Porous glass with high silica content for nuclear waste storage : preparation, characterization and leaching

International Nuclear Information System (INIS)

Aegerter, M.A.; Santos, D.I. dos; Ventura, P.C.S.

1984-01-01

Aqueous solutions simulating radioactive nuclear wastes (like Savanah River Laboratory) were incorporated in porous glass matrix with high silica content prepared by decomposition of borosilicate glass like Na 2 O - B 2 O 3 - SiO 2 . After sintering, the samples were submitted, during 28 days, to standard leaching tests MCC1, MCC5 (Soxhlet) and stagnating. The total weight loss, ph, as well as the integral and differential leaching rates and the accumulated concentrations in the leach of Si, Na, B, Ca, Mn, Al, Fe and Ni. The results are compared with the results from reference borosilicate glass, made by fusion, ceramic, synroc, concrets, etc... (E.G.) [pt

Bulk metallic glass matrix composites

International Nuclear Information System (INIS)

Choi-Yim, H.; Johnson, W.L.

1997-01-01

Composites with a bulk metallic glass matrix were synthesized and characterized. This was made possible by the recent development of bulk metallic glasses that exhibit high resistance to crystallization in the undercooled liquid state. In this letter, experimental methods for processing metallic glass composites are introduced. Three different bulk metallic glass forming alloys were used as the matrix materials. Both ceramics and metals were introduced as reinforcement into the metallic glass. The metallic glass matrix remained amorphous after adding up to a 30 vol% fraction of particles or short wires. X-ray diffraction patterns of the composites show only peaks from the second phase particles superimposed on the broad diffuse maxima from the amorphous phase. Optical micrographs reveal uniformly distributed particles in the matrix. The glass transition of the amorphous matrix and the crystallization behavior of the composites were studied by calorimetric methods. copyright 1997 American Institute of Physics

Preparation and spectroscopic properties of Yb-doped and Yb-Al-codoped high silica glasses

International Nuclear Information System (INIS)

Qiao Yanbo; Wen Lei; Wu Botao; Ren Jinjun; Chen Danping; Qiu Jianrong

2008-01-01

Yb-doped and Yb-Al-codoped high silica glasses have been prepared by sintering nanoporous glasses. The absorption, fluorescent spectra and fluorescent lifetimes have been measured and the emission cross-section and minimum pump intensities were calculated. Codoping aluminum ions enhanced the fluorescence intensity of Yb-doped high silica glass obviously. The emission cross-sections of Yb-doped and Yb-Al-codoped high silica glasses were 0.65 and 0.82 pm 2 , respectively. The results show that Yb-Al-codoped high silica glass has better spectroscopic properties for a laser material. The study of high silica glass doped with ytterbium is helpful for its application in Yb laser systems, especially for high-power and high-repetition lasers

Dynamic compressive properties and failure mechanism of glass fiber reinforced silica hydrogel

International Nuclear Information System (INIS)

Yang Jie; Li Shukui; Yan Lili; Huo Dongmei; Wang Fuchi

2010-01-01

The dynamic compressive properties of glass fiber reinforced silica (GFRS) hydrogel were investigated using a spilt Hopkinson pressure bar. Failure mechanism of GFRS hydrogel was studied by scanning electron microscopy (SEM). Result showed that dynamic compressive stresses were much higher than the quasi-static compressive stresses at the same strain. The dynamic compressive strength was directly proportional to the strain rate with same sample dimensions. The dynamic compressive strength was directly proportional to the sample basal area at same strain rate. Dynamic compressive failure strain was small. At high strain rates, glass fibers broke down and separated from the matrix, pores shrank rapidly. Failure resulted from the increase of lateral tensile stress in hydrogel under dynamic compression.

Fabrication of transparent superhydrophobic glass with fibered-silica network

Energy Technology Data Exchange (ETDEWEB)

Zhang, Feng [College of Physics, Optoelectronics and Energy & Collaborative Innovation Center of Suzhou Nano Science and Technology, Soochow University, Suzhou 215006 (China); Key Lab of Advanced Optical Manufacturing Technologies of Jiangsu Province & Key Lab of Modern Optical Technologies of Education Ministry of China, Soochow University, Suzhou 215006 (China); Shi, Zhenwu, E-mail: zwshi@suda.edu.cn [College of Physics, Optoelectronics and Energy & Collaborative Innovation Center of Suzhou Nano Science and Technology, Soochow University, Suzhou 215006 (China); Key Lab of Advanced Optical Manufacturing Technologies of Jiangsu Province & Key Lab of Modern Optical Technologies of Education Ministry of China, Soochow University, Suzhou 215006 (China); Jiang, Yingjie; Xu, Chengyun; Wu, Zhuhui; Wang, Yanyan [College of Physics, Optoelectronics and Energy & Collaborative Innovation Center of Suzhou Nano Science and Technology, Soochow University, Suzhou 215006 (China); Key Lab of Advanced Optical Manufacturing Technologies of Jiangsu Province & Key Lab of Modern Optical Technologies of Education Ministry of China, Soochow University, Suzhou 215006 (China); Peng, Changsi, E-mail: changsipeng@suda.edu.cn [College of Physics, Optoelectronics and Energy & Collaborative Innovation Center of Suzhou Nano Science and Technology, Soochow University, Suzhou 215006 (China); Key Lab of Advanced Optical Manufacturing Technologies of Jiangsu Province & Key Lab of Modern Optical Technologies of Education Ministry of China, Soochow University, Suzhou 215006 (China)

2017-06-15

Highlights: • Superhydrophobic fibred-silica film with water contact angle of 166° and sliding angle of 1° was efficiently prepared using soot as template by CVD. • The film showed transmittance of 88% in visible range. • The superhydrophobic film possesses excellent mechanical robustness, chemical corrosion resistance, and thermal stability. • The superhydrophobic film showed outstanding self-cleaning behavior. - Abstract: In this paper, silica was deposited on the soot film pre-coated glass via chemical vapor deposition. Through calcination at 500 °C with the assistance of O{sub 2} airflow, the soot film was removed and a novel robust fibered-silica network film was then decorated onto the glass substrate. After modification with fluorosilane, the surface water contact angle (WCA) was 166° and sliding angle (SA) was 1° which behaves a good self-cleaning for the as-prepared glass. And its average transmittance was still over 88% in visible wavelength. Moreover, this fibered-silica coating showed a strong tolerance for heavy water droplets, acid/alkali corrosion, salt solution immersion and thermal treatment.

Structure and Properties of Silica Glass Densified in Cold Compression and Hot Compression

Science.gov (United States)

Guerette, Michael; Ackerson, Michael R.; Thomas, Jay; Yuan, Fenglin; Bruce Watson, E.; Walker, David; Huang, Liping

2015-10-01

Silica glass has been shown in numerous studies to possess significant capacity for permanent densification under pressure at different temperatures to form high density amorphous (HDA) silica. However, it is unknown to what extent the processes leading to irreversible densification of silica glass in cold-compression at room temperature and in hot-compression (e.g., near glass transition temperature) are common in nature. In this work, a hot-compression technique was used to quench silica glass from high temperature (1100 °C) and high pressure (up to 8 GPa) conditions, which leads to density increase of ~25% and Young’s modulus increase of ~71% relative to that of pristine silica glass at ambient conditions. Our experiments and molecular dynamics (MD) simulations provide solid evidences that the intermediate-range order of the hot-compressed HDA silica is distinct from that of the counterpart cold-compressed at room temperature. This explains the much higher thermal and mechanical stability of the former than the latter upon heating and compression as revealed in our in-situ Brillouin light scattering (BLS) experiments. Our studies demonstrate the limitation of the resulting density as a structural indicator of polyamorphism, and point out the importance of temperature during compression in order to fundamentally understand HDA silica.

Structure and spectral properties of the silver-containing high-silica glasses

International Nuclear Information System (INIS)

Girsova, M A; Golovina, G F; Anfimova, I N; Antropova, T V; Arsent'ev, M Yu

2016-01-01

Silver-containing high-silica glasses were synthesized by an impregnation of the silica porous glasses (PGs) first with AgNO 3 aqueous solution (with or without the presence of the sensitizers, such as Cu(NO 3 ) 2 or Ce(NO 3 ) 3 ), next in the mixed halide salt (NH 4 Cl, KBr, KI) solution. Then some part of the samples was sintered at the temperatures from 850 to 900°C up to closing of the pores. The structure of glasses was studied by UV-VIS-NIR and IR spectroscopy and X-ray diffraction (XRD) techniques. According to XRD data the silver-containing high-silica glasses contain the AgBr, AgI, Ag 3 PO 4 , (CuBr) 0.75 (CuI) 0.25 phases. IR spectra confirmed B-O-B, Si- O-Si, P-O-P, O-P-O, O-B-O bonds, (PO 4 ) 3- and P-O - groups in glasses. (paper)

Effects of roughness on interfacial performances of silica glass and non-polar polyarylacetylene resin composites

International Nuclear Information System (INIS)

Jiang, Z.X.; Huang, Y.D.; Liu, L.; Long, J.

2007-01-01

The influence of roughness on interfacial performances of silica glass/polyarylacetylene resin composites was investigated. In order to obtain different roughness, silica glass surface was abraded by different grits of abrasives and its topography was observed by scanning electron microscopy and atomic force microscopy. At the same time, the failure mechanisms of composites were analyzed by fracture morphologies and the interfacial adhesion was evaluated by shear strength test. The results indicated that shear strength of silica glass/polyarylacetylene resin composites firstly increased and then decreased with the surface roughness of silica glass increased. The best surface roughness range of silica glass was 40-60 nm. The main mechanism for the improvement of the interfacial adhesion was physical interlocking at the interface

Synthesis of nanocrystalline LaF3 doped silica glasses by hydrofluoric acid catalyzed sol–gel process

International Nuclear Information System (INIS)

Nagayama, Shuhei; Kajihara, Koichi; Kanamura, Kiyoshi

2012-01-01

Highlights: ► Silica glasses doped by LaF 3 nanocrystals are obtained by HF-catalyzed sol–gel method. ► The processing time (∼1 week) is much shorter than that of previous studies. ► The uptake of SiF groups in the glass matrix greatly reduces the SiOH concentration. ► Effects of sintering conditions and properties of Er 3+ -doped samples are presented. - Abstract: Silica glasses doped with LaF 3 nanocrystals were prepared by HF-catalyzed sol–gel method. HF was used both as fluorine source and as catalyst of the sol–gel reaction, making it possible to shorten the processing time with reducing the concentration of SiOH groups to ∼10 18 cm −3 . The resultant glasses are transparent at visible spectral range, and the optical loss at the ultraviolet absorption edge is dominated by the Rayleigh scattering from LaF 3 crystallites. The size of LaF 3 crystallites increases with an increase in the sintering temperature and time, and is smaller than ∼40 nm in samples showing good visible transparency. Green upconversion photoluminescence is observed in an Er 3+ -doped sample under excitation at 980 nm.

Deep glass etched microring resonators based on silica-on-silicon technology

DEFF Research Database (Denmark)

Ou, Haiyan; Rottwitt, Karsten; Philipp, Hugh Taylor

2006-01-01

Microring resonators fabricated on silica-on-silicon technology using deep glass etching are demonstrated. The fabrication procedures are introduced and the transmission spectrum of a resonator is presented.......Microring resonators fabricated on silica-on-silicon technology using deep glass etching are demonstrated. The fabrication procedures are introduced and the transmission spectrum of a resonator is presented....

Glass properties in the yttria-alumina-silica system

Science.gov (United States)

Hyatt, M. J.; Day, D. E.

1987-01-01

The glass formation region in the yttria-alumina-silica system was investigated. Properties of glasses containing 25 to 55 wt pct yttria were measured and the effect of the composition was determined. The density, refractive index, thermal-expansion coefficient, and microhardness increased with increasing yttria content. The dissolution rate in 1N HCl increased with increasing yttria content and temperature. These glasses were also found to have high electrical resistivity.

Incorporation of Nanohybrid Films of Silica into Recycled Polystyrene Matrix

Directory of Open Access Journals (Sweden)

Genoveva Hernández-Padrón

2015-01-01

Full Text Available An alternative for the reutilization of polystyrene waste containers consisting in creating a hybrid material made of SiO2 nanoparticles embedded in a matrix of recycled polystyrene (PSR has been developed. Recycled polystyrene functionalized (PSRF was used to influence the morphological and antifog properties by the sol-gel synthesis of nanohybrid silica. To this end, silica nanoparticles were produced from alkoxide precursors in the presence of recycled polystyrene. The functionalization of this polymeric matrix was with the purpose of uniting in situ carboxyl and silanol groups during the sol-gel process. In this way, opaque or transparent solid substrates can be obtained, with each of these endowed with optical conditions that depend on the amount of reactants employed to prepare each nanohybrid specimen. The nanohybrids were labelled as SiO2/PSR (HPSR and SiO2/PSRF (HPSRF and their properties were then compared to those of commercial polystyrene (PS. All the prepared samples were used for coating glass substrates. The hydrophobicity of the resultant coatings was determined through contact angle measurement. The nanohybrid materials were characterized by FT-IR and 1H-NMR techniques. Additionally, TGA and SEM were employed to determine their thermal and textural properties.

Nanoporous Glasses for Nuclear Waste Containment

Directory of Open Access Journals (Sweden)

Thierry Woignier

2016-01-01

Full Text Available Research is in progress to incorporate nuclear waste in new matrices with high structural stability, resistance to thermal shock, and high chemical durability. Interactions with water are important for materials used as a containment matrix for the radio nuclides. It is indispensable to improve their chemical durability to limit the possible release of radioactive chemical species, if the glass structure is attacked by corrosion. By associating high structural stability and high chemical durability, silica glass optimizes the properties of a suitable host matrix. According to an easy sintering stage, nanoporous glasses such as xerogels, aerogels, and composite gels are alternative ways to synthesize silica glass at relatively low temperatures (≈1,000–1,200°C. Nuclear wastes exist as aqueous salt solutions and we propose using the open pore structure of the nanoporous glass to enable migration of the solution throughout the solid volume. The loaded material is then sintered, thereby trapping the radioactive chemical species. The structure of the sintered materials (glass ceramics is that of nanocomposites: actinide phases (~100 nm embedded in a vitreous silica matrix. Our results showed a large improvement in the chemical durability of glass ceramic over conventional nuclear glass.

Refractive index engineering in silica glass

DEFF Research Database (Denmark)

Kristensen, Martin

2003-01-01

. This way the glass undergoes significant physical and chemical changes and in some cases very large non-linear effects have been demonstrated. This includes a non-linear coefficient around 22 pm/V in a wavelength range near 800 nm. The author believes this is due to the combined action of silver nano......The thesis covers research performed durint the last eight years by the author in collaboration with members of his group within the field of UV-written gratings and poling of silica-based materials. The subjects cover several steps on the value chain from basic physics and chemistry via component...... in detail in chapters 4,5 and 6. Chapter 4 describes the semi-classsical model developed by the author to describe the basic UV-induced processes in germanium-doped silica. The idea behind the model is that oxygen-deficient germanium centres in the glass work as gates for the UV-photon energy, which...

Investigations on the homogeneity of silica glass and on the order of X-amorphous silica by luminescence measurements

International Nuclear Information System (INIS)

Boden, G.

1982-08-01

Silica glasses melted from crystalline SiO 2 were exposed to ionizing radiation. At room temperature the spatial intensity distribution of the emitted luminescent radiation has been recorded by means of photographic or autoradiographic materials. Thereby schlieren and inhomogeneities are made visible and information is obtained on the melting process of the crystalline SiO 2 . Synthetic fused silica made from SiCl 4 shows no luminescent radiation. Depending on the penetration depth of the ionizing radiation the bulk or the surface of the sample can be studied. The decay curves of the integral luminescence intensity yield data on inhomogeneities in the silica glass leading to conclusions on order state and structure. The luminescence intensity and its half-life are a measure for the inhomogeneity of the silica glass and the existence of so-called 'preordered states'. This connection between luminescence intensity and the order state is found also with other X-amorphous SiO 2 modifications: silica gel, precipitated silicic acids, porous SiO 2 glasses, aerosil, thin SiO 2 layers, mechanically activated quartz: whereas no luminescence phenomena occur in disordered nearly ideally amorphous SiO 2 species, the luminescence increases with increasing order degree of the SiO 2 network and attains a high intensity in the case of the crystalline SiO 2 modifications quartz and cristobalite

Studies on the Potential of Waste Soda Lime Silica Glass in Glass Ionomer Cement Production

Directory of Open Access Journals (Sweden)

V. W. Francis Thoo

2013-01-01

Full Text Available Glass ionomer cements (GIC are produced through acid base reaction between calcium-fluoroaluminosilicate glass powder and polyacrylic acid (PAA. Soda lime silica glasses (SLS, mainly composed of silica (SiO2, have been utilized in this study as the source of SiO2 for synthesis of Ca-fluoroaluminosilicate glass. Therefore, the main objective of this study was to investigate the potential of SLS waste glass in producing GIC. Two glasses, GWX 1 (analytical grade SiO2 and GWX 2 (replacing SiO2 with waste SLS, were synthesized and then characterized using X-ray diffraction (XRD and energy dispersive X-ray (EDX. Synthesized glasses were then used to produce GIC, in which the properties were characterized using Fourier transform infrared spectroscopy (FT-IR and compressive test (from 1 to 28 days. XRD results showed that amorphous glass was produced by using SLS waste glass (GWX 2, which is similar to glass produced using analytical grade SiO2 (GWX 1. Results from FT-IR showed that the setting reaction of GWX 2 cements is slower compared to cement GWX 1. Compressive strengths for GWX 1 cements reached up to 76 MPa at 28 days, whereas GWX 2 cements showed a slightly higher value, which is 80 MPa.

Enhancement of nonlinear optical properties of compounds of silica

Indian Academy of Sciences (India)

The aim of this paper is to introduce a method for enhancing the nonlinear optical properties in silica glass by using metallic nanoparticles. First, the T-matrix method is developed to calculate the effective dielectric constant for the compound of silica glass and metallic nanoparticles, both of which possess nonlinear dielectric ...

Development of high-average-power-laser medium based on silica glass

International Nuclear Information System (INIS)

Fujimoto, Yasushi; Nakatsuka, Masahiro

2000-01-01

We have developed a high-average-power laser material based on silica glass. A new method using Zeolite X is effective for homogeneously dispersing rare earth ions in silica glass to get a high quantum yield. High quality medium, which is bubbleless and quite low refractive index distortion, must be required for realization of laser action, and therefore, we have carefully to treat the gelation and sintering processes, such as, selection of colloidal silica, pH value of for hydrolysis of tetraethylorthosilicate, and sintering history. The quality of the sintered sample and the applications are discussed. (author)

The influence of glass composition on crystalline phase stability in glass-ceramic wasteforms

International Nuclear Information System (INIS)

Maddrell, Ewan; Thornber, Stephanie; Hyatt, Neil C.

2015-01-01

Highlights: • Crystalline phase formation shown to depend on glass matrix composition. • Zirconolite forms as the sole crystalline phase only for most aluminous glasses. • Thermodynamics indicate that low silica activity glasses stabilise zirconolite. - Abstract: Zirconolite glass-ceramic wasteforms were prepared using a suite of Na 2 O–Al 2 O 3 –B 2 O 3 –SiO 2 glass matrices with variable Al:B ratios. Zirconolite was the dominant crystalline phase only for the most alumina rich glass compositions. As the Al:B ratio decreased zirconolite was replaced by sphene, zircon and rutile. Thermodynamic data were used to calculate a silica activity in the glass melt below which zirconolite is the favoured crystalline phase. The concept of the crystalline reference state of glass melts is then utilised to provide a physical basis for why silica activity varies with the Al:B ratio

Silica gel matrix immobilized Chlorophyta hydrodictyon africanum ...

African Journals Online (AJOL)

Chlorophyta hydrodictyon africanum was immobilized on a silica gel matrix to improve its mechanical properties. The algae-silica gel adsorbent was used for batch sorption studies of a cationic dye, methylene blue (MB). Optimum adsorption was obtained with a dosage of 0.8 g bio sorbent. Results from sorption studies ...

Interphases, gelation, vitrification, porous glasses and the generalized Cauchy relation: epoxy/silica nanocomposites

Energy Technology Data Exchange (ETDEWEB)

Philipp, M; Mueller, U; Jimenez Rioboo, R J; Baller, J; Sanctuary, R; Krueger, J K [Laboratoire de Physique des Materiaux, University of Luxembourg, 162A avenue de la Faiencerie, L-1511 Luxembourg (Luxembourg); Possart, W [Fachbereich Werkstoffwissenschaften, Universitaet des Saarlandes, D-66123 Saarbruecken (Germany)], E-mail: martine.philipp@uni.lu

2009-02-15

The generalized Cauchy relation (gCR) of epoxy/silica nano-composites does not show either the chemically induced sol-gel transition or the chemically induced glass transition in the course of polymerization. Astonishingly, by varying the silica nanoparticles' concentration between 0 and 25 vol% in the composites, the Cauchy parameter A of the gCR remains universal and can be determined from the pure epoxy's elastic moduli. Air-filled porous silica glasses are considered as models for percolated silica particles. A longitudinal modulus versus density representation evidences the aforementioned transition phenomena during polymerization of the epoxy/silica nanocomposites. The existence of optically and mechanically relevant interphases is discussed.

Interphases, gelation, vitrification, porous glasses and the generalized Cauchy relation: epoxy/silica nanocomposites

International Nuclear Information System (INIS)

Philipp, M; Mueller, U; Jimenez Rioboo, R J; Baller, J; Sanctuary, R; Krueger, J K; Possart, W

2009-01-01

The generalized Cauchy relation (gCR) of epoxy/silica nano-composites does not show either the chemically induced sol-gel transition or the chemically induced glass transition in the course of polymerization. Astonishingly, by varying the silica nanoparticles' concentration between 0 and 25 vol% in the composites, the Cauchy parameter A of the gCR remains universal and can be determined from the pure epoxy's elastic moduli. Air-filled porous silica glasses are considered as models for percolated silica particles. A longitudinal modulus versus density representation evidences the aforementioned transition phenomena during polymerization of the epoxy/silica nanocomposites. The existence of optically and mechanically relevant interphases is discussed.

Formation of plasma induced surface damage in silica glass etching for optical waveguides

International Nuclear Information System (INIS)

Choi, D.Y.; Lee, J.H.; Kim, D.S.; Jung, S.T.

2004-01-01

Ge, B, P-doped silica glass films are widely used as optical waveguides because of their low losses and inherent compatibility with silica optical fibers. These films were etched by ICP (inductively coupled plasma) with chrome etch masks, which were patterned by reactive ion etching (RIE) using chlorine-based gases. In some cases, the etched surfaces of silica glass were very rough (root-mean square roughness greater than 100 nm) and we call this phenomenon plasma induced surface damage (PISD). Rough surface cannot be used as a platform for hybrid integration because of difficulty in alignment and bonding of active devices. PISD reduces the etch rate of glass and it is very difficult to remove residues on a rough surface. The objective of this study is to elucidate the mechanism of PISD formation. To achieve this goal, PISD formation during different etching conditions of chrome etch mask and silica glass was investigated. In most cases, PISD sources are formed on a glass surface after chrome etching, and metal compounds are identified in theses sources. Water rinse after chrome etching reduces the PISD, due to the water solubility of metal chlorides. PISD is decreased or even disappeared at high power and/or low pressure in glass etching, even if PISD sources were present on the glass surface before etching. In conclusion, PISD sources come from the chrome etching process, and polymer deposition on these sources during the silica etching cause the PISD sources to grow. In the area close to the PISD source there is a higher ion flux, which causes an increase in the etch rate, and results in the formation of a pit

Porous glass matrix method for encapsulating high-level nuclear wastes

International Nuclear Information System (INIS)

Macedo, P.B.; Tran, D.C.; Simmons, J.H.; Saleh, M.; Barkatt, A.; Simmons, C.J.; Lagakos, N.; DeWitt, E.

1979-01-01

A novel process which uses solidified porous high-silica glass powder to fixate radioactive high-level wastes is described. The process yields cylinders consisting of a core of high-silica glass containing the waste elements in its structure and a protective layer also of high-silica glass completely free of waste elements. The process can be applied to waste streams containing 0 to 100% solids. The core region exhibits a higher coefficient of thermal expansion and a lower glass transition temperature than the outer protective layer. This leads to mechanical strengthening of the glass and good resistance to stress corrosion by the development of a high residual compressive stress on the surface of the sample. Both the core and the protective layer exhibit extremely high chemical durability and offer an effective fixation of the radioactive waste elements, including 239 Pu and 99 Tc which have long half-lives, for calculated periods of more than 1 million years, when temperatures are not allowed to rise above 100 0 C

Effect of silica and water content on the glass transition of poly(ethylene glycol) monomethylether-silica gel-lithium perchlorate ormolytes

International Nuclear Information System (INIS)

Korwin, Rebecca S.; Masui, Hitoshi

2005-01-01

The effect of silica and water content on the glass transition temperature, T g , of MPEG2000-silica-LiClO 4 ormolytes was assessed by differential scanning calorimetry (DSC). The sol-gel synthesized ormolytes consisted of various amounts of poly(ethylene glycol) monomethylether (M.W. 2000 g/mol; i.e., MPEG2000) tethered to silica gel through the hydroxyl terminus via a urethane linkage. DSC features corresponding to physisorbed and hydrogen-bonded water, as well as the glass transition of the polyether, were identified. Both silica and LiClO 4 raise the T g and suppress crystallization of the polyether component. Water plasticizes the polyether and stoichiometrically solvates and sequesters Li + , thereby, lowering T g

Quantifying Silica Reactivity in Subsurface Environments: Reaction Affinity and Solute Matrix Controls on Quartz and SiO2 Glass Dissolution Kinetics

International Nuclear Information System (INIS)

Dove, Patricia M.

1999-01-01

Our goal is to develop a quantitative and mechanistic understanding of amorphous silica, SiO2(am), dissolution kinetics in aqueous solutions. A knowledge of fundamental controls on the reactivity of simple Si-O bonded phases is the baseline of behavior for understanding highly complex silica phases. In the Earth, silicate minerals comprise >70% of the crust and dominate virtually every subsurface system. More importantly for the objectives of this EMSP project, the silicates are important because compositionally complex glasses will become the front line of defense in containing radioactive wastes in the nation's long term and interim storage strategies. To date, the behavior of SiO2(am) is largely inferred from studies of the better known crystalline polymorphs (e.g. alpha-quartz). In the first step towards constructing a general model for amorphous silica reactivity in the complex fluid compositions of natural waters, we are determining the dissolution behavior as a function of temperature, solution pH and cation concentration. With these data we are determining relationships between SiO2 glass structure and dissolution rates in aqueous solutions, as described below

Lead recovery and high silica glass powder synthesis from waste CRT funnel glasses through carbon thermal reduction enhanced glass phase separation process

Energy Technology Data Exchange (ETDEWEB)

Xing, Mingfei [Henan Key Laboratory Cultivation Base of Mine Environmental Protection and Ecological Remediation, Henan Polytechnic University, Jiaozuo 454000 Henan China (China); Institute of Resource and Environment, Henan Polytechnic University, Jiaozuo 454000 Henan China (China); Fu, Zegang [Institute of Resource and Environment, Henan Polytechnic University, Jiaozuo 454000 Henan China (China); Wang, Yaping, E-mail: wangyp326@163.com [School of Surveying and Land Information Engineering, Henan Polytechnic University, Jiaozuo 454000, Henan China (China); Wang, Jingyu [Institute of Resource and Environment, Henan Polytechnic University, Jiaozuo 454000 Henan China (China); Zhang, Zhiyuan [Research Center for Eco-Environmental Sciences, Chinese Academy of Sciences, Beijing 100085 (China)

2017-01-15

Highlights: • CRT funnel glass was remelted with B{sub 2}O{sub 3} in reducing atmosphere. • A part of PbO was reduced into Pb and detached from the glass phase. • The rest of PbO and other metal oxides were mainly concentrated in the B{sub 2}O{sub 3} phase. • PbO enriched in the interconnected B{sub 2}O{sub 3} phase can be completely leached out by HNO{sub 3}. • High silica glass powder(SiO{sub 2} purity >95%) was obtained after the leaching process. - Abstract: In this study, a novel process for the removal of toxic lead from the CRT funnel glass and synchronous preparation of high silica glass powder was developed by a carbon-thermal reduction enhanced glass phase separation process. CRT funnel glass was remelted with B{sub 2}O{sub 3} in reducing atmosphere. In the thermal process, a part of PbO contained in the funnel glass was reduced into metallic Pb and detached from the glass phase. The rest of PbO and other metal oxides (including Na{sub 2}O, K{sub 2}O, Al{sub 2}O{sub 3,} BaO and CaO) were mainly concentrated in the boric oxide phase. The metallic Pb phase and boric oxide phase were completely leached out by 5 mol/L HNO{sub 3}. The lead removal rate was 99.80% and high silica glass powder (SiO{sub 2} purity >95 wt%) was obtained by setting the temperature, B{sub 2}O{sub 3} added amount and holding time at 1000 °C, 20% and 30 mins, respectively. The prepared high silicate glass powders can be used as catalyst carrier, semipermeable membranes, adsorbents or be remelted into high silicate glass as an ideal substitute for quartz glass. Thus this study proposed an eco-friendly and economical process for recycling Pb-rich electronic glass waste.

Quantifying silica reactivity in subsurface environments: Reaction affinity and solute matrix controls on quartz and SiO2 glass. 1997 annual progress report

International Nuclear Information System (INIS)

Dove, P.M.

1997-01-01

'The author reports the preliminary results of the experiments on the dissolution behavior of vitreous silica (v-SiO 2 ) into aqueous solutions of variable pH and ionic strength. The experiments are being conducted in mixed flow reactors with a high circulation rate that simulates constant-stirred conditions, the efficacy of which the authors discuss below. The preliminary results indicate that v-SiO 2 dissolves into aqueous solutions approximately two orders of magnitude more quickly than crystalline silica (e.g., quartz). With additional experiments, they will utilize the dissolution rate data as a framework for understanding the behavior of waste glass compositions in the subsurface. In other work related to the studies of glass reactivity, the author has written one book chapter that will be published as part of a proceedings for the CEA/VALRHO international nuclear waste disposal conference held in Mejannes le Clap, France. In separate work, she is presently writing a second book chapter for the volume entitled Adsorption on Silica Surfaces.'

Magnetic properties of Fe-Nd silica glass ceramics

Science.gov (United States)

Nayak, Manjunath T.; Desa, J. A. Erwin; Babu, P. D.

2018-04-01

Soda lime silica glass ceramics containing iron and neodymium have been synthesized. The XRD pattern revealed that the glass samples devitrified into multiple phases. Fe2O3 as an initial component converted into Fe3O4 in the sample during the synthesis, and was the main contributor to the magnetic property of the sample. The inclusion of Nd was found to enhance the magnetization of the sample at 5K. The coercivity of the sample increased with decrease in temperature from room to 5K.

Fluorescence lifetime studies of MeV erbium implanted silica glass

International Nuclear Information System (INIS)

Lidgard, A.; Polman, A.; Jacobsen, D.C.; Blonder, G.E.; Kistler, R.; Poate, J.M.; Becker, P.C.

1991-01-01

MeV erbium ion implantation into various SiO 2 glasses has been studied with the aim of incorporating the rare-earth dopant as an optically active ion in the silica network. The lifetime of the excited state ranges from 1.6 to 12.8 ms, depending on base material and implantation fluence. These results have positive implications for silica-based integrated optical technology. (Author)

Fluorescence lifetime studies of MeV erbium implanted silica glass

Energy Technology Data Exchange (ETDEWEB)

Lidgard, A.; Polman, A.; Jacobsen, D.C.; Blonder, G.E.; Kistler, R.; Poate, J.M.; Becker, P.C. (AT and T Bell Labs., Murray Hill, NJ (USA))

1991-05-23

MeV erbium ion implantation into various SiO{sub 2} glasses has been studied with the aim of incorporating the rare-earth dopant as an optically active ion in the silica network. The lifetime of the excited state ranges from 1.6 to 12.8 ms, depending on base material and implantation fluence. These results have positive implications for silica-based integrated optical technology. (Author).

Effect of different glasses in glass bonded zeolite

International Nuclear Information System (INIS)

Lewis, M.A.; Ackerman, J.P.; Verma, S.

1995-01-01

A mineral waste form has been developed for chloride waste salt generated during the pyrochemical treatment of spent nuclear fuel. The waste form consists of salt-occluded zeolite powders bound within a glass matrix. The zeolite contains the salt and immobilizes the fission products. The zeolite powders are hot pressed to form a mechanically stable, durable glass bonded zeolite. Further development of glass bonded zeolite as a waste form requires an understanding of the interaction between the glass and the zeolite. Properties of the glass that enhance binding and durability of the glass bonded zeolite need to be identified. Three types of glass, boroaluminosilicate, soda-lime silicate, and high silica glasses, have a range of properties and are now being investigated. Each glass was hot pressed by itself and with an equal amount of zeolite. MCC-1 leach tests were run on both. Soda-lime silicate and high silica glasses did not give a durable glass bonded zeolite. Boroaluminosilicate glasses rich in alkaline earths did bind the zeolite and gave a durable glass bonded zeolite. Scanning electron micrographs suggest that the boroaluminosilicate glasses wetted the zeolite powders better than the other glasses. Development of the glass bonded zeolite as a waste form for chloride waste salt is continuing

Development of a tuned interfacial force field parameter set for the simulation of protein adsorption to silica glass.

Science.gov (United States)

Snyder, James A; Abramyan, Tigran; Yancey, Jeremy A; Thyparambil, Aby A; Wei, Yang; Stuart, Steven J; Latour, Robert A

2012-12-01

Adsorption free energies for eight host-guest peptides (TGTG-X-GTGT, with X = N, D, G, K, F, T, W, and V) on two different silica surfaces [quartz (100) and silica glass] were calculated using umbrella sampling and replica exchange molecular dynamics and compared with experimental values determined by atomic force microscopy. Using the CHARMM force field, adsorption free energies were found to be overestimated (i.e., too strongly adsorbing) by about 5-9 kcal/mol compared to the experimental data for both types of silica surfaces. Peptide adsorption behavior for the silica glass surface was then adjusted using a modified version of the CHARMM program, which we call dual force-field CHARMM, which allows separate sets of nonbonded parameters (i.e., partial charge and Lennard-Jones parameters) to be used to represent intra-phase and inter-phase interactions within a given molecular system. Using this program, interfacial force field (IFF) parameters for the peptide-silica glass systems were corrected to obtain adsorption free energies within about 0.5 kcal/mol of their respective experimental values, while IFF tuning for the quartz (100) surface remains for future work. The tuned IFF parameter set for silica glass will subsequently be used for simulations of protein adsorption behavior on silica glass with greater confidence in the balance between relative adsorption affinities of amino acid residues and the aqueous solution for the silica glass surface.

Porous Silica Sol-Gel Glasses Containing Reactive V2O5 Groups

Science.gov (United States)

Stiegman, Albert E.

1995-01-01

Porous silica sol-gel glasses into which reactive vanadium oxide functional groups incorporated exhibit number of unique characteristics. Because they bind molecules of some species both reversibly and selectively, useful as chemical sensors or indicators or as scrubbers to remove toxic or hazardous contaminants. Materials also oxidize methane gas photochemically: suggests they're useful as catalysts for conversion of methane to alcohol and for oxidation of hydrocarbons in general. By incorporating various amounts of other metals into silica sol-gel glasses, possible to synthesize new materials with broad range of new characteristics.

Change in silica sources in Roman and post-Roman glass

International Nuclear Information System (INIS)

Aerts, A.; Velde, B.; Janssens, K.; Dijkman, W.

2003-01-01

Although Roman and post-Empire glasses found in Europe are reputed to have a very constant composition and hence source of components, it appears that some 4-5th century and later specimens show evidence of a different source of silica (sand) component. Zirconium and titanium are the discriminating elements. Data presented here for 278 specimens from 1st to 4th century German and Belgian samples indicate a strongly homogeneous Zr and Ti content; N: number of analyzed samples while 62 samples from Maastricht show low Zr-Ti contents from 1st to 3rd century samples while 4-5th century samples show a strong trend of concomitant Ti and Zr increase. If the high values of Zr-Ti represent a new source of silica (sand) the trend from low to high content suggests that a significant amount of low Zr-Ti glass was recycled to form these glass objects. Similar high Ti content can be seen in analysis results reported for other but not all 4-5th century samples found in northern Europe while earlier productions show typical low Ti contents. Although the fusing agent for these glasses seems to have always been natron (a mineral deposit in the Nile delta) from Hellenistic times to the 9th century, a change in the silica source, indicated by variation of the Ti and Zr content, could very well reflect the results of political instability of the 4-5th century exemplified by the fragmentation of the Roman Empire into two parts

Change in silica sources in Roman and post-Roman glass

Energy Technology Data Exchange (ETDEWEB)

Aerts, A.; Velde, B.; Janssens, K.; Dijkman, W

2003-04-18

Although Roman and post-Empire glasses found in Europe are reputed to have a very constant composition and hence source of components, it appears that some 4-5th century and later specimens show evidence of a different source of silica (sand) component. Zirconium and titanium are the discriminating elements. Data presented here for 278 specimens from 1st to 4th century German and Belgian samples indicate a strongly homogeneous Zr and Ti content; N: number of analyzed samples while 62 samples from Maastricht show low Zr-Ti contents from 1st to 3rd century samples while 4-5th century samples show a strong trend of concomitant Ti and Zr increase. If the high values of Zr-Ti represent a new source of silica (sand) the trend from low to high content suggests that a significant amount of low Zr-Ti glass was recycled to form these glass objects. Similar high Ti content can be seen in analysis results reported for other but not all 4-5th century samples found in northern Europe while earlier productions show typical low Ti contents. Although the fusing agent for these glasses seems to have always been natron (a mineral deposit in the Nile delta) from Hellenistic times to the 9th century, a change in the silica source, indicated by variation of the Ti and Zr content, could very well reflect the results of political instability of the 4-5th century exemplified by the fragmentation of the Roman Empire into two parts.

Change in silica sources in Roman and post-Roman glass

Science.gov (United States)

Aerts, A.; Velde, B.; Janssens, K.; Dijkman, W.

2003-04-01

Although Roman and post-Empire glasses found in Europe are reputed to have a very constant composition and hence source of components, it appears that some 4-5th century and later specimens show evidence of a different source of silica (sand) component. Zirconium and titanium are the discriminating elements. Data presented here for 278 specimens from 1st to 4th century German and Belgian samples indicate a strongly homogeneous Zr and Ti content; N: number of analyzed samples while 62 samples from Maastricht show low Zr-Ti contents from 1st to 3rd century samples while 4-5th century samples show a strong trend of concomitant Ti and Zr increase. If the high values of Zr-Ti represent a new source of silica (sand) the trend from low to high content suggests that a significant amount of low Zr-Ti glass was recycled to form these glass objects. Similar high Ti content can be seen in analysis results reported for other but not all 4-5th century samples found in northern Europe while earlier productions show typical low Ti contents. Although the fusing agent for these glasses seems to have always been natron (a mineral deposit in the Nile delta) from Hellenistic times to the 9th century, a change in the silica source, indicated by variation of the Ti and Zr content, could very well reflect the results of political instability of the 4-5th century exemplified by the fragmentation of the Roman Empire into two parts.

SAXS study of silica sols, gels and glasses obtained by the sol gel process

International Nuclear Information System (INIS)

Santos, D.I. dos; Aegerter, M.A.

1988-01-01

Systematic SAXS studies have been performed at the LURE Synchrotron, Orsay, using an intense beam of point like cross-section to obtain information about the sol -> humid gel -> dried gel -> silica glass transformation. The intensity curves have been analysed in term of power law in log-log plots, whose exponent is related to mass and surface fractal dimensions of the structure. It was found that almost all phases present fractal structures and for the case of basic gels, is of hierarchical nature. The aerogels are formed by a dense matrix, with a smooth surface and exhibit a very narrow auto-similarity range that gives a mass fractal dimension. (author) [pt

Quartz crystal reinforced quartz glass by spark plasma sintering

International Nuclear Information System (INIS)

Torikai, D.; Barazani, B.; Ono, E.; Santos, M.F.M.; Suzuki, C.K.

2011-01-01

The Spark Plasma Sintering presents fast processing time when compared to conventional sintering techniques. This allows to control the grain growth during sintering as well as the diffusion rate of a multi-material compounds, and make possible obtainment of functionally graded materials and nanostructured compounds. Powders of high purity silica glass and crystalline silica were sintered in a SPS equipment at temperatures around 1350° C, i.e., above the softening temperature of silica glass and below the melting temperature of quartz crystal. As a result, glass ceramics with pure silica glass matrix reinforced with crystalline alpha-quartz grains were fabricated at almost any desired range of composition, as well as controlled size of the crystalline reinforcement. X-ray diffraction and density measurements showed the possibility to manufacture a well controlled density and crystallinity glass-ceramic materials. (author)

Waste glass/metal interactions in brines

International Nuclear Information System (INIS)

Shade, J.W.; Pederson, L.R.; McVay, G.L.

1983-05-01

Leaching studies of MCC 76-68 glass in synthetic brines high in NaCl were performed from 50 to 150 0 C and included interactive testing with ductile iron and titanium. Hydrolysis of the glass matrix was generally slower in saturated brines than in deionized water, due to a lower solubility of silica in the brines. Inclusion of ductile iron in the tests resulted in accelerated leach rates because irion-silica reactions occurred which reduced the silica saturation fraction. At 150 0 C, iron also accelerated the rate of crystalline reaction product formation which were primarily Fe-bearing sepiolite and talc. 16 references

Glass formation and properties in the system calcia-gallia-silica

Science.gov (United States)

Angel, Paul W.; Ray, Chandra S.; Day, Delbert E.

1990-01-01

The glass-forming region in the calcia-gallia-silica system is studied and found to be fairly large, with a density of 3-4 g/cu cm, a refractive index of 1.6-1.73, an Abbe number of 35-58, a thermal expansion coefficient of 6.5-11.5 x 10 to the -7th/deg C, and a Vickers microhardness of 5.2-7.3 GPa. Crystalline phases are identified at the boundary of the glass-forming region. The structural groups in the glass-forming compositions are analyzed by infrared absorption spectroscopy.

Tetragonal zirconia quantum dots in silica matrix prepared by a modified sol-gel protocol

Science.gov (United States)

Verma, Surbhi; Rani, Saruchi; Kumar, Sushil

2018-05-01

Tetragonal zirconia quantum dots (t-ZrO2 QDs) in silica matrix with different compositions ( x)ZrO2-(100 - x)SiO2 were fabricated by a modified sol-gel protocol. Acetylacetone was added as a chelating agent to zirconium propoxide to avoid precipitation. The powders as well as thin films were given thermal treatment at 650, 875 and 1100 °C for 4 h. The silica matrix remained amorphous after thermal treatment and acted as an inert support for zirconia quantum dots. The tetragonal zirconia embedded in silica matrix transformed into monoclinic form due to thermal treatment ≥ 1100 °C. The stability of tetragonal phase of zirconia is found to enhance with increase in silica content. A homogenous dispersion of t-ZrO2 QDs in silica matrix was indicated by the mapping of Zr, Si and O elements obtained from scanning electron microscope with energy dispersive X-ray analyser. The transmission electron images confirmed the formation of tetragonal zirconia quantum dots embedded in silica. The optical band gap of zirconia QDs (3.65-5.58 eV) was found to increase with increase in zirconia content in silica. The red shift of PL emission has been exhibited with increase in zirconia content in silica.

Optical bleaching of bismuth implanted silica glass: A threshold effect

International Nuclear Information System (INIS)

Park, S.Y.; Magruder, R.H. III; Weeks, R.A.

1992-01-01

The near surface regions of high purity silica glass discs, Spectrosil A, were modified by implantation with bismuth ions at 160 key and room temperature. The glasses implanted with a nominal dose of 6x10 16 Bi/cm 2 at ∼5 μA/cm 2 were subsequently bleached with a 5.0 eV KrF pulsed excimer laser. The laser had an average pulse duration of ∼20 ns and repetition rate of 10 Hz. It was found that the bleaching was dependent upon the power density of the laser for a constant total integrated energy. Ion backscattering and optical absorption measurements were made before and after laser irradiation. Large changes in optical density and depth distribution of the implanted ions were observed at power densities of ≥45 mJ/cm 2 -pulse. Onset of threshold for bleaching of silica glass implanted with 6x10 16 Bi/cm 2 at 160 key and at room temperature is between 30 and 45 mJ/cm 2 -pulse

FABRICATION AND CHARACTERIZATION OF POLYIMIDE/POLYETHERSULFONE-FUMED SILICA MIXED MATRIX MEMBRANE FOR GAS SEPARATION

Directory of Open Access Journals (Sweden)

A. F. Ismail

2012-01-01

Full Text Available This study is performed primarily to investigate the feasibility of fumed silica as inorganic material towards gas separation performance of mixed matrix membrane. In this study, polyimide/polyethersulfone (PES-fumed silica mixed matrix membranes were casted using dry/wet technique. The results from the FESEM, DSC and FTIR analysis confirmed that the structure and physical properties of membrane is influenced by inorganic filler. FESEM’s cross-section view indicated good compatibility between polymer and fumed silica for all of range fumed silica used in this study. The gas separation performance of the mixed matrix membranes with fumed silica were relatively higher compared to that of the neat PI/PES membrane. PI/PES-fumed silica 5 wt% yielded significant selectivity enhancement of 7.21 and 40.47 for O2/N2, and CO2/CH4, respectively.

The Structure and Properties of Silica Glass Nanostructures using Novel Computational Systems

Science.gov (United States)

Doblack, Benjamin N.

The structure and properties of silica glass nanostructures are examined using computational methods in this work. Standard synthesis methods of silica and its associated material properties are first discussed in brief. A review of prior experiments on this amorphous material is also presented. Background and methodology for the simulation of mechanical tests on amorphous bulk silica and nanostructures are later presented. A new computational system for the accurate and fast simulation of silica glass is also presented, using an appropriate interatomic potential for this material within the open-source molecular dynamics computer program LAMMPS. This alternative computational method uses modern graphics processors, Nvidia CUDA technology and specialized scientific codes to overcome processing speed barriers common to traditional computing methods. In conjunction with a virtual reality system used to model select materials, this enhancement allows the addition of accelerated molecular dynamics simulation capability. The motivation is to provide a novel research environment which simultaneously allows visualization, simulation, modeling and analysis. The research goal of this project is to investigate the structure and size dependent mechanical properties of silica glass nanohelical structures under tensile MD conditions using the innovative computational system. Specifically, silica nanoribbons and nanosprings are evaluated which revealed unique size dependent elastic moduli when compared to the bulk material. For the nanoribbons, the tensile behavior differed widely between the models simulated, with distinct characteristic extended elastic regions. In the case of the nanosprings simulated, more clear trends are observed. In particular, larger nanospring wire cross-sectional radii (r) lead to larger Young's moduli, while larger helical diameters (2R) resulted in smaller Young's moduli. Structural transformations and theoretical models are also analyzed to identify

Structural modification of silica glass by laser scanning

International Nuclear Information System (INIS)

Zhao Jian; Sullivan, James; Zayac, John; Bennett, Ted D.

2004-01-01

The thermophysical nature of rapid CO 2 laser heating of silica glass is explored using a numerical simulation that considers the structural state of the glass, as characterized by the fictive temperature. The fictive temperature reflects the thermodynamic temperature at which the glass structure would be in equilibrium. To demonstrate that the thermophysical model can accurately predict the structural change in the glass, the fictive temperature is measured experimentally utilizing the fact that the fictive temperature change corresponds to a change of glass properties that can be revealed through wet chemical etching. The relationship between the etch rate and the fictive temperature is determined by preparing and etching samples of known fictive temperature. Wet chemical etching is used to measure the fictive temperature over the entire laser affected zone and the results are found to compare favorably with the results of the thermophysical model. The model and experimental measurements demonstrate that rapid laser processing results in an increased fictive temperature near the surface of the glass. The fictive temperature increase is about 1000 K and is uniform to within 5% over the laser affected zone. Near the boundary of this zone, the fictive temperature transitions abruptly to the value of the surrounding untreated glass

Room Temperature Imprint Using Crack-Free Monolithic SiO2-PVA Nanocomposite for Fabricating Microhole Array on Silica Glass

Directory of Open Access Journals (Sweden)

Shigeru Fujino

2015-01-01

Full Text Available This paper aims to fabricate microhole arrays onto a silica glass via a room temperature imprint and subsequent sintering by using a monolithic SiO2-poly(vinyl alcohol (PVA nanocomposite as the silica glass precursor. The SiO2-PVA suspension was prepared from fumed silica particles and PVA, followed by drying to obtain tailored SiO2-PVA nanocomposites. The dependence of particle size of the fumed silica particles on pore size of the nanocomposite was examined. Nanocomposites prepared from 7 nm silica particles possessed suitable mesopores, whereas the corresponding nanocomposites prepared from 30 nm silica particles hardly possessed mesopores. The pore size of the nanocomposites increased as a function of decreasing pH of the SiO2-PVA suspension. As a consequence, the crack-free monolithic SiO2-PVA nanocomposite was obtained using 7 nm silica particles via the suspension at pH 3. Micropatterns were imprinted on the monolithic SiO2-PVA nanocomposite at room temperature. The imprinted nanocomposite was sintered to a transparent silica glass at 1200°C in air. The fabricated sintered glass possessed the microhole array on their surface with aspect ratios identical to the mold.

Comparison of optical properties of Eu3+ ions in the silica gel glasses obtained by different preparation techniques

International Nuclear Information System (INIS)

Legendziewicz, J.; Sokolnicki, J.; Keller, B.; Borzechowska, M.; Strek, W.

1996-01-01

Silica-gel glasses doped with Eu 3+ ions were obtained by different preparation techniques. The absorption, emission and excitation spectra of the obtained glasses were measured in the range of 77-300 K. The energy levels diagrams of Eu 3+ ions were derived. An intensity analysis of f-f transitions was performed. In particular, polymeric structure behaviour of europium compounds entrapped in silica gel glasses was temperature controlled during the preparation of glasses. Their optical properties were investigated. (author)

Anisotropic surroundings effects on photo absorption of partially embedded Au nanospheroids in silica glass substrate

Energy Technology Data Exchange (ETDEWEB)

Meng, Xuan; Shibayama, Tamaki, E-mail: shiba@qe.eng.hokudai.ac.jp; Watanabe, Seiichi [Center for Advanced Research of Energy and Materials, Faculty of Engineering, Hokkaido University, Sapporo, Hokkaido 060–8628 (Japan); Yu, Ruixuan; Ishioka, Junya [Graduate School of Engineering, Hokkaido University, Sapporo, Hokkaido 060–8628 (Japan)

2015-02-15

The influence of a directly adjacent or an anisotropic surrounding medium alters the plasmonic properties of a nanoparticle because it provides a mechanism for symmetry breaking of the scattering. Given the success of ion irradiation induced embedment of rigid metallic nanospheroids into amorphous substrate, it is possible to examine the effect of the silica glass substrate on the plasmonic properties of these embedded nanospheroids. In this work presented here, discrete dipole approximation (DDA) calculations for the Au nanospheroids’ optical properties were performed based on 3–dimensional (3D) configuration extracted from planar SEM micrographs and cross–sectional TEM micrographs of the Au nanospheroids partially embedded in the silica glass, and the well–matched simulations with respect to the experimental measurements could demonstrate the dielectric constant at the near surface of silica glass decreased after Ar–ion irradiation.

Effects of alteration product precipitation on glass dissolution

Energy Technology Data Exchange (ETDEWEB)

Strachan, Denis M.; Neeway, James J.

2014-06-01

Understanding the mechanisms that control the durability of nuclear waste glass is paramount if reliable models are to be constructed so that the glass dissolution rate in a given geological repository can be calculated. Presently, it is agreed that (boro)silicate glasses dissolve in water at a rate dependent on the solution concentration of orthosilicic acid (H₄SiO₄) with higher [H₄SiO₄] leading to lower dissolution rates. Once the reaction has slowed as a result of the buildup of H₄SiO₄, another increase in the rate has been observed that corresponds to the precipitation of certain silica-bearing alteration products. However, it has also been observed that the concentration of silica-bearing solution species does not significantly decrease, indicating saturation, while other glass tracer elements concentrations continue to increase, indicating that the glass is still dissolving. In this study, we have used the Geochemist’s Workbench code to investigate the relationship between glass dissolution rates and the precipitation rate of a representative zeolitic silica-bearing alteration product, analcime [Na(AlSi₂O₆)∙H₂O]. To simplify the calculations, we suppressed all alteration products except analcime, gibbsite (Al(OH)₃), and amorphous silica. The pseudo-equilibrium-constant matrix for amorphous silica was substituted for the glass pseudo-equilibrium-constant matrix because it has been shown that silicate glasses act as a silica-only solid with respect to kinetic considerations. In this article, we present the results of our calculations of the glass dissolution rate at different values for the analcime precipitation rate constant and the effects of varying the glass dissolution rate constant at a constant analcime precipitation rate constant. From the simulations we conclude, firstly, that the rate of glass dissolution is dependent on the kinetics of

Silver metaphosphate glass wires inside silica fibers--a new approach for hybrid optical fibers.

Science.gov (United States)

Jain, Chhavi; Rodrigues, Bruno P; Wieduwilt, Torsten; Kobelke, Jens; Wondraczek, Lothar; Schmidt, Markus A

2016-02-22

Phosphate glasses represent promising candidates for next-generation photonic devices due to their unique characteristics, such as vastly tunable optical properties, and high rare earth solubility. Here we show that silver metaphosphate wires with bulk optical properties and diameters as small as 2 µm can be integrated into silica fibers using pressure-assisted melt filling. By analyzing two types of hybrid metaphosphate-silica fibers, we show that the filled metaphosphate glass has only negligible higher attenuation and a refractive index that is identical to the bulk material. The presented results pave the way towards new fiber-type optical devices relying on metaphosphate glasses, which are promising materials for applications in nonlinear optics, sensing and spectral filtering.

Giant basal spicule from the deep-sea glass sponge Monorhaphis chuni: synthesis of the largest bio-silica structure on Earth by silicatein

Science.gov (United States)

Wang, Xiao-hong; Zhang, Xue-hua; Schröder, Heinz C.; Müller, Werner E. G.

2009-09-01

Like all sponges (phylum Porifera), the glass sponges (Hexactinellida) are provided with an elaborate and distinct body plan, which relies on a filigree skeleton. It is constructed by an array of morphologically determined elements, the spicules. Schulze described the largest siliceous hexactinellid sponge on Earth, the up to 3 m high Monorhaphis chuni, collected during the German Deep Sea Expedition "Valdivia" (1898-1899). This species develops an equally large bio-silica structure, the giant basal spicule (3 m × 10 mm). Using these spicules as a model, one can obtain the basic knowledge on the morphology, formation, and development of silica skeletal elements. The silica matrix is composed of almost pure silica, endowing it with unusual optophysical properties, which are superior to those of man-made waveguides. Experiments suggest that the spicules function in vivo as a nonocular photoreception system. The spicules are also provided with exceptional mechanical properties. Like demosponges, the hexactinellids synthesize their silica enzymatically via the enzyme silicatein (27 kDa protein). This enzyme is located in/embedded in the silica layers. This knowledge will surely contribute to a further utilization and exploration of silica in biomaterial/biomedical science.

Celsian Glass-Ceramic Matrix Composites

Science.gov (United States)

Bansal, Narottam P.; Dicarlo, James A.

1996-01-01

Glass-ceramic matrix reinforced fiber composite materials developed for use in low dielectric applications, such as radomes. Materials strong and tough, exhibit low dielectric properties, and endure high temperatures.

Fibre-matrix bond strength studies of glass, ceramic, and metal matrix composites

Science.gov (United States)

Grande, D. H.; Mandell, J. F.; Hong, K. C. C.

1988-01-01

An indentation test technique for compressively loading the ends of individual fibers to produce debonding has been applied to metal, glass, and glass-ceramic matrix composites; bond strength values at debond initiation are calculated using a finite-element model. Results are correlated with composite longitudinal and interlaminar shear behavior for carbon and Nicalon fiber-reinforced glasses and glass-ceramics including the effects of matrix modifications, processing conditions, and high-temperature oxidation embrittlement. The data indicate that significant bonding to improve off-axis and shear properties can be tolerated before the longitudinal behavior becomes brittle. Residual stress and other mechanical bonding effects are important, but improved analyses and multiaxial interfacial failure criteria are needed to adequately interpret bond strength data in terms of composite performance.

