  1. Scandium doped Strontium Titanate Ceramics: Structure, Microstructure, and Dielectric Properties

    Directory of Open Access Journals (Sweden)

    Tkach, Alexander

    2008-08-01

    Full Text Available Sc-doped strontium titanate (ST ceramics were synthesised by solid state reaction, according to the composition Sr1-1.5xScxTiO3 with x = 0-0.01. Structural properties and microstructure development was examined by XRD and SEM. The dielectric properties were evaluated as a function of the temperature and frequency in the radio frequency range. Lattice parameter, density and grain size, were found to decrease slightly with increasing Sc content. The dielectric permittivity and losses decrease also. Sc-doping has only a weak effect on the quantum paraelectric behaviour of ST and no dielectric anomaly was observed, what is probably related to the limited solubility of Sc on the Sr site of the perovskite lattice of ST.

    Se sintetizaron materiales cerámicos de titanato de estroncio dopado con escandio mediante reacción en estado sólido De acuerdo a la composición Sr1-1.5xScxTiO3 con x= 0-0.1. Las propiedades estructurales y el desarrollo microestructural se estudiaron mediante XRD y SEM. La propiedades dieléctricas se estudiaron como función de la temperatura y de la frecuencia en el rango de la frecuencias de radio. Se observó que los parámetros de red, la densidad y el tamaño del grano disminuyen ligeramente con el contenido en Sc. La permitividad dieléctrica y las perdidas también disminuyen. El dopado con Sc tiene un efecto muy ligero sobre el comportamiento paraeléctrico cuántico del titanato de estroncio y no se observó anomalías dioeléctricas , lo que está probablemente relacionado con la baja solubilidad del Sc en posiciones del Sr en la estructura tipo perovskita del titanato de estroncio.

  2. Order-disorder phenomenon in lead scandium tantalate

    International Nuclear Information System (INIS)

    Wang, H.C.; Schulze, W.A.

    1990-01-01

    Lead scandium tatalate (PST) is a ferroelectric relaxor with the perovskite structure of A(B'B double-prime)O 3 . By suitable heat treatment, the B-site cations can be brought from a structurally disordered state into various degree of ordering. The degree of ordering is strongly affected by the amount of vacancies present in the materials. To suppress PbO loss during the sintering or annealing process, a PbO-rich atmosphere is supplied by materials having high PbO vapor pressure, such as PbZrO 3 . For PST ceramics with nearly zero weight loss, very long annealing times and higher annealing temperatures are required for ordering. The higher PbO-loss materials are found to be easily ordered. The introduction of a reducing atmosphere during annealing enhances the ordering process. The ordering process is characterized quantitatively by X-ray diffraction and qualitatively by Raman spectroscopy

  3. Electrophoretic growth of lead zirconate titanate nanorods

    Energy Technology Data Exchange (ETDEWEB)

    Limmer, S.J.; Seraji, S.; Forbess, M.J.; Wu Yun; Chou, T.P.; Nguyen, C.; Cao Guozhong [Washington Univ., Seattle, WA (United States). Dept. of Materials Science and Engineering

    2001-08-16

    Nanorods of lead zirconate titanate (PZT)-a ferro- and piezoelectric material-up to 10 {mu}m in length and 70 to 150 nm in diameter are produced by sol-gel electrophoresis of PZT in a track-etched polycarbonate membrane, which is used as a template. (orig.)

  4. Phenomenological theory of the dielectric response of lead magnesium niobate and lead scandium tantalate

    International Nuclear Information System (INIS)

    Qian, H.; Bursill, L.A.

    1997-01-01

    The influence of the random field effects originating from charges chemical defects and non-domain textures of the formation and dynamics of polar clusters is analyzed. The spatial distribution of the local fields is not totally random but contains some correlations in direction and strength. Polar clusters are classified to be dynamic or frozen according to their dynamic characteristics in the random fields. The relaxation formula of a dipolar moment in an anisotropic double-well potential is deduced. Two percolation models are introduced, one to account for frustration effects associated with multiple orientations of polar clusters, which results in a broad diffuse dielectric response and the second to account for the case whereby there may be a phase transition to a ferroelectric state. The dielectric permittivity and dissipation factor of the typical relaxors lead magnesium niobate and lead scandium tantalate are predicted as a function of both temperature and frequency, which results are in good agreement with the experimental measurements. 30 refs., 9 figs

  5. Random-field Potts model for the polar domains of lead magnesium niobate and lead scandium tantalate

    Energy Technology Data Exchange (ETDEWEB)

    Qian, H.; Bursill, L.A

    1997-06-01

    A random filed Potts model is used to establish the spatial relationship between the nanoscale distribution of charges chemical defects and nanoscale polar domains for the perovskite-based relaxor materials lead magnesium niobate (PMN) and lead scandium tantalate (PST). The random fields are not set stochastically but are determined initially by the distribution of B-site cations (Mg, Nb) or (Sc, Ta) generated by Monte Carlo NNNI-model simulations for the chemical defects. An appropriate random field Potts model is derived and algorithms developed for a 2D lattice. It is shown that the local fields are strongly correlated with the chemical domain walls and that polar domains as a function of decreasing temperature is simulated for the two cases of PMN and PST. The dynamics of the polar clusters is also discussed. 33 refs., 9 figs.

  6. Screening of spontaneous polarization in lead titanate crystals

    International Nuclear Information System (INIS)

    Gavrilyachenko, V.G.; Semenchev, A.F.; Fesenko, E.G.

    1996-01-01

    Results of experimental investigations into electric conductivity of lead titanate crystals with different domain structure including single-domain are reported. The data obtained give grounds to believe that spontaneous titanate polarization is realized by the surface level and charge volumetric of free carriers and ionized impurity

  7. Fracture mechanisms in lead zirconate titanate ceramics

    International Nuclear Information System (INIS)

    Freiman, S.W.; Chuck, L.; Mecholsky, J.J.; Shelleman, D.L.

    1986-01-01

    Lead Zirconate Titanate (PZT) ceramics can be formed over a wide range of PbTiO 3 /PbZrO 3 ratios and exist in a number of crystal structures. This study involved the use of various fracture mechanics techniques to determine critical fracture toughness, K /SUB IC/ , as a function of composition, microstructure, temperature, and electrical and thermal history. The results of these experiments indicate that variations in K /SUB IC/ are related to phase transformations in the material as well as to other toughening mechanisms such as twinning and microcracking. In addition, the strength and fracture toughness of selected PZT ceramics were determined using specimens in which a crack was introduced by a Vicker's hardness indentor. The variation of K /SUB IC/ with composition and microstructure was related to the extent of twin-crack interaction. Comparison of the plot of strength as a function of indentation load with that predicted from indentation fracture models indicates the presence of internal stresses which contribute to failure. The magnitude of these internal stresses has been correlated with electrical properties of the ceramic. Fractographic analysis was used to determine the magnitude of internal stresses in specimens failing from ''natural flaws.''

  8. Lead titanate nanotubes synthesized via ion-exchange method: Characteristics and formation mechanism

    International Nuclear Information System (INIS)

    Song Liang; Cao Lixin; Li Jingyu; Liu Wei; Zhang Fen; Zhu Lin; Su Ge

    2011-01-01

    Highlights: → Lead titanate nanotubes PbTi 3 O 7 were firstly synthesized by ion-exchange method. → Sodium titanate nanotubes have ion exchangeability. → Lead titanate nanotubes show a distinct red shift on absorption edge. - Abstract: A two-step method is presented for the synthesis of one dimensional lead titanate (PbTi 3 O 7 ) nanotubes. Firstly, titanate nanotubes were prepared by an alkaline hydrothermal process with TiO 2 nanopowder as precursor, and then lead titanate nanotubes were formed through an ion-exchange reaction. We found that sodium titanate nanotubes have ion exchangeability with lead ions, while protonated titanate nanotubes have not. For the first time, we distinguished the difference between sodium titanate nanotubes and protonated titanate nanotubes in the ion-exchange process, which reveals a layer space effect of nanotubes in the ion-exchange reaction. In comparison with sodium titanate, the synthesized lead titanate nanotubes show a narrowed bandgap.

  9. Extrusion and properties of lead zirconate titanate piezoelectric ceramics

    DEFF Research Database (Denmark)

    Cai, S.; Millar, C.E.; Pedersen, L.

    1997-01-01

    The purpose of this work was to develop a procedure for fabricating electroceramic actuators with good piezoelectric properties. The preparation of lead zirconate titanate (PZT) piezoelectric ceramic rods and tubes by extrusion processing is described. The microstructure of extrudates was investi......The purpose of this work was to develop a procedure for fabricating electroceramic actuators with good piezoelectric properties. The preparation of lead zirconate titanate (PZT) piezoelectric ceramic rods and tubes by extrusion processing is described. The microstructure of extrudates...

  10. Biamperometric analysis of nonaqueous scandium solutions containing lanthanides, lead and thorium

    International Nuclear Information System (INIS)

    Gevorgyan, A.M.; Talipov, Sh.T.; Kostylev, V.S.; Khadeev, V.A.; Nadol'skij, M.Ya.

    1978-01-01

    Investigated was a possibility of direct scandium titration in the presence of large rare earth quantities, and also a possibility of complexonometric scandium and rare earth sum determination at their joint presence in non-aqueous acetic acid solution. The titration was carried out at electrode voltage of 0.95V, background electrolyte concentration of lithium perchlorate being 0.2M. Non-aqueous magnesium complexonate was used as titrating reagent. Th and Pb complexonates are shown to be less stable as compared to Sc complexonate, and consequently, Th and Pb ions must not interfere with biamperometric titration of Sc ion. A method applied to analysis of binary mixture, containing scandium, and a method for model alloy and thortveitite mineral was developed. Well reproducible and precise enough results are obtained in all the cases. Ions of Bi, Cu, Cd, Zn, In, Ga and Ti interfere with determination

  11. Crystal structure of red lead titanate thin films

    Energy Technology Data Exchange (ETDEWEB)

    Bursill, L.A.; Peng, J.L.; Jiang, B. [Melbourne Univ., Parkville, VIC (Australia). School of Physics; Li, X. [Jilin Univ., Changchun, JL (China). Dept of Chemistry

    1998-09-01

    Orange-red lead titanate thin films are examined by high-resolution transmission electron microscopy and diffraction. It is remarkable that the structure is based on that of tetragonal-tungsten-bronze (TTB) rather than perovskite-type. The chemical basis for this result is examined. It is deduced that the TTB structure is stabilized by inclusion of hydroxyl ions during synthesis by a sol-gel route involving hydrolysis of n-Butyl titanate 7 refs., 1 tab., 4 figs.

  12. Crystal structure of red lead titanate thin films

    International Nuclear Information System (INIS)

    Bursill, L.A.; Peng, J.L.; Jiang, B.; Li, X.

    1998-01-01

    Orange-red lead titanate thin films are examined by high-resolution transmission electron microscopy and diffraction. It is remarkable that the structure is based on that of tetragonal-tungsten-bronze (TTB) rather than perovskite-type. The chemical basis for this result is examined. It is deduced that the TTB structure is stabilized by inclusion of hydroxyl ions during synthesis by a sol-gel route involving hydrolysis of n-Butyl titanate

  13. Microstructure of lead zirconium titanate (PZT) by electron microscopy

    International Nuclear Information System (INIS)

    Bursill, L.A.; Peng JuLin

    1989-01-01

    Transmission and high-resolution electron microscopy reveal the microtexture of lead zirconium titanate ceramics. Fine scale (≤ 500 Aangstroem) ferroelastic and ferroelectric twin domains, as well as dislocations were found in a complex texture. Correlations between stoichiometry, microstructure and piezoelectric properties are discussed. 6 refs., 3 figs

  14. Fatigue studies in compensated bulk lead zirconate titanate

    International Nuclear Information System (INIS)

    Verdier, Cyril; Morrison, Finlay D.; Lupascu, Doru C.; Scott, James F.

    2005-01-01

    Impedance analysis studies were carried out on compensated bulk lead zirconate titanate samples. Fatigue is concomitant with the onset of dielectric loss. This is shown to be dominantly due to an irreversibly modified near-surface layer that can be polished off. The highly compensated nature of these samples minimizes the role of oxygen vacancies

  15. Electrical and thermal properties of lead titanate glass ceramics

    International Nuclear Information System (INIS)

    Shankar, J.; Deshpande, V.K.

    2011-01-01

    Glass samples with composition of (50-X)PbO-(25+X)TiO 2 -25B 2 O 3 (where X=0, 5, 10 and 12.5 mol%) were prepared using conventional quenching technique. The glass transition temperature, T g and crystallization temperature T c were determined from the DTA. These glass samples were converted to glass ceramics by following two stage heat treatment schedule. The glass ceramic samples were characterized by XRD, SEM and dielectric constant measurements. The XRD results revealed the formation of ferroelectric lead titanate (PT) as a major crystalline phase in the glass ceramics. The density increases and the CTE decreases for all glass ceramics with increase in X (mol%). This may be attributed to increase in PT phase. The SEM results which show rounded crystallites of lead titanate, also supports other results. Hysteresis loops observed at room temperature confirms the ferroelectric nature of glass ceramics. The optimized glass ceramic sample exhibits high dielectric constant which is of technical importance. -- Research Highlights: →Lead titanate glass ceramics prepared by conventional quenching technique. →Lead titanate is a major crystalline phase in the glass ceramics. →The ferroelectric nature of glass ceramics is confirmed by the hysteresis study. →The high value of ε observed at room temperature is quite promising in the study.

  16. Pyroelectricity versus conductivity in soft lead zirconate titanate (PZT) ceramics

    NARCIS (Netherlands)

    Kamel, T.M.; With, de G.

    2007-01-01

    The electrical behavior of modified soft lead zirconate titanate (PZT) ceramics has been studied as a function of temperature at different direct current (dc) electric fields and grain sizes. As ferroelectrics, such as PZT, are highly polarizable materials, poling, depolarization, and electric

  17. Phase transformations in lead zirconate-titanate doped with lanthanum

    Energy Technology Data Exchange (ETDEWEB)

    Ishchuk, V M; Morozov, E M

    1979-07-01

    Presented are the results of studies on the character of phase transitions of the lead-lanthanum zirconate-titanate (LLZT) system. The replacement of lead by lanthanum leads to the expansion of the region of antisegnetoelectric (ASE) states of solid solutions of lead zirconate-titanate (LZT) in the direction of PbTiO/sub 3/ concentration growth. An intermediate region is revealed between segnetoelectric (SE) and ASE states, material properties in which depend on their prehistory: annealed samples are in the ASE state, whereas the application of electric field exceeding some critical value induces the SE state. A family of phase diagrams obtained at consequent replacement of lead by lanthanum permits to identify phase states in any series of LLZT with a constant ratio of Zr:Ti, in the x/65/35 series in particular. Thermally depolarized state of materials of this series at x<6.5 is shown to be antisegnetoelectric at all the temperatures below the Curie point Tsub(c), and heating causes phase transition of ASE..-->..PE (paraelectric state) at Tsub(c). Polarized samples being heated, a successiveness of phase transitions of SE..-->..ASE takes place at T/sub 0/, and that of ASE reversible PE at Tsub(C) (Tsub(0)..ASE phase transition in the LZT system.

  18. Dielectric behaviors of lead zirconate titanate ceramics with coplanar electrodes

    International Nuclear Information System (INIS)

    Wang, Y.; Cheng, Y.L.; Zhang, Y.W.; Chan, H.L.W.; Choy, C.L.

    2003-01-01

    This paper reports on the dielectric behaviors of lead zirconate titanate (PZT) capacitors with coplanar electrodes. Usually a ferroelectric device has a metal-ferroelectric-metal configuration (parallel plate capacitor); when both the electrodes are on one side of a ceramic to form a coplanar capacitor, different dielectric behaviors will be anticipated because of the change in the distribution of the test field inside the dielectrics. This paper describes how the capacitance and dielectric loss of PZT-based coplanar capacitors change with electrode distance, area and test frequency

  19. Quantitative analysis method for niobium in lead zirconate titanate

    International Nuclear Information System (INIS)

    Hara, Hideo; Hashimoto, Toshio

    1986-01-01

    Lead zirconate titanate (PZT) is a strong dielectric ceramic having piezoelectric and pyroelectric properties, and is used most as a piezoelectric material. Also it is a main component of lead lanthanum zirconate titanate (PLZT), which is a typical electrical-optical conversion element. Since these have been developed, the various electronic parts utilizing the piezoelectric characteristics have been put in practical use. The characteristics can be set up by changing the composition of PZT and the kinds and amount of additives. Among the additives, niobium has the action to make metallic ion vacancy in crystals, and by the formation of this vacancy, to ease the movement of domain walls in crystal grains, and to increase resistivity. Accordingly, it is necessary to accurately determine the niobium content for the research and development, quality control and process control. The quantitative analysis methods for niobium used so far have respective demerits, therefore, the authors examined the quantitative analysis of niobium in PZT by using an inductively coupled plasma emission spectro-analysis apparatus which has remarkably developed recently. As the result, the method of dissolving a specimen with hydrochloric acid and hydrofluoric acid, and masking unstable lead with ethylene diamine tetraacetic acid 2 sodium and fluoride ions with boric acid was established. The apparatus, reagents, the experiment and the results are reported. (Kako, I.)

  20. Improvement of conditions for ceramics sintering on the base of lead zirconate-titanate

    International Nuclear Information System (INIS)

    Glinchuk, M.D.; Kim, P.V.; Bykov, I.P.; Lyashchenko, A.B.

    1989-01-01

    Lead zirconate-titanate powders of different graininess are studied for their phase composition. The finest grains of the powder consist of lead zirconate-titanate with the rhombohedral structure. Grains of 3-5 μm size are a mixture of lead zirconate-titanate and lead titanate, the latter exceeding 50% (by weight) causes the effect of anomalous expansion in the process of sintering. Control of the technological parameters of the synthesis permits producing powder with favourable correlation of the above phases and grain sizes. Sintering of such a powder induces no effect of the anomalous expansion with an increased density of the product attained

  1. Preparation of lead titanate zirconate from metal citrates

    International Nuclear Information System (INIS)

    Bastos, C.M.R.

    1994-01-01

    Lead titanate zirconate (PZT) preparation from its metal constituent citrates have been investigated. Metal citrates were obtained by forced precipitation using a dehydration alcohol mixture. Salt solutions of lead nitrate and octahydrated zirconyl chloride, and titanium tetrachloride were treated separately with citric acid and ammonium hydroxide. Zirconium, titanium and lead oxides resulted from thermal decomposition of corresponding citrates at 500 0 C, 450 0 C and 250 0 C, respectively. Lead titanate (PT) and lead zirconate (P Z) were obtained by calcining at 450 0 C and 500 0 C, respectively, after adequate heating of citrates mechanically mixed in ethyl ether. PZT samples were obtained with different starting stoichiometry. Rhombohedral PZT-1 53/47 sample was prepared from co precipitating zirconyl ammonium and ammonium lead citrates in presence of ethanolic titanium oxide dispersion, and calcinating at 800 0 C. Rhombohedral PZT-q 52/48 sample was obtained from heating at 500 0 C for 2 hours a mixture of metal citrates coprecipitated by dehydration mixture of acetone-ethanol-formic acid (2:1:0,06). Tetragonal PZT-m stoichiometry 53/47 sample were obtained by calcining at after 600 0 C for 2 hours after heating a mechanically mixed metal citrates. PT phase arose at 400 0 C. PZT-m powders obtained in a range of 400 0 C-800 0 C were isostatically pressed, and sintered at 1100 0 C and 1200 0 C in saturated Pb O atmosphere. Rhombohedral sintered PZT was obtained with 7,78 g.cm -3 at 1200 0 C. (author). 123 refs, 53 figs, 32 tabs

  2. Ferroelastic domain switching fatigue in lead zirconate titanate ceramics

    International Nuclear Information System (INIS)

    Pojprapai, Soodkhet; Jones, Jacob L.; Studer, Andrew J.; Russell, Jennifer; Valanoor, Nagarajan; Hoffman, Mark

    2008-01-01

    The influence of the frequency and amplitude of cyclic mechanical loading on soft, tetragonal lead zirconate titanate (PZT) ceramics was investigated via neutron diffraction. Intensity change in the {2 0 0} reflections provided quantitative measurements of domain switching behavior, domain texture and the strain resulting from domain switching. The results are explained using a viscoelasticity model. It was found that the magnitude of applied stress affects the level of strain accumulated, while its frequency affects the time taken for the strain to reach saturation. Furthermore, markedly different behaviors are exhibited by poled and unpoled samples. For samples loaded under identical conditions, the frequency effect is more pronounced in unpoled samples and the accumulated ferroelastic strain is greater in poled samples

  3. Ferroelectric devices using lead zirconate titanate (PZT) nanoparticles.

    Science.gov (United States)

    Paik, Young Hun; Kojori, Hossein Shokri; Kim, Sung Jin

    2016-02-19

    We successfully demonstrate the synthesis of lead zirconate titanate nanoparticles (PZT NPs) and a ferroelectric device using the synthesized PZT NPs. The crystalline structure and the size of the nanocrystals are studied using x-ray diffraction and transmission electron microscopy, respectively. We observe PZT NPs and this result matches dynamic light scattering measurements. A solution-based low-temperature process is used to fabricate PZT NP-based devices on an indium tin oxide substrate. The fabricated ferroelectric devices are characterized using various optical and electrical measurements and we verify ferroelectric properties including ferroelectric hysteresis and the ferroelectric photovoltaic effect. Our approach enables low-temperature solution-based processes that could be used for various applications. To the best of our knowledge, this low-temperature solution processed ferroelectric device using PZT NPs is the first successful demonstration of its kind.

  4. New phase transitions in lead zirconate-titanate

    International Nuclear Information System (INIS)

    Ishchuk, V.M.; Morozov, E.M.; Klimov, V.V.

    1977-01-01

    Processes of disordering are considered in the paraelectric phase of lead zirconate-titanate. Te investigations were carried out on poly- and single-crystal specimens of the composition PbZrsub(1-x)Tisub(x)O 3 (0< x(<=)0.5). The results are presented of measurements of the temperature dependence of the dielectric constant and the dependence of the polarization on the temperature and the electric field. Anomaly is observed of the investigated characteristics above the Curie point due to a first-type phase transition. The results are interpreted within the framework of the model proposed by Coms, Lambert, and Guiniot, according to which this transition is due to the disordering of chains of unit cells existing above the Curie point

  5. Titan

    Science.gov (United States)

    Müller-Wodarg, Ingo; Griffith, Caitlin A.; Lellouch, Emmanuel; Cravens, Thomas E.

    2014-03-01

    Introduction I. C. F. Müller-Wodarg, C. A. Griffith, E. Lellouch and T. E. Cravens; Prologue 1: the genesis of Cassini-Huygens W.-H. Ip, T. Owen and D. Gautier; Prologue 2: building a space flight instrument: a P.I.'s perspective M. Tomasko; 1. The origin and evolution of Titan G. Tobie, J. I. Lunine, J. Monteux, O. Mousis and F. Nimmo; 2. Titan's surface geology O. Aharonson, A. G. Hayes, P. O. Hayne, R. M. Lopes, A. Lucas and J. T. Perron; 3. Thermal structure of Titan's troposphere and middle atmosphere F. M. Flasar, R. K. Achterberg and P. J. Schinder; 4. The general circulation of Titan's lower and middle atmosphere S. Lebonnois, F. M. Flasar, T. Tokano and C. E. Newman; 5. The composition of Titan's atmosphere B. Bézard, R. V. Yelle and C. A. Nixon; 6. Storms, clouds, and weather C. A. Griffith, S. Rafkin, P. Rannou and C. P. McKay; 7. Chemistry of Titan's atmosphere V. Vuitton, O. Dutuit, M. A. Smith and N. Balucani; 8. Titan's haze R. West, P. Lavvas, C. Anderson and H. Imanaka; 9. Titan's upper atmosphere: thermal structure, dynamics, and energetics R. V. Yelle and I. C. F. Müller-Wodarg; 10. Titan's upper atmosphere/exosphere, escape processes, and rates D. F. Strobel and J. Cui; 11. Titan's ionosphere M. Galand, A. J. Coates, T. E. Cravens and J.-E. Wahlund; 12. Titan's magnetospheric and plasma environment J.-E. Wahlund, R. Modolo, C. Bertucci and A. J. Coates.

  6. Scandium fluorides

    International Nuclear Information System (INIS)

    Melnikov, P.; Nalin, M.; Messaddeq, Y.

    1997-01-01

    A new modification of scandium fluoride has been synthesised. The compound is deficient in fluorine, with the composition ScF 2.76 . It belongs to the tetragonal system, lattice parameters being a=3.792 and c=6.740 A and may be obtained at low temperatures by the decomposition of the precursor NH 4 ScF 4 . The reaction is topotactic, tetragonal parameters of the precursor are a=4.021 and c=6.744 A. Structural relationships with various fluorides and ammonium aminofluorides are discussed. This synthesis route with IR-assisted decomposition should be considered as a soft-chemistry approach. (orig.)

  7. Titan!

    Science.gov (United States)

    Matson, Dennis L.

    2010-05-01

    Cassini-Huygens achieved Saturnian orbit on July 1, 2004. The first order of business was the safe delivery of the Huygens atmospheric probe to Titan that took place on January 14, 2005. Huygens descended under parachute obtaining observations all the way down to a safe landing. It revealed Titan for the first time. Stunning are the similarities between Titan and the Earth. Viewing the lakes and seas, the fluvial terrain, the sand dunes and other features through the hazy, nitrogen atmosphere, brings to mind the geological processes that created analogous features on the Earth. On Titan frozen water plays the geological role of rock; liquid methane takes the role of terrestrial water. The atmospheres of both Earth and Titan are predominately nitrogen gas. Titan's atmosphere contains 1.5% methane and no oxygen. The surface pressure on Titan is 1.5 times the Earth's. There are aerosol layers and clouds that come and go. Now, as Saturn proceeds along its solar orbit, the seasons are changing. The effects upon the transport of methane are starting to be seen. A large lake in the South Polar Region seems to be filling more as winter onsets. Will the size and number of the lakes in the South grow during winter? Will the northern lakes and seas diminish or dry up as northern summer progresses? How will the atmospheric circulation change? Much work remains not only for Cassini but also for future missions. Titan has many different environments to explore. These require more capable instruments and in situ probes. This work was conducted at the Jet Propulsion Laboratory, California Institute of Technology under contract with the National Aeronautics and Space Administration.

  8. Molten salt synthesis of lead lanthanum zirconate titanate ceramic powders

    International Nuclear Information System (INIS)

    Cai Zongying; Xing Xianran; Li Lu; Xu Yeming

    2008-01-01

    Lead lanthanum zirconate titanate (Pb 0.95 La 0.03 )(Zr 0.52 Ti 0.48 )O 3 (PLZT) was synthesized by one step molten salt method with the starting materials of PbC 2 O 4 , La 2 O 3 , ZrO(NO 3 ) 2 .2H 2 O and TiO 2 in the NaCl-KCl eutectic mixtures in the temperature range of 700-1000 deg. C. The single phase of (Pb 0.95 La 0.03 )(Zr 0.52 Ti 0.48 )O 3 powders was prepared at a temperature as low as 850 deg. C for 5 h. The effects of process parameters, such as soaking temperature and time, salt species, and the amount of flux with respect to the starting materials were investigated. The growth process of the PLZT particles in the molten salt undergoes a transition from a diffusion controlled mechanism to an interfacial reaction controlled mechanism at 900 deg. C

  9. Quantum confinement of lead titanate nanocrystals by wet chemical method

    Energy Technology Data Exchange (ETDEWEB)

    Kaviyarasu, K., E-mail: kaviyarasuloyolacollege@gmail.com [UNESCO-UNISA Africa Chair in Nanosciences/Nanotechnology Laboratories, College of Graduate Studies, University of South Africa (UNISA), Muckleneuk Ridge, P O Box 392, Pretoria (South Africa); Nanosciences African Network (NANOAFNET), Materials Research Department (MSD), iThemba LABS-National Research Foundation - NRF, 1 Old Faure Road, 7129, P O Box 722, Somerset West, Western Cape Province (South Africa); Manikandan, E., E-mail: maniphysics@gmail.com [Nanosciences African Network (NANOAFNET), Materials Research Department (MSD), iThemba LABS-National Research Foundation - NRF, 1 Old Faure Road, 7129, P O Box 722, Somerset West, Western Cape Province (South Africa); Central Research Laboratory, Sree Balaji Medical College & Hospital, Bharath University, Chrompet, Chennai, Tamil Nadu (India); Nuru, Z.Y. [UNESCO-UNISA Africa Chair in Nanosciences/Nanotechnology Laboratories, College of Graduate Studies, University of South Africa (UNISA), Muckleneuk Ridge, P O Box 392, Pretoria (South Africa); Nanosciences African Network (NANOAFNET), Materials Research Department (MSD), iThemba LABS-National Research Foundation - NRF, 1 Old Faure Road, 7129, P O Box 722, Somerset West, Western Cape Province (South Africa); Maaza, M., E-mail: likmaaz@gmail.com [UNESCO-UNISA Africa Chair in Nanosciences/Nanotechnology Laboratories, College of Graduate Studies, University of South Africa (UNISA), Muckleneuk Ridge, P O Box 392, Pretoria (South Africa); Nanosciences African Network (NANOAFNET), Materials Research Department (MSD), iThemba LABS-National Research Foundation - NRF, 1 Old Faure Road, 7129, P O Box 722, Somerset West, Western Cape Province (South Africa)

    2015-11-15

    Lead Titanate (PbTiO{sub 3)} is a category of the practical semiconductor metal oxides, which is widely applied in various scientific and industrial fields because of its catalytic, optical, and electrical properties. PbTiO{sub 3} nanocrystalline materials have attracted a wide attention due to their unique properties. PbTiO{sub 3} nanocrystals were investigated by X-ray diffraction (XRD) to identify the PbTiO{sub 3} nanocrystals were composed a tetragonal structure. The diameter of a single sphere was around 20 nm and the diameter reached up to 3 μm. The chemical composition of the samples and the valence states of elements were determined by X-ray photoelectron spectroscopy (XPS) in detail. - Highlights: • Single crystalline NSs of PbTiO{sub 3} fabricated by wet chemical method. • PbTiO{sub 3} NSs were uniform and continuous along the long axis. • Tetragonal perovskite structure with the diameter 20 nm and length 3 μm. • XPS spectrum was fitted with Lorentzian function respectively. • The size of the images is also 10 μm × 10 μm.

  10. Effect of dielectrophoretic structuring on piezoelectric and pyroelectric properties of lead titanate-epoxy composites

    NARCIS (Netherlands)

    Khanbareh, H.; Zwaag, S. van der; Groen, W.A.

    2014-01-01

    Functional granular composites of lead titanate particles in an epoxy matrix prepared by dielectrophoresis show enhanced dielectric, piezoelectric and pyroelectric properties compared to 0-3 composites for different ceramic volume content from 10% to 50%. Two structuring parameters, the

  11. Current—voltage characteristics of lead zirconate titanate/nickel bilayered hollow cylindrical magnetoelectric composites

    International Nuclear Information System (INIS)

    De-An, Pan; Shen-Gen, Zhang; Jian-Jun, Tian; Li-Jie, Qiao; Jun-Sai, Sun; Volinsky, Alex A.

    2010-01-01

    Current–voltage measurements obtained from lead zirconate titanate/nickel bilayered hollow cylindrical magnetoelectric composite showed that a sinusoidal current applied to the copper coil wrapped around the hollow cylinder circumference induces voltage across the lead zirconate titanate layer thickness. The current–voltage coefficient and the maximum induced voltage in lead zirconate titanate at 1 kHz and resonance (60.1 kHz) frequencies increased linearly with the number of the coil turns and the applied current. The resonance frequency corresponds to the electromechanical resonance frequency. The current–voltage coefficient can be significantly improved by optimizing the magnetoelectric structure geometry and/or increasing the number of coil turns. Hollow cylindrical lead zirconate titanate/nickel structures can be potentially used as current sensors. (condensed matter: electronic structure, electrical, magnetic, and optical properties)

  12. Real-Time Salmonella Detection Using Lead Zirconate Titanate-Titanium Microcantilevers

    National Research Council Canada - National Science Library

    McGovern, John-Paul; Shih, Wan Y; Shih, Wei-Heng; Sergi, Mauro; Chaiken, Irwin

    2005-01-01

    .... We have developed and investigated the use of a lead zirconate titanate - titanium (PZT-Ti) microcantilever for in situ detection of the common food- and water-born pathogen, Salmonella typhimurium...

  13. Ionic and electronic conductivity in lead-zirconate-titanate (PZT)

    NARCIS (Netherlands)

    Boukamp, Bernard A.; Pham thi ngoc mai, P.T.N.M.; Blank, David H.A.; Bouwmeester, Henricus J.M.

    2004-01-01

    Accurate impedance measurements on differently sized samples of lead–zirconate–titanate (PbZr0.53Ti0.47O3, PZT) have been analyzed with a CNLS procedure, resulting in the separation of the ionic and electronic conductivities over a temperature range from f150 to 630 jC. At 603 jC the electronic

  14. The preparation of a novel layered lead titanate and its conversion to the perovskite lead titanate PbTiO3

    NARCIS (Netherlands)

    Blake, G.R.; Armstrong, A.R.; Sastre, E.; Wright, P.A.

    2001-01-01

    A novel layered lead titanate with the approximate composition PbTiO2(CO3)0.3(NO3)0.35(OH) has been synthesized hydrothermally under acidic conditions. The structure has been solved and refined from X-ray and neutron powder diffraction data in the space group P -3 1 m, with cell dimensions a =

  15. Ferroelectric lead magnesium niobate-lead titanate single crystals for ultrasonic hydrophone applications

    International Nuclear Information System (INIS)

    Lau, S.T.; Lam, K.H.; Chan, H.L.W.; Choy, C.L.; Luo, H.S.; Yin, Q.R.; Yin, Z.W.

    2004-01-01

    Ferroelectric lead magnesium niobate-lead titanate (PMN-PT) single crystals with a composition around the rhombohedral-tetragonal morphotropic phase boundary (65 mol% of PMN) were used to fabricate single-element needle-type hydrophones for measuring the spatial and temporal characteristics of medical ultrasonic transducers. PMN-PT single crystal was grown by a modified Bridgman method. Discs (0.5 mm thick) with normal along the direction were cut and then poled by a dc field in the thickness direction. The single crystal has a high relative permittivity (ε r ∼4000) making it appropriate for small area hydrophone applications. Single-element needle-type hydrophones with this material as the sensing element have been fabricated and characterized. The hydrophones have flat frequency response and good receiving sensitivity over certain frequency range in the megahertz region

  16. Elution of lead from lead zirconate titanate ceramics to acid rain

    Science.gov (United States)

    Tsurumi, Takaaki; Takezawa, Shuhei; Hoshina, Takuya; Takeda, Hiroaki

    2017-10-01

    The amount of lead that eluted from lead zirconate titanate (PZT) ceramics to artificial acid rain was evaluated. Four kinds of PZT ceramics, namely, pure PZT at MPB composition, CuO-added PZT, PZT with 10 mol % substitution of Ba for Pb, and CuO-added PZT with 10 mol % substitution of Ba for Pb, were used as samples of the elution test. These PZT ceramics of 8 mm2 and 1.1-1.2 mm thickness were suspended in 300 ml of H2SO4 solution of pH 4.0. The concentration of lead eluted from PZT was in the range from 0.2 to 0.8 ppm. It was found that both liquid phase formation by the addition of CuO and the substitution of Ba for Pb were effective to reduce the amount of lead that eluted. By fitting the leaching out curve with a classical equation, a master curve assuming no sampling effect was obtained. The lead concentration evaluated from the amount of lead that eluted from a commercial PZT plate to H2SO4 solution of pH 5.3 was almost the same as the limit in city water. It is concluded that PZT is not harmful to health and the environment and the amount of lead that eluted from PZT can be controlled by modifying PZT composition.

  17. Ion exchange purification of scandium

    Science.gov (United States)

    Herchenroeder, Laurie A.; Burkholder, Harvey R.

    1990-10-23

    An improvement in purification of scandium through ion exchange chromatography is disclosed in which the oxidation potential of the eluting solution is altered by the addition of potassium chlorate or ammonium chloride so that removal of contaminants is encouraged. The temperature, pH and concentration of the eluent HEDTA are controlled in order to maintain the scandium in the column while minimizing dilution of the scandium band. Recovery of scandium is improved by pumping dilute scandium over the column prior to stripping the scandium and precipitation. This eliminates the HEDTA ion and other monovalent cations contaminating the scandium band. This method maximizes recovery of scandium while maintaining purity.

  18. Modified lead titanate thin films for pyroelectric infrared detectors on gold electrodes

    Science.gov (United States)

    Ahmed, Moinuddin; Butler, Donald P.

    2015-07-01

    Pyroelectric infrared detectors provide the advantage of both a wide spectral response and dynamic range, which also has enabled systems to be developed with reduced size, weight and power consumption. This paper demonstrates the deposition of lead zirconium titanate (PZT) and lead calcium titanate (PCT) thin films for uncooled pyroelectric detectors with the utilization of gold electrodes. The modified lead titanate thin films were deposited by pulsed laser deposition on gold electrodes. The PZT and PCT thins films deposited and annealed at temperatures of 650 °C and 550 °C respectively demonstrated the best pyroelectric performance in this work. The thin films displayed a pyroelectric effect that increased with temperature. Poling of the thin films was carried out for a fixed time periods and fixed dc bias voltages at elevated temperature in order to increase the pyroelectric coefficient by establishing a spontaneous polarization of the thin films. Poling caused the pyroelectric current to increase one order of magnitude.

  19. Structure determination and compositional modification of body-centered tetragonal PX-phase lead titanate

    Czech Academy of Sciences Publication Activity Database

    Wang, J.; Schenk, K.; Carvalho, A.; Wylie-van Eerd, B.; Trodahl, J.; Sandu, C.S.; Bonin, M.; Gregora, Ivan; He, Z.; Yamada, T.; Funakubo, H.; Briddon, P.R.; Setter, N.

    2011-01-01

    Roč. 23, č. 10 (2011), s. 2529-2535 ISSN 0897-4756 R&D Projects: GA AV ČR KAN301370701 Institutional research plan: CEZ:AV0Z10100520 Keywords : lead titanate * fibrous PX phase * structure determination * open channels * Raman scattering Subject RIV: BM - Solid Matter Physics ; Magnetism Impact factor: 7.286, year: 2011

  20. Contribution of the irreversible displacement of domain walls to the piezoelectric effect in barium titanate and lead zirconate titanate ceramics

    CERN Document Server

    Damjanovic, D

    1997-01-01

    The contribution from the irreversible displacement of non-180 deg domain walls to the direct longitudinal piezoelectric d sub 3 sub 3 coefficient of BaTiO sub 3 and Pb(Zr, Ti)O sub 3 ceramics was determined quantitatively by using the Rayleigh law. Effects of the crystal structure and microstructure of the ceramics as well as the external d.c. pressure on the domain wall contribution to d sub 3 sub 3 were examined. In barium titanate, this domain wall contribution is large (up to 35% of the total d sub 3 sub 3 , under the experimental conditions used) and dependent on the external d.c. pressure in coarse grained ceramics, and much smaller and independent of the external d.c. pressure in fine-grained samples. The presence of internal stresses in fine-grained ceramics could account for the observed behaviour. The analysis shows that the domain-wall contribution to the d sub 3 sub 3 in lead zirconate titanate ceramics is large in compositions close to the morphotropic phase boundary that contain a mixture of te...

  1. Comparative microstructure and electrical property studies of lead scandium tantalate thin films as prepared by LDCVD, sol-gel and sputtering techniques

    International Nuclear Information System (INIS)

    Huang, Z; Donohue, P P; Zhang, Q; Williams, D J; Anthony, C J; Whatmore, R W; Todd, M A

    2003-01-01

    Lead scandium tantalate (PST) thin films for uncooled infrared (IR) detector applications have been deposited by liquid delivery chemical vapour deposition (LDCVD), sputtering and sol-gel techniques. The sol-gel and sputtered films were deposited at low temperature into a non-ferroelectric phase with the required perovskite structure being formed using a high temperature rapid thermal anneal (RTA). In contrast to this, the LDCVD films were deposited at high temperature directly into the perovskite phase but were found to still require a high temperature RTA step to optimize their merit for IR detection. Detailed structural and electrical characterization of the PST films deposited by these different methods have revealed that there is no simple relationship between microstructure and electrical properties. The sol-gel and LDCVD techniques produce thin films with excellent microstructures, as determined by x-ray diffraction analysis and transmission electron microscopy, but inferior electrical properties and relatively low merit figures. By contrast, the sputtered and then rapid thermal annealed films have inferior microstructures, characterized by extensive voiding, but excellent electrical properties and high merit figures

  2. Structural and electrical properties of Nd ion modified lead zirconate titanate nanopowders and ceramics

    International Nuclear Information System (INIS)

    Da-Wei, Wang; De-Qing, Zhang; Quan-Liang, Zhao; Hong-Mei, Liu; Zhi-Ying, Wang; Mao-Sheng, Cao; Jie, Yuan

    2009-01-01

    A modified sol-gel method is used for synthesizing Nd ion doped lead zirconate titanate nanopowders Pb 1–3x/2 Nd x Zr 0.52 Ti 0.48 O 3 (PNZT) in an ethylene glycol system with zirconium nitrate as zirconium source. The results show that it is critical to add lead acetate after the reaction of zirconium nitrate with tetrabutyl titanate in the ethylene glycol system for preparing PNZT with an exact fraction of titanium content. It has been observed that the dopant of excess Nd ions can effectively improve the sintered densification and activity of the PNZT ceramics. Piezoelectric, dielectric and ferroelectric properties of the PNZT ceramics are remarkably enhanced as compared with those of monolithic lead zirconate titanate (PZT). Especially, the supreme values of piezoelectric constant (d 33 ) and dielectric constant ( element of ) for the PNZT are both about two times that of the monolithic PZT and moreover, the remnant polarization (P r ) also increases by 30%. According to the analysis of the structures and properties, we attribute the improvement in electrical properties to the lead vacancies caused by the doping of Nd ions

  3. Characterization and microstructure of porous lead zirconate titanate ...

    Indian Academy of Sciences (India)

    Unknown

    need to have porous piezoelectric materials. These can be made by combining a PZT ceramic with a passive polymer or air phase. These materials greatly extend the range of properties offered by conventional PZT ceramics. More- over, porosity in the materials could reduce the effective acoustical impedance leading to an ...

  4. Structural Contribution to the Ferroelectric Fatigue in Lead Zirconate Titanate (PZT) Ceramics

    OpenAIRE

    Hinterstein , Manuel; Rouquette , Jerome; Haines , J; Papet , Ph; Glaum , Julia; Knapp , Michael; Eckert , J; Hoffman , M

    2014-01-01

    International audience; Many ferroelectric devices are based on doped lead zirconate titanate (PZT) ceramics with compositions near the morphotropic phase boundary (MPB), at which the relevant material's properties approach their maximum. Based on a synchrotron x-ray diffraction study of MPB PZT, bulk fatigue is unambiguously found to arise from a less effective field induced tetragonal-to-monoclinic transformation, at which the degradation of the polarization flipping is detected by a less i...

  5. Fractal cluster modeling of the fatigue behavior of lead zirconate titanate

    OpenAIRE

    Priya, Shashank; Kim, Hyeoung Woo; Ryu, Jungho; Uchino, Kenji; Viehland, Dwight D.

    2002-01-01

    The fatigue behavior of lead zirconate titanate ceramics (PZT) has been studied under electrical and mechanical drives. Piezoelectric fatigue was studied using a mechanical method. Under ac mechanical drive, hard and soft PZTs showed an increase in the longitudinal piezoelectric constant at short times, reaching a maximum at intermediate times. Systematic investigations were performed to characterize the electrical fatigue behavior. A decrease in the magnitude of the remanent polarization was...

  6. Structural contribution to the ferroelectric fatigue in lead zirconate titanate ceramics

    Science.gov (United States)

    Hinterstein, M.; Rouquette, J.; Haines, J.; Papet, Ph.; Glaum, J.; Knapp, M.; Eckert, J.; Hoffman, M.

    2014-09-01

    Many ferroelectric devices are based on doped lead zirconate titanate (PZT) ceramics with compositions near the morphotropic phase boundary (MPB), at which the relevant material's properties approach their maximum. Based on a synchrotron x-ray diffraction study of MPB PZT, bulk fatigue is unambiguously found to arise from a less effective field induced tetragonal-to-monoclinic transformation, at which the degradation of the polarization flipping is detected by a less intense and more diffuse anomaly in the atomic displacement parameter of lead. The time dependence of the ferroelectric response on a structural level down to 250 μs confirms this interpretation in the time scale of the piezolectric strain response.

  7. Characterization of lead zirconate titanate (PZT)--indium tin oxide (ITO) thin film interface

    International Nuclear Information System (INIS)

    Sreenivas, K.; Sayer, M.; Laursen, T.; Whitton, J.L.; Pascual, R.; Johnson, D.J.; Amm, D.T.

    1990-01-01

    In this paper the interface between ultrathin sputtered lead zirconate titanate (PZT) films and a conductive electrode (indium tin oxide-ITO) is investigated. Structural and compositional changes at the PZT-ITO interface have been examined by surface analysis and depth profiling techniques of glancing angle x-ray diffraction, Rutherford backscattering (RBS), SIMS, Auger electron spectroscopy (AES), and elastic recoil detection analysis (ERDA). Studies indicate significant interdiffusion of lead into the underlying ITP layer and glass substrate with a large amount of residual stress at the interface. Influence of such compositional deviations at the interface is correlated to an observed thickness dependence in the dielectric properties of PZT films

  8. Anisotropy of domain switching in prepoled lead titanate zirconate ceramics under multiaxial electrical loading

    Science.gov (United States)

    Liu, Yuan-Ming; Li, Fa-Xin; Fang, Dai-Ning

    2007-01-01

    The authors report an observation of anisotropic domain switching process in prepoled lead titanate zirconate (PZT) ceramics under multiaxial electrical loading. Prepoled PZT blocks were obliquely cut to apply an electric field at discrete angles θ (0°-180°) to the initial poling direction. Both the coercive field and switchable polarization are found to decrease significantly when sinθ increases from zero to unity. The measured strain curves show that most domains that accomplished 180° domain switching actually experienced two successive 90° switching. The oriented domain texture after poling plus the induced nonuniform stress are used to explain the observed domain switching anisotropy.

  9. Cross-poling textures in a lead zirconate titanate piezoelectric material

    International Nuclear Information System (INIS)

    Wan, Shan; Bowman, Keith J.

    2000-01-01

    Tetragonal ferroelectric materials are polarized to induce the anisotropy necessary for the piezoelectric effect. This poling of the material is inherently an orientation process. Pole figure texture measurements of poling and cross-poling in a lead zirconate titanate Navy VI material show domain motion. The resulting axisymmetric and three-dimensional textures demonstrate the contribution of 90 degree sign domain motion to piezoelectricity. Cross-poling results in strong orientations with lower applied fields than in the initial poling steps. (c) 2000 Materials Research Society

  10. Dynamic fatigue on repolarization of lead zirconate-titanate base ceramics with various ferroelectric hardness

    International Nuclear Information System (INIS)

    Gavrilyachenko, V.G.; Semenchev, A.F.; Sklyarova, E.N.; Kuznetsova, E.M.

    2006-01-01

    One studied experimentally changes of the residual polarization in lead zirconate-titanate base ceramics with various ferroelectric hardness under the effect of a strong varying field. The twinning and untwinning of crystallites accompanying repolarization is assumed to be the basic mechanism of propagation of the crystalline structure defects governing the fatigue rates of the ferroelectric-soft ceramics. In ferroelectric-hard ceramics crystallites the stable configurations of mechanical twins, the result of the secondary twinning, are formed when the hysteresis loop is formed. At repolarization in the mentioned structures one observes no motion of the twin boundaries, and the fatigue rates are low ones [ru

  11. Evolution of bias field and offset piezoelectric coefficient in bulk lead zirconate titanate with fatigue

    International Nuclear Information System (INIS)

    Zhang Yong; Baturin, Ivan S.; Aulbach, Emil; Lupascu, Doru C.; Kholkin, Andrei L.; Shur, Vladimir Ya.; Roedel, Juergen

    2005-01-01

    Hysteresis loops of the piezoelectric coefficient, d 33 =f(E 3 ), are measured on virgin and fatigued lead zirconate titanate ceramics. Four parameters are directly extracted from the measurements: internal bias field E b , offset piezoelectric coefficient d offset , coercive field E c , and remnant piezoelectric coefficient d r . The reduction in d r displays the decreasing switchable polarization with fatigue cycling. E b and d offset are found to be linearly related. After thermal annealing, both offsets disappear, while the increase in E c and the reduction in d r withstand annealing. The microscopic entities responsible for the offsets are less stable than those for reduced switching

  12. Compact piezoelectric micromotor with a single bulk lead zirconate titanate stator

    Science.gov (United States)

    Yan, Liang; Lan, Hua; Jiao, Zongxia; Chen, Chin-Yin; Chen, I.-Ming

    2013-04-01

    The advance of micro/nanotechnology promotes the development of micromotors in recent years. In this article, a compact piezoelectric ultrasonic micromotor with a single bulk lead zirconate titanate stator is proposed. A traveling wave is generated by superposition of bending modes with 90° phase difference excited by d15 inverse piezoelectric effects. The operating principle simplifies the system structure significantly, and provides a miniaturization solution. A research prototype with the size of 0.75× 0.75×1.55 mm is developed. It can produce start-up torque of 0.27μNmand maximum speed of 2760 r/min at 14RMS.

  13. Investigation of the effect of temperature on aging behavior of Fe-doped lead zirconate titanate

    Science.gov (United States)

    Promsawat, Napatporn; Promsawat, Methee; Janphuang, Pattanaphong; Marungsri, Boonruang; Luo, Zhenhua; Pojprapai, Soodkhet

    The aging degradation behavior of Fe-doped Lead zirconate titanate (PZT) subjected to different heat-treated temperatures was investigated over 1000h. The aging degradation in the piezoelectric properties of PZT was indicated by the decrease in piezoelectric charge coefficient, electric field-induced strain and remanent polarization. It was found that the aging degradation became more pronounced at temperature above 50% of the PZT’s Curie temperature. A mathematical model based on the linear logarithmic stretched exponential function was applied to explain the aging behavior. A qualitative aging model based on polar macrodomain switchability was proposed.

  14. Evolution of transverse piezoelectric response of lead zirconate titanate ceramics under hydrostatic pressure

    International Nuclear Information System (INIS)

    Li Fei; Xu Zhuo; Wei Xiaoyong; Gao Junjie; Zhang, Chonghui; Yao Xi; Jin Li

    2009-01-01

    The piezoelectric properties of 31-mode resonators of lead zirconate titanate ceramics under hydrostatic pressure from 0.1 to 325 MPa were evaluated by a fitting method, in which mechanical loss was taken into account. Our results based on the fitting method showed a hydrostatic pressure independent tendency of the piezoelectric coefficient and the electromechanical coupling factor because the adopted PZT ceramic can be considered as a linear system in our experiment, while two misleading tendencies of piezoelectric coefficient were obtained based on the resonance method when ignoring the contribution of the mechanical loss. (fast track communication)

  15. Influence of crystal phases on electro-optic properties of epitaxially grown lanthanum-modified lead zirconate titanate films

    Science.gov (United States)

    Masuda, Shin; Seki, Atsushi; Masuda, Yoichiro

    2010-02-01

    We describe here how we have improved the crystal qualities and controlled the crystal phase of the lanthanum-modified lead zirconate titanate (PLZT) film without changing the composition ratio using an oxygen-pressure crystallization process. A PLZT film deposited on a SrTiO3 substrate with the largest electro-optic (EO) coefficient of 498 pm/V has been achieved by controlling the crystal phase of the film. Additionally, a fatigue-free lead zirconate titanate (PZT) capacitor with platinum electrodes has been realized by reducing the oxygen vacancies in the films.

  16. Comparison of chemical solution deposition systems for the fabrication of lead zirconate titanate thin films

    International Nuclear Information System (INIS)

    Lecarpentier, F.; Daglish, M.; Kemmitt, T.

    2001-01-01

    Ferroelectric thin films of lead zirconate titanate Pb(Zr x Ti 1-x )O 3 (PZT) were prepared from five chemical solution deposition (CSD) systems, namely methoxyethanol, citrate, diol, acetic acid and triethanolamine. Physical characteristics of the solutions, processing parameters and physical and electrical properties of the films were used to assess the relative advantages and disadvantages of the different chemical systems. All the CSD systems decomposed to produce single phase perovskite PZT at temperatures above 650 deg C. Thin film deposition was influenced by the specific characteristics of each system such as wetting on the substrate and viscosity. Distinct precursor effects on the thin film crystallinity and electrical performance were revealed. The diol route yielded films with the highest crystallite size, highest permittivity and lowest loss tangent. The relative permittivity exhibited by films made by the other routes were 25% to 35% lower at equivalent thicknesses. Copyright (2001) The Australian Ceramic Society

  17. Piezoelectric and dielectric performance of poled lead zirconate titanate subjected to electric cyclic fatigue

    Science.gov (United States)

    Wang, Hong; Matsunaga, Tadashi; Lin, Hua-Tay; Mottern, Alexander M.

    2012-02-01

    Poled lead zirconate titanate (PZT) material as a single-layer plate was tested using a piezodilatometer under electric cyclic loading in both unipolar and bipolar modes. Its responses were evaluated using unipolar and bipolar measurements on the same setup. The mechanical strain and charge density loops exhibited various variations when the material was cycled for more than 108 cycles. The various quantities including loop amplitude, hysteresis, switchable polarization, and coercive field were characterized accordingly under the corresponding measurement conditions. At the same time, the offset polarization and bias electric field of the material were observed to be changed and the trend was found to be related to the measurement conditions also. Finally, the piezoelectric and dielectric coefficients were analyzed and their implications for the application of interest have been discussed.

  18. Electrical fatigue behaviour in lead zirconate titanate: an experimental and theoretical study

    International Nuclear Information System (INIS)

    Bhattacharyya, Mainak; Arockiarajan, A

    2013-01-01

    A systematic investigation on electrical fatigue in lead zirconate titanate (PZT) is carried out for different loading frequencies. Experiments are conducted up to 10 6 cycles to measure the electrical displacement and longitudinal strain on bulk ceramics in the bipolar mode with large electrical loading conditions. A simplified macroscopic model based on physical mechanisms of domain switching is developed to predict the non-linear behaviour. In this model, the volume fraction of a domain is used as the internal variable by considering the mechanisms of domain nucleation and propagation (domain wall movement). The measured material properties at different fatigue cycles are incorporated into the switching model as damage parameters and the classical strain versus electric field and electric displacement versus electric field curves are simulated. Comparison between the experiments and simulations shows that the proposed model can reproduce the characteristics of non-linear as well as fatigue responses. (paper)

  19. Fatigue-free lead zirconate titanate-based capacitors for nonvolatile memories

    International Nuclear Information System (INIS)

    Shannigrahi, S. R.; Jang, Hyun M.

    2001-01-01

    The development of lead zirconate titanate (PZT)-based capacitors has been a long time goal of ferroelectric random access memories (FRAM). However, PZT-based perovskites with common platinum (Pt) electrodes have suffered from a significant reduction of the remanent polarization (P r ) after a certain number of read/write cycles (electrical fatigue). We now report the development of fatigue-free lanthanum-modified PZT capacitors using common Pt electrodes. The capacitors fabricated at 580 o C by applying a PZT seed layer exhibited fatigue-free behavior up to 6.5 x 10 10 switching cycles, a quite stable charge retention profile with time, and comparatively high P r values, all of which assure their suitability for practical FRAM applications. Copyright 2001 American Institute of Physics

  20. Piezoelectric and dielectric performance of poled lead zirconate titanate subjected to electric cyclic fatigue

    International Nuclear Information System (INIS)

    Wang, Hong; Matsunaga, Tadashi; Lin, Hua-Tay; Mottern, Alexander M

    2012-01-01

    Poled lead zirconate titanate (PZT) material as a single-layer plate was tested using a piezodilatometer under electric cyclic loading in both unipolar and bipolar modes. Its responses were evaluated using unipolar and bipolar measurements on the same setup. The mechanical strain and charge density loops exhibited various variations when the material was cycled for more than 10 8 cycles. The various quantities including loop amplitude, hysteresis, switchable polarization, and coercive field were characterized accordingly under the corresponding measurement conditions. At the same time, the offset polarization and bias electric field of the material were observed to be changed and the trend was found to be related to the measurement conditions also. Finally, the piezoelectric and dielectric coefficients were analyzed and their implications for the application of interest have been discussed. (paper)

  1. Fatigue responses of lead zirconate titanate stacks under semibipolar electric cycling with mechanical preload

    Science.gov (United States)

    Wang, Hong; Cooper, Thomas A.; Lin, Hua-Tay; Wereszczak, Andrew A.

    2010-10-01

    Lead zirconate titanate (PZT) stacks that had an interdigital internal electrode configuration were tested to more than 108 cycles. A 100 Hz semibipolar sine wave with a field range of +4.5/-0.9 kV/mm was used in cycling with a concurrently-applied 20 MPa preload. Significant reductions in piezoelectric and dielectric responses were observed during the cycling depending on the measuring condition. Extensive partial discharges were also observed. These surface events resulted in the erosion of external electrode and the exposure of internal electrodes. Sections prepared by sequential polishing technique revealed a variety of damage mechanisms including delaminations, pores, and etch grooves. The scale of damage was correlated with the degree of fatigue-induced reduction in piezoelectric and dielectric responses. The results from this study demonstrate the feasibility of using a semibipolar mode to drive a PZT stack under a mechanical preload and illustrate the potential fatigue and damages of the stack in service.

  2. Electrical fatigue behaviour in lead zirconate titanate: an experimental and theoretical study

    Science.gov (United States)

    Bhattacharyya, Mainak; Arockiarajan, A.

    2013-08-01

    A systematic investigation on electrical fatigue in lead zirconate titanate (PZT) is carried out for different loading frequencies. Experiments are conducted up to 106 cycles to measure the electrical displacement and longitudinal strain on bulk ceramics in the bipolar mode with large electrical loading conditions. A simplified macroscopic model based on physical mechanisms of domain switching is developed to predict the non-linear behaviour. In this model, the volume fraction of a domain is used as the internal variable by considering the mechanisms of domain nucleation and propagation (domain wall movement). The measured material properties at different fatigue cycles are incorporated into the switching model as damage parameters and the classical strain versus electric field and electric displacement versus electric field curves are simulated. Comparison between the experiments and simulations shows that the proposed model can reproduce the characteristics of non-linear as well as fatigue responses.

  3. Conformable amplified lead zirconate titanate sensors with enhanced piezoelectric response for cutaneous pressure monitoring.

    Science.gov (United States)

    Dagdeviren, Canan; Su, Yewang; Joe, Pauline; Yona, Raissa; Liu, Yuhao; Kim, Yun-Soung; Huang, YongAn; Damadoran, Anoop R; Xia, Jing; Martin, Lane W; Huang, Yonggang; Rogers, John A

    2014-08-05

    The ability to measure subtle changes in arterial pressure using devices mounted on the skin can be valuable for monitoring vital signs in emergency care, detecting the early onset of cardiovascular disease and continuously assessing health status. Conventional technologies are well suited for use in traditional clinical settings, but cannot be easily adapted for sustained use during daily activities. Here we introduce a conformal device that avoids these limitations. Ultrathin inorganic piezoelectric and semiconductor materials on elastomer substrates enable amplified, low hysteresis measurements of pressure on the skin, with high levels of sensitivity (~0.005 Pa) and fast response times (~0.1 ms). Experimental and theoretical studies reveal enhanced piezoelectric responses in lead zirconate titanate that follow from integration on soft supports as well as engineering behaviours of the associated devices. Calibrated measurements of pressure variations of blood flow in near-surface arteries demonstrate capabilities for measuring radial artery augmentation index and pulse pressure velocity.

  4. Research on output signal of piezoelectric lead zirconate titanate detector using Monte Carlo method

    Energy Technology Data Exchange (ETDEWEB)

    Takechi, Seiji, E-mail: takechi@elec.eng.osaka-cu.ac.jp [Graduate School of Engineering, Osaka City University, Osaka 558-8585 (Japan); Mitsuhashi, Tomoaki; Miura, Yoshinori [Graduate School of Engineering, Osaka City University, Osaka 558-8585 (Japan); Miyachi, Takashi; Kobayashi, Masanori; Okudaira, Osamu [Planetary Exploration Research Center, Chiba Institute of Technology, Narashino, Chiba 275-0016 (Japan); Shibata, Hiromi [The Institute of Scientific and Industrial Research, Osaka University, Ibaraki, Osaka 567-0047 (Japan); Fujii, Masayuki [Famscience Co., Ltd., Tsukubamirai, Ibaraki 300-2435 (Japan); Okada, Nagaya [Honda Electronics Co., Ltd., Toyohashi, Aichi 441-3193 (Japan); Murakami, Takeshi; Uchihori, Yukio [National Institute of Radiological Sciences, Chiba 263-8555 (Japan)

    2017-06-21

    The response of a radiation detector fabricated from piezoelectric lead zirconate titanate (PZT) was studied. The response signal due to a single 400 MeV/n xenon (Xe) ion was assumed to have a simple form that was composed of two variables, the amplitude and time constant. These variables were estimated by comparing two output waveforms obtained from a computer simulation and an experiment on Xe beam irradiation. Their values appeared to be dependent on the beam intensity. - Highlights: • The performance of PZT detector was studied by irradiation of a 400 MeV/n Xe beam. • Monte Carlo simulation was used to examine the formation process of the output. • The response signal due to a single Xe ion was assumed to have a simple form. • The form was composed of two variables, the amplitude and time constant. • These variables appeared to be dependent on the beam intensity.

  5. Substrate clamping effects on irreversible domain wall dynamics in lead zirconate titanate thin films.

    Science.gov (United States)

    Griggio, F; Jesse, S; Kumar, A; Ovchinnikov, O; Kim, H; Jackson, T N; Damjanovic, D; Kalinin, S V; Trolier-McKinstry, S

    2012-04-13

    The role of long-range strain interactions on domain wall dynamics is explored through macroscopic and local measurements of nonlinear behavior in mechanically clamped and released polycrystalline lead zirconate-titanate (PZT) films. Released films show a dramatic change in the global dielectric nonlinearity and its frequency dependence as a function of mechanical clamping. Furthermore, we observe a transition from strong clustering of the nonlinear response for the clamped case to almost uniform nonlinearity for the released film. This behavior is ascribed to increased mobility of domain walls. These results suggest the dominant role of collective strain interactions mediated by the local and global mechanical boundary conditions on the domain wall dynamics. The work presented in this Letter demonstrates that measurements on clamped films may considerably underestimate the piezoelectric coefficients and coupling constants of released structures used in microelectromechanical systems, energy harvesting systems, and microrobots.

  6. Surface bond contraction and its effect on the nanometric sized lead zirconate titanate

    International Nuclear Information System (INIS)

    Haitao Huang; Sun, Chang Q.; Hing, Peter

    2000-01-01

    The grain size effect of lead zirconate titanate PbZr 1-x Ti x O 3 (PZT, x≥0.6) caused by surface bond contraction has been investigated by using the Landau-Ginsburg-Devonshire (LGD) phenomenological theory. It has been shown that, due to the surface bond contraction, both the Curie temperature and the spontaneous polarization of tetragonal PZT decrease with decreasing grain size. These effects become more significant when the grain size is in the nanometre range. A dielectric anomaly appears with decreasing grain size, which corresponds to a size dependent phase transformation. The ferroelectric critical size below which a loss of ferroelectricity will happen is estimated from the results obtained. (author). Letter-to-the-editor

  7. Output characteristics of piezoelectric lead zirconate titanate detector using high-energy heavy-ion beam

    International Nuclear Information System (INIS)

    Takechi, Seiji; Sekiguchi, Masahiro; Miyachi, Takashi; Kobayashi, Masanori; Hattori, Maki; Okudaira, Osamu; Shibata, Hiromi; Fujii, Masayuki; Okada, Nagaya; Murakami, Takeshi; Uchihori, Yukio

    2014-01-01

    A radiation detector fabricated using piezoelectric lead zirconate titanate (PZT) has been studied by irradiating it with a 400 MeV/n xenon (Xe) beam. The beam diameter was controlled to change the irradiation conditions. It was found that the magnitude of the output observed from the PZT detector may be related to the number of Xe ions per unit area per unit time within the limits of the experimental conditions. -- Highlights: • The performance of PZT detector was studied by irradiation of a 400 MeV/n Xe beam. • The beam diameter was controlled to change the irradiation conditions. • By the control, the number of Xe ions per one pulse was changed from ∼500 to ∼1500. • The output of the PZT detector was not always larger with more intense beam. • The energy of Xe ions per unit area per unit time may determine the output

  8. Patterning lead zirconate titanate nanostructures at sub-200-nm resolution by soft confocal imprint lithography and nanotransfer molding

    NARCIS (Netherlands)

    Khan, Sajid; Göbel, Ole; Blank, David H.A.; ten Elshof, Johan E.

    2009-01-01

    Patterned sol-gel-derived lead zirconate titanate (PZT) thin films with lateral resolutions down to 100 nm on silicon are reported. Both an imprint and a transfer-molding method were employed. The formed patterns after annealing were characterized with scanning electron microscopy, atomic force

  9. On the use of non-MPB lead zirconium titanate (PZT) granules for piezoelectric ceramic–polymer sensorial composites

    NARCIS (Netherlands)

    Shaji Karapuzha, A.; Kunnamkuzhakkal James, N.; van der Zwaag, S.; Groen, W.A.

    2016-01-01

    Modern flexible and sensitive sensors based on polymer–ceramic composites employ lead zirconate titanate (PZT) granulates having the morphotropic phase boundary (MPB) composition as the piezo active ingredient, as this composition gives the best properties in fully ceramic piezoelectric sensors.

  10. On the use of non-MPB lead zirconium titanate (PZT) granules for piezoelectric ceramic–polymer sensorial composites

    NARCIS (Netherlands)

    Shaji Karapuzha, A.; Zwaag, S. van der; Groen, W.A.

    2016-01-01

    Modern flexible and sensitive sensors based on polymer–ceramic composites employ lead zirconate titanate (PZT) granulates having the morphotropic phase boundary (MPB) composition as the piezo active ingredient, as this composition gives the best properties in fully ceramic piezoelectric sensors. In

  11. The effect of physiologic aqueous solutions on the perovskite material lead-lanthanum-zirconium titanate (PLZT)

    Science.gov (United States)

    Foster, William J.; Meen, James K.; Fox, Donald A.

    2016-01-01

    Context Perovskite compounds, including Lead-Lanthanum-Zirconium Titanate (PLZT), have wide technological application because of their unique physical properties. The use of PLZT in neuro-prosthetic systems, such as retinal implants, have been discussed in a number of publications. Since inorganic lead is a retinotoxic compound that produces retinal degeneration, the long-term stability of PLZT in aqueous biological solutions must be determined. Objective We evaluated the stability and effects of prolonged immersion of a PLZT-coated crystal in a buffered balanced salt solution. Materials and Methods Scanning Electron Microscopy and Electron Dispersive Spectroscopy (EDS) using a JEOL JSM 5410 microscope equipped with EDS were utilized to evaluate the samples before and after prolonged immersion. Results We found that lead and other constituents of PLZT leached into the surrounding aqueous medium. Discussion By comparing the unit cell of PLZT with that of CaTiO3, which has been found to react with aqueous fluids, Lead is in the same site in PLZT as Ca is in CaTiO3. It is thus reasonable that PLZT will react with aqueous solutions. Conclusion The results suggest that PLZT must either be coated with a protective layer or is not appropriate for long-term in vivo or in vitro biological applications. PMID:22697294

  12. Characterization of dense lead lanthanum titanate ceramics prepared from powders synthesized by the oxidant peroxo method

    Energy Technology Data Exchange (ETDEWEB)

    Pinto, Alexandre H. [LIEC-Laboratorio Interdisciplinar de Eletroquimica e Ceramica, Departamento de Quimica, UFSCar-Universidade Federal de Sao Carlos, Rod.Washington Luis km 235, CP 676 Sao Carlos, SP 13565-905 (Brazil); Souza, Flavio L., E-mail: flavio.souza@ufabc.edu.br [Centro de Ciencias Naturais e Humanas, Universidade Federal do ABC, Rua Santa Adelia 166, Bangu, Santo Andre, SP 09210-170 (Brazil); Chiquito, Adenilson J., E-mail: chiquito@df.ufscar.br [Departamento de Fisica, UFSCar-Federal University of Sao Carlos, Rod.Washington Luis km 235, CP 676 Sao Carlos, SP 13565-905 (Brazil); Longo, Elson, E-mail: elson@iq.unesp.br [Instituto de Quimica de Araraquara, UNESP-Universidade Estadual Paulista, Rua Francisco Degni, CP 355 Araraquara, SP 14801-907 (Brazil); Leite, Edson R., E-mail: derl@power.ufscar.br [LIEC-Laboratorio Interdisciplinar de Eletroquimica e Ceramica, Departamento de Quimica, UFSCar-Universidade Federal de Sao Carlos, Rod.Washington Luis km 235, CP 676 Sao Carlos, SP 13565-905 (Brazil); Camargo, Emerson R., E-mail: camargo@ufscar.br [LIEC-Laboratorio Interdisciplinar de Eletroquimica e Ceramica, Departamento de Quimica, UFSCar-Universidade Federal de Sao Carlos, Rod.Washington Luis km 235, CP 676 Sao Carlos, SP 13565-905 (Brazil)

    2010-12-01

    Nanosized powders of lead lanthanum titanate (Pb{sub 1-x}La{sub x}TiO{sub 3}) were synthesized by means of the oxidant-peroxo method (OPM). Lanthanum was added from 5 to 30% in mol through the dissolution of lanthanum oxide in nitric acid, followed by the addition of lead nitrate to prepare a solution of lead and lanthanum nitrates, which was dripped into an aqueous solution of titanium peroxo complexes, forming a reactive amorphous precipitate that could be crystallized by heat treatment. Crystallized powders were characterized by FT-Raman spectroscopy and X-ray powder diffraction, showing that tetragonal perovskite structure is obtained for samples up to 25% of lanthanum and cubic perovskite for samples with 30% of lanthanum. Powders containing 25 and 30% in mol of lanthanum were calcined at 700 deg. C for 2 h, and in order to determine the relative dielectric permittivity and the phase transition behaviour from ferroelectric-to-paraelectric, ceramic pellets were prepared and sintered at 1100 or 1150 deg. C for 2 h and subjected to electrical characterization. It was possible to observe that sample containing 25% in mol of La presented a normal behaviour for the phase transition, whereas the sample containing 30% in mol of La presented a diffuse phase transition and relaxor behaviour.

  13. Characterization of dense lead lanthanum titanate ceramics prepared from powders synthesized by the oxidant peroxo method

    International Nuclear Information System (INIS)

    Pinto, Alexandre H.; Souza, Flavio L.; Chiquito, Adenilson J.; Longo, Elson; Leite, Edson R.; Camargo, Emerson R.

    2010-01-01

    Nanosized powders of lead lanthanum titanate (Pb 1-x La x TiO 3 ) were synthesized by means of the oxidant-peroxo method (OPM). Lanthanum was added from 5 to 30% in mol through the dissolution of lanthanum oxide in nitric acid, followed by the addition of lead nitrate to prepare a solution of lead and lanthanum nitrates, which was dripped into an aqueous solution of titanium peroxo complexes, forming a reactive amorphous precipitate that could be crystallized by heat treatment. Crystallized powders were characterized by FT-Raman spectroscopy and X-ray powder diffraction, showing that tetragonal perovskite structure is obtained for samples up to 25% of lanthanum and cubic perovskite for samples with 30% of lanthanum. Powders containing 25 and 30% in mol of lanthanum were calcined at 700 deg. C for 2 h, and in order to determine the relative dielectric permittivity and the phase transition behaviour from ferroelectric-to-paraelectric, ceramic pellets were prepared and sintered at 1100 or 1150 deg. C for 2 h and subjected to electrical characterization. It was possible to observe that sample containing 25% in mol of La presented a normal behaviour for the phase transition, whereas the sample containing 30% in mol of La presented a diffuse phase transition and relaxor behaviour.

  14. Orientation of rapid thermally annealed lead zirconate titanate thin films on (111) Pt substrate

    International Nuclear Information System (INIS)

    Brooks, K.G.; Reaney, I.M.; Klissurska, R.; Huang, Y.; Bursill, L.A.; Setter, N.

