  1. Relationship between ultrasonic Rayleigh waves and surface residual stress

    International Nuclear Information System (INIS)

    Adler, L.; Cook, K.V.; Dewey, B.R.; King, R.T.

    1977-01-01

    Local variations of Rayleigh (surface) circumferential ultrasonic wave velocity near a pipe-girth weld in large-diameter thin-wall type 316H stainless steel pipe were measured. The weldment was similar to those anticipated for the Liquid Metal Fast Breeder Reactor (LMFBR) piping systems. The residual stress distribution was estimated independently from shell theory for an elastic, infinite, thin shell with circumferential line loading. An upper bound on the magnitude of the residual stresses was estimated assuming the deformation of the shell was entirely elastic. The pattern of surface wave velocity variations matches the theoretical residual stress pattern closely. It is suggested that the monitoring of surface wave velocity variations might be used for characterizing residual stress patterns near critical welds in piping, aiding in design calculations, and for in-service monitoring of the state of stress of weldments

  2. Residual stresses estimation in tubes after rapid heating of surface

    International Nuclear Information System (INIS)

    Serikov, S.V.

    1992-01-01

    Results are presented on estimation of residual stresses in tubes of steel types ShKh15, EhP836 and 12KIMF after heating by burning pyrotechnic substance inside tubes. External tube surface was heated up to 400-450 deg C under such treatment. Axial stresses distribution over tube wall thickness was determined for initial state, after routine heat treatment and after heating with the use of fireworks. Inner surface heating was shown to essentially decrease axial stresses in tubes

  3. On machine surface to the unit event causing residual stress

    International Nuclear Information System (INIS)

    Arunachalama, R.M.; Mannanb, M.A.; Spowageca, A.

    2005-01-01

    Integrity and reduce overall costs. Within the framework of surface integrity investigations, special emphasis is given to the measurement of residual stresses because they contribute directly to premature failure of components. Since the highest residual stresses are to be found in surface layers, these deserve special attention when dealing with dynamically, heavily loaded machine parts such as gas turbine components used in aero engines. Of the many techniques available for the measurement of residual stresses, the most highly developed and widely used non-destructive method is based on X-ray diffraction (XRD). However, it is not possible to use this technique for inspection of all the components, since it is time consuming, complicated as well as expensive. In this paper, a method is being proposed that augments the XRD method but at the same time capable of inspecting all the components. A non-destructive, visual inspection technique has been developed that can correlate the characteristic features on the surface to the unit event causing the residual stress and the type of residual stress generated on the machined surface. Pictures of the machined surfaces have been taken using a digital video microscope at a magnification of 500 and the surface feature correlated to the unit event causing the residual stress. Sharp and well defined long grooves indicate that the plastic deformation is dominated by a mechanical unit event while appearance of streaks and small areas of smeared material indicate that the plastic deformation is dominated by a thermal unit event. These trends have been confirmed by measuring the residual stresses using XRD. The proposed technique is an attempt at establishing a simple methodology that would be useful to industries manufacturing aerospace and other components that require good surface integrity. (Author)

  4. Prediction of residual stress distributions due to surface machining and welding and crack growth simulation under residual stress distribution

    International Nuclear Information System (INIS)

    Ihara, Ryohei; Katsuyama, JInya; Onizawa, Kunio; Hashimoto, Tadafumi; Mikami, Yoshiki; Mochizuki, Masahito

    2011-01-01

    Research highlights: → Residual stress distributions due to welding and machining are evaluated by XRD and FEM. → Residual stress due to machining shows higher tensile stress than welding near the surface. → Crack growth analysis is performed using calculated residual stress. → Crack growth result is affected machining rather than welding. → Machining is an important factor for crack growth. - Abstract: In nuclear power plants, stress corrosion cracking (SCC) has been observed near the weld zone of the core shroud and primary loop recirculation (PLR) pipes made of low-carbon austenitic stainless steel Type 316L. The joining process of pipes usually includes surface machining and welding. Both processes induce residual stresses, and residual stresses are thus important factors in the occurrence and propagation of SCC. In this study, the finite element method (FEM) was used to estimate residual stress distributions generated by butt welding and surface machining. The thermoelastic-plastic analysis was performed for the welding simulation, and the thermo-mechanical coupled analysis based on the Johnson-Cook material model was performed for the surface machining simulation. In addition, a crack growth analysis based on the stress intensity factor (SIF) calculation was performed using the calculated residual stress distributions that are generated by welding and surface machining. The surface machining analysis showed that tensile residual stress due to surface machining only exists approximately 0.2 mm from the machined surface, and the surface residual stress increases with cutting speed. The crack growth analysis showed that the crack depth is affected by both surface machining and welding, and the crack length is more affected by surface machining than by welding.

  5. Prediction and Optimization of Residual Stresses on Machined Surface and Sub-Surface in MQL Turning

    Science.gov (United States)

    Ji, Xia; Zou, Pan; Li, Beizhi; Rajora, Manik; Shao, Yamin; Liang, Steven Y.

    Residual stress in the machined surface and subsurface is affected by materials, machining conditions, and tool geometry and can affect the component life and service quality significantly. Empirical or numerical experiments are commonly used for determining residual stresses but these are very expensive. There has been an increase in the utilization of minimum quantity lubrication (MQL) in recent years in order to reduce the cost and tool/part handling efforts, while its effect on machined part residual stress, although important, has not been explored. This paper presents a hybrid neural network that is trained using Simulated Annealing (SA) and Levenberg-Marquardt Algorithm (LM) in order to predict the values of residual stresses in cutting and radial direction on the surface and within the work piece after the MQL face turning process. Once the ANN has successfully been trained, an optimization procedure, using Genetic Algorithm (GA), is applied in order to find the best cutting conditions in order to minimize the surface tensile residual stresses and maximize the compressive residual stresses within the work piece. The optimization results show that the usage of MQL decreases the surface tensile residual stresses and increases the compressive residual stresses within the work piece.

  6. Surface preparation for residual stress measurement of an accelerated corrosion tested welded marine steel

    International Nuclear Information System (INIS)

    Ahmad, Bilal; Fitzpatrick, Michael E.

    2015-01-01

    Residual stress measurement is often required for the assessment of structural integrity of components. Measurement of residual stress in corrosion tested specimens is challenging owing to the difficulty of accessing the surface because of the rust layer. This study explored the potential methods for the surface preparation of an ultrasonically-peened and accelerated corrosion tested DH36 marine steel fillet welded specimen to ease the way for subsequent residual stress measurement using neutron diffraction and the contour method. We find that hydroblasting introduces compressive residual stress at the surface that will alter the surface stress to be measured

  7. Effects on Machining on Surface Residual Stress of SA 508 and Austenitic Stainless Steel

    International Nuclear Information System (INIS)

    Lee, Kyoung Soo; Lee, Seong Ho; Park, Chi Yong; Yang, Jun Seok; Lee, Jeong Geun; Park, Jai Hak

    2011-01-01

    Primary water stress corrosion cracking has occurred in dissimilar weld areas in nuclear power plants. Residual stress is a driving force in the crack. Residual stress may be generated by weld or surface machining. Residual stress due to surface machining depends on the machining method, e.g., milling, grinding, or EDM. The stress is usually distributed on or near the surface of the material. We present the measured residual stress for machining on SA 508 and austenitic stainless steels such as TP304 and F316. The residual stress can be tensile or compressive depending on the machining method. The depth and the magnitude of the residual stress depend on the material and the machining method

  8. Application of laser interferometry for assessment of surface residual stress by determination of stress-free state

    International Nuclear Information System (INIS)

    Kim, Dong Won; Kwon, Dong Il; Lee, Nak Kyu; Choi, Tae Hoon; Na, Kyoung Hoan

    2003-01-01

    The total relaxed stress in annealing and the thermal strain/stress were obtained from the identification of the residual stress-free state using Electronic Speckle Pattern Interferometry (ESPI). The residual stress fields in case of both single and film/substrate systems were modeled using the thermo-elastic theory and the relationship between relaxed stresses and displacements. We mapped the surface residual stress fields on the indented bulk Cu and the 0.5 μm Au film by ESPI. In indented Cu, the normal and shear residual stress are distributed over -1.7 GPa to 700 MPa and -800 GPa to 600 MPa respectively around the indented point and in deposited Au film on Si wafer, the tensile residual stress is uniformly distributed on the Au film from 500 MPa to 800 MPa. Also we measured the residual stress by the X-Ray Diffractometer (XRD) for the verification of above residual stress results by ESPI

  9. Characterization of Residual Stress in Shot Peened Al 7075 Alloy Using Surface Acoustic Wave

    International Nuclear Information System (INIS)

    Kim, Chung Seok; Kwun, Sook In; Kim, Yong Kwon; Park, Ik Keun

    2006-01-01

    The residual stress in shot-peened Al 7075 alloy was evaluated using surface acoustic wave (SAW). Shot peening was conducted to produce a variation in the residual stress with the depth below the surface under a shot velocity of 30 m/s. The SAW velocity was measured from the V(z) curve using a scanning acoustic microscopy (SAM). The Vickers hardness profile from the surface showed a significant work hardening near the surface layer with a thickness of about 0.25 mm. As the residual stress became more compressive, the SAW velocity increased, whereas as the residual stress became more tensile, the SAW velocity decreased. The variation in the SAW velocity through the shot peened surface layer was in good agreement with the distribution of the residual stress measured by X-ray diffraction technique

  10. Neutron Diffraction Evaluation of Near Surface Residual Stresses at Welds in 1300 MPa Yield Strength Steel

    Directory of Open Access Journals (Sweden)

    Ebrahim Harati

    2017-05-01

    Full Text Available Evaluation of residual stress in the weld toe region is of critical importance. In this paper, the residual stress distribution both near the surface and in depth around the weld toe was investigated using neutron diffraction, complemented with X-ray diffraction. Measurements were done on a 1300 MPa yield strength steel welded using a Low Transformation Temperature (LTT consumable. Near surface residual stresses, as close as 39 µm below the surface, were measured using neutron diffraction and evaluated by applying a near surface data correction technique. Very steep surface stress gradients within 0.5 mm of the surface were found both at the weld toe and 2 mm into the heat affected zone (HAZ. Neutron results showed that the LTT consumable was capable of inducing near surface compressive residual stresses in all directions at the weld toe. It is concluded that there are very steep stress gradients both transverse to the weld toe line and in the depth direction, at the weld toe in LTT welds. Residual stress in the base material a few millimeters from the weld toe can be very different from the stress at the weld toe. Care must, therefore, be exercised when relating the residual stress to fatigue strength in LTT welds.

  11. Neutron Diffraction Evaluation of Near Surface Residual Stresses at Welds in 1300 MPa Yield Strength Steel.

    Science.gov (United States)

    Harati, Ebrahim; Karlsson, Leif; Svensson, Lars-Erik; Pirling, Thilo; Dalaei, Kamellia

    2017-05-29

    Evaluation of residual stress in the weld toe region is of critical importance. In this paper, the residual stress distribution both near the surface and in depth around the weld toe was investigated using neutron diffraction, complemented with X-ray diffraction. Measurements were done on a 1300 MPa yield strength steel welded using a Low Transformation Temperature (LTT) consumable. Near surface residual stresses, as close as 39 µm below the surface, were measured using neutron diffraction and evaluated by applying a near surface data correction technique. Very steep surface stress gradients within 0.5 mm of the surface were found both at the weld toe and 2 mm into the heat affected zone (HAZ). Neutron results showed that the LTT consumable was capable of inducing near surface compressive residual stresses in all directions at the weld toe. It is concluded that there are very steep stress gradients both transverse to the weld toe line and in the depth direction, at the weld toe in LTT welds. Residual stress in the base material a few millimeters from the weld toe can be very different from the stress at the weld toe. Care must, therefore, be exercised when relating the residual stress to fatigue strength in LTT welds.

  12. X-ray evaluation of residual stress distributions within surface machined layer generated by surface machining and sequential welding

    International Nuclear Information System (INIS)

    Taniguchi, Yuu; Okano, Shigetaka; Mochizuki, Masahito

    2017-01-01

    The excessive tensile residual stress generated by welding after surface machining may be an important factor to cause stress corrosion cracking (SCC) in nuclear power plants. Therefore we need to understand and control the residual stress distribution appropriately. In this study, residual stress distributions within surface machined layer generated by surface machining and sequential welding were evaluated by X-ray diffraction method. Depth directional distributions were also investigated by electrolytic polishing. In addition, to consider the effect of work hardened layer on the residual stress distributions, we also measured full width at half maximum (FWHM) obtained from X-ray diffraction. Testing material was a low-carbon austenitic stainless steel type SUS316L. Test specimens were prepared by surface machining with different cutting conditions. Then, bead-on-plate welding under the same welding condition was carried out on the test specimens with different surface machined layer. As a result, the tensile residual stress generated by surface machining increased with increasing cutting speed and showed nearly uniform distributions on the surface. Furthermore, the tensile residual stress drastically decreased with increasing measurement depth within surface machined layer. Then, the residual stress approached 0 MPa after the compressive value showed. FWHM also decreased drastically with increasing measurement depth and almost constant value from a certain depth, which was almost equal regardless of the machining condition, within surface machined layer in all specimens. After welding, the transverse distribution of the longitudinal residual stress varied in the area apart from the weld center according to machining conditions and had a maximum value in heat affected zone. The magnitude of the maximum residual stress was almost equal regardless of the machining condition and decreased with increasing measurement depth within surface machined layer. Finally, the

  13. Experimental measurements of surface damage and residual stresses in micro-engineered plasma facing materials

    Science.gov (United States)

    Rivera, David; Wirz, Richard E.; Ghoniem, Nasr M.

    2017-04-01

    The thermomechanical damage and residual stresses in plasma-facing materials operating at high heat flux are experimentally investigated. Materials with micro-surfaces are found to be more resilient, when exposed to cyclic high heat flux generated by an arc-jet plasma. An experimental facility, dedicated to High Energy Flux Testing (HEFTY), is developed for testing cyclic heat flux in excess of 10 MW/m2. We show that plastic deformation and subsequent fracture of the surface can be controlled by sample cooling. We demonstrate that W surfaces with micro-pillar type surface architecture have significantly reduced residual thermal stresses after plasma exposure, as compared to those with flat surfaces. X-ray diffraction (XRD) spectra of the W-(110) peak reveal that broadening of the Full Width at Half Maximum (FWHM) for micro-engineered samples is substantially smaller than corresponding flat surfaces. Spectral shifts of XRD signals indicate that residual stresses due to plasma exposure of micro-engineered surfaces build up in the first few cycles of exposure. Subsequent cyclic plasma heat loading is shown to anneal out most of the built-up residual stresses in micro-engineered surfaces. These findings are consistent with relaxation of residual thermal stresses in surfaces with micro-engineered features. The initial residual stress state of highly polished flat W samples is compressive (≈ -1.3 GPa). After exposure to 50 plasma cycles, the surface stress relaxes to -1.0 GPa. Micro-engineered samples exposed to the same thermal cycling show that the initial residual stress state is compressive at (- 250 MPa), and remains largely unchanged after plasma exposure.

  14. A study on residual stresses in laser surface hardening of a medium carbon steel

    International Nuclear Information System (INIS)

    Yang, Y.S.; Na, S.J.

    1989-01-01

    The transient thermal stress and the residual stress in laser surface-hardening treatment of a medium carbon steel were analysed by employing a new two-dimensional finite element model. In this formulation, a sliced solution domain, having one element in the hardening direction, was introduced to satisfy the self-equilibrium of the resultant force in the hardening direction. By using the proposed model, the thermal and residual stresses in the laser surface heat treatment were successively calculated. The thermal stress was induced mainly by the temperature gradient and the martensitic phase transformation; the phase transformation was found to have a greater influence on the residual stress than the temperature gradient. The simulation results revealed that a compressive residual stress region occurs near the hardened surface of the workpiece and a tensile residual stress region occurs in the interior of the workpiece, whereas the maximum tensile residual stress occurs along the centre of the laser scanning path in the interior region (y=0). In comparison with the gaussian distribution of the beam power, the square beam mode results in a wider, but shallower, hardened zone. The calculation results also showed that the high-power beam with the high scanning speed is more suitable for laser surface hardening than the low-power beam with the low scanning speed if the heat input per unit length of the workpiece is maintained constant. (orig.)

  15. Finite Element Simulation of Shot Peening: Prediction of Residual Stresses and Surface Roughness

    Science.gov (United States)

    Gariépy, Alexandre; Perron, Claude; Bocher, Philippe; Lévesque, Martin

    Shot peening is a surface treatment that consists of bombarding a ductile surface with numerous small and hard particles. Each impact creates localized plastic strains that permanently stretch the surface. Since the underlying material constrains this stretching, compressive residual stresses are generated near the surface. This process is commonly used in the automotive and aerospace industries to improve fatigue life. Finite element analyses can be used to predict residual stress profiles and surface roughness created by shot peening. This study investigates further the parameters and capabilities of a random impact model by evaluating the representative volume element and the calculated stress distribution. Using an isotropic-kinematic hardening constitutive law to describe the behaviour of AA2024-T351 aluminium alloy, promising results were achieved in terms of residual stresses.

  16. Effect of processing conditions on residual stress distributions by bead-on-plate welding after surface machining

    International Nuclear Information System (INIS)

    Ihara, Ryohei; Mochizuki, Masahito

    2014-01-01

    Residual stress is important factor for stress corrosion cracking (SCC) that has been observed near the welded zone in nuclear power plants. Especially, surface residual stress is significant for SCC initiation. In the joining processes of pipes, butt welding is conducted after surface machining. Residual stress is generated by both processes, and residual stress distribution due to surface machining is varied by the subsequent butt welding. In previous paper, authors reported that residual stress distribution generated by bead on plate welding after surface machining has a local maximum residual stress near the weld metal. The local maximum residual stress shows approximately 900 MPa that exceeds the stress threshold for SCC initiation. Therefore, for the safety improvement of nuclear power plants, a study on the local maximum residual stress is important. In this study, the effect of surface machining and welding conditions on residual stress distribution generated by welding after surface machining was investigated. Surface machining using lathe machine and bead on plate welding with tungsten inert gas (TIG) arc under various conditions were conducted for plate specimens made of SUS316L. Then, residual stress distributions were measured by X-ray diffraction method (XRD). As a result, residual stress distributions have the local maximum residual stress near the weld metal in all specimens. The values of the local maximum residual stresses are almost the same. The location of the local maximum residual stress is varied by welding condition. It could be consider that the local maximum residual stress is generated by same generation mechanism as welding residual stress in surface machined layer that has high yield stress. (author)

  17. Surface Finish and Residual Stresses Induced by Orthogonal Dry Machining of AA7075-T651.

    Science.gov (United States)

    Jomaa, Walid; Songmene, Victor; Bocher, Philippe

    2014-02-28

    The surface finish was extensively studied in usual machining processes (turning, milling, and drilling). For these processes, the surface finish is strongly influenced by the cutting feed and the tool nose radius. However, a basic understanding of tool/surface finish interaction and residual stress generation has been lacking. This paper aims to investigate the surface finish and residual stresses under the orthogonal cutting since it can provide this information by avoiding the effect of the tool nose radius. The orthogonal machining of AA7075-T651 alloy through a series of cutting experiments was performed under dry conditions. Surface finish was studied using height and amplitude distribution roughness parameters. SEM and EDS were used to analyze surface damage and built-up edge (BUE) formation. An analysis of the surface topography showed that the surface roughness was sensitive to changes in cutting parameters. It was found that the formation of BUE and the interaction between the tool edge and the iron-rich intermetallic particles play a determinant role in controlling the surface finish during dry orthogonal machining of the AA7075-T651 alloy. Hoop stress was predominantly compressive on the surface and tended to be tensile with increased cutting speed. The reverse occurred for the surface axial stress. The smaller the cutting feed, the greater is the effect of cutting speed on both axial and hoop stresses. By controlling the cutting speed and feed, it is possible to generate a benchmark residual stress state and good surface finish using dry machining.

  18. Residual stresses in the surface layer of laser-treated steels

    NARCIS (Netherlands)

    Brussel, B.A. van; Hosson, J.Th.M. De

    1993-01-01

    Although laser treatment of certain metals may enhance the wear performance in general it may result equally well in large residual stresses which affect the wear performance detrimentally. Tensile stresses generated in the surface layer may lead to severe cracking of the material. This paper

  19. On the residual stress modeling of shot-peened AISI 4340 steel: finite element and response surface methods

    Science.gov (United States)

    Asgari, Ali; Dehestani, Pouya; Poruraminaie, Iman

    2018-02-01

    Shot peening is a well-known process in applying the residual stress on the surface of industrial parts. The induced residual stress improves fatigue life. In this study, the effects of shot peening parameters such as shot diameter, shot speed, friction coefficient, and the number of impacts on the applied residual stress will be evaluated. To assess these parameters effect, firstly the shot peening process has been simulated by finite element method. Then, effects of the process parameters on the residual stress have been evaluated by response surface method as a statistical approach. Finally, a strong model is presented to predict the maximum residual stress induced by shot peening process in AISI 4340 steel. Also, the optimum parameters for the maximum residual stress are achieved. The results indicate that effect of shot diameter on the induced residual stress is increased by increasing the shot speed. Also, enhancing the friction coefficient magnitude always cannot lead to increase in the residual stress.

  20. Finite Element Analysis of Surface Residual Stress in Functionally Gradient Cemented Carbide Tool

    Science.gov (United States)

    Su, Chuangnan; Liu, Deshun; Tang, Siwen; Li, Pengnan; Qiu, Xinyi

    2018-03-01

    A component distribution model is proposed for three-component functionally gradient cemented carbide (FGCC) based on electron probe microanalysis results obtained for gradient layer thickness, microstructure, and elemental distribution. The residual surface stress of FGCC-T5 tools occurring during the fabrication process is analyzed using an ANSYS-implemented finite element method (FEM) and X-ray diffraction. A comparison of the experimental and calculated values verifies the feasibility of using FEM to analyze the residual surface stress in FGCC-T5 tools. The effects of the distribution index, geometrical shape, substrate thickness, gradient layer thickness, and position of the cobalt-rich layer on residual surface stress are studied in detail.

  1. Residual Stress Examination In Surface Layers Turned By Auto-Rotary Tool

    Science.gov (United States)

    Struharňanský, Jozef; Stančeková, Dana; Martikáň, Anton; Varga, Daniel; Kuždál, Viktor; Rákoci, Jozef

    2015-12-01

    In this article, unconventional kinematics of turning is examined with the aim on influence of cutting parameters on surface layers residual stress. The auto-rotary cutting tool prototype for turning was developed, designed and constructed at the University of Zilina. The tool is made of high speed steel. Residual stress examination of material 100Cr6 was performed by non-destructive measuring method of X-ray diffraction. This method is able to determine normal and shear stress conditions without damaging the examined sample.

  2. A strategy for accommodating residual stresses in the assessment of repair weldments based upon measurement of near surface stresses

    International Nuclear Information System (INIS)

    Mcdonald, E.J.; Hallam, K.R.; Flewitt, P.E.J.

    2005-01-01

    On many occasions repairs are undertaken to ferritic steel weldments on plant either during construction or to remove service induced defects. These repaired weldments are subsequently put into service with or without a post-weld heat treatment. In either case, but particularly for the latter, there is a need to accommodate the associated residual stresses in structural integrity assessments such as those based upon the R6 failure avoidance procedure. Although in some circumstances the residual macro-stresses developed within weldments of components and structures can be calculated this is not so readily achieved in the case of residual stresses introduced by repair welds. There is a range of physical and mechanical techniques available to undertake the measurement of macro-residual stresses. Of these X-ray diffraction has the advantage that it is essentially non-destructive and offers the potential for evaluating stresses, which exist in the near surface layer. Although for many structural integrity assessments both the magnitude and distribution of residual stresses have to be accommodated it is not practical to make destructive measurements on weld repaired components and structures to establish the through section distribution of stresses. An approach is to derive a description of the appropriate macro-stresses by a combination of measurement and calculation on trial ferritic steel repair weldments. Surface measurements on the plant can then be made to establish the relationship between the repaired component or structure and the trial weld and thereby improve confidence in predicted stresses and their distribution from the near-surface measured values. Hence X-ray diffraction measurements at the near-surface of the plant weldment can be used to underwrite the quality of the repair by confirming the magnitude and distribution of residual stresses used for the integrity assessment to demonstrate continued safe operation

  3. Surface Finish and Residual Stresses Induced by Orthogonal Dry Machining of AA7075-T651

    Directory of Open Access Journals (Sweden)

    Walid Jomaa

    2014-02-01

    Full Text Available The surface finish was extensively studied in usual machining processes (turning, milling, and drilling. For these processes, the surface finish is strongly influenced by the cutting feed and the tool nose radius. However, a basic understanding of tool/surface finish interaction and residual stress generation has been lacking. This paper aims to investigate the surface finish and residual stresses under the orthogonal cutting since it can provide this information by avoiding the effect of the tool nose radius. The orthogonal machining of AA7075-T651 alloy through a series of cutting experiments was performed under dry conditions. Surface finish was studied using height and amplitude distribution roughness parameters. SEM and EDS were used to analyze surface damage and built-up edge (BUE formation. An analysis of the surface topography showed that the surface roughness was sensitive to changes in cutting parameters. It was found that the formation of BUE and the interaction between the tool edge and the iron-rich intermetallic particles play a determinant role in controlling the surface finish during dry orthogonal machining of the AA7075-T651 alloy. Hoop stress was predominantly compressive on the surface and tended to be tensile with increased cutting speed. The reverse occurred for the surface axial stress. The smaller the cutting feed, the greater is the effect of cutting speed on both axial and hoop stresses. By controlling the cutting speed and feed, it is possible to generate a benchmark residual stress state and good surface finish using dry machining.

  4. SCC of 2304 Duplex Stainless Steel—Microstructure, Residual Stress and Surface Grinding Effects

    Directory of Open Access Journals (Sweden)

    Nian Zhou

    2017-02-01

    Full Text Available The influence of surface grinding and microstructure on chloride induced stress corrosion cracking (SCC behavior of 2304 duplex stainless steel has been investigated. Grinding operations were performed both parallel and perpendicular to the rolling direction of the material. SCC tests were conducted in boiling magnesium chloride according to ASTM G36; specimens were exposed both without external loading and with varied levels of four-point bend loading. Residual stresses were measured on selected specimens before and after exposure using the X-ray diffraction technique. In addition, in-situ surface stress measurements subjected to four-point bend loading were performed to evaluate the deviation between the actual applied loading and the calculated values according to ASTM G39. Micro-cracks, initiated by grinding induced surface tensile residual stresses, were observed for all the ground specimens but not on the as-delivered surfaces. Loading transverse to the rolling direction of the material increased the susceptibility to chloride induced SCC. Grinding induced tensile residual stresses and micro-notches in the as-ground surface topography were also detrimental.

  5. Effect of residual stress and surface roughness on the fatigue behaviour of aluminium matrix composites

    International Nuclear Information System (INIS)

    Smaga, M; Eifler, D

    2010-01-01

    In this investigation the fatigue properties of specimens manufactured with different turning parameters were investigated in stress-controlled constant amplitude tests at ambient temperature. The change of feed rate and depth of cut lead to a change in the near surface microstructure. Hence the fatigue properties were influenced significantly due to different surface roughness and surface residual stress resulting from the unequal turning processes. The cyclic deformation behaviour of AMC225xe is characterised by pronounced initial cyclic hardening. Continuous load increase tests allow a reliable estimation of the endurance limit of AMC225xe with one single specimen on the basis of cyclic deformation, temperature and electrical resistance data.

  6. Surface residual stress evaluation in double-electrode butt welded steel plates

    International Nuclear Information System (INIS)

    Estefen, S.F.; Gurova, T.; Castello, X.; Leontiev, A.

    2010-01-01

    Surface residual stress evaluation for double-electrode welding was studied. The stresses were monitored after each operational step: positioning, implementing of constraints, welding and constraints removal. The measurements were performed at the deposited metal, heat affected zone, base metal close to the weld joint and along the plate using the X-ray diffraction method. It was observed differences in the stress evaluations for double-electrode welding which resulted in lower bending distortions and higher values of surface residual stresses, compared with single-electrode welding. This behavior is associated with the stress distribution just after the welding processes in both heat affected zone and base metal close to the fillet for double-electrode welding. The main results from the laboratorial tests indicated lower values of the bending distortions for double-electrode welding compared with the single-electrode. In relation to the residual stress, the double-electrode welding generated, in general, higher stress values in both longitudinal and transversal directions.

  7. Residual-stress measurements

    Energy Technology Data Exchange (ETDEWEB)

    Ezeilo, A.N.; Webster, G.A. [Imperial College, London (United Kingdom); Webster, P.J. [Salford Univ. (United Kingdom)

    1997-04-01

    Because neutrons can penetrate distances of up to 50 mm in most engineering materials, this makes them unique for establishing residual-stress distributions non-destructively. D1A is particularly suited for through-surface measurements as it does not suffer from instrumental surface aberrations commonly found on multidetector instruments, while D20 is best for fast internal-strain scanning. Two examples for residual-stress measurements in a shot-peened material, and in a weld are presented to demonstrate the attractive features of both instruments. (author).

  8. Influence of residual stress on the adhesion and surface morphology of PECVD-coated polypropylene

    Science.gov (United States)

    Jaritz, Montgomery; Hopmann, Christian; Behm, Henrik; Kirchheim, Dennis; Wilski, Stefan; Grochla, Dario; Banko, Lars; Ludwig, Alfred; Böke, Marc; Winter, Jörg; Bahre, Hendrik; Dahlmann, Rainer

    2017-11-01

    The properties of plasma-enhanced chemical vapour deposition (PECVD) coatings on polymer materials depend to some extent on the surface and material properties of the substrate. Here, isotactic polypropylene (PP) substrates are coated with silicon oxide (SiO x ) films. Plasmas for the deposition of SiO x are energetic and oxidative due to the high amount of oxygen in the gas mixture. Residual stress measurements using single Si cantilever stress sensors showed that these coatings contain high compressive stress. To investigate the influence of the plasma and the coatings, residual stress, silicon organic (SiOCH) coatings with different thicknesses between the PP and the SiO x coating are used as a means to protect the substrate from the oxidative SiO x coating process. Pull-off tests are performed to analyse differences in the adhesion of these coating systems. It could be shown that the adhesion of the PECVD coatings on PP depends on the coatings’ residual stress. In a PP/SiOCH/SiO x -multilayer system the residual stress can be significantly reduced by increasing the thickness of the SiOCH coating, resulting in enhanced adhesion.

  9. Modeling and Parameter Optimization for Surface Roughness and Residual Stress in Dry Turning Process

    Directory of Open Access Journals (Sweden)

    M. H. El-Axir

    2017-10-01

    Full Text Available The influence of some turning variables and tool overhang on surface roughness parameters and residual stress induced due to machining 6061-T6 aluminum alloy is investigated in this paper. Four input parameters (cutting speed, feed rate, depth of cut and tool overhang are considered. Tests are carried out by precision turning operation on a lathe. Design of experiment techniques, i.e. response surface methodology (RSM and Taguchi's technique have been used to accomplish the objective of the experimental study. Surface roughness parameters are measured using a portable surface roughness device while residual stresses are measured employing deflection-etching technique using electrochemical analysis. The results obtained reveal that feed and rotational speed play significant role in determining the average surface roughness. Furthermore, the depth of cut and tool overhang are less significant parameters, whereas tool overhang interacts with feed rate. The best result of surface roughness was obtained using low or medium values of overhang with low speed and /or feed rate. Minimum maximum tensile residual stress can be obtained with a combination of tool overhang of 37 mm with very low depth of cut, low rotational speed and feed rate of 0.188 mm/rev.

  10. Application of X-rays and Synchrotron X Rays to Residual Stress Evaluation Near Surfaces

    International Nuclear Information System (INIS)

    Pyzalla, Anke

    1999-01-01

    A nondestructive residual stress analysis can be performed using diffraction methods. The easiest accessible radiation is characteristic X radiation that has a penetration depth of ∼10 microm suitable for the determination of the residual stresses in near-surface layers. Special techniques have been developed, e.g., with respect to in situ analyses of the stress state in oxide layers and the residual stress analysis in coarse grained zones of steel welds or annealed Ni-base alloys. Depending on the size of the gauge volume, neutron diffraction can provide information at depths of tens of millimetres of steel and many tens of millimetres of Al. An alternative to the use of the characteristic synchrotron radiation is the use of a high-energy polychromatic beam in an energy dispersive arrangement, which gives access to higher penetration depths at still gauge volumes as small as 100 microm x 100 microm x 1 mm in steel rods of 15-mm diameter. The combination of neutrons with conventional X rays and monochromatic and polychromatic synchrotron radiation allows for a comprehensive investigation of the phase composition, the texture, and the residual stresses

  11. Effects of Ultrasonic Nanocrystal Surface Modification on the Residual Stress, Microstructure, and Corrosion Resistance of 304 Stainless Steel Welds

    Science.gov (United States)

    Ye, Chang; Telang, Abhishek; Gill, Amrinder; Wen, Xingshuo; Mannava, Seetha R.; Qian, Dong; Vasudevan, Vijay K.

    2018-01-01

    In this study, ultrasonic nanocrystal surface modification (UNSM) of 304 stainless steel welds was carried out. UNSM effectively eliminates the tensile stress generated during welding and imparts beneficial compressive residual stresses. In addition, UNSM can effectively refine the grains and increase hardness in the near-surface region. Corrosion tests in boiling MgCl2 solution demonstrate that UNSM can significantly improve the corrosion resistance due to the compressive residual stresses and changes in the near-surface microstructure.

  12. Effects of Ultrasonic Nanocrystal Surface Modification on the Residual Stress, Microstructure, and Corrosion Resistance of 304 Stainless Steel Welds

    Science.gov (United States)

    Ye, Chang; Telang, Abhishek; Gill, Amrinder; Wen, Xingshuo; Mannava, Seetha R.; Qian, Dong; Vasudevan, Vijay K.

    2018-03-01

    In this study, ultrasonic nanocrystal surface modification (UNSM) of 304 stainless steel welds was carried out. UNSM effectively eliminates the tensile stress generated during welding and imparts beneficial compressive residual stresses. In addition, UNSM can effectively refine the grains and increase hardness in the near-surface region. Corrosion tests in boiling MgCl2 solution demonstrate that UNSM can significantly improve the corrosion resistance due to the compressive residual stresses and changes in the near-surface microstructure.

  13. A countermeasure for external stress corrosion cracking in piping components by means of residual stress improvement on the outer surface

    International Nuclear Information System (INIS)

    Tanaka, Yasuhiro; Umemoto, Tadahiro

    1988-01-01

    Many techniques have been proposed as countermeasures for the External Stress Corrosion Cracking (ESCC) on austenitic stainless steel piping caused by sea salt particles. However, not one seems perfect. The method proposed here is an expansion of IHSI (Induction Heating Stress Improvement) which has been successfully implemented in many nuclear power plants as a remedy for Intergranular Stress Corrossion Cracking. The proposed method named EIHSI (External IHSI) can make the residual stress compressive on the outer surface of the piping components. In order to confirm the effectiveness of EIHSI, one series of tests were conducted on a weld joint between the pipe flange and the straight pipe. The measured residual stresses and also the results of the cracking test revealed that EIHSI is a superior method to suppress the ESCC. The outline of EIHSI and the verification tests are presented in this paper. (author)

  14. A wafer mapping technique for residual stress in surface micromachined films

    International Nuclear Information System (INIS)

    Schiavone, G; Murray, J; Smith, S; Walton, A J; Desmulliez, M P Y; Mount, A R

    2016-01-01

    The design of MEMS devices employing movable structures is crucially dependant on the mechanical behaviour of the deposited materials. It is therefore important to be able to fully characterize the micromachined films and predict with confidence the mechanical properties of patterned structures. This paper presents a characterization technique that enables the residual stress in MEMS films to be mapped at the wafer level by using microstructures released by surface micromachining. These dedicated MEMS test structures and the associated measurement techniques are used to extract localized information on the strain and Young’s modulus of the film under investigation. The residual stress is then determined by numerically coupling this data with a finite element analysis of the structure. This paper illustrates the measurement routine and demonstrates it with a case study using electrochemically deposited alloys of nickel and iron, particularly prone to develop high levels of residual stress. The results show that the technique enables wafer mapping of film non-uniformities and identifies wafer-to-wafer differences. A comparison between the results obtained from the mapping technique and conventional wafer bow measurements highlights the benefits of using a procedure tailored to films that are non-uniform, patterned and surface-micromachined, as opposed to simple standard stress extraction methods. The presented technique reveals detailed information that is generally unexplored when using conventional stress extraction methods such as wafer bow measurements. (paper)

  15. Surface Roughness and Residual Stresses of High Speed Turning 300 M Ultrahigh Strength Steel

    Directory of Open Access Journals (Sweden)

    Zhang Huiping

    2014-03-01

    Full Text Available Firstly, a single factor test of the surface roughness about tuning 300 M steel is done. According to the test results, it is direct to find the sequence of various factors affecting the surface roughness. Secondly, the orthogonal cutting experiment is carried out from which the primary and secondary influence factors affecting surface roughness are obtained: feed rate and corner radius are the main factors affecting surface roughness. The more the feed rate, the greater the surface roughness. In a certain cutting speed rang, the surface roughness is smaller. The influence of depth of cut to the surface roughness is small. Thirdly, according to the results of the orthogonal experiment, the prediction model of surface roughness is established by using regressing analysis method. Using MatLab software, the prediction mode is optimized and the significance test of the optimized model is done. It showed that the prediction model matched the experiment results. Finally, the surface residual stress test of turning 300 M steel is done and the residual stress of the surface and along the depth direction is measured.

  16. X-ray measurement of residual stresses in laser surface melted Ti-6Al-4V alloy

    NARCIS (Netherlands)

    Robinson, J.M.; van Brussel, B.A.; de Hosson, J.T.M.; Reed, R.C.

    1996-01-01

    In this paper, we report on the residual stresses in laser surface melted Ti-6Al-4V, determined using X-ray diffraction methods. The principal result is that there is an increase in the transverse residual stress with each successive, overlapping laser track. The result can be used to explain the

  17. Residual stress evaluation of austenitic stainless steel with a finished surface by polychromatic X-ray method

    Energy Technology Data Exchange (ETDEWEB)

    Shibano, Jun-ichi; Ukai, Takayoshi; Tadano, Shigeru [Hokkaido Univ., Sapporo (Japan). Faculty of Engineering; Todoh, Masahiro

    1995-11-01

    The residual stress in a subsurface layer of austenitic stainless steel with a finished surface was evaluated by the polychromatic X-ray method. A surface of austenitic stainless steel SUS316 plate was ground and lapped as the specimen. In this method, the relation between strain and depth was approximated with a linear function or an exponential function, and it was assumed that the plane stress state existed in each subsurface layer in the depth direction of the specimen. As a result, the residual strain which was estimated under the assumption of the exponential function showed more reasonable distribution than that of the linear function. In addition, the residual stress which was calculated from the strain distribution was maximum tension at the surface of the specimen, and maximum compression at a position 3 {mu}m below the surface. Therefore, the steep gradient of residual stress could be confirmed in a subsurface layer of the SUS316 with a finished surface. (author).

  18. Residual compressive surface stress increases the bending strength of dental zirconia.

    Science.gov (United States)

    Inokoshi, Masanao; Zhang, Fei; Vanmeensel, Kim; De Munck, Jan; Minakuchi, Shunsuke; Naert, Ignace; Vleugels, Jozef; Van Meerbeek, Bart

    2017-04-01

    To assess the influence of surface treatment and thermal annealing on the four-point bending strength of two ground dental zirconia grades. Fully-sintered zirconia specimens (4.0×3.0×45.0mm 3 ) of Y-TZP zirconia (LAVA Plus, 3M ESPE) and Y-TZP/Al 2 O 3 zirconia (ZirTough, Kuraray Noritake) were subjected to four surface treatments: (1) 'GROUND': all surfaces were ground with a diamond-coated grinding wheel on a grinding machine; (2) 'GROUND+HEAT': (1) followed by annealing at 1100°C for 30min; (3) 'GROUND+Al 2 O 3 SANDBLASTED': (1) followed by sandblasting using Al 2 O 3 ; (4) 'GROUND+CoJet SANDBLASTED': (1) followed by tribochemical silica (CoJet) sandblasting. Micro-Raman spectroscopy was used to assess the zirconia-phase composition and potentially induced residual stress. The four-point bending strength was measured using a universal material-testing machine. Weibull analysis revealed a substantially higher Weibull modulus and slightly higher characteristic strength for ZirTough (Kuraray Noritake) than for LAVA Plus (3M ESPE). For both zirconia grades, the 'GROUND' zirconia had the lowest Weibull modulus in combination with a high characteristic strength. Sandblasting hardly changed the bending strength but substantially increased the Weibull modulus of the ground zirconia, whereas a thermal treatment increased the Weibull modulus of both zirconia grades but resulted in a significantly lower bending strength. Micro-Raman analysis revealed a higher residual compressive surface stress that correlated with an increased bending strength. Residual compressive surface stress increased the bending strength of dental zirconia. Thermal annealing substantially reduced the bending strength but increased the consistency (reliability) of 'GROUND' zirconia. Copyright © 2017 The Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

  19. Near-Surface Residual Stress-Profiling with High Frequency Eddy Current Conductivity Measurement

    Science.gov (United States)

    Hillmann, S.; Heuer, H.; Baron, H.-U.; Bamberg, J.; Yashan, A.; Meyendorf, N.

    2009-03-01

    The lifetime of aero engine components can be extended by applying an additional strain to the material. Typical aero engine-alloys like Nickel-Base superalloys or Titanium alloys can be surface-treated by use of shot peening to induce the compressive strain near the surface. However, in order to use the additional life for critical aero engine components, a quantitative determination of strain gradients near the surface has to be carried out periodically. We propose to measure the depth-profile of residual stresses non-destructively by use of high frequency eddy current techniques. This paper presents results obtained with an experimental set-up based on a high precision impedance analyzer. Test samples prepared from IN718 by shot peening of different intensities can be easily distinguished. By sweeping the frequency from 100 kHz up to 100 MHz a depth profile for the electrical conductivity from 50 μm to 500 μm can be obtained. The measured conductivity profile is a resultant from residual stresses, cold work, surface roughness and the texture of the material. In addition, first results for strain profiling obtained with industry applicable NDE instrument will be presented.

  20. Evaluation of surface residual stresses in HVOF sprayed WC-12Co coatings by XRD and ED-hole drilling

    Energy Technology Data Exchange (ETDEWEB)

    Azizpour, M. Jalali; Nourouzi, S. [Babol University of Technology, Babol (Iran, Islamic Republic of)

    2013-09-15

    Thermally sprayed coatings are inherently associated with residual stresses in the coatings. These stresses have a noticeable effect on the physical and mechanical properties of coatings. The high speed hole drilling method is widely used to measure the residual stress. Due to the nature of the thermally sprayed coatings, the application of this method for WC/Co coatings has some limitations. In the current study, WC-12Co coatings were deposited using HVOF thermal spraying. The electro discharge hole drilling method was developed to measure the through thickness residual stress in WC-Co thermally sprayed coatings. Morphological studies were conducted using optical microscopy and scanning electron microscopy (SEM) to evaluate the powder and coating characteristics. The sin2ψ method was used to evaluate the surface residual stress by means of XRD. The residual stress at the surface using EDM and XRD was approximately -32.54 MPa and -40.6 MPa respectively. The experimental results reveal that the stress curves are not uniform through the coating thickness. It has been found that the mean residual stress is of approximately -126 MPa. Obtained results are in good agreement with the reported values from literatures. The developed method confirms the feasibility of residual stresses measurement for HVOF thermally sprayed WC-Co coatings.

  1. Effects of Ultrasonic Nanocrystal Surface Modification (UNSM) on Residual Stress State and Fatigue Strength of AISI 304

    Science.gov (United States)

    Cherif, A.; Pyoun, Y.; Scholtes, B.

    2010-03-01

    The effects of a new mechanical surface treatment method, called ultrasonic nanocrystal surface modification (UNSM), on near-surface microstructures and residual stress states as well as on the fatigue behavior of an austenitic steel AISI 304 are investigated and discussed. The results are compared with consequences of other mechanical surface treatment methods such as deep rolling or shot peening.

  2. Modelling the Effects of Surface Residual Stresses on Fatigue Behavior of PM Disk Alloys, Phase I

    Data.gov (United States)

    National Aeronautics and Space Administration — A finite element based model will be developed and validated to capture the evolution of residual stresses and cold work at machined features of compressor and...

  3. Non destructive evaluation of residual stresses in welding and hard-surfacing processes

    International Nuclear Information System (INIS)

    Suarez, J.C.; Fernandez, L.M.; Cruz, C.; Aragon, B.; Merino, F.

    1995-01-01

    In this paper transversal and longitudinal stress profiles in welding and hard-surfacing by welding processes are presented. The stresses were measured by RMS of Barkhausen signal. In this work it is shown that in each case the level of stresses is strongly dependent on the number of weld beads of surfacing layers deposited. The subsequent deposition of new weld beads or surfacing layers produces a stress-relieving effect

  4. Residual stresses in surface induction hardening of steels: Comparison between experiment and simulation

    International Nuclear Information System (INIS)

    Coupard, Dominique; Palin-luc, Thierry; Bristiel, Philippe; Ji, Vincent; Dumas, Christian

    2008-01-01

    Deep induction hardening has been performed on two batches of smooth cylindrical specimens with a hardening depth respectively around 2 mm and 3 mm. The distributions of axial and circumferential residual stresses are analysed for the two specimen batches by X-ray diffraction technique. The radial normal stress field is estimated through the use of the well known Moore and Evans correction. Finally, the experimental residual stresses are compared with those obtained from a multiphysic finite element modelling of the whole induction treatment process, including electromagnetic, thermal, metallurgical and mechanical phenomena. The simulated residual stress field is in good agreement with X-ray analysis especially at depths lower than one-tenth the specimen diameter. At deeper depths, a correction of the experimental X-ray analysis has been done to obtain realistic values

  5. Residual stresses around Vickers indents

    International Nuclear Information System (INIS)

    Pajares, A.; Guiberteau, F.; Steinbrech, R.W.

    1995-01-01

    The residual stresses generated by Vickers indentation in brittle materials and their changes due to annealing and surface removal were studied in 4 mol% yttria partially stabilized zirconia (4Y-PSZ). Three experimental methods to gain information about the residual stress field were applied: (i) crack profile measurements based on serial sectioning, (ii) controlled crack propagation in post indentation bending tests and (iii) double indentation tests with smaller secondary indents located around a larger primary impression. Three zones of different residual stress behavior are deduced from the experiments. Beneath the impression a crack free spherical zone of high hydrostatic stresses exists. This core zone is followed by a transition regime where indentation cracks develop but still experience hydrostatic stresses. Finally, in an outward third zone, the crack contour is entirely governed by the tensile residual stress intensity (elastically deformed region). Annealing and surface removal reduce this crack driving stress intensity. The specific changes of the residual stresses due to the post indentation treatments are described and discussed in detail for the three zones

  6. Three-dimensional welding residual stresses evaluation based on the eigenstrain methodology via X-ray measurements at the surface

    Science.gov (United States)

    Ogawa, Masaru

    2014-12-01

    In order to assure structural integrity for operating welded structures, it is necessary to evaluate crack growth rate and crack propagation direction for each observed crack non-destructively. Here, three dimensional (3D) welding residual stresses must be evaluated to predict crack propagation. Today, X-ray diffraction is used and the ultrasonic method has been proposed as non-destructive method to measure residual stresses. However, it is impossible to determine residual stress distributions in the thickness direction. Although residual stresses through a depth of several tens of millimeters can be evaluated non-destructively by neutron diffraction, it cannot be used as an on-site measurement technique. This is because neutron diffraction is only available in special irradiation facilities. Author pays attention to the bead flush method based on the eigenstrain methodology. In this method, 3D welding residual stresses are calculated by an elastic Finite Element Method (FEM) analysis from eigenstrains which are evaluated by an inverse analysis from released strains by strain gauges in the removal of the reinforcement of the weld. Here, the removal of the excess metal can be regarded as non-destructive treatment because toe of weld which may become crack starters can be eliminated. The effectiveness of the method has been proven for welded plates and pipes even with relatively lower bead height. In actual measurements, stress evaluation accuracy becomes poorer because measured values of strain gauges are affected by processing strains on the machined surface. In the previous studies, the author has developed the bead flush method that is free from the influence of the affecting strains by using residual strains on surface by X-ray diffraction. However, stress evaluation accuracy is not good enough because of relatively poor measurement accuracy of X-ray diffraction. In this study, a method to improve the estimation accuracy of residual stresses in this method is

  7. Surface preparation for XRD residual stress measurements; Preparacao de superficie para medicao de tensoes residuais em soldagem por DRX

    Energy Technology Data Exchange (ETDEWEB)

    Mishchenko, Andrii; Oliveira, Bruno Jose de; Scotti, Americo, E-mail: asmwelder@gmail.com, E-mail: brunojoliveira7@gmail.com, E-mail: ascotti@mecanica.ufu.br [Universidade Federal de Uberlandia (UFU), MG (Brazil)

    2016-10-15

    A characteristic feature of the X Ray Diffraction (XRD) method for stress determination is that measurements occur at a thin surface layer. Steel sheets come with surfaces modified by lamination, cleaning (sandblasting, grinding) and even corrosion, which induce residual stresses or roughness inherent to the material. Therefore, surface preparation prior to the residual stress measurement is essential, although no standard procedure seems to be available. A general recommendation is to remove a thin layer so that only residual stresses related to the welding process will be measured. In this study, the use of portable electrolytic equipment was evaluated for mechanized surface material removal. Chemical compositions of electrolytic solutions and the influence of current on the removed material, removal time and temperature during the process were studied. As a result, a suitable chemical solution for electro etching of low carbon steel was developed and a set of “soft” parameters that allowed the removal of about 300 um in a reasonable time was found. Higher currents reduce the removal time, yet increasing the consumption of the solution and plate temperature (which could adversely alter the microstructure or generate thermal stresses). Furthermore, the influence of these parameters on the operability of the process was demonstrated. (author)

  8. Effect of laser surface hardening on the microstructure, hardness and residual stresses of austempered ductile iron grades

    Energy Technology Data Exchange (ETDEWEB)

    Soriano, C., E-mail: csoriano@tekniker.es [Tekniker-IK4, Manufacturing Processes Department, Avda. Otaola 20, CP-20600, Eibar (Gipuzkoa) (Spain); Leunda, J.; Lambarri, J.; Garcia Navas, V.; Sanz, C. [Tekniker-IK4, Manufacturing Processes Department, Avda. Otaola 20, CP-20600, Eibar (Gipuzkoa) (Spain)

    2011-06-01

    A study of the laser surface hardening process of two austempered ductile iron grades, with different austempering treatments has been carried out. Hardening was performed with an infrared continuous wave Nd:YAG laser in cylindrical specimens. The microstructure of the laser hardened samples was investigated using an optical microscope, microhardness profiles were measured and surface and radial residual stresses were studied by an X-ray diffractometer. Similar results were achieved for both materials. A coarse martensite with retained austenite structure was found in the treated area, resulting in a wear resistant effective layer of 0.6 mm to 1 mm with a microhardness between 650 HV and 800 HV. Compressive residual stresses have been found at the hardened area being in agreement with the microhardness and microstructural variations observed. The achieved results point out that the laser surface hardening is a suitable method for improving the mechanical properties of austempered ductile irons.

  9. On the Feasibility of Eddy Current Characterization of the Near-Surface Residual Stress Distribution in Nickel-Base Superalloys

    International Nuclear Information System (INIS)

    Blodgett, Mark P.; Nagy, Peter B.

    2004-01-01

    In light of its frequency-dependent penetration depth, the measurement of eddy current conductivity has been suggested as a possible means to allow the nondestructive evaluation of subsurface residual stresses in shot-peened specimens. This technique is based on the so-called electroelastic effect, i.e., the stress-dependence of the electrical conductivity. Unfortunately, the relatively small (∼1%) change in electrical conductivity caused by the presence of compressive residual stresses is often distorted, or even completely overshadowed, by the accompanying conductivity loss caused by cold work and surface roughness effects. Recently, it was observed that, in contrast with most other materials, shot-peened Waspaloy and IN100 specimens exhibit an apparent increase in electrical conductivity at increasing inspection frequencies. This observation by itself indicates that in these materials the measured conductivity change is probably dominated by residual stress effects, since both surface roughness and increased dislocation density are known to decrease rather than increase the conductivity and the presence of crystallographic texture does not affect the electrical conductivity of these materials, which crystallize in cubic symmetry. Our preliminary experiments indicate that probably there exists a unique 'window of opportunity' for eddy current NDE in nickel-base superalloys. We identified five major effects that contribute to this fortunate constellation of material properties, which will be reviewed in this presentation

  10. The application of white radiation to residual stress analysis in the intermediate zone between surface and volume

    CERN Document Server

    Genzel, C; Wallis, B; Reimers, W

    2001-01-01

    Mechanical surface processing is known to give rise to complex residual stress fields in the near surface region of polycrystalline materials. Consequently, their analysis by means of non-destructive X-ray and neutron diffraction methods has become an important topic in materials science. However, there remains a gap with respect to the accessible near surface zone, which concerns a range between about 10 mu m and 1 mm, where the conventional X-ray methods are no longer and the neutron methods are not yet sensitive. In order to achieve the necessary penetration depth tau to perform residual stress analysis (RSA) in this region, advantageous use can be made of energy dispersive X-ray diffraction of synchrotron radiation (15-60 keV) in the reflection mode. Besides an example concerning the adaptation of methods applied so far in the angle dispersive RSA to the energy dispersive case, the concept of a new materials science beamline at BESSY II for residual stress and texture analysis is presented.

  11. Residual stresses in material processing

    Science.gov (United States)

    Kozaczek, K. J.; Watkins, T. R.; Hubbard, C. R.; Wang, Xun-Li; Spooner, S.

    Material manufacturing processes often introduce residual stresses into the product. The residual stresses affect the properties of the material and often are detrimental. Therefore, the distribution and magnitude of residual stresses in the final product are usually an important factor in manufacturing process optimization or component life prediction. The present paper briefly discusses the causes of residual stresses. It then addresses the direct, nondestructive methods of residual stress measurement by X ray and neutron diffraction. Examples are presented to demonstrate the importance of residual stress measurement in machining and joining operations.

  12. Effect of Tip Shape of Frictional Stir Burnishing Tool on Processed Layer’s Hardness, Residual Stress and Surface Roughness

    Directory of Open Access Journals (Sweden)

    Yoshimasa Takada

    2018-01-01

    Full Text Available Friction stir burnishing (FSB is a surface-enhancement method used after machining, without the need for an additional device. The FSB process is applied on a machine that uses rotation tools (e.g., machining center or multi-tasking machine. Therefore, the FSB process can be applied immediately after the cutting process using the same machine tool. Here, we apply the FSB to the shaft materials of 0.45% C steel using a multi-tasking machine. In the FSB process, the burnishing tool rotates at a high-revolution speed. The thin surface layer is rubbed and stirred as the temperature is increased and decreased. With the FSB process, high hardness or compressive residual stress can be obtained on the surface layer. However, when we applied the FSB process using a 3 mm diameter sphere tip shape tool, the surface roughness increased substantially (Ra = 20 µm. We therefore used four types of tip shape tools to examine the effect of burnishing tool tip radius on surface roughness, hardness, residual stress in the FSB process. Results indicated that the surface roughness was lowest (Ra = 10 µm when the tip radius tool diameter was large (30 mm.

  13. Micro-Slotting Technique for Reliable Measurement of Sub-Surface Residual Stress in Ti-6Al-4V (Preprint)

    Science.gov (United States)

    2017-09-28

    measuring local residual stresses in a variety of materials. The micro-slotting method relies on a Scanning Electron Microscope – Focused Ion Beam (SEM...residual stresses in a variety of materials. The micro-slotting method relies on a Scanning Electron Microscope – Focused Ion Beam (SEM-FIB) system for...between milled slots for ə% error in the stress calculations. Residual stress measurements The three series of micro-slotting measurements show

  14. Effect of residual stress and hardening on grain boundary sliding in welds of low-carbon stainless steels with surface machining

    International Nuclear Information System (INIS)

    Mori, Hiroaki; Mochizuki, Masahito; Nishimoto, Kazutoshi; Katsuyama, Jinya

    2008-01-01

    To clarify the effects of residual stress and hardening on intergranular stress corrosion cracking (IGSCC) behavior in welds of low-carbon austenitic stainless steels with surface machining, residual stress and hardness were evaluated by 3-dimentional thermo elastic-plastic analysis and grain boundary sliding behavior was examined using a constant strain rate tensile test. It was revealed that grain boundary sliding occurred in the material at 561K by the tensile test with the numerically simulated tensile residual stress due to multi-pass welding and surface machining. In addition, it was clarified that the grain boundary energy is raised by the grain boundary sliding. On the basis of these results, it was concluded that the cause of IGSCC in the welds of low-carbon austenitic stainless steel with surface hardening is the increase in grain boundary energy due to grain boundary sliding induced by residual stress of multi pass welding and surface hardening. (author)

  15. Triaxial X-Ray Diffraction Method and its Application to Monitor Residual Stress in Surface Layers after High-Feed Milling

    Science.gov (United States)

    Zaušková, Lucia; Czán, Andrej; Šajgalík, Michal; Pobijak, Jozef; Mikloš, Matej

    2017-10-01

    High-feed milling is a milling method characteristic with shallow depth of cut and high feed rate to maximize the amount of removed metal from a part, generating residual stresses in the surface and subsurface layers of the machined parts. The residual stress has a large influence on the functional properties of the components. The article is focused on the application of triaxial x-ray diffraction method to monitor residual stresses after high feed milling. Significance of triaxial measuring method is the capability of measuring in different angles so it is possible to acquire stress tensor containing normal and shear stress components.

  16. Evaluation of surface residual stresses VIA X-Ray diffraction in bars of AISI 1045 steel produced by combined cold drawing

    International Nuclear Information System (INIS)

    Nunes, Rafael Menezes; Rocha, Alexandre da Silva

    2010-01-01

    The residual stresses represent one of the main potentials for the appearance of distortions, like bending and dimensional changes in mechanical components during the manufacturing process. This work accomplished an evaluation of the surface residual stresses from bars of AISI1045. The samples were removed from five steps of a combined cold-drawing process: pre-straightening, shot-blasting, cold-drawing with 15° and 20°, straightening and polishing by crossed rolls ('PERC') with 16° and 18°. Starting from obtained deformation values the level of surface longitudinal residual stresses for each accomplished point was estimated. (author)

  17. Influence of surface treatments on corrosion resistance of stainless steels. Residual stresses in metals

    International Nuclear Information System (INIS)

    Berge, J. Philippe

    1968-05-01

    In a first part, this research thesis proposes presentation of the definition of a surface condition: chemical characteristics such as passivity and contamination, physical characteristics (obtained through micrographic methods, X ray diffusion, magnetic methods), and micro-geometrical characteristics. The author notably discusses the measurement of characteristics either by appropriate conventional methods or by an original method in the case of passivity. In a second part, the author reports the study of the influence of surface condition on different types of corrosion of stainless steels in chemical environments (corrosion in sulphuric acid, intergranular corrosion, stress corrosion cracking in magnesium chloride, pitting corrosion) and of high temperature oxidation (corrosion in pressurized water, oxidation in dry vapour or in carbon dioxide)

  18. The Surface Layer Mechanical Condition and Residual Stress Forming Model in Surface Plastic Deformation Process with the Hardened Body Effect Consideration

    Science.gov (United States)

    Mahalov, M. S.; Blumenstein, V. Yu

    2017-10-01

    The mechanical condition and residual stresses (RS) research and computational algorithms creation in complex types of loading on the product lifecycle stages relevance is shown. The mechanical state and RS forming finite element model at surface plastic deformation strengthening machining, including technological inheritance effect, is presented. A model feature is the production previous stages obtained transformation properties consideration, as well as these properties evolution during metal particles displacement through the deformation space in the present loading step.

