WorldWideScience

Sample records for showing silicon ingot

  1. Impurity segregation behavior in polycrystalline silicon ingot grown with variation of electron-beam power

    Science.gov (United States)

    Lee, Jun-Kyu; Lee, Jin-Seok; Jang, Bo-Yun; Kim, Joon-Soo; Ahn, Young-Soo; Cho, Churl-Hee

    2014-08-01

    Electron beam melting (EBM) systems have been used to improve the purity of metallurgical grade silicon feedstock for photovoltaic application. Our advanced EBM system is able to effectively remove volatile impurities using a heat source with high energy from an electron gun and to continuously allow impurities to segregate at the top of an ingot solidified in a directional solidification (DS) zone in a vacuum chamber. Heat in the silicon melt should move toward the ingot bottom for the desired DS. However, heat flux though the ingot is changed as the ingot becomes longer due to low thermal conductivity of silicon. This causes a non-uniform microstructure of the ingot, finally leading to impurity segregation at its middle. In this research, EB power irradiated on the silicon melt was controlled during the ingot growth in order to suppress the change of heat flux. EB power was reduced from 12 to 6.6 kW during the growth period of 45 min with a drop rate of 0.125 kW/min. Also, the silicon ingot was grown under a constant EB power of 12 kW to estimate the effect of the drop rate of EB power. When the EB power was reduced, the grains with columnar shape were much larger at the middle of the ingot compared to the case of constant EB power. Also, the present research reports a possible reason for the improvement of ingot purity by considering heat flux behaviors.

  2. Determination of impurity distributions in ingots of solar grade silicon by neutron activation analysis

    Energy Technology Data Exchange (ETDEWEB)

    Karches, Barbara; Hampel, Gabriele; Plonka, Christian; Stieghorst, Christian; Wiehl, Norbert [Mainz Univ. (Germany). Inst. for Nuclear Chemistry; Schoen, Jonas; Krenckel, Patricia; Riepe, Stephan [Fraunhofer Institute for Solar Energy Systems, Freiburg (Germany); Gerstenberg, Heiko [Technische Univ. Muenchen, Garching (Germany). Heinz-Maier-Leibniz Zentrum; Ponsard, Bernard [Belgian Nuclear Research Centre (SCK CEN), Mol (Belgium). BR2 reactor

    2017-09-01

    In a series of crystallization experiments, the directional solidification of silicon was investigated as a low cost path for the production of silicon wafers for solar cells. Instrumental neutron activation analysis was employed to measure the influence of different crystallization parameters on the distribution of 3d-metal impurities of the produced ingots. A theoretical model describing the involved diffusion and segregation processes during the solidification and cooling of the ingots could be verified by the experimental results. By successive etching of the samples after the irradiation, it could be shown that a layer of at least 60 μm of the samples has to be removed to get real bulk concentrations.

  3. Influence of additional heat exchanger block on directional solidification system for growing multi-crystalline silicon ingot - A simulation investigation

    Science.gov (United States)

    Nagarajan, S. G.; Srinivasan, M.; Aravinth, K.; Ramasamy, P.

    2018-04-01

    Transient simulation has been carried out for analyzing the heat transfer properties of Directional Solidification (DS) furnace. The simulation results revealed that the additional heat exchanger block under the bottom insulation on the DS furnace has enhanced the control of solidification of the silicon melt. Controlled Heat extraction rate during the solidification of silicon melt is requisite for growing good quality ingots which has been achieved by the additional heat exchanger block. As an additional heat exchanger block, the water circulating plate has been placed under the bottom insulation. The heat flux analysis of DS system and the temperature distribution studies of grown ingot confirm that the established additional heat exchanger block on the DS system gives additional benefit to the mc-Si ingot.

  4. Influence of Crucible Thermal Conductivity on Crystal Growth in an Industrial Directional Solidification Process for Silicon Ingots

    Directory of Open Access Journals (Sweden)

    Zaoyang Li

    2016-01-01

    Full Text Available We carried out transient global simulations of heating, melting, growing, annealing, and cooling stages for an industrial directional solidification (DS process for silicon ingots. The crucible thermal conductivity is varied in a reasonable range to investigate its influence on the global heat transfer and silicon crystal growth. It is found that the crucible plays an important role in heat transfer, and therefore its thermal conductivity can influence the crystal growth significantly in the entire DS process. Increasing the crucible thermal conductivity can shorten the time for melting of silicon feedstock and growing of silicon crystal significantly, and therefore large thermal conductivity is helpful in saving both production time and power energy. However, the high temperature gradient in the silicon ingots and the locally concave melt-crystal interface shape for large crucible thermal conductivity indicate that high thermal stress and dislocation propagation are likely to occur during both growing and annealing stages. Based on the numerical simulations, some discussions on designing and choosing the crucible thermal conductivity are presented.

  5. Metal impurities profile in a 450kg multi-crystalline silicon ingot by Cold Neutron Prompt Gamma-ray Activation Analysis

    International Nuclear Information System (INIS)

    Baek, Hani; Sun, Gwang Min; Kim, Ji seok; Oh, Mok; Chung, Yong Sam; Moon, Jong Hwa; Kim, Sun Ha; Baek, Sung Yeol; Tuan, Hoang Sy Minh

    2014-01-01

    Metal impurities are harmful to multi-crystalline silicon solar cells. They reduce solar cell conversion efficiencies through increased carrier recombination. They are present as isolated point-like impurities or precipitates. This work is to study the concentration profiles of some metal impurities of the directionally solidified 450kg multi-crystalline silicon ingot grown for solar cell production. The concentration of such impurities are generally below 10 15 cm -3 , and as such cannot be detected by physical techniques such as secondary-ion-mass spectroscopy(SIMS). So, we have tried to apply Cold Neutron - Prompt Gamma ray Activation Analysis(CN-PGAA) at the HANARO reactor research. The impurity concentrations of Au, Mn, Pt, Mo of a photovoltaic grade multi-crystalline silicon ingot appear by segregation from the liquid to the solid phase in the central region of the ingot during the crystallization. In the impurities concentration of the bottom region is higher than middle region due to the solid state diffusion. Towards the top region the segregation impurities diffused, during cooling process

  6. Silicon Ingot Casting - Heat Exchanger Method (HEM). Multi-Wire Slicing - Fixed Abrasive Slicing Technique (Fast). Phase 4 Silicon Sheet Growth Development for the Large Area Sheet Task of the Low-Cost Solar Array Project

    Science.gov (United States)

    Schmid, F.

    1981-01-01

    The crystallinity of large HEM silicon ingots as a function of heat flow conditions is investigated. A balanced heat flow at the bottom of the ingot restricts spurious nucleation to the edge of the melted-back seed in contact with the crucible. Homogeneous resistivity distribution over all the ingot has been achieved. The positioning of diamonds electroplated on wirepacks used to slice silicon crystals is considered. The electroplating of diamonds on only the cutting edge is described and the improved slicing performance of these wires evaluated. An economic analysis of value added costs of HEM ingot casting and band saw sectioning indicates the projected add on cost of HEM is well below the 1986 allocation.

  7. Numerical analysis of thermal stress and dislocation density distributions in large size multi-crystalline silicon ingots during the seeded growth process

    Science.gov (United States)

    Nguyen, Thi Hoai Thu; Chen, Jyh-Chen; Hu, Chieh; Chen, Chun-Hung; Huang, Yen-Hao; Lin, Huang-Wei; Yu, Andy; Hsu, Bruce

    2017-06-01

    In this study, a global transient numerical simulation of silicon growth from the beginning of the solidification process until the end of the cooling process is carried out modeling the growth of an 800 kg ingot in an industrial seeded directional solidification furnace. The standard furnace is modified by the addition of insulating blocks in the hot zone. The simulation results show that there is a significant decrease in the thermal stress and dislocation density in the modified model as compared to the standard one (a maximal decrease of 23% and 75% along the center line of ingot for thermal stress and dislocation density, respectively). This modification reduces the heating power consumption for solidification of the silicon melt by about 17% and shortens the growth time by about 2.5 h. Moreover, it is found that adjusting the operating conditions of modified model to obtain the lower growth rate during the early stages of the solidification process can lower dislocation density and total heater power.

  8. Fast Pulling of n-Type Si Ingots for Enhanced Si Solar Cell Production

    Science.gov (United States)

    Kim, Kwanghun; Park, Sanghyun; Park, Jaechang; Pang, Ilsun; Ryu, Sangwoo; Oh, Jihun

    2018-03-01

    Reducing the manufacturing costs of silicon substrates is an important issue in the silicon-based solar cell industry. In this study, we developed a high-throughput ingot growth method by accelerating the pulling speed in the Czochralski process. By controlling the heat flow of the ingot growth chamber and at the solid-liquid interfaces, the pulling speed of an ingot could be increased by 15% compared to the conventional method, while retaining high quality. The wafer obtained at a high pulling speed showed an enhanced minority carrier lifetime compared with conventional wafers, due to the vacancy passivation effect, and also demonstrated comparable bulk resistivity and impurities. The results in this work are expected to open a new way to enhance the productivity of Si wafers used for Si solar cells, and therefore, to reduce the overall manufacturing cost.

  9. Fiscal 2000 achievement report. Research and development of fast-acting innovative energy-environment technology (Development of fast-acting high-efficiency solar cell technology - Development of high-quality ingot manufacturing technology); 2000 nendo shin energy sangyo gijutsu sogo kaihatsu kiko itaku kenkyu gyomu seika hokokusho. Sokkoteki kakushinteki energy kankyo gijutsu kenkyu kaihatsu (Sokkogata kokoritsu taiyo denchi gijutsu kaihatsu - Kohinshitsu ingot seizo gijutsu kaihatsu)

    Energy Technology Data Exchange (ETDEWEB)

    NONE

    2001-03-01

    Research and development was conducted of a technology for manufacturing an ultrathin polycrystalline silicon solar cell capable of efficiency enhancement and cost reduction earlier than the types of polycrystalline solar cells now available on the market. In this fiscal year, a silicon melt/solidification experimenting apparatus was built for manufacturing high-quality silicon ingots. Using an apparatus with its performance similar to the newly built one, a preliminary experiment was conducted involving high-purity silicon ingot manufacturing. In the experiment, boron was added to 75 kg of silicon for semiconductor devices so that its resistivity may be 0.5 ohm-cm. The silicon was melted in a quartz mold, and then subjected to unidirectional coagulation at 0.13 mm/min that started at the bottom to proceed upward. The result was a silicon ingot 44 cm times 44 cm times 17 cm (height). The ingot thus obtained exhibited 0.4-0.8 ohm-cm in resistivity distribution. Solar cells produced from the ingot showed a conversion rate of 16.9%. (NEDO)

  10. Effect of annealing temperature on the thermal stress and dislocation density of mc-Si ingot grown by DS process for solar cell application

    Science.gov (United States)

    Sanmugavel, S.; Srinivasan, M.; Aravinth, K.; Ramasamy, P.

    2018-04-01

    90% of the solar industries are using crystalline silicon. Cost wise the multi-crystalline silicon solar cells are better compared to mono crystalline silicon. But because of the presence of grain boundaries, dislocations and impurities, the efficiency of the multi-crystalline silicon solar cells is lower than that of mono crystalline silicon solar cells. By reducing the defect and dislocation we can achieve high conversion efficiency. The velocity of dislocation motion increases with stress. By annealing the grown ingot at proper temperature we can decrease the stress and dislocation. Our simulation results show that the value of stress and dislocation density is decreased by annealing the grown ingot at 1400K and the input parameters can be implemented in real system to grow a better mc-Si ingot for energy harvesting applications.

  11. Improving the Quality of the Deteriorated Regions of Multicrystalline Silicon Ingots during General Solar Cell Processes

    International Nuclear Information System (INIS)

    Wu Shan-Shan; Wang Lei; Yang De-Ren

    2011-01-01

    The behavior of wafers and solar cells from the border of a multicrystalline silicon (mc-Si) ingot, which contain deteriorated regions, is investigated. It is found that the diffusion length distribution of minority carriers in the cells is uniform, and high efficiency of the solar cells (about 16%) is achieved. It is considered that the quality of the deteriorated regions could be improved to be similar to that of adjacent regions. Moreover, it is indicated that during general solar cell fabrication, phosphorus gettering and hydrogen passivation could significantly improve the quality of deteriorated regions, while aluminum gettering by RTP could not. Therefore, it is suggested that the border of a mc-Si ingot could be used to fabricate high efficiency solar cells, which will increase mc-Si utilization effectively. (condensed matter: structure, mechanical and thermal properties)

  12. Quality Management for Neutron Transmutation Doping of Silicon Ingot in HANARO

    Energy Technology Data Exchange (ETDEWEB)

    Kang, Ki-Doo; Kim, Ji-Uk; Yun, Hwa-Kyung; Lim, Chul-Hong; Kim, Young-Chil; Kim, Myong-Seop; Park, Sang-Jun [Korea Atomic Energy Research Institute, Daejeon (Korea, Republic of)

    2007-10-15

    By using this doping method, silicon semiconductors with extremely uniform dopant distributions can be produced, and this is the dominant advantage of NTD compared with a conventional chemical doping. Good uniformity of a dopant concentration is usually required for high power applications such as thyristor (SCR), IGBT, IGCT and GTO and for special sensors. Achieving an accurate neutron fluence corresponding to a target resistivity as well as a uniform irradiation is the prime target of a neutron irradiation for NTD. Generally, in order to reach an accurate neutron fluence, a real time neutron flux is monitored by a neutron detector such as a Self-powered Neutron Detector(SPND). And, after an irradiation, the total irradiation fluence is confirmed by measuring the absolute activity of a neutron activation sample that has been irradiated with a silicon ingot, and thus the SPND can be properly calibrated. Excellent irradiation uniformity and a high accuracy for a target neutron dose have been achieved from the early works of NTD. However, to maintain this excellent quality, the neutron irradiation fluence should be continuously modified and controlled. So, in this work, an activity to maintain the irradiation quality is introduced.

  13. Low cost monocrystalline silicon sheet fabrication for solar cells by advanced ingot technology

    Science.gov (United States)

    Fiegl, G. F.; Bonora, A. C.

    1980-01-01

    The continuous liquid feed (CLF) Czochralski furnace and the enhanced I.D. slicing technology for the low-cost production of monocrystalline silicon sheets for solar cells are discussed. The incorporation of the CLF system is shown to improve ingot production rate significantly. As demonstrated in actual runs, higher than average solidification rates (75 to 100 mm/hr for 150 mm 1-0-0 crystals) can be achieved, when the system approaches steady-state conditions. The design characteristics of the CLF furnace are detailed, noting that it is capable of precise control of dopant impurity incorporation in the axial direction of the crystal. The crystal add-on cost is computed to be $11.88/sq m, considering a projected 1986 25-slice per cm conversion factor with an 86% crystal growth yield.

  14. Silicon Ingot Casting - Heat Exchanger Method Multi-wire Slicing - Fixed Abrasive Slicing Technique. Phase 3 Silicon Sheet Growth Development for the Large Area Sheet Task of the Low-cost Solar Array Project

    Science.gov (United States)

    Schmid, F.; Khattak, C. P.

    1979-01-01

    Several 20 cm diameter silicon ingots, up to 6.3 kg. were cast with good crystallinity. The graphite heat zone can be purified by heating it to high temperatures in vacuum. This is important in reducing costs and purification of large parts. Electroplated wires with 45 um synthetic diamonds and 30 um natural diamonds showed good cutting efficiency and lifetime. During slicing of a 10 cm x 10 cm workpiece, jerky motion occurred in the feed and rocking mechanisms. This problem is corrected and modifications were made to reduce the weight of the bladeheat by 50%.

  15. Continuous Czochralski growth: Silicon sheet growth development of the large area sheet task of the low cost silicon solar array project

    Science.gov (United States)

    Johnson, C. M.

    1980-12-01

    The growth of 100 kg of silicon single crystal material, ten cm in diameter or greater, and 150 kg of silicon single crystal material 15 cm or greater utilizing one common silicon container material (one crucible) is investigated. A crystal grower that is recharged with a new supply of polysilicon material while still under vacuum and at temperatures above the melting point of silicon is developed. It accepts large polysilicon charges up to 30 kg, grows large crystal ingots (to 15 cm diameter and 25 kg in weight), and holds polysilicon material for recharging (rod or lump) while, at the same time, growing crystal ingots. Special equipment is designed to recharge polysilicon rods, recharge polysilicon lumps, and handle and store large, hot silicon crystal ingots. Many continuous crystal growth runs were performed lasting as long as 109 hours and producing as many as ten crystal ingots, 15 cm with weights progressing to 27 kg.

  16. Design Concept of Kijang Research Reactor for Neutron Transmutation Doping of 300 MM ingots

    International Nuclear Information System (INIS)

    Jun, B. J.; Kim, H. S.; Seo, C. G.; Kim, H. C.; Lee, B. C.

    2013-01-01

    Neutron transmutation doping will be one of the important utilization areas of the Kijang research reactor, which is currently under design. The reactor will serve for at least 50 years. As the diameter of a current NTD ingot is already large compared to the size of the reactor, unless a provision in the reactor design is specifically made for the irradiation of potential larger diameter ingots in the future, the lifetime sustainability of the NTD activity, if possible, may be difficult to achieve. While 200 mm became the largest diameter of NTD wafers a few years ago, 300 mm is the majority nowadays in the silicon semiconductor market, and one of the world leading device companies recently invested in the construction of a 450 mm fabrication plant. The usual peak time of a wafer diameter has been around 12 years. Though the generation gap of a NTD wafer diameter has become longer as time has passed, we can foresee that NTD demand for 300 mm ingots will arise within 20 years if their NTD is possible. Our calculations show that the radial uniformity for the 300 mm ingot irradiation may be acceptable by wafer companies. However, the NTD for 450 mm ingots is judged as impractical. The KJRR is designed to irradiate 6' and 200 mm ingots to accommodate the major demands in the current and near future markets. We suppose that a 6' irradiation facility will be modified into a 300 mm irradiation facility when the demand for a 300 mm NTD arises. As the demand for the 300 mm NTD increases, other 6' and 200 mm NTD facilities will be modified one by one. A minimization of the component replacement and long-lived radwaste and a facilitation of the replacement work for each modification are important factors along with a better performance of NTD facilities

  17. Primary Structure and Mechanical Properties of AlSi2 Alloy Continuous Ingots

    Directory of Open Access Journals (Sweden)

    Wróbel T.

    2017-06-01

    Full Text Available The paper presents the research results of horizontal continuous casting of ingots of aluminium alloy containing 2% wt. silicon (AlSi2. Together with the casting velocity (velocity of ingot movement we considered the influence of electromagnetic stirring in the area of the continuous casting mould on refinement of the ingot’s primary structure and their selected mechanical properties, i.e. tensile strength, yield strength, hardness and elongation. The effect of primary structure refinement and mechanical properties obtained by electromagnetic stirring was compared with refinement obtained by using traditional inoculation, which consists in introducing additives, i.e. Ti, B and Sr, to the metal bath. On the basis of the obtained results we confirmed that inoculation done by electromagnetic stirring in the range of the continuous casting mould guarantees improved mechanical properties and also decreases the negative influence of casting velocity, thus increasing the structure of AlSi2 continuous ingots.

  18. Recent developments in multi-wire fixed abrasive slicing technique (FAST). [for low cost silicon wafer production from ingots

    Science.gov (United States)

    Schmid, F.; Khattak, C. P.; Smith, M. B.; Lynch, L. D.

    1982-01-01

    Slicing is an important processing step for all technologies based on the use of ingots. A comparison of the economics of three slicing techniques shows that the fixed abrasive slicing technique (FAST) is superior to the internal diameter (ID) and the multiblade slurry (MBS) techniques. Factors affecting contact length are discussed, taking into account kerf width, rocking angle, ingot size, and surface speed. Aspects of blade development are also considered. A high concentration of diamonds on wire has been obtained in wire packs usd for FAST slicing. The material removal rate was found to be directly proportional to the pressure at the diamond tips.

  19. Effect of impurities and processing on silicon solar cells. Volume 1: Characterization methods for impurities in silicon and impurity effects data base

    Science.gov (United States)

    Hopkins, R. H.; Davis, J. R.; Rohatgi, A.; Campbell, R. B.; Blais, P. D.; Rai-Choudhury, P.; Stapleton, R. E.; Mollenkopf, H. C.; Mccormick, J. R.

    1980-01-01

    Two major topics are treated: methods to measure and evaluate impurity effects in silicon and comprehensive tabulations of data derived during the study. Discussions of deep level spectroscopy, detailed dark I-V measurements, recombination lifetime determination, scanned laser photo-response, conventional solar cell I-V techniques, and descriptions of silicon chemical analysis are presented and discussed. The tabulated data include lists of impurity segregation coefficients, ingot impurity analyses and estimated concentrations, typical deep level impurity spectra, photoconductive and open circuit decay lifetimes for individual metal-doped ingots, and a complete tabulation of the cell I-V characteristics of nearly 200 ingots.

  20. The status of silicon ribbon growth technology for high-efficiency silicon solar cells

    Science.gov (United States)

    Ciszek, T. F.

    1985-01-01

    More than a dozen methods have been applied to the growth of silicon ribbons, beginning as early as 1963. The ribbon geometry has been particularly intriguing for photovoltaic applications, because it might provide large area, damage free, nearly continuous substrates without the material loss or cost of ingot wafering. In general, the efficiency of silicon ribbon solar cells has been lower than that of ingot cells. The status of some ribbon growth techniques that have achieved laboratory efficiencies greater than 13.5% are reviewed, i.e., edge-defined, film-fed growth (EFG), edge-supported pulling (ESP), ribbon against a drop (RAD), and dendritic web growth (web).

  1. Correlation of NTD-silicon rod and slice resistivity

    International Nuclear Information System (INIS)

    Wolverton, W.M.

    1984-01-01

    Neutron transmutation doped silicon is an electronic material which presents an opportunity to explore a high level of resistivity characterization. This is due to its excellent uniformity of dopant concentration. Appropriate resistivity measurements on the ingot raw material can be used as a predictor of slice resistivity. Correlation of finished NTD rod (i.e. ingot) resistivity to as-cut slice resistivity (after the sawing process) is addressed in the scope of this paper. Empirical data show that the shift of slice-center resistivity compared to rod-end center resistivity is a function of a new kind of rod radial-resistivity gradient. This function has two domains, and most rods are in domain ''A''. Correlating equations show how to significantly improve the prediction of slice resistivity of rods in domain ''A''. The new rod resistivity specifications have resulted in manufacturing economies in the production of NTD silicon slices

  2. Process design and simulation for optimizing the oxygen concentration in Czochralski-grown single-crystal silicon

    International Nuclear Information System (INIS)

    Jung, Y. J.; Kim, W. K.; Jung, J. H.

    2014-01-01

    The highest-concentration impurity in a single-crystal silicon ingot is oxygen, which infiltrates the ingot during growth stage. This oxygen adversely affects the wafer is quality. This study was aimed at finding an optimal design for the Czochralski (Cz) process to enable high-quality and low cost (by reducing power consumption) wafer production by controlling the oxygen concentration in the silicon ingots. In the Cz process, the characteristics of silicon ingots during crystallization are greatly influenced by the design and the configuration of the hot zone, and by crystallization rate. In order to identify process conditions for obtaining an optimal oxygen concentration of 11 - 13 ppma (required for industrial-grade ingots), designed two shield shapes for the hot zone. Furthermore, oxygen concentrations corresponding to these two shapes were compared by evaluating each shape at five different production speeds. In addition, simulations were performed to identify the optimal shield design for industrial applications.

  3. Process design and simulation for optimizing the oxygen concentration in Czochralski-grown single-crystal silicon

    Energy Technology Data Exchange (ETDEWEB)

    Jung, Y. J.; Kim, W. K.; Jung, J. H. [Yeungnam University, Gyeongsan (Korea, Republic of)

    2014-08-15

    The highest-concentration impurity in a single-crystal silicon ingot is oxygen, which infiltrates the ingot during growth stage. This oxygen adversely affects the wafer is quality. This study was aimed at finding an optimal design for the Czochralski (Cz) process to enable high-quality and low cost (by reducing power consumption) wafer production by controlling the oxygen concentration in the silicon ingots. In the Cz process, the characteristics of silicon ingots during crystallization are greatly influenced by the design and the configuration of the hot zone, and by crystallization rate. In order to identify process conditions for obtaining an optimal oxygen concentration of 11 - 13 ppma (required for industrial-grade ingots), designed two shield shapes for the hot zone. Furthermore, oxygen concentrations corresponding to these two shapes were compared by evaluating each shape at five different production speeds. In addition, simulations were performed to identify the optimal shield design for industrial applications.

  4. Dehydrogenation in large ingot casting process

    International Nuclear Information System (INIS)

    Ubukata, Takashi; Suzuki, Tadashi; Ueda, Sou; Shibata, Takashi

    2009-01-01

    Forging components (for nuclear power plants) have become larger and larger because of decreased weld lines from a safety point of view. Consequently they have been manufactured from ingots requirement for 200 tons or more. Dehydrogenation is one of the key issues for large ingot manufacturing process. In the case of ingots of 200 tons or heavier, mold stream degassing (MSD) has been applied for dehydrogenation. Although JSW had developed mold stream degassing by argon (MSD-Ar) as a more effective dehydrogenating practice, MSD-Ar was not applied for these ingots, because conventional refractory materials of a stopper rod for the Ar blowing hole had low durability. In this study, we have developed a new type of stopper rod through modification of both refractory materials and the stopper rod construction and have successfully expanded the application range of MSD-Ar up to ingots weighting 330 tons. Compared with the conventional MSD, the hydrogen content in ingots after MSD-Ar has decreased by 24 percent due to the dehydrogenation rate of MSD-Ar increased by 34 percent. (author)

  5. Characterization of HEM silicon for solar cells. [Heat Exchanger Method

    Science.gov (United States)

    Dumas, K. A.; Khattak, C. P.; Schmid, F.

    1981-01-01

    The Heat Exchanger Method (HEM) is a promising low-cost ingot casting process for material used for solar cells. This is the only method that is capable of casting single crystal ingots with a square cross section using a directional solidification technique. This paper describes the chemical, mechanical and electrical properties of the HEM silicon material as a function of position within the ingot.

  6. Laser process for extended silicon thin film solar cells

    International Nuclear Information System (INIS)

    Hessmann, M.T.; Kunz, T.; Burkert, I.; Gawehns, N.; Schaefer, L.; Frick, T.; Schmidt, M.; Meidel, B.; Auer, R.; Brabec, C.J.

    2011-01-01

    We present a large area thin film base substrate for the epitaxy of crystalline silicon. The concept of epitaxial growth of silicon on large area thin film substrates overcomes the area restrictions of an ingot based monocrystalline silicon process. Further it opens the possibility for a roll to roll process for crystalline silicon production. This concept suggests a technical pathway to overcome the limitations of silicon ingot production in terms of costs, throughput and completely prevents any sawing losses. The core idea behind these thin film substrates is a laser welding process of individual, thin silicon wafers. In this manuscript we investigate the properties of laser welded monocrystalline silicon foils (100) by micro-Raman mapping and spectroscopy. It is shown that the laser beam changes the crystalline structure of float zone grown silicon along the welding seam. This is illustrated by Raman mapping which visualizes compressive stress as well as tensile stress in a range of - 147.5 to 32.5 MPa along the welding area.

  7. Vacuum induction melting of uranium ingots

    International Nuclear Information System (INIS)

    Hussain, M.M.; Bagchi, S.N.; Singh, S.P.

    1992-01-01

    Massive uranium ingot is produced from green salt (UF 4 ) using calciothermic reduction (CTR) or magnesiothermic reduction (MTR) process. CTR process has been replaced by MTR process at Trombay due to economic considerations. This paper highlights problems associated with the vacuum induction melting of MTR ingots and the remedial measures taken to produce good quality billets. Details of metallographic examination of inclusions in ingots and billets have been incorporated. (author). 3 figs

  8. Towards solar grade silicon: Challenges and benefits for low cost photovoltaics

    Energy Technology Data Exchange (ETDEWEB)

    Pizzini, Sergio [Ned Silicon Spa, Via Th. Edison 6, 60027 Osimo (Ancona) (Italy)

    2010-09-15

    It is well known that silicon in its various structural configurations (single crystal, multicrystalline, amorphous, micro-nanocrystalline) supplies almost 90% of the substrates used in the photovoltaic industry. It is also known, since years, that the photovoltaic (PV) industry shows a marked growth trend, which demanded and demands a continuous, huge increase of the bulk silicon supply in the order of 30%/yr. In order to fulfill their today- and future needs, many companies worldwide took the decision to start the installation of many thousand tons/year plants, most of them using the Siemens process, some of them using the MG route, to produce the so called solar grade (SG) silicon. The advantages of the Siemens process are well known, as it provides ultrapure silicon, directly usable for growing either single crystalline Czochralski ingots or multicrystalline ingots using the directional solidification (DS) technique. The disadvantages are its high energetic cost (a minimum of 120 kWH/kg) and the possible losses of chlorinated gases in the atmosphere, with possible severe environmental problems. The advantages of the MG route are still potential, as there is no commercially available production of solar silicon as yet, and rely on its reduced energetic costs (a maximum of 25-30 kWh/kg) for a feedstock directly usable for growing multicrystalline ingots using the DS technique. The drawbacks of silicon of MG origin are its larger concentration of metallic impurities, as compared with the Siemens one, the higher B and P content, and the potentially high carbon content. The aim of this paper is to deal with some of the problems encountered so far with the silicon of MG origin with respect to the metallic and non-metallic impurities content, as well as to propose technologically feasible solar grade feedstock specifications. (author)

  9. Process Characterization of Electrical Discharge Machining of Highly Doped Silicon

    Science.gov (United States)

    2012-06-01

    of mechanism is shown in Figure 2 showing the wire feed panel where the spool of 5 (DiBitonto, et...Uno High efficiency boring of monocrystalline silicon ingot by EDM RAM Si (P-type) conductivity 0.01 ohm-cm 1mm Cu pipe electrode, rotating at

  10. Modelling of defects in ingot forging

    DEFF Research Database (Denmark)

    Christiansen, Peter

    The present report presents an investigation of the ingot forging process with special emphasis on modelling the influence of die geometry on the soundness of the ingot after hot forging. An investigation on how to model damage is also performed. The influence of the lower die angle is quantified...... angle of 130o-140o giving rise to the largest centreline porosity closure regardless of material hardening behaviour applied. Friction was found only to have minor influence on the optimum. Multi stroke forging operations have also been modelled since the ingot forging process consists of many forging...... damage. It is found that when evaluating damage only by relative density; feed size and lower die angle does not influence whether the hot forging process is successful or not. This is in disagreement with the general understanding of the ingot forging process. When evaluating ductile damage...

  11. Zircaloy 4 ingots' industrial fabrication

    International Nuclear Information System (INIS)

    Leyt, A.

    1987-01-01

    The technology developed for the industrial fabrication of Zircaloy-4 ingots is presented. According to the results obtained: a) the homogeneity of the ingots is analyzed, regarding the distribution of components (tin, iron, chromium, oxygen) and Brinell hardness as a function of different types of charge: zirconium sponge-recycling alloy material, sponge of zirconium-alloy; b) the distribution of the same parameters as a function of production is also analyzed. (Author)

  12. Feasibility study on silicon doping using high temperature test engineering reactor

    International Nuclear Information System (INIS)

    Seki, Masaya; Takaki, Naoyuki; Goto, Minoru; Shimakawa, Satoshi

    2011-01-01

    The feasibility study on silicon doping using the High Temperature engineering Test Reactor (HTTR) is performed by numerical simulations. The HTTR is a High Temperature Gas-cooled Reactor (HTGR) situated at JAEA Oarai research and development center. It has a 30MW thermal power and the outlet coolant temperature is 950degC. The objective of this study is to evaluate the following issues, 1. The impact of loading Si-ingots into the core on the criticality, 2. The uniformity of the neutron capture reaction rate in Si-ingots, and 3. The production rate of silicon semiconductor. In this study, six Si-ingots are loaded into the irradiation area which is located in the peripheral region of the core. They are irradiated with rotation movement around the axial direction to obtain uniform neutron capture reaction rate in the radial direction. Additionally, the neutron filter, which is made of graphite containing boron, is used to obtain uniform neutron capture reaction rate in the axial direction. The evaluations were conducted by performing the HTTR whole core calculations with the Monte Carlo code MVP-2.0. In the calculations, several tally regions were defined on the Si-ingots to investigate the uniformity of the neutron capture reaction rate. As a result, loading the Si-ingots into the core causes negative reactivity by about 0.7%dk/k. Uniform neutron capture reaction rate of Si-ingot is obtained 98% in the radial and the axial direction. In case of the target of semiconductor resistivity is set to 50 Ωcm, the required irradiation time becomes 10 hours. The HTTR is able to produce silicon semiconductor of 540kg in one-time irradiation. This study was conducted as a joint research with JAEA, Nuclear Fuel Industries, LTD, Toyota Tsusho Corporation and Tokai University. (author)

  13. Flat-plate solar array project. Volume 3: Silicon sheet: Wafers and ribbons

    Science.gov (United States)

    Briglio, A.; Dumas, K.; Leipold, M.; Morrison, A.

    1986-01-01

    The primary objective of the Silicon Sheet Task of the Flat-Plate Solar Array (FSA) Project was the development of one or more low cost technologies for producing silicon sheet suitable for processing into cost-competitive solar cells. Silicon sheet refers to high purity crystalline silicon of size and thickness for fabrication into solar cells. Areas covered in the project were ingot growth and casting, wafering, ribbon growth, and other sheet technologies. The task made and fostered significant improvements in silicon sheet including processing of both ingot and ribbon technologies. An additional important outcome was the vastly improved understanding of the characteristics associated with high quality sheet, and the control of the parameters required for higher efficiency solar cells. Although significant sheet cost reductions were made, the technology advancements required to meet the task cost goals were not achieved.

  14. Application of neutron transmutation doping method to initially p-type silicon material.

    Science.gov (United States)

    Kim, Myong-Seop; Kang, Ki-Doo; Park, Sang-Jun

    2009-01-01

    The neutron transmutation doping (NTD) method was applied to the initially p-type silicon in order to extend the NTD applications at HANARO. The relationship between the irradiation neutron fluence and the final resistivity of the initially p-type silicon material was investigated. The proportional constant between the neutron fluence and the resistivity was determined to be 2.3473x10(19)nOmegacm(-1). The deviation of the final resistivity from the target for almost all the irradiation results of the initially p-type silicon ingots was at a range from -5% to 2%. In addition, the burn-up effect of the boron impurities, the residual (32)P activity and the effect of the compensation characteristics for the initially p-type silicon were studied. Conclusively, the practical methodology to perform the neutron transmutation doping of the initially p-type silicon ingot was established.

  15. Numerical simulation of convection and inclusion distribution during solidification in a heavy steel ingot

    International Nuclear Information System (INIS)

    Lin, Rui; Shen, Houfa

    2015-01-01

    Inclusions content in the steel ingot is an important index for homogeneity, and it becomes more serious for heavy steel ingots which are used for major equipment. However, knowledge about the formation of inclusion in steel ingot is limited, and modeling of inclusion distribution is still challenging, so it is of great significance to research the behavior of inclusion. In this paper, fluid flow during solidification is numerically simulated based on the equilibrium equations of mass, momentum and energy, and then inclusion distribution is modeled according to the Lagrangian Stokes trajectory method. The Results show that the inclusion distribution in the steel ingot is influenced by the flow pattern which is affected by the solidification pattern. Therefore, inclusion distribution could be controlled by the solidification front with the optimization of heat transfer condition such as the hot top design of steel ingot for the high quality steel production. (paper)

  16. Study of hot cracking potential in a 6-ton steel ingot casting

    Science.gov (United States)

    Yang, Jing'an; Liu, Baicheng; Shen, Houfa

    2018-04-01

    A new hot cracking potential (HCP) criterion, for the appearance of hot tearing in steel ingot castings, is proposed. The maximum value of the first principal stress, divided by the dynamic yield strength in the brittle temperature range (BTR), was used to identify the HCP. Experiments were carried out on a 6-ton P91 steel ingot in which severe hot tearing was detected in the upper centerline. Another ingot, with a better heat preservation riser, and without hot tearing, was used for comparison. Samples were obtained from the area of the ingot body with hot tearing, and their morphologies were inspected by a X-ray high energy industrial computed tomography. The carbon and sulfur distributions around the hot tearing were characterized by an infrared spectrometry carbon and sulfur analyzer. High temperature mechanical properties were obtained by a Gleeble thermal simulation machine, under different strain rates. Then, thermo-mechanical simulations using an elasto-viscoplastic finite-element model were conducted to analyze the stress and strain evolution during ingot solidification. The results showed that the hot tearing area, which was rich in both carbon and sulfur, was under excessive tensile stress in the BTR, bearing the highest HCP.

  17. Radiometric study of creep in ingot rolling

    International Nuclear Information System (INIS)

    Kubicek, P.; Zamyslovsky, Z.; Uherek, J.

    The radiometric study of creep during ingot rolling performed in the rolling mill of the Vitkovice Iron and Steel Works and the first results are described. Selected sites in 3 to 8 ton ingots were labelled with 2 to 3.7x10 5 Bq of 60 Co and after rolling into blocks, the transposition of the labelled sites of the ingots was investigated. The results indicate creep during rolling, local extension in certain sites under study and help to determine the inevitable bottom crop incurred in the forming. Finally, the requirements put on the radiometric apparatus for the next stages of technological research are presented. (author)

  18. Aerosol-assisted extraction of silicon nanoparticles from wafer slicing waste for lithium ion batteries.

    Science.gov (United States)

    Jang, Hee Dong; Kim, Hyekyoung; Chang, Hankwon; Kim, Jiwoong; Roh, Kee Min; Choi, Ji-Hyuk; Cho, Bong-Gyoo; Park, Eunjun; Kim, Hansu; Luo, Jiayan; Huang, Jiaxing

    2015-03-30

    A large amount of silicon debris particles are generated during the slicing of silicon ingots into thin wafers for the fabrication of integrated-circuit chips and solar cells. This results in a significant loss of valuable materials at about 40% of the mass of ingots. In addition, a hazardous silicon sludge waste is produced containing largely debris of silicon, and silicon carbide, which is a common cutting material on the slicing saw. Efforts in material recovery from the sludge and recycling have been largely directed towards converting silicon or silicon carbide into other chemicals. Here, we report an aerosol-assisted method to extract silicon nanoparticles from such sludge wastes and their use in lithium ion battery applications. Using an ultrasonic spray-drying method, silicon nanoparticles can be directly recovered from the mixture with high efficiency and high purity for making lithium ion battery anode. The work here demonstrated a relatively low cost approach to turn wafer slicing wastes into much higher value-added materials for energy applications, which also helps to increase the sustainability of semiconductor material and device manufacturing.

  19. Production of High Quality Die Steels from Large ESR Slab Ingots

    Science.gov (United States)

    Geng, Xin; Jiang, Zhou-hua; Li, Hua-bing; Liu, Fu-bin; Li, Xing

    With the rapid development of manufacture industry in China, die steels are in great need of large slab ingot of high quality and large tonnage, such as P20, WSM718R and so on. Solidification structure and size of large slab ingots produced with conventional methods are not satisfied. However, large slab ingots manufactured by ESR process have a good solidification structure and enough section size. In the present research, the new slab ESR process was used to produce the die steels large slab ingots with the maximum size of 980×2000×3200mm. The compact and sound ingot can be manufactured by the slab ESR process. The ultra-heavy plates with the maximum thickness of 410 mm can be obtained after rolling the 49 tons ingots. Due to reducing the cogging and forging process, the ESR for large slab ingots process can increase greatly the yield and production efficiency, and evidently cut off product costs.

  20. Effects of the ingot phase transition on microstructure and magnetic properties of CeNdFeB melt-spun ribbons

    Energy Technology Data Exchange (ETDEWEB)

    Wang, Xuchao [Division of Functional Materials Research, Central Iron and Steel Research Institute, Beijing 100081, China (China); College of Sciences, Northeastern University, Shenyang 110819 (China); Zhu, Minggang, E-mail: mgzhu@126.com [Division of Functional Materials Research, Central Iron and Steel Research Institute, Beijing 100081, China (China); Li, Wei; Zheng, Liyun; Guo, Zhaohui; Du, Xiao [Division of Functional Materials Research, Central Iron and Steel Research Institute, Beijing 100081, China (China); Du, An [College of Sciences, Northeastern University, Shenyang 110819 (China)

    2015-11-01

    The paper studies the phase transition of ingot with the composition (Ce{sub 50}Nd{sub 50}){sub 30}Fe{sub bal}Co{sub 4}Ga{sub 0.2}B{sub 0.92} after the annealing treatment at 1050 °C. The melt-spun ribbons which is prepared by the two treatment status ingots. The phase structure and microstructure morphologies of the ingots and melt-spun ribbons were analysed and observed by XRD and SEM. It was found that the grain size of the ribbons is on the nanometer scale. The EDS results show that there are four different phases in the ingot: (CeNd){sub 2}Fe{sub 14}B, α-Fe, Ce-rich phase and Nd-rich phase. After the annealing treatment, α-Fe, Ce-rich phase, and Nd-rich phase were obviously reduced and the contents of the main phase was significantly increased in the annealed ingot compared with the unanneal treatment ingot. The VSM results show that there is a peak waist in the ribbon which is prepared by the untreated ingot. Because the ingot is uneven, the ribbons may have the secondary phase, the Hcj is 8394 Oe. But the demagnetization curves of the ribbons, which is prepared by the annealed ingot, is relatively smooth and without the soft magnetic phase and the Hcj is 12,528 Oe, which is higher than the unanneal treatment ingot. We can know that the ingot with fine organization is the key factors to preparing high-performance ribbons.

  1. Development of advanced Czochralski Growth Process to produce low cost 150 KG silicon ingots from a single crucible for technology readiness

    Science.gov (United States)

    1981-01-01

    The goals in this program for advanced czochralski growth process to produce low cost 150 kg silicon ingots from a single crucible for technology readiness are outlined. To provide a modified CG2000 crystal power capable of pulling a minimum of five crystals, each of approximately 30 kg in weight, 150 mm diameter from a single crucible with periodic melt replenishment. Crystals to have: resistivity of 1 to 3 ohm cm, p-type; dislocation density below 1- to the 6th power per cm; orientation (100); after growth yield of greater than 90%. Growth throughput of greater than 2.5 kg per hour of machine operation using a radiation shield. Prototype equipment suitable for use as a production facility. The overall cost goal is $.70 per peak watt by 1986. To accomplish these goals, the modified CG2000 grower and development program includes: (1) increased automation with a microprocessor based control system; (2) sensors development which will increase the capability of the automatic controls system, and provide technology transfer of the developed systems.

  2. Remelt Ingot Production Technology

    Science.gov (United States)

    Grandfield, J. F.

    The technology related to the production of remelt ingots (small ingots, sows and T-Bar) is reviewed. Open mold conveyors, sow casting, wheel and belt casting and VDC and HDC casting are described and compared. Process economics, capacity, product quality and process problems are listed. Trends in casting machine technology such as longer open mold conveyor lines are highlighted. Safety issues related to the operation of these processes are discussed. The advantages and disadvantages of the various machine configurations and options e.g. such as dry filling with the mold out of water and wet filling with the mold in water for open mould conveyors are discussed. The effect of mold design on machine productivity, mold cracking and mold life is also examined.

  3. Operation of arc heating furnace on manufacturing gigantic ingots and segregation of gigantic ingots

    International Nuclear Information System (INIS)

    Niimi, Takayasu; Okamura, Masayoshi

    1976-01-01

    The techniques and procedure for manufacturing gigantic ingots heavier than 200 t are described. Especially, practical results of an arc heating furnace which plays an important role in the procedure and segregation of gigantic ingots are discussed in detail. By appropriate operations of the arc heating furnance, hydrogen and phosphorus are kept unchanged, and oxygen and sulphur decrease to very low levels. Furthermore, the temperature can be accurately controlled. The application of multipour technique reduces segregation and its degree is dependent on kinds of steel. V-segregation and inverted V-segregation in steel deoxidized with carbon in vacuum seem to be very slight. (auth.)

  4. Development of the external cooling device of increase the productivity of neutron-transmutation-doped silicon semiconductor (NTD-Si) (Joint research)

    International Nuclear Information System (INIS)

    Hirose, Akira; Wada, Shigeru; Sasajima, Fumio; Kusunoki, Tsuyoshi; Kameyama, Iwao; Aizawa, Ryouji; Kikuchi, Naoyuki

    2007-01-01

    Neutron-Transmutation-Doped Silicon Semiconductor (hereinafter referred as 'NTD-Si') is the best semiconductor for the power device. The needs of NTD-Si increase recently in proportion to the popularization of hybrid-cars. A fission research reactor, which is a steady state neutron source, is being expected as the best device to meet the needs. So far, we have reconsidered the existing approach which is employed for NTD-Si production works at the research reactors JRR-3, JRR-4 and JMTR of JAEA so as to meet the needs. As one of the effective measures, we found out that the productivity can be increased by incorporating a new device to cool down radioactivity of irradiated silicon ingots at the place outside the main stream from the loading of silicon ingots to the withdrawal of irradiated ingots to the existing JRR-3 Uniformity Irradiation System. Consequently, we developed and installed the device (hereinafter referred as 'external cooling device'). After an ingot was irradiated once, it is turned over manually and irradiated again in order to irradiate the ingot uniformly. With the conventional system, it was necessary to wait the radioactivity of ingot decrease less than the permissible level with holding the ingot in the irradiation equipment. It was effective to shorten the waiting period by using an external cooling device for production increase of NTD-Si. It is expected that the productivity of NTD-Si will be increased by using the external cooling device. This report mentions the design of the external cooling device and verification between its design specifications and the performance of the device completed. (author)

  5. Development of low-cost silicon crystal growth techniques for terrestrial photovoltaic solar energy conversion

    Science.gov (United States)

    Zoutendyk, J. A.

    1976-01-01

    Because of the growing need for new sources of electrical energy, photovoltaic solar energy conversion is being developed. Photovoltaic devices are now being produced mainly from silicon wafers obtained from the slicing and polishing of cylindrically shaped single crystal ingots. Inherently high-cost processes now being used must either be eliminated or modified to provide low-cost crystalline silicon. Basic to this pursuit is the development of new or modified methods of crystal growth and, if necessary, crystal cutting. If silicon could be grown in a form requiring no cutting, a significant cost saving would potentially be realized. Therefore, several techniques for growth in the form of ribbons or sheets are being explored. In addition, novel techniques for low-cost ingot growth and cutting are under investigation.

  6. Analysis of internal crack in a six-ton P91 ingot

    Directory of Open Access Journals (Sweden)

    Jing-an Yang

    2016-05-01

    Full Text Available P91 is a new kind of heat-resistant and high-tensile steel. It can be extruded after ingot casting and can be widely used for different pipes in power plants. However, due to its mushy freezing characteristics, a lack of feeding in the ingot center often generates many defects, such as porosity and crack. A six-ton P91 ingot was cast and sliced, and a representative part of the longitudinal section was inspected in more detail. The morphology of crack-like defects was examined by X-ray high energy industrial CT and reconstructed by 3D software. There are five main portions of defects larger than 200 mm3, four of which are interconnected. These initiated from continuous liquid film, and then were torn apart by excessive tensile stress within the brittle temperature range (BTR. The 3D FEM analysis of thermo-mechanical simulation was carried out to analyze the formation of porosity and internal crack defects. The results of shrinkage porosity and Niyama values revealed that the center of the ingot suffers from inadequate feeding. Several criteria based on thermal and mechanical models were used to evaluate the susceptibility of hot crack formation. The Clyne and Davies’ criterion and Katgerman’s criterion successfully predicted the high hot crack susceptibility in the ingot center. Six typical locations in the longitudinal section had been chosen for analysis of the stresses and strains evolution during the BTR. Locations in the defects region showed the highest tensile stresses and relative high strain values, while other locations showed either low tensile stresses or low strain values. In conclusion, hot crack develops only when stress and strain exceed a threshold value at the same time during the BTR.

  7. Microstructures and constituents of super-high strength aluminum alloy ingots made through LFEC process

    Directory of Open Access Journals (Sweden)

    WANG Shuang

    2007-11-01

    Full Text Available Ingots of a new super-high strength Al-Zn-Mg-Cu-Zr alloy were produced respectively by low frequency electromagnetic casting (LFEC and by conventional direct chill (DC casting process. Microstructure and constituents of the ingots were studied. The results indicated that the LFEC process significantly refines microstructure and constituents of the alloy, and to some extent, decreases the area (or volume fraction of constituents and eutectic structure precipitated at grain boundaries. But, no difference in the type of constituents was observed between LFEC and DC ingots. The results also showed LFEC process can improve the as-cast mechanical properties.

  8. Kinetics of steel heavy ingot formation in dies of semicontinuous-casting machines

    International Nuclear Information System (INIS)

    Tsukerman, V.Ya.; Marchenko, I.K.

    1986-01-01

    Formation kinetics of round section ingot of up to 0.67 m in diameter was analyzed in dies of semicontinuous-casting machines on casting of the most usable assortment steels: medium-carbon low-alloyed and chromium-nickel stainless steels. It is established that solidification coefficient decreases in direct proportion to ingot diameter. Value of different-thickness ingot skin at die outlet is in direct proportion to a casted steel overheating temperature, ingot diameter and inversely proportional to the number and diameter of holes in a ladder nozzle and square root of ingot drawing rate

  9. Structural Transformations Versus Hard Particles Motion in the Brass Ingots

    Directory of Open Access Journals (Sweden)

    Wołczyński W.

    2017-12-01

    Full Text Available A mathematical method for the forecast of the type of structure in the steel static ingot has been recently developed. Currently, the method has been applied to structural zones prediction in the brass ingots obtained by the continuous casting. Both the temperature field and thermal gradient field have been calculated in order to predict mathematically the existence of some structural zones in the solidifying brass ingot. Particularly, the velocity of the liquidus isotherm movement and thermal gradient behavior versus solidification time have been considered. The analysis of the mentioned velocity allows the conclusion that the brass ingots can evince: chilled columnar grains-, (CC, fine columnar grains-, (FC, columnar grains-, (C, equiaxed grains zone, (E, and even the single crystal, (SC, situated axially. The role of the mentioned morphologies is analyzed to decide whether the hard particles existing in the brass ingots can be swallowed or rejected by the solid / liquid (s/l interface of a given type of the growing grains. It is suggested that the columnar grains push the hard particles to the end of a brass ingot during its continuous casting.

  10. Modelling of macrosegregation in steel ingots: benchmark validation and industrial application

    International Nuclear Information System (INIS)

    Li Wensheng; Shen Houfa; Liu Baicheng; Shen Bingzhen

    2012-01-01

    The paper presents the recent progress made by the authors on modelling of macrosegregation in steel ingots. A two-phase macrosegregation model was developed that incorporates descriptions of heat transfer, melt convection, solute transport, and solid movement on the process scale with microscopic relations for grain nucleation and growth. The formation of pipe shrinkage at the ingot top is also taken into account in the model. Firstly, a recently proposed numerical benchmark test of macrosegregation was used to verify the model. Then, the model was applied to predict the macrosegregation in a benchmark industrial-scale steel ingot. The predictions were validated against experimental data from the literature. Furthermore, macrosegregation experiment of an industrial 53-t steel ingot was performed. The simulation results were compared with the measurements. It is indicated that the typical macrosegregation patterns encountered in steel ingots, including a positively segregated zone in the hot top and a negative segregation in the bottom part of the ingot, are well reproduced with the model.

  11. Report on achievements in fiscal 1999. Research and development of immediately effective and innovative energy environment technology (Development of immediately effective and high-efficiency solar cell technology, development of high-quality ingot manufacturing technology, and development of high-efficiency cell making technology); 1999 nendo sokkoteki kakushinteki energy kankyo gijutsu kenkyu kaihatsu seika hokokusho. Sokkogata kokoritsu taiyo denchi gijutsu kaihatsu (kohinshitsu ingot seizo gijutsu kaihatsu / kohinshitsu cell ka gijutsu kaihatsu)

    Energy Technology Data Exchange (ETDEWEB)

    NONE

    2000-03-01

    Research and development has been made on improving quality of ingots for substrates, manufacturing high-quality thin type substrates, and making high-efficiency cells. This paper summarizes the achievements in fiscal 1999. In developing the high-quality ingot manufacturing technology, discussions were given on a method for assessing impurities and crystal defects by using the total reflection scattering type infrared tomography, and on the optimal solidifying and cooling conditions during the ingot manufacturing by using simulation calculation for solidification. As a result of analyses and discussions, such findings were found effective that the ingot should be solidified through making the solid-liquid interface shape flat, and the temperature falling rate in an ingot should be maintained constant. In developing the high-efficiency cell making technology, discussions were given on the optimal construction based on a simulation that assumes the light sealing structure using the RIE method, and on the optimal construction of polycrystalline silicon solar cells by using a device simulator (PCID). The important factors in achieving a conversion efficiency of 20% are the light sealing structure, surface passivation, and substrate thickness. (NEDO)

  12. Formation and growth of crystal defects in directionally solidified multicrystalline silicon for solar cells

    Energy Technology Data Exchange (ETDEWEB)

    Ryningen, Birgit

    2008-07-01

    Included in this thesis are five publications and one report. The common theme is characterisation of directionally solidified multicrystalline silicon for solar cells. Material characterisation of solar cell silicon is naturally closely linked to both the casting process and to the solar cell processing: Many of the material properties are determined by the casting process, and the solar cell processing will to some extend determine which properties will influence the solar cell performance. Solar grade silicon (SoG-Si) made by metallurgical refining route and supplied by Elkem Solar was directionally solidified and subsequently characterised, and a simple solar cell process was applied. Except from some metallic co-precipitates in the top of the ingot, no abnormalities were found, and it is suggested that within the limits of the tests performed in this thesis, the casting and the solar cell processing, rather than the assumed higher impurity content, was the limiting factor. It is suggested in this thesis that the main quality problem in multicrystalline silicon wafers is the existence of dislocation clusters covering large wafer areas. The clusters will reduce the effect of gettering and even if gettering could be performed successfully, the clusters will still reduce the minority carrier mobility and hence the solar cell performance. It has further been pointed out that ingots solidified under seemingly equal conditions might have a pronounced difference in minority carrier lifetime. Ingots with low minority carrier lifetime have high dislocation densities. The ingots with the substantially higher lifetime seem all to be dominated by twins. It is also found a link between a higher undercooling and the ingots dominated by twins. It is suggested that the two types of ingots are subject to different nucleation and crystal growth mechanisms: For the ingots dominated by dislocations, which are over represented, the crystal growth is randomly nucleated at the

  13. Towards graphite-free hot zone for directional solidification of silicon

    Science.gov (United States)

    Dropka, Natasha; Buchovska, Iryna; Herrmann-Geppert, Iris; Klimm, Detlef; Kiessling, Frank M.; Degenhardt, Ulrich

    2018-06-01

    The reduction of SiC, Si3N4 and transition metals impurities in directionally solidified Si ingots poses one of the crucial challenges in the solar cells production. Particularly strong contamination comes from the graphite parts in the hot zone. Therefore, we selected three massive ceramic materials to replace graphite, developed the novel design of the crucible support and cover and compared the crystals grown in them with ingots from the standard graphite design. The experiments were performed for phosphorus n-doped silicon of G0 size. The ingots were compared with respect to O- and C-content, metal impurities, resistivity and lifetime. The superior performance of TiC relative to other ceramics was observed, particularly due to the lower concentration of substitutional carbon in Si ingot (up to 2.6 times) and the higher minority carrier lifetime of (up to 4.4 times) with narrow red zones.

  14. Report on achievements in fiscal 1999. Development of energy usage rationalizing silicon manufacturing process (Development of manufacturing technology for mass production of silicon for solar cells); 1999 nendo energy shiyo gorika silicon seizo process kaihatsu seika hokokusho. Taiyo denchiyo silicon ryosanka seizo gijutsu no kaihatsu

    Energy Technology Data Exchange (ETDEWEB)

    NONE

    2000-03-01

    Discussions were given on manufacture of raw material silicon for solar cells with regard to boron removal, solidification, finishing and refining of metallic impurities, refining of unutilized silicon scraps, and making them into wafers and solar cells after refining. This paper summarizes the achievements in fiscal 1999. With regard to purity deterioration due to contamination by boron containing silica powder generated during the boron removal in the manufacturing process, the facilities were modified resulting in the reduction thereof to 0.04 ppmw or less. Regarding the repetitive use of boron removing crucibles, the experiment identified the possibility of using them for more than three times. In trial fabrication of samples by using the solidification refining and cast integrated process, ingots of 550 mm square and about 300 mm high were obtained, which were sliced into 10-cm square materials for use as wafers. Measurement of the conversion efficiency has resulted in 13% or more which is almost equivalent in the center and edges of the ingot. It was revealed that solar cell wafers may be fabricated by using this process, which can use either the p-type low-resistance silicon scraps or the metallic silicon as the starting material. (NEDO)

  15. Large-Scale PV Module Manufacturing Using Ultra-Thin Polycrystalline Silicon Solar Cells: Annual Subcontract Report, 1 October 2003--30 September 2004

    Energy Technology Data Exchange (ETDEWEB)

    Wohlgemuth, J.; Narayanan, M.

    2005-03-01

    The major objectives of this program are to continue the advancement of BP Solar polycrystalline silicon manufacturing technology. The program includes work in the following areas: Efforts in the casting area to increase ingot size, improve ingot material quality, and improve handling of silicon feedstock as it is loaded into the casting stations; developing wire saws to slice 100- m-thick silicon wafers on 290- m centers; developing equipment for demounting and subsequent handling of very thin silicon wafers; developing cell processes using 100- m-thick silicon wafers that produce encapsulated cells with efficiencies of at least 15.4% at an overall yield exceeding 95%; expanding existing in-line manufacturing data reporting systems to provide active process control; establishing a 50-MW (annual nominal capacity) green-field Mega-plant factory model template based on this new thin polycrystalline silicon technology; facilitating an increase in the silicon feedstock industry's production capacity for lower-cost solar-grade silicon feedstock.

  16. Application of directional solidification ingot (LSD) in forging of PWR reactor vessel heads

    International Nuclear Information System (INIS)

    Benhamou, C.; Poitrault, I.

    1985-09-01

    Creusot-Loire Industrie uses this type of ingot for manufacture of Framatome 1300 and 1450 MW 4-loop PWR reactor vessel heads. This type of ingot offers a number advantages: improved internal soundness; greater chemical, structural and mechanical homogeneity of the finished part; simplified forging process. After a brief description of the pouring and solidification processes, this paper presents an analysis of the results of examinations performed on the prototype forging, as well as review of results obtained during industrial fabrication of dished heads from LSD ingots. The advantages of the LSD ingot over conventional ingots are discussed in conclusion

  17. Proposal of a neutron transmutation doping facility for n-type spherical silicon solar cell at high-temperature engineering test reactor.

    Science.gov (United States)

    Ho, Hai Quan; Honda, Yuki; Motoyama, Mizuki; Hamamoto, Shimpei; Ishii, Toshiaki; Ishitsuka, Etsuo

    2018-05-01

    The p-type spherical silicon solar cell is a candidate for future solar energy with low fabrication cost, however, its conversion efficiency is only about 10%. The conversion efficiency of a silicon solar cell can be increased by using n-type silicon semiconductor as a substrate. This study proposed a new method of neutron transmutation doping silicon (NTD-Si) for producing the n-type spherical solar cell, in which the Si-particles are irradiated directly instead of the cylinder Si-ingot as in the conventional NTD-Si. By using a 'screw', an identical resistivity could be achieved for the Si-particles without a complicated procedure as in the NTD with Si-ingot. Also, the reactivity and neutron flux swing could be kept to a minimum because of the continuous irradiation of the Si-particles. A high temperature engineering test reactor (HTTR), which is located in Japan, was used as a reference reactor in this study. Neutronic calculations showed that the HTTR has a capability to produce about 40t/EFPY of 10Ωcm resistivity Si-particles for fabrication of the n-type spherical solar cell. Copyright © 2018 Elsevier Ltd. All rights reserved.

  18. Microdefects in neutron-transmutationaly doped silicon

    International Nuclear Information System (INIS)

    Vysotskaya, V.V.; Gorin, S.N.; Gres'kov, I.M.; Sobolev, N.A.; Shek, E.I.

    1988-01-01

    Using the method of X-ray topography and high-voltage electron microscopy, the nature of microdefects and character of their changes in neutron-transmutationaly doped silicon depending on the sample prehistory and heat treatment (HT) conditions are refined. It is shown that the microstructure of neutron-transmutationaly doped dislocation-free silicon crystals depends on conditions of ingot growth and post-radiation annealing environment. Annealing in chlorine-containing atmosphere removes microdefects (MD), although in vacuum, argon or air growing MD are preserved and new MD are formed

  19. Microdefects in neutron-transmutationaly doped silicon

    Energy Technology Data Exchange (ETDEWEB)

    Vysotskaya, V V; Gorin, S N; Gres' kov, I M; Sobolev, N A; Shek, E I

    1988-03-01

    Using the method of X-ray topography and high-voltage electron microscopy, the nature of microdefects and character of their changes in neutron-transmutationaly doped silicon depending on the sample prehistory and heat treatment (HT) conditions are refined. It is shown that the microstructure of neutron-transmutationaly doped dislocation-free silicon crystals depends on conditions of ingot growth and post-radiation annealing environment. Annealing in chlorine-containing atmosphere removes microdefects (MD), although in vacuum, argon or air growing MD are preserved and new MD are formed.

  20. Modeling and Optimization of Direct Chill Casting to Reduce Ingot Cracking

    Energy Technology Data Exchange (ETDEWEB)

    Das, Subodh K.

    2006-01-09

    reheating-cooling method (RCM), was developed and validated for measuring mechanical properties in the nonequilibrium mushy zones of alloys. The new method captures the brittle nature of aluminum alloys at temperatures close to the nonequilibrium solidus temperature, while specimens tested using the reheating method exhibit significant ductility. The RCM has been used for determining the mechanical properties of alloys at nonequilibrium mushy zone temperatures. Accurate data obtained during this project show that the metal becomes more brittle at high temperatures and high strain rates. (4) The elevated-temperature mechanical properties of the alloy were determined. Constitutive models relating the stress and strain relationship at elevated temperatures were also developed. The experimental data fit the model well. (5) An integrated 3D DC casting model has been used to simulate heat transfer, fluid flow, solidification, and thermally induced stress-strain during casting. A temperature-dependent HTC between the cooling water and the ingot surface, cooling water flow rate, and air gap were coupled in this model. An elasto-viscoplastic model based on high-temperature mechanical testing was used to calculate the stress during casting. The 3D integrated model can be used for the prediction of temperature, fluid flow, stress, and strain distribution in DC cast ingots. (6) The cracking propensity of DC cast ingots can be predicted using the 3D integrated model as well as thermodynamic models. Thus, an ingot cracking index based on the ratio of local stress to local alloy strength was established. Simulation results indicate that cracking propensity increases with increasing casting speed. The composition of the ingots also has a major effect on cracking formation. It was found that copper and zinc increase the cracking propensity of DC cast ingots. The goal of this Aluminum Industry of the Future (IOF) project was to assist the aluminum industry in reducing the incidence of stress

  1. "Silicon millefeuille": From a silicon wafer to multiple thin crystalline films in a single step

    Science.gov (United States)

    Hernández, David; Trifonov, Trifon; Garín, Moisés; Alcubilla, Ramon

    2013-04-01

    During the last years, many techniques have been developed to obtain thin crystalline films from commercial silicon ingots. Large market applications are foreseen in the photovoltaic field, where important cost reductions are predicted, and also in advanced microelectronics technologies as three-dimensional integration, system on foil, or silicon interposers [Dross et al., Prog. Photovoltaics 20, 770-784 (2012); R. Brendel, Thin Film Crystalline Silicon Solar Cells (Wiley-VCH, Weinheim, Germany 2003); J. N. Burghartz, Ultra-Thin Chip Technology and Applications (Springer Science + Business Media, NY, USA, 2010)]. Existing methods produce "one at a time" silicon layers, once one thin film is obtained, the complete process is repeated to obtain the next layer. Here, we describe a technology that, from a single crystalline silicon wafer, produces a large number of crystalline films with controlled thickness in a single technological step.

  2. Process and Information Tracking of Polycrystalline silicon Ingot for Solar Cell%铸锭多晶硅电池生产流程及信息跟踪

    Institute of Scientific and Technical Information of China (English)

    焦富强; 乔卉莹

    2014-01-01

    Si-based photovoltaic materials account for a large proportion in the field of new energy, in which polycrystalline silicon ingot for solar cell is the main type. Many procedures must be used for production of the poly-crystalline silicon solar cell, therefore, accurate recording and tracking information of stuff and procedures play an im-portant role in technical improvement. In this paper, process and information tracking of every procedure in produc-tion of polycrystalline silicon solar cell are discussed, and easy encountered problems in information tracking are ana-lyzed.%在新能源开发利用领域硅基光伏材料占有较大比重,其中铸锭多晶硅光伏电池是当前太阳能电池的主要品种。生产多晶硅电池需要经历众多的加工工序,准确有序记录和跟踪物料流向及各工序相关信息是工艺研究和技术改进的基础。就铸锭多晶硅电池片生产流程及各工序信息跟踪问题进行了论述,并对实施信息跟踪时易出现的问题进行了分析。

  3. Large-Scale PV Module Manufacturing Using Ultra-Thin Polycrystalline Silicon Solar Cells: Annual Subcontract Report, 1 April 2002--30 September 2003 (Revised)

    Energy Technology Data Exchange (ETDEWEB)

    Wohlgemuth, J.; Shea, S. P.

    2004-04-01

    The goal of BP Solar's Crystalline PVMaT program is to improve the present polycrystalline silicon manufacturing facility to reduce cost, improve efficiency, and increase production capacity. Key components of the program are: increasing ingot size; improving ingot material quality; improving material handling; developing wire saws to slice 100 ..mu..m thick silicon wafers on 200 ..mu..m centers; developing equipment for demounting and subsequent handling of very thin silicon wafers; developing cell processes using 100 ..mu..m thick silicon wafers that produce encapsulated cells with efficiencies of at least 15.4% at an overall yield exceeding 95%; expanding existing in-line manufacturing data reporting systems to provide active process control; establishing a 50 MW (annual nominal capacity) green-field Mega plant factory model template based on this new thin polycrystalline silicon technology; and facilitating an increase in the silicon feedstock industry's production capacity for lower-cost solar-grade silicon feedstock.

  4. Prediction of qualitative parameters of slab steel ingot using numerical modelling

    Directory of Open Access Journals (Sweden)

    M. Tkadlečková

    2016-07-01

    Full Text Available The paper describes the verification of casting and solidification of heavy slab ingot weighing 40 t from tool steel by means of numerical modelling with use of a finite element method. The pre-processing, processing and post-processing phases of numerical modelling are outlined. Also, the problems with determination of the thermodynamic properties of materials and with determination of the heat transfer between the individual parts of the casting system are discussed. The final porosity, macrosegregation and the risk of cracks were predicted. The results allowed us to use the slab ingot instead of the conventional heavy steel ingot and to improve the ratio, the chamfer and the external shape of the wall of the new design of the slab ingot.

  5. The Structural Evolution and Segregation in a Dual Alloy Ingot Processed by Electroslag Remelting

    Directory of Open Access Journals (Sweden)

    Yu Liu

    2016-12-01

    Full Text Available The structural evolution and segregation in a dual alloy made by electroslag remelting (ESR was investigated by various analytical techniques. The results show that the macrostructure of the ingot consists of two crystallization structures: one is a quite narrow, fine, equiaxed grain region at the edge and the other is a columnar grain region, which plays a leading role. The typical columnar structure shows no discontinuity between the CrMoV, NiCrMoV, and transition zones. The average secondary arm-spacing is coarsened from 35.3 to 49.2 μm and 61.5 μm from the bottom to the top of the ingot. The distinctive features of the structure are attributed to the different cooling conditions during the ESR process. The Ni, Cr, and C contents markedly increase in the transition zone (TZ and show a slight increase from the bottom to the top and from the surface to the center of the ESR ingot due to the partition ratios, gravity segregation, the thermal buoyancy flow, the solutal buoyancy flow, and the inward Lorentz force. Less dendrite segregation exists in the CrMoV zone and the transition zone due to a stronger cooling rate (11.1 and 4.5 °C/s and lower Cr and C contents. The precipitation of carbides was observed in the ingot due to a lower solid solubility of the carbon element in the α phase.

  6. Large-Scale PV Module Manufacturing Using Ultra-Thin Polycrystalline Silicon Solar Cells: Final Subcontract Report, 1 April 2002--28 February 2006

    Energy Technology Data Exchange (ETDEWEB)

    Wohlgemuth, J.; Narayanan, M.

