field, with a low field sensitivity of 140%/Oe. Second, the magneto-elastic resonance of amorphous ribbons is used to demonstrate the possibility of sensitively measuring the viscosity of fluids, aimed to develop an on-line and real-time sensor capable of assessing the state of degradation of lubricant oils in machinery. A novel analysis method is shown to sensitively reveal the changes of the damping parameter of the magnetoelastic oscillations at the resonance as a function of the oil viscosity. Finally, the properties and performance of magneto-electric laminated composites of amorphous magnetic ribbons and piezoelectric polymer films are investigated, demonstrating magnetic field detection capabilities below 2.7 nT.

  6. A general perspective on the magnetization reversal in cylindrical soft magnetic nanowires with dominant shape anisotropy

    Energy Technology Data Exchange (ETDEWEB)

    Kuncser, A. [National Institute of Materials Physics, PO Box MG-7, 077125 Bucharest-Magurele (Romania); University of Bucharest, Faculty of Physics, PO Box MG-11, 077125 Bucharest-Magurele (Romania); Antohe, S. [University of Bucharest, Faculty of Physics, PO Box MG-11, 077125 Bucharest-Magurele (Romania); Kuncser, V., E-mail: kuncser@infim.ro [National Institute of Materials Physics, PO Box MG-7, 077125 Bucharest-Magurele (Romania)

    2017-02-01

    Peculiarities of the magnetization reversal process in cylindrical Ni-Cu soft magnetic nanowires with dominant shape anisotropy are analyzed via both static and time dependent micromagnetic simulations. A reversible process involving a coherent-like spin rotation is always observed for magnetic fields applied perpendicularly to the easy axis whereas nucleation of domain walls is introduced for fields applied along the easy axis. Simple criteria for making distinction between a Stoner-Wohlfarth type rotation and a nucleation mechanism in systems with uniaxial magnetic anisotropy are discussed. Superposed reversal mechanisms can be in action for magnetic fields applied at arbitrary angles with respect to the easy axis within the condition of an enough strong axial component required by the nucleation. The dynamics of the domain wall, involving two different stages (nucleation and propagation), is discussed with respect to initial computing conditions and orientations of the magnetic field. A nucleation time of about 3 ns and corkscrew domain walls propagating with a constant velocity of about 150 m/s are obtained in case of Ni-Cu alloy (Ni rich side) NWs with diameters of 40 nm and high aspect ratio. - Highlights: • The formation and the dynamics of the domain walls in magnetic nanowires have been studied by micromagnetic simulations. • Simple criteria for making distinction between Stoner-Wohlfarth type and nucleation mechanisms in nanowires were discussed. • Corkscrew domain walls or quasi-coherent spin rotation may be induced depending on the field orientation. • The nucleation time was estimated at 3 ns and the wall velocity at 150 m/s. • A simple way for tuning the wall velocity in such systems was mentioned.

  7. Controlling the competing magnetic anisotropy energies in FineMET amorphous thin films with ultra-soft magnetic properties

    Directory of Open Access Journals (Sweden)

    Ansar Masood

    2017-05-01

    Full Text Available Thickness dependent competing magnetic anisotropy energies were investigated to explore the global magnetic behaviours of FineMET amorphous thin films. A dominant perpendicular magnetization component in the as-deposited state of thinner films was observed due to high magnetoelastic anisotropy energy which arises from stresses induced at the substrate-film interface. This perpendicular magnetization component decreases with increasing film thickness. Thermal annealing at elevated temperature revealed a significant influence on the magnetization state of the FineMET thin films and controlled annealing steps leads to ultra-soft magnetic properties, making these thin films alloys ideal for a wide range of applications.

  8. Nanolaminated FeCoB/FeCo and FeCoB/NiFe soft magnetic thin films with tailored magnetic properties deposited by magnetron sputtering

    Science.gov (United States)

    Hida, Rachid; Falub, Claudiu V.; Perraudeau, Sandrine; Morin, Christine; Favier, Sylvie; Mazel, Yann; Saghi, Zineb; Michel, Jean-Philippe

    2018-05-01

    Thin films based on layers of Fe52Co28B20 (at%), Fe65Co35 (at%), and Ni80Fe20 (at%) were deposited by sputtering on 8″ bare Si and Si/200 nm-thermal-SiO2 wafers by simultaneous use of two or more cathodes. Due to the continuous rotation of the substrate cage, such that the substrates faced different targets alternately, the multilayers consisted of stacks of alternating, nanometer-thick regular layers. The composition of the films was determined by Rutherford Backscattering Spectrometry (RBS) and Nuclear Reactive Analysis (NRA), whereas Plasma Profiling Time of Flight Mass Spectrometry (PP-TOFMS) analysis gave depth profile information about the chemical elements. The structural and magnetic properties of the films were investigated by X-ray Diffraction and by TEM analysis, B-H loop tracer and high frequency single coil technique permeametry, respectively. The linear dependence of the coercivity of these thin films versus the grain size can be explained by the random anisotropy model. These novel, composite soft magnetic multilayers, with tunable in-plane anisotropy, allow operation at tunable frequencies, as shown by broadband (between 100 MHz and 10 GHz) RF measurements that exhibit a classical Landau-Lifschitz-Gilbert (LLG) behavior and, combine the magnetic properties of the individual materials in an advantageous way. This article presents a method to produce nanostructured soft magnetic multilayers, the properties of which can easily be tuned by choosing the ratio of the individual nanolayers. In this way it's possible to combine soft magnetic materials with complementary properties, e.g. high saturation magnetization, low coercivity, high specific resistivity and low magnetostriction

  9. Soft magnetic characteristics of laminated magnetic block cores assembled with a high Bs nanocrystalline alloy

    Directory of Open Access Journals (Sweden)

    Atsushi Yao

    2018-05-01

    Full Text Available This paper focuses on an evaluation of core losses in laminated magnetic block cores assembled with a high Bs nanocrystalline alloy in high magnetic flux density region. To discuss the soft magnetic properties of the high Bs block cores, the comparison with amorphous (SA1 block cores is also performed. In the high Bs block core, both low core losses and high saturation flux densities Bs are satisfied in the low frequency region. Furthermore, in the laminated block core made of the high Bs alloy, the rate of increase of iron losses as a function of the magnetic flux density remains small up to around 1.6 T, which cannot be realized in conventional laminated block cores based on amorphous alloy. The block core made of the high Bs alloy exhibits comparable core loss with that of amorphous alloy core in the high-frequency region. Thus, it is expected that this laminated high Bs block core can achieve low core losses and high saturation flux densities in the high-frequency region.

  10. Fabrication and characterization of magnetic composite membrane pressure sensor

    KAUST Repository

    Khan, Mohammed Asadullah

    2016-04-20

    This paper describes a magnetic field powered pressure sensor, which comprises a coil array and a magnetic composite membrane. The composite membrane is made by embedding a ribbon of the amorphous soft magnetic alloy Vitrovac®, in a 17 mm x 25 mm x 1.5 mm Polydimethylsiloxane (PDMS) layer. PDMS is chosen for its low Young\\'s modulus and the amorphous alloy for its high permeability. The membrane is suspended 1.5 mm above a 17x19 array of microfabricated planar coils. The coils are fabricated by patterning a 620 nm thick gold layer. Each coil occupies an area of 36000 μm2 and consists of 14 turns. The sensor is tested by subjecting it to pressure and simultaneously exciting it by a 24 A/m, 100 kHz magnetic field. A pressure change from 0 kPa to 5.1 kPa, results in a 5400 ppm change in the voltage output.

  11. Fabrication and characterization of magnetic composite membrane pressure sensor

    KAUST Repository

    Khan, Mohammed Asadullah; Alfadhel, Ahmed; Kosel, Jü rgen; Bakolka, M.

    2016-01-01

    This paper describes a magnetic field powered pressure sensor, which comprises a coil array and a magnetic composite membrane. The composite membrane is made by embedding a ribbon of the amorphous soft magnetic alloy Vitrovac®, in a 17 mm x 25 mm x 1.5 mm Polydimethylsiloxane (PDMS) layer. PDMS is chosen for its low Young's modulus and the amorphous alloy for its high permeability. The membrane is suspended 1.5 mm above a 17x19 array of microfabricated planar coils. The coils are fabricated by patterning a 620 nm thick gold layer. Each coil occupies an area of 36000 μm2 and consists of 14 turns. The sensor is tested by subjecting it to pressure and simultaneously exciting it by a 24 A/m, 100 kHz magnetic field. A pressure change from 0 kPa to 5.1 kPa, results in a 5400 ppm change in the voltage output.

  12. Hydrothermal Synthesis of Nanooctahedra MnFe₂O₄ onto the Wood Surface with Soft Magnetism, Fire Resistance and Electromagnetic Wave Absorption.

    Science.gov (United States)

    Wang, Hanwei; Yao, Qiufang; Wang, Chao; Ma, Zhongqing; Sun, Qingfeng; Fan, Bitao; Jin, Chunde; Chen, Yipeng

    2017-05-23

    In this study, nanooctahedra MnFe₂O₄ were successfully deposited on a wood surface via a low hydrothermal treatment by hydrogen bonding interactions. As-prepared MnFe₂O₄/wood composite (MW) had superior performance of soft magnetism, fire resistance and electromagnetic wave absorption. Among them, small hysteresis loops and low coercivity (magnetization-field curve of MW with saturation magnetization of 28.24 emu/g, indicating its excellent soft magnetism. The MW also exhibited a good fire-resistant property due to its initial burning time at 20 s; while only 6 s for the untreated wood (UW) in combustion experiments. Additionally, this composite revealed good electromagnetic wave absorption with a minimum reflection loss of -9.3 dB at 16.48 GHz. Therefore, the MW has great potential in the fields of special decoration and indoor electromagnetic wave absorbers.

  13. Development of Composite Grinding Wheels for Hard and Soft Metals

    OpenAIRE

    Pruti, Faruk

    2012-01-01

    This research investigates the performance of grinding wheel in terms of its internal granular particles and their effect on the surface finish for both soft and hard metals subjected to both dry and wet conditions of use. The study considers the properties of materials of construction including hardness of the granular particles and their size and distributions that affects the grinding wheel efficiency in abrading of soft and hard metal surfaces. Furthermore, in order to improve grinding pe...

  14. Engineering Gilbert damping by dilute Gd doping in soft magnetic Fe thin Films

    NARCIS (Netherlands)

    Zhang, W.; Jiang, S.; Wong, P.K.J.; Sun, Li; Wang, Y.K.; Wang, Kai; de Jong, Machiel Pieter; van der Wiel, Wilfred Gerard; van der Laan, G.; Zhai, Y.

    2014-01-01

    By analyzing the ferromagnetic resonance linewidth, we show that the Gilbert damping constant in soft magnetic Fe thin films can be enhanced by ∼6 times with Gd doping of up to 20%. At the same time, the magnetic easy axis remains in the film plane while the coercivity is strongly reduced after Gd

  15. Controlling the induced anisotropy in soft magnetic films for high-frequency applications

    NARCIS (Netherlands)

    Chezan, A.R.; Craus, C.B.; Chechenin, N.G.; Vystavel, T.; Hosson, J.Th.M. De; Niesen, L.; Boerma, D.O.

    Nanocrystalline soft magnetic Fe–Zr–N films were successfully deposited by dc magnetron reactive sputtering. The nitrogen content was controlled by varying the Ar/N2 ratio and/or the substrate temperature. The films have saturation magnetization and induced uniaxial anisotropy values in the range

  16. Soft X-ray magnetic scattering study of rotational magnetisation processes in cobalt/copper multilayers

    International Nuclear Information System (INIS)

    Hase, T.P.A.; Fulthorpe, B.D.; Wilkins, S.B.; Tanner, B.K.; Marrows, C.H.; Hickey, B.J.

    2001-01-01

    We report the observation of magnetic viscosity in the intensity of resonant magnetic soft X-ray scattering during rotational magnetisation processes in antiferromagnetically coupled Co/Cu multilayers. The hysteretic time-dependent component of the signal can be fitted to a single-exponential function that varies as a function of magnetising field

  17. Magnetic self-assembly for the synthesis of magnetically exchange coupled MnBi/Fe–Co composites

    Energy Technology Data Exchange (ETDEWEB)

    Xu, Xia [Department of Chemical and Biological Engineering and MINT Center, The University of Alabama, Tuscaloosa, AL 35487 (United States); Hong, Yang-Ki, E-mail: ykhong@eng.ua.edu [Department of Electrical and Computer Engineering and MINT Center, The University of Alabama, Tuscaloosa, AL 35487 (United States); Park, Jihoon; Lee, Woncheol [Department of Electrical and Computer Engineering and MINT Center, The University of Alabama, Tuscaloosa, AL 35487 (United States); Lane, Alan M. [Department of Chemical and Biological Engineering and MINT Center, The University of Alabama, Tuscaloosa, AL 35487 (United States); Cui, Jun [Energy and Environment Directorate, Pacific Northwestern National Laboratory, Richland, WA 99354 (United States)

    2015-11-15

    Exchange coupled hard/soft MnBi/Fe–Co core/shell structured composites were synthesized using a magnetic self-assembly process. MnBi particles were prepared by arc-melting, and Fe–Co nanoparticles were synthesized by an oleic acid assisted chemical reduction method. Grinding a mixture of micron-sized MnBi and Fe–Co nanoparticles in hexane resulted in MnBi/Fe–Co core/shell structured composites. The MnBi/Fe–Co (95/5 wt%) composites showed smooth magnetic hysteresis loops, enhanced remanent magnetization, and positive values in the ΔM curve, indicating exchange coupling between MnBi and Fe–Co particles. - Graphical abstract: Both MnBi and Fe–Co particles were dispersed in hexane for grinding. Because of the oleic acid used during the Fe–Co nanoparticle synthesis, they could be well dispersed in hexane. During the grinding, the size of MnBi particles was decreased, hexane was evaporated, and the Fe–Co nanoparticles were concentrated in the solvent and magnetically attracted by MnBi particles, forming a core/shell structure. - Highlights: • Exchange coupled MnBi/Fe–Co composites are synthesized through magnetic selfassembly. • Magnetic exchange coupling is demonstrated by smooth magnetic hysteresis loops, enhanced remanent magnetization, and dominant positive peak in the ΔM curve. • The experimental results in magnetic properties are close to the theoretical calculation results.

  18. In vivo determination of body composition of rats using magnetic resonance imaging.

    Science.gov (United States)

    Tang, H; Vasselli, J; Wu, E; Gallagher, D

    2000-05-01

    Magnetic resonance imaging (MRI) has potential as an instrument to measure body composition because it can discriminate various soft tissues in vivo. These soft tissues include adipose tissue, muscle, organs, and brain. We report on preliminary studies using a 4.2-tesla MRI for measuring body composition in the mouse and rat. We employed image segmentation methods that include an image correction method, a necessary requirement when the images are taken in the presence of nonuniform radio-frequency (RF) coil response. The software for 3-D data segmentation, quantification, correction, image manipulation, and visualization has been developed as a research tool. This method currently is being validated.

  19. A 3D-Printable Polymer-Metal Soft-Magnetic Functional Composite—Development and Characterization

    Directory of Open Access Journals (Sweden)

    Bilal Khatri

    2018-01-01

    Full Text Available In this work, a 3D printed polymer–metal soft-magnetic composite was developed and characterized for its material, structural, and functional properties. The material comprises acrylonitrile butadiene styrene (ABS as the polymer matrix, with up to 40 vol. % stainless steel micropowder as the filler. The composites were rheologically analyzed and 3D printed into tensile and flexural test specimens using a commercial desktop 3D printer. Mechanical characterization revealed a linearly decreasing trend of the ultimate tensile strength (UTS and a sharp decrease in Young’s modulus with increasing filler content. Four-point bending analysis showed a decrease of up to 70% in the flexural strength of the composite and up to a two-factor increase in the secant modulus of elasticity. Magnetic hysteresis characterization revealed retentivities of up to 15.6 mT and coercive forces of up to 4.31 kA/m at an applied magnetic field of 485 kA/m. The composite shows promise as a material for the additive manufacturing of passive magnetic sensors and/or actuators.

  20. Soft mode and magnetic phase transition in PrNi

    International Nuclear Information System (INIS)

    Alekseev, P.A.; Lazukov, V.N.; Sadikov, I.P.; Klement'ev, E.S.; Allenspach, P.; Chumlyakov, Yu.I.

    2002-01-01

    The spectrum of the magnetic excitation of the PrNi intermetallic compound monocrystal is studied through the neutrons inelastic scattering. Essential softening of certain collective modes of the magnetic excitation near the temperature of the ferromagnetic ordering T c ∼ 20 K is identified. The above result is analyzed from the viewpoint of the model, describing the magnetic phase transition in the systems with the directed magnetic moment [ru

  1. Magnetic resonance imaging of peripheral soft tissue hemangiomas

    Energy Technology Data Exchange (ETDEWEB)

    Nelson, M C; Stull, M A; Patt, R H; Freedman, M T [Georgetown Univ., Washington, DC (USA). Dept. of Radiology; Teitelbaum, G P [Georgetown Univ., Washington, DC (USA). Dept. of Radiology University of Southern California, Los Angeles (USA). Dept. of Radiology; Lack, E E [Georgetown Univ., Washington, DC (USA). Dept. of Pathology; Bogumill, G P [Georgetown Univ., Washington, DC (USA). Dept. of Orthopedic Surgery

    1990-10-01

    Ten patients with soft tissue hemangiomas outside the central nervous system were studied with MR imaging. Eight patients were studied at 1.5 Tesla (T) with T{sub 1}-weighted and triple echo T{sub 2}-weighted sequences. Two additional patients were imaged on a 0.5-T system. The MR images were correlated with images from other modalities. It was found that prolonged T{sub 2}-weighted imaging together with standard spin echo T{sub 1} and T{sub 2} pulse sequences is a good substitute for contrast-enhanced CT and arteriographic evaluation of soft tissue hemangiomas. (orig./DG).

  2. A Magnetic Resonance Compatible Soft Wearable Robotic Glove for Hand Rehabilitation and Brain Imaging.

    Science.gov (United States)

    Hong Kai Yap; Kamaldin, Nazir; Jeong Hoon Lim; Nasrallah, Fatima A; Goh, James Cho Hong; Chen-Hua Yeow

    2017-06-01

    In this paper, we present the design, fabrication and evaluation of a soft wearable robotic glove, which can be used with functional Magnetic Resonance imaging (fMRI) during the hand rehabilitation and task specific training. The soft wearable robotic glove, called MR-Glove, consists of two major components: a) a set of soft pneumatic actuators and b) a glove. The soft pneumatic actuators, which are made of silicone elastomers, generate bending motion and actuate finger joints upon pressurization. The device is MR-compatible as it contains no ferromagnetic materials and operates pneumatically. Our results show that the device did not cause artifacts to fMRI images during hand rehabilitation and task-specific exercises. This study demonstrated the possibility of using fMRI and MR-compatible soft wearable robotic device to study brain activities and motor performances during hand rehabilitation, and to unravel the functional effects of rehabilitation robotics on brain stimulation.

  3. Hemorrhagic lesions in soft tissue: utility and limitations of magnetic resonance

    International Nuclear Information System (INIS)

    Legorburu, A.; Oleaga, L.; Ibarra, V.; Grande, D.

    1998-01-01

    We present four patients with hemorrhagic soft tissue tumors. The diagnosis was malignant fibrous histiocytoma in three of the patients and hematoma in the fourth. We show the magnetic resonance findings in these four cases, stressing the value of this technique in the assessment of the extension of soft tissue tumors. The difficulty in differentiating tumors with bleeding, as often occurs with malignant fibrous histiocytoma, from true hematomas. (Author) 8 refs

  4. Unravelling the tunable exchange bias-like effect in magnetostatically-coupled two dimensional hybrid (hard/soft) composites

    International Nuclear Information System (INIS)

    Hierro-Rodriguez, A; Teixeira, J M; Rodriguez-Rodriguez, G; Rubio, H; Vélez, M; Álvarez-Prado, L M; Martín, J I; Alameda, J M

    2015-01-01

    Hybrid 2D hard-soft composites have been fabricated by combining soft (Co 73 Si 27 ) and hard (NdCo 5 ) magnetic materials with in-plane and out-of-plane magnetic anisotropies, respectively. They have been microstructured in a square lattice of CoSi anti-dots with NdCo dots within the holes. The magnetic properties of the dots allow us to introduce a magnetostatic stray field that can be controlled in direction and sense by their last saturating magnetic field. The magnetostatic interactions between dot and anti-dot layers induce a completely tunable exchange bias-like shift in the system’s hysteresis loops. Two different regimes for this shift are present depending on the lattice parameter of the microstructures. For large parameters, dipolar magnetostatic decay is observed, while for the smaller one, the interaction between the adjacent anti-dot’s characteristic closure domain structures enhances the exchange bias-like effect as clarified by micromagnetic simulations. (paper)

  5. Dynamic properties of micro-magnetic noise in soft ferromagnetic materials

    Science.gov (United States)

    Stupakov, A.; Perevertov, A.

    2018-06-01

    Dynamic response of magnetic hysteresis, magnetic Barkhausen noise and magneto-acoustic emission in a soft ribbon and electrical steels was studied comprehensively. The measurements were performed under controllable magnetization conditions: sinusoidal/triangular waveforms of the magnetic induction and a triangular waveform of the magnetic field. Magnetizing frequency was varied in a wide range: fmag = 0.5 - 500 and 0.5-100 Hz for the ribbon and the electrical steels, respectively. Magnetization amplitude was fixed on a near-saturation level Hmax ≃ 100 A/m. Barkhausen noise signal was detected by a sample-wrapping/surface-mounted coil and differently filtered. It was found that intensity of the Barkhausen noise rises approximately as a square root function of the magnetizing frequency. Whereas, level of the magneto-acoustic emission follows the hysteresis loss trend with an additional linear term (classical loss component).

  6. Simulation of motional eddy current phenomena in soft magnetic material

    Science.gov (United States)

    De Gersem, Herbert; Hameyer, Kay

    2001-05-01

    The finite element simulation of conductors moving in a magnetic field at elevated speeds, yields oscillatory solutions. To overcome the effect of the huge convection terms, the partial differential equation is stabilised by adding artificial diffusion. Accurate results are obtained by applying adaptive mesh refinement. A rotational magnetic brake with a solid ferromagnetic rotor is simulated.

  7. Simulation of motional eddy current phenomena in soft magnetic material

    International Nuclear Information System (INIS)

    Gersem, Herbert de; Hameyer, Kay

    2001-01-01

    The finite element simulation of conductors moving in a magnetic field at elevated speeds, yields oscillatory solutions. To overcome the effect of the huge convection terms, the partial differential equation is stabilised by adding artificial diffusion. Accurate results are obtained by applying adaptive mesh refinement. A rotational magnetic brake with a solid ferromagnetic rotor is simulated

  8. Mechanical design and analysis of an eight-pole superconducting vector magnet for soft x-ray magnetic dichroism measurements

    Energy Technology Data Exchange (ETDEWEB)

    Arbelaez, D.; Black, A.; Prestemon, S.O.; Wang, S.; Chen, J.; Arenholz, E.

    2010-01-13

    An eight-pole superconducting magnet is being developed for soft x-ray magnetic dichroism (XMD) experiments at the Advanced Light Source, Lawrence Berkley National Laboratory (LBNL). Eight conical Nb{sub 3}Sn coils with Holmium poles are arranged in octahedral symmetry to form four dipole pairs that provide magnetic fields of up to 5 T in any direction relative to the incoming x-ray beam. The dimensions of the magnet yoke as well as pole taper, diameter, and length were optimized for maximum peak field in the magnet center using the software package TOSCA. The structural analysis of the magnet is performed using ANSYS with the coil properties derived using a numerical homogenization scheme. It is found that the use of orthotropic material properties for the coil has an important influence in the design of the magnet.

  9. A comprehensive study of soft magnetic materials based on FeSi spheres and polymeric resin modified by silica nanorods

    International Nuclear Information System (INIS)

    Strečková, M.; Füzer, J.; Kobera, L.; Brus, J.; Fáberová, M.; Bureš, R.; Kollár, P.; Lauda, M.; Medvecký, Ĺ.; Girman, V.; Hadraba, H.; Bat'ková, M.; Bat'ko, I.

    2014-01-01

    A novel soft magnetic composite (SMC) based on spherical FeSi particles precisely covered by hybrid phenolic resin was designed. The hybrid resin including silica nano-rods chemically incorporated into the phenolic polymer matrix was prepared by the modified sol–gel method. A chemical bridge connecting silica nano-rods with the base polymeric net was verified by FTIR, 13 C and 29 Si NMR spectroscopy, whereas the shape and size of silica nano-rods were determined by TEM. It is shown that the modification of polymeric resin by silica nano-rods generally leads to the improved thermal and mechanical properties of the final samples. The hybrid resin serves as a perfect insulating coating deposited on FeSi particles and the core–shell particles can be further compacted by standard powder metallurgy methods in order to prepare final samples for mechanical, electric and magnetic testing. SEM images evidence negligible porosity, uniform distribution of the hybrid resin around FeSi particles, as well as, dimensional shape stability of the final samples after thermal treatment. The hardness, flexural strength and density of the final samples are comparable to the sintered SMCs, but they simultaneously exhibit much higher specific resistivity along with only slightly lower coercivity and permeability. - Highlights: • Soft magnetic composites are designed for electrotechnical applications. • Electroinsulating layer consists of phenolic resin modified with silica nano-rods. • NMR, FTIR and DSC analysis is used to characterize hybrid resin. • Spherical Fe–Si particles covered by hybrid resin form a core–shell composite. • Mechanical, electrical and magnetic properties are described in detail

  10. Magnetostatic bias in a composite hard/soft/hard microlayer

    Czech Academy of Sciences Publication Activity Database

    Kraus, Luděk; Pirota, K.R.; Torrejón, J.; Vázquez, M.

    2007-01-01

    Roč. 101, č. 6 (2007), 063910/1-063910/4 ISSN 0021-8979 Grant - others:Spanish Research Project(ES) MAT2004-00150 Institutional research plan: CEZ:AV0Z10100520 Keywords : magnetic bias * amorphous alloys * geometrical dimensions Subject RIV: BM - Solid Matter Physics ; Magnetism Impact factor: 2.171, year: 2007

  11. Frequency characterization of thin soft magnetic material layers used in spiral inductors

    International Nuclear Information System (INIS)

    Kriga, Adoum; Allassem, Désiré; Soultan, Malloum; Chatelon, Jean-Pierre; Siblini, Ali; Allard, Bruno; Rousseau, Jean Jacques

    2012-01-01

    The paper details the characterization of thin magnetic materials layers, particularly soft materials, with respect to their behaviour in frequency (from 10 MHz to 1 GHz). The proposed method is suitable for any soft but insulating magnetic material; Yttrium Iron Garnet (YIG) is used as an example. The principle is based on a comparison between simulations for different values of the permeability and measurement values versus frequency of planar inductor structures; an experimental validation is proposed as well. Thin magnetic material is first deposited on an alumina substrate using RF sputtering technique; a planar spiral winding of copper is then deposited on the magnetic material by the same technique. The effective permeability versus frequency is obtained by comparing two samples of spiral windings with and without magnetic material. Network analyser measurements on samples of various geometrical dimensions and of different thicknesses are necessary to determine the effective magnetic permeability; we have obtained a relative effective permeability of about 30 for seven turns spiral inductor of a 17 μm YIG film. - Highlights: ► A simple and original method is presented for the characterization of soft magnetic layer. ► This is a non-destructive method based on standard equipment. ► The principle is based on a comparison between simulations and measurement. ► An experimental validation is proposed as well.

  12. Magnetization of neutron star matter and implications in physics of soft gamma repeaters

    Energy Technology Data Exchange (ETDEWEB)

    Kondratyev, V N [Japan Atomic Energy Research Inst., Tokai, Ibaraki (Japan). Tokai Research Establishment

    2002-01-01

    The magnetization of neutron star matter is considered within the thermodynamic formalism. The quantization effects are demonstrated to result in sharp abrupt magnetic field dependence of nuclide magnetic moments. Accounting for inter-nuclide magnetic coupling we show that such anomalies give rise to erratic jumps in magnetotransport of neutron star crusts. The properties of such a noise are favorably compared with burst statistics of Soft Gamma Repeaters. PACS: 97.60.Jd, 21.10.Dr, 26.60.+c, 95.30.Ky. (author)

  13. Composite magnetic nanoparticles: Synthesis and cancer-related applications

    International Nuclear Information System (INIS)

    Cai Ping; Chen Hong-Min; Xie Jin

    2014-01-01

    Recent advances in the preparation and applications of composite magnetic nanoparticles are reviewed and summarized, with a focus on cancer-related applications. (topical review - magnetism, magnetic materials, and interdisciplinary research)

  14. High performance of low cost soft magnetic materials

    Indian Academy of Sciences (India)

    Administrator

    The consistent interest in supporting research and development of magnetic materials during the last century is revealed in their ... type of nanocrystalline alloys, i.e. crystals 10–20 nm in ..... nonetheless useful for a qualitative analysis of phase.

  15. Creep deformation of a soft magnetic iron-cobalt alloy

    OpenAIRE

    Fingers, Richard T.; Coate, Jack E.; Dowling, Norman E.

    1999-01-01

    The U.S. Air Force is in the process of developing magnetic bearings, as well as an aircraft integrated power unit and an internal starter/generator for main propulsion engines. These developments are the driving force for the new emphasis on the development of high saturation, low loss magnets capable of maintaining structural integrity in high stress and high temperature environments. It is this combination of desired material characteristics that is the motivation of this effort to measure...

  16. Current distribution and giant magnetoimpedance in composite wires with helical magnetic anisotropy

    International Nuclear Information System (INIS)

    Buznikov, N.A.; Antonov, A.S.; Granovsky, A.B.; Kim, C.G.; Kim, C.O.; Li, X.P.; Yoon, S.S.

    2006-01-01

    The giant magnetoimpedance effect in composite wires consisting of a non-magnetic inner core and soft magnetic shell is studied theoretically. It is assumed that the magnetic shell has a helical anisotropy. The current and field distributions in the composite wire are found by means of a simultaneous solution of Maxwell equations and the Landau-Lifshitz equation. The expressions for the diagonal and off-diagonal impedance are obtained for low and high frequencies. The dependences of the impedance on the anisotropy axis angle and the shell thickness are analyzed. Maximum field sensitivity is shown to correspond to the case of the circular anisotropy in the magnetic shell. It is demonstrated that the optimum shell thickness to obtain maximum impedance ratio is equal to the effective skin depth in the magnetic material

  17. Current distribution and giant magnetoimpedance in composite wires with helical magnetic anisotropy

    Energy Technology Data Exchange (ETDEWEB)

    Buznikov, N.A. [Institute for Theoretical and Applied Electrodynamics, Russian Academy of Sciences, Moscow 125412 (Russian Federation) and Research Center for Advanced Magnetic Materials, Chungnam National University, Daeduk Science Town, Daejeon 305-764 (Korea, Republic of)]. E-mail: n_buznikov@mail.ru; Antonov, A.S. [Institute for Theoretical and Applied Electrodynamics, Russian Academy of Sciences, Moscow 125412 (Russian Federation); Granovsky, A.B. [Faculty of Physics, M.V. Lomonosov Moscow State University, Moscow 119992 (Russian Federation); Kim, C.G. [Research Center for Advanced Magnetic Materials, Chungnam National University, Daeduk Science Town, Daejeon 305-764 (Korea, Republic of)]. E-mail: cgkim@cnu.ac.kr; Kim, C.O. [Research Center for Advanced Magnetic Materials, Chungnam National University, Daeduk Science Town, Daejeon 305-764 (Korea, Republic of); Li, X.P. [Department of Mechanical Engineering and Division of Bioengineering, National University of Singapore, Singapore 119260 (Singapore); Yoon, S.S. [Research Center for Advanced Magnetic Materials, Chungnam National University, Daeduk Science Town, Daejeon 305-764 (Korea, Republic of); Department of Physics, Andong National University, Andong 760-749 (Korea, Republic of)

    2006-01-15

    The giant magnetoimpedance effect in composite wires consisting of a non-magnetic inner core and soft magnetic shell is studied theoretically. It is assumed that the magnetic shell has a helical anisotropy. The current and field distributions in the composite wire are found by means of a simultaneous solution of Maxwell equations and the Landau-Lifshitz equation. The expressions for the diagonal and off-diagonal impedance are obtained for low and high frequencies. The dependences of the impedance on the anisotropy axis angle and the shell thickness are analyzed. Maximum field sensitivity is shown to correspond to the case of the circular anisotropy in the magnetic shell. It is demonstrated that the optimum shell thickness to obtain maximum impedance ratio is equal to the effective skin depth in the magnetic material.

  18. Soft x-ray resonant diffraction study of magnetic structure in magnetoelectric Y-type hexaferrite

    Science.gov (United States)

    Ueda, H.; Tanaka, Y.; Wakabayashi, Y.; Kimura, T.

    2018-05-01

    The effect of magnetic field on the magnetic structure associated with magnetoelectric properties in a Y-type hexaferrite, Ba1.3Sr0.7CoZnFe11AlO22, was investigated by utilizing the soft x-ray resonant diffraction technique. In this hexaferrite, the so-called alternating longitudinal conical phase is stabilized at room temperature and zero magnetic field. Below room temperature, however, this phase is transformed into the so-called transverse conical phase by applying an in-plane magnetic field (≈ 0.3 T). The transverse conical phase persists even after removing the magnetic field. The magnetoelectricity, which is magnetically-induced electric polarization, observed in the hexaferrite is discussed in terms of the temperature-dependent magnetic structure at zero field.

  19. Advanced Nanostructured Magnetic Materials

    National Research Council Canada - National Science Library

    Sellmyer, David J

    2004-01-01

    ... out. Novel physical systems have been synthesized and studied including: hard/soft nanocomposites, magnetic nanowires, thermally processed multilayer films, and nanoparticle-assembled composites...

  20. Soft X-ray magnetic circular dichroism study of UFe2

    International Nuclear Information System (INIS)

    Okane, T.; Takeda, Y.; Fujimori, S.-I.; Terai, K.; Saitoh, Y.; Muramatsu, Y.; Fujimori, A.; Haga, Y.; Yamamoto, E.; Onuki, Y.

    2006-01-01

    Soft X-ray magnetic circular dichroism has been measured at the U N 4,5 and Fe L 2,3 absorption edges of ferromagnetic UFe 2 . The orbital and spin magnetic moments of U 5f and Fe 3d electrons are evaluated by a sum-rule analysis of the XMCD data. It is confirmed that the U 5f orbital moment is parallel to the Fe 3d spin moment

  1. Small angle neutron scattering investigations of spin disorder in nanocomposite soft magnets

    International Nuclear Information System (INIS)

    Vecchini, C.; Moze, O.; Suzuki, K.; Cadogan, J.M.; Pranzas, K.; Michels, A.; Weissmueller, J.

    2006-01-01

    The technique of SANS (small angle neutron scattering) furnishes unique information on the characteristic magnetic length scales and local magnetic anisotropies at the nanoscale in nanocomposite ferromagnets. Such information is not presently available using any other microscopic technique. The basic principles and results of the technique will be presented with regard to a unique and unexpected observation of a dipole field controlled spin disorder in a prototypical soft nanocomposite ferromagnet of the Nanoperm type

  2. Composite quarks and their magnetic moments

    International Nuclear Information System (INIS)

    Parthasarathy, R.

    1980-08-01

    A composite quark model based on the symmetry group SU(10)sub(flavour) x SU(10)sub(colour) with the assumption of mass non-degenerate sub-quarks is considered. Magnetic moments of quarks and sub-quarks are obtained from the observed nucleon magnetic moments. Using these quark and sub-quark magnetic moments, a satisfactory agreement for the radiative decays of vector mesons (rho,ω) is obtained. The ratio of the masses of the sub-quarks constituting the u,d,s quarks are found to be Msub(p)/Msub(n) = 0.3953 and Msub(p)/Msub(lambda) = 0.596, indicating a mass hierarchy Msub(p) < Msub(n) < Msub(lambda) for the sub-quarks. (author)

  3. Ultra-soft magnetic Co-Fe-B-Si-Nb amorphous alloys for high frequency power applications

    Science.gov (United States)

    Ackland, Karl; Masood, Ansar; Kulkarni, Santosh; Stamenov, Plamen

    2018-05-01

    With the continuous shrinkage of the footprint of inductors and transformers in modern power supplies, higher flux, while still low-loss metallic replacements of traditional ferrite materials are becoming an intriguing alternative. One candidate replacement strategy is based on amorphous CoFeBSi soft-magnetic alloys, in their metallic glass form. Here the structural and magnetic properties of two different families of CoFeBSi-based soft magnetic alloys, prepared by arc-melting and subsequent melt spinning (rapid quenching) are presented, targeting potential applications at effective frequencies of 100 kHz and beyond. The nominal alloy compositions are Co67Fe4B11Si16Mo2 representing commercial Vitrovac and Co72-xFexB28-y (where B includes non-magnetic elements such as Boron, Silicon etc. x varies between 4 and 5 % and y is varied from 0 to 2 %) denoted Alloy #1 and prepared as a possible higher performance alternative, i.e. lower power loss and lower coercivity, to commercial Vitrovac. Room temperature magnetization measurements of the arc-melted alloys reveal that compared to Vitrovac, Alloy #1 already presents a ten-fold decrease in coercivity, with Hc ˜ 1.4 Am-1 and highest figure of merit of (Ms/Hc > 96). Upon melt-spinning the alloys into thin (< 30 μm) ribbons, the alloys are essentially amorphous when analyzed by XRD. Magnetization measurements of the melt-spun ribbons demonstrate that Alloy #1 possesses a coercivity of just 2 Am-1, which represents a significant improvement compared to melt-spun ribbons of Vitrovac (17 Am-1). A set of prototype transformers of approximately 10 turns of Alloy #1 ribbon exhibits systematically Hc < 10 Am-1 at 100 kHz, without a noticeable decrease in coupled flux and saturation.

  4. Single-step gas phase synthesis of stable iron aluminide nanoparticles with soft magnetic properties

    Energy Technology Data Exchange (ETDEWEB)

    Vernieres, Jerome, E-mail: Jerome.vernieres@oist.jp; Benelmekki, Maria; Kim, Jeong-Hwan; Grammatikopoulos, Panagiotis; Diaz, Rosa E. [Nanoparticles by Design Unit, Okinawa Institute of Science and Technology (OIST) Graduate University, 1919-1 Tancha, Onna Son, Okinawa 904-0495 (Japan); Bobo, Jean-François [Centre d’Elaboration de Materiaux et d’Etudes Structurales (CEMES), 29 rue Jeanne Marvig, 31055 Toulouse Cedex 4 (France); Sowwan, Mukhles, E-mail: Mukhles@oist.jp [Nanoparticles by Design Unit, Okinawa Institute of Science and Technology (OIST) Graduate University, 1919-1 Tancha, Onna Son, Okinawa 904-0495 (Japan); Nanotechnology Research Laboratory, Al-Quds University, P.O. Box 51000, East Jerusalem, Palestine (Country Unknown)

    2014-11-01

    Soft magnetic alloys at the nanoscale level have long generated a vivid interest as candidate materials for technological and biomedical purposes. Consequently, controlling the structure of bimetallic nanoparticles in order to optimize their magnetic properties, such as high magnetization and low coercivity, can significantly boost their potential for related applications. However, traditional synthesis methods stumble upon the long standing challenge of developing true nanoalloys with effective control over morphology and stability against oxidation. Herein, we report on a single-step approach to the gas phase synthesis of soft magnetic bimetallic iron aluminide nanoparticles, using a versatile co-sputter inert gas condensation technique. This method allowed for precise morphological control of the particles; they consisted of an alloy iron aluminide crystalline core (DO{sub 3} phase) and an alumina shell, which reduced inter-particle interactions and also prevented further oxidation and segregation of the bimetallic core. Remarkably, the as-deposited alloy nanoparticles show interesting soft magnetic properties, in that they combine a high saturation magnetization (170 emu/g) and low coercivity (less than 20 Oe) at room temperature. Additional functionality is tenable by modifying the surface of the particles with a polymer, to ensure their good colloidal dispersion in aqueous environments.

  5. Structure and soft magnetic properties of sputter deposited MnZn-ferrite films

    NARCIS (Netherlands)

    Gillies, M.F.; Coehoorn, R.; van Zon, J.B.A.D.; Alders, D.

    1998-01-01

    In this paper we report the soft magnetic properties of thin films of sputtered MnZn ferrite deposited on thermally oxidized Si substrates. A high deposition temperature, 600¿°C, together with the addition of water vapor to the sputtering gas was found to improve the initial ac permeability, µ. The

  6. Influence of stresses and magnetostriction on the soft magnetic behavior of metallic films

    NARCIS (Netherlands)

    Chezan, AR; Craus, CB; Chechenin, NG; Vystavel, T; Niesen, L; De Hosson, JTM; Boerma, DO

    Nanocrystalline soft magnetic Fe-Zr-N films have been successfully deposited by DC magnetron reactive sputtering. For thick films (>200 nm), the compressive stress in the as-deposited films and the positive matgnetostriction produce perpendicular anisotropy. The magnitude of this effect is smaller

  7. Computerized J-H loop tracer for soft magnetic thick films in the audio frequency range

    Directory of Open Access Journals (Sweden)

    Loizos G.

    2014-07-01

    Full Text Available A computerized J-H loop tracer for soft magnetic thick films in the audio frequency range is described. It is a system built on a PXI platform combining PXI modules for control signal generation and data acquisition. The physiscal signals are digitized and the respective data strems are processed, presented and recorded in LabVIEW 7.0.

  8. Structural Changes in Deformed Soft Magnetic Ni-Based Metallic Glass

    NARCIS (Netherlands)

    Jurikova, A.; Csach, K.; Miskuf, J.; Ocelik, V.

    The effects of intensive plastic deformation of the soft magnetic metallic glass Ni Si 13 on the structural relaxation were examined. The enthalpy changes studied by differential scanning calorimetry revealed that the intensive plastic deformation was associated with the partial structural

  9. Effect of thickness on structure, microstructure, residual stress and soft magnetic properties of DC sputtered Fe65Co35 soft magnetic thin films

    International Nuclear Information System (INIS)

    Prasanna Kumari, T.; Manivel Raja, M.; Kumar, Atul; Srinath, S.; Kamat, S.V.

    2014-01-01

    The effect of film thickness on structure, microstructure, residual stress and soft magnetic properties of Fe 65 Co 35 thin films deposited on Si(001) and MgO(001) substrates was investigated by varying film thickness from 30 to 600 nm. X-ray diffraction studies showed that the FeCo films are polycrystalline in the as-deposited condition irrespective of deposition on Si or MgO substrate. The microstructure of films consisted of spherical grains for 30 nm film thickness and columnar grains for all other film thicknesses. The grain size for the films was found to increase from 15 to 50 nm with increasing film thickness. The sputtered films also exhibited tensile residual stresses with the magnitude of stress decreasing with increasing film thickness. The Fe 65 Co 35 films deposited on both substrates also exhibited very good in-plane soft magnetic properties with a saturation magnetization 4πM s of ∼23.6–23.8 kG and coercivity of ∼27–30 Oe without any under-layer only for films with thickness of 30 nm. For all other thicknesses, these films exhibited a significantly higher coercivity. The observed variations in soft magnetic properties with film thickness were explained in terms of residual stress and microstructure of the films. - Highlights: • Spherical grain morphology transformed to columnar above 30 nm film thickness. • Sputtered films exhibited tensile residual stresses decreasing with film thickness. • An in-plane coercivity of ∼27–30 Oe was achieved without any under-layer

  10. Soft and flexible conductive PDMS/MWCNT composites

    DEFF Research Database (Denmark)

    Hassouneh, Suzan Sager; Yu, Liyun; Skov, Anne Ladegaard

    2017-01-01

    (trifluoromethanesulfonyl)imide, was used to pre-disperse MWCNT in a MWCNT/IL-gel that was used for preparation of MWCVNT/PDMS composites. The method was seen to be effective at low levels of MWCNT, but required combination with a roll mill to obtain a stable dispersion at 4 wt % MWCNT. With higher amounts of MWCNT a reduction...... for preparation of MWCNT/PDMS composites. Composites prepared by use of the IL dispersion method, use of a roll mill or by use of the f-MWCNT all had conductivities around 0.005–0.01 s/cm and retained conductivity upon extension....

  11. Magnetic resonance tomography in skeletal and soft tissue traumas

    International Nuclear Information System (INIS)

    Stiris, Morten G.

    2000-01-01

    MRI has revolutionised the diagnostic yield in musculo-skeletal trauma. Studies have documented that MRI can be an accurate, cost-effective means of assessing injuries in the knee, the foot and the ankle and it may also be cost-effective in other anatomic locations. MRTI may have a significant impact on decision-making in relation to these patients and on the follow-up. The patient does not need to be moved for evaluation in all the anatomical planes. Each study can also be post-processes if necessary. MRI may be used in patients with fractures for evaluation of complications. The fracture lines as well as accompanying soft tissue damage are well documented

  12. Magnetic imaging with full-field soft X-ray microscopies

    International Nuclear Information System (INIS)

    Fischer, Peter; Im, Mi-Young; Baldasseroni, Chloe; Bordel, Catherine; Hellman, Frances; Lee, Jong-Soo; Fadley, Charles S.

    2013-01-01

    Progress toward a fundamental understanding of magnetism continues to be of great scientific interest and high technological relevance. To control magnetization on the nanoscale, external magnetic fields and spin polarized currents are commonly used. In addition, novel concepts based on spin manipulation by electric fields or photons are emerging which benefit from advances in tailoring complex magnetic materials. Although the nanoscale is at the very origin of magnetic behavior, there is a new trend toward investigating mesoscale magnetic phenomena, thus adding complexity and functionality, both of which will become crucial for future magnetic devices. Advanced analytical tools are thus needed for the characterization of magnetic properties spanning the nano- to the meso-scale. Imaging magnetic structures with high spatial and temporal resolution over a large field of view and in three dimensions is therefore a key challenge. A variety of spectromicroscopic techniques address this challenge by taking advantage of variable-polarization soft X-rays, thus enabling X-ray dichroism effects provide magnetic contrast. These techniques are also capable of quantifying in an element-, valence- and site-sensitive way the basic properties of ferro(i)- and antiferro-magnetic systems, such as spin and orbital moments, spin configurations from the nano- to the meso-scale and spin dynamics with sub-ns time resolution. This paper reviews current achievements and outlines future trends with one of these spectromicroscopies, magnetic full field transmission soft X-ray microscopy (MTXM) using a few selected examples of recent research on nano- and meso-scale magnetic phenomena. The complementarity of MTXM to X-ray photoemission electron microscopy (X-PEEM) is also emphasized

  13. Magnetic imaging with full-field soft X-ray microscopies

    Energy Technology Data Exchange (ETDEWEB)

    Fischer, Peter, E-mail: PJFischer@lbl.gov [Center for X-ray Optics, Lawrence Berkeley National Laboratory, 1 Cyclotron Road, Berkeley, CA 94720 (United States); Im, Mi-Young [Center for X-ray Optics, Lawrence Berkeley National Laboratory, 1 Cyclotron Road, Berkeley, CA 94720 (United States); Baldasseroni, Chloe [Department of Materials Science and Engineering, University of California Berkeley, Berkeley, CA 94720 (United States); Bordel, Catherine; Hellman, Frances [Department of Physics, University of California Berkeley, Berkeley, CA 94720 (United States); Material Sciences Division, Lawrence Berkeley National Laboratory, Berkeley, CA 94270 (United States); Lee, Jong-Soo [Department of Energy Systems Engineering, Daegu Gyeongbuk Institute of Science and Technology (DGIST), Daegu 711-873 (Korea, Republic of); Fadley, Charles S. [Department of Physics, University of California Davis, Davis, CA 95616 (United States); Material Sciences Division, Lawrence Berkeley National Laboratory, Berkeley, CA 94270 (United States)

    2013-08-15

    Progress toward a fundamental understanding of magnetism continues to be of great scientific interest and high technological relevance. To control magnetization on the nanoscale, external magnetic fields and spin polarized currents are commonly used. In addition, novel concepts based on spin manipulation by electric fields or photons are emerging which benefit from advances in tailoring complex magnetic materials. Although the nanoscale is at the very origin of magnetic behavior, there is a new trend toward investigating mesoscale magnetic phenomena, thus adding complexity and functionality, both of which will become crucial for future magnetic devices. Advanced analytical tools are thus needed for the characterization of magnetic properties spanning the nano- to the meso-scale. Imaging magnetic structures with high spatial and temporal resolution over a large field of view and in three dimensions is therefore a key challenge. A variety of spectromicroscopic techniques address this challenge by taking advantage of variable-polarization soft X-rays, thus enabling X-ray dichroism effects provide magnetic contrast. These techniques are also capable of quantifying in an element-, valence- and site-sensitive way the basic properties of ferro(i)- and antiferro-magnetic systems, such as spin and orbital moments, spin configurations from the nano- to the meso-scale and spin dynamics with sub-ns time resolution. This paper reviews current achievements and outlines future trends with one of these spectromicroscopies, magnetic full field transmission soft X-ray microscopy (MTXM) using a few selected examples of recent research on nano- and meso-scale magnetic phenomena. The complementarity of MTXM to X-ray photoemission electron microscopy (X-PEEM) is also emphasized.

  14. Soft Magnetic Properties of High-Entropy Fe-Co-Ni-Cr-Al-Si Thin Films

    Directory of Open Access Journals (Sweden)

    Pei-Chung Lin

    2016-08-01

    Full Text Available Soft magnetic properties of Fe-Co-Ni-Al-Cr-Si thin films were studied. As-deposited Fe-Co-Ni-Al-Cr-Si nano-grained thin films showing no magnetic anisotropy were subjected to field-annealing at different temperatures to induce magnetic anisotropy. Optimized magnetic and electrical properties of Fe-Co-Ni-Al-Cr-Si films annealed at 200 °C are saturation magnetization 9.13 × 105 A/m, coercivity 79.6 A/m, out-of-plane uniaxial anisotropy field 1.59 × 103 A/m, and electrical resistivity 3.75 μΩ·m. Based on these excellent properties, we employed such films to fabricate magnetic thin film inductor. The performance of the high entropy alloy thin film inductors is superior to that of air core inductor.

  15. Thick film magnetic nanoparticulate composites and method of manufacture thereof

    Science.gov (United States)

    Ma, Xinqing (Inventor); Zhang, Yide (Inventor); Ge, Shihui (Inventor); Zhang, Zongtao (Inventor); Yan, Dajing (Inventor); Xiao, Danny T. (Inventor)

    2009-01-01

    Thick film magnetic/insulating nanocomposite materials, with significantly reduced core loss, and their manufacture are described. The insulator coated magnetic nanocomposite comprises one or more magnetic components, and an insulating component. The magnetic component comprises nanometer scale particles (about 1 to about 100 nanometers) coated by a thin-layered insulating phase. While the intergrain interaction between the immediate neighboring magnetic nanoparticles separated by the insulating phase provides the desired soft magnetic properties, the insulating material provides high resistivity, which reduces eddy current loss.

  16. How to obtain a magnetic hard-soft architecture by pulsed laser deposition

    International Nuclear Information System (INIS)

    Fix, T; Trassin, M; Hassan, R Sayed; Schmerber, G; Viart, N; Meny, C; Colis, S; Dinia, A

    2007-01-01

    In spin valve type systems, one ferromagnetic electrode must be magnetically hard to act as a reference layer while the other electrode must be magnetically soft to act as a sensor or storage layer. This magnetic hard-soft architecture can usually be obtained by four different methods: the use of two ferromagnets with different coercive fields (here CoFe 2 and Ni 80 Fe 20 ), the use of an underlayer enhancing the coercive field of one of the two ferromagnets (here Ta and Ru), the use of a ferromagnet coupled to a ferrimagnet or antiferromagnet (here NiO/CoFe 2 and CoFe 2 O 4 /CoFe 2 ), or the use of an artificial antiferromagnet (here CoFe 2 /Ru/CoFe 2 ). We show that at least the first and the third methods seem to work with pulsed laser deposition in the thermodynamic conditions used

  17. Soft magnetism, magnetostriction, and microwave properties of FeGaB thin films

    International Nuclear Information System (INIS)

    Lou, J.; Insignares, R. E.; Cai, Z.; Ziemer, K. S.; Liu, M.; Sun, N. X.

    2007-01-01

    A series of (Fe 100-y Ga y ) 1-x B x (x=0-21 and y=9-17) films were deposited; their microstructure, soft magnetism, magnetostrictive behavior, and microwave properties were investigated. The addition of B changes the FeGaB films from polycrystalline to amorphous phase and leads to excellent magnetic softness with coercivity s , self-biased ferromagnetic resonance (FMR) frequency of 1.85 GHz, narrow FMR linewidth (X band) of 16-20 Oe, and a high saturation magnetostriction constant of 70 ppm. The combination of these properties makes the FeGaB films potential candidates for tunable magnetoelectric microwave devices and other rf/microwave magnetic device applications

  18. Statistical analysis of magnetically soft particles in magnetorheological elastomers

    Science.gov (United States)

    Gundermann, T.; Cremer, P.; Löwen, H.; Menzel, A. M.; Odenbach, S.

    2017-04-01

    The physical properties of magnetorheological elastomers (MRE) are a complex issue and can be influenced and controlled in many ways, e.g. by applying a magnetic field, by external mechanical stimuli, or by an electric potential. In general, the response of MRE materials to these stimuli is crucially dependent on the distribution of the magnetic particles inside the elastomer. Specific knowledge of the interactions between particles or particle clusters is of high relevance for understanding the macroscopic rheological properties and provides an important input for theoretical calculations. In order to gain a better insight into the correlation between the macroscopic effects and microstructure and to generate a database for theoretical analysis, x-ray micro-computed tomography (X-μCT) investigations as a base for a statistical analysis of the particle configurations were carried out. Different MREs with quantities of 2-15 wt% (0.27-2.3 vol%) of iron powder and different allocations of the particles inside the matrix were prepared. The X-μCT results were edited by an image processing software regarding the geometrical properties of the particles with and without the influence of an external magnetic field. Pair correlation functions for the positions of the particles inside the elastomer were calculated to statistically characterize the distributions of the particles in the samples.

  19. Study on soft magnetic properties of Finemet-type nanocrystalline alloys with Mo substituting for Nb

    Energy Technology Data Exchange (ETDEWEB)

    Jiang, Dehui; Zhou, Bingwen; Jiang, Boyu; Ya, Bin; Zhang, Xingguo [School of Materials Science and Engineering, Dalian University of Technology, Dalian (China)

    2017-10-15

    The thermal stability, microstructure, and soft magnetic properties as a function of annealing time were studied for Fe{sub 73.5}Si{sub 13.5}B{sub 9}Cu{sub 1}Nb{sub 3-x}Mo{sub x} (x = 0, 1, 2, 3) (atom percent, at.%,) ribbons. It was found that substituting Nb by Mo reduced the thermal stability. After 15 min short time vacuum annealing, Fe{sub 73.5}Si{sub 13.5}B{sub 9}Cu{sub 1}Nb{sub 2}Mo{sub 1} and Fe{sub 73.5}Si{sub 13.5}B{sub 9}Cu{sub 1}Nb{sub 1}Mo{sub 2} samples obtained higher permeability and similar coercivity compared to the original Finemet alloy (Fe{sub 73.5}Si{sub 13.5}B{sub 9}Cu{sub 1}Nb{sub 3}), Mo substituting Nb reduced the optimum annealing time in Finemet-type alloys, and meanwhile marginally increased the saturation magnetization. Substituting all Nb by Mo led to the earlier formation of non-soft magnetic phase, thus deteriorated the soft magnetic properties. XRD and TEM structural analysis showed that in Fe{sub 73.5}Si{sub 13.5}B{sub 9}Cu{sub 1}Nb{sub 2}Mo{sub 1} and Fe{sub 73.5}Si{sub 13.5}B{sub 9}Cu{sub 1}Nb{sub 1}Mo{sub 2} samples (annealed for 15 min), nanocrystals ∝10 nm in size were obtained, and the good soft magnetic properties of these alloys could be attributed to the small grain size. The relationship between annealing time, soft magnetic properties, and microstructure was established. Reducing annealing time and temperature to obtain best soft magnetic properties could cut down the production costs of Finemet-type alloys. (copyright 2017 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim)

  20. Computed Tomography and Magnetic Resonance Imaging of Myoepitheliloma in the Soft Palate: A Case Report

    International Nuclear Information System (INIS)

    Lim, Hun Cheol; Yu, In Kyu; Park, Mi Ja; Jang, Dong Sik

    2011-01-01

    We report the appearance of myoepithelioma arising from minor salivary glands in the soft palate observed on computed tomography (CT) and magnetic resonance imaging (MRI). CT, the tumor was round with a smooth and partial lobulating contour, and slightly marginal contrast enhancement. On T1-weighted images, the mass had heterogeneous iso-signal intensity compared to the pharyngeal muscle. Additionally, the tumor had heterogeneously high T2 signal intensity with heterogeneously strong enhancement on the Gd-enhanced T1-weighted image. Radiologists should consider myoepithelioma in the radiological differential diagnosis of soft palate tumors.