  19. Surface mechanical property and residual stress of peened nickel-aluminum bronze determined by in-situ X-ray diffraction

    Science.gov (United States)

    Wang, Chengxi; Jiang, Chuanhai; Zhao, Yuantao; Chen, Ming; Ji, Vincent

    2017-10-01

    As one of the most important surface strengthening method, shot peening is widely used to improve the fatigue and stress corrosion crack resistance of components by introducing the refined microstructure and compressive residual stress in the surface layer. However, the mechanical properties of this thin layer are different from the base metal and are difficult to be characterized by conventional techniques. In this work, a micro uniaxial tensile tester equipped with in-situ X-ray stress analyzer was employed to make it achievable on a nickel-aluminum bronze with shot peening treatment. According to the equivalent stress-strain relationship based on Von Mises stress criterion, the Young's modulus and yield strength of the peened layer were calculated. The results showed that the Young's modulus was the same as the bulk material, and the yield strength corresponding to the permanent plastic strain of 0.2% was increased by 21% after SP. But the fractographic analysis showed that the fracture feature of the surface layer was likely to transform from the dimple to the cleavage, indicating the improved strength might be attained at the expense of ductility. The monotonic and cyclic loading were also performed via the same combined set-up. In addition, the specific relaxation behavior of compressive residual stress was quantified by linear logarithm relationship between residual stress and cycle numbers. It was found that the compressive residual stress mainly relaxed in the first few cycles, and then reached steady state with further cycles. The relaxation rate and the stable value were chiefly depended on the stress amplitude and number of cycles. The retained residual stress kept in compressive under all given applied stress levels, suggesting that the shot peening could introduce a more stable surface layer of compressive residual stress other than the elevated strength of nickel-aluminum bronze alloy.

  20. Theoretical Study on Synchronous Characterization of Surface and Interfacial Mechanical Properties of Thin-Film/Substrate Systems with Residual Stress Based on Pressure Blister Test Technique

    Directory of Open Access Journals (Sweden)

    Zhi-xin Yang

    2018-01-01

    Full Text Available In this study, based on the pressure blister test technique, a theoretical study on the synchronous characterization of surface and interfacial mechanical properties of thin-film/substrate systems with residual stress was presented, where the problem of axisymmetric deformation of a blistering film with initial stress was analytically solved and its closed-form solution was presented. The expressions to determine Poisson’s ratios, Young’s modulus, and residual stress of surface thin films were derived; the work done by the applied external load and the elastic energy stored in the blistering thin film were analyzed in detail and their expressions were derived; and the interfacial adhesion energy released per unit delamination area of thin-film/substrate (i.e., energy release rate was finally presented. The synchronous characterization technique presented here has theoretically made a big step forward, due to the consideration for the residual stress in surface thin films.

  1. Residual stress by repair welds

    International Nuclear Information System (INIS)

    Mochizuki, Masahito; Toyoda, Masao

    2003-01-01

    Residual stress by repair welds is computed using the thermal elastic-plastic analysis with phase-transformation effect. Coupling phenomena of temperature, microstructure, and stress-strain fields are simulated in the finite-element analysis. Weld bond of a plate butt-welded joint is gouged and then deposited by weld metal in repair process. Heat source is synchronously moved with the deposition of the finite-element as the weld deposition. Microstructure is considered by using CCT diagram and the transformation behavior in the repair weld is also simulated. The effects of initial stress, heat input, and weld length on residual stress distribution are studied from the organic results of numerical analysis. Initial residual stress before repair weld has no influence on the residual stress after repair treatment near weld metal, because the initial stress near weld metal releases due to high temperature of repair weld and then stress by repair weld regenerates. Heat input has an effect for residual stress distribution, for not its magnitude but distribution zone. Weld length should be considered reducing the magnitude of residual stress in the edge of weld bead; short bead induces high tensile residual stress. (author)

  2. Weld Residual Stress in Corner Boxing Joints

    OpenAIRE

    Kazuyoshi, Matsuoka; Tokuharu, Yoshii; Ship Research Institute, Ministry of Transport; Ship Research Institute, Ministry of Transport

    1998-01-01

    Fatigue damage often occurs in corner boxing welded joints because of stress concentration and residual stress. The hot spot stress approach is applicable to stress concentration. However, the number of suitable methods for estimating residual stress in welded joints is limited. The purpose of this paper is to clarify the residual stress in corner boxing joints. The method of estimating residual stresses based on the inherent stress technique is presented. Residual stress measurements are per...

  3. The method for measuring residual stress in stainless steel pipes

    International Nuclear Information System (INIS)

    Shimov, Georgy; Rozenbaum, Mikhail; Serebryakov, Alexandr; Serebryakov, Andrey

    2016-01-01

    The main reason of appearance and growth of corrosion damages of the nuclear steam generator heat exchanger tubes is the process of stress-corrosion cracking of metal under the influence of residual tensile stress. Methods used in the production for estimating residual stresses (such as a method of ring samples) allow measuring only the average tangential stress of the pipe wall. The method of ring samples does not allow to assess the level of residual stress in the surface layer of the pipe. This paper describes an experimental method for measuring the residual stresses on the pipe surface by etching a thin surface layer of the metal. The construction and working principle of a trial installation are described. The residual stresses in the wall of the tubes 16 × 1.5 mm (steel AISI 321) for nuclear steam generators is calculated. Keywords: heat exchange pipes, stress corrosion cracking, residual stresses, stress distribution, stress measurement.

  4. Residual stress analysis: a review

    International Nuclear Information System (INIS)

    Finlayson, T.R.

    1983-01-01

    The techniques which are or could be employed to measure residual stresses are outlined. They include X-ray and neutron diffraction. Comments are made on the reliability and accuracy to be expected from particular techniques

  5. Process for measuring residual stresses

    International Nuclear Information System (INIS)

    Elfinger, F.X.; Peiter, A.; Theiner, W.A.; Stuecker, E.

    1982-01-01

    No single process can at present solve all problems. The complete destructive processes only have a limited field of application, as the component cannot be reused. However, they are essential for the basic determination of stress distributions in the field of research and development. Destructive and non-destructive processes are mainly used if investigations have to be carried out on original components. With increasing component size, the part of destructive tests becomes smaller. The main applications are: quality assurance, testing of manufactured parts and characteristics of components. Among the non-destructive test procedures, X-raying has been developed most. It gives residual stresses on the surface and on surface layers near the edges. Further development is desirable - in assessment - in measuring techniques. Ultrasonic and magnetic crack detection processes are at present mainly used in research and development, and also in quality assurance. Because of the variable depth of penetration and the possibility of automation they are gaining in importance. (orig./RW) [de

  6. Validation of welded joint residual stress simulation

    International Nuclear Information System (INIS)

    Computational mechanics is being increasingly applied to predict the state of residual stress in welded joints for nuclear power plant applications. Motives for undertaking such calculations include optimising the design of welded joints and weld procedures, assessing the effectiveness of mitigation processes, providing more realistic inputs to structural integrity assessments and underwriting safety cases for operating nuclear power plant. Fusion welding processes involve intense localised heating to melt the surfaces to be joined and introduction of molten weld filler metal. A complex residual stress field develops at the weld through solidification, differential thermal contraction, cyclic thermal plasticity, phase transformation and chemical diffusion processes. The calculation of weld residual stress involves detailed non-linear analyses where many assumptions and approximations have to be made. In consequence, the accuracy and reliability of solutions can be highly variable. This paper illustrates the degree of variability that can arise in weld residual stress simulation results and summarises the new R6 guidelines which aim to improve the reliability and accuracy of computational predictions. The requirements for validating weld simulations are reviewed where residual stresses are to be used in fracture mechanics analysis. This includes a discussion of how to obtain and interpret measurements from mock-ups, benchmark weldments and published data. Benchmark weldments are described that illustrate some of the issues and show how validation of numerical prediction of weld residual stress can be achieved. Finally, plans for developing the weld modelling guidelines and associated benchmarks are outlined

  7. The effect of ammonium partial pressure on residual stresses in surface layer of SW7M HSS steel after vacuum nitriding 'NITROVAC'79'

    International Nuclear Information System (INIS)

    Gawronski, Z.

    1997-01-01

    The effect of the nitriding atmosphere on the residual stresses in the surface layer of the SW7M HSS steel has been investigated in the work. It has been proved that the pressure influences the distribution of those stresses to a great extent. At lower pressures (20 hPa and 40 hPa) at which only one zone is being created - the one of internal nitriding, without that of ε type nitrides on the surface - the highest residual stresses are operating on the HSS steel surface itself or eventually in the subsurface region very close to the surface. In the difference, in case of higher pressure (120 hPa and 240 hPa), the highest stresses are operating at great depth 8-12 μm from the steel surface - depending on the thickness of the ε type nitride layer created on the steel surface at those pressure. All the relevant stresses are compressive one. (author). 6 refs, 4 figs, 1 tab

  8. THE INFLUENCE OF GRINDING CONDITIONS ON THE DISTRIBUTION OF RESIDUAL STRESS IN THE SURFACE LAYER OF 17crni6-6 STEEL AFTER CARBURIZING

    Directory of Open Access Journals (Sweden)

    Jacek Sawicki

    2017-06-01

    Full Text Available This paper presents the results of a study aimed at determining the residual stress which results from developing the surface layer by low-pressure and conventional carburizing and grinding of 17CrNi6-6 steel. A synergistic effect of thermochemical and abrasive treatment was examined on ring samples used to study residual stress by Davidenkov’s method. Samples were subjected to vacuum carburizing and conventional carburizing, which was followed by grinding with a 38A60K8V aloxite grinding wheel and a CBN grinding wheel - RNB80/63B75V. The following cutting fluids were used during the grinding process: oil emulsion 5%, supply rate ca. 20 l/min, Micro5000 oil supplied at the minimum quantity lubrication (MQL of ca. 25 ml/h, dry machining. The study determined the effect of the type of grinding wheel and the cooling and lubricating agent on the distribution of residual stress in the sur-face layer. The best effects of grinding with respect to the residual stress were achieved with flood cooling with oil emulsion and grinding with a CBN grinding wheel.

  9. Mechanically induced residual stresses: Modelling and characterisation

    Science.gov (United States)

    Stranart, Jean-Claude E.

    Accurate characterisation of residual stress represents a major challenge to the engineering community. This is because it is difficult to validate the measurement and the accuracy is doubtful. It is with this in mind that the current research program concerning the characterisation of mechanically induced residual stresses was undertaken. Specifically, the cold expansion of fastener holes and the shot peening treatment of aerospace alloys, aluminium 7075 and titanium Ti-6Al-4V, are considered. The objective of this study is to characterise residual stresses resulting from cold working using three powerful techniques. These are: (i) theoretical using three dimensional non-linear finite element modelling, (ii) semi-destructive using a modified incremental hole drilling technique and (iii) nondestructive using a newly developed guided wave method supplemented by traditional C-scan measurements. The three dimensional finite element results of both simultaneous and sequential cold expansion of two fastener holes revealed the importance of the separation distance, the expansion level and the loading history upon the development and growth of the plastic zone and unloading residual stresses. It further showed that the commonly adopted two dimensional finite element models are inaccurate and incapable of predicting these residual stresses. Similarly, the dynamic elasto-plastic finite element studies of shot peening showed that the depth of the compressed layer, surface and sub-surface residual stresses are significantly influenced by the shot characteristics. Furthermore, the results reveal that the separation distance between two simultaneously impacting shots governs the plastic zone development and its growth. In the semi-destructive incremental hole drilling technique, the accuracy of the newly developed calibration coefficients and measurement techniques were verified with a known stress field and the method was used to measure peening residual stresses. Unlike

  10. Residual stress in polyethylene pipes

    Czech Academy of Sciences Publication Activity Database

    Poduška, Jan; Hutař, Pavel; Kučera, J.; Frank, A.; Sadílek, J.; Pinter, G.; Náhlík, Luboš

    2016-01-01

    Roč. 54, SEP (2016), s. 288-295 ISSN 0142-9418 R&D Projects: GA MŠk LM2015069; GA MŠk(CZ) LQ1601 Institutional support: RVO:68081723 Keywords : polyethylene pipe * residual stress * ring slitting method * lifetime estimation Subject RIV: JL - Materials Fatigue, Friction Mechanics Impact factor: 2.464, year: 2016

  11. Residual Stresses In 3013 Containers

    International Nuclear Information System (INIS)

    Mickalonis, J.; Dunn, K.

    2009-01-01

    The DOE Complex is packaging plutonium-bearing materials for storage and eventual disposition or disposal. The materials are handled according to the DOE-STD-3013 which outlines general requirements for stabilization, packaging and long-term storage. The storage vessels for the plutonium-bearing materials are termed 3013 containers. Stress corrosion cracking has been identified as a potential container degradation mode and this work determined that the residual stresses in the containers are sufficient to support such cracking. Sections of the 3013 outer, inner, and convenience containers, in both the as-fabricated condition and the closure welded condition, were evaluated per ASTM standard G-36. The standard requires exposure to a boiling magnesium chloride solution, which is an aggressive testing solution. Tests in a less aggressive 40% calcium chloride solution were also conducted. These tests were used to reveal the relative stress corrosion cracking susceptibility of the as fabricated 3013 containers. Significant cracking was observed in all containers in areas near welds and transitions in the container diameter. Stress corrosion cracks developed in both the lid and the body of gas tungsten arc welded and laser closure welded containers. The development of stress corrosion cracks in the as-fabricated and in the closure welded container samples demonstrates that the residual stresses in the 3013 containers are sufficient to support stress corrosion cracking if the environmental conditions inside the containers do not preclude the cracking process.

  12. Neutron residual stress measurements in linepipe

    Science.gov (United States)

    Law, Michael; Gnaëpel-Herold, Thomas; Luzin, Vladimir; Bowie, Graham

    2006-11-01

    Residual stresses in gas pipelines are generated by manufacturing and construction processes and may affect the subsequent pipe integrity. In the present work, the residual stresses in eight samples of linepipe were measured by neutron diffraction. Residual stresses changed with some coating processes. This has special implications in understanding and mitigating stress corrosion cracking, a major safety and economic problem in some gas pipelines.

  13. Neutron residual stress measurements in linepipe

    International Nuclear Information System (INIS)

    Law, Michael; Gnaepel-Herold, Thomas; Luzin, Vladimir; Bowie, Graham

    2006-01-01

    Residual stresses in gas pipelines are generated by manufacturing and construction processes and may affect the subsequent pipe integrity. In the present work, the residual stresses in eight samples of linepipe were measured by neutron diffraction. Residual stresses changed with some coating processes. This has special implications in understanding and mitigating stress corrosion cracking, a major safety and economic problem in some gas pipelines

  14. Residual stress measurement by neutron diffraction

    International Nuclear Information System (INIS)

    Akita, Koichi; Suzuki, Hiroshi

    2010-01-01

    Neutron diffraction method has great advantages, allowing us to determine the residual stress deep present within the bulk materials and components nondestructively. Therefore, the method has been applied to confirm the structural integrity of the actual mechanical components and structures and to improve the manufacturing process and strength reliability of the products. This article reviews the residual stress measurement methodology of neutron diffraction. It also refers to the appropriate treatments of diffraction plane, stress-free lattice spacing, coarse grain and surface error to obtain reliable results. Finally, a few applications are introduced to show the capabilities of the neutron stress measurement method for the studies on the strength and elasto-plastic behaviors of crystalline materials. (author)

  15. Residual stresses analysis by X-ray and neutrons diffraction

    International Nuclear Information System (INIS)

    Lodini, A.; Perrin, M.

    1996-04-01

    This conference is composed of 17 papers grouped in 13 chapters which main themes are: advantages of neutrons and synchrotron radiation for material characterization; residual stress evaluation from micro-deformation measurements in polycrystalline materials; X-ray and neutron diffractometry; residual stress evaluation by X-ray diffraction in extreme surfaces; residual stress diffraction evaluation in monocrystalline nickel base alloys, in polyphasic materials, composite materials, thin films, multilayers and joints; application to thermonuclear reactor components

  16. Effect of applied stress on the compressive residual stress introduced by laser peening

    International Nuclear Information System (INIS)

    Sumiya, Rie; Tazawa, Toshiyuki; Narazaki, Chihiro; Saito, Toshiyuki; Kishimoto, Kikuo

    2016-01-01

    Peening is the process which is able to be generated compressive residual stress and is known to be effective for preventing SCC initiation and improvement of fatigue strength. Laser peening is used for the nuclear power plant components in order to prevent SCC initiation. Although it is reported that the compressive residual stress decreases due to applied stresses under general operating condition, the change of residual stress might be large under excessive loading such as an earthquake. The objectives of this study are to evaluate the relaxation behavior of the compressive residual stress due to laser peening and to confirm the surface residual stress after loading. Therefore laser peened round bar test specimens of SUS316L which is used for the reactor internals of nuclear power plant were loaded at room temperature and elevated temperature and then surface residual stresses were measured by X-ray diffraction method. In the results of this test, it was confirmed that the compressive residual stress remained after applying uniform stress larger than 0.2% proof stress, and the effect of cyclic loading on the residual stress was small. The effect of applying compressive stress on the residual stress relaxation was confirmed to be less than that of applying tensile stress. Plastic deformation through a whole cross section causes the change in the residual stress distribution. As a result, the surface compressive residual stress is released. It was shown that the effect of specimen size on residual stress relaxation and the residual stress relaxation behavior in the stress concentration region can be explained by assumed stress relaxation mechanism. (author)

  17. Residual stress in ceramics and ceramic composites

    International Nuclear Information System (INIS)

    Oden, M.

    1992-01-01

    Residual stresses in Si 3 N 4 and SiC have been measured with X-ray diffraction after grinding and thermal shock. The produced surface stresses are compressive after both treatments. The stresses show a strong dependence on the quenching temperature up to a certain temperature when cracks relax the stresses. The influence of the amount of reinforcing phase on the residual stress state in a Al 2 O 3 /SiC whisker composite was investigated and correlated to a modified Eshelby model. The agreement is excellent. The composite was quenched in liquid He (4K) and the stress state measured after show no relaxation of stresses, indicating elastic behaviour. An in situ strain measurement as a function of temperature conducted on a Al 2 O 3 /SiC whisker composite and a SiC/TiB 2 particle composite show very good agreement with the Eshelby model for the Al 2 O 3 /SiC system but not agreement for the SiC/TiB 2 system. The reason is believed to be stress relaxation during sample preparation. (au) (53 refs., 24 figs., 14 tabs.)

  18. Residual stress measurements of welded stainless steel 304 plate using the HANARO residual stress instrument

    International Nuclear Information System (INIS)

    Mun, M. K.; Lee, C. H.; Em, V. T.

    2001-01-01

    In order to nondestructively measure in-depth residual stress distribution of the metallic materials, it is unique method to use neutron diffraction. In this paper the principles of residual stress measurements by neutron diffraction is described. The residual stress distribution of welded strainless steeel 304 plate using te HANARO residual stress instrument is also described

  19. Residual Stresses and Other Properties of Teardrops

    Energy Technology Data Exchange (ETDEWEB)

    Stroud, Mary Ann [Los Alamos National Lab. (LANL), Los Alamos, NM (United States); Veirs, Douglas Kirk [Los Alamos National Lab. (LANL), Los Alamos, NM (United States); Berg, John M. [Los Alamos National Lab. (LANL), Los Alamos, NM (United States); Hill, Mary Ann [Los Alamos National Lab. (LANL), Los Alamos, NM (United States); Rios, Daniel [Los Alamos National Lab. (LANL), Los Alamos, NM (United States); Duque, Juan [Los Alamos National Lab. (LANL), Los Alamos, NM (United States)

    2017-07-26

    The Department of Energy’s 3013 Standard for packaging plutonium-bearing materials for storage up to fifty years specifies a minimum of two individually welded, nested containers herein referred to as the 3013 outer and the 3013 inner.1 Stress corrosion cracking (SCC) is a potential failure mechanism for 3013 inner containers.2,3 The bagless transfer container (BTC), a 3013 inner container used by Hanford and Savanna River Site (SRS) made from 304L stainless steel (SS), poses the greatest concern for SCC.4,5 The Surveillance and Monitoring Program (SMP) use stressed metal samples known as teardrops as screening tools in SCC studies to evaluate factors that could result in cracks in the 3013 containers.6,7 This report provides background information on the teardrops used in the Los Alamos National Laboratory (LANL) SMP studies including method of construction, composition and variability. In addition, the report discusses measurements of residual stresses in teardrops and compares the results with residual stresses in BTCs reported previously.4 Factors affecting residual stresses, including teardrop dimensions and surface finish, are also discussed.

  20. Residual stresses in a surface remelting of castings made of cobalt alloy MAR-M509 with a plasma generated in electric arc

    Directory of Open Access Journals (Sweden)

    Z. Opiekun

    2010-01-01

    Full Text Available The manuscript presents the results of measurements of residual stresses (RS in partial meltings of casting surfaces made of cobalt alloy MAR-M509. The partial meltings were made with an argon plasma beam by GTAW method. The values of RS were deter-mined by X-ray diffraction method in grazing incident geometry, by g-sin2ψ method and in Bragg-Brentano (BB geometry. It has been stated that RS values depend on the parameters of partial melting process. It has been claimed that compressive stresses, which are present in the thin layer up to ca 2 μm, convert to tensile stresses in deeper layers of partial meltings.

  1. Residual stresses in zircaloy welds

    International Nuclear Information System (INIS)

    Santisteban, J. R.; Fernandez, L; Vizcaino, P.; Banchik, A.D.; Samper, R; Martinez, R. L; Almer, J; Motta, A.T.; Colas, K.B; Kerr, M.; Daymond, M.R

    2009-01-01

    Welds in Zirconium-based alloys are susceptible to hydrogen embrittlement, as H enters the material due to dissociation of water. The yield strain for hydride cracking has a complex dependence on H concentration, stress state and texture. The large thermal gradients produced by the applied heat; drastically changes the texture of the material in the heat affected zone, enhancing the susceptibility to delayed hydride cracking. Normally hydrides tend to form as platelets that are parallel to the normal direction, but when welding plates, hydride platelets may form on cooling with their planes parallel to the weld and through the thickness of the plates. If, in addition to this there are significant tensile stresses, the susceptibility of the heat affected zone to delayed hydride cracking will be increased. Here we have measured the macroscopic and microscopic residual stressed that appear after PLASMA welding of two 6mm thick Zircaloy-4 plates. The measurements were based on neutron and synchrotron diffraction experiments performed at the Isis Facility, UK, and at Advanced Photon Source, USA, respectively. The experiments allowed assessing the effect of a post-weld heat treatment consisting of a steady increase in temperature from room temperature to 450oC over a period of 4.5 hours; followed by cooling with an equivalent cooling rate. Peak tensile stresses of (175± 10) MPa along the longitudinal direction were found in the as-welded specimen, which were moderately reduced to (150±10) MPa after the heat-treatment. The parent material showed intergranular stresses of (56±4) MPa, which disappeared on entering the heat-affected zone. In-situ experiments during themal cyclong of the material showed that these intergranular stresses result from the anisotropy of the thermal expansion coefficient of the hexagonal crystal lattice. [es

  2. Residual stress studies of austenitic and ferritic steels

    International Nuclear Information System (INIS)

    Chrenko, R.M.

    1978-01-01

    Residual studies have been made on austenitic and ferritic steels of the types used as structural materials. The residual stress results presented here will include residual stress measurements in the heat-affected zone on butt welded Type 304 stainless steel pipes, and the stresses induced in Type 304 austenitic stainless steel and Type A508 ferritic steel by several surface preparations. Such surface preparation procedures as machining and grinding can induce large directionality effects in the residual stresses determined by X-ray techniques and some typical data will be presented. A brief description is given of the mobile X-ray residual stress apparatus used to obtain most of the data in these studies. (author)

  3. Measurement of residual stresses in alloy 600 pressurizer penetrations

    International Nuclear Information System (INIS)

    Hall, J.F.; Molkenthin, J.P.; Prevey, P.S.; Pathania, R.S.

    1994-01-01

    Alloy 600 penetrations in several pressurized water reactors have experienced primary water stress corrosion cracking near the partial penetration J-welds between the Alloy 600 and the cladding on the inside diameter of the components. The microstructure and tensile properties indicated that the Alloy 600 was susceptible to primary water stress corrosion cracking (PWSCC) providing that a high tensile stress (applied + residual) was present. The residual stress distributions at the inside diameter surface and at different depths below the surface were measured in Alloy 600 nozzle and heater sleeve mockups. Surface residual stresses on the nozzle mockup ranged from -350 to +830 MPa. For the heater sleeve mockup, the surface residual stresses ranged from -330 to +525 MPa. In the areas of high tensile residual stress, for the most part, the residual stresses decreased with increasing depth below the surface. For the nozzle and heater sleeve mockups, the percent cold-world and yield strength as a function of depth were determined. (authors). 12 figs., 4 refs

  4. Significance of residual stress on fatigue properties of welded pipes

    International Nuclear Information System (INIS)

    Ohta, A.; Maeda, Y.; Kanao, M.

    1984-01-01

    The mean stress effect on the fatigue properties of two kinds of welded pipes was investigated in cantilever bending. The fatigue strength changed with the mean stress on fillet welded pipes, but did not change on butt welded pipes. The fatigue crack initiated from the toe of weld on the outer surface of fillet welded pipes and from the undercut on the inner surface of butt welded pipes. The measurement of the fatigue crack propagation rate and the residual stress distribution through the thickness of pipe revealed that the difference in the fatigue properties between fillet and butt welded pipes arose from the weld-induced residual stress, tension on the inner surface and compression on the outer surface. It is suggested that the production of compressive residual stress along the inner surface would be an effective means for improving the fatigue strength of butt welded pipes. (author)

  5. Measured residual stresses in overlay pipe weldments removed from service

    International Nuclear Information System (INIS)

    Shack, W.J.

    1985-02-01

    Surface and throughwall residual stresses were measured on an elbow-to-pipe weldment that had been removed from the Hatch-2 reactor about a year after the application of a weld overlay. The results were compared with experimental measurements on three mock-up weldments and with finite-element calculations. The comparison shows that there are significant differences in the form and magnitude of the residual stress distributions. However, even after more than a year of service, the residual stresses over most of the inner surface of the actual plant weldment with an overlay were strongly compressive. 3 refs., 7 figs

  6. Effect of residual stresses on hydrogen permeation in iron

    International Nuclear Information System (INIS)

    Mouanga, M.; Bercot, P.; Takadoum, J.

    2010-01-01

    The effect of residual stresses on electrochemical permeation in iron membrane was investigated. Four thermal and mechanical treatments were chosen to obtain different surface states in relation to the residual stresses. Residual stresses were determined by X-ray diffraction (XRD) using the Macherauch and Mueller method. The results were completed by the microhardness measurements. For all iron membranes, compressive residual stresses were obtained. Electrochemical permeation experiments using a Devanathan and Stachurski cell were employed to determine the hydrogen permeation behaviour of the various iron membranes. The latter was charged with hydrogen by galvanostatic cathodic polarization in 0.1 M NaOH at 25 deg. C. The experimental results revealed that hydrogen permeation rate increases with increasing residual stresses introduced in iron membranes.

  7. Residual stresses in steel and zirconium weldments

    International Nuclear Information System (INIS)

    Root, J.H.; Coleman, C.E.; Bowden, J.W.

    1997-01-01

    Three-dimensional scans of residual stress within intact weldments provide insight into the consequences of various welding techniques and stress-relieving procedures. The neutron diffraction method for nondestructive evaluation of residual stresses has been applied to a circumferential weld in a ferritic steel pipe of outer diameter 114 mm and thickness 8.6 mm. The maximum tensile stresses, 250 MPa in the hoop direction, are found at mid-thickness of the fusion zone. The residual stresses approach zero within 20 mm from the weld center. The residual stresses caused by welding zirconium alloy components are partially to blame for failures due to delayed-hydride cracking. Neutron diffraction measurements in a GTA-welded Zr-2.5 Nb plate have shown that heat treatment at 530 C for 1 h reduces the longitudinal residual strain by 60%. Neutron diffraction has also been used to scan the residual stresses near circumferential electron beam welds in irradiated and unirradiated Zr-2.5 Nb pressure tubes. The residual stresses due to electron beam welding appear to be lower than 130 MPa, even in the as-welded state. No significant changes occur in the residual stress pattern of the electron-beam welded tube, during a prolonged exposure to thermal neutrons and the temperatures typical of an operating nuclear reactor

  8. The measurement of residual stresses in claddings

    International Nuclear Information System (INIS)

    Hofer, G.; Bender, N.

    1978-01-01

    The ring core method, a variation of the hole drilling method for the measurement of biaxial residual stresses, has been extended to measure stresses from depths of about 5 to 25mm. It is now possible to measure the stress profiles of clad material. Examples of measured stress profiles are shown and compared with those obtained with a sectioning technique. (author)

  9. Residual thermal stresses in injection moulded products

    NARCIS (Netherlands)

    Zoetelief, W.F.; Douven, L.F.A.; Ingen Housz, A.J.; Ingen housz, A.J.

    1996-01-01

    Nonisothermal flow of a polymer melt in a cold mold cavity introduces stresses that are partly frozen-in during solidification. Flow-induced stresses cause anisotropy of mechanical, thermal, and optical properties, while the residual thermal stresses induce warpage and stress-cracking. In this

  10. Residual stress measurement for injection molded components

    Directory of Open Access Journals (Sweden)

    Achyut Adhikari

    2016-07-01

    Full Text Available Residual stress induced during manufacturing of injection molded components such as polymethyl methacrylate (PMMA affects the mechanical and optical properties of these components. These residual stresses can be visualized and quantified by measuring their birefringence. In this paper, a low birefringence polariscope (LBP is used to measure the whole-field residual stress distribution of these injection molded specimens. Detailed analytical and experimental study is conducted to quantify the residual stress measurement in these materials. A commercial birefringence measurement system was used to validate the results obtained to our measurement system. This study can help in material diagnosis for quality and manufacturing purpose and be useful for understanding of residual stress in imaging or other applications.

  11. Neutron diffraction measurement of residual stress in NPP construction materials

    International Nuclear Information System (INIS)

    Hinca, R.; Bokuchava, G.

    2000-01-01

    The aim of the investigation is to study the level of residual stresses induced by the surfacing in the weld deposit zone and in the base metal, where considerable thermal gradients are present. Surfacing high-nickel filler on an austenitic base metal is one of techniques in repair of primary collector the primary circuit of nuclear power plant type VVER. The repair technology was developed at Welding Research Institute Bratislava. Measurements of residual stresses in the weld overlay and the base metal are necessary for approving the mechanical analysis and verifying of residual stresses determination on welded material by numerical weld g computer simulation. Investigations of residual stresses are important for developing optimal welding techniques. (authors)

  12. Evaluation Of Residual Stresses In Inner Ring Of The Bearings

    Science.gov (United States)

    Malotová, Šárka; Hemžský, Pavel; Pitela, David; Nicielnik, Henryk; Šoková, Dagmar; Kyncl, Ladislav; Mrázik, Jozef

    2015-12-01

    Residual stresses are undesirable and it should not be underestimated. They occur in many components and it is necessary to identify and try to avoid them. For detection the Residual stresses, there are many methods, but not all are suitable, because they can completely destroy of the components. The article deals with the evaluation of Residual stresses in the inner rings of Bearings, which are made from steel 100Cr6 (ČSN 14 109.4. The surfaces were turning at different cutting parameters and subsequently are evaluated Residual stresses. The stresses have been evaluated by non - destructive method X - Ray. The experiment was realized in cooperation Faculty of Mechanical Engineering VSB - TU Ostrava and Faculty of Mechanical Engineering of ZU Zilina - machining in the laboratories of ZU Žilina, Slovak Republic.

  13. Prediction of machining induced residual stresses

    Science.gov (United States)

    Pramod, Monangi; Reddy, Yarkareddy Gopi; Prakash Marimuthu, K.

    2017-07-01

    Whenever a component is machined, residual stresses are induced in it. These residual stresses induced in the component reduce its fatigue life, corrosion resistance and wear resistance. Thus it is important to predict and control the machining-induced residual stress. A lot of research is being carried out in this area in the past decade. This paper aims at prediction of residual stresses during machining of Ti-6Al-4V. A model was developed and under various combinations of cutting conditions such as, speed, feed and depth of cut, the behavior of residual stresses were simulated using Finite Element Model. The present work deals with the development of thermo-mechanical model to predict the machining induced residual stresses in Titanium alloy. The simulation results are compared with the published results. The results are in good agreement with the published results. Future work involves optimization or the cutting parameters that effect the machining induced residual stresses. The results obtained were validated with previous work.

  14. Residual stress field of ballised holes

    International Nuclear Information System (INIS)

    Lai, Man On; He, Zhimin

    2012-01-01

    Ballising, involving pushing a slightly over-sized ball made of hard material through a hole, is a kind of cold working process. Applying ballising process to fastener holes produces compressive residual stress on the edge of the holes, and therefore increases the fatigue life of the components or structures. Quantification of the residual stress field is critical to define and precede the ballising process. In this article, the ballised holes are modeled as cold-expanded holes. Elastic-perfectly plastic theory is employed to analyze the holes with cold expansion process. For theoretical simplification, an axially symmetrical thin plate with a cold expanded hole is assumed. The elasticplastic boundaries and residual stress distribution surrounding the cold expanded hole are derived. With the analysis, the residual stress field can be obtained together with actual cold expansion process in which only the diameters of hole before and after cold expansion need to be measured. As it is a non-destructive method, it provides a convenient way to estimate the elastic-plastic boundaries and residual stresses of cold worked holes. The approach is later extended to the case involving two cold-worked holes. A ballised hole is looked upon as a cold expanded hole and therefore is investigated by the approach. Specimens ballised with different interference levels are investigated. The effects of interference levels and specimen size on residual stresses are studied. The overall residual stresses of plates with two ballised holes are obtained by superposing the residual stresses induced on a single ballised hole. The effects of distance between the centers of the two holes with different interference levels on the residual stress field are revealed

  15. Development of residual stress prediction model in pipe weldment

    Energy Technology Data Exchange (ETDEWEB)

    Eom, Yun Yong; Lim, Se Young; Choi, Kang Hyeuk; Cho, Young Sam; Lim, Jae Hyuk [Korea Advanced Institute of Science and Technology, Taejon (Korea, Republic of)

    2002-03-15

    When Leak Before Break(LBB) concepts is applied to high energy piping of nuclear power plants, residual weld stresses is a important variable. The main purpose of his research is to develop the numerical model which can predict residual weld stresses. Firstly, basic theories were described which need to numerical analysis of welding parts. Before the analysis of pipe, welding of a flat plate was analyzed and compared. Appling the data of used pipes, thermal/mechanical analysis were accomplished and computed temperature gradient and residual stress distribution. For thermal analysis, proper heat flux was regarded as the heat source and convection/radiation heat transfer were considered at surfaces. The residual stresses were counted from the computed temperature gradient and they were compared and verified with a result of another research.

  16. Residual stress in Ni-W electrodeposits

    DEFF Research Database (Denmark)

    Mizushima, Io; Tang, Peter Torben; Hansen, Hans Nørgaard

    2006-01-01

    In the present work, the residual stress in Ni–W layers electrodeposited from electrolytes based on NiSO4 and Na2WO4, is investigated. Citrate, glycine and triethanolamine were used as complexing agents, enabling complex formation between the nickel ion and tungstate. The results show that the type...... of complexing agent and the current efficiency have an influence on the residual stress. In all cases, an increase in tensile stress in the deposit with time after deposition was observed. Pulse plating could improve the stress level for the electrolyte containing equal amounts of citrate...

  17. Measuring depth profiles of residual stress with Raman spectroscopy

    Energy Technology Data Exchange (ETDEWEB)

    Enloe, W.S.; Sparks, R.G.; Paesler, M.A.

    1988-12-01

    Knowledge of the variation of residual stress is a very important factor in understanding the properties of machined surfaces. The nature of the residual stress can determine a part`s susceptibility to wear deformation, and cracking. Raman spectroscopy is known to be a very useful technique for measuring residual stress in many materials. These measurements are routinely made with a lateral resolution of 1{mu}m and an accuracy of 0.1 kbar. The variation of stress with depth; however, has not received much attention in the past. A novel technique has been developed that allows quantitative measurement of the variation of the residual stress with depth with an accuracy of 10nm in the z direction. Qualitative techniques for determining whether the stress is varying with depth are presented. It is also demonstrated that when the stress is changing over the volume sampled, errors can be introduced if the variation of the stress with depth is ignored. Computer aided data analysis is used to determine the depth dependence of the residual stress.

  18. Residual-stress distributions near stainless steel butt weldments

    International Nuclear Information System (INIS)

    Elligson, W.A.; Shack, W.J.

    1978-01-01

    Concern for the integrity of stainless steel butt-weldments in boiling-water-reactor (BWR) piping systems has stimulated study of the conditions that cause stress corrosion cracking (SCC) in the heat-affected zones (HAZ) of the weldments. It is generally agreed that a high stress exceeding the initial yield strength is one of the essential elements for crack initiation. Since design procedures usually ensure that load stresses are below initial yield, the source of the high stresses necessary to produce SCC is thought to be the residual stresses due to welding. To examine the level of residual stresses in the weldments of interest, bulk residual stresses were measured on 100 mm (4-in.) and 254 mm (10-in.) diameter Schedule 80 piping weldments using strain relief techniques. Both laboratory welded specimens and field welded specimens from reactors in service were studied. Axial bulk residual stress distributions were obtained at 45 0 intervals around the circumference. At each azimuthal position, the residual stresses were measured at seven axial positions: on the weld centerline and 13, 20, and 25 mm on either side of the weld centerline on both the inside and outside surfaces

  19. Neutron diffraction residual strain / stress measurements

    International Nuclear Information System (INIS)

    Paradowska, Anna

    2012-01-01

    Residual stresses affect mechancial properties of materials and prodcuts, it is essential to estimate them practically in order to esatblish acceptable limits. Knowledge of the development of residual stresses in components at the various production stages- extrusion, rolling, machining, welding and heat treating-can be used to imporve product reliability and performance. This short article gives an example relevant to the power industry using ANSTO's 'Kowari' neutron strain scanner.

  20. Residual stress measurement at Budapest Neutron Center

    International Nuclear Information System (INIS)

    Gyula, T.

    2005-01-01

    The use of residual stress measurements of different construction element and recent possibilities of Budapest Neutron Centre are presented. The details investigated already: gas turbine wheel, axial compressor blade, turbine blade and plastically deformed stainless steel. We demonstrated the use of a neutron scattering (SANS, residual stress, diffraction) for the materials behavior investigation in order to analyze the processes going on under the different mechanical loading. The direction of possible instrumental development is presented. (author)

  1. Residual Stresses in Thermoplastic Composites: A Review

    Directory of Open Access Journals (Sweden)

    M.M. Shokrieh

    2008-12-01

    Full Text Available Applications of thermoplastic composites have developed extensively. The thermoplastic composites in comparison with the thermoset composites have many advantages. Thermoplastic composites can be melted and remolded many times. The duration of manufacturing process of these composites is short, producing very tough material, and the welding ability and multiple recyclings are their further advantages. The lack of knowledge in this group of composites is the main obstacle in their development. In this review the research works in the field of residual stresses in thermoplastic composites is presented. First, a literature survey on the available research on residual stresses on thermoplastics and thermoplastic composites reinforced with short fibers is compiled. Moreover a review on the available research on residual stresses on thermoplastic composites reinforced with long fibers is presented as well. The effects of the residual stresses on these composites are discussed. Experimental techniques for the measurement of residual stresses in thermoplastic composites and the methods for reducing the existing residual stresses are studied.

  2. Residual stresses in cold drawn ferritic rods

    International Nuclear Information System (INIS)

    Atienza, J.M.; Martinez-Perez, M.L.; Ruiz-Hervias, J.; Mompean, F.; Garcia-Hernandez, M.; Elices, M.

    2005-01-01

    The residual stress state generated by cold-drawing in a ferritic steel rod has been determined. Stress profiles in the three principal directions were measured by neutron and X-ray diffraction and calculated by 3D finite element simulation. The agreement between the simulations and the experimental data is excellent

  3. Residual stresses evaluation in a gas-pipeline crossing

    Energy Technology Data Exchange (ETDEWEB)

    Fonseca, Maria Cindra [Universidade Federal Fluminense (UFF), Niteroi, RJ (Brazil); Almeida, Manoel Messias [COMPAGAS, Curitiba, PR (Brazil); Rebello, Joao Marcos Alcoforado [Universidade Federal do Rio de Janeiro (UFRJ), RJ (Brazil); Souza Filho, Byron Goncalves de [PETROBRAS, Rio de Janeiro, RJ (Brazil)

    2009-07-01

    The X-rays diffraction technique is a well established and effectiveness method in the determination of the residual and applied stresses in fine grained crystalline materials. It allows to characterize and to quantify the magnitude and direction of the existing surface stresses in the studied point of the material. The objective of this work is the evaluation of the surface stresses in a 10 in diameter Natural Gas Distribution Pipeline manufactured from API 5 L Gr B steel of COMPAGAS company, in a crossing with a Natural Gas Transportation Pipeline, in Araucaria-PR. This kind of evaluation is important to establish weather you have to perform a repositioning of one of the pipeline or not. The measurements had been made in two transversal sections of the pipe, the one upstream (170 mm of the external wall of the pipeline) and another one downstream (840 mm of the external wall of the pipeline). Each transversal section measurements where carried out in 3 points: 9 hours, 12 hours and 3 hours. In each measured point of the pipe surface, the longitudinal and transversal stresses had been measured. The magnitude of the surface residual stresses in the pipe varied of +180 MPa at the -210 MPa. The residual stress state on the surface of the points 12 hours region is characterized by tensile stresses and by compressive stresses in the points of 3 and 9 hours region. The surface residual stresses in gas-pipeline have been measured using X-ray diffraction method, by double exposure technique, using a portable apparatus, with Cr-K-alpha radiation. (author)

  4. Effect of Plastic Pre-straining on Residual Stress and Composition Profiles in Low-Temperature Surface-Hardened Austenitic Stainless Steel

    DEFF Research Database (Denmark)

    Bottoli, Federico; Christiansen, Thomas Lundin; Winther, Grethe

    2016-01-01

    The present work deals with the evaluation of the residual stress profiles in expanded austenite by applying grazing incidence X-ray diffraction (GI-XRD) combined with successive sublayer removal. Annealed and deformed (εeq=0.5) samples of stable stainless steel EN 1.4369 were nitrided...

  5. Possible standard specimens for neutron diffraction residual stress measurements

    International Nuclear Information System (INIS)

    Brand, P.C.; Prask, H.J.; Fields, R.J.; Blackburn, J.; Proctor, T.M.

    1995-01-01

    Increasingly, sub-surface residual stress measurements by means of neutron diffraction are being conducted at various laboratories around the world. Unlike X-ray diffraction residual stress measurement setups, neutron instruments in use worldwide vary widely in design, neutron flux, and level of dedication towards residual stress measurements. Although confidence in the neutron technique has increased within the materials science and engineering communities, no demonstration of standardization or consistency between laboratories has been made. One of the steps in the direction of such standardization is the development of standard specimens, that have well characterized residual stress states and which could be examined worldwide. In this paper the authors will examine two options for a neutron stress standard specimen: (1) a steel ring-plug specimen with very well defined diametrical interference; (2) a spot weld in a High Strength Low Alloy steel disk. The results of neutron residual stress measurements on these specimens will be discussed and conclusions as to their usefulness as neutron stress standards will be presented

  6. Analysis of changes in hardness of a metal surface layer in areas of high stress and methods of determining residual life of parts for mining machines

    Science.gov (United States)

    Zvonarev, I. E.; Ivanov, S. L.

    2016-02-01

    The methodological bases for determining the energy resource of mechanical transmissions details for mining machines are considered. Based on the analysis of the accumulation of damage in metal gears, a method of estimating residual life of coarse-toothed wheels by periodically measuring the hardness of the surface layer of the teeth is justified. The regularities in change of hardness of coarse-tooth gear, conditioned by a change in metal strength properties that take into account the micro- and macromechanisms of plastic and elastic deformation, distortion of the metal crystal lattice with formation and movement of vacancies and dislocations. Experimental setup was built and the results of laboratory experiments are given related to the process of destruction of non-standard samples under different loads. Comparison of dimensions and hardness values of the sample allows concluding that a larger deformation corresponds to a greater increase in hardness, their limit value for the material being in the fracture zone. It is established that the detected changes in the local hardness occurs in areas of increased stresses above the limit of proportionality and the work of fracture forces attributed to dislocations density adjacent to the fracture plane expressed in terms of hardness increment is constant.

  7. Methods of measuring residual stresses in components

    International Nuclear Information System (INIS)

    Rossini, N.S.; Dassisti, M.; Benyounis, K.Y.; Olabi, A.G.

    2012-01-01

    Highlights: ► Defining the different methods of measuring residual stresses in manufactured components. ► Comprehensive study on the hole drilling, neutron diffraction and other techniques. ► Evaluating advantage and disadvantage of each method. ► Advising the reader with the appropriate method to use. -- Abstract: Residual stresses occur in many manufactured structures and components. Large number of investigations have been carried out to study this phenomenon and its effect on the mechanical characteristics of these components. Over the years, different methods have been developed to measure residual stress for different types of components in order to obtain reliable assessment. The various specific methods have evolved over several decades and their practical applications have greatly benefited from the development of complementary technologies, notably in material cutting, full-field deformation measurement techniques, numerical methods and computing power. These complementary technologies have stimulated advances not only in measurement accuracy and reliability, but also in range of application; much greater detail in residual stresses measurement is now available. This paper aims to classify the different residual stresses measurement methods and to provide an overview of some of the recent advances in this area to help researchers on selecting their techniques among destructive, semi destructive and non-destructive techniques depends on their application and the availabilities of those techniques. For each method scope, physical limitation, advantages and disadvantages are summarized. In the end this paper indicates some promising directions for future developments.

  8. Residual stresses of water-jet peened austenitic stainless steel

    International Nuclear Information System (INIS)

    Suzuki, Kenji; Shobu, Takahisa; Shiro, Ayumi

    2013-01-01

    The specimen material was austenitic stainless steel, SUS316L. The residual stress was induced by water-jet peening. The residual stress was measured using the 311 diffraction with conventional X-rays. The measured residual stress showed the equi-biaxial stress state. To investigate thermal stability of the residual stress, the specimen was aged thermally at 773K in air to 1000h. The residual stress kept the equi-biaxial stress state against the thermal aging. Lattice plane dependency of the residual stress induced by water-jet peening was evaluated using hard synchrotron X-rays. The residual stress measured by the soft lattice plane showed the equi-biaxial stress state, but the residual stress measured by the hard lattice plane did not. In addition, the distributions of the residual stress in the depth direction were measured using a strain scanning method with hard synchrotron X-rays and neutrons. (author)

  9. Residual stress analysis of drive shafts after induction hardening

    Energy Technology Data Exchange (ETDEWEB)

    Lemos, Guilherme Vieira Braga; Rocha, Alexandre da Silva; Nunes, Rafael Menezes, E-mail: lemos_gl@yahoo.com.br [Universidade Federal do Rio Grande do Sul (UFRS), Porto Algre, RS (Brazil); Hirsch, Thomas Karl [Stiftung Institut für Werkstofftechnik (IWT), Bremen (Germany)

    2014-08-15

    Typically, for automotive shafts, shape distortion manifests itself in most cases after the induction hardening by an effect known as bending. The distortion results in a boost of costs, especially due to machining parts in the hardened state to fabricate its final tolerances. In the present study, residual stress measurements were carried out on automotive drive shafts made of DIN 38B3 steel. The samples were selected in consequence of their different distortion properties by an industrial manufacturing line. One tested shaft was straightened, because of the considerable dimensional variation and the other one not. Firstly, the residual stress measurements were carried out by using a portable diffractometer, in order to avoid cutting the shafts and evaluate the original state of the stresses, and afterwards a more detailed analysis was realized by a conventional stationary diffractometer. The obtained results presented an overview of the surface residual stress profiles after induction hardening and displayed the influence of the straightening process on the redistribution of residual stresses. They also indicated that the effects of the straightening in the residual stresses cannot be neglected. (author)

  10. Reduction method for residual stress of welded joint using random vibration

    International Nuclear Information System (INIS)

    Aoki, Shigeru; Nishimura, Tadashi; Hiroi, Tetsumaro

    2005-01-01

    Welded joints are used for construction of many structures. Residual stress is induced near the bead caused by locally given heat. Tensile residual stress on the surface may reduce fatigue strength. In this paper, a new method for reduction of residual stress using vibration during welding is proposed. As vibrational load, random vibration, white noise and filtered white noise are used. Two thin plates are butt-welded. Residual stress is measured with a paralleled beam X-ray diffractometer with scintillation counter after removing quenched scale chemically. It is concluded that tensile residual stress near the bead is reduced by using random vibration during welding

  11. Research on measurement of residual stresses of hemispherical lithium hydride by blind-hole method

    Energy Technology Data Exchange (ETDEWEB)

    Bo, Lin, E-mail: linbo@caep.cn [China Academy of Engineering Physics, P.O. Box: 919-71, Mianyang 621900, Sichuan (China); Kaihui, He [China International Nuclear Fusion Energy Program Execution Center, 15B, Fuxing Rd, 100862 Beijing (China); Dongwei, Shan; Weicai, Yang; Yonggang, Chi; Mei, Liu; Jun, Shen [China Academy of Engineering Physics, P.O. Box: 919-71, Mianyang 621900, Sichuan (China)

    2014-04-15

    Highlights: • The residual stresses of sintered and machined lithium hydride of SR40 hyper-hemispherical and SR30 inner hemispherical sample were measured by blind-hole method. • The nearly 45 degrees direction residual stresses of SR40 hyper-hemisphere and SR30 inner hemisphere are the greatest stresses on spherical surface of lithium hydride samples. • The radial residual stress σ{sub r} of SR40 hyper-hemispherical and SR30 inner hemispherical sample is compressive stress and the circumferential residual stress σ{sub t} is tensile stress. - Abstract: The released strains of sintered and machined lithium hydride of SR40 hyper-hemispherical and SR30 inner hemispherical sample could be shown in the measuring process by blind-hole method. The residual stresses of lithium hydride sample were calculated with the formulas of residual stress and released strains. The results show that the nearly 45 degrees direction residual stresses of SR40 hyper-hemisphere and SR30 inner hemisphere are the greatest stresses on spherical surface of lithium hydride samples. The radial residual stress σ{sub r} of SR40 hyper-hemispherical and SR30 inner hemispherical sample is compressive stress and the circumferential residual stress σ{sub t} is tensile stress.

  12. Residual stress measurements by means of neutron diffraction

    International Nuclear Information System (INIS)

    Pintschovius, L.; Jung, V.; Macherauch, E.; Voehringer, O.

    1983-01-01

    A new method for the analysis of multiaxial residual stress states is presented, which is based on high resolution neutron diffraction. It is analogous to X-ray stress analysis, but the use of neutrons instead of X-rays allows the analysis of the stress distributions also in the interior of technical components in a non-destructive way. To prove the feasibility of the method, investigations of the loading stress distributions of an aluminium bar subjected to purely elastic bending were performed. Limiting factors due to the volume of the internal probe region and the sample thickness are discussed. Complete neutron residual stress analyses were carried out for a plastically deformed bending bar and a transformation-free water-quenched steel cylinder. The results are in fairly good agreement with theoretical expectations and with X-ray control measurements at the surface of the objects. (Auth.)

  13. Measurement of residual stresses in welded sample of dissimilar materials

    International Nuclear Information System (INIS)

    Mansur, Tanius Rodrigues; Gomes, Paulo de Tarso Vida; Scaldaferri, Denis Henrique Bianchi; Martins, Geraldo Antonio Scoralick; Atanazio Filho, Nelson do Nascimento

    2008-01-01

    The welding of dissimilar metals has several applications in the industry. Especially in the nuclear industry, this joint type, common between carbon steel and stainless steel, it is always reason of analysis and special cares tends in view the need to maintain the integrity of the equipment. Residual stresses are introduced in the material as a result of processes as welding, machining, sanding and polishing that can to produce deformation in the proximities of the surface of the material. Residual compressive stresses can be introduced in the material through the jetting process (bombardment of the surface for small glass spheres, dry sand or steel). That procedure allows a fine subsurface layer to suffer yielding, compressing the superficial layer and reducing the formation of areas of concentration of traction stresses, increasing the resistance of the material to the fatigue. The welding process introduces residual stresses due to the geometry resulting from the fusion of the material welded and of the heterogeneous cooling. Besides the microstructural alteration and chemical composition of the material in the affected area for the heat, introduced by the welding, it is also had the effect of the discontinuity of the passes and the formation of bubbles and emptiness that can contribute to the cracks nucleation, reducing the resistance to the fatigue. In the great majority of the times residual stresses are harmful and there are many documented cases which US these stresses went predominant factors for the failure for fatigue. A particularly dangerous aspect of the residual stresses is that their presence is not usually observed, what usually happens with an applied load to the structure. The knowledge of the surface residual stresses is important to predict the emergence of failure when the component or structure is requested. In nuclear power plants it is common to welding of piping of stainless steels with mouthpieces of carbon steel of pressure vases of

  14. Control of welding residual stress for ensuring integrity against fatigue and stress-corrosion cracking

    International Nuclear Information System (INIS)

    Mochizuki, Masahito

    2007-01-01

    The availability of several techniques for residual stress control is discussed in this paper. The effectiveness of these techniques in protecting from fatigue and stress-corrosion cracking is verified by numerical analysis and actual experiment. In-process control during welding for residual stress reduction is easier to apply than using post-weld treatment. As an example, control of the welding pass sequence for multi-pass welding is applied to cruciform joints and butt-joints with an X-shaped groove. However, residual stress improvement is confirmed for post-weld processes. Water jet peening is useful for obtaining a compressive residual stress on the surface, and the tolerance against both fatigue and stress-corrosion cracking is verified. Because cladding with a corrosion-resistant material is also effective for preventing stress-corrosion cracking from a metallurgical perspective, the residual stress at the interface of the base metal is carefully considered. The residual stress of the base metal near the clad edge is confirmed to be within the tolerance of crack generation. Controlling methods both during and after welding processes are found to be effective for ensuring the integrity of welded components

  15. Nondestructive determination of residual stresses by neutron diffraction

    International Nuclear Information System (INIS)

    Tello, H.; Barrera, E.V.

    1993-01-01

    Nondestructive determination of residual stresses and strains in engineering materials has been limited to analytical models and near-surface measurement techniques such as x-ray diffraction and ultrasonic testing. The use of neutron diffraction for residual stress determination is similar in methodology to x-ray diffraction but provides superior analysis capability because of the lower absorption of neutrons in most materials. Neutron diffraction measurements can be made from sampling depths of several millimeters in most materials as compared to micrometer sampling depth of x-rays. This paper will discuss the principles of neutron diffraction as well as the advantages and limitations of the technique. Specific examples of residual stress measurements using conventional and time-of flight techniques will be provided

  16. Recent advances in residual stress measurement

    International Nuclear Information System (INIS)

    Withers, P.J.; Turski, M.; Edwards, L.; Bouchard, P.J.; Buttle, D.J.

    2008-01-01

    Until recently residual stresses have been included in structural integrity assessments of nuclear pressure vessels and piping in a very primitive manner due to the lack of reliable residual stress measurement or prediction tools. This situation is changing the capabilities of newly emerging destructive (i.e. the contour method) and non-destructive (i.e. magnetic and high-energy synchrotron X-ray strain mapping) residual stress measurement techniques for evaluating ferritic and austenitic pressure vessel components are contrasted against more well-established methods. These new approaches offer the potential for obtaining area maps of residual stress or strain in welded plants, mock-up components or generic test-pieces. The mapped field may be used directly in structural integrity calculations, or indirectly to validate finite element process/structural models on which safety cases for pressurised nuclear systems are founded. These measurement methods are complementary in terms of application to actual plant, cost effectiveness and measurements in thick sections. In each case an exemplar case study is used to illustrate the method and to highlight its particular capabilities

  17. Structure, microstructure and residual stresses in borided steels

    Czech Academy of Sciences Publication Activity Database

    Pala, Z.; Mušálek, Radek; Kyncl, J.; Harcuba, P.; Stráský, J.; Kolařík, K.

    2013-01-01

    Roč. 20, č. 2 (2013), s. 93-95 ISSN 1211-5894. [Struktura 2013 - Kolokvium Krystalografické společnosti. Češkovice (Blansko), 09.09.2013-13.09.2013] Institutional support: RVO:61389021 Keywords : boriding * surface hardening * iron borides * tooth-shaped microstructure * residual stresses Subject RIV: JK - Corrosion ; Surface Treatment of Materials http://www.xray.cz/ms/bul2013-2/s6.pdf

  18. Experimental investigation of residual stress distribution during turning of weak stiffness revolving parts

    Science.gov (United States)

    Jiao, Sicheng; Zhang, Chengyan; Liu, Guancheng; Lu, Jiping; Tang, Shuiyuan

    2017-08-01

    A series of turning experiments have been carried out to study the effect of different cutting speed, feed rate and pre-tightening torque on residual stress distribution during turning of weak stiffness revolving parts. Surface residual stress and the peak residual compressive stress are selected from the typical residual stress distribution profile. The residual stress by turning was measured by X-ray diffraction method. In order to get the distribution of residual stress along depth direction, the specimens need to be etched layer by layer. From this investigation, it can be concluded that it is practicable to control the distribution of residual stress by changing the pre-tightening torque and cutting parameters during turning of weak stiffness revolving parts.

  19. Effect of Ultrasonic Peening and Accelerated Corrosion Exposure on the Residual Stress Distribution in Welded Marine Steel

    Science.gov (United States)

    Ahmad, Bilal; Fitzpatrick, Michael E.

    2015-03-01

    Specimens of DH36 marine steel were prepared with welded attachments. Residual stress measurements were made on the samples as-welded, following an ultrasonic peening treatment, and following accelerated corrosion exposure after ultrasonic peening. Neutron diffraction and the contour method were used for determining the residual stress profiles. The welding introduces tensile near-surface residual stress, approaching the material yield strength, and the ultrasonic peening overlays this with a compressive residual stress. Material removal by corrosion decreases the peak surface compressive stress slightly, by removal of a layer of stressed material, but does not cause significant redistribution of the residual stress profile.

  20. Residual stresses in a weldment of pressure vessel steel

    International Nuclear Information System (INIS)

    Gott, K.E.