Waste vitrification: prediction of acceptable compositions in a lime-soda-silica glass-forming system

International Nuclear Information System (INIS)

Gilliam, T.M.; Jantzen, C.M.

1996-10-01

A model is presented based upon calculated bridging oxygens which allows the prediction of the region of acceptable glass compositions for a lime-soda-silica glass-forming system containing mixed waste. The model can be used to guide glass formulation studies (e.g., treatability studies) or assess the applicability of vitrification to candidate waste streams

Fabrication and characterization of bioactive glass-ceramic using soda-lime-silica waste glass.

Science.gov (United States)

Abbasi, Mojtaba; Hashemi, Babak

2014-04-01

Soda-lime-silica waste glass was used to synthesize a bioactive glass-ceramic through solid-state reactions. In comparison with the conventional route, that is, the melt-quenching and subsequent heat treatment, the present work is an economical technique. Structural and thermal properties of the samples were examined by X-ray diffraction (XRD) and differential thermal analysis (DTA). The in vitro test was utilized to assess the bioactivity level of the samples by Hanks' solution as simulated body fluid (SBF). Bioactivity assessment by atomic absorption spectroscopy (AAS) and scanning electron microscopy (SEM) was revealed that the samples with smaller amount of crystalline phase had a higher level of bioactivity. Copyright © 2014 Elsevier B.V. All rights reserved.

Characterization of silica particles prepared via urease-catalyzed urea hydrolysis and activity of urease in sol–gel silica matrix

International Nuclear Information System (INIS)

Kato, Katsuya; Nishida, Masakazu; Ito, Kimiyasu; Tomita, Masahiro

2012-01-01

Highlights: ► Silica precipitation occurred via urease-catalytic reactions. ► Higher urease activity for silica synthesis enables mesostructure of silica–urease composites. ► Urease encapsulating in silica matrix retained high activity. - Abstract: Urease templated precipitation of silica synthesized by sol–gel chemistry produces a composite material allowing high urease activity. This study investigates the structural properties of the composite material that allow for the retention of the urease hydrolysis activity. Scanning (SEM) and transmission (TEM) electron microscopy reveal that the composite has a mesoporous structure composed of closely packed spherical structures ∼20–50 nm in diameter. Brunauer–Emmett–Teller (BET) analysis revealed that the surface area and pore volume of the composite prepared under the conditions of 50 mM urea and 25 °C is relatively high (324 m 2 /g and 1.0 cm 3 /g). These values are equivalent to those of usual mesoporous silica materials synthesized from the self-assembly of triblock copolymers as organic templates. In addition, after encapsulating in a sol–gel silica matrix, urease retained high activity (∼90% of the activity compared with native urease). Our results suggest a new method for synthesizing mesoporous silica materials with highly tunable pore sizes and shapes under mild conditions.

Size-Dependent Brittle-to-Ductile Transition in Silica Glass Nanofibers.

Science.gov (United States)

Luo, Junhang; Wang, Jiangwei; Bitzek, Erik; Huang, Jian Yu; Zheng, He; Tong, Limin; Yang, Qing; Li, Ju; Mao, Scott X

2016-01-13

Silica (SiO2) glass, an essential material in human civilization, possesses excellent formability near its glass-transition temperature (Tg > 1100 °C). However, bulk SiO2 glass is very brittle at room temperature. Here we show a surprising brittle-to-ductile transition of SiO2 glass nanofibers at room temperature as its diameter reduces below 18 nm, accompanied by ultrahigh fracture strength. Large tensile plastic elongation up to 18% can be achieved at low strain rate. The unexpected ductility is due to a free surface affected zone in the nanofibers, with enhanced ionic mobility compared to the bulk that improves ductility by producing more bond-switching events per irreversible bond loss under tensile stress. Our discovery is fundamentally important for understanding the damage tolerance of small-scale amorphous structures.

Viability for controlling long-term leaching of radionuclides from HLW glass by amorphous silica additives

International Nuclear Information System (INIS)

Inagaki, Y.; Uehara, S.

2004-01-01

Dissolution and deterioration experiments in coexistence system of amorphous silica and vitrified wastes have been executed in order to evaluating the effects of amorphous silica addition to high level radioactive vitrified waste (HLW glass) on suppression of nuclide leaching. Geo-chemical reaction mechanism among the vitrified waste, the amorphous silica and water was also evaluated. Dissolution of the silica network was suppressed by addition of the amorphous silica. However, the leaching of soluble nuclides like B proceeded depending on the hydration deterioration reaction. (A. Hishinuma)

Study of interaction in silica glass via model potential approach

Science.gov (United States)

Mann, Sarita; Rani, Pooja

2016-05-01

Silica is one of the most commonly encountered substances in daily life and in electronics industry. Crystalline SiO2 (in several forms: quartz, cristobalite, tridymite) is an important constituent of many minerals and gemstones, both in pure form and mixed with related oxides. Cohesive energy of amorphous SiO2 has been investigated via intermolecular potentials i.e weak Van der Waals interaction and Morse type short-range interaction. We suggest a simple atom-atom based Van der Waals as well as Morse potential to find cohesive energy of glass. It has been found that the study of silica structure using two different model potentials is significantly different. Van der Waals potential is too weak (P.E =0.142eV/molecule) to describe the interaction between silica molecules. Morse potential is a strong potential, earlier given for intramolecular bonding, but if applied for intermolecular bonding, it gives a value of P.E (=-21.92eV/molecule) to appropriately describe the structure of silica.

IR-spectroscopical investigations on the glass structure of porous and sintered compacts of colloidal silica gels

Science.gov (United States)

Clasen, Rolf; Hornfeck, M.; Theiss, Wolfgang

1991-08-01

The forming and sintering of fumed silica powders is an interesting route for the preparation of large, very pure or doped silica glasses with a precise geometry. The processing from the shaping of a porous compact to the sintering of transparent silica glass can be successfully investigated with optical spectroscopy. As only the dielectric function DF (a dielectric function is the square root of the complex refractive index) characterizes the material, the vibrational bands were calculated from reflectance measurements. In compacts of fine particles, the topology cannot be neglected. Therefore, the models describing topological effects are briefly reviewed. With these model calculations it could be proven that new bands in the compacts and the significant shifts in the reflectance spectra during sintering are mainly caused by topological effects and that changes in the glass structure play only a secondary role.

Fixation by ion exchange of toxic materials in a glass matrix

International Nuclear Information System (INIS)

Litovitz, T.A.; Simmons, C.J.; Simmons, J.H.; Macedo, P.B.

1981-01-01

A process for disposing of toxic materials such as radioactive waste comprises reacting a porous silicate glass or silica gel, having interconnected pores and alkali metal cations. Group 1b metal cations and/or ammonium cation bonded to silicon through divalent oxygen linkages on the internal surfaces of said pores, with a toxic material containing toxic cations as well as non-cationic portions. The toxic cations are capable of displacing the alkali metal cations, Group 1b metal cations and/or ammonium cations to provide a distribution of internal silicon-bonded toxic cation oxide groups within the pores of the glass or silica gel. (author)

On-line plutonium measurement by alpha counting using a silica glass sensor

International Nuclear Information System (INIS)

Edeline, J.C.; Furgolle, B.

1980-01-01

Some cerium activated high purity silica glasses are good sensors for ionising particles counting. These sensors may be used for measuring plutonium concentrations in corrosive solutions which are typical in reprocessing operations. The thickness of the sensor has been reduced to minimize beta sensitivity. The thin sensor is hold by molecular adhesion to a thick glass mount which is soldered to the stainless steel sample cell [fr

Fabrication of silica glass containing yellow oxynitride phosphor by the sol-gel process

Energy Technology Data Exchange (ETDEWEB)

Segawa, Hiroyo; Yoshimizu, Hisato; Hirosaki, Naoto; Inoue, Satoru, E-mail: SEGAWA.Hiroyo@nims.go.jp [National Institute for Materials Science, 1-1 Namiki, Tsukuba, Ibaraki 305-0044 (Japan)

2011-06-15

We have prepared silica glass by the sol-gel method and studied its ability to disperse the Ca-{alpha}-SiAlON:Eu{sup 2+} phosphor for application in white light emitting diodes (LEDs). The emission color generated by irradiating doped glass with a blue LED at 450 nm depended on the concentration of SiAlON and the glass thickness, resulting in nearly white light. The luminescence efficiency of 1-mm-thick glass depended on the SiAlON concentration, and was highest at 4 wt% SiAlON.

Evaluation of the glow curves of a new glass matrix

International Nuclear Information System (INIS)

Oliveira, Nathália S.; Souza, Samara P.; Ferreira, Pâmela Z.; Dantas, Noelio O.; Silva, Anielle C.A.; Neves, Lucio P.; Perini, Ana P.; Carrera, Betzabel N.S.; Watanabe, Shigueo

2017-01-01

Thermoluminescence is a dosimetric technique with may be used to personal, clinical, environmental and high doses. In this work a new glass matrix, with nominal composition of 20Li 2 CO 3 .10Al 2 O 3 .25BaO.45B 2 O 3 (mol%), was studied by the thermoluminescence technique. The glow curves was be analyzed, after the irradiation of this glass matrix with high doses. The results showed that this new glass matrix has a temperature peak in 260°C, which is ideal for dosimetry applications. (author)

Fixation by ion exchange of toxic materials in a glass matrix

International Nuclear Information System (INIS)

Simmons, C.J.; Simmons, J.H.; Macedo, P.B.; Litovitz, T.A.

1982-01-01

A process is reported for reacting a porous silicate or borosilicate glass or silica gel with alkali metal cations, Group lb cations and/or ammonium cations bonded to the silicon through divalent oxygen linkages on the internal surfaces of the pores. Ion exchange of the cations with toxic or radioactive cations was possible resulting in a distribution of internal silicon-bonded toxic cation oxide groups within the pores of the glass or silica gel. The ion exchange reaction may be done successfully with acidic, neutral or alkaline pH solutions. The aim of the immobilization is for permanent storage of hazardous materials such as Hg 2+ , Hg + , Cd 2+ , Tl + , Pb 2+ and radioactive cations

Characterization and enhanced nonlinear optical limiting response in carbon nanodots dispersed in solid-state hybrid organically modified silica gel glasses

Science.gov (United States)

Huang, Li; Zheng, Chan; Guo, Qiaohang; Huang, Dongdong; Wu, Xiukai; Chen, Ling

2018-02-01

Freely dispersed carbon nanodots (CNDs) were introduced into a 3-glycidoxy-propyltrimethoxysilane modified silicate gel glass (i.e. an organically modified silica or ORMOSIL) by a highly efficient and simple sol-gel process, which could be easily extended to prepare functional molecules/nanoparticles solid state optoelectronic devices. Scanning electron microscope imaging, Fourier transform infrared spectroscopy, pore structure measurements, ultraviolet-visible spectroscopy, and fluorescence spectroscopy were used to investigate the surface characteristics, structure, texture, and linear optical properties of the CND/SiO2 ORMOSIL gel glasses. Images and UV/Vis spectra confirmed the successful dispersion of CNDs in the ORMOSIL gel glass. The surface characteristics and pore structure of the host SiO2 matrix were markedly changed through the introduction of the CNDs. The linear optical properties of the guest CNDs were also affected by the sol-gel procedure. The nonlinear optical (NLO) properties of the CNDs were investigated by a nanosecond open-aperture Z-scan technique at 532 nm both in liquid and solid matrices. We found that the NLO response of the CNDs was considerably improved after their incorporation into the ORMOSIL gel glasses. Possible enhancement mechanisms were also explored. The nonlinear extinction coefficient gradually increased while the optical limiting (OL) threshold decreased as the CND doping level was increased. This result suggests that the NLO and OL properties of the composite gel glasses can be optimized by tuning the concentration of CNDs in the gel glass matrix. Our findings show that CND/SiO2 ORMOSIL gel glasses are promising candidates for optical limiters to protect sensitive instruments and human eyes from damage caused by high power lasers.

Study of interaction in silica glass via model potential approach

Energy Technology Data Exchange (ETDEWEB)

Mann, Sarita, E-mail: saritaiitr2003@gmail.com [Department of Physics, Panjab University, Chandigarh-160014 (India); Rani, Pooja [D.A.V. College, Sec-10, Chandigarh-160010 (India)

2016-05-06

Silica is one of the most commonly encountered substances in daily life and in electronics industry. Crystalline SiO{sub 2} (in several forms: quartz, cristobalite, tridymite) is an important constituent of many minerals and gemstones, both in pure form and mixed with related oxides. Cohesive energy of amorphous SiO{sub 2} has been investigated via intermolecular potentials i.e weak Van der Waals interaction and Morse type short-range interaction. We suggest a simple atom-atom based Van der Waals as well as Morse potential to find cohesive energy of glass. It has been found that the study of silica structure using two different model potentials is significantly different. Van der Waals potential is too weak (P.E =0.142eV/molecule) to describe the interaction between silica molecules. Morse potential is a strong potential, earlier given for intramolecular bonding, but if applied for intermolecular bonding, it gives a value of P.E (=−21.92eV/molecule) to appropriately describe the structure of silica.

Effects of ionizing radiations on the optical properties of ionic copper-activated sol-gel silica glasses

Science.gov (United States)

Al Helou, Nissrine; El Hamzaoui, Hicham; Capoen, Bruno; Ouerdane, Youcef; Boukenter, Aziz; Girard, Sylvain; Bouazaoui, Mohamed

2018-01-01

Studying the impact of radiations on doped silica glasses is essential for several technological applications. Herein, bulk silica glasses, activated with various concentrations of luminescent monovalent copper (Cu+), have been prepared using the sol-gel technique. Thereafter, these glasses were subjected to X- or γ-rays irradiation at 1 MGy(SiO2) accumulated dose. The effect of these ionizing radiations on the optical properties of these glasses, as a function of the Cu-doping content, were investigated using optical absorption and photoluminescence spectroscopies. Before any irradiation, the glass with the lowest copper concentration exhibits blue and green luminescence bands under UV excitation, suggesting that Cu+ ions occupy both cubic and tetragonal symmetry sites. However, at higher Cu-doping level, only the green emission band exists. Moreover, we showed that the hydroxyl content decreases with increasing copper doping concentration. Both X and γ radiation exposures induced visible absorption due to HC1 color centers in the highly Cu-doped glasses. In the case of the lower Cu-doped glass, the Cu+ sites with a cubic symmetry are transformed into sites with tetragonal symmetry.

Wettability of modified silica layers deposited on glass support activated by plasma

Energy Technology Data Exchange (ETDEWEB)

Terpiłowski, Konrad, E-mail: terpil@umcs.pl [Department of Physical Chemistry – Interfacial Phenomena, Faculty of Chemistry, Maria Curie-Sklodowska University, Lublin (Poland); Rymuszka, Diana [Department of Physical Chemistry – Interfacial Phenomena, Faculty of Chemistry, Maria Curie-Sklodowska University, Lublin (Poland); Goncharuk, Olena V.; Sulym, Iryna Ya.; Gun’ko, Vladimir M. [Chuiko Institute of Surface Chemistry, National Academy of Science of Ukraine, Kiev (Ukraine)

2015-10-30

Highlights: • New modified silica materials synthesis. • Support surface plasma activation. • Apparent surface free energy determination. • Equilibrium contact angle calculation. - Abstract: Fumed silica modified by hexamethyldisilazane [HDMS] and polydimethylsiloxane [PDMS] was dispersed in a polystyrene/chloroform solution. To increase adhesion between deposited silica layers and a glass surface, the latter was pretreated with air plasma for 30 s. The silica/polystyrene dispersion was deposited on the glass support using a spin coater. After deposition, the plates were dried in a desiccator for 24 h. Water advancing and receding contact angles were measured using the tilted plate method. The apparent surface free energy (γ{sub S}) was evaluated using the contact angle hysteresis approach. The surface topography was determined using the optical profilometry method. Contact angles changed from 59.7° ± 4.4 (at surface coverage with trimethylsilyl groups Θ = 0.14) to 155° ± 3.1 at Θ = 1. The value of γ{sub S} decreased from 51.3 ± 2.8 mJ/m{sup 2} (for the sample at the lowest value of Θ) to 1.0 ± 0.4 mJ/m{sup 2} for the most hydrophobic sample. Thus, some systems with a high degree of modification by HDMS showed superhydrophobicity, and the sliding angle amounted to about 16° ± 2.1.

Silica nanoparticles on front glass for efficiency enhancement in superstrate-type amorphous silicon solar cells

Science.gov (United States)

Das, Sonali; Banerjee, Chandan; Kundu, Avra; Dey, Prasenjit; Saha, Hiranmay; Datta, Swapan K.

2013-10-01

Antireflective coating on front glass of superstrate-type single junction amorphous silicon solar cells (SCs) has been applied using highly monodispersed and stable silica nanoparticles (NPs). The silica NPs having 300 nm diameter were synthesized by Stober technique where the size of the NPs was controlled by varying the alcohol medium. The synthesized silica NPs were analysed by dynamic light scattering technique and Fourier transform infrared spectroscopy. The NPs were spin coated on glass side of fluorinated tin oxide (SnO2: F) coated glass superstrate and optimization of the concentration of the colloidal solution, spin speed and number of coated layers was done to achieve minimum reflection characteristics. An estimation of the distribution of the NPs for different optimization parameters has been done using field-emission scanning electron microscopy. Subsequently, the transparent conducting oxide coated glass with the layer having the minimum reflectance is used for fabrication of amorphous silicon SC. Electrical analysis of the fabricated cell indicates an improvement of 6.5% in short-circuit current density from a reference of 12.40 mA cm-2 while the open circuit voltage and the fill factor remains unaltered. A realistic optical model has also been proposed to gain an insight into the system.

Silica nanoparticles on front glass for efficiency enhancement in superstrate-type amorphous silicon solar cells

International Nuclear Information System (INIS)

Das, Sonali; Kundu, Avra; Dey, Prasenjit; Saha, Hiranmay; Datta, Swapan K; Banerjee, Chandan

2013-01-01

Antireflective coating on front glass of superstrate-type single junction amorphous silicon solar cells (SCs) has been applied using highly monodispersed and stable silica nanoparticles (NPs). The silica NPs having 300 nm diameter were synthesized by Stober technique where the size of the NPs was controlled by varying the alcohol medium. The synthesized silica NPs were analysed by dynamic light scattering technique and Fourier transform infrared spectroscopy. The NPs were spin coated on glass side of fluorinated tin oxide (SnO 2 : F) coated glass superstrate and optimization of the concentration of the colloidal solution, spin speed and number of coated layers was done to achieve minimum reflection characteristics. An estimation of the distribution of the NPs for different optimization parameters has been done using field-emission scanning electron microscopy. Subsequently, the transparent conducting oxide coated glass with the layer having the minimum reflectance is used for fabrication of amorphous silicon SC. Electrical analysis of the fabricated cell indicates an improvement of 6.5% in short-circuit current density from a reference of 12.40 mA cm −2 while the open circuit voltage and the fill factor remains unaltered. A realistic optical model has also been proposed to gain an insight into the system. (paper)

Positron annihilation in vitreous silica glasses

International Nuclear Information System (INIS)

Uedono, Akira; Tanigawa, Shoichiro

1993-01-01

The annihilation characteristics of positrons in vitreous silica glasses (v-SiO 2 ) were studied by measurements of two-dimensional angular correlation of positron annihilation radiations and positron lifetime spectra. From the measurements, it was found that positrons and positronium (Ps) atoms mainly annihilate from trapped states by vacancy-type defects in v-SiO 2 . For v-SiO 2 specimens with cylindrical porous structures, annihilations of Ps with anisotropic momentum distributions were observed. This fact was attributed to the momentum uncertainty due to localization of Ps in a finite dimension of pores. This investigation showed possibilities for the detection of microstructures in v-SiO 2 by the positron annihilation technique. (author)

Rheology of Prepreg and Properties of Silica/bismaleimide Matrix Copper Clad Laminate

Directory of Open Access Journals (Sweden)

DAI Shankai

2017-08-01

Full Text Available The effects of the silica surface treated by coupling agents KH550, KH560 and KH570 on the rheological properties of bismaleimide (BMI resin system were investigated. The rigidity, coefficient of thermal expansion (CTE and thermal stability of the copper clad laminate (CCL were studied by DMA, TMA and TGA. The resin system containing silica surface treated by KH-560, comparing to KH550, KH570 and without surface treatment resin system has better rheological properties and low melt viscosity. The comprehensive properties of the copper clad laminate can be effectively improved by the introduction of silica in the resin system, exhibiting higher storage modulus and lower CTE compare to no silica in the CCL. When the silica mass fraction is 50%, the storage modulus is increased by 83% at 50℃, and the CTE below the glass transition temperature is decreased by 153%.

Metal-silica sol-gel materials

Science.gov (United States)

Stiegman, Albert E. (Inventor)

2002-01-01

The present invention relates to a single phase metal-silica sol-gel glass formed by the co-condensation of a transition metal with silicon atoms where the metal atoms are uniformly distributed within the sol-gel glass as individual metal centers. Any transition metal may be used in the sol-gel glasses. The present invention also relates to sensor materials where the sensor material is formed using the single phase metal-silica sol-gel glasses. The sensor materials may be in the form of a thin film or may be attached to an optical fiber. The present invention also relates to a method of sensing chemicals using the chemical sensors by monitoring the chromatic change of the metal-silica sol-gel glass when the chemical binds to the sensor. The present invention also relates to oxidation catalysts where a metal-silica sol-gel glass catalyzes the reaction. The present invention also relates to a method of performing oxidation reactions using the metal-silica sol-gel glasses. The present invention also relates to organopolymer metal-silica sol-gel composites where the pores of the metal-silica sol-gel glasses are filled with an organic polymer polymerized by the sol-gel glass.

Obtainment of silica nanofiber and its preliminary investigation and its effects as reinforcement in polymeric matrix

International Nuclear Information System (INIS)

Teixeira, R.S.; Oliveira, G.L.; Silva, F.D.C.; Teofilo, E. T.; Farias, R.C.; Menezes, R.R.

2016-01-01

Silica is widely used as fillers in polymers, and may confer flame retardant characteristics and improve mechanical properties. their use usually occurs as spherical nanoparticles or short fibers of. Studies using this reinforce in the form of nanofibers are promising. This analysis proposes to obtain silica nanofibers by blowspinning method in solution (SBS), and investigate its application in polymeric matrix. To synthesize the silica nanofibers it was used a precursor solution that has been subjected to SBS process and calcined for forming the silica layer. The DR-X indicated the obtainment of amorphous silica phase and SEM showed the the fibers are at the nanometer scale. Silica nanofibers were incorporated into filmogenic solution Polyamide 6. Preliminary results showed no improvement in mechanical properties. Future stages propose to verify that the surface chemical modification of silica nanofibers enables interaction charge / matrix. (author)

Preparation and Characterization of Lightweight Mullite-Silica Rich Glass Aggregates

Directory of Open Access Journals (Sweden)

Nan Li

2011-09-01

Full Text Available Phase compositions, microstructures and properties of four lightweight mullite-silica rich glass aggregates with high strength were investigated by X-ray diffractometry (XRD, scanning electron microscopy (SEM, and FactSage 6.2 software. It was found that the lightweight aggregates with higher Al2O3 content had higher mullite content, porosity and larger mullite crystallites, but lower content and viscosity of melt at elevated temperature. Most of Fe2O3 and TiO2 were incorporated in mullite and most of K2O and Na2O were in glass to reduce viscosity of melt at elevated temperature.

Refractive index and density in F- and Cl-doped silica glasses

International Nuclear Information System (INIS)

Kakiuchida, Hiroshi; Shimodaira, Noriaki; Sekiya, Edson H.; Saito, Kazuya; Ikushima, Akira J.

2005-01-01

The refractive index and density of fluorine- and chlorine-doped silica glasses were measured as functions of fictive temperature. The halogen concentrations were observed to have a refractive index or density that is independent of the fictive temperature were found. This implies that these properties are not affected by any heat-treatment conditions

Phase transitions and glass transition in a hyperquenched silica–alumina glass

DEFF Research Database (Denmark)

Zhang, Y.F.; Zhao, D.H.; Yue, Yuanzheng

2017-01-01

We investigate phase transitions, glass transition, and dynamic behavior in the hyperquenched 69SiO2–31Al2O3 (mol%) glass (SA glass). Upon reheating, the SA glass exhibits a series of thermal responses. Subsequent to the sub-Tg enthalpy release, the glass undergoes a large jump in isobaric heat...... capacity (ΔCp) during glass transition, implying the fragile nature of the SA glass. The mullite starts to form before the end of glass transition, indicating that the SA glass is extremely unstable against crystallization. After the mullite formation, the remaining glass phase exhibits an increased Tg...... and a suppressed ΔCp. The formation of cristobalite at 1553 K indicates the dominance of silica in the remaining glass matrix. The cristobalite gradually re-melts as the isothermal heat-treatment temperature is raised from 1823 to 1853 K, which is well below the melting point of cristobalite, while the amount...

Microwave studies on the dielectric properties of Sm3+ and Sm3+/CdTe doped sol-gel silica glasses

International Nuclear Information System (INIS)

Mathew, Siby; Rejikumar, P.R.; Yohannan, Jaimon; Mathew, K.T.; Unnikrishnan, N.V.

2008-01-01

Complex permittivity and conductivity studies of Samarium and Samarium/semiconductor cadmium telluride sol-gel silica glass samples were done. We use cavity perturbation technique at S band frequencies using TE 10p Mode. Structural evolution of the matrix on annealing is discussed based on FTIR analysis/XRD power diffraction. In cavity perturbation technique dielectric parameters like complex permittivity and conductivity are determined by measuring changes in resonant frequency due to small perturbation inside the cavity produced by the introduction of the samples. The addition of the semiconductor along with the samarium was found to lower the permittivity, loss factor and conductivity. Variations of permittivity values with annealing temperature find applications in IC Technology, optic fibre communication, etc. The Sm 3+ /CdTe doped glasses can also be used in the fabrication of new and improved materials for microwave electronic circuits and in electromagnetic shielding devices

Studies of natural and 60Co gamma radio-induced conduction in metaphosphate glasses and silica

International Nuclear Information System (INIS)

Mengual Gil, M.A.

1977-01-01

A study of natural and 60 Co gamma radio-induced conduction in metaphosphate glasses and silica is presented. The experimental study of natural conduction current in metaphosphate glasses in function of temperature enables to observe two different values of the activation energies in the respective temperature ranges T>223K and T [fr

Hydrophobic and optical characteristics of graphene and graphene oxide films transferred onto functionalized silica particles deposited glass surface

Science.gov (United States)

Yilbas, B. S.; Ibrahim, A.; Ali, H.; Khaled, M.; Laoui, T.

2018-06-01

Hydrophobic and optical transmittance characteristics of the functionalized silica particles on the glass surface prior and after transfer of graphene and graphene oxide films on the surface are examined. Nano-size silica particles are synthesized and functionalized via chemical grafting and deposited onto a glass surface. Graphene film, grown on copper substrate, was transferred onto the functionalized silica particles surface through direct fishing method. Graphene oxide layer was deposited onto the functionalized silica particles surface via spin coating technique. Morphological, hydrophobic, and optical characteristics of the functionalized silica particles deposited surface prior and after graphene and graphene oxide films transfer are examined using the analytical tools. It is found that the functionalized silica particles are agglomerated at the surface forming packed structures with few micro/nano size pores. This arrangement gives rise to water droplet contact angle and contact angle hysteresis in the order of 163° and 2°, respectively, and remains almost uniform over the entire surface. Transferring graphene and depositing graphene oxide films over the functionalized silica particles surface lowers the water droplet contact angle slightly (157-160°) and increases the contact angle hysteresis (4°). The addition of the graphene and graphene oxide films onto the surface of the deposited functionalized silica particles improves the optical transmittance.

The role of residual cracks on alkali silica reactivity of recycled glass aggregates

DEFF Research Database (Denmark)

Maraghechi, Hamed; Shafaatian, Seyed-Mohammad-Hadi; Fischer, Gregor

2012-01-01

Despite its environmental and economical advantages, crushed recycled glass has limited application as concrete aggregates due to its deleterious alkali-silica reaction. To offer feasible mitigation strategies, the mechanism of ASR should be well understood. Recent research showed that unlike some...

Quantifying Silica Reactivity in Subsurface Environments: Reaction Affinity and Solute Matrix Controls on Quartz and SiO2 Glass Dissolution Kinetics

International Nuclear Information System (INIS)

Dove, Patricia M.

2000-01-01

During the three years of this project, Professor Dove's laboratory made tremendous progress in understanding controls on amorphous silica dissolution kinetics in aqueous solutions. Our findings have already received considerable attention. In hydrothermal and low temperature studies, the work focused on determining quantitative and mechanistic controls on the most abundant silica polymorphs in Earth environments--quartz and amorphous silica. Our studies achieved goals set forth in the original proposal to establish a new quantitative understanding of amorphous silica dissolution. This support has resulted in 10 journal, 12 abstracts and 2 thesis publications. The PI and students were also recognized with 6 awards during this period. The 1998 EMSP conference in Chicago was an important meeting for our project. The symposium, enabled P.I. Dove to establish valuable contacts with ''users'' having specific needs for the findings of our EMSP project related to the urgency of problems in the Tanks Focus Area (TFA). Since that time, our working relations developed as Dove interacted with TFA scientists and engineers on the problems of waste glass properties. These interactions refined our experimental objectives to better meet their needs. Dove presented the results of EMSP research findings to a TFA subgroup at a Product Acceptance Workshop held in Salt Lake City during December 1998. The travel costs to attend this unanticipated opportunity were paid from EMSP project funds. In January 2000, Dove also attended a similar meeting in Atlanta with PNNL, SRL and BNF scientists/engineers to discuss new issues and make another level of decisions on the Product Acceptance goals. Our EMSP-funded research interfaced very well with the ongoing studies of Dr. Pete McGrail and colleagues in the Applied Geochemistry Group at PNNL. The value of our work to ''users'' was further demonstrated when Dove's EMSP-funded Postdoc, Dr. Jonathan Icenhower was hired by the same PNNL group. With

The anomalous yield behavior of fused silica glass

Science.gov (United States)

Schill, W.; Heyden, S.; Conti, S.; Ortiz, M.

2018-04-01

We develop a critical-state model of fused silica plasticity on the basis of data mined from molecular dynamics (MD) calculations. The MD data is suggestive of an irreversible densification transition in volumetric compression resulting in permanent, or plastic, densification upon unloading. The MD data also reveals an evolution towards a critical state of constant volume under pressure-shear deformation. The trend towards constant volume is from above, when the glass is overconsolidated, or from below, when it is underconsolidated. We show that these characteristic behaviors are well-captured by a critical state model of plasticity, where the densification law for glass takes the place of the classical consolidation law of granular media and the locus of constant-volume states defines the critical-state line. A salient feature of the critical-state line of fused silica, as identified from the MD data, that renders its yield behavior anomalous is that it is strongly non-convex, owing to the existence of two well-differentiated phases at low and high pressures. We argue that this strong non-convexity of yield explains the patterning that is observed in molecular dynamics calculations of amorphous solids deforming in shear. We employ an explicit and exact rank-2 envelope construction to upscale the microscopic critical-state model to the macroscale. Remarkably, owing to the equilibrium constraint the resulting effective macroscopic behavior is still characterized by a non-convex critical-state line. Despite this lack of convexity, the effective macroscopic model is stable against microstructure formation and defines well-posed boundary-value problems.

Structure and dynamics of spin-labeled insulin entrapped in a silica matrix by the sol-gel method.

Science.gov (United States)

Vanea, E; Gruian, C; Rickert, C; Steinhoff, H-J; Simon, V

2013-08-12

The structure and conformational dynamics of insulin entrapped into a silica matrix was monitored during the sol to maturated-gel transition by electron paramagnetic resonance (EPR) spectroscopy. Insulin was successfully spin-labeled with iodoacetamide and the bifunctional nitroxide reagent HO-1944. Room temperature continuous wave (cw) EPR spectra of insulin were recorded to assess the mobility of the attached spin labels. Insulin conformation and its distribution within the silica matrix were studied using double electron-electron resonance (DEER) and low-temperature cw-EPR. A porous oxide matrix seems to form around insulin molecules with pore diameters in the order of a few nanometers. Secondary structure of the encapsulated insulin investigated by Fourier transform infrared spectroscopy proved a high structural integrity of insulin even in the dried silica matrix. The results show that silica encapsulation can be used as a powerful tool to effectively isolate and functionally preserve biomolecules during preparation, storage, and release.

Ceramic fiber reinforced glass-ceramic matrix composite

Science.gov (United States)

Bansal, Narottam P. (Inventor)

1993-01-01

A slurry of BSAS glass powders is cast into tapes which are cut to predetermined sizes. Mats of continuous chemical vapor deposition (CVD)-SiC fibers are alternately stacked with these matrix tapes. This tape-mat stack is warm-pressed to produce a 'green' composite which is heated to burn out organic constituents. The remaining interim material is then hot-pressed to form a BSAS glass-ceramic fiber-reinforced composite.

Use of wasted foundry sand (WFS) as a partial substitute for silica in a soda lime glass

International Nuclear Information System (INIS)

Martin, A.C.; Ueno, O.K.; Folgueras, M.V.

2016-01-01

The waste foundry sand (WFS) is the main waste generates in foundry industries. Studies in the literature suggest the use of WFS in different materials, such as concrete, brick or asphalt. This work aims to partially replace the silica of a soda-lime glass by the WFS. The waste foundry sand has in its composition elements such as iron and aluminum that can affect the glass quality, which justifies the residue processing to reduce the impurity content. The treatments, that included mechanical agitation and thermal treatment, resulted in a slight decrease in the percent of iron with consequent increase of the silica content. After treatment, some sands were incorporated into the glass, that showed green color but with lower absorption intensity for the sand with less iron content. It was observed that it's possible to obtain glasses using WFS, however, there is difficulty in color controlling. (author

Thermal stability and practical applications of UV induced index changes in silica glasses

DEFF Research Database (Denmark)

Rathje, Jacob

2000-01-01

This thesis represents the partial fulfilment of the requirements for the danish ph.d. degree. I have been involved in both basic research of UV induced refractive index changes in silica glasses and in concrete applications. I have performed work on the thermal stability of UV-induced index...... the asymmetry showed good agreement with the obeserved data. The results were used to make a direction sensitive bend sensor of only one fiber. The sensor has further the advantage that it is insensitve to cross sensitivity from temperature, strin, and other external factors. Finally, an investigation of Nragg...... changes in silica glasses where a new continuous isochronal annealing method was introduced. The method was applied to gratings written in D2-loaded fibers and non-loaded fibers. For the non-loaded fibers the obtained results are in good agreement with what has previously been observed. For the D2-loaded...

Electrochemical redox reactions in solvated silica sol-gel glass

International Nuclear Information System (INIS)

Opallo, M.

2002-01-01

The studies of electrochemical redox reactions in solvated silica sol-gel glass were reviewed. The methodology of the experiments with emphasis on the direct preparation of the solid electrolyte and the application ultra microelectrodes was described. Generally, the level of the electrochemical signal is not much below that observed in liquid electrolyte. The current depends on time elapsed after gelation, namely the longer time, the smaller current. The differences between electrochemical behaviour of the redox couples in monoliths and thin layers were described. (author)

Ceramic fiber-reinforced monoclinic celsian phase glass-ceramic matrix composite material

Science.gov (United States)

Bansal, Narottam P. (Inventor); Dicarlo, James A. (Inventor)

1994-01-01

A hyridopolysilazane-derived ceramic fiber reinforced monoclinic celsian phase barium aluminum silicate glass-ceramic matrix composite material is prepared by ball-milling an aqueous slurry of BAS glass powder and fine monoclinic celsian seeds. The fibers improve the mechanical strength and fracture toughness and with the matrix provide superior dielectric properties.

Fabrication of 3D electro-thermal micro actuators in silica glass by femtosecond laser wet etch and microsolidics

Science.gov (United States)

Li, Qichao; Shan, Chao; Yang, Qing; Chen, Feng; Bian, Hao; Hou, Xun

2017-02-01

This paper demonstrates a novel electro-thermal micro actuator's design, fabrication and device tests which combine microfluidic technology and microsolidics process. A three-dimensional solenoid microchannel with high aspect ratio is fabricated inside the silica glass by an improved femtosecond laser wet etch (FLWE) technology, and the diameter of the spiral coil is only 200 μm. Molten alloy (Bi/In/Sn/Pb) with high melting point is injected into the three-dimensional solenoid microchannel inside the silica glass , then it solidifys and forms an electro-thermal micro actuator. The device is capable of achieving precise temperature control and quick response, and can also be easily integrated into MEMS, sensors and `lab on a chip' (LOC) platform inside the fused silica substrate.

Hydrophobic silica nanoparticles as reinforcing filler for poly (lactic acid polymer matrix

Directory of Open Access Journals (Sweden)

Pilić Branka M.

2016-01-01

Full Text Available Properties of poly (lactic acid (PLA and its nanocomposites, with silica nanoparticles (SiO2, as filler were investigated. Neat PLA films and PLA films with different percentage of hydrophobic fumed silica nanoparticles (0.2, 0.5, 1, 2, 3 and 5 wt. % were prepared by solution casting method. Several tools were used to characterize the influence of different silica content on crystalline behavior, and thermal, mechanical and barrier properties of PLA/SiO2 nanocomposites. Results from scanning electron microscope (SEM showed that the nanocomposite preparation and selection of specific hydrophobic spherical nano filler provide a good dispersion of the silica nanoparticles in the PLA matrix. Addition of silica nanoparticles improved mechanical properties, the most significant improvement being observed for lowest silica content (0.2wt.%. Barrier properties were improved for all measured gases at all loadings of silica nanoparticles. The degree of crystallinity for PLA slightly increased by adding 0.2 and 0.5 wt. % of nano filler. [Projekat Ministarstva nauke Republike Srbije, br. III46001

Electrodeposition of zinc–silica composite coatings: challenges in incorporating functionalized silica particles into a zinc matrix

Directory of Open Access Journals (Sweden)

Tabrisur Rahman Khan, Andreas Erbe, Michael Auinger, Frank Marlow and Michael Rohwerder

2011-01-01

Full Text Available Zinc is a well-known sacrificial coating material for iron and co-deposition of suitable particles is of interest for further improving its corrosion protection performance. However, incorporation of particles that are well dispersible in aqueous electrolytes, such as silica particles, is extremely difficult. Here, we report a detailed study of Zn–SiO2 nanocomposite coatings deposited from a zinc sulfate solution at pH 3. The effect of functionalization of the silica particles on the electro-codeposition was investigated. The best incorporation was achieved for particles modified with SiO2–SH, dithiooxamide or cysteamine; these particles have functional groups that can strongly interact with zinc and therefore incorporate well into the metal matrix. Other modifications (SiO2–NH3+, SiO2–Cl and N,N-dimethyldodecylamine of the silica particles lead to adsorption and entrapment only.

Chemical stability of soda-alumina-zirconia-silica glasses to Na, Na2S4, and S

International Nuclear Information System (INIS)

Bloom, S.I.; Bradley, J.; Nelson, P.A.; Roche, M.F.

1985-01-01

Twenty-two glasses with a broad range of compositions, spanning the quaternary soda-alumina-zirconia-silica system, have been prepared to allow characterization of the various properties of the system. The glasses were characterized by their resistivities, energies of activation for conduction, and glass transition temperatures. The glasses were screened for compositions of especially high chemical stability of static corrosion tests in Na, S, and Na 2 S 4 for 1000h at 400 0 C. Among the glasses tested, the high soda glasses showed the smallest weight change after exposure to the three media. The weight change observed was comparable to that seen in the Dow borate glass and beta'' alumina

Synthesis of multilayered structure of nano-dimensional silica glass/reduced graphene oxide for advanced electrochemical applications.

Science.gov (United States)

Ghosh, Arnab; Miah, Milon; Majumder, Chinmoy; Bag, Shekhar; Chakravorty, Dipankar; Saha, Shyamal Kumar

2018-03-28

During the past few years, intensive research has been carried out to design new functional materials for superior electrochemical applications. Due to low storage capacity and low charge transport, silica based glasses have not yet been investigated for their supercapacitive behavior. Therefore, in the present study, a multilayered structure of silica-based nanoglass and reduced graphene oxide has been designed to remarkably enhance the specific capacitance by exploiting the porosity, large surface area, sufficient dangling bonds in the nanoglass and high electrical conductivity of rGO. The charge transport in the composite structure is also investigated to understand the electrochemical properties. It is found that Simmons tunneling or direct tunneling is the dominant mechanism of charge conduction between the graphene layers via the potential barrier of silica nanoglass phase. We believe that this study will open up a new area in the design of glass-based two-dimensional nanocomposites for superior supercapacitor applications.

Studies of glasses by positron annihilation

International Nuclear Information System (INIS)

Brauer, G.; Boden, G.

1981-04-01

Investigations of silica glasses, pyrocerams and metallic glasses by positron annihilation (lifetime, Doppler broadening) are presented. The measurements on silica glasses showed, that silica glass fused from naturally occuring quartz exhibits a higher order than that one produced from SiCl 4 . Furthermore it was found that the order of silica glasses increases after heat treatment above 900 0 C. Thus the X-amorphous state of silica glasses could be characterized by positron annihilation what is impossible at present by diffraction methods. (author)

Optical constants of quartz, vitreous silica and neutron-irradiated vitreous silica. II. Analysis of the infrared spectrum of vitreous silica

Energy Technology Data Exchange (ETDEWEB)

Gaskell, P H [Cambridge Univ. (UK). Cavendish Lab.; Johnson, D W [Pilkington Research and Development Laboratories, Lathom, nr. Ormskirk, Lancashire, UK

1976-03-01

Optical constant data for vitreous silica and neutron-irradiated vitreous silica, given in part I are examined in an attempt to gain further knowledge of the structure of the glass. Strong features of the spectrum can be described by band broadening parameters, which are calculated using an extension of the Wilson GF matrix method, and are shown to be quantitatively related to the distribution of Si-O distances and oxygen bond angles obtained from X-ray scattering data. The approximation commonly used to generate the optically active vibrational spectra of glasses, namely to form the product of the vibrational density of states function and a weakly frequency-dependent intensity factor gives a relatively poor representation of the experimental spectrum. The magnitude of 'disorder-induced' absorption in regions well away from the major bands is semi-quantitatively estimated by subtracting the contributions of the major bands. Interpretation of some of the features of this difference spectrum is possible in terms of vibrations of nonbridging oxygen atoms, but if this interpretation is correct, it is necessary to postulate clustering of 'dangling' oxygen atoms, which would not be consistent with a random network model for the structure. An alternative explanation, that the vibrations are framework modes, leads to the conclusion that the preferred configuration in vitreous silica resembles the arrangement of silicon-oxygen tetrahedra in cristobalite.

Effect of colloidal nano-silica on the mechanical and physical behaviour of waste-glass cement mortar

International Nuclear Information System (INIS)

Aly, M.; Hashmi, M.S.J.; Olabi, A.G.; Messeiry, M.; Abadir, E.F.; Hussain, A.I.

2012-01-01

Highlights: → Glass powder (GP) and nano-silica (CS) were used as a partial cement replacement in cement mortar (CM). → No damaging effect can be detected due to the reaction between GP and CM with particle size up to 75 μm. → Hybrid combination of GP/CS greatly improved mechanical properties and microstructure of CM. -- Abstract: This paper presents a laboratory study of the properties of colloidal nano-silica (CS)/waste glass cement composites. The microstructure, alkali-silica reaction (ASR), and the mechanical properties of cement mortars containing waste glass powder (WG) as a cement replacement with and without CS are investigated and compared with plain mortar. In addition, the hydration of cement compounds was followed by differential thermal analysis (DTA), thermogravimetric analysis (TGA), and X-ray diffraction (XRD). The results show that incorporation of WG has a positive effect on the mechanical properties of cement mortars especially when CS is presented. In addition, the DTA/TGA results and XRD analysis show a reduction in the calcium hydroxide (CH) content in mortars with both WG and a hybrid combination of WG and CS. This confirms the improvement of mechanical properties and the occurrence of the pozzolanic reaction after 28 days of hydration.

Structural changes in irreversibly densified fused silica: implications for the chemical resistance of high level nuclear waste glasses

International Nuclear Information System (INIS)

Susman, S.; Volin, K.J.; Liebermann, R.C.; Gwanmesia, G.D.; Yanbin Wang

1990-01-01

Energetic photons and energetic particles create changes in the structure of nuclear waste glasses. These can be observed as changes in the average bulk physical properties. For example, exposure of fused silica to high doses of neutron bombardment leads to a maximum average compaction of 3%. However, this does not reveal the true extent of the densification that takes place at a microscopic level. Recent advances in high pressure technology have yielded large samples of fused silica which have been permanently densified under pressure and whose bulk density has been increased by 20%. These specimens have an overall structure that replicates the microstructure of a radiation damaged glass. Measurements have been made for the first time of the structural changes in this pressure densified vitreous silica using neutron diffraction and infrared absorption spectrometry. Extensive alterations in intermediate range order have been observed with consequent anticipated changes in chemical reactivity. The resistance of high level waste glasses to leaching by groundwater must be considered in light of these experimental findings. (author)

Thermosetting Polymer-Matrix Composites for Strucutral Repair Applications

Energy Technology Data Exchange (ETDEWEB)

Goertzen, William Kirby [Iowa State Univ., Ames, IA (United States)

2007-12-01

Several classes of thermosetting polymer matrix composites were evaluated for use in structural repair applications. Initial work involved the characterization and evaluation of woven carbon fiber/epoxy matrix composites for structural pipeline repair. Cyanate ester resins were evaluated as a replacement for epoxy in composites for high-temperature pipe repair applications, and as the basis for adhesives for resin infusion repair of high-temperature composite materials. Carbon fiber/cyanate ester matrix composites and fumed silica/cyanate ester nanocomposites were evaluated for their thermal, mechanical, viscoelastic, and rheological properties as they relate to their structure, chemistry, and processing characteristics. The bisphenol E cyanate ester under investigation possesses a high glass transition temperature, excellent mechanical properties, and unique ambient temperature processability. The incorporate of fumed silica served to enhance the mechanical and rheological properties of the polymer and reduce thermal expansion without sacrificing glass transition or drastically altering curing kinetics. Characterization of the composites included dynamic mechanical analysis, thermomechanical analysis, differential scanning calorimetry, thermogravimetric analysis, rheological and rheokinetic evaluation, and transmission electron microscopy.

Optical transmission of silica glass during swift-heavy-ion implantation

International Nuclear Information System (INIS)

Plaksin, Oleg; Okubo, Nariaki; Takeda, Yoshihiko; Amekura, Hiroshi; Kono, Kenichiro; Kishimoto, Naoki

2004-01-01

Metal nanoparticles fabricated by heavy-ion implantation of insulators are promising for non-linear optical applications. Spectra of optical transmission of silica glass in the visible region were measured during and after implantation of 3 MeV Cu 2+ ions. Three absorption bands contribute to the spectra: transient absorption (TA) at 2.34 eV, a surface plasmon resonance (SPR) peak at 2.21 eV and a tail of residual absorption (RA), which increases when the photon energy is increased from 2.2 to 2.6 eV. The TA and a change of the SPR peak strongly contribute to the total transient absorption obtained as the difference in absorption during and after irradiation. The effect of RA shows up as a decrease of absorption after switching on the ion beam. The TA provides a means for selective electronic excitation by a laser during implantation of silica glass. The precipitation of Cu atoms and the growth of Cu nanoparticles are well distinguishable stages of nanoparticle formation. The SPR peak appears at a fluence of 3.3 x 10 16 ions/cm 2 , corresponding to the onset of precipitation. At fluences higher than 3.4 x 10 16 ions/cm 2 , when the growth of nanoparticles predominates, the fluence dependence of the SPR peak is linear

Effect of sintering temperature on physical, structural and optical properties of wollastonite based glass-ceramic derived from waste soda lime silica glasses

Directory of Open Access Journals (Sweden)

Karima Amer Almasri

Full Text Available The impact of different sintering temperatures on physical, optical and structural properties of wollastonite (CaSiO3 based glass-ceramics were investigated for its potential application as a building material. Wollastonite based glass-ceramics was provided by a conventional melt-quenching method and followed by a controlled sintering process. In this work, soda lime silica glass waste was utilized as a source of silicon. The chemical composition and physical properties of glass were characterized by using Energy Dispersive X-ray Fluorescence (EDXRF and Archimedes principle. The Archimedes measurement results show that the density increased with the increasing of sintering temperature. The generation of CaSiO3, morphology, size and crystal phase with increasing the heat-treatment temperature were examined by field emission scanning electron microscopy (FESEM, Fourier transforms infrared reflection spectroscopy (FTIR, and X-ray diffraction (XRD. The average calculated crystal size gained from XRD was found to be in the range 60 nm. The FESEM results show a uniform distribution of particles and the morphology of the wollastonite crystal is in relict shapes. The appearance of CaO, SiO2, and Ca-O-Si bands disclosed from FTIR which showed the formation of CaSiO3 crystal phase. In addition to the calculation of the energy band gap which found to be increased with increasing sintering temperature. Keywords: Soda lime silica glass, Wollastonite, Sintering, Structural properties, Optical properties

Alkali-silica reactivity of expanded glass granules in structure of lightweight concrete

International Nuclear Information System (INIS)

Bumanis, G; Bajare, D; Korjakins, A; Locs, J

2013-01-01

Main component in the lightweight concrete, which provides its properties, is aggregate. A lot of investigations on alkali silica reaction (ASR) between cement and lightweight aggregates have been done with their results published in the academic literature. Whereas expanded glass granules, which is relatively new product in the market of building materials, has not been a frequent research object. Therefore lightweight granules made from waste glass and eight types of cement with different chemical and mineralogical composition were examined in this research. Expanded glass granules used in this research is commercially available material produced by Penostek. Lightweight concrete mixtures were prepared by using commercial chemical additives to improve workability of concrete. The aim of the study is to identify effect of cement composition to the ASR reaction which occurs between expanded glass granules and binder. Expanded glass granules mechanical and physical properties were determined. In addition, properties of fresh and hardened concrete were determined. The ASR test was processed according to RILEM AAR-2 testing recommendation. Tests with scanning electron microscope and microstructural investigations were performed for expanded glass granules and hardened concrete specimens before and after exposing them in alkali solution

The Effect of Composition on Spinel Crystals Equilibrium in Low-Silica High-Level Waste Glasses

International Nuclear Information System (INIS)

Jiricka, Milos; Hrma, Pavel R.; Vienna, John D.

2003-01-01

The liquidus temperature (TL) and the equilibrium mass fraction of spinel were measured in the regions of low-silica (less than 42 mass% SiO2) high-level waste borosilicate glasses within the spinel primary phase field as functions of glass composition. The components that varied, one at a time, were Al2O3, B2O3, Cr2O3, Fe2O3, Li2O, MnO, Na2O, NiO, SiO2, and ZrO2. The effects of Al2O3, B2O3, Fe2O3, NiO, SiO2, and ZrO2 on the TL in this region and in glasses with 42 to 56 mass% SiO2 were similar. However, in the low-silica region, Cr2O3 increased the TL substantially less, and Li2O and Na2O decreased the TL significantly less than in the region with 42 to 56 mass% SiO2. The effect of MnO on the TL of the higher SiO2 glasses is not yet understood with sufficient accuracy. The temperature at which the equilibrium mass fraction of spinel was 1 mass% was 25C to 64C below the TL

Characterization of the calcium-fluoroaluminosilicate glass prepared by a non-hydrolytic sol-gel route for future dental application as glass ionomer cement

Directory of Open Access Journals (Sweden)

Alexandre Cestari

2009-06-01

Full Text Available Glass ionomer cements are widely employed in dentistry due to their physical, biological and mainly anti-caries properties. Glass ionomers consist of an aluminosilicate glass matrix modified with other elements, and they contain large quantities of fluorine. In this study, we report on the preparation of calcium-fluoroaluminosilicate glasses by a nonhydrolytic sol-gel route as an alternative approach to obtaining alumina-silica matrices. The glass powders were prepared via the non-hydrolytic sol-gel method, by mixing AlCl3, SiCl4, CaF2, AlF3, NaF, and AlPO4. The powders were studied by thermal analysis (TG/DTA/DSC, photoluminescence (PL, nuclear magnetic resonance (NMR27Al-29Si, and X ray diffraction (XRD. TG/DTA/DSC analyses revealed a constant mass loss due to structural changes during the heating process, which was confirmed by NMR and PL. A stable aluminosilicate matrix with potential future application as a glass ionomer base was obtained.

The effect of heat treatment on the magnitude and composition of residual gas in sealed silica glass ampoules

Science.gov (United States)

Palosz, W.; Szofran, F. R.; Lehoczky, S. L.

1994-01-01

The residual gas pressure and composition in sealed silica glass ampoules as a function of different treatment procedures has been investigated. The dependence of the residual gas on the outgassing and annealing parameters has been determined. The effects of the fused silica brand, of the ampoule fabrication, and of post-outgassing procedures have been evaluated.

Ce+3-and Tb+3-luminescence in glasses. Ce+3-activated bulk silica and silica thin films. An α-particle detector based on a Ce+3-activated silica thin film. A Ce+3-Tb+3-energy transfer in a high melting point phosphate glass

International Nuclear Information System (INIS)

Heindl, R.; Loriers, J.; Sella, J.C.; Robert, A.

1984-07-01

While many Ce +3 -activated glasses of different type emit strongly under UV (253,7 nm) and β-ray excitation, only the commercial silicate glass NE 905 shows an useful emission when exposed to α-particles. Only phosphate glasses have give the green Tb +3 -emission, when doped by it, under UV and α and β radiation. Sputtered films of Ce +3 -activated silica have appropriate luminescence properties, adherence to the substrate and a perfect chemical resistance to hot nitric acid. An α-particle detector has been built which has permitted the quantitative detection of plutonium in the presence of other radiative ions

Vibrational mode frequencies of silica species in SiO2-H2O liquids and glasses from ab initio molecular dynamics.

Science.gov (United States)

Spiekermann, Georg; Steele-MacInnis, Matthew; Schmidt, Christian; Jahn, Sandro

2012-04-21

Vibrational spectroscopy techniques are commonly used to probe the atomic-scale structure of silica species in aqueous solution and hydrous silica glasses. However, unequivocal assignment of individual spectroscopic features to specific vibrational modes is challenging. In this contribution, we establish a connection between experimentally observed vibrational bands and ab initio molecular dynamics (MD) of silica species in solution and in hydrous silica glass. Using the mode-projection approach, we decompose the vibrations of silica species into subspectra resulting from several fundamental structural subunits: The SiO(4) tetrahedron of symmetry T(d), the bridging oxygen (BO) Si-O-Si of symmetry C(2v), the geminal oxygen O-Si-O of symmetry C(2v), the individual Si-OH stretching, and the specific ethane-like symmetric stretching contribution of the H(6)Si(2)O(7) dimer. This allows us to study relevant vibrations of these subunits in any degree of polymerization, from the Q(0) monomer up to the fully polymerized Q(4) tetrahedra. Demonstrating the potential of this approach for supplementing the interpretation of experimental spectra, we compare the calculated frequencies to those extracted from experimental Raman spectra of hydrous silica glasses and silica species in aqueous solution. We discuss observed features such as the double-peaked contribution of the Q(2) tetrahedral symmetric stretch, the individual Si-OH stretching vibrations, the origin of the experimentally observed band at 970 cm(-1) and the ethane-like vibrational contribution of the H(6)Si(2)O(7) dimer at 870 cm(-1).