  1. Soft magnetic properties of bulk amorphous Co-based samples

    International Nuclear Information System (INIS)

    Fuezer, J.; Bednarcik, J.; Kollar, P.

    2006-01-01

    Ball milling of melt-spun ribbons and subsequent compaction of the resulting powders in the supercooled liquid region were used to prepare disc shaped bulk amorphous Co-based samples. The several bulk samples have been prepared by hot compaction with subsequent heat treatment (500 deg C - 575 deg C). The influence of the consolidation temperature and follow-up heat treatment on the magnetic properties of bulk samples was investigated. The final heat treatment leads to decrease of the coercivity to the value between the 7.5 to 9 A/m (Authors)

  2. Preparation and properties of Cobalt-based soft magnetic material prepared by novel powder metallurgy

    Energy Technology Data Exchange (ETDEWEB)

    Srivastava, Yogesh, E-mail: 123209001_yogesh@manit.ac.in; Srivastava, Sanjay

    2017-02-01

    The present work deals with the development of nanocrystalline 60Co–26Fe–14Al (wt%) soft magnetic materials via mechanical milling of elemental powders. The evolution of solid solution during milling proceeded with continuous decrease in atomic order and the crystallite size, and an introduction of internal strain and dislocations. The milling-induced lattice defects, crystallite size reduction, and atomic disorder exhibited a decrease in saturation magnetization, remanence magnetization, squareness ratio, and blocking temperature with increasing milling time. It has been demonstrated that, at subzero temperatures, the magnetization decreases with increasing temperature due to the development of an effective anisotropy caused by an evolution of canted spin structure owing to the introduction of lattice defects during milling. - Highlights: • Co-based HA have been fabricated by mechanical alloying. • The effect of milling time was investigated. • The saturation magnetization can be reached up to 140.79 emu/g.

  3. FEM analysis of magnetic flake composites

    Science.gov (United States)

    Claassen, J. H.

    2009-07-01

    A composite comprised of layered flake-like magnetic particles embedded in an insulating medium has been proposed as a low permeability, low loss core material. This would be an alternative to "distributed air gap" compressed powder cores that are widely used for inductors in power applications. Since the lowest loss metallic materials are manufactured in the form of very thin sheets, the particles after pulverizing would be in the form of flakes. The effective permeability and average core loss have been computed for model systems of flake composites in a two-dimensional approximation. The core loss is modeled by eddy current dissipation in the low-frequency limit, where the conductor thickness is much less than the skin depth. It is found that useful values of permeability should be obtained for a modest filling fraction of magnetic material, in contrast to the powder cores which require a value close to unity. The core loss will scale as the inverse of filling fraction, with a small additional enhancement due to perpendicular field components. It is thus expected that useful core materials may be attainable without the necessity of large compaction forces.

  4. Soft x-ray resonant magnetic powder diffraction on PrNiO{sub 3}

    Energy Technology Data Exchange (ETDEWEB)

    Staub, U [Swiss Light Source, Paul Scherrer Institut, CH-5232 Villigen PSI (Switzerland); GarcIa-Fernandez, M [Swiss Light Source, Paul Scherrer Institut, CH-5232 Villigen PSI (Switzerland); Mulders, A M [Department of Applied Physics, Curtin University of Technology, GPO Box U1987, Perth WA 6845 (Australia); Bodenthin, Y [Swiss Light Source, Paul Scherrer Institut, CH-5232 Villigen PSI (Switzerland); MartInez-Lope, M J [Instituto de Ciencia de Materiales de Madrid, CSIC, Cantoblanco, E-28049 Madrid (Spain); Alonso, J A [Instituto de Ciencia de Materiales de Madrid, CSIC, Cantoblanco, E-28049 Madrid (Spain)

    2007-03-07

    We report on the first soft x-ray resonant powder diffraction experiments performed at the Ni L{sub 2,3} edges of PrNiO{sub 3}. The temperature, polarization and energy dependence of the (1/2 0 1/2) reflection indicates a magnetic origin for the signal. This experiment demonstrates that x-ray resonant magnetic powder diffraction can be relatively easily performed in the soft x-ray regime due to the very large enhancement factors at the absorption edges. Such experiments allow us to extract important information on the electronic states of the d shell. Similar results can be anticipated from orbital reflections measured in a powder. (fast track communication)

  5. Magnetic resonance imaging of local soft tissue inflammation using gadolinium-DTPA

    International Nuclear Information System (INIS)

    Paajanen, H.; Brasch, R.C.; Schmiedl, U.; Ogan, M.

    1987-01-01

    Chemical inflammation was induced subcutaneously in 10 rats using carrageenan mucopolysaccharide. Dual spin echo (SE) imaging of inflammatory loci was performed employing a 0.35 tesla resistive magnet. In addition, gadolinium-DTPA was administrated intravenously into 5 rats to evaluate the potential benefits of paramagnetic contrast medium for the detection and characterization of inflammatory loci. T2 weighted SE images demonstrated the edematous lesions as zones of high intensity. This was attributed to the increased relaxation times of lesions when compared to the adjacent soft tissue. The inflammation was also delineated on T1 weighted SE images, but only after injection of paramagnetic Gd-DTPA. Carrageenan mucopolysaccharide-induced lesions provide a useful experimental model for in viva evaluation of soft tissue inflammation using magnetic resonance imaging. No special benefit of paramagnetic contrast enhancement was demonstrated in this model of local edema. (orig.)

  6. Hard and soft supersymmetry breaking for ‘graphinos’ in uniform magnetic fields

    International Nuclear Information System (INIS)

    Hernández-Ortíz, S; Raya, A; Murguía, G

    2012-01-01

    Using irreducible and reducible representations of the Dirac matrices, we study the two- and four-component quantum mechanical supersymmetric (SUSY) theories for ultrarelativistic fermions in (2 + 1) dimensions (‘graphinos’) in a background uniform magnetic field perpendicular to their plane of motion. We then consider ordinary and parity-violating mass terms and identify the former as a soft SUSY breaking term and the latter as the hard SUSY breaking one. (paper)

  7. Axial Magneto-Inductive Effect in Soft Magnetic Microfibers, Test Methodology, and Experiments

    Science.gov (United States)

    2016-03-24

    Nickle nT Nano- Tesla Si Silicon V Volts w Exchange Energy W Watts Zm Coil Impedance, measured  Circumferential Field Direction T Micro... Tesla  Ratio of Coil Length to Diameter  Ohm ° Degrees 1 (2 blank) 1. INTRODUCTION Magneto-induction (MI) effects in soft...axial magnetic field is utilized to excite the fiber. Previous investigators have demonstrated this effect with small coils applied directly to the

  8. Fabrication of a solenoid-type inductor with Fe-based soft magnetic core

    International Nuclear Information System (INIS)

    Lei Chong; Zhou Yong; Gao Xiaoyu; Ding Wen; Cao Ying; Choi, Hyung; Won, Jonghwa

    2007-01-01

    A solenoid-type inductor was fabricated by MEMS (Microelectromechanical systems) technique. The fabrication process uses UV-LIGA, dry etching, fine polishing, and electroplating technique to achieve high performance of the solenoid-type inductor. Fe-based soft magnetic thin film was sputtered as the magnetic core, and polyimide was used as the insulation materials. The inductor was in size of 4x4 mm with coil width of 20 μm and space of 35 μm. The inductance is 1.61 μH at a frequency of 5 MHz with the maximum quality factor of 1.42

  9. Contactless remote induction of shear waves in soft tissues using a transcranial magnetic stimulation device

    International Nuclear Information System (INIS)

    Grasland-Mongrain, Pol; Miller-Jolicoeur, Erika; Cloutier, Guy; Tang, An; Catheline, Stefan

    2016-01-01

    This study presents the first observation of shear waves induced remotely within soft tissues. It was performed through the combination of a transcranial magnetic stimulation device and a permanent magnet. A physical model based on Maxwell and Navier equations was developed. Experiments were performed on a cryogel phantom and a chicken breast sample. Using an ultrafast ultrasound scanner, shear waves of respective amplitudes of 5 and 0.5 μm were observed. Experimental and numerical results were in good agreement. This study constitutes the framework of an alternative shear wave elastography method. (paper)

  10. Contactless remote induction of shear waves in soft tissues using a transcranial magnetic stimulation device

    Science.gov (United States)

    Grasland-Mongrain, Pol; Miller-Jolicoeur, Erika; Tang, An; Catheline, Stefan; Cloutier, Guy

    2016-03-01

    This study presents the first observation of shear waves induced remotely within soft tissues. It was performed through the combination of a transcranial magnetic stimulation device and a permanent magnet. A physical model based on Maxwell and Navier equations was developed. Experiments were performed on a cryogel phantom and a chicken breast sample. Using an ultrafast ultrasound scanner, shear waves of respective amplitudes of 5 and 0.5 μm were observed. Experimental and numerical results were in good agreement. This study constitutes the framework of an alternative shear wave elastography method.

  11. Design Methodology for Magnetic Field-Based Soft Tri-Axis Tactile Sensors.

    Science.gov (United States)

    Wang, Hongbo; de Boer, Greg; Kow, Junwai; Alazmani, Ali; Ghajari, Mazdak; Hewson, Robert; Culmer, Peter

    2016-08-24

    Tactile sensors are essential if robots are to safely interact with the external world and to dexterously manipulate objects. Current tactile sensors have limitations restricting their use, notably being too fragile or having limited performance. Magnetic field-based soft tactile sensors offer a potential improvement, being durable, low cost, accurate and high bandwidth, but they are relatively undeveloped because of the complexities involved in design and calibration. This paper presents a general design methodology for magnetic field-based three-axis soft tactile sensors, enabling researchers to easily develop specific tactile sensors for a variety of applications. All aspects (design, fabrication, calibration and evaluation) of the development of tri-axis soft tactile sensors are presented and discussed. A moving least square approach is used to decouple and convert the magnetic field signal to force output to eliminate non-linearity and cross-talk effects. A case study of a tactile sensor prototype, MagOne, was developed. This achieved a resolution of 1.42 mN in normal force measurement (0.71 mN in shear force), good output repeatability and has a maximum hysteresis error of 3.4%. These results outperform comparable sensors reported previously, highlighting the efficacy of our methodology for sensor design.

  12. Modeling of magnetic hystereses in soft MREs filled with NdFeB particles

    Science.gov (United States)

    Kalina, K. A.; Brummund, J.; Metsch, P.; Kästner, M.; Borin, D. Yu; Linke, J. M.; Odenbach, S.

    2017-10-01

    Herein, we investigate the structure-property relationships of soft magnetorheological elastomers (MREs) filled with remanently magnetizable particles. The study is motivated from experimental results which indicate a large difference between the magnetization loops of soft MREs filled with NdFeB particles and the loops of such particles embedded in a comparatively stiff matrix, e.g. an epoxy resin. We present a microscale model for MREs based on a general continuum formulation of the magnetomechanical boundary value problem which is valid for finite strains. In particular, we develop an energetically consistent constitutive model for the hysteretic magnetization behavior of the magnetically hard particles. The microstructure is discretized and the problem is solved numerically in terms of a coupled nonlinear finite element approach. Since the local magnetic and mechanical fields are resolved explicitly inside the heterogeneous microstructure of the MRE, our model also accounts for interactions of particles close to each other. In order to connect the microscopic fields to effective macroscopic quantities of the MRE, a suitable computational homogenization scheme is used. Based on this modeling approach, it is demonstrated that the observable macroscopic behavior of the considered MREs results from the rotation of the embedded particles. Furthermore, the performed numerical simulations indicate that the reversion of the sample’s magnetization occurs due to a combination of particle rotations and internal domain conversion processes. All of our simulation results obtained for such materials are in a good qualitative agreement with the experiments.

  13. Soft X-ray microscopy to 25 nm with applications to biology and magnetic materials

    CERN Document Server

    Denbeaux, G; Chao, W; Eimueller, T; Johnson, L; Köhler, M; Larabell, C; Legros, M; Fischer, P; Pearson, A; Schuetz, G; Yager, D; Attwood, D

    2001-01-01

    We report both technical advances in soft X-ray microscopy (XRM) and applications furthered by these advances. With new zone plate lenses we record test pattern features with good modulation to 25 nm and smaller. In combination with fast cryofixation, sub-cellular images show very fine detail previously seen only in electron microscopy, but seen here in thick, hydrated, and unstained samples. The magnetic domain structure is studied at high spatial resolution with X-ray magnetic circular dichroism (X-MCD) as a huge element-specific magnetic contrast mechanism, occurring e.g. at the L sub 2 sub , sub 3 edges of transition metals. It can be used to distinguish between in-plane and out-of-plane contributions by tilting the sample. As XRM is a photon based technique, the magnetic images can be obtained in unlimited varying external magnetic fields. The images discussed have been obtained at the XM-1 soft X-ray microscope on beamline 6.1 at the Advanced Light Source in Berkeley.

  14. Synthesis, nanostructure and magnetic properties of FeCo-reduced graphene oxide composite films by one-step electrodeposition

    International Nuclear Information System (INIS)

    Cao, Derang; Li, Hao; Wang, Zhenkun; Wei, Jinwu; Wang, Jianbo; Liu, Qingfang

    2015-01-01

    FeCo-reduced graphene oxide (FeCo-RGO) composite film was fabricated on indium tin oxide substrate using one-step electrodeposition method. Raman spectroscopy and field emission scanning electron microscope results show that the reduced graphene oxide is coprecipitated with the FeCo film. The energy-dispersive spectrometer results demonstrate that the atomic ratio of Fe/Co in FeCo-RGO composite film is larger than that of the FeCo film under the same fabrication condition. As a result, the FeCo-RGO composite film exhibits good soft magnetic properties and high-frequency properties as well as the FeCo film. The magnetic anisotropy field and saturation magnetization of FeCo-RGO composite film are increased when compared with FeCo film. Furthermore, the ferromagnetic resonance frequency is improved from 2.15 GHz for the FeCo film to 3.9 GHz for the FeCo-RGO composite film. - Highlights: • FeCo-reduced graphene oxide composite film was fabricated on indium tin oxide substrate. • One step electrodeposition method was used. • Good soft magnetic properties were exhibited by the composite films. • Increase of resonance frequency from 2.15 GHz for FeCo film to 3.9 GHz for composite film

  15. Computational alloy design of (Co1-xNix)88Zr7B4Cu1 nanocomposite soft magnets

    Science.gov (United States)

    Dong, B.; Healy, J.; Lan, S.; Daniil, M.; Willard, M. A.

    2018-05-01

    The dependence of coercivity on composition is an important factor for establishing optimized soft magnetic properties. In this study, we have used the random anisotropy and coherent rotation models to estimate the variation of coercivity with composition in (Co1-xNix)88Zr7B4Cu1 nanocomposite alloys. Our calculations that the magnetoelastic anisotropy contribution to coercivity dominates for Ni rich compositions (x > 0.5). A small range of compositions (0.65 < x < 0.75) is predicted to result in low values of coercivity (<10 A/m). To validate this prediction, (Co1-xNix)88Zr7B4Cu1 nanocomposites in this range were prepared by melt spinning followed by 3600 s isothermal annealing at the primary crystallization peak temperature (˜673 K). Hysteresis loops were measured using vibrating sample magnetometry at room temperature and saturation magnetostriction was measured using a strain gage based magnetostrictometer. Moderately small coercivities (30-40 A/m) and magnetostrictions (3-4 ppm) were measured at for samples with 0.685 < x < 0.725. Our measured coercivity had a minimum value of 32 A/m at x = 0.725, a shift in composition of about 5 at% in the direction of higher Ni content and without the anticipated low value of coercivity. Several reasons for the inaccuracy of this approach are described, including: ignored contributions from amorphous phase (especially in magnetoealstic anisotropy), composition segregation during crystallization leading to unpredictable compositional shifts in prediction, and the general observation that the predictability of minimum coercivity from minimal combined anisotropies has unexplained deviation even in far less complicated materials.

  16. Interference between magnetism and surface roughness in coherent soft X-ray scattering

    International Nuclear Information System (INIS)

    Rahmim, A.; Tixier, S.; Tiedje, T.; Eisebitt, S.; Lorgen, M.; Scherer, R.; Eberhardt, W.; Luning, J.; Scholl, A.

    2002-01-01

    In coherent soft x-ray scattering from magnetically ordered surfaces there are contributions to the scattering from the magnetic domains, from the surface roughness, and from the diffraction associated with the pinhole aperture used as a coherence filter. In the present work, we explore the interplay between these contributions by analyzing speckle patterns in diffusely scattered x rays from the surface of magnetic thin films. Magnetic contrast from the surface of anti ferro magnetically ordered LaFeO3 films is caused by magnetic linear dichroism in resonant x-ray scattering. The samples studied possess two types of domains with their magnetic orientations perpendicular to each other. By tuning the x-ray energy from one of the two Fe-L3 resonant absorption peaks to the other, the relative amplitudes of the x-ray scattering from the two domains is inverted which results in speckle pattern changes. A theoretical expression is derived for the intensity correlation between the speckle patterns with the magnetic contrast inverted and not inverted. The model is found to be in good agreement with the x-ray-scattering observations and independent measurements of the surface roughness. An analytical expression for the correlation function gives an explicit relation between the change in the speckle pattern and the roughness, and magnetic and aperture scattering. Changes in the speckle pattern are shown to arise from beating of magnetic scattering with the roughness scattering and diffraction from the aperture. The largest effect is found when the surface roughness scatter is comparable in intensity to the magnetic scatter

  17. Innovative soft magnetic multilayers with enhanced in-plane anisotropy and ferromagnetic resonance frequency for integrated RF passive devices

    Science.gov (United States)

    Falub, Claudiu V.; Bless, Martin; Hida, Rachid; MeduÅa, Mojmír; Ammann, Arnold

    2018-04-01

    We present an innovative, economical method for manufacturing soft magnetic materials that may pave the way for integrated thin film magnetic cores with dramatically improved properties. Soft magnetic multilayered thin films based on the Fe-28%Co20%B (at.%) and Co-4.5%Ta4%Zr (at.%) amorphous alloys are deposited on 8" bare Si and Si/200nm-thermal-SiO2 wafers in an industrial, high-throughput Evatec LLS EVO II magnetron sputtering system. The multilayers consist of stacks of alternating 80-nm-thick ferromagnetic layers and 4-nm-thick Al2O3 dielectric interlayers. Since in our dynamic sputter system the substrate cage rotates continuously, such that the substrates face different targets alternatively, each ferromagnetic sublayer in the multilayer consists of a fine structure comprising alternating CoTaZr and FeCoB nanolayers with very sharp interfaces. We adjust the thickness of these individual nanolayers between 0.5 and 1.5 nm by changing the cage rotation speed and the power of each gun, which is an excellent mode to engineer new, composite ferromagnetic materials. Using X-ray reflectometry (XRR) we reveal that the interfaces between the FeCoB and CoTaZr nanolayers are perfectly smooth with roughness of 0.2-0.3 nm. Kerr magnetometry and B-H looper measurements for the as-deposited samples show that the coercivity of these thin films is very low, 0.2-0.3 Oe, and gradually scales up with the thickness of FeCoB nanolayers, i.e. with the increase of the overall Fe content from 0 % (e.g. CoTaZr-based multilayers) to 52 % (e.g. FeCoB-based multilayers). We explain this trend in the random anisotropy model, based on considerations of grain size growth, as revealed by glancing angle X-ray diffraction (GAXRD), but also because of the increase of magnetostriction with the increase of Fe content as shown by B-H looper measurements performed on strained wafers. The unexpected enhancement of the in-plane anisotropy field from 18.3 Oe and 25.8 Oe for the conventional Co

  18. Improving soft magnetic properties of Mn-Zn ferrite by rare earth ions doping

    Science.gov (United States)

    Zhong, X. C.; Guo, X. J.; Zou, S. Y.; Yu, H. Y.; Liu, Z. W.; Zhang, Y. F.; Wang, K. X.

    2018-04-01

    Mn-Zn ferrites doped with different Sm2O3, Gd2O3, Ce2O3 or Y2O3 were prepared by traditional ceramic technology using industrial pre-sintered powders. A small amount of Sm2O3, Gd2O3, Ce2O3 or Y2O3 can significantly improve the microstructure and magnetic properties. The single spinel phase structure can be maintained with the doping amount up to 0.07 wt.%. A refined grain structure and uniform grain size distribution can be obtained by doping. For all rare earth oxides, a small amount of doping can significantly increase the permeability and reduce the coercivity and magnetic core loss. The optimized doping amount for Sm2O3 or Gd2O3 is 0.01 wt.%, while for Ce2O3 or Y2O3 is 0.03 wt.%. A further increase of the doping content will lead to reduced soft magnetic properties. The ferrite sample with 0.01 wt.% Sm2O3 exhibits the good magnetic properties with permeability, loss, and coercivity of 2586, 316 W/kg, and 24A/m, respectively, at 200 mT and 100 kHz. The present results indicate that rare earth doping can be suggested to be one of the effective ways to improve the performance of soft ferrites.

  19. Improving soft magnetic properties of Mn-Zn ferrite by rare earth ions doping

    Directory of Open Access Journals (Sweden)

    X. C. Zhong

    2018-04-01

    Full Text Available Mn-Zn ferrites doped with different Sm2O3, Gd2O3, Ce2O3 or Y2O3 were prepared by traditional ceramic technology using industrial pre-sintered powders. A small amount of Sm2O3, Gd2O3, Ce2O3 or Y2O3 can significantly improve the microstructure and magnetic properties. The single spinel phase structure can be maintained with the doping amount up to 0.07 wt.%. A refined grain structure and uniform grain size distribution can be obtained by doping. For all rare earth oxides, a small amount of doping can significantly increase the permeability and reduce the coercivity and magnetic core loss. The optimized doping amount for Sm2O3 or Gd2O3 is 0.01 wt.%, while for Ce2O3 or Y2O3 is 0.03 wt.%. A further increase of the doping content will lead to reduced soft magnetic properties. The ferrite sample with 0.01 wt.% Sm2O3 exhibits the good magnetic properties with permeability, loss, and coercivity of 2586, 316 W/kg, and 24A/m, respectively, at 200 mT and 100 kHz. The present results indicate that rare earth doping can be suggested to be one of the effective ways to improve the performance of soft ferrites.

  20. Novel trends in the study of magnetically soft Co-based amorphous glass-coated wires

    International Nuclear Information System (INIS)

    Chiriac, H.; Ovari, T.-A.

    2011-01-01

    An overview of the recent progress and state-of-the-art results in the investigation of the amorphous glass-coated wires with nearly zero magnetostriction is presented. These versatile microwires display enhanced soft magnetic properties, which make them suitable as sensing elements in various sensors for biomedical and automotive applications. Current results on their magnetic characteristics refer to a major refinement of their core-shell magnetic structure by taking into account the interdomain wall and to the thorough analysis of the magnetization within the outer shell. Experimental techniques such as giant magneto-impedance, magneto-resistance, and magneto-optical Kerr effect measurements are employed to prove the outcome of the theoretical calculations. The impact of the magnetic structure of the outer shell on the propagation of domain walls in bistable amorphous wires is analyzed. Very recent results on the magnetization process in nearly zero magnetostrictive amorphous glass-coated wires with submicron dimensions are also reviewed. - Highlights: → The most recent advances in the study of amorphous glass-coated wires with nearly zero magnetostriction are surveyed. → Major progress in the study of their domain structure: the wide interdomain wall, which affects high frequency phenomena. → The magnetization of the outer shell depends on wire diameter and affects the wall propagation in bistable samples. → These novel results are important for future sensor applications of nearly zero magnetostrictive amorphous microwires.

  1. Use of graphite epoxy composites in the Solar-A Soft X-Ray Telescope

    Science.gov (United States)

    Jurcevich, B. K.; Bruner, M. E.

    1990-01-01

    This paper describes the use of composite materials in the Soft X-Ray Telescope (SXT). One of the primary structural members of the telescope is a graphite epoxy metering tube. The metering tube maintains the structural stability of the telescope during launch as well as the focal length through various environmental conditions. The graphite epoxy metering tube is designed to have a negative coefficient of thermal expansion to compensate for the positive expansion of titanium structural supports. The focus is maintained to + or - 0.001 inch by matching the CTE of the composite tube to the remaining structural elements.

  2. Positive temperature coefficient of magnetic anisotropy in polyvinylidene fluoride (PVDF)-based magnetic composites

    OpenAIRE

    Liu, Yiwei; Wang, Baomin; Zhan, Qingfeng; Tang, Zhenhua; Yang, Huali; Liu, Gang; Zuo, Zhenghu; Zhang, Xiaoshan; Xie, Yali; Zhu, Xiaojian; Chen, Bin; Wang, Junling; Li, Run-Wei

    2014-01-01

    The magnetic anisotropy is decreased with increasing temperature in normal magnetic materials, which is harmful to the thermal stability of magnetic devices. Here, we report the realization of positive temperature coefficient of magnetic anisotropy in a novel composite combining β-phase polyvinylidene fluoride (PVDF) with magnetostrictive materials (magnetostrictive film/PVDF bilayer structure). We ascribe the enhanced magnetic anisotropy of the magnetic film at elevated temperature to the st...

  3. Magnetic monopoles in a model of a composite photon

    International Nuclear Information System (INIS)

    Iwazaki, Aiichi.

    1984-10-01

    We show that there are monopole solutions in a composite model where the photon is regarded as a composite of elementary constituents. These monopoles have magnetic charges of the Dirac unit but are essencially different from 't Hooft-Polyakov monopoles since they are boundstates of the constituents. The stability of the monopoles is guaranteed by the conservation of the magnetic charges. (author)

  4. Improved power transfer to wearable systems through stretchable magnetic composites

    Science.gov (United States)

    Lazarus, N.; Bedair, S. S.

    2016-05-01

    The use of wireless power transfer is common in stretchable electronics since physical wiring can be easily destroyed as the system is stretched. This work presents the first demonstration of improved inductive power coupling to a stretchable system through the addition of a thin layer of ferroelastomeric material. A ferroelastomer, an elastomeric polymer loaded with magnetic particulates, has a permeability greater than one while retaining the ability to survive significant mechanical strains. A recently developed ferroelastomer composite based on sendust platelets within a soft silicone elastomer was incorporated into liquid metal stretchable inductors based on the liquid metal galinstan in fluidic channels. For a single-turn inductor, the maximum power transfer efficiency rises from 71 % with no backplane, to 81 % for a rigid ferrite backplane on the transmitter side alone, to 86 % with a ferroelastomer backplane on the receiver side as well. The coupling between a commercial wireless power transmitter coil with ferrite backplane to a five-turn liquid metal inductor was also investigated, finding an improvement in power transfer efficiency from 81 % with only a rigid backplane to 90 % with the addition of the ferroelastomer backplane. Both the single and multi-turn inductors were demonstrated surviving up to 50 % uniaxial applied strain.

  5. Thickness measurement of soft thin films on periodically patterned magnetic substrates by phase difference magnetic force microscopy.

    Science.gov (United States)

    Passeri, D; Dong, C; Angeloni, L; Pantanella, F; Natalizi, T; Berlutti, F; Marianecci, C; Ciccarello, F; Rossi, M

    2014-01-01

    The need for accurate measurement of the thickness of soft thin films is continuously encouraging the development of techniques suitable for this purpose. We propose a method through which the thickness of the film is deduced from the quantitative measurement of the contrast in the phase images of the sample surface acquired by magnetic force microscopy, provided that the film is deposited on a periodically patterned magnetic substrate. The technique is demonstrated by means of magnetic substrates obtained from standard floppy disks. Colonies of Staphylococcus aureus adherent to such substrates were used to obtain soft layers with limited lateral (a few microns) and vertical (hundreds of nanometers) size. The technique is described and its specific merits, limitations and potentialities in terms of accuracy and measurable thickness range are discussed. These parameters depend on the characteristics of the sensing tip/cantilever as well as of the substrates, the latter in terms of spatial period and homogeneity of the magnetic domains. In particular, with the substrates used in this work we evaluated an uncertainty of about 10%, a limit of detection of 50-100 nm and an upper detection limit (maximum measurable thickness) of 1 μm, all obtained with standard lift height values (50-100 nm). Nonetheless, these parameters can be easily optimized by selecting/realizing substrates with suitable spacing and homogeneity of the magnetic domains. For example, the upper detection limit can be increased up to 25-50 μm while the limit of detection can be reduced to a few tens of nanometers or a few nanometers. © 2013 Elsevier B.V. All rights reserved.

  6. Radiation resistant organic composites for superconducting fusion magnets

    International Nuclear Information System (INIS)

    Nishijima, S.; Okada, T.

    1993-01-01

    Organic composite materials (usually reinforced by glas fibers: GFRP) are to be used in fusion superconducting magnets as insulating and/or structural materials. The fusion superconducting magnets are operated under radiation environments and hence the radiation induced degradation of magnet components is ought to be estimated. Among the components the organic composite materials were evaluated to be the most radiation sensitive. Consequently the development of radiation resistant organic composite materials is thought one of the 'key' technologies for fusion superconducting magnets. The mechanism of radiation-induced degradation was studied and the degradation of interlaminar shear strength (ILSS) was found to be the intrinsic phenomenon which controlled the overall degradation of organic composite materials. The degradation of ILSS was studied changing matrix resin, reinforcement and type of fabrics. The possible combination of the organic composites for the fusion superconducting magnet will be discussed. (orig.)

  7. Preparation of Magnetic Composite Materials: Experiments for Secondary School Students

    Czech Academy of Sciences Publication Activity Database

    Baldíková, Eva; Pospíšková, K.; Maděrová, Zdeňka; Šafaříková, Miroslava; Šafařík, Ivo

    2016-01-01

    Roč. 110, č. 1 (2016), s. 64-68 ISSN 0009-2770 Keywords : dyes removal * nanoparticles * mechanochemistry * technology * adsorbent * fe3o4 * magnetic modification * magnetic composite materials * magnetic separation * microwave-assisted synthesis * mechanochemical synthesis Impact factor: 0.387, year: 2016

  8. Electromagnetic shielding mechanisms using soft magnetic stainless steel fiber enabled polyester textiles

    Science.gov (United States)

    Shyr, Tien-Wei; Shie, Jing-Wen

    2012-11-01

    This work studied the effects of conductivity, magnetic loss, and complex permittivity when using blended textiles (SSF/PET) of polyester fibers (PET) with stainless steel fibers (SSF) on electromagnetic wave shielding mechanisms at electromagnetic wave frequencies ranging from 30 MHz to 1500 MHz. The 316L stainless steel fiber used in this study had 38 vol% γ austenite and 62 vol% α' martensite crystalline phases, which was characterized by an x-ray diffractometer. Due to the magnetic and dielectric loss of soft metallic magnetic stainless steel fiber enabled polyester textiles, the relationship between the reflection/absorption/transmission behaviors of the electromagnetic wave and the electrical/magnetic/dielectric properties of the SSF and SSF/PET fabrics was analyzed. Our results showed that the electromagnetic interference shielding of the SSF/PET textiles show an absorption-dominant mechanism, which attributed to the dielectric loss and the magnetic loss at a lower frequency and attributed to the magnetic loss at a higher frequency, respectively.

  9. PROCESSING OF SOFT MAGNETIC MATERIALS BY POWDER METALLURGY AND ANALYSIS OF THEIR PERFORMANCE IN ELECTRICAL MACHINES

    Directory of Open Access Journals (Sweden)

    W. H. D. Luna

    2017-12-01

    Full Text Available This article presents the use of finite elements to analyze the yield of electric machines based on the use of different soft magnetic materials for the rotor and the stator, in order to verify the performance in electric machine using powder metallurgy. Traditionally, the cores of electric machines are built from rolled steel plates, thus the cores developed in this work are obtained from an alternative process known as powder metallurgy, where powders of soft magnetic materials are compacted and sintered. The properties of interest were analyzed (magnetic, electric and mechanical properties and they were introduced into the software database. The topology of the rotor used was 400 W three-phase synchronous motor manufactured by WEG Motors. The results show the feasibility to replace the metal sheets of the electric machines by solid blocks obtained by powder metallurgy process with only 0.37% yield losses. In addition, the powder metallurgical process reduces the use of raw materials and energy consumption per kg of raw material processed.

  10. Effects of annealing and pulse plating on soft magnetic properties of electroplated Fe-Ni films

    Directory of Open Access Journals (Sweden)

    T. Yanai

    2016-05-01

    Full Text Available We have already reported that Fe-Ni films prepared in citric-acid-based plating baths show good soft magnetic properties. In this paper, we investigated the effect of the grain size of the Fe-Ni crystalline phase in the films on magnetic properties, and employed an annealing and a pulse plating method in order to vary the grain size. The coercivity of the annealed Fe-Ni films at 600 °C shows large value, and good correlation between the grain growth and the coercivity was observed. The pulse plating enables us to reduce the grain size of the as-plated Fe-Ni films compared with the DC plating method, and we realized smooth surface and low coercivity of the Fe-Ni films using the pulse plating method. From these results, we confirmed the importance of the reduction in the grain size, and concluded that a pulse plating is an effective method to improve the good soft magnetic properties for our previously-reported Fe-Ni films.

  11. Initial magnetic susceptibility of the diluted magnetopolymer elastic composites

    International Nuclear Information System (INIS)

    Borin, D.Yu.; Odenbach, S.

    2017-01-01

    In this work diluted magnetopolymer elastic composites based on magnetic microparticles are experimentally studied. Considered samples have varied concentration of the magnetic powder and different structural anisotropy. Experimental data on magnetic properties are accomplished by microstructural observations performed using X-Ray tomography. Influence of the particles amount and structuring effects on the initial magnetic susceptibility of the composites as well as the applicability of the Maxwell-Garnett approximation, which is widely used in considerations of magnetopolymer elastic composites, are evaluated. It is demonstrated that the approximation works well for diluted samples containing randomly distributed magnetic particles and for the diluted samples with chain-like structures oriented perpendicular to an externally applied field, while it fails to predict the susceptibility of the samples with structures oriented parallel to the field. Moreover, it is shown, that variation of the chains morphology does not significantly change the composite initial magnetic susceptibility. - Highlights: • The Maxwell-Garnet prediction works well for the diluted isotropic composites. • The Maxwell-Garnet prediction can be used for composites with structures oriented perpendicular to an applied field. • Chains oriented parallel to an applied field significantly increase the composite initial magnetic susceptibility. • The number and thickness of chains is not of the highest importance for the diluted composites. • The crucial reason of the observed effect is expected to be the demagnetisation factor of the chains.

  12. Development of keratin–chitosan–gelatin composite scaffold for soft tissue engineering

    Energy Technology Data Exchange (ETDEWEB)

    Kakkar, Prachi [Central Leather Research Institute (Council of Scientific and Industrial Research), Adyar, Chennai 600020 (India); Verma, Sudhanshu; Manjubala, I. [Biomedical Engineering Division, School of Bio Sciences and Technology, VIT University, Vellore 632014 (India); Madhan, B., E-mail: bmadhan76@yahoo.co.in [Central Leather Research Institute (Council of Scientific and Industrial Research), Adyar, Chennai 600020 (India)

    2014-12-01

    Keratin has gained much attention in the recent past as a biomaterial for wound healing owing to its biocompatibility, biodegradability, intrinsic biological activity and presence of cellular binding motifs. In this paper, a novel biomimetic scaffold containing keratin, chitosan and gelatin was prepared by freeze drying method. The prepared keratin composite scaffold had good structural integrity. Fourier Transform Infrared (FTIR) spectroscopy showed the retention of the native structure of individual biopolymers (keratin, chitosan, and gelatin) used in the scaffold. Thermogravimetric Analysis (TGA) and Differential Scanning Calorimetry (DSC) results revealed a high thermal denaturation temperature of the scaffold (200–250 °C). The keratin composite scaffold exhibited tensile strength (96 kPa), compression strength (8.5 kPa) and water uptake capacity (> 1700%) comparable to that of a collagen scaffold, which was used as control. The morphology of the keratin composite scaffold observed using a Scanning Electron Microscope (SEM) exhibited good porosity and interconnectivity of pores. MTT assay using NIH 3T3 fibroblast cells demonstrated that the cell viability of the keratin composite scaffold was good. These observations suggest that the keratin–chitosan–gelatin composite scaffold is a promising alternative biomaterial for tissue engineering applications. - Highlights: • Fabrication of novel Keratin-Chitosan-Gelatin composite scaffold • Keratin composite scaffold shows excellent water uptake capacity and porosity • Keratin composite scaffold shows good thermal and physical stability • Biocompatibility of the developed scaffold is comparable to collagen scaffolds • Developed scaffold is a promising material for soft tissue engineering applications.

  13. Analytical Analysis and Field Test Investigation of Consolidation for CCSG Pile Composite Foundation in Soft Clay

    Directory of Open Access Journals (Sweden)

    Jin Yu

    2013-01-01

    Full Text Available Low-grade concrete-cored sand-gravel (CCSG pile composite foundation is a new kind of composite foundation for thick and soft clay ground treatment. An analytical solution was derived for calculating the consolidation process of this composite foundation by considering coefficients of horizontal permeability in smear zone, the radial flow within the sand-gravel shell, and the impervious property of concrete-cored pile. The results show that Terzaghi’s one-dimensional consolidation solution and the consolidation analytical solution of ordinary composite foundation were special cases of this solution. Curves of the average consolidation degree of the composite foundation under various nondimensional parameters were observed using the program based on the theoretical formula. Meanwhile, a series of in situ measurements including the settlement of pile and soil, the pore water pressure, and the total stress under embankment load were obtained on the CCSG pile composite foundation on a section of Zhenjiang-Liyang highway. The analyzed results show that the new style composite foundation patent technology has many advantages such as small differential postconstruction settlement (differential is not good, small is, reliable quality, high bearing capacity, and stability. And the consolidation of composite foundation is largely affected by the nondimensional parameters. The analytical solution is finally verified with the actual measurement data.

  14. The percolation effect and optimization of soft magnetic properties of FeSiAl magnetic powder cores

    Energy Technology Data Exchange (ETDEWEB)

    Bai, Ruru [College of Material Science and Engineering, Nanchang University, Nanchang 330031, Jiangxi (China); Zhu, Zhenghou, E-mail: z00708@sina.com [College of Material Science and Engineering, Nanchang University, Nanchang 330031, Jiangxi (China); Zhao, Hui, E-mail: candyzhaohui@126.com [College of Material Science and Engineering, Nanchang University, Nanchang 330031, Jiangxi (China); Institute of Space Science and Technology, Nanchang University, Nanchang 330031, Jiangxi (China); Mao, Shenghua [Jiangxi Aite magnetic materials Co. Ltd., Yichun 336000, Jiangxi (China); Zhong, Qi [College of Material Science and Engineering, Nanchang University, Nanchang 330031, Jiangxi (China)

    2017-07-01

    Highlights: • A new magnetic percolation phenomenon of ρ-μe in MPCs was discovered. • The soft magnetic properties of FeSiAl MPCs were studied. • The comprehensive magnetic properties of MPCs were optimized. • The formation mechanism of magnetic conductive path was explained. - Abstract: In this paper, a new magnetic percolation phenomenon between the green compact density ρ and effective permeability μe in FeSi{sub 9.6}Al{sub 6.5} magnetic powder cores, was discovered. The Magnetic Percolation Area of ρ is the range of 5.6 g/cm{sup 3} ∼ 5.78 g/cm{sup 3}, and the percolation threshold is 5.78 g/cm{sup 3}. As a result of the guidance of the percolation theory, the best comprehensive magnetic properties have been optimized through adjusting the distribution of powders. The special distribution of the magnetic powder cores with the best comprehensive magnetic properties was as follows: the content 60% with the particle size distribution of 100–200 mesh, the content 20% with the particle size distribution of 200–325 mesh and the content 20% with the particle size distribution of ≥400 mesh. When the green compact density ρ of cores was 5.79 g/cm{sup 3}, and the frequency was in the range of 1 kHz ∼ 100 kHz, the best comprehensive magnetic properties were as follows: μe = 91, ∆μ = 0.61%, μe(H80 Oe) = 43, μe(H100 Oe) = 33, μe(H120 Oe) = 26, Pc(50 mT/20 kHz) = 30.58 kW/m{sup 3}, Pc(50 mT/50 kHz) = 76.85 kW/m{sup 3}, Pc(50 mT/100 kHz) = 178 kW/m{sup 3}. Not only have those cores the excellent constant magnetic properties with frequency, the excellent DC superposition characteristic and the lower loss at high frequency, but also the effective permeability outstandingly goes up, which has important significance for the miniaturization of inductance components.

  15. Optimization of chemical composition in the manufacturing process of flotation balls based on intelligent soft sensing

    Directory of Open Access Journals (Sweden)

    Dučić Nedeljko

    2016-01-01

    Full Text Available This paper presents an application of computational intelligence in modeling and optimization of parameters of two related production processes - ore flotation and production of balls for ore flotation. It is proposed that desired chemical composition of flotation balls (Mn=0.69%; Cr=2.247%; C=3.79%; Si=0.5%, which ensures minimum wear rate (0.47 g/kg during copper milling is determined by combining artificial neural network (ANN and genetic algorithm (GA. Based on the results provided by neuro-genetic combination, a second neural network was derived as an ‘intelligent soft sensor’ in the process of white cast iron production. The proposed ANN 12-16-12-4 model demonstrated favourable prediction capacity, and can be recommended as a ‘intelligent soft sensor’ in the alloying process intended for obtaining favourable chemical composition of white cast iron for production of flotation balls. In the development of intelligent soft sensor data from the two real production processes was used. [Projekat Ministarstva nauke Republike Srbije, br. TR35037 i br. TR35015

  16. The cation inversion and magnetization in nanopowder zinc ferrite obtained by soft mechanochemical processing

    International Nuclear Information System (INIS)

    Milutinović, A.; Lazarević, Z.; Jovalekić, Č.; Kuryliszyn-Kudelska, I.; Romčević, M.; Kostić, S.; Romčević, N.

    2013-01-01

    Graphical abstract: - Highlights: • Nano powder of ZnFe 2 O 4 prepared by a soft mechanochemical route after 18 h milling. • Phase formation controlled by XRD, Raman spectroscopy and magnetic measurements. • Size, strain and cation inversion degree determined by Rietveld refinement. • We were able to estimate the degree of inversion at most 0.348 and 0.4. • Obtained extremely high values of saturation magnetizations at T = 4.5 K. - Abstract: Two zinc ferrite nanoparticle materials were prepared by the same method – soft mechanochemical synthesis, but starting from different powder mixtures: (1) Zn(OH) 2 /α-Fe 2 O 3 and (2) Zn(OH) 2 /Fe(OH) 3 . In both cases a single phase system was obtained after 18 h of milling. The progress of the synthesis was controlled by X-ray diffractometry (XRD), Raman spectroscopy, TEM and magnetic measurements. Analysis of the XRD patterns by Rietveld refinement allowed determination of the cation inversion degree for both obtained single phase ZnFe 2 O 4 samples. The sample obtained from mixture (1) has the cation inversion degree 0.3482 and the sample obtained from mixture (2) 0.400. Magnetization measurements were confirmed that the degrees of the inversion were well estimated. Comparison with published data shows that used method of synthesis gives nano powder samples with extremely high values of saturation magnetizations: sample (1) 78.3 emu g −1 and sample (2) 91.5 emu g −1 at T = 4.5 K

  17. Exploring the Hard and Soft X-ray Emission of Magnetic Cataclysmic Variables

    Science.gov (United States)

    de Martino, D.; Anzolin, G.; Bonnet-Bidaud, J.-M.; Falanga, M.; Matt, G.; Mouchet, M.; Mukai, K.; Masetti, N.

    2009-05-01

    A non-negligible fraction of galactic hard (>20 keV) X-ray sources were identified as CVs of the magnetic Intermediate Polar type in INTEGRAL, SWIFT and RXTE surveys, that suggests a still hidden but potentially important population of faint hard X-ray sources. Simbol-X has the unique potential to simultaneously characterize their variable and complex soft and hard X-ray emission thus allowing to understand their putative role in galactic populations of X-ray sources.

  18. Soft magnetic nanoparticles of BaFe sub 1 sub 2 O sub 1 sub 9 fabricated under mild conditions

    CERN Document Server

    Che Shan; Chen Qian Wang

    2003-01-01

    Nanoparticles of barium hexaferrite, with an average size of 12 nm, were prepared by a hydrothermal route at relatively low temperatures (140-180 deg C). The effects of reaction temperature and time on the particle size and magnetic properties were discussed. The nanoparticles show a soft magnetic feature with a saturation magnetization of 1.1 emu g sup - sup 1 and coercivity of 221.0 Oe, rather than the hard magnetic characteristic that the corresponding bulk material exhibits. Annealing treatment in air at 800 deg C led to an order-of-magnitude increase of the saturation magnetization (67.3 emu g sup - sup 1) and coercive force (4511 Oe). It is suggested that the oxygen vacancies should be responsible for the soft magnetic characteristic that appeared for the as-prepared barium hexaferrite nanoparticles. (letter to the editor)

  19. Soft tissue masses with myxoid stroma: Can conventional magnetic resonance imaging differentiate benign from malignant tumors?

    Energy Technology Data Exchange (ETDEWEB)

    Crombe, A., E-mail: amandine.crombe@ens-lyon.fr [Department of Radiology, Institut Bergonié, 229 cours de l’Argonne, 33076 Bordeaux Cedex (France); Alberti, N. [Department of Radiology, Institut Bergonié, 229 cours de l’Argonne, 33076 Bordeaux Cedex (France); Stoeckle, E. [Department of Surgery, Institut Bergonié, 229 cours de l’Argonne, 33076 Bordeaux Cedex (France); Brouste, V. [Clinical and Epidemiological Research Unit, Institut Bergonié, 33000 Bordeaux (France); Buy, X. [Department of Radiology, Institut Bergonié, 229 cours de l’Argonne, 33076 Bordeaux Cedex (France); Coindre, J-M. [Department of Pathology, Institut Bergonié, 229 cours de l’Argonne, 33076 Bordeaux Cedex (France); Kind, M. [Department of Radiology, Institut Bergonié, 229 cours de l’Argonne, 33076 Bordeaux Cedex (France)

    2016-10-15

    Objectives: To retrospectively evaluate the diagnostic performance of morphological signs observed on conventional magnetic resonance (MR) imaging to differentiate benign from malignant peripheral solid tumors of soft tissue with myxoid stroma. Methods: MR images from 95 consecutive histopathologically proven tumors (26 benign and 69 malignant) of soft tissues with myxoid components were evaluated in our tertiary referral center. Two radiologists, blind to pathology results, independently reviewed conventional MR sequences including at least a) one T2-weighted sequence with or without fat suppression; b) one T1-weighted sequence without fat suppression; and c) one T1-weighted sequence with gadolinium-complex contrast enhancement and fat suppression. Multiple criteria were defined to analyze morphology, margins, architecture and tumor periphery and evaluated for each lesion. Intra- and inter-observer reproducibility and Odds ratios were calculated for each criterion. Results: The most relevant and reproducible criteria to significantly predict malignancy were: (1) ill-defined tumor margins, (2) a hemorrhagic component, (3) intra-tumoral fat, (4) fibrosis and (5) the “tail sign”. A lesion is classified as malignant if any of these 5 criteria is present, and benign if none of them are observed. Therefore, this combination provides a sensitivity of 92.9% and a specificity of 93.3%. Conclusion: Conventional MR imaging provides reproducible criteria that can be combined to differentiate between benign and malignant solid tumors of soft tissue with myxoid stroma.

  20. Synthesis and magnetic properties of cobalt-iron/cobalt-ferrite soft/hard magnetic core/shell nanowires

    Science.gov (United States)

    Leandro Londoño-Calderón, César; Moscoso-Londoño, Oscar; Muraca, Diego; Arzuza, Luis; Carvalho, Peterson; Pirota, Kleber Roberto; Knobel, Marcelo; Pampillo, Laura Gabriela; Martínez-García, Ricardo

    2017-06-01

    A straightforward method for the synthesis of CoFe2.7/CoFe2O4 core/shell nanowires is described. The proposed method starts with a conventional pulsed electrodeposition procedure on alumina nanoporous template. The obtained CoFe2.7 nanowires are released from the template and allowed to oxidize at room conditions over several weeks. The effects of partial oxidation on the structural and magnetic properties were studied by x-ray spectrometry, magnetometry, and scanning and transmission electron microscopy. The results indicate that the final nanowires are composed of 5 nm iron-cobalt alloy nanoparticles. Releasing the nanowires at room conditions promoted surface oxidation of the nanoparticles and created a CoFe2O4 shell spinel-like structure. The shell avoids internal oxidation and promotes the formation of bi-magnetic soft/hard magnetic core/shell nanowires. The magnetic properties of both the initial single-phase CoFe2.7 nanowires and the final core/shell nanowires, reveal that the changes in the properties from the array are due to the oxidation more than effects associated with released processes (disorder and agglomeration).

  1. Moving interfacial crack between two dissimilar soft ferromagnetic materials in uniform magnetic field

    International Nuclear Information System (INIS)

    Zhao, She Xu; Lee, Kang Yong

    2007-01-01

    This paper presents the dynamic magnetoelastic stress intensity factors of a Yoffe-type moving crack at the interface between two dissimilar soft ferromagnetic elastic half-planes. The solids are subjected to a uniform in-plane magnetic field and the crack is opened by internal normal and shear tractions. The problem is considered within the framework of linear magnetoelasticity. By application of the Fourier integral transform, the mixed boundary problem is reduced to a pair of integral equations of the second kind with Cauchy-type singularities. The singular integral equations are solved by means of a Jacobi polynomial expansion method. For a particular case, closed-form solutions are obtained. It is shown that the magnetoelastic stress intensity factors depend on the moving velocity of the crack, the magnetic field and the magnetoelastic properties of the materials

  2. Bright circularly polarized soft X-ray high harmonics for X-ray magnetic circular dichroism.

    Science.gov (United States)

    Fan, Tingting; Grychtol, Patrik; Knut, Ronny; Hernández-García, Carlos; Hickstein, Daniel D; Zusin, Dmitriy; Gentry, Christian; Dollar, Franklin J; Mancuso, Christopher A; Hogle, Craig W; Kfir, Ofer; Legut, Dominik; Carva, Karel; Ellis, Jennifer L; Dorney, Kevin M; Chen, Cong; Shpyrko, Oleg G; Fullerton, Eric E; Cohen, Oren; Oppeneer, Peter M; Milošević, Dejan B; Becker, Andreas; Jaroń-Becker, Agnieszka A; Popmintchev, Tenio; Murnane, Margaret M; Kapteyn, Henry C

    2015-11-17

    We demonstrate, to our knowledge, the first bright circularly polarized high-harmonic beams in the soft X-ray region of the electromagnetic spectrum, and use them to implement X-ray magnetic circular dichroism measurements in a tabletop-scale setup. Using counterrotating circularly polarized laser fields at 1.3 and 0.79 µm, we generate circularly polarized harmonics with photon energies exceeding 160 eV. The harmonic spectra emerge as a sequence of closely spaced pairs of left and right circularly polarized peaks, with energies determined by conservation of energy and spin angular momentum. We explain the single-atom and macroscopic physics by identifying the dominant electron quantum trajectories and optimal phase-matching conditions. The first advanced phase-matched propagation simulations for circularly polarized harmonics reveal the influence of the finite phase-matching temporal window on the spectrum, as well as the unique polarization-shaped attosecond pulse train. Finally, we use, to our knowledge, the first tabletop X-ray magnetic circular dichroism measurements at the N4,5 absorption edges of Gd to validate the high degree of circularity, brightness, and stability of this light source. These results demonstrate the feasibility of manipulating the polarization, spectrum, and temporal shape of high harmonics in the soft X-ray region by manipulating the driving laser waveform.

  3. Soft magnetic properties and damping parameter of (FeCo-Al alloy thin films

    Directory of Open Access Journals (Sweden)

    Isao Kanada

    2017-05-01

    Full Text Available For high frequency device applications, a systematic study of the soft magnetic properties and magnetization dynamics of (FeCo-Al alloy thin films has been carried out. A low effective damping parameter αeff of 0.002 and a high saturation magnetization of about 1,800 emu/cc are obtained at y=0.2∼0.3 for (Fe1-yCoy98Al2 alloy thin films deposited onto fused silica and MgO(100 at an ambient temperature during deposition. Those films are of the bcc structure with the orientation normal to the film plane. They possess a columnar structure, grown along the film normal. The column width is found to be about 20 nm for y=0.25. It is concluded that the (FeCo-Al thin films with a damping parameter as low as 0.002 and high saturation magnetization of about 1,800 emu/cc have been successfully fabricated, and that they are potential for future high frequency device applications.

  4. Locomotion of inchworm-inspired robot made of smart soft composite (SSC)

    International Nuclear Information System (INIS)

    Wang, Wei; Lee, Jang-Yeob; Rodrigue, Hugo; Song, Sung-Hyuk; Ahn, Sung-Hoon; Chu, Won-Shik

    2014-01-01

    A soft-bodied robot made of smart soft composite with inchworm-inspired locomotion capable of both two-way linear and turning movement has been proposed, developed, and tested. The robot was divided into three functional parts based on the different functions of the inchworm: the body, the back foot, and the front foot. Shape memory alloy wires were embedded longitudinally in a soft polymer to imitate the longitudinal muscle fibers that control the abdominal contractions of the inchworm during locomotion. Each foot of the robot has three segments with different friction coefficients to implement the anchor and sliding movement. Then, utilizing actuation patterns between the body and feet based on the looping gait, the robot achieves a biomimetic inchworm gait. Experiments were conducted to evaluate the robot’s locomotive performance for both linear locomotion and turning movement. Results show that the proposed robot’s stride length was nearly one third of its body length, with a maximum linear speed of 3.6 mm s −1 , a linear locomotion efficiency of 96.4%, a maximum turning capability of 4.3 degrees per stride, and a turning locomotion efficiency of 39.7%. (paper)

  5. Phase composition and magnetic properties in nanocrystalline permanent magnets based on misch-metal

    Science.gov (United States)

    Ma, Q.; Wang, J.; Zhang, Z. Y.; Zhang, X. F.; Liu, F.; Liu, Y. L.; Jv, X. M.; Li, Y. F.; Wang, G. F.

    2017-09-01

    The magnetic properties and phase composition of magnets based on misch-metal (MM) with nominal composition of MM13+xFe84-xB6.5 with x = 0.5, 1, 1.5, 2 and 2.5 using melt-spinning method were investigated. For x = 1.5, it could exhibit best magnetic properties (Hcj = 753.02 kA m-1, (BH)max = 70.77 kJ m-3). X-ray diffraction and energy dispersive spectroscopy show that the multi hard magnetic phase of RE2Fe14B (RE = La, Ce, Pr, Nd) existed in the magnets. The domain wall pinning effect and the exchange coupling interaction between grains are dependent on the abnormal RE-rich phase composition. Optimizing the phase constitution is necessary to improve magnetic properties in MM-Fe-B magnets for utilizing the rare earth resource in a balanced manner.