    1978-01-01

    A study was made of the distribution of residual stresses around a typical weld from a light water reactor pressure vessel by an X-ray double-exposure camera technique. So that the magnitude, sign, and distribution of the residual stresses were as similar as possible to those found in practice, a wide, full-thickness specimen of A533B Cl 1 steel containing a submerged-arc weld was stress-relief annealed. To obtain a three-dimensional distribution of the stresses the specimen was examined at different levels through the thickness. Following the removal of material by milling, the specimen surface was electropolished to free it from cold work. Corrections have been made to take into account specimen relaxation. To completely define the original stress system it is desirable also to measure the change in curvature on removing a layer of material. Unless this is done assumptions must be made which complicate the calculations unnecessarily. This became apparent after the experimental work was completed. In the centre of the plate the methods of correction which can be used are sensitive to errors in the measurements. The corrected results show that the dominant residual stress is perpendicular to the weld. It is positive at the surfaces and negative in the centre of the plate. The maximum value can reach the yield stress. The residual stresses in the weld metal can locally vary considerably: from 100 to 350N/mm 2 over a distance of 5mm. Such large variations have been found to coincide with the heat-affected zones of the individual weld runs. (author)

  1. Stability of machining induced residual stresses in Inconel 718 under quasi-static loading at room temperature

    International Nuclear Information System (INIS)

    Madariaga, A.; Esnaola, J.A.; Arrazola, P.J.; Ruiz-Hervias, J.; Muñoz, P.; Ostolaza, K.

    2015-01-01

    Tensile residual stresses are very often generated on the surface when machining nickel alloys. In order to determine their influence on the final mechanical behaviour of the component residual stress stability should be considered. In the present work the evolution of surface residual stresses induced by machining in Inconel 718 under static loading at room temperature was studied experimentally and numerically. An Inconel 718 disc was face turned employing industrial working conditions and specimens for tensile tests were extracted from the disc. Surface residual stresses were measured by X-ray diffraction for initial state and after applying different loads over the material's yield stress. Then, a finite element model based on the surface–core approach was fitted to experimental results and the study was extended to analyse the influence of load level, degree of work-hardening and initial surface conditions. For the studied case, initial tensile surface residual stress (776 MPa) became even more tensile when applying loads higher than the material yield stress, but a shift was observed at the highest applied load (1350 MPa) and initial residual stress was relaxed about 170 MPa. This particular behaviour is associated to the modified stress–strain properties of the machined affected surface layer which was strongly work-hardened. Moreover, if the work-hardened properties are not considered in the finite element model results differ substantially from experiments. Surface residual stress stability also depends on the initial surface residual stress, but the degree of work-hardening induced by the machining process must be considered as well. If the difference between the yield stress of the surface and the yield stress of the core is lower than the initial surface residual stress, the surface begins yielding first and consequently the surface residual stress is decreased. In contrast, if the difference between the yield stress of the surface and the

  2. Residual stress evaluation by neutron and synchrotron radiation

    International Nuclear Information System (INIS)

    Lodini, A.

    2000-01-01

    This lecture is dedicated to the residual stress evaluation using neutron and X ray synchrotron radiation. Residual stress evaluation is an important step for the improvement or the performance of materials, the control of the deformation of the components and the understanding of industrial process. In general, residual stress has various origins: mechanical, thermal, thermomechanical or thermochemical. In general, these residual stresses are caused by plastic deformation, or some source of local incompatibilities and are generated by three fundamental physical origins: plastic flow, volume change and thermal dilatation. These incompatibilities are compensated for partly by the elastic deformation that generates some internal stresses. In the solid, these local incompatibilities are caused by crystal defects. The exact origin of a stress is going to depend on the scale of observation. A classification of the residual stresses in three orders, related to the scale on which one considers materials, is proposed. The diffraction method for determination of macrostresses is based on the measurement of interplanar spacing for various direction in a diffraction experiment. Different examples are proposed. Polycrystalline grains or composite have different physical and elastic properties hence the stress for a particular grains or phase differs from the average value (value of macrostress). This difference is defined as the second order stress. The second order stresses occur because of small scale anisotropy or inhomogeneity in the material : for example, due to mismatch in coefficient of thermal expansion, elastic constants or plastic flow. However, the second order stress averaged over all grains or phase is not equal to zero and this average is called the mismatch stress. Using the experimental macro stress it is possible to calculate the mismatch stresses. More recently, this technique of diffraction has also been applied for the determination of microstrain (third

  3. Residual Stress Induced by Nitriding and Nitrocarburizing

    DEFF Research Database (Denmark)

    Somers, Marcel A.J.

    2005-01-01

    The present chapter is devoted to the various mechanisms involved in the buildup and relief of residual stress in nitrided and nitrocarburized cases. The work presented is an overview of model studies on iron and iron-based alloys. Subdivision is made between the compound (or white) layer......, developing at the surfce and consisting of iron-based (carbo)nitrides, and the diffusion zone underneath, consisting of iron and alloying element nitrides dispersed in af ferritic matrix. Microstructural features are related directly to the origins of stress buildup and stres relief....

  4. Residual stress distribution in extruded polypropylene pipes

    Czech Academy of Sciences Publication Activity Database

    Poduška, Jan; Kučera, J.; Hutař, Pavel; Ševčík, Martin; Křivánek, J.; Sadílek, J.; Náhlík, Luboš

    2014-01-01

    Roč. 2014, č. 40 (2014), s. 88-98 ISSN 0142-9418 R&D Projects: GA ČR(CZ) GAP108/12/1560 Institutional support: RVO:68081723 Keywords : polypropylene * extruded polymer pipe * residual stress * curved beam methodology * numerical simulations Subject RIV: JL - Materials Fatigue, Friction Mechanics Impact factor: 2.240, year: 2014 http://www.sciencedirect.com/science/article/pii/S0142941814001809

  5. Measurement of residual stress in a friction welded joint by using neutron diffraction

    International Nuclear Information System (INIS)

    Okido, Shinobu; Morii, Yukio; Hayashi, Makoto; Minakawa, Nobuaki

    2001-01-01

    The mechanism that produces residual stress near the boundary of two metals connected by friction welding was investigated by neutron diffraction. This investigation showed that the residual stress near the boundary of friction welding was compressive (about 300 MPa) at the surface and tensile (about 200 MPa) at the center of the welded specimen. These results indicate that the residual stress was produced by the heat history during cooling after the upsetting process. (author)

  6. Residual stress reduction in the penetration nozzle weld joint by overlay welding

    International Nuclear Information System (INIS)

    Jiang, Wenchun; Luo, Yun; Wang, B.Y.; Tu, S.T.; Gong, J.M.

    2014-01-01

    Highlights: • Residual stress reduction in penetration weld nozzle by overlay welding was studied. • The overlay weld can decrease the residual stress in the weld root. • Long overlay welding is proposed in the actual welding. • Overlay weld to decrease residual stress is more suitable for thin nozzle. - Abstract: Stress corrosion cracking (SCC) in the penetration nozzle weld joint endangers the structural reliability of pressure vessels in nuclear and chemical industries. How to decrease the residual stress is very critical to ensure the structure integrity. In this paper, a new method, which uses overlay welding on the inner surface of nozzle, is proposed to decrease the residual stresses in the penetration joint. Finite element simulation is used to study the change of weld residual stresses before and after overlay welding. It reveals that this method can mainly decrease the residual stress in the weld root. Before overlay welding, large tensile residual stresses are generated in the weld root. After overlay weld, the tensile hoop stress in weld root has been decreased about 45%, and the radial stress has been decreased to compressive stress, which is helpful to decrease the susceptibility to SCC. With the increase of overlay welding length, the residual stress in weld root has been greatly decreased, and thus the long overlay welding is proposed in the actual welding. It also finds that this method is more suitable for thin nozzle rather than thick nozzle

  7. Residual stress measurement in veneering ceramic by hole-drilling.

    Science.gov (United States)

    Mainjot, Amélie K; Schajer, Gary S; Vanheusden, Alain J; Sadoun, Michaël J

    2011-05-01

    Mismatch in thermal expansion properties between veneering ceramic and metallic or high-strength ceramic cores can induce residual stresses and initiate cracks when combined with functional stresses. Knowledge of the stress distribution within the veneering ceramic is a key factor for understanding and predicting chipping failures, which are well-known problems with Yttria-tetragonal-zirconia-polycrystal based fixed partial dentures. The objectives of this study are to develop a method for measuring the stress profile in veneering ceramics and to compare ceramic-fused-to-metal compounds to veneered Yttria-tetragonal-zirconia-polycrystal ceramic. The hole-drilling method, often used for engineering measurements, was adapted for use with veneering ceramic. Because of the high sensitivity needed in comparison with industrial applications, a high sensitivity electrical measurement chain was developed. All samples exhibited the same type of stress vs. depth profile, starting with compressive at the ceramic surface, decreasing with depth and becoming tensile at 0.5-1.0mm from the surface, and then becoming slightly compressive again. The zirconia samples exhibited a stress depth profile of larger magnitude. The hole drilling method was shown be a practical tool for measuring residual stresses in veneering ceramics. Copyright © 2010 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

  8. Residual stress redistribution in shot peened samples subject to mechanical loading

    International Nuclear Information System (INIS)

    Buchanan, Dennis J.; John, Reji

    2014-01-01

    Shot peening is a well-established surface treatment process that imparts large compressive residual stresses onto the surface and at shallow depths to retard initiation and growth of fatigue cracks. The plastic deformation developed during the surface treatment sets up a constraint that retains compressive stresses on the surface balanced by tensile residual stresses in the interior. However, component service histories that produce subsequent plastic deformation may redistribute these residual stresses. In most engineering components, this additional plastic deformation is localized to stress concentration sites such as holes, notches, and fillets. In the case of gross plastic deformation where the entire cross section experiences material yielding the residual stress profile may redistribute, resulting in tensile stresses on the outside surface balanced by compression in the interior. This paper describes a series of experiments combined with models to explain the redistribution in residual stress depth profiles subject to applied stresses producing gross plastic strains in shot peened laboratory specimens. The initial room temperature residual stress and plastic strain profiles provide initial conditions for predictions. Model predictions correlate well with experimental results on shot peened dogbone specimens subject to single cycle and fatigue loading conditions at elevated temperature. Experiments on shot peened notched specimens do not exhibit the same stress redistribution even for larger applied stresses

  9. finite element model for predicting residual stresses in shielded

    African Journals Online (AJOL)

    eobe

    Diffractometer (XRD 6000). From the Finite Element Model Simulation, the transverse residual stress in the x ... Keywords: Residual stress, 3D FEM, Shielded manual metal arc welding, Low Carbon Steel (ASTM A36), X-Ray diffraction, degree of ..... I. ''Residual stress effects on fatigue life of welded structures using LEFM'',.

  10. Residual stresses in U-bending deformations and expansion joints of heat exchanger tubes

    International Nuclear Information System (INIS)

    Kim, Woo Gon; Kim, Sun Jae; Jang, Jin Sung; Kuk, Ii Hiun; Bae, Kang Gug; Kim, Sung Chung

    2000-01-01

    Residual stress induced in U-bending and tube-to-tubesheet joint processes of PWR's rew-1 heat exchanger tube was measured by X-ray method and Hole-Drilling Method(HDM). Compressive residual stresses(-) at the extrados surface were induced in U-bending, and its maximum value reached -319MPa in axial direction at the position of ψ=0 deg. Tensile residual stresses (+) of 0σ zz =45 MPa and σ θθ =25MPa were introduced in the intrados surface at the position of ψ=0 deg. Maximum tensile residual stress of 170 MPa was measured at the flank side at the position of ψ=90 deg, i.e., at apex region. It was observed that higher stress gradient was generated at the irregular transition regions (ITR). The trend of residual stress induced by U-bending process of the tubes was found to be related with the change of ovality. The residual stress induced by the explosive joint method was found to be lower than that by the mechanical roll method. The gradient of residual stress along the expanded tube was highest at the transition region (TR), and the residual stress in circumferential direction was found to be higher than the residual stress in axial direction

  11. X-ray residual stress analysis on machined and tempered HPSN-ceramics

    Energy Technology Data Exchange (ETDEWEB)

    Immelmann, S.; Welle, E.; Reimers, W. [Hahn-Meitner-Institut Berlin GmbH (Germany)

    1997-11-15

    The residual stress state induced by grinding and tempering of hot pressed silicon nitride (HPSN) samples is studied by X-ray diffraction. The results reveal that the residual stress values at the surface of the samples as well as their gradient within the penetration depth of the X-rays depend on the sintering aid and thus, on the glassy phase content of the HPSN. Tempering of the ground HPSN reduces the residual stress values due to microplastic deformation, whereas an oxidation of the glassy phase leads to the formation of compressive residual stresses. (orig.) 35 refs.

  12. Optical residual stress measurement in TFT-LCD panels

    Science.gov (United States)

    Wang, Wei-Chung; Sung, Po-Chi

    2017-06-01

    The residual stress of the glass substrate might be one of causes to produce the non-uniform light distribution defect, i.e. Mura, in thin film transistor-liquid crystal display (TFT-LCD) panels. Glass is a birefringent material with very low birefringence. Furthermore, the thinner and thinner thickness request from the market makes the traditional photoelasticity almost impossible to measure the residual stresses produced in thin glass plates. Recently, a low-level stress measurement method called transmissivity extremities theory of photoelasticity (TEToP) was successfully developed to measure the residual stress in glass plate. Besides, to measure the stress of the glass plate in the TFT-LCD panel whose rear surface may has different kinds of coatings, an advanced reflection photoelasticity was also developed. In this paper, three commercially available glass plates with 0.33mm nominal thickness and three glass circular disks with different coatings were inspected to verify the feasibility of the TEToP and the advanced reflection photoelasticity, respectively.

  13. Influence of Residual Stress on Fatigue Design of AISI 304 Stainless Steel

    Directory of Open Access Journals (Sweden)

    L. Singh

    2011-06-01

    Full Text Available Austenitic stainless steel cannot be hardened by any form of heat treatment, in fact, quenching from 10000C merely softens them. They are usually cold worked to increase the hardness. Shot peening is a cold working process that changes micro-structure as well as residual stress in the surface layer. In the present work, the compressive residual stress and fatigue strength of AISI 304 austenitic stainless steel have been evaluated at various shot peening conditions. The improvement in various mechanical properties such as hardness, damping factors and fatigue strength was noticed. Compressive residual stress induced by shot peening varies with cyclic loading due to relaxation of compressive residual stress field. The consideration of relaxed compressive residual stress field instead of original compressive residual stress field provides reliable fatigue design of components. In this paper, the exact reductions in weight and control of mechanical properties due to shot peening process are discussed.

  14. Study on the residual stress relaxation in girth-welded steel pipes under bending load using diffraction methods

    International Nuclear Information System (INIS)

    Hempel, Nico; Nitschke-Pagel, Thomas; Dilger, Klaus

    2017-01-01

    This research is dedicated to the experimental investigation of the residual stress relaxation in girth-welded pipes due to quasi-static bending loads. Ferritic-pearlitic steel pipes are welded with two passes, resulting in a characteristic residual stress state with high tensile residual stresses at the weld root. Also, four-point bending is applied to generate axial load stress causing changes in the residual stress state. These are determined both on the outer and inner surfaces of the pipes, as well as in the pipe wall, using X-ray and neutron diffraction. Focusing on the effect of tensile load stress, it is revealed that not only the tensile residual stresses are reduced due to exceeding the yield stress, but also the compressive residual stresses for equilibrium reasons. Furthermore, residual stress relaxation occurs both parallel and perpendicular to the applied load stress.

  15. X-ray study of residual stress distribution of ground ceramics

    International Nuclear Information System (INIS)

    Sakaida, Yoshihisa; Tanaka, Keisuke; Ikuhara, Yuichi; Suzuki, Kenzi.

    1997-01-01

    The residual stress distribution of ground ceramics was determined from the eigen strain existing in the ground surface. The eigen strain of ground ceramics was tensile, and exponentially decreased with the distance from the surface. The residual stress distribution is given as a superposition of an exponential function of compression and a linear function. It is found that the actual residual stress distribution can be approximated by a compressive exponential function because the magnitude of tensile residual stress is negligibly small compared to the compressive residual stress. In the experiments, the diffraction angle was measured on ground silicon nitride for a wide range of sin 2 ψ using the glancing incidence X-ray diffraction technique. A strong nonlinearity was found in the 2θ-sin 2 ψ diagram at very high ψ-angles. From the analysis of nonlinearity, the residual stress distribution was determined. The residual stress distribution of silicon nitride coincided with the distribution calculated from the eigen strain distribution. Transmission electron microscopy was used to clarify the origin of generation of the residual stress. Both strain contrasts and microcracks were observed below the ground surface ; straight dislocations were also observed within silicon nitride grains near the ground surface. (author)

  16. Residual Stress Measurements After Proof and Flight: ETP-0403

    Science.gov (United States)

    Webster, Ronald L..

    1997-01-01

    The intent of this testing was to evaluate the residual stresses that occur in and around the attachment details of a case stiffener segment that has been subjected to flight/recovery followed by proof loading. Not measured in this test were stresses relieved at joint disassembly due to out-of-round and interference effects, and those released by cutting the specimens out of the case segment. The test article was lightweight case stiffener segment 1U50715, S/N L023 which was flown in the forward stiffener position on flight SRM 14A and in the aft position on flight SRM24A. Both of these flights were flown with the 3 stiffener ring configuration. Stiffener L023 had a stiffener ring installed only on the aft stub in its first flight, and it had both rings installed on its second flight. No significant post flight damage was found on either flight. Finally, the segment was used on the DM-8 static test motor in the forward position. No stiffener rings were installed. It had only one proof pressurization prior to assignment to its first use, and it was cleaned and proof tested after each flight. Thus, the segment had seen 3 proof tests, two flight pressurizations, and two low intensity water impacts prior to manufacturing for use on DM-8. On DM-8 it received one static firing pressurization in the horizontal configuration. Residual stresses at the surface and in depth were evaluated by both the x-ray diffraction and neutron beam diffraction methods. The x-ray diffraction evaluations were conducted by Technology for Energy Corporation (TEC) at their facilities in Knoxville, TN. The neutron beam evaluations were done by Atomic Energy of Canada Limited (AECL) at the Chalk River Nuclear Laboratories in Ontario. The results showed general agreement with relatively high compressive residual stresses on the surface and moderate to low subsurface tensile residual stresses.

  17. Modelling of the Residual Stress State in a new Type of Residual Stress Specimen

    DEFF Research Database (Denmark)

    Jakobsen, Johnny; Andreasen, Jens Henrik

    2014-01-01

    The paper presents a study on a new type residual stress specimen which is proposed as a simple way to conduct experimental validation for model predictions. A specimen comprising of a steel plate with circular hole embedded into a stack of CSM glass fibre and further infused with an epoxy resin...... forms the experimental case which is analysed. A FE model of the specimen is used for analysing the curing history and the residual stress build up. The model is validated against experimental strain data which are recorded by a Fibre Brag Grating sensor and good agreement has been achieved....

  18. Modelling of the Residual Stress State in a new Type of Residual Stress Specimen

    DEFF Research Database (Denmark)

    Jakobsen, Johnny; Andreasen, Jens Henrik

    2014-01-01

    forms the experimental case which is analysed. A FE model of the specimen is used for analysing the curing history and the residual stress build up. The model is validated against experimental strain data which are recorded by a Fibre Brag Grating sensor and good agreement has been achieved.......The paper presents a study on a new type residual stress specimen which is proposed as a simple way to conduct experimental validation for model predictions. A specimen comprising of a steel plate with circular hole embedded into a stack of CSM glass fibre and further infused with an epoxy resin...

  19. Relaxation behavior of laser-peening residual stress under tensile loading investigated by X-ray and neutron diffraction

    International Nuclear Information System (INIS)

    Akita, Koichi; Suzuki, Hiroshi; Moriai, Atsushi; Hayashi, Kengo; Takeda, Kazuya; Ohya, Shin-ichi; Sano, Yuji

    2014-01-01

    Compressive residual stresses induced by peening techniques improve the strength properties of steels, such as fatigue and stress corrosion cracking. However, the compressive residual stress might be reduced owing to thermal and mechanical loading in-service. In this study, the behavior of surface and internal residual stresses of a laser-peened ferritic steel under quasi-static tensile loading was investigated by X-ray and neutron diffraction. The complementary use of these diffraction techniques provided decisive experimental evidence for elucidating the relaxation process. As the applied tensile stress increases, the inside of the sample yields before the surface yielding at the critical applied stress (the applied stress for the onset of relaxation of the surface residual stress). The internal yielding causes the redistribution of residual stress, resulting in the relaxation of the surface compressive residual stress. Therefore, the relaxation of the surface compressive residual stress under tensile loading starts before the surface yielding. The critical applied stress of peened samples subjected to a tensile loading can be estimated from the von Mises yield criterion with the maximum tensile residual stress inside the sample. The FWHM of X-ray diffraction profile of the sample surface was increased by laser-peening, and it was further increased by further plastic deformation after peening. (author)

  20. Compressive residual stress relaxation in hardened steel during cyclic and static load

    Science.gov (United States)

    Cseh, D.; Mertinger, V.

    2017-05-01

    The benefits of applied compressive residual stress on fatigue properties of materials is a well-known phenomenon, but not well described in all respects. The fatigue life and the fatigue limit could be improved by targeted created compressive residual stress in the surface layers therefore, diversified surface compressing methods are developed and used in the engineering industry. The relaxation of the compressive residual stress state during a cyclic and static load is determinative for the life time of a componenet. Compressive stress relaxation was experimentally determined during the cyclic and static load. The compressive residual stress was induced by shot penning on the surface of stainless steel, micro alloyed high strength steel and hardened steel specimens. The residual stress state was investigated nondestructively by X-ray diffraction method then these specimens were load. After a certain number of cycles the fatigue load was stopped and the residual stress state was recorded again and again until fracture. To investigate the relaxation process during static load a four-point bending bench was used. The compressive residual stress relaxation was correlated to the applied fatigue stress level, the cycle number the quality of alloys.

  1. Comparison of residual stress in martensitic alloys by nondestructive techniques

    International Nuclear Information System (INIS)

    Roy, A.K.; Bandyopadhyay, S.; Suresh, S.B.; Wells, D.

    2006-01-01

    Three martensitic materials, namely Alloys EP-823, HT-9 and 422 were subjected to tensile loading at ambient temperature. The cylindrical specimens tested at different levels of tensile loading were analyzed for characterization of residual stress resulting from plastic deformation corresponding to the applied loads between the yield strength and the ultimate tensile strength. The extent of residual stress developed at these applied stresses was analyzed by nondestructive positron annihilation spectroscopy, activation, and neutron diffraction techniques. The results indicate that the residual stresses characterized by all three techniques exhibited a consistent pattern showing a gradual enhancement in residual stress with increasing applied load

  2. Residual stress delaying phase transformation in Y-TZP bio-restorations

    Science.gov (United States)

    Allahkarami, Masoud; Hanan, Jay C.

    2012-01-01

    Engineering favorable residual stress for the complex geometry of bi-layer porcelain-zirconia crowns potentially prevents crack initiation and improves the mechanical performance and lifetime of the dental restoration. In addition to external load, the stress field depends on initial residual stress before loading. Residual stress is the result of factors such as the thermal expansion mismatch of layers and compliance anisotropy of zirconia grains in the process of sintering and cooling. Stress induced phase transformation in zirconia extensively relaxes the residual stress and changes the stress state. The objective of this study is to investigate the coupling between tetragonal to monoclinic phase transformations and residual stress. Residual stress, on the surface of the sectioned single load to failure crown, at 23 points starting from the pure tetragonal and ending at a fully monoclinic region were measured using the micro X-ray diffraction sin2 ψ method. An important observation is the significant range in measured residual stress from a compressive stress of -400 MPa up to tensile stress of 400 MPa and up to 100% tetragonal to monoclinic phase transformation.

  3. Development of residual stress measurement apparatus by neutron diffraction and its application to bent carbon steel

    International Nuclear Information System (INIS)

    Hayashi, Makoto; Ohkido, Shinobu; Minakawa, Nobuaki; Morii, Yukio

    1998-01-01

    To establish the measuring technique of neutron diffraction for the internal residual stress distribution in a structural component, a neutron diffraction apparatus was designed and manufactured in Modified Japan Research Reactor 3 (JRR3M). At the first step of measurement, a basic characteristics of the diffractometer was evaluated. The incident neutron beam flux was 10 4 n/cm 2 /sec and the Full Width at Half Maximum (FWHM) was about 0.3 degree. This indicates that the manufactured neutron diffractometer is capable for the residual stress measurement. As the first application of the neutron diffraction measurement, the residual stress distribution in plastically bent carbon steel plate was measured. A typical compressive-tensile-compressive-tensile residual stress pattern in the tangential direction in the bent plane was confirmed. The maximum stress near the surface was about 180 MPa. This means that the technique for residual stress measurement by neutron diffraction can be established in Japan. (author)

  4. Convenient measurement of the residual stress using X-ray penetration depth

    Energy Technology Data Exchange (ETDEWEB)

    Ukai, Takayoshi; Shibano, Junichi [Hokkaido Univ., Sapporo (Japan). Faculty of Engineering

    1994-10-01

    The residual stress measured with a characteristic X-ray is usually evaluated as a surface stress. However, it is a weighted mean value over all penetration depth of X-ray. Thus, the classical sin{sup 2}{Psi} method with the characteristic X-ray is difficult to use for measuring the steep gradient of residual stress that occurs along the depth direction in a subsurface layer of the material after cold rolling and grinding. This paper presents a convenient method of the residual stress measurement along the depth direction in a subsurface layer using the penetration depth depending on a characteristic X-ray. The residual stress distribution of JIS SKS51 steel plate was measured as an example of applying this method. As a result, it could be confirmed that a residual stress distribution along the depth direction in a subsurface layer could be evaluated nondestructively by this convenient method. (author).

  5. Residual stress evaluation in brittle coatings using indentation technique combined with in-situ bending

    International Nuclear Information System (INIS)

    Futakawa, Masatoshi; Steinbrech, R.W.; Tanabe, Yuji; Hara, Toshiaki

    2000-01-01

    The indentation crack length approach was adopted and further elaborated to evaluate residual stress and toughness of the brittle coatings: two kinds of glass coatings on steel. The influence of the residual stress on indentation cracking was examined in as-received coating condition and by in-situ superimposing a counteracting tensile stress. For purpose of providing reference toughness values stress-free pieces of separated coating material have also been examined. Thus results of the two complementary sets of experiments were assumed to prove self-consistently toughness and residual stress data of the coating. In particular, the in-situ bending of specimen in combination with the indentation test allowed us to vary deliberately the residual stress situation in glass coating. Thus experiments which utilized the combination of bending test and micro-indentation were introduced as a method to provide unambiguous information about residual compressive stress. Toughness and residual compressive stress of glass coatings used in this study were 0.46-0.50 MPa·m 1/2 and 94-111 MPa, respectively. Furthermore, a thermoelastic calculation of the residual compressive stress was performed and it is found that the value of residual compressive stress at coating surface of specimen was 90-102 MPa. (author)

  6. A Note on the Inverse Reconstruction of Residual Fields in Surface Peened Plates

    Directory of Open Access Journals (Sweden)

    S. Ali Faghidian

    Full Text Available Abstract A modified stress function approach is developed here to reconstruct induced stress, residual stress and eigenstrain fields from limited experimental measurements. The present approach is successfully applied to three experimental measurements set in surface peened plates with shallow shot peening affected zone. The well-rehearsed advantage of the proposed approach is that it not only minimizes the deviation of measurements from its approximations but also will result in an inverse solution satisfying a full range of continuum mechanics requirements. Also, the effect of component thickness as a geometric parameter influencing the residual stress state is comprehensively studied. A key finding of present study is that the plate thickness has no influence on the maximum magnitude of eigenstrain profile and compressive residual stresses within the shot peening affected zone while having a great influence on the magnitude of tensile residual stress and the gradient of linear residual stresses present in deeper regions.

  7. Residual stress distribution in carbon steel pipe welded joints measured by neutron diffraction

    International Nuclear Information System (INIS)

    Hayashi, Makoto; Ishiwata, Masayuki; Morii, Yukio; Minakawa, Nobuaki.

    1996-01-01

    Three dimensional residual stress distributions in a 4 inch diameter carbon steel pipe welded joint were measured by neutron diffraction technique. The results showed that the residual stress distributed near the weld metal, namely within about 30mm. The major tensile stresses occurred in the hoop direction in the fusion and heat affected zones of the weldment, and they attained a level greater than 200 MPa throughout the pipe wall thickness. While the axial residual stress at the inside surface was 40 MPa, the stress at the outside surface was -100 MPa. These residual stress distributions were compared with those measured by the X-ray diffraction technique and strain gauge method, and they agreed with each other. (author)

  8. Residual stress determination of rail tread using a laser ultrasonic technique

    International Nuclear Information System (INIS)

    Wang, Jing; Feng, Qibo

    2015-01-01

    A non-destructive method for measuring the residual stress on rail tread that uses a laser-generated ultrasonic technique is proposed. The residual stress distribution of different parts on both the new rail and used rail were examined. The surface acoustic waves (SAWs) are excited by a scanning line laser and detected by a laser ultrasonic detection system. A digital correlation method was used for calculating the changes in velocity of SAWs, which reflects the stress distribution. A wavelet de-noising technique and a least square fit were used for signal processing to improve the measurement accuracy. The effects of ultrasonic propagation distance and surface roughness on the determination of residual stress were analyzed and simulated. Results from the study demonstrate that the stress distribution results are accordant with the practical situation, and the laser-generated SAWs technique is a promising tool for the determination of residual stress in the railway inspection and other industrial testing fields. (paper)

  9. Effect of metal coating and residual stress on the resonant frequency ...

    Indian Academy of Sciences (India)

    - sive type respectively. In this paper, we investigate both these cases by taking two different structures, namely, the micro cantilever beam with gold layer deposited on its top surface and the MEMS gyroscope with residual stresses. First, we ...

  10. On the Stress Transfer of Nanoscale Interlayer with Surface Effects

    Directory of Open Access Journals (Sweden)

    Quan Yuan

    2018-01-01

    Full Text Available An improved shear-lag model is proposed to investigate the mechanism through which the surface effect influences the stress transfer of multilayered structures. The surface effect of the interlayer is characterized in terms of interfacial stress and surface elasticity by using Gurtin–Murdoch elasticity theory. Our calculation result shows that the surface effect influences the efficiency of stress transfer. The surface effect is enhanced with decreasing interlayer thickness and elastic modulus. Nonuniform and large residual surface stress distribution amplifies the influence of the surface effect on stress concentration.

  11. Thermal Stability of Residual Stresses in Ti-6Al-4V components

    International Nuclear Information System (INIS)

    Stanojevic, A; Angerer, P; Oberwinkler, B

    2016-01-01

    The need for light weight design while maintaining a high safety is essential for many components, especially in the aircraft industry. Therefore, it's important to consider every aspect to reduce weight, improve fatigue life and maintain safety of crucial components. Residual stresses are a major factor which can positively influence components and fulfil all three requirements. However, due to the inconstancy of the behaviour of residual stresses during the life time of a component, residual stresses are often neglected. If the behaviour of residual stresses could be described reliably over the entire life time of a component, residual stresses could be taken into account and components could be optimized even further. Mechanical and thermal loads are the main reason for relaxation of residual stresses. This work covers the thermal stability of residual stresses in Ti-6Al-4V components. Therefore, exposure tests at raised temperatures were performed on specimens with different surface conditions. Residual stresses were measured by x-ray diffraction before and after testing. Creep tests were also carried out to describe the creep behaviour and thereby the ability for residual stress relaxation. A correlation between the creep rate and amount of relaxed stress was found. The creep behaviour of the material was described by using a combination of the Norton Power law and the Arrhenius equation. The Zener-Wert-Avrami model was used to describe the residual stress relaxation. With these models a satisfying correlation between measured and calculated data was found. Hence, the relaxation of residual stresses due to thermal load was described reliably. (paper)

  12. Moire interferometry and hole drilling system for residual stress measurement

    Science.gov (United States)

    Ya, Min; Dai, Fulong; Lu, Jian

    2003-04-01

    A combined system of four beams moire interferometer and incremental hole-driling machine was designed and applied for residual stress measurement. Two typical experiments were done using this system: non-uniform in-depth residual stress measurement of an ultrasonic shot-peening Aluminum plate; non-uniform in-plane residual stress measurement of an elastic-plastic Aluminum bent beam. Experiments results show good accordant with other measurement results and theory analysis results.

  13. The influence of alloy composition on residual stresses in heat treated aluminium alloys

    Energy Technology Data Exchange (ETDEWEB)

    Robinson, J.S., E-mail: jeremy.robinson@ul.ie [Department of Mechanical, Aeronautical and Biomedical Engineering, University of Limerick (Ireland); Redington, W. [Materials and Surface Science Institute, University of Limerick (Ireland)

    2015-07-15

    The as quenched properties of eight different heat treatable aluminium alloys are related to residual stress magnitudes with the objective being to establish if there is a relationship between the residual stress and the as quenched alloy hardness and strength. Near surface residual stresses were assessed with X-ray diffraction using both the established sin{sup 2}ψ method and the more recent cos α technique. Through thickness residual stresses were also characterised using neutron diffraction. The alloys were chosen to encompass a wide range of strengths. The low to medium strength alloys were 6060 and 6082, medium to high strength 2618A, 2014A, 7075, 7010 and two variants of 7449, while the very high strength alloy was the powder metallurgy alloy N707. To assess the as quenched strength, dynamic hardness and tensile properties were determined from samples tested immediately after quenching to minimise the influence of precipitation hardening by natural aging. In addition, hot hardness measurements were made in situ on samples cooled to simulate quench paths. Within the experimental constraints of the investigation, the distribution of residual stress through the thickness was found to follow the same pattern for all the alloys investigated, varying from tensile in the interior to surface compression. The influence of alloy strength was manifested as a change in the observed residual stress magnitudes, and surface residual stresses were found to vary linearly with as quenched hardness and strength. - Highlights: • As quenched aluminium alloys contain high magnitude residual stresses. • Surface is compressive balance by a tensile core. • As quenched surface residual stress is linear function of alloy strength. • In situ hot hardness demonstrates rapid change in intrinsic hardness during rapid cooling.

  14. Residual stress measurements in polycrystalline graphite with micro-Raman spectroscopy

    International Nuclear Information System (INIS)

    Krishna, Ram; Jones, Abbie N.; Edge, Ruth; Marsden, Barry J.

    2015-01-01

    Micro-Raman microscopy technique is applied to evaluate unevenly distributed residual stresses in the various constituents of polygranular reactor grades graphite. The wavenumber based Raman shift (cm −1 ) corresponds to the local residual stress and measurements of stress dependent first order Raman spectra in graphite have enabled localized residual stress values to be determined. The bulk polygranular graphite of reactor grades – Gilsocarbon, NBG-18 and PGA – are examined to illustrate the residual stress variations in their constituents. Binder phase and filler particles have shown to be under compressive and tensile stresses, respectively. Among the studied graphite grades, the binder phase in Gilsocarbon has the highest residual stress and NBG-18 has the lowest value. Filler particles in Gilsocarbon have the highest residual stress and PGA showed the lowest, this is most likely due to the morphology of the coke particles used in the manufacturing and applied processing techniques for fabrications. Stresses have also been evaluated along the peripheral of pores and at the tips of the cracks. Cracks in filler and binder phases have shown mixed behaviour, compressive as well as tensile, whereas pores in binder and filler particles have shown compressive behaviour. The stresses in these graphitic constituents are of the order of MPa. Non-destructive analyses presented in this study make the current state-of-the-art technique a powerful method for the study of stress variations near the graphite surface and are expected to increase its use further in property determination analysis of low to highly fluence irradiated graphite samples from the material test reactors. - Highlights: • Micro-Raman spectroscopy can measure significantly small residual stresses. • Gilsocarbon, NBG-18 and PGA graphite were evaluated for residual stresses. • Residual stresses in the constituents of graphite were evaluated. • Binder and filler particles are often found under

  15. Experiment and numerical simulation for laser ultrasonic measurement of residual stress.

    Science.gov (United States)

    Zhan, Yu; Liu, Changsheng; Kong, Xiangwei; Lin, Zhongya

    2017-01-01

    Laser ultrasonic is a most promising method for non-destructive evaluation of residual stress. The residual stress of thin steel plate is measured by laser ultrasonic technique. The pre-stress loading device is designed which can easily realize the condition of the specimen being laser ultrasonic tested at the same time in the known stress state. By the method of pre-stress loading, the acoustoelastic constants are obtained and the effect of different test directions on the results of surface wave velocity measurement is discussed. On the basis of known acoustoelastic constants, the longitudinal and transverse welding residual stresses are measured by the laser ultrasonic technique. The finite element method is used to simulate the process of surface wave detection of welding residual stress. The pulsed laser is equivalent to the surface load and the relationship between the physical parameters of the laser and the load is established by the correction coefficient. The welding residual stress of the specimen is realized by the ABAQUS function module of predefined field. The results of finite element analysis are in good agreement with the experimental method. The simple and effective numerical and experimental methods for laser ultrasonic measurement of residual stress are demonstrated. Copyright © 2016. Published by Elsevier B.V.

  16. Analytical and Experimental Study of Residual Stresses in CFRP

    Directory of Open Access Journals (Sweden)

    Chia-Chin Chiang

    2013-01-01

    Full Text Available Fiber Bragg Grating sensors (FBGs have been utilized in various engineering and photoelectric fields because of their good environment tolerance. In this research, residual stresses of carbon fiber reinforced polymer composites (CFRP were studied using both experimental and analytical approach. The FBGs were embedded inside middle layers of CFRP to study the formation of residual stress during curing process. Finite element analysis was performed using ABAQUS software to simulate the CFRP curing process. Both experimental and simulation results showed that the residual stress appeared during cooling process and the residual stresses could be released when the CFRP was machined to a different shape.

  17. Residual Stress Analysis Based on Acoustic and Optical Methods

    Directory of Open Access Journals (Sweden)

    Sanichiro Yoshida

    2016-02-01

    Full Text Available Co-application of acoustoelasticity and optical interferometry to residual stress analysis is discussed. The underlying idea is to combine the advantages of both methods. Acoustoelasticity is capable of evaluating a residual stress absolutely but it is a single point measurement. Optical interferometry is able to measure deformation yielding two-dimensional, full-field data, but it is not suitable for absolute evaluation of residual stresses. By theoretically relating the deformation data to residual stresses, and calibrating it with absolute residual stress evaluated at a reference point, it is possible to measure residual stresses quantitatively, nondestructively and two-dimensionally. The feasibility of the idea has been tested with a butt-jointed dissimilar plate specimen. A steel plate 18.5 mm wide, 50 mm long and 3.37 mm thick is braze-jointed to a cemented carbide plate of the same dimension along the 18.5 mm-side. Acoustoelasticity evaluates the elastic modulus at reference points via acoustic velocity measurement. A tensile load is applied to the specimen at a constant pulling rate in a stress range substantially lower than the yield stress. Optical interferometry measures the resulting acceleration field. Based on the theory of harmonic oscillation, the acceleration field is correlated to compressive and tensile residual stresses qualitatively. The acoustic and optical results show reasonable agreement in the compressive and tensile residual stresses, indicating the feasibility of the idea.

  18. Residual stress distribution in carbon steel pipe welded joint measured by neutron diffraction

    International Nuclear Information System (INIS)

    Hayashi, Makoto; Ishiwata, Masayuki; Morii, Yukio; Minakawa, Nobuaki

    2000-01-01

    In order to estimate crack growth behavior of fatigue and stress corrosion cracking in pipes, the residual stress distribution near the pipe weld region has to be measured through the wall thickness. Since the penetration depth of neutron is deep enough to pass through the thick pipe wall, the neutron diffraction technique for the residual stress measurement is effective for this purpose. At the first step the residual stress distribution near the weld region in a butt-welded carbon steel pipe was measured by the neutron diffraction. Significant stresses extended only to a distance of 30 mm from the center of the weld. The major tensile stresses occurred in the hoop direction in the fusion and heat affected zones of the weldment, and they attained a level greater than 200 MPa through the thickness. While the axial residual stress at the inside surface was 50 MPa, the stress at the outside surface was -100 MPa. The comparison of residual stress distributions measured by the neutron diffraction, the X-ray diffraction and the strain gauge method reveals that the neutron diffraction is the most effective for measuring the residual stress inside the structural components. (author)

  19. Evaluation of residual stresses for the multipass welds of 316L stainless steel pipe

    International Nuclear Information System (INIS)

    Kim, S. H.; Joo, Y. S.; Lee, J. H.

    2003-01-01

    It is necessary to evaluate the influence of the residual stress and distortion in the design and fabrication of welded structure and the sound welded structure can be maintained by this consideration. Multipass welds of the 316L stainless steel have been widely employed in the pipes of Liquid Metal Reactor. In this study, the residual stresses in the 316L stainless steel pipe welds were calculated by the finite element method using ANSYS code. Also, the residual stresses both on the surface and in the interior of the thickness were measured by HRPD(High Resolution Powder Diffractometer) instrumented in HANARO Reactor. The residual stresses were measured for each 18 points in small(t/d=0.075) and large pipe specimens (t/d=0.034). The experimental and calculated results were compared and the characteristics of the distribution of the residual stress discussed

  20. Neutron diffraction measurements of residual stress for industrial application

    International Nuclear Information System (INIS)

    Minakawa, Nobuaki

    1999-01-01

    The neutron diffraction method is used to measure the inner strain distribution of material using the penetrating power of neutron as one of the effective use of the research reactor for the study and to evaluate a correct fatigue and a lifetime. Internal residual stress measurements have attracted great interest in material science where it is especially important to know the distribution of the internal stress when we estimated the strength of construction materials or processed goods for the industrial applications. This measurement can be applied to the study of hardening of processed goods, metal fatigue, strain of welding. Conventional techniques to measure strain such as strain gauge method, optical interference fringes method, X-ray diffraction method, Raman spectroscopic analysis method, and magnetostriction method, etc. can measure the strain only near the surface of materials. On the other hand, neutron diffractometer for residual stress analysis, RESA, installed at T2-1 port of JRR-3M enables us to study the internal stress non-destructively. (J.P.N.)

  1. Residual stress improvement for pipe weld by means of induction heating pre-flawed pipe

    International Nuclear Information System (INIS)

    Umemoto, T.; Yoshida, K.; Okamoto, A.

    1980-01-01

    The intergranular stress corrosion cracking (IGSCC) has been found in type 304 stainless steel piping of several BWR plants. It is already well known that IGSCC is most likely to occur when three essential factors, material sensitization, high tensile stress and corrosive environment, are present. If the welding residual stress is sufficiently high (200 to approximately 400 MPa) in the inside piping surface near the welded joint, then it may be one of the biggest contributors to IGSCC. If the residual stress is reduced or reversed by some way, the IGSCC will be effectively mitigated. In this paper a method to improve the residual stress named IHSI (Induction Heating Stress Improvement) is explained. IHSI aims to improve the condition of residual stress in the inside pipe surface using the thermal stress induced by the temperature difference in pipe wall, that is produced when the pipe is heated from the outside surface by an induction heating coil and cooled on the inside surface by water simultaneously. This method becomes more attractive when it can be successfully applied to in-service piping which might have some pre-flaw. In order to verify the validity of IHSI for such piping, some experiments and calculations using finite element method were conducted. These results are mainly discussed in this paper from the view-points of residual stress, flaw behaviour during IHSI and material deterioration. (author)

  2. Barkhausen noise-magnetizing voltage sweep measurement in evaluation of residual stress in hardened components

    International Nuclear Information System (INIS)

    Santa-aho, Suvi; Vippola, Minnamari; Lepistö, Toivo; Sorsa, Aki; Leiviskä, Kauko; Hakanen, Merja

    2014-01-01

    In this study, Barkhausen noise (BN) magnetizing voltage sweep (MVS) measurement is used to evaluate non-destructively the surface residual stress state of hardened components. A new computational feature, where the maximum slope of the sweep is divided by the corresponding magnetizing voltage, is introduced. The results show that this feature has a linear relationship with the residual stress state of the samples. The determination of residual stresses during online production of components is a highly recognized task because tensile stresses may be detrimental to the component. In this study, two sets of hardened samples are used in the analysis. A linear relationship is observed in each sample set indicating that the new feature is applicable in assessment of surface residual stresses of the components. (paper)

  3. Feasibility of ultrasonic and eddy current methods for measurement of residual stress in shot peened metals

    International Nuclear Information System (INIS)

    Lavrentyev, Anton I.; Stucky, Paul A.; Veronesi, William A.

    2000-01-01

    Shot peening is a well-known method for extending the fatigue life of metal components by introducing compressive residual stresses near their surfaces. The capability to nondestructively evaluate the near surface residual stress would greatly aid the assurance of proper fatigue life in shot-peened components. This paper presents preliminary results from a feasibility study examining the use of ultrasonic and eddy current NDE methods for residual stress measurement in components where the stress has been introduced by shot peening. With an ultrasonic method, a variation of ultrasonic surface wave speed with shot peening intensity was measured. Near surface conductivity was measured by eddy current methods. Since the effective penetration depth of both methods employed is inversely related to the excitation frequency, by making measurements at different frequencies, each method has the potential to provide the stress-depth profile. Experiments were conducted on aluminum specimens (alloy 7075-T7351) peened within the Almen peening intensity range of 4C to 16C. The experimental results obtained demonstrate a correlation between peening intensity and Rayleigh wave velocity and between peening intensity and conductivity. The data suggests either of the methods may be suitable, with limitations, for detecting unsatisfactory levels of shot peening. Several factors were found to contribute to the measured responses: surface roughness, near surface plastic deformation (cold work) and residual stress. The contribution of each factor was studied experimentally. The feasibility of residual stress determination from the measured data is discussed

  4. Controlling BWR pipe cracking by residual stress modification

    International Nuclear Information System (INIS)

    Gilman, J.D.; Giannuzzi, A.J.; Childs, W.J.

    1983-01-01

    Intergranular stress corrosion cracking may occur in the weld heat-affected zone of susceptible stainless steel materials which have been used in some boiling water reactor piping systems. One of the prerequisite conditions for stress corrosion attack is a high tensile stress in the exposed, locally sensitized material near the weld root. Several processes have been developed which can deter stress corrosion attack by altering the residual stress distributions near the welds to ensure that low stresses prevail in critical locations. These residual stress modification remedies and their qualification testing are described in this paper. (author)

  5. Residual Stress Distribution In Heat Affected Zone Of Welded Steel By Means Of Neutron Diffraction Method

    International Nuclear Information System (INIS)

    Fajar, Andika; Prasuad; Gunawan; Muslich, M. Rifai

    1996-01-01

    Three dimensional residual stress distribution in the heat affected zone of 10 mm thick welded steel by means of neutron diffraction technique has been measured. The results showed that the residual stress was distributed near the welded metal, namely within about 46,25 mm. The major tensile stresses occurred in the X-direction, and they attained a level greater than 2000 MPa through the position far away fram the weld. The tensile stresses in the Y and Z- directions lied between 500 and 1500 MPa, The results also suggest that the stress in the surface was greater than that in the middle of the sample

  6. Residual stresses generated in F-522 steel by different machining processes

    International Nuclear Information System (INIS)

    Gracia-Navas, V.; Ferreres, I.; Maranon, J. A.; Garcia-Rosales, C.; Gil-Sevillano, J.

    2005-01-01

    Machining operations induce plastic deformation and heat generation in the near surface area of the machined part, giving rise to residual stresses. Depending on their magnitude and sign, these stresses can be detrimental or beneficial to the service life of the part. The final stress state depends on the machining process applied, as well as on the machining parameters. Therefore, the establishment of adequate machining guidelines requires the measurement of the residual stresses generated both at the surface and inside the material. in this work, the residual stresses generated in F-522 steel by two hard turning (conventional and laser assisted) and two grinding (production and finishing) processes were measured by X-ray diffraction. Additionally, depth profiles of the volume fraction of retained austenite, microstructure and nano hardness were obtained in order to correlate those results with the residual stress state obtained for each machining process. It has been observed that turning generates tensile stresses in the surface while grinding causes compressive stresses. Below the surface grinding generates weak tensile or nearly null stresses whereas turning generates strong compressive stresses. These results show that the optimum mechanising process (disregarding economical considerations) implies the combination of turning plus elimination of a small thickness by final grinding. (Author) 19 refs

  7. Optimization of machining and vibration parameters for residual stresses minimization in ultrasonic assisted turning of 4340 hardened steel.

    Science.gov (United States)

    Sharma, Varun; Pandey, Pulak M

    2016-08-01

    The residual stresses generated in the machined work piece have detrimental effect on fatigue life, corrosion resistance and tribological properties. However, the effect of cutting and vibration parameters on residual stresses in Ultrasonic Assisted Turning (UAT) has not been dealt with. The present paper highlights the effect of feed rate, depth of cut, cutting velocity and percentage intensity of ultrasonic power on residual stress generation. XRD analysis has been carried out to measure the residual stress while turning 4340 hardened steel using UAT. The experiments were performed based on response surface methodology to develop statistical model for residual stress. The outcome of ANOVA revealed that percentage intensity and feed rate significantly affect the residual stress generation. The significant interactions between process parameters have also been presented tin order to understand the thermo-mechanical mechanism responsible for residual stress generation. Copyright © 2016 Elsevier B.V. All rights reserved.

  8. Simulation of Residual Stresses at Holes in Tempered Glass

    DEFF Research Database (Denmark)

    Nielsen, Jens Henrik; Olesen, John Forbes; Poulsen, Peter Noe

    2010-01-01

    This work presents a full 3D numerical study of the residual stresses in tempered (toughened) glass near holes using Narayanaswamy’s model for the tempering process. It is the objective of the paper to elucidate the influence on the minimal residual compressive stresses at holes from variations in...

  9. Frontline and future of residual stress measurement by neutron diffraction

    International Nuclear Information System (INIS)

    Hayashi, Makoto

    2007-01-01

    Neutron diffraction method is very much effective for measurements of residual stress and texture. In this paper the present techniques for measurements of residual stress and texture are reviewed and plans of improvement of RESA in JRR-3 and Ibaraki Prefecture's Material Design Diffractometer to be installed in J-PARC are introduced. (author)

  10. Research on the residual stress of glass ceramic based on rotary ultrasonic drilling

    Science.gov (United States)

    Sun, Lipeng; Jin, Yuzhu; Chen, Jianhua

    2016-10-01

    In the process of machining, the glass ceramic is easy to crack and damage, etc. And the residual stress in the machined surface may cause the crack to different extent in the later stage. Some may even affect the performance of the product. The residual stress of rotary ultrasonic drilling and mechanical processing is compared in different machining parameters (spindle speed, feed rate). The effects of processing parameters and methods are researched, in order to reduce the residual stress in the mechanical processing of glass ceramic, and provide guidance for the actual processing.

  11. Residual stress evaluation and curvature behavior of aluminium 7050 peen forming processed

    International Nuclear Information System (INIS)

    Oliveira, R.R. de; Lima, N.B.; Braga, A.P.V.; Goncalves, M.

    2010-01-01

    Shot peening is a superficial cold work process used to increase the fatigue life evaluated by residual stress measurements. The peen forming process is a variant of the shot peening process, where a curvature in the plate is obtained by the compression of the grains near to the surface. In this paper, the influence of the parameters such as: pressure of shot, ball shot size and thickness of aluminum 7050 samples with respect to residual stress profile and resulting arc height was studied. The evaluation of the residual stress profile was obtained by sin 2 Ψ method. (author)

  12. Evaluation of machining effect for the residual stress of SA508 by hole drilling method

    International Nuclear Information System (INIS)

    Lee, Jeong Kun; Lee, Kyoung Soo; Song, Ki O; Kim, Young Shin

    2009-01-01

    Residual stresses on a surface of the material are welcome or undesirable since it's direction, compression or tensile. But especially for the fatigue, it is not negligible effect on the material strength. These residual stresses developed during the manufacturing processes involving material deformation, heat treatment, machining. The object of this paper is verifying the effect of machining what is mostly used for SA508. For verifying the effect of machining, three different kind of machining have been achieved, milling, grinding, wire cutting. Also to measure the residual stress, hole drill method and indentation method are used.

  13. Study of residual stresses generated in machining of AISI 4340 steel

    International Nuclear Information System (INIS)

    Reis, W.P. dos; Fonseca, M.P. Cindra; Serrao, L.F.; Chuvas, T.C.; Oliveira, L.C.

    2010-01-01

    Among the mechanical construction steels, AISI 4340 has good harden ability, while combining high strength with toughness and good fatigue strength, making it excellent for application in the metalworking industry, where it can work at different levels and types of requests. Residual stresses are generated in almost all processes of mechanical manufacturing. In this study, the residual stresses generated in different machining processes and heat treatment hardening of AISI 4340 were analyzed by X-ray diffraction, by the sen 2 ψ method, using Crκβ radiation and compared. All samples, except for turned and cut by EDM, presented compressive residual stresses in the surface with various magnitudes. (author)

  14. An Experimental Investigation into Additive Manufacturing-Induced Residual Stresses in 316L Stainless Steel

    Science.gov (United States)

    Wu, Amanda S.; Brown, Donald W.; Kumar, Mukul; Gallegos, Gilbert F.; King, Wayne E.

    2014-12-01

    Additive manufacturing (AM) technology provides unique opportunities for producing net-shape geometries at the macroscale through microscale processing. This level of control presents inherent trade-offs necessitating the establishment of quality controls aimed at minimizing undesirable properties, such as porosity and residual stresses. Here, we perform a parametric study into the effects of laser scanning pattern, power, speed, and build direction in powder bed fusion AM on residual stress. In an effort to better understand the factors influencing macroscale residual stresses, a destructive surface residual stress measurement technique (digital image correlation in conjunction with build plate removal and sectioning) has been coupled with a nondestructive volumetric evaluation method ( i.e., neutron diffraction). Good agreement between the two measurement techniques is observed. Furthermore, a reduction in residual stress is obtained by decreasing scan island size, increasing island to wall rotation to 45 deg, and increasing applied energy per unit length (laser power/speed). Neutron diffraction measurements reveal that, while in-plane residual stresses are affected by scan island rotation, axial residual stresses are unchanged. We attribute this in-plane behavior to misalignment between the greatest thermal stresses (scan direction) and largest part dimension.

  15. Effects of tooling on the residual stress distribution in an inertia weld

    International Nuclear Information System (INIS)

    Pang, J.W.L.; Preuss, M.; Withers, P.J.; Baxter, G.J.; Small, C.

    2003-01-01

    Neutron diffraction residual strain measurements have been made on a tubular structure formed by joining two nickel-based superalloy RR1000 parts by inertia welding. Residual strains in the radial, hoop and axial directions of the tube cross-section have been measured. The corresponding residual stress field has been calculated accounting for the stress-free lattice parameter variations in the region close to the weld line. Tensile residual stresses were observed near the inner diameter of the tube with magnitudes of the order of +500, +1100 and +1300 MPa in the radial, axial and hoop directions, respectively. By comparison near the outer diameter (OD) of the weld the corresponding stresses are of the order of -200, -1000 and 150 MPa. The final stress state reflects the influence of the gripping fixture tooling and thermal gradients during inertia welding. Additional X-ray (at the surface) and hole-drilling (at the near surface) measurements show a steep residual stress gradient in the near surface region. Tensile hoop and axial machining stresses at the surface indicate the potential for improving the inertia weld tooling and the machining parameters used when removing the flash

  16. Residual stress effects in tubular K-joints crack growth

    OpenAIRE

    Acevedo, Claire; Nussbaumer, Alain

    2010-01-01

    Seeking light and transparent bridge designs, engineers and architects have found an efficient and artistic way to fulfill their requirements: steel tubular bridges. Like any other welded structure, the joints of this kind of bridge suffer from high tensile weld residual stresses. Combined with high stress concentrations, tensile residual stress is a relevant factor in fatigue crack development. Therefore, an experimental study has been carried out on tubular joints in order to characterize ...

  17. Development and Applications of Residual Stress Measurements Using Neutron Beams

    OpenAIRE

    ABRIOLA S. A.; BALAGUROV A.; BASHIR J.; DAS A.; EDWARDS L.; GNAEUPEL-HEROLD T.; GOH B.; IONITA I.; MIKULA P.; OHMS Carsten; PELD N.; SCHNEIDER Rainer; SUTIARSO S.; TOROK G.; VENTER A.

    2012-01-01

    The deep penetration and selective absorption of neutrons make them a powerful tool in nondestructive testing of materials with large samples or objects. Residual stress formed in a material during manufacturing, welding, utilization or repairs can be measured by means of neutron diffraction. In fact, neutron diffraction is the only non-destructive testing method, which can facilitate 3-D mapping of residual stress in a bulk component. Stress measurement using neutron beams is a technique ...

  18. Effect of residual stress on fatigue crack propagation at 200 C in a welded joint austenitic stainless steel - ferritic steel

    International Nuclear Information System (INIS)

    Zahouane, A.I.; Gauthier, J.P.; Petrequin, P.

    1988-01-01

    Fatigue resistance of heterogeneous welded joints between austenitic stainless steels and ferritic steels is evaluated for reactor components and more particularly effect of residual stress on fatigue crack propagation in a heterogeneous welded joint. Residual stress is measured by the hole method in which a hole is drilled through the center of a strain gage glued the surface of the materials. In the non uniform stress field a transmissibility function is used for residual stress calculation. High compression residual stress in the ferritic metal near the interface ferritic steel/weld slow down fatigue crack propagation. 5 tabs., 15 figs., 19 refs [fr

  19. Residual stress in ion implanted titanium nitride studied by parallel beam glancing incidence x-ray diffraction

    International Nuclear Information System (INIS)

    Geist, D.E.; Perry, A.J.; Treglio, J.R.; Valvoda, V.; Rafaja, D.

    1995-01-01

    Ion implantation is known to increase the lifetime of cutting tools. Current theories are the increase in lifetime is caused by an increase in the residual stress, or by work hardening of the surface associated with the implantation. In this work the effect of ion implantation on the residual stress in titanium nitride coatings made by the standard industrial methods of chemical and physical vapor deposition (CVD and PVD) is studied. It is found in the as-received condition (unimplanted), the residual stress levels are near zero for CVD materials and highly compressive, of the order of 6 GPa, for PVD materials. Ion implantation has no effect on the residual stress in the coatings made by CVD. Nitrogen does increase the compressive residual stress by some 10% in the near surface regions of PVD coatings, while nickel-titanium dual metal ion implantation does not have any effect. It appears that the lifetime increase is not associated with residual stress effects

  20. Ceramic laminates with tailored residual stresses

    Directory of Open Access Journals (Sweden)

    Baudín, C.

    2009-12-01

    Full Text Available Severe environments imposed by new technologies demand new materials with better properties and ensured reliability. The intrinsic brittleness of ceramics has forced scientists to look for new materials and processing routes to improve the mechanical behaviour of ceramics in order to allow their use under severe thermomechanical conditions. The laminate approach has allowed the fabrication of a new family of composite materials with strength and reliability superior to those of monolithic ceramics with microstructures similar to those of the constituent layers. The different ceramic laminates developed since the middle 1970´s can be divided in two large groups depending on whether the development of residual stresses between layers is the main design tool. This paper reviews the developments in the control and tailoring of residual stresses in ceramic laminates. The tailoring of the thickness and location of layers in compression can lead to extremely performing structures in terms of strength values and reliability. External layers in compression lead to the strengthening of the structure. When relatively thin and highly compressed layers are located inside the material, threshold strength, crack bifurcation and crack arrest during fracture occur.

    Las severas condiciones de trabajo de las nuevas aplicaciones tecnológicas exigen el uso de materiales con mejores propiedades y alta fiabilidad. La potencialidad de uso de materiales frágiles, como los cerámicos, en estas aplicaciones exige el desarrollo de nuevos materiales y métodos de procesamiento que mejoren su comportamiento mecánico. El concepto de material laminado ha permitido la fabricación de una nueva familia de materiales con tensiones de fractura y fiabilidad superiores a las de materiales monolíticos con microestructuras similares a las de las láminas que conforman el laminado. Los distintos materiales laminados desarrollados desde mediados de los años 70 se pueden

  1. Improvement and Validation of Weld Residual Stress Modelling Procedure

    International Nuclear Information System (INIS)

    Zang, Weilin; Gunnars, Jens; Dong, Pingsha; Hong, Jeong K.