    2006-07-01

    The major objectives of this program were to continue advances of BP Solar polycrystalline silicon manufacturing technology. The Program included work in the following areas. (1) Efforts in the casting area to increase ingot size, improve ingot material quality, and improve handling of silicon feedstock as it is loaded into the casting stations. (2) Developing wire saws to slice 100-..mu..m-thick silicon wafers on 290-..mu..m-centers. (3) Developing equipment for demounting and subsequent handling of very thin silicon wafers. (4) Developing cell processes using 100-..mu..m-thick silicon wafers that produce encapsulated cells with efficiencies of at least 15.4% at an overall yield exceeding 95%. (5) Expanding existing in-line manufacturing data reporting systems to provide active process control. (6) Establishing a 50-MW (annual nominal capacity) green-field Mega-plant factory model template based on this new thin polycrystalline silicon technology. (7) Facilitating an increase in the silicon feedstock industry's production capacity for lower-cost solar-grade silicon feedstock..

  7. The characterization of high quality multicrystalline silicon by the electron beam induced current method

    International Nuclear Information System (INIS)

    Chen, J; Sekiguchi, T; Nara, S; Yang, D

    2004-01-01

    Multicrystalline silicon (mc-Si) manufactured by a multi-stage solidification control casting method has been characterized by the electron beam induced current (EBIC) method. The average diffusion length of the ingot was over 250 μm, which was much longer than that of conventional mc-Si. The EBIC study revealed that the electrical activities of grain boundaries (GBs) varied with the ingot position due to the impurity contamination level. The main impurity detected was iron. The concentration of iron in the central position was much lower than that at the bottom and top positions. GBs in the central position showed no significant EBIC contrast at 300 K, suggesting low contamination level. GBs in the top and bottom positions, however, showed strong EBIC contrast at 300 K, suggesting high contamination level. At 100 K, a denuded zone with bright contrast developed around GBs in the top and bottom positions. The existence of the denuded zone suggested that impurities were gettered at the GBs. It was considered that the variation of the diffusion length in the ingot was related to the variation of recombination activities of GBs in the different positions, which mainly depended on the impurity contamination

  8. Continuous Czochralski growth. Development of advanced Czochralski growth process to produce low cost 150 kg silicon ingots from a single crucible for technology readiness

    Science.gov (United States)

    The improvement of growth rates using radiation shielding and investigation of the crucible melt interaction for improved yields were emphasized. Growth runs were performed from both 15 and 16 inch diameter crucibles, producing 30 and 37 kg ingots respectively. Efforts to increase the growth rate of 150 mm diameter ingots were limited by temperature instabilities believed to be caused by undesirable thermal convections in the larger melts. The radiation shield improved the growth rate somewhat, but the thermal instability was still evident, leading to nonround ingots and loss of dislocation-free structure. A 38 kg crystal was grown to demonstrate the feasibility of producing 150 kg with four growth cycles. After the grower construction phase, the Hamco microprocessor control system was interfaced to the growth facility, including the sensor for automatic control of seeding temperature, and the sensor for automatic shouldering. Efforts focused upon optimization of the seeding, necking, and shoulder growth automation programs.

  9. Sequential purification and crystal growth for the production of low cost silicon substrates. Quarterly technical progress report No. 1, 15 September 1979-31 December 1979

    Energy Technology Data Exchange (ETDEWEB)

    Liaw, M.; Secco, F.; Ingle, B.; Down, D.

    1980-02-01

    Over the past several years, Motorola's Materials Technology Laboratory (MTL), has been conducting several projects with goals directed at the production of high quality low cost silicon crystals. One of the projects which is being investigated is the direct purification of MG-Si. A unique characteristic of the approach used by this project is the use of a crystal puller to perform both purification and crystal growth. Sequential steps of purification were taken. By the completion of this series of purification, the purified MG-Si melt will be further purified by impurity redistribution using ingot pulling. The final purified silicon will be in an ingot form of desired dimensions for slicing into silicon sheets. The sequential steps of purification include: (1) leaching of MG-Si charge, (2) phase separation, (3) reactive gas treatment, (4) liquid-liquid extraction (called Slagging), and (5) purification by redistribution of impurities using ingot pulling. Progress on items (1) and (2) is reported. (WHK)

  10. Development in fiscal 1998 of silicon manufacturing process to rationalize energy usage. Surveys and researches on analysis of practical application of technology to manufacture silicon raw materials for solar cells; 1998 nendo energy shiyo gorika silicon seizo process kaihatsu seika hokokusho. Taiyo denchi silicon genryo seizo gijutsu no jitsuyoka kaiseki ni kansuru chosa kenkyu

    Energy Technology Data Exchange (ETDEWEB)

    NONE

    1999-03-01

    With an objective to develop a mass production technology to manufacture silicon raw materials for solar cells, and assist its practical application, surveys and analyses were performed on trends in development of the related technologies, the problems therein , market trends and industrial trends thereof. This paper summarizes the achievements in fiscal 1998. The worldwide production amount of solar cells in 1998 is estimated to have achieved 150 MW, and the silicon consumption reached the level of 2,300 tons. In spite of the economic recession environment, there was no change in the expansion trend. In developing an SOG-Si mass production and manufacturing technology, construction of pilot plants for each process has been completed, and entered into the operation research phase. In developing a technology to manufacture high quality poly-crystalline silicon substrates, fabrication has been completed on the on-line ingot cutting equipment and the plasma heating equipment, and the stage is now in operation research of continuous electromagnetic casting process. The conversion efficiency of the poly-crystalline silicon solar cells is 14 to 16% at the mass production level, whose enhancement requires indispensably the improvement in quality of the substrate. Discussions are required on the ingot manufacturing conditions in coordination with improvement in the cell manufacturing technology. (NEDO)

  11. Numerical modelling of damage evolution in ingot forging

    DEFF Research Database (Denmark)

    Christiansen, Peter; Martins, Paulo A.F.; Bay, Niels Oluf

    2015-01-01

    The ingot forging process is numerically simulated applying both the Shima-Oyane porous plasticity model as a coupled damage model and the uncoupled normalized Cockcroft & Latham criterion. Four different cases including two different lower die angles (120º and 180º) and two different sizes of feed...... (400mm and 800mm) are analysed. Comparison of the simulation results with recommendations in literature on ingot forging, indicates the normalized Cockcroft & Latham damage criterion to be the most realistic of the two....

  12. Physical modeling and numerical simulation of V-die forging ingot with central void

    DEFF Research Database (Denmark)

    Christiansen, Peter; Hattel, Jesper Henri; Bay, Niels

    2014-01-01

    Numerical simulation and physical modeling performed on small-scale ingots made from pure lead, having a hole drilled through their centerline to mimic porosity, are utilized to characterize the deformation mechanics of a single open die forging compression stage and to identify the influence...... of the lower V-die angle on porosity closure and forging load requirements of large cast ingots. Results show that a lower V-die angle of 120 provides the best closure of centerline porosity without demanding the highest forging loads or developing unreasonably asymmetric shapes that may create difficulties...... in multi-stage open die forging procedures....

  13. Neutron transmutation doping of silicon in the SAFARI-1 research reactor

    International Nuclear Information System (INIS)

    Louw, P.A.; Robertson, D.G.; Strydom, W.J.

    1994-01-01

    The SAFARI-1 research reactor has operated with an exemplary safety record since commissioning in 1965. As part of a commercialisation effort a silicon irradiation facility (SILIRAD) has been installed in the poolside region of SAFARI-1 for Neutron Transmutation Doping (NTD) of silicon. Commissioning of the facility took place in the last quarter of 1992 with a series of trial irradiations which were performed in close collaboration with Wacker Chemitronic of Germany. A methodology for the determination of irradiation times necessary to achieve the target resistivities was verified on the basis of the results from the trial irradiations. All production activities are controlled by quality assurance procedures. To date some hundred and twelve silicon ingots (103 mm diameter) have been successfully irradiated on a commercial contract basis. The observed axial and radial variations in the resistivity profile of the ingots are very small compared to the profiles associated with conventionally doped silicon and small tolerances on target resistivities are attained. In this paper an overview of the design and characterisation of SILIRAD is given and the methods applied that ensure a quality product are described. Results obtained from trial and production irradiations are presented and the envisaged future modifications to SILIRAD discussed

  14. Neutron transmutation doping of silicon in the safari-1 research reactor

    International Nuclear Information System (INIS)

    Louw, P.A.; Robertson, D.G.; Strydom, W.J.

    1994-01-01

    The SAFARI-1 research reactor has operated with an exemplary safety record since commissioning in 1965. As part of a commercialisation effort a silicon irradiation facility (SILIRAD) has been installed in the poolside region of SAFARI-1 for Neutron Transmutation Doping (NTD) of silicon. Commissioning of the facility took place in the last quarter of 1992 with a series of trial irradiations which were performed in close collaboration the Wacker Chemitronic of Germany. A methodology for the determination of irradiation times necessary to achieve the target resistivities was verified on the basis of the results from the trial irradiations. All production activities are controlled by quality assurance procedures. To date some hundred and twelve silicon ingots (103 mm diameter) have been successfully irradiated on a commercial contract basis. The observed axial and radial variations in the resistivity profile of the ingots are very small compared to the profiles associated with conventionally doped silicon and small tolerances on target resistivities are attained. In this paper an overview of the design and characterisation of SILIRAD is given and the methods applied that ensure a quality product are described. Results obtained from trial and production irradiations are presented and the envisaged future modifications to SILIRAD discussed. 10 refs., 2 tabs., 6 figs

  15. Constrained/unconstrained solidification within the massive cast steel/iron ingots

    Directory of Open Access Journals (Sweden)

    W. S. Wołczyński

    2010-04-01

    Full Text Available Some properties of the ingot and especially of the steel forging ingots depend on the ratio of a columnar structure area to an equiaxed structure area created during solidification. The C-E transition is fundamental phenomenon that can be applied to characterize massive cast steel ingots produced by the casting house. The mentioned ratio is created spontaneously due to the rate of heat transfer towards the ceramic mould and then to the environment. The ceramic mould operates as an isolator. So that the thickness of the mould together with a growing solid fraction control the heat transfer and finally the ratio of the columnar structure area to the equiaxed structure area. At first the increase of heat accumulation within the ceramic mould is observed. Next the stationary state for heat transfer is created and finally a gentle abatement of the mould temperature associated with the heat output to the environment is expected. The steep thermal gradients correspond to the increase of heat accumulation in the ceramic mould. The steep thermal gradients are required to promote the columnar structure formation. The full heat accumulation in the mould corresponds well with the C-E transformation while the appearance of the moderate thermal gradients is referred to the gentle temperature abatement within the ceramic mould. The equiaxed structure is expected within this period of heat transfer behavior. The steep thermal gradients involve the activity of viscosity gradient in the liquid. As the result a sedimentary cones are formed at the bottom of the ingot. The C-E transformation is associated with competition between columnar and equaixed structure formation. At the end of competition a fully equiaxed structure is formed. The viscosity gradient is replaced by the thermophoresis which is the driving force for the deposition of some equiaxed grain layers onto the surface of C+E zone. The convection together with the gravity allow the layers to be uniform

  16. Correlation between impurities, defects and cell performance in semicrystalline silicon

    International Nuclear Information System (INIS)

    Doolittle, W.A.; Rohatgi, A.

    1990-01-01

    This paper reports that an in-depth analysis of Solarex CDS semicrystalline silicon has been performed and correlations between the efficiency and impurities, and defects present in the material have been made. Comparisons were made between cell performance and variations in interstitial oxygen, substitutional carbon, grain size, etch pit density, and trap location as a function of position in the ingot. The oxygen concentration was found to decrease with increasing distance from the bottom of the ingot while the carbon concentration as well as average grain size was found to increase. The best cell performance was obtained on wafers with minimum oxygen and maximum carbon (top). No correlation was found between etch pit density and cell performance. DLTS and JVT measurements revealed that samples with higher oxygen content (bottom) gave lower cell performance due to a large number of distributed states, possibly due to extended defects like oxygen precipitates. Low oxygen samples (top) showed predominately discrete states, improved cell performance and a doping dependent average trap density

  17. Preventing light-induced degradation in multicrystalline silicon

    Science.gov (United States)

    Lindroos, J.; Boulfrad, Y.; Yli-Koski, M.; Savin, H.

    2014-04-01

    Multicrystalline silicon (mc-Si) is currently dominating the silicon solar cell market due to low ingot costs, but its efficiency is limited by transition metals, extended defects, and light-induced degradation (LID). LID is traditionally associated with a boron-oxygen complex, but the origin of the degradation in the top of the commercial mc-Si brick is revealed to be interstitial copper. We demonstrate that both a large negative corona charge and an aluminum oxide thin film with a built-in negative charge decrease the interstitial copper concentration in the bulk, preventing LID in mc-Si.

  18. Summary of performance of superconducting radio-frequency cavities built from CBMM niobium ingots

    Science.gov (United States)

    Ciovati, Gianluigi; Dhakal, Pashupati; Kneisel, Peter; Myneni, Ganapati R.

    2015-12-01

    Several Nb ingots have been provided by CBMM to Jefferson Lab since 2004 as part of an R&D collaboration aimed at evaluating the performance of superconducting radio-frequency cavities built from ingots with different purity, as a results of different ingot production processes. Approximately 32 multi- and single-cell cavities with resonant frequency between ˜1.3-2.3 GHz were built, treated and tested at 2 K at Jefferson Lab between 2004 and 2014. The average peak surface field achieved in cavities made of RRR˜260 and RRR˜100-150 ingots was (119 ± 4) mT and (100 ± 8) mT, respectively. Higher quality factor values at 2.0 K have been measured in medium-purity, compared to higher purity material.

  19. Shrinkage Porosity Criterion and Its Application to A 5.5 Ton Steel Ingot

    Directory of Open Access Journals (Sweden)

    Zhang C.

    2016-06-01

    Full Text Available In order to predict the distribution of shrinkage porosity in steel ingot efficiently and accurately, a criterion R√L and a method to obtain its threshold value were proposed. The criterion R√L was derived based on the solidification characteristics of steel ingot and pressure gradient in the mushy zone, in which the physical properties, the thermal parameters, the structure of the mushy zone and the secondary dendrite arm spacing were all taken into consideration. The threshold value of the criterion R√L was obtained with combination of numerical simulation of ingot solidification and total solidification shrinkage rate. Prediction of the shrinkage porosity in a 5.5 ton ingot of 2Cr13 steel with criterion R√L>0.21 m · °C1/2 · s−3/2 agreed well with the results of experimental sectioning. Based on this criterion, optimization of the ingot was carried out by decreasing the height-to-diameter ratio and increasing the taper, which successfully eliminated the centreline porosity and further proved the applicability of this criterion.

  20. Study on Fabrication of Ni-5 at.%W Tapes for Coated Conductors from Cylinder Ingots

    DEFF Research Database (Denmark)

    Ma, L.; Suo, H. L.; Yue, Zhao

    2015-01-01

    Ni-5 at.%W (Ni5W) tapes with a strong cube texture were fabricated using the RABiTS technique and by starting from cylindrical shaped ingots. In contrast to a conventional cuboid-shaped ingot, a cylinder shaped ingot has no anisotropy along the axial direction and the resulting tape will therefore...

  1. Summary of performance of superconducting radio-frequency cavities built from CBMM niobium ingots

    International Nuclear Information System (INIS)

    Ciovati, Gianluigi; Dhakal, Pashupati; Kneisel, Peter; Myneni, Ganapati R.

    2015-01-01

    Several Nb ingots have been provided by CBMM to Jefferson Lab since 2004 as part of an R&D collaboration aimed at evaluating the performance of superconducting radio-frequency cavities built from ingots with different purity, as a results of different ingot production processes. Approximately 32 multi- and single-cell cavities with resonant frequency between ∼1.3-2.3 GHz were built, treated and tested at 2 K at Jefferson Lab between 2004 and 2014. The average peak surface field achieved in cavities made of RRR∼260 and RRR∼100-150 ingots was (119 ± 4) mT and (100 ± 8) mT, respectively. Higher quality factor values at 2.0 K have been measured in medium-purity, compared to higher purity material

  2. On the Modeling of Thermal Radiation at the Top Surface of a Vacuum Arc Remelting Ingot

    Science.gov (United States)

    Delzant, P.-O.; Baqué, B.; Chapelle, P.; Jardy, A.

    2018-06-01

    Two models have been implemented for calculating the thermal radiation emitted at the ingot top in the VAR process, namely, a crude model that considers only radiative heat transfer between the free surface and electrode tip and a more detailed model that describes all radiative exchanges between the ingot, electrode, and crucible wall using a radiosity method. From the results of the second model, it is found that the radiative heat flux at the ingot top may depend heavily on the arc gap length and the electrode radius, but remains almost unaffected by variations of the electrode height. Both radiation models have been integrated into a CFD numerical code that simulates the growth and solidification of a VAR ingot. The simulation of a Ti-6-4 alloy melt shows that use of the detailed radiation model leads to some significant modification of the simulation results compared with the simple model. This is especially true during the hot-topping phase, where the top radiation plays an increasingly important role compared with the arc energy input. Thus, while the crude model has the advantage of its simplicity, use of the detailed model should be preferred.

  3. A continuous Czochralski silicon crystal growth system

    Science.gov (United States)

    Wang, C.; Zhang, H.; Wang, T. H.; Ciszek, T. F.

    2003-03-01

    Demand for large silicon wafers has driven the growth of silicon crystals from 200 to 300 mm in diameter. With the increasing silicon ingot sizes, melt volume has grown dramatically. Melt flow becomes more turbulent as melt height and volume increase. To suppress turbulent flow in a large silicon melt, a new Czochralski (CZ) growth furnace has been designed that has a shallow melt. In this new design, a crucible consists of a shallow growth compartment in the center and a deep feeding compartment around the periphery. Two compartments are connected with a narrow annular channel. A long crystal may be continuously grown by feeding silicon pellets into the dedicated feeding compartment. We use our numerical model to simulate temperature distribution and velocity field in a conventional 200-mm CZ crystal growth system and also in the new shallow crucible CZ system. By comparison, advantages and disadvantages of the proposed system are observed, operating conditions are determined, and the new system is improved.

  4. Superconducting radio-frequency cavities made from medium and low-purity niobium ingots

    Science.gov (United States)

    Ciovati, Gianluigi; Dhakal, Pashupati; Myneni, Ganapati R.

    2016-06-01

    Superconducting radio-frequency cavities made of ingot niobium with residual resistivity ratio (RRR) greater than 250 have proven to have similar or better performance than fine-grain Nb cavities of the same purity, after standard processing. The high purity requirement contributes to the high cost of the material. As superconducting accelerators operating in continuous-wave typically require cavities to operate at moderate accelerating gradients, using lower purity material could be advantageous not only to reduce cost but also to achieve higher Q 0-values. In this contribution we present the results from cryogenic RF tests of 1.3-1.5 GHz single-cell cavities made of ingot Nb of medium (RRR = 100-150) and low (RRR = 60) purity from different suppliers. Cavities made of medium-purity ingots routinely achieved peak surface magnetic field values greater than 70 mT with an average Q 0-value of 2 × 1010 at 2 K after standard processing treatments. The performances of cavities made of low-purity ingots were affected by significant pitting of the surface after chemical etching.

  5. Numerical Model for Solidification Zones Selection in the Large Ingots

    Directory of Open Access Journals (Sweden)

    Wołczyński W.

    2015-12-01

    Full Text Available A vertical cut at the mid-depth of the 15-ton forging steel ingot has been performed by curtesy of the CELSA - Huta Ostrowiec plant. Some metallographic studies were able to reveal not only the chilled undersized grains under the ingot surface but columnar grains and large equiaxed grains as well. Additionally, the structural zone within which the competition between columnar and equiaxed structure formation was confirmed by metallography study, was also revealed. Therefore, it seemed justified to reproduce some of the observed structural zones by means of numerical calculation of the temperature field. The formation of the chilled grains zone is the result of unconstrained rapid solidification and was not subject of simulation. Contrary to the equiaxed structure formation, the columnar structure or columnar branched structure formation occurs under steep thermal gradient. Thus, the performed simulation is able to separate both discussed structural zones and indicate their localization along the ingot radius as well as their appearance in term of solidification time.

  6. Modelling the void deformation and closure by hot forging of ingot castings

    DEFF Research Database (Denmark)

    Christiansen, Peter; Hattel, Jesper Henri; Kotas, Petr

    2012-01-01

    by mechanical deformation. The aim of this paper is to analyze numerically if and to what degree the voids areclosed by the forging. Using the commercial simulation software ABAQUS, both simplified model ingots and physically manufactured ingots containing prescribed void distributions are deformed and analyzed....... The analysis concernsboth the void density change and the location of the voids in the part after deformation. The latter can be important for the subsequent reliability of the parts, for instance regarding fatigue properties. The analysis incorporates the Gurson yield criterion for metals containing voids...... and focuses on how the voids deform depending on their size and distribution in the ingot as well ashow the forging forces are applied....

  7. Production of a 304 stainless steel nuclear reactor forging from a very large electroslag refined ingot

    International Nuclear Information System (INIS)

    Watkins, E.J.; Tihansky, E.L.

    1986-01-01

    A four-loop, upper barrel flange forging for a nuclear reactor was produced from what the authors believe to be the largest 304H grade stainless steel electroslag refined (ESR) ingot ever refined. The ingot was refined in a 1524-mm-diameter, ingot withdrawal-type ESR furnace using a lime-bearing slag, low-frequency a-c power, and dry air protection. Five electrodes were remelted in order to produce the desired ingot weight. The ingot was subsequently forged in a five-step operation on a 6800-metric-ton press to produce the desired barrel flange configuration. Testing of the finished machined forging revealed excellent tensile ductility, excellent ultrasonic penetrability, and good chemical uniformity with no macrosegregation. Overall quality was judged to be superior to previously produced, conventionally melted forgings

  8. Material Properties of Laser-Welded Thin Silicon Foils

    Directory of Open Access Journals (Sweden)

    M. T. Hessmann

    2013-01-01

    Full Text Available An extended monocrystalline silicon base foil offers a great opportunity to combine low-cost production with high efficiency silicon solar cells on a large scale. By overcoming the area restriction of ingot-based monocrystalline silicon wafer production, costs could be decreased to thin film solar cell range. The extended monocrystalline silicon base foil consists of several individual thin silicon wafers which are welded together. A comparison of three different approaches to weld 50 μm thin silicon foils is investigated here: (1 laser spot welding with low constant feed speed, (2 laser line welding, and (3 keyhole welding. Cross-sections are prepared and analyzed by electron backscatter diffraction (EBSD to reveal changes in the crystal structure at the welding side after laser irradiation. The treatment leads to the appearance of new grains and boundaries. The induced internal stress, using the three different laser welding processes, was investigated by micro-Raman analysis. We conclude that the keyhole welding process is the most favorable to produce thin silicon foils.

  9. Effect of localized polycrystalline silicon properties on solar cell performance

    Science.gov (United States)

    Leung, D.; Iles, P. A.; Hyland, S.; Kachare, A.

    1984-01-01

    Several forms of polycrystalline silicon, mostly from cast ingots, (including UCP, SILSO and HEM) were studied. On typical slices, localized properties were studied in two ways. Small area (about 2.5 sq mm) mesa diodes were formed, and localized photovoltaic properties were measured. Also a small area (about .015 sq mm) light spot was scanned across the cells; the light spot response was calibrated to measure local diffusion length directly. Using these methods, the effects of grain boundaries, or of intragrain imperfections were correlated with cell performance. Except for the fine grain portion of SILSO, grain boundaries played only a secondary role in determining cell performance. The major factor was intra-grain material quality and it varied with position in ingots and probably related to solidification procedure.

  10. Numerical analysis on effect of annealing mc-Si ingot grown by DS process for PV application

    Science.gov (United States)

    Aravindan, G.; Srinivasan, M.; Aravinth, K.; Ramasamy, P.

    2017-10-01

    Silicon solar cells play a crucial role in Photo voltaic (PV) application. We have numerically investigated thermal stress and normal stress components (Sigma 11, Sigma 22, Sigma 33 and sigma 12) by using finite volume method. The maximum thermal stress has low value at the centre region for 900 K and 700 K annealing temperatures comparing all the cases. The maximum thermal stress at peripheral region is low for 700 K annealing compared to 900 K annealing. The annealing effect of mc-Si ingot normal stress components is discussed. At 700 K annealing temperature the normal stress in 11 and 33 direction has lower maximum and at the 900 K annealing temperature the normal stress in 22 and 12 direction has lower maximum.

  11. Compositional analysis of silicon oxide/silicon nitride thin films

    Directory of Open Access Journals (Sweden)

    Meziani Samir

    2016-06-01

    Full Text Available Hydrogen, amorphous silicon nitride (SiNx:H abbreviated SiNx films were grown on multicrystalline silicon (mc-Si substrate by plasma enhanced chemical vapour deposition (PECVD in parallel configuration using NH3/SiH4 gas mixtures. The mc-Si wafers were taken from the same column of Si cast ingot. After the deposition process, the layers were oxidized (thermal oxidation in dry oxygen ambient environment at 950 °C to get oxide/nitride (ON structure. Secondary ion mass spectroscopy (SIMS, Rutherford backscattering spectroscopy (RBS, Auger electron spectroscopy (AES and energy dispersive X-ray analysis (EDX were employed for analyzing quantitatively the chemical composition and stoichiometry in the oxide-nitride stacked films. The effect of annealing temperature on the chemical composition of ON structure has been investigated. Some species, O, N, Si were redistributed in this structure during the thermal oxidation of SiNx. Indeed, oxygen diffused to the nitride layer into Si2O2N during dry oxidation.

  12. Improvement in the reliability of shells for light water reactors by manufacturing from hollow ingots

    International Nuclear Information System (INIS)

    Bocquet, P.; Blondeau, R.; Poitrault, I.; Badeau, J.P.; Dumont, R.

    1989-01-01

    The example of forging shells for PWR type reactors is proposed to show how the choice of the manufacturing process may be of prime importance for the component integrity by the reduction of the detrimental effects of segregations. The forging shells (20MnMoNi55) manufactured from hollow ingot are free of any segregation in the critical area located just at the internal surface and sub-surface. Manufacturing problems associated to these segregations in shells issued from conventional ingots, in particular welding difficulties for cladding, have been reduced or eleminated. The reliability of these components present an improved resistance to irradiation embrittlement. (DG)

  13. Superconducting radio-frequency cavities made from medium and low-purity niobium ingots

    International Nuclear Information System (INIS)

    Ciovati, Gianluigi; Dhakal, Pashupati; Myneni, Ganapati R

    2016-01-01

    Superconducting radio-frequency cavities made of ingot niobium with residual resistivity ratio (RRR) greater than 250 have proven to have similar or better performance than fine-grain Nb cavities of the same purity, after standard processing. The high purity requirement contributes to the high cost of the material. As superconducting accelerators operating in continuous-wave typically require cavities to operate at moderate accelerating gradients, using lower purity material could be advantageous not only to reduce cost but also to achieve higher Q 0 -values. In this contribution we present the results from cryogenic RF tests of 1.3–1.5 GHz single-cell cavities made of ingot Nb of medium (RRR = 100–150) and low (RRR = 60) purity from different suppliers. Cavities made of medium-purity ingots routinely achieved peak surface magnetic field values greater than 70 mT with an average Q 0 -value of 2 × 10 10 at 2 K after standard processing treatments. The performances of cavities made of low-purity ingots were affected by significant pitting of the surface after chemical etching. (paper)

  14. Solidification Segregation and Homogenization Behavior of 1Cr-1.25Mo-0.25V Steel Ingot

    Energy Technology Data Exchange (ETDEWEB)

    Kim, Dong-Bae [Dae-gu Mechatronics and Materials Institute, Daegu (Korea, Republic of); Na, Young-Sang; Seo, Seong-Moon [Korea Institute of Materials Science, Changwon (Korea, Republic of); Lee, Je-Hyun [Changwon National University, Changwon (Korea, Republic of)

    2016-09-15

    As a first step to optimizing the homogenization heat treatment following high temperature upset forging, the solidification segregation and the homogenization behaviors of solute elements were quantitatively analyzed for 1Cr-1.25Mo-0.25V steel ingot by electron probe micro-analysis (EPMA). The random sampling approach, which was designed to generate continuous compositional profiles of each solute element, was employed to clarify the segregation and homogenization behaviors. In addition, ingot castings of lab-scale and a 16-ton-sized 1Cr-1.25Mo-0.25V steel were simulated using the finite element method in three dimensions to understand the size effect of the ingot on the microsegregation and its reduction during the homogenization heat treatment. It was found that the microsegregation in a large-sized ingot was significantly reduced by the promotion of solid state diffusion due to the extremely low cooling rate. On the other hand, from the homogenization point of view, increasing the ingot size causes a dramatic increase in the dendrite arm spacing, and hence the homogenization of microsegregation in a large-sized ingot appears to be practically difficult.

  15. Solar cell fabricated on welded thin flexible silicon

    Directory of Open Access Journals (Sweden)

    Hessmann Maik Thomas

    2015-01-01

    Full Text Available We present a thin-film crystalline silicon solar cell with an AM1.5 efficiency of 11.5% fabricated on welded 50 μm thin silicon foils. The aperture area of the cell is 1.00 cm2. The cell has an open-circuit voltage of 570 mV, a short-circuit current density of 29.9 mA cm-2 and a fill factor of 67.6%. These are the first results ever presented for solar cells on welded silicon foils. The foils were welded together in order to create the first thin flexible monocrystalline band substrate. A flexible band substrate offers the possibility to overcome the area restriction of ingot-based monocrystalline silicon wafers and the feasibility of a roll-to-roll manufacturing. In combination with an epitaxial and layer transfer process a decrease in production costs can be achieved.

  16. Simulation of ingot casting processes at Deutsche Edelstahlwerke GmbH®

    International Nuclear Information System (INIS)

    Hartmann, L; Ernst, C; Klung, J-S

    2012-01-01

    To enhance the quality of tool steels it is necessary to analyse all stages of the production process. During the ingot- or continuous casting processes and the following solidification, material and geometry depending reactions cause defects such as macro segregations or porosities. In former times the trial and error approach, together with the experience and creativity of the steelworks engineers was used to improve the as-cast quality, with a high amount of test procedures and a high demand of research time and costs. Further development in software and algorithms has allowed modern simulation techniques to find their way into industrial steel production and casting-simulations are widely used to achieve an accurate prediction of the ingot quality. To improve the as-cast quality, several ingot casting processes of tool steels were studied at the R and D department of Deutsche Edelstahlwerke GmbH by using the numerical casting simulation software MAGMASOFT ® . In this paper some results extracted from the simulation software are shown and compared to experimental investigations.

  17. Fast determination of impurities in metallurgical grade silicon for photovoltaics by instrumental neutron activation analysis

    International Nuclear Information System (INIS)

    Hampel, J.; Boldt, F.M.; Gerstenberg, H.; Hampel, G.; Kratz, J.V.; Reber, S.; Wiehl, N.

    2011-01-01

    Standard wafer solar cells are made of near-semiconductor quality silicon. This high quality material makes up a significant part of the total costs of a solar module. Therefore, new concepts with less expensive so called solar grade silicon directly based on physiochemically upgraded metallurgical grade silicon are investigated. Metallurgical grade silicon contains large amounts of impurities, mainly transition metals like Fe, Cr, Mn, and Co, which degrade the minority carrier lifetime and thus the solar cell efficiency. A major reduction of the transition metal content occurs during the unidirectional crystallization due to the low segregation coefficient between the solid and liquid phase. A further reduction of the impurity level has to be done by gettering procedures applied to the silicon wafers. The efficiency of such cleaning procedures of metallurgical grade silicon is studied by instrumental neutron activation analysis (INAA). Small sized silicon wafers of approximately 200 mg with and without gettering step were analyzed. To accelerate the detection of transition metals in a crystallized silicon ingot, experiments of scanning whole vertical silicon columns with a diameter of approximately 1 cm by gamma spectroscopy were carried out. It was demonstrated that impurity profiles can be obtained in a comparably short time. Relatively constant transition metal ratios were found throughout an entire silicon ingot. This led to the conclusion that the determination of several metal profiles might be possible by the detection of only one 'leading element'. As the determination of Mn in silicon can be done quite fast compared to elements like Fe, Cr, and Co, it could be used as a rough marker for the overall metal concentration level. Thus, a fast way to determine impurities in photovoltaic silicon material is demonstrated. - Highlights: → We demonstrate a fast way to determine impurities in photovoltaic silicon by NAA. → We make first experiments of locally

  18. Research and Development of the Solidification of Slab Ingots from Special Tool Steels

    Directory of Open Access Journals (Sweden)

    Tkadlečková M.

    2017-09-01

    Full Text Available The paper describes the research and development of casting and solidification of slab ingots from special tool steels by means of numerical modelling using the finite element method. The pre-processing, processing and post-processing phases of numerical modelling are outlined. Also, problems with determining the thermophysical properties of materials and heat transfer between the individual parts of the casting system are discussed. Based on the type of grade of tool steel, the risk of final porosity is predicted. The results allowed to improve the production technology of slab ingots, and also to verify the ratio, the chamfer and the external/ internal shape of the wall of the new designed slab ingots.

  19. Environmentally benign silicon solar cell manufacturing

    Energy Technology Data Exchange (ETDEWEB)

    Tsuo, Y.S. [National Renewable Energy Lab., Golden, CO (United States); Gee, J.M. [Sandia National Labs., Albuquerque, NM (United States); Menna, P. [National Agency for New Technologies Energy and Environment, Portici (Italy); Strebkov, D.S.; Pinov, A.; Zadde, V. [Intersolarcenter, Moscow (Russian Federation)

    1998-09-01

    The manufacturing of silicon devices--from polysilicon production, crystal growth, ingot slicing, wafer cleaning, device processing, to encapsulation--requires many steps that are energy intensive and use large amounts of water and toxic chemicals. In the past two years, the silicon integrated-circuit (IC) industry has initiated several programs to promote environmentally benign manufacturing, i.e., manufacturing practices that recover, recycle, and reuse materials resources with a minimal consumption of energy. Crystalline-silicon solar photovoltaic (PV) modules, which accounted for 87% of the worldwide module shipments in 1997, are large-area devices with many manufacturing steps similar to those used in the IC industry. Obviously, there are significant opportunities for the PV industry to implement more environmentally benign manufacturing approaches. Such approaches often have the potential for significant cost reduction by reducing energy use and/or the purchase volume of new chemicals and by cutting the amount of used chemicals that must be discarded. This paper will review recent accomplishments of the IC industry initiatives and discuss new processes for environmentally benign silicon solar-cell manufacturing.

  20. Silicon Solar Cell Process Development, Fabrication and Analysis, Phase 1

    Science.gov (United States)

    Yoo, H. I.; Iles, P. A.; Tanner, D. P.

    1979-01-01

    Solar cells from RTR ribbons, EFG (RF and RH) ribbons, dendritic webs, Silso wafers, cast silicon by HEM, silicon on ceramic, and continuous Czochralski ingots were fabricated using a standard process typical of those used currently in the silicon solar cell industry. Back surface field (BSF) processing and other process modifications were included to give preliminary indications of possible improved performance. The parameters measured included open circuit voltage, short circuit current, curve fill factor, and conversion efficiency (all taken under AM0 illumination). Also measured for typical cells were spectral response, dark I-V characteristics, minority carrier diffusion length, and photoresponse by fine light spot scanning. the results were compared to the properties of cells made from conventional single crystalline Czochralski silicon with an emphasis on statistical evaluation. Limited efforts were made to identify growth defects which will influence solar cell performance.

  1. Modeling and Optimization of Direct Chill Casting to Reduce Ingot Cracking

    Energy Technology Data Exchange (ETDEWEB)

    Das, S.K.; Ningileri, S.; Long, Z.; Saito, K.; Khraisheh, M.; Hassan, M.H.; Kuwana, K.; Han, Q.; Viswanathan, S.; Sabau, A.S.; Clark, J.; Hyrn, J. (ANL)

    2006-08-15

    Approximately 68% of the aluminum produced in the United States is first cast into ingots prior to further processing into sheet, plate, extrusions, or foil. The direct chill (DC) semi-continuous casting process has been the mainstay of the aluminum industry for the production of ingots due largely to its robust nature and relative simplicity. Though the basic process of DC casting is in principle straightforward, the interaction of process parameters with heat extraction, microstructural evolution, and development of solidification stresses is too complex to analyze by intuition or practical experience. One issue in DC casting is the formation of stress cracks [1-15]. In particular, the move toward larger ingot cross-sections, the use of higher casting speeds, and an ever-increasing array of mold technologies have increased industry efficiencies but have made it more difficult to predict the occurrence of stress crack defects. The Aluminum Industry Technology Roadmap [16] has recognized the challenges inherent in the DC casting process and the control of stress cracks and selected the development of 'fundamental information on solidification of alloys to predict microstructure, surface properties, and stresses and strains' as a high-priority research need, and the 'lack of understanding of mechanisms of cracking as a function of alloy' and 'insufficient understanding of the aluminum solidification process', which is 'difficult to model', as technology barriers in aluminum casting processes. The goal of this Aluminum Industry of the Future (IOF) project was to assist the aluminum industry in reducing the incidence of stress cracks from the current level of 5% to 2%. Decreasing stress crack incidence is important for improving product quality and consistency as well as for saving resources and energy, since considerable amounts of cast metal could be saved by eliminating ingot cracking, by reducing the scalping thickness of

  2. Investigation of the crystallization process of titanium alloy ingots produced by vacuum arc melting method

    International Nuclear Information System (INIS)

    Tetyukhin, V.V.; Kurapov, V.N.; Trubin, A.N.; Demchenko, M.V.; Lazarev, V.G.; Ponedilko, S.V.; Dubrovina, N.T.; Kurapova, L.A.

    1978-01-01

    The process of crystallization and hardening of the VT3-1 and VT9 titanium alloys ingots during the vacuum-arc remelting (VAR) has been studied. In order to investigate the kinetics of the hole shape changing and the peculiarities of the ingot formation during the VAR, the radiography method has been used. It is established that the VAR of the titanium alloy ingots is basically a continuous process. An intense heating of the liquid bath mirror and the availability of high temperature gradients in the hole are the typical features of the VAR process

  3. High performance superconducting radio frequency ingot niobium technology for continuous wave applications

    International Nuclear Information System (INIS)

    Dhakal, Pashupati; Ciovati, Gianluigi; Myneni, Ganapati R.

    2015-01-01

    Future continuous wave (CW) accelerators require the superconducting radio frequency cavities with high quality factor and medium accelerating gradients (≤20 MV/m). Ingot niobium cavities with medium purity fulfill the specifications of both accelerating gradient and high quality factor with simple processing techniques and potential reduction in cost. This contribution reviews the current superconducting radiofrequency research and development and outlines the potential benefits of using ingot niobium technology for CW applications

  4. Modelling of Damage During Hot Forging of Ingots

    DEFF Research Database (Denmark)

    Christiansen, Peter; Hattel, Jesper Henri; Bay, Niels

    2013-01-01

    Ductile damage modelling in the ingot forging process is discussed. Advantages and disadvantages of both coupled and uncoupled ductile damage models are presented. Some uncoupled damage models are examined in greater detail regarding their applicability to different processes, where hydrostatic...

  5. Numerical simulation on multiple pouring process for a 292 t steel ingot

    Directory of Open Access Journals (Sweden)

    Tu Wutao

    2014-01-01

    Full Text Available A ladle-tundish-mould transportation model considering the entire multiple pouring (MP process is proposed. Numerical simulation is carried out to study the carbon distribution and variation in both the tundish and the mould for making a 292 t steel ingot. Firstly, the fluid flow as well as the heat and mass transfer of the molten steel in the tundish is simulated based on the multiphase transient turbulence model. Then, the carbon mixing in the mould is calculated by using the species concentration at the tundish outlet as the inlet condition during the teeming process. The results show a high concentration of carbon at the bottom and a low concentration of carbon at the top of the mould after a MP process with carbon content high in the first ladle and low in the last ladle. Such carbon concentration distribution would help reduce the negative segregation at the bottom and the positive segregation at the top of the solidified ingot.

  6. Large grain cavities from pure niobium ingot

    Science.gov (United States)

    Myneni, Ganapati Rao [Yorktown, VA; Kneisel, Peter [Williamsburg, VA; Cameiro, Tadeu [McMurray, PA

    2012-03-06

    Niobium cavities are fabricated by the drawing and ironing of as cast niobium ingot slices rather than from cold rolled niobium sheet. This method results in the production of niobium cavities having a minimum of grain boundaries at a significantly reduced cost as compared to the production of such structures from cold rolled sheet.

  7. Intensification of heating processes of ingots in top-fired pit furnaces

    International Nuclear Information System (INIS)

    Kotlyarevskij, E.M.; Bazhenov, A.V.; Zavarova, I.S.; Baboshin, V.M.; Ioffe, Ya.E.

    1978-01-01

    The soaking pits provided with only one upper burner are characterized by the non-uniformity of the temperature field. It is suggested to improve the gas-burner device and the smoke flue for obviating that draw-back. It is the application of new compositions of dry materials for building up the bottom (preventing its growth) and the rational arrangement of cold ingots of the 12Kh18N10T steel (with their bottom part widened upward) that allowed the bottom crops to be reduced by about 0.5% (abs. %), and the temperature at the end of rolling ingots to be increased by about 40 degrees. According to the temperature readings, the most representative point in the soaking pit has been determined. If the preheating process is carried out automatically in accordance with that representative point, the calculated rational modes of the rapid preheating of ingots may be realized, and the consumption of the conventional fuel may be reduced by about 3 to 5 kg/ton of steel

  8. Evaluation of Metallurgical Quality of Master Heat IN-713C Nickel Alloy Ingots

    Directory of Open Access Journals (Sweden)

    Binczyk F.

    2012-12-01

    Full Text Available The paper presents the results of evaluation of the metallurgical quality of master heat ingots and of the identification of non-metallic inclusions (oxides of Al., Zr, Hf, Cr, etc., which have been found in the shrinkage cavities formed in these ingots. The inclusions penetrate into the liquid alloy, and on pouring of mould are transferred to the casting, especially when the filtering system is not sufficiently effective. The specific nature of the melting process of nickel and cobalt alloys, carried out in vacuum induction furnaces, excludes the possibility of alloy refining and slag removal from the melt surface. Therefore, to improve the quality of castings (parts of aircraft engines, it is so important to evaluate the quality of ingots before charging them into the crucible of an induction furnace. It has been proved that one of the methods for rapid quality evaluation is an ATD analysis of the sample solidification process, where samples are taken from different areas of the master heat ingot. The evaluation is based on a set of parameters plotted on the graph of the dT/dt derivative curve during the last stage of the solidification process in a range from TEut to Tsol.

  9. Evaluation of Metallurgical Quality of Master Heat IN-713C Nickel Alloy Ingots

    Directory of Open Access Journals (Sweden)

    F. Binczyk

    2012-12-01

    Full Text Available The paper presents the results of evaluation of the metallurgical quality of master heat ingots and of the identification of non-metallic inclusions (oxides of Al., Zr, Hf, Cr, etc., which have been found in the shrinkage cavities formed in these ingots. The inclusions penetrate into the liquid alloy, and on pouring of mould are transferred to the casting, especially when the filtering system is not sufficiently effective. The specific nature of the melting process of nickel and cobalt alloys, carried out in vacuum induction furnaces,excludes the possibility of alloy refining and slag removal from the melt surface. Therefore, to improve the quality of castings (parts of aircraft engines, it is so important to evaluate the quality of ingots before charging them into the crucible of an induction furnace. It has been proved that one of the methods for rapid quality evaluation is an ATD analysis of the sample solidification process, where samples are taken from different areas of the master heat ingot. The evaluation is based on a set of parameters plotted on the graph of the dT/dt derivative curve during the last stage of the solidification process in a range from TEut to Tsol.

  10. Low temperature spalling of silicon: A crack propagation study

    Energy Technology Data Exchange (ETDEWEB)

    Bertoni, Mariana; Uberg Naerland, Tine; Stoddard, Nathan; Guimera Coll, Pablo

    2017-06-08

    Spalling is a promising kerfless method for cutting thin silicon wafers while doubling the yield of a silicon ingot. The main obstacle in this technology is the high total thickness variation of the spalled wafers, often as high as 100% of the wafer thickness. It has been suggested before that a strong correlation exists between low crack velocities and a smooth surface, but this correlation has never been shown during a spalling process in silicon. The reason lies in the challenge associated to measuring such velocities. In this contribution, we present a new approach to assess, in real time, the crack velocity as it propagates during a low temperature spalling process. Understanding the relationship between crack velocity and surface roughness during spalling can pave the way to attain full control on the surface quality of the spalled wafer.

  11. Fiscal 2000 achievement report. Development of energy use rationalization-oriented silicon manufacturing process (Development of silicon substrate manufacturing technology for high-quality solar cell); 2000 nendo shin energy sangyo gijutsu sogo kaihatsu kiko kyodo kenkyu gyomu seika hokokusho. Energy shiyo gorika silicon seizo process kaihatsu (Kohinshitsu taiyodenchiyou silicon kiban seizo gijutsu no kaihatsu)

    Energy Technology Data Exchange (ETDEWEB)

    NONE

    2001-03-01

    Research and development was conducted for enhancing productivity and energy conservation by rendering continuous and automatic the electromagnetic casting process for manufacturing polycrystalline silicon substrates for solar cells. In the manufacture of ingots for substrates by continuous electromagnetic casting, the chuck type system for feeding power to the melt plasma was replaced by a roller type system, and the power feeding position was moved to the high temperature region. Also, an on-line ingot slicing technique was established. In the manufacture of substrates at a slicing rate of 300 {mu}m/minute, productivity of 115,000 wafers/month, yield of 98%, and thickness tolerance of 30 {mu}m were achieved. A high-speed cleaning technique was developed using a jet stream, by which the cleaning time was reduced to 5 minutes and the slurry recovery rate was elevated to 95%. Based on these, substrate-related costs in the case of 100 MW/year production was calculated, which resulted in a cost of 98.8 yen/wafer (target: 103.3 yen/wafer) for manufacturing 15 cm square substrates from ingots and in a 15 cm square substrate slicing and cleaning cost of 135.1 yen/wafer (target: 135.4 yen/wafer). (NEDO)

  12. Effect of vacuum arc melting/casting parameters on shrinkage cavity/piping of austenitic stainless steel ingot

    International Nuclear Information System (INIS)

    Kamran, J.; Feroz, M.; Sarwar, M.

    2009-01-01

    Shrinkage cavity/piping at the end of the solidified ingot of steels is one of the most common casting problem in 316L austenitic stainless steel ingot, when consumable electrode is melted and cast in a water-cooled copper mould by vacuum arc re-melting furnace. In present study an effort has been made to reduce the size of shrinkage cavity/ piping by establishing the optimum value of hot topping process parameters at the end of the melting process. It is concluded that the shrinkage cavity/piping at the top of the solidified ingot can be reduced to minimum by adjusting the process parameters particularly the melting current density. (author)

  13. Evolution of A-Type Macrosegregation in Large Size Steel Ingot After Multistep Forging and Heat Treatment

    Science.gov (United States)

    Loucif, Abdelhalim; Ben Fredj, Emna; Harris, Nathan; Shahriari, Davood; Jahazi, Mohammad; Lapierre-Boire, Louis-Philippe

    2018-06-01

    A-type macrosegregation refers to the channel chemical heterogeneities that can be formed during solidification in large size steel ingots. In this research, a combination of experiment and simulation was used to study the influence of open die forging parameters on the evolution of A-type macrosegregation patterns during a multistep forging of a 40 metric ton (MT) cast, high-strength steel ingot. Macrosegregation patterns were determined experimentally by macroetch along the longitudinal axis of the forged and heat-treated ingot. Mass spectroscopy, on more than 900 samples, was used to determine the chemical composition map of the entire longitudinal sectioned surface. FORGE NxT 1.1 finite element modeling code was used to predict the effect of forging sequences on the morphology evolution of A-type macrosegregation patterns. For this purpose, grain flow variables were defined and implemented in a large scale finite element modeling code to describe oriented grains and A-type segregation patterns. Examination of the A-type macrosegregation showed four to five parallel continuous channels located nearly symmetrical to the axis of the forged ingot. In some regions, the A-type patterns became curved or obtained a wavy form in contrast to their straight shape in the as-cast state. Mass spectrometry analysis of the main alloying elements (C, Mn, Ni, Cr, Mo, Cu, P, and S) revealed that carbon, manganese, and chromium were the most segregated alloying elements in A-type macrosegregation patterns. The observed differences were analyzed using thermodynamic calculations, which indicated that changes in the chemical composition of the liquid metal can affect the primary solidification mode and the segregation intensity of the alloying elements. Finite element modeling simulation results showed very good agreement with the experimental observations, thereby allowing for the quantification of the influence of temperature and deformation on the evolution of the shape of the

  14. Effects of silicon cross section and neutron spectrum on the radial uniformity in neutron transmutation doping.

    Science.gov (United States)

    Kim, Haksung; Ho Pyeon, Cheol; Lim, Jae-Yong; Misawa, Tsuyoshi

    2012-01-01

    The effects of silicon cross section and neutron spectrum on the radial uniformity of a Si-ingot are examined experimentally with various neutron spectrum conditions. For the cross section effect, the numerical results using silicon single crystal cross section reveal good agreements with experiments within relative difference of 6%, whereas the discrepancy is approximately 20% in free-gas cross section. For the neutron spectrum effect, the radial uniformity in hard neutron spectrum is found to be more flattening than that in soft spectrum. Copyright © 2011 Elsevier Ltd. All rights reserved.

  15. Design and burn-up analyses of new type holder for silicon neutron transmutation doping.

    Science.gov (United States)

    Komeda, Masao; Arai, Masaji; Tamai, Kazuo; Kawasaki, Kozo

    2016-07-01

    We have developed a new silicon irradiation holder with a neutron filter to increase the irradiation efficiency. The neutron filter is made of an alloy of aluminum and B4C particles. We fabricated a new holder based on the results of design analyses. This filter has limited use in applications requiring prolonged use due to a decrease in the amount of (10)B in B4C particles. We investigated the influence of (10)B reduction on doping distribution in a silicon ingot by using the Monte Carlo Code MVP. Copyright © 2016 Elsevier Ltd. All rights reserved.

  16. Formation of non-metallic inclusions and the possibility of their removal during ingot casting

    OpenAIRE

    Ragnarsson, Lars

    2010-01-01

    The present study was carried out to investigate the formation and evolution of non-metallic inclusions during ingot casting. Emphasize have been on understanding the types of inclusions formed and developed through the casting process and on the development of already existing inclusions carried over from the ladle during casting. Industrial experiments carried on at Uddeholm Tooling together with laboratory work and Computational Fluid Dynamics (CFD) simulations. Ingots of 5.8 tons have bee...

  17. Multi-objective optimization of die geometry in ingot forging

    DEFF Research Database (Denmark)

    Christiansen, Peter; Martins, Paulo A.F.; Bay, Niels

    2014-01-01

    The soundness of an ingot after hot forging with different V-shaped lower dies is evaluated using finite element simulations.Two different modelling approaches that make use of uncoupled ductile damage and coupled ductile damage based on porousplasticity are employed. It is shown that the two...

  18. Rayleigh Number Criterion for Formation of A-Segregates in Steel Castings and Ingots

    DEFF Research Database (Denmark)

    Rad, M. Torabi; Kotas, Petr; Beckermann, C.

    2013-01-01

    A Rayleigh number-based criterion is developed for predicting the formation of A-segregates in steel castings and ingots. The criterion is calibrated using available experimental data for ingots involving 27 different steel compositions. The critical Rayleigh number above which A-segregates can b......, the primary reason for this over-prediction is persumed to be the presence of a central zone of equiaxed grains in the casting sections. A-segregates do not form when the grain structure is equiaxed. © The Minerals, Metals & Materials Society and ASM International 2013...

  19. Magnetic flow control in growth and casting of photovoltaic silicon: Numerical and experimental results

    Science.gov (United States)

    Poklad, A.; Pal, J.; Galindo, V.; Grants, I.; Heinze, V.; Meier, D.; Pätzold, O.; Stelter, M.; Gerbeth, G.

    2017-07-01

    A novel, vertical Bridgman-type technique for growing multi-crystalline silicon ingots in an induction furnace is described. In contrast to conventional growth, a modified setup with a cone-shaped crucible and susceptor is used. A detailed numerical simulation of the setup is presented. It includes a global thermal simulation of the furnace and a local simulation of the melt, which aims at the influence of the melt flow on the temperature and concentration fields. Furthermore, seeded growth of cone-shaped Si ingots using either a monocrystalline seed or a seed layer formed by pieces of poly-Si is demonstrated and compared to growth without seeds. The influences of the seed material on the grain structure and the dislocation density of the ingots are discussed. The second part addresses model experiments for the Czochralski technique using the room temperature liquid metal GaInSn. The studies were focused on the influence of a rotating and a horizontally static magnetic field on the melt flow and the related heat transport in crucibles being heated from bottom and/or side, and cooled by a crystal model covering about 1/3 of the upper melt surface.

  20. The Influence of Impurities in Feed Ingots on the Quality of Castings Made from Nickel Superalloy IN-713C

    Directory of Open Access Journals (Sweden)

    Binczyk F.

    2013-12-01

    Full Text Available The paper presents the results of research on the impact of impurities in the feed ingots (master heat on the precipitation of impurities in the ATD thermal analysis probe castings. This impurities occur mostly inside shrinkage cavities and in interdendritic space. Additionally, insufficient filtration of liquid alloy during pouring promotes the transfer of impurities into the casting. The technology of melting superalloys in vacuum furnace prevents the removal of slag from the surface of molten metal. Because of that, the effective method of quality assessment of feed ingots in order to evaluate the existence of impurities is needed. The effectiveness of ATD analysis in evaluation of purity of feed ingots was researched. In addition the similarities of non-metallic inclusions in feed ingots and in castings were observed.

  1. Ingot formation using uranium dendrites recovered by electrolysis in LiCl-KCl-PuCl3-UCl3 melt

    International Nuclear Information System (INIS)

    Mineo Fukushima; Akira Nakayoshi; Shinichi Kitawaki; Masaki Kurata; Noboru Yahagi

    2008-01-01

    Products on solid cathodes recovered by the metal pyrochemical processing were processed to obtain uranium ingot. Studies on process conditions of uranium formation, assay recovered uranium products and by-products and evaluation of mass balance were carried out. In these tests, it is confirmed that uranium ingots can be obtained with heating the products more than melting temperature of metal uranium under atmospheric pressure because adhered salt cover the uranium not to oxidize it during uranium cohering. Covered salt can be removed after ingot formation. Inside the ingot, there were a lump of uranium and dark brown colored dross was observed. Material balance of uranium is 77 ∼ 96%, that of plutonium is 71 ∼ 109%, and that of americium that is a volatile substance more than uranium and plutonium become 79 ∼ 119%. Volatilization of americium is very small under the condition of high temperature. (authors)

  2. Cost of Czochralski wafers as a function of diameter

    Science.gov (United States)

    Leipold, M. H.; Radics, C.; Kachare, A.

    1980-02-01

    The impact of diameter in the range of 10 to 15 cm on the cost of wafers sliced from Czochralski ingots was analyzed. Increasing silicon waste and decreasing ingot cost with increasing ingot size were estimated along with projected costs. Results indicate a small but continuous decrease in sheet cost with increasing ingot size in this size range. Sheet costs including silicon are projected to be $50 to $60/sq m (1980 $) depending upon technique used.

  3. Solidification Mapping of a Nickel Alloy 718 Laboratory VAR Ingot

    Science.gov (United States)

    Watt, Trevor J.; Taleff, Eric M.; Lopez, Felipe; Beaman, Joe; Williamson, Rodney

    The solidification microstructure of a laboratory-scale Nickel alloy 718 vacuum arc remelted (VAR) ingot was analyzed. The cylindrical, 210-mm-diameter ingot was sectioned along a plane bisecting it length-wise, and this mid-plane surface was ground and etched using Canada's reagent to reveal segregation contrast. Over 350 photographs were taken of the etched mid-plane surface and stitched together to form a single mosaic image. Image data in the resulting mosaic were processed using a variety of algorithms to extract quantities such as primary dendrite orientation, primary dendrite arm spacing (PDAS), and secondary dendrite arm spacing (SDAS) as a function of location. These quantities were used to calculate pool shape and solidification rate during solidification using existing empirical relationships for Nickel Alloy 718. The details and outcomes of this approach, along with the resulting comparison to experimental processing conditions and computational models, are presented.

  4. Peculiarities of the coolant of large ingots in crystallizators of semicontinuous casting machines

    International Nuclear Information System (INIS)

    Tsukerman, V.Ya.; Marchenko, I.K.; Rimen, V.Kh.

    1983-01-01

    Peculiarities of heat transfer in crystallizator of semicontinuous blank casting machine were investigated, taking carbon and chromium-nickel steels as an example. The effect of crystallizator cross-section and decrease of the rate of metal casting on ingot cooling was considered at that. It was established that nonuniformity of deformation of ingot skin as well as the state of crystallizator operating walls affect on heat transfer in crystallizator. Crystallizator structure with ribs in upper part and without ribs in lower cone part is optimal. It provides more uniform skin growth in initial period of solidification and compensation of gap, which appears due to shrinkage

  5. Silicon materials outlook study for 1980-85 calendar years

    Energy Technology Data Exchange (ETDEWEB)

    Costogue, E.; Ferber, R.; Hasbach, W.; Pellin, R.; Yaws, C.

    1979-11-01

    Photovoltaic solar cell arrays converting solar energy into electrical energy can become a cost-effective, alternative energy source provided that an adequate supply of low-priced solar cell materials and automated fabrication techniques are available. Presently, the photovoltaic industry is dependent upon polycrystalline silicon which is produced primarily for the discrete semiconductor device industry. This dependency is expected to continue until DOE-sponsored new technology developments mature. Recent industry forecasts have predicted a limited supply of polycrystalline silicon material and a shortage could occur in the early 80's. The Jet Propulsion Laboratory's Technology Development and Application Lead Center formed an ad hoc committee at JPL, SERI and consultant personnel to conduct interviews with key polycrystalline manufacturers and a large cross-section of single crystal ingot growers and wafer manufacturers. Industry consensus and conclusions reached from the analysis of the data obtained by the committee are reported. The highlight of the study is that there is a high probability of polycrystalline silicon shortage by the end of CY 1982 and a strong seller's market after CY 1981 which will foster price competition for available silicon.

  6. Microstructure and mechanical properties of Al–1Mn and Al–10Si alloy circular clad ingot prepared by direct chill casting

    International Nuclear Information System (INIS)

    Fu, Ying; Jie, Jinchuan; Wu, Li; Park, Joonpyo; Sun, Jianbo; Kim, Jongho; Li, Tingju

    2013-01-01

    An innovative direct chill casting process to prepare Al–10 wt%Si and Al–1 wt%Mn alloy circular clad ingots has been developed in the present study. The experimental casting parameters were determined by theoretical analysis, numerical simulation and experimental processes. The interface of clad ingots was investigated by methods of metallographic examination, electron probe microanalysis (EPMA) and transmission electron microscopy (TEM). The results showed that excellent metallurgical bonding of two different aluminum alloys could be achieved by direct chill casting. The Al–1Mn alloy which was poured into the mold earlier served as the substrate for heterogeneous nucleation of Al–10Si alloy. Because of diffusion of Si and Mn elements, a diffusion layer with a thickness of about 40 μm on average between the Al–10Si and Al–1Mn alloys could be obtained. The tensile strength of the clad ingot was 106.8 MPa and the fractured position was located in the Al–1Mn alloy side, indicating the strength of the interfacial region is higher than that of Al–1Mn alloy.

  7. Effects of silicon cross section and neutron spectrum on the radial uniformity in neutron transmutation doping

    International Nuclear Information System (INIS)

    Kim, Haksung; Ho Pyeon, Cheol; Lim, Jae-Yong; Misawa, Tsuyoshi

    2012-01-01

    The effects of silicon cross section and neutron spectrum on the radial uniformity of a Si-ingot are examined experimentally with various neutron spectrum conditions. For the cross section effect, the numerical results using silicon single crystal cross section reveal good agreements with experiments within relative difference of 6%, whereas the discrepancy is approximately 20% in free-gas cross section. For the neutron spectrum effect, the radial uniformity in hard neutron spectrum is found to be more flattening than that in soft spectrum. - Highlights: ► The effects of silicon cross section and neutron spectrum on the radial uniformity in NTD were experimentally investigated. ► The numerical results using silicon single crystal cross section reveal good agreements. ► The radial uniformity in hard neutron spectrum was more flat than that in soft spectrum. ► The silicon single crystal cross section and hard neutron spectrum are recommended for numerical analyses and radial uniformity flattening in NTD, respectively.

  8. Surface Detail Reproduction and Effect of Disinfectant and Long-Term Storage on the Dimensional Stability of a Novel Vinyl Polyether Silicone Impression Material.

    Science.gov (United States)

    Nassar, Usama; Chow, Ava K

    2015-08-01

    This study investigated the surface detail reproduction and dimensional stability of a vinyl polyether silicone (VPES) in comparison to a vinylpolysiloxane (VPS) material as a function of prolonged storage for up to 2 weeks. Heavy-body VPES (EXA'lence(TM) Fast Set) and VPS (Imprint(TM) 3 Quick Step) were compared. Forty impression ingots of each material were made using a stainless steel die as described by ANSI/ADA specification No. 19. Twenty impressions of each material were disinfected by immersion in a 2.5% buffered glutaraldehyde solution. Surface quality was assessed and scored immediately after making the ingots. Dimensional stability measurements were made immediately and repeated on the same ingots after 7 and 14 days storage in ambient laboratory conditions. Data were analyzed using the D'Agostino and Pearson omnibus normality test followed by two-way repeated measures ANOVA with post hoc Bonferroni tests. Values of p < 0.01 were deemed to be significant. Disinfected VPES and VPS specimens had significantly reduced dimensional changes at 7 and 14 days when compared with the nondisinfected ones (p < 0.0001). The dimensional stability of both materials was within ANSI/ADA specification No. 19's acceptable limit throughout the 2-week test period, regardless of whether they were disinfected. Out of the initial 80 ingots, 8 VPES and 1 VPS ingot scored a 2 on the surface detail test, while the remaining 71 ingots scored 1. Heavy-body fast-set VPES experienced minimal contraction in vitro after prolonged storage, though surface detail scores were not as consistent as those of the VPS tested. The least contraction occurred when the material was examined immediately after ingot production. © 2014 by the American College of Prosthodontists.

  9. Controlling liquid pool depth in VAR of a 21.6 cm diameter ingot of Alloy 718

    Science.gov (United States)

    Lopez, Felipe; Beaman, Joseph; Williamson, Rodney; Taleff, Eric; Watt, Trevor

    It is believed that the final microstructure in vacuum arc remelted (VAR) ingots is strongly influenced by the molten metal pool profile. Thus, if the pool profile was properly controlled during the melt then defect-free microstructures would be obtained. The recent development of a reduced-order model of VAR solidification allowed the design of a pool depth controller to accomplish this task. The controller used a linear quadratic regulator and a Kalman filter to stabilize the melt pool solidification front under the effect of uncertain process dynamics and noisy measurements. Basic Axisymmetric Remelting (BAR), a high-fidelity VAR ingot model, was used in real time to provide pool depth measurements that were incorporated in the control loop. The controller was tested at Los Alamos National Laboratory in a 21.6 diameter Alloy 718 ingot. Details of the controller design will be presented, along with comparisons to experimentally-measured pool depths.

  10. Evolution of ESR Technology and Equipment for Long Hollow Ingots Manufacture

    Science.gov (United States)

    Medovar, Lev; Stovpchenko, Ganna; Dudka, Grigory; Kozminskiy, Alexander; Fedorovskii, Borys; Lebid, Vitalii; Gusiev, Iaroslav

    In this paper development of both ESR technology and equipment for hollow ingot manufacture review and analysis are presented. The real complications of hollow ingot manufacture and some tendentious issues which restrict process dissemination are discussed. An actual data of modern manufacture of as-cast pipes for heat and power engineering by traditional ESR with consumable electrode are given. Results of microstructure and nonmetal inclusion investigations have shown the high quality of as-cast ESR pipes. On the basis of these results the possibility to produce huge ESR hollows (up 5000 mm in dia) with final goal drastically to reduce setting ratio on forged shells and rings or even replace it by ESR hollows as-cast is grounded. Two new ESR technologies — consumable electrodes change and liquid metal usage — have passed pilot tests for heavy hollow production and shown very prospective results to be presented.

  11. Chemical Separation of Fission Products in Uranium Metal Ingots from Electrolytic Reduction Process

    International Nuclear Information System (INIS)

    Lee, Chang-Heon; Kim, Min-Jae; Choi, Kwang-Soon; Jee, Kwang-Yong; Kim, Won-Ho

    2006-01-01

    Chemical characterization of various process materials is required for the optimization of the electrolytic reduction process in which uranium dioxide, a matrix of spent PWR fuels, is electrolytically reduced to uranium metal in a medium of LiCl-Li 2 O molten at 650 .deg. C. In the uranium metal ingots of interest in this study, residual process materials and corrosion products as well as fission products are involved to some extent, which further adds difficulties to the determination of trace fission products. Besides it, direct inductively coupled plasma atomic emission spectrometric (ICP-AES) analysis of uranium bearing materials such as the uranium metal ingots is not possible because a severe spectral interference is found in the intensely complex atomic emission spectra of uranium. Thus an adequate separation procedure for the fission products should be employed prior to their determinations. In present study ion exchange and extraction chromatographic methods were adopted for selective separation of the fission products from residual process materials, corrosion products and uranium matrix. The sorption behaviour of anion and tri-nbutylphosphate (TBP) extraction chromatographic resins for the metals in acidic solutions simulated for the uranium metal ingot solutions was investigated. Then the validity of the separation procedure for its reliability and applicability was evaluated by measuring recoveries of the metals added

  12. Ingot formation using uranium dendrites recovered by electrolysis in LiCl-KCl-PuCl{sub 3}-UCl{sub 3} melt

    Energy Technology Data Exchange (ETDEWEB)

    Mineo Fukushima; Akira Nakayoshi; Shinichi Kitawaki [Japan Atomic Energy Agency (JAEA), 4-33 Muramatsu Tokai-mura Naka-gun, Ibaraki, 319-1194 (Japan); Masaki Kurata; Noboru Yahagi [Central Research Institute of Electric Power Industry (CRIEPI), 2-11-1 Iwadokita Komae-shi, Tokyo, 201-8511 (Japan)

    2008-07-01

    Products on solid cathodes recovered by the metal pyrochemical processing were processed to obtain uranium ingot. Studies on process conditions of uranium formation, assay recovered uranium products and by-products and evaluation of mass balance were carried out. In these tests, it is confirmed that uranium ingots can be obtained with heating the products more than melting temperature of metal uranium under atmospheric pressure because adhered salt cover the uranium not to oxidize it during uranium cohering. Covered salt can be removed after ingot formation. Inside the ingot, there were a lump of uranium and dark brown colored dross was observed. Material balance of uranium is 77 {approx} 96%, that of plutonium is 71 {approx} 109%, and that of americium that is a volatile substance more than uranium and plutonium become 79 {approx} 119%. Volatilization of americium is very small under the condition of high temperature. (authors)

  13. The Mathematical Model of Hydrodynamics and Heat and Mass Transfer at Formation of Steel Ingots and Castings

    Directory of Open Access Journals (Sweden)

    Bondarenko V.I.

    2015-03-01

    Full Text Available The generic mathematical model and computational algorithm considering hydrodynamics, heat and mass transfer processes during casting and forming steel ingots and castings are offered. Usage domains for turbulent, convective and non-convective models are determined depending on ingot geometry and thermal overheating of the poured melt. The expert system is developed, enabling to choose a mathematical model depending on the physical statement of a problem.

  14. Authorized limits for Fernald copper ingots

    Energy Technology Data Exchange (ETDEWEB)

    Frink, N.; Kamboj, S.; Hensley, J.; Chen, S. Y.

    1997-09-01

    This development document contains data and analysis to support the approval of authorized limits for the unrestricted release of 59 t of copper ingots containing residual radioactive material from the U.S. Department of Energy (DOE) Fernald Environmental Management Project (FEMP). The analysis presented in this document comply with the requirements of DOE Order 5400.5, {open_quotes}Radiation Protection of the Public and the Environment,{close_quotes} as well as the requirements of the proposed promulgation of this order as 10 CFR Part 834. The document was developed following the step-by-step process described in the Draft Handbook for Controlling Release for Reuse or Recycle Property Containing Residual Radioactive Material.

  15. Authorized limits for Fernald copper ingots

    International Nuclear Information System (INIS)

    Frink, N.; Kamboj, S.; Hensley, J.; Chen, S.Y.

    1997-09-01

    This development document contains data and analysis to support the approval of authorized limits for the unrestricted release of 59 t of copper ingots containing residual radioactive material from the U.S. Department of Energy (DOE) Fernald Environmental Management Project (FEMP). The analysis presented in this document comply with the requirements of DOE Order 5400.5, open-quotes Radiation Protection of the Public and the Environment,close quotes as well as the requirements of the proposed promulgation of this order as 10 CFR Part 834. The document was developed following the step-by-step process described in the Draft Handbook for Controlling Release for Reuse or Recycle Property Containing Residual Radioactive Material

  16. Multiple batch recharging for industrial CZ silicon growth

    Science.gov (United States)

    Fickett, B.; Mihalik, G.