  6. Effect of non-magnetic intermediate layer on film structure, magnetic properties, and noise characteristics of FeCSi soft magnetic multilayers

    International Nuclear Information System (INIS)

    Kawano, Hiroyasu; Morikawa, Takeshi; Matsumoto, Koji; Shono, Keiji

    2004-01-01

    The film structures, magnetic properties, and noise characteristics of soft magnetic multilayers with alternately stacked FeCSi soft magnetic layers and non-magnetic intermediate layers were investigated. The FeCSi layers in an as-deposited multilayer with C or Ta intermediate layers had the same nano-sized fine crystalline grains and low media noise as an as-deposited FeCSi monolayer. Amorphous C intermediate layers suppressed the amplitude of spike noise especially well. In contrast, FeCSi layers in an as-deposited multilayer with Cr or Ti intermediate layers were composed of coarse crystalline grains, which increased the media noise. The crystallographic match at the interface between the layers in a multilayer could explain these phenomena. The similarity of the atomic arrangement at the interface between layers and the crystallographic match of less than a few percent for the distance between atoms crystallized FeCSi layers with nano-sized fine crystalline grains into ones with coarse crystalline grains during deposition

  7. Magnetization reversal in textured NdFeB-Fe composites observed by domain imaging

    Energy Technology Data Exchange (ETDEWEB)

    Thielsch, Juliane, E-mail: j.thielsch@ifw-dresden.d [IFW Dresden, Institute for Metallic Materials, P.O. Box 27 01 16, D-01171 Dresden (Germany); Hinz, Dietrich; Schultz, Ludwig; Gutfleisch, Oliver [IFW Dresden, Institute for Metallic Materials, P.O. Box 27 01 16, D-01171 Dresden (Germany)

    2010-10-15

    Textured composite samples consisting of Nd{sub 13.6}Fe{sub 73.6}Ga{sub 0.6}Co{sub 6.6}B{sub 5.6} (MQU-F{sup TM}) and micron-sized Fe particles with weight ratios from 100:0 to 70:30 have been prepared by hot deformation. Microstructure studies revealed a layered structure of both phases with the layer normal parallel to the pressing direction. Magnetic measurements showed single-phase hysteresis curves for all samples when measured along the pressing direction, which is also the easy axis of magnetization. Coercivity decreased drastically from 1.32 T for pure NdFeB samples to 0.154 T for a sample with 30 wt% Fe. Magneto-optical Kerr microscopy with a digitally enhanced imaging technique has been used to examine the evolution of magnetic domains in the hard and soft phase during demagnetizing a sample consisting of 70 wt% NdFeB and 30 wt% Fe. It is shown that demagnetization takes place via domain rearrangements within the soft phase, which lead to and support the nucleation of reversed interaction domains at phase boundaries. Also nucleation of interaction domains within the hard magnetic phase could be revealed.

  8. Magnetization reversal in textured NdFeB-Fe composites observed by domain imaging

    International Nuclear Information System (INIS)

    Thielsch, Juliane; Hinz, Dietrich; Schultz, Ludwig; Gutfleisch, Oliver

    2010-01-01

    Textured composite samples consisting of Nd 13.6 Fe 73.6 Ga 0.6 Co 6.6 B 5.6 (MQU-F TM ) and micron-sized Fe particles with weight ratios from 100:0 to 70:30 have been prepared by hot deformation. Microstructure studies revealed a layered structure of both phases with the layer normal parallel to the pressing direction. Magnetic measurements showed single-phase hysteresis curves for all samples when measured along the pressing direction, which is also the easy axis of magnetization. Coercivity decreased drastically from 1.32 T for pure NdFeB samples to 0.154 T for a sample with 30 wt% Fe. Magneto-optical Kerr microscopy with a digitally enhanced imaging technique has been used to examine the evolution of magnetic domains in the hard and soft phase during demagnetizing a sample consisting of 70 wt% NdFeB and 30 wt% Fe. It is shown that demagnetization takes place via domain rearrangements within the soft phase, which lead to and support the nucleation of reversed interaction domains at phase boundaries. Also nucleation of interaction domains within the hard magnetic phase could be revealed.

  9. Tailoring the soft magnetic properties of sputtered multilayers by microstructure engineering for high frequency applications

    Directory of Open Access Journals (Sweden)

    Claudiu V. Falub

    2017-05-01

    Full Text Available Soft magnetic Ni78.5Fe21.5, Co91.5Ta4.5Zr4 and Fe52Co28B20 thin films laminated with SiO2, Al2O3, AlN, and Ta2O5 dielectric interlayers were deposited on 8” Si wafers using DC, pulsed DC and RF cathodes in the industrial, high-throughput Evatec LLS-EVO-II magnetron sputtering system. A typical multilayer consists of a bilayer stack up to 50 periods, with alternating (50-100 nm thick magnetic layers and (2-20 nm thick dielectric interlayers. We introduced the in-plane magnetic anisotropy in these films during sputtering by a combination of a linear magnetic field, seed layer texturing by means of linear collimators, and the oblique incidence inherent to the geometry of the sputter system. Depending on the magnetic material, the anisotropy field for these films was tuned in the range of ∼(7-120 Oe by choosing the appropriate interlayer thickness, the aspect ratios of the linear collimators in front of the targets, and the sputter process parameters (e.g. pressure, power, DC pulse frequency, while the coercivity was kept low, ∼(0.05-0.9 Oe. The alignment of the easy axis (EA on the 8” wafers was typically between ±1.5° and ±4°. We discuss the interdependence of structure and magnetic properties in these films, as revealed by atomic force microscopy (AFM, X-ray reflectivity (XRR with reciprocal space mapping (RSM and magneto-optical Kerr effect (MOKE measurements.

  10. Minor-Cu doped soft magnetic Fe-based FeCoBCSiCu amorphous alloys with high saturation magnetization

    Science.gov (United States)

    Li, Yanhui; Wang, Zhenmin; Zhang, Wei

    2018-05-01

    The effects of Cu alloying on the amorphous-forming ability (AFA) and magnetic properties of the P-free Fe81Co5B11C2Si1 amorphous alloy were investigated. Addition of ≤ 1.0 at.% Cu enhances the AFA of the base alloy without significant deterioration of the soft magnetic properties. The Fe80.5Co5B11C2Si1Cu0.5 alloy with the largest critical thickness for amorphous formation of ˜35 μm possesses a high saturation magnetization (Bs) of ˜1.78 T, low coercivity of ˜14.6 A/m, and good bending ductility upon annealing in a wide temperature range of 513-553 K with maintaining the amorphous state. The fabrication of the new high-Fe-content Fe-Co-B-C-Si-Cu amorphous alloys by minor doping of Cu gives a guideline to developing high Bs amorphous alloys with excellent AFA.

  11. Induced magnetic anisotropy in Si-free nanocrystalline soft magnetic materials: A transmission x-ray diffraction study

    International Nuclear Information System (INIS)

    Parsons, R.; Suzuki, K.; Yanai, T.; Kishimoto, H.; Kato, A.; Ohnuma, M.

    2015-01-01

    In order to better understand the origin of field-induced anisotropy (K u ) in Si-free nanocrystalline soft magnetic alloys, the lattice spacing of the bcc-Fe phase in nanocrystalline Fe 94−x Nb 6 B x (x = 10, 12, 14) alloys annealed under an applied magnetic field has been investigated by X-ray diffraction in transmission geometry (t-XRD) with the diffraction vector parallel and perpendicular to the field direction. The saturation magnetostriction (λ s ) of nanocrystalline Fe 94−x Nb 6 B x was found to increase linearly with the volume fraction of the residual amorphous phase and is well described by taking into account the volume-weighted average of two local λ s values for the bcc-Fe nanocrystallites (−5 ± 2 ppm) and the residual amorphous matrix (+8 ± 2 ppm). The lattice distortion required to produce the measured K u values (∼100 J/m 3 ) was estimated via the inverse magnetostrictive effect using the measured λ s values and was compared to the lattice spacing estimations made by t-XRD. The lattice strain required to produce K u under the magnetoelastic model was not observed by the t-XRD experiments and so the findings of this study suggest that the origin of magnetic field induced K u cannot be explained through the magnetoelastic effect

  12. Real-time soft x-ray imaging on composite materials

    International Nuclear Information System (INIS)

    Polichar, R.

    1985-01-01

    The increased use of composite materials in aircraft structures has emphasized many of the unique and difficult aspects of the inspection of such components. Ultrasound has been extensively applied to certain configurations since it is relatively sensitive to laminar discontinuities in structure. Conversely, the use of conventional x-ray examination has been severely hampered by the fact that these composite materials are virtually transparent to the x-ray energies commonly encountered in industrial radiography (25 kv and above). To produce images with contrast approaching conventional radiography, one must use x-ray beams with average energies below 10 KEV where the absorption coefficients begin to rise rapidly for these low atomic number materials. This new regime of soft x-rays presents a major challenge to real-time imaging components. Special screen and window technology is required if these lower energy x-rays are to be effectively detected. Moreover, conventional x-ray tubes become very inefficient for generating the required x-ray flux at potentials much below 29 kv and the increased operating currents put significant limitations on conventional power sources. The purpose of this paper is to explore these special problems related to soft x-ray real-time imaging and to define the optimal technologies. Practical results obtained with the latest commerical and developmental instruments for real-time imaging will be shown. These instruments include recently developed imaging systems, new x-ray tubes and various approaches to generator design. The measured results convincingly demonstrate the effectiveness practicality of real-time soft x-ray imaging. They also indicate the major changes in technology and approach that must be taken for practical systems to be truly effective

  13. Woven type smart soft composite beam with in-plane shape retention

    International Nuclear Information System (INIS)

    Wu, Renzhe; Han, Min-Woo; Lee, Gil-Yong; Ahn, Sung-Hoon

    2013-01-01

    Shape memory alloy (SMA) wire embedded composites (SMAECs) are widely used as morphing structures in small-size and high-output systems. However, conventional SMAECs cannot keep deformed shapes without additional energy. In this paper, a new kind of smart structure named the woven type smart soft composite (SSC) beam is introduced, which is not only capable of morphing, but also maintaining its deformed shape without additional energy. The woven type SSC beam consists of two parts: woven wires and matrix. The selected woven wires are nitinol (Ni–Ti) SMA wires and glass fibers, while the matrix part is polydimethylsiloxane (PDMS). In order to evaluate the performance of the woven type SSC beam in areas such as in-plane deformation, blocking force and repeatability, a beam-shape specimen is prepared of size 100 mm (length) × 8 mm (width) ×3 mm (thickness). The fabricated SSC beam achieved 21 mm deformation and 16 mm shape retention. Blocking force was measured using a dynamometer, and was about 60 mN. In the repeatability test, it recovered almost the same position when its cooling time was 90 s more. Consequently, the woven type SSC beam can be applied to bio-mimicking, soft morphing actuators, consuming less energy than traditional SMAECs. (paper)

  14. Behavior of Fiber-Reinforced Smart Soft Composite Actuators According to Material Composition

    Energy Technology Data Exchange (ETDEWEB)

    Han, Min-Woo; Kim, Hyung-Il; Song, Sung-Hyuk; Ahn, Sung-Hoon [Seoul Nat’l Univ., Seoul (Korea, Republic of)

    2017-02-15

    Fiber-reinforced polymer composites, which are made by combining a continuous fiber that acts as reinforcement and a homogeneous polymeric material that acts as a host, are engineering materials with high strength and stiffness and a lightweight structure. In this study, a shape memory alloy(SMA) reinforced composite actuator is presented. This actuator is used to generate large deformations in single lightweight structures and can be used in applications requiring a high degree of adaptability to various external conditions. The proposed actuator consists of numerous individual laminas of the glass-fiber fabric that are embedded in a polymeric matrix. To characterize its deformation behavior, the composition of the actuator was changed by changing the matrix material and the number of the glass-fiber fabric layers. In addition, current of various magnitudes were applied to each actuator to study the effect of the heating of SMA wires on applying current.

  15. Composite scalar contributions to the anomalous magnetic moments

    International Nuclear Information System (INIS)

    Stremnitzer, H.

    1984-01-01

    It is shown that the composite scalars recently introduced to explain the high Z 0 → e + e - γ rate contribute too much to the lepton anomalous magnetic moments, unless one uses very accurate chiral symmetry or composite models with two preonic scales. (Author)

  16. Measuring spectroscopy and magnetism of extracted and intracellular magnetosomes using soft X-ray ptychography.

    Science.gov (United States)

    Zhu, Xiaohui; Hitchcock, Adam P; Bazylinski, Dennis A; Denes, Peter; Joseph, John; Lins, Ulysses; Marchesini, Stefano; Shiu, Hung-Wei; Tyliszczak, Tolek; Shapiro, David A

    2016-12-20

    Characterizing the chemistry and magnetism of magnetotactic bacteria (MTB) is an important aspect of understanding the biomineralization mechanism and function of the chains of magnetosomes (Fe 3 O 4 nanoparticles) found in such species. Images and X-ray absorption spectra (XAS) of magnetosomes extracted from, and magnetosomes in, whole Magnetovibrio blakemorei strain MV-1 cells have been recorded using soft X-ray ptychography at the Fe 2p edge. A spatial resolution of 7 nm is demonstrated. Precursor-like and immature magnetosome phases in a whole MV-1 cell were visualized, and their Fe 2p spectra were measured. Based on these results, a model for the pathway of magnetosome biomineralization for MV-1 is proposed. Fe 2p X-ray magnetic circular dichroism (XMCD) spectra have been derived from ptychography image sequences recorded using left and right circular polarization. The shape of the XAS and XMCD signals in the ptychographic absorption spectra of both sample types is identical to the shape and signals measured with conventional bright-field scanning transmission X-ray microscope. A weaker and inverted XMCD signal was observed in the ptychographic phase spectra of the extracted magnetosomes. The XMCD ptychographic phase spectrum of the intracellular magnetosomes differed from the ptychographic phase spectrum of the extracted magnetosomes. These results demonstrate that spectro-ptychography offers a superior means of characterizing the chemical and magnetic properties of MTB at the individual magnetosome level.

  17. High-frequency electromagnetic properties of soft magnetic metal-polyimide hybrid thin films

    Energy Technology Data Exchange (ETDEWEB)

    Kim, Sang Woo [Nano-Materials Research Center, Korea Institute of Science and Technology, 39-1 Haweoulgog-dong, Sungbuk-gu, Seoul 136-791 (Korea, Republic of)]. E-mail: swkim@kist.re.kr; Yoon, Chong S. [Division of Advanced Materials Science, Hanyang University, Seoul 133-791 (Korea, Republic of)

    2007-09-15

    Although there are a lot of demands for suppression of unwanted high-frequency electromagnetic noise in highly integrated electronic devices such as mobile phones and notebook computers, electromagnetic thin films that effectively work in the high-frequency range have still been underdeveloped. Soft magnetic metal-polyimide (PI) hybrid films with high electrical resistivity were prepared by thermal imidization and selective oxidation between the metal alloy layer and polyamic acid (PAA) layer. Electromagnetic properties of the hybrid thin films in the radio-frequency range were characterized by using the microstrip line method and were correlated with their material parameters. Although anisotropy field of the CoFe/NiFe hybrid film was two times lower than that of the NiFe hybrid film, the saturation magnetization of the CoFe/NiFe hybrid film was three times higher than that of the NiFe hybrid film. The CoFe/NiFe hybrid film showed higher power loss in the frequency range of 3-6 GHz compared to the NiFe hybrid film. The high power loss of the CoFe/NiFe hybrid film was caused by high relative permeability and high ferromagnetic resonance (FMR) frequency due to high saturation magnetization.

  18. High-frequency electromagnetic properties of soft magnetic metal-polyimide hybrid thin films

    International Nuclear Information System (INIS)

    Kim, Sang Woo; Yoon, Chong S.

    2007-01-01

    Although there are a lot of demands for suppression of unwanted high-frequency electromagnetic noise in highly integrated electronic devices such as mobile phones and notebook computers, electromagnetic thin films that effectively work in the high-frequency range have still been underdeveloped. Soft magnetic metal-polyimide (PI) hybrid films with high electrical resistivity were prepared by thermal imidization and selective oxidation between the metal alloy layer and polyamic acid (PAA) layer. Electromagnetic properties of the hybrid thin films in the radio-frequency range were characterized by using the microstrip line method and were correlated with their material parameters. Although anisotropy field of the CoFe/NiFe hybrid film was two times lower than that of the NiFe hybrid film, the saturation magnetization of the CoFe/NiFe hybrid film was three times higher than that of the NiFe hybrid film. The CoFe/NiFe hybrid film showed higher power loss in the frequency range of 3-6 GHz compared to the NiFe hybrid film. The high power loss of the CoFe/NiFe hybrid film was caused by high relative permeability and high ferromagnetic resonance (FMR) frequency due to high saturation magnetization

  19. Magnetization reversal and exchange bias effects in hard/soft ferromagnetic bilayers with orthogonal anisotropies

    International Nuclear Information System (INIS)

    Navas, D; Ross, C A; Torrejon, J; Béron, F; Pirota, K R; Redondo, C; Sierra, B; Castaño, F; Batallan, F; Toperverg, B P; Devishvili, A

    2012-01-01

    The magnetization reversal processes are discussed for exchange-coupled ferromagnetic hard/soft bilayers made from Co 0.66 Cr 0.22 Pt 0.12 (10 and 20 nm)/Ni (from 0 to 40 nm) films with out-of-plane and in-plane magnetic easy axes respectively, based on room temperature hysteresis loops and first-order reversal curve analysis. On increasing the Ni layer thicknesses, the easy axis of the bilayer reorients from out-of-plane to in-plane. An exchange bias effect, consisting of a shift of the in-plane minor hysteresis loops along the field axis, was observed at room temperature after in-plane saturation. This effect was associated with specific ferromagnetic domain configurations experimentally determined by polarized neutron reflectivity. On the other hand, perpendicular exchange bias effect was revealed from the out-of-plane hysteresis loops and it was attributed to residual domains in the magnetically hard layer. (paper)

  20. Thermal characterization of magnetically aligned carbonyl iron/agar composites.

    Science.gov (United States)

    Diaz-Bleis, D; Vales-Pinzón, C; Freile-Pelegrín, Y; Alvarado-Gil, J J

    2014-01-01

    Composites of magnetic particles into polymeric matrices have received increasing research interest due to their capacity to respond to external magnetic or electromagnetic fields. In this study, agar from Gelidium robustum has been chosen as natural biocompatible polymer to build the matrix of the magnetic carbonyl iron particles (CIP) for their uses in biomedical fields. Heat transfer behavior of the CIP-agar composites containing different concentrations (5, 10, 15, 20, 25 and 30% w/w) of magnetically aligned and non-aligned CIP in the agar matrix was studied using photothermal radiometry (PTR) in the back-propagation emission configuration. The morphology of the CIP-agar composites with aligned and non-aligned CIP under magnetic field was also evaluated by scanning electron microscopy (SEM). The results revealed a dominant effect of CIP concentration over the alignment patterns induced by the magnetic field, which agrees with the behavior of the thermal diffusivity and thermal conductivity. Agar served as a perfect matrix to be used with CIP, and CIP-agar composites magnetically aligned at 20% CIP concentration can be considered as promising 'smart' material for hyperthermia treatments in the biomedical field. Copyright © 2013 Elsevier Ltd. All rights reserved.

  1. Application of advanced composites in tokamak magnet systems

    International Nuclear Information System (INIS)

    Long, C.J.

    1977-11-01

    The use of advanced (high-modulus) composites in superconducting magnets for tokamak fusion reactors is discussed. The most prominent potential application is as the structure in the pulsed poloidal-field coil system, where a significant reduction in eddy currents could be achieved. Present low-temperature data on the advanced composites are reviewed briefly; they are too meager to do more than suggest a broad class of composites for a particular application

  2. Development of high magnetic field soft X-ray spectroscopy and its application to the study of surface and interface

    International Nuclear Information System (INIS)

    Nakamura, Tetsuya; Narumi, Yasuo

    2014-01-01

    Magnetic materials are generally synthesized and used as alloys and compounds. They are also stacked as a multilayer film for spintronics device such as a reading-head sensor of a hard disk drive. The evaluation of magnetization is the most fundamental characterization in studies of magnetic materials. Especially, in alloys and compounds involving more than two magnetic elements, a partial magnetization with respect to each element, we call as an element specific magnetization, promises to provide the deeper understanding of their magnetic property. X-ray magnetic circular dichroism (XMCD) in absorption spectroscopy provides an element specific magnetization. As XMCD became increasingly popular, high-magnetic-field environment for XMCD measurements also became very important in order to investigate paramagnetic, antiferromagnetic, and meta-magnetic materials. Under the circumstance, a high-magnetic-field XMCD measurement technique of the soft-X-ray regime has been developed using a non-destructive pulse magnet having capability of generating 40 T at the twin helical undulators beamline, BL25SU, of SPring-8. In this review, we first introduce the concept and the technical features of high magnetic field XMCD and then show recent examples of the experiments. (author)

  3. 'Optical' soft x-ray arrays for fluctuation diagnostics in magnetic fusion energy experiments

    International Nuclear Information System (INIS)

    Delgado-Aparicio, L.F.; Stutman, D.; Tritz, K.; Finkenthal, M.; Kaita, R.; Roquemore, L.; Johnson, D.; Majeski, R.

    2004-01-01

    We are developing large pixel count, fast (≥100 kHz) and continuously sampling soft x-ray (SXR) array for the diagnosis of magnetohydrodynamics (MHD) and turbulent fluctuations in magnetic fusion energy plasmas. The arrays are based on efficient scintillators, high thoughput multiclad fiber optics, and multichannel light amplification and integration. Compared to conventional x-ray diode arrays, such systems can provide vastly increased spatial coverage, and access to difficult locations with small neutron noise and damage. An eight-channel array has been built using columnar CsI:Tl as an SXR converter and a multianode photomultiplier tube as photoamplifier. The overall system efficiency is measured using laboratory SXR sources, while the time response and signal-to-noise performance have been evaluated by recording MHD activity from the spherical tori (ST) Current Drive Experiment-Upgrade and National Spherical Torus Experiment, both at Princeton Plasma Physics Laboratory

  4. Nanostructured magnetic alginate composites for biomedical applications

    Energy Technology Data Exchange (ETDEWEB)

    Bedê, Pedro Marins; Silva, Marcelo Henrique Prado da; Figueiredo, André Ben-Hur da Silva, E-mail: marceloprado@ime.eb.br [Instituto Militar de Engenharia (IME), Rio de Janeiro, RJ (Brazil); Finotelli, Priscilla Vanessa [Universidade Federal do Rio de Janeiro (UFRJ), Rio de Janeiro, RJ (Brazil). Faculdade de Farmácia

    2017-07-01

    This is a study of the preparation and characterization of polymeric-magnetic nanoparticles. The nanoparticles used were magnetite (Fe{sub 3}O{sub 4} ) and the chosen polymers were alginate and chitosan. Two types of samples were prepared: uncoated magnetic nanoparticles and magnetic nanoparticles encapsulated in polymeric matrix. The samples were analyzed by XRD, light scattering techniques, TEM, and magnetic SQUID. The XRD patterns identified magnetite (Fe{sub 3}O{sub 4} ) as the only crystalline phase. TEM analyses showed particle sizes between 10 and 20nm for magnetite, and 15 and 30nm for the encapsulated magnetite. The values of magnetization ranged from 75 to 100emu/g for magnetite nanoparticles, and 8 to 12emu/g for coated with chitosan, at different temperatures of 20K and 300K. The saturation of both samples was in the range of 49 to 50KOe. Variations of results between the two kinds of samples were attributed to the encapsulation of magnetic nanoparticles by the polymers. (author)

  5. Innovative soft magnetic multilayers with enhanced in-plane anisotropy and ferromagnetic resonance frequency for integrated RF passive devices

    Directory of Open Access Journals (Sweden)

    Claudiu V. Falub

    2018-04-01

    Full Text Available We present an innovative, economical method for manufacturing soft magnetic materials that may pave the way for integrated thin film magnetic cores with dramatically improved properties. Soft magnetic multilayered thin films based on the Fe-28%Co20%B (at.% and Co-4.5%Ta4%Zr (at.% amorphous alloys are deposited on 8” bare Si and Si/200nm-thermal-SiO2 wafers in an industrial, high-throughput Evatec LLS EVO II magnetron sputtering system. The multilayers consist of stacks of alternating 80-nm-thick ferromagnetic layers and 4-nm-thick Al2O3 dielectric interlayers. Since in our dynamic sputter system the substrate cage rotates continuously, such that the substrates face different targets alternatively, each ferromagnetic sublayer in the multilayer consists of a fine structure comprising alternating CoTaZr and FeCoB nanolayers with very sharp interfaces. We adjust the thickness of these individual nanolayers between 0.5 and 1.5 nm by changing the cage rotation speed and the power of each gun, which is an excellent mode to engineer new, composite ferromagnetic materials. Using X-ray reflectometry (XRR we reveal that the interfaces between the FeCoB and CoTaZr nanolayers are perfectly smooth with roughness of 0.2-0.3 nm. Kerr magnetometry and B-H looper measurements for the as-deposited samples show that the coercivity of these thin films is very low, 0.2-0.3 Oe, and gradually scales up with the thickness of FeCoB nanolayers, i.e. with the increase of the overall Fe content from 0 % (e.g. CoTaZr-based multilayers to 52 % (e.g. FeCoB-based multilayers. We explain this trend in the random anisotropy model, based on considerations of grain size growth, as revealed by glancing angle X-ray diffraction (GAXRD, but also because of the increase of magnetostriction with the increase of Fe content as shown by B-H looper measurements performed on strained wafers. The unexpected enhancement of the in-plane anisotropy field from 18.3 Oe and 25.8 Oe for the

  6. Structure and properties of bulk amorphous magnetically soft coatings prepared by plasma spraying

    International Nuclear Information System (INIS)

    Kalita, V.I.; Kekalo, I.B.; Komlev, D.I.; Taranichev, V.E.

    1995-01-01

    Co-Ni-Fe-Si-B composition plasma coatings consisting of amorphous disk-shaped particles forming the bulk of a coating, of crystalline particles and of a threshold space, were studied. Iron and metalloid distribution heterogeneous by the thickness represents a peculiar feature for coating amorphous particles. Structure of coatings and their magnetic properties depend on some technological parameters. Conclusion is made that at annealing the variation of magnetic properties is determined by the processes of directed ordering and stratification of amorphous phase, while the low level of the initial magnetic properties of coatings is caused alongside with structure peculiarities, by occurrence of independent fine-dispersive domain structure in each disk-shaped amorphous phase. 14 refs., 8 figs., 6 tabs

  7. Iron losses evaluation in soft magnetic materials with a sinusoidal voltage supply

    DEFF Research Database (Denmark)

    Nedelcu, Steluţa; Ritchie, Ewen; Leban, Krisztina Monika

    2013-01-01

    This paper presents an evaluation method of for specific iron losses in non-oriented laminated steel suitable for electric motors and transformers in the case of a sinusoidal excitation. The model is based on the separation of loss contribution due to hysteresis, eddy currents and excess losses...... (between 0.35 mm and 0.65 mm) and alloy compositions. Hysteresis and eddy currents loss coefficients have been considered as dependent on the frequency. For curve fitting of these coefficients third and fourth polynomials were employed, with good result for all the frequencies and magnetic flux density...... and it is proposing an identification procedure for the model coefficients from multi-frequency single sheet tests. The frequencies used are in the range 10 Hz and 150 Hz and with the values of magnetic flux density in the range 0.1 T and 1.4 T. The model was applied on six magnetic materials of different thicknesses...

  8. Time of isothermal holding in the course of in-air heat treatment of soft magnetic Fe-based amorphous alloys and their magnetic properties

    Science.gov (United States)

    Skulkina, N. A.; Ivanov, O. A.; Pavlova, I. O.; Minina, O. A.

    2011-12-01

    On the example of soft magnetic Fe81B13Si4C2 and Fe77Ni1Si9B13 amorphous alloys, the relation between the level of magnetic properties and duration of isothermal holding in the course of heat treatment in air has been studied. The optimum temperature-dependent time τ of isothermal holding has been shown to be related to the volume fraction of domains ( V orth) with orthogonal magnetization in the initial (quenched) ribbon by equation V orth = ττ1/3. A temperature dependence of the proportionality coefficient α, which determines the degree of diffusion-process activity, has been determined. The results obtained allow us to substantially simplify the choice of optimum conditions of atmospheric heat treatment of soft magnetic Fe-based amorphous ribbons.

  9. Magnetism of triangular nanoflakes with different compositions and edge terminations

    International Nuclear Information System (INIS)

    Zhang Shunhong; Zhou Jian; Li Xiaowei; Wang Qian

    2012-01-01

    Since the discovery of the giant magnetoresistance effect, extensive research has been devoted to finding new materials for spintronic devices. The hotly pursued nanostructure-based magnetic materials are potential candidates for such applications. Among them, graphene triangular nanoflakes (G-TNFs), due to their special magnetic configurations, can serve as building blocks for design of new C-based magnetic materials. This motivates the present study to systematically investigate how magnetism of the TNFs changes with their edge termination, composition, and atomic distribution. Using density functional theory, we show that the F-terminated G-TNFs have similar magnetic behavior to the H-terminated G-TNFs. Besides the edge terminations, partially hydrogenation of interior C atoms in the G-TNFs breaks the conjugate π orbitals and thus leads to extra net magnetic moment. The IV-group binary SiC-TNFs resemble the G-TNFs in magnetic properties, while the III–V group binary BN- and AlN-TNFs are different although they also have honeycomb structures. The different magnetic behaviors originate from the different occupations of p z atomic orbitals and the resulting change of conjugate π molecular orbitals. This study provides physical insight on tuning the magnetic behavior of TNFs through controlling their composition, size, and edge termination.

  10. Induced magnetic anisotropy in Si-free nanocrystalline soft magnetic materials: A transmission x-ray diffraction study

    Energy Technology Data Exchange (ETDEWEB)

    Parsons, R., E-mail: rparsons01@gmail.com; Suzuki, K. [Department of Materials Science and Engineering, Monash University, Clayton, Victoria 3800 (Australia); Yanai, T. [Graduate School of Engineering, Nagasaki University, Nagasaki 852-8521 (Japan); Kishimoto, H.; Kato, A. [Toyota Motor Corporation, Mishuku, Susono, Shizuoka 410-1193 (Japan); Ohnuma, M. [Faculty and Graduate School of Engineering, Hokkaido University, Sapporo 060-8628 (Japan)

    2015-05-07

    In order to better understand the origin of field-induced anisotropy (K{sub u}) in Si-free nanocrystalline soft magnetic alloys, the lattice spacing of the bcc-Fe phase in nanocrystalline Fe{sub 94−x}Nb{sub 6}B{sub x} (x = 10, 12, 14) alloys annealed under an applied magnetic field has been investigated by X-ray diffraction in transmission geometry (t-XRD) with the diffraction vector parallel and perpendicular to the field direction. The saturation magnetostriction (λ{sub s}) of nanocrystalline Fe{sub 94−x}Nb{sub 6}B{sub x} was found to increase linearly with the volume fraction of the residual amorphous phase and is well described by taking into account the volume-weighted average of two local λ{sub s} values for the bcc-Fe nanocrystallites (−5 ± 2 ppm) and the residual amorphous matrix (+8 ± 2 ppm). The lattice distortion required to produce the measured K{sub u} values (∼100 J/m{sup 3}) was estimated via the inverse magnetostrictive effect using the measured λ{sub s} values and was compared to the lattice spacing estimations made by t-XRD. The lattice strain required to produce K{sub u} under the magnetoelastic model was not observed by the t-XRD experiments and so the findings of this study suggest that the origin of magnetic field induced K{sub u} cannot be explained through the magnetoelastic effect.

  11. 3D printed magnetic polymer composite transformers

    Science.gov (United States)

    Bollig, Lindsey M.; Hilpisch, Peter J.; Mowry, Greg S.; Nelson-Cheeseman, Brittany B.

    2017-11-01

    The possibility of 3D printing a transformer core using fused deposition modeling methods is explored. With the use of additive manufacturing, ideal transformer core geometries can be achieved in order to produce a more efficient transformer. In this work, different 3D printed settings and toroidal geometries are tested using a custom integrated magnetic circuit capable of measuring the hysteresis loop of a transformer. These different properties are then characterized, and it was determined the most effective 3D printed transformer core requires a high fill factor along with a high concentration of magnetic particulate.

  12. Fabrication of wrist-like SMA-based actuator by double smart soft composite casting

    Science.gov (United States)

    Rodrigue, Hugo; Wei, Wang; Bhandari, Binayak; Ahn, Sung-Hoon

    2015-12-01

    A new manufacturing method for smart soft composite (SSC) actuators that consists of double casting a SSC actuator to produce an actuator with non-linear shape memory alloy (SMA) wire positioning is proposed. This method is used to manufacture a tube-shaped SSC actuator in which the SMA wires follow the curvature of the tube and is capable of pure-twisting deformations while sustaining a cantilever load. The concept is tested by measuring the maximum twisting angle and a simple control method is proposed to control the twisting angle of the actuator. Then, a soft robotic wrist with a length of 18 cm is built, its load-carrying capability is tested by measuring the cantilever force required for deforming the actuator, and its load-carrying capability during actuation is tested by loading one end with different objects and actuating the actuator. This wrist actuator shows good repeatability, is capable of twisting deformations up to 25° while holding objects weighing 100 g, and can sustain loads above 2 N without undergoing buckling.

  13. Fused filament 3D printing of ionic polymer-metal composites for soft robotics

    Science.gov (United States)

    Carrico, James D.; Leang, Kam K.

    2017-04-01

    Additive manufacturing techniques are used to create three-dimensional structures with complex shapes and features from polymer and/or metal materials. For example, fused filament three-dimensional (3D) printing utilizes non-electroactive polymers, such as acrylonitrile butadiene styrene (ABS) and polylactic acid (PLA), to build structures and components in a layer-by-layer fashion for a wide variety of applications. Presented here is a summary of recent work on a fused filament 3D-printing technique to create 3D ionic polymer-metal composite (IPMC) structures for applications in soft robotics. The 3D printing technique overcomes some of the limitations of existing manufacturing processes for creating IPMCs, such as limited shapes and sizes and time-consuming manufacturing steps. In the process described, first a precursor material (non-acid Nafion precursor resin) is extruded into a thermoplastic filament for 3D printing. Then, a custom-designed 3D printer is described that utilizes the precursor filament to manufacture custom-shaped structures. Finally, the 3D-printed samples are functionalized by hydrolyzing them in an aqueous solution of potassium hydroxide and dimethyl sulfoxide, followed by application of platinum electrodes. Presented are example 3D-printed single and multi-degree-of-freedom IPMC actuators and characterization results, as well as example soft-robotic devices to demonstrate the potential of this process.

  14. Fabrication of wrist-like SMA-based actuator by double smart soft composite casting

    International Nuclear Information System (INIS)

    Rodrigue, Hugo; Wei, Wang; Bhandari, Binayak; Ahn, Sung-Hoon

    2015-01-01

    A new manufacturing method for smart soft composite (SSC) actuators that consists of double casting a SSC actuator to produce an actuator with non-linear shape memory alloy (SMA) wire positioning is proposed. This method is used to manufacture a tube-shaped SSC actuator in which the SMA wires follow the curvature of the tube and is capable of pure-twisting deformations while sustaining a cantilever load. The concept is tested by measuring the maximum twisting angle and a simple control method is proposed to control the twisting angle of the actuator. Then, a soft robotic wrist with a length of 18 cm is built, its load-carrying capability is tested by measuring the cantilever force required for deforming the actuator, and its load-carrying capability during actuation is tested by loading one end with different objects and actuating the actuator. This wrist actuator shows good repeatability, is capable of twisting deformations up to 25° while holding objects weighing 100 g, and can sustain loads above 2 N without undergoing buckling. (paper)

  15. Composite Materials with Magnetically Aligned Carbon Nanoparticles Having Enhanced Electrical Properties and Methods of Preparation

    Science.gov (United States)

    Hong, Haiping (Inventor); Peterson, G.P. (Bud) (Inventor); Salem, David R. (Inventor)

    2016-01-01

    Magnetically aligned carbon nanoparticle composites have enhanced electrical properties. The composites comprise carbon nanoparticles, a host material, magnetically sensitive nanoparticles and a surfactant. In addition to enhanced electrical properties, the composites can have enhanced mechanical and thermal properties.

  16. Composite Materials with Magnetically Aligned Carbon Nanoparticles and Methods of Preparation

    Science.gov (United States)

    Hong, Haiping (Inventor); Peterson, G.P. (Bud) (Inventor); Salem, David R. (Inventor)

    2018-01-01

    The present invention relates to magnetically aligned carbon nanoparticle composites and methods of preparing the same. The composites comprise carbon nanoparticles, host material, magnetically sensitive nanoparticles and surfactant. The composites may have enhanced mechanical, thermal, and/or electrical properties.

  17. Temperature dependence of microwave absorption phenomena in single and biphase soft magnetic microwires

    Energy Technology Data Exchange (ETDEWEB)

    El Kammouni, Rhimou, E-mail: elkammounirhimou@gmail.com [Instituto de Ciencia de Materiales de Madrid, CSIC, 28049 Madrid (Spain); Vázquez, Manuel [Instituto de Ciencia de Materiales de Madrid, CSIC, 28049 Madrid (Spain); Lezama, Luis [Depto. Química Inorgánica, Universidad País Vasco, UPV/EHU, Bilbao (Spain); Kurlyandskaya, Galina [Depto. Electricidad y Electrónica, Universidad País Vasco, UPV/EHU, Bilbao (Spain); Dept. Magnetism and Magnetic Nanomaterials, Ural Federal University, Ekaterinburg (Russian Federation); Kraus, Ludek [Institute of Physics, Academy of Sciences of the Czech Republic, Prague (Czech Republic)

    2014-11-15

    The microwave absorption phenomena of single and biphase magnetic microwires with soft magnetic behavior have been investigated as a function of DC applied magnetic field using two alternative techniques: (i) absorption measurements in the temperature range of 4–300 K using a spectrometer operating at X-band frequency, at 9.5 GHz, and (ii) room-temperature, RT, ferromagnetic resonance measurements in a network analyzer in the frequency range up to 20 GHz. Complementary low-frequency magnetic characterization was performed in a Vibrating Sample Magnetometer. Studies have been performed for 8 μm diameter small-magnetostriction amorphous CoFeSiB single-phase microwire, coated by micrometric Pyrex layer, and after electroplating an external shell, 2 µm or 4 µm thick, of FeNi alloys. For single phase CoFeSiB microwire, a single absorption is observed, whose DC field dependence of resonance frequency at RT fits to a Kittel-law behavior for in-plane magnetized thin film. The temperature dependence behavior shows a monotonic increase in the resonance field, H{sub r}, with temperature. A parallel reduction of the circular anisotropy field, H{sub K}, is deduced from the temperature dependence of hysteresis loops. For biphase, CoFeSiB/FeNi, microwires, the absorption phenomena at RT also follow the Kittel condition. The observed opposite evolution with temperature of resonance field, H{sub r}, in 2 and 4 µm thick FeNi samples is interpreted considering the opposite sign of magnetostriction of the respective FeNi layers. The stress-induced magnetic anisotropy field, H{sub K}, in the FeNi shell is deduced to change sign at around 130 K. - Highlights: • A single absorption phenomenon is observed for single phase CoFeSiB. • The T dependence of the microwave behavior shows a monotonic increase of H{sub r} with T. • The absorption at RT follows the Kittel condition for biphase CoFe/FeNi microwires. • The T dependence of resonant field of CoFe/FeNi is interpreted to be

  18. Tracking the harmonic response of magnetically-soft sensors for wireless temperature, stress, and corrosive monitoring

    Science.gov (United States)

    Ong, Keat G.; Grimes, Craig A.

    2002-01-01

    This paper describes the application of magnetically-soft ribbon-like sensors for measurement of temperature and stress, as well as corrosive monitoring, based upon changes in the amplitudes of the higher-order harmonics generated by the sensors in response to a magnetic interrogation signal. The sensors operate independently of mass loading, and so can be placed or rigidly embedded inside nonmetallic, opaque structures such as concrete or plastic. The passive harmonic-based sensor is remotely monitored through a single coplanar interrogation and detection coil. Effects due to the relative location of the sensor are eliminated by tracking harmonic amplitude ratios, thereby, enabling wide area monitoring. The wireless, passive, mass loading independent nature of the described sensor platform makes it ideally suited for long-term structural monitoring applications, such as measurement of temperature and stress inside concrete structures. A theoretical model is presented to explain the origin and behavior of the higher-order harmonics in response to temperature and stress. c2002 Elsevier Science B.V. All rights reserved.

  19. A turtle-like swimming robot using a smart soft composite (SSC) structure

    International Nuclear Information System (INIS)

    Kim, Hyung-Jung; Song, Sung-Hyuk; Ahn, Sung-Hoon

    2013-01-01

    This paper describes the development of a biomimetic swimming robot based on the locomotion of a marine turtle. To realize the smooth, soft flapping motions of this type of turtle, a novel actuator was also developed, using a smart soft composite (SSC) structure that can generate bending and twisting motions in a simple, lightweight structure. The SSC structure is a composite consisting of an active component to generate the actuation force, a passive component to determine the twisting angle of the structure, and a matrix to combine the components. The motion of such a structure can be designed by specifying the angle between a filament of the scaffold structure and a shape-memory alloy (SMA) wire. The bending and twisting motion of the SSC structure is explained in terms of classical laminate theory, and cross-ply and angled-ply structures were fabricated to evaluate its motion. Finally, the turtle-like motion of a swimming robot was realized by employing a specially designed SSC structure. To mimic the posterior positive twisting angle of a turtle’s flipper during the upstroke, the SMA wire on the upper side was offset, and a positive ply-angled scaffold was used. Likewise, for the anterior negative twisting angle of the flipper during the downstroke, an offset SMA wire on the lower side and a positive ply-angled scaffold were also required. The fabricated flipper’s length is 64.3 mm and it realizes 55 mm bending and 24° twisting. The resulting robot achieved a swimming speed of 22.5 mm s −1 . (paper)

  20. Influence of thermal debinding on the final properties of Fe–Si soft magnetic alloys for metal injection molding (MIM)

    Energy Technology Data Exchange (ETDEWEB)

    Páez-Pavón, A.; Jiménez-Morales, A. [Dpto. Ciencia e Ing. de materiales e Ing. Química, Universidad Carlos III de Madrid, 28911 Leganés, Madrid (Spain); Santos, T.G. [UNIDEMI, Departamento de Engenharia Mecânica e Industrial, Faculdade de Ciências e Tecnologia, Universidade Nova de Lisboa, 2829-516 Caparica (Portugal); Quintino, L. [Instituto Superior Técnico, Universidade de Lisboa, 1049-001 Lisboa (Portugal); Torralba, J.M. [Dpto. Ciencia e Ing. de materiales e Ing. Química, Universidad Carlos III de Madrid, 28911 Leganés, Madrid (Spain)

    2016-10-15

    Metal injection molding (MIM) may be used to produce soft magnetic materials with optimal mechanical and magnetic properties. Unlike other techniques, MIM enables the production of complex and small Fe–Si alloy parts with silicon contents greater than 3% by weight. In MIM process development, it is critical to design a proper debinding cycle not only to ensure complete removal of the binder system but also to obtain improved properties in the final part. This work is a preliminary study on the production of Fe-3.8Si soft magnetic parts by MIM using pre-alloyed powders and a non-industrialized binder. Two different heating rates during thermal debinding were used to study their effect on the final properties of the part. The final properties of the sintered parts are related to thermal debinding. It has been demonstrated that the heating rate during thermal debinding has a strong influence on the final properties of Fe–Si soft magnetic alloys. - Highlights: • The properties of MIM Fe-Si alloy are influenced by the debinding heating rate. • The slow debinding led to a lower porosity, lower oxygen content and grain growth. • The magnetization of the sintered samples improved after a slow thermal debinding.

  1. Magnetic force driven magnetoelectric effect in bi-cantilever composites

    Science.gov (United States)

    Zhang, Ru; Wu, Gaojian; Zhang, Ning

    2017-12-01

    The magnetic force driven magnetoelectric (ME) effect in bi-cantilever Mn-Zn-Ferrite /PZT composites is presented. Compared with single cantilever, the ME voltage coefficient in bi-cantilever composite is a little lower and the resonance frequency is higher, but the bi-cantilever structure is advantageous for integration. When the magnetic gap is 3 mm, the ME voltage coefficient can achieve 6.2 Vcm-1Oe-1 at resonance under optimum bias field Hm=1030 Oe; when the magnetic gap is 1.5 mm, the ME voltage coefficient can get the value as high as 4.4 Vcm-1Oe-1 under much lower bias field H=340 Oe. The stable ME effect in bi-cantilever composites has important potential application in the design of new type ME device.

  2. Transition from reversible to irreversible magnetic exchange-spring processes in antiferromagnetically exchange-coupled hard/soft/hard trilayer structures

    International Nuclear Information System (INIS)

    Wang Xiguang; Guo Guanghua; Zhang Guangfu

    2011-01-01

    The demagnetization processes of antiferromagnetically exchange-coupled hard/soft/hard trilayer structures have been studied based on the discrete one-dimensional atomic chain model and the linear partial domain-wall model. It is found that, when the magnetic anisotropy of soft layer is taken into account, the changes of the soft layer thickness and the interfacial exchange coupling strength may lead a transition of demagnetization process in soft layer from the reversible to the irreversible magnetic exchange-spring process. For the trilayer structures with very thin soft layer, the demagnetization process exhibits typical reversible exchange-spring behavior. However, as the thickness of soft layer is increased, there is a crossover point t c , after which the process becomes irreversible. Similarly, there is also a critical interfacial exchange coupling constant A sh c , above which the exchange-spring process is reversible. When A sh sh c , the irreversible exchange-spring process is achieved. The phase diagram of reversible and irreversible exchange-spring processes is mapped in the plane of the interfacial exchange coupling A sh and soft layer thickness N s . - Research highlights: → A differing magnetic exchange-spring process is found in antiferromagnetically exchange-coupled hard/soft/hard trilayers if the magnetic anisotropy of the soft layers is taken into account. → The change of the soft layer thickness may lead to a transition of demagnetization process in soft layer from the reversible to the irreversible exchange-spring process. → The change of the soft-hard interfacial exchange coupling strength may lead a transition of demagnetization process in soft layer from the reversible to the irreversible exchange-spring process. → The phase diagram of reversible and irreversible exchange-spring processes is mapped in the plane of the interfacial exchange coupling and soft layer thickness.

  3. A comparative study between magnetic resonance imaging and histological findings of bone and soft tissue tumors

    International Nuclear Information System (INIS)

    Itoh, Koichi

    1995-01-01

    Diagnostic methodology for bone and soft tissue tumors has made great strides recently through the development of magnetic resonance imaging (MRI). Here we report a comparative assessment of the histological findings of bone and soft tissue tumors with MRI from 212 cases. The accuracy of a qualitative diagnosis was observed in a solitary bone cyst, enchondroma, giant cell tumor, chondrosarcoma, lipoma, hemangioma, neurinoma, and in a synovial cyst. However, the qualitative diagnosis of a malignant tumor was difficult because of the variety of the intratumoral histological changes. An enhanced-image using Gd-DTPA was useful for differentiation of the viable region in the internal area of a tumor, discrimination of the reactive zone of an edema or assessing vascularity, and for discrimination between a cyst and a solid tumor. Based on comparison with findings from the excised specimen, it was found that histological changes such as calcification, fibrosis, hemorrhaging and necrosis, and the presence or absence of a tumor capsule had been reflected accurately on MR images. However, infiltration of the tumor into the bone cortex and into the articular cartilage were found frequently to be false-positive on MRI. Although problems remained to be solved regarding the evaluation of the presence or absence of tumor infiltration into adjacent tissue, the depiction of periosteal reaction, and regarding differentiation from inflammatory disease, MRI was a very useful information source for operative planning because it could evaluate the relationship between the tumor and adjacent blood vessels or nerves, the effect of preoperative therapy, and effectively discriminate between benign and malignant tumors. (author)

  4. Thermoresponsive magnetic composite nanomaterials for multimodal cancer therapy.

    Science.gov (United States)

    Purushotham, S; Ramanujan, R V

    2010-02-01

    The synthesis, characterization and property evaluation of drug-loaded polymer-coated magnetic nanoparticles (MNPs) relevant to multimodal cancer therapy has been studied. The hyperthermia and controlled drug release characteristics of these particles was examined. Magnetite (Fe(3)O(4))-poly-n-(isopropylacrylamide) (PNIPAM) composite MNPs were synthesized in a core-shell morphology by dispersion polymerization of n-(isopropylacrylamide) chains in the presence of a magnetite ferrofluid. These core-shell composite particles, with a core diameter of approximately 13nm, were loaded with the anti-cancer drug doxorubicin (dox), and the resulting composite nanoparticles (CNPs) exhibit thermoresponsive properties. The magnetic properties of the composite particles are close to those of the uncoated magnetic particles. In an alternating magnetic field (AMF), composite particles loaded with 4.15 wt.% dox exhibit excellent heating properties as well as simultaneous drug release. Drug release testing confirmed that release was much higher above the lower critical solution temperature (LCST) of the CNP, with a release of up to 78.1% of bound dox in 29h. Controlled drug release testing of the particles reveals that the thermoresponsive property can act as an on/off switch by blocking drug release below the LCST. Our work suggests that these dox-loaded polymer-coated MNPs show excellent in vitro hyperthermia and drug release behavior, with the ability to release drugs in the presence of AMF, and the potential to act as agents for combined targeting, hyperthermia and controlled drug release treatment of cancer.

  5. Soft and hard natures of Nd2Fe14B permanent magnet explored by first-order-reversal-curves

    International Nuclear Information System (INIS)

    Chen, Po-An; Yang, Chao-Yao; Chang, Shu-Jui; Lee, Min-Han; Tang, Nai-Kuang; Yen, Sheng-Chan; Tseng, Yuan-Chieh

    2014-01-01

    Two commercial Nd 2 Fe 14 B samples, MQP-B and sintered-NdFeB were investigated using synchrotron-based x-ray diffraction and first-order-reversal-curves (FORCs). Despite differing in magnetic and structural properties, the two samples were found to comprise two major ferromagnetic components in FORCs. For the sintered-NdFeB case, the soft component may originate from the intrinsically soft Nd-f site which was coupled with its local Fe atomic environment that differs in magnetic anisotropy from the Nd-g site (intrinsically hard). It may directly originate from the Nd-rich phase or microstructural imperfection, while the former possibility (Nd-f site) appears greater than the latter. While for the MQP-B, the minor second phase resulting from high structural disorder was likely in charge of the presence of the soft component. Sophisticated FORCs analyses revealed the natures of the soft and hard components, soft–hard coupling and switching reversibility of the two cases, irrespective of the origins of their two components. This provides insights to the origin of magnetic stability and reversal dynamics of Nd 2 Fe 14 B that have not been fully understood by conventional magnetic analyses. The coexistence of the two components led to an incoherent reversal undermining the magnetic stability of Nd 2 Fe 14 B. This is a fundamental problem as to why the performance extremity can only be improved finitely through extrinsic tuning. From FORCs simulation we understand that the soft–hard coupling was moderate in a real Nd 2 Fe 14 B compound. A stronger soft–hard coupling is necessary to conquer the anisotropic competition to enable a coherent reversal that will promote the magnetic hardness. - Highlights: • We investigated two commercially available Nd 2 Fe 14 B compounds with FORCs. • The two compounds were found to comprise soft and hard natures. • The coupling between the soft and hard phases is moderate in a real Nd 2 Fe 14 B

  6. Design, fabrication and characterization of an arrayable all-polymer microfluidic valve employing highly magnetic rare-earth composite polymer

    International Nuclear Information System (INIS)

    Rahbar, Mona; Gray, Bonnie L; Shannon, Lesley

    2016-01-01

    We present a new magnetically actuated microfluidic valve that employs a highly magnetic composite polymer (M-CP) containing rare-earth hard-magnetic powder for its actuating element and for its valve seat. The M-CP offers much higher magnetization compared to the soft-magnetic, ferrite-based composite polymers typically used in microfluidic applications. Each valve consists of a permanently magnetized M-CP flap and valve seat mounted on a microfluidic channel system fabricated in poly(dimethylsiloxane) (PDMS). Each valve is actuated under a relatively small external magnetic field of 80 mT provided by a small permanent magnet mounted on a miniature linear actuator. The performance of the valve with different flap thicknesses is characterized. In addition, the effect of the magnetic valve seat on the valve’s performance is also characterized. It is experimentally shown that a valve with a 2.3 mm flap thickness, actuated under an 80 mT magnetic field, is capable of completely blocking liquid flow at a flow rate of 1 ml min −1 for pressures up to 9.65 kPa in microfluidic channels 200 μ m wide and 200 μ m deep. The valve can also be fabricated into an array for flow switching between multiple microfluidic channels under continuous flow conditions. The performance of arrays of valves for flow routing is demonstrated for flow rates up to 5 ml min −1 with larger microfluidic channels of up to 1 mm wide and 500 μ m deep. The design of the valves is compatible with other commonly used polymeric microfluidic components, as well as other components that use the same novel permanently magnetic composite polymer, such as our previously reported cilia-based mixing devices. (paper)

  7. Soft Tendril-Inspired Grippers: Shape Morphing of Programmable Polymer-Paper Bilayer Composites.

    Science.gov (United States)

    Wang, Wei; Li, Chenzhe; Cho, Maenghyo; Ahn, Sung-Hoon

    2018-03-28

    Nastic movements in plants that occur in response to environmental stimuli have inspired many man-made shape-morphing systems. Tendril is an exemplification serving as a parasitic grasping component for the climbing plants by transforming from a straight shape into a coiled configuration via the asymmetric contraction of internal stratiform plant tissues. Inspired by tendrils, this study using a three-dimensional (3D) printing approach developed a class of soft grippers with preprogrammed deformations being capable of imitating the general motions of plant tendrils, including bending, spiral, and helical distortions for grasping. These grippers initially in flat configurations were tailored from a polymer-paper bilayer composite sheet fabricated via 3D printing a polymer on the paper substrate with different patterns. The rough and porous paper surface provides a printed polymer that is well-adhered to the paper substrate which in turn serves as a passive strain-limiting layer. During printing, the melted polymer filament is stretched, enabling the internal strain to be stored in the printed polymer as memory, and then it can be thermally released, which will be concurrently resisted by the paper layer, resulting in various transformations based on the different printed geometries. These obtained transformations were then used for designing grippers to grasp objects with corresponding motions. Furthermore, a fully equipped robotic tendril with three segments was reproduced, where one segment was used for grasping the object and the other two segments were used for forming a tendril-like twistless spring-like structure. This study further helps in the development of soft robots using active polymer materials for engineered systems.

  8. Experimental Investigations on Pulsed Nd:YAG Laser Welding of C17300 Copper-Beryllium and 49Ni-Fe Soft Magnetic Alloys

    International Nuclear Information System (INIS)

    Mousavi, S. A. A. Akbari; Ebrahimzadeh, H.

    2011-01-01

    Copper-beryllium and soft magnetic alloys must be joined in electrical and electro-mechanical applications. There is a high difference in melting temperatures of these alloys which cause to make the joining process very difficult. In addition, copper-beryllium alloys are of age hardenable alloys and precipitations can brittle the weld. 49Ni-Fe alloy is very hot crack sensitive. Moreover, these alloys have different heat transfer coefficients and reflection of laser beam in laser welding process. Therefore, the control of welding parameters on the formation of adequate weld puddle composition is very difficult. Laser welding is an advanced technique for joining of dissimilar materials since it can precisely control and adjust the welding parameters. In this study, a 100W Nd:YAG pulsed laser machine was used for joining 49Ni-Fe soft magnetic to C17300 copper-beryllium alloys. Welding of samples was carried out autogenously by changing the pulse duration, diameter of beam, welding speed, voltage and frequency. The spacing between samples was set to almost zero. The ample were butt welded. It was required to apply high voltage in this study due to high reflection coefficient of copper alloys. Metallography, SEM analysis, XRD and microhardness measurement was used for survey of results. The results show that the weld strength depends upon the chemical composition of the joints. To change the wells composition and heat input of the welds, it was attempted to deviate the laser focus away from the weld centerline. The best strength was achieved by deviation of the laser beam away about 0.1mm from the weld centerline. The result shows no intermetallic compounds if the laser beam is deviated away from the joint.

  9. Assessing composition and structure of soft biphasic media from Kelvin-Voigt fractional derivative model parameters

    Science.gov (United States)

    Zhang, Hongmei; Wang, Yue; Fatemi, Mostafa; Insana, Michael F.

    2017-03-01

    Kelvin-Voigt fractional derivative (KVFD) model parameters have been used to describe viscoelastic properties of soft tissues. However, translating model parameters into a concise set of intrinsic mechanical properties related to tissue composition and structure remains challenging. This paper begins by exploring these relationships using a biphasic emulsion materials with known composition. Mechanical properties are measured by analyzing data from two indentation techniques—ramp-stress relaxation and load-unload hysteresis tests. Material composition is predictably correlated with viscoelastic model parameters. Model parameters estimated from the tests reveal that elastic modulus E 0 closely approximates the shear modulus for pure gelatin. Fractional-order parameter α and time constant τ vary monotonically with the volume fraction of the material’s fluid component. α characterizes medium fluidity and the rate of energy dissipation, and τ is a viscous time constant. Numerical simulations suggest that the viscous coefficient η is proportional to the energy lost during quasi-static force-displacement cycles, E A . The slope of E A versus η is determined by α and the applied indentation ramp time T r. Experimental measurements from phantom and ex vivo liver data show close agreement with theoretical predictions of the η -{{E}A} relation. The relative error is less than 20% for emulsions 22% for liver. We find that KVFD model parameters form a concise features space for biphasic medium characterization that described time-varying mechanical properties. The experimental work was carried out at the Beckman Institute for Advanced Science and Technology, University of Illinois at Urbana-Champaign, Urbana, IL 61801, USA. Methodological development, including numerical simulation and all data analysis, were carried out at the school of Life Science and Technology, Xi’an JiaoTong University, 710049, China.