    2009-06-01

    The objective of this work is to identify and evaluate improvements for the residual stress modelling procedure currently used in Sweden. There is a growing demand to eliminate any unnecessary conservatism involved in residual stress assumptions. The study was focused on the development and validation of an improved weld residual stress modelling procedure, by taking advantage of the recent advances in residual stress modelling and stress measurement techniques. The major changes applied in the new weld residual stress modelling procedure are: - Improved procedure for heat source calibration based on use of analytical solutions. - Use of an isotropic hardening model where mixed hardening data is not available. - Use of an annealing model for improved simulation of strain relaxation in re-heated material. The new modelling procedure is demonstrated to capture the main characteristics of the through thickness stress distributions by validation to experimental measurements. Three austenitic stainless steel butt-welds cases are analysed, covering a large range of pipe geometries. From the cases it is evident that there can be large differences between the residual stresses predicted using the new procedure, and the earlier procedure or handbook recommendations. Previously recommended profiles could give misleading fracture assessment results. The stress profiles according to the new procedure agree well with the measured data. If data is available then a mixed hardening model should be used

  2. Analytic examination of mechanism for compressive residual stress introduction with low plastic strain using peening

    International Nuclear Information System (INIS)

    Ishibashi, Ryo; Hato, Hisamitsu; Miyazaki, Katsumasa; Yoshikubo, Fujio

    2016-01-01

    Our goal for this study was to understand the cause of the differences in surface properties between surfaces processed using water jet peening (WJP) and shot peening (SP) and to examine the compressive residual stress introduction process with low plastic strain using SP. The dynamic behaviors of stress and strain in surfaces during these processes were analyzed through elasto-plastic calculations using a finite-element method program, and the calculated results were compared with measured results obtained through experiments. Media impacting a surface results in a difference in the hardness and microstructure of the processed surface. During SP, a shot deforms the surface locally with stress concentration in the early stages of the impact, while shock waves deform the surface evenly throughout the wave passage across the surface during WJP. A shot with a larger diameter creates a larger impact area on the surface during shot impact. Thus, SP with a large-diameter shot suppresses the stress concentration under the same kinetic energy condition. As the shot diameter increases, the equivalent plastic strain decreases. On the other hand, the shot is subject to size restriction since the calculated results indicate the compressive residual stress at the surface decreased and occasionally became almost zero as the shot diameter increased. Thus, compressive residual stress introduction with low plastic strain by using SP is considered achievable by using shots with a large diameter and choosing the appropriate peening conditions. (author)

  3. Standard test method for determining residual stresses by the hole-drilling strain-gage method

    CERN Document Server

    American Society for Testing and Materials. Philadelphia

    2008-01-01

    1.1 Residual Stress Determination: 1.1.1 This test method specifies a hole-drilling procedure for determining residual stress profiles near the surface of an isotropic linearly elastic material. The test method is applicable to residual stress profile determinations where in-plane stress gradients are small. The stresses may remain approximately constant with depth (“uniform” stresses) or they may vary significantly with depth (“non-uniform” stresses). The measured workpiece may be “thin” with thickness much less than the diameter of the drilled hole or “thick” with thickness much greater than the diameter of the drilled hole. Only uniform stress measurements are specified for thin workpieces, while both uniform and non-uniform stress measurements are specified for thick workpieces. 1.2 Stress Measurement Range: 1.2.1 The hole-drilling method can identify in-plane residual stresses near the measured surface of the workpiece material. The method gives localized measurements that indicate the...

  4. Residual stress characteristics in a non-circular drawing sequence of pearlitic steel wire

    Science.gov (United States)

    Baek, Hyun Moo; Hwang, Sun Kwang; Son, Il-Heon; Im, Yong-Taek

    2016-11-01

    In this paper, characteristics of residual stress in pearlitic steel wire drawn by a non-circular drawing (NCD) sequence with two processing routes, NCDA and NCDB, were experimentally and numerically investigated up to the 12th pass in comparison with conventional wire drawing (WD). For experimental investigation of the axial residual stress at the surface of the drawn wire, destructive (deflection) and non-destructive methods were employed. According to the experimental results, axial surface residual stress of the drawn wire by the NCD sequence was lower and more homogeneous compared to the conventional WD. Based on the elasto-plastic numerical simulation results from the surface to the center of the drawn wire using a commercial DEFORM-3D, an empirical relationship between residual stress and reduction of area was determined to predict the residual stress evolution in the multi-pass WD, NCDA, and NCDB, in that order. From the results of this investigation, it can be construed that the NCD sequence, especially the NCDB, might be helpful in improving the residual stress characteristics of pearlitic steel wire to improve its mechanical behavior and service life.

  5. Research on Formation Mechanism of Dynamic Response and Residual Stress of Sheet Metal Induced by Laser Shock Wave

    Science.gov (United States)

    Feng, Aixin; Cao, Yupeng; Wang, Heng; Zhang, Zhengang

    2018-01-01

    In order to reveal the quantitative control of the residual stress on the surface of metal materials, the relevant theoretical and experimental studies were carried out to investigate the dynamic response of metal thin plates and the formation mechanism of residual stress induced by laser shock wave. In this paper, the latest research trends on the surface residual stress of laser shock processing technology were elaborated. The main progress of laser shock wave propagation mechanism and dynamic response, laser shock, and surface residual stress were discussed. It is pointed out that the multi-scale characterization of laser and material, surface residual stress and microstructure change is a new hotspot in laser shock strengthening technology.

  6. Neutron and X-ray residual stress measurements of WC-Co alloys

    Energy Technology Data Exchange (ETDEWEB)

    Akiniwa, Yoshiaki; Tanaka, Keisuke [Dept. of Mechanical Engineering, Nagoya Univ. (Japan); Minakawa, Nobuaki; Morii, Yukio [Japan Atomic Energy Research Inst., Tokai, Ibaraki (Japan). Tokai Research Establishment; Kamiyama, Takashi [Tsukuba Univ., Ibaraki (Japan). Inst. of Materials Science

    2001-07-01

    As cemented carbides composed of metal carbides and pure metals had low deformation and excellent abrasion resistance at high temperature, they are used for various kinds of machining tools. As WC-Co is a typical cemented carbides, some residual stress when sintering a mixed molding of powdered WC and Co at 1400 to 1450 centigrade were introduced into the alloy, to largely affect strength of its materials. In this study, by using WC-Co alloys with various Co contents, thermal residual stress at each composing phase was tested by using X-ray and neutron methods, to investigate on effect of the Co content on the residual stress. And, a comparison with forecasting values using intercalated matters theory was also investigated. As a result, it was found that on the X-ray method, as thermal compressive residual stress increased with increase of content in Co phase, at more than 23.6 % it reduced and residual stress on vertical direction of specimen surface was nearly zero. And, it was also found that on neutron diffraction using angular dispersion method, residual stress in WC phase well agreed with forecasting value using the intercalated matters theory. Furthermore, it was also found that residual stress, when compensated by tested results of WC phase on 36.9 % material obtained by the angular dispersion method, showed good agreement with the forecasting values without relation to its testing methods. (G.K.)

  7. Neutron and X-ray residual stress measurements of WC-Co alloys

    International Nuclear Information System (INIS)

    Akiniwa, Yoshiaki; Tanaka, Keisuke; Minakawa, Nobuaki; Morii, Yukio; Kamiyama, Takashi

    2001-01-01

    As cemented carbides composed of metal carbides and pure metals had low deformation and excellent abrasion resistance at high temperature, they are used for various kinds of machining tools. As WC-Co is a typical cemented carbides, some residual stress when sintering a mixed molding of powdered WC and Co at 1400 to 1450 centigrade were introduced into the alloy, to largely affect strength of its materials. In this study, by using WC-Co alloys with various Co contents, thermal residual stress at each composing phase was tested by using X-ray and neutron methods, to investigate on effect of the Co content on the residual stress. And, a comparison with forecasting values using intercalated matters theory was also investigated. As a result, it was found that on the X-ray method, as thermal compressive residual stress increased with increase of content in Co phase, at more than 23.6 % it reduced and residual stress on vertical direction of specimen surface was nearly zero. And, it was also found that on neutron diffraction using angular dispersion method, residual stress in WC phase well agreed with forecasting value using the intercalated matters theory. Furthermore, it was also found that residual stress, when compensated by tested results of WC phase on 36.9 % material obtained by the angular dispersion method, showed good agreement with the forecasting values without relation to its testing methods. (G.K.)

  8. Investigating Resulting Residual Stresses during Mechanical Forming Process

    Science.gov (United States)

    Akinlabi, Stephen A.; Fatoba, Olawale S.; Mashinini, Peter M.; Akinlabi, Esther T.

    2018-03-01

    Most manufacturing processes such as machining, welding, heat treatment, laser forming, laser cladding and, laser metal deposition, etc. are subjected to a form of heat or energy to change the geometrical shape thus changing the inherent engineering and structural properties of the material. These changes often cause the development of locked up stresses referred to as residual stresses as a result of these activities. This study reports on the residual stresses developed due to the mechanical forming process to maintain a suitable structural integrity for the formed components. The result of the analysis through the X-ray diffraction confirmed that residual stresses were induced in the manufactured parts and further revealed that residual stresses were compressive in nature as found in the parent material but with values less than the parent material.

  9. Nonlinear morphoelastic plates I: Genesis of residual stress

    KAUST Repository

    McMahon, J.

    2011-04-28

    Volumetric growth of an elastic body may give rise to residual stress. Here a rigorous analysis is given of the residual strains and stresses generated by growth in the axisymmetric Kirchhoff plate. Balance equations are derived via the Global Constraint Principle, growth is incorporated via a multiplicative decomposition of the deformation gradient, and the system is closed by a response function. The particular case of a compressible neo-Hookean material is analyzed, and the existence of residually stressed states is established. © SAGE Publications 2011.

  10. Sensitivity Analysis for Residual Stress on DVI (Direct Vessel Injection) Nozzle Welded Joint

    Energy Technology Data Exchange (ETDEWEB)

    Noh, Byeong Wook; Chung, Sung Ho; Lee, Jung Hun; Kim, Oak Sug [DOOSAN Heavy Industries and Construction Co. LTD, Reactor Design Team, 555 Guygok-dong Changwon (Korea, Republic of)

    2008-07-01

    Generally, any welding process produces high compressive or tensile residual stresses in the heat affected zone depending on the method, shape and procedures of the weldment. In particular, the tensile residual stresses have a considerable effect on the material strength, fatigue strength and corrosion cracking. For this reason, it is important that some knowledge of the internal stress state be deduced either from measurements or from modeling predictions. In this study, the residual stresses after a multi-pass welding process for DVI nozzle welding joint were evaluated by a numerical simulation method. The welding joint considered three weld joint angles of 40 deg., 6 deg. and 2 deg. Computations were made using a 2-D finite element model based on the simulation of cooling from the heat treatment temperature to room temperature with two cooling conditions at the inside surface. In these results, it is shown that the residual stress increased at the inner surface, when water cooling was applied to the inner surface, and axial compressive residual stress increased at the inner surface when the joint angle was decreased. (authors)

  11. Influence of ion irradiation on internal residual stress in DLC films

    Energy Technology Data Exchange (ETDEWEB)

    Karaseov, Platon A., E-mail: platon.karaseov@rphf.spbstu.r [St. Petersburg State Polytechnic University, Polytechnicheskaya St. 29, 195251 St. Petersburg (Russian Federation); Podsvirov, Oleg A.; Karabeshkin, Konstantin V. [St. Petersburg State Polytechnic University, Polytechnicheskaya St. 29, 195251 St. Petersburg (Russian Federation); Vinogradov, Andrei Ya. [Ioffe Physicotechnical Institute RAS, Polytechnicheskaya 26, 195252 St. Petersburg (Russian Federation); Azarov, Alexander Yu. [St. Petersburg State Polytechnic University, Polytechnicheskaya St. 29, 195251 St. Petersburg (Russian Federation); Karasev, Nikita N. [State University of Information Technologies, Mechanics and Optics, Sablinskaya Str. 14, 197101 St. Petersburg (Russian Federation); Titov, Andrei I.; Smirnov, Alexander S. [St. Petersburg State Polytechnic University, Polytechnicheskaya St. 29, 195251 St. Petersburg (Russian Federation)

    2010-10-01

    The dependence of internal residual stress in thin diamond-like carbon films grown on Si substrate by PECVD technique on most important growth parameters, namely RF-power, DC bias voltage and substrate temperature, is described. Results show that compressive stress reaches the highest value of 2.7 GPa at low RF-power and DC bias. Increase of substrate temperature from 250 to 350 {sup o}C leads to nonlinear increase of stress value. Inhomogeneity of residual stress along the film surface disappears when film is deposited at temperatures above 275 {sup o}C. Post-growth film irradiation by P{sup +} and In{sup +} ions cause decrease of compressive stress followed by its inversion to tensile. For all ion energy combinations used residual stress changes linearly with normalized fluence up to 0.2 DPA with slope (8.7 {+-} 1.3) GPa/DPA.

  12. Evaluation of stress intensity factors due to welding residual stresses for circumferential cracked pipes

    International Nuclear Information System (INIS)

    Oh, Chang-Young; Kim, Yun-Jae; Oh, Young-Jin; Kim, Jong-Sung; Song, Tae-Kwang; Kim, Yong-Beum

    2013-01-01

    To investigate the applicability of existing methods to estimate stress intensity factors due to welding residual stresses, comparisons with finite element (FE) solutions are made for two types of generic welding residual stress profiles, generated by simulating repair welds. It is found that fitting residual stresses over the crack depth using third-order polynomials gives good estimates of stress intensity factors but fitting over the entire thickness can result in inaccurate estimates even with fourth-order polynomials. Noting that welding residual stresses are often determined from FE analyses, linearization of residual stresses to estimate stress intensity factors is proposed. Comparison with FE solutions shows good agreements. -- Highlights: ► Applicability of K estimation methods is investigated for welding residual stresses. ► Two types of generic residual stress profiles with repair welds are considered. ► Fitting residual stresses over the crack depth gives good estimates of K. ► A method to estimate K by linearising residual stress profiles is proposed

  13. Residual Stress Evaluation of Weld Inlay Process on Reactor Vessel Nozzles

    Energy Technology Data Exchange (ETDEWEB)

    Cho, Kihyun; Cho, Hong Seok [KEPCO KPS, Naju (Korea, Republic of)

    2015-10-15

    Weld overlay, weld inlay and stress improvement are mitigation technologies for butt joints. Weld overlay is done on pressurizer nozzles which are the highest potential locations occurring PWSCC due to high temperature in Korea. Reactor vessel nozzles are other big safety concerns for butt joints. Weld overlay and stress improvement should be so difficult to apply to those locations because space is too limited. Weld inlay should be one of the solutions. KEPCO KPS has developed laser welding system and process for reactor nozzles. Welding residual stress analysis is necessary for flaw evaluation. United States nuclear regulatory commission has calculated GTAW(Gas Tungsten Arc Welding) residual stress using ABAQUS. To confirm effectiveness of weld inlay process, welding residual stress analysis was performed. and difference between GTAW and LASER welding process was compared. Evaluation of weld inlay process using ANSYS and ABAQUS is performed. All of the both results are similar. The residual stress generated after weld inlay was on range of 450-500 MPa. Welding residual stresses are differently generated by GTAW and LASER welding. But regardless of welding process type, residual tensile stress is generated on inside surface.

  14. Residual Stress Evaluation of Weld Inlay Process on Reactor Vessel Nozzles

    International Nuclear Information System (INIS)

    Cho, Kihyun; Cho, Hong Seok

    2015-01-01

    Weld overlay, weld inlay and stress improvement are mitigation technologies for butt joints. Weld overlay is done on pressurizer nozzles which are the highest potential locations occurring PWSCC due to high temperature in Korea. Reactor vessel nozzles are other big safety concerns for butt joints. Weld overlay and stress improvement should be so difficult to apply to those locations because space is too limited. Weld inlay should be one of the solutions. KEPCO KPS has developed laser welding system and process for reactor nozzles. Welding residual stress analysis is necessary for flaw evaluation. United States nuclear regulatory commission has calculated GTAW(Gas Tungsten Arc Welding) residual stress using ABAQUS. To confirm effectiveness of weld inlay process, welding residual stress analysis was performed. and difference between GTAW and LASER welding process was compared. Evaluation of weld inlay process using ANSYS and ABAQUS is performed. All of the both results are similar. The residual stress generated after weld inlay was on range of 450-500 MPa. Welding residual stresses are differently generated by GTAW and LASER welding. But regardless of welding process type, residual tensile stress is generated on inside surface

  15. Eddy Current Nondestructive Residual Stress Assessment in Shot-Peened Nickel-Base Superalloys

    International Nuclear Information System (INIS)

    Blodgett, M.P.; Yu, F.; Nagy, P.B.

    2005-01-01

    Shot peening and other mechanical surface enhancement methods improve the fatigue resistance and foreign-object damage tolerance of metallic components by introducing beneficial near-surface compressive residual stresses and hardening the surface. However, the fatigue life improvement gained via surface enhancement is not explicitly accounted for in current engine component life prediction models because of the lack of accurate and reliable nondestructive methods that could verify the presence of compressive near-surface residual stresses in shot-peened hardware. In light of its frequency-dependent penetration depth, the measurement of eddy current conductivity has been suggested as a possible means to allow the nondestructive evaluation of subsurface residual stresses in surface-treated components. This technique is based on the so-called piezoresistivity effect, i.e., the stress-dependence of electrical resistivity. We found that, in contrast with most other materials, surface-treated nickel-base superalloys exhibit an apparent increase in electrical conductivity at increasing inspection frequencies, i.e., at decreasing penetration depths. Experimental results are presented to illustrate that the excess frequency-dependent apparent eddy current conductivity of shot-peened nickel-base superalloys can be used to estimate the absolute level and penetration depth of the compressive residual stress layer both before and after partial thermal relaxation

  16. Triaxial Measurement Method for Analysis of Residual Stress after High Feed Milling by X-Ray Diffraction

    Science.gov (United States)

    Čuma, Matúš; Török, Jozef; Telišková, Monika

    2016-12-01

    Surface integrity is a broad term which includes various quality factors affecting the functional properties of parts. Residual stress is one of these factors. Machining generates residual stresses in the surface and subsurface layers of the structural elements. X-ray diffractometry is a non-destructive method applicable for the measurement of residual stresses in surface and subsurface layers of components. The article is focused on the non-destructive progressive method of triaxial measurement of residual stress after machining the surface of sample by high feed milling technology. Significance of triaxial measuring is the capability of measuring in different angles so it is possible to acquire stress tensor containing normal and shear stress components acting in the spot of measuring, using a Cartesian coordinate system.

  17. Evaluation of residual stress distribution in austenitic stainless steel pipe butt-welded joint

    International Nuclear Information System (INIS)

    Maekawa, Akira; Noda, Michiyasu; Takahashi, Shigeru; Oumaya, Toru; Serizawa, Hisashi; Murakawa, Hidekazu

    2009-01-01

    This paper reports measured and estimated results of residual stress distributions of butt-welded austenitic stainless steel pipe in order to improve estimation accuracy of welding residual stress. Neutron diffraction and strain gauge method were employed for the measurement of the welding residual stress and its detailed distributions on inner and outer surface of the pipe as well as the distributions within the pipe wall were obtained. Finite element method was employed for the estimation. Transient and residual stresses in 3D butt-welded joint model were computed by employing Iterative Substructure Method and also commercial FEM code ABAQUS for a reference. The measured and estimated distributions presented typical characteristic of straight butt-welded pipe which had decreasing trend along the axial direction and bending type distributions through wall of the pipe. Both results were compared and the accuracy of measurement and estimation was discussed. (author)

  18. On the influence of residual stress on nano-mechanical characterization of thin coatings.

    Science.gov (United States)

    Sebastiani, M; Bemporad, E; Carassiti, F

    2011-10-01

    In the present paper, the effect of residual stress on the mechanical behavior of thin hard coatings has been investigated by a new methodology based on the combined use of focused ion beam (FIB) micro-machining techniques and nanoindentation testing. Surface elastic residual stress were determined by nanoindentation testing on Focused Ion Beam (FIB) milled micro-pillars. The average residual stress present in a 3.8 microm CAE-PVD TiN coating on WC-Co substrate was calculated by the comparison of two different sets of load-depth curves, the first one obtained at centre of stress relieved pillars, the second one on the undisturbed (residually stressed) surface. Results for stress measurement were in good agreement with the estimate obtained by XRD (sin2 psi method) analysis on the same sample, adopting the same elastic constants. In addition, nanoindentation on stress relieved pillars also allowed to perform a more accurate evaluation of elastic modulus and hardness of the coating. The effect of residual stress on crack propagation modes was quantitatively analyzed by high-load nanoindentation and application of energy methods for fracture toughness evaluation. It is found that compressive residual stress plays a relevant role in determining the fracture behavior and failure modes of the coating. Finally, Microstructural observations of the deformation mechanisms of the TiN coating were performed by TEM analysis on the cross section of the indentation, obtained by FIB lamella thinning. Results showed that plastic deformation at the nanoscale essentially occurs by formation of shear bands inside the columnar grains, independently of residual stress. A transition between intra-granular shear deformation and columnar grain sliding is also observed as a function of the applied load.

  19. Residual stress measurement of welding area by neutron diffraction method

    International Nuclear Information System (INIS)

    Suzuki, Tamaki; Sugiyama, Masaaki; Oikawa, Hatsuhiko; Nose, Tetsuro; Imafuku, Muneyuki; Tomota, Yo; Suzuki, Hiroshi; Moriai, Atsushi

    2010-01-01

    Resistance spot welding technique is extensively applied to join the body steel sheets in the manufacturing process for the automobile industry. It is known that the fatigue crack initiates occasionally inside of the spot-welded zone in this material, which is a serious issue of the fatigue life. Although this phenomenon is supposed to be related to internal residual stress, the actual residual stress distribution inside of the spot-welded zone is not clear up to now. In this study, a neutron diffraction residual stress measurement technique with well-defined sub-mm 3 square gauge volume is applied in order to clarify the internal three dimensional residual stress distribution just below the spot-welded part of the steel sheets. (author)

  20. Neutron diffraction studies of laser welding residual stresses

    Science.gov (United States)

    Petrov, Peter I.; Bokuchava, Gizo D.; Papushkin, Igor V.; Genchev, Gancho; Doynov, Nikolay; Michailov, Vesselin G.; Ormanova, Maria A.

    2016-01-01

    The residual stress and microstrain distribution induced by laser beam welding of the low-alloyed C45 steel plate was investigated using high-resolution time-of-flight (TOF) neutron diffraction. The neutron diffraction experiments were performed on FSD diffractometer at the IBR-2 pulsed reactor in FLNP JINR (Dubna, Russia). The experiments have shown that the residual stress distribution across weld seam exhibit typical alternating sign character as it was observed in our previous studies. The residual stress level is varying in the range from -60 MPa to 450 MPa. At the same time, the microstrain level exhibits sharp maxima at weld seam position with maximal level of 4.8·10-3. The obtained experimental results are in good agreement with FEM calculations according to the STAAZ model. The provided numerical model validated with measured data enables to study the influence of different conditions and process parameters on the development of residual welding stresses.

  1. Analysis of residual stresses in a long hollow cylinder

    International Nuclear Information System (INIS)

    Tokovyy, Yuriy V.; Ma, Chien-Ching

    2011-01-01

    This paper presents an analytical method for solving the axisymmetric stress problem for a long hollow cylinder subjected to locally-distributed residual (incompatible) strains. This method is based on direct integration of the equilibrium and compatibility equations, which thereby have been reduced to the set of two governing equations for two key functions with corresponding boundary and integral conditions. The governing equations were solved by making use of the Fourier integral transformation. Application of the method is illustrated with an analysis of the welding residual stresses in a butt-welded thick-walled pipe. - Highlights: → A solution to the axisymmetric stress problem for a hollow cylinder is constructed. → The cylinder is subjected to a field of locally-distributed residual strains. → The method is based on direct integration of the equilibrium equations. → An application of our solution to analysis of welding residual stresses is considered.

  2. The nev diffractometer ARES for the analysis of residual stresses

    Czech Academy of Sciences Publication Activity Database

    Staron, P.; Ruhnau, H. U.; Marmotti, M.; Mikula, Pavol; Kampmann, R.

    276/278, - (2000), s. 158-159 ISSN 0921-4526 Institutional research plan: CEZ:AV0Z1048901 Keywords : neutron instruments * residual stress Subject RIV: BM - Solid Matter Physics ; Magnetism Impact factor: 0.893, year: 2000

  3. Neutron diffractometer RSND for residual stress analysis at CAEP

    Science.gov (United States)

    Li, Jian; Wang, Hong; Sun, Guangai; Chen, Bo; Chen, Yanzhou; Pang, Beibei; Zhang, Ying; Wang, Yun; Zhang, Changsheng; Gong, Jian; Liu, Yaoguang

    2015-05-01

    Residual Stress Neutron Diffractometer (RSND) has been built at China Academy of Engineering Physics (CAEP) in Mianyang. Due to its excellent flexibility, the residual stress measurement on different samples, as well as in-situ study for materials science, can be carried out through RSND. The basic tests on its intensity and resolution and some preliminary experimental results under mechanical load, demonstrate the high quality of RSND.

  4. Reduction of Residual Stresses and Distortion in Girth Welded Pipes.

    Science.gov (United States)

    1987-06-01

    2.10).,1. R*4 $DATA 000402 027340 ( 6000) (3000) VAL L* Vec $iATA 000116 000132 ( 45.) (9.10) Sib routies, Furc’t :ors, atemerit ... Processo r- De ...Science in Mechanical Engineering. ABSTRACT Conventionally, welding control has been used to assure that the quality of the weld itself is maintained...to control and reduce these tensile residual stresses. [4] 8 Determination of residual stresses is complex. it requires an understanding in

  5. Standard practice for estimating the approximate residual circumferential stress in straight thin-walled tubing

    CERN Document Server

    American Society for Testing and Materials. Philadelphia

    2007-01-01

    1.1 A qualitative estimate of the residual circumferential stress in thin-walled tubing may be calculated from the change in outside diameter that occurs upon splitting a length of the tubing. This practice assumes a linear stress distribution through the tube wall thickness and will not provide an estimate of local stress distributions such as surface stresses. (Very high local residual stress gradients are common at the surface of metal tubing due to cold drawing, peening, grinding, etc.) The Hatfield and Thirkell formula, as later modified by Sachs and Espey, provides a simple method for calculating the approximate circumferential stress from the change in diameter of straight, thin-walled, metal tubing. 1.2 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

  6. Residual stress measurement inside a dissimilar metal weld mock-up of the pressurizer safety and relief nozzle

    Energy Technology Data Exchange (ETDEWEB)

    Campos, Wagner R.C.; Rabello, Emerson G.; Silva, Luiz L.; Mansur, Tanius R., E-mail: wrcc@cdtn.br, E-mail: egr@cdtn.br, E-mail: silvall@cdtn.br, E-mail: tanius@cdtn.br [Centro de Desenvolvimento da Tecnologia Nuclear (CDTN/CNEN-MG), Belo Horizonte (Brazil). Servico de Integridade Estrutural; Martins, Ketsia S., E-mail: ketshinoda@hotmail.com [Universidade Federal de Minas Gerais (UFMG), Nelo Horizonte (Brazil). Departamento de Engenharia Metalurgica

    2015-07-01

    Residual stresses are present in materials or structural component in the absence of external loads or changes in temperatures. The most common causes of residual stresses being present are the manufacturing or assembling processes. All manufacturing processes, such as casting, welding, machining, molding, heat treatment, among others, introduces residual stresses into the manufactured object. The residual stresses effects could be beneficial or detrimental, depending on its distribution related to the component or structure, its load service and if it is compressive or tensile. In this work, the residual strains and stresses inside a mock-up that simulates the safety and relief nozzle of Angra 1 Nuclear Power Plant pressurizer were studied. The current paper presents a blind hole-drilling method residual stress measurements both at the inner surface of dissimilar metal welds of dissimilar metal weld nozzle mock-up. (author)

  7. DETERMINATION OF RESIDUAL STRESS DISTRIBUTION IN HIGH STRENGTH ALUMINUM ALLOY AFTER EDM

    Directory of Open Access Journals (Sweden)

    Zubair Butt

    2017-03-01

    Full Text Available Thermal energy produced by discrete and random electric sparks in electric discharge machining (EDM melts surface material. A portion of this molten material is removed and the remaining material resolidified by rapid cooling in a hydrocarbon oil. The effect of repeated heating and cooling of the surface and sub surface material with complex temperature gradient results residual stresses in machined part. The aim of this investigation is to determine the distribution of residual stresses in the depth of machined material with respect to discharge current, most important electric parameter during EDM. It is well known that surface finish is dependent on discharge current. Therefore, investigations were carried out for smaller discharge current levels i.e. 3, 6, 9, 12 ampere. Hole-drill strain gauge method is used for the determination of residual stresses in the depth of material. For comparison purpose, residual stresses are also determined for conventionally turned specimens. This study provided quantitative analysis of the residual stresses for various discharge current in EDM which is a key parameter in deciding the service life of material.

  8. Determination of residual stresses in autofrettaged steel tubes by neutron and X-ray diffraction

    International Nuclear Information System (INIS)

    Pintschovius, L.; Macherauch, E.; Scholtes, B.

    1986-01-01

    The residual stress state of an autofrettaged 30 CrNiMo 8 steel tube has been investigated by neutron and X-ray diffraction. The results of X-ray measurements on the face of a ring cut out of the tube agree well with the neutron results obtained on the central part of an unmachined specimen. The experimentally determined residual stress distributions resemble only to a first approximation that expected from theoretical estimations. As expected, the tangential stress component at the inner diameter was found to be largest and is compressive. However, the distributions of the tangential and radial residual stress components show large deviations from the expected values. The differences between experiment and theory are probably due to neglecting the Bauschinger effect, the decarburization of the surface layers and the residual stresses produced by an alignment procedure before the autofrettage process. Annealing the tube for 1 h at 450 0 C has little effect on the residual stress distribution, except for a reduction in the steep gradient of the tangential stress component close to the inner surface. (orig.)

  9. Application of the contour method to validate residual stress predictions

    International Nuclear Information System (INIS)

    Welding is the most widespread method employed to join metallic components in nuclear power plants. This is an aggressive process that introduces complex three-dimensional residual stresses of substantial magnitude into engineering components. For safety-critical applications it can be of crucial importance to have an accurate characterisation of the residual stress field present in order to assess plant lifetime and risk of failure. Finite element modelling approaches are being increasingly employed by engineers to predict welding residual stresses. However, such predictions are challenging owing to the innate complexity of the welding process and can give highly variable results. Therefore, it is always desirable to validate residual stress predictions by experimental data. This paper illustrates how the contour method of measuring residual stress can be applied to various weldments in order to provide high quality experimental data. The contour method results are compared with data obtained by other well-established residual stress measurement techniques such as neutron diffraction and slitting methods and show a very satisfactory correlation. (author)

  10. The finite element analysis for prediction of residual stresses induced by shot peening

    International Nuclear Information System (INIS)

    Kim, Cheol; Yang, Won Ho; Sung, Ki Deug; Cho, Myoung Rae; Ko, Myung Hoon

    2000-01-01

    The shot peening is largely used for a surface treatment in which small spherical parts called shots are blasted on a surface of a metallic components with velocities up to 100m/s. This treatment leads to an improvement of fatigue behavior due to the developed compressive residual stresses, and so it has gained widespread acceptance in the automobile and aerospace industries. The residual stress profile on surface layer depends on the parameters of shot peening, which are, shot velocity, shot diameter, coverage, impact angle, material properties etc. and the method to confirm this profile is only measurement by X-ray diffractometer. Despite its importance to automobile and aerospace industries, little attention has been devoted to the accurate modeling of the process. In this paper, the simulation technique is applied to predict the magnitude and distribution of the residual stress and plastic deformation caused by shot peening with the help of the finite element analysis

  11. Numerical investigation on residual stress distribution and evolution during multipass narrow gap welding of thick-walled stainless steel pipes

    International Nuclear Information System (INIS)

    Liu, C.; Zhang, J.X.; Xue, C.B.

    2011-01-01

    Research highlights: → We performed pass-by-pass simulation of stresses for welding of thick-walled pipes. → The distributions and evolution of the residual stresses are demonstrated. → After the groove is filled to a height, the through-wall stress is almost unchanged. - Abstracts: The detailed pass-by-pass finite element (FE) simulation is presented to investigate the residual stresses in narrow gap multipass welding of pipes with a wall thickness of 70 mm and 73 weld passes. The simulated residual stress on the outer surface is validated with the experimental one. The distribution and evolution of the through-wall residual stresses are demonstrated. The investigated results show that the residual stresses on the outer and inner surfaces are tensile in the weld zone and its vicinity. The through-wall axial residual stresses at the weld center line and the HAZ line demonstrate a distribution of bending type. The through-wall hoop residual stress within the weld is mostly tensile. After the groove is filled to a certain height, the peak tensile stresses and the stress distribution patterns for both axial and hoop stresses remain almost unchanged.

  12. Residual stress investigation of copper plate and canister EB-Welds Complementary Results

    International Nuclear Information System (INIS)

    Gripenberg, H.

    2009-03-01

    The residual stresses in copper as induced by EB-welding were studied by specimens where the weld had two configurations: either a linear or a circumferential weld. This report contains the residual stress measurements of two plates, containing linear welds, and the full-scale copper lid specimen to which a hollow cylinder section had been joined by a circumferential EB-weld. The residual stress state of the EB-welded copper specimens was investigated by X-ray diffraction (XRD), hole drilling (HD) ring core (RC) and contour method (CM). Three specimens, canister XK010 and plates X251 and X252, were subjected to a thorough study aiming at quantitative determination of the residual stress state in and around the EB-welds using XRD for surface and HD and RC for spatial stress analysis. The CM maps one stress component over a whole cross section. The surface residual stresses measured by XRD represent the machined condition of the copper material. The XRD study showed that the stress changes towards compression close to the weld in the hollow cylinder, which indicates shrinkage in the hoop direction. According to the same analogy, the shrinkage in the axial direction is much smaller. The HD measurements showed that the stress state in the base material is bi-axial and, in terms of von Mises stress, 50 MPa for the plates and 20 MPa for the cylinder part of the canister. The stress state in the EB-welds of all specimens differs clearly from the stress state in the base material being more tensile, with higher magnitudes of von Mises stress in the plate than in the canister welds. The HD and RC results were obtained using linear elastic theory. The RC measurements showed that the maximum principal stress in the BM is close to zero near the surface and it becomes slightly tensile, 10 MPa, deeper under the surface. Welding pushed the general stress state towards tension with the maximum principal stress reaching 50 MPa, deeper than 5 mm below the surface in the weld. The

  13. Residual stress relief in MAG welded joints of dissimilar steels

    International Nuclear Information System (INIS)

    Seodek, P.; Brozda, J.; Wang, L.; Withers, P.J.

    2003-01-01

    This paper addresses the relief of residual stress in welded joints between austenitic and non-alloyed ferritic-pearlitic steels. A series of similar and dissimilar steel joints based on the 18G2A (ferritic-pearlitic) and 1H18N10T (austenitic) steels were produced, some of which were stress relieved by annealing and some by mechanical prestressing. For the as-welded and stress relieved test joints the residual stresses were measured by trepanning. To aid the interpretation of these results, 2D plane stress finite element analysis has been performed to simulate the residual stress relieving methods. Analysis of the results has shown that thermal stress relieving of welded joints between dissimilar steels is not effective and may even increase residual stresses, due to the considerable difference in thermal expansion of the joined steels. It was found that, for the loads imposed, the effectiveness of the mechanical stress relieving of dissimilar steel welded joints was much lower than that of similar steel joints

  14. INTERFACE RESIDUAL STRESSES IN DENTAL ZIRCONIA USING LAUE MICRO-DIFFRACTION

    International Nuclear Information System (INIS)

    Bale, H. A.; Tamura, N.; Coelho, P.G.; Hanan, J. C.

    2009-01-01

    Due to their aesthetic value and high compressive strength, dentists have recently employed ceramics for restoration materials. Among the ceramic materials, zirconia provides high toughness and crack resistant characteristics. Residual stresses develop in processing due to factors including grain anisotropy and thermal coefficient mismatch. In the present study, polychromatic X-ray (Laue) micro-diffraction provided grain orientation and residual stresses on a clinically relevant zirconia model ceramic disk. A 0.5 mm x 0.024 mm region on zirconia was examined on a 500 nm scale for residual stresses using a focused poly-chromatic synchrotron X-ray beam. Large stresses ranging from - to + 1GPa were observed at some grains. On average, the method suggests a relatively small compressive stress at the surface between 47 and 75 MPa depending on direction

  15. INTERFACE RESIDUAL STRESSES IN DENTAL ZIRCONIA USING LAUE MICRO-DIFFRACTION

    Energy Technology Data Exchange (ETDEWEB)

    Bale, H. A.; Tamura, N.; Coelho, P.G.; Hanan, J. C.

    2009-01-01

    Due to their aesthetic value and high compressive strength, dentists have recently employed ceramics for restoration materials. Among the ceramic materials, zirconia provides high toughness and crack resistant characteristics. Residual stresses develop in processing due to factors including grain anisotropy and thermal coefficient mismatch. In the present study, polychromatic X-ray (Laue) micro-diffraction provided grain orientation and residual stresses on a clinically relevant zirconia model ceramic disk. A 0.5 mm x 0.024 mm region on zirconia was examined on a 500 nm scale for residual stresses using a focused poly-chromatic synchrotron X-ray beam. Large stresses ranging from - to + 1GPa were observed at some grains. On average, the method suggests a relatively small compressive stress at the surface between 47 and 75 MPa depending on direction.

  16. Residual stresses in a cast iron automotive brake disc rotor

    Science.gov (United States)

    Ripley, Maurice I.; Kirstein, Oliver

    2006-11-01

    Runout, and consequent juddering and pulsation through the brake pedal, is a multi-million dollar per year warranty problem for car manufacturers. There is some suspicion that the runout can be caused by relaxation of residual casting stresses when the disc is overheated during severe-braking episodes. We report here neutron-diffraction measurements of the levels and distribution of residual strains in a used cast iron brake disc rotor. The difficulties of measuring stresses in grey cast iron are outlined and three-dimensional residual-strain distributions are presented and their possible effects discussed.

  17. Residual stresses in a cast iron automotive brake disc rotor

    International Nuclear Information System (INIS)

    Ripley, Maurice I.; Kirstein, Oliver

    2006-01-01

    Runout, and consequent juddering and pulsation through the brake pedal, is a multi-million dollar per year warranty problem for car manufacturers. There is some suspicion that the runout can be caused by relaxation of residual casting stresses when the disc is overheated during severe-braking episodes. We report here neutron-diffraction measurements of the levels and distribution of residual strains in a used cast iron brake disc rotor. The difficulties of measuring stresses in grey cast iron are outlined and three-dimensional residual-strain distributions are presented and their possible effects discussed

  18. Residual stress measurements in the dissimilar metal weld in pressurizer safety nozzle of nuclear power plant

    Energy Technology Data Exchange (ETDEWEB)

    Campos, Wagner R.C.; Rabello, Emerson G.; Mansur, Tanius R.; Scaldaferri, Denis H.B.; Paula, Raphael G., E-mail: wrcc@cdtn.br, E-mail: egr@cdtn.br, E-mail: tanius@cdtn.br, E-mail: dhbs@cdtn.br, E-mail: tanius@cdtn.br, E-mail: raphaelmecanica@gmail.com [Centro de Desenvolvimento da Tecnologia Nuclear (CDTN/CNEN-MG), Belo Horizonte, MG (Brazil); Souto, Joao P.R.S.; Carvalho Junior, Ideir T., E-mail: joprocha@yahoo.com.br, E-mail: ideir_engenharia@yahoo.com.br [Universidade Federal de Minas Gerais (UFMG), Belo Horizonte, MG (Brazil). Dept. de Engenharia Metalurgica

    2013-07-01

    Weld residual stresses have a large influence on the behavior of cracking that could possibly occur under normal operation of components. In case of an unfavorable environment, both stainless steel and nickel-based weld materials can be susceptible to stress-corrosion cracking (SCC). Stress corrosion cracks were found in dissimilar metal welds of some pressurized water reactor (PWR) nuclear plants. In the nuclear reactor primary circuit the presence of tensile residual stress and corrosive environment leads to so-called Primary Water Stress Corrosion Cracking (PWSCC). The PWSCC is a major safety concern in the nuclear power industry worldwide. PWSCC usually occurs on the inner surface of weld regions which come into contact with pressurized high temperature water coolant. However, it is very difficult to measure the residual stress on the inner surfaces of pipes or nozzles because of inaccessibility. A mock-up of weld parts of a pressurizer safety nozzle was fabricated. The mock-up was composed of three parts: an ASTM A508 C13 nozzle, an ASTM A276 F316L stainless steel safe-end, an AISI 316L stainless steel pipe and different filler metals of nickel alloy 82/182 and AISI 316L. This work presents the results of measurements of residual strain from the outer surface of the mock-up welded in base metals and filler metals by hole-drilling strain-gage method of stress relaxation. (author)

  19. Residual stress measurements in the dissimilar metal weld in pressurizer safety nozzle of nuclear power plant

    International Nuclear Information System (INIS)

    Campos, Wagner R.C.; Rabello, Emerson G.; Mansur, Tanius R.; Scaldaferri, Denis H.B.; Paula, Raphael G.; Souto, Joao P.R.S.; Carvalho Junior, Ideir T.

    2013-01-01

    Weld residual stresses have a large influence on the behavior of cracking that could possibly occur under normal operation of components. In case of an unfavorable environment, both stainless steel and nickel-based weld materials can be susceptible to stress-corrosion cracking (SCC). Stress corrosion cracks were found in dissimilar metal welds of some pressurized water reactor (PWR) nuclear plants. In the nuclear reactor primary circuit the presence of tensile residual stress and corrosive environment leads to so-called Primary Water Stress Corrosion Cracking (PWSCC). The PWSCC is a major safety concern in the nuclear power industry worldwide. PWSCC usually occurs on the inner surface of weld regions which come into contact with pressurized high temperature water coolant. However, it is very difficult to measure the residual stress on the inner surfaces of pipes or nozzles because of inaccessibility. A mock-up of weld parts of a pressurizer safety nozzle was fabricated. The mock-up was composed of three parts: an ASTM A508 C13 nozzle, an ASTM A276 F316L stainless steel safe-end, an AISI 316L stainless steel pipe and different filler metals of nickel alloy 82/182 and AISI 316L. This work presents the results of measurements of residual strain from the outer surface of the mock-up welded in base metals and filler metals by hole-drilling strain-gage method of stress relaxation. (author)

  20. Residual stress assessment for shot peened nickel based superalloy by eddy current technique

    Science.gov (United States)

    Shen, Yuping

    Surface enhancement treatment by shot peening has been widely used in industrial applications, especially for aircraft engine components. Typical peening processes use small shots of a few hundred micrometer in diameter blasted on component surfaces, resulting in residual stress near the surface in the depth range of a few hundred micrometers nominally. Compressive surface residual stress is useful for improving crack initiation resistance that prolongs service life of the part. To implement this highly desirable maintenance strategy, an in-service nondestructive method is needed to monitor the residual stress state of parts periodically, so that appropriate maintenance actions can be taken when residual-stress protection is lost, by either replacing or re-treating the part. X-ray and neutron diffraction methods are the only two standard methods considered the most reliable. However, conventional XRD methods can achieve relatively low penetration depth (Neutron diffraction method has also a practical limitation in terms of its cost and resulting radioactivity. In this dissertation, we developed a swept high frequency eddy current (SHFEC) measurement methodology for conductivity characterization of shot peened nickel based alloys. A model-based, eddy current inversion method is presented and applied to the SHFEC data obtained from a series of shot peened nickel based alloys to determine the depth profiles of actual conductivity up to 400 mum below the samples' surfaces. By developing a modified piezo-resistivity theory that includes the effect of texture on stress-induced conductivity changes, the residual stress profile of a shot peened IN718 sample is obtained from eddy current data. The obtained residual stress depth profile agrees with that measured by the standard layer removal XRD method. Texture profile of the shot peened IN718 sample is demonstrated by an XRD partial pole figure and orientation image microscopy (OIM). A new procedure of analyzing

  1. Effects of Surface Roughness and Aging on the Electrical Contact Resistance and Residual Stress in Gold-Nickel-Copper Connector Materials

    Science.gov (United States)

    2014-12-01

    particle with the target surface ejecting target atoms. Source: Oxford Vacuum Science [22] 21 Vlll Figure 2-10. Schematic of the fundamental...include nickel, silver , palladium, platinum, and gold [7, 21, 24-28]. One of the most common, particularly for high reliability applications, is...abrasive wear, delamination, brittle fracture, and fretting. Table 2-2 provides a brief description of the common wear mechanisms. Lubrication can

  2. Residual stress evaluation and curvature behavior of aluminium 7050 peen forming processed; Avaliacao da tensao residual em aluminio 7050 conformado pelo processo peen forming

    Energy Technology Data Exchange (ETDEWEB)

    Oliveira, R.R. de; Lima, N.B., E-mail: rolivier@ipen.b, E-mail: nblima@ipen.b [Instituto de Pesquisas Energeticas e Nucleares (IPEN/CNEN-SP), Sao Paulo, SP (Brazil); Braga, A.P.V.; Goncalves, M., E-mail: anapaola@ipt.b, E-mail: mgoncalves@ipt.b [Instituto de Pesquisas Tecnologicas (IPT), Sao Paulo, SP (Brazil)

    2010-07-01

    Shot peening is a superficial cold work process used to increase the fatigue life evaluated by residual stress measurements. The peen forming process is a variant of the shot peening process, where a curvature in the plate is obtained by the compression of the grains near to the surface. In this paper, the influence of the parameters such as: pressure of shot, ball shot size and thickness of aluminum 7050 samples with respect to residual stress profile and resulting arc height was studied. The evaluation of the residual stress profile was obtained by sin{sup 2} {Psi} method. (author)

  3. Verification of residual stresses in flash-butt-weld rails using neutron diffraction

    Science.gov (United States)

    Tawfik, David; Kirstein, Oliver; Mutton, Peter John; Chiu, Wing Kong

    2006-11-01

    Residual stresses developed during flash-butt welding may play a crucial role in prolonging the fatigue life of the welded tracks under service loading conditions. The finished welds typically exhibit high levels of tensile residual stresses in the web region of the weld. Moreover, the surface condition of the web may contain shear drag or other defects resulting from the shearing process which may lead to the initiation and propagation of fatigue cracks in a horizontal split web failure mode under high axle loads. However, a comprehensive understanding into the residual stress behaviour throughout the complex weld geometry remains unclear and is considered necessary to establish the correct localised post-weld heat treatment modifications intended to lower tensile residual stresses. This investigation used the neutron diffraction technique to analyse residual stresses in an AS60 flash-butt-welded rail cooled under normal operating conditions. The findings will ultimately contribute to developing modifications to the flash-butt-welding procedure to lower tensile residual stresses which may then improve rail performance under high axle load.

  4. Thermal input control and enhancement for laser based residual stress measurements using liquid temperature indicating coatings

    Science.gov (United States)

    Pechersky, Martin J.

    1999-01-01

    An improved method for measuring residual stress in a material comprising the steps of applying a spot of temperature indicating coating to the surface to be studied, establishing a speckle pattern surrounds the spot of coating with a first laser then heating the spot of coating with a far infrared laser until the surface plastically deforms. Comparing the speckle patterns before and after deformation by subtracting one pattern from the other will produce a fringe pattern that serves as a visual and quantitative indication of the degree to which the plasticized surface responded to the stress during heating and enables calculation of the stress.

  5. Effect of shot peening treatment in the behavior of residual stress in duplex stainless steel during medium cycle fatigue

    International Nuclear Information System (INIS)

    Pedrosa, Peter D.S.; Rebello, Joao Marcos A.; Fonseca, Maria P. Cindra

    2010-01-01

    The lifetime of duplex stainless steel parts experiencing cyclic fatigue is directly influenced by the residual stresses present in the ferrite and austenite phases. The motivation for this work was to analyze the behaviour of the residual stresses fields introduced by shot peening treatment in both phases, in the sample surface as in the subsurface layers, in low fatigue cycles, using the X-rays diffraction technique. The results shows that the compressive residual stresses introduced by the shot peening treatment in both phases improved fatigue life of the material. However, the cyclical loads produce partial or total relief in these residual stresses fields. It was verified that the shot peening process induced the formation of microcracks only in the ferrite phase. The largest variations in the total compressive residual stresses fields also occurred in this phase. The samples surfaces were analyzed by scanning electron microscopy. (author)

  6. Analysis of macro and micro residual stresses in functionally graded materials by diffraction methods

    CERN Document Server

    Dantz, D; Reimers, W

    1999-01-01

    The residual stress state in microwave sintered metal-ceramic functionally graded materials (FGM) consisting of 8Y-ZrO/sub 2//Ni and 8Y-ZrO/sub 2//NiCr8020, respectively, was analysed by non- destructive diffraction methods. In $9 order to get knowledge of the complete residual stress state in the near surface region as well as in the interior of the material, complementary methods were applied. Whereas the surface was characterised by X-ray techniques using $9 conventional sources, the stresses within the bulk of the material were investigated by means of high energy synchrotron radiation. The stress state was found to obey the differences in the coefficients of thermal expansion $9 (micro-stresses) on the one hand and the inhomogeneous cooling conditions (macrostresses) on the other hand. (7 refs).

  7. As-Cast Residual Stresses in an Aluminum Alloy AA6063 Billet: Neutron Diffraction Measurements and Finite Element Modeling

    OpenAIRE

    Drezet, Jean-Marie; Phillion, André

    2010-01-01

    The presence of thermally induced residual stresses, created during the industrial direct chill (DC) casting process of aluminum alloys, can cause both significant safety concerns and the formation of defects during downstream processing. Although numerical models have been previously developed to compute these residual stresses, most of the computations have been validated only against measured surface distortions. Recently, the variation in residual elastic strains in the steady-state regim...

  8. Numerical analysis of residual stresses reconstruction for axisymmetric glass components

    Science.gov (United States)

    Tao, Bo; Xu, Shuang; Yao, Honghui

    2018-01-01

    A non-destructive measurement method for 3D stress state in a glass cylinder using photoelasticity has been analyzed by simulation in this research. Based on simulated stresses in a glass cylinder, intensity of the cylinder in a circular polariscope can be calculated by Jones calculus. Therefore, the isoclinic angle and optical retardation can be obtained by six steps phase shifting technique. Through the isoclinic angle and optical retardation, the magnitude and distribution of residual stresses inside the glass cylinder in cylindrical coordinate system can be reconstructed. Comparing the reconstructed stresses with numerical simulated stresses, the results verify this non-destructive method can be used to reconstruct the 3D stresses. However, there are some mismatches in axial stress, radial stress and circumferential stress.

  9. Determination of residual stresses at ILL present and future

    CERN Document Server

    Pirling, T

    2002-01-01

    The ILL is constructing, in collaboration with the Manchester Materials Science Centre, a neutron strain imager for the non-destructive determination of residual stresses. The project is funded by ILL and the EPSRC (Engineering and Physical Science Research Council) on a fifty-fifty basis. A special feature of the instrument is the sample table, which will be a Stewart platform or hexapod. It allows most flexible sample movement, having a load capacity of more than 500 kg and allowing sample sizes of up to 2-m length. A new supermirror neutron guide and a specially developed two-dimensional focusing monochromator will provide more than 2.6 times the neutron flux of the present instrument. A limitation of the neutron strain scanning technique is the surface effect, which introduces huge errors when scanning through interfaces or surfaces. Experiments have shown that the use of radial collimators for beam-defining optics reduces the surface error drastically. Such a configuration is one option of the present st...

  10. Prediction of residual stress using explicit finite element method

    Directory of Open Access Journals (Sweden)

    W.A. Siswanto

    2015-12-01

    Full Text Available This paper presents the residual stress behaviour under various values of friction coefficients and scratching displacement amplitudes. The investigation is based on numerical solution using explicit finite element method in quasi-static condition. Two different aeroengine materials, i.e. Super CMV (Cr-Mo-V and Titanium alloys (Ti-6Al-4V, are examined. The usage of FEM analysis in plate under normal contact is validated with Hertzian theoretical solution in terms of contact pressure distributions. The residual stress distributions along with normal and shear stresses on elastic and plastic regimes of the materials are studied for a simple cylinder-on-flat contact configuration model subjected to normal loading, scratching and followed by unloading. The investigated friction coefficients are 0.3, 0.6 and 0.9, while scratching displacement amplitudes are 0.05 mm, 0.10 mm and 0.20 mm respectively. It is found that friction coefficient of 0.6 results in higher residual stress for both materials. Meanwhile, the predicted residual stress is proportional to the scratching displacement amplitude, higher displacement amplitude, resulting in higher residual stress. It is found that less residual stress is predicted on Super CMV material compared to Ti-6Al-4V material because of its high yield stress and ultimate strength. Super CMV material with friction coefficient of 0.3 and scratching displacement amplitude of 0.10 mm is recommended to be used in contact engineering applications due to its minimum possibility of fatigue.

  11. Characteristic and principle of the residual stress measurement by neutron diffraction method

    International Nuclear Information System (INIS)

    Akiniwa, Yoshiaki

    2016-01-01

    Although X-ray method has been widely used as the nondestructive measurement method of residual stress, the object to be measured with laboratory X-ray was limited to the vicinity of surface, and the nondestructive measurement of stress inside an essential component could not be performed. Since the neutron method utilizes the wave characteristics of electrically neutral particles, the penetrability is excellent so that information up to the inside of a material can be obtained sufficiently. As the feature of neutron stress measurement, it is suitable for measurement inside metals such as iron and aluminum, which cannot be measured with X-rays. For the measurement of residual stress in localized region, the use of high energy synchrotron radiation is advantageous. In the stress measurement utilizing diffraction phenomena, there is the strain calculated from a change in diffraction lattice spacing. The measured strain is converted into stress using Hooke's Law. As the measurement examples of neutron stress evaluation, the following are introduced: (1) residual stress distribution around the ferrite steel (50 mm thick) welded joint of a large-sized structure, (2) residual stress due to the heat treatment of aluminum alloy with a plate thickness of 20 to 140 mm, and (3) change in the strain of aluminum die block in the vicinity of a cast iron cylinder liner of engine, when heating/cooling up to 470degC. (A.O.)

  12. Isolation of residuals using trend surface analysis to magnetic data ...

    African Journals Online (AJOL)

    Polynomial surfaces of various degrees are fitted to a magnetic data of Awo area, southwestern Nigeria with the aim of isolating the residuals of the area associated with mineralogy. The fourth degree surface correlates better with the magnetic map of the study area. The residualized data were obtained by subtracting the ...

  13. Residual Stress Measurement of Titanium Casting Alloy by Neutron Diffraction

    Science.gov (United States)

    Nishida, M.; Jing, T.; Muslih, M. R.; Hanabusa, T.

    2008-03-01

    Neutron stress measurement can detect strain and stress information in deep region because of large penetration ability of neutron beams. The present paper describes procedure and results in the residual stress measurement of titanium casting alloy by neutron diffraction. In this study, the three axial method using Hooke's equation was employed for neutron stress measurement. This method was applied to the cylindrical shape sample of titanium casting alloy (Ti-6Al-4V). Form the results of this study, this sample has large crystal grain in the inside whole position, it is assumed this large grain was grown up during casting manufacture process. Furthermore, the peak profile used to the stress measurement appears in very weak because of the HCP crystal system of titanium character and effect of large crystal grain. These conditions usually make difficult to measure the accuracy values of residual stresses. Therefore, it had to spend a long time to measure the satisfied data from titanium sample. Regarding to the results of stress measurement, the stress values in the cylindrical sample of three directions is almost same tendency, and residual stresses change from the compressive state in the outer part to the tensile state in the inner part gradually.

  14. THE IMPACT OF CUTTING CONDITIONS ON RESIDUAL STRESSES IN THE CASE OF PLAIN MILLING

    Directory of Open Access Journals (Sweden)

    Nikolaj Ganev

    2010-12-01

    Full Text Available The goal of the contribution is to present results of X-ray diffraction study of residual stresses in thesurface layers of guide gibs for machining centres made from hardened 14 100.3 steel. Investigated samples wereside-milled using a cutter head with tool tips. While the cutting depth was kept constant, various cutting speeds,and feeds were applied. Surface integrity was studied in order to assess the effect of the varied machiningparameters on both the surface and depth distributions of residual stresses. The state of residual stresses wasdetermined in two azimuths by means of X-ray diffraction technique. Considering that the penetration depth ofCrKalfa X-ray radiation in steels is less than 5 µm, electrochemical etching was applied for depth profiling.

  15. Experimental analysis of residual stresses in pre-straightened SAE 1045 steel

    International Nuclear Information System (INIS)

    Diehl, Carla Adriana Theis Soares; Rocha, Alexandre da Silva

    2017-01-01

    This paper aims at analyzing the effects of the roller pre-straightening of wire-rods on residual stress distributions in SAE 1045 steel bars. The combined drawing process is used in industrial production of bars in order to obtain a good surface quality and improved mechanical properties complying with specifications of the final products. In this process, prior to the drawing step, a roller straightening of the steel wire-rod is essential, because it provides the minimum straightness necessary for drawing. Metallographic analysis and hardness test were done for selected samples after different processing steps. Also, residual stress analysis of pre-straightened wire-rods by X-ray diffraction and neutron diffraction were carried out. The hardness tests show higher values near the surface and lower in the center of the wire-rod. Besides, the residual stresses results show a big inhomogeneity from one peripheral position to another and also in the evaluated cross section. (author)

  16. Experimental analysis of residual stresses in pre-straightened SAE 1045 steel

    Energy Technology Data Exchange (ETDEWEB)

    Diehl, Carla Adriana Theis Soares; Rocha, Alexandre da Silva, E-mail: carla.adriana@ufrgs.br [Universidade Federal do Rio Grande do Sul (UFRGS), Porto Alegre, RS (Brazil). Laboratorio de Formacao de Metais; Epp, Jérémy; Zoch, Hans-Werner [Stiftung Institut für Werkstofftechnik IWT, University of Bremen (Germany)

    2017-11-15

    This paper aims at analyzing the effects of the roller pre-straightening of wire-rods on residual stress distributions in SAE 1045 steel bars. The combined drawing process is used in industrial production of bars in order to obtain a good surface quality and improved mechanical properties complying with specifications of the final products. In this process, prior to the drawing step, a roller straightening of the steel wire-rod is essential, because it provides the minimum straightness necessary for drawing. Metallographic analysis and hardness test were done for selected samples after different processing steps. Also, residual stress analysis of pre-straightened wire-rods by X-ray diffraction and neutron diffraction were carried out. The hardness tests show higher values near the surface and lower in the center of the wire-rod. Besides, the residual stresses results show a big inhomogeneity from one peripheral position to another and also in the evaluated cross section. (author)

  17. Forging And Milling Contribution On Residual Stresses For A Textured Biphasic Titanium Alloy

    International Nuclear Information System (INIS)

    Deleuze, C.; Fabre, A.; Barrallier, L.; Molinas, O.

