Sample records for si-o-c composite material

  1. Characterization of SiCf/SiC and CNT/SiC composite materials produced by liquid phase sintering

    International Nuclear Information System (INIS)

    Lee, J.K.; Lee, S.P.; Cho, K.S.; Byun, J.H.; Bae, D.S.

    2011-01-01

    This paper dealt with the microstructure and mechanical properties of SiC based composites reinforced with different reinforcing materials. The composites were fabricated using reinforcing materials of carbon nanotubes (CNT) and Tyranno Lox-M SiC chopped fibers. The volume fraction of carbon nanotubes was also varied in this composite system. An Al 2 O 3 -Y 2 O 3 powder mixture was used as a sintering additive in the consolidation of the SiC matrix. The characterization of the composites was investigated by means of SEM and three point bending tests. These composites showed a dense morphology of the matrix region, by the creation of a secondary phase. The composites reinforced with SiC chopped fibers possessed a flexural strength of about 400 MPa at room temperature. The flexural strength of the carbon nanotubes composites had a tendency to decrease with increased volume fraction of the reinforcing material.

  2. Status and prospects for SiC-SiC composite materials development for fusion applications

    International Nuclear Information System (INIS)

    Sharafat, S.; Jones, R.H.; Kohyama, A.; Fenici, P.

    1995-01-01

    Silicon carbide (SiC) composites are very attractive for fusion applications because of their low afterheat and low activation characteristics coupled with excellent high temperature properties. These composites are relatively new materials that will require material development as well as evaluation of hermiticity, thermal conductivity, radiation stability, high temperature strength, fatigue, thermal shock, and joining techniques. The radiation stability of SiC-SiC composites is a critical aspect of their application as fusion components and recent results will be reported. Many of the non-fusion specific issues are under evaluation by other ceramic composite development programs, such as the US national continuous fiber ceramic composites.The current development status of various SiC-SiC composites research and development efforts is given. Effect of neutron irradiation on the properties of SiC-SiC composite between 500 and 1200 C are reported. Novel high temperature properties specific to ceramic matrix composite (CMC) materials are discussed. The chemical stability of SiC is reviewed briefly. Ongoing research and development efforts for joining CMC materials including SiC-SiC composites are described. In conclusion, ongoing research and development efforts show extremely promising properties and behavior for SiC-SiC composites for fusion applications. (orig.)

  3. Characterization of SiC based composite materials by the infiltration of ultra-fine SiC particles

    International Nuclear Information System (INIS)

    Lee, J.K.; Lee, S.P.; Byun, J.H.

    2010-01-01

    The fabrication route of SiC materials by the complex compound of ultra-fine SiC particles and oxide additive materials has been investigated. Especially, the effect of additive composition ratio on the characterization of SiC materials has been examined. The characterization of C/SiC composites reinforced with plain woven carbon fabrics was also investigated. The fiber preform for C/SiC composites was prepared by the infiltration of complex mixture into the carbon fabric structure. SiC based composite materials were fabricated by a pressure assisted liquid phase sintering process. SiC materials possessed a good density higher than about 3.0 Mg/m 3 , accompanying the creation of secondary phase by the chemical reaction of additive materials. C/SiC composites also represented a dense morphology in the intra-fiber bundle region, even if this material had a sintered density lower than that of monolithic SiC materials. The flexural strength of SiC materials was greatly affected by the composition ratio of additive materials.

  4. SiOx/C composite from rice husks as an anode material for lithium-ion batteries

    International Nuclear Information System (INIS)

    Ju, Yanming; Tang, Joel A.; Zhu, Kai; Meng, Yuan; Wang, Chunzhong; Chen, Gang; Wei, Yingjin; Gao, Yu

    2016-01-01

    Highlights: • Rice husks were utilized to prepare SiO x /C as an anode material for lithium ion battery. • SiO x /C composite was prepared by a two-step fire process. • SiO x /C contains low valence silicon owing to thermal treatment at argon/hydrogen atmosphere. • SiO x /C exhibits a high specific capacity of nearly 600 mAh g −1 at 100 mA g −1 current density after 100 cycles. - Abstract: SiO x /C composite material derived directly from agricultural rice husk byproducts through an economically viable and environmentally benign approach has been explored to be used as an anode for rechargeable lithium batteries. Rice husks were converted into a SiO x /C composite directly by heat treatment under argon/hydrogen atmosphere, at a temperature of 900 °C. The composite contains SiO x surrounded by an amorphous carbon matrix. A steady state reversible capacity of nearly 600 mAh g −1 was delivered at 100 mA g −1 current density after 100 cycles. The improved performance of the SiO x /C composite anode over other agricultural byproduct derived carbon materials is believed to be due to the presence of low valence silicon. The filth-to-wealth conversion of rice husks to battery material is a highly energy efficient process with great economic and environmental benefits.

  5. Synthesis and electrochemical characterization of mesoporous Li2FeSiO4/C composite cathode material for Li-ion batteries

    Science.gov (United States)

    Kumar, Ajay; Jayakumar, O. D.; Bazzi, Khadije; Nazri, Gholam-Abbas; Naik, Vaman M.; Naik, Ratna

    2015-03-01

    Lithium iron silicate (Li2FeSiO4) has the potential as cathode for Li ion batteries due to its high theoretical capacity (~ 330 mAh/g) and improved safety. The application of Li2FeSiO4 as cathode material has been challenged by its poor electronic conductivity and slow lithium ion diffusion in the solid phase. In order to solve these problems, we have synthesized mesoporous Li2FeSiO4/C composites by sol-gel method using the tri-block copolymer (P123) as carbon source. The phase purity and morphology of the composite materials were characterized by x-ray diffraction, SEM and TEM. The XRD pattern confirmed the formation of ~ 12 nm size Li2FeSiO4 crystallites in composites annealed at 600 °C for 6 h under argon atmosphere. The electrochemical properties are measured using the composite material as positive electrode in a standard coin cell configuration with lithium as the active anode and the cells were tested using AC impedance spectroscopy, cyclic voltammetry, and galvanostatic charge/discharge cycling. The Li2FeSiO4/C composites showed a discharge capacity of ~ 240 mAh/g at a rate of C/30 at room temperature. The effect of different annealing temperature and synthesis time on the electrochemical performance of Li2FeSiO4/C will be presented.

  6. Thermal shock properties of 2D-SiCf/SiC composites

    International Nuclear Information System (INIS)

    Lee, Sang Pill; Lee, Jin Kyung; Son, In Soo; Bae, Dong Su; Kohyama, Akira

    2012-01-01

    This paper dealt with the thermal shock properties of SiC f /SiC composites reinforced with two dimensional SiC fabrics. SiC f /SiC composites were fabricated by a liquid phase sintering process, using a commercial nano-size SiC powder and oxide additive materials. An Al 2 O 3 –Y 2 O 3 –SiO 2 powder mixture was used as a sintering additive for the consolidation of SiC matrix region. In this composite system, Tyranno SA SiC fabrics were also utilized as a reinforcing material. The thermal shock test for SiC f /SiC composites was carried out at the elevated temperature. Both mechanical strength and microstructure of SiC f /SiC composites were investigated by means of optical microscopy, SEM and three point bending test. SiC f /SiC composites represented a dense morphology with a porosity of about 8.2% and a flexural strength of about 160 MPs. The characterization of SiC f /SiC composites was greatly affected by the history of cyclic thermal shock. Especially, SiC f /SiC composites represented a reduction of flexural strength at the thermal shock temperature difference higher than 800 °C.

  7. Investigation on fabrication of SiC/SiC composite as a candidate material for fuel sub-assembly

    International Nuclear Information System (INIS)

    Lee, Jae-Kwang; Naganuma, Masayuki; Park, Joon-Soo; Kohyama, Akira

    2005-01-01

    The possibility of SiC/SiC (Silicon carbide fiber reinforced Silicon carbide) composites application for fuel sub-assembly of Fast Breeder Reactor was investigated. To select a raw material of SiC/SiC composites, a few kinds of SiC nano powder was estimated by SEM observation and XRD analysis. Furthermore, SiC monolithic was sintered from them and estimated by flexural test. SiC nano-powder which showed good sinterability, it was used for fabrication of SiC/SiC composites by Hot Pressing method. From the sintering condition of 1800, 1820degC temperature and 15, 20 MPa pressure, SiC/SiC composite was fabricated and then estimated by tensile test. SiC/SiC composite, which made by 1820degC and 20 MPa condition, showed the highest mechanical strength by the monotonic tensile test. SiC/SiC composite, which made by 1800degC and 15 MPa condition, showed a stable fracture behavior at the monotonic and cyclic tensile test. And then, the hoop stress of ideal model of SiC/SiC composites was discussed. It was confirmed that applicability of SiC/SiC composites by Hot Pressing method for fuel sub-assembly structural material. To make it real attractive one, to maintain the reliability and safety as a high temperature structural material, the design and process study on SiC/Sic composites material will be continued. (author)

  8. Optimal determination of the elastic constants of woven 2D SiC/SiC composite materials

    International Nuclear Information System (INIS)

    Mouchtachi, A; Guerjouma, R El; Baboux, J C; Rouby, D; Bouami, D

    2004-01-01

    For homogeneous materials, the ultrasonic immersion method, associated with a numerical optimization process mostly based on Newton's algorithm, allows the determination of elastic constants for various synthetic and natural composite materials. Nevertheless, a principal limitation of the existing optimization procedure occurs when the considered material is at the limit of the homogeneous hypothesis. Such is the case of the woven bidirectional SiC matrix and SiC fibre composite material. In this study, we have developed two numerical methods for the determination of the elastic constants of the 2D SiC/SiC composite material (2D SiC/SiC). The first one is based on Newton's algorithm: the elastic constants are obtained by minimizing the square deviation between experimental and calculated velocities. The second method is based on the Levenberg-Marquardt algorithm. We show that these algorithms give the same results in the case of homogeneous anisotropic composite materials. For the 2D SiC/SiC composite material, the two methods, using the same measured velocities, give different sets of elastic constants. We then note that the Levenberg-Marquardt algorithm enables a better convergence towards a global set of elastic constants in good agreement with the elastic properties, which can be measured using classical quasi-static methods

  9. Mechanical characterization of Si-C(O) fiber/SiC (CVI) matrix composites with a BN-interphase

    International Nuclear Information System (INIS)

    Prouhet, S.; Camus, G.; Labrugere, C.; Guette, A.; Martin, E.

    1994-01-01

    The mechanical behavior of three CVI-processed 2D woven SiC/BN/SiC composite materials with different initial BN interphase thicknesses has been investigated by means of tensile and impact tests. The results have established the efficiency of a BN interphase in promoting a nonlinear/noncatastrophic tensile behavior and high impact resistance. The effect of the initial BN interphase thickness on the resulting mechanical behavior has also been demonstrated. AES and TEM has revealed the presence of a SiO 2 /C double layer at the BN/fiber interface, which might result from a decomposition undergone by the Si-C(O) Nicalon fiber during processing. It has been suggested that the influence of the initial BN interphase thickness on the mechanical properties of the composites results from both changes occurring in the composition and morphology of the interfacial zones and modifications of the interfacial forces due to accommodation of the radial residual clamping stress

  10. Functional materials - Study of process for CVD SiC/C composite material

    Energy Technology Data Exchange (ETDEWEB)

    Choi, Doo Jin; Wang, Chae Chyun; Lee, Young Jin; Oh, Byung Jun [Yonsei University, Seoul (Korea)

    2000-04-01

    The CVD SiC coating techniques are the one of high functional material manufactures that improve the thermal, wear, oxidization and infiltration resistance of the surface of raw materials and extend the life of material. Silicon carbide films have been grown onto graphite substrates by low pressure chemical vapor deposition using MTS(CH{sub 3}SiCl{sub 3}) as a source precursor and H{sub 2} or N{sub 2} as a diluent gas. The experiments for temperature and diluent gas addition changes were performed. The effect of temperature from 900 deg. C to 1350 deg. C and the alteration of diluent gas species on the growth rate and structure of deposits have been studied. The experimental results showed that the deposition rate increased with increasing deposition temperature irrespective of diluent gases and reactant depletion effect increased especially at H{sub 2} diluent gas ambient. As the diluent gas added, the growth rate decreased parabolically. For N{sub 2} addition, surface morphology of leaf-like structure appeared, and for H{sub 2}, faceted structure at 1350 deg. C. The observed features were involved by crystalline phase of {beta}-SiC and surface composition with different gas ambient. We also compared the experimental results of the effect of partial pressure on the growth rate with the results of theoretical approach based on the Langmuir-Hinshelwood model. C/SiC composites were prepared by isothermal chemical vapor infiltration (ICVI). In order to fabricate the more dense C/SiC composites, a novel process of the in-situ whisker growing and filling during ICVI was devised, which was manipulated by alternating dilute gas species. The denser C/SiC composites were successfully prepared by the novel process comparing with the conventional ICVI process. 64 refs., 36 figs., 5 tabs. (Author)

  11. Rational Design of Si@SiO2/C Composites Using Sustainable Cellulose as a Carbon Resource for Anodes in Lithium-Ion Batteries.

    Science.gov (United States)

    Shen, Dazhi; Huang, Chaofan; Gan, Lihui; Liu, Jian; Gong, Zhengliang; Long, Minnan

    2018-03-07

    In this work, we propose a novel and facile route for the rational design of Si@SiO 2 /C anode materials by using sustainable and environment-friendly cellulose as a carbon resource. To simultaneously obtain a SiO 2 layer and a carbon scaffold, a specially designed homogeneous cellulose solution and commercial Si nanopowder are used as the starting materials, and the cellulose/Si composite is directly assembled by an in situ regenerating method. Subsequently, Si@SiO 2 /C composite is obtained after carbonization. As expected, Si@SiO 2 is homogeneously encapsulated in the cellulose-derived carbon network. The obtained Si@SiO 2 /C composite shows a high reversible capacity of 1071 mA h g -1 at a current density of 420 mA g -1 and 70% capacity retention after 200 cycles. This novel, sustainable, and effective design is a promising approach to obtain high-performance and cost-effective composite anodes for practical applications.

  12. Formation of permeation barriers on ceramic SiC/SiC composites

    International Nuclear Information System (INIS)

    Racault, C.; Fenici, P.

    1996-01-01

    The effectiveness as permeation barriers of the following CVD and PVD (sputtering) coatings has been investigated: TiC+Al 2 O 3 (CVD), SiC(CVD), SiO 2 (CVD), TiN(CVD), TiN(CVD)+TiN(PVD) and SiC(CVD)+Al 2 O 3 (PVD). The substrate material was a SiC/SiC composite, proposed as low activation structural material for fusion applications. Permeation measurements were performed in the temperature range 300-750 K using deuterium at pressures in the range 0.5-150 kPa. A linear dependence of permeation rate on pressure was measured. The efficiency of the coatings as deuterium permeation barriers is discussed in terms of coating microstructure. The best result was obtained with a bilayer of TiN(CVD) (15 μm) +TiN(PVD) (8 μm). (orig.)

  13. Low dose irradiation performance of SiC interphase SiC/SiC composites

    International Nuclear Information System (INIS)

    Snead, L.L.; Lowden, R.A.; Strizak, J.; More, K.L.; Eatherly, W.S.; Bailey, J.; Williams, A.M.; Osborne, M.C.; Shinavski, R.J.

    1998-01-01

    Reduced oxygen Hi-Nicalon fiber reinforced composite SiC materials were densified with a chemically vapor infiltrated (CVI) silicon carbide (SiC) matrix and interphases of either 'porous' SiC or multilayer SiC and irradiated to a neutron fluence of 1.1 x 10 25 n m -2 (E>0.1 MeV) in the temperature range of 260 to 1060 C. The unirradiated properties of these composites are superior to previously studied ceramic grade Nicalon fiber reinforced/carbon interphase materials. Negligible reduction in the macroscopic matrix microcracking stress was observed after irradiation for the multilayer SiC interphase material and a slight reduction in matrix microcracking stress was observed for the composite with porous SiC interphase. The reduction in strength for the porous SiC interfacial material is greatest for the highest irradiation temperature. The ultimate fracture stress (in four point bending) following irradiation for the multilayer SiC and porous SiC interphase materials was reduced by 15% and 30%, respectively, which is an improvement over the 40% reduction suffered by irradiated ceramic grade Nicalon fiber materials fabricated in a similar fashion, though with a carbon interphase. The degradation of the mechanical properties of these composites is analyzed by comparison with the irradiation behavior of bare Hi-Nicalon fiber and Morton chemically vapor deposited (CVD) SiC. It is concluded that the degradation of these composites, as with the previous generation ceramic grade Nicalon fiber materials, is dominated by interfacial effects, though the overall degradation of fiber and hence composite is reduced for the newer low-oxygen fiber. (orig.)

  14. Thermogravimetric and microscopic analysis of SiC/SiC materials with advanced interfaces

    Energy Technology Data Exchange (ETDEWEB)

    Windisch, C.F. Jr.; Jones, R.H. [Pacific Northwest National Lab., Richland, WA (United States); Snead, L.L. [Oak Ridge National Lab., TN (United States)

    1997-04-01

    The chemical stability of SiC/SiC composites with fiber/matrix interfaces consisting of multilayers of SiC/SiC and porous SiC have been evaluated using a thermal gravimetric analyzer (TGA). Previous evaluations of SiC/SiC composites with carbon interfacial layers demonstrated the layers are not chemically stable at goal use temperatures of 800-1100{degrees}C and O{sub 2} concentrations greater than about 1 ppm. No measureable mass change was observed for multilayer and porous SiC interfaces at 800-1100{degrees}C and O{sub 2} concentrations of 100 ppm to air; however, the total amount of oxidizable carbon is on the order of the sensitivity of the TGA. Further studies are in progress to evaluate the stability of these materials.

  15. Synthesis and electrochemical performance of Li2FeSiO4/C/carbon nanosphere composite cathode materials for lithium ion batteries

    International Nuclear Information System (INIS)

    Yang, Jinlong; Kang, Xiaochun; Hu, Lin; Gong, Xue; He, Daping; Peng, Tao; Mu, Shichun

    2013-01-01

    Highlights: •The Li 2 FeSiO 4 /C/CNS was prepared by effective double-carbon composite route. •The CNS as the conductivity belt connects the Li 2 FeSiO 4 /C particles. •The samples have a high capacity and excellent cyclic and rate performance. -- Abstract: Li 2 FeSiO 4 /C/carbon nanosphere (CNS) composites as cathode materials for lithium-ion batteries were synthesized by a simple hydro-chemical method. The double-carbon structural design of glucose pyrolysis-carbon (C) and CNS improved electrochemical performance of the composite where the CNS can build conductivity belts to connect the Li 2 FeSiO 4 /C particles and to favor electronic transmission. The exchange current density and the diffusion coefficient of lithium ions with the composite were 0.208 mA cm −2 and 1.06E−11 cm 2 S −1 , respectively, which were much larger than that of conventional Li 2 FeSiO 4 /C composite cathode materials (i = 0.131 mA cm −2 , D Li = 4.69E−12 cm 2 S −1 ). The electrochemical test results showed that the discharge capacity of 164.7 mA h g −1 could be obtained, and especially, after 60 cycles, 98.4% of the initial discharge capacity remained at 0.1 C of galvanostatic discharge in the potential range of 1.5–4.8 V (vs. Li/Li + ). In addition, the discharge capacity of 92.4 mA h g −1 at 5 C was easily recovered to 159.8 mA h g −1 at 0.1 C

  16. Compósitos SiCf /SiC utilizados em sistemas de proteção térmica SiCf /SiC composites for thermal protection systems

    Directory of Open Access Journals (Sweden)

    M. Florian

    2005-09-01

    Full Text Available Compósitos de carbeto de silício (SiC reforçado com fibras de carbeto de silício (SiCf são materiais candidatos em potencial para utilização em sistemas de proteção térmica em altas temperaturas devido principalmente à boa condutividade térmica na direção da fibra e muito baixa condutividade térmica na direção transversal à fibra, alta dureza, estabilidade térmica e à corrosão por oxidação. O compósito SiCf/SiC possui uma matriz de SiC reforçada com fibras contínuas policristalinas de SiC e é obtido por reações de conversão em altas temperaturas e atmosfera controlada, utilizando o compósito carbono/carbono como precursor. O processo de Reação Química em Vapor (CVR foi utilizado para a fabricação de compósitos SiCf/SiC com alta pureza na fase de SiC-beta. O compósito precursor de carbono/carbono foi fabricado com fibra de carbono não estabilizada e matriz carbonosa derivada da resina fenólica na forma de carbono isotrópico. O compósito convertido exibiu uma densidade de 1,75 g/cm³, com 40% de porosidade aberta e resistência à flexão de 80 MPa medida por ensaio flexão em 4 pontos. A área especifica medida pela técnica de BET é dependente da temperatura de conversão e das condições inicias do precursor de carbono, podendo chegar a 18 m²/g.Composites based on silicon carbide are potential candidate materials for thermal protection systems mainly due to its good thermal conductivity in fiber direction and very low transversal thermal conductivity, high hardness, corrosion and thermal resistance. SiCf/SiC composite presents a SiC matrix reinforced with SiC polycrystalline continuous fibers. The composite was obtained by conversion reactions at high temperature and controlled atmosphere from a carbon/carbon composite precursor. The CVR process was used to fabricate SiC /SiC composite with crystalline high-purity beta-SiC from a carbon-carbon precursor fabricated with non-stabilized carbon fiber and

  17. Novel SiO2-C composite adsorptive material

    Directory of Open Access Journals (Sweden)

    Volzone, C.

    2001-08-01

    Full Text Available The present work is about the development of a Novel Composite that has several properties in only one material. This material is composed by a silica network with a sharpened pore size distribution - diameter near 1000 Å - intercrossed with another carbon network that has carbonaceous microdomains of high activity. The first network facilitates the entrance of big molecules to the interior of the material grains so they quickly reach the active sites of the carbonous network, minimizing the diffusional resistance observed when high performance activated carbons are used in adsorption processes or catalytic applications. These two intercrossed structures are self-supporting and independent among them, so one from the other can be isolated without losing the original shape and volume of the starting composite, then, their possible uses may be multiplied. The Novel Composite is stable with respect to other support or adsorbent materials due to its high obtention temperature (1550 ºC. The obtention methods of the composite and its isolated structures are described. The material was characterized by different techniques (XRD, IR, Loss on ignition, pore size distribution, specific surface area, adsorption desorption isotherms, methylene blue adsorption and SEM.En el presente trabajo se describe el desarrollo de un nuevo material compuesto que reúne distintas propiedades en un solo material. Dicho material está formado por una red de sílice con distribución de tamaño de poro estrecha - diámetro cercano a los 1000 Å - entrecruzada con otra red de carbón pseudografítica donde los microdominios carbonosos son de alta actividad. La primer red facilita la entrada de grandes moléculas al interior de los granos del material permitiendo su rápido acceso a los sitios activos de la red carbonosa, esto minimiza la resistencia difusional observada cuando se utilizan carbones activados de alto rendimiento en los procesos de adsorción o aplicaciones

  18. Preparação e caracterização de materiais compósitos SiC/caulim/Al via "squeeze-casting" Preparation and characterization of SiC/kaolin/Al composite materials by squeeze- casting

    Directory of Open Access Journals (Sweden)

    M. Freitas

    2009-09-01

    Full Text Available Na busca de materiais com propriedades diferenciadas, vem aumentando nos últimos anos as pesquisas em materiais compósitos. Um dos importantes métodos de fabricação destes compósitos é o processo de infiltração sob pressão de metal fundido denominado "squeeze-casting". Este processo oferece algumas vantagens, tais como facilidade de produzir o compósito, baixo custo e capacidade de formação de estruturas em rede. Neste trabalho foram produzidos e caracterizados compósitos SiC-Al, com concentrações em caulim variando entre 10 e 50% em substituição a fase majoritária SiC. As pré-formas cerâmicas foram produzidas controlando-se a fração granulométrica do SiC/caulim para uma melhor infiltração. Estas pré-formas, após sinterização a 1100 ºC/1 h, resultaram altamente porosas, sendo a porosidade aumentada com o aumento do caulim em substituição ao SiC. Análises de DRX mostraram a existência de partículas de quartzo além da fase SiC como constituintes das pré-formas. Durante o processo de infiltração e tratamento térmico, o alumínio no estado líquido reagiu preferencialmente com o quartzo e outros aluminossilicatos da pré-forma reduzindo-os, precipitando alumina e silício na microestrutura, a qual apresentou também alumínio em excesso que não reagiu no processo. A sílica e os silicatos da pré-forma, ao reagirem preferencialmente com o alumínio, evitaram a reação do Al com o SiC, prevenindo a formação da fase Al4C3,, a qual é altamente higroscópica e causa a degradação do compósito. Dependendo da composição, os compósitos SiC-caulim-Al desenvolvidos neste trabalho, podem ser usados em aplicações que envolvam elevada resistência mecânica à flexão (240 a 300 MPa, baixa densidade e dureza superficial entre 180 e 380 kgf/mm².In search of materials with different properties, has been increasing the research on composite materials in recent years. One of the important methods of

  19. High-temperature mechanical and material design for SiC composites

    International Nuclear Information System (INIS)

    Ghoniem, N.M.

    1992-01-01

    Silicon Carbide (SiC) fiber reinforced composites (FRC's) are strong potential candidate structural and high heat flux materials for fusion reactors. During this past decade, they have been vigorously developed for use in aerospace and transportation applications. Recent fusion reactor systems studies, such as ARIES, have concluded that further development of SiC composites will result in significant safety, operational, and waste disposal advantages for fusion systems. A concise discussion of the main material and design issues related to the use of SiC FRC's as structural materials in future fusion systems is given in this paper. The status of material processing of SiC/SiC composites is first reviewed. The advantages and shortcomings of the leading processing technology, known as Chemical Vapor Infiltration are particularly highlighted. A brief outline of the design-relevant physical, mechanical, and radiation data base is then presented. SiC/SiC FRC's possess the advantage of increased apparent toughness under mechanical loading conditions. This increased toughness, however, is associated with the nucleation and propagation of small crack patterns in the structure. Design approaches and failure criteria under these conditions are discussed

  20. Porous SiC/SiC composites development for industrial application

    International Nuclear Information System (INIS)

    Maeta, S.; Hinoki, T.

    2014-01-01

    Silicon carbide (SiC) is promising structural materials in nuclear fields due to an excellent irradiation resistance and low activation characteristics. Conventional SiC fibers reinforced SiC matrix (SiC/SiC composites) fabricated by liquid phase sintering (LPS-SiC/SiC composites) have been required high cost and long processing time. And microstructure and mechanical property data of finally obtained LPS-SiC/SiC composites are easily scattered, because quality of the composites depend on personal skill. Thus, conventional LPS-SiC/SiC composites are inadequate for industrial use. In order to overcome these issues, the novel “porous SiC/SiC composites” have been developed by means of liquid phase sintering fabrication process. The composites consist of porous SiC matrix and SiC fibers without conventional carbon interfacial layer. The composites don’t have concerns of the degradation interfacial layer at the severe accident. Porous SiC/SiC composites preform was prepared with a thin sheet shape of SiC, sintering additives and carbon powder mixture by tape casting process which was adopted because of productive and high yielding rate fabrication process. The preform was stacked with SiC fibers and sintered in hot-press at the high temperature in argon environment. The sintered preform was decarburized obtain porous matrix structure by heat-treatment in air. Moreover, mechanical property data scattering of the obtained porous SiC/SiC composites decreased. In the flexural test, the porous SiC/SiC composites showed pseudo-ductile behavior with sufficient strength even after heat treatment at high temperature in air. From these conclusions, it was proven that porous SiC/SiC composites were reliable material at severe environment such as high temperature in air, by introducing tape casting fabrication process that could produce reproducible materials with low cost and simple way. Therefore development of porous SiC/SiC composites for industrial application was

  1. Irradiation effect on Nite-SiC/SiC composites

    International Nuclear Information System (INIS)

    Hinoki, T.; Choi, Y.B.; Kohyama, A.; Ozawa, K.

    2007-01-01

    Full text of publication follows: Silicon carbide (SiC) and SiC composites are significantly attractive materials for nuclear application in particular due to exceptional low radioactivity, excellent high temperature mechanical properties and chemical stability. Despite of the excellent potential of SiC/SiC composites, the prospect of industrialization has not been clear mainly due to the low productivity and the high material cost. Chemical vapor infiltration (CVI) method can produce the excellent SiC/SiC composites with highly crystalline and excellent mechanical properties. It has been reported that the high purity SiC/SiC composites reinforced with highly crystalline fibers and fabricated by CVI method is very stable to neutron irradiation. However the production cost is high and it is difficult to fabricate thick and dense composites by CVI method. The novel processing called Nano-powder Infiltration and Transient Eutectic Phase (NITE) Processing has been developed based on the liquid phase sintering (LPS) process modification. The NITE processing can achieve both the excellent material quality and the low processing cost. The productivity of the processing is also excellent, and various kinds of shape and size of SiC/SiC composites can be produced by the NITE processing. The NITE processing can form highly crystalline matrix, which is requirement for nuclear application. The objective of this work is to understand irradiation effect of the NITESiC/SiC composites. The SiC/SiC composites used were reinforced with high purity SiC fibers, Tyranno TM SA and fabricated by the NITE method. The NITE-SiC/SiC composite bars and reference monolithic SiC bars fabricated by CVI and NITE were irradiated at up to 1.0 dpa and 600-1000 deg. C at JMTR, Japan. Mechanical properties of non-irradiated and irradiated NITESiC/ SiC composites bars were evaluated by tensile tests. Monolithic SiC bars were evaluated by flexural tests. The fracture surface was examined by SEM. Ultimate

  2. Neutron tolerance of advanced SiC-fiber/CVI-SiC composites

    International Nuclear Information System (INIS)

    Katoh, Y.; Kohyama, A.; Snead, L.L.; Hinoki, T.; Hasegawa, A.

    2003-01-01

    Fusion blankets employing a silicon carbide (SiC) fiber-reinforced SiC matrix composite (SiC/SiC composite) as the structural material provide attractive features represented by high cycle efficiency and extremely low induced radioactivity. Recent advancement in processing and utilization techniques and application studies in ceramic gas turbine and advanced transportation systems, SiC/SiC composites are steadily getting matured as industrial materials. Reference SiC/SiC composites for fusion structural applications have been produced by a forced-flow chemical vapor infiltration (FCVI) method using conventional and advanced near-stoichiometric SiC fibers and extensively evaluated primarily in Japan-US collaborative JUPITER program. In this work, effect of neutron irradiation at elevated temperatures on mechanical property of these composites is characterized. Unlike in conventional SiC/SiC composites, practically no property degradation was identified in advanced composites with a thin carbon interphase by a neutron fluence level of approximately 8dpa at 800C. (author)

  3. Interface reactions in the Al-Si-SiC and Mg-Al-Al{sub 2}O{sub 3} composite systems

    Energy Technology Data Exchange (ETDEWEB)

    Johnson, P.K. [Commission of the European Communities, Petten (Netherlands). Inst. for Advanced Materials; Fazal-Ur-Rehman [Imperial Coll. of Science, Technology and Medicine, London (United Kingdom). Dept. of Materials; Fox, S. [Imperial Coll. of Science, Technology and Medicine, London (United Kingdom). Dept. of Materials; Flower, H.M. [Imperial Coll. of Science, Technology and Medicine, London (United Kingdom). Dept. of Materials; West, D.R.F.

    1995-12-31

    Structural and compositional observations are reported on the influence of the interfaces on the mechanisms and kinetics of liquid metal-ceramic reactions in Al-SiC, Al-Si-SiC, Mg-Al{sub 2}O{sub 3} and Mg-Al-Al{sub 2}O{sub 3} composites. The aluminium based materials contained up to 20 vol% SiC in particulate form, and were produced by a spray casting process; subsequently the interface reactions were studied in samples heated to temperatures up to 1100 C. The reaction product was Al{sub 4}C{sub 3} in both Al-SiC and Al-Si-SiC composites. The influence of the crystallography and topology of the SiC particle surfaces on the nucleation of the Al{sub 4}C{sub 3} has been demonstrated; surface asperities play an important role. Growth of nuclei proceeds to form continuous reaction product layers which control the subsequent kinetics. The magnesium based composites contained 5 vol% Al{sub 2}O{sub 3} fibres (3 {mu}m in diameter), and were produced by a liquid infiltration process. SD Safimax fibres with relatively low and high porosity, and also RF Saffil fibres, with a silica binder, were investigated. Fibre porosity plays a major role in accelerating the penetration of Mg into the fibres with reaction to form MgO. Silica binder on the fibre surface transforms to MgO. The reaction rate was reduced by the presence of aluminium in the matrix. The factors controlling the reactions in the aluminium and magnesium based composites are compared. (orig.)

  4. Oxidation protection of multilayer CVD SiC/B/SiC coatings for 3D C/SiC composite

    International Nuclear Information System (INIS)

    Liu Yongsheng; Cheng Laifei; Zhang Litong; Wu Shoujun; Li Duo; Xu Yongdong

    2007-01-01

    A CVD boron coating was introduced between two CVD SiC coating layers. EDS and XRD results showed that the CVD B coating was a boron crystal without other impurity elements. SEM results indicated that the CVD B coating was a flake-like or column-like crystal with a compact cross-section. The crack width in the CVD SiC coating deposited on CVD B is smaller than that in a CVD SiC coating deposited on CVD SiC coating. After oxidation at 700 deg. C and 1000 deg. C, XRD results indicated that the coating was covered by product B 2 O 3 or B 2 O 3 .xSiO 2 film. The cracks were sealed as observed by SEM. There was a large amount of flake-like material on hybrid coating surface after oxidation at 1300 deg. C. Oxidation weight loss and residual flexural strength results showed that hybrid SiC/B/SiC multilayer coating provided better oxidation protection for C/SiC composite than a three layer CVD SiC coating at temperatures from 700 deg. C to 1000 deg. C for 600 min, but worse oxidation protection above 1000 deg. C due to the large amount of volatilization of B 2 O 3 or B 2 O 3 .xSiO 2

  5. Conversion of wood flour/SiO2/phenolic composite to porous SiC ceramic containing SiC whiskers

    Directory of Open Access Journals (Sweden)

    Li Zhong

    2013-01-01

    Full Text Available A novel wood flour/SiO2/phenolic composite was chosen to be converted into porous SiC ceramic containing SiC whiskers via carbothermal reduction. At 1550°C the composite is converted into porous SiC ceramic with pore diameters of 10~40μm, and consisting of β-SiC located at the position of former wood cell walls. β-SiC wire-like whiskers of less than 50 nm in diameter and several tens to over 100 μm in length form within the pores. The surface of the resulting ceramic is coated with β-SiC necklace-like whiskers with diameters of 1~2μm.

  6. SiC-C Composite as A Highly Stable and Easily Regenerable Photothermal Material for Practical Water Evaporation

    KAUST Repository

    Shi, Le

    2018-05-26

    Solar-driven water distillation by photothermal materials is emerging as a promising way of renewable energy-driven clean water production. In designing photothermal materials, light absorption, photo-to-thermal conversion efficiency, and ability to localize thermal energy at the water-air interface are three important considerations. However, one additional consideration, regenerability, has so far slipped out of the photothermal material designs at status quo. This work reveals that there is a fouling layer formed during photothermal evaporation of real seawater (Red Sea water) and domestic wastewater, which once formed, would be difficult to remove. Herein, we synthesize a SiC-C composite monolith as an effective photothermal material where carbon acts as photothermal component and SiC serves as a heat conductor and strong structural support. The high mechanical strength of the monolithic composite makes it able to withstand repeatedly high strength physical cleaning by brush scrubbing and sonication and the anti-carbon-loss mechanism generates zero carbon loss during the physical cleaning. In the case of the domestic wastewater evaporation, the bio- and organic foulants on the SiC-C composite monolith can be totally removed by annealing at 1000 oC in N2 atmosphere. We believe that the SiC-C composite monoliths are promising photothermal materials in practical solar-driven water evaporation applications thanks to their highly stable and easily regenerable properties and therefore more research efforts are warranted to further improve their performances.

  7. SiC/SiC Cladding Materials Properties Handbook

    Energy Technology Data Exchange (ETDEWEB)

    Snead, Mary A. [Brookhaven National Lab. (BNL), Upton, NY (United States); Katoh, Yutai [Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States); Koyanagi, Takaaki [Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States); Singh, Gyanender P. [Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States)

    2017-08-01

    When a new class of material is considered for a nuclear core structure, the in-pile performance is usually assessed based on multi-physics modeling in coordination with experiments. This report aims to provide data for the mechanical and physical properties and environmental resistance of silicon carbide (SiC) fiber–reinforced SiC matrix (SiC/SiC) composites for use in modeling for their application as accidenttolerant fuel cladding for light water reactors (LWRs). The properties are specific for tube geometry, although many properties can be predicted from planar specimen data. This report presents various properties, including mechanical properties, thermal properties, chemical stability under normal and offnormal operation conditions, hermeticity, and irradiation resistance. Table S.1 summarizes those properties mainly for nuclear-grade SiC/SiC composites fabricated via chemical vapor infiltration (CVI). While most of the important properties are available, this work found that data for the in-pile hydrothermal corrosion resistance of SiC materials and for thermal properties of tube materials are lacking for evaluation of SiC-based cladding for LWR applications.

  8. Tribological Characteristics of C/C-SiC-Cu Composite and Al/SiC Composite Materials under Various Contact Conditions

    International Nuclear Information System (INIS)

    Kim, Byung-Kook; Shin, Dong-Gap; Kim, Chang-Lae; Kim, Dae-Eun; Goo, Byeong-Choon

    2017-01-01

    The surface temperature of disc brakes varies during braking, which can affect the friction and wear behavior of braking systems. In order to develop an efficient braking system, the friction and wear behaviors of brake materials need to be clearly understood. In this work, the friction and wear behavior of the C/C-SiC-Cu composite and the Al/SiC composite, which are used in disc braking systems, were investigated. Both the surface temperature and contact pressure were studied. A pin-on-reciprocating tribotester was used for this purpose, in order to control temperature and load. Results showed that the friction varied significantly with temperature and sliding distance. It was found that a transfer layer of compacted wear debris formed on the wear track of the two materials. These layers caused the surface roughness of the wear track to increase. The outcome of this work is expected to serve as a basis for the development of braking systems under various operating conditions.

  9. Tribological Characteristics of C/C-SiC-Cu Composite and Al/SiC Composite Materials under Various Contact Conditions

    Energy Technology Data Exchange (ETDEWEB)

    Kim, Byung-Kook; Shin, Dong-Gap; Kim, Chang-Lae; Kim, Dae-Eun [Yonsei Univ., Seoul (Korea, Republic of); Goo, Byeong-Choon [Korea Railroad Research Institute, Uiwang (Korea, Republic of)

    2017-01-15

    The surface temperature of disc brakes varies during braking, which can affect the friction and wear behavior of braking systems. In order to develop an efficient braking system, the friction and wear behaviors of brake materials need to be clearly understood. In this work, the friction and wear behavior of the C/C-SiC-Cu composite and the Al/SiC composite, which are used in disc braking systems, were investigated. Both the surface temperature and contact pressure were studied. A pin-on-reciprocating tribotester was used for this purpose, in order to control temperature and load. Results showed that the friction varied significantly with temperature and sliding distance. It was found that a transfer layer of compacted wear debris formed on the wear track of the two materials. These layers caused the surface roughness of the wear track to increase. The outcome of this work is expected to serve as a basis for the development of braking systems under various operating conditions.

  10. SiC Composite for Fuel Structure Applications

    Energy Technology Data Exchange (ETDEWEB)

    Yueh, Ken [Electric Power Research Inst. (EPRI), Charlotte, NC (United States)

    2017-12-22

    Extensive evaluation was performed to determine the suitability of using SiC composite as a boiling water reactor (BWR) fuel channel material. A thin walled SiC composite box, 10 cm in dimension by approximately 1.5 mm wall thickness was fabricated using chemical vapor deposition (CVD) for testing. Mechanical test results and performance evaluations indicate the material could meet BWR channel mechanical design requirement. However, large mass loss of up to 21% was measured in in-pile corrosion test under BWR-like conditions in under 3 months of irradiation. A fresh sister sample irradiated in a follow-up cycle under PWR conditions showed no measureable weight loss and thus supports the hypothesis that the oxidizing condition of the BWR-like coolant chemistry was responsible for the high corrosion rate. A thermodynamic evaluation showed SiC is not stable and the material may oxidize to form SiO2 and CO2. Silica has demonstrated stability in high temperature steam environment and form a protective oxide layer under severe accident conditions. However, it does not form a protective layer in water under normal BWR operational conditions due to its high solubility. Corrosion product stabilization by modifying the SiC CVD surface is an approach evaluated in this study to mitigate the high corrosion rate. Titanium and zirconium have been selected as stabilizing elements since both TiSiO4 and ZrSiO4 are insoluble in water. Corrosion test results in oxygenated water autoclave indicate TiSiO4 does not form a protective layer. However, zirconium doped test samples appear to form a stable continuous layer of ZrSiO4 during the corrosion process. Additional process development is needed to produce a good ZrSiC coating to verify functionality of the mitigation concept.

  11. Physicochemical interactions resulting from the use of a SiC/SiC composite material in typical environments of future nuclear reactors

    International Nuclear Information System (INIS)

    Braun, James

    2014-01-01

    The development of high purity SiC fibers during the nineties has led to their consideration as nuclear reactors components through the use of SiC/SiC composites. SiC and SiC/SiC composites are considered as core materials of future nuclear reactors (SFR, GFR) and as a potential replacement for the zirconium cladding of PWR. Therefore, the thermochemical compatibility of these materials with typical environments of those nuclear reactors has been studied. The composition and the growth kinetics of the reaction zone of SiC towards niobium and tantalum (considered as materials to ensure the leak-tightness of a SiC/SiC cladding for GFR) have been studied between 1050 and 1500 C. High temperature heat treatments in open and closed systems between SiC and UO 2 have shown a significant reactivity over 1200 C characterized by the formation of CO and uranium silicides. Moreover, a liquid phase has been detected between 1500 and 1650 C. The exposure of SiC/SiC to liquid sodium (550 C, up to 2000 h) has been studied as a function of the oxygen concentration dissolved in liquid sodium. An improvement of the mechanical properties of the composites elaborated for this study (increase of the tensile strength and strain at failure) has been highlighted after immersion in the liquid sodium independently of its oxygen concentration. It is believed that this phenomenon is due to the presence of residual sodium in the material. (author) [fr

  12. Phase Stability and Thermal Conductivity of Composite Environmental Barrier Coatings on SiC/SiC Ceramic Matrix Composites

    Science.gov (United States)

    Benkel, Samantha; Zhu, Dongming

    2011-01-01

    Advanced environmental barrier coatings are being developed to protect SiC/SiC ceramic matrix composites in harsh combustion environments. The current coating development emphasis has been placed on the significantly improved cyclic durability and combustion environment stability in high-heat-flux and high velocity gas turbine engine environments. Environmental barrier coating systems based on hafnia (HfO2) and ytterbium silicate, HfO2-Si nano-composite bond coat systems have been processed and their stability and thermal conductivity behavior have been evaluated in simulated turbine environments. The incorporation of Silicon Carbide Nanotubes (SiCNT) into high stability (HfO2) and/or HfO2-silicon composite bond coats, along with ZrO2, HfO2 and rare earth silicate composite top coat systems, showed promise as excellent environmental barriers to protect the SiC/SiC ceramic matrix composites.

  13. High thermal conductivity SiC/SiC composites for fusion applications -- 2

    International Nuclear Information System (INIS)

    Kowbel, W.; Tsou, K.T.; Withers, J.C.; Youngblood, G.E.

    1998-01-01

    This report covers material presented at the IEA/Jupiter Joint International Workshop on SiC/SiC Composites for Fusion Structural Applications held in conjunction with ICFRM-8, Sendai, Japan, Oct. 23--24, 1997. An unirradiated SiC/SiC composite made with MER-developed CVR SiC fiber and a hybrid PIP/CVI SiC matrix exhibited room temperature transverse thermal conductivity of 45 W/mK. An unirradiated SiC/SiC composite made from C/C composite totally CVR-converted to a SiC/SiC composite exhibited transverse thermal conductivity values of 75 and 35 W/mK at 25 and 1000 C, respectively. Both types of SiC/SiC composites exhibited non-brittle failure in flexure testing

  14. Structure-property relationships of mullite-SiC-Al{sub 2}O{sub 3}–ZrO{sub 2} composites developed during carbothermal reduction of aluminosilicate minerals

    Energy Technology Data Exchange (ETDEWEB)

    Seifollahzadeh, P., E-mail: Pseifollahzadeh.mat@stu.yazd.ac.ir; Kalantar, M.; Ghasemi, S.S.

    2015-10-25

    Evolution of SiC and ZrO{sub 2} in the matrix of Al{sub 2}O{sub 3} or mullite have been reported to enhance a higher toughness, good thermal shock resistance (lowering thermal expansion and improving thermal conductivity) and improved creep resistance of composite materials. In this study, the structure-property relationships of mullite-Al{sub 2}O{sub 3} matrix composites have been investigated in conjunction with the evolution of reinforcing phases such as SiC–ZrO{sub 2} by an economical heat treatment process called carbothermal reduction of inorganic minerals (Kaolinite, Andalusite, Zircon). The influence of starting materials in relation with the variation in molar ratio of C/SiO{sub 2} on the phase composition, microstructures, physical and mechanical properties have been studied. Light microscopy has been supplemented with scanning electron microscopy, XRD analysis, differential thermal and thermal gravity analysis to follow the structure-property relationships. The experimental results show that with increasing of C/SiO{sub 2} ratio in starting materials, very fine SiC whiskers have been formed in the microstructures. Moreover, the densification and strength are considerable higher for ZrO{sub 2} + SiC containing composites in comparison to that of only SiC added ones. Furthermore, it has been found that the appropriate ratio of C/SiO{sub 2} with the associated firing temperature to develop a higher densification and SiC crystallization have been related to the 3.5, 1550 °C for kaolinite, 3.5, 1450 °C for zircon and 5.5, 1600 °C for andalusite containing composite samples, respectively. - Highlights: • In-situ formation of SiC whiskers in matrix of alumina + mullite composites. • Advantage of availability, abundance and economical for starting materials. • Lack of environmental problems in comparable of utilization of whiskers directly. • A mixture of coke and alumina as a protective layer instead of inert atmosphere. • Fabrication of advanced

  15. Microstructures and Properties of the C/Zr-O-Si-C Composites Fabricated by Polymer Infiltration and Pyrolysis

    Science.gov (United States)

    Ma, Yan; Chen, Zhaohui

    2013-09-01

    A way to improve the ablation properties of the C/SiC composites in an oxyacetylene torch environment was investigated by the precursor infiltration and pyrolysis route using three organic precursors (zirconium butoxide, polycarbosilane, and divinylbenzene). The ceramic matrix derived from the precursors at 1200 °C was mainly a mixture of SiC, ZrO2, and C. After annealing at 1600 °C for 1 h, ZrO2 partly transformed to ZrC because of the carbothermic reductions and completely transformed to ZrC at 1800 °C in 1 h. The mechanical properties of the composites decreased with increasing temperature, while the ablation resistance increased due to the increasing content of ZrC. Compared with C/SiC composites, the ablation resistance of the C/Zr-O-Si-C composites overwhelms because of the oxide films which formed on the ablation surfaces. And, the films were composed of two layers: the porous surface layer (the mixture of ZrO2 and SiO2) and the dense underlayer (SiO2).

  16. Development of SiC/SiC composite for fusion application

    International Nuclear Information System (INIS)

    Kohyama, A.; Katoh, Y.; Snead, L.L.; Jones, R.H.

    2001-01-01

    The recent efforts to develop SiC/SiC composite materials for fusion application under the collaboration with Japan and the USA are provided, where material performance with and without radiation damage has been greatly improved. One of the accomplishments is development of the high performance reaction sintering process. Mechanical and thermal conductivity are improved extensively by process modification and optimization with inexpensive fabrication process. The major efforts to make SiC matrix by CVI, PIP and RS methods are introduced together with the representing baseline properties. The resent results on mechanical properties of SiC/SiC under neutron irradiation are quite positive. The composites with new SiC fibers, Hi-Nicalon Type-S, did not exhibit mechanical property degradation up to 10 dpa. Based on the materials data recently obtained, a very preliminary design window is provided and the future prospects of SiC/SiC technology integration is provided. (author)

  17. Tasks for development of SiC/SiC composites as structural material in a fusion reactor

    International Nuclear Information System (INIS)

    Yamada, Reiji

    1997-01-01

    SiC/SiC composites are chosen for a structural material of blankets in DREAM Reactor that has been proposed as a power reactor by JAERI. The main requirements and the target values in the DREAM conceptual design were described, and compared to available experimental data. (author)

  18. Synthesis and electrochemical performance of mesoporous SiO{sub 2}–carbon nanofibers composite as anode materials for lithium secondary batteries

    Energy Technology Data Exchange (ETDEWEB)

    Hyun, Yura; Choi, Jin-Yeong [Department of Chemistry, Keimyung University (Korea, Republic of); Park, Heai-Ku [Department of Chemical Engineering, Keimyung University (Korea, Republic of); Bae, Jae Young [Department of Chemistry, Keimyung University (Korea, Republic of); Lee, Chang-Seop, E-mail: surfkm@kmu.ac.kr [Department of Chemistry, Keimyung University (Korea, Republic of)

    2016-10-15

    Highlights: • Mesoporous SiO{sub 2}–carbon nanofibers composite synthesized on Ni foam without any binder. • This composite was directly applied as anode material of Li secondary batteries. • Showed the highest initial (2420 mAh/g) and discharging (2092 mAh/g) capacity. • This material achieved a retention rate of 86.4% after 30 cycles. - Abstract: In this study, carbon nanofibers (CNFs) and mesoporous SiO{sub 2}–carbon nanofibers composite were synthesized and applied as the anode materials in lithium secondary batteries. CNFs and mesoporous SiO{sub 2}–CNFs composite were grown via chemical vapor deposition method with iron-copper catalysts. Mesoporous SiO{sub 2} materials were prepared by sol–gel method using tetraethylorthosilicate as the silica source and cetyltrimethylammoniumchloride as the template. Ethylene was used as the carbon source and passes into a quartz reactor of a tube furnace heated to 600 °C, and the temperature was maintained at 600 °C for 10 min to synthesize CNFs and mesoporous SiO{sub 2}–CNFs composite. The electrochemical characteristics of the as-prepared CNFs and mesoporous SiO{sub 2}–CNFs composite as the anode of lithium secondary batteries were investigated using a three-electrode cell. In particular, the mesoporous SiO{sub 2}–CNFs composites synthesized without binder after depositing mesoporous SiO{sub 2} on Ni foam showed the highest charging and discharging capacity and retention rate. The initial capacity (2420 mAh/g) of mesoporous SiO{sub 2}–CNFs composites decreased to 2092 mAh/g after 30 cycles at a retention rate of 86.4%.

  19. Synthesis and characterization of nano-Li1.95FeSiO4/C composite as cathode material for lithium-ion batteries

    International Nuclear Information System (INIS)

    Huang Xiaobing; Chen Honghui; Zhou Shibiao; Chen Yuandao; Yang Jifeng; Ren Yurong; Wang Haiyan; Qu Meizhen; Pan Zhonglai; Yu Zuolong

    2012-01-01

    Li 1.95 FeSiO 4 /C and Li 2 FeSiO 4 /C composites were synthesized by a traditional solid-state reaction method and then discussed comparatively through the results of X-ray diffraction (XRD), scanning electron microscopy (SEM), the Brunauer–Emmet–Teller (BET) method, the charge–discharge test and electrochemical impedance spectra measurement, respectively. The results demonstrated that the Li 1.95 FeSiO 4 /C composite could exhibit much better battery performance in terms of the discharge capacity, cycling stability and rate capability in comparison with the Li 2 FeSiO 4 /C composite. At 0.2C and 5C, it delivered a discharge capacity of 142 mAh g −1 and 93 mAh g −1 , respectively, and after 100 cycles at 1C, 95.1% of its initial capacity was retained.

  20. Synthesis and optical characterization of C-SiO2 and C-NiO sol-gel composite films for use as selective solar absorbers

    CSIR Research Space (South Africa)

    Makiwa, G

    2008-08-01

    Full Text Available The authors present a cheaper and environmentally friendly method to fabricate efficient spectrally selective solar absorber materials. The sol-gel technique was used to fabricate carbon-silica (C-SiO2) and carbon-nickel oxide (C-NiO) composite...

  1. Oxidation-resistant interface coatings for SiC/SiC composites

    Energy Technology Data Exchange (ETDEWEB)

    Stinton, D.P.; Kupp, E.R.; Hurley, J.W.; Lowden, R.A. [Oak Ridge National Lab., TN (United States)] [and others

    1996-08-01

    The characteristics of the fiber-matrix interfaces in ceramic matrix composites control the mechanical behavior of these composites. Finite element modeling (FEM) was performed to examine the effect of interface coating modulus and coefficient of thermal expansion on composite behavior. Oxide interface coatings (mullite and alumina-titania) produced by a sol-gel method were chosen for study as a result of the FEM results. Amorphous silicon carbide deposited by chemical vapor deposition (CVD) is also being investigated for interface coatings in SiC-matrix composites. Processing routes for depositing coatings of these materials were developed. Composites with these interfaces were produced and tested in flexure both as-processed and after oxidation to examine the suitability of these materials as interface coatings for SiC/SiC composites in fossil energy applications.

  2. High-temperature deformation of SiC-whisker-reinforced MgO-PSZ/mullite composites

    International Nuclear Information System (INIS)

    Parthasarathy, T.A.; Hay, R.S.; Ruh, R.

    1996-01-01

    The effect of 33.5 vol% SiC whisker loading on high-temperature deformation of 1 wt% MgO-38.5 wt% zirconia-mullite composites was studied between 1,300 and 1,400 C. At strain rates of 10 -6 to 5 x 10 -4 /s the creep resistance of zirconia-mullite composites without SiC reinforcement was inferior to monolithic mullite of similar grain size. Analysis of the results suggested that the decreased creep resistance of mullite-zirconia composites compared to pure mullite could be at least partially explained by mechanical effects of the weaker zirconia phase, increased effective diffusivity of mullite by zirconia addition, and to the differences in mullite grain morphology. With SiC whisker reinforcement, the deformation rate at high stress was nearly the same as that of the unreinforced material, but at low stress the creep rates of the SiC-reinforced material were significantly lowered. The stress dependence of the creep rate of unreinforced material suggested that diffusional creep was the operative mechanism, while the reinforced material behaved as if a threshold stress for creep existed. The threshold stress could be rationalized based on a whisker network model. This was supported by data on other whisker-containing materials; however, the threshold stress had a temperature dependence that was orders of magnitude higher than the elastic constants, leaving the physical model incomplete. The effects of residual stresses and amorphous phases at whisker/matrix interfaces are invoked to help complete the physical model for creep threshold stress

  3. Synthesis and characterization of Yb and Er based monosilicate powders and durability of plasma sprayed Yb2SiO5 coatings on C/C–SiC composites

    International Nuclear Information System (INIS)

    Khan, Zuhair S.; Zou Binglin; Huang Wenzhi; Fan Xizhi; Gu Lijian; Chen Xiaolong; Zeng Shuibing; Wang Chunjie; Cao Xueqiang

    2012-01-01

    Highlights: ► Ultra-pure rare-earth monosilicate powders based on Er and Yb have been fabricated by solid-state reaction. ► Spray-drying treatment results in powders with free flowing characteristics and rounded surface morphologies. ► CTEs are found to be 7.1 ppm/°C for Yb 2 SiO 5 and 7.5 ppm/°C for Er 2 SiO 5 . ► Plasma spraying has been used to deposit Yb 2 SiO 5 coatings on C/C–SiC substrate. ► Coatings remain strongly intact with the substrate on thermal cycling between ∼400 °C and 1500 °C in gas burner rig experiment. - Abstract: Rare-earth silicates such as Yb 2 SiO 5 and Er 2 SiO 5 are promising environmental barrier coating materials for ceramic matrix composites. In this work, Yb 2 SiO 5 and Er 2 SiO 5 ceramic powders have been synthesized by solid-state reaction using Yb 2 O 3 , Er 2 O 3 and SiO 2 as starting materials. The fabricated powders were subjected to spray drying treatment for subsequent synthesis of coatings by plasma spraying. The spray drying resulted in well-dispersed and spherical powder particles with good flowability. Analytical techniques such as X-ray diffraction (XRD), scanning electron microscopy (SEM), thermogravimetry and differential scanning calorimetry (TGA/DSC) and dilatometry were applied to study the microstructural and thermal characteristics of the powders. Ultra-high purity monosilicate powders formed as a result of heating treatments at 1400 °C in a box furnace for 20 h. TG/DSC revealed the genesis temperatures of the silicate formation (low temperature polymorphs) and also showed that the solid-state reactions to form Yb and Er based monosilicates proceeded without any weight-loss in the tested temperature range. The values of coefficients of thermal expansion (CTE) of the fabricated compounds are found to be 7.1 ppm/°C for Yb 2 SiO 5 and 7.5 ppm/°C for Er 2 SiO 5 by dilatometric measurements. Besides these studies, coating formation by plasma spraying of spray-dried Yb 2 SiO 5 powders on the ceramic

  4. Effect of fiber surface state on mechanical properties of Cf/Si-O-C composites

    International Nuclear Information System (INIS)

    Wang Song; Chen Zhaohui; Ma Qingsong; Hu Haifeng; Zheng Wenwei

    2005-01-01

    Three-dimensional braided carbon fiber reinforced silicon oxycarbide composites (3D-B C f /Si-O-C) were fabricated via a polysiloxane infiltration and pyrolysis route. The effects of fiber surface state on microstructure and mechanical properties of C f /Si-O-C composites were investigated. The change of carbon fiber surface state was achieved via heat treatment in vacuum. The results showed that heat treatment decreased carbon fiber surface activity due to the decrease of the amount of oxygen and nitrogen atoms. The C f /Si-O-C composites fabricated from the carbon fiber with low surface activity had excellent mechanical properties, which resulted from perfect interfacial bonding and good in situ fiber strength. The flexural strength and fracture toughness of the C f /Si-O-C composites from the treated fiber were 534 MPa and 23.4 MPa m 1/2 , respectively, which were about 7 and 11 times more than those of the composites from the as-received carbon fiber, respectively

  5. Preparation of mullite whiskers reinforced SiC/Al2O3 composites by microwave sintering

    Directory of Open Access Journals (Sweden)

    Wei Li

    2016-12-01

    Full Text Available Mullite whiskers reinforced SiC/Al2O3 composites were prepared by microwave sintering in a microwave chamber with TE666 resonant mode. Original SiC particles were coated with SiO2 using sol-gel processing and mixed with Al2O3 particles. Mullite was formed in the reaction between SiO2 and Al2O3. The isostatically pressed cylindrical pellets were sintered from 1350 °C to 1600 °C for 30 min. Physical and chemical responses were investigated by detecting changes in reflected power during the microwave sintering process. XRD was carried out to characterize the samples and showed that mullite could be formed at 1200 °C. Bridging of mullite whiskers between Al2O3 and SiC particles was observed by SEM and is due to a so-called local hot spot effect, which was the unique feature for microwave sintering. The optimized microwave sintering temperature was 1500 °C corresponding to the maximum amount of mullite whiskers within SiC/Al2O3 composites. The high electro-magnetic field enhanced the decomposition of mullite at higher temperatures above 1550 °C. The mechanical properties of mullite whiskers reinforced SiC/Al2O3 composites are much better than the SiC/Al2O3 composites without mullite whiskers.

  6. Microwave electromagnetic and absorption properties of SiO2/C core/shell composites plated with metal cobalt

    Science.gov (United States)

    Shen, Guozhu; Fang, Xumin; Wu, Hongyan; Wei, Hongyu; Li, Jingfa; Li, Kaipeng; Mei, Buqing; Xu, Yewen

    2017-04-01

    A facile method has been developed to fabricate magnetic core/shell SiO2/C/Co sub-microspheres via the pyrolysis of SiO2/PANI (polyaniline) and electroless plating method. The electromagnetic parameters of these SiO2/C and SiO2/C/Co composites were measured and the microwave reflection loss properties were evaluated in the frequency range of 2-18 GHz. The results show that the dielectric loss of SiO2/C composite increases with the increase of carbonization temperature and the magnetic loss enhances due to the deposition of cobalt on the SiO2/C sub-microspheres. The reflection loss results exhibit that the microwave absorption properties of the SiO2/C/Co composites are more excellent than those of SiO2/C composites for each thickness. The maximum effective absorption bandwidth (reflection loss ≤ -10 dB) arrives at 5.0 GHz (13.0-18 GHz) for SiO2/C/Co composite with 1.5 mm of thickness and the minimum reflection loss value is -24.0 dB at 5.0 GHz with 4.0 mm of thickness. The microwave loss mechanism of the SiO2/C/Co composites was also discussed in this paper.

  7. Progress in blanket designs using SiCf/SiC composites

    International Nuclear Information System (INIS)

    Giancarli, L.; Golfier, H.; Nishio, S.; Raffray, R.; Wong, C.; Yamada, R.

    2002-01-01

    This paper summarizes the most recent design activities concerning the use of SiC f /SiC composite as structural material for fusion power reactor breeding blanket. Several studies have been performed in the past. The most recent proposals are the TAURO blanket concept in the European Union, the ARIES-AT concept in the US, and DREAM concept in Japan. The first two concepts are self-cooled lithium-lead blankets, while DREAM is an helium-cooled beryllium/ceramic blanket. Both TAURO and ARIES-AT blankets are essentially formed by a SiC f /SiC box acting as a container for the lithium-lead which has the simultaneous functions of coolant, tritium breeder, neutron multiplier and, finally, tritium carrier. The DREAM blanket is characterized by small modules using pebble beds of Be as neutron multiplier material, of Li 2 O (or other lithium ceramics) as breeder material and of SiC as shielding material. The He coolant path includes a flow through the pebble beds and a porous partition wall. For each blanket, this paper describes the main design features and performances, the most recent design improvements, and the proposed manufacturing routes in order to identify specific issues and requirements for the future R and D on SiC f /SiC

  8. Initial assessment of environmental effects on SiC/SiC composites in helium-cooled nuclear systems

    Energy Technology Data Exchange (ETDEWEB)

    Contescu, Cristian I [ORNL

    2013-09-01

    This report summarized the information available in the literature on the chemical reactivity of SiC/SiC composites and of their components in contact with the helium coolant used in HTGR, VHTR and GFR designs. In normal operation conditions, ultra-high purity helium will have chemically controlled impurities (water, oxygen, carbon dioxide, carbon monoxide, methane, hydrogen) that will create a slightly oxidizing gas environment. Little is known from direct experiments on the reactivity of third generation (nuclear grade) SiC/SiC composites in contact with low concentrations of water or oxygen in inert gas, at high temperature. However, there is ample information about the oxidation in dry and moist air of SiC/SiC composites at high temperatures. This information is reviewed first in the next chapters. The emphasis is places on the improvement in material oxidation, thermal, and mechanical properties during three stages of development of SiC fibers and at least two stages of development of the fiber/matrix interphase. The chemical stability of SiC/SiC composites in contact with oxygen or steam at temperatures that may develop in off-normal reactor conditions supports the conclusion that most advanced composites (also known as nuclear grade SiC/SiC composites) have the chemical resistance that would allow them maintain mechanical properties at temperatures up to 1200 1300 oC in the extreme conditions of an air or water ingress accident scenario. Further research is needed to assess the long-term stability of advanced SiC/SiC composites in inert gas (helium) in presence of very low concentrations (traces) of water and oxygen at the temperatures of normal operation of helium-cooled reactors. Another aspect that needs to be investigated is the effect of fast neutron irradiation on the oxidation stability of advanced SiC/SiC composites in normal operation conditions.

  9. Improved thermoelectric performance of CdO by adding SiC fibers versus by adding SiC nanoparticles inclusions

    Science.gov (United States)

    Liang, S.; Li, Longjiang

    2018-03-01

    We report the improved thermoelectric (TE) performance of CdO by alloying with SiC fibers. In contrast to the lowered thermoelectric figure of merit (ZT) in a CdO matrix with SiC nanoparticle composites, an appreciable ZT value increment of about 36% (from 0.32 to 0.435) at 1000 K was obtained in the CdO matrix with SiC fiber composites. Both kinds of composites show substantially decreased thermal conductivity due to additional phonon scattering by the nano-inclusions. Compared to the very high electrical resistivity (ρ ˜ 140 μΩ m) for 5 at. % SiC nanoparticle composites, SiC fiber composites favorably maintained a very low ρ (˜30 μΩ m) even with 5 at. % SiC at 1000 K. We think the substantial difference of specific surface areas of these two nano-inclusions (30 m2/g for fibers vs 300 m2/g for nanoparticles) might play a crucial role to fine tune the TE performance. Larger interface could be inductive to diffusion and electron acceptor activation, which affect carrier mobility considerably. This work might hint at an alternative approach to improve TE materials' performance.

  10. Present status of SiCf/SiC composites as low-activation structural materials of fusion reactor in Japan

    International Nuclear Information System (INIS)

    Kohyama, A.; Katoh, Y.; Hasegawa, A.; Noda, T.

    2001-01-01

    The outline of research subjects on SiCf/SiC composites to apply to the structural components of fusion reactors are described and present status on material development of SiCf/SiC composites in Japan is reviewed. Irradiation experiments of the composites using fission reactors conducted by international collaborations to clarify their radiation response and to optimize the fabrication processes are introduced. (author)

  11. A novel pineapple-structured Si/TiO2 composite as anode material for lithium ion batteries

    International Nuclear Information System (INIS)

    Yan, Dong; Bai, Ying; Yu, Caiyan; Li, Xiaoge; Zhang, Weifeng

    2014-01-01

    Highlights: • Pineapple-structured Si/TiO 2 composite was firstly synthesized by a simple sol–gel method. • Pineapple-structured Si/TiO 2 composite exhibits the best cycling stability. • TiO 2 layer not only effectively inhibits the volume change of Si, but also contributes its electrochemical activity. - Abstract: Nanoscaled Si is successfully wrapped with different contents of nano-TiO 2 (the molar ratios of Si/TiO 2 composites are 1:1, 1:2, 1:3, 1:4 and 1:5, respectively) to form a novel pineapple structure. X-ray diffraction (XRD), Raman spectroscopy, X-ray photoelectron spectroscopy (XPS), field emission scanning electron microscopy (FESEM) and high resolution transmission electron microscopy (HRTEM) are utilized to characterize the structure, component, chemical environment and morphology of the composite. The investigation in cycling performances demonstrates that Si/TiO 2 with molar ratio of 1:4 exhibits the best cycling stability, with specific capacity of 593 mA h g −1 after 50 cycles at 0.1 C, much higher than those of the other composites and the pristine material. Cyclic voltammetry (CV) profiles are also measured and compared. It is believed that the outside TiO 2 particles act as buffer against the huge volume change of Si during repeated alloying and de-alloying, which explains the improved electrochemical performances

  12. Effect of sintering temperature on structure of C-B4C-SiC composites with silicon additive

    International Nuclear Information System (INIS)

    Wu Lijun; Academia Sinica, Shenyang; Huang Qizhong; Yang Qiaoqin; Zhao Lihu; Xu Zhongyu

    1996-01-01

    Carbon materials possess good electric conductivity, heat conductivity, corrosion-resistance, self-lubrication and hot-shocking resistance, and are easily machined. However, they have low mechanical strength, and are easily oxidized in air at high temperature. On the contrary, ceramic materials have high mechanical strength and hardness, and have good wear-resistance and oxidation-resistance. However, they have the shortages of poor thermal-shock resistance lubrication, and are difficult to machine. Therefore, carbon/ceramic composites with the advantages of both carbon and ceramic materials have been widely studied in the recent years. Huang prepared C-B 4 C-SiC composites with the free sintering method and the hot pressing method, and studied the effects of Si, Al, Al 2 O 3 , Ni and Ti additives on the properties of the composites. The results showed that these additives could improve the properties of the composites. Zhao et al. studies the structure of C-B 4 C-SiC composites with Si additive sintered at 2,000 C and found two c-center monoclinic phases. In this paper, the authors discussed the effect of the sintering temperature on the structure of C-B 4 C-SiC composites with Si additive by means of transmission electron microscope (TEM) and x-ray diffractometer (XRD)

  13. Characterization of commercial grade Tyranno SA/CVI-SiC composites

    International Nuclear Information System (INIS)

    Riccardi, B.; Trentini, E.; Labanti, M.; Leuchs, M.; Roccella, S.; Visca, E.

    2007-01-01

    The objective of the present work was to characterize commercial-grade Tyranno SA SiC fiber reinforced chemically vapour infiltrated (CVI) SiC matrix composites (SiC f /SiC) with chemically vapour deposited (CVD) SiC coating. The characterization includes the assessment of the monotonic mechanical properties. Low cycle flexural fatigue behaviour has been investigated at room temperature (RT) and 1000 o C by means of 4-point bending tests. The creep behaviour at 1000 o C was preliminary investigated by means of constant bending stress rupture test. The material showed a pronounced degradation of monotonic mechanical properties at high temperature. Low cycle flexural fatigue behaviour showed excellent and satisfactory results at RT and 1000 o C, respectively. The creep resistance at 1000 o C is significant only at low load level

  14. Influence of polystyrene/phenyl substituents in precursors on microstructures of Si-O-C composite anodes for lithium-ion batteries

    Energy Technology Data Exchange (ETDEWEB)

    Fukui, Hiroshi; Ohsuka, Hisashi; Hino, Takakazu [Dow Corning Toray Company, Ltd., Chigusa-Kaigan, Ichihara 299-0108 (Japan); Kanamura, Kiyoshi [Department of Applied Chemistry, Tokyo Metropolitan University, Minami-Osawa, Hachioji, Tokyo 192-0397 (Japan)

    2011-01-01

    Pyrolysis of methylphenyl-substituted branched polysilane-polystyrene polymer blends led to the formation of silicon oxycarbide (Si-O-C) glasses with microstructures similar to those found in hard carbon. Electrochemical measurements showed that the Si-O-C composite materials had lithium storage capacities of more than 500 mA h g{sup -1}, with a short but characteristic pseudo-voltage plateau at ca. 0.1 V upon delithiation. This voltage plateau indicates the existence of micropores where less-ionic lithium species can be formed, as seen in the case of hard carbon. The micropores were minor electrochemically active sites but led to an increase in the capacities. {sup 7}Li NMR spectra of the Si-O-C composite materials had two resonances in the fully lithiated state, and one resonance could be attributed to less-ionic lithium species in the micropores. No voltage plateau was observed upon delithiation, and only a singular {sup 7}Li NMR resonance was observed when the polysilanes alone were pyrolyzed. Although there was no decrease in the capacities, the voltage plateau disappeared with electrochemical cycling. Furthermore, different {sup 7}Li NMR resonances from those observed in the first lithiation were clearly seen. These results indicate changes in the lithium environments in the Si-O-C composite materials. (author)

  15. Synthesis and characterization of SiC based composite materials for immobilizing radioactive graphite

    Science.gov (United States)

    Wang, Qing; Teng, Yuancheng; Wu, Lang; Zhang, Kuibao; Zhao, Xiaofeng; Hu, Zhuang

    2018-06-01

    In order to immobilize high-level radioactive graphite, silicon carbide based composite materials{ (1-x) SiC· x MgAl2O4 (0.1 ≤ x≤0.4) } were fabricated by solid-state reaction at 1370 °C for 2 h in vacuum. Residual graphite and precipitated corundum were observed in the as-synthesized product, which attributed to the interface reaction of element silicon and magnesium compounds. To further understand the reasons for the presence of graphite and corundum, the effects of mole ratio of Si/C, MgAl2O4 content and non-stoichiometry of MgAl2O4 on the synthesis were investigated. To immobilize graphite better, residual graphite should be eliminated. The target product was obtained when the mole ratio of Si/C was 1.3:1, MgAl2O4 content was x = 0.2, and the mole ratio of Al to Mg in non-stoichiometric MgAl2O4 was 1.7:1. In addition, the interface reaction between magnesium compounds and silicon not graphite was displayed by conducting a series of comparative experiments. The key factor for the occurrence of interface reaction is that oxygen atom is transferred from magnesium compound to SiO gas. Infrared and Raman spectrum revealed the increased disorders of graphite after being synthesized.

  16. Grinding, Machining Morphological Studies on C/SiC Composites

    Science.gov (United States)

    Xiao, Chun-fang; Han, Bing

    2018-05-01

    C/SiC composite is a typical material difficult to machine. It is hard and brittle. In machining, the cutting force is large, the material removal rate is low, the edge is prone to collapse, and the tool wear is serious. In this paper, the grinding of C/Si composites material along the direction of fiber distribution is studied respectively. The surface microstructure and mechanical properties of C/SiC composites processed by ultrasonic machining were evaluated. The change of surface quality with the change of processing parameters has also been studied. By comparing the performances of conventional grinding and ultrasonic grinding, the surface roughness and functional characteristics of the material can be improved by optimizing the processing parameters.

  17. SHS synthesis of Si-SiC composite powders using Mg and reactants from industrial waste

    Science.gov (United States)

    Chanadee, Tawat

    2017-11-01

    Si-SiC composite powders were synthesized by self-propagating high-temperature synthesis (SHS) using reactants of fly ash-based silica, sawdust-based activated carbon, and magnesium. Fly ash-based silica and sawdust-based activated carbon were prepared from coal mining fly ash and Para rubber-wood sawdust, respectively. The work investigated the effects of the synthesis atmosphere (air and Ar) on the phase and morphology of the SHS products. The SHS product was leached by a two-step acid leaching processes, to obtain the Si-SiC composite powder. The SHS product and SHS product after leaching were characterized by X-ray diffractometry, scanning electron microscopy and energy dispersive X-ray spectrometry. The results indicated that the SHS product synthesized in air consisted of Si, SiC, MgO, and intermediate phases (SiO2, Mg, Mg2SiO4, Mg2Si), whereas the SHS product synthesized in Ar consisted of Si, SiC, MgO and a little Mg2SiO4. The SiC content in the leached-SHS product was higher when Ar was used as the synthesis atmosphere. As well as affecting the purity, the synthesis atmospheres also affected the average crystalline sizes of the products. The crystalline size of the product synthesized in Ar was smaller than that of the product synthesized in air. All of the results showed that fly ash and sawdust could be effective waste-material reactants for the synthesis of Si-SiC composite powders.

  18. In-situ grown CNTs modified SiO2/C composites as anode with improved cycling stability and rate capability for lithium storage

    Science.gov (United States)

    Wang, Siqi; Zhao, Naiqin; Shi, Chunsheng; Liu, Enzuo; He, Chunnian; He, Fang; Ma, Liying

    2018-03-01

    Silica (SiO2) is regarded as one of the most promising anode materials for lithium ion batteries owing to its high theoretical specific capacity, relatively low operation potentials, abundance, environmental benignity and low cost. However, the low intrinsic electrical conductivity and large volume change of SiO2 during the discharge/charge cycles usually results in poor electrochemical performance. In this work, carbon nanotubes (CNTs) modified SiO2/C composites have been fabricated through an in-situ chemical vapor deposition method. The results show that the electrical conductivity of the SiO2/C/CNTs is visibly enhanced through a robust connection between the CNTs and SiO2/C particles. Compared with the pristine SiO2 and SiO2/C composites, the SiO2/C/CNTs composites display a high initial capacity of 1267.2 mA h g-1. Besides, an excellent cycling stability with the capacity of 315.7 mA h g-1 is achieved after 1000th cycles at a rate of 1 A g-1. The significantly improved electrochemical properties of the SiO2/C/CNTs composites are mainly attributed to the formation of three dimensional CNT networks in the SiO2/C substrate, which can not only shorten the Li-ion diffusion path but also relieve the volume change during the lithium-ion insertion/extraction processes.

  19. Thermal cyclic oxidation behavior of the developed compositionally gradient graphite material of SiC/C in air environment

    International Nuclear Information System (INIS)

    Nakano, Junichi; Fujii, Kimio; Shindo, Masami

    1993-08-01

    For the developed compositionally gradient graphite material composed of surface SiC coating layer, middle SiC/C layer and graphite matrix, the thermal cyclic oxidation test was performed together with two kinds of the SiC coated graphite materials in air environment. It was made clear that the developed material exhibited high performance under severe thermal cyclic condition independent of the morphology of middle SiC/C layers and had the longer time or the more cycle margins from crack initiation to failure for surface SiC coating layer compared with the SiC coated graphite materials. (author)

  20. Comparison of friction and wear performances of brake materials containing different amounts of ZrSiO4 dry sliding against SiCp reinforced Al matrix composites

    International Nuclear Information System (INIS)

    Zhang Shaoyang; Wang Fuping

    2007-01-01

    Low friction levels for brake materials dry sliding against Al matrix composites (Al-MMCs) were observed. Al matrix composites reinforced with 30 vol.% SiC p (34 μm) were used first to fabricate a new brake drum in place of the conventional cast iron brake drum for a Chase Machine. Experimental studies on the brake materials differing in amounts of zirconium silicate (0 wt%, 4 wt%, 8 wt%, and 12 wt% ZrSiO 4 ) dry sliding against the Al-MMCs drum were performed on the Chase Machine in order to examine their effects on friction and wear performances. The test procedures include friction fade and recovery, load and speed sensitivities at 177 deg. C and 316 deg. C, and wear. Experimental results show that the brake material containing 8 wt% ZrSiO 4 had the best wear resistance and higher friction level. The brake material containing 12 wt% ZrSiO 4 had the highest friction level, but wear increased rapidly. The deterioration of the latter wear suggests that this brake material is unreliable in commercial applications

  1. BN interphase in composite materials with nicalon Si-C-O fibers and with vitro ceramic matrix of MAS type; L`interphase BN dans les materiaux composites a fibres Si-C-O nicalon et a matrice vitroceramique de type MAS

    Energy Technology Data Exchange (ETDEWEB)

    Ricca, N

    1994-03-14

    BN has been suggested as an interphase in silica-based glass-ceramic matrix composites with a view to use these materials in oxidizing atmospheres at medium or high temperatures. The matrix had a boron-doped MAS (MgO-Al{sub 2}O{sub 3}-SiO{sub 2}) composition and was prepared from an hydrosol precursor. Pseudo-ID composites were prepared according to a sol impregnations/calcination/hot-pressing route. Chemical and microstructural characterizations of the fiber/matrix interfacial area were conducted by mean of TEM/EELS and AES analyses. The efficiency of BN as a coupling interphase for this particular composite system was successfully demonstrated through tensile tests performed on either as-processed or aged specimens (100 hours at 1000 deg C in air or under argon). In addition, composites maintained in air at 600 deg C, 800 deg C and 900 deg C while simultaneously loaded did not fail after 150 hours or more. Thus, a BN interphase appeared to be compatible with an oxidizing environment (i.e. the oxide matrix and/or air from 600 to 1000 deg C) and should therefore successfully replace the usual carbon interphase at least for use at medium temperatures. (author)

  2. Variation in the Optical Properties of the SiC-SiO2 Composite Antireflection Layer in Crystalline Silicon Solar Cells by Annealing

    Science.gov (United States)

    Jannat, Azmira; Li, Zhen Yu; Akhter, M. Shaheer; Yang, O.-Bong

    2017-11-01

    This study showed the effects of annealing on a sol-gel-derived SiC-SiO2 composite antireflection (AR) layer and investigated the optical and photovoltaic properties of crystalline silicon (Si) solar cells. The SiC-SiO2 composite AR coating showed a considerable decrease in reflectance from 7.18% to 3.23% at varying annealing temperatures of 450-800°C. The refractive indices of the SiC-SiO2 composite AR layer were tuned from 2.06 to 2.45 with the increase in annealing temperature. The analysis of the current density-voltage characteristics indicated that the energy conversion efficiencies of the fabricated Si solar cells gradually increased from 16.99% to 17.73% with increasing annealing temperatures of 450-800°C. The annealing of the SiC-SiO2 composite AR layer in Si solar cells was crucial to improving the optical, morphological, and photovoltaic properties.

  3. FABRICATION AND MATERIAL ISSUES FOR THE APPLICATION OF SiC COMPOSITES TO LWR FUEL CLADDING

    Directory of Open Access Journals (Sweden)

    WEON-JU KIM

    2013-08-01

    Full Text Available The fabrication methods and requirements of the fiber, interphase, and matrix of nuclear grade SiCf/SiC composites are briefly reviewed. A CVI-processed SiCf/SiC composite with a PyC or (PyC-SiCn interphase utilizing Hi-Nicalon Type S or Tyranno SA3 fiber is currently the best combination in terms of the irradiation performance. We also describe important material issues for the application of SiC composites to LWR fuel cladding. The kinetics of the SiC corrosion under LWR conditions needs to be clarified to confirm the possibility of a burn-up extension and the cost-benefit effect of the SiC composite cladding. In addition, the development of end-plug joining technology and fission products retention capability of the ceramic composite tube would be key challenges for the successful application of SiC composite cladding.

  4. High-temperature protective coatings for C/SiC composites

    Directory of Open Access Journals (Sweden)

    Xiang Yang

    2014-12-01

    Full Text Available Carbon fiber-reinforced silicon carbide (C/SiC composites were well-established light weight materials combining high specific strength and damage tolerance. For high-temperature applications, protective coatings had to provide oxidation and corrosion resistance. The literature data introduced various technologies and materials, which were suitable for the application of coatings. Coating procedures and conditions, materials design limitations related to the reactivity of the components of C/SiC composites, new approaches and coating systems to the selection of protective coatings materials were examined. The focus of future work was on optimization by further multilayer coating systems and the anti-oxidation ability of C/SiC composites at temperatures up to 2073 K or higher in water vapor.

  5. Selected mechanical properties of aluminum composite materials reinforced with SiC particles

    Directory of Open Access Journals (Sweden)

    A. Kurzawa

    2008-07-01

    Full Text Available This work presents the results of research concerning influence of ceramic particles’ content of silicon carbide on selected mechanical properties of type AW-AlCu4Mg2Mn - SiC composite materials. Composites produced of SiC particles with pressure infiltration method of porous preform and subject to hot plastic forming in the form of open die forging were investigated. The experimental samples contained from 5% up to 45% of reinforcing SiC particles of 8÷10μm diameter. Studies of strength properties demonstrated that the best results, in case of tensile strength as well as offset yield strength, might be obtained while applying reinforcement in the amount of 20-25% vol. of SiC. Application of higher than 25% vol. contents of reinforcing particles leads to gradual strength loss. The investigated composites were characterized by very high functional properties, such as hardness and abrasive wear resistance, whose values increase strongly with the increase of reinforcement amount. The presented results of the experiments shall allow for a more precise component selection of composite materials at the stage of planning and design of their properties.

  6. Preparation and oxidation protection of CVD SiC/a-BC/SiC coatings for 3D C/SiC composites

    International Nuclear Information System (INIS)

    Liu Yongsheng; Zhang Litong; Cheng Laifei; Yang Wenbin; Zhang Weihua; Xu Yongdong

    2009-01-01

    An amorphous boron carbide (a-BC) coating was prepared by LPCVD process from BCl 3 -CH 4 -H 2 -Ar system. XPS result showed that the boron concentration was 15.0 at.%, and carbon was 82.0 at.%. One third of boron was distributed to a bonding with carbon and 37.0 at.% was dissolved in graphite lattice. A multiple-layered structure of CVD SiC/a-BC/SiC was coated on 3D C/SiC composites. Oxidation tests were conducted at 700, 1000, and 1200 deg. C in 14 vol.% H 2 O/8 vol.% O 2 /78 vol.% Ar atmosphere up to 100 h. The 3D C/SiC composites with the modified coating system had a good oxidation resistance. This resulted in the high strength retained ratio of the composites even after the oxidation.