  10. Magnetic coupling mechanisms in particle/thin film composite systems

    Directory of Open Access Journals (Sweden)

    Giovanni A. Badini Confalonieri

    2010-12-01

    Full Text Available Magnetic γ-Fe2O3 nanoparticles with a mean diameter of 20 nm and size distribution of 7% were chemically synthesized and spin-coated on top of a Si-substrate. As a result, the particles self-assembled into a monolayer with hexagonal close-packed order. Subsequently, the nanoparticle array was coated with a Co layer of 20 nm thickness. The magnetic properties of this composite nanoparticle/thin film system were investigated by magnetometry and related to high-resolution transmission electron microscopy studies. Herein three systems were compared: i.e. a reference sample with only the particle monolayer, a composite system where the particle array was ion-milled prior to the deposition of a thin Co film on top, and a similar composite system but without ion-milling. The nanoparticle array showed a collective super-spin behavior due to dipolar interparticle coupling. In the composite system, we observed a decoupling into two nanoparticle subsystems. In the ion-milled system, the nanoparticle layer served as a magnetic flux guide as observed by magnetic force microscopy. Moreover, an exchange bias effect was found, which is likely to be due to oxygen exchange between the iron oxide and the Co layer, and thus forming of an antiferromagnetic CoO layer at the γ-Fe2O3/Co interface.

  11. Competing magnetic interactions and low temperature magnetic phase transitions in composite multiferroics

    International Nuclear Information System (INIS)

    Borkar, Hitesh; Singh, V N; Kumar, Ashok; Choudhary, R J; Tomar, M; Gupta, Vinay

    2015-01-01

    Novel magnetic properties and magnetic interactions in composite multiferroic oxides Pb[(Zr 0.52 Ti 0.48 ) 0.60 (Fe 0.67 W 0.33 ) .40 ]O 3 ] 0.80 –[CoFe 2 O 4 ] 0.20 (PZTFW–CFO) have been studied from 50 to 1000 Oe field cooled (FC) and zero field cooled (ZFC) probing conditions, and over a wide range of temperatures (4–350 K). Crystal structure analysis, surface morphology, and high resolution transmission electron microscopy images revealed the presence of two distinct phases, where micro- and nano-size spinel CFO were embedded in tetragonal PZTFW matrix and applied a significant built-in compressive strain (∼0.4–0.8%). Three distinct magnetic phase transitions were observed with the subtle effect of CFO magnetic phase on PZTFW magnetic phase transitions below the blocking temperature (T B ). Temperature dependence magnetic property m(T) shows a clear evidence of spin freezing in magnetic order with lowering in thermal vibration. Chemical inhomogeneity and confinement of nanoscale ferrimagnetic phase in paramagnetic/antiferromagnetic matrix restrict the long range interaction of spin which in turn develop a giant spin frustration. A large divergence in the FC and ZFC data and broad hump in ZFC data near 200 (±10) K were observed which suggests that large magnetic anisotropy and short range order magnetic dipoles lead to the development of superparamagnetic states in composite. (paper)

  12. Current Profile and Magnetic Structure Measurements through Tangential Soft X-Ray Imaging in Compact Tori

    International Nuclear Information System (INIS)

    Fonck, Raymond J.

    2004-01-01

    This report describes the fabrication and tests of a tangentially imaging soft X-ray (SXR) camera diagnostic for fusion energy plasma research. It can be used for the determination of the current distribution in strongly shaped toroidal magnetically confined plasmas, such as those found in spherical tori or advanced tokamaks. It included the development of both an appropriate imaging SXR camera and image analysis techniques necessary to deduce the plasma shape and current distribution. The basic camera concept consists of a tangentially viewing pinhole imaging system with thin-film SXR filters, a scintillator screen to provide SXR to visible conversion, a fast shuttering system, and an sensitive visible camera imaging device. The analysis approach consists of integrating the 2-D SXR image data into a Grad-Shafranov toroidal equilibrium solver code to provide strong constraints on the deduced plasma current and pressure profiles. Acceptable sensitivity in the deduced current profile can be obtained if the relative noise in the measured image can be kept in the range of 1% or less. Tests on the Pegasus Toroidal Experiment indicate very flat safety factor profiles in the plasma interior

  13. Designing bioinspired composite reinforcement architectures via 3D magnetic printing

    Science.gov (United States)

    Martin, Joshua J.; Fiore, Brad E.; Erb, Randall M.

    2015-10-01

    Discontinuous fibre composites represent a class of materials that are strong, lightweight and have remarkable fracture toughness. These advantages partially explain the abundance and variety of discontinuous fibre composites that have evolved in the natural world. Many natural structures out-perform the conventional synthetic counterparts due, in part, to the more elaborate reinforcement architectures that occur in natural composites. Here we present an additive manufacturing approach that combines real-time colloidal assembly with existing additive manufacturing technologies to create highly programmable discontinuous fibre composites. This technology, termed as `3D magnetic printing', has enabled us to recreate complex bioinspired reinforcement architectures that deliver enhanced material performance compared with monolithic structures. Further, we demonstrate that we can now design and evolve elaborate reinforcement architectures that are not found in nature, demonstrating a high level of possible customization in discontinuous fibre composites with arbitrary geometries.

  14. Designing bioinspired composite reinforcement architectures via 3D magnetic printing.

    Science.gov (United States)

    Martin, Joshua J; Fiore, Brad E; Erb, Randall M

    2015-10-23

    Discontinuous fibre composites represent a class of materials that are strong, lightweight and have remarkable fracture toughness. These advantages partially explain the abundance and variety of discontinuous fibre composites that have evolved in the natural world. Many natural structures out-perform the conventional synthetic counterparts due, in part, to the more elaborate reinforcement architectures that occur in natural composites. Here we present an additive manufacturing approach that combines real-time colloidal assembly with existing additive manufacturing technologies to create highly programmable discontinuous fibre composites. This technology, termed as '3D magnetic printing', has enabled us to recreate complex bioinspired reinforcement architectures that deliver enhanced material performance compared with monolithic structures. Further, we demonstrate that we can now design and evolve elaborate reinforcement architectures that are not found in nature, demonstrating a high level of possible customization in discontinuous fibre composites with arbitrary geometries.

  15. Anomalous dimension, chiral phase transition and inverse magnetic catalysis in soft-wall AdS/QCD

    Energy Technology Data Exchange (ETDEWEB)

    Fang, Zhen, E-mail: fangzhen@itp.ac.cn [Key Laboratory of Theoretical Physics, Institute of Theoretical Physics, Chinese Academy of Science, Beijing 100190 (China); University of Chinese Academy of Sciences, Beijing (China)

    2016-07-10

    A modified soft-wall AdS/QCD model with a z-dependent bulk scalar mass is proposed. We argue for the necessity of a modified bulk scalar mass from the quark mass anomalous dimension and carefully constrain the form of bulk mass by the corresponding UV and IR asymptotics. After fixing the form of bulk scalar mass, we calculate the mass spectra of (axial-)vector and pseudoscalar mesons, which have a good agreement with the experimental data. The behavior of chiral phase transition is also investigated, and the results are consistent with the standard scenario and lattice simulations. Finally, the issue of chiral magnetic effects is addressed. We find that the inverse magnetic catalysis emerges naturally from the modified soft-wall model, which is consistent with the recent lattice simulations.

  16. Electro-magnetic properties of composites with aligned Fe-Co hollow fibers

    Directory of Open Access Journals (Sweden)

    Seungchan Cho

    2016-05-01

    Full Text Available A novel Fe-Co binary hollow fiber was synthesized by electroless plating using hydrolyzed polyester fiber and its anisotropy characteristic was investigated for electromagnetic wave absorbing materials. The hollow fibers in parallel with magnetic field show higher saturated magnetization of 202 emu/g at the applied magnetic field of 10 kOe and lower coercivity (27.658 Oe, compared with the random and vertical oriented hollow fibers. From complex permittivity measurement, the Fe-Co hollow fiber composites clearly display a single dielectric resonance, located at ∼14 GHz. The Fe-Co hollow fibers not only provide excellent EM properties in GHz frequency ranges, resulting mainly from the strong resonance, but also adjust the soft magnetic properties through fiber alignments. The cavitary structure of the Fe-Co hollow fibers, not only giving rise to a dielectric loss resonance and also adjusting its peak frequency, may be a pathway to useful EM wave absorptive devices in GHz frequency ranges.

  17. Pure-iron/iron-based-alloy hybrid soft magnetic powder cores compacted at ultra-high pressure

    Science.gov (United States)

    Saito, Tatsuya; Tsuruta, Hijiri; Watanabe, Asako; Ishimine, Tomoyuki; Ueno, Tomoyuki

    2018-04-01

    We developed Fe/FeSiAl soft magnetic powder cores (SMCs) for realizing the miniaturization and high efficiency of an electromagnetic conversion coil in the high-frequency range (˜20 kHz). We found that Fe/FeSiAl SMCs can be formed with a higher density under higher compaction pressure than pure-iron SMCs. These SMCs delivered a saturation magnetic flux density of 1.7 T and iron loss (W1/20k) of 158 kW/m3. The proposed SMCs exhibited similar excellent characteristics even in block shapes, which are closer to the product shapes.

  18. Pure-iron/iron-based-alloy hybrid soft magnetic powder cores compacted at ultra-high pressure

    Directory of Open Access Journals (Sweden)

    Tatsuya Saito

    2018-04-01

    Full Text Available We developed Fe/FeSiAl soft magnetic powder cores (SMCs for realizing the miniaturization and high efficiency of an electromagnetic conversion coil in the high-frequency range (∼20 kHz. We found that Fe/FeSiAl SMCs can be formed with a higher density under higher compaction pressure than pure-iron SMCs. These SMCs delivered a saturation magnetic flux density of 1.7 T and iron loss (W1/20k of 158 kW/m3. The proposed SMCs exhibited similar excellent characteristics even in block shapes, which are closer to the product shapes.

  19. Microstructure and soft magnetic properties of Finemet-type ribbons obtained by twin-roller melt-spinning

    International Nuclear Information System (INIS)

    Pozo Lopez, G.; Fabietti, L.M.; Condo, A.M.; Urreta, S.E.

    2010-01-01

    Soft magnetic ribbons of Finemet-type (Fe 73.5 Cu 1 Nb 3 Si 13.5 B 9 ) alloys are synthesized by the twin-roller melt-spinning technique directly from the melt, at tangential wheel speeds of 15, 18, 19 and 20 m/s. The microstructure and the magnetic properties are characterized by X-ray diffraction (XRD), transmission electron microscopy (TEM), differential thermal analysis (DTA), thermo-gravimetric analysis (TGA) and hysteresis loops measurements. Samples cooled at 20 m/s are amorphous, while those quenched at lower wheel speeds are partially crystalline. All samples studied present saturation magnetization values (150-160 A m 2 /kg) higher than the commercial Finemet alloys (∼135 A m 2 /kg), obtained by controlled crystallization of amorphous single-roller melt-spun alloys. Optimal soft magnetic properties - σ S =(154±8) A m 2 /kg and H C =(6.9±0.9) A/m - are found in samples quenched at 19 m/s, consisting of size-distributed bcc Fe-Si nanograins (∼18 nm in average) embedded in an amorphous residual matrix. A minority nanocrystalline magnetic phase (≤10 nm) is also detected.

  20. Magnetic composite Hydrodynamic Pump with Laser Induced Graphene Electrodes

    KAUST Repository

    Khan, Mohammed Asadullah; Hristovski, Ilija R.; Marinaro, Giovanni; Kosel, Jü rgen

    2017-01-01

    A polymer based magneto hydrodynamic pump capable of actuating saline fluids is presented. The benefit of this pumping concept to operate without any moving parts is combined with simple and cheap fabrication methods and a magnetic composite material, enabling a high level of integration. The operating principle, fabrication methodology and flow characteristics of the pump are detailed. The pump electrodes are created by laser printing of polyimide, while the permanent magnet is molded from an NdFeB powder - polydimethylsiloxane (PDMS) composite. The cross-section area of the pump is 240 mm $^2$ . The electrode length is 5 mm. The magnetic characteristics of the NdFeB-PDMS composite indicate high degree of magnetization, which increases the pump efficiency. Using a saline solution similar to seawater, the pump produces 3.4 mm/s flow velocity at a voltage of 7.5V and a current density of 30 mA/cm $^2$ .

  1. Magnetic composite Hydrodynamic Pump with Laser Induced Graphene Electrodes

    KAUST Repository

    Khan, Mohammed Asadullah

    2017-05-24

    A polymer based magneto hydrodynamic pump capable of actuating saline fluids is presented. The benefit of this pumping concept to operate without any moving parts is combined with simple and cheap fabrication methods and a magnetic composite material, enabling a high level of integration. The operating principle, fabrication methodology and flow characteristics of the pump are detailed. The pump electrodes are created by laser printing of polyimide, while the permanent magnet is molded from an NdFeB powder - polydimethylsiloxane (PDMS) composite. The cross-section area of the pump is 240 mm $^2$ . The electrode length is 5 mm. The magnetic characteristics of the NdFeB-PDMS composite indicate high degree of magnetization, which increases the pump efficiency. Using a saline solution similar to seawater, the pump produces 3.4 mm/s flow velocity at a voltage of 7.5V and a current density of 30 mA/cm $^2$ .

  2. Properties of magnetic nickel/porous-silicon composite powders

    Directory of Open Access Journals (Sweden)

    Toshihiro Nakamura

    2012-09-01

    Full Text Available The magnetic and photoluminescence (PL properties of nickel/porous-silicon (Ni/PSi composite powders are investigated. Ni/PSi composite powders are prepared by stain etching of Si powder in a HF/HNO3 solution followed by electroless plating of Ni nanoparticles on the stain-etched PSi powder in a NiCl2 solution. The Ni/PSi powders exhibit hydrophillicity, superparamagnetism caused by the deposited Ni nanoparticles, and orange-red PL owing to the nanostructured PSi surface. The degree of magnetization decreases with increasing Ni plating time, indicating its dependence on the size of the Ni nanoparticles. The Ni/PSi composite powders also show a stronger magnetization as compared to that of the Ni-particle-plated Si powder. The stronger magnetization results from the larger surface area of PSi. The PL intensity, peak wavelength, and lifetime of Ni/PSi are strongly dependent on the NiCl2 concentration. This dependence is due to the different thickness of the oxide overlayer on the PSi surface formed during the Ni plating process. The existence of the oxide overlayer also results in a small change in the PL intensity against excitation time.

  3. Photoactivated Composite Biomaterial for Soft Tissue Restoration in Rodents and in Humans

    OpenAIRE

    Hillel, Alexander T.; Unterman, Shimon; Nahas, Zayna; Reid, Branden; Coburn, Jeannine M.; Axelman, Joyce; Chae, Jemin J.; Guo, Qiongyu; Trow, Robert; Thomas, Andrew; Hou, Zhipeng; Lichtsteiner, Serge; Sutton, Damon; Matheson, Christine; Walker, Patricia

    2011-01-01

    Soft tissue reconstruction often requires multiple surgical procedures that can result in scars and disfiguration. Facial soft tissue reconstruction represents a clinical challenge because even subtle deformities can severely affect an individual’s social and psychological function. We therefore developed a biosynthetic soft tissue replacement composed of poly(ethylene glycol) (PEG) and hyaluronic acid (HA) that can be injected and photocrosslinked in situ with transdermal ligh...

  4. Soft errors in 10-nm-scale magnetic tunnel junctions exposed to high-energy heavy-ion radiation

    Science.gov (United States)

    Kobayashi, Daisuke; Hirose, Kazuyuki; Makino, Takahiro; Onoda, Shinobu; Ohshima, Takeshi; Ikeda, Shoji; Sato, Hideo; Inocencio Enobio, Eli Christopher; Endoh, Tetsuo; Ohno, Hideo

    2017-08-01

    The influences of various types of high-energy heavy-ion radiation on 10-nm-scale CoFeB-MgO magnetic tunnel junctions with a perpendicular easy axis have been investigated. In addition to possible latent damage, which has already been pointed out in previous studies, high-energy heavy-ion bombardments demonstrated that the magnetic tunnel junctions may exhibit clear flips between their high- and low-resistance states designed for a digital bit 1 or 0. It was also demonstrated that flipped magnetic tunnel junctions still may provide proper memory functions such as read, write, and hold capabilities. These two findings proved that high-energy heavy ions can produce recoverable bit flips in magnetic tunnel junctions, i.e., soft errors. Data analyses suggested that the resistance flips stem from magnetization reversals of the ferromagnetic layers and that each of them is caused by a single strike of heavy ions. It was concurrently found that an ion strike does not always result in a flip, suggesting a stochastic process behind the flip. Experimental data also showed that the flip phenomenon is dependent on the device and heavy-ion characteristics. Among them, the diameter of the device and the linear energy transfer of the heavy ions were revealed as the key parameters. From their dependences, the physical mechanism behind the flip was discussed. It is likely that a 10-nm-scale ferromagnetic disk loses its magnetization due to a local temperature increase induced by a single strike of heavy ions; this demagnetization is followed by a cooling period associated with a possible stochastic recovery process. On the basis of this hypothesis, a simple analytical model was developed, and it was found that the model accounts for the results reasonably well. This model also predicted that magnetic tunnel junctions provide sufficiently high soft-error reliability for use in space, highlighting their advantage over their counterpart conventional semiconductor memories.

  5. Effect of the concentration of magnetite on the structure, electrical and magnetic properties of a polyester resin-based composite

    Directory of Open Access Journals (Sweden)

    Gabriel Peña-Rodriguez

    2018-01-01

    Full Text Available This study reports the effect of the concentration of magnetite powders (Fe3O4 on the electrical and magnetic properties of a resin-based composite of thermoset polyester. The samples were prepared by the casting method at different concentrations: 60-40, 70-30, 80-20, 90-10 and 100-0 (% in weight, where the primary phase was resin and the secondary, Fe3O4 powders. The crystalline structure was studied using X-ray diffraction and surface characterization was carried out applying the scanning electron microscopy technique. The electrical response was measured by electric polarization curves as a function of the electric field; and the volumetric electrical resistivity, by an electrometer. The magnetic response was determined by magnetization curves as a function of temperature and intensity of the applied magnetic field. The structural analysis indicates that crystallinity increases as higher concentrations of Fe3O4 are added to the samples. The electrical characterization of the material reveals that the volumetric resistivity decreases as the content of magnetite increases. These reactions indicate an insulation-conductor transition with increasing dielectric constant values. The magnetic characterization presents a linear increase of the saturation of magnetization and magnetic moment as a function of the amount of magnetite added to the polymer matrix, whereas the coercivity shows behaviors of soft magnetic materials for T ˃ Tv and for T < Tv, where Tv represents the temperature of Verwey.

  6. Outstanding efficiency in energy conversion for electric motors constructed by nanocrystalline soft magnetic alloy “NANOMET®” cores

    Directory of Open Access Journals (Sweden)

    N. Nishiyama

    2016-05-01

    Full Text Available Recently updated nanocrystalline soft magnetic Fe-Co-Si-B-P-Cu alloys “NANOMET®” exhibit high saturation magnetic flux density (Bs > 1.8 T, low coercivity (Hc < 10 A/m and low core loss (W1.7/50 ∼ 0.4 W/kg even in a ribbon form with a thickness of up to 40 μm. By utilize excellent magnetic softness, several products such as motors or transformers for electrical appliances are now under developing by industry-academia collaboration. In particular, it is found that a brushless DC motor using NANOMET® core exhibited remarkable improvement in energy consumption. The prototype motor with an outer core diameter of 70 mm and a core thickness of 50 mm was constructed using laminated nano-crystallized NANOMET® ribbons. Core-loss for the constructed motor was improved from 1.4 W to 0.4 W only by replacing the non-oriented Si-steel core with NANOMET® one. The overall motor efficiency is evaluated to be 3% improvement. In this work, the relation between processing and resulting magnetic properties will be presented. In addition, feasibility for commercialization will also be discussed.

  7. Left-handed materials in metallic magnetic granular composites

    International Nuclear Information System (INIS)

    Chui, S.T.; Lin, Z.F.; Hu, L.-B.

    2003-01-01

    There is recently interests in the 'left-handed' materials. In these materials the direction of the wave vector of electromagnetic radiation is opposite to the direction of the energy flow. We present simple arguments that suggests that magnetic composites can also be left-handed materials. However, the physics involved seems to be different from the original argument. In our argument, the imaginary part of the dielectric constant is much larger than the real part, opposite to the original argument

  8. Magnetic moments of composite quarks and leptons: further difficulties

    International Nuclear Information System (INIS)

    Lipkin, H.J.

    1980-05-01

    The previously noted difficulty of obtaining Dirac magnetic moments in composite models with two basic building blocks having different charges is combined with the observation by Shaw et al., that a light bound fermion state built from heavy constituents must have the Dirac moment in a renormalizable theory. The new constraint on any model that builds leptons from two fundamental fields bound by non-electromagnetic forces is that the ratio of the magnetic moment to the total charge of the bound state is independent of the values of the charges of the constituents; e.g., such a bound state of a spin-1/2 fermion and a scalar boson will have the same magnetic moment if the fermion is neutral and the boson has charge -e or vice versa

  9. Magnetic studies of Fe-Y compositionally modulated thin films

    International Nuclear Information System (INIS)

    Badia, F.; Ferrater, C.; Lousa, A.; Martinez, B.; Labarta, A.; Tejada, J.

    1990-01-01

    Compositionally modulated thin films of Y/Fe have been studied by using SQUID magnetometry. Samples were grown by electron-beam evaporation onto Kapton substrates. In the low applied field regime, the samples show irreversible behavior when they are submitted to ZFC-FC magnetization processes, increasing the irreversibility zone as the thickness of the Fe layers increases. In the high applied magnetic field regime (H≥10 000 Oe), samples show ferromagnetic behavior. The temperature dependence of the saturation magnetization has been studied, and it was found that both spin-wave excitations and Stoner excitations occur at temperatures higher than 40 K, and a marked deviation from the T 3/2 law was noted below 30 K

  10. Multimaterial magnetically assisted 3D printing of composite materials

    Science.gov (United States)

    Kokkinis, Dimitri; Schaffner, Manuel; Studart, André R.

    2015-10-01

    3D printing has become commonplace for the manufacturing of objects with unusual geometries. Recent developments that enabled printing of multiple materials indicate that the technology can potentially offer a much wider design space beyond unusual shaping. Here we show that a new dimension in this design space can be exploited through the control of the orientation of anisotropic particles used as building blocks during a direct ink-writing process. Particle orientation control is demonstrated by applying low magnetic fields on deposited inks pre-loaded with magnetized stiff platelets. Multimaterial dispensers and a two-component mixing unit provide additional control over the local composition of the printed material. The five-dimensional design space covered by the proposed multimaterial magnetically assisted 3D printing platform (MM-3D printing) opens the way towards the manufacturing of functional heterogeneous materials with exquisite microstructural features thus far only accessible by biological materials grown in nature.

  11. Effects of Cu substitution for Fe on the glass-forming ability and soft magnetic properties for Fe-based bulk metallic glasses

    International Nuclear Information System (INIS)

    Dou, Lintao; Liu, Haishun; Hou, Long; Xue, Lin; Yang, Weiming; Zhao, Yucheng; Chang, Chuntao

    2014-01-01

    The effects of Cu substitution for Fe on the glass-forming ability (GFA) and soft magnetic properties for Fe 72−x Cu x B 20 Si 4 Nb 4 (x=0.0, 0.2, 0.4, 0.6, 0.8, and 1.0) bulk metallic glasses (BMGs) are investigated. It is found that the investigated BMGs exhibit large GFA as well as excellent soft magnetic properties, and proper substitution of Fe by Cu improves the saturation magnetization, coercive force, and effective permeability without obvious deterioration of the GFA. - Highlights: • Fully glassy rods of Fe 72−x Cu x B 20 Si 4 Nb 4 BMGs were produced above 1 mm in diameter. • Investigated BMGs exhibit large glass-forming ability and excellent soft magnetic properties. • Proper Cu substitution improves magnetic properties without obvious deterioration of glass-forming ability

  12. Effect of annealing treatment on soft magnetic properties of Fe-6.5 wt% Si wide ribbons

    International Nuclear Information System (INIS)

    Roy, R.K.; Panda, A.K.; Ghosh, M.; Mitra, A.; Ghosh, R.N.

    2009-01-01

    The 25 mm wide ribbons of Fe-6.5 wt% Si alloy have been developed by melt spinning technique, showing sufficient ductility and white silver appearance. Two magnetic transitions take place at 676 and 760 deg. C due to the formation of B2 ordered phase and A2 disordered paramagnetic phase, respectively. The saturation magnetization of the ribbon is 17.5 kG under the applied field of 12 kG. The as-cast ribbons consist of disordered A2 structure with a low volume of B2 phases while the annealed microstructure comprises a dispersion of B2 domains in the disordered A2 matrix. The alloy shows the enhancement of the soft magnetic properties with a reduction in coercivity from 150 A/m in the as-cast state to 45 A/m in the annealed condition at 850 deg. C.

  13. Preparation of Pt-mesoporous tungsten carbide/carbon composites via a soft-template method for electrochemical methanol oxidation

    International Nuclear Information System (INIS)

    Ma, Chun’an; Kang, Lingzhi; Shi, Meiqin; Lang, Xiaoling; Jiang, Yekun

    2014-01-01

    Highlights: • Mesoporous composite Pt-m(WC/C) is prepared by a soft template method. • The structure of phenolic gives a space limitation effect on the growth of WC. • Analysis of the effect of F127 on controlling the structure of composites. • Pt-m(WC/C) exhibits more than three times higher than Pt/C in catalytic activity. -- Abstract: This paper introduces a simple and reproducible chemical process for synthesis of Pt-mesoporous tungsten carbide/carbon composites composites Pt-m(WC/C) by means of a soft-template method. In this process, low-molecular-weight phenolic resol acted as the precursor both for carbon support and also the carbon resource of tungsten carbide. Tungsten hexachloride was used as a tungsten precursor along with different amount of triblock copolymer Pluronic F127 as pore-forming component. The best performance of Pt-m(WC/C) towards methanol oxidation is found when the mass ratios of WCl 6 :F127 is 1:0.6. The composite presents an improved methanol oxidation performance evidenced by a negative shift in onset potential, and increase of peak current density, compared with commercial Pt/C. The difference is explained by the adding of appropriate amount of F127 which facilitates the construction of mesoporous matrix structure of WC/C

  14. Preparation of Pt-mesoporous tungsten carbide/carbon composites via a soft-template method for electrochemical methanol oxidation

    Energy Technology Data Exchange (ETDEWEB)

    Ma, Chun’an, E-mail: science@zjut.edu.cn; Kang, Lingzhi; Shi, Meiqin; Lang, Xiaoling; Jiang, Yekun

    2014-03-05

    Highlights: • Mesoporous composite Pt-m(WC/C) is prepared by a soft template method. • The structure of phenolic gives a space limitation effect on the growth of WC. • Analysis of the effect of F127 on controlling the structure of composites. • Pt-m(WC/C) exhibits more than three times higher than Pt/C in catalytic activity. -- Abstract: This paper introduces a simple and reproducible chemical process for synthesis of Pt-mesoporous tungsten carbide/carbon composites composites Pt-m(WC/C) by means of a soft-template method. In this process, low-molecular-weight phenolic resol acted as the precursor both for carbon support and also the carbon resource of tungsten carbide. Tungsten hexachloride was used as a tungsten precursor along with different amount of triblock copolymer Pluronic F127 as pore-forming component. The best performance of Pt-m(WC/C) towards methanol oxidation is found when the mass ratios of WCl{sub 6}:F127 is 1:0.6. The composite presents an improved methanol oxidation performance evidenced by a negative shift in onset potential, and increase of peak current density, compared with commercial Pt/C. The difference is explained by the adding of appropriate amount of F127 which facilitates the construction of mesoporous matrix structure of WC/C.

  15. Applications and Properties of Ionic Liquid- Based Gels and Soft Solid Composites

    Science.gov (United States)

    Voss, Bret Alan McGinness

    2011-12-01

    Solid-liquid composites (gels) have a combination of properties that afford new material applications in which high solute diffusion is desirable. These composites have a soft-solid mechanical integrity and will not flow under gravity, but entrain a liquid matrix (i.e. 60-98 mass %) which allows for high diffusion and high reactivity. Room temperature ionic liquid (RTILs) are molten organic salts with a melting point below room temperature and negligible vapor pressure. If the RTILs are used as the liquid component of a gel, then the gel matrix will not evaporate (unlike other organic solvents) and may be used for long term applications. This thesis research applies RTIL gels for two new applications; carbon dioxide/nitrogen separation and chemical warfare agent (CWA) barrier and decontamination. Separating CO2 from the flue gas of coal and gas fired power-plants is an increasingly economically and environmentally important gas separation. In this first study, RTIL gels are cast in a supported membrane and gas permeability and ideal selectivity are measured. The RTIL matrix has an inherent affinity for CO2 and provides a high diffusion, hence high permeability (i.e. 500-700 barrer). The solidifying component is a low molecular-weight organic gelator (LMOG) which through physical bonding interactions (i.e. hydrogen bonding, pi-pi stacking and van der Walls forces) forms an entangled network which provides mechanical stability (i.e. increase trans-membrane pressure required to expel selective material from the support). In these studies two LMOGs and five RTILs are used to make supported gel membranes and determine gas permeability and temperature dependent trends. The second application for RTIL gels is a decontaminating barrier for CWAs and toxic industrial compounds (TICs). In these studies a layer of RTIL gel is applied on top of a substrate contaminated with a CWA simulant (i.e. chloroethylethylsulfide, CEES). The gel performs well as a barrier, preventing CEES

  16. Highly efficient removal of pathogenic bacteria with magnetic graphene composite.

    Science.gov (United States)

    Zhan, Sihui; Zhu, Dandan; Ma, Shuanglong; Yu, Wenchao; Jia, Yanan; Li, Yi; Yu, Hongbing; Shen, Zhiqiang

    2015-02-25

    Magnetic Fe3O4/graphene composite (abbreviated as G-Fe3O4) was synthesized successfully by solvothermal method to effectively remove both bacteriophage and bacteria in water, which was tested by HRTEM, XRD, BET, XPS, FTIR, CV, magnetic property and zeta-potential measurements. Based on the result of HRTEM, the single-sheet structure of graphene oxide and the monodisperse Fe3O4 nanoparticles on the surface of graphene can be observed obviously. The G-Fe3O4 composite were attractive for removing a wide range of pathogens including not only bacteriophage ms2, but also various bacteria such as S. aureus, E. coli, Salmonella, E. Faecium, E. faecalis, and Shigella. The removal efficiency of E. coli for G-Fe3O4 composite can achieve 93.09%, whereas it is only 54.97% with pure Fe3O4 nanoparticles. Moreover, a detailed verification test of real water samples was conducted and the removal efficiency of bacteria in real water samples with G-Fe3O4 composite can also reach 94.8%.

  17. Percolation Phenomena For New Magnetic Composites And Tim Nanocomposites Materials

    Directory of Open Access Journals (Sweden)

    Ahmed Thabet Mohamed

    2015-01-01

    Full Text Available This paper presents a theoretical investigation in order to obtain new composite and nanocomposite magnetic industrial materials. The effective conductivity and thermal effective conductivity have been predicted by adding various types and percentages of conductive particles (Al2O3, MgO, ZnO, Graphite etc. to the main matrices of Epoxy, Iron and Silicon for formulating new composite and nanocomposite industrial materials. The characterization of effective conductivity of new polymeric composites has been investigated with various applied forces, inclusion types and their concentrations. In addition, the effect of inclusion types and their concentrations on the effective thermal conductivities of thermal interface nanocomposite industrial materials has been explained and discussed.

  18. Population inversion and gain measurements for soft x-ray-laser development in a magnetically confined plasma column

    International Nuclear Information System (INIS)

    Suckewer, S.; Skinner, C.H.; Voorhees, D.; Milchberg, H.; Keane, C.; Semet, A.

    1983-06-01

    We present population inversion and gain measurements from an experimental investigation of possibilities to obtain high gain and lasing action in the soft x-ray region. Our approach to soft x-ray-laser development is based on rapid plasma cooling after the laser pulse by radiation losses, leading to fast recombination and collisional cascade into upper excited levels of CVI, for example, while the lower excited levels depopulate rapidly by radiative transitions, thus creating population inversions and gain. A approx. = 0.5 kJ CO 2 laser was focused onto a target of solid carbon or teflon; or CO 2 , O 2 , Ne gas, and the resulting plasma confined in a 50 to 90 kG magnetic field. Spectroscopic diagnostics with absolute intensity calibration were used to measure level populations

  19. Investigation of (Fe,Co)NbB-Based Nanocrystalline Soft Magnetic Alloys by Lorentz Microscopy and Off-Axis Electron Holography.

    Science.gov (United States)

    Zheng, Changlin; Kirmse, Holm; Long, Jianguo; Laughlin, David E; McHenry, Michael E; Neumann, Wolfgang

    2015-04-01

    The relationship between microstructure and magnetic properties of a (Fe,Co)NbB-based nanocrystalline soft magnetic alloy was investigated by analytical transmission electron microscopy (TEM). The microstructures of (Fe0.5Co0.5)80Nb4B13Ge2Cu1 nanocrystalline alloys annealed at different temperatures were characterized by TEM and electron diffraction. The magnetic structures were analyzed by Lorentz microscopy and off-axis electron holography, including quantitative measurement of domain wall width, induction, and in situ magnetic domain imaging. The results indicate that the magnetic domain structure and particularly the dynamical magnetization behavior of the alloys strongly depend on the microstructure of the nanocrystalline alloys. Smaller grain size and random orientation of the fine particles decrease the magneto-crystalline anisotropy and suggests better soft magnetic properties which may be explained by the anisotropy model of Herzer.

  20. Stress induced magnetic-domain evolution in magnetoelectric composites

    Science.gov (United States)

    Trivedi, Harsh; Shvartsman, Vladimir V.; Lupascu, Doru C.; Medeiros, Marco S. A.; Pullar, Robert C.

    2018-06-01

    Local observation of the stress mediated magnetoelectric (ME) effect in composites has gained a great deal of interest over the last decades. However, there is an apparent lack of rigorous methods for a quantitative characterization of the ME effect at the local scale, especially in polycrystalline microstructures. In the present work, we address this issue by locally probing the surface magnetic state of barium titante–hexagonal barium ferrite (BaTiO3–BaFe12O19) ceramic composites using magnetic force microscopy (MFM). The effect of the piezoelectrically induced local stress on the magnetostrictive component (BaFe12O19, BaM) was observed in the form of the evolution of the magnetic domains. The local piezoelectric stress was induced by applying a voltage to the neighboring BaTiO3 grains, using a conductive atomic force microscopy tip. The resulting stochastic evolution of magnetic domains was studied in the context of the induced magnetoelastic anisotropy. In order to overcome the ambiguity in the domain changes observed by MFM, certain generalizations about the observed MFM contrast are put forward, followed by application of an algorithm for extracting the average micromagnetic changes. An average change in domain wall thickness of 50 nm was extracted, giving a lower limit on the corresponding induced magnetoelastic anisotropy energy. Furthermore, we demonstrate that this induced magnetomechanical energy is approximately equal to the K1 magnetocrystalline anisotropy constant of BaM, and compare it with a modeled value of applied elastic energy density. The comparison allowed us to judge the quality of the interfaces in the composite system, by roughly gauging the energy conversion ratio.

  1. Compensation of the Persistent Current Multipoles in the LHC Dipoles by making the Coil Protection Sheet from Soft Magnetic Material

    CERN Document Server

    Völlinger, C

    2000-01-01

    This note presents a scheme for compensating the persistent current multipole errors of the LHC dipoles by making the coil protection sheets from soft magnetic material of 0.5 mm thickness. The material properties assumed in this study are those of iron sheets with a very low content of impurities (99.99% pure Fe). The non-linearities in the upramp cycle on the b3 multipole component can be reduced by the factor of four (while decreasing the b5 variation by the factor of two. Using sheets of slightly different thicknesses offers a tuning possibility for the series magnet coils and can compensate deviations arising from cables of different suppliers. The calculation method is based on a semi-analytical hysteresis model for hard superconductors and an M(B) - iteration using the method of coupled boundary elements - finite elements (BEM - FEM). It is now possible to compute persistent current multipole errors of geometries with arbitrarily shaped iron yokes and thin layers of soft magnetic material such as tunin...

  2. CLINICAL APPLICABILITY OF HUMAN IN-VIVO LOCALIZED P-31 MAGNETIC-RESONANCE SPECTROSCOPY OF BONE AND SOFT-TISSUE TUMORS

    NARCIS (Netherlands)

    HOEKSTRA, HJ; BOEVE, WJ; KAMMAN, RL; MOOYAART, EL

    1994-01-01

    Background: Magnetic resonance imaging (MRI) is of restricted value for the in vivo characterization of tumor types. The applicability of phosphorus-31 (P-31) magnetic resonance spectroscopy (MRS) in the diagnosis of bone and soft tissue tumors is unknown. Methods: A total of 191 consecutive

  3. Low-voltage, large-strain soft electrothermal actuators based on laser-reduced graphene oxide/Ag particle composites

    Science.gov (United States)

    Wang, Qian; Li, Yu-Tao; Zhang, Tian-Yu; Wang, Dan-Yang; Tian, Ye; Yan, Jun-Chao; Tian, He; Yang, Yi; Yang, Fan; Ren, Tian-Ling

    2018-03-01

    In this paper, low-voltage, large-strain flexible electrothermal actuators (ETAs) based on laser-reduced graphene oxide (LRGO)/Ag particle composites were fabricated in a simple and cost-efficient process. By adding Ag particles to the LRGO, the sheet resistance decreased effectively. Under a driving voltage of 28 V, the actuator obtained a bending angle of 192° within 6 s. Besides, the bending deformation could be precisely controlled by the driving voltage ranging from 10° to 192°. Finally, a gripper composed of two actuators was demonstrated to manipulate a piece of polydimethylsiloxane block. With the advantages of low-voltage, fast-response, and easy-to-manufacture, the graphene based ETAs have a promising application in soft robotics and soft machines.

  4. Magnetic susceptibility of MnZn and NiZn soft ferrites using Laplace transform and the Routh-Hurwitz criterion

    International Nuclear Information System (INIS)

    Fano, Walter Gustavo; Boggi, Silvina; Razzitte, Adrian Cesar

    2011-01-01

    This paper is devoted to study the Routh-Hurwitz stability criterion from the MnZn and NiZn soft ferrites using a phenomenological model with the gyromagnetic spin contribution and domain wall contribution. The magnetodynamic equation and the harmonic oscillator equation have been used to obtain the domain walls and the spin contribution of the magnetic susceptibility. The ferrite materials have been considered as linear, time invariant, isotropic and homogeneous, and the magnetization vector is proportional to the magnetic field vector. The resulting expression of the magnetization in time domain of both ferrites under study has been obtained by mean of the inverse Laplace transformation applying the residue method. The poles of the magnetic susceptibility have negative real parts, which ensures that the response decays exponentially to zero as the time increase. The degree of the numerator's polynomial of the magnetic susceptibility is less than the degree of denominator's polynomial in the magnetic susceptibility function: and the poles are located in the half left s-plane. Then the system is bounded-input, bounded-output (BIBO), and the results agree with the Routh-Hurwitz stability criterion for the MnZn and NiZn soft ferrites. - Research Highlights: → Laplace transform of the magnetic susceptibility of the MnZn and NiZn soft ferrites. → Routh-Hurwitz stability criterion of magnetic materials. → Bode plot of magnetic susceptibility. → Inverse Laplace transform using residue theorem.

  5. Magnetic Amphiphilic Composites Applied for the Treatment of Biodiesel Wastewaters

    Directory of Open Access Journals (Sweden)

    Bruno R. S. Lemos

    2012-05-01

    Full Text Available In this work, new magnetic amphiphilic composites were prepared by chemical vapor deposition with ethanol on the surface of hydrophilic natural chrysotile matrix containing Fe catalyst. XRD, Raman, Mössbauer and SEM analyses suggest the formation of a complex nanostructured material composed of hydrophobic carbon nanotubes/nanofibers grown on the hydrophilic surface of the MgSi fiber mineral and the presence of Fe metallic nanoparticles coated by carbon. These nanostructured particles show amphiphilic properties and interact very well with both oil and aqueous phases. When added to emulsions the amphiphilic particles locate on the oil/water interface and, under a magnetic field, the oil droplets collapsed leading to the separation of the aqueous and oil phases. Preliminary work showed excellent results on the use of these particles to break wastewater emulsions in the biodiesel process.

  6. Temperature dependence of microwave absorption phenomena in single and biphase soft magnetic microwires

    Czech Academy of Sciences Publication Activity Database

    El Kammouni, R.; Vázquez, M.; Lezama, L.; Kurlyandskaya, G.; Kraus, Luděk

    2014-01-01

    Roč. 368, Nov (2014), 126-132 ISSN 0304-8853 Institutional support: RVO:68378271 Keywords : magnetic microwire * ferromagnetic resonance * microwave absorption * biphase magnetic system Subject RIV: BM - Solid Matter Physics ; Magnetism Impact factor: 1.970, year: 2014

  7. Soft tissue segmentation and 3D display from computerized tomography and magnetic resonance imaging

    International Nuclear Information System (INIS)

    Fan, R.T.; Trivedi, S.S.; Fellingham, L.L.; Gamboa-Aldeco, A.; Hedgcock, M.W.

    1987-01-01

    Volume calculation and 3D display of human anatomy facilitate a physician's diagnosis, treatment, and evaluation. Accurate segmentation of soft tissue structures is a prerequisite for such volume calculations and 3D displays, but segmentation by hand-outlining structures is often tedious and time-consuming. In this paper, methods based on analysis of statistics of image gray level are applied to segmentation of soft tissue in medical images, with the goal of making segmentation automatic or semi-automatic. The resulting segmented images, volume calculations, and 3D displays are analyzed and compared with results based on physician-drawn outlines as well as actual volume measurements

  8. Rational synthesis of zerovalent iron/bamboo charcoal composites with high saturation magnetization

    Science.gov (United States)

    Mingshan Wu; Jianfeng Ma; Zhiyong Cai; Genlin Tian; Shumin Yang; Youhong Wang; Xing' e Liu

    2015-01-01

    The synthesis of magnetic biochar composites is a major new research area in advanced materials sciences. A series of magnetic bamboo charcoal composites (MBC800, MBC1000 and MBC1200) with high saturation magnetization (Ms) was fabricated in this work by mixing bamboo charcoal powder with an aqueous ferric chloride solution and subsequently...

  9. AN INVESTIGATION ON SOFT MAGNETIC AND NON-MAGNETIC MATERIALS UNDER LOW FREQUENCY FOR BIOMEDICAL SENSOR APPLICATION

    Directory of Open Access Journals (Sweden)

    Sheroz Khan

    2012-02-01

    Full Text Available In consequence of the recent development of magnetic sensors in biomedical sector, the investigation of magneticmaterials has been a contributing factor in application stage. This paper proposes a novel technique to investigate materials by obtaining unique distinctive impedance peaks with unique impedance values. A magneto-inductive sensoris used to measure the induction of magnetic and non-magnetic impedance peaks related to the change in permeability, thus characterizing the materials under low frequency.

  10. Magnetic and electronic properties of RNiO{sub 3} (R = Pr, Nd, Eu, Ho and Y) perovskites studied by resonant soft x-ray magnetic powder diffraction

    Energy Technology Data Exchange (ETDEWEB)

    Bodenthin, Y; Staub, U; Piamonteze, C; Garcia-Fernandez, M [Swiss Light Source, Paul Scherrer Institut, CH-5232 Villigen PSI (Switzerland); Martinez-Lope, M J; Alonso, J A, E-mail: urs.staub@psi.ch [Instituto de Ciencia de Materiales de Madrid, CSIC, Cantoblanco, E-28049 Madrid (Spain)

    2011-01-26

    Soft x-ray resonant magnetic powder diffraction of the (1/2 0 1/2) reflection at the Ni L{sub 2,3} edges is used to study the magnetic and electronic properties of a series of RNiO{sub 3} materials (with R = Pr, Nd, Eu, Ho and Y) below the metal-insulator transition. The polarization and energy dependence of the reflection gives further support for a non-collinear magnetic structure and charge disproportionation in the whole RNiO{sub 3} series. Only small changes in the spectra of the magnetic (1/2 0 1/2) reflection and in the absorption spectra could be detected. The results are discussed with comparison to charge transfer multiplet calculations. Our results emphasize that the lighter and heavier RNiO{sub 3} compounds are very similar from the point of view of their local electronic and magnetic state despite the strong change of the metal-to-insulator transition temperature.

  11. Modification of structural and magnetic properties of soft magnetic multi-component metallic glass by 80 MeV {sup 16}O{sup 6+} ion irradiation

    Energy Technology Data Exchange (ETDEWEB)

    Kane, S.N., E-mail: kane_sn@yahoo.com [School of Physics, D.A. University, Khandwa Road Campus, Indore 452001 (India); Shah, M.; Satalkar, M.; Gehlot, K. [School of Physics, D.A. University, Khandwa Road Campus, Indore 452001 (India); Kulriya, P.K.; Avasthi, D.K. [Inter-University Accelerator Centre, P.O. Box No. 10502, Aruna Asaf Ali Marg, New Delhi 110067 (India); Sinha, A.K. [Raja Ramanna Centre for Advanced Technology, P.O. CAT, Indore 452013 (India); Modak, S.S. [Physics Department, Jaypee University of Eng. & Tech., A-B Road, Raghogarh, Guna 473226 (India); Ghodke, N.L.; Reddy, V.R. [UGC-DAE CSR, University Campus, Khandwa Road, Indore 452001 (India); Varga, L.K. [RISSPO, Hungarian Academy of Sciences, P.O. Box 49, 1525 Budapest (Hungary)

    2016-07-15

    Effect of 80 MeV {sup 16}O{sup 6+} ion irradiation in amorphous Fe{sub 77}P{sub 8}Si{sub 3}C{sub 5}Al{sub 2}Ga{sub 1}B{sub 4} alloy is reported. Electronic energy loss induced modifications in the structural and, magnetic properties were monitored by synchrotron X-ray diffraction (SXRD), Mössbauer and, magnetic measurements. Broad amorphous hump seen in SXRD patterns reveals the amorphous nature of the studied specimens. Mössbauer measurements suggest that: (a) alignment of atomic spins within ribbon plane, (b) changes in average hyperfine field suggests radiation-induced decrease in the inter atomic distance around Mössbauer (Fe) atom, (c) hyperfine field distribution confirms the presence of non-magnetic elements (e.g. – B, P, C) in the first near-neighbor shell of the Fe atom, thus reducing its magnetic moment, and (d) changes in isomer shift suggests variation in average number of the metalloid near neighbors and their distances. Minor changes in soft magnetic behavior – watt loss and, coercivity after an irradiation dose of 2 × 10{sup 13} ions/cm{sup 2} suggests prospective application of Fe{sub 77}P{sub 8}Si{sub 3}C{sub 5}Al{sub 2}Ga{sub 1}B{sub 4} alloy as core material in accelerators (radio frequency cavities).

  12. A comprehensive study of soft magnetic materials based on FeSi spheres and polymeric resin modified by silica nanorods

    Czech Academy of Sciences Publication Activity Database

    Strečková, M.; Füzer, J.; Kobera, Libor; Brus, Jiří; Fáberová, M.; Bureš, R.; Kollár, P.; Lauda, M.; Medvecký, L.; Girman, V.; Hadraba, Hynek; Baťková, M.; Baťko, I.

    2014-01-01

    Roč. 147, č. 3 (2014), s. 649-660 ISSN 0254-0584 Institutional support: RVO:61389013 ; RVO:68081723 Keywords : composite materials * magnetic materials * chemical synthesis Subject RIV: CD - Macromolecular Chemistry; JH - Ceramics, Fire-Resistant Materials and Glass (UFM-A) Impact factor: 2.259, year: 2014

  13. Broadband strip-line ferromagnetic resonance spectroscopy of soft magnetic CoFeTaZr patterned thin films

    Science.gov (United States)

    Gupta, S.; Kumar, D.; Jin, T. L.; Nongjai, R.; Asokan, K.; Ghosh, A.; Aparnadevi, M.; Suri, P.; Piramanayagam, S. N.

    2018-05-01

    In this paper, magnetic and magnetization dynamic properties of compositionally patterned Co46Fe40Ta9Zr5 thin films are investigated. A combination of self-assembly and ion-implantation was employed to locally alter the composition of Co46Fe40Ta9Zr5 thin film in a periodic manner. 20 keV O+ and 60 keV N+ ions were implanted at different doses in order to modify the magnetization dynamic properties of the samples in a controlled fashion. Magnetic hysteresis loop measurements revealed significant changes in the coercivity for higher influences of 5 × 1016 ions per cm2. In particular, N+ implantation was observed to induce two phase formation with high and low coercivities. Broadband strip-line ferromagnetic resonance spectroscopy over wide range of frequency (8 - 20 GHz) was used to study the magnetization dynamics as a function of ion-beam dosage. With higher fluences, damping constant showed a continuous increase from 0.0103 to 0.0430. Such control of magnetic properties at nano-scale using this method is believed to be useful for spintronics and microwave device applications.

  14. Photoactivated Composite Biomaterial for Soft Tissue Restoration in Rodents and in Humans

    Science.gov (United States)

    Nahas, Zayna; Reid, Branden; Coburn, Jeannine M.; Axelman, Joyce; Chae, Jemin J.; Guo, Qiongyu; Trow, Robert; Thomas, Andrew; Hou, Zhipeng; Lichtsteiner, Serge; Sutton, Damon; Matheson, Christine; Walker, Patricia; David, Nathaniel; Mori, Susumu; Taube, Janis M.; Elisseeff, Jennifer H.

    2015-01-01

    Soft tissue reconstruction often requires multiple surgical procedures that can result in scars and disfiguration. Facial soft tissue reconstruction represents a clinical challenge because even subtle deformities can severely affect an individual’s social and psychological function. We therefore developed a biosynthetic soft tissue replacement composed of poly(ethylene glycol) (PEG) and hyaluronic acid (HA) that can be injected and photocrosslinked in situ with transdermal light exposure. Modulating the ratio of synthetic to biological polymer allowed us to tune implant elasticity and volume persistence. In a small-animal model, implanted photocrosslinked PEG-HA showed a dose-dependent relationship between increasing PEG concentration and enhanced implant volume persistence. In direct comparison with commercial HA injections, the PEG-HA implants maintained significantly greater average volumes and heights. Reversibility of the implant volume was achieved with hyaluronidase injection. Pilot clinical testing in human patients confirmed the feasibility of the transdermal photocrosslinking approach for implantation in abdomen soft tissue, although an inflammatory response was observed surrounding some of the materials. PMID:21795587

  15. Analysis of the magnetic properties in hard-magnetic nanofibers composite

    Science.gov (United States)

    Murillo-Ortíz, R.; Mirabal-García, M.; Martínez-Huerta, J. M.; Cabal Velarde, J. G.; Castaneda-Robles, I. E.; Lobo-Guerrero, A.

    2018-03-01

    The magnetic properties of the strontium hexaferrite nanoparticles were studied as they were embedded at different concentrations in poly(vinyl alcohol) (PVA) nanofibers. These nanoparticles were prepared using the Pechini method and a low frequency sonication process obtaining a 3.4 nm average diameter. The composite consisting of hard magnetic nanoparticles homogeneously dispersed in a polymeric matrix was fabricated using a homemade electrospinning with 25 kV DC power supply. The obtained nanofibers had an average diameter of 110 nm, and nanoparticles were arranged and distributed within the nanofibers under the influence of a strong electric field. The configuration of the magnetic nanoparticles in the PVA nanofibers was such that the interparticle exchange interaction became negligible, while the magnetostatic interaction turned out predominant. The results reveal a considerable improvement in the energy product (BHmax) and in the squareness ratio (Mr/Ms) for nanoparticle concentrations between 15 and 30% per gram of PVA. The nanoparticles arrangement occurred at densities below the percolation concentration enhanced the hard-magnetic properties of the nanofibers, which indicates that the organization of the particles along the fibers induces anisotropy from the magnetostatic interaction among the magnetic nanoparticles. Finally, we close the discussion analyzing the observed effect below the percolation threshold, where the induced anisotropy caused the reduction of the full-width at half-maximum of the switching field distribution curves.

  16. Catalytic Propulsion and Magnetic Steering of Soft, Patchy Microcapsules: Ability to Pick-Up and Drop-Off Microscale Cargo.

    Science.gov (United States)

    Lu, Annie Xi; Liu, Yijing; Oh, Hyuntaek; Gargava, Ankit; Kendall, Eric; Nie, Zhihong; DeVoe, Don L; Raghavan, Srinivasa R

    2016-06-22

    We describe the creation of polymeric microcapsules that can exhibit autonomous motion along defined trajectories. The capsules are made by cross-linking aqueous microdroplets of the biopolymer chitosan using glutaraldehyde. A coflow microfluidic tubing device is used to generate chitosan droplets containing nanoparticles (NPs) with an iron (Fe) core and a platinum (Pt) shell. The droplets are then incubated in a Petri dish with the cross-linking solution, and an external magnet is placed below the Petri dish to pull the NPs together as a collective "patch" on one end of each droplet. This results in cross-linked capsules (∼150 μm in diameter) with an anisotropic (patchy) structure. When these capsules are placed in a solution of H2O2, the Pt shell of the NPs catalyzes the decomposition of H2O2 into O2 gas, which is ejected from the patchy end in the form of bubbles. As a result, the capsules (which are termed micromotors) move in a direction opposite to the bubbles. Furthermore, the micromotors can be steered along specific paths by an external magnet (the magnetic response arises due to the Fe in the core of the NPs). A given micromotor can thus be directed to meet with and adhere to an inert capsule, i.e., a model cargo. Adhesion occurs due to the soft nature of the two structures. Once the cargo is picked up, the micromotor-cargo pair can be moved along a specific path to a destination, whereupon the cargo can be released from the micromotor. We believe these soft micromotors offer significant benefits over their existing hard counterparts because of their biocompatibility, biodegradability, and ability to encapsulate a variety of payloads.

  17. Thermal, magnetic, and structural properties of soft magnetic FeCrNbCuSiB alloy ribbons

    International Nuclear Information System (INIS)

    Rosales-Rivera, A.; Valencia, V.H.; Quintero, D.L.; Pineda-Gomez, P.; Gomez, M.

    2006-01-01

    The thermal, magnetic and structural properties of amorphous magnetic Fe 73.5-x Cr x Nb 3 Cu 1 Si 13.5 B 9 alloy ribbons, with x=0, 2, 4, 6, 8, and 10, were studied by using differential scanning calorimetry (DSC), thermogravimetric analysis (TGA), magneto-impedance measurements and X-ray diffraction (XRD). The ribbons exhibit ultrasoft magnetic behavior, especially giant magneto-impedance effect, GMI. A three-peak behavior was observed in GMI curves. Particular attention has been given to observation of crystallization kinetics via DSC and TGA. The primary crystallization T pcr , and Curie T c , temperatures were determined from DSC and TGA data, respectively. The effect of partial substitution of iron by Cr on the thermal and magnetic properties is discussed

  18. The diagnostic value of diffusion-weighted magnetic resonance imaging in soft tissue abscesses

    Energy Technology Data Exchange (ETDEWEB)

    Unal, Ozkan; Koparan, Halil Ibrahim [Yuezuencue Yil University, Department of Radiology, Van (Turkey); Avcu, Serhat, E-mail: serhatavcu@hotmail.com [Yuezuencue Yil University, Department of Radiology, Van (Turkey); Kalender, Ali Murat [Yuezuencue Yil University, Department of Orthopaedics, General Surgery, Van (Turkey); Kisli, Erol [Yuezuencue Yil University, Department of General Surgery, Van (Turkey)

    2011-03-15

    Purpose: To study the diagnostic value of diffusion-weighted imaging (DWI) in soft tissue abscesses. Materials and methods: Fifty patients were included in this study who were thought to have soft tissue abscess or cystic lesion as a result of clinical and radiological examinations. Localisations of the lesions were: 1 periorbital, 3 breast, 14 intraabdominal, and 32 intramuscular lesions. After other radiological examinations, DWI was performed. The signal intensity values of the lesions were evaluated qualitatively according to the hyperintensity on b-1000 DWI, using 1.5 T MR system. All of the lesions were aspirated after DWI, and detection of pus in the aspiration material was accepted as gold standard for the diagnosis of abscess. Results: In 38 of the 50 patients, hyperintensity was obtained on diffusion-weighted images. False-positive results were maintained in 2 of these patients, and true-positive results were maintained in 36 of them. In 11 of the 50 patients, hypointensity was visualised on diffusion-weighted images. False-negative results were maintained in 3 of these patients, and true-negative results were maintained in 8 of them. An abscess which was seen on post-contrast conventional MRI could not be seen on DWI, and this was regarded as false-negative. Conclusion: The sensitivity and specificity of diffusion-weighted images for detecting soft tissue abscesses were found to be 92% and 80%, respectively. DWI has a high diagnostic value in soft tissue abscesses, and is an important imaging modality that may be used for the differentiation of cysts and abscesses.