    1994-01-01

    The nucleation, growth and orientation of lead zirconate titanate thin films prepared from organometallic precursor solutions by spin coating on (111) oriented platinum substrates and crystallized by rapid thermal annealing was investigated. The effects of pyrolysis temperature, post-pyrolysis thermal treatments, excess lead addition, and Nb dopant substitution are reported. The use of post pyrolysis oxygen anneals at temperatures in the regime of 350-450 deg C was found to strongly effect the kinetics of subsequent amorphous-pyrochlore perovskite crystallization by rapid thermal annealing. It has also allowed films of reproducible microstructure and textures (both (100) and (111)) to be prepared by rapid thermal annealing. It is suggested that such anneals and pyrolysis temperature affect the oxygen concentration/average Pb valence in the amorphous films prior to annealing. The changes in Pb valence state then affect the stability of the transient pyrochlore phase and thus the kinetics of perovskite crystallization. Nb dopant was also found to influence the crystallization kinetics. 28 refs., 18 figs

  15. Synthesis and characterization of lead zirconate titanate powders obtained by the oxidant peroxo method

    Energy Technology Data Exchange (ETDEWEB)

    Camargo, Emerson R. [LIEC-Laboratorio Interdisciplinar de Eletroquimica e Ceramica, Department of Chemistry, UFSCar-Federal University of Sao Carlos, Rod. Washington Luis km 235, CP 676, Sao Carlos SP, 13565-905 (Brazil)], E-mail: camargo@ufscar.br; Leite, Edson R. [LIEC-Laboratorio Interdisciplinar de Eletroquimica e Ceramica, Department of Chemistry, UFSCar-Federal University of Sao Carlos, Rod. Washington Luis km 235, CP 676, Sao Carlos SP, 13565-905 (Brazil)], E-mail: derl@power.ufscar.br; Longo, Elson [Department of Biochemistry, Chemistry Institute of Araraquara, UNESP, Sao Paulo State University Rua Francisco Degni, CP 355 Araraquara SP, 14801-907 Brazil (Brazil)], E-mail: elson@iq.unesp.br

    2009-02-05

    Lead zirconate titanate (PbZr{sub 1-x}Ti{sub x}O{sub 3}) was synthesized by the 'oxidant peroxo method (OPM)' with 'x' between 0.25 and 0.50. Titanium metal was dissolved into a hydrogen peroxide/ammonia aqueous solution, followed by the addition of lead and zirconium nitrate solution. The amorphous precipitated precursor obtained was crystallized by heat treatment between 400 and 1000 deg. C. Images of transmission microscopy showed spherical particles with average diameter between 20 and 60 nm, and the presence of necks between particles treated at 700 deg. C. All of the unpressed powders were characterized by X-ray diffractometry and FT-Raman spectroscopy. Powder samples with 'x' up to 0.35 showed rhombohedral structure when treated at temperatures higher than 500 deg. C, and tetragonal structure when 'x' was higher than 0.40. Analysis of XRD and Raman spectroscopy of the precursor powders showed amorphous-like structures, however powders treated at 400 deg. C showed a structure identified as an intermediate pyrochlore phase, independently of the Zr and Ti mole ratio.

  16. Nanosized lead lanthanum titanate (PLT) ceramic powders synthesized by the oxidant peroxo method

    Energy Technology Data Exchange (ETDEWEB)

    Camargo, Emerson R. [LIEC-Laboratorio Interdisciplinar de Eletroquimica e Ceramica, Department of Chemistry, UFSCar-Federal University of Sao Carlos, Rod.Washingtin Luis km 235, CP 676, Sao Carlos SP 13565-9905 (Brazil)], E-mail: camargo@ufscar.br; Barrado, Cristiano M. [LIEC-Laboratorio Interdisciplinar de Eletroquimica e Ceramica, Department of Chemistry, UFSCar-Federal University of Sao Carlos, Rod.Washingtin Luis km 235, CP 676, Sao Carlos SP 13565-9905 (Brazil); Ribeiro, Caue [EMBRAPA Instrumentacao Agropecuaria, Rua XV de Novembro 1452, Sao Carlos SP 13560-970 (Brazil)], E-mail: caue@cnpdia.embrapa.br; Longo, Elson [Department of Biochemistry, Chemistry Institute of Araraquara, UNESP-Sao Paulo State University, Rua Francisco Degni, CP 355, Araraquara SP 14801-907 (Brazil)], E-mail: elson@iq.unesp.br; Leite, Edson R. [LIEC-Laboratorio Interdisciplinar de Eletroquimica e Ceramica, Department of Chemistry, UFSCar-Federal University of Sao Carlos, Rod.Washingtin Luis km 235, CP 676, Sao Carlos SP 13565-9905 (Brazil)], E-mail: derl@power.ufscar.br

    2009-05-05

    For the first time it is reported the synthesis of lead titanate modified with rare earth by the oxidant-peroxo method (OPM). Lanthanum was added up to 20% in mol through the dissolution of lanthanum oxide in nitric acid, followed by the addition of a solution of lead and lanthanum nitrate into an aqueous solution of titanium peroxo complexes. The amorphous precipitate formed was heat-treated at different temperatures in the range from 400 to 900 deg. C for crystallization. Powders were characterized by Raman spectroscopy and X-ray diffraction. Tetragonal perovskite structure was observed for the samples up to 15% of lanthanum substitution and cubic perovskite for sample with 20% of lanthanum. Crystallographic domains calculated by Scherrer equation showing a probable suppression of the crystallite growth in function of lanthanum content. It was observed shifting to lower frequencies of Raman modes in the range between 100 and 400 cm{sup -1} and the vanishing of the A1(2TO) and E(1LO) modes could be attributed to transition phase from tetragonal to cubic. Electronic microscopy image revealed that the powders annealed at height temperature are spherical with sharp size distribution.

  17. Synthesis and characterization of lead zirconate titanate powders obtained by the oxidant peroxo method

    International Nuclear Information System (INIS)

    Camargo, Emerson R.; Leite, Edson R.; Longo, Elson

    2009-01-01

    Lead zirconate titanate (PbZr 1-x Ti x O 3 ) was synthesized by the 'oxidant peroxo method (OPM)' with 'x' between 0.25 and 0.50. Titanium metal was dissolved into a hydrogen peroxide/ammonia aqueous solution, followed by the addition of lead and zirconium nitrate solution. The amorphous precipitated precursor obtained was crystallized by heat treatment between 400 and 1000 deg. C. Images of transmission microscopy showed spherical particles with average diameter between 20 and 60 nm, and the presence of necks between particles treated at 700 deg. C. All of the unpressed powders were characterized by X-ray diffractometry and FT-Raman spectroscopy. Powder samples with 'x' up to 0.35 showed rhombohedral structure when treated at temperatures higher than 500 deg. C, and tetragonal structure when 'x' was higher than 0.40. Analysis of XRD and Raman spectroscopy of the precursor powders showed amorphous-like structures, however powders treated at 400 deg. C showed a structure identified as an intermediate pyrochlore phase, independently of the Zr and Ti mole ratio

  18. Nanosized lead lanthanum titanate (PLT) ceramic powders synthesized by the oxidant peroxo method

    International Nuclear Information System (INIS)

    Camargo, Emerson R.; Barrado, Cristiano M.; Ribeiro, Caue; Longo, Elson; Leite, Edson R.

    2009-01-01

    For the first time it is reported the synthesis of lead titanate modified with rare earth by the oxidant-peroxo method (OPM). Lanthanum was added up to 20% in mol through the dissolution of lanthanum oxide in nitric acid, followed by the addition of a solution of lead and lanthanum nitrate into an aqueous solution of titanium peroxo complexes. The amorphous precipitate formed was heat-treated at different temperatures in the range from 400 to 900 deg. C for crystallization. Powders were characterized by Raman spectroscopy and X-ray diffraction. Tetragonal perovskite structure was observed for the samples up to 15% of lanthanum substitution and cubic perovskite for sample with 20% of lanthanum. Crystallographic domains calculated by Scherrer equation showing a probable suppression of the crystallite growth in function of lanthanum content. It was observed shifting to lower frequencies of Raman modes in the range between 100 and 400 cm -1 and the vanishing of the A1(2TO) and E(1LO) modes could be attributed to transition phase from tetragonal to cubic. Electronic microscopy image revealed that the powders annealed at height temperature are spherical with sharp size distribution.

  19. Characterisation of glass matrix composites reinforced with lead zirconate titanate particles

    International Nuclear Information System (INIS)

    Cannillo, Valeria; Manfredini, Tiziano; Montorsi, Monia; Tavoni, Francesca; Minay, Emma J.; Boccaccini, Aldo R.

    2005-01-01

    A new type of glass matrix composite reinforced with ferroelectric particulate secondary phase was investigated. Samples containing lead zirconate titanate (PZT) particles in a silicate lead glass were fabricated. Various sintering strategies were tested in order to optimise the processing route. The densest samples were obtained by hot-pressing. The composites were characterized by means of SEM observations, X-ray diffraction, differential thermal analysis and Vickers indentations. In order to get a deeper insight into the thermo-mechanical behaviour of the material, a FEM based numerical model was prepared and applied. In particular, the crack-particle interaction was assessed and thus possible toughening mechanisms were investigated. By means of the numerical modelling supported by SEM observations, traditional toughening mechanisms (e.g. crack deflection, particle debonding) were ruled out. Since the experimentally measured indentation fracture toughness of the composite is significantly higher than that of the unreinforced glass, the findings suggest that a new toughening mechanism may be active, based on the piezoelectric effect

  20. Scandium, yttrium and the lanthanides

    International Nuclear Information System (INIS)

    Hart, F.A.

    1987-01-01

    This chapter on the chemistry of the coordination complexes of scandium, yttrium and the lanthanides includes sections on the nitrogen and oxygen donor ligands and complex halides of scandium, and the phosphorus and sulfur donor ligands of yttrium and the lanthanides. Complexes with the macrocylic ligands and with halides are also discussed. Sections on the NMR and electronic spectra of the lanthanides are also included. (UK)

  1. Retention Behaviour of Copper, Zinc, Cadmium and Lead Ions on Synthesized Zirconium Titanate Ion Exchanger

    International Nuclear Information System (INIS)

    El-Naggar, I.M.; Abdel-Galil, E.A.; Moustafa, M.E.; Mahmoud, M.Y.

    2013-01-01

    Zr(IV) titanate as inorganic ion exchange material has been synthesized and utilized as the adsorbent for the removal of Cu 2+ , Zn 2+ , Cd 2+ and Pb 2+ ions from aqueous waste solutions. The experimental data were analyzed by Langmuir and Freundlich models of adsorption. The results suggest that the adsorption of the studied metals Cu 2+ , Zn 2+ , Cd 2+ and Pb 2+ ions on Zr(IV) titanate was favourable for the Freundlich isotherm more than Langmuir isotherm. The numerical values of 1/n for the studied metal ions were found to be smaller than the one (1/n L ) was found to be R L > 1 which confirmed that the prepared Zr(IV) titanate unfavourable the Langmuir isotherm. Based on the obtained results, practical separation experiments for the above mentioned cations on Zr(IV) titanate (ZrTi) column from aqueous waste solutions were carried out.

  2. Scandium Terminal Imido Chemistry.

    Science.gov (United States)

    Lu, Erli; Chu, Jiaxiang; Chen, Yaofeng

    2018-02-20

    Research into transition metal complexes bearing multiply bonded main-group ligands has developed into a thriving and fruitful field over the past half century. These complexes, featuring terminal M═E/M≡E (M = transition metal; E = main-group element) multiple bonds, exhibit unique structural properties as well as rich reactivity, which render them attractive targets for inorganic/organometallic chemists as well as indispensable tools for organic/catalytic chemists. This fact has been highlighted by their widespread applications in organic synthesis, for example, as olefin metathesis catalysts. In the ongoing renaissance of transition metal-ligand multiple-bonding chemistry, there have been reports of M═E/M≡E interactions for the majority of the metallic elements of the periodic table, even some actinide metals. In stark contrast, the largest subgroup of the periodic table, rare-earth metals (Ln = Sc, Y, and lanthanides), have been excluded from this upsurge. Indeed, the synthesis of terminal Ln═E/Ln≡E multiple-bonding species lagged behind that of the transition metal and actinide congeners for decades. Although these species had been pursued since the discovery of a rare-earth metal bridging imide in 1991, such a terminal (nonpincer/bridging hapticities) Ln═E/Ln≡E bond species was not obtained until 2010. The scarcity is mainly attributed to the energy mismatch between the frontier orbitals of the metal and the ligand atoms. This renders the putative terminal Ln═E/Ln≡E bonds extremely reactive, thus resulting in the formation of aggregates and/or reaction with the ligand/environment, quenching the multiple-bond character. In 2010, the stalemate was broken by the isolation and structural characterization of the first rare-earth metal terminal imide-a scandium terminal imide-by our group. The double-bond character of the Sc═N bond was unequivocally confirmed by single-crystal X-ray diffraction. Theoretical investigations revealed the presence

  3. Develop techniques for ion implantation of PLZT [lead-lanthanum-zirconate-titanate] for adaptive optics

    International Nuclear Information System (INIS)

    Batishko, C.R.; Brimhall, J.L.; Pawlewicz, W.T.; Stahl, K.A.; Toburen, L.H.

    1987-09-01

    Research was conducted at Pacific Northwest Laboratory to develop high photosensitivity adaptive optical elements utilizing ion implanted lanthanum-doped lead-zirconate-titanate (PLZT). One centimeter square samples were prepared by implanting ferroelectric and anti-ferroelectric PLZT with a variety of species or combinations of species. These included Ne, O, Ni, Ne/Cr, Ne/Al, Ne/Ni, Ne/O, and Ni/O, at a variety of energies and fluences. An indium-tin oxide (ITO) electrode coating was designed to give a balance of high conductivity and optical transmission at near uv to near ir wavelengths. Samples were characterized for photosensitivity; implanted layer thickness, index of refraction, and density; electrode (ITO) conductivity; and in some cases, residual stress curvature. Thin film anti-ferroelectric PLZT was deposited in a preliminary experiment. The structure was amorphous with x-ray diffraction showing the beginnings of a structure at substrate temperatures of approximately 550 0 C. This report summarizes the research and provides a sampling of the data taken during the report period

  4. Effect of compositional variations in the lead lanthanum zirconate stannate titanate system on electrical properties

    International Nuclear Information System (INIS)

    Markowski, K.; Park, S.E.; Yoshikawa, Shoko; Cross, L.E.

    1996-01-01

    The purpose of this work was to evaluate the effect of compositional modifications on the electrical properties of lead lanthanum zirconate stannate titanate (PLZST) ceramics, as well as to examine their electrically induced phase-change behavior. Variations in the Ti:Sn ratio were evaluated. Increased Ti 4+ content produced the following: decreased switching field, related to an increased antiferroelectric-ferroelectric (AFE-FE) transition temperature; constant hysteresis (ΔE) correlated with a constant temperature of the maximum dielectric constant (T max ); a sharper dielectric-constant maximum peak; and increased room-temperature dielectric constant (K). Variations in the Zr:Sn ratio also were evaluated. Increased Zr 4+ content produced the following: increased hysteresis with increased T max , decreased maximum dielectric constant, and decreased switching field with increased AFE-FE transition temperature (T AFE-FE ). From these results, with respect to compositional modifications, the AFE-FE switching field (E AFE-FE ) and ΔE were observed to be dependent strongly on T AFE-FE and T max , respectively. Negligible change existed in the strain achievable at the switching field, which remained constant for all compositions at ∼0.16%. The significance of this research was the ability demonstrated to tailor the properties of phase-change materials through compositional modifications

  5. Chemical solution deposited BaPbO3 buffer layers for lead zirconate titanate ferroelectric films

    International Nuclear Information System (INIS)

    Tseng, T.-K.; Wu, J.-M.

    2005-01-01

    Conductive perovskite BaPbO 3 (BPO) films have been prepared successfully by chemical solution deposition method through spin-coating on Pt/Ti/SiO 2 /Si substrates. The choice of baking temperature is a key factor on the development of conducting BPO perovskite phase. When the baking temperature is higher than 350 deg. C, the BPO films contain a high content of BaCO 3 phase after annealing at temperatures higher than 500 deg. C. If the baking temperature is chosen lower than 300 deg. C, such as 200 deg. C, the annealed BPO films consist mostly of perovskite with only traces of BaCO 3 . Choosing 200 deg. C as the baking temperature, the BPO films developed single perovskite phase at temperatures as low as 550 deg. C. The perovskite BPO phase is stable in the range of 550-650 deg. C and the measured sheet resistance of the BPO films is about 2-3 Ω/square. The perovskite BPO film as a buffer layer provides improvement in electric properties of lead zirconate titanate films

  6. Lead titanate/cyclic carbonate dependence on ionic conductivity of ferro/acrylate blend polymer composites

    Energy Technology Data Exchange (ETDEWEB)

    Jayaraman, R. [Department of Physics, GTN Arts and Science College, Dindigul (India); Vickraman, P., E-mail: vrsvickraman@yahoo.com; Subramanian, N. M. V.; Justin, A. Simon [Department of Physics, Gandhigram Rural Institute- Deemed University, Gandhigram (India)

    2016-05-23

    Impedance, XRD, DSC and FTIR studies had been carried out for PVdF-co-HFP/LIBETI based system for three plasticizer (EC/DMC) – filler (PbTiO3) weight ratios. The enhanced conductivity 4.18 × 10{sup −5} Scm{sup −1} was noted for 57.5 wt% −7.5 wt% plasticizer – filler. while blending PEMA to PVdF-co-HFP respectively 7.5: 22.5 wt % (3/7), 15 wt%: 15 wt % (5/5) and 22.5wt %: 7.5 wt % (7/3), the improved conductivity was noted for 3/7 ratio 1.22 × 10{sup −5} S cm{sup −1} and its temperature dependence abide Arrhenius behavior. The intensity of peaks in XRD diffractogram registered dominance of lead titanate, from 2θ = 10° to 80° and absence of VdF crystallites (α+β phase) was noted. In DSC studies, the presence of the exotherm events, filler effect was distinctively seen exhibiting recrystallization of VdF crystallites. In blending PEMA, however, no trace of exotherms was found suggestive of PEMA better inhibiting recrystallization. FTIR study confirmed molecular interactions of various constituents in the vibrational band 500 – 1000 cm{sup −1} both in pristine PVdF-co-HFP and PEMA blended composites with reference to C-F stretching, C-H stretching and C=O carbonyl bands.

  7. Modification of surface texture by grinding and polishing lead zirconate titanate ceramics

    International Nuclear Information System (INIS)

    Cheng, S.; Lloyd, I.K.

    1992-01-01

    This paper reports that grinding and polishing affected the orientation of 90 degrees domains at the surface of lead zirconate titanate (PZT) ceramics. This was quantified by using changes in the intensity ratio of the (002) and (200) X-ray reflections. Grinding unpoled PZT with 600-grit SiC paper gave X-ray intensity ratios similar to those of poled material. This implies that 90 degrees domain realignments had occurred in the near surface region probed by the X-rays. Grinding poled samples with 600-grit SiC further increased the X-ray intensity ratio beyond that caused by poling, indicating that additional surface reorientation of 90 degrees domains had occurred. The effects of diamond polishing depended on the size of the diamond particles. The use of 6-μm diamond had no effect on the (002)/(200) intensity ratio of either poled or unpoled samples, while polishing with 15- or 45-μm diamond significantly enhanced the 90 degrees domain rotation. In unpoled samples, the increase in the X-ray intensity ratio then approached that induced by poling or grinding with 600-grit SiC paper. While the observed increase in X-ray intensity ratio upon grinding is attributed to the rotation of 90 degrees domains, the simultaneous formation of 180 degrees domains appears to minimize or reduce the increase in electrical polarization

  8. Crystallization of sol-gel derived lead zirconate titanate thin films in argon and oxygen atmospheres

    International Nuclear Information System (INIS)

    Bursill, L.A.

    1994-01-01

    Electron diffraction and high-resolution electron microscopic techniques are applied to reveal the mechanisms of crystallization of 75 nm thin films of ferroelectric lead-zirconate-titanate (PZT). Sol-gel methods, followed by pyrolysis at 350 deg C, were used to provide a common starting point after which a variety of rapid-thermal annealing (RTA) experiments in the temperature range 400-700 deg C were made in argon, oxygen and nitrogen/hydrogen atmospheres. The results are interpreted in terms of the crystal chemical analysis, which points out that partial pressure of oxygen and heating rate are important experimental parameters which must be controlled if ferroelectric perovskite-type Pb 2 ZrTiO 6 , rather than pyrochlore-type Pb 2 ZrTiO 6+x , where O < X < 1 or -1 < X < O, is to be obtained after the RTA step. Thus significant improvements in the crystallization of perovskite-type PZT were clearly demonstrated by using argon atmospheres for the RTA step. The results have significance for the production of high-quality ferroelectric thin films, with improved switching and fatigue characteristics, since even small amounts of the pyrochlore phase prove detrimental for these properties. 18 refs., 1 tab., 10 figs

  9. Fatigue of extracted lead zirconate titanate multilayer actuators under unipolar high field electric cycling

    International Nuclear Information System (INIS)

    Wang, Hong; Lee, Sung-Min; Wang, James L.; Lin, Hua-Tay

    2014-01-01

    Testing of large prototype lead zirconate titanate (PZT) stacks presents substantial technical challenges to electronic testing systems, so an alternative approach that uses subunits extracted from prototypes has been pursued. Extracted 10-layer and 20-layer plate specimens were subjected to an electric cycle test under an electric field of 3.0/0.0 kV/mm, 100 Hz to 10 8 cycles. The effects of measurement field level and stack size (number of PZT layers) on the fatigue responses of piezoelectric and dielectric coefficients were observed. On-line monitoring permitted examination of the fatigue response of the PZT stacks. The fatigue rate (based on on-line monitoring) and the fatigue index (based on the conductance spectrum from impedance measurement or small signal measurement) were developed to quantify the fatigue status of the PZT stacks. The controlling fatigue mechanism was analyzed against the fatigue observations. The data presented can serve as input to design optimization of PZT stacks and to operation optimization in critical applications, such as piezoelectric fuel injectors in heavy-duty diesel engines

  10. Fatigue of extracted lead zirconate titanate multilayer actuators under unipolar high field electric cycling

    Science.gov (United States)

    Wang, Hong; Lee, Sung-Min; Wang, James L.; Lin, Hua-Tay

    2014-12-01

    Testing of large prototype lead zirconate titanate (PZT) stacks presents substantial technical challenges to electronic testing systems, so an alternative approach that uses subunits extracted from prototypes has been pursued. Extracted 10-layer and 20-layer plate specimens were subjected to an electric cycle test under an electric field of 3.0/0.0 kV/mm, 100 Hz to 108 cycles. The effects of measurement field level and stack size (number of PZT layers) on the fatigue responses of piezoelectric and dielectric coefficients were observed. On-line monitoring permitted examination of the fatigue response of the PZT stacks. The fatigue rate (based on on-line monitoring) and the fatigue index (based on the conductance spectrum from impedance measurement or small signal measurement) were developed to quantify the fatigue status of the PZT stacks. The controlling fatigue mechanism was analyzed against the fatigue observations. The data presented can serve as input to design optimization of PZT stacks and to operation optimization in critical applications, such as piezoelectric fuel injectors in heavy-duty diesel engines.

  11. Effect of bipolar electric fatigue on polarization switching in lead-zirconate-titanate ceramics

    Science.gov (United States)

    Zhukov, Sergey; Fedosov, Sergey; Glaum, Julia; Granzow, Torsten; Genenko, Yuri A.; von Seggern, Heinz

    2010-07-01

    From comparison of experimental results on polarization switching in fresh and electrically fatigued lead-zirconate-titanate (PZT) over a wide range of applied fields and switching times it is concluded that fatigue alters the local field distribution inside the sample due to the generation of discrete defects, such as voids and cracks. Such defects have a strong influence on the overall electric field distribution by their shape and dielectric permittivity. On this hypothesis, a new phenomenological model of polarization switching in fatigued PZT is proposed. The model assumes that the fatigued sample can be composed of different local regions which exhibit different field strengths but otherwise can be considered as unfatigued. Consequently the temporal response of a fatigued sample is assumed to be the superposition of the field-dependent temporal responses of unfatigued samples weighted by their respective volume fraction. A certain part of the volume is excluded from the overall switching process due to the domain pinning even at earlier stages of fatigue, which can be recovered by annealing. Suitability of the proposed model is demonstrated by a good correlation between experimental and calculated data for differently fatigued samples. Plausible cause of the formation of such regions is the generation of defects such as microcracks and the change in electrical properties at imperfections such as pores or voids.

  12. Crystallization of sol-gel derived lead zirconate titanate thin films in argon and oxygen atmospheres

    Energy Technology Data Exchange (ETDEWEB)

    Bursill, L A [Melbourne Univ., Parkville, VIC (Australia). School of Physics; Brooks, K G [Ecole Polytechnique Federale, Lausanne (Switzerland)

    1994-12-31

    Electron diffraction and high-resolution electron microscopic techniques are applied to reveal the mechanisms of crystallization of 75 nm thin films of ferroelectric lead-zirconate-titanate (PZT). Sol-gel methods, followed by pyrolysis at 350 deg C, were used to provide a common starting point after which a variety of rapid-thermal annealing (RTA) experiments in the temperature range 400-700 deg C were made in argon, oxygen and nitrogen/hydrogen atmospheres. The results are interpreted in terms of the crystal chemical analysis, which points out that partial pressure of oxygen and heating rate are important experimental parameters which must be controlled if ferroelectric perovskite-type Pb{sub 2}ZrTiO{sub 6}, rather than pyrochlore-type Pb{sub 2}ZrTiO{sub 6+x}, where O < X < 1 or -1 < X < O, is to be obtained after the RTA step. Thus significant improvements in the crystallization of perovskite-type PZT were clearly demonstrated by using argon atmospheres for the RTA step. The results have significance for the production of high-quality ferroelectric thin films, with improved switching and fatigue characteristics, since even small amounts of the pyrochlore phase prove detrimental for these properties. 18 refs., 1 tab., 10 figs.

  13. Structural and dielectric characterization of praseodymium-modified lead titanate ceramics synthesized by the OPM route

    Energy Technology Data Exchange (ETDEWEB)

    Pinto, Alexandre H., E-mail: alehp1@yahoo.com.br [LIEC-Laboratorio Interdisciplinar de Eletroquimica e Ceramica, Department of Chemistry, UFSCar-Federal University of Sao Carlos, Rod. Washington Luis km 235, CP 676, Sao Carlos 13565-905, SP (Brazil); Souza, Flavio L., E-mail: fleandro.ufabc@gmail.com [Centro de Ciencias Naturais e Humanas, UFABC - Universidade Federal do ABC, Santo Andre 09210-170, SP (Brazil); Longo, Elson, E-mail: elson@iq.unesp.br [Department of Biochemistry, Chemistry Institute of Araraquara, UNESP - Sao Paulo State University, Rua Francisco Degni, CP 355, Araraquara 14801-907, SP (Brazil); Leite, Edson R., E-mail: derl@power.ufscar.br [LIEC-Laboratorio Interdisciplinar de Eletroquimica e Ceramica, Department of Chemistry, UFSCar-Federal University of Sao Carlos, Rod. Washington Luis km 235, CP 676, Sao Carlos 13565-905, SP (Brazil); Camargo, Emerson R., E-mail: camargo@ufscar.br [LIEC-Laboratorio Interdisciplinar de Eletroquimica e Ceramica, Department of Chemistry, UFSCar-Federal University of Sao Carlos, Rod. Washington Luis km 235, CP 676, Sao Carlos 13565-905, SP (Brazil)

    2011-10-17

    Highlights: {yields} Highly reactive nanosized powders of Pb(0.8)Pr(0.2)TiO(3) were obtained by the OPM route. {yields} Tetragonal phase was observed by X-ray diffraction and confirmed by Raman spectroscopy. {yields} SEM images showed powders partially sintered with particles of approximately 54 nm. {yields} Dielectric measurements show a normal behavior for the ferroelectric to paraelectric transition. - Abstract: Quasi-spherical nanoparticles of praseodymium-modified lead titanate powder (Pb{sub 0.80}Pr{sub 0.20}TiO{sub 3}) with an average size of 54.8 nm were synthesized successfully by the oxidant-peroxo method (OPM) and were used to prepare highly dense ceramic bodies which were sintered at 1100 and 1150 deg. C for 2 h. A tetragonal phase was identified in the powder and ceramic samples by X-ray powder diffraction and FT-Raman spectroscopy at room temperature. The fractured surface of the ceramic sample showed a high degree of densification with fairly uniform grain sizes. Dielectric constants measured in the range of 30-300 deg. C at different frequencies (120 Hz and at 1, 10 and 100 kHz) indicated that samples with 20 mol% praseodymium showed normal ferroelectric behavior regardless of the sintering temperature.

  14. Structural and dielectric characterization of praseodymium-modified lead titanate ceramics synthesized by the OPM route

    International Nuclear Information System (INIS)

    Pinto, Alexandre H.; Souza, Flavio L.; Longo, Elson; Leite, Edson R.; Camargo, Emerson R.

    2011-01-01

    Highlights: → Highly reactive nanosized powders of Pb(0.8)Pr(0.2)TiO(3) were obtained by the OPM route. → Tetragonal phase was observed by X-ray diffraction and confirmed by Raman spectroscopy. → SEM images showed powders partially sintered with particles of approximately 54 nm. → Dielectric measurements show a normal behavior for the ferroelectric to paraelectric transition. - Abstract: Quasi-spherical nanoparticles of praseodymium-modified lead titanate powder (Pb 0.80 Pr 0.20 TiO 3 ) with an average size of 54.8 nm were synthesized successfully by the oxidant-peroxo method (OPM) and were used to prepare highly dense ceramic bodies which were sintered at 1100 and 1150 deg. C for 2 h. A tetragonal phase was identified in the powder and ceramic samples by X-ray powder diffraction and FT-Raman spectroscopy at room temperature. The fractured surface of the ceramic sample showed a high degree of densification with fairly uniform grain sizes. Dielectric constants measured in the range of 30-300 deg. C at different frequencies (120 Hz and at 1, 10 and 100 kHz) indicated that samples with 20 mol% praseodymium showed normal ferroelectric behavior regardless of the sintering temperature.

  15. Non-aqueous electrochemical deposition of lead zirconate titanate films for flexible sensor applications

    Science.gov (United States)

    Joseph, Sherin; Kumar, A. V. Ramesh; John, Reji

    2017-11-01

    Lead zirconate titanate (PZT) is one of the most important piezoelectric materials widely used for underwater sensors. However, PZTs are hard and non-compliant and hence there is an overwhelming attention devoted toward making it flexible by preparing films on flexible substrates by different routes. In this work, the electrochemical deposition of composition controlled PZT films over flexible stainless steel (SS) foil substrates using non-aqueous electrolyte dimethyl sulphoxide (DMSO) was carried out. Effects of various key parameters involved in electrochemical deposition process such as current density and time of deposition were studied. It was found that a current density of 25 mA/cm2 for 5 min gave a good film. The morphology and topography evaluation of the films was carried out by scanning electron microscopy (SEM) and atomic force microscopy (AFM), respectively, which showed a uniform morphology with a surface roughness of 2 nm. The PZT phase formation was studied using X-ray diffraction (XRD) and corroborated with Raman spectroscopic studies. The dielectric constant, dielectric loss, hysteresis and I-V characteristics of the film was evaluated.

  16. Piezoelectric Lead Zirconate Titanate (PZT) Ring Shaped Contour-Mode MEMS Resonators

    Science.gov (United States)

    Kasambe, P. V.; Asgaonkar, V. V.; Bangera, A. D.; Lokre, A. S.; Rathod, S. S.; Bhoir, D. V.

    2018-02-01

    Flexibility in setting fundamental frequency of resonator independent of its motional resistance is one of the desired criteria in micro-electromechanical (MEMS) resonator design. It is observed that ring-shaped piezoelectric contour-mode MEMS resonators satisfy this design criterion than in case of rectangular plate MEMS resonators. Also ring-shaped contour-mode piezoelectric MEMS resonator has an advantage that its fundamental frequency is defined by in-plane dimensions, but they show variation of fundamental frequency with different Platinum (Pt) thickness referred as change in ratio of fNEW /fO . This paper presents the effects of variation in geometrical parameters and change in piezoelectric material on the resonant frequencies of Platinum piezoelectric-Aluminium ring-shaped contour-mode MEMS resonators and its electrical parameters. The proposed structure with Lead Zirconate Titanate (PZT) as the piezoelectric material was observed to be a piezoelectric material with minimal change in fundamental resonant frequency due to Platinum thickness variation. This structure was also found to exhibit extremely low motional resistance of 0.03 Ω as compared to the 31-35 Ω range obtained when using AlN as the piezoelectric material. CoventorWare 10 is used for the design, simulation and corresponding analysis of resonators which is Finite Element Method (FEM) analysis and design tool for MEMS devices.

  17. The Effect of Acceptor and Donor Doping on Oxygen Vacancy Concentrations in Lead Zirconate Titanate (PZT).

    Science.gov (United States)

    Slouka, Christoph; Kainz, Theresa; Navickas, Edvinas; Walch, Gregor; Hutter, Herbert; Reichmann, Klaus; Fleig, Jürgen

    2016-11-22

    The different properties of acceptor-doped (hard) and donor-doped (soft) lead zirconate titanate (PZT) ceramics are often attributed to different amounts of oxygen vacancies introduced by the dopant. Acceptor doping is believed to cause high oxygen vacancy concentrations, while donors are expected to strongly suppress their amount. In this study, La 3+ donor-doped, Fe 3+ acceptor-doped and La 3+ /Fe 3+ -co-doped PZT samples were investigated by oxygen tracer exchange and electrochemical impedance spectroscopy in order to analyse the effect of doping on oxygen vacancy concentrations. Relative changes in the tracer diffusion coefficients for different doping and quantitative relations between defect concentrations allowed estimates of oxygen vacancy concentrations. Donor doping does not completely suppress the formation of oxygen vacancies; rather, it concentrates them in the grain boundary region. Acceptor doping enhances the amount of oxygen vacancies but estimates suggest that bulk concentrations are still in the ppm range, even for 1% acceptor doping. Trapped holes might thus considerably contribute to the charge balancing of the acceptor dopants. This could also be of relevance in understanding the properties of hard and soft PZT.

  18. Dynamic magnetoelectric effects in bulk and layered composites of cobalt zinc ferrite and lead zirconate titanate

    Energy Technology Data Exchange (ETDEWEB)

    Srinivasan, G.; Hayes, R.; DeVreugd, C.P. [Oakland University, Physics Department, Rochester, MI (United States); Laletsin, V.M.; Paddubnaya, N. [National Academy of Sciences, Institute of Technical Acoustics, Vitebsk (Belarus)

    2005-02-01

    Low-frequency magnetoelectric (ME) coupling is investigated in bulk samples and multilayers of cobalt zinc ferrite, Co{sub 1-x}Zn{sub x}Fe{sub 2}O{sub 4} (x=0-0.6), and lead zirconate titanate. In bulk samples, the transverse and longitudinal couplings are weak and of equal magnitude. A substantial strengthening of ME interactions is evident in layered structures, with the ME voltage coefficient a factor of 10-30 higher than in bulk samples. Important findings of our studies of layered composites are as follows. (i) The transverse coupling is stronger than the longitudinal coupling. (ii) The strength of ME interactions is dependent on Zn substitution, with a maximum for x=0.4. (iii) A weak coupling exists at the ferromagnetic-piezoelectric interface, as revealed by an analysis of the volume and static magnetic field dependence of ME voltage coefficients. (iv) The interface coupling k increases with Zn substitution and the k versus x profile shows a maximum centered at x=0.4. (v) The Zn-assisted enhancement can be attributed to efficient magneto-mechanical coupling in the ferrite. (orig.)

  19. Unexpectedly high piezoelectricity of Sm-doped lead zirconate titanate in the Curie point region.

    Science.gov (United States)

    Seshadri, Shruti B; Nolan, Michelle M; Tutuncu, Goknur; Forrester, Jennifer S; Sapper, Eva; Esteves, Giovanni; Granzow, Torsten; Thomas, Pam A; Nino, Juan C; Rojac, Tadej; Jones, Jacob L

    2018-03-07

    Large piezoelectric coefficients in polycrystalline lead zirconate titanate (PZT) are traditionally achieved through compositional design using a combination of chemical substitution with a donor dopant and adjustment of the zirconium to titanium compositional ratio to meet the morphotropic phase boundary (MPB). In this work, a different route to large piezoelectricity is demonstrated. Results reveal unexpectedly high piezoelectric coefficients at elevated temperatures and compositions far from the MPB. At temperatures near the Curie point, doping with 2 at% Sm results in exceptionally large piezoelectric coefficients of up to 915 pm/V. This value is approximately twice those of other donor dopants (e.g., 477 pm/V for Nb and 435 pm/V for La). Structural changes during the phase transitions of Sm-doped PZT show a pseudo-cubic phase forming ≈50 °C below the Curie temperature. Possible origins of these effects are discussed and the high piezoelectricity is posited to be due to extrinsic effects. The enhancement of the mechanism at elevated temperatures is attributed to the coexistence of tetragonal and pseudo-cubic phases, which enables strain accommodation during electromechanical deformation and interphase boundary motion. This work provides insight into possible routes for designing high performance piezoelectrics which are alternatives to traditional methods relying on MPB compositions.

  20. Fatigue of extracted lead zirconate titanate multilayer actuators under unipolar high field electric cycling

    Energy Technology Data Exchange (ETDEWEB)

    Wang, Hong, E-mail: wangh@ornl.gov; Lee, Sung-Min; Wang, James L. [Materials Science and Technology Division, Oak Ridge National Laboratory, Oak Ridge, Tennessee 37831 (United States); Lin, Hua-Tay [School of Mechanical and Electronic Engineering, Guangdong University of Technology, Guangzhou, 510006 (China)

    2014-12-21

    Testing of large prototype lead zirconate titanate (PZT) stacks presents substantial technical challenges to electronic testing systems, so an alternative approach that uses subunits extracted from prototypes has been pursued. Extracted 10-layer and 20-layer plate specimens were subjected to an electric cycle test under an electric field of 3.0/0.0 kV/mm, 100 Hz to 10{sup 8} cycles. The effects of measurement field level and stack size (number of PZT layers) on the fatigue responses of piezoelectric and dielectric coefficients were observed. On-line monitoring permitted examination of the fatigue response of the PZT stacks. The fatigue rate (based on on-line monitoring) and the fatigue index (based on the conductance spectrum from impedance measurement or small signal measurement) were developed to quantify the fatigue status of the PZT stacks. The controlling fatigue mechanism was analyzed against the fatigue observations. The data presented can serve as input to design optimization of PZT stacks and to operation optimization in critical applications, such as piezoelectric fuel injectors in heavy-duty diesel engines.

  1. The Effect of Acceptor and Donor Doping on Oxygen Vacancy Concentrations in Lead Zirconate Titanate (PZT

    Directory of Open Access Journals (Sweden)

    Christoph Slouka

    2016-11-01

    Full Text Available The different properties of acceptor-doped (hard and donor-doped (soft lead zirconate titanate (PZT ceramics are often attributed to different amounts of oxygen vacancies introduced by the dopant. Acceptor doping is believed to cause high oxygen vacancy concentrations, while donors are expected to strongly suppress their amount. In this study, La3+ donor-doped, Fe3+ acceptor-doped and La3+/Fe3+-co-doped PZT samples were investigated by oxygen tracer exchange and electrochemical impedance spectroscopy in order to analyse the effect of doping on oxygen vacancy concentrations. Relative changes in the tracer diffusion coefficients for different doping and quantitative relations between defect concentrations allowed estimates of oxygen vacancy concentrations. Donor doping does not completely suppress the formation of oxygen vacancies; rather, it concentrates them in the grain boundary region. Acceptor doping enhances the amount of oxygen vacancies but estimates suggest that bulk concentrations are still in the ppm range, even for 1% acceptor doping. Trapped holes might thus considerably contribute to the charge balancing of the acceptor dopants. This could also be of relevance in understanding the properties of hard and soft PZT.

  2. Adhesion strength of lead zirconate titanate sol-gel thin films

    Energy Technology Data Exchange (ETDEWEB)

    Berfield, Thomas A., E-mail: tom.berfield@louisville.edu [Department of Mechanical Engineering, University of Louisville, Louisville, KY 40292 (United States); Kitey, Rajesh [Department of Aerospace Engineering, Indian Institute of Technology Kanpur, Kanpur (India); Kandula, Soma S. [Intel Corporation, Portland, OR (United States)

    2016-01-01

    The adhesion strength between a thin film and substrate is often the critical parameter that controls the initiation as well as the mode of film failure. In this work, a laser-based spallation method is used to determine the adhesion strength of “as deposited” lead zirconate titanate (PZT) sol-gel thin films on the two functionally different substrates. For the first case, PZT sol-gel film is deposited onto bare Si/SiO{sub 2} substrates via spin casting. The extremely high adhesion strength between the film and the substrate necessitated an additional platinum mass superlayer to be deposited on top of the PZT film in order to induce interfacial failure. For the superlayer film system, a hybrid experimental/numerical method is employed for determining the substrate/film interfacial strength, quantified to be in the range of 460–480 MPa. A second substrate variation with lower adhesion strength is also prepared by applying a self-assembled octadecyltrichlorosilane (ODS) monolayer to the Si/SiO{sub 2} substrate prior to the film deposition. For the monolayer-coated substrate case, the adhesion strength is observed to be significantly lower (54.7 MPa) when compared to the earlier case. - Highlights: • A non-contact laser spallation method is used to determine PZT film adhesion. • A mediated self-assembled monolayer is shown to greatly reduce interface strength. • Adhesion strength for even well-bonded thin films was found using a superlayer.

  3. Processing and optical characterization of lead calcium titanate borosilicate glass doped with germanium

    Science.gov (United States)

    Gautam, C. R.; Das, Sangeeta; Gautam, S. S.; Madheshiya, Abhishek; Singh, Anod Kumar

    2018-04-01

    In this study, various compositions of lead calcium titanate borosilicate glass doped with a fixed amount of germanium were synthesized using the rapid melt quench technique. The amorphous nature of the synthesized glass was confirmed by X-ray diffraction and scanning electron microscopy analyses. The structural and optical properties were deduced using Raman, Fourier transform infrared (FTIR), and ultraviolet-visible (UV-Vis) spectroscopy. FTIR spectroscopy confirmed the presence of borate groups in triangular and tetrahedral coordination. Infrared and Raman analyses detected the vibrational bonds of Gesbnd Osbnd Ge, Bsbnd Osbnd Ge, Sisbnd Osbnd Ge, Sisbnd Osbnd Si, and Pbsbnd Osbnd Ge. The energy band gaps were evaluated for the prepared glass samples based on Tauc plots of the UV-Vis spectra. The calculated values of the optical band gap decreased from 2.91 to 2.85 eV as the PbO content increased from x = 0.0 to x = 0.7. Furthermore, the Urbach energy was studied based on the UV-Vis results to confirm the disordered structure of the glass. The calculated densities of the glass samples (1.5835 g/cm3 to 3.9184 g/cm3) increased as the concentration of PbO increased, whereas they decreased with the molar volume.

  4. Investigation of the additive induced doping effects in gelcast soft lead zirconate titanate ceramics

    International Nuclear Information System (INIS)

    Guo Dong; Cai Kai; Li Longtu; Gui Zhilun

    2009-01-01

    Due to the high sensitivity of the electrical properties of electronic ceramics to various factors, knowledge about the possible influence of the processing procedure on their electrical performance is critical for applying a new technique to the fabrication of the materials. In this study, various electrical parameters, complex impedance spectra, ferroelectric hysteresis loops, and microstructures of soft lead zirconate titanate (PZT) ceramics formed by the gelcasting technique from suspensions with various dispersants were investigated in comparison with those of the conventional dry pressed ones. We found that the sodium ion, which is the main cation in many commercial surfactants, exhibited obvious hard doping effects; thus causing deteriorated performance of the gelcast PZT ceramics. While a certain impurity ion introduced by a dispersant was also found to induce soft doping characteristics and improve the electrical performance of the materials. The results suggest that the doping effects of the metal ions or impurities introduced by the dispersants, or other additives, should be generally considered for applying a wet processing technique to forming multicomponent electronic ceramics.

  5. Raman analysis of ferroelectric switching in niobium-doped lead zirconate titanate thin films

    International Nuclear Information System (INIS)

    Ferrari, P.; Ramos-Moore, E.; Guitar, M.A.; Cabrera, A.L.

    2014-01-01

    Characteristic Raman vibration modes of niobium-doped lead zirconate titanate (PNZT) are studied as a function of ferroelectric domain switching. The microstructure of PNZT is characterized by scanning electron microscopy and X-ray diffraction. Ferroelectric switching is achieved by applying voltages between the top (Au) and bottom (Pt) electrodes, while acquiring the Raman spectra in situ. Vibrational active modes associated with paraelectric and ferroelectric phases are identified after measuring above and below the ferroelectric Curie temperature, respectively. Changes in the relative intensities of the Raman peaks are observed as a function of the switching voltage. The peak area associated with the ferroelectric modes is analyzed as a function of the applied voltage within one ferroelectric polarization loop, showing local maxima around the coercive voltage. This behavior can be understood in terms of the correlation between vibrational and structural properties, since ferroelectric switching modifies the interaction between the body-centered atom (Zr, Ti or Nb) and the Pb–O lattice. - Highlights: • Electric fields induce structural distortions on ferroelectric perovskites. • Ferroelectric capacitor was fabricated to perform hysteresis loops. • Raman analysis was performed in situ during ferroelectric switching. • Raman modes show hysteresis and inflections around the coercive voltages. • Data can be understood in terms of vibrational–structural correlations

  6. Wafer scale lead zirconate titanate film preparation by sol-gel method using stress balance layer

    International Nuclear Information System (INIS)

    Lu Jian; Kobayashi, Takeshi; Yi Zhang; Maeda, Ryutaro; Mihara, Takashi

    2006-01-01

    In this paper, platinum/titanium (Pt/Ti) film was introduced as a residual stress balance layer into wafer scale thick lead zirconate titanate (PZT) film fabrication by sol-gel method. The stress developing in PZT film's bottom electrode as well as in PZT film itself during deposition were analyzed; the wafer curvatures, PZT crystallizations and PZT electric properties before and after using Pt/Ti stress balance layer were studied and compared. It was found that this layer is effective to balance the residual stress in PZT film's bottom electrode induced by thermal expansion coefficient mismatch and Ti diffusion, thus can notably reduce the curvature of 4-in. wafer from - 40.5 μm to - 12.9 μm after PZT film deposition. This stress balance layer was also found effective to avoid the PZT film cracking even when annealed by rapid thermal annealing with heating-rate up to 10.5 deg. C/s. According to X-ray diffraction analysis and electric properties characterization, crack-free uniform 1-μm-thick PZT film with preferred pervoskite (001) orientation, excellent dielectric constant, as high as 1310, and excellent remanent polarization, as high as 39.8 μC/cm 2 , can be obtained on 4-in. wafer

  7. Temperature behavior of electrical properties of high-k lead-magnesium-niobium titanate thin-films

    Energy Technology Data Exchange (ETDEWEB)

    Chen Wenbin, E-mail: cwb0201@163.com [Electromechanical Engineering College, Guilin University of Electronic Technology (China); McCarthy, Kevin G. [Department of Electrical and Electronic Engineering, University College Cork (Ireland); Copuroglu, Mehmet; O' Brien, Shane; Winfield, Richard; Mathewson, Alan [Tyndall National Institute, University College Cork (Ireland)

    2012-05-01

    This paper reports on the temperature dependence of the electrical properties of high-k lead-magnesium-niobium titanate thin films processed with different compositions (with and without nanoparticles) and with different annealing temperatures (450 Degree-Sign C and 750 Degree-Sign C). These characterization results support the ongoing investigation of the material's electrical properties which are necessary before the dielectric can be used in silicon-based IC applications.

  8. Development of a stress sensor based on the piezoelectric lead zirconate titanate for impact stress measurement

    Science.gov (United States)

    Liu, Yiming; Xu, Bin; Li, Lifei; Li, Bing

    2012-04-01

    The measurement of stress of concrete structures under impact loading and other strong dynamic loadings is crucial for the monitoring of health and damage detection. Due to its main advantages including availability, extremely high rigidity, high natural frequency, wide measuring range, high stability, high reproducibility, high linearity and wide operating temperature range, piezoelectric (Lead Zirconate Titanate, PZT) ceramic materials has been a widely used smart material for both sensing and actuation for monitoring and control in engineering structures. In this paper, a kind of stress sensor based on piezoelectric ceramics for impact stress measuring of concrete structures is developed. Because the PZT is fragile, in order to employ it for the health monitoring of concrete structures, special handling and treatment should be taken to protect the PZT and to make it survive and work properly in concrete. The commercially available PZT patch with lead wires is first applied with an insulation coating to prevent water and moisture damage, and then is packaged by jacketing it by two small precasted cylinder concrete blocks with enough strength to form a smart aggregate (SA). The employed PZT patch has a dimension of 10mm x 10mm x 0.3mm. In order to calibrate the PZT based stress sensor for impact stress measuring, a dropping hammer was designed and calibration test on the sensitivity of the proposed transducer was carried out with an industry charge amplifier. The voltage output of the stress sensor and the impact force under different free falling heights and impact mass were recorded with a high sampling rate data acquisition system. Based on the test measurements, the sensibility of the PZT based stress sensor was determined. Results show that the output of the PZT based stress sensor is proportional to the stress level and the repeatability of the measurement is very good. The self-made piezoelectric stress sensor can be easily embedded in concrete and provide

  9. Synthesis, by alkaline fusion of zirconia from zirconite: characterization and preparation of lead zirconate-titanate

    International Nuclear Information System (INIS)

    Zaghete, M.A.

    1985-01-01

    Zirconium oxide was prepared from zirconite by alkaline fusion. The purity of zirconia was determined by atomic absorption spectroscopy and was found to be 99,94 wt%. In order to prepare en unglomerated and dry hidrous zirconia powder it was used alcohol and acetone for washing and gel suspension; control of the drying rate; and control of the atmosphere and temperature of the oven. The physical characteristics of the hidrous zirconia powder were determined after calcining in several conditions. The zirconia obtained by calcining at 800 0 C during 5 hours (13,9m 2 /g) was used with titanium oxide (7,6m 2 /g and lead oxide (0,6m 2 /g) to prepare a lead zirconate-titanate (PZT) with composition Pb(Zr 0,5 Ti 0,5 O 3 . Two different procedures were used to obtain high densits PZT pellets: in the first procedure the misture of the oxide powder with above composition were reacted at 850 0 C for 4 hours. Then the powder was pressed and sintered at 1200 0 C during 4 and 6 hours; in the second procedure the mixture of unreacted oxide were pressed in pellets and then reacted at 850 0 C during 4 hours and sintered at 1200 0 C during 4 and 6 hours. The apparent density of the sintered pellets were determined By mercury displacement and ranged from 7,25 to 7,39 g/cm 3 for the compacts obtained by the second procedure and from 8,08 to 8,10g/cm 3 for the compacts obtained by the first procedure. The microstructure observed by scanning electron microscopy showed that sintered compact obtained by the first procedure has a more homogeneous size distribution when compared with samples obtained be the second procedure. (author) [pt

  10. Metalorganic solution deposition of lead zirconate titanate films onto an additively manufactured Ni-based superalloy

    International Nuclear Information System (INIS)

    Patel, T.; Khassaf, H.; Vijayan, S.; Bassiri-Gharb, N.; Aindow, M.; Alpay, S.P.; Hebert, R.J.

    2017-01-01

    Recent advances in additive manufacturing of high-temperature alloys for structural aerospace applications has led to interest in integrating additional functionality into such parts. Lead zirconate titanate (PZT) is a prototypical ferroelectric ceramic used as the electro-active material in many piezoelectric sensors and actuators. In this study, 300 nm thick PbZr_0_._2Ti_0_._8O_3 (PZT 20/80) films were grown using metalorganic solution deposition onto additively manufactured substrates of Inconel 718. The microstructures of the films and the nature of the film/substrate interfaces were characterized using a combination of X-ray diffraction and electron microscopy techniques. Electrical measurements were performed to determine the ferroelectric, dielectric, and conductive responses of the PZT films. Our findings show that the PZT films exhibit robust ferroelectricity characterized by well-defined polarization-applied electric field (P-E) hysteresis loops. The samples display internal bias of up to ∼40 kV/cm. The room temperature remnant polarization and the small signal dielectric permittivity are ∼70 μC/cm"2 and 205, respectively. The dielectric loss (tan δ) and the leakage current at 1 kHz are 9% and 1 nA at 1 V, respectively. We attribute the internal bias observed in the hysteresis loops and the overall large dielectric losses to the presence of an intermediate oxide layer at the PZT/Inconel interface, which forms during the high temperature crystallization of the ferroelectric film. These results show that it is possible to grow functional oxides with promising electrical properties onto additively manufactured metallic substrates.

  11. Ferroelectric and Piezoelectric properties of (111) oriented lanthanum modified lead zirconate titanate film

    International Nuclear Information System (INIS)

    Dutta, Soma; Antony Jeyaseelan, A.; Sruthi, S.

    2014-01-01

    Lanthanum modified lead zirconate titanate (PLZT) thick film with molecular formula of Pb 0.92 La 0.08 (Zr 0.52 Ti 0.48 ) 0.98 O 3 was grown preferentially along (111) direction on Pt/SiO 2 /Si (platinum/silicon oxide/silicon) substrate by spin coating of chemical solution. The directional growth of the film was facilitated by platinum (Pt) (111) template and rapid thermal annealing. X-ray diffraction pattern and atomic force microscopy revealed the preferential growth of the PLZT film. The film was characterized for ferroelectric and detailed piezoelectric properties in a parallel plate capacitor (metal–PLZT–metal) configuration. Ferroelectric characterization of the film showed saturated hysteresis loop with remanent polarization and coercive electric field values of 10.14 μC/cm 2 and 42 kV/cm, respectively, at an applied field of 300 kV/cm. Longitudinal piezoelectric coefficient (d 33,f ) was measured by employing converse piezoelectric effect where electrical charge response and displacement were measured with electrical voltage excitation on the sample electrodes. The effective transverse piezoelectric coefficient (e 31,f ) was derived from charge measurement with an applied mechanical excitation strain by using the four point bending method. d 33,f and e 31,f coefficients of PLZT films were found to be 380 pm/V and − 0.831 C/m 2 respectively. - Highlights: • PLZT (111) film is prepared by spin coating of chemical sol on Pt (111) template. • Piezoelectric d 33 value (380 pm/V) of PLZT film is found 20% higher than PZT. • Transverse piezocoefficient e 31,f of PLZT film is reported for the first time

  12. Microwave emission from lead zirconate titanate induced by impulsive mechanical load

    Energy Technology Data Exchange (ETDEWEB)

    Aman, A., E-mail: alexander.aman@ovgu.de [Department of Engineering, Brandenburg University of Applied Science, 14470 Brandenburg an derHavel (Germany); Packaging Group, Institute of Micro- and Sensorsytems, Otto-von-Guericke University, Universitätsplatz 2, 39106 Magdeburg (Germany); Majcherek, S. [Packaging Group, Institute of Micro- and Sensorsytems, Otto-von-Guericke University, Universitätsplatz 2, 39106 Magdeburg (Germany); Hirsch, S. [Department of Engineering, Brandenburg University of Applied Science, 14470 Brandenburg an derHavel (Germany); Schmidt, B. [Chair of Micorsystem Technology, Institute of Micro- and Sensorsytems, Otto-von-Guericke University, Universitätsplatz 2, 39106 Magdeburg (Germany)

    2015-10-28

    This paper focuses on microwave emission from Lead zirconate titanate Pb [Zr{sub x}Ti{sub 1−x}] O{sub 3} (PZT) induced by mechanical stressing. The mechanical stress was initiated by impact of a sharp tungsten indenter on the upper surface of PZT ceramic. The sequences of microwave and current impulses, which flew from indenter to electric ground, were detected simultaneously. The voltage between the upper and lower surface of ceramic was measured to obtain the behavior of mechanical force acting on ceramic during the impact. It was found that the amplitude, form, and frequency of measured microwave impulses were different by compression and restitution phase of impact. Two different mechanisms of electron emission, responsible for microwave impulse generation, were proposed based on the dissimilar impulse behavior. The field emission from tungsten indenter is dominant during compression, whereas ferroemission dominates during restitution phase. Indeed, it was observed that the direction of the current flow, i.e., sign of current impulses is changed by transitions from compression to restitution phase of impact. The observed dissimilar behavior of microwave impulses, caused by increasing and decreasing applied force, can be used to calculate the contact time and behavior of mechanical force during mechanical impact on ceramic surface. It is shown that the generation of microwave impulses exhibits high reproducibility, impulse intensity, a low damping factor, and high mechanical failure resistance. Based on these microwave emission properties of PZT, the development of new type of stress sensor with spatial resolution of few microns becomes possible.

  13. Reduction of etching damage in lead-zirconate-titanate thin films with inductively coupled plasma

    International Nuclear Information System (INIS)

    Lim, Kyu-Tae; Kim, Kyoung-Tae; Kim, Dong-Pyo; Kim, Chang-Il

    2003-01-01

    In this work, we etched lead-zirconate-titanate (PZT) films with various additive gases (O 2 and Ar) in Cl 2 /CF 4 plasmas, while mixing ratio was fixed at 8/2. After the etching, the plasma induced damages are characterized in terms of hysteresis curves, leakage current, retention properties, and switching polarization. When the electrical properties of PZT etched in O 2 or Ar added to Cl 2 /CF 4 were compared, the value of remanent polarization in O 2 added to Cl 2 /CF 4 plasma is higher than that in Ar added plasma. The maximum etch rate of the PZT thin films was 145 nm/min for 30% Ar added Cl 2 /CF 4 gas having mixing ratio of 8/2 and 110 nm/min for 10% O 2 added to that same gas mixture. In order to recover the ferroelectric properties of the PZT thin films after etching, we annealed the etched PZT thin films at 550 deg. C in an O 2 atmosphere for 10 min. From the hysteresis curves, leakage current, retention property, and switching polarization, the reduction of the etching damage and the recovery via the annealing turned out to be more effective when O 2 was added to Cl 2 /CF 4 than Ar. X-ray diffraction showed that the structural damage was lower when O 2 was added to Cl 2 /CF 4 and the improvement in the ferroelectric properties of the annealed samples was consistent with the increased intensities of the (100) and the (200) PZT peaks

  14. Transverse piezoelectric coefficient measurement of flexible lead zirconate titanate thin films

    Energy Technology Data Exchange (ETDEWEB)

    Dufay, T.; Guiffard, B.; Seveno, R. [LUNAM Université, Université de Nantes, IETR (Institut d' Électronique et de Télécommunications de Rennes), UMR CNRS 6164, 2 rue de la Houssinière, BP 92208, 44322 Nantes Cedex 3 (France); Thomas, J.-C. [LUNAM Université, Université de Nantes-École Centrale Nantes, GeM (Institut de Recherche en Génie Civil et Ingénierie Mécanique), UMR CNRS 6183, 2 rue de la Houssinière, BP 92208, 44322 Nantes Cedex 3 (France)

    2015-05-28

    Highly flexible lead zirconate titanate, Pb(Zr,Ti)O{sub 3} (PZT), thin films have been realized by modified sol-gel process. The transverse piezoelectric coefficient d{sub 31} was determined from the tip displacement of bending-mode actuators made of PZT cantilever deposited onto bare or RuO{sub 2} coated aluminium substrate (16 μm thick). The influence of the thickness of ruthenium dioxide RuO{sub 2} and PZT layers was investigated for Pb(Zr{sub 0.57}Ti{sub 0.43})O{sub 3}. The modification of Zr/Ti ratio from 40/60 to 60/40 was done for 3 μm thick PZT thin films onto aluminium (Al) and Al/RuO{sub 2} substrates. A laser vibrometer was used to measure the beam displacement under controlled electric field. The experimental results were fitted in order to find the piezoelectric coefficient. Very large tip deflections of about 1 mm under low voltage (∼8 V) were measured for every cantilevers at the resonance frequency (∼180 Hz). For a given Zr/Ti ratio of 58/42, it was found that the addition of a 40 nm thick RuO{sub 2} interfacial layer between the aluminium substrate and the PZT layer induces a remarkable increase of the d{sub 31} coefficient by a factor of 2.7, thus corresponding to a maximal d{sub 31} value of 33 pC/N. These results make the recently developed PZT/Al thin films very attractive for both low frequency bending mode actuating applications and vibrating energy harvesting.

  15. Ferroelectric and Piezoelectric properties of (111) oriented lanthanum modified lead zirconate titanate film

    Energy Technology Data Exchange (ETDEWEB)

    Dutta, Soma, E-mail: som@nal.res.in; Antony Jeyaseelan, A.; Sruthi, S.

    2014-07-01

    Lanthanum modified lead zirconate titanate (PLZT) thick film with molecular formula of Pb{sub 0.92}La{sub 0.08}(Zr{sub 0.52}Ti{sub 0.48}){sub 0.98}O{sub 3} was grown preferentially along (111) direction on Pt/SiO{sub 2}/Si (platinum/silicon oxide/silicon) substrate by spin coating of chemical solution. The directional growth of the film was facilitated by platinum (Pt) (111) template and rapid thermal annealing. X-ray diffraction pattern and atomic force microscopy revealed the preferential growth of the PLZT film. The film was characterized for ferroelectric and detailed piezoelectric properties in a parallel plate capacitor (metal–PLZT–metal) configuration. Ferroelectric characterization of the film showed saturated hysteresis loop with remanent polarization and coercive electric field values of 10.14 μC/cm{sup 2} and 42 kV/cm, respectively, at an applied field of 300 kV/cm. Longitudinal piezoelectric coefficient (d{sub 33,f}) was measured by employing converse piezoelectric effect where electrical charge response and displacement were measured with electrical voltage excitation on the sample electrodes. The effective transverse piezoelectric coefficient (e{sub 31,f}) was derived from charge measurement with an applied mechanical excitation strain by using the four point bending method. d{sub 33,f} and e{sub 31,f} coefficients of PLZT films were found to be 380 pm/V and − 0.831 C/m{sup 2} respectively. - Highlights: • PLZT (111) film is prepared by spin coating of chemical sol on Pt (111) template. • Piezoelectric d{sub 33} value (380 pm/V) of PLZT film is found 20% higher than PZT. • Transverse piezocoefficient e{sub 31,f} of PLZT film is reported for the first time.

  16. Dielectric and electrical properties of gadolinium-modified lead-zirconate-titanate system

    International Nuclear Information System (INIS)

    Panigrahi, S.C.; Das, Piyush R.; Parida, B.N.; Padhee, R.; Choudhary, R.N.P.

    2014-01-01

    Highlights: • Gadolinium modified PZT have very good dielectric and ferroelectric properties. • The impedance analysis of shows grain and grain boundary phenomena. • Electrical properties of the compounds show very good transport properties. • Piezoelectric coefficient of the samples have higher values. - Abstract: The gadolinium (Gd) modified lead zirconate titanate (PbZr,TiO 3 ) ceramics with Zr/Ti = 48/52 (i.e., near morphotropic phase boundary (MPB)) in a general chemical formula Pb 1−x Gd x (Zr 0.48 Ti 0.52 ) 1−x/4 O 3 (PGZT; x = 0, 0.07, 0.10 and 0.12) have been synthesized using a high-temperature solid-state reaction method. Preliminary structural analysis using X-ray powder diffraction (XRD) shows the formation of a single-phase tetragonal structure of the compounds. Detailed studies of dielectric parameters of PGZT exhibit the diffuse phase transition but non-relaxor characteristics in the material for the higher concentration of gadolinium. The ac conductivity spectra of PGZT are found to obey Jonscher’s universal power law. The electrical impedance parameters of PGZT (near MPB) were obtained in a wide range of temperature (25–500 °C) and frequency (1–1000 kHz) using complex impedance spectroscopy (CIS) technique. Detailed analysis of these parameters shows that bulk (grain) and grain boundary resistance have significant effect on the total impedance of the materials. Temperature dependence of hysteresis characteristics of PGZT confirms that the phase transition parameter of the material is strongly affected by the substitution of Gd at the Pb-sites

  17. Study of samarium modified lead zirconate titanate and nickel zinc ferrite composite system

    Energy Technology Data Exchange (ETDEWEB)

    Rani, Rekha [Department of Physics, SD PG College, Panipat 132103 (India); School of Physics and Materials Science, Thapar University, Patiala 147004 (India); Juneja, J.K., E-mail: jk_juneja@yahoo.com [Department of Physics, Hindu College, Sonepat 131001 (India); Singh, Sangeeta [Department of Physics, GVM Girls College, Sonepat 131001 (India); Raina, K.K. [School of Physics and Materials Science, Thapar University, Patiala 147004 (India); Prakash, Chandra [Solid State Physics Laboratory, Timarpur, Delhi 110054 (India)

    2015-03-15

    In the present work, composites of samarium substituted lead zirconate titanate and nickel zinc ferrite with compositional formula 0.95Pb{sub 1−3x/2} Sm{sub x}Zr{sub 0.65}Ti{sub 0.35}O{sub 3}–0.05Ni{sub 0.8}Zn{sub 0.2}Fe{sub 2}O{sub 4} (x=0, 0.01, 0.02 and 0.03) were prepared by the conventional solid state route. X-ray diffraction analysis was carried out to confirm the coexistence of individual phases. Microstructural study was done by using scanning electron microscope. Dielectric constant and loss were studied as a function of temperature and frequency. To study ferroelectric and magnetic properties of the composite samples, corresponding P–E and M–H hysteresis loops were recorded. Change in magnetic properties of electrically poled composite sample (x=0.02) was studied to confirm the magnetoelectric (ME) coupling. ME coefficient (dE/dH) of the samples (x=0 and 0.02) was measured as a function of DC magnetic field. - Highlights: • We are reporting the effect of Sm substitution on PZT–NiZn ferrite composites. • Observation of both P–E and M–H loops confirms ferroelectric and magnetic ordering. • With Sm substitution, significant improvement in properties was observed. • Increase in magnetization for electrically poled sample is evidence of ME coupling. • Electric polarization is generated by applying magnetic field.

  18. In situ synchrotron diffraction of lead-zirconate-titanate at its morphotropic phase boundary

    International Nuclear Information System (INIS)

    Schoenau, K.A.

    2008-01-01

    Ferroelectric lead zirconate titanate ceramics (PZT,Pb(Zr x Ti 1-x )O 3 ) find in industry intensifiedly applications as piezoactors. Their largest macroscopic strain under electric field they show in the region of the morphotropic phase boundary (MPB), the transition region between the Ti rich tetragonal and the Zr rich structure. The structure of PZT at the MPB was controversially discussed since the detection of a monoclinic intermediate phase by Noheda et al. [Appl. Phys. Lett.,74(14), 2059(1999)], whereby into the considerations the domain structure of the material not entered, which however is essentially responsible for the reaction under electric field. In order to understand the domain structure of PZT under electric field and to study possible causes for the fatigue behaviour of the material under bipolar cycling a bridge must be built between macroscopic and local structure. For this at the measuring place B2 of the Hasylab, Hamburg, synchrotron X-ray powder diffractometry was in situ performed under different sample environments in transmission geometry, which was correlated with transmission-electron-microscopical studies and electron spin resonance. Samples with compositions over the whole MPB were beside temperature-dependent measurements measured at room temperature in high resolution and under applied electric field. Furthermore for studies under electric field at elevated temperatures a special E-field furnace was constructed. It could be shown the large piezoelectric reaction of PZT at its MPB is strongly correlated with a diminishment of the domain structure, which simulates in X-ray diffraction a lower symmetric phase. The stability range of the nanodomains with temperature and electric field reflects in the switching behaviour of the matter and by the detection of a relaxor behavior of the nanodomain structure for the first time a direct comparison with relaxoceramics is possible. The varying stress conditions within the sample influence

  19. Determination of temperature dependence of piezoelectric coefficients matrix of lead zirconate titanate ceramics by quasi-static and resonance method

    International Nuclear Information System (INIS)

    Li Fei; Xu Zhuo; Wei Xiaoyong; Yao Xi

    2009-01-01

    The piezoelectric coefficients (d 33 , -d 31 , d 15 , g 33 , -g 31 , g 15 ) of soft and hard lead zirconate titanate ceramics were measured by the quasi-static and resonance methods, at temperatures from 20 to 300 0 C. The results showed that the piezoelectric coefficients d 33 , -d 31 and d 15 obtained by these two methods increased with increasing temperature for both hard and soft PZT ceramics, while the piezoelectric coefficients g 33 , -g 31 and g 15 decreased with increasing temperature for both hard and soft PZT ceramics. In this paper, the observed results were also discussed in terms of intrinsic and extrinsic contributions to piezoelectric response.

  20. Effect of polarization fatigue on the Rayleigh coefficients of ferroelectric lead zirconate titanate thin films: Experimental evidence and implications

    Science.gov (United States)

    Lou, X. J.; Zhang, H. J.; Luo, Z. D.; Zhang, F. P.; Liu, Y.; Liu, Q. D.; Fang, A. P.; Dkhil, B.; Zhang, M.; Ren, X. B.; He, H. L.

    2014-09-01

    The effect of polarization fatigue on the Rayleigh coefficients of ferroelectric lead zirconate titanate (PZT) thin film was systematically investigated. It was found that electrical fatigue strongly affects the Rayleigh behaviour of the PZT film. Both the reversible and irreversible Rayleigh coefficients decrease with increasing the number of switching cycles. This phenomenon is attributed to the growth of an interfacial degraded layer between the electrode and the film during electrical cycling. The methodology used in this work could serve as an alternative way for evaluating the fatigue endurance and degradation in dielectric properties of ferroelectric thin-film devices during applications.

  1. Acoustic response of piezoelectric lead-zirconate-titanate to a 400MeV/n xenon beam

    CERN Document Server

    Miyachi, T; Ito, H

    2003-01-01

    Characteristics of lead-zirconate-titanate (PZT) elements were studied by directly irradiating them with a 400 MeV/n Xe beam. The elements were sensitive to 10 sup 4 Xe ions and their output amplitudes were proportional to the beam intensity. An ensemble of those output amplitudes displayed a Bragg-curve-like response towards the range of 400 MeV/n Xe ion. We discuss the potential of PZT elements as a radiation detector and their application to high-intensity and high-energy detectors. (author)

  2. Influence of KF substitution on the ferroelectric phase transition of lead titanate single crystals studied by Brillouin light scattering

    Directory of Open Access Journals (Sweden)

    Seonhyeop Shin

    2015-06-01

    Full Text Available The elastic properties of KF-substituted perovskite lead titanate (PbTiO3 were investigated by dielectric measurements and Brillouin light scattering. The ferroelectric phase transition occurred at substantially lower temperature due to KF substitution, which was attributed to the modification of the covalency in Pb–O and Ti–O bonds. The longitudinal acoustic (LA mode of KF-substituted PbTiO3 showed a frequency softening in the paraelectric phase, which was accompanied by increasing acoustic damping. This indicated that polarization fluctuations responsible for the acoustic anomalies were enhanced by KF substitution.

  3. Preparation of lead titanate zirconate from metal citrates; Preparacao do titanato zirconato de chumbo a partir dos citratos metalicos

    Energy Technology Data Exchange (ETDEWEB)

    Bastos, C M.R.

    1994-12-31

    Lead titanate zirconate (PZT) preparation from its metal constituent citrates have been investigated. Metal citrates were obtained by forced precipitation using a dehydration alcohol mixture. Salt solutions of lead nitrate and octahydrated zirconyl chloride, and titanium tetrachloride were treated separately with citric acid and ammonium hydroxide. Zirconium, titanium and lead oxides resulted from thermal decomposition of corresponding citrates at 500{sup 0} C, 450{sup 0} C and 250{sup 0} C, respectively. Lead titanate (PT) and lead zirconate (P Z) were obtained by calcining at 450{sup 0} C and 500{sup 0} C, respectively, after adequate heating of citrates mechanically mixed in ethyl ether. PZT samples were obtained with different starting stoichiometry. Rhombohedral PZT-1 53/47 sample was prepared from co precipitating zirconyl ammonium and ammonium lead citrates in presence of ethanolic titanium oxide dispersion, and calcinating at 800{sup 0} C. Rhombohedral PZT-q 52/48 sample was obtained from heating at 500{sup 0} C for 2 hours a mixture of metal citrates coprecipitated by dehydration mixture of acetone-ethanol-formic acid (2:1:0,06). Tetragonal PZT-m stoichiometry 53/47 sample were obtained by calcining at after 600{sup 0} C for 2 hours after heating a mechanically mixed metal citrates. PT phase arose at 400{sup 0} C. PZT-m powders obtained in a range of 400{sup 0} C-800{sup 0} C were isostatically pressed, and sintered at 1100{sup 0} C and 1200{sup 0} C in saturated Pb O atmosphere. Rhombohedral sintered PZT was obtained with 7,78 g.cm{sup -3} at 1200{sup 0} C. (author). 123 refs, 53 figs, 32 tabs.

  4. Stability constants of scandium complexes, 1

    International Nuclear Information System (INIS)

    Itoh, Hisako; Itoh, Naomi; Suzuki, Yasuo

    1984-01-01

    The stability constants of scandium complexes with some carboxylate ligands were determined potentiometrically at 25.0 and 40.0 0 C and at an ionic strength of 0.10 with potassium nitrate as supporting electrolyte. The constants of the scandium complexes were appreciably greater than those of the corresponding lanthanoid complexes, as expected. The changes in free energy, enthalpy, and entropy for the formation of the scandium complexes were calculated from the stability constants at two temperatures. (author)

  5. The determination of major and some minor constituents in lead zirconate-titanate compositions by x-ray fluorescence and atomic absorption spectrometry

    NARCIS (Netherlands)

    van Willigen, J.H.H.G.; Kruidhof, H.; Dahmen, E.A.M.F.

    1972-01-01

    An accurate X-ray fluorescence spectrometric method is described for the determination of lead, zirconium and titanium in lead zirconate-titanate ceramics. Careful matching of samples and standards by a borax fusion method resulted in a relative standard deviation of about 0.2% for the major

  6. Low temperature heat capacity of scandium and alloys of scandium

    Energy Technology Data Exchange (ETDEWEB)

    Tsang, T. W.E.