  7. Current status and recent research achievements in SiC/SiC composites

    Energy Technology Data Exchange (ETDEWEB)

    Katoh, Y., E-mail: katohy@ornl.gov [Oak Ridge National Laboratory, Oak Ridge, TN (United States); Snead, L.L. [Oak Ridge National Laboratory, Oak Ridge, TN (United States); Henager, C.H. [Pacific Northwest National Laboratory, Richland, WA (United States); Nozawa, T. [Japan Atomic Energy Agency, Rokkasho, Aomori (Japan); Hinoki, T. [Institute of Advanced Energy, Kyoto University, Kyoto (Japan); Iveković, A.; Novak, S. [Jožef Stefan Institute, Ljubljana (Slovenia); Gonzalez de Vicente, S.M. [EFDA Close Support Unit, Garching (Germany)

    2014-12-15

    The silicon carbide fiber-reinforced silicon carbide matrix (SiC/SiC) composite system for fusion applications has seen a continual evolution from development a fundamental understanding of the material system and its behavior in a hostile irradiation environment to the current effort which is directed at a broad-based program of technology maturation program. In essence, over the past few decades this material system has steadily moved from a laboratory curiosity to an engineering material, both for fusion structural applications and other high performance application such as aerospace. This paper outlines the recent international scientific and technological achievements towards the development of SiC/SiC composite material technologies for fusion application and discusses future research directions. It also reviews the materials system in the larger context of progress to maturity as an engineering material for both the larger nuclear community and broader engineering applications.

  8. Current status and recent research achievements in SiC/SiC composites

    International Nuclear Information System (INIS)

    Katoh, Y.; Snead, L.L.; Henager, C.H.; Nozawa, T.; Hinoki, T.; Iveković, A.; Novak, S.; Gonzalez de Vicente, S.M.

    2014-01-01

    The silicon carbide fiber-reinforced silicon carbide matrix (SiC/SiC) composite system for fusion applications has seen a continual evolution from development a fundamental understanding of the material system and its behavior in a hostile irradiation environment to the current effort which is directed at a broad-based program of technology maturation program. In essence, over the past few decades this material system has steadily moved from a laboratory curiosity to an engineering material, both for fusion structural applications and other high performance application such as aerospace. This paper outlines the recent international scientific and technological achievements towards the development of SiC/SiC composite material technologies for fusion application and discusses future research directions. It also reviews the materials system in the larger context of progress to maturity as an engineering material for both the larger nuclear community and broader engineering applications

  9. Current status and recent research achievements in SiC/SiC composites

    Science.gov (United States)

    Katoh, Y.; Snead, L. L.; Henager, C. H.; Nozawa, T.; Hinoki, T.; Iveković, A.; Novak, S.; Gonzalez de Vicente, S. M.

    2014-12-01

    The silicon carbide fiber-reinforced silicon carbide matrix (SiC/SiC) composite system for fusion applications has seen a continual evolution from development a fundamental understanding of the material system and its behavior in a hostile irradiation environment to the current effort which is directed at a broad-based program of technology maturation program. In essence, over the past few decades this material system has steadily moved from a laboratory curiosity to an engineering material, both for fusion structural applications and other high performance application such as aerospace. This paper outlines the recent international scientific and technological achievements towards the development of SiC/SiC composite material technologies for fusion application and discusses future research directions. It also reviews the materials system in the larger context of progress to maturity as an engineering material for both the larger nuclear community and broader engineering applications.

  10. Innovative SiC/SiC composite for nuclear applications

    International Nuclear Information System (INIS)

    Chaffron, L.; Sauder, C.; Lorrette, C.; Briottet, L.; Michaux, A.; Gelebart, L.; Coupe, A.; Zabiego, M.; Le Flem, M.; Seran, J. L.

    2013-01-01

    Among various refractory materials, SiC/SiC ceramic matrix composites (CMC) are of prime interest for fusion and advanced fission energy applications, due to their excellent irradiation tolerance and safety features (low activation, low tritium permeability,K). Initially developed as fuel cladding materials for the Fourth generation Gas cooled Fast Reactor (GFR), this material has been recently envisaged by CEA for different core structures of Sodium Fast Reactor (SFR) which combines fast neutrons and high temperature (500 deg.C). Regarding fuel cladding generic application, in the case of GFR, the first challenge facing this project is to demonstrate the feasibility of a fuel operating under very harsh conditions that are (i) temperatures of structures up to 700 deg.C in nominal and over 1600 deg.C in accidental conditions, (ii) irradiation damage higher than 60 dpa SiC , (iii) neutronic transparency, which disqualifies conventional refractory metals as structural core materials, (iv) mechanical behavior that guarantees in most circumstances the integrity of the first barrier (e.g.: ε> 0.5%), which excludes monolithic ceramics and therefore encourages the development of new types of fibrous composites SiC/SiC adapted to the fast reactor conditions. No existing material being capable to match all these requirements, CEA has launched an ambitious program of development of an advanced material satisfying the specifications [1]. This project, that implies many laboratories, inside and outside CEA, has permitted to obtain a very high quality compound that meets most of the challenging requirements. We present hereinafter few recent results obtained regarding the development of the composite. One of the most relevant challenges was to make a gas-tight composite up to the ultimate rupture. Indeed, multi-cracking of the matrix is the counterpart of the damageable behavior observed in these amazing compounds. Among different solutions envisaged, an innovative one has been

  11. Microstructural optimization of high temperature SiC/SiC composites by nite process

    International Nuclear Information System (INIS)

    Shimoda, K.; Park, J.S.; Hinoki, T.; Kohyama, A.

    2007-01-01

    Full text of publication follows: SiC/SiC composites are one of the promising structural materials for future fusion reactor because of the excellent potentiality in thermal and mechanical properties under very severe environment including high temperature and high energy neutron bombardment. For fusion-grade SiC/SiC composites, high-crystallinity and near-stoichiometric characteristic are required to keep excellent stability against neutron irradiation. The realization of the reactor will be strongly depend on optimization of SiC/SiC composites microstructure, particularly in regard to the materials and processes used for the fiber, interphase and matrix constituents. One of the important accomplishments is the new process, called nano-particle infiltration and transient eutectic phase (NITE) process developed in our group. The microstructure of NITE-SiC/SiC composites, such as fiber volume fraction, porosity and type of pores, can be controlled precisely by the selection of sintering temperature/applied stress history. The objective of this study is to investigate thermal stability and mechanical properties of NITE-SiC/SiC composites at high-temperature. Two kinds of highly-densified SiC/SiC composites with the difference of fiber volume fraction were prepared, and were subjected to exposure tests from 1000 deg. C to 1500 deg. C in an argon-oxygen gas mixture with an oxygen partial pressure of 0.1 Pa. The thermal stability of the composites was characterized through mass change and TEM/SEM observation. The in-situ tensile tests at 1300 deg. C and 1500 deg. C were carried out in the same atmosphere. Most of SiC/SiC composites, even for the advanced CVI-SiC/SiC composites with multi-layered SiC/C inter-phases, underwent reduction in the maximum strength by about 20% at 1300 deg. C. In particular, this reduction was attributed to a slight burnout of the carbon interphase due to oxygen impurities in test atmosphere. However, there was no significant degradation for

  12. Microstructural optimization of high temperature SiC/SiC composites by nite process

    Energy Technology Data Exchange (ETDEWEB)

    Shimoda, K. [Kyoto Univ., Graduate School of Energy Science (Japan); Park, J.S. [Kyoto Univ., Institute of Advanced Energy (Japan); Hinoki, T.; Kohyama, A. [Kyoto Univ., lnstitute of Advanced Energy, Gokasho, Uji (Japan)

    2007-07-01

    Full text of publication follows: SiC/SiC composites are one of the promising structural materials for future fusion reactor because of the excellent potentiality in thermal and mechanical properties under very severe environment including high temperature and high energy neutron bombardment. For fusion-grade SiC/SiC composites, high-crystallinity and near-stoichiometric characteristic are required to keep excellent stability against neutron irradiation. The realization of the reactor will be strongly depend on optimization of SiC/SiC composites microstructure, particularly in regard to the materials and processes used for the fiber, interphase and matrix constituents. One of the important accomplishments is the new process, called nano-particle infiltration and transient eutectic phase (NITE) process developed in our group. The microstructure of NITE-SiC/SiC composites, such as fiber volume fraction, porosity and type of pores, can be controlled precisely by the selection of sintering temperature/applied stress history. The objective of this study is to investigate thermal stability and mechanical properties of NITE-SiC/SiC composites at high-temperature. Two kinds of highly-densified SiC/SiC composites with the difference of fiber volume fraction were prepared, and were subjected to exposure tests from 1000 deg. C to 1500 deg. C in an argon-oxygen gas mixture with an oxygen partial pressure of 0.1 Pa. The thermal stability of the composites was characterized through mass change and TEM/SEM observation. The in-situ tensile tests at 1300 deg. C and 1500 deg. C were carried out in the same atmosphere. Most of SiC/SiC composites, even for the advanced CVI-SiC/SiC composites with multi-layered SiC/C inter-phases, underwent reduction in the maximum strength by about 20% at 1300 deg. C. In particular, this reduction was attributed to a slight burnout of the carbon interphase due to oxygen impurities in test atmosphere. However, there was no significant degradation for

  13. SiC/SiC composites through transient eutectic-phase route for fusion applications

    International Nuclear Information System (INIS)

    Katoh, Y.; Kohyama, A.; Nozawa, T.; Sato, M.

    2004-01-01

    Factors that may limit attractiveness of silicon-carbide-based ceramic composites to fusion applications include thermal conductivity, applicable design stress, chemical compatibility, hermeticity, radiation stability and fabrication cost. A novel SiC/SiC composite, which has recently been developed through nano-infiltration and transient eutectic-phase (NITE) processing route, surpasses conventional materials in many of these properties. In this paper, the latest development, property evaluation and prospect of the NITE SiC/SiC composites are briefly reviewed. The topics range from fundamental aspects of process development to industrial process development. Elevated temperature strength, fracture behavior, and thermo-physical properties in various environments are summarized. Future directions of materials and application technology development are also discussed

  14. Production of Al2O3–SiC nano-composites by spark plasma sintering

    International Nuclear Information System (INIS)

    Mansour Razavi; Ali Reza Farajipour; Mohammad Zakeri; Mohammad Reza Rahimipour; Ali Reza Firouzbakht

    2017-01-01

    In this paper, Al2O3–SiC composites were produced by SPS at temperatures of 1600°C for 10min under vacuum atmosphere. For preparing samples, Al2O3 with the second phase including of micro and nano-sized SiC powder were milled for 5h. The milled powders were sintered in a SPS machine. After sintering process, phase studies, densification and mechanical properties of Al2O3–SiC composites were examined. Results showed that the specimens containing micro-sized SiC have an important effect on bulk density, hardness and strength. The highest relative density, hardness and strength were 99.7%, 324.6 HV and 2329MPa, respectively, in Al2O3–20wt% SiCmicro composite. Due to short time sintering, the growth was limited and grains still remained in nano-meter scale. [es

  15. Mechanical properties of hot-pressed SiC-TiC composites

    Directory of Open Access Journals (Sweden)

    Kamil Kornaus

    2017-12-01

    Full Text Available SiC-TiC composites, with 0, 5, 10 and 20 vol.% of TiC, were sintered by the hot-pressing technique at temperature of 2000 °C under argon atmosphere. SiC sintering process was activated by liquid phase created by the reaction between Al2O3 and Y2O3, in which it is possible to dissolve passivating oxide layers (SiO2 and TiO2 and partially SiC and TiC carbides. Microstructure observation and density measurements confirmed that the composites were dense with uniformly distributed components. Differences in thermal expansion coefficients between SiC and TiC led to complex stress state occurrence. These stresses combined with the liquid-derived separate phase between grains boundaries increased fracture toughness of the composites, which ranged from 5.8 to 6.3 MPa·m0.5. Opposite to the bending strength, fracture toughness increased with the TiC volume fraction. By means of simulation of residual thermal stresses in the composites, it was found that with the increasing volume fraction of TiC, tensile stress in TiC grains is reduced simultaneously with strong rise of compressive stresses in the matrix.

  16. Aerospace Ceramic Materials: Thermal, Environmental Barrier Coatings and SiC/SiC Ceramic Matrix Composites for Turbine Engine Applications

    Science.gov (United States)

    Zhu, Dongming

    2018-01-01

    Ceramic materials play increasingly important roles in aerospace applications because ceramics have unique properties, including high temperature capability, high stiffness and strengths, excellent oxidation and corrosion resistance. Ceramic materials also generally have lower densities as compared to metallic materials, making them excellent candidates for light-weight hot-section components of aircraft turbine engines, rocket exhaust nozzles, and thermal protection systems for space vehicles when they are being used for high-temperature and ultra-high temperature ceramics applications. Ceramic matrix composites (CMCs), including non-oxide and oxide CMCs, are also recently being incorporated in gas turbine engines for high pressure and high temperature section components and exhaust nozzles. However, the complexity and variability of aerospace ceramic processing methods, compositions and microstructures, the relatively low fracture toughness of the ceramic materials, still remain the challenging factors for ceramic component design, validation, life prediction, and thus broader applications. This ceramic material section paper presents an overview of aerospace ceramic materials and their characteristics. A particular emphasis has been placed on high technology level (TRL) enabling ceramic systems, that is, turbine engine thermal and environmental barrier coating systems and non-oxide type SiC/SiC CMCs. The current status and future trend of thermal and environmental barrier coatings and SiC/SiC CMC development and applications are described.

  17. Gas leak tightness of SiC/SiC composites at elevated temperature

    Energy Technology Data Exchange (ETDEWEB)

    Hayasaka, Daisuke, E-mail: hayasaka@oasis.muroran-it.ac.jp [OASIS, Muroran Institute of Technology, Muroran, Hokkaido (Japan); Graduate School of Engineering, Muroran Institute of Technology, Muroran, Hokkaido (Japan); Park, Joon-Soo. [OASIS, Muroran Institute of Technology, Muroran, Hokkaido (Japan); Kishimoto, Hirotatsu [OASIS, Muroran Institute of Technology, Muroran, Hokkaido (Japan); Graduate School of Engineering, Muroran Institute of Technology, Muroran, Hokkaido (Japan); Kohyama, Akira [OASIS, Muroran Institute of Technology, Muroran, Hokkaido (Japan)

    2016-11-01

    Highlights: • NITE-SiC/SiC has extremely densified microstructure compared with other SiC/SiC composite like CVI. • Excellent helium and hydrogen gas-leak tightness of SiC/SiC composites by DEMO-NITE method from prototype industrialization production line was presented. • The excellence against stainless steel and Zircaloy at elevated temperature, together with generic excellent properties of SiC will be inevitable for innovative blanket and divertors for DEMO- and power- fusion reactors. - Abstract: SiC/SiC composite materials are attractive candidates for high heat flux components and blanket of fusion reactor, mainly due to their high temperature properties, radiation damage tolerance and low induced radioactivity. One of the challenges for SiC/SiC application in fusion reactors is to satisfy sufficient gas leak tightness of hydrogen and helium isotopes. Although many efforts have been carried-out, SiC/SiC composites by conventional processes have not been successful to satisfy the requirements, except SiC/SiC composites by NITE-methods. Toward the early realization of SiC/SiC components into fusion reactor systems process development of NITE-process has been continued. Followed to the brief introduction of recently developed DEMO-NITE process, baseline properties and hydrogen and helium gas leak tightness is presented. SiC/SiC claddings with 10 mm in diameter and 1 mm in wall thickness are tested by gas leak tightness system developed. The leak tightness measurements are done room temperature to 400 °C. Excellent gas leak tightness equivalent or superior to Zircaloy claddings for light water fission reactors is confirmed. The excellent gas leak tightness suggests nearly perfect suppression of large gas leak path in DEMO-NITE SiC/SiC.

  18. Development and Performance Evaluations of HfO2-Si and Rare Earth-Si Based Environmental Barrier Bond Coat Systems for SiC/SiC Ceramic Matrix Composites

    Science.gov (United States)

    Zhu, Dongming

    2014-01-01

    Ceramic environmental barrier coatings (EBC) and SiCSiC ceramic matrix composites (CMCs) will play a crucial role in future aircraft propulsion systems because of their ability to significantly increase engine operating temperatures, improve component durability, reduce engine weight and cooling requirements. Advanced EBC systems for SiCSiC CMC turbine and combustor hot section components are currently being developed to meet future turbine engine emission and performance goals. One of the significant material development challenges for the high temperature CMC components is to develop prime-reliant, high strength and high temperature capable environmental barrier coating bond coat systems, since the current silicon bond coat cannot meet the advanced EBC-CMC temperature and stability requirements. In this paper, advanced NASA HfO2-Si based EBC bond coat systems for SiCSiC CMC combustor and turbine airfoil applications are investigated. The coating design approach and stability requirements are specifically emphasized, with the development and implementation focusing on Plasma Sprayed (PS) and Electron Beam-Physic Vapor Deposited (EB-PVD) coating systems and the composition optimizations. High temperature properties of the HfO2-Si based bond coat systems, including the strength, fracture toughness, creep resistance, and oxidation resistance were evaluated in the temperature range of 1200 to 1500 C. Thermal gradient heat flux low cycle fatigue and furnace cyclic oxidation durability tests were also performed at temperatures up to 1500 C. The coating strength improvements, degradation and failure modes of the environmental barrier coating bond coat systems on SiCSiC CMCs tested in simulated stress-environment interactions are briefly discussed and supported by modeling. The performance enhancements of the HfO2-Si bond coat systems with rare earth element dopants and rare earth-silicon based bond coats are also highlighted. The advanced bond coat systems, when

  19. Minimum bar size for flexure testing of irradiated SiC/SiC composite

    International Nuclear Information System (INIS)

    Youngblood, G.E.; Jones, R.H.

    1998-01-01

    This report covers material presented at the IEA/Jupiter Joint International Workshop on SiC/SiC Composites for Fusion structural Applications held in conjunction with ICFRM-8, Sendai, Japan, Oct. 23-24, 1997. The minimum bar size for 4-point flexure testing of SiC/SiC composite recommended by PNNL for irradiation effects studies is 30 x 6 x 2 mm 3 with a span-to-depth ratio of 10/1

  20. Production of Al2O3–SiC nano-composites by spark plasma sintering

    Directory of Open Access Journals (Sweden)

    Mansour Razavi

    2017-07-01

    Full Text Available In this paper, Al2O3–SiC composites were produced by SPS at temperatures of 1600 °C for 10 min under vacuum atmosphere. For preparing samples, Al2O3 with the second phase including of micro and nano-sized SiC powder were milled for 5 h. The milled powders were sintered in a SPS machine. After sintering process, phase studies, densification and mechanical properties of Al2O3–SiC composites were examined. Results showed that the specimens containing micro-sized SiC have an important effect on bulk density, hardness and strength. The highest relative density, hardness and strength were 99.7%, 324.6 HV and 2329 MPa, respectively, in Al2O3–20 wt% SiCmicro composite. Due to short time sintering, the growth was limited and grains still remained in nano-meter scale.

  1. Joining of SiCf/SiC composites for thermonuclear fusion reactors

    International Nuclear Information System (INIS)

    Ferraris, M.; Badini, C.; Montorsi, M.; Appendino, P.; Scholz, H.W.

    1994-01-01

    Due to their favourable radiological behaviour, SiC f /SiC composites are promising structural materials for future use in fusion reactors. A problem to cope with is the joining of the ceramic composite material (CMC) to itself for more complex structures. Maintenance concepts for a reactor made of SiC f /SiC will demand a method of joining. The joining agents should comply with the low-activation approach of the base material. With the acceptable elements Si and Mg, sandwich structures of composite/metal/composite were prepared in Ar atmosphere at temperatures just above the melting points of the metals. Another promising route is the use of joining agents of boro-silicate glasses: their composition can be tailored to obtain softening temperatures of interest for fusion applications. The glassy joint can be easily ceramised to improve thermomechanical properties. The joining interfaces were investigated by SEM-EDS, XRD and mechanical tests. ((orig.))

  2. Interfacial characterization of CVI-SiC/SiC composites

    International Nuclear Information System (INIS)

    Yang, W.; Kohyama, A.; Noda, T.; Katoh, Y.; Hinoki, T.; Araki, H.; Yu, J.

    2002-01-01

    The mechanical properties of the interfaces of two families of chemical vapor infiltration SiC/SiC composites, advanced Tyranno-SA and Hi-Nicalon fibers reinforced SiC/SiC composites with various carbon and SiC/C interlayers, were investigated by single fiber push-out/push-back tests. Interfacial debonding and fibers sliding mainly occurred adjacent to the first carbon layer on the fibers. The interfacial debonding strengths and frictional stresses for both Tyranno-SA/SiC and Hi-Nicalon/SiC composites were correlated with the first carbon layer thickness. Tyranno-SA/SiC composites exhibited much larger interfacial frictional stresses compared to Hi-Nicalon/SiC composites. This was assumed to be mainly contributed by the rather rough surface of the Tyranno-SA fiber

  3. A novel pineapple-structured Si/TiO{sub 2} composite as anode material for lithium ion batteries

    Energy Technology Data Exchange (ETDEWEB)

    Yan, Dong; Bai, Ying; Yu, Caiyan; Li, Xiaoge; Zhang, Weifeng, E-mail: wfzhang6@163.com

    2014-10-01

    Highlights: • Pineapple-structured Si/TiO{sub 2} composite was firstly synthesized by a simple sol–gel method. • Pineapple-structured Si/TiO{sub 2} composite exhibits the best cycling stability. • TiO{sub 2} layer not only effectively inhibits the volume change of Si, but also contributes its electrochemical activity. - Abstract: Nanoscaled Si is successfully wrapped with different contents of nano-TiO{sub 2} (the molar ratios of Si/TiO{sub 2} composites are 1:1, 1:2, 1:3, 1:4 and 1:5, respectively) to form a novel pineapple structure. X-ray diffraction (XRD), Raman spectroscopy, X-ray photoelectron spectroscopy (XPS), field emission scanning electron microscopy (FESEM) and high resolution transmission electron microscopy (HRTEM) are utilized to characterize the structure, component, chemical environment and morphology of the composite. The investigation in cycling performances demonstrates that Si/TiO{sub 2} with molar ratio of 1:4 exhibits the best cycling stability, with specific capacity of 593 mA h g{sup −1} after 50 cycles at 0.1 C, much higher than those of the other composites and the pristine material. Cyclic voltammetry (CV) profiles are also measured and compared. It is believed that the outside TiO{sub 2} particles act as buffer against the huge volume change of Si during repeated alloying and de-alloying, which explains the improved electrochemical performances.

  4. Chemical vapor deposition of SiC on C-C composites as plasma facing materials for fusion application

    International Nuclear Information System (INIS)

    Kim, W. J.; Lee, M. Y.; Park, J. Y.; Hong, G. W.; Kim, J. I.; Choi, D. J.

    2000-01-01

    Because of the low activation and excellent mechanical properties at elevated temperatures, carbon-fiber reinforced carbon(C-C) composites have received much attention for plasma facing materials for fusion reactor and high-temperature structural applications such as aircrafts and space vehicles. These proposed applications have been frustrated by the lack of resistance to hydrogen erosion and oxidation on exposure to ambient oxidizing conditions at high temperature. Although Silicon Carbide (SiC) has shown excellent properties as an effective erosion-and oxidation-protection coating, many cracks are developed during fabrication and thermal cycles in use due to the Coefficients of Thermal Expansion(CTE) mismatch between SiC and C-C composite. In this study, we adopted a pyrolitic carbon as an interlayer between SiC and C-C substrate in order to minimize the CTE mismatch. The oxidation-protection performance of this composite was investigated as well

  5. Interweaved Si@C/CNTs and CNFs composites as anode materials for Li-ion batteries

    Energy Technology Data Exchange (ETDEWEB)

    Zhang, Miao [School of Physics and Telecommunication Engineering, South China Normal University, Guangzhou 510006 (China); Hou, Xianhua, E-mail: houxh@scnu.edu.cn [School of Physics and Telecommunication Engineering, South China Normal University, Guangzhou 510006 (China); Engineering Research Center of Materials and Technology for Electrochemical Energy Storage Ministry of Education, Guangzhou 510006 (China); Wang, Jie; Li, Min [School of Physics and Telecommunication Engineering, South China Normal University, Guangzhou 510006 (China); Hu, Shejun [School of Physics and Telecommunication Engineering, South China Normal University, Guangzhou 510006 (China); Engineering Research Center of Materials and Technology for Electrochemical Energy Storage Ministry of Education, Guangzhou 510006 (China); Shao, Zongping [Nanjing University of Technology, College of Chemistry and Chemical Engineering, Nanjing 210009 (China); Liu, Xiang [Institute of Advanced Materials, Nanjing University of Technology, Nanjing 210009 (China)

    2014-03-05

    Graphical abstract: In summary, a serious of high-energy wet ball milling, closed spray drying and subsequent chemical vapor deposition methods were introduced successfully to fabricated novel Si@C/CNTs and CNFs composites with carbon nanotubes and carbon nanofibres interweaved with carbon coated silicon spherical composites as superior anodes in lithium-ion batteries. The core-shell structure of Si@C composites can accommodate the volume change of electrode during charge and discharge. Meanwhile, the citric acid pyrolyzed carbon was coated on the surface of the silicon perfectly and constructs the connection network of nano silicon particles. Moreover, the carbon nanotubes and carbon nanofibres, which is interweaved with nano-silicon, also allows high electrical conductivity, improved solid–electrolyte interface formation and structural integrity. Compared with pure silicon and Si@C composites, the novel Si@C/CNTs and CNFs composites had the best combination of reversible capacity and cycleablity, and this anode materials exhibited excellent electrochemical performance. The Si/C composite had a fairly high initial discharge capacity of 2168.7 mA h g{sup −1} with an efficiency of 73%, and the discharge capacity of the 50th cycle maintained surprisingly of 1194.9 mA h g{sup −1}. Meanwhile, spray drying and chemical vapor deposition are environmentally friendly, economical, and relatively high-yield method for the production of the Si@C/CNTs and CNFs composites in large quantities. Consequently, the novel Si@C/CNTs and CNFs composite electrodes may be a potential alternative to graphite for high energy density lithium ion batteries. Highlights: • The core/shell structured silicon/carbon composites were prepared by a facile way. • The as-prepared Si@C/CNTs and CNFs composites shows excellent electrochemical performance. • The preparation method has mild experiment conditions and high production rate. • The structure benefited electronic transfer and

  6. Preparation and characterization of the electrodeposited Cr-Al{sub 2}O{sub 3}/SiC composite coating

    Energy Technology Data Exchange (ETDEWEB)

    Gao Jifeng, E-mail: readlot@tom.com [State Key Laboratory of Mould Technology, Institute of Materials Science and Engineering, Huazhong University of Science and Technology, Wuhan 430074 (China); Suo Jinping, E-mail: jpsuo@yahoo.com.cn [State Key Laboratory of Mould Technology, Institute of Materials Science and Engineering, Huazhong University of Science and Technology, Wuhan 430074 (China)

    2011-09-01

    To increase the SiC content in Cr-based coatings, Cr-Al{sub 2}O{sub 3}/SiC composite coatings were plated in Cr(VI) baths which contained Al{sub 2}O{sub 3}-coated SiC powders. The Al{sub 2}O{sub 3}-coated SiC composite particles were synthesized by calcining the precursor prepared by heterogeneous deposition method. The transmission electron microscopy analysis of the particles showed that the nano-SiC particle was packaged by alumina. The zeta potential of the particles collected from the bath was up to +23 mV, a favorable condition for the co-deposition of the particles and chromium. Pulse current was used during the electrodeposition. Scanning Electron Microscopy (SEM) indicated that the coating was compact and combined well with the substrate. Energy dispersive X-ray analysis of Cr-Al{sub 2}O{sub 3}/SiC coatings demonstrated that the concentration of SiC in the coating reached about 2.5 wt.%. The corrosion behavior of the composite coating was studied by potentiodynamic polarization and electrochemical impedance spectroscopy techniques. The data obtained suggested that the Al{sub 2}O{sub 3}/SiC particles significantly enhanced the corrosion resistance of the composite coating in 0.05 M HCl solution.

  7. Effect of heat treatment on microstructure and mechanical properties of PIP-SiC/SiC composites

    Energy Technology Data Exchange (ETDEWEB)

    Zhao, Shuang, E-mail: zhsh6007@126.com [Key Laboratory of Advanced Ceramic Fibres and Composites, College of Aerospace and Materials Engineering, National University of Defense Technology, Changsha 410073 (China); School of Mechanical, Aerospace, and Civil Engineering, University of Manchester, Manchester M13 9PL (United Kingdom); Zhou, Xingui; Yu, Jinshan [Key Laboratory of Advanced Ceramic Fibres and Composites, College of Aerospace and Materials Engineering, National University of Defense Technology, Changsha 410073 (China); Mummery, Paul [School of Mechanical, Aerospace, and Civil Engineering, University of Manchester, Manchester M13 9PL (United Kingdom)

    2013-01-01

    Continuous SiC fibre reinforced SiC matrix composites (SiC/SiC) have been studied as materials for heat resistant and nuclear applications. Thermal stability is one of the key issues for SiC/SiC composites. In this study, 3D SiC/SiC composites are fabricated via the polymer impregnation and pyrolysis (PIP) process, and then heat treated at 1400 Degree-Sign C, 1600 Degree-Sign C and 1800 Degree-Sign C in an inert atmosphere for 1 h, respectively. The effect of heat treatment on microstructure and mechanical properties of the composites is investigated. The results indicate that the mechanical properties of the SiC/SiC composites are significantly improved after heat treatment at 1400 Degree-Sign C mainly because the mechanical properties of the matrix are greatly improved due to crystallisation. With the increasing of heat treatment temperature, the properties of the composites are conversely decreased because of severe damage of the fibres and the matrix.

  8. Design of a creep experiment for SiC/SiC composites in HFIR

    Energy Technology Data Exchange (ETDEWEB)

    Hecht, S.L.; Hamilton, M.L.; Jones, R.H. [and others

    1997-08-01

    A new specimen was designed for performing in-reactor creep tests on composite materials, specifically on SiC/SiC composites. The design was tailored for irradiation at 800{degrees}C in a HFIR RB position. The specimen comprises a composite cylinder loaded by a pressurized internal bladder that is made of Nb1Zr. The experiment was designed for approximately a one year irradiation.

  9. Design of a creep experiment for SiC/SiC composites in HFIR

    International Nuclear Information System (INIS)

    Hecht, S.L.; Hamilton, M.L.; Jones, R.H.

    1997-01-01

    A new specimen was designed for performing in-reactor creep tests on composite materials, specifically on SiC/SiC composites. The design was tailored for irradiation at 800 degrees C in a HFIR RB position. The specimen comprises a composite cylinder loaded by a pressurized internal bladder that is made of Nb1Zr. The experiment was designed for approximately a one year irradiation

  10. Prototype tokamak fusion reactor based on SiC/SiC composite material focusing on easy maintenance

    International Nuclear Information System (INIS)

    Nishio, S.; Ueda, S.; Kurihara, R.; Kuroda, T.; Miura, H.; Sako, K.; Takase, H.; Seki, Y.; Adachi, J.; Yamazaki, S.; Hashimoto, T.; Mori, S.; Shinya, K.; Murakami, Y.; Senda, I.; Okano, K.; Asaoka, Y.; Yoshida, T.

    2000-01-01

    If the major part of the electric power demand is to be supplied by tokamak fusion power plants, the tokamak reactor must have an ultimate goal, i.e. must be excellent in construction cost, safety aspect and operational availability (maintainability and reliability), simultaneously. On way to the ultimate goal, the approach focusing on the safety and the availability (including reliability and maintainability) issues must be the more promising strategy. The tokamak reactor concept with the very high aspect ratio configuration and the structural material of SiC/SiC composite is compatible with this approach, which is called the DRastically Easy Maintenance (DREAM) approach. This is because SiC/SiC composite is a low activation material and an insulation material, and the high aspect ratio configuration leads to a good accessibility for the maintenance machines. As the intermediate steps along this strategy between the experimental reactor such as international thermonuclear experimental reactor (ITER) and the ultimate goal, a prototype reactor and an initial phase commercial reactor have been investigated. Especially for the prototype reactor, the material and technological immaturities are considered. The major features of the prototype and commercial type reactors are as follows. The fusion powers of the prototype and the commercial type are 1.5 and 5.5 GW, respectively. The major/minor radii for the prototype and the commercial type are of 12/1.5 m and 16/2 m, respectively. The plasma currents for the prototype and the commercial type are 6 and 9.2 MA, respectively. The coolant is helium gas, and the inlet/outlet temperatures of 500/800 and 600/900 deg. C for the prototype and the commercial type, respectively. The thermal efficiencies of 42 and 50% are obtainable in the prototype and the commercial type, respectively. The maximum toroidal field strengths of 18 and 20 tesla are assumed in the prototype and the commercial type, respectively. The thermal

  11. Fiber/matrix interfaces for SiC/SiC composites: Multilayer SiC coatings

    Energy Technology Data Exchange (ETDEWEB)

    Halverson, H.; Curtin, W.A. [Virginia Polytechnic Institute and State Univ., Blacksburg, VA (United States)

    1996-08-01

    Tensile tests have been performed on composites of CVI SiC matrix reinforced with 2-d Nicalon fiber cloth, with either pyrolitic carbon or multilayer CVD SiC coatings [Hypertherm High-Temperature Composites Inc., Huntington Beach, CA.] on the fibers. To investigate the role played by the different interfaces, several types of measurements are made on each sample: (i) unload-reload hysteresis loops, and (ii) acoustic emission. The pyrolitic carbon and multilayer SiC coated materials are remarkably similar in overall mechanical responses. These results demonstrate that low-modulus, or compliant, interface coatings are not necessary for good composite performance, and that complex, hierarchical coating structures may possibly yield enhanced high-temperature performance. Analysis of the unload/reload hysteresis loops also indicates that the usual {open_quotes}proportional limit{close_quotes} stress is actually slightly below the stress at which the 0{degrees} load-bearing fibers/matrix interfaces slide and are exposed to atmosphere.

  12. SiC/SiC composite fabricated with carbon nanotube interface layer and a novel precursor LPVCS

    Energy Technology Data Exchange (ETDEWEB)

    Zhao, Shuang, E-mail: zhsh6007@126.com [Science and Technology on Advanced Ceramic Fibers and Composites Laboratory, National University of Defense Technology, Changsha 410073 (China); School of Mechanical, Aerospace, and Civil Engineering, University of Manchester, Manchester M13 9PL (United Kingdom); Zhou, Xingui; Yu, Jinshan [Science and Technology on Advanced Ceramic Fibers and Composites Laboratory, National University of Defense Technology, Changsha 410073 (China); Mummery, Paul [School of Mechanical, Aerospace, and Civil Engineering, University of Manchester, Manchester M13 9PL (United Kingdom)

    2014-02-15

    Highlights: • The CNTs were distributed uniformly on the SiC fibers in the fabric by CVD process. • The microstructural evolution of the CNTs interface coating was studied. • The closed porosity was investigated by X-ray tomography. • The liquid precursor LPVCS exhibited high densification efficiency. - Abstract: Continuous SiC fiber reinforced SiC matrix composites (SiC/SiC) have been studied as promising candidate materials for nuclear applications. Three-dimensional SiC/SiC composite was fabricated via polymer impregnation and pyrolysis (PIP) process using carbon nanotubes (CNTs) as the interface layer and LPVCS as the polymer precursor. The microstructural evolution of the fiber/matrix interface was studied. The porosity, mechanical properties, thermal and electrical conductivities of the SiC/SiC composite were investigated. The results indicated that the high densification efficiency of the liquid precursor LPVCS resulted in a low porosity of the SiC/SiC composite. The SiC/SiC composite exhibited non-brittle fracture behavior, however, bending strength and fracture toughness of the composite were relatively low because of the absence of CNTs as the interface layer. The thermal and electrical conductivities of the SiC/SiC composite were low enough to meet the requirements desired for flow channel insert (FCI) applications.

  13. Zirconia toughened SiC whisker reinforced alumina composites small business innovation research

    Science.gov (United States)

    Loutfy, R. O.; Stuffle, K. L.; Withers, J. C.; Lee, C. T.

    1987-01-01

    The objective of this phase 1 project was to develop a ceramic composite with superior fracture toughness and high strength, based on combining two toughness inducing materials: zirconia for transformation toughening and SiC whiskers for reinforcement, in a controlled microstructure alumina matrix. The controlled matrix microstructure is obtained by controlling the nucleation frequency of the alumina gel with seeds (submicron alpha-alumina). The results demonstrate the technical feasibility of producing superior binary composites (Al2O3-ZrO2) and tertiary composites (Al2O3-ZrO2-SiC). Thirty-two composites were prepared, consolidated, and fracture toughness tested. Statistical analysis of the results showed that: (1) the SiC type is the key statistically significant factor for increased toughness; (2) sol-gel processing with a-alumina seed had a statistically significant effect on increasing toughness of the binary and tertiary composites compared to the corresponding mixed powder processing; and (3) ZrO2 content within the range investigated had a minor effect. Binary composites with an average critical fracture toughness of 6.6MPam sup 1/2, were obtained. Tertiary composites with critical fracture toughness in the range of 9.3 to 10.1 MPam sup 1/2 were obtained. Results indicate that these composites are superior to zirconia toughened alumina and SiC whisker reinforced alumina ceramic composites produced by conventional techniques with similar composition from published data.

  14. Elevated Temperature Properties of Commercially Available NITE-SiC/SiC Composites

    International Nuclear Information System (INIS)

    Choi, Y.B.; Hinoki, T.; Kohyama, A.

    2007-01-01

    Full text of publication follows: Continuous fiber-reinforced ceramic matrix composites (CMCs) have been expected as a new type of material having high fracture resistance up to a high temperature. In recent years, there have been extensive efforts in our research group to develop high performance SiC/SiC composites for energy applications, where improvements in mechanical properties and damage resistance by innovative new fabrication process with emphasis on interface improvement have been greatly accomplished. One of the most outstanding accomplishments is the Nano-powder Infiltration and Transient Eutectic (NITE) process using PyC coated Tyranno-SA fibers. For making SiC/SiC composites more attractive and competitive for high temperature structural components and for other industrial applications, one of the key issues is to demonstrate its reliability and safety under severe environments. Also to demonstrate the potential to produce SiC/SiC by NITE process from large scale production line at industries is very important. This paper provides fundamental database of mechanical properties and microstructure of Cera-NITE, the trade name of NITE-SiC/SiC composites. The mechanical properties were evaluated by uni-axial tensile test from room temperature to high temperatures. The tensile properties, including elastic modulus, PLS and ultimate tensile strength, are superior to those of other conventional SiC/SiC composites. The macroscopic observation of Cera-NITE indicated high density as planned with almost no-porosity and cracks. Furthermore, Cera-NITE showed outstanding microstructural uniformity. The characteristic variation coming from the sampling location was hardly observed.. Further information about database of properties and microstructure at evaluated temperature will be provided. (authors)

  15. Solvothermal synthesis of Mg-doped Li2FeSiO4/C nanocomposite cathode materials for lithium-ion batteries

    Science.gov (United States)

    Kumar, Ajay; Jayakumar, O. D.; Naik, V. M.; Nazri, G. A.; Naik, R.

    Lithium transition metal orthosilicates, such as Li2FeSiO4 and Li2MnSiO4, as cathode material have attracted much attention lately due to their high theoretical capacity ( 330 mAh/g), low cost, and environmental friendliness. However, they suffer from poor electronic conductivity and slow lithium ion diffusion in the solid phase. Several cation-doped orthosilicates have been studied to improve their electrochemical performance. We have synthesized partially Mg-substituted Li2Mgx Fe1-x SiO4-C, (x = 0.0, 0.01, 0.02, and 0.04) nano-composites by solvothermal method followed by annealing at 600oC in argon flow. The structure and morphology of the composites were characterized by XRD, SEM and TEM. The surface area and pore size distribution were measured by using N2 adsorption/desorption curves. The electrochemical performance of the Li2MgxFe1-x SiO4-C composites was evaluated by Galvanostatic cycling against metallic lithium anode, electrochemical impedance spectroscopy, and cyclic voltammetry. Li2Mg0.01Fe0.99SiO4-C sample shows a capacity of 278 mAh/g (at C/30 rate in the 1.5-4.6 V voltage window) with an excellent rate capability and stability, compared to the other samples. We attribute this observation to its higher surface area, enhanced electronic conductivity and higher lithium ion diffusion coefficient.

  16. Effect of irradiation on thermal expansion of SiCf/SiC composites

    International Nuclear Information System (INIS)

    Senor, D.J.; Trimble, D.J.; Woods, J.J.

    1996-06-01

    Linear thermal expansion was measured on five different SiC-fiber-reinforced/SiC-matrix (SiC f /SiC) composite types in the unirradiated and irradiated conditions. Two matrices were studied in combination with Nicalon CG reinforcement and a 150 nm PyC fiber/matrix interface: chemical vapor infiltrated (CVI) SiC and liquid-phase polymer impregnated precursor (PIP) SiC. Composites of PIP SiC with Tyranno and HPZ fiber reinforcement and a 150 nm PyC interface were also tested, as were PIP SiC composites with Nicalon CG reinforcement and a 150 nm BN fiber/matrix interface. The irradiation was conducted in the Experimental Breeder Reactor-II at a nominal temperature of 1,000 C to doses of either 33 or 43 dpa-SiC. Irradiation caused complete fiber/matrix debonding in the CVI SiC composites due to a dimensional stability mismatch between fiber and matrix, while the PIP SiC composites partially retained their fiber/matrix interface after irradiation. However, the thermal expansion of all the materials tested was found to be primarily dependent on the matrix and independent of either the fiber or the fiber/matrix interface. Further, irradiation had no significant effect on thermal expansion for either the CVI SiC or PIP SiC composites. In general, the thermal expansion of the CVI SiC composites exceeded that of the PIP SiC composites, particularly at elevated temperatures, but the expansion of both matrix types was less than chemical vapor deposited (CVD) β-SiC at all temperatures

  17. Microstructure and Mechanical Property of SiCf/SiC and Cf/SiC Composites

    International Nuclear Information System (INIS)

    Lee, S P; Cho, K S; Lee, H U; Lee, J K; Bae, D S; Byun, J H

    2011-01-01

    The mechanical properties of SiC based composites reinforced with different types of fabrics have been investigated, in conjunction with the detailed analyses of their microstructures. The thermal shock properties of SiC f /SiC composites were also examined. All composites showed a dense morphology in the matrix region. Carbon coated PW-SiC f /SiC composites had a good fracture energy, even if their strength was lower than that of PW-C f /SiC composites. SiC f /SiC composites represented a great reduction of flexural strength at the thermal shock temperature difference of 300 deg. C.

  18. The Effect of Nano sized Carbon Black on the Physical and Thermomechanical Properties of Al2O3-SiC-SiO2-C Composite

    International Nuclear Information System (INIS)

    Amin, M.H.; Ebrahimabadi, M.A.; Rahimipour, M.R.

    2009-01-01

    The effects of using nano sized carbon black in the range of 010 weight percentages on the physical and thermomechanical properties of Al 2 O 3 -Si C-SiO 2 graphite refractory composites were investigated. Nano sized carbon black addition improved the relative heat resistance and oxidation resistance of composites. The bulk density of the composites is reduced with increasing carbon black (CB) content. Increase in CB content first causes an increase in the apparent porosity, but at more than 3 wt % amount of CB, a decrease of apparent porosity was observed. The cold crushing strength (CCS) increased with increasing CB content in samples fired at 800 degree C and in samples fired at 1500 degree C when the content is increased to 3 wt %, but the CCS decreased with increasing CB content in samples fired at 1500 degree C when the CB content was less than 3 wt %. The composite without CB exhibits the highest value of CCS at firing temperature of 1500 degree C.

  19. In-situ generation of Li2FeSiO4/C nanocomposite as cathode material for lithium ion battery

    International Nuclear Information System (INIS)

    Yi, Jin; Hou, Meng-yan; Bao, Hong-liang; Wang, Cong-xiao; Wang, Jian-qiang; Xia, Yong-yao

    2014-01-01

    Highlights: • A Li 2 FeSiO 4 /C nanocomposite is prepared via thermal vapor deposition technology. • The Li 2 FeSiO 4 /C nanocomposite is free from impurity and coated with carbon layer. • The Li 2 FeSiO 4 /C nanocomposite exhibits good rate capability and cycling stability. • Lithium benzoate serves as both lithium and carbon sources. - Abstract: A Li 2 FeSiO 4 /C nanocomposite is prepared via solvothermal method in combination with carbon coating technology. The as-prepared Li 2 FeSiO 4 /C nanocomposite is a single phase Li 2 FeSiO 4 with nano-tickness coated carbon layer and connected by the mutual cross-linked carbon conductive matrix. As cathode material for lithium ion battery, the composite delivers a discharge capacity of 154 mAh g −1 at 1 C and exhibits good rate capability with a discharge capacity of 106 mAh g −1 at the rate of 10 C, which is ascribed to the small particle size and enhanced electronic conductivity using carbon coating technology. The as-prepared Li 2 FeSiO 4 /C nanocomposite also behaves a good cycling stability with capacity retention of over 100 cycles

  20. Organic/inorganic composite membranes based on polybenzimidazole and nano-SiO2

    International Nuclear Information System (INIS)

    Pu Hongting; Liu Lu; Chang Zhihong; Yuan Junjie

    2009-01-01

    Organic/inorganic composite membranes based on polybenzimidazole (PBI) and nano-SiO 2 were prepared in this work. However, the preparation of PBI/SiO 2 composite membrane is not easy since PBI is insoluble in water, while nano-SiO 2 is hydrophilic due to the hydrophilicity of nano-SiO 2 and water-insolubility of PBI. Thus, a solvent-exchange method was employed to prepare the composite membrane. The morphology of the composite membranes was studied by scanning electron microscopy (SEM). It was revealed that inorganic particles were dispersed homogenously in the PBI matrix. The thermal stability of the composite membrane is higher than that of pure PBI, both for doped and undoped membranes. PBI/SiO 2 composite membranes with up to 15 wt% SiO 2 exhibited improved mechanical properties compared with PBI membranes. The proton conductivity of the composite membranes containing phosphoric acid was studied. The nano-SiO 2 in the composite membranes enhanced the ability to trap phosphoric acid, which improved the proton conductivity of the composite membranes. The membrane with 15 wt% of inorganic material is oxidatively stable and has a proton conductivity of 3.9 x 10 -3 S/cm at 180 deg. C.

  1. Fabrication and characterization of 2.5D and 3D SiC{sub f}/SiC composites

    Energy Technology Data Exchange (ETDEWEB)

    Zhao, Shuang, E-mail: zhsh6007@126.co [Key Laboratory of Advanced Ceramic Fibers and Composites, National University of Defense Technology, Changsha 410073 (China); School of Mechanical, Aerospace, and Civil Engineering, University of Manchester, Manchester M13 9PL (United Kingdom); Zhou, Xingui; Yu, Jinshan [Key Laboratory of Advanced Ceramic Fibers and Composites, National University of Defense Technology, Changsha 410073 (China); Mummery, Paul [School of Mechanical, Aerospace, and Civil Engineering, University of Manchester, Manchester M13 9PL (United Kingdom)

    2013-10-15

    Highlights: • 2.5D and 3D KD-I SiC fiber fabrics were used as the reinforcement. • Closed porosity was investigated by X-ray tomographic techniques. • The properties of the composites were improved by the CVD process. -- Abstract: SiC{sub f}/SiC composites are considered promising candidate materials for fusion applications. 2.5D and 3D KD-I SiC fiber fabrics were used as the reinforcement and SiC{sub f}/SiC composites were fabricated via polymer impregnation and pyrolysis (PIP) process and coated with chemical vapor deposited (CVD) SiC. The porosity, thermal conductivity and mechanical property of the composites were characterized. The results indicated that 2.5D and 3D SiC{sub f}/SiC composites fabricated via PIP process exhibited high porosity, and hence low thermal conductivity. After the CVD process, the density, thermal conductivity and mechanical properties of the composites were increased.

  2. Preparation & characterization of SiO2 interface layer by dip coating technique on carbon fibre for Cf/SiC composites

    Science.gov (United States)

    Kumar, Kundan; Jariwala, C.; Pillai, R.; Chauhan, N.; Raole, P. M.

    2015-08-01

    Carbon fibres (Cf) are one of the most important reinforced materials for ceramic matrix composites such as Cf - SiC composites and they are generally sought for high temperature applications in as space application, nuclear reactor and automobile industries. But the major problem arise when Cf reinforced composites exposed to high temperature in an oxidizing environment, Cf react with oxygen and burnt away. In present work, we have studied the effect of silica (SiO2) coating as a protective coating on Cf for the Cf / SiC composites. The silica solution prepared by the sol-gel process and coating on Cf is done by dip coating technique with varying the withdrawing speed i.e. 2, 5, 8 mm/s with fixed dipping cycle (3 Nos.). The uniform silica coating on the Cf is shown by the Scanning Electron Microscope (SEM) analysis. The tensile test shows the increase in tensile strength with respect to increase in withdrawing speed. The isothermal oxidation analysis confirmed enhancement of oxidation resistance of silica coated Cf as compared tothe uncoated Cf.

  3. Influence of Constituents on Creep Properties of SiC/SiC Composites

    Science.gov (United States)

    Bhatt, R.; DiCarlo, J.

    2016-01-01

    SiC-SiC composites are being considered as potential candidate materials for next generation turbine components such as combustor liners, nozzle vanes and blades because of their low density, high temperature capability, and tailorable mechanical properties. These composites are essentially fabricated by infiltrating matrix into a stacked array of fibers or fiber preform by one or a combination of manufacturing methods such as, Melt Infiltration (MI) of molten silicon metal, Chemical Vapor Infiltration (CVI), Polymer Infiltration and Pyrolysis (PIP). To understand the influence of constituents, the SiC-SiC composites fabricated by MI, CVI, and PIP methods were creep tested in air between 12000 and 14500 degrees Centigrade for up to 500 hours. The failed specimens were analyzed under a scanning electron microscope to assess damage mechanisms. Also, knowing the creep deformation parameters of the fiber and the matrix under the testing conditions, the creep behavior of the composites was modeled and compared with the measured data. The implications of the results on the long term durability of these composites will be discussed.

  4. Effect of different parameters on machining of SiC/SiC composites via pico-second laser

    Energy Technology Data Exchange (ETDEWEB)

    Li, Weinan; Zhang, Ruoheng [State Key Laboratory of Transient Optics and Photonics, Xi’an Institute of Optics and Precision Mechanics, Chinese Academy of Sciences, Xi’an, Shaanxi 10068 (China); Liu, Yongsheng, E-mail: yongshengliu@nwpu.edu.cn [Science and technology on Thermostructure Composite Materials Laboratory, Northwestern Polytechnical University, Xi’an, Shaanxi 710072 (China); Wang, Chunhui; Wang, Jing [Science and technology on Thermostructure Composite Materials Laboratory, Northwestern Polytechnical University, Xi’an, Shaanxi 710072 (China); Yang, Xiaojun [State Key Laboratory of Transient Optics and Photonics, Xi’an Institute of Optics and Precision Mechanics, Chinese Academy of Sciences, Xi’an, Shaanxi 10068 (China); Cheng, Laifei [Science and technology on Thermostructure Composite Materials Laboratory, Northwestern Polytechnical University, Xi’an, Shaanxi 710072 (China)

    2016-02-28

    Graphical abstract: - Highlights: • The highlights of the manuscript include the following two aspects. • First, we found that the different machining modes (helical line scanning and single ring line scanning) and processing power of machining have remarkable effect on the surface morphology of the machined area, such as the shape, depth and the formation of different surface structures. • Secondly, we investigated that the debris consisted of C, Si and O was observed on the machined surface. • Some of the Si–C bonds of the SiC matrix and fibers would be transformed into Si–O bonds after machined, depending on the processing power. - Abstract: Pico-second laser plays an important role in modern machining technology, especially in machining high hardness materials. In this article, pico-second laser was utilized for irradiation on SiC/SiC composites, and effects of different processing parameters including the machining modes and laser power were discussed in detail. The results indicated that the machining modes and laser power had great effect on machining of SiC/SiC composites. Different types of surface morphology and structure were observed under helical line scanning and single ring line scanning, and the analysis of their formulation was discussed in detail. It was believed that the machining modes would be responsible to the different shapes of machining results at the same parameters. The processing power shall also influence the surface morphology and quality of machining results. In micro-hole drilling process, large amount of debris and fragments were observed within the micro-holes, and XPS analysis showed that there existed Si–O bonds and Si–C bonds, indicating that the oxidation during processing was incomplete. Other surface morphology, such as pores and pits were discussed as well.

  5. Production of Al2O3–SiC nano-composites by spark plasma sintering; Producción de nano-compositesSiC–Al2O3 por spark plasma sinterizado

    Energy Technology Data Exchange (ETDEWEB)

    Mansour Razavi; Ali Reza Farajipour; Mohammad Zakeri; Mohammad Reza Rahimipour; Ali Reza Firouzbakht

    2017-11-01

    In this paper, Al2O3–SiC composites were produced by SPS at temperatures of 1600°C for 10min under vacuum atmosphere. For preparing samples, Al2O3 with the second phase including of micro and nano-sized SiC powder were milled for 5h. The milled powders were sintered in a SPS machine. After sintering process, phase studies, densification and mechanical properties of Al2O3–SiC composites were examined. Results showed that the specimens containing micro-sized SiC have an important effect on bulk density, hardness and strength. The highest relative density, hardness and strength were 99.7%, 324.6 HV and 2329MPa, respectively, in Al2O3–20wt% SiCmicro composite. Due to short time sintering, the growth was limited and grains still remained in nano-meter scale. [Spanish] En este trabajo se muestran compuestos de Al2O3-SiC producidos por SPS, en vacío, a 1.600 °C durante 10 min. Para la preparación de muestras, se molieron polvos de Al2O3 durante 5 h con la segunda fase de micro-y-nano polvo de SiC. Posteriormente, estos polvos molidos se sinterizaron mediante SPS. Después del proceso de sinterización, se realizaron estudios de fase, densificación y propiedades mecánicas de los compuestos de Al2O3-SiC obtenidos. Los resultados mostraron que micro-SiC en las muestras tiene un efecto importante en su densidad aparente, dureza y resistencia. La mayor densidad relativa, dureza y resistencia fueron respectivamente del 99,7%, 324,6 HV y 2.329 MPa para Al2O3 con un 20% en peso micro-SiC. Debido al corto tiempo de sinterización, el crecimiento los granos fue limitado y se mantuvieron en escala nanométrica.

  6. Residual stresses and mechanical properties of Si3N4/SiC multilayered composites with different SiC layers

    International Nuclear Information System (INIS)

    Liua, S.; Lia, Y.; Chena, P.; Lia, W.; Gaoa, S.; Zhang, B.; Yeb, F.

    2017-01-01

    The effect of residual stresses on the strength, toughness and work of fracture of Si3N4/SiC multilayered composites with different SiC layers has been investigated. It may be an effective way to design and optimize the mechanical properties of Si3N4/SiC multilayered composites by controlling the properties of SiC layers. Si3N4/SiC multilayered composites with different SiC layers were fabricated by aqueous tape casting and pressureless sintering. Residual stresses were calculated by using ANSYS simulation, the maximum values of tensile and compressive stresses were 553.2MPa and −552.1MPa, respectively. Step-like fracture was observed from the fracture surfaces. Fraction of delamination layers increased with the residual stress, which can improve the reliability of the materials. Tensile residual stress was benefit to improving toughness and work of fracture, but the strength of the composites decreased. [es

  7. Use of SiCf/SiC ceramic composites as structure material of a fusion reactor toroid internal components

    International Nuclear Information System (INIS)

    Aiello, G.

    2001-01-01

    The use of low neutron-induced activation structural materials seems necessary in order to improve safety in future fusion power reactors. Among them, SiC f /SiC composites appear as a very promising solution because of their low activation characteristics coupled with excellent mechanical properties at high temperatures. With the main objective of evaluating the limit of present-day composites, a tritium breeding blanket using SiC f /SiC as structural material (the TAURO blanket) has been developed in the last years by the Commissariat a l'Energie Atomique (CEA). The purpose of this thesis was to modify the available design tools (computer codes, design criteria), normally used for the analyses of metallic structures, in order to better take into account the mechanical behaviour of SiC f /SiC. Alter a preliminary improvement of the calculation methods, two main topics of study could be identified: the modelling of the mechanical behaviour of the composite and the assessment of appropriate design criteria. The different behavioural models available in literature were analysed in order to find the one that was the best suited to the specific problems met in the field of fusion power. The selected model was then implemented in the finite elements code CASTEM 2000 used within the CEA for the thermo-mechanical analyses of the TAURO blanket. For the design of the blanket, we proposed a new resistance criterion whose main advantage, with respect to the other examined, lies in the easiness of identification. The suggested solutions were then applied in the design studies of the TAURO blanket. We then could show that the use of appropriate calculation methodologies is necessary in order to achieve a correct design of the blanket and a more realistic estimate of the limits of present day composites. The obtained results can also be extended to all nuclear components making use of SiC f /SiC structures. (author) [fr

  8. Lost foam casting of aluminum alloy-SiCp composite material

    International Nuclear Information System (INIS)

    Baalasuburamaniam, R.; Cvetnic, C.; Ravindran, C.

    2002-01-01

    Metal matrix composites are a viable alternative to cast irons in automotive components with possible increase in strength-to-weight ratio. Lost foam casting of aluminum alloy matrix composite containing 20 volume percent SiC was carried out at 690, 730, and 770 o C with a view to determining the effects of cooling rate on microstructure, particle distribution, microporosity and mechanical properties. These results were compared with those for the matrix material cast under similar conditions. The results and the correlations are of particular interest as there is no published literature on lost foam casting of composite materials. (author)

  9. Fiber/matrix interfacial thermal conductance effect on the thermal conductivity of SiC/SiC composites

    International Nuclear Information System (INIS)

    Nguyen, Ba Nghiep; Henager, Charles H.

    2013-01-01

    SiC/SiC composites used in fusion reactor applications are subjected to high heat fluxes and require knowledge and tailoring of their in-service thermal conductivity. Accurately predicting the thermal conductivity of SiC/SiC composites as a function of temperature will guide the design of these materials for their intended use, which will eventually include the effects of 14-MeV neutron irradiations. This paper applies an Eshelby–Mori–Tanaka approach (EMTA) to compute the thermal conductivity of unirradiated SiC/SiC composites. The homogenization procedure includes three steps. In the first step EMTA computes the homogenized thermal conductivity of the unidirectional (UD) SiC fiber embraced by its coating layer. The second step computes the thermal conductivity of the UD composite formed by the equivalent SiC fibers embedded in a SiC matrix, and finally the thermal conductivity of the as-formed SiC/SiC composite is obtained by averaging the solution for the UD composite over all possible fiber orientations using the second-order fiber orientation tensor. The EMTA predictions for the transverse thermal conductivity of several types of SiC/SiC composites with different fiber types and interfaces are compared to the predicted and experimental results by Youngblood et al. [J. Nucl. Mater. 307–311 (2002) 1120–1125, Fusion Sci. Technol. 45 (2004) 583–591, Compos. Sci. Technol. 62 (2002) 1127–1139.

  10. Significantly Enhanced Dielectric Performances and High Thermal Conductivity in Poly(vinylidene fluoride)-Based Composites Enabled by SiC@SiO2 Core-Shell Whiskers Alignment.

    Science.gov (United States)

    He, Dalong; Wang, Yao; Song, Silong; Liu, Song; Deng, Yuan

    2017-12-27

    Design of composites with ordered fillers arrangement results in anisotropic performances with greatly enhanced properties along a specific direction, which is a powerful tool to optimize physical properties of composites. Well-aligned core-shell SiC@SiO 2 whiskers in poly(vinylidene fluoride) (PVDF) matrix has been achieved via a modified spinning approach. Because of the high aspect ratio of SiC whiskers, strong anisotropy and significant enhancement in dielectric constant were observed with permittivity 854 along the parallel direction versus 71 along the perpendicular direction at 20 vol % SiC@SiO 2 loading, while little increase in dielectric loss was found due to the highly insulating SiO 2 shell. The anisotropic dielectric behavior of the composite is perfectly understood macroscopically to have originated from anisotropic intensity of interfacial polarization based on an equivalent circuit model of two parallel RC circuits connected in series. Furthermore, finite element simulations on the three-dimensional distribution of local electric field, polarization, and leakage current density in oriented SiC@SiO 2 /PVDF composites under different applied electrical field directions unambiguously revealed that aligned core-shell SiC@SiO 2 whiskers with a high aspect ratio significantly improved dielectric performances. Importantly, the thermal conductivity of the composite was synchronously enhanced over 7 times as compared to that of PVDF matrix along the parallel direction at 20 vol % SiC@SiO 2 whiskers loading. This study highlights an effective strategy to achieve excellent comprehensive properties for high-k dielectrics.

  11. Mechanical properties of MeV ion-irradiated SiC/SiC composites characterized by indentation technique

    International Nuclear Information System (INIS)

    Park, J.Y.; Park, K.H.; Kim, W.; Kishimoto, H.; Kohyama, A.

    2007-01-01

    Full text of publication follows: SiC/SiC composites have been considered as a structural material for advanced fusion concepts. In the core of fusion reactor, those SiC/SiC composites are experienced the complex attacks such as strong neutron, high temperature and transmuted gases. One of the vital data for designing the SiC/SiC composites to the fusion reactor is mechanical properties under the severe neutron irradiation. In this work, various SiC/SiC composites were prepared by the different fabrication processes like CVI (chemical vapor infiltration), WA-CVI (SiC whisker assisted CVI) and hot-pressed method. The expected neutron irradiation was simulated by a silicon self-ion irradiation at a DuET facility; Dual-beam for Energy Technologies, Kyoto University. The irradiation temperature were 600 deg. C and 1200 deg. C, and the irradiation does were 5 dpa and 20 dpa, respectively. The 5.1 MeV Si ions were irradiated to the intrinsic CVI-SiC, SiC whisker reinforced SiC and SiC composites produced by hot-press method. The mechanical properties like hardness, elastic modulus and fracture toughness were characterized by an indentation technique. The ion irradiation caused the increase of the hardness and fracture toughness, which was dependent on the irradiation temperature. SiC whisker reinforcement in the SiC matrix accelerated the increase of the fracture toughness by the ion irradiation. For SiC/SiC composites after the ion irradiation, this work will provide the additional data for the mechanical properties as well as the effect of SiC whisker reinforcement. (authors)

  12. Environmental Stability and Oxidation Behavior of HfO2-Si and YbGd(O) Based Environmental Barrier Coating Systems for SiCSiC Ceramic Matrix Composites

    Science.gov (United States)

    Zhu, Dongming; Farmer, Serene; McCue, Terry R.; Harder, Bryan; Hurst, Janet B.

    2017-01-01

    Ceramic environmental barrier coatings (EBC) and SiCSiC ceramic matrix composites (CMCs) will play a crucial role in future aircraft propulsion systems because of their ability to significantly increase engine operating temperatures, improve component durability, reduce engine weight and cooling requirements. Advanced EBC systems for SiCSiC CMC turbine and combustor hot section components are currently being developed to meet future turbine engine emission and performance goals. One of the significant material development challenges for the high temperature CMC components is to develop prime-reliant, environmental durable environmental barrier coating systems. In this paper, the durability and performance of advanced Electron Beam-Physical Vapor Deposition (EB-PVD) NASA HfO2-Si and YbGdSi(O) EBC bond coat top coat systems for SiCSiC CMC have been summarized. The high temperature thermomechanical creep, fatigue and oxidation resistance have been investigated in the laboratory simulated high-heat-flux environmental test conditions. The advanced NASA EBC systems showed promise to achieve 1500C temperature capability, helping enable next generation turbine engines with significantly improved engine component temperature capability and durability.

  13. Synthesis of micro-sized interconnected Si-C composites

    Science.gov (United States)

    Wang, Donghai; Yi, Ran; Dai, Fang

    2016-02-23

    Embodiments provide a method of producing micro-sized Si--C composites or doped Si--C and Si alloy-C with interconnected nanoscle Si and C building blocks through converting commercially available SiO.sub.x (0

  14. Fabrication and characterization of SiC and ZrC composite coating on TRISO coated particle

    Energy Technology Data Exchange (ETDEWEB)

    Lee, H. G.; Lee, S. H.; Kim, D. J.; Park, J. Y.; Kim, W. J. [Korea Atomic Energy Research Institute, Daejeon (Korea, Republic of)

    2016-10-15

    SiC coating is widely suggested as structural materials for nuclear application due to its excellent high irradiation resistance properties and high temperature mechanical properties. SiC coating on TRistructural-ISOtropic (TRISO) coated fuel particles plays an important role as a protective layer from radioactive fission gas and a mechanical structural layer. TRISO coating layer was deposited on a spherical particle by a FBCVD method. The ZrO{sub 2} spherical particles were used as a simulant kernel. TRISO coating layers consisting of a porous buffer layer, an inner PyC layer were sequentially deposited before depositing SiC or ZrC coating layer. In order investigate the phase of each composite coating layer, Raman analysis was conducted. SiC, ZrC coating and SiC/ZrC composite coating on spherical particle were successfully deposited via FBCVD method by adjusting source gas flow rate. In the SiC and ZrC composite coating, SiC phase and ZrC phase were observed by XRD and SEM analysis. In the condition of 100 sccm of ZrCl{sub 4}, 25 sccm of CH{sub 4}, and 30 sccm of MTS, only two phases of SiC and ZrC were observed and two phases are located with clean grain boundary.

  15. The Degradation Behavior of SiCf/SiO2 Composites in High-Temperature Environment

    Science.gov (United States)

    Yang, Xiang; Cao, Feng; Qing, Wang; Peng, Zhi-hang; Wang, Yi

    2018-04-01

    SiCf/SiO2 composites had been fabricated efficiently by Sol-Gel method. The oxidation behavior, thermal shock property and ablation behavior of SiCf/SiO2 composites was investigated. SiCf/SiO2 composites showed higher oxidation resistance in oxidation atmosphere, the flexural strength retention ratio was larger than 90.00%. After 1300 °C thermal shock, the mass retention ratio was 97.00%, and the flexural strength retention ratio was 92.60%, while after 1500 °C thermal shock, the mass retention ratio was 95.37%, and the flexural strength retention ratio was 83.34%. After 15 s ablation, the mass loss rate was 0.049 g/s and recession loss rate was 0.067 mm/s. The SiO2 matrix was melted in priority and becomes loosen and porous. With the ablation going on, the oxides were washed away by the shearing action of the oxyacetylene flame. The evaporation of SiO2 took away large amount of heat, which is also beneficial to the protection for SiCf/SiO2 composites.

  16. Microstructure and mechanical properties of SiC materials

    International Nuclear Information System (INIS)

    Yarahmadi, M.

    1985-01-01

    The effect of the microstructure on the mechanical properties of SiC materials of different chemical composition (SSiC, SiSiC, and RSiC) was investigated. Furthermore, the creep strength was determined on oxidized samples and on non-pretreated samples. (HSCH)

  17. Influence of surface morphology and UFG on damping and mechanical properties of composite reinforced with spinel MgAl{sub 2}O{sub 4}-SiC core-shell microcomposites

    Energy Technology Data Exchange (ETDEWEB)

    Singh, Subhash; Pal, Kaushik, E-mail: pl_kshk@yahoo.co.in

    2017-01-15

    Interface between ceramic particulate and matrix is known to control the response of the materials and functionality of the composite. Among numerous physical properties, grain structure of the materials has also played a significant role in defining the behaviour of metal matrix composites. Usually, silicon carbide (SiC) particles show poor interfacial wettability in aluminium melt. Herein, we were successfully synthesized magnesium oxide (MgO) and nanocrystalline magnesium aluminate (MgAl{sub 2}O{sub 4}) spinel coated silicon carbide (SiC) core-shell micro-composites through sol-gel technique to improve the wettability of dispersoids. Core-shell structures of submicron size were thoroughly investigated by various characterization techniques. Further, aluminium matrix composites incorporated with pristine SiC, MgO grafted SiC and MgAl{sub 2}O{sub 4} grafted SiC particles were fabricated by stir casting technique, respectively. Additionally, as-cast composites were processed via friction stir processing (FSP) technique to observe the influence of grain refinement on mechanical and damping properties. Electron back scattered diffraction (EBSD), Field emission scanning electron microscopy (FE-SEM) and X-ray energy dispersion spectroscopy (EDX) analysis were conducted for investigating grain size refinement, adequate dispersion, stability and de-agglomeration of encapsulated SiC particles in aluminium matrix. The mechanical as well as thermal cyclic (from − 100 to 400 °C) damping performance of the as-cast and friction stir processed composites were studied, respectively. Finally, the enhanced properties were attributable to reduced agglomeration, stabilization and proper dispersion of the tailored SiC particles Al matrix. - Highlights: •Synthesizing a novel coating layer of MgO and MgAl{sub 2}O{sub 4} spinel onto SiC particles •Significant improvement in UTS and hardness by reinforcing tailored SiC in Al •Significant grain refinements were obtained through

  18. Purity and radioactive decay behaviour of industrial 2D-reinforced SiCf/SiC composites

    International Nuclear Information System (INIS)

    Scholz, H.W.; Zucchetti, M.; Casteleyn, K.; Adelhelm, C.

    1994-01-01

    Ceramic matrix composites based on SiC with continuous fibres (SiC f /SiC) are considered promising structural materials for future fusion devices. It was still to clarify, whether impurities in industrial SiC f /SiC could jeopardise radiological advantages. Experimental impurity analyses revealed a two-dimensionally reinforced SiC f /SiC with the matrix produced by CVI as very pure. Chemo-spectrometric methods were combined with radioactivation methods (CPAA, NAA). A quantification of the main constituents Si, C and O was added. Calculations with the FISPACT-2.4 code and EAF-2 library identified elements detrimental for different low-activation criteria. For the neutron exposure, EEF reactor-study first wall and blanket conditions were simulated. The calculated SiC f /SiC included 48 trace elements. Even under conservative assumptions, all low-activation limits of European interest are fulfilled. Exclusively the hands-on recycling limit for the First Wall can intrinsically not be satisfied with SiC. The theoretical goal of a SiC f /SiC depleted of 28 Si (isotopic tailoring) is critically discussed. ((orig.))

  19. Synthesis and characterization of laminated Si/SiC composites

    Science.gov (United States)

    Naga, Salma M.; Kenawy, Sayed H.; Awaad, Mohamed; Abd El-Wahab, Hamada S.; Greil, Peter; Abadir, Magdi F.

    2012-01-01

    Laminated Si/SiC ceramics were synthesized from porous preforms of biogenous carbon impregnated with Si slurry at a temperature of 1500 °C for 2 h. Due to the capillarity infiltration with Si, both intrinsic micro- and macrostructure in the carbon preform were retained within the final ceramics. The SEM micrographs indicate that the final material exhibits a distinguished laminar structure with successive Si/SiC layers. The produced composites show weight gain of ≈5% after heat treatment in air at 1300 °C for 50 h. The produced bodies could be used as high temperature gas filters as indicated from the permeability results. PMID:25685404

  20. Synthesis and characterization of laminated Si/SiC composites

    Directory of Open Access Journals (Sweden)

    Salma M. Naga

    2013-01-01

    Full Text Available Laminated Si/SiC ceramics were synthesized from porous preforms of biogenous carbon impregnated with Si slurry at a temperature of 1500 °C for 2 h. Due to the capillarity infiltration with Si, both intrinsic micro- and macrostructure in the carbon preform were retained within the final ceramics. The SEM micrographs indicate that the final material exhibits a distinguished laminar structure with successive Si/SiC layers. The produced composites show weight gain of ≈5% after heat treatment in air at 1300 °C for 50 h. The produced bodies could be used as high temperature gas filters as indicated from the permeability results.

  1. Carbon fiber/SiC composite for reduced activation

    International Nuclear Information System (INIS)

    Noda, T.; Araki, H.; Abe, F.; Okada, M.

    1991-01-01

    A carbon fiber/SiC composite fabricated by a chemical vapor infiltration process at 1173-1623 K was studied to develop a low-activation material. A high-purity composite was obtained with the total amount of impurities less than 0.02 wt%. The microstructure and the mechanical properties using a bend test were examined. A composite with woven carbon yarn showed both high strength and toughness. Further, the induced activity of the material was evaluated by calculations simulating fusion neutron irradiation. The carbon fiber/SiC composite shows an excellent low-activation behavior. (orig.)

  2. Synthesis of high-performance Li2FeSiO4/C composite powder by spray-freezing/freeze-drying a solution with two carbon sources

    Science.gov (United States)

    Fujita, Yukiko; Iwase, Hiroaki; Shida, Kenji; Liao, Jinsun; Fukui, Takehisa; Matsuda, Motohide

    2017-09-01

    Li2FeSiO4 is a promising cathode active material for lithium-ion batteries due to its high theoretical capacity. Spray-freezing/freeze-drying, a practical process reported for the synthesis of various ceramic powders, is applied to the synthesis of Li2FeSiO4/C composite powders and high-performance Li2FeSiO4/C composite powders are successfully synthesized by using starting solutions containing both Indian ink and glucose as carbon sources followed by heating. The synthesized composite powders have a unique structure, composed of Li2FeSiO4 nanoparticles coated with a thin carbon layer formed by the carbonization of glucose and carbon nanoparticles from Indian ink. The carbon layer enhances the electrochemical reactivity of the Li2FeSiO4, and the carbon nanoparticles play a role in the formation of electron-conducting paths in the cathode. The composite powders deliver an initial discharge capacity of 195 and 137 mAh g-1 at 0.1 C and 1 C, respectively, without further addition of conductive additive. The discharge capacity at 1 C is 72 mAh g-1 after the 100th cycle, corresponding to approximately 75% of the capacity at the 2nd cycle.

  3. Mechanical behavior of SiCf/SiC composites with alternating PyC/SiC multilayer interphases

    International Nuclear Information System (INIS)

    Yu, Haijiao; Zhou, Xingui; Zhang, Wei; Peng, Huaxin; Zhang, Changrui

    2013-01-01

    Highlights: ► Superior combination of flexural strength and fracture toughness of the 3D SiC/SiC composite was achieved by interface tailoring. ► Resulted composite possesses a much higher flexural strength and fracture toughness than its counterparts in literatures. ► Mechanisms that PyC/SiC multilayer coatings improve the mechanical properties were illustrated. -- Abstract: In order to tailor the fiber–matrix interface of continuous silicon carbide fiber reinforced silicon carbide (SiC f /SiC) composites for improved fracture toughness, alternating pyrolytic carbon/silicon carbide (PyC/SiC) multilayer coatings were applied to the KD-I SiC fibers using chemical vapor deposition (CVD) method. Three dimensional (3D) KD-I SiC f /SiC composites reinforced by these coated fibers were fabricated using a precursor infiltration and pyrolysis (PIP) process. The interfacial characteristics were determined by the fiber push-out test and microstructural examination using scanning electron microscopy (SEM). The effect of interface coatings on composite mechanical properties was evaluated by single-edge notched beam (SENB) test and three-point bending test. The results indicate that the PyC/SiC multilayer coatings led to an optimum interfacial bonding between fibers and matrix and greatly improved the fracture toughness of the composites.

  4. Tunable Synthesis of SiC/SiO2 Heterojunctions via Temperature Modulation

    Directory of Open Access Journals (Sweden)

    Wei Li

    2018-05-01

    Full Text Available A large-scale production of necklace-like SiC/SiO2 heterojunctions was obtained by a molten salt-mediated chemical vapor reaction technique without a metallic catalyst or flowing gas. The effect of the firing temperature on the evolution of the phase composition, microstructure, and morphology of the SiC/SiO2 heterojunctions was studied. The necklace-like SiC/SiO2 nanochains, several centimeters in length, were composed of SiC/SiO2 core-shell chains and amorphous SiO2 beans. The morphologies of the as-prepared products could be tuned by adjusting the firing temperature. In fact, the diameter of the SiO2 beans decreased, whereas the diameter of the SiC fibers and the thickness of the SiO2 shell increased as the temperature increased. The growth mechanism of the necklace-like structure was controlled by the vapor-solid growth procedure and the modulation procedure via a molten salt-mediated chemical vapor reaction process.

  5. In situ observation of mechanical damage within a SiC-SiC ceramic matrix composite

    Energy Technology Data Exchange (ETDEWEB)

    Saucedo-Mora, L. [Institute Eduardo Torroja for Construction Sciences-CSIC, Madrid (Spain); Department of Materials, University of Oxford (United Kingdom); Lowe, T. [Manchester X-ray Imaging Facility, The University of Manchester (United Kingdom); Zhao, S. [Department of Materials, University of Oxford (United Kingdom); Lee, P.D. [Research Complex at Harwell, Rutherford Appleton Laboratory (United Kingdom); Mummery, P.M. [School of Mechanical, Aerospace and Civil Engineering, The University of Manchester (United Kingdom); Marrow, T.J., E-mail: james.marrow@materials.ox.ac.uk [Department of Materials, University of Oxford (United Kingdom)

    2016-12-01

    SiC-SiC ceramic matrix composites are candidate materials for fuel cladding in Generation IV nuclear fission reactors and as accident tolerant fuel clad in current generation plant. Experimental methods are needed that can detect and quantify the development of mechanical damage, to support modelling and qualification tests for these critical components. In situ observations of damage development have been obtained of tensile and C-ring mechanical test specimens of a braided nuclear grade SiC-SiC ceramic composite tube, using a combination of ex situ and in situ computed X-ray tomography observation and digital volume correlation analysis. The gradual development of damage by matrix cracking and also the influence of non-uniform loading are examined. - Highlights: • X-ray tomography with digital volume correlation measures 3D deformation in situ. • Cracking and damage in the microstructure can be detected using the strain field. • Fracture can initiate from the monolithic coating of a SiC-SiC ceramic composite.

  6. In situ observation of mechanical damage within a SiC-SiC ceramic matrix composite

    International Nuclear Information System (INIS)

    Saucedo-Mora, L.; Lowe, T.; Zhao, S.; Lee, P.D.; Mummery, P.M.; Marrow, T.J.

    2016-01-01

    SiC-SiC ceramic matrix composites are candidate materials for fuel cladding in Generation IV nuclear fission reactors and as accident tolerant fuel clad in current generation plant. Experimental methods are needed that can detect and quantify the development of mechanical damage, to support modelling and qualification tests for these critical components. In situ observations of damage development have been obtained of tensile and C-ring mechanical test specimens of a braided nuclear grade SiC-SiC ceramic composite tube, using a combination of ex situ and in situ computed X-ray tomography observation and digital volume correlation analysis. The gradual development of damage by matrix cracking and also the influence of non-uniform loading are examined. - Highlights: • X-ray tomography with digital volume correlation measures 3D deformation in situ. • Cracking and damage in the microstructure can be detected using the strain field. • Fracture can initiate from the monolithic coating of a SiC-SiC ceramic composite.

  7. Magnetohydrodynamic (MHD) considerations for liquid metal blanket and a SiC/SiC composite structure

    International Nuclear Information System (INIS)

    Scholz, R.; Greeff, J. de; Vinche, C.

    1998-01-01

    The electrical conductivity was measured on SiC/SiC composite specimens, in the as-received conditions and after neutron irradiation, for temperatures between 20 deg. C and 1000 deg. C. The tests were aimed at estimating the magnitude of MHD effects in liquid metal blankets and a SiC/SiC composites structure. The electrical conductivity of the unirradiated samples increased continuously with temperature and ranged from 330 (Ω m) -1 at 20 deg. C to 550 (Ω m) -1 at 1000 deg.C. The irradiation reduced only slightly the magnitude of σ indicating the materials tested cannot be treated as an electrical insulator in a MHD analysis for liquid metal blankets. (authors)

  8. Magnetohydrodynamic (MHD) considerations for liquid metal blanket and a SiC/SiC composite structure

    Energy Technology Data Exchange (ETDEWEB)

    Scholz, R.; Greeff, J. de; Vinche, C. [Commission Europeenne Community, JRC, Vatican City State, Holy See (Italy)

    1998-07-01

    The electrical conductivity was measured on SiC/SiC composite specimens, in the as-received conditions and after neutron irradiation, for temperatures between 20 deg. C and 1000 deg. C. The tests were aimed at estimating the magnitude of MHD effects in liquid metal blankets and a SiC/SiC composites structure. The electrical conductivity of the unirradiated samples increased continuously with temperature and ranged from 330 ({omega} m){sup -1} at 20 deg. C to 550 ({omega} m){sup -1} at 1000 deg.C. The irradiation reduced only slightly the magnitude of {sigma} indicating the materials tested cannot be treated as an electrical insulator in a MHD analysis for liquid metal blankets. (authors)

  9. SiC/SiC composites by preceramic polymer infiltration and pyrolysis

    International Nuclear Information System (INIS)

    Schiroky, G.H.

    1997-01-01

    Lanxide Corporation has been developing fiber-reinforced silicon carbide matrix composites using the technique of preceramic polymer infiltration and pyrolysis, commonly referred to as the PIP-process. In this method, liquid CERASET TM preceramic polymer is being infiltrated into lay-ups of ceramic fibers, thermoset, and pyrolized at elevated temperatures for conversion into a SiC matrix. Several cycles of reinfiltration and pyrolysis must be performed to build up the SiC matrix because of the increase in density during pyrolysis from 1.0 g/cm 3 for the liquid polymer to between 2.2 and 3.2 g/cm 3 for the ceramic matrix. Composites have been fabricated using three different approaches: first, polymer infiltration of free-standing fiber preforms in which the fiber plies are being held together with a C/SiC duplex coating applied by chemical vapor infiltration; second, infiltration of individually coated fiber plies contained in a mold using the resin transfer molding method; and third, infiltration of vacuum-bagged, individually coated fiber plies using the vacuum assisted resin infiltration technique. Very good mechanical properties of Nicalon TM /SiC and Hi-Nicalon TM /SiC composites have been obtained, with four-point flexural strengths exceeding 400 MPa and toughnesses in the 20 to 30 MPa·m 1/2 range. The thermal conductivity of the fabricated composites is low (below 5 W/m·K) and must be improved substantially to meet the requirements for fusion structural applications. The fabricated components are relatively dense and impermeable to nitrogen, however, are readily permeated by helium. Chemical analysis has indicated the presence of a small amount of nitrogen (ca. 1 wt%) in the SiC material after pyrolysis of the CERASET preceramic polymer at 1600degC. (author)

  10. SiC/SiC composites by preceramic polymer infiltration and pyrolysis

    Energy Technology Data Exchange (ETDEWEB)

    Schiroky, G.H. [Lanxide Corporation, Newark, DE (United States)

    1997-12-31

    Lanxide Corporation has been developing fiber-reinforced silicon carbide matrix composites using the technique of preceramic polymer infiltration and pyrolysis, commonly referred to as the PIP-process. In this method, liquid CERASET{sup TM} preceramic polymer is being infiltrated into lay-ups of ceramic fibers, thermoset, and pyrolized at elevated temperatures for conversion into a SiC matrix. Several cycles of reinfiltration and pyrolysis must be performed to build up the SiC matrix because of the increase in density during pyrolysis from 1.0 g/cm{sup 3} for the liquid polymer to between 2.2 and 3.2 g/cm{sup 3} for the ceramic matrix. Composites have been fabricated using three different approaches: first, polymer infiltration of free-standing fiber preforms in which the fiber plies are being held together with a C/SiC duplex coating applied by chemical vapor infiltration; second, infiltration of individually coated fiber plies contained in a mold using the resin transfer molding method; and third, infiltration of vacuum-bagged, individually coated fiber plies using the vacuum assisted resin infiltration technique. Very good mechanical properties of Nicalon{sup TM}/SiC and Hi-Nicalon{sup TM}/SiC composites have been obtained, with four-point flexural strengths exceeding 400 MPa and toughnesses in the 20 to 30 MPa{center_dot}m{sup 1/2} range. The thermal conductivity of the fabricated composites is low (below 5 W/m{center_dot}K) and must be improved substantially to meet the requirements for fusion structural applications. The fabricated components are relatively dense and impermeable to nitrogen, however, are readily permeated by helium. Chemical analysis has indicated the presence of a small amount of nitrogen (ca. 1 wt%) in the SiC material after pyrolysis of the CERASET preceramic polymer at 1600degC. (author)

  11. Microwave joining of SiC ceramics and composites

    Energy Technology Data Exchange (ETDEWEB)

    Ahmad, I.; Silberglitt, R.; Tian, Y.L. [FM Technologies, Inc., Fairfax, VA (United States); Katz, J.D. [Los Alamos National Lab., NM (United States)

    1997-04-01

    Potential applications of SiC include components for advanced turbine engines, tube assemblies for radiant burners and petrochemical processing and heat exchangers for high efficiency electric power generation systems. Reliable methods for joining SiC are required in order to cost-effectively fabricate components for these applications from commercially available shapes and sizes. This manuscript reports the results of microwave joining experiments performed using two different types of SiC materials. The first were on reaction bonded SiC, and produced joints with fracture toughness equal to or greater than that of the base material over an extended range of joining temperatures. The second were on continuous fiber-reinforced SiC/SiC composite materials, which were successfully joined with a commercial active brazing alloy, as well as by using a polymer precursor.