OD bands in the IR spectra of a deuterated soda-lime-silica glass

Energy Technology Data Exchange (ETDEWEB)

Peuker, C.; Brzezinka, K.W.; Gaber, M.; Kohl, A.; Geissler, H. [Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin (Germany)

2001-07-01

IR spectra of a deuterated glass of the composition (in mol%) 16 Na{sub 2}O . 10 CaO . 74 SiO{sub 2} complete earlier spectroscopic studies on water-poor soda-lime-silica glasses. The approved IR spectroscopic method of the deuterium exchange allows a reliable assignment of the hydroxyl bands also in the case of glasses. By spectra comparison the assignment of the IR bands at 3500 and 2800 cm{sup -1} to hydroxyl groups with different hydrogen bonding is verified. The IR band at about 4500 cm{sup -1} is interpreted as both a combination of the stretching vibrations {nu}O-H and {nu}Si-OH and a combination of the stretching vibration {nu}O-H and the deformation vibration {delta}SiOH. The bands at 1763 and 1602 cm{sup -1} are attributed to combination vibrations of the glass network. (orig.)

Study of a new glass matrix by the thermoluminescence technique

International Nuclear Information System (INIS)

Ferreira, Pamela Z.; Vedovato, Uly P.; Cunha, Diego M. da; Dantas, Noelio O.; Silva, Anielle C.A.; Neves, Lucio P.; Perini, Ana P.; Carrera, Betzabel N.S.; Watanabe, Shigueo

2015-01-01

The thermoluminescence technique is widely used for both personal and for high-dose dosimetry. In this work, the thermoluminescence technique was utilized to study a new glass matrix, with nominal composition of 20Li 2 CO 3 .10Al 2 O 3 .20BaO.50B 2 O 3 (mol%), irradiated with different doses in a 60 Co source. The glow curves and the dose-response curve were obtained for radiation doses between 50 Gy and 900 Gy. The results showed that this new glass matrix presents potential use in high-dose dosimetry. (author)

Preparation of SnO_2-Glass Composite Containing Cu Particles Reduced from Copper Ions in Glass Matrix : Effect of Glass Particle Size on Microstructure and Electrical Property

OpenAIRE

Haruhisa, SHIOMI; Kaori, UMEHARA; Faculty of Engineering and Design, Kyoto Institute of Technology; Faculty of Engineering and Design, Kyoto Institute of Technology

2000-01-01

An attempt was made to improve the electrical properties of SnO_2-glass composites by dispersing Cu particles with low resistivity and positive temperature coefficient of resistance(TCR)in the glass matrix. Cu metal particles were precipitated by reducing Cu_2O previously dissolved into the matrix glass by adding LaB_6 as a reducing agent. The effect of the glass particle size, which influences the homogeneity of LaB_6 dispersion in the powder mixture before firing, on the Cu precipitation in...

High-performance geometric phase elements in silica glass

Directory of Open Access Journals (Sweden)

Rokas Drevinskas

2017-06-01

Full Text Available High-precision three-dimensional ultrafast laser direct nanostructuring of silica glass resulting in multi-layered space-variant dielectric metasurfaces embedded in volume is demonstrated. Continuous phase profiles of nearly any optical component are achieved solely by the means of geometric phase. Complex designs of half-wave retarders with 90% transmission at 532 nm and >95% transmission at >1 μm, including polarization gratings with efficiency nearing 90% and computer generated holograms with a phase gradient of ∼0.8π rad/μm, were fabricated. A vortex half-wave retarder generating a single beam optical vortex with a tunable orbital angular momentum of up to ±100ℏ is shown. The high damage threshold of silica elements enables the simultaneous optical manipulation of a large number of micro-objects using high-power laser beams. Thus, the continuous control of torque without altering the intensity distribution was implemented in optical trapping demonstration with a total of 5 W average power, which is otherwise impossible with alternate beam shaping devices. In principle, the direct-write technique can be extended to any transparent material that supports laser assisted nanostructuring and can be effectively exploited for the integration of printed optics into multi-functional optoelectronic systems.

Investigation of the mechanical properties of silica glasses by indentation tests

Energy Technology Data Exchange (ETDEWEB)

Juhasz, A. (Inst. for General Physics, Lorand Eoetvoes Univ., Budapest (Hungary)); Voeroes, G. (Inst. for General Physics, Lorand Eoetvoes Univ., Budapest (Hungary)); Tasnadi, P. (Inst. for General Physics, Lorand Eoetvoes Univ., Budapest (Hungary)); Kovacs, I. (Inst. for General Physics, Lorand Eoetvoes Univ., Budapest (Hungary)); Somogyi, I. (Inst. for General Physics, Lorand Eoetvoes Univ., Budapest (Hungary) Brody Research Center, G.E. Tungsram, Budapest (Hungary)); Szoellosi, J. (Inst. for General Physics, Lorand Eoetvoes Univ., Budapest (Hungary) Brody Research Center, G.E. Tungsram, Budapest (Hungary))

1993-11-01

Soda lime silica glasses were investigated by continuous indentation tests. The load indentation depth curves were taken during the loading as well as the unloading period by a computer controlled MTS machine. It was found that the loading force is a quadratic function of the indentation depth during both the loading and unloading stage of the deformation. The validity of the quadratic relationship in the case of the unloading stage seems to be characteristic only for glasses. Taking into account the elastic relaxation of the indentation depth an estimation is given for the size of the hydrostatic core which is necessary to symmetrize the stress field around the indenter. Using the measured length of the radial cracks started from the corners of the Vickers indentation pattern the K[sub IC] values were calculated. (orig.).

Borosilicate glass as a matrix for the immobilization of Savannah River Plant waste

International Nuclear Information System (INIS)

Plodinec, M.J.; Wicks, G.G.; Bibler, N.E.

1982-01-01

The reference waste form for immobilization of Savannah River Plant (SRP) waste is borosilicate glass. In the reference process, waste is mixed with glass-forming chemicals and melted in a Joule-heated ceramic melter at 1150 0 C. Waste glass made with actual or simulated waste on a small scale and glass made with simulated waste on a large scale confirm that the current reference process and glass-former composition are able to accommodate all SRP waste compositions and can produce a glass with: high waste loading; low leach rates; good thermal stability; high resistance to radiation effects; and good impact resistance. Borosilicate glass has been studied as a matrix for the immobilization of SRP waste since 1974. This paper reviews the results of extensive characterization and performance testing of the glass product. These results show that borosilicate glass is a very suitable matrix for the immobilization of SRP waste. 18 references, 3 figures, 10 tables

Effect of sintering on crystallization and structural properties of soda lime silica glass

Directory of Open Access Journals (Sweden)

Zaid Mohd Hafiz Mohd

2017-01-01

Full Text Available The effect of sintering temperatures on crystallization and structural of the soda lime silica (SLS glass was reported. Elemental weight composition of the SLS glass powder was identified through Energy dispersive X-ray fluorescence (EDXRF analysis while the thermal behavior of the glass was determined using Differential thermal analysis (DTA technique. Archimedes’ method and direct geometric measurement were respectively used to determine bulk density and linear shrinkage of the glass samples. Crystallisation behavior of the samples was investigated by X-ray diffraction (XRD analysis and chemical bonds present in the samples were measured using Fourier Transform Infrared (FTIR spectroscopy. Results showed an increase in the density and linear shrinkage of the samples as a function of the sintering temperature. The XRD analysis revealed the formation of α-quartz (SiO2 and a minor amount of devitrite phases in the samples and these were further verified through the detection of chemical bonds by FTIR after sintering at 800ºC. The properties of the glass-ceramics can be explained on the basis of crystal chemistry which indicated that the alkali ions formed as carriers in the random network structure and can be recommended for the manufacture of glass fiber or toughened glass-ceramic insulators.

Preparation and characterization of aluminium-silica metal matrix composite

Science.gov (United States)

Mallikarjuna, G. B.; Basavaraj, E.

2018-04-01

Aluminum alloys are widely used in aerospace and automobile industries due to their low density and good mechanical properties, better corrosion resistance and wear, low thermal coefficient of expansion as compared to conventional metals and alloys. The excellent properties of these materials and relatively low production cost make them a very attractive for a variety of applications. In this present work, Al alloy LM13-SiO2 composites were produced by stir casting method. The reinforcement SiO2 particle size used for preparation of composites are 106 µm, 150 µm, 250 µm and 355 µm with varying amount of 3 to 12 wt% in steps of 3. The prepared composite specimens were machined as per test standards. Effects of weight percentage of SiO2 particles on wear, tensile strength of Al alloy LM13-SiO2 composites have been investigated. The microstructures of the composites were studied to know the dispersion of the SiO2 particles in matrix. Experimental results shows that there is enhanced mechanical properties, when silica weighing 9% was added to the base aluminium alloy and also similar trend exists in all four different micron size of silica and also it has been observed that addition of SiO2 particles significantly improves wear resistance properties as compared with that of unreinforced matrix.

Sol-Gel Glasses

Science.gov (United States)

Mukherjee, S. P.

1985-01-01

Multicomponent homogeneous, ultrapure noncrystalline gels/gel derived glasses are promising batch materials for the containerless glass melting experiments in microgravity. Hence, ultrapure, homogeneous gel precursors could be used to: (1) investigate the effect of the container induced nucleation on the glass forming ability of marginally glass forming compositions; and (2) investigate the influence of gravity on the phase separation and coarsening behavior of gel derived glasses in the liquid-liquid immiscibility zone of the nonsilicate systems having a high density phase. The structure and crystallization behavior of gels in the SiO2-GeO2 as a function of gel chemistry and thermal treatment were investigated. As are the chemical principles involved in the distribution of a second network former in silica gel matrix being investigated. The procedures for synthesizing noncrystalline gels/gel-monoliths in the SiO2-GeO2, GeO2-PbO systems were developed. Preliminary investigations on the levitation and thermal treatment of germania silicate gel-monoliths in the Pressure Facility Acoustic Levitator were done.

Towards Luminescence Dating Of Mosaic Glass

Science.gov (United States)

Galli, A.; Martini, M.; Sibila, E.; Villa, I.

The possibility of dating archaeological glass by means of luminescent techniques has been investigated in recent years, despite the difficulties of this application, mainly linked to the amorphous structure of the material. We focused in particular on mosaic glass, after the encouraging results obtained on byzantine and medieval samples. Further studies were devoted to the comprehension of the luminescent mechanisms in silica glasses, and to the investigation of the relationships between luminescence, colouring or opacifier ions and crystalline phase of the vitreous matrix. The results of a study on the dosimetric characteristics of thermoluminescence (TL) and Optically Stimulated Luminescence (OSL) of a few medieval blue-green mosaic glasses from the San Lorenzo church (Milan) are presented, and the experimental protocols established to identify their suitability for dating are discussed.

Experimental Investigation on Cutting Characteristics in Nanometric Plunge-Cutting of BK7 and Fused Silica Glasses.

Science.gov (United States)

An, Qinglong; Ming, Weiwei; Chen, Ming

2015-03-27

Ductile cutting are most widely used in fabricating high-quality optical glass components to achieve crack-free surfaces. For ultra-precision machining of brittle glass materials, critical undeformed chip thickness (CUCT) commonly plays a pivotal role in determining the transition point from ductile cutting to brittle cutting. In this research, cutting characteristics in nanometric cutting of BK7 and fused silica glasses, including machined surface morphology, surface roughness, cutting force and specific cutting energy, were investigated with nanometric plunge-cutting experiments. The same cutting speed of 300 mm/min was used in the experiments with single-crystal diamond tool. CUCT was determined according to the mentioned cutting characteristics. The results revealed that 320 nm was found as the CUCT in BK7 cutting and 50 nm was determined as the size effect of undeformed chip thickness. A high-quality machined surface could be obtained with the undeformed chip thickness between 50 and 320 nm at ductile cutting stage. Moreover, no CUCT was identified in fused silica cutting with the current cutting conditions, and brittle-fracture mechanism was confirmed as the predominant chip-separation mode throughout the nanometric cutting operation.

Spectral dependence of nonlinear optical absorption of silica glass with copper nanoparticles

International Nuclear Information System (INIS)

Golubev, A N; Nikitin, S I; Smirnov, M A; Stepanov, A L

2011-01-01

The nonlinear optical properties of silica glass with copper nanoparticles synthesized by ion implantation were investigated by z-scan method in nanosecond time scale. The reverse saturation absorption (RSA) at the wavelength range of 450–540 nm and saturation absorption (SA) at 550–585 nm were observed. It was supposed that the two-photon electron absorption from bound of d-states determined the RSA effect and the SA is due to saturation of plasmon excitation.

Long-term modeling of glass waste in portland cement- and clay-based matrices

International Nuclear Information System (INIS)

Stockman, H.W.; Nagy, K.L.; Morris, C.E.

1995-12-01

A set of ''templates'' was developed for modeling waste glass interactions with cement-based and clay-based matrices. The templates consist of a modified thermodynamic database, and input files for the EQ3/6 reaction path code, containing embedded rate models and compositions for waste glass, cement, and several pozzolanic materials. Significant modifications were made in the thermodynamic data for Th, Pb, Ra, Ba, cement phases, and aqueous silica species. It was found that the cement-containing matrices could increase glass corrosion rates by several orders of magnitude (over matrixless or clay matrix systems), but they also offered the lowest overall solubility for Pb, Ra, Th and U. Addition of pozzolans to cement decreased calculated glass corrosion rates by up to a factor of 30. It is shown that with current modeling capabilities, the ''affinity effect'' cannot be trusted to passivate glass if nuclei are available for precipitation of secondary phases that reduce silica activity

Heat accumulation regime of femtosecond laser writing in fused silica and Nd:phosphate glass

Energy Technology Data Exchange (ETDEWEB)

Bukharin, M.A. [Moscow Institute of Physics and Technology, Moscow Region (Russian Federation); Optosystems Ltd., Troitsk, Moscow (Russian Federation); Khudyakov, D.V. [Optosystems Ltd., Troitsk, Moscow (Russian Federation); Physics Instrumentation Center of the General Physics Institute, Troitsk, Moscow (Russian Federation); Vartapetov, S.K. [Physics Instrumentation Center of the General Physics Institute, Troitsk, Moscow (Russian Federation)

2015-04-01

We investigated refractive index induced by direct femtosecond laser writing inside fused silica and Nd:phosphate glass in heat accumulation regime. Spatial profile and magnitude of induced refractive index were investigated at various pulse repetition rates and translation velocities. It was shown that the magnitude of induced refractive index significantly rises with decreasing in time interval between successive laser pulses below the time for thermal diffusion. Going from nonthermal regime to heat accumulation regime, we achieved induced refractive index growth from 4 x 10{sup -3} up to 6.5 x 10{sup -3} in fused silica and from -6 x 10{sup -3} to -9 x 10{sup -3} in Nd:phosphate glass. Aspect ratio of treated area decreased from 2.1 down to less than 1.5 without correcting optical elements. It was shown that in heat accumulation regime, the treated area was surrounded by region of alternatively changed refractive index with significant magnitude up to -2 x 10{sup -3}. Wide regions of decreased refractive index enable fabrication of depressed cladding waveguides. We demonstrated low-loss (0.3 dB/cm) tubular waveguide inside fused silica. For orthogonal polarizations of guiding light, we achieved a small difference between losses as 0.1 dB/cm using highly symmetric written tracks forming the cladding. The desired structure was simulated with the beam propagation method, and the results were in good agreement with experiment data. (orig.)

Monte Carlo simulations of homogeneous upconversion in erbium-doped silica glasses

DEFF Research Database (Denmark)

Philipsen, Jacob Lundgreen; Bjarklev, Anders Overgaard

1997-01-01

Quenching of Er3+ ions by homogeneous energy-transfer upconversion in high-concentration erbium-doped silica glasses has been theoretically investigated, The results indicate that at Er3+ concentrations of 1.0-2.0·1026 m-3 or below, the kinetic limit of strong migration is not reached, and hence...... the widely accepted quadratic upconversion model is not generally valid. Nevertheless, the results offer an explanation of the experimental observations of quadratic upconversion. Furthermore, it has been shown that at a given population inversion, the quenching rate depends on the rate of exchange...

Fiber fuse light-induced continuous breakdown of silica glass optical fiber

CERN Document Server

Todoroki, Shin-ichi

2014-01-01

This book describes the fiber fuse phenomenon that causes a serious problem for the present optical communication systems. High-power light often brings about catastrophic damage to optical devices. Silica glass optical fibers with ultralow transmission loss are not the exception. A fiber fuse appears in a heated region of the fiber cable delivering a few watts of light and runs toward the light source destroying its core region. Understanding this phenomenon is a necessary first step in the development of future optical communication systems. This book provides supplementary videos and photog

Electron, hole and exciton self-trapping in germanium doped silica glass from DFT calculations with self-interaction correction

International Nuclear Information System (INIS)

Du Jincheng; Rene Corrales, L.; Tsemekhman, Kiril; Bylaska, Eric J.

2007-01-01

Density functional theory (DFT) calculations were employed to understand the refractive index change in germanium doped silica glasses for the trapped states of electronic excitations induced by UV irradiation. Local structure relaxation and excess electron density distribution were calculated upon self-trapping of an excess electron, hole, and exciton in germanium doped silica glass. The results show that both the trapped exciton and excess electron are highly localized on germanium ion and, to some extent, on its oxygen neighbors. Exciton self-trapping is found to lead to the formation of a Ge E' center and a non-bridging hole center. Electron trapping changes the GeO 4 tetrahedron structure into trigonal bi-pyramid with the majority of the excess electron density located along the equatorial line. The self-trapped hole is localized on bridging oxygen ions that are not coordinated to germanium atoms that lead to elongation of the Si-O bonds and change of the Si-O-Si bond angles. We carried out a comparative study of standard DFT versus DFT with a hybrid PBE0 exchange and correlation functional. The results show that the two methods give qualitatively similar relaxed structure and charge distribution for electron and exciton trapping in germanium doped silica glass; however, only the PBE0 functional produces the self-trapped hole

Development of an eco-friendly material recycling process for spent lead glass using a mechanochemical process and Na2EDTA reagent.

Science.gov (United States)

Sasai, Ryo; Kubo, Hisashi; Kamiya, Masahiro; Itoh, Hideaki

2008-06-01

To develop a novel nonheating method with lower energy consumption and higher efficiency for recovering both lead and SiO2 glass matrix from spent lead-glass powder, we attempted to treat the spent lead glass by the mechanochemical method using the metal chelate reagent, sodium ethylenediaminetetraacetate (Na2EDTA). As a result of the wet ball-milling treatment of spent lead-glass powder sealed in a polypropylene bottle with zirconia balls, Na2EDTA, and water at room temperature, we found that more than 99 mass % of lead contained in the spentlead-glass powder was extracted as a lead-EDTA species from the solid silica glass network matrix. This separation phenomenon was accelerated by the enlargement of the solid-liquid interface area due to ball-milling atomization and by the high stability constant of lead-EDTA. High extraction yield suggests that Pb-O-Pb bonds in lead glass are weakened or are broken down by the wet ball-milling treatment, i.e., the strong mechanical energy such as the potential and/ or friction energy provided by ball-milling may be high enough to elute lead ions from silica matrix. Moreover, we succeeded in recovering both lead ions as lead sulfate, which is the main compound of anglesite, and the EDTA as sodium-EDTA, which is reusable as the metal chelate reagent in wet chemical process using the ferric sulfate.

Jordanian silica sand and cement as a reinforcement material for polystyrene matrix composites

International Nuclear Information System (INIS)

Jalham, S. I.

1999-01-01

The behaviour of polystyrene matrix composites with different percentages of Jordaanian Silica Sand as a Reinforcement Materials (0, 5, 25, 50, and 75 wt%) and different mean grain sizes of sand particles (60, 75, 85, and 300μ m) and with cement as a boning materials in the amount fo 1/6 wt% of the wt% of silica sand were manufactured and tested under compression loading in the Industrial Engineering Department as the Uninersity of Jordan as a part of large study on local materials. The main conclusions of this investigation are: a long-term, durable structure of the polystyrene composite reinforced by silica sand and cement was achieved by mixing the constituents with water; the higher the volume fraction of the reinforcement, the higher the volume fraction of reinforcement, the higher the strength while for 75% of reinforcement, the strength dropped to an amount less than that of the matrix; the higher the grain size, the higher the strength; longitudinal brittle fracture was observed for the composites, and a homogeneous distribution of the sand particles helped in increasing the strength of the composite by playing an important role in distributing the applied load. (author). 11 refs., 6 tabs, 2 figs

Use of wasted foundry sand (WFS) as a partial substitute for silica in a soda lime glass; Utilizacao de areia descartada de fundicao (ADF) como substituinte parcial da silica em um vidro soda-cal

Energy Technology Data Exchange (ETDEWEB)

Martin, A.C.; Ueno, O.K.; Folgueras, M.V., E-mail: amandacarolinemartin@gmail.com [Universidade do Estado de Santa Catarina (CCT/UDESC), Joinville, SC (Brazil). Centro de Ciencias Tecnologicas

2016-07-01

The waste foundry sand (WFS) is the main waste generates in foundry industries. Studies in the literature suggest the use of WFS in different materials, such as concrete, brick or asphalt. This work aims to partially replace the silica of a soda-lime glass by the WFS. The waste foundry sand has in its composition elements such as iron and aluminum that can affect the glass quality, which justifies the residue processing to reduce the impurity content. The treatments, that included mechanical agitation and thermal treatment, resulted in a slight decrease in the percent of iron with consequent increase of the silica content. After treatment, some sands were incorporated into the glass, that showed green color but with lower absorption intensity for the sand with less iron content. It was observed that it's possible to obtain glasses using WFS, however, there is difficulty in color controlling. (author.

EFFECTS OF LIGHTWEIGHT MULLITE-SILICA RICH GLASS COMPOSITE AGGREGATES ON PROPERTIES OF CASTABLES

Directory of Open Access Journals (Sweden)

Li Y.

2013-09-01

Full Text Available Mullite-silica rich glass (MSRG composite is a material which is more efficient than chamotte for refractory utilization of clay. The effects of lightweight MSRG composite aggregate on the properties of refractory castables were studied by XRD, SEM and EDS, etc. Comparing with a common lightweight chamotte aggregate, it was found that the hot modulus of rupture, refractoriness under load and thermal shock resistance of the castable with lightweight MSRG aggregate were higher than those of the castable with a common lightweight chamotte aggregate because MSRG did not contain silica crystalline phases and contained a liquid phase with very high viscosity at high temperature. The castables with lightweight chamotte aggregate have higher thermal expansion because of existence of cristobalite and quartz, and have lower thermal conductivity because of higher porosity.

Controlled generation of silver nanocolloid in amorphous silica materials

International Nuclear Information System (INIS)

Gil, C.; Garcia-Heras, M.; Carmona, N.; Villages, M. A.

2004-01-01

Amorphous silica-based materials bulk and superficially doped with silver nano colloids were prepared. Bulk doped glasses were obtained by conventional melting and doped monolithic slabs by sol-gel. Superficially doped glasses were obtained by ion-exchange and doped coatings by sol-gel. The samples were characterised by TEM and UV-VIS spectrometry. Depending on the composition, the silver incorporation process, and the thermal treatments, several colourings were obtained. By controlling these parameters, metallic silver nano colloids can be generated in the matrices studied. Colloids aggregation and growing up depends on the matrix nature and on the experimental process carried out. (Author) 10 refs

Preparation and characterization of monodisperse large-porous silica microspheres as the matrix for protein separation.

Science.gov (United States)

Xia, Hongjun; Wan, Guangping; Zhao, Junlong; Liu, Jiawei; Bai, Quan

2016-11-04

High performance liquid chromatography (HPLC) is a kind of efficient separation technology and has been used widely in many fields. Micro-sized porous silica microspheres as the most popular matrix have been used for fast separation and analysis in HPLC. In this paper, the monodisperse large-porous silica microspheres with controllable size and structure were successfully synthesized with polymer microspheres as the templates and characterized. First, the poly(glycidyl methacrylate-co-ethyleneglycol dimethacrylate) microspheres (P GMA-EDMA ) were functionalized with tetraethylenepentamine (TEPA) to generate amino groups which act as a catalyst in hydrolysis of tetraethyl orthosilicate (TEOS) to form Si-containing low molecular weight species. Then the low molecular weight species diffused into the functionalized P GMA-EDMA microspheres by induction force of the amino groups to form polymer/silica hybrid microspheres. Finally, the organic polymer templates were removed by calcination, and the large-porous silica microspheres were obtained. The compositions, morphology, size distribution, specific surface area and pore size distribution of the porous silica microspheres were characterized by infrared analyzer, scanning-electron microscopy, dynamic laser scattering, the mercury intrusion method and thermal gravimetric analysis, respectively. The results show that the agglomeration of the hybrid microspheres can be overcome when the templates were functionalized with TEPA as amination reagent, and the yield of 95.7% of the monodisperse large-porous silica microspheres can be achieved with high concentration of polymer templates. The resulting large-porous silica microspheres were modified with octadecyltrichlorosilane (ODS) and the chromatographic evaluation was performed by separating the proteins and the digest of BSA. The baseline separation of seven kinds of protein standards was achieved, and the column delivered a better performance when separating BSA digests

Superparamagnetism and coercivity in HCP-Co nanoparticles dispersed in silica matrix

Energy Technology Data Exchange (ETDEWEB)

Julian Fernandez, C. de E-mail: dejulian@padova.infm.it; Mattei, G.; Sangregorio, C.; Battaglin, C.; Gatteschi, D.; Mazzoldi, P

2004-05-01

The magnetic properties of Co HCP nanoparticles dispersed in a silica matrix with sizes between 2{+-}0.7 and 5{+-}2.2 nm were investigated. The temperature dependence of zero-field cooled and field cooled magnetizations and of the coercive field were analyzed considering the thermal activated demagnetization process. Enhanced anisotropy was observed for the 2 nm nanoparticles, while the demagnetization process of the larger ones is dominated by interparticle interactions.

Enhancement of the glass corrosion in the presence of clay minerals: testing experimental results with an integrated glass dissolution model

International Nuclear Information System (INIS)

Godon, N.; Vernaz, E.Y.

1992-01-01

Recent glass dissolution experiments, conducted at 90 deg C in the presence of potential backfill materials, indicate remarkably faster glass corrosion in the presence of clay, compared to tests where the glass is leached either alone or with alternative backfill materials. This effect correlates with the clay content in the backfill, and may be attributed to the removal of silica from solution. Scorpion, or dissolution with reprecipitation of a silica-rich clay, have been proposed as possible mechanisms for the silica consumption. The results of some experiments have been tested against a glass dissolution model, in which a widely used kinetic equation for glass corrosion is coupled with diffusive silica transport through a single porosity, linearly sorbing medium, which represents the backfilling. Because the glass corrosion rates imposed by the kinetic equation are inversely proportional to the silicic acid concentration of the leachant contacting the glass, the model predicts enhanced glass dissolution if silica is sorbed by the porous medium. The experimental data proved to be consistent with the predicted enhancement of the glass dissolution. Moreover, the model-estimated distribution coefficients for silica sorption (K d ) fall within the range of values extracted from available literature data, thus supporting the hypothesis that the observed high corrosion rates are due to sorption of silica on the clay mineral surfaces. (author)

Short and medium range order in two-component silica glasses by positron annihilation spectroscopy

International Nuclear Information System (INIS)

Inoue, K.; Kataoka, H.; Nagai, Y.; Hasegawa, M.; Kobayashi, Y.

2014-01-01

The dependence of chemical composition on the average sizes of subnanometer-scale intrinsic structural open spaces surrounded by glass random networks in two-component silica-based glasses was investigated systematically using positronium (Ps) confined in the open spaces. The average sizes of the open spaces for SiO 2 -B 2 O 3 and SiO 2 -GeO 2 glasses are only slightly dependent on the chemical compositions because the B 2 O 3 and GeO 2 are glass network formers that are incorporated into the glass network of the base SiO 2 . However, the open space sizes for all SiO 2 -R 2 O (R = Li, Na, K) glasses, where R 2 O is a glass network modifier that occupies the open spaces, decrease rapidly with an increase in the R 2 O concentration. Despite the large difference in the ionic radii of the alkali metal (R) atoms, the open space sizes decrease similarly for all the alkali metal atoms studied. This dependence of the chemical composition on the open space sizes in SiO 2 -R 2 O observed by Ps shows that the alkali metal atoms do not randomly occupy the structural open spaces, but filling of the open spaces by R 2 O proceeds selectively from the larger to the smaller open spaces as the R 2 O concentrations are increased.

Laser ablation of toluene liquid for surface micro-structuring of silica glass

International Nuclear Information System (INIS)

Niino, H.; Kawaguchi, Y.; Sato, T.; Narazaki, A.; Gumpenberger, T.; Kurosaki, R.

2006-01-01

Microstructures with well-defined micropatterns were fabricated on the surfaces of silica glass using a laser-induced backside wet etching (LIBWE) method by diode-pumped solid state (DPSS) UV laser at the repetition rate of 10 kHz. For a demonstration of flexible rapid prototyping as mask-less exposure system, the focused laser beam was directed to the sample by galvanometer-based point scanning system. Additionally, a diagnostics study of plume propagation in the ablated products of toluene solid film was carried out with an intensified CCD (ICCD) camera

Mechanical performance and thermal stability of glass fiber reinforced silica aerogel composites based on co-precursor method by freeze drying

Science.gov (United States)

Zhou, Ting; Cheng, Xudong; Pan, Yuelei; Li, Congcong; Gong, Lunlun; Zhang, Heping

2018-04-01

In order to maintain the integrity, glass fiber (GF) reinforced silica aerogel composites were synthesized using methltrimethoxysilane (MTMS) and water glass co-precursor by freeze drying method. The composites were characterized by scanning electron microscopy, Brunauer-Emmett-Teller analysis, uniaxial compressive test, three-point bending test, thermal conductivity analysis, contact angle test, TG-DSC analysis. It was found that the molar ratio of MTMS/water glass could significantly affect the properties of composites. The bulk density and thermal conductivity first decreased and then increased with the increasing molar ratio. The composites showed remarkable mechanical strength and flexibility compared with pure silica aerogel. Moreover, when the molar ratio is 1.8, the composites showed high specific surface area (870.9 m2/g), high contact angle (150°), great thermal stability (560 °C) and low thermal conductivity (0.0248 W/m·K). These outstanding properties indicate that GF/aerogels have broad prospects in the field of thermal insulation.

Potentiometric urea biosensor based on multi-walled carbon nanotubes (MWCNTs)/silica composite material

International Nuclear Information System (INIS)

Ahuja, Tarushee; Kumar, D.; Singh, Nahar; Biradar, A.M.; Rajesh

2011-01-01

A novel potentiometric urea biosensor has been fabricated with urease (Urs) immobilized multi-walled carbon nanotubes (MWCNTs) embedded in silica matrix deposited on the surface of indium tin oxide (ITO) coated glass plate. The enzyme Urs was covalently linked with the exposed free -COOH groups of functionalized MWCNTs (F-MWCNTs), which are subsequently incorporated within the silica matrix by sol-gel method. The Urs/MWCNTs/SiO 2 /ITO composite modified electrode was characterized by Fourier transform infrared (FTIR) spectroscopy, thermal gravimetric analysis (TGA) and UV-visible spectroscopy. The morphologies and electrochemical performance of the modified Urs/MWCNTs/SiO 2 /ITO electrode have been investigated by scanning electron microscopy (SEM) and potentiometric method, respectively. The synergistic effect of silica matrix, F-MWCNTs and biocompatibility of Urs/MWCNTs/SiO 2 made the biosensor to have the excellent electro catalytic activity and high stability. The resulting biosensor exhibits a good response performance to urea detection with a wide linear range from 2.18 x 10 -5 to 1.07 x 10 -3 M urea. The biosensor shows a short response time of 10-25 s and a high sensitivity of 23 mV/decade/cm 2 .

Basaltic glasses from Iceland and the deep sea: Natural analogues to borosilicate nuclear waste-form glass

International Nuclear Information System (INIS)

Jercinovic, M.J.; Ewing, R.C.

1987-12-01

The report provides a detailed analysis of the alteration process and products for natural basaltic glasses. Information of specific applicability to the JSS project include: * The identification of typical alteration products which should be expected during the long-term corrosion process of low-silica glasses. The leached layers contain a relatively high proportion of crystalline phases, mostly in the form of smectite-type clays. Channels through the layer provide immediate access of solutions to the fresh glass/alteration layer interface. Thus, glasses are not 'protected' from further corrosion by the surface layer. * Corrosion proceeds with two rates - an initial rate in silica-undersaturated environments and a long-term rate in silica-saturated environments. This demonstrates that there is no unexpected change in corrosion rate over long periods of time. The long-term corrosion rate is consistent with that of borosilicate glasses. * Precipitation of silica-containing phases can result in increased alteration of the glass as manifested by greater alteration layer thicknesses. This emphasizes the importance of being able to predict which phases form during the reaction sequence. * For natural basaltic glasses the flow rate of water and surface area of exposed glass are critical parameters in minimizing glass alteration over long periods of time. The long-term stability of basalt glasses is enhanced when silica concentrations in solution are increased. In summary, there is considerable agreement between corrosion phenomena observed for borosilicate glasses in the laboratory and those observed for natural basalt glasses of great age. (With 121 refs.) (authors)

FY 1999 results of the regional consortium R and D project/the regional consortium energy R and D. 1st year. Development of the energy-saving type production technology of high-purity/transparent silica glass; 1999 nendo kojundo tomei sekiei glass no sho energy gata seizo gijutsu no kaihatsu seika hokokusho. 1

Energy Technology Data Exchange (ETDEWEB)

NONE

2000-03-01

For the purpose of achieving the remarkable energy conservation, high accuracy and low cost in the production of high-purity/transparent silica glass, the developmental research was conducted on slip casting method. In the development of technology to synthesize silica powder by the sol-gel method, monodisperse - polydisperse high-purity colloidal silica was obtained. In the development of technology to make silica power ultra-highly pure, a process was found out in which silica particles can be obtained by applying moderate amounts of ammonium bicarbonate and aqueous ammonia to the solution of silicic acid for heating. In the slip cast forming, a high-density forming body with a mean particle size of 1.5{mu}m was obtained. In the trial manufacture of reflector model, a translucent silica glass sintered body was obtained by transcribing the gypsum type dimensional shape in high purity. Besides, experimental researches were conducted on the examination of gypsum type/resin type and evaluation of physical properties, heat deterioration characteristics of the actual multi-layer film and trial manufacture of the heat resistant film, analysis/evaluation of trace impurities inside silica glass, conditions for the manufacture of dense silica glass sheets, etc. (NEDO)

Effect of sintering temperature variations on fabrication of 45S5 bioactive glass-ceramics using rice husk as a source for silica.

Science.gov (United States)

Leenakul, Wilaiwan; Tunkasiri, Tawee; Tongsiri, Natee; Pengpat, Kamonpan; Ruangsuriya, Jetsada

2016-04-01

45S5 bioactive glass is a highly bioactive substance that has the ability to promote stem cell differentiation into osteoblasts--the cells that create bone matrix. The aim of this work is to analyze physical and mechanical properties of 45S5 bioactive glass fabricated by using rice husk ash as its silica source. The 45S5 bioactive glass was prepared by melting the batch at 1300 °C for 3h. The samples were sintered at different temperatures ranging from 900 to 1050 °C with a fixed dwell-time of 2h. The phase transitions, density, porosity and microhardness values were investigated and reported. DTA analysis was used to examine the crystallization temperatures of the glasses prepared. We found that the sintering temperature had a significant effect on the mechanical and physical properties of the bioactive glass. The XRD showed that when the sintering temperature was above 650 °C, crystallization occurred and bioactive glass-ceramics with Na2Ca2Si3O9, Na2Ca4(PO4)2SiO4 and Ca3Si2O7 were formed. The optimum sintering temperature resulting in maximum mechanical values was around 1050 °C, with a high density of 2.27 g/cm(3), 16.96% porosity and the vicker microhardness value of 364HV. Additionally, in vitro assay was used to examine biological activities in stimulated body fluid (SBF). After incubation in SBF for 7 days, all of the samples showed formations of apatite layers indicating that the 45S5 bioactive glasses using rice husk as a raw material were also bioactive. Copyright © 2015 Elsevier B.V. All rights reserved.

Remaining uncertainties in predicting long-term performance of nuclear waste glass from experiments

International Nuclear Information System (INIS)

Grambow, B.

1994-01-01

The current knowledge on the glass dissolution mechanism and the representation of glass dissolution concepts within overall repository performance assessment models are briefly summarized and uncertainties related to mechanism, radionuclide chemistry and parameters are discussed. Understanding of the major glass dissolution processes has been significantly increased in recent years. Long-term glass stability is related to the long-term maintenance of silica saturated conditions. The behavior of individual radionuclides in the presence of a dissolving glass has not been sufficiently and results do no yet allow meaningful predictions. Conserving long-term predictions of glass matrix dissolution as upper limit for radionuclide release can be made with sufficient confidence, however these estimations generally result in a situation where the barrier function of the glass is masked by the efficiency of the geologic barrier. Realistic long-term predictions may show that the borosilicate waste glass contributes to overall repository safety to a much larger extent than indicated by overconservatism. Today realistic predictions remain highly uncertain and much more research work is necessary. In particular, the long-term rate under silica saturated conditions needs to be understood and the behavior of individual radionuclides in the presence of a dissolving glass deserves more systematic investigations

Superparamagnetism and coercivity in HCP-Co nanoparticles dispersed in silica matrix

International Nuclear Information System (INIS)

Julian Fernandez, C. de; Mattei, G.; Sangregorio, C.; Battaglin, C.; Gatteschi, D.; Mazzoldi, P.

2004-01-01

The magnetic properties of Co HCP nanoparticles dispersed in a silica matrix with sizes between 2±0.7 and 5±2.2 nm were investigated. The temperature dependence of zero-field cooled and field cooled magnetizations and of the coercive field were analyzed considering the thermal activated demagnetization process. Enhanced anisotropy was observed for the 2 nm nanoparticles, while the demagnetization process of the larger ones is dominated by interparticle interactions

Thermal expansion at low temperatures of glass-ceramics and glasses

Energy Technology Data Exchange (ETDEWEB)

White, G K [National Measurement Lab., Sydney (Australia)

1976-08-01

The linear thermal expansion coefficient, ..cap alpha.., has been measured from 2 to 32 K and from 55 to 90 K for a machineable glass-ceramic, an 'ultra-low expansion' titanium silicate glass (Corning ULE), and ceramic glasses (Cer-Vit and Zerodur), and for glassy carbon. ..cap alpha.. is negative for the ultra-low expansion materials below 100 K, as for pure vitreous silica. Comparative data are reported for ..cap alpha..-quartz , ..cap alpha..-cristobalite, common opal, and vitreous silica.

Analysis of polycyclic aromatic hydrocarbons I. Determination by gas chromatography with glass and fused silica capillary columns

International Nuclear Information System (INIS)

Perez, M. M.; Gonzalez, D.

1987-01-01

A study of the analysis by gas chromatography of aromatic polycyclic hydrocarbons is presented. The separation has been carried out by glass and fused silica capillary column. The limitations and the advantages of the procedure are discussed in terms of separation efficiency, sensitivity and precision. (Author) 17 refs

Ionic conductivity of sodium silicate glasses grown within confined volume of mesoporous silica template

Science.gov (United States)

Chatterjee, Soumi; Saha, Shyamal Kumar; Chakravorty, Dipankar

2018-04-01

Nanodimensional sodium silicate glasses of composition 30Na2O.70SiO2 has been prepared within the pores of 5.5 nm of mesoporous silica as a template using the surfactant P123. The nanocomposite was characterized by X-ray diffraction, transmission electron microscope, and X-ray photoelectron spectroscopy. Electrical conductivity of the sample was studied by ac impedance spectroscopy. The activation energy for ionic conduction was found to be 0.13 eV with dc conductivity at room temperature of 10-6 S-cm-1. This is attributed to the creation of oxygen ion vacancies at the interface of mesoporous silica and nanoglass arising out of the presence of Si2+ species in the system. These nanocomposites are expected to be useful for applications in sodiumion battery for storage of renewable energy.

Glass Dissolution Parameters: Update for Entsorgungsnachweis

International Nuclear Information System (INIS)

Curti, E.

2003-11-01

This document provides updated long-term corrosion rates for borosilicate glasses used in Switzerland as a matrix for high-level radioactive waste. The new rates are based on long-term leaching experiments conducted at PSI and are corroborated by recent investigations. The asymptotic rates have been determined through weighted linear regressions of the normalised mass losses, directly calculated from B and Li concentrations in the leaching solutions. Special attention was given to the determination of the analytical uncertainty of the mass losses. The sensitivity of the corrosion rates to analytical uncertainties and to other criteria (e.g. the choice of data points for the regressions) was also studied. A major finding was that the uncertainty of the corrosion rate mainly depends on the uncertainty of the specific glass surface area. The reference rates proposed for safety assessment calculations are 1.5 mg m -2 d -1 for BNFL glasses and 0.2 mg m -2 d -1 for Cogema glasses. The relevance of the proposed corrosion rates for repository conditions is shown based on the analysis of processes and parameters currently known to affect the long-term kinetics of silicate glasses. Specifically, recent studies indicate that potentially detrimental effects, notably the removal of silica from solution through adsorption on clay minerals, are transitory and will not affect the long-term corrosion rate of the Swiss reference glasses. Iron corrosion products are also known to bind silica, but present data are not sufficient to quantify their influence on the long-term rate. (author)

Three dimensional multilayer solenoid microcoils inside silica glass

Science.gov (United States)

Meng, Xiangwei; Yang, Qing; Chen, Feng; Shan, Chao; Liu, Keyin; Li, Yanyang; Bian, Hao; Si, Jinhai; Hou, Xun

2016-01-01

Three dimensional (3D) solenoid microcoils could generate uniform magnetic field. Multilayer solenoid microcoils are highly pursued for strong magnetic field and high inductance in advanced magnetic microsystems. However, the fabrication of the 3D multilayer solenoid microcoils is still a challenging task. In this paper, 3D multilayer solenoid microcoils with uniform diameters and high aspect ratio were fabricated in silica glass. An alloy (Bi/In/Sn/Pb) with high melting point was chosen as the conductive metal to overcome the limitation of working temperature and improve the electrical property. The inductance of the three layers microcoils was measured, and the value is 77.71 nH at 100 kHz and 17.39 nH at 120 MHz. The quality factor was calculated, and it has a value of 5.02 at 120 MHz. This approach shows an improvement method to achieve complex 3D metal microstructures and electronic components, which could be widely integrated in advanced magnetic microsystems.

Modification of medium-range order in silica glass by ball-milling: real- and reciprocal-space structural correlations for the first sharp diffraction peak

International Nuclear Information System (INIS)

Mukai, Akira; Kohara, Shinji; Uchino, Takashi

2007-01-01

We have carried out high-energy x-ray diffraction measurements on mechanically milled silica glass. It has been found that the first sharp diffraction peak (FSDP) in the structure factor S(Q) of silica glass appreciably decreases in intensity as a result of mechanical milling, whereas the observed features of the other peaks in S(Q) almost remain unchanged. The corresponding real-space correlation function of the milled samples shows a marked decrease in intensity at r∼5 A. This gives an experimental manifestation that the dominant real-space structural correlation pertaining to the FSDP occurs at r∼5 A

Modification of medium-range order in silica glass by ball-milling: real- and reciprocal-space structural correlations for the first sharp diffraction peak

Energy Technology Data Exchange (ETDEWEB)

Mukai, Akira [Department of Chemistry, Kobe University, Kobe 657-8501 (Japan); Kohara, Shinji [SPring-8, Japan Synchrotron Radiation Research Institute, Sayo, Hyogo 679-5198 (Japan); Uchino, Takashi [Department of Chemistry, Kobe University, Kobe 657-8501 (Japan)

2007-11-14

We have carried out high-energy x-ray diffraction measurements on mechanically milled silica glass. It has been found that the first sharp diffraction peak (FSDP) in the structure factor S(Q) of silica glass appreciably decreases in intensity as a result of mechanical milling, whereas the observed features of the other peaks in S(Q) almost remain unchanged. The corresponding real-space correlation function of the milled samples shows a marked decrease in intensity at r{approx}5 A. This gives an experimental manifestation that the dominant real-space structural correlation pertaining to the FSDP occurs at r{approx}5 A.

A-thermal elastic behavior of silicate glasses.

Science.gov (United States)

Rabia, Mohammed Kamel; Degioanni, Simon; Martinet, Christine; Le Brusq, Jacques; Champagnon, Bernard; Vouagner, Dominique

2016-02-24

Depending on the composition of silicate glasses, their elastic moduli can increase or decrease as function of the temperature. Studying the Brillouin frequency shift of these glasses versus temperature allows the a-thermal composition corresponding to an intermediate glass to be determined. In an intermediate glass, the elastic moduli are independent of the temperature over a large temperature range. For sodium alumino-silicate glasses, the a-thermal composition is close to the albite glass (NaAlSi3O8). The structural origin of this property is studied by in situ high temperature Raman scattering. The structure of the intermediate albite glass and of silica are compared at different temperatures between room temperature and 600 °C. When the temperature increases, it is shown that the high frequency shift of the main band at 440 cm(-1) in silica is a consequence of the cristobalite-like alpha-beta transformation of 6-membered rings. This effect is stronger in silica than bond elongation (anharmonic effects). As a consequence, the elastic moduli of silica increase as the temperature increases. In the albite glass, the substitution of 25% of Si(4+) ions by Al(3+) and Na(+) ions decreases the proportion of SiO2 6-membered rings responsible for the silica anomaly. The effects of the silica anomaly balance the anharmonicity in albite glass and give rise to an intermediate a-thermal glass. Different networks, formers or modifiers, can be added to produce different a-thermal glasses with useful mechanical or chemical properties.

Luminescence of Tb.sup.3+./sup.-doped high silica glass under UV and X-ray excitation

Czech Academy of Sciences Publication Activity Database

Chewpraditkul, W.; Shen, Y.; Chen, D.; Beitlerová, Alena; Nikl, Martin

2013-01-01

Roč. 35, č. 3 (2013), s. 426-430 ISSN 0925-3467 R&D Projects: GA MŠk LH12185 Institutional support: RVO:68378271 Keywords : Tb 3+ * luminescence * luminescence decays * porous silica glass * scintillation Subject RIV: BM - Solid Matter Physics ; Magnetism Impact factor: 2.075, year: 2013 http://dx.doi.org/10.1016/j.optmat.2012.09.012

Diffusion and aggregation of implanted Ag and Au in a lithia--alumina--silica glass

International Nuclear Information System (INIS)

Arnold, G.W.; Borders, J.A.

1975-01-01

Optical extinction and Rutherford backscattering (RBS) techniques were employed to obtain information on the size and spatial distribution of Au- and Ag-colloids in implanted (Au + , Ag + ) lithia-alumina-silica glass. The formation of metallic aggregates (colloids), necessary for preparation of a glass-ceramic surface layer, proceeds readily with annealing temperature for Au-implanted samples but not for Ag-implanted material. The optical and RBS spectra show that the particle size and spatial distribution in as-implanted samples are sensitive to sample temperature and ion-beam heating effects, while these parameters for Au-implanted samples are relatively insensitive to temperature and beam current. It is suggested that this behavior is related to differences in the dissolution energies of Ag and Au aggregates. A two-peaked spatial distribution for Ag implanted at room temperature at a dose rate of approximately 1 μA/cm 2 is observed which may result from the trapping of Ag in the compacted damage region of the glass during implantation. (auth)

Diffusion and aggrigation of implanted Ag and Au in a lithia-alumina-silica glass

International Nuclear Information System (INIS)

Arnold, G.W.; Borders, J.A.

1976-01-01

Optical extinction and Rutherford backscattering (RBS) techniques have been employed to obtain information on the size and spatial distribution of Au and Ag colloids in implanted (Au + ,Ag + )lithia-alumina-silica glass. The formation of metallic aggregates (colloids), necessary for preparation of a glass-ceramic surface layer, proceeds readily with annealing temperature for Au-implanted samples but not for Ag-implanted material. The optical and RBS spectra show that the particle size and spatial distribution in Ag-implanted samples are sensitive to sample temperature and ion-beam heating effects, while these parameters for Au-implanted samples are relatively insensitive to temperature and beam current. It is suggested that this behaviour is related to differences in the dissolution energies of Ag and Au aggregates. A two-peaked spatial distribution for Ag implanted at room temperature at a dose rate of approximately 1 μA cm -2 is observed which may result from the trappings of Ag in the ion displacement damage region of the glass during implantation. (author)

Quantitative micro-Raman analysis of volcanic glasses: influence and correction of matrix effects

Science.gov (United States)

Di Muro, Andrea

2014-05-01

Micro-Raman spectroscopy, even though a very promising micro-analytical technique, is still not used to routinely quantify volatile elements dissolved in glasses. Following an original idea of Galeener and Mikkelsen (1981) for the quantification of hydroxyl (OH) in silica glass, several quantitative procedures have been recently proposed for the analysis of water, sulphur and carbon in natural glasses (obsidians, pumices, melt inclusions). The quantification of a single analyte requires the calibration of the correlation between the intensity I (height or area) of the related Raman band, normalized or not to a reference band RB, and the analyte concentration. For the analysis of alumino-silicate glasses, RB corresponds to one of the two main envelopes (LF and HF) related to the vibration of the glass network. Calibrations are linear, provided the increase in the analyte concentration does not dramatically affect RB intensity. Much attention has been paid to identify the most appropriate spectral treatment (spectra reduction; baseline subtraction; etc) to achieve accurate measurement of band intensities. I here show that the accuracy of Raman procedures for volatile quantification critically depends on the capability in predicting and in taking into account the influence of multiple matrix effects, which are often correlated with the average polymerization degree of the glass network. A general model has been developed to predict matrix effects affecting micro-Raman analysis of natural glasses. The specific and critical influence of iron redox state and pressure are discussed. The approach has been extensively validated for the study of melt inclusions and matrices spanning a broad range of compositions and dissolved volatile contents. References Analytical procedures Mercier, M, Di Muro, A., Métrich, N., Giordano, D., Belhadj, O., Mandeville, C.W. (2010) Spectroscopic analysis (FTIR, Raman) of water in mafic and intermediate glasses and glass inclusions

Fracture behaviour of brittle (glass) matrix composites

Czech Academy of Sciences Publication Activity Database

Dlouhý, Ivo; Chlup, Zdeněk; Boccaccini, A. R.

2005-01-01

Roč. 482, - (2005), s. 115-122 ISSN 0255-5476. [International Conference on Materials Structure and Micromechanics of Fracture /4./. Brno, 23.06.2004-25.06.2004] R&D Projects: GA AV ČR(CZ) IAA2041003; GA ČR(CZ) GA101/02/0683 Institutional research plan: CEZ:AV0Z2041904 Keywords : Ceramic matrix composites * fracture toughness * toughening effects Subject RIV: JH - Ceramic s, Fire-Resistant Materials and Glass Impact factor: 0.399, year: 2005

Transverse Writing of Multimode Interference Waveguides inside Silica Glass by Femtosecond Laser Pulses

International Nuclear Information System (INIS)

Da-Yong, Liu; Yan, Li; Yan-Ping, Dou; Heng-Chang, Guo; Hong, Yang; Qi-Huang, Gong

2008-01-01

Multi-mode interference waveguides are fabricated inside silica glass by transverse writing geometry with femtosecond laser pulses. The influences of several writing and reading factors on the output mode are systematically studied. The experimental results of straight waveguides are in good agreement with the simulations by the beam propagation method. By integrating a straight waveguide with a bent waveguide, a 1 × 2 multi-mode splitter is formed and 2 × 3 lobes are observed in the output mode. (fundamental areas of phenomenology (including applications))

Alkali passivation mechanism of sol-gel derived TiO2-SiO2 films coated on soda-lime-silica glass substrates

Energy Technology Data Exchange (ETDEWEB)

Matsuda, A; Matsuno, Y; Katayama, S; Tsuno, T [Nippon Steel Glass Co. Ltd., Tokyo (Japan); Toge, N; Minami, T [University of Osaka Prefecture, Osaka (Japan). College of Engineering

1992-09-01

TiO2-SiO2 films prepared by the sol-gel method serves as an effective alkali passivation layer on a soda-lime-silica glass substrate and the film is superior to a sol-gel derived pure SiO2 film from the view point of weathering resistance improvement. To clarify the reason, alkali passivation mechanism of sol-gel derived TiO2-SiO2 glass films with different TiO2 contents coated on a soda-lime-silica glass substrate was studied by SIMS (secondary ion mass spectroscopy) and XPS (X-ray photoelectron spectroscopy) analyses, and compared with the results of a sol-gel derived pure SiO2 film. As a result, the following conclusions were obtained: An increase in TiO2 content in the TiO2 SiO2 film increases the sodium concentration in the film, which was induced by sodium migration from the glass substrate during the heat-treatment. Because of the presence of sodium the TiO2 -SiO2 films serve not as a barrier but as an effective getter of alkali ions and thereby effectively improve the weathering resistance Of the glass substrate. 10 refs., 6 figs.

Large third-order optical nonlinearity of silver colloids in silica glasses synthesized by ion implantation

International Nuclear Information System (INIS)

Ghosh, Binita; Chakraborty, Purushottam

2011-01-01

Silver ion implantations in fused silica glasses have been made to synthesize silver nanocluster-glass composites and a combination of 'Anti-Resonant Interferometric Nonlinear Spectroscopy (ARINS)' and 'Z-scan' techniques has been employed for the measurement of the third-order optical susceptibility of these nanocomposites. The ARINS technique utilizes the dressing of two unequal-intensity counter-propagating pulsed optical beams with differential nonlinear phases, which occurs upon traversing the sample. This difference in phase manifests itself in the intensity-dependent transmission, measurement of which enables us to extract the values of nonlinear refractive index (η 2 ) and nonlinear absorption coefficient (β), finally yielding the real and imaginary parts of the third-order dielectric susceptibility (χ (3) ). The real and imaginary parts of χ (3) are obtained in the orders of 10 -10 e.s.u for silver nanocluster-glass composites. The present value of χ (3) , to our knowledge, is extremely accurate and much more reliable compared to the values previously obtained by other workers for similar silver-glass nanocomposites using only Z-scan technique. Optical nonlinearity has been explained to be due to two-photon absorption in the present nanocomposite glasses and is essentially of electronic origin.

Structural and optical properties of Eu3+ activated low cost zinc soda lime silica glasses

Directory of Open Access Journals (Sweden)

Nur Alia Sheh Omar

Full Text Available A low cost method was employed to synthesize ZnO-SLS:xEu3+ phosphors using recyclable bottle glass as silica source. The structural and optical properties of ZnO-SLS:xEu3+ (x = 0, 1, 2, 3, 4 and 5 wt.% glasses were determined using X-ray diffraction (XRD, Fourier transform infrared reflectance (FTIR, UV-visible (Uv-Vis and photoluminescence (PL spectroscopy. Structural investigation using XRD measurement had broadened the halo peak with the doping of dopants. FTIR spectra showed the glass system consists of –OH and SiO4 bands. Meanwhile, the optical measurement using UV-Vis absorption has been induced a blue shift of the electronic absorption edge. The emission peak intensity of ZnO-SLS:xEu3+ phosphors was enhanced with the progression of doping concentration and thus, revealed their potential as red emitting phosphors under 400 nm excitation. Keywords: Eu3+ doped ZnO-SLS glasses, Solid state method, Optical band gap, Photoluminescence

Excellent plasticity of a new Ti-based metallic glass matrix composite upon dynamic loading

Energy Technology Data Exchange (ETDEWEB)

Wu, R.F. [Laboratory of Applied Physics and Mechanics of Advanced Materials, College of Materials Science and Engineering, Taiyuan University of Technology, Taiyuan 030024 (China); State Key Laboratory of Explosion Science and Technology, Beijing Institute of Technology, Beijing 100081 (China); Jiao, Z.M. [Institute of Applied Mechanics and Biomedical Engineering, Taiyuan University of Technology, Taiyuan 030024 (China); Wang, Y.S.; Wang, Z. [Laboratory of Applied Physics and Mechanics of Advanced Materials, College of Materials Science and Engineering, Taiyuan University of Technology, Taiyuan 030024 (China); Wang, Z.H.; Ma, S.G. [Institute of Applied Mechanics and Biomedical Engineering, Taiyuan University of Technology, Taiyuan 030024 (China); Qiao, J.W., E-mail: qiaojunwei@gmail.com [Laboratory of Applied Physics and Mechanics of Advanced Materials, College of Materials Science and Engineering, Taiyuan University of Technology, Taiyuan 030024 (China); State Key Laboratory of Explosion Science and Technology, Beijing Institute of Technology, Beijing 100081 (China)

2016-11-20

Quasi-static and dynamic compressive properties of in-situ Ti{sub 60}Zr{sub 14}V{sub 12}Cu{sub 4}Be{sub 10} bulk metallic glass matrix composites containing ductile dendrites were investigated. Upon quasi-static compressive loading, the composite exhibits a high fracture strength of ~2,600 MPa, combined with a considerable plasticity of ~40% at room temperature. However, upon dynamic loading, an excellent plasticity of ~16% can be obtained due to the abundant dislocations and severe lattice distortions within dendrites and multiplication of shear bands within the glass matrix analyzed by transmission-electron microscopy. A constitutive relationship is obtained by Johnson-Cook plasticity model, which is employed to model the dynamic flow stress behavior. In addition, under dynamic compression, the adiabatic temperature rise increases with increasing strain rates, resulting in that the softening effect within the glass matrix is obviously enhanced during deformation.