    1977-12-01

    The heat capacity of three electrotransport purified scandium samples has been measured from 1 to 20/sup 0/K. The resultant electronic specific heat constant and Debye temperature are 10.337 +- 0.015 mJ/gm-atom K/sup 2/ and 346.7 +- 0.8/sup 0/K respectively, and these values are believed to be truly representative of intrinsic scandium. Alloying studies have also been carried out to investigate the band structure of scandium based on the rigid band model, with zirconium to raise the electron concentration and magnesium to lower it. The results are then compared to the theoretical band structure calculations. Low temperature heat capacity measurements have also been made on some dilute Sc-Fe alloys. An anomaly is observed in the C/T vs. T/sup 2/ plot, but the C vs. T curve shows no evidence of magnetic ordering down to 1/sup 0/K, and electrical resistance measurement from 4 to 0.3/sup 0/K also indicates that no magnetic ordering took place.

  7. Thickness effect on the structure, grain size, and local piezoresponse of self-polarized lead lanthanum zirconate titanate thin films

    Energy Technology Data Exchange (ETDEWEB)

    Melo, M.; Araújo, E. B., E-mail: eudes@dfq.feis.unesp.br [Departamento de Física e Química, Faculdade de Engenharia de Ilha Solteira, UNESP—Univ. Estadual Paulista, 15385-000 Ilha Solteira, SP (Brazil); Shvartsman, V. V. [Institute for Materials Science, University Duisburg-Essen, 45141 Essen (Germany); Shur, V. Ya. [Institute of Natural Sciences, Ural Federal University, 620000 Ekaterinburg (Russian Federation); Kholkin, A. L. [Institute of Natural Sciences, Ural Federal University, 620000 Ekaterinburg (Russian Federation); Department of Physics and CICECO—Aveiro Institute of Materials, University of Aveiro, 3810-193 Aveiro (Portugal)

    2016-08-07

    Polycrystalline lanthanum lead zirconate titanate (PLZT) thin films were deposited on Pt/TiO{sub 2}/SiO{sub 2}/Si substrates to study the effects of the thickness and grain size on their structural and piezoresponse properties at nanoscale. Thinner PLZT films show a slight (100)-orientation tendency that tends to random orientation for the thicker film, while microstrain and crystallite size increases almost linearly with increasing thickness. Piezoresponse force microscopy and autocorrelation function technique were used to demonstrate the existence of local self-polarization effect and to study the thickness dependence of correlation length. The obtained results ruled out the bulk mechanisms and suggest that Schottky barriers near the film-substrate are likely responsible for a build-in electric field in the films. Larger correlation length evidence that this build-in field increases the number of coexisting polarization directions in larger grains leading to an alignment of macrodomains in thinner films.

  8. Dynamic processes of domain switching in lead zirconate titanate under cyclic mechanical loading by in situ neutron diffraction

    International Nuclear Information System (INIS)

    Pojprapai, Soodkhet; Luo, Zhenhua; Clausen, Bjorn; Vogel, Sven C.; Brown, Donald W.; Russel, Jennifer; Hoffman, Mark

    2010-01-01

    The performance of ferroelectric ceramics is governed by the ability of domains to switch. A decrease in the switching ability can lead to degradation of the materials and failure of ferroelectric devices. In this work the dynamic properties of domain reorientation are studied. In situ time-of-flight neutron diffraction is used to probe the evolution of ferroelastic domain texture under mechanical cyclic loading in bulk lead zirconate titanate ceramics. The high sensitivity of neutron diffraction to lattice strain is exploited to precisely analyze the change of domain texture and strain through a full-pattern Rietveld method. These results are then used to construct a viscoelastic model, which explains the correlation between macroscopic phenomena (i.e. creep and recovered deformation) and microscopic dynamic behavior (i.e. ferroelastic switching, lattice strain).

  9. Interaction of scandium sesquioxide with carbon

    International Nuclear Information System (INIS)

    Vodop'yanov, A.G.; Zakharov, R.G.

    1986-01-01

    In the range of 2350-2470 degrees K at a PCO = 0.0 MPa, interaction in Sc 2 O 3 with carbon mixtures initially occurs by CO chemisorption at the scandium oxide surface and disproportionation into CO 2 and C, with subsequent replacement of oxygen in the oxide anion sublattice by carbon to form ScC. The carbide melt, creating a contact between the reagents, then transforms the process to a diffusion-based one. At 1820-2220 K in vacuum, reduction of the studied mixtures occurs by dissociative vaporization of the oxide, with precipitation of ScC at the carbon surface and generation of CO. The appearance of CO in the vapors of mixture leads to formation of an oxycarbide phase and to the partial occurrence of oxide dissociation

  10. Generation of electrical energy using lead zirconate titanate (PZT-5A) piezoelectric material: Analytical, numerical and experimental verifications

    Energy Technology Data Exchange (ETDEWEB)

    Butt, Zubair; Ahmad, Nasir [Dept. of Mechanical, Mechatronics and Manufacturing Engineering, UET Lahore, Faisalabad Campus, Lahore (Pakistan); Pasha, Riffat Asim; Qayyum, Faisal; Anjum, Zeeshan [Dept. of Mechanical Engineering, University of Engineering and Technology, Taxila (Pakistan); Elahi, Hassan [Northwestern Polytechnical University, Xian (China)

    2016-08-15

    Energy harvesting is the process of attaining energy from the external sources and transforming it into usable electrical energy. An analytical model of piezoelectric energy harvester has been developed to determine the output voltage across an electrical circuit when it is forced to undergo a base excitation. This model gives an easy approach to design and investigate the behavior of piezoelectric material. Numerical simulations have been carried out to determine the effect of frequency and loading on a Lead zirconate titanate (PZT-5A) piezoelectric material. It has been observed that the output voltage from the harvester increases when loading increases whereas its resonance frequency decreases. The analytical results were found to be in good agreement with the experimental and numerical simulation results.

  11. Mechanical and dielectric characterization of lead zirconate titanate(PZT)/polyurethane(PU) thin film composite for energy harvesting

    Science.gov (United States)

    Aboubakr, S.; Rguiti, M.; Hajjaji, A.; Eddiai, A.; Courtois, C.; d'Astorg, S.

    2014-04-01

    The Lead Zirconate titanate (PZT) ceramic is known by its piezoelectric feature, but also by its stiffness, the use of a composite based on a polyurethane (PU) matrix charged by a piezoelectric material, enable to generate a large deformation of the material, therefore harvesting more energy. This new material will provide a competitive alternative and low cost manufacturing technology of autonomous systems (smart clothes, car seat, boat sail, flag ...). A thin film of the PZT/PU composite was prepared using up to 80 vol. % of ceramic. Due to the dielectric nature of the PZT, inclusions of this one in a PU matrix raises the permittivity of the composite, on other hand this latter seems to decline at high frequencies.

  12. The large magnetoelectric effect in Ni-lead zirconium titanate-Ni trilayers derived by electroless deposition

    International Nuclear Information System (INIS)

    Bi, K; Wang, Y G; Wu, W; Pan, D A

    2010-01-01

    Magnetoelectric (ME) Ni-lead zirconium titanate-Ni trilayers with neither electrodes nor bonding layers have been derived by electroless deposition. The structure and magnetic properties of the electroless deposited Ni layers with different pH values are characterized by x-ray diffraction and vibrating sample magnetometer. The influence of the bias magnetic field and the magnetic field frequency (f) on ME coupling is discussed. It is seen that α E,31 depends strongly on H dc and f. The value of the ME coefficient increases as the thickness of the Ni layer and the pH of the bath increase. A maximum of the ME voltage coefficient α E,31 = 5.77 V cm -1 Oe -1 at resonance frequency with a deposited Ni layer thickness t Ni = 302 μm is obtained. The large ME coefficient makes these Ni-PZT-Ni trilayers suitable for applications in sensors, actuators and transducers. (fast track communication)

  13. Effect of oxygen partial pressure on texture development in lead zirconate titanate thin films processed from metalorganic precursors

    International Nuclear Information System (INIS)

    Norton, Jarrod L.; Liedl, Gerald L.; Slamovich, Elliott B.

    1999-01-01

    Metalorganic liquid precursors were used to examine the effects of processing atmosphere on texture development in oriented Pb(Zr 0.60 Ti 0.40 )O 3 thin films. After removal of organic ligands via pyrolysis, the films were heated at 25 degree sign C/min in a 5% H 2 /Ar atmosphere until a switching temperature, after which the atmosphere was switched to pure oxygen. The films were heated to a maximum temperature of 650 degree sign C with switching temperatures ranging from 450 to 600 degree sign C. The degree of (111) orientation in the lead zirconate titanate (PZT) films increased with increasing switching temperature, resulting in highly textured (111) PZT films. These results suggest that atmosphere control plays a significant role in texture development during rapid thermal processing. (c) 1999 Materials Research Society

  14. Fracture mechanisms in ferroelectric-ferroelastic lead zirconate titanate (Zr:Ti = 0.54:0.46) ceramics

    International Nuclear Information System (INIS)

    Mehta, K.; Virkar, A.V.

    1990-01-01

    Fracture toughness, K IC , of a single-phase commercial lead zirconate titanate (PZT) ceramic of tetragonal structure was measured using the single edge notched beam method above and below the Curie temperature. Domain switching (poling) under electrical and mechanical loading was examined using x-ray diffraction. Surface grinding, electrical poling, and mechanical poling caused crystallographic texture. Similar texture, indicative of domain switching, was also observed on fracture surfaces of some samples fractured at room temperature. At room temperature, the highest K IC measured was 1.85 MPa · m 1/2 , while above the Curie temperature it was about 1.0 MPa · m 1/2 . Cracks emanating from Vickers indents in poled samples were different in the poling and the transverse directions. The difference in crack sizes is explained on the basis of domain switching during crack growth. These results indicate that ferroelastic domain switching (twinning) is a viable toughening mechanism in the PZT materials tested

  15. Improvement of fatigue resistance for multilayer lead zirconate titanate (PZT)-based ceramic actuators by external mechanical loads

    Science.gov (United States)

    Yang, Gang; Yue, Zhenxing; Ji, Ye; Chu, Xiangcheng; Li, Longtu

    2008-12-01

    The influence of external compressive loads, applied along a direction perpendicular to polarization, on fatigue behaviors of multilayer lead zirconate titanate (PZT)-based ceramic actuators was investigated. Under no external mechanical load, a normal fatigue behavior was observed, demonstrating that both switching polarization (Pswitching) and remnant polarization (Pr) progressively decreased with increasing switching cycles due to domain pinning by charge point defects. However, an anomalous enhancement in both switching and remnant polarizations was observed upon application of the external compressive loads. After 5×106 cycles of polarization switching, Pswitching and Pr increase by about 13% and 6% at 40 MPa, respectively, while Pswitching and Pr increase by about 11% and 21% at 60 MPa, respectively. The improvement of fatigue resistance can be attributed to non-180° domain switching and suppression of microcracking, triggered by external mechanical loads.

  16. Grain growth kinetics and electrical properties of lanthanum modified lead zirconate titanate (9/65/35) based ferroelectric ceramics

    International Nuclear Information System (INIS)

    Roca, R. Alvarez; Guerrero, F.; Botero, E. R.; Garcia, D.; Eiras, J. A.; Guerra, J. D. S.

    2009-01-01

    The influence of the microstructural characteristics on the dielectric and electrical properties has been investigated for Nd 3+ doped lanthanum modified lead zirconate titanate ferroelectric ceramics, obtained by the conventional solid-state reaction method, by taking into account different sintering conditions. The grain growth mechanism has been investigated and a cubic-type grain growth law was observed for samples with grain size varying from 1.00 up to 2.35 μm. The porosity and grain size dependences of the phase transition parameters, such as the maximum dielectric permittivity and its corresponding temperature (ε m and T m , respectively) were also investigated. The ac conductivity analyses followed the universal Jonscher law. The behavior of the frequency exponent (s) was analyzed through the correlated barrier hopping model. Both ac and dc conductivity results have been correlated with the observed microstructural features

  17. Lead zirconate titanate nanoscale patterning by ultraviolet-based lithography lift-off technique for nano-electromechanical system applications.

    Science.gov (United States)

    Guillon, Samuel; Saya, Daisuke; Mazenq, Laurent; Costecalde, Jean; Rèmiens, Denis; Soyer, Caroline; Nicu, Liviu

    2012-09-01

    The advantage of using lead zirconate titanate (PbZr(0.54)Ti(0.46)O(3)) ceramics as an active material in nanoelectromechanical systems (NEMS) comes from its relatively high piezoelectric coefficients. However, its integration within a technological process is limited by the difficulty of structuring this material with submicrometer resolution at the wafer scale. In this work, we develop a specific patterning method based on optical lithography coupled with a dual-layer resist process. The main objective is to obtain sub-micrometer features by lifting off a 100-nm-thick PZT layer while preserving the material's piezoelectric properties. A subsequent result of the developed method is the ability to stack several layers with a lateral resolution of few tens of nanometers, which is mandatory for the fabrication of NEMS with integrated actuation and read-out capabilities.

  18. Determination of temperature dependence of piezoelectric coefficients matrix of lead zirconate titanate ceramics by quasi-static and resonance method

    Energy Technology Data Exchange (ETDEWEB)

    Li Fei; Xu Zhuo; Wei Xiaoyong; Yao Xi, E-mail: lifei1216@gmail.co [Electronic Materials Research Laboratory, Key Laboratory of the Ministry of Education, Xi' an Jiaotong University, Xi' an 710049 (China)

    2009-05-07

    The piezoelectric coefficients (d{sub 33}, -d{sub 31}, d{sub 15}, g{sub 33}, -g{sub 31}, g{sub 15}) of soft and hard lead zirconate titanate ceramics were measured by the quasi-static and resonance methods, at temperatures from 20 to 300 {sup 0}C. The results showed that the piezoelectric coefficients d{sub 33}, -d{sub 31} and d{sub 15} obtained by these two methods increased with increasing temperature for both hard and soft PZT ceramics, while the piezoelectric coefficients g{sub 33}, -g{sub 31} and g{sub 15} decreased with increasing temperature for both hard and soft PZT ceramics. In this paper, the observed results were also discussed in terms of intrinsic and extrinsic contributions to piezoelectric response.

  19. Using the methods of radiospectroscopy (EPR, NMR) to study the nature of the defect structure of solid solutions based on lead zirconate titanate (PZT)

    Czech Academy of Sciences Publication Activity Database

    Bykov, I. P.; Zagorodniy, A.Y.; Yurchenko, L.P.; Korduban, A.M.; Nejezchleb, K.; Trachevsky, V.V.; Dimza, V.; Jastrabík, Lubomír; Dejneka, Alexandr

    2014-01-01

    Roč. 61, č. 8 (2014), 1379-1385 ISSN 0885-3010 R&D Projects: GA TA ČR TA01010517; GA ČR GAP108/12/1941 Institutional support: RVO:68378271 Keywords : lead zirconate titanate ( PZT ) * EPR * NMR * XPS spectroscopy Subject RIV: BM - Solid Matter Physics ; Magnetism Impact factor: 1.512, year: 2014

  20. Refinement of the crystal structure of lead titanate with different degrees of imperfection of cationic and anionic sublattices by the Rietveld method

    International Nuclear Information System (INIS)

    Akimov, A.I.; Savchuk, G.K.; Rubtsov, V.A.; Letko, A.K.

    2003-01-01

    The parameters of the crystal structure of lead titanate with different degrees of imperfection of the anionic and cationic sublattices are refined by the Rietveld method. The experiments are carried out on a DRON-4 diffractometer (CuK α radiation; 20 deg. d 5.0-6.0%

  1. The effect of physiologic aqueous solutions on the perovskite material lead-lanthanum-zirconium titanate (PLZT): potential retinotoxicity.

    Science.gov (United States)

    Foster, William J; Meen, James K; Fox, Donald A

    2013-03-01

    Perovskite compounds, including lead-lanthanum-zirconium titanate (PLZT), have wide technological application because of their unique physical properties. The use of PLZT in neuro-prosthetic systems, such as retinal implants, has been discussed in a number of publications. Since inorganic lead is a retinotoxic compound that produces retinal degeneration, the long-term stability of PLZT in aqueous biological solutions must be determined. We evaluated the stability and effects of prolonged immersion of a PLZT-coated crystal in a buffered balanced salt solution. Scanning Electron Microscopy and Electron Dispersive Spectroscopy (EDS) using a JEOL JSM 5410 microscope equipped with EDS were utilized to evaluate the samples before and after prolonged immersion. We found that lead and other constituents of PLZT leached into the surrounding aqueous medium. By comparing the unit cell of PLZT with that of CaTiO(3), which has been found to react with aqueous fluids, Lead is in the same site in PLZT as Ca is in CaTiO(3). It is thus reasonable that PLZT will react with aqueous solutions. The results suggest that PLZT must either be coated with a protective layer or is not appropriate for long-term in vivo or in vitro biological applications.

  2. X-band EPR studies of ferroelectric lead titanate (PT), piezoelectric lead magnesium niobate (PMN), and PMN/PT powders at 10 and 85 K

    International Nuclear Information System (INIS)

    Huang, J.; Fitzgerald, J.J.; Chasteen, N.D.

    1998-01-01

    X-band EPR spectra of lead titanate (PT) and lead magnesium niobate (PMN) powders prepared by different synthetic methods and a PMN/PT powder of the composition 0.9 PMN/01 PT were obtained at 85 and 10 K. Several EPR signals due to adventitious Fe 3+ ion impurities, a signal due to the Ti 3+ ion, and a signal due to the Pb 3+ ion are observed for PT, PMN, and PMN/PT powders. The EPR signals observed at g = 2.0 and 6.0 are assigned to Fe 3+ ions in the B-sites of the perovskite lattice structure of lad titanate with axial symmetry. The EPR signals observed at g = 1.99 and 4.25 are assigned to Fe 3+ ions in the B-sites of the perovskite lattice structure of PMN and 0.9 PMN/0.1 PT materials with cubic and rhombic symmetries, respectively. The sharp EPR signal observed at g = 1.94 is assigned to Ti 3= ion for PT and 0.9 PMN/0.1 PT powders. In addition, a broader EPR signal at g = 2.28--2.30 for PMN obtained by the molten salt method is assigned to axial Pb 3+ ion sites in this PMN material. EPR results obtained here for the e 3+ ions in the B-sites of the PMN materials, in particular, suggest that both cubic and rhombic symmetry sites corresponding to a range of Nb(OMg) x (ONb) 6-x site configurations exist in the PMN. These EPR results indicate that PMN likely exists with partial B-site cation (Mg/Nb) ordering in the perovskite lattice structure

  3. Pressure, temperature, and electric field dependence of phase transformations in niobium modified 95/5 lead zirconate titanate

    Energy Technology Data Exchange (ETDEWEB)

    Dong, Wen D.; Carlos Valadez, J.; Gallagher, John A.; Jo, Hwan R.; Lynch, Christopher S., E-mail: cslynch@seas.ucla.edu [Department of Mechanical and Aerospace Engineering, The University of California, Los Angeles, 420 Westwood Plaza, Los Angeles, California 90095 (United States); Sahul, Raffi; Hackenberger, Wes [TRS Technologies, 2820 East College Avenue, State College, Pennsylvania 16801 (United States)

    2015-06-28

    Ceramic niobium modified 95/5 lead zirconate-lead titanate (PZT) undergoes a pressure induced ferroelectric to antiferroelectric phase transformation accompanied by an elimination of polarization and a volume reduction. Electric field and temperature drive the reverse transformation from the antiferroelectric to ferroelectric phase. The phase transformation was monitored under pressure, temperature, and electric field loading. Pressures and temperatures were varied in discrete steps from 0 MPa to 500 MPa and 25 °C to 125 °C, respectively. Cyclic bipolar electric fields were applied with peak amplitudes of up to 6 MV m{sup −1} at each pressure and temperature combination. The resulting electric displacement–electric field hysteresis loops were open “D” shaped at low pressure, characteristic of soft ferroelectric PZT. Just below the phase transformation pressure, the hysteresis loops took on an “S” shape, which split into a double hysteresis loop just above the phase transformation pressure. Far above the phase transformation pressure, when the applied electric field is insufficient to drive an antiferroelectric to ferroelectric phase transformation, the hysteresis loops collapse to linear dielectric behavior. Phase stability maps were generated from the experimental data at each of the temperature steps and used to form a three dimensional pressure–temperature–electric field phase diagram.

  4. Extraction of scandium by organic substance melts

    International Nuclear Information System (INIS)

    Gladyshev, V.P.; Lobanov, F.I.; Zebreva, A.I.; Andreeva, N.N.; Manuilova, O.A.; Il'yukevich, Yu.A.

    1984-01-01

    Regularities of scandium extraction by the melts of octadecanicoic acid, n-carbonic acids of C 17 -C 20 commerical fraction and mixtures of tributylphosphate (TBP) with paraffin at (70+-1) deg C have been studied. The optimum conditions for scandium extraction in the melt of organic substances are determined. A scheme of the extraction by the melts of higher carbonic acids at ninitial metal concentrations of 10 -5 to 10 -3 mol/l has been suggested. The scandium compound has been isolated in solid form, its composition having been determined. The main advantages of extraction by melts are as follows: a possibility to attain high distribution coefficients, distinct separation of phases after extraction, the absence of emulsions, elimination of employing inflammable and toxic solvents, a possibility of rapid X-ray fluorescence determinatinon of scandium directly in solid extract

  5. Scandium, yttrium and the lanthanide metals

    International Nuclear Information System (INIS)

    Brown, Paul L.; Ekberg, Christian

    2016-01-01

    The hydroxide and oxide phases that exist for scandium(III) include scandium hydroxide, which likely has both amorphous and crystalline forms, ScOOH(s), and scandium oxide. This chapter presents the data selected for the stability constants of the polymeric hydrolysis species of scandium at zero ionic strength. The behaviour of yttrium, and the lanthanide metals, in the environment is largely dependent on their solution equilibria. Hydrolysis and other complexation reactions of yttrium and the lanthanide metals are important in the disposal of nuclear waste. The trivalent lanthanide metals include lanthanum(III) through lutetium(III). A number of studies have reported a tetrad effect for the geochemical behaviour of the lanthanide series, including stability constants and distribution coefficients. The solubility of many of the lanthanide hydroxide phases has been studied at fixed ionic strength. In studying the hydrolysis of cerium(IV), a number of studies have utilised oxidation-reduction reactions in determining the relevant stability constants.

  6. Electric field tuning of magnetism in heterostructure of yttrium iron garnet film/lead magnesium niobate-lead zirconate titanate ceramic

    Science.gov (United States)

    Lian, Jianyun; Ponchel, Freddy; Tiercelin, Nicolas; Chen, Ying; Rémiens, Denis; Lasri, Tuami; Wang, Genshui; Pernod, Philippe; Zhang, Wenbin; Dong, Xianlin

    2018-04-01

    In this paper, the converse magnetoelectric (CME) effect by electric field tuning of magnetization in an original heterostructure composed of a polycrystalline yttrium iron garnet (YIG) film and a lead magnesium niobate-lead zirconate titanate (PMN-PZT) ceramic is presented. The magnetic performances of the YIG films with different thicknesses under a DC electric field applied to the PMN-PZT ceramics and a bias magnetic field are investigated. All the magnetization-electric field curves are found to be in good agreement with the butterfly like strain curve of the PMN-PZT ceramic. Both the sharp deformation of about 2.5‰ of PMN-PZT and the easy magnetization switching of YIG are proposed to be the reasons for the strongest CME interaction in the composite at the small electric coercive field of PMN-PZT (4.1 kV/cm) and the small magnetic coercive field of YIG (20 Oe) where the magnetic susceptibility reaches its maximum value. A remarkable CME coefficient of 3.1 × 10-7 s/m is obtained in the system with a 600 nm-thick YIG film. This heterostructure combining multiferroics and partially magnetized ferrite concepts is able to operate under a small or even in the absence of an external bias magnetic field and is more compact and power efficient than the traditional magnetoelectric devices.

  7. Extraction of scandium by aromatic carboxylic acids

    International Nuclear Information System (INIS)

    Kamenev, V.F.; Fadeeva, V.I.

    1977-01-01

    Extraction of complex compounds af scandium with salicylic, phenyl- and diphenylacetic acids with chloroform solutions of tetraethyldiamideheptylphosphate as a donor-active additive in relation to the pH and reagent concentration has been studied. Extraction of salicylates of some elements (Ta, Nb, Zr, Hf, Mo) by solutions of tetraethyldiamideheptylphosphate in chloroform has been investigated, and the possibility of their extraction separation from scandium is shown

  8. Extraction of scandium by aromatic carboxylic acids

    Energy Technology Data Exchange (ETDEWEB)

    Kamenev, V F; Fadeeva, V I [Moskovskij Gosudarstvennyj Univ. (USSR)

    1977-04-01

    Extraction of complex compounds af scandium with salicylic, phenyl- and diphenylacetic acids with chloroform solutions of tetraethyldiamideheptylphosphate as a donor-active additive in relation to the pH and reagent concentration has been studied. Extraction of salicylates of some elements (Ta, Nb, Zr, Hf, Mo) by solutions of tetraethyldiamideheptylphosphate in chloroform has been investigated, and the possibility of their extraction separation from scandium is shown.

  9. High Discharge Energy Density at Low Electric Field Using an Aligned Titanium Dioxide/Lead Zirconate Titanate Nanowire Array.

    Science.gov (United States)

    Zhang, Dou; Liu, Weiwei; Guo, Ru; Zhou, Kechao; Luo, Hang

    2018-02-01

    Polymer-based capacitors with high energy density have attracted significant attention in recent years due to their wide range of potential applications in electronic devices. However, the obtained high energy density is predominantly dependent on high applied electric field, e.g., 400-600 kV mm -1 , which may bring more challenges relating to the failure probability. Here, a simple two-step method for synthesizing titanium dioxide/lead zirconate titanate nanowire arrays is exploited and a demonstration of their ability to achieve high discharge energy density capacitors for low operating voltage applications is provided. A high discharge energy density of 6.9 J cm -3 is achieved at low electric fields, i.e., 143 kV mm -1 , which is attributed to the high relative permittivity of 218.9 at 1 kHz and high polarization of 23.35 µC cm -2 at this electric field. The discharge energy density obtained in this work is the highest known for a ceramic/polymer nanocomposite at such a low electric field. The novel nanowire arrays used in this work are applicable to a wide range of fields, such as energy harvesting, energy storage, and photocatalysis.

  10. Analysis on the anisotropic electromechanical properties of lead magnoniobate titanate single crystal for ring type ultrasonic motors

    Directory of Open Access Journals (Sweden)

    Xiang Shi

    2016-11-01

    Full Text Available This work discussed the optimized cut of single crystal lead magnoniobate titanate (PMNT for use of ring type travelling wave ultrasonic motors (USMs, according to anisotropic analysis on electromechanical properties. The selection criterion of crystal orientation relies on the circular uniformity of the induced travelling wave amplitude on the stator surface. By calculating the equivalent elastic coefficient c11 and lateral piezoelectric constant d31, the optimal crystal orientations were proposed for PMNT single crystals poled along different directions. For single crystal poled along c directions, the optimal orientation lies along [001]c with d31=-1335pC/N and k31=0.87. The crystallographic orientation [025]c is the optimized orientation for single crystals poled along c direction with d31=199pC/N and k31=0.55. The optimal orientation of 1R configuration is [332¯]c with a large enhancement of d31 = 1201 and k31=0.92.

  11. Effects of Thickness, Pulse Duration, and Size of Strip Electrode on Ferroelectric Electron Emission of Lead Zirconate Titanate Films

    Science.gov (United States)

    Yaseen, Muhammad; Ren, Wei; Chen, Xiaofeng; Feng, Yujun; Shi, Peng; Wu, Xiaoqing

    2018-02-01

    Sol-gel-derived lead zirconate titanate (PZT) thin-film emitters with thickness up to 9.8 μm have been prepared on Pt/TiO2/SiO2/Si wafer via chemical solution deposition with/without polyvinylpyrrolidone (PVP) modification, and the relationship between the film thickness and electron emission investigated. Notable electron emission was observed on application of a trigger voltage of 120 V for PZT film with thickness of 1.1 μm. Increasing the film thickness decreased the threshold field to initiate electron emission for non-PVP-modified films. In contrast, the electron emission behavior of PVP-modified films did not show significant dependence on film thickness, probably due to their porous structure. The emission current increased with decreasing strip width and space between strips. Furthermore, it was observed that increasing the duration of the applied pulse increased the magnitude of the emission current. The stray field on the PZT film thickness was also calculated and found to increase with increasing ferroelectric sample thickness. The PZT emitters were found to be fatigue free up to 105 emission cycles. Saturated emission current of around 25 mA to 30 mA was achieved for the electrode pattern used in this work.

  12. Fatigue and failure responses of lead zirconate titanate multilayer actuator under unipolar high-field electric cycling

    Science.gov (United States)

    Zeng, Fan Wen; Wang, Hong; Lin, Hua-Tay

    2013-07-01

    Lead zirconate titanate (PZT) multilayer actuators with an interdigital electrode design were studied under high electric fields (3 and 6 kV/mm) in a unipolar cycling mode. A 100 Hz sine wave was used in cycling. Five specimens tested under 6 kV/mm failed from 3.8 × 105 to 7 × 105 cycles, whereas three other specimens tested under 3 kV/mm were found to be still functional after 108 cycles. Variations in piezoelectric and dielectric responses of the tested specimens were observed during the fatigue test, depending on the measuring and cycling conditions. Selected fatigued and damaged actuators were characterized using an impedance analyzer or small signal measurement. Furthermore, involved fatigue and failure mechanisms were investigated using scanning acoustic microscope and scanning electron microscope. The extensive cracks and porous regions were revealed across the PZT layers on the cross sections of a failed actuator. The results from this study have demonstrated that the high-field cycling can accelerate the fatigue of PZT stacks as long as the partial discharge is controlled. The small signal measurement can also be integrated into the large signal measurement to characterize the fatigue response of PZT stacks in a more comprehensive basis. The former can further serve as an experimental method to test and monitor the behavior of PZT stacks.

  13. Fabrication and energy harvesting characteristics of unimorph piezoelectric cantilever generators with interdigitated electrode lead zirconate titanate laminates

    Science.gov (United States)

    Lee, Min-seon; Yun, Ji-sun; Park, Woon-ik; Hong, Youn-woo; Cho, Jeong-ho; Paik, Jong-hoo; Park, Yong Ho; Son, Chun-myung; Jeong, Young Hun

    2017-12-01

    Interdigitated electrode (IDE) unimorph piezoelectric cantilever generators (UPCGs) were fabricated and their energy harvesting characteristics were investigated. A hard lead zirconate titanate (PZT) material with a high mechanical quality factor (Q m) of 1280 was used for the active piezoelectric film of the IDE UPCGs. Two different laminated IDE UPCGs were prepared; one has Ag/Pd interdigitated electrode (IDE) formed only on the top and bottom PZT sheets (D-IDE), while the other has Ag/Pd IDE on all of the PZT sheets (M-IDE). Cofiring was conducted at 1050 °C for 2 h for PZT laminates with IDEs. The fabricated IDE UPCGs exhibited power densities of 50.4 µW/cm3 for the D-IDE and 820 µW/cm3 for the M-IDE. The UPCG with the M-IDE exhibited a higher performance than that with the D-IDE. Specifically, a significantly enhanced normalized power factor of 670 µW/(g2·cm3) was found at 118 Hz across 100 kΩ.

  14. Bath temperature effect on magnetoelectric performance of Ni-lead zirconate titanate-Ni laminated composites synthesized by electroless deposition

    Energy Technology Data Exchange (ETDEWEB)

    Wu, W. [College of Materials Science and Technology, Nanjing University of Aeronautics and Astronautics, Nanjing 210016 (China); Wang, Y.G., E-mail: yingang.wang@nuaa.edu.c [College of Materials Science and Technology, Nanjing University of Aeronautics and Astronautics, Nanjing 210016 (China); Bi, K. [College of Materials Science and Technology, Nanjing University of Aeronautics and Astronautics, Nanjing 210016 (China)

    2011-03-15

    Magnetoelectric (ME) Ni-lead zirconate titanate-Ni laminated composites have been prepared by electroless deposition at various bath temperatures. The structure of the Ni layers deposited at various bath temperatures was characterized by X-ray diffraction, and microstructures were investigated by transmission electron microscopy. The magnetostrictive coefficients were measured by means of a resistance strain gauge. The transverse ME voltage coefficient {alpha}{sub E,31} was measured with the magnetic field applied parallel to the sample plane. The deposition rate of Ni increases with bath temperature. Ni layer with smaller grain size is obtained at higher bath temperature and shows higher piezomagnetic coefficient, promoting the ME effect of corresponding laminated composites. It is advantageous to increase the bath temperature, while trying to avoid the breaking of bath constituents. - Research Highlights: Laminated composites without interlayer are prepared by electroless deposition. Bath temperature affects the grain size of the deposited Ni layers. Higher bath temperature is beneficial to obtain stronger ME response.

  15. Pulsed laser deposition of piezoelectric lead zirconate titanate thin films maintaining a post-CMOS compatible thermal budget

    Science.gov (United States)

    Schatz, A.; Pantel, D.; Hanemann, T.

    2017-09-01

    Integration of lead zirconate titanate (Pb[Zrx,Ti1-x]O3 - PZT) thin films on complementary metal-oxide semiconductor substrates (CMOS) is difficult due to the usually high crystallization temperature of the piezoelectric perovskite PZT phase, which harms the CMOS circuits. In this work, a wafer-scale pulsed laser deposition tool was used to grow 1 μm thick PZT thin films on 150 mm diameter silicon wafers. Three different routes towards a post-CMOS compatible deposition process were investigated, maintaining a post-CMOS compatible thermal budget limit of 445 °C for 1 h (or 420 °C for 6 h). By crystallizing the perovskite LaNiO3 seed layer at 445 °C, the PZT deposition temperature can be lowered to below 400 °C, yielding a transverse piezoelectric coefficient e31,f of -9.3 C/m2. With the same procedure, applying a slightly higher PZT deposition temperature of 420 °C, an e31,f of -10.3 C/m2 can be reached. The low leakage current density of below 3 × 10-6 A/cm2 at 200 kV/cm allows for application of the post-CMOS compatible PZT thin films in low power micro-electro-mechanical-systems actuators.

  16. Effect of multi-layered bottom electrodes on the orientation of strontium-doped lead zirconate titanate thin films

    Energy Technology Data Exchange (ETDEWEB)

    Bhaskaran, M. [Microelectronics and Materials Technology Centre, School of Electrical and Computer Engineering, RMIT University, GPO Box 2476V, Melbourne, Victoria 3001 (Australia)], E-mail: madhu.bhaskaran@gmail.com; Sriram, S. [Microelectronics and Materials Technology Centre, School of Electrical and Computer Engineering, RMIT University, GPO Box 2476V, Melbourne, Victoria 3001 (Australia); Mitchell, D.R.G.; Short, K.T. [Institute of Materials Engineering, Australian Nuclear Science and Technology Organisation (ANSTO), PMB 1, Menai, New South Wales 2234 (Australia); Holland, A.S. [Microelectronics and Materials Technology Centre, School of Electrical and Computer Engineering, RMIT University, GPO Box 2476V, Melbourne, Victoria 3001 (Australia)

    2008-09-30

    This article discusses the results from X-ray diffraction (XRD) analysis of piezoelectric strontium-doped lead zirconate titanate (PSZT) thin films deposited on multi-layer coatings on silicon. The films were deposited by RF magnetron sputtering on a metal coated substrate. The aim was to exploit the pronounced piezoelectric effect that is theoretically expected normal to the substrate. This work highlighted the influence that the bottom electrode architecture exerts on the final crystalline orientation of the deposited thin films. A number of bottom electrode architectures were used, with the uppermost metal layer on which PSZT was deposited being gold or platinum. The XRD analysis revealed that the unit cell of the PSZT thin films deposited on gold and on platinum were deformed, relative to expected unit cell dimensions. Experimental results have been used to estimate the unit cell parameters. The XRD results were then indexed based on these unit cell parameters. The choice and the thickness of the intermediate adhesion layers influenced the relative intensity, and in some cases, the presence of perovskite peaks. In some cases, undesirable reactions between the bottom electrode layers were observed, and layer architectures to overcome these reactions are also discussed.

  17. Enhanced electrocaloric analysis and energy-storage performance of lanthanum modified lead titanate ceramics for potential solid-state refrigeration applications.

    Science.gov (United States)

    Zhang, Tian-Fu; Huang, Xian-Xiong; Tang, Xin-Gui; Jiang, Yan-Ping; Liu, Qiu-Xiang; Lu, Biao; Lu, Sheng-Guo

    2018-01-10

    The unique properties and great variety of relaxer ferroelectrics make them highly attractive in energy-storage and solid-state refrigeration technologies. In this work, lanthanum modified lead titanate ceramics are prepared and studied. The giant electrocaloric effect in lanthanum modified lead titanate ceramics is revealed for the first time. Large refrigeration efficiency (27.4) and high adiabatic temperature change (1.67 K) are achieved by indirect analysis. Direct measurements of electrocaloric effect show that reversible adiabatic temperature change is also about 1.67 K, which exceeds many electrocaloric effect values in current direct measured electrocaloric studies. Both theoretical calculated and direct measured electrocaloric effects are in good agreements in high temperatures. Temperature and electric field related energy storage properties are also analyzed, maximum energy-storage density and energy-storage efficiency are about 0.31 J/cm 3 and 91.2%, respectively.

  18. Electron Emission And Beam Generation Using Ferroelectric Cathodes (electron Beam Generation, Lead Lanthanum Zicronate Titanate, High Power Traveling Wave Tube Amplfier)

    CERN Document Server

    Flechtner, D D

    1999-01-01

    In 1989, researchers at CERN published the discovery of significant electron emission (1– 100 A/cm2) from Lead- Lanthanum-Zirconate-Titanate (PLZT). The publication of these results led to international interest in ferroelectric cathodes studies for use in pulsed power devices. At Cornell University in 1991, experiments with Lead-Zirconate-Titanate (PZT) compositions were begun to study the feasibility of using this ferroelectric material as a cathode in the electron gun section of High Power Traveling Wave Tube Amplifier Experiments. Current-voltage characteristics were documented for diode voltages ranging from 50– 500,000 V with anode cathode gaps of.5– 6 cm. A linear current-voltage relation was found for voltages less than 50 kV. For diode voltages ≥ 200 kV, a typical Child-Langmuir V3/2 dependence was observed...

  19. Lead removal from aqueous solutions by potassium titanate doped with silica; Remocion de plomo de soluciones acuosas por titanato de potasio dopado con silice

    Energy Technology Data Exchange (ETDEWEB)

    Aguilar G, M. A.; Aguilar E, A. [Centro de Investigacion en Materiales Avanzados, Miguel de Cervantes No. 120, 31109 Chihuahua (Mexico); Gorokhovsky, A. V.; Escalante G, J. I. [Centro de Investigacion y de Estudios Avanzados, Unidad Saltillo, Carretera Saltillo-Mty Km. 13, Apdo. Postal 663, Saltillo 25000, Coahuila (Mexico)], e-mail: mgzlz@hotmail.com

    2009-07-01

    This paper is related to elimination of Pb{sup 2+} ions from aqueous solutions by adsorption in potassium tetra titanate doped with silica. The adsorbent was prepared in the form of granules with pastes of potassium poly titanate (45 %), powdered Pyrex glass (5 %) and potato starch (50 %), which were extruded and thermally treated at 1100 C. The structural characteristic of the granulated adsorbent allows reducing the Pb concentration, from the solutions eluted through an adsorption column, to levels below the requirement of national standards. The effects of the time of saturation of the adsorbent and the ph of the solution were also investigated on the effectiveness of the adsorption of Pb. The mechanism of lead adsorption, by the developed adsorbent, is considered as a combination of adsorption, ion-exchange and co-precipitation processes. It is also shown that the lead-saturated adsorbent could be utilized to produce high-strength non-dangerous ceramic materials. (Author)

  20. Dynamic pyroelectric response of composite based on ferroelectric copolymer of poly(vinylidene fluoride-trifluoroethylene) and ferroelectric ceramics of barium lead zirconate titanate

    Energy Technology Data Exchange (ETDEWEB)

    Solnyshkin, A.V. [Tver State University, Department of Condensed Matter Physics, Tver (Russian Federation); National Research University ' ' MIET' ' , Department of Intellectual Technical Systems, Zelenograd, Moscow (Russian Federation); Morsakov, I.M.; Bogomolov, A.A. [Tver State University, Department of Condensed Matter Physics, Tver (Russian Federation); Belov, A.N.; Vorobiev, M.I.; Shevyakov, V.I.; Silibin, M.V. [National Research University ' ' MIET' ' , Department of Intellectual Technical Systems, Zelenograd, Moscow (Russian Federation); Shvartsman, V.V. [University of Duisburg-Essen, Institute for Materials Science, Essen (Germany)

    2015-10-15

    In this work, pyroelectric properties of composite films on the basis of poly(vinylidene fluoride-trifluoroethylene) copolymer with a various level of ferroelectric ceramics inclusions of barium lead zirconate titanate solid solution were investigated by the dynamic method. The composite films were prepared by the solvent cast method. The unusual spike-like dynamic response with a quasi-stationary component was observed. It is supposed that composite films may be effectively used for pyroelectric applications. (orig.)

  1. Influence of poling on far-infrared response of lead zirconate titanate ceramics

    Czech Academy of Sciences Publication Activity Database

    Simon, E.; Hlinka, Jiří; Kamba, Stanislav; Gregora, Ivan; Erhart, J.

    2009-01-01

    Roč. 106, č. 7 (2009), 074104/1-074104/5 ISSN 0021-8979 R&D Projects: GA AV ČR KAN301370701; GA MŠk ME08109; GA ČR GA202/06/0411 Institutional research plan: CEZ:AV0Z10100520 Keywords : ceramics * dielectric polarisation * infrared spectra * lead compounds * phonons Subject RIV: BM - Solid Matter Physics ; Magnetism Impact factor: 2.072, year: 2009

  2. Effect of ultraviolet light on fatigue of lead zirconate titanate thin-film capacitors

    Science.gov (United States)

    Lee, J.; Esayan, S.; Safari, A.; Ramesh, R.

    1994-07-01

    Fatigue of Pb(Zr0.52Ti0.48)O3 (PZT) thin-film capacitors was studied under UV light (He-Cd laser, λ=325 nm). The remanent polarization of the PZT film capacitors increased upon light illumination. Fatigue resistance was also improved under UV light. During fatigue test, the change in polarization of PZT films upon UV light illumination increased gradually with cycling. These results were examined within the framework of the polarization screening model, which is suggested as an essential process for fatigue. This leads to a conclusion that more charged defects are involved in the fatigue process through internal screening of polarization.

  3. A basic evaluated neutronic data file for elemental scandium

    International Nuclear Information System (INIS)

    Smith, A.B.; Meadows, J.W.; Howerton, R.J.

    1992-01-01

    This report documents an evaluated neutronic data file for elemental scandium, presented in the ENDF/B-VI format. This file should provide basic nuclear data essential for neutronic calculations involving elemental scandium. No equivalent file was previously available

  4. Defect enhanced optic and electro-optic properties of lead zirconate titanate thin films

    Directory of Open Access Journals (Sweden)

    M. M. Zhu

    2011-12-01

    Full Text Available Pb(Zr1-xTixO3 (PZT thin films near phase morphotropic phase boundary were deposited on (Pb0.86La0.14TiO3-coated glass by radio frequency sputtering. A retrieved analysis shows that the lattice parameters of the as-grown PZT thin films were similar to that of monoclinic PZT structure. Moreover, the PZT thin films possessed refractive index as high as 2.504 in TE model and 2.431 in TM model. The as-grown PZT thin film had one strong absorption peak at 632.6 nm, which attributed to lead deficiency by quantitative XPS analysis. From the attractive properties achieved, electro-optic and photovoltaic characteristic of the films were carried out.

  5. Lead-free piezoelectric (K,Na)NbO3-based ceramic with planar-mode coupling coefficient comparable to that of conventional lead zirconate titanate

    Science.gov (United States)

    Ohbayashi, Kazushige; Matsuoka, Takayuki; Kitamura, Kazuaki; Yamada, Hideto; Hishida, Tomoko; Yamazaki, Masato

    2017-06-01

    We developed a (K,Na)NbO3-based lead-free piezoelectric ceramic with a KTiNbO5 system, (K1- x Na x )0.86Ca0.04Li0.02Nb0.85O3-δ-K0.85Ti0.85Nb1.15O5-BaZrO3-Fe2O3-MgO (K1- x N x N-NTK-FM). K1- x N x N-NTK-FM ceramic exhibits a very dense microstructure and a coupling coefficient of k p = 0.59, which is almost comparable to that of conventional lead zirconate titanate (PZT). The (K,Na)NbO3-based ceramic has the Γ15 mode for a wide x range. The nanodomains of orthorhombic (K,Na)NbO3 with the M3 mode coexist within the tetragonal Γ15 mode (K,Na)NbO3 matrix. Successive phase transition cannot occur with increasing x. The maximum k p is observed at approximately the minimum x required to generate the M3 mode phase. Unlike the behavior at the morphotropic phase boundary (MPB) in PZT, the characteristics of K1- x N x N-NTK-FM ceramic in this region changed moderately. This gentle phase transition seems to be a relaxor, although the diffuseness degree is not in line with this hypothesis. Furthermore, piezoelectric properties change from “soft” to “hard” upon the M3 mode phase aggregation.

  6. Electrical conductivity improvement of strontium titanate doped lead vanadate glasses by nanocrystallization

    Energy Technology Data Exchange (ETDEWEB)

    El-Desoky, M.M., E-mail: mmdesoky@gmail.co [Physics Department, Faculty of Education, Suez Canal University, El-Arish (Egypt); Zayed, H.S.S.; Ibrahim, F.A.; Ragab, H.S. [Physics Department, Faculty of Education, Suez Canal University, El-Arish (Egypt)

    2009-11-15

    The structural and electrical conductivity (sigma) of annealed SrTiO{sub 3}-PbO{sub 2}-V{sub 2}O{sub 5} glasses were studied. The annealing of initially glass samples leads to formation of nanocrystalline grains embedded in the glassy matrix. XRD patterns of the glass-ceramic samples show that nanocrystals were embedded in the glassy matrix with an average grain size of 32 nm. The glass-ceramic nanocrystals obtained by annealing at temperatures close to the crystallization temperature T{sub c} exhibit enhancement of electrical conductivity up to four orders of magnitude than initially glasses. The enhancement of the electrical conductivity due to annealing was attributed to two interdependent factors: (i) an increase of concentration of V{sup 4+}-V{sup 5+} pairs; and (ii) formation of defective, well-conducting regions along the glass-crystallites interfaces. From the conductivity temperature relation, it was found that small polaron hopping model was applicable at temperature above theta{sub D}/2 (theta{sub D}, the Debye temperature). The electrical conduction at T >theta{sub D}/2 was due to non-adiabatic small polaron hopping (SPH) of electrons between vanadium ions. The parameters obtained from the fits of the experimental data to this model appear reasonable and are consistent with glass composition.

  7. Electrical conductivity improvement of strontium titanate doped lead vanadate glasses by nanocrystallization

    International Nuclear Information System (INIS)

    El-Desoky, M.M.; Zayed, H.S.S.; Ibrahim, F.A.; Ragab, H.S.

    2009-01-01

    The structural and electrical conductivity (σ) of annealed SrTiO 3 -PbO 2 -V 2 O 5 glasses were studied. The annealing of initially glass samples leads to formation of nanocrystalline grains embedded in the glassy matrix. XRD patterns of the glass-ceramic samples show that nanocrystals were embedded in the glassy matrix with an average grain size of 32 nm. The glass-ceramic nanocrystals obtained by annealing at temperatures close to the crystallization temperature T c exhibit enhancement of electrical conductivity up to four orders of magnitude than initially glasses. The enhancement of the electrical conductivity due to annealing was attributed to two interdependent factors: (i) an increase of concentration of V 4+ -V 5+ pairs; and (ii) formation of defective, well-conducting regions along the glass-crystallites interfaces. From the conductivity temperature relation, it was found that small polaron hopping model was applicable at temperature above θ D /2 (θ D , the Debye temperature). The electrical conduction at T >θ D /2 was due to non-adiabatic small polaron hopping (SPH) of electrons between vanadium ions. The parameters obtained from the fits of the experimental data to this model appear reasonable and are consistent with glass composition.

  8. A polarized Raman study of the relaxor and ferroelectric states of La-modified lead zirconate titanate ceramics

    International Nuclear Information System (INIS)

    El Marssi, M.; Farhi, R.; Viehland, D.

    1997-01-01

    Lanthanum modified lead zirconate titanate ceramics with La/Zr/Ti ratios of 6/40/60, 12/40/60, 5/65/35, and 9/65/35 have been studied by polarized Raman scattering. In the two former (tetragonal-type) compositions, selection rules were rather well defined and allowed an assignment of the Raman lines at lower temperature. These selection rules disappeared for 6/40/60 but remained for 12/40/60 even at higher temperatures. The behavior of the two latter (rhombohedral-type compositions) was quite different. No assignment of lines could be done. In addition, the spectra recorded in parallel and crossed polarizations were almost identical for 5/65/35 regardless of temperature. A very smeared paraelectric to ferroelectric transition was evidenced by Raman intensity measurements for this composition. On the contrary, selection rules were always present for the relaxor composition 9/65/35 which were similar to those for 12/40/60 and 6/40/60. This suggests that both tetragonal and rhombohedral-type local polar order is present for 9/65/35. The spectra of the field induced ferroelectric phase for 9/65/35 revealed no selection rules, similar to 5/65/35. This is attributed to the onset of only medium range ferroelectric order. Finally, Raman spectra recorded on powders of every composition did not reveal any selection rules, suggesting that intergranular effects might play a significant role in the behavior of these materials. copyright 1997 American Institute of Physics

  9. X-ray and neutron scattering on disordered nanosize clusters: a case study of lead-zirconate-titanate solid solutions

    Energy Technology Data Exchange (ETDEWEB)

    Frantti, Johannes; Fujioka, Yukari [Finnish Research and Engineering, Helsinki (Finland)

    2015-04-01

    Defects and frequently used defect models of solids are reviewed. Signatures for identifying the disorder from x-ray and neutron scattering data are given. To give illustrative examples how technologically important defects contribute to x-ray and neutron scattering numerical method able to treat non-periodical solids possessing several simultaneous defect types is given for simulating scattering in nanosize disordered clusters. The approach takes particle size, shape, and defects into account and isolates element specific signals. As a case study a statistical approximation model for lead-zirconate titanate [Pb(Zr{sub x}Ti{sub 1-x})O{sub 3}, PZT] is introduced. PZT is a material possessing several defect types, including substitutional, displacement and surface defects. Spatial composition variation is taken into account by introducing a model in which the edge lengths of each cell depend on the distribution of Zr and Ti ions in the cluster. Spatially varying edge lengths and angles is referred to as microstrain. The model is applied to compute the scattering from ellipsoid shaped PZT clusters and to simulate the structural changes as a function of average composition. Two-phase co-existence range, the so called morphotropic phase boundary composition is given correctly. The composition at which the rhombohedral and tetragonal cells are equally abundant was x ∼ 0.51. Selected x-ray and neutron Bragg reflection intensities and line shapes were simulated. Examples of the effect of size and shape of the scattering clusters on diffraction patterns are given and the particle dimensions, computed through Scherrer equation, are compared with the exact cluster dimensions. Scattering from two types of 180 domains in spherical particles, one type assigned to Ti-rich PZT and the second to the MPB and Zr-rich PZT, is computed. We show how the method can be used for modelling polarization reversal. (copyright 2015 by WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim)

  10. Fabrication and characterization of thick-film piezoelectric lead zirconate titanate ceramic resonators by tape-casting.

    Science.gov (United States)

    Qin, Lifeng; Sun, Yingying; Wang, Qing-Ming; Zhong, Youliang; Ou, Ming; Jiang, Zhishui; Tian, Wei

    2012-12-01

    In this paper, thick-film piezoelectric lead zirconate titanate (PZT) ceramic resonators with thicknesses down to tens of micrometers have been fabricated by tape-casting processing. PZT ceramic resonators with composition near the morphotropic phase boundary and with different dopants added were prepared for piezoelectric transducer applications. Material property characterization for these thick-film PZT resonators is essential for device design and applications. For the property characterization, a recently developed normalized electrical impedance spectrum method was used to determine the electromechanical coefficient and the complex piezoelectric, elastic, and dielectric coefficients from the electrical measurement of resonators using thick films. In this work, nine PZT thick-film resonators have been fabricated and characterized, and two different types of resonators, namely thickness longitudinal and transverse modes, were used for material property characterization. The results were compared with those determined by the IEEE standard method, and they agreed well. It was found that depending on the PZT formulation and dopants, the relative permittivities ε(T)(33)/ε(0) measured at 2 kHz for these thick-films are in the range of 1527 to 4829, piezoelectric stress constants (e(33) in the range of 15 to 26 C/m(2), piezoelectric strain constants (d(31)) in the range of -169 × 10(-12) C/N to -314 × 10(-12) C/N, electromechanical coupling coefficients (k(t)) in the range of 0.48 to 0.53, and k(31) in the range of 0.35 to 0.38. The characterization results shows tape-casting processing can be used to fabricate high-quality PZT thick-film resonators, and the extracted material constants can be used to for device design and application.

  11. Dielectric properties of composite based on ferroelectric copolymer of poly(vinylidene fluoride-trifluoroethylene and ferroelectric ceramics of barium lead zirconate titanate

    Directory of Open Access Journals (Sweden)

    A. V. Solnyshkin

    2017-10-01

    Full Text Available A study of dielectric properties of composite films on the base of poly(vinylidene fluoride-trifluoroethylene copolymer P(VDF-TrFE and ferroelectric ceramics of barium lead zirconate titanate (BPZT solid solution is presented in this work. The composite films containing up to 50 vol.% of BPZT grains with size ∼1μm were prepared by the solvent cast method. Frequency dependences of real and imaginary components of the complex permittivity were determined. The concentration dependence of the dielectric constant was discussed.

  12. Experimental Determination of Effect of Variable Resistance on Lead ZirconateTitanate (PZT-5A4Eunder various Thermal and Frequency Conditions

    Directory of Open Access Journals (Sweden)

    Hassan Elahi

    2014-12-01

    Full Text Available A specially designed apparatus and circuit working on the principle of inverse piezoelectricity due to the effect of polarization was used to find the relationship between resistance and peak to peak voltage of Lead Zirconate Titanate (PZT-5A4E by shocking it at variable frequencies and at variable resistances under various thermal conditions within Curie temperature limit using equivalent circuit method. It was found that by increasing temperature, peak to peak voltage increases and similarly by increasing frequency, peak to peak voltage decreases and with the increase in resistance peak to peak voltage decreases.

  13. Method for chromatographically recovering scandium and yttrium

    International Nuclear Information System (INIS)

    Snyder, T.S.; Stoltz, R.A.

    1991-01-01

    This paper describes a method for chromatographically recovering scandium and yttrium from the residue of a sand chlorinator. It comprises: providing a residue from a sand chlorinator, the residue containing scandium, yttrium, sodium, calcium and at least one radioactive metal of the group consisting of radium, thorium and uranium; digesting the residue with an acid to produce an aqueous liquid containing scandium, yttrium, sodium, calcium and at least one radioactive metal of the group consisting of radium, thorium and uranium; feeding the metal containing liquid through a cation exchanger; eluding the cation exchanger with an acid eluant to to produce: a first eluate containing at least half of the total weight of the calcium and sodium in the feed liquid; a second eluate containing at least half of the total weight of the one or more radioactive metals in the feed liquid; a third eluate containing at least half of the yttrium in the feed liquid, and a fourth eluate containing at least half of the weight of the scandium in the feed liquid

  14. Titan Casts Revealing Shadow

    Science.gov (United States)

    2004-05-01

    A rare celestial event was captured by NASA's Chandra X-ray Observatory as Titan -- Saturn's largest moon and the only moon in the Solar System with a thick atmosphere -- crossed in front of the X-ray bright Crab Nebula. The X-ray shadow cast by Titan allowed astronomers to make the first X-ray measurement of the extent of its atmosphere. On January 5, 2003, Titan transited the Crab Nebula, the remnant of a supernova explosion that was observed to occur in the year 1054. Although Saturn and Titan pass within a few degrees of the Crab Nebula every 30 years, they rarely pass directly in front of it. "This may have been the first transit of the Crab Nebula by Titan since the birth of the Crab Nebula," said Koji Mori of Pennsylvania State University in University Park, and lead author on an Astrophysical Journal paper describing these results. "The next similar conjunction will take place in the year 2267, so this was truly a once in a lifetime event." Animation of Titan's Shadow on Crab Nebula Animation of Titan's Shadow on Crab Nebula Chandra's observation revealed that the diameter of the X-ray shadow cast by Titan was larger than the diameter of its solid surface. The difference in diameters gives a measurement of about 550 miles (880 kilometers) for the height of the X-ray absorbing region of Titan's atmosphere. The extent of the upper atmosphere is consistent with, or slightly (10-15%) larger, than that implied by Voyager I observations made at radio, infrared, and ultraviolet wavelengths in 1980. "Saturn was about 5% closer to the Sun in 2003, so increased solar heating of Titan may account for some of this atmospheric expansion," said Hiroshi Tsunemi of Osaka University in Japan, one of the coauthors on the paper. The X-ray brightness and extent of the Crab Nebula made it possible to study the tiny X-ray shadow cast by Titan during its transit. By using Chandra to precisely track Titan's position, astronomers were able to measure a shadow one arcsecond in

  15. Complexometric determination of scandium and aluminium

    International Nuclear Information System (INIS)

    Tikhonov, V.N.

    1980-01-01

    Described is the complexometric determination of scandium and aluminium by the method of reverse titration of EDTA excess by indium salt solution in the presence of the xylenol orange indicator. For the method selectivity increase fluorides are used as a camouflage substance at low pH values (2.5-3.0). The excess fluoride-ions preventing titration are bound by boric acid. Y, Tb, Ti, Zr, Cu, Zn, V, Mo, Co, Cr prevent the determination of Sc and Al

  16. Damage-free patterning of ferroelectric lead zirconate titanate thin films for microelectromechanical systems via contact printing

    Science.gov (United States)

    Welsh, Aaron

    This thesis describes the utilization and optimization of the soft lithographic technique, microcontact printing, to additively pattern ferroelectric lead zirconate titanate (PZT) thin films for application in microelectromechanical systems (MEMS). For this purpose, the solution wetting, pattern transfer, printing dynamics, stamp/substrate configurations, and processing damages were optimized for incorporation of PZT thin films into a bio-mass sensor application. This patterning technique transfers liquid ceramic precursors onto a device stack in a desired configuration either through pattern definition in the stamp, substrate or both surfaces. It was determined that for ideal transfer of the pattern from the stamp to the substrate surface, wetting between the solution and the printing surface is paramount. To this end, polyurethane-based stamp surfaces were shown to be wet uniformly by polar solutions. Patterned stamp surfaces revealed that printing from raised features onto flat substrates could be accomplished with a minimum feature size of 5 mum. Films patterned by printing as a function of thickness (0.1 to 1 mum) showed analogous functional properties to continuous films that were not patterned. Specifically, 1 mum thick PZT printed features had a relative permittivity of 1050 +/- 10 and a loss tangent of 2.0 +/- 0.4 % at 10 kHz; remanent polarization was 30 +/- 0.4 muC/cm 2 and the coercive field was 45 +/- 1 kV/cm; and a piezoelectric coefficient e31,f of -7 +/- 0.4 C/m2. No pinching in the minor hysteresis loops or splitting of the first order reversal curve (FORC) distributions was observed. Non-uniform distribution of the solution over the printed area becomes more problematic as feature size is decreased. This resulted in solutions printed from 5 mum wide raised features exhibiting a parabolic shape with sidewall angles of ˜ 1 degree. As an alternative, printing solutions from recesses in the stamp surface resulted in more uniform solution thickness

  17. Potential for photocatalytic degradation of the potassic diclofenac using scandium and silver modified titanium dioxide thin films

    International Nuclear Information System (INIS)

    Ciola, R.A.; Oliveira, C.T.; Lopes, S.A.; Cavalheiro, A.A.

    2011-01-01

    The potential for photocatalytic degradation of the potassic diclofenac drug was investigated using titanium dioxide thin films modified with two modifier types, scandium and silver, both prepared by Sol-Gel method. It was demonstrated by UVVis spectroscopy analysis of the solutions containing the drug, under UV-A light irradiation that the degradation efficiency of the titanium dioxide photocatalyst is dependent of the semiconductor nature and that the scandium accelerates the first step of the degradation when compared to the silver. This result seems to be related to the redox potential of the electron-hole pair, once the scandium modifying sample generates a p type semiconductor that reduces the band gap. The extra holes attract more strongly the chorine ion present in diclofenac and leading to the releasing more easily. However, after the first byproducts degradation the following steps are not facilitated, making the silver modifying more advantageous. (author)

  18. Using the methods of radiospectroscopy (EPR, NMR) to study the nature of the defect structure of solid solutions based on lead zirconate titanate (PZT).

    Science.gov (United States)

    Bykov, Igor; Zagorodniy, Yuriy; Yurchenko, Lesya; Korduban, Alexander; Nejezchleb, Karel; Trachevsky, Vladimir; Dimza, Vilnis; Jastrabik, Lubomir; Dejneka, Alexander

    2014-08-01

    The nature of intrinsic and impurity point defects in lead zirconate titanate (PZT) ceramics has been explored. Using electron paramagnetic resonance (EPR), nuclear magnetic resonance (NMR), and X-ray photoelectron spectroscopy (XPS) methods, several impurity sites have been identified in the materials, including the Fe(3+)-oxygen vacancy (VO) complex and Pb ions. Both of these centers are incorporated into the PZT lattice. The Fe(3+) –VО paramagnetic complex serves as a sensitive probe of the local crystal field in the ceramic; the symmetry of this defect roughly correlates with PZT phase diagram as the composition is varied from PbTiO3 to PbZrO3. NMR spectra (207)Pb in PbTiO3, PbZrO3, and PZT with iron content from 0 to 0.4 wt% showed that increasing the iron concentration leads to a distortion of the crystal structure and to improvement of the electrophysical parameters of the piezoceramics. This is due to the formation of a phase which has a higher symmetry, but at high concentrations of iron (>0.4 wt%), it leads to sharp degradation of electrophysical parameters.

  19. Ternary scandium and transition metals germanides

    International Nuclear Information System (INIS)

    Kotur, B.Ya.

    1992-01-01

    Brief review of data on phase diagram of ternary Sc-Me-Ge systems (Me-d - , f-transition element) is given. Isothermal sections at 870 and 1070 K of 17 ternary systems are plotted. Compositions and their structural characteristics are presented. Variability of crystal structure is typical for ternary scandium germanides: 70 compounds with the studied structure belong to 23 structural types. Ternary germanides isostructural to types of Sm 4 Ge 4 , ZrCrSi 2 , ZrNiAl, ScCeSi, TiNiSi U 4 Re 7 Si 6 145 compounds from 70 under investigation are mostly formed in studied systems

  20. Extraction of scandium salicylate by tetraethyldiamidoheptyl phosphate

    Energy Technology Data Exchange (ETDEWEB)

    Kamenev, V F; Fadeeva, V I; Zyk, N V [Moskovskij Gosudarstvennyj Univ. (USSR). Kafedra Analiticheskoj Khimii

    1976-11-01

    Scandium salicylate is extracted with chloroform in a narrow pH range 3-4 and at the maximum concentration of salicylic acid (H/sub 2/A) in an organic phase, the distribution coefficient reaches 0.1. In the presence of tetraethyldiamideheptylphosphate (DAHP) the zone of maximum extraction grows and the distribution coefficient increases. The ratio of the components in the complex extracted is Sc:H/sub 2/A:DAHPh=1:3:2. The extraction constant is Ksub(ex)=(2.00+-0.02).

  1. Influence of scandium on the pitting behaviour of Al-Zn-Mg-Cu alloys

    Energy Technology Data Exchange (ETDEWEB)

    Wloka, J. [Department of Materials Sciences, University of Erlangen-Nuremberg, Martensstrasse 7, D-91058 Erlangen (Germany); Virtanen, S. [Department of Materials Sciences, University of Erlangen-Nuremberg, Martensstrasse 7, D-91058 Erlangen (Germany)], E-mail: virtanen@ww.uni-erlangen.de

    2007-11-15

    In this paper the influence of small scandium additions (<0.26 wt.%) on the corrosion properties of the high-strength Al-Zn-Mg-Cu alloy AA7010 is investigated. The addition of scandium (in combination with the grain refiner Zr) leads to the formation of Al{sub 3}Sc{sub x}Zr{sub 1-x} phases. These coarse particles disturb the grain structure near the particle/matrix interface, which facilitates the initiation of localized corrosion in potentio-dynamic scans. Microelectrochemical investigations revealed a slightly cathodic character of these particles and a passive range beyond the breakdown potential of the matrix. Mass loss measurements show that the addition of scandium increases the mass loss during the initial period. The corrosion morphology was investigated with optical and scanning electron microscopy. The composition of the phases was determined with energy-dispersive X-ray analysis. Micro-capillary measurements were performed to investigate the electrochemical properties of single phases surrounded by matrix.

  2. Titan's greenhouse and antigreenhouse effects

    Science.gov (United States)

    Mckay, Christopher P.; Pollack, James B.; Courtin, Regis

    1992-01-01

    Thermal mechanisms active in Titan's atmosphere are discussed in a brief review of data obtained during the Voyager I flyby in 1980. Particular attention is given to the greenhouse effect (GHE) produced by atmospheric H2, N2, and CH4; this GHE is stronger than that on earth, with CH4 and H2 playing roles similar to those of H2O and CO2 on earth. Also active on Titan is an antigreenhouse effect, in which dark-brown and orange organic aerosols block incoming solar light while allowing IR radiation from the Titan surface to escape. The combination of GHE and anti-GHE leads to a surface temperature about 12 C higher than it would be if Titan had no atmosphere.

  3. An Optimal Image-Based Method for Identification of Acoustic Emission (AE) Sources in Plate-Like Structures Using a Lead Zirconium Titanate (PZT) Sensor Array

    Science.gov (United States)

    Zhou, Li

    2018-01-01

    This paper proposes an innovative method for identifying the locations of multiple simultaneous acoustic emission (AE) events in plate-like structures from the view of image processing. By using a linear lead zirconium titanate (PZT) sensor array to record the AE wave signals, a reverse-time frequency-wavenumber (f-k) migration is employed to produce images displaying the locations of AE sources by back-propagating the AE waves. Lamb wave theory is included in the f-k migration to consider the dispersive property of the AE waves. Since the exact occurrence time of the AE events is usually unknown when recording the AE wave signals, a heuristic artificial bee colony (ABC) algorithm combined with an optimal criterion using minimum Shannon entropy is used to find the image with the identified AE source locations and occurrence time that mostly approximate the actual ones. Experimental studies on an aluminum plate with AE events simulated by PZT actuators are performed to validate the applicability and effectiveness of the proposed optimal image-based AE source identification method. PMID:29466310

  4. An Optimal Image-Based Method for Identification of Acoustic Emission (AE) Sources in Plate-Like Structures Using a Lead Zirconium Titanate (PZT) Sensor Array.

    Science.gov (United States)

    Yan, Gang; Zhou, Li

    2018-02-21

    This paper proposes an innovative method for identifying the locations of multiple simultaneous acoustic emission (AE) events in plate-like structures from the view of image processing. By using a linear lead zirconium titanate (PZT) sensor array to record the AE wave signals, a reverse-time frequency-wavenumber (f-k) migration is employed to produce images displaying the locations of AE sources by back-propagating the AE waves. Lamb wave theory is included in the f-k migration to consider the dispersive property of the AE waves. Since the exact occurrence time of the AE events is usually unknown when recording the AE wave signals, a heuristic artificial bee colony (ABC) algorithm combined with an optimal criterion using minimum Shannon entropy is used to find the image with the identified AE source locations and occurrence time that mostly approximate the actual ones. Experimental studies on an aluminum plate with AE events simulated by PZT actuators are performed to validate the applicability and effectiveness of the proposed optimal image-based AE source identification method.

  5. Effect of MnO2, Bi2O3, and ZnO additions on the electrical properties of lead zirconate titanate piezo ceramics

    International Nuclear Information System (INIS)

    Klimov, V.V.; Selikova, N.I.; Bronnikov, A.N.

    2006-01-01

    The effect of manganese dioxide additions on the electrical properties of lead zirconate titanate (PZT) piezo ceramics has been investigated. The results demonstrate that, taken alone, manganese dioxide does not ensure the formation of hard PZT. The valence state of manganese in the piezo ceramics is shown to be 4+ if no other dopants are present and 3+ if manganese is introduced in combination with Bi and Zn. Microstructural examination indicates that the grain size of the singly doped ceramics is 5-15 μm, while that of the codoped ceramics is 1-3 μm. The polarization current curves of the piezo ceramics containing manganese, bismuth, and zinc oxides have extra maxima, which points to significant internal fields. The manganese is shown to reside at grain boundaries. The conclusion is made that it is the composition of Mn-containing intergranular phases, rather than the presence of manganese ions, that plays a key role in the formation of hard piezo ceramics [ru

  6. Scandium: its occurrence, chemistry, physics, metallurgy, biology, and technology

    International Nuclear Information System (INIS)

    Horovitz, C.T.

    1975-01-01

    This book describes the following aspects of scandium: discovery and history, occurrence in nature, geochemistry and mineralogy, chemical, physical and technological properties, fabrication and metallurgy, its biological significance and toxicology, and its uses. (Extensive references for each chapter)

  7. The crystal structure of scandium dyhydrate triglycolate

    International Nuclear Information System (INIS)

    Dukareva, L.M.; Antishkina, A.S.; Porai-Koshits, M.A.; Ostrikova, V.N.; Arkhangel'skij, I.V.; Amanov, A.Z.

    1978-01-01

    The structure of colorless crystals of scandium glycolate dehydrate Sc(CH 2 OHCOO) 3 x2H 2 O, synthesized at the chemical department of MSU has been investigated. Parameters of the monoclinic lattice are determined according to roentgenograms of swing and Kforograms and are specified using the DRON-1 diffractor: a=14.624-+0.005 A; b=13.052-+0.003 A; c=5.730+-0.003 A; γ=96.26 deg+-0.01 deg; rhosub(exper.)=1.09 g/cm 3 ; Z=4; Sp.=P 2/b. Experimental photographic data are obtained using the KFOR chamber. Scannings of the layer lines h anti Ko-h anti K4, containing 742 independent reflexes are taken. Deciphering of the structure is carried out by means of analysis of the Paterson functions distribution and conventional and differential electron densities. Description of the system is presented

  8. Thickness dependence of the poling and current-voltage characteristics of paint films made up of lead zirconate titanate ceramic powder and epoxy resin

    Science.gov (United States)

    Egusa, Shigenori; Iwasawa, Naozumi

    1995-11-01

    A specially prepared paint made up of lead zirconate titanate (PZT) ceramic powder and epoxy resin was coated on an aluminum plate and was cured at room temperature, thus forming the paint film of 25-300 μm thickness with a PZT volume fraction of 53%. The paint film was then poled at room temperature, and the poling behavior was determined by measuring the piezoelectric activity as a function of poling field. The poling behavior shows that the piezoelectric activity obtained at a given poling field increases with an increase in the film thickness from 25 to 300 μm. The current-voltage characteristic of the paint film, on the other hand, shows that the increase in the film thickness leads not only to an increase in the magnitude of the current density at a given electric field but also to an increase in the critical electric field at which the transition from the ohmic to space-charge-limited conduction takes place. This fact indicates that the amount of the space charge of electrons injected into the paint film decreases as the film thickness increases. Furthermore, comparison of the current-voltage characteristic of the paint film with that of a pure epoxy film reveals that the space charge is accumulated largely at the interface between the PZT and epoxy phases in the paint film. On the basis of this finding, a model is developed for the poling behavior of the paint film by taking into account a possible effect of the space-charge accumulation and a broad distribution of the electric field in the PZT phase. This model is shown to give an excellent fit to the experimental data of the piezoelectric activity obtained here as a function of poling field and film thickness.

  9. A concept for the development of piezoceramic materials based on lead zirconate titanate (PZT). Part 2; Ein Entwicklungskonzept piezokeramischer Werkstoffe auf der Basis von Bleizirkonattitanat (PZT). Teil 2

    Energy Technology Data Exchange (ETDEWEB)

    Helke, G. [CeramTec AG, Lauf a.d. Pegnitz (Germany)

    2002-07-01

    Piezoceramic ceramics based on Lead Zircontate Titanate (PZT) show - within a relatively close Zr/Ti ratio range (close to the ratio 0.5/0.5) - extreme values for remanent polarization P{sub r} and the dielectric coefficient {epsilon}{sub 33}{sup {tau}}/{epsilon}{sub 0} as well as their corresponding piezoelectric coefficients. Remanent polarization P{sub t} can be directly correlated to the structural parameter {delta} (spontaneous deformation) and the domain mobility {eta}. PZT modification results from the substitution of isovalent or heterovalent ions, thereby taking ion radii and valency at the A and B sites of the perovskite-type lattice under consideration. The substitution of specific ions is the process used to develop new piezoceramic materials which is mainly applied to determine the values of specific parameters corresponding to technical requirements. (orig.) [German] Piezoelektrische Keramiken auf der Basis von Bleizirkonattitanat (PZT) weisen in einem relativ engen Bereich des Zr/Ti-Verhaeltnisses (nahe dem Verhaeltnis 0,5/0,5). Extremwerte der remanenten Polarisation P{sub r} und der Dielektrizitaetskonstanten {epsilon}{sub 33}{sup {tau}}/{epsilon}{sub 0} sowie der von ihnen abhaengigen piezoelektrischen Kenngroessen auf. Die remanente Polarisation P{sub r} laesst sich unmittelbar dem Strukturparameter {delta} (spontane Deformation) und der Domaenenbeweglichkeit {eta} zuordnen. Die Modifikation von PZT erfolgt durch Substitution isovalenter oder heterovalenter Ionen unter Beruecksichtigung von Ionenradien und -wertigkeit auf A- und B-Plaetzen des Perowskigitters. Die Substitution bestimmter Ionen ist das Verfahren zur Schaffung neuer piezokeramischer Werkstoffe und wird insbesondere zur Einstellung der Werte einzelner Kenngroessen auf einem bestimmten Niveau entsprechend den technischen Anforderungen angewendet. (orig.)