    2011-01-01

    Ti-10V-2Fe-3Al is a biphasic titanium alloy (α+β) used in aeronautical applications for its mechanical properties, such as its yield strength of 1200 MPa and it weighs 40% less than steel. This alloy is particularly useful for vital parts with complex geometry, because of its high forging capability. In order to predict the capability for fatigue lifetime, the designers need to know the residual stresses. X-Ray diffraction is the main experimental technique used to determine residual stresses on the surface. In this case, stress levels are primarily influenced by the complex forging and milling process. On this alloy in particular, it may be difficult to characterize stress due to modification of the microstructure close to the surface. Results obtained by x-ray analysis depend on the correct definition of the shape of the diffraction peaks. The more precisely defined the position of the peak, the more accurately the stresses are evaluated. This paper presents a method to detect if residual stresses can be characterized by x-ray diffraction. The characterization of hardness seems to be a relevant technique to quickly analyze the capability of x-ray diffraction to determine residual stresses.

  18. Study on production mechanism of welding residual stress at the juncture of a pipe penetrating a thick plate

    International Nuclear Information System (INIS)

    Mochizuki, Masahito; Enomoto, Kunio; Okamoto, Noriaki; Saitoh, Hideyo; Hayashi, Eisaku.

    1994-01-01

    This paper studies welding residual stresses at the intersection of a small diameter pipe penetrating a thick plate. The pipe is welded to the plate, and Tungsten Innert Gas (TIG) cladding is melted on the inner surface of the pipe to protect it from stress corrosion cracking due to long operation in nuclear power plants. Stresses are calculated by heat conduction analysis and thermal elasto-plastic analysis, and also measured by strain gauges. Welding residual stresses are shown to have no corrosive influence on the inner pipe surface, and the stresses are compressed enough to protect the pipe against stress corrosion cracking on the outer surface. It was also studied to make clear the production mechanism of the residual stresses which were generated by welding processes at the pipe. (author)

  19. Residual stresses in the Al2O3 matrix of Al2O3ZrO2

    International Nuclear Information System (INIS)

    Feng, G.; Tsakalakos, T.; Mayo, W.; Wilfinger, K.; Cannon, W.R.

    1989-01-01

    Residual stresses in the Al 2 O 3 matrix of ground and unground surfaces of zirconia toughened alumina were measured with x-ray techniques. No net residual stresses were found on as-fired surfaces, but residual stresses were found on ground surfaces, increasing with severity of grinding and were proportional to the percent ZrO 2 undergoing the tetragonal monoclinic transformation during grinding. Principal stresses and directions with respect to the grinding direction were obtained. Also Warren-Averbach measurements were made on as- fired surfaces to determine the nonuniform stresses surrounding the particles. These stresses were also found to depend on the monoclinic content which in turn was controlled by the size of the particles

  20. Residual Stress in Brazing of Submicron Al2O3 to WC-Co

    Science.gov (United States)

    Grunder, T.; Piquerez, A.; Bach, M.; Mille, P.

    2016-07-01

    This study evaluated the residual stresses induced by brazing and grinding submicron Al2O3, using different methods. Energy dispersive x-ray spectrometry analysis (EDX) of 72Ag-Cu filler and filler/WC-Co interface showed evidence of atomic diffusion and possible formation of titanium oxide layers between the joint and the bonding materials. An analytical model supported by the finite element method (FEM) based on strain determination due to the difference in variation of thermal expansion was used to assess the stress distribution at the coupling interface and in bulk materials. The model took into account the evolution of the Young's modulus and of the thermal expansion with temperature. The model could be used to follow strain and stress evolutions of the bonded materials during the cooling cycle. The maximum stress rose above -300 MPa at the center of the 100 × 100 × 3 mm ceramic plates. The residual stresses on the external surface of ceramic were investigated by x-ray diffraction (XRD) and indentation fracture method (IFM). After brazing and grinding the plate, the principal stresses were 128.1 and 94.9 MPa, and the shear stress was -20.1 MPa. Microscopic examination revealed grain pull-out promoted by the global residual stresses induced by the brazing and grinding processes. The surface stresses evaluated by the different methods were reasonably correlated.

  1. Reduction of tensile residual stresses during the drawing process of tungsten wires

    International Nuclear Information System (INIS)

    Rodriguez Ripoll, Manel; Weygand, Sabine M.; Riedel, Hermann

    2010-01-01

    Tungsten wires are commonly used in the lighting industry as filaments for lamps. During the drawing process, the inhomogeneous deformation imparted by the drawing die causes tensile residual stresses at the wire surface in circumferential direction. These stresses have a detrimental effect for the wire because they are responsible for driving longitudinal cracks, known as splits. This work proposes two methods for reducing the residual stresses during wire drawing, namely applying an advanced die geometry and performing an inexpensive post-drawing treatment based on targeted bending operations. These two methods are analyzed with finite element simulations using material parameters obtained by mechanical tests on tungsten wires at different temperatures as input data. The computed results predict a substantial reduction of the circumferential residual stresses, thus reducing the risk of splitting.

  2. Residual stress evolution regularity in thermal barrier coatings under thermal shock loading

    Directory of Open Access Journals (Sweden)

    Ximin Chen

    2014-01-01

    Full Text Available Residual stress evolution regularity in thermal barrier ceramic coatings (TBCs under different cycles of thermal shock loading of 1100°C was investigated by the microscopic digital image correlation (DIC and micro-Raman spectroscopy, respectively. The obtained results showed that, as the cycle number of the thermal shock loading increases, the evolution of the residual stress undergoes three distinct stages: a sharp increase, a gradual change, and a reduction. The extension stress near the TBC surface is fast transformed to compressive one through just one thermal cycle. After different thermal shock cycles with peak temperature of 1100°C, phase transformation in TBC does not happen, whereas the generation, development, evolution of the thermally grown oxide (TGO layer and micro-cracks are the main reasons causing the evolution regularity of the residual stress.

  3. Residual Stress Analysis of Severe Plastic Deformed Materials using the Finite Element Method and the Neutron Diffraction Method

    International Nuclear Information System (INIS)

    Kang, Mi Hyun; Seong, Back Suck; Kim, Hyoung Seop

    2009-01-01

    Severe plastic deformation (SPD) is one of the most promising top-down techniques, moving towards industrialization to fabricate bulk ultrafine grain materials. The strain distribution and deformation behavior during the ECAP (equal channel angular pressing), influenced by tool angles, friction and material behavior, was studied through experimental and numerical analyses. The residual stress of work piece which was straight before ECAP produces many serious problems in the next processing e.g. input of the work piece for the next ECAP. The bent work piece needs additional straightening or surface polishing even if the amount of bending is small, and residual stress need to be released before service applications. Residual stress, particularly tensile residual stress can be a very important factor in affecting the reliability and integrity of working parts. The formation of tensile residual stress may result in initiation of fatigue cracks, stress corrosion cracking, or other types of fracture. Hence, residual stress and resulting bending need to be controlled during ECAP. Thus, in current study the bending behavior and the residual stress of the work piece in ECAP are analyzed through experimental and finite element analyses by considering the effects of material, geometric, and processing parameters individually. The stress states in the ECAP processed work piece were measured by the non-destructive way using neutron diffraction. Efforts were made to suggest the alternate routes to reduce the residual stress and bending of work piece in ECAP

  4. Surface stress-based biosensors.

    Science.gov (United States)

    Sang, Shengbo; Zhao, Yuan; Zhang, Wendong; Li, Pengwei; Hu, Jie; Li, Gang

    2014-01-15

    Surface stress-based biosensors, as one kind of label-free biosensors, have attracted lots of attention in the process of information gathering and measurement for the biological, chemical and medical application with the development of technology and society. This kind of biosensors offers many advantages such as short response time (less than milliseconds) and a typical sensitivity at nanogram, picoliter, femtojoule and attomolar level. Furthermore, it simplifies sample preparation and testing procedures. In this work, progress made towards the use of surface stress-based biosensors for achieving better performance is critically reviewed, including our recent achievement, the optimally circular membrane-based biosensors and biosensor array. The further scientific and technological challenges in this field are also summarized. Critical remark and future steps towards the ultimate surface stress-based biosensors are addressed. Copyright © 2013 Elsevier B.V. All rights reserved.

  5. Measurements of residual stresses and textures by neutron diffraction

    International Nuclear Information System (INIS)

    Hayashi, Makoto

    2008-01-01

    Many measurement methods of residual stress are compared and characteristic properties of neutron diffraction method are described. The penetration depth of neutron, photon radiation and Cu-Kα ray to metals are compared and the values of neutron are larger than others. Two kinds of measurement methods of residual stress by neutron diffraction, the angular scattering and the time of flight method, are explained. The results of measurement of residual stresses of carbon steel and titanium butt weld joint, Wasploy alloy, aluminum alloy and Incoloy 800 tube in stream generator of nuclear power plant are reported. Neutron diffraction profile of SiCp/Al2024-T6 was measured by TOF method. The textures of Zr-2.5% Nb and SUS316 steel were observed. (S.Y.)

  6. Neutron measurement of residual stresses in a used railway rail

    International Nuclear Information System (INIS)

    Webster, P.J.; Low, K.S.; Mills, G.; Webster, G.A.

    1990-01-01

    The high resolution neutron diffraction technique has been applied to determine, non-destructively, the residual stress distribution developed in the head of a railway rail after normal service. Measurements were made, using the neutron strain scanner at the Institute Laue Langevin, Grenoble, on a transverse slice of rail 12mm thick taken from a section of straight track. The rail head was scanned in the three principal orientations in a series of parallel traverses sufficiently close to enable a two-dimensional matrix of data to be accumulated and vertical, transverse and longitudinal residual stress contours to be drawn. The results demonstrate the effectiveness and unique characteristics of the neutron technique to determine nondestructively and continuously the residual stresses inside engineering components

  7. European standardization activities on residual stress analysis by neutron diffraction

    CERN Document Server

    Youtsos, A G

    2002-01-01

    A main objective of a recently completed European research project, RESTAND - residual stress standard using neutron diffraction, was to develop industrial confidence in the application of the neutron-diffraction technique for residual stress measurement and its principal deliverable was a relevant draft code of practice. In fact this draft standard was jointly developed within RESTAND and VAMAS TWA 20 - an international pre-normative research activity. As no such standard is yet available, on the basis of this draft standard document the European Standards Committee on Non-Destructive Testing (CEN TC/138) has established a new ad hoc Work Group (AHG7). The objective of this group is the development of a European pre-standard on a 'test method for measurement of residual stress by neutron diffraction'. The document contains the proposed protocol for making the measurements. It includes the scope of the method, an outline of the technique, the calibration and measurement procedures recommended, and details of ...

  8. Diffraction plane dependence of elastic constants in residual stress measurement by neutron diffraction

    International Nuclear Information System (INIS)

    Okido, Shinobu; Hayashi, Makoto; Morii, Yukio; Minakawa, Nobuaki; Tsuchiya, Yoshinori

    1997-01-01

    In a residual stress measurement by x-ray diffraction method and a neutron diffraction method, strictly speaking, the strain measurement of various diffracted surface was conducted and it is necessary to use its elastic modulus to convert from the strain to the stress. Then, in order to establish the residual stress measuring technique using neutron diffraction, it is an aim at first to make clear a diffraction surface dependency of elastic modulus for the stress conversion in various alloys. As a result of investigations the diffraction surface dependency of elastic module on SUS304 and STS410 steels by using RESA (Neutron diffractometer for residual stress analysis) installed at JRR-3M in Tokai Establishment of JAERI, following results are obtained. The elastic modulus of each diffraction surface considering till plastic region could be confirmed to be in a region of ±20% of that calculated by Kroner's model and to be useful for that used on conversion to the stress. And, error of this elastic modulus was thought to cause the transition and defect formed at inner portion of the materials due to a plastic deformation. (G.K.)

  9. Residual stresses analysis in ball end milling of nickel-based superalloy Inconel 718

    Energy Technology Data Exchange (ETDEWEB)

    Wang, Junteng; Zhang, Dinghua; Wu, Baohai; Luo, Ming [Key Laboratory of Contemporary Design and Integrated Manufacturing Technology, Northwestern Polytechnical University (China)

    2017-11-15

    Inconel 718 is widely used in the aviation, space, automotive and biomedical industries because of its outstanding properties. Near-surface residual stresses that are induced by ball end milling in Inconel 718 can be crucial for the performance and service time of the machined parts. In this paper, the influences of cutting conditions, including the use of cutting parameters, cutting fluid and spindle angles, on the residual stresses in the ball end milling process of Inconel 718 alloy were investigated experimentally. X-ray diffraction measurements reveal that residual stress distributions are highly influenced by cutting parameters, especially the depth of cut and cutting speed. The milling operation with cooling induces more compressive stresses trend and the magnitude of the residual stresses increases in the tensile direction with the increase of spindle angles. These cutting induced effects were further discussed with respect to thermal- mechanical coupling theory and some observations made by optical microscopy. From this investigation, it is suggested that the machining process parameters are not the smaller the better for the control of residual stresses in the ball end milling process of Inconel 718. (author)

  10. Influence of veneer thickness on residual stress profile in veneering ceramic: measurement by hole-drilling.

    Science.gov (United States)

    Mainjot, Amélie K; Schajer, Gary S; Vanheusden, Alain J; Sadoun, Michaël J

    2012-02-01

    The veneering process of frameworks induces residual stresses and can initiate cracks when combined with functional stresses. The stress distribution within the veneering ceramic as a function of depth is a key factor influencing failure by chipping. This is a well-known problem with Yttria-tetragonal-zirconia-polycrystal based fixed partial dentures. The objective of this study is to investigate the influence of veneer thickness on the stress profile in zirconia- and metal-based structures. The hole-drilling method, often used for engineering measurements, was adapted for use with veneering ceramic. The stress profile was measured in bilayered disc samples of 20 mm diameter, with a 1 mm thick zirconia or metal framework. Different veneering ceramic thicknesses were performed: 1 mm, 1.5 mm, 2 mm, 2.5 mm and 3 mm. All samples exhibited the same type of stress vs. depth profile, starting with compressive at the ceramic surface, decreasing with depth up to 0.5-1.0 mm from the surface, and then becoming compressive again near the framework, except for the 1.5 mm-veneered zirconia samples which exhibited interior tensile stresses. Stresses in the surface of metal samples were not influenced by veneer thickness. Variation of interior stresses at 1.2 mm from the surface in function of veneer thickness was inverted for metal and zirconia samples. Veneer thickness influences in an opposite way the residual stress profile in metal- and in zirconia-based structures. A three-step approach and the hypothesis of the crystalline transformation are discussed to explain the less favorable residual stress development in zirconia samples. Copyright © 2011 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

  11. Residual stresses associated with welds in austenitic steel

    International Nuclear Information System (INIS)

    Fidler, R.

    1978-01-01

    Two exploratory welds have been made with AISI 316 austenitic steel and Armex GT electrodes by the manual metal-arc process, and residual stress measurements made in the as-welded condition and after various periods of stress relief. The results show that substantial stress relief occurs at temperatures of 850 0 and 750 0 C after 1 hr, but is not complete. The stress distributions are compared with those obtained from ferritic welds and the effect of differences in thermal expansion coefficients is examined using finite element analysis. (author)

  12. Residual Stress Distribution and Microstructure of a Multiple Laser-Peened Near-Alpha Titanium Alloy

    Science.gov (United States)

    Umapathi, A.; Swaroop, S.

    2018-04-01

    Laser peening without coating (LPwC) was performed on a Ti-2.5 Cu alloy with multiple passes (1, 3 and 5), using a Nd:YAG laser (1064 nm) at a constant overlap rate of 70% and power density of 6.7 GW cm-2. Hardness and residual stress profiles indicated thermal softening near the surface (hardness (235 HV at 500 μm) and maximum residual stress (- 890 MPa at 100 μm) were observed for LPwC with 1 pass. Surface roughness and surface 3-D topography imaging showed that the surface roughness increased with the increase in the number of passes. XRD results indicated no significant β phases. However, peak shifts, broadening and asymmetry were observed and interpreted based on dislocation activity. Microstructures indicated no melting or resolidification or refinement of grains at the surface. Twin density was found to increase with the increase in the number of passes.

  13. Fatigue life estimation of welded components considering welding residual stress relaxation and its mean stress effect

    International Nuclear Information System (INIS)

    Han, Seung Ho; Han, Jeong Woo; Shin, Byung Chun; Kim, Jae Hoon

    2003-01-01

    The fatigue life of welded joints is sensitive to welding residual stress and complexity of their geometric shapes. To predict the fatigue life more reasonably, the effects of welding residual stress and its relaxation on their fatigue strengths should be considered quantitatively, which are often regarded to be equivalent to the effects of mean stresses by external loads. The hot-spot stress concept should be also adopted which can reduce the dependence of fatigue strengths for various welding details. Considering the factors mentioned above, a fatigue life prediction model using the modified Goodman's diagram was proposed. In this model, an equivalent stress was introduced which is composed of the mean stress based on the hot-spot stress concept and the relaxed welding residual stress. From the verification of the proposed model to real welding details, it is proved that this model can be applied to predict reasonably their fatigue lives

  14. Fatigue life estimation considering welding residual stress and hot-spot stress of welded components

    International Nuclear Information System (INIS)

    Han, S. H.; Lee, T. K.; Shin, B. C.

    2002-01-01

    The fatigue life of welded joints is sensitive to welding residual stress and complexity of their geometric shapes. To predict the fatigue life more reasonably, the effects of welding residual stress and its relaxation have to be considered quantitatively which are equivalent to mean stress by external loads. The hot-spot stress concept should be also adopted which can be reduce the dependence of fatigue strengths for various welding details. Considering the factors mentioned above, a fatigue life prediction model using the modified Goodman's diagram was proposed. In this model, an equivalent stress was introduced which are composed of the mean stress based on the hot-spot stress concept and the relaxed welding residual stress. From the verification of the proposed model to real welding details, it is confirmed that this model can be applied to predict reasonably their fatigue lives

  15. The maximum possible stress intensity factor for a crack in an unknown residual stress field

    International Nuclear Information System (INIS)

    Coules, H.E.; Smith, D.J.

    2015-01-01

    Residual and thermal stress fields in engineering components can act on cracks and structural flaws, promoting or inhibiting fracture. However, these stresses are limited in magnitude by the ability of materials to sustain them elastically. As a consequence, the stress intensity factor which can be applied to a given defect by a self-equilibrating stress field is also limited. We propose a simple weight function method for determining the maximum stress intensity factor which can occur for a given crack or defect in a one-dimensional self-equilibrating stress field, i.e. an upper bound for the residual stress contribution to K I . This can be used for analysing structures containing defects and subject to residual stress without any information about the actual stress field which exists in the structure being analysed. A number of examples are given, including long radial cracks and fully-circumferential cracks in thick-walled hollow cylinders containing self-equilibrating stresses. - Highlights: • An upper limit to the contribution of residual stress to stress intensity factor. • The maximum K I for self-equilibrating stresses in several geometries is calculated. • A weight function method can determine this maximum for 1-dimensional stress fields. • Simple MATLAB scripts for calculating maximum K I provided as supplementary material.

  16. Residual stress characterization of steel TIG welds by neutron diffraction and by residual magnetic stray field mappings

    Science.gov (United States)

    Stegemann, Robert; Cabeza, Sandra; Lyamkin, Viktor; Bruno, Giovanni; Pittner, Andreas; Wimpory, Robert; Boin, Mirko; Kreutzbruck, Marc

    2017-03-01

    The residual stress distribution of tungsten inert gas welded S235JRC+C plates was determined by means of neutron diffraction (ND). Large longitudinal residual stresses with maxima around 600 MPa were found. With these results as reference, the evaluation of residual stress with high spatial resolution GMR (giant magneto resistance) sensors was discussed. The experiments performed indicate a correlation between changes in residual stresses (ND) and the normal component of local residual magnetic stray fields (GMR). Spatial variations in the magnetic field strength perpendicular to the welds are in the order of the magnetic field of the earth.

  17. X-ray diffraction analysis of residual stress in zirconia dental composites

    Science.gov (United States)

    Allahkarami, Masoud

    Dental restoration ceramic is a complex system to be characterized. Beside its essential biocompatibility, and pleasant appearance, it requires being mechanically strong in a catastrophic loading environment. Any design is restricted with geometry boundary and material property limits. Inspired by natural teeth, a multilayer ceramic is a smart way of achieving an enhanced restoration. Bi-layers of zirconia core covered by porcelain are known as one of the best multilayer restorations. Residual stresses may be introduced into a bi-layer dental ceramic restoration during its entire manufacturing process due to thermal expansion and elastic property mismatch. It is impossible to achieve a free of residual stresses bi-layer zirconia-porcelain restoration. The idea is to take the advantage of residual stress in design in such a way to prevent the crack initiation and progression. The hypothesis is a compressive residual stress at external contact surface would be enabling the restoration to endure a greater tensile stress. Optimizing the layers thickness, manufacturing process, and validating 3D simulations require development of new techniques of thickness, residual stresses and phase transformation measurement. In the present work, a combined mirco-tomography and finite element based method were adapted for thickness measurement. Two new 2D X-ray diffraction based techniques were adapted for phase transformation area mapping and combined phase transformation and residual stress measurement. Concerning the complex geometry of crown, an efficient method for X-ray diffraction data collection mapping on a given curved surface was developed. Finally a novel method for 3D dimensional x-ray diffraction data collection and visualization were introduced.

  18. Investigation of residual stress in laser welding between carbon steel AISI 1010 and stainless AISI 304

    International Nuclear Information System (INIS)

    Mirim, Denilson de Camargo

    2011-01-01

    The dissimilar materials union has the residual stress formation as one of the most critical problems, which occurs mainly because these materials have both different thermal expansion coefficients and thermal conductivities. In this study, it was investigated the laser welding technique between steels, AISI 1010 and AISI 304. The materials were joined by butt autogenous welding with a continuous Nd:YAG laser. The main objective was to identify the welding parameters influence by the residual stresses analysis in the heat affected zone (HAZ). It was executed a factorial design with three-factor at two levels with a replica, which were varied power, welding speed and focal position of the laser beam. Residual stress measurements by the diffraction of X-rays were performed on the sample surface, to study their variation as a function of the parameters investigated. The blind hole method was also used to evaluate the residual stress along the samples depth, up to depth of 1mm. Besides residual stress measurement, weld seams were evaluated by optical and scanned electron microscopy, which were aimed to determine the weld geometry and changes in the microstructure. It was also made Vickers hardness measurements to evaluate the extent of HAZ. To evaluate the mechanical properties of the union were performed tensile and fatigue test. The MINITAB 15 software was used to analyze the residual stresses obtained by the blind hole method at different depths of the HAZ. It was also used statistical regression based on both the influences different and the combination of this input factors, in the residual stress of union. The results indicate that the models can satisfactorily predict the responses and provide users a guide to better define the welding parameters. (author)

  19. Residual stress measurement of large scaled welded pipe using neutron diffraction method. Effect of SCC crack propagation and repair weld on residual stress distribution

    International Nuclear Information System (INIS)

    Suzuki, Hiroshi; Katsuyama, Jinya; Tobita, Tohru; Morii, Yukio

    2011-01-01

    The RESA-1 neutron engineering diffractometer in the JRR-3 (Japan Research Reactor No.3) at the Japan Atomic Energy Agency, which is used for stress measurements, was upgraded to realize residual stress measurements of large scaled mechanical components. A series of residual stress measurements was made to obtain through-thickness residual stress distributions in a Type 304 stainless steel butt-welded pipe of 500A-sch.80 using the upgraded RESA-1 diffractometer. We evaluated effects of crack propagation such as stress corrosion cracking (SCC) and a part-circumference repair weld on the residual stress distributions induced by girth welding. Measured residual stress distributions near original girth weld revealed good agreement with typical results shown in some previous works using finite element method, deep hole drilling as well as neutron diffraction. After introducing a mock crack with 10 mm depth in the heat affected zone on the inside wall of the pipe by electro discharge machining, the axial residual stresses were found to be released in the part of the mock crack. However, changes in the through-wall bending stress component and the self-equilibrated stress component were negligible and hence the axial residual stress distribution in the ligament was remained in the original residual stresses near girth weld without the mock crack. Furthermore, changes in hoop and radial residual stress were also small. The residual stress distributions after a part repair welding on the outer circumference of the girth weld were significantly different from residual stress distributions near the original girth weld. The through-thickness average axial residual stress was increased due to increase of the tensile membrane stress and mitigation of the bending stress after repair welding. Throughout above studies, we evidenced that the neutron diffraction technique is useful and powerful tool for measuring residual stress distributions in large as well as thick mechanical

  20. Temperature dependence of residual stress in TiC coated Mo

    International Nuclear Information System (INIS)

    Yoshizawa, I.; Fukutomi, M.; Kamada, K.

    1984-01-01

    The effects of fabrication temperature and heat treatment on the residual stress in TiC coated Mo have been studied by using X-ray diffractometry. TiC coatings on Mo single crystal substrates with (100) and (111) surfaces were carried out with the Activated Reactive Evaporation (ARE) method. It was found that all Mo substrates measured show tensile residual stresses, and their values decrease as the fabrication temperature increases from 300 to 700 0 C. On the other hand, TiC films measured showed compressive residual stresses, for both TiC/Mo(100) and TiC/Mo(111) specimens. These compressive stresses also decreased with increasing the fabrication temperature. The residual stresses measured were higher in TiC/Mo(100) than in TiC/Mo(111). It was found that the compressive stresses in as-grown TiC films change to the tensile stresses after annealing at 1700 0 C for 30 min. The preferred orientations of TiC films were observed to depend on the fabrication temperature. However, no epitaxial growth of TiC films was found as far as the present experiment was concerned. (orig.)

  1. Ultrasonic measurements on residual stress in autofrettged thick walled petroleum pipes

    International Nuclear Information System (INIS)

    Woias, G.; Mizera, J.

    2008-01-01

    The residual stresses in a component or structure are caused by incompatible permanent deformation and related gradient of plastic/elastic strains. They may be generated or modified at every stage in the components life cycle, from original material production to final disposal. Residual stresses can be measured by non-destructive techniques, including X-ray and neutron diffraction, magnetic and ultrasonic methods. The selection of the optimum measurement technique should take account volumetric resolution, material, geometry and access to the component. For large metallic components neutron diffraction is of prime importance as it provides quantitative information on stresses in relatively large volume of methods disregarding its shape complexity. Residual stresses can play a significant role in explaining or preventing failure of components of industrial installations. One example of residual stresses preventing failure are the ones generated by shot peening, inducing surface compressive stresses that improve the fatigue life. Petroleum refinery piping is generally characterized by large-diameters, operated at elevated temperature and under high pressure. Pipelines of a polyethylene plant working in one of the Polish refineries are subjected to pressures exceeding 300 MPa at temperatures above 200 o C. The pipes considered here were pressurized with pressure of 600 MPa. The wall thickness of the pipes is 27 mm and pipe dimensions are 46 x 100 mm. The material is steel with Re=580 MPa. Due to pressurizing, the components retain compressive stresses at the internal surface. These stresses increase resistance to cracking of the pipes. Over the period of exploitation these stresses diminish due to temperature activated relaxation or creep. The purpose of the project is to verify kinetics of such a relaxation process and calibrate alternative methods of their measurements. To avoid stress relaxation, numerical analysis from Finite Element Modelling (FEM)gave an

  2. Investigation of Performance and Residual Stress Generation of AlSi10Mg Processed by Selective Laser Melting

    Directory of Open Access Journals (Sweden)

    Lianfeng Wang

    2018-01-01

    Full Text Available During the selective laser melting (SLM process, the scanned layers are subjected to rapid thermal cycles. By working on the mechanical properties, residual stress, and microstructure, the high-temperature gradients can have significant effect on the proper functioning and the structural integrity of built parts. This work presents a comprehensive study on the scanning path type and preheating temperature for AlSi10Mg alloy during SLM. According to the results, SLM AlSi10Mg parts fabricated in chessboard scanning strategy have higher mechanical properties or at least comparable to the parts fabricated in uniformity scanning strategy. In the SLM processing, the residual stress in different parts of the specimen varies with temperature gradient, and the residual stress at the edge of the specimen is obviously larger than that at the center. Under the chessboard scanning and preheating temperature 160°C, the residual stress in each direction of the specimens reaches the minimum. Under different forming processes, the morphology of the microstructure is obviously different. With the increase of preheating temperature, the molten pool in the side surface is obviously elongated and highly unevenly distributed. From the coupling relationship between the residual stress and microstructure, it can be found that the microstructure of top surface is affected by residual stresses σx and σy. But the side surface is mainly governed by residual stress σy; moreover, the greater the residual stress, the more obvious the grain tilt. In the XY and XZ surfaces, the scanning strategy has little influence on the tilt angle of the grain. But, the tilt angle and morphology of the microstructure are obviously affected by the preheating temperature. The results show that the residual stresses can effectively change the properties of the materials under the combined influence of scanning strategy and preheating temperature.

  3. Modeling of residual stress mitigation in austenitic stainless steel pipe girth weldment

    International Nuclear Information System (INIS)

    Li, M.; Atteridge, D.G.; Anderson, W.E.; West, S.L.

    1994-01-01

    This study provides numerical procedures to model 40-cm-diameter, schedule 40, Type 304L stainless steel pipe girth welding and a newly proposed post-weld treatment. The treatment can be used to accomplish the goal of imparting compressive residual stresses at the inner surface of a pipe girth weldment to prevent/retard the intergranular stress corrosion cracking (IGSCC) of the piping system in nuclear reactors. This new post-weld treatment for mitigating residual stresses is cooling stress improvement (CSI). The concept of CSI is to establish and maintain a certain temperature gradient across the pipe wall thickness to change the final stress state. Thus, this process involves sub-zero low temperature cooling of the inner pipe surface of a completed girth weldment, while simultaneously keeping the outer pipe surface at a slightly elevated temperature with the help of a certain heating method. Analyses to obtain quantitative results on pipe girth welding and CSI by using a thermo-elastic-plastic finite element model are described in this paper. Results demonstrate the potential effectiveness of CSI for introducing compressive residual stresses to prevent/retard IGSCC. Because of the symmetric nature of CSI, it shows great potential for industrial application

  4. Effect of geometric construction on residual stress distribution in designing a nuclear rotor joined by multipass narrow gap welding

    International Nuclear Information System (INIS)

    Tan, Long; Zhang, Linjie; Zhang, Jianxun; Zhuang, Dong

    2014-01-01

    Highlights: • The internal stress of the pipe is measured using local material removal method. • Bottom protrusion at weld seam can release the stress and mitigate stress evolution. The through-wall axial stress is bending type under the effect of the rotor discs. • The impact of geometric construction on the stress evolution begins after pass 15. - Abstract: The purpose of this study is to investigate the effect of geometric construction on the distribution of residual stresses before and after heat treatment in designing a nuclear welded rotor. The local material removal method was used to measure internal residual stress of the experimental pipe after post weld heat treatment. Three finite element models were employed as follows: a model of experimental pipe, a model with a bottom protrusion existed at the weld region, and a model of two rotor discs butt-welded with a bottom protrusion at the weld region. Investigated results showed that the bottom protrusion existed at the weld region can decrease the residual stress and mitigate the stress evolution significantly on the inner surface. Under the binding effect of the rotor discs, the axial stress of inner surface region is compressive stress; the through-wall axial stress at the weld center line can be deemed to a bending type; both the hoop stress and axial stress at the weld center line on the inner surface are compressive. The impact of geometric construction on the stress evolution at the root bead begins after pass 15 deposited

  5. Viscoelastic finite element analysis of residual stresses in porcelain-veneered zirconia dental crowns.

    Science.gov (United States)

    Kim, Jeongho; Dhital, Sukirti; Zhivago, Paul; Kaizer, Marina R; Zhang, Yu

    2018-03-21

    The main problem of porcelain-veneered zirconia (PVZ) dental restorations is chipping and delamination of veneering porcelain owing to the development of deleterious residual stresses during the cooling phase of veneer firing. The aim of this study is to elucidate the effects of cooling rate, thermal contraction coefficient and elastic modulus on residual stresses developed in PVZ dental crowns using viscoelastic finite element methods (VFEM). A three-dimensional VFEM model has been developed to predict residual stresses in PVZ structures using ABAQUS finite element software and user subroutines. First, the newly established model was validated with experimentally measured residual stress profiles using Vickers indentation on flat PVZ specimens. An excellent agreement between the model prediction and experimental data was found. Then, the model was used to predict residual stresses in more complex anatomically-correct crown systems. Two PVZ crown systems with different thermal contraction coefficients and porcelain moduli were studied: VM9/Y-TZP and LAVA/Y-TZP. A sequential dual-step finite element analysis was performed: heat transfer analysis and viscoelastic stress analysis. Controlled and bench convection cooling rates were simulated by applying different convective heat transfer coefficients 1.7E-5 W/mm 2 °C (controlled cooling) and 0.6E-4 W/mm 2 °C (bench cooling) on the crown surfaces exposed to the air. Rigorous viscoelastic finite element analysis revealed that controlled cooling results in lower maximum stresses in both veneer and core layers for the two PVZ systems relative to bench cooling. Better compatibility of thermal contraction coefficients between porcelain and zirconia and a lower porcelain modulus reduce residual stresses in both layers. Copyright © 2018 Elsevier Ltd. All rights reserved.

  6. Residual stress measurements in laser clad repaired low pressure turbine blades for the power industry

    Energy Technology Data Exchange (ETDEWEB)

    Bendeich, P. [Australian Nuclear Science and Technology Organisation, Lucas Heights, Menai, NSW 2234 (Australia)]. E-mail: pbx@ansto.gov.au; Alam, N. [CSIRO Manufacturing Science and Technology, 32 Audley St., Woodville, SA 5011 (Australia); Brandt, M. [IRIS Swinburne University of Technology, 533-545 Burwood Rd., Hawthorne, Vic. 3122 (Australia); Carr, D. [Australian Nuclear Science and Technology Organisation, Lucas Heights, Menai, NSW 2234 (Australia); Short, K. [Australian Nuclear Science and Technology Organisation, Lucas Heights, Menai, NSW 2234 (Australia); Blevins, R. [Australian Nuclear Science and Technology Organisation, Lucas Heights, Menai, NSW 2234 (Australia); Curfs, C. [Australian Nuclear Science and Technology Organisation, Lucas Heights, Menai, NSW 2234 (Australia); Kirstein, O. [Australian Nuclear Science and Technology Organisation, Lucas Heights, Menai, NSW 2234 (Australia); Atkinson, G. [Australian Nuclear Science and Technology Organisation, Lucas Heights, Menai, NSW 2234 (Australia); Holden, T. [Northern Stress Technologies, 20, Pine Point Rd., Deep River, Ont., K0J 1P0 (Canada); Rogge, R. [National Research Council, Neutron Program for Materials Research, Chalk River Laboratories, Chalk River, Ont., KOJ 1JO (Canada)

    2006-11-10

    Low pressure turbine blades in power stations suffer from leading edge erosion damage due to water impingement. In an effort to extend the life of these blades, repair of the eroded regions has been proposed using laser cladding with Stellite material. However, the addition of Stellite results in residual stresses being generated in the parent metal due to contraction during cooling and differences in thermal expansion between the two materials. In this work test coupons and laser clad blades were examined for residual stresses using both the L3 diffractometer at the NRU reactor, Chalk River, Canada and the TASS strain scanner at ANSTO's HIFAR reactor, Lucas Heights, Australia. In addition XRD results were used to measure residual stresses on the surface of the blade to complement the neutron measurements. An FEA model of a simplified weld was used to explain some of the results.

  7. An analytical model to predict and minimize the residual stress of laser cladding process

    Science.gov (United States)

    Tamanna, N.; Crouch, R.; Kabir, I. R.; Naher, S.

    2018-02-01

    Laser cladding is one of the advanced thermal techniques used to repair or modify the surface properties of high-value components such as tools, military and aerospace parts. Unfortunately, tensile residual stresses generate in the thermally treated area of this process. This work focuses on to investigate the key factors for the formation of tensile residual stress and how to minimize it in the clad when using dissimilar substrate and clad materials. To predict the tensile residual stress, a one-dimensional analytical model has been adopted. Four cladding materials (Al2O3, TiC, TiO2, ZrO2) on the H13 tool steel substrate and a range of preheating temperatures of the substrate, from 300 to 1200 K, have been investigated. Thermal strain and Young's modulus are found to be the key factors of formation of tensile residual stresses. Additionally, it is found that using a preheating temperature of the substrate immediately before laser cladding showed the reduction of residual stress.

  8. Modeling of CMUTs with Multiple Anisotropic Layers and Residual Stress

    DEFF Research Database (Denmark)

    Engholm, Mathias; Thomsen, Erik Vilain

    2014-01-01

    Usually the analytical approach for modeling CMUTs uses the single layer plate equation to obtain the deflection and does not take anisotropy and residual stress into account. A highly accurate model is developed for analytical characterization of CMUTs taking an arbitrary number of layers...

  9. Effect of prior machining deformation on the development of tensile residual stresses in weld-fabricated nuclear components

    International Nuclear Information System (INIS)

    Prevey, P.S.; Mason, P.W.; Hornbach, D.J.; Molkenthin, J.P.

    1996-01-01

    Austenitic alloy weldments in nuclear systems may be subject to stress-corrosion cracking (SCC) failure if the sum of residual and applied stresses exceeds a critical threshold. Residual stresses developed by prior machining and welding may either accelerate or retard SCC, depending on their magnitude and sign. A combined x-ray diffraction and mechanical procedure was used to determine the axial and hoop residual stress and yield strength distributions into the inside-diameter surface of a simulated Alloy 600 penetration J-welded into a reactor pressure vessel. The degree of cold working and the resulting yield strength increase caused by prior machining and weld shrinkage were calculated from the line-broadening distributions. Tensile residual stresses on the order of +700 MPa were observed in both the axial and the hoop directions at the inside-diameter surface in a narrow region adjacent to the weld heat-affected zone. Stresses exceeding the bulk yield strength were found to develop due to the combined effects of cold working of the surface layers during initial machining and subsequent weld shrinkage. The residual stress and cold work distributions produced by prior machining were found to influence strongly the final residual stress state developed after welding

  10. Cantilever measurements of surface stress, surface reconstruction, film stress and magnetoelastic stress of monolayersc

    Directory of Open Access Journals (Sweden)

    Jürgen Kirschner

    2008-07-01

    Full Text Available We review the application of cantilever-based stress measurements in surface science and magnetism. The application of thin (thickness appr. 0.1 mm single crystalline substrates as cantilevers has been used successfully to measure adsorbate-induced surface stress changes, lattice misfit induced film stress, and magneto-elastic stress of ferromagnetic monolayers. Surface stress changes as small as 0.01 N/m can be readily measured, and this translates into a sensitivity for adsorbate-coverage well below 0.01 of one layer. Stress as large as several GPa, beyond the elasticity limits of high strength materials, is measured, and it is ascribed to the lattice misfit between film and substrate. Our results point at the intimate relation between surface stress and surface reconstruction, stress-induced structural changes in epitaxially strained films, and strain-induced modifications of the magneto-elastic coupling in ferromagnetic monolayers.

  11. Cantilever measurements of surface stress, surface reconstruction, film stress and magnetoelastic stress of monolayers.

    Science.gov (United States)

    Sander, Dirk; Tian, Zhen; Kirschner, Jürgen

    2008-07-29

    We review the application of cantilever-based stress measurements in surface science and magnetism. The application of thin (thickness appr. 0.1 mm) single crystalline substrates as cantilevers has been used successfully to measure adsorbate-induced surface stress changes, lattice misfit induced film stress, and magneto-elastic stress of ferromagnetic monolayers. Surface stress changes as small as 0.01 N/m can be readily measured, and this translates into a sensitivity for adsorbate-coverage well below 0.01 of one layer. Stress as large as several GPa, beyond the elasticity limits of high strength materials, is measured, and it is ascribed to the lattice misfit between film and substrate. Our results point at the intimate relation between surface stress and surface reconstruction, stress-induced structural changes in epitaxially strained films, and strain-induced modifications of the magneto-elastic coupling in ferromagnetic monolayers.

  12. Method for improve x-ray diffraction determinations of residual stress in nickel-base alloys

    Science.gov (United States)

    Berman, Robert M.; Cohen, Isadore

    1990-01-01

    A process for improving the technique of measuring residual stress by x-ray diffraction in pieces of nickel-base alloys which comprises covering part of a predetermined area of the surface of a nickel-base alloy with a dispersion, exposing the covered and uncovered portions of the surface of the alloy to x-rays by way of an x-ray diffractometry apparatus, making x-ray diffraction determinations of the exposed surface, and measuring the residual stress in the alloy based on these determinations. The dispersion is opaque to x-rays and serves a dual purpose since it masks off unsatisfactory signals such that only a small portion of the surface is measured, and it supplies an internal standard by providing diffractogram peaks comparable to the peaks of the nickel alloy so that the alloy peaks can be very accurately located regardless of any sources of error external to the sample.

  13. Method for improving x-ray diffraction determinations of residual stress in nickel-base alloys

    Science.gov (United States)

    Berman, R.M.; Cohen, I.

    1988-04-26

    A process for improving the technique of measuring residual stress by x-ray diffraction in pieces of nickel-base alloys is discussed. Part of a predetermined area of the surface of a nickel-base alloy is covered with a dispersion. This exposes the covered and uncovered portions of the surface of the alloy to x-rays by way of an x-ray diffractometry apparatus, making x-ray diffraction determinations of the exposed surface, and measuring the residual stress in the alloy based on these determinations. The dispersion is opaque to x-rays and serves a dual purpose, since it masks off unsatisfactory signals such that only a small portion of the surface is measured, and it supplies an internal standard by providing diffractogram peaks comparable to the peaks of the nickel alloy so that the alloy peaks can be very accurately located regardless of any sources of error external to the sample. 2 figs.

  14. Influence of cooling rate on residual stress profile in veneering ceramic: measurement by hole-drilling.

    Science.gov (United States)

    Mainjot, Amélie K; Schajer, Gary S; Vanheusden, Alain J; Sadoun, Michaël J

    2011-09-01

    The manufacture of dental crowns and bridges generates residual stresses within the veneering ceramic and framework during the cooling process. Residual stress is an important factor that control the mechanical behavior of restorations. Knowing the stress distribution within the veneering ceramic as a function of depth can help the understanding of failures, particularly chipping, a well-known problem with Yttria-tetragonal-zirconia-polycrystal based fixed partial dentures. The objective of this study is to investigate the cooling rate dependence of the stress profile in veneering ceramic layered on metal and zirconia frameworks. The hole-drilling method, often used for engineering measurements, was adapted for use with veneering ceramic. The stress profile was measured in bilayered disc samples 20 mm in diameter, with a 0.7 mm thick metal or Yttria-tetragonal-zirconia-polycrystal framework and a 1.5mm thick veneering ceramic. Three different cooling procedures were investigated. The magnitude of the stresses in the surface of the veneering ceramic was found to increase with cooling rate, while the interior stresses decreased. At the surface, compressive stresses were observed in all samples. In the interior, compressive stresses were observed in metal samples and tensile in zirconia samples. Cooling rate influences the magnitude of residual stresses. These can significantly influence the mechanical behavior of metal-and zirconia-based bilayered systems. The framework material influenced the nature of the interior stresses, with zirconia samples showing a less favorable stress profile than metal. Copyright © 2011 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

  15. Characterization of residual stresses generated during inhomogeneous plastic deformation

    DEFF Research Database (Denmark)

    Lorentzen, T.; Faurholdt, T.; Clausen, B.

    1998-01-01

    Residual stresses generated by macroscopic inhomogeneous plastic deformation are predicted by an explicit finite element (FE) technique. The numerical predictions are evaluated by characterizing the residual elastic strains by neutron diffraction using two different (hkl) reflections. Intergranular...... residual elastic strains between subsets of grains are predicted numerically and verified by neutron diffraction. Subsequently, the measured residual strain profiles in the test samples are modified by the intergranular strains and compared to the engineering predictions of the FE technique. Results...... compare well and verify the capability of the numerical technique as well as the possibilities of experimental validation using neutron diffraction. The presented experimental and numerical approach will subsequently be utilized for the evaluation of more complicated plastic deformation processes...

  16. Effectiveness of stress release geometries on reducing residual stress in electroforming metal microstructure

    Science.gov (United States)

    Song, Chang; Du, Liqun; Zhao, Wenjun; Zhu, Heqing; Zhao, Wen; Wang, Weitai

    2018-04-01

    Micro electroforming, as a mature micromachining technology, is widely used to fabricate metal microdevices in micro electro mechanical systems (MEMS). However, large residual stress in the local positions of the micro electroforming layer often leads to non-uniform residual stress distributions, dimension accuracy defects and reliability issues during fabrication of the metal microdevice. To solve this problem, a novel design method of presetting stress release geometries in the topological structure of the metal microstructure is proposed in this paper. First, the effect of stress release geometries (circular shape, annular groove shape and rivet shape) on the residual stress in the metal microstructure was investigated by finite element modeling (FEM) analysis. Two evaluation parameters, stress concentration factor K T and stress non-uniformity factor δ were calculated. The simulation results show that presetting stress release geometries can effectively reduce and homogenize the residual stress in the metal microstructures were measured metal microstructure. By combined use with stress release geometries of annular groove shape and rivet shape, the stress concentration factor K T and the stress non-uniformity factor δ both decreased at a maximum of 49% and 53%, respectively. Meanwhile, the average residual stress σ avg decreased at a maximum of 20% from  -292.4 MPa to  -232.6 MPa. Then, micro electroforming experiments were carried out corresponding to the simulation models. The residual stresses in the metal microstructures were measured by micro Raman spectroscopy (MRS) method. The results of the experiment proved that the stress non-uniformity factor δ and the average residual stress σ avg also decreased at a maximum with the combination use of annular groove shape and rivet shape stress release geometries, which is in agreement with the results of FEM analysis. The stress non-uniformity factor δ has a maximum decrease of 49% and the

  17. Effects of post weld heat treatment and weld overlay on the residual stress and mechanical properties in dissimilar metal weld

    International Nuclear Information System (INIS)

    Campos, Wagner R.C.; Ribeiro, Vladimir S.; Vilela, Alisson H.F.; Almeida, Camila R.O.; Rabello, Emerson G.

    2017-01-01

    The object of this work is a dissimilar metal weld (DMW) pipe joint between carbon steel (A-106 Gr B) and stainless steel (A-312 TP316L) pipes and filler metals of Nickel alloy (82/182), which find wide application in the field of chemical, oil, petroleum industries, fossil fuel and nuclear power plant. A lot of the failures that have occurred in dissimilar metal welded are affected greatly by residual stresses. Residual stress is often a cause of premature failure of critical components under normal operation of welded components. Several methods have been tested and developed for removing the tensile residual stresses. The aim of the methods is to reduce the tensile stress state or to create compressive stresses at a predefined area, such as the inner surface of a welded pipe joint. Post weld heat treatment (PWHT) and weld overlay (WOL) are two of the residual stress mitigation methods which reduce the tensile residual stress, create compressive stresses and arrest crack initiation and crack growth. The technique used to substantially minimized or eliminated this failure development in the root weld is the post weld heat treatments (stress relief heat treatment) or the weld overlay. In this work was studied the effectiveness in reducing internal residual stress in dissimilar metal welded pipe joints subjected to post weld heat treatment and weld overlay, measurement by hole-drilling strain-gage method of stress relaxation. Also held was mechanical characterization of the welded pipe joint itself. (author)

  18. Effects of post weld heat treatment and weld overlay on the residual stress and mechanical properties in dissimilar metal weld

    Energy Technology Data Exchange (ETDEWEB)

    Campos, Wagner R.C.; Ribeiro, Vladimir S.; Vilela, Alisson H.F.; Almeida, Camila R.O.; Rabello, Emerson G., E-mail: wrcc@cdtn.br, E-mail: camilarezende.cr@gmail.com, E-mail: egr@cdtn.br, E-mail: vladimirsoler@hotmail.com, E-mail: ahfv02@outlook.com [Centro de Desenvolvimento da Tecnologia Nuclear (CDTN/CNEN-MG), Belo Horizonte, MG (Brazil)

    2017-07-01

    The object of this work is a dissimilar metal weld (DMW) pipe joint between carbon steel (A-106 Gr B) and stainless steel (A-312 TP316L) pipes and filler metals of Nickel alloy (82/182), which find wide application in the field of chemical, oil, petroleum industries, fossil fuel and nuclear power plant. A lot of the failures that have occurred in dissimilar metal welded are affected greatly by residual stresses. Residual stress is often a cause of premature failure of critical components under normal operation of welded components. Several methods have been tested and developed for removing the tensile residual stresses. The aim of the methods is to reduce the tensile stress state or to create compressive stresses at a predefined area, such as the inner surface of a welded pipe joint. Post weld heat treatment (PWHT) and weld overlay (WOL) are two of the residual stress mitigation methods which reduce the tensile residual stress, create compressive stresses and arrest crack initiation and crack growth. The technique used to substantially minimized or eliminated this failure development in the root weld is the post weld heat treatments (stress relief heat treatment) or the weld overlay. In this work was studied the effectiveness in reducing internal residual stress in dissimilar metal welded pipe joints subjected to post weld heat treatment and weld overlay, measurement by hole-drilling strain-gage method of stress relaxation. Also held was mechanical characterization of the welded pipe joint itself. (author)

  19. Aging of residual surface resistance of superconducting lead cavities

    DEFF Research Database (Denmark)

    Danielsen, M.

    1972-01-01

    Measurements of the residual surface resistance of superconducting lead cavities as a function of time during a period of a month showed an oscillating variation. An explanation of the ageing curves is proposed. ©1972 The American Institute of Physics......Measurements of the residual surface resistance of superconducting lead cavities as a function of time during a period of a month showed an oscillating variation. An explanation of the ageing curves is proposed. ©1972 The American Institute of Physics...

  20. Role of residual stresses induced by double peening on fatigue durability of automotive leaf springs

    International Nuclear Information System (INIS)

    Scuracchio, Bruno Geoffroy; Batista de Lima, Nelson; Schön, Cláudio Geraldo

    2013-01-01

    Highlights: ► Proper choice of peening media is needed for higher fatigue strength in leaf springs. ► Optimum double-peening condition for leaf springs: 0.8 mm shot, followed by 0.3 mm. ► Fatigue life correlates with residual stress levels at the surface (up to 0.02 mm). ► Residual stress profile below 0.02 mm has no measurable effect over fatigue life. ► Failure of the investigated parts is nucleation-controlled. - Abstract: Improvement of fatigue life in parts subjected to cyclic stresses by application of mechanical surface treatment processes is already well known, both in the industry and in the academy. Dealing with automotive springs, the shot peening process becomes an essential step in manufacturing. In the case of leaf springs, however, a systematic investigation of the effect of shot peening on fatigue life is still required. The aim of the present work is to improve the knowledge on the role of shot peening in manufacturing leaf springs for vehicles, through the analysis of residual stresses by X-ray diffraction and fatigue tests on a series of samples that were subject to ten different peening schedules. Among the investigated processes, the usage of 0.8 mm diameter cast steel shot followed by a second peening with 0.3 mm diameter cast steel shot leads to optimal performance, regarding fatigue life. X-ray diffraction analysis shows that this improved performance may be attributed to residual compressive stress maintained until a depth of 0.02 mm below the surface, which directly influences fatigue crack nucleation. Residual stresses induced by shot peening in larger depths have no influence on the sample’s fatigue life

  1. Analysis and measurement of residual stress distribution of vanadium/ceramics joints for fusion reactor applications

    International Nuclear Information System (INIS)

    Nemoto, Y.; Ueda, K.

    1998-01-01

    Vanadium alloys are considered as candidate structural materials for fusion reactor system. When vanadium alloys are used in fusion reactor system, joining with ceramics for insulating is one of material issues to be solved to make component of fusion reactor. In the application of ceramics/metal jointing and coating, residual stress caused by difference of thermal expansion rate between ceramics and metals is an important factor in obtaining good bonding strength and soundness of coating. In this work, residual stress distribution in direct diffusion bonded vanadium/alumina joint (jointing temperature: 1400 C) was measured by small area X-ray diffraction method. And the comparison of finite element method (FEM) analysis and actual stress distribution was carried out. Tensile stress concentration at the edge of the boundary of the joint in alumina was observed. The residual stress concentration may cause cracks in alumina, or failure of bonding. Actually, cracks in alumina caused by thermal stress after bonding at 1500 C was observed. The stress concentration of the joint must be reduced to obtain good bonded joint. Lower bonding temperature or to devise the shape of the outer surface of the joint will reduce the stress concentration. (orig.)

  2. Influence of veneering porcelain thickness and cooling rate on residual stresses in zirconia molar crowns.

    Science.gov (United States)

    Al-Amleh, Basil; Neil Waddell, J; Lyons, Karl; Swain, Michael V

    2014-03-01

    The aim of this study was to investigate the influence of increasing veneering porcelain thickness in clinically representative zirconia molar crowns on the residual stresses under fast and slow cooling protocols. Six veneered zirconia copings (Procera, Nobel Biocare AB, Gothenburg, Sweden) based on a mandibular molar form, were divided into 3 groups with flattened cusp heights that were 1mm, 2mm, or 3mm. Half the samples were fast cooled during final glazing; the other half were slow cooled. Vickers indentation technique was used to determine surface residual stresses. Normality distribution within each sample was done using Kolmogorov-Smirnov & Shapiro-Wilk tests, and one-way ANOVA tests used to test for significance between various cusp heights within each group. Independent t-tests used to evaluate significance between each cusp height group with regards to cooling. Compressive stresses were recorded with fast cooling, while tensile stresses with slow cooling. The highest residual compressive stresses were recorded on the fast cooled 1mm cusps which was significantly higher than the 2 and 3mm fast cooled crowns (Pcrown anatomy have substantially different effects on residual stress profiles with increasing veneering porcelain thickness compared to the basic flat plate model. Copyright © 2013 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

  3. Evaluation of residual stresses in dissimilar weld joints

    International Nuclear Information System (INIS)

    Bonaventure, A.; Ayrault, D.; Montay, G.; Klosek, V.

    2011-01-01

    Dissimilar metal joints between pipes of ferritic and austenitic steels are present in primary coolant circuit of pressurized water reactors. Over the last years in particular in USA and Japan, stress corrosion cracks, often associated with weld repairs, have been observed for some dissimilar welds made with an Inconel filler metal. The integrity of this type of components is thus a major safety issue. In this context, the goal of this work is to evaluate the welding residual stresses field for a dissimilar weld joint. A representative bi-metallic tubular weld joint was fabricated and residual stresses profiles in the different weld zones were evaluated by means of the hole drilling and neutron diffraction methods. (authors)

  4. Residual Stresses in SAVY 4000 and Hagan Container Bodies

    Energy Technology Data Exchange (ETDEWEB)

    Stroud, Mary Ann [Los Alamos National Lab. (LANL), Los Alamos, NM (United States); Hill, Mary Ann [Los Alamos National Lab. (LANL), Los Alamos, NM (United States); Tokash, Justin Charles [Los Alamos National Lab. (LANL), Los Alamos, NM (United States); Forsyth, Robert Thomas [Los Alamos National Lab. (LANL), Los Alamos, NM (United States); Hyer, Holden Christopher [Los Alamos National Lab. (LANL), Los Alamos, NM (United States)

    2017-11-02

    Chloride-induced stress corrosion cracking (SCC) has been investigated as a potential failure mechanism for the SAVY 4000 and the Hagan containers used to store plutonium-bearing materials at Los Alamos National Laboratory. This report discusses the regions of the container bodies most susceptible to SCC and the magnitude of the residual stresses in those regions. Boiling MgCl2 testing indicated that for both containers the region near the top weld was most susceptible to SCC. The Hagan showed through wall cracking after 22-24 hours of exposure both parallel (axial stresses) and perpendicular (hoop stresses) to the weld. The SAVY 4000 container showed significant cracking above and below the weld after 47 hours of exposure but there was no visual evidence of a through wall crack and the cracks did not leak water. Two through wall holes formed in the bottom of the SAVY 4000 container after 44-46 hours of exposure. For both containers, average “through wall” residual stresses were determined from hole drilling data 4 mm below the weld. In the Hagan body, average tensile hoop stresses were 194 MPa and average compressive axial stresses were -120 MPa. In the SAVY 4000 body, average compressive hoop stresses were 11 MPa and average tensile axial stresses were 25 MPa. Results suggest that because the Hagan container exhibited through wall cracking in a shorter time in boiling MgCl2 and had the higher average tensile stress, 194 MPa hoop stress, it is more susceptible to SCC than the SAVY 4000 container.

  5. Analysis of residual stress in the resin of metal-resin adhesion structures by scanning acoustic microscopy.

    Science.gov (United States)

    Ohno, Hiroki; Endo, Kazuhiko; Nagano-Takebe, Futami; Ida, Yusuke; Kakino, Ken; Narita, Toshio

    2013-01-01

    The residual stress caused by polymerization shrinkage and thermal contraction of a heat-curing resin containing 4-META on a metal-resin structure was measured by a scanning acoustic microscope. The tensile residual stress in the resin occurred within 70 µm of the adhesion interface with a flat plate specimen. The maximum tensile stress was about 58 MPa at the interface. On a metal plate specimen with retention holes, ring-like cracks in the resin occurred around the retention holes with the adhesive specimen and many linear cracks occurred in the resin vertical to the longitudinal direction of the metal frame with the non-adhesive specimens. There was tensile residual stress on the resin surface at the center of the retention holes of the adhesion specimen, indicating that the stress in the specimen with surface treatment for adhesion was higher than in that without surface treatment.

  6. Welding residual stress estimation by inherent strain analysis and thermal elastic plastic analysis and its verification using neutron diffraction measurement

    International Nuclear Information System (INIS)

    Mochizuki, Masahito; Hayashi, Makoto; Hattori, Toshio

    1997-01-01

    The internal residual stress distribution that resulted from welding a 4-inch-diameter carbon-steel pipe butt-joint was evaluated using several methods and the results were compared. The analytical evaluation methods used were inherent strain analysis and thermal elastic plastic analysis, and the experimental methods were X-ray diffraction and strain gauge for the surface residual stress, and neutron diffraction for the internal stress. The residual stress distributions determined using the various methods agreed well with each other, both for surface stress and internal stress. The characteristics of the evaluation methods were summarized and it was found the most suitable method for any particular situation can be selected by considering the evaluated location and the operating conditions of the object to be evaluated. (author)

  7. Development and Applications of Residual Stress Measurements Using Neutron Beams

    International Nuclear Information System (INIS)

    2014-01-01

    The deep penetration and selective absorption of neutrons make them a powerful tool for the non-destructive testing of large samples of material or large objects. Residual stress that is formed in a material during manufacturing, welding, utilization or repair can be measured by means of neutron diffraction. In fact, neutron diffraction is the only non-destructive testing method which can facilitate three dimensional mapping of residual stress in a bulk component. Stress measurement using neutron beams is a technique that enables this kind of high quality non-destructive investigation, and provides insight into the material strain and stress state deep within engineering components and structures under various conditions representative of those which might be experienced in service. Such studies are of importance to improve the quality of industrial components in production and to optimize design criteria in applications. Anisotropies in macroscopic properties such as thermal and electrical conductivities, for instance of fuel elements, and mechanical properties of materials depend on the textures developed during their preparation or thermal treatment. Such textures also can be studied using neutron diffraction techniques. There is currently substantial scientific and industrial demand for high quality non-destructive residual stress measurements, and the continuing competitive drive to optimize performance and minimize weight in many applications indicates that this demand will continue to grow. As such, the neutron diffraction technique is an increasingly important tool for mechanical and materials engineering in the search for improved manufacturing processes to reduce stress and distortion. Considering this trend, and in accordance with its purpose of promoting the peaceful use of nuclear applications, in 2006-2009 the IAEA organized a Coordinated Research Project on the Development and Application of the Techniques of Residual Stress Measurements in Materials

  8. Residual stresses in a stainless steel - titanium alloy joint made with the explosive technique

    Science.gov (United States)

    Taran, Yu V.; Balagurov, A. M.; Sabirov, B. M.; Evans, A.; Davydov, V.; Venter, A. M.