Synthesis, properties and host effects of rare-earth doped silica nanopowders for photonic applications

Science.gov (United States)

Halpern, Susan B.

In this study, SiO2/Al2O3/Er2O 3 (SAE) nanopowders were fabricated by the CF-CVC technique with average primary particle sizes ranging from 10--30 nm. Fluorescence and lifetime measurements were made both on as-prepared powders, as well as heat treated powders, with the latter exhibiting significantly higher emission intensities. At ˜1000°C, the SAE became partially devitrified with extremely broad (FWHM ≈ 78 nm) and flat emission spectra, which is highly desirable for Wavelength Division Multiplexing (WDM) in optical amplifiers. The unique optical properties of the powders are attributed to the formation of a metastable phase consisting of an uniform nano-scale dispersion of a metastable intermediate SiO2 (Al,Er)2O3 phase in an amorphous SiO 2 matrix. At higher heat treatments (1400°C), a dual-phase equilibrium structure was formed, consisting of a pyrochlore phase in a crystobalite matrix. The SAE nanopowders were incorporated into various optical hybrid glass hosts for active planar waveguide applications. Host selection was dependent on transparency in the wavelength region of interest (900 nm--1600 nm), index matching (n ˜ 1.5), chemical/thermal stability, and ease of processing. Furthermore, the inorganic-organic glasses were hydrophobic, resulting in a minimal level of residual OH- which can quench fluorescence emission. Four separate groups of host materials were studied: Perfluoro-alkyl Hybrid Glass (n ≈ 1.42), Alumina-Silica Hybrid Glass (n ≈ 1.49), Polyurethane-Silica Hybrid Glass (n ≈ 1.44), and Methyl/Epoxy Group Hybrid Glass (n ≈ 1.48). All hosts showed high spectral transparency, uniform dispersion of the nanopowder in the host, and minimal surface quenching of emission, and therefore represent excellent candidates for fabrication of next generation nanophotonic planar devices.

Correlation between acoustical and structural properties of glasses: Extension of Abd El-Moneim model for bioactive silica based glasses

Energy Technology Data Exchange (ETDEWEB)

Abd El-Moneim, Amin, E-mail: aminabdelmoneim@hotmail.com

2016-04-15

Correlation between room temperature ultrasonic attenuation coefficient and the most significant structural parameters has been studied in the bioactive silica based glasses, for the first time. The correlation has been carried out in the quaternary SiO{sub 2}–Na{sub 2}O–CaO–P{sub 2}O{sub 5} glass system using the two semi-empirical formulas, which have been presented recently by the author. Changes in the elastic properties, related to the substitution of SiO{sub 2} by alkali Na{sub 2}O and alkaline earth CaO oxides, have also been deduced by evaluating the mean atomic volume, packing density, fractal bond connectivity and density of the analogous crystalline structure. Furthermore, values of the theoretical elastic moduli have been calculated on the basis of Makishima-Mackenzie theory and compared with the corresponding observed values. Results show that the correlation between ultrasonic attenuation coefficient and the oxygen density, average atomic ring size, first-order stretching force constant and experimental bulk modulus was achieved at 5 MHz frequency. Values of the theoretically calculated shear modulus are in excellent correlation (C. R. ≻95%) with the corresponding experimental ones. The divergence between the theoretical and experimental values of bulk modulus has been discussed. - Highlights: • Abd El-Moneim model was extended for bioactive glasses. • Ultrasonic attenuation was correlated with structural parameters. • Correlation was carried out in Si–Na–Ca–P glasses. • The model is valid for all investigated glass samples. • Agreement between theoretical and experimental elastic moduli was studied.

Anomalous enthalpy relaxation in vitreous silica

DEFF Research Database (Denmark)

Yue, Yuanzheng

2015-01-01

scans. It is known that the liquid fragility (i.e., the speed of the viscous slow-down of a supercooled liquid at its Tg during cooling) has impact on enthalpy relaxation in glass. Here, we find that vitreous silica (as a strong system) exhibits striking anomalies in both glass transition and enthalpy...... relaxation compared to fragile oxide systems. The anomalous enthalpy relaxation of vitreous silica is discovered by performing the hyperquenching-annealing-calorimetry experiments. We argue that the strong systems like vitreous silica and vitreous Germania relax in a structurally cooperative manner, whereas...... the fragile ones do in a structurally independent fashion. We discuss the origin of the anomalous enthalpy relaxation in the HQ vitreous silica....

Insignificant influence of the matrix on the melting of ice confined in decorated mesoporous silica

Science.gov (United States)

Xu, Yunbo; Zhao, Zhenyan; Wang, Lianwen

2018-01-01

For a critical examination of matrix effect on the melting of confined ice, mesoporous silica (SBA-15) are synthesised and decorated with n-Alkyl and aminopropyl groups to tune the surface hydrophobicity. Water contact angle to these decorated surfaces are estimated to be about 100° and 60°, respectively. By examining the melting of ice confined in these decorated samples, we find that the influence of the matrix is indeed not significant. The reported apparent matrix effect is more likely method effect in the determination of pore diameters as was demonstrated in our previous studies (Philos. Mag. 93 (2013), p. 1827).

X-ray micro-tomography investigation of the foaming process in the system of waste glass–silica mud–MnO{sub 2}

Energy Technology Data Exchange (ETDEWEB)

Ducman, V., E-mail: vilma.ducman@zag.si [ZAG Ljubljana, Dimičeva 12, 1000 Ljubljana (Slovenia); Korat, L.; Legat, A. [ZAG Ljubljana, Dimičeva 12, 1000 Ljubljana (Slovenia); Mirtič, B. [NTF, Aškerčeva 12, 1000 Ljubljana (Slovenia)

2013-12-15

In case of foamed lightweight aggregates (LWAs), porosity is introduced by the addition of a foaming agent to the glassy matrix, which degasses at an elevated temperature, so that the resulting gases remain trapped inside the glassy structure. The efficiency of action of MnO{sub 2} as a foaming agent in waste glass and waste glass/silica mud systems was studied. Samples were fired at different temperatures and with different dwelling times at a certain temperature, and the development of porosity was investigated by means of X-ray micro-tomography. It was found that, with the prolongation in dwelling times, the number of pores decreased, while, on the other hand, the volume of these pores increased, and that the addition of silica mud increases the foaming temperature and slows down the foaming process. - Highlights: • Preparation of lightweight aggregate from waste glass, silica sludge, and MnO{sub 2} • DTA/TG investigation of MnO{sub 2} • Characterization of pore-forming process by means of X-ray micro-tomography (μcT)

Fumed silica. Fumed silica

Energy Technology Data Exchange (ETDEWEB)

Sukawa, T.; Shirono, H. (Nippon Aerosil Co. Ltd., Tokyo (Japan))

1991-10-18

The fumed silica is explained in particulate superfineness, high purity, high dispersiveness and other remarkable characteristics, and wide application. The fumed silica, being presently produced, is 7 to 40nm in average primary particulate diameter and 50 to 380m{sup 2}/g in specific surface area. On the surface, there coexist hydrophilic silanol group (Si-OH) and hydrophobic siloxane group (Si-O-Si). There are many characteristics, mutually different between the fumed silica, made hydrophobic by the surface treatment, and untreated hydrophilic silica. The treated silica, if added to the liquid product, serves as agent to heighten the viscosity, prevent the sedimentation and disperse the particles. The highest effect is given to heighten the viscosity in a region of 4 to 9 in pH in water and alcohol. As filling agent to strengthen the elastomer and polymer, and powder product, it gives an effect to prevent the consolidation and improve the fluidity. As for its other applications, utilization is made of particulate superfineness, high purity, thermal insulation properties and adsorption characteristics. 2 to 3 patents are published for it as raw material of quartz glass. 38 refs., 16 figs., 4 tabs.

A Comparative Study of the Addition Effect of Diopside and Silica Sulfuric Acid Nanoparticles on Mechanical Properties of Glass Ionomer Cements

Directory of Open Access Journals (Sweden)

M. Rezazadeh

2016-09-01

Full Text Available The aim of the present study is to study the effects of adding  diopside (CaMgSi2O6 as well as silica sulfuric acid nanoparticles to ceramic part of glass ionomer cement (GIC in order to improve its mechanical properties. To do this, firstly, diopside (DIO nanoparticles with chemical formula of CaMgSi2O6 were synthesized using sol-gel process and then, the structural and morphological properties of synthesized diopside nanoparticles were investigated. The results of scanning electron microscopy (SEM and particle size analyzing (PSA confirmed that synthesized diopside are nanoparticles and agglomerated. Besides, the result of X-ray diffraction (XRD analyses approved the purity of diopside nanoparticles compounds. Silica sulfuric acid (SSA nanoparticles are also prepared by chemical modification of silica nanoparticles by means of chlorosulfonic acid. Fourier transform infrared spectroscopy (FTIR technique was used to find about the presence of the (SO3H groups on the surface of silica sulfuric acid nanoparticles. Furthermore, various amounts (0.1, 3 and 5 wt.% of diopside and silica sulfuric acid nanoparticles were added to the ceramic part of GIC (Fuji II GIC commercial type to produce glass ionomer cement nanocomposites. The mechanical properties of the produced nanocomposites were measured using the compressive strength, three-point flexural strength and diametral tensile strength methods. Fourier transform infrared spectroscopy technique confirmed the presence of the (SO3H groups on the surface of silica nanoparticles. The compressive strength, three-point flexural strength and diametral tensile strength were 42.5, 15.4 and 6 MPa, respectively, without addition. Although adding 1% silica solfonic acid improved nanocomposite mchanical properties by almost 122%, but maximum increase in nanocomposite mechanical properties was observed in the nanocomposites with 3% diposid, in which 160% increase was seen in the mechanical properties.

EPR study of gamma and neutron irradiation effects on KU1, KS-4V and Infrasil 301 silica glasses

International Nuclear Information System (INIS)

Lagomacini, Juan C.; Bravo, David; Leon, Monica; Martin, Piedad; Ibarra, Angel; Martin, Agustin; Lopez, Fernando J.

2011-01-01

Electron paramagnetic resonance (EPR) studies have been carried out on KU1 and KS-4V high purity quartz glasses and commercial silica Infrasil 301, irradiated with gamma rays up to a dose of 11.6 MGy and neutron fluences of 10 21 and 10 22 n/m 2 . Gamma irradiations produce a much higher concentration of defect centres (mainly E', POR and NBOHC) for KU1 and I301 than for KS-4V silica. In contrast, neutron irradiation at the highest fluence produces similar concentrations in all silica types. These results agree to a good extent with those obtained in previous optical absorption measurements. Moreover, oxygen-related centres (POR and NBOHC) have been well characterized by means of electron paramagnetic resonance.

EPR study of gamma and neutron irradiation effects on KU1, KS-4V and Infrasil 301 silica glasses

Energy Technology Data Exchange (ETDEWEB)

Lagomacini, Juan C., E-mail: jc.lagomacini@uam.es [Dept. Fisica de Materiales, Universidad Autonoma de Madrid, E-28049 Madrid (Spain); Bravo, David [Dept. Fisica de Materiales, Universidad Autonoma de Madrid, E-28049 Madrid (Spain); Leon, Monica; Martin, Piedad; Ibarra, Angel [Materiales para Fusion, CIEMAT, Avda. Complutense 22, E-28040 Madrid (Spain); Martin, Agustin [Dept. Fisica e Instalaciones, ETS Arquitectura UPM, E-28040 Madrid (Spain); Lopez, Fernando J. [Dept. Fisica de Materiales, Universidad Autonoma de Madrid, E-28049 Madrid (Spain)

2011-10-01

Electron paramagnetic resonance (EPR) studies have been carried out on KU1 and KS-4V high purity quartz glasses and commercial silica Infrasil 301, irradiated with gamma rays up to a dose of 11.6 MGy and neutron fluences of 10{sup 21} and 10{sup 22} n/m{sup 2}. Gamma irradiations produce a much higher concentration of defect centres (mainly E', POR and NBOHC) for KU1 and I301 than for KS-4V silica. In contrast, neutron irradiation at the highest fluence produces similar concentrations in all silica types. These results agree to a good extent with those obtained in previous optical absorption measurements. Moreover, oxygen-related centres (POR and NBOHC) have been well characterized by means of electron paramagnetic resonance.

Surface layer effects on waste glass corrosion

International Nuclear Information System (INIS)

Feng, X.

1993-01-01

Water contact subjects waste glass to chemical attack that results in the formation of surface alteration layers. Two principal hypotheses have been advanced concerning the effect of surface alteration layers on continued glass corrosion: (1) they act as a mass transport barrier and (2) they influence the chemical affinity of the glass reaction. In general, transport barrier effects have been found to be less important than affinity effects in the corrosion of most high-level nuclear waste glasses. However, they can be important under some circumstances, for example, in a very alkaline solution, in leachants containing Mg ions, or under conditions where the matrix dissolution rate is very low. The latter suggests that physical barrier effect may affect the long-term glass dissolution rate. Surface layers influence glass reaction affinity through the effects of the altered glass and secondary phases on the solution chemistry. The reaction affinity may be controlled by various precipitates and crystalline phases, amorphous silica phases, gel layer, or all the components of the glass. The surface alteration layers influence radionuclide release mainly through colloid formation, crystalline phase incorporation, and gel layer retention. This paper reviews current understanding and uncertainties

Porous SiO2 nanofiber grafted novel bioactive glass-ceramic coating: A structural scaffold for uniform apatite precipitation and oriented cell proliferation on inert implant.

Science.gov (United States)

Das, Indranee; De, Goutam; Hupa, Leena; Vallittu, Pekka K

2016-05-01

A composite bioactive glass-ceramic coating grafted with porous silica nanofibers was fabricated on inert glass to provide a structural scaffold favoring uniform apatite precipitation and oriented cell proliferation. The coating surfaces were investigated thoroughly before and after immersion in simulated body fluid. In addition, the proliferation behavior of fibroblast cells on the surface was observed for several culture times. The nanofibrous exterior of this composite bioactive coating facilitated homogeneous growth of flake-like carbonated hydroxyapatite layer within a short period of immersion. Moreover, the embedded porous silica nanofibers enhanced hydrophilicity which is required for proper cell adhesion on the surface. The cells proliferated well following a particular orientation on the entire coating by the assistance of nanofibrous scaffold-like structural matrix. This newly engineered composite coating was effective in creating a biological structural matrix favorable for homogeneous precipitation of calcium phosphate, and organized cell growth on the inert glass surface. Copyright © 2016 Elsevier B.V. All rights reserved.

Atomic dynamics of tin nanoparticles embedded into porous glass

Energy Technology Data Exchange (ETDEWEB)

Parshin, P. P.; Zemlyanov, M. G., E-mail: zeml@isssph.kiae.ru; Panova, G. Kh.; Shikov, A. A. [Russian Research Centre Kurchatov Institute (Russian Federation); Kumzerov, Yu. A.; Naberezhnov, A. A. [Russian Academy of Sciences, Ioffe Physicotechnical Institute (Russian Federation); Sergueev, I.; Crichton, W. [European Synchrotron Radiation Facility (France); Chumakov, A. I. [Russian Research Centre Kurchatov Institute (Russian Federation); Rueffer, R. [European Synchrotron Radiation Facility (France)

2012-03-15

The method of resonant nuclear inelastic absorption of synchrotron radiation has been used to study the phonon spectrum for tin nanoparticles (with a natural isotope mixture) embedded into a porous glassy (silica) matrix with an average pore diameter of 7 nm in comparison to the analogous spectrum of bulk tin enriched with {sup 119}Sn isotope. Differences between the spectra have been observed, which are related to both the dimensional effects and specific structural features of the porous glass-tin nanocomposite. Peculiarities in the dynamics of tin atoms embedded into nanopores of glass are interpreted in terms of a qualitative model of the nanocomposite structure.

Atomic dynamics of tin nanoparticles embedded into porous glass

International Nuclear Information System (INIS)

Parshin, P. P.; Zemlyanov, M. G.; Panova, G. Kh.; Shikov, A. A.; Kumzerov, Yu. A.; Naberezhnov, A. A.; Sergueev, I.; Crichton, W.; Chumakov, A. I.; Rüffer, R.

2012-01-01

The method of resonant nuclear inelastic absorption of synchrotron radiation has been used to study the phonon spectrum for tin nanoparticles (with a natural isotope mixture) embedded into a porous glassy (silica) matrix with an average pore diameter of 7 nm in comparison to the analogous spectrum of bulk tin enriched with 119 Sn isotope. Differences between the spectra have been observed, which are related to both the dimensional effects and specific structural features of the porous glass-tin nanocomposite. Peculiarities in the dynamics of tin atoms embedded into nanopores of glass are interpreted in terms of a qualitative model of the nanocomposite structure.

Glass leaching performance

International Nuclear Information System (INIS)

Chick, L.A.; Turcotte, R.P.

1983-05-01

Current understanding of the leaching performance of high-level nuclear waste (HLW) glass is summarized. The empirical model of waste glass leaching behavior developed shows that at high water flow rates the glass leach rate is kinetically limited to a maximum value. At intermediate water flow rates, leaching is limited by the solution concentration of silica and decreases with decreasing water flow rates. Release of soluble elements is controlled by silica dissolution because silica forms the binding network of the glass. At low water flow rates, mass loss rates reach values controlled by formation rates of alteration minerals, or by diffusion of dissolution products through essentially stagnant water. The parameters reviewed with respect to their quantifiable influence on leaching behavior include temperature, pH, leachant composition, glass composition, thermal history, and radiation. Of these, temperature is most important since the rate of mass loss approximately doubles with each 10 0 C increase in dilute solutions. The pH has small effects within the 4 to 10 range. The chemical composition of the leachant is most important with regard to its influence on alteration product formation. Glass composition exhibits the largest effects at high flow rates where improved glasses leach from ten to thirty times slower than glass 76 to 68. The effects of the thermal history (devitrification) of the glass are not likely to be significant. Radiation effects are important primarily in that radiolysis can potentially drive pH values to less than 4. Radiation damage to the glass causes insignificant changes in leaching performance

Photon emission induced by brittle fracture of borosilicate glasses

Energy Technology Data Exchange (ETDEWEB)

Shiota, Tadashi, E-mail: tshiota@ceram.titech.ac.jp [Department of Metallurgy and Ceramic Science, Tokyo Institute of Technology, 2-12-1 Ookayama, Meguro-ku, Tokyo 152-8550 (Japan); Sato, Yoshitaka [Department of Metallurgy and Ceramic Science, Tokyo Institute of Technology, 2-12-1 Ookayama, Meguro-ku, Tokyo 152-8550 (Japan); Kishi, Tetsuo [Department of Chemistry and Materials Science, Tokyo Institute of Technology, 2-12-1 Ookayama, Meguro-ku, Tokyo 152-8550 (Japan); Yasuda, Kouichi [Department of Metallurgy and Ceramic Science, Tokyo Institute of Technology, 2-12-1 Ookayama, Meguro-ku, Tokyo 152-8550 (Japan)

2016-05-15

Photon emission (PE) at wavelength ranges of 430–490 nm (B-PE), 500–600 nm (G-PE) and 610–680 nm (R-PE) caused by brittle fracture was simultaneously measured in the nanosecond-to-microsecond and millisecond time domains for two types of borosilicate glasses: Pyrex-type Tempax glass and BK7 glass. The results were compared to those for silica and soda lime glasses. The time dependence of the PE of Tempax glass was similar to that of silica glass, while the PE intensity was lower. Because Tempax glass contains both silica-rich and borate-rich amorphous phases, the PE must be mainly produced by the fracture of the silica-rich phase. Moreover, the proportion of B-PE of Tempax glass was higher than that of silica glass. This suggests that the measured B-PE might also include very weak PE caused by the fracture of the borate-rich phase. The PE time dependence of BK7 glass was similar to that of soda lime glass, which was different from the case for Tempax glass. The PE intensity of BK7 glass was slightly higher than that of soda lime glass, but much lower than that of Tempax glass. The result indicates that non-bridging oxygen in the glasses affects crack propagation behavior and reduces the PE. - Highlights: • Photon emission (PE) upon brittle fracture of borosilicate glasses was measured. • Pyrex-type Tempax and BK7 glasses showed different PE characteristics. • The rupture of Si–O bonds produces much stronger PE than that of B–O bonds. • Non-bridging oxygen in glass affects crack propagation behavior and reduces the PE.

Ultrafine Ceramic Grains Embedded in Metallic Glass Matrix: Achieving Superior Wear Resistance via Increase in Both Hardness and Toughness.

Science.gov (United States)

Yang, Lina; Wen, Mao; Dai, Xuan; Cheng, Gang; Zhang, Kan

2018-05-09

As structural materials, crystalline or metallic glass materials have attracted scientific and practical interests. However, some mechanisms involving critical size and shear bands have adverse effects on their mechanical properties. Here, we counter these two effects by introducing a special structure with ultrafine ceramic grains (with a diameter of ∼2.0 nm) embedded into a metallic glass matrix, wherein the grains are mainly composed of a Ta-W-N solid solution structure in nature, surrounded by a W-based amorphous matrix that contains Ta and N atoms. Such a structure is in situ formed during preparation, which combines the merits of both phases to achieve simultaneous increase in hardness and toughness relative to references (pure TaN and W) and thus superior wear resistance. Even more remarkable, a favorable variation of increased hardness but reduced elasticity modulus can be induced by this structure. Intrinsically, ultrafine ceramic grains (free of dislocations), embedded in the metallic glass matrix, could prevent shear band propagation within the glass matrix and further improve the hardness of the matrix material. In return, such glass matrix allows for stiffness neutralization and structural relaxation to reduce the elasticity modulus of ceramic grains. This study will offer a new guidance to fabricate ultrahigh-performance metal-based composites.

Molecular dynamics study of a nuclear waste glass matrix with plutonium

International Nuclear Information System (INIS)

Meis, C.; Delaye, J.M.; Ghaleb, D.

1999-01-01

Molecular dynamics simulation techniques were applied to model the incorporation of plutonium in the French nuclear waste glass matrix. Born-Mayer-Huggins analytical potentials were established to characterize short-range interactions between Pu-O and Pu-Pu pairs; the potentials were fitted to the structural properties of plutonium dioxide in the light of a recent experimental study showing that plutonium is found as Pu(IV) in the glass. The transferability of the established potentials to the glass structure is discussed, and the potential parameters are further refined by molecular dynamics simulations in an aluminoborosilicate glass to obtain mean Pu-O interatomic distances and first-neighbor coordination numbers matching the experimental values as closely as possible. Previously published Born-Mayer-Huggins potentials supplemented by Stillinger-Weber three-body terms were used for oxygen-cation and cation-cation interactions. The difficulties encountered in establishing a Pu-O potential that provides satisfactory results in both oxides and glasses are also discussed

Wear behaviour of Zr-based in situ bulk metallic glass matrix ...

Indian Academy of Sciences (India)

based bulk metallic glass (BMG) and its in situ BMG matrix composites with diameter of 3 mm were fabricated by conventional Cu-mould casting method and ... The composites showed lower friction coefficient and wear rate than the pure BMG.

Barium borosilicate glass - a potential matrix for immobilization of sulfate bearing high-level radioactive liquid waste

International Nuclear Information System (INIS)

Kaushik, C.P.; Mishra, R.K.; Sengupta, P.; Kumar, Amar; Das, D.; Kale, G.B.; Raj, Kanwar

2006-01-01

Borosilicate glass formulations adopted worldwide for immobilization of high-level radioactive liquid waste (HLW) is not suitable for sulphate bearing HLW, because of its low solubility in such glass. A suitable glass matrix based on barium borosilicate has been developed for immobilization of sulphate bearing HLW. Various compositions based on different glass formulations were made to examine compatibility with waste oxide with around 10 wt% sulfate content. The vitrified waste product obtained from barium borosilicate glass matrix was extensively evaluated for its characteristic properties like homogeneity, chemical durability, glass transition temperature, thermal conductivity, impact strength, etc. using appropriate techniques. Process parameters like melt viscosity and pour temperature were also determined. It is found that SB-44 glass composition (SiO 2 : 30.5 wt%, B 2 O 3 : 20.0 wt%, Na 2 O: 9.5 wt% and BaO: 19.0 wt%) can be safely loaded with 21 wt% waste oxide without any phase separation. The other product qualities of SB-44 waste glass are also found to be on a par with internationally adopted waste glass matrices. This formulation has been successfully implemented in plant scale

Study of a new glass matrix by thermoluminescent technique for high-dose dosimetry

Energy Technology Data Exchange (ETDEWEB)

Ferreira, Pamela Z.; Carvalho, Gabriel S. Marchiori de; Cunha, Diego M. da; Dantas, Noelio O.; Silva, Anielle C.A.; Neves, Lucio P.; Perini, Ana P., E-mail: anapaula.perini@ufu.br [Universidade Federal de Uberlandia (UFU), MG (Brazil). Instituto de Fisica; Linda, V.E. Caldas [Instituto de Pesquisas Energeticas e Nucleares (IPEN/CNEN-SP), Sao Paulo, SP (Brazil); Carrera, Betzabel N.S.; Watanabe, Shigueo [Universidade de Sao Paulo (IF/USP), Sao Paulo, SP (Brazil). Instituto de Fisica

2016-07-01

The thermoluminescence technique is widely used for both personal and for high-dose dosimetry. In this work, the thermoluminescence technique was utilized to study a new glass matrix, with nominal composition of 20Li{sub 2}CO{sub 3}.10Al{sub 2}O{sub 3}.30BaO.40B{sub 2}O{sub 3} (mol%), irradiated with different doses in a {sup 60}Co source. The glow curves and the dose-response curve were obtained for radiation doses of 10, 50, 100, 200 e 700 Gy. The results showed that this new glass matrix has potential use in high-dose dosimetry. (author)

Porous glasses as a matrix for incorporation of photonic materials. Pore determination by positron annihilation lifetime spectroscopy

Science.gov (United States)

Reisfeld, Pore determination by positron annihilation lifetime spectroscopy R.; Saraidarov, T.; Jasinska, B.

2004-07-01

Porous glasses prepared by the sol-gel technique have a variety of applications when incorporated by photonic materials: tunable lasers, sensors, luminescence solar concentrators, semiconductor quantum dots, biological markers. The known methods of pore size determinations, the nitrogen adsorption and mercury porosimetry allow to determine the sizes of open pores. Positron annihilation lifetime spectroscopy (PALS) allows to determine pore sizes also of closed pores. As an example we have performed measurements of non-doped zirconia-silica-polyurethane (ZSUR) ormocer glasses and the same glasses doped with lead sulfide quantum dots. The pore radii range between 0.25-0.38 nm, total surface area 15.5-23.8 m 2/g.

Properties Of Soda/Yttria/Silica Glasses

Science.gov (United States)

Angel, Paul W.; Hann, Raiford E.

1994-01-01

Experimental study of glass-formation compositional region of soda/ yttria/silicate system and of selected physical properties of glasses within compositional region part of continuing effort to identify glasses with high coefficients of thermal expansion and high softening temperatures, for use as coatings on superalloys and as glass-to-metal seals.

Er3+-Al2O3 nanoparticles doping of borosilicate glass

International Nuclear Information System (INIS)

Massera, Jonathan; Petit, Laeticia; Hupa, Leena; Hupa, Mikko; Koponen, Joona; Glorieux, Benoit

2015-01-01

Novel borosilicate glasses were developed by adding in the glass batch Er 3+ -Al 2 O 3 nanoparticles synthetized by using a soft chemical method. A similar nanoparticle doping with modified chemical vapour deposition (MCVD) process was developed to increase the efficiency of the amplifying silica fibre in comparison to using MCVD and solution doping. It was shown that with the melt quench technique, a Er 3+ -Al 2 O 3 nanoparticle doping neither leads to an increase in the Er 3+ luminescence properties nor allows one to control the rare-earth chemical environment in a borosilicate glass. The site of Er 3+ in the Er 3+ -Al 2 O 3 nanoparticle containing glass seems to be similar as in glasses with the same composition prepared using standard raw materials. We suspect the Er 3+ ions to diffuse from the nanoparticles into the glass matrix. There was no clear evidence of the presence of Al 2 O 3 nanoparticles in the glasses after melting. (author)

Dielectric breakdown in silica-amorphous polymer nanocomposite films: the role of the polymer matrix.

Science.gov (United States)

Grabowski, Christopher A; Fillery, Scott P; Westing, Nicholas M; Chi, Changzai; Meth, Jeffrey S; Durstock, Michael F; Vaia, Richard A

2013-06-26

The ultimate energy storage performance of an electrostatic capacitor is determined by the dielectric characteristics of the material separating its conductive electrodes. Polymers are commonly employed due to their processability and high breakdown strength; however, demands for higher energy storage have encouraged investigations of ceramic-polymer composites. Maintaining dielectric strength, and thus minimizing flaw size and heterogeneities, has focused development toward nanocomposite (NC) films; but results lack consistency, potentially due to variations in polymer purity, nanoparticle surface treatments, nanoparticle size, and film morphology. To experimentally establish the dominant factors in broad structure-performance relationships, we compare the dielectric properties for four high-purity amorphous polymer films (polymethyl methacrylate, polystyrene, polyimide, and poly-4-vinylpyridine) incorporating uniformly dispersed silica colloids (up to 45% v/v). Factors known to contribute to premature breakdown-field exclusion and agglomeration-have been mitigated in this experiment to focus on what impact the polymer and polymer-nanoparticle interactions have on breakdown. Our findings indicate that adding colloidal silica to higher breakdown strength amorphous polymers (polymethyl methacrylate and polyimide) causes a reduction in dielectric strength as compared to the neat polymer. Alternatively, low breakdown strength amorphous polymers (poly-4-vinylpyridine and especially polystyrene) with comparable silica dispersion show similar or even improved breakdown strength for 7.5-15% v/v silica. At ∼15% v/v or greater silica content, all the polymer NC films exhibit breakdown at similar electric fields, implying that at these loadings failure becomes independent of polymer matrix and is dominated by silica.

Storage and sustained release of volatile substances from a hollow silica matrix

Energy Technology Data Exchange (ETDEWEB)

Wang Jiexin [Key Lab for Nanomaterials, Ministry of Education, Beijing 100029 (China); Ding Haomin [Research Center of the Ministry of Education for High Gravity Engineering and Technology, Beijing University of Chemical Technology, Beijing 100029 (China); Tao Xia [Key Lab for Nanomaterials, Ministry of Education, Beijing 100029 (China); Chen Jianfeng [Key Lab for Nanomaterials, Ministry of Education, Beijing 100029 (China)

2007-06-20

Porous hollow silica nanospheres (PHSNSs) prepared by adopting a nanosized CaCO{sub 3} template were utilized for the first time as a novel carrier for the storage and sustained release of volatile substances. Two types of volatile substances, Indian pipal from perfumes and peroxyacetic acid from disinfectants, were selected and then tested by one simple adsorption process with two separate comparative carriers, i.e. activated carbon and solid porous silica. It was demonstrated that a high storage capacity (9.6 ml{sub perfume}/mg{sub carrier}) of perfume could be achieved in a PHSNS matrix, which was almost 14 times as much as that of activated carbon. The perfume release profiles showed that PHSNSs exhibited sustained multi-stage release behaviour, while the constant release of activated carbon at a low level was discerned. Further, a Higuchi model study proved that the release process of perfume in both carriers followed a Fickian diffusion mechanism. For peroxyacetic acid as a disinfectant model, PHSNSs also displayed a much better delayed-delivery process than a solid porous silica system owing to the existence of unique hollow frameworks. Therefore, the aforementioned excellent sustained-release behaviours would make PHSNSs a promising carrier for storage and sustained delivery applications of volatile substances.

Iron phosphate glass: a promising matrix for the immobilization of Cs and Mo

International Nuclear Information System (INIS)

Hemadevi, V.; Joseph, Kitheri

2015-01-01

Presently, borosilicate glass (BSG) is the acceptable vitrification matrix for the immobilization of high level waste. The solubility of Mo in BSG is limited in the presence of Cs. As per the literature, solubility of Mo in BSG is about 2.5 wt. % in the presence of Cs. Hence it is difficult to immobilize nuclear waste rich in Cs and Mo in borosilicate glass. It is observed that the composition of Cs and Mo expressed as oxides are 10.4 and 14.7 wt. % respectively in simulated fast reactor waste. Iron phosphate glass containing 20 wt. % simulated fast reactor waste (referred as IP20FRW) was synthesized and characterized. IP20FRW contains ~ 3 wt. % of molybdenum oxide along with 2 wt. % cesium oxide. IPG is a suitable matrix for the immobilization of Cs and Mo separately. Hence it is essential to understand the glass characteristics of IPG containing both Cs and Mo. This paper explores systematic loading of both Cs and Mo such that the final composition corresponds to 10.5 wt. % Cs 2 O-15 wt. % MoO 3 -31.9 wt. % Fe 2 O 3 -42.6 wt. % P 2 O 5 . In addition to synthesis, the present study also includes understanding the change in glass characteristics of IPG containing both Cs and Mo. The possibility of higher percent loading of both Cs and Mo in IPG demonstrates the better glass forming characteristics of IPG. The synthesis and characterization of Cs-Mo loaded glasses will be discussed in this paper. (author)

A study of positron properties in quartz crystals and synthetic silica glass

International Nuclear Information System (INIS)

Anwand, W.; Brauer, G.; Hesegawa, M.; Dersch, O.; Rauch, F.

2001-01-01

The monoenergetic positron beamline 'SPONSOR' at Rossendorf has been used to investigate the positron behaviour in a naturally grown Brasilian quartz, two synthetic quartz crystals of different origin, and synthetic silica glass. The measurements allow us to obtain the positron diffusion length of free positrons and Bloch para-positronium, if formed, in these materials. In addition, hydrothermal treatment of a synthetic quartz has been used to introduce hydrogen into the crystal up to a certain depth. The presence of hydrogen is found to influence the formation of para-positronium. The depth distribution of hydrogen has been measured independently by the nuclear reaction analysis, and will be discussed in comparison with the results deduced from the positron studies. (author)

Gold nano-particles fixed on glass

International Nuclear Information System (INIS)

Worsch, Christian; Wisniewski, Wolfgang; Kracker, Michael; Rüssel, Christian

2012-01-01

Highlights: ► We produced wear resistant gold–ruby coatings on amorphous substrates. ► Thin sputtered gold layers were covered by or embedded in silica coatings. ► Annealing above T g of the substrate glass led to the formation of gold nano particles. ► A 1 1 1-texture of the gold particles is observed via XRD and EBSD. ► EBSD-patterns can be acquired from crystals covered by a thin layer of glass. - Abstract: A simple process for producing wear resistant gold nano-particle coatings on transparent substrates is proposed. Soda-lime-silica glasses were sputtered with gold and subsequently coated with SiO 2 using a combustion chemical vapor deposition technique. Some samples were first coated with silica, sputtered with gold and then coated with a second layer of silica. The samples were annealed for 20 min at either 550 or 600 °C. This resulted in the formation of round, well separated gold nano-particles with sizes from 15 to 200 nm. The color of the coated glass was equivalent to that of gold–ruby glasses. Silica/gold/silica coatings annealed at 600 °C for 20 min were strongly adherent and scratch resistant. X-ray diffraction and electron backscatter diffraction (EBSD) were used to describe the crystal orientations of the embedded particles. The gold particles are preferably oriented with their (1 1 1) planes perpendicular to the surface.

The effect of clay on the dissolution of nuclear waste glass

Science.gov (United States)

Lemmens, K.

2001-09-01

In a nuclear waste repository, the waste glass can interact with metals, backfill materials (if present) and natural host rock. Of the various host rocks considered, clays are often reported to delay the onset of the apparent glass saturation, where the glass dissolution rate becomes very small. This effect is ascribed to the sorption of silica or other glass components on the clay. This can have two consequences: (1) the decrease of the silica concentration in solution increases the driving force for further dissolution of glass silica, and (2) the transfer of relatively insoluble glass components (mainly silica) from the glass surface to the clay makes the alteration layer less protective. In recent literature, the latter explanation has gained credibility. The impact of the environmental materials on the glass surface layers is however not well understood. Although the glass dissolution can initially be enhanced by clay, there are arguments to assume that it will decrease to very low values after a long time. Whether this will indeed be the case, depends on the fate of the released glass components in the clay. If they are sorbed on specific sites, it is likely that saturation of the clay will occur. If however the released glass components are removed by precipitation (growth of pre-existing or new secondary phases), saturation of the clay is less likely, and the process can continue until exhaustion of one of the system components. There are indications that the latter mechanism can occur for varying glass compositions in Boom Clay and FoCa clay. If sorption or precipitation prevents the formation of protective surface layers, the glass dissolution can in principle proceed at a high rate. High silica concentrations are assumed to decrease the dissolution rate (by a solution saturation effect or by the impact on the properties of the glass alteration layer). In glass corrosion tests at high clay concentrations, silica concentrations are, however, often higher

The effect of clay on the dissolution of nuclear waste glass

International Nuclear Information System (INIS)

Lemmens, K.

2001-01-01

In a nuclear waste repository, the waste glass can interact with metals, backfill materials (if present) and natural host rock. Of the various host rocks considered, clays are often reported to delay the onset of the apparent glass saturation, where the glass dissolution rate becomes very small. This effect is ascribed to the sorption of silica or other glass components on the clay. This can have two consequences: (1) the decrease of the silica concentration in solution increases the driving force for further dissolution of glass silica, and (2) the transfer of relatively insoluble glass components (mainly silica) from the glass surface to the clay makes the alteration layer less protective. In recent literature, the latter explanation has gained credibility. The impact of the environmental materials on the glass surface layers is however not well understood. Although the glass dissolution can initially be enhanced by clay, there are arguments to assume that it will decrease to very low values after a long time. Whether this will indeed be the case, depends on the fate of the released glass components in the clay. If they are sorbed on specific sites, it is likely that saturation of the clay will occur. If however the released glass components are removed by precipitation (growth of pre-existing or new secondary phases), saturation of the clay is less likely, and the process can continue until exhaustion of one of the system components. There are indications that the latter mechanism can occur for varying glass compositions in Boom Clay and FoCa clay. If sorption or precipitation prevents the formation of protective surface layers, the glass dissolution can in principle proceed at a high rate. High silica concentrations are assumed to decrease the dissolution rate (by a solution saturation effect or by the impact on the properties of the glass alteration layer). In glass corrosion tests at high clay concentrations, silica concentrations are, however, often higher

Radiation hardening of sol gel-derived silica fiber preforms through fictive temperature reduction.

Science.gov (United States)

Hari Babu, B; Lancry, Matthieu; Ollier, Nadege; El Hamzaoui, Hicham; Bouazaoui, Mohamed; Poumellec, Bertrand

2016-09-20

The impact of fictive temperature (Tf) on the evolution of point defects and optical attenuation in non-doped and Er3+-doped sol-gel silica glasses was studied and compared to Suprasil F300 and Infrasil 301 glasses before and after γ-irradiation. To this aim, sol-gel optical fiber preforms have been fabricated by the densification of erbium salt-soaked nanoporous silica xerogels through the polymeric sol-gel technique. These γ-irradiated fiber preforms have been characterized by FTIR, UV-vis-NIR absorption spectroscopy, electron paramagnetic resonance, and photoluminescence measurements. We showed that a decrease in the glass fictive temperature leads to a decrease in the glass disorder and strained bonds. This mainly results in a lower defect generation rate and thus less radiation-induced attenuation in the UV-vis range. Furthermore, it was found that γ-radiation "hardness" is higher in Er3+-doped sol-gel silica compared to un-doped sol-gel silica and standard synthetic silica glasses. The present work demonstrates an effective strategy to improve the radiation resistance of optical fiber preforms and glasses through glass fictive temperature reduction.

Defect production in silica glasses under gamma-irradiation at the quenched nuclear reactor

International Nuclear Information System (INIS)

Mussaeva, M.A.; Kalanov, M.U.; Ibragimova, E.M.; Sandalov, V.N.; Muminov, M.L.

2004-01-01

Full text: Radiation defect production in oxides is highly interesting for atom and solar energy, and also for burying nuclear waste. Combine effect of neutron and gamma-radiation on materials was studied extensively and only neutrons are believed to displace atoms, although 60 Co-gamma quanta were proved to displace light anions (O, F) by inelastic mechanism. On the example of polished plates of pure fused quartz and barium-silica glasses containing nano-crystalline inclusions, and also nano-porous glass, the effect of gamma-radiation of the quenched reactor was studied in the energy range of 0.2-7 MeV. The time period was selected when practically constant current ∼10-20 nA is maintained in the ionizing chamber, corresponding to the average gamma-flux of 15-30 Gy/s. Optical absorption and photoluminescence spectra and also structure of the grasses were studied. It turned out, that the charged oxygen vacancies accumulation rate is higher in Barium glass than in the pure one, because for SiO 2 with small Z the photoelectric effect is weak, while the Compton scattering and photonuclear reactions prevail, and for Barium - just the opposite. The radiation-induced growth of the crystalline precipitates was noticed in the both glasses, which before had been attributed to the elastic atom displacements by fast neutrons. The density of Ba-glass increases with irradiation. The efficiency of defect production by the gamma-component even of the quenched reactor turned out much higher than that under irradiation with 60 Co gamma-source of ∼1.25 MeV to the equivalent dose at the current dose rate of ∼ 7 Gy/s (and before at 45 Gy/s). A 100-times increase of the surface proton conductivity was discovered in the porous glasses under gamma-irradiation due to water vapor radiolysis on the pore surface. The irradiated porous glass is recommended as an active electrode in the hydrogen fuel element. The work was done under the grant F2.1.2 from Center of Science and Technology

Effectiveness of high temperature innovative geometry fixed ceramic matrix regenerators used in glass furnaces

Directory of Open Access Journals (Sweden)

Wołkowycki Grzegorz

2016-03-01

Full Text Available The paper presents the effectiveness of waste heat recovery regenerators equipped with innovative ceramic matrix forming an integral part of a real glass furnace. The paper full description of the regenerators’ matrix structure with its dimensions, thermo-physical properties and operating parameters is included experimentally determined was the effectiveness of the regenerators has been descrbed using the obtained experimental data such as the operating temperature, gas flows as well as the gases generated during the liquid glass manufacturing process. The effectiveness values refer not only to the heating cycle when the regenerator matrix is heated by combustion gases but also to the cooling cycle in which the matrix is cooled as a result of changes in the direction of the flowing gas. On the basis of the determined effectiveness values for both cycles and measurement uncertainties it was possible, to calculate the weighted average efficiency for each of the regenerators.

Effects of annealing atmosphere on ZnO{sup -} ions-implanted silica glass: synthesis of Zn and ZnO nanoparticles

Energy Technology Data Exchange (ETDEWEB)

Kuiri, P K [Department of Physics, Achhruram Memorial College, P.O. Jhalda, Purulia 723202 (India); Mahapatra, D P, E-mail: kuiripk@gmail.co [Institute of Physics, Sachivalaya Marg, Bhubaneswar 751005 (India)

2010-10-06

The effects of annealing atmosphere (argon or oxygen) on Zn nanoparticles (NPs), embedded in silica glass, synthesized by implanting 50 keV ZnO{sup -} ions to a fluence of 7 x 10{sup 16} cm{sup -2} have been studied. Optical absorption (OA) measurements carried out on the as-implanted samples have been found to result in a surface plasmon resonance (SPR) band centred at {approx}255 nm due to the presence of Zn NPs in the silica glass. An increase in SPR peak intensity with a corresponding reduction of its full width at half maximum have been seen in the OA spectrum taken from the as-implanted sample following annealing in Ar ambient at 700 {sup 0}C for 2 h, indicating a growth in the size of Zn NPs. However, annealing the as-implanted sample in O{sub 2} gas at 700 {sup 0}C for 2 h has been found to result in a steep absorption edge at {approx}364 nm in the OA spectrum which indicates the formation of ZnO NPs. These ZnO NPs show quantum confinement effects due to their small sizes. No observable photoluminescence (PL) emission has been seen from Zn NPs, whereas an excitonic band at {approx}368 nm and three deep-level PL emission bands at {approx}453 nm, {approx}521 nm and {approx}650 nm, respectively, have been seen from ZnO NPs. It was argued that the deep-level PLs were due to the singly ionized oxygen vacancies located at ZnO NPs' surfaces. These observations suggest that ZnO NPs were formed due to oxidation of Zn NPs via interaction with the indiffusing O{sub 2} molecules during annealing in O{sub 2} ambient, but not with the interaction of the implanted oxygen in silica glass.

Optical Fibre NO2 Sensor Based on Lutetium Bisphthalocyanine in a Mesoporous Silica Matrix

Directory of Open Access Journals (Sweden)

Marc Debliquy

2018-03-01

Full Text Available In this article, we describe a NO2 sensor consisting of a coating based on lutetium bisphthalocyanine (LuPc2 in mesoporous silica. The sensor exploits the absorption spectrum change of this material which strongly and reversibly decreases in contact with NO2. NO2 is measured by following the amplitude change in the reflected spectrum of the coating deposited on the tip of a silica fibre. As diffusion of NO2 in LuPc2 is slow, the response time could be slow. To reduce it, the active molecules are dispersed in a mesoporous silica matrix deposited by a sol-gel process (Evaporation Induced Self Assembly avoiding the formation of large crystals. Doing so, the response is fairly fast. As the recovery is slow at room temperature, the recovery time is reduced by exposure to UV light at 365 nm. This UV light is directly introduced in the fibre yielding a practical sensor sensitive to NO2 in the ppm range suitable for pollution monitoring.

Fabrication of semi-transparent super-hydrophobic surface based on silica hierarchical structures

KAUST Repository

Chen, Ping-Hei

2011-01-01

This study successfully develops a versatile method of producing superhydrophobic surfaces with micro/nano-silica hierarchical structures on glass surfaces. Optically transparent super hydrophobic silica thin films were prepared by spin-coating silica particles suspended in a precursor solution of silane, ethanol, and H2O with molar ratio of 1:4:4. The resulting super hydrophobic films were characterized by scanning electron microscopy (SEM), optical transmission, and contact angle measurements. The glass substrates in this study were modified with different particles: micro-silica particles, nano-silica particles, and hierarchical structures. This study includes SEM micrographs of the modified glass surfaces with hierarchical structures at different magnifications. © 2011 The Korean Society of Mechanical Engineers and Springer-Verlag Berlin Heidelberg.

Nano-phase separation and structural ordering in silica-rich mixed network former glasses.

Science.gov (United States)

Liu, Hao; Youngman, Randall E; Kapoor, Saurabh; Jensen, Lars R; Smedskjaer, Morten M; Yue, Yuanzheng

2018-06-13

We investigate the structure, phase separation, glass transition, and crystallization in a mixed network former glass series, i.e., B2O3-Al2O3-SiO2-P2O5 glasses with varying SiO2/B2O3 molar ratio. All the studied glasses exhibit two separate glassy phases: droplet phase (G1) with the size of 50-100 nm and matrix phase (G2), corresponding to a lower calorimetric glass transition temperature (Tg1) and a higher one (Tg2), respectively. Both Tg values decrease linearly with the substitution of B2O3 for SiO2, but the magnitude of the decrease is larger for Tg1. Based on nuclear magnetic resonance and Raman spectroscopy results, we infer that the G1 phase is rich in boroxol rings, while the G2 phase mainly involves the B-O-Si network. Both phases contain BPO4- and AlPO4-like units. Ordered domains occur in G2 upon isothermal and dynamic heating, driven by the structural heterogeneity in the as-prepared glasses. The structural ordering lowers the activation energy of crystal growth, thus promoting partial crystallization of G2. These findings are useful for understanding glass formation and phase separation in mixed network former oxide systems, and for tailoring their properties.

Glass formation, properties and structure of soda-yttria-silica glasses

Science.gov (United States)

Angel, Paul W.; Hann, Raiford E.

1992-01-01

The glass formation region of the soda yttria silicate system was determined. The glasses within this region were measured to have a density of 2.4 to 3.1 g/cu cm, a refractive index of 1.50 to 1.60, a coefficient of thermal expansion of 7 x 10(exp -6)/C, softening temperatures between 500 and 780 C, and Vickers hardness values of 3.7 to 5.8 GPa. Aqueous chemical durability measurements were made on select glass compositions while infrared transmission spectra were used to study the glass structure and its effect on glass properties. A compositional region was identified which exhibited high thermal expansion, high softening temperatures, and good chemical durability.

High thermal behavior of a new glass ceramic developed from silica xerogel/SnO{sub 2} composite

Energy Technology Data Exchange (ETDEWEB)

Aripin, H., E-mail: aripin@unsil.ac.id [Faculty of Learning Teacher and Education Science, Siliwangi University, Jl. Siliwangi 24 Tasikmalaya 46115, West Java (Indonesia); Mitsudo, Seitaro, E-mail: mitsudo@fir.u-fukui.ac.jp [Research Center for Development of Far Infrared Region (FIR Center), University of Fukui, Bunkyo 3-9-1 Fukui 910-8507 (Japan); Sudiana, I. Nyoman, E-mail: sudiana75@yahoo.com [Departement Physics, Faculty of Mathematics and Natural Science, Haluoleo University, Kampus Bumi Tridharma Anduonohu, Kendari 93232 (Indonesia); Priatna, Edvin, E-mail: ujack05@yahoo.com [Department of Electrical Engineering, Faculty of Engineering, Siliwangi University, Tasikmalaya (Indonesia); Sabchevski, Svilen, E-mail: sabch@ie.bas.bg [Lab. Plasma Physics and Engineering, Institute of Electronics of the Bulgarian Academy of Sciences, 72 Tzarigradsko Shose Blvd., Sofia 1784 (Bulgaria)

2016-02-08

In this investigation, a new glass ceramics have been produced by mixing SnO{sub 2} and amorphous silica xerogel (ASX) extracted from sago waste ash. The composition has been prepared by adding 10 mol% of SnO{sub 2} into SX. The samples have been dry pressed and sintered in the temperature range between 800 °C and 1500 °C. The effects of temperature on the crystallization of silica xerogel after adding SnO{sub 2} and their relationship to bulk density have been studied. The crystallization process of the silica xerogel/SnO{sub 2} composite has been examined by an X-ray diffraction (XRD) and the bulk density has been characterized on the basis of the experimental data obtained using Archimedes′ principle. It has been found that an addition of SnO{sub 2} confers an appreciable effect on the grain and from the interpretation of XRD patterns allow one to explain the increase in the density by an increased crystallite size of SnO{sub 2} in the composite.

Immobilisation of radio cesium loaded ammonium molybdo phosphate in glass matrices

International Nuclear Information System (INIS)

Yalmali, Vrunda S.; Singh, I.J.; Sathi Sasidharan, N.; Deshingkar, D.S.

2004-11-01

Long half life and easy availability from high level wastes make 137 Cesium most economical radiation source. High level liquid waste processing for 137 Cesium removal has become easier due to development of Cesium specific granulated ammonium molybdophosphate (AMP) composite. In such applications, resulting spent composite AMP itself represents high active solid waste and immobilization of these materials in cement may not be acceptable. Studies on immobilization of 137 Cs loaded AMP were taken up in order to achieve twin goals of increasing safety and minimizing processing costs of the final matrix. Studies indicated that phosphate modified sodium borosilicate SPNM glasses prepared under usual oxidizing conditions are not suitable for immobilization of 137 Cs loaded on AMP .Phosphate glasses containing Na 2 O, P 2 O 5 , B 2 O 3 , Fe 2 O 3 , Al 2 O 3 and SiO 2 as major constituents are capable of incorporating 6 to 8 % AMP. The Normalized Leach rates of these glasses for sodium, cesium, boron and silica are 10 -4 to 10 -6 gm/cm 2 /day which are comparable to or better than those reported for NBS glasses incorporating HLW. Homogeneity of the final matrix was confirmed by x-ray diffraction analysis. Further studies on characterization of these glasses would establish their acceptability. (author)

Development of a glass matrix for vitrification of sulphate bearing high level radioactive liquid waste

International Nuclear Information System (INIS)

Kaushik, C.P.; Mishra, R.K.; Thorat, Vidya; Ramchandran, M.; Amar Kumar; Ozarde, P.D.; Raj, Kanwar; Das, D.

2004-07-01

High level radioactive liquid waste (HLW) is generated during reprocessing of spent nuclear fuel. In the earlier reprocessing flow sheet ferrous sulphamate has been used for valancy adjustment of Pu from IV to III for effective separation. This has resulted in generation of HLW containing significance amount of sulphate. Internationally borosilicate glass matrix has been adopted for vitrification of HLW. The first Indian vitrification facility at Waste Immobilislition Plant (WIP), Tarapur a five component borosilicate matrix (SiO 2 :B 2 O 3 :Na 2 O : MnO : TiO 2 ) has been used for vitrification of waste. However at Trombay HLW contain significant amount of sulphate which is not compatible with standard borosilicate formulation. Extensive R and D efforts were made to develop a glass formulation which can accommodate sulphate and other constituents of HLW e.g., U, Al, Ca, etc. This report deals with development work of a glass formulations for immobilization of sulphate bearing waste. Different glass formulations were studied to evaluate the compatibility with respect to sulphate and other constituents as mentioned above. This includes sodium, lead and barium borosilicate glass matrices. Problems encountered in different glass matrices for containment of sulphate have also been addressed. A glass formulation based on barium borosilicate was found to be effective and compatible for sulphate bearing high level waste. (author)

Studies of ionizing radiation shielding effectiveness of silica-based commercial glasses used in Bangladeshi dwellings

Directory of Open Access Journals (Sweden)

Sabina Yasmin

2018-06-01

Full Text Available Following the rapid growing economy, the Bangladeshi dwellers are replacing their traditional (mud-, bamboo-, and wood-based houses to modern multistoried buildings, where different types of glasses are being used as decorative as well as structural materials due to their various advantageous properties. In this study, we inquire the protective and dosimetric capability of commercial glasses for ionizing radiation. Four branded glass samples (PHP-Bangladesh, Osmania-Bangladesh, Nasir-Bangladesh, and Rider-China of same thickness and color but different elemental weight fractions were analyzed for shielding and dosimetric properties. The chemical composition of the studied material was evaluated by EDX technique. A well-shielded HPGe γ-ray spectrometer combined with associated electronics was used to evaluate the attenuation coefficients of the studied materials for 59 keV, 661 keV, 1173 keV and 1332 keV photon energies. A number of shielding parameters- half value layer (HVL, radiation protection efficiency (RPE and effective atomic number (Zeff were also evaluated. The data were compared with the available literature (where applicable to understand its shielding capability relative to the standard materials such as lead. Among the studied brands, Rider (China shows relatively better indices to be used as ionizing radiation shielding material. The obtained, Zeff of the studied glass samples showed comparable values to the TLD-200 dosimeter, thus considered suitable for environmental radiation monitoring purposes. Keywords: Silica-based commercial glass, HPGe γ-ray spectrometry, EDX analyses, Shielding effectiveness, Dosimetric properties

Deep-UV Raman spectroscopic analysis of structure and dissolution rates of silica-rich sodium borosilicate glasses

Energy Technology Data Exchange (ETDEWEB)

Windisch, Charles F.; Pierce, Eric M.; Burton, Sarah D.; Bovaird, Chase C.