  10. A concept for the development of piezoceramic materials based on lead zirconate titanate (PZT). Part 1; Ein Entwicklungskonzept piezokeramischer Werkstoffe auf der Basis von Gleizirkonattitanat (PZT). Teil 1

    Energy Technology Data Exchange (ETDEWEB)

    Helke, G. [CeramTec AG, Lauf a.d. Pegnitz (Germany)

    2002-07-01

    Piezoceramic ceramics based on Lead Zircontate Titanate (PZT) show - within a relatively close Zr/Ti ratio range (close to the ratio 0.5/0.5) - extreme values for remanent polarization P{sub r} and the dielectric coefficient {epsilon}{sub 33}{sup {tau}}/{epsilon}{sub 0} as well as their corresponding piezoelectric coefficients. Remanent polarization P{sub t} can be directly correlated to the structural parameter {delta} (spontaneous deformation) and the domain mobility {eta}. PZT modification results from the substitution of isovalent or heterovalent ions, thereby taking ion radii and valency at the A and B sites of the perovskite-type lattice under consideration. The substitution of specific ions is the process used to develop new piezoceramic materials which is mainly applied to determine the values of specific parameters corresponding to technical requirements. (orig.) [German] Piezoelektrische Keramiken auf der Basis von Bleizirkonattitanat (PZT) weisen in einem relativ engen Bereich des Zr/Ti-Verhaeltnisses (nahe dem Verhaeltnis 0,5/0,5). Extremwerte der remanenten Polarisation P{sub r} und der Dielektrizitaetskonstanten {epsilon}{sub 33}{sup {tau}}/{epsilon}{sub 0} sowie der von ihnen abhaengigen piezoelektrischen Kenngroessen auf. Die remanente Polarisation P{sub r} laesst sich unmittelbar dem Strukturparameter {delta} (spontane Deformation) und der Domaenenbeweglichkeit {eta} zuordnen. Die Modifikation von PZT erfolgt durch Substitution isovalenter oder heterovalenter Ionen unter Beruecksichtigung von Ionenradien und -wertigkeit auf A- und B-Plaetzen des Perowskigitters. Die Substitution bestimmter Ionen ist das Verfahren zur Schaffung neuer piezokeramischer Werkstoffe und wird insbesondere zur Einstellung der Werte einzelner Kenngroessen auf einem bestimmten Niveau entsprechend den technischen Anforderungen angewendet. (orig.)

  11. High energy storage density over a broad temperature range in sodium bismuth titanate-based lead-free ceramics.

    Science.gov (United States)

    Yang, Haibo; Yan, Fei; Lin, Ying; Wang, Tong; Wang, Fen

    2017-08-18

    A series of (1-x)Bi 0.48 La 0.02 Na 0.48 Li 0.02 Ti 0.98 Zr 0.02 O 3 -xNa 0.73 Bi 0.09 NbO 3 ((1-x)LLBNTZ-xNBN) (x = 0-0.14) ceramics were designed and fabricated using the conventional solid-state sintering method. The phase structure, microstructure, dielectric, ferroelectric and energy storage properties of the ceramics were systematically investigated. The results indicate that the addition of Na 0.73 Bi 0.09 NbO 3 (NBN) could decrease the remnant polarization (P r ) and improve the temperature stability of dielectric constant obviously. The working temperature range satisfying TCC 150  °C  ≤±15% of this work spans over 400 °C with the compositions of x ≥ 0.06. The maximum energy storage density can be obtained for the sample with x = 0.10 at room temperature, with an energy storage density of 2.04 J/cm 3 at 178 kV/cm. In addition, the (1-x)LLBNTZ-xNBN ceramics exhibit excellent energy storage properties over a wide temperature range from room temperature to 90 °C. The values of energy storage density and energy storage efficiency is 0.91 J/cm 3 and 79.51%, respectively, for the 0.90LLBNTZ-0.10NBN ceramic at the condition of 100 kV/cm and 90 °C. It can be concluded that the (1-x)LLBNTZ-xNBN ceramics are promising lead-free candidate materials for energy storage devices over a broad temperature range.

  12. Lifetime measurements and oscillator strengths in singly ionized scandium and the solar abundance of scandium

    Science.gov (United States)

    Pehlivan Rhodin, A.; Belmonte, M. T.; Engström, L.; Lundberg, H.; Nilsson, H.; Hartman, H.; Pickering, J. C.; Clear, C.; Quinet, P.; Fivet, V.; Palmeri, P.

    2017-12-01

    The lifetimes of 17 even-parity levels (3d5s, 3d4d, 3d6s and 4p2) in the region 57 743-77 837 cm-1 of singly ionized scandium (Sc II) were measured by two-step time-resolved laser induced fluorescence spectroscopy. Oscillator strengths of 57 lines from these highly excited upper levels were derived using a hollow cathode discharge lamp and a Fourier transform spectrometer. In addition, Hartree-Fock calculations where both the main relativistic and core-polarization effects were taken into account were carried out for both low- and high-excitation levels. There is a good agreement for most of the lines between our calculated branching fractions and the measurements of Lawler & Dakin in the region 9000-45 000 cm-1 for low excitation levels and with our measurements for high excitation levels in the region 23 500-63 100 cm-1. This, in turn, allowed us to combine the calculated branching fractions with the available experimental lifetimes to determine semi-empirical oscillator strengths for a set of 380 E1 transitions in Sc II. These oscillator strengths include the weak lines that were used previously to derive the solar abundance of scandium. The solar abundance of scandium is now estimated to logε⊙ = 3.04 ± 0.13 using these semi-empirical oscillator strengths to shift the values determined by Scott et al. The new estimated abundance value is in agreement with the meteoritic value (logεmet = 3.05 ± 0.02) of Lodders, Palme & Gail.

  13. Highly sensitive luminescence method of scandium determination in the products of metallurgical reprocessing

    International Nuclear Information System (INIS)

    Matveets, M.A.; Akhmetova, S.D.

    1988-01-01

    Highly sensitive reaction of scandium with 1,10-phenanthroline and eosin is used for the development of luminescence method of its determination in metallurgical products. The effect of interfering elements is eliminated by scandium extraction with monocarboxylic acids. The method permits to determine scandium content from 5 x 10 -5 % (Sr 0.15 - 0.25)

  14. Size Effects on Deformation and Fracture of Scandium Deuteride Films.

    Energy Technology Data Exchange (ETDEWEB)

    Teresi, C. S. [Univ. of Minnesota, Minneapolis, MN (United States); Hintsala, E. [Univ. of Minnesota, Minneapolis, MN (United States); Hysitron, Inc., Eden Prairie, MN (United States); Adams, David P. [Sandia National Lab. (SNL-NM), Albuquerque, NM (United States); Yang, Nancy Y. C. [Sandia National Lab. (SNL-NM), Albuquerque, NM (United States); Kammler, Daniel [Sandia National Lab. (SNL-NM), Albuquerque, NM (United States); Moody, N. R. [Univ. of Minnesota, Minneapolis, MN (United States); Gerberich, W. W. [Univ. of Minnesota, Minneapolis, MN (United States)

    2017-07-01

    Metal hydride films have been observed to crack during production and use, prompting mechanical property studies of scandium deuteride films. The following focuses on elastic modulus, fracture, and size effects observed in the system for future film mechanical behavior modeling efforts. Scandium deuteride films were produced through the deuterium charging of electron beam evaporated scandium films using X-ray diffraction, scanning Auger microscopy, and electron backscatter diffraction to monitor changes in the films before and after charging. Scanning electron microscopy, nanoindentation, and focused ion beam machined micropillar compression tests were used for mechanical characterization of the scandium deuteride films. The micropillars showed a size effect for flow stress, indicating that film thickness is a relevant tuning parameter for film performance, and that fracture was controlled by the presence of grain boundaries. Elastic modulus was determined by both micropillar compression and nanoindentation to be approximately 150 GPa, Fracture studies of bulk film channel cracking as well as compression induced cracks in some of the pillars yielded a fracture toughness around 1.0 MPa-m1/2. Preliminary Weibull distributions of fracture in the micropillars are provided. Despite this relatively low value of fracture toughness, scandium deuteride micropillars can undergo a large degree of plasticity in small volumes and can harden to some degree, demonstrating the ductile and brittle nature of this material

  15. Formation of scandium carbides and scandium oxycarbide from the elements at high-(P, T) conditions

    International Nuclear Information System (INIS)

    Juarez-Arellano, Erick A.; Winkler, Bjoern; Bayarjargal, Lkhamsuren; Friedrich, Alexandra; Milman, Victor; Kammler, Daniel R.; Clark, Simon M.; Yan Jinyuan; Koch-Mueller, Monika; Schroeder, Florian; Avalos-Borja, Miguel

    2010-01-01

    Synchrotron diffraction experiments with in situ laser heated diamond anvil cells and multi-anvil press synthesis experiments have been performed in order to investigate the reaction of scandium and carbon from the elements at high-(P,T) conditions. It is shown that the reaction is very sensitive to the presence of oxygen. In an oxygen-rich environment the most stable phase is ScO x C y , where for these experiments x=0.39 and y=0.50-0.56. If only a small oxygen contamination is present, we have observed the formation of Sc 3 C 4 , Sc 4 C 3 and a new orthorhombic ScC x phase. All the phases formed at high pressures and temperatures are quenchable. Experimentally determined elastic properties of the scandium carbides are compared to values obtained by density functional theory based calculations. - Graphical Abstract Legend (TOC Figure): Table of Contents Figure Selected images recorded with a MAR345 image plate detector show the reaction of α-Sc and graphite at high-(P,T) conditions. Left: mixture of α-Sc and graphite. Right: recovered sample after laser heated the diamond anvil cell.

  16. Smelting of Scandium by Microwave Irradiation

    Directory of Open Access Journals (Sweden)

    Satoshi Fujii

    2017-09-01

    Full Text Available Scandium is being explored as an alloying element for aluminum alloys, which are gaining importance as high-performance lightweight structural alloys in the transportation industry. A few years ago, Sc was also found to be suitable for use in electrical devices. High-Sc-content ScAlN thin films have attracted significant attention because of their strong piezoelectricity. The piezoelectric response of ScAlN suggests that ScAlN thin films formed on a hard substrate would be suitable surface acoustic wave wideband filters for next-generation wireless communication systems. However, it is often difficult to use ScAlN thin films in MEMS devices—including acoustic ones—because of the extremely high price of metallic Sc, given the difficulty associated with smelting it. Here, we propose a novel process for smelting Sc metal by microwave irradiation. Sc metal was able to be obtained successfully from ScF3 through a microwave-irradiation-based carbon reduction reaction. The reaction temperature for this reduction process was approximately 880°C, which is half of that for the conventional smelting process involving reduction with Ca. Thus, the proposed microwave irradiation process has significant potential for use in the smelting of Sc metal.

  17. Polar and chemical domain structures of lead scandium tantalate (PST)

    International Nuclear Information System (INIS)

    Peng, J.L.; Bursill, L.A.

    1993-01-01

    The local structure of chemical and polar domains and domain walls is determined directly by atomic resolution high-resolution electron microscopy. Thus the Pb, Ta and Sc atomic positions may be located in the images of very thin crystals. Furthermore the Pb cation displacements away from the ideal perovskite A-site have been measured directly for the first time. Local variations in polarization direction may be mapped directly off the images, provided certain electron optical conditions are met. The results are relevant to recent theories of polar-glass behaviour in relaxor-type complex oxide functional ceramics. 17 refs., 9 figs

  18. Scandium and zirconium ion complexing with salicylic acid

    International Nuclear Information System (INIS)

    Fadeeva, V.I.; Kochetkova, S.K.

    1979-01-01

    A study has been made of the extraction of complexes containing scandium and zirconium compounds and salicylic acid by using benzene, nitrobenzene, chloroform and isoamyl alcohol. It is shown that in the metal concentration range 10 -5 -10 -3 mole/l scandium forms mononuclear complexes composed of Sc(HSal) 3 (pH 2 (pH>4), zirconium - polynuclear complexes Zrsub(x)(OH)sub(y)(HSal)sub(n), where the x:n ratio varies from 0.5 to 1.5. Stability constants have been calculated for the salicylate scandium complexes in aqueous solution, equal to β 1 =(3+-1)x10 2 ; β 2 =(5.0+-0.6)x10 4 ; β 3 =(5.3+-0.3)x10 6

  19. Scandium and zirconium ion complexing with salicylic acid

    Energy Technology Data Exchange (ETDEWEB)

    Fadeeva, V I; Kochetkova, S K [Moskovskij Gosudarstvennyj Univ. (USSR)

    1979-08-01

    A study has been made of the extraction of complexes containing scandium and zirconium compounds and salicylic acid by using benzene, nitrobenzene, chloroform and isoamyl alcohol. It is shown that in the metal concentration range 10/sup -5/-10/sup -3/ mole/l scandium forms mononuclear complexes composed of Sc(HSal)/sub 3/ (pH<=4) and Sc(OH)(HSal)/sub 2/ (pH>4), zirconium - polynuclear complexes Zrsub(x)(OH)sub(y)(HSal)sub(n), where the x:n ratio varies from 0.5 to 1.5. Stability constants have been calculated for the salicylate scandium complexes in aqueous solution, equal to ..beta../sub 1/=(3+-1)x10/sup 2/; ..beta../sub 2/=(5.0+-0.6)x10/sup 4/; ..beta../sub 3/=(5.3+-0.3)x10/sup 6/.

  20. Titan Aerial Daughtercraft

    Data.gov (United States)

    National Aeronautics and Space Administration — Saturn's giant moon Titan has become one of the most fascinating bodies in the Solar System. Titan is the richest laboratory in the solar system for studying...

  1. Titanic: A Statistical Exploration.

    Science.gov (United States)

    Takis, Sandra L.

    1999-01-01

    Uses the available data about the Titanic's passengers to interest students in exploring categorical data and the chi-square distribution. Describes activities incorporated into a statistics class and gives additional resources for collecting information about the Titanic. (ASK)

  2. Scandium/carbon filters for soft x rays

    NARCIS (Netherlands)

    Artioukov, IA; Kasyanov, YS; Kopylets, IA; Pershin, YP; Romanova, SA

    2003-01-01

    This Note deals with thin-film soft x-ray filters for operation at the wavelengths near carbon K edge (similar to4.5 nm). The filters were fabricated by magnetron sputtering deposition of thin layers of scandium (total thickness 0.1-0.2 mum) onto films of polypropylene (thickness 1.5 mum) and

  3. Heat capacity and solid solubility of iron in scandium

    International Nuclear Information System (INIS)

    Tsang, T.-W.E.

    1981-01-01

    The maximum solid solubility of iron in scandium was determined to be between 50 and 85 at.ppm in the as-cast condition. As the concentration of iron increases, it segregates along the grain boundary, as is evident from optical metallography and electron microprobe examinations. Annealing also causes the iron dissolved in scandium to separate out and cluster along the grain boundary. Heat capacity measurements show an anomaly in the C/T versus T 2 plots for iron concentrations of 19 at.ppm or greater. For iron dissolved in solid scandium the excess entropy due to the iron impurity is in agreement with the theoretical prediction of ck ln(2S + 1) for an impurity-conduction electron (Kondo) interaction, but is 4 - 8 times larger than the theoretical prediction when iron segregates along the grain boundary. Furthermore, our results suggest that most of the previously reported low temperature physical properties of scandium are probably in error because of either iron impurity-conduction electron interactions or Fe-Fe interactions in the precipitated second-phase Sc-Fe compound. (Auth.)

  4. Thermoelectric material comprising scandium doped zinc cadmium oxide

    DEFF Research Database (Denmark)

    2016-01-01

    There is presented a composition of scandium doped Zinc Cadmium Oxide with the general formula ZnzCdxScyO which the inventors have prepared, and for which material the inventors have made the insight that it is particularly advantageous as an n-type oxide material, such as particularly advantageous...

  5. Synthesis and properties of scandium ortho-phosphate

    International Nuclear Information System (INIS)

    Eshchenko, L.S.; Pechkovskij, V.V.; Dvoskina, R.N.

    1979-01-01

    With the aim to elucidate the influence of synthesis conditions on the chemical composition and properties of orthophosphates of scandium, the interaction of orthophosphoric acid and scandium-containing component (oxide or salt) was studied under various conditions. In the interaction of scandium salt, phosphoric acid and ammonia at room temperature and pH 3.0; 5.0; 7.0 and 9.0 amorphous scandium phosphates have been obtained with the composition of x Sc 2 O 3 xY P 2 O 5 xz NH 3 xn H 2 O. After prolonged staying in mother liquor, roentgenoamorphous precipitates of phosphates transform into the crystalline state. The dependences are studied of the specific surface of amorphous phosphates on pH of precipitation and temperature of the heat treatment (200-800 deg C). Precipitates obtained in a neutral medium at 400 deg C temperature of thermal treatment, show a maximum specific surface. At a temperature of 820-840 deg C the crystallization of amorphous phase occurs followed by the recrystallization and formation of anhydrous SePO 4 of zircon type

  6. Chemical investigation of Titan and Triton tholins

    Science.gov (United States)

    Mcdonald, Gene D.; Thompson, W. R.; Heinrich, Michael; Khare, Bishun N.; Sagan, Carl

    1994-01-01

    We report chromatographic and spectroscopic analyses of both Titan and Triton tholins, organic solids made from the plasma irradiation of 0.9:0.1 and 0.999:0.001 N2/CH4 gas mixtures, respectively. The lower CH4 mixing ratio leads to a nitrogen-richer tholin (N/C greater than 1), probably including nitrogen heterocyclic compounds. Unlike Titan tholin, bulk Triton tholin is poor in nitriles. From high-pressure liquid chromatography, ultraviolet and infrared spectroscopy, and molecular weight estimation by gel filtration chromatography, we conclude that (1) several H2O-soluble fractions, each with distinct UV and IR spectral signatures, are present, (2) these fractions are not identical in the two tholins, (3) the H2O-soluble fractions of Titan tholins do not contain significant amounts of nitriles, despite the major role of nitriles in bulk Titan tholin, and (4) the H2O-soluble fractions of both tholins are mainly molcules containing about 10 to 50 (C + N) atoms. We report yields of amino acids upon hydrolysis of Titan and Triton tholins. Titan tholin is largely insoluble in the putative hydrocarbon lakes or oceans on Titan, but can yield the H2O-soluble species investigated here upon contact with transient (e.g., impact-generated) liquid water.

  7. Characterization and excitation behaviour studies of radionuclide (scandium) in glass matrix

    International Nuclear Information System (INIS)

    Rehana, Ishrat; Shahid, K.A.; Husain, S.; Muhammad, Din

    1999-01-01

    Directional movements of bed load in marine sediments are studied using a radioactive tracer, scandium, similar to the natural sediment in the area. Scandium glass prepared for this purpose was analyzed by atomic emission spectrography for quality assurance purposes. A buffer composed of graphite with 5% germanium oxide was used for accurate and reproducible analyses. The role of this buffer in the excitation behavior of scandium and variations in spectral line intensity with respect to various influencing parameters are reported. Volatilization of scandium was observed using the moving plate technique, with a dc-arc as the excitation source

  8. Scandium - problem of ultra-trace-element essentiality

    International Nuclear Information System (INIS)

    Kist, A.A.; Zkuk, L.I.; Danilova, E.A.; Makhmudov, E.A.

    2006-01-01

    Full text: Role of constitutional and essential elements in Life is known quite well. It is also well known that all chemical elements present in the living matter. Nevertheless essentiality of at least 55 chemical elements (more than a half of number of natural elements) is still not accepted. In many cases these elements presumably play important role in the Life. On the other hand their essentiality is still under doubt. One of the 'strange' elements in this connection is scandium. Scandium is an element which is very 'simple' for instrumental neutron activation analysis (INAA). For many years in our laboratory were carried out studies on animals and human tissues and fluids elemental composition using INAA in which data for scandium were obtained as 'redundant' information. Essentiality of scandium was newer proven using accepted criteria of elements. Nevertheless in our studies were found various regularities, statistically significant inter-elemental correlations and correlations between elements in tissues and fluids versus clinic and biochemical data. There are some examples. There were found correlations of scandium hair concentration and blood glucose (r=0.68±0.13), body mass index (r=0.86±0.07), leukocyte with phagocytic activity migration inhibition test (r=0.68±0.18), size of cavity of the left heart auricle (r=-0.65±0.16), final systolic bulk (r=0.80±0.12), stroke output of heart (r=-0.79±0.12), final diastolic bulk (0.88±0.0080) etc. In addition using gel filtration in rat liver cytosol was found peak of scandium in elution curve. Examples and correlations given in the paper say in favor that scandium may play quite important role in biological processes and that the biological role of scandium should be studied more intensive. The most important criterion is an appearance of the organism dysfunction in case of removal of the studied elements from the diet (intake) which in all other sides remains completely valuable and disappearance of all

  9. Complexing of scandium with eriochromecyanine R and cetyltrimethylammonium

    International Nuclear Information System (INIS)

    Tikhonov, V.N.; Samarkina, T.V.

    1978-01-01

    Complexing of scandium with eriochromecyanine R (ECC) in the presence of cetyltrimethylammonium (CTA) is studied. At optimum value of pH 6.2 a three-component complex of blue colour is forming with the Sc:ECC:CTA = 1:3:5 relation of compounds. Lambdasub(max) for the complex varies from 585 to 615 nm, molarabsorption coefficient is equal to (1.48+-0.02)x10 5 . A method of photometric determination of Sc with ECC and CTA is suggested. Even considerable quantities of Mg, Ca, Sr, Zn, Cd, La, Mn, Ni do not affect the Sc determination, whereas Cu, Be, Al, Ga, Fe(3) and Pd(2) affect it to a great degree even in relation of 1:1. Camouflaging substances such as fluorides, citrates, tartrates and EDTA prevent from scandium complexing, that is why they should not be used to increase the determination selectivity

  10. Incommensurate composite crystal structure of scandium-II

    International Nuclear Information System (INIS)

    Fujihisa, Hiroshi; Gotoh, Yoshito; Yamawaki, Hiroshi; Sakashita, Mami; Takeya, Satoshi; Honda, Kazumasa; Akahama, Yuichi; Kawamura, Haruki

    2005-01-01

    The long-unknown crystal structure of the high pressure phase scandium-II was solved by powder x-ray diffraction and was found to have tetragonal host channels along the c axis and guest chains that are incommensurate with the host, as well as the high pressure phases of Ba, Sr, Bi, and Sb. The pressure dependences of the lattice constants, the incommensurability, the atomic distances, and the atomic volume were investigated

  11. Tetragonal ternary borides: superconductivity, ferromagnetism and the role of scandium

    International Nuclear Information System (INIS)

    Matthias, B.T.; Patel, C.K.N.; Barz, H.; Corenzwit, E.; Vandenberg, J.M.

    1978-01-01

    The authors report and discuss two discoveries made while studying the condensation phenomena of ternary rhodium borides, MRh 4 B 4 . M is generally a trivalent transition metal, usually a rare earth element RE. An exception is scandium which by itself does not form an isomorphous boride, but in combination with many other elements will do just that. A suprising correlation between ferromagnetic and superconducting transition temperatures has been found. (Auth.)

  12. Determination of scandium with salicylaldehyde and 2-aminobenzenearsonic acid

    International Nuclear Information System (INIS)

    Farias, P.A.M.; Hainberger, L.; Andrade, H.A.S.

    1984-01-01

    A new method for the spectrophotometric determination of scandium by means of a coloured complex formed with salicylaldehyde and 2-aminobenzenearsonic acid is described. Lambert-Beer's law is followed in the range of 0.2 - 2.0 μg/ml of the final solution. The maximum amounts of 39 ions that may be present without interfering in the method are listed. (Author) [pt

  13. Hubble Observes Surface of Titan

    Science.gov (United States)

    1994-01-01

    's first flyby of Titan, the spacecraft is to release the European Space Agency's Huygens Probe to parachute to Titan's surface. Images like Smith's team has taken of Titan can be used to identify choice landing spots - - and help engineers and scientists understand how Titan's winds will blow the parachute through the satellite's atmosphere.UA scientists play major roles in the Cassini mission: Carolyn C. Porco, an associate professor at the Lunar and Planetary Laboratory, leads the 14-member Cassini Imaging Team. Jonathan I. Lunine, also an associate professor at the lab, is the only American selected by the European Space Agency to be on the three-member Huygens Probe interdisciplinary science team. Smith is a member of research professor Martin G. Tomasko's international team of scientists who will image the surface of Titan in visible light and in color with the Descent Imager/Spectral Radiometer, one of five instruments in the Huygens Probe's French, German, Italian and U.S. experiment payload. Senior research associate Lyn R. Doose is also on Tomasko's team. Lunine and LPL professor Donald M. Hunten are members of the science team for another U.S. instrument on that payload, the gas chromatograph mass spectrometer. Hunten was on the original Cassini mission science definition team back in 1983.PHOTO CAPTION: Four global projections of the HST Titan data, separated in longitude by 90 degrees. Upper left: hemisphere facing Saturn. Upper right: leading hemisphere (brightest region). Lower left: the hemisphere which never faces Saturn. Lower right: trailing hemisphere. Not that these assignments assume that the rotation is synchronous. The imaging team says its data strongly support this assumption -- a longer time baseline is needed for proof. The surface near the poles is never visible to an observer in Titan's equatorial plane because of the large optical path.The Wide Field/Planetary Camera 2 was developed by the Jet Propulsion Laboratory and managed by the Goddard

  14. The characteristics of aluminum-scandium alloys processed by ECAP

    International Nuclear Information System (INIS)

    Venkateswarlu, K.; Rajinikanth, V.; Ray, Ajoy Kumar; Xu Cheng; Langdon, Terence G.

    2010-01-01

    Aluminum-scandium alloys were prepared having different scandium additions of 0.2, 1.0 and 2.0 wt.% and these alloys were processed by equal-channel angular pressing (ECAP) at 473 K. The results show the grain refinement of the aluminum matrix and the morphology of the Al 3 Sc precipitates depends strongly on the scandium concentration. The tensile properties were evaluated after ECAP by pulling to failure at initial strain rates from 1.0 x 10 -3 to 1.0 x 10 -1 s -1 . The Al-1% Sc alloy exhibited the highest tensile strength of ∼250 MPa at a strain rate of 1.0 x 10 -1 s -1 . This alloy also exhibited a superior grain refinement of ∼0.4 μm after ECAP where this is attributed to a smaller initial grain size and an optimum volume fraction of dispersed Al 3 Sc precipitates having both micrometer and nanometer sizes.

  15. Potential for photocatalytic degradation of the potassic diclofenac using scandium and silver modified titanium dioxide thin films; Potencial de degradacao fotocatalitica do diclofenaco potassico utilizando filmes finos de dioxido de titanio modificado com escandio e prata

    Energy Technology Data Exchange (ETDEWEB)

    Ciola, R.A.; Oliveira, C.T.; Lopes, S.A.; Cavalheiro, A.A., E-mail: rafaelciola@hotmail.com [Universidade Estadual de Mato Grosso do Sul (UFMS), Navirai, MS (Brazil). Centro de Pesquisas Tecnologicas em Recursos Naturais

    2011-07-01

    The potential for photocatalytic degradation of the potassic diclofenac drug was investigated using titanium dioxide thin films modified with two modifier types, scandium and silver, both prepared by Sol-Gel method. It was demonstrated by UVVis spectroscopy analysis of the solutions containing the drug, under UV-A light irradiation that the degradation efficiency of the titanium dioxide photocatalyst is dependent of the semiconductor nature and that the scandium accelerates the first step of the degradation when compared to the silver. This result seems to be related to the redox potential of the electron-hole pair, once the scandium modifying sample generates a p type semiconductor that reduces the band gap. The extra holes attract more strongly the chorine ion present in diclofenac and leading to the releasing more easily. However, after the first byproducts degradation the following steps are not facilitated, making the silver modifying more advantageous. (author)

  16. Nonthermal atmospheric escape from Mars and Titan

    International Nuclear Information System (INIS)

    Lammer, H.; Bauer, S.J.

    1991-01-01

    Energy flux spectra and particle concentrations of the hot O and N coronae from Mars and Titan, respectively, resulting primarily from dissociative recombination of molecular ions, have been calculated by means of a Monte Carlo method. The calculated energy flux spectra lead to an escape flux null esc ∼ 6 x 10 6 cm -2 s -1 for Mars and null esc ∼ 2 x 10 6 cm -2 s -1 for Titan, corresponding to a mass loss of about 0.14 kg/s for Mars and about 0.3 kg/s for Titan. (The contribution of electron impact ionization on N 2 amounts to only about 25% of Titan's mass loss.) Mass loss via solar and magnetospheric wind is also estimated using newly calculated mass loading limits. The mass loss via ion pickup from the extended hot atom corona for Mars amounts to about 0.25 kg/s (O + ) and for Titan to about 50 g/s (N 2 + or H 2 CN + ). Thus, the total mass loss rate from Mars and Titan is about the same, i.e., 0.4 kg/s

  17. Interaction of scandium and titanium atoms with a carbon surface containing five- and seven-membered rings

    International Nuclear Information System (INIS)

    Krasnov, P. O.; Eliseeva, N. S.; Kuzubov, A. A.

    2012-01-01

    The use of carbon nanotubes coated by atoms of transition metals to store molecular hydrogen is associated with the problem of the aggregation of these atoms, which leads to the formation of metal clusters. The quantum-chemical simulation of cluster models of the carbon surface of a graphene type with scandium and titanium atoms has been performed. It has been shown that the presence of five- and seven-membered rings, in addition to six-membered rings, in these structures makes it possible to strongly suppress the processes of the migration of metal atoms over the surface, preventing their clustering.

  18. Adsorption and desorption of hydrolyzed metal ions. 3. Scandium and chromium

    International Nuclear Information System (INIS)

    Gray, B.; Matijevic, E.; Clarkson Univ., Potsdam, NY

    1987-01-01

    Adsorption of scandium(III) and chromium(III) species on a PVC latex was measured using radioactive isotopes; the uptake increased with increasing pH. The data were interpreted by combining aspects of the models of James and Healy and also of Anderson and Bockris. The experimental and calculated results agree quite well for scandium, but not for chromium. The deviation in the latter case is believed to be due to polymerization of the hydrolyzed chromium cations and to the interaction of chromium with the anionic surface groups of the latex. Neither of these interactions occur with scandium. Hydrolyzed scandium species adsorbed on the latex were removed by acidifying the dispersion, while chromium complexes were not, substantiating the proposed difference in the chemical nature of chromium and scandium species at the solid/solution interface. 32 refs.; 8 figs.; 8 tabs

  19. A new model for prediction of dispersoid precipitation in aluminium alloys containing zirconium and scandium

    International Nuclear Information System (INIS)

    Robson, J.D.

    2004-01-01

    A model has been developed to predict precipitation of ternary Al 3 (Sc, Zr) dispersoids in aluminium alloys containing zirconium and scandium. The model is based on the classical numerical method of Kampmann and Wagner, extended to predict precipitation of a ternary phase. The model has been applied to the precipitation of dispersoids in scandium containing AA7050. The dispersoid precipitation kinetics and number density are predicted to be sensitive to the scandium concentration, whilst the dispersoid radius is not. The dispersoids are predicted to enrich in zirconium during precipitation. Coarsening has been investigated in detail and it has been predicted that a steady-state size distribution is only reached once coarsening is well advanced. The addition of scandium is predicted to eliminate the dispersoid free zones observed in scandium free 7050, greatly increasing recrystallization resistance

  20. R.M.S Titanic 2003 Expedition on the Russian Research Vessel Akademik Mstislav Keldysh between 20030622 and 20030702

    Data.gov (United States)

    National Oceanic and Atmospheric Administration, Department of Commerce — As the leading ocean agency, and as per the Guidelines for Research, Exploration and Salvage of RMS Titanic, issued under the authority of the RMS Titanic Maritime...

  1. Kinetics and mechanism of hydrolysis of scandium sulfate

    International Nuclear Information System (INIS)

    Koshchej, E.V.; Stryapkov, A.V.; Podosenov, D.E.; Makarov, G.V.; Razdobreev, D.A.

    1998-01-01

    The Sc 2 (SO 4 ) 3 -H 2 SO 4 -H 2 O system is studied through the methods of pH-potentiometry, conductometry and turbidimetry at 298 and 318 K and ion force 0.01, 0.1 and 1.0. The hydrolysis mechanism including the processes in the system homogenous and heterogeneous constituents. The hydrolysis rates of scandium salts and their dependences on OH-ions concentration, solution ions force and temperature are found; the constants of the processes rate with participation of OH - and SO 4 2- ions and constants of the solid phase formation rate are calculated [ru

  2. Vibrational spectra of double oxides of calcium and scandium

    International Nuclear Information System (INIS)

    Porotnikov, N.V.; Kondratov, O.I.; Petrov, K.I.; Olikov, I.I.

    1981-01-01

    The vibrational spectra of calcium and scandium double oxides 40 CaSc 2 O 4 and 44 CaSc 2 O 4 in the range of 30-1000 cm -1 are studied. In the approximation of the polymer chains of the method of valent-force field the calculation of the theoretical vibrational spectrum of isotope-substituted compounds is made, the attribution of the experimental spectra is suggested, the frequency branches of the vibrations of periodic chains are built, the force field of crystals is evaluated [ru

  3. Study on the coextraction of scandium-yttrium-lumogallion complex

    International Nuclear Information System (INIS)

    Okada, T.; Shimoishi, Y.; Miyata, H.; Toei, K.

    1977-01-01

    The coextraction of scandium-yttrium-lumogallion [LMG;4-chloro-6-(2,4-dihydroxyphenylazo)-1-hydroxybenzene-2-sulfonic acid] into diethyl ether has been studied. The acid dissociation constants of LMG, pKsub(a2) and pKsub(a3), were estimated to be 6.24 and 8.05 respectively. The composition of the complex extracted was determined by using the radioisotopes 46 Sc and 90 Y and by spectrophotometry of LMG and the ratio of the components was Sc:Y:LMG = 1:1:3. The coextraction scheme was discussed briefly. (author)

  4. Titan's organic chemistry

    Science.gov (United States)

    Sagan, C.; Thompson, W. R.; Khare, B. N.

    1985-01-01

    Voyager discovered nine simple organic molecules in the atmosphere of Titan. Complex organic solids, called tholins, produced by irradiation of the simulated Titanian atmosphere, are consistent with measured properties of Titan from ultraviolet to microwave frequencies and are the likely main constituents of the observed red aerosols. The tholins contain many of the organic building blocks central to life on earth. At least 100-m, and possibly kms thicknesses of complex organics have been produced on Titan during the age of the solar system, and may exist today as submarine deposits beneath an extensive ocean of simple hydrocarbons.

  5. Selections from 2017: Discoveries in Titan's Atmosphere

    Science.gov (United States)

    Kohler, Susanna

    2017-12-01

    Editors note:In these last two weeks of 2017, well be looking at a few selections that we havent yet discussed on AAS Nova from among the most-downloaded paperspublished in AAS journals this year. The usual posting schedule will resume in January.Carbon Chain Anions and the Growth of Complex Organic Molecules in Titans IonospherePublished July2017Main takeaway:Graphic depicting some of the chemical reactions taking place in Titans atmosphere, leading to the generation of organic haze particles. [ESA]In a recently published study led by Ravi Desai (University College London), scientists used data from the Cassini mission to identify negatively charged molecules known as carbon chain anions in the atmosphere of Saturns largest moon, Titan.Why its interesting:Carbon chain anions are the building blocks ofmore complex molecules, and Titans thick nitrogen and methane atmosphere mightmimic the atmosphere of earlyEarth. This first unambiguous detection of carbon chain anions in a planet-like atmosphere might therefore teach us about the conditions and chemical reactions that eventually led to the development of life on Earth. And ifwe can use Titan to learn about how complex molecules grow from these anion chains, we may be able to identify auniversal pathway towards the ingredients for life.What weve learned so far:Cassini measured fewer and fewer lower-mass anions the deeper in Titans ionosphere that it looked and at the same time,an increase in the number of precursors to larger aerosol molecules further down. This tradeoff strongly suggests that the anions are indeed involved in building up the more complex molecules, seeding their eventual growth into the complex organic haze of Titans lower atmosphere.CitationR. T. Desai et al 2017 ApJL 844 L18. doi:10.3847/2041-8213/aa7851

  6. Scandium effect on mechanical properties of Al-6.5 % Mg alloy

    International Nuclear Information System (INIS)

    Drits, M.E.; Toropova, L.S.; Bykov, Yu.G.

    1982-01-01

    Quantitative evaluation of influence of small scandium additions (up to 0.5 wt%) on properties of Al-6.5% Mg binary alloy are carried out depending on test temperature in the range of -196 to 310 deg C. Alloys were tested on ''Instron'' machine at 1.3x10 - 3 s - 1 strain rate. Scandium additions are shown to increase plasticity at -196 deg C. Yield strength also increases with introduction of 0.2% Sc if deformation temperature does not exceed 250 deg C. The growth of ultimate strength is less significant. Elevated strength properties of alloys with scandium additions can be explained by a fine-grained structure

  7. Effect of scandium additions on microstructure and mechanical properties of Al-Zn-Mg alloy welds

    International Nuclear Information System (INIS)

    Dev, Selvi; Stuart, A. Archibald; Kumaar, R.C. Ravi Dev; Murty, B.S.; Rao, K. Prasad

    2007-01-01

    The microstructure and mechanical properties of fusion zones of medium strength Al-Zn-Mg alloy (RDE-40) welds obtained by using different fillers containing various amount of scandium was investigated. It was observed that addition of scandium led to very significant grain refinement in the fusion zone especially for scandium levels greater than the eutectic composition (0.55 wt%). The grain refinement led to the reduction in solidification cracking and improved the tensile properties of fusion zone compared to the ones obtained by the commercial AA5556 filler

  8. Raising the Titanic.

    Science.gov (United States)

    Baker, Romona

    1990-01-01

    Described is an activity in which groups of students investigate engineering principles by writing a feasibility study to raise the luxury liner, Titanic. The problem statement and directions, and suggestions for problem solutions are included. (CW)

  9. Clash of the Titans

    Science.gov (United States)

    Subramaniam, Karthigeyan

    2010-01-01

    WebQuests and the 5E learning cycle are titans of the science classroom. These popular inquiry-based strategies are most often used as separate entities, but the author has discovered that using a combined WebQuest and 5E learning cycle format taps into the inherent power and potential of both strategies. In the lesson, "Clash of the Titans,"…

  10. Titan's Ammonia Feature

    Science.gov (United States)

    Smythe, W.; Nelson, R.; Boryta, M.; Choukroun, M.

    2011-01-01

    NH3 has long been considered an important component in the formation and evolution of the outer planet satellites. NH3 is particularly important for Titan, since it may serve as the reservoir for atmospheric nitrogen. A brightening seen on Titan starting in 2004 may arise from a transient low-lying fog or surface coating of ammonia. The spectral shape suggests the ammonia is anhydrous, a molecule that hydrates quickly in the presence of water.

  11. The TITAN reversed-field-pinch fusion reactor study

    International Nuclear Information System (INIS)

    1990-01-01

    This report discusses the following topics: overview of titan-2 design; titan-2 fusion-power-core engineering; titan-2 divertor engineering; titan-2 tritium systems; titan-2 safety design and radioactive-waste disposal; and titan-2 maintenance procedures

  12. The TITAN reversed-field-pinch fusion reactor study

    Energy Technology Data Exchange (ETDEWEB)

    1990-01-01

    This report discusses the following topics: overview of titan-2 design; titan-2 fusion-power-core engineering; titan-2 divertor engineering; titan-2 tritium systems; titan-2 safety design and radioactive-waste disposal; and titan-2 maintenance procedures.

  13. Anion and cation diffusion in barium titanate and strontium titanate

    International Nuclear Information System (INIS)

    Kessel, Markus Franz

    2012-01-01

    Perovskite oxides show various interesting properties providing several technical applications. In many cases the defect chemistry is the key to understand and influence the material's properties. In this work the defect chemistry of barium titanate and strontium titanate is analysed by anion and cation diffusion experiments and subsequent time-of-flight secondary ion mass spectrometry (ToF-SIMS). The reoxidation equation for barium titanate used in multi-layer ceramic capacitors (MLCCs) is found out by a combination of different isotope exchange experiments and the analysis of the resulting tracer diffusion profiles. It is shown that the incorporation of oxygen from water vapour is faster by orders of magnitude than from molecular oxygen. Chemical analysis shows the samples contain various dopants leading to a complex defect chemistry. Dysprosium is the most important dopant, acting partially as a donor and partially as an acceptor in this effectively acceptor-doped material. TEM and EELS analysis show the inhomogeneous distribution of Dy in a core-shell microstructure. The oxygen partial pressure and temperature dependence of the oxygen tracer diffusion coefficients is analysed and explained by the complex defect chemistry of Dy-doped barium titanate. Additional fast diffusion profiles are attributed to fast diffusion along grain boundaries. In addition to the barium titanate ceramics from an important technical application, oxygen diffusion in cubic, nominally undoped BaTiO 3 single crystals has been studied by means of 18 O 2 / 16 O 2 isotope exchange annealing and subsequent determination of the isotope profiles in the solid by ToF-SIMS. It is shown that a correct description of the diffusion profiles requires the analysis of the diffusion through the surface space-charge into the material's bulk. Surface exchange coefficients, space-charge potentials and bulk diffusion coefficients are analysed as a function of oxygen partial pressure and temperature. The

  14. Safe prescribing: a titanic challenge.

    Science.gov (United States)

    Routledge, Philip A

    2012-10-01

    The challenge to achieve safe prescribing merits the adjective 'titanic'. The organisational and human errors leading to poor prescribing (e.g. underprescribing, overprescribing, misprescribing or medication errors) have parallels in the organisational and human errors that led to the loss of the Titanic 100 years ago this year. Prescribing can be adversely affected by communication failures, critical conditions, complacency, corner cutting, callowness and a lack of courage of conviction, all of which were also factors leading to the Titanic tragedy. These issues need to be addressed by a commitment to excellence, the final component of the 'Seven C's'. Optimal prescribing is dependent upon close communication and collaborative working between highly trained health professionals, whose role is to ensure maximum clinical effectiveness, whilst also protecting their patients from avoidable harm. Since humans are prone to error, and the environments in which they work are imperfect, it is not surprising that medication errors are common, occurring more often during the prescribing stage than during dispensing or administration. A commitment to excellence in prescribing includes a continued focus on lifelong learning (including interprofessional learning) in pharmacology and therapeutics. This should be accompanied by improvements in the clinical working environment of prescribers, and the encouragement of a strong safety culture (including reporting of adverse incidents as well as suspected adverse drug reactions whenever appropriate). Finally, members of the clinical team must be prepared to challenge each other, when necessary, to ensure that prescribing combines the highest likelihood of benefit with the lowest potential for harm. © 2012 The Author. British Journal of Clinical Pharmacology © 2012 The British Pharmacological Society.

  15. Complexonometric photometric titration of scandium in the presence of xylenol orange

    International Nuclear Information System (INIS)

    Kornev, V.I.

    1977-01-01

    Possibility has been studied of using xylenol orange (XO) for chelatometric determination of scandium by means of various chelates with the aid of photometric techniques. It has been established that the chelates applicable for the purpose are ethylenediamineteraacetic acid (EDTA), diethylenediaminetetraacetic acid (DEDTA), diethylenetriaminepentaacetic acid (DETPA), upon introducing of which into a solution containing a complex of scandium with XO (maximum light adsorption at 550 nm) the optical density gradually diminishes. Weakening of the light absorption is, evidently, associated with the destruction of the scandium complex with XO and formation of a colourless chelate acetate with one of the chelates. Chelatometric determination of scandium, using EDTA, DEDTA and DEPTA solutions with XO should be carried out in an acidic medium at pH=2.5-3.0. In this range of pH values interferences caused by the appearance of the Sc-XO complex in the solution are insignificant

  16. Knight shift in scandium and its alloys with hafnium and titanium

    International Nuclear Information System (INIS)

    Chachkhiani, Z.B.; Chechernikov, V.I.; Martynova, L.F.; Nidel'ko, V.I.; Chachkhiani, L.G.; Georgadze, G.S.

    1981-01-01

    Results of the investigation of NMR on 45 Sc nuclei and magnetic susceptibility of scandium and its solid solutions with titanium and hafnium are presented. It is shown that the existing hybridization of S and d zones in pure scandium and its alloys with titanium and hafnium affects the Knight shift reducing the value of the contact contribution. The temperature behaviour of the Knight shift from the temperature dependence and spin susceptibility of collectivized d electrons [ru

  17. Use of scandium ionic associates with salicylic- or 2-phenylquinoline-4-carboxylic acid and rhodamine C

    Energy Technology Data Exchange (ETDEWEB)

    Kononenko, L.I.; Bel' tyukova, S V; Drobyazko, V N; Poluehktov, N S [AN Ukrainskoj SSR, Kiev. Inst. Obshchej i Neorganicheskoj Khimii; AN Ukrainskoj SSR, Odessa. Inst. Obshchej i Neorganicheskoj Khimii)

    1975-09-01

    With salicylic or 2-phenylquinoline-4-carboxylic acid and rhodamine C scandium forms ion associations whose benzene solutions are capable of luminescence. Optimum conditions for the formation of complexes and the composition of the complex with the ratio of Sc:acid:rhodamine C = 1:2:1 are established. A possibility of luminescence determination of scandium in the presence of rare earths is shown.

  18. Analogs of N-cynnamoylphenylhydroxylamine as reagents for amperometric determination of scandium

    International Nuclear Information System (INIS)

    Shvedene, N.V.; Gallaj, Z.A.; Sheina, N.M.; Zujkova, N.V.

    1978-01-01

    To decrease the detection limit of scandium and increase selectivity of amperometric determination, oxidation of 2-furylacryloyl-N-p-chlorophenylhydroxylamine (FACPhHA) and 3-styrylacryloyl-N-phenylhydroxylamine (SAPhHA) on a graphite electrode has been studied by volt-amperometry. The possibility has been established of using the oxidation current of the reagent for plotting the titration curves. The solubility of scandium complexes with FACPhHA and SAPhHA under conditions of titration against the background with pH 6.0 has been determined and equals (2.1+-0.3)x10 -6 and (5.3+-0.3)x10 -7 , respectively. The methods have been developed of amperometric determination of scandium with the use of the considered reagents against backgrounds with pH 5.5-6.5. The use of SAPhHA has decreased the limit of scandium detection down to 0.1 mgk/ml. Besides, the amperometric method makes it possible to titrate in turbid and coloured media what is an advantage of this method. The developed method is used for determination of scandium in scandium silicide

  19. Effect of composition on the superplasticity of aluminium scandium alloys

    International Nuclear Information System (INIS)

    Bradley, E.L. III; Morris, J.W. Jr.

    1992-01-01

    Several aluminum alloys have been shown to exhibit superplasticty in the as-rolled condition. Previous work has shown that aluminum-scandium alloys also exhibit this behavior, but only with the addition of ternary alloying elements such as lithium and magnesium. These additions raised the strain-rate sensitivity of these alloys to 0.4-0.5 for selected strain rates at temperatures above 400 degrees C. A systematic study was undertaken of five Al-Sc alloys with varying lithium and magnesium concentrations in order to fully characterize the high temperature deformation mechanism. Specimens were deformed at a constant strain rate to predetermined true strains for textural and microstructural characterization. In this paper work is presented that will elucidate the effect of these different ternary additives on the superplastic deformation mechanism in these alloys

  20. Application of scandium oxide in an electron emission material

    International Nuclear Information System (INIS)

    Suqiu, Y.; Zhizheng, Z.; Yongde, W.

    1985-01-01

    Modern microwave devices impose a number of harsh requirements on the cathodes. For instance, they require cathodes having low working temperature, high emissive current density, slow evaporation rate of the emissive-active material, long lifetime, quick heating and so on. The commercial B-cathode is no longer able to meet these requirements completely. A scandate cathode may be a promising one for use in these devices. Adding rare-earth elements in the electron emission material has been reported in many papers. Based on a B-cathode we add a little amount of scandium oxide (about 3%) into emission material to manufacture a scandate cathode. The emission property of such a cathode has been improved greatly. If the composition is controlled correctly, the emission level of such a cathode may be five times more as high as the B-cathode

  1. Titan Polar Landscape Evolution

    Science.gov (United States)

    Moore, Jeffrey M.

    2016-01-01

    With the ongoing Cassini-era observations and studies of Titan it is clear that the intensity and distribution of surface processes (particularly fluvial erosion by methane and Aeolian transport) has changed through time. Currently however, alternate hypotheses substantially differ among specific scenarios with respect to the effects of atmospheric evolution, seasonal changes, and endogenic processes. We have studied the evolution of Titan's polar region through a combination of analysis of imaging, elevation data, and geomorphic mapping, spatially explicit simulations of landform evolution, and quantitative comparison of the simulated landscapes with corresponding Titan morphology. We have quantitatively evaluated alternate scenarios for the landform evolution of Titan's polar terrain. The investigations have been guided by recent geomorphic mapping and topographic characterization of the polar regions that are used to frame hypotheses of process interactions, which have been evaluated using simulation modeling. Topographic information about Titan's polar region is be based on SAR-Topography and altimetry archived on PDS, SAR-based stereo radar-grammetry, radar-sounding lake depth measurements, and superposition relationships between geomorphologic map units, which we will use to create a generalized topographic map.

  2. Titan Orbiter Aerorover Mission

    Science.gov (United States)

    Sittler Jr., E. C.; Acuna, M.; Burchell, M. J.; Coates, A.; Farrell, W.; Flasar, M.; Goldstein, B. E.; Gorevan, S.; Hartle, R. E.; Johnson, W. T. K.

    2001-01-01

    We propose a combined Titan orbiter and Titan Aerorover mission with an emphasis on both in situ and remote sensing measurements of Titan's surface, atmosphere, ionosphere, and magnetospheric interaction. The biological aspect of the Titan environment will be emphasized by the mission (i.e., search for organic materials which may include simple organics to 'amono' analogues of amino acids and possibly more complex, lightening detection and infrared, ultraviolet, and charged particle interactions with Titan's surface and atmosphere). An international mission is assumed to control costs. NASA will provide the orbiter, launch vehicle, DSN coverage and operations, while international partners will provide the Aerorover and up to 30% of the cost for the scientific instruments through collaborative efforts. To further reduce costs we propose a single PI for orbiter science instruments and a single PI for Aerorover science instruments. This approach will provide single command/data and power interface between spacecraft and orbiter instruments that will have redundant central DPU and power converter for their instruments. A similar approach could be used for the Aerorover. The mission profile will be constructed to minimize conflicts between Aerorover science, orbiter radar science, orbiter radio science, orbiter imaging science, and orbiter fields and particles (FP) science. Additional information is contained in the original extended abstract.

  3. F-center mechanism of long-term relaxation in lead zirconate-titanate-based piezoelectric ceramics. 1. After-heating relaxation

    Directory of Open Access Journals (Sweden)

    V. M. Ishchuk

    2015-12-01

    The oxygen vacancies-based model for description of the long-time relaxation processes is suggested. The model takes into account oxygen vacancies on the sample’s surface ends, their conversion into F+- and F0-centers under external effects (due to the liberation of the pyroelectric charge and subsequent relaxation of these centers into the simple oxygen vacancies after the actions termination. The initial sample’s state is electroneutrality one. F-center formation leads to the violation of the original sample’s electroneutrality, and generates DC electric field into the sample. Relaxation of F-centers is accompanied by decreasing of electric field, induced by them, and dielectric constant relaxation as consequent effect.

  4. The tides of Titan.

    Science.gov (United States)

    Iess, Luciano; Jacobson, Robert A; Ducci, Marco; Stevenson, David J; Lunine, Jonathan I; Armstrong, John W; Asmar, Sami W; Racioppa, Paolo; Rappaport, Nicole J; Tortora, Paolo

    2012-07-27

    We have detected in Cassini spacecraft data the signature of the periodic tidal stresses within Titan, driven by the eccentricity (e = 0.028) of its 16-day orbit around Saturn. Precise measurements of the acceleration of Cassini during six close flybys between 2006 and 2011 have revealed that Titan responds to the variable tidal field exerted by Saturn with periodic changes of its quadrupole gravity, at about 4% of the static value. Two independent determinations of the corresponding degree-2 Love number yield k(2) = 0.589 ± 0.150 and k(2) = 0.637 ± 0.224 (2σ). Such a large response to the tidal field requires that Titan's interior be deformable over time scales of the orbital period, in a way that is consistent with a global ocean at depth.

  5. Diurnal variations of Titan

    Science.gov (United States)

    Cui, J.; Galand, M.; Yelle, R. V.; Vuitton, V.; Wahlund, J.-E.; Lavvas, P. P.; Mueller-Wodarg, I. C. F.; Kasprzak, W. T.; Waite, J. H.

    2009-04-01

    We present our analysis of the diurnal variations of Titan's ionosphere (between 1,000 and 1,400 km) based on a sample of Ion Neutral Mass Spectrometer (INMS) measurements in the Open Source Ion (OSI) mode obtained from 8 close encounters of the Cassini spacecraft with Titan. Though there is an overall ion depletion well beyond the terminator, the ion content on Titan's nightside is still appreciable, with a density plateau of ~700 cm-3 below ~1,300 km. Such a plateau is associated with the combination of distinct diurnal variations of light and heavy ions. Light ions (e.g. CH5+, HCNH+, C2H5+) show strong diurnal variation, with clear bite-outs in their nightside distributions. In contrast, heavy ions (e.g. c-C3H3+, C2H3CNH+, C6H7+) present modest diurnal variation, with significant densities observed on the nightside. We propose that the distinctions between light and heavy ions are associated with their different chemical loss pathways, with the former primarily through "fast" ion-neutral chemistry and the latter through "slow" electron dissociative recombination. The INMS data suggest day-to-night transport as an important source of ions on Titan's nightside, to be distinguished from the conventional scenario of auroral ionization by magnetospheric particles as the only ionizing source on the nightside. This is supported by the strong correlation between the observed night-to-day ion density ratios and the associated ion lifetimes. We construct a time-dependent ion chemistry model to investigate the effects of day-to-night transport on the ionospheric structures of Titan. The predicted diurnal variation has similar general characteristics to those observed, with some apparent discrepancies which could be reconciled by imposing fast horizontal thermal winds in Titan's upper atmosphere.

  6. Concentration and Separation of Scandium from Ni Laterite Ore Processing Streams

    Directory of Open Access Journals (Sweden)

    Şerif Kaya

    2017-12-01

    Full Text Available The presence of a considerable amount of scandium in lateritic nickel-cobalt ores necessitates the investigation of possible processing alternatives to recover scandium as a byproduct during nickel and cobalt production. Therefore, in this study, rather than interfering with the main nickel-cobalt production circuit, the precipitation-separation behavior of scandium during a pH-controlled precipitation process from a synthetically prepared solution was investigated to adopt the Sc recovery circuit into an already existing hydrometallurgical nickel-cobalt hydroxide processing plant. The composition of the synthetic solution was determined according to the hydrometallurgical nickel laterite ore processing streams obtained from a HPAL (high-pressure sulphuric acid leaching process. In order to selectively precipitate and concentrate scandium with minimum nickel and cobalt co-precipitation, the pH of the solution was adjusted by CaCO3, MgO, Na2CO3, and NaOH. It was found that precipitation with MgO or Na2CO3 is more advantageous to obtain a precipitate containing higher amounts of scandium with minimum mass when compared to the CaCO3 route, which makes further processing more viable. As a result of this study, it is proposed that by a simple pH-controlled precipitation process, scandium can be separated from the nickel and cobalt containing process solutions as a byproduct without affecting the conventional nickel-cobalt hydroxide production. By further processing this scandium-enriched residue by means of leaching, SX (solvent extraction, and precipitation, an intermediate (NH42NaScF6 product can be obtained.

  7. Analysis of separation quality of scandium-46 and titanium using silica gel column

    International Nuclear Information System (INIS)

    Muhamad Basit Febrian; Yanuar Setiadi; Duyeh Setiawan; Titin Sri Mulyati; Nana Suherman

    2015-01-01

    In this study, quality test of scandium and titanium mixture separation system using a silica gel column has been conducted. This system will be used in the separation of medical radioisotopes of 47 Sc from TiO 2 enriched targets. 20 mg of TiO 2 and 5 mg of Sc 2 O 3 dissolved using 0.5 mL of 50% HF solvent with gentle heating at 60°C - 80°C for 1 hour then 4.5 mL H 2 O was added. Sc and Ti mixture is separated by passing it through a column of silica gel. In the determination of scandium released from silica gel, Sc-46 radiotracer was used. Only 51.60 ± 4.5% of 5 mg of scandium could be retained in the silica gel column. From 51.60% of absorbed scandium in the column, 98.29 ± 3.4% were eluted with 5 mL of H 2 O eluent. During elution of scandium from silica gel column, 2.81 grams of 20 mg of titanium came apart as breakthrough. In determination of recovery of titanium from silica gel, 51.76 ± 5.5% of the 20 mg Ti can be recovered from silica gel column using 5M HCl eluent, whereas remaining Ti were eluted using 40 ml of HCl 5M. Based on those result, it can be concluded that there are still titanium portion in scandium after the separation using a silica gel column. Further purification step using fresh silica gel column, can separate escaped titanium from scandium. (author)

  8. Titan's icy scar

    Science.gov (United States)

    Griffith, C. A.; Penteado, P. F.; Turner, J. D.; Neish, C. D.; Mitri, G.; Montiel, M. J.; Schoenfeld, A.; Lopes, R. M. C.

    2017-09-01

    We conduct a Principal Components Analysis (PCA) of Cassini/VIMS [1] infrared spectral windows to identify and quantify weak surface features, with no assumptions on the haze and surface characteris- tics. This study maps the organic sediments, supplied by past atmospheres, as well as ice-rich regions that constitute Titan's bedrock.

  9. Effect of Aqueous Media on the Recovery of Scandium by Selective Precipitation

    Directory of Open Access Journals (Sweden)

    Bengi Yagmurlu

    2018-05-01

    Full Text Available This research presents a novel precipitation method for scandium (Sc concentrate refining from bauxite residue leachates and the effect of aqueous media on this triple-stage successive precipitation process. The precipitation pattern and the precipitation behavior of the constituent elements was investigated using different precipitation agents in three major mineral acid media, namely, H2SO4, HNO3, and HCl in a comparative manner. Experimental investigations showed behavioral similarities between HNO3 and HCl media, while H2SO4 media was different from them because of the nature of the formed complexes. NH4OH was found to be the best precipitation agent in every leaching media to remove Fe(III with low Sc co-precipitation. To limit Sc loss from the system, Fe(III removal was divided into two steps, leading to more than 90% of Fe(III removal at the end of the process. Phosphate concentrates were produced in the final step of the precipitation process with dibasic phosphates which have a strong affinity towards Sc. Concentrates containing more than 50% of ScPO4 were produced in each case from the solutions after Fe(III removal, as described. A flow diagram of the selective precipitation process is proposed for these three mineral acid media with their characteristic parameters.

  10. Comparative study of A-site order in the lead-free bismuth titanates M1/2Bi1/2TiO3 (M=Li, Na, K, Rb, Cs, Ag, Tl) from first-principles

    International Nuclear Information System (INIS)

    Gröting, Melanie; Albe, Karsten

    2014-01-01

    We investigate the possibility of enhancing chemical order in the relaxor ferroelectric Na 1/2 Bi 1/2 TiO 3 upon substitution of Na + by other monovalent cations M + using total energy calculations based on density functional theory. All chemically available monovalent cations M + , which are Li, Na, Ag, K, Tl, Rb and Cs, are considered and an analysis of the structurally relaxed structures in terms of symmetry-adapted distortion modes is given in order to quantify the chemically induced structural distortions. We demonstrate that the replacement of Na + by other monovalent cations can hardly alter the tendency of chemical order with respect to Na 1/2 Bi 1/2 TiO 3 . Only Tl 1/2 Bi 1/2 TiO 3 and Ag 1/2 Bi 1/2 TiO 3 show enhanced tendency for chemical ordering. Both heavy metals behave similar to the light alkali metals in terms of structural relaxations and relative stabilities of the ordered configurations. Although a comparison of the Goldschmidt factors of components (M TiO 3 ) − reveals for Tl a value above the upper stability limit for perovskites, the additional lone-pair effect of Tl + stabilizes the ordered structure. - Graphical abstract: Amplitudes of chemically induced distortion modes in different ordered perovskites M 1/2 Bi 1/2 TiO 3 and visualisation of atomic displacements associated with distortion mode X + 1 in the 001-ordered compounds Li 1/2 Bi 1/2 TiO 3 and Cs 1/2 Bi 1/2 TiO 3 . Due to a substantial size mismatch between bismuth (green) and caesium (dark blue), incorporation of the latter leads to enhanced displacements of oxygen atoms (red) and suppresses displacements of titanium (silver) as compared to lithium (light blue) or other smaller monovalent cations. - Highlights: • Lead-free A-site mixed bismuth titanates M 1/2 Bi 1/2 TiO 3 are studied by first-principles calculations. • Investigation of chemical ordering tendency for M=Li, Na, K, Rb, Cs, Ag, and Tl. • Group theoretical analysis of different ordered structures. • Ag and Tl

  11. Scandium doping brings speed improvement in Sb2Te alloy for phase change random access memory application.

    Science.gov (United States)

    Chen, Xin; Zheng, Yonghui; Zhu, Min; Ren, Kun; Wang, Yong; Li, Tao; Liu, Guangyu; Guo, Tianqi; Wu, Lei; Liu, Xianqiang; Cheng, Yan; Song, Zhitang

    2018-05-01

    Phase change random access memory (PCRAM) has gained much attention as a candidate for nonvolatile memory application. To develop PCRAM materials with better properties, especially to draw closer to dynamic random access memory (DRAM), the key challenge is to research new high-speed phase change materials. Here, Scandium (Sc) has been found it is helpful to get high-speed and good stability after doping in Sb 2 Te alloy. Sc 0.1 Sb 2 Te based PCRAM cell can achieve reversible switching by applying even 6 ns voltage pulse experimentally. And, Sc doping not only promotes amorphous stability but also improves the endurance ability comparing with pure Sb 2 Te alloy. Moreover, according to DFT calculations, strong Sc-Te bonds lead to the rigidity of Sc centered octahedrons, which may act as crystallization precursors in recrystallization process to boost the set speed.

  12. Effects of iron on intermetallic compound formation in scandium modified Al–Si–Mg Alloys

    Energy Technology Data Exchange (ETDEWEB)

    Patakham, Ussadawut [National Metal and Materials Technology Center, National Science and Technology Development Agency, 114 Thailand Science Park, Klong Nueng, Klong Luang, Pathumthani 12120 (Thailand); Limmaneevichitr, Chaowalit, E-mail: chaowalit.lim@mail.kmutt.ac.th [Production Engineering Department, Faculty of Engineering, King Mongkut’s University of Technology Thonburi, 126 Pracha-Utid Rd., Bangmod, Tungkhru, Bangkok 10140 (Thailand)

    2014-12-15

    Highlights: • Iron reduces the modification effects of scandium in Al–Si–Mg alloys. • Morphologies of Sc-rich intermetallic phases vary with Fe and Sc contents and the cooling rates. • Sc neutralizes effects of Fe by changing Fe-rich intermetallic phases from platelets to more cubic. - Abstract: In general, iron has a strong tendency to dissolve in molten aluminum. Iron has very low solid solubility in aluminum–silicon casting alloys, so it will form intermetallic compounds that cause detrimental effects on mechanical properties. In this work, the effects of iron on intermetallic compound formations in scandium modified Al–Si–Mg alloys were studied. There were two levels of iron addition (0.2 and 0.4 wt.%) and two levels of scandium addition (0.2 and 0.4 wt.%). We found that the effects of scandium modification decreased with increasing iron addition. The morphologies of the complex intermetallic compounds were characterized by scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS) and electron backscatter diffraction (EBSD) techniques. It was found that scandium changes the morphology of Fe-rich intermetallic compounds from β-phase (plate-like) to α-phase, which reduces the harmful effects of β-phase.

  13. Thermodynamic and kinetic study of scandium(III) complexes of DTPA and DOTA: a step toward scandium radiopharmaceuticals.

    Science.gov (United States)

    Pniok, Miroslav; Kubíček, Vojtěch; Havlíčková, Jana; Kotek, Jan; Sabatie-Gogová, Andrea; Plutnar, Jan; Huclier-Markai, Sandrine; Hermann, Petr

    2014-06-23

    Diethylenetriamine-N,N,N',N'',N''-pentaacetic acid (DTPA) and 1,4,7,10-tetraazacyclododecane-1,4,7,10-tetraacetic acid (DOTA) scandium(III) complexes were investigated in the solution and solid state. Three (45)Sc NMR spectroscopic references suitable for aqueous solutions were suggested: 0.1 M Sc(ClO4)3 in 1 M aq. HClO4 (δSc =0.0 ppm), 0.1 M ScCl3 in 1 M aq. HCl (δSc =1.75 ppm) and 0.01 M [Sc(ox)4](5-) (ox(2-) = oxalato) in 1 M aq. K2C2O4 (δSc =8.31 ppm). In solution, [Sc(dtpa)](2-) complex (δSc = 83 ppm, Δν = 770 Hz) has a rather symmetric ligand field unlike highly unsymmetrical donor atom arrangement in [Sc(dota)](-) anion (δSc = 100 ppm, Δν = 4300 Hz). The solid-state structure of K8[Sc2(ox)7]⋅13 H2O contains two [Sc(ox)3](3-) units bridged by twice "side-on" coordinated oxalate anion with Sc(3+) ion in a dodecahedral O8 arrangement. Structures of [Sc(dtpa)](2-) and [Sc(dota)](-) in [(Hguanidine)]2[Sc(dtpa)]⋅3 H2O and K[Sc(dota)][H6 dota]Cl2⋅4 H2O, respectively, are analogous to those of trivalent lanthanide complexes with the same ligands. The [Sc(dota)](-) unit exhibits twisted square-antiprismatic arrangement without an axial ligand (TSA' isomer) and [Sc(dota)](-) and (H6 dota)(2+) units are bridged by a K(+) cation. A surprisingly high value of the last DOTA dissociation constant (pKa =12.9) was determined by potentiometry and confirmed by using NMR spectroscopy. Stability constants of scandium(III) complexes (log KScL 27.43 and 30.79 for DTPA and DOTA, respectively) were determined from potentiometric and (45)Sc NMR spectroscopic data. Both complexes are fully formed even below pH 2. Complexation of DOTA with the Sc(3+) ion is much faster than with trivalent lanthanides. Proton-assisted decomplexation of the [Sc(dota)](-) complex (τ1/2 =45 h; 1 M aq. HCl, 25 °C) is much slower than that for [Ln(dota)](-) complexes. Therefore, DOTA and its derivatives seem to be very suitable ligands for scandium

  14. Titan: a laboratory for prebiological organic chemistry

    Science.gov (United States)

    Sagan, C.; Thompson, W. R.; Khare, B. N.

    1992-01-01

    When we examine the atmospheres of the Jovian planets (Jupiter, Saturn, Uranus, and Neptune), the satellites in the outer solar system, comets, and even--through microwave and infrared spectroscopy--the cold dilute gas and grains between the stars, we find a rich organic chemistry, presumably abiological, not only in most of the solar system but throughout the Milky Way galaxy. In part because the composition and surface pressure of the Earth's atmosphere 4 x 10(9) years ago are unknown, laboratory experiments on prebiological organic chemistry are at best suggestive; but we can test our understanding by looking more closely at the observed extraterrestrial organic chemistry. The present Account is restricted to atmospheric organic chemistry, primarily on the large moon of Saturn. Titan is a test of our understanding of the organic chemistry of planetary atmospheres. Its atmospheric bulk composition (N2/CH4) is intermediate between the highly reducing (H2/He/CH4/NH3/H2O) atmospheres of the Jovian planets and the more oxidized (N2/CO2/H2O) atmospheres of the terrestrial planets Mars and Venus. It has long been recognized that Titan's organic chemistry may have some relevance to the events that led to the origin of life on Earth. But with Titan surface temperatures approximately equal to 94 K and pressures approximately equal to 1.6 bar, the oceans of the early Earth have no ready analogue on Titan. Nevertheless, tectonic events in the water ice-rich interior or impact melting and slow re-freezing may lead to an episodic availability of liquid water. Indeed, the latter process is the equivalent of a approximately 10(3)-year-duration shallow aqueous sea over the entire surface of Titan.

  15. Double tungstates of metals of scandium and ammonium subgroups

    Energy Technology Data Exchange (ETDEWEB)

    Maksin, V I [AN Ukrainskoj SSR, Kiev. Inst. Kolloidnoj Khimii i Khimii Vody

    1980-06-01

    The methods of pH-potentiometry, conductometry, determination of residual concentrations of liquid phases and precipitations, selected by chemical analysis have been used for investigation R(NO/sub 3/)/sub 3/-(NH/sub 4/)/sub 2/WO/sub 2/-H/sub 2/O systems, (where R=Sc, Y, La). The formation of double tungstates NH/sub 4/R(WO/sub 4/)/sub 2/xnH/sub 2/O is established. The NH/sub 4/Sc(WO/sub 4/)/sub 2/x4.5H/sub 2/O, NH/sub 4/Yx(WO/sub 4/)/sub 2/x3H/sub 2/O, NH/sub 4/La(WO/sub 4/)/sub 2/x1.5H/sub 2/O compounds are synthesized in individual form. Precipitation conditions (pH, concentration ratio) and composition of the solid phase are determined. The behaviour of synthesized slats at thermolysis up to 880 deg C is studied. Physicochemical properties (color, solubility of the simple and double tungstates of scandium, yttrium and lanthanum with ammonium) is studied. IR spectra and X-ray diffraction analysis give idea about double salts structural transformations.

  16. Hydrogen storage in thin film magnesium-scandium alloys

    International Nuclear Information System (INIS)

    Niessen, R.A. H.; Notten, P.H. L.

    2005-01-01

    Thorough electrochemical materials research has been performed on thin films of novel magnesium-scandium hydrogen storage alloys. It was found that palladium-capped thin films of Mg x Sc (1-x) with different compositions (ranging from x=0.50 -0.90) show an increase in hydrogen storage capacity of more than 5-20% as compared to their bulk equivalents using even higher discharge rates. The maximum reversible hydrogen storage capacity at the optimal composition (Mg 80 Sc 20 ) amounts to 1795-bar mAh/g corresponding to a hydrogen content of 2.05 H/M or 6.7-bar wt.%, which is close to five times that of the commonly used hydride-forming materials in commercial NiMH batteries. Galvanostatic intermittent titration technique (GITT) measurements show that the equilibrium pressure during discharge is lower than that of bulk powders by one order of magnitude (10 -7 -bar mbar versus 10 -6 -bar mbar, respectively)

  17. The spectrum of four times ionized scandium, Sc V

    International Nuclear Information System (INIS)

    Smitt, R.; Ekberg, J.O.

    1985-01-01

    The spectrum of four times ionized scandium emitted from a sliding spark discharge has been observed using a 3 m normal incidence spectrograph and a 5 m grazing incidence spectrograph. About 450 lines in the wavelength region 160 A to 220 A have been identified as combinations between 46 odd levels belonging to the 3s 2 3p 5 , 3s 2 3p 4 4p and 3s3p 5 3d configurations and 72 even levels of the 3s3p 6 , 3s 2 3p 4 3d, 4d, 4s and 5s configurations. Of the previous identifications we have confirmed 18 levels. The level structure of the observed configurations has been theoretically interpreted by including configuration interaction effects. The inclusion of 3s 2 3p 3 3d 2 in the calculations of the odd parity configurations is found to be important. Almost all levels of 3s3p 5 3d show a considerable mixing with levels of 3s 2 3p 3 3d 2 , in some cases by as much as 50%. The energy parameters determined from least-squares fits to the observed level values are compared with Hartree-Fock calculations. The ionization energy is estimated to be 739 500 +- 1000 cm -1 . (91.65 +- 0,12 eV). (orig.)

  18. Aluminum-Scandium: A Material for Semiconductor Packaging

    Science.gov (United States)

    Geissler, Ute; Thomas, Sven; Schneider-Ramelow, Martin; Mukhopadhyay, Biswajit; Lang, Klaus-Dieter

    2016-10-01

    A well-known aluminum-scandium (Al-Sc) alloy, already used in lightweight sports equipment, is about to be established for use in electronic packaging. One application for Al-Sc alloy is manufacture of bonding wires. The special feature of the alloy is its ability to harden by precipitation. The new bonding wires with electrical conductivity similar to pure Al wires can be processed on common wire bonders for aluminum wedge/wedge (w/w) bonding. The wires exhibit very fine-grained microstructure. Small Al3Sc particles are the main reason for its high strength and prevent recrystallization and grain growth at higher temperatures (>150°C). After the wire-bonding process, the interface is well closed. Reliability investigations by active power cycling demonstrated considerably improved lifetime compared with pure Al heavy wires. Furthermore, the Al-Sc alloy was sputter-deposited onto silicon wafer to test it as chip metallization in copper (Cu) ball/wedge bonding technology. After deposition, the layers exhibited fine-grained columnar structure and small coherent Al3Sc particles with dimensions of a few nanometers. These particles inhibit softening processes such as Al splashing in fine wire bonding processes and increase the thickness of remnant Al under the copper balls to 85% of the initial thickness.