  12. A facile synthesis of Li_2Fe_1_/_3Mn_1_/_3Ni_1_/_3SiO_4/C composites as cathode materials for lithium-ion batteries

    International Nuclear Information System (INIS)

    Yang, Rong; Wang, Liqing; Deng, Kunfa; Lv, Mengni; Xu, Yunhua

    2016-01-01

    The novel Li_2Fe_1_/_3Mn_1_/_3Ni_1_/_3SiO_4/C has been successfully synthesized by a feasible solution process in ternary system. The spherical carbon-coated composites are obtained using a heat treatment in the presence of sucrose. X-ray diffraction (XRD) diffractogram displays that the Li_2Fe_1_/_3Mn_1_/_3Ni_1_/_3SiO_4/C crystallized in an orthorhombic structure with a space group of Pmn21. The energy-dispersive X-ray spectroscopy mappings indicate that Fe, Mn and Ni elements are distributed homogenously in Li_2Fe_1_/_3Mn_1_/_3Ni_1_/_3SiO_4/C nano-spherical particle with size less than 50 nm. The lithium storage capacity and cycling performance of the Li_2Fe_1_/_3Mn_1_/_3Ni_1_/_3SiO_4/C presents good results when tested as cathode materials in lithium cells at room temperature. It delivers an initial discharge capacity of 181.4 mAh g"−"1 and a discharge capacity of 172.9 mAh g"−"1 after 20 cycles at 0.1C in the voltage range of 1.5–4.6V. Furthermore, it also exhibits an excellent rate capability with a capacity under different current densities of about 144.0 mAh g"−"1 (0.2 C), 117.9 mAh g"−"1 (0.5 C), 106.1 mAh g"−"1 (1 C), respectively and a good capacity cycling maintenance of 153.7 mAh g"−"1 after 60 cycles. Above results indicate that the spherical Li_2Fe_1_/_3Mn_1_/_3Ni_1_/_3SiO_4/C becomes a very promising candidate for cathode material in lithium-ion batteries. - Highlights: • Li_2Fe_1_/_3Mn_1_/_3Ni_1_/_3SiO_4/C was obtained by solution process in a ternary system. • The material was pure phase ternary solid solution with tetrahedral morphology. • The spherical particle size was less than 50 nm with graphitized carbon coating. • The nanocomposite revealed high discharge capacity and excellent rate capability.

  13. Investigation on Mechanical and Fatigue behaviour of Aluminium Based SiC/ZrO2 Particle Reinforced MMC

    Science.gov (United States)

    Ramesh, S.; Govindaraju, N.; Suryanarayan, C. P.

    2018-04-01

    The study is the work on Aluminium Metal Matrix Composites (MMC’s), which have wider applications in automobile, aerospace and defense industries, hi-tech engineering and power transmission due to their lightweight, high strength and other unique properties. The Aluminium Matrix Composites (AMC’s) refer to a kind of light weight high performance Aluminium centric material system. AMC’s consist of a non-metallic reinforcement which when included into aluminium matrix offers an advantage over the base material. Reinforcements like SiC, B4C, Al2O3, TiC, TiB2, TiO2 are normally preferred to improve mechanical properties of such composites. Here Aluminium 6061 is preferred as matrix material, while silicon carbide (SiC) and Zirconium di-oxide (ZrO2) is selected as reinforcement compounds. Conventional Stir casting procedure is employed to fabricate the necessary composites compositions, which are I. Al:SiC::100:5 and II. Al:ZrO2:SiC::100:3:2. Experimental results depict that the composition II provides higher hardness of 53.6 RHN as opposed to 45.8 RHN of composition I. In tensile strength composition II demonstrates 96.43 N/mm2 as opposed to 67.229 N/mm2 tensile strength of composition II. The fatigue test indicate a expected number of life cycles to failure of 105 cycles for composition II and over 104 cycles for composition I, at stress ranges of 79.062 MPa and 150.651 MPa respectively.

  14. Evaluation of a Melt Infiltrated SiC/SiC Ceramic Matrix Composite

    Science.gov (United States)

    2017-12-20

    temperature performance of a state- of-the-art CMC provides evidence that this new class of materials can, or perhaps cannot, meet the harsh...and elevated temperature . This report describes tensile, creep, and fatigue testing procedures and presents the results. 15. SUBJECT TERMS ceramic...matrix composites, creep, dwell fatigue, fatigue, high temperature , melt infiltrated, SiC/SiC 16. SECURITY CLASSIFICATION OF: 17. LIMITATION OF

  15. Effects of SiC amount on phase compositions and properties of Ti3SiC2-based composites

    Institute of Scientific and Technical Information of China (English)

    蔡艳芝; 殷小玮; 尹洪峰

    2015-01-01

    The phase compositions and properties of Ti3SiC2-based composites with SiC addition of 5%−30% in mass fraction fabricated by in-situ reaction and hot pressing sintering were studied. SiC addition effectively prevented TiC synthesis but facilitated SiC synthesis. The Ti3SiC2/TiC−SiC composite had better oxidation resistance when SiC added quantity reached 20% but poorer oxidation resistance with SiC addition under 15%than Ti3SiC2/TiC composite at higher temperatures. There were more than half of the original SiC and a few Ti3SiC2 remaining in Ti3SiC2/TiC−SiC with 20% SiC addition, but all constituents in Ti3Si2/TiC composite were oxidized after 12 h in air at 1500 °C. The oxidation scale thickness of TS30, 1505.78μm, was near a half of that of T, 2715μm, at 1500 °C for 20 h. Ti3SiC2/TiC composite had a flexural strength of 474 MPa, which was surpassed by Ti3SiC2/TiC−SiC composites when SiC added amount reached 15%. The strength reached the peak of 518 MPa at 20%SiC added amount.

  16. SiC-Based Composite Materials Obtained by Siliconizing Carbon Matrices

    Science.gov (United States)

    Shikunov, S. L.; Kurlov, V. N.

    2017-12-01

    We have developed a method for fabrication of parts of complicated configuration from composite materials based on SiC ceramics, which employs the interaction of silicon melt with the carbon matrix having a certain composition and porosity. For elevating the operating temperatures of ceramic components, we have developed a method for depositing protective silicon-carbide coatings that is based on the interaction of the silicon melt and vapor with carbon obtained during thermal splitting of hydrocarbon molecules. The new structural ceramics are characterized by higher operating temperatures; chemical stability; mechanical strength; thermal shock, wear and radiation resistance; and parameters stability.

  17. Joining of SiC ceramics and SiC/SiC composites

    Energy Technology Data Exchange (ETDEWEB)

    Rabin, B.H. [Idaho National Engineering Lab., Idaho Falls, ID (United States)

    1996-08-01

    This project has successfully developed a practical and reliable method for fabricating SiC ceramic-ceramic joints. This joining method will permit the use of SiC-based ceramics in a variety of elevated temperature fossil energy applications. The technique is based on a reaction bonding approach that provides joint interlayers compatible with SiC, and excellent joint mechanical properties at temperatures exceeding 1000{degrees}C. Recent emphasis has been given to technology transfer activities, and several collaborative research efforts are in progress. Investigations are focusing on applying the joining method to sintered {alpha}-SiC and fiber-reinforced SiC/SiC composites for use in applications such as heat exchangers, radiant burners and gas turbine components.

  18. 3Y-TZP/Si2N2O composite obtained by pressureless sintering

    International Nuclear Information System (INIS)

    Santos, Carlos Augusto Xavier

    2006-01-01

    Zirconia 3YTZP presents excellent properties at room temperature. These properties decrease as the temperature increases because high temperature acts negatively over the stress induced transformation toughening in the matrix. The addition of Si 3 N 4 and SiC in a Y-TZP matrix is very interesting because leads to formation of silicon oxynitride and it increases the mechanical properties like toughness and hardness. Certainly the mechanical properties increment is limited by several difficulties which have appeared during processing and heating of these materials. This paper studies the Y-TZP/Si 2 N 2 0 pressureless sintered composite, under different temperatures, showing the behavior of 20 vol %Si 3 N 4 -SiC when added in YTZP matrix and heated under no pressure system. Al 2 O 3 and Y 2 O 3 were used as sintering aids. The mixture was milled and molded by cold isostatic pressure. Samples were heated at 1500 deg, 1600 deg and 17000 deg C x 2h without pressure under atmospheric conditions using Si 3 N 4 bed-powder. Samples were characterized by XRD and density, hardness, toughness, bending strength were measured. The structure of the material was observed in SEMITEM/EPMA to verify the distribution and composition of the materials in the composite and the contact between filler surface and the matrix. The formation of SiON 2 was observed in the sintered material due to reaction between both nitride and carbide with Y - TZP matrix. Furthermore the material showed an increment of both hardness and toughness as temperature increases. The samples presented considerable resistance to oxidation below 1000 deg C. (author)

  19. Chemical compatibility issues associated with use of SiC/SiC in advanced reactor concepts

    Energy Technology Data Exchange (ETDEWEB)

    Wilson, Dane F. [Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States)

    2015-09-01

    Silicon carbide/silicon carbide (SiC/SiC) composites are of interest for components that will experience high radiation fields in the High Temperature Gas Cooled Reactor (HTGR), the Very High Temperature Reactor (VHTR), the Sodium Fast Reactor (SFR), or the Fluoride-cooled High-temperature Reactor (FHR). In all of the reactor systems considered, reactions of SiC/SiC composites with the constituents of the coolant determine suitability of materials of construction. The material of interest is nuclear grade SiC/SiC composites, which consist of a SiC matrix [high-purity, chemical vapor deposition (CVD) SiC or liquid phase-sintered SiC that is crystalline beta-phase SiC containing small amounts of alumina-yttria impurity], a pyrolytic carbon interphase, and somewhat impure yet crystalline beta-phase SiC fibers. The interphase and fiber components may or may not be exposed, at least initially, to the reactor coolant. The chemical compatibility of SiC/SiC composites in the three reactor environments is highly dependent on thermodynamic stability with the pure coolant, and on reactions with impurities present in the environment including any ingress of oxygen and moisture. In general, there is a dearth of information on the performance of SiC in these environments. While there is little to no excess Si present in the new SiC/SiC composites, the reaction of Si with O2 cannot be ignored, especially for the FHR, in which environment the product, SiO2, can be readily removed by the fluoride salt. In all systems, reaction of the carbon interphase layer with oxygen is possible especially under abnormal conditions such as loss of coolant (resulting in increased temperature), and air and/ or steam ingress. A global outline of an approach to resolving SiC/SiC chemical compatibility concerns with the environments of the three reactors is presented along with ideas to quickly determine the baseline compatibility performance of SiC/SiC.

  20. Oxidation of BN-coated SiC fibers in ceramic matrix composites

    International Nuclear Information System (INIS)

    Sheldon, B.W.; Sun, E.Y.

    1996-01-01

    Thermodynamic calculations were performed to analyze the simultaneous oxidation of BN and SiC. The results show that, with limited amounts of oxygen present, the formation of SiO 2 should occur prior to the formation of B 2 O 3 . This agrees with experimental observations of oxidation in glass-ceramic matrix composites with BN-coated SiC fibers, where a solid SiO 2 reaction product containing little or no boron has been observed. The thermodynamic calculations suggest that this will occur when the amount of oxygen available is restricted. One possible explanation for this behavior is that SiO 2 formation near the external surfaces of the composite closes off cracks or pores, such that vapor phase O 2 diffusion into the composite occurs only for a limited time. This indicates that BN-coated SiC fibers will not always oxidize to form significant amounts of a low-melting, borosilicate glass

  1. SiC/C composite sheets produced from polycarbosilane/resin/bonder mixtures. Polycarbosilane/jushi/bonder kongokei kara sakuseishita SiC/C fukugo sheet

    Energy Technology Data Exchange (ETDEWEB)

    Kawamura, K. (The National Defense Academy, Kanagawa (Japan)); Koga, J.; Iwata, T.; Yamanaka, S.; Ono, M. (Mitsubishi Materials Corp., Saitama (Japan))

    1992-02-01

    In a course of work to improve anti-oxidative property and strength of sheets of carbonic composite materials with resins, and further to produce those sheets in an industrial scale, it was tried to prepare two types of 0.4 {approximately} 0.6 m thickness SiC / C composite sheets by heat treatment of two green sheets polycarbosilane ( PCS ) / fran resin / binder type and PCS / (phenol-formaldehyde resin / binder type ) at temperature of 1200 {approximately} 1400{degree}C in an atmosphere of nitrogen. The sheets thus made were subjected to SEM observation, X-ray diffraction, measurement of density and electric resistance, and to tests on weight loss by heating and on bending. The texture of them were as tight as that of their resin carbon ( glassy carbon ). The structural feature is formation of amorphous SiO{sub 2} as a secondary product, This indicates that Si in PCS reacts with oxygen in resin during pyrolysis. The bending strength and anti-oxidative property depend on the SiC content from PCS and that the mixing effect of SiC on them are feasible when a mixing ratio of PCS / resin is higher than (2/1). 13 ref., 7 figs., 2 tabs.

  2. Pd/CeO2/SiC Chemical Sensors

    Science.gov (United States)

    Lu, Weijie; Collins, W. Eugene

    2005-01-01

    The incorporation of nanostructured interfacial layers of CeO2 has been proposed to enhance the performances of Pd/SiC Schottky diodes used to sense hydrogen and hydrocarbons at high temperatures. If successful, this development could prove beneficial in numerous applications in which there are requirements to sense hydrogen and hydrocarbons at high temperatures: examples include monitoring of exhaust gases from engines and detecting fires. Sensitivity and thermal stability are major considerations affecting the development of high-temperature chemical sensors. In the case of a metal/SiC Schottky diode for a number of metals, the SiC becomes more chemically active in the presence of the thin metal film on the SiC surface at high temperature. This increase in chemical reactivity causes changes in chemical composition and structure of the metal/SiC interface. The practical effect of the changes is to alter the electronic and other properties of the device in such a manner as to degrade its performance as a chemical sensor. To delay or prevent these changes, it is necessary to limit operation to a temperature sensor structures. The present proposal to incorporate interfacial CeO2 films is based partly on the observation that nanostructured materials in general have potentially useful electrical properties, including an ability to enhance the transfer of electrons. In particular, nanostructured CeO2, that is CeO2 with nanosized grains, has shown promise for incorporation into hightemperature electronic devices. Nanostructured CeO2 films can be formed on SiC and have been shown to exhibit high thermal stability on SiC, characterized by the ability to withstand temperatures somewhat greater than 700 C for limited times. The exchanges of oxygen between CeO2 and SiC prevent the formation of carbon and other chemical species that are unfavorable for operation of a SiC-based Schottky diode as a chemical sensor. Consequently, it is anticipated that in a Pd/CeO2/SiC Schottky

  3. Self-sealing multilayer coating for SiC/SiC composites

    International Nuclear Information System (INIS)

    Ferraris, M.; Appendino Montorsi, M.; Salvo, M.; Isola, C.; Kohyama, A.

    1997-01-01

    A double layer coating for SiC/SiC for fusion applications is proposed: the first layer consists in a homogeneous, crack free, glass-ceramic with high characteristic temperatures and thermal expansion coefficient compatible to the composite one; the second layer is amorphous and shows self-sealing properties above 700degC. The glass and the glass-ceramic materials used for this double layer coating do not contain lithium and boron oxide, making them particularly interesting for thermonuclear fusion applications. The self-sealing property of the double layer coating was valued by inducing cracks on the coatings and observing their reparation after heating. (author)

  4. Molecular dynamics simulation of damage cascade creation in SiC composites containing SiC/graphite interface

    Energy Technology Data Exchange (ETDEWEB)

    Wallace, Joseph; Chen, Di; Wang, Jing; Shao, Lin, E-mail: lshao@tamu.edu

    2013-07-15

    Silicon carbide composites have been investigated for their use as structural materials for advanced nuclear reactor designs. Although the composites have significantly enhanced mechanical properties and structure integrity, there is little known about the behavior of defects in the presence of a graphite-silicon carbide interface. In this study, molecular dynamics simulations have been used to model defect creation and clustering in a composite containing a SiC/graphite interface. Evolution of displacements as a function of time were studied and compared to bulk SiC. The results show that the first a few SiC atomic layers closest to the interface are easily damaged. However, beyond these first few atomic layers the system appears to be unaffected by the SiC interface.

  5. Fracture Characteristics of C/SiC Composites for Rocket Nozzle at Elevated Temperature

    Energy Technology Data Exchange (ETDEWEB)

    Yoon, Dong Hyun; Lee, Jeong Won; Kim, Jae Hoon [Chungnam Nat’l Univ., Daejeon (Korea, Republic of); Sihn, Ihn Cheol; Lim, Byung Joo [Dai-Yang Industries Co., Daejeon (Korea, Republic of)

    2016-11-15

    In a solid propulsion system, the rocket nozzle is exposed to high temperature combustion gas. Hence, choosing an appropriate material that could demonstrate adequate performance at high temperature is important. As advanced materials, carbon/silicon carbide composites (C/SiC) have been studied with the aim of using them for the rocket nozzle throat. However, when compared with typical structural materials, C/SiC composites are relatively weak in terms of both strength and toughness, owing to their quasi-brittle behavior and oxidation at high temperatures. Therefore, it is important to evaluate the thermal and mechanical properties of this material before using it in this application. This study presents an experimental method to investigate the fracture behavior of C/SiC composite material manufactured using liquid silicon infiltration (LSI) method at elevated temperatures. In particular, the effects of major parameters, such as temperature, loading, oxidation conditions, and fiber direction on strength and fracture characteristics were investigated. Fractography analysis of the fractured specimens was performed using an SEM.

  6. Microstructure and fracture in SiC whisker reinforced 2124 aluminum composite

    Science.gov (United States)

    Nieh, T. G.; Raninen, R. A.; Chellman, D. J.

    1985-01-01

    The microstructures of extruded and hot-rolled 2124 Al-15 percent (by weight) SiC whisker composites have been investigated, experimentally. Among the specific factors studied were: the strength of the whisker-matrix interfaces; (2) the presence of oxides; (3) the presence of defective whiskers; (4) and the presence of distribution of intermetallic compounds, impurities in the SiC(w) powder, and microstructural inhomogeneities. Modifications in the microstructure of the SiC/AL composites due to hot rolling and extrusion are illustrated in a series of microphotographs. It was found that hot rolling along the axis of extrusion was associated with some types of whisker damage, while the whiskers still retain their original orientation. Hot-rolling perpendicular to the axis of extrusion, however, tended to rotate the whiskers and produced a nearly isotropic material. Whisker free zones were virtually eliminated or reduced in size by hot rolling. In situ Auger fractography of the composite showed that the interfacial bonding between the SiC and the Al matrix was good and that Al2O2 had no significant influence on the fracture mechanics of the composite.

  7. Chemically activated graphene/porous Si@SiO{sub x} composite as anode for lithium ion batteries

    Energy Technology Data Exchange (ETDEWEB)

    Tao, Hua-Chao [College of Materials and Chemical Engineering, China Three Gorges University, 8 Daxue Road, Yichang, Hubei 443002 (China); Collaborative Innovation Center for Microgrid of New Energy, Hubei Province (China); Yang, Xue-Lin, E-mail: xlyang@ctgu.edu.cn [College of Materials and Chemical Engineering, China Three Gorges University, 8 Daxue Road, Yichang, Hubei 443002 (China); Collaborative Innovation Center for Microgrid of New Energy, Hubei Province (China); Zhang, Lu-Lu; Ni, Shi-Bing [College of Materials and Chemical Engineering, China Three Gorges University, 8 Daxue Road, Yichang, Hubei 443002 (China); Collaborative Innovation Center for Microgrid of New Energy, Hubei Province (China)

    2014-10-15

    Chemically activated graphene/porous Si@SiO{sub x} (CAG/Si@SiO{sub x}) composite has been synthesized via magnesiothemic reduction of mesoporous SiO{sub 2} (MCM-48) to porous Si@SiO{sub x} and dispersing in the suspension of chemically activated graphene oxide (CAGO) followed by thermal reduction. The porous Si@SiO{sub x} particles are well encapsulated in chemically activated graphene (CAG) matrix. The resulting CAG/Si@SiO{sub x} composite exhibits a high reversible capacity and excellent cycling stability up to 763 mAh g{sup −1} at a current density of 100 mA g{sup −1} after 50 cycles. The porous structure of CAG layer and Si@SiO{sub x} is beneficial to accommodate volume expansion of Si during discharge and charge process and the interconnected CAG improves the electronic conductivity of composite. - Highlights: • Chemically activated graphene encapsulated porous Si composite was prepared. • The graphene offers a continuous electrically conductive network. • The porous structure can accommodate volume expansion of Si-based materials. • The composite exhibits excellent lithium storage performance.

  8. Creep/Stress Rupture Behavior and Failure Mechanisms of Full CVI and Full PIP SiC/SiC Composites at Elevated Temperatures in Air

    Science.gov (United States)

    Bhatt, R. T.; Kiser, J. D.

    2017-01-01

    SiC/SiC composites fabricated by melt infiltration are being considered as potential candidate materials for next generation turbine components. However these materials are limited to 2400 F application because of the presence of residual silicon in the SiC matrix. Currently there is an increasing interest in developing and using silicon free SiC/SiC composites for structural aerospace applications above 2400 F. Full PIP or full CVI or CVI + PIP hybrid SiC/SiC composites can be fabricated without excess silicon, but the upper temperature stress capabilities of these materials are not fully known. In this study, the on-axis creep and rupture properties of the state-of-the-art full CVI and full PIP SiC/SiC composites with Sylramic-iBN fibers were measured at temperatures to 2700 F in air and their failure modes examined. In this presentation creep rupture properties, failure mechanisms and upper temperature capabilities of these two systems will be discussed and compared with the literature data.

  9. Effects of dual-ion irradiation on the swelling of SiC/SiC composites

    International Nuclear Information System (INIS)

    Kishimoto, Hirotatsu; Kohyama, Akira; Ozawa, Kazumi; Kondo, Sosuke

    2005-01-01

    Silicon carbide (SiC) matrix composites reinforced by SiC fibers is a candidate structural material of fusion gas-cooled blanket system. From the viewpoint of material designs, it is important to investigate the swelling by irradiation, which results from the accumulation of displacement damages. In the fusion environment, (n, α) nuclear reactions are considered to produce helium gas in SiC. For the microstructural evolution, a dual-ion irradiation method is able to simulate the effects of helium. In the present research, 1.7 MeV tandem and 1 MeV single-end accelerators were used for Si self-ion irradiation and helium implantation, respectively. The average helium over displacement per atom (dpa) ratio in SiC was adjusted to 60 appm/dpa. The irradiation temperature ranged from room temperature to 1400degC. The irradiation-induced swelling was measured by the step height method. Helium that was implanted simultaneously with displacement damages in dual-ion irradiated SiC increased the swelling that was larger than that by single-ion irradiated SiC below 800degC. Since this increase was not observed above 1000degC, the interaction of helium and displacement damages was considered to change above 800degC. In this paper, the microstructural behavior and dimensional stability of SiC materials under the fusion relevant environment are discussed. (author)

  10. Abrasive Wear of AlSi12-Al2O3 Composite Materials Manufactured by Pressure Infiltration

    Directory of Open Access Journals (Sweden)

    Kremzer M.

    2016-09-01

    Full Text Available The aim of this study is to investigate tribological properties of EN AC-AlSi12 alloy composite materials matrix manufactured by pressure infiltration of Al2O3 porous preforms. In the paper, a technique of manufacturing composite materials was described in detail as well as wear resistance made on pin on disc was tested. Metallographic observations of wear traces of tested materials using stereoscopic and confocal microscopy were made. Studies allow concluding that obtained composite materials have much better wear resistance than the matrix alloy AlSi12. It was further proved that the developed technology of their preparation consisting of pressure infiltration of porous ceramic preforms can find a practical application.

  11. High-temperature protective coatings for C/SiC composites

    OpenAIRE

    Xiang Yang; Chen Zhao-hui; Cao Feng

    2014-01-01

    Carbon fiber-reinforced silicon carbide (C/SiC) composites were well-established light weight materials combining high specific strength and damage tolerance. For high-temperature applications, protective coatings had to provide oxidation and corrosion resistance. The literature data introduced various technologies and materials, which were suitable for the application of coatings. Coating procedures and conditions, materials design limitations related to the reactivity of the components of C...

  12. Solvothermal synthesis and electrochemical performance of Li2MnSiO4/C cathode materials for lithium ion batteries

    International Nuclear Information System (INIS)

    Wang, Yan-Chao; Zhao, Shi-Xi; Zhai, Peng-Yuan; Li, Fang; Nan, Ce-Wen

    2014-01-01

    Highlights: • Li 2 MnSiO 4 /C nanocomposite has been synthesized by the solvothermal method. • The particles of Li 2 MnSiO 4 /C are much smaller and more uniform. • The presence of Ni improves discharge capacity of Li 2 MnSiO 4 /C cathode material. • The initial discharge capacity of Ni-modified Li 2 MnSiO 4 /C is 274.5 mAh g −1 at 25 °C. - Abstract: Orthorhombic structure Li 2 MnSiO 4 /C with Pmn2 1 space group is synthesized by the solvothermal method. Carbon coating and Ni 2+ doping are used to improve the electronic conductivity and the cycling performance of Li 2 MnSiO 4 cathode material, respectively. The particles of Li 2 MnSiO 4 /C are much smaller and more uniform than those of Li 2 MnSiO 4 due to the carbon coating. It is shown that Ni 2+ has been reduced into metal Ni during the synthesis process. The synthesized Ni-modified Li 2 MnSiO 4 /C (denoted as (LMS@Ni)/C) cathode material exhibits better electrochemical performance in comparison with Li 2 MnSiO 4 /C, attributing to higher lithium ion diffusion coefficient as well as electronic conductivity. The initial discharge capacity of (LMS@Ni)/C is 274.5 mA h g −1 and the reversible capacity after 20 cycles is 119.8 mA h g −1 at 25 °C

  13. Electrochemical characteristics of nc-Si/SiC composite for anode electrode of lithium ion batteries

    International Nuclear Information System (INIS)

    Jeon, Bup Ju; Lee, Joong Kee

    2014-01-01

    Graphical abstract: Cycling performances and coulombic efficiencies of the nc-Si/SiC composite anodes at different CH 4 /SiH 4 mole ratios. -- Highlights: • Our work has focused on irreversible discharge capacity and capacity retention of nc-Si/SiC composite particles. • Particles comprised a mixed construction of nc-Si/SiC structure with dual phases. • The SiC phase acted as retarding media, leading to enhanced cycle stability. -- Abstract: nc-Si/SiC composite particles were prepared as an anode material for lithium ion batteries using a plasma jet with DC arc discharge. The composition of the nc-Si/SiC composite particles was controlled by setting the mole ratio of CH 4 and SiH 4 precursor gases. X-ray diffraction, TEM images, and Raman shift analyses revealed that the synthesized nc-Si/SiC composite particles comprised a construction of nano-nocaled structure with crystalline phases of active silicon, highly disordered amorphous carbon of graphite and crystalline phases of β-SiC. In the experimental range examined, the nc-Si/SiC composite particles showed good coulombic efficiency in comparison with particles high Si–Si bonding content due to the interplay of particles with a small proportion of carbon and the buffering effect against volume expansion by structural stabilization, and played a role as retarding media for the rapid electrochemical reactions of the SiC crystal against lithium

  14. Electrochemical characteristics of nc-Si/SiC composite for anode electrode of lithium ion batteries

    Energy Technology Data Exchange (ETDEWEB)

    Jeon, Bup Ju [Department of Energy Resources, Shinhan University, 233-1, Sangpae-dong, Dongducheon, Gyeonggi-do, 483-777 (Korea, Republic of); Lee, Joong Kee, E-mail: leejk@kist.re.kr [Advanced Energy Materials Processing Laboratory, Center for Energy Convergence Research, Green City Technology Institute, Korea Institute of Science and Technology, Hwarangno 14-gil 5, Seongbuk-gu, Seoul 136-791 (Korea, Republic of)

    2014-03-25

    Graphical abstract: Cycling performances and coulombic efficiencies of the nc-Si/SiC composite anodes at different CH{sub 4}/SiH{sub 4} mole ratios. -- Highlights: • Our work has focused on irreversible discharge capacity and capacity retention of nc-Si/SiC composite particles. • Particles comprised a mixed construction of nc-Si/SiC structure with dual phases. • The SiC phase acted as retarding media, leading to enhanced cycle stability. -- Abstract: nc-Si/SiC composite particles were prepared as an anode material for lithium ion batteries using a plasma jet with DC arc discharge. The composition of the nc-Si/SiC composite particles was controlled by setting the mole ratio of CH{sub 4} and SiH{sub 4} precursor gases. X-ray diffraction, TEM images, and Raman shift analyses revealed that the synthesized nc-Si/SiC composite particles comprised a construction of nano-nocaled structure with crystalline phases of active silicon, highly disordered amorphous carbon of graphite and crystalline phases of β-SiC. In the experimental range examined, the nc-Si/SiC composite particles showed good coulombic efficiency in comparison with particles high Si–Si bonding content due to the interplay of particles with a small proportion of carbon and the buffering effect against volume expansion by structural stabilization, and played a role as retarding media for the rapid electrochemical reactions of the SiC crystal against lithium.

  15. Designing the fiber volume ratio in SiC fiber-reinforced SiC ceramic composites under Hertzian stress

    International Nuclear Information System (INIS)

    Lee, Kee Sung; Jang, Kyung Soon; Park, Jae Hong; Kim, Tae Woo; Han, In Sub; Woo, Sang Kuk

    2011-01-01

    Highlights: → Optimum fiber volume ratios in the SiC/SiC composite layers were designed under Hertzian stress. → FEM analysis and spherical indentation experiments were undertaken. → Boron nitride-pyrocarbon double coatings on the SiC fiber were effective. → Fiber volume ratio should be designed against flexural stress. -- Abstract: Finite element method (FEM) analysis and experimental studies are undertaken on the design of the fiber volume ratio in silicon carbide (SiC) fiber-reinforced SiC composites under indentation contact stresses. Boron nitride (BN)/Pyrocarbon (PyC) are selected as the coating materials for the SiC fiber. Various SiC matrix/coating/fiber/coating/matrix structures are modeled by introducing a woven fiber layer in the SiC matrix. Especially, this study attempts to find the optimum fiber volume ratio in SiC fiber-reinforced SiC ceramics under Hertzian stress. The analysis is performed by changing the fiber type, fiber volume ratio, coating material, number of coating layers, and stacking sequence of the coating layers. The variation in the stress for composites in relation to the fiber volume ratio in the contact axial or radial direction is also analyzed. The same structures are fabricated experimentally by a hot process, and the mechanical behaviors regarding the load-displacement are evaluated using the Hertzian indentation method. Various SiC matrix/coating/fiber/coating/matrix structures are fabricated, and mechanical characterization is performed by changing the coating layer, according to the introduction (or omission) of the coating layer, and the number of woven fiber mats. The results show that the damage mode changes from Hertzian stress to flexural stress as the fiber volume ratio increases in composites because of the decreased matrix volume fraction, which intensifies the radial crack damage. The result significantly indicates that the optimum fiber volume ratio in SiC fiber-reinforced SiC ceramics should be designed for

  16. Facile Synthesis of SiO2@C Nanoparticles Anchored on MWNT as High-Performance Anode Materials for Li-ion Batteries

    Science.gov (United States)

    Zhao, Yan; Liu, Zhengjun; Zhang, Yongguang; Mentbayeva, Almagul; Wang, Xin; Maximov, M. Yu.; Liu, Baoxi; Bakenov, Zhumabay; Yin, Fuxing

    2017-07-01

    Carbon-coated silica nanoparticles anchored on multi-walled carbon nanotubes (SiO2@C/MWNT composite) were synthesized via a simple and facile sol-gel method followed by heat treatment. Scanning and transmission electron microscopy (SEM and TEM) studies confirmed densely anchoring the carbon-coated SiO2 nanoparticles onto a flexible MWNT conductive network, which facilitated fast electron and lithium-ion transport and improved structural stability of the composite. As prepared, ternary composite anode showed superior cyclability and rate capability compared to a carbon-coated silica counterpart without MWNT (SiO2@C). The SiO2@C/MWNT composite exhibited a high reversible discharge capacity of 744 mAh g-1 at the second discharge cycle conducted at a current density of 100 mA g-1 as well as an excellent rate capability, delivering a capacity of 475 mAh g-1 even at 1000 mA g-1. This enhanced electrochemical performance of SiO2@C/MWNT ternary composite anode was associated with its unique core-shell and networking structure and a strong mutual synergistic effect among the individual components.

  17. Improved C/SiC Ceramic Composites Made Using PIP

    Science.gov (United States)

    Easler, Timothy

    2007-01-01

    Improved carbon-fiber-reinforced SiC ceramic-matrix composite (C/SiC CMC) materials, suitable for fabrication of thick-section structural components, are producible by use of a combination of raw materials and processing conditions different from such combinations used in the prior art. In comparison with prior C/SiC CMC materials, these materials have more nearly uniform density, less porosity, and greater strength. The majority of raw-material/processing-condition combinations used in the prior art involve the use of chemical vapor infiltration (CVI) for densifying the matrix. In contrast, in synthesizing a material of the present type, one uses a combination of infiltration with, and pyrolysis of, a preceramic polymer [polymer infiltration followed by pyrolysis (PIP)]. PIP processing is performed in repeated, tailored cycles of infiltration followed by pyrolysis. Densification by PIP processing takes less time and costs less than does densification by CVI. When one of these improved materials was tested by exposure to a high-temperature, inert-gas environment that caused prior C/SiC CMCs to lose strength, this material did not lose strength. (Information on the temperature and exposure time was not available at the time of writing this article.) A material of the present improved type consists, more specifically, of (1) carbon fibers coated with an engineered fiber/matrix interface material and (2) a ceramic matrix, containing SiC, derived from a pre-ceramic polymer with ceramic powder additions. The enhancements of properties of these materials relative to those of prior C/SiC CMC materials are attributable largely to engineering of the fiber/ matrix interfacial material and the densification process. The synthesis of a material of this type includes processing at an elevated temperature to a low level of open porosity. The approach followed in this processing allows one to fabricate not only simple plates but also more complexly shaped parts. The carbon fiber

  18. Silicon Effects on Properties of Melt Infiltrated SiC/SiC Composites

    Science.gov (United States)

    Bhatt, Ramakrishna T.; Gyekenyesi, John Z.; Hurst, Janet B.

    2000-01-01

    Silicon effects on tensile and creep properties, and thermal conductivity of Hi-Nicalon SiC/SiC composites have been investigated. The composites consist of 8 layers of 5HS 2-D woven preforms of BN/SiC coated Hi-Nicalon fiber mats and a silicon matrix, or a mixture of silicon matrix and SiC particles. The Hi-Nicalon SiC/silicon and Hi-Nicalon SiC/SiC composites contained about 24 and 13 vol% silicon, respectively. Results indicate residual silicon up to 24 vol% has no significant effect on creep and thermal conductivity, but does decrease the primary elastic modulus and stress corresponding to deviation from linear stress-strain behavior.

  19. Advanced Environmental Barrier Coating Development for SiC/SiC Ceramic Matrix Composites: NASA's Perspectives

    Science.gov (United States)

    Zhu, Dongming

    2016-01-01

    This presentation reviews NASA environmental barrier coating (EBC) system development programs and the coating materials evolutions for protecting the SiC/SiC Ceramic Matrix Composites in order to meet the next generation engine performance requirements. The presentation focuses on several generations of NASA EBC systems, EBC-CMC component system technologies for SiC/SiC ceramic matrix composite combustors and turbine airfoils, highlighting the temperature capability and durability improvements in simulated engine high heat flux, high pressure, high velocity, and with mechanical creep and fatigue loading conditions. The current EBC development emphasis is placed on advanced NASA 2700F candidate environmental barrier coating systems for SiC/SiC CMCs, their performance benefits and design limitations in long-term operation and combustion environments. Major technical barriers in developing environmental barrier coating systems, the coating integrations with next generation CMCs having the improved environmental stability, erosion-impact resistance, and long-term fatigue-environment system durability performance are described. The research and development opportunities for advanced turbine airfoil environmental barrier coating systems by utilizing improved compositions, state-of-the-art processing methods, and simulated environment testing and durability modeling are discussed.

  20. Preparation, characterization and catalytic behavior of hierachically porous CuO/α-Fe2O3/SiO2 composite material for CO and o-DCB oxidation

    Institute of Scientific and Technical Information of China (English)

    Xiaodong Ma; Xi Feng; Xuan He; Hongwen Guo; Lu Lü

    2011-01-01

    Hierachically porous (HP) CuO/α-Fe2O3/SiO2 composite material was fabricated by sol-gel method and multi-hydrothermal processes using HP-SiO2 as support.The resulting material was characterized by N2 adsorption-desorption,X-ray diffraction and scanning electron microscopy.The as-prepared CuO/Fe2O3/HP-SiO2 sample,with α-Fe2O3 and CuO nanocrystals,possessed a co-continuous skeleton,through-macroporous and mesoporous structure.Its catalytic behavior for CO and o-DCB oxidation was investigated.The result showed that CuO/Fe2O3/HP-SiO2 catalyst exhibited high catalytic activity for both CO and o-DCB oxidation,indicating its potential application in combined abatement of CO and chlorinated volatile organic compounds.

  1. Multi-scale approach to the mechanical behavior of SiC/SiC composites: the concept of mini-composite

    International Nuclear Information System (INIS)

    Lamon, J.

    2007-01-01

    Full text of publication follows: The concept of composite materials is very powerful, since one can tailor the properties with respect to end use applications, through a sound combination of constituents, including fibre, matrix and inter-phases. Ceramic matrix composites (CMCs) are at the forefront of advanced materials technology because of their light weight, high strength and toughness, high temperature capabilities and graceful failure under loading. This key behaviour is achieved by proper design of the fiber/matrix interface which helps in arresting and deflecting the cracks formed in the brittle matrix under load and preventing the early failure of the fiber arrangement. Ceramic matrix composites are considered as enabling technology for advanced aero-propulsion, space power, aerospace vehicles, space structures, ground transportation, as well as nuclear and chemical industries. During the last 30 years, tremendous progress has been made in the development of CMCs. Much research work has been conducted by LCTS on those SiC/SiC composites made via Chemical Vapor Infiltration. A multi-scale approach to mechanical behaviour has been developed. This multi-scale approach is aimed at relating the mechanical behaviour at macroscopic scale to constituent properties. It involves experiments and modelling. It allows chemical effects to be introduced in the models of mechanical behaviour. The present paper discusses the main features of the mechanical behaviour of textile SiC/SiC composites. These features are related to composite microstructure, properties of constituents (fibers, matrix and interphase) and fiber arrangement. Relationships between properties at different scales are established. Then the mini-composite concept is addressed. This concept is very powerful for composite design and investigation. Mini-composites consist of unidirectional composites reinforced by multi-filament tows. Mini-composites represent the mesoscale of textile composites. In

  2. Characterization of rare-earth doped Si 3 N4 /SiC micro/nanocomposites

    Directory of Open Access Journals (Sweden)

    Peter Tatarko

    2010-03-01

    Full Text Available Influence of various rare-earth oxide additives (La2O3, Nd2O3, Sm2O3, Y2O3, Yb2O3 and Lu2O3 on the mechanical properties of hot-pressed silicon nitride and silicon nitride/silicon carbide micro/nano-composites has been investigated. The bimodal character of microstructures was observed in all studied materials where elongated β-Si3N4 grains were embedded in the matrix of much finer Si3N4 grains. The fracture toughness values increased with decreasing ionic radius of rare-earth elements. The fracture toughness of composites was always lower than that of monoliths due to their finer Si3N4/SiC microstructures. Similarly, the hardness and bending strength values increased with decreasing ionic radius of rare-earth elements either in monoliths or composites. On the other hand, the positive influence of finer microstructure of the composites on strength was not observed due to the present defects in the form of SiC clusters and non-reacted carbon zones. Wear resistance at room temperature also increased with decreasing ionic radius of rare-earth element. Significantly improved creep resistance was observed in case either of composite materials or materials with smaller radius of RE3+.

  3. Microstructure and mechanical properties of in situ TiC and Nd2O3 particles reinforced Ti-4.5 wt.%Si alloy composites

    International Nuclear Information System (INIS)

    Zhang, Xinjiang; Li, Yibin; Song, Guangping; Sun, Yue; Peng, Qingyu; Li, Yuxin; He, Xiaodong

    2011-01-01

    Highlights: → (TiC + Nd 2 O 3 )/Ti-4.5 wt.%Si composites were in situ synthesized. → The phase components and microstructures of the composites were investigated. → In situ reinforcements improve the mechanical properties of the matrix alloy. -- Abstract: (TiC + Nd 2 O 3 )/Ti-4.5 wt.%Si composites were in situ synthesized by a non-consumable arc-melting technology. The phases in the composites were identified by X-ray diffraction. Microstructures of the composites were observed by optical microscope and scanning electron microscope. The composite contains four phases: TiC, Nd 2 O 3 , Ti 5 Si 3 and Ti. The TiC and Nd 2 O 3 particles with dendritic and near-equiaxed shapes are well distributed in Ti-4.5 wt.%Si alloy matrix, and the fine Nd 2 O 3 particles exist in the network Ti + Ti 5 Si 3 eutectic cells and Ti matrix of the composites. The hardness and compressive strength of the composites are markedly higher than that of Ti-4.5 wt.%Si alloy. When the TiC content is fixed as 10 wt.% in the composites, the hardness is enhanced as the Nd 2 O 3 content increases from 8 wt.% to 13 wt.%, but the compressive strength peaks at the Nd 2 O 3 content of 8 wt.%.

  4. Simulation of thermal stresses in SiC-Al2O3 composite tritium penetration barrier by finite-element analysis

    International Nuclear Information System (INIS)

    Liu, Hongbing; Tao, Jie; Gautreau, Yoann; Zhang, Pingze; Xu, Jiang

    2009-01-01

    Tritium penetration barrier (TPB) composed of Al 2 O 3 and SiC on 316L stainless steel was proposed to improve the tritium penetration resistance of the substrate in this work. At the same time, the concept of functionally graded materials (FGM) was applied to manage to decrease residual stresses between Al 2 O 3 and 316L stainless steel substrate due to the mismatch of their thermal expansion coefficients. The effects of system architecture on the residual stresses developed in the composite coatings were investigated numerically by means of finite-element analysis (FEA). Modeling results showed that the presence of the graded properties and the compositions within the coating did reduce the stress discontinuity at the interfaces between the coating and the substrate. Also, the magnitudes of the residual stresses on the coating surface and at the coating/substrate interface were dependent on the Al 2 O 3 and SiC coating thickness.

  5. Liquidus Temperature of SrO-Al2O3-SiO2 Glass-Forming Compositions

    DEFF Research Database (Denmark)

    Abel, Brett M.; Morgan, James M.; Mauro, John C.

    2013-01-01

    . In the composition range of interest for industrial glasses, Tliq tends to decrease with increasing strontium-to-alumina ratio. We find that cristobalite, mullite, and slawsonite are the dominant devitrification phases for the compositions with high SiO2, SiO2+Al2O3, and SrO contents, respectively. By comparison...... with the phase diagrams for CaO-Al2O3-SiO2 and MgO-Al2O3-SiO2 systems, we have found that for the highest [RO]/[Al2O3] ratios, Tliq exhibits a minimum value for R = Ca. Based on the phase diagram established here, the composition of glass materials, for example, for liquid crystal display substrates, belonging...... to the SrO-Al2O3-SiO2 family may be designed with a more exact control of the glass-forming ability by avoiding the regions of high liquidus temperature....

  6. Oxidation-resistant interface coatings for Nicalon/SiC composites

    Energy Technology Data Exchange (ETDEWEB)

    Stinton, D.P.; Besmann, T.M.; Lowden, R.A. [Oak Ridge National Lab., TN (United States); Liaw, P.K.; Shanmugham, S. [Univ. of Tennessee, Knoxville, TN (United States)

    1997-12-01

    Nicalon/SiC composites with thin C and C/oxide/C interfaces were fabricated. The oxide layers, mullite and Al{sub 2}O{sub 3}-TiO{sub 2}, were deposited by a sol-gel process, while the C layer was deposited by a chemical vapor infiltration method. The fabricated composites were flexure tested in both as-processed and oxidized conditions. Composites with C and C/oxide/C interfaces retained graceful failure even after 500 h oxidation at 1000 C, but with reduced flexural strengths.

  7. Oxidation of SiC/BN/SiC Composites in Reduced Oxygen Partial Pressures

    Science.gov (United States)

    Opila, Elizabeth J.; Boyd, Meredith

    2010-01-01

    SiC fiber-reinforced SiC composites with a BN interphase are proposed for use as leading edge structures of hypersonic vehicles. The durability of these materials under hypersonic flight conditions is therefore of interest. Thermogravimetric analysis was used to characterize the oxidation kinetics of both the constituent fibers and composite coupons at four temperatures: 816, 1149, 1343, and 1538 C (1500, 2100, 2450, and 2800 F) and in oxygen partial pressures between 5% and 0.1% (balance argon) at 1 atm total pressure. One edge of the coupons was ground off so the effects of oxygen ingress into the composite could be monitored by post-test SEM and EDS. Additional characterization of the oxidation products was conducted by XPS and TOF-SIMS. Under most conditions, the BN oxidized rapidly, leading to the formation of borosilicate glass. Rapid initial oxidation followed by volatilization of boria lead to protective oxide formation and further oxidation was slow. At 1538C in 5% oxygen, both the fibers and coupons exhibited borosilicate glass formation and bubbling. At 1538C in 0.1% oxygen, active oxidation of both the fibers and the composites was observed leading to rapid SiC degradation. BN oxidation at 1538C in 0.1% oxygen was not significant.

  8. Phase Equilibria Study in the TeO2-Na2O-SiO2 System in Air Between 723 K (500 °C) and 1473 K (1200 °C)

    Science.gov (United States)

    Santoso, Imam; Taskinen, Pekka

    2016-08-01

    Knowledge of phase equilibria in the TeO2-Na2O-SiO2 system at elevated temperatures is important for ceramic and glass industries and for improving the operation of the smelting process of tellurium-containing materials. A review of previous investigations has indicated, however, that there are omissions in the available datasets on the liquidus temperatures of the molten TeO2-Na2O-SiO2 mixtures. The employed experimental method included equilibration of mixtures made from high purity oxides, rapid quenching of the equilibrated samples in water and followed by compositional analysis of the phases using an electron probe X-ray microanalyzer. The liquidus and phase equilibria in the TeO2-SiO2, TeO2-Na2O, and SiO2-TeO2-Na2O systems have been studied for a wide range of compositions between 723 K (500 °C) and 1473 K (1200 °C) at TeO2, SiO2, and Na2SiO3 saturations. New data have been generated in the SiO2-TeO2-Na2O system at SiO2 saturation. The liquidus compositions in the TeO2-Na2O system at TeO2 saturation have been compared with the previous data and an assessed phase diagram.

  9. Microstructure, thermal behavior and mechanical properties of squeeze cast SiC, ZrO2 or C reinforced ZA27 composites

    International Nuclear Information System (INIS)

    El-khair, M.T. Abou; Lotfy, A.; Daoud, A.; El-Sheikh, A.M.

    2011-01-01

    Research highlights: → ZA27 with 5% SiC, ZrO2 or C particles are synthesized by stirring then squeezed. → Particles refine the structure. 50 MPa decreases porosity% and increases density. → α and β nucleation temperatures of the composites are lower than those of the matrix. → Particles accelerate age hardening and increase peak hardness of the composites → Particles reduce the CTEs of composites compared to those of the matrix. - Abstract: ZA27 alloy based composites were synthesized by stirring method, followed by squeeze casting. Stir casting was employed successfully to incorporate 5 vol.% of various reinforcement particulates, namely, SiC, ZrO 2 or C. The porosity in the composites was decreased by squeeze pressure. The presence of particles and/or application of squeeze pressure during solidification resulted in considerable refinement in the structure of the composites. The microstructures, X-ray diffraction (XRD) and energy dispersive X-ray analysis (EDXA) results indicated that no significant reactions occurred at the interface between the SiC or C particles and ZA27 alloy. However, in case of ZrO 2 reinforced ZA27, the ZrO 2 reacted with Cu present in the molten ZA27 alloy, forming Cu 5 Zr. Thermal analysis showed that both α and β nucleation and growth temperatures of the composites were lower than those of the ZA27 alloy. The presence of particles in the as-cast or squeezed composites led to not only an accelerated age hardening response, but also an increase in the peak hardness of the composites. The values of coefficient of thermal expansion (CTE) of the composites were drastically lower as compared to those of the ZA27 alloy. The tensile properties of the composites decreased as a result of the addition of the particles. Scanning electron microscope (SEM) pictures of the composites indicated that cracks mainly initiated at particle-matrix interface, propagated through the matrix and linked up with other cracks leading to failure of the

  10. The effect of SiC particle size on the properties of Cu–SiC composites

    International Nuclear Information System (INIS)

    Celebi Efe, G.; Zeytin, S.; Bindal, C.

    2012-01-01

    Graphical abstract: The relative densities of Cu–SiC composites sintered at 700 °C for 2 h are ranged from 97.3% to 91.8% for SiC with 1 μm particle size and 97.5% to 95.2% for SiC with 5 μm particle size, microhardness of composites ranged from 143 to 167 HV for SiC having 1 μm particle size and 156–182 HVN for SiC having 5 μm particle size and the electrical conductivity of composites changed between 85.9% IACS and 55.7% IACS for SiC with 1 μm particle size, 87.9% IACS and 65.2%IACS for SiC with 5 μm particle size. It was found that electrical conductivity of composites containing SiC with 5 μm particle size is better than that of Cu–SiC composites containing SiC with particle size of 1 μm. Highlights: ► In this research, the effect of SiC particle size on some properties of Cu–SiC composites were investigated. ► The mechanical properties were improved. ► The electrical properties were obtained at desirable level. -- Abstract: SiC particulate-reinforced copper composites were prepared by powder metallurgy (PM) method and conventional atmospheric sintering. Scanning electron microscope (SEM), X-ray diffraction (XRD) techniques were used to characterize the sintered composites. The effect of SiC content and particle size on the relative density, hardness and electrical conductivity of composites were investigated. The relative densities of Cu–SiC composites sintered at 700 °C for 2 h are ranged from 97.3% to 91.8% for SiC with 1 μm particle size and from 97.5% to 95.2% for SiC with 5 μm particle size. Microhardness of composites ranged from 143 to 167 HV for SiC having 1 μm particle size and from 156 to 182 HV for SiC having 5 μm particle size. The electrical conductivity of composites changed between 85.9% IACS and 55.7% IACS for SiC with 1 μm particle size, between 87.9% IACS and 65.2% IACS for SiC with 5 μm particle size.

  11. Mechanical Properties of SiC, Al2O3 Reinforced Aluminium 6061-T6 Hybrid Matrix Composite

    Science.gov (United States)

    Murugan, S. Senthil; Jegan, V.; Velmurugan, M.

    2018-04-01

    This paper contains the investigation of tensile, compression and impact characterization of SiC, Al2O3 reinforced Aluminium 6061-T6 matrix hybrid composite. Hybrid matrix composite fabrication was done by stir casting method. An attempt has been made by keeping Al2O3 percentage (7%) constant and increasing SiC percentage (10, 15, and 20%). After fabricating, the samples were prepared and tested to find out the various mechanical properties like tensile, compressive, and impact strength of the developed composites of different weight % of silicon carbide and Alumina in Aluminium alloy. The main objective of the study is to compare the values obtained and choose the best composition of the hybrid matrix composite from the mechanical properties point of view.

  12. Matrix densification of SiC composites by sintering process

    International Nuclear Information System (INIS)

    Kim, Young-Wook; Jang, Doo-Hee; Eom, Jung-Hye; Chun, Yong-Seong

    2007-02-01

    The objectives of this research are to develop a process for dense SiC fiber-SiC composites with a porosity of 5% or less and to develop high-strength SiC fiber-SiC composites with a strength of 500 MPa or higher. To meet the above objectives, the following research topics were investigated ; new process development for the densification of SiC fiber-SiC composites, effect of processing parameters on densification of SiC fiber-SiC composites, effect of additive composition on matrix microstructure, effects of additive composition and content on densification of SiC fiber-SiC composites, mechanical properties of SiC fiber-SiC composites, effect of fiber coating on densification and strength of SiC fiber-SiC composites, development of new additive composition. There has been a great deal of progress in the development of technologies for the processing and densification of SiC fiber-SiC composites and in better understanding of additive-densification-mechanical property relations as results of this project. Based on the progress, dense SiC fiber-SiC composites (≥97%) and high strength SiC fiber-SiC composites (≥600 MPa) have been developed. Development of 2D SiC fiber-SiC composites with a relative density of ≥97% and a strength of ≥600 MPa can be counted as a notable achievement

  13. Preliminary calculations of stress change of fuel pin using SiC/SiC composites for GFR with changing of thermal conductivity degradation by irradiation

    International Nuclear Information System (INIS)

    Lee, J. K.; Naganuma, M.

    2006-01-01

    Gas cooled Fast Reactor (GFR) is being researched as a candidate concept of Generation IV international Forum. As a main feature of GFR, it should be maintained high temperature and pressure of coolant gas for heat transfer efficiency. Such a demanding environment requires high-temperature-resistant structural materials distinguished from traditional steel material. Consequently, ceramics are promising candidate material of core components. Especially, Silicon Carbide fiber reinforced Silicon Carbide composites (SiC/SiC) have encouraging characteristics such as refractoriness, low activation and toughness. Application of new material to core components must be explained by the viewpoint of engineering validity. Therefore, present study surveyed that current report for mechanical strength and thermal conductivity of SiC/SiC composites. According to the reports, neutron irradiation environment degraded mechanical properties of SiC/SiC composites. To confirm applicability to core components, model of fuel pin using SiC/SiC composites was assumed with feasible mechanical properties. Furthermore, it was calculated and estimated that the stress caused by temperature variation of inner and outer side of assumed model of cladding tube. Stress was calculated by changing of input date such as thickness of cladding tube, temperature variation, thermal conductivity and linear power. In the range of this study, the most important factor was identified as degradation of thermal conductivity by irradiation. It caused a significant stress and limited a geometrical design of fuel pin. It was discussed that the differences of heat transfer between isotropic and anisotropic materials like a metal and composites. These results should be helpful not only to determine a design factor of core component but also to indicate an improvement direction of SiC/SiC composites. Through these work, reliability and safety of GFR will be increased

  14. Thermochemical instability effects in SiC-based fibers and SiC{sub f}/SiC composites

    Energy Technology Data Exchange (ETDEWEB)

    Youngblood, G.E.; Henager, C.H.; Jones, R.H. [Pacific Northwest National Laboratory, Richland, WA (United States)

    1997-08-01

    Thermochemical instability in irradiated SiC-based fibers with an amorphous silicon oxycarbide phase leads to shrinkage and mass loss. SiC{sub f}/SiC composites made with these fibers also exhibit mass loss as well as severe mechanical property degradation when irradiated at 800{degrees}C, a temperature much below the generally accepted 1100{degrees}C threshold for thermomechanical degradation alone. The mass loss is due to an internal oxidation mechanism within these fibers which likely degrades the carbon interphase as well as the fibers in SiC{sub f}/SiC composites even in so-called {open_quotes}inert{close_quotes} gas environments. Furthermore, the mechanism must be accelerated by the irradiation environment.

  15. Yttrium silicate as an oxidation protection layer for C/C-SiC materials. Synthesis, electrophoretic deposition and high temperature oxidation; Yttriumsilikat als Oxidationsschutzschicht fuer C/C-SiC-Werkstoffe. Synthese, elektrophoretische Abscheidung und Hochtemperaturoxidation

    Energy Technology Data Exchange (ETDEWEB)

    Grosse-Brauckmann, Jana

    2012-07-01

    Carbon fibre reinforced carbon composites are promising materials for high temperature applications. They exhibit excellent thermal shock resistance and nearly constant mechanical strength. A serious draw-back of this material is their poor resistivity towards oxidation at temperatures above 400 C. To make use of the very good thermal stability the material needs an outer oxidation protection coating. Silicon carbide has been successfully employed at temperatures up to 1300 C. To increase the application range towards higher temperatures an outer environmental barrier coating is needed. In the present work yttrium silicates were used to complement the silicon carbide coated carbon fibre reinforced carbon material. Both stable compounds in the quasi-binary system Y{sub 2}O{sub 3}-SiO{sub 2}, yttrium orthosilicate (Y{sub 2}SiO{sub 5}) and yttrium pyrosilicate (Y{sub 2}Si{sub 2}O{sub 7}), were separately applied to the test samples via electrophoretic deposition. Suitable suspensions were prepared in butanone with iodine as charging agent to adjust conductivity and particle charge. Galvanostatic deposition obeys a linear growth law for the selected deposition times. Alternatively the feasibility of direct electrophoretic deposition from an yttrium silicate precursor sol was tested. Emphasis was put on the development of a suitable sol-system based on alkoxide precursors. Samples coated either with Y{sub 2}SiO{sub 5} or Y{sub 2}Si{sub 2}O{sub 7} were investigated using thermogravimetric high temperature oxidation in the temperature range from 1450 C to 1650 C, respectively. The coated samples exhibited very good oxidation resistance up to temperatures of 1600 C, while the performance was reduced at 1650 C to a few hours. All samples showed a parabolic mass increase with time indicating a diffusion limited process governing the oxidation kinetics. The cross sections of the samples show a sharp border between the SiO{sub 2} that crystallizes to cristobalite and the

  16. Synthesis of Li2MnSiO4-graphene composite and its electrochemical performances as a cathode material for lithium ion batteries.

    Science.gov (United States)

    Kim, Jeonghyun; Song, Taeseup; Park, Hyunjung; Yuh, Junhan; Paik, Ungyu

    2014-10-01

    The Li2MnSiO4 is a promising candidate as a cathode for lithium ion batteries due to its large theoretical capacity of 330 mA h g(-1) and high thermal stability. However, the problems related to low electronic conductivity and large irreversible capacity at the first cycle limits its practical use as a Li-ion cathode material. We have developed a carbon coated Li2MnSiO4-graphene composite electrode to overcome these problems. Our designed electrode exhibits high reversible capacity of 301 mA h g(-1), with a high initial coulombic efficiency, and a discharge capacity at current rate of 0.5 C, that is double value of carbon coated Li2MnSiO4-carbon black composite electrode. These significant improvements are attributed to fast electron transport along the graphene sheet.

  17. Synthesis and structural stability of Cr-doped Li2MnSiO4/C cathode materials by solid-state method

    Science.gov (United States)

    Cheng, Hong-Mei; Zhao, Shi-Xi; Wu, Xia; Zhao, Jian-Wei; Wei, Lei; Nan, Ce-Wen

    2018-03-01

    The crystal structure of the Li2MnSiO4 cathode material would collapse during the charge and discharge process because of that the Mn-O coordination polyhedron changed from [MnO4] into [MnO6] in the process of Mn+2 to Mn+4, but the Cr element could remain [CrO4] crystal ligand from Cr+2 to Cr+4, so Cr element substitution was used to improve the structural stability of the Li2MnSiO4 cathode material. In this work, Li2Mn1-xCrxSiO4/C nanocomposites were synthesized by solid-state method. XRD, SEM and TEM observations show that the as-prepared Li2Mn1-xCrxSiO4/C materials presents an orthorhombic crystal structure (S.G. Pmn21), the particle size of Li2Mn1-xCrxSiO4/C powder ranges from 50 to 100 nm. The XRD and XPS results indicate that Cr+2 is successfully doped into Li2MnSiO4 lattice and has well compatibility with Li2MnSiO4. The electrochemical results display that Li2Mn92.5%Cr7.5%SiO4/C exhibits significantly enhanced cycle stability and discharge capability. The initial discharge capacity of the Li2Mn92.5%Cr7.5%SiO4/C sample is 255 mAh g-1, and the discharge capacity was still about 60 mAh g-1 after 50 cycles. Furthermore, the XRD patterns, TEM images and Raman analysis reveal that the Cr doping enhances the structural stability of Li2Mn1-xCrxSiO4/C and improves the electrochemical activity of the cathode. Thus, the Li2Mn92.5%Cr7.5%SiO4/C have shown potential applications for lithium ion batteries.

  18. Self assembly of SiO2-encapsulated carbon microsphere composites

    International Nuclear Information System (INIS)

    Yang Yongzhen; Song Jingjing; Han Yanxing; Guo Xingmei; Liu Xuguang; Xu Bingshe

    2011-01-01

    SiO 2 was firstly coated onto the surface of carbon microspheres (CMSs) using tetraethyl orthosilicate (TEOS) as precursor by Stoeber method. Then SiO 2 -encapsulated CMS (CMS-SiO 2 ) composites were self-assembled by vertical deposition, in which the effects of deposition temperature and suspension concentration on the quality of self-assembling film were investigated. Morphologies and structures of the samples were characterized by field emission scanning electron microscopy, Fourier transformation infrared spectrometry, X-ray diffraction and thermogravimetry. The results show that uniform CMS-SiO 2 composites with good mono-dispersion were prepared by Stober method with 0.5 g of CMSs, 2 mL of TEOS, 30 mL of ammonia and 12 h of reaction time, the CMSs-based films with ordered and denser structure were prepared by vertical deposition using CMS-SiO 2 composites as monodipersion spheres under suspension concentration of 1 wt% and deposition temperature of 50 deg. C. The ultraviolet-visible absorption measurement shows that the absorbance of CMS-SiO 2 composite films grew steadily with increasing suspension concentration.

  19. Joining of SiC/SiCf ceramic matrix composites for fusion reactor blanket applications

    International Nuclear Information System (INIS)

    Colombo, P.; Riccardi, B.; Donato, A.; Scarinci, G.

    2000-01-01

    Using a preceramic polymer, joints between SiC/SiC f ceramic matrix composites were obtained. The polymer, upon pyrolysis at high temperature, transforms into a ceramic material and develops an adhesive bonding with the composite. The surface morphology of 2D and 3D SiC/SiC f composites did not allow satisfactory results to be obtained by a simple application of the method initially developed for monolithic SiC bodies, which employed the use of a pure silicone resin. Thus, active or inert fillers were mixed with the preceramic polymer, in order to reduce its volumetric shrinkage which occurs during pyrolysis. In particular, the joints realized using the silicone resin with Al-Si powder as reactive additive displayed remarkable shear strength (31.6 MPa maximum). Large standard deviation for the shear strength has nevertheless been measured. The proposed joining method is promising for the realization of fusion reactor blanket structures, even if presently the measured strength values are not fully satisfactory

  20. Effect of inclusion of SiC particulates on the mechanical resistance behaviour of stir-cast AA6063/SiC composites

    International Nuclear Information System (INIS)

    Balasubramanian, I.; Maheswaran, R.

    2015-01-01

    Highlights: • AA6063/SiC composites with different weight percent are stir cast. • Resistance properties against indentation, stretching force and sliding force are studied. • Increase in initiation of cleavage facets and reduces the tensile strength for 15% SiC. • Transition from micro ploughing to micro cutting wear mechanism is less due to SiC inclusion. - Abstract: This study investigates the mechanical resistance behaviour of AA6063 particulate composites with the inclusion of micron-sized silicon carbide (SiC) particles with different weight percentages in an AA6063 aluminium matrix. AA6063/SiC particulate composites containing 0, 5, 10, and 15 weight percent of SiC particles were produced by stir casting. Standard mechanical tests were conducted on the composite plates, and the mechanical resistance to indentation, tensile force and sliding force are evaluated. It has been observed that upon addition of SiC particles, the resistance against indentation is increased and the resistance against tensile force is initially increased and then decreased. Furthermore, using scanning electron microscopy (SEM), the fracture appearance of the broken specimen subjected to tensile force and morphological changes in the surface subjected to sliding force are analysed. The SEM images reveal that the addition of SiC particles in the AA6063 aluminium matrix initiates more cleavage facets. This leads to brittle fracture in the specimen subjected to tensile forces and less transition from material displacement to material removal in the specimen subjected to sliding forces

  1. Fracture behavior of C/SiC composites at elevated temperature

    Energy Technology Data Exchange (ETDEWEB)

    Yoon, Dong Hyun; Lee, Jeong Won; Kim, Jae Hoon; Shin, Ihn Cheol; Lim, Byung Joo [Chungnam National University, Daejeon (Korea, Republic of)

    2017-08-15

    The fracture behavior of carbon fiber-reinforced silicon carbide (C/SiC) composites used in rocket nozzles has been investigated under tension, compression, and fracture conditions at room temperature, 773 K and 1173 K. The C/SiC composites used in this study were manufactured by liquid silicon infiltration process at ~1723 K. All experiments were conducted using two types of specimens, considering fiber direction and oxidation condition. Experimental results show that temperature, fiber direction, and oxidation condition affect the behavior of C/SiC composites. Oxidation was found to be the main factor that changes the strength of C/SiC composites. By applying an anti-oxidation coating, the tensile and compressive strengths of the C/SiC composites increased with temperature. The fracture toughness of the C/SiC composites also increased with increase temperature. A fractography analysis of the fractured specimens was conducted using a scanning electron microscope.

  2. Electrochemical properties of Li2 FeSiO4 /C nanocomposites prepared by sol-gel and hydrothermal methods

    Science.gov (United States)

    Kumar, Ajay; Jayakumar, O. D.; Naik, Vaman M.; Nazri, Gholam A.; Naik, Ratna

    Li2FeSiO4 is considered as potential cathode material for next generation lithium ion batteries because of its high specific theoretical capacity, low cost, and safety. However, it suffers from poor electronic conductivity and slow lithium ion diffusion in the solid phase. To address these issues, we have studied mesoporous Li2FeSiO4/C composites synthesized by sol-gel (SG) and hydrothermal (HT) methods using tri-block copolymer (P123) as carbon source and structure directing agent. The structure and morphology of the composites were characterized by XRD, SEM and TEM and the surface area and pore size distribution were measured by using N2 adsorption/desorption. Galvanostatic cycling, electrochemical impedance spectroscopy, and cyclic voltammetry were used to evaluate the electrochemical performance of the Li2FeSiO4/C composites. The Li2FeSiO4/C (HT) composites show a superior electrochemical performance compared to Li2FeSiO4/C (SG). At C/30 rate, the discharge capacity of Li2FeSiO4/C (HT) reached ~276 mAh/g in the 1.5-4.6 V window and shows better rate capability and stability at high rates. We attribute the improved electrochemical performance of Li2FeSiO4/C (HT) to its large surface area and reduced particle size. The details of the study will be presented.

  3. Wear resistance of polypropylene-SiC composite

    Science.gov (United States)

    Abenojar, J.; Enciso, B.; Martínez, MA; Velasco, F.

    2017-05-01

    In this work, the wear resistance of thermoplastic composites with a high amount of ceramic is evaluated. Composites made of polypropylene (PP) and silicon carbide (SiC) powder at 50 wt% were used with the final objective of manufacturing ablative materials. This is the first part of a project studying the wear resistance and the mechanical properties of those composites, to be used in applications like habitat industry. In theory, the exposure to high temperature of ablative materials involves the elimination of thermal energy by the sacrifice of surface polymer. In our case, PP will act as a heat sink, up to the reaction temperature (melting or sublimation), where endothermic chemical decomposition into charred material and gaseous products occurs. As the surface is eroded, it is formed a SiC like-foam with improved insulation performance. Composites were produced by extrusion and hot compression. The wear characterization was performed by pin-on-disk test. Wear test was carried out under standard ASTM G99. The parameters were 120 rpm speed, 15 N load, a alumina ball with 6 mm as pin and 1000 m sliding distance. The tracks were also observed by opto-digital microscope.

  4. Wear resistance of polypropylene-SiC composite

    International Nuclear Information System (INIS)

    Abenojar, J; Enciso, B; Martínez, MA; Velasco, F

    2017-01-01

    In this work, the wear resistance of thermoplastic composites with a high amount of ceramic is evaluated. Composites made of polypropylene (PP) and silicon carbide (SiC) powder at 50 wt% were used with the final objective of manufacturing ablative materials. This is the first part of a project studying the wear resistance and the mechanical properties of those composites, to be used in applications like habitat industry. In theory, the exposure to high temperature of ablative materials involves the elimination of thermal energy by the sacrifice of surface polymer. In our case, PP will act as a heat sink, up to the reaction temperature (melting or sublimation), where endothermic chemical decomposition into charred material and gaseous products occurs. As the surface is eroded, it is formed a SiC like-foam with improved insulation performance. Composites were produced by extrusion and hot compression. The wear characterization was performed by pin-on-disk test. Wear test was carried out under standard ASTM G99. The parameters were 120 rpm speed, 15 N load, a alumina ball with 6 mm as pin and 1000 m sliding distance. The tracks were also observed by opto-digital microscope. (paper)

  5. Sintering of new SiC-Phosphate composite materials for grinding wheels fabrication

    Directory of Open Access Journals (Sweden)

    Silva, R. F.

    2004-04-01

    Full Text Available The effect of several variables such as molar ratio P2O5/B2O3 (X, temperature and heating cycle on the strength of chemically bonded SiC materials for grinding wheels fabrication was studied. It was shown that the highest compressive strength (52.4 MPa could be obtained using an optimal molar ratio X = 4.5 and a multiple step heating cycle up to a sintering temperature of 800oC. DTA, XRD, SEM and dilatometrical analysis were performed to follow the different stages of the structural development.

    Se estudia el efecto de diferentes variables tales como la razón molar P2O5/B2O3(X, temperatura y ciclo de calentamieno sobre la resistencia de materiales de SiC aglomerados quimicamente para la fabricación de muelas arasivas. Se ha comprobado que la más alta resistencia a la compresión (52,4MPa pueda obtenerse usando una razón molar òptima x= 4,5 y un ciclo de calentamiento en múltiples etapas hasta la temperatura de 800º C. Estudios mediante ATD, DRX, MEB y análisis dilatométricos fueron llevados a cabo para seguir las diferentes etapas del desarrollo microestructura.

  6. Effects of the curing methods on the fabrication of polycarbosilane derived SiCf/SiC composite

    International Nuclear Information System (INIS)

    Park, Ji Yeon; Kim, Weon Ju; Ryu, Woo Seog; Woo, Chang Hyun; Han, Bum Soo

    2005-01-01

    Silicon carbide has potential advantages for structural applications in the next generation energy system- VHTR, GFR and the fusion reactor due to its unique properties such as a good irradiation resistance and thermo-mechanical properties, less severe waste generation due to neutron activation and improved plant conversion efficiencies by higher operating temperatures. Among the several fabrication processes for SiC f /SiC composites, the polymer impregnation and pyrolysis (PIP) process is the only method derived from polymeric precursors. In the PIP process, the careful control of the oxygen content is important to avoid the property degradation at a high temperature because polymeric precursors are used as source materials of SiC ceramics. During the polymer precursor conversion process, unintended oxygen may be introduced for a cross-linking with producing the Si-O-Si bonds at the curing step. High oxygen content affects the degradation of the high temperature stability in SiC ceramics. Therefore, a decrease of the oxygen content is desirable to obtain SiC ceramics with the high temperature stability. One of the methods to reduce the oxygen content of polymer derived SiC ceramics is the irradiation curing process by gamma ray or electron beam. Polymer derived SiC ceramics with the low oxygen content prepared by the electron beam curing showed the improved thermal stability at a higher temperature. In this study, the electron beam (EB) and the thermal oxidation curing methods were applied to make SiC f /SiC composite using a polymer precursor, polycarbosilane (PCS) by the PIP process. And the evaluations of the curing effects, the pyrolysis behaviors and a high temperature stability were performed

  7. Introduction of nano-laminate Ti3SiC2 and SiC phases into Cf-C composite by liquid silicon infiltration method

    Directory of Open Access Journals (Sweden)

    Omid Yaghobizadeh

    2017-03-01

    Full Text Available The material Cf-C-SiC-Ti3SiC2 is promising for high temperature application. Due to the laminated structure and special properties, the Ti3SiC2 is one of the best reinforcements for Cf-C-SiC composites. In this paper, Cf-C-SiC-Ti3SiC2 composites were fabricated by liquid silicon infiltration (LSI method; the effect of the TiC amount on the various composites properties were studied. For samples with 0, 50 and 90 vol.% of TiC, the results show that bending strength are 168, 190, and 181 MPa; porosities are 3.2, 4.7, and 9%; the fracture toughness are 6.1, 8.9, and 7.8 MPa∙m1/2; interlaminar shear strength are 27, 36, and 30 MPa; the amount of the MAX phase are 0, 8.5, and 5.6 vol.%, respectively. These results show that amount of TiC is not the main effective parameter in synthesis of Ti3SiC2. The existence of carbon promotes the synthesis of Ti3SiC2 indicating that only sufficient carbon content can lead to the appearance of Ti3SiC2 in the LSI process.

  8. Compositional and optical properties of SiO x films and (SiO x /SiO y ) junctions deposited by HFCVD

    Science.gov (United States)

    2014-01-01

    In this work, non-stoichiometric silicon oxide (SiO x ) films and (SiO x /SiO y ) junctions, as-grown and after further annealing, are characterized by different techniques. The SiO x films and (SiO x /SiO y ) junctions are obtained by hot filament chemical vapor deposition technique in the range of temperatures from 900°C to 1,150°C. Transmittance spectra of the SiO x films showed a wavelength shift of the absorption edge thus indicating an increase in the optical energy band gap, when the growth temperature decreases; a similar behavior is observed in the (SiO x /SiO y ) structures, which in turn indicates a decrease in the Si excess, as Fourier transform infrared spectroscopy (FTIR) reveals, so that, the film and junction composition changes with the growth temperature. The analysis of the photoluminescence (PL) results using the quantum confinement model suggests the presence of silicon nanocrystal (Si-nc) embedded in a SiO x matrix. For the case of the as-grown SiO x films, the absorption and emission properties are correlated with quantum effects in Si-nc and defects. For the case of the as-grown (SiO x /SiO y ) junctions, only the emission mechanism related to some kinds of defects was considered, but silicon nanocrystal embedded in a SiO x matrix is present. After thermal annealing, a phase separation into Si and SiO2 occurs, as the FTIR spectra illustrates, which has repercussions in the absorption and emission properties of the films and junctions, as shown by the change in the A and B band positions on the PL spectra. These results lead to good possibilities for proposed novel applications in optoelectronic devices. PACS 61.05.-a; 68.37.Og; 61.05.cp; 78.55.-m; 68.37.Ps; 81.15.Gh PMID:25342935

  9. Influence of helium atoms on the shear behavior of the fiber/matrix interphase of SiC/SiC composite

    Science.gov (United States)

    Jin, Enze; Du, Shiyu; Li, Mian; Liu, Chen; He, Shihong; He, Jian; He, Heming

    2016-10-01

    Silicon carbide has many attractive properties and the SiC/SiC composite has been considered as a promising candidate for nuclear structural materials. Up to now, a computational investigation on the properties of SiC/SiC composite varying in the presence of nuclear fission products is still missing. In this work, the influence of He atoms on the shear behavior of the SiC/SiC interphase is investigated via Molecular Dynamics simulation following our recent paper. Calculations are carried out on three dimensional models of graphite-like PyC/SiC interphase and amorphous PyC/SiC interphase with He atoms in different regions (the SiC region, the interface region and the PyC region). In the graphite-like PyC/SiC interphase, He atoms in the SiC region have little influence on the shear strength of the material, while both the shear strength and friction strength may be enhanced when they are in the PyC region. Low concentration of He atoms in the interface region of the graphite-like PyC/SiC interphase increases the shear strength, while there is a reduction of shear strength when the He concentration is high due to the switch of sliding plane. In the amorphous PyC/SiC interphase, He atoms can cause the reduction of the shear strength regardless of the regions that He atoms are located. The presence of He atoms may significantly alter the structure of SiC/SiC in the interface region. The influence of He atoms in the interface region is the most significant, leading to evident shear strength reduction of the amorphous PyC/SiC interphase with increasing He concentration. The behaviors of the interphases at different temperatures are studied as well. The dependence of the shear strengths of the two types of interphases on temperatures is studied as well. For the graphite-like PyC/SiC interphase, it is found strongly related to the regions He atoms are located. Combining these results with our previous study on pure SiC/SiC system, we expect this work may provide new insight

  10. Influence of helium atoms on the shear behavior of the fiber/matrix interphase of SiC/SiC composite

    Energy Technology Data Exchange (ETDEWEB)

    Jin, Enze [State Nuclear Power Research Institute, Beijing, 100029 (China); Du, Shiyu, E-mail: dushiyu@nimte.ac.cn [Engineering Laboratory of Specialty Fibers and Nuclear Energy Materials, Ningbo Institute of Materials Technology and Engineering, Chinese Academy of Sciences, Ningbo, Zhejiang, 315201 (China); Li, Mian [Engineering Laboratory of Specialty Fibers and Nuclear Energy Materials, Ningbo Institute of Materials Technology and Engineering, Chinese Academy of Sciences, Ningbo, Zhejiang, 315201 (China); Liu, Chen [Beijing Research Institute of Chemical Engineering and Metallurgy (China); He, Shihong [State Nuclear Power Research Institute, Beijing, 100029 (China); Engineering Laboratory of Specialty Fibers and Nuclear Energy Materials, Ningbo Institute of Materials Technology and Engineering, Chinese Academy of Sciences, Ningbo, Zhejiang, 315201 (China); He, Jian [Center for Translational Medicine, Department of Biotechnology, Dalian Institute of Chemical Physics, Chinese Academy of Sciences, Dalian, Liaoning, 116023 (China); He, Heming, E-mail: heheming@snptc.com.cn [State Nuclear Power Research Institute, Beijing, 100029 (China)

    2016-10-15

    Silicon carbide has many attractive properties and the SiC/SiC composite has been considered as a promising candidate for nuclear structural materials. Up to now, a computational investigation on the properties of SiC/SiC composite varying in the presence of nuclear fission products is still missing. In this work, the influence of He atoms on the shear behavior of the SiC/SiC interphase is investigated via Molecular Dynamics simulation following our recent paper. Calculations are carried out on three dimensional models of graphite-like PyC/SiC interphase and amorphous PyC/SiC interphase with He atoms in different regions (the SiC region, the interface region and the PyC region). In the graphite-like PyC/SiC interphase, He atoms in the SiC region have little influence on the shear strength of the material, while both the shear strength and friction strength may be enhanced when they are in the PyC region. Low concentration of He atoms in the interface region of the graphite-like PyC/SiC interphase increases the shear strength, while there is a reduction of shear strength when the He concentration is high due to the switch of sliding plane. In the amorphous PyC/SiC interphase, He atoms can cause the reduction of the shear strength regardless of the regions that He atoms are located. The presence of He atoms may significantly alter the structure of SiC/SiC in the interface region. The influence of He atoms in the interface region is the most significant, leading to evident shear strength reduction of the amorphous PyC/SiC interphase with increasing He concentration. The behaviors of the interphases at different temperatures are studied as well. The dependence of the shear strengths of the two types of interphases on temperatures is studied as well. For the graphite-like PyC/SiC interphase, it is found strongly related to the regions He atoms are located. Combining these results with our previous study on pure SiC/SiC system, we expect this work may provide new insight

  11. Influence of helium atoms on the shear behavior of the fiber/matrix interphase of SiC/SiC composite

    International Nuclear Information System (INIS)

    Jin, Enze; Du, Shiyu; Li, Mian; Liu, Chen; He, Shihong; He, Jian; He, Heming

    2016-01-01

    Silicon carbide has many attractive properties and the SiC/SiC composite has been considered as a promising candidate for nuclear structural materials. Up to now, a computational investigation on the properties of SiC/SiC composite varying in the presence of nuclear fission products is still missing. In this work, the influence of He atoms on the shear behavior of the SiC/SiC interphase is investigated via Molecular Dynamics simulation following our recent paper. Calculations are carried out on three dimensional models of graphite-like PyC/SiC interphase and amorphous PyC/SiC interphase with He atoms in different regions (the SiC region, the interface region and the PyC region). In the graphite-like PyC/SiC interphase, He atoms in the SiC region have little influence on the shear strength of the material, while both the shear strength and friction strength may be enhanced when they are in the PyC region. Low concentration of He atoms in the interface region of the graphite-like PyC/SiC interphase increases the shear strength, while there is a reduction of shear strength when the He concentration is high due to the switch of sliding plane. In the amorphous PyC/SiC interphase, He atoms can cause the reduction of the shear strength regardless of the regions that He atoms are located. The presence of He atoms may significantly alter the structure of SiC/SiC in the interface region. The influence of He atoms in the interface region is the most significant, leading to evident shear strength reduction of the amorphous PyC/SiC interphase with increasing He concentration. The behaviors of the interphases at different temperatures are studied as well. The dependence of the shear strengths of the two types of interphases on temperatures is studied as well. For the graphite-like PyC/SiC interphase, it is found strongly related to the regions He atoms are located. Combining these results with our previous study on pure SiC/SiC system, we expect this work may provide new insight

  12. Development and Property Evaluation of Selected HfO2-Silicon and Rare Earth-Silicon Based Bond Coats and Environmental Barrier Coating Systems for SiC/SiC Ceramic Matrix Composites

    Science.gov (United States)

    Zhu, Dongming

    2016-01-01

    Ceramic environmental barrier coatings (EBC) and SiC/SiC ceramic matrix composites (CMCs) will play a crucial role in future aircraft propulsion systems because of their ability to significantly increase engine operating temperatures, improve component durability, reduce engine weight and cooling requirements. Advanced EBC systems for SiC/SiC CMC turbine and combustor hot section components are currently being developed to meet future turbine engine emission and performance goals. One of the significant material development challenges for the high temperature CMC components is to develop prime-reliant, high strength and high temperature capable environmental barrier coating bond coat systems, since the current silicon bond coat cannot meet the advanced EBC-CMC temperature and stability requirements. In this paper, advanced NASA HfO2-Si and rare earth Si based EBC bond coat EBC systems for SiC/SiC CMC combustor and turbine airfoil applications are investigated. High temperature properties of the advanced EBC systems, including the strength, fracture toughness, creep and oxidation resistance have been studied and summarized. The advanced NASA EBC systems showed some promise to achieve 1500C temperature capability, helping enable next generation turbine engines with significantly improved engine component temperature capability and durability.

  13. Designing Si/porous-C composite with buffering voids as high capacity anode for lithium-ion batteries

    International Nuclear Information System (INIS)

    Yue, Lu; Zhang, Wenhui; Yang, Jingfeng; Zhang, Lingzhi

    2014-01-01

    A novel Si/porous-C composite with buffering voids was prepared by the co-assembly of phenol-formaldehyde resin, SiO 2 and Si nanoparticles, followed by a carbonizing process and subsequent removal of SiO 2 template. Si nanoparticle was coated with a layer of porous carbon shell with rationally designed void in between which provides the accommodating space for the volume change of Si over cycling. The as-prepared composite electrode exhibited good electrochemical performances as an anode material in lithium-ion cells, showing a stable reversible capacity of 980 mAh g −1 over 80 cycles with small capacity fade of 0.17%/cycle and high rate capability (721 mAh g −1 at 2000 mA g −1 )

  14. Electrical properties of SiO{sub 2}/SiC interfaces on 2°-off axis 4H-SiC epilayers

    Energy Technology Data Exchange (ETDEWEB)

    Vivona, M., E-mail: marilena.vivona@imm.cnr.it [CNR-IMM, Strada VIII, n. 5 – Zona Industriale, I-95121 Catania (Italy); Fiorenza, P. [CNR-IMM, Strada VIII, n. 5 – Zona Industriale, I-95121 Catania (Italy); Sledziewski, T.; Krieger, M. [Friedrich-Alexander-University (FAU) Erlangen-Nuremberg, Department of Physics, Staudtstrasse 7/Bld. A3, D-91058 Erlangen (Germany); Chassagne, T.; Zielinski, M. [NOVASiC, Savoie Technolac, BP267, F-73375 Le Bourget-du-Lac Cedex (France); Roccaforte, F. [CNR-IMM, Strada VIII, n. 5 – Zona Industriale, I-95121 Catania (Italy)

    2016-02-28

    Graphical abstract: - Highlights: • Processing and electrical characterization of MOS capacitors fabricated on 4H-SiC epilayers grown on 2°-off axis heavily doped substrates. • Excellent characteristics of the SiO{sub 2}/4H-SiC interface in terms of flatness, interface state density and oxide reliability. • Electrical behavior of the MOS devices comparable with that obtained for the state-of-the-art of 4°-off axis 4H-SiC material. • Demonstration of the maturity of the 2°-off axis material for application in 4H-SiC MOSFET device technology. - Abstract: In this paper, the electrical properties of the SiO{sub 2}/SiC interface on silicon carbide (4H-SiC) epilayers grown on 2°-off axis substrates were studied. After epilayer growth, chemical mechanical polishing (CMP) allowed to obtain an atomically flat surface with a roughness of 0.14 nm. Metal-oxide-semiconductor (MOS) capacitors, fabricated on this surface, showed an interface state density of ∼1 × 10{sup 12} eV{sup −1} cm{sup −2} below the conduction band, a value which is comparable to the standard 4°-off-axis material commonly used for 4H-SiC MOS-based device fabrication. Moreover, the Fowler–Nordheim and time-zero-dielectric breakdown analyses confirmed an almost ideal behavior of the interface. The results demonstrate the maturity of the 2°-off axis material for 4H-SiC MOSFET device fabrication.