2011-03-24

As part of ongoing studies to evaluate the relationships between structural variations in silicate glasses and rates of glass dissolution in aqueous media, molecular structures present in sodium borosilicate glasses of composition Na2O.xB2O3.(3-x)SiO2, with x 1 (Na2O/B2O3 ratio 1), were analyzed using deep-UV Raman spectroscopy. The results were quantified in terms of the fraction of SiO4 tetrahedra with one non-bridging oxygen (Q3) and then correlated with Na2O and B2O3 content. Increasing Na2O was found to raise the fraction of Q3 units in the glasses systematically, in agreement with studies on related glasses, and, as long as the value of x was not too high, contribute to higher rates of dissolution in single pass flow-through testing. The finding was obtained across more than one series of silica-rich glasses prepared for independent dissolution studies. In contrast, dissolution rates were less strongly determined by the Q3 fraction when the value of x was near unity and appeared to grow larger upon further reduction of the Q3 fraction. The results were interpreted to indicate the increasingly important role of network hydrolysis in the glass dissolution mechanism as the BO4 tetrahedron replaces the Q3 unit as the charge-compensating structure for Na+ ions. Finally, the use of deep-UV Raman spectroscopy was found to be advantageous in studying finely powdered glasses in cases where visible Raman spectroscopy suffered from weak Raman scattering and fluorescence interference.

What Is Crystalline Silica?

Science.gov (United States)

... and ceramic manufacturing and the tool and die, steel and foundry industries. Crystalline silica is used in manufacturing, household abrasives, adhesives, paints, soaps, and glass. Additionally, ...

Surface chemistry and durability of borosilicate glass

International Nuclear Information System (INIS)

Carroll, S.A.; Bourcier, W.L.; Phillips, B.L.

1994-01-01

Important glass-water interactions are poorly understood for borosilicate glass radioactive waste forms. Preliminary results show that glass durability is dependent on reactions occurring at the glass-solution interface. CSG glass (18.2 wt. % Na 2 O, 5.97 wt. % CaO, 11.68 wt. % Al 2 O 3 , 8.43 wt. % B 2 O 3 , and 55.73 wt. % SiO 2 ) dissolution and net surface H + and OH - adsorption are minimal at near neutral pH. In the acid and alkaline pH regions, CSG glass dissolution rates are proportional to [H + ] adsorbed 2 and [OH - ] adsorbed 0.8 , respectively. In contrast, silica gel dissolution and net H + and OH - adsorption are minimal and independent of pH in acid to neutral solutions. In the alkaline pH region, silica gel dissolution is proportional to [OH - ] adsorbed 0.9 adsorbed . Although Na adsorption is significant for CSG glass and silica gel in the alkaline pH regions, it is not clear if it enhances dissolution, or is an artifact of depolymerization of the framework bonds

water alteration processes and kinetics of basaltic glasses, natural analogue of nuclear glasses

International Nuclear Information System (INIS)

Techer, I.; Advocat, Th.; Vernaz, E.; Lancelot, J.R.; Liotard, J.M.

1997-01-01

Dissolution experiments of a basaltic glass were carried out at 90 deg C for different reaction progresses. The initial dissolution rate was compared with values obtained for rhyolitic glass and the R7T7 nuclear glass. The activation energy was also determined by computing literature data. The results provide similar reactional mechanism for basaltic and nuclear glasses. Dissolution rates measured under saturation conditions were compared to theoretical dissolution rates. These ones were calculated using two kinetic models: the first rate equation is the Grambow's law which only takes into account ortho-silica acid activity; the second rate equation was proposed by Daux et al., where silica and aluminum are combined to formulate the affinity. The comparison between experimental and theoretical results point out that these two models are not appropriate to describe the alteration kinetic of basaltic glasses. (authors)

Influence of phosphate glass recrystallization on the stability of a waste matrix to leaching

Science.gov (United States)

Yudintsev, S. V.; Pervukhina, A. M.; Mokhov, A. V.; Malkovsky, V. I.; Stefanovsky, S. V.

2017-04-01

In Russia, highly radioactive liquid wastes from recycling of spent fuel of nuclear reactors are solidified into Na-Al-P glass for underground storage. The properties of the matrix including the radionuclide fixation will change with time due to crystallization. This is supported by the results of study of the interaction between glassy matrices, products of their crystallization, and water. The concentration of Cs in a solution at the contact of a recrystallized sample increased by three orders of magnitude in comparison with an experiment with glass. This difference is nearly one order of magnitude for Sr, Ce, and Nd (simulators of actinides) and U due to their incorporation into phases with low solubility in water. Based on data on the compositional change of solutions after passing through filters of various diameters, it is concluded that Cs occurs in the dissolved state in runs with a glass and recrystallized matrix. At the same time, Sr, lanthanides, and U occur in the dissolved state and in the composition of colloids in runs with glass, and mostly in colloid particles after contact with the recrystallized sample. These results should be regarded for substantiation of safety for geological waste storage.

Mechanical characterization of SiC particulate & E-glass fiber reinforced Al 3003 hybrid metal matrix composites

Science.gov (United States)

Narayana, K. S. Lakshmi; Shivanand, H. K.

2018-04-01

Metal matrix composites constitute a class of low cost high quality materials which offer high performance for various industrial applications. The orientation of this research is towards the study of mechanical properties of as cast silicon carbide (SiC) particulates and Short E-Glass fibers reinforced Aluminum matrix composites (AMCs). The Hybrid metal matrix composite is developed by reinforcing SiC particulates of 100 microns and short E-Glass fibers of 2-3 mm length with Al 3003 in different compositions. The vortex method of stir casting was employed, in which the reinforcements were introduced into the vortex created by the molten metal by means of mechanical stirrer. The mechanical properties of the prepared metal matrix composites were analyzed. From the studies it was noticed that an improvement in mechanical properties of the reinforced alloys compared to unreinforced alloys.

Sol-gel approach to the novel organic-inorganic hybrid composite films with ternary europium complex covalently bonded with silica matrix

International Nuclear Information System (INIS)

Dong Dewen; Yang Yongsheng; Jiang Bingzheng

2006-01-01

Novel organic-inorganic hybrid composite films with ternary lanthanide complex covalently bonded with silica matrix were prepared in situ via co-ordination of N-(3-propyltriethoxysilane)-4-carboxyphthalimide (TAT) and 1,10-phenanthroline (Phen) with europium ion (Eu 3+ ) during a sol-gel approach and characterized by the means of spectrofluorimeter, phosphorimeter and infrared spectrophotometer (FTIR). The resulting transparent films showed improved photophysical properties, i.e. increased luminescence intensity and longer luminescence lifetime, compared with the corresponding binary composite films without Phen. All the results revealed that the intense luminescence of the composite film was attributed to the efficient energy transfer from ligands, especially Phen, to chelated Eu 3+ and the reduced non-radiation through the rigid silica matrix and 'site isolation'

In-situ ductile metal/bulk metallic glass matrix composites formed by chemical partitioning

Science.gov (United States)

Kim, Choong Paul; Hays, Charles C.; Johnson, William L.

2004-03-23

A composite metal object comprises ductile crystalline metal particles in an amorphous metal matrix. An alloy is heated above its liquidus temperature. Upon cooling from the high temperature melt, the alloy chemically partitions, forming dendrites in the melt. Upon cooling the remaining liquid below the glass transition temperature it freezes to the amorphous state, producing a two-phase microstructure containing crystalline particles in an amorphous metal matrix. The ductile metal particles have a size in the range of from 0.1 to 15 micrometers and spacing in the range of from 0.1 to 20 micrometers. Preferably, the particle size is in the range of from 0.5 to 8 micrometers and spacing is in the range of from 1 to 10 micrometers. The volume proportion of particles is in the range of from 5 to 50% and preferably 15 to 35%. Differential cooling can produce oriented dendrites of ductile metal phase in an amorphous matrix. Examples are given in the Zr--Ti--Cu--Ni--Be alloy bulk glass forming system with added niobium.

Effects of β-irradiation in multicomponent glasses simulating the matrix of the French nuclear waste glass (R7T7)

International Nuclear Information System (INIS)

Boizot, B.; Ghaleb, D.; Petite, G.

2001-01-01

4-, 5- and 6-oxide components alumino-borosilicate glasses, with compositions closed to the matrix of the french nuclear glass 'R7T7' have been irradiated with electrons (β) at 2.5 MeV with a Van de Graff accelerator. These glasses have been studied after irradiation with different spectroscopic methods: Electron Paramagnetic Resonance for the study of defects, Raman Micro-spectroscopy for the study of amorphous network evolution under irradiation, and by 11 B MAS NMR. The results of these studies are presented here. It shows in particular a great sensibility to the irradiation conditions like dose rate and irradiation temperature, who are therefore important parameters for the representativeness of such experiments. (authors)

Fabrication and characterization of strontium incorporated 3-D bioactive glass scaffolds for bone tissue from biosilica

Energy Technology Data Exchange (ETDEWEB)

Özarslan, Ali Can, E-mail: alicanozarslan@gmail.com; Yücel, Sevil, E-mail: syucel@yildiz.edu.tr

2016-11-01

Bioactive glass scaffolds that contain silica are high viable biomaterials as bone supporters for bone tissue engineering due to their bioactive behaviour in simulated body fluid (SBF). In the human body, these materials help inorganic bone structure formation due to a combination of the particular ratio of elements such as silicon (Si), calcium (Ca), sodium (Na) and phosphorus (P), and the doping of strontium (Sr) into the scaffold structure increases their bioactive behaviour. In this study, bioactive glass scaffolds were produced by using rice hull ash (RHA) silica and commercial silica based bioactive glasses. The structural properties of scaffolds such as pore size, porosity and also the bioactive behaviour were investigated. The results showed that undoped and Sr-doped RHA silica-based bioactive glass scaffolds have better bioactivity than that of commercial silica based bioactive glass scaffolds. Moreover, undoped and Sr-doped RHA silica-based bioactive glass scaffolds will be able to be used instead of undoped and Sr-doped commercial silica based bioactive glass scaffolds for bone regeneration applications. Scaffolds that are produced from undoped or Sr-doped RHA silica have high potential to form new bone for bone defects in tissue engineering. - Highlights: • Production of 3-D bioactive glass scaffolds from different silica sources • The effect of biosilica from rice hull ash on the bioactive glass scaffold • Sr additive impact on the bioactivity and biodegradability properties of scaffolds.

Cordierite Glass-Ceramics for Dielectric Materials

International Nuclear Information System (INIS)

Siti Mazatul Azwa Saiyed Mohd Nurddin; Selamat, Malek; Ismail, Abdullah

2007-01-01

The objective of this project is to examine the potential of using Malaysian silica sand deposit as SiO2 raw material in producing cordierite glass-ceramics (2MgO-2Al2O3-5SiO2) for dielectric materials. Upgraded silica sands from Terengganu and ex-mining land in Perak were used in the test-works. The glass batch of the present work has a composition of 45.00% SiO2, 24.00% Al2O3, 15.00% MgO and 8.50% TiO2 as nucleation agent. From the differential thermal analysis results, the crystallization temperature was found to start around 900 deg. C. The glass samples were heat-treated at 900 deg. C and 1000 deg. C. The X-ray diffraction analysis (XRD) results showed glass-ceramics from Terengganu samples containing mainly cordierite and minor β-quartz crystals. However, glass-ceramics from ex-mining land samples contained mainly α-quartz and minor cordierite crystals. Glass-ceramics with different crystal phases exhibit different mechanical, dielectric and thermal properties. Based on the test works, both silica sand deposits, can be potentially used to produce dielectric material component

Stress relaxation in tempered glass caused by heat soak testing

DEFF Research Database (Denmark)

Schneider, Jens; Hilcken, Jonas; Aronen, Antti

2016-01-01

Heat soak testing of tempered glass is a thermal process required after the tempering process itself to bring glasses of commercial soda-lime-silica-glass to failure that are contaminated with nickel sulphide inclusions, diameter 50 mm to 500 mm typically. Thus, the tests avoid a so-called "spont...... of commercial soda-lime-silica glass, it causes stress relaxation in tempered glass and the fracture pattern of the glass changes accordingly, especially thin glasses are affected. Based on the Tool-Narayanaswamy-Model, this paper comprises the theoretical background of the stress...

Shielding of electromagnetic fields by metallic glasses with Fe and Co matrix

International Nuclear Information System (INIS)

Nowosielski, R.; Griner, S.

1997-01-01

The influence of chemical composition and magnetic and electric properties for shielding of electromagnetic fields with frequency 10-1000 kHz, by metallic glasses has been analysed. For investigation were selected two groups of metallic glasses with matrix of Fe and Co. Particularly, in there were selected metallic glasses as follows; Fe 78 Si 9 B 13 , Co 68 Fe 4 Mo 1.5 Si 13.5 B 13 , Co 69 Mo 2 Fe 4 Si 14 B 11 , Co 70.5 Fe 2.5 Mn 4 Mo 1 Si 9 B 15 . The experiments were realised for casting metallic glasses by the CMBS method in the form of strips with width 10 mm. Obtained results of shielding indicate clear for very good shielding effectiveness of one layer shields both electric and magnetic components of electromagnetic fields, although shielding of magnetic component is smaller than electric. (author). 17 refs, 5 figs, 9 tabs

Visible-light-induced hydrogen production over Pt-Eosin Y catalysts with high surface area silica gel as matrix

Energy Technology Data Exchange (ETDEWEB)

Zhang, Xiaojie [State Key Laboratory for Oxo Synthesis and Selective Oxidation, Lanzhou Institute of Chemical Physics, The Chinese Academy of Sciences, Lanzhou 730000 (China); Graduate University of the Chinese Academy of Sciences, Beijing 100101 (China); Jin, Zhiliang; Li, Shuben; Lu, Gongxuan [State Key Laboratory for Oxo Synthesis and Selective Oxidation, Lanzhou Institute of Chemical Physics, The Chinese Academy of Sciences, Lanzhou 730000 (China); Li, Yuexiang [Department of Chemistry, Nanchang University, Nanjing Road 245, Nanchang, 330047 (China)

2007-03-30

A new system for the production of hydrogen, constructed using silica gel as a matrix, Eosin Y as a photosensitizer, and Pt as a cocatalyst, has been reported. It was found that the rate of photosensitized hydrogen evolution in the presence of silica gel is enhanced about 10-fold relative to the homogeneous phase, i.e. in the absence of silica gel. The pH value of the solution and the concentration of Eosin Y have remarkable effects on the rate of hydrogen evolution. The optimal pH and concentration of Eosin Y are 7 and 3.60 x 10{sup -4} mol dm{sup -3} (E/S = 1/3) to 7.24 x 10{sup -4} mol dm{sup -3} (E/S = 1/1), respectively. Triethanolamine (TEOA) as an electron donor, the rate of hydrogen evolution and the apparent quantum efficiency in the silica gel system under visible-light irradiation ({lambda} {>=} 420 nm) can reach about 43 {mu}mol h{sup -1} and 10.4%, respectively. In addition, the roles of silica gel, Pt and TEOA, respectively; and the probable mechanism of photosensitized hydrogen evolution have been discussed. (author)

Visible-light-induced hydrogen production over Pt-Eosin Y catalysts with high surface area silica gel as matrix

Science.gov (United States)

Zhang, Xiaojie; Jin, Zhiliang; Li, Yuexiang; Li, Shuben; Lu, Gongxuan

A new system for the production of hydrogen, constructed using silica gel as a matrix, Eosin Y as a photosensitizer, and Pt as a cocatalyst, has been reported. It was found that the rate of photosensitized hydrogen evolution in the presence of silica gel is enhanced about 10-fold relative to the homogeneous phase, i.e. in the absence of silica gel. The pH value of the solution and the concentration of Eosin Y have remarkable effects on the rate of hydrogen evolution. The optimal pH and concentration of Eosin Y are 7 and 3.60 × 10 -4 mol dm -3 (E/S = 1/3) to 7.24 × 10 -4 mol dm -3 (E/S = 1/1), respectively. Triethanolamine (TEOA) as an electron donor, the rate of hydrogen evolution and the apparent quantum efficiency in the silica gel system under visible-light irradiation (λ ≥ 420 nm) can reach about 43 μmol h -1 and 10.4%, respectively. In addition, the roles of silica gel, Pt and TEOA, respectively; and the probable mechanism of photosensitized hydrogen evolution have been discussed.

IRON REDOX EQUILIBRIUM AND DIFFUSIVITY IN MIXED ALKALI-ALKALINE EARTH-SILICA GLASS MELTS

Directory of Open Access Journals (Sweden)

KI-DONG KIM

2011-03-01

Full Text Available Dependence of redox behavior and diffusivity of iron on temperature and composition was studied in mixed alkali-alkaline earth-silica glass melts by means of square wave voltammetry (SWV. The voltammograms showed that irrespective of K2O/(Na2O+K2O the peak potential due to Fe3+/Fe2+ moved toward negative direction with temperature decrease and the peak current showed a strong dependence on frequency at constant temperature. Iron diffusion coefficient versus melt viscosity showed a good linearity. The compositional dependence showed that the peak potential shifted to the positive direction with increase of K2O but a typical mixed alkali effect occurred in iron diffusion either at constant temperature or at constant viscosity.

Kinetic and thermodynamic controls on silica reactivity: an analog for waste disposal media

International Nuclear Information System (INIS)

Dove, P.M.; Icenhower, J.

1997-01-01

Silicate glasses are currently being proposed as the disposal media for radioactive and other toxic wastes. The dissolution behaviour of borosilicate glass is incompletely understood. One approach is to simplify the chemistry and first develop a better understanding of vitreous silica (v-SiO 2 ) as a simple analog of waste glass. This article reviews all the knowledge that is known about the dissolution of silica. Studies quantifying the effects of temperature, solution pH, and single salts on dissolution rates of quartz suggest that pH and cation-dependent dissolution trends hold for all of the silica polymorphs. The purpose of this review is to develop a consistent picture of glass reactivity by understanding how the molecular arrangement of constituents within glass, beginning with the Si-O bond, affects the dissolution processes. (A.C.)

Investigation of Electrochemical and Morphological Properties of Mixed Matrix Polysulfone-Silica Anion Exchange Membrane

Directory of Open Access Journals (Sweden)

Khoiruddin

2016-02-01

Full Text Available Mixed matrix anion exchange membranes (AEMs were synthesized using dry-wet phase inversion. The casting solutions were prepared by dispersing finely ground anion-exchange resin particles in N,N-dimethylacetamide (DMAc solutions of polysulfone (PSf. Subsequently, nanosilica particles were introduced into the membranes. The results show that evaporation time (tev and solution composition contributed to membrane properties formation. A longer tev produces membranes with reduced void fraction inside the membranes, thus the amount of water adsorbed and membrane conductivity are reduced. Meanwhile, the permselectivity was improved by increasing tev, since a longer tev produces membranes with a narrower channel for ion migration and more effective Donnan exclusion. The incorporation of 0.5 %-wt nanosilica particles into the polymer matrix led to conductivity improvement (from 2.27 to 3.41 mS.cm-1. This may be associated with additional pathway formation by hydroxyl groups on the silica surface that entraps water and assists ion migration. However, at further silica loading (1.0 and 1.5 %-wt, these properties decreased (to 1.9 and 1.4 mS.cm-1 respectively, which attributed to inaccessibility of ion-exchange functional groups due to membrane compactness. It was found from the results that nanosilica contributes to membrane formation (increases casting solution viscosity then reduces void fraction and membrane functional group addition (provides hydroxyl groups.

Study of the focusing effect of silica microspheres on the upconversion of Er3+–Yb3+ codoped glass ceramics

International Nuclear Information System (INIS)

Pérez-Rodríguez, C.; Imanieh, M.H.; Martín, L.L; Ríos, S.; Martín, I.R.; Yekta, Bijan Eftekhari

2013-01-01

Highlights: •Silica microspheres have been located on the surface of glass and glass ceramics samples codoped with Er and Yb. •Microspheres act as microlens of the 950 nm excitation light resulting in focalized excited regions in the samples with sizes under the micron. •Intense red upconversion is achieved in the focalized areas. •Microspheres collect the upconversion emission light, scoping with the together microlensing properties an enhancement of the detected signal in a 3x factor. •Performed Finite-Difference Time-Domain simulations predict the size of the focalized regions in good agreement with the experimental measurements. -- Abstract: The upconversion emission properties of Er 3+ –Yb 3+ codoped glass and glass ceramic samples with different Si/Al ratios and thermal treatments were analyzed by covering their surfaces with silica microspheres (3.8 μm diameter). A 950 nm laser beam is focused by the microspheres producing a set of photonic nanojets near the surface of the samples. After the upconversion processes of the Er 3+ ions located in each microsphere focus area, these ions emit light in the green and red regions. The red emission from each sample was measured, yielding an upconversion intensity in the focal areas three times higher than the emission from the bare substrate. To estimate the real size of the red emission area under a single microsphere, a deconvolution of the measured focal spots with the Point Spread Function of the experimental setup was performed, resulting in a Full Width at Half Maximum of 330 nm. The results obtained by Finite-Difference Time-Domain simulations are in good agreement with the experimental values

Study on Effect of Ultrasonic Vibration on Grinding Force and Surface Quality in Ultrasonic Assisted Micro End Grinding of Silica Glass

Directory of Open Access Journals (Sweden)

Zhang Jianhua

2014-01-01

Full Text Available Ultrasonic vibration assisted micro end grinding (UAMEG is a promising processing method for micro parts made of hard and brittle materials. First, the influence of ultrasonic assistance on the mechanism of this processing technology is theoretically analyzed. Then, in order to reveal the effects of ultrasonic vibration and grinding parameters on grinding forces and surface quality, contrast grinding tests of silica glass with and without ultrasonic assistance using micro radial electroplated diamond wheel are conducted. The grinding forces are measured using a three-component dynamometer. The surface characteristics are detected using the scanning electron microscope. The experiment results demonstrate that grinding forces are significantly reduced by introducing ultrasonic vibration into conventional micro end grinding (CMEG of silica glass; ultrasonic assistance causes inhibiting effect on variation percentages of tangential grinding force with grinding parameters; ductile machining is easier to be achieved and surface quality is obviously improved due to ultrasonic assistance in UAMEG. Therefore, larger grinding depth and feed rate adopted in UAMEG can lead to the improvement of removal rate and machining efficiency compared with CMEG.

Melt flow and mechanical properties of silica/perfluoropolymer nanocomposites Fabricated by direct melt-compounding without surface modification on nano-silica.

Science.gov (United States)

Tanahashi, Mitsuru; Watanabe, Yusuke; Lee, Jeong-Chang; Takeda, Kunihiko; Fujisawa, Toshiharu

2009-01-01

The authors have previously developed a novel method for the fabrication of silica/perfluoropolymer nanocomposites, wherein nano-sized silica particles without surface modification were dispersed uniformly through breakdown of loosely packed agglomerates of silica nanoparticles with low fracture strength in a polymer melt during direct melt-compounding. The method consists of two stages; the first stage involves preparation of the loose silica agglomerate, and the second stage involves melt-compounding of a completely hydrophobic perfluoropolymer, PFA (poly(tetrafluoroethylene-co-perfluoropropylvinylether)), with the loose silica agglomerates. By using this simple method without any lipophilic treatment of the silica surfaces, silica nanoparticles with a primary diameter of 190 nm could be dispersed uniformly into the PFA matrix. The main purpose of the present study is to evaluate the melt flow and tensile properties of silica/PFA nanocomposites fabricated by the above method. In order to elucidate the effects of the size of the dispersed silica in the PFA matrix on the properties of the composites, silica/PFA composite samples exhibiting the dispersion of larger-sized silica particle-clusters were fabricated as negative controls of the silica dispersion state. The results obtained under the present experimental conditions showed that the size of the dispersed silica in the PFA matrix exerts a strong influence on the ultimate tensile properties, such as tensile strength and elongation at break, and the melt flow rate (MFR) of the composite materials. The MFR of the silica/PFA nanocomposite became higher than that of the pure PFA without silica addition, although the MFR of the PFA composites containing larger silica particle-clusters became much lower than that of the pure PFA. Furthermore, uniform dispersion of isolated silica nanoparticles was found to improve not only the Young's modulus but also the ultimate tensile properties of the composite.

Effect of silver ions on the energy transfer from host defects to Tb ions in sol–gel silica glass

Energy Technology Data Exchange (ETDEWEB)

Abbass, Abd Ellateef [Department of Physics, University of the Free State, Bloemfontein (South Africa); Department of Physics, Sudan University of Science and Technology (Sudan); Swart, H.C. [Department of Physics, University of the Free State, Bloemfontein (South Africa); Kroon, R.E., E-mail: KroonRE@ufs.ac.za [Department of Physics, University of the Free State, Bloemfontein (South Africa)

2015-04-15

Plasmonic metal structures have been suggested to enhance the luminescence from rare-earth (RE) ions, but this enhancement is not yet well understood or applied to phosphor materials. Although some reports using Ag nanoparticles (NPs) in glass have attributed enhancement of RE emission to the strong electric fields associated with Ag NPs, it has also been proposed that the enhancement is instead due to energy transfer from Ag ions to RE ions. Our work using sol–gel silica shows a third possibility, namely that enhancement of the RE (e.g. Tb) emission is due to energy transfer from defects of the host material to the Tb ions, where the addition of Ag influences the silica host defects. The oxidation state of Ag as a function of annealing temperature was investigated by x-ray diffraction, transmission electron microscopy, UV–vis measurements and x-ray photoelectron spectroscopy, while optical properties were investigated using a Cary Eclipse fluorescence spectrophotometer or by exciting samples with a 325 nm He–Cd laser. The results showed that Ag ions have a significant effect on the silica host defects, which resulted in enhancement of the green Tb emission at 544 nm for non-resonant excitation using a wavelength of 325 nm. - Highlights: • Conversion of Ag ions to metallic nanoparticles after annealing of sol–gel silica. • Addition of Ag resulted in enhanced green luminescence from Tb ions in silica. • Enhancement is attributed to the effect of added Ag on the host defects of silica.

Characterisation of glass matrix composites reinforced with lead zirconate titanate particles

International Nuclear Information System (INIS)

Cannillo, Valeria; Manfredini, Tiziano; Montorsi, Monia; Tavoni, Francesca; Minay, Emma J.; Boccaccini, Aldo R.

2005-01-01

A new type of glass matrix composite reinforced with ferroelectric particulate secondary phase was investigated. Samples containing lead zirconate titanate (PZT) particles in a silicate lead glass were fabricated. Various sintering strategies were tested in order to optimise the processing route. The densest samples were obtained by hot-pressing. The composites were characterized by means of SEM observations, X-ray diffraction, differential thermal analysis and Vickers indentations. In order to get a deeper insight into the thermo-mechanical behaviour of the material, a FEM based numerical model was prepared and applied. In particular, the crack-particle interaction was assessed and thus possible toughening mechanisms were investigated. By means of the numerical modelling supported by SEM observations, traditional toughening mechanisms (e.g. crack deflection, particle debonding) were ruled out. Since the experimentally measured indentation fracture toughness of the composite is significantly higher than that of the unreinforced glass, the findings suggest that a new toughening mechanism may be active, based on the piezoelectric effect

Crystalline Silica Primer

Science.gov (United States)

,

1992-01-01

Crystalline silica is the scientific name for a group of minerals composed of silicon and oxygen. The term crystalline refers to the fact that the oxygen and silicon atoms are arranged in a threedimensional repeating pattern. This group of minerals has shaped human history since the beginning of civilization. From the sand used for making glass to the piezoelectric quartz crystals used in advanced communication systems, crystalline silica has been a part of our technological development. Crystalline silica's pervasiveness in our technology is matched only by its abundance in nature. It's found in samples from every geologic era and from every location around the globe. Scientists have known for decades that prolonged and excessive exposure to crystalline silica dust in mining environments can cause silicosis, a noncancerous lung disease. During the 1980's, studies were conducted that suggested that crystalline silica also was a carcinogen. As a result of these findings, crystalline silica has been regulated under the Occupational Safety and Health Administration's (OSHA) Hazard Communication Standard (HCS). Under HCS, OSHAregulated businesses that use materials containing 0.1% or more crystalline silica must follow Federal guidelines concerning hazard communication and worker training. Although the HCS does not require that samples be analyzed for crystalline silica, mineral suppliers or OSHAregulated

Utilization of recycled glass derived from cathode ray tube glass as fine aggregate in cement mortar

International Nuclear Information System (INIS)

Ling, Tung-Chai; Poon, Chi-Sun

2011-01-01

Graphical abstract: Display Omitted Highlights: → A recycling/treatment process to remove lead on funnel glass surface is described. → Utilizing recycled funnel glass in mortar can reduce hazardous CRT glass wastes. → Effects of CRT glass content on the properties of cement mortar are studied. → Fly ash can effectively mitigate ASR expansion of mortar even at 100% glass content. → Alkaline medium in cement matrix successfully prevented the leaching of lead. - Abstract: Rapid advances in the electronic industry led to an excessive amount of early disposal of older electronic devices such as computer monitors and old televisions (TV) before the end of their useful life. The management of cathode ray tubes (CRT), which have been a key component in computer monitors and TV sets, has become a major environmental problem worldwide. Therefore, there is a pressing need to develop sustainable alternative methods to manage hazardous CRT glass waste. This study assesses the feasibility of utilizing CRT glass as a substitute for natural aggregates in cement mortar. The CRT glass investigated was an acid-washed funnel glass of dismantled CRT from computer monitors and old TV sets. The mechanical properties of mortar mixes containing 0%, 25%, 50%, 75% and 100% of CRT glass were investigated. The potential of the alkali-silica reaction (ASR) and leachability of lead were also evaluated. The results confirmed that the properties of the mortar mixes prepared with CRT glass was similar to that of the control mortar using sand as fine aggregate, and displayed innocuous behaviour in the ASR expansion test. Incorporating CRT glass in cement mortar successfully prevented the leaching of lead. We conclude that it is feasible to utilize CRT glass in cement mortar production.

Influence of thermal cycling on flexural properties of composites reinforced with unidirectional silica-glass fibers.

Science.gov (United States)

Meriç, Gökçe; Ruyter, I Eystein

2008-08-01

The purpose was to investigate the effect of water storage and thermal cycling on the flexural properties of differently sized unidirectional fiber-reinforced composites (FRCs) containing different quantities of fibers. The effect of fiber orientation on the thermal expansion of FRCs as well as how the stresses in the composites can be affected was considered. An experimental polymeric base material was reinforced with silica-glass fibers. The cleaned and silanized fibers were sized with either linear PBMA-size or crosslinked PMMA-size. For the determination of flexural properties and water uptake, specimens were processed with various quantities of differently sized unidirectional fibers. Water uptake of FRC was measured. Water immersed specimens were thermally cycled for 500 and 12,000 cycles (5 degrees C/55 degrees C). Flexural properties of "dry" and wet specimens with and without thermal cycling were determined by a three-point bending test. The linear coefficients of thermal expansion (LCTE) for FRC samples with different fiber orientations were determined using a thermomechanical analyzer. Water uptake of the FRC specimens increased with a decrease in fiber content of the FRC. Flexural properties of FRCs improved with increasing fiber content, whereas the flexural properties were not influenced significantly by water and thermal cycling. Fiber orientation had different effects on LCTE of FRCs. Unidirectional FRCs had two different LCTE in longitudinal and transverse directions whereas bidirectional FRCs had similar LCTE in two directions and a higher one in the third direction. The results of the study suggest that the surface-treated unidirectional silica-glass FRC can be used for long-term clinical applications in the oral cavity.

Silica Nephropathy

Directory of Open Access Journals (Sweden)

N Ghahramani

2010-06-01

Full Text Available Occupational exposure to heavy metals, organic solvents and silica is associated with a variety of renal manifestations. Improved understanding of occupational renal disease provides insight into environmental renal disease, improving knowledge of disease pathogenesis. Silica (SiO2 is an abundant mineral found in sand, rock, and soil. Workers exposed to silica include sandblasters, miners, quarry workers, masons, ceramic workers and glass manufacturers. New cases of silicosis per year have been estimated in the US to be 3600–7300. Exposure to silica has been associated with tubulointerstitial disease, immune-mediated multisystem disease, chronic kidney disease and end-stage renal disease. A rare syndrome of painful, nodular skin lesions has been described in dialysis patients with excessive levels of silicon. Balkan endemic nephropathy is postulated to be due to chronic intoxication with drinking water polluted by silicates released during soil erosion. The mechanism of silica nephrotoxicity is thought to be through direct nephrotoxicity, as well as silica-induced autoimmune diseases such as scleroderma and systemic lupus erythematosus. The renal histopathology varies from focal to crescentic and necrotizing glomerulonephritis with aneurysm formation suggestive of polyarteritis nodosa. The treatment for silica nephrotoxicity is non-specific and depends on the mechanism and stage of the disease. It is quite clear that further research is needed, particularly to elucidate the pathogenesis of silica nephropathy. Considering the importance of diagnosing exposure-related renal disease at early stages, it is imperative to obtain a thorough occupational history in all patients with renal disease, with particular emphasis on exposure to silica, heavy metals, and solvents.

Kinetic and thermodynamic controls on silica reactivity: an analog for waste disposal media

Energy Technology Data Exchange (ETDEWEB)

Dove, P.M.; Icenhower, J. [Georgia Inst. of Tech., School of Earth and Atmospheric Sciences, Atlanta, GA (United States)

1997-07-01

Silicate glasses are currently being proposed as the disposal media for radioactive and other toxic wastes. The dissolution behaviour of borosilicate glass is incompletely understood. One approach is to simplify the chemistry and first develop a better understanding of vitreous silica (v-SiO{sub 2}) as a simple analog of waste glass. This article reviews all the knowledge that is known about the dissolution of silica. Studies quantifying the effects of temperature, solution pH, and single salts on dissolution rates of quartz suggest that pH and cation-dependent dissolution trends hold for all of the silica polymorphs. The purpose of this review is to develop a consistent picture of glass reactivity by understanding how the molecular arrangement of constituents within glass, beginning with the Si-O bond, affects the dissolution processes. (A.C.)

Effect of fiber content on the properties of glass fiber-phenolic matrix composite

International Nuclear Information System (INIS)

Zaki, M.Y.; Shahid, M.R.; Subhani, T.; Sharif, M.N.

2003-01-01

Glass fiber-Phenolic matrix composite is used for the manufacturing of parts /components related to electronic and aerospace industry due to its high strength, dimensional stability and excellent electrical insulation properties. The evaluation of this composite material is necessary prior to make parts/components of new designs. In the present research, thermosetting phenolic plastic was reinforced with E-glass fiber in different fiber-to-resin ratios to produce composites of different compositions. Mechanical and electrical properties of these composite materials were evaluated with reference to the effect of fiber content variation in phenolic resin. (author)

Laser oxidative pyrolysis synthesis and annealing of TiO{sub 2} nanoparticles embedded in carbon–silica shells/matrix

Energy Technology Data Exchange (ETDEWEB)

Fleaca, C.T. [National Institute for Plasma, Laser and Radiation Physics (NILPRP), Atomistilor 409, P.O. Box MG 36, R-077125 Magurele, Bucharest (Romania); “Politehnica” University of Bucharest, Physics Department, Independentei 313, Bucharest (Romania); Scarisoreanu, M., E-mail: monica.scarisoreanu@inflpr.ro [National Institute for Plasma, Laser and Radiation Physics (NILPRP), Atomistilor 409, P.O. Box MG 36, R-077125 Magurele, Bucharest (Romania); Morjan, I.; Luculescu, C.; Niculescu, A.-M.; Badoi, A. [National Institute for Plasma, Laser and Radiation Physics (NILPRP), Atomistilor 409, P.O. Box MG 36, R-077125 Magurele, Bucharest (Romania); Vasile, E. [“Politehnica” University of Bucharest, Faculty of Applied Chemistry and Materials Science, Department of Oxide Materials and Nanomaterials, Gh. Polizu 1-7, Bucharest (Romania); Kovacs, G. [“Babes-Boyai” University, Faculty of Chemistry and Chemical Engineering, Arany Janos 11, Cluj-Napoca (Romania)

2015-05-01

Highlights: • TiO{sub 2}-based nanocomposites were obtained by one-step laser oxidative pyrolysis. • Titania particles are surrounded by/embedded in carbon/silica shells/matrix. • They contain an anatase/rutile mixture with mean crystalline diameters up to 24 nm. • Their carbon content decreased with the increasing of introduced air coflow. • Their bandgap energy decreased due to the carbon incorporation. - Abstract: Titania nanoparticles containing a mixture of anatase and rutile phases (with mean crystalline sizes up to 24 nm) covered with/embedded in carbon/silica thin layers or matrix were obtained in a single step using laser oxidative pyrolysis. Titanium tetrachloride and hexamethyldisiloxane (HMDSO) vapors were separately introduced into the reaction zone – both together with the laser-absorbing agent (sensitizer) ethylene – which acts also as carbon source – and the oxidant (air) – through the inner and the concentric nozzle, respectively. By increasing the air flow through the annular nozzle, while keeping constant the TiC{sub 4}, inner air, HMDSO and C{sub 2}H{sub 4} flows, the atomic carbon concentration as well as the rutile to anatase ratio in the resulted nanopowders decrease. A much brighter and extended flame was observed for the experiment involving the greatest air flow. The Ti/Si atomic ratio in the resulted nanocomposites was higher than that from the introduced precursors (1.8), indicating a partial siloxane conversion to silica. The annealed powders (at 450 °C to further carbon content reducing) exhibit a lower bandgap energy than those of the reference sample without silica (and also lower than the commercial Degussa P25 nano-TiO{sub 2})

Modification of a Phenolic Resin with Epoxy- and Methacrylate-Functionalized Silica Sols to Improve the Ablation Resistance of Their Glass Fiber-Reinforced Composites

Directory of Open Access Journals (Sweden)

Yu Hu

2014-01-01

Full Text Available Functionalized silica sols were obtained by the hydrolytic condensation of (γ-methacryloxypropyltrimethoxysilane (MPMS, (γ-glycidyloxypropyltrimethoxysilane (GPMS and tetraethoxysilane (TEOS. Three different sols were obtained: MPS (derived from MPMS and TEOS, GPS-MPS (derived from GPMS, MPMS and TEOS, and GPSD (derived from GPMS, TEOS and diglycidyl ether of bisphenol A, DGEBA. These silica sols were mixed with a phenolic resin (PR. Ethylenediamine was used as a hardener for epoxy-functionalized sols and benzoyl peroxide was used as an initiator of the free-radical polymerization of methacrylate-functionalized silica sols. Glass fiber-reinforced composites were obtained from the neat PR and MPS-PR, GPS-MPS-PR and GPSD-PR. The resulting composites were evaluated as ablation resistant materials in an acetylene-oxygen flame. A large increase in the ablation resistance was observed when the PR was modified by the functionalized silica sols. The ablation resistance of the composites decreased as follows: GPSD-PR > MPS-PR > GPS-MPS-PR > PR.

Workability of glass reinforced concrete (GRC) with granite and silica sand aggregates

Science.gov (United States)

Moceikis, R.; Kičaitė, A.; Keturakis, E.

2017-10-01

Glass fiber reinforced concrete (GRC) opens the door for lightweight and complex shaped innovative construction, adding architectural value to buildings. With panel thickness down to 15 mm, considerable amount of total loads and materials per square meter of facade can be saved, if compared to conventionally used 80 mm thickness outer layer in insulated precast concrete wall elements. Even though GRC is used for over 50 years in such countries as Great Britain, USA and Japan, there are very few examples and little research done in Eastern Europe with this building material. European Commission propagates sustainable design as commitment to energy efficiency, environmental stewardship and conservation. For this reason, GRC plays important role in mowing toward these goals. In this paper, GRC premix recipes including fine granite and silica sands, reinforced with 13mm length alkali resistant glass fibers are investigated. Two CEM I 52,5R cements with different particle sizes were used and severe water dissociation noticed in one of concrete mixes. Cement particle size distribution determined with laser diffraction particle analyser Cilas 1090LD. To determine modulus of rupture (M.O.R.) and limit of proportionality (L.O.P), plates thickness 15 and 20 mm were produced and tested for flexural resistance according to 4-point bending scheme. Concrete workability tests were made according EN 1170-1.

Singlet and doublet states UV-vis spectrum and electronic properties of 3-methylchrysene and 4-methylchrysene in glass matrix.

Science.gov (United States)

Husain, Mudassir M; Tandon, H C; Varadwaj, Pradeep R

2008-03-01

The ultraviolet-visual spectrum of 3-methylchrysene, 4-methylchrysene and their radical cations formed by ultraviolet radiations, were measured in glass matrix at the room temperature. In the measured singlet state spectrum we were able to identify the alpha, p, beta, beta' (Clar's) or (1)L(b), (1)L(a)(1)B(b), (1)B(a) (Platt's notation) bands. The presence of alpha, beta or (1)L(b), (1)B(b) was confirmed by calculating their wavelength ratio lambda(alpha)/lambda(beta). Since matrix induces perturbation in the measured spectrum; it becomes necessary to take into account the perturbation while computing the spectrum. An effort has been made in this work to simulate the electronic spectrum in the same environment as is measured. This study presents the first calculated spectrum of these systems and their cations in glass matrix by semi empirical methods. To observe the magnitude of perturbation and hence to see the spectral shift in glass matrix, the spectrum was calculated in the free state as well. Spectral properties such as frontier orbitals gap, dipole moment, mean polarizabilities and its tensors were also computed both in glass matrix and free state using semiemperical method. The measured bands of 3-methylchrysene cation at wavelength 416.50 and 473.85 nm closely match with the available diffuse intersteallar bands (DIBs) at 417.55 and 472.64 nm, respectively. Also the observed 474.85 nm band of 4-methylchrysene cation matches the DIB at 476.00 nm.

Glass Furnace Project, October 1982-March 1983

International Nuclear Information System (INIS)

Armstrong, K.M.; Klingler, L.M.

1983-01-01

In the Glass Furnace Project currently under way at Mound, a treatment technology for low-level radioactive waste is being evaluated that will combine volume reduction and immobilization in one step. Initial work focused on demonstrating the ability of the furnace to efficiently incinerate nonradioactive, simulated power-plant waste and on determining the adequacy of immobilization in a soda-lime silica matrix. Further evaluation of the system will involve a demonstration of the combustion and containment of radioactive waste. In preparation for this next phase of the program, preliminary investigation and design work were conducted during the past six months. 5 figures, 1 table

Coating extracellular matrix proteins on a (3-aminopropyl)triethoxysilane-treated glass substrate for improved cell culture.

Science.gov (United States)

Masuda, Hiro-taka; Ishihara, Seiichiro; Harada, Ichiro; Mizutani, Takeomi; Ishikawa, Masayori; Kawabata, Kazushige; Haga, Hisashi

2014-01-01

We demonstrate that a (3-aminopropyl)triethoxysilane-treated glass surface is superior to an untreated glass surface for coating with extracellular matrix (ECM) proteins when used as a cell culture substrate to observe cell physiology and behavior. We found that MDCK cells cultured on untreated glass coated with ECM removed the coated ECM protein and secreted different ECM proteins. In contrast, the cells did not remove the coated ECM protein when seeded on (3-aminopropyl)triethoxysilane-treated (i.e., silanized) glass coated with ECM. Furthermore, the morphology and motility of cells grown on silanized glass differed from those grown on non-treated glass, even when both types of glass were initially coated with laminin. We also found that cells on silanized glass coated with laminin had higher motility than those on silanized glass coated with fibronectin. Based on our results, we suggest that silanized glass is a more suitable cell culture substrate than conventional non-treated glass when coated by ECM for observations of ECM effects on cell physiology.

Thiol-functionalized silica colloids, grains, and membranes for irreversible adsorption of metal(oxide) nanoparticles

NARCIS (Netherlands)

Claesson, E.M.; Philipse, A.P.

2007-01-01

Thiol-functionalization is described for silica surfaces from diverging origin, including commercial silica nanoparticles and St¨ober silica as well as silica structures provided by porous glasses and novel polymer-templated silica membranes. The functionalization allows in all cases for the

Application of the atomic absorption technical to available the concentration of silver ions incorporated in glass matrix by ionic exchange process

International Nuclear Information System (INIS)

Mendes, E.; Silva, K.F.; Teixeira, A.; Silva, L.; Paula, M.M.S.; Angioletto, E.; Riella, H.G.; Fiori, M. A.

2009-01-01

Ion specimens can be incorporated in glasses or natural clays by ionic exchange process with different concentrations dependent of matrix's type and of the ionic exchange parameters. In particular, the incorporation of silver ions presents high interest by its biocidal properties. A compound contending ion silver specimens presents bactericidal and fungicidal properties with effect proportional to ion concentration. This work presents results about application of the atomic absorption technical to determine the silver ion concentration incorporated in a glass matrix by ionic exchange process. The ionic exchange experiments were realized with different AgNO 3 concentration and constant temperature. After ionic exchange process, the glass samples were submitted to characterization by Energy Dispersive X-Ray Spectroscopy and Atomic Absorption Techniques. The comparative results between different techniques showed that atomic absorption technical is adequate to determine ion silver concentration incorporated in the glass matrix after ionic exchange process. (author)

Nanostructural Organization of Naturally Occurring Composites—Part I: Silica-Collagen-Based Biocomposites

Directory of Open Access Journals (Sweden)

Hermann Ehrlich

2008-01-01

Full Text Available Glass sponges, as examples of natural biocomposites, inspire investigations aiming at both a better understanding of biomineralization mechanisms and novel developments in the synthesis of nanostructured biomimetic materials. Different representatives of marine glass sponges of the class Hexactinellida (Porifera are remarkable because of their highly flexible basal anchoring spicules. Therefore, investigations of the biochemical compositions and the micro- and nanostructure of the spicules as examples of naturally structured biomaterials are of fundamental scientific relevance. Here we present a detailed study of the structural and biochemical properties of the basal spicules of the marine glass sponge Monorhaphis chuni. The results show unambiguously that in this glass sponge a fibrillar protein of collagenous nature is the template for the silica mineralization in all silica-containing structural layers of the spicule. The structural similarity and homology of collagens derived from M. chuni spicules to other sponge and vertebrate collagens have been confirmed by us using FTIR, amino acid analysis and mass spectrometric sequencing techniques. We suggest that nanomorphology of silica formed on proteinous structures could be determined as an example of biodirected epitaxial nanodistribution of amorphous silica phase on oriented fibrillar collagen templates. Finally, the present work includes a discussion relating to silica-collagen-based hybrid materials for practical applications as biomaterials.

Investigating the use of coupling agents to improve the interfacial properties between a resorbable phosphate glass and polylactic acid matrix.

Science.gov (United States)

Hasan, Muhammad Sami; Ahmed, Ifty; Parsons, Andrew J; Rudd, Chris D; Walker, Gavin S; Scotchford, Colin A

2013-09-01

Eight different chemicals were investigated as potential candidate coupling agents for phosphate glass fibre reinforced polylactic acid composites. Evidence of reaction of the coupling agents with phosphate glass and their effect on surface wettability and glass degradation were studied along with their principle role of improving the interface between glass reinforcement and polymer matrix. It was found that, with an optimal amount of coupling agent on the surface of the glass/polymer, interfacial shear strength improved by a factor of 5. Evidence of covalent bonding between agent and glass was found for three of the coupling agents investigated, namely: 3-aminopropyltriethoxysilane; etidronic acid and hexamethylene diisocyanate. These three coupling agents also improved the interfacial shear strength and increased the hydrophobicity of the glass surface. It is expected that this would provide an improvement in the macroscopic properties of full-scale composites fabricated from the same materials which may also help to retain these properties for the desired length of time by retarding the breakdown of the fibre/matrix interface within these composites.

Scanning Auger microscopy study of lanthanum partitioning in sphene-based glass-ceramics

International Nuclear Information System (INIS)

Hocking, W.H.; Hayward, P.J.; Watson, D.G.; Allen, G.C.

1984-01-01

Glass-ceramics are being investigated as possible hosts for the radioactive wastes that would result from recycling irradiated nuclear fuels. The partitioning of lanthanum in sphene-based glass-ceramics has been studied by scanning Auger electron microscopy for lanthanum concentrations from 0.2 to 2.0 mol.%. Sphene crystals (CaTiSiO 5 ) were located in the silica-rich glass matrix by recording digital Auger images of the calcium and titanium distributions. The sphene crystals were typically 0.5 to 5 μm in size and occupied approximately 40% of the total specimen volume. Auger spot analyses revealed that lanthanum was strongly partitioned into the sphene phase of phosphorus-free glass-ceramics; however, when a small amount of phosphorus was included in the glass-ceramic composition as a crystal nucleating agent, the lanthanum was concentrated in a third minor phase which also contained calcium, phosphorus and oxygen. Chemical shift effects in the Auger spectra of silicon, titanium and phosphorus showed evidence for electron-stimulated desorption of oxygen. (author)

Nanostructure and magnetic properties of CoNi-alloy-based nanoparticles dispersed in a silica matrix

International Nuclear Information System (INIS)

De Julian, C.; Sangregorio, C.; Mattei, G.; Battaglin, G.; Cattaruzza, E.; Gonella, F.; Lo Russo, S.; D'Orazio, F.; Lucari, F.; De, G.; Gatteschi, D.; Mazzoldi, P.

2001-01-01

A comparative study of the magnetic behavior of FCC alloy CoNi (1:1) nanoparticles, embedded in a silica matrix and prepared by the ion implantation and sol-gel techniques, is presented. The blocking temperature is related to the size distribution, and, at least for the ion-implanted samples, only an enhanced effective anisotropy explains the experimental results. The hysteretic behavior is explained in terms of the temperature dependence of the anisotropy and of the particle volume fraction that determines the dipolar interactions

Nanostructure and magnetic properties of CoNi-alloy-based nanoparticles dispersed in a silica matrix

Energy Technology Data Exchange (ETDEWEB)

De Julian, C. E-mail: dejulian@padova.infm.it; Sangregorio, C.; Mattei, G.; Battaglin, G.; Cattaruzza, E.; Gonella, F.; Lo Russo, S.; D' Orazio, F.; Lucari, F.; De, G.; Gatteschi, D.; Mazzoldi, P

2001-05-01

A comparative study of the magnetic behavior of FCC alloy CoNi (1:1) nanoparticles, embedded in a silica matrix and prepared by the ion implantation and sol-gel techniques, is presented. The blocking temperature is related to the size distribution, and, at least for the ion-implanted samples, only an enhanced effective anisotropy explains the experimental results. The hysteretic behavior is explained in terms of the temperature dependence of the anisotropy and of the particle volume fraction that determines the dipolar interactions.

Rare Earth-Activated Silica-Based Nanocomposites

Directory of Open Access Journals (Sweden)

C. Armellini

2007-01-01

Full Text Available Two different kinds of rare earth-activated glass-based nanocomposite photonic materials, which allow to tailor the spectroscopic properties of rare-earth ions: (i Er3+-activated SiO2-HfO2 waveguide glass ceramic, and (ii core-shell-like structures of Er3+-activated silica spheres obtained by a seed growth method, are presented.

Osseointegration properties of titanium dental implants modified with a nanostructured coating based on ordered porous silica and bioactive glass nanoparticles

Energy Technology Data Exchange (ETDEWEB)

Covarrubias, Cristian, E-mail: ccovarrubias@odontologia.uchile.cl [Laboratory of Nanobiomaterials, Institute for Research in Dental Sciences, Faculty of Dentistry, University of Chile, Santiago (Chile); Mattmann, Matías [Laboratory of Nanobiomaterials, Institute for Research in Dental Sciences, Faculty of Dentistry, University of Chile, Santiago (Chile); Von Marttens, Alfredo [Department of Prosthesis, Faculty of Dentistry, University of Chile, Santiago (Chile); Caviedes, Pablo; Arriagada, Cristián [Laboratory of Cell Therapy, ICBM, Faculty of Medicine, University of Chile (Chile); Valenzuela, Francisco [Laboratory of Nanobiomaterials, Institute for Research in Dental Sciences, Faculty of Dentistry, University of Chile, Santiago (Chile); Rodríguez, Juan Pablo [Laboratory of Cell Biology, INTA, University of Chile, Santiago (Chile); Corral, Camila [Department of Restorative Dentistry, Faculty of Dentistry, University of Chile, Santiago (Chile)

2016-02-15

Graphical abstract: - Highlights: • The fabrication of a coating for osseointegration of titanium implant is presented. • The coating consists of nanoporous silica loaded with bioactive glass nanoparticles. • Coating accelerates the in vitro formation of apatite in simulated body fluid. • Coating promotes the osteogenic differentiation of stem cells. • Coating accelerates the formation of bone tissue in the periphery of the implant. - Abstract: The fabrication of a nanoporous silica coating loaded with bioactive glass nanoparticles (nBG/NSC) on titanium dental implant surface and its in vitro and in vivo evaluation is presented. The coating was produced by a combined sol–gel and evaporation induced self-assembly process. In vitro bioactivity was assessed in simulated body fluid (SBF) and investigating the osteogenic differentiation of human bone marrow mesenchymal stem cells (hBMSCs). A rat tibial model was employed to analyze the bone response to nBG/NSC-modified titanium implant surface in vivo. The nBG/NSC coating was confirmed at nano level to be constituted by a highly ordered nanoporous silica structure. The coating nanotopography in conjunction with the bioactivity of the BG particles accelerate the in vitro apatite formation and promote the osteogenic differentiation of hBMSCs in absence of osteogenic supplements. These properties accelerate the formation of bone tissue in the periphery of the implant after 3 weeks of implantation. Backscattered scanning electron microscopy images revealed the presence of gaps and soft tissue in the unmodified implant after 6 weeks, whereas the nBG/NSC-modified implant showed mature bone in intimate contact with the implant surface. The nBG/NSC coating appears promising for accelerating the osseointegration of dental implants.

Osseointegration properties of titanium dental implants modified with a nanostructured coating based on ordered porous silica and bioactive glass nanoparticles

International Nuclear Information System (INIS)

Covarrubias, Cristian; Mattmann, Matías; Von Marttens, Alfredo; Caviedes, Pablo; Arriagada, Cristián; Valenzuela, Francisco; Rodríguez, Juan Pablo; Corral, Camila

2016-01-01

Graphical abstract: - Highlights: • The fabrication of a coating for osseointegration of titanium implant is presented. • The coating consists of nanoporous silica loaded with bioactive glass nanoparticles. • Coating accelerates the in vitro formation of apatite in simulated body fluid. • Coating promotes the osteogenic differentiation of stem cells. • Coating accelerates the formation of bone tissue in the periphery of the implant. - Abstract: The fabrication of a nanoporous silica coating loaded with bioactive glass nanoparticles (nBG/NSC) on titanium dental implant surface and its in vitro and in vivo evaluation is presented. The coating was produced by a combined sol–gel and evaporation induced self-assembly process. In vitro bioactivity was assessed in simulated body fluid (SBF) and investigating the osteogenic differentiation of human bone marrow mesenchymal stem cells (hBMSCs). A rat tibial model was employed to analyze the bone response to nBG/NSC-modified titanium implant surface in vivo. The nBG/NSC coating was confirmed at nano level to be constituted by a highly ordered nanoporous silica structure. The coating nanotopography in conjunction with the bioactivity of the BG particles accelerate the in vitro apatite formation and promote the osteogenic differentiation of hBMSCs in absence of osteogenic supplements. These properties accelerate the formation of bone tissue in the periphery of the implant after 3 weeks of implantation. Backscattered scanning electron microscopy images revealed the presence of gaps and soft tissue in the unmodified implant after 6 weeks, whereas the nBG/NSC-modified implant showed mature bone in intimate contact with the implant surface. The nBG/NSC coating appears promising for accelerating the osseointegration of dental implants.

Structure and Properties of LENRA/ Silica Composite

International Nuclear Information System (INIS)

Mahathir Mohamed; Dahlan Mohd

2010-01-01

The sol-gel reaction using tetra ethoxysilane (TEOS) was conducted for modified natural rubber (NR) matrix to obtain in situ generated NR/ silica composite. The present of acrylate group in the modified NR chain turns the composite into radiation-curable. The maximum amount of silica generated in the matrix was 50 p hr by weight. During the sol-gel process the inorganic mineral was deposited in the rubber matrix forming hydrogen bonding between organic and inorganic phases. The composites obtained were characterized by various techniques including thermogravimetric analysis and infrared spectrometry to study their molecular structure. The increase in mechanical properties was observed for low silica contents ( 30 p hr) where more silica were generated, agglomerations were observed at the expense of the mechanical properties. From the DMTA data, it shows an increase of the interaction between the rubber and silica phases up to 30 p hr TEOS. Structure and morphology of the heterogeneous system were analyzed by transmission electron microscopy. The average particle sizes of between 150 nm to 300 nm were achieved for the composites that contain less than 20 p hr of TEOS. (author)

Vulcanization characteristics and dynamic mechanical behavior of natural rubber reinforced with silane modified silica.