    2012-02-01

    Joining of pipes from stainless steel (SS) and titanium (Ti) alloy still experience serious technical problems. Recently, reliable and hermetic joining of SS and Ti pipes has been achieved with the explosive bonding technique in the Russian Federal Nuclear Center. Such adapters are earmarked for use at the future International Linear Collider. The manufactured SS-Ti adapters have excellent mechanical behavior at room and liquid nitrogen temperatures, during high-pressure tests and thermal cycling. We here report the first neutron diffraction investigation of the residual stresses in a SS-Ti adapter on the POLDI instrument at the SINQ spallation source. The strain scanning across the adapter walls into the SS-SS and SS-Ti pipes sections encompassed measurement of the axial, radial and hoop strain components, which were transformed into residual stresses. The full stress information was successfully determined for the three steel pipes involved in the joint. The residual stresses do not exceed 300 MPa in magnitude. All stress components have tensile values close to the adapter internal surface, whilst they are compressive close to the outer surface. The strong incoherent and weak coherent neutron scattering cross-sections of Ti did not allow for the reliable determination of stresses inside the titanic pipe.

  9. Residual stresses in a stainless steel – titanium alloy joint made with the explosive technique

    International Nuclear Information System (INIS)

    Taran, Yu V; Balagurov, A M; Sabirov, B M; Evans, A; Davydov, V; Venter, A M

    2012-01-01

    Joining of pipes from stainless steel (SS) and titanium (Ti) alloy still experience serious technical problems. Recently, reliable and hermetic joining of SS and Ti pipes has been achieved with the explosive bonding technique in the Russian Federal Nuclear Center. Such adapters are earmarked for use at the future International Linear Collider. The manufactured SS-Ti adapters have excellent mechanical behavior at room and liquid nitrogen temperatures, during high-pressure tests and thermal cycling. We here report the first neutron diffraction investigation of the residual stresses in a SS-Ti adapter on the POLDI instrument at the SINQ spallation source. The strain scanning across the adapter walls into the SS-SS and SS-Ti pipes sections encompassed measurement of the axial, radial and hoop strain components, which were transformed into residual stresses. The full stress information was successfully determined for the three steel pipes involved in the joint. The residual stresses do not exceed 300 MPa in magnitude. All stress components have tensile values close to the adapter internal surface, whilst they are compressive close to the outer surface. The strong incoherent and weak coherent neutron scattering cross-sections of Ti did not allow for the reliable determination of stresses inside the titanic pipe.

  10. An Evaluation on the Residual Stresses Induced by EFR Welding of CEDM Nozzle

    Energy Technology Data Exchange (ETDEWEB)

    Lee, Sang Ho; Park, Gi Yeol; Kim, Tae Ryong [KEPCO International Nuclear Graduate School, Ulsan (Korea, Republic of)

    2015-10-15

    In this paper, carried out the welding analysis to use the SYSWELD as welding interpretation code based on the reactor upper head nozzle. In this paper, evaluated the residual stress in CEDM nozzle by EFR through the SYSWELD which is the welding interpretation code. The conclusion are same as below. 1) When comparing with Hoop Stress and Axial Stress by J-Groove and EFR, after welding residual stress by EFR is lower than after J-Groove. 2) After EFR, it was confirmed that the tensile stress is reduced after increasing over the point3. The PWSCC of Dissimilar Metal Zone of reactor can degrade the integrity of the main device in nuclear power plant, and according to the power plant stopped for inspection, it can cause an enormous amount of lost sales when the crack is occurred. Various methods have been developed to reduce residual stress to prevent the PWSCC like Weld Overlay (WOL), Mechanical Stress Improvement Process (Msp), Laser Peening, Inlay Weld, etc. Among them, Wol is the most commonly used welding method in nuclear power plant. When performing a Wol, structure rigidity will be increase, and residual stress of welding zone will be changed into compressive stress from the tensile stress. This has the advantage that improved resistance to PWSCC. The most commonly used material in nuclear power plant is Inconel 600. Inconel 600 consist of a Ni-Cr-Fe and it has 14-17% of Cr content, 10% of Fe content and susceptible to PWSCC. The more Cr content is more stronger against PWSCC. Inconel 690 which has 2 times more Cr content than Inconel 600 has very strong resistance to PWSCC than Inconel 600. Embedded Flaw Repair (EFR) has been developed in Westinghouse by 1994. The welding metal with high corrosion resistance is embedded on the surface of component, and could protect cracking part from the PWSCC. It is permanent repair method that isolates the flaw from the environment, eliminating further crack propagation due to PWSCC. EFR method is that at least three layers

  11. An Evaluation on the Residual Stresses Induced by EFR Welding of CEDM Nozzle

    International Nuclear Information System (INIS)

    Lee, Sang Ho; Park, Gi Yeol; Kim, Tae Ryong

    2015-01-01

    In this paper, carried out the welding analysis to use the SYSWELD as welding interpretation code based on the reactor upper head nozzle. In this paper, evaluated the residual stress in CEDM nozzle by EFR through the SYSWELD which is the welding interpretation code. The conclusion are same as below. 1) When comparing with Hoop Stress and Axial Stress by J-Groove and EFR, after welding residual stress by EFR is lower than after J-Groove. 2) After EFR, it was confirmed that the tensile stress is reduced after increasing over the point3. The PWSCC of Dissimilar Metal Zone of reactor can degrade the integrity of the main device in nuclear power plant, and according to the power plant stopped for inspection, it can cause an enormous amount of lost sales when the crack is occurred. Various methods have been developed to reduce residual stress to prevent the PWSCC like Weld Overlay (WOL), Mechanical Stress Improvement Process (Msp), Laser Peening, Inlay Weld, etc. Among them, Wol is the most commonly used welding method in nuclear power plant. When performing a Wol, structure rigidity will be increase, and residual stress of welding zone will be changed into compressive stress from the tensile stress. This has the advantage that improved resistance to PWSCC. The most commonly used material in nuclear power plant is Inconel 600. Inconel 600 consist of a Ni-Cr-Fe and it has 14-17% of Cr content, 10% of Fe content and susceptible to PWSCC. The more Cr content is more stronger against PWSCC. Inconel 690 which has 2 times more Cr content than Inconel 600 has very strong resistance to PWSCC than Inconel 600. Embedded Flaw Repair (EFR) has been developed in Westinghouse by 1994. The welding metal with high corrosion resistance is embedded on the surface of component, and could protect cracking part from the PWSCC. It is permanent repair method that isolates the flaw from the environment, eliminating further crack propagation due to PWSCC. EFR method is that at least three layers

  12. Influence of cold rolling and fatigue on the residual stress state of a metal matrix composite

    International Nuclear Information System (INIS)

    Hanus, E.; Ericsson, T.; Lu, J.; Decomps, F.

    1993-01-01

    The large difference in the coefficient of thermal expansion between the matrix alloy and the particle in a metal matrix composite gives rise to residual stresses in the material. In the present work the effect of cold rolling and four-point bending fatigue on the residual stress state of a silicon carbide particle reinforced aluminium alloy (AA 2014) has been investigated. The three dimensional stress state measured in both phases: matrix and reinforcement, has been determined by using an X-ray diffraction technique. It was found that cold rolling induces surface compressive macrostresses of about -250 MPa, with a penetration depth around 2 mm. The absolute values of the pseudomacrostresses in both phases are significantly reduced due to the single track rolling. Stress relaxation occurs during four-point bending fatigue. (orig.)

  13. Residual strain and stress measurements by neutron diffraction in the industry

    International Nuclear Information System (INIS)

    Hayashi, Makoto

    2011-01-01

    The residual stress remarkably affects fracture strength, fatigue strength and stress corrosion cracking. It is very much important to measure the residual stresses in the materials in order to secure the reliability of structure. One of the big characteristics of neutron is large penetration depth. This feature enables to measure the residual strain or stress inside of structural components and machine parts. In this paper, several industrial applications of residual stress and strain measurements by neutron diffraction would be introduced. (author)

  14. Residual stress distribution of a 6061-T6 aluminum alloy under shear deformation

    Energy Technology Data Exchange (ETDEWEB)

    Reyes-Ruiz, C.; Figueroa, I.A. [Instituto de Investigaciones en Materiales, Universidad Nacional Autónoma de México, Circuito exterior S/N, Cd. Universitaria, A.P. 70-360, Coyoacán C.P. 04510 (Mexico); Braham, C. [Laboratoire Procédés et Ingénierie Mécanique et Matériaux, CNRS UMR 8006, ENSAM-CNAM, 151, Bd de l’Hôpital, 75013 Paris (France); Cabrera, J.M. [Departamento de Ciencia de los Materiales e Ingeniería Metalúrgica, ETSEIB-Universidad Politécnica de Cataluña, Av Diagonal 647, 08028 Barcelona (Spain); Fundació CTM Centre Tecnológic, Pl. de la Ciencia 2, 08243 Manresa (Spain); Zanellato, O.; Baiz, S. [Laboratoire Procédés et Ingénierie Mécanique et Matériaux, CNRS UMR 8006, ENSAM-CNAM, 151, Bd de l’Hôpital, 75013 Paris (France); Gonzalez, G., E-mail: joseggr@unam.mx [Instituto de Investigaciones en Materiales, Universidad Nacional Autónoma de México, Circuito exterior S/N, Cd. Universitaria, A.P. 70-360, Coyoacán C.P. 04510 (Mexico)

    2016-07-18

    There is a lack of information with regards to the friction effect in ECAPed aluminum alloys, even though it might substantially modify the deformation at the surface. In this work, the friction effect at the surface and the deformation heterogeneity in the ECAPed aluminum alloy 6061-T6 were characterized. X-Ray diffraction was used to determine residual stresses (RS) on the sample surface. The volumetric sections were characterized by Synchrotron diffraction at ESRF beamline ID15B (Grenoble, France). It was found that the microhardness mapping and residual stress results showed a good agreement with the finite element analysis for the first layer studied. Minor strain variation, Δd/d as a function of (hkl) planes, for the different analyzed sections was found. The study also showed that there was an incomplete symmetry in the residual stress near the surface, even at up to a depth of 400 µm. The regions with higher deformation were found to be at the top and bottom parts of the sample, while the central region showed stress variations of up to 50 MPa.

  15. Stress and Fatigue Life Modeling of Cannon Breech Closures Including Effects of Material Strength and Residual Stress

    National Research Council Canada - National Science Library

    Underwood, John

    2000-01-01

    ...; overload residual stress. Modeling of applied and residual stresses at the location of the fatigue failure site is performed by elastic-plastic finite element analysis using ABAQUS and by solid...

  16. BOOK REVIEW: Analysis of Residual Stress by Diffraction Using Neutron and Synchrotron Radiation

    Science.gov (United States)

    Fitzpatrick, ed M. E.; Lodini, A.

    2003-09-01

    The presence of residual stresses within engineering components is often a key feature in determining their usable lifetimes and failure characteristics. Residual surface compression can, for example, restrict the propagation of surface cracks through the bulk. As a consequence, it is essential to characterize the magnitude and spatial distribution of residual stresses and, at least for non-destructive testing, this is most widely achieved using diffraction of neutron and high energy synchrotron radiations. This book aims to provide a detailed description of the methodology used to determine residual stresses. The major emphasis is placed on the neutron method, this being the more widely established approach at present. It contains 20 chapters contributed by 23 authors, divided into five major parts. The overall layout is very logical, with the first part giving a general introduction to the use of neutrons and x-rays for materials research and summarizing the methods used for their production. Part 2 considers the more specific aspects of extracting the residual stress distribution within a bulk sample and includes some valuable comments on a number of potential experimental problems, such as the determination of the stress-free lattice parameter and the effects of broadening of the Bragg peaks. The experimental facilities currently available or under development are described in part 3, with the remaining two parts devoted to general and specific applications of the residual stress measurement technique. As expected with such a large number of different authors, there is some variation in style and quality. However, the text is generally easy to follow and, more importantly, it is largely free of the problems of inconsistent notation and dupication of material that can afflict multi-authored texts. My only negative comment concerns the latter portion of the book devoted to specific applications of the technique, which is illustrative rather than comprehensive. In

  17. The Effect of Weld Residual Stress on Life of Used Nuclear Fuel Dry Storage Canisters

    Energy Technology Data Exchange (ETDEWEB)

    Ronald G. Ballinger; Sara E. Ferry; Bradley P. Black; Sebastien P. Teysseyre

    2013-08-01

    With the elimination of Yucca Mountain as the long-term storage facility for spent nuclear fuel in the United States, a number of other storage options are being explored. Currently, used fuel is stored in dry-storage cask systems constructed of steel and concrete. It is likely that used fuel will continue to be stored at existing open-air storage sites for up to 100 years. This raises the possibility that the storage casks will be exposed to a salt-containing environment for the duration of their time in interim storage. Austenitic stainless steels, which are used to construct the canisters, are susceptible to stress corrosion cracking (SCC) in chloride-containing environments if a continuous aqueous film can be maintained on the surface and the material is under stress. Because steel sensitization in the canister welds is typically avoided by avoiding post-weld heat treatments, high residual stresses are present in the welds. While the environment history will play a key role in establishing the chemical conditions for cracking, weld residual stresses will have a strong influence on both crack initiation and propagation. It is often assumed for modeling purposes that weld residual stresses are tensile, high and constant through the weld. However, due to the strong dependence of crack growth rate on stress, this assumption may be overly conservative. In particular, the residual stresses become negative (compressive) at certain points in the weld. The ultimate goal of this research project is to develop a probabilistic model with quantified uncertainties for SCC failure in the dry storage casks. In this paper, the results of a study of the residual stresses, and their postulated effects on SCC behavior, in actual canister welds are presented. Progress on the development of the model is reported.

  18. Residual Stresses in Porcelain-veneered Zirconia Prostheses

    Science.gov (United States)

    Baldassarri, Marta; Stappert, Christian F. J.; Wolff, Mark S.; Thompson, Van P.; Zhang, Yu

    2012-01-01

    Objectives Compressive stress has been intentionally introduced into the overlay porcelain of zirconia-ceramic prostheses to prevent veneer fracture. However, recent theoretical analysis has predicted that the residual stresses in the porcelain may be also tensile in nature. This study aims to determine the type and magnitude of the residual stresses in the porcelain veneers of full-contour fixed-dental prostheses (FDPs) with an anatomic zirconia coping design and in control porcelain with the zirconia removed using a well-established Vickers indentation method. Methods Six 3-unit zirconia FDPs were manufactured (NobelBiocare, Gothenburg, Sweden). Porcelain was hand-veneered using a slow cooling rate. Each FDP was sectioned parallel to the occlusal plane for Vickers indentations (n = 143; load = 9.8 N; dwell time = 5 s). Tests were performed in the veneer of porcelain-zirconia specimens (bilayers, n = 4) and porcelain specimens without zirconia cores (monolayers, n = 2). Results The average crack lengths and standard deviation, in the transverse and radial directions (i.e. parallel and perpendicular to the veneer/core interface, respectively), were 67 ± 12 μm and 52 ± 8 μm for the bilayers and 64 ± 8 μm and 64 ± 7 μm for the monolayers. These results indicated a major hoop compressive stress (~40 to 50 MPa) and a moderate radial tensile stress (~10 MPa) in the bulk of the porcelain veneer. Significance Vickers indentation is a powerful method to determine the residual stresses in veneered zirconia systems. Our findings revealed the presence of a radial tensile stress in the overlay porcelain, which may contributed to the large clinical chip fractures observed in these prostheses. PMID:22578663

  19. The influence of texture on residual stress measurements

    International Nuclear Information System (INIS)

    Lima, N.B. de.

    1991-01-01

    A computer program to calculate the orientation distribution function (ODF) from incomplete pole figures has been developed for rolled materials with a cubic structure. This program is based on Bunge's series expansion. The use of incomplete pole figures results in the loss of orthogonality among symmetric spherical harmonic functions and makes it necessary to explicitly evaluate the integrals. The ODF has been used to quantitatively evaluate the influence of texture in determining residual stresses. This has been done by calculating theoretically the strain undergone by each cell as a function of its orientation to residual stress relationship. To test the ODF program, cold rolled Cu and Al specimens were used and to evaluate residual stresses as a function of texture, cold rolled AISI 430 and 324 specimens were used. Simulations have also be presented based on the texture for each of the materials, to verify the nature of the curve d x sin 2 ψ as a function of each stress tensor components. (author)

  20. Stress distribution prevents ischaemia and bone resorption in residual ridge.

    Science.gov (United States)

    Maruo, Yukinori; Nishigawa, Goro; Irie, Masao; Oka, Morihiko; Hara, Tetsuya; Suzuki, Kazuomi; Minagi, Shogo

    2010-11-01

    Intensive mechanical stress and/or inflammation are known to induce alveolar bone resorption. This study investigated whether a distribution of mechanical stress would reduce residual ridge resorption or improve ischaemia. Thirty rats were divided into six experimental groups (n=5). The control group received no intentional stimulation, but rats in the experimental groups wore denture stimulators made of acrylic resin or a soft lining material. The stimulator transmitted masticatory pressure to the rats' palates for four weeks. The four types of soft lining materials investigated in this study dispersed the applied pressure, with compressive stress ranging from 20.8 to 90.8kPa. Volumes of blood flow and bone resorption of denture foundations were measured every week for 4 weeks. Statistical evaluation of these results was performed using two-way ANOVA and Holm-Sidak test within 5% error limits. Non-viscoelastic material clearly induced bone resorption and ischaemia of denture foundations, while viscoelastic materials reduced these phenomena to different extents according to their viscoelastic properties. Ischaemia in the alveolar ridge preceded residual ridge resorption, because the amount of residual ridge resorption and blood flow rate showed a simple linear regression. Animal model of this study suggested that a distribution or reduction of mechanical stress could improve blood flow and decrease alveolar ridge resorption. Copyright © 2010 Elsevier Ltd. All rights reserved.

  1. European standardization activities on residual stress analysis by neutron diffraction

    International Nuclear Information System (INIS)

    Youtsos, A.G.; Ohms, C.

    2002-01-01

    A main objective of a recently completed European research project, RESTAND - residual stress standard using neutron diffraction, was to develop industrial confidence in the application of the neutron-diffraction technique for residual stress measurement and its principal deliverable was a relevant draft code of practice. In fact this draft standard was jointly developed within RESTAND and VAMAS TWA 20 - an international pre-normative research activity. As no such standard is yet available, on the basis of this draft standard document the European Standards Committee on Non-Destructive Testing (CEN TC/138) has established a new ad hoc Work Group (AHG7). The objective of this group is the development of a European pre-standard on a 'test method for measurement of residual stress by neutron diffraction'. The document contains the proposed protocol for making the measurements. It includes the scope of the method, an outline of the technique, the calibration and measurement procedures recommended, and details of how the strain data should be analysed to calculate stresses and establish the reliability of the results obtained. (orig.)

  2. European standardization activities on residual stress analysis by neutron diffraction

    Science.gov (United States)

    Youtsos, A. G.; Ohms, C.

    A main objective of a recently completed European research project, RESTAND - residual stress standard using neutron diffraction, was to develop industrial confidence in the application of the neutron-diffraction technique for residual stress measurement and its principal deliverable was a relevant draft code of practice. In fact this draft standard was jointly developed within RESTAND and VAMAS TWA 20 - an international pre-normative research activity. As no such standard is yet available, on the basis of this draft standard document the European Standards Committee on Non-Destructive Testing (CEN TC/138) has established a new ad hoc Work Group (AHG7). The objective of this group is the development of a European pre-standard on a `test method for measurement of residual stress by neutron diffraction'. The document contains the proposed protocol for making the measurements. It includes the scope of the method, an outline of the technique, the calibration and measurement procedures recommended, and details of how the strain data should be analysed to calculate stresses and establish the reliability of the results obtained.

  3. Neutron diffraction measurements of residual stresses in a 50 mm thick weld

    International Nuclear Information System (INIS)

    Woo, Wanchuck; Em, Vyacheslav; Mikula, Pavel; An, Gyu-Baek; Seong, Baek-Seok

    2011-01-01

    Research highlights: → Determined residual stresses through the thickness of the 50 mm thick weld. → Two-dimensional mapping of the longitudinal stress. Observed significant stresses along the heat-affected zone. → Measured the maximum stress of 460 MPa at 40 mm below from the top surface. - Abstract: Residual stresses were determined through the thickness of a 50 mm thick ferrite steel weld plate using neutron diffraction. Whereas the limiting penetration depth for iron-based alloys is about 25 mm in the most typical neutron diffractometers, we significantly enhanced the penetration depth up to 50 mm with 2 mm spatial resolution by using the neutron wavelength of 2.39 A. The selected wavelength minimizes the total neutron cross-section and beam attenuation, thereby, maximizes the neutron fluxes at depth. Two-dimensional mapping of the residual stresses shows that significant amounts of the tensile longitudinal stresses (over 90% of yield strength) were developed along the heat-affected zone of the weld.

  4. Optical properties and residual stress in aluminum nitride films prepared by alternating-current dual reactive magnetron sputtering.

    Science.gov (United States)

    Tang, Chien-Jen; Jaing, Cheng-Chung; Lee, Kun-Hsien; Lee, Cheng-Chung

    2011-05-01

    Aluminum nitride films were deposited by alternating-current dual reactive magnetron sputtering. The influence of different nitrogen flow and working pressures at a sputtering power of 5 kW on the refractive index, extinction coefficient, crystalline structure, residual stress, and surface roughness of aluminum nitride films was discussed. The aluminum nitride film would have high refractive index, low extinction coefficient and small residual stress at suitable nitrogen flow rate and low working pressure.

  5. Effects of ion implantation on the microstructure and residual stress of filter arc CrN films

    International Nuclear Information System (INIS)

    Weng, K.-W.; Chen, Y.-C.; Han Sheng; Hsu, C.-S.; Chen, Y.-L.; Wang, D.-Y.

    2008-01-01

    Chromium nitride coatings were deposited using a hybrid physical vapor deposition (PVD) system containing a filter arc deposition (FAD) and a metal plasma ion implantation source (MPII). Exactly how surface residual stress affects film characteristics is investigated using glancing incident X-ray diffraction (GIXRD) and pole figure analyses. Compared with unimplanted CrN, implanted carbon typically increases compressive residual stress and hardness. Wear resistance was also improved by implanted carbon

  6. Evaluation of residual stresses in metal matrix composite materials, by the means of neutron and X-ray diffraction

    International Nuclear Information System (INIS)

    Ceretti, M.; Braham, C.

    1996-01-01

    Thermally- as well as mechanically-induced residual stresses in metal matrix composites have been analyzed by the means of two complementary techniques: X-ray diffraction for surface analysis, and neutron diffraction for volume analysis. The residual stress relaxation is examined through in-situ measurements with neutron diffraction. Results from both techniques are well correlated, on condition that the same basic assumptions are used

  7. Residual stresses and fatigue in a duplex stainless steel

    International Nuclear Information System (INIS)

    Johansson, Johan

    1999-01-01

    Duplex stainless steels, consisting of approximately equal amounts of austenite and ferrite, often combine the best features of austenitic and ferritic stainless steels. They generally have good mechanical properties, including high strength and ductility, and the corrosion resistance is often better than conventional austenitic grades. This has lead to a growing use of duplex stainless steels as a material in mechanically loaded constructions. However, detailed knowledge regarding its mechanical properties and deformation mechanisms are still lacking. In this thesis special emphasis has been placed on the residual stresses and their influence on mechanical behaviour of duplex stainless steels. Due to the difference in coefficient of thermal expansion between the two phases, tensile microstresses are found in the austenitic phase and balancing compressive microstresses in the ferritic phase. The first part of this thesis is a literature survey, which will give an introduction to duplex stainless steels and review the fatigue properties of duplex stainless steels and the influence of residual stresses in two-phase material. The second part concerns the evolution of the residual stress state during uniaxial loading. Initial residual stresses were found to be almost two times higher in the transverse direction compared to the rolling direction. During loading the absolute value of the microstresses increased in the macroscopic elastic regime but started to decrease with increasing load in the macroscopic plastic regime. A significant increase of the microstresses was also found to occur during unloading. Finite element simulations also show stress variation within one phase and a strong influence of both the elastic and plastic anisotropy of the individual phases on the simulated stress state. In the third part, the load sharing between the phases during cyclic loading is studied. X-ray diffraction stress analysis and transmission electron microscopy show that even if

  8. Residual stresses and fatigue in a duplex stainless steel

    Energy Technology Data Exchange (ETDEWEB)

    Johansson, Johan

    1999-05-01

    Duplex stainless steels, consisting of approximately equal amounts of austenite and ferrite, often combine the best features of austenitic and ferritic stainless steels. They generally have good mechanical properties, including high strength and ductility, and the corrosion resistance is often better than conventional austenitic grades. This has lead to a growing use of duplex stainless steels as a material in mechanically loaded constructions. However, detailed knowledge regarding its mechanical properties and deformation mechanisms are still lacking. In this thesis special emphasis has been placed on the residual stresses and their influence on mechanical behaviour of duplex stainless steels. Due to the difference in coefficient of thermal expansion between the two phases, tensile microstresses are found in the austenitic phase and balancing compressive microstresses in the ferritic phase. The first part of this thesis is a literature survey, which will give an introduction to duplex stainless steels and review the fatigue properties of duplex stainless steels and the influence of residual stresses in two-phase material. The second part concerns the evolution of the residual stress state during uniaxial loading. Initial residual stresses were found to be almost two times higher in the transverse direction compared to the rolling direction. During loading the absolute value of the microstresses increased in the macroscopic elastic regime but started to decrease with increasing load in the macroscopic plastic regime. A significant increase of the microstresses was also found to occur during unloading. Finite element simulations also show stress variation within one phase and a strong influence of both the elastic and plastic anisotropy of the individual phases on the simulated stress state. In the third part, the load sharing between the phases during cyclic loading is studied. X-ray diffraction stress analysis and transmission electron microscopy show that even if

  9. Residual stress evaluation in the vicinity of ceramic coating interface using polychromatic X-ray method

    Energy Technology Data Exchange (ETDEWEB)

    Shibano, Jun-ichi; Ukai, Takayoshi; Tadano, Shigeru [Hokkaido Univ., Sapporo (Japan). Faculty of Engineering; Todoh, Masahiro

    1995-06-01

    This paper presents a polychromatic X-ray method for nondestructive evaluation of residual stress distributed in the vicinity of the interface between a ceramic coating layer and a substrate metal. Since the strain is assumed to be a linear function of the depth, the strain distribution along the depth direction can be obtained from the weighted mean strain equation calculated by considering the intensity of diffracted X-rays over the penetration depth. Therefore, the distribution along the depth direction of the residual stress was determined by the strain distributions in two directions: the vertical direction and the inclined direction to the surface. SUS316 coated with TiN by the PVD process was used as the specimen. The residual stress distributions in the coating layer and the substrate of the specimen were evaluated using this method. As a result, not only compressive residual stress in the coating layer but also the stress gradient in the substrate could be confirmed simultaneously and nondestructively. (author).

  10. Residual Stresses in a NiCrY-Coated Powder Metallurgy Disk Superalloy

    Science.gov (United States)

    Gabb, Timothy P.; Rogers, Richard B.; Nesbitt, James A.; Puleo, Bernadette J.; Miller, Robert A.; Telesman, Ignacy; Draper, Susan L.; Locci, Ivan E.

    2017-01-01

    Protective ductile coatings will be necessary to mitigate oxidation and corrosion attack on superalloy disks exposed to increasing operating temperatures in some turbine engine environments. However, such coatings must be resistant to harmful surface cracking during service. The objective of this study was to investigate how residual stresses evolve in such coatings. Cylindrical gage fatigue specimens of powder metallurgy-processed disk superalloy LSHR were coated with a NiCrY coating, shot peened, and then subjected to fatigue in air at room and high temperatures. The effects of shot peening and fatigue cycling on average residual stresses and other aspects of the coating were assessed. Shot peening did induce beneficial compressive residual stresses in the coating and substrate. However, these stresses became more tensile in the coating with subsequent heating and contributed to cracking of the coating in long intervals of cycling at 760 C. Substantial compressive residual stresses remained in the substrate adjacent to the coating, sufficient to suppress fatigue cracking. The coating continued to protect the substrate from hot corrosion pitting, even after fatigue cracks initiated in the coating.

  11. Weld residual stress predictions in reactor vessel head penetrations

    Energy Technology Data Exchange (ETDEWEB)

    Suanno, Rodolfo L.M.; Ferrari, Lucio D.B. [ELETROBRAS Termonuclear S.A. - ELETRONUCLEAR, Rio de Janeiro, RJ (Brazil). Stress Analysis Department], e-mail: rsuanno@eletronuclear.gov.br; Teughels, Anne; Malekian, Christian [Tractebel Engineering, Brussels (Belgium). Reliability Nuclear Department], e-mail: anne.teughels@tractebel.com

    2009-07-01

    The penetrations in the early Pressurized Water Reactors Vessels are characterized by Alloy 600 tubes, welded by Alloy 182/82. The Alloy 600 tubes have been shown to be susceptible to PWSCC (Primary Water Stress Corrosion Cracking) which may lead to crack forming. The cracking mechanism is driven mainly by the welding residual stress and, in a second place, by the operational stress in the weld region. It is therefore of big interest to quantify the weld residual stress field correctly. In this paper the weld residual stress field is calculated by finite elements using a sequentially coupled approach, which is well known in literature. It includes a transient thermal analysis simulating the heating during the multipass welding, followed by a transient thermo-mechanical analysis for the determination of the stresses involved with it. The welding consists of a sequence of weld beads, each of which is deposited in its entirety, at once, instead of gradually. Central as well as eccentric sidehill nozzles on the vessel head are analyzed in the paper. For the former a 2- dimensional axisymmetrical finite element model is used, whereas for the latter a 3-dimensional model is set up. Different positions on the vessel head are compared and the influence of the sidehill effect is illustrated. In the framework of a common project for Angra 1, Tractebel Engineering (Belgium) and ELETRONUCLEAR (Nuclear Utility, Brazil) had the opportunity to compare their analysis method, which they applied to the Belgian and the Brazilian nuclear reactors, respectively. The global approach in both cases is very similar but is applied to different configurations, specific for each plant. In the article the results of both cases are compared. (author)

  12. Residual stress measurements by X-ray and neutron diffractions in heat-treated SiCw/A2014 composites

    International Nuclear Information System (INIS)

    Ohnuki, Takahisa; Fujita, Motoo; Tomota, Yo; Ono, Masayoshi

    1998-01-01

    Residual stresses due to various heat treatments in a 22 volume percent SiC whisker/A2014 metal matrix composite (MMC) were measured by using X-ray and neutron diffractions. Micro residual stresses generated from the differences in thermal expansion coefficients of the constituents and macro residual stresses associated with different cooling rates in the outer and inner regions of an MMC specimen must be distinguished in X-ray stress measurements. The conventional sin 2 ψ method under an assumption of plane stress condition has been found not to be applicable to the present MMC, because interactions among whiskers in the X-ray penetrating area yields σ 33 where the x 3 -axis is normal with respect to specimen's surface. An average value of σ 33 can be measured by X-ray diffraction technique, but does not seem enough to evaluate micro residual stresses. It is found that neutron diffraction is the most powerful method to measure micro residual stresses in the constituents. Elastic residual strains obtained by neutron diffraction in solution treated or T6 heat treated samples show good agreements with predictions calculated by using Eshelby inclusion theory coupled with the Mori-Tanaka mean field concept, indicating that the influence of stress relaxation is negligible. In addition, internal stresses relaxations during holding at room temperature, slow cooling from solution treatment temperature, or subzero cooling are discussed. (author)

  13. Opportunities for inelastic neutron scattering and residual stress measurements

    International Nuclear Information System (INIS)

    Hagen, M.; Studer, A.J.; Cussen, L.; Kirstein, O.

    2003-01-01

    Full text: The Triple Axis Spectrometer (TAS) at the HIFAR reactor has recently undergone a major refurbishment consisting of the replacement of the motors and motor control system, the construction of a sample table with XYZ translation, modification of the analyser system and the installation of a multiwire position sensitive detector. This has enabled its use for both inelastic neutron scattering and residual stress measurements. This instrument will provide a facility for such fields of work within Australia until the installation of a new state-of-the-art TAS and Residual Stress diffractometer at the Replacement Research Reactor. In this talk we will describe the capabilities of the refurbished TAS and how it fits into the overall picture of neutron scattering facilities available, at present and in the future, to the Australian science community

  14. Neutron diffraction measurements of residual stresses in NPP construction materials

    International Nuclear Information System (INIS)

    Hinca, R.; Bokuchava, G.

    2001-01-01

    Neutron diffraction is one of the most powerful methods for condensed matter studies. This method is used for non-destructive determination of residual stresses in material. The fundamental aspects of neutron diffraction are discussed, together with a brief description of the experimental facility. The principal advantage of using neutrons rather than the more conventional X-rays is the fact that neutron can penetrate deeply (2-4 cm for steel and more than 10 cm for aluminium) into metals to determine internal parameters within the bulk of materials. We present results of measurements residual stresses in NPP construction material - austenitic stainless steel (Cr-18%, Ni-10%, Ti-1%) coated with high-nickel alloy. (authors)

  15. Residual stress investigations by neutron diffraction at JRC-Petten

    Science.gov (United States)

    Youtsos, A. G.; Ohms, C.; Timke, Th.

    1997-02-01

    Reliable estimates of residual stresses based on non-destructive testing techniques have recently become an essential requirement for the efficient design of advanced materials. Over the last ten years the neutron scattering technique has been recognized as a powerful tool in the characterization of such materials. In this paper we briefly describe the neutron diffraction facilities at the high flux reactor (HFR) at Petten. Experimental data on two specimens are next presented. For the first specimen, an austenitic steel ring exhibiting sharp residual stress gradients, our findings, are compared against similar data obtained elsewhere. For the second specimen, a metal/ceramic composite, the test data, are compared against numerical results derived by numerical modelling of the composite's manufacturing process.

  16. Modeling of plates with multiple anisotropic layers and residual stress

    DEFF Research Database (Denmark)

    Engholm, Mathias; Pedersen, Thomas; Thomsen, Erik Vilain

    2016-01-01

    , and an excellent agreement between the two models is seen with a relative difference of less than 2% for all calculations. The model was also used to extract the cell capacitance, the parasitic capacitance and the residual stress of a pressure sensor composed of a multilayered plate of silicon and silicon oxide....... The extracted values were in good agreement with the expected and it showed that the behavior of devices with a plate could easily be predicted with a low uncertainty....

  17. Measurement of residual stress in a sphere by x-ray under the consideration of its penetration depth

    International Nuclear Information System (INIS)

    Doi, Osamu; Ukai, Takayoshi

    1981-01-01

    It was pointed out in the case of a plate that when stress gradient is large, the use of the X-ray with large penetration depth caused large measurement error. In this paper, the theoretical equations for measuring the residual stress in a sphere with X-ray, taking penetration depth into account, are proposed, and the example of application is shown. As the method of measuring the residual stress in a hollow sphere with X-ray, only the method of combining external surface removal and external surface irradiation is practically in use. It was assumed that a sphere is isotropic, and that the residual stress is a function of the radius only. First, the theory of measuring the residual stress in a sphere with X-ray taking penetration depth into account is explained, and the equations for calculating the residual stresses in tangential and radial directions are derived. As the example of applying this theory, the distribution of the residual stress in a steel ball for a ball bearing was measured with Cr characteristic X-ray. The ball of 30 mm diameter was made of high-carbon chromium bearing steel, grade 2, (JIS SUJ2) and quenched and tempered. The removal of the thin layer was made by chemical etching and electrolysis. The measured values and the calculated values are shown. (Kako, I.)

  18. Effect of laser shock peening on residual stress and fatigue life of clad 2024 aluminium sheet containing scribe defects

    International Nuclear Information System (INIS)

    Dorman, M.; Toparli, M.B.; Smyth, N.; Cini, A.; Fitzpatrick, M.E.; Irving, P.E.

    2012-01-01

    Highlights: ► Effect of laser peen intensity on local residual stress fields in 2024 aluminium. ► Peening induces significant changes in surface topography and local hardness. ► Residual stress at peen spot centre in tension, spot overlap in compression. ► Notched fatigue lives increased; crack morphology correlated to residual stress field. ► Large peening power densities can cause fatigue life reduction in notched samples. - Abstract: Laser peening at a range of power densities has been applied to 2 mm-thick sheets of 2024 T351 aluminium. The induced residual stress field was measured using incremental hole drilling and synchrotron X-ray diffraction techniques. Fatigue samples were subjected to identical laser peening treatments followed by scribing at the peen location to introduce stress concentrations, after which they were fatigue tested. The residual stresses were found to be non-biaxial: orthogonal to the peen line they were tensile at the surface, moving into the desired compression with increased depth. Regions of peen spot overlap were associated with large compression strains; the centre of the peen spot remaining tensile. Fatigue lives showed moderate improvement over the life of unpeened samples for 50 μm deep scribes, and slight improvement for samples with 150 μm scribes. Use of the residual stress intensity K resid approach to calculate fatigue life improvement arising from peening was unsuccessful at predicting the relative effects of the different peening treatments. Possible reasons for this are explored.

  19. Engineered Surfaces for Mitigation of Insect Residue Adhesion

    Science.gov (United States)

    Siochi, Emilie J.; Smith, Joseph G.; Wohl, Christopher J.; Gardner, J. M.; Penner, Ronald K.; Connell, John W.

    2013-01-01

    Maintenance of laminar flow under operational flight conditions is being investigated under NASA s Environmentally Responsible Aviation (ERA) Program. Among the challenges with natural laminar flow is the accretion of residues from insect impacts incurred during takeoff or landing. Depending on air speed, temperature, and wing structure, the critical residue height for laminar flow disruption can be as low as 4 microns near the leading edge. In this study, engineered surfaces designed to minimize insect residue adhesion were examined. The coatings studied included chemical compositions containing functional groups typically associated with abhesive (non-stick) surfaces. To reduce surface contact by liquids and enhance abhesion, the engineered surfaces consisted of these coatings doped with particulate additives to generate random surface topography, as well as coatings applied to laser ablated surfaces having precision patterned topographies. Performance evaluation of these surfaces included contact angle goniometry of pristine coatings and profilometry of surfaces after insect impacts were incurred in laboratory scale tests, wind tunnel tests and flight tests. The results illustrate the complexity of designing antifouling surfaces for effective insect contamination mitigation under dynamic conditions and suggest that superhydrophobic surfaces may not be the most effective solution for preventing insect contamination on aircraft wing leading edges.

  20. Stress-Softening and Residual Strain Effects in Suture Materials

    Directory of Open Access Journals (Sweden)

    Alex Elías-Zúñiga

    2013-01-01

    Full Text Available This work focuses on the experimental characterization of suture material samples of MonoPlus, Monosyn, polyglycolic acid, polydioxanone 2–0, polydioxanone 4–0, poly(glycolide-co-epsilon-caprolactone, nylon, and polypropylene when subjected to cyclic loading and unloading conditions. It is found that all tested suture materials exhibit stress-softening and residual strain effects related to the microstructural material damage upon deformation from the natural, undistorted state of the virgin suture material. To predict experimental observations, a new constitutive material model that takes into account stress-softening and residual strain effects is developed. The basis of this model is the inclusion of a phenomenological nonmonotonous softening function that depends on the strain intensity between loading and unloading cycles. The theory is illustrated by modifying the non-Gaussian average-stretch, full-network model to capture stress-softening and residual strains by using pseudoelasticity concepts. It is shown that results obtained from theoretical simulations compare well with suture material experimental data.

  1. On the thermally-induced residual stresses in thick fiber-thermoplastic matrix (PEEK) cross-ply laminated plates

    Science.gov (United States)

    Hu, Shoufeng; Nairn, John A.

    1992-01-01

    An analytical method for calculating thermally-induced residual stresses in laminated plates is applied to cross-ply PEEK laminates. We considered three cooling procedures: slow cooling (uniform temperature distribution); convective and radiative cooling; and rapid cooling by quenching (constant surface temperature). Some of the calculated stresses are of sufficient magnitude to effect failure properties such as matrix microcracking.

  2. Characterization of residual stress as a function of friction stir welding parameters in oxide dispersion strengthened (ODS) steel MA956

    Energy Technology Data Exchange (ETDEWEB)

    Brewer, L.N., E-mail: lnbrewer1@eng.ua.edu [Naval Postgraduate School (United States); Bennett, M.S.; Baker, B.W. [Naval Postgraduate School (United States); Payzant, E.A.; Sochalski-Kolbus, L.M. [Oak Ridge National Laboratory (United States)

    2015-10-28

    Friction stir welding (FSW) can generate large residual stresses during solid state joining of oxide dispersion strengthened steels. In this work, a plate of MA956 steel was friction stir welded at three conditions: 500 rpm/25 mm per minute (mmpm), 400 rpm/50 mmpm and 400 rpm/100 mmpm. The residual stresses across these welds were measured using both x-ray and neutron diffraction techniques. The distribution and magnitude of the residual stresses agreed well between the two techniques. Longitudinal residual stresses up to eighty percent of the yield strength were observed for the 400 rpm/100 mmpm condition. The surface residual stresses were somewhat larger on the root side of the weld than on the crown side. Increases in the relative heat input during FSW decreased the measured residual stresses in the stir zone and the thermomechanically affected zone (TMAZ). Increasing the traverse rate while holding the rotational speed fixed increased the residual stress levels. The fatigue strength of the material is predicted to decrease by at least twenty percent with cracking most likely in the TMAZ.

  3. Characterization of residual stress as a function of friction stir welding parameters in oxide dispersion strengthened (ODS) steel MA956

    International Nuclear Information System (INIS)

    Brewer, L.N.; Bennett, M.S.; Baker, B.W.; Payzant, E.A.; Sochalski-Kolbus, L.M.

    2015-01-01

    Friction stir welding (FSW) can generate large residual stresses during solid state joining of oxide dispersion strengthened steels. In this work, a plate of MA956 steel was friction stir welded at three conditions: 500 rpm/25 mm per minute (mmpm), 400 rpm/50 mmpm and 400 rpm/100 mmpm. The residual stresses across these welds were measured using both x-ray and neutron diffraction techniques. The distribution and magnitude of the residual stresses agreed well between the two techniques. Longitudinal residual stresses up to eighty percent of the yield strength were observed for the 400 rpm/100 mmpm condition. The surface residual stresses were somewhat larger on the root side of the weld than on the crown side. Increases in the relative heat input during FSW decreased the measured residual stresses in the stir zone and the thermomechanically affected zone (TMAZ). Increasing the traverse rate while holding the rotational speed fixed increased the residual stress levels. The fatigue strength of the material is predicted to decrease by at least twenty percent with cracking most likely in the TMAZ.

  4. Membranes fabricated with a deep single corrugation for package stress reduction and residual stress relief

    NARCIS (Netherlands)

    Spiering, V.L.; Spiering, V.L.; Bouwstra, S.; Bouwstra, S.; Burger, Johannes Faas; Elwenspoek, Michael Curt

    1993-01-01

    Thin square membranes including a deep circular corrugation are realized and tested for application in a strain-based pressure sensor. Package-induced stresses are reduced and relief of the residual stress is obtained, resulting in a larger pressure sensitivity and a reduced temperature sensitivity.

  5. Residual stress of diffusion bonded aluminum-to-stainless steel joins. Final report

    Energy Technology Data Exchange (ETDEWEB)

    Stroud, R.D.; Shackelford, J.F.

    1980-09-01

    An x-ray method for determination of residual stress as a function of surface position on a metal sample is described. This method is capable of spatial resolution on the order of 0.040 inch (1 mm) and precision positioning of the sample along three orthogonal axes to better than 0.001 inch. A high precision sample holder was designed and fabricated for this purpose. Apparent residual stress was found to be a strong function of sample position with respect to the axis of rotation of the diffractometer circle. This relationship is on the order of 400 to 500 Kpsi/inch for aluminum. The high precision sample holder allowed careful centering of the sample providing true (rather than apparent) residual stress measurements in the range of low stresses (less than 10 Ksi). Comparison was made between applied stress values obtained with strain gage output and those obtained by x-ray diffraction. Correlation was good with the accuracy of stress measurements being approximately +-500 psi.

  6. Effects of LSP on micro-structures and residual stresses in a 4 mm CLAM steel weld joints

    Energy Technology Data Exchange (ETDEWEB)

    Chen, Xizhang, E-mail: chenxizhang@wzu.edu.cn [School of Mechanical and Electrical Engineering, Wenzhou University., Wenzhou 325035 (China); School of Materials Science and Engineering, Jiangsu University, Zhenjiang 212013, Jiangsu (China); Fang, Yuanyuan [School of Materials Science and Engineering, Jiangsu University, Zhenjiang 212013, Jiangsu (China); Zhang, Shuyan; Kelleher, Joe F. [ISIS, Rutherford Appleton Laboratory, Chilton, Didcot OX11 0QX (United Kingdom); Zhou, Jianzhong [School of Mechanical Engineering, Jiangsu University, Zhenjiang 212013, Jiangsu (China)

    2015-05-15

    The effects of laser shock processing (LSP) on the distribution of residual stress and micro-structure of China Low Activation Martensitic (CLAM) steel weldment were investigated via neutron diffraction and optical microscope (OM). A pair of 4 mm CLAM steel plates joined by GTA welding. Special attention is paid to the generation of high level compressive residual stresses introduced by LSP. Residual stress in longitudinal, normal and transversal direction at weldment surface and longitudinal stress through thickness are evaluated via neutron diffraction. Compressive residual stress after LSP occurred at more than 90% areas within the weld joint, it is almost double the areas of compressive stress compare to weldment surface before LSP. The maximum compressive normal residual stress becomes to −183 MPa after LSP from −63 MPa before LSP. The Modification of surface micro-structures including weld zone (WZ), heat affected zone (HAZ) and base metal (BM) are also discussed. Results to date demonstrate that laser shock processing has been a great potential method for the improvement of mechanical performance of components.

  7. Effects of LSP on micro-structures and residual stresses in a 4 mm CLAM steel weld joints

    International Nuclear Information System (INIS)

    Chen, Xizhang; Fang, Yuanyuan; Zhang, Shuyan; Kelleher, Joe F.; Zhou, Jianzhong

    2015-01-01

    The effects of laser shock processing (LSP) on the distribution of residual stress and micro-structure of China Low Activation Martensitic (CLAM) steel weldment were investigated via neutron diffraction and optical microscope (OM). A pair of 4 mm CLAM steel plates joined by GTA welding. Special attention is paid to the generation of high level compressive residual stresses introduced by LSP. Residual stress in longitudinal, normal and transversal direction at weldment surface and longitudinal stress through thickness are evaluated via neutron diffraction. Compressive residual stress after LSP occurred at more than 90% areas within the weld joint, it is almost double the areas of compressive stress compare to weldment surface before LSP. The maximum compressive normal residual stress becomes to −183 MPa after LSP from −63 MPa before LSP. The Modification of surface micro-structures including weld zone (WZ), heat affected zone (HAZ) and base metal (BM) are also discussed. Results to date demonstrate that laser shock processing has been a great potential method for the improvement of mechanical performance of components

  8. Influence of Hardening Model on Weld Residual Stress Distribution

    International Nuclear Information System (INIS)

    Mullins, Jonathan; Gunnars, Jens

    2009-06-01

    This study is the third stage of a project sponsored by the Swedish Radiation Safety Authority (SSM) to improve the weld residual stress modelling procedures currently used in Sweden. The aim of this study was to determine which material hardening model gave the best agreement with experimentally measured weld residual stress distributions. Two girth weld geometries were considered: 19mm and 65mm thick girth welds with Rin/t ratios of 10.5 and 2.8, respectively. The FE solver ABAQUS Standard v6.5 was used for analysis. As a preliminary step some improvements were made to the welding simulation procedure used in part one of the project. First, monotonic stress strain curves and a mixed isotropic/kinematic hardening model were sourced from the literature for 316 stainless steel. Second, more detailed information was obtained regarding the geometry and welding sequence for the Case 1 weld (compared with phase 1 of this project). Following the preliminary step, welding simulations were conducted using isotropic, kinematic and mixed hardening models. The isotropic hardening model gave the best overall agreement with experimental measurements; it is therefore recommended for future use in welding simulations. The mixed hardening model gave good agreement for predictions of the hoop stress but tended to under estimate the magnitude of the axial stress. It must be noted that two different sources of data were used for the isotropic and mixed models in this study and this may have contributed to the discrepancy in predictions. When defining a mixed hardening model it is difficult to delineate the relative contributions of isotropic and kinematic hardening and for the model used it may be that a greater isotropic hardening component should have been specified. The kinematic hardening model consistently underestimated the magnitude of both the axial and hoop stress and is not recommended for use. Two sensitivity studies were also conducted. In the first the effect of using a

  9. Welding residual stress distributions for dissimilar metal nozzle butt welds in pressurized water reactors

    Energy Technology Data Exchange (ETDEWEB)

    Kim, Ji Soo; Kim, Ju Hee; Bae, Hong Yeol; OH, Chang Young; Kim, Yun Jae [Korea Univ., Seoul (Korea, Republic of); Lee, Kyungsoo [Korea Electric Power Research Institute, Daejeon (Korea, Republic of); Song, Tae Kwang [Korea Institute of Nuclear Safety, Daejeon (Korea, Republic of)

    2012-02-15

    In pressurized water nuclear reactors, dissimilar metal welds are susceptible to primary water stress corrosion cracking. To access this problem, accurate estimation of welding residual stresses is important. This paper provides general welding residual stress profiles in dissimilar metal nozzle butt welds using finite element analysis. By introducing a simplified shape for dissimilar metal nozzle butt welds, changes in the welding residual stress distribution can be seen using a geometry variable. Based on the results, a welding residual stress profile for dissimilar metal nozzle butt welds is proposed that modifies the existing welding residual stress profile for austenitic pipe butt welds.

  10. Residual stress alleviation of aircraft metal structures reinforced with filamentary composites

    Science.gov (United States)

    Kelly, J. B.; June, R. R.

    1973-01-01

    Methods to eliminate or reduce residual stresses in aircraft metal structures reinforced by filamentary composites are discussed. Residual stress level reductions were achieved by modifying the manufacturing procedures used during adhesive bonding. The residual stress alleviation techniques involved various forms of mechanical constraint which were applied to the components during bonding. Nine methods were evaluated, covering a wide range in complexity. All methods investigated during the program affected the residual stress level. In general, residual stresses were reduced by 70 percent or more from the stress level produced by conventional adhesive bonding procedures.

  11. Residual stress characterization of steel TIG welds by neutron diffraction and by residual magnetic stray field mappings

    International Nuclear Information System (INIS)

    Stegemann, Robert; Cabeza, Sandra; Lyamkin, Viktor; Bruno, Giovanni; Pittner, Andreas; Wimpory, Robert; Boin, Mirko; Kreutzbruck, Marc

    2017-01-01

    The residual stress distribution of tungsten inert gas welded S235JRC+C plates was determined by means of neutron diffraction (ND). Large longitudinal residual stresses with maxima around 600 MPa were found. With these results as reference, the evaluation of residual stress with high spatial resolution GMR (giant magneto resistance) sensors was discussed. The experiments performed indicate a correlation between changes in residual stresses (ND) and the normal component of local residual magnetic stray fields (GMR). Spatial variations in the magnetic field strength perpendicular to the welds are in the order of the magnetic field of the earth. - Highlights: • Comparison of magnetic microstructure with neutron diffraction stress analysis. • High spatial resolution magnetic stray field images of hypereutectoid TIG welds. • Spatial variations of the stray fields are below the magnetic field of the earth. • GMR spin valve gradiometer arrays adapted for the evaluation of magnetic microstructures. • Magnetic stray fields are closely linked to microstructure of the material.

  12. Residual stress characterization of steel TIG welds by neutron diffraction and by residual magnetic stray field mappings

    Energy Technology Data Exchange (ETDEWEB)

    Stegemann, Robert, E-mail: Robert.Stegemann@bam.de [Bundesanstalt für Materialforschung und -prüfung (BAM), Unter den Eichen 87, 12200 Berlin (Germany); Cabeza, Sandra; Lyamkin, Viktor; Bruno, Giovanni; Pittner, Andreas [Bundesanstalt für Materialforschung und -prüfung (BAM), Unter den Eichen 87, 12200 Berlin (Germany); Wimpory, Robert; Boin, Mirko [HZB Helmholtz-Zentrum Berlin, Hahn-Meitner-Platz 1, 14109 Berlin (Germany); Kreutzbruck, Marc [Bundesanstalt für Materialforschung und -prüfung (BAM), Unter den Eichen 87, 12200 Berlin (Germany); IKT, University of Stuttgart, Pfaffenwaldring 32, 70569 Stuttgart (Germany)

    2017-03-15

    The residual stress distribution of tungsten inert gas welded S235JRC+C plates was determined by means of neutron diffraction (ND). Large longitudinal residual stresses with maxima around 600 MPa were found. With these results as reference, the evaluation of residual stress with high spatial resolution GMR (giant magneto resistance) sensors was discussed. The experiments performed indicate a correlation between changes in residual stresses (ND) and the normal component of local residual magnetic stray fields (GMR). Spatial variations in the magnetic field strength perpendicular to the welds are in the order of the magnetic field of the earth. - Highlights: • Comparison of magnetic microstructure with neutron diffraction stress analysis. • High spatial resolution magnetic stray field images of hypereutectoid TIG welds. • Spatial variations of the stray fields are below the magnetic field of the earth. • GMR spin valve gradiometer arrays adapted for the evaluation of magnetic microstructures. • Magnetic stray fields are closely linked to microstructure of the material.

  13. Neutron diffraction measurements of residual stress in a powder metallurgy component

    International Nuclear Information System (INIS)

    Schneider, L.C.R.; Hainsworth, S.V.; Cocks, A.C.F.; Fitzpatrick, M.E.

    2005-01-01

    Residual stresses in a typical industrial green component were determined using neutron diffraction. The measured residual stresses were found to correlate with cross-sectional variations. Residual stress at the edge of the compact in contact with the die wall during compaction reached up to +80 MPa (tension) and -100 MPa (compression)

  14. Principles of the measurement of residual stress by neutron diffraction

    Energy Technology Data Exchange (ETDEWEB)

    Webster, G.A.; Ezeilo, A.N. [Imperial Coll. of Science and Technology, London (United Kingdom). Dept. of Mechanical Engineering

    1996-11-01

    The presence of residual stresses in engineering components can significantly affect their load carrying capacity and resistance to fracture. In order to quantify their effect it is necessary to know their magnitude and distribution. Neutron diffraction is the most suitable method of obtaining these stresses non-destructively in the interior of components. In this paper the principles of the technique are described. A monochromatic beam of neutrons, or time of flight measurements, can be employed. In each case, components of strain are determined directly from changes in the lattice spacings between crystals. Residual stresses can then be calculated from these strains. The experimental procedures for making the measurements are described and precautions for achieving reliable results discussed. These include choice of crystal planes on which to make measurements, extent of masking needed to identify a suitable sampling volume, type of detector and alignment procedure. Methods of achieving a stress free reference are also considered. A selection of practical examples is included to demonstrate the success of the technique. (author) 14 figs., 1 tab., 18 refs.

  15. Mapping residual and internal stress in materials by neutron diffraction

    International Nuclear Information System (INIS)

    Withers, Ph.J.

    2007-01-01

    Neutron diffraction provides one of the few means of mapping residual stresses deep within the bulk of materials and components. This article reviews the basic scientific methodology by which internal strains and stresses are inferred from recorded diffraction peaks. Both conventional angular scans and time-of-flight measurements are reviewed and compared. Their complementarity with analogous synchrotron X-ray methods is also highlighted. For measurements to be exploited in structural integrity calculations underpinning the safe operation of engineering components, measurement standards have been defined and the major findings are summarised. Examples are used to highlight the unique capabilities of the method showing how it can provide insights ranging from the basic physics of slip mechanisms in hexagonal polycrystalline materials, through the materials optimisation of stress induced transformations in smart nano-materials, to the industrial introduction of novel friction welding processes exploiting stress residual measurements transferred from prototype sub-scale tests to the joining of full-scale aero-engine assemblies. (author)

  16. Mapping residual and internal stress in materials by neutron diffraction

    Science.gov (United States)

    Withers, Philip J.

    2007-09-01

    Neutron diffraction provides one of the few means of mapping residual stresses deep within the bulk of materials and components. This article reviews the basic scientific methodology by which internal strains and stresses are inferred from recorded diffraction peaks. Both conventional angular scans and time-of-flight measurements are reviewed and compared. Their complementarity with analogous synchrotron X-ray methods is also highlighted. For measurements to be exploited in structural integrity calculations underpinning the safe operation of engineering components, measurement standards have been defined and the major findings are summarised. Examples are used to highlight the unique capabilities of the method showing how it can provide insights ranging from the basic physics of slip mechanisms in hexagonal polycrystalline materials, through the materials optimisation of stress induced transformations in smart nanomaterials, to the industrial introduction of novel friction welding processes exploiting stress residual measurements transferred from prototype sub-scale tests to the joining of full-scale aeroengine assemblies. To cite this article: P.J. Withers, C. R. Physique 8 (2007).

  17. Quantification of Residual Stress from Photonic Signatures of Fused Silica

    Science.gov (United States)

    Cramer, K. Elliott; Hayward, Maurice; Yost, William E.

    2013-01-01

    A commercially available grey-field polariscope (GFP) instrument for photoelastic examination is used to assess impact damage inflicted upon the outer-most pane of Space Shuttle windows made from fused silica. A method and apparatus for calibration of the stress-optic coefficient using four-point bending is discussed. The results are validated on known material (acrylic) and are found to agree with literature values to within 6%. The calibration procedure is then applied to fused-silica specimens and the stress-optic coefficient is determined to be 2.43 +/- 0.54 x 10(exp -12)/Pa. Fused silica specimens containing impacts artificially made at NASA's Hypervelocity Impact Technology Facility (HIT-F), to simulate damage typical during space flight, are examined. The damage sites are cored from fused silica window carcasses and examined with the GFP. The calibrated GFP measurements of residual stress patterns surrounding the damage sites are presented. Keywords: Glass, fused silica, photoelasticity, residual stress

  18. Principles of the measurement of residual stress by neutron diffraction

    International Nuclear Information System (INIS)

    Webster, G.A.; Ezeilo, A.N.

    1996-01-01

    The presence of residual stresses in engineering components can significantly affect their load carrying capacity and resistance to fracture. In order to quantify their effect it is necessary to know their magnitude and distribution. Neutron diffraction is the most suitable method of obtaining these stresses non-destructively in the interior of components. In this paper the principles of the technique are described. A monochromatic beam of neutrons, or time of flight measurements, can be employed. In each case, components of strain are determined directly from changes in the lattice spacings between crystals. Residual stresses can then be calculated from these strains. The experimental procedures for making the measurements are described and precautions for achieving reliable results discussed. These include choice of crystal planes on which to make measurements, extent of masking needed to identify a suitable sampling volume, type of detector and alignment procedure. Methods of achieving a stress free reference are also considered. A selection of practical examples is included to demonstrate the success of the technique. (author) 14 figs., 1 tab., 18 refs

  19. A review of inducing compressive residual stress - shot peening; on structural metal and welded connection

    Science.gov (United States)

    Kanchidurai, S.; Krishanan, P. A.; Baskar, K.; Saravana Raja Mohan, K.