  15. Effect of Si3N4 Addition on Oxidation Resistance of ZrB2-SiC Composites

    Directory of Open Access Journals (Sweden)

    Manab Mallik

    2017-06-01

    Full Text Available The oxidation behavior of ZrB2-20 vol % SiC and ZrB2-20 vol % SiC-5 vol % Si3N4 composites prepared by hot-pressing and subjected to isothermal exposure at 1200 or 1300 °C for durations of 24 or 100 h in air, as well as cyclic exposure at 1300 °C for 24 h, have been investigated. The oxidation resistance of the ZrB2-20 vol % SiC composite has been found to improve by around 20%–25% with addition of 5 vol % Si3N4 during isothermal or cyclic exposures at 1200 or 1300 °C. This improvement in oxidation resistance has been attributed to the formation of higher amounts of SiO2 and Si2N2O, as well as a greater amount of continuity in the oxide scale, because these phases assist in closing the pores and lower the severity of cracking by exhibiting self-healing type behavior. For both the composites, the mass changes are found to be higher during cyclic exposure at 1300 °C by about 2 times compared to that under isothermal conditions.

  16. Al-Si/B{sub 4}C composite coatings on Al-Si substrate by plasma spray technique

    Energy Technology Data Exchange (ETDEWEB)

    Sarikaya, Ozkan [Sakarya University, Faculty of Engineering, Department of Mechanical Engineering, Esentepe Campus, Sakarya 54187 (Turkey); Anik, Selahaddin [Sakarya University, Faculty of Engineering, Department of Mechanical Engineering, Esentepe Campus, Sakarya 54187 (Turkey); Aslanlar, Salim [Sakarya University, Faculty of Technical Education, Department of Mechanical Engineering, Esentepe Campus, Sakarya 54187 (Turkey); Cem Okumus, S. [Sakarya University, Faculty of Engineering, Department of Metallurgical and Materials Engineering, Esentepe Campus, Sakarya 54187 (Turkey); Celik, Erdal [Dokuz Eylul University, Engineering Faculty, Department of Metallurgical and Materials Engineering, Buca, Izmir 35160 (Turkey)]. E-mail: erdal.celik@deu.edu.tr

    2007-07-01

    Plasma-sprayed coatings of Al-Si/B{sub 4}C have been prepared on Al-Si piston alloys for diesel engine motors. The Al-Si/B{sub 4}C composite powders including 5-25 wt% B{sub 4}C were prepared by mixing and ball-milling processes. These powders were deposited on Al-Si substrate using an atmospheric plasma spray technique. The coatings have been characterised with respect to phase composition, microstructure, microhardness, bond strength and thermal expansion. It was found that Al, Si, B{sub 4}C and Al{sub 2}O{sub 3} phases were determined in the coatings with approximately 600 {mu}m thick by using X-ray diffraction analysis. Scanning electron microscope observation revealed that boron carbide particles were uniformly distributed in composite coatings and B{sub 4}C particles were fully wetted by Al-Si alloy. Also, no reaction products were observed in Al-Si/B{sub 4}C composite coatings. It was found that surface roughness, porosity, bond strength and thermal expansion coefficient of composite coatings decreased with increasing fraction of the boron carbide particle. It was demonstrated that the higher the B{sub 4}C content, the higher the hardness of coatings because the hardness of B{sub 4}C is higher than that of Al-Si.

  17. Residual Stress Measurement of SiC tile/Al7075 Hybrid Composites by Neutron Diffraction

    Energy Technology Data Exchange (ETDEWEB)

    Park, Jong Bok; Lee, Jun Ho; Hong, Soon Hyung; Ryu, Ho Jin [KAIST, Daejeon (Korea, Republic of); Lee, Sang Bok; Lee, Sang Kwan [Korea Institute of Materials Science, Changwon (Korea, Republic of); Muslihd, M. Rifai [Center for Advanced Materials Science and Technology, Tangerang (India)

    2016-05-15

    In this research, SiC which has low density, high compressive strength, and high elastic modulus was used to fabricate the armor plate. In addition, Al which has low density and high toughness was used for a metal matrix of the composites. If two materials are combined, the composite can be effective materials for light weight armor applications. However, the existence of a large difference in coefficients of thermal expansion (CTE) between SiC and Al matrix, SiC/Al composites can have residual stresses while cooled in the fabrication process. Previous research reported that residual stresses in the composites or microstructures have an effect on the fatigue life and their mechanical properties. Some researchers reported about the residual stresses in the SiCp/Al metal matrix composites by numerical simulation systems, X-ray diffraction, and destructive methods. In order to analyze the residual stress of SiC/Al composites, the neutron diffraction as the non-destructive method was performed in this research. The 50 vol.% SiC{sub p}/Al7075 composites and SiC tile inserted 50 vol.% SiC{sub p}/Al7075 hybrid composites were measured to analyze the residual stress of Al (111) and SiC (111). Both samples had the tensile residual stresses in the Al (111) and the compressive residual stresses in the SiC (111) due to the difference in CTE.

  18. Effect of SiC particles on microarc oxidation process of magnesium matrix composites

    International Nuclear Information System (INIS)

    Wang, Y.Q.; Wang, X.J.; Gong, W.X.; Wu, K.; Wang, F.H.

    2013-01-01

    SiC particles are an important reinforced phase in metal matrix composites. Their effect on the microarc oxidation (MAO, also named plasma electrolytic oxidation-PEO) process of SiC p /AZ91 Mg matrix composites (MMCs) was studied and the mechanism was revealed. The corrosion resistance of MAO coating was also investigated. Voltage–time curves during MAO were recorded to study the barrier film status on the composites. Scanning electron microscopy was used to characterize the existing state of SiC particles in MAO. Energy dispersive X-ray spectrometry and X-ray photoelectron spectroscopy were used to analyze the chemical composition of the coating. Corrosion resistance of the bare and coated composites was evaluated by potentiodynamic polarization curves in 3.5% NaCl solution. Results showed that the integrality and electrical insulation properties of the barrier film on the composites were destroyed by the SiC particles. Consequently, the sparking discharge at the early stage of MAO was inhibited, and the growth efficiency of the MAO coating decreased with the increase in the volume fraction of SiC particles. SiC particles did not exist stably during MAO; they were oxidized or partially oxidized into SiO 2 before the overall sparking discharge. The transformation from semi-conductive SiC to insulating SiO 2 by oxidation restrained the current leakage at the original SiC positions and then promoted sparking discharge and coating growth. The corrosion current density of SiC p /AZ91 MMCs was reduced by two orders of magnitude after MAO treatment. However, the corrosion resistances of the coated composites were lower than that of the coated alloy.

  19. Radiation effects and micromechanics of SiC/SiC composites (December 1, 1990--November 14, 1993) and modeling the mechanical behavior of SiC/SiC composites in fusion environments (November 15, 1993--November 14, 1996). Final report, December 1, 1990--November 14, 1996

    International Nuclear Information System (INIS)

    Ghoniem, N.M.

    1997-01-01

    The development of Silicon Carbide composite materials for structural applications in fusion energy systems is mainly motivated by the prospect that fusion power systems utilizing the material will have a much more favorable environmental impact. The research team at UCLA was the first to identify the potential advantages of SiC/SiC composite materials through early System Studies. Consequently, two three-year term grants have been awarded to the team, in order to focus on modeling the effects of irradiation on key properties that have been recognized by the community as fundamental to the successful development of the composite. Two main tasks, which are further subdivided into several subtasks each, have been pursued during the course of research during the period: December 1990 through November 1996. The first task deals with modeling the effects of irradiation on the dimensional stability of SiC. To achieve this goal, a substantial effort was launched for modeling the evolution of the microstructure under irradiation. Rate and Fokker-Planck theories have been advanced to model the complex multi-component system of SiC under irradiation. The effort has resulted in a deeper understanding of the interaction between displacement damage components, and transmutant helium gas atoms. Utilizing the methods of Molecular Dynamics (MD) and Monte Carlo (MC), the energetics of defects and the basic displacement mechanisms in SiC have been fully delineated. An advanced Fokker-Planck approach was formulated to determine the phase content and size distribution of damage microstructure in SiC. Finally, a rate theory model was developed and successfully applied to the experimental swelling data on SiC. In the second task, the authors investigated the mechanical behavior of SiC/SiC composites under the irradiation conditions of fusion reactors. The main focus of the second task has been on developing models for the micro-mechanics of cracks in the fiber reinforced matrix of the

  20. Non-stoichiometric mullites from Al2O3-SiO2-ZrO2 amorphous materials by rapid quenching

    International Nuclear Information System (INIS)

    Yoshimura, M.; Hanaue, Y.; Somiya, S.

    1990-01-01

    In order to study the formation of zirconia dispersed mullite ceramics from homogeneous starting materials hot-pressing and heat-treatments have been carried out for rapidly quenched amorphous materials with 0 to 20 wt% ZrO 2 mullite compositions. These amorphous materials crystallized directly to mullite for 0-10 wt% ZrO 2 samples or mullite + t-ZrO 2 for 20 wt% ZrO 2 at about 970 degrees C. An A1 2 O 3 - rich composition (82 wt% A1 2 O 3 ) and also a significant solid solubility of ZrO 2 (>10 wt%) were estimated for these mullites by XRD studies. Amorphous speres of 10 nm which were considered to be SiO 2 - rich phase were produced by a phase separation in mullite grains

  1. Ion irradiation effects on the matrix phase of SiCf/SiC composites prepared by the whisker growing assisted CVI process

    International Nuclear Information System (INIS)

    Park, Kyeong Hwan; Park, Ji Yeon; Kang, Suk Min; Kim, Weon Ju; Jung, Choong Hwan; Ryu, Woo Seog

    2005-01-01

    SiC f /SiC composites are one of promising candidates for structural material of the next generation energy system such as GFR and fusion reactors. A number of fabrication methods have been studied for obtaining an outstanding SiC f /SiC composite with a high density, high crystallinity and purity. SiC f /SiC composites consisted of whisker-reinforced matrix have a great potential at the viewpoint both of the fabrication process and the mechanical properties. SiC whiskers formed between SiC fibers improve the densification of SiC matrix during CVI process. In addition, the reinforced whiskers would be likely to enhance the mechanical properties of matrix and SiC f /SiC composite. While there has been significant developmental work on manufacturing the SiC f /SiC composite by the whisker growing assisted CVI process, detailed understanding of what effects the complex in the operating conditions combined with realistic materials property data is not adequately understood. Especially, its irradiation effects are even less clear and not well understood. A method of charged-particle irradiation is the most important R and D topics for simulating the core conditions of the advanced nuclear systems. Many studies on radiation effects of SiC and SiC f /SiC composites using a method of ion irradiation have in progress for R and D of the advanced nuclear systems. In this present work, changes of the mechanical property of SiC whisker-reinforced matrix in SiC f /SiC composite were evaluated by means of the depth sensing indentation method before and after chargedparticle irradiation

  2. Reaction mechanisms at 4H-SiC/SiO2 interface during wet SiC oxidation

    Science.gov (United States)

    Akiyama, Toru; Hori, Shinsuke; Nakamura, Kohji; Ito, Tomonori; Kageshima, Hiroyuki; Uematsu, Masashi; Shiraishi, Kenji

    2018-04-01

    The reaction processes at the interface between SiC with 4H structure (4H-SiC) and SiO2 during wet oxidation are investigated by electronic structure calculations within the density functional theory. Our calculations for 4H-SiC/SiO2 interfaces with various orientations demonstrate characteristic features of the reaction depending on the crystal orientation of SiC: On the Si-face, the H2O molecule is stable in SiO2 and hardly reacts with the SiC substrate, while the O atom of H2O can form Si-O bonds at the C-face interface. Two OH groups are found to be at least necessary for forming new Si-O bonds at the Si-face interface, indicating that the oxidation rate on the Si-face is very low compared with that on the C-face. On the other hand, both the H2O molecule and the OH group are incorporated into the C-face interface, and the energy barrier for OH is similar to that for H2O. By comparing the calculated energy barriers for these reactants with the activation energies of oxide growth rate, we suggest the orientation-dependent rate-limiting processes during wet SiC oxidation.

  3. Hot pressing of B4C/SiC composites

    International Nuclear Information System (INIS)

    Sahin, F.C.; Turhan, E.; Yesilcubuk, S.A.; Addemir, O.

    2005-01-01

    B 4 C/SiC ceramic composites containing 10-20-30 vol % SiC were prepared by hot pressing method. The effect of SiC addition and hot pressing temperature on sintering behaviour and mechanical properties of hot pressed composites were investigated. Microstructures of hot pressed samples were examined by SEM technique. Three different temperatures (2100 deg. C, 2200 deg. C and 2250 deg. C) were used to optimize hot pressing temperature applying 100 MPa pressure under argon atmosphere during the sintering procedure. The highest relative density of 98.44 % was obtained by hot pressing at 2250 deg. C. However, bending strengths of B 4 C/SiC composite samples were lower than monolithic B 4 C in all experimental conditions. (authors)

  4. Ablation behavior and mechanism of 3D Cf/ZrC-SiC composites in a plasma wind tunnel environment

    Directory of Open Access Journals (Sweden)

    Qinggang Li

    2015-12-01

    Full Text Available Three-dimensional needle-like Cf/ZrC-SiC composites were successfully fabricated by polymer infiltration and pyrolysis combined with ZrC precursor impregnation. The ablation properties of the composites were tested in a plasma wind tunnel environment at different temperatures and different times. The microstructure and morphology of the composites were examined after ablation by scanning electron microscopy, and their composition was confirmed by energy dispersive spectroscopy. The composites exhibited good configurational stability with a surface temperature of greater than 2273 K over a 300–1000 s period. The formation of ZrSiO4 and SiO2 melts on the surface of the 3D Cf/ZrC-SiC composites contributed significantly to improvement in their ablation properties. However, these composites exhibited serious ablation when the temperature was increased to 2800 K. The 3D Cf/ZrC-SiC composites obtained after ablation showed three different layers attributed to the temperature and pressure gradients: the ablation central region, the ablation transition region, and the unablation region.

  5. Thermal fatigue behavior of C/C composites modified by SiC-MoSi2-CrSi2 coating

    International Nuclear Information System (INIS)

    Chu Yanhui; Fu Qiangang; Li Hejun; Li Kezhi

    2011-01-01

    Highlights: → The low-density C/C composites were modified by SiC-MoSi 2 -CrSi 2 multiphase coating by pack cementation. → The thermal fatigue behavior of the modified C/C composites was studied after undergoing thermal cycling for 20 times under the different environments. → The decrease of the flexural strength of the modified C/C composites during thermal cycle in air was primarily attributed to the partial oxidation of the modified C/C samples. - Abstract: Carbon/carbon (C/C) composites were modified by SiC-MoSi 2 -CrSi 2 multiphase coating by pack cementation, and their thermal fatigue behavior under thermal cycling in Ar and air environments was investigated. The modified C/C composites were characterized by scanning electron microscopy and X-ray diffraction. Results of tests show that, after 20-time thermal cycles between 1773 K and room temperature in Ar environment, the flexural strength of modified C/C samples decreased lightly and the percentage of remaining strength was 94.92%. While, after thermal cycling between 1773 K and room temperature in air for 20 times, the weight loss of modified C/C samples was 5.1%, and the flexural strength of the modified C/C samples reduced obviously and the percentage of remaining strength was only 75.22%. The fracture mode of modified C/C samples changed from a brittle behavior to a pseudo-plastic one as the service environment transformed from Ar to air. The decrease of the flexural strength during thermal cycle in air was primarily attributed to the partial oxidation of modified C/C samples.

  6. Influence of SiO2 Addition on Properties of PTFE/TiO2 Microwave Composites

    Science.gov (United States)

    Yuan, Ying; Wang, Jie; Yao, Minghao; Tang, Bin; Li, Enzhu; Zhang, Shuren

    2018-01-01

    Composite substrates for microwave circuit applications have been fabricated by filling polytetrafluoroethylene (PTFE) polymer matrix with ceramic powder consisting of rutile TiO2 ( D 50 ≈ 5 μm) partially substituted with fused amorphous SiO2 ( D 50 ≈ 8 μm) with composition x vol.% SiO2 + (50 - x) vol.% TiO2 ( x = 0, 3, 6, 9, 12), and the effects of SiO2 addition on characteristics such as the density, moisture absorption, microwave dielectric properties, and thermal properties systematically investigated. The results show that the filler was well distributed throughout the matrix. High dielectric constant ( ɛ r > 7.19) and extremely low moisture absorption (ceramic particles served as barriers and improved the thermal stability of the PTFE polymer, retarding its decomposition. The temperature coefficient of dielectric constant ( τ ɛ ) of the composites shifted toward the positive direction (from - 309 ppm/°C to - 179 ppm/°C) as the SiO2 content was increased, while the coefficient of thermal expansion remained almost unchanged (˜ 35 ppm/°C).

  7. Synergistic effect of displacement damage, helium and hydrogen on microstructural change of SiC/SiC composites fabricated by reaction bonding process

    Energy Technology Data Exchange (ETDEWEB)

    Taguchi, T.; Igawa, N.; Wakai, E.; Jitsukawa, S. [Japan Atomic Energy Agency, Naga-gun, Ibaraki-ken (Japan); Hasegawa, A. [Tohoku Univ., Dept. of Quantum Science and Energy Engr., Sendai (Japan)

    2007-07-01

    Full text of publication follows: Continuous silicon carbide (SiC) fiber reinforced SiC matrix (SiC/SiC) composites are known to be attractive candidate materials for first wall and blanket components in fusion reactors. In the fusion environment, helium and hydrogen are produced and helium bubbles can be formed in the SiC by irradiation of 14-MeV neutrons. Authors reported the synergistic effect of helium and hydrogen as transmutation products on swelling behavior and microstructural change of the SiC/SiC composites fabricated by chemical vapor infiltration (CVI) process. Authors also reported about the fabrication of high thermal conductive SiC/SiC composites by reaction bonding (RB) process. The matrix fabricated by RB process has different microstructures such as bigger grain size of SiC and including Si phase as second phase from that by CVI process. It is, therefore, investigated the synergistic effect of displacement damage, helium and hydrogen as transmutation products on the microstructure of SiC/SiC composite by RB process in this study. The SiC/SiC composites by RB process were irradiated by the simultaneous triple ion irradiation (Si{sup 2+}, He{sup +} and H{sup +}) at 800 and 1000 deg. C. The displacement damage was induced by 6.0 MeV Si{sup 2+} ion irradiation up to 10 dpa. The microstructures of irradiated SiC/SiC composites by RB process were observed by TEM. The double layer of carbon and SiC as interphase between fiber and matrix by a chemical vapor deposition (CVD) was coated on SiC fibers in the SiC/SiC composites by RB process. The TEM observation revealed that He bubbles were formed both in the matrix by RB and SiC interphase by CVD process. Almost all He bubbles were formed at the grain boundary in SiC interphase by CVD process. On the other hand, He bubbles were formed both at the grain boundary and in Si grain of the matrix by RB process. The average size of He bubbles in the matrix by RB was smaller than that in SiC interphase by CVD

  8. Mechanical performance of Hi-Nicalon/CVI-SiC composites with multilayer SiC/C interfaces

    Energy Technology Data Exchange (ETDEWEB)

    Halverson, H.G.; Carter, R.H.; Curtin, W.A. [Virginia Polytechnic Inst. and State Univ., Blacksburg, VA (United States). Dept. of Engineering Science and Mechanics

    1997-12-01

    The mechanical properties and interfacial characteristics of new SiC/SiC ceramic composites, composed of Hi-Nicalon fibers in a CVI-SiC matrix and having a variety of multilayer SiC/C coatings between the fibers and the matrix, are studied in detail to elucidate the roles of the coatings and fibers. Axial tension tests and unload/reload hysteresis loop measurements are performed to determine mechanical performance. All materials exhibit the strong and tough behavior characteristic of good ceramic composites, with all multilayer variants performing quite similarly. SEM microscopy demonstrates that matrix cracks penetrate through the multilayers and debond at the fiber/inner-coating interface. Analysis of the hysteretic behavior leads to values for interfacial sliding resistance {tau} {approx} 11 ksi and interfacial toughness {Gamma}{sub i} {approx} 2 J/m{sup 2} that are nearly independent of multilayer structure, and are similar to values obtained for standard pyrolitic carbon interfaces. These results all indicate debonding at the fiber surface for all coating structures, which provides a common roughness, {tau}, and {Gamma}{sub i}. Analysis of fiber fracture mirrors provides an estimate of the in-situ strength of the fibers and demonstrates the high strength retention of the Hi-Nicalon fibers. The in-situ fiber strengths are combined with the measured pullout lengths to obtain an independent determination of {tau} = 8.5 ksi that agrees well with the value found from the hysteretic behavior. Predictions of composite strength using the derived fiber strengths agree well with the measured value although the predicted failure strain is too large. This study demonstrates that Hi-Nicalon fiber/CVI-SiC composites perform well for a wide range of multilayer interface structures and that the interfaces present relatively high values of {tau} and {Gamma}{sub i}, both of which are beneficial to strength and toughness. The small carbon layer thicknesses in these multilayer

  9. The corrosion behavior of CVI SiC matrix in SiC{sub f}/SiC composites under molten fluoride salt environment

    Energy Technology Data Exchange (ETDEWEB)

    Wang, Hongda [Structural Ceramics and Composites Engineering Research Center, Shanghai Institute of Ceramics, Chinese Academy of Sciences, Shanghai 200050 (China); State Key Laboratory of High Performance Ceramics and Superfine Microstructure, Shanghai Institute of Ceramics, Chinese Academy of Sciences, Shanghai 200050 (China); School of Graduate, University of Chinese Academy of Sciences, Beijing 100049 (China); Feng, Qian [Analysis and Testing Center, Donghua University, Shanghai 201600 (China); Wang, Zhen, E-mail: jeff@mail.sic.ac.cn [Structural Ceramics and Composites Engineering Research Center, Shanghai Institute of Ceramics, Chinese Academy of Sciences, Shanghai 200050 (China); State Key Laboratory of High Performance Ceramics and Superfine Microstructure, Shanghai Institute of Ceramics, Chinese Academy of Sciences, Shanghai 200050 (China); Zhou, Haijun; Kan, Yanmei; Hu, Jianbao [Structural Ceramics and Composites Engineering Research Center, Shanghai Institute of Ceramics, Chinese Academy of Sciences, Shanghai 200050 (China); State Key Laboratory of High Performance Ceramics and Superfine Microstructure, Shanghai Institute of Ceramics, Chinese Academy of Sciences, Shanghai 200050 (China); Dong, Shaoming, E-mail: smdong@mail.sic.ac.cn [Structural Ceramics and Composites Engineering Research Center, Shanghai Institute of Ceramics, Chinese Academy of Sciences, Shanghai 200050 (China); State Key Laboratory of High Performance Ceramics and Superfine Microstructure, Shanghai Institute of Ceramics, Chinese Academy of Sciences, Shanghai 200050 (China)

    2017-04-15

    High temperature corrosion behavior and microstructural evolution of designed chemical-vapor-infiltrated SiC matrix in SiC fiber reinforced SiC ceramic matrix composites in 46.5LiF-11.5NaF-42.0KF (mol. %) eutectic salt at 800 °C for various corrosion time was studied. Worse damage was observed as extending the exposure time, with the mass loss ratio increasing from 0.716 wt. % for 50 h to 5.914 wt. % for 500 h. The mass loss rate showed a trend of first decrease and then increase with the extended corrosion exposure. Compared with the near-stoichiometric SiC matrix layers, the O-contained boundaries between deposited matrix layers and the designed Si-rich SiC matrix layers were much less corrosion resistant and preferentially corroded. Liner relationship between the mass loss ratio and the corrosion time obtained from 50 h to 300 h indicated that the corrosion action was reaction-control process. Further corrosion would lead to matrix layer exfoliation and higher mass loss ratio.

  10. Temperature Dependence of Electrical Resistance of Woven Melt-Infiltrated SiCf/SiC Ceramic Matrix Composites

    Science.gov (United States)

    Appleby, Matthew P.; Morscher, Gregory N.; Zhu, Dongming

    2016-01-01

    Recent studies have successfully shown the use of electrical resistance (ER)measurements to monitor room temperature damage accumulation in SiC fiber reinforced SiC matrix composites (SiCf/SiC) Ceramic Matrix Composites (CMCs). In order to determine the feasibility of resistance monitoring at elevated temperatures, the present work investigates the temperature dependent electrical response of various MI (Melt Infiltrated)-CVI (Chemical Vapor Infiltrated) SiC/SiC composites containing Hi-Nicalon Type S, Tyranno ZMI and SA reinforcing fibers. Test were conducted using a commercially available isothermal testing apparatus as well as a novel, laser-based heating approach developed to more accurately simulate thermomechanical testing of CMCs. Secondly, a post-test inspection technique is demonstrated to show the effect of high-temperature exposure on electrical properties. Analysis was performed to determine the respective contribution of the fiber and matrix to the overall composite conductivity at elevated temperatures. It was concluded that because the silicon-rich matrix material dominates the electrical response at high temperature, ER monitoring would continue to be a feasible method for monitoring stress dependent matrix cracking of melt-infiltrated SiC/SiC composites under high temperature mechanical testing conditions. Finally, the effect of thermal gradients generated during localized heating of tensile coupons on overall electrical response of the composite is determined.

  11. Fabrication of SiC Composites with Synergistic Toughening of Carbon Whisker and In Situ 3C-SiC Nanowire

    Directory of Open Access Journals (Sweden)

    Zhang Yunlong

    2016-01-01

    Full Text Available The SiC composites with synergistic toughening of carbon whisker and in situ 3C-SiC nanowire have been fabricated by hot press sinter technology and annealed treatment technology. Effect of annealed time on the morphology of SiC nanowires and mechanical properties of the Cw/SiC composites was surveyed in detail. The appropriate annealed time improved mechanical properties of the Cw/SiC composites. The synergistic effect of carbon whisker and SiC nanowire can improve the fracture toughness for Cw/SiC composites. The vapor-liquid-solid growth (VLS mechanism was proposed. TEM photo showed that 3C-SiC nanowire can be obtained with preferential growth plane ({111}, which corresponded to interplanar spacing about 0.25 nm.

  12. Dielectric Properties of SiCf/PyC/SiC Composites After Oxidation

    Institute of Scientific and Technical Information of China (English)

    SONG Huihui; ZHOU Wancheng; LUO Fa; QING Yuchang; CHEN Malin; LI Zhimin

    2016-01-01

    In this paper, the SiC fiber-reinforced SiC matrix composites with a 0.15mm thick pyrocarbon interphase (notedas SiCf/PyC/SiC) were prepared by chemical vapor infiltration (CVI). The SiCf/PyC/SiC were oxidized in air at 950℃ for 50h. The dielectric properties after this high temperature oxidation were investigated in X-band from room temperature (RT) to 700℃. Results suggested that:e' of the SiCf/PyC/SiC after oxidation increased at first then de-creased with temperature elevating;e" increased with temperature raising in the temperature range studied.

  13. Environmental Barrier Coating Development for SiC/SiC Ceramic Matrix Composites: Recent Advances and Future Directions

    Science.gov (United States)

    Zhu, Dongming

    2016-01-01

    This presentation briefly reviews the SiC/SiC major environmental and environment-fatigue degradations encountered in simulated turbine combustion environments, and thus NASA environmental barrier coating system evolution for protecting the SiC/SiC Ceramic Matrix Composites for meeting the engine performance requirements. The presentation will review several generations of NASA EBC materials systems, EBC-CMC component system technologies for SiC/SiC ceramic matrix composite combustors and turbine airfoils, highlighting the temperature capability and durability improvements in simulated engine high heat flux, high pressure, high velocity, and with mechanical creep and fatigue loading conditions. This paper will also focus on the performance requirements and design considerations of environmental barrier coatings for next generation turbine engine applications. The current development emphasis is placed on advanced NASA candidate environmental barrier coating systems for SiC/SiC CMCs, their performance benefits and design limitations in long-term operation and combustion environments. The efforts have been also directed to developing prime-reliant, self-healing 2700F EBC bond coat; and high stability, lower thermal conductivity, and durable EBC top coats. Major technical barriers in developing environmental barrier coating systems, the coating integrations with next generation CMCs having the improved environmental stability, erosion-impact resistance, and long-term fatigue-environment system durability performance will be described. The research and development opportunities for turbine engine environmental barrier coating systems by utilizing improved compositions, state-of-the-art processing methods, and simulated environment testing and durability modeling will be briefly discussed.

  14. Phase relations in the SiC-Al2O3-Pr2O3 system

    International Nuclear Information System (INIS)

    Pan, W.; Wu, L.; Jiang, Y.; Huang, Z.

    2016-01-01

    Phase relations in the Si-Al-Pr-O-C system, including the SiC-Al 2 O 3 -Pr 2 O 3 , the Al 2 O 3 -Pr 2 O 3 -SiO 2 and the SiC-Al 2 O 3 -Pr 2 O 3 -SiO 2 subsystems, were determined by means of XRD phase analysis of solid-state-reacted samples fabricated by using SiC, Al 2 O 3 , Pr 2 O 3 and SiO 2 powders as the starting materials. Subsolidus phase diagrams of the systems were presented. Two Pr-aluminates, namely PrAlO 3 (PrAP) and PrAl 11 O 18 (β(Pr) β-Al 2 O 3 type) were formed in the SiC-Al 2 O 3 -Pr 2 O 3 system. SiC was compatible with both of them. Pr-silicates of Pr 2 SiO 5 , Pr 2 Si 2 O 7 and Pr 9.33 Si 6 O 26 (H(Pr) apatite type) were formed owing to presence of SiO 2 impurity in the SiC powder. The presence of the SiO 2 extended the ternary system of SiC-Al 2 O 3 -Pr 2 O 3 into a quaternary system of SiC-Al 2 O 3 -SiO 2 -Pr 2 O 3 (Si-Al-Pr-O-C). SiC was compatible with Al 2 O 3 , Pr 2 O 3 and the Pr-silicates. The effect of SiO 2 on the phase relations and liquid phase sintering of SiC ceramics was discussed.

  15. Combined Thermomechanical and Environmental Durability of Environmental Barrier Coating Systems on SiC/SiC Ceramic Matrix Composites

    Science.gov (United States)

    Zhu, Dongming; Harder, Bryan; Bhatt, Ramakrishna

    2016-01-01

    Environmental barrier coatings (EBCs) and SiC/SiC ceramic matrix composites (CMCs) will play a crucial role in next generation turbine engines for hot-section component applications. The development of prime-reliant environmental barrier coatings is essential to the EBC-CMC system durability, ensuring the successful implementations of the high temperature and lightweight engine component technologies for engine applications.This paper will emphasize recent NASA environmental barrier coating and CMC developments for SiC/SiC turbine airfoil components, utilizing advanced coating compositions and processing methods. The emphasis has been particularly placed on thermomechanical and environment durability evaluations of EBC-CMC systems. We have also addressed the integration of the EBCs with advanced SiC/SiC CMCs, and studied the effects of combustion environments and Calcium-Magnesium-Alumino-Silicate (CMAS) deposits on the durability of the EBC-CMC systems under thermal gradient and mechanical loading conditions. Advanced environmental barrier coating systems, including multicomponent rare earth silicate EBCs and HfO2-Si based bond coats, will be discussed for the performance improvements to achieve better temperature capability and CMAS resistance for future engine operating conditions.

  16. Stability analysis of SiO2/SiC multilayer coatings

    International Nuclear Information System (INIS)

    Fu Zhiqiang; Jean-Charles, R.

    2006-01-01

    The stability behaviours of SiC coatings and SiO 2 /SiC coatings in helium with little impurities are studied by HSC Chemistry 4.1, the software for analysis of Chemical reaction and equilibrium in multi-component complex system. It is found that in helium with a low partial pressure of oxidative impurities under different total pressure, the key influence factor controlling T cp of SiC depends is the partial pressure of oxidative impurities; T cp of SiC increases with the partial pressure of oxidative impurities. In helium with a low partial pressure of different impurities, the key influence factor of T cs of SiO 2 are both the partial pressure of impurities and the amount of impurities for l mol SiO 2 ; T cs of SiO 2 increases with the partial pressure of oxidative impurities at the same amount of the impurities for 1 mol SiO 2 while it decreases with the amount of the impurities for 1 mm SiO 2 at the same partial pressure of the impurities. The influence of other impurities on T cp of SiC in He-O 2 is studied and it is found that CO 2 , H 2 O and N-2 increase T cp of SiC in He-O 2 while H 2 , CO and CH 4 decrease T cp of SiC He-O 2 . When there exist both oxidative impurities and reductive impurities, their effect on T cs of SiO 2 can be suppressed by the other. In HTR-10 operation atmosphere, SiO 2 /SiC coatings can keep stable status at higher temperature than SiC coatings, so SiO 2 /SiC coatings is more suitable to improve the oxidation resistance of graphite in HTR-10 operation atmosphere compared with SiC coatings. (authors)

  17. Effect of simultaneous ion irradiation on microstructural change of SiC/SiC composites at high temperature

    International Nuclear Information System (INIS)

    Taguchi, T.; Wakai, E.; Igawa, N.; Nogami, S.; Snead, L.L.; Hasegawa, A.; Jitsukawa, S.

    2002-01-01

    The effect of simultaneous triple ion irradiation of He, H and Si on microstructural evolution of two kinds of SiC/SiC composites (HNS composite (using Hi-Nicalon type S SiC fiber) and TSA composite (using Tyranno SA SiC fiber)) at 1000 deg. C has been investigated. The microstructure observations of SiC/SiC composites irradiated to 10 dpa were examined by transmission electron microscopy. He bubbles were hardly formed in matrix of TSA composite, but many helium bubbles and some cracks were observed at grain boundaries of matrix of HNS composite. He bubbles and cracks were not, on the other hand, observed in the both fiber fabrics of HNS and TSA composites. Debonding between fiber and carbon layer following irradiation region was not observed in the both composites. Under these irradiation conditions, TSA composite showed the better microstructural stability against ion beams irradiation than one of HNS composite

  18. Influence of SiC coating thickness on mechanical properties of SiCf/SiC composite

    Science.gov (United States)

    Yu, Haijiao; Zhou, Xingui; Zhang, Wei; Peng, Huaxin; Zhang, Changrui

    2013-11-01

    Silicon carbide (SiC) coatings with varying thickness (ranging from 0.14 μm to 2.67 μm) were deposited onto the surfaces of Type KD-I SiC fibres with native carbonaceous surface using chemical vapour deposition (CVD) process. Then, two dimensional SiC fibre reinforced SiC matrix (2D SiCf/SiC) composites were fabricated using polymer infiltration and pyrolysis (PIP) process. Influences of the fibre coating thickness on mechanical properties of SiC fibre and SiCf/SiC composite were investigated using single-filament test and three-point bending test. The results indicated that flexural strength of the composites initially increased with the increasing CVD SiC coating thickness and reached a peak value of 363 MPa at the coating thickness of 0.34 μm. Further increase in the coating thickness led to a rapid decrease in the flexural strength of the composites. The bending modulus of composites showed a monotonic increase with increasing coating thickness. A chemical attack of hydrogen or other ions (e.g. a C-H group) on the surface of SiC fibres during the coating process, owing to the formation of volatile hydrogen, lead to an increment of the surface defects of the fibres. This was confirmed by Wang et al. [35] in their work on the SiC coating of the carbon fibre. In the present study, the existing ˜30 nm carbon on the surface of KD-I fibre [36] made the fibre easy to be attacked. Deposition of non-stoichiometric SiC, causing a decrease in strength. During the CVD process, a small amount of free silicon or carbon always existed [35]. The existence of free silicon, either disordered the structure of SiC and formed a new source of cracks or attacked the carbon on fibre surface resulting in properties degeneration of the KD-I fibre. The effect of residual stress. The different thermal expansion coefficient between KD-I SiC fibre and CVD SiC coating, which are 3 × 10-6 K-1 (RT ˜ 1000 °C) and 4.6 × 10-6 K-1 (RT ˜ 1000 °C), respectively, could cause residual stress

  19. TaxHf1−xB2–SiC multiphase oxidation protective coating for SiC-coated carbon/carbon composites

    International Nuclear Information System (INIS)

    Ren, Xuanru; Li, Hejun; Fu, Qiangang; Li, Kezhi

    2014-01-01

    Highlights: • Ta x Hf 1−x B 2 –SiC coating was prepared on SiC coated C/C by in-situ reaction method. • TaB 2 and HfB 2 were introduced in the form of solid solution Ta x Hf 1−x B 2 . • The coating could protect C/C for 1480 h with only 0.57% mass loss at 1773 K in air. • Oxidation layer consists of out Ta–Si–O compound layer and inner SiO 2 glass layer. • Ta–Si–O compound silicate layer presents a better stability than SiO 2 glass layer. - Abstract: A Ta x Hf 1−x B 2 –SiC coating was prepared by in-situ reaction method on SiC coated C/C composites. Ta x Hf 1−x B 2 phase is the form of solid solution between TaB 2 and HfB 2 . Isothermal oxidation behavior at 1773 K and ablation behavior of the coated C/C were tested. Ta x Hf 1−x B 2 –SiC/SiC coating could protect the C/C from oxidation at 1773 K for 1480 h and ablation above 2200 K for 40 s. During oxidation, oxides of Ta and Hf atoms exist as “pinning phases” in the compound glass layer consisted of outer Ta–Si–O compound silicate layer and inner SiO 2 glass layer, which was responsible for the excellent oxidation resistance

  20. New evaluation method of crack growth in SiC/SiC composites using interface elements

    International Nuclear Information System (INIS)

    Serizawa, H.; Ando, M.; Lewinsohn, C.A.; Murakawa, H.

    2000-01-01

    Crack propagation behavior in SiC/SiC composites was analyzed using a new computer simulation method that included time-dependent interface elements. The simulation method was used to describe the time-dependent crack growth in SiC/SiC composites under four-point bending of single-edge-notched beam bend-bars. Two methods were used to simulate time-dependent crack growth in SiC/SiC composites due to fiber creep. In one method, the creep property was introduced into the interface elements by the general method of finite element method (FEM) analysis. In the second method, a new technique making the best use of the potential function was used to represent crack closure tractions due to creeping fibers. The stage-II slow crack growth of a general creep deformation was simulated by both methods. Additionally, stage-III crack growth and the transition from stage-II to stage-III could be simulated by the new method. The new method has the potential to completely simulate time-dependent crack growth behavior in SiC/SiC composites due to fiber creep

  1. Thermal Gradient Cyclic Behavior of a Thermal/Environmental Barrier Coating System on SiC/SiC Ceramic Matrix Composites

    Science.gov (United States)

    Zhu, Dongming; Lee, Kang N.; Miller, Robert A.

    2002-01-01

    Thermal barrier and environmental barrier coatings (TBCs and EBCs) will play a crucial role in future advanced gas turbine engines because of their ability to significantly extend the temperature capability of the ceramic matrix composite (CMC) engine components in harsh combustion environments. In order to develop high performance, robust coating systems for effective thermal and environmental protection of the engine components, appropriate test approaches for evaluating the critical coating properties must be established. In this paper, a laser high-heat-flux, thermal gradient approach for testing the coatings will be described. Thermal cyclic behavior of plasma-sprayed coating systems, consisting of ZrO2-8wt%Y2O3 thermal barrier and NASA Enabling Propulsion Materials (EPM) Program developed mullite+BSAS/Si type environmental barrier coatings on SiC/SiC ceramic matrix composites, was investigated under thermal gradients using the laser heat-flux rig in conjunction with the furnace thermal cyclic tests in water-vapor environments. The coating sintering and interface damage were assessed by monitoring the real-time thermal conductivity changes during the laser heat-flux tests and by examining the microstructural changes after the tests. The coating failure mechanisms are discussed based on the cyclic test results and are correlated to the sintering, creep, and thermal stress behavior under simulated engine temperature and heat flux conditions.

  2. Effect of Cold Forging on Microstructure and MechanicalProperties of Al/SiC Composites

    Science.gov (United States)

    Hanamantraygouda, M. B.; Shivakumar, B. P., Dr; Siddappa, P. N.; Sampathkumar, L.; Prashanth, L.

    2018-02-01

    The objective of this work was to investigate the effect of cold forging on mechanical properties and microstructural study of Al MMCs, at different wt% of SiC and forging cycle. The Al-SiC composite material was fabricated by stir casting method at different weight percentage of SiC such as 2.5, 5, 7.5 and 10%. Further, the deformation characteristics during open-die forging of Al-SiC composite at cold conditions was investigated. Cast and forged composite material was subjected to hardness test, tensile test and impact test. The grain size, microstructure behaviour was investigated using optical microscope. The results show that hardness and strength of Al-SiC composite increases and ductility decreases as compared to Al alloy in both as-cast and forged conditions. Optical microscope images showed that the distribution of SiC in Al matrix was more homogeneous in a forged composite as compared to cast one and reduction of porosity was found. Further, it showed that due to forging cycle the grain size was reduced by 30% to 35% from initial size.

  3. Impact resistance of uncoated SiC/SiC composites

    International Nuclear Information System (INIS)

    Bhatt, Ramakrishna T.; Choi, Sung R.; Cosgriff, Laura M.; Fox, Dennis S.; Lee, Kang N.

    2008-01-01

    Two-dimensional woven SiC/SiC composites fabricated by melt infiltration method were impact tested at room temperature and at 1316 deg. C in air using 1.59-mm diameter steel-ball projectiles at velocities ranging from 115 to 400 m/s. The extent of substrate damage with increasing projectile velocity was imaged and analyzed using optical and scanning electron microscopy, and non-destructive evaluation (NDE) methods such as pulsed thermography, and computed tomography. The impacted specimens were tensile tested at room temperature to determine their residual mechanical properties. Results indicate that at 115 m/s projectile velocity, the composite showed no noticeable surface or internal damage and retained its as-fabricated mechanical properties. As the projectile velocity increased above this value, the internal damage increased and mechanical properties degraded. At velocities >300 m/s, the projectile penetrated through the composite, but the composite retained ∼50% of the ultimate tensile strength of the as-fabricated composite and exhibited non-brittle failure. Predominant internal damages are delamination of fiber plies, fiber fracture and matrix shearing

  4. Radiation effects and micromechanics of SiC/SiC composites

    International Nuclear Information System (INIS)

    Ghoniem, N.M.

    1992-01-01

    The basic displacement damage process in SiC has been fully explored, and the mechanisms identified. Major modifications have been made to the theory of damage dosimetry in Fusion, Fission and Ion Simulation studies of Sic. For the first time, calculations of displacements per atoms in SiC can be made in any irradiation environment. Applications to irradiations in fusion first wall neutron spectra (ARIES and PROMETHEUS) as well as in fission spectra (HIFIR and FFTF) are given. Nucleation of helium-filled cavities in SiC was studied, using concepts of stability theory to determine the size of the critical nucleus under continuous generation of helium and displacement damage. It is predicted that a bimodal distribution of cavity sizes is likely to occur in heavily irradiated SiC. A study of the chemical compatibility of SiC composite structures with fusion reactor coolants at high-temperatures was undertaken. It was shown that SiC itself is chemically very stable in helium coolants in the temperature range 500--1000 degree C. However, current fiber/matrix interfaces, such as C and BN are not. The fracture mechanics of high-temperature matrix cracks with bridging fibers is now in progress. A fundamentally unique approach to study the propagation and interaction of cracks in a composite was initiated. The main focus of our research during the following period will be : (1) Theory and experiments for the micro-mechanics of high-temperature failure; and (2) Analysis of radiation damage and microstructure evolution

  5. Modes of oxidation in SiC-reinforced mullite/ZrO2 composites: Oxidation vs depth behavior

    International Nuclear Information System (INIS)

    Lin, C.C.; Ruh, R.

    1999-01-01

    Two basic oxidation modes of composites with oxidizing particles in a non-oxidizing matrix have been observed. Mode I is defined as the complete oxidation of all the particles within an outer layer of the composite, while mode II exhibits partial oxidation of the particles, deep into the composite. Using microscopic observations to plot the silica layer thickness on particles (whiskers) vs the depth of the particles (whiskers) below the composite surface is proposed as a powerful means of categorizing and quantifying actual oxidation modes. Thus, mullite/SiC-whisker composites were found to have mode I oxidation behavior, while certain (mullite + ZrO 2 )/SiC-whisker composites were found to exhibit mode II behavior, followed by a mixed mode after severe exposures. It is proposed that mode II behavior appears when oxygen diffusivity in the matrix is much higher than that in the product oxide layer

  6. Sintering Behavior of Spark Plasma Sintered SiC with Si-SiC Composite Nanoparticles Prepared by Thermal DC Plasma Process

    Science.gov (United States)

    Yu, Yeon-Tae; Naik, Gautam Kumar; Lim, Young-Bin; Yoon, Jeong-Mo

    2017-11-01

    The Si-coated SiC (Si-SiC) composite nanoparticle was prepared by non-transferred arc thermal plasma processing of solid-state synthesized SiC powder and was used as a sintering additive for SiC ceramic formation. Sintered SiC pellet was prepared by spark plasma sintering (SPS) process, and the effect of nano-sized Si-SiC composite particles on the sintering behavior of micron-sized SiC powder was investigated. The mixing ratio of Si-SiC composite nanoparticle to micron-sized SiC was optimized to 10 wt%. Vicker's hardness and relative density was increased with increasing sintering temperature and holding time. The relative density and Vicker's hardness was further increased by reaction bonding using additional activated carbon to the mixture of micron-sized SiC and nano-sized Si-SiC. The maximum relative density (97.1%) and Vicker's hardness (31.4 GPa) were recorded at 1800 °C sintering temperature for 1 min holding time, when 0.2 wt% additional activated carbon was added to the mixture of SiC/Si-SiC.

  7. Thermophysical and mechanical properties of SiC/SiC composites

    International Nuclear Information System (INIS)

    Zinkle, S.J.; Snead, L.L.

    1998-01-01

    The key thermophysical and mechanical properties for SiC/SiC composites are summarized, including temperature-dependent tensile properties, elastic constants, thermal conductivity, thermal expansion, and specific heat. The effects of neutron irradiation on the thermal conductivity and dimensional stability (volumetric swelling, creep) of SiC is discussed. The estimated lower and upper temperatures limits for structural applications in high power density fusion applications are 400 and 1000 C due to thermal conductivity degradation and void swelling considerations, respectively. Further data are needed to more accurately determine these estimated temperature limits

  8. EFFECT OF THE Si POWDER ADDITIONS ON THE PROPERTIES OF SiC COMPOSITES

    Directory of Open Access Journals (Sweden)

    GUOGANG XU

    2012-09-01

    Full Text Available By means of transient plastic phase process, the SiC silicon carbide kiln furniture materials were produced through adding Si powder to SiC materials. At the condition of the same additions of SiO2 powder, the effect of the Si powder additions on properties of silicon carbide materials after sintered at 1450°C for 3 h in air atmosphere was studied by means of SEM and other analysis methods. The results showed that silicon powder contributes to both sintering by liquid state and plastic phase combination to improve the strength of samples. When the Si powder additions is lower than 3.5 %, the density and strength of samples increase and porosity decrease with increasing Si powder additions. However when the Si powder additions is higher than 3.5 %, the density and strength of samples decrease and porosity increase with increasing Si powder additions. With increasing of Si additions, the residual strength of sample after thermal shocked increased and linear change rate decreased, and get to boundary value when Si additions is 4.5 %. The results also indicated that at the same sintering temperature, the sample with 3.5 % silicon powder has maximum strength.

  9. Nanocrystalline SiC and Ti3SiC2 Alloys for Reactor Materials: Annual Report

    Energy Technology Data Exchange (ETDEWEB)

    Henager, Charles H. [pnnl; Alvine, Kyle J. [Pacific Northwest National Lab. (PNNL), Richland, WA (United States); Roosendaal, Timothy J. [Pacific Northwest National Lab. (PNNL), Richland, WA (United States); Shin, Yongsoon [Pacific Northwest National Lab. (PNNL), Richland, WA (United States); Nguyen, Ba Nghiep; Borlaug, Brennan A. [Pacific Northwest National Lab. (PNNL), Richland, WA (United States); Jiang, Weilin [Pacific Northwest National Lab. (PNNL), Richland, WA (United States); Arreguin, Shelly A. [Pacific Northwest National Lab. (PNNL), Richland, WA (United States)

    2015-01-15

    A new dual-phase nanocomposite of Ti₃SiC₂/SiC is being synthesized using preceramic polymers, ceramic powders, and carbon nanotubes (CNTs) designed to be suitable for advanced nuclear reactors and perhaps as fuel cladding. The material is being designed to have superior fracture toughness compared to SiC, adequate thermal conductivity, and higher density than SiC/SiC composites. This annual report summarizes the progress towards this goal and reports progress in understanding certain aspects of the material behavior but some shortcomings in achieving full density or in achieving adequate incorporation of CNTs. The measured thermal conductivity is adequate and falls into an expected range based on SiC and Ti₃SiC₂. Part of this study makes an initial assessment for Ti₃SiC₂ as a barrier to fission product transport. Ion implantation was used to introduce fission product surrogates (Ag and Cs) and a noble metal (Au) in Ti₃SiC₂, SiC, and a synthesized at PNNL. The experimental results indicate that the implanted Ag in SiC is immobile up to the highest temperature (1273 K) applied in this study; in contrast, significant out-diffusion of both Ag and Au in MAX phase Ti₃SiC₂ occurs during ion implantation at 873 K. Cs in Ti₃SiC₂ is found to diffuse during post-irradiation annealing at 973 K, and noticeable Cs release from the sample is observed. This study may suggest caution in using Ti₃SiC₂ as a fuel cladding material for advanced nuclear reactors operating at very high temperatures. Progress is reported in thermal conductivity modeling of SiC-based materials that is relevant to this research, as is progress in modeling the effects of CNTs on fracture strength of SiC-based materials.

  10. SiC as an oxidation-resistant refractory material. Pt. 1

    International Nuclear Information System (INIS)

    Schlichting, J.

    1979-01-01

    Uses his own investigations and gives a literature survey on the oxidation and corrosion behaviour of SiC (in the form of a pure SiC powder, hot-pressed and reaction-sintered materials). The excellent stability of SiC in oxidizing atmosphere is due to the development of protective SiO 2 coatings. Any changes in these protective coatings (e.g. due to impurities with corrosive media, high porosity of SiC, etc.) lead in most cases to increased rates of oxidation and thus restrict the field of application of SiC. (orig.) [de

  11. Sintering Behavior of Spark Plasma Sintered SiC with Si-SiC Composite Nanoparticles Prepared by Thermal DC Plasma Process.

    Science.gov (United States)

    Yu, Yeon-Tae; Naik, Gautam Kumar; Lim, Young-Bin; Yoon, Jeong-Mo

    2017-11-25

    The Si-coated SiC (Si-SiC) composite nanoparticle was prepared by non-transferred arc thermal plasma processing of solid-state synthesized SiC powder and was used as a sintering additive for SiC ceramic formation. Sintered SiC pellet was prepared by spark plasma sintering (SPS) process, and the effect of nano-sized Si-SiC composite particles on the sintering behavior of micron-sized SiC powder was investigated. The mixing ratio of Si-SiC composite nanoparticle to micron-sized SiC was optimized to 10 wt%. Vicker's hardness and relative density was increased with increasing sintering temperature and holding time. The relative density and Vicker's hardness was further increased by reaction bonding using additional activated carbon to the mixture of micron-sized SiC and nano-sized Si-SiC. The maximum relative density (97.1%) and Vicker's hardness (31.4 GPa) were recorded at 1800 °C sintering temperature for 1 min holding time, when 0.2 wt% additional activated carbon was added to the mixture of SiC/Si-SiC.

  12. Fabrication and Mechanical Properties of SiCw(p/SiC-Si Composites by Liquid Si Infiltration using Pyrolysed Rice Husks and SiC Powders as Precursors

    Directory of Open Access Journals (Sweden)

    Dan Zhu

    2014-03-01

    Full Text Available Dense silicon carbide (SiC matrix composites with SiC whiskers and particles as reinforcement were prepared by infiltrating molten Si at 1550 °C into porous preforms composed of pyrolysed rice husks (RHs and extra added SiC powder in different ratios. The Vickers hardness of the composites showed an increase from 18.6 to 21.3 GPa when the amount of SiC added in the preforms was 20% (w/w, and then decreased to 17.3 GPa with the increase of SiC added in the preforms up to 80% (w/w. The values of flexural strength of the composites initially decreased when 20% (w/w SiC was added in the preform and then increased to 587 MPa when the SiC concentration reached 80% (w/w. The refinement of SiC particle sizes and the improvement of the microstructure in particle distribution of the composites due to the addition of external SiC played an effective role in improving the mechanical properties of the composites.

  13. Hot pressing of B{sub 4}C/SiC composites

    Energy Technology Data Exchange (ETDEWEB)

    Sahin, F.C.; Turhan, E.; Yesilcubuk, S.A.; Addemir, O. [Ystanbul Technical University, Faculty of Chemistry and Metallurgy, Materials and Metallurgical Engineering Dept., Maslak-Ystanbul (Turkey)

    2005-07-01

    B{sub 4}C/SiC ceramic composites containing 10-20-30 vol % SiC were prepared by hot pressing method. The effect of SiC addition and hot pressing temperature on sintering behaviour and mechanical properties of hot pressed composites were investigated. Microstructures of hot pressed samples were examined by SEM technique. Three different temperatures (2100 deg. C, 2200 deg. C and 2250 deg. C) were used to optimize hot pressing temperature applying 100 MPa pressure under argon atmosphere during the sintering procedure. The highest relative density of 98.44 % was obtained by hot pressing at 2250 deg. C. However, bending strengths of B{sub 4}C/SiC composite samples were lower than monolithic B{sub 4}C in all experimental conditions. (authors)

  14. Advanced SiC/SiC Ceramic Composites For Gas-Turbine Engine Components

    Science.gov (United States)

    Yun, H. M.; DiCarlo, J. A.; Easler, T. E.

    2004-01-01

    NASA Glenn Research Center (GRC) is developing a variety of advanced SiC/SiC ceramic composite (ASC) systems that allow these materials to operate for hundreds of hours under stress in air at temperatures approaching 2700 F. These SiC/SiC composite systems are lightweight (approximately 30% metal density) and, in comparison to monolithic ceramics and carbon fiber-reinforced ceramic composites, are able to reliably retain their structural properties for long times under aggressive gas-turbine engine environments. The key for the ASC systems is related first to the NASA development of the Sylramic-iBN Sic fiber, which displays higher thermal stability than any other SiC- based ceramic fibers and possesses an in-situ grown BN surface layer for higher environmental durability. This fiber is simply derived from Sylramic Sic fiber type that is currently produced at ATK COI Ceramics (COIC). Further capability is then derived by using chemical vapor infiltration (CVI) and/or polymer infiltration and pyrolysis (PIP) to form a Sic-based matrix with high creep and rupture resistance as well as high thermal conductivity. The objectives of this study were (1) to optimize the constituents and processing parameters for a Sylramic-iBN fiber reinforced ceramic composite system in which the Sic-based matrix is formed at COIC almost entirely by PIP (full PIP approach), (2) to evaluate the properties of this system in comparison to other 2700 F Sylramic-iBN systems in which the matrix is formed by full CVI and CVI + PIP, and (3) to examine the pros and cons of the full PIP approach for fabricating hot-section engine components. A key goal is the development of a composite system with low porosity, thereby providing high modulus, high matrix cracking strength, high interlaminar strength, and high thermal conductivity, a major property requirement for engine components that will experience high thermal gradients during service. Other key composite property goals are demonstration at

  15. Influence of Adhesive System on Performance of SiO/C Lithium-ion Battery

    Directory of Open Access Journals (Sweden)

    Teng Xin

    2015-01-01

    Full Text Available Silicon based anode material is turning into the research hot point of lithium-ion battery material field due to Si inside supporting higher capacity. Furthermore binder applied as major accessory material of anode system could bring anode material & current collector together, thus the influence given by binder system to battery performance becomes the key point. The paper describes the procedure of adopting commercial LiCoO2 SiO/C as composite material & electrolyte, with using styrene butadiene rubber and acrylic acid copolymer as binder to figure out lithium-ion battery with 2.5Ah, which is testified to present better performance on cold temperature & cycle life plus having a little bit swelling compared with the lithium-ion battery using only styrene butadiene rubber as binder.

  16. Growing GaN LEDs on amorphous SiC buffer with variable C/Si compositions

    Science.gov (United States)

    Cheng, Chih-Hsien; Tzou, An-Jye; Chang, Jung-Hung; Chi, Yu-Chieh; Lin, Yung-Hsiang; Shih, Min-Hsiung; Lee, Chao-Kuei; Wu, Chih-I; Kuo, Hao-Chung; Chang, Chun-Yen; Lin, Gong-Ru

    2016-01-01

    The epitaxy of high-power gallium nitride (GaN) light-emitting diode (LED) on amorphous silicon carbide (a-SixC1−x) buffer is demonstrated. The a-SixC1−x buffers with different nonstoichiometric C/Si composition ratios are synthesized on SiO2/Si substrate by using a low-temperature plasma enhanced chemical vapor deposition. The GaN LEDs on different SixC1−x buffers exhibit different EL and C-V characteristics because of the extended strain induced interfacial defects. The EL power decays when increasing the Si content of SixC1−x buffer. The C-rich SixC1−x favors the GaN epitaxy and enables the strain relaxation to suppress the probability of Auger recombination. When the SixC1−x buffer changes from Si-rich to C-rich condition, the EL peak wavelengh shifts from 446 nm to 450 nm. Moreover, the uniform distribution contour of EL intensity spreads between the anode and the cathode because the traping density of the interfacial defect gradually reduces. In comparison with the GaN LED grown on Si-rich SixC1−x buffer, the device deposited on C-rich SixC1−x buffer shows a lower turn-on voltage, a higher output power, an external quantum efficiency, and an efficiency droop of 2.48 V, 106 mW, 42.3%, and 7%, respectively. PMID:26794268

  17. SiC-dopped MCM-41 materials with enhanced thermal and hydrothermal stabilities

    International Nuclear Information System (INIS)

    Wang, Yingyong; Jin, Guoqiang; Tong, Xili; Guo, Xiangyun

    2011-01-01

    Graphical abstract: Novel SiC-dopped MCM-41 materials were synthesized by adding silicon carbide suspension in the molecular sieve precursor solvent followed by in situ hydrothermal synthesis. The dopped materials have a wormhole-like mesoporous structure and exhibit enhanced thermal and hydrothermal stabilities. Highlights: → SiC-dopped MCM-41 was synthesized by in situ hydrothermal synthesis of molecular sieve precursor combined with SiC. → The dopped MCM-41 materials show a wormhole-like mesoporous structure. → The thermal stability of the dopped materials have an increment of almost 100 o C compared with the pure MCM-41. → The hydrothermal stability of the dopped materials is also better than that of the pure MCM-41. -- Abstract: SiC-dopped MCM-41 mesoporous materials were synthesized by the in situ hydrothermal synthesis, in which a small amount of SiC was added in the precursor solvent of molecular sieve before the hydrothermal treatment. The materials were characterized by X-ray diffraction, transmission electron microscopy, X-ray photoelectron spectroscopy, N 2 physical adsorption and thermogravimetric analysis, respectively. The results show that the thermal and hydrothermal stabilities of MCM-41 materials can be improved obviously by incorporating a small amount of SiC. The structure collapse temperature of SiC-dopped MCM-41 materials is 100 o C higher than that of pure MCM-41 according to the differential scanning calorimetry analysis. Hydrothermal treatment experiments also show that the pure MCM-41 will losses it's ordered mesoporous structure in boiling water for 24 h while the SiC-dopped MCM-41 materials still keep partial porous structure.

  18. Development of the fabrication process of SiC composite by radiation beam

    International Nuclear Information System (INIS)

    Park, Ji Yeon; Kim, Weon Ju; Jung, Choong Hwan; Woo, Chang Hyeon; Ryu, Woo Seog

    2006-01-01

    In order to operate the nuclear system at high temperatures, core materials with a good irradiation resistance at high temperatures must be developed. SiC composite is one of candidates for high temperature structural materials. Among several fabrication processes, the PIP process includes the curing and pyrolysis process. Generally, the thermal oxidation curing method has some disadvantages; difficulty in the control of oxygen contents and volatilization of many constituents. To overcome these disadvantages and reduce the process time, a new and improved method like the beam curing process has been proposed as one of the effective methods for the fabrication of SiC composite. In this study, the electron beam curing method in the PIP process was optimized to develop SiCf/SiC composite with low oxygen contents. Using the electron beam curing method with full doses of 2∼10 MGy and the pyrolysis process at 1300∼1400 .deg. C, composite with the oxygen content of less than 1 wt% could be obtained. Additionally, if the slurry impregnation and curing/pyrolysis processes were repeated several times, dense composite could be produced

  19. Facile synthesis and lithium storage properties of a porous NiSi2/Si/carbon composite anode material for lithium-ion batteries.

    Science.gov (United States)

    Jia, Haiping; Stock, Christoph; Kloepsch, Richard; He, Xin; Badillo, Juan Pablo; Fromm, Olga; Vortmann, Britta; Winter, Martin; Placke, Tobias

    2015-01-28

    In this work, a novel, porous structured NiSi2/Si composite material with a core-shell morphology was successfully prepared using a facile ball-milling method. Furthermore, the chemical vapor deposition (CVD) method is deployed to coat the NiSi2/Si phase with a thin carbon layer to further enhance the surface electronic conductivity and to mechanically stabilize the whole composite structure. The morphology and porosity of the composite material was evaluated by scanning electron microscopy (SEM), transmission electron microscopy (TEM), and nitrogen adsorption measurements (BJH analysis). The as-prepared composite material consists of NiSi2, silicon, and carbon phases, in which the NiSi2 phase is embedded in a silicon matrix having homogeneously distributed pores, while the surface of this composite is coated with a carbon layer. The electrochemical characterization shows that the porous and core-shell structure of the composite anode material can effectively absorb and buffer the immense volume changes of silicon during the lithiation/delithiation process. The obtained NiSi2/Si/carbon composite anode material displays an outstanding electrochemical performance, which gives a stable capacity of 1272 mAh g(-1) for 200 cycles at a charge/discharge rate of 1C and a good rate capability with a reversible capacity of 740 mAh g(-1) at a rate of 5C.

  20. Determining the fracture resistance of advanced SiC fiber reinforced SiC matrix composites

    International Nuclear Information System (INIS)

    Nozawa, T.; Katoh, Y.; Kishimoto, H.

    2007-01-01

    Full text of publication follows: One of the perceived advantages for highly-crystalline and stoichiometric silicon carbide (SiC) and SiC composites, e.g., advanced SiC fiber reinforced chemically-vapor-infiltrated (CVI) SiC matrix composites, is the retention of fast fracture properties after neutron irradiation at high-temperatures (∼1000 deg. C) to intermediate-doses (∼15 dpa). Accordingly, it has been clarified that the maximum allowable stress (or strain) limit seems unaffected in certain irradiation conditions. Meanwhile, understanding the mechanism of crack propagation from flaws, as potential weakest link to cause composite failure, is somehow lacking, despite that determining the strength criterion based on the fracture mechanics will eventually become important considering the nature of composites' fracture. This study aims to evaluate crack propagation behaviors of advanced SiC/SiC and to provide fundamentals on fracture resistance of the composites to define the strength limit for the practical component design. For those purposes, the effects of irreversible energies related to interfacial de-bonding, fiber bridging, and microcrack forming on the fracture resistance were evaluated. Two-dimensional SiC/SiC composites were fabricated by CVI or nano-infiltration and transient-eutectic-phase (NITE ) methods. Hi-Nicalon TM Type-S or Tyranno TM -SA fibers were used as reinforcements. In-plane mode-I fracture resistance was evaluated by the single edge notched bend technique. The key finding is the continuous Load increase with the crack growth for any types of advanced composites, while many studies specified the gradual load decrease for the conventional composites once the crack initiates. This high quasi-ductility appeared due primarily to high friction (>100 MPa) at the fiber/matrix interface using rough SiC fibers. The preliminary analysis based on the linear elastic fracture mechanics, which does not consider the effects of irreversible energy

  1. Thermo-mechanical assessment of full SiC/SiC composite cladding for LWR applications with sensitivity analysis

    Science.gov (United States)

    Singh, Gyanender; Terrani, Kurt; Katoh, Yutai

    2018-02-01

    SiC/SiC composites are considered among leading candidates for accident tolerant fuel cladding in light water reactors. However, when SiC-based materials are exposed to neutron irradiation, they experience significant changes in dimensions and physical properties. Under a large heat flux application (i.e. fuel cladding), the non-uniform changes in the dimensions and physical properties will lead to build-up of stresses in the structure over the course of time. To ensure reliable and safe operation of such a structure it is important to assess its thermo-mechanical performance under in-reactor conditions of irradiation and elevated temperature. In this work, the foundation for 3D thermo-mechanical analysis of SiC/SiC cladding is put in place and a set of analyses with simplified boundary conditions has been performed. The analyses were carried out with two different codes that were benchmarked against one another and prior results in the literature. A constitutive model is constructed and solved numerically to predict the stress distribution and variation in the cladding under normal operating conditions. The dependence of dimensions and physical properties variation with irradiation and temperature has been incorporated. These robust models may now be modified to take into account the axial and circumferential variation in neutron and heat flux to fully account for 3D effects. The results from the simple analyses show the development of high tensile stresses especially in the circumferential and axial directions at the inner region of the cladding. Based on the results obtained, design guidelines are recommended. For lack of certainty in or tailor-ability for the physical and mechanical properties of SiC/SiC composite material a sensitivity analysis is conducted. The analysis results establish a precedence order of the properties based on the extent to which these properties influence the temperature and the stresses.

  2. SiO2/ZnO Composite Hollow Sub-Micron Fibers: Fabrication from Facile Single Capillary Electrospinning and Their Photoluminescence Properties

    Directory of Open Access Journals (Sweden)

    Guanying Song

    2017-02-01

    Full Text Available In this work, SiO2/ZnO composite hollow sub-micron fibers were fabricated by a facile single capillary electrospinning technique followed by calcination, using tetraethyl orthosilicate (TEOS, polyvinylpyrrolidone (PVP and ZnO nanoparticles as raw materials. The characterization results of the scanning electron microscopy (SEM, transmission electron microscopy (TEM, X-ray diffraction (XRD and Fourier transform infrared spectroscopy (FT-IR spectra indicated that the asprepared composite hollow fibers consisted of amorphous SiO2 and hexagonal wurtzite ZnO. The products revealed uniform tubular structure with outer diameters of 400–500 nm and wall thickness of 50–60 nm. The gases generated and the directional escaped mechanism was proposed to illustrate the formation of SiO2/ZnO composite hollow sub-micron fibers. Furthermore, a broad blue emission band was observed in the photoluminescence (PL of SiO2/ZnO composite hollow sub-micron fibers, exhibiting great potential applications as blue light-emitting candidate materials.

  3. Si-O-C ceramic foams derived from polymethylphenylsiloxane precursor with starch as foaming agent

    Czech Academy of Sciences Publication Activity Database

    Černý, Martin; Chlup, Zdeněk; Strachota, Adam; Svítilová, Jaroslava; Schweigstillová, Jana; Halasová, Martina; Rýglová, Šárka

    2015-01-01

    Roč. 35, č. 13 (2015), s. 3427-3436 ISSN 0955-2219 R&D Projects: GA ČR GAP107/12/2445 Institutional support: RVO:67985891 ; RVO:68081723 ; RVO:61389013 Keywords : pyrolysis * ceramic foam * precursor * starch * Si-O-C Subject RIV: JI - Composite Materials; JH - Ceramics, Fire-Resistant Materials and Glass (UFM-A) Impact factor: 2.933, year: 2015

  4. Effect of Ti and Si interlayer materials on the joining of SiC ceramics

    Energy Technology Data Exchange (ETDEWEB)

    Jung, Yang Il; Park, Jung Hwan; Kim, Hyun Gil; Park, Dong Jun; Park, Jeong Yong; Kim, Weon Ju [LWR Fuel Technology Division, Korea Atomic Energy Research Institute, Daejeon (Korea, Republic of)

    2016-08-15

    SiC-based ceramic composites are currently being considered for use in fuel cladding tubes in light-water reactors. The joining of SiC ceramics in a hermetic seal is required for the development of ceramic-based fuel cladding tubes. In this study, SiC monoliths were diffusion bonded using a Ti foil interlayer and additional Si powder. In the joining process, a very low uniaxial pressure of ∼0.1 MPa was applied, so the process is applicable for joining thin-walled long tubes. The joining strength depended strongly on the type of SiC material. Reaction-bonded SiC (RB-SiC) showed a higher joining strength than sintered SiC because the diffusion reaction of Si was promoted in the former. The joining strength of sintered SiC was increased by the addition of Si at the Ti interlayer to play the role of the free Si in RB-SiC. The maximum joint strength obtained under torsional stress was ∼100 MPa. The joint interface consisted of TiSi{sub 2}, Ti{sub 3}SiC{sub 2}, and SiC phases formed by a diffusion reaction of Ti and Si.

  5. Microstructure and mechanical properties of low-activation glass-ceramic joining and coating for SiC/SiC composites

    International Nuclear Information System (INIS)

    Katoh, Yutai; Kotani, M.; Kohyama, A.; Montorsi, M.; Salvo, M.; Ferraris, M.

    2000-01-01

    Calcia-alumina (CA) glass-ceramic was studied as a candidate low-activation joining and sealing material for SiC/SiC components for fusion blanket and diverter structures, in terms of microstructural stability and mechanical properties. The CA glass-ceramic joining and seal coating were applied to the Hi-Nicalon TM SiC fiber-reinforced SiC matrix composites in which the matrix had been formed through chemical vapor infiltration and polymer impregnation and pyrolysis methods. Microstructural characterization was carried out for the joined and coated materials by optical and scanning electron microscopy (SEM). The mechanical property of the joint was evaluated through a shear test on sandwich joints. The average shear strength of the joined structures was 28 MPa at room temperature. Fractography revealed that the fracture occurred in the glass phase and the shear strength may be improved by reduction of the glass fraction

  6. Obtenção de substratos cerâmicos no sistema Si-Al-O-N-C empregando polissiloxanos e carga de Si e Al2O3 Ceramic tapes of Si-Al-O-N-C compounds using mixtures of polyssiloxane and Si-Al2O3 fillers

    Directory of Open Access Journals (Sweden)

    R. M. Rocha

    2005-03-01

    Full Text Available A técnica de processamento de colagem por fita (tape casting tem sido amplamente utilizada na obtenção de cerâmicas para diferentes aplicações: substratos cerâmicos e estruturas planares em multicamadas para circuitos integrados e capacitores; eletrólitos sólidos para células a combustível e sensores; cerâmicas piezoelétricas para atuadores e transdutores; membranas de separação para micro-filtragem; compósitos estruturais e trocadores de calor. Neste trabalho, a técnica convencional de colagem por fita foi adaptada com a utilização do processo de pirólise controlada de misturas de polímeros e carga, empregando-se polissiloxanos e cargas de silício e alumina nas suspensões. Foram preparadas suspensões com 60% vol. de fase polimérica (polissiloxanos e metil-trietoxi-silano e 40% vol. de carga (Si e Al2O3, com diferentes concentrações dos polímeros e das cargas. As amostras na forma de substratos foram pirolisadas em atmosfera de nitrogênio a 1400 °C/2 h e 1500 °C/2 h, sendo convertidas em materiais cerâmicos no sistema Si-Al-O-N-C. O processo de pirólise foi caracterizado até a temperatura de 1000 ºC por análise termogravimétrica. As cerâmicas foram caracterizadas quanto às fases formadas, microestrutura, massa específica aparente e condutividade térmica. Os substratos cerâmicos apresentaram porosidade relativamente alta (entre 12 e 22% e baixa condutividade térmica (entre 3 e 8 W/m.K, sendo constituídos por fases cristalinas de beta-SiC, Si2ON2, O'-SiAlON, Al2O3, mulita e fase amorfa de SiOC; o Si foi observado nas amostras pirolisadas a 1400 ºC.The tape casting technique has been widely used to prepare ceramic tapes for different applications: ceramic substrates and multilayer planar structures for integrated circuits and capacitors, solid electrolytes for fuel cells and sensors, piezoelectric ceramics for actuators and transducers, membrane systems for micro-filtration, structural composites and

  7. CoFe2O4-SiO2 Composites: Preparation and Magnetodielectric Properties

    Directory of Open Access Journals (Sweden)

    T. Ramesh

    2016-01-01

    Full Text Available Cobalt ferrite (CoFe2O4 and silica (SiO2 nanopowders have been prepared by the microwave hydrothermal (M-H method using metal nitrates as precursors of CoFe2O4 and tetraethyl orthosilicate as a precursor of SiO2. The synthesized powders were characterized by XRD and FESEM. The (100-x (CoFe2O4 + xSiO2 (where x = 0%, 10%, 20%, and 30% composites with different weight percentages have been prepared using ball mill method. The composite samples were sintered at 800°C/60 min using the microwave sintering method and then their structural and morphological studies were investigated using X-ray diffraction (XRD, Fourier transformation infrared (FTIR spectra, and scanning electron microscopy (SEM, respectively. The effect of SiO2 content on the magnetic and electrical properties of CoFe2O4/SiO2 nanocomposites has been studied via the magnetic hysteresis loops, complex permeability, permittivity spectra, and DC resistivity measurements. The synthesized nanocomposites with adjustable grain sizes and controllable magnetic properties make the applicability of cobalt ferrite even more versatile.

  8. SiC-Si as a support material for oxygen evolution electrode in PEM steam electrolysers

    DEFF Research Database (Denmark)

    Nikiforov, Aleksey; Tomás García, Antonio Luis; Petrushina, Irina

    2011-01-01

    The need of higher energy efficiency in hydrogen production has promoted the research on improved catalysts for water electrolysis. In this work, a novel supported catalyst for oxygen evolution electrodes was prepared and characterized with different techniques. IrO2 supported on a SiC/Si composite...

  9. Effect of Environment on the Stress- Rupture Behavior of a C/SiC Composite Studied

    Science.gov (United States)

    Verrilli, Michael J.; Kiser, J. Douglas; Opila, Elizabeth J.; Calomino, Anthony M.

    2002-01-01

    Advanced reusable launch vehicles will likely incorporate fiber-reinforced ceramic matrix composites (CMC's) in critical propulsion and airframe components. The use of CMC's is highly desirable to save weight, improve reuse capability, and increase performance. One of the candidate CMC materials is carbon-fiber-reinforced silicon carbide (C/SiC). In potential propulsion applications, such as turbopump rotors and nozzle exit ramps, C/SiC components will be subjected to a service cycle that includes mechanical loading under complex, high-pressure environments containing hydrogen, oxygen, and steam. Degradation of both the C fibers and the SiC matrix are possible in these environments. The objective of this effort was to evaluate the mechanical behavior of C/SiC in various environments relevant to reusable launch vehicle applications. Stress-rupture testing was conducted at the NASA Glenn Research Center on C/SiC specimens in air and steam-containing environments. Also, the oxidation kinetics of the carbon fibers that reinforce the composite were monitored by thermogravimetric analysis in the same environments and temperatures used for the stress-rupture tests of the C/SiC composite specimens. The stress-rupture lives obtained for C/SiC tested in air and in steam/argon mixtures are shown in the following bar chart. As is typical for most materials, lives obtained at the lower temperature (600 C) are longer than for the higher temperature (1200 C). The effect of environment was most pronounced at the lower temperature, where the average test duration in steam at 600 C was at least 30 times longer than the lives obtained in air. The 1200 C data revealed little difference between the lives of specimens tested in air and steam at atmospheric pressure.

  10. Electrolytic Production of Ti5Si3/TiC Composites by Solid Oxide Membrane Technology

    Science.gov (United States)

    Zheng, Kai; Zou, Xingli; Xie, Xueliang; Lu, Changyuan; Chen, Chaoyi; Xu, Qian; Lu, Xionggang

    2018-02-01

    This paper investigated the electrolytic production of Ti5Si3/TiC composites from TiO2/SiO2/C in molten CaCl2. The solid-oxide oxygen-ion-conducting membrane tube filled with carbon-saturated liquid tin was served as the anode, and the pressed spherical TiO2/SiO2/C pellet was used as the cathode. The electrochemical reduction process was carried out at 1273 K and 3.8 V. The characteristics of the obtained cathode products and the reaction mechanism of the electroreduction process were studied by a series of time-dependent electroreduction experiments. It was found that the electroreduction process generally proceeds through the following steps: TiO2/SiO2/C → Ti2O3, CaTiO3, Ca2SiO4, SiC → Ti5Si3, TiC. The morphology observation and the elemental distribution analysis indicate that the reaction routes for Ti5Si3 and TiC products are independent during the electroreduction process.

  11. Heterogeneous Ag-TiO2-SiO2 composite materials as novel catalytic systems for selective epoxidation of cyclohexene by H2O2.

    Directory of Open Access Journals (Sweden)

    Xin Wang

    Full Text Available TiO2-SiO2 composites were synthesized using cetyl trimethyl ammonium bromide (CTAB as the structure directing template. Self-assembly hexadecyltrimethyl- ammonium bromide TiO2-SiO2/(CTAB were soaked into silver nitrate (AgNO3 aqueous solution. The Ag-TiO2-SiO2(Ag-TS composite were prepared via a precipitation of AgBr in soaking process and its decomposition at calcination stage. Structural characterization of the materials was carried out by various techniques including X-ray diffraction (XRD, scanning electron microscopy (SEM, transmission electron microscopy (TEM, N2 adsorption-desorption and ultraviolet visible spectroscopy (UV-Vis. Characterization results revealed that Ag particles were incorporated into hierarchical TiO2-SiO2 without significantly affecting the structures of the supports. Further heating-treatment at 723 K was more favorable for enhancing the stability of the Ag-TS composite. The cyclohexene oxide was the major product in the epoxidation using H2O2 as the oxidant over the Ag-TS catalysts. Besides, the optimum catalytic activity and stability of Ag-TS catalysts were obtained under operational conditions of calcined at 723 K for 2 h, reaction time of 120 min, reaction temperature of 353 K, catalyst amount of 80 mg, aqueous H2O2 (30 wt.% as oxidant and chloroform as solvent. High catalytic activity with conversion rate up to 99.2% of cyclohexene oxide could be obtainable in water-bathing. The catalyst was found to be stable and could be reused three times without significant loss of catalytic activity under the optimized reaction conditions.

  12. Preparation of ZnO/SiO{sub 2} gel composites and their performance of H{sub 2}S removal at room temperature

    Energy Technology Data Exchange (ETDEWEB)

    Liu, Guoqiang [Laboratory of Advanced Materials, Department of Materials Science and Engineering, Tsinghua University, Beijing 100084 (China); Huang, Zheng-Hong, E-mail: zhhuang@tsinghua.edu.cn [Laboratory of Advanced Materials, Department of Materials Science and Engineering, Tsinghua University, Beijing 100084 (China); Kang, Feiyu [Laboratory of Advanced Materials, Department of Materials Science and Engineering, Tsinghua University, Beijing 100084 (China); Institute of Advanced Materials Research, Graduate School at Shenzhen, Tsinghua University, Shenzhen 518055 (China)

    2012-05-15

    Graphical abstract: The ZnO/SiO{sub 2} gel composites exhibit mixed type isotherms, in which the initial part is type I, and intermediate and high relative pressures are type IV with a hysteresis loop of type H2. The breakthrough time of ZnO/SiO{sub 2} composites first increased sharply up to 400 Degree-Sign C with the H{sub 2}S breakthrough capacity is up to 96.4 mg/g, and then decrease dramatically with further rising of temperature beyond 500 Degree-Sign C. Highlights: Black-Right-Pointing-Pointer High surface area ZnO/SiO{sub 2} gel composites were prepared by co-sol-gel method. Black-Right-Pointing-Pointer The active phase (ZnO) well disperses in the composites. Black-Right-Pointing-Pointer The highest H{sub 2}S adsorption capacity of the composites reaches up to 96.4 mg/g. Black-Right-Pointing-Pointer Both physisorption and the active phase reactivation governed the H{sub 2}S removal process. - Abstract: ZnO/SiO{sub 2} gel composites with different active component loading were prepared by sol-gel method combined with ambient drying process, followed by thermal treatment. The gel composites were characterized by scanning electron microscopy (SEM), nitrogen adsorption, X-ray diffraction (XRD), FTIR and X-ray photoelectron spectroscopy (XPS), and their performances for H{sub 2}S removal were evaluated by dynamic testing at room temperature. The as prepared materials exhibited high surface area with multimodal pore size distributions in micropore and mesopore region. The porous properties were significantly influenced both by the ZnO loading ratio and the treated temperature. The gel composites showed a high performance for H{sub 2}S removal, with the highest H{sub 2}S adsorption capacity of 96.4 mg/g for the sample treated at 400 Degree-Sign C with 30 wt% ZnO. Both physisorption and the active phase reactivation governed the H{sub 2}S removal process. It needs to optimize the composites' porous structure and active component loading amount.

  13. Oxidation of C/SiC Composites at Reduced Oxygen Partial Pressures

    Science.gov (United States)

    Opila, Elizabeth J.; Serra, Jessica

    2009-01-01

    Carbon-fiber reinforced SiC (C/SiC) composites are proposed for leading edge applications of hypersonic vehicles due to the superior strength of carbon fibers at high temperatures (greater than 1500 C). However, the vulnerability of the carbon fibers in C/SiC to oxidation over a wide range of temperatures remains a problem. Previous oxidation studies of C/SiC have mainly been conducted in air or oxygen, so that the oxidation behavior of C/SiC at reduced oxygen partial pressures of the hypersonic flight regime are less well understood. In this study, both carbon fibers and C/SiC composites were oxidized over a wide range of temperatures and oxygen partial pressures to facilitate the understanding and modeling of C/SiC oxidation kinetics for hypersonic flight conditions.

  14. Liquid phase sintered SiC ceramics from starting materials of different grade Cerâmicas à base de SiC sinterizadas via fase líquida a partir de matérias-primas de diferentes purezas

    Directory of Open Access Journals (Sweden)

    V. A. Izhevskyi

    2004-09-01

    Full Text Available Possibility of high performance ceramics manufactured from commercial SiC powder of technical grade has been shown. Sintering behavior and microstructure formation under conditions of liquid phase sintering (LPS with oxynitride sintering aids (AlN-Y2O3 of three SiC-based compositions have been investigated. Two of the compositions were based on Alcoa 1000 SiC powder of technical grade, and the third one, which was used as a reference, was based on H.C. Starck UF-15 fine grade commercial powder. Milling process used for Alcoa 1000 SiC powder granulometry improvement has been investigated in detail, while chemical treatment of milled SiC powders has been used for pick-up impurities removal. Dilatometric experiments showed that SiC powder of technical grade after appropriate treatment exhibits sinterability comparable with the fine grade SiC. Microstructural investigations performed on sintered samples showed that the final microstructure of the Alcoa 1000 SiC based materials was practically identical with the H.C. Starck SiC based reference ones. Preliminary investigations of hardness and fracture toughness were carried out revealing excellent results for the materials produced from cheaper, nationally produced starting powder.Neste trabalho é apresentada a possibilidade de obtenção de cerâmicas de SiC de alto desempenho a partir de matéria-prima comercial de grau técnico. Foi realizado o estudo de sinterização via fase líquida e desenvolvimento microestrutural de três composições à base de SiC tendo como aditivos de sinterização AlN e Y2O3 . Duas destas composições são à base de SiC-1000 da Alcoa, grau técnico, e a terceira, utilizada como referência, à base do UF-15 da H.C. Starck - Alemanha, pó comercial de granulometria fina. O processo de moagem do pó SiC-1000 da Alcoa foi acompanhado por medidas de distribuição granulométrica e posterior ataque químico, para remoção de impurezas. Os pós de grau técnico, ap

  15. Additive Manufacturing of SiC Based Ceramics and Ceramic Matrix Composites

    Science.gov (United States)

    Halbig, Michael Charles; Singh, Mrityunjay

    2015-01-01

    Silicon carbide (SiC) ceramics and SiC fiber reinforcedSiC ceramic matrix composites (SiCSiC CMCs) offer high payoff as replacements for metals in turbine engine applications due to their lighter weight, higher temperature capability, and lower cooling requirements. Additive manufacturing approaches can offer game changing technologies for the quick and low cost fabrication of parts with much greater design freedom and geometric complexity. Four approaches for developing these materials are presented. The first two utilize low cost 3D printers. The first uses pre-ceramic pastes developed as feed materials which are converted to SiC after firing. The second uses wood containing filament to print a carbonaceous preform which is infiltrated with a pre-ceramic polymer and converted to SiC. The other two approaches pursue the AM of CMCs. The first is binder jet SiC powder processing in collaboration with rp+m (Rapid Prototyping+Manufacturing). Processing optimization was pursued through SiC powder blending, infiltration with and without SiC nano powder loading, and integration of nanofibers into the powder bed. The second approach was laminated object manufacturing (LOM) in which fiber prepregs and laminates are cut to shape by a laser and stacked to form the desired part. Scanning electron microscopy was conducted on materials from all approaches with select approaches also characterized with XRD, TGA, and bend testing.