    2001-05-01

    The Czochralski (CZ) crystal growth process used in the Siemens Solar Industries’ (SSI) Vancouver, WA facility was non-continuous. Each furnace run's production was limited by the size of the starting charge. Once the charge was depleted, the furnace was shut down, cooled, and set back up for the next run. A recharge system was developed which transforms standard CZ growth into a semi-continuous process. Now when the charge is depleted, the crucible can be refilled in situ as the grown ingot is being removed from the furnace. SSI has demonstrated up to 14 recharge cycles in a single run. The resulting benefits included: significant cost reduction, increased yield, increased throughput, reduced energy consumption, improved process capability, reduced material handling requirements, and reduced labor. The recharge system also enables the use of granular silicon, which requires less than 30% of the energy required when manufacturing silicon-starting materials. This significantly reduces the energy “pay-back” time associated with SSI's finished product, photovoltaic panels.

  17. Control of the Gas Flow in an Industrial Directional Solidification Furnace for Production of High Purity Multicrystalline Silicon Ingots

    Directory of Open Access Journals (Sweden)

    Lijun Liu

    2015-01-01

    Full Text Available A crucible cover was designed as gas guidance to control the gas flow in an industrial directional solidification furnace for producing high purity multicrystalline silicon. Three cover designs were compared to investigate their effect on impurity transport in the furnace and contamination of the silicon melt. Global simulations of coupled oxygen (O and carbon (C transport were carried out to predict the SiO and CO gases in the furnace as well as the O and C distributions in the silicon melt. Cases with and without chemical reaction on the cover surfaces were investigated. It was found that the cover design has little effect on the O concentration in the silicon melt; however, it significantly influences CO gas transport in the furnace chamber and C contamination in the melt. For covers made of metal or with a coating on their surfaces, an optimal cover design can produce a silicon melt free of C contamination. Even for a graphite cover without a coating, the carbon concentration in the silicon melt can be reduced by one order of magnitude. The simulation results demonstrate a method to control the contamination of C impurities in an industrial directional solidification furnace by crucible cover design.

  18. Optimization of heat transfer during the directional solidification process of 1600 kg silicon feedstock

    Science.gov (United States)

    Hu, Chieh; Chen, Jyh Chen; Nguyen, Thi Hoai Thu; Hou, Zhi Zhong; Chen, Chun Hung; Huang, Yen Hao; Yang, Michael

    2018-02-01

    In this study, the power ratio between the top and side heaters and the moving velocity of the side insulation are designed to control the shape of the crystal-melt interface during the growth process of a 1600 kg multi-crystalline silicon ingot. The power ratio and insulation gap are adjusted to ensure solidification of the melt. To ensure that the crystal-melt interface is slightly convex in relation to the melt during the entire solidification process, the power ratio should be augmented gradually in the initial stages while being held to a constant value in the middle stages. Initially the gap between the side and the bottom insulation is kept small to reduce thermal stress inside the seed crystals. However, the growth rate will be slow in the early stages of the solidification process. Therefore, the movement of the side insulation is fast in the initial stages but slower in the middle stages. In the later stages, the side insulation gap is fixed. With these modifications, the convexity of the crystal-melt interface in relation to the melt can be maintained during the growth process with an approximately 41% reduction in the thermal stress inside the growing ingot and an 80% reduction in dislocation density along the center line of the ingot compared with the original case.

  19. Analytical/Experimental Investigation of Corpuscular Radiation Detectors

    Science.gov (United States)

    1985-09-15

    with germa- nium and silicon ingots. In our case, we must apply it to ingots of tin, or aluminum , or lead. The impurities problem is alleviated...fundamental proper- ties of this sensor can be summarized as follows. * A silicon block is well suited for thermometric detection of recoil electrons

  20. Development of the irradiation facilities for silicon neutron doping in France

    International Nuclear Information System (INIS)

    Breant, P.; Cherruau, F.; Genthon, J.P.

    1980-08-01

    Irradiation facilities for silicon irradiations in France may be classified in two categories: on the one hand the devices directly implemented in the light water of α swimming-pool reactor and on the other hand the devices implemented in a neutronic medium -heavy water here- providing a high value of the thermal to fast neutron flux ratio. The tools used in France for silicon neutron doping are recapitulated according to this classification in tables, with their main characteristics; in addition it is specified that all existing facilities are instrumented with ingot rotation, flux monitoring, automatic time integration and are associated with handling, storage, cleaning, decontamination and activity control equipment. Finally, concerning the irradiation capacities given in these tables, it is pointed out that they are realistic and present capacities, for presently running devices and according to the way they are used on an average; that is to say that they take into account the real average dimensions of the ingot supplied and not the maximum possible loading with the maximum diameters. Further extensions of capacity are possible if need be by the installation of supplementary standard irradiation modules in the pools. Particular attention will given to the new developments: -new irradiaton facilities with a high Oth/Or ratio being developed in the new research reactor ORPHEE: - developments in the OSIRIS H 2 O reactor. In particular and in connection with the facilities developped in OSIRIS, neutronic problems typical and swimming-pool reactors will be contemplated and the adopted solutions given

  1. Fabrication of a 1200 kg Ingot of V-4Cr-4Ti for the DIII-D Radiative Divertor Program

    International Nuclear Information System (INIS)

    Johnson, W.R.; Smith, J.P.

    1998-01-01

    Vanadium chromium titanium alloys are attractive materials for fusion reactors because of their high temperature capability and their potential for low neutron active and rapid activation decay. A V-4Cr-4Ti alloy has been selected in the U.S. as the current leading candidate vanadium alloy for future use in fusion reactor structural applications. General Atomics (GA), in conjunction with the Department of Energy's (DOE) DIII-D Program, is carrying out a plan for the utilization of this vanadium alloy in the DIII-D tokamak. The plan will culminate in the fabrication, installation, and operation of a V-4Ti alloy structure in the DIII-D Radiative Divertor (RD) upgrade. The deployment of vanadium alloy will provide a meaningful step in the development and technology acceptance of this advanced material for future fusion power devices. Under a GA contract and material specification, an industrial scale 1200 kg heat (ingot) of a V-4Cr-4Ti alloy has been produced and converted into product forms by Wah Chang of Albany, Oregon (WCA). To assure the proper control of minor and trace impurities which affect the mechanical and activation behavior of this vanadium alloy, selected lots of raw vanadium base metal were processed by aluminothermic reduction of high purity vanadium oxide, and were then electron beam melted into two high purity vanadium ingots. The ingots were then consolidated with high purity Cr and Ti, and double vacuum-arc melted to obtain a 1200 kg V-4Cr-4Ti alloy ingot. Several billets were extruded from the ingot, and were then fabricated into plate, sheet, and rod at WCA. Tubing was subsequently processed from plate material. The chemistry and fabrication procedures for the product forms were specified on the basis of experience and knowledge gained from DOE Fusion Materials Program studies on previous laboratory scale heats and a large scale ingot (500 kg)

  2. Production and fabrication of 2500-lb Nb--Ti ingots to rod

    International Nuclear Information System (INIS)

    Cordier, T.E.; McDonald, W.K.

    1975-01-01

    Interest in Nb--Ti superconducting devices is exploding. This paper outlines the critical production criteria for this material. Areas discussed include ingot blending, melting, forging, extrusion, and rod reducing with emphasis on the metallurgical considerations affecting mechanical properties. Data are included relating process parameters to TEM finding as well as R.T. ductility and optical microscopy

  3. Preliminary neutron design of the flux flatter for silicon doping at the RA10

    International Nuclear Information System (INIS)

    Cintas, A.; Bazzana, S.

    2012-01-01

    The neutron transmutation doping of silicon (NTD) is one of the facilities under development for the RA10 project. In order to obtain high quality semiconductor, commercial requirements of NTD include achieving high axial and radial uniformity in the silicon targets. Axial uniformity is achieved locating a neutron screen around the Si ingot, obtaining a flat axial distribution of the dopant concentration. We present the neutron design of this screen, also known as flux flattener. MCNP5 was used to model the screen design. We have reached a satisfactory preliminary screen design after numerous iterations. The fluctuation in the axial distribution of the reaction capture rate ( 30 Si(n,γ) 31 Si) is under ≠1,5%, which is the required level by the semiconductor industry to accept the final product (author)

  4. Optimization of hybrid-type instrumentation for Pu accountancy of U/TRU ingot in pyroprocessing.

    Science.gov (United States)

    Seo, Hee; Won, Byung-Hee; Ahn, Seong-Kyu; Lee, Seung Kyu; Park, Se-Hwan; Park, Geun-Il; Menlove, Spencer H

    2016-02-01

    One of the final products of pyroprocessing for spent nuclear fuel recycling is a U/TRU ingot consisting of rare earth (RE), uranium (U), and transuranic (TRU) elements. The amounts of nuclear materials in a U/TRU ingot must be measured as precisely as possible in order to secure the safeguardability of a pyroprocessing facility, as it contains the most amount of Pu among spent nuclear fuels. In this paper, we propose a new nuclear material accountancy method for measurement of Pu mass in a U/TRU ingot. This is a hybrid system combining two techniques, based on measurement of neutrons from both (1) fast- and (2) thermal-neutron-induced fission events. In technique #1, the change in the average neutron energy is a signature that is determined using the so-called ring ratio method, according to which two detector rings are positioned close to and far from the sample, respectively, to measure the increase of the average neutron energy due to the increased number of fast-neutron-induced fission events and, in turn, the Pu mass in the ingot. We call this technique, fast-neutron energy multiplication (FNEM). In technique #2, which is well known as Passive Neutron Albedo Reactivity (PNAR), a neutron population's changes resulting from thermal-neutron-induced fission events due to the presence or absence of a cadmium (Cd) liner in the sample's cavity wall, and reflected in the Cd ratio, is the signature that is measured. In the present study, it was considered that the use of a hybrid, FNEM×PNAR technique would significantly enhance the signature of a Pu mass. Therefore, the performance of such a system was investigated for different detector parameters in order to determine the optimal geometry. The performance was additionally evaluated by MCNP6 Monte Carlo simulations for different U/TRU compositions reflecting different burnups (BU), initial enrichments (IE), and cooling times (CT) to estimate its performance in real situations. Copyright © 2015 Elsevier Ltd. All

  5. Four-Phase Dendritic Model for the Prediction of Macrosegregation, Shrinkage Cavity, and Porosity in a 55-Ton Ingot

    Science.gov (United States)

    Ge, Honghao; Ren, Fengli; Li, Jun; Han, Xiujun; Xia, Mingxu; Li, Jianguo

    2017-03-01

    A four-phase dendritic model was developed to predict the macrosegregation, shrinkage cavity, and porosity during solidification. In this four-phase dendritic model, some important factors, including dendritic structure for equiaxed crystals, melt convection, crystals sedimentation, nucleation, growth, and shrinkage of solidified phases, were taken into consideration. Furthermore, in this four-phase dendritic model, a modified shrinkage criterion was established to predict shrinkage porosity (microporosity) of a 55-ton industrial Fe-3.3 wt pct C ingot. The predicted macrosegregation pattern and shrinkage cavity shape are in a good agreement with experimental results. The shrinkage cavity has a significant effect on the formation of positive segregation in hot top region, which generally forms during the last stage of ingot casting. The dendritic equiaxed grains also play an important role on the formation of A-segregation. A three-dimensional laminar structure of A-segregation in industrial ingot was, for the first time, predicted by using a 3D case simulation.

  6. Vertical Bridgman growth and characterization of Cd0.95-xMnxZn0.05Te (x=0.20, 0.30) single-crystal ingots

    Energy Technology Data Exchange (ETDEWEB)

    Bolotnikov, A. [Brookhaven National Lab. (BNL), Upton, NY (United States); Kopach, V. [Brookhaven National Lab. (BNL), Upton, NY (United States); Kopach, O. [Brookhaven National Lab. (BNL), Upton, NY (United States); Shcherbak, L. [Brookhaven National Lab. (BNL), Upton, NY (United States); Fochuk, P. [Brookhaven National Lab. (BNL), Upton, NY (United States); Filonenko, S. [Brookhaven National Lab. (BNL), Upton, NY (United States); James, R. [Brookhaven National Lab. (BNL), Upton, NY (United States)

    2017-08-01

    Solid-liquid phase transitions in Cd0.95-xMnxZn0.05Te alloys with x = 0.20 and 0.30 were investigated by differential thermal analysis (DTA). The heating/cooling rates were 5 and 10 K/min with a melt dwell time of 10, 30 and 60 minutes. Cd0.95-xMnxZn0.05Te (x=0.20, 0.30) single-crystal ingots were grown by the vertical Bridgman method guided using the DTA results. Te inclusions (1-20 microns), typical for CdTe and Cd(Zn)Te crystals, were observed in the ingots by infrared transmission microscopy. The measured X-ray diffraction patterns showed that all compositions are found to be in a single phase. Using current-voltage (I-V) measurements, the resistivity of the samples from each ingot was estimated to be about 105 Ohm·cm. The optical transmission analysis demonstrated that the band-gap width of the investigated ingots increased from 1.77 to 1.88 eV with the increase of the MnTe content from 20 to 30 mol. %.

  7. NUMERICAL MODELING OF STRESSES NEAR THE SURFACE IN THE INGOT OF CIRCULAR SECTION, CRYSTALLIZABLE AT CIRCULAR TORCH SECONDARY COOLING

    Directory of Open Access Journals (Sweden)

    A. N. Chichko

    2004-01-01

    Full Text Available The results of computer calculations of the stresses, generated in outside layer of ingot of steel 20 of circular section with diameter 300 mm, in application to one of the industrial technological schemas of RUP “BMZ”, are presented. The segments of compressive and tensile stresses formation along the length of ingot are determined and the principal possibility of production of continuously cast slug of circular section at circular-torch spray cooling is shown.

  8. Deep level transient spectroscopy and minority carrier lifetime study on Ga-doped continuous Czochralski silicon

    Science.gov (United States)

    Yoon, Yohan; Yan, Yixin; Ostrom, Nels P.; Kim, Jinwoo; Rozgonyi, George

    2012-11-01

    Continuous-Czochralski (c-Cz) crystal growth has been suggested as a viable technique for the fabrication of photovoltaic Si wafers due to its low resistivity variation of any dopant, independent of segregation, compared to conventional Cz. In order to eliminate light induced degradation due to boron-oxygen traps in conventional p-type silicon wafers, gallium doped wafers have been grown by c-Cz method and investigated using four point probe, deep level transient spectroscopy (DLTS), and microwave-photoconductance decay. Iron-gallium related electrically active defects were identified using DLTS as the main lifetime killers responsible for reduced non-uniform lifetimes in radial and axial positions of the c-Cz silicon ingot. A direct correlation between minority carrier lifetime and the concentration of electrically active Fe-Ga pairs was established.

  9. Development of an In-Line Minority-Carrier Lifetime Monitoring Tool for Process Control during Fabrication of Crystalline Silicon Solar Cells: Annual Subcontract Report, June 2003 (Revised)

    Energy Technology Data Exchange (ETDEWEB)

    Sinton, R. A.

    2004-04-01

    Under the PV Manufacturing R&D subcontract''Development of an In-Line, Minority-Carrier Lifetime Monitoring Tool for Process Control during Fabrication of Crystalline Silicon Solar Cells'', Sinton Consulting developed prototypes for several new instruments for use in the manufacture of silicon solar cells. These instruments are based on two families of R&D instruments that were previously available, an illumination vs. open-circuit-voltage technique and the quasi-steady state RF photoconductance technique for measuring minority-carrier lifetime. Compared to the previous instruments, the new prototypes are about 20 times faster per measurement, and have automated data analysis that does not require user intervention even when confronted by challenging cases. For example, un-passivated multi-crystalline wafers with large variations in lifetime and trapping behavior can be measured sequentially without error. Five instruments have been prototyped in this project to date, including a block tester for evaluating cast or HEM silicon blocks, a CZ ingot tester, an FZ boule tester for use with long-lifetime silicon, and an in-line sample head for measuring wafers. The CZ ingot tester and the FZ boule tester are already being used within industry and there is interest in the other prototypes. For each instrument, substantial R&D work was required in developing the device physics and analysis as well as for the hardware. This work has been documented in a series of application notes and conference publications, and will result in significant improvements for both the R&D and the industrial types of instruments.

  10. The certification of boron in primary ingot aluminium. BCR No.25

    International Nuclear Information System (INIS)

    Vandecasteele, C.; Colinet, E.

    1984-01-01

    This report sets out the experimental procedures used for the certification of boron in primary ingot aluminium, which has already been certified for carbon and oxygen. Samples were analysed by seven different laboratories using the following methods: spectrophotometry, ICP-emission spectrometry, isotope dilution mass spectrometry, spark source mass spectrometry and charged particle activation analysis. The analytical methods and the statistical approach to analyse the data are described

  11. Continuous Czochralski Growth. Silicon Sheet Growth Development of the Large Area Silicon Sheet Task of the Low Cost Silicon Solar Array Project

    Science.gov (United States)

    Merz, F.

    1979-01-01

    During the reporting period, a successful 100 kilogram run was performed. Six ingots of 13 cm diameter were grown, ranging in size from 15.5 kg to 17.7 kg. Melt replenishment methods included both poly rod and lump feed material. Samples from each ingot were prepared for solar cell fabrication and analyses, impurity analysis, and structural studies. The furnace was converted to the 14-inch hot zone and preliminary heat runs were performed. Two sucessful runs were demonstrated, by growing 25 kg ingots from 30 kg melts. Also, a 100 kg run was attempted, utilizing the 14 inch crucible hot zone, but was prematurely terminated due to excessive monoxide which accumulated on the viewports and a seed failure.

  12. Development and Manufacturing Technology of Prototype Monoblock Low Pressure Rotor Shaft by 650ton Large Ingot

    Energy Technology Data Exchange (ETDEWEB)

    Song, Duk-Yong; Kim, Dong-Soo; Kim, Jungyeup; Lee, Jongwook; Ko, Seokhee [Doosan Heavy Industries and Construction, Changwon(Korea, Republic of)

    2016-10-15

    In order to establish the manufacturing technology for monoblock LP rotor shaft, DHI has produced the prototype monoblock LP rotor shaft with a maximum diameter of φ 2,800 mm using 650 ton ingot and investigated the mechanical properties and the internal quality of the ingot. As a result, the quality and mechanical properties required the large rotor shaft for nuclear power plant met a target. These results indicate that DHI can be contributed to increasing demands with high efficiency and capacity at the nuclear power plant. Additionally, some tests such as high cycle fatigue (HCF), low cycle fatigue (LCF), fracture toughness (K1C/J1C) and dynamic crack propagation velocity (da/dN) are in progress.

  13. Improvement in the reliability of shells for light water reactors by manufacture from hollow ingots

    International Nuclear Information System (INIS)

    Bocquet, P.; Blondeau, R.; Poitrault, I.; Badeau, J.P.; Dumont, R.

    1991-01-01

    The problems associated to the segregation located at the inner surface and subsurface of heavy shell forgings used in nuclear light water reactors are presented. The effect of A segregation on cold or reheat cracking HAZ has conducted fabricators to use severe welding procedures with high preheat temperature and refining HAZ grain size sequences. For shells and rings, the hollow ingot as developed by CLI, with a good control of the location of the center line of segregation, is an excellent answer to these problems. The use of core shell forgings issued from this type of hollow ingots, free of segregation at the inner surface and subsurface area, contributes, by reducing the irradiation embrittlement effect, to increase the safety factor relatively to the risk of failure of the reactor. (orig.)

  14. Inductive ingot heating for extrusion press applications; Induktive Bolzenerwaermung fuer Strangpressanwendungen

    Energy Technology Data Exchange (ETDEWEB)

    Beer, Stefan [I.A.S. Induktions-Anlagen + Service GmbH und Co. KG, Iserlohn (Germany)

    2013-03-15

    Inductive heating of large-format aluminium ingots on modern extrusion press lines generates significant process-engineering benefits. In addition, the proportion of special alloys processed is continuously increasing, accompanied simultaneously by ever smaller production batches, both of which are factors necessitating improvement of and greater flexibility in process-cycle control. This report examines a system concept recently commissioned on one of the world's largest aluminium extrusion presses. (orig.)

  15. Neutron transmutation doping technology of silicon and overview of trial irradiations at Cirus reactor

    International Nuclear Information System (INIS)

    Singh, Tej; Bhatnagar, Anil; Singh, Kanchhi; Raina, V.K.

    2007-12-01

    Neutron transmutation doped silicon (NTD-Si) has been used extensively in manufacturing of high power semiconductor devices. The quality of NTD-Si, both from view points of dopant concentration and homogeneity has been found superior to the quality of doped silicon produced by conventional methods. The technology of NTD-Si has been perfected to achieve more accurate resistivity and homogenous resistivity with complete elimination of hot spots. In addition, the greater spatial uniformity, as well as the precise control over the resistivity achievable by using the NTD process, has led to a substantial increase in the breakdown voltage capability of thyristors. The report describes the fundamentals of NTD-Si production and discusses various techniques used for control of dopant concentration and homogeneity. Various aspects like radiation damage, residual radio-activity, nuclear heating, surface contamination and annealing requirements of the silicon ingots after irradiation have also been discussed. Details of trail irradiation and characterization of NTD-Si samples have been provided. Future plans for production of NTD-Si in Cirus and Dhruva reactors have also been discussed. (author)

  16. Silicon Sheet Growth Development for the Large Area Sheet Task of the Low Cost Solar Array Project. Heat Exchanger Method - Ingot Casting Fixed Abrasive Method - Multi-Wire Slicing

    Science.gov (United States)

    Schmid, F.; Khattak, C. P.

    1978-01-01

    Solar cells fabricated from HEM cast silicon yielded up to 15% conversion efficiencies. This was achieved in spite of using unpurified graphite parts in the HEM furnace and without optimization of material or cell processing parameters. Molybdenum retainers prevented SiC formation and reduced carbon content by 50%. The oxygen content of vacuum cast HEM silicon is lower than typical Czochralski grown silicon. Impregnation of 45 micrometers diamonds into 7.5 micrometers copper sheath showed distortion of the copper layer. However, 12.5 micrometers and 15 micrometers copper sheath can be impregnated with 45 micrometers diamonds to a high concentration. Electroless nickel plating of wires impregnated only in the cutting edge showed nickel concentration around the diamonds. This has the possibility of reducing kerf. The high speed slicer fabricated can achieve higher speed and longer stroke with vibration isolation.

  17. Positive segregation as a function of buoyancy force during steel ingot solidification

    International Nuclear Information System (INIS)

    Radovic, Zarko; Jaukovic, Nada; Lalovic, Milisav; Tadic, Nebojsa

    2008-01-01

    We analyze theoretically and experimentally solute redistribution in the dendritic solidification process and positive segregation during solidification of steel ingots. Positive segregation is mainly caused by liquid flow in the mushy zone. Changes in the liquid steel velocity are caused by the temperature gradient and by the increase in the solid fraction during solidification. The effects of buoyancy and of the change in the solid fraction on segregation intensity are analyzed. The relationships between the density change, liquid fraction and the steel composition are considered. Such elements as W, Ni, Mo and Cr decrease the effect of the density variations, i.e. they show smaller tendency to segregate. Based on the modeling and experimental results, coefficients are provided controlling the effects of chemical composition, secondary dendrite arm spacing and the solid fraction.

  18. An attempt to specify thermal history in CZ silicon wafers and possibilities for its modification

    International Nuclear Information System (INIS)

    Kissinger, G.; Sattler, A.; Mueller, T.; Ammon, W. von

    2007-01-01

    The term thermal history of silicon wafers represents the whole variety of process parameters of crystal growth. The aim of this contribution is an attempt to specify thermal history by one parameter that is directly correlated to the bulk microdefect density. The parameter that reflects thermal history and correlates it with nucleation of oxide precipitates is the concentration of VO 2 complexes. The VO 2 concentration in silicon wafers is too low to be measured by FTIR but it can be obtained from the loss of interstitial oxygen during a standardized thermal treatment. Based on this, the vacancy concentration frozen during crystal cooling in the ingot can be calculated. RTA treatments above 1150 deg. C create a well defined level of the VO 2 concentration in silicon wafers. This means that a well controlled modification of the thermal history is possible. We also investigated the kinetics of reduction of the as-grown excess VO 2 concentration during RTA treatments at 950 deg. C and 1050 deg. C and the effectiveness of this attempt to totally delete the thermal history

  19. Thermal Stability of Zone Melting p-Type (Bi, Sb)2Te3 Ingots and Comparison with the Corresponding Powder Metallurgy Samples

    Science.gov (United States)

    Jiang, Chengpeng; Fan, Xi'an; Hu, Jie; Feng, Bo; Xiang, Qiusheng; Li, Guangqiang; Li, Yawei; He, Zhu

    2018-04-01

    During the past few decades, Bi2Te3-based alloys have been investigated extensively because of their promising application in the area of low temperature waste heat thermoelectric power generation. However, their thermal stability must be evaluated to explore the appropriate service temperature. In this work, the thermal stability of zone melting p-type (Bi, Sb)2Te3-based ingots was investigated under different annealing treatment conditions. The effect of service temperature on the thermoelectric properties and hardness of the samples was also discussed in detail. The results showed that the grain size, density, dimension size and mass remained nearly unchanged when the service temperature was below 523 K, which suggested that the geometry size of zone melting p-type (Bi, Sb)2Te3-based materials was stable below 523 K. The power factor and Vickers hardness of the ingots also changed little and maintained good thermal stability. Unfortunately, the thermal conductivity increased with increasing annealing temperature, which resulted in an obvious decrease of the zT value. In addition, the thermal stabilities of the zone melting p-type (Bi, Sb)2Te3-based materials and the corresponding powder metallurgy samples were also compared. All evidence implied that the thermal stabilities of the zone-melted (ZMed) p-type (Bi, Sb)2Te3 ingots in terms of crystal structure, geometry size, power factor (PF) and hardness were better than those of the corresponding powder metallurgy samples. However, their thermal stabilities in terms of zT values were similar under different annealing temperatures.

  20. Proposed sale of radioactively contaminated nickel ingots located at the Paducah Gaseous Diffusion Plant, Paducah, Kentucky

    International Nuclear Information System (INIS)

    1995-10-01

    The U.S. Department of Energy (DOE) proposes to sell 8,500 radioactively contaminated nickel ingots (9.350 short tons), currently in open storage at the Paducah Gaseous Diffusion Plant (PGDP), to Scientific Ecology Group, Inc. (SEG) for decontamination and resale on the international market. SEG would take ownership of the ingots when they are loaded for transport by truck to its facility in Oak Ridge, Tennessee. SEG would receive approximately 200 short tons per month over approximately 48 months (an average of 180 ingots per month). The nickel decontamination process specified in SEG's technical proposal is considered the best available technology and has been demonstrated in prototype at SEG. The resultant metal for resale would have contamination levels between 0.3 and 20 becquerel per gram (Bq/g). The health hazards associated with release of the decontaminated nickel are minimal. The activity concentration of the end product would be further reduced when the nickel is combined with other metals to make stainless steel. Low-level radioactive waste from the SEG decontamination process, estimated to be approximately 382 m 3 (12,730 ft), would be shipped to a licensed commercial or DOE disposal facility. If the waste were packaged in 0.23 m 3 -(7.5 ft 3 -) capacity drums, approximately 1,500 to 1,900 drums would be transported over the 48-month contract period. Impacts from the construction of decontamination facilities and the selected site are minimal

  1. Obtention of uranium-molybdenum alloy ingots microstructure and phase characterization

    Energy Technology Data Exchange (ETDEWEB)

    Pedrosa, Tercio A.; Braga, Daniel M.; Paula, Joao Bosco de; Brina, Jose Giovanni M.; Ferraz, Wilmar B., E-mail: tap@cdtn.b, E-mail: bragadm@cdtn.b, E-mail: jbp@cdtn.b, E-mail: jgmb@cdtn.b, E-mail: ferrazw@cdtn.b [Centro de Desenvolvimento da Tecnologia Nuclear (CDTN/CNEN-MG), Belo Horizonte, MG (Brazil)

    2011-07-01

    The replacement of high enriched uranium (U-{sup 235} > 85 wt%) by low enriched uranium (U-{sup 235} < 20 wt%) nuclear fuels in research and test reactors is being implemented as an initiative of the Reduced Enrichment for Research and Test Reactors (RERTR) program, conceived in the USA since mid-70s, in order to avoid nuclear weapons proliferation. Such replacement implies in the use of compounds or alloys with higher uranium densities. Several uranium alloys that fill this requirement has been investigated since then. Among these alloys, U-Mo presents great application potential due to its physical properties and good behavior during irradiation, which makes it an important option as a nuclear fuel material for the Brazilian Multipurpose Reactor - RMB. The development of the plate-type nuclear fuel based on U-Mo alloys is being performed at the Nuclear Technology Development Centre (CDTN) and also at the Institute of Energetic and Nuclear Research - IPEN. U-{sup 10}Mo ingots were melted in an induction furnace with protective argon atmosphere. The microstructure of the ingots were characterized through optical and scanning electronic microscopy in the as cast and heat treated conditions. Energy Dispersive Spectrometry and X-Ray Diffraction were used as characterization techniques for elemental analysis and phases determination. It was confirmed the presence of metastable gamma-phase in the as cast condition, surrounded by hypereutectoid alpha-phase (uranium-rich phase), as well as a pearlite-like constituent, composed by alternated lamellas of U{sub 2}Mo compound and alpha-phase, in the heat treated condition. (author)

  2. Preparation of uranium ingots from double fluorides

    International Nuclear Information System (INIS)

    Le Boulbin, E.

    1967-05-01

    A simple method has been developed for the preparation of uranium double fluorides and has given a new impetus to the study of the reduction of these compounds with a view to obtaining very pure uranium ingots. This reduction can be carried out using calcium or magnesium as the reducing agent, this latter metal being very interesting from the practical point of view. A comparative study of the heat balances of the reduction processes for the double fluorides and for uranium tetrafluoride has shown that reduction of the double fluorides is possible. The exact experimental conditions for these reductions have been determined. Our study has shown in particular that the reduction of the double salt UF 4 , CaF 2 by magnesium leads to the production of small (20 to 500 g) samples of high-purity uranium with a yield of 99 per cent. (author) [fr

  3. On the cooling rate of strip cast ingots for sintered NdFeB magnets

    Energy Technology Data Exchange (ETDEWEB)

    Yu, L.Q. [State Key Lab of Silicon Materials, Zhejiang University, Hangzhou 310027 (China); Yan, M. [State Key Lab of Silicon Materials, Zhejiang University, Hangzhou 310027 (China)]. E-mail: mse_yanmi@dial.zju.edu.cn; Wu, J.M. [State Key Lab of Silicon Materials, Zhejiang University, Hangzhou 310027 (China); Luo, W. [State Key Lab of Silicon Materials, Zhejiang University, Hangzhou 310027 (China); Cui, X.G. [State Key Lab of Silicon Materials, Zhejiang University, Hangzhou 310027 (China); Ying, H.G. [State Key Lab of Silicon Materials, Zhejiang University, Hangzhou 310027 (China)

    2007-04-30

    Effects of the cooling rate of strip cast ingots on magnetic properties of sintered NdFeB magnets were studied. It is found that the magnetic properties greatly depend on wheel speed due to different alloy microstructures, which affect readily the particle size distribution of powders obtained after the subsequent jet milling. At higher cooling rate, interlamellar spacing between Nd-rich platelets of the alloy was small, resulting in a lower saturated magnetization due to increased amounts of small particles after jet milling. With further decreasing cooling rate, the resultant larger interlamellar spacing led to too large particle sizes as well as a more irregular shape; thus deteriorated the magnetic properties of the final magnet. A model was developed to disclose the effects of particle sizes on the magnetic alignment process. In the current investigation, optimum magnetic properties of the final magnets were obtained with a cooling rate of 2.6 m/s for preparing the strip. The magnets made by conventionally cast ingot technique exhibited the lowest magnetic properties because of the slowest cooling rate.

  4. Continuous Czochralski growth: Silicon sheet growth development of the large area silicon sheet task of the Low Cost Silicon Solar Array project

    Science.gov (United States)

    1978-01-01

    The primary objective of this contract is to develop equipment and methods for the economic production of single crystal ingot material by the continuous Czochralski (CZ) process. Continuous CZ is defined for the purpose of this work as the growth of at least 100 kilograms of ingot from only one melt container. During the reporting period (October, 1977 - September, 1978), a modified grower was made fully functional and several recharge runs were performed. The largest run lasted 44 hours and over 42 kg of ingot was produced. Little, if any, degradation in efficiency was observed as a result of pulling multiple crystals from one crucible. Solar efficiencies observed were between 9.3 and 10.4% AMO (13.0 and 14.6% AMI) compared to 10.5% (14.7% AMI) for optimum CZ material control samples. Using the SAMICS/IPEG format, economic analysis of continuous CZ suggests that 1986 DoE cost goals can only be met by the growth of large diameter, large mass crystals.

  5. Production of Solar Grade (SoG) Silicon by Refining Liquid Metallurgical Grade (MG) Silicon: Final Report, 19 April 2001; FINAL

    International Nuclear Information System (INIS)

    Khattack, C. P.; Joyce, D. B.; Schmid, F.

    2001-01-01

    This report summarizes the results of the developed technology for producing SoG silicon by upgrading MG silicon with a cost goal of$20/kg in large-scale production. A Heat Exchanger Method (HEM) furnace originally designed to produce multicrystalline ingots was modified to refine molten MG silicon feedstock prior to directional solidification. Based on theoretical calculations, simple processing techniques, such as gas blowing through the melt, reaction with moisture, and slagging have been used to remove B from molten MG silicon. The charge size was scaled up from 1 kg to 300 kg in incremental steps and effective refining was achieved. After the refining parameters were established, improvements to increase the impurity reduction rates were emphasized. With this approach, 50 kg of commercially available as-received MG silicon was processed for a refining time of about 13 hours. A half life of and lt;2 hours was achieved, and the B concentration was reduced to 0.3 ppma and P concentration to 10 ppma from the original values of 20 to 60 ppma, and all other impurities to and lt;0.1 ppma. Achieving and lt;1 ppma B by this simple refining technique is a breakthrough towards the goal of achieving low-cost SoG silicon for PV applications. While the P reduction process was being optimized, the successful B reduction process was applied to a category of electronics industry silicon scrap previously unacceptable for PV feedstock use because of its high B content (50-400 ppma). This material after refining showed that its B content was reduced by several orders of magnitude, to(approx)1 ppma (0.4 ohm-cm, or about 5x1016 cm-3). NREL's Silicon Materials Research team grew and wafered small and lt;100 and gt; dislocation-free Czochralski (Cz) crystals from the new feedstock material for diagnostic tests of electrical properties, C and O impurity levels, and PV performance relative to similar crystals grown from EG feedstock and commercial Cz wafers. The PV conversion

  6. Disposal of metal fragments released during polycrystalline slicing by multi-wire saw

    Science.gov (United States)

    Boutouchent-Guerfi, N.; Drouiche, N.; Medjahed, S.; Ould-Hamou, M.; Sahraoui, F.

    2016-08-01

    The environmental and economic impacts linked with solar systems are largely based on discharges of slurry generated during the various stages of sawing and cutting ingots. These discharges into the environment are subject to the general regulations on hazardous and special industrial waste disposal. Therefore, they should not be abandoned or burned in open air. The cutting of Silicon ingots leads to the production of Silicon wafers additional costs, losing more than 30% of Silicon material. Abrasive grains (Silicon Carbide) trapped between the wire and the block of Silicon need to be removed by various mechanisms to be later evacuated by slurry fragments. In the interest of decreasing operational costs during polycrystalline ingot slicing at Semiconductors Research Center, and, avoid environmental problems; it is necessary to recover the solar grade Silicon from the Silicon sawing waste. For this reason, the removal of metal fragments has become a preliminary requirement to regenerate the slurry; in addition, the solid phase needs to be separated from the liquid phase after the dissolution PEG with the solvent. In the present study, magnetic separation and centrifugation methods were adopted for metals removal, followed by the analysis of some operating parameters such as: washing time, pH, and initial concentration of Silicon. Finally, analytical, morphological and basic methods were performed in order to evaluate the efficiency of the process undertaken.

  7. Randomized controlled trial assessing the efficacy of a reusable fish-shaped iron ingot to increase hemoglobin concentration in anemic, rural Cambodian women.

    Science.gov (United States)

    Rappaport, Aviva I; Whitfield, Kyly C; Chapman, Gwen E; Yada, Rickey Y; Kheang, Khin Meng; Louise, Jennie; Summerlee, Alastair J; Armstrong, Gavin R; Green, Timothy J

    2017-08-01

    Background: Anemia affects 45% of women of childbearing age in Cambodia. Iron supplementation is recommended in populations in which anemia prevalence is high. However, there are issues of cost, distribution, and adherence. A potential alternative is a reusable fish-shaped iron ingot, which, when added to the cooking pot, leaches iron into the fluid in which it is prepared. Objective: We sought to determine whether there was a difference in hemoglobin concentrations in rural Cambodian anemic women (aged 18-49 y) who cooked with the iron ingot or consumed a daily iron supplement compared with a control after 1 y. Design: In Preah Vihear, 340 women with mild or moderate anemia were randomly assigned to 1 ) an iron-ingot group, 2 ) an iron-supplement (18 mg/d) group, or 3 ) a nonplacebo control group. A venous blood sample was taken at baseline and at 6 and 12 mo. Blood was analyzed for hemoglobin, serum ferritin, and serum transferrin receptor. Hemoglobin electrophoresis was used to detect structural hemoglobin variants. Results: Anemia prevalence was 44% with the use of a portable hemoglobinometer during screening. At baseline, prevalence of iron deficiency was 9% on the basis of a low serum ferritin concentration. There was no significant difference in mean hemoglobin concentrations between the iron-ingot group (115 g/L; 95% CI: 113, 118 g/L; P = 0.850) or iron-supplement group (115 g/L; 95% CI: 113, 117 g/L; P = 0.998) compared with the control group (115 g/L; 95% CI: 113, 117 g/L) at 12 mo. Serum ferritin was significantly higher in the iron-supplement group (73 μg/L; 95% CI: 64, 82 μg/L; P = 0.002) than in the control group at 6 mo; however, this significance was not maintained at 12 mo (73 μg/L; 95% CI: 58, 91 μg/L; P = 0.176). Conclusions: Neither the iron ingot nor iron supplements increased hemoglobin concentrations in this population at 6 or 12 mo. We do not recommend the use of the fish-shaped iron ingot in Cambodia or in countries where the prevalence

  8. Review of ingot niobium as a material for superconducting radiofrequency accelerating cavities

    Energy Technology Data Exchange (ETDEWEB)

    Kneisel, P., E-mail: kneisel@jlab.org [Jefferson Lab, Newport News, VA 23606 (United States); Ciovati, G.; Dhakal, P. [Jefferson Lab, Newport News, VA 23606 (United States); Saito, K. [Michigan State University, East Lansing, MI 48824 (United States); Singer, W.; Singer, X. [DESY, Notkestrasse 85, D-22607 Hamburg (Germany); Myneni, G.R., E-mail: rao@jlab.org [Jefferson Lab, Newport News, VA 23606 (United States)

    2015-02-21

    As a result of collaboration between Jefferson Lab and niobium manufacturer Companhia Brasileira de Metalurgia e Mineração (CBMM), ingot niobium was explored as a possible material for superconducting radiofrequency (SRF) cavity fabrication. The first single cell cavity from large-grain high purity niobium was fabricated and successfully tested at Jefferson Lab in 2004. This work triggered research activities in other SRF laboratories around the world. Large-grain (LG) niobium became not only an interesting alternative material for cavity builders, but also material scientists and surface scientists were eager to participate in the development of this technology. Many single cell cavities made from material of different suppliers have been tested successfully and several multi-cell cavities have shown performances comparable to the best cavities made from standard fine-grain niobium. Several 9-cell cavities fabricated by Research Instruments and tested at DESY exceeded the best performing fine grain cavities with a record accelerating gradient of E{sub acc}=45.6 MV/m. The quality factor of those cavities was also higher than that of fine-grain (FG) cavities processed with the same methods. Such performance levels push the state-of-the art of SRF technology and are of great interest for future accelerators. This contribution reviews the development of ingot niobium technology and highlights some of the differences compared to standard FG material and opportunities for further developments.

  9. Behavior of Particle Depots in Molten Silicon During Float-Zone Growth in Strong Magnetic Fields

    Science.gov (United States)

    Jauss, T.; Croell, A.; SorgenFrei, T.; Azizi, M.; Reimann, C.; Friedrich, J.; Volz, M. P.

    2014-01-01

    Solar cells made from directionally solidified silicon cover 57% of the photovoltaic industry's market [1]. One major issue during directional solidification of silicon is the precipitation of foreign phase particles. These particles, mainly SiC and Si3N4, are precipitated from the dissolved crucible coating, which is made of silicon nitride, and the dissolution of carbon monoxide from the furnace atmosphere. Due to their hardness and size of several hundred micrometers, those particles can lead to severe problems during the wire sawing process for wafering the ingots. Additionally, SiC particles can act as a shunt, short circuiting the solar cell. Even if the particles are too small to disturb the wafering process, they can lead to a grit structure of silicon micro grains and serve as sources for dislocations. All of this lowers the yield of solar cells and reduces the performance of cells and modules. We studied the behaviour of SiC particle depots during float-zone growth under an oxide skin, and strong static magnetic fields. For high field strengths of 3T and above and an oxide layer on the sample surface, convection is sufficiently suppressed to create a diffusive like regime, with strongly dampened convection [2, 3]. To investigate the difference between atomically rough phase boundaries and facetted growth, samples with [100] and [111] orientation were processed.

  10. Formation of hypereutectic silicon particles in hypoeutectic Al-Si alloys under the influence of high-intensity ultrasonic vibration

    Directory of Open Access Journals (Sweden)

    Xiaogang Jian

    2013-03-01

    Full Text Available The modification of eutectic silicon is of general interest since fine eutectic silicon along with fine primary aluminum grains improves mechanical properties and ductilities. In this study, high intensity ultrasonic vibration was used to modify the complex microstructure of aluminum hypoeutectic alloys. The ultrasonic vibrator was placed at the bottom of a copper mold with molten aluminum. Hypoeutectic Al-Si alloy specimens with a unique in-depth profile of microstructure distribution were obtained. Polyhedral silicon particles, which should form in a hypereutectic alloy, were obtained in a hypoeutectic Al-Si alloy near the ultrasonic radiator where the silicon concentration was higher than the eutectic composition. The formation of hypereutectic silicon near the radiator surface indicates that high-intensity ultrasonic vibration can be used to influence the phase transformation process of metals and alloys. The size and morphology of both the silicon phase and the aluminum phase varies with increasing distance from the ultrasonic probe/radiator. Silicon morphology develops into three zones. Polyhedral primary silicon particles present in zone I, within 15 mm from the ultrasonic probe/radiator. Transition from hypereutectic silicon to eutectic silicon occurs in zone II about 15 to 20 祄 from the ultrasonic probe/radiator. The bulk of the ingot is in zone III and is hypoeutectic Al-Si alloy containing fine lamellar and fibrous eutectic silicon. The grain size is about 15 to 25 祄 in zone I, 25 to 35 祄 in zone II, and 25 to 55 祄 in zone III. The morphology of the primary ?Al phase is also changed from dendritic (in untreated samples to globular. Phase evolution during the solidification process of the alloy subjected to ultrasonic vibration is described.

  11. Copper alloys with improved properties: standard ingot metallurgy vs. powder metallurgy

    Directory of Open Access Journals (Sweden)

    Milan T. Jovanović

    2014-09-01

    Full Text Available Three copper-based alloys: two composites reinforced with Al2O3 particles and processed through powder metallurgy (P/M route, i.e. by internal oxidation (Cu-2.5Al composite and by mechanical alloying (Cu-4.7Al2O3 and Cu-0.4Cr-0.08Zr alloy produced by ingot metallurgy (vacuum melting and casting were the object of this investigation. Light microscope and scanning electron microscope (SEM equipped with electron X-ray spectrometer (EDS were used for microstructural characterization. Microhardness and electrical conductivity were also measured. Compared to composite materials, Cu-0.4Cr-0.08Zr alloy possesses highest electrical conductivity in the range from 20 to 800 ℃, whereas the lowest conductivity shows composite Cu-2.5Al processed by internal oxidation. In spite to somewhat lower electrical conductivity (probably due to inadequate density, Cu-2.5Al composite exhibits thermal stability enabling its application at much higher temperatures than materials processed by mechanical alloying or by vacuum melting and casting.

  12. Cellular dislocations patterns in monolike silicon: Influence of stress, time under stress and impurity doping

    Science.gov (United States)

    Oliveira, V. A.; Rocha, M.; Lantreibecq, A.; Tsoutsouva, M. G.; Tran-Thi, T. N.; Baruchel, J.; Camel, D.

    2018-05-01

    Besides the well-known local sub-grain boundaries (SGBs) defects, monolike Si ingots grown by Directional Solidification present distributed background cellular dislocation structures. In the present work, the influence of stress level, time under stress, and doping by O and Ge, on the formation of dislocation cells in monolike silicon, is analysed. This is achieved by performing a comparative study of the dislocation structures respectively obtained during crystallisation of pilot scale monolike ingots on Czochralski (CZ) and monolike seeds, during annealing of Float Zone (FZ), CZ, and 1 × 1020 at/cm3 Ge-doped CZ (GCZ) samples, and during 4-point bending of FZ and GCZ samples at 1300 °C under resolved stresses of 0.3, 0.7 and 1.9 MPa during 1-20 h. Synchrotron X-ray White-beam Topography and Rocking Curve Imaging (RCI) are applied to visualize the dislocation arrangements and to quantify the spatial distribution of the associated lattice distortions. Annealed samples and samples bent under 0.3 MPa present dislocation structures corresponding to transient creep stages where dislocations generated from surface defects are propagating and multiplying in the bulk. The addition of the hardening element Ge is found to block the propagation of dislocations from these surface sources during the annealing test, and to retard dislocation multiplication during bending under 0.3 MPa. On the opposite, cellular structures corresponding to the final stationary creep stage are obtained both in the non-molten seeds and grown part of monolike ingots and in samples bent under 0.7 and 1.9 MPa. A comparative discussion is made of the dynamics of formation of these final dislocation structures during deformation at high temperature and monolike growth.

  13. The Linear Thermal Expansion of Bulk Nanocrystalline Ingot Iron from Liquid Nitrogen to 300 K.

    Science.gov (United States)

    Wang, S G; Mei, Y; Long, K; Zhang, Z D

    2009-09-17

    The linear thermal expansions (LTE) of bulk nanocrystalline ingot iron (BNII) at six directions on rolling plane and conventional polycrystalline ingot iron (CPII) at one direction were measured from liquid nitrogen temperature to 300 K. Although the volume fraction of grain boundary and residual strain of BNII are larger than those of CPII, LTE of BNII at the six measurement directions were less than those of CPII. This phenomenon could be explained with Morse potential function and the crystalline structure of metals. Our LTE results ruled out that the grain boundary and residual strain of BNII did much contribution to its thermal expansion. The higher interaction potential energy of atoms, the less partial derivative of interaction potential energy with respect to temperature T and the porosity free at the grain boundary of BNII resulted in less LTE in comparison with CPII from liquid nitrogen temperature to 300 K. The higher LTE of many bulk nanocrystalline materials resulted from the porosity at their grain boundaries. However, many authors attributed the higher LTE of many nanocrystalline metal materials to their higher volume fraction of grain boundaries.

  14. The Linear Thermal Expansion of Bulk Nanocrystalline Ingot Iron from Liquid Nitrogen to 300 K

    Directory of Open Access Journals (Sweden)

    Mei Y

    2009-01-01

    Full Text Available Abstract The linear thermal expansions (LTE of bulk nanocrystalline ingot iron (BNII at six directions on rolling plane and conventional polycrystalline ingot iron (CPII at one direction were measured from liquid nitrogen temperature to 300 K. Although the volume fraction of grain boundary and residual strain of BNII are larger than those of CPII, LTE of BNII at the six measurement directions were less than those of CPII. This phenomenon could be explained with Morse potential function and the crystalline structure of metals. Our LTE results ruled out that the grain boundary and residual strain of BNII did much contribution to its thermal expansion. The higher interaction potential energy of atoms, the less partial derivative of interaction potential energy with respect to temperature T and the porosity free at the grain boundary of BNII resulted in less LTE in comparison with CPII from liquid nitrogen temperature to 300 K. The higher LTE of many bulk nanocrystalline materials resulted from the porosity at their grain boundaries. However, many authors attributed the higher LTE of many nanocrystalline metal materials to their higher volume fraction of grain boundaries.

  15. The influence of the mould cooling temperature on the surface appearance and the internal quality of ESR ingots

    Science.gov (United States)

    Kubin, M.; Ofner, B.; Holzgruber, H.; Schneider, R.; Enzenhofer, D.; Filzwieser, A.; Konetschnik, S.

    2016-07-01

    One of the main benefits of the ESR process is to obtain an ingot surface which is smooth and allows a subsequent forging operation without any surface dressing. The main influencing factor on surface quality is the precise controlling of the process such as melt rate and electrode immersion depth. However, the relatively strong cooling effect of water as a cooling medium can result in the solidification of the meniscus of the liquid steel on the boundary liquid steel and slag which is most likely the origin of surface defects. The usage of different cooling media like ionic liquids, a salt solution which can be heated up to 250°C operating temperature might diminish the meniscus solidification phenomenon. This paper shows the first results of the usage of an ionic liquid as a mould cooling medium. In doing so, 210mm diameter ESR ingots were produced with the laboratory scale ESR furnace at the university of applied science using an ionic liquid cooling device developed by the company METTOP. For each trial melt different inlet and outlet temperatures of the ionic liquid were chosen and the impact on the surface appearance and internal quality were analyzed. Furthermore the influence on the energy balance is also briefly highlighted. Ultimately, an effect of the usage of ionic liquids as a cooling medium could be determined and these results will be described in detail within the scope of this paper.

  16. Ge-Si single crystal growth when the begining of an ingot prepared by a new method is used as the begining of the feeding alloy

    International Nuclear Information System (INIS)

    Tahirov, V.I.; Quliyev, A.F.; Hasanov, Z.Y.; Qahramanov, N.F.

    2008-01-01

    Ge-Si system is used to describe binary solid solution single crystal growth when the beginning of the ingot prepared by a new method is used as the beginning of the feeding alloy. At first the feeding ingot is prepared by Bridgman method, then it is exposed to the zone melting. Content distribution of the feeding alloy and the grown crystal is determined by solving the continuity equation. The crystals grown by this method can be used for construction of the vary-zone structures

  17. Development and pilot production of three ingot-source beryllium sheet metal parts

    International Nuclear Information System (INIS)

    Floyd, D.R.

    1975-01-01

    Results of an extensive development program aimed at making three, separate, structural components from beryllium, using sheet-metal fabrication methods, are presented. Ingot-source beryllium sheet at thicknesses of 0.100, 0.125, and 0.170 inch is formed in a fully-recrystallized and in a partially-recrystallized condition. The tensile yield strength is 26,000 psi after full recrystallization. After partial recrystallization, tensile yield strength is between 35,000 and 45,000 psi, depending upon sheet thickness, heat treat temperature, and time at temperature. The high yield strength is retained in the parts after forming. (U.S.)

  18. Silicon epitaxy on textured double layer porous silicon by LPCVD

    International Nuclear Information System (INIS)

    Cai Hong; Shen Honglie; Zhang Lei; Huang Haibin; Lu Linfeng; Tang Zhengxia; Shen Jiancang

    2010-01-01

    Epitaxial silicon thin film on textured double layer porous silicon (DLPS) was demonstrated. The textured DLPS was formed by electrochemical etching using two different current densities on the silicon wafer that are randomly textured with upright pyramids. Silicon thin films were then grown on the annealed DLPS, using low-pressure chemical vapor deposition (LPCVD). The reflectance of the DLPS and the grown silicon thin films were studied by a spectrophotometer. The crystallinity and topography of the grown silicon thin films were studied by Raman spectroscopy and SEM. The reflectance results show that the reflectance of the silicon wafer decreases from 24.7% to 11.7% after texturing, and after the deposition of silicon thin film the surface reflectance is about 13.8%. SEM images show that the epitaxial silicon film on textured DLPS exhibits random pyramids. The Raman spectrum peaks near 521 cm -1 have a width of 7.8 cm -1 , which reveals the high crystalline quality of the silicon epitaxy.

  19. The electrochemical corrosion of bulk nanocrystalline ingot iron in HCl solutions with different concentrations

    International Nuclear Information System (INIS)

    Wang, S.G.; Sun, M.; Cheng, P.C.; Long, K.

    2011-01-01

    Highlights: → The corrosion resistance of BNII was enhanced in comparison with CPII in 0.1-0.4 mol L -1 solution. → The function work of BNII is 0.47 eV larger that of CPII. → The energy state density of 4s electrons of BNII is 13.73% less than that of CPII. → BNII corrosion resistance was enhanced due to its larger work function and less 4s electrons weight. → The specific adsorption of Cl - on BNII was weaker than that of CPII due to its larger function work. - Abstract: We studied the corrosion properties of bulk nanocrystalline ingot iron (BNII) and conventional polycrystalline ingot iron (CPII) in HCl solutions from 0.1 mol L -1 to 0.4 mol L -1 at room temperature. The corrosion resistance of BNII was enhanced in comparison with CPII. We investigated the surface energy state densities of BNII and CPII with ultra-violet photoelectron spectroscopy. The energy state density of BNII 4s electrons was 13.73% less than that of CPII. The function work of BNII was 0.47 eV larger that of CPII. The corrosion resistance of BNII was enhanced in comparison with CPII due to its less energy state density of 4s electrons, larger work function and weaker Cl - specific adsorption.

  20. Photoluminescence and electrical properties of silicon oxide and silicon nitride superlattices containing silicon nanocrystals

    International Nuclear Information System (INIS)

    Shuleiko, D V; Ilin, A S

    2016-01-01

    Photoluminescence and electrical properties of superlattices with thin (1 to 5 nm) alternating silicon-rich silicon oxide or silicon-rich silicon nitride, and silicon oxide or silicon nitride layers containing silicon nanocrystals prepared by plasma-enhanced chemical vapor deposition with subsequent annealing were investigated. The entirely silicon oxide based superlattices demonstrated photoluminescence peak shift due to quantum confinement effect. Electrical measurements showed the hysteresis effect in the vicinity of zero voltage due to structural features of the superlattices from SiOa 93 /Si 3 N 4 and SiN 0 . 8 /Si 3 N 4 layers. The entirely silicon nitride based samples demonstrated resistive switching effect, comprising an abrupt conductivity change at about 5 to 6 V with current-voltage characteristic hysteresis. The samples also demonstrated efficient photoluminescence with maximum at ∼1.4 eV, due to exiton recombination in silicon nanocrystals. (paper)

  1. Technological development for super-high efficiency solar cells. Technological development of solar-high efficiency singlecrystalline silicon solar cells (high quality singlecrystalline silicon substrates); Chokokoritsu taiyo denchi no gijutsu kaihatsu. Chokokoritsu tankessho silicon taiyo denchi no gijutsu kaihatsu (kohinshitsu tankessho silicon kiban no gijutsu kaihatsu)

    Energy Technology Data Exchange (ETDEWEB)

    Tatsuta, M [New Energy and Industrial Technology Development Organization, Tokyo (Japan)

    1994-12-01

    This paper reports the study results on technological development for high quality efficiency singlecrystalline silicon substrates in fiscal 1994. (1) On electromagnetic casting/once FZ bath method, a Si single crystal of 600mm long was successfully obtained by improvement of power source frequency and furnace parts. High carbon content resulted in no single crystal including solids. In undoped electromagnetic casting ingots, resistivities over 1500ohm-cm were obtained because of effective preventive measures from contaminants. (2) On electromagnetic melting CZ method, since vibration and temperature control of melt surface by magnetic shield was insufficient for stable pulling of single crystals, its practical use was hopeless. (3) On electron beam melting CZ method, a Si single crystal of 25mm in diameter was obtained by preventive measures from evaporation of Si and influence of deposits, and improved uniform deposition distribution in a furnace. The oscillation circuit constant of power source, and water-cooling copper crucible structure were also analyzed for the optimum design of electromagnetic melting furnaces. 3 figs., 1 tab.

  2. Analysis and calculation of macrosegregation in a casting ingot. MPS solidification model. Volume 1: Formulation and analysis

    Science.gov (United States)

    Maples, A. L.; Poirier, D. R.

    1980-01-01

    The physical and numerical formulation of a model for the horizontal solidification of a binary alloy is described. It can be applied in an ingot. The major purpose of the model is to calculate macrosegregation in a casting ingot which results from flow of interdendritic liquid during solidification. The flow, driven by solidification contractions and by gravity acting on density gradients in the interdendritic liquid, was modeled as flow through a porous medium. The symbols used are defined. The physical formulation of the problem leading to a set of equations which can be used to obtain: (1) the pressure field; (2) the velocity field: (3) mass flow and (4) solute flow in the solid plus liquid zone during solidification is presented. With these established, the model calculates macrosegregation after solidification is complete. The numerical techniques used to obtain solution on a computational grid are presented. Results, evaluation of the results, and recommendations for future development of the model are given. The macrosegregation and flow field predictions for tin-lead, aluminum-copper, and tin-bismuth alloys are included as well as comparisons of some of the predictions with published predictions or with empirical data.

  3. FY 1977 Annual report on Sunshine Project results. Research and development of photovoltaic power generation systems (Research and development of particle nonacceleration growth type silicon thin-film crystals); 1977 nendo taiyoko hatsuden system no kenkyu kaihatsu seika hokokusho. Ryushi hikasoku seichogata silicon usumaku kessho no kenkyu kaihatsu

    Energy Technology Data Exchange (ETDEWEB)

    NONE

    1978-03-01

    As part of the research and development project for producing photovoltaic power generation systems at reduced cost, the R and D efforts are made for producing particle nonacceleration growth type silicon thin-film crystals. The research items are (1) research on thin-film crystals, and (2) research on cell-structuring method. The item (1) studies quantities, types and electrical properties of impurities and crystal defects in the polycrystalline ingots, produced by the Czochralski method from metal grade silicon and purified metal grade silicon stocks. Next, the substrate prepared above is coated with a thin film of silicon by the vapor-phase growth method with dichlorosilane as the source, to evaluate the thin-film crystals by measuring the crystal defects and lifetime of small numbers of carriers. The item (2) studies the effects of the solder dipping method. In addition, unevenness of photoelectric current is analyzed by a laser scanning microscope, to investigate the effects of the secondary impurities and crystal defects in the substrate crystals on photoelectric current. As a result, it is found that conversion efficiency is improved by grading the hole concentration in the p-type activated layer. The targets of 10 to 20 m{sup 2} as the area and 7 to 8% as the conversion efficiency are attained by preparing the crystals again. (NEDO)

  4. Sequential separation of transuranic elements and fission products from uranium metal ingots in electrolytic reduction process of spent PWR fuels

    International Nuclear Information System (INIS)

    Chang Heon Lee; Kih Soo Joe; Won Ho Kim; Euo Chang Jung; Kwang Yong Jee

    2009-01-01

    A sequential separation procedure has been developed for the determination of transuranic elements and fission products in uranium metal ingot samples from an electrolytic reduction process for a metallization of uranium dioxide to uranium metal in a medium of LiCl-Li 2 O molten salt at 650 deg C. Pu, Np and U were separated using anion-exchange and tri-n-butylphosphate (TBP) extraction chromatography. Cs, Sr, Ba, Ce, Pr, Nd, Sm, Eu, Gd, Zr and Mo were separated in several groups from Am and Cm using TBP and di(2-ethylhexyl)phosphoric acid (HDEHP) extraction chromatography. Effect of Fe, Ni, Cr and Mg, which were corrosion products formed through the process, on the separation of the analytes was investigated in detail. The validity of the separation procedure was evaluated by measuring the recovery of the stable metals and 239 Pu, 237 Np, 241 Am and 244 Cm added to a synthetic uranium metal ingot dissolved solution. (author)

  5. Characteristics of the natural uranium ingots developed in IPEN - CNEN/SP

    International Nuclear Information System (INIS)

    Soares, M.C.B.; Koshimizu, S.

    1990-01-01

    The natural uranium consists of two primary isotopes, the U sup(235) (0,7%) and the U sup(238) (99,3%). The isotopic separation carried out in order to obtain enriched uranium, generates a by-product called depleted uranium, which can be applied for industrial uses. The most singular property, from engineering standpoint, is its high density. When the density is the only important factor, the uranium has great advantage over other heavy metals related to economic and technical considerations. Among some applications of uranium are aircraft and missile counterweights, kinetics energy penetrators, radiation shielding, gyro rotors and oil-well sinker bars. The uranium ingot fabrication is done by direct reduction of UF, with magnesium, without remelting. The microstructure of as-cast uranium is, as in the other as-cast, formed by coarse and. (author)

  6. Formation of porous silicon oxide from substrate-bound silicon rich silicon oxide layers by continuous-wave laser irradiation

    Science.gov (United States)

    Wang, Nan; Fricke-Begemann, Th.; Peretzki, P.; Ihlemann, J.; Seibt, M.

    2018-03-01

    Silicon nanocrystals embedded in silicon oxide that show room temperature photoluminescence (PL) have great potential in silicon light emission applications. Nanocrystalline silicon particle formation by laser irradiation has the unique advantage of spatially controlled heating, which is compatible with modern silicon micro-fabrication technology. In this paper, we employ continuous wave laser irradiation to decompose substrate-bound silicon-rich silicon oxide films into crystalline silicon particles and silicon dioxide. The resulting microstructure is studied using transmission electron microscopy techniques with considerable emphasis on the formation and properties of laser damaged regions which typically quench room temperature PL from the nanoparticles. It is shown that such regions consist of an amorphous matrix with a composition similar to silicon dioxide which contains some nanometric silicon particles in addition to pores. A mechanism referred to as "selective silicon ablation" is proposed which consistently explains the experimental observations. Implications for the damage-free laser decomposition of silicon-rich silicon oxides and also for controlled production of porous silicon dioxide films are discussed.

  7. Silicon heterojunction transistor

    International Nuclear Information System (INIS)

    Matsushita, T.; Oh-uchi, N.; Hayashi, H.; Yamoto, H.

    1979-01-01

    SIPOS (Semi-insulating polycrystalline silicon) which is used as a surface passivation layer for highly reliable silicon devices constitutes a good heterojunction for silicon. P- or B-doped SIPOS has been used as the emitter material of a heterojunction transistor with the base and collector of silicon. An npn SIPOS-Si heterojunction transistor showing 50 times the current gain of an npn silicon homojunction transistor has been realized by high-temperature treatments in nitrogen and low-temperature annealing in hydrogen or forming gas

  8. Characterization of electrical and optical properties of silicon based materials

    Energy Technology Data Exchange (ETDEWEB)

    Jia, Guobin

    2009-12-04

    In this work, the electrical and luminescence properties of a series of silicon based materials used for photovoltaics, microelectronics and nanoelectronics have been investigated by means of electron beam induced current (EBIC), cathodoluminescence (CL), photoluminescence (PL) and electroluminescence (EL) methods. Photovoltaic materials produced by block casting have been investigated by EBIC on wafers sliced from different parts of the ingot. Various solar cell processings have been compared in parallel wafers by means of EBIC collection efficiency measurements and contrast-temperature C(T) behaviors of the extended defects, i. e. dislocations and grain boundaries (GBs). It was found that the solar cell processing with phosphorus diffusion gettering (PDG) followed with a SiN firing greatly reduces the recombination activity of extended defects at room temperature, and improves the bulk property simultaneously. A remaining activity of the dislocations indicates the limitation of the PDG at extended defects. Abnormal behavior of the dislocation activity after certain solar cell processes was also observed in the region with high dislocation density, the dislocations are activated after certain solar cell processings. In order to evaluate the properties of a thin polycrystalline silicon layer prepared by Al-induced layer exchange (Alile) technique, epitaxially layer grown on silicon substrate with different orientations was used as a model system to investigate the impact by the process temperature and the substrates. EBIC energy dependent collection efficiency measurements reveal an improvement of the epilayer quality with increasing substrate temperature during the growth from 450 C to 650 C, and a decrease of epilayer quality at 700 C. PL measurements on the epitaxially grown Si layer on silicon substrates revealed no characteristic dislocation-related luminescence (DRL) lines at room temperature and 77 K, while in the samples prepared by Alile process, intense

  9. Procedure for the qualification of a manufacturer of ingot iron pieces for application in nuclear power plant components

    International Nuclear Information System (INIS)

    Rahn, K.M.M.; Jusevicius, E.; Michael, H.

    1981-01-01

    The process for the qualification of 'Sao Caetano do Sul (Acos Villares S/A)' Plant as manufacturers of ingot iron pieces for application in components of Angra 2 and Angra 3 Nuclear Power Plants, is presented. The qualification was executed by IBQN - Instituto Brasileiro de Qualidade Nuclear - the organ officially in charge of the execution of qualification of suppliers of materials for the nuclear industry. (E.G.) [pt

  10. Control of HANARO NTD No.2 driving unit

    Energy Technology Data Exchange (ETDEWEB)

    Jung, H. S.; Kim, Y. K.; Choi, Y. S.; Woo, J. S.; Jeon, B. J. [KAERI, Taejon (Korea, Republic of)

    2002-10-01

    Automatic control system and control algorithm has been developed for Neutron Transmutation doping system No.2 (NTD No.2) of HANARO research reactor. A motor control system, a neutron flux measurement system using SPND(Self-Powered Neutron Detector) and a PC-based control and data acquisition system were developed. The motor control system was designed to control up-down and rotation of the silicon ingot motion and the set point of each motor speed could be easily adjusted by the control PC. Through the actual irradiation with the real silicon ingot under 24MW of reactor power, it has been confirmed that the motor control system developed could be applied to the commercial production. Rh-type SPNDs are used for real-time monitoring of the accumulated neutron irradiation. It has been verified, by the sample irradiation test for validation of the design that the neutron measurement system gives an accurate and stable signal. To precisely control the target fluence, the NTD control program has been designed so that the silicon ingot be automatically removed from its irradiation hole by the pre-defined irradiation time or accumulated neutron flux. Data acquisition system has been also developed for real-time monitoring and analysis of the analog signals, like SPND flux, control rod position and reactor power.

  11. Reprogramming hMSCs morphology with silicon/porous silicon geometric micro-patterns.

    Science.gov (United States)

    Ynsa, M D; Dang, Z Y; Manso-Silvan, M; Song, J; Azimi, S; Wu, J F; Liang, H D; Torres-Costa, V; Punzon-Quijorna, E; Breese, M B H; Garcia-Ruiz, J P

    2014-04-01

    Geometric micro-patterned surfaces of silicon combined with porous silicon (Si/PSi) have been manufactured to study the behaviour of human Mesenchymal Stem Cells (hMSCs). These micro-patterns consist of regular silicon hexagons surrounded by spaced columns of silicon equilateral triangles separated by PSi. The results show that, at an early culture stage, the hMSCs resemble quiescent cells on the central hexagons with centered nuclei and actin/β-catenin and a microtubules network denoting cell adhesion. After 2 days, hMSCs adapted their morphology and cytoskeleton proteins from cell-cell dominant interactions at the center of the hexagonal surface. This was followed by an intermediate zone with some external actin fibres/β-catenin interactions and an outer zone where the dominant interactions are cell-silicon. Cells move into silicon columns to divide, migrate and communicate. Furthermore, results show that Runx2 and vitamin D receptors, both specific transcription factors for skeleton-derived cells, are expressed in cells grown on micropatterned silicon under all observed circumstances. On the other hand, non-phenotypic alterations are under cell growth and migration on Si/PSi substrates. The former consideration strongly supports the use of micro-patterned silicon surfaces to address pending questions about the mechanisms of human bone biogenesis/pathogenesis and the study of bone scaffolds.

  12. Development of Solar Grade (SoG) Silicon

    Energy Technology Data Exchange (ETDEWEB)

    Joyce, David B; Schmid, Frederick

    2008-01-18

    , as well as liners and coatings to allow the vacuum to be achieved. These developments also hold the promise of lower cost ingot growth, because several of these developments led to a reusable crucible. Liners and coatings were tested on 37 runs, under a variety of conditions. Although many of these did not fulfill the requirements of the program, several were very successful, particularly in allowing the crucible to be reused several times. The most interesting result was with slags and additives used to reduce P and Al. Although slags have been much studied with little success in removing P and B effectively, certain modeling suggested a particular type of slagging might be effective. This was tried, and found to be highly effective for P and surprisingly effective for B, as well. The best results indicate that > 99% of the P was removed, and > 75% of the B was removed by a slagging treatment. An operability issue involving separation of the slag and silicon was the final technical problem preventing the full-scale use of this technique, and there has been progress on this front. A slagging/additive technique is highly promising, because the rates of equilibration are very high, and this is a rapid technique that scales very well to large volumes with little increase in time. Materials of containment and slag/metal separation are issues that are continuing to be developed.