    2017-07-01

    Shot peening treatment (SPT) is a significant mechanical method to enhance the surface of the material by inducing compressive residual stress on the layer. This study provides a review of prominent improvement in fatigue life on high strength aluminium alloy, steel and welded connection by SPT. Compressive residual stress measurement and its factors data are extracted from assorted literature, optimized peening process commented in this paper, also different types of mechanical peening methods and its effectiveness are mentioned. Fatigue life improvement is focused commented to welded structural connections. The extracted results shows significant changes in the surface layer of metals, aluminium alloy 15 - 250% of fatigue life improvement, steel plain members 6-200% of fatigue life improvement, welded connections 50-75% of fatigue life improvement and significant improvement in mechanical properties like roughness reduction, wear, hardness, tensile strength, corrosion and scuffing.

  20. Development of procedures for the measurement of residual stress by neutron diffraction

    CERN Document Server

    Webster, G A

    2002-01-01

    Neutron diffraction is a non-destructive method for determining residual stresses in crystalline materials. It is a relatively new technique and no standard is currently available for making these measurements. This paper gives the background to research that has been carried out to develop a standard. It outlines the main findings and indicates the precautions that are required to achieve accurate positioning and alignment of specimens (and components) in a neutron beam and the analysis required to obtain reliable results. It also shows that special attention is needed in dealing with near-surface measurements because of surface aberration. It is demonstrated that, provided the recommended procedures are followed, a positional tolerance of +-0.1 mm can be achieved with an accuracy in strain of propor to 10 sup - sup 4 , to give a resolution in residual stress of propor to 7 to 20 MPa in most materials of practical interest. (orig.)

  1. Effect of surface treatments on stress corrosion cracking susceptibility of nickel base alloys

    International Nuclear Information System (INIS)

    Iwanami, Masaru; Kaneda, Junya; Tamako, Hiroaki; Hato, Hisamitsu; Takamoto, Shinichi

    2009-01-01

    Effect of surface treatment on SCC susceptibility of Ni base alloys was investigated. Cracks were observed in all grinding specimens in a creviced bent beam (CBB) test. On the other hand, no cracks occurred in shot peening (SP), water jet peening (WJP) specimens. It was indicated that these surface treatments effectively reduced the SCC susceptibility of nickel-base alloys. As a result of a residual stress test, the surface of specimens with grinding had high tensile residual stress. However, SP and WJP improved surface residual stress to compressive stress. The depth of the compressive effect of WJP was almost the same as that of SP. However, the surface hardness of WJP specimens differed from that of SP and it was found that WJP had less impact on surface hardening. This difference was consistent with their surface microstructures. The surface of SP specimens had clearly the deformation region, but the surface of WJP specimens was localized. (author)

  2. Investigation of the Effect of Residual Stress Gradient on the Wear Behavior of PVD Thin Films

    Science.gov (United States)

    Tlili, B.; Nouveau, C.; Guillemot, G.; Besnard, A.; Barkaoui, A.

    2018-02-01

    The control of residual stresses has been seldom investigated in multilayer coatings dedicated to improvement of wear behavior. Here, we report the preparation and characterization of superposed structures composed of Cr, CrN and CrAlN layers. Nano-multilayers CrN/CrAlN and Cr/CrN/CrAlN were deposited by Physical Vapor Deposition (PVD) onto Si (100) and AISI4140 steel substrates. The Cr, CrN and CrAlN monolayers were developed with an innovative approach in PVD coatings technologies corresponding to deposition with different residual stresses levels. Composition and wear tracks morphologies of the coatings were characterized by scanning electron microscopy, high-resolution transmission electron microscopy, atomic force microscopy, x-ray photoelectron spectroscopy, energy-dispersive x-ray spectroscopy, x-ray diffraction and 3D-surface analyzer. The mechanical properties (hardness, residual stresses and wear) were investigated by nanoindentation, interferometry and micro-tribometry (fretting-wear tests). Observations suggest that multilayer coatings are composed mostly of nanocrystalline. The residual stresses level in the films has practically affected all the physicochemical and mechanical properties as well as the wear behavior. Consequently, it is demonstrated that the coating containing moderate stresses has a better wear behavior compared to the coating developed with higher residual stresses. The friction contact between coated samples and alumina balls shows also a large variety of wear mechanisms. In particular, the abrasive wear of the coatings was a combination of plastic deformation, fine microcracking and microspallation. The application of these multilayers will be wood machining of green wood.

  3. Investigation of the Effect of Residual Stress Gradient on the Wear Behavior of PVD Thin Films

    Science.gov (United States)

    Tlili, B.; Nouveau, C.; Guillemot, G.; Besnard, A.; Barkaoui, A.

    2018-01-01

    The control of residual stresses has been seldom investigated in multilayer coatings dedicated to improvement of wear behavior. Here, we report the preparation and characterization of superposed structures composed of Cr, CrN and CrAlN layers. Nano-multilayers CrN/CrAlN and Cr/CrN/CrAlN were deposited by Physical Vapor Deposition (PVD) onto Si (100) and AISI4140 steel substrates. The Cr, CrN and CrAlN monolayers were developed with an innovative approach in PVD coatings technologies corresponding to deposition with different residual stresses levels. Composition and wear tracks morphologies of the coatings were characterized by scanning electron microscopy, high-resolution transmission electron microscopy, atomic force microscopy, x-ray photoelectron spectroscopy, energy-dispersive x-ray spectroscopy, x-ray diffraction and 3D-surface analyzer. The mechanical properties (hardness, residual stresses and wear) were investigated by nanoindentation, interferometry and micro-tribometry (fretting-wear tests). Observations suggest that multilayer coatings are composed mostly of nanocrystalline. The residual stresses level in the films has practically affected all the physicochemical and mechanical properties as well as the wear behavior. Consequently, it is demonstrated that the coating containing moderate stresses has a better wear behavior compared to the coating developed with higher residual stresses. The friction contact between coated samples and alumina balls shows also a large variety of wear mechanisms. In particular, the abrasive wear of the coatings was a combination of plastic deformation, fine microcracking and microspallation. The application of these multilayers will be wood machining of green wood.

  4. Quantification of residual stress from photonic signatures of fused silica

    International Nuclear Information System (INIS)

    Cramer, K. Elliott; Yost, William T.; Hayward, Maurice

    2014-01-01

    A commercially available grey-field polariscope (GFP) instrument for photoelastic examination is used to assess impact damage inflicted upon the outer-most pane of Space Shuttle windows made from fused silica. A method and apparatus for calibration of the stress-optic coefficient using four-point bending is discussed. The results are validated on known material (acrylic) and are found to agree with literature values to within 6%. The calibration procedure is then applied to fused-silica specimens and the stress-optic coefficient is determined to be 2.43 ± 0.54 × 10 −12 Pa −1 . Fused silica specimens containing impacts artificially made at NASA’s Hypervelocity Impact Technology Facility (HIT-F), to simulate damage typical during space flight, are examined. The damage sites are cored from fused silica window carcasses and examined with the GFP. The calibrated GFP measurements of residual stress patterns surrounding the damage sites are presented

  5. REAL STRUCTURE AND RESIDUAL STRESSES IN ADVANCED WELDS DETERMINED BY X-RAY AND NEUTRON DIFFRACTION

    Directory of Open Access Journals (Sweden)

    Karel Trojan

    2017-07-01

    Full Text Available The paper outlines the capability of X-ray diffraction (XRD for evaluation of real structure changes and residual stresses (RS on cross-section of advanced thick welds due to the welding of ferromagnetic plates. The results of neutron diffraction describe a three-dimensional state of RS and also verify previous assumptions of RS redistribution as a result of the surface preparation for determination 2D maps measured by XRD.

  6. Residual Stress in Sprayed Ni+5% Al Coatings Determined by Neutron Diffraction

    Czech Academy of Sciences Publication Activity Database

    Matějíček, Jiří; Sampath, S.; Gnaupel-Herold, T.; Prask, H. J.

    2002-01-01

    Roč. 74, supplement 8 (2002), s. S1692-S1694 ISSN 0947-8396 R&D Projects: GA ČR GA106/01/0094 Grant - others:NSF DMR(US) 6932570 Institutional research plan: CEZ:AV0Z2043910 Keywords : residual stress, thermal spray coatings, neutron diffraction Subject RIV: JK - Corrosion ; Surface Treatment of Materials Impact factor: 2.231, year: 2002

  7. Neutron diffraction analysis of residual stresses near unannealed welds in anhydrous ammonia nurse tanks.

    Science.gov (United States)

    Becker, A T; Chumbley, L S; Goettee, D; Russell, A M

    2014-01-01

    Neutron diffraction analysis was employed to measure residual stresses near welds in used anhydrous ammonia nurse tanks. Tensile residual stresses contribute to stress corrosion cracking of nurse tanks, which can cause tanks to release toxic ammonia vapor. The analysis showed that tensile residual stresses were present in the tanks measured, and the magnitudes of these stresses approached the yield strength of the steel. Implications for agricultural safety and health are discussed.

  8. Non-destructive measurement of residual stresses in nuclear welds by means of neutron diffraction

    International Nuclear Information System (INIS)

    Ohms, C.; Youtsos, A.G.; Idsert, P. v.d.

    2001-01-01

    Non-destructive measurement of welding stresses in structural components remains a challenging task. One out of very few techniques applicable to such problems is the neutron diffraction technique, which is closely related to the well-established X-ray diffraction. Whereas the latter provides for non-destructive measurement of surface stresses only, neutron diffraction enables the engineer to obtain in- depth measurements of residual stress. At the High Flux Reactor (HFR) of the Joint Research Centre (JRC), Petten, a new residual stress diffractometer has been installed capable of handling components up to 1000 kg - the Large Component Neutron Diffraction Facility (LCNDF). It has facilitated residual stress measurements in various weldments, including steel piping welds for nuclear applications. In this paper the principles of the technique are outlined and major elements of testing equipment and procedures are presented. Particularities to be taken into account especially in testing of austenitic steel welds are explained. Finally test results obtained on two thick steel nuclear piping welds are presented. (orig.)

  9. Residual Stresses in DC cast Aluminum Billet: Neutron Diffraction Measurements and Thermomechanical Modeling

    Science.gov (United States)

    Drezet, J.-M.; Evans, A.; Pirling, T.

    2011-05-01

    Thermally-induced residual stresses, generated during the industrial Direct Chill casting process of aluminum alloys, can cause both significant safety concerns as well as the formation of defects during down-stream processing. Although these thermally induced strains can be partially relieved by permanent deformation, cracks will be generated either during solidification (hot tears) or post-solidification cooling (cold cracks) when stresses exceed the deformation limit of the alloy. Furthermore, the thermally induced strains result in the presence of large internal stresses within the billet before further processing steps. Although numerical models have been previously developed to compute these residual stresses, most of the computations have been validated only against measured surface distortions. In the present work, the variation in residual elastic strains and stresses in the steady state regime of casting has been measured as a function of radial position using neutron diffraction in an AA6063 grain-refined cylindrical billet. These measurements have been carried out on the same billet section at Poldi at PSI-Villigen and at Salsa at ILL-Grenoble and compare favorably. The results are used to validate a thermo-mechanical finite element casting model and to assess the level of stored elastic energy within the billet.

  10. In-situ observation of dislocation and analysis of residual stresses by FEM/DDM modeling in water cavitation peening of pure titanium

    Science.gov (United States)

    Y Ju, D.; Han, B.

    2015-04-01

    In this paper, in order to approach this problem, specimens of pure titanium were treated with WCP, and the subsequent changes in microstructure, residual stress, and surface morphologies were investigated as a function of WCP duration. The influence of water cavitation peening (WCP) treatment on the microstructure of pure titanium was investigated. A novel combined finite element and dislocation density method (FEM/DDM), proposed for predicting macro and micro residual stresses induced on the material subsurface treated with water cavitation peening, is also presented. A bilinear elastic-plastic finite element method was conducted to predict macro-residual stresses and a dislocation density method was conducted to predict micro-residual stresses. These approaches made possible the prediction of the magnitude and depth of residual stress fields in pure titanium. The effect of applied impact pressures on the residual stresses was also presented. The results of the FEM/DDM modeling were in good agreement with those of the experimental measurements.

  11. Effects of shot peening on the residual stress of welded SS400 steel

    International Nuclear Information System (INIS)

    Lee, Jong Man; Kim, Tae Hyung; Cheong, Seong Kyun; Lee, Seung Ho

    2002-01-01

    The fatigue life of structures is usually determined by welding zone. The tensile residual stress, which is induced by welding, reduces the fatigue life and fatigue strength of welded structures. If we remove the tensile residual stress or induce the compressive residual stress, the fatigue life of welded structures will be improved. The change of hardness and compressive residual stress of welded zone after shot peening was investigated in this paper. The results show that the hardness was increased by shot peening. The residual stress was reduced by shot peening

  12. Effects of location, thermal stress and residual stress on corner cracks in nozzles with cladding

    International Nuclear Information System (INIS)

    McLean, J.L.; Cohen, L.M.; Besuner, P.M.

    1979-01-01

    The stress intensity factors (K 1 ) for corner cracks in a boiling water reactor feedwater nozzle with stainless steel cladding are obtained for loading by internal pressure and a fluid quench in the nozzle. Conditions both with and without residual stress in the component are considered. The residual stress is simulated by means of a reference temperature change. The stress distribution for the uncracked structure is obtained from a three-dimensional finite element model. A three-dimensional influence function (IF) method, in conjunction with the boundary-integral equation method for structural analysis, is employed to compute K 1 values from the uncracked stress distribution. For each type of loading K 1 values are given for cracks at 15 nozzle locations and for 6 crack depths. Reasonable agreement is noted between calculated and previously published pressure-induced K 1 values. Comparisons are made to determine the effect on K 1 of crack location, thermal stress and residual stress, as compared with pressure stress. For the thermal transient it is shown that K 1 for small crack depths is maximised early in the transient, while K 1 for large cracks is maximised later under steady state conditions. Computation should, therefore, be made for several transient time points and the maximum K 1 for a given crack depth should be used for design analysis. It is concluded that the effects on K 1 of location, thermal stresses and residual stresses are significant and generally too complex to evaluate without advanced numerical procedures. The utilised combination of finite element analysis of the uncracked structure and three-dimensional influence function analysis of the cracked structure is demonstrated and endorsed. (author)

  13. Residual stress measurements in inconel alloy 600 tubing using an advanced x-ray instrument and Cr K /SUB beta/ radiation

    International Nuclear Information System (INIS)

    Ivkovich, D.P.; Ruud, C.O.; Snoha, D.J.

    1985-01-01

    Residual stresses in an inconel alloy 600 U-bend tube, used in heat exchangers in nuclear reactors, were studied using an advanced x-ray instrument developed at The Pennsylvania State University. The work funded by the Electric Power Research Institute (EPRI) mapped both the axial and circumferential (hoop) stresses on the outside surface of the tube. The residual stresses, inherent in the fabrication of the U-bend tubes, are a major contributor to stress corrosion cracking

  14. Residual Stress Developed During the Cure of Thermosetting Polymers: Optimizing Cure Schedule to Minimize Stress.

    Energy Technology Data Exchange (ETDEWEB)

    Kropka, Jamie Michael; Stavig, Mark E.; Jaramillo, Rex

    2016-06-01

    When thermosetting polymers are used to bond or encapsulate electrical, mechanical or optical assemblies, residual stress, which often affects the performance and/or reliability of these devices, develops within the structure. The Thin-Disk-on-Cylinder structural response test is demonstrated as a powerful tool to design epoxy encapsulant cure schedules to reduce residual stress, even when all the details of the material evolution during cure are not explicitly known. The test's ability to (1) distinguish between cohesive and adhesive failure modes and (2) demonstrate methodologies to eliminate failure and reduce residual stress, make choices of cure schedules that optimize stress in the encapsulant unambiguous. For the 828/DEA/GMB material in the Thin-Disk-on-Cylinder geometry, the stress associated with cure is significant and outweighs that associated with cool down from the final cure temperature to room temperature (for measured lid strain, Scure I > I I e+h erma * II) * The difference between the final cure temperature and 1 1 -- the temperature at which the material gels, Tf-T ge i, was demonstrated to be a primary factor in determining the residual stress associated with cure. Increasing T f -T ge i leads to a reduction in cure stress that is described as being associated with balancing some of the 828/DEA/GMB cure shrinkage with thermal expansion. The ability to tune residual stress associated with cure by controlling T f -T ge i would be anticipated to translate to other thermosetting encapsulation materials, but the times and temperatures appropriate for a given material may vary widely.

  15. Measuring multiple residual-stress components using the contour method and multiple cuts

    Energy Technology Data Exchange (ETDEWEB)

    Prime, Michael B [Los Alamos National Laboratory; Swenson, Hunter [Los Alamos National Laboratory; Pagliaro, Pierluigi [U. PALERMO; Zuccarello, Bernardo [U. PALERMO

    2009-01-01

    The conventional contour method determines one component of stress over the cross section of a part. The part is cut into two, the contour of the exposed surface is measured, and Bueckner's superposition principle is analytically applied to calculate stresses. In this paper, the contour method is extended to the measurement of multiple stress components by making multiple cuts with subsequent applications of superposition. The theory and limitations are described. The theory is experimentally tested on a 316L stainless steel disk with residual stresses induced by plastically indenting the central portion of the disk. The stress results are validated against independent measurements using neutron diffraction. The theory has implications beyond just multiple cuts. The contour method measurements and calculations for the first cut reveal how the residual stresses have changed throughout the part. Subsequent measurements of partially relaxed stresses by other techniques, such as laboratory x-rays, hole drilling, or neutron or synchrotron diffraction, can be superimposed back to the original state of the body.

  16. Effect of residual stress induced by cold expansion on fatigue crack ...

    African Journals Online (AJOL)

    Fatigue life and fatigue crack growth rate are controlled by stress ratio, stress level, orientation of crack, temper-ature, residual stress, corrosion, etc. The effects of residual stress on fatigue crack growth in aluminium (Al) alloy 2024-T351 by Mode I crack were investigated by applying constant amplitude cycles based on ...

  17. Reduction of Residual Stresses in Sapphire Cover Glass Induced by Mechanical Polishing and Laser Chamfering Through Etching

    Directory of Open Access Journals (Sweden)

    Shih-Jeh Wu

    2016-10-01

    Full Text Available Sapphire is a hard and anti-scratch material commonly used as cover glass of mobile devices such as watches and mobile phones. A mechanical polishing using diamond slurry is usually necessary to create mirror surface. Additional chamfering at the edge is sometimes needed by mechanical grinding. These processes induce residual stresses and the mechanical strength of the sapphire work piece is impaired. In this study wet etching by phosphate acid process is applied to relief the induced stress in a 1” diameter sapphire cover glass. The sapphire is polished before the edge is chamfered by a picosecond laser. Residual stresses are measured by laser curvature method at different stages of machining. The results show that the wet etching process effectively relief the stress and the laser machining does not incur serious residual stress.

  18. Effect of thermal exposure on the residual stress relaxation in a hardened cylindrical sample under creep conditions

    Science.gov (United States)

    Radchenko, V. P.; Saushkin, M. N.; Tsvetkov, V. V.

    2016-05-01

    This paper describes the effect of thermal exposure (high-temperature exposure) ( T = 675°C) on the residual creep stress relaxation in a surface hardened solid cylindrical sample made of ZhS6UVI alloy. The analysis is carried out with the use of experimental data for residual stresses after micro-shot peening and exposures to temperatures equal to T = 675°C during 50, 150, and 300 h. The paper presents the technique for solving the boundary-value creep problem for the hardened cylindrical sample with the initial stress-strain state under the condition of thermal exposure. The uniaxial experimental creep curves obtained under constant stresses of 500, 530, 570, and 600 MPa are used to construct the models describing the primary and secondary stages of creep. The calculated and experimental data for the longitudinal (axial) tensor components of residual stresses are compared, and their satisfactory agreement is determined.

  19. Development of an on-site measurement method for residual stress in primary system piping of nuclear power plants

    International Nuclear Information System (INIS)

    Maekawa, Akira; Takahashi, Shigeru; Fujiwara, Masaharu

    2014-01-01

    In residual stress measurement for large-scale pipes and vessels in high radiation areas and highly contaminated areas of nuclear plants, it is difficult to bring the radioactivated pipes and vessels out of the areas as they are. If they can brought out, it is very burdensome to handle them for the measurement. Development of an on-site measurement method of residual stress which can be quickly applied and has sufficient measurement accuracy is desirable. In this study, a new method combining an electric discharge skim-cut method with a microscopic strain measurement method using markers was proposed to realize the on-site residual stress measurement on pipes in high radiation areas and highly contaminated areas. In the electric discharge skim-cut method, a boat-type sample is skimmed out of a pipe outer/inner surface using electric discharge machining and released residual stress is measured. The on-site measurement of residual stress by the method can be done using a small, portable electric discharge machine. In the microscopic strain measurement method using markers, the residual stress is estimated by microscopic measurement of the distance between markers after the stress release. The combination of both methods can evaluate the residual stress with the same accuracy as conventional methods offer and it can achieve reduction of radiation exposure in the measurement because the work is done simply and rapidly. In this study, the applicability of the electric discharge skim-cut method was investigated because the applicability of the microscopic strain measurement method using markers was confirmed previously. The experimental examination clarified the applicable conditions for the residual stress measurement with the same accuracy as the conventional methods. Furthermore, the electric discharge machining conditions using pure water as the machining liquid was found to eliminate the amount of liquid radioactive waste completely. (author)

  20. Differential RF MEMS interwoven capacitor immune to residual stress warping

    KAUST Repository

    Elshurafa, Amro M.

    2012-07-27

    A RF MEMS capacitor with an interwoven structure is designed, fabricated in the PolyMUMPS process and tested in an effort to address fabrication challenges usually faced in MEMS processes. The interwoven structure was found to offer several advantages over the typical MEMS parallel-plate design including eliminating the warping caused by residual stress, eliminating the need for etching holes, suppressing stiction, reducing parasitics and providing differential capability. The quality factor of the proposed capacitor was higher than five throughout a 2–10 GHz range and the resonant frequency was in excess of 20 GHz.

  1. Quantification of Residual Stresses in External Attachment Welding Applications

    DEFF Research Database (Denmark)

    Alhajri, R.; Liu, S.; Yu, Z.

    2017-01-01

    It is uncertain whether postweld heat treatment (PWHT) should be required for external attachment welds in petrochemical industry applications where stress corrosion cracking (SCC) is a possibility. An industrial criterion established by NACE SP0472 indicates that PWHT is not required if residual...... welding (GMAW) process to deposit single beadonplate welds with ER70S6 wire on ASTM516 grade 70 pressure vessel steel plates of 6.3, 12.7, and 19 mm thicknesses. Microstructural analysis, temperature, and distortion measurements of weldments were performed to qualify the FEA modeling results. In addition...

  2. Numerical and Experimental Analyses of Residual Stresses in

    DEFF Research Database (Denmark)

    Hansen, Jan Langkjær; Hattel, Jesper; Lorentzen, Torben

    1999-01-01

    been done using the novel non-destructive technique of neutron diffraction.The thermal model takes into account the moving heat source in the V-shaped weld. The heat source is modelled by filler material being added continuously in connection with a body flux. In order to obtain a more realistic weld......Butt-welding in one pass with SMAW of two 10mm mild steel plates is investigated. In order to predict the residual stress fields associated with the welding procedure, a finite element model in 3D has been developed in ABAQUS. This model applies a sequential thermal and mechanical numerical...

  3. The effect of residual stress on polymer pipe lifetime

    Czech Academy of Sciences Publication Activity Database

    Hutař, Pavel; Ševčík, Martin; Frank, A.; Náhlík, Luboš; Kučera, J.; Pinter, G.

    2013-01-01

    Roč. 108, SI (2013), s. 98-108 ISSN 0013-7944. [Crack paths 2012. Gaeta, 19.09.2012-21.09.2012] R&D Projects: GA ČR(CZ) GAP108/12/1560; GA MŠk(CZ) ED1.1.00/02.0068; GA MŠk(CZ) EE2.3.30.0063 Institutional support: RVO:68081723 Keywords : Residual stress * Linear elastic fracture mechanics * Lifetime estimation * Polyethylene pipes * Slow crack growth Subject RIV: JL - Materials Fatigue, Friction Mechanics Impact factor: 1.662, year: 2013

  4. Residual stress of particulate polymer composites with reduced thermal expansion

    International Nuclear Information System (INIS)

    Nishino, T; Kotera, M; Sugiura, Y

    2009-01-01

    Thermal expansion behavior was investigated for tangusten zirconium phosphate (Zr 2 (WO 4 )(PO 4 ) 2 (ZWP)) particulate filled poly(ether ether ketone) (PEEK) composite. ZWP is known as ceramic filler with a negative thermal expansion. By incorporating ZWP with 40 volume %, the linear thermal expansion coefficient of the PEEK composite was reduced to almost same value (2.53 X 10 -5 K -1 ) with that of aluminum. This decrease was found to be quite effective for the decrease of the residual stress at the interface between aluminum plate and the composite.

  5. X ray measurement of residual stresses on metallic structures

    International Nuclear Information System (INIS)

    Barbarin, P.; Convert, M.; Miege

    1983-01-01

    The principle of measuring residual stresses by X ray diffraction (the famous Bragg'law is used) may be applied at an industrial level. CETIM has perfected an outfit adjusted to measurements on the spot, which can be used on metallic parts of a large size. This paper describes this equipment, giving its advantages towards previous devices, and assessing measurements errors. Some actual cases for results obtained are given. This paper starts with a brief historical account and theoretical backgrounds of the method [fr

  6. The effects of location, thermal stress, and residual stress on corner cracks in nozzles with cladding

    International Nuclear Information System (INIS)

    Besuner, P.M.; Cohen, L.M.; McLean, J.L.

    1977-01-01

    The stress intensity factors (Ksub(I)) for corner cracks in a boiling water reactor feedwater nozzle with stainless steel cladding are obtained for loading by internal pressure, and a fluid quench in the nozzle. Conditions with and without residual stress in the component are considered. The residual stress is simulated by means of a reference temperature change. The stress distribution for the uncracked structure is obtained from a three-dimensional finite element model. A three-dimensional influence function (IF) method, in conjunction with the boundary-integral equation method for structural analysis is employed to compute Ksub(I) values from the uncracked structure's stress distribution. It is concluded that the effects on Ksub(I) of location, thermal stresses, and residual stresses are significant and generally too complex to evaluate without advanced numerical procedures. The ulilized combination of finite element analysis of the uncracked structure and three-dimensional influence function analysis of the cracked structure is demonstrated and endorsed. (Auth.)

  7. Model Of Relaxation Of Residual Stresses In Hot-Rolled Strips

    Directory of Open Access Journals (Sweden)

    Milenin A.

    2015-09-01

    Full Text Available Residual stresses in hot-rolled strips are of practical importance when the laser cutting of these strip is applied. The factors influencing the residual stresses include the non uniform distribution of elastic-plastic deformations, phase transformation occurring during cooling and stress relaxation during rolling and cooling. The latter factor, despite its significant effect on the residual stress, is scarcely considered in the scientific literature. The goal of the present study was development of a model of residual stresses in hot-rolled strips based on the elastic-plastic material model, taking into account the stress relaxation.

  8. Comparison of Measured Residual Stress in an Extra Thick Multi-pass Weld Using Neutron Diffraction Method and Inherent Strain Method

    International Nuclear Information System (INIS)

    Park, JeongUng; An, GyuBaek; Woo, Wan Chuck

    2015-01-01

    With the increase of large-scale containership, a large amount of high-strength steels with extra thick plates is being extensively used. The welding stress existing in the extra thick welded plates has a significant effect on the integrity of the component in terms of brittle fracture and fatigue behavior. It has been reported that welding residual stress distribution in an extra thick plate can affect the propagation path of the crack. Therefore, it is important to measure the distribution of welding residual stresses for the reliable design of the welded structures. So far various researches have been carried out for the determination of residual stresses on the surface of steels. In this paper, the total residual stresses in the 70 mm thick multipass FACW butt joint were measured by integrating initial stress into ISM. Concretely, two methods named as initial stress integrated ISM and initial inherent strain integrated ISM were employed to determine the total residual stresses. Furthermore, the distributions of residual stresses were compared with the results of the Neutron Diffraction Method(NDM). In order to measure the three dimensional residual stresses in the welded joint with initial stresses existing before welding, initial stress integrated ISM and initial inherent strain integrated ISM were developed. The residual stresses in 70 mm-thick butt joint by flux cored arc welding were carried out with a good accuracy using the two developed methods. The residual stresses in welded joint using both initial stress integrated ISM and initial inherent strain integrated ISM agreed well with the results measured by Neutron Diffraction Method. This suggests that the integrated ISM is a reliable method for residual stress measurement if initial stress existed

  9. Effect of residual stress on crack-tip for fatigue crack propagation

    International Nuclear Information System (INIS)

    Kim, Kyung Mo

    1995-02-01

    Fatigue tests were performed in cyclic loading at 10Hz and stress ratios, R of 0.1 and 0.2 at room temperature. The type 304 stainless steel specimens are prepared into two different thickness (3mm and 25mm). The fatigue crack growth rate of 25mm thick specimen is faster than that of 3mm thick specimen, and this result is attributed to the difference of plasticity in the crack tip region from the elastic-plastic fracture mechanical analysis. The residual stress fields are induced by the surface hardening treatments by induction heating at temperatures of ∼600 .deg. C, 750 .deg. C and 900 .deg. C, and the induced residual stresses are verified by the X-ray measurements of the induction heating treated specimen at 750 .deg. C. It is observed that the tensile residual stress is formed at heat affected zone and, behind this zone, the compressive residual stress is formed with maximum value of ∼200 MPa. The results of fatigue tests showed the acceleration of the growth rate in tensile region, and the retardation in compressive region. The results of constant stress intensity tests illustrated that the variations of the crack growth rate are related with the change of crack closure level. A simple model for fatigue crack propagation of materials is derived with energy balance approach on the basis of the Dugdale model, and this model is verified through the experiments of two kinds of materials (type 304 stainless steel and Inconel 718). The energy balance model demonstrated that the variations of material's tearing modulus results in the change of fatigue crack propagation

  10. A quantitative non-destructive residual stress assessment tool for pipelines.

    Science.gov (United States)

    2014-09-01

    G2MT successfully demonstrated the eStress system, a powerful new nondestructive evaluation : system for analyzing through-thickness residual stresses in mechanical damaged areas of steel : pipelines. The eStress system is designed to help pipe...

  11. Residual and operating stresses in welded Alloy 600 penetrations

    International Nuclear Information System (INIS)

    Hunt, E.S.; Gross, D.J.; Pathania, R.

    1995-01-01

    An elastic-plastic finite element model has been developed for calculating residual and operating stresses in Alloy 600 penetrations which are installed in pressure vessel shells by J-groove welds. The welding process is simulated by multiple passes of heat input with heat transfer into the adjacent parts during welding and cooling. Analysis results are presented for CRDM nozzles, pressurizer instrument nozzles and pressurizer heater sleeves. The effect of several key variables such as nozzle material yield strength, angle of the nozzle relative to the vessel shell, weld size, presence of counterbores, etc. are explored. Results of the modelling are correlated with field and laboratory data. Application of the stress analysis results to PWSCC predictive modeling is discussed. (author). 6 refs, 12 figs, 2 tabs

  12. Pattern formation under residual compressive stress in free sustained aluminum films

    International Nuclear Information System (INIS)

    Yu Senjiang; Ye Quanlin; Zhang Yongju; Cai Pinggen; Xu Xiaojun; Chen Jiangxing; Ye Gaoxiang

    2005-01-01

    A nearly free sustained aluminum (Al) film system has been successfully fabricated by vapor phase deposition of Al atoms on silicone oil surfaces and an unusual type of ordered patterns at the micrometer scale has been systematically studied. The ordered patterns are composed of a large number of parallel key-shaped domains and possess a sandwiched structure. The nucleation and growth of the patterns are very susceptible to the growth period, deposition rate, nominal film thickness and location of the film. The experiment shows that the ordered patterns are induced by the residual compressive stress in the film owing to contraction of the liquid surface after deposition. The appearance of these stress relief patterns generally represents the stress distribution in the nearly free sustained Al films, which mainly results from the characteristic boundary condition and the nearly zero adhesion of the solid-liquid interface

  13. Residual stresses in a bulk metallic glass-stainless steel composite

    International Nuclear Information System (INIS)

    Aydiner, C.C.; Uestuendag, E.; Clausen, B.; Hanan, J.C.; Winholtz, R.A.; Bourke, M.A.M.; Peker, A.

    2005-01-01

    Bulk metallic glasses (BMGs) are new structural materials with impressive mechanical properties. They can now be cast into large dimensions, which can lead to significant residual stress generation due to thermal tempering. In this process, a surface compression develops balanced with tension in the interior. To evaluate this phenomenon non-destructively, a model cylindrical stainless steel (SS)-BMG composite was prepared and studied using neutron diffraction and finite element (FE) modeling. The residual strain data from the SS obtained by diffraction were used in modeling calculations to show that significant tempering could be achieved in the composite (about -200 MPa surface compression in the SS). The strong bond between the SS and BMG allowed efficient load transfer and facilitated stress generation. The final values of the residual stresses were seen to be relatively insensitive to the high temperature constitutive behavior of the SS due to the physics of the thermal tempering in BMGs. The approach presented here constitutes an effective means to study non-destructively thermal tempering in BMGs

  14. Investigation of residual stresses in a sleeve coldworked lug specimen by neutron and x-ray diffraction

    International Nuclear Information System (INIS)

    Lin, R.; Jaensson, B.; Holden, T.M.; Rogge, R.B.; Root, J.H.

    1995-01-01

    Sleeve coldworking (SCW) is a mechanical process used in the aircraft industry to strengthen fastener holes of structural parts. By cold-expanding the holes, compressive residual stresses and a high dislocation density are introduced around the holes, the effect of which is to counteract the initiation and propagation of fatigue cracks and thus increase the fatigue life of the parts. The knowledge of residual stress due to SCW is therefore crucial for assessing the fatigue properties of a treated part. In this study, residual stresses were investigated, by employing neutron and X-ray diffraction methods, in a lug specimen that was sleeve coldworked and fatigued. The specimen had been used for testing the influence of the SCW process on fatigue life and crack propagation behaviour under constant amplitude or variable amplitude cyclic loading. X-ray diffraction has been widely used to determine surface residual stresses in engineering components. Neutron diffraction measurements, on the other hand, probe in-depth stresses, owing to the penetration of the neutron beam into most engineering materials. By using both techniques, we were able to investigate the surface as well as the in-depth distribution of residual stress in the specimen

  15. Minimization and Mitigation of Wire EDM Cutting Errors in the Application of the Contour Method of Residual Stress Measurement

    Science.gov (United States)

    Ahmad, Bilal; Fitzpatrick, Michael E.

    2016-01-01

    The contour method of residual stress measurement relies on the careful application of wire electro-discharge machining (WEDM) for the cutting stage. Changes in material removal rates during the cut lead to errors in the final calculated values of residual stress. In this study, WEDM cutting parameters have been explored to identify the optimum conditions for contour method residual stress measurements. The influence of machine parameters on the surface roughness and cutting artifacts in the contour cut is discussed. It has been identified that the critical parameter in improving the surface finish is the spark pulse duration. A typical cutting artifact and its impact on measured stress values have been identified and demonstrated for a contour cut in a welded marine steel. A procedure is presented to correct contour displacement data from the influence of WEDM cutting artifacts, and is demonstrated on the correction of a measured weld residual stress. The corrected contour method improved the residual stress magnitude up to 150 MPa. The corrected contour method results were validated by X-ray diffraction, incremental center hole drilling, and neutron diffraction.

  16. Residual Stresses in 21-6-9 Stainless Steel Warm Forgings

    Energy Technology Data Exchange (ETDEWEB)

    Everhart, Wesley A.; Lee, Jordan D.; Broecker, Daniel J.; Bartow, John P.; McQueen, Jamie M.; Switzner, Nathan T.; Neidt, Tod M.; Sisneros, Thomas A.; Brown, Donald W.

    2012-11-14

    Forging residual stresses are detrimental to the production and performance of derived machined parts due to machining distortions, corrosion drivers and fatigue crack drivers. Residual strains in a 21-6-9 stainless steel warm High Energy Rate Forging (HERF) were measured via neutron diffraction. The finite element analysis (FEA) method was used to predict the residual stresses that occur during forging and water quenching. The experimentally measured residual strains were used to calibrate simulations of the three-dimensional residual stress state of the forging. ABAQUS simulation tools predicted residual strains that tend to match with experimental results when varying yield strength is considered.

  17. The effects of machine parameters on residual stress determined using micro-Raman spectroscopy

    Energy Technology Data Exchange (ETDEWEB)

    Sparks, R.G.; Enloe, W.S.; Paesler, M.A.

    1988-12-01

    The effects of machine parameters on residual stresses in single point diamond turned silicon and germanium have been investigated using micro-Raman spectroscopy. Residual stresses were sampled across ductile feed cuts in < 100 > silicon and germanium which were single point diamond turned using a variety of feed rates, rake angles and clearance angles. High spatial resolution micro-Raman spectra (1{mu}m spot) were obtained in regions of ductile cutting where no visible surface damage was present. The use of both 514-5nm and 488.0nm excitation wavelengths, by virtue of their differing characteristic penetration depths in the materials, allowed determinations of stress profiles as a function of depth into the sample. Previous discussions have demonstrated that such Raman spectra will exhibit asymmetrically broadened peaks which are characteristic of the superposition of a continuum of Raman scatterers from the various depths probed. Depth profiles of residual stress were obtained using computer deconvolution of the resulting asymmetrically broadened raman spectra.

  18. Residual stress evaluation and curvature behavior of aluminum 7050 peen forming processed

    International Nuclear Information System (INIS)

    Oliveira, Rene Ramos de

    2011-01-01

    Shot peening is a superficial cold work process used to increase the fatigue life evaluated by residual stress measurements. The peen forming process is a variant of the shot peening process, where a curvature in the plate is obtained by the compression of the grains near to the surface. In this paper, the influence of the parameters such as: pressure of shot, ball shot size and thickness of aluminum 7050 samples with respect to residual stress profile and resulting arc height was studied. The evaluation of the residual stress profile was obtained by sin 2 ψ method. The results show that the formation of the curvature arc height is proportional to the shot peening pressure, of spheres size and inversely proportional to the thickness of the sample, and that stress concentration factor is larger for samples shot peened with small balls. On final of this paper presents an additional study on micro strain and average crystallite size, which can evaluate the profile of the samples after blasting. (author)

  19. Alternative Gas Mixtures in Arc Spraying: A Chance to Improve Coating Properties and Residual Stress States

    Science.gov (United States)

    Hauer, Michél; Henkel, Knuth Michael; Krebs, Sebastian; Kroemmer, Werner

    2018-01-01

    The highly cavitation erosion-resistant propeller alloys CuAl9Ni5Fe4Mn (Ni-Al-Bronze) and CuMn13Al8Fe3Ni2 (Mn-Al-Bronze) were arc-sprayed using a mixture of nitrogen and 2% of hydrogen as atomizing gas and different traverse speeds. The objective was to identify the influences of the different spraying conditions, such as temperature regime and melting loss, on the resulting residual stress states and coating properties. Residual stresses were measured by the incremental hole-drilling method using ESPI. Temperature measurements were carried out by thermographic imaging. Microstructural, chemical and mechanical analyses were realized to examine adhesive and cohesive properties. Additionally, the cavitation erosion behavior was investigated to analyze cohesive coating properties. The spraying process itself was improved, which was apparent by mainly enhanced deposition efficiency and reduced surface temperatures. The amount of oxides and pores as well as the melting loss of alloying elements were reduced. Moreover, an increased cavitation erosion resistance and thus coating cohesion as well as less residual stresses were identified. The change in atomizing gas diminished the impact of the quenching stresses on the coating properties. In contrast, the adhesive strength, Young's moduli and partially the hardness were slightly reduced. With regard to materials, Ni-Al-Bronze revealed superior coating properties in comparison with Mn-Al-Bronze.

  20. Relation of hardness with FWHM and residual stress of GCr15 steel after shot peening

    Science.gov (United States)

    Fu, Peng; Chu, Ruiqing; Xu, Zhijun; Ding, Guanjun; Jiang, Chuanhai

    2018-02-01

    The variations of XRD full width at half maximum (FWHM), residual stress and hardness for the surface of GCr15 steel after triple shot peening (TSP) as a function of annealing time and temperature are studied. The results show that with the increase of annealing temperature and time, hardness and FWHM increase gradually while compressive residual stress (CRS) decreases gradually. CRS and micro- structure work together on the hardness values, and the micro-structure is the most important factor for hardness. According to establishing the quantitive relationship of hardness with FWHM and CRS, the value of hardness can be calculated; a new type of noncontact and nondestructive hardness testing can be realized by XRD method.

  1. Effects on residual stresses of aluminum alloy LC4 by laser shock processing

    Science.gov (United States)

    Zhang, Yong-kang; Lu, Jin-zhong; Kong, De-jun; Yao, Hui-xue; Yang, Chao-jun

    2007-12-01

    The influences of processing parameters on laser-induced shock waves in metal components are discussed and analyzed. The effects of different parameters of laser shock processing (LSP) on residual stress of aerospace aluminum alloy LC4 were investigated. LSP was performed by using an Nd: glass phosphate laser with 23 ns pulse width and up to ~45 J pulse energy at power densities above GW/mm -2. Special attention is paid to the residual stresses from laser shock processing. Modification of microstructure, surface morphology by laser shock processing is also discussed. Results to date indicate that laser shock processing has great potential as a means of improving the mechanical performance of components.

  2. Residual stress diffractometer KOWARI at the Australian research reactor OPAL: Status of the project

    Science.gov (United States)

    Brule, Alain; Kirstein, Oliver

    2006-11-01

    Neutron scattering using diffraction techniques is now recognized as the most precise and reliable method of mapping sub-surface residual stresses in materials or even components, which are not only of academic but also of industrial-economic relevance. The great potential of neutrons in the field of residual stresses was recognized by ANSTO and its external Beam Instrument Advisory Group for the new research reactor OPAL. The recommendation was to build the dedicated strain scanner KOWARI among the first suite of instruments available to users. We give an update on the overall project and present the current status of the diffractometer. It is anticipated that the instrument will be commissioned in mid 2006 and available to users at the end of the OPAL project.

  3. Residual stress diffractometer KOWARI at the Australian research reactor OPAL: Status of the project

    International Nuclear Information System (INIS)

    Brule, Alain; Kirstein, Oliver

    2006-01-01

    Neutron scattering using diffraction techniques is now recognized as the most precise and reliable method of mapping sub-surface residual stresses in materials or even components, which are not only of academic but also of industrial-economic relevance. The great potential of neutrons in the field of residual stresses was recognized by ANSTO and its external Beam Instrument Advisory Group for the new research reactor OPAL. The recommendation was to build the dedicated strain scanner KOWARI among the first suite of instruments available to users. We give an update on the overall project and present the current status of the diffractometer. It is anticipated that the instrument will be commissioned in mid 2006 and available to users at the end of the OPAL project

  4. Thermal Aging Effects on Residual Stress and Residual Strain Distribution on Heat Affected Zone of Alloy 600 in Dissimilar Metal Weld

    International Nuclear Information System (INIS)

    Ham, Junhyuk; Choi, Kyoung Joon; Kim, Ji Hyun

    2016-01-01

    Dissimilar metal weld (DMW), consisting of Alloy 600, Alloy 182, and A508 Gr.3, has been widely used as a joining material of the reactor pressure vessel penetration nozzle and the steam generator tubing for pressurized water reactors (PWR) because of its good mechanical strength, thermal conductivity, and corrosion resistance. Residual tensile stress is mainly nominated as a cause of SCC in light water reactors by IAEA report. So, to relax the residual stress, post-weld heat treatment is required after manufacturing process such as welding. However, thermal treatment has a great effect on the microstructure and the chromium depletion profile on Alloy 600, so called sensitization. By this reason, HAZ on Alloy 600 is critical to crack. According to G.A. Young et al., Crack growth rates (CGR) in the Alloy 600 HAZ were about 30 times faster than those in the Alloy 600 base metal tested under the same conditions. And according to Z.P. Lu et al., CGR in the Alloy 600 HAZ can be more than 20 times higher than that in its base metal. There are some methods to measure the exact value of residual stress on the material surface. The most common way is X-ray diffraction method (XRD). The principle of XRD is based on lattice strains and depends on the changes in the spacing of the atomic planes in material. And there is a computer simulation method to estimate residual stress distribution which is called ANSYS. This study was conducted to investigate how thermal aging affects residual stress and residual strain distribution of Alloy 600 HAZ. Following conclusions can be drawn from this study. According to preceding researches and this study, both the relaxation of residual stress and the change of residual strain follow as similar way, spreading out from concentrated region. The result of Vickers micro-hardness tester shows that tensile residual stresses are distributed broadly on the material aged by 15 years. Therefore, HT400 Y 15 material is weakest state for PWSCC. The

  5. Measurement of the residual stresses in a stainless steel pipe girth weld containing long and short repairs

    International Nuclear Information System (INIS)

    Bouchard, P.J.; George, D.; Santisteban, J.R.; Bruno, G.; Dutta, M.; Edwards, L.; Kingston, E.; Smith, D.J.

    2005-01-01

    A series of residual measurements were made to obtain the through-thickness residual stress profiles in an as-welded and repair welded stainless steel pipe. Long and short length repairs were manufactured after initial measurements in the original girth weld. Measurements were made using neutron diffraction, deep hole and surface hole techniques. The various measurement methods were found to complement each other well. All the measurements revealed a characteristic profile for the through-thickness distribution of the residual stresses in the heat-affected zone. The residual stresses at mid-length of the heat affected zone of the short repair were found to be higher than in the long repair

  6. Assessment of interplay between UV wavelengths, material surfaces and food residues in open surface hygiene validation

    DEFF Research Database (Denmark)

    Abban, Stephen; Jakobsen, Mogens; Jespersen, Lene

    2014-01-01

    The use of UV-visible radiation for detecting invisible residue on different surfaces as a means of validating cleanliness was investigated. Wavelengths at 365, 395, 435, 445, 470 and 490 nm from a monochromator were used to detect residues of beef, chicken, apple, mango and skim milk. These were...

  7. Comparison of neutron and synchrotron diffraction measurements of residual stress in bead-on-plate weldments

    International Nuclear Information System (INIS)

    Paradowska, A.M.; Price, J.W.; Finlayson, T.R.; Lienert, U.; Ibrahim, R.

    2010-01-01

    This paper explores the use of neutron and synchrotron diffractions for the evaluation of residual stresses in welded components. It has been shown that it is possible to achieve very good agreement between the two independent diffraction techniques. This study shows the significance of the weld start and end sites on the residual strain/stress distribution. Quantitative evaluation of the residual stress development process for multibead weldments has been presented. Some measurements were also taken before and after postweld stress relieving to establish the reduction and redistribution of the residual stress. The detailed measurements of residual stress around the weld achieved in this work significantly improve the knowledge and understanding of residual stress in welded components.

  8. Residual stress measurement of the jacket material for ITER coil by neutron diffraction

    Energy Technology Data Exchange (ETDEWEB)

    Tsuchiya, Yoshinori [Japan Atomic Energy Research Inst., Tokai, Ibaraki (Japan). Tokai Research Establishment

    1998-03-01

    Nickel-Iron based super alloy INCOLOY 908 is used for the jacket of a central solenoid coil (CS coil) of the International Thermonuclear Experimental Reactor (ITER). INCOLOY 908, however, has a possibility of fracture due to Stress Accelerated Grain Boundary Oxidation (SAGBO) under a tensile residual stress beyond 200MPa. Therefore it is necessary to measure the residual stress of the jacket to avoid SAGBO. We performed residual stress measurement of the jacket by neutron diffraction using the neutron diffractometer for residual stress analysis (RESA) installed at JRR-3M in JAERI. A sample depth dependence of internal strain was obtained from the (111) plane spacing. A residual stress distribution was calculated from the strain using Young`s modulus and Poisson`s ratio that were evaluated by a tensile test with neutron diffraction. The result shows that the tensile residual stress exceeds 200MPa of the SAGBO condition in some regions inside the jacket. (author)

  9. Effect of residual stress on the integrity of a branch connection

    International Nuclear Information System (INIS)

    Law, M.; Kirstein, O.; Luzin, V.

    2012-01-01

    A new connection to an existing gas pipeline was made by hot-tapping, welding directly onto a pressurised pipeline. The welds were not post-weld heat treated, causing significant residual stresses. The critical weld had residual stresses determined by neutron diffraction using ANSTO's residual stress diffractometer, Kowari. The maximum measured residual stress (290 MPa) was 60% of the yield strength. The magnitudes of errors from a number of sources were estimated. An integrity assessment of the welded branch connection was performed with the measured residual stress values and with residual stress distributions from the BS 7910 and API 579 analysis codes. Analysis using estimates of residual stress from API 579 overestimated the critical crack size. Highlights: ► Residual stresses were measured by neutron diffraction in a thick section, non post-weld heat treated ferritic weld. ► There is little published data on these welds. ► The work compares the measured residual stresses with code-based residual stress distributions.

  10. On residual stress prescriptions for fitness for service assessment of pipe girth welds

    International Nuclear Information System (INIS)

    Dong, Pingsha; Song, Shaopin; Zhang, Jinmiao; Kim, Myung H.

    2014-01-01

    This paper aims to provide a detailed assessment of some of the existing residual stress profiles stipulated in widely used fitness-for-service assessment codes and standards, such as BS 7910 Appendix Q and API 579 RP Annex E, by taking advantage of some comprehensive residual stress studies that have recently become available. After presenting a case study on which residual stress measurements are available for validating finite element based residual stress analysis procedure, residual stress profiles stipulated in BS 7910 for pipe girth welds are selected for detailed evaluation by comparing residual stress distribution characteristics shown in parametric finite element results. A shell theory based full-field residual stress profile estimation scheme is then presented to illustrate how an improved estimation of residual stress profiles can be achieved in light of some of the deficiencies in BS 7910 and API 579 identified in this study. - Highlights: • Critically assessed girth weld residual stress profiles in major FFS Codes and Standards. • Identified deficiencies in relating to pipe geometry, heat input, and axial distance from weld. • Presented a shell theory based scheme for prescribing full-field residual stress profiles

  11. Experimental and Numerical Studies on Residual Stress in Wide Butt Welds

    Directory of Open Access Journals (Sweden)

    Yang Ding

    2017-01-01

    Full Text Available The presence of residual stress in steel members can significantly compromise the stiffness and fatigue life of steel structural components. This influence becomes more serious for the wide butt welds in the construction of large-sized steel members due to the different residual stress distribution from the normal size butt welds. This paper experimentally studied the residual stress in the wide butt welds through an 8-experiment test program. High residual stress was produced during the wide butt welding and this stress was observed to be even higher than the yield strength of the steel. Moreover, this residual stress in the steel plate was firstly compressive and then transferred into tensile stress with the increase in the distance away from the butt weld line. The magnitude of the residual stress increased with the increase in the width of the welding seams. This paper also developed a finite element model by SYSWELD to simulate the residual stress produced by the wide butt welding. The accuracy of the FE simulation was checked by the reported test results. In order to reduce the residual stress, the ultrasonic peening method was adopted. The analysis results indicated that ultrasonic peening method effectively reduced the residual stress caused by the wide butt welding during the construction.

  12. Interaction of stress and phase transformations during thermochemical surface engineering

    DEFF Research Database (Denmark)

    Jespersen, Freja Nygaard

    dissolution. The present project is devoted to understanding the mutual interaction of stresses and phase transformations during thermochemical surface engineering by combining numerical modelling with experimental materials science. The modelling was done by combining solid mechanics with thermodynamics...... by chromium atoms, and the effect of composition-induced stress on surface concentration and diffusive flux. The effect of plasticity was also included. Temperature and concentration dependencies of mechanical and diffusion material properties were studied, and the effect of incorporation in the model...... examined. The effect of pre-stressing the sample was also tested, to investigate the effects of a residual stress-state that might be present from processing of the metal specimen. Controlled thermochemical treatment of austenitic stainless steel was investigated experimentally by in-diffusion of nitrogen...

  13. Development of a measuring and evaluation method for X-ray analysis of residual stresses in the surface region of polycrystalline materials; Entwicklung eines Mess- und Auswerteverfahrens zur roentgenographischen Analyse des Eigenspannungszustandes im Oberflaechenbereich vielkristalliner Werkstoffe

    Energy Technology Data Exchange (ETDEWEB)

    Genzel, C.

    2000-11-01

    The topic of the habilitation thesis is the development of an X-ray diffraction method for measurement and depth-resolved analysis of internal stresses in the surface region of polycrystalline materials. The method relies on the basic approach of varying {tau}, the penetration depth of the X-rays in the materials, by the scattering vector g{sub theta{psi}} via stepwise specimen rotation. Thus, depth profiles of the interlattice plane distances d(hkl) in the specimen system can be derived for given direction and inclination angles {theta} and {psi} of the scattering vector. This offers the possibility to identify individual components of the stress tensors of the basic equation of the X-ray diffraction analysis, and to perform separate analyses of those components. For calculation of the relevant internal stress distributions {sigma}{sub ij}({tau}) using the interlattice plane distance profiles, a self-consistent method is established which takes into account the high sensitivity of the derived internal stresses in relation to the interlattice plane distance d{sub 0}(hkl) in the stress-free crystal lattice. The evaluation yields results describing the depth profiles as well as the strain-free interlattice plane distance d{sub 0}(hkl), so that a quantitative analysis is possible of tri-axial internal stress states in the surface region of the materials. (orig./CB) [German] Den Gegenstand der vorliegenden Arbeit bildet die Entwicklung eines roentgenographischen Mess- und Auswerteverfahrens zur tiefenaufgeloesten Analyse des oberflaechennahen Eigenspannungszustandes in vielkristallinen Werkstoffen. Der Grundgedanke der Methode besteht darin, die Eindringtiefe {tau} der Roentgenstrahlung in den Werkstoff durch schrittweise Drehung der Probe um den Streuvektor g{sub {theta}}{sub {psi}} zu variieren. Damit koennen Tiefenprofile der Netzebenenabstaende d(hkl) fuer fest vorgegebene Azimut- und Neigungswinkel {theta} und {psi} des Streuvektors im Probensystem ermittelt

  14. Determination of Bulk Residual Stresses in Electron Beam Additive-Manufactured Aluminum

    Science.gov (United States)

    Brice, Craig A.; Hofmeister, William H.

    2013-11-01

    Additive-manufactured aluminum alloy deposits were analyzed using neutron diffraction to characterize the effect of intermediate stress relief anneal heat treatment on bulk residual stresses in the final part. Based on measured interplanar spacing, stresses were calculated at various locations along a single bead, stacked wall deposit. A comparison between an uninterrupted deposited wall and an interrupted, stress-relieved, and annealed deposited wall showed a measureable reduction in residual stress magnitude at the interface with a corresponding shift in stress character into the deposit. This shift changes the interface stresses from purely compressive to partially tensile. The residual stress profile varied along the length of the deposit, and the heat-treatment procedure reduced the overall magnitude of the stress at the interface by 10 through 25 MPa. These results are interpreted in terms of thermal gradients inherent to the process and compared with prior residual stress-characterization studies in additive-manufactured metallic structures.

  15. Residual Stress Analysis in Deep Drawn Twinning Induced Plasticity (TWIP) Steels Using Neutron Diffraction Method

    Science.gov (United States)

    Hong, Seokmin; Lee, Junghoon; Lee, Sunghak; Woo, Wanchuck; Kim, Sung-Kyu; Kim, Hyoung Seop

    2014-04-01

    In Twinning Induced Plasticity (TWIP) steels, delayed fracture occurs due to residual stresses induced during deep drawing. In order to investigate the relation between residual stresses and delayed fracture, in the present study, residual stresses of deep drawn TWIP steels (22Mn-0.6C and 18Mn-2Al-0.6C steels) were investigated using the finite element method (FEM) and neutron diffraction measurements. In addition, the delayed fracture properties were examined by dipping tests of cup specimens in the boiled water. In the FEM analysis, the hoop direction residual stress was highly tensile at cup edge, and the delayed fracture was initiated by the separation of hoop direction and propagated in an axial direction. According to the neutron diffraction analysis, residual stresses in 18Mn-2Al-0.6C steel were about half the residual stresses in 22Mn-0.6C steel. From the residual strain measurement using electron back-scatter diffraction, formation of deformation twins caused a lot of grain rotation and local strain at the grain boundaries and twin boundaries. These local residual strains induce residual stress at boundaries. Al addition in TWIP steels restrained the formation of deformation twins and dynamic strain aging, resulting in more homogeneous stress and strain distributions in cup specimens. Thus, in Al-added TWIP steels, residual stress of cup specimen considerably decreased, and delayed fracture resistance was remarkably improved by the addition of Al in TWIP steels.

  16. Characterization of Residual Stress Effects on Fatigue Crack Growth of a Friction Stir Welded Aluminum Alloy

    Science.gov (United States)

    Newman, John A.; Smith, Stephen W.; Seshadri, Banavara R.; James, Mark A.; Brazill, Richard L.; Schultz, Robert W.; Donald, J. Keith; Blair, Amy

    2015-01-01

    An on-line compliance-based method to account for residual stress effects in stress-intensity factor and fatigue crack growth property determinations has been evaluated. Residual stress intensity factor results determined from specimens containing friction stir weld induced residual stresses are presented, and the on-line method results were found to be in excellent agreement with residual stress-intensity factor data obtained using the cut compliance method. Variable stress-intensity factor tests were designed to demonstrate that a simple superposition model, summing the applied stress-intensity factor with the residual stress-intensity factor, can be used to determine the total crack-tip stress-intensity factor. Finite element, VCCT (virtual crack closure technique), and J-integral analysis methods have been used to characterize weld-induced residual stress using thermal expansion/contraction in the form of an equivalent delta T (change in local temperature during welding) to simulate the welding process. This equivalent delta T was established and applied to analyze different specimen configurations to predict residual stress distributions and associated residual stress-intensity factor values. The predictions were found to agree well with experimental results obtained using the crack- and cut-compliance methods.

  17. Residual stresses in a co-sintered SOC half-cell during post-sintering cooling

    DEFF Research Database (Denmark)

    Charlas, Benoit; Chatzichristodoulou, Christodoulos; Brodersen, Karen

    2014-01-01

    Due to the thermal expansion mismatch between the layers of a Solid Oxide Cell, residual stresses (thermal stresses) develop during the cooling after sintering. Residual stresses can induce cell curvature for asymmetric cells but more importantly they also result in more fragile cells. Depending...

  18. The Microscopic Origin of Residual Stress for Flat Self-Actuating Piezoelectric Cantilevers

    Directory of Open Access Journals (Sweden)

    Hwang Kyo

    2011-01-01

    Full Text Available Abstract In this study, flat piezoelectric microcantilevers were fabricated under low-stress Pb(Zr0.52Ti0.48O3 (PZT film conditions. They were analyzed using the Raman spectrum and wafer curvature methods. Based on the residual stress analysis, we found that a thickness of 1 μm was critical, since stress relaxation starts to occur at greater thicknesses, due to surface roughening. The (111 preferred orientation started to decrease when the film thickness was greater than 1 μm. The d33 value was closely related to the stress relaxation associated with the preferred orientation changes. We examined the harmonic response at different PZT cantilever lengths and obtained a 9.4-μm tip displacement at 3 Vp-p at 1 kHz. These analyses can provide a platform for the reliable operation of piezoelectric microdevices, potentially nanodevice when one needs to have simultaneous control of the residual stress and the piezoelectric properties.