Science.gov (United States)

Chonkaew, Wunpen; Minghvanish, Withawat; Kungliean, Ulchulee; Rochanawipart, Nutthaya; Brostow, Witold

2011-03-01

Two silane coupling agents were used for hydrolysis-condensation reaction modification of nanosilica surfaces. The surface characteristics were analyzed using Fourier transform infrared spectroscopy (FTIR). The vulcanization kinetics of natural rubber (NR) + silica composites was studied and compared to behavior of the neat NR using differential scanning calorimetry (DSC) in the dynamic scan mode. Dynamic mechanical analysis (DMA) was performed to evaluate the effects of the surface modification. Activation energy E(a) values for the reaction are obtained. The presence of silica, modified or otherwise, inhibits the vulcanization reaction of NR. The neat silica containing system has the lowest cure rate index and the highest activation energy for the vulcanization reaction. The coupling agent with longer chains causes more swelling and moves the glass transition temperature T(g) downwards. Below the glass transition region, silica causes a lowering of the dynamic storage modulus G', a result of hindering the cure reaction. Above the glass transition, silica-again modified or otherwise-provides the expected reinforcement effect.

Oxide glass structure evolution under swift heavy ion irradiation

International Nuclear Information System (INIS)

Mendoza, C.; Peuget, S.; Charpentier, T.; Moskura, M.; Caraballo, R.; Bouty, O.; Mir, A.H.; Monnet, I.; Grygiel, C.; Jegou, C.

2014-01-01

Highlights: • Structure of SHI irradiated glass is similar to the one of a hyper quenched glass. • D2 Raman band associated to 3 members ring is only observed in irradiated glass. • Irradiated state seems slightly different to an equilibrated liquid quenched rapidly. - Abstract: The effects of ion tracks on the structure of oxide glasses were examined by irradiating a silica glass and two borosilicate glass specimens containing 3 and 6 oxides with krypton ions (74 MeV) and xenon ions (92 MeV). Structural changes in the glass were observed by Raman and nuclear magnetic resonance spectroscopy using a multinuclear approach ( 11 B, 23 Na, 27 Al and 29 Si). The structure of irradiated silica glass resembles a structure quenched at very high temperature. Both borosilicate glass specimens exhibited depolymerization of the borosilicate network, a lower boron coordination number, and a change in the role of a fraction of the sodium atoms after irradiation, suggesting that the final borosilicate glass structures were quenched from a high temperature state. In addition, a sharp increase in the concentration of three membered silica rings and the presence of large amounts of penta- and hexacoordinate aluminum in the irradiated 6-oxide glass suggest that the irradiated glass is different from a liquid quenched at equilibrium, but it is rather obtained from a nonequilibrium liquid that is partially relaxed by very rapid quenching within the ion tracks

Study of the focusing effect of silica microspheres on the upconversion of Er{sup 3+}–Yb{sup 3+} codoped glass ceramics

Energy Technology Data Exchange (ETDEWEB)

Pérez-Rodríguez, C., E-mail: cjperez@ull.edu.es [Dpto. Física Fundamental y Experimental, Electrónica y Sistemas, Universidad de La Laguna, Av. Astrofísico Francisco Sánchez, s/n E-38206 La Laguna, Tenerife (Spain); Imanieh, M.H. [Department of Chemical and Environmental Engineering, University of Toledo, Toledo, OH (United States); Department of Materials, Ceramic Division, Iran University of Science and Technology, Tehran (Iran, Islamic Republic of); Martín, L.L [Dpto. Física Fundamental y Experimental, Electrónica y Sistemas, Universidad de La Laguna, Av. Astrofísico Francisco Sánchez, s/n E-38206 La Laguna, Tenerife (Spain); Ríos, S. [Dpto. de Física Básica, Universidad de La Laguna, Av. Astrofísico Francisco Sánchez, s/n E-38206 La Laguna, Tenerife (Spain); Martín, I.R. [Dpto. Física Fundamental y Experimental, Electrónica y Sistemas, Universidad de La Laguna, Av. Astrofísico Francisco Sánchez, s/n E-38206 La Laguna, Tenerife (Spain); MALTA Consolider Team, Av. Astrofísico Francisco Sánchez, s/n E-38206 La Laguna, Tenerife (Spain); Yekta, Bijan Eftekhari [Department of Materials, Ceramic Division, Iran University of Science and Technology, Tehran (Iran, Islamic Republic of)

2013-11-05

Highlights: •Silica microspheres have been located on the surface of glass and glass ceramics samples codoped with Er and Yb. •Microspheres act as microlens of the 950 nm excitation light resulting in focalized excited regions in the samples with sizes under the micron. •Intense red upconversion is achieved in the focalized areas. •Microspheres collect the upconversion emission light, scoping with the together microlensing properties an enhancement of the detected signal in a 3x factor. •Performed Finite-Difference Time-Domain simulations predict the size of the focalized regions in good agreement with the experimental measurements. -- Abstract: The upconversion emission properties of Er{sup 3+}–Yb{sup 3+} codoped glass and glass ceramic samples with different Si/Al ratios and thermal treatments were analyzed by covering their surfaces with silica microspheres (3.8 μm diameter). A 950 nm laser beam is focused by the microspheres producing a set of photonic nanojets near the surface of the samples. After the upconversion processes of the Er{sup 3+} ions located in each microsphere focus area, these ions emit light in the green and red regions. The red emission from each sample was measured, yielding an upconversion intensity in the focal areas three times higher than the emission from the bare substrate. To estimate the real size of the red emission area under a single microsphere, a deconvolution of the measured focal spots with the Point Spread Function of the experimental setup was performed, resulting in a Full Width at Half Maximum of 330 nm. The results obtained by Finite-Difference Time-Domain simulations are in good agreement with the experimental values.

Delamination propensity of pharmaceutical glass containers by accelerated testing with different extraction media.

Science.gov (United States)

Guadagnino, Emanuel; Zuccato, Daniele

2012-01-01

can cause glass particles to appear in vials, a problem that has forced a number of drug product recalls in recent years. To combat this, pharmaceutical and biopharmaceutical manufacturers need to understand the reasons for glass delamination. The most recent cases of product recall due to the presence of particles in the filling liquid have involved borosilicate glass containers carrying drugs made of active components with known ability to corrode glass and to dissolve the silica matrix. Sometimes these ingredients are dissolved in an alkaline medium that dramatically increases the glass corrosion and potentially causes the issue. As this action is strongly affected by time and temperature, flaking may become visible only after a long incubation during storage and requires systematic monitoring to be detected at its early stage. If the nature of the filling liquid is the driving force of the phenomenon, other factors are of primary importance. The surface morphology created during vial forming is a key issue, being a function of the forming temperature that is higher in the cutting step and the forming of the bottom. Delamination occurs generally on the vial's bottom and shoulder, where extensive flaming can favor a strong evaporation of alkali and borate species and the formation of heavily enriched silica layers. When these layers are in contact with a solution, they are subject to a differential re-hydration that may result in cracking and detachment of scales. The purpose of this investigation is to identify testing conditions and parameters that can be used as indicators of an incipient delamination process. Extractions with 0.9% KCl solution for 1 h at 121 °C can be used to simulate a long-term contact with aggressive pharmaceutical preparations, while SiO(2) concentration in the extract solution can be taken as an index of glass dissolution. The conclusions developed by this study can provide pharmaceutical manufacturers with information needed to help

Effects of MgO on short and long term stabilities in water of R7T7 and M7 nuclear waste glasses

Energy Technology Data Exchange (ETDEWEB)

Advocat, T; Vernaz, E; Dussossoy, J [CEA Centre d` Etudes de la Vallee du Rhone, 30 - Marcoule (France). Dept. des Procedes de Retraitement; Crovisier, J L [Centre National de la Recherche Scientifique (CNRS), 67 - Strasbourg (France)

1993-12-31

Magnesium oxide was added to the standard R7T7 and M7 glass compositions developed for containment of fission product solutions. M7 differs from the R7T7 reference glass mainly by a larger proportion of network modifier elements and a correspondingly lower proportion of glass network forming elements. The percentage of fission products, simulated in this study by inactive elements, was the same in both cases. Increasing the MgO content of the glass compositions by 2 to 5 wt% resulted in significant variations in the aqueous leaching resistance at 90 and 100 deg C. Experimental findings demonstrated that the initial dissolution rate measured at 100 deg C in a Soxhlet apparatus was proportional to the MgO content and inversely proportional to the network former content (mainly SiO2). This was confirmed by a glass hydration model based on the thermodynamic stability of the glass matrix components. Aqueous corrosion tests were also conducted at 90 deg C under static conditions at various SA/V ratios to simulate the progress of the reaction. Under these conditions, the glass dissolution rate diminished more slowly in time when the initial magnesium content was high and the network former content was low. This may be due primarily to a variation in the glass silica solubility limit related to the glass composition; it may also be related to the formation of secondary silica and magnesia alteration products controlling the glass dissolution reaction affinity.

Watching Silica's Dance: Imaging the Structure and Dynamics of the Atomic (Re-) Arrangements in 2D Glass

Science.gov (United States)

Muller, David

2014-03-01

Even though glasses are almost ubiquitous--in our windows, on our iPhones, even on our faces--they are also mysterious. Because glasses are notoriously difficult to study, basic questions like: ``How are the atoms arranged? Where and how do glasses break?'' are still under contention. We use aberration corrected transmission electron microscopy (TEM) to image the atoms in a new two-dimensional phase of silica glass - freestanding it becomes the world's thinnest pane of glass at only 3-atoms thick, and take a unique look into these questions. Using atom-by-atom imaging and spectroscopy, we are able to reconstruct the full structure and bonding of this 2D glass and identify it as a bi-tetrahedral layer of SiO2. Our images also strikingly resemble Zachariasen's original cartoon models of glasses, drawn in 1932. As such, our work realizes an 80-year-old vision for easily understandable glassy systems and introduces promising methods to test theoretical predictions against experimental data. We image atoms in the disordered solid and track their motions in response to local strain. We directly obtain ring statistics and pair distribution functions that span short-, medium-, and long-range order, and test these against long-standing theoretical predictions of glass structure and dynamics. We use the electron beam to excite atomic rearrangements, producing surprisingly rich and beautiful videos of how a glass bends and breaks, as well as the exchange of atoms at a solid/liquid interface. Detailed analyses of these videos reveal a complex dance of elastic and plastic deformations, phase transitions, and their interplay. These examples illustrate the wide-ranging and fundamental materials physics that can now be studied at atomic-resolution via transmission electron microscopy of two-dimensional glasses. Work in collaboration with: S. Kurasch, U. Kaiser, R. Hovden, Q. Mao, J. Kotakoski, J. S. Alden, A. Shekhawat, A. A. Alemi, J. P. Sethna, P. L. McEuen, A.V. Krasheninnikov

Compressive behavior of wire reinforced bulk metallic glass matrix composites

Energy Technology Data Exchange (ETDEWEB)

Lee, Seung-Yub [Department of Materials Science, M/C 138-78, California Institute of Technology, Pasadena, CA 91125 (United States); Clausen, Bjorn [Lujan Neutron Science Center, Los Alamos National Laboratory, Los Alamos, NM 87545 (United States); Uestuendag, Ersan [Department of Materials Science and Engineering, Iowa State University, Ames, IA 50011 (United States)]. E-mail: ustundag@iastate.edu; Choi-Yim, Haein [Department of Materials Science, M/C 138-78, California Institute of Technology, Pasadena, CA 91125 (United States); Aydiner, C. Can [Department of Materials Science and Engineering, Iowa State University, Ames, IA 50011 (United States); Bourke, Mark A.M. [Materials Science and Technology Division, Los Alamos National Laboratory, Los Alamos, NM 87545 (United States)

2005-06-15

Bulk metallic glasses (BMGs) possess a unique set of mechanical properties that make them attractive structural materials. However, when loaded without constraint, BMGs fracture catastrophically due to formation of macroscopic shear bands and this behavior reduces their reliability. To address this issue, BMG matrix composites have been developed. In this investigation, neutron diffraction was used during uniaxial compressive loading to measure the internal strains in the second phases of various BMG composites reinforced with Ta, Mo, or stainless steel wires. The diffraction data were then employed to develop a finite element model that deduced the in situ constitutive behavior of each phase. It was found that the reinforcements yielded first and started transferring load to the matrix, which remained elastic during the whole experiment. While the present composites exhibited enhanced ductility, largely due to their ductile reinforcements, they yielded at applied stresses lower than those found in W reinforced composites.

Microstructured fibers with high lanthanum oxide glass core for nonlinear applications

Science.gov (United States)

Kobelke, J.; Schuster, K.; Litzkendorf, D.; Schwuchow, A.; Kirchhof, J.; Bartelt, H.; Tombelaine, V.; Leproux, P.; Couderc, V.; Labruyere, A.

2009-05-01

We demonstrate a low loss microstructured fiber (MOF) with a high nonlinear glass core and silica holey cladding. The substitution of mostly used silica as core material of microstructured fibers by lanthanum oxide glass promises a high nonlinear conversion efficiency for supercontinuum (SC) generation. The glass composition is optimized in terms of thermochemical and optical requirements. The glass for the MOF core has a high lanthanum oxide concentration (10 mol% La2O3) and a good compatibility with the silica cladding. This is performed by adding a suitable alumina concentration up to 20 mol%. The lanthanum oxide glass preform rods were manufactured by melting technique. Besides purity issues the material homogeneity plays an important role to achieve low optical loss. The addition of fluorides allows the better homogenization of the glass composition in the preform volume by refining. The minimum attenuation of an unstructured fiber drawn from this glass is about 0.6 dB/m. It is mostly caused by decreasing of scattering effects. The microstructured silica cladding allows the considerable shifting of dispersive behavior of the MOF for an optimal pump light conversion. The MOF shows zero dispersion wavelengths (ZDW) of 1140 nm (LP01 mode) and 970 nm (LP11 mode). The supercontinuum generation was investigated with a 1064 nm pump laser (650 ps). It shows a broad band emission between 500 nm and 2200 nm.

100 MeV silver ions induced defects and modifications in silica glass

Energy Technology Data Exchange (ETDEWEB)

Jadhav, Vijay S.; Deore, Avinash V.; Dahiwale, S.S. [Department of Physics, University of Pune, Pune 411007 (India); Kanjilal, D. [Inter University Accelerator Centre, New Delhi 110067 (India); Bhoraskar, V.N. [Department of Physics, University of Pune, Pune 411007 (India); Dhole, S.D., E-mail: sanjay@physics.unipune.ac.in [Department of Physics, University of Pune, Pune 411007 (India)

2014-07-15

Highlights: •Study of silver ion induced defects and modifications in silica glass. •Variation in oxygen deficiency centres (ODA-II) and nonbridging oxygen hole centres (NBOHC). •Study of structural damage in terms of Urbach energy. -- Abstract: A few silica glass samples having 1 cm{sup 2} area and 0.1 cm thickness were irradiated with 100 MeV energy Ag{sup 7+} ions for the fluences ranging from 1 × 10{sup 12} ions/cm{sup 2} to 5 × 10{sup 13} ions/cm{sup 2}. The optical properties and the corresponding induced defects were characterised by the techniques such as UV–Visible, Photoluminescence (PL), Fourier transform infrared (FTIR), and Electron spin resonance (ESR) spectroscopy. The UV–Visible absorption spectra show two peaks, one at 5 eV and another weak peak at 5.8 eV. A peak observed at 5.0 eV corresponds to B{sub 2} band (oxygen deficiency in SiO{sub 2} network) and the peak at 5.8 eV is due to the paramagnetic defects like E′ centre. The intensities of these peaks found to be increased with increase in ion fluence. It attributes to the increase in the concentration of E′ centres and B{sub 2} band respectively. In addition, the optical band gap energy, Urbach energy and the defects concentration have been calculated using Urbach plot. The optical band gap found to be decreased from 4.65 eV to 4.39 eV and the Urbach energy found to be increased from 60 meV to 162 meV. The defect concentration of nonbridging oxygen hole centres (NBOHC) and E′ centres are found to be increased to 1.69 × 10{sup 13} cm{sup −3} and 3.134 × 10{sup 14} cm{sup −3} respectively. In PL spectra, the peak appeared at 1.92 eV and 2.7 eV envisage the defects of nonbridging oxygen hole centres and B{sub 2α} oxygen deficient centres respectively. ESR spectra also confirms the existence of E′ and NBOHC centres. FTIR spectra shows scissioning of Si-O-Si bonds and the formation of Si-H and Si-OH bonds, which supports to the co-existence of the defects induced by Ag

Determining the fracture resistance of fibre-reinforced glass matrix composites by means of the chevron-notch flexural technique

Czech Academy of Sciences Publication Activity Database

Boccaccini, A. R.; Kern, H.; Dlouhý, Ivo

2001-01-01

Roč. 308, 1/2 (2001), s. 111-117 ISSN 0921-5093 R&D Projects: GA ČR GV101/96/K264 Institutional research plan: CEZ:AV0Z2041904 Keywords : glass matrix composites * fracture toughness * chevron notch test Subject RIV: JH - Ceramics, Fire-Resistant Materials and Glass Impact factor: 0.978, year: 2001

Lipase B from Candida antarctica Immobilized on a Silica-Lignin Matrix as a Stable and Reusable Biocatalytic System

Directory of Open Access Journals (Sweden)

Jakub Zdarta

2016-12-01

Full Text Available A study was conducted of the possible use of a silica-lignin hybrid as a novel support for the immobilization of lipase B from Candida antarctica. Results obtained by elemental analysis, Fourier transform infrared spectroscopy (FTIR, X-ray photoelectron spectroscopy (XPS, and atomic force microscopy (AFM, as well as the determination of changes in porous structure parameters, confirmed the effective immobilization of the enzyme on the surface of the composite matrix. Based on a hydrolysis reaction, a determination was made of the retention of activity of the immobilized lipase, found to be 92% of that of the native enzyme. Immobilization on a silica-lignin matrix produces systems with maximum activity at pH = 8 and at a temperature of 40 °C. The immobilized enzyme exhibited increased thermal and chemical stability and retained more than 80% of its activity after 20 reaction cycles. Moreover immobilized lipase exhibited over 80% of its activity at pH range 7–9 and temperature from 30 °C to 60 °C, while native Candida antarctica lipase B (CALB exhibited the same only at pH = 7 and temperature of 30 °C.

Glass matrix armor

International Nuclear Information System (INIS)

Calkins, N.C.

1991-01-01

This patent describes an armor system which utilizes glass. A plurality of constraint cells are mounted on a surface of a substrate, which is metal armor plate or a similar tough material, such that the cells almost completely cover the surface of the substrate. Each constraint cell has a projectile receiving wall parallel to the substrate surface and has sides which are perpendicular to and surround the perimeter of the receiving wall. The cells are mounted such that, in one embodiment, the substrate surface serves as a sixth side or closure for each cell. Each cell has inside of it a plate, termed the front plate, which is parallel to and in contact with substantially all of the insides surface of the receiving wall. The balance of each cell is completely filled with a projectile-abrading material consisting of glass and a ceramic material and, in certain embodiments, a polymeric material

Striking role of non-bridging oxygen on glass transition temperature of calcium aluminosilicate glass-formers

International Nuclear Information System (INIS)

Bouhadja, M.; Jakse, N.; Pasturel, A.

2014-01-01

Molecular dynamics simulations are used to study the structural and dynamic properties of calcium aluminosilicate, (CaO-Al 2 O 3 ) 1−x (SiO 2 ) x , glass formers along three joins, namely, R = 1, 1.57, and 3, in which the silica content x can vary from 0 to 1. For all compositions, we determined the glass-transition temperature, the abundances of the non-bridging oxygen, triclusters, and AlO 5 structural units, as well as the fragility from the temperature evolution of the α-relaxation times. We clearly evidence the role played by the non-bridging oxygen linked either to Al atoms or Si atoms in the evolution of the glass-transition temperature as well as of the fragility as a function of silica content along the three joins

Silica artificial opal incorporated with silver nanoparticles

Energy Technology Data Exchange (ETDEWEB)

Li Wenjiang, E-mail: wjli@zju.edu.cn [Center for Optical and Electromagnetic Research, State Key Laboratory for Modern Optical Instrumentation, Zhejiang University, Joint Research Center of Photonics of the Royal Institute of Technology and Zhejiang University, Zijingang Campus, Room 210, East Building 5, Hangzhou 310058 (China); Sun Tan [Center for Optical and Electromagnetic Research, State Key Laboratory for Modern Optical Instrumentation, Zhejiang University, Joint Research Center of Photonics of the Royal Institute of Technology and Zhejiang University, Zijingang Campus, Room 210, East Building 5, Hangzhou 310058 (China)

2009-07-15

The silica artificial opal with a three-dimensional (3D) periodic structure was prepared using highly monodispersed silica microspheres by a force packing method in ITO glass cell. The silica artificial opal incorporated with silver nanoparticles was fabricated by the electroplating technique. The optical microscope images of the synthetic sample and the corresponding optical properties were measured after each treatment of electroplating-washing-drying circle. The transmission and reflection spectra presented a red shift, showing that the effective refractive index of the complex silver/silica opal increased after each electroplating. Combining the SEM images, it was seen that the silver nanoparticles could be directly deposited on the surface of silica spheres in the opaline structure. The silver/silica complex opal film could provide a simple way to tune the opal properties by controlling silver nanoparticles in the silica opal. The silver/silica opal crystal structures could be used for nano-photonic circuits, white-light LEDs or as photocatalysts.

Silica artificial opal incorporated with silver nanoparticles

International Nuclear Information System (INIS)

Li Wenjiang; Sun Tan

2009-01-01

The silica artificial opal with a three-dimensional (3D) periodic structure was prepared using highly monodispersed silica microspheres by a force packing method in ITO glass cell. The silica artificial opal incorporated with silver nanoparticles was fabricated by the electroplating technique. The optical microscope images of the synthetic sample and the corresponding optical properties were measured after each treatment of electroplating-washing-drying circle. The transmission and reflection spectra presented a red shift, showing that the effective refractive index of the complex silver/silica opal increased after each electroplating. Combining the SEM images, it was seen that the silver nanoparticles could be directly deposited on the surface of silica spheres in the opaline structure. The silver/silica complex opal film could provide a simple way to tune the opal properties by controlling silver nanoparticles in the silica opal. The silver/silica opal crystal structures could be used for nano-photonic circuits, white-light LEDs or as photocatalysts.

On the improvement of mechanical properties of monolithic silica aerogels (for transparent insulating material); Silica aerogel (tomei dannetsu zairyo) kyodo no kaizen ni tsuite

Energy Technology Data Exchange (ETDEWEB)

Tajiri, K; Igarashi, K; Tanemura, S [National Industrial Research Institute of Nagoya, Nagoya (Japan)

1997-11-25

Study was made on improvement of the strength of silica aerogel as transparent insulating material. Silica aerogel is a low-density porous material with high heat insulation and transparency. To develop a insulating material with high transparency, monolithic silica aerogel was studied. For direct use of it for windows, its strength improvement was attempted. The aerogel was prepared by supercritical drying (alcohol or CO2) of silica wet gel obtained by hydrolysis and condensation of silicon alkoxide solution. To prepare the aerogel bonded on plate glass for strength improvement, the aerogel was bonded to alkoxide by exposing active silanol radical through F-etching of plate glass surface. However, to obtain the practical large-area bonded aerogel, shrinkage control of the aerogel in supercritical drying was necessary. Addition of Laponite into a silica network for strength improvement by polymer increased the bending strength by 50%. Although some reduction of its transparency was observed because of clouding, its heat insulation was stable. Further strength improvement is necessary for its practical use. 5 figs., 1 tab.

Green synthesis of water-glass from municipal solid waste incineration bottom ash

NARCIS (Netherlands)

Hendrix, Y.; Alam, Q.; Thijs, L.; Lazaro Garcia, A.; Brouwers, H.J.H.

2017-01-01

Water-glass is extensively used as a silica precursor in different chemical applications such as alkali activated binders and nano-silica. The current production of water-glass involves the fusion of sand with soda ash at temperatures above 1000 ºC, which makes the production expensive and

Surface modification on a glass surface with a combination technique of sol–gel and air brushing processes

KAUST Repository

Tsai, Meng-Yu; Hsu, Chin-Chi; Chen, Ping-Hei; Lin, Chao-Sung; Chen, Alexander

2011-01-01

This study fabricated the large area and optically transparent superhydrophobic silica based films on glass surface with optimized hardness. A silane coupling agent, tetraethoxysilane (TEOS), effectively bonds silica particles onto the glass substrate. Desired surface roughness was obtained by adjusting nano silica particles concentration of the precursors prepared by the sol-gel process. Silica suspension was coated onto the glass substrate by the air brushing methods. This method can deposit a uniform, transparent coating on the glass substrate efficiently. Diluting the precursor by adding ethanol or a mixture of D.I. water and ethanol further improved the transmittance and superhydrophobicity efficiency. The results showed that as the silica particle concentration and the thickness of the coating were increased, the surface roughness was enhanced. Rougher surface displayed a higher superhydrophobicity and lower transmittance. Therefore, the concentration of silica particle, volume of coatings, and the ratio of ethanol and D.I. water are of great importance to deposit a transparent, superhydrophobic coating on glass. © 2011 Elsevier B.V. All rights reserved.

Surface modification on a glass surface with a combination technique of sol–gel and air brushing processes

KAUST Repository

Tsai, Meng-Yu

2011-08-01

This study fabricated the large area and optically transparent superhydrophobic silica based films on glass surface with optimized hardness. A silane coupling agent, tetraethoxysilane (TEOS), effectively bonds silica particles onto the glass substrate. Desired surface roughness was obtained by adjusting nano silica particles concentration of the precursors prepared by the sol-gel process. Silica suspension was coated onto the glass substrate by the air brushing methods. This method can deposit a uniform, transparent coating on the glass substrate efficiently. Diluting the precursor by adding ethanol or a mixture of D.I. water and ethanol further improved the transmittance and superhydrophobicity efficiency. The results showed that as the silica particle concentration and the thickness of the coating were increased, the surface roughness was enhanced. Rougher surface displayed a higher superhydrophobicity and lower transmittance. Therefore, the concentration of silica particle, volume of coatings, and the ratio of ethanol and D.I. water are of great importance to deposit a transparent, superhydrophobic coating on glass. © 2011 Elsevier B.V. All rights reserved.

Metal particles constraint in glass matrix composites and its impact on fracture toughness enhancement

Czech Academy of Sciences Publication Activity Database

Kotoul, M.; Dlouhý, Ivo

387-389 (2004), s. 404-408 ISSN 0921-5093 R&D Projects: GA ČR GA101/02/0683 Institutional research plan: CEZ:AV0Z2041904 Keywords : brittle matrix composites * crack bridging * crack trapping Subject RIV: JH - Ceramics, Fire-Resistant Materials and Glass Impact factor: 1.445, year: 2004

Soda-based glass fabricated from Thailand quartz sands doped with silver compound

Science.gov (United States)

Won-in, Krit; Dararutana, Pisutti

2012-10-01

Yellow colored glass which used for luxury art glass in ancient time was fabricated by the addition of silver compound into the molten glass. It was proved that it was actually silver nanoparticle technology. In this work, the SiO2-(Na2O,K2O)-CaO-B2O3-Al2O3-MgO glass system was prepared in the laboratory scale based on local quartz sands from Trat Province, eastern area of Thailand as the silica raw material. Various concentrations of silver nitrate were added. After the complete conventional melting process, the bubble-free yellow glasses were yielded. Physical and optical properties such as density, refractive index and optical absorption spectra were measured. Scanning electron microscope coupled with energy dispersive spectroscopy was carried out to study their morphology. The refractive indices and densities were increased as the increase of the silver contents. Electron micrographs showed the presence of silver nanoparticle in the glass matrix. UV-VIS spectra were in good agreement with that found from SEM measurements and corresponded with the universally accepted. It was also showed that the more brilliance on the surface of the glass products was obtained after firing with a gas torch.

a study on silica sand quality in yazaram and mugulbu deposits

African Journals Online (AJOL)

ENGR. G A DUVUNA

A STUDY ON SILICA SAND QUALITY IN YAZARAM AND MUGULBU ... the lowest percentage of silica content of 77.60% and the grain morphology was found to be angular with specific ..... things.com/articles/glass colouring.html, accessed.

Preparation and thermal properties of mesoporous silica/phenolic resin nanocomposites via in situ polymerization

Directory of Open Access Journals (Sweden)

J. Lv

2012-10-01

Full Text Available In order to enhance the adhesion between inorganic particles and polymer matrix, in this paper, the mesoporous silica SBA-15 material was synthesized by the sol-gel method. The surface of SBA-15 was modified using γ-glycidyloxypropyltrimethoxysilane (GOTMS as a coupling agent, and then mesoporous silica/phenolic resin (SBA-15/PF nanocomposites were prepared via in situ polymerization. The structural parameters and physical properties of SBA-15, SBA-15-GOTMS (SBA-15 surface treated using GOTMS as coupling agents and E-SBA-15/PF (SBA-15/PF nanocomposites extracted using ethanol as solvent were characterized by X-ray diffraction (XRD, N2 adsorption-desorption, Fourier transform infrared spectroscopy (FTIR, scanning electron microscopy (SEM, transmission electron microscopy (TEM and thermogravimetric analysis (TGA. The thermal properties of the nanocomposites were studied by differential scanning calorimetry (DSC and thermogravimetric analysis (TGA. The results demonstrated that the GOTMS were successfully grafted onto the surface of SBA-15, and chemical bonds between PF and SBA-15-GOTMS were formed after in situ polymerization. In addition, it is found that the in situ polymerization method has great effects on the textural parameters of SBA-15. The results also showed that the glass transition temperatures and thermal stability of the PF nanocomposites were obviously enhanced as compared with the pure PF at silica contents between 1–3 wt%, due to the uniform dispersion of the modified SBA-15 in the matrix.

Immobilisation of radwastes in glass containers and products formed thereby

International Nuclear Information System (INIS)

Macedo, P.B.; Simmons, C.J.; Lagakos, N.; Simmons, J.H.; Tran, D.C.

1980-01-01

A method of preventing the dissemination of toxic material to the environment comprises forming an admixture of toxic material and glass packing in a hollow doped glass container of high silica content, or forming the admixture in a first container and then depositing at least a portion of the admixture in a hollow doped glass container of high silica content. The glass container is then heated to collapse its walls and to seal the container so that the toxic material is entrapped and sealed within the collapsed doped glass container. The thermal expansion coefficient of the container may be decreased prior to use by exchanging hydrogen ion in pores thereof with other cations followed by collapsing the pores. (author)

All-silica nanofluidic devices for DNA-analysis fabricated by imprint of sol-gel silica with silicon stamp

DEFF Research Database (Denmark)

Mikkelsen, Morten Bo Lindholm; Letailleur, Alban A; Søndergård, Elin

2011-01-01

We present a simple and cheap method for fabrication of silica nanofluidic devices for single-molecule studies. By imprinting sol-gel materials with a multi-level stamp comprising micro- and nanofeatures, channels of different depth are produced in a single process step. Calcination of the imprin......We present a simple and cheap method for fabrication of silica nanofluidic devices for single-molecule studies. By imprinting sol-gel materials with a multi-level stamp comprising micro- and nanofeatures, channels of different depth are produced in a single process step. Calcination...... of the imprinted hybrid sol-gel material produces purely inorganic silica, which has very low autofluorescence and can be fusion bonded to a glass lid. Compared to top-down processing of fused silica or silicon substrates, imprint of sol-gel silica enables fabrication of high-quality nanofluidic devices without...

High-Strength / High Alkaline Resistant Fe-Phosphate Glass Fibers as Concrete Reinforcement

Energy Technology Data Exchange (ETDEWEB)

Mariano Velez

2008-03-31

Calcium-iron-phosphate glasses were developed whose chemical durabilities in alkaline solutions (pH 13) were comparable or superior to those of commercial alkaline-resistant (AR) silica-based glasses. However, the tensile strength of Ca-Fe-phosphate fibers, after being exposed to alkaline environments, including wet Portland cement pastes, is lower than that of current AR silicate fibers. Another series of Ca-Fe-phosphate glasses were developed with excellent chemical durability in strong acidic solutions (H2SO4, HF), indicating potential applications where silica-based fibers degrade very quickly, including E-glass. The new Ca-Fe-phosphate glasses can be melted and processed 300 to 500°C lower than silica-based glasses. This offers the possibility of manufacturing glass fibers with lower energy costs by 40-60% and the potential to reduce manufacturing waste and lower gas emissions. It was found that Ca-Fe-phosphate melts can be continuously pulled into fibers depending on the slope of the viscosity-temperature curve and with viscosity ~100 poise, using multi-hole Pt/Rh bushings.

Effect of static pre-loading on fracture toughness of Nicalon fibre glass matrix composite

Czech Academy of Sciences Publication Activity Database

Dlouhý, Ivo; Chlup, Zdeněk; Chawla, K. K.; Kulkarmi, R.; Koopman, M.; Boccaccini, A. R.

č. 367 (2004), s. 17-23 ISSN 0921-5093 R&D Projects: GA AV ČR IAA2041003; GA MŠk ME 491 Institutional research plan: CEZ:AV0Z2041904 Keywords : Nicalon fibre * glass matrix composite * fracture toughness Subject RIV: JL - Materials Fatigue, Friction Mechanics Impact factor: 1.445, year: 2004

Interfacial interaction between the epoxidized natural rubber and silica in natural rubber/silica composites

Science.gov (United States)

Xu, Tiwen; Jia, Zhixin; Luo, Yuanfang; Jia, Demin; Peng, Zheng

2015-02-01

The epoxidized natural rubber (ENR) as an interfacial modifier was used to improve the mechanical and dynamical mechanical properties of NR/silica composites. In order to reveal the interaction mechanism between ENR and silica, the ENR/Silica model compound was prepared by using an open mill and the interfacial interaction of ENR with silica was investigated by Fourier transform infrared spectroscopy (FTIR), X-ray photoelectron spectroscopy (XPS), transmission electron microscopy (TEM), X-ray diffraction (XRD) and stress-strain testing. The results indicated that the ring-opening reaction occurs between the epoxy groups of ENR chains and Si-OH groups on the silica surfaces and the covalent bonds are formed between two phases, which can improve the dispersion of silica in the rubber matrix and enhance the interfacial combination between rubber and silica. The ring-opening reaction occurs not only in vulcanization process but also in mixing process, meanwhile, the latter seems to be more important due to the simultaneous effects of mechanical force and temperature.

Investigation of vacuum deposited hybrid coatings of protic organic UV absorbers embedded in a silica matrix used for the UV protection of Polycarbonate glazing

OpenAIRE

Weber, C.; Schulz, U.; Mühlig, C.; Kaiser, N.; Tünnermann, A.

2016-01-01

A study of vacuum-deposited organic-inorganic hybrid coatings for UV protection of polycarbonate is presented. UV-absorbing compounds, which are commonly used for polycarbonate, were embedded in a silica matrix by thermal co-evaporation under high vacuum. In addition to the optical properties of the coatings, the influence of the silica network on the organic UV absorber and the stability of the intramolecular hydrogen bond (IMHB) are discussed. A model is presented to show the interaction be...

Effect of silver nanoparticles on the dielectric properties of holmium doped silica glass

International Nuclear Information System (INIS)

Rejikumar, P.R.; Jyothy, P.V.; Mathew, Siby; Thomas, Vinoy; Unnikrishnan, N.V.

2010-01-01

The effect of silver nanoparticle co-doping on the dielectric properties of holmium doped silica glasses was studied. Silver nanoparticles of size between 20 and 22 nm were produced by the sol-gel technique. One of the samples showed an icosahedral morphology of the nanocrystal formed, along with spherical morphology. It was found that the tuning of the dielectric constant values could be accomplished by co-doping. The sample, with 1 wt% of Ho, had low dielectric constant values within the range 100 Hz-3 MHz due to the formation of quasi-molecular structures of holmium. This effect was evaded to some extent with silver co-doping as a result of the interdispersion of holmium complexes. Also it was found that the co-doping produced a higher dielectric loss which was calculated from the tan δ-log f graph. The Cole-Cole parameters and the Jonscher power law parameters were also calculated and are presented.

Hydration of high-silica glasses in the deep sea

International Nuclear Information System (INIS)

Federman, A.N.

1986-01-01

Natural analogs of nuclear waste glasses are important because they provide information of the one variable that is not controllable in the laboratory - long intervals of time in the actual environment of storage. Some natural glasses have persisted for millions of years in deep-sea sediments in the form of disseminated particles and distinct tephra layers, while other apparently similar specimens have been completely altered to clay assemblages relatively quickly. Geologists have reached no firm conclusions as to why these differences exist, and more research is certainly warranted. These glasses vary in age, composition, and in the in-situ conditions they have experienced. They may provide important information for two different aspects of nuclear waste glass research: First, the chemical composition and especially the water content of these glasses as a function of time may give an understanding of the mechanisms and rates of diffusion in glasses in the natural environment. Second, the apparent differing durability of these glasses in different environmental conditions may suggest the optimal characteristics of a nuclear waste glass depository

Prevention of Bacterial Contamination of a Silica Matrix Containing Entrapped β-Galactosidase through the Action of Covalently Bound Lysozymes

Directory of Open Access Journals (Sweden)

Heng Li

2017-02-01

Full Text Available β-galactosidase was successfully encapsulated within an amino-functionalised silica matrix using a “fish-in-net” approach and molecular imprinting technique followed by covalent binding of lysozyme via a glutaraldehyde-based method. Transmission electron microscopy (TEM, X-ray diffraction (XRD, scanning electron microscopy (SEM, and Fourier transform infrared (FTIR spectroscopy were used to characterise the silica matrix hosting the two enzymes. Both encapsulated β-galactosidase and bound lysozyme exhibited high enzymatic activities and outstanding operational stability in model reactions. Moreover, enzyme activities of the co-immobilised enzymes did not obviously change relative to enzymes immobilised separately. In antibacterial tests, bound lysozyme exhibited 95.5% and 89.6% growth inhibition of Staphylococcus aureus ATCC (American type culture collection 653 and Escherichia coli ATCC 1122, respectively. In milk treated with co-immobilised enzymes, favourable results were obtained regarding reduction of cell viability and high lactose hydrolysis rate. In addition, when both co-immobilised enzymes were employed to treat milk, high operational and storage stabilities were observed. The results demonstrate that the use of co-immobilised enzymes holds promise as an industrial strategy for producing low lactose milk to benefit people with lactose intolerance.

Mechanical Properties of a High Lead Glass Used in the Mars Organic Molecule Analyzer

Science.gov (United States)

Salem, Jonathan A.; Smith, Nathan A.; Ersahin, Akif

2015-01-01

The elastic constants, strength, fracture toughness, slow crack growth parameters, and mirror constant of a high lead glass supplied as tubes and funnels were measured using ASTM International (formerly ASTM, American Society for Testing and Materials) methods and modifications thereof. The material exhibits lower Young's modulus and slow crack growth exponent as compared to soda-lime silica glass. Highly modified glasses exhibit lower fracture toughness and slow crack growth exponent than high purity glasses such as fused silica.

Experimental and Theoretical Investigations of Glass Surface Charging Phenomena

Science.gov (United States)

Agnello, Gabriel

Charging behavior of multi-component display-type (i.e. low alkali) glass surfaces has been studied using a combination of experimental and theoretical methods. Data obtained by way of a Rolling Sphere Test (RST), streaming/zeta potential and surface energy measurements from commercially available display glass surfaces (Corning EAGLE XGRTM and Lotus(TM) XT) suggest that charge accumulation is highly dependent on surface treatment (chemical and/or physical modification) and measurement environment, presumably through reactionary mechanisms at the surface with atmospheric moisture. It has been hypothesized that water dissociation, along with the corresponding hydroxylation of the glass surface, are important processes related to charging in glass-metal contact systems. Classical Molecular Dynamics (MD) simulations, in conjunction with various laboratory based measurements (RST, a newly developed ElectroStatic Gauge (ESG) and Diffuse Reflectance Infrared Fourier Transform Spectroscopy (DRIFTS)) on simpler Calcium AluminoSilicate (CAS) glass surfaces were used to further explore these phenomena. Analysis of simulated high-silica content (≥50%) (CAS) glass structures suggest that controlled variation of bulk chemistry can directly affect surface defect concentrations, such as non-bridging oxygen (NBO), which can be suitable high-energy sites for hydrolysis-type reactions to occur. Calculated NBO surface concentrations correlate well with charge based measurements on laboratory fabricated CAS surfaces. The data suggest that a directional/polar shift in contact-charge transfer occurs at low silica content (≤50%) where the highest concentrations of NBOs are observed. Surface charging sensitivity with respect to NBO concentration decreases as the relative humidity of the measurement environment increases; which should be expected as the highly reactive sites are progressively covered by liquid water layers. DRIFTS analysis of CAS powders expand on this analysis showing

Permanently densified SiO2 glasses: a structural approach.

Science.gov (United States)

Martinet, C; Kassir-Bodon, A; Deschamps, T; Cornet, A; Le Floch, S; Martinez, V; Champagnon, B

2015-08-19

Densified silica can be obtained by different pressure and temperature paths and for different stress conditions, hydrostatic or including shear. The density is usually the macroscopic parameter used to characterize the different compressed silica samples. The aim of our present study is to compare structural modifications for silica glass, densified from several routes. For this, densified silica glasses are prepared from cold and high temperature (up to 1020 °C) compressions. The different densified glasses obtained in our study are characterized by micro-Raman spectroscopy. Intertetrahedral angles from the main band relative to the bending mode decrease and their values are larger for densified samples from high temperature compression than those samples from cold compression. The relative amount of 3-membered rings deduced from the D2 line area increases as a function of density for cold compression. The temperature increase during the compression process induces a decrease of the 3 fold ring population. Moreover, 3 fold rings are more deformed and stressed for densified samples at room temperature at the expense of those densified at high temperature. Temperature plays a main role in the reorganization structure during the densification and leads to obtaining a more relaxed structure with lower stresses than glasses densified from cold compression. The role of hydrostatic or non-hydrostatic applied stresses on the glass structure is discussed. From the Sen and Thorpe central force model, intertetrahedral angle average value and their distribution are estimated.

The applicability of alkaline-resistant glass fiber in cement mortar of road pavement: Corrosion mechanism and performance analysis

Directory of Open Access Journals (Sweden)

Qin Xiaochun

2017-11-01

Full Text Available The main technical requirements of road pavement concrete are high flexural strength and fatigue durability. Adding glass fiber into concrete could greatly increase flexural strength and wearing resistance of concrete. However, glass fiber has the great potential of corrosion during the cement hydration, which will directly affect the long-term performance and strength stability. In this paper, accelerated corrosion experiments have been done to find out the corrosion mechanism and property of alkali-resistant glass fiber in cement mortar. The applicability and practicability of alkaline-resistant glass fiber in road concrete have been illustrated in the analysis of flexural strength changing trend of cement mortar mixed with different proportions of activated additives to protect the corrosion of glass fiber by cement mortar. The results have shown that a 30% addition of fly ash or 10% addition of silica fume to cement matrix could effectively improve the corrosion resistance of alkali-resistant glass fiber. The optimal mixing amount of alkali-resistant glass fiber should be about 1.0 kg/m3 in consideration of ensuring the compressive strength of reinforced concrete in road pavement. The closest-packing method has been adopted in the mixture ratio design of alkali-resistant glass fiber reinforced concrete, not only to reduce the alkalinity of the cement matrix through large amount addition of activated additives but also to greatly enhance the flexural performance of concrete with the split pressure ratio improvement of 12.5–16.7%. The results suggested a prosperous application prospect for alkaline-resistant glass fiber reinforced concrete in road pavement.

Effects of ion implantation on the hardness and friction behaviour of soda-lime silica glass

International Nuclear Information System (INIS)

Bull, S.J.; Page, T.F.

1992-01-01

Ion implantation-induced changes in the near-surface mechanical properties of soda-lime silica glass have been investigated by indentation and scratch testing and have been found to be more complicated than changes in the corresponding properties of crystalline ceramic materials. Argon, nitrogen, carbon and potassium ions were used with energies in the range 45-300 keV. Hardness and scratch friction tests were performed under ambient laboratory conditions. At low doses, a decrease in hardness and an increase in both friction and surface stress are observed which are attributed to the electronic damage produced by ion implantation. At higher doses, the hardness increases again and a maximum is produced similar to the behaviour observed for crystalline materials. Similarly there is found to be a second stress and friction peak at this dose. This behaviour is shown to be due to the build-up of displacement damage produced by ion implantation and is thus very similar to the radiation hardening (and eventual amorphization) behaviour of ion-implanted crystalline ceramics. For glass, ''amorphization'' probably corresponds to some change in the existing amorphous state which, in turn, is responsible for the reduction in hardness, stress and friction at the highest doses. (author)

The analysis of lightweight brick strength pressure with mixture of glass powder and silica fume

Science.gov (United States)

Nursyamsi; Liang, William

2018-03-01

Little by little the engineers research how the development of concrete that can utilize waste. In the utilization of the waste, it can be functioned as mixing material which the chemical or the physical traits of the used goods contain similarity to the mixture of concrete in general, one of them is glass powder as the substitute of cement. The glass powder that utilizes is the one that is sifted through sieve No. 200 as much as 10% of the weight of the cement. The testing specimen of the concrete brick is make of the mixture with the ratio of 1:7, then is added with the foaming agent (1:30) and silica fume (10% of the weight of the cement). Furthermore, visual examination, absorption, net weight and testing specimen compressive strength. The data analysis uses the reference of SNI 03 – 0349 – 1989 regarding Concrete Brick for the Match for the Wall. Foaming Agent is make by using modified hand drill and brace. The testing specimen uses the brick mold with the size of 40 cm x 20cm x 10 cm. Based on this research, it shows that the quality that results from brick is still qualified based on SNI 03 – 0349 – 1989.

Glass transition of poly (methyl methacrylate) filled with nanosilica and core-shell structured silica

DEFF Research Database (Denmark)

Song, Yihu; Bu, Jing; Zuo, Min

2017-01-01

transition and segmental dynamics of PMMA in the nanocomposites prepared via solution casting was compared. The remarkable depression (≥10 °C) of glass transition temperature (Tg) induced by the incorporation of SiO2 and CS was both observed at low loadings. Here, different mechanisms were responsible...... for the effect of SiO2 and CS on the segmental acceleration of PMMA matrix. The formation of rigid amorphous fraction (RAF) layer around SiO2 with the thickness of 16.4 nm led to the adjacent molecular packing frustration, while the “lubrication” effect of nonwetting interface between the grafted crosslinked......Core-shell (CS) nanocomposite particles with 53.4 wt% cross-linked poly (methyl methacrylate) (PMMA) shell of 11.6 nm in thickness were fabricated via miniemulsion polymerization of methyl methacrylate in the presence of modified nanosilica. The influence of nanosilica and CS nanoparticles on glass...

Silica-based ionic liquid coating for 96-blade system for extraction of aminoacids from complex matrixes

International Nuclear Information System (INIS)

Mousavi, Fatemeh; Pawliszyn, Janusz

2013-01-01

Graphical abstract: -- Highlights: •Silica-based 1-vinyl-3-octadecylimidazolium bromide ionic liquid was synthesized and characterized. •The synthesized polymer was immobilized on the stainless steel blade using polyacrylonitrile glue. •SiImC 18 -PAN 96-blade SPME was applied as an extraction phase for extraction of highly polar compounds in grape matrix. •This system provides high extraction efficiency and reproducibility for up to 50 extractions from tartaric buffer and 20 extractions from grape pulp. -- Abstract: 1-Vinyl-3-octadecylimidazolium bromide ionic liquid [C 18 VIm]Br was prepared and used for the modification of mercaptopropyl-functionalized silica (Si-MPS) through surface radical chain-transfer addition. The synthesized octadecylimidazolium-modified silica (SiImC 18 ) was characterized by thermogravimetric analysis (TGA), infrared spectroscopy (IR), 13 C NMR and 29 Si NMR spectroscopy and used as an extraction phase for the automated 96-blade solid phase microextraction (SPME) system with thin-film geometry using polyacrylonitrile (PAN) glue. The new proposed extraction phase was applied for extraction of aminoacids from grape pulp, and LC–MS–MS method was developed for separation of model compounds. Extraction efficiency, reusability, linearity, limit of detection, limit of quantitation and matrix effect were evaluated. The whole process of sample preparation for the proposed method requires 270 min for 96 samples simultaneously (60 min preconditioning, 90 min extraction, 60 min desorption and 60 min for carryover step) using 96-blade SPME system. Inter-blade and intra-blade reproducibility were in the respective ranges of 5–13 and 3–10% relative standard deviation (RSD) for all model compounds. Limits of detection and quantitation of the proposed SPME-LC–MS/MS system for analysis of analytes were found to range from 0.1 to 1.0 and 0.5 to 3.0 μg L −1 , respectively. Standard addition calibration was applied for quantitative

Silica-based ionic liquid coating for 96-blade system for extraction of aminoacids from complex matrixes

Energy Technology Data Exchange (ETDEWEB)

Mousavi, Fatemeh; Pawliszyn, Janusz, E-mail: janusz@uwaterloo.ca

2013-11-25

Graphical abstract: -- Highlights: •Silica-based 1-vinyl-3-octadecylimidazolium bromide ionic liquid was synthesized and characterized. •The synthesized polymer was immobilized on the stainless steel blade using polyacrylonitrile glue. •SiImC{sub 18}-PAN 96-blade SPME was applied as an extraction phase for extraction of highly polar compounds in grape matrix. •This system provides high extraction efficiency and reproducibility for up to 50 extractions from tartaric buffer and 20 extractions from grape pulp. -- Abstract: 1-Vinyl-3-octadecylimidazolium bromide ionic liquid [C{sub 18}VIm]Br was prepared and used for the modification of mercaptopropyl-functionalized silica (Si-MPS) through surface radical chain-transfer addition. The synthesized octadecylimidazolium-modified silica (SiImC{sub 18}) was characterized by thermogravimetric analysis (TGA), infrared spectroscopy (IR), {sup 13}C NMR and {sup 29}Si NMR spectroscopy and used as an extraction phase for the automated 96-blade solid phase microextraction (SPME) system with thin-film geometry using polyacrylonitrile (PAN) glue. The new proposed extraction phase was applied for extraction of aminoacids from grape pulp, and LC–MS–MS method was developed for separation of model compounds. Extraction efficiency, reusability, linearity, limit of detection, limit of quantitation and matrix effect were evaluated. The whole process of sample preparation for the proposed method requires 270 min for 96 samples simultaneously (60 min preconditioning, 90 min extraction, 60 min desorption and 60 min for carryover step) using 96-blade SPME system. Inter-blade and intra-blade reproducibility were in the respective ranges of 5–13 and 3–10% relative standard deviation (RSD) for all model compounds. Limits of detection and quantitation of the proposed SPME-LC–MS/MS system for analysis of analytes were found to range from 0.1 to 1.0 and 0.5 to 3.0 μg L{sup −1}, respectively. Standard addition calibration was

Physical matrix correction for RFA of mass and special glasses

International Nuclear Information System (INIS)

Medicus, G.; Ritter, R.

1984-01-01

A theoretical matrix correction model with relatively complex mass absorption coefficients is reported, which takes into account the adsorption of the stimulating radiation and the radiation in the specimen to be measured, as well as the geometry of the spectrometer. With the realized concept of an effective primary wave length, good correction results were obtained over large regions of concentrations and elements. The computer program renders possible besides of the usual reference measurement at uniform reference wave length - the reference of several elements in the specimen to one special element of the reference specimen. The correction method was tested with 42 test glasses, which were previously analyzed. (author)

Borosilicate glass as a matrix for immobilization of SRP high-level waste

International Nuclear Information System (INIS)

Wicks, G.G.

1980-01-01

Approximately 22 million gallons of high-level radioactive defense waste are currently being stored in large underground tanks located on the Savannah River Plant (SRP) site in Aiken, South Carolina. One option now being considered for long-term management of this waste involves removing the waste from the tanks, chemically processing the waste, and immobilizing the potentially harmful radionuclides in the waste into a borosilicate glass matrix. The technology for producing waste glass forms is well developed and has been demonstrated on various scales using simulated as well as radioactive SRP waste. Recently, full-scale prototypical equipment has been made operational at SRP. This includes both a joule-heated ceramic melter and an in-can melter. These melters are a part of an integrated vitrification system which is under evaluation and includes a spray calciner, direct liquid feed apparatus, and various elements of an off-gas system. Two of the most important properties of the waste glass are mechanical integrity and leachability. Programs are in progress at SRL aimed at minimizing thermally induced cracking by carefully controlling cooling cycles and using ceramic liners or coatings. The leachability of SRP waste glass has been studied under many different conditions and consistently found to be low. For example, the leachability of actual SRP waste glass was found to be 10 -6 to 10 -5 g/(cm 2 )(day) initially and decreasing to 10 -9 to 10 -8 g/(cm 2 )(day) after 100 days. Waste glass is also being studied under anticipated storage conditions. In brine at 90 0 C, the leachability is about 5 x 10 -8 g/(cm 2 )(day) after 60 days. The effects of other geological media including granite, basalt, shale, and tuff are also being studied as part of the multibarrier isolation system

A study on the plasticity of soda-lime silica glass via molecular dynamics simulations

Science.gov (United States)

Urata, Shingo; Sato, Yosuke

2017-11-01

Molecular dynamics (MD) simulations were applied to construct a plasticity model, which enables one to simulate deformations of soda-lime silica glass (SLSG) by using continuum methods. To model the plasticity, stress induced by uniaxial and a variety of biaxial deformations was measured by MD simulations. We found that the surfaces of yield and maximum stresses, which are evaluated from the equivalent stress-strain curves, are reasonably represented by the Mohr-Coulomb ellipsoid. Comparing a finite element model using the constructed plasticity model to a large scale atomistic model on a nanoindentation simulation of SLSG reveals that the empirical method is accurate enough to evaluate the SLSG mechanical responses. Furthermore, the effect of ion-exchange on the SLSG plasticity was examined by using MD simulations. As a result, it was demonstrated that the effects of the initial compressive stress on the yield and maximum stresses are anisotropic contrary to our expectations.

Integrated modelling of the glass-iron-clay system

International Nuclear Information System (INIS)

Bildstein, O.