  13. Analysis and calculation of macrosegregation in a casting ingot, exhibits C and E

    Science.gov (United States)

    Poirier, D. R.; Maples, A. L.

    1984-01-01

    A computer model which describes the solidification of a binary metal alloy in an insulated rectangular mold with a temperature gradient is presented. A numerical technique, applicable to a broad class of moving boundary problems, was implemented therein. The solidification model described is used to calculate the macrosegregation within the solidified casting by coupling the equations for liquid flow in the solid/liquid or mushy zone with the energy equation for heat flow throughout the ingot and thermal convection in the bulk liquid portion. The rate of development of the solid can be automatically calculated by the model. Numerical analysis of such solidification parameters as enthalpy and boundary layer flow is displayed. On-line user interface and software documentation are presented.

  14. Fundamental Research and Development for Improved Crystalline Silicon Solar Cells: Final Subcontract Report, March 2002 - July 2006

    Energy Technology Data Exchange (ETDEWEB)

    Rohatgi, A.

    2007-11-01

    This report summarizes the progress made by Georgia Tech in the 2002-2006 period toward high-efficiency, low-cost crystalline silicon solar cells. This program emphasize fundamental and applied research on commercial substrates and manufacturable technologies. A combination of material characterization, device modeling, technology development, and complete cell fabrication were used to accomplish the goals of this program. This report is divided into five sections that summarize our work on i) PECVD SiN-induced defect passivation (Sections 1 and 2); ii) the effect of material inhomogeneity on the performance of mc-Si solar cells (Section 3); iii) a comparison of light-induced degradation in commercially grown Ga- and B-doped Czochralski Si ingots (Section 4); and iv) the understanding of the formation of high-quality thick-film Ag contacts on high sheet-resistance emitters (Section 5).

  15. Vertical integration of high-Q silicon nitride microresonators into silicon-on-insulator platform.

    Science.gov (United States)

    Li, Qing; Eftekhar, Ali A; Sodagar, Majid; Xia, Zhixuan; Atabaki, Amir H; Adibi, Ali

    2013-07-29

    We demonstrate a vertical integration of high-Q silicon nitride microresonators into the silicon-on-insulator platform for applications at the telecommunication wavelengths. Low-loss silicon nitride films with a thickness of 400 nm are successfully grown, enabling compact silicon nitride microresonators with ultra-high intrinsic Qs (~ 6 × 10(6) for 60 μm radius and ~ 2 × 10(7) for 240 μm radius). The coupling between the silicon nitride microresonator and the underneath silicon waveguide is based on evanescent coupling with silicon dioxide as buffer. Selective coupling to a desired radial mode of the silicon nitride microresonator is also achievable using a pulley coupling scheme. In this work, a 60-μm-radius silicon nitride microresonator has been successfully integrated into the silicon-on-insulator platform, showing a single-mode operation with an intrinsic Q of 2 × 10(6).

  16. The POSEIDON Project

    International Nuclear Information System (INIS)

    Benoit, Ph.

    2009-01-01

    Concerns about clean air and global warming led car manufacturers to develop hybrid cars. A few models already reached the market but the manufacturers anticipate that the production figure will hit the million mark at the horizon 2010. Hybrid cars make an extensive use of power electronics, which implies - relatively - large size semi-conductor components. The initial doping of those components is best made by neutron irradiation, which achieves a better doping uniformity than chemical processes. Silicon doping becomes therefore a growing market for a number of research reactors, in supplement to their medical isotopes productions. With the SIDONIE facility in operation since 1992, the doping of silicon is not a new activity in the BR2 reactor. However, SIDONIE is limited to 5 inch diameter ingots whereas the trend is to 6 inch and 8 inch diameter or even 12 inch. The purpose of POSEIDON (POol Side Equipment for Irradiation and DOping of silicon by Neutrons) is to allow the large scale irradiation of 6 inch and 8 inch diameter silicon ingots

  17. Investigation of neutron fluence using fluence monitors for irradiation test at WWR-K

    International Nuclear Information System (INIS)

    Romanova, N.K.; Takemoto, N.

    2013-01-01

    Irradiation test of a Si ingot is planned using WWR-K in Institute of Nuclear Physics Republic of Kazakhstan (INP RK) to develop an irradiation technology for Si semiconductor production by Neutron Transmutation Doping (NTD) method in the framework of an international cooperation between INP RK and Japan Atomic Energy Agency (JAEA), Japan. It is possible to irradiate the Si ingot of 6 inch in diameter at the K-23 irradiation channel in the WWR-K. The preliminary irradiation test using 4 Al ingots was performed to evaluate the actual neutronic irradiation field at the K-23 channel in the WWR-K. Each Al ingot has the same dimension as the Si ingot, and 15 fluence monitors are equipped in it. Iron wire and aluminum-cobalt wire are inserted into them, and it is possible to evaluate both fast and thermal neutron fluxes by measurement of these radiation activities after irradiation. This report described the results of the preliminary irradiation test and the neutronic calculations by Monte Carlo method in order to evaluate the neutronic irradiation field in the irradiation position for the silicon ingot at the channel in the WWR-K. (authors)

  18. Using silicon nanostructures for the improvement of silicon solar cells' efficiency

    International Nuclear Information System (INIS)

    Torre, J. de la; Bremond, G.; Lemiti, M.; Guillot, G.; Mur, P.; Buffet, N.

    2006-01-01

    Silicon nanostructures (ns-Si) show interesting optical and electrical properties as a result of the band gap widening caused by quantum confinement effects. Along with their potential utilization for silicon-based light emitters' fabrication, they could also represent an appealing option for the improvement of energy conversion efficiency in silicon-based solar cells whether by using their luminescence properties (photon down-conversion) or the excess photocurrent produced by an improved high-energy photon's absorption. In this work, we report on the morphological and optical studies of non-stoichiometric silica (SiO x ) and silicon nitride (SiN x ) layers containing silicon nanostructures (ns-Si) in view of their application for solar cell's efficiency improvement. The morphological studies of the samples performed by transmission electron microscopy (TEM) unambiguously show the presence of ns-Si in a crystalline form for high temperature-annealed SiO x layers and for low temperature deposition of SiN x layers. The photoluminescence emission (PL) shows a rather high efficiency in both kind of layers with an intensity of only a factor ∼ 100 lower than that of porous silicon (pi-Si). The photocurrent spectroscopy (PC) shows a significant increase of absorption at high photon energy excitation most probably related to photon absorption within ns-Si quantized states. Moreover, the absorption characteristics obtained from PC spectra show a good agreement with the PL emission states unambiguously demonstrating a same origin, related to Q-confined excitons within ns-Si. Finally, the major asset of this material is the possibility to incorporate it to solar cells manufacturing processing for an insignificant cost

  19. Precipitated iron. A limit on gettering efficacy in multicrystalline silicon

    Energy Technology Data Exchange (ETDEWEB)

    Fenning, D.P.; Hofstetter, J.; Bertoni, M.I.; Buonassisi, T. [Massachusetts Institute of Technology MIT, Cambridge, Massachusetts 02139 (United States); Coletti, G. [ECN Solar Energy, Westerduinweg 3, NL-1755 LE Petten (Netherlands); Lai, B. [Advanced Photon Source, Argonne National Laboratory, Argonne, Illinois 60439 (United States); Del Canizo, C. [Instituto de Energia Solar, Universidad Politecnica de Madrid, 28040 Madrid (Spain)

    2013-01-31

    A phosphorus diffusion gettering model is used to examine the efficacy of a standard gettering process on interstitial and precipitated iron in multicrystalline silicon. The model predicts a large concentration of precipitated iron remaining after standard gettering for most as-grown iron distributions. Although changes in the precipitated iron distribution are predicted to be small, the simulated post-processing interstitial iron concentration is predicted to depend strongly on the as-grown distribution of precipitates, indicating that precipitates must be considered as internal sources of contamination during processing. To inform and validate the model, the iron distributions before and after a standard phosphorus diffusion step are studied in samples from the bottom, middle, and top of an intentionally Fe-contaminated laboratory ingot. A census of iron-silicide precipitates taken by synchrotron-based X-ray fluorescence microscopy confirms the presence of a high density of iron-silicide precipitates both before and after phosphorus diffusion. A comparable precipitated iron distribution was measured in a sister wafer after hydrogenation during a firing step. The similar distributions of precipitated iron seen after each step in the solar cell process confirm that the effect of standard gettering on precipitated iron is strongly limited as predicted by simulation. Good agreement between the experimental and simulated data supports the hypothesis that gettering kinetics is governed by not only the total iron concentration but also by the distribution of precipitated iron. Finally, future directions based on the modeling are suggested for the improvement of effective minority carrier lifetime in multicrystalline silicon solar cells.

  20. Energy-efficiency in inductive heating of forging ingots; Energieeffizienz bei der induktiven Erwaermung von Schmiedebloecken

    Energy Technology Data Exchange (ETDEWEB)

    Padberg, Michael; Doetsch, Erwin [ABP Induction Systems, Dortmund (Germany)

    2012-03-15

    The continuously increasing importance of the CO{sub 2} balance and of conservation of resources is resulting in ever greater demands for high energy-efficiency in the process used for heating of forging ingots. Plant and process engineering play roles of parallel significance in the fulfillment of these requirements, and this article focuses on both in equal degree. The shares of the individual components in the overall energy consumption of an induction heating installation are therefore firstly determined, and their respective potentials for optimization then discussed. The quality of the heating process itself, and its optimum design for reduction of energy consumption, are then examined. (orig.)

  1. POSEIDON project

    International Nuclear Information System (INIS)

    Benoit, P.

    2007-01-01

    Concerns about clean air and global warming among their customers led car manufacturers to develop hybrid cars. A few models already reached the market but the manufacturers anticipate that the production figure will hit the million mark at the horizon 2010. Hybrid cars make an extensive use of power electronics, which implies - relatively - large size semi-conductor components. The initial doping of those components is best made by neutron irradiation, which achieves a better doping uniformity than chemical processes. Silicon doping becomes therefore a growing market for a number of research reactors, in supplement to their medical isotopes productions. With the SIDONIE facility in operation since 1992, the doping of silicon is not a new activity at BR2. However, SIDONIE is limited to 5 inch diameter ingots whereas the trend is to 6 inch and 8 inch diameter. The purpose of POSEIDON is to allow the large scale irradiation of 6 inch and 8 inch diameter silicon ingots

  2. Research and Manufacture of Casting Automation Line for LBMA 1000 Ounces Standard Silver Ingot Based on Production Logistics%基于生产物流的LBMA1000盎司标准银锭自动化铸造线的研制

    Institute of Scientific and Technical Information of China (English)

    郑端; 吴建明; 安国瑞; 朱建斌; 王天才; 周鹤立; 翟瑞锋; 王勇

    2016-01-01

    In order to improve the production efficiency of the London bullion market association (LBMA)1 000 ounces standard silver,using the method of production logistics management to analyze its production process,delete the redundant movement of production logistics and optimize the logistics process,a set of silver ingot automatic casting line was developed in wkich several logistics action were completed by an integrated device for casting silver ingot,such as baking molds,casting and molding of 7 pieces of silver ingots one by one,feedbacking pouring mass signal,slow cooling temperature and demoulding,etc.Trial production shows that the casting line can shorten the silver ingot manufacturing time by 36.5%,handling time by 94%,transport distance by 91.6%,and it can reduce operating staff by 40%,improve yield rate of finished products by 5.33%,significantly improve the production efficiency.The produced 1000 ounces standard silver ingots can meet the requirements of LBMA.%为了提高伦敦金银市场协会(LBMA)1 000盎司标准银锭的生产效率,从生产物流的角度分析了1000盎司标准银锭的生产工艺,删除了生产物流中的多余动作,优化了物流过程,设计了一套银锭自动化铸造线.研制了铸造线的关键设备:银锭铸造车,它把烘模、7块银锭逐一浇注成型、反馈浇注质量信号、补温缓冷、脱模等物流动作集中在一台单体设备上.通过试生产表明,铸造线能够缩短银锭制造时间36.5%、搬运时间94%、搬运距离91.6%,减少操作人员40%,提高成品率5.33%,生产出符合LBMA要求的1000盎司标准银锭.

  3. Solar cells from 120 PPMA carbon-contaminated feedstock without significantly higher reverse current or shunt

    Energy Technology Data Exchange (ETDEWEB)

    Manshanden, P.; Coletti, G. [ECN Solar Energy, Petten (Netherlands)

    2012-09-15

    In a bid to drive down the cost of silicon wafers, several options for solar grade silicon feedstock have been investigated over the years. All methods have in common that the resulting silicon contains higher levels of impurities like dopants, oxygen, carbon or transition metals, the type and level of impurities depending on the raw materials and refining processes. In this work wafers from a p-type mc-Si ingot made with feedstock contaminated with 120 ppma of carbon have been processed into solar cells together with reference uncontaminated feedstock from semiconductor grade polysilicon with <0.4 ppma carbon. The results show that comparable reverse current, shunts, and efficiencies can be reached for both types of wafers. Gettering and defect hydrogenation effectiveness also did not deviate from the reference. Electroluminescence pictures do not show increased hotspot formation, even at -16V.

  4. Silicon-Rich Silicon Carbide Hole-Selective Rear Contacts for Crystalline-Silicon-Based Solar Cells.

    Science.gov (United States)

    Nogay, Gizem; Stuckelberger, Josua; Wyss, Philippe; Jeangros, Quentin; Allebé, Christophe; Niquille, Xavier; Debrot, Fabien; Despeisse, Matthieu; Haug, Franz-Josef; Löper, Philipp; Ballif, Christophe

    2016-12-28

    The use of passivating contacts compatible with typical homojunction thermal processes is one of the most promising approaches to realizing high-efficiency silicon solar cells. In this work, we investigate an alternative rear-passivating contact targeting facile implementation to industrial p-type solar cells. The contact structure consists of a chemically grown thin silicon oxide layer, which is capped with a boron-doped silicon-rich silicon carbide [SiC x (p)] layer and then annealed at 800-900 °C. Transmission electron microscopy reveals that the thin chemical oxide layer disappears upon thermal annealing up to 900 °C, leading to degraded surface passivation. We interpret this in terms of a chemical reaction between carbon atoms in the SiC x (p) layer and the adjacent chemical oxide layer. To prevent this reaction, an intrinsic silicon interlayer was introduced between the chemical oxide and the SiC x (p) layer. We show that this intrinsic silicon interlayer is beneficial for surface passivation. Optimized passivation is obtained with a 10-nm-thick intrinsic silicon interlayer, yielding an emitter saturation current density of 17 fA cm -2 on p-type wafers, which translates into an implied open-circuit voltage of 708 mV. The potential of the developed contact at the rear side is further investigated by realizing a proof-of-concept hybrid solar cell, featuring a heterojunction front-side contact made of intrinsic amorphous silicon and phosphorus-doped amorphous silicon. Even though the presented cells are limited by front-side reflection and front-side parasitic absorption, the obtained cell with a V oc of 694.7 mV, a FF of 79.1%, and an efficiency of 20.44% demonstrates the potential of the p + /p-wafer full-side-passivated rear-side scheme shown here.

  5. The Impact of Metallic Impurities on Minority Carrier Lifetime in High Purity N-type Silicon

    Science.gov (United States)

    Yoon, Yohan

    Boron-doped p-type silicon is the industry standard silicon solar cell substrate. However, it has serious limitations: iron boron (Fe-B) pairs and light induced degradation (LID). To suppress LID, the replacement of boron by gallium as a p-type dopant has been proposed. Although this eliminates B-O related defects, gallium-related pairing with iron, oxygen, and carbon can reduce lifetime in this material. In addition resistivity variations are more pronounced in gallium doped ingots, however Continuous-Czochralski (c-Cz) growth technologies are being developed to overcome this problem. In this work lifetime limiting factors and resistivity variations have been investigated in this material. The radial and axial variations of electrically active defects were observed using deep level transient spectroscopy (DLTS) these have been correlated to lifetime and resistivity variations. The DLTS measurements demonstrated that iron-related pairs are responsible for the lifetime variations. Specifically, Fe-Ga pairs were found to be important recombination sites and are more detrimental to lifetime than Fei. Typically n-type silicon has a higher minority carrier lifetime than p-type silicon with similar levels of contamination. That is because n-type silicon is more tolerant to metallic impurities, especially Fe. Also, it has no serious issues in relation to lifetime degradation, such as FeB pairs and light-induced degradation (LID). However, surface passivation of the p + region in p+n solar cells is much more problematic than the n+p case where silicon nitride provides very effective passivation of the cell. SiO2 is the most effective passivation for n type surfaces, but it does not work well on B-doped surfaces, resulting in inadequate performance. Al2O3 passivation layer suggested for B-doped emitters. With this surface passivation layer a 23.2 % conversion efficiency has been achieved. After this discovery n-type silicon is now being seriously considered for

  6. Transformational silicon electronics

    KAUST Repository

    Rojas, Jhonathan Prieto

    2014-02-25

    In today\\'s traditional electronics such as in computers or in mobile phones, billions of high-performance, ultra-low-power devices are neatly integrated in extremely compact areas on rigid and brittle but low-cost bulk monocrystalline silicon (100) wafers. Ninety percent of global electronics are made up of silicon. Therefore, we have developed a generic low-cost regenerative batch fabrication process to transform such wafers full of devices into thin (5 μm), mechanically flexible, optically semitransparent silicon fabric with devices, then recycling the remaining wafer to generate multiple silicon fabric with chips and devices, ensuring low-cost and optimal utilization of the whole substrate. We show monocrystalline, amorphous, and polycrystalline silicon and silicon dioxide fabric, all from low-cost bulk silicon (100) wafers with the semiconductor industry\\'s most advanced high-κ/metal gate stack based high-performance, ultra-low-power capacitors, field effect transistors, energy harvesters, and storage to emphasize the effectiveness and versatility of this process to transform traditional electronics into flexible and semitransparent ones for multipurpose applications. © 2014 American Chemical Society.

  7. Study on structural properties of epitaxial silicon films on annealed double layer porous silicon

    International Nuclear Information System (INIS)

    Yue Zhihao; Shen Honglie; Cai Hong; Lv Hongjie; Liu Bin

    2012-01-01

    In this paper, epitaxial silicon films were grown on annealed double layer porous silicon by LPCVD. The evolvement of the double layer porous silicon before and after thermal annealing was investigated by scanning electron microscope. X-ray diffraction and Raman spectroscopy were used to investigate the structural properties of the epitaxial silicon thin films grown at different temperature and different pressure. The results show that the surface of the low-porosity layer becomes smooth and there are just few silicon-bridges connecting the porous layer and the substrate wafer. The qualities of the epitaxial silicon thin films become better along with increasing deposition temperature. All of the Raman peaks of silicon films with different deposition pressure are situated at 521 cm -1 under the deposition temperature of 1100 °C, and the Raman intensity of the silicon film deposited at 100 Pa is much closer to that of the monocrystalline silicon wafer. The epitaxial silicon films are all (4 0 0)-oriented and (4 0 0) peak of silicon film deposited at 100 Pa is more symmetric.

  8. Ultrafast Terahertz Conductivity of Photoexcited Nanocrystalline Silicon

    DEFF Research Database (Denmark)

    Cooke, David; MacDonald, A. Nicole; Hryciw, Aaron

    2007-01-01

    The ultrafast transient ac conductivity of nanocrystalline silicon films is investigated using time-resolved terahertz spectroscopy. While epitaxial silicon on sapphire exhibits a free carrier Drude response, silicon nanocrystals embedded in glass show a response that is best described by a class...... in the silicon nanocrystal films is dominated by trapping at the Si/SiO2 interface states, occurring on a 1–100 ps time scale depending on particle size and hydrogen passivation......The ultrafast transient ac conductivity of nanocrystalline silicon films is investigated using time-resolved terahertz spectroscopy. While epitaxial silicon on sapphire exhibits a free carrier Drude response, silicon nanocrystals embedded in glass show a response that is best described...

  9. Study on the graphene/silicon Schottky diodes by transferring graphene transparent electrodes on silicon

    International Nuclear Information System (INIS)

    Wang, Xiaojuan; Li, Dong; Zhang, Qichong; Zou, Liping; Wang, Fengli; Zhou, Jun; Zhang, Zengxing

    2015-01-01

    Graphene/silicon heterostructures present a Schottky characteristic and have potential applications for solar cells and photodetectors. Here, we fabricated graphene/silicon heterostructures by using chemical vapor deposition derived graphene and n-type silicon, and studied the electronic and optoelectronic properties through varying their interface and silicon resistivity. The results exhibit that the properties of the fabricated configurations can be effectively modulated. The graphene/silicon heterostructures with a Si (111) interface and high resistivity show a better photovoltaic behavior and should be applied for high-performance photodetectors. With the combined atomic force microscopy and theoretical analysis, the possible origination is discussed. The work here should be helpful on exploring high-performance graphene/silicon photoelectronics. - Highlights: • Different graphene/silicon heterostructures were fabricated. • Electronic and optoelectronic properties of the heterostructures were studied. • Graphene/silicon heterostructures were further explored for photodetectors.

  10. Study on the graphene/silicon Schottky diodes by transferring graphene transparent electrodes on silicon

    Energy Technology Data Exchange (ETDEWEB)

    Wang, Xiaojuan [MOE Key Laboratory of Advanced Micro-structured Materials & Shanghai Key Laboratory of Special Artificial Microstructure Materials and Technology, School of Physics Science and Engineering, Tongji University, Shanghai 200092 (China); School of Physics and Electronics, Henan University, Kaifeng 475004 (China); Li, Dong; Zhang, Qichong; Zou, Liping; Wang, Fengli [MOE Key Laboratory of Advanced Micro-structured Materials & Shanghai Key Laboratory of Special Artificial Microstructure Materials and Technology, School of Physics Science and Engineering, Tongji University, Shanghai 200092 (China); Zhou, Jun, E-mail: zhoujunzhou@tongji.edu.cn [Center for Phononics and Thermal Energy Science, School of Physics Science and Engineering, Tongji University, Shanghai 200092 (China); Zhang, Zengxing, E-mail: zhangzx@tongji.edu.cn [MOE Key Laboratory of Advanced Micro-structured Materials & Shanghai Key Laboratory of Special Artificial Microstructure Materials and Technology, School of Physics Science and Engineering, Tongji University, Shanghai 200092 (China)

    2015-10-01

    Graphene/silicon heterostructures present a Schottky characteristic and have potential applications for solar cells and photodetectors. Here, we fabricated graphene/silicon heterostructures by using chemical vapor deposition derived graphene and n-type silicon, and studied the electronic and optoelectronic properties through varying their interface and silicon resistivity. The results exhibit that the properties of the fabricated configurations can be effectively modulated. The graphene/silicon heterostructures with a Si (111) interface and high resistivity show a better photovoltaic behavior and should be applied for high-performance photodetectors. With the combined atomic force microscopy and theoretical analysis, the possible origination is discussed. The work here should be helpful on exploring high-performance graphene/silicon photoelectronics. - Highlights: • Different graphene/silicon heterostructures were fabricated. • Electronic and optoelectronic properties of the heterostructures were studied. • Graphene/silicon heterostructures were further explored for photodetectors.

  11. Behavior of Particle Depots in Molten Silicon During Float-Zone Growth in Strong Static Magnetic Fields

    Science.gov (United States)

    Jauss, T.; SorgenFrei, T.; Croell, A.; Azizi, M.; Reimann, C.; Friedrich, J.; Volz, M. P.

    2014-01-01

    In the photovoltaics industry, the largest market share is represented by solar cells made from multicrystalline silicon, which is grown by directional solidification. During the growth process, the silicon melt is in contact with the silicon nitride coated crucible walls and the furnace atmosphere which contains carbon monoxide. The dissolution of the crucible coating, the carbon bearing gas, and the carbon already present in the feedstock, lead to the precipitation of silicon carbide, and silicon nitride, at later stages of the growth process. The precipitation of Si3N4 and SiC particles of up to several hundred micrometers in diameter leads to severe problems during the wire sawing process for wafering the ingots. Furthermore the growth of the silicon grains can be negatively influenced by the presence of particles, which act as nucleation sources and lead to a grit structure of small grains and are sources for dislocations. If doped with Nitrogen from the dissolved crucible coating, SiC is a semi conductive material, and can act as a shunt, short circuiting parts of the solar cell. For these reasons, the incorporation of such particles needs to be avoided. In this contribution we performed model experiments in which the transport of intentionally added SiC particles and their interaction with the solid-liquid interface during float zone growth of silicon in strong steady magnetic fields was investigated. SiC particles of 7µm and 60µm size are placed in single crystal silicon [100] and [111] rods of 8mm diameter. This is achieved by drilling a hole of 2mm diameter, filling in the particles and closing the hole by melting the surface of the rod until a film of silicon covers the hole. The samples are processed under a vacuum of 1x10(exp -5) mbar or better, to prevent gas inclusions. An oxide layer to suppress Marangoni convection is applied by wet oxidation. Experiments without and with static magnetic field are carried out to investigate the influence of melt

  12. Microstructure Evolution and Flow Stress Model of a 20Mn5 Hollow Steel Ingot during Hot Compression.

    Science.gov (United States)

    Liu, Min; Ma, Qing-Xian; Luo, Jian-Bin

    2018-03-21

    20Mn5 steel is widely used in the manufacture of heavy hydro-generator shaft due to its good performance of strength, toughness and wear resistance. However, the hot deformation and recrystallization behaviors of 20Mn5 steel compressed under high temperature were not studied. In this study, the hot compression experiments under temperatures of 850-1200 °C and strain rates of 0.01/s-1/s are conducted using Gleeble thermal and mechanical simulation machine. And the flow stress curves and microstructure after hot compression are obtained. Effects of temperature and strain rate on microstructure are analyzed. Based on the classical stress-dislocation relation and the kinetics of dynamic recrystallization, a two-stage constitutive model is developed to predict the flow stress of 20Mn5 steel. Comparisons between experimental flow stress and predicted flow stress show that the predicted flow stress values are in good agreement with the experimental flow stress values, which indicates that the proposed constitutive model is reliable and can be used for numerical simulation of hot forging of 20Mn5 hollow steel ingot.

  13. Thermoelectric characteristics of Pt-silicide/silicon multi-layer structured p-type silicon

    International Nuclear Information System (INIS)

    Choi, Wonchul; Jun, Dongseok; Kim, Soojung; Shin, Mincheol; Jang, Moongyu

    2015-01-01

    Electric and thermoelectric properties of silicide/silicon multi-layer structured devices were investigated with the variation of silicide/silicon heterojunction numbers from 3 to 12 layers. For the fabrication of silicide/silicon multi-layered structure, platinum and silicon layers are repeatedly sputtered on the (100) silicon bulk substrate and rapid thermal annealing is carried out for the silicidation. The manufactured devices show ohmic current–voltage (I–V) characteristics. The Seebeck coefficient of bulk Si is evaluated as 195.8 ± 15.3 μV/K at 300 K, whereas the 12 layered silicide/silicon multi-layer structured device is evaluated as 201.8 ± 9.1 μV/K. As the temperature increases to 400 K, the Seebeck coefficient increases to 237.2 ± 4.7 μV/K and 277.0 ± 1.1 μV/K for bulk and 12 layered devices, respectively. The increase of Seebeck coefficient in multi-layered structure is mainly attributed to the electron filtering effect due to the Schottky barrier at Pt-silicide/silicon interface. At 400 K, the thermal conductivity is reduced by about half of magnitude compared to bulk in multi-layered device which shows the efficient suppression of phonon propagation by using Pt-silicide/silicon hetero-junctions. - Highlights: • Silicide/silicon multi-layer structured is proposed for thermoelectric devices. • Electric and thermoelectric properties with the number of layer are investigated. • An increase of Seebeck coefficient is mainly attributed the Schottky barrier. • Phonon propagation is suppressed with the existence of Schottky barrier. • Thermal conductivity is reduced due to the suppression of phonon propagation

  14. Silicon (100)/SiO2 by XPS

    Energy Technology Data Exchange (ETDEWEB)

    Jensen, David S.; Kanyal, Supriya S.; Madaan, Nitesh; Vail, Michael A.; Dadson, Andrew; Engelhard, Mark H.; Linford, Matthew R.

    2013-09-25

    Silicon (100) wafers are ubiquitous in microfabrication and, accordingly, their surface characteristics are important. Herein, we report the analysis of Si (100) via X-ray photoelectron spectroscopy (XPS) using monochromatic Al K radiation. Survey scans show that the material is primarily silicon and oxygen, and the Si 2p region shows two peaks that correspond to elemental silicon and silicon dioxide. Using these peaks the thickness of the native oxide (SiO2) was estimated using the equation of Strohmeier.1 The oxygen peak is symmetric. The material shows small amounts of carbon, fluorine, and nitrogen contamination. These silicon wafers are used as the base material for subsequent growth of templated carbon nanotubes.

  15. Polycrystalline Silicon Gettered by Porous Silicon and Heavy Phosphorous Diffusion

    Institute of Scientific and Technical Information of China (English)

    LIU Zuming(刘祖明); Souleymane K Traore; ZHANG Zhongwen(张忠文); LUO Yi(罗毅)

    2004-01-01

    The biggest barrier for photovoltaic (PV) utilization is its high cost, so the key for scale PV utilization is to further decrease the cost of solar cells. One way to improve the efficiency, and therefore lower the cost, is to increase the minority carrier lifetime by controlling the material defects. The main defects in grain boundaries of polycrystalline silicon gettered by porous silicon and heavy phosphorous diffusion have been studied. The porous silicon was formed on the two surfaces of wafers by chemical etching. Phosphorous was then diffused into the wafers at high temperature (900℃). After the porous silicon and diffusion layers were removed, the minority carrier lifetime was measured by photo-conductor decay. The results show that the lifetime's minority carriers are increased greatly after such treatment.

  16. Present status and prospect of NTD in Korea

    International Nuclear Information System (INIS)

    Park, Sang-Jun; Kang, Ki-Doo; Kim, Myung-Seop; Jung, Hoan-Sung

    2012-01-01

    Two vertical irradiation holes in the heavy water reflector region of HANARO have been utilized for the commercial NTD (Neutron Transmutation Doping) service since 2003. Now the service is concentrated on 5 and 6 inch silicon ingots and increasingly involved in 8 inch also. In spite of fixed NTD facility in HANARO, the production has steadily increased every year due to market demand change towards higher target resistivity and continuous improvements of the management. In 2011 total 23 tons of irradiated ingot was supplied to the NTD market. Because one irradiation hole is dedicated to the irradiation for 8 inch silicon ingot and its current market occupancy rate is less than 20%, the service volume from HANARO is expected to increase up to 40 tons per year in next few years. In 2012, a national project for the construction of Korean New Research Reactor is starting. The new reactor will be sited in Ki-Jang, the south part of Korea, and plans to complete in 2016. One of the important missions of the new research reactor is to increase NTD capacity for the stable supply of NTD service. With the experiences in HANARO, the full scale study is started in order to achieve advanced neutron irradiation techniques and handling systems for the higher quality. The irradiation of larger diameter silicon more than 8 inch is included in the study for the future market demand. (author)

  17. Développement de procédés plasma pour l'élaboration et la caractérisation du silicium photovoltaïque : dépôt de couches minces épitaxiées de silicium par PECVD : mesure de la pureté du silicium à l'état solide ( 20°C) et liquide (1414°C) par LIBS

    OpenAIRE

    Benrabbah , Rafik

    2015-01-01

    Today, the main limiting factor of PV is the high price of electricity production by the PV modules. To cope with this difficulty, current researches focus on several ways and alternatives solutions: reducing energy costs including reducing the cost of the raw material, which consists in reducing the thickness of silicon wafers or in the development of cells in thin silicon layers. The latter process is intended to overcome the sawing step of silicon ingots which is necessary for the realizat...

  18. Effects of Non-equilibrium Solidification on the Material Properties of Brick Silicon for Photovoltaics

    Science.gov (United States)

    Regnault, W. F.; Yoo, K. C.; Soltani, P. K.; Johnson, S. M.

    1984-01-01

    Silicon ingot growth technologies like the Ubiquitous Crystallization Process (UCP) are solidified within a shaping crucible. The rate at which heat can be lost from this crucible minus the rate at which heat is input from an external source determines the rate at which crystallization will occur. Occasionally, when the process parameters for solidification are exceeded, the normally large multi-centimeter grain size material assocated with the UCP will break down into regions containing extremely small, millimeter or less, grain size material. Accompanying this breakdown in grain growth is the development of so called sinuous grain boundaries. The breakdown in grain growth which results in this type of small grain structure with sinuous boundaries is usually associated with the rapid crystallization that would accompany a system failure. This suggests that there are limits to the growth velocity that one can obtain and still expect to produce material that would possess good photovoltaic properties. It is the purpose to determine the causes behind the breakdown of this material and what parameters will determine the best rates of solidification.

  19. Operating experience in processing of differently sourced deeply depleted uranium oxide and production of deeply depleted uranium metal ingots

    International Nuclear Information System (INIS)

    Manna, S.; Ladola, Y.S.; Sharma, S.; Chowdhury, S.; Satpati, S.K.; Roy, S.B.

    2009-01-01

    Uranium Metal Plant (UMP) of BARC had first time experience on production of three Depleted Uranium Metal (DUM) ingots of 76kg, 152kg and 163kg during March 1991. These ingots were produced by processing depleted uranyl nitrate solution produced at Plutonium Plant (PP), Trombay. In recent past Uranium Metal Plant (UMP), Uranium Extraction Division (UED), has been assigned to produce tonnage quantity of Deeply DUM (DDUM) from its oxide obtained from PP, PREFRE and RMP, BARC. This is required for shielding the high radioactive source of BHABHATRON Tele-cobalt machine, which is used for cancer therapy. The experience obtained in processing of various DDU oxides is being utilized for design of large scale DDU-metal plant under XIth plan project. The physico- chemical characteristics like morphology, density, flowability, reactivity, particle size distribution, which are having direct effect on reactivity of the powders of the DDU oxide powder, were studied and the shop-floor operational experience in processing of different oxide powder were obtained and recorded. During campaign trials utmost care was taken to standardized all operating conditions using the same equipment which are in use for natural uranium materials processing including safety aspects both with respect to radiological safety and industrial safety. Necessary attention and close monitoring were specially arranged and maintained for the safety aspects during the trial period. In-house developed pneumatic transport system was used for powder transfer and suitable dust arresting system was used for reduction of powder carry over

  20. Irradiation effects of swift heavy ions on gallium arsenide, silicon and silicon diodes

    International Nuclear Information System (INIS)

    Bhoraskar, V.N.

    2001-01-01

    The irradiation effects of high energy lithium, boron, oxygen and silicon ions on crystalline silicon, gallium arsenide, porous silicon and silicon diodes were investigated. The ion energy and fluence were varied over the ranges 30 to 100 MeV and 10 11 to 10 14 ions/cm 2 respectively. Semiconductor samples were characterized with the x-ray fluorescence, photoluminescence, thermally stimulated exo-electron emission and optical reflectivity techniques. The life-time of minority carriers in crystalline silicon was measured with a pulsed electron beam and the lithium depth distribution in GaAs was measured with the neutron depth profiling technique. The diodes were characterized through electrical measurements. The results of optical reflectivity, life-time of minority carriers and photoluminescence show that swift heavy ions induce defects in the surface region of crystalline silicon. In the ion-irradiated GaAs, migration of silicon, oxygen and lithium atoms from the buried region towards the surface was observed, with orders of magnitude enhancement in the diffusion coefficients. Enhancement in the photoluminescence intensity was observed in the GaAs and porous silicon samples that, were irradiated with silicon ions. The trade-off between the turn-off time and the voltage, drop in diodes irradiated with different swift heavy ions was also studied. (author)

  1. Periodically poled silicon

    Science.gov (United States)

    Hon, Nick K.; Tsia, Kevin K.; Solli, Daniel R.; Khurgin, Jacob B.; Jalali, Bahram

    2010-02-01

    Bulk centrosymmetric silicon lacks second-order optical nonlinearity χ(2) - a foundational component of nonlinear optics. Here, we propose a new class of photonic device which enables χ(2) as well as quasi-phase matching based on periodic stress fields in silicon - periodically-poled silicon (PePSi). This concept adds the periodic poling capability to silicon photonics, and allows the excellent crystal quality and advanced manufacturing capabilities of silicon to be harnessed for devices based on χ(2)) effects. The concept can also be simply achieved by having periodic arrangement of stressed thin films along a silicon waveguide. As an example of the utility, we present simulations showing that mid-wave infrared radiation can be efficiently generated through difference frequency generation from near-infrared with a conversion efficiency of 50% based on χ(2) values measurements for strained silicon reported in the literature [Jacobson et al. Nature 441, 199 (2006)]. The use of PePSi for frequency conversion can also be extended to terahertz generation. With integrated piezoelectric material, dynamically control of χ(2)nonlinearity in PePSi waveguide may also be achieved. The successful realization of PePSi based devices depends on the strength of the stress induced χ(2) in silicon. Presently, there exists a significant discrepancy in the literature between the theoretical and experimentally measured values. We present a simple theoretical model that produces result consistent with prior theoretical works and use this model to identify possible reasons for this discrepancy.

  2. Catastrophic degradation of the interface of epitaxial silicon carbide on silicon at high temperatures

    Energy Technology Data Exchange (ETDEWEB)

    Pradeepkumar, Aiswarya; Mishra, Neeraj; Kermany, Atieh Ranjbar; Iacopi, Francesca [Queensland Micro and Nanotechnology Centre and Environmental Futures Research Institute, Griffith University, Nathan QLD 4111 (Australia); Boeckl, John J. [Materials and Manufacturing Directorate, Air Force Research Laboratories, Wright-Patterson Air Force Base, Ohio 45433 (United States); Hellerstedt, Jack; Fuhrer, Michael S. [Monash Centre for Atomically Thin Materials, Monash University, Monash, VIC 3800 (Australia)

    2016-07-04

    Epitaxial cubic silicon carbide on silicon is of high potential technological relevance for the integration of a wide range of applications and materials with silicon technologies, such as micro electro mechanical systems, wide-bandgap electronics, and graphene. The hetero-epitaxial system engenders mechanical stresses at least up to a GPa, pressures making it extremely challenging to maintain the integrity of the silicon carbide/silicon interface. In this work, we investigate the stability of said interface and we find that high temperature annealing leads to a loss of integrity. High–resolution transmission electron microscopy analysis shows a morphologically degraded SiC/Si interface, while mechanical stress measurements indicate considerable relaxation of the interfacial stress. From an electrical point of view, the diode behaviour of the initial p-Si/n-SiC junction is catastrophically lost due to considerable inter-diffusion of atoms and charges across the interface upon annealing. Temperature dependent transport measurements confirm a severe electrical shorting of the epitaxial silicon carbide to the underlying substrate, indicating vast predominance of the silicon carriers in lateral transport above 25 K. This finding has crucial consequences on the integration of epitaxial silicon carbide on silicon and its potential applications.

  3. Slag inclusions in vacuum-melted ingots of the KhN73MBTYu nickel base alloy

    International Nuclear Information System (INIS)

    Gorin, V.A.; Kleshchev, A.S.; Kazharskaya, L.P.

    1977-01-01

    Three types of slag inclusions in ingots of the vacuum-arc-remelted nickel alloy KhN73MBTYu are considered. Type 1 inclusions are those in the surface zone; type 2 inclusions are agglomerations of nitrides and oxides formed due to the fall of lining slag; type 3 inclusions consist of agglomerations of nitrides and oxides as a result of interaction of dissolved oxygen and nitrogen with melt components. The inclusions are removed by machining of the lateral surface. It should be noted that the presence of a large amount of slag on the surface of the molten pool adversely affects the stability of the electrical regime of melting. Strict adherence to the recommendations on the melting and pouring of the initial metal reduces the pollution of the consumable electrode with nonmetallic inclusions

  4. Laser-beam-induced current mapping evaluation of porous silicon-based passivation in polycrystalline silicon solar cells

    Energy Technology Data Exchange (ETDEWEB)

    Rabha, M. Ben; Bessais, B. [Laboratoire de Nanomateriaux et des Systemes pour l' Energie, Centre de Recherches et des Technologies de l' Energie - Technopole de Borj-Cedria BP 95, 2050 Hammam-Lif (Tunisia); Dimassi, W.; Bouaicha, M.; Ezzaouia, H. [Laboratoire de photovoltaique, des semiconducteurs et des nanostructures, Centre de Recherches et des Technologies de l' Energie - Technopole de Borj-Cedria BP 95, 2050 Hammam-Lif (Tunisia)

    2009-05-15

    In the present work, we report on the effect of introducing a superficial porous silicon (PS) layer on the performance of polycrystalline silicon (pc-Si) solar cells. Laser-beam-induced current (LBIC) mapping shows that the PS treatment on the emitter of pc-Si solar cells improves their quantum response and reduce the grain boundaries (GBs) activity. After the porous silicon treatment, mapping investigation shows an enhancement of the LBIC and the internal quantum efficiency (IQE), due to an improvement of the minority carrier diffusion length and the passivation of recombination centers at the GBs as compared to the reference substrate. It was quantitatively shown that porous silicon treatment can passivate both the grains and GBs. (author)

  5. Silicon nanowire hybrid photovoltaics

    KAUST Repository

    Garnett, Erik C.

    2010-06-01

    Silicon nanowire Schottky junction solar cells have been fabricated using n-type silicon nanowire arrays and a spin-coated conductive polymer (PEDOT). The polymer Schottky junction cells show superior surface passivation and open-circuit voltages compared to standard diffused junction cells with native oxide surfaces. External quantum efficiencies up to 88% were measured for these silicon nanowire/PEDOT solar cells further demonstrating excellent surface passivation. This process avoids high temperature processes which allows for low-cost substrates to be used. © 2010 IEEE.

  6. Silicon nanowire hybrid photovoltaics

    KAUST Repository

    Garnett, Erik C.; Peters, Craig; Brongersma, Mark; Cui, Yi; McGehee, Mike

    2010-01-01

    Silicon nanowire Schottky junction solar cells have been fabricated using n-type silicon nanowire arrays and a spin-coated conductive polymer (PEDOT). The polymer Schottky junction cells show superior surface passivation and open-circuit voltages compared to standard diffused junction cells with native oxide surfaces. External quantum efficiencies up to 88% were measured for these silicon nanowire/PEDOT solar cells further demonstrating excellent surface passivation. This process avoids high temperature processes which allows for low-cost substrates to be used. © 2010 IEEE.

  7. Four-Wave Mixing in Silicon-Rich Nitride Waveguides

    DEFF Research Database (Denmark)

    Mitrovic, Miranda; Guan, Xiaowei; Ji, Hua

    2015-01-01

    We demonstrate four-wave mixing wavelength conversion in silicon-rich nitride waveguides which are a promising alternative to silicon for nonlinear applications. The obtained conversion efficiency reaches -13.6 dB while showing no significant nonlinear loss.......We demonstrate four-wave mixing wavelength conversion in silicon-rich nitride waveguides which are a promising alternative to silicon for nonlinear applications. The obtained conversion efficiency reaches -13.6 dB while showing no significant nonlinear loss....

  8. Study of double porous silicon surfaces for enhancement of silicon solar cell performance

    Science.gov (United States)

    Razali, N. S. M.; Rahim, A. F. A.; Radzali, R.; Mahmood, A.

    2017-09-01

    In this work, design and simulation of double porous silicon surfaces for enhancement of silicon solar cell is carried out. Both single and double porous structures are constructed by using TCAD ATHENA and TCAD DEVEDIT tools of the SILVACO software respectively. After the structures were created, I-V characteristics and spectral response of the solar cell were extracted using ATLAS device simulator. Finally, the performance of the simulated double porous solar cell is compared with the performance of both single porous and bulk-Si solar cell. The results showed that double porous silicon solar cell exhibited 1.8% efficiency compared to 1.3% and 1.2% for single porous silicon and bulk-Si solar cell.

  9. Silicon nanowire-based solar cells

    Energy Technology Data Exchange (ETDEWEB)

    Stelzner, Th; Pietsch, M; Andrae, G; Falk, F; Ose, E; Christiansen, S [Institute of Photonic Technology, Albert-Einstein-Strasse 9, D-07745 Jena (Germany)], E-mail: thomas.stelzner@ipht-jena.de

    2008-07-23

    The fabrication of silicon nanowire-based solar cells on silicon wafers and on multicrystalline silicon thin films on glass is described. The nanowires show a strong broadband optical absorption, which makes them an interesting candidate to serve as an absorber in solar cells. The operation of a solar cell is demonstrated with n-doped nanowires grown on a p-doped silicon wafer. From a partially illuminated area of 0.6 cm{sup 2} open-circuit voltages in the range of 230-280 mV and a short-circuit current density of 2 mA cm{sup -2} were obtained.

  10. Silicon nanowire-based solar cells

    International Nuclear Information System (INIS)

    Stelzner, Th; Pietsch, M; Andrae, G; Falk, F; Ose, E; Christiansen, S

    2008-01-01

    The fabrication of silicon nanowire-based solar cells on silicon wafers and on multicrystalline silicon thin films on glass is described. The nanowires show a strong broadband optical absorption, which makes them an interesting candidate to serve as an absorber in solar cells. The operation of a solar cell is demonstrated with n-doped nanowires grown on a p-doped silicon wafer. From a partially illuminated area of 0.6 cm 2 open-circuit voltages in the range of 230-280 mV and a short-circuit current density of 2 mA cm -2 were obtained

  11. Methods To Determine the Silicone Oil Layer Thickness in Sprayed-On Siliconized Syringes.

    Science.gov (United States)

    Loosli, Viviane; Germershaus, Oliver; Steinberg, Henrik; Dreher, Sascha; Grauschopf, Ulla; Funke, Stefanie

    2018-01-01

    The silicone lubricant layer in prefilled syringes has been investigated with regards to siliconization process performance, prefilled syringe functionality, and drug product attributes, such as subvisible particle levels, in several studies in the past. However, adequate methods to characterize the silicone oil layer thickness and distribution are limited, and systematic evaluation is missing. In this study, white light interferometry was evaluated to close this gap in method understanding. White light interferometry demonstrated a good accuracy of 93-99% for MgF 2 coated, curved standards covering a thickness range of 115-473 nm. Thickness measurements for sprayed-on siliconized prefilled syringes with different representative silicone oil distribution patterns (homogeneous, pronounced siliconization at flange or needle side, respectively) showed high instrument (0.5%) and analyst precision (4.1%). Different white light interferometry instrument parameters (autofocus, protective shield, syringe barrel dimensions input, type of non-siliconized syringe used as base reference) had no significant impact on the measured average layer thickness. The obtained values from white light interferometry applying a fully developed method (12 radial lines, 50 mm measurement distance, 50 measurements points) were in agreement with orthogonal results from combined white and laser interferometry and 3D-laser scanning microscopy. The investigated syringe batches (lot A and B) exhibited comparable longitudinal silicone oil layer thicknesses ranging from 170-190 nm to 90-100 nm from flange to tip and homogeneously distributed silicone layers over the syringe barrel circumference (110- 135 nm). Empty break-loose (4-4.5 N) and gliding forces (2-2.5 N) were comparably low for both analyzed syringe lots. A silicone oil layer thickness of 100-200 nm was thus sufficient for adequate functionality in this particular study. Filling the syringe with a surrogate solution including short

  12. Obtention of uranium-molybdenum alloy ingots technique to avoid carbon contamination

    Energy Technology Data Exchange (ETDEWEB)

    Pedrosa, Tercio A.; Paula, Joao Bosco de; Reis, Sergio C.; Brina, Jose Giovanni M.; Faeda, Kelly Cristina M.; Ferraz, Wilmar B., E-mail: tap@cdtn.b, E-mail: jbp@cdtn.b, E-mail: jgmb@cdtn.b, E-mail: ferrazw@cdtn.b [Centro de Desenvolvimento da Tecnologia Nuclear (CDTN/CNEN-MG), Belo Horizonte, MG (Brazil)

    2011-07-01

    The replacement of high enriched uranium (U{sup 235} > 85 wt%) by low enriched uranium (U{sup 235} < 20wt%) nuclear fuels in research and test reactors is being implemented as an initiative of the Reduced Enrichment for Research and Test Reactors (RERTR) program, conceived in the USA since mid-70s, in order to avoid nuclear weapons proliferation. Such replacement implies in the use of compounds or alloys with higher uranium densities. Among the several uranium alloys investigated since then, U-Mo presents great application potential due to its physical properties and good behavior during irradiation, which makes it an important option as a nuclear fuel material for the Brazilian Multipurpose Reactor - RMB. The development of the plate-type nuclear fuel based on U-Mo alloy is being performed at the Nuclear Technology Development Centre (CDTN) and also at IPEN. The carbon contamination of the alloy is one of the great concerns during the melting process. It was observed that U-Mo alloy is more critical considering carbon contamination when using graphite crucibles. Alternative melting technique was implemented at CDTN in order to avoid carbon contamination from graphite crucible using Yttria stabilized ZrO{sub 2} crucibles. Ingots with low carbon content and good internal quality were obtained. (author)

  13. Radiation Hardening of Silicon Detectors

    CERN Multimedia

    Leroy, C; Glaser, M

    2002-01-01

    %RD48 %title\\\\ \\\\Silicon detectors will be widely used in experiments at the CERN Large Hadron Collider where high radiation levels will cause significant bulk damage. In addition to increased leakage current and charge collection losses worsening the signal to noise, the induced radiation damage changes the effective doping concentration and represents the limiting factor to long term operation of silicon detectors. The objectives are to develop radiation hard silicon detectors that can operate beyond the limits of the present devices and that ensure guaranteed operation for the whole lifetime of the LHC experimental programme. Radiation induced defect modelling and experimental results show that the silicon radiation hardness depends on the atomic impurities present in the initial monocrystalline material.\\\\ \\\\ Float zone (FZ) silicon materials with addition of oxygen, carbon, nitrogen, germanium and tin were produced as well as epitaxial silicon materials with epilayers up to 200 $\\mu$m thickness. Their im...

  14. Enhanced Raman scattering in porous silicon grating.

    Science.gov (United States)

    Wang, Jiajia; Jia, Zhenhong; Lv, Changwu

    2018-03-19

    The enhancement of Raman signal on monocrystalline silicon gratings with varying groove depths and on porous silicon grating were studied for a highly sensitive surface enhanced Raman scattering (SERS) response. In the experiment conducted, porous silicon gratings were fabricated. Silver nanoparticles (Ag NPs) were then deposited on the porous silicon grating to enhance the Raman signal of the detective objects. Results show that the enhancement of Raman signal on silicon grating improved when groove depth increased. The enhanced performance of Raman signal on porous silicon grating was also further improved. The Rhodamine SERS response based on Ag NPs/ porous silicon grating substrates was enhanced relative to the SERS response on Ag NPs/ porous silicon substrates. Ag NPs / porous silicon grating SERS substrate system achieved a highly sensitive SERS response due to the coupling of various Raman enhancement factors.

  15. Measurement of the ratio of liquid to solid phases in a continuous ingot

    International Nuclear Information System (INIS)

    Deryabina, G.N.; Ripp, A.G.

    1980-01-01

    A radiometric method of measuring the ratio of liquid and solid phases (crust thickness) in a continuous ingot for automation of the continuous steel casting process, has been proposed. The essence of the method is, that radiation flux, bearing information on the object tested, is transformed in a succession of electric pulses, which is processed afterwords for obtaining necessary information. In this case either the flux of non-scattered radiation, passed through the object, or the flux of single-scattered radiation reflected from the object is registered. Block-diagram and specifications of a radiometric device with the Co source of 50 gxequiv. Ra activity developed for this purpose are presented. The technique for calibration ob the device and the results of its tests, are described. It is shown, that introduction of such devices for the control crust thickness at the installations of continuous steel casting of metallurgical works would permit to exercise casting in the optimum regime, to exclude metal leakage, to increase its quality and yield of the useful metal

  16. Silicon-to-silicon wafer bonding using evaporated glass

    DEFF Research Database (Denmark)

    Weichel, Steen; Reus, Roger De; Lindahl, M.

    1998-01-01

    Anodic bending of silicon to silicon 4-in. wafers using an electron-beam evaporated glass (Schott 8329) was performed successfully in air at temperatures ranging from 200 degrees C to 450 degrees C. The composition of the deposited glass is enriched in sodium as compared to the target material....... The roughness of the as-deposited films was below 5 nm and was found to be unchanged by annealing at 500 degrees C for 1 h in air. No change in the macroscopic edge profiles of the glass film was found as a function of annealing; however, small extrusions appear when annealing above 450 degrees C. Annealing...... of silicon/glass structures in air around 340 degrees C for 15 min leads to stress-free structures. Bonded wafer pairs, however, show no reduction in stress and always exhibit compressive stress. The bond yield is larger than 95% for bonding temperatures around 350 degrees C and is above 80% for bonding...

  17. Flexible Thermoelectric Generators on Silicon Fabric

    KAUST Repository

    Sevilla, Galo T.

    2012-11-01

    In this work, the development of a Thermoelectric Generator on Flexible Silicon Fabric is explored to extend silicon electronics for flexible platforms. Low cost, easily deployable plastic based flexible electronics are of great interest for smart textile, wearable electronics and many other exciting applications. However, low thermal budget processing and fundamentally limited electron mobility hinders its potential to be competitive with well established and highly developed silicon technology. The use of silicon in flexible electronics involve expensive and abrasive materials and processes. In this work, high performance flexible thermoelectric energy harvesters are demonstrated from low cost bulk silicon (100) wafers. The fabrication of the micro- harvesters was done using existing silicon processes on silicon (100) and then peeled them off from the original substrate leaving it for reuse. Peeled off silicon has 3.6% thickness of bulk silicon reducing the thermal loss significantly and generating nearly 30% more output power than unpeeled harvesters. The demonstrated generic batch processing shows a pragmatic way of peeling off a whole silicon circuitry after conventional fabrication on bulk silicon wafers for extremely deformable high performance integrated electronics. In summary, by using a novel, low cost process, this work has successfully integrated existing and highly developed fabrication techniques to introduce a flexible energy harvester for sustainable applications.

  18. Synthesis of Silicon Nanocrystals in Microplasma Reactor

    Science.gov (United States)

    Nozaki, Tomohiro; Sasaki, Kenji; Ogino, Tomohisa; Asahi, Daisuke; Okazaki, Ken

    Nanocrystalline silicon particles with a grain size of at least less than 10 nm are widely recognized as one of the key materials in optoelectronic devices, electrodes of lithium battery, bio-medical labels. There is also important character that silicon is safe material to the environment and easily gets involved in existing silicon technologies. To date, several synthesis methods such as sputtering, laser ablation, and plasma enhanced chemical vapor deposition (PECVD) based on low-pressure silane chemistry (SiH4) have been developed for precise control of size and density distributions of silicon nanocrystals. We explore the possibility of microplasma technologies for the efficient production of mono-dispersed nanocrystalline silicon particles in a micrometer-scale, continuous-flow plasma reactor operated at atmospheric pressure. Mixtures of argon, hydrogen, and silicon tetrachloride were activated using very high frequency (VHF = 144 MHz) power source in a capillary glass tube with a volume of less than 1 μ-liter. Fundamental plasma parameters of VHF capacitively coupled microplasma were characterized by optical emission spectroscopy, showing electron density of approximately 1015 cm-3 and rotational temperature of 1500 K, respectively. Such high-density non-thermal reactive plasma has a capability of decomposing silicon tetrachloride into atomic silicon to produce supersaturated atomic silicon vapor, followed by gas phase nucleation via three-body collision. The particle synthesis in high-density plasma media is beneficial for promoting nucleation process. In addition, further growth of silicon nuclei was able to be favorably terminated in a short-residence time reactor. Micro Raman scattering spectrum showed that as-deposited particles were mostly amorphous silicon with small fraction of silicon nanocrystals. Transmission electron micrograph confirmed individual silicon nanocrystals of 3-15 nm size. Although those particles were not mono-dispersed, they were

  19. Correlation between surface microstructure and optical properties of porous silicon

    Directory of Open Access Journals (Sweden)

    Saeideh Rhramezani Sani

    2007-12-01

    Full Text Available   We have studied the effect of increasing porosity and its microstructure surface variation on the optical and dielectric properties of porous silicon. It seems that porosity, as the surface roughness within the range of a few microns, shows quantum effect in the absorption and reflection process of porous silicon. Optical constants of porous silicon at normal incidence of light with wavelength in the range of 250-3000 nm have been calculated by Kramers-Kroning method. Our experimental analysis shows that electronic structure and dielectric properties of porous silicon are totally different from silicon. Also, it shows that porous silicon has optical response in the visible region. This difference was also verified by effective media approximation (EMA.

  20. Silicon Micromachined Microlens Array for THz Antennas

    Science.gov (United States)

    Lee, Choonsup; Chattopadhyay, Goutam; Mehdi, IImran; Gill, John J.; Jung-Kubiak, Cecile D.; Llombart, Nuria

    2013-01-01

    5 5 silicon microlens array was developed using a silicon micromachining technique for a silicon-based THz antenna array. The feature of the silicon micromachining technique enables one to microfabricate an unlimited number of microlens arrays at one time with good uniformity on a silicon wafer. This technique will resolve one of the key issues in building a THz camera, which is to integrate antennas in a detector array. The conventional approach of building single-pixel receivers and stacking them to form a multi-pixel receiver is not suited at THz because a single-pixel receiver already has difficulty fitting into mass, volume, and power budgets, especially in space applications. In this proposed technique, one has controllability on both diameter and curvature of a silicon microlens. First of all, the diameter of microlens depends on how thick photoresist one could coat and pattern. So far, the diameter of a 6- mm photoresist microlens with 400 m in height has been successfully microfabricated. Based on current researchers experiences, a diameter larger than 1-cm photoresist microlens array would be feasible. In order to control the curvature of the microlens, the following process variables could be used: 1. Amount of photoresist: It determines the curvature of the photoresist microlens. Since the photoresist lens is transferred onto the silicon substrate, it will directly control the curvature of the silicon microlens. 2. Etching selectivity between photoresist and silicon: The photoresist microlens is formed by thermal reflow. In order to transfer the exact photoresist curvature onto silicon, there needs to be etching selectivity of 1:1 between silicon and photoresist. However, by varying the etching selectivity, one could control the curvature of the silicon microlens. The figure shows the microfabricated silicon microlens 5 x5 array. The diameter of the microlens located in the center is about 2.5 mm. The measured 3-D profile of the microlens surface has a

  1. Silicon Alloying On Aluminium Based Alloy Surface

    International Nuclear Information System (INIS)

    Suryanto

    2002-01-01

    Silicon alloying on surface of aluminium based alloy was carried out using electron beam. This is performed in order to enhance tribological properties of the alloy. Silicon is considered most important alloying element in aluminium alloy, particularly for tribological components. Prior to silicon alloying. aluminium substrate were painted with binder and silicon powder and dried in a furnace. Silicon alloying were carried out in a vacuum chamber. The Silicon alloyed materials were assessed using some techniques. The results show that silicon alloying formed a composite metal-non metal system in which silicon particles are dispersed in the alloyed layer. Silicon content in the alloyed layer is about 40% while in other place is only 10.5 %. The hardness of layer changes significantly. The wear properties of the alloying alloys increase. Silicon surface alloying also reduced the coefficient of friction for sliding against a hardened steel counter face, which could otherwise be higher because of the strong adhesion of aluminium to steel. The hardness of the silicon surface alloyed material dropped when it underwent a heating cycle similar to the ion coating process. Hence, silicon alloying is not a suitable choice for use as an intermediate layer for duplex treatment

  2. Synthesis of Novel Reactive Disperse Silicon-Containing Dyes and Their Coloring Properties on Silicone Rubbers

    Directory of Open Access Journals (Sweden)

    Ning Yu

    2018-01-01

    Full Text Available Novel red and purple reactive disperse silicon-containing dyes were designed and synthesized using p-nitroaniline and 6-bromo-2,4-dinitro-aniline as diazonium components, the first condensation product of cyanuric chloride and 3-(N,N-diethylamino-aniline as coupling component, and 3-aminopropylmethoxydimethylsilane, 3-aminopropylmethyldimethoxysilane, and 3-aminopropyltrimethoxysilane as silicone reactive agents. These dyes were characterized by UV-Vis, 1H-NMR, FT-IR, and MS. The obtained reactive disperse silicon-containing dyes were used to color silicone rubbers and the color fastness of the dyes were evaluated. The dry/wet rubbing and washing fastnesses of these dyes all reached 4–5 grade and the sublimation fastness was also above 4 grade, indicating outstanding performance in terms of color fastness. Such colored silicone rubbers showed bright and rich colors without affecting its static mechanical properties.

  3. Hydrothermal deposition and characterization of silicon oxide nanospheres

    International Nuclear Information System (INIS)

    Pei, L.Z.

    2008-01-01

    Silicon oxide nanospheres with the average diameter of about 100 nm have been synthesized by hydrothermal deposition process using silicon and silica as the starting materials. The silicon oxide nanospheres were characterized by field emission scanning electron microscopy (FESEM), energy dispersive X-ray spectrum (EDS), transmission electron microscopy (TEM), high-resolution transmission electron microscopy (HRTEM) and photoluminescence (PL) spectrum, respectively. The results show that large scale silicon oxide nanospheres with the uniform size are composed of Si and O showing the amorphous structure. Strong PL peak at 435 nm is observed demonstrating the good blue light emission property

  4. Silicone metalization

    Energy Technology Data Exchange (ETDEWEB)

    Maghribi, Mariam N. (Livermore, CA); Krulevitch, Peter (Pleasanton, CA); Hamilton, Julie (Tracy, CA)

    2008-12-09

    A system for providing metal features on silicone comprising providing a silicone layer on a matrix and providing a metal layer on the silicone layer. An electronic apparatus can be produced by the system. The electronic apparatus comprises a silicone body and metal features on the silicone body that provide an electronic device.

  5. Process Research on Polycrystalline Silicon Material (PROPSM)

    Science.gov (United States)

    Culik, J. S.; Wrigley, C. Y.

    1985-01-01

    Results of hydrogen-passivated polycrysalline silicon solar cell research are summarized. The short-circuit current of solar cells fabricated from large-grain cast polycrystalline silicon is nearly equivalent to that of single-crystal cells, which indicates long bulk minority-carrier diffusion length. Treatments with molecular hydrogen showed no effect on large-grain cast polycrystalline silicon solar cells.

  6. P-type silicon drift detectors

    International Nuclear Information System (INIS)

    Walton, J.T.; Krieger, B.; Krofcheck, D.; O'Donnell, R.; Odyniec, G.; Partlan, M.D.; Wang, N.W.

    1995-06-01

    Preliminary results on 16 CM 2 , position-sensitive silicon drift detectors, fabricated for the first time on p-type silicon substrates, are presented. The detectors were designed, fabricated, and tested recently at LBL and show interesting properties which make them attractive for use in future physics experiments. A pulse count rate of approximately 8 x l0 6 s -1 is demonstrated by the p-type silicon drift detectors. This count rate estimate is derived by measuring simultaneous tracks produced by a laser and photolithographic mask collimator that generates double tracks separated by 50 μm to 1200 μm. A new method of using ion-implanted polysilicon to produce precise valued bias resistors on the silicon drift detectors is also discussed

  7. Oxygen defect processes in silicon and silicon germanium

    KAUST Repository

    Chroneos, A.

    2015-06-18

    Silicon and silicon germanium are the archetypical elemental and alloy semiconductor materials for nanoelectronic, sensor, and photovoltaic applications. The investigation of radiation induced defects involving oxygen, carbon, and intrinsic defects is important for the improvement of devices as these defects can have a deleterious impact on the properties of silicon and silicon germanium. In the present review, we mainly focus on oxygen-related defects and the impact of isovalent doping on their properties in silicon and silicon germanium. The efficacy of the isovalent doping strategies to constrain the oxygen-related defects is discussed in view of recent infrared spectroscopy and density functional theory studies.

  8. Oxygen defect processes in silicon and silicon germanium

    KAUST Repository

    Chroneos, A.; Sgourou, E. N.; Londos, C. A.; Schwingenschlö gl, Udo

    2015-01-01

    Silicon and silicon germanium are the archetypical elemental and alloy semiconductor materials for nanoelectronic, sensor, and photovoltaic applications. The investigation of radiation induced defects involving oxygen, carbon, and intrinsic defects is important for the improvement of devices as these defects can have a deleterious impact on the properties of silicon and silicon germanium. In the present review, we mainly focus on oxygen-related defects and the impact of isovalent doping on their properties in silicon and silicon germanium. The efficacy of the isovalent doping strategies to constrain the oxygen-related defects is discussed in view of recent infrared spectroscopy and density functional theory studies.

  9. Hot Deformation Behavior and a Two-Stage Constitutive Model of 20Mn5 Solid Steel Ingot during Hot Compression

    Directory of Open Access Journals (Sweden)

    Min Liu

    2018-03-01

    Full Text Available 20Mn5 steel is widely used in the manufacture of heavy hydro-generator shaft forging due to its strength, toughness, and wear resistance. However, the hot deformation and recrystallization behaviors of 20Mn5 steel compressed under a high temperature were not studied. For this article, hot compression experiments under temperatures of 850–1200 °C and strain rates of 0.01 s−1–1 s−1 were conducted using a Gleeble-1500D thermo-mechanical simulator. Flow stress-strain curves and microstructure after hot compression were obtained. Effects of temperature and strain rate on microstructure are analyzed. Based on the classical stress-dislocation relationship and the kinetics of dynamic recrystallization, a two-stage constitutive model is developed to predict the flow stress of 20Mn5 steel. Comparisons between experimental flow stress and predicted flow stress show that the predicted flow stress values are in good agreement with the experimental flow stress values, which indicates that the proposed constitutive model is reliable and can be used for numerical simulation of hot forging of 20Mn5 solid steel ingot.

  10. Plasma-made silicon nanograss and related nanostructures

    International Nuclear Information System (INIS)

    Shieh, Jiann; Ravipati, Srikanth; Ko, Fu-Hsiang; Ostrikov, Kostya

    2011-01-01

    Plasma-made nanostructures show outstanding potential for applications in nanotechnology. This paper provides a concise overview on the progress of plasma-based synthesis and applications of silicon nanograss and related nanostructures. The materials described here include black silicon, Si nanotips produced using a self-masking technique as well as self-organized silicon nanocones and nanograss. The distinctive features of the Si nanograss, two-tier hierarchical and tilted nanograss structures are discussed. Specific applications based on the unique features of the silicon nanograss are also presented.

  11. Silicon Nanocrystal Synthesis in Microplasma Reactor

    Science.gov (United States)

    Nozaki, Tomohiro; Sasaki, Kenji; Ogino, Tomohisa; Asahi, Daisuke; Okazaki, Ken

    Nanocrystalline silicon particles with grains smaller than 5 nm are widely recognized as a key material in optoelectronic devices, lithium battery electrodes, and bio-medical labels. Another important characteristic is that silicon is an environmentally safe material that is used in numerous silicon technologies. To date, several synthesis methods such as sputtering, laser ablation, and plasma-enhanced chemical vapor deposition (PECVD) based on low-pressure silane chemistry (SiH4) have been developed for precise control of size and density distributions of silicon nanocrystals. In this study, we explore the possibility of microplasma technologies for efficient production of mono-dispersed nanocrystalline silicon particles on a micrometer-scale, continuous-flow plasma reactor operated at atmospheric pressure. Mixtures of argon, hydrogen, and silicon tetrachloride were activated using a very-high-frequency (144 MHz) power source in a capillary glass tube with volume of less than 1 μl. Fundamental plasma parameters of the microplasma were characterized using optical emission spectroscopy, which respectively indicated electron density of 1015 cm-3, argon excitation temperature of 5000 K, and rotational temperature of 1500 K. Such high-density non-thermal reactive plasma can decompose silicon tetrachloride into atomic silicon to produce supersaturated silicon vapor, followed by gas-phase nucleation via three-body collision: particle synthesis in high-density plasma media is beneficial for promoting nucleation processes. In addition, further growth of silicon nuclei can be terminated in a short-residence-time reactor. Micro-Raman scattering spectra showed that as-deposited particles are mostly amorphous silicon with a small fraction of silicon nanocrystals. Transmission electron micrography confirmed individual 3-15 nm silicon nanocrystals. Although particles were not mono-dispersed, they were well separated and not coagulated.

  12. Radiation hard cryogenic silicon detectors

    International Nuclear Information System (INIS)

    Casagrande, L.; Abreu, M.C.; Bell, W.H.; Berglund, P.; Boer, W. de; Borchi, E.; Borer, K.; Bruzzi, M.; Buontempo, S.; Chapuy, S.; Cindro, V.; Collins, P.; D'Ambrosio, N.; Da Via, C.; Devine, S.; Dezillie, B.; Dimcovski, Z.; Eremin, V.; Esposito, A.; Granata, V.; Grigoriev, E.; Hauler, F.; Heijne, E.; Heising, S.; Janos, S.; Jungermann, L.; Konorov, I.; Li, Z.; Lourenco, C.; Mikuz, M.; Niinikoski, T.O.; O'Shea, V.; Pagano, S.; Palmieuri, V.G.; Paul, S.; Pirollo, S.; Pretzl, K.; Rato, P.; Ruggiero, G.; Smith, K.; Sonderegger, P.; Sousa, P.; Verbitskaya, E.; Watts, S.; Zavrtanik, M.