  16. Solid-state synthesis of uniform Li2MnSiO4/C/graphene composites and their performance in lithium-ion batteries

    Science.gov (United States)

    Gong, Huaxu; Zhu, Yongchun; Wang, Linlin; Wei, Denghu; Liang, Jianwen; Qian, Yitai

    2014-01-01

    Uniform nanospherical Li2MnSiO4/C/graphene composites have been obtained by polyethylene glycol-600 (PEG-600) assisted solid-state reaction using spherical SiO2 as precursor, and heat treatment with the mixed carbon sources (glucose, cellulose acetate and graphene oxide). The transmission electron microscope (TEM) images show that Li2MnSiO4 nanospheres with size of 50 nm are embedded in the three-dimensional (3D) nest-like carbon network. Electrochemical measurements reveal that the composites exhibit first discharge capacity of 215.3 mAh g-1 under 0.05 C, together with a stable discharge capacity of 175 mAh g-1 after 40 cycles. The 3D carbon network and the carbon layer (amorphous carbon and graphene) are favorable for improving the electrochemical performance.

  17. C/SiC/MoSi2-Si multilayer coatings for carbon/carbon composites for protection against oxidation

    International Nuclear Information System (INIS)

    Zhang Yulei; Li Hejun; Qiang Xinfa; Li Kezhi; Zhang Shouyang

    2011-01-01

    Highlights: → A C/SiC/MoSi 2 -Si multilayer coating was prepared on C/C by slurry and pack cementation. → Multilayer coating can protect C/C for 300 h at 1873 K or 103 h at 1873 K in air. → The penetration cracks in the coating result in the weight loss of the coated C/C. → The fracture of the coated C/C in wind tunnel result from the excessive local stress. - Abstract: To improve the oxidation resistance of carbon/carbon (C/C) composites, a C/SiC/MoSi 2 -Si multilayer oxidation protective coating was prepared by slurry and pack cementation. The microstructure of the as-prepared coating was characterized by scanning electron microscopy, X-ray diffraction and energy dispersive spectroscopy. The isothermal oxidation and erosion resistance of the coating was investigated in electrical furnace and high temperature wind tunnel. The results showed that the multilayer coating could effectively protect C/C composites from oxidation in air for 300 h at 1773 K and 103 h at 1873 K, and the coated samples was fractured after erosion for 27 h at 1873 K h in wind tunnel. The weight loss of the coated specimens was considered to be caused by the formation of penetration cracks in the coating. The fracture of the coated C/C composites might result from the excessive local stress in the coating.

  18. Residual stresses and mechanical properties of Si3N4/SiC multilayered composites with different SiC layers; Las tensiones residuales y las propiedades mecánicas de compuestos multicapa de Si3N4/SiC con diferentes capas de SiC

    Energy Technology Data Exchange (ETDEWEB)

    Liua, S.; Lia, Y.; Chena, P.; Lia, W.; Gaoa, S.; Zhang, B.; Yeb, F.

    2017-11-01

    The effect of residual stresses on the strength, toughness and work of fracture of Si3N4/SiC multilayered composites with different SiC layers has been investigated. It may be an effective way to design and optimize the mechanical properties of Si3N4/SiC multilayered composites by controlling the properties of SiC layers. Si3N4/SiC multilayered composites with different SiC layers were fabricated by aqueous tape casting and pressureless sintering. Residual stresses were calculated by using ANSYS simulation, the maximum values of tensile and compressive stresses were 553.2MPa and −552.1MPa, respectively. Step-like fracture was observed from the fracture surfaces. Fraction of delamination layers increased with the residual stress, which can improve the reliability of the materials. Tensile residual stress was benefit to improving toughness and work of fracture, but the strength of the composites decreased. [Spanish] Se ha investigado el efecto de las tensiones residuales en la resistencia, dureza y trabajo de fractura de los compuestos multicapa de Si3N4/SiC con diferentes capas de SiC. Puede ser una manera eficaz de diseñar y optimizar las propiedades mecánicas de los compuestos multicapa de Si3N4/SiC mediante el control de las propiedades de las capas de SiC. Los compuestos multicapa de Si3N4/SiC con diferentes capas de SiC se fabricaron por medio de colado en cinta en medio acuoso y sinterización sin presión. Las tensiones residuales se calcularon mediante el uso de la simulación ANSYS, los valores máximos de las fuerzas de tracción y compresión fueron 553,2 MPa y −552,1 MPa, respectivamente. Se observó una fractura escalonada a partir de las superficies de fractura. La fracción de capas de deslaminación aumenta con la tensión residual, lo que puede mejorar la fiabilidad de los materiales. La fuerza de tracción residual era beneficiosa para la mejora de la dureza y el trabajo de fractura, pero la resistencia de los compuestos disminuyó.

  19. PIE of nuclear grade SiC/SiC flexural coupons irradiated to 10 dpa at LWR temperature

    Energy Technology Data Exchange (ETDEWEB)

    Koyanagi, Takaaki [Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States); Katoh, Yutai [Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States)

    2017-03-01

    Silicon carbide fiber-reinforced SiC matrix (SiC/SiC) composites are being actively investigated for accident-tolerant core structures of light water reactors (LWRs). Owing to the limited number of irradiation studies previously conducted at LWR-coolant temperature, this study examined SiC/SiC composites following neutron irradiation at 230–340°C to 2.0 and 11.8 dpa in the High Flux Isotope Reactor. The investigated materials are chemical vapor infiltrated (CVI) SiC/SiC composites with three different reinforcement fibers. The fiber materials were monolayer pyrolytic carbon (PyC)-coated Hi-NicalonTM Type-S (HNS), TyrannoTM SA3 (SA3), and SCS-UltraTM (SCS) SiC fibers. The irradiation resistance of these composites was investigated based on flexural behavior, dynamic Young’s modulus, swelling, and microstructures. There was no notable mechanical properties degradation of the irradiated HNS and SA3 SiC/SiC composites except for reduction of the Young’s moduli by up to 18%. The microstructural stability of these composites supported the absence of degradation. In addition, no progressive swelling from 2.0 to 11.8 dpa was confirmed for these composites. On the other hand, the SCS composite showed significant mechanical degradation associated with cracking within the fiber. This study determined that SiC/SiC composites with HNS or SA3 SiC/SiC fibers, a PyC interphase, and a CVI SiC matrix retain their properties beyond the lifetime dose for LWR fuel cladding at the relevant temperature.

  20. Nanostructured Si/TiC composite anode for Li-ion batteries

    International Nuclear Information System (INIS)

    Zeng, Z.Y.; Tu, J.P.; Yang, Y.Z.; Xiang, J.Y.; Huang, X.H.; Mao, F.; Ma, M.

    2008-01-01

    Si/TiC nanocomposite anode was synthesized by a surface sol-gel method in combination with a following heat-treatment process. Through this process, nanosized Si was homogeneously distributed in a titanium carbide matrix. The electrochemically less active TiC working as a buffer matrix successfully prevented Si from cracking/crumbling during the charging/discharging process. The interspaces in the Si/TiC nanocomposite could offer convenient channels for Li ions to react with active Si. The Si/TiC composite exhibited a reversible charge/discharge capacity of about 1000 mAh g -1 with average discharge capacity fading of 1.8 mAh g -1 (0.18%) from 2nd to 100th cycle, indicating its excellent cyclability when used as anode materials for lithium-ion batteries

  1. Preparation and characterization of reduced graphene oxide/copper composites incorporated with nano-SiO2 particles

    International Nuclear Information System (INIS)

    Zhang, Xinjiang; Dong, Pengyu; Zhang, Benguo; Tang, Shengyang; Yang, Zirun; Chen, Yong; Yang, Wenchao

    2016-01-01

    Reduced graphene oxide/copper (rGO/Cu) composites incorporated with nano-SiO 2 particles were successfully fabricated using the raw materials of GO dispersion, hydrophilic nano-SiO 2 and electrolytic Cu powder. The as-prepared composites were characterized by X-ray diffraction, field-emission scanning electron microscope and energy dispersive spectroscopy. Microstructural observation of the composite powders indicated that the graphene oxide (GO) was effectively reduced by N 2 H 4 ·H 2 O addition in the composite slurry, and the nano-SiO 2 particles and rGO sheets were randomly and completely mixed with Cu particles. The as-sintered composites exhibited the small rGO agglomerations in the Cu matrix, and the more nano-SiO 2 additions led to the agglomerations increase. The mechanical property testing revealed that rGO/Cu composites with nano-SiO 2 incorporation exhibited the higher hardness and strength, compared with the rGO/Cu composite and as-cast pure Cu. However, the strengthening in the composites with higher SiO 2 content accompanied with the expense of compressive ductility. Microstructural formation and strengthening mechanism of the composites are also discussed in details. - Highlights: • Nano-SiO 2 incorporated rGO/Cu composites were successfully fabricated. • The more nano-SiO 2 additions led to the agglomerations increase in the composites. • The nano-SiO 2 incorporated composites exhibited the better hardness and strength. • The formation and strengthening mechanism of the composite was discussed in detail.

  2. Synthesis of Nanoscale CaO-Al2O3-SiO2-H2O and Na2O-Al2O3-SiO2-H2O Using the Hydrothermal Method and Their Characterization

    Directory of Open Access Journals (Sweden)

    Jingbin Yang

    2017-06-01

    Full Text Available C-A-S-H (CaO-Al2O3-SiO2-H2O and N-A-S-H (Na2O-Al2O3-SiO2-H2O have a wide range of chemical compositions and structures and are difficult to separate from alkali-activated materials. Therefore, it is difficult to analyze their microscopic properties directly. This paper reports research on the synthesis of C-A-S-H and N-A-S-H particles with an average particle size smaller than 300 nm by applying the hydrothermal method. The composition and microstructure of the products with different CaO(Na2O/SiO2 ratios and curing conditions were characterized using XRD, the RIR method, FTIR, SEM, TEM, and laser particle size analysis. The results showed that the C-A-S-H system products with a low CaO/SiO2 ratio were mainly amorphous C-A-S-H gels. With an increase in the CaO/SiO2 ratio, an excess of Ca(OH2 was observed at room temperature, while in a high-temperature reaction system, katoite, C4AcH11, and other crystallized products were observed. The katoite content was related to the curing temperature and the content of Ca(OH2 and it tended to form at a high-temperature and high-calcium environment, and an increase in the temperature renders the C-A-S-H gels more compact. The main products of the N-A-S-H system at room temperature were amorphous N-A-S-H gels and a small amount of sodalite. An increase in the curing temperature promoted the formation of the crystalline products faujasite and zeolite-P. The crystallization products consisted of only zeolite-P in the high-temperature N-A-S-H system and its content were stable above 70%. An increase in the Na2O/SiO2 ratio resulted in more non-bridging oxygen and the TO4 was more isolated in the N-A-S-H structure. The composition and microstructure of the C-A-S-H and N-A-S-H system products synthesized by the hydrothermal method were closely related to the ratio of the raw materials and the curing conditions. The results of this study increase our understanding of the hydration products of alkali

  3. Multi-length-scale Material Model for SiC/SiC Ceramic-Matrix Composites (CMCs): Inclusion of In-Service Environmental Effects

    Science.gov (United States)

    Grujicic, M.; Galgalikar, R.; Snipes, J. S.; Ramaswami, S.

    2016-01-01

    In our recent work, a multi-length-scale room-temperature material model for SiC/SiC ceramic-matrix composites (CMCs) was derived and parameterized. The model was subsequently linked with a finite-element solver so that it could be used in a general room-temperature, structural/damage analysis of gas-turbine engine CMC components. Due to its multi-length-scale character, the material model enabled inclusion of the effects of fiber/tow (e.g., the volume fraction, size, and properties of the fibers; fiber-coating material/thickness; decohesion properties of the coating/matrix interfaces; etc.) and ply/lamina (e.g., the 0°/90° cross-ply versus plain-weave architectures, the extent of tow crimping in the case of the plain-weave plies, cohesive properties of the inter-ply boundaries, etc.) length-scale microstructural/architectural parameters on the mechanical response of the CMCs. One of the major limitations of the model is that it applies to the CMCs in their as-fabricated conditions (i.e., the effect of prolonged in-service environmental exposure and the associated material aging-degradation is not accounted for). In the present work, the model is upgraded to include such in-service environmental-exposure effects. To demonstrate the utility of the upgraded material model, it is used within a finite-element structural/failure analysis involving impact of a toboggan-shaped turbine shroud segment by a foreign object. The results obtained clearly revealed the effects that different aspects of the in-service environmental exposure have on the material degradation and the extent of damage suffered by the impacted CMC toboggan-shaped shroud segment.

  4. Microstructural evolution and mechanical properties of Ti3SiC2-TiC composites

    International Nuclear Information System (INIS)

    Tian, WuBian; Sun, ZhengMing; Hashimoto, Hitoshi; Du, YuLei

    2010-01-01

    Ti 3 SiC 2 -TiC composites were fabricated by pulse discharge sintering technique using three different sets of powder mixtures, i.e. Ti/Si/TiC (TC30), Ti/Si/C/TiC (SI30) and Ti/Si/C (TSC30). Based on X-ray diffraction (XRD) analysis and microstructural observations, starting powder reactants were found to have little effect on phase content but strong influence on the microstructure in terms of phase distribution. The phase distribution mainly relies on the heat released from reaction and the liquid phase content formed during sintering. The mechanical properties of the fabricated dense samples demonstrate that more homogeneous phase distribution, available by choosing the starting reactants of SI30, results in higher flexural strength, whereas the Vickers hardness is almost independent of the microstructure. The enhanced flexural strength in sample SI30 sintered at 1400 o C is mainly attributed to the homogeneous TiC distribution in the microstructure.

  5. Microstructure and thermal properties of Cu-SiC composite materials depending on the sintering technique

    Directory of Open Access Journals (Sweden)

    Chmielewski Marcin

    2017-01-01

    Full Text Available The presented paper investigates the relationship between the microstructure and thermal properties of copper-silicon carbide composites obtained through hot pressing (HP and spark plasma sintering (SPS techniques. The microstructural analysis showed a better densification in the case of composites sintered in the SPS process. TEM investigations revealed the presence of silicon in the area of metallic matrix in the region close to metal-ceramic boundary. It is the product of silicon dissolving process in copper occurring at an elevated temperature. The Cu-SiC interface is significantly defected in composites obtained through the hot pressing method, which has a major influence on the thermal conductivity of materials.

  6. Microstructural characterization of hybrid CFRP/SiC composites

    International Nuclear Information System (INIS)

    Von Dollinger, C.F.A.; Pardini, L.C.; Alves, S.C.N.

    2016-01-01

    In present work a hybrid matrix C-C/SiC composites were produced. Carbon fiber fabric was impregnated with phenolic resin mixed with powder Si in proportions of 5%, 10%, 15% e 20%wt. Optical microscopy under reflected light and polarized light were used in order to characterize samples in the as molded condition and after carbonization at 1000°C, and heat treatment 1600°C in order to react carbon and liquid silicon in order to form in situ SiC . The pore volume fraction ranges from 33% to 41% for composites after heat treatment at 1600°C due to volatiles released specially during carbonization process. Complementary analyses were done by Scanning Electron microscopy (SEM) and X-Ray diffraction to confirm in situ conversion of SiC. The results showed that the impregnation of a carbon fabric with phenolic resin added with silicon proved to be an alternative route to produce CFRP/SiC composites. (author)

  7. Controlled surface chemistry of diamond/β-SiC composite films for preferential protein adsorption.

    Science.gov (United States)

    Wang, Tao; Handschuh-Wang, Stephan; Yang, Yang; Zhuang, Hao; Schlemper, Christoph; Wesner, Daniel; Schönherr, Holger; Zhang, Wenjun; Jiang, Xin

    2014-02-04

    Diamond and SiC both process extraordinary biocompatible, electronic, and chemical properties. A combination of diamond and SiC may lead to highly stable materials, e.g., for implants or biosensors with excellent sensing properties. Here we report on the controllable surface chemistry of diamond/β-SiC composite films and its effect on protein adsorption. For systematic and high-throughput investigations, novel diamond/β-SiC composite films with gradient composition have been synthesized using the hot filament chemical vapor deposition (HFCVD) technique. As revealed by scanning electron microscopy (SEM), the diamond/β-SiC ratio of the composite films shows a continuous change from pure diamond to β-SiC over a length of ∼ 10 mm on the surface. X-ray photoelectron spectroscopy (XPS) and time-of-flight secondary ion mass spectrometry (ToF-SIMS) was employed to unveil the surface termination of chemically oxidized and hydrogen treated surfaces. The surface chemistry of the composite films was found to depend on diamond/β-SiC ratio and the surface treatment. As observed by confocal fluorescence microscopy, albumin and fibrinogen were preferentially adsorbed from buffer: after surface oxidation, the proteins preferred to adsorb on diamond rather than on β-SiC, resulting in an increasing amount of proteins adsorbed to the gradient surfaces with increasing diamond/β-SiC ratio. By contrast, for hydrogen-treated surfaces, the proteins preferentially adsorbed on β-SiC, leading to a decreasing amount of albumin adsorbed on the gradient surfaces with increasing diamond/β-SiC ratio. The mechanism of preferential protein adsorption is discussed by considering the hydrogen bonding of the water self-association network to OH-terminated surfaces and the change of the polar surface energy component, which was determined according to the van Oss method. These results suggest that the diamond/β-SiC gradient film can be a promising material for biomedical applications which

  8. TiC/Ti3SiC2复合材料的制备及其性能研究%Preparation and properties of TiC/Ti3SiC2 composites

    Institute of Scientific and Technical Information of China (English)

    贾换; 尹洪峰; 袁蝴蝶; 杨祎诺

    2012-01-01

    以粉末Ti,Si,TiC和炭黑为原料,采用反应热压烧结法制备TiC/Ti3SiC2复合材料.借助XRD和SEM研究TiC含量对TiC/Ti3SiC2复合材料相组成、显微结构及力学特性的影响.结果表明:通过热压烧结可以得到致密度较高的TiC/Ti3SiC2复合材料;引入TiC可以促进Ti3SiC2的生成,当引入TiC的质量分数达30%,TiC/Ti3SiC2复合材料的弯曲强度和断裂韧性分别为406.9 MPa,3.7 MPa·m1/2;复合材料中Ti3SiC2相以穿晶断裂为主,TiC晶粒易产生拔出.%TiC/Ti3SiC2 composites were fabricated by reactive hot pressing sintering method using the mixture powder of Ti, Si, C and TiC as raw material. The effect of TiC content on phase composition, microstructure and mechanical properties of TiC/Ti3SiC2 composites was investigated by X-ray diffraction and scanning electron microscopy. The results demonstrate that dense TiC/ Ti3SiC2 composites can be obtained by hot pressing. The addition of TiC into composites can enhance the formation of TisSiC2. When the additional content of TiC reaches 30% (mass fraction) , the flexural strength and fracture toughness of TiC/Ti3SiC2 composite are 406.9 MPa and 3.7 MPa·m-2, respectively. Ti3SiC2 phase displays intergranular fracture and TiC grain pulls out from Ti3SiC2 matrix when TiC/Ti3SiC2 composite fractures.

  9. ZnO epitaxy on SiC(0001-bar) substrate: Comparison with ZnO/SiC(0 0 0 1) heterostructure

    International Nuclear Information System (INIS)

    Ashrafi, Almamun; Aminuzzaman, Mohammod

    2011-01-01

    ZnO thin layers deposited on 6H-SiC substrates showed six-fold crystal symmetry with an epitaxial relationship of (0 0 0 2) ZnO ||(0 0 0 6) SiC and [112-bar 0] ZnO ||[112-bar 0] SiC . Despite the different 6H-SiC substrate surface orientations for the ZnO epitaxy, the orientation relationship of ZnO/6H-SiC heterostructures is identical, as confirmed by X-ray diffraction studies. In these ZnO/6H-SiC(0 0 0 1) and ZnO/6H-SiC(0001-bar) heterostructures, the valence band offsets are measured to be 1.12 eV and 1.09 eV, leading to the conduction band offset values of 0.75 eV and 0.72 eV, respectively. These slightly different band-offset values in ZnO/6H-SiC heterojunctions are attributed to the variation of valence band maximums and the different interface charge compensation mechanisms.

  10. Biomorphous SiSiC/Al-Si ceramic composites manufactured by squeeze casting: microstructure and mechanical properties

    Energy Technology Data Exchange (ETDEWEB)

    Zollfrank, C.; Travitzky, N.; Sieber, H.; Greil, P. [Department of Materials Science, Glass and Ceramics, University of Erlangen-Nuernberg (Germany); Selchert, T. [Advanced Ceramics Group, Technical University of Hamburg-Harburg (Germany)

    2005-08-01

    SiSiC/Al-Si composites were fabricated by pressure-assisted infiltration of an Al-Si alloy into porous biocarbon preforms derived from the rattan palm. Al-Si alloy was found in the pore channels of the biomorphous SiSiC preform, whereas SiC and carbon were present in the struts. The formation of a detrimental Al{sub 4}C{sub 3}-phase was not observed in the composites. A bending strength of 200 MPa was measured. The fractured surfaces showed pull-out of the Al-alloy. (Abstract Copyright [2005], Wiley Periodicals, Inc.)

  11. Characterization on C/SiC Ceramic Matrix Composites with Novel Fiber Coatings

    Science.gov (United States)

    Petko, Jeanne; Kiser, J. Douglas; McCue, Terry; Verrilli, Michael

    2002-01-01

    Ceramic Matrix Composites (CMCs) are attractive candidate materials in the aerospace industry due to their high specific strength, low density and higher temperature capabilities. The National Aeronautics and Space Administration (NASA) is pursuing the use of CMC components in advanced Reusable Launch Vehicle (RLV) propulsion applications. Carbon fiber-reinforced silicon carbide (C/SiC) is the primary material of interest for a variety of RLV propulsion applications. These composites offer high- strength carbon fibers and a high modulus, oxidation-resistant matrix. For comparison, two types of carbon fibers were processed with novel types of interface coatings (multilayer and pseudoporous). For RLV propulsion applications, environmental durability will be critical. The coatings show promise of protecting the carbon fibers from the oxidizing environment. The strengths and microstructures of these composite materials are presented.

  12. Development of the fabrication process of SiC composite by polycarbosilane

    International Nuclear Information System (INIS)

    Park, Ji Yeon; Kim, Weon Ju; Kim, Jung Il; Ryu, Woo Seog

    2004-11-01

    This technical report reviewed the fabrication process of fiber reinforced ceramic composites, characteristics of the PIP process, and applications of SiC f /SiC composite to develop a silicon carbide composite by PIP method. Additionally, characteristics and thermal behaviors of a PCS+SiC powder slurry and infiltration behaviors of slurry into the SiC fabric was evaluated. The stacking behaviors of SiC fabrics infiltrated a PCS+SiC powder slurry was also investigated. Using this stacked preforms, SiC f /SiC composites were fabricated by the electron beam curing and pyrolysis process and the thermal oxidation curing and pyrolysis process, respectively. And the characteristics of both composites were compared

  13. SiC Nanofibers as Long-Life Lithium-Ion Battery Anode Materials

    Directory of Open Access Journals (Sweden)

    Xuejiao Sun

    2018-05-01

    Full Text Available The development of high energy lithium-ion batteries (LIBs has spurred the designing and production of novel anode materials to substitute currently commercial using graphitic materials. Herein, twisted SiC nanofibers toward LIBs anode materials, containing 92.5 wt% cubic β-SiC and 7.5 wt% amorphous C, were successfully synthesized from resin-silica composites. The electrochemical measurements showed that the SiC-based electrode delivered a stable reversible capacity of 254.5 mAh g−1 after 250 cycles at a current density of 0.1 A g−1. It is interesting that a high discharge capacity of 540.1 mAh g−1 was achieved after 500 cycles at an even higher current density of 0.3 A g−1, which is higher than the theoretical capacity of graphite. The results imply that SiC nanomaterials are potential anode candidate for LIBs with high stability due to their high structure stability as supported with the transmission electron microscopy images.

  14. SiC Nanofibers as Long-Life Lithium-Ion Battery Anode Materials.

    Science.gov (United States)

    Sun, Xuejiao; Shao, Changzhen; Zhang, Feng; Li, Yi; Wu, Qi-Hui; Yang, Yonggang

    2018-01-01

    The development of high energy lithium-ion batteries (LIBs) has spurred the designing and production of novel anode materials to substitute currently commercial using graphitic materials. Herein, twisted SiC nanofibers toward LIBs anode materials, containing 92.5 wt% cubic β-SiC and 7.5 wt% amorphous C, were successfully synthesized from resin-silica composites. The electrochemical measurements showed that the SiC-based electrode delivered a stable reversible capacity of 254.5 mAh g -1 after 250 cycles at a current density of 0.1 A g -1 . It is interesting that a high discharge capacity of 540.1 mAh g -1 was achieved after 500 cycles at an even higher current density of 0.3 A g -1 , which is higher than the theoretical capacity of graphite. The results imply that SiC nanomaterials are potential anode candidate for LIBs with high stability due to their high structure stability as supported with the transmission electron microscopy images.

  15. Experimental design and analysis for irradiation of SiC/SiC composite tubes under a prototypic high heat flux

    Science.gov (United States)

    Petrie, Christian M.; Koyanagi, Takaaki; McDuffee, Joel L.; Deck, Christian P.; Katoh, Yutai; Terrani, Kurt A.

    2017-08-01

    The purpose of this work is to design an irradiation vehicle for testing silicon carbide (SiC) fiber-reinforced SiC matrix composite cladding materials under conditions representative of a light water reactor in order to validate thermo-mechanical models of stress states in these materials due to irradiation swelling and differential thermal expansion. The design allows for a constant tube outer surface temperature in the range of 300-350 °C under a representative high heat flux (∼0.66 MW/m2) during one cycle of irradiation in an un-instrumented ;rabbit; capsule in the High Flux Isotope Reactor. An engineered aluminum foil was developed to absorb the expansion of the cladding tubes, due to irradiation swelling, without changing the thermal resistance of the gap between the cladding and irradiation capsule. Finite-element analyses of the capsule were performed, and the models used to calculate thermal contact resistance were validated by out-of-pile testing and post-irradiation examination of the foils and passive SiC thermometry. Six irradiated cladding tubes (both monoliths and composites) were irradiated and subsequently disassembled in a hot cell. The calculated temperatures of passive SiC thermometry inside the capsules showed good agreement with temperatures measured post-irradiation, with two calculated temperatures falling within 10 °C of experimental measurements. The success of this design could lead to new opportunities for irradiation applications with materials that suffer from irradiation swelling, creep, or other dimensional changes that can affect the specimen temperature during irradiation.

  16. Experimental design and analysis for irradiation of SiC/SiC composite tubes under a prototypic high heat flux

    Energy Technology Data Exchange (ETDEWEB)

    Petrie, Christian M. [Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States); Koyanagi, Takaaki [Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States); McDuffee, Joel L. [Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States); Deck, Christian P. [General Atomics, San Diego, CA (United States); Katoh, Yutai [Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States); Terrani, Kurt A. [Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States)

    2017-05-04

    The purpose of this work is to design an irradiation vehicle for testing silicon carbide (SiC) fiber-reinforced SiC matrix composite cladding materials under conditions representative of a light water reactor in order to validate thermo-mechanical models of stress states in these materials due to irradiation swelling and differential thermal expansion. The design allows for a constant tube outer surface temperature in the range of 300–350 °C under a representative high heat flux (~0.66 MW/m2) during one cycle of irradiation in an un-instrumented “rabbit” capsule in the High Flux Isotope Reactor. An engineered aluminum foil was developed to absorb the expansion of the cladding tubes, due to irradiation swelling, without changing the thermal resistance of the gap between the cladding and irradiation capsule. Finite-element analyses of the capsule were performed, and the models used to calculate thermal contact resistance were validated by out-of-pile testing and post-irradiation examination of the foils and passive SiC thermometry. Six irradiated cladding tubes (both monoliths and composites) were irradiated and subsequently disassembled in a hot cell. The calculated temperatures of passive SiC thermometry inside the capsules showed good agreement with temperatures measured post-irradiation, with two calculated temperatures falling within 10 °C of experimental measurements. Furthermore, the success of this design could lead to new opportunities for irradiation applications with materials that suffer from irradiation swelling, creep, or other dimensional changes that can affect the specimen temperature during irradiation.

  17. Wear-triggered self-healing behavior on the surface of nanocrystalline nickel aluminum bronze/Ti3SiC2 composites

    Science.gov (United States)

    Zhai, Wenzheng; Lu, Wenlong; Zhang, Po; Wang, Jian; Liu, Xiaojun; Zhou, Liping

    2018-04-01

    Self-healing can protect materials from diverse damages, but is intrinsically difficult in metals. This paper demonstrates a potential method through a simultaneous decomposition and oxidation of Ti3SiC2 to achieve healing of stress cracking on the surface of nickel aluminum bronze (NAB)/Ti3SiC2 nanocrystalline composites during fretting wear. At the finest nanocrystalline materials, a crack recovery would be attained at 76.5%. The repetitive fretting wear leads to a modest amount of 'flowability' of Ti3SiC2 toward the crack, facilitating crack recovery. Along with the wear-triggered self-healing, the NAB/Ti3SiC2 shows an improved tribological performance with the stable decreased friction torque due to the formation of lubrication TiO2 oxide.

  18. Microstructure Evolution and Durability of Advanced Environmental Barrier Coating Systems for SiC/SiC Ceramic Matrix Composites

    Science.gov (United States)

    Zhu, Dongming; Evans, Laura J.; McCue, Terry R.; Harder, Bryan

    2016-01-01

    Environmental barrier coated SiC-SiC ceramic matrix composites (CMCs) systems will play a crucial role in next generation turbine engines for hot-section component applications because of their ability to significantly increase engine operating temperatures with improved efficiency, reduce engine weight and cooling requirements. Advanced HfO2 and rare earth silicate environmental barrier coatings (EBCs), along with multicomponent hafnium and rare earth silicide EBC bond coats have been developed. The coating degradation mechanisms in the laboratory simulated engine thermal cycling, and fatigue-creep operating environments are also being investigated. This paper will focus on the microstructural and compositional evolutions of an advanced environmental barrier coating system on a SiC-SiC CMC substrate during the high temperature simulated durability tests, by using a Field Emission Gun Scanning Electron Microscopy, Energy Dispersive Spectroscopy (EDS) and Wavelength Dispersive Spectroscopy (WDS). The effects of Calcium-Magnesium-Alumino-Silicate (CMAS) from road sand or volcano-ash deposits on the degradation mechanisms of the environmental barrier coating systems will also be discussed. The detailed analysis results help understand the EBC-CMC system performance, aiming at the durability improvements to achieve more robust, prime-reliant environmental barrier coatings.

  19. Optimizing Thermal-Elastic Properties of C/C–SiC Composites Using a Hybrid Approach and PSO Algorithm

    Science.gov (United States)

    Xu, Yingjie; Gao, Tian

    2016-01-01

    Carbon fiber-reinforced multi-layered pyrocarbon–silicon carbide matrix (C/C–SiC) composites are widely used in aerospace structures. The complicated spatial architecture and material heterogeneity of C/C–SiC composites constitute the challenge for tailoring their properties. Thus, discovering the intrinsic relations between the properties and the microstructures and sequentially optimizing the microstructures to obtain composites with the best performances becomes the key for practical applications. The objective of this work is to optimize the thermal-elastic properties of unidirectional C/C–SiC composites by controlling the multi-layered matrix thicknesses. A hybrid approach based on micromechanical modeling and back propagation (BP) neural network is proposed to predict the thermal-elastic properties of composites. Then, a particle swarm optimization (PSO) algorithm is interfaced with this hybrid model to achieve the optimal design for minimizing the coefficient of thermal expansion (CTE) of composites with the constraint of elastic modulus. Numerical examples demonstrate the effectiveness of the proposed hybrid model and optimization method. PMID:28773343

  20. Crystallization kinetics of BaO-Al2O3-SiO2 glasses

    Science.gov (United States)

    Bansal, Narottam P.; Hyatt, Mark J.

    1989-01-01

    Barium aluminosilicate glasses are being investigated as matrix materials in high-temperature ceramic composites for structural applications. Kinetics of crystallization of two refractory glass compositions in the barium aluminosilicate system were studied by differential thermal analysis (DTA), X-ray diffraction (XRD), and scanning electron microscopy (SEM). From variable heating rate DTA, the crystallization activation energies for glass compositions (wt percent) 10BaO-38Al2O3-51SiO2-1MoO3 (glass A) and 39BaO-25Al2O3-35SiO2-1MoO3 (glass B) were determined to be 553 and 558 kJ/mol, respectively. On thermal treatment, the crystalline phases in glasses A and B were identified as mullite (3Al2O3-2SiO2) and hexacelsian (BaO-Al2O3-2SiO2), respectively. Hexacelsian is a high-temperature polymorph which is metastable below 1590 C. It undergoes structural transformation into the orthorhombic form at approximately 300 C accompanied by a large volume change which is undesirable for structural applications. A process needs to be developed where stable monoclinic celsian, rather than hexacelsian, precipitates out as the crystal phase in glass B.

  1. ZnO epitaxy on SiC(0001-bar) substrate: Comparison with ZnO/SiC(0 0 0 1) heterostructure

    Energy Technology Data Exchange (ETDEWEB)

    Ashrafi, Almamun, E-mail: ash2phy@gmail.com [Department of Physics, University of Vermont, VT 05405 (United States); Aminuzzaman, Mohammod [Department of Chemical Science, Universiti Tunku Abdul Rahman, Perak (Malaysia)

    2011-05-01

    ZnO thin layers deposited on 6H-SiC substrates showed six-fold crystal symmetry with an epitaxial relationship of (0 0 0 2){sub ZnO}||(0 0 0 6){sub SiC} and [112-bar 0]{sub ZnO}||[112-bar 0]{sub SiC}. Despite the different 6H-SiC substrate surface orientations for the ZnO epitaxy, the orientation relationship of ZnO/6H-SiC heterostructures is identical, as confirmed by X-ray diffraction studies. In these ZnO/6H-SiC(0 0 0 1) and ZnO/6H-SiC(0001-bar) heterostructures, the valence band offsets are measured to be 1.12 eV and 1.09 eV, leading to the conduction band offset values of 0.75 eV and 0.72 eV, respectively. These slightly different band-offset values in ZnO/6H-SiC heterojunctions are attributed to the variation of valence band maximums and the different interface charge compensation mechanisms.

  2. Electrical properties of the n-ZnO/c-Si heterojunction prepared by chemical spray pyrolysis

    International Nuclear Information System (INIS)

    Romero, R.; Lopez, M.C.; Leinen, D.; Martin, F.; Ramos-Barrado, J.R.

    2004-01-01

    Electrical, structural and compositional properties of n-ZnO/c-Si heterojunctions prepared by chemical spray pyrolysis on single-crystal n-type and p-type monocrystalline silicon(1 0 0) substrates are examined with the C-V method and admittance spectroscopy at temperature ranges between 223 and 373 K. The n-ZnO/c-Si heterojunctions show a height barrier consistent with the difference in energy of the work functions of Si and ZnO; however, the n-ZnO:Al/c-Si heterojunctions present a more complex behavior due to the defects at or near the n-ZnO:Al/c-Si interface, causing a Fermi energy pinning

  3. Analysis on the sequence of formation of Ti{sub 3}SiC{sub 2} and Ti{sub 3}SiC{sub 2}/SiC composites

    Energy Technology Data Exchange (ETDEWEB)

    Radhakrishnan, R.; Bhaduri, S.B. [Idaho Univ., Moscow, ID (United States). Dept. of Mining and Metallurgy; Henager, C.H. Jr. [Pacific Northwest Lab., Richland, WA (United States)

    1995-05-01

    Ti{sub 3}SiC{sub 2}, a compound in the ternary Ti-Si-C system, is reported to be ductile. This paper reports the sequence of formation of Ti{sub 3}SiC{sub 2} and Ti{sub 3}SiC{sub 2}/SiC composites involving either combustion synthesis or by displacement reaction, respectively. Onset of exothermic reaction temperatures were determined using Differential Thermal Analysis (DTA). Phases present after the exothermic temperatures were analyzed by X-Ray diffraction. Based on these observations, a route to formation of Ti{sub 3}SiC{sub 2} and Ti{sub 3}SiC{sub 2}/SiC composites is proposed for the two`s thesis methods.

  4. SiO2-coated LiNi0.915Co0.075Al0.01O2 cathode material for rechargeable Li-ion batteries.

    Science.gov (United States)

    Zhou, Pengfei; Zhang, Zhen; Meng, Huanju; Lu, Yanying; Cao, Jun; Cheng, Fangyi; Tao, Zhanliang; Chen, Jun

    2016-11-24

    We reported a one-step dry coating of amorphous SiO 2 on spherical Ni-rich layered LiNi 0.915 Co 0.075 Al 0.01 O 2 (NCA) cathode materials. Combined characterization of XRD, EDS mapping, and TEM indicates that a SiO 2 layer with an average thickness of ∼50 nm was uniformly coated on the surface of NCA microspheres, without inducing any change of the phase structure and morphology. Electrochemical tests show that the 0.2 wt% SiO 2 -coated NCA material exhibits enhanced cyclability and rate properties, combining with better thermal stability compared with those of pristine NCA. For example, 0.2 wt% SiO 2 -coated NCA delivers a high specific capacity of 181.3 mA h g -1 with a capacity retention of 90.7% after 50 cycles at 1 C rate and 25 °C. Moreover, the capacity retention of this composite at 60 °C is 12.5% higher than that of pristine NCA at 1 C rate after 50 cycles. The effects of SiO 2 coating on the electrochemical performance of NCA are investigated by EIS, CV, and DSC tests, the improved performance is attributed to the surface coating layer of amorphous SiO 2 , which effectively suppresses side reactions between NCA and electrolytes, decreases the SEI layer resistance, and retards the growth of charge-transfer resistance, thus enhancing structural and cycling stability of NCA.

  5. Microstructure of a SiC/Ti-15-3 composite

    Science.gov (United States)

    Lerch, B. A.; Hull, D. R.; Leonhardt, T. A.

    1990-01-01

    A continuous SiC-fiber-reinforced titanium (Ti-15V-3Cr-3Sn-3A1) composite was metallographically examined. Several methods for examining composite materials were investigated and documented. Polishing techniques for this material are described. An interference layering method was developed to reveal the structure of the fiber, the reaction zone, and various phases within the matrix. Microprobe and TEM analyses were performed on the fiber-matrix interface. Detailed descriptions of the fiber distribution and the microstructure of the fiber and matrix are presented.

  6. Machinability and Tribological Properties of Stir Cast LM6/SiC/GR Hybrid Metal Matrix Composite

    Directory of Open Access Journals (Sweden)

    Tahat Montasser S.

    2016-01-01

    Full Text Available Analysis on machining characteristics in turning of LM6/SiC/Gr hybrid metal matrix composites is made of (Al-11.8%Si/SiC/Gr hybrid metal matrix composites. The process performances such as porosity, wear rate of the composites, tool wear, tool life, specific modulus, surface roughness and material removal rate with equal weight fraction of SiC and Gr particulates of 3%, 7%, 10% and 13% reinforcement are investigated. This experimental analysis and test results on the machinability of Al/SiCMMC will provide essential guidelines to the manufacturers. Hybird metal matrix composites reinforced with graphite particles posses better machinability and tribological properties.

  7. Technique development for modulus, microcracking, hermeticity, and coating evaluation capability characterization of SiC/SiC tubes

    Energy Technology Data Exchange (ETDEWEB)

    Hu, Xunxiang [Oak Ridge National Laboratory (ORNL), Oak Ridge, TN (United States); Ang, Caen K. [Oak Ridge National Laboratory (ORNL), Oak Ridge, TN (United States); Singh, Gyanender P. [Oak Ridge National Laboratory (ORNL), Oak Ridge, TN (United States); Katoh, Yutai [Oak Ridge National Laboratory (ORNL), Oak Ridge, TN (United States)

    2016-08-01

    Driven by the need to enlarge the safety margins of nuclear fission reactors in accident scenarios, research and development of accident-tolerant fuel has become an important topic in the nuclear engineering and materials community. A continuous-fiber SiC/SiC composite is under consideration as a replacement for traditional zirconium alloy cladding owing to its high-temperature stability, chemical inertness, and exceptional irradiation resistance. An important task is the development of characterization techniques for SiC/SiC cladding, since traditional work using rectangular bars or disks cannot directly provide useful information on the properties of SiC/SiC composite tubes for fuel cladding applications. At Oak Ridge National Laboratory, experimental capabilities are under development to characterize the modulus, microcracking, and hermeticity of as-fabricated, as-irradiated SiC/SiC composite tubes. Resonant ultrasound spectroscopy has been validated as a promising technique to evaluate the elastic properties of SiC/SiC composite tubes and microcracking within the material. A similar technique, impulse excitation, is efficient in determining the basic mechanical properties of SiC bars prepared by chemical vapor deposition; it also has potential for application in studying the mechanical properties of SiC/SiC composite tubes. Complete evaluation of the quality of the developed coatings, a major mitigation strategy against gas permeation and hydrothermal corrosion, requires the deployment of various experimental techniques, such as scratch indentation, tensile pulling-off tests, and scanning electron microscopy. In addition, a comprehensive permeation test station is being established to assess the hermeticity of SiC/SiC composite tubes and to determine the H/D/He permeability of SiC/SiC composites. This report summarizes the current status of the development of these experimental capabilities.

  8. Comparative study on stress in AlGaN/GaN HEMT structures grown on 6H-SiC, Si and on composite substrates of the 6H-SiC/poly-SiC and Si/poly-SiC

    International Nuclear Information System (INIS)

    Guziewicz, M; Kaminska, E; Piotrowska, A; Golaszewska, K; Domagala, J Z; Poisson, M-A; Lahreche, H; Langer, R; Bove, P

    2008-01-01

    The stresses in GaN-based HEMT structures grown on both single crystal 6H SiC(0001) and Si(111) have been compared to these in the HEMT structures grown on new composite substrates engendered as a thin monocrystalline film attached to polycrystalline 3C-SiC substrate. By using HRXRD technique and wafer curvature method we show that stress of monocrystalline layer in composite substrates of the type mono-Si/poly-SiC is lower than 100 MPa and residual stress of epitaxial GaN buffer grown on the composite substrate does not exceed 0.31 GPa, but in the cases of single crystal SiC or Si substrates the GaN buffer stress is compressive in the range of -0.5 to -0.75 GPa. The total stress of the HEMT structure calculated from strains is consistent with the averaged stress of the multilayers stack measured by wafer curvature method. The averaged stress of HEMT structure grown on single crystals is higher than those in structures grown on composites substrates

  9. Thermal shock behavior of nano-sized SiC particulate reinforced AlON composites

    Energy Technology Data Exchange (ETDEWEB)

    Zhao, X.J. [Department of Materials Science and Engineering, School of Materials and Metallurgy, Northeastern University, Shenyang, Liaoning 110004 (China); Department of Mechanical and Industrial Engineering, Ryerson University, Toronto, Ontario M5B 2K3 (Canada); Ru, H.Q., E-mail: ruhq@smm.neu.edu.cn [Department of Materials Science and Engineering, School of Materials and Metallurgy, Northeastern University, Shenyang, Liaoning 110004 (China); Chen, D.L., E-mail: dchen@ryerson.ca [Department of Mechanical and Industrial Engineering, Ryerson University, Toronto, Ontario M5B 2K3 (Canada); Zhang, N.; Liang, B. [Key Laboratory of Advanced Materials Manufacturing Technology of Liaoning Province, Shenyang University, Shenyang, Liaoning 110044 (China)

    2012-03-25

    Highlights: Black-Right-Pointing-Pointer Addition of nano-SiC particles enhances residual strength and critical temperature. Black-Right-Pointing-Pointer Young's modulus decreases with increasing quenching temperature. Black-Right-Pointing-Pointer Linear relationship between residual strength and thermal shock times is obtained. Black-Right-Pointing-Pointer Rougher fracture surfaces in the SiC-AlON composites are observed. - Abstract: Aluminum oxynitride (AlON) has been considered as a potential ceramic material for high-performance structural and advanced refractory applications. Thermal shock resistance is a major concern and an important performance index of high-temperature ceramics. While silicon carbide (SiC) particles have been proven to improve mechanical properties of AlON ceramic, the high-temperature thermal shock behavior was unknown. The aim of this investigation was to identify the thermal shock resistance and underlying mechanisms of AlON ceramic and 8 wt% SiC-AlON composites over a temperature range between 175 Degree-Sign C and 275 Degree-Sign C. The residual strength and Young's modulus after thermal shock decreased with increasing quenching temperature and thermal shock times due to large temperature gradients and thermal stresses caused by abrupt water-quenching. A linear relationship between the residual strength and thermal shock times was observed in both pure AlON and SiC-AlON composites. The addition of nano-sized SiC particles increased both residual strength and critical temperature from 200 Degree-Sign C in the monolithic AlON to 225 Degree-Sign C in the SiC-AlON composites due to the toughening effect, the lower coefficient of thermal expansion and higher thermal conductivity of SiC. The enhancement of the thermal shock resistance in the SiC-AlON composites was directly related to the change of fracture mode from intergranular cracking along with cleavage-type fracture in the AlON to a rougher fracture surface with ridge

  10. Fabrication of Multi-Layerd SiC Composite Tube for LWR Applications

    Energy Technology Data Exchange (ETDEWEB)

    Kim, Daejong; Jung, Choonghwan; Kim, Weonju; Park, Jiyeon [Korea Atomic Energy Research Institute, Daejeon (Korea, Republic of); Lee, Jongmin [Chungnam National Univ., Daejeon (Korea, Republic of)

    2013-05-15

    In this study, the chemical vapor deposition (CVD) and chemical vapor infiltration (CVI) methods were employed for the fabrication of the composite tubes. SiC ceramics and SiC-based composites have recently been studied for LWR fuel cladding applications because of good mechanical/physical properties, neutron irradiation resistance and excellent compatibility with coolant under severe accident. A multi-layered SiC composite tube as the nuclear fuel cladding is composed of the monolith SiC inner layer, SiC/SiC composite intermediate layer, and monolith SiC outer layer. Since all constituents should be highly pure, stoichiometric to achieve the good properties, it has been considered that the chemical process is a well-suited technique for the fabrication of the SiC phases.

  11. SiC Nanoparticles Toughened-SiC/MoSi2-SiC Multilayer Functionally Graded Oxidation Protective Coating for Carbon Materials at High Temperatures

    Science.gov (United States)

    Abdollahi, Alireza; Ehsani, Naser; Valefi, Zia; Khalifesoltani, Ali

    2017-05-01

    A SiC nanoparticle toughened-SiC/MoSi2-SiC functionally graded oxidation protective coating on graphite was prepared by reactive melt infiltration (RMI) at 1773 and 1873 K under argon atmosphere. The phase composition and anti-oxidation behavior of the coatings were investigated. The results show that the coating was composed of MoSi2, α-SiC and β-SiC. By the variations of Gibbs free energy (calculated by HSC Chemistry 6.0 software), it could be suggested that the SiC coating formed at low temperatures by solution-reprecipitation mechanism and at high temperatures by gas-phase reactions and solution-reprecipitation mechanisms simultaneously. SiC nanoparticles could improve the oxidation resistance of SiC/MoSi2-SiC multiphase coating. Addition of SiC nanoparticles increases toughness of the coating and prevents spreading of the oxygen diffusion channels in the coating during the oxidation test. The mass loss and oxidation rate of the SiC nanoparticle toughened-SiC/MoSi2-SiC-coated sample after 10-h oxidation at 1773 K were only 1.76% and 0.32 × 10-2 g/cm3/h, respectively.

  12. Impurities and evaluation of induced activity of SiCf/SiC composites

    International Nuclear Information System (INIS)

    Noda, Tetsuji; Araki, Hiroshi; Ito, Shinji; Fujita, Mitsutane; Maki, Koichi

    1997-01-01

    Impurity of SiC f /SiC composites prepared by CVI was analyzed by neutron activation analysis and glow discharge mass spectrometry. The evaluation of the induced activity of the composites based on the chemical compositions was made using a simulation calculation for fusion reactor blanket. Impurities of 35 elements were detected in the composites. However the total concentration of metallic impurities was below 20 mass ppm. The analyses of induced activity of the composites show that the dose rate decreases by about 5 orders of magnitude in a day after the shutdown. It is recommended that the purification of SiC fibers is necessary to reduce the activity by 10 9 after several ten years cooling of fusion reactors. (author)

  13. Use of the Materials Genome Initiative (MGI approach in the design of improved-performance fiber-reinforced SiC/SiC ceramic-matrix composites (CMCs

    Directory of Open Access Journals (Sweden)

    Jennifer S. Snipes

    2016-07-01

    Full Text Available New materials are traditionally developed using costly and time-consuming trial-and-error experimental efforts. This is followed by an even lengthier material-certification process. Consequently, it takes 10 to 20 years before a newly-discovered material is commercially employed. An alternative approach to the development of new materials is the so-called materials-by-design approach within which a material is treated as a complex hierarchical system, and its design and optimization is carried out by employing computer-aided engineering analyses, predictive tools and available material databases. In the present work, the materials-by-design approach is utilized to design a grade of fiber-reinforced (FR SiC/SiC ceramic matrix composites (CMCs, the type of materials which are currently being used in stationary components, and are considered for use in rotating components, of the hot sections of gas-turbine engines. Towards that end, a number of mathematical functions and numerical models are developed which relate CMC constituents’ (fibers, fiber coating and matrix microstructure and their properties to the properties and performance of the CMC as a whole. To validate the newly-developed materials-by-design approach, comparisons are made between experimentally measured and computationally predicted selected CMC mechanical properties. Then an optimization procedure is employed to determine the chemical makeup and processing routes for the CMC constituents so that the selected mechanical properties of the CMCs are increased to a preset target level.

  14. Interfacial push-out measurements of fully-bonded SiC/SiC composites

    International Nuclear Information System (INIS)

    Snead, L.L.; Steiner, D.; Zinkle, S.J.

    1990-01-01

    The direct measurement of interfacial bond strength and frictional resistance to sliding in a fully-bonded SiC/SiC composite is measured. It is shown that a fiber push-out technique can be utilized for small diameter fibers and very thin composite sections. Results are presented for a 22 micron thick section for which 37 out of 44 Nicalon fibers tested were pushed-out within the maximum nanoindentor load of 120 mN. Fiber interfacial yielding, push-out and sliding resistance were measured for each fiber. The distribution of interfacial strengths is treated as being Weibull in form. 14 refs., 5 figs

  15. Characterization of modified SiC@SiO2 nanocables/MnO2 and their potential application as hybrid electrodes for supercapacitors.

    Science.gov (United States)

    Zhang, Yujie; Chen, Junhong; Fan, Huili; Chou, Kuo-Chih; Hou, Xinmei

    2015-12-14

    In this research, we demonstrate a simple route for preparing SiC@SiO2 core-shell nanocables and furthermore obtain SiC@SiO2 nanocables/MnO2 as hybrid electrodes for supercapacitors using various modified methods. The modified procedure consists of mild modifications using sodium hydroxide as well as UV light irradiation and deposition of MnO2. The morphology and microstructural characteristics of the composites are investigated using XRD, XPS, FE-SEM with EDS and TEM. The results indicate that the surfaces of modified SiC@SiO2 nanocables are uniformly coated with a MnO2 thin layer. The electrochemical behaviors of the hybrid electrodes are systematically measured in a three-electrode system using cyclic voltammetry, galvanostatic charge/discharge and electrochemical impedance spectroscopy. The resultant electrode presents a superb charge storage characteristic with a large specific capacitance of 276.3 F g(-1) at the current density of 0.2 A g(-1). Moreover, the hybrid electrode also displays a long cycle life with a good capacitance retention (∼92.0%) after 1000 CV cycles, exhibiting a promising potential for supercapacitors.

  16. Synthesis of ZnFe2O4/SiO2 composites derived from a diatomite template.

    Science.gov (United States)

    Liu, Zhaoting; Fan, Tongxiang; Zhou, Han; Zhang, Di; Gong, Xiaolu; Guo, Qixin; Ogawa, Hiroshi

    2007-03-01

    A novel porous ZnFe2O4/SiO2 composite product has been generated with a template-directed assembly method from porous diatomite under different synthesis conditions, such as precursor concentrations (metallic nitrates), calcination temperature and diatomite type. The phase composition and morphology of all the materials were examined by x-ray diffraction (XRD), field emission scanning electron microscopy (FESEM) and transmission electron microscopy (TEM). The results indicated that an inherited hierarchical porous structure from the diatomite template can be obtained, and the synthesis conditions were found to have clear effects on the formation of the ZnFe2O4/SiO2 composite. The ideal composite of ZnFe2O4/SiO2 can be obtained through optimization of diatomite template type, precursor solution and calcination temperature. Furthermore, the adsorption abilities of two types of diatomites were analyzed in detail using FTIR spectra and nitrogen adsorption measurements etc, which proved that A-diatomite (Shengzhou-diatomite) is better than B-diatomite (Changbai-diatomite) on the aspect of adsorbing Zn and Fe ions, and of forming the ZnFe2O4.

  17. Si/C composite lithium-ion battery anodes synthesized using silicon nanoparticles from porous silicon

    International Nuclear Information System (INIS)

    Park, Jung-Bae; Lee, Kwan-Hee; Jeon, Young-Jun; Lim, Sung-Hwan; Lee, Sung-Man

    2014-01-01

    The synthesis of Si nanoparticles by ultrasonication processing of porous Si powder and a novel method for preparing a high-capacity Si/C composite using this technique is reported. The porous Si powder is prepared by selectively etching the silicide phase of a Ti 24 Si 76 alloy consisting of Si and silicide phases. The particle size of the nanocrystalline Si is determined by the crystallite size of the Si and silicide phases in the alloy powder. Ultrasonication of the porous Si obtained from the mechanically alloyed Ti 24 Si 76 alloy generates nanocrystalline Si particles of size about 5 nm. Growth of the Si and silicide phases in the alloy is induced by annealing of the mechanically alloyed sample, with a consequent increase in the size of the Si particles obtained after ultrasonication. Application of the ultrasonication process to the fabrication of Si/C composite anode materials generates nanometer-scale Si particles in situ that are distributed in the matrix. Analysis of the phases obtained and evaluation of the distribution of the nanometer-scale Si particles in the composites via XRD/TEM measurements show that the nanometer-scale Si particles are effectively synthesized and uniformly distributed in the carbon matrix, leading to enhanced electrochemical performance of the Si/C composites

  18. In-situ synthesis of SiO2@MOF composites for high-efficiency removal of aniline from aqueous solution

    Science.gov (United States)

    Han, Tongtong; Li, Caifeng; Guo, Xiangyu; Huang, Hongliang; Liu, Dahuan; Zhong, Chongli

    2016-12-01

    A series of SiO2@aluminum-MOF(MIL-68) composites with different SiO2 loadings have been synthesized by a simple and mild compositing strategy for high-efficiency removal of aniline. As evidenced from SEM and TEM images as well as the particle size distribution, the incorporation of SiO2 can improve the dispersity of MIL-68(Al) in composites, and result in the smaller particle size than that of pristine MIL-68(Al). Besides, the adsorption of aniline over SiO2, MIL-68(Al), the physical mixture of these two materials, and SiO2@MIL-68(Al) composites was investigated comparatively, demonstrating a relatively high adsorption capacity (531.9 mg g-1) of 7% SiO2@MIL-68(Al) towards aniline. Combining the ultrafast adsorption dynamics (reaching equilibrium within 40 s) and great reusability, 7% SiO2@MIL-68(Al) shows excellent adsorption performance. This indicates that the SiO2@MIL-68(Al) composites possess great potential applications as a kind of fascinating adsorbent in water pollution protection.

  19. Thermo-mechanical design windows for SiC/SiC composite first wall of A-SSTR2

    International Nuclear Information System (INIS)

    He Kaihui; Satoshi Nishio

    2002-01-01

    The finite element analysis and calculation is performed for the blanket first wall made of SiC/SiC composite material for Advanced Steady-state Tokamak Reactor 2, A-SSTR2, which is now conceptually designed in Naka Fusion Research Establishment, JAERI. Comparison analysis and design window is analyzed by using the finite element code ADINA 7.4. Through 2D calculation for various geometrical configurations and sensitive material properties, a fundamental guideline for first wall and blanket design is established with respect to maximum temperature, thermal and mechanical stress for many configurations. To satisfy hydrodynamic requirement, a4d4 (the dimension of coolant channel is 4 mm x 8 mm, and the distance between neighboring channels is 4 mm) is chosen as design point for high thermal conductivity up to 50 W/m·K

  20. The Properties of Nano TiO2-Geopolymer Composite as a Material for Functional Surface Application

    Directory of Open Access Journals (Sweden)

    Syamsidar D.

    2017-01-01

    Full Text Available The aim of this study is to examine the properties of Nano TiO2-geopolymer as a material for functional surface applications such as walls, floors, bench top, arts and decoration materials. Class-C fly ash and metakaolin were used as raw materials to produce geopolymers pastes (binder. Geopolymers were synthesized through alkali activation method cured at 50°C for 2 hours using molar oxide ratios of SiO2/Al2O3 = 3.0, Na2O/SiO2 = 0.2, and H2O/Na2O = 10. Nano TiO2 was added into geopolymers paste at different concentration namely 0 wt%, 5wt%, 10wt% and 15wt % relative the weight of fly ash or metakaolin. The measurements were commenced after the samples aged 7 days. The samples made from fly ash were immersed in 1 M H2SO4 solution for 3 days for acid resistance examination. The self-cleaning properties of the composites were observed by immersing the sample into red clays solution. The X-Ray Diffraction (XRD was performed to examine the structure and phase of the samples before and after acid resistance measurement. Scanning Electron Microscopy (SEM was performed to examine the surface morphology of the resulting composites. The measurements results showed that Nano TiO2–geopolymers composite can be applied as functionally surface materials.

  1. SiO{sub 2}@SnO{sub 2}/graphene composite with a coating and hierarchical structure as high performance anode material for lithium ion battery

    Energy Technology Data Exchange (ETDEWEB)

    Xu, Xingfa; Zhang, Haiyan, E-mail: hyzhang@gdut.edu.cn; Chen, Yiming; Li, Na; Li, Yunyong; Liu, Liying

    2016-08-25

    In order to ease the agglomeration and huge volume change of SnO{sub 2} particles, SnO{sub 2} nanoparticles were usually anchored on reduced graphene oxide (rGO) and used as anode materials for lithium ion batteries. Unfortunately, graphene sheets tended to overlap with adjacent ones and SnO{sub 2} nanoparticles still suffered from agglomeration and huge volume changes to some extent. In this paper, a composite SiO{sub 2}@SnO{sub 2}/rGO with coating and hierarchical structure was synthesized by a facile hydrothermal method. SnO{sub 2} nanoparticles mono-dispersed on the surface of rGO sheets and SiO{sub 2} spheres, while the SiO{sub 2}@SnO{sub 2} spheres were imbedded in the layers of rGO, which was in favor of alleviating the overlapping of graphene sheets and could make large spacious room to accommodate the huge volume changes of SnO{sub 2} nanoparticles. SiO{sub 2}@SnO{sub 2}/rGO composite also displayed good electrochemical performance. In the first charge/discharge cycle, the SiO{sub 2}@SnO{sub 2}/rGO electrode exhibited a large discharge capacity of 1548 mA h g{sup −1} at a current density of 100 mA g{sup −1} and it still retained a discharge capacity of about 600 mA h g{sup −1} after 100 cycles. - Highlights: • Anodes fabricated by using activated carbon have the highest fracture strength. • SnO{sub 2} nanoparticles are mono-dispersed on the surface of rGO sheets and SiO{sub 2} spheres. • The hierarchical structure SiO{sub 2}@SnO{sub 2}/rGO shows a good electrochemical performance.

  2. Embedded Si/Graphene Composite Fabricated by Magnesium-Thermal Reduction as Anode Material for Lithium-Ion Batteries

    Science.gov (United States)

    Zhu, Jiangliu; Ren, Yurong; Yang, Bo; Chen, Wenkai; Ding, Jianning

    2017-12-01

    Embedded Si/graphene composite was fabricated by a novel method, which was in situ generated SiO2 particles on graphene sheets followed by magnesium-thermal reduction. The tetraethyl orthosilicate (TEOS) and flake graphite was used as original materials. On the one hand, the unique structure of as-obtained composite accommodated the large volume change to some extent. Simultaneously, it enhanced electronic conductivity during Li-ion insertion/extraction. The MR-Si/G composite is used as the anode material for lithium ion batteries, which shows high reversible capacity and ascendant cycling stability reach to 950 mAh·g-1 at a current density of 50 mA·g-1 after 60 cycles. These may be conducive to the further advancement of Si-based composite anode design.

  3. Structural and optical properties of SiC-SiO2 nanocomposite thin films

    Science.gov (United States)

    Bozetine, I.; Keffous, A.; Kaci, S.; Menari, H.; Manseri, A.

    2018-03-01

    This study deals with the deposition of thin films of a SiC-SiO2nanocomposite deposited on silicon substrates. The deposition is carried out by a co-sputtering RF magnetron 13.56 MHz, using two targets a polycristallin 6H-SiC and sprigs of SiO2. In order to study the influence of the deposition time on the morphology, the structural and optical properties of the thin films produced, two series of samples were prepared, namely a series A with a 30 min deposition time and a series B of one hour duration. The samples were investigated using different characterization techniques such as Scanning Electron Microscope (SEM), X-ray Diffraction (DRX), Fourier Transform Infrared Spectroscopy (FTIR), Secondary Ion Mass Spectrometry (SIMS) and photoluminescence. The results obtained, reveal an optical gap varies between 1.4 and 2.4 eV depending on the thickness of the film; thus depending on the deposition time. The SIMS profile recorded the presence of oxygen (16O) on the surface, which the signal beneath the silicon signal (28Si) and carbon (12C) signals, which confirms that the oxide (SiO2) is the first material deposited at the interface film - substrate with an a-OSiC structure. The photoluminescence (PL) measurement exhibits two peaks, centred at 390 nm due to the oxide and at 416 nm due probably to the nanocrystals of SiC crystals, note that when the deposition time increases, the intensity of the PL drops drastically, result in agreement with dense and smooth film.

  4. Nitric acid oxidation of Si (NAOS) method for low temperature fabrication of SiO{sub 2}/Si and SiO{sub 2}/SiC structures

    Energy Technology Data Exchange (ETDEWEB)

    Kobayashi, H., E-mail: koba771@ybb.ne.jp [Institute of Scientific and Industrial Research, Osaka University, and CREST, Japan Science and Technology Agency, 8-1 Mihogaoka, Ibaraki, Osaka 567-0047 (Japan); Imamura, K.; Kim, W.-B.; Im, S.-S.; Asuha [Institute of Scientific and Industrial Research, Osaka University, and CREST, Japan Science and Technology Agency, 8-1 Mihogaoka, Ibaraki, Osaka 567-0047 (Japan)

    2010-07-15

    We have developed low temperature formation methods of SiO{sub 2}/Si and SiO{sub 2}/SiC structures by use of nitric acid, i.e., nitric acid oxidation of Si (or SiC) (NAOS) methods. By use of the azeotropic NAOS method (i.e., immersion in 68 wt% HNO{sub 3} aqueous solutions at 120 deg. C), an ultrathin (i.e., 1.3-1.4 nm) SiO{sub 2} layer with a low leakage current density can be formed on Si. The leakage current density can be further decreased by post-metallization anneal (PMA) at 200 deg. C in hydrogen atmosphere, and consequently the leakage current density at the gate bias voltage of 1 V becomes 1/4-1/20 of that of an ultrathin (i.e., 1.5 nm) thermal oxide layer usually formed at temperatures between 800 and 900 deg. C. The low leakage current density is attributable to (i) low interface state density, (ii) low SiO{sub 2} gap-state density, and (iii) high band discontinuity energy at the SiO{sub 2}/Si interface arising from the high atomic density of the NAOS SiO{sub 2} layer. For the formation of a relatively thick (i.e., {>=}10 nm) SiO{sub 2} layer, we have developed the two-step NAOS method in which the initial and subsequent oxidation is performed by immersion in {approx}40 wt% HNO{sub 3} and azeotropic HNO{sub 3} aqueous solutions, respectively. In this case, the SiO{sub 2} formation rate does not depend on the Si surface orientation. Using the two-step NAOS method, a uniform thickness SiO{sub 2} layer can be formed even on the rough surface of poly-crystalline Si thin films. The atomic density of the two-step NAOS SiO{sub 2} layer is slightly higher than that for thermal oxide. When PMA at 250 deg. C in hydrogen is performed on the two-step NAOS SiO{sub 2} layer, the current-voltage and capacitance-voltage characteristics become as good as those for thermal oxide formed at 900 deg. C. A relatively thick (i.e., {>=}10 nm) SiO{sub 2} layer can also be formed on SiC at 120 deg. C by use of the two-step NAOS method. With no treatment before the NAOS method

  5. Reciprocating Wear Behaviour of 7075Al/SiC and 6061Al/Al2O3 Composites: A study of Effect of Reinforcement, Stroke and Load

    Directory of Open Access Journals (Sweden)

    J. Lakshmipathy

    2014-06-01

    Full Text Available The wear behaviour comparison of Al/SiC and Al/Al2O3 composites prepared by stir casting technique is investigated to find out the effects of weight percentage of SiC/Al2O3, load and the number of strokes on a reciprocating wear testing machine. The MMC pins are prepared with different weight percentage of SiC and Al2O3 (10, 15 and 20 %. The tests are carried out with different load conditions (25, 50 and 75 N and different number of strokes (420,780 and 1605 strokes. Wear surfaces of tested samples are examined in Scanning Electron Microscope (SEM. Hardness test and impact test are also carried out on the MMC samples. The experimental results shows that hardness of composites increases with increase in SiC and Al2O3 particle and the impact strength decreases with increase in SiC and Al2O3 content. The volume loss of MMC specimens are less than that of the matrix alloy. The temperature rise near the contact surface of the MMC specimens increases with increase in wt% of SiC and Al2O3, load and number of strokes. The coefficient of friction decreases with increase in the number of strokes. The WVAS (Wireless Vibration Acquisition System interfaced with MAT Lab software is used to record the amplitudes during the test.

  6. Mechanical Properties and Fabrication of Nanostructured Mg_2SiO_4-MgAl_2O_4 Composites by High-Frequency Induction Heated Combustion

    International Nuclear Information System (INIS)

    Shon, In-Jin; Kang, Hyun-Su; Hong, Kyung-Tae; Doh, Jung-Mann; Yoon, Jin-Kook

    2011-01-01

    Nanopowders of MgO, Al_2O_3 and SiO_2 were made by high energy ball milling. The rapid sintering of nanostructured MgAl_2O_4-Mg_2SiO_4 composites was investigated by a high-frequency induction heating sintering process. The advantage of this process is that it allows very quick densification to near theoretical density and inhibition of grain growth. Nanocrystalline materials have received much attention as advanced engineering materials with improved physical and mechanical properties. As nanomaterials possess high strength, high hardness, excellent ductility and toughness, undoubtedly, more attention has been paid for the application of nanomaterials. Highly dense nanostructured MgAl_2O_4-Mg_2SiO_4 composites were produced with simultaneous application of 80 MPa pressure and induced output current of total power capacity (15 kW) within 2 min. The sintering behavior, gain size and mechanical properties of MgAl_2O_4-Mg_2SiO_4 composites were investigated.

  7. Process-property relationships of SiC chemical vapor deposition in the Si/H/C/O system

    International Nuclear Information System (INIS)

    Richardson, C.; Takoudis, C.G.

    1999-01-01

    The thermal, chemical, and physical properties of SiC make it an attractive material for a wide range of applications from wear resistant coatings on tools to high temperature microelectronics operations. A comprehensive thermodynamic analysis has been performed for the Si/H/C/O system from which a priori process-property relationships of the chemical vapor deposition (CVD) of silicon carbide (SiC) are obtained. The parameter space for pure silicon carbide growth is reported for five orders of magnitude of the system water vapor level (1 ppb--100 ppm), four orders of magnitude of system pressure (0.1--760 Torr), and two orders of magnitude of C/Si feed ratio (0.25--20) and H 2 /Si feed ratio (50--10,000). Lower growth temperatures for pure SiC are predicted in clean systems with low system water vapor levels, at stoichiometric to near carbon excess conditions (C/Si ≅ 1 to C/Si > 1), at high carrier gas flow rates (large H 2 /Si feed ratios), and at low operating pressures. Because relative C/Si and H 2 /Si feed ratios have been considered, the predictions in this study are applicable to both multiple and single precursor systems. Further, these results are valid for the CVD of α-SiC as well as β-SiC. Experimental data reported on the growth of α-SiC and β-SiC are found to be in satisfactory agreement with the theoretical predictions, for numerous systems that include multiple and single source, silicon and carbon, species

  8. Metastability of a-SiO{sub x}:H thin films for c-Si surface passivation

    Energy Technology Data Exchange (ETDEWEB)

    Serenelli, L., E-mail: luca.serenelli@enea.it [ENEA Research centre “Casaccia”, via Anguillarese 301, 00123 Rome (Italy); DIET University of Rome “Sapienza”, via Eudossiana 18, 00184 Rome (Italy); Martini, L. [DIET University of Rome “Sapienza”, via Eudossiana 18, 00184 Rome (Italy); Imbimbo, L. [ENEA Research centre “Casaccia”, via Anguillarese 301, 00123 Rome (Italy); DIET University of Rome “Sapienza”, via Eudossiana 18, 00184 Rome (Italy); Asquini, R. [DIET University of Rome “Sapienza”, via Eudossiana 18, 00184 Rome (Italy); Menchini, F.; Izzi, M.; Tucci, M. [ENEA Research centre “Casaccia”, via Anguillarese 301, 00123 Rome (Italy)

    2017-01-15

    Highlights: • a-SiO{sub x}:H film deposition by RF-PECVD is optimized from SiH{sub 4}, CO{sub 2} and H{sub 2} gas mixture. • Metastability of a-SiO{sub x}:H/c-Si passivation is investigated under thermal annealing and UV exposure. • A correlation between passivation metastability and Si−H bonds is found by FTIR spectra. • A metastability model is proposed. - Abstract: The adoption of a-SiO{sub x}:H films obtained by PECVD in heterojunction solar cells is a key to further increase their efficiency, because of its transparency in the UV with respect to the commonly used a-Si:H. At the same time this layer must guarantee high surface passivation of the c-Si to be suitable in high efficiency solar cell manufacturing. On the other hand the application of amorphous materials like a-Si:H and SiN{sub x} on the cell frontside expose them to the mostly energetic part of the sun spectrum, leading to a metastability of their passivation properties. Moreover as for amorphous silicon, thermal annealing procedures are considered as valuable steps to enhance and stabilize thin film properties, when performed at opportune temperature. In this work we explored the reliability of a-SiO{sub x}:H thin film layers surface passivation on c-Si substrates under UV exposition, in combination with thermal annealing steps. Both p- and n-type doped c-Si substrates were considered. To understand the effect of UV light soaking we monitored the minority carriers lifetime and Si−H and Si−O bonding, by FTIR spectra, after different exposure times to light coming from a deuterium lamp, filtered to UV-A region, and focused on the sample to obtain a power density of 50 μW/cm{sup 2}. We found a certain lifetime decrease after UV light soaking in both p- and n-type c-Si passivated wafers according to a a-SiO{sub x}:H/c-Si/a-SiO{sub x}:H structure. The role of a thermal annealing, which usually enhances the as-deposited SiO{sub x} passivation properties, was furthermore considered. In

  9. Study of SiO2/PMMA/CE tri-component interpenetrating polymer network composites

    International Nuclear Information System (INIS)

    Wang Junlong; Wang Chuang; Jiao Gengsheng; Wang Qiuya

    2010-01-01

    A technology of conjugated tri-component interpenetrating polymer networks was applied to synthesize a nano-SiO 2 /polymethylmethacrylate (PMMA)/cyanate (CE) composite through an asynchronous synthesis way. The microstructure of the composite was characterized using infrared spectroscopy (IR) and transmission electron microscopy (TEM). The mechanical properties were measured in German-made DL-1000B and XCL-40 universal material test machines, respectively. Results showed that both the impact strength and the flexural strength were in the optimum status when 3% SiO 2 /PMMA/CE was chosen as a sample with the PMMA/CE ratio of 20/80. Compared with the strengths of pure cyanate, those of the composite were raised by 137.28% and 31.29%, respectively. When 3% nano-SiO 2 was added, the impact strength was increased by 29.96% and the flexural strength by 20.05%, compared with the strengths of polymers without SiO 2 . Analysis and measurements by IR and TEM indicated that no chemical reactions took place among components in the composite. The interpenetration of the conjugated tri-component improved the loading capacity of the polymer, hence the toughness enhancement of cyanate.

  10. INVESTIGATION ON PHYSICAL AND ELECTRICAL PROPERTIES OF THE SiO2-ZnO NANOCOMPOSITE AT DIFFERENT COMPOSITION MIXINGS

    Directory of Open Access Journals (Sweden)

    Moh. Sinol

    2018-01-01

    Full Text Available Physical and electrical properties of The SiO2-ZnO mixing at different compositions were investigated. The experiment used simple mixing method at the sintering temperature 600oC. It was used the composition mixing ratio of SiO2:ZnO ie. 0:10; 7:3; 5:5; 3:7; and 10:0 (%Wt. Based on X-Ray Diffraction (XRD results, it obtained that a new phase in each sample was not formed even though having different diffraction peak. The mixing ratio of SiO2: ZnO nanocomposite (7:3 %wt had the biggest grain size (77,92 nm, the highest dielectric constant (3.00E+05 and the smallest conductivity (0,726549 (Ωm-1. On the other side, the mixing ratio of SiO2: ZnO nanocomposite (5:5 %wt had the smallest grain size (35.42nm, dielectric constant (3.00E+2 and the highest conductivity (25.36729  (Ωm-1. It can be concluded that the difference of composition ratio offered the change on both physical and electrical properties of SiO2-ZnO nanocomposite.

  11. Delamination Mechanisms of Thermal and Environmental Barrier Coatings on SiC/SiC Ceramic Matrix Composites

    Science.gov (United States)

    Zhu, Dongming; Choi, Sung R.; Lee, Kang N.; Miller, Robert A.

    2003-01-01

    Advanced ceramic thermal harrier coatings will play an increasingly important role In future gas turbine engines because of their ability to effectively protect the engine components and further raise engine temperatures. However, the coating durability issue remains a major concern with the ever-increasing temperature requirements. In this paper, thermal cyclic response and delamination failure modes of a ZrO2-8wt%Y2O3 and mullite/BSAS thermaVenvironmenta1 barrier coating system on SiC/SiC ceramic matrix composites were investigated using a laser high-heat-flux technique. The coating degradation and delamination processes were monitored in real time by measuring coating apparent conductivity changes during the cyclic tests under realistic engine temperature and stress gradients, utilizing the fact that delamination cracking causes an apparent decrease in the measured thermal conductivity. The ceramic coating crack initiation and propagation driving forces under the cyclic thermal loads, in conjunction with the mechanical testing results, will be discussed.

  12. Pós de Al2O3/SiC obtidos a partir de reação de redução carbotérmica Al2O3/SiC powders from carbothermal reduction reaction

    Directory of Open Access Journals (Sweden)

    F. M. Spiandorello

    1999-12-01

    Full Text Available Neste trabalho foram utilizadas matérias-primas naturais para a obtenção de pós Al2O3/SiC através da redução carbotérmica das mesmas por um agente rico em carbono. Os aluminossilicatos estudados foram caulim, cianita e ilita-moscovita, sendo que os mesmos foram reduzidos ou por negro de fumo ou por grafite. Os pós resultantes da reação foram caracterizados por microscopia eletrônica de varredura e transmissão, difração de raios X e picnometria de hélio. Durante a reação, as diferenças existentes tanto na estrutura das matérias-primas quanto na composição química produziram pós com morfologia diversa. Foram encontradas estruturas como grandes aglomerados esféricos, whiskers, partículas e aglomerados fibrosos.In this work natural raw materials were used to obtain Al2O3/SiC powders by carbothermal reduction. The aluminosilicates studied were kaolin, kyanite and illite-muscovite and the reductor agents were carbon black or graphite. The reaction powders were characterized by transmission and scanning electron microscopy, X-ray diffraction and helium picnometry. During the reaction, the differences among the raw materials structures as well as into the chemical composition produced powders with several morphologies. Big spherical agglomerates, whiskers, particles and fibrous clusters were found.

  13. Effect of Carbon in Fabrication Al-SiC Nanocomposites for Tribological Application

    Directory of Open Access Journals (Sweden)

    Bartosz Hekner

    2017-06-01

    Full Text Available Aluminium-based hybrid composites are a new class of advanced materials with the potential of satisfying the demands in engineering applications. This paper describes the effects of carbon addition on the formation and properties of AMC with SiC nanoparticles reinforcement. The composites were produced via mechanical alloying followed by hot pressing. Three forms of carbon, graphite (GR, multiwalled carbon nanotubes (CNTs, and, for the first time, glassy carbon (GC, were used for the hybrid composites manufacturing and compared with tribological properties of Al-SiC composite without carbon addition. GC and CNTs enhanced formation of Al-SiC composite particles and resulted in a homogeneous distribution of reinforcing particles. On the other hand, GR addition altered mechanochemical alloying and did not lead to a proper distribution of nanoparticulate SiC reinforcement. Hot pressing technique led to the reaction between Al and carbon as well as SiC particles and caused the formation of Al4C3 and γ-Al2O3. The subsistence of carbon particles in the composites altered the predominant wear mechanisms since the wear reduction and the stabilization of the friction coefficient were observed. GC with simultaneous γ-Al2O3 formation in the hybrid Al-SiC(n-C composites turned out to be the most effective additive in terms of their tribological behaviour.

  14. Qualification of SiC materials for fusion and fission reactors

    International Nuclear Information System (INIS)

    Ryazanov, Alexander

    2009-01-01

    Ceramic materials such as silicon carbide (SiC) and SiC/SiC composites are both considered, due to their high-temperature strength, pseudo-ductile fracture behavior and low-induced radioactivity, as candidate materials for fusion reactor (test blanket module for ITER) and high temperature gas-cooled reactors (HTGR). The radiation swelling and creep of SiC are very important physical phenomena that determine the radiation resistance of them in these reactors. Other important problem which exists especially in fusion reactor is an effect of accumulation of high concentrations of helium atoms in SiC (up to 15000-20000 at.ppm) due to (n,α) nuclear reaction on physical mechanical properties. An understanding of the physical mechanism of this phenomenon is very important for the investigations of helium atom effect on radiation swelling in SiC. In this report a compilation of non-irradiated and irradiated properties of SiC are provided and analyzed in terms of their application to fusion and high temperature gas cooled reactors. Special topic of this report is oriented on the micro structural changes in chemically vapor-deposited (CVD) high-purity beta-SiC during neutron and ion irradiations at elevated temperatures. The evolutions of various radiation induced defects including dislocation loops, network dislocations and cavities are presented here as a function of irradiation temperature and fluencies. These observations are discussed in relation with such irradiation phenomena in SiC as low temperature swelling and cavity swelling. One of the main difficulties in the radiation damage studies of SiC materials lies in the absence of theoretical models and interpretation of many physical mechanisms of radiation phenomena including the radiation swelling and creep. The point defects in ceramic materials are characterized by the charge states and they can have an effective charge. The internal effective electrical field is formed due to the accumulation of charged point

  15. Embedded Si/Graphene Composite Fabricated by Magnesium-Thermal Reduction as Anode Material for Lithium-Ion Batteries.

    Science.gov (United States)

    Zhu, Jiangliu; Ren, Yurong; Yang, Bo; Chen, Wenkai; Ding, Jianning

    2017-12-16

    Embedded Si/graphene composite was fabricated by a novel method, which was in situ generated SiO 2 particles on graphene sheets followed by magnesium-thermal reduction. The tetraethyl orthosilicate (TEOS) and flake graphite was used as original materials. On the one hand, the unique structure of as-obtained composite accommodated the large volume change to some extent. Simultaneously, it enhanced electronic conductivity during Li-ion insertion/extraction. The MR-Si/G composite is used as the anode material for lithium ion batteries, which shows high reversible capacity and ascendant cycling stability reach to 950 mAh·g -1 at a current density of 50 mA·g -1 after 60 cycles. These may be conducive to the further advancement of Si-based composite anode design.

  16. Enhanced cycle stability of micro-sized Si/C anode material with low carbon content fabricated via spray drying and in situ carbonization

    Energy Technology Data Exchange (ETDEWEB)

    Wang, Dingsheng; Gao, Mingxia, E-mail: gaomx@zju.edu.cn; Pan, Hongge; Liu, Yongfeng; Wang, Junhua; Li, Shouquan; Ge, Hongwei

    2014-08-01

    Highlights: • Micro-sized Si/C composites were fabricated via. spray drying and carbonization. • Multi-morphology carbon was formed in the Si/C composites. • Si/C composite with 5.6 wt.% C provides significant improved cycling stability. • Multi-morphology carbon plays effective role in improving the electrochemical property. • The method provides potential for mass production of superior Si-based anode materials. - Abstract: Micro-sized Si/C composites with in situ introduced carbon of multi-morphology were fabricated via spray drying a suspension of commercial micro-sized Si and citric acid followed by a carbonization. Different ratios of Si to citric acid were used to optimize the composition and structure of the composites and thus the electrochemical performance. Carbon flakes including crooked and flat ones were well dispersed in between the Si particles, forming Si/C composites. Floc-like carbon layers and carbon fragments were also found to cover partially the Si particles. The Si/C composite with a low carbon content of 5.6 wt.% provides an initial reversible capacity of 2700 mA h/g and a capacity of 1860 mA h/g after 60 cycles at a current density of 100 mA/g as anode material for lithium-ion batteries (LIBs), which are much higher than those of pristine Si and the Si/C composites with higher carbon content. The mechanism of the enhancement of electrochemical performance of the micro-sized Si/C composite is discussed. The fabrication method and the structure design of the composites offer valuable potential in developing adaptable Si-based anode materials for industrial applications.