  19. The diagnostic value of diffusion-weighted magnetic resonance imaging in soft tissue abscesses

    International Nuclear Information System (INIS)

    Unal, Ozkan; Koparan, Halil Ibrahim; Avcu, Serhat; Kalender, Ali Murat; Kisli, Erol

    2011-01-01

    Purpose: To study the diagnostic value of diffusion-weighted imaging (DWI) in soft tissue abscesses. Materials and methods: Fifty patients were included in this study who were thought to have soft tissue abscess or cystic lesion as a result of clinical and radiological examinations. Localisations of the lesions were: 1 periorbital, 3 breast, 14 intraabdominal, and 32 intramuscular lesions. After other radiological examinations, DWI was performed. The signal intensity values of the lesions were evaluated qualitatively according to the hyperintensity on b-1000 DWI, using 1.5 T MR system. All of the lesions were aspirated after DWI, and detection of pus in the aspiration material was accepted as gold standard for the diagnosis of abscess. Results: In 38 of the 50 patients, hyperintensity was obtained on diffusion-weighted images. False-positive results were maintained in 2 of these patients, and true-positive results were maintained in 36 of them. In 11 of the 50 patients, hypointensity was visualised on diffusion-weighted images. False-negative results were maintained in 3 of these patients, and true-negative results were maintained in 8 of them. An abscess which was seen on post-contrast conventional MRI could not be seen on DWI, and this was regarded as false-negative. Conclusion: The sensitivity and specificity of diffusion-weighted images for detecting soft tissue abscesses were found to be 92% and 80%, respectively. DWI has a high diagnostic value in soft tissue abscesses, and is an important imaging modality that may be used for the differentiation of cysts and abscesses.

  20. Improved soft magnetic properties in nanocrystalline FeCuNbSiB Nanophy{sup ®} cores by intense magnetic field annealing

    Energy Technology Data Exchange (ETDEWEB)

    Madugundo, Rajasekhar; Geoffroy, Olivier [Univ. Grenoble Alpes, Inst NEEL, F-38000 Grenoble (France); CNRS, Inst NEEL, F-38000 Grenoble (France); Grenoble Electrical Engineering Laboratory (G2Elab), Bâtiment GreEn-ER, 21 avenue des martyrs, 38031 Grenoble (France); Waeckerle, Thierry [Aperam Research Center, 58160 Imphy (France); Frincu, Bianca; Kodjikian, Stéphanie [Univ. Grenoble Alpes, Inst NEEL, F-38000 Grenoble (France); CNRS, Inst NEEL, F-38000 Grenoble (France); Rivoirard, Sophie, E-mail: sophie.rivoirard@neel.cnrs.fr [Univ. Grenoble Alpes, Inst NEEL, F-38000 Grenoble (France); CNRS, Inst NEEL, F-38000 Grenoble (France)

    2017-01-15

    The effect of high external magnetic field (up to 7 T) on soft magnetic properties in nanocrystalline Fe{sub 74.1}Si{sub 15.7}Nb{sub 3.1}B{sub 6.1}Cu{sub 1} Nanophy{sup ®} cores has been investigated. The as-quenched amorphous ribbons were nanocrystallized by annealing between 540 and 620 °C in transverse magnetic field. By varying annealing field from 0 to 7 T, induced anisotropy ranging from as low as 4 J/m{sup 3} to as high as 41 J/m{sup 3} is obtained. It is responsible for an increase in the cut-off frequency up to 300 kHz when the material is submitted to dynamic magnetic excitations. A minimum coercivity of 0.74 A/m is observed in the core annealed in 1 T associated to low losses. The relative permeability decreases on increasing the annealing field intensity with a minimum value of 13,654 at 7 T. Such permeability level opens the way to new applications of the Nanophy{sup ®} alloys. - Highlights: • Effect of magnetic field (0–7 T) in nanocrystalline Nanophy{sup ®} cores was investigated. • Amorphous ribbons were annealing between 540 and 620 °C in transverse magnetic field. • Induced anisotropy ranging from 4 to 41 J/m{sup 3} was obtained by annealing in field 0−7 T. • Permeability ranging between 135,122 and 13,654 was obtained. • A minimum coercivity of 0.74 A/m was observed.

  1. Enhancement of soft magnetic properties of La–Zn co-doped nanocrystalline Ni{sub 2}Y hexaferrite

    Energy Technology Data Exchange (ETDEWEB)

    Hosseinkhan Nejad, Ehsan, E-mail: ehsanhkhani66@gmail.com [Department of Material Science and Engineering, Semnan University, Semnan (Iran, Islamic Republic of); Farzin, Yousef Alizad [School of Metallurgy and Materials Engineering, College of Engineering, University of Tehran, P.O. Box 14395-553, Tehran (Iran, Islamic Republic of); Heydari, Mohammad Ali [Department of Material Science and Engineering, Azad University of Saveh, Saveh (Iran, Islamic Republic of)

    2017-02-01

    The La-Zn substituted nanocrystalline Sr{sub 2−x}La{sub x}Ni{sub 2}Fe{sub 12−x}Zn{sub x}O{sub 22} (with x=0.0, 0.4, 0.5, 0.6, 0.7, 0.8 and 0.9) hexaferrites were prepared using sol-gel auto-combustion method to investigate the microstructure and magnetic properties. Fourier transform infrared spectroscopy (FT-IR) spectra showed two main absorption bands at 429 and 594 cm{sup −1} corresponding to the stretching and vibration of tetrahedral and octahedral groups in S blocks. The X-ray diffraction pattern confirmed the phase formation of Y-type hexaferrite with R-3 m space group which also provided the lattice constants and crystallite sizes of each product. Furthermore, the crystallite size (D) was found to be in the range of 31.4–43.1 nm. Field emission electron microscopy (FESEM) images confirmed that the grain size was reduced from 600 to 150 nm due to the increase of dopant cations and, subsequently, caused soft magnetic properties to improve. By performing a thorough investigation on the M–H hysteresis loops, it was found that the magnetization first increased up to x=0.7 and then decreased, while coercivity monotonously decreased from 1313 to 569 Oe. This behavior can be attributed to the migration of Fe3+ ions from spin-down to spin-up, local strains, deviation of spin arrangement and strength of superexchange interactions. - Highlights: • A systematic study was done on the effect of La–Zn substitution of Ni{sub 2}Y. • The crystallite size of this ferrites is in the range of 31.4–41.3 nm. • Coercivity of synthesis samples monotonously decreased from 1313 to 569 Oe. • The magnetization and the coercivity strongly depend on La–Zn substitution. • The soft magnetic properties of ferrites improved by increasing of dopant cations.

  2. Magnetite/CdTe magnetic-fluorescent composite nanosystem for magnetic separation and bio-imaging

    International Nuclear Information System (INIS)

    Kale, Anup; Yadav, Prasad; Gholap, Haribhau; Jog, J P; Ogale, Satishchandra; Kale, Sonia; Shastry, Padma; Pasricha, Renu; Lefez, Benoit; Hannoyer, Beatrice

    2011-01-01

    A new synthesis protocol is described to obtain a CdTe decorated magnetite bifunctional nanosystem via dodecylamine (DDA) as cross linker. High resolution transmission electron microscopy (HRTEM), energy-dispersive x-ray spectroscopy (EDAX), vibrating sample magnetometry (VSM), Fourier transform infrared spectroscopy (FTIR), diffuse reflectance spectroscopy (DRS) and fluorescence microscopy are used to characterize the constitution, size, composition and physical properties of these superparamagnetic-fluorescent nanoparticles. These CdTe decorated magnetite nanoparticles were then functionalized with anti-epidermal growth factor receptor (EGFR) antibody to specifically target cells expressing this receptor. The EGFR is a transmembrane glycoprotein and is expressed on tumor cells from different tissue origins including human leukemic cell line Molt-4 cells. The magnetite-CdTe composite nanosystem is shown to perform excellently for specific selection, magnetic separation and fluorescent detection of EGFR positive Molt-4 cells from a mixed population. Flow cytometry and confocal laser scanning microscopy results show that this composite nanosystem has great potential in antibody functionalized magnetic separation and imaging of cells using cell surface receptor antibody.

  3. Soft-edged magnet models for higher-order beam-optics map codes

    International Nuclear Information System (INIS)

    Walstrom, P.L.

    2004-01-01

    Continuously varying surface and volume source-density distributions are used to model magnetic fields inside of cylindrical volumes. From these distributions, a package of subroutines computes on-axis generalized gradients and their derivatives at arbitrary points on the magnet axis for input to the numerical map-generating subroutines of the Lie-algebraic map code Marylie. In the present version of the package, the magnet menu includes: (1) cylindrical current-sheet or radially thick current distributions with either open boundaries or with a surrounding cylindrical boundary with normal field lines (which models high-permeability iron), (2) Halbach-type permanent multipole magnets, either as sheet magnets or as radially thick magnets, (3) modeling of arbitrary fields inside a cylinder by use of a fictitious current sheet. The subroutines provide on-axis gradients and their z derivatives to essentially arbitrary order, although in the present third- and fifth-order Marylie only the zeroth through sixth derivatives are needed. The formalism is especially useful in beam-optics applications, such as magnetic lenses, where realistic treatment of fringe-field effects is needed

  4. Magnetic properties of Cobalt thin films deposited on soft organic layers

    Energy Technology Data Exchange (ETDEWEB)

    Bergenti, I. [ISMN-CNR via P. Gobetti 101, Bologna 40129 (Italy)]. E-mail: i.bergenti@bo.ismn.cnr.it; Riminucci, A. [ISMN-CNR via P. Gobetti 101, Bologna 40129 (Italy); Arisi, E. [ISMN-CNR via P. Gobetti 101, Bologna 40129 (Italy); Murgia, M. [ISMN-CNR via P. Gobetti 101, Bologna 40129 (Italy); Cavallini, M. [ISMN-CNR via P. Gobetti 101, Bologna 40129 (Italy); Solzi, M. [Dipartimento di Fisica dell' Universita di Parma and CNISM, Parco Area delle Scienze 7/A, Parma 43100 (Italy); Casoli, F. [IMEM-CNR Parco Area delle Scienze 37/A, Parma 43100 (Italy); Dediu, V. [ISMN-CNR via P. Gobetti 101, Bologna 40129 (Italy)

    2007-09-15

    Magnetic and morphological properties of Cobalt thin films grown by RF sputtering on organic Alq3 layers were investigated by magneto-optical Kerr effect (MOKE) technique and atomic force microscopy (AFM). The AFM images indicate a template growth of Co layers on top of Alq3, the magnetic film 'decorates' the surface of organic material. This peculiar morphology induces a strong uniaxial magnetic anisotropy in the Co films, as detected by MOKE measurements. Results are important for the operation of a new class of devices-vertical organic spin valves.

  5. Discrepancies between soft x-ray emissivity contours and magnetic flux surfaces in Alcator C-Mod

    International Nuclear Information System (INIS)

    Borras, M.C.; Granetz, R.S.

    1996-01-01

    The soft x-ray diagnostic system of Alcator C-Mod, equipped with 152 detectors distributed in four arrays, is used to obtain iso-emissivity surfaces. These surfaces have been characterized by giving their elongation and relative shift from the centre of the tokamak as functions of plasma radius. Flux surfaces, provided by magnetic diagnostics, have also been described with elongation and shift. Results from the comparison of the two sets of geometric parameters obtained from magnetic and x-ray diagnostics are presented. We find that, whereas the shifts obtained from these two diagnostic methods are always in good agreement, the corresponding elongation curves show different patterns. An agreement between elongations better than 2% is only found in a range of about 2 cm in minor radius. On the other hand, the elongations can differ by 10% towards the plasma edge and the plasma centre. Error bars for the x-ray diagnostic are obtained by propagating the effect of ± 1% random errors at the detector signals, and can amount to ± 1-2% of the estimated values near the edge and the centre of the plasma. The estimated uncertainties in the determination of elongation from magnetic flux surfaces are of the order of 4%. A series of tests and simulations performed to verify the accuracy of the X-ray diagnostic system is presented. The discrepancies found could imply the existence of asymmetries in impurity concentration. (Author)

  6. Tailoring of magnetoimpedance effect and magnetic softness of Fe-rich glass-coated microwires by stress- annealing.

    Science.gov (United States)

    Zhukova, V; Blanco, J M; Ipatov, M; Churyukanova, M; Taskaev, S; Zhukov, A

    2018-02-16

    There is a pressing need for improving of the high-frequency magneto-impedance effect of cost-effective soft magnetic materials for use in high-performance sensing devices. The impact of the stress-annealing on magnetic properties and high frequency impedance of Fe-rich glass-coated microwires was studied. Hysteresis loops of Fe-rich microwires have been considerably affected by stress- annealing. In stress-annealed Fe- rich microwire we obtained drastic decreasing of coercivity and change of character of hysteresis loop from rectangular to linear. By controlling stress-annealing conditions (temperature and time) we achieved drastic increasing (by order of magnitude) of giant magnetoimpedance ratio. Coercivity, remanent magnetization, diagonal and of-diagonal magnetoimpedance effect of Fe-rich microwires can be tuned by stress-annealing conditions: annealing temperature and time. Observed experimental results are discussed considering relaxation of internal stresses, compressive "back-stresses" arising after stress annealing and topological short range ordering.

  7. Structure and soft magnetic properties of Fe-Si-B-P-Cu nanocrystalline alloys with minor Mn addition

    Directory of Open Access Journals (Sweden)

    Xingjie Jia

    2018-05-01

    Full Text Available Addition of minor Mn effectively improves the amorphous-forming ability and thermal stability of the Fe85Si2B8P4Cu1 alloy. With increasing the Mn content from 0 to 3 at.%, the critical thickness for amorphous formation and onset temperature of the primary crystallization increase from 14 μm and 659 K to 27 μm and 668 K, respectively. The fine nanocrystalline structure with α-Fe grains in size (D of < 20 nm was obtained for the annealed amorphous alloys, which show excellent soft magnetic properties. The alloying of Mn reduces the coercivity (Hc by decreasing the D value and widens the optimum annealing temperature range for obtaining low Hc, although the saturation magnetic flux density (Bs is decreased slightly. The Fe83Mn2Si2B8P4Cu1 nanocrystalline alloy possesses fine structure with a D of ∼17.5 nm, and exhibits a high Bs of ∼1.75 T and a low Hc of ∼5.9 A/m. The mechanism related to the alloying effects on the structure and magnetic properties was discussed in term of the crystallization activation energy.

  8. Structure and soft magnetic properties of Fe-Si-B-P-Cu nanocrystalline alloys with minor Mn addition

    Science.gov (United States)

    Jia, Xingjie; Li, Yanhui; Wu, Licheng; Zhang, Wei

    2018-05-01

    Addition of minor Mn effectively improves the amorphous-forming ability and thermal stability of the Fe85Si2B8P4Cu1 alloy. With increasing the Mn content from 0 to 3 at.%, the critical thickness for amorphous formation and onset temperature of the primary crystallization increase from 14 μm and 659 K to 27 μm and 668 K, respectively. The fine nanocrystalline structure with α-Fe grains in size (D) of < 20 nm was obtained for the annealed amorphous alloys, which show excellent soft magnetic properties. The alloying of Mn reduces the coercivity (Hc) by decreasing the D value and widens the optimum annealing temperature range for obtaining low Hc, although the saturation magnetic flux density (Bs) is decreased slightly. The Fe83Mn2Si2B8P4Cu1 nanocrystalline alloy possesses fine structure with a D of ˜17.5 nm, and exhibits a high Bs of ˜1.75 T and a low Hc of ˜5.9 A/m. The mechanism related to the alloying effects on the structure and magnetic properties was discussed in term of the crystallization activation energy.

  9. Magnetic characterisation of large grain, bulk Y–Ba–Cu–O superconductor–soft ferromagnetic alloy hybrid structures

    International Nuclear Information System (INIS)

    Philippe, M.P.; Fagnard, J.-F.; Kirsch, S.; Xu, Z.; Dennis, A.R.; Shi, Y.-H.; Cardwell, D.A.; Vanderheyden, B.; Vanderbemden, P.

    2014-01-01

    Highlights: • Large grain, bulk YBaCuO superconductor (SC) combined with ferromagnetic elements. • The flux lines curve outwards through the ferromagnet in the remanent state. • The trapped field in the SC is enhanced by the presence of the ferromagnet. • The effects of the SC and the ferromagnet add when the ferromagnet is saturated. - Abstract: Large grain, bulk Y–Ba–Cu–O (YBCO) high temperature superconductors (HTS) have significant potential for use in a variety of practical applications that incorporate powerful quasi-permanent magnets. In the present work, we investigate how the trapped field of such magnets can be improved by combining bulk YBCO with a soft FeNi, ferromagnetic alloy. This involves machining the alloy into components of various shapes, such as cylinders and rings, which are attached subsequently to the top surface of a solid, bulk HTS cylinder. The effect of these modifications on the magnetic hysteresis curve and trapped field of the bulk superconductor at 77 K are then studied using pick-up coil and Hall probe measurements. The experimental data are compared to finite element modelling of the magnetic flux distribution using Campbell’s algorithm. Initially we establish the validity of the technique involving pick-up coils wrapped around the bulk superconductor to obtain its magnetic hysteresis curve in a non-destructive way and highlight the difference between the measured signal and the true magnetization of the sample. We then consider the properties of hybrid ferromagnet/superconductor (F/S) structures. Hall probe measurements, together with the results of the model, establish that flux lines curve outwards through the ferromagnet, which acts, effectively, like a magnetic short circuit. Magnetic hysteresis curves show that the effects of the superconductor and the ferromagnet simply add when the ferromagnet is saturated fully by the applied field. The trapped field of the hybrid structure is always larger than that of the

  10. Preparation and characterization of temperature-responsive magnetic composite particles for multi-modal cancer therapy.

    Science.gov (United States)

    Yao, Aihua; Chen, Qi; Ai, Fanrong; Wang, Deping; Huang, Wenhai

    2011-10-01

    The temperature-responsive magnetic composite particles were synthesized by emulsion-free polymerization of N-isopropylacrylamide (NIPAAm) and acrylamide (Am) in the presence of oleic acid-modified Fe(3)O(4) nanoparticles. The magnetic properties and heat generation ability of the composite particles were characterized. Furthermore, temperature and alternating magnetic field (AMF) triggered drug release behaviors of vitamin B(12)-loaded composite particles were also examined. It was found that composite particles enabled drug release to be controlled through temperature changes in the neighborhood of lower critical solution temperature. Continuous application of AMF resulted in an accelerated release of the loaded drug. On the other hand, intermittent AMF application to the composite particles resulted in an "on-off", stepwise release pattern. Longer release duration and larger overall release could be achieved by intermittent application of AMF as compared to continuous magnetic field. Such composite particles may be used for magnetic drug targeting followed by simultaneous hyperthermia and drug release.

  11. Surface effects on magnetic Freedericksz transition in ferronematics with soft particle anchoring

    International Nuclear Information System (INIS)

    Bena, R.-E.; Petrescu, Emil

    2003-01-01

    The magnetic field-induced Freedericksz transition in a homeotropically aligned ferronematic (FN) in the case of weak anchoring molecules to the walls is studied. A correction to the Burylov-Raikher expression for the second-order transition threshold field is found. The possibility of a first-order transition is discussed in connection with the similar results for nematic liquid crystals. The saturation magnetic field is also obtained in terms of FN, surface and device parameters

  12. Development of a high gradient rf system using a nanocrystalline soft magnetic alloy

    Directory of Open Access Journals (Sweden)

    Chihiro Ohmori

    2013-11-01

    Full Text Available The future high intensity upgrade project of the J-PARC (Japan Proton Accelerator Research Complex MR (Main Ring includes developments of high gradient rf cavities and magnet power supplies for high repetition rate. The scenario describing the cavity replacements is reported. By the replacement plan, the total acceleration voltage will be almost doubled, while the number of rf stations remains the same. The key issue is the development of a high gradient rf system using high impedance magnetic alloy, FT3L. The FT3L is produced by the transverse magnetic field annealing although the present cavity for the J-PARC adopts the magnetic alloy, FT3M, which is annealed without magnetic field. After the test production using a large spectrometer magnet in 2011, a dedicated production system for the FT3L cores was assembled in 2012. This setup demonstrated that we can produce material with 2 times higher μ_{p}^{′}Qf product compared to the cores used for present cavities. In this summer, the production system was moved to the company from J-PARC and is used for mass production of 280 FT3L cores for the J-PARC MR. The cores produced in the first test production are already used for standard machine operation. The operation experience shows that the power loss in the cores was reduced significantly as expected.

  13. Application of magnetic resonance to the diagnosis of tumorous processes in soft tissues

    International Nuclear Information System (INIS)

    Kreuzberg, B.

    1998-01-01

    The methodology and results of MR examination of 22 patients with soft tissue tumors (STT) are summarized, and the findings of nine histologically confirmed results are demonstrated. Discussion of the results concentrates on the reliability of the specific diagnosis (which is relatively low) and reliability of discrimination between non-malignant and malignant processes (which is relatively high). The reliability of the examination is enhanced by the intravenous administration of the paramagnetic contrast substance. It is concluded that the examination is of great value for the surgeon and his decision making, in particular with respect to staging. MR completes the set of imaging methods in the diagnosis of STT

  14. Gadolinium-DTPA enhancement of experimental soft tissue carcinoma and hemorrhage in magnetic resonance imaging

    International Nuclear Information System (INIS)

    Pettersson, H.; Ackerman, N.; Kaude, J.; Googe, R.E.; Mancuso, A.A.; Scott, K.N.; Hackett, R.H.; Hager, D.A.; Caballero, S.; Florida Univ., Gainesville

    1987-01-01

    An experimental series in the rabbit was performed to test gadolinium-DTPA (Gd-DTPA) enhancement of VX-2 carcinoma and hemorrhages induced in the soft tissues. The recognition of both malignant and benign lesions was greatly facilitated on T1 weighted images after intravenous administration of 0.3 mmol Gd-DTPA/kg body weigth because of reduced T1 relaxation times. Gd-DTPA enhancement reached its maximum after 10-15 minutes and was most apparent in tumor tissue, connective tissue surrounding the tumor and in the area of fresh hemorrhage. (orig.)

  15. Composite particles formed by complexation of poly(methacrylic acid) - stabilized magnetic fluid with chitosan: Magnetic material for bioapplications.

    Science.gov (United States)

    Safarik, Ivo; Stepanek, Miroslav; Uchman, Mariusz; Slouf, Miroslav; Baldikova, Eva; Nydlova, Leona; Pospiskova, Kristyna; Safarikova, Mirka

    2016-10-01

    A simple procedure for the synthesis of magnetic fluid (ferrofluid) stabilized by poly(methacrylic acid) has been developed. This ferrofluid was used to prepare a novel type of magnetically responsive chitosan-based composite material. Both ferrofluid and magnetic chitosan composite were characterized by a combination of microscopy (optical microscopy, TEM, SEM), scattering (static and dynamic light scattering, SANS) and spectroscopy (FTIR) techniques. Magnetic chitosan was found to be a perspective material for various bioapplications, especially as a magnetic carrier for immobilization of enzymes and cells. Lipase from Candida rugosa was covalently attached after cross-linking and activation of chitosan using glutaraldehyde. Baker's yeast cells (Saccharomyces cerevisiae) were incorporated into the chitosan composite during its preparation; both biocatalysts were active after reaction with appropriate substrates. Copyright © 2016 Elsevier B.V. All rights reserved.

  16. Magnetic resonance imaging of intraoral hard and soft tissues using an intraoral coil and FLASH sequences

    Energy Technology Data Exchange (ETDEWEB)

    Fluegge, Tabea; Eisenbeiss, Anne-Kathrin; Schmelzeisen, Rainer; Nelson, Katja [University Medical Center Freiburg, Department of Oral and Maxillofacial Surgery, Freiburg (Germany); Hoevener, Jan-Bernd; Ludwig, Ute; Hennig, Juergen [University Medical Center Freiburg, Medical Physics, Department of Radiology, Freiburg (Germany); Spittau, Bjoern [Albert Ludwig University of Freiburg, Institute of Anatomy and Cell Biology, Freiburg (Germany)

    2016-12-15

    To ascertain the feasibility of MRI as a non-ionizing protocol for routine dentomaxillofacial diagnostic imaging. Wireless coils were used for MRI of intraoral hard and soft tissues. FLASH MRI was applied in vivo with a mandible voxel size of 250 x 250 x 500 μm{sup 3}, FOV of 64 x 64 x 28 mm{sup 3} and acquisition time of 3:57 min and with a maxilla voxel size of 350 μm{sup 3} and FOV of 34 cm{sup 3} in 6:40 min. Ex vivo imaging was performed in 4:38 min, with a resolution of 200 μm{sup 3} and FOV of 36.5 cm{sup 3}. Cone beam (CB) CT of the mandible and subjects were acquired. MRI was compared to CBCT and histological sections. Deviations were calculated with intraclass correlation coefficient (ICC) and coefficient of variation (c{sub v}). A high congruence between CBCT, MRI and specimens was demonstrated. Hard and soft tissues including dental pulp, periodontium, gingiva, cancellous bone and mandibular canal contents were adequately displayed with MRI. Imaging of select intraoral tissues was achieved using custom MRI protocols with an easily applicable intraoral coil in a clinically acceptable acquisition time. Comparison with CBCT and histological sections helped demonstrate dimensional accuracy of the MR images. The course of the mandibular canal was accurately displayed with CBCT and MRI. (orig.)

  17. Magnetic resonance imaging of intraoral hard and soft tissues using an intraoral coil and FLASH sequences

    International Nuclear Information System (INIS)

    Fluegge, Tabea; Eisenbeiss, Anne-Kathrin; Schmelzeisen, Rainer; Nelson, Katja; Hoevener, Jan-Bernd; Ludwig, Ute; Hennig, Juergen; Spittau, Bjoern

    2016-01-01

    To ascertain the feasibility of MRI as a non-ionizing protocol for routine dentomaxillofacial diagnostic imaging. Wireless coils were used for MRI of intraoral hard and soft tissues. FLASH MRI was applied in vivo with a mandible voxel size of 250 x 250 x 500 μm 3 , FOV of 64 x 64 x 28 mm 3 and acquisition time of 3:57 min and with a maxilla voxel size of 350 μm 3 and FOV of 34 cm 3 in 6:40 min. Ex vivo imaging was performed in 4:38 min, with a resolution of 200 μm 3 and FOV of 36.5 cm 3 . Cone beam (CB) CT of the mandible and subjects were acquired. MRI was compared to CBCT and histological sections. Deviations were calculated with intraclass correlation coefficient (ICC) and coefficient of variation (c v ). A high congruence between CBCT, MRI and specimens was demonstrated. Hard and soft tissues including dental pulp, periodontium, gingiva, cancellous bone and mandibular canal contents were adequately displayed with MRI. Imaging of select intraoral tissues was achieved using custom MRI protocols with an easily applicable intraoral coil in a clinically acceptable acquisition time. Comparison with CBCT and histological sections helped demonstrate dimensional accuracy of the MR images. The course of the mandibular canal was accurately displayed with CBCT and MRI. (orig.)

  18. Magnetic orientation of single-walled carbon nanotubes or their composites using polymer wrapping

    Directory of Open Access Journals (Sweden)

    Hiroaki Yonemura et al

    2008-01-01

    Full Text Available The magnetic orientation of single-walled carbon nanotubes (SWNTs or the SWNT composites wrapped with polymer using poly[2-methoxy-5-(2'-ethylhexyloxy-1,4-phenylene vinylene] (MEHPPV as the conducting polymer were examined. The formation of SWNT/MEHPPV composites was confirmed by examining absorption and fluorescence spectra. The N,N-dimethylformamide solution of SWNT/MEHPPV composites or the aqueous solution of the shortened SWNTs was introduced dropwise onto a mica or glass plate. The magnetic processing of the composites or the SWNTs was carried out using a superconducting magnet with a horizontal direction (8 T. The AFM images indicated that the SWNT/MEHPPV composites or the SWNTs were oriented randomly without magnetic processing, while with magnetic processing (8 T, they were oriented with the tube axis of the composites or the SWNTs parallel to the magnetic field. In polarized absorption spectra of SWNT/MEHPPV composites on glass plates without magnetic processing, the absorbance due to semiconducting SWNT in the near-IR region in horizontal polarized light was almost the same as that in vertical polarized light. In contrast, with magnetic processing (8 T, the absorbance due to semiconducting SWNT in the horizontal polarization direction against the direction of magnetic field was stronger than that in the vertical polarization direction. Similar results were obtained from the polarized absorption spectra for the shortened SWNTs. These results of polarized absorption spectra also support the magnetic orientation of the SWNT/MEHPPV composites or the SWNTs. On the basis of a comparison of the composites and the SWNTs alone, the magnetic orientation of SWNT/MEHPPV composites is most likely ascribable to the anisotropy in susceptibilities of SWNTs.

  19. Study of soft magnetic iron cobalt based alloys processed by powder injection molding

    International Nuclear Information System (INIS)

    Silva, Aline; Lozano, Jaime A.; Machado, Ricardo; Escobar, Jairo A.; Wendhausen, Paulo A.P.

    2008-01-01

    As a near net shape process, powder injection molding (PIM) opens new possibilities to process Fe-Co alloys for magnetic applications. Due to the fact that PIM does not involve plastic deformation of the material during processing, we envisioned the possibility of eliminating vanadium (V), which is generally added to Fe-Co alloys to improve the ductility in order to enable its further shaping by conventional processes such as forging and cold rolling. In our investigation we have found out two main futures related to the elimination of V, which lead to a cost-benefit gain in manufacturing small magnetic components where high-saturation induction is needed at low frequencies. Firstly, the elimination of V enables the achievement of much better magnetic properties when alloys are processed by PIM. Secondly, a lower sintering temperature can be used when the alloy is processed starting with elemental Fe and Co powders without the addition of V

  20. Ultra-high resistive and anisotropic CoPd-CaF2 nanogranular soft magnetic films prepared by tandem-sputtering deposition

    Science.gov (United States)

    Naoe, Masayuki; Kobayashi, Nobukiyo; Ohnuma, Shigehiro; Iwasa, Tadayoshi; Arai, Ken-Ichi; Masumoto, Hiroshi

    2015-10-01

    Ultra-high resistive and anisotropic soft magnetic films for gigahertz applications are desirable to demonstrate the really practical films. Here we present a study of novel nanogranular films fabricated by tandem-sputtering deposition. Their electromagnetic properties and nanostructure have also been discussed. These films consisted of nanocrystallized CoPd alloy-granules and CaF2 matrix, and a specimen having a composition of (Co0.69Pd0.31)52-(Ca0.31F0.69)48 exhibited distinct in-plane uniaxial anisotropy after uniaxial field annealing with granule growth. Its complex permeability spectra have a ferromagnetic resonance frequency extending to the Super-High-Frequency band due to its higher anisotropy field, and its frequency response was quite well reproduced by a numerical calculation based on the Landau-Lifshitz-Gilbert equation. Furthermore, it was clarified that the CaF2-based nanogranular film exhibits a hundredfold higher electrical resistivity than conventional oxide or nitride-based films. Higher resistivity enables the film thickness to achieve a margin exceeding threefold against eddy current loss. The greater resistivity of nanogranular films is attributed to the wide energy bandgap and superior crystallinity of CaF2 matrix.

  1. Early invasion population structure of quagga mussel and associated benthic invertebrate community composition on soft sediment in a large reservoir

    Science.gov (United States)

    Wittmann, Marion E.; Chandra, Sudeep; Caires, Andrea; Denton, Marianne; Rosen, Michael R.; Wong, Wai Hing; Teitjen, Todd; Turner, Kent; Roefer, Peggy; Holdren, G. Chris

    2010-01-01

    In 2007 an invasive dreissenid mussel species, Dreissena bugensis (quagga mussel), was discovered in Lake Mead reservoir (AZ–NV). Within 2 years, adult populations have spread throughout the lake and are not only colonizing hard substrates, but also establishing in soft sediments at depths ranging from 1 to >100 m. Dreissena bugensis size class and population density distribution differs between basins; cluster analysis revealed 5 adult cohorts within Boulder Basin and Overton Arm but low densities and low cohort survival in the Las Vegas Basin. Regression analysis suggests depth and temperature are not primary controllers of D. bugensis density in Lake Mead, indicating other factors such as sediment type, food availability or other resource competition may be important. Monthly veliger tows showed at least 2 major spawning events per year, with continuous presence of veligers in the water column. Adult mussels have been found in spawn or post-spawn condition in soft sediments in shallow to deep waters (>80 m) indicating the potential for reproduction at multiple depths. Comparisons to a 1986 benthic survey suggest there have been shifts in nondreissenid macroinvertebrate composition; however, it is unclear if this is due to D. bugensis presence. Current distribution of nondreissenid macroinvertebrates is heterogeneous in all 3 basins, and their biodiversity decreased when D. bugensis density was 2500/m2 or greater.

  2. Impact of intra- and extra-osseous soft tissue composition on changes in bone mineral density with weight loss and regain.

    Science.gov (United States)

    Bosy-Westphal, Anja; Later, Wiebke; Schautz, Britta; Lagerpusch, Merit; Goele, Kristin; Heller, Martin; Glüer, Claus-C; Müller, Manfred J

    2011-07-01

    Recent studies report a significant gain in bone mineral density (BMD) after diet-induced weight loss. This might be explained by a measurement artefact. We therefore investigated the impact of intra- and extra-osseous soft tissue composition on bone measurements by dual X-ray absorptiometry (DXA) in a longitudinal study of diet-induced weight loss and regain in 55 women and 17 men (19-46 years, BMI 28.2-46.8 kg/m(2)). Total and regional BMD were measured before and after 12.7 ± 2.2 week diet-induced weight loss and 6 months after significant weight regain (≥30%). Hydration of fat free mass (FFM) was assessed by a 3-compartment model. Skeletal muscle (SM) mass, extra-osseous adipose tissue, and bone marrow were measured by whole body magnetic resonance imaging (MRI). Mean weight loss was -9.2 ± 4.4 kg (P BMAT) were not related to changes in BMD.

  3. Magnetic resonance tomography in skeletal and soft tissue traumas; Magnetisk resonanstomografi ved skjelett- og bloetdelstraumer

    Energy Technology Data Exchange (ETDEWEB)

    Stiris, Morten G

    2000-07-01

    MRI has revolutionised the diagnostic yield in musculo-skeletal trauma. Studies have documented that MRI can be an accurate, cost-effective means of assessing injuries in the knee, the foot and the ankle and it may also be cost-effective in other anatomic locations. MRTI may have a significant impact on decision-making in relation to these patients and on the follow-up. The patient does not need to be moved for evaluation in all the anatomical planes. Each study can also be post-processes if necessary. MRI may be used in patients with fractures for evaluation of complications. The fracture lines as well as accompanying soft tissue damage are well documented.

  4. CRADA/NFE-15-05779 Report: Fabrication of Large Area Printable Composite Magnets

    Energy Technology Data Exchange (ETDEWEB)

    Paranthaman, M Parans [ORNL

    2016-09-29

    The technical objective of this technical collaboration phase I proposal was to fabricate large area NdFeB composite magnets at the Oak Ridge National Laboratory Manufacturing Demonstration Facility (ORNL MDF). The goal was to distribute domestically produced isotropic and highly anisotropic high energy density magnetic particles throughout the composite structure in order to enable site specific placement of magnetic phases and minimize the generated waste associated with permanent magnet manufacturing. Big area additive manufacturing (BAAM) and magnet composite fabrication methods were used in this study. BAAM was used to fabricate 65 vol % isotropic MQP NdFeB magnets in nylon polymer matrix. BAAM magnet cylinder was sliced to two magnetic arc-shaped braces. The density of the small BAAM magnet pieces reached 4.1 g/cm3, and the room temperature magnetic properties are: Intrinsic coercivity Hci = 8.8 kOe, Remanence Br = 4.2 kG, and energy product (BH)max = 3.7 MGOe. Also, 1.5” x 1.5” composite magnets with anisotropic MQA NdFeB magnet in a resin were also fabricated under magnetic field. The unaligned sample had a density of 3.75 g/cm3. However, aligned sample possessed a density of 4.27 g/cm3. The magnetic properties didn’t degrade during this process. This study provides a pathway for preparing composite magnets for various magnetic applications.

  5. On the GHz frequency response in nanocrystalline FeXN ultra-soft magnetic films

    NARCIS (Netherlands)

    Chechenin, NG; Craus, CB; Chezan, AR; Vystavel, T; Boerma, DO; De Hosson, JTM; Niesen, L; Tidrow, SC; Horwitz, JS; Xi, XX; Levy, J

    2002-01-01

    The periodicity and angular spread of the in-plane magnetization for ultrasoft nanocrystalline FeZrN films were estimated from an analysis of the ripple structure, observed in Lorentz transmission electron microscopy (LTEM) images. The influence of the micromagnetic ripple on the ferromagnetic

  6. Effect of heat treatment on the microstructure and properties of Ni based soft magnetic alloy.

    Science.gov (United States)

    Li, Chunhong; Ruan, Hui; Chen, Dengming; Li, Kejian; Guo, Donglin; Shao, Bin

    2018-04-20

    A Ni-based alloy was heat treated by changing the temperature and ambient atmosphere of the heat treatment. Morphology, crystal structure, and physical performance of the Ni-based alloy were characterized via SEM, XRD, TEM, and PPMS. Results show that due to the heat treatment process, the grain growth of the Ni-based alloy and the removal of impurities and defects are promoted. Both the orientation and stress caused by rolling are reduced. The permeability and saturation magnetization of the alloy are improved. The hysteresis loss and coercivity are decreased. Higher heat treatment temperature leads to increased improvement of permeability and saturation magnetization. Heat treatment in hydrogen is more conducive to the removal of impurities. At the same temperature, the magnetic performance of the heat-treated alloy in hydrogen is better than that of an alloy with heat treatment in vacuum. The Ni-based alloy shows an excellent magnetic performance on 1,373 K heat treatment in hydrogen atmosphere. In this process, the µ m , B s , P u , and H c of the obtained alloy are 427 mHm -1 , 509 mT, 0.866 Jm -3 , and 0.514 Am -1 , respectively. At the same time, the resistivity of alloy decreases and its thermal conductivity increases in response to heat treatment. © 2018 Wiley Periodicals, Inc.

  7. Soft X-ray magnetic dichroism and Faraday rotation measured with linearly polarised light

    Czech Academy of Sciences Publication Activity Database

    Mertins, H. Ch.; Schäfers, F.; Gaupp, A.; Gudat, W.; Kuneš, Jan; Oppeneer, P. M.

    467-468, - (2001), s. 1407-1410 ISSN 0168-9002 Grant - others:ERBFM(XX) GECT 980105; SFB(XX) 463 Institutional research plan: CEZ:AV0Z1010914 Keywords : Faraday-effect * magneto-optical effects * optical properties of consensed matter * synchrotron radiation * X-ray Subject RIV: BM - Solid Matter Physics ; Magnetism Impact factor: 1.026, year: 2001

  8. Ultra-high resistive and anisotropic CoPd–CaF{sub 2} nanogranular soft magnetic films prepared by tandem-sputtering deposition

    Energy Technology Data Exchange (ETDEWEB)

    Naoe, Masayuki, E-mail: naoe@denjiken.ne.jp [Research Institute for Electromagnetic Materials, 2-1-1 Yagiyama-Minami, Taihaku-ku, Sendai 982-0807 (Japan); Kobayashi, Nobukiyo [Research Institute for Electromagnetic Materials, 2-1-1 Yagiyama-Minami, Taihaku-ku, Sendai 982-0807 (Japan); Ohnuma, Shigehiro [Research Institute for Electromagnetic Materials, 2-1-1 Yagiyama-Minami, Taihaku-ku, Sendai 982-0807 (Japan); Frontier Research Institute for Interdisciplinary Sciences, Tohoku University, 6-3 Aramaki-aza-Aoba, Aoba-ku, Sendai 980-8578 (Japan); Iwasa, Tadayoshi; Arai, Ken-Ichi [Research Institute for Electromagnetic Materials, 2-1-1 Yagiyama-Minami, Taihaku-ku, Sendai 982-0807 (Japan); Masumoto, Hiroshi [Frontier Research Institute for Interdisciplinary Sciences, Tohoku University, 6-3 Aramaki-aza-Aoba, Aoba-ku, Sendai 980-8578 (Japan)

    2015-10-01

    Ultra-high resistive and anisotropic soft magnetic films for gigahertz applications are desirable to demonstrate the really practical films. Here we present a study of novel nanogranular films fabricated by tandem-sputtering deposition. Their electromagnetic properties and nanostructure have also been discussed. These films consisted of nanocrystallized CoPd alloy-granules and CaF{sub 2} matrix, and a specimen having a composition of (Co{sub 0.69}Pd{sub 0.31}){sub 52}–(Ca{sub 0.31}F{sub 0.69}){sub 48} exhibited distinct in-plane uniaxial anisotropy after uniaxial field annealing with granule growth. Its complex permeability spectra have a ferromagnetic resonance frequency extending to the Super-High-Frequency band due to its higher anisotropy field, and its frequency response was quite well reproduced by a numerical calculation based on the Landau–Lifshitz–Gilbert equation. Furthermore, it was clarified that the CaF{sub 2}-based nanogranular film exhibits a hundredfold higher electrical resistivity than conventional oxide or nitride-based films. Higher resistivity enables the film thickness to achieve a margin exceeding threefold against eddy current loss. The greater resistivity of nanogranular films is attributed to the wide energy bandgap and superior crystallinity of CaF{sub 2} matrix. - Highlights: • We fabricated high-resistive and anisotropic granular films by tandem-sputtering. • CaF{sub 2}-based films exhibit a hundredfold higher resistivity than conventional films. • Uniaxial field annealing improved the magnetic properties dramatically. • High uniaxial anisotropy extended ferromagnetic resonance frequency to 4 GHz. • Annealed samples can be regarded as a ferromagnetic homogenized material.

  9. An increase of structural order parameter in Fe endash Co endash V soft magnetic alloy after thermal aging

    International Nuclear Information System (INIS)

    Zhu, Q.; Li, L.; Masteller, M.S.; Del Corso, G.J.

    1996-01-01

    Alloys of Fe 49 Co 49 V 2 (Hiperco Alloy 50) (Hiperco is a registered trademark of CRS Holdings, Inc.), both annealed and thermally aged, were studied using anomalous synchrotron x-ray and neutron powder diffraction. Rietveld and diffraction profile analysis indicated both an increase in the structural order parameter and a small lattice expansion (∼0.0004 A) after aging at 450 degree C for 200 h. In addition, a cubic minority phase (<0.3%) was identified in the open-quote open-quote annealed close-quote close-quote sample, which increased noticeably (0.3%→0.8%) as a result of aging. The presence of antiphase domain boundaries in the alloys was also revealed. These results directly correlate with the observed changes in the magnetization behavior and challenge the notion that a open-quote open-quote fully close-quote close-quote ordered Fe endash Co alloy demonstrates optimum soft magnetic properties. copyright 1996 American Institute of Physics

  10. Characterisation of soft magnetic materials by measurement: Evaluation of uncertainties up to 1.8 T and 9 kHz

    Science.gov (United States)

    Elfgen, S.; Franck, D.; Hameyer, K.

    2018-04-01

    Magnetic measurements are indispensable for the characterization of soft magnetic material used e.g. in electrical machines. Characteristic values are used as quality control during production and for the parametrization of material models. Uncertainties and errors in the measurements are reflected directly in the parameters of the material models. This can result in over-dimensioning and inaccuracies in simulations for the design of electrical machines. Therefore, existing influencing factors in the characterization of soft magnetic materials are named and their resulting uncertainties contributions studied. The analysis of the resulting uncertainty contributions can serve the operator as additional selection criteria for different measuring sensors. The investigation is performed for measurements within and outside the currently prescribed standard, using a Single sheet tester and its impact on the identification of iron loss parameter is studied.

  11. Magnetic field effects on the soft mode in a singlet ground-state dimer system: a neutron scattering study of Cs3Cr2Br9

    DEFF Research Database (Denmark)

    Leuenberger, Bruno; Gudel, Hans U.; Feile, Rudolf

    1985-01-01

    Neutron scattering experiments in a magnetic field have been performed on the singlet ground-state dimer system Cs3Cr2Br9. At low fields the Zeeman splitting of the soft mode evolves in agreement with the isotropic random-phase approximation (RPA) model, with the notable absence of a quasielastic...... peak. At a temperature of 1.7K the expected long-range magnetic order is not found at the predicted field of 2.8 T, indicating the shortcomings of the isotropic RPA model in the critical region. Magnetic intensity on the weak nuclear Bragg peak (1¯1¯4) indicates a probable ordering with a ferromagnetic...

  12. Localized Induced Current Stimulation to Neuronal Culture Using Soft Magnetic Material

    Science.gov (United States)

    Saito, Atsushi; Saito, Aki; Moriguchi, Hiroyuki; Kotani, Kiyoshi; Jimbo, Yasuhiko

    To establish precisely focused magnetic stimulation, we developed a Mu-meal based low-frequency localized induced current (LIC) stimulation system with micro-fabricated dual cell-culture chamber. The dual cell-culture chamber was arranged in a concentric circle manner. Between the inner and outer chambers, 4 or 8 connecting micro-channels were fabricated using polydimethylsiloxane (PDMS). Rat cortical neurons were separately cultured in outer and inner chambers. Through the micro-channels, functional synaptic connections were formed. Mu-metal that has very high magnetic permeability was aligned along the outer circle, which allowed us of LIC stimulation to the cells in the outer chamber. Applying low-frequency magnetic fields to the Mu-metal, induced currents were generated and the electrical activity of the cells in the outer chamber was modified depending on the stimulation intensity. Following the modified activity in the outer circles, the cells in the inner chamber also showed slightly depressed activity patterns. These results suggested that our system would be promising for localized stimulation of neuronal networks and highly regulation of network activities.

  13. Interaction of ultra soft magnetic materials with the high-T{sub c} superconductor YBCO

    Energy Technology Data Exchange (ETDEWEB)

    Stahl, Claudia; Treiber, Sebastian; Schuetz, Gisela [Max Planck Institute for Intelligent Systems, Heisenbergstrasse 3, 70569 Stuttgart (Germany); Walker, Patrick [Max Planck Institute for Intelligent Systems, Heisenbergstrasse 3, 70569 Stuttgart (Germany); Aalen University, Beethovenstrasse 1, 73430 Aalen (Germany); Albrecht, Joachim [Aalen University, Beethovenstrasse 1, 73430 Aalen (Germany)

    2013-07-01

    We have grown bilayers of optimally doped YBa{sub 2}Cu{sub 3}O{sub 7-δ} (YBCO) and ferromagnetic CoFeB on single-crystalline substrates by pulsed laser deposition and sputtering. These heterostructures are typically composed of about 100 nm YBCO and several 10 nm of CoFeB. Regarding the superconductor, the properties of the YBCO film change as a consequence of the vicinity of the ferromagnet. In detail we investigated the critical current density as a function of temperature, applied field and time as well as the transition temperature by SQUID magnetization measurements and quantitative magneto-optical measurements. The amorphous material CoFeB exhibits an in plane anisotropy and a very low coercivity. From magneto-optical images we find that the flux line lattice of the superconductor is mapped into the magnet and still visible as significant magnetic out-of-plane contrast at room temperature. We discuss this phenomenon as a new route to high-resolution mapping of the flux line distribution on a nanometer scale.

  14. Preparation and soft magnetic properties of spark plasma sintered compacts based on Fe–Si–B glassy powder

    Energy Technology Data Exchange (ETDEWEB)

    Neamţu, B.V., E-mail: bogdan.neamtu@stm.utcluj.ro [Materials Science and Engineering Department, Technical University of Cluj-Napoca, 400614 Cluj-Napoca (Romania); Marinca, T.F.; Chicinaş, I. [Materials Science and Engineering Department, Technical University of Cluj-Napoca, 400614 Cluj-Napoca (Romania); Isnard, O. [Institut Néel, CNRS/University Joseph Fourier, BP 166, 38042 Grenoble Cédex 9 (France); Popa, F. [Materials Science and Engineering Department, Technical University of Cluj-Napoca, 400614 Cluj-Napoca (Romania); Păşcuţă, P. [Physics and Chemistry Department Technical University of Cluj-Napoca, 400614 Cluj-Napoca (Romania)

    2014-07-05

    Highlights: • Amorphous powder of Fe{sub 75}Si{sub 20}B{sub 5} (at.%) was prepared by wet mechanical alloying. • Spark plasma sintering was used for compaction of amorphous Fe{sub 75}Si{sub 20}B{sub 5} powder. • Increasing SPS time/temperature leads to improvement of AC/DC compacts properties. - Abstract: Amorphous powder of Fe{sub 75}Si{sub 20}B{sub 5} (at.%) was prepared by wet mechanical alloying route using benzene as surfactant. The amorphous phase is obtained after 60 h of milling. Structural, morphological, and thermal characteristics were investigated. The as-milled powder consists in micrometric particles with a mean diameter of 10.4 μm which are formed by the agglomeration of smaller particles. The amorphous powder is thermally stable up to the temperature of 490 °C. Spark plasma sintered compacts were prepared from the amorphous powders at sintering temperatures of 800, 850 and 900 °C. The phases formation and their evolution was investigated by X-ray diffraction technique showing that Fe{sub 3}Si and Fe{sub 2}B are the main phases formed during the spark plasma sintering process. Fe{sub 75}Si{sub 20}B{sub 5} (at.%) samples in the form of a ring were investigated in DC and AC magnetization regime. It was found that the boride phase formation (during sintering) and the low density of the compacts affect the magnetic properties of the compacts. In addition, a superficial contamination of the compacts with carbon (a layer of 2–3 μm) was evidenced, contributing thus to their soft magnetic deterioration. Increasing of the saturation induction, maximum relative permeability and initial relative permeability was observed by increasing both sintering temperature and time. It was generally observed that the compacts with high density have higher total core losses at high frequency.

  15. Soft-tissue perineurioma of the retroperitoneum in a 63-year-old man, computed tomography and magnetic resonance imaging findings: a case report

    Directory of Open Access Journals (Sweden)

    Yasumoto Mayumi

    2010-08-01

    Full Text Available Abstract Introduction Soft-tissue perineuriomas are rare benign peripheral nerve sheath tumors in the subcutis of the extremities and the trunks of young patients. To our knowledge, this the first presentation of the computed tomography and magnetic resonance imaging of a soft-tissue perineurioma in the retroperitoneum with pathologic correlation. Case presentation A 63-year-old Japanese man was referred for assessment of high blood pressure. Abdominal computed tomography and magnetic resonance imaging showed a well-defined, gradually enhancing tumor without focal degeneration or hemorrhage adjacent to the pancreatic body. Tumor excision with distal pancreatectomy and splenectomy was performed, as a malignant tumor of pancreatic origin could not be ruled out. No recurrence has been noted in the 16 months since the operation. Pathologic examination of the tumor revealed a soft-tissue perineurioma of the retroperitoneum. Conclusion Although the definitive diagnosis of soft-tissue perineurioma requires biopsy and immunohistochemical reactivity evaluation, the computed tomography and magnetic resonance imaging findings described in this report suggest inclusion of this rare tumor in the differential diagnosis when such findings occur in the retroperitoneum.

  16. Soft electronics for soft robotics

    Science.gov (United States)

    Kramer, Rebecca K.

    2015-05-01

    As advanced as modern machines are, the building blocks have changed little since the industrial revolution, leading to rigid, bulky, and complex devices. Future machines will include electromechanical systems that are soft and elastically deformable, lending them to applications such as soft robotics, wearable/implantable devices, sensory skins, and energy storage and transport systems. One key step toward the realization of soft systems is the development of stretchable electronics that remain functional even when subject to high strains. Liquid-metal traces embedded in elastic polymers present a unique opportunity to retain the function of rigid metal conductors while leveraging the deformable properties of liquid-elastomer composites. However, in order to achieve the potential benefits of liquid-metal, scalable processing and manufacturing methods must be identified.

  17. Wear and friction behaviour of soft particles filled random direction short GFRP composites

    International Nuclear Information System (INIS)

    Srivastava, V.K.; Wahne, S.

    2007-01-01

    The random direction short E-glass fibre reinforced epoxy resin composites filled with the particles of mica and tricalcium phosphate (TCP) were prepared by hand lay-up method. The wear and friction behaviour of random direction short E-glass fibre reinforced epoxy resin (GFRP) composites sliding against AISI-1045 steel in a pin-on-disc configuration were evaluated on a TR-20LE wear and friction tester. The microhardness, density, tensile strength and compressive strength of the filled and unfilled mica as well as TCP particles were determined. The morphology of the worn surfaces of the unfilled and filled random E-glass fibre composites and the transfer films were analyzed with the scanning electron microscope. It was found that the particles as the fillers contributed significantly to improve the mechanical properties and wear resistance of the E-glass fibre. This was because the particulates as the fillers contributed to enhance the bonding strength between the fibre and the epoxy resin. Moreover, the wear and friction properties of the random E-glass fibre composites were reduced by increasing filler weight of particles

  18. Microstructural and magnetic behavior of nanostructured soft alloys prepared by mechanical grinding and gas atomization

    International Nuclear Information System (INIS)

    Marin, P.; Lopez, M.; Garcia-Escorial, A.; Lieblich, M.

    2007-01-01

    Nanocrystalline powder of Fe-Si-B-Cu-Nb has been obtained by means of mechanical milling of the corresponding nanocrystalline ribbons. Gas atomization technique has been used to minimize the magnetic hardening due to stress effects observed in ball-milled samples. Fe-Si-B-Cu-Nb and Fe-Si nanocrystalline samples have been prepared by gas atomization. The aim of our work is to analyse the particle size dependence of coercivity in this nanostructured alloys and to show the analogies and differences between ball-milled and gas atomized samples

  19. Magnetism and Microwave Absorption Properties of Fe3O4 Microflake-Paraffin Composites Without and With Magnetic Orientation

    Science.gov (United States)

    Wang, Peng; Zhang, Junming; Chen, Yuanwei; Wang, Guowu; Wang, Dian; Wang, Tao; Li, Fashen

    2018-01-01

    We have synthesized thin Fe3O4 microflakes by a simple hydrothermal method and prepared Fe3O4 microflake-paraffin composites without and with magnetic orientation using the method of simple ultrasonic mixing and rotating samples in a magnetic field. X-ray diffractometer, Mössbauer spectrum, scanning electron microscope and vibrating sample magnetometer were used to characterize the samples. The complex permittivity and permeability of Fe3O4 microflake-paraffin composites without and with magnetic orientation were measured in the frequency range of 0.1-18 GHz by a vector network analyzer using a coaxial method. The reflection loss (RL) was calculated by the measured electromagnetic parameters using transmission line theory. The measurement of electromagnetic parameters shows that magnetic orientation makes the complex permittivity and permeability increase. The calculated RL shows that the Fe3O4 microflake-paraffin composite with magnetic orientation has enhanced microwave absorption properties in the frequency range of 1-3 GHz and the thickness range of 2.9-3.5 mm, indicating that the Fe3O4 microflake-paraffin composite with magnetic orientation is a promising thin microwave absorption material in the L-S band.