    2002-01-01

    It has been recently observed that heavily irradiated silicon detectors, no longer functional at room temperature, 'resuscitate' when operated at temperatures below 130 K. This is often referred to as the 'Lazarus effect'. The results presented here show that cryogenic operation represents a new and reliable solution to the problem of radiation tolerance of silicon detectors

  13. Design and Fabrication of Silicon-on-Silicon-Carbide Substrates and Power Devices for Space Applications

    Directory of Open Access Journals (Sweden)

    Gammon P.M.

    2017-01-01

    Full Text Available A new generation of power electronic semiconductor devices are being developed for the benefit of space and terrestrial harsh-environment applications. 200-600 V lateral transistors and diodes are being fabricated in a thin layer of silicon (Si wafer bonded to silicon carbide (SiC. This novel silicon-on-silicon-carbide (Si/SiC substrate solution promises to combine the benefits of silicon-on-insulator (SOI technology (i.e device confinement, radiation tolerance, high and low temperature performance with that of SiC (i.e. high thermal conductivity, radiation hardness, high temperature performance. Details of a process are given that produces thin films of silicon 1, 2 and 5 μm thick on semi-insulating 4H-SiC. Simulations of the hybrid Si/SiC substrate show that the high thermal conductivity of the SiC offers a junction-to-case temperature ca. 4× less that an equivalent SOI device; reducing the effects of self-heating, and allowing much greater power density. Extensive electrical simulations are used to optimise a 600 V laterally diffused metal-oxide-semiconductor field-effect transistor (LDMOSFET implemented entirely within the silicon thin film, and highlight the differences between Si/SiC and SOI solutions.

  14. The relationship between silicon availability, and growth and silicon concentration of the salt marsh halophyte Spartina anglica

    NARCIS (Netherlands)

    De Bakker, N.; Hemminga, M.A.; Van Soelen, J.

    1999-01-01

    Analysis of silicon concentrations of various halophytes from salt marshes in the S.W. Netherlands shows that the silicon concentration of Spartina anglica (Gramineae) is relatively high. To study the influence of dissolved Si concentrations on growth and plant tissue concentrations of S. anglica,

  15. Rectangular-cladding silicon slot waveguide with improved nonlinear performance

    Science.gov (United States)

    Huang, Zengzhi; Huang, Qingzhong; Wang, Yi; Xia, Jinsong

    2018-04-01

    Silicon slot waveguides have great potential in hybrid silicon integration to realize nonlinear optical applications. We propose a rectangular-cladding hybrid silicon slot waveguide. Simulation result shows that, with a rectangular-cladding, the slot waveguide can be formed by narrower silicon strips, so the two-photon absorption (TPA) loss in silicon is decreased. When the cladding material is a nonlinear polymer, the calculated TPA figure of merit (FOMTPA) is 4.4, close to the value of bulk nonlinear polymer of 5.0. This value confirms the good nonlinear performance of rectangular-cladding silicon slot waveguides.

  16. Solar cells with gallium phosphide/silicon heterojunction

    Science.gov (United States)

    Darnon, Maxime; Varache, Renaud; Descazeaux, Médéric; Quinci, Thomas; Martin, Mickaël; Baron, Thierry; Muñoz, Delfina

    2015-09-01

    One of the limitations of current amorphous silicon/crystalline silicon heterojunction solar cells is electrical and optical losses in the front transparent conductive oxide and amorphous silicon layers that limit the short circuit current. We propose to grow a thin (5 to 20 nm) crystalline Gallium Phosphide (GaP) by epitaxy on silicon to form a more transparent and more conducting emitter in place of the front amorphous silicon layers. We show that a transparent conducting oxide (TCO) is still necessary to laterally collect the current with thin GaP emitter. Larger contact resistance of GaP/TCO increases the series resistance compared to amorphous silicon. With the current process, losses in the IR region associated with silicon degradation during the surface preparation preceding GaP deposition counterbalance the gain from the UV region. A first cell efficiency of 9% has been obtained on ˜5×5 cm2 polished samples.

  17. Creep analysis of silicone for podiatry applications.

    Science.gov (United States)

    Janeiro-Arocas, Julia; Tarrío-Saavedra, Javier; López-Beceiro, Jorge; Naya, Salvador; López-Canosa, Adrián; Heredia-García, Nicolás; Artiaga, Ramón

    2016-10-01

    This work shows an effective methodology to characterize the creep-recovery behavior of silicones before their application in podiatry. The aim is to characterize, model and compare the creep-recovery properties of different types of silicone used in podiatry orthotics. Creep-recovery phenomena of silicones used in podiatry orthotics is characterized by dynamic mechanical analysis (DMA). Silicones provided by Herbitas are compared by observing their viscoelastic properties by Functional Data Analysis (FDA) and nonlinear regression. The relationship between strain and time is modeled by fixed and mixed effects nonlinear regression to compare easily and intuitively podiatry silicones. Functional ANOVA and Kohlrausch-Willians-Watts (KWW) model with fixed and mixed effects allows us to compare different silicones observing the values of fitting parameters and their physical meaning. The differences between silicones are related to the variations of breadth of creep-recovery time distribution and instantaneous deformation-permanent strain. Nevertheless, the mean creep-relaxation time is the same for all the studied silicones. Silicones used in palliative orthoses have higher instantaneous deformation-permanent strain and narrower creep-recovery distribution. The proposed methodology based on DMA, FDA and nonlinear regression is an useful tool to characterize and choose the proper silicone for each podiatry application according to their viscoelastic properties. Copyright © 2016 Elsevier Ltd. All rights reserved.

  18. Position-controlled epitaxial III-V nanowires on silicon

    Energy Technology Data Exchange (ETDEWEB)

    Roest, Aarnoud L; Verheijen, Marcel A; Wunnicke, Olaf; Serafin, Stacey; Wondergem, Harry; Bakkers, Erik P A M [Philips Research Laboratories, Professor Holstlaan 4, 5656 AA Eindhoven (Netherlands); Kavli Institute of NanoScience, Delft University of Technology, PO Box 5046, 2600 GA Delft (Netherlands)

    2006-06-14

    We show the epitaxial integration of III-V semiconductor nanowires with silicon technology. The wires are grown by the VLS mechanism with laser ablation as well as metal-organic vapour phase epitaxy. The hetero-epitaxial growth of the III-V nanowires on silicon was confirmed with x-ray diffraction pole figures and cross-sectional transmission electron microscopy. We show preliminary results of two-terminal electrical measurements of III-V nanowires grown on silicon. E-beam lithography was used to predefine the position of the nanowires.

  19. Position-controlled epitaxial III-V nanowires on silicon

    International Nuclear Information System (INIS)

    Roest, Aarnoud L; Verheijen, Marcel A; Wunnicke, Olaf; Serafin, Stacey; Wondergem, Harry; Bakkers, Erik P A M

    2006-01-01

    We show the epitaxial integration of III-V semiconductor nanowires with silicon technology. The wires are grown by the VLS mechanism with laser ablation as well as metal-organic vapour phase epitaxy. The hetero-epitaxial growth of the III-V nanowires on silicon was confirmed with x-ray diffraction pole figures and cross-sectional transmission electron microscopy. We show preliminary results of two-terminal electrical measurements of III-V nanowires grown on silicon. E-beam lithography was used to predefine the position of the nanowires

  20. Thermogravimetric analysis of silicon carbide-silicon nitride fibers at ambient to 1000 C in air

    Science.gov (United States)

    Daniels, J. G.; Ledbetter, F. E., III; Clemons, J. M.; Penn, B. G.

    1984-01-01

    Thermogravimetric analysis of silicon carbide-silicon nitride fibers was carried out at ambient to 1000 C in air. The weight loss over this temperature range was negligible. In addition, the oxidative stability at high temperature for a short period of time was determined. Fibers heated at 1000 C in air for fifteen minutes showed negligible weight loss (i.e., less than 1 percent).

  1. Production of electronic grade lunar silicon by disproportionation of silicon difluoride

    Science.gov (United States)

    Agosto, William N.

    1993-01-01

    Waldron has proposed to extract lunar silicon by sodium reduction of sodium fluorosilicate derived from reacting sodium fluoride with lunar silicon tetrafluoride. Silicon tetrafluoride is obtained by the action of hydrofluoric acid on lunar silicates. While these reactions are well understood, the resulting lunar silicon is not likely to meet electronic specifications of 5 nines purity. Dale and Margrave have shown that silicon difluoride can be obtained by the action of silicon tetrafluoride on elemental silicon at elevated temperatures (1100-1200 C) and low pressures (1-2 torr). The resulting silicon difluoride will then spontaneously disproportionate into hyperpure silicon and silicon tetrafluoride in vacuum at approximately 400 C. On its own merits, silicon difluoride polymerizes into a tough waxy solid in the temperature range from liquid nitrogen to about 100 C. It is the silicon analog of teflon. Silicon difluoride ignites in moist air but is stable under lunar surface conditions and may prove to be a valuable industrial material that is largely lunar derived for lunar surface applications. The most effective driver for lunar industrialization may be the prospects for industrial space solar power systems in orbit or on the moon that are built with lunar materials. Such systems would require large quantities of electronic grade silicon or compound semiconductors for photovoltaics and electronic controls. Since silicon is the most abundant semimetal in the silicate portion of any solar system rock (approximately 20 wt percent), lunar silicon production is bound to be an important process in such a solar power project. The lunar silicon extraction process is discussed.

  2. An FPGA-based silicon neuronal network with selectable excitability silicon neurons

    Directory of Open Access Journals (Sweden)

    Jing eLi

    2012-12-01

    Full Text Available This paper presents a digital silicon neuronal network which simulates the nerve system in creatures and has the ability to execute intelligent tasks, such as associative memory. Two essential elements, the mathematical-structure-based digital spiking silicon neuron (DSSN and the transmitter release based silicon synapse, allow the network to show rich dynamic behaviors and are computationally efficient for hardware implementation. We adopt mixed pipeline and parallel structure and shift operations to design a sufficient large and complex network without excessive hardware resource cost. The network with $256$ full-connected neurons is built on a Digilent Atlys board equipped with a Xilinx Spartan-6 LX45 FPGA. Besides, a memory control block and USB control block are designed to accomplish the task of data communication between the network and the host PC. This paper also describes the mechanism of associative memory performed in the silicon neuronal network. The network is capable of retrieving stored patterns if the inputs contain enough information of them. The retrieving probability increases with the similarity between the input and the stored pattern increasing. Synchronization of neurons is observed when the successful stored pattern retrieval occurs.

  3. Current-voltage characteristics of porous-silicon structures

    International Nuclear Information System (INIS)

    Diligenti, A.; Nannini, A.; Pennelli, G.; Pieri, F.; Fuso, F.; Allegrini, M.

    1996-01-01

    I-V DC characteristics have been measured on metal/porous-silicon structures. In particular, the measurements on metal/free-standing porous-silicon film/metal devices confirmed the result, already obtained, that the metal/porous-silicon interface plays a crucial role in the transport of any device. Four-contacts measurements on free-standing layers showed that the current linearly depends on the voltage and that the conduction process is thermally activated, the activation energy depending on the porous silicon film production parameters. Finally, annealing experiments performed in order to improve the conduction of rectifying contacts, are described

  4. Plasmonic and silicon spherical nanoparticle antireflective coatings

    Science.gov (United States)

    Baryshnikova, K. V.; Petrov, M. I.; Babicheva, V. E.; Belov, P. A.

    2016-03-01

    Over the last decade, plasmonic antireflecting nanostructures have been extensively studied to be utilized in various optical and optoelectronic systems such as lenses, solar cells, photodetectors, and others. The growing interest to all-dielectric photonics as an alternative optical technology along with plasmonics motivates us to compare antireflective properties of plasmonic and all-dielectric nanoparticle coatings based on silver and crystalline silicon respectively. Our simulation results for spherical nanoparticles array on top of amorphous silicon show that both silicon and silver coatings demonstrate strong antireflective properties in the visible spectral range. For the first time, we show that zero reflectance from the structure with silicon coatings originates from the destructive interference of electric- and magnetic-dipole responses of nanoparticle array with the wave reflected from the substrate, and we refer to this reflection suppression as substrate-mediated Kerker effect. We theoretically compare the silicon and silver coating effectiveness for the thin-film photovoltaic applications. Silver nanoparticles can be more efficient, enabling up to 30% increase of the overall absorbance in semiconductor layer. Nevertheless, silicon coatings allow up to 64% absorbance increase in the narrow band spectral range because of the substrate-mediated Kerker effect, and band position can be effectively tuned by varying the nanoparticles sizes.

  5. Experimental analysis of segregation and porosity during the transient unidirectional solidification of an Al-9%Si-3%Cu ternary

    International Nuclear Information System (INIS)

    Gomes, L.G.; Moutinho, D.J.; Rocha, O.L.; Ferreira, I.L.; Garcia, A.

    2010-01-01

    The solute macro segregation and formation of micro porosity were experimental y investigated in the transient unidirectional solidification of a ternary league. The solute macro segregation profile, the specific theoretical mass and the apparent specific mass are presented alongside of ingot length. The experimental segregation profile of the solute were obtained through the X ray fluorescence spectrometry technique. The micro porosity measurements were performed by using the technique of picnometry. The presence of silicon on the league acted as inhibitor of inverse segregation of the copper, which is a typically observed in the transient unidirectional solidified of Al-Cu leagues. The volumetric fractions of porous has shown a ascendent tendency from the base to the top of ingot

  6. Shrinking of silicon nanocrystals embedded in an amorphous silicon oxide matrix during rapid thermal annealing in a forming gas atmosphere

    Science.gov (United States)

    van Sebille, M.; Fusi, A.; Xie, L.; Ali, H.; van Swaaij, R. A. C. M. M.; Leifer, K.; Zeman, M.

    2016-09-01

    We report the effect of hydrogen on the crystallization process of silicon nanocrystals embedded in a silicon oxide matrix. We show that hydrogen gas during annealing leads to a lower sub-band gap absorption, indicating passivation of defects created during annealing. Samples annealed in pure nitrogen show expected trends according to crystallization theory. Samples annealed in forming gas, however, deviate from this trend. Their crystallinity decreases for increased annealing time. Furthermore, we observe a decrease in the mean nanocrystal size and the size distribution broadens, indicating that hydrogen causes a size reduction of the silicon nanocrystals.

  7. Colloidal characterization of ultrafine silicon carbide and silicon nitride powders

    Science.gov (United States)

    Whitman, Pamela K.; Feke, Donald L.

    1986-01-01

    The effects of various powder treatment strategies on the colloid chemistry of aqueous dispersions of silicon carbide and silicon nitride are examined using a surface titration methodology. Pretreatments are used to differentiate between the true surface chemistry of the powders and artifacts resulting from exposure history. Silicon nitride powders require more extensive pretreatment to reveal consistent surface chemistry than do silicon carbide powders. As measured by titration, the degree of proton adsorption from the suspending fluid by pretreated silicon nitride and silicon carbide powders can both be made similar to that of silica.

  8. Vibrational modes of porous silicon

    International Nuclear Information System (INIS)

    Sabra, M.; Naddaf, M.

    2012-01-01

    On the basis of theoretical and experimental investigations, the origin of room temperature photoluminescence (PL) from porous silicon is found to related to chemical complexes constituted the surface, in particular, SiHx, SiOx and SiOH groups. Ab initio atomic and molecular electronic structure calculations on select siloxane compounds were used for imitation of infrared (IR) spectra of porous silicon. These are compared to the IR spectra of porous silicon recorded by using Fourier Transform Infrared Spectroscopy (FTIR). In contrast to linear siloxane, the suggested circular siloxane terminated with linear siloxane structure is found to well-imitate the experimental spectra. These results are augmented with EDX (energy dispersive x-ray spectroscopy) measurements, which showed that the increase of SiOx content in porous silicon due to rapid oxidation process results in considerable decrease in PL peak intensity and a blue shift in the peak position. (author)

  9. A study of positron irradiated porous silicon

    International Nuclear Information System (INIS)

    Huang Yuanming; Xue Qing; Zhai Baogai; Xu Aijun; Liu Shewen; Yu Weizhong

    1998-01-01

    The effect of positron irradiation on photoluminescence (PL) of porous silicon has been studied. After four hour positron irradiation, the red PL spectrum of porous silicon blue shifts into greenish spectral region, and a higher energy luminescence band is introduced into this blueshifted spectrum. The fourier transform infrared absorption experiment shows that the positron irradiation can cause further oxidization of porous silicon. A possible mechanism causing this change of PL spectra after positron irradiation is suggested

  10. Structural, optical and electrical properties of quasi-monocrystalline silicon thin films obtained by rapid thermal annealing of porous silicon layers

    International Nuclear Information System (INIS)

    Hajji, M.; Khardani, M.; Khedher, N.; Rahmouni, H.; Bessais, B.; Ezzaouia, H.; Bouchriha, H.

    2006-01-01

    Quasi-mono-crystalline silicon (QMS) layers have a top surface like crystalline silicon with small voids in the body. Such layers are reported to have a higher absorption coefficient than crystalline silicon at the interesting range of the solar spectrum for photovoltaic application. In this work we present a study of the structural, optical and electrical properties of quasimonocrystalline silicon thin films. Quasimonocrystalline silicon thin films were obtained from porous silicon, which has been annealed at a temperature ranging from 950 to 1050 deg. C under H 2 atmosphere for different annealing durations. The porous layers were prepared by conventional electrochemical anodization using a double tank cell and a HF / Ethanol electrolyte. Porous silicon is formed on highly doped p + -type silicon substrates that enable us to prevent back contacts for the anodization. Atomic Force Microscope (AFM) was used to study the morphological quality of the prepared layers. Optical properties were extracted from transmission and reflectivity spectra. Dark I-V characteristics were used to determine the electrical conductivity of quasimonocrystalline silicon thin films. Results show an important improvement of the absorption coefficient of the material and electrical conductivity reaches a value of twenty orders higher than that of starting mesoporous silicon

  11. Arsenic implantation into polycrystalline silicon and diffusion to silicon substrate

    International Nuclear Information System (INIS)

    Tsukamoto, K.; Akasaka, Y.; Horie, K.

    1977-01-01

    Arsenic implantation into polycrystalline silicon and drive-in diffusion to silicon substrate have been investigated by MeV He + backscattering analysis and also by electrical measurements. The range distributions of arsenic implanted into polycrystalline silicon are well fitted to Gaussian distributions over the energy range 60--350 keV. The measured values of R/sub P/ and ΔR/sub P/ are about 10 and 20% larger than the theoretical predictions, respectively. The effective diffusion coefficient of arsenic implanted into polycrystalline silicon is expressed as D=0.63 exp[(-3.22 eV/kT)] and is independent of the arsenic concentration. The drive-in diffusion of arsenic from the implanted polycrystalline silicon layer into the silicon substrate is significantly affected by the diffusion atmosphere. In the N 2 atmosphere, a considerable amount of arsenic atoms diffuses outward to the ambient. The outdiffusion can be suppressed by encapsulation with Si 3 N 4 . In the oxidizing atmosphere, arsenic atoms are driven inward by growing SiO 2 due to the segregation between SiO 2 and polycrystalline silicon, and consequently the drive-in diffusion of arsenic is enhanced. At the interface between the polycrystalline silicon layer and the silicon substrate, arsenic atoms are likely to segregate at the polycrystalline silicon side

  12. Metallization of DNA on silicon surface

    International Nuclear Information System (INIS)

    Puchkova, Anastasiya Olegovna; Sokolov, Petr; Petrov, Yuri Vladimirovich; Kasyanenko, Nina Anatolievna

    2011-01-01

    New simple way for silver deoxyribonucleic acid (DNA)-based nanowires preparation on silicon surface was developed. The electrochemical reduction of silver ions fixed on DNA molecule provides the forming of tightly matched zonate silver clusters. Highly homogeneous metallic clusters have a size about 30 nm. So the thickness of nanowires does not exceed 30–50 nm. The surface of n-type silicon monocrystal is the most convenient substrate for this procedure. The comparative analysis of DNA metallization on of n-type silicon with a similar way for nanowires fabrication on p-type silicon, freshly cleaved mica, and glass surface shows the advantage of n-type silicon, which is not only the substrate for DNA fixation but also the source of electrons for silver reduction. Images of bound DNA molecules and fabricated nanowires have been obtained using an atomic force microscope and a scanning ion helium microscope. DNA interaction with silver ions in a solution was examined by the methods of ultraviolet spectroscopy and circular dichroism.

  13. Porous silicon: silicon quantum dots for photonic applications

    International Nuclear Information System (INIS)

    Pavesi, L.; Guardini, R.

    1996-01-01

    Porous silicon formation and structure characterization are briefly illustrated. Its luminescence properties rae presented and interpreted on the basis of exciton recombination in quantum dot structures: the trap-controlled hopping mechanism is used to describe the recombination dynamics. Porous silicon application to photonic devices is considered: porous silicon multilayer in general, and micro cavities in particular are described. The present situation in the realization of porous silicon LEDs is considered, and future developments in this field of research are suggested. (author). 30 refs., 30 figs., 13 tabs

  14. Self-diffusion in single crystalline silicon nanowires

    Science.gov (United States)

    Südkamp, T.; Hamdana, G.; Descoins, M.; Mangelinck, D.; Wasisto, H. S.; Peiner, E.; Bracht, H.

    2018-04-01

    Self-diffusion experiments in single crystalline isotopically controlled silicon nanowires with diameters of 70 and 400 nm at 850 and 1000 °C are reported. The isotope structures were first epitaxially grown on top of silicon substrate wafers. Nanowires were subsequently fabricated using a nanosphere lithography process in combination with inductively coupled plasma dry reactive ion etching. Three-dimensional profiling of the nanosized structure before and after diffusion annealing was performed by means of atom probe tomography (APT). Self-diffusion profiles obtained from APT analyses are accurately described by Fick's law for self-diffusion. Data obtained for silicon self-diffusion in nanowires are equal to the results reported for bulk silicon crystals, i.e., finite size effects and high surface-to-volume ratios do not significantly affect silicon self-diffusion. This shows that the properties of native point defects determined from self-diffusion in bulk crystals also hold for nanosized silicon structures with diameters down to 70 nm.

  15. Tailoring the optical constants in single-crystal silicon with embedded silver nanostructures for advanced silicon photonics applications

    International Nuclear Information System (INIS)

    Akhter, Perveen; Huang, Mengbing; Spratt, William; Kadakia, Nirag; Amir, Faisal

    2015-01-01

    Plasmonic effects associated with metal nanostructures are expected to hold the key to tailoring light emission/propagation and harvesting solar energy in materials including single crystal silicon which remains the backbone in the microelectronics and photovoltaics industries but unfortunately, lacks many functionalities needed for construction of advanced photonic and optoelectronics devices. Currently, silicon plasmonic structures are practically possible only in the configuration with metal nanoparticles or thin film arrays on a silicon surface. This does not enable one to exploit the full potential of plasmonics for optical engineering in silicon, because the plasmonic effects are dominant over a length of ∼50 nm, and the active device region typically lies below the surface much beyond this range. Here, we report on a novel method for the formation of silver nanoparticles embedded within a silicon crystal through metal gettering from a silver thin film deposited at the surface to nanocavities within the Si created by hydrogen ion implantation. The refractive index of the Ag-nanostructured layer is found to be 3–10% lower or higher than that of silicon for wavelengths below or beyond ∼815–900 nm, respectively. Around this wavelength range, the optical extinction values increase by a factor of 10–100 as opposed to the pure silicon case. Increasing the amount of gettered silver leads to an increased extinction as well as a redshift in wavelength position for the resonance. This resonance is attributed to the surface plasmon excitation of the resultant silver nanoparticles in silicon. Additionally, we show that the profiles for optical constants in silicon can be tailored by varying the position and number of nanocavity layers. Such silicon crystals with embedded metal nanostructures would offer novel functional base structures for applications in silicon photonics, optoelectronics, photovoltaics, and plasmonics

  16. Synthesis and characterization of carboxylic acid functionalized silicon nanoparticles

    Science.gov (United States)

    Shaner, Ted V.

    Silicon nanoparticles are of great interest in a great number of fields. Silicon nanoparticles show great promise particularly in the field of bioimaging. Carboxylic acid functionalized silicon nanoparticles have the ability to covalently bond to biomolecules through the conjugation of the carboxylic acid to an amine functionalized biomolecule. This thesis explores the synthesis of silicon nanoparticles functionalized by both carboxylic acids and alkenes and their carboxylic acid functionality. Also discussed is the characterization of the silicon nanoparticles by the use of x-ray spectroscopy. Finally, the nature of the Si-H bond that is observed on the surface of the silicon nanoparticles will be investigated using photoassisted exciton mediated hydrosilation reactions. The silicon nanoparticles are synthesized from both carboxylic acids and alkenes. However, the lack of solubility of diacids is a significant barrier to carboxylic acid functionalization by a mixture of monoacids and diacids. A synthesis route to overcome this obstacle is to synthesize silicon nanoparticles with terminal vinyl group. This terminal vinyl group is distal to the surface of the silicon nanoparticle. The conversion of the vinyl group to a carboxylic acid is accomplished by oxidative cleavage using ozonolysis. The carboxylic acid functionalized silicon nanoparticles were then successfully conjugated to amine functionalized DNA strand through an n-hydroxy succinimide ester activation step, which promotes the formation of the amide bond. Conjugation was characterized by TEM and polyacrylamide gel electrophoresis (PAGE). The PAGE results show that the silicon nanoparticle conjugates move slower through the polyacrylamide gel, resulting in a significant separation from the nonconjugated DNA. The silicon nanoparticles were then characterized by the use of x-ray absorption near edge spectroscopy (Xanes) and x-ray photoelectron spectroscopy (XPS) to investigate the bonding and chemical

  17. MOS structures containing silicon nanoparticles for memory device applications

    International Nuclear Information System (INIS)

    Nedev, N; Zlatev, R; Nesheva, D; Manolov, E; Levi, Z; Brueggemann, R; Meier, S

    2008-01-01

    Metal-oxide-silicon structures containing layers with amorphous or crystalline silicon nanoparticles in a silicon oxide matrix are fabricated by sequential physical vapour deposition of SiO x (x = 1.15) and RF sputtering of SiO 2 on n-type crystalline silicon, followed by high temperature annealing in an inert gas ambient. Depending on the annealing temperature, 700 deg. C or 1000 deg. C, amorphous or crystalline silicon nanoparticles are formed in the silicon oxide matrix. The annealing process is used not only for growing nanoparticles but also to form a dielectric layer with tunnelling thickness at the silicon/insulator interface. High frequency C-V measurements demonstrate that both types of structures can be charged negatively or positively by applying a positive or negative voltage on the gate. The structures with amorphous silicon nanoparticles show several important advantages compared to the nanocrystal ones, such as lower defect density at the interface between the crystalline silicon wafer and the tunnel silicon oxide, better retention characteristics and better reliability

  18. Formation of silicon carbide by laser ablation in graphene oxide-N-methyl-2-pyrrolidone suspension on silicon surface

    Science.gov (United States)

    Jaleh, Babak; Ghasemi, Samaneh; Torkamany, Mohammad Javad; Salehzadeh, Sadegh; Maleki, Farahnaz

    2018-01-01

    Laser ablation of a silicon wafer in graphene oxide-N-methyl-2-pyrrolidone (GO-NMP) suspension was carried out with a pulsed Nd:YAG laser (pulse duration = 250 ns, wavelength = 1064 nm). The surface of silicon wafer before and after laser ablation was studied using optical microscopy, scanning electron microscopy (SEM) and energy dispersive X-ray analysis (EDX). The results showed that the ablation of silicon surface in liquid by pulsed laser was done by the process of melt expulsion under the influence of the confined plasma-induced pressure or shock wave trapped between the silicon wafer and the liquid. The X-ray diffraction‌ (XRD) pattern of Si wafer after laser ablation showed that 4H-SiC layer is formed on its surface. The formation of the above layer was also confirmed by Raman spectroscopy, and X-ray photoelectron spectroscopy‌ (XPS), as well as EDX was utilized. The reflectance of samples decreased with increasing pulse energy. Therefore, the morphological alteration and the formation of SiC layer at high energy increase absorption intensity in the UV‌-vis regions. Theoretical calculations confirm that the formation of silicon carbide from graphene oxide and silicon wafer is considerably endothermic. Development of new methods for increasing the reflectance without causing harmful effects is still an important issue for crystalline Si solar cells. By using the method described in this paper, the optical properties of solar cells can be improved.

  19. Combination of silicon nitride and porous silicon induced optoelectronic features enhancement of multicrystalline silicon solar cells

    Energy Technology Data Exchange (ETDEWEB)

    Rabha, Mohamed Ben; Dimassi, Wissem; Gaidi, Mounir; Ezzaouia, Hatem; Bessais, Brahim [Laboratoire de Photovoltaique, Centre de Recherches et des Technologies de l' Energie, Technopole de Borj-Cedria, BP 95, 2050 Hammam-Lif (Tunisia)

    2011-06-15

    The effects of antireflection (ARC) and surface passivation films on optoelectronic features of multicrystalline silicon (mc-Si) were investigated in order to perform high efficiency solar cells. A double layer consisting of Plasma Enhanced Chemical Vapor Deposition (PECVD) of silicon nitride (SiN{sub x}) on porous silicon (PS) was achieved on mc-Si surfaces. It was found that this treatment decreases the total surface reflectivity from about 25% to around 6% in the 450-1100 nm wavelength range. As a result, the effective minority carrier diffusion length, estimated from the Laser-beam-induced current (LBIC) method, was found to increase from 312 {mu}m for PS-treated cells to about 798 {mu}m for SiN{sub x}/PS-treated ones. The deposition of SiN{sub x} was found to impressively enhance the minority carrier diffusion length probably due to hydrogen passivation of surface, grain boundaries and bulk defects. Fourier Transform Infrared Spectroscopy (FTIR) shows that the vibration modes of the highly suitable passivating Si-H bonds exhibit frequency shifts toward higher wavenumber, depending on the x ratio of the introduced N atoms neighbors. (copyright 2011 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim) (orig.)

  20. Photoluminescence studies on porous silicon/polymer heterostructure

    International Nuclear Information System (INIS)

    Mishra, J.K.; Bhunia, S.; Banerjee, S.; Banerji, P.

    2008-01-01

    Hybrid devices formed by filling porous silicon with MEH-PPV or poly [2-methoxy-5(2-ethylhexyloxy-p-phenylenevinylene)] have been investigated in this work. Analyses of the structures by scanning electron microscopy (SEM) demonstrated that the porous silicon layer was filled by the polymer with no significant change of the structures except that the polymer was infiltrated in the pores. The photoluminescence (PL) of the structures at 300 K showed that the emission intensity was very high as compared with that of the MEH-PPV films on different substrates such as crystalline silicon (c-Si) and indium tin oxide (ITO). The PL peak in the MEH-PPV/porous silicon composite structure is found to be shifted towards higher energy in comparison with porous silicon PL. A number of possibilities are discussed to explain the observations

  1. Thin film silicon by a microwave plasma deposition technique: Growth and devices, and, interface effects in amorphous silicon/crystalline silicon solar cells

    Science.gov (United States)

    Jagannathan, Basanth

    Thin film silicon (Si) was deposited by a microwave plasma CVD technique, employing double dilution of silane, for the growth of low hydrogen content Si films with a controllable microstructure on amorphous substrates at low temperatures (prepared by this technique. Such films showed a dark conductivity ˜10sp{-6} S/cm, with a conduction activation energy of 0.49 eV. Film growth and properties have been compared for deposition in Ar and He carrier systems and growth models have been proposed. Low temperature junction formation by undoped thin film silicon was examined through a thin film silicon/p-type crystalline silicon heterojunctions. The thin film silicon layers were deposited by rf glow discharge, dc magnetron sputtering and microwave plasma CVD. The hetero-interface was identified by current transport analysis and high frequency capacitance methods as the key parameter controlling the photovoltaic (PV) response. The effect of the interface on the device properties (PV, junction, and carrier transport) was examined with respect to modifications created by chemical treatment, type of plasma species, their energy and film microstructure interacting with the substrate. Thermally stimulated capacitance was used to determine the interfacial trap parameters. Plasma deposition of thin film silicon on chemically clean c-Si created electron trapping sites while hole traps were seen when a thin oxide was present at the interface. Under optimized conditions, a 10.6% efficient cell (11.5% with SiOsb2 A/R) with an open circuit voltage of 0.55 volts and a short circuit current density of 30 mA/cmsp2 was fabricated.

  2. Damage-free laser patterning of silicon nitride on textured crystalline silicon using an amorphous silicon etch mask for Ni/Cu plated silicon solar cells

    Energy Technology Data Exchange (ETDEWEB)

    Bailly, Mark S., E-mail: mbailly@asu.edu; Karas, Joseph; Jain, Harsh; Dauksher, William J.; Bowden, Stuart

    2016-08-01

    We investigate the optimization of laser ablation with a femtosecond laser for direct and indirect removal of SiN{sub x} on alkaline textured c-Si. Our proposed resist-free indirect removal process uses an a-Si:H etch mask and is demonstrated to have a drastically improved surface quality of the laser processed areas when compared to our direct removal process. Scanning electron microscope images of ablated sites show the existence of substantial surface defects for the standard direct removal process, and the reduction of those defects with our proposed process. Opening of SiN{sub x} and SiO{sub x} passivating layers with laser ablation is a promising alternative to the standard screen print and fire process for making contact to Si solar cells. The potential for small contacts from laser openings of dielectrics coupled with the selective deposition of metal from light induced plating allows for high-aspect-ratio metal contacts for front grid metallization. The minimization of defects generated in this process would serve to enhance the performance of the device and provides the motivation for our work. - Highlights: • Direct laser removal of silicon nitride (SiN{sub x}) damages textured silicon. • Direct laser removal of amorphous silicon (a-Si) does not damage textured silicon. • a-Si can be used as a laser patterned etch mask for SiN{sub x}. • Chemically patterned SiN{sub x} sites allow for Ni/Cu plating.

  3. Characterization of oxygen dimer-enriched silicon detectors

    CERN Document Server

    Boisvert, V; Moll, M; Murin, L I; Pintilie, I

    2005-01-01

    Various types of silicon material and silicon p+n diodes have been treated to increase the concentration of the oxygen dimer (O2i) defect. This was done by exposing the bulk material and the diodes to 6 MeV electrons at a temperature of about 350 °C. FTIR spectroscopy has been performed on the processed material confirming the formation of oxygen dimer defects in Czochralski silicon pieces. We also show results from TSC characterization on processed diodes. Finally, we investigated the influence of the dimer enrichment process on the depletion voltage of silicon diodes and performed 24 GeV/c proton irradiations to study the evolution of the macroscopic diode characteristics as a function of fluence.

  4. Silicon heterojunction solar cells with novel fluorinated n-type nanocrystalline silicon oxide emitters on p-type crystalline silicon

    Science.gov (United States)

    Dhar, Sukanta; Mandal, Sourav; Das, Gourab; Mukhopadhyay, Sumita; Pratim Ray, Partha; Banerjee, Chandan; Barua, Asok Kumar

    2015-08-01

    A novel fluorinated phosphorus doped silicon oxide based nanocrystalline material have been used to prepare heterojunction solar cells on flat p-type crystalline silicon (c-Si) Czochralski (CZ) wafers. The n-type nc-SiO:F:H material were deposited by radio frequency plasma enhanced chemical vapor deposition. Deposited films were characterized in detail by using atomic force microscopy (AFM), high resolution transmission electron microscopy (HRTEM), Raman, fourier transform infrared spectroscopy (FTIR) and optoelectronics properties have been studied using temperature dependent conductivity measurement, Ellipsometry, UV-vis spectrum analysis etc. It is observed that the cell fabricated with fluorinated silicon oxide emitter showing higher initial efficiency (η = 15.64%, Jsc = 32.10 mA/cm2, Voc = 0.630 V, FF = 0.77) for 1 cm2 cell area compare to conventional n-a-Si:H emitter (14.73%) on flat c-Si wafer. These results indicate that n type nc-SiO:F:H material is a promising candidate for heterojunction solar cell on p-type crystalline wafers. The high Jsc value is associated with excellent quantum efficiencies at short wavelengths (<500 nm).

  5. Formation of iron disilicide on amorphous silicon

    Science.gov (United States)

    Erlesand, U.; Östling, M.; Bodén, K.

    1991-11-01

    Thin films of iron disilicide, β-FeSi 2 were formed on both amorphous silicon and on crystalline silicon. The β-phase is reported to be semiconducting with a direct band-gap of about 0.85-0.89 eV. This phase is known to form via a nucleation-controlled growth process on crystalline silicon and as a consequence a rather rough silicon/silicide interface is usually formed. In order to improve the interface a bilayer structure of amorphous silicon and iron was sequentially deposited on Czochralski silicon in an e-gun evaporation system. Secondary ion mass spectrometry profiling (SIMS) and scanning electron micrographs revealed an improvement of the interface sharpness. Rutherford backscattering spectrometry (RBS) and X-ray diffractiometry showed β-FeSi 2 formation already at 525°C. It was also observed that the silicide growth was diffusion-controlled, similar to what has been reported for example in the formation of NiSi 2 for the reaction of nickel on amorphous silicon. The kinetics of the FeSi 2 formation in the temperature range 525-625°C was studied by RBS and the activation energy was found to be 1.5 ± 0.1 eV.

  6. Thermal Properties of the Silicon Microstrip Endcap Detector

    CERN Document Server

    Feld, Lutz; Hammarström, R

    1998-01-01

    Irradiated silicon detectors must be cooled in order to guarantee stable short and long term operation. Using the SiF1 milestone prototype we have performed a detailed analysis of the thermal properties of the silicon microstrip endcap detector. The strongest constraint on the cooling system is shown to be set by the need to avoid thermal runaway of the silicon detectors. We show that, taking into account the radiation damage to the silicon after 10 years of LHC operation and including some safety margin, the detector will need a cooling fluid temperature of around -20 C. The highest temperature on the silicon will then be in the range -15 C to -10 C. This sets an upper limit on the ambient temperature in the tracker volume.

  7. Controlling the flow of light with silicon nanostructures

    International Nuclear Information System (INIS)

    Park, W

    2010-01-01

    Silicon is an important material for integrated photonics applications. High refractive index and transparency in the infrared region makes it an ideal platform to implement nanostructures for novel optical devices. We fabricated silicon photonic crystals and experimentally demonstrated negative refraction and self-collimation. We also used heterodyne near-field scanning optical microscope to directly visualize the anomalous wavefronts. When the periodicity is much smaller than wavelength, silicon photonic crystal can be described by the effective medium theory. By engineering effective refractive index with silicon nanorod size, we demonstrated an all-dielectric cloak structure which can hide objects in front of a highly reflecting plane. The work discussed in this review shows the powerful design flexibility and versatility of silicon nanostructures

  8. Quantum Properties of Dichroic Silicon Vacancies in Silicon Carbide

    Science.gov (United States)

    Nagy, Roland; Widmann, Matthias; Niethammer, Matthias; Dasari, Durga B. R.; Gerhardt, Ilja; Soykal, Öney O.; Radulaski, Marina; Ohshima, Takeshi; Vučković, Jelena; Son, Nguyen Tien; Ivanov, Ivan G.; Economou, Sophia E.; Bonato, Cristian; Lee, Sang-Yun; Wrachtrup, Jörg

    2018-03-01

    Although various defect centers have displayed promise as either quantum sensors, single photon emitters, or light-matter interfaces, the search for an ideal defect with multifunctional ability remains open. In this spirit, we study the dichroic silicon vacancies in silicon carbide that feature two well-distinguishable zero-phonon lines and analyze the quantum properties in their optical emission and spin control. We demonstrate that this center combines 40% optical emission into the zero-phonon lines showing the contrasting difference in optical properties with varying temperature and polarization, and a 100% increase in the fluorescence intensity upon the spin resonance, and long spin coherence time of their spin-3 /2 ground states up to 0.6 ms. These results single out this defect center as a promising system for spin-based quantum technologies.

  9. Geochemistry of silicon isotopes

    Energy Technology Data Exchange (ETDEWEB)

    Ding, Tiping; Li, Yanhe; Gao, Jianfei; Hu, Bin [Chinese Academy of Geological Science, Beijing (China). Inst. of Mineral Resources; Jiang, Shaoyong [China Univ. of Geosciences, Wuhan (China).

    2018-04-01

    Silicon is one of the most abundant elements in the Earth and silicon isotope geochemistry is important in identifying the silicon source for various geological bodies and in studying the behavior of silicon in different geological processes. This book starts with an introduction on the development of silicon isotope geochemistry. Various analytical methods are described and compared with each other in detail. The mechanisms of silicon isotope fractionation are discussed, and silicon isotope distributions in various extraterrestrial and terrestrial reservoirs are updated. Besides, the applications of silicon isotopes in several important fields are presented.

  10. High-performance silicon nanotube tunneling FET for ultralow-power logic applications

    KAUST Repository

    Fahad, Hossain M.; Hussain, Muhammad Mustafa

    2013-01-01

    To increase typically low output drive currents from tunnel field-effect transistors (FETs), we show a silicon vertical nanotube (NT) architecture-based FET's effectiveness. Using core (inner) and shell (outer) gate stacks, the silicon NT tunneling FET shows a sub-60 mV/dec subthreshold slope, ultralow off -state leakage current, higher drive current compared with gate-all-around nanowire silicon tunnel FETs. © 1963-2012 IEEE.

  11. Photonic Crystal Sensors Based on Porous Silicon

    Directory of Open Access Journals (Sweden)

    Claudia Pacholski

    2013-04-01

    Full Text Available Porous silicon has been established as an excellent sensing platform for the optical detection of hazardous chemicals and biomolecular interactions such as DNA hybridization, antigen/antibody binding, and enzymatic reactions. Its porous nature provides a high surface area within a small volume, which can be easily controlled by changing the pore sizes. As the porosity and consequently the refractive index of an etched porous silicon layer depends on the electrochemial etching conditions photonic crystals composed of multilayered porous silicon films with well-resolved and narrow optical reflectivity features can easily be obtained. The prominent optical response of the photonic crystal decreases the detection limit and therefore increases the sensitivity of porous silicon sensors in comparison to sensors utilizing Fabry-Pérot based optical transduction. Development of porous silicon photonic crystal sensors which allow for the detection of analytes by the naked eye using a simple color change or the fabrication of stacked porous silicon photonic crystals showing two distinct optical features which can be utilized for the discrimination of analytes emphasize its high application potential.

  12. Photonic Crystal Sensors Based on Porous Silicon

    Science.gov (United States)

    Pacholski, Claudia

    2013-01-01

    Porous silicon has been established as an excellent sensing platform for the optical detection of hazardous chemicals and biomolecular interactions such as DNA hybridization, antigen/antibody binding, and enzymatic reactions. Its porous nature provides a high surface area within a small volume, which can be easily controlled by changing the pore sizes. As the porosity and consequently the refractive index of an etched porous silicon layer depends on the electrochemial etching conditions photonic crystals composed of multilayered porous silicon films with well-resolved and narrow optical reflectivity features can easily be obtained. The prominent optical response of the photonic crystal decreases the detection limit and therefore increases the sensitivity of porous silicon sensors in comparison to sensors utilizing Fabry-Pérot based optical transduction. Development of porous silicon photonic crystal sensors which allow for the detection of analytes by the naked eye using a simple color change or the fabrication of stacked porous silicon photonic crystals showing two distinct optical features which can be utilized for the discrimination of analytes emphasize its high application potential. PMID:23571671

  13. Silicon Micromachines for Science and Technology

    International Nuclear Information System (INIS)

    Bishop, David J.

    2002-01-01

    The era of silicon micromechanics is upon us. In areas as diverse as telecommunications, automotive, aerospace, chemistry, entertainment and basic science, the ability to build microscopic machines from silicon is having a revolutionary impact. In my talk, I will discuss what micromachines are, how they are built and show examples of how they will have a revolutionary impact in many areas of science as well as technology.

  14. Stable configurations of graphene on silicon

    Energy Technology Data Exchange (ETDEWEB)

    Javvaji, Brahmanandam; Shenoy, Bhamy Maithry [Department of Aerospace Engineering, Indian Institute of Science, Bangalore 560012 (India); Mahapatra, D. Roy, E-mail: droymahapatra@aero.iisc.ernet.in [Department of Aerospace Engineering, Indian Institute of Science, Bangalore 560012 (India); Ravikumar, Abhilash [Department of Metallurgical and Materials Engineering, National Institute of Technology Karnataka, Surathkal 575025 (India); Hegde, G.M. [Center for Nano Science and Engineering, Indian Institute of Science, Bangalore 560012 (India); Rizwan, M.R. [Department of Metallurgical and Materials Engineering, National Institute of Technology Karnataka, Surathkal 575025 (India)

    2017-08-31

    Highlights: • Simulations of epitaxial growth process for silicon–graphene system is performed. • Identified the most favourable orientation of graphene sheet on silicon substrate. • Atomic local strain due to the silicon–carbon bond formation is analyzed. - Abstract: Integration of graphene on silicon-based nanostructures is crucial in advancing graphene based nanoelectronic device technologies. The present paper provides a new insight on the combined effect of graphene structure and silicon (001) substrate on their two-dimensional anisotropic interface. Molecular dynamics simulations involving the sub-nanoscale interface reveal a most favourable set of temperature independent orientations of the monolayer graphene sheet with an angle of ∽15° between its armchair direction and [010] axis of the silicon substrate. While computing the favorable stable orientations, both the translation and the rotational vibrations of graphene are included. The possible interactions between the graphene atoms and the silicon atoms are identified from their coordination. Graphene sheet shows maximum bonding density with bond length 0.195 nm and minimum bond energy when interfaced with silicon substrate at 15° orientation. Local deformation analysis reveals probability distribution with maximum strain levels of 0.134, 0.047 and 0.029 for 900 K, 300 K and 100 K, respectively in silicon surface for 15° oriented graphene whereas the maximum probable strain in graphene is about 0.041 irrespective of temperature. Silicon–silicon dimer formation is changed due to silicon–carbon bonding. These results may help further in band structure engineering of silicon–graphene lattice.

  15. Superacid Passivation of Crystalline Silicon Surfaces.

    Science.gov (United States)

    Bullock, James; Kiriya, Daisuke; Grant, Nicholas; Azcatl, Angelica; Hettick, Mark; Kho, Teng; Phang, Pheng; Sio, Hang C; Yan, Di; Macdonald, Daniel; Quevedo-Lopez, Manuel A; Wallace, Robert M; Cuevas, Andres; Javey, Ali

    2016-09-14

    The reduction of parasitic recombination processes commonly occurring within the silicon crystal and at its surfaces is of primary importance in crystalline silicon devices, particularly in photovoltaics. Here we explore a simple, room temperature treatment, involving a nonaqueous solution of the superacid bis(trifluoromethane)sulfonimide, to temporarily deactivate recombination centers at the surface. We show that this treatment leads to a significant enhancement in optoelectronic properties of the silicon wafer, attaining a level of surface passivation in line with state-of-the-art dielectric passivation films. Finally, we demonstrate its advantage as a bulk lifetime and process cleanliness monitor, establishing its compatibility with large area photoluminescence imaging in the process.

  16. The influence of ingot annealing on the corrosion resistance of a PrFeCoBNbP alloy

    International Nuclear Information System (INIS)

    Oliveira, M.C.L.; Takiishi, H.; Faria, R.N.; Costa, I.

    2008-01-01

    The influence of the annealing time on the corrosion resistance of a Pr-Fe-Co-B-Nb alloy with the addition of 0.1 wt% P was investigated here using potentiodynamic polarization and electrochemical impedance spectroscopy (EIS). The cast ingot alloys were annealed at 1100 deg. C for 10, 15 and 20 h. The specimens were immersed for 30 days in naturally aerated 0.02 M Na 2 HPO 4 solution at room temperature, during which period the evolution of the electrochemical behavior was assessed using EIS. The results indicated that the corrosion resistance of the Pr 14 Fe bal Co 16 B 6 Nb 0.1 P 0.25 alloy was related to the annealing time and, hence, to its microstructure. Annealing at 1100 deg. C for 10 h was insufficient to eliminate the Fe-α phase from the alloy microstructure, whereas annealing for 15 and 20 h removed an increasing amount of Fe-α phase, thereby increasing the alloy's corrosion resistance

  17. Strain-induced generation of silicon nanopillars

    International Nuclear Information System (INIS)

    Bollani, Monica; Osmond, Johann; Nicotra, Giuseppe; Spinella, Corrado; Narducci, Dario

    2013-01-01

    Silicon metal-assisted chemical etching (MACE) is a nanostructuring technique exploiting the enhancement of the silicon etch rate at some metal–silicon interfaces. Compared to more traditional approaches, MACE is a high-throughput technique, and it is one of the few that enables the growth of vertical 1D structures of virtually unlimited length. As such, it has already found relevant technological applications in fields ranging from energy conversion to biosensing. Yet, its implementation has always required metal patterning to obtain nanopillars. Here, we report how MACE may lead to the formation of porous silicon nanopillars even in the absence of gold patterning. We show how the use of inhomogeneous yet continuous gold layers leads to the generation of a stress field causing spontaneous local delamination of the metal—and to the formation of silicon nanopillars where the metal disruption occurs. We observed the spontaneous formation of nanopillars with diameters ranging from 40 to 65 nm and heights up to 1 μm. Strain-controlled generation of nanopillars is consistent with a mechanism of silicon oxidation by hole injection through the metal layer. Spontaneous nanopillar formation could enable applications of this method to contexts where ordered distributions of nanopillars are not required, while patterning by high-resolution techniques is either impractical or unaffordable. (paper)

  18. Porous silicon-based passivation and gettering in polycrystalline silicon solar cells

    International Nuclear Information System (INIS)

    Dimassi, W.; Bouaiecha, M.; Saadoun, M.; Bessaies, B.; Ezzaouia, H.; Bennaceur, R.

    2002-01-01

    In this work, we report on the effect of introducing a superficial porous silicon (PS) layer on the electrical characteristics of polycrystalline silicon solar cells. The PS layer was formed using a vapour etching (VE)-based method. In addition to its known anti-reflecting action, the forming hydrogen-rich PS layer acts as a passivating agent for the surface of the cell. As a result we found an improvement of the I-V characteristics in dark conditions and AM1 illumination. We show that when the formation of a superficial PS layer is followed by a heat treatment, gettering of impurities from the polycrystalline silicon material is possible. After the removal of the PS layer and the formation of the photovoltaic (PV) structure, we observed an increase of the light-beam-induced-current (LBIC) for treatment temperatures not exceeding 900 deg. C. An improvement of the bulk minority carrier diffusion length and the grain boundary (GB) recombination velocity were observed as the temperature rises, although a global decrease of the LBIC current was observed for temperatures greater than 900 deg. C

  19. High-performance silicon nanotube tunneling FET for ultralow-power logic applications

    KAUST Repository

    Fahad, Hossain M.

    2013-03-01

    To increase typically low output drive currents from tunnel field-effect transistors (FETs), we show a silicon vertical nanotube (NT) architecture-based FET\\'s effectiveness. Using core (inner) and shell (outer) gate stacks, the silicon NT tunneling FET shows a sub-60 mV/dec subthreshold slope, ultralow off -state leakage current, higher drive current compared with gate-all-around nanowire silicon tunnel FETs. © 1963-2012 IEEE.

  20. Large volume cryogenic silicon detectors

    International Nuclear Information System (INIS)

    Braggio, C.; Boscardin, M.; Bressi, G.; Carugno, G.; Corti, D.; Galeazzi, G.; Zorzi, N.

    2009-01-01

    We present preliminary measurements for the development of a large volume silicon detector to detect low energy and low rate energy depositions. The tested detector is a one cm-thick silicon PIN diode with an active volume of 31 cm 3 , cooled to the liquid helium temperature to obtain depletion from thermally-generated free carriers. A thorough study has been done to show that effects of charge trapping during drift disappears at a bias field value of the order of 100V/cm.

  1. Influence of Chemical Composition and Structure in Silicon Dielectric Materials on Passivation of Thin Crystalline Silicon on Glass.

    Science.gov (United States)

    Calnan, Sonya; Gabriel, Onno; Rothert, Inga; Werth, Matteo; Ring, Sven; Stannowski, Bernd; Schlatmann, Rutger

    2015-09-02

    In this study, various silicon dielectric films, namely, a-SiOx:H, a-SiNx:H, and a-SiOxNy:H, grown by plasma enhanced chemical vapor deposition (PECVD) were evaluated for use as interlayers (ILs) between crystalline silicon and glass. Chemical bonding analysis using Fourier transform infrared spectroscopy showed that high values of oxidant gases (CO2 and/or N2), added to SiH4 during PECVD, reduced the Si-H and N-H bond density in the silicon dielectrics. Various three layer stacks combining the silicon dielectric materials were designed to minimize optical losses between silicon and glass in rear side contacted heterojunction pn test cells. The PECVD grown silicon dielectrics retained their functionality despite being subjected to harsh subsequent processing such as crystallization of the silicon at 1414 °C or above. High values of short circuit current density (Jsc; without additional hydrogen passivation) required a high density of Si-H bonds and for the nitrogen containing films, additionally, a high N-H bond density. Concurrently high values of both Jsc and open circuit voltage Voc were only observed when [Si-H] was equal to or exceeded [N-H]. Generally, Voc correlated with a high density of [Si-H] bonds in the silicon dielectric; otherwise, additional hydrogen passivation using an active plasma process was required. The highest Voc ∼ 560 mV, for a silicon acceptor concentration of about 10(16) cm(-3), was observed for stacks where an a-SiOxNy:H film was adjacent to the silicon. Regardless of the cell absorber thickness, field effect passivation of the buried silicon surface by the silicon dielectric was mandatory for efficient collection of carriers generated from short wavelength light (in the vicinity of the glass-Si interface). However, additional hydrogen passivation was obligatory for an increased diffusion length of the photogenerated carriers and thus Jsc in solar cells with thicker absorbers.

  2. Internal friction in irradiated silicon

    International Nuclear Information System (INIS)

    Kalanov, M.U.; Pajzullakhanov, M.S.; Khajdarov, T.; Ummatov, Kh.

    1999-01-01

    The submicroscopic heterogeneities in mono- and polycrystal silicon and the influence of X-ray radiation on them were investigated using the ultrasound resonance method. Disk-shaped samples of 27.5 mm in diameter and 4 mm in thickness, with the flat surface parallel to crystallographic plane (111), were irradiated by X-ray beam of 1 Wt/cm 2 (50 KeV, Mo K α ) during 10 hours. Relations of internal frictions (Q -1 ) of samples and their relative attitude (ψ) - Q -1 (ψ) show that there is a presence of double-humped configuration for monocrystal silicon with the peaks at ψ=900 and 270 degrees. The relations Q -1 (ψ) remain the same after the irradiation. However, the peak width becomes larger. This data show that the configuration and attitude of the heterogeneities remain the same after the irradiation. The double-humped configuration was not discovered for the relations Q -1 (ψ) of polycrystal silicon. It is explained by the fact that there is an isotropic distribution in the content of many blocks and granules

  3. Stain-etched porous silicon nanostructures for multicrystalline silicon-based solar cells

    Science.gov (United States)

    Ben Rabha, M.; Hajji, M.; Belhadj Mohamed, S.; Hajjaji, A.; Gaidi, M.; Ezzaouia, H.; Bessais, B.

    2012-02-01

    In this paper, we study the optical, optoelectronic and photoluminescence properties of stain-etched porous silicon nanostructures obtained with different etching times. Special attention is given to the use of the stain-etched PS as an antireflection coating as well as for surface passivating capabilities. The surface morphology has been analyzed by scanning electron microscopy. The evolution of the Si-O and Si-H absorption bands was analyzed by Fourier transform infrared spectrometry before and after PS treatment. Results show that stain etching of the silicon surface drops the total reflectivity to about 7% in the 400-1100 nm wavelength range and the minority carrier lifetime enhances to about 48 μs.

  4. Femtosecond laser irradiation-induced infrared absorption on silicon surfaces

    Directory of Open Access Journals (Sweden)

    Qinghua Zhu

    2015-04-01

    Full Text Available The near-infrared (NIR absorption below band gap energy of crystalline silicon is significantly increased after the silicon is irradiated with femtosecond laser pulses at a simple experimental condition. The absorption increase in the NIR range primarily depends on the femtosecond laser pulse energy, pulse number, and pulse duration. The Raman spectroscopy analysis shows that after the laser irradiation, the silicon surface consists of silicon nanostructure and amorphous silicon. The femtosecond laser irradiation leads to the formation of a composite of nanocrystalline, amorphous, and the crystal silicon substrate surface with microstructures. The composite has an optical absorption enhancement at visible wavelengths as well as at NIR wavelength. The composite may be useful for an NIR detector, for example, for gas sensing because of its large surface area.

  5. White-light emission from porous-silicon-aluminium Schottky junctions

    International Nuclear Information System (INIS)

    Masini, G.; La Monica, S.; Maiello, G.

    1996-01-01

    Porous-silicon-based white-light-emitting devices are presented. The fabrication process on different substrates is described. The peculiarities of technological steps for device fabrication (porous-silicon formation and aluminium treatment) are underlined. Doping profile of the porous layer, current-voltage characteristics, time response, lifetime tests and electroluminescence emission spectrum of the device are presented. A model for electrical behaviour of Al/porous silicon Schottky junction is presented. Electroluminescence spectrum of the presented devices showed strong similarities with white emission from crystalline silicon junctions in the breakdown region

  6. Analytical and Experimental Evaluation of Joining Silicon Carbide to Silicon Carbide and Silicon Nitride to Silicon Nitride for Advanced Heat Engine Applications Phase II

    Energy Technology Data Exchange (ETDEWEB)

    Sundberg, G.J.

    1994-01-01

    Techniques were developed to produce reliable silicon nitride to silicon nitride (NCX-5101) curved joins which were used to manufacture spin test specimens as a proof of concept to simulate parts such as a simple rotor. Specimens were machined from the curved joins to measure the following properties of the join interlayer: tensile strength, shear strength, 22 C flexure strength and 1370 C flexure strength. In parallel, extensive silicon nitride tensile creep evaluation of planar butt joins provided a sufficient data base to develop models with accurate predictive capability for different geometries. Analytical models applied satisfactorily to the silicon nitride joins were Norton's Law for creep strain, a modified Norton's Law internal variable model and the Monkman-Grant relationship for failure modeling. The Theta Projection method was less successful. Attempts were also made to develop planar butt joins of siliconized silicon carbide (NT230).

  7. Electrical effects of transient neutron irradiation of silicon devices

    International Nuclear Information System (INIS)

    Hjalmarson, H.P.; Pease, R.L.; Van Ginhoven, R.M.; Schultz, P.A.; Modine, N.A.

    2007-01-01

    The key effects of combined transient neutron and ionizing radiation on silicon diodes and bipolar junctions transistors are described. The results show that interstitial defect reactions dominate the annealing effects in the first stage of annealing for certain devices. Furthermore, the results show that oxide trapped charge can influence the effects of bulk silicon displacement damage for particular devices

  8. Electrical leakage phenomenon in heteroepitaxial cubic silicon carbide on silicon

    Science.gov (United States)

    Pradeepkumar, Aiswarya; Zielinski, Marcin; Bosi, Matteo; Verzellesi, Giovanni; Gaskill, D. Kurt; Iacopi, Francesca

    2018-06-01

    Heteroepitaxial 3C-SiC films on silicon substrates are of technological interest as enablers to integrate the excellent electrical, electronic, mechanical, thermal, and epitaxial properties of bulk silicon carbide into well-established silicon technologies. One critical bottleneck of this integration is the establishment of a stable and reliable electronic junction at the heteroepitaxial interface of the n-type SiC with the silicon substrate. We have thus investigated in detail the electrical and transport properties of heteroepitaxial cubic silicon carbide films grown via different methods on low-doped and high-resistivity silicon substrates by using van der Pauw Hall and transfer length measurements as test vehicles. We have found that Si and C intermixing upon or after growth, particularly by the diffusion of carbon into the silicon matrix, creates extensive interstitial carbon traps and hampers the formation of a stable rectifying or insulating junction at the SiC/Si interface. Although a reliable p-n junction may not be realistic in the SiC/Si system, we can achieve, from a point of view of the electrical isolation of in-plane SiC structures, leakage suppression through the substrate by using a high-resistivity silicon substrate coupled with deep recess etching in between the SiC structures.

  9. Fluorescence and thermoluminescence in silicon oxide films rich in silicon

    International Nuclear Information System (INIS)

    Berman M, D.; Piters, T. M.; Aceves M, M.; Berriel V, L. R.; Luna L, J. A.

    2009-10-01

    In this work we determined the fluorescence and thermoluminescence (TL) creation spectra of silicon rich oxide films (SRO) with three different silicon excesses. To study the TL of SRO, 550 nm of SRO film were deposited by Low Pressure Chemical Vapor Deposition technique on N-type silicon substrates with resistivity in the order of 3 to 5 Ω-cm with silicon excess controlled by the ratio of the gases used in the process, SRO films with Ro= 10, 20 and 30 (12-6% silicon excess) were obtained. Then, they were thermally treated in N 2 at high temperatures to diffuse and homogenize the silicon excess. In the fluorescence spectra two main emission regions are observed, one around 400 nm and one around 800 nm. TL creation spectra were determined by plotting the integrated TL intensity as function of the excitation wavelength. (Author)

  10. High damage tolerance of electrochemically lithiated silicon

    Science.gov (United States)

    Wang, Xueju; Fan, Feifei; Wang, Jiangwei; Wang, Haoran; Tao, Siyu; Yang, Avery; Liu, Yang; Beng Chew, Huck; Mao, Scott X.; Zhu, Ting; Xia, Shuman

    2015-01-01

    Mechanical degradation and resultant capacity fade in high-capacity electrode materials critically hinder their use in high-performance rechargeable batteries. Despite tremendous efforts devoted to the study of the electro–chemo–mechanical behaviours of high-capacity electrode materials, their fracture properties and mechanisms remain largely unknown. Here we report a nanomechanical study on the damage tolerance of electrochemically lithiated silicon. Our in situ transmission electron microscopy experiments reveal a striking contrast of brittle fracture in pristine silicon versus ductile tensile deformation in fully lithiated silicon. Quantitative fracture toughness measurements by nanoindentation show a rapid brittle-to-ductile transition of fracture as the lithium-to-silicon molar ratio is increased to above 1.5. Molecular dynamics simulations elucidate the mechanistic underpinnings of the brittle-to-ductile transition governed by atomic bonding and lithiation-induced toughening. Our results reveal the high damage tolerance in amorphous lithium-rich silicon alloys and have important implications for the development of durable rechargeable batteries. PMID:26400671

  11. Varying temperature and silicon content in nanodiamond growth: effects on silicon-vacancy centres.

    Science.gov (United States)

    Choi, Sumin; Leong, Victor; Davydov, Valery A; Agafonov, Viatcheslav N; Cheong, Marcus W O; Kalashnikov, Dmitry A; Krivitsky, Leonid A

    2018-02-28

    Nanodidamonds containing colour centres open up many applications in quantum information processing, metrology, and quantum sensing. However, controlling the synthesis of nanodiamonds containing silicon vacancy (SiV) centres is still not well understood. Here we study nanodiamonds produced by a high-pressure high-temperature method without catalyst metals, focusing on two samples with clear SiV signatures. Different growth temperatures and relative content of silicon in the initial compound between the samples altered their nanodiamond size distributions and abundance of SiV centres. Our results show that nanodiamond growth can be controlled and optimised for different applications.

  12. Buried oxide layer in silicon

    Science.gov (United States)

    Sadana, Devendra Kumar; Holland, Orin Wayne

    2001-01-01

    A process for forming Silicon-On-Insulator is described incorporating the steps of ion implantation of oxygen into a silicon substrate at elevated temperature, ion implanting oxygen at a temperature below 200.degree. C. at a lower dose to form an amorphous silicon layer, and annealing steps to form a mixture of defective single crystal silicon and polycrystalline silicon or polycrystalline silicon alone and then silicon oxide from the amorphous silicon layer to form a continuous silicon oxide layer below the surface of the silicon substrate to provide an isolated superficial layer of silicon. The invention overcomes the problem of buried isolated islands of silicon oxide forming a discontinuous buried oxide layer.

  13. Ion beam studied of silicon oxynitride and silicon nitroxide thin layers

    International Nuclear Information System (INIS)

    Oude Elferink, J.B.

    1989-01-01

    In this the processes occurring during high temperature treatments of silicon oxynitride and silicon oxide layers are described. Oxynitride layers with various atomic oxygen to nitrogen concentration ration (O/N) are considered. The high energy ion beam techniques Rutherford backscattering spectroscopy, elastic recoil detection and nuclear reaction analysis have been used to study the layer structures. A detailed discussion of these ion beam techniques is given. Numerical methods used to obtain quantitative data on elemental compositions and depth profiles are described. The electrical compositions and depth profiles are described. The electrical properties of silicon nitride films are known to be influenced by the behaviour of hydrogen in the film during high temperature anneling. Investigations of the behaviour of hydrogen are presented. Oxidation of silicon (oxy)nitride films in O 2 /H 2 0/HCl and nitridation of silicon dioxide films in NH 3 are considered since oxynitrides are applied as an oxidation mask in the LOCOS (Local oxidation of silicon) process. The nitridation of silicon oxide layers in an ammonia ambient is considered. The initial stage and the dependence on the oxide thickness of nitrogen and hydrogen incorporation are discussed. Finally, oxidation of silicon oxynitride layers and of silicon oxide layers are compared. (author). 76 refs.; 48 figs.; 1 tab

  14. Porous-shaped silicon carbide ultraviolet photodetectors on porous silicon substrates

    Energy Technology Data Exchange (ETDEWEB)

    Naderi, N., E-mail: naderi.phd@gmail.com [Nano-Optoelectronics Research Laboratory, School of Physics, Universiti Sains Malaysia, 11800 USM, Penang (Malaysia); Hashim, M.R. [Nano-Optoelectronics Research Laboratory, School of Physics, Universiti Sains Malaysia, 11800 USM, Penang (Malaysia)

    2013-03-05

    Highlights: ► Porous-shaped silicon carbide thin film was deposited on porous silicon substrate. ► Thermal annealing was followed to enhance the physical properties of samples. ► Metal–semiconductor-metal ultraviolet detectors were fabricated on samples. ► The effect of annealing temperature on electrical performance of devices was studied. ► The efficiency of photodetectors was enhanced by annealing at elevated temperatures. -- Abstract: A metal–semiconductor-metal (MSM) ultraviolet photodetector was fabricated based on a porous-shaped structure of silicon carbide (SiC). For increasing the surface roughness of SiC and hence enhancing the light absorption effect in fabricated devices, porous silicon (PS) was chosen as a template; SiC was deposited on PS substrates via radio frequency magnetron sputtering. Therefore, the deposited layers followed the structural pattern of PS skeleton and formed a porous-shaped SiC layer on PS substrate. The structural properties of samples showed that the as-deposited SiC was amorphous. Thus, a post-deposition annealing process with elevated temperatures was required to convert its amorphous phase to crystalline phase. The morphology of the sputtered samples was examined via scanning electron and atomic force microscopies. The grain size and roughness of the deposited layers clearly increased upon an increase in the annealing temperature. The optical properties of sputtered SiC were enhanced due to applying high temperatures. The most intense photoluminescence peak was observed for the sample with 1200 °C of annealing temperature. For the metallization of the SiC substrates to fabricate MSM photodetectors, two interdigitated Schottky contacts of Ni with four fingers for each electrode were deposited onto all the porous substrates. The optoelectronic characteristics of MSM UV photodetectors with porous-shaped SiC substrates were studied in the dark and under UV illumination. The electrical characteristics of fabricated

  15. Porous-shaped silicon carbide ultraviolet photodetectors on porous silicon substrates

    International Nuclear Information System (INIS)

    Naderi, N.; Hashim, M.R.