  17. Preparation and characterization of Fe3O4/SiO2/Bi2MoO6 composite as magnetically separable photocatalyst

    International Nuclear Information System (INIS)

    Hou, Xuemei; Tian, Yanlong; Zhang, Xiang; Dou, Shuliang; Pan, Lei; Wang, Wenjia; Li, Yao; Zhao, Jiupeng

    2015-01-01

    Highlights: • Fe 3 O 4 /SiO 2 /Bi 2 MoO 6 composite was prepared by a hydrothermal method. • The composite has an enhanced visible absorption compared with pure Bi 2 MoO 6 . • The magnetic photocatalyst displayed excellent stability and reusability. • O 2 ·− and · OH play a major role during the photocatalytic process. - Abstract: In this paper, Fe 3 O 4 /SiO 2 /Bi 2 MoO 6 microspheres were prepared by a facile hydrothermal method. The scanning electron microscope (SEM) results revealed that flower-like three dimensional (3D) Bi 2 MoO 6 microspheres were decorated with Fe 3 O 4 /SiO 2 magnetic nanoparticles. The UV–vis diffuse reflection spectra showed extended absorption within the visible light range compared with pure Bi 2 MoO 6 . We evaluated the photocatalytic activities of Fe 3 O 4 /SiO 2 /Bi 2 MoO 6 microspheres on the degradation of Rhodamine B (RhB) under visible light irradiation and found that the obtained composite exhibited higher photocatalytic activity than pure Bi 2 MoO 6 and P25. Moreover, the Fe 3 O 4 /SiO 2 /Bi 2 MoO 6 composite also displayed excellent stability and their photocatalytic activity decreased slightly after reusing 5 cycles. Meanwhile, the composite could be easily separated by applying an external magnetic field. The trapping experiment results suggest that superoxide radical species O 2 ·− and hydroxyl radicals · OH play a major role in Fe 3 O 4 /SiO 2 /Bi 2 MoO 6 system under visible light irradiation. The combination of flower-like three dimensional (3D) Bi 2 MoO 6 microspheres and Fe 3 O 4 /SiO 2 magnetic nanospheres provides a useful strategy for designing multifunctional nanostructure materials with enhanced photocatalytic activities in the potential applications of water purification

  18. Sheet-like Li3V2(PO4)3 nanocomposite coated by SiO2 + C with better electrochemical properties for lithium-ion batteries

    International Nuclear Information System (INIS)

    Lai, Chunyan; Wu, Tingting; Wang, Zhen

    2016-01-01

    Sheet-like Li 3 V 2 (PO 4 ) 3 nanocomposite coated by SiO 2  + C layer was synthesized with one-step solid-state method. Dihydroxydiphenylsilane (DPSD) was used as the source of SiO 2 and C. The sheet-like Li 3 V 2 (PO 4 ) 3 nanocomposite has a thickness in the range of 20–30 nm. Because of the SiO 2  + C-coated layer and the sheet-like morphology, the Li 3 V 2 (PO 4 ) 3 /(SiO 2  + C) composites show better stability and higher capacity than pure Li 3 V 2 (PO 4 ) 3 material and granular Li 3 V 2 (PO 4 ) 3 /(SiO 2  + C) composites. The best sample, Li 3 V 2 (PO 4 ) 3 /(SiO 2  + C)(2:8), shows a discharge capacity of 193.7 mAh g −1 at 1C within the voltage range of 3.0–4.8 V and retains almost 90 % of the capacity after 50 cycles.

  19. Impurities and evaluation of induced activity of CVI SiCf/SiC composites

    International Nuclear Information System (INIS)

    Noda, Tetsuji; Fujita, Mitsutane; Araki, Hiroshi; Kohyama, Akira

    2000-01-01

    Impurity of SiC f /SiC composites prepared by CVI was analyzed by neutron activation analysis and glow discharge mass spectrometry. The evaluation of the induced activity of the composites based on the chemical compositions was made using a simulation calculation for fusion reactor blanket. Impurities of 35 elements were detected in the composites. However, the total concentration of metallic impurities was below 20 mass ppm. The analyses of induced activity of the composites show that the dose rate decreases by about six orders of magnitude in a day after the shutdown. It is recommended that the purification of SiC composites, especially reduction of Fe and Ni contents, is necessary to reduce the activity to satisfy the limit of remote handling recycling after several 10 years cooling of fusion reactors

  20. Si K-edge XANES study of SiOxCyHz amorphous polymeric materials

    International Nuclear Information System (INIS)

    Chaboy, J.; Barranco, A.; Yanguas-Gil, A.; Yubero, F.; Gonzalez-Elipe, A. R.

    2007-01-01

    This work reports on x-ray absorption spectroscopy study at the Si K edge of several amorphous SiO x C y H z polymers prepared by plasma-enhanced chemical-vapor deposition with different C/O ratios. SiO 2 and SiC have been used as reference materials. The comparison of the experimental Si K-edge x-ray absorption near-edge structure spectra with theoretical computations based on multiple scattering theory has allowed us to monitor the modification of the local coordination around Si as a function of the overall C/O ratio in this kind of materials

  1. Preparation of biomorphic SiC ceramic by carbothermal reduction of oak wood charcoal

    International Nuclear Information System (INIS)

    Qian Junmin; Wang Jiping; Jin Zhihao

    2004-01-01

    Highly porous silicon carbide (SiC) ceramic with woodlike microstructure has been prepared at 1400-1600 deg. C by carbothermal reduction reaction of charcoal/silica composites in static argon atmosphere. These composites were fabricated by infiltrating silica sol into a porous biocarbon template from oak wood using a vacuum/pressure infiltration process. The morphology of resulting porous SiC ceramic, as well as the conversion mechanism of wood to porous SiC ceramic, have been investigated by scanning electron microscopy (SEM), X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR), and thermogravimetric analysis (TGA) and differential scanning calorimetry (DSC) techniques. Experimental results show that the biomorphic cellular morphology of oak wood charcoal is remained in the porous SiC ceramic with high precision that consists of β-SiC with traces of α-SiC. Silica in the charcoal/silica composites exists in the cellular pores in form of fibers and rods. The SiC strut material is formed by gas-solid reaction between SiO (g) and C (s) during the charcoal-to-ceramic conversion. The densification of SiC strut material may occur at moderate temperatures and holding time

  2. Preparation of biomorphic SiC ceramic by carbothermal reduction of oak wood charcoal

    Energy Technology Data Exchange (ETDEWEB)

    Qian Junmin; Wang Jiping; Jin Zhihao

    2004-04-25

    Highly porous silicon carbide (SiC) ceramic with woodlike microstructure has been prepared at 1400-1600 deg. C by carbothermal reduction reaction of charcoal/silica composites in static argon atmosphere. These composites were fabricated by infiltrating silica sol into a porous biocarbon template from oak wood using a vacuum/pressure infiltration process. The morphology of resulting porous SiC ceramic, as well as the conversion mechanism of wood to porous SiC ceramic, have been investigated by scanning electron microscopy (SEM), X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR), and thermogravimetric analysis (TGA) and differential scanning calorimetry (DSC) techniques. Experimental results show that the biomorphic cellular morphology of oak wood charcoal is remained in the porous SiC ceramic with high precision that consists of {beta}-SiC with traces of {alpha}-SiC. Silica in the charcoal/silica composites exists in the cellular pores in form of fibers and rods. The SiC strut material is formed by gas-solid reaction between SiO (g) and C (s) during the charcoal-to-ceramic conversion. The densification of SiC strut material may occur at moderate temperatures and holding time.

  3. Joining SiC/SiC composites for fusion applications

    International Nuclear Information System (INIS)

    Henager, C.J.

    2007-01-01

    Full text of publication follows: The use of SiC-reinforced composites for fusion reactors or other nuclear applications will likely require some form of joining in order to form large structural or functional sections. Joints must be able to allow load transfer to the composite material so that the fiber reinforcements are able to carry their designed loads and the joint should not fail in a brittle manner. In addition, joints must be tolerant of radiation damage similar to the composite material to maintain the structural integrity of the joined section. Other requirements of interest are low activation joints and ease of joining application and processing, which are a difficult set of criteria to meet. Research at PNNL has been directed at high-strength joints using solid-state displacement reactions and pre-ceramic polymer joints that are easy to apply and that could be used in field repair situations. This research will report on the further development and testing of such joints using a double notch shear (DNS) specimen that is suitable for in-reactor testing. The results reveal that the solid-state joints are stronger than the polymer-based joints but require high-temperature, high-pressure processing. The polymer-based joints can be applied with reduced pressure and temperature processing compared to the solid-state joints. The polymer-based joints may have adequate strength for some applications where ease of application and in situ processing are required. Although irradiation testing is not reported in this study the use of the DNS specimen is discussed with regard to future neutron irradiations. (authors)

  4. Synthesis of graphene supported Li2SiO3 as a high performance anode material for lithium-ion batteries

    Science.gov (United States)

    Yang, Shuai; Wang, Qiufen; Miao, Juan; Zhang, Jingyang; Zhang, Dafeng; Chen, Yumei; Yang, Hong

    2018-06-01

    The Li2SiO3-graphene composite is successfully synthesized through an easy hydrothermal method. The structures and morphologies of the produced samples are characterized by X-ray diffraction, X-ray photoelectron spectroscopy, Fourier transform infrared spectrum, Brunauer-Emmett-Teller formalism, scanning electron microscope, transmission electron microscope, and electrochemistry methods. The result shows a well crystalline of the Li2SiO3-GE composite. The existence of graphene doesn't change the crystalline of Li2SiO3. In addition, the Li2SiO3 compound with an average diameter of 20 nm can be seen on the surface of graphene with uniform distribution. After the composite with graphene, the composite displays large surface area which ensures the well electrochemistry of the composite. Finally, the Li2SiO3-graphene composite delivers a high initial capacity of 878.3 mAh g-1 at 1C as well as a high recovery capacity of 400 mAh g-1 after 200 cycles. When charged and discharged at high rate, the Li2SiO3-doping graphene composite still exhibits a high specific capacity of 748.3 mAh g-1 (at 2C, and 576 mAh g-1 at 5C) and well cycling performance. The well synthesized composite possesses well structure and well electrochemistry performance.

  5. Influence of reinforcement proportion and matrix composition on pitting corrosion behaviour of cast aluminium matrix composites (A3xx.x/SiCp)

    International Nuclear Information System (INIS)

    Pardo, A.; Merino, M.C.; Merino, S.; Viejo, F.; Carboneras, M.; Arrabal, R.

    2005-01-01

    The influence of silicon carbide (SiCp) proportion and matrix composition on four aluminium metal matrix composites (A360/SiC/10p, A360/SiC/20p, A380/SiC/10p, A380/SiC/20p) immersed in 1-3.5 wt% NaCl at 22 deg C was investigated by potentiodynamic polarization. The kinetics of the corrosion process was studied on the basis of gravimetric measurements. The nature of corrosion products was analysed by scanning electron microscopy (SEM) and low angle X-ray diffraction (XRD). The corrosion damage in Al/SiCp composites was caused by pitting attack and by nucleation and growth of Al 2 O 3 . 3H 2 O on the material surface. The main attack nucleation sites were the interface region between the matrix and the reinforcement particles. The corrosion process was influenced more by the concentration of alloy elements in the matrix than by the proportion of SiCp reinforcement and saline concentration

  6. Influence of reinforcement proportion and matrix composition on pitting corrosion behaviour of cast aluminium matrix composites (A3xx.x/SiCp)

    Energy Technology Data Exchange (ETDEWEB)

    Pardo, A. [Departamento de Ciencia de Materiales, Facultad de Quimica, Universidad Complutense, 28040 Madrid (Spain)]. E-mail: anpardo@quim.ucm.es; Merino, M.C. [Departamento de Ciencia de Materiales, Facultad de Quimica, Universidad Complutense, 28040 Madrid (Spain); Merino, S. [Departamento de Tecnologia Industrial, Universidad Alfonso X El Sabio, 28691, Villanueva de la Canada, Madrid (Spain); Viejo, F. [Departamento de Ciencia de Materiales, Facultad de Quimica, Universidad Complutense, 28040 Madrid (Spain); Carboneras, M. [Departamento de Ciencia de Materiales, Facultad de Quimica, Universidad Complutense, 28040 Madrid (Spain); Arrabal, R. [Departamento de Ciencia de Materiales, Facultad de Quimica, Universidad Complutense, 28040 Madrid (Spain)

    2005-07-01

    The influence of silicon carbide (SiCp) proportion and matrix composition on four aluminium metal matrix composites (A360/SiC/10p, A360/SiC/20p, A380/SiC/10p, A380/SiC/20p) immersed in 1-3.5 wt% NaCl at 22 deg C was investigated by potentiodynamic polarization. The kinetics of the corrosion process was studied on the basis of gravimetric measurements. The nature of corrosion products was analysed by scanning electron microscopy (SEM) and low angle X-ray diffraction (XRD). The corrosion damage in Al/SiCp composites was caused by pitting attack and by nucleation and growth of Al{sub 2}O{sub 3} . 3H{sub 2}O on the material surface. The main attack nucleation sites were the interface region between the matrix and the reinforcement particles. The corrosion process was influenced more by the concentration of alloy elements in the matrix than by the proportion of SiCp reinforcement and saline concentration.

  7. Circumferential tensile test method for mechanical property evaluation of SiC/SiC tube

    Energy Technology Data Exchange (ETDEWEB)

    Yu, Ju-Hyeon, E-mail: 15096018@mmm.muroran-it.ac.jp [Graduate School, Muroran Institute of Technology, 27-1, Muroran, Hokkaido (Japan); Kishimoto, Hirotatsu [Graduate School, Muroran Institute of Technology, 27-1, Muroran, Hokkaido (Japan); OASIS, Muroran Institute of Technology, 27-1, Muroran, Hokkaido (Japan); Park, Joon-soo [OASIS, Muroran Institute of Technology, 27-1, Muroran, Hokkaido (Japan); Nakazato, Naofumi [Graduate School, Muroran Institute of Technology, 27-1, Muroran, Hokkaido (Japan); Kohyama, Akira [OASIS, Muroran Institute of Technology, 27-1, Muroran, Hokkaido (Japan)

    2016-11-01

    Highlights: • NITE SiC/SiC cooling channel system to be a candidate of divertor system in future. • Hoop strength is one of the important factors for a tube. • This research studies the relationship between deformation and strain of SiC/SiC tube. - Abstract: SiC fiber reinforced/SiC matrix (SiC/SiC) composite is expected to be a candidate material for the first-wall, components in the blanket and divertor of fusion reactors in future. In such components, SiC/SiC composites need to be formed to be various shapes. SiC/SiC tubes has been expected to be employed for blanket and divertor after DEMO reactor, but there is not established mechanical investigation technique. Recent progress of SiC/SiC processing techniques is likely to realize strong, having gas tightness SiC/SiC tubes which will contribute for the development of fusion reactors. This research studies the relationship between deformation and strain of SiC/SiC tube using a circumferential tensile test method to establish a mechanical property investigation method of SiC/SiC tubes.

  8. Fracture surface analysis on nano-SiO{sub 2}/epoxy composite

    Energy Technology Data Exchange (ETDEWEB)

    Zhao Rongguo [Institute of Fundamental Mechanics and Material Engineering, Xiangtan University, Hunan 411105 (China); Key Laboratory of Low Dimensional Materials and Application Technology, Xiangtan University, Ministry of Education, Hunan 411105 (China)], E-mail: zhaorongguo@xtu.edu.cn; Luo Wenbo [Institute of Fundamental Mechanics and Material Engineering, Xiangtan University, Hunan 411105 (China); Key Laboratory of Low Dimensional Materials and Application Technology, Xiangtan University, Ministry of Education, Hunan 411105 (China)

    2008-06-15

    Fracture surface morphologies of nano-SiO{sub 2}/epoxy composite with different weight percentage of SiO{sub 2} are investigated using scanning electron microscopy. Two types of curing agent, dimethylbenzanthracene (DMBA) and methyltetrahydrophthalic anhydride (MeTHPA), are individually used for preparing the composites. It is found that the fracture surface morphology of the composite cured by DMBA shows as radial striations, which suggests a rapid brittle fracture mode, while the fracture surface morphology of the composite cured by MeTHPA shows as regularly spaced 'rib' markings, which indicates a stick-slip motion during the fracture process. Furthermore, the uniaxial tensile behavior under constant loading rate and ambient temperature are investigated. It is shown that the elastic modulus of the composite cured by DMBA firstly increases, and then decreases with the mass fraction of nano-SiO{sub 2} particles, but the elongation of the composite cured by MeTHPA is reversed with increasing fraction of nano-SiO{sub 2} particles. For nano-SiO{sub 2}/epoxy composite cured with MeTHPA that possesses a suitable fraction of nano-SiO{sub 2}, an excellent synthetic mechanical property on elastic modulus and elongation is obtained.

  9. Effects of Interface Coating and Nitride Enhancing Additive on Properties of Hi-Nicalon SiC Fiber Reinforced Reaction-Bonded Silicon Nitride Composites

    Science.gov (United States)

    Bhatt, Ramakrishana T.; Hull, David R.; Eldridge, Jeffrey I.; Babuder, Raymond

    2000-01-01

    Strong and tough Hi-Nicalon SiC fiber reinforced reaction-bonded silicon nitride matrix composites (SiC/ RBSN) have been fabricated by the fiber lay-up approach. Commercially available uncoated and PBN, PBN/Si-rich PBN, and BN/SiC coated SiC Hi-Nicalon fiber tows were used as reinforcement. The composites contained approximately 24 vol % of aligned 14 micron diameter SiC fibers in a porous RBSN matrix. Both one- and two-dimensional composites were characterized. The effects of interface coating composition, and the nitridation enhancing additive, NiO, on the room temperature physical, tensile, and interfacial shear strength properties of SiC/RBSN matrix composites were evaluated. Results indicate that for all three coated fibers, the thickness of the coatings decreased from the outer periphery to the interior of the tows, and that from 10 to 30 percent of the fibers were not covered with the interface coating. In the uncoated regions, chemical reaction between the NiO additive and the SiC fiber occurs causing degradation of tensile properties of the composites. Among the three interface coating combinations investigated, the BN/SiC coated Hi-Nicalon SiC fiber reinforced RBSN matrix composite showed the least amount of uncoated regions and reasonably uniform interface coating thickness. The matrix cracking stress in SiC/RBSN composites was predicted using a fracture mechanics based crack bridging model.

  10. Rare-earth element doped Si3N4/SiC micro/nano-composites-RT and HT mechanical properties

    Czech Academy of Sciences Publication Activity Database

    Lojanová, Š.; Tatarko, P.; Chlup, Zdeněk; Hnatko, M.; Dusza, J.; Lenčéš, Z.; Šajgalík, P.

    2010-01-01

    Roč. 30, č. 9 (2010), s. 1931-1944 ISSN 0955-2219 Institutional research plan: CEZ:AV0Z20410507 Keywords : Si3N4 * SiC * Nano-composites * Fracture toughness * Hardness * Strength * Creep Subject RIV: JH - Ceramics, Fire-Resistant Materials and Glass Impact factor: 2.574, year: 2010

  11. High ink absorption performance of inkjet printing based on SiO2@Al13 core-shell composites

    Science.gov (United States)

    Chen, YiFan; Jiang, Bo; Liu, Li; Du, Yunzhe; Zhang, Tong; Zhao, LiWei; Huang, YuDong

    2018-04-01

    The increasing growth of the inkjet market makes the inkjet printing more necessary. A composite material based on core-shell structure has been developed and applied to prepare inkjet printing layer. In this contribution, the ink printing record layers based on SiO2@Al13 core-shell composite was elaborated. The prepared core-shell composite materials were characterized by X-ray photoelectron spectroscopy (XPS), zeta potential, X-ray diffraction (XRD), scanning electron microscopy (SEM). The results proved the presence of electrostatic adsorption between SiO2 molecules and Al13 molecules with the formation of the well-dispersed system. In addition, based on the adsorption and the liquid permeability analysis, SiO2@Al13 ink printing record layer achieved a relatively high ink uptake (2.5 gmm-1) and permeability (87%), respectively. The smoothness and glossiness of SiO2@Al13 record layers were higher than SiO2 record layers. The core-shell structure facilitated the dispersion of the silica, thereby improved its ink absorption performance and made the clear printed image. Thus, the proposed procedure based on SiO2@Al13 core-shell structure of dye particles could be applied as a promising strategy for inkjet printing.

  12. Effects of neutron irradiation on the strength of continuous fiber reinforced SiC/SiC composites

    Energy Technology Data Exchange (ETDEWEB)

    Youngblood, G.E.; Henager, C.H. Jr.; Jones, R.H. [Pacific National Lab., Richland, WA (United States)

    1997-04-01

    Flexural strength data as a function of irradiation temperature and dose for a SiC{sub f}/SiC composite made with Nicalon-CG fiber suggest three major degradation mechanisms. Based on an analysis of tensile strength and microstructural data for irradiated Nicalon-CG and Hi-Nicalon fibers, it is anticipated that these degradation mechanisms will be alleviated in Hi-Nicalon reinforced composites.

  13. Liquid phase sintered SiC. Processing and transformation controlled microstructure tailoring

    Directory of Open Access Journals (Sweden)

    V.A. Izhevskyi

    2000-10-01

    Full Text Available Microstructure development and phase formation processes during sintering of silicon carbide based materials with AlN-Y2O3, AlN-Yb2O3, and AlN-La2O3 sintering additives were investigated. Densification of the materials occurred by liquid-phase sintering mechanism. Proportion of alpha- and beta-SiC powders in the initial mixtures was a variable parameter, while the molar ratio of AlN/RE2O3, and the total amount of additives (10 vol. % were kept constant. Shrinkage behavior during sintering in interrelation with the starting composition of the material and the sintering atmosphere was investigated by high temperature dilatometry. Kinetics of b-SiC to a-SiC phase transformation during post-sintering heat treatment at temperatures 1900-1950 °C was studied, the degree of phase transformation being determined by quantitative x-ray analysis using internal standard technique. Evolution of microstructure resulting from beta-SiC to alpha-SiC transformation was followed up by scanning electron microscopy on polished and chemically etched samples. Transformation-controlled grain growth mechanism similar to the one observed for silicon nitride based ceramics was established. Possibility of in-situ platelet reinforced dense SiC-based ceramics fabrication with improved mechanical properties by means of sintering was shown.

  14. Advanced Environmental Barrier Coating Development for SiC-SiC Ceramic Matrix Composite Components

    Science.gov (United States)

    Zhu, Dongming; Harder, Bryan; Hurst, Janet B.; Halbig, Michael Charles; Puleo, Bernadette J.; Costa, Gustavo; Mccue, Terry R.

    2017-01-01

    This presentation reviews the NASA advanced environmental barrier coating (EBC) system development for SiC-SiC Ceramic Matrix Composite (CMC) combustors particularly under the NASA Environmentally Responsible Aviation, Fundamental Aeronautics and Transformative Aeronautics Concepts Programs. The emphases have been placed on the current design challenges of the 2700-3000F capable environmental barrier coatings for low NOX emission combustors for next generation turbine engines by using advanced plasma spray based processes, and the coating processing and integration with SiC-SiC CMCs and component systems. The developments also have included candidate coating composition system designs, degradation mechanisms, performance evaluation and down-selects; the processing optimizations using TriplexPro Air Plasma Spray Low Pressure Plasma Spray (LPPS), Plasma Spray Physical Vapor Deposition and demonstration of EBC-CMC systems. This presentation also highlights the EBC-CMC system temperature capability and durability improvements under the NASA development programs, as demonstrated in the simulated engine high heat flux, combustion environments, in conjunction with high heat flux, mechanical creep and fatigue loading testing conditions.

  15. Spectroscopic Studies of Semiconductor Materials for Aggressive-scaled Micro- and Opto-electronic Devices: nc-SiO2, GeO2; ng-Si, Ge and ng-Transition metal (TM) oxides

    Science.gov (United States)

    Cheng, Cheng

    transitions. Intra-d states are observed in all high-K dielectrics regardless of morphology, e.g. ng-TiO2, nc- Ti silicate , c-LaTiO3, nc-HfSiON334. This dissertation also discussed spectroscopic studies of: (i) nc-SiO 2, nc-GeO2 and (ii) nc-(SiO2)x(GeO2) 1-x pseudo-binary alloys. These studies, and the interpretation of these spectra and those in Chapter 3 in the This dissertation also discussed spectroscopic studies of: (i) nc-SiO2, nc-GeO2 and (ii) nc-(SiO 2)x(GeO2)1-x pseudo-binary alloys. These studies, and the interpretation of these spectra and those in Chapter 3 in the context of ab-initio theory provide a science base for the implementation of nc-oxides onto Germaniumsubstrates for aggressively scaled CMOS FETs, imaging devices as well as photovoltaics. X-Ray photoelectron spectroscopy(XPS) and Auger electron spectroscopy(AES) were used to determine SiO2 and GeO2 concentration in (SiO2)x(GeO2)1-x alloys. A linear trend in chemical shifts with compositions is observed and explained with charge-potential model, which incorporates the results of calculated partial charge from an empirical model for ionicity. The compositional linear relationships between binding energies nc-SiO 2, nc-GeO2, and (SiO2)x(GeO2)1-x alloy concentration agrees with the calculated results in charge potential model. SE and XAS spectral results show relatively strong O-vacancy in nc-GeO 2. O-vacancy defects in c-SiO2 are weaker. This is due to differences between Ge-O and Si-O bond (657.5kJ/mol and 799.6kJ/mol respectively). SE data shows a strong defect feature in GeO2, while SiO2 has no significant and distinct defect signature. Percolation theory describes the interconnection of bonds, e.g. Si-O and Ge-O in an otherwise nc-material, a (SiO2)x(GeO2)1-x pseudo-binary alloy. Changes in the band-gap energy of binary Si-Ge alloys occur at 0%Si (or 100% Ge), and the band gap energy increases from ˜ 0.6 eV to ˜0.87 eV as the Si concentration increases. A inflection point is at the percolation

  16. Synthesis and characterization of in situ carbon-coated Li2FeSiO4 cathode materials for lithium ion battery

    International Nuclear Information System (INIS)

    Yan Zipeng; Cai Shu; Miao Lijuan; Zhou Xing; Zhao Yongming

    2012-01-01

    Highlights: → Sucrose and L-ascorbic acid as carbon additives. → Li 2 FeSiO 4 /C were obtained under our carbon coating experimental conditions. → Graphite-rich carbon was formed uniformly when ascorbic acid was employed. → The composites employing L-ascorbic acid exhibited a large specific surface area. → Sample using L-ascorbic acid exhibited better rate performance and cycling stability. - Abstract: Li 2 FeSiO 4 /C composites with in situ carbon coating were synthesized via sol-gel method based on acid-catalyzed hydrolysis/condensation of tetraethoxysilane (TEOS) with sucrose and L-ascorbic acid as carbon additives, respectively. As-obtained Li 2 FeSiO 4 /C composites prepared with L-ascorbic acid as a carbon additive are composed of nanoparticulate Li 2 FeSiO 4 in an intimate contact with a continuous thin layer of residual carbon and exhibit large specific surface area up to 395.7 m 2 g -1 . The results indicate that structure of the residual carbon is graphene-rich with obviously lower disordered/graphene (D/G) ratio. These as-obtained Li 2 FeSiO 4 /C composites exhibit first discharge capacity of 135.3 mAh g -1 at C/16 and perform cycling stability, which are superior to those of Li 2 FeSiO 4 /C composites synthesized with sucrose as a carbon additive.

  17. Materiales vitrocerámicos del sistema MgO-Al2O3-SiO2 a partir de ceniza de cáscara de arroz

    Directory of Open Access Journals (Sweden)

    Romero, M.

    2011-08-01

    Full Text Available This wok shows the results of a valorisation study to use rice husk ash as raw material to develop glass-ceramic materials. An original glass has been formulated in the base system MgO-Al2O3-SiO2 with addition of B2O3 and Na2O to facilitate the melting and poring processes. Glass characterization was carried out by determining its chemical composition. Sintering behaviour has been examined by Hot Stage Microscopy (HSM. Thermal stability and crystallization mechanism have been studied by Differential Thermal Analysis (DTA. Mineralogy analyses of the glass-ceramic materials were carried out using X-ray Diffraction (XRD. Results show that it is possible to use ash rice husk to produce glass-ceramic materials by a sintercrystallization process, with nepheline (Na2O·Al2O3 · SiO2 as major crystalline phase in the temperature interval 700-950ºC and forsterite (2MgO·SiO2 at temperatures above 950ºC.En este trabajo se muestran los resultados de un estudio de valorización de la ceniza de cáscara de arroz como materia prima en la obtención de materiales vitrocerámicos. Se ha formulado un vidrio en el sistema base MgO-Al2O3-SiO2 incorporando B2O3 y Na2O para facilitar los procesos de fusión y colado del vidrio. El vidrio se ha caracterizado mediante la determinación de su composición química. Su comportamiento frente a la sinterización se ha llevado a cabo mediante Microscopía de Calefacción (MC. La estabilidad térmica de las muestras y el mecanismo de cristalización preferente se ha estudiado mediante Análisis Térmico Diferencial (ATD. La mineralogía de los materiales vitrocerámicos se ha llevado a cabo por Difracción de rayos-X (DRX. Los resultados obtenidos muestran que es posible utilizar ceniza de cáscara de arroz para producir materiales vitrocerámicos mediante un proceso de sinterización seguido de cristalización, con nefelina (Na2O·Al2O3·2SiO2 como fase cristalina mayoritaria en el intervalo de temperatura 700º-950ºC y

  18. Effect of TiO2 addition on reaction between SiC and Ni in SiC-Ni cermet spray coatings. Part 2. ; Development of SiC-based cermet spray coatings. SiC-Ni yosha himakuchu no SiC-Ni kaimen hanno ni oyobosu TiO2 tenka no koka. 2. ; SiC-ki sametto yosha himaku no kaihatsu

    Energy Technology Data Exchange (ETDEWEB)

    Nakamura, T [Kumano Technical College, Mie (Japan); Oki, S; Goda, S [Kinki Univ., Higashi-Osaka, Osaka (Japan). Faculty of Science and Technology

    1992-09-30

    The depression of the reaction between SiC and Ni, by adding TiO2 powder in spraying powder which has caused uniform dispersion in spray coating and reduction of TiO2 by the reaction during spraying, was studied. The mass ratio of the mixed components has been, SiC:Ni:TiO2=3:2:1. The spray coating was examined by electron prove microanalysis as well as X-ray diffractometry, centering mainly to the SiC-metal interface reaction. The formation of Ni-Si compounds have been depressed by the addition of TiO2 to spraying powder and by using plasma gas containing H2. Reason for this has been that the TiC formed in the SiC-Ni interface has depressed the reaction at the SiC-Ni interface. Further, TiO2 is reduced during spraying, and TiC is thought to be formed by the reaction between Ti and SiC or reaction between TiO2 and SiC. 8 refs., 6 figs., 1 tab.

  19. Sorption and physical properties of Mn O2-Si O2 composite

    International Nuclear Information System (INIS)

    Labayru M, R.; Correa N, M.; Andalaft J, E.

    1992-01-01

    These results show that the addition of silica improve the sorption and mechanical properties of Mn O 2 -Si O 2 composite. This ion-exchange material has an high Sr adsorption capacity still in the presence of Cs and Al, its capacity being higher than that of commercially available products. The particle size distribution of the ground solid is homogeneous ranging from 90 to 600 μm. The largest particle size fraction is directly proportional to the amount of silica. (author)

  20. Thermal characterization of tubular SiC/SiC composite structures for nuclear applications

    International Nuclear Information System (INIS)

    Duquesne, Loys

    2015-01-01

    Researches on the development on SiCf/SiC refractory composites for generation IV nuclear fuel cladding led the CEA to focus on the thermal behavior of these materials. In particular, knowledge of the thermal properties is essential for designing the components. Regarding the development of the 'sandwich' cladding concept, for which the complexity and the geometry differ from the conventionally used flat tubes, usual measurement methods are unsuitable. This study reports on the characterization and modeling of the thermal behavior of these structures. The first part deals with the identification of the global thermal parameters for the different layers of a 'sandwich' cladding. For this purpose, a flash method is used and an experimental device suitable for tubular geometries was developed. A new estimation method based on the combination of both collected signals in front and rear faces allows the identification of the thermal diffusivity of tubular composites using infrared thermography. The second part focuses on a virtual material approach, established to describe the thermal behavior of a 'sandwich' cladding, starting from the measured properties of the elementary components (fibers and matrix). They are then used as input data for the heat transfer modeling. Confrontations between experimental measurements and numerical results finally allow us to understand the importance of the various key parameters governing the heat transfer. (author) [fr

  1. Composited reduced graphene oxide into LiFePO4/Li2SiO3 and its electrochemical impedance spectroscopy properties

    Science.gov (United States)

    Arifin, M.; Rus, Y. B.; Aimon, A. H.; Iskandar, F.; Winata, T.; Abdullah, M.; Khairurrijal, K.

    2017-03-01

    LiFePO4 is commonly used as cathode material for Li-ion batteries due to its stable operational voltage and high specific capacity. However, it suffers from certain disadvantages such as low intrinsic electronic conductivity and low ionic diffusion. This study was conducted to analyse the effect of reduced graphene oxide (rGO) on the electrochemical properties of LiFePO4/Li2SiO3 composite. This composite was synthesized by a hydrothermal method. Fourier transform infrared spectroscopy measurement identified the O-P-O, Fe-O, P-O, and O-Si-O- bands in the LiFePO4/Li2SiO3 composite. X-ray diffraction measurement confirmed the formation of LiFePO4. Meanwhile, Raman spectroscopy confirmed the number of rGO layers. Further, scanning electron microscopy images showed that rGO was distributed around the LiFePO4/Li2SiO3 particles. Finally, the electrochemical impedance spectroscopy results showed that the addition of 1 wt% of rGO to the LiFePO4/Li2SiO3 composite reduced charge transfer resistance. It may be concluded that the addition of 1 wt% rGO to LiFePO4/Li2SiO3 composite can enhance its electrochemical performance as a cathode material.

  2. Flexural creep of coated SiC-fiber-reinforced glass-ceramic composites

    International Nuclear Information System (INIS)

    Sun, E.Y.

    1995-01-01

    This study reports the flexural creep behavior of a fiber-reinforced glass-ceramic and associated changes in microstructure. SiC fibers were coated with a dual layer of SiC/BN to provide a weak interface that was stable at high temperatures. Flexural creep, creep-rupture, and creep-strain recovery experiments were conducted on composite material and barium-magnesium aluminosilicate matrix from 1,000 to 1,200 C. Below 1,130 C, creep rates were extremely low (∼10 -9 s -1 ), preventing accurate measurement of the stress dependence. Above 1,130 C, creep rates were in the 10 -8 s -1 range. The creep-rupture strength of the composite at 1,100 C was about 75--80% of the fast fracture strength. Creep-strain recovery experiments showed recovery of up to 90% under prolonged unloading. Experimental creep results from the composite and the matrix were compared, and microstructural observations by TEM were employed to assess the effectiveness of the fiber coatings and to determine the mechanism(s) of creep deformation and damage

  3. Effect of re-melting on particle distribution and interface formation in SiC reinforced 2124Al matrix composite

    Energy Technology Data Exchange (ETDEWEB)

    Mandal, Durbadal, E-mail: durbadal73@yahoo.co.in [MEF Division, CSIR-National Metallurgical Laboratory, Jamshedpur 831007 (India); Viswanathan, Srinath [Dept of Metallurgical and Materials Engineering, University of Alabama, Tuscaloosa, AL (United States)

    2013-12-15

    The interface between metal matrix and ceramic reinforcement particles plays an important role in improving properties of the metal matrix composites. Hence, it is important to find out the interface structure of composite after re-melting. In the present investigation, the 2124Al matrix with 10 wt.% SiC particle reinforced composite was re-melted at 800 °C and 900 °C for 10 min followed by pouring into a permanent mould. The microstructures reveal that the SiC particles are distributed throughout the Al-matrix. The volume fraction of SiC particles varies from top to bottom of the composite plate and the difference increases with the decrease of re-melting temperature. The interfacial structure of re-melted 2124Al–10 wt.%SiC composite was investigated using scanning electron microscopy, an electron probe micro-analyzer, a scanning transmission electron detector fitted with scanning electron microscopy and an X-ray energy dispersive spectrometer. It is found that a thick layer of reaction product is formed at the interface of composite after re-melting. The experimental results show that the reaction products at the interface are associated with high concentration of Cu, Mg, Si and C. At re-melting temperature, liquid Al reacts with SiC to form Al{sub 4}C{sub 3} and Al–Si eutectic phase or elemental Si at the interface. High concentration of Si at the interface indicates that SiC is dissociated during re-melting. The X-ray energy dispersive spectrometer analyses confirm that Mg- and Cu-enrich phases are formed at the interface region. The Mg is segregated at the interface region and formed MgAl{sub 2}O{sub 4} in the presence of oxygen. The several elements identified at the interface region indicate that different types of interfaces are formed in between Al matrix and SiC particles. The Al–Si eutectic phase is formed around SiC particles during re-melting which restricts the SiC dissolution. - Highlights: • Re-melted composite shows homogeneous particle

  4. MAX Phase Modified SiC Composites for Ceramic-Metal Hybrid Cladding Tubes

    International Nuclear Information System (INIS)

    Jung, Yang-Il; Kim, Sun-Han; Park, Dong-Jun; Park, Jeong-Hwan; Park, Jeong-Yong; Kim, Hyun-Gil; Koo, Yang-Hyun

    2015-01-01

    A metal-ceramic hybrid cladding consists of an inner zirconium tube, and an outer SiC fiber-matrix SiC ceramic composite with surface coating as shown in Fig. 1 (left-hand side). The inner zirconium allows the matrix to remain fully sealed even if the ceramic matrix cracks through. The outer SiC composite can increase the safety margin by taking the merits of the SiC itself. In addition, the outermost layer prevents the dissolution of SiC during normal operation. On the other hand, a ceramic-metal hybrid cladding consists of an outer zirconium tube, and an inner SiC ceramic composite as shown in Fig. 1 (right-hand side). The outer zirconium protects the fuel rod from a corrosion during reactor operation, as in the present fuel claddings. The inner SiC composite, additionally, is designed to resist the severe oxidation under a postulated accident condition of a high-temperature steam environment. Reaction-bonded SiC was fabricated by modifying the matrix as the MAX phase. The formation of Ti 3 SiC 2 was investigated depending on the compositions of the preform and melt. In most cases, TiSi 2 was the preferential phase because of its lowest melting point in the Ti-Si-C system. The evidence of Ti 3 SiC 2 was the connection with the pressurizing

  5. Solution based synthesis of mixed-phase materials in the Li{sub 2}TiO{sub 3}–Li{sub 4}SiO{sub 4} system

    Energy Technology Data Exchange (ETDEWEB)

    Hanaor, Dorian A.H., E-mail: dorian.hanaor@sydney.edu.au [School of Civil Engineering, University of Sydney, NSW 2006 (Australia); Kolb, Matthias H.H. [Institute for Applied Materials, Karlsruhe Institute of Technology, 76021 (Germany); Gan, Yixiang [School of Civil Engineering, University of Sydney, NSW 2006 (Australia); Kamlah, Marc; Knitter, Regina [Institute for Applied Materials, Karlsruhe Institute of Technology, 76021 (Germany)

    2015-01-15

    Highlights: • Investigation of phase stability in the quasi-binary Li{sub 2}TiO{sub 3}–Li{sub 4}SiO{sub 4} system. • Sol-based syntheses of mixed phase materials from organometallic precursors. • LiCl based synthesis results in greater lithium deficiency than LiOH synthesis. • The Li{sub 2}TiO{sub 3}–Li{sub 4}SiO{sub 4} quasi binary system appears to exhibit monotectic behaviour. • Mixed phase materials show liquid formation from melting of silicate material at 1100 °C. - Abstract: As candidate tritium breeder materials for use in the ITER helium cooled pebble bed, ceramic multiphasic compounds lying in the region of the quasi-binary lithium metatitanate–lithium orthosilicate system may exhibit mechanical and physical advantages relative to single phase materials. Here we present an organometallic solution-based synthesis procedure for the low-temperature fabrication of compounds in the Li{sub 2}TiO{sub 3}–Li{sub 4}SiO{sub 4} region and investigate phase stability and transformations through temperature varied X-ray diffraction and scanning calorimetry. Results demonstrate that the metatitanate and metasilicate phases Li{sub 2}TiO{sub 3} and Li{sub 2}SiO{sub 3} readily crystallise in nanocrystalline form at temperatures below 180 °C. Lithium deficiency in the region of 5% results from Li sublimation from Li{sub 4}SiO{sub 4} and/or from excess Li incorporation in the metatitanate phase and brings about a stoichiometry shift, with product compounds exhibiting mixed lithium orthosilicate/metasilicate content towards the Si rich region and predominantly Li{sub 2}TiO{sub 3} content towards the Ti rich region. Above 1150 °C the transformation of monoclinic to cubic γ-Li{sub 2}TiO{sub 3} disordered solid-solution occurs while the melting of silicate phases indicates a likely monotectic type system with a solidus line in the region 1050–1100 °C. Synthesis procedures involving a lithium chloride precursor are not likely to be a viable option for

  6. Core–shell structured FeSiAl/SiO{sub 2} particles and Fe{sub 3}Si/Al{sub 2}O{sub 3} soft magnetic composite cores with tunable insulating layer thicknesses

    Energy Technology Data Exchange (ETDEWEB)

    Fan, Xi’an, E-mail: groupfxa@163.com [The State Key Laboratory of Refractories and Metallurgy, Wuhan University of Science and Technology, Wuhan, Hubei 430081 (China); Key Laboratory for Ferrous Metallurgy and Resources Utilization of Ministry of Education, Wuhan University of Science and Technology, Wuhan, Hubei 430081 (China); Wang, Jian, E-mail: snove418562@163.com [The State Key Laboratory of Refractories and Metallurgy, Wuhan University of Science and Technology, Wuhan, Hubei 430081 (China); Key Laboratory for Ferrous Metallurgy and Resources Utilization of Ministry of Education, Wuhan University of Science and Technology, Wuhan, Hubei 430081 (China); Wu, Zhaoyang, E-mail: wustwuzhaoyang@163.com [The State Key Laboratory of Refractories and Metallurgy, Wuhan University of Science and Technology, Wuhan, Hubei 430081 (China); Key Laboratory for Ferrous Metallurgy and Resources Utilization of Ministry of Education, Wuhan University of Science and Technology, Wuhan, Hubei 430081 (China); Li, Guangqiang, E-mail: ligq-wust@mail.wust.edu.cn [The State Key Laboratory of Refractories and Metallurgy, Wuhan University of Science and Technology, Wuhan, Hubei 430081 (China); Key Laboratory for Ferrous Metallurgy and Resources Utilization of Ministry of Education, Wuhan University of Science and Technology, Wuhan, Hubei 430081 (China)

    2015-11-15

    Graphical abstract: - Highlights: • FeSiAl/SiO{sub 2} core–shell particles and Fe{sub 3}Si/Al{sub 2}O{sub 3} composite cores were prepared. • SiO{sub 2} surrounding FeSiAl were replaced by Al{sub 2}O{sub 3} during sintering process. • Fe{sub 3}Si particles were separated by Al{sub 2}O{sub 3} with tunable thickness in composite cores. • Fe{sub 3}Si/Al{sub 2}O{sub 3} had lower core loss and better frequency stability than FeSiAl core. • The insulating layer between ferromagnetic particles can reduce core loss. - Abstract: FeSiAl/SiO{sub 2} core–shell particles and Fe{sub 3}Si/Al{sub 2}O{sub 3} composite cores with tunable insulating layer thicknesses have been synthesized via a modified Stöber method combined with following high temperature sintering process. Most of the conductive FeSiAl particles could be coated by insulating SiO{sub 2} using the modified Stöber method. During the sintering process, the reaction 4Al + 3SiO{sub 2} ≣ 2α-Al{sub 2}O{sub 3} + 3Si took place and the new Fe{sub 3}Si/Al{sub 2}O{sub 3} composite was formed. The Fe{sub 3}Si/Al{sub 2}O{sub 3} composite cores displayed more excellent soft magnetic properties, better frequency stability at high frequencies, much higher resistivity and lower core loss than the raw FeSiAl core. Based on this, several types of FeSiAl/SiO{sub 2} particles and Fe{sub 3}Si/Al{sub 2}O{sub 3} composite cores with tunable insulating layer thicknesses were selectively prepared by simply varying TEOS contents. The thickness of Al{sub 2}O{sub 3} insulating layer and resistivity of Fe{sub 3}Si/Al{sub 2}O{sub 3} composite cores increased with increasing the TEOS contents, while the permeability and core loss changed in the opposite direction.

  7. 3D cellular automata finite element (CAFE) modelling and experimental observation of damage in quasi-brittle nuclear materials: Indentation of a SiC-SiC-fibre ceramic matrix composite

    International Nuclear Information System (INIS)

    Saucedo Mora, Luis; Mostafavi, Mahmoud; Marrow, T. James; Khoshkhou, Danial; Connolly, Brian; Reinhard, Christina; Atwood, Robert; Zhao, Shuang

    2015-01-01

    Cellular automata integrated with finite elements (CAFE) have been used to develop a method to account for the effect of microstructure on quasi-brittle damage development. The microstructure is simulated explicitly by subdividing a finite element into smaller cells. A heterogeneous structure is created from key cells (seeds) using defined characteristics; the influence of the initial finite element mesh is effectively removed during the development of the microstructure. Graded microstructures, textures, particle anisotropy and multiple phases can be readily simulated, such as those in composites and porous materials. A mesh-free framework has been developed to compute the damage development through the microstructure, using cellular automata. With this method, we can study the development of discontinuous cracking and damage coalescence, and its sensitivity to microstructure. Experiments have been carried out to observe the three-dimensional development of damage, using high-resolution synchrotron X-ray computed tomography and digital volume correlation to observe Hertzian indentation of a SiC-SiC fibre composite, quantifying damage by measurement of the displacement fields within the material. The results demonstrate the applicability of the modelling strategy to damage development, and show how model input data may be obtained from small specimen tests, which could be performed at elevated temperatures with irradiated materials. (authors)

  8. Influence of SiO2 coating on dielectric property of TiC reinforced PVDF composite%SiO2涂层对TiC/PVDF复合材料介电性能的影响研究

    Institute of Scientific and Technical Information of China (English)

    贺新福; 吴红菊; 刘天涯; 冉安; 周文英

    2017-01-01

    为降低碳化钛(TiC)/聚偏氟乙烯(PVDF)体系的介电损耗,通过溶胶-凝胶法在TiC粒子表面包覆SiO2绝缘层,形成SiO2@TiC核壳结构粒子,再与PVDF复合,制备出SiO2@TiC/PVDF复合材料.研究结果表明,TiC表面成功包覆上SiO2涂层;在质量分数为9%的TiC或SiO2@TiC总用量时,SiO2@TiC/PVDF的损耗因子相比TiC/PVDF明显降低,随SiO2包覆量的增加,SiO2@TiC/PVDF的介电常数、损耗因子和电导率均下降;包覆量相同时,随SiO2@TiC粒子含量增加,SiO2@TiC/PVDF的介电常数、电导率、损耗因子均逐步增大.

  9. Deformation and recrystallization of Nb-10Si in-situ composite

    International Nuclear Information System (INIS)

    Saqib, M.; Thirukkonda, M.; Cockeram, B.; Srinivasan, R.; Weiss, I.

    1993-01-01

    Materials for elevated temperature applications require a balance of strength, fracture toughness, mechanical and microstructural stability over the temperature range between room temperature and service temperatures which are expected to exceed 1,200 C, as well as oxidation and creep resistance. Recent trends indicate that Carbon/Carbon and Ceramic/Ceramic Composites do not meet all of these requirements. For example, carbon/carbon composites have good strength to density ratio, but inherently possess poor oxidation resistance, and SiC/SiC composites ha e excellent oxidation resistance, but are brittle over the entire temperature range of their stability. Ductile phase toughened composites with refractory intermetallic matrices are attractive alternatives. At service temperatures of about 1,200 C, most of the applied load will be carried by the intermetallic matrix phase, while the ductile (metallic) phase increases toughness by impeding crack propagation. As compared to other materials with potential for elevated temperature applications, mentioned above, these materials provide a better combination of elevated temperature strength and room temperature fracture toughness. Nb 10 a/o Si is a model material for ductile phase toughened in situ composites. In the as-cast condition the microstructure contains both the ductile metallic niobium phase and the continuous inter-metallic Nb 3 Si phase. The microstructure of this in situ composite can be tailored by thermomechanical processing (TMP). The changes in the morphology and spacing of the phases, and microstructural refinement following TMP, have been shown to improve the fracture toughness of the alloy. as compared to the as-cast material. Therefore, understanding of the deformation behavior and the mechanisms of recovery and recrystallization are of great importance in tailoring the microstructure of in situ composites by TMP

  10. Comparing the effect of processing temperature on microstructure and mechanical behavior of (ZrSiO4 or TiB2)/aluminum composites

    International Nuclear Information System (INIS)

    Abdizadeh, H.; Baharvandi, H.R.; Moghaddam, K. Shirvani

    2008-01-01

    Recently, a large number of metal matrix composites have been developed for high-performance applications. The first requirement for superior performance of a composite material is the homogeneous distribution of the reinforcing phase. In particulate-reinforced composites, any agglomeration of reinforcement particles deteriorates the mechanical properties of composite. Stir casting route has been used to achieve homogeneity of particle distribution throughout the matrix. In present study, ZrSiO 4 and TiB 2 particles were incorporated in A356.1 alloy. The size of ZrSiO 4 and TiB 2 particles was 1 μm. Reinforcement particles were added to melted aluminum at different temperatures above pure aluminum melting point (750, 850, 950 deg. C). The volume fraction of reinforcement particles was 5%. After addition of reinforcement, stirring was continued for 12 min for better distribution and better solidification conditions. The microstructure and mechanical behavior of prepared composites were studied. Scanning electron microscopy and X-ray diffraction were used to investigate dispersion of reinforcement particles in aluminum matrix and chemical composition of composites. Hardness and tensile tests were carried out to test mechanical properties. The results of these experiments show that the mechanical properties and microstructure of composites were changed by increasing temperature; also the best condition of ZrSiO 4 case was 750 deg. C but 850 deg. C for TiB 2

  11. Characterization of C/SiC Ceramic Matrix Composites (CMCs) with Novel Interface Fiber Coatings

    Science.gov (United States)

    Petko, Jeanne F.; Kiser, J. Douglas; Gray, Hugh R. (Technical Monitor)

    2002-01-01

    Ceramic Matrix Composites (CMCs) are attractive candidate aerospace materials due to their high specific strength, low density and high temperature capabilities. The National Aeronautics and Space Administration (NASA) is pursuing the use of CMC components in advanced Reusable Launch Vehicle (RLV) propulsion applications. Carbon fiber-reinforced silicon carbide (C/SiC) is the primary material of interest for a variety of RLV propulsion applications. These composites consist of high-strength carbon fibers and a high modulus, oxidation resistant matrix. For RLV propulsion applications, environmental durability will be critical. Two types of carbon fibers were processed with both standard (pyrolytic carbon) and novel (multilayer and pseudoporous) types of interface coatings as part of a study investigating various combinations of constituents. The benefit of protecting the composites with a surface sealant was also investigated. The strengths, durability in oxidizing environments, and microstructures of these developmental composite materials are presented. The novel interface coatings and the surface sealant show promise for protecting the carbon fibers from the oxidizing environment.

  12. Hierarchical NiO-SiO2 composite hollow microspheres with enhanced adsorption affinity towards Congo red in water.

    Science.gov (United States)

    Lei, Chunsheng; Zhu, Xiaofeng; Zhu, Bicheng; Yu, Jiaguo; Ho, Wingkei

    2016-03-15

    Hollow microspheres and hierarchical porous nanostructured materials with desired morphologies have gained remarkable attention for their potential applications in environmental technology. In this study, NiO-SiO2 hollow microspheres were prepared by co-precipitation with SiO2 and nickel salt as precursors, followed by dipping in alkaline solution and calcination. The samples were characterized by X-ray diffraction, field-emission scanning electron microscopy, transmission electron microscopy, Fourier transform infrared spectroscopy, nitrogen adsorption, and X-ray photoelectron spectroscopy. The synthesized hollow spheres were composed of a SiO2 shell and hierarchical porous NiO nanosheets on the surface. Adsorption experiments suggested that NiO-SiO2 composite particles were powerful adsorbents for removal of Congo red from water, with a maximum adsorption capacity of 204.1 mg/g. The high specific surface areas, hollow structures, and hierarchical porous surfaces of the hollow composite particles are suitable for various applications, including adsorption of pollutants, chemical separation, and water purification. Copyright © 2015 Elsevier Inc. All rights reserved.

  13. Synthesis and characterisation of composite based biohydroxyapatite bovine bone mandible waste (BHAp) doped with 10 wt % amorphous SiO{sub 2} from rice husk by solid state reaction

    Energy Technology Data Exchange (ETDEWEB)

    Asmi, Dwi, E-mail: dwiasmi82@yahoo.com, E-mail: dwi.asmi@fmipa.unila.ac.id; Sulaiman, Ahmad, E-mail: ahmadsulaiman@yahoo.co.id; Oktavia, Irene Lucky, E-mail: ireneluckyo@gmail.com [Department of Physics, Faculty of Mathematics and Natural Sciences, University of Lampung Jl. Sumantri Brojonegoro No.1 Gedung Meneng Bandar Lampung 35145 (Indonesia); Badaruddin, Muhammad, E-mail: mbruddin@eng.unila.ac.id [Department of Mechanical Engineering, Faculty of Engineering, University of Lampung Jl. Sumantri Brojonegoro No.1 Gedung Meneng Bandar Lampung 35145 (Indonesia); Zulfia, Anne, E-mail: anne@metal.ui.ac.id [Department of Metallurgy and Materials Engineering, Faculty of Engineering, University of Indonesia, Kampus Baru-UI, Depok 16424 (Indonesia)

    2016-04-19

    Effect of 10 wt% amorphous SiO{sub 2} from rice husk addition on the microstructures of biohydroxyapatite (BHAp) obtained from bovine bone was synthesized by solid state reaction. In this study, biohydroxyapatite powder was obtained from bovine bone mandible waste heat treated at 800 °C for 5 h and amorphous SiO{sub 2} powder was extracted from citric acid leaching of rice husk followed by combustion at 700°C for 5 h. The composite powder then mixed and sintered at 1200 °C for 3 h. X-ray diffraction (XRD), Fourier transformed infrared (FTIR) spectroscopy and Scanning electron microscopy (SEM) techniques are utilized to characterize the phase relations, functional group present and morphology of the sample. The study has revealed that the processing procedures played an important role in microstructural development of BHAp-10 wt% SiO{sub 2} composite. The XRD study of the raw material revealed that the primary phase material in the heat treated of bovine bone mandible waste is hydroxyapatite and in the combustion of rice husk is amorphous SiO{sub 2}. However, in the composite the hydroxyapatite, β-tricalcium phosphate, and calcium phosphate silicate were observed. The FTIR result show that the hydroxyl stretching band in the composite decrease compared with those of hydroxyapatite spectra and the evolution of morphology was occurred in the composite.

  14. Glass-ceramic materials of system MgO-Al2O3-SiO2 from rice husk ash

    OpenAIRE

    Martín Hernández, María Isabel; Rincón López, Jesús María; Andreola, F.; Barbieri, L.; Bondioli, F.; Lancellotti, I.; Romero, Maximina

    2011-01-01

    This wok shows the results of a valorisation study to use rice husk ash as raw material to develop glass-ceramic materials. An original glass has been formulated in the base system MgO-Al2O3-SiO2 with addition of B2O3 and Na2O to facilitate the melting and poring processes. Glass characterization was carried out by determining its chemical composition. Sintering behaviour has been examined by Hot Stage Microscopy (HSM). Thermal stability and crystallization mechanism have been studied by Diff...

  15. Ablation behavior of rare earth La-modified ZrC coating for SiC-coated carbon/carbon composites under an oxyacetylene torch

    International Nuclear Information System (INIS)

    Jia, Yujun; Li, Hejun; Feng, Lei; Sun, Jiajia; Li, Kezhi; Fu, Qiangang

    2016-01-01

    Highlights: • La-modified ZrC coating was prepared by supersonic atmosphere plasma spraying. • The oxyacetylene ablation behavior of La-modified ZrC/SiC coating was evaluated. • The coating shows a good ablation resistance under heat flux of 2.4 MW/m"2. • La promotes the liquid phase sintering of ZrO_2 and the formation of a compact scale. • The protection of the scale results in retaining elemental C in its inner layer. - Abstract: To improve the ablation resistance of carbon/carbon (C/C) composites at ultra-high temperature, La-modified ZrC coating was prepared on SiC-coated C/C composites by supersonic atmosphere plasma spraying. The coating shows a significant improvement on the ablation resistance compared with ZrC coating and could protect C/C composites for more than 120 s under heat flux of 2.4 MW/m"2. La acted as a role in promoting the liquid phase sintering of ZrO_2 and forming a compact scale with high thermal stability, improving the ablation resistance of C/C composites.

  16. Wear behaviour of plasma-sprayed AlSi/B4C composite coatings

    International Nuclear Information System (INIS)

    Sarikaya, Ozkan; Anik, Selahaddin; Celik, Erdal; Okumus, S. Cem; Aslanlar, Salim

    2007-01-01

    This paper describes the wear behaviour of AlSi/B 4 C composite coatings with 0-25 wt% B 4 C particles for diesel engine motors. These coatings were successfully fabricated on AlSi substrates using an atmospheric plasma spray technique. The produced samples were characterized by means of an optical microscope, scanning electron microscope and microhardness tester. The obtained results pointed out that an increase of B 4 C particles in AlSi coatings was caused on the rising of the microhardness values and the decrease of the thermal expansion coefficient of the coatings. The friction and wear experiments were performed under dry conditions using a ball-on-dics configuration against WC/Co counter material for different loads. It was concluded that wear resistance of the coatings produced using B 4 C powders is greatly improved compared with the substrate material. The highest wear resistance of the coatings were also determined in the 20% B 4 C coating

  17. The effect of the gate electrode on the C-V- characteristics of the structure M-TmF3-SiO2-Si

    International Nuclear Information System (INIS)

    Basily, R.R.

    1979-09-01

    The C-V characteristics of the structure M-TmF 3 -SiO 2 -Si, thermally treated at a temperature of 300 0 C for 15 minutes, were investigated. At higher temperatures to about 150 0 C, the hysteresis of the C-V characteristics is completely absent, whereas at room temperature hysteresis depends on the applied voltage and on the material of the gate electrode. The dependence of the flat band voltage shift on the applied voltage, the thickness of SiO 2 layer and the material of the gate electrode were measured. (author)

  18. Rapid removal of uranium from aqueous solutions using magnetic Fe3O4@SiO2 composite particles.

    Science.gov (United States)

    Fan, Fang-Li; Qin, Zhi; Bai, Jing; Rong, Wei-Dong; Fan, Fu-You; Tian, Wei; Wu, Xiao-Lei; Wang, Yang; Zhao, Liang

    2012-04-01

    Rapid removal of U(VI) from aqueous solutions was investigated using magnetic Fe(3)O(4)@SiO(2) composite particles as the novel adsorbent. Batch experiments were conducted to study the effects of initial pH, amount of adsorbent, shaking time and initial U(VI) concentrations on uranium sorption efficiency as well as the desorbing of U(VI). The sorption of uranium on Fe(3)O(4)@SiO(2) composite particles was pH-dependent, and the optimal pH was 6.0. In kinetics studies, the sorption equilibrium can be reached within 180 min, and the experimental data were well fitted by the pseudo-second-order model, and the equilibrium sorption capacities calculated by the model were almost the same as those determined by experiments. The Langmuir sorption isotherm model correlates well with the uranium sorption equilibrium data for the concentration range of 20-200 mg/L. The maximum uranium sorption capacity onto magnetic Fe(3)O(4)@SiO(2) composite particles was estimated to be about 52 mg/g at 25 °C. The highest values of uranium desorption (98%) was achieved using 0.01 M HCl as the desorbing agent. Fe(3)O(4)@SiO(2) composite particles showed a good selectivity for uranium from aqueous solution with other interfering cation ions. Present study suggested that magnetic Fe(3)O(4)@SiO(2) composite particles can be used as a potential adsorbent for sorption uranium and also provided a simple, fast separation method for removal of heavy metal ion from aqueous solution. Copyright © 2011 Elsevier Ltd. All rights reserved.

  19. Enhanced the hydrophobic surface and the photo-activity of TiO2-SiO2 composites

    Science.gov (United States)

    Wahyuni, S.; Prasetya, A. T.

    2017-02-01

    The aim of this research is to develop nanomaterials for coating applications. This research studied the effect of various TiO2-SiO2 composites in acrylic paint to enhance the hydrophobic properties of the substrate. Titanium dioxide containing silica in the range 20-35 mol% has been synthesized using sol-gel route. The XRD’s spectra show that increasing SiO2 content in the composite, decreasing its crystalline properties but increasing the surface area. TiO2-SiO2 composite was dispersed in acrylic paint in 2% composition by weight. The largest contact angle was 70, which produced by the substrate coated with TS-35-modified acrylic paint. This study also investigated the enhanced photo-activity of TiO2-SiO2 modified with poly-aniline. The XRD spectra show that the treatment does not change the crystal structure of TiO2. The photo-activity of the composite was evaluated by degradation of Rhodamine-B with visible light. The best performance of the degradation process was handled by the composite treated with 0.1mL anilines per gram of TiO2-SiO2 composite (TSP-A). On the other side, the contact angle 70 has not shown an excellent hydrophobic activity. However, the AFM spectra showed that nanoroughness has started to form on the surface of acrylic paint modified with TiO2-SiO2 than acrylic alone.

  20. Dual-Layer Oxidation-Protective Plasma-Sprayed SiC-ZrB2/Al2O3-Carbon Nanotube Coating on Graphite

    Science.gov (United States)

    Ariharan, S.; Sengupta, Pradyut; Nisar, Ambreen; Agnihotri, Ankur; Balaji, N.; Aruna, S. T.; Balani, Kantesh

    2017-02-01

    Graphite is used in high-temperature gas-cooled reactors because of its outstanding irradiation performance and corrosion resistance. To restrict its high-temperature (>873 K) oxidation, atmospheric-plasma-sprayed SiC-ZrB2-Al2O3-carbon nanotube (CNT) dual-layer coating was deposited on graphite substrate in this work. The effect of each layer was isolated by processing each component of the coating via spark plasma sintering followed by isothermal kinetic studies. Based on isothermal analysis and the presence of high residual thermal stress in the oxide scale, degradation appeared to be more severe in composites reinforced with CNTs. To avoid the complexity of analysis of composites, the high-temperature activation energy for oxidation was calculated for the single-phase materials only, yielding values of 11.8, 20.5, 43.5, and 4.5 kJ/mol for graphite, SiC, ZrB2, and CNT, respectively, with increased thermal stability for ZrB2 and SiC. These results were then used to evaluate the oxidation rate for the composites analytically. This study has broad implications for wider use of dual-layer (SiC-ZrB2/Al2O3) coatings for protecting graphite crucibles even at temperatures above 1073 K.

  1. Deposition temperature dependence of material and Si surface passivation properties of O3-based atomic layer deposited Al2O3-based films and stacks

    International Nuclear Information System (INIS)

    Bordihn, Stefan; Mertens, Verena; Müller, Jörg W.; Kessels, W. M. M.

    2014-01-01

    The material composition and the Si surface passivation of aluminum oxide (Al 2 O 3 ) films prepared by atomic layer deposition using Al(CH 3 ) 3 and O 3 as precursors were investigated for deposition temperatures (T Dep ) between 200 °C and 500 °C. The growth per cycle decreased with increasing deposition temperature due to a lower Al deposition rate. In contrast the material composition was hardly affected except for the hydrogen concentration, which decreased from [H] = 3 at. % at 200 °C to [H]  2 O 3 /SiN x stacks complemented the work and revealed similar levels of surface passivation as single-layer Al 2 O 3 films, both for the chemical and field-effect passivation. The fixed charge density in the Al 2 O 3 /SiN x stacks, reflecting the field-effect passivation, was reduced by one order of magnitude from 3·10 12  cm −2 to 3·10 11  cm −2 when T Dep was increased from 300 °C to 500 °C. The level of the chemical passivation changed as well, but the total level of the surface passivation was hardly affected by the value of T Dep . When firing films prepared at of low T Dep , blistering of the films occurred and this strongly reduced the surface passivation. These results presented in this work demonstrate that a high level of surface passivation can be achieved for Al 2 O 3 -based films and stacks over a wide range of conditions when the combination of deposition temperature and annealing or firing temperature is carefully chosen

  2. Interlaminar shear strength of SiC matrix composites reinforced by continuous fibers at 900 °C in air

    International Nuclear Information System (INIS)

    Zhang, Chengyu; Gou, Jianjie; Qiao, Shengru; Wang, Xuanwei; Zhang, Jun

    2014-01-01

    Highlights: • The application of SiC fiber could improve ILSS of the SiC matrix composites. • The orientation of the warp fibers plays a critical role in determining ILSS of 2.5D-C/SiC. • The failure mechanisms of 2D composites involve matrix cracking, and interfacial debonding. - Abstract: To reveal the shear properties of SiC matrix composites, interlaminar shear strength (ILSS) of three kinds of silicon carbide matrix composites was investigated by compression of the double notched shear specimen (DNS) at 900 °C in air. The investigated composites included a woven plain carbon fiber reinforced silicon carbide composite (2D-C/SiC), a two-and-a-half-dimensional carbon fiber-reinforced silicon carbide composite (2.5D-C/SiC) and a woven plain silicon carbon fiber reinforced silicon carbide composite (2D-SiC/SiC). A scanning electron microscope was employed to observe the microstructure and fracture morphologies. It can be found that the fiber type and reinforcement architecture have significant impacts on the ILSS of the SiC matrix composites. Great anisotropy of ILSS can be found for 2.5D-C/SiC because of the different fracture resistance of the warp fibers. Larger ILSS can be obtained when the specimens was loaded along the weft direction. In addition, the SiC fibers could enhance the ILSS, compared with carbon fibers. The improvement is attributed to the higher oxidation resistance of SiC fibers and the similar thermal expansion coefficients between the matrix and the fibers

  3. Oxide Structure Dependence of SiO2/SiOx/3C-SiC/n-Type Si Nonvolatile Resistive Memory on Memory Operation Characteristics

    Science.gov (United States)

    Yamaguchi, Yuichiro; Shouji, Masatsugu; Suda, Yoshiyuki

    2012-11-01

    We have investigated the dependence of the oxide layer structure of our previously proposed metal/SiO2/SiOx/3C-SiC/n-Si/metal metal-insulator-semiconductor (MIS) resistive memory device on the memory operation characteristics. The current-voltage (I-V) measurement and X-ray photoemission spectroscopy results suggest that SiOx defect states mainly caused by the oxidation of 3C-SiC at temperatures below 1000 °C are related to the hysteresis memory behavior in the I-V curve. By restricting the SiOx interface region, the number of switching cycles and the on/off current ratio are more enhanced. Compared with a memory device formed by one-step or two-step oxidation of 3C-SiC, a memory device formed by one-step oxidation of Si/3C-SiC exhibits a more restrictive SiOx interface with a more definitive SiO2 layer and higher memory performances for both the endurance switching cycle and on/off current ratio.

  4. Interfacial chemistry and energy band alignment of TiAlO on 4H-SiC determined by X-ray photoelectron spectroscopy

    International Nuclear Information System (INIS)

    Wang, Qian; Cheng, Xinhong; Zheng, Li; Ye, Peiyi; Li, Menglu; Shen, Lingyan; Li, Jingjie; Zhang, Dongliang; Gu, Ziyue; Yu, Yuehui

    2017-01-01

    Highlights: • Composite TiAlO rather than TiO_2-Al_2O_3 laminations is deposited on 4H-SiC by PEALD. • An interfacial layer composed of Ti, Si, O and C forms between TiAlO and 4H-SiC. • TiAlO offers competitive barrier heights (>1 eV) for both electrons and holes. - Abstract: Intermixing of TiO_2 with Al_2O_3 to form TiAlO films on 4H-SiC is expected to simultaneously boost the dielectric constant and achieve sufficient conduction/valence band offsets (CBO/VBO) between dielectrics and 4H-SiC. In this work, a composite TiAlO film rather than TiO_2-Al_2O_3 laminations is deposited on 4H-SiC by plasma enhanced atomic layer deposition (PEALD). X-ray photoelectron spectroscopy (XPS) is performed to systematically analyze the interfacial chemistry and energy band alignment between TiAlO and 4H-SiC. An interfacial layer composed of Ti, Si, O and C forms between TiAlO and 4H-SiC during PEALD process. The VBO and CBO between TiAlO and 4H-SiC are determined to be 1.45 eV and 1.10 eV, respectively, which offer competitive barrier heights (>1 eV) for both electrons and holes and make it suitable for the fabrication of 4H-SiC metal-oxide-semiconductor field effect transistors (MOSFETs).

  5. Interfacial chemistry and energy band alignment of TiAlO on 4H-SiC determined by X-ray photoelectron spectroscopy

    Energy Technology Data Exchange (ETDEWEB)

    Wang, Qian [State Key Laboratory of Functional Materials for Informatics, Shanghai Institute of Micro-System & Information Technology, Chinese Academy of Sciences, Changning Road 865, Shanghai 200050 (China); University of Chinese Academy of Sciences, Beijing 100049 (China); Cheng, Xinhong, E-mail: xh_cheng@mail.sim.ac.cn [State Key Laboratory of Functional Materials for Informatics, Shanghai Institute of Micro-System & Information Technology, Chinese Academy of Sciences, Changning Road 865, Shanghai 200050 (China); Zheng, Li, E-mail: zhengli@mail.sim.ac.cn [State Key Laboratory of Functional Materials for Informatics, Shanghai Institute of Micro-System & Information Technology, Chinese Academy of Sciences, Changning Road 865, Shanghai 200050 (China); University of Chinese Academy of Sciences, Beijing 100049 (China); Ye, Peiyi; Li, Menglu [Department of Materials Science and Engineering, University of California, Los Angeles, CA, 90095 (United States); Shen, Lingyan; Li, Jingjie; Zhang, Dongliang; Gu, Ziyue [State Key Laboratory of Functional Materials for Informatics, Shanghai Institute of Micro-System & Information Technology, Chinese Academy of Sciences, Changning Road 865, Shanghai 200050 (China); University of Chinese Academy of Sciences, Beijing 100049 (China); Yu, Yuehui [State Key Laboratory of Functional Materials for Informatics, Shanghai Institute of Micro-System & Information Technology, Chinese Academy of Sciences, Changning Road 865, Shanghai 200050 (China)

    2017-07-01

    Highlights: • Composite TiAlO rather than TiO{sub 2}-Al{sub 2}O{sub 3} laminations is deposited on 4H-SiC by PEALD. • An interfacial layer composed of Ti, Si, O and C forms between TiAlO and 4H-SiC. • TiAlO offers competitive barrier heights (>1 eV) for both electrons and holes. - Abstract: Intermixing of TiO{sub 2} with Al{sub 2}O{sub 3} to form TiAlO films on 4H-SiC is expected to simultaneously boost the dielectric constant and achieve sufficient conduction/valence band offsets (CBO/VBO) between dielectrics and 4H-SiC. In this work, a composite TiAlO film rather than TiO{sub 2}-Al{sub 2}O{sub 3} laminations is deposited on 4H-SiC by plasma enhanced atomic layer deposition (PEALD). X-ray photoelectron spectroscopy (XPS) is performed to systematically analyze the interfacial chemistry and energy band alignment between TiAlO and 4H-SiC. An interfacial layer composed of Ti, Si, O and C forms between TiAlO and 4H-SiC during PEALD process. The VBO and CBO between TiAlO and 4H-SiC are determined to be 1.45 eV and 1.10 eV, respectively, which offer competitive barrier heights (>1 eV) for both electrons and holes and make it suitable for the fabrication of 4H-SiC metal-oxide-semiconductor field effect transistors (MOSFETs).

  6. Effect of Steam Activation on Development of Light Weight Biomorphic Porous SiC from Pine Wood Precursor

    Science.gov (United States)

    Manocha, Satish M.; Patel, Hemang; Manocha, L. M.

    2013-02-01

    Biomorphic SiC materials with tailor-made microstructure and properties similar to ceramic materials manufactured by conventional method are a new class of materials derived from natural biopolymeric cellulose templates (wood). Porous silicon carbide (SiC) ceramics with wood-like microstructure have been prepared by carbothermal reduction of charcoal/silica composites at 1300-1600 °C in inert Ar atmosphere. The C/SiO2 composites were fabricated by infiltrating silica sol into porous activated biocarbon template. Silica in the charcoal/silica composite, preferentially in the cellular pores, was found to get transformed in forms of fibers and rods due to shrinkage during drying. The changes in the morphology of resulting porous SiC ceramics after heat treatment to 1600 °C, as well as the conversion mechanism of wood to activated carbon and then to porous SiC ceramic have been investigated using scanning electron microscope, x-ray diffraction, thermogravimetric analysis, and differential scanning calorimetry. Activation of carbon prior to silica infiltration has been found to enhance conversion of charcoal to SiC. The pore structure is found to be uniform in these materials than in those made from as-such charcoal/silica composites. This provides a low-cost and eco-friendly route to advanced ceramic materials, with near-net shape potential.

  7. Photocatalytic activity of the binary composite CeO{sub 2}/SiO{sub 2} for degradation of dye

    Energy Technology Data Exchange (ETDEWEB)

    Phanichphant, Sukon [Materials Science Research Center, Faculty of Science, Chiang Mai University, Chiang Mai 50200 (Thailand); Nakaruk, Auppatham [Department of Industrial Engineering, Faculty of Engineering, Naresuan University, Phitsanulok 65000 (Thailand); Centre of Excellence for Innovation and Technology for Water Treatment, Naresuan University, Phitsanulok 65000 (Thailand); Channei, Duangdao, E-mail: duangdaoc@nu.ac.th [Department of Chemistry, Faculty of Science, Naresuan University, Phitsanulok 65000 (Thailand); Research Center for Academic Excellence in Petroleum, Petrochemicals and Advanced Materials, Naresuan University, Phitsanulok 65000 (Thailand)

    2016-11-30

    Highlights: • The enhanced photocatalytic activity of the CeO{sub 2}/SiO{sub 2} composite can be explained by the presence of the SiO{sub 2} adsorbent, which effectively increased the surface area of the CeO{sub 2}. • The increased surface area of CeO{sub 2} should be helpful to facilitate more effective adsorption sites, which enhances the photocatalytic degradation of organic pollutant significantly. • SiO{sub 2} modification is effective in separating the photogenerated electrons and holes, which is of great importance for photocatalytic activity. • SiO{sub 2} acted as a carrier for CeO{sub 2} attachment and avoided the agglomeration of CeO{sub 2} particles. - Abstract: In this study, CeO{sub 2} photocatalyst was modified by composite with SiO{sub 2} to increase efficiency and improve photocatalytic activity. The as-prepared SiO{sub 2} particles have been incorporated into the precursor mixture of CeO{sub 2} by homogeneous precipitation and subsequent calcination process. The phase compositions of CeO{sub 2} before and after compositing with SiO{sub 2} were identified by X-ray diffraction (XRD). The morphology and particle size of CeO{sub 2}/SiO{sub 2} composite was analyzed by high resolution transmission electron microscopy (HRTEM) and field emission scanning electron microscopy (FESEM). The results showed SiO{sub 2} spheres with the particle size approximately 100–120 nm, and a uniform layer of CeO{sub 2} nanoparticles with a diameter of about 5–7 nm that were fully composite to the surfaces of SiO{sub 2}. The X-ray photoelectron spectroscopy (XPS) technique was carried out in order to characterize the change in valence state and composite characteristic by shifted peaks of binding energies. The photocatalytic activity was studied through the degradation of Rhodamine B in aqueous solution under visible light exposure. The highest photocatalytic efficiency of CeO{sub 2}/SiO{sub 2} composite was also obtained. To explain the high photocatalytic

  8. Characterization of SiC–SiC composites for accident tolerant fuel cladding

    Energy Technology Data Exchange (ETDEWEB)

    Deck, C.P., E-mail: Christian.Deck@ga.com; Jacobsen, G.M.; Sheeder, J.; Gutierrez, O.; Zhang, J.; Stone, J.; Khalifa, H.E.; Back, C.A.

    2015-11-15

    Silicon carbide (SiC) is being investigated for accident tolerant fuel cladding applications due to its high temperature strength, exceptional stability under irradiation, and reduced oxidation compared to Zircaloy under accident conditions. An engineered cladding design combining monolithic SiC and SiC–SiC composite layers could offer a tough, hermetic structure to provide improved performance and safety, with a failure rate comparable to current Zircaloy cladding. Modeling and design efforts require a thorough understanding of the properties and structure of SiC-based cladding. Furthermore, both fabrication and characterization of long, thin-walled SiC–SiC tubes to meet application requirements are challenging. In this work, mechanical and thermal properties of unirradiated, as-fabricated SiC-based cladding structures were measured, and permeability and dimensional control were assessed. In order to account for the tubular geometry of the cladding designs, development and modification of several characterization methods were required.

  9. Reaction sintering process of tyranno SA/SiC composites and their characterization

    International Nuclear Information System (INIS)

    Lee, S.P.; Yoon, H.K.; Park, J.S.; Katoh, Y.; Kohyama, A.; Kim, D.H.; Lee, J.K.

    2002-01-01

    This paper deals with the efficiency of fiber preform preparation route for the fabrication of reaction sintering (RS) SiC f /SiC composites and their characterization, including density, microstructure and mechanical property. The applicability of carbon interfacial layer has been investigated in the RS process. The fiber preform was prepared by the consecutive slurry infiltration process, which associated with the combination of constant gas impregnation pressure and different magnitudes of cold pressure. The consecutive slurry infiltration process used for the preparation of fiber preform can be regarded as a promising technique for high density RS-SiC f /SiC composites, even if their mechanical properties depend on the magnitudes of cold pressure used. RS-SiC f /SiC composites entirely showed the morphology of near stoichiometric SiC phase in the intra-fiber bundle matrix, compared to that in the inter-fiber bundle matrix. The carbon interfacial layer was insufficient for the pseudo-ductile failure of RS-SiC f /SiC composites, even if some amount of fiber pull-out and interfacial delamination was observed in the tensile surface of bending test sample

  10. Computational Modeling of Radiation Phenomenon in SiC for Nuclear Applications

    Science.gov (United States)

    Ko, Hyunseok

    Silicon carbide (SiC) material has been investigated for promising nuclear materials owing to its superior thermo-mechanical properties, and low neutron cross-section. While the interest in SiC has been increasing, the lack of fundamental understanding in many radiation phenomena is an important issue. More specifically, these phenomena in SiC include the fission gas transport, radiation induced defects and its evolution, radiation effects on the mechanical stability, matrix brittleness of SiC composites, and low thermal conductivities of SiC composites. To better design SiC and SiC composite materials for various nuclear applications, understanding each phenomenon and its significance under specific reactor conditions is important. In this thesis, we used various modeling approaches to understand the fundamental radiation phenomena in SiC for nuclear applications in three aspects: (a) fission product diffusion through SiC, (b) optimization of thermodynamic stable self-interstitial atom clusters, (c) interface effect in SiC composite and their change upon radiation. In (a) fission product transport work, we proposed that Ag/Cs diffusion in high energy grain boundaries may be the upper boundary in unirradiated SiC at relevant temperature, and radiation enhanced diffusion is responsible for fast diffusion measured in post-irradiated fuel particles. For (b) the self-interstitial cluster work, thermodynamically stable clusters are identified as a function of cluster size, shape, and compositions using a genetic algorithm. We found that there are compositional and configurational transitions for stable clusters as the cluster size increases. For (c) the interface effect in SiC composite, we investigated recently proposed interface, which is CNT reinforced SiC composite. The analytical model suggests that CNT/SiC composites have attractive mechanical and thermal properties, and these fortify the argument that SiC composites are good candidate materials for the cladding

  11. Influence wt.% of SiC and borax on the mechanical properties of AlSi-Mg-TiB-SiC composite by the method of semi solid stir casting

    Science.gov (United States)

    Bhiftime, E. I.; Guterres, Natalino F. D. S.; Haryono, M. B.; Sulardjaka, Nugroho, Sri

    2017-04-01

    SiC particle reinforced metal matrix composites (MMCs) with solid semi stir casting method is becoming popular in recent application (automotive, aerospace). Stirring the semi solid condition is proven to enhance the bond between matrix and reinforcement. The purpose of this study is to investigate the effect of the SiC wt.% and the addition of borax on mechanical properties of composite AlSi-Mg-TiB-SiC and AlSi-Mg-TiB-SiC/Borax. Specimens was tested focusing on the density, porosity, tensile test, impact test microstructure and SEM. AlSi is used as a matrix reinforced by SiC with percentage variations (10, 15, 20 wt.%). Giving wt.% Borax which is the ratio of 1: 4 between wt.% SiC. The addition of 1.5% of TiB gives grain refinement. The use of semi-solid stir casting method is able to increase the absorption of SiC particles into a matrix AlSi evenly. The improved composite presented here can be used as a guideline to make a new composite.

  12. Fabrication of Cf/SiC composite by chemical vapor infiltration

    International Nuclear Information System (INIS)

    Park, Ji Yeon; Kim, Weon Ju

    2003-07-01

    This technical report reviewed the fabrication process of fiber reinforced ceramic composites, characteristics of the chemical vapor infiltration process, and applications for C f /SiC composite to develop a carbon fiber reinforced silicon carbide composite. Infiltration process was performed by the chemical vapor infiltration process using methyltrichlorosilane and hydrogen gas as a source and a diluent, respectively. Infiltration behavior, phase analysis, microstructure observation were carried out. Parameter study results of C f /SiC composite fabricated with some variables such as reaction pressure, reaction temperature, input gas ratio and preform thickness were described

  13. Effect of atmosphere on the fabrication of Si2N2O matrix composites

    Directory of Open Access Journals (Sweden)

    Wei Li

    2018-03-01

    Full Text Available Si2N2O matrix composites were fabricated by solid/gas reaction in air or N2 atmosphere. The effects of atmosphere on the phase and microstructure of the composites were investigated. The reaction mechanism of Si2N2O system was discussed by analysing the variation of the Gibbs free energy with temperature. The effect of N2 and air on sintering of Si2N2O matrix composites was discussed in relation to observed kinetics and thermodynamic calculations. The results showed that gradient structure of Si2N2O matrix composites were obtained in N2 atmosphere. While high N2 concentration was useful for the formation of the pure β-Si3N4 ceramics, low N2 concentration was proposed to form the pure Si2N2O ceramics. However, in the air atmosphere, structure of the Si3N4/SiO2 composites is homogeneous without the gradient structure appearing. Its composition is a little different as the O2 concentration changes.

  14. Stress Wave attenuation in SiC3D/Al Composite

    International Nuclear Information System (INIS)

    Yuan Chunyuan; Wang Yangwei; Li Guoju; Zhang Xu; Gao Jubin

    2013-01-01

    SiC 3D /Al composite is a kind of special composite with interpenetrating network microstructure. The attenuation properties of stress wave propagation along the SiC 3D /Al composite are studied by a Split Hopkinson Pressure Bar system and FEM simulations, and the attenuation mechanism is discussed in this paper. Results show that the attenuation rate of the stress wave in the composite is up to 1.73MPa·mm −1 . The reduction of the amplitude of waves is caused by that plenty of interfaces between SiC and Al within the composite acting with stress waves. When the incident plane wave reaches the SiC 3D /Al interface, reflection wave and transmission wave propagates in different directions along the irregular interface between SiC phase and aluminium phase due to the impedance mismatch of them, which leads to the divergence of stress wave. At the same time, some stress micro-focuses occurs in the aluminium phase for the complex wave superimposition, and some plastic deformation may take place within such micro-regions, which results in the consumption of stress wave energy. In conclusion, the stress wave attenuation is derived from divergence and consumption of stress wave.

  15. Average thermal stress in the Al+SiC composite due to its manufacturing process

    International Nuclear Information System (INIS)

    Miranda, Carlos A.J.; Libardi, Rosani M.P.; Marcelino, Sergio; Boari, Zoroastro M.