  20. Dynamic magnetization models for soft ferromagnetic materials with coarse and fine domain structures

    Energy Technology Data Exchange (ETDEWEB)

    Zirka, S.E., E-mail: zirka@email.dp.ua [Department of Physics and Technology, Dnepropetrovsk National University, Gagarin 72, 49050 Dnepropetrovsk (Ukraine); Moroz, Y.I. [Department of Physics and Technology, Dnepropetrovsk National University, Gagarin 72, 49050 Dnepropetrovsk (Ukraine); Steentjes, S.; Hameyer, K. [Institute of Electrical Machines, RWTH Aachen University, Schinkelstr. 4, 52056 Aachen (Germany); Chwastek, K. [Faculty of Electrical Engineering, Czestochowa University of Technology, al. AK 17, 42-201 Czestochowa (Poland); Zurek, S. [Megger Instruments Ltd., Archcliffe Road, Dover, Kent, CT17 9EN (United Kingdom); Harrison, R.G. [Department of Electronics, Carleton University, Ottawa, Canada K1S 5B6 (Canada)

    2015-11-15

    We consider dynamic models, both numerical and analytical, that reproduce the magnetization field H(B) and the energy loss in ferromagnetic sheet materials with different domain structures. Conventional non-oriented (NO) and grain-oriented (GO) electrical steels are chosen as typical representatives of fine-domain and coarse-domain materials. The commonly-accepted loss separation procedures in these materials are critically analyzed. The use of a well-known simplified (“classical”) expression for the eddy-current loss is identified as the primary source of mistaken evaluations of excess loss in NO steel, in which the loss components can only be evaluated using the Maxwell (penetration) equation. The situation is quite different in GO steel, in which the loss separation is uncertain, but the total dynamic loss is several times higher than that explained by any version (numerical or analytical) of the classical approach. To illustrate the uncertainty of the loss separation in GO steel, we show that the magnetization field, and thus the total loss, in this material can be represented with equal accuracy using either the existing three-component approach or our proposed two-component technique, which makes no distinction between classical eddy-current and excess fields and losses. - Highlights: • Critical analysis of a ferromagnetic-material loss-separation principle. • This is to warn materials-science engineers about the inaccuracies resulting from this principle. • A transient model having a single dynamic component is proposed.

  1. Soft and hard natures of Nd{sub 2}Fe{sub 14}B permanent magnet explored by first-order-reversal-curves

    Energy Technology Data Exchange (ETDEWEB)

    Chen, Po-An; Yang, Chao-Yao; Chang, Shu-Jui [Department of Materials Science and Engineering, National Chiao Tung University, Hsinchu, Taiwan, ROC (China); Lee, Min-Han [Undergraduate Honors Program of Nano Science and Engineering, National Chiao Tung University, Hsinchu, Taiwan, ROC (China); Tang, Nai-Kuang; Yen, Sheng-Chan [Metal Industries Research and Development Center, Kaohsiung, Taiwan (China); Tseng, Yuan-Chieh, E-mail: yctseng21@mail.nctu.edu.tw [Department of Materials Science and Engineering, National Chiao Tung University, Hsinchu, Taiwan, ROC (China)

    2014-12-15

    Two commercial Nd{sub 2}Fe{sub 14}B samples, MQP-B and sintered-NdFeB were investigated using synchrotron-based x-ray diffraction and first-order-reversal-curves (FORCs). Despite differing in magnetic and structural properties, the two samples were found to comprise two major ferromagnetic components in FORCs. For the sintered-NdFeB case, the soft component may originate from the intrinsically soft Nd-f site which was coupled with its local Fe atomic environment that differs in magnetic anisotropy from the Nd-g site (intrinsically hard). It may directly originate from the Nd-rich phase or microstructural imperfection, while the former possibility (Nd-f site) appears greater than the latter. While for the MQP-B, the minor second phase resulting from high structural disorder was likely in charge of the presence of the soft component. Sophisticated FORCs analyses revealed the natures of the soft and hard components, soft–hard coupling and switching reversibility of the two cases, irrespective of the origins of their two components. This provides insights to the origin of magnetic stability and reversal dynamics of Nd{sub 2}Fe{sub 14}B that have not been fully understood by conventional magnetic analyses. The coexistence of the two components led to an incoherent reversal undermining the magnetic stability of Nd{sub 2}Fe{sub 14}B. This is a fundamental problem as to why the performance extremity can only be improved finitely through extrinsic tuning. From FORCs simulation we understand that the soft–hard coupling was moderate in a real Nd{sub 2}Fe{sub 14}B compound. A stronger soft–hard coupling is necessary to conquer the anisotropic competition to enable a coherent reversal that will promote the magnetic hardness. - Highlights: • We investigated two commercially available Nd{sub 2}Fe{sub 14}B compounds with FORCs. • The two compounds were found to comprise soft and hard natures. • The coupling between the soft and hard phases is moderate in a real Nd

  2. Magnetic responsive hydroxyapatite composite scaffolds construction for bone defect reparation.

    Science.gov (United States)

    Zeng, Xiao Bo; Hu, Hao; Xie, Li Qin; Lan, Fang; Jiang, Wen; Wu, Yao; Gu, Zhong Wei

    2012-01-01

    In recent years, interest in magnetic biomimetic scaffolds for tissue engineering has increased considerably. A type of magnetic scaffold composed of magnetic nanoparticles (MNPs) and hydroxyapatite (HA) for bone repair has been developed by our research group. In this study, to investigate the influence of the MNP content (in the scaffolds) on the cell behaviors and the interactions between the magnetic scaffold and the exterior magnetic field, a series of MNP-HA magnetic scaffolds with different MNP contents (from 0.2% to 2%) were fabricated by immersing HA scaffold into MNP colloid. ROS 17/2.8 and MC3T3-E1 cells were cultured on the scaffolds in vitro, with and without an exterior magnetic field, respectively. The cell adhesion, proliferation and differentiation were evaluated via scanning electron microscopy; confocal laser scanning microscopy; and 3-(4,5-Dimethylthiazol-2-yl)-2,5-diphenyltetrazolium bromide (MTT), alkaline phosphatase, and bone gla protein activity tests. The results demonstrated the positive influence of the magnetic scaffolds on cell adhesion, proliferation, and differentiation. Further, a higher amount of MNPs on the magnetic scaffolds led to more significant stimulation. The magnetic scaffold can respond to the exterior magnetic field and engender some synergistic effect to intensify the stimulating effect of a magnetic field to the proliferation and differentiation of cells.

  3. Microwave assisted synthesis of Magnetically responsive composite materials

    Czech Academy of Sciences Publication Activity Database

    Šafařík, Ivo; Horská, Kateřina; Pospíšková, K.; Maděrová, Zdeňka; Šafaříková, Miroslava

    2013-01-01

    Roč. 49, č. 1 (2013), s. 213-218 ISSN 0018-9464 R&D Projects: GA ČR(CZ) GAP503/11/2263; GA MŠk LH12190 Institutional support: RVO:67179843 Keywords : magnetic materials * magnetic modification * magnetic separation * microwaves Subject RIV: EH - Ecology, Behaviour Impact factor: 1.213, year: 2013

  4. Probing buried solid-solid interfaces in magnetic multilayer structures and other nanostructures using spectroscopy excited by soft x-ray standing waves

    International Nuclear Information System (INIS)

    Yang, S.-H.; Mun, B.S.; Mannella, N.; Sell, B.; Ritchey, S.B.; Fadley, C.S.; Pham, L.; Nambu, A.; Watanabe, M.

    2004-01-01

    Full text: Buried solid-solid interfaces are becoming increasingly more important in all aspects of nanoscience, and we here dis- cuss the st applications of a new method for selectively studying them with the vuv/soft x-ray spectroscopies. As specific examples, magnetic multilayer structures represent key elements of current developments in spintronics, including giant magnetoresistance, exchange bias, and magnetic tunnel resistance. The buried interfaces in such structures are of key importance to their performance, but have up to now been difficult to study selectively with these spectroscopies. This novel method involves excitation of photoelectrons or fluorescent x-rays with soft x-ray standing waves created by Bragg reflection from a multilayer mirror substrate on which the sample is grown. We will discuss core and valence photoemission, as well soft x-ray emission, results from applying this method to multilayer structures relevant to both giant magnetoresistance (Fe/Cr-[2]) and magnetic tunnel junctions (Al 2 O 3 /FeCo) , including magnetic dichroism measurements. Work supported by the Director, Of e of Science, Of e of Basic Energy Sciences, Materials Science and Engineering Division, U.S. Department of Energy, Contract No. DE-AC03-76SF000

  5. The importance of benchmarking habitat structure and composition for understanding the extent of fishing impacts in soft sediment ecosystems

    Science.gov (United States)

    Handley, Sean J.; Willis, Trevor J.; Cole, Russell G.; Bradley, Anna; Cairney, Daniel J.; Brown, Stephen N.; Carter, Megan E.

    2014-02-01

    Trawling and dredge fisheries remove vulnerable fauna, homogenise sediments and assemblages, and break down biogenic habitats, but the full extent of these effects can be difficult to quantify in the absence of adequate control sites. Our study utilised rare control sites containing biogenic habitat, the Separation Point exclusion zone, formally protected for 28 years, as the basis for assessing the degree of change experienced by adjacent areas subject to benthic fishing. Sidescan sonar surveys verified that intensive trawling and dredging occurred in areas adjacent to, but not inside, the exclusion area. We compared sediment composition, biogenic cover, macrofaunal assemblages, biomass, and productivity of the benthos, inside and outside the exclusion zone. Disturbed sites were dominated by fine mud, with little or no shell-gravel, reduced number of species, and loss of large bodied animals, with concomitant reductions in biomass and productivity. At protected sites, large, rarer molluscs were more abundant and contributed the most to size-based estimates of productivity and biomass. Functional changes in fished assemblages were consistent with previously reported relative increases in scavengers, predators and deposit feeders at the expense of filter feeders and a grazer. We propose that the colonisation of biogenic species in protected sites was contingent on the presence of shell-gravel atop these soft sediments. The process of sediment homogenisation by bottom fishing and elimination of shell-gravels from surficial sediments appeared to have occurred over decades - a ‘shifting baseline’. Therefore, benchmarking historical sediment structure at control site like the Separation Point exclusion zone is necessary to determine the full extent of physical habitat change wrought by contact gears on sheltered soft sediment habitats to better underpin appropriate conservation, restoration or fisheries management goals.

  6. Magnetic responsive hydroxyapatite composite scaffolds construction for bone defect reparation

    Directory of Open Access Journals (Sweden)

    Zeng XB

    2012-07-01

    Full Text Available Xiao Bo Zeng, Hao Hu, Li Qin Xie, Fang Lan, Wen Jiang, Yao Wu, Zhong Wei GuNational Engineering Research Center for Biomaterials, Sichuan University, Chengdu, Sichuan, People's Republic of ChinaIntroduction: In recent years, interest in magnetic biomimetic scaffolds for tissue engineering has increased considerably. A type of magnetic scaffold composed of magnetic nanoparticles (MNPs and hydroxyapatite (HA for bone repair has been developed by our research group.Aim and methods: In this study, to investigate the influence of the MNP content (in the scaffolds on the cell behaviors and the interactions between the magnetic scaffold and the exterior magnetic field, a series of MNP-HA magnetic scaffolds with different MNP contents (from 0.2% to 2% were fabricated by immersing HA scaffold into MNP colloid. ROS 17/2.8 and MC3T3-E1 cells were cultured on the scaffolds in vitro, with and without an exterior magnetic field, respectively. The cell adhesion, proliferation and differentiation were evaluated via scanning electron microscopy; confocal laser scanning microscopy; and 3-(4,5-Dimethylthiazol-2-yl-2,5-diphenyltetrazolium bromide (MTT, alkaline phosphatase, and bone gla protein activity tests.Results: The results demonstrated the positive influence of the magnetic scaffolds on cell adhesion, proliferation, and differentiation. Further, a higher amount of MNPs on the magnetic scaffolds led to more significant stimulation.Conclusion: The magnetic scaffold can respond to the exterior magnetic field and engender some synergistic effect to intensify the stimulating effect of a magnetic field to the proliferation and differentiation of cells.Keywords: magnetic therapy, magnetic nanoparticles, bone repair, magnetic responsive

  7. Influence of soft ferromagnetic sections on the magnetic flux density profile of a large grain, bulk Y–Ba–Cu–O superconductor

    International Nuclear Information System (INIS)

    Philippe, M P; Wéra, L; Fagnard, J-F; Vanderheyden, B; Vanderbemden, P; Ainslie, M D; Dennis, A R; Shi, Y-H; Cardwell, D A

    2015-01-01

    Bulk, high temperature superconductors have significant potential for use as powerful permanent magnets in a variety of practical applications due to their ability to trap record magnetic fields. In this paper, soft ferromagnetic sections are combined with a bulk, large grain Y–Ba–Cu–O high temperature superconductor to form superconductor/ferromagnet hybrid structures. We study how the ferromagnetic sections influence the shape of the profile of the trapped magnetic induction at the surface of each structure and report the surface magnetic flux density measured by Hall probe mapping. These configurations have been modelled using a 2D axisymmetric finite element method based on the H-formulation and the results show excellent qualitative and quantitative agreement with the experimental measurements. The model has also been used to study the magnetic flux distribution and predict the behaviour for other constitutive laws and geometries. The results show that the ferromagnetic material acts as a magnetic shield, but the flux density and its gradient are enhanced on the face opposite to the ferromagnet. The thickness and saturation magnetization of the ferromagnetic material are important and a characteristic ferromagnet thickness d* is derived: below d*, saturation of the ferromagnet occurs, and above d*, a weak thickness-dependence is observed. The influence of the ferromagnet is observed even if its saturation magnetization is lower than the trapped flux density of the superconductor. Conversely, thin ferromagnetic discs can be driven to full saturation even though the outer magnetic field is much smaller than their saturation magnetization. (paper)

  8. Microstructure, soft magnetic properties and applications of amorphous Fe-Co-Si-B-Mo-P alloy

    Science.gov (United States)

    Hasiak, Mariusz; Miglierini, Marcel; Łukiewski, Mirosław; Łaszcz, Amadeusz; Bujdoš, Marek

    2018-05-01

    DC thermomagnetic properties of Fe51Co12Si16B8Mo5P8 amorphous alloy in the as-quenched and after annealing below crystallization temperature are investigated. They are related to deviations in the microstructure as revealed by Mössbauer spectrometry. Study of AC magnetic properties, i.e. hysteresis loops, relative permeability and core losses versus maximum induction was aimed at obtaining optimal initial parameters for simulation process of a resonant transformer for a rail power supply converter. The results obtained from numerical analyses including core losses, winding losses, core mass, and dimensions were compared with the same parameters calculated for Fe-Si alloy and ferrite. Moreover, Steinmetz coefficients were also calculated for the as-quenched Fe51Co12Si16B8Mo5P8 amorphous alloy.

  9. Microstructure, soft magnetic properties and applications of amorphous Fe-Co-Si-B-Mo-P alloy

    Directory of Open Access Journals (Sweden)

    Mariusz Hasiak

    2018-05-01

    Full Text Available DC thermomagnetic properties of Fe51Co12Si16B8Mo5P8 amorphous alloy in the as-quenched and after annealing below crystallization temperature are investigated. They are related to deviations in the microstructure as revealed by Mössbauer spectrometry. Study of AC magnetic properties, i.e. hysteresis loops, relative permeability and core losses versus maximum induction was aimed at obtaining optimal initial parameters for simulation process of a resonant transformer for a rail power supply converter. The results obtained from numerical analyses including core losses, winding losses, core mass, and dimensions were compared with the same parameters calculated for Fe-Si alloy and ferrite. Moreover, Steinmetz coefficients were also calculated for the as-quenched Fe51Co12Si16B8Mo5P8 amorphous alloy.

  10. Effects of accelerated aging upon the lipid composition of seeds from two soft wheat varieties from Morocco

    Energy Technology Data Exchange (ETDEWEB)

    Ouzouline, M.; Tahani, N.; Demandre, C.; El Amrani, A.; Benhassaine-Kesri, G.; Serghini Caid, H.

    2009-07-01

    The lipid composition of the seeds from two soft wheat varieties (Triticum aestivum, cv. Marchouche and Mahdia) were analyzed before and after accelerated aging. Eight days of accelerated aging resulted in a total inhibition of seed germ inability as well as a decrease in their total and especially unsaturated fatty acid contents. Oleic and linoleic acid contents decreased particularly in the phosphatidylcholine of the seeds from both varieties. The proportion of polar lipids also decreased after aging as compared to neutral lipids: a 5.8% and 7.2% decrease in polar lipids was e observed in Mahdia and Marchouche cultivars, respectively. In the neutral lipids of the seeds from the Marchouche variety, the percentage of free fatty acids increased whereas the triacylglycerols decreased. After aging, the fatty acid compositions of all lipid classes were modified in the same manner as total fatty acid compositions. Among polar lipids, phospholipid proportions were particularly small, especially the phosphatidylcholine percentages with an 18.1% and 19.1% decrease in Mahdia and Marchouche varieties, respectively. In contrast, MGDG percentages increased, especially in the seeds from the Marchouche variety. A 15.5% increase was noticed when compared with seeds which were not aged. At the same time, the DGDG percentage showed a 16.6% decrease after accelerated aging of the seeds from the Marchouche variety. From these results we concluded that the lipid content decrease observed in seeds after accelerated aging could be linked to a loss in the germination and vigor of wheat seeds. (Author) 38 refs.

  11. Soft sensor based composition estimation and controller design for an ideal reactive distillation column.

    Science.gov (United States)

    Vijaya Raghavan, S R; Radhakrishnan, T K; Srinivasan, K

    2011-01-01

    In this research work, the authors have presented the design and implementation of a recurrent neural network (RNN) based inferential state estimation scheme for an ideal reactive distillation column. Decentralized PI controllers are designed and implemented. The reactive distillation process is controlled by controlling the composition which has been estimated from the available temperature measurements using a type of RNN called Time Delayed Neural Network (TDNN). The performance of the RNN based state estimation scheme under both open loop and closed loop have been compared with a standard Extended Kalman filter (EKF) and a Feed forward Neural Network (FNN). The online training/correction has been done for both RNN and FNN schemes for every ten minutes whenever new un-trained measurements are available from a conventional composition analyzer. The performance of RNN shows better state estimation capability as compared to other state estimation schemes in terms of qualitative and quantitative performance indices. Copyright © 2010 ISA. Published by Elsevier Ltd. All rights reserved.

  12. Effect of composition polymeric PVB binder on physical, magnetic properties and microstructure of bonded magnet NdFeB

    Science.gov (United States)

    Sardjono, P.; Muljadi; Suprapedi; Sinuaji, P.; Ramlan; Gulo, F.

    2017-04-01

    The bonded magnet NdFeB has been made by using the hot press method and using Poly Vinyl Butiral (PVB) as a binder. The composition of polymeric binder was varied: 0, 2, 4, 6 and 7 % of weight. Both raw materials are weighed and mixed according to the composition of PVB, then formed by hot press with a pressure 30 MPa, a temperature of 160 ° C and holding time for 30 minutes. The bulk density was measured by using Archimedes method. SEM observation was done to determine the microstructure of bonded magnet NdFeB. The flux magnetic value was measured by using a Gauss meter and the measurement of hysteresis curves was done to know value of remanence Br, coercivity Hc and energy product BHmax by using VSM. According to the characterization results show that the best composition of PVB is 2 of weight. The properties of bonded magnet NdFeB of those compositions are the bulk density around 5.66 g/cm3. Flux Magnetic value: 1862 Gauss, Br value: 5000 kGauss, Hc value: 8.49 kOe and BHmax value : 5.10 MGOe. According of SEM observation results show that the polymer matrix of PVB appears to have covered on all surface grain and filled grain boundary.

  13. Preparation and magnetic properties of polymer magnetic composites based on acrylate resin filled with nickel plating graphite nanosheets

    Energy Technology Data Exchange (ETDEWEB)

    Zhang Yi, E-mail: zhangyi520love@yahoo.com.cn [Department of Applied Chemistry, School of Science, Northwestern Polytechnical University, Xi' an 710072 (China); Qi Shuhua; Zhang Fan; Yang Yongqing; Duan Guochen [Department of Applied Chemistry, School of Science, Northwestern Polytechnical University, Xi' an 710072 (China)

    2011-11-01

    Nickel plating graphite nanosheets (Ni/GNs) were prepared by electroless plating method using graphite nanosheets (GNs). Then a novel polymer magnetic composites based on acrylate pressure-sensitive adhesive (acrylate PSA) filled with Ni/GNs were fabricated by solution blend method. The Ni/GNs and acrylate PSA/Ni/GNs composites were characterized by scanning electron microscope (SEM)/energy dispersive spectroscopy (EDS), X-ray diffraction (XRD), vibrating sample magnetometer (VSM) and transmission electron microscope (TEM). All results showed that relatively uniform and compact Ni layer is successfully coated onto GNs under the given conditions, furthermore, Ni/GNs are homogeneously dispersed in acrylate PSA. The VSM results showed that the saturation magnetization of acrylate PSA/Ni/GNs composites increases with an increasing content of Ni/GNs while the coercivity decreases with an increasing content of Ni/GNs. When the content of GNs is 20 wt%, acrylate PSA/Ni/GNs composites exhibites good mechanical properties.

  14. Preparation and magnetic properties of polymer magnetic composites based on acrylate resin filled with nickel plating graphite nanosheets

    International Nuclear Information System (INIS)

    Zhang Yi; Qi Shuhua; Zhang Fan; Yang Yongqing; Duan Guochen

    2011-01-01

    Nickel plating graphite nanosheets (Ni/GNs) were prepared by electroless plating method using graphite nanosheets (GNs). Then a novel polymer magnetic composites based on acrylate pressure-sensitive adhesive (acrylate PSA) filled with Ni/GNs were fabricated by solution blend method. The Ni/GNs and acrylate PSA/Ni/GNs composites were characterized by scanning electron microscope (SEM)/energy dispersive spectroscopy (EDS), X-ray diffraction (XRD), vibrating sample magnetometer (VSM) and transmission electron microscope (TEM). All results showed that relatively uniform and compact Ni layer is successfully coated onto GNs under the given conditions, furthermore, Ni/GNs are homogeneously dispersed in acrylate PSA. The VSM results showed that the saturation magnetization of acrylate PSA/Ni/GNs composites increases with an increasing content of Ni/GNs while the coercivity decreases with an increasing content of Ni/GNs. When the content of GNs is 20 wt%, acrylate PSA/Ni/GNs composites exhibites good mechanical properties.

  15. The design and validation of a magnetic resonance imaging-compatible device for obtaining mechanical properties of plantar soft tissue via gated acquisition.

    Science.gov (United States)

    Williams, Evan D; Stebbins, Michael J; Cavanagh, Peter R; Haynor, David R; Chu, Baocheng; Fassbind, Michael J; Isvilanonda, Vara; Ledoux, William R

    2015-10-01

    Changes in the mechanical properties of the plantar soft tissue in people with diabetes may contribute to the formation of plantar ulcers. Such ulcers have been shown to be in the causal pathway for lower extremity amputation. The hydraulic plantar soft tissue reducer (HyPSTER) was designed to measure in vivo, rate-dependent plantar soft tissue compressive force and three-dimensional deformations to help understand, predict, and prevent ulcer formation. These patient-specific values can then be used in an inverse finite element analysis to determine tissue moduli, and subsequently used in a foot model to show regions of high stress under a wide variety of loading conditions. The HyPSTER uses an actuator to drive a magnetic resonance imaging-compatible hydraulic loading platform. Pressure and actuator position were synchronized with gated magnetic resonance imaging acquisition. Achievable loading rates were slower than those found in normal walking because of a water-hammer effect (pressure wave ringing) in the hydraulic system when the actuator direction was changed rapidly. The subsequent verification tests were, therefore, performed at 0.2 Hz. The unloaded displacement accuracy of the system was within 0.31%. Compliance, presumably in the system's plastic components, caused a displacement loss of 5.7 mm during a 20-mm actuator test at 1354 N. This was accounted for with a target to actual calibration curve. The positional accuracy of the HyPSTER during loaded displacement verification tests from 3 to 9 mm against a silicone backstop was 95.9% with a precision of 98.7%. The HyPSTER generated minimal artifact in the magnetic resonance imaging scanner. Careful analysis of the synchronization of the HyPSTER and the magnetic resonance imaging scanner was performed. With some limitations, the HyPSTER provided key functionality in measuring dynamic, patient-specific plantar soft tissue mechanical properties. © IMechE 2015.

  16. Complex permeability and core loss of soft magnetic Fe-based nanocrystalline powder cores

    Energy Technology Data Exchange (ETDEWEB)

    Füzerová, Jana, E-mail: jana.fuzerova@tuke.sk [Faculty of Mechanical Engineering, Technical University, Letná 1, 042 00 Košice (Slovakia); Füzer, Ján; Kollár, Peter [Institute of Physics, P.J. Šafárik University, Park Angelinum 9, 040 23 Košice (Slovakia); Bureš, Radovan; Fáberová, Mária [Institute of Materials Research, Slovak Academy of Sciences, Watsonova 47, 043 53 Košice (Slovakia)

    2013-11-15

    Rapidly quenched ribbons of Fe{sub 73}Cu{sub 1}Nb{sub 3}Si{sub 16}B{sub 7} were ball milled and cryomilled to get powder and warm consolidated to get bulk compacts. The data presented here are relative to different experimental procedures, one corresponding to milling at room temperature (sample R1) and the other corresponding to cryomilling at temperature of liquid nitrogen (sample L1). It was found that the properties of the initial powder influenced the density, the electrical resistivity and electromagnetic properties of the resulting bulk alloys. Permeability and core loss are structure sensitive and depend on factors such as powder size and shape, porosity, purity, and internal stress. Permeability spectra of sample R1 decreases with increasing the frequency and its values are larger than that for sample L1 at low frequencies. On the other hand the permeability of sample L1 remains steady up to 1 kHz and at certain frequency is larger than that for sample R1. Also there are different frequency dependences of the imaginary parts of permeability and loss factor, respectively. The cryomilling of the amorphous ribbon positively influences on the AC magnetic properties at higher frequencies (above 100 Hz) of resulting bulk sample. - Highlights: • We prepared two different amorphous powder vitroperm samples. • We have examined changes in the properties of the bulk samples prepared by compaction. • It was found that properties of the initial powder influence the density, the electrical resistivity and electromagnetic properties of the resulting bulk alloys.

  17. Anisotropic magnetoelectric characteristics in five-layer magnetization-graded multiferroic composites

    Directory of Open Access Journals (Sweden)

    Lei Chen

    2017-05-01

    Full Text Available We investigate the anisotropic magnetoelectric(ME characteristics for the five-layer magnetization-graded multiferroic composites(MGMC. The magnetic anisotropy and corresponding anisotropic magnetomechanical effect, demagnetization effect and magneto-mechanical damping’s dependence on magnetic field direction result in an obvious anisotropic ME coupling effect. The experimental results show that ME voltage coefficient in H33 mode is remarkably larger than the other ones (H11, H31 and H13 over the whole Hdc range. Correspondingly, ∂VME/∂Hdc arrives about 420mV/Oe at an optimum bias magnetic field of 46Oe, which is approximately 40 times larger than that of the previous reported composite. Furthermore, it also demonstrates an obvious angular dependence on dc magnetic field. Taking advantage of these specifications, the MGMC can be used to detect weak dc magnetic field and its spatial orientation.

  18. Interface influence on the properties of Co{sub 90}Fe{sub 10} films on soft magnetic underlayers – Magnetostrictive and Mössbauer spectrometry studies

    Energy Technology Data Exchange (ETDEWEB)

    Szumiata, Tadeusz, E-mail: t.szumiata@uthrad.pl [Department of Physics, Faculty of Mechanical Engineering, University of Technology and Humanities in Radom, 54 Krasickiego Street, 26-600 Radom (Poland); Gzik-Szumiata, Małgorzata; Brzózka, Katarzyna; Górka, Bogumił; Gawroński, Michał [Department of Physics, Faculty of Mechanical Engineering, University of Technology and Humanities in Radom, 54 Krasickiego Street, 26-600 Radom (Poland); Caruana Finkel, Anastasia; Reeves-McLaren, Nik; Morley, Nicola A. [Department of Materials Science and Engineering, University of Sheffield, Mappin Street, Sheffield S1 3JD (United Kingdom)

    2016-03-01

    The main aim of the work was to show the correlation between magnetostrictive properties and microstructure of 25 nm thick Co{sub 90}Fe{sub 10} films deposited on soft magnetic underlayers. A special attention was paid to the role of the interface region. In the case of Co{sub 90}Fe{sub 10} on 25 nm and 35 nm thick METGLAS underlayers one can resolve in conversion electron Mössbauer spectra two hyperfine field distributions (high-field and medium-field ones) corresponding to both constituents of bilayers. Analogical distributions describe the spectra of Co{sub 90}Fe{sub 10} on 25 nm and 35 nm thick Ni{sub 81}Fe{sub 19} underlayers, however an additional low-field, smeared component has been observed. It has been attributed to the interface layer (of partially disordered structure) between magnetostrictive layer and soft magnetic layer. Such interpretation is backed up by the obtained strong correlation between mean hyperfine field value and magnetostriction constant of the films. The investigated bilayers are good candidates for MRAM devices. - Highlights: • We investigate Co–Fe thin films on the soft magnetic underlayers. • We measured magnetostriction and collected conversion electron Mössbauer spectra. • In the case of Permalloy underlayer a rapid drop of magnetostriction was observed. • Strong correlation between magnetostriction and hyperfine fields was shown. • Our results point to the essential role of the Co–Fe/underlayer interface.

  19. Addition of magnetic markers for non-destructive evaluation of polymer composites

    Directory of Open Access Journals (Sweden)

    Ana Paula Pereira Fulco

    2011-12-01

    Full Text Available Polymer composite pipes are an appealing option as a substitute for conventional steel pipes, particularly due to their inherent corrosion resistance. However, the composite pipes currently used do not allow non-destructive evaluation (NDE using instrumented devices which operate with magnetic sensors. The present work aims at the development of polymer composites with the addition magnetic markers to allow the application non-destructive evaluation techniques which use magnetic sensors. Glass-polyester composite flat, circular plates were fabricated with the addition of ferrite particles (barium ferrite and strontium ferrite and four types of notches were introduced on the plates' surfaces. The influence of these notches on the measured magnetic properties of each material was measured. X-ray diffraction (XRD, X-ray fluorescence (XRF and Brunauer, Emmett, and Teller (BET nitrogen adsorption were used for the characterization of the ferrite particles. Particle dispersion in the polymer matrix was analyzed by scanning electron microscopy (SEM. According to the results, a particular variation in magnetic field was detected over the region surrounding each type of notch. The results suggest that the proposed technique has great potential for damage detection in polymer composites using magnetic sensors and thus constitute a valuable contribution which may ultimately lead to the development of non-destructive evaluation techniques for assessing the structural integrity polymer composite pipes.

  20. Composite bonded magnets with controlled anisotropy directions prepared by viscous deformation technique

    International Nuclear Information System (INIS)

    Yamashita, Fumitoshi; Kawamura, Kiyomi; Okada, Yukihiro; Murakami, Hiroshi; Ogushi, Masaki; Nakano, Masaki; Fukunaga, Hirotoshi

    2007-01-01

    When a radially anisotropic rare earth bonded magnet for a rotor with a high (BH) max value is magnetized multi-polarly, its flux distributes rectangularly and increases a cogging torque. In order to overcome this difficulty, we newly developed highly dense Sm 2 Fe 17 N 3 and Nd 2 Fe 14 B-based composite bonded magnets with continuously controlled anisotropy directions by using a viscous deformation technique

  1. Thermal analysis and microstructure of hexaperrite based magnet composite with natural rubber matrix

    International Nuclear Information System (INIS)

    Sudirman; Ridwan; Jamilah; Trijono, Waluyo

    2000-01-01

    Thermal and microstructure analyse of hexa ferrite based on composite magnets with natural rubber matrix have been done to investigate their performance. Such magnets play an important role in the toy and house-hold industries because of their suitable magnetic properties, low cost, lightness and flexibility. The composite magnets were synthesized by blending the ferrite powder and natural rubber at composition 30%-70% rubber volume. The microstructure and thermal behaviour of the composite were examined by using SEM and OTA/TGA. The result show that the natural rubber swelling is optimally at 181,17 o C, which is the recommended top condition for blending. The performance magnet composite is limited by the change of natural rubber properties which decompose at temperature around 400 o C. In the decomposition process, the natural rubber molecule trapped in a composite system based on BaM is more difficult are more compared to the composite system based on SrM because the BaM system particle microstructure and its distribution more homogeneous

  2. Sequential chimeric medial femoral condyle and anterolateral thigh flow-through flaps for one-stage reconstructions of composite bone and soft tissue defects: Report of three cases.

    Science.gov (United States)

    Henn, Dominic; Abouarab, Mohamed H; Hirche, Christoph; Hernekamp, Jochen F; Schmidt, Volker J; Kneser, Ulrich; Kremer, Thomas

    2017-10-01

    Small recalcitrant non-unions with poor perfusion require reconstruction with vascularized bone flaps. Cases with concomitant large soft tissue defects are especially challenging, since vascularized soft tissue transfer is often indicated and distant microvascular anastomoses may be required. We introduce a sequential chimeric free flap composed of a medial femoral condyle corticoperiosteal flap anastomosed to an anterolateral thigh flow-through flap (MFC-ALT flap) and report its use for reconstruction of small non-unions with concomitant large soft tissue defects in three exemplary patients. Two female and one male patients ages 39-58 years suffered from composite bone and soft tissue defects of the lower extremity and clavicle caused by tumor resection and postoperative radiation resp. infected tibial pilon fracture. The sizes of the soft tissue defects ranged from 15-23 × 4.5-6 cm and the sizes of the bone defects ranged from 1.5-4 × 2-4 cm. Defect reconstructions were performed in all cases with sequential chimeric MFC-ALT flaps with sizes ranging from 2-4 × 1.6-4 cm for the MFC and 21-23 × 7-8 cm for the ALT skin paddles. Functional reconstructions were achieved in all cases resulting in stable unions and soft tissue coverage enabling the patients to bear full weight without assistance on 5-months follow-up. Postoperative course was uneventful and complications were restricted to a small skin necrosis at the suture line in one case. MFC-ALT flaps may be a safe, and effective procedure for one-stage reconstructions of small, irregularly shaped bone defects with concomitant large soft tissue loss or surrounding instable scarring, particularly in cases of recalcitrant non-unions after radiation exposure. © 2017 Wiley Periodicals, Inc.

  3. Nickel-zinc ferrite/permalloy (Ni0.5Zn0.5Fe2O4/Ni-Fe soft magnetic nanocomposites fabricated by electro-infiltration

    Directory of Open Access Journals (Sweden)

    Xiao Wen

    2016-05-01

    Full Text Available Magnetically soft NiZn ferrite (Ni0.5Zn0.5Fe2O4 nanoparticles are embedded within a permalloy (Ni-Fe matrix via an electro-infiltration process as thin films intended for use as on-chip inductor cores in the MHz frequency regime. A layer of NiZn ferrite nanoparticles is first deposited, and then permalloy is electroplated through the voids to encapsulate the particles and form three-dimensional ferrite/alloy nanocomposites. The composites are estimated to contain 37% ferrite by volume and exhibit a relative permeability of ∼320, a saturation of ∼1.15 T, and an operational bandwidth of 93 MHz. Compared to a permalloy thin film of similar thickness, the nanocomposite exhibits 39% higher electrical resistivity and 50% higher bandwidth.

  4. Effect of P addition on glass forming ability and soft magnetic properties of melt-spun FeSiBCuC alloy ribbons

    International Nuclear Information System (INIS)

    Xu, J.; Yang, Y.Z.; Li, W.; Chen, X.C.; Xie, Z.W.

    2016-01-01

    The dependency of phosphorous content on the glass forming ability, thermal stability and soft magnetic properties of Fe 83.4 Si 2 B 14−x P x Cu 0.5 C 0.1 (x=0,1,2,3,4) alloys was investigated. The experimental results showed that the substitution of B by P increased the glass forming ability in this alloy system. The Fe 83.4 Si 2 B 10 P 4 Cu 0.5 C 0.1 alloy shows a fully amorphous character. Thermal stability of melt-spun ribbons increases and temperature interval between the first and second crystallization peaks enlarges with the increase of P content. And the saturation magnetic flux density (Bs) shows a slight increase with the increase of P content. The Fe 83.4 Si 2 B 11 P 3 Cu 0.5 C 0.1 nanocrystalline alloy exhibits a high Bs about 200.6 emu/g. The Bs of fully amorphous alloy Fe 83.4 Si 2 B 10 P 4 Cu 0.5 C 0.1 drops dramatically to 172.1 emu/g, which is lower than that of other nanocrystallines. Low material cost and excellent soft magnetic properties make the FeSiBPCuC alloys promise soft magnetic materials for industrial applications. - Highlights: • Partial substituting B by P helps to improve the glass forming ability of the alloy. • The addition of P content reduces the thermal stability and improves heat treatment temperature region for these alloys. • The Fe 83.4 Si 2 B 11 P 3 Cu 0.5 C 0.1 nanocrystalline alloy exhibits a high saturation magnetic density of 200.6 emu/g.

  5. Compositional trends and magnetic excitations in binary and ternary Fe–Pd–X magnetic shape memory alloys

    International Nuclear Information System (INIS)

    Gruner, Markus Ernst; Hamann, Sven; Brunken, Hayo; Ludwig, Alfred; Entel, Peter

    2013-01-01

    Highlights: ► We discuss compositional trends in Fe–Pd–Cu and Fe–Pd–Mn magnetic shape memory alloys. ► We combine density functional theory and combinatorial thin film experiments. ► Magnetic excitations contribute decisively to the structural transformation behavior. -- Abstract: High throughput thin film experiments and first-principles calculations are combined in order to get insight into the relation between finite temperature transformation behavior and structural ground state properties of ternary Fe–Pd–X alloys. In particular, we consider the binding surface, i.e., the energy of the disordered alloy calculated along the Bain path between bcc and fcc which we model by a 108 atom supercell. We compare stoichiometric Fe 75 Pd 25 with ternary systems, where 4.6% of the Fe atoms were substituted by Cu and Mn, respectively. The computational trends are related to combinatorial experiments on thin film libraries for the systems Fe–Pd–Mn and Fe–Pd–Cu which reveal a systematic evolution of the martensitic start temperature with composition within the relevant concentration range for magnetic shape memory (MSM) applications. Our calculations include atomic relaxations, which were shown to be relevant for a correct description of the structural properties. Furthermore, we find that magnetic excitations can substantially alter the binding surface. The comparison of experimental and theoretical trends indicates that, both, compositional changes and magnetic excitations contribute significantly to the structural stability which may thus be tailored by specifically adding antiferromagnetic components

  6. Compositional disorder, magnetism, and their interplay in metallic alloys

    International Nuclear Information System (INIS)

    Johnson, D.D.; Staunton, J.B.; Pinski, F.J.; Gyorffy, B.L.; Stocks, G.M.

    1992-01-01

    Chemical disorder leads to a variety of intriguing phenomena in alloys which have yet to be fully understood, particularly those phenomena occurring when chemical and magnetic effects interplay with one another. For example, magnetic order gives rise to chemical ordering in alloys, as in Ni-rich NiFe alloys. Two examples of the interplay of chemical disorder and magnetism will be discussed. Our recently developed ab-initio Landau (mean-field) theory for calculating the chemical-chemical, magneto-chemical, and magnetic-magnetic correlation functions in substitutional random alloys is used to describe electronic/magnetic mechanisms (e.g. in FeV) which give rise to the chemical short-range order as determined by neutron, X-ray, or electron diffuse scattering intensities. New developments within this approach that account for charge rearrangement effect will be mentioned. These calculations are performed within the multiple-scattering framework, developed by Korringa, Kohn, and Rostoker (KKR), combined with the coherent potential approximation (CPA) to describe the disorder. This approach allows a first-principles description of the electronic structure of the high-temperature, chemically disordered state and its instability to ordering a low temperatures. This paper reports that this method provides not only a direct comparison of diffuse scattering data with theory but a means to understand more fully the underlying mechanisms which drive chemical and/or magnetic ordering

  7. Magnetization of in situ multifilamentary superconducting Nb3Sn-Cu composites

    International Nuclear Information System (INIS)

    Shen, S.S.; Verhoeven, J.D.

    1980-01-01

    Magnetic properties are reported for in situ superconducting Nb 3 Sn composites that have exhibited attractive electrical properties and superior mechanical characteristics. Magnetization measurements were conducted up to 4 T at 4.2 K on a variety of samples of different sizes and twist pitches, and the results are presented in absolute M-H curves and losses per cycle. It is observed that the magnetization of such composites is generally proportional to the size of the wire (approx. 0.25 to 0.51 mm) rather than the fiber size (approx. 10 -7 m), which indicates a strong coupling effect among Nb 3 Sn fibers

  8. Magnetic and Electric Properties of Magneto polymer Composites

    Directory of Open Access Journals (Sweden)

    Jozef Slama

    2004-01-01

    Full Text Available Permeability spectra of MnZn ferrite composite materials, prepared by mixing ferrite particles with PVC, have been studied. As the ferrite filler content decreases in composite, the quasistatic permeability of the rotation component decreases and relaxation and the resonance frequency shift is higher. The real part of the permeability in the ferrite composite materials becomes larger than of sintered ferrite in high frequency region.

  9. A novel approach to fabrication of superparamagnetite hollow silica/magnetic composite spheres

    Energy Technology Data Exchange (ETDEWEB)

    Yuan Junjie, E-mail: yuanjunjie@tongji.edu.c [School of Materials Science and Engineering, Tongji University, Shanghai 200092 (China); Key Laboratory of Molecular Engineering of Polymers, Fudan University, Shanghai 200433 (China); Zhang Xiong; Qian He [School of Materials Science and Engineering, Tongji University, Shanghai 200092 (China)

    2010-08-15

    We described a method for synthesizing hollow silica/magnetic composite spheres using sulfonic acid functionalized hollow silica spheres (SAFHSS) as templates. The Fe{sub 3}O{sub 4} nanoparticles were deposited on or imbedded in the hollow silica shell by a precipitation reaction. The morphologies, composition and properties of the hollow composite spheres were characterized by transmission electron microscopy, Fourier transform infrared analysis, X-ray diffraction measurement and vibrating-sample magnetometry measurement. The results indicated crystal sizes and amount of the Fe{sub 3}O{sub 4} nanoparticles on the SAFHSS. The magnetic properties of the hollow composite spheres were controlled by adjusting the proportion between Fe{sup 2+} and Fe{sup 3+} and iron ion total concentration. When appropriate loading species were added into the system, superparamagnetite hollow composite spheres were obtained. The method also could be applicable to prepare other superparamagnetite hollow silica/ferrite composite spheres.

  10. Investigation of the electrical and magnetic properties in the composite BaNb_xFe_2_-_xO_4

    International Nuclear Information System (INIS)

    Gontijo, Marcelo Robert Fonseca

    2007-01-01

    The ferrites material magnetic are classified as soft ferrite and hard ferrite in function of its coercive field. They possess a vast field of application in electronic devices had its magnetic property and electric resistivity. This present work reports the influence of the Nb"3 substitution on the structural parameter, magnetic and electrical properties of Ba ferrite. The ferrite system BaNb_xFe_2_-_xO_4, 0.00 ≤ x ≤ 1.0 and the variation of x is in steps of 0.02 until 0.10 from higher iron concentration and from steps of 0.2 until 1.0 to low iron concentration, were prepared using the conventional ceramic technique. The composite utilized was BaCO_3, Fe_2O_3 and Nb_2O_3 were weighed in stoichiometric proportion. The samples had been calcined in oxidant atmosphere in 400°C for 6h, 600°C for 24h and sintered at 1000°C for 48h, using an electrical furnace type Muffle. The structure properties are investigated using a X-ray diffraction (XRD) trough the monochromatic radiation CuK α in 35kV and 40mA, under the 2θ angle with variation of 10° until 70°. The magnetic properties of powders have been studied form the hysteresis loops using a vibration sample magnetometer (VSM) with the variation of measurements is 1x10"-"7emu until 1000emu. The important characteristics desired for a soft magnetic material are the induction saturation B_S or equivalent a magnetic saturation M_S, coercivity H_C, induction remained M_R all of which can be visualized in the M-H loop, and the magnetic susceptibility was calculated using the formula χ=dM/dH. . The temperature dependence of the electrical conductivity of different compositions has been investigated form temperature of 28°C, 50°C, 100°C, 150°C, 200°C and 250°C measurements using current versus voltage (IxV). When, more than one straight line in variation of log σ with 1000/T is obtained indication the different conduction mechanisms and the slope of theses lines given the activation energy. The present work

  11. In-Situ Preparation and Magnetic Properties of Fe3O4/WOOD Composite

    Science.gov (United States)

    Gao, Honglin; Zhang, Genlin; Wu, Guoyuan; Guan, Hongtao

    2011-06-01

    Fe3O4/wood composite, a magnetic material, was prepared by In-situ chemosynthesis method at room temperature. The X-ray diffraction (XRD) shows that the average partical size of Fe3O4 was about 14 nm. The magnetic properties of the resulting composites were investigated by vibrating sample magnetometer (VSM). The composites have saturation magnetization (Ms) values from 4.7 to 25.3 emu/g with the increase of weight percent gains (WPG) of the wood for the composites, but coercive forces (Hc) are invariable, which is different from the magnetic materials reported before. It may be due to the fact that the interaction between wood and Fe3O4 becomes stronger when less of Fe3O4 particles are introduced in the composition, and this also changes the surface anisotropy (Ks) of the magnetism. A structural characterization by Fourier transform infrared (FTIR) proved the interaction between Fe3O4 particles and wood matrix, and it also illustrates that this interaction influences the coercive force of the composite.

  12. Sensitivity Enhancement in Magnetic Sensors Based on Ferroelectric-Bimorphs and Multiferroic Composites

    Directory of Open Access Journals (Sweden)

    Gollapudi Sreenivasulu

    2016-02-01

    Full Text Available Multiferroic composites with ferromagnetic and ferroelectric phases have been studied in recent years for use as sensors of AC and DC magnetic fields. Their operation is based on magneto-electric (ME coupling between the electric and magnetic subsystems and is mediated by mechanical strain. Such sensors for AC magnetic fields require a bias magnetic field to achieve pT-sensitivity. Novel magnetic sensors with a permanent magnet proof mass, either on a ferroelectric bimorph or a ferromagnetic-ferroelectric composite, are discussed. In both types, the interaction between the applied AC magnetic field and remnant magnetization of the magnet results in a mechanical strain and a voltage response in the ferroelectric. Our studies have been performed on sensors with a Nd-Fe-B permanent magnet proof mass on (i a bimorph of oppositely-poled lead zirconate titanate (PZT platelets and (ii a layered multiferroic composite of PZT-Metglas-Ni. The sensors have been characterized in terms of sensitivity and equivalent magnetic noise N. Noise N in both type of sensors is on the order of 200 pT/√Hz at 1 Hz, a factor of 10 improvement compared to multiferroic sensors without a proof mass. When the AC magnetic field is applied at the bending resonance for the bimorph, the measured N ≈ 700 pT/√Hz. We discuss models based on magneto-electro-mechanical coupling at low frequency and bending resonance in the sensors and theoretical estimates of ME voltage coefficients are in very good agreement with the data.

  13. Sensitivity Enhancement in Magnetic Sensors Based on Ferroelectric-Bimorphs and Multiferroic Composites.

    Science.gov (United States)

    Sreenivasulu, Gollapudi; Qu, Peng; Petrov, Vladimir; Qu, Hongwei; Srinivasan, Gopalan

    2016-02-20

    Multiferroic composites with ferromagnetic and ferroelectric phases have been studied in recent years for use as sensors of AC and DC magnetic fields. Their operation is based on magneto-electric (ME) coupling between the electric and magnetic subsystems and is mediated by mechanical strain. Such sensors for AC magnetic fields require a bias magnetic field to achieve pT-sensitivity. Novel magnetic sensors with a permanent magnet proof mass, either on a ferroelectric bimorph or a ferromagnetic-ferroelectric composite, are discussed. In both types, the interaction between the applied AC magnetic field and remnant magnetization of the magnet results in a mechanical strain and a voltage response in the ferroelectric. Our studies have been performed on sensors with a Nd-Fe-B permanent magnet proof mass on (i) a bimorph of oppositely-poled lead zirconate titanate (PZT) platelets and (ii) a layered multiferroic composite of PZT-Metglas-Ni. The sensors have been characterized in terms of sensitivity and equivalent magnetic noise N. Noise N in both type of sensors is on the order of 200 pT/√Hz at 1 Hz, a factor of 10 improvement compared to multiferroic sensors without a proof mass. When the AC magnetic field is applied at the bending resonance for the bimorph, the measured N ≈ 700 pT/√Hz. We discuss models based on magneto-electro-mechanical coupling at low frequency and bending resonance in the sensors and theoretical estimates of ME voltage coefficients are in very good agreement with the data.

  14. Soft template synthesis of mesoporous Co3O4/RuO2.xH2O composites for electrochemical capacitors

    International Nuclear Information System (INIS)

    Liu Yang; Zhao Weiwei; Zhang Xiaogang

    2008-01-01

    Co 3 O 4 /RuO 2 .xH 2 O composites with various Ru content (molar content of Ru = 5%, 10%, 20%, 50%) were synthesized by one-step co-precipitation method. The precursors were prepared via adjusting pH of the mixed aqueous solutions of Co(NO 3 ) 2 .6H 2 O and RuCl 3 .0.5H 2 O by using Pluronic123 as a soft template. For the composite with molar ratio of Co:Ru = 1:1 annealed at 200 deg. C, Brunauer-Emmet-Teller (BET) results indicated that the composite showed mesoporous structure, and the specific surface area of the composite was as high as 107 m 2 g -1 . The electrochemical performances of these composites were measured in 1 M KOH electrolyte. Compared with the composite prepared without template, the composite with P123 exhibited a higher specific capacitance. When the molar content of Ru was rising, the specific capacitance of the composites increased significantly. It was also observed that the crystalline structures as well as the electrochemical activities were strongly dependent on the annealing temperature. A capacitance of 642 F/g was obtained for the composite (Co:Ru = 1:1) annealed at 150 deg. C. Meanwhile, the composites also exhibited good cycle stability. Besides, the morphologies and textural characteristic of the samples were also investigated by X-ray diffraction (XRD), transmission electron microscopy (TEM)

  15. Preparation of ring-shaped composite bonded magnets with continuously controlled anisotropy distribution for internal space

    International Nuclear Information System (INIS)

    Yamashita, F; Yamada, O; Ohya, S; Kobayashi, O; Nakano, M; Fukunaga, H

    2010-01-01

    We have already reported an advanced method for producing a radially-anisotropic rare earth composite bonded magnet with continuously controlled direction of anisotropy. The magnet has been applied to an inner rotor as a practical usage. In this study, the outstanding preparation method was adopted into the preparation of a magnet applied for an outer rotor. An optimized condition of extrusion and compaction at an elevated temperature could be obtained. In addition, a low pressure configuration to the ring-shaped magnet from plural preformed magnets was carried out, which had specific distribution of magnetic anisotropy for internal space for a small motor, by using self recoverability based on the viscous deformation without an alignment field. No deterioration of magnetic properties was detected through the process even if those magnets were miniaturized. Resultantly, the (BH) max of a ring-shaped magnet with the continuously controlled direction of magnetic anisotropy attained the value of 186 kJ/m 3 , and we obtained sine-wave magnetic anisotropy distribution, even if those magnets were miniaturized.

  16. An autonomously electrically self-healing liquid metal-elastomer composite for robust soft-matter robotics and electronics.

    Science.gov (United States)

    Markvicka, Eric J; Bartlett, Michael D; Huang, Xiaonan; Majidi, Carmel

    2018-07-01

    Large-area stretchable electronics are critical for progress in wearable computing, soft robotics and inflatable structures. Recent efforts have focused on engineering electronics from soft materials-elastomers, polyelectrolyte gels and liquid metal. While these materials enable elastic compliance and deformability, they are vulnerable to tearing, puncture and other mechanical damage modes that cause electrical failure. Here, we introduce a material architecture for soft and highly deformable circuit interconnects that are electromechanically stable under typical loading conditions, while exhibiting uncompromising resilience to mechanical damage. The material is composed of liquid metal droplets suspended in a soft elastomer; when damaged, the droplets rupture to form new connections with neighbours and re-route electrical signals without interruption. Since self-healing occurs spontaneously, these materials do not require manual repair or external heat. We demonstrate this unprecedented electronic robustness in a self-repairing digital counter and self-healing soft robotic quadruped that continue to function after significant damage.

  17. Soft magnetic properties of hybrid ferromagnetic films with CoFe, NiFe, and NiFeCuMo layers

    Energy Technology Data Exchange (ETDEWEB)

    Choi, Jong-Gu [Eastern-western Biomedical Engineering, Sangji University, Wonju 220-702 (Korea, Republic of); Hwang, Do-Guwn [Dept. of Oriental Biomedical Engineering, Sangji University, Wonju 220-702 (Korea, Republic of); Rhee, Jang-Roh [Dept. of Physics, Sookmyung Women' s University, Seoul 140-742 (Korea, Republic of); Lee, Sang-Suk, E-mail: sslee@sangji.ac.kr [Dept. of Oriental Biomedical Engineering, Sangji University, Wonju 220-702 (Korea, Republic of)

    2011-09-30

    Two-layered ferromagnetic alloy films (NiFe and CoFe) with intermediate NiFeCuMo soft magnetic layers of different thicknesses were investigated to understand the relationship between coercivity and magnetization process by taking into account the strength of hard-axis saturation field. The thickness dependence of H{sub EC} (easy-axis coercivity), H{sub HS} (hard-axis saturation field), and {chi} (susceptibility) of the NiFeCuMo thin films in glass/Ta(5 nm)/[CoFe or NiFe(5 nm-t/2)]/NiFeCuMo(t = 0, 4, 6, 8, 10 nm)/[CoFe or NiFe(5 nm-t/2)]/Ta(5 nm) films prepared using the ion beam deposition method was determined. The magnetic properties (H{sub EC}, H{sub HS}, and {chi}) of the ferromagnetic CoFe, NiFe three-layers with an intermediate NiFeCuMo super-soft magnetic layer were strongly dependent on the thickness of the NiFeCuMo layer.

  18. Magnetic composite beads for sorption of cesium ions from aqueous streams

    International Nuclear Information System (INIS)

    Shinde, Rakesh N.; Pandey, A.K.; Acharya, R.; Rajurkar, N.S.

    2014-01-01

    Magnetic separation of metal ions is one of the promising methods due to simple, fast, efficient and cost effective technology. Highly selective magnetic sorbents can be designed by immobilizing functional groups in magnetic carrier which binds to the target specific ions. In the present work chitosan-(3-aminopropyl) triethoxysilane (APTS)- copperferrocyanide (CFC) composite beads have been synthesized for sorption of 137 Cs ions from aqueous streams. Physical characterization of the best resulted polymer beads was carried out by SEM-EDX and VSM technique. Sorption of Cs ions in the various magnetic polymer beads were studied in different aqueous condition by 137 Cs (662 KeV) radiotracer assay

  19. Element-specific observation of the ferromagnetic ordering process in UCoAl via soft x-ray magnetic circular dichroism

    Science.gov (United States)

    Takeda, Yukiharu; Saitoh, Yuji; Okane, Tetsuo; Yamagami, Hiroshi; Matsuda, Tatsuma D.; Yamamoto, Etsuji; Haga, Yoshinori; Ōnuki, Yoshichika

    2018-05-01

    We have performed soft x-ray magnetic circular dichroism (XMCD) experiments on the itinerant-electron metamagnet UCoAl at the U 4 d -5 f (N4 ,5) and Co 2 p -3 d (L2 ,3) absorption edges in order to investigate the magnetic properties of the U 5 f and Co 3 d electrons separately. From the line shape of the XMCD spectrum, it is deduced that the orbital magnetic moment of the Co 3 d electrons is unusually large. Through the systematic temperature (T )- and magnetic field (H )-dependent XMCD measurements, we have obtained two types of the magnetization curve as a function of H and T (M-H curve and M-T curve, respectively). The metamagnetic transition from a paramagnetic state to a field-induced ferromagnetic state was clearly observed under 15 K at HM. The value of the HM and its T dependence agree well between the U and Co sites, and the bulk magnetization. Whereas, we have discovered the remarkable differences in the M-H and M-T curves between the U and Co sites. The present findings clearly show that the role of the Co 3 d electrons should be considered more carefully in order to understand the origin of the magnetic ordering in UCoAl.

  20. Magnetic properties and densification of Manganese-Zinc soft ferrites (Mn1-xZnxFe2O4) doped with low melting point oxides

    International Nuclear Information System (INIS)

    Shokrollahi, H.