    2013-01-01

    Highlights: ► Porous-shaped silicon carbide thin film was deposited on porous silicon substrate. ► Thermal annealing was followed to enhance the physical properties of samples. ► Metal–semiconductor-metal ultraviolet detectors were fabricated on samples. ► The effect of annealing temperature on electrical performance of devices was studied. ► The efficiency of photodetectors was enhanced by annealing at elevated temperatures. -- Abstract: A metal–semiconductor-metal (MSM) ultraviolet photodetector was fabricated based on a porous-shaped structure of silicon carbide (SiC). For increasing the surface roughness of SiC and hence enhancing the light absorption effect in fabricated devices, porous silicon (PS) was chosen as a template; SiC was deposited on PS substrates via radio frequency magnetron sputtering. Therefore, the deposited layers followed the structural pattern of PS skeleton and formed a porous-shaped SiC layer on PS substrate. The structural properties of samples showed that the as-deposited SiC was amorphous. Thus, a post-deposition annealing process with elevated temperatures was required to convert its amorphous phase to crystalline phase. The morphology of the sputtered samples was examined via scanning electron and atomic force microscopies. The grain size and roughness of the deposited layers clearly increased upon an increase in the annealing temperature. The optical properties of sputtered SiC were enhanced due to applying high temperatures. The most intense photoluminescence peak was observed for the sample with 1200 °C of annealing temperature. For the metallization of the SiC substrates to fabricate MSM photodetectors, two interdigitated Schottky contacts of Ni with four fingers for each electrode were deposited onto all the porous substrates. The optoelectronic characteristics of MSM UV photodetectors with porous-shaped SiC substrates were studied in the dark and under UV illumination. The electrical characteristics of fabricated

  16. Large volume cryogenic silicon detectors

    Energy Technology Data Exchange (ETDEWEB)

    Braggio, C. [Dipartimento di Fisica, Universita di Padova, via Marzolo 8, 35131 Padova (Italy); Boscardin, M. [Fondazione Bruno Kessler (FBK), via Sommarive 18, I-38100 Povo (Italy); Bressi, G. [INFN sez. di Pavia, via Bassi 6, 27100 Pavia (Italy); Carugno, G.; Corti, D. [INFN sez. di Padova, via Marzolo 8, 35131 Padova (Italy); Galeazzi, G. [INFN lab. naz. Legnaro, viale dell' Universita 2, 35020 Legnaro (Italy); Zorzi, N. [Fondazione Bruno Kessler (FBK), via Sommarive 18, I-38100 Povo (Italy)

    2009-12-15

    We present preliminary measurements for the development of a large volume silicon detector to detect low energy and low rate energy depositions. The tested detector is a one cm-thick silicon PIN diode with an active volume of 31 cm{sup 3}, cooled to the liquid helium temperature to obtain depletion from thermally-generated free carriers. A thorough study has been done to show that effects of charge trapping during drift disappears at a bias field value of the order of 100V/cm.

  17. Nonlinear silicon photonics

    Science.gov (United States)

    Tsia, Kevin K.; Jalali, Bahram

    2010-05-01

    An intriguing optical property of silicon is that it exhibits a large third-order optical nonlinearity, with orders-ofmagnitude larger than that of silica glass in the telecommunication band. This allows efficient nonlinear optical interaction at relatively low power levels in a small footprint. Indeed, we have witnessed a stunning progress in harnessing the Raman and Kerr effects in silicon as the mechanisms for enabling chip-scale optical amplification, lasing, and wavelength conversion - functions that until recently were perceived to be beyond the reach of silicon. With all the continuous efforts developing novel techniques, nonlinear silicon photonics is expected to be able to reach even beyond the prior achievements. Instead of providing a comprehensive overview of this field, this manuscript highlights a number of new branches of nonlinear silicon photonics, which have not been fully recognized in the past. In particular, they are two-photon photovoltaic effect, mid-wave infrared (MWIR) silicon photonics, broadband Raman effects, inverse Raman scattering, and periodically-poled silicon (PePSi). These novel effects and techniques could create a new paradigm for silicon photonics and extend its utility beyond the traditionally anticipated applications.

  18. Report on achievements in fiscal 1999 on research and development of immediately effective and innovative energy environment technology. Part 1. Development of immediately effective and high-efficiency solar cells, and development of technology to slice and manufacture thin-type large-area polycrystalline substrates; 1999 nendo sokkoteki kakushinteki energy kankyo gijutsu kenkyu kaihatsu seika hokokusho. Sokkogata kokoritsu taiyo denchi gijutsu kaihatsu (usugata daimenseki takessho kiban slice seizo gijutsu kaihatsu 1)

    Energy Technology Data Exchange (ETDEWEB)

    NONE

    2000-03-01

    With an objective of decreasing silicon usage quantity for the purpose of reducing the solar cell production cost, development is being performed on an ingot cutting technology to cut a silicon ingot to Kerf loss of 150 {mu} m and thickness of 150 {mu} m, and in which the produced wafers can withstand the cell making. Investigations revealed that a wire saw is suitable as the cutting system, and the wire used must have a diameter of less than 120 {mu} m, and a strength of more than 3850 N/mm{sup 2}. A prototype wire was fabricated, whose diameter is 120 {mu} m, and in which the strength is distributed between 3870 and 4110 N/mm{sup 2}. It was found possible that a wire of 160 {mu} m can be used to slice an ingot having a cross section surface of 150 mm square and a length of 300 mm into a slice having a Kerf loss of 200 {mu} m and a thickness of 180 {mu} m. This wafer had the in-plane distribution of the substrate thickness at {+-} 12.5 {mu}, swell of 120 {mu} at maximum, and surface roughness of 5 {mu}. Making ten of these wafers into a cell resulted in a yield of 60%. Assignments are the clarification of the properties of the cutting wire, the preparation of a thin wire with homogeneous quality, and the establishment of a technology to cut Kerf loss of 150 {mu} and substrate thickness of 150 {mu}. (NEDO)

  19. Tin - an unlikely ally for silicon field effect transistors?

    KAUST Repository

    Hussain, Aftab M.; Fahad, Hossain M.; Singh, Nirpendra; Sevilla, Galo T.; Schwingenschlö gl, Udo; Hussain, Muhammad Mustafa

    2014-01-01

    We explore the effectiveness of tin (Sn), by alloying it with silicon, to use SiSn as a channel material to extend the performance of silicon based complementary metal oxide semiconductors. Our density functional theory based simulation shows

  20. Position-controlled epitaxial III-V nanowires on silicon

    NARCIS (Netherlands)

    Roest, A.L.; Verheijen, M.A.; Wunnicke, O.; Serafin, S.N.; Wondergem, H.J.; Bakkers, E.P.A.M.

    2006-01-01

    We show the epitaxial integration of III-V semiconductor nanowires with silicon technology. The wires are grown by the VLS mechanism with laser ablation as well as metal-organic vapour phase epitaxy. The hetero-epitaxial growth of the III-V nanowires on silicon was confirmed with x-ray diffraction

  1. Liquid phase epitaxial growth of silicon on porous silicon for photovoltaic applications

    International Nuclear Information System (INIS)

    Berger, S.; Quoizola, S.; Fave, A.; Kaminski, A.; Perichon, S.; Barbier, D.; Laugier, A.

    2001-01-01

    The aim of this experiment is to grow a thin silicon layer ( 2 atmosphere, and finally LPE silicon growth with different temperature profiles in order to obtain a silicon layer on the sacrificial porous silicon (p-Si). We observed a pyramidal growth on the surface of the (100) porous silicon but the coalescence was difficult to obtain. However, on a p-Si (111) oriented wafer, homogeneous layers were obtained. (orig.)

  2. Hardness and microstructural characteristics of rapidly solidified Al-8-16 wt.%Si alloys

    International Nuclear Information System (INIS)

    Uzun, O.; Karaaslan, T.; Gogebakan, M.; Keskin, M.

    2004-01-01

    Al-Si alloys with nominal composition of Al-8 wt.%Si, Al-12 wt.%Si, and Al-16 wt.%Si were rapidly solidified by using melt-spinning technique to examine the influence of the cooling rate/conditions on microstructure and mechanical properties. The microstructures of the rapidly solidified ribbons and ingot samples were investigated by the optical microscopy, electron microscopy and X-ray diffraction (XRD) techniques. The results showed that the structures of all melt-spun ribbons were completely composed of finely dispersed α-Al and eutectic Si phase, and primary silicon was not observed. The XRD analysis indicated that the solubility of Si in the α-Al matrix was greatly increased with rapid solidification. Additionally, mechanical properties of both conventionally cast (ingot) and melt-spun ribbons were examined by using Vickers indenter for one applied load (0.098 N). The hardness values of the melt-spun ribbons were about three times higher than those of ingot counterparts. The high hardness of the rapidly solidified state can be attributed to the supersaturated solid solutions. Besides, hardness values with different applied loads were measured for melt-spun ribbons. The results indicated that Vickers hardness values (H v ) of the ribbons depended on the applied load. Applying the concept of Hays-Kendall, the load independent hardness values were calculated as 694.0, 982.8 and 1186.8 MN/m 2 for Al-8 wt.%Si, Al-12 wt.%Si and Al-16 wt.%Si, respectively

  3. Attenuation of Thermal Neutrons by Crystalline Silicon

    International Nuclear Information System (INIS)

    Adib, M.; Habib, N.; Ashry, A.; Fathalla, M.

    2002-01-01

    A simple formula is given which allows to calculate the contribution of the total neutron cross - section including the Bragg scattering from different (hkt) planes to the neutron * transmission through a solid crystalline silicon. The formula takes into account the silicon form of poly or mono crystals and its parameters. A computer program DSIC was developed to provide the required calculations. The calculated values of the total neutron cross-section of perfect silicon crystal at room and liquid nitrogen temperatures were compared with the experimental ones. The obtained agreement shows that the simple formula fits the experimental data with sufficient accuracy .A good agreement was also obtained between the calculated and measured values of polycrystalline silicon in the energy range from 5 eV to 500μ eV. The feasibility study on using a poly-crystalline silicon as a cold neutron filter and mono-crystalline as a thermal neutron one is given. The optimum crystal thickness, mosaic spread, temperature and cutting plane for efficiently transmitting the thermal reactor neutrons, while rejecting both fast neutrons and gamma rays accompanying the thermal ones for the mono crystalline silicon are also given

  4. Superhydrophobic SERS substrates based on silicon hierarchical nanostructures

    Science.gov (United States)

    Chen, Xuexian; Wen, Jinxiu; Zhou, Jianhua; Zheng, Zebo; An, Di; Wang, Hao; Xie, Weiguang; Zhan, Runze; Xu, Ningsheng; Chen, Jun; She, Juncong; Chen, Huanjun; Deng, Shaozhi

    2018-02-01

    Silicon nanostructures have been cultivated as promising surface enhanced Raman scattering (SERS) substrates in terms of their low-loss optical resonance modes, facile functionalization, and compatibility with today’s state-of-the-art CMOS techniques. However, unlike their plasmonic counterparts, the electromagnetic field enhancements induced by silicon nanostructures are relatively small, which restrict their SERS sensing limit to around 10-7 M. To tackle this problem, we propose here a strategy for improving the SERS performance of silicon nanostructures by constructing silicon hierarchical nanostructures with a superhydrophobic surface. The hierarchical nanostructures are binary structures consisted of silicon nanowires (NWs) grown on micropyramids (MPs). After being modified with perfluorooctyltriethoxysilane (PFOT), the nanostructure surface shows a stable superhydrophobicity with a high contact angle of ˜160°. The substrate can allow for concentrating diluted analyte solutions into a specific area during the evaporation of the liquid droplet, whereby the analytes are aggregated into a small volume and can be easily detected by the silicon nanostructure SERS substrate. The analyte molecules (methylene blue: MB) enriched from an aqueous solution lower than 10-8 M can be readily detected. Such a detection limit is ˜100-fold lower than the conventional SERS substrates made of silicon nanostructures. Additionally, the detection limit can be further improved by functionalizing gold nanoparticles onto silicon hierarchical nanostructures, whereby the superhydrophobic characteristics and plasmonic field enhancements can be combined synergistically to give a detection limit down to ˜10-11 M. A gold nanoparticle-functionalized superhydrophobic substrate was employed to detect the spiked melamine in liquid milk. The results showed that the detection limit can be as low as 10-5 M, highlighting the potential of the proposed superhydrophobic SERS substrate in

  5. Pseudo-direct bandgap transitions in silicon nanocrystals: effects on optoelectronics and thermoelectrics

    Science.gov (United States)

    Singh, Vivek; Yu, Yixuan; Sun, Qi-C.; Korgel, Brian; Nagpal, Prashant

    2014-11-01

    While silicon nanostructures are extensively used in electronics, the indirect bandgap of silicon poses challenges for optoelectronic applications like photovoltaics and light emitting diodes (LEDs). Here, we show that size-dependent pseudo-direct bandgap transitions in silicon nanocrystals dominate the interactions between (photoexcited) charge carriers and phonons, and hence the optoelectronic properties of silicon nanocrystals. Direct measurements of the electronic density of states (DOS) for different sized silicon nanocrystals reveal that these pseudo-direct transitions, likely arising from the nanocrystal surface, can couple with the quantum-confined silicon states. Moreover, we demonstrate that since these transitions determine the interactions of charge carriers with phonons, they change the light emission, absorption, charge carrier diffusion and phonon drag (Seebeck coefficient) in nanoscaled silicon semiconductors. Therefore, these results can have important implications for the design of optoelectronics and thermoelectric devices based on nanostructured silicon.While silicon nanostructures are extensively used in electronics, the indirect bandgap of silicon poses challenges for optoelectronic applications like photovoltaics and light emitting diodes (LEDs). Here, we show that size-dependent pseudo-direct bandgap transitions in silicon nanocrystals dominate the interactions between (photoexcited) charge carriers and phonons, and hence the optoelectronic properties of silicon nanocrystals. Direct measurements of the electronic density of states (DOS) for different sized silicon nanocrystals reveal that these pseudo-direct transitions, likely arising from the nanocrystal surface, can couple with the quantum-confined silicon states. Moreover, we demonstrate that since these transitions determine the interactions of charge carriers with phonons, they change the light emission, absorption, charge carrier diffusion and phonon drag (Seebeck coefficient) in

  6. Silicon nitride and intrinsic amorphous silicon double antireflection coatings for thin-film solar cells on foreign substrates

    International Nuclear Information System (INIS)

    Li, Da; Kunz, Thomas; Wolf, Nadine; Liebig, Jan Philipp; Wittmann, Stephan; Ahmad, Taimoor; Hessmann, Maik T.; Auer, Richard; Göken, Mathias; Brabec, Christoph J.

    2015-01-01

    Hydrogenated intrinsic amorphous silicon (a-Si:H) was investigated as a surface passivation method for crystalline silicon thin film solar cells on graphite substrates. The results of the experiments, including quantum efficiency and current density-voltage measurements, show improvements in cell performance. This improvement is due to surface passivation by an a-Si:H(i) layer, which increases the open circuit voltage and the fill factor. In comparison with our previous work, we have achieved an increase of 0.6% absolute cell efficiency for a 40 μm thick 4 cm 2 aperture area on the graphite substrate. The optical properties of the SiN x /a-Si:H(i) stack were studied using spectroscopic ellipsometer techniques. Scanning transmission electron microscopy inside a scanning electron microscope was applied to characterize the cross section of the SiN x /a-Si:H(i) stack using focus ion beam preparation. - Highlights: • We report a 10.8% efficiency for thin-film silicon solar cell on graphite. • Hydrogenated intrinsic amorphous silicon was applied for surface passivation. • SiN x /a-Si:H(i) stacks were characterized by spectroscopic ellipsometer techniques. • Cross-section micrograph was obtained by scanning transmission electron microscopy. • Quantum efficiency and J-V measurements show improvements in the cell performance

  7. Instrumental studies on silicone oil adsorption to the surface of intraocular lenses

    Energy Technology Data Exchange (ETDEWEB)

    Kim, Chun Ho [Lab. of Tissue Engineering, Korea Institute of Radiological and Medical Sciences, Seoul 139-706 (Korea, Republic of); Joo, Choun-Ki [Department of Ophthalmology and Visual Science, Medical College of Catholic University, Seoul 137-701 (Korea, Republic of); Chun, Heung Jae, E-mail: chunhj@catholic.ac.kr [Institute of Cell and Tissue Engineering, Medical College of Catholic University, Seoul 137-701 (Korea, Republic of); Yoo, Bok Ryul [Organosilicone Chemistry Laboratory, Korea Institute of Science and Technology, Seoul 130-650 (Korea, Republic of); Noh, Dong Il; Shim, Young Bock [Research Institute of Biomedical Engineering, Korea Bone Bank Co. Ltd., Seoul 153-782 (Korea, Republic of)

    2012-12-01

    Highlights: Black-Right-Pointing-Pointer It was found that PHEMA and Acrysof IOLs possess silicone oil repellant ability. Black-Right-Pointing-Pointer The residual silicone oil was detected on the surfaces of PMMA and silicone IOLs. Black-Right-Pointing-Pointer XPS studies showed that silicone oil coverage of PMMA lenses was 12%. Black-Right-Pointing-Pointer Silicone oil covered the entire surface of the silicone IOLs. - Abstract: The purpose of this study was to examine the degree of adherence of silicone oil to various intraocular lenses (IOLs) through comparison of the physico-chemical properties of the oil and IOLs. Four kinds of IOLs comprising various biomaterials were examined: PMMA (720A Trade-Mark-Sign ), PHEMA (IOGEL 1103 Trade-Mark-Sign ), Acrysof (MA60BM Trade-Mark-Sign ), and silicone (SI30NB Trade-Mark-Sign ). Each lens was immersed in silicone oil or carboxylated silicone (CS-PDMS) oil for 72 h. For determination of the changes in chemical and elemental compositions on the surfaces of IOLs caused by the contact with silicone oil, IOLs were washed and rinsed with n-pentane to remove as much of the adsorbed silicone oil as possible, then subjected to Fourier transform infrared spectroscopic (FTIR) and X-ray photoelectron spectroscopic (XPS) analyses. The results of FTIR studies strongly indicate that washing with n-pentane completely removed the adhered silicone oil on the surfaces of PHEMA and Acrysof IOLs, whereas the residual silicone oil was detected on the surfaces of PMMA and silicone IOLs. XPS studies showed that silicone oil coverage of PMMA lenses was 12%, even after washing with n-pentane. In the case of silicone IOLs, the relative O1s peak area of carboxyl group in the residual CS-PDMS oil was found to be {approx}2.7%. Considering that 2.8% carboxyl group-substituted silicone oil was used in the present study, CS-PDMS oil covered the entire surface of the silicone IOLs.

  8. Ultrafast Silicon Photonics with Visible to Mid-Infrared Pumping of Silicon Nanocrystals.

    Science.gov (United States)

    Diroll, Benjamin T; Schramke, Katelyn S; Guo, Peijun; Kortshagen, Uwe R; Schaller, Richard D

    2017-10-11

    Dynamic optical control of infrared (IR) transparency and refractive index is achieved using boron-doped silicon nanocrystals excited with mid-IR optical pulses. Unlike previous silicon-based optical switches, large changes in transmittance are achieved without a fabricated structure by exploiting strong light coupling of the localized surface plasmon resonance (LSPR) produced from free holes of p-type silicon nanocrystals. The choice of optical excitation wavelength allows for selectivity between hole heating and carrier generation through intraband or interband photoexcitation, respectively. Mid-IR optical pumping heats the free holes of p-Si nanocrystals to effective temperatures greater than 3500 K. Increases of the hole effective mass at high effective hole temperatures lead to a subpicosecond change of the dielectric function, resulting in a redshift of the LSPR, modulating mid-IR transmission by as much as 27%, and increasing the index of refraction by more than 0.1 in the mid-IR. Low hole heat capacity dictates subpicosecond hole cooling, substantially faster than carrier recombination, and negligible heating of the Si lattice, permitting mid-IR optical switching at terahertz repetition frequencies. Further, the energetic distribution of holes at high effective temperatures partially reverses the Burstein-Moss effect, permitting the modulation of transmittance at telecommunications wavelengths. The results presented here show that doped silicon, particularly in micro- or nanostructures, is a promising dynamic metamaterial for ultrafast IR photonics.

  9. Ionizing Energy Depositions After Fast Neutron Interactions in Silicon

    CERN Document Server

    Bergmann, Benedikt; Caicedo, Ivan; Kierstead, James; Takai, Helio; Frojdh, Erik

    2016-01-01

    In this study we present the ionizing energy depositions in a 300 μm thick silicon layer after fast neutron impact. With the Time-of-Flight (ToF) technique, the ionizing energy deposition spectra of recoil silicons and secondary charged particles were assigned to (quasi-)monoenergetic neutron energies in the range from 180 keV to hundreds of MeV. We show and interpret representative measured energy spectra. By separating the ionizing energy losses of the recoil silicon from energy depositions by products of nuclear reactions, the competition of ionizing (IEL) and non-ionizing energy losses (NIEL) of a recoil silicon within the silicon lattice was investigated. The data give supplementary information to the results of a previous measurement and are compared with different theoretical predictions.

  10. Photoconductivity relaxation and electron transport in macroporous silicon structures

    Directory of Open Access Journals (Sweden)

    L.A. Karachevtseva

    2017-12-01

    Full Text Available Kinetics and temperature dependence of photoconductivity were measured in macroporous silicon at 80…300 K after light illumination with the wavelength 0.9 μm. The influence of mechanisms of the charge carrier transport through the macropore surface barrier on the kinetics of photoconductivity at various temperatures was investigated. The kinetics of photoconductivity distribution in macroporous silicon and Si substrate has been calculated using the finite-difference time-domain method. The maximum of photoconductivity has been found both in the layer of macroporous silicon and in the monocrystalline substrate. The kinetics of photoconductivity distribution in macroporous silicon showed rapid relaxation of the photoconductivity maximum in the layer of macroporous silicon and slow relaxation of it in the monocrystalline substrate.

  11. Analysis of IV characteristics of solar cells made of hydrogenated amorphous, polymorphous and microcrystalline silicon

    International Nuclear Information System (INIS)

    Hamadeh, H.

    2009-03-01

    The IV characteristics of pin solar cells made of amorphous, polymorphous and microcrystalline silicon were investigated. The temperature dependence was measured in the temperature range between 150 K and 395 K. This range covers the most terrestrial applications condition. Using simplex procedure, the IV parameter of the cells were deduce using line fitting. It has been shown that polymorphous silicon shows electrical properties that are close to properties of microcrystalline silicon but as it is well known, polymorphous silicon shows higher absorption similar to amorphous silicon. The polymorphous silicon solar cells showed higher efficiencies, lower shunting and higher filling factors. In the above mentioned temperature range, polymorphous silicon is the better material for the manufacturing of thin film hydrogenated silicon pin solar cells. More investigations concerning the structural properties are necessary to make stronger conclusions in regards to the stability of the material, what we hope to do in the future. (author)

  12. Tin - an unlikely ally for silicon field effect transistors?

    KAUST Repository

    Hussain, Aftab M.

    2014-01-13

    We explore the effectiveness of tin (Sn), by alloying it with silicon, to use SiSn as a channel material to extend the performance of silicon based complementary metal oxide semiconductors. Our density functional theory based simulation shows that incorporation of tin reduces the band gap of Si(Sn). We fabricated our device with SiSn channel material using a low cost and scalable thermal diffusion process of tin into silicon. Our high-κ/metal gate based multi-gate-field-effect-transistors using SiSn as channel material show performance enhancement, which is in accordance with the theoretical analysis. © 2014 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

  13. Nonlinear silicon photonics

    Science.gov (United States)

    Borghi, M.; Castellan, C.; Signorini, S.; Trenti, A.; Pavesi, L.

    2017-09-01

    Silicon photonics is a technology based on fabricating integrated optical circuits by using the same paradigms as the dominant electronics industry. After twenty years of fervid development, silicon photonics is entering the market with low cost, high performance and mass-manufacturable optical devices. Until now, most silicon photonic devices have been based on linear optical effects, despite the many phenomenologies associated with nonlinear optics in both bulk materials and integrated waveguides. Silicon and silicon-based materials have strong optical nonlinearities which are enhanced in integrated devices by the small cross-section of the high-index contrast silicon waveguides or photonic crystals. Here the photons are made to strongly interact with the medium where they propagate. This is the central argument of nonlinear silicon photonics. It is the aim of this review to describe the state-of-the-art in the field. Starting from the basic nonlinearities in a silicon waveguide or in optical resonator geometries, many phenomena and applications are described—including frequency generation, frequency conversion, frequency-comb generation, supercontinuum generation, soliton formation, temporal imaging and time lensing, Raman lasing, and comb spectroscopy. Emerging quantum photonics applications, such as entangled photon sources, heralded single-photon sources and integrated quantum photonic circuits are also addressed at the end of this review.

  14. Mechanical Properties of Photovoltaic Silicon in Relation to Wafer Breakage

    Science.gov (United States)

    Kulshreshtha, Prashant Kumar

    This thesis focuses on the fundamental understanding of stress-modified crack-propagation in photovoltaic (PV) silicon in relation to the critical issue of PV silicon "wafer breakage". The interactions between a propagating crack and impurities/defects/residual stresses have been evaluated for consequential fracture path in a thin PV Si wafer. To investigate the mechanism of brittle fracture in silicon, the phase transformations induced by elastic energy released at a propagating crack-tip have been evaluated by locally stressing the diamond cubic Si lattice using a rigid Berkovich nanoindenter tip (radius ≈50 nm). Unique pressure induced phase transformations and hardness variations have been then related to the distribution of precipitates (O, Cu, Fe etc.), and the local stresses in the wafer. This research demonstrates for the first time the "ductile-like fracture" in almost circular crack path that significantly deviates from its energetically favorable crystallographic [110](111) system. These large diameter (≈ 200 mm) Si wafers were sliced to less than 180 microm thickness from a Czochralski (CZ) ingot that was grown at faster than normal growth rates. The vacancy (vSi) driven precipitation of oxygen at enhanced thermal gradients in the wafer core develops large localized stresses (upto 100 MPa) which we evaluated using Raman spectral analysis. Additional micro-FTIR mapping and microscopic etch pit measurements in the wafer core have related the observed crack path deviations to the presence of concentric ring-like distributions of oxygen precipitates (OPs). To replicate these "real-world" breakage scenarios and provide better insight on crack-propagation, several new and innovative tools/devices/methods have been developed in this study. An accurate quantitative profiling of local stress, phase changes and load-carrying ability of Si lattice has been performed in the vicinity of the controlled micro-cracks created using micro-indentations to represent

  15. Silicon Microspheres Photonics

    International Nuclear Information System (INIS)

    Serpenguzel, A.

    2008-01-01

    Electrophotonic integrated circuits (EPICs), or alternatively, optoelectronic integrated circuit (OEICs) are the natural evolution of the microelectronic integrated circuit (IC) with the addition of photonic capabilities. Traditionally, the IC industry has been based on group IV silicon, whereas the photonics industry on group III-V semiconductors. However, silicon based photonic microdevices have been making strands in siliconizing photonics. Silicon microspheres with their high quality factor whispering gallery modes (WGMs), are ideal candidates for wavelength division multiplexing (WDM) applications in the standard near-infrared communication bands. In this work, we will discuss the possibility of using silicon microspheres for photonics applications in the near-infrared

  16. Excellent Silicon Surface Passivation Achieved by Industrial Inductively Coupled Plasma Deposited Hydrogenated Intrinsic Amorphous Silicon Suboxide

    Directory of Open Access Journals (Sweden)

    Jia Ge

    2014-01-01

    Full Text Available We present an alternative method of depositing a high-quality passivation film for heterojunction silicon wafer solar cells, in this paper. The deposition of hydrogenated intrinsic amorphous silicon suboxide is accomplished by decomposing hydrogen, silane, and carbon dioxide in an industrial remote inductively coupled plasma platform. Through the investigation on CO2 partial pressure and process temperature, excellent surface passivation quality and optical properties are achieved. It is found that the hydrogen content in the film is much higher than what is commonly reported in intrinsic amorphous silicon due to oxygen incorporation. The observed slow depletion of hydrogen with increasing temperature greatly enhances its process window as well. The effective lifetime of symmetrically passivated samples under the optimal condition exceeds 4.7 ms on planar n-type Czochralski silicon wafers with a resistivity of 1 Ωcm, which is equivalent to an effective surface recombination velocity of less than 1.7 cms−1 and an implied open-circuit voltage (Voc of 741 mV. A comparison with several high quality passivation schemes for solar cells reveals that the developed inductively coupled plasma deposited films show excellent passivation quality. The excellent optical property and resistance to degradation make it an excellent substitute for industrial heterojunction silicon solar cell production.

  17. Radiation modification of silicone rubber with glycidylmethacrylate

    International Nuclear Information System (INIS)

    Segura, Tania; Burillo, Guillermina

    2013-01-01

    The grafting of glycidilmethacrylate(GMA) was grafted onto silicone rubber (SR) by using the γ-ray pre-irradiation grafting method under different conditions. The effect of reaction time, total dose, reaction temperature and monomer concentration on the graft yield was studied. It was found that the degree of grafting can be controlled by adjusting these parameters. The chemical structure of SR before and after grafting was characterized using FTIR-ATR and SEM–EDS. The analysis revealed that the surface of the SR was uniformly covered by GMA and the cross-section analysis indicated that the grafting occurred in the bulk. Thermogravimetric analysis (TGA) showed that the graft copolymer was more thermally stable than polyglycidylmethacrylate but less stable than SR, and the DSC confirmed that the GMA was grafting onto silicone rubber. - Highlights: • A graft copolymer with silicone rubber was synthesized by gamma pre-irradiation method. • SEM–EDS analysis showed that the surface and the bulk of the new copolymer were grafted. • The thermal properties of the silicone rubber used were modified with grafting. • The new copolymer could be used to immobilize nucleophilic biomolecules

  18. DC characteristics and parameters of silicon carbide high-voltage power BJTs

    International Nuclear Information System (INIS)

    Patrzyk, Joanna; Zarębski, Janusz; Bisewski, Damian

    2016-01-01

    The paper shows the static characteristics and operating parameters of the bipolar power transistors made of silicon carbide and for comparison their equivalents made of classical silicon technology. The characteristics and values of selected operating parameters with special emphasis on the effect of temperature and operating point of considered devices are discussed. Quantitative as well as qualitative differences between the characteristics of the transistor made of silicon and silicon carbide are indicated as well

  19. Thin silicon foils produced by epoxy-induced spalling of silicon for high efficiency solar cells

    Energy Technology Data Exchange (ETDEWEB)

    Martini, R., E-mail: roberto.martini@imec.be [Department of Electrical Engineering, KU Leuven, Kasteelpark 10, 3001 Leuven (Belgium); imec, Kapeldreef 75, 3001 Leuven (Belgium); Kepa, J.; Stesmans, A. [Department of Physics, KU Leuven, Celestijnenlaan 200 D, 3001 Leuven (Belgium); Debucquoy, M.; Depauw, V.; Gonzalez, M.; Gordon, I. [imec, Kapeldreef 75, 3001 Leuven (Belgium); Poortmans, J. [Department of Electrical Engineering, KU Leuven, Kasteelpark 10, 3001 Leuven (Belgium); imec, Kapeldreef 75, 3001 Leuven (Belgium); Universiteit Hasselt, Martelarenlaan 42, B-3500 Hasselt (Belgium)

    2014-10-27

    We report on the drastic improvement of the quality of thin silicon foils produced by epoxy-induced spalling. In the past, researchers have proposed to fabricate silicon foils by spalling silicon substrates with different stress-inducing materials to manufacture thin silicon solar cells. However, the reported values of effective minority carrier lifetime of the fabricated foils remained always limited to ∼100 μs or below. In this work, we investigate epoxy-induced exfoliated foils by electron spin resonance to analyze the limiting factors of the minority carrier lifetime. These measurements highlight the presence of disordered dangling bonds and dislocation-like defects generated by the exfoliation process. A solution to remove these defects compatible with the process flow to fabricate solar cells is proposed. After etching off less than 1 μm of material, the lifetime of the foil increases by more than a factor of 4.5, reaching a value of 461 μs. This corresponds to a lower limit of the diffusion length of more than 7 times the foil thickness. Regions with different lifetime correlate well with the roughness of the crack surface which suggests that the lifetime is now limited by the quality of the passivation of rough surfaces. The reported values of the minority carrier lifetime show a potential for high efficiency (>22%) thin silicon solar cells.

  20. Thin silicon foils produced by epoxy-induced spalling of silicon for high efficiency solar cells

    International Nuclear Information System (INIS)

    Martini, R.; Kepa, J.; Stesmans, A.; Debucquoy, M.; Depauw, V.; Gonzalez, M.; Gordon, I.; Poortmans, J.

    2014-01-01

    We report on the drastic improvement of the quality of thin silicon foils produced by epoxy-induced spalling. In the past, researchers have proposed to fabricate silicon foils by spalling silicon substrates with different stress-inducing materials to manufacture thin silicon solar cells. However, the reported values of effective minority carrier lifetime of the fabricated foils remained always limited to ∼100 μs or below. In this work, we investigate epoxy-induced exfoliated foils by electron spin resonance to analyze the limiting factors of the minority carrier lifetime. These measurements highlight the presence of disordered dangling bonds and dislocation-like defects generated by the exfoliation process. A solution to remove these defects compatible with the process flow to fabricate solar cells is proposed. After etching off less than 1 μm of material, the lifetime of the foil increases by more than a factor of 4.5, reaching a value of 461 μs. This corresponds to a lower limit of the diffusion length of more than 7 times the foil thickness. Regions with different lifetime correlate well with the roughness of the crack surface which suggests that the lifetime is now limited by the quality of the passivation of rough surfaces. The reported values of the minority carrier lifetime show a potential for high efficiency (>22%) thin silicon solar cells.

  1. Production of technical silicon and silicon carbide from rice-husk

    Directory of Open Access Journals (Sweden)

    A. Z. Issagulov

    2014-10-01

    Full Text Available In the article there are studied physical and chemical properties of silicon-carbonic raw material – rice-husk, thermophysical characteristics of the process of rice-husk pyrolysis in nonreactive and oxidizing environment; structure and phase composition of products of the rice-husk pyrolysis in interval of temperatures 150 – 850 °С and high temperature pyrolysis in interval of temperatures 900 – 1 500 °С. There are defined the silicon-carbon production conditions, which meet the requirements applicable to charging materials at production of technical silicon and silicon carbide.

  2. Photovoltaic characteristics of porous silicon /(n+ - p) silicon solar cells

    International Nuclear Information System (INIS)

    Dzhafarov, T.D.; Aslanov, S.S.; Ragimov, S.H.; Sadigov, M.S.; Nabiyeva, A.F.; Yuksel, Aydin S.

    2012-01-01

    Full text : The purpose of this work is to improve the photovoltaic parameters of the screen-printed silicon solar cells by formation the nano-porous silicon film on the frontal surface of the cell. The photovoltaic characteristics of two type silicon solar cells with and without porous silicon layer were measured and compared. A remarkable increment of short-circuit current density and the efficiency by 48 percent and 20 percent, respectively, have been achieved for PS/(n + - pSi) solar cell comparing to (n + - p)Si solar cell without PS layer

  3. Detection of carbon dioxide in the gases evolved during the hot extraction determination of hydrogen in uranium ingots

    International Nuclear Information System (INIS)

    Jursik, M.L.; Pope, J.D.

    1977-08-01

    The hot extraction method was used at the National Lead Company of Ohio to determine hydrogen in uranium metal at the 2 ppM level. The volume of gas evolved from the heated sample was assumed to be hydrogen. When a liquid nitrogen trap was placed into the system the hydrogen values were reduced 5 to 10%. The gas retained by the nitrogen trap was identified by mass spectrometry as predominantly carbon dioxide. Low hydrogen values were observed only when the nitrogen trap was used in the analysis of high-carbon (300 to 600 ppM) uranium from NLO production ingots. However, hydrogen values for low-carbon (30 to 50 ppM) uranium were unaffected by the nitrogen trap. The formation of carbon dioxide appears to be associated with the carbon content of the uranium metal. Comparisons of hydrogen values obtained with the hot extraction method and with an inert fusion--thermal conductivity method are also presented. 3 tables, 4 figures

  4. Nanoscale semiconducting silicon as a nutritional food additive

    Energy Technology Data Exchange (ETDEWEB)

    Canham, L T [pSiNutria Ltd, Malvern Hills Science Park, Geraldine Road, Malvern, Worcestershire WR14 3SZ (United Kingdom)

    2007-05-09

    Very high surface area silicon powders can be realized by high energy milling or electrochemical etching techniques. Such nanoscale silicon structures, whilst biodegradable in the human gastrointestinal tract, are shown to be remarkably stable in most foodstuffs and beverages. The potential for using silicon to improve the shelf life and bioavailability of specific nutrients in functional foods is highlighted. Published drug delivery data implies that the nanoentrapment of hydrophobic nutrients will significantly improve their dissolution kinetics, through a combined effect of nanostructuring and solid state modification. Nutrients loaded to date include vitamins, fish oils, lycopene and coenzyme Q10. In addition, there is growing published evidence that optimized release of orthosilicic acid, the biodegradation product of semiconducting silicon in the gut, offers beneficial effects with regard bone health. The utility of nanoscale silicon in the nutritional field shows early promise and is worthy of much further study.

  5. Nanoscale semiconducting silicon as a nutritional food additive

    International Nuclear Information System (INIS)

    Canham, L T

    2007-01-01

    Very high surface area silicon powders can be realized by high energy milling or electrochemical etching techniques. Such nanoscale silicon structures, whilst biodegradable in the human gastrointestinal tract, are shown to be remarkably stable in most foodstuffs and beverages. The potential for using silicon to improve the shelf life and bioavailability of specific nutrients in functional foods is highlighted. Published drug delivery data implies that the nanoentrapment of hydrophobic nutrients will significantly improve their dissolution kinetics, through a combined effect of nanostructuring and solid state modification. Nutrients loaded to date include vitamins, fish oils, lycopene and coenzyme Q10. In addition, there is growing published evidence that optimized release of orthosilicic acid, the biodegradation product of semiconducting silicon in the gut, offers beneficial effects with regard bone health. The utility of nanoscale silicon in the nutritional field shows early promise and is worthy of much further study

  6. Heterogeneous silicon mesostructures for lipid-supported bioelectric interfaces

    Energy Technology Data Exchange (ETDEWEB)

    Jiang, Yuanwen; Carvalho-de-Souza, João L.; Wong, Raymond C. S.; Luo, Zhiqiang; Isheim, Dieter; Zuo, Xiaobing; Nicholls, Alan W.; Jung, Il Woong; Yue, Jiping; Liu, Di-Jia; Wang, Yucai; De Andrade, Vincent; Xiao, Xianghui; Navrazhnykh, Luizetta; Weiss, Dara E.; Wu, Xiaoyang; Seidman, David N.; Bezanilla, Francisco; Tian, Bozhi

    2016-06-27

    Silicon-based materials have widespread application as biophysical tools and biomedical devices. Here we introduce a biocompatible and degradable mesostructured form of silicon with multi-scale structural and chemical heterogeneities. The material was synthesized using mesoporous silica as a template through a chemical vapour deposition process. It has an amorphous atomic structure, an ordered nanowire-based framework and random submicrometre voids, and shows an average Young’s modulus that is 2–3 orders of magnitude smaller than that of single-crystalline silicon. In addition, we used the heterogeneous silicon mesostructures to design a lipid-bilayer-supported bioelectric interface that is remotely controlled and temporally transient, and that permits non-genetic and subcellular optical modulation of the electrophysiology dynamics in single dorsal root ganglia neurons. Our findings suggest that the biomimetic expansion of silicon into heterogeneous and deformable forms can open up opportunities in extracellular biomaterial or bioelectric systems.

  7. Performance improvement of silicon solar cells by nanoporous silicon coating

    Directory of Open Access Journals (Sweden)

    Dzhafarov T. D.

    2012-04-01

    Full Text Available In the present paper the method is shown to improve the photovoltaic parameters of screen-printed silicon solar cells by nanoporous silicon film formation on the frontal surface of the cell using the electrochemical etching. The possible mechanisms responsible for observed improvement of silicon solar cell performance are discussed.

  8. Synthesis of silicon nanowires and novel nano-dendrite structures

    International Nuclear Information System (INIS)

    Sinha, Saion; Gao Bo; Zhou, Otto

    2004-01-01

    We report a study on the effects of various parameters on the synthesis of silicon nanowires (5--50 nm in diameter) by pulsed laser ablation. A novel silicon nanodendrite structure is observed by changing some of the growth parameters abruptly. This growth mechanism is explained by a qualitative model. These nanodendrites show a promise of being used as a template in fabricating nanocircuits. Thermal quantum confinement effects were also observed on the silicon nanowires and have been reported

  9. Electroless siliconizing Fe-3% Cr-3% Si alloy

    International Nuclear Information System (INIS)

    Nurlina, Enung; Darmono, Budy; Purwadaria, Sunara

    2000-01-01

    In this research Fe-3%Cr-3%Mo-3%Si and Fe-3%Cr-3%Cu-3%Si alloys had been coated by silicon metal without electricity current which knows as electroless siliconizing. Coating was conducted by immersed sampler into melt fluoride-chloride salt bath at temperature of 750 o C for certain period. The layer consisted of Fe3Si phase. Observation by microscope optic and EDAX showed that the silicide layer were thick enough, adherent, free for crack and had silicon content on the surface more than 15%. The growth rate of silicide layer followed parabolic rate law, where the process predominantly controlled by interdiffusion rate in the solid phase. Key words : electroless siliconizing, the melt fluoride- chloride salt mix, silicide layer

  10. Effect of Silicon in U-10Mo Alloy

    Energy Technology Data Exchange (ETDEWEB)

    Kautz, Elizabeth J. [Pacific Northwest National Lab. (PNNL), Richland, WA (United States); Devaraj, Arun [Pacific Northwest National Lab. (PNNL), Richland, WA (United States); Kovarik, Libor [Pacific Northwest National Lab. (PNNL), Richland, WA (United States); Lavender, Curt A. [Pacific Northwest National Lab. (PNNL), Richland, WA (United States); Joshi, Vineet V. [Pacific Northwest National Lab. (PNNL), Richland, WA (United States)

    2017-08-31

    This document details a method for evaluating the effect of silicon impurity content on U-10Mo alloys. Silicon concentration in U-10Mo alloys has been shown to impact the following: volume fraction of precipitate phases, effective density of the final alloy, and 235-U enrichment in the gamma-UMo matrix. This report presents a model for calculating these quantities as a function of Silicon concentration, which along with fuel foil characterization data, will serve as a reference for quality control of the U-10Mo final alloy Si content. Additionally, detailed characterization using scanning electron microscope imaging, transmission electron microscope diffraction, and atom probe tomography showed that Silicon impurities present in U-10Mo alloys form a Si-rich precipitate phase.

  11. Light-Induced Degradation of Thin Film Silicon Solar Cells

    International Nuclear Information System (INIS)

    Hamelmann, F U; Weicht, J A; Behrens, G

    2016-01-01

    Silicon-wafer based solar cells are still domination the market for photovoltaic energy conversion. However, most of the silicon is used only for mechanical stability, while only a small percentage of the material is needed for the light absorption. Thin film silicon technology reduces the material demand to just some hundred nanometer thickness. But even in a tandem stack (amorphous and microcrystalline silicon) the efficiencies are lower, and light-induced degradation is an important issue. The established standard tests for characterisation are not precise enough to predict the performance of thin film silicon solar cells under real conditions, since many factors do have an influence on the degradation. We will show some results of laboratory and outdoor measurements that we are going to use as a base for advanced modelling and simulation methods. (paper)

  12. Release of low molecular weight silicones and platinum from silicone breast implants.

    Science.gov (United States)

    Lykissa, E D; Kala, S V; Hurley, J B; Lebovitz, R M

    1997-12-01

    We have conducted a series of studies addressing the chemical composition of silicone gels from breast implants as well as the diffusion of low molecular weight silicones (LM-silicones) and heavy metals from intact implants into various surrounding media, namely, lipid-rich medium (soy oil), aqueous tissue culture medium (modified Dulbecco's medium, DMEM), or an emulsion consisting of DMEM plus 10% soy oil. LM-silicones in both implants and surrounding media were detected and quantitated using gas chromatography (GC) coupled with atomic emission (GC-AED) as well as mass spectrometric (GC/MS) detectors, which can detect silicones in the nanogram range. Platinum, a catalyst used in the preparation of silicone gels, was detected and quantitated using inductive argon-coupled plasma/mass spectrometry (ICP-MS), which can detect platinum in the parts per trillion range. Our results indicate that GC-detectable low molecular weight silicones contribute approximately 1-2% to the total gel mass and consist predominantly of cyclic and linear poly-(dimethylsiloxanes) ranging from 3 to 20 siloxane [(CH3)2-Si-O] units (molecular weight 200-1500). Platinum can be detected in implant gels at levels of approximately 700 micrograms/kg by ICP-MS. The major component of implant gels appears to be high molecular weight silicone polymers (HM-silicones) too large to be detected by GC. However, these HM-silicones can be converted almost quantitatively (80% by mass) to LM-silicones by heating implant gels at 150-180 degrees C for several hours. We also studied the rates at which LM-silicones and platinum leak through the intact implant outer shell into the surrounding media under a variety of conditions. Leakage of silicones was greatest when the surrounding medium was lipid-rich, and up to 10 mg/day LM-silicones was observed to diffuse into a lipid-rich medium per 250 g of implant at 37 degrees C. This rate of leakage was maintained over a 7-day experimental period. Similarly, platinum was

  13. Intravitreal properties of porous silicon photonic crystals

    Science.gov (United States)

    Cheng, L; Anglin, E; Cunin, F; Kim, D; Sailor, M J; Falkenstein, I; Tammewar, A; Freeman, W R

    2009-01-01

    Aim To determine the suitability of porous silicon photonic crystals for intraocular drug-delivery. Methods A rugate structure was electrochemically etched into a highly doped p-type silicon substrate to create a porous silicon film that was subsequently removed and ultrasonically fractured into particles. To stabilise the particles in aqueous media, the silicon particles were modified by surface alkylation (using thermal hydrosilylation) or by thermal oxidation. Unmodified particles, hydrosilylated particles and oxidised particles were injected into rabbit vitreous. The stability and toxicity of each type of particle were studied by indirect ophthalmoscopy, biomicroscopy, tonometry, electroretinography (ERG) and histology. Results No toxicity was observed with any type of the particles during a period of >4 months. Surface alkylation led to dramatically increased intravitreal stability and slow degradation. The estimated vitreous half-life increased from 1 week (fresh particles) to 5 weeks (oxidised particles) and to 16 weeks (hydrosilylated particles). Conclusion The porous silicon photonic crystals showed good biocompatibility and may be used as an intraocular drug-delivery system. The intravitreal injectable porous silicon photonic crystals may be engineered to host a variety of therapeutics and achieve controlled drug release over long periods of time to treat chronic vitreoretinal diseases. PMID:18441177

  14. Light emitting structures porous silicon-silicon substrate

    International Nuclear Information System (INIS)

    Monastyrskii, L.S.; Olenych, I.B.; Panasjuk, M.R.; Savchyn, V.P.

    1999-01-01

    The research of spectroscopic properties of porous silicon has been done. Complex of photoluminescence, electroluminescence, cathodoluminescence, thermostimulated depolarisation current analyte methods have been applied to study of geterostructures and free layers of porous silicon. Light emitting processes had tendency to decrease. The character of decay for all kinds of luminescence were different

  15. Behavior and effect of Ti2Ni phase during processing of NiTi shape memory alloy wire from cast ingot

    International Nuclear Information System (INIS)

    Bhagyaraj, J.; Ramaiah, K.V.; Saikrishna, C.N.; Bhaumik, S.K.; Gouthama

    2013-01-01

    Highlights: •Ti 2 Ni second phase particles forms in different sizes and shapes in cast ingot. •TEM evidences showed shearing/fragmentation of Ti 2 Ni during processing. •Matrix close to Ti 2 Ni experienced severe plastic deformation lead to amorphisation. •Ti 2 Ni interfaces were mostly faceted and assist in nucleation of martensite. •Heterogeneity of microstructure observed near to and away from Ti 2 Ni. -- Abstract: Binary NiTi alloy is one of the commercially successful shape memory alloys (SMAs). Generally, the NiTi alloy composition used for thermal actuator application is slightly Ti-rich. In the present study, vacuum arc melted alloy of 50.2Ti–Ni (at.%) composition was prepared and characterized using optical, scanning and transmission electron microcopy. Formation of second phase particles (SPPs) in the cast alloy and their influence on development of microstructure during processing of the alloy into wire form has been investigated. Results showed that the present alloy contained Ti 2 Ni type SPPs in the matrix. In the cast alloy, the Ti 2 Ni particles form in varying sizes (1–10 μm) and shapes. During subsequent thermo-mechanical processing, these SPPs get sheared/fragmented into smaller particles with low aspect ratio. The presence of SPPs plays a significant role in refinement of the microstructure during processing of the alloy. During deformation of the alloy, the matrix phase around the SPPs experiences conditions similar to that observed in severe plastic deformation of metallic materials, leading to localized amorphisation of the matrix phase

  16. Gelcasting of SiC/Si for preparation of silicon nitride bonded silicon carbide

    International Nuclear Information System (INIS)

    Xie, Z.P.; Tsinghua University, Beijing,; Cheng, Y.B.; Lu, J.W.; Huang, Y.

    2000-01-01

    In the present paper, gelcasting of aqueous slurry with coarse silicon carbide(1mm) and fine silicon particles was investigated to fabricate silicon nitride bonded silicon carbide materials. Through the examination of influence of different polyelectrolytes on the Zeta potential and viscosity of silicon and silicon carbide suspensions, a stable SiC/Si suspension with 60 vol% solid loading could be prepared by using polyelectrolyte of D3005 and sodium alginate. Gelation of this suspension can complete in 10-30 min at 60-80 deg C after cast into mold. After demolded, the wet green body can be dried directly in furnace and the green strength will develop during drying. Complex shape parts with near net size were prepared by the process. Effects of the debindering process on nitridation and density of silicon nitride bonded silicon carbide were also examined. Copyright (2000) The Australian Ceramic Society

  17. Microstructure and textural characterization of hot extruded Zr-2.5Nb alloy PHWR pressure tube fabricated by various ingot processing route

    International Nuclear Information System (INIS)

    Vaibhaw, Kumar; Jha, S.K.; Saibaba, N.; Neogy, S.; Mani Krishna, K.V.; Srivastava, D.; Dey, G.K.

    2011-01-01

    Zr-2.5 Nb alloys finds its applications as a pressure tube component in pressure tube type thermal reactors such as PHWRs and RBMK due to properties attributed such as low neutron absorption cross section, high temperature strength and corrosion resistance etc. Manufacturing of this life time components involves series of thermo-mechanical processes of hot working and cold working with intermediate annealing. The life time of Pressure tube are limited due to their diametral creep properties which is governed by metallurgical characteristics such as texture, microstructure dislocation density etc. The primary breakdown of cast structure in Vacuum Arc Melted ingot can be effected by either hot extrusion or forging in single or multiple stages before final hot extrusion step into the blank for manufacturing of seamless pressure tube. Elevated temperature deformation carried out in hot working above the recrystallization temperature would enable impositions of large strains in single step. This deformation causes a significant change in the microstructure of the material and depends on process parameters such as extrusion ratio, temperature and strain rate. Basic microstructure developed at this deformation stage has significant bearing on the final properties of the material fabricated with subsequent cold working steps. The major texture in α+β Zr-2.5 Nb alloy is established during final extrusion to blank which does not change significantly during subsequent cold pilgering. However, microstructure is modified significantly in subsequent cold working which can be effected by cold pilgering or cold drawing in single or multiple steps. Present paper brings out the various ingot processing routes using forging and or extrusion followed for fabrication of pressure tubes. The development of texture and microstructures has been discussed at the blank stage from these processing routes and also with respect to varying extrusion variable such as extrusion ratio

  18. Silicon detectors

    International Nuclear Information System (INIS)

    Klanner, R.

    1984-08-01

    The status and recent progress of silicon detectors for high energy physics is reviewed. Emphasis is put on detectors with high spatial resolution and the use of silicon detectors in calorimeters. (orig.)

  19. FTIR studies of swift silicon and oxygen ion irradiated porous silicon

    International Nuclear Information System (INIS)

    Bhave, Tejashree M.; Hullavarad, S.S.; Bhoraskar, S.V.; Hegde, S.G.; Kanjilal, D.

    1999-01-01

    Fourier Transform Infrared Spectroscopy has been used to study the bond restructuring in silicon and oxygen irradiated porous silicon. Boron doped p-type (1 1 1) porous silicon was irradiated with 10 MeV silicon and a 14 MeV oxygen ions at different doses ranging between 10 12 and 10 14 ions cm -2 . The yield of PL in porous silicon irradiated samples was observed to increase considerably while in oxygen irradiated samples it was seen to improve only by a small extent for lower doses whereas it decreased for higher doses. The results were interpreted in view of the relative intensities of the absorption peaks associated with O-Si-H and Si-H stretch bonds

  20. Second-harmonic generation in substoichiometric silicon nitride layers

    Science.gov (United States)

    Pecora, Emanuele; Capretti, Antonio; Miano, Giovanni; Dal Negro, Luca

    2013-03-01

    Harmonic generation in optical circuits offers the possibility to integrate wavelength converters, light amplifiers, lasers, and multiple optical signal processing devices with electronic components. Bulk silicon has a negligible second-order nonlinear optical susceptibility owing to its crystal centrosymmetry. Silicon nitride has its place in the microelectronic industry as an insulator and chemical barrier. In this work, we propose to take advantage of silicon excess in silicon nitride to increase the Second Harmonic Generation (SHG) efficiency. Thin films have been grown by reactive magnetron sputtering and their nonlinear optical properties have been studied by femtosecond pumping over a wide range of excitation wavelengths, silicon nitride stoichiometry and thermal processes. We demonstrate SHG in the visible range (375 - 450 nm) using a tunable 150 fs Ti:sapphire laser, and we optimize the SH emission at a silicon excess of 46 at.% demonstrating a maximum SHG efficiency of 4x10-6 in optimized films. Polarization properties, generation efficiency, and the second order nonlinear optical susceptibility are measured for all the investigated samples and discussed in terms of an effective theoretical model. Our findings show that the large nonlinear optical response demonstrated in optimized Si-rich silicon nitride materials can be utilized for the engineering of nonlinear optical functions and devices on a Si chip.

  1. RTV Silicone Rubber Degradation Induced by Temperature Cycling

    Directory of Open Access Journals (Sweden)

    Xishan Wen

    2017-07-01

    Full Text Available Room temperature vulcanized (RTV silicone rubber is extensively used in power system due to its hydrophobicity and hydrophobicity transfer ability. Temperature has been proven to markedly affect the performance of silicone rubbers. This research investigated the degradation of RTV silicone rubber under temperature cycling treatment. Hydrophobicity and its transfer ability, hardness, functional groups, microscopic appearance, and thermal stability were analyzed using the static contact angle method, a Shore A durometer, Fourier transform infrared spectroscopy (FTIR, scanning electron microscopy (SEM, and thermogravimetry (TG, respectively. Some significant conclusions were drawn. After the temperature was cycled between −25 °C and 70 °C, the hydrophobicity changed modestly, but its transfer ability changed remarkably, which may result from the competition between the formation of more channels for the transfer of low molecular weight (LMW silicone fluid and the reduction of LMW silicone fluid in the bulk. A hardness analysis and FTIR analysis demonstrated that further cross-linking reactions occurred during the treatment. SEM images showed the changes in roughness of the RTV silicone rubber surfaces. TG analysis also demonstrated the degradation of RTV silicone rubber by presenting evidence that the content of organic materials decreased during the temperature cycling treatment.

  2. Nanostructured silicon anodes for lithium ion rechargeable batteries.

    Science.gov (United States)

    Teki, Ranganath; Datta, Moni K; Krishnan, Rahul; Parker, Thomas C; Lu, Toh-Ming; Kumta, Prashant N; Koratkar, Nikhil

    2009-10-01

    Rechargeable lithium ion batteries are integral to today's information-rich, mobile society. Currently they are one of the most popular types of battery used in portable electronics because of their high energy density and flexible design. Despite their increasing use at the present time, there is great continued commercial interest in developing new and improved electrode materials for lithium ion batteries that would lead to dramatically higher energy capacity and longer cycle life. Silicon is one of the most promising anode materials because it has the highest known theoretical charge capacity and is the second most abundant element on earth. However, silicon anodes have limited applications because of the huge volume change associated with the insertion and extraction of lithium. This causes cracking and pulverization of the anode, which leads to a loss of electrical contact and eventual fading of capacity. Nanostructured silicon anodes, as compared to the previously tested silicon film anodes, can help overcome the above issues. As arrays of silicon nanowires or nanorods, which help accommodate the volume changes, or as nanoscale compliant layers, which increase the stress resilience of silicon films, nanoengineered silicon anodes show potential to enable a new generation of lithium ion batteries with significantly higher reversible charge capacity and longer cycle life.

  3. Development and characterization of Al-Zn alloy by ingot metallurgy and powder metallurgy with improved mechanical properties

    International Nuclear Information System (INIS)

    Waseem, M.; Awais, H.B.; Zauha, M.S.; Tariq, N.H.

    2007-01-01

    Current project focuses on the production of AI-Zn alloy AA7075 used for wide range of applications like Aircraft components, missile and other structural applications. The above alloy was developed by two different routes. One was melting /casting, after which alloy was characterized by microstructural - examination (optical and SEM) and mechanical testing. Other route was the preparation of this alloy by powder metallurgy. This involves preparation of powders, mechanical alloying, compaction, sintering, rolling, solution treatment and aging then analysis. Powders of Aluminum, Zinc and powders of master alloys of AI-Cu, AI-Mg, AI-Mn, and AI-Cr were Mechanical alloyed. Then this powder was compacted by uniaxial press to form pellets. Sintering was carried out at 500 degree C and then hot rolled in Ar atmosphere. After solution and aging treatments samples were characterized. It is observed that there is about 12-21% improvement in mechanical properties such as tensile strength, yield strength, ductility and fracture toughness due to the more fine microstructure and less segregation than ingot metallurgy route. (author)

  4. Microelectronic temperature sensor; silicon temperature sensor

    International Nuclear Information System (INIS)

    Beitner, M.; Kanert, W.; Reichert, H.

    1982-01-01

    The goal of this work was to develop a silicon temperature sensor with a sensitivity and a reliability as high and a tolerance as small as possible, for use in measurement and control. By employing the principle of spreading-resistance, using silicon doped by neutron transmutation, and trimming of the single wafer tolerances of resistance less than +- 5% can be obtained; overstress tests yielded a long-term stability better than 0.2%. Some applications show the advantageous use of this sensor. (orig.) [de

  5. Molecular dynamics study of the thermal expansion coefficient of silicon

    Energy Technology Data Exchange (ETDEWEB)

    Nejat Pishkenari, Hossein, E-mail: nejat@sharif.edu; Mohagheghian, Erfan; Rasouli, Ali

    2016-12-16

    Due to the growing applications of silicon in nano-scale systems, a molecular dynamics approach is employed to investigate thermal properties of silicon. Since simulation results rely upon interatomic potentials, thermal expansion coefficient (TEC) and lattice constant of bulk silicon have been obtained using different potentials (SW, Tersoff, MEAM, and EDIP) and results indicate that SW has a better agreement with the experimental observations. To investigate effect of size on TEC of silicon nanowires, further simulations are performed using SW potential. To this end, silicon nanowires of different sizes are examined and their TEC is calculated by averaging in different directions ([100], [110], [111], and [112]) and various temperatures. Results show that as the size increases, due to the decrease of the surface effects, TEC approaches its bulk value. - Highlights: • MD simulations of TEC and lattice constant of bulk silicon. • Effects of four potentials on the results. • Comparison to experimental data. • Investigating size effect on TEC of silicon nanowires.

  6. Annealing temperature dependence of photoluminescent characteristics of silicon nanocrystals embedded in silicon-rich silicon nitride films grown by PECVD

    International Nuclear Information System (INIS)

    Chao, D.S.; Liang, J.H.

    2013-01-01

    Recently, light emission from silicon nanostructures has gained great interest due to its promising potential of realizing silicon-based optoelectronic applications. In this study, luminescent silicon nanocrystals (Si–NCs) were in situ synthesized in silicon-rich silicon nitride (SRSN) films grown by plasma-enhanced chemical vapor deposition (PECVD). SRSN films with various excess silicon contents were deposited by adjusting SiH 4 flow rate to 100 and 200 sccm and keeping NH 3 one at 40 sccm, and followed by furnace annealing (FA) treatments at 600, 850 and 1100 °C for 1 h. The effects of excess silicon content and post-annealing temperature on optical properties of Si–NCs were investigated by photoluminescence (PL) and Fourier transform infrared spectroscopy (FTIR). The origins of two groups of PL peaks found in this study can be attributed to defect-related interface states and quantum confinement effects (QCE). Defect-related interface states lead to the photon energy levels almost kept constant at about 3.4 eV, while QCE results in visible and tunable PL emission in the spectral range of yellow and blue light which depends on excess silicon content and post-annealing temperature. In addition, PL intensity was also demonstrated to be highly correlative to the excess silicon content and post-annealing temperature due to its corresponding effects on size, density, crystallinity, and surface passivation of Si–NCs. Considering the trade-off between surface passivation and structural properties of Si–NCs, an optimal post-annealing temperature of 600 °C was suggested to maximize the PL intensity of the SRSN films

  7. Electrical properties improvement of multicrystalline silicon solar cells using a combination of porous silicon and vanadium oxide treatment

    International Nuclear Information System (INIS)

    Derbali, L.; Ezzaouia, H.

    2013-01-01

    In this paper, we will report the enhancement of the conversion efficiency of multicrystalline silicon solar cells after coating the front surface with a porous silicon layer treated with vanadium oxide. The incorporation of vanadium oxide into the porous silicon (PS) structure, followed by a thermal treatment under oxygen ambient, leads to an important decrease of the surface reflectivity, a significant enhancement of the effective minority carrier lifetime (τ eff ) and a significant enhancement of the photoluminescence (PL) of the PS structure. We Obtained a noticeable increase of (τ eff ) from 3.11 μs to 134.74 μs and the surface recombination velocity (S eff ) have decreased from 8441 cm s −1 to 195 cm s −1 . The reflectivity spectra of obtained films, performed in the 300–1200 nm wavelength range, show an important decrease of the average reflectivity from 40% to 5%. We notice a significant improvement of the internal quantum efficiency (IQE) in the used multicrystalline silicon substrates. Results are analyzed and compared to those carried out on a reference (untreated) sample. The electrical properties of the treated silicon solar cells were improved noticeably as regard to the reference (untreated) sample.

  8. High-performance lithium battery anodes using silicon nanowires.

    Science.gov (United States)

    Chan, Candace K; Peng, Hailin; Liu, Gao; McIlwrath, Kevin; Zhang, Xiao Feng; Huggins, Robert A; Cui, Yi

    2008-01-01

    There is great interest in developing rechargeable lithium batteries with higher energy capacity and longer cycle life for applications in portable electronic devices, electric vehicles and implantable medical devices. Silicon is an attractive anode material for lithium batteries because it has a low discharge potential and the highest known theoretical charge capacity (4,200 mAh g(-1); ref. 2). Although this is more than ten times higher than existing graphite anodes and much larger than various nitride and oxide materials, silicon anodes have limited applications because silicon's volume changes by 400% upon insertion and extraction of lithium which results in pulverization and capacity fading. Here, we show that silicon nanowire battery electrodes circumvent these issues as they can accommodate large strain without pulverization, provide good electronic contact and conduction, and display short lithium insertion distances. We achieved the theoretical charge capacity for silicon anodes and maintained a discharge capacity close to 75% of this maximum, with little fading during cycling.

  9. Electrical behavior of free-standing porous silicon layers

    International Nuclear Information System (INIS)

    Bazrafkan, I.; Dariani, R.S.

    2009-01-01

    The electrical behavior of porous silicon (PS) layers has been investigated on one side of p-type silicon with various anodization currents and electrolytes. The two contact I-V characteristic is assigned by the metal/porous silicon rectifying interface, whereas, by using the van der Pauw technique, a nonlinear dependence of the current vs voltage was found. By using Dimethylformamide (DMF) in electrolyte, regular structures and columns were formed and porosity increased. Our results showed that by using DMF, surface resistivity of PS samples increased and became double for free-standing porous silicon (FPS). The reason could be due to increasing surface area and adsorbing some more gas molecules. Activation energy of PS samples was also increased from 0.31 to 0.34 eV and became 0.35 eV for FPS. The changes induced by storage are attributed to the oxidation process of the internal surface of free-standing porous silicon layers.

  10. Hydrogen Incorporation during Aluminium Anodisation on Silicon Wafer Surfaces

    International Nuclear Information System (INIS)

    Lu, Pei Hsuan Doris; Strutzberg, Hartmuth; Wenham, Stuart; Lennon, Alison

    2014-01-01

    Hydrogen can act to reduce recombination at silicon surfaces for solar cell devices and consequently the ability of dielectric layers to provide a source of hydrogen for this purpose is of interest. However, due to the ubiquitous nature of hydrogen and its mobility, direct measurements of hydrogen incorporation in dielectric layers are challenging. In this paper, we report the use of secondary ion mass spectrometry measurements to show that deuterium from an electrolyte can be incorporated in an anodic aluminium oxide (AAO) layer and be introduced into an underlying amorphous silicon layer during anodisation of aluminium on silicon wafers. After annealing at 400 °C, the concentration of deuterium in the AAO was reduced by a factor of two, as the deuterium was re-distributed to the interface between the amorphous silicon and AAO and to the amorphous silicon. The assumption that hydrogen, from an aqueous electrolyte, could be similarly incorporated in AAO, is supported by the observation that the hydrogen content in the underlying amorphous silicon was increased by a factor of ∼ 3 after anodisation. Evidence for hydrogen being introduced into crystalline silicon after aluminium anodisation was provided by electrochemical capacitance voltage measurements indicating boron electrical deactivation in the underlying crystalline silicon. If introduced hydrogen can electrically deactivate dopant atoms at the surface, then it is reasonable to assume that it could also deactivate recombination-active states at the crystalline silicon interface therefore enabling higher minority carrier lifetimes in the silicon wafer

  11. Large grain CBMM Nb ingot slices: An ideal test bed for exploring the microstructure-electromagnetic property relationships relevant to SRF

    International Nuclear Information System (INIS)

    Sung, Zu-Hawn; Lee, Peter J.; Polyanskii, Anatolii; Balachandran, Shreyas; Chetri, Santosh; Larbalestier, David C.; Wang, Mingmin; Compton, Christopher; Bieler, Thomas R.

    2015-01-01

    High purity (RRR > 200), large grain (> 5-10 cm) niobium ingot slices have been successfully used to fabricate radio frequency (RF) cavities for particle accelerators. They offer significantly reduced fabrication cost by eliminating processing steps and furthermore they provide the opportunity to study the influence of individual grain boundaries in SRF Nb. Here we summarize our measurements of grain boundary (GB) effects on the superconducting properties of large grain high purity niobium sheet manufactured by CBMM. We show by magneto-optical (MO) imaging that GBs allow premature flux penetration, but only when they are oriented close to the direction of the magnetic field. However, even low angle GBs produced by minor deformations commensurate with half-cell forming produce localized flux penetration. The transport properties of grain boundaries were investigated by direct transport across them and evidence for preferential vortex flow along the GBs of SRF Nb was observed for the first time. Using transmission electron microscopy (TEM) and micro crystallographic analysis with electron backscattered diffraction (EBSD), we were able to quantitatively characterize surface substructures that can lead to localized thermal breakdown of superconductivity. Important to these studies was the development of sample preparation techniques that made the cutout single, bi-crystal and tri-crystal Nb coupons as representative as possible of the surface properties of cavities manufactured by standard techniques

  12. The two sides of silicon detectors

    International Nuclear Information System (INIS)

    Devine, S.R.

    2001-10-01

    Results are presented on in situ irradiation of silicon detector's at cryogenic temperature. The results show that irradiation at cryogenic temperatures does not detrimentally effect a silicon detectors performance when compared to its irradiation at room temperature. Operation of silicon devices at cryogenic temperatures offers the advantage of reducing radiation-induced leakage current to levels of a few pA, while at 130K the Lazarus Effect plays an important role i.e. minimum voltage required for full depletion. Performing voltage scans on a 'standard' silicon pad detector pre- and post annealing, the charge collection efficiency was found to be 60% at 200V and 95% at 200V respectively. Time dependence measurements are presented, showing that for a dose of 6.5x10 14 p/cm 2 (450GeV protons) the time dependence of the charge collection efficiency is negligible. However, for higher doses, 1.2x10 15 p/cm 2 , the charge collection efficiency drops from an initial measured value of 67% to a stable value of 58% over a period of 15 minutes for reversed biased diodes. An analysis of the 'double junction' effect is also presented. A comparison between the Transient Current Technique and an X-ray technique is presented. The double junction has been observed in p + /n/n + silicon detectors after irradiation beyond 'type inversion', corresponding to a fluence equivalent to ∼3x10 13 cm -2 1MeV neutrons, producing p + /p/n + and essentially two p-n junctions within one device. With increasing bias voltage, as the electric field is extending into the detector bulk from opposite sides of the silicon detector, there are two distinct depletion regions that collect charge signal independently. Summing the signal charge from the two regions, one is able to reconstruct the initial energy of the incident particle. From Transient Current measurements it is apparent that E-field manipulation is possible by excess carrier injection, enabling a high enough E-field to extend across the

  13. Nonlinear behavior of photoluminescence from silicon particles under two-photon excitation

    International Nuclear Information System (INIS)

    Xu Xingsheng; Yokoyama, Shiyoshi

    2011-01-01

    Two-photon excited fluorescence (TPEF) under continuous-wave excitation from silicon particles produced by a pulsed laser is investigated. Spectra and images of TPEF from silicon particles are studied under different excitation intensities and operation modes (continuous wave or pulse). It is found that the photoluminescence depends superlinearly on the excitation intensity and that the spectral shape and peaks vary with different silicon particles. The above phenomena show the nonlinear behavior of TPEF from silicon particles, and stimulated emission is a possible process.