2007-01-01

This report summarizes the results of integrated calculations on the near-field evolution in the VHLW/steel/bentonite/clay system. The calculations of the near-field evolution include different components: the vitrified waste packages, the steel container, the bentonite-based EBS (optional), the EDZ and the geological medium. Coupled reaction-transport (X-T) is used to simulate the corrosion of the steel canister and the glass alteration phase in presence of corrosion products (CPs), looking at mass transfer for chemical elements, especially iron and silica, pH, and porosity change. Calculations as performed give actual parameters for PA calculations: rate of glass alteration (through the calculated pH) as a function of time, extension of altered zone for iron-clay interactions with their own transport parameters, nature of CPs, effect on porosity distribution. According to the operational model currently used at the CEA and the calculations performed on the glass-iron-clay system, the alteration rate of glass and the evolution of the system strongly depend on the timing of CPs saturation with respect to silica sorption. The fate of silica which can be sorbed or precipitate is crucial to the lifetime of glass and to the overall evolution of the system. The other process that might influence the glass is the porosity decrease due to the precipitation of CPs and silica rich phases. However, it is difficult to assign a safety functions to clogging. It is scarcely observed in experiments, either because the conditions are not met for clogging or because the timescale of experiments does not allow for observable clogging. Moreover, the effect of mechanical stress in the NF has to be accounted for in the assessment of the effect of porosity changes. (author)

Integrated modelling of the glass-iron-clay system

Energy Technology Data Exchange (ETDEWEB)

Bildstein, O

2007-01-15

This report summarizes the results of integrated calculations on the near-field evolution in the VHLW/steel/bentonite/clay system. The calculations of the near-field evolution include different components: the vitrified waste packages, the steel container, the bentonite-based EBS (optional), the EDZ and the geological medium. Coupled reaction-transport (X-T) is used to simulate the corrosion of the steel canister and the glass alteration phase in presence of corrosion products (CPs), looking at mass transfer for chemical elements, especially iron and silica, pH, and porosity change. Calculations as performed give actual parameters for PA calculations: rate of glass alteration (through the calculated pH) as a function of time, extension of altered zone for iron-clay interactions with their own transport parameters, nature of CPs, effect on porosity distribution. According to the operational model currently used at the CEA and the calculations performed on the glass-iron-clay system, the alteration rate of glass and the evolution of the system strongly depend on the timing of CPs saturation with respect to silica sorption. The fate of silica which can be sorbed or precipitate is crucial to the lifetime of glass and to the overall evolution of the system. The other process that might influence the glass is the porosity decrease due to the precipitation of CPs and silica rich phases. However, it is difficult to assign a safety functions to clogging. It is scarcely observed in experiments, either because the conditions are not met for clogging or because the timescale of experiments does not allow for observable clogging. Moreover, the effect of mechanical stress in the NF has to be accounted for in the assessment of the effect of porosity changes. (author)

Preparation of EVA/silica nano composites characterized with solid state nuclear magnetic resonance; Obtencao de nanocomposito de EVA/SILICA e caracterizacao por ressonancia magnetica nuclear no estado solido

Energy Technology Data Exchange (ETDEWEB)

Passos, Adriano A; Tavares, Maria I.B.; Neto, Roberto C.P.; Moreira, Leonardo A; Ferreira, Antonio G., E-mail: mibt@ima.ufrj.br [Centro de Tecnologia, Instituto de Macromoleculas Professora Eloisa Mano, Universidade Federal do Rio de Janeiro, Rio de Janeiro, RJ (Brazil)

2011-07-01

Nano composites of poly(ethylene-co-vinyl acetate)/silica (SiO{sub 2}) with dimensions of ca. 40 nm were prepared via solution intercalation employing chloroform as a solvent. They were mainly characterized with nuclear magnetic resonance spectroscopy (NMR) employing carbon-13 (polymeric matrix), silicon-29 (nanoparticles) and through the determination of the proton spin-lattice relaxation time in the rotating frame (T{sub 1{rho}H}) (polymer matrix). From the NMR results it was inferred that up to 5% of silica in mass a well dispersed nano composite was obtained, owing to a strong interaction between silica and the EVA matrix. (author)

Study of a new glass matrix by the thermoluminescence technique; Estudo de uma nova matriz vitrea pela tecnica de termoluminescencia

Energy Technology Data Exchange (ETDEWEB)

Ferreira, Pamela Z.; Vedovato, Uly P.; Cunha, Diego M. da; Dantas, Noelio O.; Silva, Anielle C.A.; Neves, Lucio P.; Perini, Ana P., E-mail: anapaula.perini@ufu.br [Universidade Federal de Uberlandia (INFIS/UFU), MG (Brazil). Instituto de Fisica; Caldas, Linda V.E. [Instituto de Pesquisas Energeticas e Nucleares (IPEN/CNEN-SP), Sao Paulo, SP (Brazil); Carrera, Betzabel N.S.; Watanabe, Shigueo [Universidade de Sao Paulo (IF/USP), Sao Paulo, SP (Brazil). Instituto de Fisica

2015-07-01

The thermoluminescence technique is widely used for both personal and for high-dose dosimetry. In this work, the thermoluminescence technique was utilized to study a new glass matrix, with nominal composition of 20Li{sub 2}CO{sub 3}.10Al{sub 2}O{sub 3}.20BaO.50B{sub 2}O{sub 3} (mol%), irradiated with different doses in a {sup 60}Co source. The glow curves and the dose-response curve were obtained for radiation doses between 50 Gy and 900 Gy. The results showed that this new glass matrix presents potential use in high-dose dosimetry. (author)

A general model for the dissolution of nuclear waste glasses in salt brine

International Nuclear Information System (INIS)

McGrail, B.P.; Strachan, D.M.

1988-07-01

A mechanistic model describing a dynamic mass balance between the production and consumption of dissolved silica was found to describe the dissolution of SRL-165 defense waste glass in a high-magnesium (PBB3) brine at a temperature of 90/degree/C. The synergetic effect of the waste package container on the glass dissolution rate was found to depend on a precipitation reaction for a ferrous silicate mineral. The model predicted that the ferrous silicate precipitate should be variable in composition where the iron-silica ratio depended on the metal-to-glass surface area ratio used in the experiment. This prediction was confirmed experimentally by the variable iron-silica ratios observed in filtered leachates. However, the interaction between dissolved silica and iron corrosion products needs to be much better understood before the model could be used with confidence in predicting radionuclide release rates for a salt repository. If the deleterious effects of the iron corrosion products can be shown to be transient, and the fracturing of the glass can be minimized, it appears that the performance of SRL-165 defense waste glass will be near the NRC regulatory criterion for fraction release of one part in 100,000 in PBB3 brine at 90/degree/C under silica-saturated conditions. 47 refs., 6 figs., 1 tab

Numerical modelling of glass dissolution: gel layer morphology

Energy Technology Data Exchange (ETDEWEB)

Devreux, F. E-mail: fd@pmc.polytechnique.fr; Barboux, P

2001-09-01

Numerical simulations of glass dissolution are presented. The glass is modelized as a random binary mixture composed of two species representing silica and soluble oxides, such as boron and alkali oxides. The soluble species are dissolved immediately when they are in contact with the solution. For the species which represents silica, one introduces dissolution and condensation probabilities. It is shown that the morphology and the thickness of the surface hydration layer (the gel) are highly dependent on the dissolution model, especially on the parameter which controls the surface tension. Simulations with different glass surface area to solution volume ratio (S/V) show that this experimental parameter has important effects on both the shrinkage and the gel layer thickness.

Sol–gel glass-ceramics comprising rare-earth doped SnO2 and LaF3 nanocrystals: an efficient simultaneous UV and IR to visible converter

International Nuclear Information System (INIS)

Yanes, A. C.; Castillo, J. del; Méndez-Ramos, J.; Rodríguez, V. D.

2011-01-01

We report a novel class of nanostructured glass-ceramics comprising two co-existing rare-earth doped nanocrystalline phases, SnO 2 semiconductor nanocrystal (quantum dot), and LaF 3 , presenting sizes at around 4.6 and 9.8 nm, respectively, embedded into a silica glass matrix for an efficient simultaneous UV and IR to visible photon conversion. On one hand, the wide and strong UV absorption by SnO 2 quantum dot and subsequent efficient energy transfer to Eu 3+ and, on the other hand, the also very efficient IR to visible up-conversion with the pair Yb 3+ –Er 3+ partitioned into low phonon LaF 3 nanocrystalline environment, yield to visible emissions with application in improving the spectral response of photovoltaic solar cells.Graphical AbstractWe report a novel class of nanostructured glass-ceramics comprising two co-existing rare-earth doped nanocrystalline phases, SnO 2 semiconductor nanocrystal (quantum dot) and LaF 3 , presenting sizes at around 4.6 and 9.8 nm, respectively, embedded into a silica glass matrix for an efficient simultaneous UV and IR to visible photon conversion. On one hand, the wide and strong UV absorption by SnO 2 quantum dot and subsequent efficient energy transfer to Eu 3+ and, on the other hand, the also very efficient IR to visible up-conversion with the pair Yb 3+ –Er 3+ partitioned into low phonon LaF 3 nanocrystalline environment, yield to visible emissions with application in improving the spectral response of photovoltaic solar cells.

High-quality substrate for fluorescence enhancement using agarose-coated silica opal film.

Science.gov (United States)

Xu, Ming; Li, Juan; Sun, Liguo; Zhao, Yuanjin; Xie, Zhuoying; Lv, Linli; Zhao, Xiangwei; Xiao, Pengfeng; Hu, Jing; Lv, Mei; Gu, Zhongze

2010-08-01

To improve the sensitivity of fluorescence detection in biochip, a new kind of substrates was developed by agarose coating on silica opal film. In this study, silica opal film was fabricated on glass substrate using the vertical deposition technique. It can provide stronger fluorescence signals and thus improve the detection sensitivity. After coating with agarose, the hybrid film could provide a 3D support for immobilizing sample. Comparing with agarose-coated glass substrate, the agarose-coated opal substrates could selectively enhance particular fluorescence signals with high sensitivity when the stop band of the silica opal film in the agarose-coated opal substrate overlapped the fluorescence emission wavelength. A DNA hybridization experiment demonstrated that fluorescence intensity of special type of agarose-coated opal substrates was about four times that of agarose-coated glass substrate. These results indicate that the optimized agarose-coated opal substrate can be used for improving the sensitivity of fluorescence detection with high quality and selectivity.

Crystallization kinetics of a soda lime silica glass with TiO2 addition

International Nuclear Information System (INIS)

De la Parra A, S. M.; Alvarez M, A.; Torres G, L. C.; Sanchez, E. M.

2009-01-01

Studies conducted into Na 2 O-CaO-3SiO 2 glass composition suggest that its phase transformation occurs from the surface towards the interior of the sample. In a study carried out in 1982, it was reported that no addition of nucleating agents modified the mechanism. Taking advantage of the disposition materials synthesized by nanotechnology, in this study TiO 2 in nanometer size was used with the idea that, because of its qualities, it could modify the crystallization mechanism. The glasses obtained as well as the thermally treated samples, were evaluated by the X-ray diffraction (XRD) powder method, differential thermal analysis (DTA), and by optical microscopy and high resolution transmission electron microscopy (HRTEM). Within the range of TiO 2 concentration studied (0 - 10 wt %), 10 wt % of TiO 2 considerably reduced the Na 2 O-2CaO-3SiO 2 phase crystallization process. The crystallization mechanism was not modified and TiO 2 did not form compounds with the matrix components. (Author)

Heat Transfer Modelling of Glass Media within TPV Systems

Science.gov (United States)

Bauer, Thomas; Forbes, Ian; Penlington, Roger; Pearsall, Nicola

2004-11-01

Understanding and optimisation of heat transfer, and in particular radiative heat transfer in terms of spectral, angular and spatial radiation distributions is important to achieve high system efficiencies and high electrical power densities for thermophtovoltaics (TPV). This work reviews heat transfer models and uses the Discrete Ordinates method. Firstly one-dimensional heat transfer in fused silica (quartz glass) shields was examined for the common arrangement, radiator-air-glass-air-PV cell. It has been concluded that an alternative arrangement radiator-glass-air-PV cell with increased thickness of fused silica should have advantages in terms of improved transmission of convertible radiation and enhanced suppression of non-convertible radiation.

Kinetics of silica-phase transitions

International Nuclear Information System (INIS)

Duffy, C.J.

1993-07-01

In addition to the stable silica polymorph quartz, several metastable silica phases are present in Yucca Mountain. The conversion of these phases to quartz is accompanied by volume reduction and a decrease in the aqueous silica activity, which may destabilize clinoptilolite and mordenite. The primary reaction sequence for the silica phases is from opal or glass to disordered opal-CT, followed by ordering of the opal-CT and finally by the crystallization of quartz. The ordering of opal-CT takes place in the solid state, whereas the conversion of opal-CT takes place through dissolution-reprecipitation involving the aqueous phase. It is proposed that the rate of conversion of opal-CT to quartz is controlled by diffusion of defects out of a disordered surface layer formed on the crystallizing quartz. The reaction rates are observed to be dependent on temperature, pressure, degree of supersaturation, and pH. Rate equations selected from the literature appear to be consistent with observations at Yucca Mountain

Effect of the glass transition temperature on alpha-amylase activity in a starch matrix.

Science.gov (United States)

Chaudhary, Vinita; Panyoyai, Naksit; Small, Darryl M; Shanks, Robert A; Kasapis, Stefan

2017-02-10

This study optimises a protocol for the estimation of α-amylase activity in a condensed starch matrix in the vicinity of the glass transition region. Enzymatic activity on the vitrified starch system was compared with that of a reference substrate, maltodextrin. The activity was assayed as the rate of release of reducing sugar using a dinitrosalicylic acid procedure. The condensed carbohydrate matrices served the dual purpose of acting as a substrate as well as producing a pronounced effect on the ability to enzymatic hydrolysis. Activation energies were estimated throughout the glass transition region of condensed carbohydrate preparations based on the concept of the spectroscopic shift factor. Results were used to demonstrate a considerable moderation by the mechanical glass transition temperature, beyond the expected linear effect of the temperature dependence, on the reaction rate of starch hydrolysis by α-amylase in comparison with the low-molecular weight chain of maltodextrin. Copyright © 2016. Published by Elsevier Ltd.

Direct writing of birefringent elements by ultrafast laser nanostructuring in multicomponent glass

Science.gov (United States)

Fedotov, S. S.; Drevinskas, R.; Lotarev, S. V.; Lipatiev, A. S.; Beresna, M.; ČerkauskaitÄ--, A.; Sigaev, V. N.; Kazansky, P. G.

2016-02-01

Self-assembled nanostructures created by femtosecond laser irradiation are demonstrated in alkali-free aluminoborosilicate glass. The growth of the induced retardance associated with the nanograting formation is three orders of magnitude slower than in silica glass and is observed only within a narrow range of pulse energies. However, the strength of retardance asymptotically approaches the value typically measured in pure silica glass, which is attractive for practical applications. A similar intensity threshold for nanograting formation of about 1 TW/cm2 is observed for all glasses studied. The radially polarized vortex beam micro-converter designed as a space-variant quarter-wave retarder for the near-infrared spectral range is imprinted in commercial Schott AF32 glass.

Glasses obtained from industrial wastes

International Nuclear Information System (INIS)

Bortoluzzi, D.; Oliveira Fillho, J.; Uggioni, E.; Bernardin, A.M.

2009-01-01

This paper deals with the study of the vitrification mechanism as an inertization method for industrial wastes contaminated with heavy metals. Ashes from coal (thermoelectric), wastes from mining (fluorite and feldspar) and plating residue were used to compose vitreous systems planed by mixture design. The chemical composition of the wastes was determined by XRF and the formulations were melted at 1450 deg C for 2h using 10%wt of CaCO 3 (fluxing agent). The glasses were poured into a mold and annealed (600 deg C). The characteristic temperatures were determined by thermal analysis (DTA, air, 20 deg C/min) and the mechanical behavior by Vickers microhardness. As a result, the melting temperature is strongly dependent on silica content of each glass, and the fluorite residue, being composed mainly by silica, strongly affects Tm. The microhardness of all glasses is mainly affected by the plating residue due to the high iron and zinc content of this waste. (author)

Phase formation during corrosion experiments with two simulated borosilicate nuclear waste glasses

International Nuclear Information System (INIS)

Haaker, R.F.

1985-10-01

Corrosion products resulting from the reaction of simulated high-level radioactive waste glasses with various solutions have been identified. At 200degC, in saturated NaCl, a degree of reaction of 10 g C31-3 glass or 2.6 g SON 68 glass per liter of solution was obtained. Analcime, vermiculite (a phyllosilicate) and a 2:1 zinc silicate are the major silica containing alteration products for the C31-3 glass. Analcime was the only silicate alteration product which could be identified for SON 68 glass. C31-3 glass appeared to be less reactive with a quinary brine containing Mg ++ than with NaCl. With the quinary brine, montmorillonite (a phyllosilicate) was the predominant silica containing alteration product. Hydrotalcite (a Mg-Al hydroxysulfate) and montmorillonite were the major Al-containing phases. A phyllosilicate, probably montmorillonite, was observed to form during the reaction of SON 68 glass with quinary brine. With either glass, modified NaCl brines which contained small amounts of MgCl 2 seem to have the effect of decreasing the amount of analcime and increasing the amount of phyllosilicate which is formed. In the case of C31-3 glass, there is approximately enough Mg, Al and Zn to precipitate most of the leached Si; measured Si concentrations remain well below that expected for amorphous silica. SON 68 glass has less Zn, Al and Mg than C31-3 glass and much higher Si concentrations of the leachates. (orig./RB)

Zirconium based bulk metallic glasses

International Nuclear Information System (INIS)

Dey, G.K.; Neogy, S.; Savalia, R.T.; Tewari, R.; Srivastava, D.; Banerjee, S.

2006-01-01

Metallic glasses have come into prominence in recent times because their nanocrystalline atomic arrangement imparts many useful and unusual properties to these metallic solids. In this study, bulk glasses have been obtained in Zr based multicomponent alloy by induction melting these alloys in silica crucibles and casting these in form of rods 3 and 6 mm in diameter in a copper mould

Effect of magnesium aluminum silicate glass on the thermal shock resistance of BN matrix composite ceramics

NARCIS (Netherlands)

Cai, Delong; Jia, Dechang; Yang, Zhihua; Zhu, Qishuai; Ocelik, Vaclav; Vainchtein, Ilia D.; De Hosson, Jeff Th M.; Zhou, Yu

The effects of magnesium aluminum silicate (MAS) glass on the thermal shock resistance and the oxidation behavior of h-BN matrix composites were systematically investigated at temperature differences from 600 degrees C up to 1400 degrees C. The retained strength rate of the composites rose with the

Silica scintillating materials prepared by sol-gel methods

International Nuclear Information System (INIS)

Werst, D.W.; Sauer, M.C. Jr.; Cromack, K.R.; Lin, Y.; Tartakovsky, E.A.; Trifunac, A.D.

1993-01-01

Silica was investigated as a rad-hard alternative to organic polymer hosts for organic scintillators. Silica sol-gels were prepared by hydrolysis of tetramethoxysilane in alcohol solutions. organic dyes were incorporated into the gels by dissolving in methanol at the sol stage of gel formation. The silica sol-gel matrix is very rad-hard. The radiation stability of silica scintillators prepared by this method is dye-limited. Transient radioluminescence was measured following excitation with 30 ps pulses of 20 MeV electrons

Enhanced emission of nile red fluorescent nanoparticles embedded in hybrid sol-gel glasses.

Science.gov (United States)

Ferrer, Maria L; del Monte, Francisco

2005-01-13

Highly fluorescent Nile Red (NR) nanoparticles embedded in a hybrid sol-gel glass are reported. The crystallite growth within the confined system created by the porous hybrid matrix results in NR nanoparticles of averaged dimensions below 36 nm. The preparation process allows for the control of both the conformation adopted by single NR molecules prior to aggregation (e.g., near planar) and the configuration of the aggregates (e.g., oblique with phi architecture which ultimately forms the nanoparticles. The full preservation of the fluorescent configuration of the aggregates in the nanoparticles is confirmed through the application of the exciton theory, and it is responsible for the significant increase of the fluorescence emission intensity (e.g., up to 525- and 70-fold as compared to that obtained for single NR molecules embedded in pure and hybrid silica glasses, respectively).

Enhancing Hydrogen Diffusion in Silica Matrix by Using Metal Ion Implantation to Improve the Emission Properties of Silicon Nanocrystals

Directory of Open Access Journals (Sweden)

J. Bornacelli

2014-01-01

Full Text Available Efficient silicon-based light emitters continue to be a challenge. A great effort has been made in photonics to modify silicon in order to enhance its light emission properties. In this aspect silicon nanocrystals (Si-NCs have become the main building block of silicon photonic (modulators, waveguide, source, and detectors. In this work, we present an approach based on implantation of Ag (or Au ions and a proper thermal annealing in order to improve the photoluminescence (PL emission of Si-NCs embedded in SiO2. The Si-NCs are obtained by ion implantation at MeV energy and nucleated at high depth into the silica matrix (1-2 μm under surface. Once Si-NCs are formed inside the SiO2 we implant metal ions at energies that do not damage the Si-NCs. We have observed by, PL and time-resolved PL, that ion metal implantation and a subsequent thermal annealing in a hydrogen-containing atmosphere could significantly increase the emission properties of Si-NCs. Elastic Recoil Detection measurements show that the samples with an enhanced luminescence emission present a higher hydrogen concentration. This suggests that ion metal implantation enhances the hydrogen diffusion into silica matrix allowing a better passivation of surface defects on Si NCs.

Phosphate-core silica-clad Er/Yb-doped optical fiber and cladding pumped laser.

Science.gov (United States)

Egorova, O N; Semjonov, S L; Velmiskin, V V; Yatsenko, Yu P; Sverchkov, S E; Galagan, B I; Denker, B I; Dianov, E M

2014-04-07

We present a composite optical fiber with a Er/Yb co-doped phosphate-glass core in a silica glass cladding as well as cladding pumped laser. The fabrication process, optical properties, and lasing parameters are described. The slope efficiency under 980 nm cladding pumping reached 39% with respect to the absorbed pump power and 28% with respect to the coupled pump power. Due to high doping level of the phosphate core optimal length was several times shorter than that of silica core fibers.

Fabrication of 3D solenoid microcoils in silica glass by femtosecond laser wet etch and microsolidics

Science.gov (United States)

Meng, Xiangwei; Yang, Qing; Chen, Feng; Shan, Chao; Liu, Keyin; Li, Yanyang; Bian, Hao; Du, Guangqing; Hou, Xun

2015-02-01

This paper reports a flexible fabrication method for 3D solenoid microcoils in silica glass. The method consists of femtosecond laser wet etching (FLWE) and microsolidics process. The 3D microchannel with high aspect ratio is fabricated by an improved FLWE method. In the microsolidics process, an alloy was chosen as the conductive metal. The microwires are achieved by injecting liquid alloy into the microchannel, and allowing the alloy to cool and solidify. The alloy microwires with high melting point can overcome the limitation of working temperature and improve the electrical property. The geometry, the height and diameter of microcoils were flexibly fabricated by the pre-designed laser writing path, the laser power and etching time. The 3D microcoils can provide uniform magnetic field and be widely integrated in many magnetic microsystems.

Facing slag glass and slag glass ceramic produced from thermal power plant ash

Energy Technology Data Exchange (ETDEWEB)

Buruchenko, A.E.; Kolesnikov, A.A.; Lukoyanov, A.G.

1990-10-01

Evaluates properties of fly ash and slags from the Krasnoyarsk coal-fired power plants and their utilization for glass and ceramic glass production. Composition of a mixture of fly ash and slag was: silica 40-55%, aluminium oxides 10-40%, ferric trioxide 6-14%, calcium oxides 20-35%, magnesium oxides 3-6%, potassium oxides 0.3-1.5%, sodium oxides 0.2-05%, sulfur trioxide 0.9-5.0%. The analyzed fly ash and slags from the Krasnoyarsk plant were an economic waste material for glass production. Properties of sand, clay and other materials used in glass production and properties of glass and ceramic glass produced on the basis of fly ash and slags are analyzed. Economic aspects of fly ash and slag utilization are also evaluated. 3 refs.

A Study on Silica Sand Quality in Yazaram and Mugulbu Deposits ...

African Journals Online (AJOL)

The suitability of silica sand deposits of Yazaram and Mugulbu in Mubi South Local Government Area of Adamawa State, Nigeria for commercial glass production were assessed based on the chemical and physical properties of the silica sand samples collected along the river side's. Test was carried out at the National ...

Fluorescence metrology of silica sol–gels – The effect of D2O and ...

Indian Academy of Sciences (India)

Administrator

industrial quality control and helping fundamental research. ... Of all the possible syntheses, sodium silicate (i.e. water glass) production of silica gel, ... fine silica gel powders used in many applications (e.g. chromatography, toothpaste etc).

Evaluation of the glow curves of a new glass matrix; Avaliação das curvas de emissão termoluminescente de uma nova matriz vítrea

Energy Technology Data Exchange (ETDEWEB)

Oliveira, Nathália S.; Souza, Samara P.; Ferreira, Pâmela Z.; Dantas, Noelio O.; Silva, Anielle C.A.; Neves, Lucio P.; Perini, Ana P., E-mail: anapaula.perini@ufu.br [Universidade Federal de Uberlândia (INFIS/UFU), Uberlândia, MG (Brazil). Instituto de Física; Caldas, Linda V.E. [Instituto de Pesquisas Energéticas e Nucleares (IPEN/CNEN-SP), São Paulo, SP (Brazil); Carrera, Betzabel N.S.; Watanabe, Shigueo [Universidade de São Paulo (IF/USP), São Paulo, SP (Brazil). Instituto de Física

2017-07-01

Thermoluminescence is a dosimetric technique with may be used to personal, clinical, environmental and high doses. In this work a new glass matrix, with nominal composition of 20Li{sub 2}CO{sub 3}.10Al{sub 2}O{sub 3}.25BaO.45B{sub 2}O{sub 3} (mol%), was studied by the thermoluminescence technique. The glow curves was be analyzed, after the irradiation of this glass matrix with high doses. The results showed that this new glass matrix has a temperature peak in 260°C, which is ideal for dosimetry applications. (author)

The interaction of encapsulated pharmaceutical drugs with a silica matrix.

Science.gov (United States)

Morais, Everton C; Correa, Gabriel G; Brambilla, Rodrigo; Radtke, Claudio; Baibich, Ione Maluf; dos Santos, João Henrique Z

2013-03-01

A series of seven drugs, namely, fluoxetine, gentamicin, lidocaine, morphine, nifedipine, paracetamol and tetracycline, were encapsulated. The encapsulated systems were characterized using a series of complementary techniques: Fourier-transform infrared spectroscopy (FT-IR), diffusive reflectance spectroscopy in the UV-vis region (DRS) and X-ray photoelectron spectroscopy (XPS). According to the DRS spectra, most of the encapsulated systems showed a band shift of the maximum absorption when compared with the corresponding bare pharmaceutical. Additionally, after encapsulation, the drugs exhibited infrared band shifts toward higher wavenumbers, which in turn provided insight into potential sites for interaction with the silica framework. The amine group showed a band shift in the spectra of almost all the drugs (except nifedipine and tetracycline). This finding indicates the possibility of a hydrogen bonding interaction between the drug and the silica via electron donation from the amine group to the silica framework. XPS confirmed this interaction between the pharmaceuticals and the silica through the amine group. A correlation was observed between the textural characteristics of the solids and the spectroscopic data, suggesting that the amine groups from the pharmaceuticals were more perturbed upon encapsulation. Copyright © 2012 Elsevier B.V. All rights reserved.

Investigating in vitro bioactivity and magnetic properties of the ferrimagnetic bioactive glass–ceramic fabricated using soda-lime–silica waste glass

Energy Technology Data Exchange (ETDEWEB)

Abbasi, M. [Department of Materials Science and Engineering, School of Engineering, Shiraz University, Zand Street, Shiraz (Iran, Islamic Republic of); Hashemi, B., E-mail: hashemib@shirazu.ac.ir [Department of Materials Science and Engineering, School of Engineering, Shiraz University, Zand Street, Shiraz (Iran, Islamic Republic of); Shokrollahi, H. [Electroceramics Group, Materials Science and Engineering Department, Shiraz University of Technology, Shiraz (Iran, Islamic Republic of)

2014-04-01

The main purpose of the current research is the production and characterization of a ferrimagnetic bioactive glass–ceramic prepared through the solid-state reaction method using soda-lime–silica waste glass as the main raw material. In comparison with the conventional route, that is, the melt-quenching and subsequent heat treatment, the present work is an economical technique. Structural, thermal and magnetic properties of the samples were examined by X-ray diffraction (XRD), differential thermal analysis (DTA) and vibrating sample magnetometer (VSM). The in vitro test was utilized to assess the bioactivity level of the samples by Hanks' solution as simulated body fluid (SBF). The apatite surface layer formation was examined by the scanning electron microscopy (SEM) equipped with energy dispersive spectroscopy (EDS). The calcium ion concentration in the solutions was measured by atomic absorption spectroscopy (AAS). VSM results revealed that with the addition of 5–20 wt% strontium hexaferrite to bioactive glass–ceramics, the ferrimagnetic bioactive glass–ceramics with hysteresis losses between 7024 and 75,852 erg/g were obtained. The in vitro test showed that the onset formation time of hydroxyapatite layer on the surface of the samples was 14 days and after 30 days, this layer was completed. - Highlights: • A novel ferrimagnetic bioactive glass–ceramic was synthesized by an incorporation method. • The bioactive part was synthesized by the solid-state reaction method using soda-lime–silica waste glass. • The doping of SrFe{sub 12}O{sub 19} to Bioglass{sup ®} 45S5 glass–ceramic is likely to decrease bioactivity.

Environmentally responsive surface-modified silica nanoparticles for enhanced oil recovery

International Nuclear Information System (INIS)

Behzadi, Abed; Mohammadi, Aliasghar

2016-01-01

Environmentally responsive surface-modified nanoparticles are colloidal nanoparticles coated with, at least, two physicochemically distinct surface groups. Recent advances in the synthesis and production of nanoparticles have enabled the production of environmentally responsive surface-modified nanoparticles with both hydrophilic and hydrophobic surface groups. These nanoparticles act like colloidal surfactants. In this paper, environmentally responsive surface-modified silica nanoparticles are synthesized and used for enhancement of oil recovery. For this purpose, silica nanoparticles are coated with polyethylene glycol chains as hydrophilic agent and propyl chains as hydrophobic agent at various quantities, and their ability to modulate oil–water interface properties and oil recovery is examined. Oil–water interfacial tension and water surface tension are decreased by 50 % in the presence of silica nanoparticles coated with both agents. Measuring oil-drop contact angle on oil-wetted glass slides and carbonate rock sections, after aging in various surface-modified silica nanofluids, indicates that the wettability of various oil-wetted surfaces is modified from strongly oil-wet to water-wet. Flooding nanofluids to glass micro-models and pore-level investigations demonstrate that surface modification of silica nanoparticles, specially, with both hydrophilic and hydrophobic agents improves considerably their performance in increasing oil recovery and wettability alteration.

Environmentally responsive surface-modified silica nanoparticles for enhanced oil recovery

Energy Technology Data Exchange (ETDEWEB)

Behzadi, Abed; Mohammadi, Aliasghar, E-mail: amohammadi@sharif.edu [Sharif University of Technology, Department of Chemical and Petroleum Engineering (Iran, Islamic Republic of)

2016-09-15

Environmentally responsive surface-modified nanoparticles are colloidal nanoparticles coated with, at least, two physicochemically distinct surface groups. Recent advances in the synthesis and production of nanoparticles have enabled the production of environmentally responsive surface-modified nanoparticles with both hydrophilic and hydrophobic surface groups. These nanoparticles act like colloidal surfactants. In this paper, environmentally responsive surface-modified silica nanoparticles are synthesized and used for enhancement of oil recovery. For this purpose, silica nanoparticles are coated with polyethylene glycol chains as hydrophilic agent and propyl chains as hydrophobic agent at various quantities, and their ability to modulate oil–water interface properties and oil recovery is examined. Oil–water interfacial tension and water surface tension are decreased by 50 % in the presence of silica nanoparticles coated with both agents. Measuring oil-drop contact angle on oil-wetted glass slides and carbonate rock sections, after aging in various surface-modified silica nanofluids, indicates that the wettability of various oil-wetted surfaces is modified from strongly oil-wet to water-wet. Flooding nanofluids to glass micro-models and pore-level investigations demonstrate that surface modification of silica nanoparticles, specially, with both hydrophilic and hydrophobic agents improves considerably their performance in increasing oil recovery and wettability alteration.

Raman band intensities of tellurite glasses.

Science.gov (United States)

Plotnichenko, V G; Sokolov, V O; Koltashev, V V; Dianov, E M; Grishin, I A; Churbanov, M F

2005-05-15

Raman spectra of TeO2-based glasses doped with WO3, ZnO, GeO2, TiO2, MoO3, and Sb2O3 are measured. The intensity of bands in the Raman spectra of MoO3-TeO2 and MoO3-WO3-TeO2 glasses is shown to be 80-95 times higher than that for silica glass. It is shown that these glasses can be considered as one of the most promising materials for Raman fiber amplifiers.

Silica gel matrix immobilized Chlorophyta hydrodictyon africanum ...

African Journals Online (AJOL)

Aghomotsegin

2015-08-05

Aug 5, 2015 ... The algae-silica gel adsorbent was used for batch sorption studies of a cationic dye, ... traditional methods of treating industrial effluent, these ... Author(s) agree that this article remains permanently open access under the terms of the Creative ... sodium silicate solution (v/v) and 25 mL of distilled water. With.

Synthesize and characterization of a novel anticorrosive cobalt ferrite nanoparticles dispersed in silica matrix (CoFe2O4-SiO2) to improve the corrosion protection performance of epoxy coating

International Nuclear Information System (INIS)

Gharagozlou, M.; Ramezanzadeh, B.; Baradaran, Z.

2016-01-01

Highlights: • An anticorrosive cobalt ferrite nanopigment dispersed in silica matrix was synthesized. • The nanopigment showed proper inhibition performance in solution study. • The nanopigment significantly improved the corrosion resistance of the epoxy coating. - Abstract: This study aimed at studying the effect of an anticorrosive nickel ferrite nanoparticle dispersed in silica matrix (NiFe 2 O 4 -SiO 2 ) on the corrosion protection properties of steel substrate. NiFe 2 O 4 and NiFe 2 O 4 -SiO 2 nanopigments were synthesized and then characterized by X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FT-IR) and transmission electron microscope (TEM). Then, 1 wt.% of nanopigments was dispersed in an epoxy coating and the resultant nanocomposites were applied on the steel substrates. The corrosion inhibition effects of nanopigments were tested by an electrochemical impedance spectroscopy (EIS) and salt spray test. Results revealed that dispersing nickel ferrite nanoparticles in a silica matrix (NiFe 2 O 4 -SiO 2 ) resulted in the enhancement of the nanopigment dispersion in the epoxy coating matrix. Inclusion of 1 wt.% of NiFe 2 O 4 -SiO 2 nanopigment into the epoxy coating enhanced its corrosion protection properties before and after scratching.

Study of silica sol-gel materials for sensor development

Science.gov (United States)

Lei, Qiong

Silica sol-gel is a transparent, highly porous silicon oxide glass made at room temperature by sol-gel process. The name of silica sol-gel comes from the observable physical phase transition from liquid sol to solid gel during its preparation. Silica sol-gel is chemically inert, thermally stable, and photostable, it can be fabricated into different desired shapes during or after gelation, and its porous structure allows encapsulation of guest molecules either before or after gelation while still retaining their functions and sensitivities to surrounding environments. All those distinctive features make silica sol-gel ideal for sensor development. Study of guest-host interactions in silica sol-gel is important for silica-based sensor development, because it helps to tailor local environments inside sol-gel matrix so that higher guest loading, longer shelf-life, higher sensitivity and faster response of silica gel based sensors could be achieved. We focused on pore surface modification of two different types of silica sol-gel by post-grafting method, and construction of stable silica hydrogel-like thin films for sensor development. By monitoring the mobility and photostability of rhodamine 6G (R6G) molecules in silica alcogel thin films through single molecule spectroscopy (SMS), the guest-host interactions altered by post-synthesis grafting were examined. While physical confinement remains the major factor that controls mobility in modified alcogels, both R6G mobility and photostability register discernable changes after surface charges are respectively reversed and neutralized by aminopropyltriethoxysilane (APTS) and methyltriethoxysilane (MTES) grafting. The change in R6G photostability was found to be more sensitive to surface grafting than that of mobility. In addition, silica film modification by 0.4% APTS is as efficient as that by pure MTES in lowering R6G photostability, which suggests that surface charge reversal is more effective than charge neutralization

Phase boundary effects in metal matrix embedded glasses

International Nuclear Information System (INIS)

Schiewer, E.

1979-01-01

An investigation was performed to study reactions at the phase boundaries of glass-lead composites at temperatures up to the softening point of the glass. Some metal was oxidized at the boundary and penetrated into the glass. Solid-state diffusion was rate controlling. In the case of a phosphate glass, fission products were depleted in the boundary area. Molybdenum migrated into the lead, and cesium migrated into the glass core. 2 figures, 3 tables

Assessment of thermal shock induced damage in silicon carbide fibre reinforced glass matrix composites

Directory of Open Access Journals (Sweden)

Boccaccini, A. R.

1998-09-01

Full Text Available The development of microstructural damage in silicon carbide fibre (Nicalon™ reinforced glass matrix composite samples subjected to thermal shock was investigated by using a nondestructive forced resonance technique and fibre push out indentation tests. Thermal shock testing involved quenching samples in a water bath maintained at room temperature from a high temperature (650ºC. Changes in the Young's modulus and internal friction of the samples with increasing number of shocks were measured accurately by the forced resonance technique. Fibre push-out tests showed no significant changes in the properties of the fibre-matrix interface, indicating that damage in the composite was concentrated mainly in the development of matrix microcracking. It was also shown that the internal friction is a very sensitive parameter by which to detect the onset and development of such microcracking. A simple semi-empirical model is proposed to correlate the internal friction level with the microcracking density in the glass matrix. Finally, the relevance of detecting nondestructively the existence of microcracks in the glass matrix, before any significant interfacial degradation occurs, is emphasized, in conextion with the possibility of inducing a crack healing process by a thermal treatment (annealing, taking advantage of the viscous flow properties of the glass.

El desarrollo de daño microestructural en materiales compuestos de matriz de vidrio reforzados con fibras de carburo de silicio (Nicalon™ sometidos a choque térmico fue investigado mediante la técnica no-destructiva de resonancia forzada y por mediciones de indentación "push-out" de fibras. Los ensayos de choque térmico involucraron el enfriamiento brusco en un baño de agua a temperatura ambiente de las piezas previamente calentadas a una temperatura elevada (650ºC. La técnica de resonancia forzada permitió medir cambios en el módulo de Young de elasticidad y en la fricci

Evaluation of optical properties of the amorphous carbon film on fused silica

International Nuclear Information System (INIS)

Baydogan, Nilguen Dogan

2004-01-01

Deposition was done using a pulsed filtered cathodic arc with a graphite cathode. The carbon plasma is fully ionised and condenses on the substrate, forming diamond-like material but with amorphous structure. Optical properties of amorphous carbon films on fused-silica glass were investigated and the curves of optical density have a characteristic band at approximately 950 nm. Changes of the colourimetric quantities were evaluated and compared to uncoated fused silica glass. These changes were investigated as a function of the applied substrate bias voltage using the CIE and CIELAB colour systems. It is suggested that the mechanism of absorption is related to an allowed direct transition at the amorphous carbon films on fused silica glass. The optical energy gap of the amorphous carbon film depends on the bias voltage applied to the substrate holder. The optical colour parameters and optical band gap indicated that there is a relation between the dominant wavelength of the reflectance in the visible range and the wavelength of the optical band gap

Overview of chemical modeling of nuclear waste glass dissolution

International Nuclear Information System (INIS)

Bourcier, W.L.

1991-02-01

Glass dissolution takes place through metal leaching and hydration of the glass surface accompanied by development of alternation layers of varying crystallinity. The reaction which controls the long-term glass dissolution rate appears to be surface layer dissolution. This reaction is reversible because the buildup of dissolved species in solution slows the dissolution rate due to a decreased dissolution affinity. Glass dissolution rates are therefore highly dependent on silica concentrations in solution because silica is the major component of the alteration layer. Chemical modeling of glass dissolution using reaction path computer codes has successfully been applied to short term experimental tests and used to predict long-term repository performance. Current problems and limitations of the models include a poorly defined long-term glass dissolution mechanism, the use of model parameters determined from the same experiments that the model is used to predict, and the lack of sufficient validation of key assumptions in the modeling approach. Work is in progress that addresses these issues. 41 refs., 7 figs., 2 tabs

Interfacial interaction between the epoxidized natural rubber and silica in natural rubber/silica composites

Energy Technology Data Exchange (ETDEWEB)

Xu, Tiwen [College of Materials Science and Engineering, South China University of Technology, Guangzhou 510640 (China); Jia, Zhixin, E-mail: zxjia@scut.edu.cn [College of Materials Science and Engineering, South China University of Technology, Guangzhou 510640 (China); Luo, Yuanfang; Jia, Demin [College of Materials Science and Engineering, South China University of Technology, Guangzhou 510640 (China); Peng, Zheng [Agricultural Product Processing Research Institute, Chinese Academy of Tropical Agriculture Sciences, Zhanjiang 524001 (China)

2015-02-15

Highlights: • Substantiate the ring open reaction between Si-OH of silica and epoxy groups of ENR. • ENR can act as a bridge between NR and silica to enhance the interfacial interaction. • As a modifier, ENR gets the potential to be used in the tread of green tire for improving the wet skid resistance apparently. - Abstract: The epoxidized natural rubber (ENR) as an interfacial modifier was used to improve the mechanical and dynamical mechanical properties of NR/silica composites. In order to reveal the interaction mechanism between ENR and silica, the ENR/Silica model compound was prepared by using an open mill and the interfacial interaction of ENR with silica was investigated by Fourier transform infrared spectroscopy (FTIR), X-ray photoelectron spectroscopy (XPS), transmission electron microscopy (TEM), X-ray diffraction (XRD) and stress–strain testing. The results indicated that the ring-opening reaction occurs between the epoxy groups of ENR chains and Si-OH groups on the silica surfaces and the covalent bonds are formed between two phases, which can improve the dispersion of silica in the rubber matrix and enhance the interfacial combination between rubber and silica. The ring-opening reaction occurs not only in vulcanization process but also in mixing process, meanwhile, the latter seems to be more important due to the simultaneous effects of mechanical force and temperature.

Modeling the dissolution behavior of defense waste glass in a salt repository environment

International Nuclear Information System (INIS)

McGrain, B.P.

1988-02-01

A mechanistic model describing a dynamic mass balance between the production and consumption of dissolved silica was found to describe the dissolution behavior of SRL-165 defense waste glass in a high-magnesium brine (PBB3) at a temperature of 90 0 C. The synergistic effect of the waste package container on the glass dissolution rate was found to depend on a precipitation reaction for a ferrous silicate mineral. The model predicted that the ferrous silicate precipitate should be variable in composition where the iron/silica stoichiometry depended on the metal/glass surface area ratio used in the experiment. This prediction was confirmed experimentally by the variable iron/silica ratios observed in filtered leachates. However, the interaction between dissolved silica and iron corrosion products needs to be much better understood before the model can be used with confidence in predicting radionuclide release rates for a salt repository. 25 refs., 4 figs., 1 tab

Dielectric study of Poly(styrene- co -butadiene) Composites with Carbon Black, Silica, and Nanoclay

KAUST Repository

Vo, Loan T.

2011-08-09

Dielectric spectroscopy is used to measure polymer relaxation in styrene-butadiene rubber (SBR) composites. In addition to the bulk polymer relaxation, the SBR nanocomposites also exhibit a slower relaxation attributed to polymer relaxation at the polymer-nanoparticle interface. The glass transition temperature associated with the slower relaxation is used as a way to quantify the interaction strength between the polymer and the surface. Comparisons were made among composites containing nanoclay, silica, and carbon black. The interfacial relaxation glass transition temperature of SBR-clay nanocomposites is more than 80 °C higher than the SBR bulk glass transition temperature. An interfacial mode was also observed for SBR-silica nanocomposites, but the interfacial glass transition temperature of SBR-silica nanocomposite is somewhat lower than that of clay nanocomposites. An interfacial mode is also seen in the carbon black filled system, but the signal is too weak to analyze quantitatively. The interfacial polymer relaxation in SBR-clay nanocomposites is stronger compared to both SBR-carbon black and SBR-silica composites indicating a stronger interfacial interaction in the nanocomposites containing clay. These results are consistent with dynamic shear rheology and dynamic mechanical analysis measurements showing a more pronounced reinforcement for the clay nanocomposites. Comparisons were also made among clay nanocomposites using different SBRs of varying styrene concentration and architecture. The interfacial glass transition temperature of SBR-clay nanocomposites increases as the amount of styrene in SBR increases indicating that styrene interacts more strongly than butadiene with clay. © 2011 American Chemical Society.

Composite properties for S-2 glass in a room-temperature-curable epoxy matrix

Science.gov (United States)

Clements, L. L.; Moore, R. L.

1979-01-01

The authors have measured thermal and mechanical properties of several composites of S-2 glass fiber in a room-temperature-curable epoxy matrix. The filament-wound composites ranged from 50 to 70 vol% fiber. The composites had generally good to excellent mechanical properties, particularly in view of the moderate cost of the material. However, the composites showed rapid increases in transverse thermal expansion above 50 C, and this property must be carefully considered if any use above that temperature is contemplated.

Organic inorganic hybrid coating (poly(methyl methacrylate)/monodisperse silica)

Science.gov (United States)

Rubio, E.; Almaral, J.; Ramírez-Bon, R.; Castaño, V.; Rodríguez, V.

2005-04-01

Polymethylmethacrylate-silica hybrid coatings were prepared from methyl methacrylate and monodisperse colloidal silica prepared by the Stöber method. The surfaces of the spheres were successfully modified by chemical reaction with 3-(trimethoxysilyl) propyl methacrylate (TMSPM) to compatibilise the organic and inorganic components of the precursor solution mixture. The coatings were deposited by dip-coating on glass substrates. They result with good properties of homogeneity, optical transparence, hardness and adhesion.

Uniform silica nanoparticles encapsulating two-photon absorbing fluorescent dye

International Nuclear Information System (INIS)

Wu Weibing; Liu Chang; Wang Mingliang; Huang Wei; Zhou Shengrui; Jiang Wei; Sun Yueming; Cui Yiping; Xu Chunxinag

2009-01-01

We have prepared uniform silica nanoparticles (NPs) doped with a two-photon absorbing zwitterionic hemicyanine dye by reverse microemulsion method. Obvious solvatochromism on the absorption spectra of dye-doped NPs indicates that solvents can partly penetrate into the silica matrix and then affect the ground and excited state of dye molecules. For dye-doped NP suspensions, both one-photon and two-photon excited fluorescence are much stronger and recorded at shorter wavelength compared to those of free dye solutions with comparative overall dye concentration. This behavior is possibly attributed to the restricted twisted intramolecular charge transfer (TICT), which reduces fluorescence quenching when dye molecules are trapped in the silica matrix. Images from two-photon laser scanning fluorescence microscopy demonstrate that the dye-doped silica NPs can be actively uptaken by Hela cells with low cytotoxicity. - Graphical abstract: Water-soluble silica NPs doped with a two-photon absorbing zwitterionic hemicyanine dye were prepared. They were found of enhanced one-photon and two-photon excited fluorescence compared to free dye solutions. Images from two-photon laser scanning fluorescence microscopy demonstrate that the dye-doped silica NPs can be actively uptaken by Hela cells.

One-step synthesis of dye-incorporated porous silica particles

Energy Technology Data Exchange (ETDEWEB)

Liu Qing; DeShong, Philip; Zachariah, Michael R., E-mail: mrz@umd.edu [University of Maryland, Department of Chemistry and Biochemistry (United States)

2012-07-15

Fluorescent nanoparticles have a variety of biomedical applications as diagnostics and traceable drug delivery agents. Highly fluorescent porous silica nanoparticles were synthesized in a water/oil phase by a microemulsion method. What is unique about the resulting porous silica nanoparticles is the combination of a single-step, efficient synthesis and the high stability of its fluorescence emission in the resulting materials. The key of the success of this approach is the choice of a lipid dye that functions as a surrogate surfactant in the preparation. The surfactant dye was incorporated at the interface of the inorganic silica matrix and organic environment (pore template), and thus insures the stability of the dye-silica hybrid structure. The resulting fluorescent silica materials have a number of properties that make them attractive for biomedical applications: the availability of various color of the resulting nanoparticle from among a broad spectrum of commercially dyes, the controllablity of pore size (diameters of {approx}5 nm) and particle size (diameters of {approx}40 nm) by adjusting template monomer concentration and the water/oil ratio, and the stability and durability of particle fluorescence because of the deep insertion of surfactant's tail into the silica matrix.

Functionalization of silica nanoparticles for polypropylene nanocomposites applications

International Nuclear Information System (INIS)

Bracho, Diego; Palza, Humberto; Quijada, Raul; Dougnac, Vivianne

2011-01-01

Synthetic silica nanospheres of different diameters produced via the sol-gel method were used in order to enhance the barrier properties of the polypropylene-silica nanocomposites. Modification of the silica surface by reaction with organic chlorosilanes was performed in order to improve the particles interaction with the polypropylene matrix and its dispersion. Unmodified and modified silica nanoparticles were characterized using electronic microscopy (TEM), elemental analysis, thermo gravimetric analysis (TGA), and solid state nuclear magnetic resonance (NMR) spectroscopy. Preliminary permeability tests of the polymer-silica nanocomposite films showed no significant change at low particles load (3 wt%) regardless its size or surface functionality, mainly because of the low aspect ratio of the silica nanospheres. However, it is expected that at a higher concentration of silica particles differences will be observed. (author)

Reuse of ground waste glass as aggregate for mortars.

Science.gov (United States)

Corinaldesi, V; Gnappi, G; Moriconi, G; Montenero, A

2005-01-01

This work was aimed at studying the possibility of reusing waste glass from crushed containers and building demolition as aggregate for preparing mortars and concrete. At present, this kind of reuse is still not common due to the risk of alkali-silica reaction between the alkalis of cement and silica of the waste glass. This expansive reaction can cause great problems of cracking and, consequently, it can be extremely deleterious for the durability of mortar and concrete. However, data reported in the literature show that if the waste glass is finely ground, under 75mum, this effect does not occur and mortar durability is guaranteed. Therefore, in this work the possible reactivity of waste glass with the cement paste in mortars was verified, by varying the particle size of the finely ground waste glass. No reaction has been detected with particle size up to 100mum thus indicating the feasibility of the waste glass reuse as fine aggregate in mortars and concrete. In addition, waste glass seems to positively contribute to the mortar micro-structural properties resulting in an evident improvement of its mechanical performance.

High power operation of cladding pumped holmium-doped silica fibre lasers.

Science.gov (United States)

Hemming, Alexander; Bennetts, Shayne; Simakov, Nikita; Davidson, Alan; Haub, John; Carter, Adrian

2013-02-25

We report the highest power operation of a resonantly cladding-pumped, holmium-doped silica fibre laser. The cladding pumped all-glass fibre utilises a fluorine doped glass layer to provide low loss cladding guidance of the 1.95 µm pump radiation. The operation of both single mode and large-mode area fibre lasers was demonstrated, with up to 140 W of output power achieved. A slope efficiency of 59% versus launched pump power was demonstrated. The free running emission was measured to be 2.12-2.15 µm demonstrating the potential of this architecture to address the long wavelength operation of silica based fibre lasers with high efficiency.

Histological and histomorphometrical analysis of a silica matrix embedded nanocrystalline hydroxyapatite bone substitute using the subcutaneous implantation model in Wistar rats

Energy Technology Data Exchange (ETDEWEB)

Ghanaati, Shahram; Orth, Carina; Barbeck, Mike; Kirkpatrick, Charles James [Institute of Pathology, University Medical Center of the Johannes Gutenberg University Mainz, Langenbeckstrasse 1, 55101 Mainz (Germany); Willershausen, Ines [Institute for Dental Material Sciences and Technology, University Medical Center of the Johannes Gutenberg University Mainz, Anselm-Franz-von-Bentzel-Weg 14, 55128 Mainz (Germany); Thimm, Benjamin W [Institute for Biomechanics, ETH Zuerich, Wolfgang-Pauli-Str.10, 8093 Zuerich (Switzerland); Booms, Patrick [Leeds Institute of Molecular Medicine, Section of Medicine, Surgery and Anaesthesia, University of Leeds (United Kingdom); Stuebinger, Stefan; Landes, Constantin; Sader, Robert Anton, E-mail: ghanaati@uni-mainz.d [Department for Oral, Cranio-Maxillofacial and Facial Plastic Surgery, Medical Center of the Goethe University Frankfurt, Theodor-Stein-Kai 7, 60596 Frankfurt am Main (Germany)

2010-06-01

The clinical suitability of a bone substitute material is determined by the ability to induce a tissue reaction specific to its composition. The aim of this in vivo study was to analyze the tissue reaction to a silica matrix-embedded, nanocrystalline hydroxyapatite bone substitute. The subcutaneous implantation model in Wistar rats was chosen to assess the effect of silica degradation on the vascularization of the biomaterial and its biodegradation within a time period of 6 months. Already at day 10 after implantation, histomorphometrical analysis showed that the vascularization of the implantation bed reached its peak value compared to all other time points. Both vessel density and vascularization significantly decreased until day 90 after implantation. In this time period, the bone substitute underwent a significant degradation initiated by TRAP-positive and TRAP-negative multinucleated giant cells together with macrophages and lymphocytes. Although no specific tissue reaction could be related to the described silica degradation, the biomaterial was close to being fully degraded without a severe inflammatory response. These characteristics are advantageous for bone regeneration and remodeling processes.

Histological and histomorphometrical analysis of a silica matrix embedded nanocrystalline hydroxyapatite bone substitute using the subcutaneous implantation model in Wistar rats

International Nuclear Information System (INIS)

Ghanaati, Shahram; Orth, Carina; Barbeck, Mike; Kirkpatrick, Charles James; Willershausen, Ines; Thimm, Benjamin W; Booms, Patrick; Stuebinger, Stefan; Landes, Constantin; Sader, Robert Anton

2010-01-01

The clinical suitability of a bone substitute material is determined by the ability to induce a tissue reaction specific to its composition. The aim of this in vivo study was to analyze the tissue reaction to a silica matrix-embedded, nanocrystalline hydroxyapatite bone substitute. The subcutaneous implantation model in Wistar rats was chosen to assess the effect of silica degradation on the vascularization of the biomaterial and its biodegradation within a time period of 6 months. Already at day 10 after implantation, histomorphometrical analysis showed that the vascularization of the implantation bed reached its peak value compared to all other time points. Both vessel density and vascularization significantly decreased until day 90 after implantation. In this time period, the bone substitute underwent a significant degradation initiated by TRAP-positive and TRAP-negative multinucleated giant cells together with macrophages and lymphocytes. Although no specific tissue reaction could be related to the described silica degradation, the biomaterial was close to being fully degraded without a severe inflammatory response. These characteristics are advantageous for bone regeneration and remodeling processes.

Studies of crystallization of SiO2-glass by positron annihilation

International Nuclear Information System (INIS)

Hugenschmidt, C.; Kohn, S.; Janson, M.; Holzwarth, U.; Maier, K.

1996-01-01

The crystallization of silica glass has been studied by positron lifetime spectroscopy and accompanying investigations using X-ray diffraction and nuclear magnetic resonance (NMR). To this end isothermal and isochronal heat treatments were performed in the range from 700 deg C up to 1600 deg C. The lifetime spectra are analyzed by two lifetime components. The decrease of the short lifetime (200 ps) is attributed to the increasing volume fraction of the crystalline phase. The long lifetime (1000 ps) is related with the pick-off annihilation of the ο-Ps states in cavities. With starting formation of crystallization nuclei the long lifetime increases which is explained by expanding cavities at the interface between crystalline phase and amorphous matrix. (author)

Influence of the Processing Parameters on the Fiber-Matrix-Interphase in Short Glass Fiber-Reinforced Thermoplastics

Directory of Open Access Journals (Sweden)

Anna Katharina Sambale

2017-06-01

Full Text Available The interphase in short fiber thermoplastic composites is defined as a three-dimensional, several hundred nanometers-wide boundary region at the interface of fibers and the polymer matrix, exhibiting altered mechanical properties. This region is of key importance in the context of fiber-matrix adhesion and the associated mechanical strength of the composite material. An interphase formation is caused by morphological, as well as thermomechanical processes during cooling of the plastic melt close to the glass fibers. In this study, significant injection molding processing parameters are varied in order to investigate the influence on the formation of an interphase and the resulting mechanical properties of the composite. The geometry of the interphase is determined using nano-tribological techniques. In addition, the influence of the glass fiber sizing on the geometry of the interphase is examined. Tensile tests are used in order to determine the resulting mechanical properties of the produced short fiber composites. It is shown that the interphase width depends on the processing conditions and can be linked to the mechanical properties of the short fiber composite.

Surface Modification of Indium Tin Oxide Nanoparticles to Improve Its Distribution in Epoxy-Silica Polymer Matrix

Directory of Open Access Journals (Sweden)

Mostafa Jafari

2014-10-01

Full Text Available A semiconducting nanoparticle indium tin oxide (ITO was modified with silane groups and for this purpose trimethoxysilane (TMOS precursor was used under specific experimental conditions for surface modification of ITO nanoparticles. It is found that the modification of ITO nanoparticles increases the interactions between the filler and the matrix and subsequently improves the distibution of indium tin oxide nanoparticles in the polymer matrix. The epoxisilica polymer matrix was produced using trimethoxysilane and 3-glycidyloxypropyl trimethoxysilane precursors and ethylenediamine (EDA as curing agent at low temperature by sol-gel process. The sol-gel process was very useful due to its easily controllable process, solution concentration and homogeneity without using expensive and complicated equipments in comparison with other methods. Then, Fourier transform infrared (FTIR spectroscopy was employed to study the formation of Si-O-Si and Si-OH groups on ITO nanoparticles. X-Ray diffraction (XRD technique and thermal gravimetric analysis (TGA were employed to investigate the modification and weight loss of the modified ITO, respectively, as an indication of the presence of organic groups on these nanoparticles. The separation analyzer tests were performed to check the stability of the nanoparticles suspension and it revealed that due to better interaction of nanoparticles with the polymer matrix the stability of modified ITO suspention is higher than the unmodified sample. The morphology and particle distribution were determined by scanning electron microscopy (SEM. It was found that the distibution of modified indium tin oxide in epoxy-silica polymer matrix was improved in comparison with pure ITO.