  19. Safe prescribing: a titanic challenge

    Science.gov (United States)

    Routledge, Philip A

    2012-01-01

    The challenge to achieve safe prescribing merits the adjective ‘titanic’. The organisational and human errors leading to poor prescribing (e.g. underprescribing, overprescribing, misprescribing or medication errors) have parallels in the organisational and human errors that led to the loss of the Titanic 100 years ago this year. Prescribing can be adversely affected by communication failures, critical conditions, complacency, corner cutting, callowness and a lack of courage of conviction, all of which were also factors leading to the Titanic tragedy. These issues need to be addressed by a commitment to excellence, the final component of the ‘Seven C's’. Optimal prescribing is dependent upon close communication and collaborative working between highly trained health professionals, whose role is to ensure maximum clinical effectiveness, whilst also protecting their patients from avoidable harm. Since humans are prone to error, and the environments in which they work are imperfect, it is not surprising that medication errors are common, occurring more often during the prescribing stage than during dispensing or administration. A commitment to excellence in prescribing includes a continued focus on lifelong learning (including interprofessional learning) in pharmacology and therapeutics. This should be accompanied by improvements in the clinical working environment of prescribers, and the encouragement of a strong safety culture (including reporting of adverse incidents as well as suspected adverse drug reactions whenever appropriate). Finally, members of the clinical team must be prepared to challenge each other, when necessary, to ensure that prescribing combines the highest likelihood of benefit with the lowest potential for harm. PMID:22738396

  20. Thermomechanical treatment of welded joints of aluminum-lithium alloys modified by scandium

    Science.gov (United States)

    Malikov, A. G.

    2017-12-01

    At present, the aeronautical equipment manufacture involves up-to-date high-strength aluminum alloys of decreased density resulting from the lithium admixture. Various technologies of fusible welding of these alloys are being developed. The paper presents experimental investigations of the optimization of the laser welding of aluminum alloys with the scandium-modified welded joint after thermomechanical treatment. The effect of scandium on the micro- and macrostructure is studied along with strength characteristics of the welded joint. It is found that thermomechanical treatment allows us to obtain the strength of the welded joint 0.89 for the Al-Mg-Li system and 0.99 for the Al-Cu-Li system with the welded joint modified by scandium in comparison with the base alloy after treatment.

  1. The enthalpy of solid scandium in the temperature range 406 - 1812 K

    International Nuclear Information System (INIS)

    Lyapunov, K.M.; Baginskij, A.V.; Stankus, S.V.

    2001-01-01

    Enthalpy of pure scandium was measured on massive calorimeter in the range from 406 to 1812 K by mixing method. The enthalpy of face centered close cubic lattice - body centered cubic lattice transformation is equal to ΔH t 4068 J/mol. Obtained value within the limits of error is compatible with the results given earlier (4009 J/mol). The dependence of the middle specific heat of scandium C p (T) on the temperature was shown in correlation with the results of other works. The results of the conducted experiments reinforce the conclusion made earlier about an absence (or a little) in the decomposition of an anharmonic component of the oscillation specific heat of scandium C p a (T) members proportional to the first or the second degrees of temperature [ru

  2. Pressure-induced structural change from hexagonal to fcc metal lattice in scandium trihydride

    International Nuclear Information System (INIS)

    Ohmura, A.; Machida, A.; Watanuki, T.; Aoki, K.; Nakano, S.; Takemura, K.

    2007-01-01

    We synthesized scandium hydrides by hydrogenation of a scandium foil with hydrogen fluid under high pressure at ambient temperature. Scandium dihydride (ScH 2 ) and trihydride (ScH 3 ) were prepared near 4 and 5 GPa, respectively. The hydrogenation process and pressure-induced structural changes in ScH 3 were investigated by synchrotron radiation X-ray diffraction measurements up to 54.7 GPa. A structural transition from hexagonal to the fcc lattice began at 30 GPa and was completed at 46 GPa via an intermediate state similar to those reported for other hexagonal trihydrides. The intermediate state was not interpreted in terms of a coexisting state for the low-pressure hexagonal and the high-pressure fcc structures. The onset transition pressure of ScH 3 supported the previously proposed relation that the hexagonal-fcc transition pressure is inversely proportional to the ionic radius of the trihydride

  3. Titanic exploration with GIS

    Science.gov (United States)

    Kerski, J.J.

    2004-01-01

    To help teachers and students investigate one of the world's most famous historical events using the geographic perspective and GIS tools and methods, the U.S. Geological Survey (USGS) created a set of educational lessons based on the RMS Titanic's April 1912 sailing. With these lessons, student researchers can learn about latitude and longitude, map projections, ocean currents, databases, maps, and images through the analysis of the route, warnings, sinking, rescue, and eventual discovery of the submerged ocean liner in 1985. They can also consider the human and physical aspects of the maiden voyage in the North Atlantic Ocean at a variety of scales, from global to regional to local. Likewise, their investigations can reveal how the sinking of the Titanic affected future shipping routes.

  4. Ethane ocean on Titan

    Science.gov (United States)

    Lunine, J. I.; Stevenson, D. J.; Yung, Y.L.

    1983-01-01

    Voyager I radio occultation data is employed to develop a qualitative model of an ethane ocean on Titan. It is suggested that the ocean contains 25 percent CH4 and that the ocean is in dynamic equilibrium with an N2 atmosphere. Previous models of a CH4 ocean are discounted due to photolysis rates of CH4 gas. Tidal damping of Titan's orbital eccentricity is taken as evidence for an ocean layer approximately 1 km deep, with the ocean floor being covered with a solid C2H2 layer 100 to 200 m thick. The photolytic process disrupting the CH4, if the estimates of the oceanic content of CH4 are correct, could continue for at least one billion years. Verification of the model is dependent on detecting CH4 clouds in the lower atmosphere, finding C2H6 saturation in the lower troposphere, or obtaining evidence of a global ocean.

  5. Organic chemistry on Titan

    Science.gov (United States)

    Chang, S.; Scattergood, T.; Aronowitz, S.; Flores, J.

    1979-01-01

    Features taken from various models of Titan's atmosphere are combined in a working composite model that provides environmental constraints within which different pathways for organic chemical synthesis are determined. Experimental results and theoretical modeling suggest that the organic chemistry of the satellite is dominated by two processes: photochemistry and energetic particle bombardment. Photochemical reactions of CH4 in the upper atmosphere can account for the presence of C2 hydrocarbons. Reactions initiated at various levels of the atmosphere by cosmic rays, Saturn 'wind', and solar wind particle bombardment of a CH4-N2 atmospheric mixture can account for the UV-visible absorbing stratospheric haze, the reddish appearance of the satellite, and some of the C2 hydrocarbons. In the lower atmosphere photochemical processes will be important if surface temperatures are sufficiently high for gaseous NH3 to exist. It is concluded that the surface of Titan may contain ancient or recent organic matter (or both) produced in the atmosphere.

  6. Landscape Evolution of Titan

    Science.gov (United States)

    Moore, Jeffrey

    2012-01-01

    Titan may have acquired its massive atmosphere relatively recently in solar system history. The warming sun may have been key to generating Titan's atmosphere over time, starting from a thin atmosphere with condensed surface volatiles like Triton, with increased luminosity releasing methane, and then large amounts of nitrogen (perhaps suddenly), into the atmosphere. This thick atmosphere, initially with much more methane than at present, resulted in global fluvial erosion that has over time retreated towards the poles with the removal of methane from the atmosphere. Basement rock, as manifested by bright, rough, ridges, scarps, crenulated blocks, or aligned massifs, mostly appears within 30 degrees of the equator. This landscape was intensely eroded by fluvial processes as evidenced by numerous valley systems, fan-like depositional features and regularly-spaced ridges (crenulated terrain). Much of this bedrock landscape, however, is mantled by dunes, suggesting that fluvial erosion no longer dominates in equatorial regions. High midlatitude regions on Titan exhibit dissected sedimentary plains at a number of localities, suggesting deposition (perhaps by sediment eroded from equatorial regions) followed by erosion. The polar regions are mainly dominated by deposits of fluvial and lacustrine sediment. Fluvial processes are active in polar areas as evidenced by alkane lakes and occasional cloud cover.

  7. Fabrication of crystal-oriented barium-bismuth titanate ceramics in high magnetic field and subsequent reaction sintering

    International Nuclear Information System (INIS)

    Tanaka, Satoshi; Tomita, Yusuke; Furushima, Ryoichi; Uematsu, Keizo; Shimizu, Hiroyuki; Doshida, Yutaka

    2009-01-01

    High magnetic field was applied to fabricate novel lead-free piezoelectric ceramics with a textured structure. A compact of crystallographically oriented grains was prepared by dry forming in a high magnetic field from a mixed slurry of bismuth titanate and barium titanate powders. Bismuth titanate particles with a size of about 1 μ m were used as the host material. In the forming process, the slurry was poured into a mold and set in a magnetic field of 10 T until completely dried. Bismuth titanate particles were highly oriented in the slurry under the magnetic field. The dried powder compact consisted of highly oriented bismuth titanate particles and randomly oriented barium titanate particles. Barium bismuth titanate ceramics with a- and b-axis orientations were successfully produced from the dried compact by sintering at temperatures above 1100 deg. C.

  8. Titan's methane clock

    Science.gov (United States)

    Nixon, C. A.; Jennings, D. E.; Romani, P. N.; Teanby, N. A.; Irwin, P. G. J.; Flasar, F. M.

    2010-04-01

    Measurements of the 12C/13C and D/H isotopic ratios in Titan's methane show intriguing differences from the values recorded in the giant planets. This implies that either (1) the atmosphere was differently endowed with material at the time of formation, or (2) evolutionary processes are at work in the moon's atmosphere - or some combination of the two. The Huygens Gas Chromatograph Mass Spectrometer Instrument (GCMS) found 12CH4/13CH4 = 82 +/- 1 (Niemann et al. 2005), some 7% lower than the giant planets' value of 88 +/- 7 (Sada et al. 1996), which closely matches the terrestrial inorganic standard of 89. The Cassini Composite Infrared Spectrometer (CIRS) has previously reported 12CH4/13CH4 of 77 +/-3 based on nadir sounding, which we now revise upwards to 80 +/- 4 based on more accurate limb sounding. The CIRS and GCMS results are therefore in agreement about an overall enrichment in 13CH4 of ~10%. The value of D/H in Titan's CH4 has long been controversial: historical measurements have ranged from about 8-15 x 10-5 (e.g. Coustenis et al. 1989, Coustenis et al. 2003). A recent measurement based on CIRS limb data by Bezard et al. (2007) puts the D/H in CH4 at (13 +/- 1) x 10-5, very much greater than in Jupiter and Saturn, ~2 x 10-5 (Mahaffy et al. 1998, Fletcher et al. 2009). To add complexity, the 12C/13C and D/H vary among molecules in Titan atmosphere, typically showing enhancement in D but depletion in 13C in the daughter species (H2, C2H2, C2H6), relative to the photochemical progenitor, methane. Jennings et al. (2009) have sought to interpret the variance in carbon isotopes as a Kinetic Isotope Effect (KIE), whilst an explanation for the D/H in all molecules remains elusive (Cordier et al. 2008). In this presentation we argue that evolution of isotopic ratios in Titan's methane over time forms a ticking 'clock', somewhat analogous to isotopic ratios in geochronology. Under plausible assumptions about the initial values and subsequent replenishment, various

  9. Remember the Titans: A Theoretical Analysis

    Directory of Open Access Journals (Sweden)

    Rameca Leary

    2013-06-01

    Full Text Available This paper addresses a pivotal time in American history, when a 1971 Supreme Court mandate required southern school districts to end segregation (Daugherity, 2011. In Alexandria, Virginia, the merger of three rival high schools yielded a racially diverse football team and coaching staff. Beforehand, blacks and whites had their own schools. Many wondered how the new T.C. Williams Titans football team would fare. This paper takes an in-depth look at the film, Remember the Titans, which is based on this story. It analyzes the film using Gordon Allport’s (1954 Intergroup Contact Theory to assess how people from different backgrounds interact within group settings. It explores how communication barriers and the absence of knowledge can lead to ignorance. A 21st century legacy is also discussed, including ideas for further research. 

  10. Remember the Titans: A Theoretical Analysis

    Directory of Open Access Journals (Sweden)

    Rameca Leary

    2013-06-01

    Full Text Available This paper addresses a pivotal time in American history, when a 1971 Supreme Court mandate required southern school districts to end segregation (Daugherity, 2011. In Alexandria, Virginia, the merger of three rival high schools yielded a racially diverse football team and coaching staff. Beforehand, blacks and whites had their own schools. Many wondered how the new T.C. Williams Titans football team would fare. This paper takes an in-depth look at the film, Remember the Titans, which is based on this story. It analyzes the film using Gordon Allport’s (1954 Intergroup Contact Theory to assess how people from different backgrounds interact within group settings. It explores how communication barriers and the absence of knowledge can lead to ignorance. A 21st century legacy is also discussed, including ideas for further research.

  11. Scandium complexes with the tetraphenylethylene and anthracene dianions.

    Science.gov (United States)

    Ellis, John E; Minyaev, Mikhail E; Nifant'ev, Ilya E; Churakov, Andrei V

    2018-06-01

    The structural study of Sc complexes containing dianions of anthracene and tetraphenylethylene should shed some light on the nature of rare-earth metal-carbon bonding. The crystal structures of (18-crown-6)bis(tetrahydrofuran-κO)sodium bis(η 6 -1,1,2,2-tetraphenylethenediyl)scandium(III) tetrahydrofuran disolvate, [Na(C 4 H 8 O) 2 (C 12 H 24 O 6 )][Sc(C 26 H 20 ) 2 ]·2C 4 H 8 O or [Na(18-crown-6)(THF) 2 ][Sc(η 6 -C 2 Ph 4 ) 2 ]·2(THF), (1b), (η 5 -1,3-diphenylcyclopentadienyl)(tetrahydrofuran-κO)(η 6 -1,1,2,2-tetraphenylethenediyl)scandium(III) toluene hemisolvate, [Sc(C 17 H 13 )(C 26 H 20 )(C 4 H 8 O)]·0.5C 7 H 8 or [(η 5 -1,3-Ph 2 C 5 H 3 )Sc(η 6 -C 2 Ph 4 )(THF)]·0.5(toluene), (5b), poly[[(μ 2 -η 3 :η 3 -anthracenediyl)bis(η 6 -anthracenediyl)bis(η 5 -1,3-diphenylcyclopentadienyl)tetrakis(tetrahydrofuran)dipotassiumdiscandium(III)] tetrahydrofuran monosolvate], {[K 2 Sc 2 (C 14 H 10 ) 3 (C 17 H 13 ) 2 (C 4 H 8 O) 4 ]·C 4 H 8 O} n or [K(THF) 2 ] 2 [(1,3-Ph 2 C 5 H 3 ) 2 Sc 2 (C 14 H 10 ) 3 ]·THF, (6), and 1,4-diphenylcyclopenta-1,3-diene, C 17 H 14 , (3a), have been established. The [Sc(η 6 -C 2 Ph 4 ) 2 ] - complex anion in (1b) contains the tetraphenylethylene dianion in a symmetrical bis-η 3 -allyl coordination mode. The complex homoleptic [Sc(η 6 -C 2 Ph 4 ) 2 ] - anion retains its structure in THF solution, displaying hindered rotation of the coordinated phenyl rings. The 1D 1 H and 13 C{ 1 H}, and 2D COSY 1 H- 1 H and 13 C- 1 H NMR data are presented for M[Sc(Ph 4 C 2 ) 2 ]·xTHF [M = Na and x = 4 for (1a); M = K and x = 3.5 for (2a)] in THF-d 8 media. Complex (5b) exhibits an unsymmetrical bis-η 3 -allyl coordination mode of the dianion, but this changes to a η 4 coordination mode for (1,3-Ph 2 C 5 H 3 )Sc(Ph 4 C 2 )(THF) 2 , (5a), in THF-d 8 solution. A 45 Sc NMR study of (2a) and UV-Vis studies of (1a), (2a) and (5a) indicate a significant covalent contribution to the Sc-Ph 4 C 2 bond character. The unique Sc ate complex, (6

  12. Titan after Cassini Huygens

    Science.gov (United States)

    Beauchamp, P. M.; Lunine, J.; Lebreton, J.; Coustenis, A.; Matson, D.; Reh, K.; Erd, C.

    2008-12-01

    In 2005, the Huygens Probe gave us a snapshot of a world tantalizingly like our own, yet frozen in its evolution on the threshold of life. The descent under parachute, like that of Huygens in 2005, is happening again, but this time in the Saturn-cast twilight of winter in Titan's northern reaches. With a pop, the parachute is released, and then a muffled splash signals the beginning of the first floating exploration of an extraterrestrial sea-this one not of water but of liquid hydrocarbons. Meanwhile, thousands of miles away, a hot air balloon, a "montgolfiere," cruises 6 miles above sunnier terrain, imaging vistas of dunes, river channels, mountains and valleys carved in water ice, and probing the subsurface for vast quantities of "missing" methane and ethane that might be hidden within a porous icy crust. Balloon and floater return their data to a Titan Orbiter equipped to strip away Titan's mysteries with imaging, radar profiling, and atmospheric sampling, much more powerful and more complete than Cassini was capable of. This spacecraft, preparing to enter a circular orbit around Saturn's cloud-shrouded giant moon, has just completed a series of flybys of Enceladus, a tiny but active world with plumes that blow water and organics from the interior into space. Specialized instruments on the orbiter were able to analyze these plumes directly during the flybys. Titan and Enceladus could hardly seem more different, and yet they are linked by their origin in the Saturn system, by a magnetosphere that sweeps up mass and delivers energy, and by the possibility that one or both worlds harbor life. It is the goal of the NASA/ESA Titan Saturn System Mission (TSSM) to explore and investigate these exotic and inviting worlds, to understand their natures and assess the possibilities of habitability in this system so distant from our home world. Orbiting, landing, and ballooning at Titan represent a new and exciting approach to planetary exploration. The TSSM mission

  13. Bonding in scandium monosulfide a NaCl crystal type

    International Nuclear Information System (INIS)

    Merrick, J.A.

    1980-08-01

    The transition temperature of an order-disorder transition in Sc 0 81 S (R anti 3m to Fm3m) occurs at 700 0 C. A group of ordered sublattices on the NaCl-type lattice (Fm3m) was generated and a Madelung energy and configurational entropy were calculated for each sublattice assuming the ions to be Sc 2 48+ and S 2- . Mean field and pair interaction approximations were used to model long-range and short-range orderings, respectively. The electrostatic model fails to predict the observed short-range and long-range orderings. The high temperature vaporization of ScP was investigated by mass spectrometry and target collection Knudsen effusion at 1767 to 2209K. The composition ScP 1 00 vaporizes congruently to the gaseous species Sc, P, and P 2 . A temperature independent third law enthalpy of atomization (ΔH 0 /sub atom,298/ = 252.2 +- 2.8 kcal mole -1 ) has a value approx. 12 kcal larger than that reported for ScS. Nonrelativistic, nonself-consistent LAPW band structure calculations are reported for ScS. XPS and UPS measurements are reported for Sc 2 S 3 and several compositions Sc/sub 1-x/S (0.0 less than or equal to x less than or equal to 0.2). The Sc and S 2p binding energies (XPS) obtained for the defect scandium monosulfides are very close to those found in the pure elements, suggesting covalent bonding. The Sc 2p energy region has an interesting satellite structure

  14. Titan's Methane Cycle is Closed

    Science.gov (United States)

    Hofgartner, J. D.; Lunine, J. I.

    2013-12-01

    Doppler tracking of the Cassini spacecraft determined a polar moment of inertia for Titan of 0.34 (Iess et al., 2010, Science, 327, 1367). Assuming hydrostatic equilibrium, one interpretation is that Titan's silicate core is partially hydrated (Castillo-Rogez and Lunine, 2010, Geophys. Res. Lett., 37, L20205). These authors point out that for the core to have avoided complete thermal dehydration to the present day, at least 30% of the potassium content of Titan must have leached into an overlying water ocean by the end of the core overturn. We calculate that for probable ammonia compositions of Titan's ocean (compositions with greater than 1% ammonia by weight), that this amount of potassium leaching is achievable via the substitution of ammonium for potassium during the hydration epoch. Formation of a hydrous core early in Titan's history by serpentinization results in the loss of one hydrogen molecule for every hydrating water molecule. We calculate that complete serpentinization of Titan's core corresponds to the release of more than enough hydrogen to reconstitute all of the methane atoms photolyzed throughout Titan's history. Insertion of molecular hydrogen by double occupancy into crustal clathrates provides a storage medium and an opportunity for ethane to be converted back to methane slowly over time--potentially completing a cycle that extends the lifetime of methane in Titan's surface atmosphere system by factors of several to an order of magnitude over the photochemically-calculated lifetime.

  15. Cryovolcanism on Titan

    Science.gov (United States)

    Mitri, G.; Showman, A. P.; Lunine, J. I.; Lopes, R. M.

    2008-12-01

    Remote sensing observations yield evidence for cryovolcanism on Titan, and evolutionary models support (but do not require) the presence of an ammonia-water subsurface ocean. The impetus for invoking ammonia as a constituent in an internal ocean and cryovolcanic magma comes from two factors. First, ammonia-water liquid has a lower freezing temperature than pure liquid water, enabling cryovolcanism under the low- temperature conditions prevalent in the outer Solar System. Second, pure water is negatively buoyant with respect to pure water ice, which discourages eruption from the subsurface ocean to the surface. In contrast, the addition of ammonia to the water decreases its density, hence lessening this problem of negative buoyancy. A marginally positive buoyant ammonia-water mixture might allow effusive eruptions from a subsurface ocean. If the subsurface ocean were positively buoyant, all the ammonia would have been erupted very early in Titan's history. Contrary to this scenario, Cassini-Huygens has so far observed neither a global abundance nor a complete dearth of cryovolcanic features. Further, an ancient cryovolcanic epoch cannot explain the relative youth of Titan's surface. Crucial to invoking ammonia-water resurfacing as the source of the apparently recent geological activity is not how to make ammonia-water volcanism work (because the near neutral buoyancy of the ammonia-water mixture encourages an explanation), but rather how to prevent eruption from occurring so easily that cryovolcanic activity is over early on. Although cryovolcanism by ammonia-water has been proposed as a resurfacing process on Titan, few models have specifically dealt with the problem of how to transport ammonia-water liquid onto the surface. We proposed a model of cryovolcanism that involve cracking at the base of the ice shell and formation of ammonia-water pockets in the ice. While the ammonia-water pockets cannot easily become neutral buoyant and promote effusive eruptions

  16. The effects of aluminum or scandium on the toughness, density and ...

    African Journals Online (AJOL)

    The effects of the substitution of aluminum or scandium on the density, toughness as well as the stability of the phases formed by such an addition on platinum, iridium, rhodium and palladium metals were evaluated with the density functional quantum mechanical calculation methods. All the metals had four atoms per ...

  17. Study of competitive complexing in scandium(3)-xylenol-orange-hydroxyethyliminodiacetic acid system

    International Nuclear Information System (INIS)

    Kornev, V.I.; Mukanov, I.P.; Artem'eva, O.A.

    1976-01-01

    The competitive complexing in the system scandium(3)-xylene orange (XO)-hydroxyethyliminodiacetic acid (H 3 L) has been studied. Ligands act as competitive particles. It has been established preliminarily that introduction of H 3 L into the solution containing a mixture of Sc and Xo changes considerably the absorption spectra of the coloured complex. Weakening of light absorption indicates that the coloured complex with XO is destructed and colourless hydroxyethyliminodiacetate of scandium is formed. The formation of scandium hydroxyethyliminoacetate has been studied spectrophotometrically by equilibrium between the complexes. The dependence of optical density on pH, when the concentrations of reagents are constant, as well as on concetration of H 3 L has been studied. The composition of the complex (1:1) formed at pH 3.2 has been established graphically and the constant of the complex ScHL + instability has been calculated (PKsub(H)=10.69+-0.45). It has been shown that H 3 L, when interacting with scandium, behaves as dibasic ligand. It is most probable that during complex formation the hydrogen ion of the hydroxygroup is not replaced, although the participation of hydroxygroup in coordination is possible due to a donor-acceptor bond

  18. Structural differences of half-sandwich complexes of scandium and yttrium containing bulky substituents

    Czech Academy of Sciences Publication Activity Database

    Fridrichová, Adéla; Růžička, A.; Lamač, Martin; Horáček, Michal

    2017-01-01

    Roč. 76, FEB 2017 (2017), s. 62-66 ISSN 1387-7003 R&D Projects: GA ČR(CZ) GAP207/12/2368 Institutional support: RVO:61388955 Keywords : scandium * yttrium * half-sandwich Subject RIV: CF - Physical ; Theoretical Chemistry OBOR OECD: Physical chemistry Impact factor: 1.640, year: 2016

  19. In situ observation of the reaction of scandium and carbon by neutron diffraction

    Energy Technology Data Exchange (ETDEWEB)

    Juarez-Arellano, Erick A., E-mail: eajuarez@unpa.edu.m [Institut fuer Geowissenschaften, Universitaet Frankfurt, Altenhoeferallee 1, 60438 Frankfurt a.M. (Germany); Universidad del Papaloapan, Circuito Central 200, Parque Industrial, Tuxtepec 68301 (Mexico); Winkler, Bjorn [Institut fuer Geowissenschaften, Universitaet Frankfurt, Altenhoeferallee 1, 60438 Frankfurt a.M. (Germany); Vogel, Sven C. [Los Alamos National Laboratory, Lujan Center. Mail Stop H805, Los Alamos, NM 87545 (United States); Senyshyn, Anatoliy [Forschungsneutronenquelle Heinz Maier-Leibnitz (FRM II), Technische Universitaet Muenchen, Lichtenbergstr. 1, D-85747 Garching (Germany); Materialwissenschaft, TU Darmstadt, Petersensstr. 23, D-64287 Darmstadt (Germany); Kammler, Daniel R. [Sandia National Laboratories, Albuquerque, NM 87185 (United States); Avalos-Borja, Miguel [CNyN, UNAM, A. Postal 2681, Ensenada, B.C. (Mexico)

    2011-01-05

    Research highlights: {yields} Exist two ScC cubic phases with B1-structure type differing in site occupancy of C. {yields} A new orthorhombic scandium carbide phase is formed at 1473(50) K. {yields} The recrystallization of alpha-Sc occurs between 1000 and 1223 K. - Abstract: The formation of scandium carbides by reaction of the elements has been investigated by in situ neutron diffraction up to 1823 K. On heating, the recrystallization of {alpha}-Sc occurs between 1000 and 1223 K. The formation of Sc{sub 2}C and ScC (NaCl-B1 type structure) phases has been detected at 1323 and 1373 K, respectively. The formation of a new orthorhombic scandium carbide phase was observed at 1473(50) K. Once the scandium carbides are formed they are stable upon heating or cooling. No other phases were detected in the present study, in which the system was always carbon saturated. The thermal expansion coefficients of all phases have been determined, they are constant throughout the temperature interval studied.

  20. Acetylene on Titan

    Science.gov (United States)

    Singh, Sandeep; McCord, Thomas B.; Combe, Jean-Philippe; Rodriguez, Sebastien; Cornet, Thomas; Le Mouélic, Stéphane; Clark, Roger Nelson; Maltagliati, Luca; Chevrier, Vincent

    2016-10-01

    Saturn's moon Titan possesses a thick atmosphere that is mainly composed of N2 (98%), CH4 (2 % overall, but 4.9% close to the surface) and less than 1% of minor species, mostly hydrocarbons [1]. A dissociation of N2 and CH4 forms complex hydrocarbons in the atmsophere and acetylene (C2H2) and ethane (C2H6) are produced most abundently. Since years, C2H2 has been speculated to exist on the surface of Titan based on its high production rate in the stratosphere predicted by photochemical models [2,3] and from its detection as trace gas sublimated/evaporated from the surface after the landing of the Huygens probe by the Gas Chromatograph Mass Spectrometer (GCMS) [1]. Here we show evidence of acetylene (C2H2) on the surface of Titan by detecting absorption bands at 1.55 µm and 4.93 µm using Cassini Visual and Infrared Mapping Spectrometer (VIMS) [4] at equatorial areas of eastern Shangri-La, and Fensal-Aztlan/Quivira.An anti-correlation of absorption band strength with albedo indicates greater concentrations of C2H2 in the dark terrains, such as sand dunes and near the Huygens landing site. The specific location of the C2H2 detections suggests that C2H2 is mobilized by surface processes, such as surface weathering by liquids through dissolution/evaporation processes.References:[1]Niemann et al., Nature 438, 779-784 (2005).[2]Lavvas et al., Planetary and Space Science 56, 67 - 99 (2008).[3]Lavvas et al., Planetary and Space Science 56, 27 - 66 (2008).[4] Brown et al., The Cassini-Huygens Mission 111-168 (Springer, 2004).

  1. Titan's Radioactive Haze : Production and Fate of Radiocarbon On Titan

    Science.gov (United States)

    Lorenz, R. D.; Jull, A. J. T.; Swindle, T. D.; Lunine, J. I.

    Just as cosmic rays interact with nitrogen atoms in the atmosphere of Earth to gener- ate radiocarbon (14C), the same process should occur in Titan`s nitrogen-rich atmo- sphere. Titan`s atmosphere is thick enough that cosmic ray flux, rather than nitrogen column depth, limits the production of 14 C. Absence of a strong magnetic field and the increased distance from the sun suggest production rates of 9 atom/cm2/s, approx- imately 4 times higher than Earth. On Earth the carbon is rapidly oxidised into CO2. The fate and detectability of 14C on Titan depends on the chemical species into which it is incorporated in Titan's reducing atmosphere : as methane it would be hopelessly diluted even in only the atmosphere (ignoring the other, much more massive carbon reservoirs likely to be present on Titan, like hydrocarbon lakes.) However, in the more likely case that the 14C attaches to the haze that rains out onto the surface (as tholin, HCN or acetylene and their polymers - a much smaller carbon reservoir) , haze in the atmosphere or recently deposited on the surface would therefore be quite intrinsically radioactive. Such activity may modify the haze electrical charging and hence its coag- ulation. Measurements with compact instrumentation on future in-situ missions could place useful constraints on the mass deposition rates of photochemical material on the surface and identify locations where surface deposits of such material are `freshest`.

  2. Titan's Gravitational Field

    Science.gov (United States)

    Schubert, G.; Anderson, J. D.

    2013-12-01

    Titan's gravitational field is inferred from an analysis of archived radio Doppler data for six Cassini flybys. The analysis considers each flyby separately in contrast to the approach of lumping all the data together in a massive inversion. In this way it is possible to gain an improved understanding of the character of each flyby and its usefulness in constraining the gravitational coefficient C22 . Though our analysis is not yet complete and our final determination of C22 could differ from the result we report here by 1 or 2 sigma, we find a best-fit value of C22 equal to (13.21 × 0.17) × 10-6, significantly larger than the value of 10.0 × 10-6 obtained from an inversion of the lumped Cassini data. We also find no determination of the tidal Love number k2. The larger value of C22 implies a moment of inertia factor equal to 0.3819 × 0.0020 and a less differentiated Titan than is suggested by the smaller value. The larger value of C22 is consistent with an undifferentiated model of the satellite. While it is not possible to rule out either value of C22 , we prefer the larger value because its derivation results from a more hands on analysis of the data that extracts the weak hydrostatic signal while revealing the effects of gravity anomalies and unmodeled spacecraft accelerations on each of the six flybys.

  3. Titan's Emergence from Winter

    Science.gov (United States)

    Flasar, F. Michael; Achterberg, Richard; Jennings, Donald; Schinder, Paul

    2011-01-01

    We summarize the changes in Titans thermal structure derived from Cassini CIRS and radio-occultation data during the transition from winter to early spring. Titan's surface, and middle atmosphere show noticeable seasonal change, whereas that in most of the troposphere is mated. This can be understood in terms of the relatively small radiative relaxation time in the middle atmosphere and much larger time scale in the troposphere. The surface exhibits seasonal change because the heat capacity in an annual skin depth is much smaller than that in the lowest scale height of the troposphere. Surface temperatures rise 1 K at raid and high latitudes in the winter northern hemisphere and cool in the southern hemisphere. Changes in in the middle atmosphere are more complicated. Temperatures in the middle stratosphere (approximately 1 mbar) increase by a few kelvin at mid northern latitudes, but those at high latitudes first increase as that region moves out of winter shadow, and then decrease. This probably results from the combined effect of increased solar heating as the suit moves higher in the sky and the decreased adiabatic warming as the sinking motions associated with the cross-equatorial meridional cell weaken. Consistent with this interpretation, the warm temperatures observed higher up at the winter polar stratopause cool significantly.

  4. Seasonal Changes in Titan's Meteorology

    Science.gov (United States)

    Turtle, E. P.; DelGenio, A. D.; Barbara, J. M.; Perry, J. E.; Schaller, E. L.; McEwen, A. S.; West, R. A.; Ray, T. L.

    2011-01-01

    The Cassini Imaging Science Subsystem has observed Titan for 1/4 Titan year, and we report here the first evidence of seasonal shifts in preferred locations of tropospheric methane clouds. South \\polar convective cloud activity, common in late southern summer, has become rare. North \\polar and northern mid \\latitude clouds appeared during the approach to the northern spring equinox in August 2009. Recent observations have shown extensive cloud systems at low latitudes. In contrast, southern mid \\latitude and subtropical clouds have appeared sporadically throughout the mission, exhibiting little seasonality to date. These differences in behavior suggest that Titan s clouds, and thus its general circulation, are influenced by both the rapid temperature response of a low \\thermal \\inertia surface and the much longer radiative timescale of Titan s cold thick troposphere. North \\polar clouds are often seen near lakes and seas, suggesting that local increases in methane concentration and/or lifting generated by surface roughness gradients may promote cloud formation. Citation

  5. The age of Titan's surface

    Science.gov (United States)

    Neish, C. D.; Lorenz, R. D.

    2010-04-01

    High-resolution images of the surface of Titan taken by the Cassini spacecraft reveal a world with an extreme paucity of impact craters. Planetary surfaces are commonly dated by dividing the number of impact craters by the estimated impactor flux, but this approach has been confounded at Titan by several difficulties. First, high-resolution imaging of the surface of Titan is far from complete (in the near-infrared as well as radar). As of December 2007, Cassini RADAR images covered only 22% of its surface. However, we can use Monte-Carlo models to explore how many craters of a given size (with large or very large craters being of particular interest) may be present in the unobserved areas. Second, literature descriptions of the crater formation rate (e.g. Korycansky and Zahnle 2005 and Artemieva and Lunine 2005) are apparently not in agreement. We discuss possible resolutions. Third, since surface modification processes are ongoing, the actual number of craters on Titan's surface remains uncertain, as craters may be eroded beyond recognition, or obscured by lakes or sand seas. In this connection, we use the Earth as an analogue. The Earth is in many ways the most "Titan-like" world in the solar system, with extensive modification by erosion, burial, tectonism, and volcanism. We compare the observed number of terrestrial craters to the expected terrestrial impactor flux to determine the crater reduction factor for a world similar to Titan. From this information, we can back out the actual number of craters on Titan's surface and estimate its crater retention age. An accurate age estimate will be critical for constraining models of Titan's formation and evolution.

  6. Monosodium titanate particle characterization

    International Nuclear Information System (INIS)

    Chandler, G.T.; Hobbs, D.T.

    1993-01-01

    A characterization study was performed on monosodium titanate (MST) particles to determine the effect of high shear forces expected from the In-Tank Precipitation (ITP) process pumps on the particle size distribution. The particles were characterized using particle size analysis and scanning electron microscopy (SEM). No significant changes in particle size distributions were observed between as-received MST and after 2--4 hours of shearing. Both as-received and sheared MST particles contained a large percentage of porosity with pore sizes on the order of 500 to 2,000 Angstroms. Because of the large percentage of porosity, the overall surface area of the MST is dominated by the internal surfaces. The uranium and plutonium species present in the waste solution will have access to both interior and exterior surfaces. Therefore, uranium and plutonium loading should not be a strong function of MST particle size

  7. Chemistry in Titan

    Science.gov (United States)

    Plessis, S.; Carrasco, N.; Pernot, P.

    2009-04-01

    Modelling the chemical composition of Titan's ionosphere is a very challenging issue. Latest works perform either inversion of CASSINI's INMS mass spectra (neutral[1] or ion[2]), or design coupled ion-neutral chemistry models[3]. Coupling ionic and neutral chemistry has been reported to be an essential feature of accurate modelling[3]. Electron Dissociative Recombination (EDR), where free electrons recombine with positive ions to produce neutral species, is a key component of ion-neutral coupling. There is a major difficulty in EDR modelling: for heavy ions, the distribution of neutral products is incompletely characterized by experiments. For instance, for some hydrocarbon ions only the carbon repartition is measured, leaving the hydrogen repartition and thus the exact neutral species identity unknown[4]. This precludes reliable deterministic modelling of this process and of ion-neutral coupling. We propose a novel stochastic description of the EDR chemical reactions which enables efficient representation and simulation of the partial experimental knowledge. The description of products distribution in multi-pathways reactions is based on branching ratios, which should sum to unity. The keystone of our approach is the design of a probability density function accounting for all available informations and physical constrains. This is done by Dirichlet modelling which enables one to sample random variables whose sum is constant[5]. The specifics of EDR partial uncertainty call for a hierarchiral Dirichlet representation, which generalizes our previous work[5]. We present results on the importance of ion-neutral coupling based on our stochastic model. C repartition H repartition (measured) (unknown ) → C4H2 + 3H2 + H .. -→ C4 . → C4H2 + 7H → C3H8. + CH C4H+9 + e- -→ C3 + C .. → C3H3 + CH2 + 2H2 → C2H6 + C2H2 + H .. -→ C2 + C2 . → 2C2H2 + 2H2 + H (1) References [1] J. Cui, R.V. Yelle, V. Vuitton, J.H. Waite Jr., W.T. Kasprzak

  8. Methane rain on Titan

    Science.gov (United States)

    Toon, Owen B.; Mckay, Christopher P.; Courtin, Regis; Ackerman, Thomas P.

    1988-01-01

    The atmosphere of Titan is characterized by means of model computations based on Voyager IRIS IR spectra and published data from laboratory determinations of absorption coefficients and cloud refractive indices. The results are presented in tables and graphs, and it is pointed out that the presence of Ar is not required in the model. Particular attention is given to the role of CH4, which is found to form patchy clouds (with particle radii of 50 microns or greater and visible/IR optical depths of 2-5) at altitudes up to about 30 km. The mechanisms by which such rain-sized particles could form are discussed, and it is suggested that the observed 500-600/cm spectrum is affected much less by the CH4 clouds than by H2 or variations in the temperature of the high-altitude haze.

  9. Strontium titanate thin film deposition - structural and electronical characterization

    Energy Technology Data Exchange (ETDEWEB)

    Hanzig, Florian; Hanzig, Juliane; Stoecker, Hartmut; Mehner, Erik; Abendroth, Barbara; Meyer, Dirk C. [TU Bergakademie Freiberg, Institut fuer Experimentelle Physik (Germany); Franke, Michael [TU Bergakademie Freiberg, Institut fuer Elektronik- und Sensormaterialien (Germany)

    2012-07-01

    Strontium titanate is on the one hand a widely-used model oxide for solids which crystallize in perovskite type of structure. On the other hand, with its large band-gap energy and its mixed ionic and electronic conductivity, SrTiO{sub 3} is a promising isolating material in metal-insulator-metal (MIM) structures for resistive switching memory cells. Here, we used physical vapour deposition methods (e. g. electron-beam and sputtering) to produce strontium titanate layers. Sample thicknesses were probed with X-ray reflectometry (XRR) and spectroscopic ellipsometry (SE). Additionally, layer densities and dielectric functions were quantified with XRR and SE, respectively. Using infrared spectroscopy free electron concentrations were obtained. Phase and element composition analysis was carried out with grazing incidence X-ray diffraction and X-ray photoelectron spectroscopy. Subsequent temperature treatment of samples lead to crystallization of the initially amorphous strontium titanate.

  10. The TITAN reversed-field-pinch fusion reactor study

    Energy Technology Data Exchange (ETDEWEB)

    1990-01-01

    This report discusses research on the titan-1 fusion power core. The major topics covered are: titan-1 fusion-power-core engineering; titan-1 divertor engineering; titan-1 tritium systems; titan-1 safety design and radioactive-waste disposal; and titan-1 maintenance procedures.

  11. The TITAN reversed-field-pinch fusion reactor study

    International Nuclear Information System (INIS)

    1990-01-01

    This report discusses research on the titan-1 fusion power core. The major topics covered are: titan-1 fusion-power-core engineering; titan-1 divertor engineering; titan-1 tritium systems; titan-1 safety design and radioactive-waste disposal; and titan-1 maintenance procedures

  12. Freeze cast porous barium titanate for enhanced piezoelectric energy harvesting

    Science.gov (United States)

    Roscow, J. I.; Zhang, Y.; Kraśny, M. J.; Lewis, R. W. C.; Taylor, J.; Bowen, C. R.

    2018-06-01

    Energy harvesting is an important developing technology for a new generation of self-powered sensor networks. This paper demonstrates the significant improvement in the piezoelectric energy harvesting performance of barium titanate by forming highly aligned porosity using freeze casting. Firstly, a finite element model demonstrating the effect of pore morphology and angle with respect to poling field on the poling behaviour of porous ferroelectrics was developed. A second model was then developed to understand the influence of microstructure-property relationships on the poling behaviour of porous freeze cast ferroelectric materials and their resultant piezoelectric and energy harvesting properties. To compare with model predictions, porous barium titanate was fabricated using freeze casting to form highly aligned microstructures with excellent longitudinal piezoelectric strain coefficients, d 33. The freeze cast barium titanate with 45 vol.% porosity had a d 33  =  134.5 pC N‑1 compared to d 33  =  144.5 pC N‑1 for dense barium titanate. The d 33 coefficients of the freeze cast materials were also higher than materials with uniformly distributed spherical porosity due to improved poling of the aligned microstructures, as predicted by the models. Both model and experimental data indicated that introducing porosity provides a large reduction in the permittivity () of barium titanate, which leads to a substantial increase in energy harvesting figure of merit, , with a maximum of 3.79 pm2 N‑1 for barium titanate with 45 vol.% porosity, compared to only 1.40 pm2 N‑1 for dense barium titanate. Dense and porous barium titanate materials were then used to harvest energy from a mechanical excitation by rectification and storage of the piezoelectric charge on a capacitor. The porous barium titanate charged the capacitor to a voltage of 234 mV compared to 96 mV for the dense material, indicating a 2.4-fold increase that was similar to that

  13. Selective adsorption and ion exchange of metal cations and anions with silico-titanates and layered titanates

    International Nuclear Information System (INIS)

    Anthony, R.G.; Philip, C.V.

    1993-01-01

    Metal ions may be removed from aqueous wastes from metal processing plants and from refineries. They may also be used in concentrating radioactive elements found in dilute, aqueous, nuclear wastes. A new series of silico-titanates and alkali titanates are shown to have specific selectivity for cations of lead, mercury, and cadmium and the dichromate anion in solutions with low and high pH. Furthermore, one particular silico-titanate, TAM-5, was found to be highly selective for Cs + and Sr 2+ in solutions of 5.7 M Na + and 0.6 M Oh - . A high potential exists for these materials for removing Cs + and Sr 2+ from radioactive aqueous wastes containing high concentrations of Na + at high and low pH

  14. Titan LEAF: A Sky Rover Granting Targeted Access to Titan's Lakes and Plains

    Science.gov (United States)

    Ross, Floyd; Lee, Greg; Sokol, Daniel; Goldman, Benjamin; Bolisay, Linden

    2016-10-01

    Northrop Grumman, in collaboration with L'Garde Inc. and Global Aerospace Corporation (GAC), has been developing the Titan Lifting Entry Atmospheric Flight (T-LEAF) sky rover to roam the atmosphere and observe at close quarters the lakes and plains of Titan. T-LEAF also supports surface exploration and science by providing precision delivery of in situ instruments to the surface.T-LEAF is a maneuverable, buoyant air vehicle. Its aerodynamic shape provides its maneuverability, and its internal helium envelope reduces propulsion power requirements and also the risk of crashing. Because of these features, T-LEAF is not restricted to following prevailing wind patterns. This freedom of mobility allows it be commanded to follow the shorelines of Titan's methane lakes, for example, or to target very specific surface locations.T-LEAF utilizes a variable power propulsion system, from high power at ~200W to low power at ~50W. High power mode uses the propellers and control surfaces for additional mobility and maneuverability. It also allows the vehicle to hover over specific locations for long duration surface observations. Low power mode utilizes GAC's Titan Winged Aerobot (TWA) concept, currently being developed with NASA funding, which achieves guided flight without the use of propellers or control surfaces. Although slower than high powered flight, this mode grants increased power to science instruments while still maintaining control over direction of travel.Additionally, T-LEAF is its own entry vehicle, with its leading edges protected by flexible thermal protection system (f-TPS) materials already being tested by NASA's Hypersonic Inflatable Aerodynamic Decelerator (HIAD) group. This f-TPS technology allows T-LEAF to inflate in space, like HIAD, and then enter the atmosphere fully deployed. This approach accommodates entry velocities from as low as ~1.8 km/s if entering from Titan orbit, up to ~6 km/s if entering directly from Saturn orbit, like the Huygens probe

  15. Process Design Aspects for Scandium-Selective Leaching of Bauxite Residue with Sulfuric Acid

    OpenAIRE

    Konstantinos Hatzilyberis; Theopisti Lymperopoulou; Lamprini-Areti Tsakanika; Klaus-Michael Ochsenkühn; Paraskevas Georgiou; Nikolaos Defteraios; Fotios Tsopelas; Maria Ochsenkühn-Petropoulou

    2018-01-01

    Aiming at the industrial scale development of a Scandium (Sc)-selective leaching process of Bauxite Residue (BR), a set of process design aspects has been investigated. The interpretation of experimental data for Sc leaching yield, with sulfuric acid as the leaching solvent, has shown significant impact from acid feed concentration, mixing time, liquid to solids ratio (L/S), and number of cycles of leachate re-usage onto fresh BR. The thin film diffusion model, as the fundamental theory for l...

  16. Diagrammatic Representation of Electronic Correlations in Photoionization Process: Application to Scandium

    International Nuclear Information System (INIS)

    Liu Mengmeng; Ma Xiaoguang

    2011-01-01

    The conversion rules under which an algebraic expression can be obtained from a corresponding photoionization Goldstone diagram have been given systematically in the present work. The electronic correlations in the photoionization processes then could be studied diagrammatically. The application to atomic scandium shows that the present theoretical scheme can give reasonable photoionization cross sections, which agree well with the experimental results. (atomic and molecular physics)

  17. Titan Montgolfiere Terrestrial Test Bed, Phase II

    Data.gov (United States)

    National Aeronautics and Space Administration — With the Titan Saturn System Mission, NASA is proposing to send a Montgolfiere balloon to probe the atmosphere of Titan. To better plan this mission and create a...

  18. Titan Montgolfiere Terrestrial Test Bed, Phase I

    Data.gov (United States)

    National Aeronautics and Space Administration — With the Titan Saturn System Mission, NASA is proposing to send a Montgolfiere balloon to probe the atmosphere of Titan. In order to better plan this mission and...

  19. Pilot-scale recovery of rare earths and scandium from phosphogypsum and uranium leachates

    Directory of Open Access Journals (Sweden)

    Mashkovtsev Maxim

    2016-01-01

    Full Text Available Ural Federal University (UrFU and VTT have performed joint research on development of industrial technologies for the extraction of REM and Scandium compounds from phosphogypsum and Uranium ISL leachate solutions. Leaching-absorption experiments at UrFU have been supported with multicomponent solution modelling by VTT. The simulations have been performed with VTT’s ChemSheet/Balas program and can be used for speciation calculations in the lixiviant solution. The experimental work combines solvent extraction with advanced ion exchange methodology in a pilot facility capable of treating 5 m3 solution per hour. Currently, the plant produces cerium carbonate, lanthanum oxide, neodymium oxide and concentrate of heavy rare earth metals. A batch of 45 t solids has been processed with the gain of 100 kg’s of REM concentrate. A mini-pilot plant with productivity above 50 liters per hour has been applied to recover scandium oxide and REE concentrates from the uranium ISL solution. As the preliminary product contains radioactivity (mainly strontium, an additional decontamination and cleaning of both concentrates by extraction has rendered a necessity. Finally a purified 99% concentrate of scandium oxide as well as 99% rare earth concentrate are received.

  20. Effect of scandium on the phase composition and mechanical properties of ABM alloys

    Science.gov (United States)

    Molchanova, L. V.

    2010-09-01

    The effect of scandium on the composition and mechanical properties of ABM-1 alloys (Al-30% Be-5% Mg) is studied. The scandium content is varied from 0.1 to 0.5 wt %. It is established that, in the studied part of the Al-Be-Mg-Sc system, an aluminum solid solution (Al) and the ScBe13 compound are in equilibrium with a beryllium solid solution (Be). Magnesium dissolves in both the aluminum component and the ScBe13 compound. The strengthening effect related to the decomposition of the solid solution and the precipitation of Al3Sc cannot be extended to the strengthening of ABM-type alloys. Additions of 0.1-0.15 wt % Sc only weakly improve the mechanical properties of the alloys due to the refinement of beryllium-component grains. At high scandium contents, the strength increases insignificantly due to primary precipitation of ScBe13 and the plasticity decreases simultaneously.

  1. The atmospheric temperature structure of Titan

    Science.gov (United States)

    Mckay, Christopher P.; Pollack, J. B.; Courtin, Regis; Lunine, Jonathan I.

    1992-01-01

    The contribution of various factors to the thermal structure of Titan's past and present atmosphere are discussed. A one dimensional model of Titan's thermal structure is summarized. The greenhouse effect of Titan's atmosphere, caused primarily by pressure induced opacity of N2, CH4, and H2, is discussed together with the antigreenhouse effect dominated by the haze which absorbs incident sunlight. The implications for the atmosphere of the presence of an ocean on Titan are also discussed.

  2. Titan's Primordial Soup: Formation of Amino Acids via Low Temperature Hydrolysis of Tholins

    Science.gov (United States)

    Neish, Catherine; Somogyi, Á.; Smith, M. A.

    2009-09-01

    Titan, Saturn's largest moon, is a world rich in the "stuff of life". Reactions occurring in its dense nitrogen-methane atmosphere produce a wide variety of organic molecules, which subsequently rain down onto its surface. Water - thought to be another important ingredient for life - is likewise abundant on Titan. Theoretical models of Titan's formation predict that its interior consists of an ice I layer several tens of kilometers thick overlying a liquid ammonia-rich water layer several hundred kilometers thick (Tobie et al., 2005). Though its surface temperature of 94K dictates that Titan is on average too cold for liquid water to persist at its surface, melting caused by impacts and/or cryovolcanism may lead to its episodic availability. Impact melt pools on Titan would likely remain liquid for 102 - 104 years before freezing (O'Brien et al., 2005). The combination of complex organic molecules and transient locales of liquid water make Titan an interesting natural laboratory for studying prebiotic chemistry. In this work, we sought to determine what biomolecules might be formed under conditions analogous to those found in transient liquid water environments on Titan. We hydrolyzed Titan organic haze analogues, or "tholins", in 13 wt. % ammonia-water at 253K and 293K for a year. Using a combination of high resolution mass spectroscopy and tandem mass spectroscopy fragmentation techniques, four amino acids were identified in the hydrolyzed tholin sample. These four species have been assigned as the amino acids asparagine, aspartic acid, glutamine, and glutamic acid. This represents the first detection of biologically relevant molecules created under conditions similar to those found in impact melt pools and cryolavas on Titan. Future missions to Titan should therefore carry instrumentation capable of detecting amino acids and other prebiotically relevant molecules on its surface This work was supported by the NASA Exobiology Program.

  3. Observations of CO in Titan's Atmosphere Using ALMA

    Science.gov (United States)

    Serigano, Joseph; Nixon, Conor A.; Cordiner, Martin; Irwin, Patrick G. J.; Teanby, Nicholas; Charnley, Steven B.; Lindberg, Johan E.; Remijan, Anthony J.

    2015-11-01

    The advent of the Atacama Large Millimeter/submillimeter Array (ALMA) has provided a powerful facility for probing the atmospheres of solar system targets at long wavelengths (84-720 GHz) where the rotational lines of small, polar molecules are prominent. In the dense, nitrogen-dominated atmosphere of Titan, photodissociation of molecular nitrogen and methane leads to a wealth of complex hydrocarbons and nitriles in small abundances. Past millimeter/submillimeter observations, including ground-based observations as well as those by the Composite Infrared Spectrometer (CIRS) aboard the Cassini spacecraft, have proven the significance of this wavelength region for the derivation of vertical mixing profiles, latitudinal and seasonal variations, and molecular detections. Previous ALMA studies of Titan have presented mapping and vertical column densities of hydrogen isocyanide (HNC) and cyanoacetylene (HC3N) (Cordiner et al. 2014) as well as the first spectroscopic detection of ethyl cyanide (C2H5CN) in Titan’s atmosphere (Cordiner et al. 2015).Here, we report several submillimetric observations of carbon monoxide (CO) and its isotopologues 13CO, C18O, and C17O in Titan’s atmosphere obtained with flux calibration data from the ALMA Science Archive. We employ NEMESIS, a line-by-line radiative transfer code, to determine the stratospheric abundances of these molecules. The abundance of CO in Titan's atmosphere is determined to be approximately 50±1 ppm, constant with altitude, and isotopic ratios are determined to be approximately 12C/13C = 90, 16O/18O = 470, and 16O/17O = 2800. This report presents the first spectroscopic detection of C17O in the outer solar system, detected at >11σ confidence. This talk will focus on isotopic ratios in CO in Titan's atmosphere and will compare our results to previously measured values for Titan and other bodies in the Solar System. General implications for the history of Titan from measurements of CO and its isotopologues will be

  4. Titan's cold case files - Outstanding questions after Cassini-Huygens

    Science.gov (United States)

    Nixon, C. A.; Lorenz, R. D.; Achterberg, R. K.; Buch, A.; Coll, P.; Clark, R. N.; Courtin, R.; Hayes, A.; Iess, L.; Johnson, R. E.; Lopes, R. M. C.; Mastrogiuseppe, M.; Mandt, K.; Mitchell, D. G.; Raulin, F.; Rymer, A. M.; Todd Smith, H.; Solomonidou, A.; Sotin, C.; Strobel, D.; Turtle, E. P.; Vuitton, V.; West, R. A.; Yelle, R. V.

    2018-06-01

    The entry of the Cassini-Huygens spacecraft into orbit around Saturn in July 2004 marked the start of a golden era in the exploration of Titan, Saturn's giant moon. During the Prime Mission (2004-2008), ground-breaking discoveries were made by the Cassini orbiter including the equatorial dune fields (flyby T3, 2005), northern lakes and seas (T16, 2006), and the large positive and negative ions (T16 & T18, 2006), to name a few. In 2005 the Huygens probe descended through Titan's atmosphere, taking the first close-up pictures of the surface, including large networks of dendritic channels leading to a dried-up seabed, and also obtaining detailed profiles of temperature and gas composition during the atmospheric descent. The discoveries continued through the Equinox Mission (2008-2010) and Solstice Mission (2010-2017) totaling 127 targeted flybys of Titan in all. Now at the end of the mission, we are able to look back on the high-level scientific questions from the start of the mission, and assess the progress that has been made towards answering these. At the same time, new scientific questions regarding Titan have emerged from the discoveries that have been made. In this paper we review a cross-section of important scientific questions that remain partially or completely unanswered, ranging from Titan's deep interior to the exosphere. Our intention is to help formulate the science goals for the next generation of planetary missions to Titan, and to stimulate new experimental, observational and theoretical investigations in the interim.

  5. Coexistence of Dunes and Humid Conditions at Titan's Tropics

    Science.gov (United States)

    Radebaugh, Jani; Lorenz, R. D.; Lunine, J. I.; Kirk, R. L.; Ori, G. G.; Farr, T. G.; Malaska, M.; Le Gall, A.; Liu, Z. Y. C.; Encrenaz, P. J.; Paillou, P.; Hayes, A.; Lopes, R. M. C.; Turtle, E. P.; Wall, S. D.; Stofan, E. R.; Wood, C. A.; Cassini RADAR Team

    2012-10-01

    At Titan's equatorial latitudes there are tens of thousands of dunes, a landform typical of desert environments where sand does not become anchored by vegetation or fluids. Model climate simulations predict generally dry conditions at the equator and humid conditions near the poles of Titan, where lakes of methane/ethane are found. However, moderate relative methane humidity was observed at the Huygens landing site, recent rainfall was seen by Cassini ISS near the Belet Sand Sea, and a putative transient lake in Shangri-La was observed by Cassini VIMS, all of which indicate abundant fluids may be present, at least periodically, at Titan's equatorial latitudes. Terrestrial observations and studies demonstrate dunes can exist and migrate in conditions of high humidity. Active dunes are found in humid climates, indicating the movement of sand is not always prohibited by the presence of fluids. Sand mobility is related to precipitation, evaporation and wind speed and direction. If dune surfaces become wetted by rainfall or rising subsurface fluids, they can become immobilized. However, winds can act to dry the uppermost layers, freeing sands for saltation and enabling dune migration in wet conditions. Active dunes are found in tropical NE Brazil and NE Australia, where there are alternating dry and wet periods, a condition possible for Titan's tropics. Rising and falling water levels lead to the alteration of dune forms, mainly from being anchored by vegetation, but also from cementation by carbonates or clays. Studies of Titan's dunes, which could undergo anchoring of organic sediments by hydrocarbon fluids, could inform the relative strength of vegetation vs. cementation at humid dune regions on Earth. Furthermore, a comprehensive survey of dune morphologies near regions deemed low by SARTopo and stereo, where liquids may collect in wet conditions, could reveal if bodies of liquid have recently existed at Titan's tropics.

  6. Bismuth Sodium Titanate Based Materials for Piezoelectric Actuators.

    Science.gov (United States)

    Reichmann, Klaus; Feteira, Antonio; Li, Ming

    2015-12-04

    The ban of lead in many electronic products and the expectation that, sooner or later, this ban will include the currently exempt piezoelectric ceramics based on Lead-Zirconate-Titanate has motivated many research groups to look for lead-free substitutes. After a short overview on different classes of lead-free piezoelectric ceramics with large strain, this review will focus on Bismuth-Sodium-Titanate and its solid solutions. These compounds exhibit extraordinarily high strain, due to a field induced phase transition, which makes them attractive for actuator applications. The structural features of these materials and the origin of the field-induced strain will be revised. Technologies for texturing, which increases the useable strain, will be introduced. Finally, the features that are relevant for the application of these materials in a multilayer design will be summarized.

  7. Organic chemistry on Titan: Surface interactions

    Science.gov (United States)

    Thompson, W. Reid; Sagan, Carl

    1992-01-01

    The interaction of Titan's organic sediments with the surface (solubility in nonpolar fluids) is discussed. How Titan's sediments can be exposed to an aqueous medium for short, but perhaps significant, periods of time is also discussed. Interactions with hydrocarbons and with volcanic magmas are considered. The alteration of Titan's organic sediments over geologic time by the impacts of meteorites and comets is discussed.

  8. Modeling the Chemical Complexity in Titan's Atmosphere

    Science.gov (United States)

    Vuitton, Veronique; Yelle, Roger; Klippenstein, Stephen J.; Horst, Sarah; Lavvas, Panayotis

    2018-06-01

    Titan's atmospheric chemistry is extremely complicated because of the multiplicity of chemical as well as physical processes involved. Chemical processes begin with the dissociation and ionization of the most abundant species, N2 and CH4, by a variety of energy sources, i.e. solar UV and X-ray photons, suprathermal electrons (reactions involving radicals as well as positive and negative ions, all possibly in some excited electronic and vibrational state. Heterogeneous chemistry at the surface of the aerosols could also play a significant role. The efficiency and outcome of these reactions depends strongly on the physical characteristics of the atmosphere, namely pressure and temperature, ranging from 1.5×103 to 10-10 mbar and from 70 to 200 K, respectively. Moreover, the distribution of the species is affected by molecular diffusion and winds as well as escape from the top of the atmosphere and condensation in the lower stratosphere.Photochemical and microphysical models are the keystones of our understanding of Titan's atmospheric chemistry. Their main objective is to compute the distribution and nature of minor chemical species (typically containing up to 6 carbon atoms) and haze particles, respectively. Density profiles are compared to the available observations, allowing to identify important processes and to highlight those that remain to be constrained in the laboratory, experimentally and/or theoretically. We argue that positive ion chemistry is at the origin of complex organic molecules, such as benzene, ammonia and hydrogen isocyanide while neutral-neutral radiative association reactions are a significant source of alkanes. We find that negatively charged macromolecules (m/z ~100) attract the abundant positive ions, which ultimately leads to the formation of the aerosols. We also discuss the possibility that an incoming flux of oxygen from Enceladus, another Saturn's satellite, is responsible for the presence of oxygen-bearing species in Titan's reductive

  9. Solvent extraction of tricomponent complexes of zirconium and scandium with salicylic acid and collidine

    International Nuclear Information System (INIS)

    Kochetkova, S.K.; Fadeeva, V.I.; Kalistratova, V.P.

    1976-01-01

    Extraction of tricomponent compounds of zirconium and scandium with salicylic acid (Sal) and collidine (Col) has been studied. Addition of Col widens considerably the pH range of maximum extraction of zirconium salicylate and makes it possible to extract quantitatively both zirconium and scandium in the following pH range: scandium at pH 3.8-5.2; zirconium at pH 2-4. Optimum concentrations of salicylic acid and collidine are 0.05 mol/l and 0.375 mol/l, respectively. The composition of the complexes being extracted has been studied by the shift equilibrium method. Chloroform extracts complexes having the ratio Zr:Sal:Col=1:2:1(pH=3); Sc:Sal:Col=1:3:1(pH=4), and 1:2:1(pH=5). The composition of the complexes being formed is assumed to be [Zr(OH) 3 (HSal) 2 ] - [ColH + ] (pH=3); Sc(HSal) 3 xCol (pH=4.0); Sc(OH)(HSal) 2 xCol (pH=5.0). Extraction of collidine-salicylate complexes of Hf, Th, La, and Y under the conditions of optimum extraction of zirconium and scandium has been investigated when concentration of Zr and Sc in the solution is 3.0.10μ- 5 -1.37.10 -4 mol/l, respectively. It has been shown that hafnium is extracted quantitatively (95-100%) at pH 2.3-4.6; thorium at pH 3.0-6.4; 60% of yttrium is extracted at pH 4.0-4.8; 25% of lanthanum is extracted at pH 3.3-4.9. At pH 2.0 it is possible to separate Zr from Sc,Y, and La; at pH 1.4-1.5 from small amounts of Hf and Tn. Separation of zirconium, from small amounts of hafnium, 10-fold amounts of thorium, 100-fold amounts of scandium and lanthanum is also possible

  10. Solvent extraction of tricomponent complexes of zirconium and scandium with salicylic acid and collidine

    Energy Technology Data Exchange (ETDEWEB)

    Kochetkova, S K; Fadeeva, V I; Kalistratova, V P [Moskovskij Gosudarstvennyj Univ. (USSR)

    1976-01-01

    Extraction of tricomponent compounds of zirconium and scandium with salicylic acid (Sal) and collidine (Col) has been studied. Addition of Col widens considerably the pH range of maximum extraction of zirconium salicylate and makes it possible to extract quantitatively both zirconium and scandium in the following pH range: scandium at pH 3.8-5.2; zirconium at pH 2-4. Optimum concentrations of salicylic acid and collidine are 0.05 mol/l and 0.375 mol/l, respectively. The composition of the complexes being extracted has been studied by the shift equilibrium method. Chloroform extracts complexes having the ratio Zr:Sal:Col=1:2:1(pH=3); Sc:Sal:Col=1:3:1(pH=4), and 1:2:1(pH=5). The composition of the complexes being formed is assumed to be (Zr(OH)/sub 3/(HSal)/sub 2/)/sup -/(ColH/sup +/) (pH=3); Sc(HSal)/sub 3/xCol (pH=4.0); Sc(OH)(HSal)/sub 2/xCol (pH=5.0). Extraction of collidine-salicylate complexes of Hf, Th, La, and Y under the conditions of optimum extraction of zirconium and scandium has been investigated when concentration of Zr and Sc in the solution is 3.0.10..mu..-/sup 5/-1.37.10/sup -4/ mol/l, respectively. It has been shown that hafnium is extracted quantitatively (95-100%) at pH 2.3-4.6; thorium at pH 3.0-6.4; 60% of yttrium is extracted at pH 4.0-4.8; 25% of lanthanum is extracted at pH 3.3-4.9. At pH 2.0 it is possible to separate Zr from Sc,Y, and La; at pH 1.4-1.5 from small amounts of Hf and Tn. Separation of zirconium, from small amounts of hafnium, 10-fold amounts of thorium, 100-fold amounts of scandium and lanthanum is also possible.

  11. Diurnal variations of Titan's ionosphere

    Science.gov (United States)

    Cui, J.; Galand, M.; Yelle, R. V.; Vuitton, V.; Wahlund, J.-E.; Lavvas, P. P.; Müller-Wodarg, I. C. F.; Cravens, T. E.; Kasprzak, W. T.; Waite, J. H.

    2009-06-01

    We present our analysis of the diurnal variations of Titan's ionosphere (between 1000 and 1300 km) based on a sample of Ion Neutral Mass Spectrometer (INMS) measurements in the Open Source Ion (OSI) mode obtained from eight close encounters of the Cassini spacecraft with Titan. Although there is an overall ion depletion well beyond the terminator, the ion content on Titan's nightside is still appreciable, with a density plateau of ˜700 cm-3 below ˜1300 km. Such a plateau is a combined result of significant depletion of light ions and modest depletion of heavy ones on Titan's nightside. We propose that the distinctions between the diurnal variations of light and heavy ions are associated with their different chemical loss pathways, with the former primarily through “fast” ion-neutral chemistry and the latter through “slow” electron dissociative recombination. The strong correlation between the observed night-to-day ion density ratios and the associated ion lifetimes suggests a scenario in which the ions created on Titan's dayside may survive well to the nightside. The observed asymmetry between the dawn and dusk ion density profiles also supports such an interpretation. We construct a time-dependent ion chemistry model to investigate the effect of ion survival associated with solid body rotation alone as well as superrotating horizontal winds. For long-lived ions, the predicted diurnal variations have similar general characteristics to those observed. However, for short-lived ions, the model densities on the nightside are significantly lower than the observed values. This implies that electron precipitation from Saturn's magnetosphere may be an additional and important contributor to the densities of the short-lived ions observed on Titan's nightside.

  12. Calorimetric measurements on hafnium titanate

    International Nuclear Information System (INIS)

    Kandan, R.; Prabhakara Reddy, B.; Panneerselvam, G.; Nagarajan, K.

    2012-01-01

    Owing to its desirable nuclear and mechanical properties such as good absorption cross-section for thermal neutrons (105 barns), hafnium titanate (HfTiO 4 ) finds application as control rods for nuclear reactors. An accurate knowledge of the thermo physical properties of this material is necessary for design of control rod and for modeling its performance. Heat capacity is an important thermodynamic property that determines the temperature dependent variation of all other thermodynamic properties. Hence enthalpy increments of hafnium titanate (HfTiO 4 ) were measured in the temperature range 803-1663 K by employing the method of inverse drop calorimetry using high temperature differential calorimeter

  13. Titan's hydrodynamically escaping atmosphere

    Science.gov (United States)

    Strobel, Darrell F.

    2008-02-01

    The upper atmosphere of Titan is currently losing mass at a rate ˜(4-5)×10 amus, by hydrodynamic escape as a high density, slow outward expansion driven principally by solar UV heating by CH 4 absorption. The hydrodynamic mass loss is essentially CH 4 and H 2 escape. Their combined escape rates are restricted by power limitations from attaining their limiting rates (and limiting fluxes). Hence they must exhibit gravitational diffusive separation in the upper atmosphere with increasing mixing ratios to eventually become major constituents in the exosphere. A theoretical model with solar EUV heating by N 2 absorption balanced by HCN rotational line cooling in the upper thermosphere yields densities and temperatures consistent with the Huygens Atmospheric Science Investigation (HASI) data [Fulchignoni, M., and 42 colleagues, 2005. Nature 438, 785-791], with a peak temperature of ˜185-190 K between 3500-3550 km. This model implies hydrodynamic escape rates of ˜2×10 CHs and 5×10 Hs, or some other combination with a higher H 2 escape flux, much closer to its limiting value, at the expense of a slightly lower CH 4 escape rate. Nonthermal escape processes are not required to account for the loss rates of CH 4 and H 2, inferred by the Cassini Ion Neutral Mass Spectrometer (INMS) measurements [Yelle, R.V., Borggren, N., de la Haye, V., Kasprzak, W.T., Niemann, H.B., Müller-Wodarg, I., Waite Jr., J.H., 2006. Icarus 182, 567-576].

  14. Interaction of Titan's atmosphere with Saturn's magnetosphere

    International Nuclear Information System (INIS)

    Hartle, R.E.

    1985-01-01

    The Voyager 1 measurements made during the Titan flyby reveal that Saturn's rotating magnetospheric plasma interacts directly with Titan's neutral atmosphere and ionosphere. This results from the lack of an intrinsic magnetic field at Titan. The interaction induces a magnetosphere which deflects the flowing plasma around Titan and forms a plasma wake downstream. Within the tail of the induced magnetosphere, ions of ionospheric origin flow away from Titan. Just outside Titan's magnetosphere, a substantial ion-exosphere forms from an extensive hydrogen-nitrogen exosphere. The exospheric ions are picked up and carried downstream into the wake by the plasma flowing around Titan. Mass loading produced by the addition of exospheric ions slows the wake plasma down considerably in the vicinity of the magnetopause. 36 references

  15. Barium titanate coated with magnesium titanate via fused salt method and its dielectric property

    International Nuclear Information System (INIS)

    Chen Renzheng; Cui Aili; Wang Xiaohui; Li Longtu

    2003-01-01

    Barium titanate fine particles were coated homogeneously with magnesium titanate via the fused salt method. The thickness of the magnesium titanate film is 20 nm, as verified by TEM and XRD. The mechanism of the coating is that: when magnesium chloride is liquated in 800 deg. C, magnesium will replace barium in barium titanate, and form magnesium titanate film on the surface of barium titanate particles. Ceramics sintered from the coated particles show improved high frequency ability. The dielectric constant is about 130 at the frequency from 1 to 800 MHz

  16. Hardening mechanisms of spray formed Al-Zn-Mg-Cu alloys with scandium and other elemental additions

    International Nuclear Information System (INIS)

    Sharma, M.M.; Amateau, M.F.; Eden, T.J.

    2006-01-01

    The hardening mechanisms in spray formed Al-Zn-Mg-Cu alloys with additions of chromium, zinc and scandium were studied. The microstructure of the spray formed alloys was analyzed by transmission electron microscopy. A range of tensile strengths were achieved, and varied based on elemental additions, and second phase particle strengthening. To explain the significantly higher strength in one alloy with scandium, theoretical results due to the yield stress of Al-Zn-Mg-Cu alloys as a function of volume fraction and precipitate particle size, were compared to experimental data. Both the possibilities of coherency and order strengthening are examined. The significant additional hardening achieved in the alloy with scandium is attributed to small ordered particles of Al 3 Sc, which precipitated during aging

  17. Organic chemistry in Titan's atmosphere

    Science.gov (United States)

    Scattergood, T.

    1982-01-01

    Laboratory photochemical simulations and other types of chemical simulations are discussed. The chemistry of methane, which is the major known constituent of Titan's atmosphere was examined with stress on what can be learned from photochemistry and particle irradiation. The composition of dust that comprises the haze layer was determined. Isotope fractionation in planetary atmospheres is also discussed.

  18. The influence of the diluent nature on scandium extraction by the phenol-formaldehyde resol oligomer yarrezin B

    International Nuclear Information System (INIS)

    Semenov, S.A.; Valkina, E.M.; Reznik, A.M.

    1996-01-01

    The paper studies the effect of diluent nature on scandium extraction by Yarrezin B phenol-formaldehyde resol oligomer using n-octan, toluene, chloroform, n-octanol and kerosene as an example. Correlation coefficients of dependences of scandium distribution factor on some parameters of diluents are calculated. Possibility to use some parameters of diluents to predict their effect on extraction indices is determined. Hildebrandt solubility parameter of extracting agent and parameters of extracting agent-diluent interaction according to Flory-Haggins are calculated. 13 refs., 2 figs., 4 tabs

  19. Determination of aluminium, scandium and rare earth elements by emission flame spectrometry

    International Nuclear Information System (INIS)

    Otruba, V.; Sommer, L.

    1989-01-01

    Emission spectrometry in nitrous oxide-acetylene flames in combination with a highly resolving double monochromator and sensitive detecting system enables simple, sensitive and selective determinations of aluminium, scandium and all rare earth elements with exception of cerium in complicated matrices. Calibration plots are linear for a large concentration interval (≤ 100 μgxml -1 ), detection limits are in ngxml -1 level and RSD does not exceed 3% on the optimal concentration level of the particular element. The determination of Al, Sc, Eu and Yb showed particular advantages as to methods using ICP-spectrometry. (orig.)

  20. 3He release characteristics of metal tritides and scandium--tritium solid solutions

    International Nuclear Information System (INIS)

    Perkins, W.G.; Kass, W.J.; Beavis, L.C.