    2013-01-01

    The numerical analyses framework to obtain the average thermal stress in the Al+SiC Composite due to its manufacturing process is presented along with the obtained results. The mixing of Aluminum and SiC powders is done at elevated temperature and the usage is at room temperature. A thermal stress state arises in the composite due to the different thermal expansion coefficients of the materials. Due to the particles size and randomness in the SiC distribution, some sets of models were analyzed and a statistical procedure used to evaluate the average stress state in the composite. In each model the particles position, form and size are randomly generated considering a volumetric ratio (VR) between 20% and 25%, close to an actual composite. The obtained stress field is represented by a certain number of iso stress curves, each one weighted by the area it represents. Systematically it was investigated the influence of: (a) the material behavior: linear x non-linear; (b) the carbide particles form: circular x quadrilateral; (c) the number of iso stress curves considered in each analysis; and (e) the model size (the number of particles). Each of above analyzed condition produced conclusions to guide the next step. Considering a confidence level of 95%, the average thermal stress value in the studied composite (20% ≤ VR ≤ 25%) is 175 MPa with a standard deviation of 10 MPa. Depending on its usage, this value should be taken into account when evaluating the material strength. (author)

  16. Sol-gel derived C-SiC composites and protective coatings for sustained durability in the space environment

    Science.gov (United States)

    Haruvy, Yair; Liedtke, Volker

    2003-09-01

    Composites and coatings were produced via the fast sol-gel process of a mixture of alkoxysilane precursors. The composites were comprised of carbon fibers, fabrics, or their precursors as reinforcement, and sol-gel-derived silicon carbide as matrix, aiming at high-temperature stable ceramics that can be utilized for re-entry structures. The protective coatings were comprised of fluorine-rich sol-gel derived resins, which exhibit high flexibility and coherence to provide sustained ATOX protection necessary for LEO space-exposed elements. For producing the composites, the sol-gel-derived resin is cast onto the reinforcement fibers/fabrics mat (carbon or its precursors) to produce a 'green' composite that is being cured. The 'green' composite is converted into a C-SiC composite via a gradual heat-pressure process under inert atmosphere, during which the organic substituents on the silicon atoms undergo internal oxidative pyrolysis via the schematic reaction: (SiRO3/2)n -> SiC + CO2 + H2O. The composition of the resultant silicon-oxi-carbide is tailorable via modifying the composition of the sol-gel reactants. The reinforcement, when made of carbon precursors, is converted into carbon during the heat-and-pressure processing as well. The C-SiC composites thus derived exhibit superior thermal stability and comparable thermal conductivity, combined with good mechanical strength features and failure resistance, which render them greatly applicable for re-entry shielding, heat-exchange pipes, and the like. Fluorine rich sol-gel derived coatings were developed as well, via the use of HF rich sol-gel process. These coatings provide oxidation-protection via the silica formation process, together with flexibility that allows 18,000 repetitive folding of the coating without cracking.

  17. Mechanical behaviour of AlSiC nano composites produced by ball milling and spark plasma sintering =

    Science.gov (United States)

    Buchheim, Claudia Sofia de Andrade Redondo Murilhas

    Neste trabalho foram produzidos nanocompositos de AlSiC misturando aluminio puro com nano particulas de SiC com diâmetro de 45 - 55 nm, usando, de forma sequencial, a tecnica da metalurgia do po e a compactacao por "Spark Plasma Sintering". O composito obtido apresentava graos com 100 nm de diâmetro, encontrandose as particulas de SiC localizadas, principalmente, nas fronteiras de grao. O nanocomposito sob a forma de provetes cilindricos foi submetido a testes de compressao uniaxial e a testes de nanoindentacao para analisar a influencia das nanoparticulas de SiC, da fracao volumica de acido estearico e do tempo de moagem, nas propriedades mecânicas do material. Para efeitos de comparacao, utilizouse o comportamento mecânico do Al puro processado em condicoes similares e da liga de aluminio AA1050O. A tensao limite de elasticidade do nanocomposito com 1% Vol./Vol. de SiC e dez vezes superior a do AA1050. O refinamento de grao a escala nano constitui o principal mecanismo de aumento de resistencia mecânica. Na realidade, o Al nanocristalino sem reforco de particulas de SiC, apresenta uma tensao limite de elasticidade sete vezes superior a da liga AA1050O. A adicao de 0,5 % Vol./Vol. e de 1 % Vol./Vol. de SiC conduzem, respetivamente, ao aumento da tensao limite de elasticidade em 47 % e 50%. O aumento do tempo de moagem e a adicao de acido estearico ao po durante a moagem conduzem apenas a um pequeno aumento da tensao de escoamento. A dureza do material medida atraves de testes de nanoindentacao confirmaram os dados anteriores. A estabilidade das microestruturas do aluminio puro e do nanocomposito AlSiC, foi testada atraves de recozimento de restauracao realizado as temperaturas de 150 °C e 250 °C durante 2 horas. Aparentemente, o tratamento termico nao influenciou as propriedades mecânicas dos materiais, excepto do nanocomposito com 1 % Vol./Vol. de SiC restaurado a temperatura de 250 °C, para o qual se observou uma reducao da tensao limite de elasticidade

  18. Processing and mechanical behavior of Nicalon{reg_sign}/SiC composites with sol-gel derived oxide interfacial coatings

    Energy Technology Data Exchange (ETDEWEB)

    Shanmugham, S.; Liaw, P.K. [Tennessee Univ., Knoxville, TN (United States). Dept. of Materials Science and Engineering

    1996-10-01

    Recent analytical and finite element modeling studies have indicated that low modulus interface materials are desirable for obtaining Nicalon/SiC composites with good toughness. Two oxides, Al titanate and mullite, were chosen on this basis as interface materials. The oxide and C coatings were deposited by sol-gel and CVD, respectively. Nicalon/SiC composites with oxide/C and C/oxide/C interfaces were fabricated and evaluated for flexure strength in the as-processed and oxidized conditions. Composites with C/oxide/C interfaces retained considerable strength and damage-tolerant behavior even after 500 h oxidation at 1000 C in air. The C/oxide/C interface shows promise as a viable oxidation-resistant interface alternative to C or BN interfaces.

  19. Determination of material properties for short fibre reinforced C/C-SiC

    Directory of Open Access Journals (Sweden)

    Hausherr J.-M.

    2015-01-01

    Full Text Available Determining the mechanical properties of short fibre reinforced CMC using standard sized coupons has always been a challenge due to a high statistical scattering of the measured values. Although the random orientation of short fibres results in a quasi-isotropic material behavior of 2D-structures with a sufficiently large volume, the small volume typical for test coupons usually results in a non-isotropic fibre orientation in the tested volume. This paper describes a method for manufacturing unidirectional oriented short fibre reinforced CMC materials and presents material properties of UD-C/C-SiC. After verifying the fibre orientation of the CMC using micro-computed tomography, coupons were extracted to determine the orthotropic material properties. These orthotropic material properties were then used to predict the properties of C/C-SiC with randomly distributed short fibres. To validate the method, micro-computed tomography is used to quantitatively determine the fibre orientation within coupons extracted from randomly distributed short fibre C/C-SiC. After mechanical three-point-bending tests, the measured stiffness and bending strength is compared with the predicted properties. Finally, the data are used to devise a method suited for reducing the inherent large spread of material properties associated with the measurement of CMC materials with randomly distributed short fibres.

  20. Thermal Shock Properties of Cladding with SiC{sub f}/SiC Composite Protective Films

    Energy Technology Data Exchange (ETDEWEB)

    Lee, Donghee; Park, Kwangheon [Kyunghee University, Yongin (Korea, Republic of); Kim, Weonju; Park, Jiyeon; Kim, Daejong; Lee, Hyeon Geun [Korea Atomic Energy Research Institute, Daejeon (Korea, Republic of)

    2015-05-15

    In general, Zr-4 alloy is used for such nuclear fuel cladding. Zr-4 possesses a very small thermal neutron absorption cross-section and has superior corrosion resistance in the normal operating conditions of a nuclear reactor. However, in the case of a critical accident such as a LOCA (loss-of-coolant accident) in the Fukushima disaster, the risk of hydrogen explosion becomes serious. That is, in the case of coolant leakage, a dramatic reaction between the nuclear fuel cladding and steam can cause a heating reaction accompanied by rapid high-temperature oxidation, while creating a huge amount of hydrogen. Hence, the search for an alternative material for nuclear fuel cladding is being actively undertaken. Ceramic-based nuclear fuel cladding is receiving much attention as a means of improving safety. SiC has excellent properties of resistance to high temperature and high exposure and superior mechanical properties, as well as a very small thermal neutron absorption cross-section (0.09 barns), which causes almost no decrease in mechanical strength or volume change following exposure. This experiment examined the thermal shock properties and microstructure of cladding that has SiCf/SiC composite protective film, using polycarbosilane preceramic polymer.

  1. Plasma-assisted ALD for the conformal deposition of SiO2 : process, material and electronic properties

    NARCIS (Netherlands)

    Dingemans, G.; Helvoirt, van C.A.A.; Pierreux, D.; Keuning, W.; Kessels, W.M.M.

    2012-01-01

    Plasma-assisted atomic layer deposition (ALD) was used to deposit SiO2 films in the temperature range of Tdep = 50–400°C on Si(100). H2Si[N(C2H5)2]2 and an O2 plasma were used as Si precursor and oxidant, respectively. The ALD growth process and material properties were characterized in detail.

  2. Composition and crystallization kinetics of R2O-Al2O3-SiO2 glass-ceramics

    International Nuclear Information System (INIS)

    Xiong, Dehua; Cheng, Jinshu; Li, Hong

    2010-01-01

    The crystallization behavior and microstructure of R 2 O-Al 2 O 3 -SiO 2 (R means K, Na and Li) glass were investigated by means of differential scanning calorimeter (DSC), X-ray diffraction (XRD) and scanning electron microscopy (SEM). The crystallization kinetic parameters including the crystallization apparent activation energy (E a ), the Avrami parameter (n), glass transition temperature (T g ) and the activity energy of glass transition (E t ) were also measured with different methods. The results have shown that: the DSC traces of composition A parent glass have two different precipitation crystallization peaks corresponding to E a1 (A) = 151.4 kJ/mol (Li 2 SiO 3 ) and E a2 (A) = 623.1 kJ/mol (Li 2 Si 2 O 5 ), the average value of n = 1.70 (Li 2 Si 2 O 5 ) for the surface crystallization and E t (A) = 202.8 kJ/mol. And E a (B) = 50.7 kJ/mol (Li 2 SiO 3 ), the average value of n = 3.89 (Li 2 SiO 3 ) for the bulk crystallization and E t (B) = 220.4 kJ/mol for the composition B parent glass. Because of the content of R 2 O is bigger than composition A, composition B parent glass has a lower E a , T g and a larger n, E t .

  3. Influence of microstructure on hydrothermal corrosion of chemically vapor processed SiC composite tubes

    Science.gov (United States)

    Kim, Daejong; Lee, Ho Jung; Jang, Changheui; Lee, Hyeon-Geun; Park, Ji Yeon; Kim, Weon-Ju

    2017-08-01

    Multi-layered SiC composites consisting of monolithic SiC and a SiCf/SiC composite are one of the accident tolerant fuel cladding concepts in pressurized light water reactors. To evaluate the integrity of the SiC fuel cladding under normal operating conditions of a pressurized light water reactor, the hydrothermal corrosion behavior of multi-layered SiC composite tubes was investigated in the simulated primary water environment of a pressurized water reactor without neutron fluence. The results showed that SiC phases with good crystallinity such as Tyranno SA3 SiC fiber and monolithic SiC deposited at 1200 °C had good corrosion resistance. However, the SiC phase deposited at 1000 °C had less crystallinity and severely dissolved in water, particularly the amorphous SiC phase formed along grain boundaries. Dissolved hydrogen did not play a significant role in improving the hydrothermal corrosion resistance of the CVI-processed SiC phases containing amorphous SiC, resulting in a significant weight loss and reduction of hoop strength of the multi-layered SiC composite tubes after corrosion.

  4. Strength and conductivity of unidirectional copper composites reinforced by continuous SiC fibers

    International Nuclear Information System (INIS)

    Kimmig, S.; Allen, I.; You, J.H.

    2013-01-01

    A SiC long fiber-reinforced copper composite offers a beneficial combination of high strength and high thermal conductivity at elevated temperatures. Both properties make the composite a promising material for the heat sink of high-heat-flux components. In this work, we developed a novel Cu/SiC f composite using the Sigma fiber. Based on HIP technique, a metallurgical process was established for fabricating high quality specimens using a TiC interface coating. Extensive tensile tests were conducted on the unidirectionally reinforced composite at 20 °C and 300 °C for a wide range of fiber volume fraction (V f ). In this paper, a large amount of test data is presented. The transversal thermal conductivity varies from 260 to 130 W/mK at 500 °C as V f is increased from 13% to 37%. The tensile strength reached up to 1246 MPa at 20 °C for V f = 37.6%, where the fracture strain was limited to 0.8%. The data of both elastic modulus and ultimate strength exhibited a good agreement with the rule-of-mixture predictions indicating a high quality of the materials. The strength of the composite with the Sigma fibers turned out to be superior to those of the SCS6 fibers at 300 °C, although the SCS6 fiber actually has a higher strength than the Sigma fiber. The fractographic pictures of tension test and fiber push-out test manifested a sufficient interfacial bonding

  5. Synthesis of SiC decorated carbonaceous nanorods and its hierarchical composites Si@SiC@C for high-performance lithium ion batteries

    Energy Technology Data Exchange (ETDEWEB)

    Wang, Chundong [School of Optical and Electronic Information, Huazhong University of Science and Technology, Wuhan 430074 (China); Center of Super-Diamond and Advanced Films (COSDAF), Department of Physics and Materials Science, City University of Hong Kong, Hong Kong SAR (China); Li, Yi, E-mail: liyi@suda.edu.cn [College of Chemistry, Chemical Engineering and Materials Science, Soochow University, Suzhou (China); Center of Super-Diamond and Advanced Films (COSDAF), Department of Physics and Materials Science, City University of Hong Kong, Hong Kong SAR (China); Ostrikov, Kostya [School of Chemistry, Physics and Mechanical Engineering, Queensland University of Technology, Brisbane, Queensland 4000 (Australia); Plasma Nanoscience, Industrial Innovation Program, CSIRO Manufacturing Flagship, Lindfield, New South Wales 2070 (Australia); Yang, Yonggang [College of Chemistry, Chemical Engineering and Materials Science, Soochow University, Suzhou (China); Zhang, Wenjun, E-mail: apwjzh@cityu.edu.hk [Center of Super-Diamond and Advanced Films (COSDAF), Department of Physics and Materials Science, City University of Hong Kong, Hong Kong SAR (China)

    2015-10-15

    SiC- based nanomaterials possess superior electric, thermal and mechanical properties. However, due to the tricky synthesis process, which needs to be carried out under high temperature with multi-step reaction procedures, the further application is dramatically limited. Herein, a simple as well as a controllable approach is proposed for synthesis of SiC- based nanostructures under low temperature. Phenyl-bridged polysilsesquioxane was chosen as the starting material to react with magnesium at 650 °C, following which SiC@C nanocomposites were finally obtained, and it maintains the original bent rod-like architecture of polysilsesquioxanes. The possible formation process for the nanocomposites can proposed as well. The electrochemical behaviour of nanocomposites was accessed, verifying that the synthesized SiC@C nanocomposites deliver good electrochemical performance. Moreover, SiC@C also shows to be a promising scaffold in supporting Si thin film electrode in achieving stable cycling performance in lithium ion batteries. - Highlights: • SiC@C bent nanorods were synthesized with a magnesium reaction approach. • Carbon nanorod spines studded with ultrafine β-SiC nanocrystallines was realized. • The synthesized SiC@C keeps the original rod-like structure of polysilsesquioxanes. • The possible formation process for the nanocomposites was analysed and proposed. • Si@SiC@C nanocomposites reveal good electrochemical performance in LIBs.

  6. Microstructure and mechanical properties of CVI carbon fiber/SiC composites

    International Nuclear Information System (INIS)

    Noda, T.; Araki, H.; Abe, F.; Okada, M.

    1992-01-01

    Microstructures and mechanical properties of carbon fiber/SiC composites prepared with chemical vapor infiltration (CVI) were examined to optimize the process conditions such as reactant and infiltration temperature. Ethyl-trichloro-silane (ETS) and methyl-trichloro-silane (MTS) were used as a source of SiC. CVI was conducted for 108 ks at maximum under a pressure of 13.3 kPa at 1273-1573 K. The composite with a density higher than 80% was obtained at 1373-1423 K and 1423-1374 K from ETS and MTS, respectively. The main matrix formed was β SiC for both reactants. However, silicon also deposited in SiC matrix for MTS. Preferential wettability of SiC to the carbon fiber was observed, and graphite was detected in the interface between the matrix and the carbon fiber by TEM. Mechanical properties were evaluated by bend tests at room temperature. High strength of around 800 MPa was obtained for the composites if the thickness of the surface coated layer was less than 50 μm. Apparent fracture thoughness of the present carbon fiber/SiC composite was 6-10 MPa m 1/2 at room temperature. (orig.)

  7. Influence of load and reinforcement content on selected tribological properties of Al/SiC/Gr hybrid composites

    Directory of Open Access Journals (Sweden)

    Sandra Veličković

    2018-04-01

    Full Text Available Hybrid materials with the metal matrix are important engineering materials due to their outstanding mechanical and tribological properties. Here are presented selected tribological properties of the hybrid composites with the matrix made of aluminum alloy and reinforced by the silicon carbide and graphite particles. The tribological characteristics of such materials are superior to characteristics of the matrix – the aluminum alloy, as well as to characteristics of the classical metal-matrix composites with a single reinforcing material. Those characteristics depend on the volume fractions of the reinforcing components, sizes of the reinforcing particles, as well as on the fabrication process of the hybrid composites. The considered tribological characteristics are the friction coefficient and the wear rate as functions of the load levels and the volume fractions of the graphite and the SiC particles. The wear rate increases with increase of the load and the Gr particles content and with reduction of the SiC particles content. The friction coefficient increases with the load, as well as with the SiC particles content increase.

  8. Steel-SiC Metal Matrix Composite Development. Final report

    International Nuclear Information System (INIS)

    Smith, Don D.

    2005-01-01

    One of the key materials challenges for Generation IV reactor technology is to improve the strength and resistance to corrosion and radiation damage in the metal cladding of the fuel pins during high-temperature operation. Various candidate Gen IV designs call for increasing core temperature to improve efficiency and facilitate hydrogen production, operation with molten lead moderator to use fast neutrons. Fuel pin lifetime against swelling and fracture is a significant limit in both respects. The goal of this project is to develop a method for fabricating SiC-reinforced high-strength steel. We are developing a metal-matrix composite (MMC) in which SiC fibers are be embedded within a metal matrix of steel, with adequate interfacial bonding to deliver the full benefit of the tensile strength of the SiC fibers in the composite. In the context of the mission of the SBIR program, this Phase I grant has been successful. The development of a means to attain interfacial bonding between metal and ceramic has been a pacing challenge in materials science and technology for a century. It entails matching or grading of thermal expansion across the interface and attaining a graded chemical composition so that impurities do not concentrate at the boundary to create a slip layer. To date these challenges have been solved in only a modest number of pairings of compatible materials, e.g. Kovar and glass, titanium and ceramic, and aluminum and ceramic. The latter two cases have given rise to the only presently available MMC materials, developed for aerospace applications. Those materials have been possible because the matrix metal is highly reactive at elevated temperature so that graded composition and intimate bonding happens naturally at the fiber-matrix interface. For metals that are not highly reactive at processing temperature, however, successful bonding is much more difficult. Recent success has been made with copper MMCs for cooling channels in first-wall designs for fusion

  9. Simulation of Degraded Properties of 2D plain Woven C/SiC Composites under Preloading Oxidation Atmosphere

    Science.gov (United States)

    Chen, Xihui; Sun, Zhigang; Sun, Jianfen; Song, Yingdong

    2017-12-01

    In this paper, a numerical model which incorporates the oxidation damage model and the finite element model of 2D plain woven composites is presented for simulation of the oxidation behaviors of 2D plain woven C/SiC composite under preloading oxidation atmosphere. The equal proportional reduction method is firstly proposed to calculate the residual moduli and strength of unidirectional C/SiC composite. The multi-scale method is developed to simulate the residual elastic moduli and strength of 2D plain woven C/SiC composite. The multi-scale method is able to accurately predict the residual elastic modulus and strength of the composite. Besides, the simulated residual elastic moduli and strength of 2D plain woven C/SiC composites under preloading oxidation atmosphere show good agreements with experimental results. Furthermore, the preload, oxidation time, temperature and fiber volume fractions of the composite are investigated to show their influences upon the residual elastic modulus and strength of 2D plain woven C/SiC composites.

  10. Fabrication of laminated ZrC-SiC composite by vacuum hot-pressing sintering

    Directory of Open Access Journals (Sweden)

    Yuanyuan Li

    2015-03-01

    Full Text Available Laminated ZrC-SiC ceramic was prepared through tape casting and hot pressing. The green tapes of ZrC and SiC were prepared at room temperature. In order to improve the density of composite, the binder of green tapes were removed at 550 °C for 1 h. The laminated structure and the cracks propagation path, which is not a straight line, are observed by optical metalloscope. The compact laminated ZrC-SiC composite sintered by vacuum hot-pressing at 1650 °C for 90 min under pressure of 20 MPa was researched by X-ray diffraction and scanning electron microscopy (SEM equipped with energy dispersive X-ray analysis. The results showed that interlayer bonding is tight, and no disordered phase has formed in the interlayers of ZrC or SiC, and the combination mode is physical mechanism.

  11. Lateral boron distribution in polycrystalline SiC source materials

    DEFF Research Database (Denmark)

    Linnarsson, M. K.; Kaiser, M.; Liljedahl, R.

    2013-01-01

    . The materials are co-doped materials with nitrogen and boron to a concentration of 1x1018 cm-3 and 1x1019 cm-3, respectively. Depth profiles as well as ion images have been recorded. According to ocular inspection, the analyzed poly-SiC consists mainly of 4H-SiC and 6H-SiC grains. In these grains, the boron...

  12. MICROSTRUCTURAL AND MECHANICAL CHARACTERIZATION OF 2-D AND 3-D SiC/SiNC CERAMIC MATRIX COMPOSITES

    Science.gov (United States)

    2018-02-23

    any other person or corporation; or convey any rights or permission to manufacture, use, or sell any patented invention that may relate to them...AFRL/RXCC 5d. PROJECT NUMBER 4347 5e. TASK NUMBER 5f. WORK UNIT NUMBER X0S7 7. PERFORMING ORGANIZATION NAME(S) AND ADDRESS(ES) AFRL/RXCC...0.145-inch material.. 15. SUBJECT TERMS Ceramic-matrix composites, SiC/SiNC, tensile, interlaminar shear, creep, stress rupture, elevated

  13. Synthesis of ceramic powders of La9,56 (SiO4)6O2,34 and La9,8Si5,7MgO,3O26,4 by modified sol-gel process

    International Nuclear Information System (INIS)

    Lira, Sabrina Lopes; Paiva, Mayara Rafaela Soares; Misso, Agatha Matos; Elias, Daniel Ricco; Yamagata, Chieko

    2012-01-01

    Lanthanum silicate oxyapatite materials are promising for application as electrolyte in solid oxide fuel cells because of high ionic conductivity at temperatures between 600 deg C and 800 deg C. In this work, oxyapatites with the composition La 9,56 (SiO 4 ) 6 O 2,34 , and La 9,8 Si 5,7 Mg 0,3 O 26,4 were synthesized by using the sol-gel method, followed by precipitation. Initially, the gel of silica was synthesized from sodium silicate solution, by acid catalysis using lanthanum and magnesium chloride solution. Then, the La and Mg hydroxides were precipitated with NaOH in the gel. The powders were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM) and measurements of specific surface area. The crystalline oxyapatite phase of La 9,56 (SiO 4 ) 6 O 2,34 , and was La 9,8 Si 5,7 Mg 0,3 O 26,4 obtained by calcination at 900 deg C for 2 and 1h respectively (author)

  14. Laser cladding of Al-Si/SiC composite coatings : Microstructure and abrasive wear behavior

    NARCIS (Netherlands)

    Anandkumar, R.; Almeida, A.; Vilar, R.; Ocelik, V.; De Hosson, J.Th.M.

    2007-01-01

    Surface coatings of an Al-Si-SiC composite were produced on UNS A03560 cast Al-alloy substrates by laser cladding using a mixture of powders of Al-12 wt.% Si alloy and SiC. The microstructure of the coatings depends considerably on the processing parameters. For a specific energy of 26 MJ/m2 the

  15. Superhydrophobicity and regeneration of PVDF/SiO2 composite films

    Science.gov (United States)

    Liu, Tao; Li, Xianfeng; Wang, Daohui; Huang, Qinglin; Liu, Zhen; Li, Nana; Xiao, Changfa

    2017-02-01

    Superhydrophobicity of polymers is easily destroyed by careless touching due to the softness of microstructures. In this study, based on a well-constructed polyvinylidene fluoride (PVDF) surface, a novel superhydrophobic PVDF/SiO2 composite film was fabricated by adding hydrophobic SiO2 nanoparticle and solvent into a coagulation bath. The water contact angle of the composite film reached 162.3° and the sliding angle was as low as 1.5°. More importantly, the composite film could be regenerated only through immersing the composite film in the designed regeneration agent. The composition of the designed regeneration agent ensured that SiO2 nanoparticles were firmly adhered on the film surface even under the ultrasonic cleaning. Hence, the superhydrophobicity and self-cleaing property could be regenerated and maintained effectively, and moreover, these propeties could resist a proper pressure. In addition, after many rubbing-regenerating cycles, the regeneration method was still valid.

  16. Effects of Heat Treatment on SiC-SiC Ceramic Matrix Composites

    Science.gov (United States)

    Knauf, Michael W.

    Residual stresses resulting from the manufacturing process found within a silicon carbide/silicon carbide (SiC/SiC) ceramic matrix composite were thoroughly investigated through the use of high-energy X-ray diffraction and Raman microspectroscopy. The material system studied was a Rolls-Royce composite produced with Hi-Nicalon fibers woven into a five harness satin weave, coated with boron nitride and silicon carbide interphases, and subsequently infiltrated with silicon carbide particles and a silicon matrix. Constituent stress states were measured before, during, and after heat treatments ranging from 900 °C to 1300 °C for varying times between one and sixty minutes. Stress determination methods developed through these analyses can be utilized in the development of ceramic matrix composites and other materials employing boron-doped silicon. X-ray diffraction experiments were performed at the Argonne National Laboratory Advanced Photon Source to investigate the evolution of constituent stresses through heat treatment, and determine how stress states are affected at high temperature through in situ measurements during heat treatments up to 1250 °C for 30 minutes. Silicon carbide particles in the as-received condition exhibited a nearly isotropic stress state with average tensile stresses of approximately 300 MPa. The silicon matrix exhibited a complimentary average compressive stress of approximately 300 MPa. Strong X-ray diffraction evidence is presented demonstrating solid state boron diffusion and increased boron solubility found in silicon throughout heat treatment. While the constituent stress states did evolve through the heat treatment cycles, including approaching nearly stress-free conditions at temperatures close to the manufacturing temperature, no permanent relaxation of stress was observed. Raman spectroscopy was utilized to investigate stresses found within silicon carbide particles embedded within the matrix and the silicon matrix as an alternate

  17. One-pot synthesis of NiO/C composite nanoparticles as anode materials for lithium-ion batteries

    Energy Technology Data Exchange (ETDEWEB)

    Zhang, Lipeng, E-mail: lipeng.zhang@jcu.edu.au [School of Chemical Engineering, Shandong University of Technology, Zibo 255049 (China); College of Science, Technology and Engineering, James Cook University, Douglas, Queensland 4811 (Australia); Mu, Jiechen; Wang, Zhao; Li, Guomin; Zhang, Yanling [School of Chemical Engineering, Shandong University of Technology, Zibo 255049 (China); He, Yinghe, E-mail: yinghe.he@jcu.edu.au [College of Science, Technology and Engineering, James Cook University, Douglas, Queensland 4811 (Australia)

    2016-06-25

    Nanostructured NiO/C composite particles with controlled carbon content for lithium-ion battery anode were prepared via a one-pot hydrothermal approach and subsequent calcination in a high purity nitrogen atmosphere. The composites were composed of amorphous carbon and nanocrystalline NiO. The structure of the NiO crystals was determined with X-ray diffraction (XRD) analysis and the content of carbon was calculated from the energy dispersive spectroscopy (EDS) results. Scanning electron microscopy (SEM) images showed a relatively narrow distribution of particle size for both the neat NiO and NiO/C nanoparticles. Electrochemical performance measurements demonstrated that, after 50 cycles, NiO/C nanocomposites maintained a high reversible capacity of 585.9 mAh g{sup −1}, much higher than that of 356.1 mAh g{sup −1} of the neat NiO nanoparticles without carbon. The NiO/C nanoparticles also exhibited a remarkable discharge capacity, a high charge/discharge rate and an excellent cycle stability. The improvements can be attributed to the even carbon coating on the NiO particles, which significantly enhances the conductivity and improves the structural stability of the electrode. - Highlights: • NiO/C nanocomposite material is prepared via a one-pot hydrothermal approach. • Both NiO and NiO/C composite have a narrow particle size distribution. • Carbon in the NiO/C enhanced the conductivity and suppressed particle aggregation. • NiO/C composites maintained a reversible capacity of 585.9 mAh g{sup −1} after 50 cycles.

  18. Correlations Between Arrangement of Reinforcing Particles and Mechanical Properties in Pressure Die Cast AlSi11-SiC Composites

    Directory of Open Access Journals (Sweden)

    Konopka Z.

    2014-06-01

    Full Text Available The work presents the investigation results concerning the structure of composite pressure die castings with AlSi11 alloy matrix reinforced with SiC particles. Examination has been held for composites containing 10 and 20 volume percent of SiC particles. The arrangement of the reinforcing particles within the matrix has been qualitatively assessed in specimens cut out of the castings. The index of distribution was determined on the basis of particle count in elementary measuring fields. The tensile strength, the yield point and elongation of the obtained composite were measured. Composite castings were produced at various values of the piston velocity in the second stage of injection, diverse intensification pressure values, and various injection gate width values. The regression equation describing the change of the considered arrangement particles index and mechanical properties were found as a function of the pressure die casting parameters. The infuence of particle arrangement in composite matrix on mechanical properties these material was examined and the functions of correlations between values were obtained. The conclusion gives the analysis and the interpretation of the obtained results.

  19. Film Cooled Recession of SiC/SiC Ceramic Matrix Composites: Test Development, CFD Modeling and Experimental Observations

    Science.gov (United States)

    Zhu, Dongming; Sakowski, Barbara A.; Fisher, Caleb

    2014-01-01

    SiCSiC ceramic matrix composites (CMCs) systems will play a crucial role in next generation turbine engines for hot-section component applications because of their ability to significantly increase engine operating temperatures, reduce engine weight and cooling requirements. However, the environmental stability of Si-based ceramics in high pressure, high velocity turbine engine combustion environment is of major concern. The water vapor containing combustion gas leads to accelerated oxidation and corrosion of the SiC based ceramics due to the water vapor reactions with silica (SiO2) scales forming non-protective volatile hydroxide species, resulting in recession of the ceramic components. Although environmental barrier coatings are being developed to help protect the CMC components, there is a need to better understand the fundamental recession behavior of in more realistic cooled engine component environments.In this paper, we describe a comprehensive film cooled high pressure burner rig based testing approach, by using standardized film cooled SiCSiC disc test specimen configurations. The SiCSiC specimens were designed for implementing the burner rig testing in turbine engine relevant combustion environments, obtaining generic film cooled recession rate data under the combustion water vapor conditions, and helping developing the Computational Fluid Dynamics (CFD) film cooled models and performing model validation. Factors affecting the film cooled recession such as temperature, water vapor concentration, combustion gas velocity, and pressure are particularly investigated and modeled, and compared with impingement cooling only recession data in similar combustion flow environments. The experimental and modeling work will help predict the SiCSiC CMC recession behavior, and developing durable CMC systems in complex turbine engine operating conditions.

  20. Pressureless sintering of dense Si3N4 and Si3N4/SiC composites with nitrate additives

    International Nuclear Information System (INIS)

    Kim, J.Y.; Iseki, Takayoshi; Yano, Toyohiko

    1996-01-01

    The effect of aluminum and yttrium nitrate additives on the densification of monolithic Si 3 N 4 and a Si 3 N 4 /SiC composite by pressureless sintering was compared with that of oxide additives. The surfaces of Si 3 N 4 particles milled with aluminum and yttrium nitrates, which were added as methanol solutions, were coated with a different layer containing Al and Y from that of Si 3 N 4 particles milled with oxide additives. Monolithic Si 3 N 4 could be sintered to 94% of theoretical density (TD) at 1,500 C with nitrate additives. The sintering temperature was about 100 C lower than the case with oxide additives. After pressureless sintering at 1,750 C for 2 h in N 2 , the bulk density of a Si 3 N 4 /20 wt% SiC composite reached 95% TD with nitrate additives

  1. Effects of sintering additives on the microstructural and mechanical properties of the ion-irradiated SiCf/SiC

    Science.gov (United States)

    Fitriani, Pipit; Sharma, Amit Siddharth; Yoon, Dang-Hyok

    2018-05-01

    SiCf/SiC composites containing three different types of sintering additives viz. Sc-nitrate, Al2O3-Sc2O3, and Al2O3-Y2O3, were subjected to ion irradiation using 0.2 MeV H+ ions with a fluence of 3 × 1020 ions/m2 at room temperature. Although all composites showed volumetric swelling upon ion irradiation, SiCf/SiC with Sc-nitrate showed the smallest change followed by those with the Al2O3-Sc2O3 and Al2O3-Y2O3 additives. In particular, SiCf/SiC containing the conventional Al2O3-Y2O3 additive revealed significant microstructural changes, such as surface roughening and the formation of cracks and voids, resulting in reduced fiber pullout upon irradiation. On the other hand, the SiCf/SiC with Sc-nitrate showed the highest resistance against ion irradiation without showing any macroscopic changes in surface morphology and mechanical strength, indicating the importance of the sintering additive in NITE-based SiCf/SiC for nuclear structural applications.

  2. Development and application of graphite-SiO2/Al2O3/Nb2O5-methylene blue (GRP-SiAlNb-MB composite for electrochemical determination of dopamine

    Directory of Open Access Journals (Sweden)

    Juliana de Fátima Giarola

    2017-03-01

    Full Text Available In the present paper an amperometric sensor based on graphite-SiO2/Al2O3/Nb2O5-methylene blue (GRP-SiAlNb-MB composite has been successfully prepared for dopamine (DA determination in real samples. The electrochemical behavior of DA at the GRP-SiAlNb-MB has been evaluated by employing cyclic voltammetry. The best ratio (m/m of GRP-SiAlNb-MB composite was found to be 1:0.54. Under optimized conditions (pH 7.5 in 0.15 mol L−1 phosphate buffer the amperometry method responds linearly to DA from 5.0 up to 500.0 μmol L−1 (r = 0.995 with limits of detection and quantification of 1.49 and 4.97 μmol L−1, respectively. The developed method was successfully applied for DA determination in real samples of pharmaceutical formulations and can be used for routine quality control analysis of pharmaceutical formulations containing DA. The use of inorganic matrix SiAlNb was found to be very useful to adsorb MB in the composite material with further improvement of the anodic peak current of DA.

  3. Preparation of Si/TiO2 Composite by the Sol-Gel Method Using As the Lithium-Ion Battery Anode

    Science.gov (United States)

    Wang, Quanwei; Ban, Yueqin; Zhou, Hengwei; Zhang, Lili; Huang, Yineng; Shao, Weiquan; Chen, Shaou

    2017-10-01

    Si was a promising anode material for next-generation LIBs due to its extremely large capacity of 4200mAh/g (Li4.4Si phase). However, during repeated lithium insertion/extraction processes, the accompanied huge volume change (400%) induced the structural failure of the active material and resulted in rapid capacity fading. To overcome this problem, Si/TiO2 composite with different mole ratio were prepared by the sol-gel method. The inclusion of TiO2 not only worked as a stable electric conductive pathway but also buffered the volume expansion of the Si during the process of charging and discharging. The Si/TiO2 composite with different mole ratio of 1:2, 1:3, 1:4 electrode reaches 480mAh/g, 2590mAh/g and 980mAh/g, and it delivered a charge capacity of 461mAh/g, 2510mAh/g and 891mAh/g at the first cycle, corresponding to an initial coulombic efficiency of 96%, 96% and 91%. In contrast, the cell with the pure Si nanoparticle exhibited an initial discharge/charge capacity of 48 and 33mAh/g, respectively, which was much lower than the Si/TiO2 composite electrode.

  4. Thermal conductivity analysis of SiC ceramics and fully ceramic microencapsulated fuel composites

    International Nuclear Information System (INIS)

    Lee, Hyeon-Geun; Kim, Daejong; Lee, Seung Jae; Park, Ji Yeon; Kim, Weon-Ju

    2017-01-01

    Highlights: • Thermal conductivity of SiC ceramics and FCM pellets was measured and discussed. • Thermal conductivity of FCM pellets was analyzed by the Maxwell-Eucken equation. • Effective thermal conductivity of TRISO particles applied in this study was assumed. - Abstract: The thermal conductivity of SiC ceramics and FCM fuel composites, consisting of a SiC matrix and TRISO coated particles, was measured and analyzed. SiC ceramics and FCM pellets were fabricated by hot press sintering with Al_2O_3 and Y_2O_3 sintering additives. Several factors that influence thermal conductivity, specifically the content of sintering additives for SiC ceramics and the volume fraction of TRISO particles and the matrix thermal conductivity of FCM pellets, were investigated. The thermal conductivity values of samples were analyzed on the basis of their microstructure and the arrangement of TRISO particles. The thermal conductivity of the FCM pellets was compared to that predicted by the Maxwell-Eucken equation and the thermal conductivity of TRISO coated particles was calculated. The thermal conductivity of FCM pellets in various sintering conditions was in close agreement to that predicted by the Maxwell-Eucken equation with the fitted thermal conductivity value of TRISO particles.

  5. Pressureless sintering behavior and mechanical properties of ZrB2–SiC composites: effect of SiC content and particle size

    Directory of Open Access Journals (Sweden)

    Mehri Mashhadi

    2015-10-01

    Full Text Available In the present paper, ZrB2–SiC composites were prepared by pressureless sintering at temperatures of 2000–2200 °C for 1 h under argon atmosphere. In order to prepare composite samples, ZrB2 powder was milled for 2 h, then the reinforcing particles including of micron and nano-sized SiC powder were added. The mixtures were formed and, after the pyrolysis, they were sintered. Densification, microstructural and mechanical properties of ZrB2–SiC composites were investigated. The shrinkage of samples was measured both before and after the sintering, and the microstructure of samples was examined using scanning electron microscopy (SEM, equipped with EDS spectroscopy. Both mass fraction and size of SiC powder have a great effect on relative density, porosity, shrinkage, hardness and microstructure of these composites. The highest relative density and hardness were 98.12% and 15.02 GPa, respectively, in ZrB2–10 wt% SiCnano composite sintered at 2200 °C.

  6. Phenomenological inelastic constitutive equations for SiC and SiC fibers under irradiation

    International Nuclear Information System (INIS)

    El-Azab, A.; Ghoniem, N.M.

    1994-01-01

    Experimental data on irradiation-induced dimensional changes and creep in β-SiC and SiC fibers is analyzed, with the objective of studying the constitutive behavior of these materials under high-temperature irradiation. The data analysis includes empirical representation of irradiation-induced dimensional changes in SiC matrix and SiC fibers as function of time and irradiation temperature. The analysis also includes formulation of simple scaling laws to extrapolate the existing data to fusion conditions on the basis of the physical mechanisms of radiation effects on crystalline solids. Inelastic constitutive equations are then developed for SCS-6 SiC fibers, Nicalon fibers and CVD SiC. The effects of applied stress, temperature, and irradiation fields on the deformation behavior of this class of materials are simultaneously represented. Numerical results are presented for the relevant creep functions under the conditions of the fusion reactor (ARIES IV) first wall. The developed equations can be used in estimating the macro mechanical properties of SiC-SiC composite systems as well as in performing time-dependent micro mechanical analysis that is relevant to slow crack growth and fiber pull-out under fusion conditions

  7. Structure and chemistry of passivated SiC/SiO{sub 2} interfaces

    Energy Technology Data Exchange (ETDEWEB)

    Houston Dycus, J.; Xu, Weizong; LeBeau, James M. [Department of Materials Science and Engineering, North Carolina State University, Raleigh, North Carolina 27695-7907 (United States); Lichtenwalner, Daniel J.; Hull, Brett; Palmour, John W. [Power Devices R& D, Wolfspeed, A Cree Company, Research Triangle Park, North Carolina 27709 (United States)

    2016-05-16

    Here, we report on the chemistry and structure of 4H-SiC/SiO{sub 2} interfaces passivated either by nitric oxide annealing or Ba deposition. Using aberration corrected scanning transmission electron microscopy and spectroscopy, we find that Ba and N remain localized at SiC/SiO{sub 2} interface after processing. Further, we find that the passivating species can introduce significant changes to the near-interface atomic structure of SiC. Specifically, we quantify significant strain for nitric oxide annealed sample where Si dangling bonds are capped by N. In contrast, strain is not observed at the interface of the Ba treated samples. Finally, we place these results in the context of field effect mobility.

  8. Effect of fiber directionality on the static and dynamic mechanical properties of 3D SiCf/SiC composites

    International Nuclear Information System (INIS)

    Hou, Zhenhua; Luo, Ruiying; Yang, Wei; Xu, Huaizhe; Han, Tao

    2016-01-01

    The static and dynamic mechanical properties of three-dimensional (3D) 4-directional and 3D 5-directional braided SiC f /SiC composites fabricated by polymer infiltration and pyrolysis (PIP) were investigated using static and dynamic bending tests, as well as microstructural characterization. X-ray diffraction revealed that polycarbosilane was converted into a matrix of crystalline β-SiC after PIP cycling. Test results indicated that the density, flexural strength, elastic modulus, fracture toughness, and storage modulus of 3D 5-directional SiC f /SiC composites were superior to those of 3D 4-directional braided SiC f /SiC composites; the former also showed a smaller internal friction than the latter. Results from Weibull statistical analysis indicated that the scale parameter σ 0 (736.9 MPa) and Weibull modulus m (21.7) of the 3D 5-directional specimen were higher than those of 3D 4-directional braided SiC f /SiC composites (629.6 MPa, 14.7). Both 3D braided composites demonstrated good toughness and avoided catastrophic brittle fractures under loading because of the effective crack energy dissipating mechanisms of crack deflection, interface debonding, and fiber pull-out. The internal friction and storage modulus of the 3D braided composites were sensitive to temperature. The cross angle of fiber placement in the preform and the direction of the applied force, as well as the pre-crack propagation remarkably influenced the static mechanical properties and failure behavior of the 3D braided SiC f /SiC composites. The dynamic mechanical properties of the 3D braided composites, including internal friction and storage modulus, were also considerably affected by fiber directionality in their preforms.

  9. Computer Aided Multi-scale Design of SiC-Si3N4 Nanoceramic Composites for High-Temperature Structural Applications

    Energy Technology Data Exchange (ETDEWEB)

    Vikas Tomer; John Renaud

    2010-08-31

    It is estimated that by using better and improved high temperature structural materials, the power generation efficiency of the power plants can be increased by 15% resulting in significant cost savings. One such promising material system for future high-temperature structural applications in power plants is Silicon Carbide-Silicon Nitride (SiC-Si{sub 3}N{sub 4}) nanoceramic matrix composites. The described research work focuses on multiscale simulation-based design of these SiC-Si{sub 3}N{sub 4} nanoceramic matrix composites. There were two primary objectives of the research: (1) Development of a multiscale simulation tool and corresponding multiscale analyses of the high-temperature creep and fracture resistance properties of the SiC-Si{sub 3}N{sub 4} nanocomposites at nano-, meso- and continuum length- and timescales; and (2) Development of a simulation-based robust design optimization methodology for application to the multiscale simulations to predict the range of the most suitable phase morphologies for the desired high-temperature properties of the SiC-Si{sub 3}N{sub 4} nanocomposites. The multiscale simulation tool is based on a combination of molecular dynamics (MD), cohesive finite element method (CFEM), and continuum level modeling for characterizing time-dependent material deformation behavior. The material simulation tool is incorporated in a variable fidelity model management based design optimization framework. Material modeling includes development of an experimental verification framework. Using material models based on multiscaling, it was found using molecular simulations that clustering of the SiC particles near Si{sub 3}N{sub 4} grain boundaries leads to significant nanocomposite strengthening and significant rise in fracture resistance. It was found that a control of grain boundary thicknesses by dispersing non-stoichiometric carbide or nitride phases can lead to reduction in strength however significant rise in fracture strength. The

  10. PENGUJIAN AKTIVITAS KOMPOSIT Fe2O3-SiO2 SEBAGAI FOTOKATALIS PADA FOTODEGRADASI 4-KLOROFENOL (The Activity Test of Fe2O3-SiO2 Composite As Photocatalyst on 4-Chlorophenol Photodegradation

    Directory of Open Access Journals (Sweden)

    Eko Sri Kunarti

    2009-03-01

    Full Text Available ABSTRAK  Pada penelitian ini telah dilakukan pengujian aktivitas komposit Fe2O3-SiO2 sebagai fotokatalis pada fotodegradasi 4-klorofenol. Penelitian diawali dengan preparasi dan karakterisasi fotokatalis Fe2O3-SiO2. Preparasi dilakukan dengan metode sol-gel pada temperatur kamar menggunakan tetraetil ortosilikat (TEOS dan besi (III nitrat sebagai prekursor diikuti dengan perlakuan termal pada temperature 500 oC. Karakterisasi dilakukan dengan metode spektrometri inframerah, difraksi sinar-X dan spektrometri fluoresensi sinar-X. Uji aktivitas komposit untuk fotodegradasi 4-klorofenol dilakukan dalam reaktor tertutup yang dilengkapi dengan lampu UV. Pada uji ini telah dipelajari pengaruh waktu penyinaran dan pH larutan terhadap efektivitas fotodegradasi 4-klorofenol. Hasil penelitian menunjukkan bahwa komposit Fe2O3-SiO2 dapat dipreparasi dengan metode sol-gel pada temperatur kamar diikuti perlakuan termal. Komposit Fe2O3-SiO2 dapat meningkatkan efektivitas fotodegradasi 4-klorofenol dari 11,86 % menjadi 55,38 %. Efektivitas fotodegradasi 4- klorofenol dipengaruhi waktu penyinaran dan pH larutan yang semakin lama waktu penyinaran efektifitas fotodegradasi semakin tinggi, namun waktu penyinaran yang lebih lama dari 4 jam dapat menurunkan efektivitasnya. pH larutan memberikan pengaruh yang berbeda-beda pada efektivitas fotodegradasi 4-klorofenol.   ABSTRACT The activity test of Fe2O3-SiO2 composite as photocatalyst on 4-chlorophenol photodegradation has been studied. The research was initiated by preparation of Fe2O3-SiO2 photocatalyst and followed by characterization. The preparation was conducted by sol-gel method at room temperature using tetraethylorthosilicate (TEOS and iron (III nitrate as precursors followed by thermal treatment at a temperature of 500oC. The characterizations were performed by X-ray Diffraction (XRD, Infrared and X-ray Fluorescence Spectrophotometry. The photocatalytic activity test of composites for 4 chlorophenol

  11. Comparison between experimental stiffness changes and crack-thickness-dependent predictions on a 1D SiC-SiC composite

    Energy Technology Data Exchange (ETDEWEB)

    Morvan, J.-M. [Bordeaux-1 Univ., 33 - Talence (France). Lab. de Mecanique Physique; Baste, S. [Bordeaux-1 Univ., 33 - Talence (France). Lab. de Mecanique Physique

    1997-08-01

    The use of an ultrasonic device gives access to all the stiffness coefficients of materials. With the analytical expressions of the effective compliances of an anisotropic solid containing a crack system, it is possible to predict the compliances variation along a monotonous loading, the cracks being considered as slit cracks. When the crack opening displacement is taken into account, that leads to a good agreement between experimental and predicted compliances. The non linear behaviour of the 1D SiC-SiC composite is then simply described by the constitutive laws of both the various crack densities and cracks opening displacement functions. Furthermore, the comparison between experimental and predicted stiffnesses changes gives access to the schematic geometry of the cracks systems. (orig.)

  12. A thermochemical approach to enhance hydrophobicity of SiC/SiO{sub 2} powder using γ-methacryloxypropyl trimethoxy silane and octylphenol polyoxyethylene ether (7)

    Energy Technology Data Exchange (ETDEWEB)

    Li, Chunxue; Feng, Dandan; Wang, Xiangke; Li, Zhihong; Zhu, Yumei, E-mail: zhuyumei@tju.edu.cn

    2016-01-01

    Graphical abstract: Through the exploration of modification mechanism, the hydrophilic properties of SiC/SiO{sub 2}-KH570-OP-7 were far superior to SiC/SiO{sub 2}-KH570. - Highlights: • A novel universal method is performed to enhance hydrophobicity of SiC/SiO{sub 2} powder. • Through pyrolysis of KH570 and OP-7, hydrophilic groups is grafted. • The hydrophobicity of SiC/SiO{sub 2}-KH570-OP-7 was far superior to SiC/SiO{sub 2}-KH570. • A possible formation mechanism of hydrophilic surface was proposed. • Surface changes on SiC/SiO{sub 2}-KH570-OP-7 powder were analyzed via SEM, FTIR, XPS. - Abstract: A thermochemical synthetic methodology for silicon carbide/silica (SiC/SiO{sub 2}) powder modified by integrating γ-methacryloxypropyl trimethoxy silane (KH570) and octylphenol polyoxyethylene ether (7) (OP-7) with hydrophilic SiC/SiO{sub 2} particles is described. On account of weak hydrophobicity of SiC/SiO{sub 2} powder modified by KH570 (SiC/SiO{sub 2}-KH570), the study focuses on the improvement of hydrophobicity utilizing alkylation reaction between OP-7 and KH570 at high temperature. Compared with using KH570 alone, SiC/SiO{sub 2} powder modified by KH570 and OP-7 (SiC/SiO{sub 2}-KH570-OP-7) shows better water resistance, and also an increased contact angle from 73.8° to 136.4°, resulting thus an improved hydrophobicity. Fourier transform infrared spectroscopy (FTIR), as well as X-ray photoelectron spectroscopy (XPS), was utilized to characterize these surfaces, and the results indicated that KH570 and OP-7 can be covalently bonded on the surface of SiC/SiO{sub 2} powder. Furthermore, it has been deeply investigated in the paper not only the possible modes of non-oxidative thermal degradation of OP-7 and KH570, but also the formation mechanism of more hydrophobic SiC/SiO{sub 2}-KH570-OP-7 powder, which probably will have a potential utility for other inorganic materials.

  13. Preparation of amorphous-crystalline SiO{sub 2} composite by hot isostatic pressing (HIP). 2; HIP ho ni yoru SiO{sub 2} kei hishoshitsu-kesshoshitsu fukugo zairyo no sakusei. 2

    Energy Technology Data Exchange (ETDEWEB)

    Ito, S.; Nishii, J.; Fujii, T.; Akashi, K. [Science University of Tokyo, Tokyo (Japan). Faculty of Science and Tecnology

    2000-08-15

    The composites consisting of {alpha}-quartz crystallites and amorphous SiO{sub 2} were prepared by HIP technique, imitating the structure of natural agate. In the previous study, the K{sub IC} of the composite prepared from the mixed powder of crystallites and amorphous SiO{sub 2} was comparable to that of the natural agate (0.56MN/m{sup 1.5}). In this study, to increase the toughness of the composite, (1) the mixture of silica sol and {alpha}-quartz powder and (2) silica sol including nucleation promoter were examined as starting materials respectively. These starting materials were pressed into powder compacts with {phi} 10 multiplied 50mm in size. The Pyrex glass capsule containing the compact was hipped at 800-1,200 degrees C for 0-120 minutes under the pressure of 200 MPa. The K{sub IC} of the composite obtained from the mixture of silica sol and {alpha}-quartz powder was equivalent to that obtained in the previous study, while the maximum K{sub IC} (0.63 MN/m{sup 1.5}) was obtained when PbCl{sub 2} was used as a nucleation promoter. The nucleation promoter having low solubility in water was useful for the homogeneous generation of the crystallites. (author)

  14. Glass-ceramic materials of system MgO-Al{sub 2}O{sub 3}-SiO{sub 2} from rice husk ash; Materiales vitroceramicos del sistema MgO-Al2O3-SiO2 a partir de ceniza de cascara de arroz

    Energy Technology Data Exchange (ETDEWEB)

    Martin, M. I.; Rincon, J. M.; Andreola, F.; Barbieri, L.; Bondioli, F.; Lancellotti, I.; Romero, M.

    2011-07-01

    This wok shows the results of a valorisation study to use rice husk ash as raw material to develop glass-ceramic materials. An original glass has been formulated in the base system MgO-Al{sub 2}O{sub 3}-SiO{sub 2} with addition of B{sub 2}O{sub 3} and Na{sub 2}O to facilitate the melting and poring processes. Glass characterization was carried out by determining its chemical composition. Sintering behaviour has been examined by Hot Stage Microscopy (HSM). Thermal stability and crystallization mechanism have been studied by Differential Thermal Analysis (DTA). Mineralogy analyses of the glass-ceramic materials were carried out using X-ray Diffraction (XRD). Results show that it is possible to use ash rice husk to produce glass-ceramic materials by a sinter crystallization process, with nepheline (Na{sub 2}O-Al{sub 2}O{sub 3}-SiO{sub 2}) as major crystalline phase in the temperature interval 700-950 degree centigrade and forsterite (2MgO-SiO{sub 2}) at temperatures above 950 degree centigrade. (Author) 15 refs.

  15. SiC/C components for nuclear applications from low cost precursor

    International Nuclear Information System (INIS)

    Narciso, J.; Calderon, N.R.

    2009-01-01

    The development of structural materials with the desired properties to produce the components facing the plasma in fusion reactors is one of the key problems in fusion technology. The structural materials used in the first wall and breeder blanket limits the operating temperature of the system, and higher operating temperatures means higher efficiency. Among the advanced material under consideration for those parts (first wall and breeder blanket) SiC based composites offers the greatest potential. However, considerable research is still required in order to solve engineering feasibility and manufacturing issues, as the improvement of the maximum working temperature and the capability of fabrication of components with homogeneous properties at reasonable cost. Last decade, there has been a strong effort in blanket design using SiC f /SiC composites which are rather expensive while excellent mechanical properties are not so mandatory as resistance to neutron irradiation for this application. In this work, an experimental procedure for manufacturing SiC/C composite materials with homogeneous properties from low cost precursors is described. The process consists in classical reactive infiltration of porous carbon preforms by liquid silicon to produce RBSC where the porous carbon preforms are tailor-made for the fabrication of SiC components without residual Si. The proper selection of the feedstock nature and the pyrolysis conditions determine the microstructure and sinterability of the carbon particles, respectively. These two features control the reactivity of the carbon substrate and porosity of the carbon preform for complete infiltration. The absence of silicon and the homogeneous microstructure of the SiC materials produced by this procedure make them suitable for structural applications at temperatures higher than 1200 deg. C. Furthermore, the technique allows near-net-shape capability and the carbon source is a low cost material. (author)

  16. Irradiation project of SiC/SiC fuel pin 'INSPIRE': Status and future plan

    International Nuclear Information System (INIS)

    Kohyama, Akira; Kishimoto, Hirotatsu

    2015-01-01

    After the March 11 Disaster in East-Japan, Research and Development towards Ensuring Nuclear Safety Enhancement for LWR becomes a top priority R and D in nuclear energy policy of Japan. The role of high temperature non-metallic materials, such as SiC/SiC, is becoming important for the advanced nuclear reactor systems. SiC fibre reinforced SiC composite has been recognised to be the most attractive option for the future, now, METI fund based project, INSPIRE, has been launched as 5-year termed project at OASIS in Muroran Institute of Technology aiming at early realisation of this system. INSPIRE is the irradiation project of SiC/SiC fuel pins aiming to accumulate material, thermal, irradiation effect data of NITE-SiC/SiC in BWR environment. Nuclear fuel inserted SiC/SiC fuel pins are planned to be installed in the Halden reactor. The project includes preparing the NITE-SiC/SiC tubes, joining of end caps, preparation of rigs to control the irradiation environment to BWR condition and the instruments to measure the condition of rigs and pins in operation. Also, basic neutron irradiation data will be accumulated by SiC/SiC coupon samples currently under irradiation in BR2. The output from this project may present the potentiality of NITE-SiC/SiC fuel cladding with the first stage fuel-cladding interaction. (authors)

  17. Sensing performance of plasma-enhanced chemical vapor deposition SiC-SiO2-SiC horizontal slot waveguides

    NARCIS (Netherlands)

    Pandraud, G.; Margallo-Balbas, E.; Sarro, P.M.

    2012-01-01

    We have studied, for the first time, the sensing capabilities of plasma-enhanced chemical vapor deposition (PECVD) SiC-SiO2-SiC horizontal slot waveguides. Optical propagation losses were measured to be 23.9 dB?cm for the quasi-transverse magnetic mode. To assess the potential of this device as a

  18. Durability Evaluation of a Thin Film Sensor System With Enhanced Lead Wire Attachments on SiC/SiC Ceramic Matrix Composites

    Science.gov (United States)

    Lei, Jih-Fen; Kiser, J. Douglas; Singh, Mrityunjay; Cuy, Mike; Blaha, Charles A.; Androjna, Drago

    2000-01-01

    An advanced thin film sensor system instrumented on silicon carbide (SiC) fiber reinforced SiC matrix ceramic matrix composites (SiC/SiC CMCs), was evaluated in a Mach 0.3 burner rig in order to determine its durability to monitor material/component surface temperature in harsh environments. The sensor system included thermocouples in a thin film form (5 microns thick), fine lead wires (75 microns diameter), and the bonds between these wires and the thin films. Other critical components of the overall system were the heavy, swaged lead wire cable (500 microns diameter) that contained the fine lead wires and was connected to the temperature readout, and ceramic attachments which were bonded onto the CMCs for the purpose of securing the lead wire cables, The newly developed ceramic attachment features a combination of hoops made of monolithic SiC or SiC/SiC CMC (which are joined to the test article) and high temperature ceramic cement. Two instrumented CMC panels were tested in a burner rig for a total of 40 cycles to 1150 C (2100 F). A cycle consisted of rapid heating to 1150 C (2100 F), a 5 minute hold at 1150 C (2100 F), and then cooling down to room temperature in 2 minutes. The thin film sensor systems provided repeatable temperature measurements for a maximum of 25 thermal cycles. Two of the monolithic SiC hoops debonded during the sensor fabrication process and two of the SiC/SiC CMC hoops failed during testing. The hoops filled with ceramic cement, however, showed no sign of detachment after 40 thermal cycle test. The primary failure mechanism of this sensor system was the loss of the fine lead wire-to-thin film connection, which either due to detachment of the fine lead wires from the thin film thermocouples or breakage of the fine wire.

  19. SAW propagation characteristics of TeO3/3C-SiC/LiNbO3 layered structure

    Science.gov (United States)

    Soni, Namrata D.

    2018-04-01

    Surface acoustic wave (SAW) devices based on Lithium Niobate (LiNbO3) single crystal are advantageous because of its high SAW phase velocity, electromechanical coupling coefficient and cost effectiveness. In the present work a new multi-layered TeO3/3C-SiC/128° Y-X LiNbO3 SAW device has been proposed. SAW propagation properties such as phase velocity, coupling coefficient and temperature coefficient of delay (TCD) of the TeO3/SiC/128° Y-X LiNbO3 multi layered structure is examined using theoretical calculations. It is found that the integration of 0.09λ thick 3C-SiC over layer on 128° Y-X LiNbO3 increases its electromechanical coupling coefficient from 5.3% to 9.77% and SAW velocity from 3800 ms‑1 to 4394 ms‑1. The SiC/128° Y-X LiNbO3 bilayer SAW structure exhibits a high positive TCD value. A temperature stable layered SAW device could be obtained with introduction of 0.007λ TeO3 over layer on SiC/128° Y-X LiNbO3 bilayer structure without sacrificing the efficiency of the device. The proposed TeO3/3C-SiC/128° Y-X LiNbO3 multi-layered SAW structure is found to be cost effective, efficient, temperature stable and suitable for high frequency application in harsh environment.

  20. Synthesis, microstructure and magnetic properties of Fe{sub 3}Si{sub 0.7}Al{sub 0.3}@SiO{sub 2} core–shell particles and Fe{sub 3}Si/Al{sub 2}O{sub 3} soft magnetic composite core

    Energy Technology Data Exchange (ETDEWEB)

    Wang, Jian, E-mail: snove418562@163.com [The State Key Laboratory of Refractories and Metallurgy, Wuhan University of Science and Technology, Wuhan, Hubei 430081 (China); Key Laboratory for Ferrous Metallurgy and Resources Utilization of Ministry of Education, Wuhan University of Science and Technology, Wuhan, Hubei 430081 (China); Fan, Xi’an, E-mail: groupfxa@163.com [The State Key Laboratory of Refractories and Metallurgy, Wuhan University of Science and Technology, Wuhan, Hubei 430081 (China); Key Laboratory for Ferrous Metallurgy and Resources Utilization of Ministry of Education, Wuhan University of Science and Technology, Wuhan, Hubei 430081 (China); Wu, Zhaoyang, E-mail: wustwuzhaoyang@163.com [The State Key Laboratory of Refractories and Metallurgy, Wuhan University of Science and Technology, Wuhan, Hubei 430081 (China); Key Laboratory for Ferrous Metallurgy and Resources Utilization of Ministry of Education, Wuhan University of Science and Technology, Wuhan, Hubei 430081 (China); Li, Guangqiang [The State Key Laboratory of Refractories and Metallurgy, Wuhan University of Science and Technology, Wuhan, Hubei 430081 (China); Key Laboratory for Ferrous Metallurgy and Resources Utilization of Ministry of Education, Wuhan University of Science and Technology, Wuhan, Hubei 430081 (China)

    2015-11-15

    Fe{sub 3}Si{sub 0.7}Al{sub 0.3}@SiO{sub 2} core–shell particles and Fe{sub 3}Si/Al{sub 2}O{sub 3} soft magnetic composite core have been synthesized via a modified stöber method combined with following high temperature sintering process. Most of conductive Fe{sub 3}Si{sub 0.7}Al{sub 0.3} particles could be uniformly coated by insulating SiO{sub 2} using the modified stöber method. The Fe{sub 3}Si{sub 0.7}Al{sub 0.3}@SiO{sub 2} core–shell particles exhibited good soft magnetic properties with low coercivity and high saturation magnetization. The reaction 4Al+3SiO{sub 2}=2α-Al{sub 2}O{sub 3}+3Si took place during the sintering process. As a result the new Fe{sub 3}Si/Al{sub 2}O{sub 3} composite was formed. The Fe{sub 3}Si/Al{sub 2}O{sub 3} composite core displayed more excellent soft magnetic properties, better frequency stability at high frequencies, much higher electrical resistivity and lower core loss than the pure Fe{sub 3}Si{sub 0.7}Al{sub 0.3} core. The method of introducing insulating layers surrounding magnetic particles provides a promising route to develop new and high compact soft magnetic materials with good magnetic and electric properties. - Graphical abstract: In Fe{sub 3}Si/Al{sub 2}O{sub 3} composite, Fe{sub 3}Si phases are separated by Al{sub 2}O{sub 3} layers and the eddy currents are confined in Fe{sub 3}Si phases, thus increasing resistivity and reducing core loss. - Highlights: • Fe{sub 3}Si{sub 0.7}Al{sub 0.3}@SiO{sub 2} core–shell particles and Fe{sub 3}Si/Al{sub 2}O{sub 3} cores were prepared. • Fe{sub 3}Si{sub 0.7}Al{sub 0.3} particles could be uniformly coated by nano-sized SiO{sub 2} clusters. • Fe{sub 3}Si{sub 0.7}Al{sub 0.3}@SiO{sub 2} particles and Fe{sub 3}Si/Al{sub 2}O{sub 3} cores showed good soft magnetic properties. • Fe{sub 3}Si/Al{sub 2}O{sub 3} had lower core loss and better frequency stability than Fe{sub 3}Si{sub 0.7}Al{sub 0.3} cores.

  1. Effect of Pre-Oxidation Treatment of Nano-SiC Particulates on Microstructure and Mechanical Properties of SiC/Mg-8Al-1Sn Composites Fabricated by Powder Metallurgy Combined with Hot Extrusion.

    Science.gov (United States)

    Li, Chuan-Peng; Wang, Zhi-Guo; Zha, Min; Wang, Cheng; Yu, Hong-Chen; Wang, Hui-Yuan; Jiang, Qi-Chuan

    2016-11-26

    Nano-SiC particulates (n-SiC p ) reinforced Mg-8Al-1Sn (AT81) composites with different pre-oxidation parameters were fabricated by powder metallurgy (P/M) process combined with hot extrusion. The effects of pre-oxidization treatment of n-SiC p on the microstructure and tensile properties of 0.5 vol % n-SiC p /AT81 composites were investigated accordingly. The distribution of n-SiC p with different pre-oxidation parameters was homogeneous in the composites. Moreover, it was found that a thin MgAl₂O₄ layer formed at the interface when the n-SiC p were pre-oxidized at 1073 K for 2 h, while the MgAl₂O₄ layer became much thicker with pre-oxidization temperature increasing to 1273 K for 2 h. After an appropriate pre-oxidization treatment of n-SiC p at 1073 K for 2 h, the as-extruded 0.5 vol % n-SiC p /AT81 composites exhibited an enhanced strength. It was found that the yield strength (YS) and ultimate tensile strength (UTS) increased from 168 MPa and 311 MPa to 255 MPa and 393 MPa compared with the as-extruded AT81 alloy, reflecting 51.8% and 26.4% increments, respectively. The improvement of mechanical properties should be mainly attributed to the grain refinement and homogeneous distribution of n-SiC p in the composites. Moreover, a well-bonded interface and the formation of an appropriate amount of interfacial product (MgAl₂O₄) benefited the material's mechanical properties.

  2. Effects of neutron irradiation on thermal conductivity of SiC-based composites and monolithic ceramics

    International Nuclear Information System (INIS)

    Senor, D.J.; Youngblood, G.E.; Moore, C.E.; Trimble, D.J.; Woods, J.J.

    1996-06-01

    A variety of SiC-based composites and monolithic ceramics were characterized by measuring their thermal diffusivity in the unirradiated, thermal annealed, and irradiated conditions over the temperature range 400 to 1,000 C. The irradiation was conducted in the EBR-II to doses of 33 and 43 dpa-SiC (185 EFPD) at a nominal temperature of 1,000 C. The annealed specimens were held at 1,010 C for 165 days to approximately duplicate the thermal exposure of the irradiated specimens. Thermal diffusivity was measured using the laser flash method, and was converted to thermal conductivity using density data and calculated specific heat values. Exposure to the 165 day anneal did not appreciably degrade the conductivity of the monolithic or particulate-reinforced composites, but the conductivity of the fiber-reinforced composites was slightly degraded. The crystalline SiC-based materials tested in this study exhibited thermal conductivity degradation of irradiation, presumably caused by the presence of irradiation-induced defects. Irradiation-induced conductivity degradation was greater at lower temperatures, and was typically more pronounced for materials with higher unirradiated conductivity. Annealing the irradiated specimens for one hour at 150 C above the irradiation temperature produced an increase in thermal conductivity, which is likely the result of interstitial-vacancy pair recombination. Multiple post-irradiation anneals on CVD β-SiC indicated that a portion of the irradiation-induced damage was permanent. A possible explanation for this phenomenon was the formation of stable dislocation loops at the high irradiation temperature and/or high dose that prevented subsequent interstitial/vacancy recombination

  3. Effects of neutron irradiation on thermal conductivity of SiC-based composites and monolithic ceramics

    International Nuclear Information System (INIS)

    Senor, D.J.; Youngblood, G.E.; Moore, C.E.; Trimble, D.J.; Woods, J.J.

    1997-05-01

    A variety of SiC-based composites and monolithic ceramics were characterized by measuring their thermal diffusivity in the unirradiated, thermal annealed, and irradiated conditions over the temperature range 400 to 1,000 C. The irradiation was conducted in the EBR-II to doses of 33 and 43 dpa-SiC (185 EFPD) at a nominal temperature of 1,000 C. The annealed specimens were held at 1,010 C for 165 days to approximately duplicate the thermal exposure of the irradiated specimens. Thermal diffusivity was measured using the laser flash method, and was converted to thermal conductivity using density data and calculated specific heat values. Exposure to the 165 day anneal did not appreciably degrade the conductivity of the monolithic or particulate-reinforced composites, but the conductivity of the fiber-reinforced composites was slightly degraded. The crystalline SiC-based materials tested in this study exhibited thermal conductivity degradation after irradiation, presumably caused by the presence of irradiation-induced defects. Irradiation-induced conductivity degradation was greater at lower temperatures, and was typically more pronounced for materials with higher unirradiated conductivity. Annealing the irradiated specimens for one hour at 150 C above the irradiation temperature produced an increase in thermal conductivity, which is likely the result of interstitial-vacancy pair recombination. Multiple post-irradiation anneals on CVD β-SiC indicated that a portion of the irradiation-induced damage was permanent. A possible explanation for this phenomenon was the formation of stable dislocation loops at the high irradiation temperature and/or high dose that prevented subsequent interstitial/vacancy recombination

  4. The solubility limit of SiO2 in α-alumina at 1600 °C

    International Nuclear Information System (INIS)

    Moshe, Ruth; Berner, Alex; Kaplan, Wayne D.

    2014-01-01

    The solubility limit of Si in α-alumina was measured using wavelength-dispersive spectroscopy on a scanning electron microscope. Samples were doped with Si such that the equilibrated material would contain two phases: mullite (3Al 2 O 3 ·2SiO 2 ) and alumina saturated with Si. Thus the amount of Si measured in the alumina grains represents the solubility limit. Measurements were conducted on water-quenched and furnace-cooled samples. For the quenched samples the Si solubility limit in Al 2 O 3 was found to be 188 ± 7 ppm at 1600 °C

  5. Young’s modulus evaluation and thermal shock behavior of a porous SiC/cordierite composite material

    Directory of Open Access Journals (Sweden)

    Pošarac-Marković M.

    2015-01-01

    Full Text Available Porous SiC/Cordierite Composite Material with graphite content (10% was synthesized. Evaluation of Young modulus of elasticity and thermal shock behavior of these samples was presented. Thermal shock behavior was monitored using water quench test, and non destructive methods such are UPVT and image analysis were also used for accompaniment the level of destruction of the samples during water quench test. Based on the level of destruction graphical modeling of critical number of cycles was given. This approach was implemented on discussion of the influence of the graphite content on thermal stability behavior of the samples. [Projekat Ministarstva nauke Republike Srbije, br. III 45012

  6. Exploration of porous SiC nanostructures as thermal insulator with high thermal stability and low thermal conductivity

    Institute of Scientific and Technical Information of China (English)

    Peng; WAN; Jingyang; WANG

    2016-01-01

    The crucial challenge for current nanoscale thermal insulation materials,such as Al2O3 and SiO2 aerogel composites,is to solve the trade-off between extremely low thermal conductivity and unsatisfied thermal stability.Typical high-temperature ceramic SiC possesses excellent mechanical properties and

  7. Synthesis of TiO2-doped SiO2 composite films and its applications

    Indian Academy of Sciences (India)

    Wintec

    structure of the titanium oxide species in the TiO2-doped SiO2 composite films and the photocatalytic reactiv- ity in order to ... gaku D-max γA diffractometer with graphite mono- chromized ... FT–IR absorption spectra of TiO2-doped SiO2 com-.

  8. Si-Carbon Composite Nanofibers with Good scalability and Favorable Architecture for Highly Reversible Lithium Storage and Superb Kinetics

    International Nuclear Information System (INIS)

    Lee, Youngmin; Heo, Yoon-Uk; Song, Dahye; Shin, Dong Wook; Kang, Yong-Mook

    2014-01-01

    We demonstrate a simple electrospinning for preparing Si-carbon composite Nanofiber (NF) in which aciniform aggregates of Si particles are well encased by amorphous carbon. The Si-carbon composite NF exhibit a significantly improved electrochemical performance with a high specific capacity of 1250 mAh·g −1 and a superior cycling performance during 50 cycles at a rate of 0.2 C. More importantly, Si-carbon composite NF maintain about 70% of initial capacity at 0.2 C and an excellent cycling stability even at 25 times higher current density compared to the initial condition, proving that it has superb kinetics compared to ever reported Si or SiO x materials. The electrochemical superiority of Si-carbon composite NF can be attributed to amorphous carbon framework accommodating the inherent volume expansion of Si during lithiation as well as the enlarged contact area between active materials and conducting agent attributed to the morphological characteristics of its one dimensional (1D) nanostructure

  9. TEM study of a hot-pressed Al2O3-NbC composite material

    Directory of Open Access Journals (Sweden)

    Wilson Acchar

    2005-03-01

    Full Text Available Alumina-based composites have been developed in order to improve the mechanical properties of the monolithic matrix and to replace the WC-Co material for cutting tool applications. Al2O3 reinforced with refractory carbides improves hardness, fracture toughness and wear resistance to values suitable for metalworking applications. Al2O3-NbC composites were uniaxially hot-pressed at 1650 °C in an inert atmosphere and their mechanical properties and microstructures were analyzed. Sintered density, average grain size, microhardness and fracture toughness measurements and microstructural features were evaluated. Results have shown that the mechanical properties of alumina-NbC are comparable to other carbide systems. Microstructural analysis has shown that the niobium carbide particles are mainly located at the grain boundaries of alumina grains, which is an evidence of the "pinning effect", produced by NbC particles.

  10. Probabilistic Modeling of High-Temperature Material Properties of a 5-Harness 0/90 Sylramic Fiber/ CVI-SiC/ MI-SiC Woven Composite

    Science.gov (United States)

    Nagpal, Vinod K.; Tong, Michael; Murthy, P. L. N.; Mital, Subodh

    1998-01-01

    An integrated probabilistic approach has been developed to assess composites for high temperature applications. This approach was used to determine thermal and mechanical properties and their probabilistic distributions of a 5-harness 0/90 Sylramic fiber/CVI-SiC/Mi-SiC woven Ceramic Matrix Composite (CMC) at high temperatures. The purpose of developing this approach was to generate quantitative probabilistic information on this CMC to help complete the evaluation for its potential application for HSCT combustor liner. This approach quantified the influences of uncertainties inherent in constituent properties called primitive variables on selected key response variables of the CMC at 2200 F. The quantitative information is presented in the form of Cumulative Density Functions (CDFs). Probability Density Functions (PDFS) and primitive variable sensitivities on response. Results indicate that the scatters in response variables were reduced by 30-50% when the uncertainties in the primitive variables, which showed the most influence, were reduced by 50%.

  11. Visible Light Excited Catalysis and Reusability Performances of TiO2@Pr:Y2SiO5 Upconversion Materials

    Directory of Open Access Journals (Sweden)

    Yan Jiao

    2017-01-01

    Full Text Available To get high efficiency photodegradation on pollutants under visible light, Pr(III doped Y2SiO5 upconversion materials and anatase TiO2 nanofilm coated Pr:Y2SiO5 composite have been prepared by using a sol-gel method. XRD and SEM test results indicated that TiO2 nanofilm was well coated on Pr:Y2SiO5 to form TiO2@Pr:Y2SiO5 composite particles with the sizes of 0.5–1.0 μm. To avoid secondary pollution resulting from incomplete recovery of catalyst particles, TiO2@Pr:Y2SiO5 was loaded on the glass fiber filters by using a dip-coating method. It is found that the catalyst particles were embedded into the carrier firmly, even after having been reused for 6 times. The luminescence intensities of TiO2@Pr:Y2SiO5 were getting down sharply with the coating contents of TiO2 increased, which was attributed to the adsorption of the luminescence by the TiO2 film in situ. As a result, TiO2@Pr:Y2SiO5 with 4% TiO2, which presented lowest luminescence intensity, showed the highest efficiency on the photodegradation of nitrobenzene wastewater. The catalysts loaded on glass fiber filters showed excellent reusability on the photodegradation of nitrobenzene and presented a photodegradation rate of 95% at the first time and up to 75.9% even after 6 times of reusing by the treatment time of 12 h.

  12. Crystallization behavior of Li2O-SiO2, Na2O-SiO2 and Na2O-CaO-SiO2 glasses; Li2O-SiO2, Na2O-SiO2, Na2O-CaO-SiO2 kei glass no kessho sekishutsu kyodo

    Energy Technology Data Exchange (ETDEWEB)

    Tsutsumi, K.; Otake, J.; Nagasaka, T.; Hino, M. [Tohoku University, Sendai (Japan)

    1998-06-01

    It has been known that crystallization of mold powder is effective on the disturbance of heat transfer between mold and solidified shell in production of middle carbon steel slabs in continuous casting process. But it has not yet been made clear which composition of mold powder is the most suitable for crystallization. The crystallization behavior of Li2O-SiO2, Na2O-SiO2 and Na2O-CaO-SiO2 glasses was observed by differential thermal analysis (DTA) and hot-thermocouple methods with DTA in the present work. As a result, addition of alkaline metal and alkaline earth metal oxides to SiO2 increased the critical cooling rate for glass formation in binary system of Li2O-SiO2 and Na2O-SiO2 and Li2O-SiO2 system crystallized easier than Na2O-SiO2 system. In ternary system of Na2O-CaO-SiO2, addition of Na2O hurried the critical cooling rate at CaO/SiO2=0.93 mass ratio, but the rate was almost constant in the composition range of more than 15 mass% Na2O. The slag of CaO/SiO2=0.93 made the rate faster than the slag of CaO/SiO2=0.47 at constant content of 10mass% Na2O. 17 refs., 10 figs., 3 tabs.

  13. Manufacturing and investigation of surface morphology and optical properties of composite thin films reinforced by TiO2, Bi2O3 and SiO2 nanoparticles

    Science.gov (United States)

    Jarka, Paweł; Tański, Tomasz; Matysiak, Wiktor; Krzemiński, Łukasz; Hajduk, Barbara; Bilewicz, Marcin

    2017-12-01

    The aim of submitted paper is to present influence of manufacturing parameters on optical properties and surface morphology of composite materials with a polymer matrix reinforced by TiO2 and SiO2 and Bi2O3 nanoparticles. The novelty proposed by the authors is the use of TiO2 and SiO2 and Bi2O3 nanoparticles simultaneously in polymeric matrix. This allows using the combined effect of nanoparticles to a result composite material. The thin films of composite material were prepared by using spin-coating method with various spinning rates from solutions of different concentration of nanoparticles. In order to prepare the spinning solution polymer, Poly(methyl methacrylate) (PMMA) was used as a matrix. The reinforcing phase was the mixture of the nanoparticles of SiO2, TiO2 and B2O3. In order to identify the surface morphology of using thin films and arrangement of the reinforcing phase Atomic Force Microscope (AFM) and Scanning Electron Microscope (SEM) were used. In order to study the optical properties of the obtained thin films, the thin films of composites was subjected to an ellipsometry analysis. The measurements of absorbance of the obtained materials, from which the value of the band gap width was specified, were carried out using the UV/VIS spectroscopy. The optical properties of obtain composite thin films depend not only on the individual components used, but also on the morphology and the interfacial characteristics. Controlling the participation of three kinds of nanoparticles of different sizes and optical parameters allows to obtaining the most optimal optical properties of nanocomposites and also controlling the deposition parameters allows to obtaining the most optimal surface morphology of nanocomposites.

  14. BURNER RIG TESTING OF A500 C/SiC

    Science.gov (United States)

    2018-03-17

    AFRL-RX-WP-TR-2018-0071 BURNER RIG TESTING OF A500® C /SiC Larry P. Zawada Universal Technology Corporation Jennifer Pierce UDRI...TITLE AND SUBTITLE BURNER RIG TESTING OF A500® C /SiC 5a. CONTRACT NUMBER In-House 5b. GRANT NUMBER 5c. PROGRAM ELEMENT NUMBER 62102F 6...test program characterized the durability behavior of A500® C /SiC ceramic matrix composite material at room and elevated temperature. Specimens were

  15. Synthesis of Y2O3-ZrO2-SiO2 composite coatings on carbon fiber reinforced resin matrix composite by an electro-plasma process

    Science.gov (United States)

    Zhang, Yuping; Lin, Xiang; Chen, Weiwei; Cheng, Huanwu; Wang, Lu

    2016-05-01

    In the present paper the Y2O3-ZrO2-SiO2 composite coating was successfully synthesized on carbon fiber reinforced resin matrix composite by an electro-plasma process. The deposition process, microstructures and oxidation resistance of the coatings with different SiO2 concentrations were systematically investigated. A relatively dense microstructure was observed for the Y2O3-ZrO2-SiO2 composite coating with the SiO2 concentration above 5 g/L. The coating exhibited very good oxidation resistance at 1273 K with the mass loss rate as low as ∼30 wt.%, compared to 100 wt.% of the substrate. The formation of the ceramic composites was discussed in detail based on the electrochemical mechanism and the deposition dynamics in order to explain the effect of the plasma discharge. We believe that the electro-plasma process will find wide applications in preparing ceramics and coatings in industries.

  16. Effects of Preform Density on Structure and Property of C/C-SiC Composites Fabricated by Gaseous Silicon Infiltration

    Directory of Open Access Journals (Sweden)

    CAO Yu

    2016-07-01

    Full Text Available The 3-D needled C/C preforms with different densities deposited by chemical vapor infiltration (CVI method were used to fabricate C/C-SiC composites by gaseous silicon infiltration (GSI. The porosity and CVI C thickness of the preforms were studied, and the effects of preform density on the mechanical and thermal properties of C/C-SiC composites were analyzed. The results show that with the increase of preform density, the preform porosity decreases and the CVI C thickness increases from several hundred nanometers to several microns. For the C/C-SiC composites, as the preform density increases, the residual C content increases while the density and residual Si content decreases. The SiC content first keeps at a high level of about 40% (volume fraction, which then quickly reduces. Meanwhile, the mechanical properties increase to the highest values when the preform density is 1.085g/cm3, with the flexure strength up to 308.31MP and fracture toughness up to 11.36MPa·m1/2, which then decrease as the preform density further increases. The thermal conductivity and CTE of the composites, however, decrease with the increase of preform density. It is found that when the preform porosity is too high, sufficient infiltration channels lead to more residual Si, and thinner CVI C thickness results in the severe corrosion of the reinforcing fibers by Si and lower mechanical properties. When the preform porosity is relatively low, the contents of Si and SiC quickly reduce since the infiltration channels are rapidly blocked, resulting in the formation of large closed pores and not high mechanical properties.

  17. Dependence of Photocatalytic Activity of TiO2-SiO2 Nanopowders

    Directory of Open Access Journals (Sweden)

    M. Riazian

    2014-10-01

    Full Text Available Structural properties and chemical composition change the photocatalytic activity in TiO2-SiO2 nanopowder composite. The SiO2-TiO2 nanostructure is synthesized based on sol–gel method. The nanoparticles are characterized by x-ray fluorescents (XRF, x- ray diffraction (XRD, tunneling electron microscopy (TEM, field emission scanning electron microscopy (FE-SEM, UV-vis. Spectrophotometer and furrier transmission create infrared absorption (FTIR techniques. The rate constant k for the degradation of methylen blue in its aqueous solution under UV irradiation is determined as a measure of photocatalytic activity. Dependence between photocatalytic activity and SiO2 content in the composite is determined. Rate constant k is found dependent on the content of SiO2 in the composite that calcined at 900 oC. The addition of low composition SiO2 to the TiO2 matrix (lower than 45% enhances the photocatalytic activity due to thermal stability and increasing in the surface area. The effects of chemical compositions on the surface topography and the crystallization of phases are studied.

  18. Polymer-derived-SiCN ceramic/graphite composite as anode material with enhanced rate capability for lithium ion batteries

    Science.gov (United States)

    Graczyk-Zajac, M.; Fasel, C.; Riedel, R.

    2011-08-01

    We report on a new composite material in view of its application as a negative electrode in lithium-ion batteries. A commercial preceramic polysilazane mixed with graphite in 1:1 weight ratio was transformed into a SiCN/graphite composite material through a pyrolytic polymer-to-ceramic conversion at three different temperatures, namely 950 °C, 1100 °C and 1300 °C. By means of Raman spectroscopy we found successive ordering of carbon clusters into nano-crystalline graphitic regions with increasing pyrolysis temperature. The reversible capacity of about 350 mAh g-1 was measured with constant current charging/discharging for the composite prepared at 1300 °C. For comparison pure graphite and pure polysilazane-derived SiCN ceramic were examined as reference materials. During fast charging and discharging the composite material demonstrates enhanced capacity and stability. Charging and discharging in half an hour lead to about 200 and 10 mAh g-1, for the composite annealed at 1300 °C and pure graphite, respectively. A clear dependence between the final material capacity and pyrolysis temperature is found and discussed with respect to possible application in batteries, i.e. practical discharging potential limit. The best results in terms of capacity recovered under 1 V and high rate capability were also obtained for samples synthesized at 1300 °C.