Shock Wave Response of Iron-based In Situ Metallic Glass Matrix Composites.

Science.gov (United States)

Khanolkar, Gauri R; Rauls, Michael B; Kelly, James P; Graeve, Olivia A; Hodge, Andrea M; Eliasson, Veronica

2016-03-02

The response of amorphous steels to shock wave compression has been explored for the first time. Further, the effect of partial devitrification on the shock response of bulk metallic glasses is examined by conducting experiments on two iron-based in situ metallic glass matrix composites, containing varying amounts of crystalline precipitates, both with initial composition Fe49.7Cr17.7Mn1.9Mo7.4W1.6B15.2C3.8Si2.4. The samples, designated SAM2X5-600 and SAM2X5-630, are X-ray amorphous and partially crystalline, respectively, due to differences in sintering parameters during sample preparation. Shock response is determined by making velocity measurements using interferometry techniques at the rear free surface of the samples, which have been subjected to impact from a high-velocity projectile launched from a powder gun. Experiments have yielded results indicating a Hugoniot Elastic Limit (HEL) to be 8.58 ± 0.53 GPa for SAM2X5-600 and 11.76 ± 1.26 GPa for SAM2X5-630. The latter HEL result is higher than elastic limits for any BMG reported in the literature thus far. SAM2X5-600 catastrophically loses post-yield strength whereas SAM2X5-630, while showing some strain-softening, retains strength beyond the HEL. The presence of crystallinity within the amorphous matrix is thus seen to significantly aid in strengthening the material as well as preserving material strength beyond yielding.

Formation of Uniform Hollow Silica microcapsules

Science.gov (United States)

Yan, Huan; Kim, Chanjoong

2013-03-01

Microcapsules are small containers with diameters in the range of 0.1 - 100 μm. Mesoporous microcapsules with hollow morphologies possess unique properties such as low-density and high encapsulation capacity, while allowing controlled release by permeating substances with a specific size and chemistry. Our process is a one-step fabrication of monodisperse hollow silica capsules with a hierarchical pore structure and high size uniformity using double emulsion templates obtained by the glass-capillary microfluidic technique to encapsulate various active ingredients. These hollow silica microcapsules can be used as biomedical applications such as drug delivery and controlled release.

Fractal dimensions of silica gels generated using reactive molecular dynamics simulations

International Nuclear Information System (INIS)

Bhattacharya, Sudin; Kieffer, John

2005-01-01

We have used molecular dynamics simulations based on a three-body potential with charge transfer to generate nanoporous silica aerogels. Care was taken to reproduce the sol-gel condensation reaction that forms the gel backbone as realistically as possible and to thereby produce credible gel structures. The self-similarity of aerogel structures was investigated by evaluating their fractal dimension from geometric correlations. For comparison, we have also generated porous silica glasses by rupturing dense silica and computed their fractal dimension. The fractal dimension of the porous silica structures was found to be process dependent. Finally, we have determined that the effect of supercritical drying on the fractal nature of condensed silica gels is not appreciable

Experimental Investigations on the effect of Additive on the Tensile Properties of Fiber Glass Fabric Lamina

Science.gov (United States)

Nava Sai Divya, A.; Raghu Kumar, B., Dr; Lakshmi Narayana, G., Dr

2017-09-01

The main objective of this work is to investigate the effect of additives on tensile behaviour of fiber glass fabric at lamina level to explore an alternative skin material for the outer body of aerospace applications and machines. This experimental work investigates the effect of silica concentration in epoxy resin lapox L-12 on the tensile properties of glass fabric lamina of 4H-satin weave having 3.6 mm thickness. The lamina was prepared by using hand lay-up method and tests were conducted on it. Various tensile properties values obtained from experimentation were compared for four glass fiber lamina composites fabricated by adding the silica powder to resin bath. The effect of variations in silica concentration (0% SiO2, 5% SiO2, 10% SiO2 and 15% SiO2) on the tensile properties of prepared material revealed that maximum stiffness was obtained at 15% and yield strength at 10% SiO2 concentration in glass fiber lamina. Increasing the silica concentration beyond 10% had led to deterioration in the material properties. The experimentation that was carried out on test specimen was reasonably successful as the effect of silica powder as an additive in glass fiber lamina enhanced the mechanical properties up to certain limit. The underpinning microscopic behaviour at the source of these observations will be investigated in a follow up work.

Simulation of MeV electron energy deposition in CdS quantum dots absorbed in silicate glass for radiation dosimetry

Energy Technology Data Exchange (ETDEWEB)

Baharin, R; Hobson, P R; Smith, D R, E-mail: ruzalina.baharin@brunel.ac.u [Centre for Sensors and Instrumentation, School of Engineering and Design, Brunel University, Uxbridge UB8 3PH (United Kingdom)

2010-09-01

We are currently developing 2D dosimeters with optical readout based on CdS or CdS/CdSe core-shell quantum-dots using commercially available materials. In order to understand the limitations on the measurement of a 2D radiation profile the 3D deposited energy profile of MeV energy electrons in CdS quantum-dot-doped silica glass have been studied by Monte Carlo simulation using the CASINO and PENELOPE codes. Profiles for silica glass and CdS quantum-dot-doped silica glass were then compared.

Simulation of MeV electron energy deposition in CdS quantum dots absorbed in silicate glass for radiation dosimetry

International Nuclear Information System (INIS)

Baharin, R; Hobson, P R; Smith, D R

2010-01-01

We are currently developing 2D dosimeters with optical readout based on CdS or CdS/CdSe core-shell quantum-dots using commercially available materials. In order to understand the limitations on the measurement of a 2D radiation profile the 3D deposited energy profile of MeV energy electrons in CdS quantum-dot-doped silica glass have been studied by Monte Carlo simulation using the CASINO and PENELOPE codes. Profiles for silica glass and CdS quantum-dot-doped silica glass were then compared.

Effect of Silica Nanoparticles on the Local Segmental Dynamics in Polyvinylacetate

Science.gov (United States)

Bogoslovov, R. B.; Roland, C. M.; Ellis, A. R.; Randall, A. M.; Robertson, C. G.

2008-07-01

The effect of nanosized silica particles on the properties of polyvinylacetate (PVAc) was investigated for a range of silica concentrations encompassing the filler network percolation threshold. The quantity of polymer adsorbed to the particles ("bound rubber") increased systematically with silica content and was roughly equal to the quantity shielded from shear stresses ("occluded rubber"). A variety of experimental techniques was employed including pressure-volume-temperature measurements, broadband dielectric spectroscopy, thermal analysis (modulated DSC), dynamic-mechanical spectroscopy, viscometry. The glass transition properties of PVAc, i.e. the glass transition temperature and the changes in the thermal expansion coefficient and heat capacity at Tg, as well as the isothermal compressibility and the volume sensitivity of the local segmental dynamics of the polymer chains in the presence of the polymer-filler interface are discussed. The implication of this result and possible directions for new research are considered.

FTIR and morphology of liquid epoxidized natural rubber acrylate (LENRA)/silica hybrid composites

International Nuclear Information System (INIS)

Eda Yuhana Ariffin; Azizan Ahmad; Dahlan Mohd; Mahathir Mohamed

2009-01-01

Synthesis of organic-inorganic hybrid composites was carried out by combination of liquid epoxidized natural rubber acrylate (LENRA) and silica. Silica was introduce to the matrix by sol gel technique. The sol-gel technique was employed to prepare silica using tetraethyorthosilicate (TEOS) as precursor. HDDA and irga cure 184 were added to the formulations as reactive diluents and photosensitizer, respectively. The chemical modification was studied by Fourier Transform Infrared (FTIR) and energy dispersive X-ray analysis (EDAX). The morphological studies were conducted by the optical and scanning electron microscopes (SEM). It shows that silica was dispersed very well in the matrix for lower concentration of TEOS while agglomeration occurs at the higher concentration. The average particles size of silica were less than 100 nm. (Author)

Effect of phosphate-based glass fibre surface properties on thermally produced poly(lactic acid) matrix composites.

Science.gov (United States)

Mohammadi, Maziar Shah; Ahmed, Ifty; Muja, Naser; Rudd, Christopher D; Bureau, Martin N; Nazhat, Showan N

2011-12-01

Incorporation of soluble bioactive glass fibres into biodegradable polymers is an interesting approach for bone repair and regeneration. However, the glass composition and its surface properties significantly affect the nature of the fibre-matrix interface and composite properties. Herein, the effect of Si and Fe on the surface properties of calcium containing phosphate based glasses (PGs) in the system (50P(2)O(5)-40CaO-(10-x)SiO(2)-xFe(2)O(3), where x = 0, 5 and 10 mol.%) were investigated. Contact angle measurements revealed a higher surface energy, and surface polarity as well as increased hydrophilicity for Si doped PG which may account for the presence of surface hydroxyl groups. Two PG formulations, 50P(2)O(5)-40CaO-10Fe(2)O(3) (Fe10) and 50P(2)O(5)-40CaO-5Fe(2)O(3)-5SiO(2) (Fe5Si5), were melt drawn into fibres and randomly incorporated into poly(lactic acid) (PLA) produced by melt processing. The ageing in deionised water (DW), mechanical property changes in phosphate buffered saline (PBS) and cytocompatibility properties of these composites were investigated. In contrast to Fe10 and as a consequence of the higher surface energy and polarity of Fe5Si5, its incorporation into PLA led to increased inorganic/organic interaction indicated by a reduction in the carbonyl group of the matrix. PLA chain scission was confirmed by a greater reduction in its molecular weight in PLA-Fe5Si5 composites. In DW, the dissolution rate of PLA-Fe5Si5 was significantly higher than that of PLA-Fe10. Dissolution of the glass fibres resulted in the formation of channels within the matrix. Initial flexural strength was significantly increased through PGF incorporation. After PBS ageing, the reduction in mechanical properties was greater for PLA-Fe5Si5 compared to PLA-Fe10. MC3T3-E1 preosteoblasts seeded onto PG discs, PLA and PLA-PGF composites were evaluated for up to 7 days indicating that the materials were generally cytocompatible. In addition, cell alignment along the PGF

The chemical durability of glasses suitable for the storage of high level radioactive wastes, (1)

International Nuclear Information System (INIS)

Terai, Ryohei; Hara, Shigeo; Kawamoto, Takamichi; Nanbu, Tadahiko; Nakamura, Takao.

1975-01-01

To develop the glassy materials suitable for the long-term storage of high level radioactive wastes, the chemical durability of the glasses of borax-alumina-silica system has been investigated. The test was carried out by the following three ways, (1) glass-disk immersion method, (2) continuous leach method and (3) method prescribed in JIS-R3502. In the continuous leach method, glass grains were exposed to circulating water at a constant temperature for a week to obtain the leach factor or leach rate. It was found from the experimental results that, as the silica content increased, the melting temperature of the glasses progressively increased and the chemical durability was considerably improved, and that B 2 O 3 and Na 2 O constituents were preferentially dissolved in water leaving relatively insoluble components such as SiO 2 and Al 2 O 3 . The rate at which B 2 O 3 and Na 2 O in glass are leached out is governed by three processes, that is, (1) the boundary reaction on the glass surface, (2) the diffusion process through the hydrated layer, and (3) the disintegration of hydrated layer. The first process probably corresponds to the hydration of boric oxides on the glass surface or to the ion exchange between protons in solution and Na + ions in glass, and the second process seems to correspond to the diffusion of protons through the hydrated layer on the glass surface. Although the ratio of [Na-BO 4 ]/[BO 3 ] in the borax-silica glasses was determined to be 0.5 by means of NMR measurement, Na 2 O/B 2 O 3 ratio in leached solution was less than 0.5, indicating that [BO 3 ] groups in glass were more soluble than [Na-BO 4 ] groups. From the viewpoint of appreciation of safety, the chemical durability of the glasses of borax-aluminasilica system was rather unsatisfactory, but that of the glasses containing silica in quantities was comparable to the soda-lime silicate sheet glasses. (auth.)

Biomimetic silica encapsultation of living cells

Science.gov (United States)

Jaroch, David Benjamin

Living cells perform complex chemical processes on size and time scales that artificial systems cannot match. Cells respond dynamically to their environment, acting as biological sensors, factories, and drug delivery devices. To facilitate the use of living systems in engineered constructs, we have developed several new approaches to create stable protective microenvironments by forming bioinspired cell-membrane-specific silica-based encapsulants. These include vapor phase deposition of silica gels, use of endogenous membrane proteins and polysaccharides as a site for silica nucleation and polycondensation in a saturated environment, and protein templated ordered silica shell formation. We demonstrate silica layer formation at the surface of pluripotent stem-like cells, bacterial biofilms, and primary murine and human pancreatic islets. Materials are characterized by AFM, SEM and EDS. Viability assays confirm cell survival, and metabolite flux measurements demonstrate normal function and no major diffusion limitations. Real time PCR mRNA analysis indicates encapsulated islets express normal levels of genetic markers for β-cells and insulin production. The silica glass encapsulant produces a secondary bone like calcium phosphate mineral layer upon exposure to media. Such bioactive materials can improve device integration with surrounding tissue upon implantation. Given the favorable insulin response, bioactivity, and long-term viability observed in silica-coated islets, we are currently testing the encapsulant's ability to prevent immune system recognition of foreign transplants for the treatment of diabetes. Such hybrid silica-cellular constructs have a wide range of industrial, environmental, and medical applications.

Processability analysis of candidate waste forms

International Nuclear Information System (INIS)

Gould, T.H. Jr.; Dunson, J.B. Jr.; Eisenberg, A.M.; Haight, H.G. Jr.; Mello, V.E.; Schuyler, R.L. III.

1982-01-01

A quantitative merit evaluation, or processability analysis, was performed to assess the relative difficulty of remote processing of Savannah River Plant high-level wastes for seven alternative waste form candidates. The reference borosilicate glass process was rated as the simplest, followed by FUETAP concrete, glass marbles in a lead matrix, high-silica glass, crystalline ceramics (SYNROC-D and tailored ceramics), and coated ceramic particles. Cost estimates for the borosilicate glass, high-silica glass, and ceramic waste form processing facilities are also reported

Terahertz-induced Kerr effect in amorphous chalcogenide glasses

DEFF Research Database (Denmark)

Zalkovskij, Maksim; Strikwerda, Andrew; Iwaszczuk, Krzysztof

2013-01-01

We have investigated the terahertz-induced third-order (Kerr) nonlinear optical properties of the amorphous chalcogenide glasses As2S3 and As2Se3. Chalcogenide glasses are known for their high optical Kerr nonlinearities which can be several hundred times greater than those of fused silica. We use...

Lifetime Prediction of Nano-Silica based Glass Fibre/Epoxy composite by Time Temperature Superposition Principle

Science.gov (United States)

Anand, Abhijeet; Banerjee, Poulami; Prusty, Rajesh Kumar; Ray, Bankin Chandra

2018-03-01

The incorporation of nano fillers in Fibre reinforced polymer (FRP) composites has been a source of experimentation for researchers. Addition of nano fillers has been found to improve mechanical, thermal as well as electrical properties of Glass fibre reinforced polymer (GFRP) composites. The in-plane mechanical properties of GFRP composite are mainly controlled by fibers and therefore exhibit good values. However, composite exhibits poor through-thickness properties, in which the matrix and interface are the dominant factors. Therefore, it is conducive to modify the matrix through dispersion of nano fillers. Creep is defined as the plastic deformation experienced by a material for a temperature at constant stress over a prolonged period of time. Determination of Master Curve using time-temperature superposition principle is conducive for predicting the lifetime of materials involved in naval and structural applications. This is because such materials remain in service for a prolonged time period before failure which is difficult to be kept marked. However, the failure analysis can be extrapolated from its behaviour in a shorter time at an elevated temperature as is done in master creep analysis. The present research work dealt with time-temperature analysis of 0.1% SiO2-based GFRP composites fabricated through hand-layup method. Composition of 0.1% for SiO2nano fillers with respect to the weight of the fibers was observed to provide optimized flexural properties. Time and temperature dependence of flexural properties of GFRP composites with and without nano SiO2 was determined by conducting 3-point bend flexural creep tests over a range of temperature. Stepwise isothermal creep tests from room temperature (30°C) to the glass transition temperature Tg (120°C) were performed with an alternative creep/relaxation period of 1 hour at each temperature. A constant stress of 40MPa was applied during the creep tests. The time-temperature superposition principle was

An investigation of waste glass-based geopolymers supplemented with alumina

Science.gov (United States)

Christiansen, Mary U.

An increased consideration of sustainability throughout society has resulted in a surge of research investigating sustainable alternatives to existing construction materials. A new binder system, called a geopolymer, is being investigated to supplement ordinary portland cement (OPC) concrete, which has come under scrutiny because of the CO2 emissions inherent in its production. Geopolymers are produced from the alkali activation of a powdered aluminosilicate source by an alkaline solution, which results in a dense three-dimensional matrix of tetrahedrally linked aluminosilicates. Geopolymers have shown great potential as a building construction material, offering similar mechanical and durability properties to OPC. Additionally, geopolymers have the added value of a considerably smaller carbon footprint than OPC. This research considered the compressive strength, microstructure and composition of geopolymers made from two types of waste glass with varying aluminum contents. Waste glass shows great potential for mainstream use in geopolymers due to its chemical and physical homogeneity as well as its high content of amorphous silica, which could eliminate the need for sodium silicate. However, the lack of aluminum is thought to negatively affect the mechanical performance and alkali stability of the geopolymer system. 39 Mortars were designed using various combinations of glass and metakaolin or fly ash to supplement the aluminum in the system. Mortar made from the high-Al glass (12% Al2O3) reached over 10,000 psi at six months. Mortar made from the low-Al glass (use in geopolymers, when care is given to consider the compositional and physical properties of the glass in mixture design.

Thermal conductivities of some lead and bismuth glasses

NARCIS (Netherlands)

Velden, P.F. van

1965-01-01

Thermal conductivities have been measured, mainly at 40°C, of glasses within the systems PbO-Bi2O3-SiO2, PbO-Bi2O3-Al2O3-SiO2, and BaO- (Bi2O3 or PbO) -SiO2. Aiming at lowest thermal conductivity, preference was given to glasses of low silica and low alumina contents. Glass formation persists at

Micromechanical modeling of tungsten-based bulk metallic glass matrix composites

Energy Technology Data Exchange (ETDEWEB)

Li Hao [Department of Mechanical Engineering-Engineering Mechanics, Michigan Technological University, 1400 Townsend Drive, Houghton, MI 49931 (United States); Li Ke [Department of Mechanical Engineering, Texas A and M University, TAMU 3123, College Station, TX 77843 (United States)]. E-mail: keli@tamu.edu; Subhash, Ghatu [Department of Mechanical Engineering-Engineering Mechanics, Michigan Technological University, 1400 Townsend Drive, Houghton, MI 49931 (United States); Kecskes, Laszlo J. [Weapons and Materials Research Directorate, US Army Research Laboratory, Aberdeen Proving Ground, MD 21005 (United States); Dowding, Robert J. [Weapons and Materials Research Directorate, US Army Research Laboratory, Aberdeen Proving Ground, MD 21005 (United States)

2006-08-15

Micromechanics models are developed for tungsten (W)-based bulk metallic glass (BMG) matrix composites employing the Voronoi tessellation technique and the finite element (FE) method. The simulation results indicate that the computed elastic moduli are close to those measured in the experiments. The predicted stress-strain curves agree well with their experimentally obtained counterparts in the early stage of the plastic deformation. An increase in the W volume fraction leads to a decrease in the yield stress and an increase in the Young's modulus of the composite. In addition, contours of equivalent plastic strain for increasing applied strains provide an explanation why shear bands were observed in the glassy phase, along the W/BMG interface, and in the W phase of failed W/BMG composite specimens.

Pore radius fine tuning of a silica matrix (MCM-41) based on the synthesis of alumina nanolayers with different thicknesses by atomic layer deposition

International Nuclear Information System (INIS)

Zemtsova, Elena G.; Arbenin, Andrei Yu.; Plotnikov, Alexander F.; Smirnov, Vladimir M.

2015-01-01

The authors investigated a new approach to modify the surface of the mesoporous silica matrix MCM-41. This approach is based on manipulating the chemical composition of the porous surface layer and also on fine tuning the pore radius by applying the atomic layer deposition (ALD) technique. The synthesis of alumina nanolayers was performed on the planar and the porous matrix (MCM-41) by the ALD technique using aluminum tri-sec-butoxide and water as precursors. The authors show that one cycle on silicon, using aluminum tri-sec-butoxide and water as precursors, results in a 1–1.2 Å increase in alumina nanolayer thickness. This is comparable to the increase in thickness per cycle for other precursors such as trimethylaluminum and aluminum chloride. The authors show that the synthesis of an Al 2 O 3 nanolayer on the pore surface of the mesoporous silica matrix MCM-41 by the ALD technique results in a regular change in the porous structure of the samples. The specific porosity (ml/g) of the MCM-41 was 0.95 and that of MCM-41 after 5 ALD cycles was 0.39. The pore diameter (nm) of MCM-41 was 3.3 and that of MCM-41 after 5 ALD cycles was 2.3

Ge nanoclusters in PECVD-deposited glass after heat treating and electron irradiation

DEFF Research Database (Denmark)

Ou, Haiyan; Rørdam, Troels Peter; Rottwitt, Karsten

2007-01-01

This paper reports the formation of Ge nanoclusters in silica glass thin films deposited by plasma-enhanced chemical vapor deposition (PECVD). We studied the samples by transmission electron microscopy (TEM) and Raman spectroscopy after annealing. TEM investigation shows that the Ge nanoclusters...... at two areaswere formed by different mechanisms. The Ge nanoclusters formed in a single row along the interface of a silicon substrate and the silica glass film by annealing during high-temperature heat treatment. Ge nanoclusters did not initially form in the bulk of the film but could be subsequently...... formed by the electron-beam irradiation. The interface between the silicon substrate and the silica glass film was investigated by Raman spectroscopy. The shift of the Raman peaks around 286.8 cm−1 and 495 cm−1 suggests that the interface is a Si1−xGex alloy film and that the composition x varies along...

Mechanical and chemical properties of polyvinyl alcohol modified cement mortar with silica fume used as matrix including radioactive waste

International Nuclear Information System (INIS)

Dakroury, A. M.

2007-01-01

This paper discussed the mechanical and chemical properties of polyvinyl alcohol - modified cement mortar with silica fume to assess the safety for disposal of radioactive waste. The modified cement mortars containing polyvinyl alcohol (PVA) in the presence of 10 % silica fume (SF) .The chemical reaction between polymer and cement - hydrated product were investigated by the Infrared Spectral Technology, Differential Thermal Analysis and X-ray diffraction. The leaching of 137Cs from a waste composite into a surrounding fluid has been studied .The results shown that PVA increases the strength and decreases the porosity. The increase in strength duo to the interaction of PVA with cement , may be forming some new compound that fill the pores or improve the bond between the cement . The pozzolanic reaction of the SF increases the calcium silicate hydrates in the hardening matrix composites. There is distinct change in the refinement of the pore structure in cement composites giving fewer capillary pores and more of the finer gel pores

Activators generated by electron transfer for atom transfer radical polymerization of styrene in the presence of mesoporous silica nanoparticles

Energy Technology Data Exchange (ETDEWEB)

Khezri, Khezrollah, E-mail: kh.khezri@ut.ac.ir [School of Chemistry, University College of Science, University of Tehran, PO Box 14155-6455, Tehran (Iran, Islamic Republic of); Roghani-Mamaqani, Hossein [Department of Polymer Engineering, Sahand University of Technology, PO Box 51335-1996, Tabriz (Iran, Islamic Republic of)

2014-11-15

Graphical abstract: Effect of mesoporous silica nanoparticles (MCM-41) on the activator generated by electron transfer for atom transfer radical polymerization (AGET ATRP) is investigated. Decrement of conversion and number average molecular weight and also increment of polydispersity index (PDI) values are three main results of addition of MCM-41 nanoparticles. Incorporation of MCM-41 nanoparticles in the polystyrene matrix can clearly increase thermal stability and decrease glass transition temperature of the nanocomposites. - Highlights: • Spherical morphology, hexagonal structure, and high surface area with regular pore diameters of the synthesized MCM-41 nanoparticles are examined. • AGET ATRP of styrene in the presence of MCM-41 nanoparticles is performed. • Effect of MCM-41 nanoparticles addition on the polymerization rate, conversion and molecular weights of the products are discussed. • Improvement in thermal stability of the nanocomposites and decreasing T{sub g} values was also observed by incorporation of MCM-41 nanoparticles. - Abstract: Activator generated by electron transfer for atom transfer radical polymerization was employed to synthesize well-defined mesoporous silica nanoparticles/polystyrene composites. Inherent features of spherical mesoporous silica nanoparticles were evaluated by nitrogen adsorption/desorption isotherm, X-ray diffraction and scanning electron microscopy analysis techniques. Conversion and molecular weight evaluations were carried out using gas and size exclusion chromatography respectively. By the addition of only 3 wt% mesoporous silica nanoparticles, conversion decreases from 81 to 58%. Similarly, number average molecular weight decreases from 17,116 to 12,798 g mol{sup −1}. However, polydispersity index (PDI) values increases from 1.24 to 1.58. A peak around 4.1–4.2 ppm at proton nuclear magnetic resonance spectroscopy results clearly confirms the living nature of the polymerization. Thermogravimetric

Acoustic properties of a porous glass (vycor) at hypersonic frequencies

International Nuclear Information System (INIS)

Levelut, C; Pelous, J

2007-01-01

Brillouin scattering experiments have been performed from 5 to 1600 K in vycor, a porous silica glass. The acoustic velocity and attenuation at hypersonic frequencies are compared to those of bulk silica and others porous silica samples. The experimental evidence for the influence of porosity on the scattering by acoustic waves is compared to calculations. The correlation between internal friction and thermal conductivity at low temperature is discussed

Influence of nuclear glasses composition on their liability to deterioration

International Nuclear Information System (INIS)

Tovena, I.

1995-01-01

The aim of this thesis is to contribute to the study of the nuclear glasses composition influence on their liability to deterioration. The methodology of the experimental research used has lead to define between the thirty oxides which form the reference glass light water, six oxides of interest. For each of these oxides, a composition variation area has been defined. A matrix of twenty glass compositions has then been defined. The preparation of materials of these compositions has sometimes lead to materials weakly heterogeneous which have been characterized before deterioration. This study has been completed by those of three glasses in a composition variation area narrower of the light water nuclear glass : the R7T7 and two glasses at limits having respectively an initial dissolution velocity at 100 degrees Celsius theoretically maximum and minimum. Some deterioration parameters in pure water have been experimentally measured on the twenty three glasses : 1) an initial dissolution velocity at 100 degrees (Vo 1 00) Celsius and another one at 90 degrees Celsius (Vo 9 0) 2) a dissolution velocity in conditions near the saturation at 90 degrees Celsius 3) an apparent solubility of glass based on the ortho silicic acid activity 4) the evolution of the dissolution kinetics at 90 degrees Celsius in sub-saturated medium towards saturated medium 5) the alteration films nature developed at the glasses surface during these last alteration tests. Some thermodynamic and structural models have been studied in order to predict Vo 9 0 and Vo 1 00. The dissolution kinetic law developed from reference glass dissolution results has been studied with the calculation code LIXIVER. It has not been able to be used for most of the glasses compositions studied. As a consequence, the glasses dissolution control by a surface reaction which are itself controlled by the only dissolved silica is an hypothesis which is not verified for the greater part of the glasses. (O.L.). refs., figs

Fluorescence metrology of silica sol-gels

Indian Academy of Sciences (India)

We have developed a new method for measuring in-situ the growth of the nanometre-size silica particles which lead to the formation of sol-gel glasses. This technique is based on the decay of fluorescence polarisation anisotropy due to Brownian rotation of dye molecules bound to the particles. Results to date give near ...

The Largest Bio-Silica Structure on Earth: The Giant Basal Spicule from the Deep-Sea Glass Sponge Monorhaphis chuni

Directory of Open Access Journals (Sweden)

Xiaohong Wang

2011-01-01

Full Text Available The depth of the ocean is plentifully populated with a highly diverse fauna and flora, from where the Challenger expedition (1873–1876 treasured up a rich collection of vitreous sponges [Hexactinellida]. They have been described by Schulze and represent the phylogenetically oldest class of siliceous sponges [phylum Porifera]; they are eye-catching because of their distinct body plan, which relies on a filigree skeleton. It is constructed by an array of morphologically determined elements, the spicules. Later, during the German Deep Sea Expedition “Valdivia” (1898-1899, Schulze could describe the largest siliceous hexactinellid sponge on Earth, the up to 3 m high Monorhaphis chuni, which develops the equally largest bio-silica structures, the giant basal spicules (3 m × 10 mm. With such spicules as a model, basic knowledge on the morphology, formation, and development of the skeletal elements could be elaborated. Spicules are formed by a proteinaceous scaffold which mediates the formation of siliceous lamellae in which the proteins are encased. Up to eight hundred 5 to 10 μm thick lamellae can be concentrically arranged around an axial canal. The silica matrix is composed of almost pure silicon and oxygen, providing it with unusual optophysical properties that are superior to those of man-made waveguides. Experiments indicated that the spicules function in vivo as a nonocular photoreception system. In addition, the spicules have exceptional mechanical properties, combining mechanical stability with strength and stiffness. Like demosponges the hexactinellids synthesize their silica enzymatically, via the enzyme silicatein. All these basic insights will surely contribute also to a further applied utilization and exploration of bio-silica in material/medical science.

The largest Bio-Silica Structure on Earth: The Giant Basal Spicule from the Deep-Sea Glass Sponge Monorhaphis chuni.

Science.gov (United States)

Wang, Xiaohong; Gan, Lu; Jochum, Klaus P; Schröder, Heinz C; Müller, Werner E G

2011-01-01

The depth of the ocean is plentifully populated with a highly diverse fauna and flora, from where the Challenger expedition (1873-1876) treasured up a rich collection of vitreous sponges [Hexactinellida]. They have been described by Schulze and represent the phylogenetically oldest class of siliceous sponges [phylum Porifera]; they are eye-catching because of their distinct body plan, which relies on a filigree skeleton. It is constructed by an array of morphologically determined elements, the spicules. Later, during the German Deep Sea Expedition "Valdivia" (1898-1899), Schulze could describe the largest siliceous hexactinellid sponge on Earth, the up to 3 m high Monorhaphis chuni, which develops the equally largest bio-silica structures, the giant basal spicules (3 m × 10 mm). With such spicules as a model, basic knowledge on the morphology, formation, and development of the skeletal elements could be elaborated. Spicules are formed by a proteinaceous scaffold which mediates the formation of siliceous lamellae in which the proteins are encased. Up to eight hundred 5 to 10 μm thick lamellae can be concentrically arranged around an axial canal. The silica matrix is composed of almost pure silicon and oxygen, providing it with unusual optophysical properties that are superior to those of man-made waveguides. Experiments indicated that the spicules function in vivo as a nonocular photoreception system. In addition, the spicules have exceptional mechanical properties, combining mechanical stability with strength and stiffness. Like demosponges the hexactinellids synthesize their silica enzymatically, via the enzyme silicatein. All these basic insights will surely contribute also to a further applied utilization and exploration of bio-silica in material/medical science.

Structural refinement of vitreous silica bilayers

Science.gov (United States)

Sadjadi, Mahdi; Wilson, Mark; Thorpe, M. F.

The importance of glasses resides not only in their applications but in fundamental questions that they put forth. The continuous random network model can successfully describe the glass structure, but determining details, like ring statistics, has always been difficult using only diffraction data. But recent atomic images of 2D vitreous silica bilayers can offer valuable new insights which are hard to be observed directly in 3D silica models/experiments (for references see). However, the experimental results are prone to uncertainty in atomic positions, systematic errors, and being finite. We employ special boundary conditions developed for such networks to refine the experimental structures. We show the best structure can be found by using various potentials to maximize information gained from the experimental samples. We find a range of densities, the so-called flexibility window, in which tetrahedra are perfect. We compare results from simulations using harmonic potentials, MD with atomic polarizabilities included and DFT. We should thank David Drabold and Bishal Bhattarai for useful discussions. Support through NSF Grant # DMS 1564468 is gratefully acknowledged.

Assessment of processes, facilities, and costs for alternative solid forms for immobilization of SRP defense waste

International Nuclear Information System (INIS)

Dunson, J.B. Jr.; Eisenberg, A.M.; Schuyler, R.L. III; Haight, H.G. Jr.; Mello, V.E.; Gould, T.H. Jr.; Butler, J.L.; Pickett, J.B.

1982-03-01

A quantitative merit evaluation which assesses the relative difficulty of remote processing of Savannah River Plant high-level wastes for seven alternative waste forms is presented. The reference borosilicate glass process is rated as the simplest, followed by FUETAP concrete. The other processes evaluated in order of increasing complexity were: glass marbles in a lead matrix, high-silica glass, crystalline ceramic (Synroc-D and tailored ceramic), and coated ceramic particles. Cost appraisals are summarized for the borosilicate glass, high-silica glass, and ceramic waste form processing facilities

Microporous Silica Based Membranes for Desalination

Directory of Open Access Journals (Sweden)

João C. Diniz da Costa

2012-09-01

Full Text Available This review provides a global overview of microporous silica based membranes for desalination via pervaporation with a focus on membrane synthesis and processing, transport mechanisms and current state of the art membrane performance. Most importantly, the recent development and novel concepts for improving the hydro-stability and separating performance of silica membranes for desalination are critically examined. Research into silica based membranes for desalination has focussed on three primary methods for improving the hydro-stability. These include incorporating carbon templates into the microporous silica both as surfactants and hybrid organic-inorganic structures and incorporation of metal oxide nanoparticles into the silica matrix. The literature examined identified that only metal oxide silica membranes have demonstrated high salt rejections under a variety of feed concentrations, reasonable fluxes and unaltered performance over long-term operation. As this is an embryonic field of research several target areas for researchers were discussed including further improvement of the membrane materials, but also regarding the necessity of integrating waste or solar heat sources into the final process design to ensure cost competitiveness with conventional reverse osmosis processes.

Inverse opal photonic crystal of chalcogenide glass by solution processing.

Science.gov (United States)

Kohoutek, Tomas; Orava, Jiri; Sawada, Tsutomu; Fudouzi, Hiroshi

2011-01-15

Chalcogenide opal and inverse opal photonic crystals were successfully fabricated by low-cost and low-temperature solution-based process, which is well developed in polymer films processing. Highly ordered silica colloidal crystal films were successfully infilled with nano-colloidal solution of the high refractive index As(30)S(70) chalcogenide glass by using spin-coating method. The silica/As-S opal film was etched in HF acid to dissolve the silica opal template and fabricate the inverse opal As-S photonic crystal. Both, the infilled silica/As-S opal film (Δn ~ 0.84 near λ=770 nm) and the inverse opal As-S photonic structure (Δn ~ 1.26 near λ=660 nm) had significantly enhanced reflectivity values and wider photonic bandgaps in comparison with the silica opal film template (Δn ~ 0.434 near λ=600 nm). The key aspects of opal film preparation by spin-coating of nano-colloidal chalcogenide glass solution are discussed. The solution fabricated "inorganic polymer" opal and the inverse opal structures exceed photonic properties of silica or any organic polymer opal film. The fabricated photonic structures are proposed for designing novel flexible colloidal crystal laser devices, photonic waveguides and chemical sensors. Copyright © 2010 Elsevier Inc. All rights reserved.

Formation of silver nanoparticles inside a soda-lime glass matrix in the presence of a high intensity Ar+ laser beam

International Nuclear Information System (INIS)

Niry, M. D.; Khalesifard, H. R.; Mostafavi-Amjad, J.; Ahangary, A.; Azizian-Kalandaragh, Y.

2012-01-01

Formation and motion of the silver nanoparticles inside an ion-exchanged soda-lime glass in the presence of a focused high intensity continuous wave Ar + laser beam (intensity: 9.2 x 10 4 W/cm 2 ) have been studied in here. One-dimensional diffusion equation has been used to model the diffusion of the silver ions into the glass matrix, and a two-dimensional reverse diffusion model has been introduced to explain the motion of the silver clusters and their migration toward the glass surface in the presence of the laser beam. The results of the mentioned models were in agreement with our measurements on thickness of the ion-exchange layer by means of optical microscopy and recorded morphology of the glass surface around the laser beam axis by using a Mirau interferometer. SEM micrographs were used to extract the size distribution of the migrated silver particles over the glass surface.

Investigation of matrix effects in 193 nm laser ablation-inductively coupled plasma-mass spectrometry analysis using reference glasses of different transparencies

International Nuclear Information System (INIS)

Czas, J.; Jochum, K.P.; Stoll, B.; Weis, U.; Yang, Q.-C.; Jacob, D.E.; Andreae, M.O.

2012-01-01

The degree of transparency of glasses, which depends on the Fe content, may influence the ablation behavior during laser ablation-inductively coupled plasma-mass spectrometry (LA-ICP-MS) analysis. To test possible matrix effects when using a 193 nm Nd:YAG laser, we have analyzed transparent and opaque NIST, BAM and USGS reference glasses. These reference materials are ideal for such investigations, because they are well characterized, most elements are homogeneously distributed at the micrometer scale, and their Fe content varies over a very large range, from 16 to 130,000 μg g −1 . Our measurements show that the fractionation factors of refractory and volatile lithophile elements, such as Sr, Ba, and Rb, are 1.00 ± 0.03 and independent of the degree of transparency. However, for volatile chalcophile/siderophile elements (e.g., Zn and Pb) the fractionation factors vary significantly between 0.7 and 1, depending on the spot sizes and the transparency of the material. Mass-load-induced matrix effects may also influence the accuracy of LA-ICP-MS analysis. They are less than 2% for the lithophile and up to 10% for volatile chalcophile/siderophile elements when the mass load varies by a factor 2.4. Relative sensitivity factors used for calibration of lithophile elements agree within uncertainty limits for transparent and opaque glasses when using a 193 nm laser. Even for volatile/chalcophile elements they differ only by 5–10%. The reliability of the LA-ICP-MS analyses is demonstrated by presenting concentration data of 27 trace elements in the NIST, BAM and USGS reference glasses using NIST SRM 612 for calibration, where highly accurate reference values are available. For trace element concentrations in the range between 1 and 500 μg g −1 , the reproducibility and the uncertainties at the 95% confidence level of the measurements vary between 1–4%, and 7–10%, respectively. - Highlights: ► Matrix effects are low for lithophile elements using a 193 nm laser

Synthesis and Properties of Carbon Nanotube-Grafted Silica Nanoarchitecture-Reinforced Poly(Lactic Acid

Directory of Open Access Journals (Sweden)

Yao-Wen Hsu

2017-07-01

Full Text Available A novel nanoarchitecture-reinforced poly(lactic acid (PLA nanocomposite was prepared using multi-walled carbon nanotube (MWCNT-grafted silica nanohybrids as reinforcements. MWCNT-grafted silica nanohybrids were synthesized by the generation of silica nanoparticles on the MWCNT surface through the sol-gel technique. This synthetic method involves organo-modified MWCNTs that are dispersed in tetrahydrofuran, which incorporates tetraethoxysilane that undergoes an ultrasonic sol-gel process. Gelation yielded highly dispersed silica on the organo-modified MWCNTs. The structure and properties of the nanohybrids were established using 29Si nuclear magnetic resonance, Raman spectroscopy, wide-angle X-ray diffraction, thermogravimetric analysis, and transmission electron microscopy. The resulting MWCNT nanoarchitectures were covalently assembled into silica nanoparticles, which exhibited specific and controllable morphologies and were used to reinforce biodegradable PLA. The tensile strength and the heat deflection temperature (HDT of the PLA/MWCNT-grafted silica nanocomposites increased when the MWCNT-grafted silica was applied to the PLA matrix; by contrast, the surface resistivity of the PLA/MWCNT-grafted silica nanocomposites appeared to decline as the amount of MWCNT-grafted silica in the PLA matrix increased. Overall, the reinforcement of PLA using MWCNT-grafted silica nanoarchitectures was efficient and improved its mechanical properties, heat resistance, and electrical resistivity.

Li diffusion and the effect of local structure on Li mobility in Li2O-SiO2 glasses.

Science.gov (United States)

Bauer, Ute; Welsch, Anna-Maria; Behrens, Harald; Rahn, Johanna; Schmidt, Harald; Horn, Ingo

2013-12-05

Aimed to improve the understanding of lithium migration mechanisms in ion conductors, this study focuses on Li dynamics in binary Li silicate glasses. Isotope exchange experiments and conductivity measurements were carried out to determine self-diffusion coefficients and activation energies for Li migration in Li2Si3O7 and Li2Si6O13 glasses. Samples of identical composition but different isotope content were combined for diffusion experiments in couples or triples. Diffusion profiles developed between 511 and 664 K were analyzed by femtosecond laser ablation combined with multiple collector inductively coupled plasma mass spectrometry (fs LA-MC-ICP-MS) and secondary ion mass spectrometry (SIMS). Analyses of diffusion profiles and comparison of diffusion data reveal that the isotope effect of lithium diffusion in silicate glasses is rather small, consistent with classical diffusion behavior. Ionic conductivity of glasses was measured between 312 and 675 K. The experimentally obtained self-diffusion coefficient, D(IE), and ionic diffusion coefficient, D(σ), derived from specific DC conductivity provided information about correlation effects during Li diffusion. The D(IE)/D(σ) is higher for the trisilicate (0.27 ± 0.05) than that for the hexasilicate (0.17 ± 0.02), implying that increasing silica content reduces the efficiency of Li jumps in terms of long-range movement. This trend can be rationalized by structural concepts based on nuclear magnetic resonance (NMR) and Raman spectroscopy as well as molecular dynamic simulations, that is, lithium is percolating in low-dimensional, alkali-rich regions separated by a silica-rich matrix.

Fabrication and characterization of chromium-doped nanophase separated yttria-alumina-silica glass-based optical fibers

Energy Technology Data Exchange (ETDEWEB)

Dutta, Debjit; Dhar, Anirban; Das, Shyamal; Paul, Mukul C. [Fiber Optics and Photonics Division, CSIR-Central Glass and Ceramic Research Institute, Kolkata (India); Kir' yanov, Alexander V. [Centro de Investigaciones en Optica, Guanajuato (Mexico); Bysakh, Sandip [Electron Microscopic Section, Material Characterization Division, CSIR-Central Glass and Ceramic Research Institute, Kolkata (India)

2015-08-15

The basic material and optical properties of chromium-doped nanophase-separated yttria-alumina-silica (YAS) glass based optical preforms and fibers, fabricated through the modified chemical vapor deposition process in conjunction with solution doping technique under suitable thermal annealing conditions are reported. The size of the phase-separated particles within the core of the annealed preform is around 20-30 nm which is significantly reduced to around 5.0 nm in the drawn fiber. The absorption spectra of fibers drawn from the annealed and non-annealed preform samples revealed the presence of Cr{sup 4+}, Cr{sup 3+}, and Cr{sup 6+} specie. Numerically, extinction of absorption drops ∝3-3.5 times for the annealed sample as a result of nano-phase restructuration during annealing process. Intense broadband emission (within 500-800 nm) in case of the annealed preform sample is observed as compared to the non-annealed one and is associated with the presence of Cr{sup 3+} ions in nanostructured environment inside the YAS core glass. The final fibers show broadband emission ranging from 900 to 1400 nm under pumping at 1064 nm which is attributed mainly to the presence of Cr{sup 3+}/Cr{sup 4+} ions. The fabricated fibers seem to be a potential candidate for the development of fiber laser sources for the visible and near-infra ranges and for effective Q-switching units for ∝1-1.1 μm all-fiber ytterbium lasers. (copyright 2015 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim)

Colloidal silica films for high-capacity DNA arrays

Science.gov (United States)

Glazer, Marc Irving

The human genome project has greatly expanded the amount of genetic information available to researchers, but before this vast new source of data can be fully utilized, techniques for rapid, large-scale analysis of DNA and RNA must continue to develop. DNA arrays have emerged as a powerful new technology for analyzing genomic samples in a highly parallel format. The detection sensitivity of these arrays is dependent on the quantity and density of immobilized probe molecules. We have investigated substrates with a porous, "three-dimensional" surface layer as a means of increasing the surface area available for the synthesis of oligonucleotide probes, thereby increasing the number of available probes and the amount of detectable bound target. Porous colloidal silica films were created by two techniques. In the first approach, films were deposited by spin-coating silica colloid suspensions onto flat glass substrates, with the pores being formed by the natural voids between the solid particles (typically 23nm pores, 35% porosity). In the second approach, latex particles were co-deposited with the silica and then pyrolyzed, creating films with larger pores (36 nm), higher porosity (65%), and higher surface area. For 0.3 mum films, enhancements of eight to ten-fold and 12- to 14-fold were achieved with the pure silica films and the films "templated" with polymer latex, respectively. In gene expression assays for up to 7,000 genes using complex biological samples, the high-capacity films provided enhanced signals and performed equivalently or better than planar glass on all other functional measures, confirming that colloidal silica films are a promising platform for high-capacity DNA arrays. We have also investigated the kinetics of hybridization on planar glass and high-capacity substrates. Adsorption on planar arrays is similar to ideal Langmuir-type adsorption, although with an "overshoot" at high solution concentration. Hybridization on high-capacity films is

One-pot synthesis of hydroxyapatite–silica nanopowder composite ...

Indian Academy of Sciences (India)

(GIC) and Vickers hardness was evaluated. Results shown that the ... property might lead to extend the clinical indications, especially in stress bearing areas. Keywords. Hydroxyapatite–silica nanopowder; sol–gel technique; glass ionomer cement; hardness. 1. ..... A large hardness means greater resistance to plastic defor-.

Modeling of Viscosity and Thermal Expansion of Bioactive Glasses

OpenAIRE

Farid, Saad B. H.

2012-01-01

The behaviors of viscosity and thermal expansion for different compositions of bioactive glasses have been studied. The effect of phosphorous pentoxide as a second glass former in addition to silica was investigated. Consequently, the nonlinear behaviors of viscosity and thermal expansion with respect to the oxide composition have been modeled. The modeling uses published data on bioactive glass compositions with viscosity and thermal expansion. -regression optimization technique has been uti...

Ion beam assisted synthesis of nano-crystals in glasses (silver and lead chalcogenides)

International Nuclear Information System (INIS)

Espiau de Lamaestre, R.

2005-04-01

This work deals with the interest in ion beams for controlling nano-crystals synthesis in glasses. We show two different ways to reach this aim, insisting on importance of redox phenomena induced by the penetration and implantation of ions in glasses. We first show that we can use the great energy density deposited by the ions to tailor reducing conditions, favorable to metallic nano-crystal precipitation. In particular, we show that microscopic mechanism of radiation induced silver precipitation in glasses are analogous to the ones of classical photography. Ion beams can also be used to overcome supersaturation of elements in a given matrix. In this work, we synthesized lead chalcogenide nano-crystals (PbS, PbSe, PbTe) whose optical properties are interesting for telecommunication applications. We demonstrate the influence of complex chalcogenide chemistry in oxide glasses, and its relationship with the observed loss of growth control when nano-crystals are synthesized by sequential implantation of Pb and S in pure silica. As a consequence of this understanding, we demonstrate a novel and controlled synthesis of PbS nano-crystals, consisting in implanting sulfur into a Pb-containing glass, before annealing. Choice of glass composition provides a better control of precipitation physico-chemistry, whereas the use of implantation allows high nano-crystal volume fractions to be reached. Our study of IR emission properties of these nano-crystals shows a very high excitation cross section, and evidence for a 'dark exciton' emitting level. (author)

Self-diffusion of charged colloidal tracer spheres in transparent porous glass media: Effect of ionic strength and pore size

Science.gov (United States)

Kluijtmans, Sebastiaan G. J. M.; de Hoog, Els H. A.; Philipse, Albert P.

1998-05-01

The influence of charge on diffusion in porous media was studied for fluorescent colloidal silica spheres diffusing in a porous glass medium. The bicontinuous porous silica glasses were optically matched with an organic solvent mixture in which both glass and tracers are negatively charged. Using fluorescence recovery after photobleaching, the long-time self-diffusion coefficient DSL of the confined silica particles was monitored in situ as a function of the ionic strength and particle to pore size ratio. At high salt concentration DSL reaches a relatively high plateau value, which depends on the particle to pore size ratio. This plateau value is unexpectedly higher than the value found for uncharged silica spheres in these porous glasses, but still significantly smaller than the free particle bulk diffusion coefficient of the silica spheres. At low salt concentration DSL reduces markedly, up to the point where colloids are nearly immobilized. This peculiar retardation probably originates from potential traps and barriers at pore intersections due to deviations from cylinder symmetry in the double layer interactions between tracers and pore walls. This indicates that diffusion of charged particles in tortuous porous media may be very different from transport in long capillaries without such intersections.

Styrene grafted natural rubber reinforced by in situ silica generated via sol–gel technique

Energy Technology Data Exchange (ETDEWEB)

Sittiphan, Torpong [Program of Petrochemistry and Polymer Sciences, Faculty of Science, Chulalongkorn University, Bangkok 10330 (Thailand); Prasassarakich, Pattarapan [Department of Chemical Technology, Faculty of Science, Chulalongkorn University, Bangkok 10330 (Thailand); Poompradub, Sirilux, E-mail: sirilux.p@chula.ac.th [Department of Chemical Technology, Faculty of Science, Chulalongkorn University, Bangkok 10330 (Thailand)

2014-02-15

Highlights: • Sol–gel reaction by NR latex was the absence of use of organic solvent and base catalyst. • Well dispersed in situ formed silica particles in the rubber matrix were obtained. • In situ silica was better to improve mechanical properties of rubber vulcanizates. -- Abstract: The filling of styrene graft natural rubber (ST-GNR) with in situ formed silica was performed using the sol–gel reaction via the latex solution method. The mechanical properties of ST-GNR/NR vulcanizate were improved when using the in situ formed silica to levels higher than those obtained with the commercial ex situ formed silica filled ST-GNR/NR vulcanizates at a comparable silica content of 12 parts by weight per hundred parts of rubber. Transmission electron microscopy analysis revealed that the in situ silica particles were small (∼40 nm diameter) and well dispersed, while the commercial silica particles were larger (∼60 nm diameter) and markedly agglomerated in the rubbery matrix. The mechanical properties of the composites prepared via both the solid rubber and latex solution methods were comparable.

Effect of thermal treatments on sputtered silver nanocluster/silica composite coatings on soda-lime glasses: ionic exchange and antibacterial activity

Energy Technology Data Exchange (ETDEWEB)

Ferraris, M.; Ferraris, S., E-mail: sara.ferraris@polito.it; Miola, M.; Perero, S.; Balagna, C.; Verne, E. [Politecnico di Torino, Department of Applied Science and Technology, Institute of Materials Physics and Engineering (Italy); Gautier, G. [IMAMOTER Institute for Agricultural and Earthmoving Machines (Italy); Manfredotti, Ch.; Battiato, A.; Vittone, E. [University of Torino, Physics Department, NIS Excellence Centre and CNISM (Italy); Speranza, G. [Fondazione Bruno Kessler FBK (Italy); Bogdanovic, I. [Ruder Boskovic Institute, Experimental Physics Department (Croatia)

2012-12-15

Silver nanocluster/silica composite coatings were deposited on both soda-lime and silica glasses by radio frequency (RF) co-sputtering. The effect of thermal treatments on the microstructure in the range of 150-450 Degree-Sign C were examined by UV-visible spectroscopy, X-ray diffraction, X-ray photoelectron spectroscopy and Time of Flight-Elastic Recoil Detection Analysis. Sodium/silver ionic exchange was evidenced for coatings sputtered on soda-lime substrates after heating at 450 Degree-Sign C; presence of silver ions and/or silver nanoclusters, nanocluster size and their position inside the sputtered layers will be discussed for as-deposited and heated coatings on both substrates. The antibacterial activity of all coatings was determined against Staphylococcus aureus and Candida albicans by disk diffusion method and colonies forming units count; in agreement with microstructural results, the antibacterial activity present on all coatings was slightly reduced after heating at 450 Degree-Sign C. All coatings have been submitted to humidity plus UV ageing and sterilization by autoclave, gamma ray and ethylene oxide gas. Tape resistance (ASTM D3359-97) tests have been done on each coating before and after ageing and sterilizations, revealing a good adhesion on soda-lime substrates, except for those aged in humidity plus UV and sterilized by autoclave. Scratch tests and nanoindentation tests have been done on each coating, as-deposited and after heating at 450 Degree-Sign C. The coating hardness was improved by heating only when coatings were deposited on silica. The heating of coatings deposited on soda-lime substrates gave opposite effect on their hardness.

Silanization of silica and glass slides for DNA microarrays by impregnation and gas phase protocols: A comparative study

International Nuclear Information System (INIS)

Phaner-Goutorbe, Magali; Dugas, Vincent; Chevolot, Yann; Souteyrand, Eliane

2011-01-01

Surface immobilization of oligonucleotide probes (oligoprobes) is a key issue in the development of DNA-chips. The immobilization protocol should guarantee good availability of the probes, low non-specific adsorption and reproducibility. We have previously reported a silanization protocol with tert-butyl-11-(dimethylamino)silylundecanoate performed by impregnation (Impregnation Protocol, IP) of silica substrates from dilute silane solutions, leading to surfaces bearing carboxylic groups. In this paper, the Impregnation protocol is compared with a Gas phase Protocol (GP) which is more suited to industrial requirements such as reliable and robust processing, cost efficiency, etc.... The morphology of the oligoprobe films at the nanoscale (characterized by Atomic Force Microscopy) and the reproducibility of subsequent oligoprobes immobilization steps have been investigated for the two protocols on thermal silica (Si/SiO 2 ) and glass slide substrates. IP leads to smooth surfaces whereas GP induces the formation of islands features suggesting a non-continuous silane layer. The reproducibility of the overall surface layer (18.75 mm 2 ) has been evaluated through the covalent immobilization of a fluorescent oligoprobes. Average fluorescent signals of 6 (a.u.) and 4 (a.u.) were observed for IP and GP, respectively, with a standard deviation of 1 for both protocols. Thus, despite a morphological difference of the silane layer at the nanometer scale, the density of the immobilized probes remained similar.

Crystallization of Na2O-SiO2 gel and glass

Science.gov (United States)

Neilson, G. F.; Weinberg, M. C.

1984-01-01

The crystallization behavior of a 19 wt pct soda silica gel and gel-derived glass was compared to that of the ordinary glass of the same composition. Both bulk and ground glass samples were utilized. X-ray diffraction measurements were made to identify the crystalline phases and gauge the extent of crystallization. It was found that the gel crystallized in a distinctive manner, while the gel glass behavior was not qualitatively different from that of the ordinary glass.

In situ-growth of silica nanowires in ceramic carbon composites

Directory of Open Access Journals (Sweden)

Rahul Kumar

2017-09-01

Full Text Available An understanding of the processing and microstructure of ceramic–carbon composites is critical to development of these composites for applications needing electrically conducting, thermal shock resistant ceramic materials. In the present study green compacts of carbon ceramic composites were prepared either by slurry processing or dry powder blending of one or more of the three — clay, glass, alumina and carbon black or graphite. The dried green compacts were sintered at 1400 °C in flowing argon. The ceramic carbon composites except the ones without clay addition showed formation of silica nanowires. The silica nanowire formation was observed in both samples prepared by slip casting and dry powder compaction containing either carbon black or graphite. TEM micrographs showed presence of carbon at the core of the silica nanowires indicating that carbon served the role of a catalyst. Selected area electron diffraction (SAED suggested that the silica nanowires are amorphous. Prior studies have reported formation of silica nanowires from silicon, silica, silicon carbide but this is the first report ever on formation of silica nanowires from clay.

Morphology and stress at silicon-glass interface in anodic bonding