    1975-01-01

    Tritides of such metals as scandium, titanium, and erbium are useful materials for determining the effects of helium accumulation in metallic solids, for example, CTR first wall materials. Such effects include lattice strain and gross deformation, as reported elsewhere, which are related to 3 He retention and ultimate release. Long term gas release studies have indicated that, during the early life of a metal ditritide, a large fraction of the 3 He is retained in the solid. At more advanced ages (2 to 4 years, depending on the parent metal), the 3 He release rate becomes comparable to the generation rate. Statistical analysis of the data indicates that the acceleration in 3 He release rate depends on accumulated 3 He concentration rather than strictly on age. 3 He outgassing results are presented for thin films of ScT 2 , TiT 2 , and ErT 2 , and the critical 3 He concentrations are discussed in terms of a percolation model. Phase transformations which occur on tritide formation cast some doubt on the validity of extrapolating results obtained for metal tritides to predictions regarding the accumulation of helium in metals. Scandium is unique among the early transition and rare-earth metals in that the metal exhibits a very high room temperature tritium solubility (T/Sc = 0.4) with no phase transformation. Indeed, even the lattice parameters of the hcp scandium lattice are only minimally changed by tritium solution, and we have succeeded in obtaining single crystal ScT 0 . 3 samples in two crystallographic orientations. Using a very sensitive technique, we have measured 3 He emission from both these samples, as well as from fine-grained thin film scandium-tritium solid solution samples (ScT 0 . 3 - 0 . 4 ). The fine-grained film samples release 3 He at 2 to 3 percent of the generation rate, while the emission rate from the single-crystal samples is approximately 0.05 percent of the generation rate, indicating a strong grain size effect

  1. Scandium-doped zinc cadmium oxide as a new stable n-type oxide thermoelectric material

    DEFF Research Database (Denmark)

    Han, Li; Christensen, Dennis Valbjørn; Bhowmik, Arghya

    2016-01-01

    Scandium-doped zinc cadmium oxide (Sc-doped ZnCdO) is proposed as a new n-type oxide thermoelectric material. The material is sintered in air to maintain the oxygen stoichiometry and avoid instability issues. The successful alloying of CdO with ZnO at a molar ratio of 1 : 9 significantly reduced...... is a good candidate for improving the overall conversion efficiencies in oxide thermoelectric modules. Meanwhile, Sc-doped ZnCdO is robust in air at high temperatures, whereas other n-type materials, such as Al-doped ZnO, will experience rapid degradation of their electrical conductivity and ZT....

  2. Scandium sorption by immobilized microdispersed forms of phosporus-containing ion exchangers

    International Nuclear Information System (INIS)

    Sokolova, Yu.V.; Kurdyumov, G.M.; Smirnov, A.V.; Mezhirov, M.S.

    1991-01-01

    The possibility to improve considerably kinetics of scandium sorption by phosphate ion exchangers, immobilized into polyacrylonitrile (PAN) fibers, as compared with granular samples of ion exchangers, was shown. The influence of dispersion degree of immobilized ionite particles on sorption rate was studied. It is ascertained that the ionite grinding to the particle size ≤ 52 μm is sufficient for the rate increase by 1-1.5 orders. A lower swelling of the immobilized ion exchanger is its additional advantage as compared with granular form

  3. Amino acidis derived from Titan tholins

    Science.gov (United States)

    Khare, Bishun N.; Sagan, Carl; Ogino, Hiroshi; Nagy, Bartholomew; Er, Cevat

    1986-01-01

    The production of amino acids by acid treatment of Titan tholin is experimentally investigated. The synthesis of Titan tholin and the derivatization of amino acids to N-trifluoroacetyl isopropyl esters are described. The gas chromatography/mass spectroscopy analysis of the Titan tholins reveals the presence of glycine, alpha and beta alainine, and aspartic acid, and the total yield of amino acids is about 0.01.

  4. Titan Montgolfiere Buoyancy Modulation System, Phase I

    Data.gov (United States)

    National Aeronautics and Space Administration — Titan is ideally suited for balloon exploration due to its low gravity and dense atmosphere. Current NASA mission architectures baseline Montgolfiere balloon...

  5. Titan's geoid and hydrology: implications for Titan's geological evolution

    Science.gov (United States)

    Sotin, Christophe; Seignovert, Benoit; Lawrence, Kenneth; MacKenzie, Shannon; Barnes, Jason; Brown, Robert

    2014-05-01

    A 1x1 degree altitude map of Titan is constructed from the degree 4 gravity potential [1] and Titan's shape [2] determined by the Radio Science measurements and RADAR observations of the Cassini mission. The amplitude of the latitudinal altitude variations is equal to 300 m compared to 600 m for the amplitude of the latitudinal shape variations. The two polar caps form marked depressions with an abrupt change in topography at exactly 60 degrees at both caps. Three models are envisaged to explain the low altitude of the polar caps: (i) thinner ice crust due to higher heat flux at the poles, (ii) fossil shape acquired if Titan had higher spin rate in the past, and (iii) subsidence of the crust following the formation of a denser layer of clathrates as ethane rain reacts with the H2O ice crust [3]. The later model is favored because of the strong correlation between the location of the cloud system during the winter season and the latitude of the abrupt change in altitude. Low altitude polar caps would be the place where liquids would run to and eventually form large seas. Indeed, the large seas of Titan are found at the deepest locations at the North Pole. However, the lakes and terrains considered to be evaporite candidates due to their spectral characteristics in the infrared [4,5] seem to be perched. Lakes may have been filled during Titan's winter and then slowly evaporated leaving material on the surface. Interestingly, the largest evaporite deposits are located at the equator in a deep depression 150 m below the altitude of the northern seas. This observation seems to rule out the presence of a global subsurface hydrocarbon reservoir unless the evaporation rate at the equator is faster than the transport of fluids from the North Pole to the equator. This work has been performed at the Jet Propulsion Laboratory, California Institute of Technology, under contract to NASA. [1] Iess L. et al. (2012) Science, doi 10.1126/science.1219631. [2] Lorenz R.D. (2013

  6. Oxidation of scandium thin films on tungsten surface

    International Nuclear Information System (INIS)

    Gorodetskij, D.A.; Martynyuk, A.V.

    1988-01-01

    Presence of Sc on the surface of W in amounts larger than a monolayer coverage leads to a decrease of the work function at the initial oxidation stage, which is attributed to oxygen implantation into the surface layer of the metal. A subsequent oxidation is followed by the formation on the surface of a thin oxide layer and an increase of the work function. An increase of the amount of Sc deposited on the surface before the oxidation decreases the work function of the obtained oxide from 5.8 (clean W surface) down to 3.3 eV (thick Sc layer on W)

  7. Titan from Cassini-Huygens

    CERN Document Server

    Brown, Robert H; Waite, J. Hunter

    2010-01-01

    This book reviews our current knowledge of Saturn's largest moon Titan featuring the latest results obtained by the Cassini-Huygens mission. A global author team addresses Titan’s origin and evolution, internal structure, surface geology, the atmosphere and ionosphere as well as magnetospheric interactions. The book closes with an outlook beyond the Cassini-Huygens mission. Colorfully illustrated, this book will serve as a reference to researchers as well as an introduction for students.

  8. Thermal stability of titanate nanotubes

    Czech Academy of Sciences Publication Activity Database

    Králová, Daniela; Kužel, R.; Kovářová, Jana; Dybal, Jiří; Šlouf, Miroslav

    2009-01-01

    Roč. 16, 2a (2009), s. 41-43 ISSN 1211-5894. [Struktura - Colloquium of Czech and Slovak Crystallographic Association. Hluboká nad Vltavou, 22.06.2009-25.06.2009] R&D Projects: GA ČR GA203/07/0717; GA AV ČR KAN200520704 Institutional research plan: CEZ:AV0Z40500505 Keywords : titanate nanotubes * thermal stability Subject RIV: CD - Macromolecular Chemistry

  9. Formation of titanate nanostructures under different NaOH concentration and their application in wastewater treatment

    International Nuclear Information System (INIS)

    Huang Jiquan; Cao Yongge; Deng Zhonghua; Tong Hao

    2011-01-01

    The effects of the concentration of NaOH on the formation and transformation of various titanate nanostructures were studied. With increasing NaOH concentration, three different formation mechanisms were proposed. Nanotubes can only be obtained under moderate NaOH conditions, and should transform into nanowires with prolonged hydrothermal treatment, and their formation rate is accelerated by increasing NaOH concentration. Low concentration of NaOH results in the direct formation of nanowires, while extra high concentration of NaOH leads to the formation of amorphous nanoparticles. Adsorption and photocatalysis studies show that titanate nanowires and nanotubes might be potential adsorbents for the removal of both heavy metal ions and dyes and photocatalysts for the removal of dyes from wastewater. -- Graphical abstract: The morphologies of the titanates depend deeply on the concentration of NaOH. With increasing NaOH concentration, three different formation mechanisms were proposed. The application of these titanate nanostructures in the wastewater treatment was studied. Display Omitted Research highlights: → Effect of NaOH concentration on the structures of various titanates was reported. → Three different formation mechanisms were presented with increasing NaOH concentration. → Various titanates were used as adsorbents/photocatalysts in wastewater treatment.

  10. Effects of additives on microstructures of titanate based nanotubes prepared by the hydrothermal process

    International Nuclear Information System (INIS)

    Kubo, Takashi; Sugimoto, Keijiro; Onoki, Takamasa; Nakahira, Atsushi; Yamasaki, Yuki

    2009-01-01

    Silica-containing TiO 2 -derived titanate nanotubes were prepared by the addition of a small amount of tetraethyl orthosilicate (TEOS) to TiO 2 -derived titanate nanotubes prepared by the hydrothermal process and a subsequent heat-treatment at 473 K in air. The microstructure and thermal behavior of synthesized silica containing TiO 2 -derived titanate nanotubes were investigated by various methods such as X-ray diffraction (XRD), X-ray absorption fine structure (XAF), and X-ray photoelectron spectroscopy (XPS). As a result, the addition of a small amount of TEOS leaded to the improvement of the thermal stability for TiO 2 -derived titanate nanotubes. XPS results revealed that Si was combined onto the surface of TiO 2 -derived titanate nanotubes, forming partial Si-O-Ti chemical bonds. Therefore, it was inferred that the thermal stability could be modified by forming partial Si-O-Ti chemical bonds at interface of silica and TiO 2 -derived titanate nanotubes. (author)

  11. Experimental studies on 3D printing of barium titanate ceramics for medical applications

    Directory of Open Access Journals (Sweden)

    Schult Mark

    2016-09-01

    Full Text Available The present work deals with the 3D printing of porous barium titanate ceramics. Barium titanate is a biocompatible material with piezoelectric properties. Due to insufficient flowability of the starting material for 3D printing, the barium titanate raw material has been modified in three different ways. Firstly, barium titanate powder has been calcined. Secondly, flow additives have been added to the powder. And thirdly, flow additives have been added to the calcined powder. Finally, a polymer has been added to the three materials and specimens have been printed from these three material mixtures. The 3D printed parts were then sintered at 1320°C. The sintering leads to shrinkage which differs between 29.51–71.53% for the tested material mixtures. The porosity of the parts is beneficial for cell growth which is relevant for future medical applications. The results reported in this study demonstrate the possibility to fabricate porous piezoelectric barium titanate parts with a 3D printer that can be used for medical applications. 3D printed porous barium titanate ceramics can especially be used as scaffold for bone tissue engineering, where the bone formation can be promoted by electrical stimulation.

  12. A Model of Titan-like Chemistry to Connect Experiments and Cassini Observations

    Science.gov (United States)

    Raymond, Alexander W.; Sciamma-O’Brien, Ella; Salama, Farid; Mazur, Eric

    2018-02-01

    A numerical model is presented for interpreting the chemical pathways that lead to the experimental mass spectra acquired in the Titan Haze Simulation (THS) laboratory experiments and for comparing the electron density and temperature of the THS plasma to observations made at Titan by the Cassini spacecraft. The THS plasma is a pulsed glow-discharge experiment designed to simulate the reaction of N2/CH4-dominated gas in Titan's upper atmosphere. The transient, one-dimensional model of THS chemistry tracks the evolution of more than 120 species in the direction of the plasma flow. As the minor species C2H2 and C2H4 are added to the N2/CH4-based mixture, the model correctly predicts the emergence of reaction products with up to five carbon atoms in relative abundances that agree well with measured mass spectra. Chemical growth in Titan's upper atmosphere transpires through ion–neutral and neutral–neutral chemistry, and the main reactions involving a series of known atmospheric species are retrieved from the calculation. The model indicates that the electron density and chemistry are steady during more than 99% of the 300 μs long discharge pulse. The model also suggests that the THS ionization fraction and electron temperature are comparable to those measured in Titan's upper atmosphere. These findings reaffirm that the THS plasma is a controlled analog environment for studying the first and intermediate steps of chemistry in Titan's upper atmosphere.

  13. Numerical simulation of the circulation of the atmosphere of Titan

    Science.gov (United States)

    Hourdin, F.; Levan, P.; Talagrand, O.; Courtin, Regis; Gautier, Daniel; Mckay, Christopher P.

    1992-01-01

    A three dimensional General Circulation Model (GCM) of Titan's atmosphere is described. Initial results obtained with an economical two dimensional (2D) axisymmetric version of the model presented a strong superrotation in the upper stratosphere. Because of this result, a more general numerical study of superrotation was started with a somewhat different version of the GCM. It appears that for a slowly rotating planet which strongly absorbs solar radiation, circulation is dominated by global equator to pole Hadley circulation and strong superrotation. The theoretical study of this superrotation is discussed. It is also shown that 2D simulations systemically lead to instabilities which make 2D models poorly adapted to numerical simulation of Titan's (or Venus) atmosphere.

  14. In situ Sn2+-incorporation synthesis of titanate nanotubes for photocatalytic dye degradation under visible light illumination

    International Nuclear Information System (INIS)

    Tsai, Chien-Cheng; Chen, Liang-Che; Yeh, Te-Fu; Teng, Hsisheng

    2013-01-01

    Highlights: ► Sn 2+ ions sensitize titanate nanotubes for photocatalysis under visible-light illumination. ► The Sn 5s orbital replaces the O 2p orbital as the top level of the valence band of titanates. ► The presence of Sn 2+ lifts the valence band of titanate nanotubes by approximately 0.9 eV. ► The doped Sn 2+ sites are active in donating photo-induced charges to dye degradation. - Abstract: Sn 2+ -incorporated titanate nanotubes, prepared by washing a layered sodium titanate with a SnCl 2 solution for tube formation, exhibit noticeable photocatalytic activity under visible light irradiation. This in situ synthesis results in a Sn/Ti ratio of approximately 0.6. Because of the introduction of Sn 2+ ions, the Sn 5s orbital replaces the O 2p orbital as the top level of the valence band of titanate nanotubes. Optical absorption analysis shows that Sn doping reduces the bandgap of titanate nanotubes from 3.5 to 2.6 eV. Oxidation of the Sn 2+ -incorporated titanate nanotubes leads to oxidation of Sn 2+ to Sn 4+ , hence, widening the bandgap. Under visible light irradiation, Sn 2+ -incorporated titanate nanotubes effectively degrade methylene blue in an aqueous solution, whereas the bare titanate nanotubes exhibit substantially lower photocatalytic activity. Photoluminescence analysis demonstrates that the induced charges from excitation of the Sn 2+ ions tend to be relaxed through chemical interactions, rather than irradiative recombination.

  15. The tide in the seas of Titan

    International Nuclear Information System (INIS)

    Sagan, C.; Dermott, S.F.

    1982-01-01

    It is argued that, if Titan has oceans consisting of liquid methane, then the present high eccentricity of the satellite necessitates that the depth would be greater than 400 m. Such an ocean should be detectable by radar. The effects of tidal dissipation due to the possible existence of an ocean on Titan are considered. (author)

  16. Geodetic data support trapping of ethane in Titan's polar crust

    Science.gov (United States)

    Sotin, Christophe; Rambaux, Nicolas

    2016-04-01

    Titan's surface is characterized by polar depressions that strongly influence interpretations of the gravity data. This study investigates several geodynamical models that can explain these depressions. For each model, the values of the three moments of inertia are computed numerically by discretizing the interior in spherical coordinates. The study shows that a Pratt model where the polar subsurface is made of ethane clathrates can explain the polar depression, the abrupt jump in altitude at about 60 degrees latitude, and the values of the degree 2 gravity coefficients. This model, proposed by Choukroun and Sotin [1], is based on the stability of ethane clathrate hydrates relative to methane clathrate hydrates. In addition to fitting the geodetic data, it explains the absence of ethane in Titan's atmosphere although ethane is the main product of the photolysis of methane. Other geophysical models based on latitudinal variations in the tidal heating production or in the heat flux at the base of the icy crust do not provide such a good match to the gravity and topographic observations. The ethane-clathrate model predicts that all the ethane produced by photolysis of methane at the present rate during the last billion years could be stored in the polar subsurface. It is consistent with the age of Titan's surface and that of Titan's atmospheric methane inferred from geological and geochemical observations by the Cassini/Huygens mission. The present study also emphasizes the role of mass anomalies on the interpretation of the degree 2 gravity coefficients. It shows that for Titan, a slow rotator, the values of the two equatorial moments of inertia (MoI) are largely affected by the polar depressions whereas the value of polar MoI is not. Therefore, as pointed out by previous calculations [2], calculating the moment of inertia (MoI) factor from the value of J2 could lead to major errors. This is not the case for our preferred Titan's model for which the negative polar

  17. This is Commercial Titan Inc.

    Science.gov (United States)

    Van Rensselaer, F. L.; Slovikoski, R. D.; Abels, T. C.

    Out of a quarter-century heritage of eminently successful expendable launch vehicle history with the U.S. government, a commercial launch services enterprise which challenges the corporation as well as the competition has been launched within the Martin Marietta Corporation. This paper is an inside look at the philosophy, structure, and success of the new subsidiary, Commercial Titan Inc., which is taking on its U.S. and foreign rocket-making competitors to win a share of the international communication satellite market as well as the U.S. government commercial launch services market.

  18. Why does the lumen maintenance of sodium-scandium metal halide lamps improve by VHF operation?

    International Nuclear Information System (INIS)

    Van Erk, W; Luijks, G M J F; Hitchcock, W

    2011-01-01

    Lifetime experiments show that sodium-scandium metal halide lamps perform better on very high frequency (VHF) drivers than on low frequency (LF) constant wattage autotransformer (CWA) ballasts. The question why, will be addressed with focus on arc tube aspects. It is argued that at high frequency operation sodium loss is less, and that the absence of thermal fluctuations in the electrode tip causes less damage and cracking to this part of the electrode. Sudden lm W -1 drops, observed with CWA-operated lamps, most probably occur when the arc attaches on such a corroded and cracked surface. Thorium is effective as an emitter both in the CWA and the VHF operation mode, despite the absence of cataphoretic transport to the cathode in the VHF case.

  19. Why does the lumen maintenance of sodium-scandium metal halide lamps improve by VHF operation?

    Energy Technology Data Exchange (ETDEWEB)

    Van Erk, W [Philips Lighting, Sondervick 47, 5505 NB Veldhoven (Netherlands); Luijks, G M J F [Advanced Development Lighting, Philips Lighting, PO Box 80020, 5600 JM Eindhoven (Netherlands); Hitchcock, W, E-mail: Gerard.luijks@philips.com [Philips Lighting Company, 7265 Route 54, Bath, NY 14810 (United States)

    2011-06-08

    Lifetime experiments show that sodium-scandium metal halide lamps perform better on very high frequency (VHF) drivers than on low frequency (LF) constant wattage autotransformer (CWA) ballasts. The question why, will be addressed with focus on arc tube aspects. It is argued that at high frequency operation sodium loss is less, and that the absence of thermal fluctuations in the electrode tip causes less damage and cracking to this part of the electrode. Sudden lm W{sup -1} drops, observed with CWA-operated lamps, most probably occur when the arc attaches on such a corroded and cracked surface. Thorium is effective as an emitter both in the CWA and the VHF operation mode, despite the absence of cataphoretic transport to the cathode in the VHF case.

  20. Influence of scandium on the microstructure and mechanical properties of A319 alloy

    International Nuclear Information System (INIS)

    Emadi, Daryoush; Rao, A.K. Prasada; Mahfoud, Musbah

    2010-01-01

    Recycling of aluminum scrap alloys by melting is gaining its importance in foundry sector. During recycling, some of the alloying elements present in scrap alloys eventually become trace/tramp impurities in the recycled alloy. These elements could potentially affect the alloy's microstructure and hence its mechanical properties. In the present work, an attempt has been made to investigate the effect of one of such trace elements on the microstructure and mechanical properties of A319 alloy. The element chosen for the present investigation is scandium (Sc). This paper discusses the effects of the additions of trace amount of Sc on the microstructure and mechanical properties of A319 alloy in as-cast, T6 and T7 heat treated conditions.

  1. Thermodynamic study of sublimation, melting and vaporization of scandium(III) dipivaloylmethanate derivatives

    International Nuclear Information System (INIS)

    Zherikova, Kseniya V.; Zelenina, Ludmila N.; Chusova, Tamara P.; Gelfond, Nikolay V.; Morozova, Natalia B.

    2016-01-01

    Highlights: • Thermal properties of two volatile fluorinated Sc(III) beta-diketonates were studied. • Saturated and unsaturated vapor pressures were measured. • DSC analysis was carried out. • Sublimation, evaporation and melting enthalpies and entropies were derived. • Effect of fluorine introduction on volatility and thermal stability was established. - Abstract: The present work deals with the investigation of thermal properties of two volatile scandium(III) beta-diketonates with 2,2,6,6-tetramethyl-4-fluoro-3,5-heptanedione and 1,1,1-trifluoro-5,5-dimethyl-2,4-hexanedione which have been synthesized and purified. Using the static method with glass membrane gauge-manometer the temperature dependencies of saturated and unsaturated vapor pressure were measured for the first time. The temperatures and enthalpies of melting were measured for these compounds by differential scanning calorimetry. The standard thermodynamic characteristics of enthalpy and entropy for sublimation, vaporization and melting processes were derived.

  2. Dielectric matrix, dynamical matrix and phonon dispersion in hcp transition metal scandium

    International Nuclear Information System (INIS)

    Singh, Joginder; Singh, Natthi; Prakash, S.

    1976-01-01

    Complete dielectric matrix is evaluated for hcp transition metal scandium using the non-interacting s- and d-band model. The local field corrections which are consequence of the non-diagonal part of the dielectric matrix are calculated explicitly. The free electron approximation is used for the s-electrons and the simple tight-binding approximation is used for the d-electrons. The theory developed by Singh and others is used to invert the dielectric matrix and the explicit expressions for the dynamical matrix are obtained. The phonon dispersion relations are investigated by using the renormalized Animalu transition metal model potential (TMMP) for bare ion potential. The contribution due to non-central forces which arise due to local fields is found to be 20%. The results are found in resonably good agreement with the experimental values. (author)

  3. Bottom sediment transport study at Haiphong port using radioactive scandium as tracer

    International Nuclear Information System (INIS)

    Pham Ngoc Chuong; Phan Son Hai; Pham Duy Hien

    1993-01-01

    A radioisotope tracer experiment was performed for investigating the bedload movement at the site near the access channel to Haiphong port, North Vietnam. The scandium glass and a number of mechanical devices were manufactured locally for the experiment. Simple and safe procedures were adopted for the production, transportation and injection of radioactive tracer materials. Five tracking experiments were carried out covering the period of 84 days in winter 1992-1993. The experimental results provide a firm basis for elaborating appropriate measures against the siltation problem at Haiphong port, especially for the design of a new access channel with a better orientation with respect to the directions of the water flow and bedload transport, as proposed recently by the Port Authority. (Author). 2 refs, 4 figs

  4. Study of barium bismuth titanate prepared by mechanochemical synthesis

    Directory of Open Access Journals (Sweden)

    Lazarević Z.Ž.

    2009-01-01

    Full Text Available Barium-bismuth titanate, BaBi4Ti4O15 (BBT, a member of Aurivillius bismuth-based layer-structure perovskites, was prepared from stoichiometric amounts of barium titanate and bismuth titanate obtained via mechanochemical synthesis. Mechanochemical synthesis was performed in air atmosphere in a planetary ball mill. The reaction mechanism of BaBi4Ti4O15 and the preparation and characteristics of BBT ceramic powders were studied using XRD, Raman spectroscopy, particle analysis and SEM. The Bi-layered perovskite structure of BaBi4Ti4O15 ceramic forms at 1100 °C for 4 h without a pre-calcination step. The microstructure of BaBi4Ti4O15 exhibits plate-like grains typical for the Bi-layered structured material and spherical and polygonal grains. The Ba2+ addition leads to changes in the microstructure development, particularly in the change of the average grain size.

  5. Partially collisional model of the Titan hydrogen torus

    International Nuclear Information System (INIS)

    Hilton, D.A.

    1987-01-01

    A numerical model was developed for atomic hydrogen densities in the Titan hydrogen torus. The effects of occasional collisions were included in order to accurately simulate physical conditions inferred from the Voyager 1 and 2 Ultraviolet Spectrometer (UVS) results of Broadfoot et al. (1981) and Sandel et al. (1982). The model employed Lagrangian perturbation of orbital elements of hydrogen atoms launched from Titan and Monte Carlo simulation of collisions and loss mechanisms. The torus is found to be azimuthally symmetric with the density sharply peaked at Titan's orbit, and decreasing rapidly in the outward and perpendicular directions and more gradually inward from 17 to 5 R/sub s/. The energetic hydrogen atoms from Saturn's upper atmosphere, first predicted by Shemansky and Smith (1982), were also investigated. Collisions of these Saturnian atoms with the torus population do not contribute to the torus density, and will lead to a net loss of torus atoms if their launch speeds from Saturn extend above 40 km/sec. The Saturnian atoms produce a corona which was modeled using the theory of Chamberlain (1963)

  6. Modification mechanism of eutectic silicon in Al–6Si–0.3Mg alloy with scandium

    Energy Technology Data Exchange (ETDEWEB)

    Patakham, Ussadawut [Manufacturing and Systems Engineering Program, Department of Production Engineering, Faculty of Engineering, King Mongkut’s University of Technology Thonburi, 126 Pracha-Utid Rd., Bangmod, Tungkhru, Bangkok 10140 (Thailand); Kajornchaiyakul, Julathep [National Metal and Material Technology Center, National Science and Technology Development Agency, 114 Thailand Science Park, Klong Nueng, Klong Luang, Pathumthani 12120 (Thailand); Limmaneevichitr, Chaowalit, E-mail: chaowalit.lim@kmutt.ac.th [Manufacturing and Systems Engineering Program, Department of Production Engineering, Faculty of Engineering, King Mongkut’s University of Technology Thonburi, 126 Pracha-Utid Rd., Bangmod, Tungkhru, Bangkok 10140 (Thailand)

    2013-10-25

    Highlights: •Morphologies and growth of Sc and Sr-modified eutectic silicon resemble those of dendrites. •Crystal orientation of eutectic aluminum depends on growth characteristics of eutectic silicon. •We report strong evidence of the occurrence of an impurity-induced twinning mechanism. -- Abstract: The modification mechanism of eutectic silicon in Al–6Si–0.3Mg alloy with scandium was studied. The crystallographic orientation relationships between primary dendrites and the eutectic phase of unmodified and modified Al–6Si–0.3 Mg alloys were determined using electron backscatter diffraction (EBSD). The orientation of aluminum modified with scandium in the eutectic phase was different from that of the neighboring primary dendrites. This result implies that eutectic aluminum grows epitaxially from the surrounding primary aluminum dendrites in the unmodified alloy and that eutectic aluminum grows competitively from the surrounding primary aluminum dendrites in the modified alloy. The pole figure maps of eutectic Si in the [1 0 0], [1 1 0] and [1 1 1] axes of the unmodified and Sc-modified alloys were different, suggesting that the eutectic Al and Si crystals in modified alloy growth are more isotropic and cover a larger set of directions. The lattice fringes of Si of the alloys with and without Sc modification were different in the TEM results. The lattice fringes of Si in modified alloy were found to be multiple twins. However, this was not observed in the unmodified alloy. The growth characteristic of eutectic Si crystal in modified alloy suggests the occurrence of multiple twinning reactions and the formation of a high density of twins. This modification mechanism by Sc is explained by the results of scanning electron microscopy (SEM), electron backscatter diffraction (EBSD) and transmission electron microscopy (TEM) analysis, which provide strong evidence of the occurrence of the impurity-induced twinning (IIT) mechanism.

  7. Insights into the mantle geochemistry of scandium from a meta-analysis of garnet data

    Science.gov (United States)

    Chassé, Mathieu; Griffin, William L.; Alard, Olivier; O'Reilly, Suzanne Y.; Calas, Georges

    2018-06-01

    The meta-analysis of about 13,000 analyses of scandium content in garnet grains shows that, below the spinel-garnet transition, this phase carries about three-quarters of the Sc budget of the mantle, indicating its control on Sc mobility. The Sc content of garnets in mafic rocks is low, due to a dilution effect resulting from their high modal content in garnet. Garnets from ultramafic rocks exhibit a wider range of Sc concentrations. We assess the relative influence of thermobarometry, crystal chemistry and fluid-related events on the distribution of Sc in garnet from such rocks to improve the tracking of geochemical processes in the mantle. Pressure and temperature of equilibration in the mantle are second-order factors influencing the Sc content of garnet, while crystal chemistry, in particular Cr/Cr+Al and Ca/Ca+Mg, is the main parameter controlling the compatibility of Sc. Scandium is incorporated in both X and Y sites of Cr-Ca-rich garnets, resulting in a behaviour intermediate between rare-earth elements, incorporated in the X site, and trivalent transition elements, occupying the Y site. This affinity for both sites results in a mild compatibility of Sc in the garnet stability field of the mantle; hence Sc concentration in garnet increases with melt extraction and can be reduced by silicate-melt metasomatism. In contrast, metasomatism by volatile-rich fluids increases the Sc concentration in garnet. The control of garnet on the compatibility of Sc in deep lithospheric rocks demonstrates the potential of using Sc to track the conditions of formation of magmas and their residual rocks, as well as the origin and nature of metasomatic fluids.

  8. Photoreactivity of condensed species in Titan lower atmosphere

    Science.gov (United States)

    Fleury, Benjamin; Gudipati, Murthy; Couturier-Tamburelli, Isabelle; Carrasco, Nathalie

    2017-10-01

    Photochemical processes initiated in the thermosphere of Titan at about 1000 km by the dissociation and the ionization of N2 and CH4 by the VUV solar photons [1] lead to the formation of a number of hydrocarbons and nitriles species. Some of these species can condense in the troposphere and the lower stratosphere of Titan ( 300 nm) can reach these lower atmospheric layers [4], ongoing possible further solid-state chemistry as demonstrated experimentally [5]. We will present here an experimental study simulating the reactivity of ices in the atmosphere of Titan and will discuss the photoreactivity occurring in the lower atmospheric layers of Titan despite the absorption of the most energetic photons.AcknowledgmentsThis work is supported by NASA Solar System Workings grant " Photochemistry in Titan’s Lower Atmosphere". The research work has been carried out at the Jet Propulsion Laboratory, California Institute of Technology under a contract with the National Aeronautics and Space Administration. NC acknowledges the European Research Council for their financial support (ERC Starting Grant PRIMCHEM, grant agreement n°636829).References[1] Waite, J. H., et al., The process of Tholin formation in Titan’s upper atmosphere, (2007), Science 316, 870-875.[2] Barth, E. L., Modeling survey of ices in Titan’s stratosphere, (2017), Planetary and Space Science 137, 20-31.[3] Fulchignoni, M., et al., In situ measurements of the physical characteristics of Titan’s environment, (2005), Nature 438, 785-791.[4] Tomasko, M. G., et al., Rain, winds and haze during the Huygens probe’s descent to Titan’s surface, (2005), Nature 438, 765-778.[5] Gudipati, M. S., et al., Photochemical activity of Titan’s low-altitude condensed haze, (2013), Nature Communications, 4: p1648.

  9. Implications of Wind-Assisted Aerial Navigation for Titan Mission Planning and Science Exploration

    Science.gov (United States)

    Elfes, A.; Reh, K.; Beauchamp, P.; Fathpour, N.; Blackmore, L.; Newman, C.; Kuwata, Y.; Wolf, M.; Assad, C.

    2010-01-01

    The recent Titan Saturn System Mission (TSSM) proposal incorporates a montgolfiere (hot air balloon) as part of its architecture. Standard montgolfiere balloons generate lift through heating of the atmospheric gases inside the envelope, and use a vent valve for altitude control. A Titan aerobot (robotic aerial vehicle) would have to use radioisotope thermoelectric generators (RTGs) for electric power, and the excess heat generated can be used to provide thermal lift for a montgolfiere. A hybrid montgolfiere design could have propellers mounted on the gondola to generate horizontal thrust; in spite of the unfavorable aerodynamic drag caused by the shape of the balloon, a limited amount of lateral controllability could be achieved. In planning an aerial mission at Titan, it is extremely important to assess how the moon-wide wind field can be used to extend the navigation capabilities of an aerobot and thereby enhance the scientific return of the mission. In this paper we explore what guidance, navigation and control capabilities can be achieved by a vehicle that uses the Titan wind field. The control planning approach is based on passive wind field riding. The aerobot would use vertical control to select wind layers that would lead it towards a predefined science target, adding horizontal propulsion if available. The work presented in this paper is based on aerodynamic models that characterize balloon performance at Titan, and on TitanWRF (Weather Research and Forecasting), a model that incorporates heat convection, circulation, radiation, Titan haze properties, Saturn's tidal forcing, and other planetary phenomena. Our results show that a simple unpropelled montgolfiere without horizontal actuation will be able to reach a broad array of science targets within the constraints of the wind field. The study also indicates that even a small amount of horizontal thrust allows the balloon to reach any area of interest on Titan, and to do so in a fraction of the time needed

  10. Chemistry and evolution of Titan's atmosphere

    International Nuclear Information System (INIS)

    Strobel, D.F.

    1982-01-01

    The chemistry and evolution of Titan's atmosphere is reviewed in the light of the scientific findings from the Voyager mission. It is argued that the present N 2 atmosphere may be Titan's initial atmosphere rather than photochemically derived from an original NH 3 atmosphere. The escape rate of hydrogen from Titan is controlled by photochemical production from hydrocarbons. CH 4 is irreversibly converted to less hydrogen rich hydrocarbons, which over geologic time accumulate on the surface to a layer thickness of approximately 0.5 km. Magnetospheric electrons interacting with Titan's exosphere may dissociate enough N 2 into hot, escaping N atoms to remove approximately 0.2 of Titan's present atmosphere over geologic time. The energy dissipation of magnetospheric electrons exceeds solar e.u.v. energy deposition in Titan's atmosphere by an order of magnitude and is the principal driver of nitrogen photochemistry. The environmental conditions in Titan's upper atmosphere are favorable to building up complex molecules, particularly in the north polar cap region. (author)

  11. Titan the earth-like moon

    CERN Document Server

    Coustenis, Athena

    1999-01-01

    This is the first book to deal with Titan, one of the most mysterious bodies in the solar system. The largest satellite of the giant planet Saturn, Titan is itself larger than the planet Mercury, and is unique in being the only known moon with a thick atmosphere. In addition, its atmosphere bears a startling resemblance to the Earth's, but is much colder.The American and European space agencies, NASA and ESA, have recently combined efforts to send a huge robot spacecraft to orbit Saturn and land on Titan. This book provides the background to this, the greatest deep space venture of our time, a

  12. Ceria and strontium titanate based electrodes

    DEFF Research Database (Denmark)

    2010-01-01

    A ceramic anode structure obtainable by a process comprising the steps of: (a) providing a slurry by dispersing a powder of an electronically conductive phase and by adding a binder to the dispersion, in which said powder is selected from the group consisting of niobium-doped strontium titanate......, vanadium-doped strontium titanate, tantalum-doped strontium titanate, and mixtures thereof, (b) sintering the slurry of step (a), (c) providing a precursor solution of ceria, said solution containing a solvent and a surfactant, (d) impregnating the resulting sintered structure of step (b...

  13. The greenhouse and antigreenhouse effects on Titan

    Science.gov (United States)

    Mckay, Christopher P.; Pollack, James B.; Courtin, Regis

    1991-01-01

    The parallels between the atmospheric thermal structure of the Saturnian satellite Titan and the hypothesized terrestrial greenhouse effect can serve as bases for the evaluation of competing greenhouse theories. Attention is presently drawn to the similarity between the roles of H2 and CH4 on Titan and CO2 and H2O on earth. Titan also has an antigreenhouse effect due to a high-altitude haze layer which absorbs at solar wavelengths, while remaining transparent in the thermal IR; if this haze layer were removed, the antigreenhouse effect would be greatly reduced, exacerbating the greenhouse effect and raising surface temperature by over 20 K.

  14. The commercial evolution of the Titan program

    Science.gov (United States)

    Isakowitz, Steven

    1988-07-01

    The present status evaluation of proprietary efforts to turn the once exclusively government-requirements-oriented Titan launch vehicle into a successful commercial competitor is divided into three phases. The first phase notes recent changes in U.S. space transportation policy and the Titan configurations evaluated for commercial feasibility. The second phase is a development history for the current vehicle's marketing organization and the right-to-use agreement for a launch site. Phase three projects the prospective marketing climate for a commercial Titan vehicle and its planned improvements.

  15. Titan's organic chemistry: Results of simulation experiments

    Science.gov (United States)

    Sagan, Carl; Thompson, W. Reid; Khare, Bishun N.

    1992-01-01

    Recent low pressure continuous low plasma discharge simulations of the auroral electron driven organic chemistry in Titan's mesosphere are reviewed. These simulations yielded results in good accord with Voyager observations of gas phase organic species. Optical constants of the brownish solid tholins produced in similar experiments are in good accord with Voyager observations of the Titan haze. Titan tholins are rich in prebiotic organic constituents; the Huygens entry probe may shed light on some of the processes that led to the origin of life on Earth.

  16. TSSM: The in situ exploration of Titan

    Science.gov (United States)

    Coustenis, A.; Lunine, J. I.; Lebreton, J. P.; Matson, D.; Reh, K.; Beauchamp, P.; Erd, C.

    2008-09-01

    The Titan Saturn System Mission (TSSM) mission was born when NASA and ESA decided to collaborate on two missions independently selected by each agency: the Titan and Enceladus mission (TandEM), and Titan Explorer, a 2007 Flagship study. TandEM, the Titan and Enceladus mission, was proposed as an L-class (large) mission in response to ESA's Cosmic Vision 2015-2025 Call. The mission concept is to perform remote and in situ investigations of Titan primarily, but also of Enceladus and Saturn's magentosphere. The two satellites are tied together by location and properties, whose remarkable natures have been partly revealed by the ongoing Cassini-Huygens mission. These bodies still hold mysteries requiring a complete exploration using a variety of vehicles and instruments. TSSM will study Titan as a system, including its upper atmosphere, the interactions with the magnetosphere, the neutral atmosphere, surface, interior, origin and evolution, as well as the astrobiological potential of Titan. It is an ambitious mission because its targets are two of the most exciting and challenging bodies in the Solar System. It is designed to build on but exceed the scientific and technological accomplishments of the Cassini- Huygens mission, exploring Titan and Enceladus in ways that are not currently possible (full close-up and in situ coverage over long periods of time for Titan, several close flybys of Enceladus). One overarching goal of the TSSM mission is to explore in situ the atmosphere and surface of Titan. In the current mission architecture, TSSM consists of an orbiter (under NASA's responsibility) with a large host of instruments which would perform several Enceladus and Titan flybys before stabilizing in an orbit around Titan alone, therein delivering in situ elements (a Montgolfière, or hot air balloon, and a probe/lander). The latter are being studied by ESA. The balloon will circumnavigate Titan above the equator at an altitude of about 10 km for several months. The

  17. Multiscale Study of Hydrogen Adsorption on Six Designed Covalent Organic Frameworks Based on Porphyrazine, Cyclobutane and Scandium

    International Nuclear Information System (INIS)

    Li Le-Le; Gao Teng-Fei; Zhang Ruan-Yu; Zhang Hong

    2014-01-01

    The first-principles method of hydrogen adsorption is used to investigate the interaction of H_2 with the scandium-porphyrazine (Sc-Pz) and porphyrazine (Pz) clusters. The result shows that the interaction of H_2 with Sc-Pz is stronger than with Pz. Then grand canonical Monte Carlo simulations are used to investigate hydrogen adsorption in six designed covalent organic frameworks (COFs), which are designed based on porphyrazine, cyclobutane and scandium. When the pressure is from 0.1 to 100 bar and the temperature is 298 K and 77 K, the hydrogen adsorption capacities of the six COFs are calculated. We further study the importance of Sc and fillers to improve the H_2 uptake in the modified COFs by analyzing the isosteric heat of hydrogen adsorption. (condensed matter: electronic structure, electrical, magnetic, and optical properties)

  18. Titan's Atmospheric Dynamics and Meteorology

    Science.gov (United States)

    Flasar, F. M.; Baines, K. H.; Bird, M. K.; Tokano, T.; West, R. A.

    2008-01-01

    Titan, after Venus, is the second example of an atmosphere with a global cyclostrophic circulation in the solar system, but a circulation that has a strong seasonal modulation in the middle atmosphere. Direct measurement of Titan's winds, particularly observations tracking the Huygens probe at 10degS, indicate that the zonal winds are generally in the sense of the satellites rotation. They become cyclostrophic approx. 35 km above the surface and generally increase with altitude, with the exception of a sharp minimum centered near 75 km, where the wind velocity decreases to nearly zero. Zonal winds derived from the temperature field retrieved from Cassini measurements, using the thermal wind equation, indicate a strong winter circumpolar vortex, with maximum winds at mid northern latitudes of 190 ms-' near 300 km. Above this level, the vortex decays. Curiously, the zonal winds and temperatures are symmetric about a pole that is offset from the surface pole by approx.4 degrees. The cause of this is not well understood, but it may reflect the response of a cyclostrophic circulation to the offset between the equator, where the distance to the rotation axis is greatest, and the solar equator. The mean meridional circulation can be inferred from the temperature field and the meridional distribution of organic molecules and condensates and hazes. Both the warm temperatures in the north polar region near 400 km and the enhanced concentration of several organic molecules suggests subsidence there during winter and early spring. Stratospheric condensates are localized at high northern latitudes, with a sharp cut-off near 50degN. Titan's winter polar vortex appears to share many of the same characteristics of winter vortices on Earth-the ozone holes. Global mapping of temperatures, winds, and composition in he troposphere, by contrast, is incomplete. The few suitable discrete clouds that have bee found for tracking indicate smaller velocities than aloft, consistent with the

  19. Scandium interaction with diantipyrylmethane homologues and 2-(n-sulphophenylazo)-1,8-dihydroxynaphthalene-3,6 sodium disulphonate

    Energy Technology Data Exchange (ETDEWEB)

    Ganago, L I; Alinovskaya, L A [AN Belorusskoj SSR, Minsk. Inst. Fiziki Tverdogo Tela i Poluprovodnikov

    1979-01-01

    The reactions of scandium with homologs of diantipyrilmethane (DAM)-propyldiantipyrilmethane (PDAM) and phenyldiantipyrilmethane (PhDAM) - are studied. The relationship of components in the complexes formed is found, and chemism of their formation is established. The complexes Sc-SPADNE (sodium salt 2-(n-sulphophenylazo)-1,8-dioxynaphthalene-3,6-disulphonic acid) are shown to form within a wide pH range. The maximum yield of complexes is observed at 6.0-7.5 pH. By the ion-exchange method the anion character of heteroligand scandium complexes is established. The complex Sc-SPADNE-PDAM is faster as compared with the complexes Sc-SPADNE-DAM and Sc-SPADNE-PhDAM. The decrease in amine excess and increase in the sensitivity of heteroligand formation of the complexes of scandium with SPADNE and PDAM make them better suited for analysis. The technique is developed for the determination of Sc/sub 2/O/sub 3/ in perovskites using the complete differential spectrophotometry method.

  20. Titanic või turist? / Karin Paulus

    Index Scriptorium Estoniae

    Paulus, Karin, 1975-

    2006-01-01

    Tallinnas Tartu maanteel asuva endise Turisti poe (arhitektid Peep Jänes, Henno Sepmann) asemele tahavad hoone omanikud ehitada kõrghoone nimega Titanic. Hoone ajutine võtmine muinsuskaitse alla on põhjustanud kohtuvaidluse

  1. Titan Submarine: Exploring the Depths of Kraken

    Data.gov (United States)

    National Aeronautics and Space Administration — Titan is unique in the outer solar system in that it is the only one of the bodies outside the Earth with liquid lakes and seas on its surface. The Titanian seas,...

  2. Aluminum titanate crucible for molten uranium

    International Nuclear Information System (INIS)

    Asbury, J.J.

    1975-01-01

    An improved crucible for molten uranium is described. The crucible or crucible liner is formed of aluminum titanate which essentially eliminates contamination of uranium and uranium alloys during molten states thereof. (U.S.)

  3. Investigating the Chemical Pathways to PAH- and PANH-Based Aerosols in Titan's Atmospheric chemistry

    Science.gov (United States)

    Sciamma-O'Brien, Ella Marion; Contreras, Cesar; Ricketts, Claire Louise; Salama, Farid

    2011-01-01

    A complex organic chemistry between Titan's two main constituents, N2 and CH4, leads to the production of more complex molecules and subsequently to solid organic aerosols. These aerosols are at the origin of the haze layers giving Titan its characteristic orange color. In situ measurements by the Ion Neutral Mass Spectrometer (INMS) and Cassini Plasma Spectrometer (CAPS) instruments onboard Cassini have revealed the presence of large amounts of neutral, positively and negatively charged heavy molecules in the ionosphere of Titan. In particular, benzene (C6H6) and toluene (C6H5CH3), which are critical precursors of polycyclic aromatic hydrocarbon (PAH) compounds, have been detected, suggesting that PAHs might play a role in the production of Titan s aerosols. Moreover, results from numerical models as well as laboratory simulations of Titan s atmospheric chemistry are also suggesting chemical pathways that link the simple precursor molecules resulting from the first steps of the N2-CH4 chemistry (C2H2, C2H4, HCN ...) to benzene, and to PAHs and nitrogen-containing PAHs (or PANHs) as precursors to the production of solid aerosols.

  4. Effects of PEG4000 template on sol-gel synthesis of porous cerium titanate photocatalyst

    Science.gov (United States)

    Zhang, Wenjie; Tao, Yingjie; Li, Chuanguo

    2018-04-01

    Porous cerium titanate was synthesized by sol-gel method, using polyethylene glycol (PEG4000) as template agent. Brannerite structured CeTi2O6 in monoclinic system is the major substance formed in the materials. Formation of CeO2 and rutile TiO2 depends on the amount of PEG4000. The addition of PEG4000 leads to production of fine particles in the samples, but it does not apparently affect the band gap energy. Pore volume of the cerium titanate sample continuously increases with rising PEG4000 amount. The sample obtained using 3.5 g PEG4000 has BET surface area of 16.2 m2/g and pore volume of 0.0232 cm3/g. The addition of PEG4000 can obviously promote photocatalytic activity of cerium titanate, which can be proven by both enhanced production of hydroxyl radical and ofloxacin degradation efficiency. As much as 95.2% of the initial ofloxacin molecules are removed from the solution after 50 min of photocatalytic degradation on the cerium titanate obtained using 3.5 g PEG4000, while only 48.4% ofloxacin is removed on cerium titanate obtained without PEG4000.

  5. Electronic structure of barium strontium titanate by soft-x-ray absorption spectroscopy

    International Nuclear Information System (INIS)

    Uehara, Y.; Underwood, J.H.; Gullikson, E.M.; Perera, R.C.C.

    1997-01-01

    Perovskite-type titanates, such as Strontium Titanate (STO), Barium Titanate (BTO), and Lead Titanate (PTO) have been widely studied because they show good electric and optical properties. In recent years, thin films of Barium Strontium Titanate (BST) have been paid much attention as dielectrics of dynamic random access memory (DRAM) capacitors. BST is a better insulator with a higher dielectric constant than STO and can be controlled in a paraelectric phase with an appropriate ratio of Ba/Sr composition, however, few studies have been done on the electronic structure of the material. Studies of the electronic structure of such materials can be beneficial, both for fundamental physics research and for improving technological applications. BTO is a famous ferroelectric material with a tetragonal structure, in which Ti and Ba atoms are slightly displaced from the lattice points. On the other hand, BST keeps a paraelectric phase, which means that the atoms are still at the cubic lattice points. It should be of great interest to see how this difference of the local structure around Ti atoms between BTO and BST effects the electronic structure of these two materials. In this report, the authors present the Ti L 2,3 absorption spectra of STO, BTO, and BST measured with very high accuracy in energy of the absorption features

  6. Electronic structure of barium strontium titanate by soft-x-ray absorption spectroscopy

    Energy Technology Data Exchange (ETDEWEB)

    Uehara, Y. [Mitsubishi Electric Co., Hyogo (Japan); Underwood, J.H.; Gullikson, E.M.; Perera, R.C.C. [Ernest Orlando Lawrence Berkeley National Lab., CA (United States)

    1997-04-01

    Perovskite-type titanates, such as Strontium Titanate (STO), Barium Titanate (BTO), and Lead Titanate (PTO) have been widely studied because they show good electric and optical properties. In recent years, thin films of Barium Strontium Titanate (BST) have been paid much attention as dielectrics of dynamic random access memory (DRAM) capacitors. BST is a better insulator with a higher dielectric constant than STO and can be controlled in a paraelectric phase with an appropriate ratio of Ba/Sr composition, however, few studies have been done on the electronic structure of the material. Studies of the electronic structure of such materials can be beneficial, both for fundamental physics research and for improving technological applications. BTO is a famous ferroelectric material with a tetragonal structure, in which Ti and Ba atoms are slightly displaced from the lattice points. On the other hand, BST keeps a paraelectric phase, which means that the atoms are still at the cubic lattice points. It should be of great interest to see how this difference of the local structure around Ti atoms between BTO and BST effects the electronic structure of these two materials. In this report, the authors present the Ti L{sub 2,3} absorption spectra of STO, BTO, and BST measured with very high accuracy in energy of the absorption features.

  7. NASA-ESA Joint Mission to Explore Two Worlds of Great Astrobiological Interest - Titan and Enceladus

    Science.gov (United States)

    Reh, K.; Coustenis, A.; Lunine, J.; Matson, D.; Lebreton, J.-P.; Erd, C.; Beauchamp, P.

    2009-04-01

    Rugged shorelines, laced with canyons, leading to ethane/methane seas glimpsed through an organic haze, vast fields of dunes shaped by alien sciroccos… An icy moon festooned with plumes of water-ice and organics, whose warm watery source might be glimpsed through surface cracks that glow in the infrared… The revelations by Cassini-Huygens about Saturn's crown jewels, Titan and Enceladus, have rocked the public with glimpses of new worlds unimagined a decade before. The time is at hand to capitalize on those discoveries with a broad mission of exploration that combines the widest range of planetary science disciplines—Geology, Geophysics, Atmospheres, Astrobiology,Chemistry, Magnetospheres—in a single NASA/ESA collaboration. The Titan Saturn System Mission will explore these exciting new environments, flying through Enceladus' plumes and plunging deep into Titan's atmosphere with instruments tuned to find what Cassini could only hint at. Exploring Titan with an international fleet of vehicles; from orbit, from the surface of a great polar sea, and from the air with the first hot air balloon to ride an extraterrestrial breeze, TSSM will turn our snapshot gaze of these worlds into an epic film. This paper will describe a collaborative NASA-ESA Titan Saturn System Mission that will open a new phase of planetary exploration by projecting robotic presence on the land, on the sea, and in the air of an active, organic-rich world.

  8. Future Exploration of Titan and Enceladus

    Science.gov (United States)

    Matson, D. L.; Coustenis, A.; Lunine, J.; Lebreton, J.; Reh, K.; Beauchamp, P.

    2009-05-01

    The future exploration of Titan and Enceladus has become very important for the planetary community. The study conducted last year of the Titan Saturn System Mission (TSSM) led to an announcement in which ESA and NASA prioritized future OPF missions, stating that TSSM is planned after EJSM (for details see http://www.lpi.usra.edu/opag/). TSSM consists of a TSSM Orbiter that would carry two in situ elements: the Titan Montgolfiere hot air balloon and the Titan Lake Lander. The mission could launch in the 2023-2025 timeframe on a trajectory to arrive ~9 years later for a 4-year mission in the Saturn system. Soon after arrival at Saturn, the montgolfiere would be delivered to Titan to begin its mission of airborne, scientific observations of Titan from an altitude of about 10 km. The montgolfiere would have a Multi-Mission Radioisotope Thermoelectric Generator (MMRTG) power system and would be designed to last at least 6-12 months in Titan's atmosphere. With the predicted winds and weather, that would be sufficient to circumnavigate the globe! On a subsequent fly-by, the TSSM orbiter would release the Lake Lander on a trajectory toward Titan for a targeted entry. It would descend through the atmosphere making scientific measurements, much like Huygens did, and then land and float on one of Titan's seas. This would be its oceanographic phase, making a physical and chemical assessment of the sea. The Lake Lander would operate 8-10 hours until its batteries become depleted. Following the delivery of the in situ elements, the TSSM orbiter would explore the Saturn system via a 2-year tour that includes in situ sampling of Enceladus' plumes as well as Titan flybys. After the Saturn system tour, the TSSM orbiter would enter orbit around Titan for a global survey phase. Synergistic and coordinated observations would be carried out between the TSSM orbiter and the in situ elements. The scientific requirements were developed by the international TSSM Joint Science Definition

  9. The rotation of Titan and Ganymede

    Science.gov (United States)

    Van Hoolst, Tim; Coyette, Alexis; Baland, Rose-Marie; Trinh, Antony

    2016-10-01

    The rotation rates of Titan and Ganymede, the largest satellites of Saturn and Jupiter, are on average equal to their orbital mean motion. Here we discuss small deviations from the average rotation for both satellites and evaluate the polar motion of Titan induced by its surface fluid layers. We examine different causes at various time scales and assess possible consequences and the potential of using librations and polar motion as probes of the interior structure of the satellites.The rotation rate of Titan and Ganymede cannot be constant on the orbital time scale as a result of the gravitational torque of the central planet acting on the satellites. Titan is moreover expected to show significant polar motion and additional variations in the rotation rate due to angular momentum exchange with the atmosphere, mainly at seasonal periods. Observational evidence for deviations from the synchronous state has been reported several times for Titan but is unfortunately inconclusive. The measurements of the rotation variations are based on determinations of the shift in position of Cassini radar images taken during different flybys. The ESA JUICE (JUpiter ICy moons Explorer) mission will measure the rotation variations of Ganymede during its orbital phase around the satellite starting in 2032.We report on different theoretical aspects of the librations and polar motion. We consider the influence of the rheology of the ice shell and take into account Cassini measurements of the external gravitational field and of the topography of Titan and similar Galileo data about Ganymede. We also evaluate the librations and polar motion induced by Titan's hydrocarbon seas and use the most recent results of Titan's atmosphere dynamics. We finally evaluate the potential of rotation variations to constrain the satellite's interior structure, in particular its ice shell and ocean.

  10. Titan Orbiter with Aerorover Mission (TOAM)

    Science.gov (United States)

    Sittler, Edward C.; Cooper, J. F.; Mahaffey, P.; Esper, J.; Fairbrother, D.; Farley, R.; Pitman, J.; Kojiro, D. R.; TOAM Team

    2006-12-01

    We propose to develop a new mission to Titan called Titan Orbiter with Aerorover Mission (TOAM). This mission is motivated by the recent discoveries of Titan, its atmosphere and its surface by the Huygens Probe, and a combination of in situ, remote sensing and radar mapping measurements of Titan by the Cassini orbiter. Titan is a body for which Astrobiology (i.e., prebiotic chemistry) will be the primary science goal of any future missions to it. TOAM is planned to use an orbiter and balloon technology (i.e., aerorover). Aerobraking will be used to put payload into orbit around Titan. The Aerorover will probably use a hot air balloon concept using the waste heat from the MMRTG 500 watts. Orbiter support for the Aerorover is unique to our approach for Titan. Our strategy to use an orbiter is contrary to some studies using just a single probe with balloon. Autonomous operation and navigation of the Aerorover around Titan will be required, which will include descent near to the surface to collect surface samples for analysis (i.e., touch and go technique). The orbiter can provide both relay station and GPS roles for the Aerorover. The Aerorover will have all the instruments needed to sample Titan’s atmosphere, surface, possible methane lakes-rivers, use multi-spectral imagers for surface reconnaissance; to take close up surface images; take core samples and deploy seismometers during landing phase. Both active and passive broadband remote sensing techniques will be used for surface topography, winds and composition measurements.

  11. Influence of trace aromatics on the chemical growth mechanisms of Titan aerosol analogues

    Science.gov (United States)

    Gautier, Thomas; Sebree, Joshua A.; Li, Xiang; Pinnick, Veronica T.; Grubisic, Andrej; Loeffler, Mark J.; Getty, Stephanie A.; Trainer, Melissa G.; Brinckerhoff, William B.

    2017-06-01

    The chemical structure and formation pathways of Titan aerosols remain largely unknown. In this work, we studied the effect of trace aromatics on the chemical composition and formation pathways of laboratory analogues of Titan's organic aerosols. The aerosol analogues were produced using four different trace aromatic molecules, comprised of one or two aromatic rings, each with or without a nitrogen heteroatom. Samples were then analyzed by laser desorption/ionization Mass Spectrometry (LDMS), revealing a high variability in the sample composition depending on the trace aromatic used. Our work reveals that the final chemical structure of the aerosols depends strongly on the number of aromatic rings in the trace molecule, leading either to a polymeric or to a random co-polymeric growth of the sample. These different chemical structures can affect the physical properties of the aerosol. Future analysis of Titan's aerosols using better resolution could potentially determine whether either of the growth hypotheses are preferred.

  12. Synergism of Saturn, Enceladus and Titan and Formation of HCNO Prebiotic Molecules

    Science.gov (United States)

    Sittler, Edward C.; Cooper, John F.

    2011-01-01

    Saturn as a system has two very exotic moons Titan and Enceladus. Titan, taking in energy from Saturn's magnetosphere, solar UV irradiation, and cosmic rays, can make HCN based molecules as discussed in earlier paper by Raulin and Owen. Space radiation effects at both moons, and as coupled by the Saturn magnetosphere, could cause an unexpected series of events potentially leading to prebiotic chemical evolution at Titan with HCNO from magnetospheric oxygen as the new ingredient. The "Old Faithful" model suggests that Enceladus, highly irradiated by Saturn magnetospheric electrons and thus having a source of chemical energy from radiolytic gas production, has episodic ejections of water vapor, carbon dioxide, and various hydrocarbons into Saturn's magnetosphere. The hydrocarbons do not survive transport through the plasma environment, but oxygen ions from Enceladus water molecules become the dominant ion species in the outer magnetosphere. At Titan, Cassini discovered that 1) keV oxygen ions, evidently from Enceladus, are bombarding Titan's upper atmosphere and 2) heavy positive and negative ions exist in significant abundances within Titan's upper atmosphere. Initial models of heavy ion formation in Titan's upper atmosphere invoked polymerization of aromatics such as benzenes and their radicals to make polycyclic aromatic hydrocarbons (PAH) , while a more recent model by Sittler et al., has raised the possibility of carbon chains forming from the polymerization of acetylene and its radicals to make fullerenes. Laboratory measurements indicate that fullerenes, which are hollow carbon shells, can trap keV oxygen ions. Clustering of the fullerenes with aerosol mixtures from PAHs and the dominant nitrogen molecules could form larger aerosols enriched in trapped oxygen. Aerosol precipitation could then convey these chemically complex structures deeper into the atmosphere and to the moon surface. Ionizing solar UV, magnetospheric electron, and galactic cosmic ray

  13. Lead palladium titanate: A room-temperature multiferroic

    Science.gov (United States)

    Gradauskaite, Elzbieta; Gardner, Jonathan; Smith, Rebecca M.; Morrison, Finlay D.; Lee, Stephen L.; Katiyar, Ram S.; Scott, James F.

    2017-09-01

    There have been a large number of papers on bismuth ferrite (BiFe O3 ) over the past few years, trying to exploit its room-temperature magnetoelectric multiferroic properties. Although these are attractive, BiFe O3 is not the ideal multiferroic due to weak magnetization and the difficulty in limiting leakage currents. Thus there is an ongoing search for alternatives, including such materials as gallium ferrite (GaFe O3 ). In the present work we report a comprehensive study of the perovskite PbT i1 -xP dxO3 with 0

  14. Phase transition in lead titanate thin films: a Brillouin study

    International Nuclear Information System (INIS)

    Kuzel, P; Dugautier, C; Moch, P; Marrec, F Le; Karkut, M G

    2002-01-01

    The elastic properties of both polycrystalline and epitaxial PbTiO 3 (PTO) thin films are studied using Brillouin scattering spectroscopy. The epitaxial PTO films were prepared by pulsed laser ablation on (1) a [0 0 1] single crystal of SrTiO 3 (STO) doped with Nb and (2) a [0 0 1] STO buffered with a layer of YBa 2 Cu 3 O 7 . The polycrystalline PTO films were prepared by sol-gel on a Si substrate buffered with TiO 2 and Pt layers. The data analysis takes into account the ripple and the elasto-optic contributions. The latter significantly affects the measured spectra since it gives rise to a Love mode in the p-s scattering geometry. At room temperature, the spectra of the epitaxially grown samples are interpreted using previously published elastic constants of PTO single crystals. Sol-gel samples exhibit appreciable softening of the effective elastic properties compared to PTO single crystals: this result is explained by taking into account the random orientation of the microscopic PTO grains. For both the polycrystalline and the epitaxial films we have determined that the piezoelectric terms do not contribute to the spectra. The temperature dependence of the spectra shows strong anomalies of the elastic properties near the ferroelectric phase transition. Compared to the bulk, T C is higher in the sol-gel films, while in the epitaxial films the sign of the T C shift depends on the underlying material

  15. Raman study of lead zirconate titanate under uniaxial stress

    International Nuclear Information System (INIS)

    Tallant, David R.; Simpson, Regina L.; Grazier, J. Mark; Zeuch, David H.; Olson, Walter R.; Tuttle, Bruce A.

    2000-01-01

    The authors used micro-Raman spectroscopy to monitor the ferroelectric (FE) to antiferroelectric (AFE) phase transition in PZT ceramic bars during the application of uniaxial stress. They designed and constructed a simple loading device, which can apply sufficient uniaxial force to transform reasonably large ceramic bars while being small enough to fit on the mechanical stage of the microscope used for Raman analysis. Raman spectra of individual grains in ceramic PZT bars were obtained as the stress on the bar was increased in increments. At the same time gauges attached to the PZT bar recorded axial and lateral strains induced by the applied stress. The Raman spectra were used to calculate an FE coordinate, which is related to the fraction of FE phase present. The authors present data showing changes in the FE coordinates of individual PZT grains and correlate these changes to stress-strain data, which plot the macroscopic evolution of the FE-to-AFE transformation. Their data indicates that the FE-to-AFE transformation does not occur simultaneously for all PZT grains but that grains react individually to local conditions

  16. A poling study on lead zirconate titanate composition

    International Nuclear Information System (INIS)

    Bryant, P.J.

    1992-01-01

    Ceramics produced by the conventional mixed oxide route are dual phased. Because the titania and zirconia are not perfectly homogenized, some parts of the ceramic are more tetragonal (titanium rich) and other parts more rhombohedral (zirconium rich). This inhomogeneity means that some domains can be more easily poled than others. Lastly, the density and porosity can affect the poling process if the flaw density becomes such that the breakdown voltage is exceeded by the required poling voltage. The phase boundary determined by most dielectric and piezoelectric measurements is significantly removed from the 44% titanium content determined by neutron diffraction. The indicators that are most consistent with this value are the minimum in the poling efficiency curve and the shape of the dissipative factor curve. The reason for the discrepancy appears to be related to the broad coexistence region of the two phases and the differing poling efficiencies of each phase. It has been established that different poling temperature profiles can substantially modify the observed properties. Such behaviour is again related to the inhomogeneity of the ceramic and the presence of the two phases. 4 refs., 5 figs

  17. Optical effects induced by epitaxial tension in lead titanate

    Czech Academy of Sciences Publication Activity Database

    Dejneka, Alexandr; Chvostová, Dagmar; Pacherová, Oliva; Kocourek, Tomáš; Jelínek, Miroslav; Tyunina, Marina

    2018-01-01

    Roč. 112, č. 3 (2018), s. 1-5, č. článku 031111. ISSN 0003-6951 R&D Projects: GA ČR GA15-13778S; GA ČR GA15-15123S Institutional support: RVO:68378271 Keywords : epitaxy * inorganic compounds * optical properties * ferroelectric materials * optical metrology Subject RIV: BM - Solid Matter Physics ; Magnetism OBOR OECD: Condensed matter physics (including formerly solid state physics , supercond.) Impact factor: 3.411, year: 2016

  18. Mechanism of electric fatigue crack growth in lead zirconate titanate

    International Nuclear Information System (INIS)

    Westram, Ilona; Oates, William S.; Lupascu, Doru C.; Roedel, Juergen; Lynch, Christopher S.

    2007-01-01

    A series of experiments was performed with through-thickness cracks in ferroelectric double cantilever beam (DCB) specimens. Cyclic electric fields of different amplitudes were applied which resulted in cyclic crack propagation perpendicular to the electric field direction. Crack propagation was observed optically and three regimes were identified: a pop-in from a notch, steady-state crack growth and a decrease of the crack growth rate with increasing cycle number. Crack growth only occurred if the applied field exceeded the coercive field strength of the material. Furthermore, the crack extended during each field reversal and the crack growth rate increased with increasing field. Based on the experimental observations, a mechanistic understanding was developed and contrasted with a nonlinear finite element analysis which quantified the stress intensity in the DCB specimens. The driving forces for crack formation at the notch and subsequent fatigue crack growth were computed based on the distribution of residual stresses due to ferroelectric switching. The finite element results are in good agreement with the experimental observations and support the proposed mechanism

  19. Crystallographic changes in lead zirconate titanate due to neutron irradiation

    Directory of Open Access Journals (Sweden)

    Alexandra Henriques

    2014-11-01

    Full Text Available Piezoelectric and ferroelectric materials are useful as the active element in non-destructive monitoring devices for high-radiation areas. Here, crystallographic structural refinement (i.e., the Rietveld method is used to quantify the type and extent of structural changes in PbZr0.5Ti0.5O3 after exposure to a 1 MeV equivalent neutron fluence of 1.7 × 1015 neutrons/cm2. The results show a measurable decrease in the occupancy of Pb and O due to irradiation, with O vacancies in the tetragonal phase being created preferentially on one of the two O sites. The results demonstrate a method by which the effects of radiation on crystallographic structure may be investigated.

  20. Studies on the effects of titanate and silane coupling agents on the performance of poly (methyl methacrylate)/barium titanate denture base nanocomposites.

    Science.gov (United States)

    Elshereksi, Nidal W; Ghazali, Mariyam J; Muchtar, Andanastuti; Azhari, Che H

    2017-01-01

    This study aimed to fabricate and characterise silanated and titanated nanobarium titanate (NBT) filled poly(methyl methacrylate) (PMMA) denture base composites and to evaluate the behaviour of a titanate coupling agent (TCA) as an alternative coupling agent to silane. The effect of filler surface modification on fracture toughness was also studied. Silanated, titanated and pure NBT at 5% were incorporated in PMMA matrix. Neat PMMA matrix served as a control. NBT was sonicated in MMA prior to mixing with the PMMA. Curing was carried out using a water bath at 75°C for 1.5h and then at 100°C for 30min. NBT was characterised via Fourier transform-infrared spectroscopy (FTIR), Transmission Electron Microscopy (TEM) and Brunauer-Emmett-Teller (BET) analysis before and after surface modification. The porosity and fracture toughness of the PMMA nanocomposites (n=6, for each formulation and test) were also evaluated. NBT was successfully functionalised by the coupling agents. The TCA exhibited the lowest percentage of porosity (0.09%), whereas silane revealed 0.53% porosity. Statistically significant differences in fracture toughness were observed among the fracture toughness values of the tested samples (pPMMA composites. Thus, TCA seemed to be more effective than silane. Minimising the porosity level could have the potential to reduce fungus growth on denture base resin to be hygienically accepTable Such enhancements obtained with Ti-NBT could lead to promotion of the composites' longevity. Copyright © 2016 Elsevier Ltd. All rights reserved.

  1. Reduced-graphene-oxide-and-strontium-titanate-based double ...

    Indian Academy of Sciences (India)

    GO)/strontium titanate were pre- ... R-GO and strontium titanate were synthesized and characterized before ... Microwave absorption capabilities of the composite absorbers were investigated using a .... was backed with a conducting metal sheet.

  2. Anion and cation diffusion in barium titanate and strontium titanate; Anionen- und Kationendiffusion in Barium- und Strontiumtitanat

    Energy Technology Data Exchange (ETDEWEB)

    Kessel, Markus Franz

    2012-12-19

    Perovskite oxides show various interesting properties providing several technical applications. In many cases the defect chemistry is the key to understand and influence the material's properties. In this work the defect chemistry of barium titanate and strontium titanate is analysed by anion and cation diffusion experiments and subsequent time-of-flight secondary ion mass spectrometry (ToF-SIMS). The reoxidation equation for barium titanate used in multi-layer ceramic capacitors (MLCCs) is found out by a combination of different isotope exchange experiments and the analysis of the resulting tracer diffusion profiles. It is shown that the incorporation of oxygen from water vapour is faster by orders of magnitude than from molecular oxygen. Chemical analysis shows the samples contain various dopants leading to a complex defect chemistry. Dysprosium is the most important dopant, acting partially as a donor and partially as an acceptor in this effectively acceptor-doped material. TEM and EELS analysis show the inhomogeneous distribution of Dy in a core-shell microstructure. The oxygen partial pressure and temperature dependence of the oxygen tracer diffusion coefficients is analysed and explained by the complex defect chemistry of Dy-doped barium titanate. Additional fast diffusion profiles are attributed to fast diffusion along grain boundaries. In addition to the barium titanate ceramics from an important technical application, oxygen diffusion in cubic, nominally undoped BaTiO{sub 3} single crystals has been studied by means of {sup 18}O{sub 2}/{sup 16}O{sub 2} isotope exchange annealing and subsequent determination of the isotope profiles in the solid by ToF-SIMS. It is shown that a correct description of the diffusion profiles requires the analysis of the diffusion through the surface space-charge into the material's bulk. Surface exchange coefficients, space-charge potentials and bulk diffusion coefficients are analysed as a function of oxygen partial

  3. Influence of Mg O and B2O3 addition on reaction sintering, properties and microstructure of Aluminum titanate

    International Nuclear Information System (INIS)

    Ajami, R.; Sarpoolaki, H.; Akbari, G. H.

    2007-01-01

    The effect of Mg O and B 2 O 3 on the formation, physical properties, phase analysis and microstructure of aluminum titanate was investigated. Density results showed the sample containing of 1 wt percent B 2 O 3 and 2 wt percent Mg O leads to the highest density while the lowest density was seen in samples containing 1 wt percent B 2 O 3 compared to pure aluminum titanate. Regarding the phase analysis of samples, Mg O was found most effective additive on reaction sintering of aluminum titanate through the intermediate phases. Furthermore at the temperatures above 1350 d eg C , B 2 O 3 promote the formation reaction of aluminum titanate. Microstructural analysis showed the samples containing Mg O are fine grain and homogeneous. Thermal expansion coefficient of samples with additives is greater than pure aluminum titanate. Pure aluminum titanate samples and one containing B 2 O 3 additive decompose to Al 2 O 3 and TiO 2 after 5 hours heat treatment at 1150 d eg C while the samples containing 2 wt percent Mg O was stable even after 25 hours

  4. Microstructure and age-hardening effects of aluminium alloys with additions of scandium and zirconium

    Energy Technology Data Exchange (ETDEWEB)

    Galun, R.; Mordike, B.L. [Inst. fuer Werkstoffkunde und Werkstofftechnik, Technische Univ. Clausthal, Clausthal-Zellerfeld (Germany); Maiwald, T.; Smola, B. [Zentrum fuer Funktionswerkstoffe GmbH, Clausthal-Zellerfeld (Germany); Mergen, R.; Manner, M.; Uitz, W. [Miba Gleitlager GmbH, Laakirchen (Australia)

    2004-12-01

    The aim of the work presented in this report was to produce age-hardenable aluminium alloys containing scandium and zirconium by a casting process with similar cooling conditions like an industrial casting process. Microstructure, precipitation structure and age-hardening response of different alloys with up to 0.4 wt.% Sc and Zr were investigated. Age-hardening experiments from the as-cast condition without solution annealing showed a significant increase of hardness of about 100% for Sc-rich alloys and of 50% for Zr-rich alloys compared to the as-cast condition. TEM investigations revealed the formation of precipitates of ternary Al{sub 3}(Sc{sub x}Zr{sub 1-x}) phases with a cubic cP4 crystal structure. In addition to the strengthening effect, a high thermal stability especially of the precipitates in Zr-rich alloys up to 400 C let these alloys look very promising for high-temperature applications. (orig.)

  5. Partitioning of Iron and Scandium in Soils Having Water Drainage Limitations

    International Nuclear Information System (INIS)

    Aide, M.; Braden, I.; Mueller, W.