  14. Strategies for doped nanocrystalline silicon integration in silicon heterojunction solar cells

    Czech Academy of Sciences Publication Activity Database

    Seif, J.; Descoeudres, A.; Nogay, G.; Hänni, S.; de Nicolas, S.M.; Holm, N.; Geissbühler, J.; Hessler-Wyser, A.; Duchamp, M.; Dunin-Borkowski, R.E.; Ledinský, Martin; De Wolf, S.; Ballif, C.

    2016-01-01

    Roč. 6, č. 5 (2016), s. 1132-1140 ISSN 2156-3381 R&D Projects: GA MŠk LM2015087 Institutional support: RVO:68378271 Keywords : microcrystalline silicon * nanocrystalline silicon * silicon heterojunctions (SHJs) * solar cells Subject RIV: BM - Solid Matter Physics ; Magnetism Impact factor: 3.712, year: 2016

  15. Characterization of New-Generation Silicon Photomultipliers for Nuclear Security Applications

    Science.gov (United States)

    Wonders, Marc A.; Chichester, David L.; Flaska, Marek

    2018-01-01

    Silicon photomultipliers have received a great deal of interest recently for use in applications spanning a wide variety of fields, including nuclear safeguards and nonproliferation. For nuclear-related applications, the ability of silicon photomultipliers to discriminate neutrons from gamma rays using pulse shape discrimination when coupled with certain organic scintillators is a characteristic of utmost importance. This work reports on progress characterizing the performance of twenty different silicon photomultipliers from five manufacturers with an emphasis on pulse shape discrimination performance and timing. Results are presented on pulse shape discrimination performance as a function of overvoltage for 6-mm x 6-mm silicon photomultipliers, and the time response to stilbene is characterized for silicon photomultipliers of three different sizes. Finally, comparison with a photomultiplier tube shows that some new-generation silicon photomultipliers can perform as well as photomultiplier tubes in neutron-gamma ray discrimination.

  16. Thermal processing of strained silicon-on-insulator for atomically precise silicon device fabrication

    International Nuclear Information System (INIS)

    Lee, W.C.T.; Bishop, N.; Thompson, D.L.; Xue, K.; Scappucci, G.; Cederberg, J.G.; Gray, J.K.; Han, S.M.; Celler, G.K.; Carroll, M.S.; Simmons, M.Y.

    2013-01-01

    Highlights: ► Strained silicon-on-insulator (sSOI) samples were flash-annealed at high temperature under ultra-high vacuum conditions. ► The extend of surface strain relaxation depends on the annealing temperature with no strain relaxation observed below 1020 °C. ► A 2 × 1 reconstructed surface with low defect density can be achieved. ► The annealed sSOI surface shows enhanced step undulations due to the unique energetics caused by surface strain. - Abstract: We investigate the ability to reconstruct strained silicon-on-insulator (sSOI) substrates in ultra-high vacuum for use in atomic scale device fabrication. Characterisation of the starting sSOI substrate using μRaman shows an average tensile strain of 0.8%, with clear strain modulation in a crosshatch pattern across the surface. The surfaces were heated in ultra-high vacuum from temperatures of 900 °C to 1100 °C and subsequently imaged using scanning tunnelling microscopy (STM). The initial strain modulation on the surface is observed to promote silicon migration and the formation of crosshatched surface features whose height and pitch increases with increasing annealing temperature. STM images reveal alternating narrow straight S A steps and triangular wavy S B steps attributed to the spontaneous faceting of S B and preferential adatom attachment on S B under biaxial tensile strain. Raman spectroscopy shows that despite these high temperature anneals no strain relaxation of the substrate is observed up to temperatures of 1020 °C. Above 1100 °C, strain relaxation is evident but is confined to the surface.

  17. Efficiency Enhancement of Silicon Solar Cells by Porous Silicon Technology

    Directory of Open Access Journals (Sweden)

    Eugenijus SHATKOVSKIS

    2012-09-01

    Full Text Available Silicon solar cells produced by a usual technology in p-type, crystalline silicon wafer were investigated. The manufactured solar cells were of total thickness 450 mm, the junction depth was of 0.5 mm – 0.7 mm. Porous silicon technologies were adapted to enhance cell efficiency. The production of porous silicon layer was carried out in HF: ethanol = 1 : 2 volume ratio electrolytes, illuminating by 50 W halogen lamps at the time of processing. The etching current was computer-controlled in the limits of (6 ÷ 14 mA/cm2, etching time was set in the interval of (10 ÷ 20 s. The characteristics and performance of the solar cells samples was carried out illuminating by Xenon 5000 K lamp light. Current-voltage characteristic studies have shown that porous silicon structures produced affect the extent of dark and lighting parameters of the samples. Exactly it affects current-voltage characteristic and serial resistance of the cells. It has shown, the formation of porous silicon structure causes an increase in the electric power created of solar cell. Conversion efficiency increases also respectively to the initial efficiency of cell. Increase of solar cell maximum power in 15 or even more percent is found. The highest increase in power have been observed in the spectral range of Dl @ (450 ÷ 850 nm, where ~ 60 % of the A1.5 spectra solar energy is located. It has been demonstrated that porous silicon technology is effective tool to improve the silicon solar cells performance.DOI: http://dx.doi.org/10.5755/j01.ms.18.3.2428

  18. Chiral silicon nanostructures

    International Nuclear Information System (INIS)

    Schubert, E.; Fahlteich, J.; Hoeche, Th.; Wagner, G.; Rauschenbach, B.

    2006-01-01

    Glancing angle ion beam assisted deposition is used for the growth of amorphous silicon nanospirals onto [0 0 1] silicon substrates in a temperature range from room temperature to 475 deg. C. The nanostructures are post-growth annealed in an argon atmosphere at various temperatures ranging from 400 deg. C to 800 deg. C. Recrystallization of silicon within the persisting nanospiral configuration is demonstrated for annealing temperatures above 800 deg. C. Transmission electron microscopy and Raman spectroscopy are used to characterize the silicon samples prior and after temperature treatment

  19. Flexible integration of free-standing nanowires into silicon photonics.

    Science.gov (United States)

    Chen, Bigeng; Wu, Hao; Xin, Chenguang; Dai, Daoxin; Tong, Limin

    2017-06-14

    Silicon photonics has been developed successfully with a top-down fabrication technique to enable large-scale photonic integrated circuits with high reproducibility, but is limited intrinsically by the material capability for active or nonlinear applications. On the other hand, free-standing nanowires synthesized via a bottom-up growth present great material diversity and structural uniformity, but precisely assembling free-standing nanowires for on-demand photonic functionality remains a great challenge. Here we report hybrid integration of free-standing nanowires into silicon photonics with high flexibility by coupling free-standing nanowires onto target silicon waveguides that are simultaneously used for precise positioning. Coupling efficiency between a free-standing nanowire and a silicon waveguide is up to ~97% in the telecommunication band. A hybrid nonlinear-free-standing nanowires-silicon waveguides Mach-Zehnder interferometer and a racetrack resonator for significantly enhanced optical modulation are experimentally demonstrated, as well as hybrid active-free-standing nanowires-silicon waveguides circuits for light generation. These results suggest an alternative approach to flexible multifunctional on-chip nanophotonic devices.Precisely assembling free-standing nanowires for on-demand photonic functionality remains a challenge. Here, Chen et al. integrate free-standing nanowires into silicon waveguides and show all-optical modulation and light generation on silicon photonic chips.

  20. Self-organized, effective medium black silicon antireflection structures for silicon optics in the mid-infrared

    Science.gov (United States)

    Steglich, Martin; Käsebier, Thomas; Kley, Ernst-Bernhard; Tünnermann, Andreas

    2016-09-01

    Thanks to its high quality and low cost, silicon is the material of choice for optical devices operating in the mid-infrared (MIR; 2 μm to 6 μm wavelength). Unfortunately in this spectral region, the refractive index is comparably high (about 3.5) and leads to severe reflection losses of about 30% per interface. In this work, we demonstrate that self-organized, statistical Black Silicon structures, fabricated by Inductively Coupled Plasma Reactive Ion Etching (ICP-RIE), can be used to effectively suppress interface reflection. More importantly, it is shown that antireflection can be achieved in an image-preserving, non-scattering way. This enables Black Silicon antireflection structures (ARS) for imaging applications in the MIR. It is demonstrated that specular transmittances of 97% can be easily achieved on both flat and curved substrates, e.g. lenses. Moreover, by a combined optical and morphological analysis of a multitude of different Black Silicon ARS, an effective medium criterion for the examined structures is derived that can also be used as a design rule for maximizing sample transmittance in a desired wavelength range. In addition, we show that the mechanical durability of the structures can be greatly enhanced by coating with hard dielectric materials like diamond-like carbon (DLC), hence enabling practical applications. Finally, the distinct advantages of statistical Black Silicon ARS over conventional AR layer stacks are discussed: simple applicability to topological substrates, absence of thermal stress and cost-effectiveness.

  1. On numerical modeling of low-head direct chill ingot caster for magnesium alloy AZ31

    Directory of Open Access Journals (Sweden)

    Mainul Hasan

    2014-12-01

    Full Text Available A comprehensive 3D turbulent CFD study has been carried out to simulate a Low-Head (LH vertical Direct Chill (DC rolling ingot caster for the common magnesium alloy AZ31. The model used in this study takes into account the coupled laminar/turbulent melt flow and solidification aspects of the process and is based on the control-volume finite-difference approach. Following the aluminum/magnesium DC casting industrial practices, the LH mold is taken as 30 mm with a hot top of 60 mm. The previously verified in-house code has been modified to model the present casting process. Important quantitative results are obtained for four casting speeds, for three inlet melt pouring temperatures (superheats and for three metal-mold contact heat transfer coefficients for the steady state operational phase of the caster. The variable cooling water temperatures reported by the industry are considered for the primary and secondary cooling zones during the simulations. Specifically, the temperature and velocity fields, sump depth and sump profiles, mushy region thickness, solid shell thickness at the exit of the mold and axial temperature profiles at the center and at three strategic locations at the surface of the slab are presented and discussed.

  2. The chemistry of silicon

    CERN Document Server

    Rochow, E G; Emeléus, H J; Nyholm, Ronald

    1975-01-01

    Pergamon Texts in Organic Chemistry, Volume 9: The Chemistry of Silicon presents information essential in understanding the chemical properties of silicon. The book first covers the fundamental aspects of silicon, such as its nuclear, physical, and chemical properties. The text also details the history of silicon, its occurrence and distribution, and applications. Next, the selection enumerates the compounds and complexes of silicon, along with organosilicon compounds. The text will be of great interest to chemists and chemical engineers. Other researchers working on research study involving s

  3. Effects of nanostructurized silicon on proliferation of stem and cancer cell.

    Science.gov (United States)

    Osminkina, L A; Luckyanova, E N; Gongalsky, M B; Kudryavtsev, A A; Gaydarova, A Kh; Poltavtseva, R A; Kashkarov, P K; Timoshenko, V Yu; Sukhikh, G T

    2011-05-01

    In vitro experiments showed that stem and cancer cells retained their viability on the surface of porous silicon with 10-100 nm nanostructures, but their proliferation was inhibited. Silicon nanoparticles of 100 nm in size obtained by mechanical grinding of porous silicon films or crystal silicon plates in a concentration below 1 mg/ml in solution did not modify viability and proliferation of mouse fibroblast and human laryngeal cancer cells. Additional ultrasonic exposure of cancer cells in the presence of 1 mg/ml silicon nanoparticles added to nutrient medium led to complete destruction of cells or to the appearance of membrane defects blocking their proliferation and initiating their apoptotic death.

  4. Characterization of New-Generation Silicon Photomultipliers for Nuclear Security Applications

    Directory of Open Access Journals (Sweden)

    Wonders Marc A.

    2018-01-01

    Full Text Available Silicon photomultipliers have received a great deal of interest recently for use in applications spanning a wide variety of fields, including nuclear safeguards and nonproliferation. For nuclear-related applications, the ability of silicon photomultipliers to discriminate neutrons from gamma rays using pulse shape discrimination when coupled with certain organic scintillators is a characteristic of utmost importance. This work reports on progress characterizing the performance of twenty different silicon photomultipliers from five manufacturers with an emphasis on pulse shape discrimination performance and timing. Results are presented on pulse shape discrimination performance as a function of overvoltage for 6-mm x 6-mm silicon photomultipliers, and the time response to stilbene is characterized for silicon photomultipliers of three different sizes. Finally, comparison with a photomultiplier tube shows that some new-generation silicon photomultipliers can perform as well as photomultiplier tubes in neutron-gamma ray discrimination.

  5. Ocular silicon distribution and clearance following intravitreal injection of porous silicon microparticles.

    Science.gov (United States)

    Nieto, Alejandra; Hou, Huiyuan; Sailor, Michael J; Freeman, William R; Cheng, Lingyun

    2013-11-01

    Porous silicon (pSi) microparticles have been investigated for intravitreal drug delivery and demonstrated good biocompatibility. With the appropriate surface chemistry, pSi can reside in vitreous for months or longer. However, ocular distribution and clearance pathway of its degradation product, silicic acid, are not well understood. In the current study, rabbit ocular tissue was collected at different time point following fresh pSi (day 1, 5, 9, 16, and 21) or oxidized pSi (day 3, 7, 14, 21, and 35) intravitreal injection. In addition, dual-probe simultaneous microdialysis of aqueous and vitreous humor was performed following a bolus intravitreal injection of 0.25 mL silicic acid (150 μg/mL) and six consecutive microdialysates were collected every 20 min. Silicon was quantified from the samples using inductively coupled plasma-optical emission spectroscopy. The study showed that following the intravitreal injection of oxidized pSi, free silicon was consistently higher in the aqueous than in the retina (8.1 ± 6.5 vs. 3.4 ± 3.9 μg/mL, p = 0.0031). The area under the concentration-time curve (AUC) of the retina was only about 24% that of the aqueous. The mean residence time was 16 days for aqueous, 13 days for vitreous, 6 days for retina, and 18 days for plasma. Similarly, following intravitreal fresh pSi, free silicon was also found higher in aqueous than in retina (7 ± 4.7 vs. 3.4 ± 4.1 μg/mL, p = 0.014). The AUC for the retina was about 50% of the AUC for the aqueous. The microdialysis revealed the terminal half-life of free silicon in the aqueous was 30 min and 92 min in the vitreous; the AUC for aqueous accounted for 38% of the AUC for vitreous. Our studies indicate that aqueous humor is a significant pathway for silicon egress from the eye following intravitreal injection of pSi crystals. Copyright © 2013 Elsevier Ltd. All rights reserved.

  6. Analytical and experimental evaluation of joining silicon carbide to silicon carbide and silicon nitride to silicon nitride for advanced heat engine applications Phase 2. Final report

    Energy Technology Data Exchange (ETDEWEB)

    Sundberg, G.J.; Vartabedian, A.M.; Wade, J.A.; White, C.S. [Norton Co., Northboro, MA (United States). Advanced Ceramics Div.

    1994-10-01

    The purpose of joining, Phase 2 was to develop joining technologies for HIP`ed Si{sub 3}N{sub 4} with 4wt% Y{sub 2}O{sub 3} (NCX-5101) and for a siliconized SiC (NT230) for various geometries including: butt joins, curved joins and shaft to disk joins. In addition, more extensive mechanical characterization of silicon nitride joins to enhance the predictive capabilities of the analytical/numerical models for structural components in advanced heat engines was provided. Mechanical evaluation were performed by: flexure strength at 22 C and 1,370 C, stress rupture at 1,370 C, high temperature creep, 22 C tensile testing and spin tests. While the silicon nitride joins were produced with sufficient integrity for many applications, the lower join strength would limit its use in the more severe structural applications. Thus, the silicon carbide join quality was deemed unsatisfactory to advance to more complex, curved geometries. The silicon carbide joining methods covered within this contract, although not entirely successful, have emphasized the need to focus future efforts upon ways to obtain a homogeneous, well sintered parent/join interface prior to siliconization. In conclusion, the improved definition of the silicon carbide joining problem obtained by efforts during this contract have provided avenues for future work that could successfully obtain heat engine quality joins.

  7. Silicon microspheres for near-IR communication applications

    International Nuclear Information System (INIS)

    Serpengüzel, Ali; Demir, Abdullah

    2008-01-01

    We have performed transverse electric and transverse magnetic polarized elastic light scattering calculations at 90° and 0° in the o-band at 1.3 µm for a 15 µm radius silicon microsphere with a refractive index of 3.5. The quality factors are on the order of 10 7 and the mode/channel spacing is 7 nm, which correlate well with the refractive index and the optical size of the microsphere. The 90° elastic light scattering can be used to monitor a dropped channel (drop port), whereas the 0° elastic scattering can be used to monitor the transmission channel (through port). The optical resonances of the silicon microspheres provide the necessary narrow linewidths that are needed for high-resolution optical communication applications. Potential telecommunication applications include filters, modulators, switches, wavelength converters, detectors, amplifiers and light sources. Silicon microspheres show promise as potential building blocks for silicon-based electrophotonic integration

  8. Recycling of silicon: from industrial waste to biocompatible nanoparticles for nanomedicine

    Science.gov (United States)

    Kozlov, N. K.; Natashina, U. A.; Tamarov, K. P.; Gongalsky, M. B.; Solovyev, V. V.; Kudryavtsev, A. A.; Sivakov, V.; Osminkina, L. A.

    2017-09-01

    The formation of photoluminescent porous silicon (PSi) nanoparticles (NPs) is usually based on an expensive semiconductor grade wafers technology. Here, we report a low-cost method of PSi NPs synthesis from the industrial silicon waste remained after the wafer production. The proposed method is based on metal-assisted wet-chemical etching (MACE) of the silicon surface of cm-sized metallurgical grade silicon stones which leads to a nanostructuring of the surface due to an anisotropic etching, with subsequent ultrasound fracturing in water. The obtained PSi NPs exhibit bright red room temperature photoluminescence (PL) and demonstrate similar microstructure and physical characteristics in comparison with the nanoparticles synthesized from semiconductor grade Si wafers. PSi NPs prepared from metallurgical grade silicon stones, similar to silicon NPs synthesized from high purity silicon wafer, show low toxicity to biological objects that open the possibility of using such type of NPs in nanomedicine.

  9. Hydrogen in amorphous silicon

    International Nuclear Information System (INIS)

    Peercy, P.S.

    1980-01-01

    The structural aspects of amorphous silicon and the role of hydrogen in this structure are reviewed with emphasis on ion implantation studies. In amorphous silicon produced by Si ion implantation of crystalline silicon, the material reconstructs into a metastable amorphous structure which has optical and electrical properties qualitatively similar to the corresponding properties in high-purity evaporated amorphous silicon. Hydrogen studies further indicate that these structures will accomodate less than or equal to 5 at.% hydrogen and this hydrogen is bonded predominantly in a monohydride (SiH 1 ) site. Larger hydrogen concentrations than this can be achieved under certain conditions, but the excess hydrogen may be attributed to defects and voids in the material. Similarly, glow discharge or sputter deposited amorphous silicon has more desirable electrical and optical properties when the material is prepared with low hydrogen concentration and monohydride bonding. Results of structural studies and hydrogen incorporation in amorphous silicon were discussed relative to the different models proposed for amorphous silicon

  10. A convenient way of manufacturing silicon nanotubes on a silicon substrate

    Energy Technology Data Exchange (ETDEWEB)

    Zhang, Changchang; Cheng, Heming; Liu, Xiang, E-mail: liuxiang@ahut.edu.cn

    2016-07-01

    A convenient approach of preparing silicon nanotubes (SiNTs) on a silicon substrate is described in this work in detail. Firstly, a porous silicon (PSi) slice is prepared by a galvanic displacement reaction. Then it is put into aqueous solutions of 20% (w%) ammonium fluoride and 2.5 mM cobalt nitrate for a predetermined time. The cobalt ions are reduced and the resulted cobalt particles are deposited on the PSi slice. After the cobalt particles are removed with 5 M nitric acid a plenty of SiNTs come out and exhibit disorderly on the silicon substrate, which are illustrated by scanning electron microscopy (SEM). The compositions of the SiNTs are examined by energy-dispersive X-ray spectroscopy. Based on the SEM images, a suggested mechanism is put forward to explain the generation of the SiNTs on the PSi substrate. - Highlights: • A facile approach of preparing silicon nano tubes was invented. • The experimental results demonstrated the strong reducibility of Si-H{sub x} species. • It provided a new way of manufacturing silicon-contained hybrids.

  11. Development of Radiation Hard Radiation Detectors, Differences between Czochralski Silicon and Float Zone Silicon

    CERN Document Server

    Tuominen, Eija

    2012-01-01

    The purpose of this work was to develop radiation hard silicon detectors. Radiation detectors made ofsilicon are cost effective and have excellent position resolution. Therefore, they are widely used fortrack finding and particle analysis in large high-energy physics experiments. Silicon detectors willalso be used in the CMS (Compact Muon Solenoid) experiment that is being built at the LHC (LargeHadron Collider) accelerator at CERN (European Organisation for Nuclear Research). This work wasdone in the CMS programme of Helsinki Institute of Physics (HIP).Exposure of the silicon material to particle radiation causes irreversible defects that deteriorate theperformance of the silicon detectors. In HIP CMS Programme, our approach was to improve theradiation hardness of the silicon material with increased oxygen concentration in silicon material. Westudied two different methods: diffusion oxygenation of Float Zone silicon and use of high resistivityCzochralski silicon.We processed, characterised, tested in a parti...

  12. Thiolated silicone oils as adhesive skin protectants for improved barrier function.

    Science.gov (United States)

    Partenhauser, A; Zupančič, O; Rohrer, J; Bonengel, S; Bernkop-Schnürch, A

    2016-06-01

    The purpose of this study was the evaluation of thiolated silicone oil as novel skin protectant exhibiting prolonged residence time, enhanced barrier function and reinforced occlusivity. Two silicone conjugates were synthesized with mercaptopropionic acid (MPA) and thioglycolic acid (TGA) as thiol ligands. Adhesion, protection against artificial urine and water vapour permeability with both a Payne cup set-up and transepidermal water loss (TEWL) measurements on porcine skin were assessed. Silicone thiomers showed pronounced substantivity on skin with 22.1 ± 6.3% and 39.2 ± 6.7% remaining silicone after 8 h for silicone-TGA and silicone-MPA, respectively, whereas unmodified silicone oil and dimethicone were no longer detectable. In particular, silicone-MPA provided a protective shield against artificial urine penetration with less than 25% leakage within 6 h. An up to 2.5-fold improved water vapour impermeability for silicone-MPA in comparison with unmodified control was discovered with the Payne cup model. In addition, for silicone-MPA a reduced TEWL by two-thirds corresponding to non-thiolated control was determined for up to 8 h. Thiolation of silicone oil leads to enhanced skin adhesiveness and barrier function, which is a major advantage compared to commonly used silicones and might thus be a promising treatment modality for various topical applications. © 2015 Society of Cosmetic Scientists and the Société Française de Cosmétologie.

  13. Fabrication of micromirrors with pyramidal shape using anisotropic etching of silicon

    OpenAIRE

    Moktadir, Z.; Vijaya Prakash, G.; Trupke, M.; Koukharenko, E.; Kraft, M.; Baumberg, J.J.; Eriksson, S.; Hinds, E.A.

    2005-01-01

    Gold micro-mirrors have been formed in silicon in an inverted pyramidal shape. The pyramidal structures are created in the (100) surface of a silicon wafer by anisotropic etching in potassium hydroxide. High quality micro-mirrors are then formed by sputtering gold onto the smooth silicon (111) faces of the pyramids. These mirrors show great promise as high quality optical devices suitable for integration into MOEMS systems.

  14. SVX/silicon detector studies

    International Nuclear Information System (INIS)

    Bagby, L.; Johnson, M.; Lipton, R.; Gu, W.

    1995-11-01

    AC coupled silicon detectors, being used for the DO upgrade, may have substantial voltage across the coupling capacitor. Failed capacitors can present ∼50 V to the input of the SVX, Silicon Vertex, device. We measured the effects that failed detector coupling capacitors have on the SVXD (rad soft 3μm), SVXH (rad hard 1.2μm), and SVXIIb (rad soft 1.2μm) amplifier / readout devices. The test results show that neighboring channels saturate when an excessive voltage is applied directly to a SVX channel. We believe that the effects are due to current diffusion within the SVX substrate rather than surface currents on the detectors. This paper discusses the magnitude of the saturation and a possible solution to the problem

  15. Investigation of magnetism in aluminum-doped silicon carbide nanotubes

    Science.gov (United States)

    Behzad, Somayeh; Chegel, Raad

    2013-11-01

    The effect of aluminum doping on the structural, electronic and magnetic properties of (8,0) silicon carbide nanotube (SiCNT) is investigated using spin-polarized density functional theory. It is found from the calculation of the formation energies that aluminum substitution for silicon atom is preferred. Our results show that the magnetization depends on the substitutional site, aluminum substitution at silicon site does not introduce any spin-polarization, whereas the aluminum substitution for carbon atom yields a spin polarized, almost dispersionless π band within the original band gap.

  16. Performance of irradiated silicon microstrip detectors

    International Nuclear Information System (INIS)

    Catacchini, E.; Civinini, C.; D'Alessandro, R.; Focardi, E.; Lenzi, M.; Meschini, M.; Parrini, G.; Pieri, M.

    1999-01-01

    Silicon microstrip devices to be installed in Large Hadron Collider (LHC) tracking detectors will have to operate in a high radiation environment. We report on performance studies of silicon microstrip detectors irradiated with neutrons or protons, up to fluences comparable to the first ten years of running at LHC. Obtained results show that irradiated detectors can still be operated with satisfactory signal-to-noise ratio,and in the case of inhomogeneously type inverted detector a very good position resolution is achieved regardless of the zone crossed by the particle

  17. Silicon photomultiplier as a detector of Cherenkov photons

    International Nuclear Information System (INIS)

    Korpar, S.; Dolenec, R.; Hara, K.; Iijima, T.; Krizan, P.; Mazuka, Y.; Pestotnik, R.; Stanovnik, A.; Yamaoka, M.

    2008-01-01

    A novel photon detector-i.e. the silicon photomultiplier-whose main advantage over conventional photomultiplier tubes is the operation in high magnetic fields, has been tested as a photon detector in a proximity focusing RICH with aerogel radiator. This type of RICH counter is proposed for the upgrade of the Belle detector at the KEK B-factory. Recently produced silicon photomultipliers show less noise and have larger size, which are important issues for a large area photon detector. We measured the single photon pulse height distribution, the timing resolution and the position sensitivity for different silicon photomultipliers (Hamamatsu MPPC HC025, HC050, and HC100). The silicon photomultipliers were then used to detect Cherenkov photons emitted by cosmic ray particles in a proximity focusing aerogel RICH. Various light guides were investigated in order to increase the detection efficiency

  18. Formation and properties of porous silicon layers

    International Nuclear Information System (INIS)

    Vitanov, P.; Kamenova, M.; Dimova-Malinovska, D.

    1993-01-01

    Preparation, properties and application of porous silicon films are investigated. Porous silicon structures were formed by an electrochemical etching process resulting in selective dissolution of the silicon substrate. The silicon wafers used with a resistivity of 5-10Ω.cm were doped with B to concentrations 6x10 18 -1x10 19 Ω.cm -3 in the temperature region 950 o C-1050 o C. The density of each porous films was determined from the weight loss during the anodization and it depends on the surface resistivity of the Si wafer. The density decreases with decreasing of the surface resistivity. The surface of the porous silicon layers was studied by X-ray photoelectron spectroscopy which indicates the presence of SiF 4 . The kinetic dependence of the anode potential and the porous layer thickness on the time of anodization in a galvanostatic regime for the electrolytes with various HF concentration were studied. In order to compare the properties of the resulting porous layers and to establish the dependence of the porosity on the electrolyte, three types of electrolytes were used: concentrated HF, diluted HF:H 2 O=1:1 and ethanol-hydrofluoric solutions HF:C 2 H 5 OH:H 2 O=2:1:1. High quality uniform and reproducible layers were formed using aqueous-ethanol-hydrofluoric electrolyte. Both Kikuchi's line and ring patterns were observed by TEM. The porous silicon layer was single crystal with the same orientation as the substrate. The surface shows a polycrystalline structure only. The porous silicon layers exhibit visible photoluminescence (PL) at room temperature under 480 nm Ar + laser line excitation. The peak of PL was observed at about 730 nm with FWHM about 90 nm. Photodiodes was made with a W-porous silicon junction. The current voltage and capacity voltage characteristics were similar to those of an isotype heterojunction diode. (orig.)

  19. Process Development in the Preparation and Characterization of Silicon Alkoxide From Rice Husk

    International Nuclear Information System (INIS)

    Khin San Win; Toe Shein; Nyunt Wynn

    2011-12-01

    The preparation and characterization of silicon alkoxide (silicon isopropoxide) from rice husk char has been studied. In the investigation, four kinds of Myanmar paddies were chemically assayed. Analyses showed the silicon contend varies from 73-92% . Based on the silicon content, the process development in the production of silicon isopropoxide was carried out. In the process development, silicon isopropoxide with a yield of 44.21% was achieved by the direct reaction of isopropanol in situ by silicon tetrachloride, which was directly produced by the chlorination of rice husk char at the high temperature range of 900-1100 C. The novelity of the process was that, silicon isopropoxide was achieved in situ and not by using the old process, where generally isopropanol was reacted with silicon tetrachloride. The physiochemical properties of silicon isopropoxide was confirmed by conventional and modern techniques. In the investigation, the starting materials, silica in the reaction products were characterized, identified and confirmed by modren techniques. Silicon isopropoxide can be a sources of pore silica whereby silicon of 97-99% of purity can be achieved.

  20. CHARACTERIZATION OF THE ELECTROPHYSICAL PROPERTIES OF SILICON-SILICON DIOXIDE INTERFACE USING PROBE ELECTROMETRY METHODS

    Directory of Open Access Journals (Sweden)

    V. А. Pilipenko

    2017-01-01

    Full Text Available Introduction of submicron design standards into microelectronic industry and a decrease of the gate dielectric thickness raise the importance of the analysis of microinhomogeneities in the silicon-silicon dioxide system. However, there is very little to no information on practical implementation of probe electrometry methods, and particularly scanning Kelvin probe method, in the interoperational control of real semiconductor manufacturing process. The purpose of the study was the development of methods for nondestructive testing of semiconductor wafers based on the determination of electrophysical properties of the silicon-silicon dioxide interface and their spatial distribution over wafer’s surface using non-contact probe electrometry methods.Traditional C-V curve analysis and scanning Kelvin probe method were used to characterize silicon- silicon dioxide interface. The samples under testing were silicon wafers of KEF 4.5 and KDB 12 type (orientation <100>, diameter 100 mm.Probe electrometry results revealed uniform spatial distribution of wafer’s surface potential after its preliminary rapid thermal treatment. Silicon-silicon dioxide electric potential values were also higher after treatment than before it. This potential growth correlates with the drop in interface charge density. At the same time local changes in surface potential indicate changes in surface layer structure.Probe electrometry results qualitatively reflect changes of interface charge density in silicon-silicon dioxide structure during its technological treatment. Inhomogeneities of surface potential distribution reflect inhomogeneity of damaged layer thickness and can be used as a means for localization of interface treatment defects.

  1. Silicon in Imperata cylindrica (L.) P. Beauv: content, distribution, and ultrastructure.

    Science.gov (United States)

    Rufo, Lourdes; Franco, Alejandro; de la Fuente, Vicenta

    2014-07-01

    Silicon concentration, distribution, and ultrastructure of silicon deposits in the Poaceae Imperata cylindrica (L.) P. Beauv. have been studied. This grass, known for its medicinal uses and also for Fe hyperaccumulation and biomineralization capacities, showed a concentration of silicon of 13,705 ± 9,607 mg/kg dry weight. Silicon was found as an important constituent of cell walls of the epidermis of the whole plant. Silica deposits were found in silica bodies, endodermis, and different cells with silicon-collapsed lumen as bulliforms, cortical, and sclerenchyma cells. Transmission electron microscope observations of these deposits revealed an amorphous material of an ultrastructure similar to that previously reported in silica bodies of other Poaceae.

  2. Radiation damage in silicon detectors

    CERN Document Server

    Lindström, G

    2003-01-01

    Radiation damage effects in silicon detectors under severe hadron and gamma-irradiation are surveyed, focusing on bulk effects. Both macroscopic detector properties (reverse current, depletion voltage and charge collection) as also the underlying microscopic defect generation are covered. Basic results are taken from the work done in the CERN-RD48 (ROSE) collaboration updated by results of recent work. Preliminary studies on the use of dimerized float zone and Czochralski silicon as detector material show possible benefits. An essential progress in the understanding of the radiation-induced detector deterioration had recently been achieved in gamma irradiation, directly correlating defect analysis data with the macroscopic detector performance.

  3. Silicon microphotonic waveguides

    International Nuclear Information System (INIS)

    Ta'eed, V.; Steel, M.J.; Grillet, C.; Eggleton, B.; Du, J.; Glasscock, J.; Savvides, N.

    2004-01-01

    Full text: Silicon microphotonic devices have been drawing increasing attention in the past few years. The high index-difference between silicon and its oxide (Δn = 2) suggests a potential for high-density integration of optical functions on to a photonic chip. Additionally, it has been shown that silicon exhibits strong Raman nonlinearity, a necessary property as light interaction can occur only by means of nonlinearities in the propagation medium. The small dimensions of silicon waveguides require the design of efficient tapers to couple light to them. We have used the beam propagation method (RSoft BeamPROP) to understand the principles and design of an inverse-taper mode-converter as implemented in several recent papers. We report on progress in the design and fabrication of silicon-based waveguides. Preliminary work has been conducted by patterning silicon-on-insulator (SOI) wafers using optical lithography and reactive ion etching. Thus far, only rib waveguides have been designed, as single-mode ridge-waveguides are beyond the capabilities of conventional optical lithography. We have recently moved to electron beam lithography as the higher resolutions permitted will provide the flexibility to begin fabricating sub-micron waveguides

  4. Electrochemical characterization of carbon coated bundle-type silicon nanorod for anode material in lithium ion secondary batteries

    International Nuclear Information System (INIS)

    Halim, Martin; Kim, Jung Sub; Choi, Jeong-Gil; Lee, Joong Kee

    2015-01-01

    Highlights: • Bundle-type silicon nanorods (BSNR) were synthesized by metal assisted chemical etching. • Novel bundle-type nanorods electrode showed self-relaxant characteristics. • The self-relaxant property was enhanced by increasing the silver concentration. • PAA binder enhanced the self-relaxant property of the silicon material. • Carbon coated BSNR (BSNR@C) has evidently provided better cycle performance. - Abstract: Nanostructured silicon synthesis by surface modification of commercial micro-powder silicon was investigated in order to reduce the maximum volume change over cycle. The surface of micro-powder silicon was modified using an Ag metal-assisted chemical etching technique to produce nanostructured material in the form of bundle-type silicon nanorods. The volume change of the electrode using the nanostructured silicon during cycle was investigated using an in-situ dilatometer. Our result shows that nanostructured silicon synthesized using this method showed a self-relaxant characteristic as an anode material for lithium ion battery application. Moreover, binder selection plays a role in enhancing self-relaxant properties during delithiation via strong hydrogen interaction on the surface of the silicon material. The nanostructured silicon was then coated with carbon from propylene gas and showed higher capacity retention with the use of polyacrylic acid (PAA) binder. While the nano-size of the pore diameter control may significantly affect the capacity fading of nanostructured silicon, it can be mitigated via carbon coating, probably due to the prevention of Li ion penetration into 10 nano-meter sized pores

  5. Electrochemical characterization of carbon coated bundle-type silicon nanorod for anode material in lithium ion secondary batteries

    Energy Technology Data Exchange (ETDEWEB)

    Halim, Martin [Center for Energy Convergence, Korea Institute of Science and Technology, Hwarangno 14-gil 5, Seongbuk-gu, Seoul 136-791 (Korea, Republic of); Energy and Environmental Engineering, Korea University of Science and Technology, Gwahangno, Yuseong-gu, Daejeon, 305-333 (Korea, Republic of); Kim, Jung Sub [Center for Energy Convergence, Korea Institute of Science and Technology, Hwarangno 14-gil 5, Seongbuk-gu, Seoul 136-791 (Korea, Republic of); Department of Material Science & Engineering, Korea University, Seoul 136-713 (Korea, Republic of); Choi, Jeong-Gil [Department of Chemical Engineering, Hannam University, 461-1 Junmin-dong, Yusung-gu, Taejon 305-811 (Korea, Republic of); Lee, Joong Kee, E-mail: leejk@kist.re.kr [Center for Energy Convergence, Korea Institute of Science and Technology, Hwarangno 14-gil 5, Seongbuk-gu, Seoul 136-791 (Korea, Republic of); Energy and Environmental Engineering, Korea University of Science and Technology, Gwahangno, Yuseong-gu, Daejeon, 305-333 (Korea, Republic of)

    2015-04-15

    Highlights: • Bundle-type silicon nanorods (BSNR) were synthesized by metal assisted chemical etching. • Novel bundle-type nanorods electrode showed self-relaxant characteristics. • The self-relaxant property was enhanced by increasing the silver concentration. • PAA binder enhanced the self-relaxant property of the silicon material. • Carbon coated BSNR (BSNR@C) has evidently provided better cycle performance. - Abstract: Nanostructured silicon synthesis by surface modification of commercial micro-powder silicon was investigated in order to reduce the maximum volume change over cycle. The surface of micro-powder silicon was modified using an Ag metal-assisted chemical etching technique to produce nanostructured material in the form of bundle-type silicon nanorods. The volume change of the electrode using the nanostructured silicon during cycle was investigated using an in-situ dilatometer. Our result shows that nanostructured silicon synthesized using this method showed a self-relaxant characteristic as an anode material for lithium ion battery application. Moreover, binder selection plays a role in enhancing self-relaxant properties during delithiation via strong hydrogen interaction on the surface of the silicon material. The nanostructured silicon was then coated with carbon from propylene gas and showed higher capacity retention with the use of polyacrylic acid (PAA) binder. While the nano-size of the pore diameter control may significantly affect the capacity fading of nanostructured silicon, it can be mitigated via carbon coating, probably due to the prevention of Li ion penetration into 10 nano-meter sized pores.

  6. Cavity-assisted quantum computing in a silicon nanostructure

    International Nuclear Information System (INIS)

    Tang Bao; Qin Hao; Zhang Rong; Xue Peng; Liu Jin-Ming

    2014-01-01

    We present a scheme of quantum computing with charge qubits corresponding to one excess electron shared between dangling-bond pairs of surface silicon atoms that couple to a microwave stripline resonator on a chip. By choosing a certain evolution time, we propose the realization of a set of universal single- and two-qubit logical gates. Due to its intrinsic stability and scalability, the silicon dangling-bond charge qubit can be regarded as one of the most promising candidates for quantum computation. Compared to the previous schemes on quantum computing with silicon bulk systems, our scheme shows such advantages as a long coherent time and direct control and readout. (general)

  7. Rapid diffusion of molybdenum trace contamination in silicon

    International Nuclear Information System (INIS)

    Tobin, S.P.; Greenwald, A.C.; Wolfson, R.G.; Meier, D.L.; Drevinsky, P.J.

    1985-01-01

    Molybdenum contamination has been detected in silicon epitaxial layers and substrate wafers after processing in any one of several epitaxial silicon reactors. Greatly reduced minority carrier diffusion lengths and lifetimes are consistent with Mo concentrations measured by DLTS in the 10 12 and 10 13 cm -3 ranges. Depth profiling of diffusion length and the Mo deep level show much greater penetration than expected from previous reports of Mo as a slow diffuser. The data indicate a lower limit of 10 -8 cm 2 /sec for the diffusion coefficient of Mo in silicon at 1200 0 C, consistent with high diffusivities measured for other transition metals

  8. Surface chemistry of a hydrogenated mesoporous p-type silicon

    Energy Technology Data Exchange (ETDEWEB)

    Media, El-Mahdi, E-mail: belhadidz@tahoo.fr; Outemzabet, Ratiba, E-mail: oratiba@hotmail.com

    2017-02-15

    Highlights: • Due to its large specific surface porous silicon is used as substrate for drug therapy and biosensors. • We highlight the evidency of the contribution of the hydrides (SiHx) in the formation of the porous silicon. • The responsible species in the porous silicon formation are identified and quantified at different conditions. • By some chemical treatments we show that silicon surface can be turn from hydrophobic to hydrophilic. - Abstract: The finality of this work is devoted to the grafting of organic molecules on hydrogen passivated mesoporous silicon surfaces. The study would aid in the development for the formation of organic monolayers on silicon surface to be exploited for different applications such as the realisation of biosensors and medical devices. The basic material is silicon which has been first investigated by FTIR at atomistic plane during the anodic forward and backward polarization (i.e. “go” and “return”). For this study, we applied a numerical program based on least squares method to infrared absorbance spectra obtained by an in situ attenuated total reflection on p-type silicon in diluted HF electrolyte. Our numerical treatment is based on the fitting of the different bands of IR absorbance into Gaussians corresponding to the different modes of vibration of molecular groups such as siloxanes and hydrides. An adjustment of these absorbance bands is done systematically. The areas under the fitted bands permit one to follow the intensity of the different modes of vibration that exist during the anodic forward and backward polarization in order to compare the reversibility of the phenomenon of the anodic dissolution of silicon. It permits also to follow the evolution between the hydrogen silicon termination at forward and backward scanning applied potential. Finally a comparison between the states of the initial and final surface was carried out. We confirm the presence of clearly four and three distinct vibration modes

  9. The Effect of Polymer Char on Nitridation Kinetics of Silicon

    Science.gov (United States)

    Chan, Rickmond C.; Bhatt, Ramakrishna T.

    1994-01-01

    Effects of polymer char on nitridation kinetics of attrition milled silicon powder have been investigated from 1200 to 1350 C. Results indicate that at and above 1250 C, the silicon compacts containing 3.5 wt percent polymer char were fully converted to Si3N4 after 24 hr exposure in nitrogen. In contrast, the silicon compacts without polymer char could not be fully converted to Si3N4 at 1350 C under similar exposure conditions. At 1250 and 1350 C, the silicon compacts with polymer char showed faster nitridation kinetics than those without the polymer char. As the polymer char content is increased, the amount of SiC in the nitrided material is also increased. By adding small amounts (approx. 2.5 wt percent) of NiO, the silicon compacts containing polymer char can be completely nitrided at 1200 C. The probable mechanism for the accelerated nitridation of silicon containing polymer char is discussed.

  10. INFLUENCE OF THE SILICON INTERLAYER ON DIAMOND-LIKE CARBON FILMS DEPOSITED ON GLASS SUBSTRATES

    Directory of Open Access Journals (Sweden)

    Deiler Antonio Lima Oliveira

    2012-06-01

    Full Text Available Diamond-like carbon (DLC films as a hard protective coating have achieved great success in a diversity of technological applications. However, adhesion of DLC films to substrates can restrict their applications. The influence of a silicon interlayer in order to improve DLC adhesion on glass substrates was investigated. Amorphous silicon interlayer and DLC films were deposited using plasma enhanced chemical vapor deposition from silane and methane, respectively. The bonding structure, transmittance, refraction index, and adherence of the films were also evaluated regarding the thickness of the silicon interlayer. Raman scattering spectroscopy did not show any substantial difference in DLC structure due to the interlayer thickness of the silicon. Optical measurements showed a sharp decrease of transmittance in the ultra-violet region caused by the fundamental absorption of the light. In addition, the absorption edge of transmittance shifted toward longer wavelength side in the ultra-violet region as the thickness of the silicon interlayer increased. The tribological results showed an increase of DLC adherence as the silicon interlayer increased, which was characterized by less cracks around the grooves.

  11. Ceramic silicon-boron-carbon fibers from organic silicon-boron-polymers

    Science.gov (United States)

    Riccitiello, Salvatore R. (Inventor); Hsu, Ming-Ta S. (Inventor); Chen, Timothy S. (Inventor)

    1993-01-01

    Novel high strength ceramic fibers derived from boron, silicon, and carbon organic precursor polymers are discussed. The ceramic fibers are thermally stable up to and beyond 1200 C in air. The method of preparation of the boron-silicon-carbon fibers from a low oxygen content organosilicon boron precursor polymer of the general formula Si(R2)BR(sup 1) includes melt-spinning, crosslinking, and pyrolysis. Specifically, the crosslinked (or cured) precursor organic polymer fibers do not melt or deform during pyrolysis to form the silicon-boron-carbon ceramic fiber. These novel silicon-boron-carbon ceramic fibers are useful in high temperature applications because they retain tensile and other properties up to 1200 C, from 1200 to 1300 C, and in some cases higher than 1300 C.

  12. Using a colorimeter to develop an intrinsic silicone shade guide for facial prostheses.

    Science.gov (United States)

    Over, L M; Andres, C J; Moore, B K; Goodacre, C J; Muñoz, C A

    1998-12-01

    To determine if using CIE L*a*b* color measurements of white facial skin could be correlated to those of silicone shade samples that visually matched the skin. Secondly, to see if a correlation in color measurements could be achieved between the silicone shade samples and duplicated silicone samples made using a shade-guide color formula. A color booth was designed according to ASTM specifications, and painted using a Munsell Value 8 gray. A Minolta colorimeter was used to make facial skin measurements on 15 white adults. The skin color was duplicated using custom-shaded silicone samples. A 7-step wedge silicone shade guide was then fabricated, representing the commonly encountered thicknesses when fabricating facial prostheses. The silicone samples were then measured with the Minolta colorimeter. The readings were compared with the previous L*a*b* readings from the corresponding patient's skin measurements, and the relative color difference was then calculated. Silicone samples were fabricated and analyzed for three of the patients to determine if duplication of the visually matched silicone specimen was possible using the silicone color formula, and if the duplicates were visually and colorimetrically equivalent to each other. The color difference Delta E and chromaticity was calculated, and the data were analyzed using a coefficient-of-variation formula expressed by percent. A Pearson Product Moment Correlation Coefficient was performed to determine if a correlation existed between the skin and the silicone samples at the p 0), but only the 1-mm and 4-mm b* readings were very strong. Patient and silicone L*a*b* measurement results showed very little change in the a* axis, while the L* and b* measurements showed more change in their numbers, with changes in depth for all patient silicone samples. Delta E numbers indicated the lowest Delta E at the 1-mm depth and the highest Delta E at the 10-mm depth. All duplicated samples matched their original silicone samples

  13. High performance high-κ/metal gate complementary metal oxide semiconductor circuit element on flexible silicon

    KAUST Repository

    Sevilla, Galo T.

    2016-02-29

    Thinned silicon based complementary metal oxide semiconductor(CMOS)electronics can be physically flexible. To overcome challenges of limited thinning and damaging of devices originated from back grinding process, we show sequential reactive ion etching of silicon with the assistance from soft polymeric materials to efficiently achieve thinned (40 μm) and flexible (1.5 cm bending radius) silicon based functional CMOSinverters with high-κ/metal gate transistors. Notable advances through this study shows large area of silicon thinning with pre-fabricated high performance elements with ultra-large-scale-integration density (using 90 nm node technology) and then dicing of such large and thinned (seemingly fragile) pieces into smaller pieces using excimer laser. The impact of various mechanical bending and bending cycles show undeterred high performance of flexible siliconCMOSinverters. Future work will include transfer of diced silicon chips to destination site, interconnects, and packaging to obtain fully flexible electronic systems in CMOS compatible way.

  14. Silicon nanowire transistors

    CERN Document Server

    Bindal, Ahmet

    2016-01-01

    This book describes the n and p-channel Silicon Nanowire Transistor (SNT) designs with single and dual-work functions, emphasizing low static and dynamic power consumption. The authors describe a process flow for fabrication and generate SPICE models for building various digital and analog circuits. These include an SRAM, a baseband spread spectrum transmitter, a neuron cell and a Field Programmable Gate Array (FPGA) platform in the digital domain, as well as high bandwidth single-stage and operational amplifiers, RF communication circuits in the analog domain, in order to show this technology’s true potential for the next generation VLSI. Describes Silicon Nanowire (SNW) Transistors, as vertically constructed MOS n and p-channel transistors, with low static and dynamic power consumption and small layout footprint; Targets System-on-Chip (SoC) design, supporting very high transistor count (ULSI), minimal power consumption requiring inexpensive substrates for packaging; Enables fabrication of different types...

  15. Metal-like self-organization of periodic nanostructures on silicon and silicon carbide under femtosecond laser pulses

    International Nuclear Information System (INIS)

    Gemini, Laura; Hashida, Masaki; Shimizu, Masahiro; Miyasaka, Yasuhiro; Inoue, Shunsuke; Tokita, Shigeki; Sakabe, Shuji; Limpouch, Jiri; Mocek, Tomas

    2013-01-01

    Periodic structures were generated on Si and SiC surfaces by irradiation with femtosecond laser pulses. Self-organized structures with spatial periodicity of approximately 600 nm appear on silicon and silicon carbide in the laser fluence range just above the ablation threshold and upon irradiation with a large number of pulses. As in the case of metals, the dependence of the spatial periodicity on laser fluence can be explained by the parametric decay of laser light into surface plasma waves. The results show that the proposed model might be universally applicable to any solid state material

  16. Memory characteristics of silicon nitride with silicon nanocrystals as a charge trapping layer of nonvolatile memory devices

    International Nuclear Information System (INIS)

    Choi, Sangmoo; Yang, Hyundeok; Chang, Man; Baek, Sungkweon; Hwang, Hyunsang; Jeon, Sanghun; Kim, Juhyung; Kim, Chungwoo

    2005-01-01

    Silicon nitride with silicon nanocrystals formed by low-energy silicon plasma immersion ion implantation has been investigated as a charge trapping layer of a polycrystalline silicon-oxide-nitride-oxide-silicon-type nonvolatile memory device. Compared with the control sample without silicon nanocrystals, silicon nitride with silicon nanocrystals provides excellent memory characteristics, such as larger width of capacitance-voltage hysteresis, higher program/erase speed, and lower charge loss rate at elevated temperature. These improved memory characteristics are derived by incorporation of silicon nanocrystals into the charge trapping layer as additional accessible charge traps with a deeper effective trap energy level

  17. Achievement report for fiscal 1997. Technological development for practical application of a solar energy power generation system/development of technology to manufacture thin film solar cells/development of technology to manufacture low-cost large-area modules/development of technology to manufacture next generation thin film solar cells (development of technology to manufacture applied type thin film solar cells with new construction); 1997 nendo tiayoko hatsuden system jitsuyoka gijutsu kaihatsu. Usumaku taiyo denchi no seizo gijutsu kaihatsu, tei cost daimenseki module esizo gijutsu kaihatsu (jisedai usumaku taiyo denchi no seizo gijutsu kaihatsu, oyogata shinkozo usumaku taiyo denchi no seizo gijutsu kaihatsu)

    Energy Technology Data Exchange (ETDEWEB)

    NONE

    1998-03-01

    A thin film single crystal silicon solar cell module is developed, in which a porous silicon layer is formed on the surface of a long-sized single crystal silicon substrate, a single crystal silicon film is integrated on the layer by epitaxially growing the film thereon to form a solar cell, and the solar cell is peeled off from the silicon substrate and transferred to a plastic film substrate. The achievements during this fiscal year may be summarized as follows: simultaneous formation of a porous silicon layer on a silicon substrate, reduction of anode formation current density from 200 mA/cm{sup 2} to 10 mA/cm{sup 2}, development of a silicon epitaxial device using a carbon heater, and attainment of aperture conversion efficiency of 11.8% in a thin film single crystal silicon solar cell. Three kinds of methods were developed to peel off the solar cell. A method was developed to grind silicon substrate surface from which the solar cell has been peeled off. A technology was developed to obtain a long-sized silicon substrate of about 30 cm times 10 cm times 0.1 cm from a 4-inch silicon ingot by using a wire saw. (NEDO)

  18. A review of recent progress in heterogeneous silicon tandem solar cells

    Science.gov (United States)

    Yamaguchi, Masafumi; Lee, Kan-Hua; Araki, Kenji; Kojima, Nobuaki

    2018-04-01

    Silicon solar cells are the most established solar cell technology and are expected to dominate the market in the near future. As state-of-the-art silicon solar cells are approaching the Shockley-Queisser limit, stacking silicon solar cells with other photovoltaic materials to form multi-junction devices is an obvious pathway to further raise the efficiency. However, many challenges stand in the way of fully realizing the potential of silicon tandem solar cells because heterogeneously integrating silicon with other materials often degrades their qualities. Recently, above or near 30% silicon tandem solar cell has been demonstrated, showing the promise of achieving high-efficiency and low-cost solar cells via silicon tandem. This paper reviews the recent progress of integrating solar cell with other mainstream solar cell materials. The first part of this review focuses on the integration of silicon with III-V semiconductor solar cells, which is a long-researched topic since the emergence of III-V semiconductors. We will describe the main approaches—heteroepitaxy, wafer bonding and mechanical stacking—as well as other novel approaches. The second part introduces the integration of silicon with polycrystalline thin-film solar cells, mainly perovskites on silicon solar cells because of its rapid progress recently. We will also use an analytical model to compare the material qualities of different types of silicon tandem solar cells and project their practical efficiency limits.

  19. Project analysis and integration economic analyses summary

    Science.gov (United States)

    Macomber, H. L.

    1986-01-01

    An economic-analysis summary was presented for the manufacture of crystalline-silicon modules involving silicon ingot/sheet, growth, slicing, cell manufacture, and module assembly. Economic analyses provided: useful quantitative aspects for complex decision-making to the Flat-plate Solar Array (FSA) Project; yardsticks for design and performance to industry; and demonstration of how to evaluate and understand the worth of research and development both to JPL and other government agencies and programs. It was concluded that future research and development funds for photovoltaics must be provided by the Federal Government because the solar industry today does not reap enough profits from its present-day sales of photovoltaic equipment.

  20. Use of hydroxypropylmethylcellulose 2% for removing adherent silicone oil from silicone intraocular lenses

    OpenAIRE

    Wong , S Chien; Ramkissoon , Yashin D; Lopez , Mauricio; Page , Kristopher; Parkin , Ivan P; Sullivan , Paul M

    2009-01-01

    Abstract Background / aims: To investigate the effect of hydroxypropylmethylcellulose (HPMC) on the physical interaction (contact angle) between silicone oil and a silicone intraocular lens (IOL). Methods: In vitro experiments were performed, to determine the effect of HPMC (0.5%, 1% or 2%), with or without an additional simple mechanical manoeuvre, on the contact angle of silicone oil at the surface of both silicone and acrylic (control) IOLs. A balanced salt solu...

  1. Soft chemical synthesis of silicon nanosheets and their applications

    Energy Technology Data Exchange (ETDEWEB)

    Nakano, Hideyuki; Ikuno, Takashi [Toyota Central R& D Labs., Inc., 41-1 Yokomichi, Nagakute, Aichi 480-1192 (Japan)

    2016-12-15

    Two-dimensional silicon nanomaterials are expected to show different properties from those of bulk silicon materials by virtue of surface functionalization and quantum size effects. Since facile fabrication processes of large area silicon nanosheets (SiNSs) are required for practical applications, a development of soft chemical synthesis route without using conventional vacuum processes is a challenging issue. We have recently succeeded to prepare SiNSs with sub-nanometer thicknesses by exfoliating layered silicon compounds, and they are found to be composed of crystalline single-atom-thick silicon layers. In this review, we present the synthesis and modification methods of SiNSs. These SiNSs have atomically flat and smooth surfaces due to dense coverage of organic moieties, and they are easily self-assembled in a concentrated state to form a regularly stacked structure. We have also characterized the electron transport properties and the electronic structures of SiNSs. Finally, the potential applications of these SiNSs and organic modified SiNSs are also reviewed.

  2. Single-Event Effects in Silicon and Silicon Carbide Power Devices

    Science.gov (United States)

    Lauenstein, Jean-Marie; Casey, Megan C.; LaBel, Kenneth A.; Topper, Alyson D.; Wilcox, Edward P.; Kim, Hak; Phan, Anthony M.

    2014-01-01

    NASA Electronics Parts and Packaging program-funded activities over the past year on single-event effects in silicon and silicon carbide power devices are presented, with focus on SiC device failure signatures.

  3. Photovoltaic research and development in Japan

    Science.gov (United States)

    Shimada, K.

    1983-01-01

    The status of the Japanese photovoltaic (PV) R&D activities was surveyed through literature searches, private communications, and site visits in 1982. The results show that the Japanese photovoltaic technology is maturing rapidly, consistent with the steady government funding under the Sunshine Project. Two main thrusts of the Project are: (1) completion of the solar panel production pilot plants using cast ingot and sheet silicon materials, and (2) development of large area amorphous silicon solar cells with acceptable efficiency (10 to 12%). An experimental automated solar panel production plant rated at 500 kW/yr is currently under construction for the Sunshine Project for completion in March 1983. Efficiencies demonstrated by experimental large are amorphous silicon solar cells are approaching 8%. Small area amorphous silicon solar cells are, however, currently being mass produced and marketed by several companies at an equivalent annual rate of 2 MW/yr for consumer electronic applications. There is no evidence of an immediate move by the Japanese PV industry to enter extensively into the photovoltaic power market, domestic or otherwise. However, the photovoltaic technology itself could become ready for such an entry in the very near future, especially by making use of advanced process automation technologies.

  4. Porous Silicon Nanowires

    Science.gov (United States)

    Qu, Yongquan; Zhou, Hailong; Duan, Xiangfeng

    2011-01-01

    In this minreview, we summarize recent progress in the synthesis, properties and applications of a new type of one-dimensional nanostructures — single crystalline porous silicon nanowires. The growth of porous silicon nanowires starting from both p- and n-type Si wafers with a variety of dopant concentrations can be achieved through either one-step or two-step reactions. The mechanistic studies indicate the dopant concentration of Si wafers, oxidizer concentration, etching time and temperature can affect the morphology of the as-etched silicon nanowires. The porous silicon nanowires are both optically and electronically active and have been explored for potential applications in diverse areas including photocatalysis, lithium ion battery, gas sensor and drug delivery. PMID:21869999

  5. Formation of multiple levels of porous silicon for buried insulators and conductors in silicon device technologies

    Science.gov (United States)

    Blewer, Robert S.; Gullinger, Terry R.; Kelly, Michael J.; Tsao, Sylvia S.

    1991-01-01

    A method of forming a multiple level porous silicon substrate for semiconductor integrated circuits including anodizing non-porous silicon layers of a multi-layer silicon substrate to form multiple levels of porous silicon. At least one porous silicon layer is then oxidized to form an insulating layer and at least one other layer of porous silicon beneath the insulating layer is metallized to form a buried conductive layer. Preferably the insulating layer and conductive layer are separated by an anodization barrier formed of non-porous silicon. By etching through the anodization barrier and subsequently forming a metallized conductive layer, a fully or partially insulated buried conductor may be fabricated under single crystal silicon.

  6. Silicon: electrochemistry and luminescence

    NARCIS (Netherlands)

    Kooij, Ernst Stefan

    1997-01-01

    The electrochemistry of crystalline and porous silicon and the luminescence from porous silicon has been studied. One chapter deals with a model for the anodic dissolution of silicon in HF solution. In following chapters both the electrochemistry and various ways of generating visible

  7. Interaction between rare-earth ions and amorphous silicon nanoclusters produced at low processing temperatures

    Energy Technology Data Exchange (ETDEWEB)

    Meldrum, A. [Department of Physics, University of Alberta, Edmonton, T6G2J1 (Canada)]. E-mail: ameldrum@ualberta.ca; Hryciw, A. [Department of Physics, University of Alberta, Edmonton, T6G2J1 (Canada); MacDonald, A.N. [Department of Physics, University of Alberta, Edmonton, T6G2J1 (Canada); Blois, C. [Department of Physics, University of Alberta, Edmonton, T6G2J1 (Canada); Clement, T. [Department of Electrical and Computer Engineering, University of Alberta, Edmonton, T6G2V4 (Canada); De Corby, R. [Department of Electrical and Computer Engineering, University of Alberta, Edmonton, T6G2V4 (Canada); Wang, J. [Department of Physics, Chinese University of Hong Kong, Shatin, Hong Kong (China); Li Quan [Department of Physics, Chinese University of Hong Kong, Shatin, Hong Kong (China)

    2006-12-15

    Temperatures of 1000 deg. C and higher are a significant problem for the incorporation of erbium-doped silicon nanocrystal devices into standard silicon technology, and make the fabrication of contacts and reflectors in light emitting devices difficult. In the present work, we use energy-filtered TEM imaging techniques to show the formation of size-controlled amorphous silicon nanoclusters in SiO films annealed between 400 and 500 deg. C. The PL properties of such films are characteristic of amorphous silicon, and the spectrum can be controlled via a statistical size effect-as opposed to quantum confinement-that has previously been proposed for porous amorphous silicon. Finally, we show that amorphous nanoclusters sensitize the luminescence from the rare-earth ions Er, Nd, Yb, and Tm with excitation cross-sections similar in magnitude to erbium-doped silicon nanocrystal composites, and with a similar nonresonant energy transfer mechanism.

  8. Structural and elastic properties of porous silicon

    Energy Technology Data Exchange (ETDEWEB)

    Matthai, C C [Department of Physics and Astronomy, University of Wales College of Cardiff, Cardiff CF2 3YB (United Kingdom); Gavartin, J L [Department of Physics and Astronomy, University of Wales College of Cardiff, Cardiff CF2 3YB (United Kingdom); Cafolla, A A [Department of Physics, Dublin City University, Dublin (Ireland)

    1995-01-15

    We have implemented a modified diffusion-limited aggregation model to simulate the porous silicon structure obtained by electrochemical dissolution. The resulting fractal structures were fully equilibrated using the molecular dynamics method. An analysis of the relaxed structure shows it to be quite stable with the presence of one-, two- and three-coordinated atoms as well as the four-coordinated atoms found in bulk silicon. It is suggested that the different substructures or nanocrystals might be responsible for the observed photoluminescence. ((orig.))

  9. Research Progress about the Relationship between Nanoparticles Silicon Dioxide and Lung Cancer

    Directory of Open Access Journals (Sweden)

    Chun DAI

    2014-10-01

    Full Text Available Nano-silicon dioxide widely distributed in plastic, rubber, ceramics, paint, adhesives, and many other fields, and it is the product of coal combustion. A growing evidence shows that nano-silicon dioxide has certain correlation with respiratory system disease. In this paper, we synthesized existing researches of domestic and abroad, summarized the lung toxicity of nanoparticles. This article are reviewed from the physical and chemical properties of nanoparticles silicon dioxide, exposure conditions and environment, and the pathogenic mechanism of nano-silicon dioxide.

  10. A study on the effect of silicon content on mechanical properties

    International Nuclear Information System (INIS)

    Kwon, C.T.; Nam, T.W.; Lee, S.I.

    1978-01-01

    In Al-Si alloy, the variation of mechanical properties with silicon contents was investigated the silicon content being varied from 5% to 25%, and the effects of additives and refining elements were also studied. The results obtained are as follows: 1) Sodium treatment made the primary silicon crystals refined and spheroidized, and made the matrix structure intensified. The effect of P treatment on refining primary silicon crystals was greater then that of Na. 2) Tensile strength showed the maximum value at near the eutectic composition and was improved considerably by addition of Mg and treatment with Na. 3) The variation of matrix hardness with silicon contents was not perceptible and the hardness was improved by addition of Mg and treatment with Na. (author)

  11. Low cost Czochralski crystal growing technology. Near implementation of the flat plate photovoltaic cost reduction of the low cost solar array project

    Science.gov (United States)

    Roberts, E. G.

    1980-01-01

    Equipment developed for the manufacture of over 100 kg of silicon ingot from one crucible by rechanging from another crucible is described. Attempts were made to eliminate the cost of raising the furnace temperature to 250 C above the melting point of silicon by using an RF coil to melt polycrystalline silicon rod as a means of rechanging the crucible. Microprocessor control of the straight growth process was developed and domonstrated for both 4 inch and 6 inch diameter. Both meltdown and melt stabilization processes were achieved using operator prompting through the microprocessor. The use of the RF work coil in poly rod melting as a heat sink in the accelerated growth process was unsuccessful. The total design concept for fabrication and interfacing of the total cold crucible system was completed.

  12. Deformation mechanisms of silicon during nanoscratching

    Energy Technology Data Exchange (ETDEWEB)

    Gassilloud, R.; Gasser, P.; Buerki, G.; Michler, J. [EMPA, Materials Science and Technology, Feuerwerkerstrasse 39, 3602 Thun (Switzerland); Ballif, C. [University of Neuchatel, A.-L. Breguet 2, 2000 Neuchatel (Switzerland)

    2005-12-01

    The deformation mechanisms of silicon {l_brace}001{r_brace} surfaces during nanoscratching were found to depend strongly on the loading conditions. Nanoscratches with increasing load were performed at 2 {mu}m/s (low velocity) and 100 {mu}m/s (high velocity). The load-penetration-distance curves acquired during the scratching process at low velocity suggests that two deformation regimes can be defined, an elasto-plastic regime at low loads and a fully plastic regime at high loads. High resolution scanning electron microscopy of the damaged location shows that the residual scratch morphologies are strongly influenced by the scratch velocity and the applied load. Micro-Raman spectroscopy shows that after pressure release, the deformed volume inside the nanoscratch is mainly composed of amorphous silicon and Si-XII at low scratch speeds and of amorphous silicon at high speeds. Transmission electron microscopy shows that Si nanocrystals are embedded in an amorphous matrix at low speeds, whereas at high speeds the transformed zone is completely amorphous. Furthermore, the extend of the transformed zone is almost independent of the scratching speed and is delimited by a dislocation rich area that extends about as deep as the contact radius into the surface. To explain the observed phase and defect distribution a contact mechanics based decompression model that takes into account the load, the velocity, the materials properties and the contact radius in scratching is proposed. It shows that the decompression rate is higher at low penetration depth, which is consistent with the observation of amorphous silicon in this case. The stress field under the tip is computed using an elastic contact mechanics model based on Hertz's theory. The model explains the observed shape of the transformed zone and suggests that during load increase, phase transformation takes place prior to dislocation nucleation. (copyright 2005 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim) (orig.)

  13. VCSELs and silicon light sources exploiting SOI grating mirrors

    DEFF Research Database (Denmark)

    Chung, Il-Sug; Mørk, Jesper

    2012-01-01

    In this talk, novel vertical-cavity laser structure consisting of a dielectric Bragg reflector, a III-V active region, and a high-index-contrast grating made in the Si layer of a silicon-on-insulator (SOI) wafer will be presented. In the Si light source version of this laser structure, the SOI...... the Bragg reflector. Numerical simulations show that both the silicon light source and the VCSEL exploiting SOI grating mirrors have superior performances, compared to existing silicon light sources and long wavelength VCSELs. These devices are highly adequate for chip-level optical interconnects as well...

  14. Colloidal Photoluminescent Amorphous Porous Silicon, Methods Of Making Colloidal Photoluminescent Amorphous Porous Silicon, And Methods Of Using Colloidal Photoluminescent Amorphous Porous Silicon

    KAUST Repository

    Chaieb, Sahraoui

    2015-04-09

    Embodiments of the present disclosure provide for a colloidal photoluminescent amorphous porous silicon particle suspension, methods of making a colloidal photoluminescent amorphous porous silicon particle suspension, methods of using a colloidal photoluminescent amorphous porous silicon particle suspension, and the like.

  15. Colloidal Photoluminescent Amorphous Porous Silicon, Methods Of Making Colloidal Photoluminescent Amorphous Porous Silicon, And Methods Of Using Colloidal Photoluminescent Amorphous Porous Silicon

    KAUST Repository

    Chaieb, Saharoui; Mughal, Asad Jahangir

    2015-01-01

    Embodiments of the present disclosure provide for a colloidal photoluminescent amorphous porous silicon particle suspension, methods of making a colloidal photoluminescent amorphous porous silicon particle suspension, methods of using a colloidal photoluminescent amorphous porous silicon particle suspension, and the like.

  16. The effect of silicon crystallographic orientation on the formation of silicon nanoclusters during anodic electrochemical etching

    International Nuclear Information System (INIS)

    Timokhov, D. F.; Timokhov, F. P.

    2009-01-01

    Possible ways for increasing the photoluminescence quantum yield of porous silicon layers have been investigated. The effect of the anodization parameters on the photoluminescence properties for porous silicon layers formed on silicon substrates with different crystallographic orientations was studied. The average diameters for silicon nanoclusters are calculated from the photoluminescence spectra of porous silicon. The influence of the substrate crystallographic orientation on the photoluminescence quantum yield of porous silicon is revealed. A model explaining the effect of the substrate orientation on the photoluminescence properties for the porous silicon layers formed by anode electrochemical etching is proposed.