  19. Investigation of local environments in Nafion-SiO(2) composite membranes used in vanadium redox flow batteries.

    Science.gov (United States)

    Vijayakumar, M; Schwenzer, Birgit; Kim, Soowhan; Yang, Zhenguo; Thevuthasan, S; Liu, Jun; Graff, Gordon L; Hu, Jianzhi

    2012-04-01

    Proton conducting polymer composite membranes are of technological interest in many energy devices such as fuel cells and redox flow batteries. In particular, polymer composite membranes, such as SiO(2) incorporated Nafion membranes, are recently reported as highly promising for the use in redox flow batteries. However, there is conflicting reports regarding the performance of this type of Nafion-SiO(2) composite membrane in the redox flow cell. This paper presents results of the analysis of the Nafion-SiO(2) composite membrane used in a vanadium redox flow battery by nuclear magnetic resonance (NMR) spectroscopy, X-ray photoelectron spectroscopy (XPS), Fourier Transform Infra Red (FTIR) spectroscopy, and ultraviolet-visible spectroscopy. The XPS study reveals the chemical identity and environment of vanadium cations accumulated at the surface. On the other hand, the (19)F and (29)Si NMR measurement explores the nature of the interaction between the silica particles, Nafion side chains and diffused vanadium cations. The (29)Si NMR shows that the silica particles interact via hydrogen bonds with the sulfonic groups of Nafion and the diffused vanadium cations. Based on these spectroscopic studies, the chemical environment of the silica particles inside the Nafion membrane and their interaction with diffusing vanadium cations during flow cell operations are discussed. This study discusses the origin of performance degradation of the Nafion-SiO(2) composite membrane materials in vanadium redox flow batteries. Copyright © 2011 Elsevier Inc. All rights reserved.

  20. Joining of thin thickness SiCf/SiC composites: research of a joining composition and of an associated elaboration process

    International Nuclear Information System (INIS)

    Jacques, E.

    2012-01-01

    The present work is part of the Fourth Generation Fast Reactors program. One of the key issues is the joining of the SiC f /SiC ceramic matrix composites (CMC) to seal the combustible cladding. At the present time, no chemical composition as a joint is refractive enough to face the expected operating temperatures. The aims of this study are the following: (1) the identification of a joining composition and its associated elaboration process answering the specifications, (2) the validation of a local and fast heating process and (3) the definition of mechanical tests to characterise these joinings. We describe the methodology and the results for joining SiC and SiC f /SiC substrates at solid and liquid state using metallic silicides. Joint integrity and joint strength can be improved by adding small SiC particles to the silicides powders. Chemical reactivity, wettability tests and thermomechanical properties analysis have been carried out on the joints. Cross sections of the assembly were prepared to study the joint/substrate chemical bonding, the cracking and the crack deflection in the vicinity of the interface. Also, one of the challenge consists in using a local heating at a high temperature (around 1800 C) for a short time to avoid the degradation of the composite structure. The assemblies have been then performed in an inductive furnace but in order to prepare the joining technology, trials of local heating have also been investigated with a CO 2 laser beam and a microwave generator. Finally, descriptions of the 4-points bending mechanical test used and the associated results are presented. (author) [fr

  1. Effect of Reactant Concentration on the Microstructure of SiC Nano wires Grown In Situ within SiC Fiber Preforms

    International Nuclear Information System (INIS)

    Kim, Weon Ju; Kang, Seok Min; Park, Ji Yeon; Ryu, Woo Seog

    2006-01-01

    Silicon carbide fiber-reinforced silicon carbide matrix (SiC f /SiC) composites are considered as advanced materials for control rods and other in-core components of high-temperature gas cooled reactors. Although the carbon fiber-reinforced carbon matrix (C f /C) composites are more mature and have advantages in cost, manufacturability and some thermomechanical properties, the SiC f /SiC composites have a clear advantage in irradiation stability, specifically a lower level of swelling and retention of mechanical properties. This offers a lifetime component for control rod application to HTGRs while the Cf/C composites would require 2-3 replacements over the reactor lifetime. In general, the chemical vapor infiltration (CVI) technique has been used most widely to produce SiC f /SiC composites. Although the technique produces a highly pure SiC matrix, it requires a long processing time and inevitably contains large interbundle pores. The present authors have recently developed 'whisker growing-assisted process,' in which one-dimensional SiC nano structures with high aspect ratios such as whiskers, nano wires and nano rods are introduced into the fiber preform before the matrix infiltration step. This novel method can produce SiC f /SiC composites with a lower porosity and an uniform distribution of pores when compared with the conventional CVI. This would be expected to increase mechanical and thermal properties of the SiC f /SiC composites. In order to take full advantage of the whisker growing strategy, however, a homogeneous growth of long whiskers is required. In this study, we applied the atmospheric pressure CVI process without metallic catalysts for the growth of SiC nano wires within stacked SiC fiber fabrics. We focused on the effect of the concentration of a reactant gas on the growth behavior and microstructures of the SiC nano wires and discussed a controlling condition for the homogenous growth of long SiC nano wires

  2. Synthesis of PANi-SiO2 Nanocomposite with In-Situ Polymerization Method: Nanoparticle Silica (NPS) Amorphous and Crystalline Phase

    Science.gov (United States)

    Munasir; Luvita, N. R. D.; Kusumawati, D. H.; Putri, N. P.; Triwikantoro; Supardi, Z. A. I.

    2018-03-01

    Silica which is synthesized from natural materials such as Bancar Tuban’s sand composited with Polyaniline (PANi), where the silica used are silica has an amorphous phase and cristobalite phase. In this research, the composite method used is in- situ polymerization, which is silica entered during the fabrication of PANi, then automatically silica will be substitute into the chain bonding of PANi. The aim of this research is to find out the results of a composite process using in-situ methods as well as differences in the morphology of PANi/a- SiO2 and PANi/c-SiO2. For the characterization of samples tested in the form of FTIR to determine the functional groups of the composite and SEM to determine the morphology of the sample. From the test results of FTIR are known composite possibility has occurred because there are several functional groups belonging to silica also functional groups belonging polyaniline, functional group that’s happened in wave numbers were almost identical between PANi/a-SiO2 and PANi/c-SiO2, but there are little differences were seen in the form of a graph generated from the peak and intensity that occurred charts for PANi/c-SiO2 has peak more pointed or sharp compared to PANi/a-SiO2 because that bond of crystal is strong, stiff and has a larger particle size than the amorphous composite. Then from the data of SEM seen clearly their morphological differences between PANi/a-SiO2 and PANi/c-SiO2 where polyaniline is composited with amorphous silica will have a fault that is not uniform or irregular different from PANi/c -SiO2 has a regular fault and this is corresponding with the nature of the typical structure of amorphous and crystalline.

  3. Interfacial reaction in SiC_f/Ti-6Al-4V composite by using transmission electron microscopy

    International Nuclear Information System (INIS)

    Huang, Bin; Li, Maohua; Chen, Yanxia; Luo, Xian; Yang, Yanqing

    2015-01-01

    The interfacial reactions of continuous SiC fiber reinforced Ti-6Al-4V matrix composite (SiC_f/Ti-6Al-4V composite) and continuous SiC fiber coated by C reinforced Ti-6Al-4V matrix composite (SiC_f/C/Ti-6Al-4V composite) were investigated by using micro-beam electron diffraction (MBED) and energy disperse spectroscopy (EDS) on transmission electron microscopy (TEM). The sequence of the interfacial reactions in the as-processed and exposed at 900°C for 50h SiC_f/Ti-6Al-4V composites can be described as SiC||TiC||Ti_5Si_3 + TiC||Ti-6Al-4V and SiC||TiC||Ti_5Si_3||TiC||Ti_5Si_3||TiC||Ti_5Si_3||Ti-6Al-4V, respectively. Additionally, both in as-processed and exposed composites, Ti_3SiC_2 and Ti_3Si are absent at the interfaces. For the SiC_f/C/Ti-6Al-4V composite exposed at 900 °C for 50 h, the sequence of the interfacial reaction can be described as SiC||C||TiC_F||TiC_C||Ti-6Al-4V before C coating is completely consumed by interfacial reaction. When interfacial reaction consumes C coating completely, the sequence of the interfacial reaction can be described as SiC||TiC||Ti_5Si_3||TiC||Ti-6Al-4V. Furthermore, in SiC_f/C/Ti-6Al-4V composite, C coating can absolutely prevent Si diffusion from SiC fiber to matrix. Basing on these results, the model of formation process of the interfacial reaction products in the composites was proposed. - Highlights: • We obtained the sequence of the interfacial reactions in the as-processed and exposed at 900 °C for 50 h SiC_f/Ti-6Al-4 V composites as well as in the SiC_f/C/Ti-6Al-4 V composite exposed at 900 °C for 50 h. • We verified that both in as-processed and exposed SiC_f/Ti-6Al-4 V composites, Ti_3SiC_2 and Ti_3Si are absent at the interfaces. • Carbon coating can absolutely prevent silicon diffusion from SiC fiber to matrix. • Basing on these results, the model of formation process of the interfacial reaction products in the composites was proposed.

  4. Sol–gel hybrid membranes loaded with meso/macroporous SiO2, TiO2–P2O5 and SiO2–TiO2–P2O5 materials with high proton conductivity

    International Nuclear Information System (INIS)

    Castro, Yolanda; Mosa, Jadra; Aparicio, Mario; Pérez-Carrillo, Lourdes A.; Vílchez, Susana; Esquena, Jordi; Durán, Alicia

    2015-01-01

    In this work, highly conductive hybrid organic–inorganic membranes loaded with SiO 2 , TiO 2 –P 2 O 5 and SiO 2 –TiO 2 –P 2 O 5 meso/macroporous particles were prepared via a sol–gel process. Meso/macroporous particles were incorporated to hybrid membranes, for improving water retention and enhancing electrochemical performance. These particles with a polymodal pore size distribution were prepared by templating in highly concentrated emulsions, the particles showed a specific surface area between 50 m 2 /g (TiO 2 –P 2 O 5 ) and 300 m 2 /g (SiO 2 –TiO 2 –P 2 O 5 ). The particles were dispersed in a hybrid silica sol and further sprayed onto glass paper. The films were polymerized and sintered; those loaded with meso/macroporous particles had a homogenous distribution. High temperature proton conductivity measurements confirmed a high water retention. Conductivity of these materials is higher than that of Nafion ® at higher temperatures (120 °C) (2·10 −2  S/cm). This study provides processing guideline to achieve hybrid electrolytes for efficient conduction of protons due to their high surface area and porous structure. - Highlights: • Hybrid electrolyte with meso/macroporous particles were synthesized by sol–gel. • Depositions of hybrid solutions by spraying onto glass substrates were performed. • Proton conductivity was evaluated as a function of composition and porous structure

  5. Effects of antimony (Sb) on electron trapping near SiO{sub 2}/4H-SiC interfaces

    Energy Technology Data Exchange (ETDEWEB)

    Mooney, P. M.; Jiang, Zenan; Basile, A. F. [Physics Department, Simon Fraser University, Burnaby, British Columbia V5A 1S6 (Canada); Zheng, Yongju; Dhar, Sarit [Physics Department, Auburn University, Auburn, Alabama 36849 (United States)

    2016-07-21

    To investigate the mechanism by which Sb at the SiO{sub 2}/SiC interface improves the channel mobility of 4H-SiC MOSFETs, 1 MHz capacitance measurements and constant capacitance deep level transient spectroscopy (CCDLTS) measurements were performed on Sb-implanted 4H-SiC MOS capacitors. The measurements reveal a significant concentration of Sb donors near the SiO{sub 2}/SiC interface. Two Sb donor related CCDLTS peaks corresponding to shallow energy levels in SiC were observed close to the SiO{sub 2}/SiC interface. Furthermore, CCDLTS measurements show that the same type of near-interface traps found in conventional dry oxide or NO-annealed capacitors are present in the Sb implanted samples. These are O1 traps, suggested to be carbon dimers substituted for O dimers in SiO{sub 2}, and O2 traps, suggested to be interstitial Si in SiO{sub 2}. However, electron trapping is reduced by a factor of ∼2 in Sb-implanted samples compared with samples with no Sb, primarily at energy levels within 0.2 eV of the SiC conduction band edge. This trap passivation effect is relatively small compared with the Sb-induced counter-doping effect on the MOSFET channel surface, which results in improved channel transport.

  6. Microstructural characterization of hybrid CFRP/SiC composites; Caracterizacao microestrutural de compositos de fibras de carbono com matriz hibrida de Carbono/SiC

    Energy Technology Data Exchange (ETDEWEB)

    Von Dollinger, C.F.A.; Pardini, L.C., E-mail: Christian.dcta@gmail.com [Instituto de Aeronautica e Espaco (DCTA/IAE), Sao Jose dos Campos, SP (Brazil). Departamento de Ciencia e Tecnologia Aeroespacial; Pazini, J.C. [Universidade de Sao Paulo (USP), Lorena, SP (Brazil); Alves, S.C.N. [Universidade Federal de Itajuba (UNIFEI), MG (Brazil)

    2016-07-01

    In present work a hybrid matrix C-C/SiC composites were produced. Carbon fiber fabric was impregnated with phenolic resin mixed with powder Si in proportions of 5%, 10%, 15% e 20%wt. Optical microscopy under reflected light and polarized light were used in order to characterize samples in the as molded condition and after carbonization at 1000°C, and heat treatment 1600°C in order to react carbon and liquid silicon in order to form in situ SiC . The pore volume fraction ranges from 33% to 41% for composites after heat treatment at 1600°C due to volatiles released specially during carbonization process. Complementary analyses were done by Scanning Electron microscopy (SEM) and X-Ray diffraction to confirm in situ conversion of SiC. The results showed that the impregnation of a carbon fabric with phenolic resin added with silicon proved to be an alternative route to produce CFRP/SiC composites. (author)

  7. UV-visible light photocatalytic properties of NaYF4:(Gd, Si)/TiO2 composites

    Science.gov (United States)

    Mavengere, Shielah; Kim, Jung-Sik

    2018-06-01

    In this study, a new novel composite photocatalyst of NaYF4:(Gd, Si)/TiO2 phosphor has been synthesized by two step method of solution combustion and sol-gel. The photocatalyst powders were characterized by X-ray diffraction (XRD), Raman spectroscopy, scanning electron microscopy (SEM), UV-vis spectroscopy and photoluminescence (PL) spectroscopy. Raman spectroscopy confirmed the anatase TiO2 phase which remarkably increased with existence of yttrium silicate compounds between 800 cm-1 and 900 cm-1. Double-addition of Gd3+-Si4+ ions in NaYF4 host introduced sub-energy band levels with intense absorption in the ultraviolet (UV) light region. Photocatalytic activity was examined by exposing methylene blue (MB) solutions mixed with photocatalyst powders to 254 nm UV-C fluorescent lamp and 200 W visible lights. The UV and visible photocatalytic reactivity of the NaYF4:(Gd, 1% Si)/TiO2 phosphor composites showed enhanced MB degradation efficiency. The coating of NaYF4:(Gd, 1% Si) phosphor with TiO2 nanoparticles creates energy band bending at the phosphor/TiO2 interfaces. Thus, these composites exhibited enhanced absorption of UV/visible light and the separation of electron and hole pairs for efficient photocatalysis.

  8. Al-oxynitride interfacial layer investigations for Pr{sub X}O{sub Y} on SiC and Si

    Energy Technology Data Exchange (ETDEWEB)

    Henkel, K; Karavaev, K; Torche, M; Schwiertz, C; Burkov, Y; Schmeisser, D [Brandenburgische Technische Universitaet Cottbus, Angewandte Physik-Sensorik, K-Wachsmann-Allee 17, 03046 Cottbus (Germany)], E-mail: henkel@tu-cottbus.de

    2008-01-15

    We investigate the dielectric properties of Praseodymium based oxides Pr{sub X}O{sub Y} by preparing MIS (metal insulator semiconductor) structures consisting of Pr{sub X}O{sub Y} as a high-k insulating layer and silicon (Si) or silicon carbide (SiC) as semiconductor substrates. The use of a buffer layer between Pr{sub X}O{sub Y} and the semiconductor is necessary as we found deleterious reactions between these materials such as silicate and graphite formation. Possessing a higher permittivity value ({epsilon}{sub r}) than silicon dioxide (SiO{sub 2}) and good lattice matching in conjunction with similar thermal expansion coefficient to SiC, we focus on aluminum oxynitride (AlON) as a suitable buffer layer for this high-k/wide-bandgap system. In our spectroscopic investigations we found a decrease or indeed prevention of silicon diffusion into the oxide and an increased Pr{sub 2}O{sub 3} fraction after deposition. In electrical characterizations of Pr{sub X}O{sub Y}/AlON stacks we found considerable improvements in the leakage current by several orders on both substrates, especially on silicon where we obtain values down to 10{sup -7}A/cm{sup 2} at a CET (capacitance equivalent thickness) of 4nm. We observed interface state densities in the range of 5 x 10{sup 11}-1 x 10{sup 12}/eVcm{sup 2} and 1-5 x 10{sup 12}/eVcm{sup 2} on Si and SiC, respectively.

  9. Effect of heat treatment on microstructure and interface of SiC particle reinforced 2124 Al matrix composite

    Energy Technology Data Exchange (ETDEWEB)

    Mandal, Durbadal, E-mail: durbadal73@yahoo.co.in [MEF Division, CSIR-National Metallurgical Laboratory, Jamshedpur 831007 (India); Viswanathan, Srinath [Dept of Metallurgical and Materials Engineering, University of Alabama, Tuscaloosa, AL (United States)

    2013-11-15

    -48 hrs. • A layer of 50-75 nm is formed at interface after heat treatment. • No Carbide formation and SiC dissolution is observed at this temperature. • MgAl{sub 2}O{sub 4}, CuMgAl{sub 2} phases are segregated at interface of Al-SiC composite. • Mg and Cu are also segregated at near to the grain boundary.

  10. Diffusion barrier and adhesion properties of SiO(x)N(y) and SiO(x) layers between Ag/polypyrrole composites and Si substrates.

    Science.gov (United States)

    Horváth, Barbara; Kawakita, Jin; Chikyow, Toyohiro

    2014-06-25

    This paper describes the interface reactions and diffusion between silver/polypyrrole (Ag/PPy) composite and silicon substrate. This composite material can be used as a novel technique for 3D-LSI (large-scale integration) by the fast infilling of through-silicon vias (TSV). By immersion of the silicon wafer with via holes into the dispersed solution of Ag/PPy composite, the holes are filled with the composite. It is important to develop a layer between the composite and the Si substrate with good diffusion barrier and adhesion characteristics. In this paper, SiOx and two types of SiOxNy barrier layers with various thicknesses were investigated. The interface structure between the Si substrate, the barrier, and the Ag/PPy composite was characterized by transmission electron microscopy. The adhesion and diffusion properties of the layers were established for Ag/PPy composite. Increasing thickness of SiOx proved to permit less Ag to transport into the Si substrate. SiOxNy barrier layers showed very good diffusion barrier characteristics; however, their adhesion depended strongly on their composition. A barrier layer composition with good adhesion and Ag barrier properties has been identified in this paper. These results are useful for filling conductive metal/polymer composites into TSV.

  11. Effect of surface morphology and densification on the infrared emissivity of C/SiC composites

    International Nuclear Information System (INIS)

    Wang, Fuyuan; Cheng, Laifei; Zhang, Qing; Zhang, Litong

    2014-01-01

    Highlights: • The cauliflower-like microstructure improved the infrared emissivity multiply. • The infrared emissivity decreased continually with the improving surface flatness. • The densification process boosted the infrared emissivity. - Abstract: The effects of surface morphology and densification on the infrared emissivity of 2D C/SiC composites were investigated in 6–16 μm from 1000 °C to 1600 °C. As the sample surface was polished, the reflection and scattering for the electromagnetic waves of thermal radiation were reduced, causing a sustained decrease in the infrared emissivity. The space-variant polarizations caused by the cauliflower-like microstructure were enervated in the smooth surface, which enhanced the reduction trendy in the infrared emissivity. In densification process, the increasing SiC content and the growing amount of the cauliflower-like microstructure on sample surface improved the infrared emissivity of C/SiC composites, while the decreasing porosity decreased it. Due to the greater positive effects on the thermal radiation during the densification process, the infrared emissivity of C/SiC composites increased successively with density

  12. Effect of surface morphology and densification on the infrared emissivity of C/SiC composites

    Energy Technology Data Exchange (ETDEWEB)

    Wang, Fuyuan, E-mail: wangfy1986@gmail.com; Cheng, Laifei; Zhang, Qing, E-mail: zhangqing@nwpu.edu.cn; Zhang, Litong

    2014-09-15

    Highlights: • The cauliflower-like microstructure improved the infrared emissivity multiply. • The infrared emissivity decreased continually with the improving surface flatness. • The densification process boosted the infrared emissivity. - Abstract: The effects of surface morphology and densification on the infrared emissivity of 2D C/SiC composites were investigated in 6–16 μm from 1000 °C to 1600 °C. As the sample surface was polished, the reflection and scattering for the electromagnetic waves of thermal radiation were reduced, causing a sustained decrease in the infrared emissivity. The space-variant polarizations caused by the cauliflower-like microstructure were enervated in the smooth surface, which enhanced the reduction trendy in the infrared emissivity. In densification process, the increasing SiC content and the growing amount of the cauliflower-like microstructure on sample surface improved the infrared emissivity of C/SiC composites, while the decreasing porosity decreased it. Due to the greater positive effects on the thermal radiation during the densification process, the infrared emissivity of C/SiC composites increased successively with density.

  13. Effect of Copper Coated SiC Reinforcements on Microstructure, Mechanical Properties and Wear of Aluminium Composites

    Science.gov (United States)

    Kori, P. S.; Vanarotti, Mohan; Angadi, B. M.; Nagathan, V. V.; Auradi, V.; Sakri, M. I.

    2017-08-01

    Experimental investigations are carried out to study the influence of copper coated Silicon carbide (SiC) reinforcements in Aluminum (Al) based Al-SiC composites. Wear behavior and mechanical Properties like, ultimate tensile strength (UTS) and hardness are studied in the present work. Experimental results clearly revealed that, an addition of SiC particles (5, 10 and 15 Wt %) has lead in the improvement of hardness and ultimate tensile strength. Al-SiC composites containing the Copper coated SiC reinforcements showed better improvement in mechanical properties compared to uncoated ones. Characterization of Al-SiC composites are carried out using optical photomicrography and SEM analysis. Wear tests are carried out to study the effects of composition and normal pressure using Pin-On Disc wear testing machine. Results suggested that, wear rate decreases with increasing SiC composition, further an improvement in wear resistance is observed with copper coated SiC reinforcements in the Al-SiC metal matrix composites (MMC’s).

  14. A Robust CuCr2O4/SiO2 Composite Photothermal Material with Underwater Black Property and Extremely High Thermal Stability for Solar-Driven Water Evaporation

    KAUST Repository

    Shi, Yusuf

    2017-12-27

    The design and fabrication of efficient photothermal materials is the key issue in solar-driven water evaporation. In this work, a robust CuCr2O4/SiO2 composite membrane with outstanding solar-driven water evaporation performance (1.32 kg m−2 h−1) under one sun irradiation is rationally designed and synthesized by using quartz glass fibrous membrane as supporting matrix and stable CuCr2O4 particles as the active light absorber. Instead of coating a separate layer on top of the support, the CuCr2O4 particles are evenly distributed inside the matrix, which endows the membrane with great mechanical strength and excellent wear and abrasion resistance. The highly porous composite survives 6 atm pressure and retains its performance even after 75% of the membrane is removed by sandpaper. This work also looks into a generally overlooked aspect of wet versus dry state of photothermal material and its implications. Interestingly, the composite possesses a gray color with a high reflectance in dry state but turns into deep black with a low reflectance in wet state due to the decreased subsurface scattering and strong NIR light absorbance of water in wet state. This composite material also possesses excellent thermal stability and thermal shock resistance, making it able to be easily recovered by calcination in air or direct burning in fire for contaminants removal. The results demonstrate that this composite is a competitive photothermal material for practical solar distillation and indicate that the optical properties of material in wet state are more relevant to photothermal material screening and optimization for solar distillation.

  15. Compositional change of some first wall materials by considering multiple step nuclear reaction

    Energy Technology Data Exchange (ETDEWEB)

    Noda, Tetsuji; Utsumi, Misako; Fujita, Mitsutane [National Research Inst. for Metals, Tsukuba, Ibaraki (Japan)

    1997-03-01

    The conceptual system for nuclear material design is considered and some trials on WWW server with functions of the easily accessible simulation of nuclear reactions are introduced. Moreover, as an example of the simulation on the system using nuclear data, transmutation calculation was made for candidate first wall materials such as 9Cr-2W steel, V-5Cr-5Ti and SiC in SUS316/Li{sub 2}O/H{sub 2}O(SUS), 9Cr-2WLi{sub 2}O/H{sub 2}O(RAF), V alloy/Li/Be(V), and SiC/Li{sub 2}ZrO{sub 3}/He(SiC) blanket/shield systems based on ITER design model. Neutron spectrum varies with different blanket/shield compositions. The flux of low energy neutrons decreases in order of V-SiC-RAF-SUS blanket/shield systems. Fair amounts of W depletion in 9Cr-2W steel and the increase of Cr content in V-5Cr-5Ti were predicted in SUS or RAF systems. Concentration change in W and Cr is estimated to be suppressed if Li coolant is used in place of water. Helium and hydrogen production are not strongly affected by the different blanket/shield compositions. (author)

  16. A promising tritium breeding material: Nanostructured 2Li2TiO3-Li4SiO4 biphasic ceramic pebbles

    Science.gov (United States)

    Dang, Chen; Yang, Mao; Gong, Yichao; Feng, Lan; Wang, Hailiang; Shi, Yanli; Shi, Qiwu; Qi, Jianqi; Lu, Tiecheng

    2018-03-01

    As an advanced tritium breeder material for the fusion reactor blanket of the International Thermonuclear Experimental Reactor (ITER), Li2TiO3-Li4SiO4 biphasic ceramic has attracted widely attention due to its merits. In this paper, the uniform precursor powders were prepared by hydrothermal method, and nanostructured 2Li2TiO3-Li4SiO4 biphasic ceramic pebbles were fabricated by an indirect wet method at the first time. In addition, the composition dependence (x/y) of their microstructure characteristics and mechanical properties were investigated. The results indicated that the crush load of biphasic ceramic pebbles was better than that of single phase ceramic pebbles under identical conditions. The 2Li2TiO3-Li4SiO4 ceramic pebbles have good morphology, small grain size (90 nm), satisfactory crush load (37.8 N) and relative density (81.8 %T.D.), which could be a promising breeding material in the future fusion reactor.

  17. Pitting corrosion behaviour study of aluminium matrix composites (A3xx.x/SiCp)

    International Nuclear Information System (INIS)

    Pardo, A.; Merino, M. C.; Merino, S.; Lopez, M. D.; Viejo, F.; Carboneras, M.; Arrabal, R.

    2004-01-01

    The influence of the SiCp proportion on the pitting corrosion of A3xx.x/SiC/xxp composites was studies by means of potenciodinamic polarization and double cyclic polarization in saline environment at 25 degree centigrade A360/SiC/xxp matrix does not contain copper, whereas the A380/SiC/xxp matric contains 1,39-1,44 wt %Cu. The kinetic study was carried out by gravimetric measurements. The nature of corrosion products was analysed by low angle XRD and Scanning Electron Microscopy (SEM). The corrosion is due to nucleation and growth of Al 2 O 3 -3H 2 O on the material surface. The corrosion increases with the reinforcement proportion, chloride concentration and copper content. (Author) 10 refs

  18. Spherical nanostructured Si/C composite prepared by spray drying technique for lithium ion batteries anode

    Energy Technology Data Exchange (ETDEWEB)

    Chen Libao [Energy Science and Technology Laboratory, Shanghai Institute of Microsystem and Information Technology, Chinese Academy of Sciences, Shanghai 200050 (China); Graduate School of Chinese Academy of Sciences, Beijing 100049 (China); Xie Xiaohua [Energy Science and Technology Laboratory, Shanghai Institute of Microsystem and Information Technology, Chinese Academy of Sciences, Shanghai 200050 (China); Graduate School of Chinese Academy of Sciences, Beijing 100049 (China); Wang Baofeng [Department of Chemical Engineering, Shanghai Jiao Tong University, Shanghai 200240 (China); Wang Ke [Energy Science and Technology Laboratory, Shanghai Institute of Microsystem and Information Technology, Chinese Academy of Sciences, Shanghai 200050 (China); Xie Jingying [Energy Science and Technology Laboratory, Shanghai Institute of Microsystem and Information Technology, Chinese Academy of Sciences, Shanghai 200050 (China) and Graduate School of Chinese Academy of Sciences, Beijing 100049 (China)]. E-mail: jyxie@mail.sim.ac.cn

    2006-07-15

    Spherical nanostructured Si/C composite was prepared by spray drying technique, followed by heat treatment, in which nanosized silicon and fine graphite particles were homogeneously embedded in carbon matrix pyrolyzed by phenol formaldehyde resin. Cyclic voltammetry tests showed two pairs of redox peaks corresponding to lithiation and delithiation of Si/C composite. The Si/C composite exhibited a reversible capacity of 635 mAh g{sup -1} and good cycle performance used in lithium ion batteries. To improve cycle performance of this Si/C composite further, the carbon-coated Si/C composite was synthesized by the second spray drying and heat treatment processing. The cycle performance of carbon-coated Si/C composite was improved significantly, which was attributed to the formation of stable SEI passivation layers on the outer surface of carbon shell which protected the bared silicon from exposing to electrolyte directly.

  19. Spherical nanostructured Si/C composite prepared by spray drying technique for lithium ion batteries anode

    International Nuclear Information System (INIS)

    Chen Libao; Xie Xiaohua; Wang Baofeng; Wang Ke; Xie Jingying

    2006-01-01

    Spherical nanostructured Si/C composite was prepared by spray drying technique, followed by heat treatment, in which nanosized silicon and fine graphite particles were homogeneously embedded in carbon matrix pyrolyzed by phenol formaldehyde resin. Cyclic voltammetry tests showed two pairs of redox peaks corresponding to lithiation and delithiation of Si/C composite. The Si/C composite exhibited a reversible capacity of 635 mAh g -1 and good cycle performance used in lithium ion batteries. To improve cycle performance of this Si/C composite further, the carbon-coated Si/C composite was synthesized by the second spray drying and heat treatment processing. The cycle performance of carbon-coated Si/C composite was improved significantly, which was attributed to the formation of stable SEI passivation layers on the outer surface of carbon shell which protected the bared silicon from exposing to electrolyte directly

  20. Development of Advanced Environmental Barrier Coatings for SiC/SiC Ceramic Matrix Composites: Path Toward 2700 F Temperature Capability and Beyond

    Science.gov (United States)

    Zhu, Dongming; Harder, Bryan; Hurst, Janet B.; Good, Brian; Costa, Gustavo; Bhatt, Ramakrishna T.; Fox, Dennis S.

    2017-01-01

    Advanced environmental barrier coating systems for SiC-SiC Ceramic Matrix Composite (CMC) turbine and combustor hot section components are currently being developed to meet future turbine engine emission and performance goals. One of the significant coating development challenges is to achieve prime-reliant environmental barrier coating systems to meet the future 2700F EBC-CMC temperature stability and environmental durability requirements. This presentation will emphasize recent NASA environmental barrier coating system testing and down-selects, particularly the development path and properties towards 2700-3000F durability goals by using NASA hafnium-hafnia-rare earth-silicon-silicate composition EBC systems for the SiC-SiC CMC turbine component applications. Advanced hafnium-based compositions for enabling next generation EBC and CMCs capabilities towards ultra-high temperature ceramic coating systems will also be briefly mentioned.

  1. ZnO-SiO{sub 2} based nanocomposites prepared by a modified sol-gel method

    Energy Technology Data Exchange (ETDEWEB)

    Grigorie, Alexandra Carmen [Politehnica University Timisoara, Faculty of Industrial Chemistry and Environmental Engineering, 6 V. Parvan Blv., RO-300223, Timisoara (Romania); Muntean, Cornelia, E-mail: cornelia.muntean@upt.ro [Politehnica University Timisoara, Faculty of Industrial Chemistry and Environmental Engineering, 6 V. Parvan Blv., RO-300223, Timisoara (Romania); Politehnica University Timisoara, Research Institute for Renewable Energy, 2 Piata Victoriei, RO-300006, Timisoara (Romania); Vlase, Titus [West University of Timisoara, 4 V. Parvan Blv., RO-300223, Timisoara (Romania); Locovei, Cosmin [Politehnica University Timisoara, Research Institute for Renewable Energy, 2 Piata Victoriei, RO-300006, Timisoara (Romania); Politehnica University Timisoara, Faculty of Mechanical Engineering, 1 Mihai Viteazul Blv., RO-300222, Timisoara (Romania); Stefanescu, Mircea [Politehnica University Timisoara, Faculty of Industrial Chemistry and Environmental Engineering, 6 V. Parvan Blv., RO-300223, Timisoara (Romania)

    2017-01-15

    This paper presents a study on nanocomposites formation in ZnO-SiO{sub 2} systems with different ZnO:SiO{sub 2} molar ratios (1:4, 1:1, and 4:1), prepared employing a sol-gel method modified by an original procedure. The evolution of ZnO-SiO{sub 2} systems depending on the composition and temperature was studied by thermal analysis, Fourier transform infrared spectroscopy, X-ray diffractometry and transmission electron microscopy. Zn(II) carboxylate was synthesized in situ in hybrid silica gels by redox reaction between zinc nitrate and 1,3-propanediol. Its thermal decomposition at low temperatures led to ZnO dispersed in the pores of silica matrix. Only for the 4:1 system, at 400 and 600 °C, ZnO nanocrystallites (average size ∼9 nm) embedded in the amorphous silica matrix were obtained, the other systems being amorphous. Whatever the mixture composition is, above 600 °C, ZnO reacts with SiO{sub 2} to form zinc silicate. At 800 °C, for both 1:4 and 1:1 systems, poor crystallized β-Zn{sub 2}SiO{sub 4} and α-Zn{sub 2}SiO{sub 4} phases embedded in silica matrix were formed. Increasing the temperature, at 1000 °C, only for 1:1 system, β-Zn{sub 2}SiO{sub 4} phase turned into single phase α-Zn{sub 2}SiO{sub 4} (average crystallites size 28.3 nm). For 4:1 composition, at 800 and 1000 °C, systems consisting of ZnO and α-Zn{sub 2}SiO{sub 4} nanocrystallites dispersed in silica were obtained. - Highlights: • By modified sol-gel method, ZnO/SiO{sub 2} and Zn{sub 2}SiO{sub 4}/SiO{sub 2} nanocomposites were obtained. • ZnO dispersed in silica matrix results from zinc carboxylate thermal decomposition. • Zinc carboxylate was synthesized in situ in hybrid silica gels via redox reaction. • Evolution of ZnO in SiO{sub 2} matrix depends on temperature and system composition.

  2. Silicon carbide modified carbon materials. Formation of nanocrystalline SiC from thermochemical processes in the system coal tar pitch/poly(carbosilane)

    Energy Technology Data Exchange (ETDEWEB)

    Czosnek, C.; Janik, J.F.; Olejniczak, Z. [Stanislaw Staszic University of Mining & Meterology, AGH, Krakow (Poland)

    2002-12-01

    Poly(carbosilane) or PCS, (-CH{sub 2}-SiH(CH{sub 3})-){sub n}, is used as a Si-bearing precursor in combination with a coal tar pitch to study thermally induced transformations toward SiC-modified carbon composites. Following mixing of the components in the molten pitch at 160{sup o}C, the mixture is heated under argon atmosphere at 500{sup o}C yielding a solid carbonizate that is further subjected to separate pyrolysis experiments at 1300{sup o}C or 1650{sup o}C. At temperatures up to 500{sup o}C, the PCS reacts with suitable pitch components as well as undergoing decomposition reactions. At higher temperatures, clusters of prevailingly nanocrystalline beta-SiC are confirmed after the 1650{sup o}C pyrolysis step with indications that the formation of the compound starts at 1300{sup o}C. Si-29 MAS NMR, XRD, FT-IR, XPS, and elemental analysis are used to characterize each pyrolysis step, especially, from the viewpoint of transformation of silicon species to silicon carbide in the carbon matrix evolved from the pitch.

  3. Wear study of Al-SiC metal matrix composites processed through microwave energy

    Science.gov (United States)

    Honnaiah, C.; Srinath, M. S.; Prasad, S. L. Ajit

    2018-04-01

    Particulate reinforced metal matrix composites are finding wider acceptance in many industrial applications due to their isotropic properties and ease of manufacture. Uniform distribution of reinforcement particulates and good bonding between matrix and reinforcement phases are essential features in order to obtain metal matrix composites with improved properties. Conventional powder metallurgy technique can successfully overcome the limitation of stir casting techniques, but it is time consuming and not cost effective. Use of microwave technology for processing particulate reinforced metal matrix composites through powder metallurgy technique is being increasingly explored in recent times because of its cost effectiveness and speed of processing. The present work is an attempt to process Al-SiC metal matrix composites using microwaves irradiated at 2.45 GHz frequency and 900 W power for 10 minutes. Further, dry sliding wear studies were conducted at different loads at constant velocity of 2 m/s for various sliding distances using pin-on-disc equipment. Analysis of the obtained results show that the microwave processed Al-SiC composite material shows around 34 % of resistance to wear than the aluminium alloy.

  4. Evaluation of damage accumulation behavior and strength anisotropy of NITE SiC/SiC composites by acoustic emission, digital image correlation and electrical resistivity monitoring

    International Nuclear Information System (INIS)

    Nozawa, Takashi; Ozawa, Kazumi; Asakura, Yuuki; Kohyama, Akira; Tanigawa, Hiroyasu

    2014-01-01

    Understanding the cracking process of the composites is essential to establish the design basis for practical applications. This study aims to investigate the damage accumulation process and its anisotropy for nano-infiltration transient eutectic sintered (NITE) SiC/SiC composites by various characterization techniques such as the acoustic emission (AE), digital image correlation (DIC) and electrical resistivity (ER) measurements. Cracking behavior below the proportional limit stress (PLS) was specifically addressed. Similar to the other generic SiC/SiC composites, the 1st AE event was identified below the PLS for NITE SiC/SiC composites with a dependency of fabric orientation. The DIC results support that the primary failure mode depending on fiber orientation affected more than the other minor modes did. Detailed AE waveform analysis by wavelet shows a potential to classify the failure behavior depending on architecture. Cracking below the PLS is a potential concern in component deign but the preliminary ER measurements imply that the impact of cracking below the PLS on composite function was limited

  5. Wearproof composition coatings on the basis of SiC-AL2O3 for restoration and reiforcement of the components of aircraft ground support equipment

    Directory of Open Access Journals (Sweden)

    О. П. Уманський

    2013-07-01

    Full Text Available On the ground of research of a contact interaction of the melts of the system Ni–Al with the ceramics of SiC–Al2O3 content, the possibility of wearproof coating deposition of the system SiC–Al2O3–Ni–Al by gas-flame techniques has been proved. Technological features of their acquisition also have been studied. The structure of coatings from composition material that contains the SiC–Al2O3 wearproof component and Ni–Al metallic binder, deposited by the method of high velocity air fuel deposition (HVAF on medium-carbon steel steels has been researched. Tribotechnical descriptions of the deposited coatings under the conditions of friction without lubricating materials in the air environment in wide range of speed-load modes of the “pin–on–disk” layout have been studied. The features and regularities of their wear mechanisms retaining the constant speed and constant load have been determined

  6. Protección contra la oxidación de materiales compuestos SiC(C/SiC mediante la combinación de recubrimientos de silicatos de itrio y sílice

    Directory of Open Access Journals (Sweden)

    Aparicio, M.

    2001-12-01

    Full Text Available The factor which currently precludes the use of carbon fibre reinforced silicon carbide (C/SiC in high temperature structural applications is the oxidation of carbon fibres at temperatures greater than 450ºC (1. For this reason, it is necessary to develop coatings capable of protecting C/SiC components from oxidation for extended periods at 1600ºC. Conventional coatings consist of multilayers of different materials with complementary antioxidant properties. The objective of this work was to develop a multilayer coating consisted by a bonding layer of SiC, a intermediate layer of yttrium silicates: Y2Si2O7 and Y2SiO5, and an external layer of SiO2. Different techniques have been used to prepare the layers: painting with policarbosilane solutions, slip-coating and sol-gel, respectively. The behaviour against oxidation of coated composite material has been evaluated, and the samples before and after oxidation has been characterised by SEM. The cracking of SiC coating leads to a very low oxidation resistance at low temperatures. Only when the substrate is protected by the trilayer coating the reduction of the oxidation rate is considerable, and the weight loss is reduced from 50% (with a SiC coating to 15%.

    El principal inconveniente para la utilización de los materiales compuestos C/SiC en aplicaciones estructurales de alta temperatura es la elevada velocidad de oxidación de la fibra de carbono por encima de 450°C (1. Por esta razón, es necesario el desarrollo de recubrimientos capaces de proteger de la oxidación a estos materiales durante periodos prolongados a temperaturas de hasta 1600°C. Habitualmente, los recubrimientos están formados por multicapas con características antioxidantes complementarias. El objetivo de este trabajo ha sido el desarrollo de un recubrimiento multicapa formado por una capa interior de SiC, una intermedia de silicatos de itrio: Y2Si2O7 y Y2SiO5, y una exterior de SiO2. En su procesamiento se han

  7. Dependence of glass-forming ability on starting compositions in Y2O3–Al2O3–SiO2 system

    Directory of Open Access Journals (Sweden)

    Yixiang Chen

    2011-09-01

    Full Text Available The dependence of glass-forming ability on starting compositions in Y2O3–Al2O3–SiO2 (YAS system has been investigated by melting experiment. Transparent YAS glasses have been prepared under the condition of furnace cooling instead of quenching. It is found that, in the YAS ternary phase diagram, the compositions on the Y3Al5O12–SiO2 line and with 52-68 mol% SiO2 have a higher glass-forming ability to produce pure glass. For the compositions with too much or less SiO2 or with Y/Al = 5/3, 1/1, or 1/3, crystallization occurs with the formation of Y3Al5O12, Y2Si2O7, Al6Si2O13, or SiO2. The densities of the YAS glasses increase with decreasing SiO2 contents and increasing Y/Al ratios, and for the samples with Y/Al = 3/5 there is a good linear relationship between the density and SiO2 content.

  8. Performance and Durability of Environmental Barrier Coatings on SiC/SiC Ceramic Matrix Composites

    Science.gov (United States)

    Zhu, Dongming; Harder, Bryan; Bhatt, Ramakrishna

    2016-01-01

    This presentation highlights advanced environmental barrier coating (EBC) and SiC-SiC Ceramic Matrix Composites (CMC) systems for next generation turbine engines. The emphasis will be placed on fundamental coating and CMC property evaluations; and the integrated system performance and degradation mechanisms in simulated laboratory turbine engine testing environments. Long term durability tests in laser rig simulated high heat flux the rmomechanical creep and fatigue loading conditions will also be presented. The results can help improve the future EBC-CMC system designs, validating the advanced EBC-CMC technologies for hot section turbine engine applications.

  9. X-ray tomography investigation of intensive sheared Al–SiC metal matrix composites

    Energy Technology Data Exchange (ETDEWEB)

    De Giovanni, Mario; Warnett, Jason M.; Williams, Mark A. [WMG, University of Warwick, Coventry CV4 7AL (United Kingdom); Haribabu, Nadendla [BCAST, Brunel University London, Uxbridge UB8 3PH (United Kingdom); Srirangam, Prakash, E-mail: p.srirangam@warwick.ac.uk [WMG, University of Warwick, Coventry CV4 7AL (United Kingdom)

    2015-12-15

    X-ray computed tomography (XCT) was used to characterise three dimensional internal structure of Al–SiC metal matrix composites. The alloy composite was prepared by casting method with the application of intensive shearing to uniformly disperse SiC particles in the matrix. Visualisation of SiC clusters as well as porosity distribution were evaluated and compared with non-shearing samples. Results showed that the average particle size as well as agglomerate size is smaller in sheared sample compared to conventional cast samples. Further, it was observed that the volume fraction of porosity was reduced by 50% compared to conventional casting, confirming that the intensive shearing helps in deagglomeration of particle clusters and decrease in porosity of Al–SiC metal matrix composites. - Highlights: • XCT was used to visualise 3D internal structure of Al-SiC MMC. • Al-SiC MMC was prepared by casting with the application of intensive shearing. • SiC particles and porosity distribution were evaluated. • Results show shearing deagglomerates particle clusters and reduces porosity in MMC.

  10. High-efficient production of SiC/SiO2 core-shell nanowires for effective microwave absorption

    KAUST Repository

    Zhong, Bo; Sai, Tianqi; Xia, Long; Yu, Yuanlie; Wen, Guangwu

    2017-01-01

    In the current report, we have demonstrated that the high-efficient production of SiC/SiO2 core-shell nanowires can be achieved through the introduction of trace of water vapor during the chemical vapor deposition process. The yield of the SiC/SiO2 core-shell nanowires is dramatically improved due to the introduction of water vapor. The SiC/SiO2 core-shell nanowires exhibit an excellent microwave absorption property in the frequency range of 2.0–18.0GHz with a very low weight percentage of 0.50wt.% in the absorbers. A minimum reflection loss value of −32.72dB (>99.99% attenuation) at 13.84GHz has been observed with the absorber thickness of 3.0mm. Moreover, the SiC/SiO2 core-shell nanowires based absorber can reach an effective absorption bandwidth (<−10dB) of 5.32GHz with the absorber thickness of 3.5mm. Furthermore, a possible absorption mechanism is also proposed in detail for such effective attenuation of microwave which can be attributed to the dielectric loss and magnetic loss of SiC/SiO2 core-shell nanowires.

  11. High-efficient production of SiC/SiO2 core-shell nanowires for effective microwave absorption

    KAUST Repository

    Zhong, Bo

    2017-02-21

    In the current report, we have demonstrated that the high-efficient production of SiC/SiO2 core-shell nanowires can be achieved through the introduction of trace of water vapor during the chemical vapor deposition process. The yield of the SiC/SiO2 core-shell nanowires is dramatically improved due to the introduction of water vapor. The SiC/SiO2 core-shell nanowires exhibit an excellent microwave absorption property in the frequency range of 2.0–18.0GHz with a very low weight percentage of 0.50wt.% in the absorbers. A minimum reflection loss value of −32.72dB (>99.99% attenuation) at 13.84GHz has been observed with the absorber thickness of 3.0mm. Moreover, the SiC/SiO2 core-shell nanowires based absorber can reach an effective absorption bandwidth (<−10dB) of 5.32GHz with the absorber thickness of 3.5mm. Furthermore, a possible absorption mechanism is also proposed in detail for such effective attenuation of microwave which can be attributed to the dielectric loss and magnetic loss of SiC/SiO2 core-shell nanowires.

  12. Property Evaluation and Damage Evolution of Environmental Barrier Coatings and Environmental Barrier Coated SiC/SiC Ceramic Matrix Composite Sub-Elements

    Science.gov (United States)

    Zhu, Dongming; Halbig, Michael; Jaskowiak, Martha; Hurst, Janet; Bhatt, Ram; Fox, Dennis S.

    2014-01-01

    This paper describes recent development of environmental barrier coatings on SiC/SiC ceramic matrix composites. The creep and fatigue behavior at aggressive long-term high temperature conditions have been evaluated and highlighted. Thermal conductivity and high thermal gradient cyclic durability of environmental barrier coatings have been evaluated. The damage accumulation and complex stress-strain behavior environmental barrier coatings on SiCSiC ceramic matrix composite turbine airfoil subelements during the thermal cyclic and fatigue testing of have been also reported.

  13. Early implementation of SiC cladding fuel performance models in BISON

    Energy Technology Data Exchange (ETDEWEB)

    Powers, Jeffrey J. [Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States)

    2015-09-18

    SiC-based ceramic matrix composites (CMCs) [5–8] are being developed and evaluated internationally as potential LWR cladding options. These development activities include interests within both the DOE-NE LWR Sustainability (LWRS) Program and the DOE-NE Advanced Fuels Campaign. The LWRS Program considers SiC ceramic matrix composites (CMCs) as offering potentially revolutionary gains as a cladding material, with possible benefits including more efficient normal operating conditions and higher safety margins under accident conditions [9]. Within the Advanced Fuels Campaign, SiC-based composites are a candidate ATF cladding material that could achieve several goals, such as reducing the rates of heat and hydrogen generation due to lower cladding oxidation rates in HT steam [10]. This work focuses on the application of SiC cladding as an ATF cladding material in PWRs, but these work efforts also support the general development and assessment of SiC as an LWR cladding material in a much broader sense.

  14. Ceramic matrix micro-composites prepared by P-Rcvd within the (Ti-Si-B-C) system

    International Nuclear Information System (INIS)

    Jacques, Sylvain

    2014-01-01

    Nano-scale carbide multilayered inter-phases were deposited within the (Ti-Si-B-C) system by pressure-Pulsed Reactive Chemical Vapor Deposition (P-RCVD) on single filament Hi-Nicalon fibers and embedded in a SiC matrix sheath. The Reactive method, in which the titanium-containing layer growth involves the consumption of the pre-deposited Si-B-C sublayer, allowed TiC- and TiB 2 -based films to be obtained with a porous multilayer microstructure as a result of the Kirkendall effect. A first difficulty relied on the protection of the fiber surface which was very sensitive to chemical attack by P-RCVD. This difficulty could be circumvented through a first deposited SiC sub-layer thick enough to protect the surface of the fiber. But, because the porosity volume fraction was still not high enough, the role of mechanical fuse of these pyrocarbon-free inter-phases could not be evidenced from the micro-composite tensile curves, which remained fully linear up to the failure. Finally, the P-RCVD method was applied to the matrix processing itself. Micro-composites, this time with a pyrocarbon interphase but also with new matrix materials such as Ti 3 SiC 2 , were prepared and characterized. (author)

  15. Creep Behavior of Hafnia and Ytterbium Silicate Environmental Barrier Coating Systems on SiC/SiC Ceramic Matrix Composites

    Science.gov (United States)

    Zhu, Dongming; Fox, Dennis S.; Ghosn, Louis J.; Harder, Bryan

    2011-01-01

    Environmental barrier coatings will play a crucial role in future advanced gas turbine engines because of their ability to significantly extend the temperature capability and stability of SiC/SiC ceramic matrix composite (CMC) engine components, thus improving the engine performance. In order to develop high performance, robust coating systems for engine components, appropriate test approaches simulating operating temperature gradient and stress environments for evaluating the critical coating properties must be established. In this paper, thermal gradient mechanical testing approaches for evaluating creep and fatigue behavior of environmental barrier coated SiC/SiC CMC systems will be described. The creep and fatigue behavior of Hafnia and ytterbium silicate environmental barrier coatings on SiC/SiC CMC systems will be reported in simulated environmental exposure conditions. The coating failure mechanisms will also be discussed under the heat flux and stress conditions.

  16. Development ceramic composites based on Al2O3, SiO2 and IG-017 additive

    Science.gov (United States)

    Kurovics, E.; Shmakova, A.; Kanev, B.; Gömze, L. A.

    2017-02-01

    Based on high purity alumina and quartz powders and IG-017 bio-original additives the authors have developed new ceramic composite materials for different industrial purposes. The main goal was to fine a material and morphological structures of high performance ceramic composites as frames for development complex materials for extreme consumptions in the future. For this the mixed powders of Al2O3 , SiO2 and IG-017 bio-original additive were uniaxially pressed at different compaction pressures into disc shapes and were sintered in electric kiln under air (1) and nitrogrn (2) atmosphere. The grain size distributions of the raw materials were determined by laser granulometry. There thermo-physical properties were also determined by derivatography. The prepared and sintered specimens were tested on geometrical sizes, microstructure and morphology by scanning electron microscopy, porosity and water absorption. In this work the authors present the results of their research and investigation.

  17. Investigation into solubility and diffusion in SiC-NbC, SiC-TiC, SiC-ZrC systems

    International Nuclear Information System (INIS)

    Safaraliev, G.K.; Tairov, Yu.M.; Tsvetkov, V.F.; Shabanov, Sh.Sh.

    1991-01-01

    An investigation is carried out which demonstrates solid-phase interaction between SiC and NbC, TiC and ZrC monocrystals. The monocrystals are subjected to hot pressing in SiC powder with dispersity of 5x10 -6 m. The pressing temperature is 2270-2570 K and pressure is varied in the range of 20-40 MPa. Element composition and the distribution profile in a thin layer near the boundary of SiC-NbC, SiC-TiC and SiC-ZrC are investigated by the Anger spectroscopy method. The obtained results permit to make the conclusion in the possibility of solid solution formation in investigated systems

  18. X-ray absorption spectroscopy study on SiC-side interface structure of SiO2–SiC formed by thermal oxidation in dry oxygen

    Science.gov (United States)

    Isomura, Noritake; Kosaka, Satoru; Kataoka, Keita; Watanabe, Yukihiko; Kimoto, Yasuji

    2018-06-01

    Extended X-ray absorption fine structure (EXAFS) spectroscopy is demonstrated to measure the fine atomic structure of SiO2–SiC interfaces. The SiC-side of the interface can be measured by fabricating thin SiO2 films and using SiC-selective EXAFS measurements. Fourier transforms of the oscillations of the EXAFS spectra correspond to radial-structure functions and reveal a new peak of the first nearest neighbor of Si for m-face SiC, which does not appear in measurements of the Si-face. This finding suggests that the m-face interface could include a structure with shorter Si–C distances. Numerical calculations provide additional support for this finding.

  19. Stress-temperature-lifetime response of nicalon fiber-reinforced SiC composites in air

    International Nuclear Information System (INIS)

    Lin, Hua-Tay; Becher, P.F.

    1996-01-01

    Time-to-failure tests were conducted in four-point flexure and in air as a function of stress levels and temperatures to study the lifetime response of various Nicalon fiber-reinforced SiC (designated as Nic/SiC) composites with a graphitic interfacial coating. The results indicated that all of the Nic/SiC composites exhibit a similar stress-dependent failure at applied stress greater than a threshold value. In this case, the lifetimes of the composites increased with decrease in both stress level and test temperature. The lifetime of the composites appeared to be relatively insensitive to the thickness of graphitic interface layer and was enhanced somewhat by the addition of oxidation inhibitors. Electron microscopy and oxidation studies indicated that the life of the Nic/SiC composites was governed by the oxidation of the graphitic interfaces and the on of glass(es) in composites due to the oxidation of the fiber and matrix, inhibitor phases

  20. In-pile Hydrothermal Corrosion Evaluation of Coated SiC Ceramics and Composites

    Energy Technology Data Exchange (ETDEWEB)

    Carpenter, David [Massachusetts Inst. of Technology (MIT), Cambridge, MA (United States); Ang, Caen [Univ. of Tennessee, Knoxville, TN (United States); Katoh, Yutai [Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States); Linton, Kory D. [Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States); Terrani, Kurt A. [Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States)

    2017-09-01

    Hydrothermal corrosion accelerated by water radiolysis during normal operation is among the most critical technical feasibility issues remaining for silicon carbide (SiC) composite-based cladding that could provide enhanced accident-tolerance fuel technology for light water reactors. An integrated in-pile test was developed and performed to determine the synergistic effects of neutron irradiation, radiolysis, and pressurized water flow, all of which are relevant to a typical pressurized water reactor (PWR). The test specimens were chosen to cover a range of SiC materials and a variety of potential options for environmental barrier coatings. This document provides a summary of the irradiation vehicle design, operations of the experiment, and the specimen loading into the irradiation vehicle.

  1. Cs2.5H0.5PWO40/SiO2 as addition self-humidifying composite membrane for proton exchange membrane fuel cells

    International Nuclear Information System (INIS)

    Wang, L.; Yi, B.L.; Zhang, H.M.; Xing, D.M.

    2007-01-01

    In this paper, we first reported a novel self-humidifying composite membrane for the proton exchange membrane fuel cell (PEMFC). Cs 2.5 H 0.5 PWO 40 /SiO 2 catalyst particles were dispersed uniformly into the Nafion (registered) resin, and then Cs 2.5 H 0.5 PWO 40 -SiO 2 /Nafion composite membrane was prepared using solution-cast method. Compared with the H 3 PWO 40 (PTA) , the Cs 2.5 H 0.5 PWO 40 /SiO 2 was steady due to the substitute of H + with Cs + and the interaction between the Cs 2.5 H 0.5 PWO 40 and SiO 2 . And compared with the performance of the fuel cell with commercial Nafion (registered) NRE-212 membrane, the cell performance with the self-humidifying composite membrane was obviously improved under both humidified and dry conditions at 60 and 80 o C. The best performance under dry condition was obtained at 60 o C. The self-humidifying composite membrane could minimize membrane conductivity loss under dry conditions due to the presence of catalyst and hydrophilic Cs 2.5 H 0.5 PWO 40 /SiO 2 particles

  2. Dual-nanoparticulate-reinforced aluminum matrix composite materials

    International Nuclear Information System (INIS)

    Kwon, Hansang; Cho, Seungchan; Kawasaki, Akira; Leparoux, Marc

    2012-01-01

    Aluminum (Al) matrix composite materials reinforced with carbon nanotubes (CNT) and silicon carbide nanoparticles (nano-SiC) were fabricated by mechanical ball milling, followed by hot-pressing. Nano-SiC was used as an active mixing agent for dispersing the CNTs in the Al powder. The hardness of the produced composites was dramatically increased, up to eight times higher than bulk pure Al, by increasing the amount of nano-SiC particles. A small quantity of aluminum carbide (Al 4 C 3 ) was observed by TEM analysis and quantified using x-ray diffraction. The composite with the highest hardness values contained some nanosized Al 4 C 3 . Along with the CNT and the nano-SiC, Al 4 C 3 also seemed to play a role in the enhanced hardness of the composites. The high energy milling process seems to lead to a homogeneous dispersion of the high aspect ratio CNTs, and of the nearly spherical nano-SiC particles in the Al matrix. This powder metallurgical approach could also be applied to other nanoreinforced composites, such as ceramics or complex matrix materials. (paper)

  3. The effect of CaO/SiO2 molar ratio of CaO-Al2O3-SiO2 glasses on their structure and reactivity in alkali activated system.

    Science.gov (United States)

    Kucharczyk, Sylwia; Sitarz, Maciej; Zajac, Maciej; Deja, Jan

    2018-04-05

    The influence of CaO/SiO 2 molar ratio of calcium aluminosilicate glasses on resulting structure and reactivity was investigated. Chemical compositions of glasses were chosen to mimic the composition of the fly ash and slag amorphous phase. Understanding the reactivity of these materials is of high importance allowing further development of the composite cements to limit the environmental footprint of cement industry. Fourier transform infrared spectroscopy (FTIR) and Raman spectroscopy were employed to examine the structure of glasses. Reactivity of the glasses was analyzed on paste samples after 1, 2, 7, 28 and 90days of curing by means of thermogravimetry (TGA), X-ray diffraction (XRD) and FTIR. Spectroscopic results emphasize dependence of the structure on the chemical composition of the glasses. The higher CaO/SiO 2 the more depolymerized the glass network is, though there is no direct correlation with the reactivity. Significant differences in reactivity is observed primarily between the glasses of peraluminous (CaO/Al 2 O 3 1). Amongst the pastes made of glasses of percalcic region a higher degree of reaction at later ages is observed for the paste containing glass of lower CaO/SiO 2 molar ratio. This is due to both degree of depolimerization and the nature of these glasses (pozzolanic and hydraulic materials). No difference of degree of reaction has been observed within the glasses of CaO/SiO 2 lower than 1. Copyright © 2018 Elsevier B.V. All rights reserved.

  4. The effect of CaO/SiO2 molar ratio of CaO-Al2O3-SiO2 glasses on their structure and reactivity in alkali activated system

    Science.gov (United States)

    Kucharczyk, Sylwia; Sitarz, Maciej; Zajac, Maciej; Deja, Jan

    2018-04-01

    The influence of CaO/SiO2 molar ratio of calcium aluminosilicate glasses on resulting structure and reactivity was investigated. Chemical compositions of glasses were chosen to mimic the composition of the fly ash and slag amorphous phase. Understanding the reactivity of these materials is of high importance allowing further development of the composite cements to limit the environmental footprint of cement industry. Fourier transform infrared spectroscopy (FTIR) and Raman spectroscopy were employed to examine the structure of glasses. Reactivity of the glasses was analyzed on paste samples after 1, 2, 7, 28 and 90 days of curing by means of thermogravimetry (TGA), X-ray diffraction (XRD) and FTIR. Spectroscopic results emphasize dependence of the structure on the chemical composition of the glasses. The higher CaO/SiO2 the more depolymerized the glass network is, though there is no direct correlation with the reactivity. Significant differences in reactivity is observed primarily between the glasses of peraluminous (CaO/Al2O3 1). Amongst the pastes made of glasses of percalcic region a higher degree of reaction at later ages is observed for the paste containing glass of lower CaO/SiO2 molar ratio. This is due to both degree of depolimerization and the nature of these glasses (pozzolanic and hydraulic materials). No difference of degree of reaction has been observed within the glasses of CaO/SiO2 lower than 1.

  5. Advanced Environmental Barrier Coating and SA Tyrannohex SiC Composites Integration for Improved Thermomechanical and Environmental Durability

    Science.gov (United States)

    Zhu, Dongming; Halbig, Michael; Singh, Mrityunjay

    2018-01-01

    The development of 2700 degF capable environmental barrier coating (EBC) systems, particularly, the Rare Earth "Hafnium" Silicon bond coat systems, have significantly improved the temperature capability and environmental stability of SiC/SiC Ceramic Matrix Composite Systems. We have specifically developed the advanced 2700 degF EBC systems, integrating the EBC to the high temperature SA Tyrannohex SiC fiber composites, for comprehensive performance and durability evaluations for potential turbine engine airfoil component applications. The fundamental mechanical properties, environmental stability and thermal gradient cyclic durability performance of the EBC - SA Tyrannohex composites were investigated. The paper will particularly emphasize the high pressure combustion rig recession, cyclic thermal stress resistance and thermomechanical low cycle fatigue testing of uncoated and environmental barrier coated Tyrannohex SiC SA composites in these simulated turbine engine combustion water vapor, thermal gradients, and mechanical loading conditions. We have also investigated high heat flux and flexural fatigue degradation mechanisms, determined the upper limits of operating temperature conditions for the coated SA composite material systems in thermomechanical fatigue conditions. Recent progress has also been made by using the self-healing rare earth-silicon based EBCs, thus enhancing the SA composite hexagonal fiber columns bonding for improved thermomechanical and environmental durability in turbine engine operation environments. More advanced EBC- composite systems based on the new EBC-Fiber Interphases will also be discussed.

  6. Preparation, characterization and infrared emissivity study of helical polyurethane-SiO2 core-shell composite

    International Nuclear Information System (INIS)

    Wang Zhiqiang; Zhou Yuming; Yao Qingzhao; Sun Yanqing

    2009-01-01

    Helical polyurethane-SiO 2 (HPU-SiO 2 ) core-shell composite was prepared after surface modification of SiO 2 nanoparticles. HPU-SiO 2 was characterized by Fourier-transform infrared (FT-IR) spectroscopy, X-ray photoelectron spectroscopy (XPS), ultraviolet (UV) spectroscopy, X-ray diffraction (XRD) and transmission electron microscopy (TEM). The results indicate that the helical polyurethane has been successfully grafted onto the surfaces of the modified SiO 2 . HPU-SiO 2 composite exhibits clearly core-shell structure. The ultraviolet absorption and crystallizability of HPU-SiO 2 are changed due to the shell of helical polyurethane, which possesses regular single-handed conformation and inter-chain hydrogen bonds. The infrared emissivity of HPU-SiO 2 was also investigated. The result indicates that the interfacial interactions between organic shell and inorganic core induce the infrared emissivity value being reduced from 0.781 for SiO 2 to 0.503 for HPU-SiO 2 .

  7. Preparation of SiC and Ag/SiC coatings on TRISO surrogate particles by Pulsed Laser Deposition

    International Nuclear Information System (INIS)

    Lustfeld, Martin; Reinecke, Anne-Maria; Lippman, Wolfgang; Hurtado, Antonio; Ruiz-Moreno, Ana

    2014-01-01

    Recently published research results suggest significant advantages of using nanocrystalline instead of coarse grained SiC for nuclear applications. In this work it was attempted to prepare nanocrystalline SiC coatings on TRISO surrogate kernels using the pulsed laser deposition (PLD) process. As a plasma-based physical vapor deposition process, PLD allows the synthesis of dense and stoichiometric coatings in the amorphous or nanocrystalline phase. Two different types of TRISO surrogate kernels were used with outer diameters of 500 pm and 800 μm, respectively: plain Al_2O_3 kernels and ZrO_2 kernels coated with TRISO-like buffer and pyrolytic carbon (PyC) layers. In a second step, the PLD process was used for the preparation of multilayer coatings consisting of a Ag layer buried with a SiC layer. The samples were analyzed regarding their morphology, microstructure, crystalline phase and chemical composition using scanning electron microscopy (SEM), laser scanning microscopy (LSM), x-ray diffraction (XRD) and energy- dispersive x-ray spectroscopy (EDX). The samples will be used in future work for out-of-pile investigations of both thermal stability and Ag retention capability of nanocrystalline SiC layers. X-ray diflraction measurements did not confirm nano crystallinity of the SiC coatings, but rather indicated that the coatings were mainly amorphous possibly with a little fraction of the nanocrystalline phase. Further analyses showed that some of the SiC coatings had an adequate stoichiometric composition and that Ag/SiC multilayer coatings were successfully produced by PLD. Coatings on TRISO- like buffer and PyC layers exhibited good adhesion to the substrate while coatings on Al_2O_3 kernels were susceptible to delamination. The results suggest that PLD is generally suitable for SiC coating of TRISO particles. However, further optimization of the process parameters such as the coating temperature is needed to obtain fine- grained non-columnar SiC layers that are

  8. Fabrication of Au_n_a_n_o_p_a_r_t_i_c_l_e@mSiO_2@Y_2O_3:Eu nanocomposites with enhanced fluorescence

    International Nuclear Information System (INIS)

    Li, Huiqin; Kang, Jianmiao; Yang, Jianhui; Wu, Biao

    2016-01-01

    Herein, Au_n_a_n_o_p_a_r_t_i_c_l_e@mSiO_2@Y_2O_3:Eu nanocomposites are synthesized through layer-by-layer assembly technology. Au_n_a_n_o_p_a_r_t_i_c_l_e@mSiO_2 core–shell nanospheres were prepared at first in the presence of CTAB in aqueous solution system by the modified one-pot method. A chemical precipitation method and a succeeding calcination process were adopted to the growth of Y_2O_3:Eu shells on the surfaces of Au_n_a_n_o_p_a_r_t_i_c_l_e@mSiO_2 core–shell nanospheres. The structure, morphology and composition of the nanocomposites were confirmed by XRD, TEM and UV–vis absorption spectrum. The prepared Au_n_a_n_o_p_a_r_t_i_c_l_e@mSiO_2@Y_2O_3:Eu nanocomposites have showed the emission intensity enhances to 6.23 times at 30 nm thickness of the silica spacer between the core of Au nanoparticle and the shell of Y_2O_3:Eu. According to the observations of fluorescent lifetime and the modeling of local electric field, the metal-enhanced and quenched fluorescence is closely related with the enhancement of excitation and radiative decay rate and the quenching by NRET comes as a result of competition between the distance-dependent mechanisms. This kind of multifunctional inorganic material will be widely used in electronics, biology and medical drug loading, etc. - Highlights: • Fabrication of Au_n_a_n_o_p_a_r_t_i_c_l_e@mSiO_2@Y_2O_3:Eu nanocomposites with core-spacer-shell structure. • The controllable fluorescence is achieved by adjusting the spacer thickness of silica. • The fluorescence enhancement is 6.23-fold at an optimal spacer thickness about 30 nm. • The metal-enhanced fluorescence mechanism is proposed.

  9. Microstructure and Mechanical Properties of Multiphase Strengthened Al/Si/Al_2O_3/SiO_2/MWCNTs Nano composites Sintered by In Situ Vacuum Hot Pressing

    International Nuclear Information System (INIS)

    Li, J.; Jiang, X.; Zhu, D.; Zhu, M.; Shao, Z.; Johnson, S.; Luo, Z.

    2015-01-01

    Eutectic Al/Si binary alloy is technically one of the most important Al casting alloys due to its high corrosion resistance, evident shrinkage reduction, low thermal expansion coefficient, high fluidity, and good weldability. In this work, multi phased Al/Si matrix nano composites reinforced with Al_2O_3 and multi walled carbon nano tubes (MWCNTs) have been sintered by an in situ vacuum hot-pressing method. The alumina Al_2O_3 nanoparticles were introduced by an in situ reaction of Al with SiO_2. Microstructure and mechanical properties of the sintered Al/Si/Al_2O_3/SiO_2/MWCNTs nano composites with different alumina contents were investigated. The mechanical properties were determined by micro-Vickers hardness and compressive and shear strength tests. The results demonstrated that in situ alumina and MWCNTs had impacts on microstructure and mechanical properties of the nano composites. Based on the mechanical properties and microstructure of the nano composites, strengthening and fracture mechanisms by multiple reinforcements were analyzed

  10. Temperature stability of c-axis oriented LiNbO3/SiO2/Si thin film layered structures

    International Nuclear Information System (INIS)

    Tomar, Monika; Gupta, Vinay; Mansingh, Abhai; Sreenivas, K.

    2001-01-01

    Theoretical calculations have been performed for the temperature stability of the c-axis oriented LiNbO 3 thin film layered structures on passivated silicon (SiO 2 /Si) substrate with and without a non-piezoelectric SiO 2 overlayer. The phase velocity, electromechanical coupling coefficient and temperature coefficient of delay (TCD) have been calculated. The thicknesses of various layers have been determined for optimum SAW performance with zero TCD. The presence of a non-piezoelectric SiO 2 overlayer on LiNbO 3 film is found to significantly enhance the coupling coefficient. The optimized results reveal that a high coupling coefficient of K 2 =3.45% and a zero TCD can be obtained in the SiO 2 /LiNbO 3 /SiO 2 /Si structure with a 0.235λ thick LiNbO 3 layer sandwiched between 0.1λ thick SiO 2 layers. (author)

  11. Preparation of Ag@mSiO{sub 2} and Pt@mSiO{sub 2}nano composites using trioctylmethyl ammonium hydrogen phthalate (TOMAHP) ionic liquid as reaction medium

    Energy Technology Data Exchange (ETDEWEB)

    Biswas, Sujoy, E-mail: sujoyb@barc.gov.in [Chemical Engineering Group, Bhabha Atomic Research Centre, Mumbai 400085 (India); Dasgupta, Kinshuk [Materials Group, Bhabha Atomic Research Centre, Mumbai 400085 (India); Bahadur, Jitendra [Solid State Physics Division, Bhabha Atomic Research Centre, Mumbai 400085 (India); Tewari, Raghavendra [Materials Group, Bhabha Atomic Research Centre, Mumbai 400085 (India); Mazumder, Subhasish [Solid State Physics Division, Bhabha Atomic Research Centre, Mumbai 400085 (India)

    2016-09-15

    A novel one step green chemistry approach utilizing trioctylmethyl ammonium hydrogen phthalate (TOMAHP), task specific ionic liquid has been attempted for synthesis of Ag and Pt nanoparticles supported on silica (Ag@mSiO{sub 2} and Pt@mSiO{sub 2}). Structure, size distribution and morphology of these nano-composite particles were evaluated using X-ray diffraction (XRD), transmission electron microscopy (TEM), small angle neutron scattering (SANS) as well as small angle X-ray scattering (SAXS) techniques. The XRD results show that Ag/Pt metal nanoparticles deposited on to SiO{sub 2} surface are face center cubic (fcc) in nature. The TEM and SAXS/SANS results show the morphology and size distributions of Ag and Pt nanoparticles loaded on to the surface of SiO{sub 2}. It has been found that Ag nanoparticles are well dispersed on to the SiO{sub 2} surface and are quite monodisperse in size, whereas Pt nanoparticles are quite polydisperse in size and forms aggregate or chain like structure on SiO{sub 2} surface containing primary nanoparticles of typical size range 3–7 nm. The stability of nanoparticles, which controls its dispersion on SiO{sub 2} substrate, has been discussed. - Graphical abstract: Mechanism for Ag@mSiO{sub 2} and Pt@mSiO{sub 2} nano composites in TOMAHP ionic liquid medium. - Highlights: • Novel methods for preparation of Pt@SiO{sub 2} and Ag@SiO{sub 2} nano composite in functionalized ionic liquid. • Pt@SiO{sub 2} and Ag@SiO{sub 2} nano composite are characterized using XRD, TEM as well as small angle x-ray scattering techniques. • The sizes of nano composite is <10 nm in size. • The method is simple one step, green chemical reduction method to prepare SiO{sub 2} support nano catalyst.

  12. Report on the Fracture Analysis of HfB(sub 2)-SiC and ZrB(sub 2)-SiC Composites; TOPICAL

    International Nuclear Information System (INIS)

    MECHOLSKY, JR. JOHN J.

    2001-01-01

    Hafnium diboride-silicon carbide (HS) and zirconium diboride-silicon carbide (ZS) composites are potential materials for high temperature, thermal shock applications such as for components on re-entry vehicles. In order to establish material constants necessary for evaluation of in situ fracture, bars fractured in four-point flexure were examined using fractographic principles. The fracture toughness was determined from measurements of the critical crack sizes and the strength values and the crack branching constants were established to use in forensic fractography for future in-flight tests. The fracture toughnesses range from about 13 MPam(sup 1/2) at room temperature to about 6 MPam(sup 1/2) at 1400 C for ZrB(sub 2)-Sic composites and from about 13 MPam(sup 1/2) at room temperature to about 4 MPam(sup 1/2) at 1400 C for HfB(sub 2)-SiC composites. Thus, the toughnesses of either the HS or ZS composites have the potential for use in thermal shock applications. Processing and manufacturing defects limited the strength of the test bars. However, examination of the microstructure on the fracture surfaces shows that the processing of these composites can be improved. There is potential for high toughness composites with high strength to be used in thermal shock conditions if the processing and handling are controlled

  13. Formation, structure, and phonon confinement effect of nanocrystalline Si1-xGex in SiO2-Si-Ge cosputtered films

    International Nuclear Information System (INIS)

    Yang, Y.M.; Wu, X.L.; Siu, G.G.; Huang, G.S.; Shen, J.C.; Hu, D.S.

    2004-01-01

    Using magnetron cosputtering of SiO 2 , Ge, and Si targets, Si-based SiO 2 :Ge:Si films were fabricated for exploring the influence of Si target proportion (P Si ) and annealing temperature (Ta) on formation, local structure, and phonon properties of nanocrystalline Si 1-x Ge x (nc-Si 1-x Ge x ). At low P Si and Ta higher than 800 deg. C, no nc-Si 1-x Ge x but a kind of composite nanocrystal consisting of a Ge core, GeSi shell, and amorphous Si outer shell is formed in the SiO 2 matrix. At moderate P Si , nc-Si 1-x Ge x begins to be formed at Ta=800 deg. C and coexists with nc-Ge at Ta=1100 deg. C. At high P Si , it was disclosed that both optical phonon frequency and lattice spacing of nc-Si 1-x Ge x increase with raising Ta. The possible origin of this phenomenon is discussed by considering three factors, the phonon confinement, strain effect, and composition variation of nc-Si 1-x Ge x . This work will be helpful in understanding the growth process of ternary GeSiO films and beneficial to further investigations on optical properties of nc-Ge 1-x Si x in the ternary matrix

  14. Spherical NiO-C composite for anode material of lithium ion batteries

    International Nuclear Information System (INIS)

    Huang, X.H.; Tu, J.P.; Zhang, C.Q.; Chen, X.T.; Yuan, Y.F.; Wu, H.M.

    2007-01-01

    Spherical NiO-C composite was prepared by dispersing spherical NiO in glucose solution and subsequent carbonization under hydrothermal conditions at 180 o C. The microstructure and morphology of the NiO-C and NiO powders were characterized by means of X-ray diffraction (XRD) and scanning electron microscopy (SEM). The electrochemical properties of the electrodes were measured by galvanostatic charge-discharge tests, cyclic voltammetric analysis (CV), and electrochemical impedance spectroscopy (EIS). SEM images showed that the amorphous carbon not only coated on the surface but also filled the inner pores of the NiO spheres. Electrochemical tests showed that the NiO-C composite exhibited higher initial coulombic efficiency (66.6%) than NiO (56.4%), and better cycling performances. The improvement of these properties is attributed to the carbon, as it can reduce the specific surface area of porous sphere, and enhance the conductivity of porous NiO

  15. The characteristics of photo-CVD SiO{sub 2} and its application on SiC MIS UV photodetectors

    Energy Technology Data Exchange (ETDEWEB)

    Liu, C.H.; Chang, C.S.; Chang, S.J.; Su, Y.K.; Chiou, Y.Z.; Liu, S.H.; Huang, B.R

    2003-07-15

    SiO{sub 2} layers were deposited onto SiC by photo-chemical vapor deposition (photo-CVD) using deuterium (D{sub 2}) lamp as the excitation source. For the photo-SiO{sub 2} deposited 500 deg. C, interface state density (D{sub it}) was estimated to be 5.66x10{sup 11} cm{sup -2} eV{sup -1}. With an applied electric field of 4 MV cm{sup -1}, it was found that the leakage current was only 3.15x10{sup -8} A cm{sup -2} for the photo-CVD SiO{sub 2} layer prepared at 500 deg. C. It was also found that photo-SiO{sub 2} could effectively suppress dark current of SiC-based photodetectors (PDs). It was found that we could reduce dark current of SiC-based PDs by about three orders of magnitude by the insertion of a 5 nm-thick photo-CVD SiO{sub 2} film in between Indium-tin-oxide (ITO) contact and the underneath SiC. Photocurrent to dark current ratio of ITO/SiO{sub 2}/SiC MIS PDs was also found to be much larger than that of conventional ITO/SiC Schottky barrier PDs.

  16. New High-Performance SiC Fiber Developed for Ceramic Composites

    Science.gov (United States)

    DiCarlo, James A.; Yun, Hee Mann

    2002-01-01

    Sylramic-iBN fiber is a new type of small-diameter (10-mm) SiC fiber that was developed at the NASA Glenn Research Center and was recently given an R&D 100 Award for 2001. It is produced by subjecting commercially available Sylramic (Dow Corning, Midland, MI) SiC fibers, fabrics, or preforms to a specially designed high-temperature treatment in a controlled nitrogen environment for a specific time. It can be used in a variety of applications, but it currently has the greatest advantage as a reinforcement for SiC/SiC ceramic composites that are targeted for long-term structural applications at temperatures higher than the capability of metallic superalloys. The commercial Sylramic SiC fiber, which is the precursor for the Sylramic-iBN fiber, is produced by Dow Corning, Midland, Michigan. It is derived from polymers at low temperatures and then pyrolyzed and sintered at high temperatures using boron-containing sintering aids (ref. 1). The sintering process results in very strong fibers (>3 GPa) that are dense, oxygen-free, and nearly stoichiometric. They also display an optimum grain size that is beneficial for high tensile strength, good creep resistance, and good thermal conductivity (ref. 2). The NASA-developed treatment allows the excess boron in the bulk to diffuse to the fiber surface where it reacts with nitrogen to form an in situ boron nitride (BN) coating on the fiber surface (thus the product name of Sylramic-iBN fiber). The removal of boron from the fiber bulk allows the retention of high tensile strength while significantly improving creep resistance and electrical conductivity, and probably thermal conductivity since the grains are slightly larger and the grain boundaries cleaner (ref. 2). Also, as shown in the graph, these improvements allow the fiber to display the best rupture strength at high temperatures in air for any available SiC fiber. In addition, for CMC applications under oxidizing conditions, the formation of an in situ BN surface layer

  17. Deposition of stress free c-axis oriented LiNbO3 thin film grown on (002) ZnO coated Si substrate

    International Nuclear Information System (INIS)

    Shandilya, Swati; Gupta, Vinay; Tomar, Monika

    2012-01-01

    C-axis oriented lithium niobate thin films have been deposited on Si substrate using RF sputtering technique. A thin buffer layer of c-axis (002) oriented ZnO on Si substrate has been used as a nucleating layer to promote the growth of (006) oriented LiNbO 3 film. The processing gas composition and pressure are found to be very critical in obtaining stress free LiNbO 3 film having desired (006) orientation. The LiNbO 3 films deposited under unique combination of sputtering pressure (10 mTorr) and argon percentage (80%) in reactive gas (Ar + O 2 ) composition become almost stress free having lattice parameter (1.3867 A) close to the bulk value. The observed variation in the structural properties and optical phonon modes observed by Raman spectroscopic studies of the oriented LiNbO 3 thin film with stress has been correlated with growth kinetics.

  18. Nd{sup 3+}-doped colloidal SiO{sub 2} composite abrasives: Synthesis and the effects on chemical mechanical polishing (CMP) performances of sapphire wafers

    Energy Technology Data Exchange (ETDEWEB)

    Liu, Tingting; Lei, Hong, E-mail: hong_lei2005@aliyun.com

    2017-08-15

    higher material removal rate (MRR) than the pure colloidal SiO{sub 2} abrasives in the same polishing conditions, which was attributed to the solid-state chemical reactions between shells of Nd{sup 3+}-doped colloidal SiO{sub 2} composite abrasives and sapphire.

  19. C-H and C-C activation of n -butane with zirconium hydrides supported on SBA15 containing N-donor ligands: [(≡SiNH-)(≡SiX-)ZrH2], [(≡SiNH-)(≡SiX-)2ZrH], and[(≡SiN=)(≡SiX-)ZrH] (X = -NH-, -O-). A DFT study

    KAUST Repository

    Pasha, Farhan Ahmad; Bendjeriou-Sedjerari, Anissa; Huang, Kuo-Wei; Basset, Jean-Marie

    2014-01-01

    : [(≡SiNH-)(≡SiO-)ZrH2] (A), [(≡SiNH-)2ZrH2] (B), [(≡SiNH-)(≡SiO-) 2ZrH] (C), [(≡SiNH-)2(≡SiO-)ZrH] (D), [(≡SiN=)(≡Si-O-)ZrH] (E), and [(≡SiN=)(≡SiNH-)ZrH] (F). The roles of these hydrides have been investigated in C-H/C-C bond activation and cleavage

  20. Electrosynthesis of Ti5Si3, Ti5Si3/TiC, and Ti5Si3/Ti3SiC2 from Ti-Bearing Blast Furnace Slag in Molten CaCl2

    Science.gov (United States)

    Li, Shangshu; Zou, Xingli; Zheng, Kai; Lu, Xionggang; Chen, Chaoyi; Li, Xin; Xu, Qian; Zhou, Zhongfu

    2018-04-01

    Ti5Si3, Ti5Si3/TiC, and Ti5Si3/Ti3SiC2 have been electrochemically synthesized from the Ti-bearing blast furnace slag/TiO2 and/or C mixture precursors at a cell voltage of 3.8 V and 1223 K to 1273 K (950 °C to 1000 °C) in molten CaCl2. The pressed porous mixture pellets were used as the cathode, and a solid oxide oxygen-ion-conducting membrane (SOM)-based anode was used as the anode. The phase composition and morphologies of the cathodic products were systematically characterized. The final products possess a porous nodular microstructure due to the interconnection of particles. The variations of impurity elements, i.e., Ca, Mg, and Al, have been analyzed, and the result shows that Ca and Mg can be almost completely removed; however, Al cannot be easily removed from the pellet due to the formation of Ti-Al alloys during the electroreduction process. The electroreduction process has also been investigated by the layer-depended phase composition analysis of the dipped/partially reduced pellets to understand the detailed reaction process. The results indicate that the electroreduction process of the Ti-bearing blast furnace slag/TiO2 and/or C mixture precursors can be typically divided into four periods, i.e., (i) the decomposition of initial Ca(Mg,Al)(Si,Al)2O6, (ii) the reduction of Ti/Si-containing intermediate phases, (iii) the removal of impurity elements, and (iv) the formation of Ti5Si3, TiC, and Ti3SiC2. It is suggested that the SOM-based anode process has great potential to be used for the direct and facile preparation of Ti alloys and composites from cheap Ti-containing ores.