    2010-01-01

    Soil chemistry of Fe includes weathering reactions, adsorption, hydrolysis, complexation, and oxidation-reduction reactions. Soil chemistry for scandium (Sc) is similar, but Sc does not include oxidation-reduction reactions. To determine if geochemical analysis may be used to identify Sc partitioning with respect to Fe among the particle size fractions, two Alfisol and two Ultisol soils were assessed using an aqua-regia digestion to estimate Sc and Fe concentrations for whole soil and particle size separates. Aqua-regia digestion data showed Sc depletion relative to Fe in sand separate. Sand separate is largely composed on quartz sand and Fe-Mn-bearing nodules, which are redoximorphic features produced by alternating oxic and suboxic/anoxic conditions associated with seasonally fluctuating water tables. Relative partitioning of Fe and Sc in these soils warrants further study to assess if selective extractions could quantify the extent of modern or ancestral oxidation-reduction processes responsible in some soil features involved in soil genesis.

  6. Adsorption of hydrogen in Scandium/Titanium decorated nitrogen doped carbon nanotube

    Energy Technology Data Exchange (ETDEWEB)

    Mananghaya, Michael, E-mail: mikemananghaya@gmail.com [De La Salle University, 2401 Taft Ave, 0922, Manila (Philippines); DLSU STC Laguna Boulevard, LTI Spine Road Barangays Biñan and Malamig, Biñan City, Laguna (Philippines); DOST-ASTHRDP, PCIEERD, Gen. Santos Ave., Bicutan, Taguig City 1631 (Philippines); Belo, Lawrence Phoa; Beltran, Arnel [De La Salle University, 2401 Taft Ave, 0922, Manila (Philippines); DLSU STC Laguna Boulevard, LTI Spine Road Barangays Biñan and Malamig, Biñan City, Laguna (Philippines)

    2016-09-01

    Nitrogen doped Carbon Nanotube with divacancy (4ND-CN{sub x}NT) that is decorated with Scandium and Titanium as potential hydrogen storage medium using the pseudo potential density functional method was investigated. Highly localized states near the Fermi level, which are derived from the nitrogen defects, contribute to strong Sc and Ti bindings, which prevent metal aggregation and improve the material stability. A detailed Comparison of the Hydrogen adsorption capability with promising system-weight efficiency of Sc over Ti was elucidated when functionalized with 4ND-CN{sub x}NT. Finally, the (Sc/4ND){sub 10}-CN{sub x}CNT composite material has a thermodynamically favorable adsorption and consecutive adsorption energy for ideal reversible adsorption and desorption of hydrogen at room temperature such that it can hold at least 5.8 wt% hydrogen molecules at the LDA and GGA level. - Highlights: • Carbon Nanotube with divacancy (4ND-CN{sub x}NT) decorated with Sc and Ti. • Nitrogen defects, contribute to strong Sc and Ti bindings. • H{sub 2} and (Sc/4ND){sub 10}-CN{sub x}CNT has a favorable adsorption. • 5.8 wt% adsorption at the LDA and GGA level.

  7. Spacecraft Exploration of Titan and Enceladus

    Science.gov (United States)

    Matson, D.; Coustenis, A.; Lunine, J. I.; Lebreton, J.; Reh, K.; Beauchamp, P.; Erd, C.

    2009-12-01

    The future exploration of Titan and Enceladus is very important for planetary science. The study titled Titan Saturn System Mission (TSSM) led to an announcement in which ESA and NASA prioritized future OPF missions, stating that TSSM is planned after EJSM (for details see http://www.lpi.usra.edu/opag/). The TSSM concept consists of an Orbiter that would carry two in situ elements: the Titan Montgolfiere hot air balloon and the Titan Lake Lander. This mission could launch in the 2023-2025 timeframe on a trajectory to arrive ~9 years later and begin a 4-year mission in the Saturnian system. At an appropriate time after arrival at Saturn, the montgolfiere would be delivered to Titan to begin its mission of airborne, scientific observations of Titan from an altitude of about 10 km above the surface. The montgolfiere would have a Multi-Mission Radioisotope Thermoelectric Generator (MMRTG) power system whose waste heat would warm the gas in the balloon, providing buoyancy. It would be designed to survive at least 6-12 months in Titan’s atmosphere. With the predicted winds and weather, it should be possible to circumnavigate the globe! Later, on a subsequent fly-by, the TSSM orbiter would send the Lake Lander to Titan. It would descend through the atmosphere making scientific measurements, much like Huygens did, and then land and float on one of Titan’s seas. This would be its oceanographic phase of making a physical and chemical assessment of the sea. The Lake Lander would operate for 8-10 hours until its batteries become depleted. Following the delivery of the in situ elements, the TSSM orbiter would then explore the Saturn system for two years on a tour that includes in situ sampling of Enceladus’ plumes as well as flybys of Titan. After the Saturn tour, the TSSM orbiter would go into orbit around Titan and carry out a global survey phase. Synergistic observations would be carried out by the TSSM orbiter and the in situ elements. The scientific requirements for

  8. Influence of scandium on the microstructure and strength properties of the welded joint at the laser welding of aluminum-lithium alloys

    Science.gov (United States)

    Malikov, A. G.; Golyshev, A. A.; Ivanova, M. Yu.

    2017-10-01

    Today, aeronautical equipment manufacture involves up-to-date high-strength aluminum alloys of decreased density resulting from lithium admixture. Various technologies of fusible welding of these alloys are being developed. Serious demands are imposed to the welded joints of aluminum alloys in respect to their strength characteristics. The paper presents experimental investigations of the optimization of the laser welding of aluminum alloys with the scandium-modified welded joint. The effect of scandium on the micro-and macro-structure has been studied as well as the strength characteristics of the welded joint. It has been found that scandium under in the laser welding process increases the welded joint elasticity for the system Al-Mg-Li, aluminum alloy 1420 by 20 %, and almost doubles the same for the system Al-Cu-Li, aluminum alloy 1441.

  9. Modeling of synchrotron-based laboratory simulations of Titan's ionospheric photochemistry

    Science.gov (United States)

    Carrasco, Nathalie; Peng, Zhe; Pernot, Pascal

    2014-11-01

    The APSIS reactor has been designed to simulate in the laboratory with a VUV synchrotron irradiation the photochemistry occurring in planetary upper atmospheres. A N2-CH4 Titan-like gas mixture has been studied, whose photochemistry in Titan's ionospheric irradiation conditions leads to a coupled chemical network involving both radicals and ions. In the present work, an ion-neutral coupled model is developed to interpret the experimental data, taking into account the uncertainties on the kinetic parameters by Monte Carlo sampling. The model predicts species concentrations in agreement with mass spectrometry measurements of the methane consumption and product blocks intensities. Ion chemistry and in particular dissociative recombination are found to be very important through sensitivity analysis. The model is also applied to complementary environmental conditions, corresponding to Titan's ionospheric average conditions and to another existing synchrotron setup. An innovative study of the correlations between species concentrations identifies two main competitive families, leading respectively to saturated and unsaturated species. We find that the unsaturated growth family, driven by C2H2 , is dominant in Titan's upper atmosphere, as observed by the Cassini INMS. But the saturated species are substantially more intense in the measurements of the two synchrotron experimental setups, and likely originate from catalysis by metallic walls of the reactors.

  10. Noble gases, nitrogen, and methane from the deep interior to the atmosphere of Titan

    Science.gov (United States)

    Glein, Christopher R.

    2015-04-01

    Titan's thick N2-CH4 atmosphere is unlike any in the Solar System, and its origin has been shrouded in mystery for over half a century. Here, I perform a detailed analysis of chemical and isotopic data from the Cassini-Huygens mission to develop the hypothesis that Titan's (non-photochemical) atmospheric gases came from deep within. It is suggested that Titan's CH4, N2, and noble gases originated in a rocky core buried inside the giant satellite, and hydrothermal and cryovolcanic processes were critical to the creation of Titan's atmosphere. Mass balance and chemical equilibrium calculations demonstrate that all aspects of this hypothesis can be considered geochemically plausible with respect to contemporary observational, experimental, and theoretical knowledge. Specifically, I show that a rocky core with a bulk noble gas content similar to that in CI carbonaceous meteorites would contain sufficient 36Ar and 22Ne to explain their reported abundances. I also show that Henry's law constants for noble gases in relevant condensed phases can be correlated with the size of their atoms, which leads to expected mixing ratios for 84Kr (∼0.2 ppbv) and 132Xe (∼0.01 ppbv) that can explain why these species have yet to be detected (Huygens upper limit serpentinization). I show that sufficient CH4 can be produced to replenish Titan's atmosphere many times over in the face of irreversible photolysis and escape of CH4, which is consistent with the favored model of episodic cryovolcanic outgassing. There should also have been enough NH3 inside Titan so that its thermal decomposition in a hot rocky core can generate the observed atmospheric N2, and if correct this model would imply that Titan's interior has experienced vigorous hydrothermal processing. The similarity in 14N/15N between cometary NH3 and Titan's N2 is consistent with this picture. As for the isotopes in CH4, I show that their observed relative abundances can be explained by low-temperature (∼20 °C) equilibria

  11. Laboratory studies into the use of the scandium-46-EDTA complex as a tracer for groundwater flow

    International Nuclear Information System (INIS)

    Cheng, H.; Nixon, S.C.

    1988-01-01

    Gamma ray emitting metal radionuclides, when complexed with an appropriate complexing agent, provide a wide choice of water tracers particularly for groundwater studies where a radionuclide of appropriate half-life suited to the particular study can be selected. Scandium-46 has easily detectable gamma emission and a suitable half-life (84 days) for medium term studies. It has been widely and successfully used as a tracer in studies of sediment movement but has not yet been introduced as a groundwater tracer. In our experiments the chemical aspects of the preparation of Sc-46-EDTA were studied in some detail and its behaviour in various mineralogical environments was evaluated with reference to the standard tracer, tritiated water. The experimental results have shown that the scandium cation can be easily complexed with EDTA to form soluble SC-EDTA. The complex is very stable in a wide range of pH; the adsorptive properties of Sc-EDTA in the batch studies and the retardation and recovery in the column tests in comparison with tritiated water are quite satisfactory. In general Sc-46-EDTA is a promising tracer for groundwater studies. In the report the appropriate conditions, procedures and some rational and efficient methods for testing the purity of Sc-46-EDTA in the preparation of the tracer solution of Sc-46-EDTA are described. In addition, it has been found that the formation of the metal hydroxide colloids is the major reason for the great loss in groundwater aquifers of most trivalent metal nuclide tracers in the cationic form including scandium-46. (author). 29 refs, 11 figs, 12 tabs

  12. TITAN'S TRANSPORT-DRIVEN METHANE CYCLE

    International Nuclear Information System (INIS)

    Mitchell, Jonathan L.

    2012-01-01

    The mechanisms behind the occurrence of large cloud outbursts and precipitation on Titan have been disputed. A global- and annual-mean estimate of surface fluxes indicated only 1% of the insolation, or ∼0.04 W m –2 , is exchanged as sensible and/or latent fluxes. Since these fluxes are responsible for driving atmospheric convection, it has been argued that moist convection should be quite rare and precipitation even rarer, even if evaporation globally dominates the surface-atmosphere energy exchange. In contrast, climate simulations indicate substantial cloud formation and/or precipitation. We argue that the top-of-atmosphere (TOA) radiative imbalance is diagnostic of horizontal heat transport by Titan's atmosphere, and thus constrains the strength of the methane cycle. Simple calculations show the TOA radiative imbalance is ∼0.5-1 W m –2 in Titan's equatorial region, which implies 2-3 MW of latitudinal heat transport by the atmosphere. Our simulation of Titan's climate suggests this transport may occur primarily as latent heat, with net evaporation at the equator and net accumulation at higher latitudes. Thus, the methane cycle could be 10-20 times previous estimates. Opposing seasonal transport at solstices, compensation by sensible heat transport, and focusing of precipitation by large-scale dynamics could further enhance the local, instantaneous strength of Titan's methane cycle by a factor of several. A limited supply of surface liquids in regions of large surface radiative imbalance may throttle the methane cycle, and if so, we predict more frequent large storms over the lakes district during Titan's northern summer.

  13. Experimental simulations of ethylene evaporites on Titan

    Science.gov (United States)

    Czaplinski, E.; Farnsworth, K.; Singh, S.; Chevrier, V.

    2017-12-01

    Titan has an abundance of lakes and seas, as identified by the Cassini spacecraft. Major components of these liquid bodies include methane (CH4) and ethane (C2H6), however minor constituents are also thought to exist (e.g. ethylene (C2H4)). As the lakes and seas evaporate, 5-μm-bright deposits, resembling evaporite deposits on Earth, are left behind in a "bathtub ring" fashion. Previous studies include models of evaporites, and observations of the 5-μm-bright regions, but the community is still lacking a complete suite of experimental evaporite studies. In this study, we experimentally investigate evaporites in order to determine their composition and how they affect infrared spectra during the evaporation process. The University of Arkansas owns a specialized chamber that simulates the surface conditions of Titan ( 90 K and 1.5 bar). Gaseous hydrocarbons are condensed within the chamber and analyzed with Fourier Transform Infrared (FTIR) Spectroscopy and band depth calculations. In this study, three types of experiments were performed: ethane/ethylene, methane/ethylene, and methane/ethane/ethylene. For these experiments, methane was the only species that readily evaporated at Titan conditions (due to its high volatility), while ethane, being the more stable solvent, did not readily evaporate. Therefore, we will present spectral results of ethylene evaporite formation within these mixtures. Our results imply that evaporite formation is strongly dependent on the composition of the solvent. The north polar lakes of Titan are predicted to be methane-rich, indicating that they may be more likely to form evaporites. Alternatively, Ontario Lacus, a south polar lake, is predominately composed of ethane, which may make it more difficult to form evaporites. As we continue to study Titan's mysterious lakes and seas, we hope to draw insights on their exact composition, conditions for evaporite formation, habitability potential, and comparing Titan to prebiotic Earth.

  14. Volatile products controlling Titan's tholins production

    KAUST Repository

    Carrasco, Nathalie

    2012-05-01

    A quantitative agreement between nitrile relative abundances and Titan\\'s atmospheric composition was recently shown with a reactor simulating the global chemistry occurring in Titan\\'s atmosphere (Gautier et al. [2011]. Icarus, 213, 625-635). Here we present a complementary study on the same reactor using an in situ diagnostic of the gas phase composition. Various initial N 2/CH 4 gas mixtures (methane varying from 1% to 10%) are studied, with a monitoring of the methane consumption and of the stable gas neutrals by in situ mass spectrometry. Atomic hydrogen is also measured by optical emission spectroscopy. A positive correlation is found between atomic hydrogen abundance and the inhibition function for aerosol production. This confirms the suspected role of hydrogen as an inhibitor of heterogeneous organic growth processes, as found in Sciamma-O\\'Brien et al. (Sciamma-O\\'Brien et al. [2010]. Icarus, 209, 704-714). The study of the gas phase organic products is focussed on its evolution with the initial methane amount [CH 4] 0 and its comparison with the aerosol production efficiency. We identify a change in the stationary gas phase composition for intermediate methane amounts: below [CH 4] 0=5%, the gas phase composition is mainly dominated by nitrogen-containing species, whereas hydrocarbons are massively produced for [CH 4] 0>5%. This predominance of N-containing species at lower initial methane amount, compared with the maximum gas-to solid conversion observed in Sciamma-O\\'Brien et al. (2010) for identical methane amounts confirms the central role played by N-containing gas-phase compounds to produce tholins. Moreover, two protonated imines (methanimine CH 2NH and ethanamine CH 3CHNH) are detected in the ion composition in agreement with Titan\\'s INMS measurements, and reinforcing the suspected role of these chemical species on aerosol production. © 2012 Elsevier Inc.

  15. Complexometric determination of aluminium and scandium using fluorides as masking agent at low pH value

    International Nuclear Information System (INIS)

    Tikhonov, V.N.

    1978-01-01

    A complexometric method is suggested to determine Al and Sc by back titration of Bi(NO 3 ) 3 solution with xylenol orange indicator at low pH values. To increase selectivity fluoride additions were used which were masked by boron acid at the end titration point. EDTA was used as a complexing agent. Metals which create at low pH values stable complexes with EDTA undestroyed by fluoride, do not interfere with Al and Sc determination. Scandium is shown to be determined more selectively than aluminium

  16. Titan Submarine : AUV Design for Cryogenic Extraterrestrial Seas of Hydrocarbons

    Science.gov (United States)

    Lorenz, Ralph D.; Oleson, Steven; Colozza, Tony; Hartwig, Jason; Schmitz, Paul; Landis, Geoff; Paul, Michael; Walsh, Justin

    2016-04-01

    Saturn's moon Titan has three seas, apparently composed predominantly of liquid methane, near its north pole. The largest of these, Ligeia Mare and Kraken Mare, span about 400km and 1000km respectively, and are linked by a narrow strait. Radar measurements from the Cassini spacecraft (currently in orbit around Saturn) show that Ligeia at least is 160m deep, Kraken perhaps deeper. Titan has a nitrogen atmosphere somewhat denser than Earth's, and gravity about the same as the Earth's moon, and its surface temperature is about 92K ; the seas are liquid under conditions rather similar to those of liquified natural gas (LNG) a commodity with familiar engineering properties. We report a NASA Innovative Advanced Concepts (NIAC) study into a submersible vehicle able to explore these seas, to survey shoreline geomorphology, investigate air-sea exchange processes, measure composition to evaluate stratification and mixing, and map the seabed. The Titan environment poses unique thermal management and buoyancy control challenges (the temperature-dependent solubility of nitrogen in methane leads to the requirement to isolate displacement gas from liquid in buoyancy control tanks, and may result in some effervescence due to the heat dissipation into the liquid from the vehicle's radioisotope power supply, a potential noise source for sonar systems). The vehicle must also be delivered from the air, either by parachute extraction from or controlled ditching of a slender entry system, and must communicate its results back to Earth. Nominally the latter function is achieved with a large dorsal phased-array antenna, operated while surfaced, but solutions using an orbiting relay spacecraft and even communication while submerged, are being examined. While these aspects seem fantastical, in many respects the structural, propulsion and navigation/autonomy challenges of such a vehicle are little different from terrestrial autonomous underwater vehicles. We discuss the results of the study

  17. Predicting Passenger Survival Rates on the Titanic

    OpenAIRE

    Prateek Chanda

    2017-01-01

    The sinking of the RMS Titanic is one of the most infamous shipwrecks in history. On April 15, 1912, during her maiden voyage, the Titanic sank after colliding with an iceberg, killing 1502 out of 2224 passengers and crew. This sensational tragedy shocked the international community and led to better safety regulations for ships. One of the reasons that the shipwreck led to such loss of life was that there were not enough lifeboats for the passengers and crew. Although there was some el...

  18. Behavior under Extreme Conditions: The Titanic Disaster

    OpenAIRE

    Bruno S. Frey; David A. Savage; Benno Torgler

    2011-01-01

    During the night of April 14, 1912, the RMS Titanic collided with an iceberg on her maiden voyage. Two hours and 40 minutes later she sank, resulting in the loss of 1,501 lives—more than two-thirds of her 2,207 passengers and crew. This remains one of the deadliest peacetime maritime disasters in history and by far the most famous. For social scientists, evidence about how people behaved as the Titanic sunk offers a quasi-natural field experiment to explore behavior under extreme conditions o...

  19. Technological properties and structure of titanate melts

    International Nuclear Information System (INIS)

    Morozov, A.A.

    2002-01-01

    Power substantiation of existence of tough stream of complex anion ([TiO 6 ] 8- ) as a prevalent unit in titanate melts is given on the base of up-to-date knowledge about structure of metallurgical slags and results of investigations of thermophysical properties of these melts. It is shown that high crystallization ability of titanate melts at technological temperatures is determined by heterogeneity of liquid state - by presence up to 30 % of dispersed particles of solid phase solutions in matrix liquid [ru

  20. Printed Barium Strontium Titanate capacitors on silicon

    Energy Technology Data Exchange (ETDEWEB)

    Sette, Daniele [Univ. Grenoble Alpes, F-38000 Grenoble (France); CEA, LETI, MINATEC Campus, F-38054 Grenoble (France); Luxembourg Institute of Science and Technology LIST, Materials Research and Technology Department, L-4422 Belvaux (Luxembourg); Kovacova, Veronika [Univ. Grenoble Alpes, F-38000 Grenoble (France); CEA, LETI, MINATEC Campus, F-38054 Grenoble (France); Defay, Emmanuel, E-mail: emmanuel.defay@list.lu [Univ. Grenoble Alpes, F-38000 Grenoble (France); CEA, LETI, MINATEC Campus, F-38054 Grenoble (France); Luxembourg Institute of Science and Technology LIST, Materials Research and Technology Department, L-4422 Belvaux (Luxembourg)

    2015-08-31

    In this paper, we show that Barium Strontium Titanate (BST) films can be prepared by inkjet printing of sol–gel precursors on platinized silicon substrate. Moreover, a functional variable capacitor working in the GHz range has been made without any lithography or etching steps. Finally, this technology requires 40 times less precursors than the standard sol–gel spin-coating technique. - Highlights: • Inkjet printing of Barium Strontium Titanate films • Deposition on silicon substrate • Inkjet printed silver top electrode • First ever BST films thinner than 1 μm RF functional variable capacitor that has required no lithography.

  1. Bismuth titanate nanorods and their visible light photocatalytic properties

    International Nuclear Information System (INIS)

    Pei, L.Z.; Liu, H.D.; Lin, N.; Yu, H.Y.

    2015-01-01

    Highlights: • Bismuth titanate nanorods have been synthesized by a simple hydrothermal process. • The size of bismuth titanate nanorods can be controlled by growth conditions. • Bismuth titanate nanorods show good photocatalytic activities of methylene blue and Rhodamine B. - Abstract: Bismuth titanate nanorods have been prepared using a facile hydrothermal process without additives. The bismuth titanate products were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), high-resolution TEM (HRTEM) and UV-vis diffusion reflectance spectrum. XRD pattern shows that the bismuth titanate nanorods are composed of cubic Bi 2 Ti 2 O 7 phase. Electron microscopy images show that the length and diameter of the bismuth titanate nanorods are 50-200 nm and 2 μm, respectively. Hydrothermal temperature and reaction time play important roles on the formation and size of the bismuth titanate nanorods. UV-vis diffusion reflectance spectrum indicates that bismuth titanate nanorods have a band gap of 2.58 eV. The bismuth titanate nanorods exhibit good photocatalytic activities in the photocatalytic degradation of methylene blue (MB) and Rhodamine B (RB) under visible light irradiation. The bismuth titanate nanorods with cubic Bi 2 Ti 2 O 7 phase are a promising candidate as a visible light photocatalyst

  2. Non-LTE diagnositics of infrared radiation of Titan's atmosphere

    Science.gov (United States)

    Feofilov, Artem; Rezac, Ladislav; Kutepov, Alexander; Vinatier, Sandrine; Rey, Michael; Nikitin, Andrew; Tyuterev, Vladimir

    2016-06-01

    Yelle (1991) and Garcia-Comas et al, (2011) demonstrated the importance of accounting for the local thermodynamic equilibrium (LTE) breakdown in the middle and upper atmosphere of Titan for the interpretation of infrared radiances measured at these heights. In this work, we make further advance in this field by: • updating the non-LTE model of CH4 emissions in Titan's atmosphere and including a new extended database of CH4 spectroscopic parameters • studying the non-LTE CH4 vibrational level populations and the impact of non-LTE on limb infrared emissions of various CH4 ro-vibrational bands including those at 7.6 and 3.3 µm • implementing our non-LTE model into the LTE-based retrieval algorithm applied by Vinatier et al., (2015) for processing the Cassini/CIRS spectra. We demonstrate that accounting for non-LTE leads to an increase in temperatures retrieved from CIRS 7.6 µm limb emissions spectra (˜10 K at 600 km altitude) and estimate how this affects the trace gas density retrieval. Finally, we discuss the effects of including a large number of weak one-quantum and combinational bands on the calculated daytime limb 3.3 µm emissions and the impact they may have on the CH4 density retrievals from the Cassini VIMS 3.3 µm limb emission observations.

  3. The Titan Sky Simulator ™ - Testing Prototype Balloons in Conditions Approximating those in Titan's Atmosphere

    Science.gov (United States)

    Nott, Julian

    This paper will describe practical work flying prototype balloons in the "The Titan Sky Simulator TM " in conditions approximating those found in Titan's atmosphere. Saturn's moon, Titan, is attracting intense scientific interest. This has led to wide interest in exploring it with Aerobots, balloons or airships. Their function would be similar to the Rovers exploring Mars, but instead of moving laboriously across the rough terrain on wheels, they would float freely from location to location. To design any balloon or airship it is essential to know the temperature of the lifting gas as this influences the volume of the gas, which in turn influences the lift. To determine this temperature it is necessary to know how heat is transferred between the craft and its surroundings. Heat transfer for existing balloons is well understood. However, Titan conditions are utterly different from those in which balloons have ever been flown, so heat transfer rates cannot currently be calculated. In particular, thermal radiation accounts for most heat transfer for existing balloons but over Titan heat transfer will be dominated by convection. To be able to make these fundamental calculations, it is necessary to get fundamental experimental data. This is being obtained by flying balloons in a Simulator filled with nitrogen gas at very low temperature, about 95° K / minus 180° C, typical of Titan's temperatures. Because the gas in the Simulator is so cold, operating at atmospheric pressure the density is close to that of Titan's atmosphere. "The Titan Sky Simulator TM " has an open interior approximately 4.5 meter tall and 2.5 meters square. It has already been operated at 95° K/-180° C. By the time of the Conference it is fully expected to have data to present from actual balloons flying at this temperature. Perhaps the most important purpose of this testing is to validate numerical [computational fluid dynamics] models being developed by Tim Colonius of Caltech. These numerical

  4. Electron-molecule chemistry and charging processes on organic ices and Titan's icy aerosol surrogates

    Science.gov (United States)

    Pirim, C.; Gann, R. D.; McLain, J. L.; Orlando, T. M.

    2015-09-01

    Electron-induced polymerization processes and charging events that can occur within Titan's atmosphere or on its surface were simulated using electron irradiation and dissociative electron attachment (DEA) studies of nitrogen-containing organic condensates. The DEA studies probe the desorption of H- from hydrogen cyanide (HCN), acetonitrile (CH3CN), and aminoacetonitrile (NH2CH2CN) ices, as well as from synthesized tholin materials condensed or deposited onto a graphite substrate maintained at low temperature (90-130 K). The peak cross sections for H- desorption during low-energy (3-15 eV) electron irradiation were measured and range from 3 × 10-21 to 2 × 10-18 cm2. Chemical and structural transformations of HCN ice upon 2 keV electron irradiation were investigated using X-ray photoelectron and Fourier-transform infrared spectroscopy techniques. The electron-beam processed materials displayed optical properties very similar to tholins produced by conventional discharge methods. Electron and negative ion trapping lead to 1011 charges cm-2 on a flat surface which, assuming a radius of 0.05 μm for Titan aerosols, is ∼628 charges/radius (in μm). The facile charge trapping indicates that electron interactions with nitriles and complex tholin-like molecules could affect the conductivity of Titan's atmosphere due to the formation of large negative ion complexes. These negatively charged complexes can also precipitate onto Titan's surface and possibly contribute to surface reactions and the formation of dunes.

  5. Barium zirconate-titanate/barium calcium-titanate ceramics via sol-gel process: novel high-energy-density capacitors

    International Nuclear Information System (INIS)

    Puli, Venkata Sreenivas; Kumar, Ashok; Scott, J F; Katiyar, Ram S; Chrisey, Douglas B; Tomozawa, M

    2011-01-01

    Lead-free barium zirconate-titanate/barium calcium-titanate, [(BaZr 0.2 Ti 0.80 )O 3 ] 1-x -[(Ba 0.70 Ca 0.30 )TiO 3 ] x (x = 0.10, 0.15, 0.20) (BZT-BCT) ceramics with high dielectric constant, low dielectric loss and moderate electric breakdown field were prepared by the sol-gel synthesis technique. X-ray diffraction patterns revealed tetragonal crystal structure and this was further confirmed by Raman spectra. Well-behaved ferroelectric hysteresis loops and moderate polarizations (spontaneous polarization, P s ∼ 3-6 μC cm -2 ) were obtained in these BZT-BCT ceramics. Frequency-dependent dielectric spectra confirmed that ferroelectric diffuse phase transition (DPT) exists near room temperature. Scanning electron microscope images revealed monolithic grain growth in samples sintered at 1280 deg. C. 1000/ε versus (T) plots revealed ferroelectric DPT behaviour with estimated γ values of ∼1.52, 1.51 and 1.88, respectively, for the studied BZT-BCT compositions. All three compositions showed packing-limited breakdown fields of ∼47-73 kV cm -1 with an energy density of 0.05-0.6 J cm -3 for thick ceramics (>1 mm). Therefore these compositions might be useful in Y5V-type capacitor applications.

  6. Barium zirconate-titanate/barium calcium-titanate ceramics via sol-gel process: novel high-energy-density capacitors

    Energy Technology Data Exchange (ETDEWEB)

    Puli, Venkata Sreenivas; Kumar, Ashok; Scott, J F; Katiyar, Ram S [SPECLAB, Department of Physics, University of Puerto Rico, San Juan, PR 00936 (Puerto Rico); Chrisey, Douglas B; Tomozawa, M, E-mail: rkatiyar@uprrp.edu [Department of Materials Science and Engineering, Rensselaer Polytechnic Institute, Troy, NY 12180-3590 (United States)

    2011-10-05

    Lead-free barium zirconate-titanate/barium calcium-titanate, [(BaZr{sub 0.2}Ti{sub 0.80})O{sub 3}]{sub 1-x}-[(Ba{sub 0.70}Ca{sub 0.30})TiO{sub 3}]{sub x} (x = 0.10, 0.15, 0.20) (BZT-BCT) ceramics with high dielectric constant, low dielectric loss and moderate electric breakdown field were prepared by the sol-gel synthesis technique. X-ray diffraction patterns revealed tetragonal crystal structure and this was further confirmed by Raman spectra. Well-behaved ferroelectric hysteresis loops and moderate polarizations (spontaneous polarization, P{sub s} {approx} 3-6 {mu}C cm{sup -2}) were obtained in these BZT-BCT ceramics. Frequency-dependent dielectric spectra confirmed that ferroelectric diffuse phase transition (DPT) exists near room temperature. Scanning electron microscope images revealed monolithic grain growth in samples sintered at 1280 deg. C. 1000/{epsilon} versus (T) plots revealed ferroelectric DPT behaviour with estimated {gamma} values of {approx}1.52, 1.51 and 1.88, respectively, for the studied BZT-BCT compositions. All three compositions showed packing-limited breakdown fields of {approx}47-73 kV cm{sup -1} with an energy density of 0.05-0.6 J cm{sup -3} for thick ceramics (>1 mm). Therefore these compositions might be useful in Y5V-type capacitor applications.

  7. The Titan Environmental Transmission Electron Microscope

    DEFF Research Database (Denmark)

    Hansen, Thomas Willum; Wagner, Jakob Birkedal; Jinschek, Jörg R.

    2009-01-01

    University of Denmark (DTU) provides a unique combination of techniques for studying materials of interest to the catalytic as well as the electronics and other communities [5]. DTU’s ETEM is based on the FEI Titan platform providing ultrahigh microscope stability pushing the imaging resolution into the sub...

  8. Infrared characterization of strontium titanate thin films

    International Nuclear Information System (INIS)

    Almeida, B.G.; Pietka, A.; Mendes, J.A.

    2004-01-01

    Strontium titanate thin films have been prepared at different oxygen pressures with various post-deposition annealing treatments. The films were deposited by pulsed laser ablation at room temperature on Si(0 0 1) substrates with a silica buffer layer. Infrared reflectance measurements were performed in order to determine relevant film parameters such as layer thicknesses and chemical composition. The infrared reflectance spectra were fitted by using adequate dielectric function forms for each layer. The fitting procedure provided the extraction of the dielectric functions of the strontium titanate film, the silica layer and the substrate. The as-deposited films are found to be amorphous, and their infrared spectra present peaks corresponding to modes with high damping constants. As the annealing time and temperature increases the strontium titanate layer becomes more ordered so that it can be described by its SrTiO 3 bulk mode parameters. Also, the silica layer grows along with the ordering of the strontium titanate film, due to oxidation during annealing

  9. The mechanochemical stability of hydrogen titanate nanostructures

    International Nuclear Information System (INIS)

    Plodinec, M.; Friscic, I.; Ivekovic, D.; Tomasic, N.; Su, D.S.; Zhang, J.; Gajovic, A.

    2010-01-01

    The structural stability of some nanostructured titanates was investigated in terms of their subsequent processing and possible applications. With the aim to investigate their mechanochemical stability, we applied high-energy ball milling and studied the resulting induced phase transitions. Hydrogen titanates with two different morphologies, microcrystals and nanotubes, were taken into consideration. The phase-transition sequence was studied by Raman spectroscopy and X-ray powder diffraction, while the morphology and crystal structure, on the nanoscale, were analyzed by high-resolution transmission electron microscopy. During the mechanochemical treatment of both morphologies, the phase transitions from hydrogen titanate to TiO 2 anatase and subsequently to TiO 2 rutile were observed. In the case of hydrogen trititanate crystals, the phase transition to anatase starts after a longer milling time than in the case of the titanate nanotubes, which is explained by the larger particle size of the crystalline powder. However, the phase transition from anatase to rutile occurred more quickly in the crystalline powder than in the case of the nanotubes.

  10. The seasonal cycle of Titan's detached haze

    Science.gov (United States)

    West, Robert A.; Seignovert, Benoît; Rannou, Pascal; Dumont, Philip; Turtle, Elizabeth P.; Perry, Jason; Roy, Mou; Ovanessian, Aida

    2018-04-01

    Titan's `detached' haze, seen in Voyager images in 1980 and 1981 and monitored by the Cassini Imaging Science Subsystem (ISS) during the period 2004-2017, provides a measure of seasonal activity in Titan's mesosphere with observations over almost half of Saturn's seasonal cycle. Here we report on retrieved haze extinction profiles that reveal a depleted layer (having a diminished aerosol content), visually manifested as a gap between the main haze and a thin, detached upper layer. Our measurements show the disappearance of the feature in 2012 and its reappearance in 2016, as well as details after the reappearance. These observations highlight the dynamical nature of the detached haze. The reappearance seems congruent with earlier descriptions by climate models but more complex than previously described. It occurs in two steps, first as haze reappearing at 450 ± 20 km and one year later at 510 ± 20 km. These observations provide additional tight and valuable constraints about the underlying mechanisms, especially for Titan's mesosphere, that control Titan's haze cycle.

  11. An update of nitrile photochemistry on Titan

    Science.gov (United States)

    Yung, Yuk L.

    1987-01-01

    Comparisons are undertaken between laboratory kinetics experiments and Voyager observations in order to shed light on possible chemical reaction pathways to the generation of cyanogen and dicyanoacetylene in Titan's upper atmosphere. The predicted concentrations of the simple nitrile compounds are found to be of a magnitude realistically corresponding to the Voyager observations.

  12. TandEM: Titan and Enceladus mission

    Science.gov (United States)

    Coustenis, A.; Atreya, S.K.; Balint, T.; Brown, R.H.; Dougherty, M.K.; Ferri, F.; Fulchignoni, M.; Gautier, D.; Gowen, R.A.; Griffith, C.A.; Gurvits, L.I.; Jaumann, R.; Langevin, Y.; Leese, M.R.; Lunine, J.I.; McKay, C.P.; Moussas, X.; Muller-Wodarg, I.; Neubauer, F.; Owen, T.C.; Raulin, F.; Sittler, E.C.; Sohl, F.; Sotin, Christophe; Tobie, G.; Tokano, T.; Turtle, E.P.; Wahlund, J.-E.; Waite, J.H.; Baines, K.H.; Blamont, J.; Coates, A.J.; Dandouras, I.; Krimigis, T.; Lellouch, E.; Lorenz, R.D.; Morse, A.; Porco, C.C.; Hirtzig, M.; Saur, J.; Spilker, T.; Zarnecki, J.C.; Choi, E.; Achilleos, N.; Amils, R.; Annan, P.; Atkinson, D.H.; Benilan, Y.; Bertucci, C.; Bezard, B.; Bjoraker, G.L.; Blanc, M.; Boireau, L.; Bouman, J.; Cabane, M.; Capria, M.T.; Chassefiere, E.; Coll, P.; Combes, M.; Cooper, J.F.; Coradini, A.; Crary, F.; Cravens, T.; Daglis, I.A.; de Angelis, E.; De Bergh, C.; de Pater, I.; Dunford, C.; Durry, G.; Dutuit, O.; Fairbrother, D.; Flasar, F.M.; Fortes, A.D.; Frampton, R.; Fujimoto, M.; Galand, M.; Grasset, O.; Grott, M.; Haltigin, T.; Herique, A.; Hersant, F.; Hussmann, H.; Ip, W.; Johnson, R.; Kallio, E.; Kempf, S.; Knapmeyer, M.; Kofman, W.; Koop, R.; Kostiuk, T.; Krupp, N.; Kuppers, M.; Lammer, H.; Lara, L.-M.; Lavvas, P.; Le, Mouelic S.; Lebonnois, S.; Ledvina, S.; Li, Ji; Livengood, T.A.; Lopes, R.M.; Lopez-Moreno, J. -J.; Luz, D.; Mahaffy, P.R.; Mall, U.; Martinez-Frias, J.; Marty, B.; McCord, T.; Salvan, C.M.; Milillo, A.; Mitchell, D.G.; Modolo, R.; Mousis, O.; Nakamura, M.; Neish, Catherine D.; Nixon, C.A.; Mvondo, D.N.; Orton, G.; Paetzold, M.; Pitman, J.; Pogrebenko, S.; Pollard, W.; Prieto-Ballesteros, O.; Rannou, P.; Reh, K.; Richter, L.; Robb, F.T.; Rodrigo, R.; Rodriguez, S.; Romani, P.; Bermejo, M.R.; Sarris, E.T.; Schenk, P.; Schmitt, B.; Schmitz, N.; Schulze-Makuch, D.; Schwingenschuh, K.; Selig, A.; Sicardy, B.; Soderblom, L.; Spilker, L.J.; Stam, D.; Steele, A.; Stephan, K.; Strobel, D.F.; Szego, K.; Szopa,

    2009-01-01

    TandEM was proposed as an L-class (large) mission in response to ESA’s Cosmic Vision 2015–2025 Call, and accepted for further studies, with the goal of exploring Titan and Enceladus. The mission concept is to perform in situ investigations of two worlds tied together by location and properties, whose remarkable natures have been partly revealed by the ongoing Cassini–Huygens mission. These bodies still hold mysteries requiring a complete exploration using a variety of vehicles and instruments. TandEM is an ambitious mission because its targets are two of the most exciting and challenging bodies in the Solar System. It is designed to build on but exceed the scientific and technological accomplishments of the Cassini–Huygens mission, exploring Titan and Enceladus in ways that are not currently possible (full close-up and in situ coverage over long periods of time). In the current mission architecture, TandEM proposes to deliver two medium-sized spacecraft to the Saturnian system. One spacecraft would be an orbiter with a large host of instruments which would perform several Enceladus flybys and deliver penetrators to its surface before going into a dedicated orbit around Titan alone, while the other spacecraft would carry the Titan in situ investigation components, i.e. a hot-air balloon (Montgolfière) and possibly several landing probes to be delivered through the atmosphere.

  13. Low-Latitude Ethane Rain on Titan

    Science.gov (United States)

    Dalba, Paul A.; Buratti, Bonnie J.; Brown, R. H.; Barnes, J. W.; Baines, K. H.; Sotin, C.; Clark, R. N.; Lawrence, K. J.; Nicholson, P. D.

    2012-01-01

    Cassini ISS observed multiple widespread changes in surface brightness in Titan's equatorial regions over the past three years. These brightness variations are attributed to rainfall from cloud systems that appear to form seasonally. Determining the composition of this rainfall is an important step in understanding the "methanological" cycle on Titan. I use data from Cassini VIMS to complete a spectroscopic investigation of multiple rain-wetted areas. I compute "before-and-after" spectral ratios of any areas that show either deposition or evaporation of rain. By comparing these spectral ratios to a model of liquid ethane, I find that the rain is most likely composed of liquid ethane. The spectrum of liquid ethane contains multiple absorption features that fall within the 2-micron and 5-micron spectral windows in Titan's atmosphere. I show that these features are visible in the spectra taken of Titan's surface and that they are characteristically different than those in the spectrum of liquid methane. Furthermore, just as ISS saw the surface brightness reverting to its original state after a period of time, I show that VIMS observations of later flybys show the surface composition in different stages of returning to its initial form.

  14. Montgolfiere balloon missions from Mars and Titan

    Science.gov (United States)

    Jones, Jack A.

    2005-01-01

    Montgolfieres, which are balloons that are filled with heated ambient atmospheric gas, appear promising for the exploration of Mars as well as of Saturn's moon, Titan. On Earth, Montgolfieres are also known as 'hot air balloons'. Commercial versions are typically heated by burning propane, although a number of radiant and solar-heated Montgolfieres have been flown on earth by CNES.

  15. Impurities in barium titanate posistor ceramics

    Czech Academy of Sciences Publication Activity Database

    Korniyenko, S. M.; Bykov, I. P.; Glinchuk, M. J.; Laguta, V. V.; Belous, A. G.; Jastrabík, Lubomír

    2000-01-01

    Roč. 239, - (2000), s. 1209-1218 ISSN 0015-0193 Institutional research plan: CEZ:AV0Z1010914 Keywords : barium titanate phase transition * ESR * positive temperature coefficient of resistivity Subject RIV: BM - Solid Matter Physics ; Magnetism Impact factor: 0.547, year: 2000

  16. Radiation effects in uranium-niobium titanates

    International Nuclear Information System (INIS)

    Lian, J.; Wang, S.X.; Wang, L.M.; Ewing, R.C.

    2000-01-01

    Pyrochlore is an important actinide host phase proposed for the immobilization of high level nuclear wastes and excess weapon plutonium.[1] Synthetic pyrochlore has a great variety of chemical compositions due to the possibility of extensive substitutions in the pyrochlore structure.[2] During the synthesis of pyrochlore, additional complex titanate phases may form in small quantities. The response of these phases to radiation damage must be evaluated because volume expansion of minor phases may cause micro-fracturing. In this work, two complex uranium-niobium titanates, U 3 NbO 9.8 (U-rich titanate) and Nb 3 UO 10 (Nb-rich titanate) were synthesized by the alkoxide/nitrate route at 1300 deg. C under an argon atmosphere. The phase composition and structure were analyzed by EDS, BSE, XRD, EMPA and TEM techniques. An 800 KeVKr 2+ irradiation was performed using the IVEM-Tandem Facility at Argonne National Laboratory in a temperature range from 30 K to 973 K. The radiation effects were observed by in situ TEM

  17. Magnetic susceptibility of scandium-hydrogen and lutetium-hydrogen solid-solution alloys from 2 to 3000K

    International Nuclear Information System (INIS)

    Stierman, R.J.

    1982-12-01

    Results for pure Sc show that the maximum and minimum in the susceptibility discovered earlier are enhanced as the impurity level of iron in scandium decreases. The Stoner enhancement factor, calculated from low-temperature heat capacity data, susceptibility data, and band-structure calculations show Sc to be a strongly enhanced paramagnet. Below 2 0 K, the magnetic anisotropy between the hard and easy directions of scandium decreases linearly with decreasing temperature, tending toward zero at 0 K. The large increase in the susceptibility of Sc at lower temperatures indicates magnetic ordering. Pure Lu and Lu-H alloys showed an anisotropy in susceptibility vs orientation; thus the samples were not random polycrystalline samples. Pure Lu shows the shallow maximum and minimum, but the increase in susceptibility at low temperatures is larger than previously observed. The susceptibility-composition dependence of the Lu-H alloys also did not match other data. The susceptibility-composition dependence does not match the composition dependence of the electronic specific heat constant below 150 K, showing the electronic specific heat is being affected by terms other than phonon-electron and pure electron-electron interactions

  18. A green synthesis of a layered titanate, potassium lithium titanate; lower temperature solid-state reaction and improved materials performance

    International Nuclear Information System (INIS)

    Ogawa, Makoto; Morita, Masashi; Igarashi, Shota; Sato, Soh

    2013-01-01

    A layered titanate, potassium lithium titanate, with the size range from 0.1 to 30 µm was prepared to show the effects of the particle size on the materials performance. The potassium lithium titanate was prepared by solid-state reaction as reported previously, where the reaction temperature was varied. The reported temperature for the titanate preparation was higher than 800 °C, though 600 °C is good enough to obtain single-phase potassium lithium titanate. The lower temperature synthesis is cost effective and the product exhibit better performance as photocatalysts due to surface reactivity. - Graphical abstract: Finite particle of a layered titanate, potassium lithium titanate, was prepared by solid-state reaction at lower temperature to show modified materials performance. Display Omitted - Highlights: • Potassium lithium titanate was prepared by solid-state reaction. • Lower temperature reaction resulted in smaller sized particles of titanate. • 600 °C was good enough to obtain single phased potassium lithium titanate. • The product exhibited better performance as photocatalyst

  19. Unstable Titan-generated Rayleigh-Taylor Lakes Impact Ice

    Science.gov (United States)

    Umurhan, O. M.; Korycansky, D. G.; Zahnle, K. J.

    2014-12-01

    The evolution of surface morphology on Titan, Triton, and other worlds is strongly influenced by the interplay of various fluid dynamical processes. Specifically, overturning instabilities can easily arise due to the special circumstances of landform evolution that probably occurred on these worlds. On Titan, large impacts that formed basins like Menrva crater (and possibly Hotei Regio) would have generated impact-melt ice lakes unstably arranged over less dense ice. Cantaloupe terrains, for example as seen on Triton, may be the result of condensation of volatiles (methane, nitrogen) leading to unstably stratified layers of different compositions and densities. In each of these cases, Rayleigh-Taylor instabilities leading to large scale diapirism may be at play. In addition to the dynamics of these instabilities, other physical effects (e.g. heat diffusion, freezing/melting, porosity, temperature dependent viscosity) likely play an important role in the evolution of these features. In this ongoing study, we examine the properties of unstably stratified fluids in which the lower less-dense ice has a temperature dependent viscosity. Surprisingly, we find that there exists an optimal disturbance length scale corresponding to the fastest growth of the Rayleigh-Taylor instability. For unstably stratified layers of water (low viscosity heavy liquid lying above an ice whose viscosity increases with depth) the fastest growing mode corresponds to 40-60 km scales with overturn times of approximately 100 days. We present a detailed numerical stability analysis in a corresponding Boussinessq model (in the creeping flow limit) incorporating thermal conduction and latent heat release and we examine the stability properties surveying a variety of parameters. We have also developed a two-dimensional numerical code (a hybrid spectral/compact-differencing scheme) to model the evolution of such systems for which we shall present preliminary numerical results depicting the outcome of

  20. Characterizing the Upper Atmosphere of Titan using the Titan Global Ionosphere- Thermosphere Model: Nitrogen and Methane.

    Science.gov (United States)

    Bell, J. M.; Waite, J. H.; Bar-Nun, A.; Bougher, S. W.; Ridley, A. J.; Magee, B.

    2008-12-01

    Recently, a great deal of effort has been put forth to explain the Cassini Ion-Neutral Mass Spectrometer (Waite et al [2004]) in-situ measurements of Titan's upper atmosphere (e.g. Muller-Wodarg [2008], Strobel [2008], Yelle et al [2008]). Currently, the community seems to agree that large amounts of CH4 are escaping from Titan's upper atmosphere at a rate of roughly 2.0 x 1027 molecules of CH4/s (3.33 x 1028 amu/s), representing a significant mass source to the Kronian Magnetosphere. However, such large escape fluxes from Titan are currently not corroborated by measurements onboard the Cassini Spacecraft. Thus, we posit another potential scenario: Aerosol depletion of atmospheric methane. Using the three-dimensional Titan Global Ionosphere-Thermosphere Model (T-GITM) (Bell et al [2008]), we explore the possible removal mechanisms of atmospheric gaseous constituents by these aerosols. Titan simulations are directly compared against Cassini Ion-Neutral Mass Spectrometer in-situ densities of N2 and CH4. From this work, we can then compare and contrast this aerosol depletion scenario against the currently posited hydrodynamic escape scenario, illustrating the merits and shortcomings of both.

  1. Isotherms of ion exchange on titanates of alkaline metals

    International Nuclear Information System (INIS)

    Fillina, L.P.; Belinskaya, F.A.

    1986-01-01

    Present article is devoted to isotherms of ion exchange on titanates of alkaline metals. Therefore, finely dispersed hydrated titanates of alkaline metals (lithium, sodium, potassium) with ion exchange properties are obtained by means of alkaline hydrolysis of titanium chloride at high ph rates. Sorption of cations from salts solution of Li 2 SO 4 , NaNO 3 , Ca(NO 3 ) 2 , AgNO 3 by titanates is studied.

  2. Description of tritium release from lithium titanate at constant temperature

    Energy Technology Data Exchange (ETDEWEB)

    Pena, L; Lagos, S; Jimenez, J; Saravia, E [Comision Chilena de Energia Nuclear, Santiago (Chile)

    1998-03-01

    Lithium Titanate Ceramics have been prepared by the solid-state route, pebbles and pellets were fabricated by extrusion and their microstructure was characterized in our laboratories. The ceramic material was irradiated in the La Reina Reactor, RECH-1. A study of post-irradiation annealing test, was performed measuring Tritium release from the Lithium Titanate at constant temperature. The Bertone`s method modified by R. Verrall is used to determine the parameters of Tritium release from Lithium Titanate. (author)

  3. Coupled atmosphere-ocean models of Titan's past

    Science.gov (United States)

    Mckay, Christopher P.; Pollack, James B.; Lunine, Jonathan I.; Courtin, Regis

    1993-01-01

    The behavior and possible past evolution of fully coupled atmosphere and ocean model of Titan are investigated. It is found that Titan's surface temperature was about 20 K cooler at 4 Gyr ago and will be about 5 K warmer 0.5 Gyr in the future. The change in solar luminosity and the conversion of oceanic CH4 to C2H6 drive the evolution of the ocean and atmosphere over time. Titan appears to have experienced a frozen epoch about 3 Gyr ago independent of whether an ocean is present or not. This finding may have important implications for understanding the inventory of Titan's volatile compounds.

  4. History and challenges of barium titanate: Part I

    Directory of Open Access Journals (Sweden)

    Vijatović M.M.

    2008-01-01

    Full Text Available Barium titanate is the first ferroelectric ceramics and a good candidate for a variety of applications due to its excellent dielectric, ferroelectric and piezoelectric properties. Barium titanate is a member of a large family of compounds with the general formula ABO3 called perovskites. Barium titanate can be prepared using different methods. The synthesis method depends on the desired characteristics for the end application. The used method has a significant influence on the structure and properties of barium titanate materials. In this review paper, Part I contains a study of the BaTiO3 structure and frequently used synthesis methods.

  5. The thermal structure of Titan's atmosphere

    Science.gov (United States)

    Mckay, Christopher P.; Pollack, James B.; Courtin, Regis

    1989-01-01

    The present radiative-convective model of the Titan atmosphere thermal structure obtains the solar and IR radiation in a series of spectral intervals with vertical resolution. Haze properties have been determined with a microphysics model encompassing a minimum of free parameters. It is determined that gas and haze opacity alone, using temperatures established by Voyager observations, yields a model that is within a few percent of the radiative convective balance throughout the Titan atmosphere. Model calculations of the surface temperature are generally colder than the observed value by 5-10 K; better agreement is obtained through adjustment of the model parameters. Sunlight absorption by stratospheric haze and pressure-induced gas opacity in the IR are the most important thermal structure-controlling factors.

  6. Heat capacity measurements on dysprosium titanate

    International Nuclear Information System (INIS)

    Kandan, R.; Prabhakara Reddy, B.; Panneerselvam, G.; Nagarajan, K.

    2014-01-01

    Dysprosium titanate is considered as a candidate material for use in the control rods of future nuclear reactors. The Dy 2 TiO 5 compound was prepared by solid-state synthesis and characterized by XRD technique. The high temperature enthalpy increments of dysprosium titanates have been measured for the first time by employing the method of inverse drop calorimetry in the temperature range 748-1645 K by using high temperature drop calorimeter. The calorimeter, the method of measurement and the procedure adopted for enthalpy increment measurements and analysis of the measured data to compute thermodynamic functions have been described elsewhere. The measured enthalpy increments were fitted to polynomial in temperature by using the least squares method. The fit equation in the temperature range from 298 to 1800 K is given

  7. Texturing of sodium bismuth titanate-barium titanate ceramics by templated grain growth

    Science.gov (United States)

    Yilmaz, Huseyin

    2002-01-01

    Sodium bismuth titanate modified with barium titanate, (Na1/2Bi 1/2)TiO3-BaTiO3 (NBT-BT), is a candidate lead-free piezoelectric material which has been shown to have comparatively high piezoelectric response. In this work, textured (Na1/2Bi1/2)TiO 3-BaTiO3 (5.5mol% BaTiO3) ceramics with pc (where pc denotes the pseudocubic perovskite cell) orientation were fabricated by Templated Grain Growth (TGG) or Reactive Templated Grain Growth (RTGG) using anisotropically shaped template particles. In the case of TGG, molten salt synthesized SrTiO3 platelets were tape cast with a (Na1/2Bi1/2)TiO3-5.5mol%BaTiO3 powder and sintered at 1200°C for up to 12 hours. For the RTGG approach, Bi4Ti3O12 (BiT) platelets were tape cast with a Na2CO3, Bi2O3, TiO 2, and BaCO3 powder mixture and reactively sintered. The TGG approach using SrTiO3 templates gave stronger texture along [001] compared to the RTGG approach using BiT templates. The textured ceramics were characterized by X-ray and electron backscatter diffraction for the quality of texture. The texture function was quantified by the Lotgering factor, rocking curve, pole figures, inverse pole figures, and orientation imaging microscopy. Electrical and electromechanical property characterization of randomly oriented and pc textured (Na1/2Bi1/2)TiO 3-5.5 mol% BaTiO3 rhombohedral ceramics showed 0.26% strain at 70 kV/cm, d33 coefficients over 500 pC/N have been obtained for highly textured samples (f ˜ 90%). The piezoelectric coefficient from Berlincourt was d33 ˜ 200 pC/N. The materials show considerable hysteresis. The presence of hysteresis in the unipolar-electric field curve is probably linked to the ferroelastic phase transition seen in the (Na 1/2Bi1/2)TiO3 system on cooling from high temperature at ˜520°C. The macroscopic physical properties (remanent polarization, dielectric constant, and piezoelectric coefficient) of random and textured ([001] pc) rhombohedral perovskites were estimated by linear averaging of single

  8. Big Impacts and Transient Oceans on Titan

    Science.gov (United States)

    Zahnle, K. J.; Korycansky, D. G.; Nixon, C. A.

    2014-01-01

    We have studied the thermal consequences of very big impacts on Titan [1]. Titan's thick atmosphere and volatile-rich surface cause it to respond to big impacts in a somewhat Earth-like manner. Here we construct a simple globally-averaged model that tracks the flow of energy through the environment in the weeks, years, and millenia after a big comet strikes Titan. The model Titan is endowed with 1.4 bars of N2 and 0.07 bars of CH4, methane lakes, a water ice crust, and enough methane underground to saturate the regolith to the surface. We assume that half of the impact energy is immediately available to the atmosphere and surface while the other half is buried at the site of the crater and is unavailable on time scales of interest. The atmosphere and surface are treated as isothermal. We make the simplifying assumptions that the crust is everywhere as methane saturated as it was at the Huygens landing site, that the concentration of methane in the regolith is the same as it is at the surface, and that the crust is made of water ice. Heat flow into and out of the crust is approximated by step-functions. If the impact is great enough, ice melts. The meltwater oceans cool to the atmosphere conductively through an ice lid while at the base melting their way into the interior, driven down in part through Rayleigh-Taylor instabilities between the dense water and the warm ice. Topography, CO2, and hydrocarbons other than methane are ignored. Methane and ethane clathrate hydrates are discussed quantitatively but not fully incorporated into the model.

  9. The key to Mars, Titan and beyond?

    International Nuclear Information System (INIS)

    Zubrin, R.M.

    1990-01-01

    This paper discusses the use of nuclear rockets using indigenous Mars propellants for future missions to Mars and Titan, which would drastically reduce the mass and cost of the mission while increasing its capability. Special attention is given to the CO2-powered nuclear rocket using indigenous Martian fuel (NIMF) vehicle for hopping around on Mars. If water is available on Mars, it could make a NIMF propellant yielding an exhaust velocity of 3.4 km/sec, good enough to allow a piloted NIMF spacecraft to ascent from the surface of Mars and propel itself directly to LEO; if water is available on Phobos, a NIMF spacecraft could travel to earth orbit and then back to Phobos or Mars without any additional propellant from earth. One of the many exciting missions beyond Mars that will be made possible by NIMF technology is the exploration of Saturn's moon Titan. A small automated NIMF Titan explorer, with foldout wings and a NERVA (Nuclear Engine for Rocket Vehicle Applications) engine, is proposed

  10. Investigations of the Structure of Titanate Nanoscrolls

    International Nuclear Information System (INIS)

    Sheppard, D.A.; Buckley, C.E.

    2005-01-01

    Full text: Nanosized materials have attracted much research lately due to their unique properties and their potential application in nanoelectronic and optoelectronic devices. Nanostructured materials have also sparked interest as possible hydrogen storage candidates. Research at Curtin University has shown titanate nanoscrolls to absorb modest amounts of hydrogen at low temperatures. Whether or not this capacity can be improved will be dependent on a thorough understanding of the structure and the way it interacts with hydrogen. Titanate nanoscrolls are made via a soft chemical process that involves ageing TiO 2 powder in a concentrated NaOH solution. The resultant nanoscrolls, once filtered and washed, are typically 8-10 nm in diameter and hundreds of nanometers long. The walls consist of 3-5 layers and the diameter of the hollow centre is typically 5 nm. A number of different structures have been assigned to nanoscrolls produced via the soft chemical process. These include anatase, H 2 Ti 3 O 7 , lepidocrocite-type structure and H 2 Ti 4 O 9 .H 2 O. Many of these structures are similar, consisting of titanate type layers, and qualitatively reproduce the X-ray diffraction data. However, preliminary data suggests that these structures are inconsistent with neutron diffraction data. Here we attempt a more quantitative analysis of the structure than those published previously using neutron and X-ray diffraction. (authors)

  11. Titanate nanotube coatings on biodegradable photopolymer scaffolds

    Energy Technology Data Exchange (ETDEWEB)

    Beke, S., E-mail: szabolcs.beke@iit.it [Department of Nanophysics, Istituto Italiano di Tecnologia, via Morego 30, 16163 Genova (Italy); Kőrösi, L. [Department of Biotechnology, Nanophage Therapy Center, Enviroinvest Corporation, Kertváros u. 2, H-7632, Pécs (Hungary); Scarpellini, A. [Department of Nanochemistry, Istituto Italiano di Tecnologia, via Morego 30, 16163 Genova (Italy); Anjum, F.; Brandi, F. [Department of Nanophysics, Istituto Italiano di Tecnologia, via Morego 30, 16163 Genova (Italy)

    2013-05-01

    Rigid, biodegradable photopolymer scaffolds were coated with titanate nanotubes (TNTs) by using a spin-coating method. TNTs were synthesized by a hydrothermal process at 150 °C under 4.7 bar ambient pressure. The biodegradable photopolymer scaffolds were produced by mask-assisted excimer laser photocuring at 308 nm. For scaffold coating, a stable ethanolic TNT sol was prepared by a simple colloid chemical route without the use of any binding compounds or additives. Scanning electron microscopy along with elemental analysis revealed that the scaffolds were homogenously coated by TNTs. The developed TNT coating can further improve the surface geometry of fabricated scaffolds, and therefore it can further increase the cell adhesion. Highlights: ► Biodegradable scaffolds were produced by mask-assisted UV laser photocuring. ► Titanate nanotube deposition was carried out without binding compounds or additives. ► The titanate nanotube coating can further improve the surface geometry of scaffolds. ► These reproducible platforms will be of high importance for biological applications.

  12. Modified titanate perovskites in photocatalytic water splitting

    Energy Technology Data Exchange (ETDEWEB)

    Wlodarczak, M.; Ludwiczak, M.; Laniecki, M. [A. Mickiewicz Univ. (Poland)

    2010-07-01

    Received materials have structure of perovskite, what was shown by XRD diffraction patterns. Perovskite structure is present in all samples with strontium, barium and one sample with calcium. Moreover, received barium and strontium titanate are very similar to pattern materials. XRD results show, that temperature 500 C is too low to create perovskite structure in CaTiO{sub 3}. However, it is high enough in case of SrTiO{sub 3} and BaTiO{sub 3}. One regularity is obvious, surface area increases for samples calcined in lower temperature. There is a connection between surface area and dispersion of platinum. Both of them reach the greatest value to the calcium titanate. Catalytic activity was shown by all of received samples. Measurable values were received to samples calcined in 700 C. Calcium titanate had the best catalytic activity, both an amount of hydrogen and a ratio of hydrogen to platinum. There is one regularity to all samples, the ration of hydrogen to platinum increase when amount of platinum decrease. (orig.)

  13. Barium Titanate Nanoparticles for Biomarker Applications

    International Nuclear Information System (INIS)

    Matar, O; Hondow, N S; Brydson, R M D; Milne, S J; Brown, A P; Posada, O M; Wälti, C; Saunders, M; Murray, C A

    2015-01-01

    A tetragonal crystal structure is required for barium titanate nanoparticles to exhibit the nonlinear optical effect of second harmonic light generation (SHG) for use as a biomarker when illuminated by a near-infrared source. Here we use synchrotron XRD to elucidate the tetragonal phase of commercially purchased tetragonal, cubic and hydrothermally prepared barium titanate (BaTiO 3 ) nanoparticles by peak fitting with reference patterns. The local phase of individual nanoparticles is determined by STEM electron energy loss spectroscopy (EELS), measuring the core-loss O K-edge and the Ti L 3 -edge energy separation of the t 2g , e g peaks. The results show a change in energy separation between the t 2g and e g peak from the surface and core of the particles, suggesting an intraparticle phase mixture of the barium titanate nanoparticles. HAADF-STEM and bright field TEM-EDX show cellular uptake of the hydrothermally prepared BaTiO 3 nanoparticles, highlighting the potential for application as biomarkers. (paper)

  14. Large catchment area recharges Titan's Ontario Lacus

    Science.gov (United States)

    Dhingra, Rajani D.; Barnes, Jason W.; Yanites, Brian J.; Kirk, Randolph L.

    2018-01-01

    We seek to address the question of what processes are at work to fill Ontario Lacus while other, deeper south polar basins remain empty. Our hydrological analysis indicates that Ontario Lacus has a catchment area spanning 5.5% of Titan's surface and a large catchment area to lake surface area ratio. This large catchment area translates into large volumes of liquid making their way to Ontario Lacus after rainfall. The areal extent of the catchment extends to at least southern mid-latitudes (40°S). Mass conservation calculations indicate that runoff alone might completely fill Ontario Lacus within less than half a Titan year (1 Titan year = 29.5 Earth years) assuming no infiltration. Cassini Visual and Infrared Mapping Spectrometer (VIMS) observations of clouds over the southern mid and high-latitudes are consistent with precipitation feeding Ontario's large catchment area. This far-flung rain may be keeping Ontario Lacus filled, making it a liquid hydrocarbon oasis in the relatively dry south polar region.

  15. Titan through Time: Evolution of Titan's Atmosphere and its Hydrocarbon Cycle on the Surface

    Science.gov (United States)

    Gilliam, Ashley E.

    The Introduction and Appendix i-A outline briefly the history of Titan exploration since its discovery by Christiaan Huygens in 1675 through the recent International Mission of Cassini-Huygens.. Chapter 1: This chapter discusses two possible pathways of loss of the two main gases from Titan's post-accretional atmosphere, methane (CH 4) and ammonia (NH3), by the mechanisms of thermal escape and emission from the interior coupled with thermal escape. Chapter 2: In this chapter, a simple photolysis model is created, where the second most abundant component of the present-day Titan atmosphere, methane (CH4), can either escape the atmosphere or undergo photolytic conversion to ethane (C2H6). Chapter 3: This chapter examines different fluvial features on Titan, identified by the Cassini spacecraft, and evaluates the possibilities of channel formation by two mechanisms: dissolution of ice by a concentrated solution of ammonium sulfate, and by mechanical erosion by flow of liquid ammonia and liquid ethane. Chapter 4: This chapter presents: (1) new explicit mathematical solutions of mixed 1st and 2nd order chemical reactions, represented by ordinary differential first-degree and Riccati equations; (2) the computed present-day concentrations of the three gases in Titan's scale atmosphere, treated as at near-steady state; and (3) an analysis of the reported and computed atmospheric concentrations of CH4, CH 3, and C2H6 on Titan, based on the reaction rate parameters of the species, the rate parameters taken as constants representative of their mean values. Chapter 5: This chapter examines the possible reactions of methane formation in terms of the thermodynamic relationships of the reactions that include pure carbon as graphite, the gases H2, CO2, H2 O, and serpentinization and magnetite formation from olivine fayalite. (Abstract shortened by ProQuest.).

  16. Titan AVIATR - Aerial Vehicle for In Situ and Airborne Titan Reconnaissance

    Science.gov (United States)

    Kattenhorn, Simon A.; Barnes, J. W.; McKay, C. P.; Lemke, L.; Beyer, R. A.; Radebaugh, J.; Adamkovics, M.; Atkinson, D. H.; Burr, D. M.; Colaprete, T.; Foch, R.; Le Mouélic, S.; Merrison, J.; Mitchell, J.; Rodriguez, S.; Schaller, E.

    2010-10-01

    Titan AVIATR - Aerial Vehicle for In Situ and Airborne Titan Reconnaissance - is a small (120 kg), nuclear-powered Titan airplane in the Discovery/New Frontiers class based on the concept of Lemke (2008 IPPW). The scientific goals of the mission are designed around the unique flexibility offered by an airborne platform: to explore Titan's diversity of surface landforms, processes, and compositions, as well as to study and measure the atmospheric circulation, aerosols, and humidity. AVIATR would address and surpass many of the science goals of hot-air balloons in Titan flagship studies. The strawman instrument payload is narrowly focused on the stated scientific objectives. The optical remote sensing suite comprises three instruments - an off-nadir high-resolution 2-micron camera, a horizon-looking 5-micron imager, and a 1-6 micron pushbroom near-infrared spectrometer. The in situ instruments include atmospheric structure, a methane humidity sensor, and a raindrop detector. An airplane has operational advantages over a balloon. Its piloted nature allows a go-to capability to image locations of interest in real time, thereby allowing for directed exploration of many features of primary geologic interest: Titan's sand dunes, mountains, craters, channels, and lakes. Subsequent imaging can capture changes in these features during the primary mission. AVIATR can fly predesigned routes, building up large context mosaics of areas of interest before swooping down to low altitude to acquire high-resolution images at 30-cm spatial sampling, similar to that of HiRISE at Mars. The elevation flexibility of the airplane allows us to acquire atmospheric profiles as a function of altitude at any desired location. Although limited by the direct-to-Earth downlink bandwidth, the total scientific data return from AVIATR will be >40 times that returned from Huygens. To maximize the science per bit, novel data storage and downlink techniques will be employed, including lossy compression

  17. Self-Assembled Nanocomposite Organic Polymers with Aluminum and Scandium as Heterogeneous Water-Compatible Lewis Acid Catalysts.

    Science.gov (United States)

    Miyamura, Hiroyuki; Sonoyama, Arisa; Hayrapetyan, Davit; Kobayashi, Shū

    2015-09-01

    While water-compatible Lewis acids have great potential as accessible and environmentally benign catalysts for various organic transformations, efficient immobilization of such Lewis acids while keeping high activity and without leaching of metals even under aqueous conditions is a challenging task. Self-assembled nanocomposite catalysts of organic polymers, carbon black, aluminum reductants, and scandium salts as heterogeneous water-compatible Lewis acid catalysts are described. These catalysts could be successfully applied to various C-C bond-forming reactions without leaching of metals. Scanning transmission electron microscopy analyses revealed that the nanocomposite structure of Al and Sc was fabricated in these heterogeneous catalysts. It is noted that Al species, which are usually decomposed rapidly in the presence of water, are stabilized under aqueous conditions. © 2015 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

  18. Modification of radiation sensitivity by salts of the metals beryllium and indium and the rare earths cerium, lanthanum and scandium

    International Nuclear Information System (INIS)

    Floersheim, G.L.

    1995-01-01

    The LD 50 of 46 salts of metals and rare earths (lanthanoids) was determined in mice. Half the LD 50 of the compounds was then combined with lethal radiation (10.5 Gy) and the modification of survival time was scored. Only the metals beryllium and indium and the rare earths cerium, lanthanum and scandium displayed activity in our assay. There were then tested at a wider range of lower doses and reduced survival time in a dose-dependent fashion. This appears to be compatible with enhancement of radiation sensitivity. The interaction of these metals and rare earths with radiation adds a new facet to their toxicological spectrum and, by enhancing radiation effects, may influence estimates of risk. On the other hand, radiosensitizing properties of the metals may be useful for further development of compounds to be used as adjuncts in specific situations of cancer radiotherapy. 31 refs., 1 fig., 1 tab

  19. AVIATR - Aerial Vehicle for In-situ and Airborne Titan Reconnaissance A Titan Airplane Mission Concept

    Science.gov (United States)

    Barnes, Jason W.; Lemke, Lawrence; Foch, Rick; McKay, Christopher P.; Beyer, Ross A.; Radebaugh, Jani; Atkinson, David H.; Lorenz, Ralph D.; LeMouelic, Stephane; Rodriguez, Sebastien; hide

    2011-01-01

    We describe a mission concept for a stand-alone Titan airplane mission: Aerial Vehicle for In-situ and Airborne Titan Reconnaissance (AVIATR). With independent delivery and direct-to-Earth communications, AVIATR could contribute to Titan science either alone or as part of a sustained Titan Exploration Program. As a focused mission, AVIATR as we have envisioned it would concentrate on the science that an airplane can do best: exploration of Titan's global diversity. We focus on surface geology/hydrology and lower-atmospheric structure and dynamics. With a carefully chosen set of seven instruments-2 near-IR cameras, 1 near-IR spectrometer, a RADAR altimeter, an atmospheric structure suite, a haze sensor, and a raindrop detector-AVIATR could accomplish a significant subset of the scientific objectives of the aerial element of flagship studies. The AVIATR spacecraft stack is composed of a Space Vehicle (SV) for cruise, an Entry Vehicle (EV) for entry and descent, and the Air Vehicle (AV) to fly in Titan's atmosphere. Using an Earth-Jupiter gravity assist trajectory delivers the spacecraft to Titan in 7.5 years, after which the AVIATR AV would operate for a 1-Earth-year nominal mission. We propose a novel 'gravity battery' climb-then-glide strategy to store energy for optimal use during telecommunications sessions. We would optimize our science by using the flexibility of the airplane platform, generating context data and stereo pairs by flying and banking the AV instead of using gimbaled cameras. AVIATR would climb up to 14 km altitude and descend down to 3.5 km altitude once per Earth day, allowing for repeated atmospheric structure and wind measurements all over the globe. An initial Team-X run at JPL priced the AVIATR mission at FY10 $715M based on the rules stipulated in the recent Discovery announcement of opportunity. Hence we find that a standalone Titan airplane mission can achieve important science building on Cassini's discoveries and can likely do so within

  20. Lithium insertion in nanostructured titanates

    NARCIS (Netherlands)

    Borghols, W.J.H.

    2010-01-01

    Upon nano-sizing of insertion compounds several significant changes in Li-insertion behavior have been observed for sizes below approximately 50 nm. Although the origins of the phenomena are interrelated, the changes can be divided in three main observations. (1) The formation of new phases, leading

  1. Lead-free piezoceramics.

    Science.gov (United States)

    Saito, Yasuyoshi; Takao, Hisaaki; Tani, Toshihiko; Nonoyama, Tatsuhiko; Takatori, Kazumasa; Homma, Takahiko; Nagaya, Toshiatsu; Nakamura, Masaya

    2004-11-04

    Lead has recently been expelled from many commercial applications and materials (for example, from solder, glass and pottery glaze) owing to concerns regarding its toxicity. Lead zirconium titanate (PZT) ceramics are high-performance piezoelectric materials, which are widely used in sensors, actuators and other electronic devices; they contain more than 60 weight per cent lead. Although there has been a concerted effort to develop lead-free piezoelectric ceramics, no effective alternative to PZT has yet been found. Here we report a lead-free piezoelectric ceramic with an electric-field-induced strain comparable to typical actuator-grade PZT. We achieved this through the combination of the discovery of a morphotropic phase boundary in an alkaline niobate-based perovskite solid solution, and the development of a processing route leading to highly textured polycrystals. The ceramic exhibits a piezoelectric constant d33 (the induced charge per unit force applied in the same direction) of above 300 picocoulombs per newton (pC N(-1)), and texturing the material leads to a peak d33 of 416 pC N(-1). The textured material also exhibits temperature-independent field-induced strain characteristics.