    2008-01-01

    Mn-Zn ferrites have high electrical resistivity, low power loss and high initial permeability up to several MHz range. Oxide additives can greatly affect the magnetic properties of these ferrites. The effects of the additives on the sintering behaviour and magnetic properties of Mn-Zn ferrites are different. Some low melting point additives such as Bi 2 O 3 enhance the sintering by forming a liquid phase in the ferrites. The additive V 2 O 5 enhances the sintering by increasing bulk diffusion due to the increased vacancy concentration which is accompanied by the solubility of V 5+ in the ferrites. Some additives are cations that are soluble in the host lattice and enter regular positions on the tetrahedral or octahedral sites. This paper investigates the effect of several low melting point oxides on the magnetic properties, microstructure and densification of Mn-Zn soft ferrites

  1. Mechanical Properties Analysis Of Composite Magnetic Base On hexa ferrite And Polyester Or Epoxy Matrix With Silane Additive Addition

    International Nuclear Information System (INIS)

    Sudirman; Ridwan; Mujamilah; K K, Aloma; Rembulan, Marisa; Fitriyanti

    2003-01-01

    Application of composite magnetic especially hexa ferrite magnet for industry and home industry in Indonesia has been used. Research purposes were making composite magnetic by mixing hexa ferrite powder with polyester or epoxy and studying the effect of coupling agent 3-aminopropyltriethoxysilane (3-APE) addition on mechanical properties of composite magnetic. The coupling agent may increase bonding properties between magnetic powder and matrix polymer, so that tensile strength of magnetic composite will increase without decreasing the magnetic properties. Magnetic powder (SrM or BaM) wich be coated by coupling agent were added to matrix polyester and mekpo or epoxy and versamid, mixed until homogen then pressing into to the dumbbell form molding. For epoxy matrix, pressing was done in hot press at 70 deg. C and 150 kg/cm 2 following by cooling in cold press, while for polyester matrix pressing was done in hydraulic press and following by curing at 70 deg. C in an oven for 1 hour. The composition of magnetic powder were varied to 30, 40 and 50% volume fraction and coupling agent were varied to 5, 10 and 15 ml for every volume fraction. The result showed that 10 ml added of coupling agent was give best mechanical properties both polyester and epoxy matrix. However generally, increasing of magnetic powder content decreased the tensile strength of magnetic composite. The properties of magnetic composite SrM was better than BaM either in polyester or epoxy matrix

  2. Magnetic Composite Thin Films of FexOy Nanoparticles and Photocrosslinked Dextran Hydrogels

    International Nuclear Information System (INIS)

    Brunsen, Annette; Utech, Stefanie; Maskos, Michael; Knoll, Wolfgang; Jonas, Ulrich

    2012-01-01

    Magnetic hydrogel composites are promising candidates for a broad field of applications from medicine to mechanical engineering. Here, surface-attached composite films of magnetic nanoparticles (MNP) and a polymeric hydrogel (HG) were prepared from magnetic iron oxide nanoparticles and a carboxymethylated dextran with photoreactive benzophenone substituents. A blend of the MNP and the dextran polymer was prepared by mixing in solution, and after spin-coating and drying the blend film was converted into a stable MNP–HG composite by photocrosslinking through irradiation with UV light. The bulk composite material shows strong mobility in a magnetic field, imparted by the MNPs. By utilizing a surface layer of a photoreactive adhesion promoter on the substrates, the MNP–HG films were covalently immobilized during photocrosslinking. The high stability of the composite was documented by rinsing experiments with UV–Vis spectroscopy, while surface plasmon resonance and optical waveguide mode spectroscopy was employed to investigate the swelling behavior in dependence of the nanoparticle concentration, the particle type, and salt concentration. - Highlights: ► blending of iron oxide nanoparticles with photocrosslinkable carboxymethyldextran. ► UV irradiation of blend yields surface-attached, magnetic hydrogel films. ► film characterization by surface plasmon resonance/optical waveguide spectroscopy. ► swelling decreases with increasing nanoparticle content. ► swelling decreases with increasing NaCl salt concentration in the aqueous medium.

  3. Analysis of physical and magnetic properties of composite NdFeB bind with polyvinyl alcohol

    Science.gov (United States)

    Ramlan; Sardjono, P.; Muljadi; Setiabudidaya, D.; Gulo, F.

    2018-03-01

    The composite magnet NdFeB has been made using magnetic powder MQP-B and polyvinyl alcohol (PVA) as the binder. The mixing compositions of raw materials used are: 95 wt% NdFeB - 5 wt% PVA, 92.5 wt% NdFeB - 7.5 wt% PVA, 90 wt.% NdFeB - 10 wt% PVA, and 87.5 wt% NdFeB - 12.5 wt% PVA. Both raw materials are weighed according to the composition, and then mixed until homogeneous. Furthermore, pellet forming was made using dry pressing at 50 kgf/cm2 pressures and continued with drying at 100 °C and 10 mmbar for 4 hours. The characterization includes bulk density, hardness, compressive strength measurements, and magnetic properties testing. The characterization results show that the optimal composition of binder PVA is achieved at 5–7.5 wt% NdFeB composite magnet with following properties: bulk density = 5.21–5.25 g/cm3, hardness = 302.17 - 304.32 Hv, compressive strength = 25.17–3.17 kgf/cm2, magnetic flux = 1150-1170 Gauss, remanence = 70.90–74.97 emu/g or 4.7–5.0 kGauss, coercivity = 8.68–8.76 kOe, and energy product = 2.89–3.04 MgOe.

  4. Effect of high intensity vs. soft-start halogen irradiation on light-cured resin-based composites. Part I. Temperature rise and polymerization shrinkage.

    Science.gov (United States)

    Hofmann, Norbert; Markert, Tanja; Hugo, Burkard; Klaiber, Bernd

    2003-12-01

    To determine polymerization shrinkage kinetics and temperature rise of light-cured resin-based composites after high intensity vs. soft-start quartz tungsten halogen irradiation. Shrinkage kinetics was evaluated using the "deflecting disk technique", modified for simultaneous measurement of temperature within the resin-based composite using a thermocouple. Additional irradiations after 60 and 65 minutes allowed the determination of temperature rises caused by radiation or by reaction heat. Four hybrids (Filtek Z250, Herculite, Solitaire 2, Tetric Ceram), an inhomogeneously filled hybrid (InTen-S) and a microfill (Filtek A110, formerly Silux Plus) were cured using the quartz tungsten halogen units Astralis 10 and Optilux 501 in the high intensity (A10 HiPo: 10 seconds at 1300 mW/cm2; OL Boost: 10 seconds at 1140 mW/cm2) or soft-start modes (A10 Pulse: increase to 700 mW/cm2 within 10 seconds, three periods of 2 seconds at 1300 mW/cm2 alternating with two periods of 2 seconds at 700 mW/cm2; OL Ramp: exponential increase within 10 seconds, followed by 10 seconds at 1140 mW/cm2). The soft-start protocols produced less contraction, and polymerization shrinkage started later and progressed slower (or: more slowly), compared to high intensity irradiation [correction]. The lowest shrinkage was observed for InTen-S, followed by Filtek Z250 and A110, whereas Solitaire 2, Herculite and Tetric Ceram scored highest for this parameter. Temperature rise was caused more or less equally by radiation and by reaction heat and reached values of up to 28.9 degrees C relative to a baseline of 37 degrees C. For some combinations of curing modes and resin-based composites, less heat was generated by the soft-start protocols and by Optilux 501.

  5. Magnetic nanowires (Fe, Fe-Co, Fe-Ni – magnetic moment reorientation in respect of wires composition

    Directory of Open Access Journals (Sweden)

    Kalska-Szostko Beata

    2015-03-01

    Full Text Available Magnetic nanowires of Fe, Fe-Co, and Fe-Ni alloy and layered structure were prepared by electrochemical alternating current (AC deposition method. The morphology of the nanowires in and without the matrix was studied by energy dispersive X-ray spectroscopy (EDX, scanning electron microscopy (SEM, and X-ray diffraction (XRD, respectively. The wires either show strong dependence on the combination of elements deposition (alloy or layered or chemical composition (Co or Ni. The magnetic properties of the nanostructures were determined on the basis of Mössbauer spectroscopy (MS.

  6. Reduced Magnetism in Core–Shell Magnetite@MOF Composites

    Energy Technology Data Exchange (ETDEWEB)

    Elsaidi, Sameh K.; Sinnwell, Michael A.; Banerjee, Debasis; Devaraj, Arun; Kukkadapu, Ravi K.; Droubay, Timothy C.; Nie, Zimin; Kovarik, Libor; Murugesan, Vijayakumar; Manandhar, Sandeep; Nandasiri, Manjula I.; McGrail, Bernard P.; Thallapally, Praveen K.

    2017-10-17

    Rare-earth elements (REEs) have significant commercial and military uses.1-3 However, REE extraction through conventional mining processes is expensive and feasible at only a few locations worldwide. Alternative methods are needed to produce REEs from more geographically disperse resources and in a cost effective, environmental friendly manner.4,5 Among various sources, geothermal brine, used for generating geothermal energy can possess attractive concentrations (ppb to ppm level) of REEs along with other dissolved metal ions.6 A system that can selectively trap the REEs using an existing geothermal power plant infrastructure would be an attractive additional revenue stream for the plant operator that could accelerate the development and deployment of geothermal plants in the United States and rest of the world.7,8 Here, we demonstrate a magnetic core-shell approach that can effectively extract REEs in their ionic form from aqueous solution with up to 99.99% removal efficiency. The shell, composed of thermally and chemically stable functionalized metal-organic framework (MOF), is grown over a synthesized Fe3O4 magnetic core. Magnetic susceptibility of the particles was found to decline significantly after in situ growth of a MOF shell, which resulted from oxidation of Fe2+ species of the magnetite (Fe3O4) to Fe3+ species (maghemite). The core-shell particles can be completely removed from the mixture under an applied magnetic field, offering a practical, economic, and efficient REE-removal process.

  7. Mechanical properties, microstructure and magnetic properties of composite magnet base on SrO.6Fe_2O_3 (SRM)-thermoplastic and thermoset polymer

    International Nuclear Information System (INIS)

    Grace Tj Sulungbudi; Aloma Karo Karo; Mujamilah; Sudirman

    2010-01-01

    The use of magnets in industrial applications do not always require high magnetic properties. Therefore, the use of polymer as a matrix that serves as a binder can be applied to obtain lightweight, flexible and cheap composite magnet. This report discuss composite magnet base on SrO.6Fe_2O_3(SRM)-thermoplastic and thermoset polymer. Thermoplastic polymer consist of polypropylene (PP) type of PP2 and PP10 and polyethylene (PE) type of LDPE were used. For thermoset polymer, epoxy and polyester were used. Synthesis of composite magnet based on thermoplastic polymer (PP2, PP10, LDPE) were carried using the blending method, while the thermoset composites magnet using casting method. Thermoplastic composite magnets were prepared with compositions of 50, 41, 38, 33 and 29 % weight of SRM with the blending temperature of 160 °C for LDPE and 180 °C for PP2 and PP10. For thermoset composite magnets, the compositions were 30, 40, 50 and 60 % by weight of SRM. The mechanical test conducted include tensile strength and elongation at break. Microstructure on the surface of the composite materials were observed using SEM (Scanning Electron Microscope) and the magnetic properties were measured using VSM (Vibrating Sample Magnetometer). The SEM results showed the formation of flat shape powder particle with size of 1.6 µm. In general, the mechanical properties of polypropylene polymer composite magnet are better than that using polyethylene (LDPE) binder. For polypropylene binder PP10 is better than PP2. Magnetic properties are not significantly affected by the change of polymer or binder types. (author)

  8. Phase formation, dielectric and magnetic properties of bismuth ferrite–lead magnesium niobate multiferroic composites

    Energy Technology Data Exchange (ETDEWEB)

    Wongmaneerung, R., E-mail: re_nok@yahoo.com [Faculty of Science, Maejo University, Chiang Mai 50290 (Thailand); Padchasri, J.; Tipakontitikul, R. [Department of Physics, Ubonratchathani University, Ubonratchathani 31490 (Thailand); Loan, T.H. [International Training Institute for Materials Science (ITIMS), Hanoi University of Science and Technology, No. 1, Dai Co Viet, Hanoi (Viet Nam); Jantaratana, P. [Department of Physics, Kasetsart University, Bangkok 10900 (Thailand); Yimnirun, R. [School of Physics, Institute of Science, and NANOTEC-SUT Center of Excellence of Advanced Functional Nanomaterials, Suranaree University of Technology, Nakhon Ratchasima 30000 (Thailand); Ananta, S. [Department of Physics and Materials Science, Faculty of Science, Chiang Mai University, Chiang Mai 50200 (Thailand)

    2014-09-01

    Highlights: • A bimodal particle size concept was designed in the production of BF–PMN composites. • A very abnormal diffuse dielectric pattern is observed during the heating process. • BF–PMN composites show highly saturated magnetization. - Abstract: Binary multiferroic composites (1−x)BiFeO{sub 3}–xPb(Mg{sub 1/3}Nb{sub 2/3})O{sub 3} (BF–PMN; x = 0.0–50 wt%) were fabricated through a traditional ceramic process. The effect of the PMN contents on the phase assemblage, microstructure, dielectric and magnetic properties of the samples were investigated by X-ray diffraction (XRD), scanning electron microscope (SEM), LCR meter and vibrating sample magnetometer (VSM), respectively. The results indicate that all composites show that perovskite structure and PMN phase is compatible with the BF phase. The microstructure displays the mix phases between BF, PMN, Bi-rich BF and Fe-rich BF phases. Dielectric anomalies of these composites are totally different from BiFeO{sub 3} single phase. Moreover, the dielectric constant is found to increase as the content of PMN decreases. Magnetic transition temperatures are in the range of 270–440 °C. Interestingly, the M–H hysteresis loop measurements indicated that all composites exhibited weak ferromagnetism behavior at room temperature. The maximum remanent magnetization M{sub r} is observed for x = 30 wt% and then decreases when the PMN content is more than 40 wt%.

  9. Fast determination of seven synthetic pigments from wine and soft drinks using magnetic dispersive solid-phase extraction followed by liquid chromatography-tandem mass spectrometry.

    Science.gov (United States)

    Chen, Xiao-Hong; Zhao, Yong-Gang; Shen, Hao-Yu; Zhou, Li-Xin; Pan, Sheng-Dong; Jin, Mi-Cong

    2014-06-13

    A novel, simple and sensitive method based on the use of magnetic dispersive solid-phase extraction (M-dSPE) procedure combined with ultra-fast liquid chromatography-tandem quadrupole mass spectrometry (UFLC-MS/MS) was developed to determine seven synthetic pigments (tartrazine, amaranth, carmine, sunset yellow, allura red, brilliant blue and erythrosine) in wines and soft drinks. An amino-functionalized low degrees of cross-linking magnetic polymer (NH2-LDC-MP) was synthesized via suspension polymerization, and characterized by transmission electron microscopy (TEM). The NH2-LDC-MP was used as the M-dSPE sorbent to remove the matrix from the solution, and the main factors affecting the extraction were investigated in detail. The obtained results demonstrated the higher extraction capacity of NH2-LDC-MP with recoveries between 84.0 and 116.2%. The limits of quantification (LOQs) for the seven synthetic pigments were between 1.51 and 5.0μg/L in wines and soft drinks. The developed M-dSPE UFLC-MS/MS method had been successfully applied to the real wines and soft drinks for food-safety risk monitoring in Zhejiang Province, China. The results showed that sunset yellow was in three out of thirty soft drink samples (2.95-42.6μg/L), and erythrosine in one out of fifteen dry red wine samples (3.22μg/L), respectively. It was confirmed that the NH2-LDC-MP was a kind of highly effective M-dSPE materials for the pigments analyses. Copyright © 2014 Elsevier B.V. All rights reserved.

  10. Spin dynamics and frequency dependence of magnetic damping study in soft ferromagnetic FeTaC film with a stripe domain structure

    Energy Technology Data Exchange (ETDEWEB)

    Samantaray, B., E-mail: iitg.biswanath@gmail.com; Ranganathan, R.; Mandal, P. [Saha Institute of Nuclear Physics, 1/AF Bidhannagar, Calcutta 700 064 (India); Singh, Akhilesh K.; Perumal, A. [Department of Physics, Indian Institute of Technology Guwahati, Guwahati - 781039 (India)

    2015-06-15

    Perpendicular magnetic anisotropy (PMA) and low magnetic damping are the key factors for the free layer magnetization switching by spin transfer torque technique in magnetic tunnel junction devices. The magnetization precessional dynamics in soft ferromagnetic FeTaC thin film with a stripe domain structure was explored in broad band frequency range by employing micro-strip ferromagnetic resonance technique. The polar angle variation of resonance field and linewidth at different frequencies have been analyzed numerically using Landau-Lifshitz-Gilbert equation by taking into account the total free energy density of the film. The numerically estimated parameters Landé g-factor, PMA constant, and effective magnetization are found to be 2.1, 2 × 10{sup 5} erg/cm{sup 3} and 7145 Oe, respectively. The frequency dependence of Gilbert damping parameter (α) is evaluated by considering both intrinsic and extrinsic effects into the total linewidth analysis. The value of α is found to be 0.006 at 10 GHz and it increases monotonically with decreasing precessional frequency.

  11. A self-strain feedback tuning-fork-shaped ionic polymer metal composite clamping actuator with soft matter elasticity-detecting capability for biomedical applications.

    Science.gov (United States)

    Feng, Guo-Hua; Huang, Wei-Lun

    2014-12-01

    This paper presents a smart tuning-fork-shaped ionic polymer metal composite (IPMC) clamping actuator for biomedical applications. The two fingers of the actuator, which perform the clamping motion, can be electrically controlled through a unique electrode design on the IPMC material. The generated displacement or strain of the fingers can be sensed using an integrated soft strain-gage sensor. The IPMC actuator and associated soft strain gage were fabricated using a micromachining technique. A 13.5×4×2 mm(3) actuator was shaped from Nafion solution and a selectively grown metal electrode formed the active region. The strain gage consisted of patterned copper foil and polyethylene as a substrate. The relationship between the strain gage voltage output and the displacement at the front end of the actuator's fingers was characterized. The equivalent Young's modulus, 13.65 MPa, of the soft-strain-gage-integrated IPMC finger was analyzed. The produced clamping force exhibited a linear increasing rate of 1.07 mN/s, based on a dc driving voltage of 7 V. Using the developed actuator to clamp soft matter and simultaneously acquire its Young's modulus was achieved. This demonstrated the feasibility of the palpation function and the potential use of the actuator in minimally invasive surgery. Copyright © 2014 Elsevier B.V. All rights reserved.

  12. Effects of intermediate layers on magnetic properties and read/write performance in CoCrPt perpendicular recording media with an FeHfN soft magnetic underlayer

    International Nuclear Information System (INIS)

    Hong, D.H.; Shin, J.N.; Lee, T.D.; Hong, S.Y.; Lee, H.J.

    2003-01-01

    In this study, the effects of CoCrPtTa and CoCrPtB magnetic intermediate layers (ILs) on the magnetic properties and read/write performance of CoCrPt/soft magnetic layer perpendicular recording media were investigated. Even though the perpendicular coercivity of the media with these ILs was reduced by 500 Oe, these media still showed a low exchange slope of 1.4 and a large negative nucleation field of about -1000 Oe. Additionally, the reduced grain size of the media with these IL was observed by transmission electron microscopy. From the read/write test, these media with ILs showed improved performance of 3-5 dB higher signal-to-noise ratio and overwrite ratio (OW) compared to the media without ILs. These enhancements could be attributed to the reduction of grain size of the magnetic layer and weakening of the intergranular interaction between grains by insertion of the IL

  13. DC conductivity and magnetic properties of piezoelectric–piezomagnetic composite system

    International Nuclear Information System (INIS)

    Hemeda, O.M.; Tawfik, A.; A-Al-Sharif; Amer, M.A.; Kamal, B.M.; El Refaay, D.E.; Bououdina, M.

    2012-01-01

    A series of composites (1−x) (Ni 0.8 Zn 0.2 Fe 2 O 4 )+x (BaTiO 3 ), where x=0%, 20%, 40%, 60%, 80% and 100% BT content, have been prepared by the standard ceramic technique, then sintered at 1200 °C for 8 h. X-ray diffraction analysis shows that the prepared composites consist of two phases, ferrimagnetic and ferroelectric. DC electrical resistivity, thermoelectric power, charge carriers concentration and charge carrier mobility have been studied at different temperatures. It was found that the DC electrical conductivity increases with increasing BT content. The values of the thermoelectric power were positive and negative for the composites indicating that there are two conduction mechanisms, hopping and band conduction, respectively. Using the values of DC electrical conductivity and thermoelectric power, the values of charge carrier mobility and the charge carrier concentration were calculated. Magnetic measurements (hysteresis loop and magnetic permeability) show that the magnetization decreases by increasing BT content. M–H loop of pure Ni 0.6 Zn 0.4 Fe 2 O 4 composite indicates that it is paramagnetic at room temperature and that the magnetization is diluted by increasing the BT content in the composite system. The value of magnetoelectric coefficient for the composites decreases by increasing BT content for all the compositions except for 40% BT content, which may be due to the low resistivity of magnetic phase compared with the BT phase that causes a leakage of induced charges on the piezoelectric phase. Since both ferroelectric and magnetic phases preserve their basic properties in the bulk composite, the present BT–NZF composite are potential candidates for applications as pollution sensors and electromagnetic waves. - Highlights: ► Studied composite has a high magnetoelectric coefficient compared with other composites. ► A p–n transition is observed for the composite with 80% BT and 100% BT content. ► Ni-ferrite can lead to a strong shift

  14. DC conductivity and magnetic properties of piezoelectric-piezomagnetic composite system

    Energy Technology Data Exchange (ETDEWEB)

    Hemeda, O.M., E-mail: omhemeda@yahoo.co.uk [Tanta University, Faculty of Science, Physics Department (Egypt); Taif University, Faculty of Science, Physics Department (Saudi Arabia); Tawfik, A. [Taif University, Faculty of Science, Physics Department (Saudi Arabia); A-Al-Sharif [Moata University, Faculty of Science, Physics Department (Jordan); Amer, M.A. [Taif University, Faculty of Science, Physics Department (Saudi Arabia); Kamal, B.M.; El Refaay, D.E. [Suez Canal University, Faculty of Science, Physics Department (Egypt); Bououdina, M. [Nanotechnology Centre, College of Science, University of Bahrain, PO Box 32038 (Bahrain); Department of Physics, College of Science, University of Bahrain, PO Box 32038 (Bahrain)

    2012-11-15

    A series of composites (1-x) (Ni{sub 0.8}Zn{sub 0.2}Fe{sub 2}O{sub 4})+x (BaTiO{sub 3}), where x=0%, 20%, 40%, 60%, 80% and 100% BT content, have been prepared by the standard ceramic technique, then sintered at 1200 Degree-Sign C for 8 h. X-ray diffraction analysis shows that the prepared composites consist of two phases, ferrimagnetic and ferroelectric. DC electrical resistivity, thermoelectric power, charge carriers concentration and charge carrier mobility have been studied at different temperatures. It was found that the DC electrical conductivity increases with increasing BT content. The values of the thermoelectric power were positive and negative for the composites indicating that there are two conduction mechanisms, hopping and band conduction, respectively. Using the values of DC electrical conductivity and thermoelectric power, the values of charge carrier mobility and the charge carrier concentration were calculated. Magnetic measurements (hysteresis loop and magnetic permeability) show that the magnetization decreases by increasing BT content. M-H loop of pure Ni{sub 0.6} Zn{sub 0.4} Fe{sub 2}O{sub 4} composite indicates that it is paramagnetic at room temperature and that the magnetization is diluted by increasing the BT content in the composite system. The value of magnetoelectric coefficient for the composites decreases by increasing BT content for all the compositions except for 40% BT content, which may be due to the low resistivity of magnetic phase compared with the BT phase that causes a leakage of induced charges on the piezoelectric phase. Since both ferroelectric and magnetic phases preserve their basic properties in the bulk composite, the present BT-NZF composite are potential candidates for applications as pollution sensors and electromagnetic waves. - Highlights: Black-Right-Pointing-Pointer Studied composite has a high magnetoelectric coefficient compared with other composites. Black-Right-Pointing-Pointer A p-n transition is observed

  15. The thermal stability of magnetically exchange coupled MnBi/FeCo composites at electric motor working temperature

    Science.gov (United States)

    Cheng, Ye; Wang, Hongying; Li, Zhigang; Liu, Wanhui; Bao, Ilian

    2018-04-01

    The magnetically exchange coupled MnBi/FeCo composites were synthesized through a magnetic self-assembly process. The MnBi/FeCo composites were then hot pressed in a magnetic field to form magnets. The thermal stability of the magnets were tested by annealing at electric motor working temperature of 200 °C for 20, 40 and 60 h, respectively. It was found that after heating for 20 h, there was negligible change in its hysteresis loop. However, when the heating time was increased 40 and 60 h, the magnetic hysteresis loops presented two-phase magnetic behaviors, and the maximum energy products of the magnet were decreased. This research showed that the magnetically exchange coupled MnBi/FeCo composites had low thermal stability at electric motor working temperature.

  16. An investigation on the role of texture evolution and ordered phase transition in soft magnetic properties of Fe–6.5 wt%Si electrical steel

    Energy Technology Data Exchange (ETDEWEB)

    Cai, Guojun; Li, Changsheng, E-mail: lics@ral.neu.edu.cn; Cai, Ban; Wang, Qiwen

    2017-05-15

    Fe–6.5 wt%Si electrical steel characterized with excellent soft magnetic properties such as almost zero magnetostriction, low eddy current and hysteresis losses characteristics has been widely applied in high frequency fields. In this work, the role of texture evolution and ordered phase transition in soft magnetic properties of annealed sheets was explored using EBSD, XRD and TEM. The results demonstrate that accompanied with the increase of annealing temperatures, an increase on the B8 is attributable to a contribution combining the sizes of recrystallization grains with APBs of ordered phases as pinning the migration of magnetic domain wall. Whereas B50 declines to a minimum value (1.479 T) and then increases to a certain value (1.695 T) due to different types and intensities of textures affecting on the magnetocrystalline anisotropy energy. Meanwhile, the dislocation density gradually decreases and corresponding to a gradual decline in the internal stress, which makes the coercive force (H{sub c}) decrease monotonically. - Highlights: • Role of texture and ordered phase in Fe–6.5 wt%Si were studied. • With increasing annealing temperatures, H{sub c} decreases monotonically. • Combining grain sizes with APBs in B8 measurements. • Increasing annealing temperatures, B50 declines and then increases due to texture.

  17. Composite of ceramic-coated magnetic alloy particles

    Science.gov (United States)

    Moorhead, Arthur J.; Kim, Hyoun-Ee

    2000-01-01

    A composite structure and method for manufacturing same, the composite structure being comprised of metal particles and an inorganic bonding media. The method comprises the steps of coating particles of a metal powder with a thin layer of an inorganic bonding media selected from the group of powders consisting of a ceramic, glass, and glass-ceramic. The particles are assembled in a cavity and heat, with or without the addition of pressure, is thereafter applied to the particles until the layer of inorganic bonding media forms a strong bond with the particles and with the layer of inorganic bonding media on adjacent particles. The resulting composite structure is strong and remains cohesive at high temperatures.

  18. Energy and momentum management of the Space Station using magnetically suspended composite rotors

    Science.gov (United States)

    Eisenhaure, D. B.; Oglevie, R. E.; Keckler, C. R.

    1985-01-01

    The research addresses the feasibility of using magnetically suspended composite rotors to jointly perform the energy and momentum management functions of an advanced manned Space Station. Recent advancements in composite materials, magnetic suspensions, and power conversion electronics have given flywheel concepts the potential to simultaneously perform these functions for large, long duration spacecraft, while offering significant weight, volume, and cost savings over conventional approaches. The Space Station flywheel concept arising out of this study consists of a composite-material rotor, a large-angle magnetic suspension (LAMS) system, an ironless armature motor/generator, and high-efficiency power conversion electronics. The LAMS design permits the application of appropriate spacecraft control torques without the use of conventional mechanical gimbals. In addition, flywheel systems have the growth potential and modularity needed to play a key role in many future system developments.

  19. The Magnetic Properties of Metal-Alloy Glass Composites Prepared by Ion Implantation

    International Nuclear Information System (INIS)

    Julian Fernandez, Cesar de; Mattei, Giovanni; Sada, Cinzia; Maurizio, Chiara; Padovani, Sara; Mazzoldi, Paolo; Sangregorio, Claudio; Gatteschi, Dante

    2003-01-01

    The structural and magnetic properties of Co-Ni, Co-Fe and Ni-Cu alloy nanoparticles formed in silica matrix by sequential ion implantation are presented. These nanoparticles show crystal structure similar to the corresponding bulk alloys. In the Co-Ni and Co-Fe, magnetization saturation and coercive field depend on the the alloy composition, crystal structure and size effects. Ferromagnetic resonance studies show that collective magnetic processes are present and these are determined by the film-like morphology of the implanted region. The temperature dependence of the magnetization of the NixCu100-x samples indicates that their Curie Temperatures are larger than the corresponding bulk ones. This feature is discussed considering the composition of the nanoparticles and the size effects

  20. A colloidal assembly approach to synthesize magnetic porous composite nanoclusters for efficient protein adsorption

    Science.gov (United States)

    Yang, Qi; Lan, Fang; Yi, Qiangying; Wu, Yao; Gu, Zhongwei

    2015-10-01

    A combination strategy of the inverse emulsion crosslinking approach and the colloidal assembly technique is first proposed to synthesize Fe3O4/histidine composite nanoclusters as new-type magnetic porous nanomaterials. The nanoclusters possess uniform morphology, high magnetic content and excellent protein adsorption capacity, exhibiting their great potential for bio-separation.A combination strategy of the inverse emulsion crosslinking approach and the colloidal assembly technique is first proposed to synthesize Fe3O4/histidine composite nanoclusters as new-type magnetic porous nanomaterials. The nanoclusters possess uniform morphology, high magnetic content and excellent protein adsorption capacity, exhibiting their great potential for bio-separation. Electronic supplementary information (ESI) available: Experimental details. See DOI: 10.1039/c5nr05800g

  1. Study of electric, magnetic properties and improvements in ME effects of NMFO + BZT particulate composites

    Energy Technology Data Exchange (ETDEWEB)

    Chavan, Pradeep [Department of Physics, Karnatak University, Dharwad 580003, Karnataka (India); Naik, L.R., E-mail: naik_40@rediffmail.com [Department of Physics, Karnatak University, Dharwad 580003, Karnataka (India); Kotnala, R.K. [National Physical Laboratory, K. S. Krishnan Marg, Pusa, New Delhi 110012 (India)

    2017-07-01

    ME composite materials with the general formula (x)Ni{sub 0.9}Mg{sub 0.1}Fe{sub 2}O{sub 4} + (1 − x)BaZr{sub 0.2}Ti{sub 0.8}O{sub 3} (x = 0.1, 0.2, 0.3, 0.4 and 0.5) were synthesized by solid state reaction method. X-ray diffraction (XRD) study reveals the coexistence of piezomagnetic and piezoelectric phases without interacting with each other. The cubic spinel structure of Ni{sub 0.9}Mg{sub 0.1}Fe{sub 2}O{sub 4} (NMFO) piezomagnetic phase and tetragonal perovskite structure of BaZr{sub 0.2}Ti{sub 0.8}O{sub 3} (BZT) piezoelectric phase for synthesized composites were confirmed by XRD measurements. The lattice constant of piezomagnetic and piezoelectric phases increases with increase in composition of the substituent. The dielectric constant and dielectric loss tangent of the composites measured as a function of frequency in the range 10 Hz–1 MHz at room temperature are found to decrease rapidly in low frequency regime and remain constant in high frequency regime shows the dielectric dispersion behavior. The magnetic properties of the composites have been studied using M-H hysteresis loops to see the response of the magnetic field on the NMFO phase in the composites. The saturation magnetization increases with increase in the mole% of piezomagnetic phase in the composites. The ME voltage coefficient measured as a function of the applied DC magnetic field; shows maximum value (8.622 mV cm{sup −1} Oe) for (50%)NMFO + (50%)BZT bulk composites. The addition of NMFO and BZT enhances the ME properties of the composites.

  2. Synthesis of a magnetic composite resin and its cobalt removal characteristics in aqueous solution

    International Nuclear Information System (INIS)

    Kim, Young Kyun; Lee, Kun Jai

    2001-01-01

    A series of stepwise procedures to prepare a new organic-inorganic composite magnetic resin with phenolsulphonic-formaldehyde and freshly formed iron ferrite was established, based upon wet-and-neutralization method for synthesizing iron ferrite and pearl-polymerization method for synthesizing rigid bead-type composite resin. The ion exchange and sorption characteristics of the composite resin prepared by the above method at various conditions were experimentally disclosed. The composite resin prepared shows stably high removal efficiency to Co(II) species in aqueous solution in a wide range of solution pH. The overall isotherm is qualitatively explained by the generalized adsorption isotherm concept proposed by McKinley. The standard enthalpy change derived from van't Hoff equation conforms to the typical range for chemisorption or ion exchange. The selectivity of the PSF-F (phenolsulphonic formaldehyde-iron ferrite) composite resin to Co(II) species and other competing chemicals (i.e. Na 2 EDTA, Ca(II) and Na) was compared. It is anticipated that the composite resin can also be used for column-operation with process-control by applying external magnetic field, since the rigid bead-type composite resin shows magnetic-susceptibility due to its paramagnetic inorganic constituent (i.e. iron ferrite). (author)

  3. Interfacial effect on physical properties of composite media: Interfacial volume fraction with non-spherical hard-core-soft-shell-structured particles.

    Science.gov (United States)

    Xu, Wenxiang; Duan, Qinglin; Ma, Huaifa; Chen, Wen; Chen, Huisu

    2015-11-02

    Interfaces are known to be crucial in a variety of fields and the interfacial volume fraction dramatically affects physical properties of composite media. However, it is an open problem with great significance how to determine the interfacial property in composite media with inclusions of complex geometry. By the stereological theory and the nearest-surface distribution functions, we first propose a theoretical framework to symmetrically present the interfacial volume fraction. In order to verify the interesting generalization, we simulate three-phase composite media by employing hard-core-soft-shell structures composed of hard mono-/polydisperse non-spherical particles, soft interfaces, and matrix. We numerically derive the interfacial volume fraction by a Monte Carlo integration scheme. With the theoretical and numerical results, we find that the interfacial volume fraction is strongly dependent on the so-called geometric size factor and sphericity characterizing the geometric shape in spite of anisotropic particle types. As a significant interfacial property, the present theoretical contribution can be further drawn into predicting the effective transport properties of composite materials.

  4. Compositional optimization for nanocrystalline hard magnetic MRE–Fe–B–Zr alloys via modifying RE and B contents

    Energy Technology Data Exchange (ETDEWEB)

    Qian, D.Y.; Hussain, M.; Zheng, Z.G.; Zhong, X.C. [School of Materials Science and Engineering, South China University of Technology, Guangzhou 510640 (China); Gao, X.X. [State Key Laboratory for Advanced Metals and Materials, University of Science and Technology Beijing, Beijing 100083 (China); Liu, Z.W., E-mail: zwliu@scut.edu.cn [School of Materials Science and Engineering, South China University of Technology, Guangzhou 510640 (China); State Key Laboratory for Advanced Metals and Materials, University of Science and Technology Beijing, Beijing 100083 (China)

    2015-06-15

    To reduce the rare earth content and maintain good magnetic properties for NdFeB based alloys, the effects of RE and B contents on the micro-structure and magnetic properties of nanocrystalline MRE{sub 11−y}Fe{sub 79.5}B{sub 8+y}Zr{sub 1.5} (MRE=Nd{sub 0.8}(Dy{sub 0.5}Y{sub 0.5}){sub 0.2}, y=0–3) alloys have been investigated. Increasing B concentration leads to the appearance and increase of soft magnetic Fe{sub 3}B phase and reduced grain size. With decreasing MRE and increasing B concentrations, the coercivity decreased from 1159.8 kA/m for y=0 to 619.0 kA/m for y=3. The saturation magnetization and remanence increased with B content until y=2 then decreases. The B content also has effects on the exchange coupling, microstructure and thermal stability. While comparing MRE{sub 10}Fe{sub 82.5}B{sub 6}Zr{sub 1.5} alloy with MRE{sub 11−y}Fe{sub 79.5}B{sub 8+y}Zr{sub 1.5} (y=1 and 2) alloys, the alloy with 9 at% MRE can achieve similar magnetic properties as that with 10 at% MRE. The magnetic properties with coercivity of 792.2 kA/m, (BH){sub max} of 128 kJ/m{sup 3} and good thermal stability have been obtained for MRE{sub 9}Fe{sub 79.5}B{sub 10}Zr{sub 1.5} alloy. - Highlights: • Nanocomposite NdFeB composition is optimized to reduce RE from 10 to 9 at.%. • Increasing B content benefits microstructure, exchange coupling, thermal stability. • Alloy with 9% RE has H{sub c}=792kA/m, (BH){sub max}=128kJ/m{sup 3} and low temperature coefficients.

  5. Background Information: Magnetars, Soft Gamma-Ray Repeaters and the Most Powerful Magnetic Fields in the Universe

    Science.gov (United States)

    1998-08-01

    Near the end of its life, a star more massive than our Sun finds itself no longer able to support its own weight from the crush of gravity and so it collapses, producing an expanding shock wave that sweeps through the surrounding gas, creating what is called a supernova remnant. All that remains of the original star is a dense, compact object known as a neutron star. Magnetars are the latest addition to the "zoo" of neutron stars and they are truly exotic beasts with magnetic fields hundreds of millions of times stronger than have ever been seen on Earth. The story which led to the prediction of magnetars and then to their discovery is given elsewhere. Here we will focus on the other part of the story, the supernova remnants born at the same time as magnetars and the diffuse emission produced by the energetic outpourings of the magnetars. All four of the soft gamma-ray repeaters that we currently know are located in or near a supernova remnant. It was this discovery that led astronomers to determine that soft gamma-ray repeaters were in our Galaxy and the nearby galaxy known as the Large Magellanic Cloud. Through the study of these supernova remnants, astronomers were able to infer that soft gamma-ray repeaters were solitary young neutron stars speeding away from their birthplace at 3 million miles per hour. Theories predict that the same process which can produce the fantastic bursts of hard X-ray emission that give soft gamma-ray repeaters their name, can also accelerate particles (electrons, protons, etc) to speeds approaching the speed of light. As the saying goes, "where there's smoke there's fire" and this case is no exception. Most of the energy released by the burst event is carried away by these high energy particles and not the gamma-ray burst itself. As the particles spiral in the surrounding magnetic field, they too emit radiation, creating extended nebulae called "plerions". Provided there is some way to confine the outflow, these plerions act as "wind

  6. Rubber Composites Based on Polar Elastomers with Incorporated Modified and Unmodified Magnetic Filler

    Directory of Open Access Journals (Sweden)

    Ján Kruželák

    2016-01-01

    Full Text Available Rubber magnetic composites were prepared by incorporation of unmodified and surface modified strontium ferrite into rubber matrices based on NBR and NBR/PVC. Strontium ferrite was dosed to the rubber matrices in concentration scale ranging from 0 to 100 phr. The main goal was to investigate the influence of the type of ferrite on the curing process, physical-mechanical and magnetic properties of composites. The mutual interactions between the filler and rubber matrices were investigated by determination of cross-link density and SEM analysis. The incorporation of magnetic fillers leads to the increase of cross-link density and remanent magnetic induction of composites. Moreover, the improvement of physical-mechanical properties was achieved in dependence on the content of magnetic fillers. Surface modification of ferrite contributed to the enhancement of adhesion on the interphase filler-rubber. It can be stated that ferrite exhibits reinforcing effect in the composite materials and this reinforcing behavior was emphasized with the increase in polarity of the rubber matrix.

  7. Thermal Analysis of NR Composite with MWCNTs Aligned in a Magnetic Field

    Directory of Open Access Journals (Sweden)

    Jin Xu

    2015-01-01

    Full Text Available We got the aligned carbon tube in the rubber matrix through magnetic field. TEM shows that Fe3O4 is symmetrically coated on the outer surface of MWCNTs. Diffraction peaks corresponding to Fe3O4 cubic crystal also appeared in the X-ray diffraction spectra. Thermal conductivity of composites increases by filling the appropriate content of carbon tube. If the magnetic field is larger and the direction time is longer, a greater thermal conductivity of composites can be obtained.

  8. In-situ synthesis of magnetic iron-oxide nanoparticle-nanofibre composites using electrospinning

    International Nuclear Information System (INIS)

    Burke, Luke; Mortimer, Chris J.; Curtis, Daniel J.; Lewis, Aled R.; Williams, Rhodri; Hawkins, Karl; Maffeis, Thierry G.G.; Wright, Chris J.

    2017-01-01

    We demonstrate a facile, one-step process to form polymer scaffolds composed of magnetic iron oxide nanoparticles (MNPs) contained within electrospun nano- and micro-fibres of two biocompatible polymers, Poly(ethylene oxide) (PEO) and Poly(vinyl pyrrolidone) (PVP). This was achieved with both needle and free-surface electrospinning systems demonstrating the scalability of the composite fibre manufacture; a 228 fold increase in fibre fabrication was observed for the free-surface system. In all cases the nanoparticle-nanofibre composite scaffolds displayed morphological properties as good as or better than those previously described and fabricated using complex multi-stage techniques. Fibres produced had an average diameter (Needle-spun: 125 ± 18 nm (PEO) and 1.58 ± 0.28 μm (PVP); Free-surface electrospun: 155 ± 31 nm (PEO)) similar to that reported previously, were smooth with no bead defects. Nanoparticle-nanofibre composites were characterised using scanning electron microscopy (SEM), energy dispersive X-ray spectroscopy (EDX), dynamic light scattering (DLS) (Nanoparticle average diameter ranging from 8 ± 3 nm to 27 ± 5 nm), XRD (Phase of iron oxide nanoparticles identified as magnetite) and nuclear magnetic resonance relaxation measurements (NMR) (T1/T2: 32.44 for PEO fibres containing MNPs) were used to verify the magnetic behaviour of MNPs. This study represents a significant step forward for production rates of magnetic nanoparticle-nanofibre composite scaffolds by the electrospinning technique. - Graphical abstract: We present a novel facile, one-step process for the in-situ synthesis of magnetic iron oxide nanoparticle-nanofibre composites using both needle and free-surface electrospinning. This is a significant step forward for production rates of magnetic nanoparticle-nanofibre scaffolds both in terms of fibre and nanoparticle production. - Highlights: • We present a novel process for the in-situ synthesis of magnetic iron oxide nanoparticle

  9. In-situ synthesis of magnetic iron-oxide nanoparticle-nanofibre composites using electrospinning

    Energy Technology Data Exchange (ETDEWEB)

    Burke, Luke; Mortimer, Chris J. [Biomaterials, Biofouling and Biofilms Engineering Laboratory (B3EL), Systems and Process Engineering Centre, College of Engineering, Swansea University, Fabian Way, Swansea SA1 8EN (United Kingdom); Systems and Process Engineering Centre, College of Engineering, Swansea University, Fabian Way, Swansea SA1 8EN (United Kingdom); Curtis, Daniel J.; Lewis, Aled R.; Williams, Rhodri [Systems and Process Engineering Centre, College of Engineering, Swansea University, Fabian Way, Swansea SA1 8EN (United Kingdom); Hawkins, Karl [Centre for NanoHealth (CNH), Swansea University, Singleton Park, Swansea SA2 8PP (United Kingdom); Maffeis, Thierry G.G. [Systems and Process Engineering Centre, College of Engineering, Swansea University, Fabian Way, Swansea SA1 8EN (United Kingdom); Wright, Chris J., E-mail: c.wright@swansea.ac.uk [Biomaterials, Biofouling and Biofilms Engineering Laboratory (B3EL), Systems and Process Engineering Centre, College of Engineering, Swansea University, Fabian Way, Swansea SA1 8EN (United Kingdom); Systems and Process Engineering Centre, College of Engineering, Swansea University, Fabian Way, Swansea SA1 8EN (United Kingdom); Centre for NanoHealth (CNH), Swansea University, Singleton Park, Swansea SA2 8PP (United Kingdom)

    2017-01-01

    We demonstrate a facile, one-step process to form polymer scaffolds composed of magnetic iron oxide nanoparticles (MNPs) contained within electrospun nano- and micro-fibres of two biocompatible polymers, Poly(ethylene oxide) (PEO) and Poly(vinyl pyrrolidone) (PVP). This was achieved with both needle and free-surface electrospinning systems demonstrating the scalability of the composite fibre manufacture; a 228 fold increase in fibre fabrication was observed for the free-surface system. In all cases the nanoparticle-nanofibre composite scaffolds displayed morphological properties as good as or better than those previously described and fabricated using complex multi-stage techniques. Fibres produced had an average diameter (Needle-spun: 125 ± 18 nm (PEO) and 1.58 ± 0.28 μm (PVP); Free-surface electrospun: 155 ± 31 nm (PEO)) similar to that reported previously, were smooth with no bead defects. Nanoparticle-nanofibre composites were characterised using scanning electron microscopy (SEM), energy dispersive X-ray spectroscopy (EDX), dynamic light scattering (DLS) (Nanoparticle average diameter ranging from 8 ± 3 nm to 27 ± 5 nm), XRD (Phase of iron oxide nanoparticles identified as magnetite) and nuclear magnetic resonance relaxation measurements (NMR) (T1/T2: 32.44 for PEO fibres containing MNPs) were used to verify the magnetic behaviour of MNPs. This study represents a significant step forward for production rates of magnetic nanoparticle-nanofibre composite scaffolds by the electrospinning technique. - Graphical abstract: We present a novel facile, one-step process for the in-situ synthesis of magnetic iron oxide nanoparticle-nanofibre composites using both needle and free-surface electrospinning. This is a significant step forward for production rates of magnetic nanoparticle-nanofibre scaffolds both in terms of fibre and nanoparticle production. - Highlights: • We present a novel process for the in-situ synthesis of magnetic iron oxide nanoparticle

  10. High damping properties of magnetic particles doped rubber composites at wide frequency

    Energy Technology Data Exchange (ETDEWEB)

    Tian, Ye, E-mail: schtiany@163.com [Research Center for Engineering Technology of Polymeric Composites of Shanxi Province, North University of China, Taiyuan 030051 (China); College of Material Science and Engineering, North University of China, Taiyuan 030051 (China); Liu, Yaqing, E-mail: lyq@nuc.edu.cn [Research Center for Engineering Technology of Polymeric Composites of Shanxi Province, North University of China, Taiyuan 030051 (China); College of Material Science and Engineering, North University of China, Taiyuan 030051 (China); He, Minhong; Zhao, Guizhe; Sun, Youyi [Research Center for Engineering Technology of Polymeric Composites of Shanxi Province, North University of China, Taiyuan 030051 (China); College of Material Science and Engineering, North University of China, Taiyuan 030051 (China)

    2013-05-15

    Highlights: ► A new kind of permanent magnetic rubber was prepared. ► The microstructure and magnetic properties were investigated. ► The mechanical and damping properties were discussed. ► The new material is expected to be an isolator material to a changed frequency. - Abstract: A new kind of rubber composite was prepared by doping SrFe{sub 12}O{sub 19} nanoparticles coated with silane coupling agents (Si-69) into nitrile butadiene rubber (NBR) matrix, which was characterized by the scanning electron microscopy and X-ray spectroscopy. The results showed that the SrFe{sub 12}O{sub 19} nanoparticles were well dispersed in rubber matrix. Furthermore, the mechanical and magnetic properties of the rubber composites were investigated, in which the high tensile strength (15.8 MPa) and high saturation magnetization (22.9 emu/g) were observed. What is more, the high loss factor of the rubber composites was also obtained in a wide frequency range (0–100 Hz) at high loading (80 phr). The result is attributed to that the permanent magnetic field in rubber nanocomposites can absorb shock energy. These results indicate that the new kind of permanent magnetic rubber is expected to be a smart isolator material, in which the isolator will be able to adapt to a changed frequency.

  11. Effects of acute exposure to magnetic field on ionic composition of frog sciatic nerve

    International Nuclear Information System (INIS)

    Salem, A.; Hafedh, A.; Mohsen, S.

    2004-01-01

    Objective: To evaluate the possible interaction between magnetic field and cadmium on ionic composition of frog sciatic nerve. Design: The combined effect of magnetic field and cadmium (1.5mg/kg; in lymphatic sac) were studied in frog sciatic nerves (Rana Esculenta). Sciatic nerve samples were extracted, weighed and mixed in bidistilled water in order to analyze by inductively coupled plasma (ICP) ionic composition. Setting: Frogs (Rana Esculenta) were reared in swimming-pool (Faculte des Sciences de Bizerte, Tunisia). Frogs were cared for under the Tunisian Code of Practice for the Care and Use of Animals for Scientific purpose and the Experimental Protocols were approved by the Ethics Committee. Subjects: Treated and control groups (n=6) weighing 50-100g at the time of experiments were housed in the same condition three weeks before the beginning of the experiments. Results: Acute exposure to magnetic field increased significantly the calcium (+298%, p<0.05) and iron (+50%, p<0.05) contents of frog sciatic nerve, whereas magnesium and copper contents remained unchanged. The association between magnetic field and cadmium, induced marked increase of calcium (+360%, p<0.05), whereas magnesium content remained stable. Conclusions: Magnetic field exposure alters the ionic composition in the frog sciatic nerve, especially calcium and iron. Magnetic field magnifies the effect of cadmium on calcium homeostasis. (author)

  12. Energy dissipation of composite multifilamentary superconductors for high-current ramp-field magnet applications

    International Nuclear Information System (INIS)

    Gung, C.Y.

    1993-01-01

    Energy dissipation, which is also called AC loss, of a composite multifilamentary superconducting wire is one of the most fundamental concerns in building a stable superconducting magnet. Characterization and reduction of AC losses are especially important in designing a superconducting magnet for generating transient magnetic fields. The goal of this thesis is to improve the understanding of AC-loss properties of superconducting wires developed for high-current ramp-field magnet applications. The major tasks include: (1) building an advanced AC-loss measurement system, (2) measuring AC losses of superconducting wires under simulated pulse magnet operations, (3) developing an analytical model for explaining the new AC-loss properties found in the experiment, and (4) developing a computational methodology for comparing AC losses of a superconducting wire with those of a cable for a superconducting pulse magnet. A new experimental system using an isothermal calorimetric method was designed and constructed to measure the absolute AC losses in a composite superconductor. This unique experimental setup is capable of measuring AC losses of a brittle Nb 3 Sn wire carrying high AC current in-phase with a large-amplitude pulse magnetic field. Improvements of the accuracy and the efficiency of this method are discussed. Three different types of composite wire have been measured: a Nb 3 Sn modified jelly-roll (MJR) internal-tin wire used in a prototype ohmic heating coil, a Nb 3 Sn internal-tin wire developed for a fusion reactor ohmic heating coil, and a NbTi wire developed for the magnets in a particle accelerator. The cross sectional constructions of these wires represent typical commercial wires manufactured for pulse magnet applications

  13. Structural and Magnetic Properties of Type-M Barium Ferrite - Thermoplastic Natural Rubber Nano composites

    International Nuclear Information System (INIS)

    Nurhidayaty Mokhtar

    2012-01-01

    Structural and magnetic properties of type-M barium ferrite (BaFe 12 O 19 ) nanoparticles (∼ 20 nm) embedded in non-magnetic thermoplastic natural rubber (TPNR) matrices were investigated. The TPNR matrices were prepared from high density polyethylene (HDPE) and natural rubber (NR) in the weight ratios of 80:20 and 60:40, respectively, with 10 wt % of NR in the form of liquid natural rubber (LNR) which act as a comparabilities. BaFe 12 O 19 - filled nano composites with 2 - 12 wt % BaFe 12 O 19 ferrite were prepared using a melt- blending technique. Magnetic hysteresis was measured using a vibrating sample magnetometer (VSM) in a maximum field of 10 kOe at room temperature (25 degree Celsius). The saturation magnetisation (MS), remanence (MR) and coercivity (Hc) were derived from the hysteresis loops. The results show that the structural and magnetic properties of nano composites depend on both the ferrite content and the composition of the natural rubber or plastic in the nano composites. All the nano composites exhibit an exchange bias-like phenomenon resulting from the exchange coupling of spins at the interface between the core ferrimagnetic region and the disordered surface region of the nanoparticles. (author)

  14. Nuclear magnetic resonance applied to the study of polymeric nano composites

    International Nuclear Information System (INIS)

    Tavares, Maria Ines Bruno

    2011-01-01

    Polymers and nanoparticles based nano composites were prepared by intercalation by solution. The obtained nano composites were characterized mainly by the nuclear magnetic spectroscopy (NMR), applying the analysis of carbon-13 (polymeric matrix), silicon-29 (nanoparticle), and by determination of spin-lattice relaxation of the hydrogen nucleus (T 1 H) (polymeric matrix). The NMR have presented a promising technique in the characterization of the nano charge dispersion in the studied polymeric matrixes.

  15. A preliminary study of patient-specific mechanical properties of diabetic and healthy plantar soft tissue from gated magnetic resonance imaging.

    Science.gov (United States)

    Williams, Evan D; Stebbins, Michael J; Cavanagh, Peter R; Haynor, David R; Chu, Baocheng; Fassbind, Michael J; Isvilanonda, Vara; Ledoux, William R

    2017-07-01

    Foot loading rate, load magnitude, and the presence of diseases such as diabetes can all affect the mechanical properties of the plantar soft tissues of the human foot. The hydraulic plantar soft tissue reducer instrument was designed to gain insight into which variables are the most significant in determining these properties. It was used with gated magnetic resonance imaging to capture three-dimensional images of feet under dynamic loading conditions. Custom electronics controlled by LabVIEW software simultaneously recorded system pressure, which was then translated to applied force values based on calibration curves. Data were collected for two subjects, one without diabetes (Subject A) and one with diabetes (Subject B). For a 0.2-Hz loading rate, and strains 0.16, 0.18, 0.20, and 0.22, Subject A's average tangential heel pad stiffness was 10 N/mm and Subject B's was 24 N/mm. Maximum test loads were approximately 200 N. Loading rate and load magnitude limitations (both were lower than physiologic values) will continue to be addressed in the next version of the instrument. However, the current hydraulic plantar soft tissue reducer did produce a data set for healthy versus diabetic tissue stiffness that agrees with previous trends. These data are also being used to improve finite element analysis models of the foot as part of a related project.

  16. Silver nanowire/polymer composite soft conductive film fabricated by large-area compatible coating for flexible pressure sensor array

    Science.gov (United States)

    Chen, Sujie; Li, Siying; Peng, Sai; Huang, Yukun; Zhao, Jiaqing; Tang, Wei; Guo, Xiaojun

    2018-01-01

    Soft conductive films composed of a silver nanowire (AgNW) network, a neutral-pH PEDOT:PSS over-coating layer and a polydimethylsiloxane (PDMS) elastomer substrate are fabricated by large area compatible coating processes. The neutral-pH PEDOT:PSS layer is shown to be able to significantly improve the conductivity, stretchability and air stability of the conductive films. The soft conductive films are patterned using a simple maskless patterning approach to fabricate an 8 × 8 flexible pressure sensor array. It is shown that such soft conductive films can help to improve the sensitivity and reduce the signal crosstalk over the pressure sensor array. Project supported by the Science and Technology Commission of Shanghai Municipality (No. 16JC1400603).

  17. Electromagnetic wave absorption properties of composites with micro-sized magnetic particles dispersed in amorphous carbon

    Energy Technology Data Exchange (ETDEWEB)

    Li, Bin Peng [Research Center of Carbon Fiber, Key Laboratory for Liquid–Solid Structural Evolution and Processing of Materials of Ministry of Education, Shandong University, Jinan 250061 (China); Tianjin Binhai New Area Finance Bureau, Tianjin 300450 (China); Wang, Cheng Guo, E-mail: sduwangchg@gmail.com [Research Center of Carbon Fiber, Key Laboratory for Liquid–Solid Structural Evolution and Processing of Materials of Ministry of Education, Shandong University, Jinan 250061 (China); Wang, Wen [Norinco Group China North Material Science and Engineering Technology Group Corporation, Jinan 250031 (China); Yu, Mei Jie; Gao, Rui; Chen, Yang; Xiang Wang, Yan [Research Center of Carbon Fiber, Key Laboratory for Liquid–Solid Structural Evolution and Processing of Materials of Ministry of Education, Shandong University, Jinan 250061 (China)

    2014-09-01

    Composites with micro-sized magnetic particles dispersed in amorphous carbon were fabricated conveniently and economically by carbonizing polyacrylonitrile (PAN) fibers mixed with micro-sized iron particles under different temperatures. The composites were characterized by X-ray diffraction (XRD) and scanning electric microscope (SEM). The electromagnetic (EM) properties were measured by a vector network analyzer in the frequency range of 2–18 GHz based on which analog computations of EM wave absorption properties were carried out. The influences of temperature on phase composition and EM wave absorption properties were also investigated, indicating that the composites had good electromagnetic absorption properties with both electrical loss and magnetic loss. Effective reflection loss (RL<−10 dB) was observed in a large frequency range of 7.5–18 GHz with the absorber thickness of 2.0–3.0 mm for the paraffin samples with composite powders heated up to 750 °C and the minimum absorption peak around −40 dB appeared at approximately 10 GHz with matching thickness of 2.0 mm for the paraffin sample with composite powders heated up to 800 °C. - Highlights: • High-performance electromagnetic wave absorption materials were fabricated conveniently and economically. • The materials are composites with micro-sized magnetic particles dispersed in porous amorphous carbon. • The influences of temperature on phase composition and electromagnetic wave absorption properties were investigated. • The composites heated up to 750 °C and 800 °C had good electromagnetic wave absorption property.