  17. On the use of silicon as thermal neutron filter

    International Nuclear Information System (INIS)

    Adib, M.; Habib, N.; Ashry, A.; Fathalla, M.

    2003-01-01

    A simple formula is given which allows to calculate the contribution of the total neutron cross-section including the Bragg scattering from different (hkl) planes to the neutron transmission through a solid crystalline silicon. The formula takes into account the silicon form of poly or mono crystals and its parameters. A computer program DSIC was developed to provide the required calculations. The calculated values of the total neutron cross-section of perfect silicon crystal at room and liquid nitrogen temperatures were compared with the experimental ones. The obtained agreement shows that the simple formula fits the experimental data with sufficient accuracy. A good agreement was also obtained between the calculated and measured values of polycrystalline silicon in the energy range from 5 eV to 500 μeV. The feasibility study on using a poly-crystalline silicon as a cold neutron filter and mono-crystalline as a thermal neutron one is given. The optimum crystal thickness, mosaic spread, temperature and cutting plane for efficiently transmitting the thermal reactor neutrons, while rejecting both fast neutrons and gamma rays accompanying the thermal ones for the mono crystalline silicon are also given

  18. On the use of silicon as thermal neutron filter

    Energy Technology Data Exchange (ETDEWEB)

    Adib, M.; Habib, N.; Ashry, A.; Fathalla, M. E-mail: mohamedfathalla@hotmail.com

    2003-12-01

    A simple formula is given which allows to calculate the contribution of the total neutron cross-section including the Bragg scattering from different (hkl) planes to the neutron transmission through a solid crystalline silicon. The formula takes into account the silicon form of poly or mono crystals and its parameters. A computer program DSIC was developed to provide the required calculations. The calculated values of the total neutron cross-section of perfect silicon crystal at room and liquid nitrogen temperatures were compared with the experimental ones. The obtained agreement shows that the simple formula fits the experimental data with sufficient accuracy. A good agreement was also obtained between the calculated and measured values of polycrystalline silicon in the energy range from 5 eV to 500 {mu}eV. The feasibility study on using a poly-crystalline silicon as a cold neutron filter and mono-crystalline as a thermal neutron one is given. The optimum crystal thickness, mosaic spread, temperature and cutting plane for efficiently transmitting the thermal reactor neutrons, while rejecting both fast neutrons and gamma rays accompanying the thermal ones for the mono crystalline silicon are also given.

  19. Type I Clathrates as Novel Silicon Anodes: An Electrochemical and Structural Investigation

    Science.gov (United States)

    Li, Ying; Raghavan, Rahul; Wagner, Nicholas A.; Davidowski, Stephen K.; Baggetto, Loïc; Zhao, Ran; Cheng, Qian; Yarger, Jeffery L.; Veith, Gabriel M.; Ellis‐Terrell, Carol; Miller, Michael A.; Chan, Kwai S.

    2015-01-01

    Silicon clathrates contain cage‐like structures that can encapsulate various guest atoms or molecules. An electrochemical evaluation of type I silicon clathrates based on Ba8AlySi46−y as the anode material for lithium‐ion batteries is presented here. Postcycling characterization with nuclear magnetic resonance and X‐ray diffraction shows no discernible structural or volume changes even after electrochemical insertion of 44 Li (≈1 Li/Si) into the clathrate structure. The observed properties are in stark contrast with lithiation of other silicon anodes, which become amorphous and suffer from large volume changes. The electrochemical reactions are proposed to occur as single phase reactions at approximately 0.2 and 0.4 V versus Li/Li+ during lithiation and delithiation, respectively, distinct from diamond cubic or amorphous silicon anodes. Reversible capacities as high as 499 mAh g−1 at a 5 mA g−1 rate were observed for silicon clathrate with composition Ba8Al8.54Si37.46, corresponding to ≈1.18 Li/Si. These results show that silicon clathrates could be promising durable anodes for lithium‐ion batteries. PMID:27980951

  20. Joining elements of silicon carbide

    International Nuclear Information System (INIS)

    Olson, B.A.

    1979-01-01

    A method of joining together at least two silicon carbide elements (e.g.in forming a heat exchanger) is described, comprising subjecting to sufficiently non-oxidizing atmosphere and sufficiently high temperature, material placed in space between the elements. The material consists of silicon carbide particles, carbon and/or a precursor of carbon, and silicon, such that it forms a joint joining together at least two silicon carbide elements. At least one of the elements may contain silicon. (author)

  1. Silicon fabric for multi-functional applications

    KAUST Repository

    Sevilla, Galo T.; Rojas, Jhonathan Prieto; Ahmed, Sally; Hussain, Aftab M.; Inayat, Salman Bin; Hussain, Muhammad Mustafa

    2013-01-01

    This paper reports a generic process flow to fabricate mechanically flexible and optically semi-transparent thermoelectric generators (TEGs), micro lithium-ion batteries (μLIB) and metal-oxide-semiconductor capacitors (MOSCAPs) on mono-crystalline silicon fabric platforms from standard bulk silicon (100) wafers. All the fabricated devices show outstanding mechanical flexibility and performance, making an important step towards monolithic integration of Energy Chip (self-powered devices) including energy harvesters and electronic devices on flexible platforms. We also report a recyclability process for the remaining bulk substrate after release, allowing us to achieve a low cost flexible platform for high performance applications. © 2013 IEEE.

  2. Silicon fabric for multi-functional applications

    KAUST Repository

    Sevilla, Galo T.

    2013-06-01

    This paper reports a generic process flow to fabricate mechanically flexible and optically semi-transparent thermoelectric generators (TEGs), micro lithium-ion batteries (μLIB) and metal-oxide-semiconductor capacitors (MOSCAPs) on mono-crystalline silicon fabric platforms from standard bulk silicon (100) wafers. All the fabricated devices show outstanding mechanical flexibility and performance, making an important step towards monolithic integration of Energy Chip (self-powered devices) including energy harvesters and electronic devices on flexible platforms. We also report a recyclability process for the remaining bulk substrate after release, allowing us to achieve a low cost flexible platform for high performance applications. © 2013 IEEE.

  3. Influence of transport mechanisms on nucleation and grain structure formation in DC cast aluminium alloy ingots

    Science.gov (United States)

    Bedel, M.; Založnik, M.; Kumar, A.; Combeau, H.; Jarry, P.; Waz, E.

    2012-01-01

    The grain structure formation in direct chill (DC) casting is directly linked to nucleation, which is generally promoted by inoculation. Inoculation prevents defects, but also modifies the physical properties by changing the microstructure. We studied the coupling of the nucleation on inoculant particles and the grain growth in the presence of melt flow induced by thermosolutal convection and of the transport of free-floating equiaxed grains. We used a volume-averaged two-phase multiscale model with a fully coupled description of phenomena on the grain scale (nucleation on grain refiner particles and grain growth) and on the product scale (macroscopic transport). The transport of inoculant particles is also modeled, which accounts for the inhomogeneous distribution of inoculant particles in the melt. The model was applied to an industrial sized (350mm thick) DC cast aluminium alloy ingot. A discretised nuclei size distribution was defined and the impact of different macroscopic phenomena on the grain structure formation was studied: the zone and intensity of nucleation and the resulting grain size distribution. It is shown that nucleation in the presence of macroscopic transport cannot be explained only in terms of cooling rate, but variations of composition, nuclei density and grain density, all affected by transport, must be accounted for.

  4. The intrinsic gettering in neutron irradiation Czochralski-silicon

    CERN Document Server

    Li Yang Xian; Niu Ping Juan; Liu Cai Chi; Xu Yue Sheng; Yang Deren; Que Duan Lin

    2002-01-01

    The intrinsic gettering in neutron irradiated Czochralski-silicon is studied. The result shows that a denuded zone at the surface of the neutron irradiated Czochralski-silicon wafer may be formed through one-step short-time annealing. The width of the denuded zone is dependent on the annealing temperature and the dose of neutron irradiation, while it is irrelated to the annealing time in case the denuded zone is formed. The authors conclude that the interaction between the defects induced by neutron irradiation and the oxygen in the silicon accelerates the oxygen precipitation in the bulk, and becomes the dominating factor of the quick formation of intrinsic gettering. It makes the effect of thermal history as the secondary factor

  5. Thermophysical Property Measurements of Silicon-Transition Metal Alloys

    Science.gov (United States)

    Banish, R. Michael; Erwin, William R.; Sansoucie, Michael P.; Lee, Jonghyun; Gave, Matthew A.

    2014-01-01

    Metals and metallic alloys often have high melting temperatures and highly reactive liquids. Processing reactive liquids in containers can result in significant contamination and limited undercooling. This is particularly true for molten silicon and it alloys. Silicon is commonly termed "the universal solvent". The viscosity, surface tension, and density of several silicon-transition metal alloys were determined using the Electrostatic Levitator system at the Marshall Space Flight Center. The temperature dependence of the viscosity followed an Arrhenius dependence, and the surface tension followed a linear temperature dependence. The density of the melts, including the undercooled region, showed a linear behavior as well. Viscosity and surface tension values were obtain for several of the alloys in the undercooled region.

  6. Silicon nanomaterials platform for bioimaging, biosensing, and cancer therapy.

    Science.gov (United States)

    Peng, Fei; Su, Yuanyuan; Zhong, Yiling; Fan, Chunhai; Lee, Shuit-Tong; He, Yao

    2014-02-18

    biomedical applications, including biosensor, bioimaging, and cancer therapy. First, we show that the interesting photoluminescence properties (e.g., strong fluorescence and robust photostability) and excellent biocompatibility of silicon nanoparticles (SiNPs) are superbly suitable for direct and long-term visualization of biological systems. The strongly fluorescent SiNPs are highly effective for bioimaging applications, especially for long-term cellular labeling, cancer cell detection, and tumor imaging in vitro and in vivo with high sensitivity. Next, we discuss the utilization of silicon nanomaterials to construct high-performance biosensors, such as silicon-based field-effect transistors (FET) and surface-enhanced Raman scattering (SERS) sensors, which hold great promise for ultrasensitive and selective detection of biological species (e.g., DNA and protein). Then, we introduce recent exciting research findings on the applications of silicon nanomaterials for cancer therapy with encouraging therapeutic outcomes. Lastly, we highlight the major challenges and promises in this field, and the prospect of a new nanobiotechnology platform based on silicon nanomaterials.

  7. Improvement in photovoltaic properties of silicon solar cells with a doped porous silicon layer with rare earth (Ce, La) as antireflection coatings

    International Nuclear Information System (INIS)

    Atyaoui, Malek; Dimassi, Wissem; Atyaoui, Atef; Elyagoubi, Jalel; Ouertani, Rachid; Ezzaouia, Hatem

    2013-01-01

    The performance improvement of solar cells due to the formation of a porous silicon layer treated with rare earth (Ce, La) in the n + emitter of silicon n + /p junctions has been investigated. The photovoltaic properties of the cells with and without treatment of the porous silicon layer are compared. From the reflection measurements, it was shown that the cells with treated PS layers have lower reflectivity value compared to cell with untreated PS layer. The main result is that the photovoltaic energy conversion efficiency of solar cells can be enhanced by using the treated porous silicon layers with the rare earth (Ce, La) as anti-reflection coatings. -- Highlights: • The reduction of optical loss in silicon (c-Si) solar cells attracts the attention of many researches to achieve high efficiencies. • To attain this aim, the treated PS layers with rare earth (La, Ce) are suggested to be used as an (ARC) of c-Si solar cell. • The result showed a decrease in the optical losses which can explain the improved photovoltaic properties

  8. Improvement in photovoltaic properties of silicon solar cells with a doped porous silicon layer with rare earth (Ce, La) as antireflection coatings

    Energy Technology Data Exchange (ETDEWEB)

    Atyaoui, Malek, E-mail: atyaoui.malek@yahoo.fr [Laboratoire de Photovoltaïque, Centre de recherches et des technologies de l' energie, technopole de Borj-Cédria, PB:95, Hammam Lif 2050 (Tunisia); Dimassi, Wissem [Laboratoire de Photovoltaïque, Centre de recherches et des technologies de l' energie, technopole de Borj-Cédria, PB:95,Hammam Lif 2050 (Tunisia); Atyaoui, Atef [Laboratoire de traitement des eaux usées, Centre de recherches et des technologies des eaux, technopole de Borj-Cédria, PB: 273, Soliman 8020 (Tunisia); Elyagoubi, Jalel; Ouertani, Rachid; Ezzaouia, Hatem [Laboratoire de Photovoltaïque, Centre de recherches et des technologies de l' energie, technopole de Borj-Cédria, PB:95,Hammam Lif 2050 (Tunisia)

    2013-09-15

    The performance improvement of solar cells due to the formation of a porous silicon layer treated with rare earth (Ce, La) in the n{sup +} emitter of silicon n{sup +}/p junctions has been investigated. The photovoltaic properties of the cells with and without treatment of the porous silicon layer are compared. From the reflection measurements, it was shown that the cells with treated PS layers have lower reflectivity value compared to cell with untreated PS layer. The main result is that the photovoltaic energy conversion efficiency of solar cells can be enhanced by using the treated porous silicon layers with the rare earth (Ce, La) as anti-reflection coatings. -- Highlights: • The reduction of optical loss in silicon (c-Si) solar cells attracts the attention of many researches to achieve high efficiencies. • To attain this aim, the treated PS layers with rare earth (La, Ce) are suggested to be used as an (ARC) of c-Si solar cell. • The result showed a decrease in the optical losses which can explain the improved photovoltaic properties.

  9. Graphitized silicon carbide microbeams: wafer-level, self-aligned graphene on silicon wafers

    International Nuclear Information System (INIS)

    Cunning, Benjamin V; Ahmed, Mohsin; Mishra, Neeraj; Kermany, Atieh Ranjbar; Iacopi, Francesca; Wood, Barry

    2014-01-01

    Currently proven methods that are used to obtain devices with high-quality graphene on silicon wafers involve the transfer of graphene flakes from a growth substrate, resulting in fundamental limitations for large-scale device fabrication. Moreover, the complex three-dimensional structures of interest for microelectromechanical and nanoelectromechanical systems are hardly compatible with such transfer processes. Here, we introduce a methodology for obtaining thousands of microbeams, made of graphitized silicon carbide on silicon, through a site-selective and wafer-scale approach. A Ni-Cu alloy catalyst mediates a self-aligned graphitization on prepatterned SiC microstructures at a temperature that is compatible with silicon technologies. The graphene nanocoating leads to a dramatically enhanced electrical conductivity, which elevates this approach to an ideal method for the replacement of conductive metal films in silicon carbide-based MEMS and NEMS devices. (paper)

  10. Heterogeneous integration of lithium niobate and silicon nitride waveguides for wafer-scale photonic integrated circuits on silicon.

    Science.gov (United States)

    Chang, Lin; Pfeiffer, Martin H P; Volet, Nicolas; Zervas, Michael; Peters, Jon D; Manganelli, Costanza L; Stanton, Eric J; Li, Yifei; Kippenberg, Tobias J; Bowers, John E

    2017-02-15

    An ideal photonic integrated circuit for nonlinear photonic applications requires high optical nonlinearities and low loss. This work demonstrates a heterogeneous platform by bonding lithium niobate (LN) thin films onto a silicon nitride (Si3N4) waveguide layer on silicon. It not only provides large second- and third-order nonlinear coefficients, but also shows low propagation loss in both the Si3N4 and the LN-Si3N4 waveguides. The tapers enable low-loss-mode transitions between these two waveguides. This platform is essential for various on-chip applications, e.g., modulators, frequency conversions, and quantum communications.

  11. The influence of diffusion of fluorine compounds for silicon lateral etching

    Energy Technology Data Exchange (ETDEWEB)

    Verdonck, Patrick; Goodyear, Alec; Braithwaite, Nicholas St.John

    2004-07-01

    In an earlier study, it was proposed that long-range surface transport of fluorine atoms could precede the eventual binding to a silicon atom. The rate of binding increases if the silicon is bombarded with high energy ions. In this study, the lateral etching of a silicon layer, sandwiched between two silicon dioxide layers, was studied in order to investigate and extend these hypotheses. The under etching of the silicon layer was higher for wafers which suffered ion bombardment, showing that this mechanism is important even for horizontal etching. At the same time, the thickness of the silicon layer was varied. In all cases, the thinner silicon layer etched much faster then the thicker layer, indicating that fluorine surface transport is much more important than re-emission for these processes. The etch rate increase with ion bombardment can be explained by the fact that part of the energy of the incoming ions is transferred to the fluorine compounds which are on the horizontal surfaces and that ion bombardment enhances the fluorine surface transport.

  12. Electrochemical Fabrication of Nanostructures on Porous Silicon for Biochemical Sensing Platforms.

    Science.gov (United States)

    Ko, Euna; Hwang, Joonki; Kim, Ji Hye; Lee, Joo Heon; Lee, Sung Hwan; Tran, Van-Khue; Chung, Woo Sung; Park, Chan Ho; Choo, Jaebum; Seong, Gi Hun

    2016-01-01

    We present a method for the electrochemical patterning of gold nanoparticles (AuNPs) or silver nanoparticles (AgNPs) on porous silicon, and explore their applications in: (1) the quantitative analysis of hydroxylamine as a chemical sensing electrode and (2) as a highly sensitive surface-enhanced Raman spectroscopy (SERS) substrate for Rhodamine 6G. For hydroxylamine detection, AuNPs-porous silicon can enhance the electrochemical oxidation of hydroxylamine. The current changed linearly for concentrations ranging from 100 μM to 1.32 mM (R(2) = 0.995), and the detection limit was determined to be as low as 55 μM. When used as SERS substrates, these materials also showed that nanoparticles decorated on porous silicon substrates have more SERS hot spots than those decorated on crystalline silicon substrates, resulting in a larger SERS signal. Moreover, AgNPs-porous silicon provided five-times higher signal compared to AuNPs-porous silicon. From these results, we expect that nanoparticles decorated on porous silicon substrates can be used in various types of biochemical sensing platforms.

  13. Use of porous silicon to minimize oxidation induced stacking fault defects in silicon

    International Nuclear Information System (INIS)

    Shieh, S.Y.; Evans, J.W.

    1992-01-01

    This paper presents methods for minimizing stacking fault defects, generated during oxidation of silicon, include damaging the back of the wafer or depositing poly-silicon on the back. In either case a highly defective structure is created and this is capable of gettering either self-interstitials or impurities which promote nucleation of stacking fault defects. A novel method of minimizing these defects is to form a patch of porous silicon on the back of the wafer by electrochemical etching. Annealing under inert gas prior to oxidation may then result in the necessary gettering. Experiments were carried out in which wafers were subjected to this treatment. Subsequent to oxidation, the wafers were etched to remove oxide and reveal defects. The regions of the wafer adjacent to the porous silicon patch were defect-free, whereas remote regions had defects. Deep level transient spectroscopy has been used to examine the gettering capability of porous silicon, and the paper discusses the mechanism by which the porous silicon getters

  14. Tailorable stimulated Brillouin scattering in nanoscale silicon waveguides.

    Science.gov (United States)

    Shin, Heedeuk; Qiu, Wenjun; Jarecki, Robert; Cox, Jonathan A; Olsson, Roy H; Starbuck, Andrew; Wang, Zheng; Rakich, Peter T

    2013-01-01

    Nanoscale modal confinement is known to radically enhance the effect of intrinsic Kerr and Raman nonlinearities within nanophotonic silicon waveguides. By contrast, stimulated Brillouin-scattering nonlinearities, which involve coherent coupling between guided photon and phonon modes, are stifled in conventional nanophotonics, preventing the realization of a host of Brillouin-based signal-processing technologies in silicon. Here we demonstrate stimulated Brillouin scattering in silicon waveguides, for the first time, through a new class of hybrid photonic-phononic waveguides. Tailorable travelling-wave forward-stimulated Brillouin scattering is realized-with over 1,000 times larger nonlinearity than reported in previous systems-yielding strong Brillouin coupling to phonons from 1 to 18 GHz. Experiments show that radiation pressures, produced by subwavelength modal confinement, yield enhancement of Brillouin nonlinearity beyond those of material nonlinearity alone. In addition, such enhanced and wideband coherent phonon emission paves the way towards the hybridization of silicon photonics, microelectromechanical systems and CMOS signal-processing technologies on chip.

  15. Tailorable stimulated Brillouin scattering in nanoscale silicon waveguides

    Science.gov (United States)

    Shin, Heedeuk; Qiu, Wenjun; Jarecki, Robert; Cox, Jonathan A.; Olsson, Roy H.; Starbuck, Andrew; Wang, Zheng; Rakich, Peter T.

    2013-01-01

    Nanoscale modal confinement is known to radically enhance the effect of intrinsic Kerr and Raman nonlinearities within nanophotonic silicon waveguides. By contrast, stimulated Brillouin-scattering nonlinearities, which involve coherent coupling between guided photon and phonon modes, are stifled in conventional nanophotonics, preventing the realization of a host of Brillouin-based signal-processing technologies in silicon. Here we demonstrate stimulated Brillouin scattering in silicon waveguides, for the first time, through a new class of hybrid photonic–phononic waveguides. Tailorable travelling-wave forward-stimulated Brillouin scattering is realized—with over 1,000 times larger nonlinearity than reported in previous systems—yielding strong Brillouin coupling to phonons from 1 to 18 GHz. Experiments show that radiation pressures, produced by subwavelength modal confinement, yield enhancement of Brillouin nonlinearity beyond those of material nonlinearity alone. In addition, such enhanced and wideband coherent phonon emission paves the way towards the hybridization of silicon photonics, microelectromechanical systems and CMOS signal-processing technologies on chip. PMID:23739586

  16. Optoelectronic properties of Black-Silicon generated through inductively coupled plasma (ICP) processing for crystalline silicon solar cells

    Energy Technology Data Exchange (ETDEWEB)

    Hirsch, Jens, E-mail: J.Hirsch@emw.hs-anhalt.de [Anhalt University of Applied Sciences, Faculty EMW, Bernburger Str. 55, DE-06366 Köthen (Germany); Fraunhofer Center for Silicon Photovoltaics CSP, Otto-Eißfeldt-Str. 12, DE-06120 Halle (Saale) (Germany); Gaudig, Maria; Bernhard, Norbert [Anhalt University of Applied Sciences, Faculty EMW, Bernburger Str. 55, DE-06366 Köthen (Germany); Lausch, Dominik [Fraunhofer Center for Silicon Photovoltaics CSP, Otto-Eißfeldt-Str. 12, DE-06120 Halle (Saale) (Germany)

    2016-06-30

    Highlights: • Fabrication of black silicon through inductively coupled plasma (ICP) processing. • Suppressed formation a self-bias and therefore a reduced ion bombardment of the silicon sample. • Reduction of the average hemispherical reflection between 300 and 1120 nm up to 8% within 5 min ICP process time. • Reflection is almost independent of the angle of incidence up to 60°. • 2.5 ms effective lifetime at 10{sup 15} cm{sup −3} MCD after ALD Al{sub 2}O{sub 3} surface passivation. - Abstract: The optoelectronic properties of maskless inductively coupled plasma (ICP) generated black silicon through SF{sub 6} and O{sub 2} are analyzed by using reflection measurements, scanning electron microscopy (SEM) and quasi steady state photoconductivity (QSSPC). The results are discussed and compared to capacitively coupled plasma (CCP) and industrial standard wet chemical textures. The ICP process forms parabolic like surface structures in a scale of 500 nm. This surface structure reduces the average hemispherical reflection between 300 and 1120 nm up to 8%. Additionally, the ICP texture shows a weak increase of the hemispherical reflection under tilted angles of incidence up to 60°. Furthermore, we report that the ICP process is independent of the crystal orientation and the surface roughness. This allows the texturing of monocrystalline, multicrystalline and kerf-less wafers using the same parameter set. The ICP generation of black silicon does not apply a self-bias on the silicon sample. Therefore, the silicon sample is exposed to a reduced ion bombardment, which reduces the plasma induced surface damage. This leads to an enhancement of the effective charge carrier lifetime up to 2.5 ms at 10{sup 15} cm{sup −3} minority carrier density (MCD) after an atomic layer deposition (ALD) with Al{sub 2}O{sub 3}. Since excellent etch results were obtained already after 4 min process time, we conclude that the ICP generation of black silicon is a promising technique

  17. Highly featured amorphous silicon nanorod arrays for high-performance lithium-ion batteries

    International Nuclear Information System (INIS)

    Soleimani-Amiri, Samaneh; Safiabadi Tali, Seied Ali; Azimi, Soheil; Sanaee, Zeinab; Mohajerzadeh, Shamsoddin

    2014-01-01

    High aspect-ratio vertical structures of amorphous silicon have been realized using hydrogen-assisted low-density plasma reactive ion etching. Amorphous silicon layers with the thicknesses ranging from 0.5 to 10 μm were deposited using radio frequency plasma enhanced chemical vapor deposition technique. Standard photolithography and nanosphere colloidal lithography were employed to realize ultra-small features of the amorphous silicon. The performance of the patterned amorphous silicon structures as a lithium-ion battery electrode was investigated using galvanostatic charge-discharge tests. The patterned structures showed a superior Li-ion battery performance compared to planar amorphous silicon. Such structures are suitable for high current Li-ion battery applications such as electric vehicles

  18. Highly featured amorphous silicon nanorod arrays for high-performance lithium-ion batteries

    Energy Technology Data Exchange (ETDEWEB)

    Soleimani-Amiri, Samaneh; Safiabadi Tali, Seied Ali; Azimi, Soheil; Sanaee, Zeinab; Mohajerzadeh, Shamsoddin, E-mail: mohajer@ut.ac.ir [Thin Film and Nanoelectronics Lab, Nanoelectronics Center of Excellence, School of Electrical and Computer Engineering, University of Tehran, Tehran 143957131 (Iran, Islamic Republic of)

    2014-11-10

    High aspect-ratio vertical structures of amorphous silicon have been realized using hydrogen-assisted low-density plasma reactive ion etching. Amorphous silicon layers with the thicknesses ranging from 0.5 to 10 μm were deposited using radio frequency plasma enhanced chemical vapor deposition technique. Standard photolithography and nanosphere colloidal lithography were employed to realize ultra-small features of the amorphous silicon. The performance of the patterned amorphous silicon structures as a lithium-ion battery electrode was investigated using galvanostatic charge-discharge tests. The patterned structures showed a superior Li-ion battery performance compared to planar amorphous silicon. Such structures are suitable for high current Li-ion battery applications such as electric vehicles.

  19. Indentation fatigue in silicon nitride, alumina and silicon carbide ...

    Indian Academy of Sciences (India)

    Repeated indentation fatigue (RIF) experiments conducted on the same spot of different structural ceramics viz. a hot pressed silicon nitride (HPSN), sintered alumina of two different grain sizes viz. 1 m and 25 m, and a sintered silicon carbide (SSiC) are reported. The RIF experiments were conducted using a Vicker's ...

  20. Silicon web process development

    Science.gov (United States)

    Duncan, C. S.; Seidensticker, R. G.; Mchugh, J. P.; Skutch, M. E.; Driggers, J. M.; Hopkins, R. H.

    1981-01-01

    The silicon web process takes advantage of natural crystallographic stabilizing forces to grow long, thin single crystal ribbons directly from liquid silicon. The ribbon, or web, is formed by the solidification of a liquid film supported by surface tension between two silicon filaments, called dendrites, which border the edges of the growing strip. The ribbon can be propagated indefinitely by replenishing the liquid silicon as it is transformed to crystal. The dendritic web process has several advantages for achieving low cost, high efficiency solar cells. These advantages are discussed.

  1. Characterization of silicon oxynitride films prepared by the simultaneous implantation of oxygen and nitrogen ions into silicon

    International Nuclear Information System (INIS)

    Hezel, R.; Streb, W.

    1985-01-01

    Silicon oxynitride films about 5 nm in thickness were prepared by simultaneously implanting 5 keV oxygen and nitrogen ions into silicon at room temperature up to saturation. These films with concentrations ranging from pure silicon oxide to silicon nitride were characterized using Auger electron spectroscopy, electron energy loss spectroscopy and depth-concentration profiling. The different behaviour of the silicon oxynitride films compared with those of silicon oxide and silicon nitride with regard to thermal stability and hardness against electron and argon ion irradiation is pointed out. (Auth.)

  2. Ultra-high-speed Optical Signal Processing using Silicon Photonics

    DEFF Research Database (Denmark)

    Oxenløwe, Leif Katsuo; Ji, Hua; Jensen, Asger Sellerup

    with a photonic layer on top to interconnect them. For such systems, silicon is an attractive candidate enabling both electronic and photonic control. For some network scenarios, it may be beneficial to use optical on-chip packet switching, and for high data-density environments one may take advantage...... of the ultra-fast nonlinear response of silicon photonic waveguides. These chips offer ultra-broadband wavelength operation, ultra-high timing resolution and ultra-fast response, and when used appropriately offer energy-efficient switching. In this presentation we review some all-optical functionalities based...... on silicon photonics. In particular we use nano-engineered silicon waveguides (nanowires) [1] enabling efficient phasematched four-wave mixing (FWM), cross-phase modulation (XPM) or self-phase modulation (SPM) for ultra-high-speed optical signal processing of ultra-high bit rate serial data signals. We show...

  3. Geochemistry of the stable isotopes of silicon

    Energy Technology Data Exchange (ETDEWEB)

    Douthitt, C B [California Inst. of Tech., Pasadena (USA). Div. of Geological and Planetary Sciences

    1982-08-01

    One hundred thirty two new measurements of the relative abundances of the stable isotopes of silicon in terrestrial materials are presented. The total variation of delta/sup 30/Si found is 6.2 parts per thousand, centered on the mean of terrestrial mafic and ultramafic igneous rocks, delta/sup 30/Si = -0.4 parts per thousand. Igneous rocks show limited variation; coexisting minerals exhibit small, systematic silicon isotopic fractionations that are roughly 1/3 the magnitude of concomitant oxygen isotopic fractionations at 1150/sup 0/C. In both igneous minerals and rocks, delta/sup 30/Si shows a positive correlation with silicon content, as does delta/sup 18/O. Opal from both sponge spicules and sinters is light, with delta/sup 30/Si = -2.3 and -1.4 parts per thousand respectively. Large delta/sup 30/Si values of both positive and negative sign are reported for the first time from clay minerals, opaline phytoliths, and authigenic quartz. All highly fractionated samples were precipitated from solution at low temperatures; however, aqueous silicon is not measurably fractionated relative to quartz at equilibrium. A kinetic isotope fractionation of approximately 3.5 parts per thousand is postulated to occur during the low temperature precipitation of opal and, possibly, poorly ordered phyllosilicates, with the silicate phase being enriched in /sup 28/Si. This fractionation, coupled with a Rayleigh precipitation model, is capable of explaining most non-magmatic delta/sup 30/Si variations.

  4. Silicon germanium mask for deep silicon etching

    KAUST Repository

    Serry, Mohamed

    2014-07-29

    Polycrystalline silicon germanium (SiGe) can offer excellent etch selectivity to silicon during cryogenic deep reactive ion etching in an SF.sub.6/O.sub.2 plasma. Etch selectivity of over 800:1 (Si:SiGe) may be achieved at etch temperatures from -80 degrees Celsius to -140 degrees Celsius. High aspect ratio structures with high resolution may be patterned into Si substrates using SiGe as a hard mask layer for construction of microelectromechanical systems (MEMS) devices and semiconductor devices.

  5. Silicon germanium mask for deep silicon etching

    KAUST Repository

    Serry, Mohamed; Rubin, Andrew; Refaat, Mohamed; Sedky, Sherif; Abdo, Mohammad

    2014-01-01

    Polycrystalline silicon germanium (SiGe) can offer excellent etch selectivity to silicon during cryogenic deep reactive ion etching in an SF.sub.6/O.sub.2 plasma. Etch selectivity of over 800:1 (Si:SiGe) may be achieved at etch temperatures from -80 degrees Celsius to -140 degrees Celsius. High aspect ratio structures with high resolution may be patterned into Si substrates using SiGe as a hard mask layer for construction of microelectromechanical systems (MEMS) devices and semiconductor devices.

  6. Evanescent field phase shifting in a silicon nitride waveguide using a coupled silicon slab

    DEFF Research Database (Denmark)

    Jensen, Asger Sellerup; Oxenløwe, Leif Katsuo; Green, William M. J.

    2015-01-01

    An approach for electrical modulation of low-loss silicon nitride waveguides is proposed, using a silicon nitride waveguide evanescently loaded with a thin silicon slab. The thermooptic phase-shift characteristics are investigated in a racetrack resonator configuration....

  7. Selective formation of porous silicon

    Science.gov (United States)

    Fathauer, Robert W. (Inventor); Jones, Eric W. (Inventor)

    1993-01-01

    A pattern of porous silicon is produced in the surface of a silicon substrate by forming a pattern of crystal defects in said surface, preferably by applying an ion milling beam through openings in a photoresist layer to the surface, and then exposing said surface to a stain etchant, such as HF:HNO3:H2O. The defected crystal will preferentially etch to form a pattern of porous silicon. When the amorphous content of the porous silicon exceeds 70 percent, the porous silicon pattern emits visible light at room temperature.

  8. Ethanol-water separation by pervaporation using silicone and polyvinyl alcohol membranes

    Directory of Open Access Journals (Sweden)

    Chinchiw, S.

    2006-09-01

    Full Text Available In this research, experiments were carried out to investigate the effects of operating parameters onthe pervaporation performance for the separation of ethanol-water solutions. Composite silicone membranessupported on polysulfone prepared with varied silicone contents and commercial polyvinyl alcohol (Pervap®2211, Sulzer membranes were used. The results showed that the composite silicone/polysulfone membranescoated with 3 wt% of silicone exhibited highest permeation flux with slightly lower separation factor forethanol. Furthermore, it was found that the composite silicone/polysulfone membranes were suitable for theseparation of ethanol from a dilute ethanol solutions. Both the separation factor and permeation flux of the composite membranes increased with increasing temperature and feed concentration. A membrane coated with a 7 wt% silicone gave highest separation factor of 7.32 and permeation flux of 0.44 kg/m2h at 5 wt% ethanol feed concentration and feed temperature of 70ºC. For polyvinyl alcohol membranes, the results showed that the membranes were suitable for the dehydration of concentrated ethanol solutions. The permeation flux increased and the separation factor for water decreased with increasing water feed concentration and temperature. The membrane gave highest separation factor of 248 and permeation flux of 0.02 kg/m2h at 5 wt% water feed concentration and feed temperature of 30ºC.

  9. Modulation Doping of Silicon using Aluminium-induced Acceptor States in Silicon Dioxide

    OpenAIRE

    K?nig, Dirk; Hiller, Daniel; Gutsch, Sebastian; Zacharias, Margit; Smith, Sean

    2017-01-01

    All electronic, optoelectronic or photovoltaic applications of silicon depend on controlling majority charge carriers via doping with impurity atoms. Nanoscale silicon is omnipresent in fundamental research (quantum dots, nanowires) but also approached in future technology nodes of the microelectronics industry. In general, silicon nanovolumes, irrespective of their intended purpose, suffer from effects that impede conventional doping due to fundamental physical principles such as out-diffusi...

  10. STM-excited luminescence of porous and spark-processed silicon

    International Nuclear Information System (INIS)

    Andrienko, I.; Kuznetsov, V.; Yuan, J.; Haneman, D.

    1998-01-01

    Full text: Scanning tunneling microscopy (STM) permits highly local electronic excitation of light emission (LE) from the surface of silicon. Measuring STM LE, one can study simultaneously both the topography and the luminescence properties of areas down to nm dimensions and thus make conclusions about the luminescence mechanism of the material. We have built an STM spectroscopy system which allows measurement of spectra of visible light emitted from areas as small as 13 x 13 nm 2 (porous silicon) and 10 x 10 nm 2 (spark-processed silicon). Porous silicon shows a broad emission band centered at 630 nm, and spark-processed silicon, one at 690 nm. The STM LE spectra of spark-processed silicon obtained for the first time. We have found that visible light is emitted only from areas containing nanometer-scale structures down to around 2 nm in diameter. STM LE occurs under negative bias voltage applied to the tip, i.e. when electrons are injected into the sample. Other workers used p-type silicon for the sample preparations, but it has been found that STM LE can be induced also from n-type silicon. Furthermore, we have shown that STM LE spectra can be resolved using much lover voltages and tunneling currents: -(7-9) V and 25 - 50 nA vs -(25-50) V and 100 nA. To consider different excitation mechanisms, the STM LE measurements are compared with photoluminescence and electroluminescence spectra of similar samples. We suggest that excitation of individual quantum confinement structures has been observed

  11. Optical property of silicon quantum dots embedded in silicon nitride by thermal annealing

    Energy Technology Data Exchange (ETDEWEB)

    Kim, Baek Hyun, E-mail: bhkim@andrew.cmu.ed [Department of Materials Science and Engineering, Carnegie Mellon University, Pittsburgh, PA 15213, United Sates (United States); Davis, Robert F. [Department of Materials Science and Engineering, Carnegie Mellon University, Pittsburgh, PA 15213, United Sates (United States); Park, Seong-Ju [Nanophotonic Semiconductors Laboratory, Department of Materials Science and Engineering, Gwangju Institute of Science and Technology, Gwangju, 500-712 (Korea, Republic of)

    2010-01-01

    We present the effects on the thermal annealing of silicon quantum dots (Si QDs) embedded in silicon nitride. The improved photoluminescence (PL) intensities and the red-shifted PL spectra were obtained with annealing treatment in the range of 700 to 1000 {sup o}C. The shifts of PL spectra were attributed to the increase in the size of Si QDs. The improvement of the PL intensities was also attributed to the reduction of point defects at Si QD/silicon nitride interface and in the silicon nitride due to hydrogen passivation effects.

  12. Silicon photonics fundamentals and devices

    CERN Document Server

    Deen, M Jamal

    2012-01-01

    The creation of affordable high speed optical communications using standard semiconductor manufacturing technology is a principal aim of silicon photonics research. This would involve replacing copper connections with optical fibres or waveguides, and electrons with photons. With applications such as telecommunications and information processing, light detection, spectroscopy, holography and robotics, silicon photonics has the potential to revolutionise electronic-only systems. Providing an overview of the physics, technology and device operation of photonic devices using exclusively silicon and related alloys, the book includes: * Basic Properties of Silicon * Quantum Wells, Wires, Dots and Superlattices * Absorption Processes in Semiconductors * Light Emitters in Silicon * Photodetectors , Photodiodes and Phototransistors * Raman Lasers including Raman Scattering * Guided Lightwaves * Planar Waveguide Devices * Fabrication Techniques and Material Systems Silicon Photonics: Fundamentals and Devices outlines ...

  13. Fabrication and Modification of Nanoporous Silicon Particles

    Science.gov (United States)

    Ferrari, Mauro; Liu, Xuewu

    2010-01-01

    Silicon-based nanoporous particles as biodegradable drug carriers are advantageous in permeation, controlled release, and targeting. The use of biodegradable nanoporous silicon and silicon dioxide, with proper surface treatments, allows sustained drug release within the target site over a period of days, or even weeks, due to selective surface coating. A variety of surface treatment protocols are available for silicon-based particles to be stabilized, functionalized, or modified as required. Coated polyethylene glycol (PEG) chains showed the effective depression of both plasma protein adsorption and cell attachment to the modified surfaces, as well as the advantage of long circulating. Porous silicon particles are micromachined by lithography. Compared to the synthesis route of the nanomaterials, the advantages include: (1) the capability to make different shapes, not only spherical particles but also square, rectangular, or ellipse cross sections, etc.; (2) the capability for very precise dimension control; (3) the capacity for porosity and pore profile control; and (4) allowance of complex surface modification. The particle patterns as small as 60 nm can be fabricated using the state-of-the-art photolithography. The pores in silicon can be fabricated by exposing the silicon in an HF/ethanol solution and then subjecting the pores to an electrical current. The size and shape of the pores inside silicon can be adjusted by the doping of the silicon, electrical current application, the composition of the electrolyte solution, and etching time. The surface of the silicon particles can be modified by many means to provide targeted delivery and on-site permanence for extended release. Multiple active agents can be co-loaded into the particles. Because the surface modification of particles can be done on wafers before the mechanical release, asymmetrical surface modification is feasible. Starting from silicon wafers, a treatment, such as KOH dipping or reactive ion

  14. Twenty-fold plasmon-induced enhancement of radiative emission rate in silicon nanocrystals embedded in silicon dioxide

    International Nuclear Information System (INIS)

    Gardelis, S; Gianneta, V.; Nassiopoulou, A.G

    2016-01-01

    We report on a 20-fold enhancement of the integrated photoluminescence (PL) emission of silicon nanocrystals, embedded in a matrix of silicon dioxide, induced by excited surface plasmons from silver nanoparticles, which are located in the vicinity of the silicon nanocrystals and separated from them by a silicon dioxide layer of a few nanometers. The electric field enhancement provided by the excited surface plasmons increases the absorption cross section and the emission rate of the nearby silicon nanocrystals, resulting in the observed enhancement of the photoluminescence, mainly attributed to a 20-fold enhancement in the emission rate of the silicon nanocrystals. The observed remarkable improvement of the PL emission makes silicon nanocrystals very useful material for photonic, sensor and solar cell applications.

  15. Luminescence and optical absorption determination in porous silicon

    International Nuclear Information System (INIS)

    Nogal, U.; Calderon, A.; Marin, E.; Rojas T, J. B.; Juarez, A. G.

    2012-10-01

    We applied the photoacoustic spectroscopy technique in order to obtain the optical absorption spectrum in porous silicon samples prepared by electrochemical anodic etching on n-type, phosphorous doped, (100)-oriented crystal-line silicon wafer with thickness of 300 μm and 1-5 ωcm resistivity. The porous layers were prepared with etching times of 13, 20, 30, 40 and 60 minutes. Also, we realized a comparison among the optical absorption spectrum with the photoluminescence and photo reflectance ones, both obtained at room temperature. Our results show that the absorption spectrum of the samples of porous silicon depends notably of the etching time an it consist of two distinguishable absorption bands, one in the Vis region and the other one in the UV region. (Author)

  16. Lighting emitting microstructures in porous silicon

    International Nuclear Information System (INIS)

    Squire, E.

    1999-01-01

    Experimental and theoretical techniques are used to examine microstructuring effects on the optical properties of single layer, multilayer, single and multiple microcavity structures fabricated from porous silicon. Two important issues regarding the effects of the periodic structuring of this material are discussed. Firstly, the precise role played by this microstructuring, given that the luminescence is distributed throughout the entire structure and the low porosity layers are highly absorbing at short wavelengths. The second issue examined concerns the observed effects on the optical spectra of the samples owing to the emission bandwidth of the material being greater than the optical stopband of the structure. Measurements of the reflectivity and photoluminescence spectra of different porous silicon microstructures are presented and discussed. The results are modelled using a transfer matrix technique. The matrix method has been modified to calculate the optical spectra of porous silicon specifically by accounting for the effects of dispersion, absorption and emission within the material. Layer thickness and porosity gradients have also been included in the model. The dielectric function of the two component layers (i.e. silicon and air) is calculated using the Looyenga formula. This approach can be adapted to suit other porous semiconductors if required. Examination of the experimental results have shown that the emitted light is strongly controlled by the optical modes of the structures. Furthermore, the data display an interplay of a wide variety of effects dependent upon the structural composition. Comparisons made between the experimental and calculated reflectivity and photoluminescence spectra of many different porous silicon microstructures show very good agreement. (author)

  17. CMOS compatible generic batch process towards flexible memory on bulk monocrystalline silicon (100)

    KAUST Repository

    Ghoneim, Mohamed T.

    2014-12-01

    Today\\'s mainstream flexible electronics research is geared towards replacing silicon either totally, by having organic devices on organic substrates, or partially, by transferring inorganic devices onto organic substrates. In this work, we present a pragmatic approach combining the desired flexibility of organic substrates and the ultra-high integration density, inherent in silicon semiconductor industry, to transform bulk/inflexible silicon into an ultra-thin mono-crystalline fabric. We also show the effectiveness of this approach in achieving fully flexible electronic systems. Furthermore, we provide a progress report on fabricating various memory devices on flexible silicon fabric and insights for completely flexible memory modules on silicon fabric.

  18. CMOS compatible generic batch process towards flexible memory on bulk monocrystalline silicon (100)

    KAUST Repository

    Ghoneim, Mohamed T.; Rojas, Jhonathan Prieto; Kutbee, Arwa T.; Hanna, Amir; Hussain, Muhammad Mustafa

    2014-01-01

    Today's mainstream flexible electronics research is geared towards replacing silicon either totally, by having organic devices on organic substrates, or partially, by transferring inorganic devices onto organic substrates. In this work, we present a pragmatic approach combining the desired flexibility of organic substrates and the ultra-high integration density, inherent in silicon semiconductor industry, to transform bulk/inflexible silicon into an ultra-thin mono-crystalline fabric. We also show the effectiveness of this approach in achieving fully flexible electronic systems. Furthermore, we provide a progress report on fabricating various memory devices on flexible silicon fabric and insights for completely flexible memory modules on silicon fabric.

  19. Optical modelling of thin-film silicon solar cells deposited on textured substrates

    International Nuclear Information System (INIS)

    Krc, J.; Zeman, M.; Smole, F.; Topic, M.

    2004-01-01

    Optical modelling is used to investigate effects of light scattering in amorphous silicon and microcrystalline silicon solar cells. The role of enhanced haze parameter and different angular distribution function of scattered light is analyzed. Results of optical simulation show that enhanced haze parameter compared to that of Asahi U-type SnO 2 :F does not improve external quantum efficiency and short-circuit current density of amorphous silicon solar cell significantly, whereas for microcrystalline silicon solar cell the improvement is larger. Angular distribution function affects the external quantum efficiency and the short-circuit current density significantly

  20. Direct Production of Silicones From Sand

    Energy Technology Data Exchange (ETDEWEB)

    Larry N. Lewis; F.J. Schattenmann: J.P. Lemmon

    2001-09-30

    Silicon, in the form of silica and silicates, is the second most abundant element in the earth's crust. However the synthesis of silicones (scheme 1) and almost all organosilicon chemistry is only accessible through elemental silicon. Silicon dioxide (sand or quartz) is converted to chemical-grade elemental silicon in an energy intensive reduction process, a result of the exceptional thermodynamic stability of silica. Then, the silicon is reacted with methyl chloride to give a mixture of methylchlorosilanes catalyzed by cooper containing a variety of tract metals such as tin, zinc etc. The so-called direct process was first discovered at GE in 1940. The methylchlorosilanes are distilled to purify and separate the major reaction components, the most important of which is dimethyldichlorosilane. Polymerization of dimethyldichlorosilane by controlled hydrolysis results in the formation of silicone polymers. Worldwide, the silicones industry produces about 1.3 billion pounds of the basic silicon polymer, polydimethylsiloxane.

  1. Effect of UV irradiations on the structural and optical features of porous silicon: application in silicon solar cells

    International Nuclear Information System (INIS)

    Aouida, S.; Saadoun, M.; Boujmil, M.F.; Ben Rabha, M.; Bessaies, B.

    2004-01-01

    The aim of this paper is to investigate the structural and optical stability of porous silicon layers (PSLs) planned to be used in silicon solar cells technology. The PSLs were prepared by a HNO 3 /HF vapor etching (VE) based method. Fourier transform infrared (FT-IR) spectroscopy shows that fresh VE-based PSLs contain N-H and Si-F bonds related to a ammonium hexafluorosilicate (NH 4 ) 2 SiF 6 minor phase, and conventional Si-H x and Si-O x bonds. Free air exposures of PSLs without and with UV irradiation lead to oxidation or photo-oxidation of the porous layer, respectively. FT-IR characterisation of the PSLs shows that UV irradiations modify the transformation kinetics replacing instable Si-H x by Si-O x or Si-O-H bonds. When fresh PSLs undergo free air oxidation within 7 days, the surface reflectivity decreases from 10 to about 8%, while it drops to about 4% when a 10 min free air UV irradiation is applied. Long periods of free air oxidation do not ensure the reflectivity to be stable, whereas it becomes stable after only 10 min of UV irradiation. This behaviour was explained taking into account the kinetic differences between oxidation with and without UV irradiation. Fresh VE-based PSLs were found to improve efficiently the photovoltaic (PV) characteristics of crystalline silicon solar cells. The passivating action of VE-based PSLs was discussed. An improvement of the PV performances was observed solely for stable oxidized porous silicon (PS) structures obtained from UV irradiations

  2. Subwavelength silicon photonics

    International Nuclear Information System (INIS)

    Cheben, P.; Bock, P.J.; Schmid, J.H.; Lapointe, J.; Janz, S.; Xu, D.-X.; Densmore, A.; Delage, A.; Lamontagne, B.; Florjanczyk, M.; Ma, R.

    2011-01-01

    With the goal of developing photonic components that are compatible with silicon microelectronic integrated circuits, silicon photonics has been the subject of intense research activity. Silicon is an excellent material for confining and manipulating light at the submicrometer scale. Silicon optoelectronic integrated devices have the potential to be miniaturized and mass-produced at affordable cost for many applications, including telecommunications, optical interconnects, medical screening, and biological and chemical sensing. We review recent advances in silicon photonics research at the National Research Council Canada. A new type of optical waveguide is presented, exploiting subwavelength grating (SWG) effect. We demonstrate subwavelength grating waveguides made of silicon, including practical components operating at telecom wavelengths: input couplers, waveguide crossings and spectrometer chips. SWG technique avoids loss and wavelength resonances due to diffraction effects and allows for single-mode operation with direct control of the mode confinement by changing the refractive index of a waveguide core over a range as broad as 1.6 - 3.5 simply by lithographic patterning. The light can be launched to these waveguides with a coupling loss as small as 0.5 dB and with minimal wavelength dependence, using coupling structures similar to that shown in Fig. 1. The subwavelength grating waveguides can cross each other with minimal loss and negligible crosstalk which allows massive photonic circuit connectivity to overcome the limits of electrical interconnects. These results suggest that the SWG waveguides could become key elements for future integrated photonic circuits. (authors)

  3. Silicon photonic integration in telecommunications

    Directory of Open Access Journals (Sweden)

    Christopher Richard Doerr

    2015-08-01

    Full Text Available Silicon photonics is the guiding of light in a planar arrangement of silicon-based materials to perform various functions. We focus here on the use of silicon photonics to create transmitters and receivers for fiber-optic telecommunications. As the need to squeeze more transmission into a given bandwidth, a given footprint, and a given cost increases, silicon photonics makes more and more economic sense.

  4. Silicon microphones - a Danish perspective

    DEFF Research Database (Denmark)

    Bouwstra, Siebe; Storgaard-Larsen, Torben; Scheeper, Patrick

    1998-01-01

    Two application areas of microphones are discussed, those for precision measurement and those for hearing instruments. Silicon microphones are under investigation for both areas, and Danish industry plays a key role in both. The opportunities of silicon, as well as the challenges and expectations......, are discussed. For precision measurement the challenge for silicon is large, while for hearing instruments silicon seems to be very promising....

  5. Nanocrystalline Silicon Carrier Collectors for Silicon Heterojunction Solar Cells and Impact on Low-Temperature Device Characteristics

    KAUST Repository

    Nogay, Gizem

    2016-09-26

    Silicon heterojunction solar cells typically use stacks of hydrogenated intrinsic/doped amorphous silicon layers as carrier selective contacts. However, the use of these layers may cause parasitic optical absorption losses and moderate fill factor (FF) values due to a high contact resistivity. In this study, we show that the replacement of doped amorphous silicon with nanocrystalline silicon is beneficial for device performance. Optically, we observe an improved short-circuit current density when these layers are applied to the front side of the device. Electrically, we observe a lower contact resistivity, as well as higher FF. Importantly, our cell parameter analysis, performed in a temperature range from -100 to +80 °C, reveals that the use of hole-collecting p-type nanocrystalline layer suppresses the carrier transport barrier, maintaining FF s in the range of 70% at -100 °C, whereas it drops to 40% for standard amorphous doped layers. The same analysis also reveals a saturation onset of the open-circuit voltage at -100 °C using doped nanocrystalline layers, compared with saturation onset at -60 °C for doped amorphous layers. These findings hint at a reduced importance of the parasitic Schottky barrier at the interface between the transparent electrodes and the selective contact in the case of nanocrystalline layer implementation. © 2011-2012 IEEE.

  6. Nanocrystalline Silicon Carrier Collectors for Silicon Heterojunction Solar Cells and Impact on Low-Temperature Device Characteristics

    KAUST Repository

    Nogay, Gizem; Seif, Johannes Peter; Riesen, Yannick; Tomasi, Andrea; Jeangros, Quentin; Wyrsch, Nicolas; Haug, Franz-Josef; De Wolf, Stefaan; Ballif, Christophe

    2016-01-01

    Silicon heterojunction solar cells typically use stacks of hydrogenated intrinsic/doped amorphous silicon layers as carrier selective contacts. However, the use of these layers may cause parasitic optical absorption losses and moderate fill factor (FF) values due to a high contact resistivity. In this study, we show that the replacement of doped amorphous silicon with nanocrystalline silicon is beneficial for device performance. Optically, we observe an improved short-circuit current density when these layers are applied to the front side of the device. Electrically, we observe a lower contact resistivity, as well as higher FF. Importantly, our cell parameter analysis, performed in a temperature range from -100 to +80 °C, reveals that the use of hole-collecting p-type nanocrystalline layer suppresses the carrier transport barrier, maintaining FF s in the range of 70% at -100 °C, whereas it drops to 40% for standard amorphous doped layers. The same analysis also reveals a saturation onset of the open-circuit voltage at -100 °C using doped nanocrystalline layers, compared with saturation onset at -60 °C for doped amorphous layers. These findings hint at a reduced importance of the parasitic Schottky barrier at the interface between the transparent electrodes and the selective contact in the case of nanocrystalline layer implementation. © 2011-2012 IEEE.

  7. Characterization of nanostructured CuO-porous silicon matrixformed on copper coated silicon substrate via electrochemical etching

    International Nuclear Information System (INIS)

    Naddaf, M.; Mrad, O.; Al-Zier, A.

    2015-01-01

    A pulsed anodic etching method has been utilized for nanostructuring of a copper-coated p-type (100) silicon substrate, using HF-based solution as electrolyte. Scanning electron microscopy reveals the formation of a nanostructured matrix that consists of island-like textures with nanosize grains grown onto fiber-like columnar structures separated with etch pits of grooved porous structures. Spatial micro-Raman scattering analysis indicates that the island-like texture is composed of single-phase cupric oxide (CuO) nanocrystals, while the grooved porous structure is barely related to formation of porous silicon (PS). X-ray diffraction shows that both the grown CuO nanostructures and the etched silicon layer have the same preferred (220) orientation. Chemical composition obtained by means of X-ray photoelectron spectroscopic (XPS) analysis confirms the presence of the single-phase CuO on the surface of the patterned CuO-PS matrix. As compared to PS formed on the bare silicon substrate, the room-temperature photoluminescence (PL) from the CuO-PS matrix exhibits an additional weak (blue) PL band as well as a blue shift in the PL band of PS (S-band). This has been revealed from XPS analysis to be associated with the enhancement in the SiO2 content as well as formation of the carbonyl group on the surface in the case of the CuO-PS matrix.(author)

  8. Characterization of Ag-porous silicon nanostructured layer formed by an electrochemical etching of p-type silicon surface for bio-application

    Science.gov (United States)

    Naddaf, M.; Al-Mariri, A.; Haj-Mhmoud, N.

    2017-06-01

    Nanostructured layers composed of silver-porous silicon (Ag-PS) have been formed by an electrochemical etching of p-type (1 1 1) silicon substrate in a AgNO3:HF:C2H5OH solution at different etching times (10 min-30 min). Scanning electron microscopy (SEM) and energy-dispersive x-ray spectroscopy (EDS) results reveal that the produced layers consist of Ag dendrites and a silicon-rich porous structure. The nanostructuring nature of the layer has been confirmed by spatial micro-Raman scattering and x-ray diffraction techniques. The Ag dendrites exhibit a surface-enhanced Raman scattering (SERS) spectrum, while the porous structure shows a typical PS Raman spectrum. Upon increasing the etching time, the average size of silicon nanocrystallite in the PS network decreases, while the average size of Ag nanocrystals is slightly affected. In addition, the immobilization of prokaryote Salmonella typhimurium DNA via physical adsorption onto the Ag-PS layer has been performed to demonstrate its efficiency as a platform for detection of biological molecules using SERS.

  9. Integrated silicon optoelectronics

    CERN Document Server

    Zimmermann, Horst

    2000-01-01

    'Integrated Silicon Optoelectronics'assembles optoelectronics and microelectronics The book concentrates on silicon as the major basis of modern semiconductor devices and circuits Starting from the basics of optical emission and absorption and from the device physics of photodetectors, the aspects of the integration of photodetectors in modern bipolar, CMOS, and BiCMOS technologies are discussed Detailed descriptions of fabrication technologies and applications of optoelectronic integrated circuits are included The book, furthermore, contains a review of the state of research on eagerly expected silicon light emitters In order to cover the topic of the book comprehensively, integrated waveguides, gratings, and optoelectronic power devices are included in addition Numerous elaborate illustrations promote an easy comprehension 'Integrated Silicon Optoelectronics'will be of value to engineers, physicists, and scientists in industry and at universities The book is also recommendable for graduate students speciali...

  10. Process for making silicon

    Science.gov (United States)

    Levin, Harry (Inventor)

    1987-01-01

    A reactor apparatus (10) adapted for continuously producing molten, solar grade purity elemental silicon by thermal reaction of a suitable precursor gas, such as silane (SiH.sub.4), is disclosed. The reactor apparatus (10) includes an elongated reactor body (32) having graphite or carbon walls which are heated to a temperature exceeding the melting temperature of silicon. The precursor gas enters the reactor body (32) through an efficiently cooled inlet tube assembly (22) and a relatively thin carbon or graphite septum (44). The septum (44), being in contact on one side with the cooled inlet (22) and the heated interior of the reactor (32) on the other side, provides a sharp temperature gradient for the precursor gas entering the reactor (32) and renders the operation of the inlet tube assembly (22) substantially free of clogging. The precursor gas flows in the reactor (32) in a substantially smooth, substantially axial manner. Liquid silicon formed in the initial stages of the thermal reaction reacts with the graphite or carbon walls to provide a silicon carbide coating on the walls. The silicon carbide coated reactor is highly adapted for prolonged use for production of highly pure solar grade silicon. Liquid silicon (20) produced in the reactor apparatus (10) may be used directly in a Czochralski or other crystal shaping equipment.

  11. Silicon etch process

    International Nuclear Information System (INIS)

    Day, D.J.; White, J.C.

    1984-01-01

    A silicon etch process wherein an area of silicon crystal surface is passivated by radiation damage and non-planar structure produced by subsequent anisotropic etching. The surface may be passivated by exposure to an energetic particle flux - for example an ion beam from an arsenic, boron, phosphorus, silicon or hydrogen source, or an electron beam. Radiation damage may be used for pattern definition and/or as an etch stop. Ethylenediamine pyrocatechol or aqueous potassium hydroxide anisotropic etchants may be used. The radiation damage may be removed after etching by thermal annealing. (author)

  12. Porous silicon gettering

    Energy Technology Data Exchange (ETDEWEB)

    Tsuo, Y.S.; Menna, P.; Pitts, J.R. [National Renewable Energy Lab., Golden, CO (United States)] [and others

    1996-05-01

    The authors have studied a novel extrinsic gettering method that uses the large surface areas produced by a porous-silicon etch as gettering sites. The annealing step of the gettering used a high-flux solar furnace. They found that a high density of photons during annealing enhanced the impurity diffusion to the gettering sites. The authors used metallurgical-grade Si (MG-Si) prepared by directional solidification casing as the starting material. They propose to use porous-silicon-gettered MG-Si as a low-cost epitaxial substrate for polycrystalline silicon thin-film growth.

  13. Monitoring of the Irradiated Neutron Fluence in the Neutron Transmutation Doping Process of Hanaro

    Science.gov (United States)

    Kim, Myong-Seop; Park, Sang-Jun

    2009-08-01

    Neutron transmutation doping (NTD) for silicon is a process of the creation of phosphorus impurities in intrinsic or extrinsic silicon by neutron irradiation to obtain silicon semiconductors with extremely uniform dopant distribution. HANARO has two vertical holes for the NTD, and the irradiation for 5 and 6 inch silicon ingots has been going on at one hole. In order to achieve the accurate neutron fluence corresponding to the target resistivity, the real time neutron flux is monitored by self-powered neutron detectors. After irradiation, the total irradiation fluence is confirmed by measuring the absolute activity of activation detectors. In this work, a neutron fluence monitoring method using zirconium foils with the mass of 10 ~ 50 mg was applied to the NTD process of HANARO. We determined the proportional constant of the relationship between the resistivity of the irradiated silicon and the neutron fluence determined by using zirconium foils. The determined constant for the initially n-type silicon was 3.126 × 1019 n·Ω/cm. It was confirmed that the difference between this empirical value and the theoretical one was only 0.5%. Conclusively, the practical methodology to perform the neutron transmutation doping of silicon was established.

  14. Investigation of the interface region between a porous silicon layer and a silicon substrate

    International Nuclear Information System (INIS)

    Lee, Ki-Won; Park, Dae-Kyu; Kim, Young-You; Shin, Hyun-Joon

    2005-01-01

    Atomic force microscopy (AFM) measurement and X-ray diffraction (XRD) analysis were performed to investigate the physical and structural characteristics of the interface region between a porous silicon layer and a silicon substrate. We discovered that, when anodization time was increased under a constant current density, the Si crystallites in the interface region became larger and formed different lattice parameters than observed in the porous silicon layer. Secondary ion mass spectrometry (SIMS) analysis also revealed that the Si was more concentrated in the interface region than in the porous silicon layer. These results were interpreted by the deficiency of the HF solution in reaching to the interface through the pores during the porous silicon formation

  15. The geochemistry of the stable isotopes of silicon

    International Nuclear Information System (INIS)

    Douthitt, C.B.

    1982-01-01

    One hundred thirty two new measurements of the relative abundances of the stable isotopes of silicon in terrestrial materials are presented. The total variation of delta 30 Si found is 6.2 parts per thousand, centered on the mean of terrestrial mafic and ultramafic igneous rocks, delta 30 Si = -0.4 parts per thousand. Igneous rocks show limited variation; coexisting minerals exhibit small, systematic silicon isotopic fractionations that are roughly 1/3 the magnitude of concomitant oxygen isotopic fractionations at 1150 0 C. In both igneous minerals and rocks, delta 30 Si shows a positive correlation with silicon content, as does delta 18 O. Opal from both sponge spicules and sinters is light, with delta 30 Si = -2.3 and -1.4 parts per thousand respectively. Large delta 30 Si values of both positive and negative sign are reported for the first time from clay minerals, opaline phytoliths, and authigenic quartz. All highly fractionated samples were precipitated from solution at low temperatures; however, aqueous silicon is not measurably fractionated relative to quartz at equilibrium. A kinetic isotope fractionation of approximately 3.5 parts per thousand is postulated to occur during the low temperature precipitation of opal and, possibly, poorly ordered phyllosilicates, with the silicate phase being enriched in 28 Si. This fractionation, coupled with a Rayleigh precipitation model, is capable of explaining most non-magmatic delta 30 Si variations. (author)

  16. Vapor Pressure and Evaporation Coefficient of Silicon Monoxide over a Mixture of Silicon and Silica

    Science.gov (United States)

    Ferguson, Frank T.; Nuth, Joseph A., III

    2012-01-01

    The evaporation coefficient and equilibrium vapor pressure of silicon monoxide over a mixture of silicon and vitreous silica have been studied over the temperature range (1433 to 1608) K. The evaporation coefficient for this temperature range was (0.007 plus or minus 0.002) and is approximately an order of magnitude lower than the evaporation coefficient over amorphous silicon monoxide powder and in general agreement with previous measurements of this quantity. The enthalpy of reaction at 298.15 K for this reaction was calculated via second and third law analyses as (355 plus or minus 25) kJ per mol and (363.6 plus or minus 4.1) kJ per mol respectively. In comparison with previous work with the evaporation of amorphous silicon monoxide powder as well as other experimental measurements of the vapor pressure of silicon monoxide gas over mixtures of silicon and silica, these systems all tend to give similar equilibrium vapor pressures when the evaporation coefficient is correctly taken into account. This provides further evidence that amorphous silicon monoxide is an intimate mixture of small domains of silicon and silica and not strictly a true compound.

  17. Synthesis of silicon carbide coating on diamond by microwave heating of diamond and silicon powder: A heteroepitaxial growth

    Energy Technology Data Exchange (ETDEWEB)

    Leparoux, S. [Empa, Department of Materials Technology, Feuerwerkerstrasse 39, CH-3602 Thun (Switzerland)], E-mail: susanne.leparoux@empa.ch; Diot, C. [Consultant, allee de Mozart 10, F-92300 Chatillon (France); Dubach, A. [Empa, Department of Materials Technology, Feuerwerkerstrasse 39, CH-3602 Thun (Switzerland); Vaucher, S. [Empa, Department of Materials Technology, Feuerwerkerstrasse 39, CH-3602 Thun (Switzerland)

    2007-10-15

    When a powder mixture of diamond and silicon is heated by microwaves, heteroepitaxial growth of SiC is observed on the (1 1 1) as well as on the (1 0 0) faces of the diamond. The SiC over-layer was characterized by X-ray diffraction and scanning electron microscopy. High-resolution scanning electron microscopy shows the presence of triangular silicon carbide on the (1 1 1) faces of diamond while prismatic crystals are found on the (1 0 0) faces. The crystal growth seems to be favored in the plane parallel to the face (1 1 1)

  18. Synthesis of silicon carbide coating on diamond by microwave heating of diamond and silicon powder: A heteroepitaxial growth

    International Nuclear Information System (INIS)

    Leparoux, S.; Diot, C.; Dubach, A.; Vaucher, S.

    2007-01-01

    When a powder mixture of diamond and silicon is heated by microwaves, heteroepitaxial growth of SiC is observed on the (1 1 1) as well as on the (1 0 0) faces of the diamond. The SiC over-layer was characterized by X-ray diffraction and scanning electron microscopy. High-resolution scanning electron microscopy shows the presence of triangular silicon carbide on the (1 1 1) faces of diamond while prismatic crystals are found on the (1 0 0) faces. The crystal growth seems to be favored in the plane parallel to the face (1 1 1)

  19. Tuning up and fabrication of U3Si2 nuclear material

    International Nuclear Information System (INIS)

    Pasqualini, Enrique E.; Echenique, Patricia N.; Rossi, Gustavo S.; Canil, Eduardo E.; Esteban, Adolfo; Lopez, Marisol; Adelfang, Pablo

    2000-01-01

    This work describes the tuning up and fabrication of uranium-silicide powder for its utilization as nuclear fuel in material testing reactors taking in account NUREG-1313 recommendations, the experience of several suppliers and the one acquired in this work.Several alloy compositions were melted with natural uranium at temperatures of about 1800 degree C for adjusting composition and ingot homogeneity. Alumina, magnesia and zirconia-5% stabilized yttria crucibles were tested to evaluate the degree of contamination introduced by chemical attack of molten uranium and silicon. The fabrication procedure of 20% enriched uranium-silicide powder was established for building up the P-06 fuel element that actually is being irradiated at the RA-3 reactor facility. The selected procedures of fabrication and the critical analysis for the interpretation of several specifications are discussed. Results are shown of the obtained ingots and powder produced with the enriched uranium-silicide. (author)

  20. Refractive index contrast in porous silicon multilayers

    Energy Technology Data Exchange (ETDEWEB)

    Nava, R.; Mora, M.B. de la; Tagueena-Martinez, J. [Centro de Investigacion en Energia, Universidad Nacional Autonoma de Mexico, Temixco, Morelos (Mexico); Rio, J.A. del [Centro de Investigacion en Energia, Universidad Nacional Autonoma de Mexico, Temixco, Morelos (Mexico); Centro Morelense de Innovacion y Transferencia Tecnologica, Consejo de Ciencia y Tecnologia del Estado de Morelos (Mexico)

    2009-07-15

    Two of the most important properties of a porous silicon multilayer for photonic applications are flat interfaces and a relative large refractive index contrast between layers in the optical wavelength range. In this work, we studied the effect of the current density and HF electrolyte concentration on the refractive index of porous silicon. With the purpose of increasing the refractive index contrast in a multilayer, the refractive index of porous silicon produced at low current was studied in detail. The current density applied to produce the low porosity layers was limited in order to keep the electrolyte flow through the multilayer structure and to avoid deformation of layer interfaces. We found that an electrolyte composed of hydrofluoric acid, ethanol and glycerin in a ratio of 3:7:1 gives a refractive index contrast around 1.3/2.8 at 600 nm. Several multilayer structures with this refractive index contrast were fabricated, such as dielectric Bragg mirrors and microcavities. Reflectance spectra of the structures show the photonic quality of porous silicon multilayers produced under these electrochemical conditions. (copyright 2009 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim) (orig.)