  2. Yttrium bismuth titanate pyrochlore mixed oxides for photocatalytic hydrogen production

    Energy Technology Data Exchange (ETDEWEB)

    Merka, Oliver

    2012-10-18

    In this work, the sol-gel synthesis of new non-stoichiometric pyrochlore titanates and their application in photocatalytic hydrogen production is reported. Visible light response is achieved by introducing bismuth on the A site or by doping the B site by transition metal cations featuring partially filled d orbitals. This work clearly focusses on atomic scale structural changes induced by the systematical introduction of non-stoichiometry in pyrochlore mixed oxides and the resulting influence on the activity in photocatalytic hydrogen production. The materials were characterized in detail regarding their optical properties and their atomic structure. The pyrochlore structure tolerates tremendous stoichiometry variations. The non-stoichiometry in A{sub 2}O{sub 3} rich compositions is compensated by distortions in the cationic sub-lattice for the smaller Y{sup 3+} cation and by evolution of a secondary phase for the larger Bi{sup 3+} cation on the A site. For TiO{sub 2} rich compositions, the non-stoichiometry leads to a special vacancy formation in the A and optionally O' sites. It is shown that pyrochlore mixed oxides in the yttrium bismuth titanate system represent very active and promising materials for photocatalytic hydrogen production, if precisely and carefully tuned. Whereas Y{sub 2}Ti{sub 2}O{sub 7} yields stable hydrogen production rates over time, the bismuth richer compounds of YBiTi{sub 2}O{sub 7} and Bi{sub 2}Ti{sub 2}O{sub 7} are found to be not stable under irradiation. This drawback is overcome by applying a special co-catalyst system consisting of a precious metal core and a Cr{sub 2}O{sub 3} shell on the photocatalysts.

  3. Preparation of Lead Magnesium Niobate-Lead Zirconate Titanate Films and Their Crystallization Behaviors

    International Nuclear Information System (INIS)

    Tursiloadi, Silvester

    2002-01-01

    The thin films with composition near morpotropic phase boundary (MPB) of the system xPb(Mg 1 /3, Nb 2 /3) O 3 -yPbTiO 3 -zPbZrO 3 (x = 0-0.35, y = 0.47 and z = 0.53), were prepared by sol-gel method. The starting materials were consisted of Pb(iso-OC 3 H 7 ) 2 , Zr(n-OC 4 H 9 ) 4 , Ti(iso-OC 3 H 7 ) 4 , Mg(CH 3 COO) 2 4H 2 O and Nb(OC 2 H 5 ) 5 . The l-propanol was used as solvent. The concentration of PMN-PT-PZ in coating solution was 0.7 M, and the pH of the solution was 4.5. The thin films were prepared by dip coating and spin coating. The crystallization behaviors of the PMN-PT-PZ thin films showed that the formation of perovskite phase at low temperature becomes difficult with increasing the content of PMN. The amounts of pyrochlore and perovskite phase in PMN-PT-PZ films depended on the heating temperatures, and PMN contents. Single-phase perovskite was found for the coated films containing 0 and 12.5 mol% after calculating at 600 o C, 21 mol% after calculating at 700 o C, and 30 mol% after calculating at 750 o C. Single-phase perovskite of coated films will never be found when the content of PMN was 35 mol%

  4. Radiation stability of sodium titanate ion exchange materials

    International Nuclear Information System (INIS)

    Kenna, B.T.

    1980-02-01

    Sodium titanate and sodium titanate loaded macroreticular resin are being considered as ion exchangers to remove 90 Sr and actinides from the large volume of defense waste stored at Hanford Site in Washington. Preliminary studies to determine the radiation effect on Sr +2 and I - capacity of these ion-exchange materials were conducted. Samples of sodium titanate powder, sodium titanate loaded macroreticular resin, as well as the nitrate form of macroreticular anion resin were irradiated with up to 2 x 10 9 Rads of 60 Co gamma rays. Sodium titanate cation capacity decreased about 50% while the sodium titanate loaded macroeticular resin displayed a dramatic decrease in cation capacity when irradiated with 10 8 -10 9 Rad. The latter decrease is tentatively ascribed to radiation damage to the organic portion which subsequently inhibits interaction with the contained sodium titanate. The anion capacity of both macroreticular resin and sodium titanate loaded macroreticular resin exhibited significant decreases with increasing radiation exposure. These results suggest that consideration should be given to the potential effects of radiation degradation if column regeneration is to be used. 5 figures, 2 tables

  5. A Raman Study of Titanate Nanotubes | Liu | South African Journal ...

    African Journals Online (AJOL)

    The effect of the addition of NaOH or KOH on commercial Degussa Titania P25 was investigated using TEM, Raman and in situ Raman spectroscopy. Treatment of titania with conc. NaOH generated a tubular material corresponding to a sodium titanate. An in situ Raman study on the sodium titanate nanotubes as a function ...

  6. Reduced-graphene-oxide-and-strontium-titanate-based double

    Indian Academy of Sciences (India)

    Microwave-absorbing materials based on reduced graphene oxide (r-GO)/ strontium titanate were prepared by embedding in epoxy matrix. R-GO and strontium titanate were synthesized and characterized before composite fabrication. Microstructures of the constituent elements were studied by scanning electron ...

  7. Thermal conductivity reduction in oxygen-deficient strontium titanates

    NARCIS (Netherlands)

    Yu, Choongho; Scullin, Matthew L.; Huijben, Mark; Ramesh, Ramamoorthy; Majumdar, Arun

    2008-01-01

    We report significant thermal conductivity reduction in oxygen-deficient lanthanum-doped strontium titanate (Sr1−xLaxTiO3−δ) films as compared to unreduced strontium titanates. Our experimental results suggest that the oxygen vacancies could have played an important role in the reduction. This could

  8. Processing, microstructure, leaching, and long-term stability studies related to titanate high-level waste forms

    International Nuclear Information System (INIS)

    Dosch, R.G.; Headley, T.J.; Northrup, C.J.; Hlava, P.F.

    1983-05-01

    A process leading to titanate-based waste forms for commercial high-level nuclear waste is described. Radionuclides are fixed on hydrous calcium titanate by ion exchange/sorption reactions and the material is converted to a dense, ceramic form by hot pressing. Transmission electron microscopy-electron microprobe characterization was done to determine the effects of compositional changes and process variations on microstructure. Leaching studies in the range of 22 to 150 0 C and pH 2 to 12 were done to assess the effects of the same variables on leaching behavior. Samples of a reference borosilicate glass waste form were leached under the same conditions to provide a direct comparison between the two waste forms. Lead-ion implantation was used to simulate long-term α-recoil damage in the crystalline titanate phases. Comparison of α-recoil damage in natural minerals with damage induced in synthesized samples of the same mineral suggest that Pb-ion implantation is a valid technique for simulating α-recoil effects. All the titanate phases sustained significant lattice damage at equivalent α-doses of 1 x 10 19 /cm 3 ; however, Rutherford backscattering and transmission electron microscopy studies showed that the damage did not result in significant matrix dissolution in these leaching tests

  9. Maintenance procedures for the TITAN-I and TITAN-II reversed field pinch reactors

    International Nuclear Information System (INIS)

    Grotz, S.P.; Duggan, W.; Krakowski, R.; Najmabadi, F.; Wong, C.P.C.

    1989-01-01

    The TITAN reactor is a compact, high-power-density (neutron wall loading 18 MW/m 2 ) machine, based on the reversed-field-pinch (RFP) confinement concept. Two designs for the fusion power core have been examined: TITAN-I is based on a self-cooled lithium loop with a vanadium-alloy structure for the first wall, blanket and shield; and TITAN-II is based on an aqueous loop-in-pool design with a LiNO 3 solution as the coolant and breeder. The compact design of the TITAN fusion power core, (FPC) reduces the system to a few small and relatively low mass components, making toroidal segmentation of the FPC unnecessary. A single-piece maintenance procedure is possible. The potential advantages of single-piece maintenance procedures are: (1) Short period of down time; (2) improved reliability; (3) no adverse effects resulting from unequal levels of irradiation; and (4) ability to continually modify the FPC design. Increased availability can be expected from a fully pre-tested, single-piece FPC. Pre-testing of the FPC throughout the assembly process and prior to installation into the reactor vault is discussed. (orig.)

  10. Thermal stability of titanate nanorods and titania nanowires formed from titanate nanotubes by heating

    Czech Academy of Sciences Publication Activity Database

    Brunátová, T.; Matěj, Z.; Oleynikov, P.; Vesely, J.; Danis, S.; Popelková, Daniela; Kuzel, R.

    2014-01-01

    Roč. 98, December (2014), s. 26-36 ISSN 1044-5803 Institutional support: RVO:61389013 Keywords : titania nanowires * titanate nanorods * X-ray diffraction Subject RIV: BM - Solid Matter Physics ; Magnetism Impact factor: 1.845, year: 2014

  11. Study of strength properties of semi-finished products from economically alloyed high-strength aluminium-scandium alloys for application in automobile transport and shipbuilding

    Science.gov (United States)

    Baranov, Vladimir; Sidelnikov, Sergey; Zenkin, Evgeny; Frolov, Viktor; Voroshilov, Denis; Yakivyuk, Olga; Konstantinov, Igor; Sokolov, Ruslan; Belokonova, Irina

    2018-04-01

    The results of a study on the strength of rolled products from aluminium alloys doped with scandium under various processing conditions of hot and cold rolling are presented. The regularities of metal flow and the level of strength of deformed semi-finished products from aluminum-scandium alloys are established, depending on the total degree of deformation and the various modes of single reduction during rolling. It is shown that when using one heating of a cast billet to obtain high-quality semi-finished products, the temperature during the rolling process should not be lower than 350-370°, and the total degree of deformation does not exceed 50-60%. It was found that the semi-finished products from alloys with a content of scandium in the range 0.11-0.12% in the deformed state had elevated values of ultimate tensile strength and yield strength of the metal, which allows them to be recommended for industrial production of sheet metal products.

  12. Methane, Ethane, and Nitrogen Stability on Titan

    Science.gov (United States)

    Hanley, J.; Grundy, W. M.; Thompson, G.; Dustrud, S.; Pearce, L.; Lindberg, G.; Roe, H. G.; Tegler, S.

    2017-12-01

    Many outer solar system bodies are likely to have a combination of methane, ethane and nitrogen. In particular the lakes of Titan are known to consist of these species. Understanding the past and current stability of these lakes requires characterizing the interactions of methane and ethane, along with nitrogen, as both liquids and ices. Our cryogenic laboratory setup allows us to explore ices down to 30 K through imaging, and transmission and Raman spectroscopy. Our recent work has shown that although methane and ethane have similar freezing points, when mixed they can remain liquid down to 72 K. Concurrently with the freezing point measurements we acquire transmission or Raman spectra of these mixtures to understand how the structural features change with concentration and temperature. Any mixing of these two species together will depress the freezing point of the lake below Titan's surface temperature, preventing them from freezing. We will present new results utilizing our recently acquired Raman spectrometer that allow us to explore both the liquid and solid phases of the ternary system of methane, ethane and nitrogen. In particular we will explore the effect of nitrogen on the eutectic of the methane-ethane system. At high pressure we find that the ternary creates two separate liquid phases. Through spectroscopy we determined the bottom layer to be nitrogen rich, and the top layer to be ethane rich. Identifying the eutectic, as well as understanding the liquidus and solidus points of combinations of these species, has implications for not only the lakes on the surface of Titan, but also for the evaporation/condensation/cloud cycle in the atmosphere, as well as the stability of these species on other outer solar system bodies. These results will help interpretation of future observational data, and guide current theoretical models.

  13. Composition And Geometry Of Titan'S Dunes

    Science.gov (United States)

    Le Gall, Alice; Janssen, M. A.; Wye, L. C.; Lorenz, R. D.; Radebaugh, J.; Cassini RADAR Team

    2009-09-01

    Fields of linear dunes cover a large portion of Titan's equatorial regions. As the Cassini mission continues, more of them are unveiled and examined by the microwave Titan RADAR Mapper both in the active and passive modes of operation of the instrument and with an increasing variety of observational geometries. In this presentation, we will show that the joint analysis of the SAR (Synthetic Aperture Radar) and radiometry observations of the dunes at closest approach supports the idea of different composition between the dunes and the interdunes. It suggests that the icy bedrock of Titan may be exposed, or partially exposed, in the interdunes. We also see regional differences among dune fields. Dunes are highly directional features; their visibility is controlled by the look direction and the incidence angle. We have developed a backscatter and emissivity model that takes into account the topography of the dunes relative to the geometry of observation as well as the composition of the dunes and interdunes. Compared to observations and, in particular, to multiple observations of areas at the overlap of several swaths, we argue the need for a diffuse scattering mechanism. The presence of ripples in the dunes and/or interdunes might account for the recorded backscatter. In this presentation we will also report the results of the T61 experiment. The T61 HiSAR sequence (on August 25, 2009) was designed to examine a small region of the Shangri-La dune field with a substantial sampling of incidence angles around the direction perpendicular to the dunes long axis. The spot in question was already observed during the T55 SAR swath and the T61 experiment should allow us to determine the slope of the dunes.

  14. Electronic properties of lithium titanate ceramic

    International Nuclear Information System (INIS)

    Padilla-Campos, Luis; Buljan, Antonio

    2001-01-01

    Research on tritium breeder material is fundamental to the development of deuterium-tritium type fusion reactors for producing clean, non contaminating, electrical energy, since only energy and helium, a harmless gas, are produced from the fusion reaction. Lithium titanate ceramic is one of the possible candidates for the tritium breeder material. This last material is thought to form part of the first wall of the nucleus of the reactor which will provide the necessary tritium for the fusion and will also serve as a shield. Lithium titanate has advantageous characteristics compared to other materials. Some of these are low activation under the irradiation of neutrons, good thermal stability, high density of lithium atoms and relatively fast tritium release at low temperatures. However, there are still several physical and chemical properties with respect to the tritium release mechanism and mechanical properties that have not been studied at all. This work presents a theoretical study of the electronic properties of lithium titanate ceramic and the corresponding tritiated material. Band calculations using the Extended H kel Tight-Binding approach were carried out. Results show that after substituting lithium for tritium atoms, the electronic states for the latter appear in the middle of prohibited band gap which it is an indication that the tritiated material should behave as a semiconductor, contrary to Li 2 TiO 3 which is a dielectric isolator. A study was also carried out to determine the energetically most favorable sites for the substitution of lithium for tritium atoms. Additionally, we analyzed possible pathways for the diffusion of a tritium atom within the crystalline structure of the Li 2 TiO 3

  15. Development of methods for the selective separation of scandium, zirconium and tin for radiopharmaceutical applications; Entwicklung von Methoden zur selektiven Trennung von Scandium, Zirkonium und Zinn fuer radiopharmazeutische Anwendungen

    Energy Technology Data Exchange (ETDEWEB)

    Dirks-Fandrei, Carina

    2014-07-01

    The subject of the present work is the development of fast and highly selective methods for the separation and purification of scandium, zirconium and tin radionuclides from potential target materials for use in nuclear medicine. A number of selected resins (TrisKem International) were first characterized with respect to their extraction behaviour towards a large number of cations. Characterization studies were performed in batch experiments by determination of weight distribution ratios D{sub w} and further the influence of interferences on the uptake of these elements was evaluated. Weight distribution ratios were determined in different acids and acid concentrations with main focus on scandium, tin or zirconium. The interference of macro amounts of Calcium and Ti on the Sc extraction was evaluated as well as the interference of macro amounts of Y on the Zr extraction. Best suited uptake conditions were found for Scandium on DGA were determined to be 2.5 M HNO{sub 3} for Ti-Targets and 0.1 M HNO{sub 3} for Calcium-Targets. Otherwise it is also possible to extract Sc with TRU Resin. High uptakes were obtained at 2.5 M HNO{sub 3} for simulated Ti- and Calcium-targets. Separation methods were developed using elution studies; employed conditions were chosen according to parameters evaluated in the batch-experiment. The developed methods allowed separating Sc very rapidly in high purity very rapidly from Ti- or Calcium-targets. For Zr a separation method based on UTEVA Resin has been developed. Following results of batch experiments simulated Y-target solution were loaded onto a UTEVA resin column from 6 M HNO{sub 3}; the elution of Zr could be performed in 0.01 M oxalic acid. Decontamination factors in the order of 10{sup 4}-10{sup 5} could be obtained applying the developed method; the method thus allowed separating Zr in a high purity. Initial testing of a method for the separation of Sn from Cd targets based on the use of TBP Resin showed that the TBP resin seems

  16. Phase 1 Final Report: Titan Submarine

    Science.gov (United States)

    Oleson, Steven R.; Lorenz, Ralph D.; Paul, Michael V.

    2015-01-01

    The conceptual design of a submarine for Saturn's moon Titan was a funded NASA Innovative Advanced Concepts (NIAC) Phase 1 for 2014. The proposal stated the desire to investigate what science a submarine for Titan's liquid hydrocarbon seas might accomplish and what that submarine might look like. Focusing on a flagship class science system (100 kg), it was found that a submersible platform can accomplish extensive science both above and below the surface of the Kraken Mare. Submerged science includes mapping using side-looking sonar, imaging and spectroscopy of the lake, as well as sampling of the lake's bottom and shallow shoreline. While surfaced, the submarine will not only sense weather conditions (including the interaction between the liquid and atmosphere) but also image the shoreline, as much as 2 km inland. This imaging requirement pushed the landing date to Titan's next summer period (2047) to allow for lighted conditions, as well as direct-to-Earth communication, avoiding the need for a separate relay orbiter spacecraft. Submerged and surfaced investigation are key to understanding both the hydrological cycle of Titan as well as gather hints to how life may have begun on Earth using liquid, sediment, and chemical interactions. An estimated 25 Mb of data per day would be generated by the various science packages. Most of the science packages (electronics at least) can be safely kept inside the submarine pressure vessel and warmed by the isotope power system.The baseline 90-day mission would be to sail submerged and surfaced around and through Kraken Mare investigating the shoreline and inlets to evaluate the sedimentary interaction both on the surface and then below. Depths of Kraken have yet to be sensed (Ligeia to the north is thought to be 200 m (656 ft) deep), but a maximum depth of 1,000 m (3,281 ft) for Kraken Mare was assumed for the design). The sub would spend 20 d at the interface between Kraken Mare and Ligeia Mare for clues to the drainage of

  17. Gamma Radiation Effect on Titan Yellow Solutions

    International Nuclear Information System (INIS)

    El-Banna, M.

    2012-01-01

    In the present work, the radiation induced color bleaching of Titan yellow dye (TY) in different solvents has been studied. The color bleaching of the dye solutions upon irradiation was followed spectrophotometrically. The % color bleaching of the dyes in different solvent systems was plotted against different gamma irradiation doses used and was determined and the obtained relationships were found to be linear in most cases. These relationships were used as calibration curves to determine the unknown irradiation dose. The results obtained were reproducible and showed differences from calculated values ranging from 10 % to 15 %

  18. FEI Titan 80-300 STEM

    Directory of Open Access Journals (Sweden)

    Marc Heggen

    2016-02-01

    Full Text Available The FEI Titan 80-300 STEM is a scanning transmission electron microscope equipped with a field emission electron gun, a three-condenser lens system, a monochromator unit, and a Cs probe corrector (CEOS, a post-column energy filter system (Gatan Tridiem 865 ER as well as a Gatan 2k slow scan CCD system. Characterised by a STEM resolution of 80 pm at 300 kV, the instrument was one of the first of a small number of sub-ångström resolution scanning transmission electron microscopes in the world when commissioned in 2006.

  19. Adherence and electrochemical behavior of calcium titanate coatings onto 304 stainless steel substrate

    Energy Technology Data Exchange (ETDEWEB)

    Esguerra A, J.; Aguilar, Y. [Universidad del Valle, Escuela de Ingenieria de Materiales, TPMR, Calle 13 No. 100-00, A. A. 25360 Cali (Colombia); Aperador, W. [Escuela Colombiana de Ingenieria Julio Garavito, Escuela de Ingenieria Mecanica, AK 45 No. 205-59 (Autopista Norte), A. A. 14520 Bogota (Colombia); Alba de Sanchez, N. [Universidad Autonoma de Occidente, Grupo de Investigacion en Ciencia e Ingenieria de Materiales, Calle 25 No. 115-85, A. A. 2790 Cali (Colombia); Bolanos P, G.; Rincon, C., E-mail: johanna.esguerra@univalle.edu.co [Universidad del Cauca, Departamento de Fisica, Laboratorio de Fisica de Bajas Temperaturas, Calle 5 No. 4-70, A. A. 996 Popayan (Colombia)

    2014-07-01

    Calcium titanate has been proposed as a coating for biomedical applications but it has not been reported characterization of adhesion failure mechanisms or electrochemical properties in time. In this work have been studied these properties of a calcium titanate coating growth onto AISI 304 steel deposited by r.f. magnetron sputtering. It was found that the coating has a critical adhesive load of 6.53 ± 0.14 N. With respect to its electrochemical properties potentiodynamic polarization curves show that the calcium titanate coating provides protection to AISI 304 steel. However. EIS indicates that even though metal dissolution occur through the pores in the coating, this leads to the precipitation of salts that block pores; this precipitates layer acts like and additional barrier to the metal dissolution in the system. The coatings deposition was carried out via magnetron sputtering during 4 hours at 500 grades C. The crystal structure of the films was determined by using glancing incident X-ray diffraction. The chemical composition of deposited films was performed by impedance dispersive X-ray spectroscopy (EDX) in the scanning electron microscopy (Jeol JSM-649 OLV Sem), and the grain size and the roughness was obtained using an atomic force microscopy from Asylum Research MFP-3D using a cantilever silicon tip in non-contact mode and calculated by scanning probe image processor. (Author)

  20. Magnetostrictive properties of titanate coupling agent treated Terfenol-D composites

    Energy Technology Data Exchange (ETDEWEB)

    Dong Xufeng, E-mail: dongxf@dlut.edu.cn [School of Materials Science and Engineering, Dalian University of Technology, 116024 Dalian (China); Qi Min [School of Materials Science and Engineering, Dalian University of Technology, 116024 Dalian (China); Guan Xinchun [School of Civil Engineering, Harbin Institute of Technology, 150090 Harbin (China); Li Jinhai [School of Civil Engineering, Dalian University of Technology, 116024 Dalian (China); Ou Jinping [School of Civil Engineering, Harbin Institute of Technology, 150090 Harbin (China); School of Civil Engineering, Dalian University of Technology, 116024 Dalian (China)

    2012-03-15

    As a kind of composites, the bond strength between the polymer matrix and the Terfenol-D particles affects the performance of magnetostrictive composites. By observing the fracture morphologies, the bond strength of the magnetostrictive composites prepared with untreated Terfenol-D was proved weak. Titanate coupling agent was used for particles to improve the bond strength. Contact angle analysis indicates the work of adhesion of the epoxy resin to the treated Terfenol-D is larger than that to the untreated Terfenol-D. Different magnetostrictive composites with 20%, 35% and 50% particle volume fractions were prepared with treated and untreated Terfenol-D particles. Their static and dynamic magnetostriction was tested without pre-stress at room temperature. The results indicate titanate coupling agent treating increases the magnetostrictive properties of magnetostrictive composites, that is probably because the bond strength improves due to the particle treating. - Highlights: Black-Right-Pointing-Pointer Our experimental results indicate the particles and the polymer matrix have poor bonding. Black-Right-Pointing-Pointer The poor bonding prevents the effective transfer of the strain from the particles to the matrix. Black-Right-Pointing-Pointer We used titanate as the coupling agent to improve the bond strength between the particles and the matrix. Black-Right-Pointing-Pointer The results indicate the bond strength does increase as expected. Black-Right-Pointing-Pointer The promotion of the bond strength leads to the increase of magnetostrictive properties.

  1. Adherence and electrochemical behavior of calcium titanate coatings onto 304 stainless steel substrate

    International Nuclear Information System (INIS)

    Esguerra A, J.; Aguilar, Y.; Aperador, W.; Alba de Sanchez, N.; Bolanos P, G.; Rincon, C.

    2014-01-01

    Calcium titanate has been proposed as a coating for biomedical applications but it has not been reported characterization of adhesion failure mechanisms or electrochemical properties in time. In this work have been studied these properties of a calcium titanate coating growth onto AISI 304 steel deposited by r.f. magnetron sputtering. It was found that the coating has a critical adhesive load of 6.53 ± 0.14 N. With respect to its electrochemical properties potentiodynamic polarization curves show that the calcium titanate coating provides protection to AISI 304 steel. However. EIS indicates that even though metal dissolution occur through the pores in the coating, this leads to the precipitation of salts that block pores; this precipitates layer acts like and additional barrier to the metal dissolution in the system. The coatings deposition was carried out via magnetron sputtering during 4 hours at 500 grades C. The crystal structure of the films was determined by using glancing incident X-ray diffraction. The chemical composition of deposited films was performed by impedance dispersive X-ray spectroscopy (EDX) in the scanning electron microscopy (Jeol JSM-649 OLV Sem), and the grain size and the roughness was obtained using an atomic force microscopy from Asylum Research MFP-3D using a cantilever silicon tip in non-contact mode and calculated by scanning probe image processor. (Author)

  2. Titan's Tropopause Temperatures from CIRS: Implications for Stratospheric Methane Cloud Formation

    Science.gov (United States)

    Anderson, C. M.; Samuelson, R. E.; Achterberg, R. K.; Barnes, J. W.; Flasar, F. M.

    2012-01-01

    Analysis of Cassini Composite Infrared Spectrometer (CIRS) far-IR spectra enable the construction of Titan's temperature profile in the altitude region containing the tropopause. Whereas the methane V4 band at 1306/cm (7.7 microns) is the primary opacity source for deducing thermal structure between 100 km and 500 km, N2-N2 collision-induced absorption between 70 and 140/cm (143 microns and 71 microns) is utilized to determine temperatures at Titan's tropopause. Additional opacity due to aerosol and nitrile ices must also be taken into account in this part of the far-IR spectral region. The spectral characteristics of these particulate opacities have been deduced from CIRS limb data at 58degS, 15degS, 15degN, and 85degN. Empirically, the spectral shapes of these opacities appear to be independent of both latitude and altitude below 300 km (Anderson and Samuelson, 2011, Icarus 212, 762-778), justifying the extension of these spectral properties to all latitudes. We find that Titan's tropopause temperature is cooler than the HAS! value of 70.5K by approx. 6K. This leads to the possibility that subsidence at high northern latitudes can cause methane condensation in the winter polar stratosphere. A search for methane clouds in this region is in progress.

  3. Measurements of Dune Parameters on Titan Suggest Differences in Sand Availability

    Science.gov (United States)

    Stewart, Brigitte W.; Radebaugh, Jani

    2014-11-01

    The equatorial region of Saturn’s moon Titan has five large sand seas with dunes similar to large linear dunes on Earth. Cassini Radar SAR swaths have high enough resolution (300 m) to measure dune parameters such as width and spacing, which helps inform us about formation conditions and long-term evolution of the sand dunes. Previous measurements in locations scattered across Titan have revealed an average width of 1.3 km and spacing of 2.7 km, with variations by location. We have taken over 1200 new measurements of dune width and spacing in the T8 swath, a region on the leading hemisphere of Titan in the Belet Sand Sea, between -5 and -9 degrees latitude. We have also taken over 500 measurements in the T44 swath, located on the anti-Saturn hemisphere in the Shangri-La Sand Sea, between 0 and 20 degrees latitude. We correlated each group of 50 measurements with the average distance from the edge of the dune field to obtain an estimate of how position within a dune field affects dune parameters. We found that in general, the width and spacing of dunes decreases with distance from the edge of the dune field, consistent with similar measurements in sand seas on Earth. We suggest that this correlation is due to the lesser availability of sand at the edges of dune fields. These measurements and correlations could be helpful in determining differences in sand availability across different dune fields, and along the entire equatorial region of Titan.

  4. PEROXOTITANATE- AND MONOSODIUM METAL-TITANATE COMPOUNDS AS INHIBITORS OF BACTERIAL GROWTH

    Energy Technology Data Exchange (ETDEWEB)

    Hobbs, D.

    2011-01-19

    Sodium titanates are ion-exchange materials that effectively bind a variety of metal ions over a wide pH range. Sodium titanates alone have no known adverse biological effects but metal-exchanged titanates (or metal titanates) can deliver metal ions to mammalian cells to alter cell processes in vitro. In this work, we test a hypothesis that metal-titanate compounds inhibit bacterial growth; demonstration of this principle is one prerequisite to developing metal-based, titanate-delivered antibacterial agents. Focusing initially on oral diseases, we exposed five species of oral bacteria to titanates for 24 h, with or without loading of Au(III), Pd(II), Pt(II), and Pt(IV), and measuring bacterial growth in planktonic assays through increases in optical density. In each experiment, bacterial growth was compared with control cultures of titanates or bacteria alone. We observed no suppression of bacterial growth by the sodium titanates alone, but significant (p < 0.05, two-sided t-tests) suppression was observed with metal-titanate compounds, particularly Au(III)-titanates, but with other metal titanates as well. Growth inhibition ranged from 15 to 100% depending on the metal ion and bacterial species involved. Furthermore, in specific cases, the titanates inhibited bacterial growth 5- to 375-fold versus metal ions alone, suggesting that titanates enhanced metal-bacteria interactions. This work supports further development of metal titanates as a novel class of antibacterials.

  5. Titan and habitable planets around M-dwarfs.

    Science.gov (United States)

    Lunine, Jonathan I

    2010-01-01

    The Cassini-Huygens mission discovered an active "hydrologic cycle" on Saturn's giant moon Titan, in which methane takes the place of water. Shrouded by a dense nitrogen-methane atmosphere, Titan's surface is blanketed in the equatorial regions by dunes composed of solid organics, sculpted by wind and fluvial erosion, and dotted at the poles with lakes and seas of liquid methane and ethane. The underlying crust is almost certainly water ice, possibly in the form of gas hydrates (clathrate hydrates) dominated by methane as the included species. The processes that work the surface of Titan resemble in their overall balance no other moon in the solar system; instead, they are most like that of the Earth. The presence of methane in place of water, however, means that in any particular planetary system, a body like Titan will always be outside the orbit of an Earth-type planet. Around M-dwarfs, planets with a Titan-like climate will sit at 1 AU--a far more stable environment than the approximately 0.1 AU where Earth-like planets sit. However, an observable Titan-like exoplanet might have to be much larger than Titan itself to be observable, increasing the ratio of heat contributed to the surface atmosphere system from internal (geologic) processes versus photons from the parent star.

  6. Nanosized lithium titanates produced by plasma technique

    International Nuclear Information System (INIS)

    Grabis, J; Orlovs, A; Rasmane, Dz

    2007-01-01

    The synthesis of nanosized lithium titanates is studied by evaporation of coarse grained commercially available titanium and lithium carbonate particles in radio-frequency plasma flow with subsequent controlling formation and growth conditions of product particles. In accordance with the XRD analysis the phase composition of the obtained powders is determined by feeding rate of precursors and strongly by ratio of lithium and titanium. The Li 2 TiO 3 and Li 4 Ti 5 O 12 particles containing small amounts of extra phases were obtained at ratio of Li/Ti = 2 and Li/Ti = 0.8 respectively, feeding rate of precursors being in the range of 0.6-0.9 kg/h. Specific surface area of powders is in the range of 20-40 m2/g depending on concentration of vapours in gas flow and cooling rate of the products. Additional calcination of nanosize particles at 800-900 deg. C improves phase composition of lithium titanates

  7. Storms in the tropics of Titan.

    Science.gov (United States)

    Schaller, E L; Roe, H G; Schneider, T; Brown, M E

    2009-08-13

    Methane clouds, lakes and most fluvial features on Saturn's moon Titan have been observed in the moist high latitudes, while the tropics have been nearly devoid of convective clouds and have shown an abundance of wind-carved surface features like dunes. The presence of small-scale channels and dry riverbeds near the equator observed by the Huygens probe at latitudes thought incapable of supporting convection (and thus strong rain) has been suggested to be due to geological seepage or other mechanisms not related to precipitation. Here we report the presence of bright, transient, tropospheric clouds in tropical latitudes. We find that the initial pulse of cloud activity generated planetary waves that instigated cloud activity at other latitudes across Titan that had been cloud-free for at least several years. These observations show that convective pulses at one latitude can trigger short-term convection at other latitudes, even those not generally considered capable of supporting convection, and may also explain the presence of methane-carved rivers and channels near the Huygens landing site.

  8. Big Bang Cosmic Titanic: Cause for Concern?

    Science.gov (United States)

    Gentry, Robert

    2013-04-01

    This abstract alerts physicists to a situation that, unless soon addressed, may yet affect PRL integrity. I refer to Stanley Brown's and DAE Robert Caldwell's rejection of PRL submission LJ12135, A Cosmic Titanic: Big Bang Cosmology Unravels Upon Discovery of Serious Flaws in Its Foundational Expansion Redshift Assumption, by their claim that BB is an established theory while ignoring our paper's Titanic, namely, that BB's foundational spacetime expansion redshifts assumption has now been proven to be irrefutably false because it is contradicted by our seminal discovery that GPS operation unequivocally proves that GR effects do not produce in-flight photon wavelength changes demanded by this central assumption. This discovery causes the big bang to collapse as quickly as did Ptolemaic cosmology when Copernicus discovered its foundational assumption was heliocentric, not geocentric. Additional evidence that something is amiss in PRL's treatment of LJ12135 comes from both Brown and EiC Gene Spouse agreeing to meet at my exhibit during last year's Atlanta APS to discuss this cover-up issue. Sprouse kept his commitment; Brown didn't. Question: If Brown could have refuted my claim of a cover-up, why didn't he come to present it before Gene Sprouse? I am appealing LJ12135's rejection.

  9. Ionization balance in Titan's nightside ionosphere

    Science.gov (United States)

    Vigren, E.; Galand, M.; Yelle, R. V.; Wellbrock, A.; Coates, A. J.; Snowden, D.; Cui, J.; Lavvas, P.; Edberg, N. J. T.; Shebanits, O.; Wahlund, J.-E.; Vuitton, V.; Mandt, K.

    2015-03-01

    Based on a multi-instrumental Cassini dataset we make model versus observation comparisons of plasma number densities, nP = (nenI)1/2 (ne and nI being the electron number density and total positive ion number density, respectively) and short-lived ion number densities (N+, CH2+, CH3+, CH4+) in the southern hemisphere of Titan's nightside ionosphere over altitudes ranging from 1100 and 1200 km and from 1100 to 1350 km, respectively. The nP model assumes photochemical equilibrium, ion-electron pair production driven by magnetospheric electron precipitation and dissociative recombination as the principal plasma neutralization process. The model to derive short-lived-ion number densities assumes photochemical equilibrium for the short-lived ions, primary ion production by electron-impact ionization of N2 and CH4 and removal of the short-lived ions through reactions with CH4. It is shown that the models reasonably reproduce the observations, both with regards to nP and the number densities of the short-lived ions. This is contrasted by the difficulties in accurately reproducing ion and electron number densities in Titan's sunlit ionosphere.

  10. Discovery of Temperate Latitude Clouds on Titan

    Science.gov (United States)

    Roe, H. G.; Bouchez, A. H.; Trujillo, C. A.; Schaller, E. L.; Brown, M. E.

    2005-01-01

    Until now, all the clouds imaged in Titan's troposphere have been found at far southern latitudes (60°-90° south). The occurrence and location of these clouds is thought to be the result of convection driven by the maximum annual solar heating of Titan's surface, which occurs at summer solstice (2002 October) in this south polar region. We report the first observations of a new recurring type of tropospheric cloud feature, confined narrowly to ~40° south latitude, which cannot be explained by this simple insolation hypothesis. We propose two classes of formation scenario, one linked to surface geography and the other to seasonally evolving circulation, which will be easily distinguished with continued observations over the next few years. Some of the data presented herein were obtained at the W. M. Keck Observatory, which is operated as a scientific partnership among the California Institute of Technology, the University of California, and the National Aeronautics and Space Administration. The Observatory was made possible by the generous financial support of the W. M. Keck Foundation. Based on observations obtained at the Gemini Observatory, which is operated by the Association of Universities for Research in Astronomy, Inc., under a cooperative agreement with the NSF on behalf of the Gemini partnership: the National Science Foundation (US), the Particle Physics and Astronomy Research Council (UK), the National Research Council (Canada), CONICYT (Chile), the Australian Research Council (Australia), CNPq (Brazil), and CONICET (Argentina).

  11. Titan Coupled Surface/Atmosphere Retrievals

    Science.gov (United States)

    West, R. A.; Pitman, K. M.

    2009-05-01

    Titan's thick haze obscures its surface at visible wavelengths and hinders surface photometric studies in the near-infrared. The large vertical extent of the haze produces two effects which require radiative transfer analysis beyond the capability of plane-parallel multi-scatter models. Haze aerosols extend to altitudes above 500 km and require a spherical-shell RT algorithm close to the limb or terminator. Even near nadir viewing, horizontal scattering at spatial scales less than a few hundred km requires a code capable of simulating the adjacency effect. The adjacency effect will reduce contrast more for small spatial scales than for large spatial scales, and the amount of contrast reduction depends on many factors (haze optical thickness, vertical distribution, single scattering albedo, scattering geometry, spatial scale). Titan's haze is strongly forward scattering even near 1-µm wavelength and many RT codes do a poor job. Fortunately the problem is more tractable at longer wavelengths. We show how data from the Cassini VIMS and ISS instruments can be used to understand surface contrast and atmospheric haze properties.

  12. Exfoliation and thermal transformations of Nb-substituted layered titanates

    DEFF Research Database (Denmark)

    Song, H.; Sjåstad, Anja O.; Fjellvåg, Helmer

    2011-01-01

    Single-layer Nb-substituted titanate nanosheets of ca. 1 nm thickness were obtained by exfoliating tetrabutylammonium (TBA)-intercalated Nb-substituted titanates in water. AFM images and turbidity measurements reveal that the exfoliated nanosheets crack and corrugate when sonicated. Upon heating...... factors for increasing the transformation temperatures for conversion of the nanosheets to anatase and finally into rutile. It is further tempting to link the delay in crystallization to morphology limitations originating from the nanosheets. The present work shows that layered Nb-titanates...

  13. Progressive Climate Change on Titan: Implications for Habitability

    Science.gov (United States)

    Moore, J. M.; A. D. Howard

    2014-01-01

    Titan's landscape is profoundly shaped by its atmosphere and comparable in magnitude perhaps with only the Earth and Mars amongst the worlds of the Solar System. Like the Earth, climate dictates the intensity and relative roles of fluvial and aeolian activity from place to place and over geologic time. Thus Titan's landscape is the record of climate change. We have investigated three broad classes of Titan climate evolution hypotheses (Steady State, Progressive, and Cyclic), regulated by the role, sources, and availability of methane. We favor the Progressive hypotheses, which we will outline here, then discuss their implication for habitability.

  14. Cosmic-rays induced Titan tholins and their astrobiological significances

    Science.gov (United States)

    Kobayashi, Kensei; Taniuchi, Toshinori; Hosogai, Tomohiro; Kaneko, Takeo; Takano, Yoshinori; Khare, Bishun; McKay, Chris

    Titan is the largest satellite of Saturn. It is quite unique satellite since it has a dense atmosphere composed of nitrogen and methane, and has been sometimes considered as a model of primitive Earth. In Titan atmosphere, a wide variety of organic compounds and mists made of complex organics. Such solid complex organics are often referred to as tholins. A number of laboratory experiments simulating reactions in Titan atmosphere have been conducted. In most of them, ultraviolet light and discharges (simulating actions of electrons in Saturn magnetosphere) were used, which were simulation of the reactions in upper dilute atmosphere of Titan. We examined possible formation of organic compounds in the lower dense atmosphere of Titan, where cosmic rays are major energies. A Mixture of 35 Torr of methane and 665 Torr of nitrogen was irradiated with high-energy protons (3 MeV) from a van de Graaff accelerator (TIT, Japan) or from a Tandem accelerator (TIARA, QUBS, JAEA, Japan). In some experiments, 13 C-labelled methane was used. We also performed plasma discharges in a mixture of methane (10 %) and nitrogen (90 %) to simulate the reactions in the upper atmosphere of Titan. Solid products by proton irradiation and those by plasma discharges are hereafter referred to as PI-tholins and PD-tholins, respectively. The resulting PI-tholins were observed with SEM and AFM. They were characterized by pyrolysis-GC/MS, gel permeation chromatography, FT-IR, etc. Amino acids in PI-and PD-tholins were analyzed by HPLC, GC/MS and MALDI-TOF-MS after acid hydrolysis. 18 O-Labelled water was used in some cases during hydrolysis. Filamentary and/or globular-like structures were observed by SEM and AFM. By pyrolysis-GC/MS of PI-tholins, ammonia and hydrogen cyanide were detected, which was the same as the results obtained in Titan atmosphere during the Huygens mission. A wide variety of amino acids were detected after hydrolysis of both tholins. It was proved that oxygen atoms in the amino

  15. Decontamination of 2-chloroethyl ethylsulfide using titanate nanoscrolls

    Science.gov (United States)

    Kleinhammes, Alfred; Wagner, George W.; Kulkarni, Harsha; Jia, Yuanyuan; Zhang, Qi; Qin, Lu-Chang; Wu, Yue

    2005-08-01

    Titanate nanoscrolls, a recently discovered variant of TiO 2 nanocrystals, are tested as reactive sorbent for chemical warfare agent (CWA) decontamination. The large surface area of the uncapped tubules provides the desired rapid absorption of the contaminant while water molecules, intrinsic constituents of titanate nanoscrolls, provide the necessary chemistry for hydrolytic reaction. In this study the decomposition of 2-chloroethyl ethylsulfide (CEES), a simulant for the CWA mustard, was monitored using 13C NMR. The NMR spectra reveal reaction products as expected from the hydrolysis of CEES. This demonstrates that titanate nanoscrolls could potentially be employed as a decontaminant for CWAs.

  16. Mission Techniques for Exploring Saturn's icy moons Titan and Enceladus

    Science.gov (United States)

    Reh, Kim; Coustenis, Athena; Lunine, Jonathan; Matson, Dennis; Lebreton, Jean-Pierre; Vargas, Andre; Beauchamp, Pat; Spilker, Tom; Strange, Nathan; Elliott, John

    2010-05-01

    The future exploration of Titan is of high priority for the solar system exploration community as recommended by the 2003 National Research Council (NRC) Decadal Survey [1] and ESA's Cosmic Vision Program themes. Cassini-Huygens discoveries continue to emphasize that Titan is a complex world with very many Earth-like features. Titan has a dense, nitrogen atmosphere, an active climate and meteorological cycles where conditions are such that the working fluid, methane, plays the role that water does on Earth. Titan's surface, with lakes and seas, broad river valleys, sand dunes and mountains was formed by processes like those that have shaped the Earth. Supporting this panoply of Earth-like processes is an ice crust that floats atop what might be a liquid water ocean. Furthermore, Titan is rich in very many different organic compounds—more so than any place in the solar system, except Earth. The Titan Saturn System Mission (TSSM) concept that followed the 2007 TandEM ESA CV proposal [2] and the 2007 Titan Explorer NASA Flagship study [3], was examined [4,5] and prioritized by NASA and ESA in February 2009 as a mission to follow the Europa Jupiter System Mission. The TSSM study, like others before it, again concluded that an orbiter, a montgolfiѐre hot-air balloon and a surface package (e.g. lake lander, Geosaucer (instrumented heat shield), …) are very high priority elements for any future mission to Titan. Such missions could be conceived as Flagship/Cosmic Vision L-Class or as individual smaller missions that could possibly fit within NASA's New Frontiers or ESA's Cosmic Vision M-Class budgets. As a result of a multitude of Titan mission studies, several mission concepts have been developed that potentially fit within various cost classes. Also, a clear blueprint has been laid out for early efforts critical toward reducing the risks inherent in such missions. The purpose of this paper is to provide a brief overview of potential Titan (and Enceladus) mission

  17. The Exploration of Titan and the Saturnian System

    Science.gov (United States)

    Coustenis, Athena

    The exploration of the outer solar system and in particular of the giant planets and their environments is an on-going process with the Cassini spacecraft currently around Saturn, the Juno mission to Jupiter preparing to depart and two large future space missions planned to launch in the 2020-2025 time frame for the Jupiter system and its satellites (Europa and Ganymede) on the one hand, and the Saturnian system and Titan on the other hand [1,2]. Titan, Saturn's largest satellite, is the only other object in our Solar system to possess an extensive nitrogen atmosphere, host to an active organic chemistry, based on the interaction of N2 with methane (CH4). Following the Voyager flyby in 1980, Titan has been intensely studied from the ground-based large telescopes (such as the Keck or the VLT) and by artificial satellites (such as the Infrared Space Observatory and the Hubble Space Telescope) for the past three decades. Prior to Cassini-Huygens, Titan's atmospheric composition was thus known to us from the Voyager missions and also through the explorations by the ISO. Our perception of Titan had thus greatly been enhanced accordingly, but many questions remained as to the nature of the haze surrounding the satellite and the composition of the surface. The recent revelations by the Cassini-Huygens mission have managed to surprise us with many discoveries [3-8] and have yet to reveal more of the interesting aspects of the satellite. The Cassini-Huygens mission to the Saturnian system has been an extraordinary success for the planetary community since the Saturn-Orbit-Insertion (SOI) in July 2004 and again the very successful probe descent and landing of Huygens on January 14, 2005. One of its main targets was Titan. Titan was revealed to be a complex world more like the Earth than any other: it has a dense mostly nitrogen atmosphere and active climate and meteorological cycles where the working fluid, methane, behaves under Titan conditions the way that water does on

  18. Thermal, spectroscopic and laser properties of Nd3+ in gadolinium scandium gallium garnet crystal produced by optical floating zone method

    Science.gov (United States)

    Tian, Li; Wang, Shuxian; Wu, Kui; Wang, Baolin; Yu, Haohai; Zhang, Huaijin; Cai, Huaqiang; Huang, Hui

    2013-12-01

    A neodymium-doped gadolinium scandium gallium garnet (Nd:GSGG) single crystal with dimensions of Φ 5 × 20 mm2 has been grown by means of optical floating zone (OFZ). X-ray powder diffraction (XRPD) result shows that the as-grown Nd:GSGG crystal possesses a cubic structure with space group Ia3d and a cell parameter of a = 1.2561 nm. Effective elemental segregation coefficients of the Nd:GSGG as-grown crystal were calculated by using X-ray fluorescence (XRF). The thermal properties of the Nd:GSGG crystal were systematically studied by measuring the specific heat, thermal expansion and thermal diffusion coefficient, and the thermal conductivity of this crystal was calculated. The absorption and luminescence spectra of Nd:GSGG were measured at room temperature (RT). By using the Judd-Ofelt (J-O) theory, the theoretical radiative lifetime was calculated and compared with the experimental result. Continuous wave (CW) laser performance was achieved with the Nd:GSGG at the wavelength of 1062 nm when it was pumped by a laser diode (LD). A maximum output power of 0.792 W at 1062 nm was obtained with a slope efficiency of 11.89% under a pump power of 7.36 W, and an optical-optical conversion efficiency of 11.72%.

  19. A Report of Clouds on Titan

    Science.gov (United States)

    Corlies, Paul; Hayes, Alexander; Adamkovics, Mate; Rodriguez, Sebastien; Kelland, John; Turtle, Elizabeth P.; Mitchell, Jonathan; Lora, Juan M.; Rojo, Patricio; Lunine, Jonathan I.

    2017-10-01

    We present in this work a detailed analysis of many of the clouds in the Cassini Visual and Infrared Mapping Spectrometer (VIMS) dataset in order to understand their global and seasonal properties. Clouds are one of the few direct observables in Titan’s atmosphere (Griffith et al 2009, Rodriguez et al 2009, Adamkovics et al 2010), and so determining their characteristics allows for a better understanding of surface atmosphere interactions, winds, transport of volatile material, and general circulation. We find the clouds on Titan generally reside in at 5-15km altitude, which agrees with previous modelling efforts (Rafkin et al. 2015), as well as a power law distribution for cloud optical depth. We assume an average cloud droplet size of 100um. No seasonal dependence is observed with either cloud altitude or optical depth, suggesting there is no preferred seasonal formation mechanisms. Combining these characteristics with cloud size (Kelland et al 2017) can trace the transport of volatiles in Titan’s atmosphere, which can be compared against general circulation models (GCMs) (Lora et al 2015). We also present some specific analysis of interesting cloud systems including hypothesized surface fogs (Brown et al 2009) and orographic cloud formation (Barth et al 2010, Corlies et al 2017). In this analysis we use a correlation between Cassini VIMS and RADAR observations as well as an updated topographic map of Titan’s southern hemisphere to better understand the role that topography plays in influencing and driving atmospheric phenomena.Finally, with the end of the Cassini mission, ground based observing now acts as the only means with which to observe clouds on Titan. We present an update of an ongoing cloud campaign to search for clouds on Titan and to understand their seasonal evolution.References:Adamkovics et al. 2010, Icarus 208:868Barth et al. 2010, Planet. Space Sci. 58:1740Corlies et al. 2017, 48th LPSC, 2870CGriffith et al. 2009, ApJ 702:L105Kelland et al

  20. The TITAN reversed-field-pinch fusion reactor study

    International Nuclear Information System (INIS)

    1990-01-01

    This paper on titan plasma engineering contains papers on the following topics: reversed-field pinch as a fusion reactor; parametric systems studies; magnetics; burning-plasma simulations; plasma transient operations; current drive; and physics issues for compact RFP reactors

  1. Niobium-doped strontium titanates as SOFC anodes

    DEFF Research Database (Denmark)

    Blennow Tullmar, Peter; Kammer Hansen, Kent; Wallenberg, L. Reine

    2008-01-01

    been synthesized with a recently developed modified glycine-nitrate process. The synthesized powders have been calcined and sintered in air or in 9% H(2) / N(2) between 800 - 1400 degrees C. After calcination the samples were single phase Nb-doped strontium titanate with grain sizes of less than 100 nm...... in diameter on average. The phase purity, defect structure, and microstructure of the materials have been analyzed with SEM, XRD, and TGA. The electrical conductivity of the Nb-doped titanate decreased with increasing temperature and showed a phonon scattering conduction mechanism with sigma > 120 S...... ability of the Nb-doped titanates to be used as a part of a SOFC anode. However, the catalytic activity of the materials was not sufficient and it needs to be improved if titanate based materials are to be realized as constituents in SOFC anodes....

  2. Cation interdiffusion in polycrystalline calcium and strontium titanate

    International Nuclear Information System (INIS)

    Butler, E.P.; Jain, H.; Smyth, D.M.

    1991-01-01

    This paper discusses a method that has been developed to study bulk lattice interdiffusion between calcium and strontium titanate by fabrication of a diffusion couple using cosintering. The measured interdiffusion coefficients, D(C), indicate that strontium impurity diffusion in calcium titanate occurs at a faster rate than calcium impurity diffusion in strontium titanate. These interdiffusion coefficients are composition independent when the concentration of the calcium cation exceeds that of the strontium cation; otherwise D(C) is strongly composition dependent. Investigations into the effect of cation nonstoichiometry give results that are consistent with a defect incorporation reaction in which excess TiO 2 , within the solid solubility limit, produces A-site cation vacancies as compensating defects. The interdiffusion coefficients increase with increasing concentrations of TiO 2 , so it is concluded that interdiffusion of these alkaline-earth cations in their titanates occurs via a vacancy mechanism

  3. METHANE GAS STABILIZES SUPERCOOLED ETHANE DROPLETS IN TITAN'S CLOUDS

    International Nuclear Information System (INIS)

    Wang, Chia C.; Lang, E. Kathrin; Signorell, Ruth

    2010-01-01

    Strong evidence for ethane clouds in various regions of Titan's atmosphere has recently been found. Ethane is usually assumed to exist as ice particles in these clouds, although the possible role of liquid and supercooled liquid ethane droplets has been recognized. Here, we report on infrared spectroscopic measurements of ethane aerosols performed in the laboratory under conditions mimicking Titan's lower atmosphere. The results clearly show that liquid ethane droplets are significantly stabilized by methane gas which is ubiquitous in Titan's nitrogen atmosphere-a phenomenon that does not have a counterpart for water droplets in Earth's atmosphere. Our data imply that supercooled ethane droplets are much more abundant in Titan's clouds than previously anticipated. Possibly, these liquid droplets are even more important for cloud processes and the formation of lakes than ethane ice particles.

  4. The Titanic Origin of Humans: The Melian Nymphs and Zagreus

    Directory of Open Access Journals (Sweden)

    Velvet Yates

    2010-11-01

    Full Text Available Hesiod's creation myth implies that the human race derived from the "ash tree nymphs" (meliai; the Neoplatonists, with their etymological arguments, seem to have this in mind in tracing human origins to the Titans' "limbs" (melea.

  5. Tut and the Titanic and Finding History Beneath the Sea.

    Science.gov (United States)

    Hennessey, Gail Skroback; Ballard, Robert

    1988-01-01

    Two articles discuss the controversy about exploration of the shipwrecked Titanic. Suggested are questions for discussion and activities to stimulate student interest and to explore ethical issues involved in the treatment of historic artifacts. (CB)

  6. Amphibious Quadcopter Swarm for the Exploration of Titan

    Science.gov (United States)

    Rajguru, A.; Faler, A. C.; Franz, B.

    2014-06-01

    This is a proposal for a low mass and cost effective mission architecture consisting of an amphibious quadcopter swarm flight vehicle system for the exploration of Titan's liquid methane lake, Ligeia Mare. The paper focuses on the EDL and operations.

  7. Simulating the 3-D Structure of Titan's Upper Atmosphere

    Science.gov (United States)

    Bell, J. M.; Waite, H.; Westlake, J.; Magee, B.

    2009-05-01

    We present results from the 3-D Titan Global Ionosphere-Thermosphere Model (Bell et al [2009], PSS, in review). We show comparisons between simulated N2, CH4, and H2 density fields and the in-situ data from the Cassini Ion Neutral Mass Spectrometer (INMS). We describe the temperature and wind fields consistent with these density calculations. Variations with local time, longitude, and latitude will be addressed. Potential plasma heating sources can be estimated using the 1-D model of De La Haye et al [2007, 2008] and the impacts on the thermosphere of Titan can be assessed in a global sense in Titan-GITM. Lastly, we will place these findings within the context of recent work in modeling the 2-D structure of Titan's upper atmosphere (Mueller-Wodarg et al [2008]).

  8. Organic titanates: a model for activating rapid room-temperature synthesis of shape-controlled CsPbBr3 nanocrystals and their derivatives.

    Science.gov (United States)

    Fang, Shaofan; Li, Guangshe; Li, Huixia; Lu, Yantong; Li, Liping

    2018-04-12

    The application of lead halide perovskite nanocrystals is challenged by the lack of strategies in rapid room-temperature synthesis with controlled morphologies. Here, we report on an initial study of adopting organic titanates as a model activator that promotes rapid room-temperature synthesis of shape-controlled, highly luminescent CsPbBr3 nanocrystals and their derivatives.

  9. Studying Titan's surface photometry in the 5 microns atmospheric window with the Cassini/VIMS instrument

    Science.gov (United States)

    Cornet, T.; Altobelli, N.; Sotin, C.; Le Mouelic, S.; Rodriguez, S.; Philippe, S.; Brown, R. H.; Barnes, J. W.; Buratti, B. J.; Baines, K. H.; Clark, R. N.; Nicholson, P. D.

    2014-12-01

    Due to the influence of methane gas and a thick aerosols haze in the atmosphere, Titan's surface is only visible in 7 spectral atmospheric windows centered at 0.93, 1.08, 1.27, 1.59, 2.01, 2.7-2.8 and 5 microns with the Cassini Visual and Infrared Mapping Spectrometer (VIMS). The 5 microns atmospheric window constitutes the only one being almost insensitive to the haze scattering and which presents only a reduced atmospheric absorption contribution to the signal recorded by the instrument. Despite these advantages leading to the almost direct view of the surface, the 5 microns window is also the noisiest spectral window of the entire VIMS spectrum (an effect highly dependent on the time exposure used for the observations), and it is not totally free from atmospheric contributions, enough to keep "artefacts" in mosaics of several thousands of cubes due to atmospheric and surface photometric effects amplified by the very heterogeneous viewing conditions between each Titan flyby. At first order, a lambertian surface photometry at 5 microns has been used as an initial parameter in order to estimate atmospheric opacity and surface photometry in all VIMS atmospheric windows and to determine the albedo of the surface, yet unknown, both using radiative transfer codes on single cubes or empirical techniques on global hyperspectral mosaics. Other studies suggested that Titan's surface photometry would not be uniquely lambertian but would also contain anisotropic lunar-like contributions. In the present work, we aim at constraining accurately the surface photometry of Titan and residual atmospheric absorption effects in this 5 microns window using a comprehensive study of relevant sites located at various latitudes. Those include bright and dark (dunes) terrains, 5-microns bright terrains (Hotei Regio and Tui Regio), the Huygens Landing Site and high latitudes polar lakes and seas. The VIMS 2004 to 2014 database, composed of more than 40,000 hyperspectral cubes acquired on

  10. Plasma environment of Titan: a 3-D hybrid simulation study

    Directory of Open Access Journals (Sweden)

    S. Simon

    2006-05-01

    Full Text Available Titan possesses a dense atmosphere, consisting mainly of molecular nitrogen. Titan's orbit is located within the Saturnian magnetosphere most of the time, where the corotating plasma flow is super-Alfvénic, yet subsonic and submagnetosonic. Since Titan does not possess a significant intrinsic magnetic field, the incident plasma interacts directly with the atmosphere and ionosphere. Due to the characteristic length scales of the interaction region being comparable to the ion gyroradii in the vicinity of Titan, magnetohydrodynamic models can only offer a rough description of Titan's interaction with the corotating magnetospheric plasma flow. For this reason, Titan's plasma environment has been studied by using a 3-D hybrid simulation code, treating the electrons as a massless, charge-neutralizing fluid, whereas a completely kinetic approach is used to cover ion dynamics. The calculations are performed on a curvilinear simulation grid which is adapted to the spherical geometry of the obstacle. In the model, Titan's dayside ionosphere is mainly generated by solar UV radiation; hence, the local ion production rate depends on the solar zenith angle. Because the Titan interaction features the possibility of having the densest ionosphere located on a face not aligned with the ram flow of the magnetospheric plasma, a variety of different scenarios can be studied. The simulations show the formation of a strong magnetic draping pattern and an extended pick-up region, being highly asymmetric with respect to the direction of the convective electric field. In general, the mechanism giving rise to these structures exhibits similarities to the interaction of the ionospheres of Mars and Venus with the supersonic solar wind. The simulation results are in agreement with data from recent Cassini flybys.

  11. Titan Lifting Entry & Atmospheric Flight (T-LEAF) Science Mission

    Science.gov (United States)

    Lee, G.; Sen, B.; Ross, F.; Sokol, D.

    2016-12-01

    Northrop Grumman has been developing the Titan Lifting Entry & Atmospheric Flight (T-LEAF) sky rover to roam the lower atmosphere and observe at close quarters the lakes and plains of Saturn's ocean moon, Titan. T-LEAF also supports surface exploration and science by providing precision delivery of in-situ instruments to the surface of Titan. T-LEAF is a highly maneuverable sky rover and its aerodynamic shape (i.e., a flying wing) does not restrict it to following prevailing wind patterns on Titan, but allows mission operators to chart its course. This freedom of mobility allows T-LEAF to follow the shorelines of Titan's methane lakes, for example, or to target very specific surface locations. We will present a straw man concept of T-LEAF, including size, mass, power, on-board science payloads and measurement, and surface science dropsonde deployment CONOPS. We will discuss the various science instruments and their vehicle level impacts, such as meteorological and electric field sensors, acoustic sensors for measuring shallow depths, multi-spectral imagers, high definition cameras and surface science dropsondes. The stability of T-LEAF and its long residence time on Titan will provide for time to perform a large aerial survey of select prime surface targets deployment of dropsondes at selected locations surface measurements that are coordinated with on-board remote measurements communication relay capabilities to orbiter (or Earth). In this context, we will specifically focus upon key factors impacting the design and performance of T-LEAF science: science payload accommodation, constraints and opportunities characteristics of flight, payload deployment and measurement CONOPS in the Titan atmosphere. This presentation will show how these factors provide constraints as well as enable opportunities for novel long duration scientific studies of Titan's surface.

  12. The TITAN Reversed-Field Pinch fusion reactor study

    International Nuclear Information System (INIS)

    1988-03-01

    The TITAN Reversed-Field Pinch (RFP) fusion reactor study is a multi-institutional research effort to determine the technical feasibility and key developmental issues of an RFP fusion reactor, especially at high power density, and to determine the potential economics, operations, safety, and environmental features of high-mass-power-density fusion systems. The TITAN conceptual designs are DT burning, 1000 MWe power reactors based on the RFP confinement concept. The designs are compact, have a high neutron wall loading of 18 MW/m 2 and a mass power density of 700 kWe/tonne. The inherent characteristics of the RFP confinement concept make fusion reactors with such a high mass power density possible. Two different detailed designs have emerged: the TITAN-I lithium-vanadium design, incorporating the integrated-blanket-coil concept; and the TITAN-II aqueous loop-in-pool design with ferritic steel structure. This report contains a collection of 16 papers on the results of the TITAN study which were presented at the International Symposium on Fusion Nuclear Technology. This collection describes the TITAN research effort, and specifically the TITAN-I and TITAN-II designs, summarizing the major results, the key technical issues, and the central conclusions and recommendations. Overall, the basic conclusions are that high-mass power-density fusion reactors appear to be technically feasible even with neutron wall loadings up to 20 MW/m 2 ; that single-piece maintenance of the FPC is possible and advantageous; that the economics of the reactor is enhanced by its compactness; and the safety and environmental features need not to be sacrificed in high-power-density designs. The fact that two design approaches have emerged, and others may also be possible, in some sense indicates the robustness of the general findings

  13. Aerosol chemistry in Titan's ionosphere: simultaneous growth and etching processes

    Science.gov (United States)

    Carrasco, Nathalie; Cernogora, Guy; Jomard, François; Etcheberry, Arnaud; Vigneron, Jackie

    2016-10-01

    Since the Cassini-CAPS measurements, organic aerosols are known to be present and formed at high altitudes in the diluted and partially ionized medium that is Titan's ionosphere [1]. This unexpected chemistry can be further investigated in the laboratory with plasma experiments simulating the complex ion-neutral chemistry starting from N2-CH4 [2]. Two sorts of solid organic samples can be produced in laboratory experiments simulating Titan's atmospheric reactivity: grains in the volume and thin films on the reactor walls. We expect that grains are more representative of Titan's atmospheric aerosols, but films are used to provide optical indices for radiative models of Titan's atmosphere.The aim of the present study is to address if these two sorts of analogues are chemically equivalent or not, when produced in the same N2-CH4 plasma discharge. The chemical compositions of both these materials are measured by using elemental analysis, XPS analysis and Secondary Ion Mass Spectrometry. We find that films are homogeneous but significantly less rich in nitrogen and hydrogen than grains produced in the same experimental conditions. This surprising difference in their chemical compositions is explained by the efficient etching occurring on the films, which stay in the discharge during the whole plasma duration, whereas the grains are ejected after a few minutes [3]. The impact for our understanding of Titan's aerosols chemical composition is important. Our study shows that chemical growth and etching process are simultaneously at stake in Titan's ionosphere. The more the aerosols stay in the ionosphere, the more graphitized they get through etching process. In order to infer Titan's aerosols composition, our work highlights a need for constraints on the residence time of aerosols in Titan's ionosphere. [1] Waite et al. (2009) Science , 316, p. 870[2] Szopa et al. (2006) PSS, 54, p. 394[3] Carrasco et al. (2016) PSS, 128, p. 52

  14. Plasma environment of Titan: a 3-D hybrid simulation study

    Directory of Open Access Journals (Sweden)

    S. Simon

    2006-05-01

    Full Text Available Titan possesses a dense atmosphere, consisting mainly of molecular nitrogen. Titan's orbit is located within the Saturnian magnetosphere most of the time, where the corotating plasma flow is super-Alfvénic, yet subsonic and submagnetosonic. Since Titan does not possess a significant intrinsic magnetic field, the incident plasma interacts directly with the atmosphere and ionosphere. Due to the characteristic length scales of the interaction region being comparable to the ion gyroradii in the vicinity of Titan, magnetohydrodynamic models can only offer a rough description of Titan's interaction with the corotating magnetospheric plasma flow. For this reason, Titan's plasma environment has been studied by using a 3-D hybrid simulation code, treating the electrons as a massless, charge-neutralizing fluid, whereas a completely kinetic approach is used to cover ion dynamics. The calculations are performed on a curvilinear simulation grid which is adapted to the spherical geometry of the obstacle. In the model, Titan's dayside ionosphere is mainly generated by solar UV radiation; hence, the local ion production rate depends on the solar zenith angle. Because the Titan interaction features the possibility of having the densest ionosphere located on a face not aligned with the ram flow of the magnetospheric plasma, a variety of different scenarios can be studied. The simulations show the formation of a strong magnetic draping pattern and an extended pick-up region, being highly asymmetric with respect to the direction of the convective electric field. In general, the mechanism giving rise to these structures exhibits similarities to the interaction of the ionospheres of Mars and Venus with the supersonic solar wind. The simulation results are in agreement with data from recent Cassini flybys.

  15. Does Titan have an Active Surface?

    Science.gov (United States)

    Nelson, R.

    2009-12-01

    Robert M. Nelson-1, L. W. Kamp-1, R. M. C. Lopes-1, D. L. Matson-1, R. L. Kirk-2, B. W. Hapke-3, M. D. Boryta-4, F. E. Leader-1, W. D. Smythe-1, K. L. Mitchell-1, K. H. Baines-1, R. Jaumann-5, C. Sotin-1, R. N. Clark-6, D. P. Cruikshank-7 , P. Drossart-8, J. I. Lunine-9, M. Combes-10, G. Bellucci-11, J.-P. Bibring-12, F. Capaccioni-11, P. Cerroni-11, A. Coradini-11, V. Formisano-11, G. Filacchione-11, Y. Langevin-12, T. B. McCord-13, V. Mennella-14, B. Sicardy-8, P. G. J. Irwin-15 ,J.C. Pearl-16 1-JPL, 4800 Oak Grove Drive, Pasadena CA 91109;2-USGS, Flagstaff; 3-U Pittsburgh; 4-Mt. San Antonio College; 5-DLR, Berlin;6-USGS Denver; 7-NASA AMES; 8-U Paris-Meudon; 9-U Arizona; 10- Obs de Paris; 11-INAF-ISAF Rome; 12-U Paris -Sud. Orsay; 13-Bear Flt Cntr. Winthrop WA;14-Obs Capodimonte Naples; 15-Clarendon Laboratory, Oxford, UK, 16-Goddard Space Flight Center, Greenbelt MD Surface changes on Saturn’s moon Titan have been reported during the Cassini spacecraft’s four-year orbital tour of the Saturnian system based on Cassini Visual and Infrared Mapping Spectrometer (VIMS) data [1]. Titan’s surface is hard to observe because it’s atmosphere is opaque at visual wavelengths due to absorption by methane in Titan’s atmosphere. VIMS is able to image the surface through “windows” at infrared wavelengths where the methane is relatively transparent [1,2]. VIMS infrared images find surface reflectance variability at Hotei Reggio (26S,78W) and suggest that the variability might be due to deposition, followed by coverage or dissipation, of ammonia frost. Subsequently, Cassini RADAR images found that Hotei Reggio, has lobate “flow” forms, consistent with the morphology of volcanic terrain [3]. Here we report the discovery of lobate “flow” patterns at Hotei Reggio based on VIMS infrared images taken during Cassini close flybys during 2008-2009. This new evidence is consistent with the suggestion that the brightness variability at Hotei Reggio is associated with

  16. What makes the difference in perovskite titanates?

    Science.gov (United States)

    Bussmann-Holder, Annette; Roleder, Krystian; Ko, Jae-Hyeon

    2018-06-01

    We have investigated in detail the lattice dynamics of five different perovskite titanates ATiO3 (A = Ca, Sr, Ba, Pb, Eu) where the A sites are occupied by +2 ions. In spite of the largely ionic character of these ions, the properties of these compounds differ substantially. They range from order/disorder like, to displacive ferroelectric, quantum paraelectric, and antiferromagnetic. All compounds crystallize in the cubic structure at high temperature and undergo structural phase transitions to tetragonal symmetry, partly followed by further transitions to lower symmetries. Since the TiO6 moiety is the essential electronic and structural unit, the question arises, what makes the significant difference between them. It is shown that the lattice dynamics of these compounds are very different, and that mode-mode coupling effects give rise to many distinct properties. In addition, the oxygen ion nonlinear polarizability plays a key role since it dominates the anharmonicity of these perovskites and determines the structural instability.

  17. Synthesis and characterization of bismuth alkaline titanate powders

    Energy Technology Data Exchange (ETDEWEB)

    Torres-Huerta, A.M., E-mail: atorresh@ipn.mx [CICATA-Altamira, Instituto Politecnico Nacional, Km. 14.5 Carretera Tampico Puerto Industrial Altamira, Altamira, Tamps. 89600 (Mexico); Dominguez-Crespo, M.A. [CICATA-Altamira, Instituto Politecnico Nacional, Km. 14.5 Carretera Tampico Puerto Industrial Altamira, Altamira, Tamps. 89600 (Mexico); Hernandez-Perez, M.A. [ESIQIE, Metalurgia, Instituto Politecnico Nacional, Mexico, D. F (Mexico); Garcia-Zaleta, D.S. [CICATA-Altamira, Instituto Politecnico Nacional, Km. 14.5 Carretera Tampico Puerto Industrial Altamira, Altamira, Tamps. 89600 (Mexico); Brachetti-Sibaja, S.B. [CICATA-Altamira, Instituto Politecnico Nacional, Km. 14.5 Carretera Tampico Puerto Industrial Altamira, Altamira, Tamps. 89600 (Mexico); Instituto Tecnologico de Ciudad Madero, Av. 1o. de Mayo esq. Sor Juana Ines de la Cruz s/n Col. Los Mangos C.P.89440 Cd. Madero Tamaulipas (Mexico)

    2011-06-15

    In this work, samples of bismuth alkaline titanate, (K{sub 0.5}Na{sub 0.5}){sub (2-x/2)}Bi{sub (x/6)}TiO{sub 3}, (x = 0.05-0.75) have been prepared by conventional ceramic technique and molten salts. Metal oxides or carbonates powders were used as starting raw materials. The crystalline phase of the synthesized powders was identified by the X-ray diffraction (XRD) and particle morphology was characterized by scanning electron microscopy (SEM). Solid state reaction method was unsuccessful to obtain pellets. From XRD results, a rhombohedral structure was detected and the parameter lattice were estimated to be a = 5.5478 A and {alpha} = 59.48{sup o}. These parameters were used to refine the structure by Rietveld analysis. SEM results showed several morphologies. Apparently, bismuth is promoting the grain growth whose sizes vary from 30 nm to 180 nm It is expected that these materials can be utilized in practical applications as substitutes for lead zirconatetitanate (PZT)-based ceramics.

  18. LEADING WITH LEADING INDICATORS

    International Nuclear Information System (INIS)

    PREVETTE, S.S.

    2005-01-01

    This paper documents Fluor Hanford's use of Leading Indicators, management leadership, and statistical methodology in order to improve safe performance of work. By applying these methods, Fluor Hanford achieved a significant reduction in injury rates in 2003 and 2004, and the improvement continues today. The integration of data, leadership, and teamwork pays off with improved safety performance and credibility with the customer. The use of Statistical Process Control, Pareto Charts, and Systems Thinking and their effect on management decisions and employee involvement are discussed. Included are practical examples of choosing leading indicators. A statistically based color coded dashboard presentation system methodology is provided. These tools, management theories and methods, coupled with involved leadership and employee efforts, directly led to significant improvements in worker safety and health, and environmental protection and restoration at one of the nation's largest nuclear cleanup sites

  19. Titan atmospheric composition by hypervelocity shock layer analysis

    International Nuclear Information System (INIS)

    Nelson, H.F.; Park, C.; Whiting, E.E.

    1989-01-01

    The Cassini Mission, a NASA/ESA cooperative project which includes a deployment of probe into the atmosphere of Titan, is described, with particular attention given to the shock radiometer experiment planned for the Titan probe for the analysis of Titan's atmosphere. Results from a shock layer analysis are presented, demonstrating that the mole fractions of the major species (N2, CH4, and, possibly Ar) in the Titan atmosphere can be successfully determined by the Titan-probe radiometer, by measuring the intensity of the CN(violet) radiation emitted in the shock layer during the high velocity portion of the probe entry between 200 and 400 km altitude. It is shown that the sensitivity of the CN(violet) radiation makes it possible to determine the mole fractions of N2, CH4, and Ar to about 0.015, 0.003, and 0.01, respectively, i.e., much better than the present uncertainties in the composition of Titan atmosphere. 29 refs

  20. Experimental basis for a Titan probe organic analysis

    International Nuclear Information System (INIS)

    Mckay, C.P.; Scattergood, T.W.; Borucki, W.J.; Kasting, J.F.; Miller, S.L.; California Univ., San Diego, La Jolla)

    1986-01-01

    The recent Voyager flyby of Titan produced evidence for at least nine organic compounds in that atmosphere that are heavier than methane. Several models of Titan's atmosphere, as well as laboratory simulations, suggest the presence of organics considerably more complex that those observed. To ensure that the in situ measurements are definitive with respect to Titan's atmosphere, experiment concepts, and the related instrumentation, must be carefully developed specifically for such a mission. To this end, the possible composition of the environment to be analyzed must be bracketed and model samples must be provided for instrumentation development studies. Laboratory studies to define the optimum flight experiment and sampling strategy for a Titan entry probe are currently being conducted. Titan mixtures are being subjected to a variety of energy sources including high voltage electron from a DC discharge, high current electric shock, and laser detonation. Gaseous and solid products are produced which are then analyzed. Samples from these experiements are also provided to candidate flight experiments as models for instrument development studies. Preliminary results show that existing theoretical models for chemistry in Titan's atmosphere cannot adequetely explain the presence and abundance of all trace gases observed in these experiments