  18. ROSAT EUV and soft X-ray studies of atmospheric composition and structure in G191-B2B

    Science.gov (United States)

    Barstow, M. A.; Fleming, T. A.; Finley, D. S.; Koester, D.; Diamond, C. J.

    1993-01-01

    Previous studies of the hot DA white dwarf GI91-B2B have been unable to determine whether the observed soft X-ray and EUV opacity arises from a stratified hydrogen and helium atmosphere or from the presence of trace metals in the photosphere. New EUV and soft X-ray photometry of this star, made with the ROSAT observatory, when analyzed in conjunction with the earlier data, shows that the stratified models cannot account for the observed fluxes. Consequently, we conclude that trace metals must be a substantial source of opacity in the photosphere of G191-B2B.

  19. Magnetic proximity effects in nanoparticle composite systems and macrocrystals

    Energy Technology Data Exchange (ETDEWEB)

    Wilbs, Genevieve

    2017-07-01

    Assemblies of magnetic nanoparticles are of major interest for future applications e.g. in spintronic devices, high density data storage systems or biomedical applications. The reason is not only the obvious miniaturization, but also their novel properties emerging only at the nanoscale. Hence, arranging nanoparticles like atoms in a crystal enables the fabrication of a new class of materials. To gain in-depth understanding of these systems, it is necessary to investigate them on all length scales. The present work provides a novel and extensive contribution to the understanding of the selfassembly of iron oxide nanoparticle superstructures and their influence on polarizable matrix materials. Through the investigation of the samples at all stages of preparation, a comprehensive picture of the unique phenomena observed at the end is derived. For this purpose, oleic acid coated iron oxide nanoparticles were deposited on silicon substrates by spincoating to manufacture two-dimensional arrangements. Hereby, the influence of several parameters has been investigated and optimized. Afterwards, the organic surfactant shell was removed by oxygen plasma treatment. This process has been studied in detail, because it initiates a phase transformation that significantly influences the magnetic properties of the system (e.g. by reducing the blocking temperature). Thin palladium or platinum films were then respectively deposited to create a matrix material. Aside from magnetometry measurements, first order reversal curves were obtained in cooperation with the Max-Planck-Institute for Intelligent Systems, both revealing that the matrix materials significantly influence the inter-particle interaction and vice versa. However, only by performing X-ray magnetic circular dichroism experiments at the Advanced Photon Source of the Argonne National Laboratory, it could be evidenced unambiguously that platinum can be polarized by an oxide. Additionally, these systems were investigated

  20. Magnetic proximity effects in nanoparticle composite systems and macrocrystals

    International Nuclear Information System (INIS)

    Wilbs, Genevieve

    2017-01-01

    Assemblies of magnetic nanoparticles are of major interest for future applications e.g. in spintronic devices, high density data storage systems or biomedical applications. The reason is not only the obvious miniaturization, but also their novel properties emerging only at the nanoscale. Hence, arranging nanoparticles like atoms in a crystal enables the fabrication of a new class of materials. To gain in-depth understanding of these systems, it is necessary to investigate them on all length scales. The present work provides a novel and extensive contribution to the understanding of the selfassembly of iron oxide nanoparticle superstructures and their influence on polarizable matrix materials. Through the investigation of the samples at all stages of preparation, a comprehensive picture of the unique phenomena observed at the end is derived. For this purpose, oleic acid coated iron oxide nanoparticles were deposited on silicon substrates by spincoating to manufacture two-dimensional arrangements. Hereby, the influence of several parameters has been investigated and optimized. Afterwards, the organic surfactant shell was removed by oxygen plasma treatment. This process has been studied in detail, because it initiates a phase transformation that significantly influences the magnetic properties of the system (e.g. by reducing the blocking temperature). Thin palladium or platinum films were then respectively deposited to create a matrix material. Aside from magnetometry measurements, first order reversal curves were obtained in cooperation with the Max-Planck-Institute for Intelligent Systems, both revealing that the matrix materials significantly influence the inter-particle interaction and vice versa. However, only by performing X-ray magnetic circular dichroism experiments at the Advanced Photon Source of the Argonne National Laboratory, it could be evidenced unambiguously that platinum can be polarized by an oxide. Additionally, these systems were investigated

  1. Methodology for repeated load analysis of composite structures with embedded magnetic microwires

    Directory of Open Access Journals (Sweden)

    K. Semrád

    2017-01-01

    Full Text Available The article processes issue of strength of cyclically loaded composite structures with the possibility of contactless stress measuring inside a material. For this purpose a contactless tensile stress sensor using improved induction principle based on the magnetic microwires embedded in the composite structure has been developed. The methodology based on the E-N approach was applied for the analysis of the repeated load of the wing hinge connection, including finite element method (FEM fatigue strength analysis. The results proved that composites in comparison with the metal structures offer significant weight reduction of the small aircraft construction, whereas the required strength, stability and lifetime of the components are remained.

  2. Bioinspired Flexible and Highly Responsive Dual-Mode Strain/Magnetism Composite Sensor.

    Science.gov (United States)

    Huang, Pei; Li, Yuan-Qing; Yu, Xiao-Guang; Zhu, Wei-Bin; Nie, Shu-Yan; Zhang, Hao; Liu, Jin-Rui; Hu, Ning; Fu, Shao-Yun

    2018-04-04

    The mimicry of human skin to detect both oncoming and physical-contacting object is of great importance in the fields of manufacturing, artificial robots and vehicles, etc. Herein, a novel bioinspired flexible and highly responsive dual-mode strain/magnetism composite sensor, which works via both contact and contactless modes, is first fabricated by incorporating Fe 3 O 4 /silicone system into a carbon fiber aerogel (CFA). The distance dependence of magnetic field endorses the CFA/Fe 3 O 4 /silicone composite possible for spatial sensing due to the introduction of Fe 3 O 4 magnetic nanoparticles. As a result, the as-prepared flexible sensor exhibits precise and real-time response not only to direct-contact compression as usual but also to contactless magnetic field in a wide frequency range from 0.1 to 10 Hz, achieving the maximum variance of 68% and 86% in relative electrical resistance, respectively. The contact and contactless sensing modes of the strain/magnetism sensor are clearly demonstrated by recording the speeds of bicycle riding and walking, respectively. Interestingly, this dual-mode composite sensor exhibits the capacity of identifying the contact and contactless state, which is the first report for flexible sensors. The current protocol is eco-friendly, facile, and thought-provoking for the fabrication of multifunctional sensors.

  3. Composite magnetic refrigerants for an Ericsson cycle: New method of selection using a numerical approach

    International Nuclear Information System (INIS)

    Smaieli, A.; Chahine, R.

    1997-01-01

    The efficient operation of an Ericsson cycle requires the magnetic entropy change (AS) be constant as a function of temperature. To realize this condition using composite materials, a numerical method has been developed to determine the optimum proportions of the components. The Gd x Er 1-x (x = 0.69, 0.90) alloys have been used to investigate the validity of the numerical method. The values of ΔS have been determined from experimental magnetization curves of these alloys, in the 0.1-9 T magnetic field and the 200-290 K range. The calculations have led to the mass ratio y = 0.56 for the composite (Gd 0.90 Er 0.10 ) y (Gd 0.69 Er 0.31 ) 1-y . The ΔS of this composite is fairly constant in the 225-280 K range. To confirm this result, the magnetization curves of the composite material have been determined experimentally, and the corresponding ΔS was compared with the one predicted numerically. A good agreement was found proving the method's ability to properly determine the required fractions of the refrigerant's constituent materials

  4. Magnetically responsive (nano) composites as perspective materials for environmental technology applications

    Czech Academy of Sciences Publication Activity Database

    Šafařík, Ivo; Šafaříková, Miroslava

    -, č. 0 (2010), s. 85-90 R&D Projects: GA MPO(CZ) 2A-1TP1/094; GA MŠk OC09052 Institutional research plan: CEZ:AV0Z60870520 Keywords : magnetically responsive materials * ( nano )biocomposites * environmental technology Subject RIV: JI - Composite Materials

  5. Nd composition dependence of microstructure and magnetic properties for gradient sputtered NdFeB films

    International Nuclear Information System (INIS)

    Li Shandong; Wang Dawei; Fang Jianglin; Duh, J.-G.; Wang Yinying; Wu Yizhi; Huang Junheng; Zheng Hongjun

    2008-01-01

    NdFeB films with Nd compositions varied from 13.34 to 24.30 at% were deposited by DC gradient sputtering using targets Nd 12.5 Fe 71.5 B 16 and Nd. The hard magnetic properties, grain growth direction and magnetic domain structures were dramatically influenced by Nd composition. The samples with intermediate Nd concentrations exhibited optimal magnetic properties and microstructures, such as large squareness ratio over 0.9, large energy product up to 174 kJ/m 3 , and vertical domain structure. However, the samples with higher and lower Nd compositions showed almost isotropic loops. (0 0 l) as main X-ray diffraction peaks in the optimal Nd composition region indicated most of Nd 2 Fe 14 B grains with c-axis perpendicular to the film plane, while NdFeB grains in other region are almost random growth. The good magnetic properties can be attributed to the vertical growth of Nd 2 Fe 14 B grains

  6. Nd composition dependence of microstructure and magnetic properties for gradient sputtered NdFeB films

    Energy Technology Data Exchange (ETDEWEB)

    Li Shandong [Department of Physics, Fujian Normal University, Fuzhou 350007 (China)], E-mail: dylsd007@yahoo.com.cn; Wang Dawei [Department of Physics, Fujian Normal University, Fuzhou 350007 (China); Fang Jianglin [Center for Materials Analysis, Nanjing University, Nanjing 210093 (China); Duh, J.-G. [Department of Materials Science and Engineering, National TsingHua Universtiy, Hsinchu, Taiwan (China); Wang Yinying; Wu Yizhi; Huang Junheng; Zheng Hongjun [Department of Physics, Fujian Normal University, Fuzhou 350007 (China)

    2008-08-15

    NdFeB films with Nd compositions varied from 13.34 to 24.30 at% were deposited by DC gradient sputtering using targets Nd{sub 12.5}Fe{sub 71.5}B{sub 16} and Nd. The hard magnetic properties, grain growth direction and magnetic domain structures were dramatically influenced by Nd composition. The samples with intermediate Nd concentrations exhibited optimal magnetic properties and microstructures, such as large squareness ratio over 0.9, large energy product up to 174 kJ/m{sup 3}, and vertical domain structure. However, the samples with higher and lower Nd compositions showed almost isotropic loops. (0 0 l) as main X-ray diffraction peaks in the optimal Nd composition region indicated most of Nd{sub 2}Fe{sub 14}B grains with c-axis perpendicular to the film plane, while NdFeB grains in other region are almost random growth. The good magnetic properties can be attributed to the vertical growth of Nd{sub 2}Fe{sub 14}B grains.

  7. Exterior Decay of Wood-Plastic Composite Boards: Characterization and Magnetic Resonance Imaging

    Science.gov (United States)

    Rebecca Ibach; Grace Sun; Marek Gnatowski; Jessie Glaeser; Mathew Leung; John Haight

    2016-01-01

    Magnetic resonance imaging (MRI) was used to evaluate free water content and distribution in wood-plastic composite (WPC) materials decayed during exterior exposure near Hilo, Hawaii. Two segments of the same board blend were selected from 6 commercial decking boards that had fungal fruiting bodies. One of the two board segments was exposed in sun, the other in shadow...

  8. Magnetic and electromagnetic properties of Pr doped strontium ferrite/polyaniline composite film

    Energy Technology Data Exchange (ETDEWEB)

    Huang, Ying; Li, Yuqing; Wang, Yan, E-mail: wangyan287580632@126.com

    2014-11-15

    This paper reported three acid (including hydrochloric acid HCl, p-toluenesulfonic acid PTS and D-camphor-10-acid CSA) doped SrPr{sub 0.2}Fe{sub 11.8}O{sub 19}/PANI composite film and the HCl–PANI film prepared by a sol–gel method and in-situ oxidative polymerization. The characteristics of the film phase structure, surface morphology, conductivity and magnetic and electromagnetic properties were studied by using XRD, XPS, FESEM, four-probe tester, VSM and Vector Network Analyzer. The resistivity of organic acid doped composite films is higher than that of the HCl doped one. The saturation and remanent magnetization of PTS and HCl doped composite films are greater than the CSA-doped one; however, the coercivity of the three acid doped composite films is basically 5546 Oe. The saturation magnetization, remanent magnetization and coercivity of SrPr{sub 0.2}Fe{sub 11.8}O{sub 19} film are greater than those of the SrPr{sub 0.2}Fe{sub 11.8}O{sub 19}–PANI composite film. In the frequency range of 8–12 GHz, the dielectric loss of HCl–PANI film is the maximum, and the dielectric loss of SrPr{sub 0.2}Fe{sub 11.8}O{sub 19} film is the minimum; the magnetic loss of the four films is in descending order as SrPr{sub 0.2}Fe{sub 11.8}O{sub 19} film, PrSrM/(HCl–PANI) composite film, PrSrM/(CSA–PANI) and HCl–PANI film. - Highlights: • Synthesizing three acid doped SrPr{sub 0.2}Fe{sub 11.8}O{sub 19}/PANI composite films. • By sol–gel method and in-situ oxidative polymerization. • With excellent magnetic and electromagnetic properties. • The particular coating structure of PANI and Sr-ferrite. • Great interest for magnetic material and microwave absorbers.

  9. Fabrication and temperature dependent magnetic properties of Ni–Cu–Co composite nanowires

    Energy Technology Data Exchange (ETDEWEB)

    Hussain, Muhammad [Nanomaterials Research Group, Physics Division PINSTECH, Islamabad 44000 (Pakistan); Khan, Maaz, E-mail: maaz@impcas.ac.cn [Nanomaterials Research Group, Physics Division PINSTECH, Islamabad 44000 (Pakistan); Sun, Hongyu [Beijing National Center for Electron Microscopy, Laboratory of Advanced Materials and The State Key Laboratory of New Ceramics and Fine Processing, Department of Materials Science and Engineering, Tsinghua University, Beijing 100084 (China); Nairan, Adeela [Centre for High Energy Physics, University of the Punjab, Lahore 54590 (Pakistan); Karim, Shafqat; Nisar, Amjad [Nanomaterials Research Group, Physics Division PINSTECH, Islamabad 44000 (Pakistan); Maqbool, M. [Department of Physics and Astronomy, Ball State University, Muncie, IN 47306 (United States); Ahmad, Mashkoor, E-mail: mashkoorahmad2003@yahoo.com [Nanomaterials Research Group, Physics Division PINSTECH, Islamabad 44000 (Pakistan)

    2015-10-15

    Ni–Cu–Co composite magnetic nanowires have been successfully synthesized by electrochemical deposition. Microstructural and compositional analyses were carried out using FESEM, TEM, HRTEM and XRD. Magnetic measurements were performed from in the temperature range 5–300 K. A strong diamagnetic contribution, which results from the polycarbonate template, was found to show s-shape behavior of the hysteresis loops of the nanowires. The coercivity of the samples was found to increase with the decreasing temperature following simple model of thermal activation of particle’s moment over the anisotropy barrier in the temperature range 50–300 K. Saturation magnetization was found to increase with decreasing temperature following the modified Bloch’s law at low temperatures.

  10. Fabrication and temperature dependent magnetic properties of Ni–Cu–Co composite nanowires

    International Nuclear Information System (INIS)

    Hussain, Muhammad; Khan, Maaz; Sun, Hongyu; Nairan, Adeela; Karim, Shafqat; Nisar, Amjad; Maqbool, M.; Ahmad, Mashkoor

    2015-01-01

    Ni–Cu–Co composite magnetic nanowires have been successfully synthesized by electrochemical deposition. Microstructural and compositional analyses were carried out using FESEM, TEM, HRTEM and XRD. Magnetic measurements were performed from in the temperature range 5–300 K. A strong diamagnetic contribution, which results from the polycarbonate template, was found to show s-shape behavior of the hysteresis loops of the nanowires. The coercivity of the samples was found to increase with the decreasing temperature following simple model of thermal activation of particle’s moment over the anisotropy barrier in the temperature range 50–300 K. Saturation magnetization was found to increase with decreasing temperature following the modified Bloch’s law at low temperatures

  11. Ferrimagnetic Tb-Fe Alloy Thin Films: Composition and Thickness Dependence of Magnetic Properties and All-Optical Switching

    Directory of Open Access Journals (Sweden)

    Birgit eHebler

    2016-02-01

    Full Text Available Ferrimagnetic rare earth - transition metal Tb-Fe alloy thin films exhibit a variety of different magnetic properties, which depends strongly on composition and temperature. In this study, first the influence of the film thickness (5 - 85 nm on the sample magnetic properties was investigated in a wide composition range between 15 at.% and 38 at.% of Tb. From our results, we find that the compensation point, remanent magnetization, and magnetic anisotropy of the Tb-Fe films depend not only on the composition but also on the thickness of the magnetic film up to a critical thickness of about 20-30 nm. Beyond this critical thickness, only slight changes in magnetic properties are observed. This behavior can be attributed to a growth-induced modification of the microstructure of the amorphous films, which affects the short range order. As a result, a more collinear alignment of the distributed magnetic moments of Tb along the out-of-plane direction with film thickness is obtained. This increasing contribution of the Tb sublattice magnetization to the total sample magnetization is equivalent to a sample becoming richer in Tb and can be referred to as an effective composition. Furthermore, the possibility of all-optical switching, where the magnetization orientation of Tb-Fe can be reversed solely by circularly polarized laser pulses, was analyzed for a broad range of compositions and film thicknesses and correlated to the underlying magnetic properties.

  12. Effect of Y addition on crystallization behavior and soft-magnetic properties of Fe{sub 78}Si{sub 9}B{sub 13} ribbons

    Energy Technology Data Exchange (ETDEWEB)

    Zhanwei, Liu; Dunbo, Yu, E-mail: yudb2008@126.com; Kuoshe, Li; Yang, Luo; Chao, Yuan; Zilong, Wang; Liang, Sun; Kuo, Men

    2017-08-15

    Highlights: • Thermal stability of Fe-Si-B amorphous alloy is enhanced by Y addition. • Y addition can improve soft magnetic properties of Fe-Si-B amorphous alloy. • Decomposition of metastable Fe{sub 3}B phase is related to Y content in Fe-Si-B matrix. - Abstract: A series of amorphous Fe-Si-B ribbons with various Y addition were prepared by melt-spinning. The effect of Y addition on crystallization behavior, thermal and magnetic properties was systematically investigated. With the increase of Y content, the initial crystallization temperature shifted to a higher temperature, indicating that the thermal stability of amorphous state in Fe-Si-B-Y ribbon is enhanced compared to that of Fe-Si-B alloy. Meanwhile, compared to the two exothermic peaks in the samples with lower Y content, a new exothermic peak was found in the ribbons with Y content higher than 1 at%, which corresponded to the decomposition of metastable Fe{sub 3}B phase. Among all the alloys, Fe{sub 76.5}Si{sub 9}B{sub 13}Y{sub 1.5} alloy exhibits optimized magnetic properties, with high saturation magnetization M{sub s} of 187 emu/g and low coercivity H{sub cJ} of 7.6 A/m.

  13. An X-ray Pulsar with a Superstrong Magnetic Field in the Soft Gamma-Ray Repeater SGR1806-20

    Science.gov (United States)

    Kouveliotou, C.; Dieters, S.; Strohmayer, T.; vanParadijs, J.; Fishman, G. J.; Meegan, C. A.; Hurley, K.; Kommers, J.; Smith, I.; Frail, D.; hide

    1998-01-01

    Soft gamma-ray repeaters (SGRs) emit multiple, brief (approximately O.1 s) intense outbursts of low-energy gamma-rays. They are extremely rare; three are known in our galaxy and one in the Large Magellanic Cloud. Two SGRs are associated with young supernova remnants (SNRs), and therefore most probably with neutron stars, but it remains a puzzle why SGRs are so different from 'normal' radio pulsars. Here we report the discovery of pulsations in the persistent X-ray flux of SGR1806-20, with a period of 7.47 s and a spindown rate of 2.6 x 10(exp -3) s/yr. We argue that the spindown is due to magnetic dipole emission and find that the pulsar age and (dipolar) magnetic field strength are approximately 1500 years and 8 x 10(exp 14) gauss, respectively. Our observations demonstrate the existence of 'magnetars', neutron stars with magnetic fields about 100 times stronger than those of radio pulsars, and support earlier suggestions that SGR bursts are caused by neutron-star 'crust-quakes' produced by magnetic stresses. The 'magnetar' birth rate is about one per millenium, a substantial fraction of that of radio pulsars. Thus our results may explain why some SNRs have no radio pulsars.

  14. Synthesis and characterization of magnetic Fe/CNTs composites with controllable Fe nanoparticle concentration

    International Nuclear Information System (INIS)

    Zhao Fan; Duan Hongyan; Wang Weigao; Wang Jun

    2012-01-01

    Fe/CNTs composites, with different concentrations of Fe nanoparticles (NPs) on carbon nanotube (CNT) surfaces, were successfully fabricated via a facile solvothermal method. The lengths of CNTs are up to 10 μm and the mean diameter of the Fe nanoparticles is about 25 nm. The structures, composition and magnetic properties of the Fe/CNTs were characterized by XRD, FTIR, FE-SEM, TEM and PPMS. We found that the concentrations of Fe nanoparticles depositing on the CNTs could be controlled by adjusting the initial mass ratio of ferrocene to CNTs. The Fe/CNTs composites display good ferromagnetic properties at room temperature, with a saturation magnetization of 125 emu/g-Fe and a coercivity of 276 Oe. The Curie temperature of the sample is about 1038 K, slightly lower than that (1043 K) of the bulk iron.

  15. Magnetic enhancement of ferroelectric polarization in a self-grown ferroelectric-ferromagnetic composite

    Science.gov (United States)

    Kumar, Amit; Narayan, Bastola; Pachat, Rohit; Ranjan, Rajeev

    2018-02-01

    Ferroelectric-ferromagnetic multiferroic composites are of great interest both from the scientific and technological standpoints. The extent of coupling between polarization and magnetization in such two-phase systems depends on how efficiently the magnetostrictive and electrostrictive/piezoelectric strain gets transferred from one phase to the other. This challenge is most profound in the easy to make 0-3 ferroelectric-ferromagnetic particulate composites. Here we report a self-grown ferroelectric-ferromagnetic 0-3 particulate composite through controlled spontaneous precipitation of ferrimagnetic barium hexaferrite phase (BaF e12O19 ) amid ferroelectric grains in the multiferroic alloy system BiFe O3-BaTi O3 . We demonstrate that a composite specimen exhibiting merely ˜1% hexaferrite phase exhibits ˜34% increase in saturation polarization in a dc magnetic field of ˜10 kOe. Using modified Rayleigh analysis of the polarization field loop in the subcoercive field region we argue that the substantial enhancement in the ferroelectric switching is associated with the reduction in the barrier heights of the pinning centers of the ferroelectric-ferroelastic domain walls in the stress field generated by magnetostriction in the hexaferrite grains when the magnetic field is turned on. Our study proves that controlled precipitation of the magnetic phase is a good strategy for synthesis of 0-3 ferroelectric-ferromagnetic particulate multiferroic composite as it not only helps in ensuring a good electrical insulating character of the composite, enabling it to sustain high enough electric field for ferroelectric switching, but also the factors associated with the spontaneity of the precipitation process ensure efficient transfer of the magnetostrictive strain/stress to the surrounding ferroelectric matrix making domain wall motion easy.

  16. RF and microwave noise suppression in a transmission line using Fe-Si-Al/Ni-Zn magnetic composite films

    International Nuclear Information System (INIS)

    Lee, J. W.; Hong, Y. K.; Kim, K.; Joo, J.; Yoon, Y. W.; Kim, S. W.; Kim, Y. B.; Kim, K. Y.

    2006-01-01

    Radio-frequency (RF) and microwave noise suppression by using magnetic composite films on a microstrip line (MSL) was studied in the frequency range from 50 MHz to 13.5 GHz. The MSL was composed of a Cu transmission line, dielectric materials, and a Cu substrate. The Fe-Si-Al/Ni-Zn magnetic composite films were placed on the MSL, and the reflection and the transmission characteristics were investigated. We observed that RF and microwave noise suppression caused by the Fe-Si-Al/Ni-Zn magnetic composite films varied with the concentration ratio of the sendust (Fe-Si-Al) and the Ni-Zn ferrite. The frequency dependence of the power loss due to the composite films on the MSL was measured and the power loss increased at higher frequencies with increasing concentration of the sendust in the composites. The electromagnetic interference shielding efficiencies of the magnetic composite films in the far-field region are also discussed.

  17. Core/shell fluorescent magnetic silica-coated composite nanoparticles for bioconjugation

    Science.gov (United States)

    He, Rong; You, Xiaogang; Shao, Jun; Gao, Feng; Pan, Bifeng; Cui, Daxiang

    2007-08-01

    A new class of highly fluorescent, photostable, and magnetic core/shell nanoparticles has been synthesized from a reverse microemulsion method. The obtained bifunctional nanocomposites were characterized by transmission electron microscopy (TEM), ultraviolet-visible (UV-vis) spectrometry, photoluminescence (PL) spectrometry, and fluorescence microscopy in a magnetic field. To further improve their biocompatibility, the silica-coated nanoparticles were functionalized with amino groups. The fluorescent magnetic composite nanoparticles (FMCNPs) had a typical diameter of 50 ± 5 nm and a saturation magnetization of 3.21 emu g-1 at room temperature, and exhibited strong excitonic photoluminescence. Through activation with glutaraldehyde, the FMCNPs were successfully conjugated with goat anti-mouse immunoglobin G (GM IgG), and the bioactivity and binding specificity of the as-prepared FMCNPs-GM IgG were confirmed via immunofluorescence assays, commonly used in bioanalysis. So they are potentially useful for many applications in biolabelling, imaging, drug targeting, bioseparation and bioassays.

  18. Core/shell fluorescent magnetic silica-coated composite nanoparticles for bioconjugation

    International Nuclear Information System (INIS)

    He Rong; You Xiaogang; Shao Jun; Gao Feng; Pan Bifeng; Cui Daxiang

    2007-01-01

    A new class of highly fluorescent, photostable, and magnetic core/shell nanoparticles has been synthesized from a reverse microemulsion method. The obtained bifunctional nanocomposites were characterized by transmission electron microscopy (TEM), ultraviolet-visible (UV-vis) spectrometry, photoluminescence (PL) spectrometry, and fluorescence microscopy in a magnetic field. To further improve their biocompatibility, the silica-coated nanoparticles were functionalized with amino groups. The fluorescent magnetic composite nanoparticles (FMCNPs) had a typical diameter of 50 ± 5 nm and a saturation magnetization of 3.21 emu g -1 at room temperature, and exhibited strong excitonic photoluminescence. Through activation with glutaraldehyde, the FMCNPs were successfully conjugated with goat anti-mouse immunoglobin G (GM IgG), and the bioactivity and binding specificity of the as-prepared FMCNPs-GM IgG were confirmed via immunofluorescence assays, commonly used in bioanalysis. So they are potentially useful for many applications in biolabelling, imaging, drug targeting, bioseparation and bioassays

  19. Pulsed field magnetization strategies and the field poles composition in a bulk-type superconducting motor

    Energy Technology Data Exchange (ETDEWEB)

    Huang, Zhen, E-mail: zhen.huang@sjtu.edu.cn [Academy of Information Technology and Electrical Engineering, Shanghai Jiao Tong University, 800 Dongchuan Road, Shanghai 200240 (China); Ruiz, H.S., E-mail: dr.harold.ruiz@le.ac.uk [Department of Engineering, University of Leicester, University Road, Leicester LE1 7RH (United Kingdom); Coombs, T.A., E-mail: tac1000@cam.ac.uk [Department of Engineering, University of Cambridge, 9 JJ Thomson Avenue, Cambridge CB3 0FA (United Kingdom)

    2017-03-15

    Highlights: • Different compositions of the magnetic poles have been obtained depending on the relative orientation of the magnetizing coil and the surfaces of the columns of bulks that conform a magnetic pole. • Two bidimensional models accounting for the electromagnetic response of the top and lateral cross sections of three columns of HTS bulks subjected to multiple pulsed magnetic fields have been created. • An extended PFM strategy has been proposed by considering the magnetization of at least three successive columns of HTS bulks per pole. In the extended PFM strategy the area of each one of the poles can be seen increased by a factor of 200%-400% - Abstract: High temperature superconducting (HTS) bulks offer the potential of trapping and maintaining much higher magnetic loading level compared with the conventional permanent magnets used in rotary machines, although the effective magnetization of multiple HTS bulks with different relative orientations over the surface of cylindrical rotors creates new challenges. In this paper, we present the design and numerical validation of the Pulse Field Magnetization (PFM) strategy considered for the magnetization of the four-pole synchronous fully superconducting motor developed at the University of Cambridge. In a first instance, singular columns of up to five HTS bulks aligned over the height of the rotor were subjected to up to three magnetic pulses of 1.5 T peak, and the experimental results have been simulated by considering the electrical and thermal properties of the system in a 2D approach. The entire active surface of the rotor is covered by HTS bulks of approximately the same dimensions, resulting in an uneven distribution of pole areas with at least one of the poles formed by up to 3 columns of magnetized bulks, with relatively the same peaks of trapped magnetic field. Thus, in order to effectively use the entire area of the superconducting rotor, multiple pulsed fields per column have been applied

  20. Pulsed field magnetization strategies and the field poles composition in a bulk-type superconducting motor

    International Nuclear Information System (INIS)

    Huang, Zhen; Ruiz, H.S.; Coombs, T.A.

    2017-01-01

    Highlights: • Different compositions of the magnetic poles have been obtained depending on the relative orientation of the magnetizing coil and the surfaces of the columns of bulks that conform a magnetic pole. • Two bidimensional models accounting for the electromagnetic response of the top and lateral cross sections of three columns of HTS bulks subjected to multiple pulsed magnetic fields have been created. • An extended PFM strategy has been proposed by considering the magnetization of at least three successive columns of HTS bulks per pole. In the extended PFM strategy the area of each one of the poles can be seen increased by a factor of 200%-400% - Abstract: High temperature superconducting (HTS) bulks offer the potential of trapping and maintaining much higher magnetic loading level compared with the conventional permanent magnets used in rotary machines, although the effective magnetization of multiple HTS bulks with different relative orientations over the surface of cylindrical rotors creates new challenges. In this paper, we present the design and numerical validation of the Pulse Field Magnetization (PFM) strategy considered for the magnetization of the four-pole synchronous fully superconducting motor developed at the University of Cambridge. In a first instance, singular columns of up to five HTS bulks aligned over the height of the rotor were subjected to up to three magnetic pulses of 1.5 T peak, and the experimental results have been simulated by considering the electrical and thermal properties of the system in a 2D approach. The entire active surface of the rotor is covered by HTS bulks of approximately the same dimensions, resulting in an uneven distribution of pole areas with at least one of the poles formed by up to 3 columns of magnetized bulks, with relatively the same peaks of trapped magnetic field. Thus, in order to effectively use the entire area of the superconducting rotor, multiple pulsed fields per column have been applied

  1. Adsorption behavior of multiwall carbon nanotube/iron oxide magnetic composites for Ni(II) and Sr(II)

    International Nuclear Information System (INIS)

    Chen Changlun; Hu Jun; Shao Dadong; Li Jiaxing; Wang Xiangke

    2009-01-01

    Multiwall carbon nanotube (MWCNT)/iron oxide magnetic composites were prepared, and were characterized by scan electron microscopy using a field emission scanning electron microscope, X-ray diffraction and vibrating sample magnetometer. The adsorptions of Ni(II) and Sr(II) onto MWCNT/iron oxide magnetic composites were studied as a function of pH and ionic strength. The results show that the adsorptions of Ni(II) and Sr(II) on the magnetic composites is strongly dependent on pH and ionic strength. The adsorption capacity of the magnetic composites is much higher than that of MWCNTs and iron oxides. The solid magnetic composites can be separated from the solution by a magnetic process. The Langmuir model fits the adsorption isotherm data of Ni(II) better than the Freundlich model. Results of desorption study shows that Ni(II) adsorbed onto the magnetic composites can be easily desorbed at pH < 2.0. MWCNT/iron oxide magnetic composites may be a promising candidate for pre-concentration and solidification of heavy metal ions and radionuclides from large volumes of aqueous solution, as required for remediation purposes.

  2. Mechanism of the X-ray and Soft Gamma-ray Emissions from the High Magnetic Field Pulsar: PSR B1509-58

    Directory of Open Access Journals (Sweden)

    Yu Wang

    2013-06-01

    Full Text Available We use the outer gap model to explain the spectrum and the energy dependent light curves of the X-ray and soft γ-ray radiations of the spin-down powered pulsar PSR B1509-58. In the outer gap model, most pairs inside the gap are created around the null charge surface and the gap’s electric field separates the opposite charges to move in opposite directions. Consequently, the region from the null charge surface to the light cylinder is dominated by the outflow current and that from the null charge surface to the star is dominated by the inflow current. We suggest that the viewing angle of PSR B1509-58 only receives the inflow radiation. The incoming curvature photons are converted to pairs by the strong magnetic field of the star. The X-rays and soft γ-rays of PSR B1509-58 result from the synchrotron radiation of these pairs. The magnetic pair creation requires a large pitch angle, which makes the pulse profile of the synchrotron radiation distinct from that of the curvature radiation. We carefully trace the pulse profiles of the synchrotron radiation with different pitch angles. We find that the differences between the light curves of different energy bands are due to the different pitch angles of the secondary pairs, and the second peak appearing at E > 10 MeV comes from the region near the star, where the stronger magnetic field allows the pair creation to happen with a smaller pitch angle.

  3. Biological cell as a soft magnetoelectric material: Elucidating the physical mechanisms underpinning the detection of magnetic fields by animals

    Science.gov (United States)

    Krichen, S.; Liu, L.; Sharma, P.

    2017-10-01

    Sharks, birds, bats, turtles, and many other animals can detect magnetic fields. Aside from using this remarkable ability to exploit the terrestrial magnetic field map to sense direction, a subset is also able to implement a version of the so-called geophysical positioning system. How do these animals detect magnetic fields? The answer to this rather deceptively simple question has proven to be quite elusive. The currently prevalent theories, while providing interesting insights, fall short of explaining several aspects of magnetoreception. For example, minute magnetic particles have been detected in magnetically sensitive animals. However, how is the detected magnetic field converted into electrical signals given any lack of experimental evidence for relevant electroreceptors? In principle, a magnetoelectric material is capable of converting magnetic signals into electricity (and vice versa). This property, however, is rare and restricted to a rather small set of exotic hard crystalline materials. Indeed, such elements have never been detected in the animals studied so far. In this work we quantitatively outline the conditions under which a biological cell may detect a magnetic field and convert it into electrical signals detectable by biological cells. Specifically, we prove the existence of an overlooked strain-mediated mechanism and show that most biological cells can act as nontrivial magnetoelectric materials provided that the magnetic permeability constant is only slightly more than that of a vacuum. The enhanced magnetic permeability is easily achieved by small amounts of magnetic particles that have been experimentally detected in magnetosensitive animals. Our proposed mechanism appears to explain most of the experimental observations related to the physical basis of magnetoreception.

  4. Nanocomposite permanent magnetic materials Nd-Fe-B type: The influence of nanocomposite on magnetic properties

    Directory of Open Access Journals (Sweden)

    Talijan Nadežda M.

    2005-01-01

    Full Text Available The influence on the magnetic properties of nanocristalline ribbons and powders has character of microstructure, between others – the grain size volume of hard and soft magnetic phases and their distribution. Magnetic properties of ribbons and powders depend mainly on their chemical composition and parameters of their heat treatment [1]. Technology of magnets from nanocristalline ribbon consists of the following process: preparing the Nd-Fe- B alloy, preparing the ribbon, powdering of the ribbon, heat treatment of the powder and finally preparing the magnets. Nanocomposite permanent magnet materials based on Nd-Fe- B alloy with Nd low content are a new type of permanent magnetic material. The microstructure of this nanocomposite permanent magnet is composed of a mixture of magnetically soft and hard phases which provide so called exchange coupling effect.

  5. Chemical compositions of magnetic, stony spherules from deep-sea sediments determined by instrumental neutron activation analysis

    International Nuclear Information System (INIS)

    Yamakoshi, Kazuo

    1984-01-01

    Chemical compositions of magnetic, stony spherules from deep sea sediments were determined by instrumental neutron activation analysis. High Ir, Au, Ni and Co contents indicate their extraterrestrial origin. The obtained compositions are considerably different from those of chondrites. It can be qualitatively interpreted, however, that cosmic matters having the compositions of chondrites are changed into magnetic, stony spherules by thermal degenerations during their atmospheric entry. (author)

  6. Study of dependence upon the magnetic field and transport current of the magnetoresistive effect in YBCO-based bulk composites

    International Nuclear Information System (INIS)

    Balaev, D A; Prus, A G; Shaykhutdinov, K A; Gokhfeld, D M; Petrov, M I

    2007-01-01

    The magnetoresistive properties of bulk YBCO + CuO and YBCO+BaPb 0.75 Sn 0.25 O 3 composites for different orientations of external magnetic field H and macroscopic transport current j have been measured. These composites exhibit large magnetoresistance in weak magnetic fields ( 2 θ. This fact suggests that the flux flow in the intergrain boundaries is responsible for the large magnetoresistive effect observed in the composites

  7. Peroneal perforator-based peroneus longus tendon and sural neurofasciocutaneous composite flap transfer for a large soft-tissue defect of the forearm: A case report.

    Science.gov (United States)

    Hayashida, Kenji; Saijo, Hiroto; Fujioka, Masaki

    2018-01-01

    We describe the use of a composite flap composed of a sural neurofasciocutaneous flap and a vascularized peroneus longus tendon for the reconstruction of severe composite forearm tissue defects in a patient. A 43-year-old man had his left arm caught in a conveyor belt resulting in a large soft-tissue defect of 18 × 11 cm over the dorsum forearm. The extensor carpi radialis, superficial radial nerve, and radial artery were severely damaged. A free neurofasciocutaneous composite flap measuring 16 × 11 cm was outlined on the patient's left lower leg to allow simultaneous skin, tendon, nerve, and artery reconstruction. The flap, which included the peroneus longus tendon, was elevated on the subfascial plane. After the flap was transferred to the recipient site, the peroneal artery was anastomosed to the radial artery in a flow-through manner. The vascularized tendon graft with 15 cm in length was used to reconstruct the extensor carpi radialis longus tendon defect using an interlacing suture technique. As the skin paddle of the sural neurofasciocutaneous flap and the vascularized peroneus longus tendon graft were linked by the perforator and minimal fascial tissue, the skin paddle was able to rotate and slide with comparative ease. The flap survived completely without any complications. The length of follow-up was 12 months and was uneventful. Range of motion of his left wrist joint was slightly limited to 75 degrees. This novel composite flap may be useful for reconstructing long tendon defects associated with extensive forearm soft tissue defects. © 2016 Wiley Periodicals, Inc.

  8. Magnetic behavior of NiCu nanowire arrays: Compositional, geometry and temperature dependence

    International Nuclear Information System (INIS)

    Palmero, E. M.; Bran, C.; Real, R. P. del; Vázquez, M.; Magén, C.

    2014-01-01

    Arrays of Ni 100−x Cu x nanowires ranging in composition 0 ≤ x ≤ 75, diameter from 35 to 80 nm, and length from 150 nm to 28 μm have been fabricated by electrochemical co-deposition of Ni and Cu into self-ordered anodic aluminum oxide membranes. As determined by X-ray diffraction and Transmission Electron Microscopy, the crystalline structure shows fcc cubic symmetry with [111] preferred texture and preferential Ni or Cu lattice depending on the composition. Their magnetic properties such as coercivity and squareness have been determined as a function of composition and geometry in a Vibrating Sample Magnetometer in the temperature range from 10 to 290 K for applied magnetic fields parallel and perpendicular to the nanowires axis. Addition of Cu into the NiCu alloy up to 50% enhances both parallel coercivity and squareness. For the higher Cu content, these properties decrease and the magnetization easy axis becomes oriented perpendicular to the wires. In addition, coercivity and squareness increase by decreasing the diameter of nanowires which is ascribed to the increase of shape anisotropy. The temperature dependent measurements reflect a complex behavior of the magnetic anisotropy as a result of energy contributions with different evolution with temperature.

  9. Magnetic Field Sensing by Exploiting Giant Nonstrain-Mediated Magnetodielectric Response in Epitaxial Composites.

    Science.gov (United States)

    Kang, Min Gyu; Kang, Han Byul; Clavel, Michael; Maurya, Deepam; Gollapudi, Sreenivasulu; Hudait, Mantu; Sanghadasa, Mohan; Priya, Shashank

    2018-04-10

    Heteroepitaxial magnetoelectric (ME) composites are promising for the development of a new generation of multifunctional devices, such as sensors, tunable electronics, and energy harvesters. However, challenge remains in realizing practical epitaxial composite materials, mainly due to the interfacial lattice misfit strain between magnetostrictive and piezoelectric phases and strong substrate clamping that reduces the strain-mediated ME coupling. Here, we demonstrate a nonstrain-mediated ME coupling in PbZr 0.52 Ti 0.48 O 3 (PZT)/La 0.67 Sr 0.33 MnO 3 (LSMO) heteroepitaxial composites that resolves these challenges, thereby, providing a giant magnetodielectric (MD) response of ∼27% at 310 K. The factors driving the magnitude of the MD response were found to be the magnetoresistance-coupled dielectric dispersion and piezoelectric strain-mediated modulation of magnetic moment. Building upon this giant MD response, we demonstrate a magnetic field sensor architecture exhibiting a high sensitivity of 54.7 pF/T and desirable linearity with respect to the applied external magnetic field. The demonstrated technique provides a new mechanism for detecting magnetic fields based upon the MD effect.

  10. Microstructure and composition in rapidly quenched NdFeB-based hard magnet alloys

    International Nuclear Information System (INIS)

    Nguyen, T.D.; Krishnan, K.M.; Lewis, L.H.; Zhu, Y.; Welch, D.O.

    1996-01-01

    A detailed study of the microstructure and composition in hot-pressed (MQ-2) and die-upset (MQ-3) magnet alloys based on the Nd 2 Fe 14 B composition, utilizing high resolution and analytical transmission electron microscopy, is reported. The initial magnetic properties of the two samples show different behaviors, which are attributed to the difference in the anisotropy of the grain structure and the grain boundaries. The hot-pressed sample shows faceted grains of the 2-14-1 phase, while die-upset sample shows plate-like grains, together with larger equiaxed grains that contain a speckling of precipitates in the grain interior. The grain structure and composition remain rather similar in the two samples. The grain boundary phase averages ∼1 endash approx-gt 10 nm in width. The thicker grain boundaries are Nd-rich, while the thinner grain boundaries in the hot-pressed sample exhibit an Fe-rich composition near that of the NdFe 3 phase. Nd-rich phases are found at the grain boundary junctions of both samples, with the Nd:Fe ratio near 7:3 in the die-upset sample, and up to 3:2 in the hot-pressed sample. The significance of the microstructure and the grain boundary phases on the magnetic behavior in the two samples is discussed. copyright 1996 American Institute of Physics

  11. Polymer Magnetic Composite Core Based Microcoils and Microtransformers for Very High Frequency Power Applications

    Directory of Open Access Journals (Sweden)

    Saravana Guru Mariappan

    2016-04-01

    Full Text Available We present a rapid prototyping and a cost effective fabrication process on batch fabricated wafer-level micro inductive components with polymer magnetic composite (PMC cores. The new PMC cores provide a possibility to bridge the gap between the non-magnetic and magnetic core inductive devices in terms of both the operating frequency and electrical performance. An optimized fabrication process of molding, casting, and demolding which uses teflon for the molding tool is presented. High permeability NiFeZn powder was mixed with Araldite epoxy to form high resistive PMC cores. Cylindrical PMC cores having a footprint of 0.79 mm 2 were fabricated with varying percentage of the magnetic powder on FR4 substrates. The core influence on the electrical performance of the inductive elements is discussed. Inductor chips having a solenoidal coil as well as transformer chips with primary and secondary coils wound around each other have been fabricated and evaluated. A core with 65% powder equipped with a solenoid made out of 25 µm thick insulated Au wire having 30 turns, yielded a constant inductance value of 2 µH up to the frequency of 50 MHz and a peak quality factor of 13. A 1:1 transformer with similar PMC core and solenoidal coils having 10 turns yielded a maximum efficiency of 84% and a coupling factor of 96%. In order to protect the solenoids and to increase the mechanical robustness and handling of the chips, a novel process was developed to encapsulate the components with an epoxy based magnetic composite. The effect on the electrical performance through the magnetic composite encapsulation is reported as well.

  12. Spin waves in the soft layer of exchange-coupled soft/hard bilayers

    Energy Technology Data Exchange (ETDEWEB)

    Xiong, Zheng-min; Ge, Su-qin; Wang, Xi-guang; Li, Zhi-xiong; Xia, Qing-lin; Wang, Dao-wei; Nie, Yao-zhuang; Guo, Guang-hua, E-mail: guogh@mail.csu.edu.cn [School of Physics and Electronics, Central South University, Changsha 410083 (China); Tang, Wei [School of Physics and Electronics, Central South University, Changsha 410083 (China); Suzhou Institute of Nano-tech and Nano-bionics, Chinese Academy of Sciences, Suzhou 215123 (China); Zeng, Zhong-ming [Suzhou Institute of Nano-tech and Nano-bionics, Chinese Academy of Sciences, Suzhou 215123 (China)

    2016-05-15

    The magnetic dynamical properties of the soft layer in exchange-coupled soft/hard bilayers have been investigated numerically using a one-dimensional atomic chain model. The frequencies and spatial profiles of spin wave eigenmodes are calculated during the magnetization reversal process of the soft layer. The spin wave modes exhibit a spatially modulated amplitude, which is especially evident for high-order modes. A dynamic pinning effect of surface magnetic moment is observed. The spin wave eigenfrequency decreases linearly with the increase of the magnetic field in the uniformly magnetized state and increases nonlinearly with field when spiral magnetization configuration is formed in the soft layer.

  13. Spin waves in the soft layer of exchange-coupled soft/hard bilayers

    Directory of Open Access Journals (Sweden)

    Zheng-min Xiong

    2016-05-01

    Full Text Available The magnetic dynamical properties of the soft layer in exchange-coupled soft/hard bilayers have been investigated numerically using a one-dimensional atomic chain model. The frequencies and spatial profiles of spin wave eigenmodes are calculated during the magnetization reversal process of the soft layer. The spin wave modes exhibit a spatially modulated amplitude, which is especially evident for high-order modes. A dynamic pinning effect of surface magnetic moment is observed. The spin wave eigenfrequency decreases linearly with the increase of the magnetic field in the uniformly magnetized state and increases nonlinearly with field when spiral magnetization configuration is formed in the soft layer.

  14. Preparation and properties of novel magnetic composite nanostructures: Arrays of nanowires in porous membranes

    International Nuclear Information System (INIS)

    Vazquez, M.; Hernandez-Velez, M.; Asenjo, A.; Navas, D.; Pirota, K.; Prida, V.; Sanchez, O.; Baldonedo, J.L.

    2006-01-01

    In the present work, we introduce our latest achievements in the development of novel highly ordered composite magnetic nanostructures employing anodized nanoporous membranes as precursor templates where long-range hexagonal symmetry is induced by self-assembling during anodization process. Subsequent processing as electroplating, sputtering or pressing are employed to prepare arrays of metallic, semiconductor or polymeric nanowires embedded in oxide or metallic membranes. Particular attention is paid to recent results on controlling the magnetic anisotropy in arrays of metallic nanowires, particularly Co, and nanohole arrays in Ni membranes

  15. Optimization on microwave absorbing properties of carbon nanotubes and magnetic oxide composite materials

    Science.gov (United States)

    Mingdong, Chen; Huangzhong, Yu; Xiaohua, Jie; Yigang, Lu

    2018-03-01

    Based on the physical principle of interaction between electromagnetic field and the electromagnetic medium, the relationship between microwave absorbing coefficient (MAC) and the electromagnetic parameters of materials was established. With the composite materials of nickel ferrite (NiFe2O4), carbon nanotubes (CNTs) and paraffin as an example, optimization on absorbing properties of CNTs/magnetic oxide composite materials was studied at the frequency range of 2-18 GHz, and a conclusion is drawn that the MAC is the biggest at the same frequency, when the CNTs is 10 wt% in the composite materials. Through study on the relationship between complex permeability and MAC, another interesting conclusion is drawn that MAC is obviously affected by the real part of complex permeability, and increasing real part of complex permeability is beneficial for improving absorbing properties. The conclusion of this paper can provide a useful reference for the optimization research on the microwave absorbing properties of CNTs/ferrite composite materials.

  16. Novel functional magnetic materials fundamentals and applications

    CERN Document Server

    2016-01-01

    This book presents current research on advanced magnetic materials and multifunctional composites. Recent advances in technology and engineering have resulted from the development of advanced magnetic materials with improved functional magnetic and magneto-transport properties. Certain industrial sectors, such as magnetic sensors, microelectronics, and security, demand cost-effective materials with reduced dimensionality and desirable magnetic properties such as enhanced magnetic softness, giant magnetic field sensitivity, and large magnetocaloric effect.  Expert chapters present the most up-to-date information on the fabrication process, processing, tailoring of properties, and applications of different families of modern functional materials for advanced smart applications. Topics covered include novel magnetic materials and applications; amorphous and nanocrystalline magnetic materials and applications; hard magnetic materials; magnetic shape memory alloys; and magnetic oxides. The book's highly interdis...

  17. Enhanced magnetization in morphologically and magnetically distinct BiFeO3 and La0.7Sr0.3MnO3 composites

    Science.gov (United States)

    Pillai, Shreeja; Reshi, Hilal Ahmad; Bagwaiya, Toshi; Banerjee, Alok; Shelke, Vilas

    2017-09-01

    Nanomaterials exhibit properties different from those of their bulk counterparts. The modified magnetic characteristics of manganite nanoparticles were exploited to improve magnetization in multiferroic BiFeO3 compound. We studied the composite of two morphologically and magnetically distinct compounds BiFeO3 (BFO) and La0.7Sr0.3MnO3 (LSMO). The microcrystalline BiFeO3 sample was prepared by solid state reaction method and the nanocrystalline La0.7Sr0.3MnO3 by sol-gel method. Composites with nominal compositions (1-x)BiFeO3-(x)La0.7Sr0.3MnO3 were prepared by modified solid state reaction method. The phase purity and crystal structures were checked by using X-ray diffraction. The formation of composites with phase separated BFO and LSMO was confirmed using Raman and Fourier Transform Infrared spectroscopy studies. The composite samples showed relatively high value of magnetization with finite coercivity. This improvement in magnetic behavior is ascribed to the coexistence of multiple magnetic orderings in composite samples. We scrutinized the possibility of oxygen vacancy or Fe mixed valency formation in the samples using X-ray photoelectron spectroscopy technique.

  18. Antagonistic effects on mechanical properties of microfibrillar composites with dual reinforcement: explanation by FEA model of soft interface

    Czech Academy of Sciences Publication Activity Database

    Kelnar, Ivan; Kratochvíl, Jaroslav; Kaprálková, Ludmila; Zhigunov, Alexander; Padovec, Z.; Růžička, M.; Nevoralová, Martina

    2017-01-01

    Roč. 134, č. 20 (2017), s. 1-9, č. článku 44712. ISSN 0021-8995 R&D Projects: GA ČR(CZ) GA13-15255S Institutional support: RVO:61389013 Keywords : finite element analysis * interface * microfibrillar composites Subject RIV: JI - Composite Materials OBOR OECD: Composites (including laminates, reinforced plastics, cermets, combined natural and synthetic fibre fabrics Impact factor: 1.860, year: 2016

  19. Note: Enhanced energy harvesting from low-frequency magnetic fields utilizing magneto-mechano-electric composite tuning-fork.

    Science.gov (United States)

    Yang, Aichao; Li, Ping; Wen, Yumei; Yang, Chao; Wang, Decai; Zhang, Feng; Zhang, Jiajia

    2015-06-01

    A magnetic-field energy harvester using a low-frequency magneto-mechano-electric (MME) composite tuning-fork is proposed. This MME composite tuning-fork consists of a copper tuning fork with piezoelectric Pb(Zr(1-x)Ti(x))O3 (PZT) plates bonded near its fixed end and with NdFeB magnets attached at its free ends. Due to the resonance coupling between fork prongs, the MME composite tuning-fork owns strong vibration and high Q value. Experimental results show that the proposed magnetic-field energy harvester using the MME composite tuning-fork exhibits approximately 4 times larger maximum output voltage and 7.2 times higher maximum power than the conventional magnetic-field energy harvester using the MME composite cantilever.

  20. Fascinating Magnetic Energy Storage Nanomaterials: A Brief Review.

    Science.gov (United States)

    Sreenivasulu, Kummari V; Srikanth, Vadali V S S

    2017-07-10

    In this brief review, the importance of nanotechnology in developing novel magnetic energy storage materials is discussed. The discussion covers recent patents on permanent magnetic materials and especially covers processing of permanent magnets (rare-earth and rare-earth free magnets), importance of rare-earth permanent magnets and necessity of rare-earth free permanent magnets. Magnetic energy storage materials are those magnetic materials which exhibit very high energy product (BH)max (where B is the magnetic induction in Gauss (G) whereas H is the applied magnetic field in Oersted (Oe)). (BH)max is the direct measure of the ability of a magnetic material to store energy. In this context, processing of magnetic energy storage composite materials constituted by soft and hard magnetic materials played a predominant role in achieving high (BH)max values due to the exchange coupling phenomenon between the soft and hard magnetic phases within the composite. Magnetic energy storage composites are normally composed of rare-earth magnetic materials as well as rare-earth free magnetic materials. Nanotechnology's influence on the enhancement of energy product due to the exchange coupling phenomenon is of great prominence and therefore discussed in this review. Copyright© Bentham Science Publishers; For any queries, please email at epub@benthamscience.org.

  1. Composite magnetorheological elastomers as dielectrics for plane capacitors: Effects of magnetic field intensity

    Directory of Open Access Journals (Sweden)

    Maria Balasoiu

    Full Text Available The fabrication of composite magnetorheological elastomers (MRECs based on silicone rubber, carbonyl iron microparticles (10% vol. and polyurethane elastomer doped with 0%, 10% and 20% volume concentration TiO2 microparticles is presented. The obtained MRECs have the shape of thin foils and are used as dielectric materials for manufacturing plane capacitors. Using the plane capacitor method and expression of capacitance as a function of magnetic field intensity, combined with linear elasticity theory, the static magnetoelastic model of the composite is obtained and analyzed. Keywords: Magnetorheological elastomer, TiO2 microparticles, Silicone rubber, Carbonyl iron, Plane capacitor, Magnetoelasticity

  2. Conceptual design of the tomographic system for simultaneous studying of soft and hard X-ray emission from dense magnetized plasma

    Energy Technology Data Exchange (ETDEWEB)

    Bielecki, J., E-mail: jakub.bielecki@ifj.edu.edu; Wójcik-Gargula, A.; Scholz, M.

    2016-11-15

    The article presents a new approach for investigation of spatial distributions of soft and hard X-rays emitted from dense magnetized plasma. The approach is based on the application of tomographic methods to the X-ray emission reconstruction in a plasma focus (PF) device. Quantitative investigation of the anisotropy of the reconstructed X–ray plasma emissivity may help to explain the nature of fusion reaction mechanisms in a PF device. The aim of this work is to present a conceptual design of a novel dual-energy X-ray emission tomographic system dedicated to the PF-24 plasma focus device. The system, which enables the simultaneous registration of soft and hard X-rays, is composed of three X‐ray pinhole cameras. Each camera is equipped with a pair of 16-element Si photodiode arrays arranged in two layers separated by an aluminum attenuator. The Geant4 code w