  19. Neutron-diffraction measurements for residual stress analysis in automotive steel gears

    Science.gov (United States)

    Annibali, G.; Bruno, G.; Fiori, F.; Giuliani, A.; Manescu, A.; Marcantoni, M.; Turquier, F.

    Standard production and machining of automotive components is still attractive, although it is not cost-effective if the life of the component has the highest priority. An important parameter to increase the fatigue life of these components is the beneficial introduction of residual stress, especially in the most loaded superficial layers. The aim of the present study is to investigate the residual stress in two steel gears produced from extruded bars cut and machined and then submitted to tempering and nitriding. The results have been compared with those obtained on sintered, nitro-carburised steel gears manufactured using the net-shape forming technique. They show a higher tensile stress level in the bulk of the component with higher carbon and chromium content, that is, a strong influence of nitriding elements. Consequently, in the nitrided layers, the calculated compressive stresses reach relatively high values in an aluminium- and carbon-rich sample. These stresses are sensibly larger than those found in the sintered and nitro-carburised gears, both in the surface and in the bulk.

  20. Novel approaches to determining residual stresses by ultramicroindentation techniques: Application to sandblasted austenitic stainless steel

    International Nuclear Information System (INIS)

    Frutos, E.; Multigner, M.; Gonzalez-Carrasco, J.L.

    2010-01-01

    This research addresses the determination of residual stresses in sandblasted austenitic steel by ultramicroindentation techniques using a sharp indenter, of which the sensitivity to residual stress effects is said to be inferior to that of spherical ones. The introduction of an angular correction in the model of Wang et al. which relates variations in the maximum load to the presence of residual stresses is proposed. Similarly, the contribution to the hardness of grain size refinement and work hardening, developed as a consequence of the severe plastic deformation during blasting, is determined in order to avoid overestimation of the residual stresses. Measurements were performed on polished cross sections along a length of several microns, thus obtaining a profile of the residual stresses. Results show good agreement with those obtained by synchrotron radiation on the same specimens, which validates the method and demonstrates that microindentation using sharp indenters may be sensitive to the residual stress effect.

  1. Novel approaches to determining residual stresses by ultramicroindentation techniques: Application to sandblasted austenitic stainless steel

    Energy Technology Data Exchange (ETDEWEB)

    Frutos, E. [Centro de Bioingenieria, Biomateriales y Nanomedicina, CIBER-BBN, Instituto de Salud Carlos III (Spain)] [Centro Nacional de Investigaciones Metalurgicas, CENIM-CSIC, 28040 Madrid (Spain); Multigner, M. [Centro Nacional de Investigaciones Metalurgicas, CENIM-CSIC, 28040 Madrid (Spain)] [Centro de Bioingenieria, Biomateriales y Nanomedicina, CIBER-BBN, Instituto de Salud Carlos III (Spain); Gonzalez-Carrasco, J.L., E-mail: jlg@cenim.csic.es [Centro Nacional de Investigaciones Metalurgicas, CENIM-CSIC, 28040 Madrid (Spain)] [Centro de Bioingenieria, Biomateriales y Nanomedicina, CIBER-BBN, Instituto de Salud Carlos III (Spain)

    2010-07-15

    This research addresses the determination of residual stresses in sandblasted austenitic steel by ultramicroindentation techniques using a sharp indenter, of which the sensitivity to residual stress effects is said to be inferior to that of spherical ones. The introduction of an angular correction in the model of Wang et al. which relates variations in the maximum load to the presence of residual stresses is proposed. Similarly, the contribution to the hardness of grain size refinement and work hardening, developed as a consequence of the severe plastic deformation during blasting, is determined in order to avoid overestimation of the residual stresses. Measurements were performed on polished cross sections along a length of several microns, thus obtaining a profile of the residual stresses. Results show good agreement with those obtained by synchrotron radiation on the same specimens, which validates the method and demonstrates that microindentation using sharp indenters may be sensitive to the residual stress effect.

  2. A High-Frequency Eddy Current Inspection System and Its Application to the Residual Stress Characterization

    International Nuclear Information System (INIS)

    Nakagawa, N.; Lee, C.; Shen, Y.

    2006-01-01

    This paper reports on an on-going project toward developing electromagnetic residual-stress characterization method. Specifically, we present recent work on an eddy current technique and model-based inversion method, specific to nickel-based superalloys. In our approach, we treat residual stress measurements essentially as a 'layer-substrate' problem (a shot-peened layer on an alloy substrate), to which the swept-frequency EC technique is applicable. To this end, a high-sensitivity eddy current system with operating frequency up to 50MHz has been recently developed and validated. We present a description of our instrumentation that includes proprietary probes fabricated by the PCB technology, and laboratory-grade instruments under software control. The paper also describes the experimental procedure for performance studies, supported by preliminary data that distinguish clearly between surfaces before and after shot-peening for nickel-based alloys. In addition, we present forward and inverse model validations which will determine their reliability in the subsequent use in model-based residual stress profile inversion

  3. On the Influence of Laser Cladding and Post-processing Strategies on Residual Stresses in Steel Specimens

    Science.gov (United States)

    Köhler, H.; Rajput, R.; Khazan, P.; Kornmeier, J. Rebelo

    Thermal cycles during laser cladding can alter mechanical properties of the original part significantly. In case of cyclically loaded parts residual stresses are suspected to be a property strongly determining fatigue life. Therefore, in this paper the influence of processing and post-processing strategies on resulting residual stresses are determined by neutron-diffraction. A low-alloy as well as a high-alloy steel have been considered within this study, both cladded with the Co-based superalloy Stellite 21. Processing speed and post-treatment by laser annealing and by deep rolling strategies have been tested. Residual stresses in low-alloyed steel show high sensitivity on applied treatment strategies. In the present study only deep rolling induced compressive residual stress close to the part surface. In high-alloy steel compressive stress in this area resulted directly after laser cladding, where its magnitude depends on processing speed. A compressive residual stress statewhich is suspected to be beneficial for fatigue strength could be achieved at the two representative steels.

  4. Research on residual stress inside Fe-Mn-Si shape memory alloy coating by laser cladding processing

    Science.gov (United States)

    Ju, Heng; Lin, Cheng-xin; Zhang, Jia-qi; Liu, Zhi-jie

    2016-09-01

    The stainless Fe-Mn-Si shape memory alloy (SMA) coating was prepared on the surface of AISI 304 stainless steel. The principal residual stress measured by the mechanical hole-drilling method indicates that the Fe-Mn-Si SMA cladding specimen possesses a lower residual stress compared with the 304 stainless steel cladding specimen. The mean stress values of the former and the latter on 10-mm-thick substrate are 4.751 MPa and 7.399 MPa, respectively. What's more, their deformation values on 2-mm-thick substrate are about 0° and 15°, respectively. Meanwhile, the variation trend and the value of the residual stress simulated by the ANSYS finite element software consist with experimental results. The X-ray diffraction (XRD) pattern shows ɛ-martensite exists in Fe-Mn-Si SMA coating, which verifies the mechanism of low residual stress. That's the γ→ɛ martensite phase transformation, which relaxes the residual stress of the specimen and reduces its deformation in the laser cladding processing.

  5. Numerical methods for calculating thermal residual stresses and hydrogen diffusion

    International Nuclear Information System (INIS)

    Leblond, J.B.; Devaux, J.; Dubois, D.

    1983-01-01

    Thermal residual stresses and hydrogen concentrations are two major factors intervening in cracking phenomena. These parameters were numerically calculated by a computer programme (TITUS) using the FEM, during the deposition of a stainless clad on a low-alloy plate. The calculation was performed with a 2-dimensional option in four successive steps: thermal transient calculation, metallurgical transient calculation (determination of the metallurgical phase proportions), elastic-plastic transient (plain strain conditions), hydrogen diffusion transient. Temperature and phase dependence of hydrogen diffusion coefficient and solubility constant. The following results were obtained: thermal calculations are very consistent with experiments at higher temperatures (due to the introduction of fusion and solidification latent heats); the consistency is not as good (by 70 degrees) for lower temperatures (below 650 degrees C); this was attributed to the non-introduction of gamma-alpha transformation latent heat. The metallurgical phase calculation indicates that the heat affected zone is almost entirely transformed into bainite after cooling down (the martensite proportion does not exceed 5%). The elastic-plastic calculations indicate that the stresses in the heat affected zone are compressive or slightly tensile; on the other hand, higher tensile stresses develop on the boundary of the heat affected zone. The transformation plasticity has a definite influence on the final stress level. The return of hydrogen to the clad during the bainitic transformation is but an incomplete phenomenon and the hydrogen concentration in the heat affected zone after cooling down to room temperature is therefore sufficient to cause cold cracking (if no heat treatment is applied). Heat treatments are efficient in lowering the hydrogen concentration. These results enable us to draw preliminary conclusions on practical means to avoid cracking. (orig.)

  6. Residual stresses analysis of friction stir welding using one-way FSI simulation

    International Nuclear Information System (INIS)

    Kang, Sung Wook; Jang, Beom Seon; Song, Ha Cheol

    2015-01-01

    When certain mechanisms, such as plastic deformations and temperature gradients, occur and are released in a structure, stresses remain because of the shape of the structure and external constraints. These stresses are referred to as residual stresses. The base material locally expands during heating in the welding process. When the welding is completed and cooled to room temperature, the residual stresses are left at nearly the yield strength level. In the case of friction stir welding, the maximum temperature is 80% to 90% of the melting point of the materials. Thus, the residual stresses in the welding process are smaller than those in other fusion welding processes; these stresses have not been considered previously. However, friction stir welding residual stresses are sometimes measured at approximately 70% or above. These residual stresses significantly affect fatigue behavior and lifetime. The present study investigates the residual stress distributions in various welding conditions and shapes of friction stir welding. In addition, the asymmetric feature is considered in temperature and residual stress distribution. Heat transfer analysis is conducted using the commercial computational fluid dynamics program Fluent, and results are used in the finite element structural analysis with the ANSYS Multiphysics software. The calculated residual stresses are compared with experimental values using the X-ray diffraction method.

  7. Variation behavior of residual stress distribution by manufacturing processes in welded pipes of austenitic stainless steel

    International Nuclear Information System (INIS)

    Ihara, Ryohei; Hashimoto, Tadafumi; Mochizuki, Masahito

    2012-01-01

    Stress corrosion cracking (SCC) has been observed near heat affected zone (HAZ) of primary loop recirculation pipes made of low-carbon austenitic stainless steel type 316L in the nuclear power plants. For the non-sensitization material, residual stress is the important factor of SCC, and it is generated by machining and welding. In the actual plants, welding is conducted after machining as manufacturing processes of welded pipes. It could be considered that residual stress generated by machining is varied by welding as a posterior process. This paper presents residual stress variation due to manufacturing processes of pipes using X-ray diffraction method. Residual stress distribution due to welding after machining had a local maximum stress in HAZ. Moreover, this value was higher than residual stress generated by welding or machining. Vickers hardness also had a local maximum hardness in HAZ. In order to clarify hardness variation, crystal orientation analysis with EBSD method was performed. Recovery and recrystallization were occurred by welding heat near the weld metal. These lead hardness decrease. The local maximum region showed no microstructure evolution. In this region, machined layer was remained. Therefore, the local maximum hardness was generated at machined layer. The local maximum stress was caused by the superposition effect of residual stress distributions due to machining and welding. Moreover, these local maximum residual stress and hardness are exceeded critical value of SCC initiation. In order to clarify the effect of residual stress on SCC initiation, evaluation including manufacturing processes is important. (author)

  8. Residual stress development and relief in high strength aluminium alloys using standard and retrogression thermal treatments

    OpenAIRE

    Robinson, J.S; Tanner, D.A

    2003-01-01

    peer-reviewed Residual stresses develop in the aluminium alloy 7010 when the material is quenched from the solution heat treatment temperature. Residual stress measurements have been made using the X-ray diffraction technique and a longitudinal split sawcut method to determine the magnitude of residual stress that develops in specimens sectioned from large open die forgings as a result of (a) quenching these specimens into water at different temperatures, and (b) cold water quenching from ...

  9. Determination of residual stress within complex-shaped coarse-grained cobalt-chrome biomedical castings

    OpenAIRE

    Conroy, Brian P; Tanner, David A

    2016-01-01

    peer-reviewed ASTM F75 femoral knee implant casting components distort during manufacture due to residual stress re-distribution or inducement. These castings pose a number of challenges for residual stress determination methods; they have a complex geometry, their micro-structure is inhomogeneous, they work-harden rapidly and they have a coarse, elastically-anisotropic grain structure. The contour method is anticipated to be the most promising residual stress determination technique. X-ra...

  10. Several methods applied to measuring residual stress in a known specimen

    International Nuclear Information System (INIS)

    Prime, M.B.; Rangaswamy, P.; Daymond, M.R.; Abelin, T.G.

    1998-01-01

    In this study, a beam with a precisely known residual stress distribution provided a unique experimental opportunity. A plastically bent beam was carefully prepared in order to provide a specimen with a known residual stress profile. 21Cr-6Ni-9Mn austenitic stainless steel was obtained as 43 mm square forged stock. Several methods were used to determine the residual stresses, and the results were compared to the known values. Some subtleties of applying the various methods were exposed

  11. Final Report: Characterization of Canister Mockup Weld Residual Stresses

    Energy Technology Data Exchange (ETDEWEB)

    Enos, David [Sandia National Lab. (SNL-NM), Albuquerque, NM (United States); Bryan, Charles R. [Sandia National Lab. (SNL-NM), Albuquerque, NM (United States)

    2016-12-01

    Stress corrosion cracking (SCC) of interim storage containers has been indicated as a high priority data gap by the Department of Energy (DOE) (Hanson et al., 2012), the Electric Power Research Institute (EPRI, 2011), the Nuclear Waste Technical Review Board (NWTRB, 2010a), and the Nuclear Regulatory Commission (NRC, 2012a, 2012b). Uncertainties exist in terms of the environmental conditions that prevail on the surface of the storage containers, the stress state within the container walls associated both with weldments as well as within the base metal itself, and the electrochemical properties of the storage containers themselves. The goal of the work described in this document is to determine the stress states that exists at various locations within a typical storage canister by evaluating the properties of a full-diameter cylindrical mockup of an interim storage canister. This mockup has been produced using the same manufacturing procedures as the majority of the fielded spent nuclear fuel interim storage canisters. This document describes the design and procurement of the mockup and the characterization of the stress state associated with various portions of the container. It also describes the cutting of the mockup into sections for further analyses, and a discussion of the potential impact of the results from the stress characterization effort.

  12. Relaxation of Shot-Peened Residual Stresses Under Creep Loading (Preprint)

    National Research Council Canada - National Science Library

    Buchanan, Dennis J; John, Reji; Brockman, Robert A

    2008-01-01

    .... Compressive residual stresses retard initiation and growth of fatigue cracks. During the component loading history, loading, or during elevated temperature static loading, such as thermal exposure and creep...

  13. The effect of initial stress induced during the steel manufacturing process on the welding residual stress in multi-pass butt welding

    Directory of Open Access Journals (Sweden)

    Jeong-ung Park

    2018-03-01

    Full Text Available A residual stress generated in the steel structure is broadly categorized into initial residual stress during manufacturing steel material, welding residual stress caused by welding, and heat treatment residual stress by heat treatment. Initial residual stresses induced during the manufacturing process is combined with welding residual stress or heat treatment residual stress, and remained as a final residual stress. Because such final residual stress affects the safety and strength of the structure, it is of utmost importance to measure or predict the magnitude of residual stress, and to apply this point on the design of the structure. In this study, the initial residual stress of steel structures having thicknesses of 25 mm and 70 mm during manufacturing was measured in order to investigate initial residual stress (hereinafter, referred to as initial stress. In addition, thermal elastic plastic FEM analysis was performed with this initial condition, and the effect of initial stress on the welding residual stress was investigated. Further, the reliability of the FE analysis result, considering the initial stress and welding residual stress for the steel structures having two thicknesses, was validated by comparing it with the measured results. In the vicinity of the weld joint, the initial stress is released and finally controlled by the weld residual stress. On the other hand, the farther away from the weld joint, the greater the influence of the initial stress. The range in which the initial stress affects the weld residual stress was not changed by the initial stress. However, in the region where the initial stress occurs in the compressive stress, the magnitude of the weld residual compressive stress varies with the compression or tension of the initial stress. The effect of initial stress on the maximum compression residual stress was far larger when initial stress was considered in case of a thickness of 25 mm with a value of 180

  14. Neutron diffraction measurements for the determination of heat treatment effectiveness in generating compressive residual stress in an automotive crown gear

    International Nuclear Information System (INIS)

    Albertini, G.; Fiori, F.; Girardin, E.; Giuliani, A.; Pyzalla, A.; Quadrini, E.

    1999-01-01

    Complete text of publication follows. Thermal austenitizing and tempering treatments are being developed in automotive industry to prevent crack initiation and avoid crack propagation, especially in components where stress intensity factors influence the stress field and then the fatigue life of the component itself. This is the case of crown gears, where the teeth root undergoes frequently to cracking when tensile residual stresses are present at the surface, as typical loads are impulsive and very high. The sign reversal of these stresses is the aim of austenitizing and tempering treatments. In this work residual stress measurements carried out at HMI-BENSC are presented, in a UNI55Cr3 steel crown gear submitted to such kind of treatments, performed with a new multi-frequency induction technique whose effectiveness is checked. (author)

  15. Evaluation of the residue from microset on various metal surfaces.

    Energy Technology Data Exchange (ETDEWEB)

    Brumbach, Michael Todd

    2011-04-01

    Fast-curing impression materials are sometimes used to cast negative-mold replications of physical defects on material surfaces. The negative-mold impressions can then be used for further measurements to record the nature of the defect. These impression materials have been designed to cure quickly, and with very low adhesion, so that they can be easily removed from the surface leaving little residual contamination. Unfortunately, some contaminant is retained by the substrate material. This investigation seeks to identify the composition and quantity of the remaining material upon removal of Microset Synthetic Rubber Replicating Compound from several material surfaces. Coe-Flex was used as a relative comparison to Microset. On fifteen different substrate materials the Microset leaves no visible trace of contaminant, however, X-ray photoelectron spectroscopy shows evidence of a thin silicone-based contaminant film of approximately 2 nm thickness.

  16. Neutron and ultrasonic determination of residual stress in an aluminum ring-plug

    International Nuclear Information System (INIS)

    Prask, H.J.; Gnaeupel-Herold, T.; Clark, A.V.; Hehman, C.S.; Nguyen, T.N.

    2000-01-01

    Stress is a principal cause of material failure. This has been a well-recognized problem for decades, yet--in general--neutron diffraction remains the only way to measure sub-surface residual stresses without destroying the component. A field-portable ultrasonic strain-meter is being developed at NIST (Boulder) to determine residual stresses in engineering specimens, nondestructively. To test this and other techniques an array of stress-measurement standards are being prepared. These will be characterized by neutron diffraction and then used to evaluate, quantitatively, the potential of new methods. The first standard specimen produced for this purpose is a large shrink-fit ring-plug of 2024 aluminum (305 mm OD, 25.4 mm thick, 101.6 mm diameter plug). Because of large grain size, a sample-rotation averaging technique was developed to make reliable neutron measurements possible. A comparison of the neutron diffraction and ultrasonic results for this specimen will be presented, along with strain gauge results

  17. Mapping residual stresses in PbWO$_{4}$ crystals using photo-elastic analysis

    CERN Document Server

    Lebeau, Michel; Majni, G; Paone, N; Pietroni, P; Rinaldi, D

    2005-01-01

    Large scintillating crystals are affected by internal stresses induced by the crystal growth temperature gradient remanence. Cutting boules (ingots) into finished crystal shapes allows for a partial tension relaxation but residual stresses remain the main cause of breaking. Quality control of residual stresses is essential in the application of Scintillating Crystals to high-energy physics calorimeters (e.g. CMS ECAL at CERN LHC). In this context the industrial process optimisation towards stress reduction is mandatory. We propose a fast technique for testing samples during the production process in order to evaluate the residual stress distribution after the first phases of mechanical processing. We mapped the stress distribution in PbWO/sub 4/slabs cut from the same production boule. The analysis technique is based on the stress intensity determination using the photo-elastic properties of the samples. The stress distribution is mapped in each sample. The analysis shows that there are regions of high residu...

  18. Stress Free Temperature Testing and Residual Stress Calculations on Out-of-Autoclave Composites

    Science.gov (United States)

    Cox, Sarah; Tate, LaNetra C.; Danley, Susan; Sampson, Jeff; Taylor, Brian; Miller, Sandi

    2012-01-01

    Future launch vehicles will require the incorporation large composite parts that will make up primary and secondary components of the vehicle. NASA has explored the feasibility of manufacturing these large components using Out-of-Autoclave impregnated carbon fiber composite systems through many composites development projects. Most recently, the Composites for Exploration Project has been looking at the development of a 10 meter diameter fairing structure, similar in size to what will be required for a heavy launch vehicle. The development of new material systems requires the investigation of the material properties and the stress in the parts. Residual stress is an important factor to incorporate when modeling the stresses that a part is undergoing. Testing was performed to verify the stress free temperature with two-ply asymmetric panels. A comparison was done between three newly developed out of autoclave IM7 /Bismalieimide (BMI) systems. This paper presents the testing results and the analysis performed to determine the residual stress of the materials.

  19. Residual Stress Estimation and Fatigue Life Prediction of an Autofrettaged Pressure Vessel

    Energy Technology Data Exchange (ETDEWEB)

    Song, Kyung Jin; Kim, Eun Kyum; Koh, Seung Kee [Kunsan Nat’l Univ., Kunsan (Korea, Republic of)

    2017-09-15

    Fatigue failure of an autofrettaged pressure vessel with a groove at the outside surface occurs owing to the fatigue crack initiation and propagation at the groove root. In order to predict the fatigue life of the autofrettaged pressure vessel, residual stresses in the autofrettaged pressure vessel were evaluated using the finite element method, and the fatigue properties of the pressure vessel steel were obtained from the fatigue tests. Fatigue life of a pressure vessel obtained through summation of the crack initiation and propagation lives was calculated to be 2,598 cycles for an 80% autofrettaged pressure vessel subjected to a pulsating internal pressure of 424 MPa.

  20. An Assessment of Subsurface Residual Stress Analysis in SLM Ti-6Al-4V

    Directory of Open Access Journals (Sweden)

    Tatiana Mishurova

    2017-03-01

    Full Text Available Ti-6Al-4V bridges were additively fabricated by selective laser melting (SLM under different scanning speed conditions, to compare the effect of process energy density on the residual stress state. Subsurface lattice strain characterization was conducted by means of synchrotron diffraction in energy dispersive mode. High tensile strain gradients were found at the frontal surface for samples in an as-built condition. The geometry of the samples promotes increasing strains towards the pillar of the bridges. We observed that the higher the laser energy density during fabrication, the lower the lattice strains. A relief of lattice strains takes place after heat treatment.

  1. Quantitative estimation of nonmonotonic residual stress depth-profiles using an extended Kypris-Jiles model of the magnetic Barkhausen noise spectrum

    Science.gov (United States)

    Lasaosa, Aitor; Gurruchaga, Kizkitza; Arizti, Fernando; Martínez-de-Guerenu, Ane

    2018-01-01

    Using nondestructive techniques to quantitatively estimate residual stresses along the depth is necessary to improve the ability to predict the real fatigue life of pieces for many applications. Magnetic Barkhausen noise has been proven to successfully estimate the residual stress at the surface produced by machining, plastic deformation, phase transformation or surface treatments such as shot peening, also allowing one to obtain information of the residual stress depth-profile in shot peened pieces which presented similar depth-profile shapes. However, residual stress depth-profiles with nonmonotonic or different shapes have not been successfully estimated. In the present study, an extended approach is developed in order to estimate these stresses independent of the shape of the residual stress depth-profile. The approach proposed here improves an existing model of the Barkhausen noise spectrum (Kypris-Jiles model) by adding the effect of the attenuation of the applied magnetic field on the Barkhausen noise. This extended approach is used to estimate the residual stress depth-profiles of samples with different depth-profiles using a calibration process. The approach is validated by estimating the residual stress depth-profiles, with errors smaller than 70 MPa in a depth of 130 μm, in all the samples studied.

  2. Effects of shot-peening residual stresses on the fracture and crack-growth properties of D6AC steel

    Science.gov (United States)

    Elber, W.

    1974-01-01

    The fracture strength and cyclic crack-growth properties of surface-flawed, shot-peened D6AC steel plate were investigated. For short crack lengths (up to 1.5 mm) simple linear elastic fracture mechanics - based only on applied loading - did not predict the fracture strengths. Also, Paris' Law for cyclic crack growth did not correlate the crack-growth behavior. To investigate the effect of shot-peening, additional fracture and crack-growth tests were performed on material which was precompressed to remove the residual stresses left by the shot-peening. Both tests and analysis show that shot-peening residual stresses influence the fracture and crack-growth properties of the material. This report presents the analytical method of compensating for residual stresses and the fracture and cyclic crack-growth test results and predictions.

  3. The effects of shot-peening residual stresses on the fracture and crack growth properties of D6AC steel

    Science.gov (United States)

    Elber, W.

    1973-01-01

    The fracture strength and cyclic crack-growth properties of surface-flawed, shot-peened D6AC steel plate were investigated. For short crack lengths (up to 1.5mm) simple linear elastic fracture mechanics - based only on applied loading - did not predict the fracture strengths. Also, Paris' Law for cyclic crack growth did not correlate the crack-growth behavior. To investigate the effect of shot-peening, additional fracture and crack-growth tests were performed on material which was precompressed to remove the residual stresses left by the shot-peening. Both tests and analysis show that the shot-peening residual stresses influence the fracture and crack-growth properties of the material. The analytical method of compensating for residual stresses and the fracture and cyclic crack-growth test results and predictions are presented.

  4. The Effect of Creep on the Residual Stresses Generated During Silicon Sheet Growth

    Science.gov (United States)

    Hutchinson, J. W.; Lambropoulos, J. C.

    1984-01-01

    The modeling of stresses generated during the growth of thin silicon sheets at high speeds is an important part of the EFG technique since the experimental measurement of the stresses is difficult and prohibitive. The residual stresses which arise in such a growth process lead to serious problems which make thin Si ribbons unsuitable for fabrication. The constitutive behavior is unrealistic because at high temperature (close to the melting point) Si exhibits considerable creep which significantly relaxes the residual stresses. The effect of creep on the residual stresses generated during the growth of Si sheets at high speeds was addressed and the basic qualitative effect of creep are reported.

  5. Residual stress distribution in steel butt welds measured using neutron and synchrotron diffraction.

    Science.gov (United States)

    Paradowska, A M; Price, J W H; Finlayson, T R; Lienert, U; Walls, P; Ibrahim, R

    2009-03-25

    70 keV synchrotron radiation and thermal neutrons have been employed to investigate the residual stress characteristics in a fully restrained, steel, butt weld. The focus is on the values of the subsurface and through-thickness strain/stress variation in the middle of the weld. The advantages and limitations of the techniques have been addressed, in relation to the gauge volume, the stress-free reference sample and positioning. The measurement of residual stress around the weld achieved in this work significantly improves the resolution at which residual stress in welded components has been determined.

  6. On Residual Stresses in Resistance Spot-Welded Aluminum Alloy 6061-T6: Experimental and Numerical Analysis

    Science.gov (United States)

    Afshari, D.; Sedighi, M.; Karimi, M. R.; Barsoum, Z.

    2013-12-01

    In this study, an electro-thermal-structural-coupled finite element (FE) model and x-ray diffraction residual stress measurements have been utilized to analyze distribution of residual stresses in an aluminum alloy 6061-T6 resistance spot-welded joint with 2-mm-thickness sheet. Increasing the aluminum sheet thickness to more than 1 mm leads to creating difficulty in spot-welding process and increases the complexity of the FE model. The electrical and thermal contact conductances, as mandatory factors are applied in contact areas of electrode-workpiece and workpiece-workpiece to resolve the complexity of the FE model. The physical and mechanical properties of the material are defined as thermal dependent to improve the accuracy of the model. Furthermore, the electrodes are removed after the holding cycle using the birth-and-death elements method. The results have a good agreement with experimental data obtained from x-ray diffraction residual stress measurements. However, the highest internal tensile residual stress occurs in the center of the nugget zone and decreases toward nugget edge; surface residual stress increases toward the edge of the welding zone and afterward, the area decreases slightly.

  7. Evaluation of residual stress distribution of butt-weld pipe and redistribution behavior with crack extension using neutron diffraction method

    International Nuclear Information System (INIS)

    Okido, Shinobu; Hayashi, Makoto; Minakawa, Nobuaki; Morii, Yukio; Ando, Kotoji

    2005-01-01

    Residual stress is known to be redistributed as a result of crack extension. The neutron diffraction method was used to evaluate this residual stress redistribution, using a specimen consisting of a butt-weld-jointed pipe made of type-304 austenitic stainless steel (inner diameter φ=97.1 mm, thickness t=8.9mm). Half-elliptical cracks were introduced by an electrical discharge machining at the inner surface of a heat-affected zone. The ratios of a/t, for crack depth a and specimen thickness t, were 0.25 and 0.5, with aspect ratios a/c, for crack half-length c, of 0.1 and 0.5 Comparing the residual stress distribution before and after the crack introduction showed that although the residual stress distribution along the line of the ligament at the deepest point of the crack changed slightly in front of the crack tip, it did not change throughout the ligament. This result shows that residual stress redistributes through-out in the whole crack tip region, including the width of the crack. (author)

  8. Analysis of shot-peening and residual stress relaxation in the nickel-based superalloy RR1000

    International Nuclear Information System (INIS)

    Foss, B.J.; Gray, S.; Hardy, M.C.; Stekovic, S.; McPhail, D.S.; Shollock, B.A.

    2013-01-01

    This work assesses the residual stress relaxation of the nickel-based alloy RR1000 due to thermal exposure and dwell-fatigue loading. A number of different characterization methods, including X-ray residual stress analysis, electron back-scattered diffraction, microhardness testing and focused ion beam secondary electron imaging, contributed to a detailed study of the shot-peened region. Thermal exposure at 700 °C resulted in a large reduction in the residual stresses and work-hardening effects in the alloy, but the subsurface remained in a beneficial compressive state. Oxidizing environments caused recrystallization in the near surface, but did not affect the residual stress-relaxation behaviour. Dwell-fatigue loading caused the residual stresses to return to approximately zero at nearly all depths. This work forms part of an ongoing investigation to determine the effects of shot-peening in this alloy with the motivation to improve the fatigue and oxidation resistance at 700 °C

  9. Numerical modeling of residual stresses generation due to 316L turning. A new experimental and numerical approach

    International Nuclear Information System (INIS)

    Valiorgue, F.

    2008-12-01

    The main goal of this thesis proposed by AREVA NP is to predict the residual stresses induced by finishing turning of AISI 316L. The numerical model is simulating the residual stresses generation with a new approach by applying directly equivalent thermo-mechanical loadings onto the finished work piece surface without modeling the chip removal process. Thus, this study is divided in two complementary main subsections. On one hand, an experimental campaign is carried out to record data and to compute thermomechanical loadings. This task is made using the AREVA NP parameters. On the other hand numerical models are set up using previous measured values. They are made to reproduce the residual stresses generation by applying and moving the thermo mechanical loadings. The study leads to interesting results because the shapes of the residual stresses curves agree with previous works concerning this topic and with XRD measured residual stresses. The new approach seems to be pertinent because it is possible to simulate several tool passages like no other numerical model. (author)

  10. An accurate method for determining residual stresses with magnetic non-destructive techniques in welded ferromagnetic steels

    Science.gov (United States)

    Vourna, P.

    2016-03-01

    The scope of the present research work was to investigate the proper selection criteria for developing a suitable methodology for the accurate determination of residual stresses existing in welded parts. Magnetic non-destructive testing took place by the use of two magnetic non-destructive techniques: by the measurement of the magnetic Barkhausen noise and by the evaluation of the magnetic hysteresis loop parameters. The spatial distribution of residual stresses in welded metal parts by both non-destructive magnetic methods and two diffraction methods was determined. The conduction of magnetic measurements required an initial calibration of ferromagnetic steels. Based on the examined volume of the sample, all methods used were divided into two large categories: the first one was related to the determination of surface residual stress, whereas the second one was related to bulk residual stress determination. The first category included the magnetic Barkhausen noise and the X-ray diffraction measurements, while the second one included the magnetic permeability and the neutron diffraction data. The residual stresses determined by the magnetic techniques were in a good agreement with the diffraction ones.

  11. In Situ Tensile Deformation and Residual Stress Measurement by Neutron Diffraction in Modified 9Cr-1Mo Steel

    Science.gov (United States)

    Shrestha, Triratna; Charit, Indrajit; Potirniche, Gabriel

    2015-12-01

    The deformation behavior of monolithic modified 9Cr-1Mo (Grade 91) steel during uniaxial tensile loading was studied using the in situ neutron diffraction technique. The residual stress distribution across gas tungsten arc welds in the Grade 91 steel was measured by the time-of-flight neutron diffraction method using the SMARTS diffractometer at Lujan Neutron Scattering Center, Los Alamos National Laboratory. Grade 91 plates were welded using the gas tungsten arc welding (GTAW) technique. The load sharing by different grain orientations was observed during the tensile loading. The residual stresses along three orthogonal directions were determined at the mid-thickness, 4.35 and 2.35 mm below the surface of both the as-welded and post-weld heat-treated plates. The residual stresses of the as-welded plates were compared with those of the post-weld heat-treated plates. The post-weld heat treatment significantly reduced the residual stress level in the base metal, the heat-affected zone, and the weld zone. Vickers microhardness across the weld zone of the as-welded and post-weld heat-treated specimens was evaluated and correlated with the observed residual stress profile and microstructure.

  12. Verification and Validation of Residual Stresses in Bi-Material Composite Rings

    Energy Technology Data Exchange (ETDEWEB)

    Nelson, Stacy Michelle [Sandia National Lab. (SNL-CA), Livermore, CA (United States); Hanson, Alexander Anthony [Sandia National Lab. (SNL-CA), Livermore, CA (United States); Briggs, Timothy [Sandia National Lab. (SNL-CA), Livermore, CA (United States); Werner, Brian T. [Sandia National Lab. (SNL-CA), Livermore, CA (United States)

    2017-07-01

    Process-induced residual stresses commonly occur in composite structures composed of dissimilar materials. These residual stresses form due to differences in the composite materials’ coefficients of thermal expansion and the shrinkage upon cure exhibited by polymer matrix materials. Depending upon the specific geometric details of the composite structure and the materials’ curing parameters, it is possible that these residual stresses could result in interlaminar delamination or fracture within the composite. Therefore, the consideration of potential residual stresses is important when designing composite parts and their manufacturing processes. However, the experimental determination of residual stresses in prototype parts can be time and cost prohibitive. As an alternative to physical measurement, it is possible for computational tools to be used to quantify potential residual stresses in composite prototype parts. Therefore, the objectives of the presented work are to demonstrate a simplistic method for simulating residual stresses in composite parts, as well as the potential value of sensitivity and uncertainty quantification techniques during analyses for which material property parameters are unknown. Specifically, a simplified residual stress modeling approach, which accounts for coefficient of thermal expansion mismatch and polymer shrinkage, is implemented within the Sandia National Laboratories’ developed SIERRA/SolidMechanics code. Concurrent with the model development, two simple, bi-material structures composed of a carbon fiber/epoxy composite and aluminum, a flat plate and a cylinder, are fabricated and the residual stresses are quantified through the measurement of deformation. Then, in the process of validating the developed modeling approach with the experimental residual stress data, manufacturing process simulations of the two simple structures are developed and undergo a formal verification and validation process, including a mesh

  13. Measuring residual stress in ceramic zirconia-porcelain dental crowns by nanoindentation.

    Science.gov (United States)

    Zhang, Y; Allahkarami, M; Hanan, J C

    2012-02-01

    Residual stress plays a critical role in failure of ceramic dental crowns. The magnitude and distribution of residual stress in the crown system are largely unknown. Determining the residual stress quantitatively is challenging since the crown has such complex contours and shapes. This work explored the feasibility and validity of measuring residual stress of zirconia and porcelain in ceramic crowns by nanoindentation. Nanoindentation tests were performed on the cross-section of a crown for both porcelain and zirconia along four critical locations: the thickest, thinnest and medium porcelain thicknesses. Zirconia and porcelain pieces, chipped off from the crown and annealed at 400 °C, were used as reference samples. The residual stress was determined by comparing the measured hardness of the stressed sample with that of the reference sample. Nanoindentation impression images were acquired through a scanning probe microscope (SPM) equipped with a Hysitron Triboindenter. Zirconia showed large pile-up. Residual stress is determined along the thickness of crowns at the chosen locations for both porcelain and zirconia. The measured results were compared with the results from X-ray diffraction (XRD) and finite element modeling (FEM). Results show there are large amounts of residual stresses in the dental crown and their magnitude differs between locations due to the complex shape of the crown. The average residual stress readings were as high as -637 MPa and 323 MPa for zirconia and porcelain respectively. Copyright © 2011 Elsevier Ltd. All rights reserved.

  14. Rapid surface enhanced Raman scattering detection method for chloramphenicol residues

    Science.gov (United States)

    Ji, Wei; Yao, Weirong

    2015-06-01

    Chloramphenicol (CAP) is a widely used amide alcohol antibiotics, which has been banned from using in food producing animals in many countries. In this study, surface enhanced Raman scattering (SERS) coupled with gold colloidal nanoparticles was used for the rapid analysis of CAP. Density functional theory (DFT) calculations were conducted with Gaussian 03 at the B3LYP level using the 3-21G(d) and 6-31G(d) basis sets to analyze the assignment of vibrations. Affirmatively, the theoretical Raman spectrum of CAP was in complete agreement with the experimental spectrum. They both exhibited three strong peaks characteristic of CAP at 1104 cm-1, 1344 cm-1, 1596 cm-1, which were used for rapid qualitative analysis of CAP residues in food samples. The use of SERS as a method for the measurements of CAP was explored by comparing use of different solvents, gold colloidal nanoparticles concentration and absorption time. The method of the detection limit was determined as 0.1 μg/mL using optimum conditions. The Raman peak at 1344 cm-1 was used as the index for quantitative analysis of CAP in food samples, with a linear correlation of R2 = 0.9802. Quantitative analysis of CAP residues in foods revealed that the SERS technique with gold colloidal nanoparticles was sensitive and of a good stability and linear correlation, and suited for rapid analysis of CAP residue in a variety of food samples.

  15. Measurement of residual stress in textured Al alloy by neutron diffraction method

    International Nuclear Information System (INIS)

    Okido, S.; Hayashi, M.; Tanaka, K.; Akiniwa, Y.; Minakawa, N.; Morii, Y.

    1999-01-01

    Residual stress generated in a shrunken aluminum alloy specimen, which was prepared for the round robin test conducted by VAMAS (Versailles Project on Advanced Materials and Standards) TWA-20 organized for the purpose of standardizing residual stress measurement methods, was evaluated by a neutron diffraction method. The main purpose of the round robin test was to assess the reproducibility of data obtained with the measurement facilities of the participants. The general standard of the Residual Stress Analyzer (RESA) constructed in the Japan Atomic Energy Research Institute was verified from the measured residual strains, which were equivalent to the values calculated by FEM and values measured by the research facilities in North America. Residual stress was calculated from residual strain in three perpendicular directions. The diffraction intensities were dependent on measurement directions since the prepared specimen possessed texture. Diffraction profiles in directions having a weak diffraction intensity caused an inaccurate evaluation of the residual stress. To solve this problem, a new method for evaluating residual stress with respect to diffraction plane dependency of the elastic constant was applied. The diffraction plane giving the highest intensity among 110, 200, and 220 diffraction was used to evaluate the residual strain in each of three directions. The residual strain obtained on the used diffraction plane was converted to the equivalent strain for the defined diffraction plane using the ratio of elastic constants of these two planes. The developed evaluation method achieved highly accurate measurement and remarkable efficiency in the measurement process. (author)

  16. Effect of residual stress on the nanoindentation response of (100) copper single crystal

    International Nuclear Information System (INIS)

    Zhu, Li-na; Xu, Bin-shi; Wang, Hai-dou; Wang, Cheng-biao

    2012-01-01

    Experimental measurements were used to investigate the effect of residual stress on the nanoindentation of (100) copper single crystal. Equi-biaxial tensile and compressive stresses were applied to the copper single crystal using a special designed apparatus. It was found that residual stresses greatly affected peak load, curvature of the loading curve, elastically recovered depth, residual depth, indentation work, pile-up amount and contact area. The Suresh and Giannakopoulos and Lee and Kwon methods were used to calculate the residual stresses from load-depth data and morphology observation of nanoindents using atomic force microscopy. Comparison of the obtained results with stress values from strain gage showed that the residual stresses analyzed from the Suresh and Giannakopoulos model agreed well with the applied stresses. -- Highlights: ► Residual stresses greatly affected various nanoindentation parameters. ► The contact area can be accurately measured from AFM observation. ► The residual stresses analyzed from the S and G model agreed well with applied stresses.

  17. Residual stress profiles in veneering ceramic on Y-TZP, alumina and ZTA frameworks: measurement by hole-drilling.

    Science.gov (United States)

    Fukushima, K A; Sadoun, M J; Cesar, P F; Mainjot, A K

    2014-02-01

    The residual stress profile developed within the veneering ceramic during the manufacturing process is an important predicting factor in chipping failures, which constitute a well-known problem with yttria-tetragonal-zirconia polycrystal (Y-TZP) based restorations. The objectives of this study are to measure and to compare the residual stress profile in the veneering ceramic layered on three different polycrystalline ceramic framework materials: Y-TZP, alumina polycrystal (AL) and zirconia toughened alumina (ZTA). The stress profile was measured with the hole-drilling method in bilayered disk samples of 19 mm diameter with a 0.7 mm thick Y-TZP, AL or ZTA framework and a 1.5mm thick layer of the corresponding veneering ceramic. The AL samples exhibited increasing compressive stresses with depth, while compressive stresses switching into interior tensile stresses were measured in Y-TZP samples. ZTA samples exhibited compressive stress at the ceramic surface, decreasing with depth up to 0.6mm from the surface, and then becoming compressive again near the framework. Y-TZP samples exhibited a less favorable stress profile than those of AL and ZTA samples. Results support the hypothesis of the occurrence of structural changes within the Y-TZP surface in contact with the veneering ceramic to explain the presence of tensile stresses. Even if the presence of Y-TZP in the alumina matrix seems to negatively affect the residual stress profiles in ZTA samples in comparison with AL samples, the registered profiles remain positive in terms of veneer fracture resistance. Copyright © 2013 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

  18. Predictive modeling and multi-objective optimization of machining-induced residual stresses: Investigation of machining parameter effects

    Science.gov (United States)

    Ulutan, Durul

    2013-01-01

    In the aerospace industry, titanium and nickel-based alloys are frequently used for critical structural components, especially due to their higher strength at both low and high temperatures, and higher wear and chemical degradation resistance. However, because of their unfavorable thermal properties, deformation and friction-induced microstructural changes prevent the end products from having good surface integrity properties. In addition to surface roughness, microhardness changes, and microstructural alterations, the machining-induced residual stress profiles of titanium and nickel-based alloys contribute in the surface integrity of these products. Therefore, it is essential to create a comprehensive method that predicts the residual stress outcomes of machining processes, and understand how machining parameters (cutting speed, uncut chip thickness, depth of cut, etc.) or tool parameters (tool rake angle, cutting edge radius, tool material/coating, etc.) affect the machining-induced residual stresses. Since experiments involve a certain amount of error in measurements, physics-based simulation experiments should also involve an uncertainty in the predicted values, and a rich set of simulation experiments are utilized to create expected value and variance for predictions. As the first part of this research, a method to determine the friction coefficients during machining from practical experiments was introduced. Using these friction coefficients, finite element-based simulation experiments were utilized to determine flow stress characteristics of materials and then to predict the machining-induced forces and residual stresses, and the results were validated using the experimental findings. A sensitivity analysis on the numerical parameters was conducted to understand the effect of changing physical and numerical parameters, increasing the confidence on the selected parameters, and the effect of machining parameters on machining-induced forces and residual

  19. A finite element elastic-plastic analysis of residual stresses due to clad welding in reactor vessels

    International Nuclear Information System (INIS)

    Buchalet, C.; Riccardella, P.C.

    1972-01-01

    Residual stresses due to weld deposited cladding on the inside of a typical Westinghouse pressurized water reactor vessel are investigated using an axisymmetric finite element elastic-plastic analysis. At the beginning of the analysis, one head of the weld cladding is assumed to lie on the reactor vessel wall at melting temperature (2600degF), but in the solid phase, while the vessel remains at 300degF (preheat temperature). All material properties used in the calculations are taken as temperature-dependent. Temperature profiles are obtained in the cladding and base metal at several discrete time intervals. These temperatures profiles are used to obtain the stress distribution for the same time intervals. Residual hoop tensile stresses of approximately 25 ksi were found to exist in the cladding. Peak tensile stresses in the hoop direction occur in the base metal near the cladding interface and reach a value of 60 ksi at the end of the transient. The tensile stress decreases very rapidly through the thickness of the base metal and becomes insignificant at about two inches from the inside surface. In order to lower residual stresses, a post-weld heat treatment is performed by uniformly heating the vessel to 1100degF, holding at that temperature for a specified period of time and then cooling slowly. The analysis shows that after this treatment, the peak stresses in the base metal decrease from 60 ksi to 32 ksi, while the stress in the cladding does not change significantly. (author)

  20. Residual stress evaluation by Barkhausen signals with a magnetic field sensor for high efficiency electrical motors

    Science.gov (United States)

    Tsuchida, Yuji; Enokizono, Masato

    2018-04-01

    The iron loss of industrial motors increases by residual stress during manufacturing processes. It is very important to make clear the distribution of the residual stress in the motor cores to reduce the iron loss in the motors. Barkhausen signals which occur on electrical steel sheets can be used for the evaluation of the residual stress because they are very sensitive to the material properties. Generally, a B-sensor is used to measure Barkhausen signals, however, we developed a new H-sensor to measure them and applied it into the stress evaluation. It is supposed that the Barkhausen signals by using a H-sensor can be much effective to the residual stress on the electrical steel sheets by referring our results regarding to the stress evaluations. We evaluated the tensile stress of the electrical steel sheets by measuring Barkhausen signals by using our developed H-sensor for high efficiency electrical motors.

  1. Separating plasticity-induced closure and residual stress contributions to fatigue crack retardation following an overload

    Science.gov (United States)

    Salvati, Enrico; Zhang, Hongjia; Fong, Kai Soon; Song, Xu; Korsunsky, Alexander M.

    2017-01-01

    The introduction of an overload or underload within a constant amplitude loading fatigue test leads to a retardation or acceleration of the Fatigue Crack Growth Rate (FCGR). The understanding of the causes of these effects is essential in the context of variable amplitude fatigue loading, since in principle any loading history can be represented as a sequence of overloads and underloads. In the case of overload, along with some other minor causes, the residual stress changes at the crack tip and crack closure behind the tip can be thought of as the main factors that affect the fatigue crack growth rate. Whilst this has been recognised and accepted for many decades, controversy persists regarding the relative significance and presence of these two effects, and consensus is yet to emerge. The effect of crack closure, when the baseline loading ratio is high enough, can be inhibited so that the main cause of retardation becomes doubtless the residual stress present ahead the crack tip. In the present paper we report our attempt to deconvolve the contributions of crack closure and residual stress on crack retardation following an overload. To accomplish this task we analyse the results of fatigue tests run at two baseline load ratios, namely R=0.1 and R=0.7. At the load ratio of R=0.7 the crack closure effect is not operative, as confirmed by Digital Image Correlation analysis of the crack flanks close to the tip, and post mortem fractographic analysis of crack surfaces. Therefore, for R=0.7 the compressive residual stress region created by the overload ahead of the crack tip is the sole mechanism causing crack retardation. Therefore, for R=0.7 the focus must be placed entirely on the strain field around the crack tip. To this end, line profiles along the crack bisector of elastic strain in the crack opening direction were collected at several stages of crack propagation past the overload using in situ Synchrotron X-ray Powder Diffraction (SXRPD) technique. By

  2. Influence of thermal expansion mismatch on residual stress profile in veneering ceramic layered on zirconia: Measurement by hole-drilling.

    Science.gov (United States)

    Mainjot, Amélie K; Najjar, Achref; Jakubowicz-Kohen, Boris D; Sadoun, Michaël J

    2015-09-01

    Mismatch in thermal expansion coefficient between core and veneering ceramic (Δα=αcore-αveneer, ppm/°C) is reported as a crucial parameter influencing veneer fractures with Yttria-tetragonal-zirconia-polycrystal (Y-TZP) prostheses, which still constitutes a misunderstood problem. However, the common positive Δα concept remains empirical. The objective of this study is to investigate the Δα dependence of residual stress profiles in veneering ceramic layered on Y-TZP frameworks. The stress profile was measured with the hole-drilling method in bilayered disc samples of 20mm diameter with a 0.7mm thick Y-TZP framework and a 1.5mm thick veneer layer. 3 commercial and 4 experimental veneering ceramics (n=3 per group) were used to obtain different Δα varying from -1.3ppm/°C to +3.2ppm/°C, which were determined by dilatometric analyses. Veneer fractures were observed in samples with Δα≥+2.3 or ≤-0.3ppm/°C. Residual stress profiles measured in other groups showed compressive stresses in the surface, these stresses decreasing with depth and then becoming more compressive again near the interface. Small Δα variations were shown to induce significant changes in residual stress profiles. Compressive stress near the framework was found to decrease inversely to Δα. Veneer CTE close to Y-TZP (+0.2ppm/°C Δα) gived the most favorable stress profile. Yet, near the framework, Δα-induced residual stress varied inversely to predictions. This could be explained by the hypothesis of structural changes occurrence within the Y-TZP surface. Consequently, the optimum Δα value cannot be determined before understanding Y-TZP's particular behavior when veneered. Copyright © 2015 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

  3. Comparison of residual stress distributions of similar and dissimilar thick butt-weld plates

    International Nuclear Information System (INIS)

    Suzuki, Hiroshi; Katsuyama, Jinya; Morii, Yukio

    2012-01-01

    Residual stress distributions of 35 mm thick dissimilar metal butt-weld between A533B ferritic steel and Type 304 austenitic stainless steel (304SS) with Ni alloy welds and similar metal butt-weld of 304SS were measured using neutron diffraction. Effects of differences in thermal expansion coefficients (CTEs) and material strengths on the weld residual stress distributions were discussed by comparison of the residual stress distributions between the similar and dissimilar metal butt-welds. Residual stresses in the similar metal butt-weld exhibited typical distributions found in a thick butt-weld and they were distributed symmetrically on either side of the weld line. Meanwhile, asymmetric residual stress distributions were observed near the root of the dissimilar metal butt-weld, which was caused by differences in CTEs and yield strengths among both parent materials and weld metals. Transverse residual stress distribution of the dissimilar metal butt-weld was similar trend to that of the similar metal butt-weld, since effect of difference in CTEs were negligible, while magnitude of the transverse residual stress near the root depended on the yield strengths of each metal. In contrast, the normal and longitudinal residual stresses in the dissimilar metal butt-weld distributed asymmetrically on either side of weld line due to influence of differences in CTEs. (author)

  4. On the role of the residual stress state in product manufacturing

    NARCIS (Netherlands)

    Zijlstra, G.; Groen, M.; Post, J.; Ocelik, V.; de Hosson, J.Th.M.

    2016-01-01

    This paper concentrates on the effect of the residual stress state during product manufacturing of AISI 420 steel on the final shape of the product. The work includes Finite Element (FE) calculations of the distribution of the residual stresses after metal forming and a heat treatment. The evolution

  5. Reduction method for residual stress of welded joint using harmonic vibrational load

    International Nuclear Information System (INIS)

    Aoki, Shigeru; Nishimura, Tadashi; Hiroi, Tetsumaro; Hirai, Seiji

    2007-01-01

    Welding is widely used for construction of many structures. Since welding is a process using locally given heat, residual stress is generated near the bead. Tensile residual stress degrades fatigue strength. Some reduction methods of residual stress have been presented and, for example, heat treatment and shot peening are practically used. However, those methods need special tools and are time consuming. In this paper, a new method for reduction of residual stress using harmonic vibrational load during welding is proposed. The proposed method is examined experimentally for some conditions. Two thin plates are supported on the supporting device and butt-welded using an automatic CO 2 gas shielded arc welding machine. Residual stress in the direction of the bead is measured by using a paralleled beam X-ray diffractometer with scintillation counter after removing quenched scale chemically. First, the welding of rolled steel for general structure for some excitation frequencies is examined. Specimens are welded along the groove on both sides. For all frequencies, tensile residual stress near the bead is significantly reduced. Second, welding of the specimen made of high tensile strength steel is examined. In this case, tensile residual stress near the bead is also reduced. Finally, the proposed method is examined by an analytical method. An analytical model which consists of mass and preloaded springs with elasto-plastic characteristic is used. Reduction of residual stress is demonstrated using this model

  6. Modelling of composition and stress profiles in low temperature surface engineered stainless steel

    DEFF Research Database (Denmark)

    Jespersen, Freja Nygaard; Hattel, Jesper Henri; Somers, Marcel A. J.

    2015-01-01

    stresses are introduced in the developing case, arising from the volume expansion that accompanies the dissolution of high interstitial contents in expanded austenite. Modelling of the composition and stress profiles developing during low temperature surface engineering from the processing parameters...... temperature, time and gas composition is a prerequisite for targeted process optimization. A realistic model to simulate the developing case has to take the following influences on composition and stress into account: - a concentration dependent diffusion coefficient - trapping of nitrogen by chromium atoms...... - the effect of residual stress on diffusive flux - the effect of residual stress on solubility of interstitials - plastic accommodation of residual stress. The effect of all these contributions on composition and stress profiles will be addressed....

  7. Residual stress measurement in a metal microdevice by micro Raman spectroscopy

    International Nuclear Information System (INIS)

    Song, Chang; Du, Liqun; Qi, Leijie; Li, Yu; Li, Xiaojun; Li, Yuanqi

    2017-01-01

    Large residual stress induced during the electroforming process cannot be ignored to fabricate reliable metal microdevices. Accurate measurement is the basis for studying the residual stress. Influenced by the topological feature size of micron scale in the metal microdevice, residual stress in it can hardly be measured by common methods. In this manuscript, a methodology is proposed to measure the residual stress in the metal microdevice using micro Raman spectroscopy (MRS). To estimate the residual stress in metal materials, micron sized β -SiC particles were mixed in the electroforming solution for codeposition. First, the calculated expression relating the Raman shifts to the induced biaxial stress for β -SiC was derived based on the theory of phonon deformation potentials and Hooke’s law. Corresponding micro electroforming experiments were performed and the residual stress in Ni–SiC composite layer was both measured by x-ray diffraction (XRD) and MRS methods. Then, the validity of the MRS measurements was verified by comparing with the residual stress measured by XRD method. The reliability of the MRS method was further validated by the statistical student’s t -test. The MRS measurements were found to have no systematic error in comparison with the XRD measurements, which confirm that the residual stresses measured by the MRS method are reliable. Besides that, the MRS method, by which the residual stress in a micro inertial switch was measured, has been confirmed to be a convincing experiment tool for estimating the residual stress in metal microdevice with micron order topological feature size. (paper)

  8. Residual stress measurement in a metal microdevice by micro Raman spectroscopy

    Science.gov (United States)

    Song, Chang; Du, Liqun; Qi, Leijie; Li, Yu; Li, Xiaojun; Li, Yuanqi

    2017-10-01

    Large residual stress induced during the electroforming process cannot be ignored to fabricate reliable metal microdevices. Accurate measurement is the basis for studying the residual stress. Influenced by the topological feature size of micron scale in the metal microdevice, residual stress in it can hardly be measured by common methods. In this manuscript, a methodology is proposed to measure the residual stress in the metal microdevice using micro Raman spectroscopy (MRS). To estimate the residual stress in metal materials, micron sized β-SiC particles were mixed in the electroforming solution for codeposition. First, the calculated expression relating the Raman shifts to the induced biaxial stress for β-SiC was derived based on the theory of phonon deformation potentials and Hooke’s law. Corresponding micro electroforming experiments were performed and the residual stress in Ni-SiC composite layer was both measured by x-ray diffraction (XRD) and MRS methods. Then, the validity of the MRS measurements was verified by comparing with the residual stress measured by XRD method. The reliability of the MRS method was further validated by the statistical student’s t-test. The MRS measurements were found to have no systematic error in comparison with the XRD measurements, which confirm that the residual stresses measured by the MRS method are reliable. Besides that, the MRS method, by which the residual stress in a micro inertial switch was measured, has been confirmed to be a convincing experiment tool for estimating the residual stress in metal microdevice with micron order topological feature size.

  9. Study on distribution and optimization of residual stress inside plate-fin structure after braze welding

    International Nuclear Information System (INIS)

    Zhou Guoyan; Tu Shandong; Xuan Fuzhen; Wang Zhengdong

    2010-01-01

    The residual stress inside the plate-fin structure has been analyzed by the finite element method under different operation conditions. The calculated results show that a large scale of residual stress will occur in the plate-fin structure and the maximum value is found at the braze corner. The rapid cooling process and the pressured assembly technology have a significant effect on the distribution of the residual stress. The brazed material owns a better performance with a quicker cooling rate. However, the quicker cooling rate also leads to a tensile residual stress near the brazed seam, which is deleterious to the whole structure. The pressure assembly technology can change the residual stress from a tensile state to the compressed state which can improve the safety and extend the service life of the plate-fin structure effectively. (authors)

  10. Depth-resolved X-ray residual stress analysis in PVD (Ti, Cr) N hard coatings

    CERN Document Server

    Genzel, C

    2003-01-01

    Physical vapour deposition (PVD) of thin hard coatings on TiN basis is usually performed at rather low temperatures (T sub D < 500 C) far from thermal equilibrium, which leads to high intrinsic residual stresses in the growing film. In contrast to the extrinsic thermal residual stresses which can easily be estimated from the difference of the coefficients of thermal expansion between the substrate and the coating, a theoretical prediction of the intrinsic residual stresses is difficult, because their amount as well as their distribution within the film depend in a very complex way on the deposition kinetics. By the example of strongly fibre-textured PVD (Ti, Cr)N coatings which have been prepared under defined variation of the deposition parameters in order to adjust the residual stress distribution within the coatings, the paper compares different X-ray diffraction techniques with respect to their applicability for detecting residual stresses which are non-uniform over the coating thickness. (orig.)

  11. Effect of residual stress on modal patterns of MEMS vibratory gyroscope

    Energy Technology Data Exchange (ETDEWEB)

    Dutta, Shankar, E-mail: shankardutta77@gmail.com; Panchal, Abha; Kumar, Manoj; Pal, Ramjay; Bhan, R. K. [Solid State Physics Laboratory, DRDO, Lucknow Road, Timarpur, Delhi, India 110054 (India)

    2016-04-13

    Deep boron diffusion often induces residual stress in bulk micromachined MEMS structures, which may affect the MEMS devices operation. In this study, we studied the modal patterns of MEMS vibratory gyroscope under the residual stress (100 – 1000 MPa). Modal patterns and modal frequencies of the gyro are found to be dependent on the residual stress values. Without any residual stress, the modal frequencies drive and sense modeswere found to be 20.06 kHz and 20.36 kHz respectively. In presence of 450 MPa residual stress, the modal frequencies of the drive and sense modes were changed to 42.75 kHz and 43.07 kHz respectively.

  12. A novel biaxial specimen for inducing residual stresses in thermoset polymers and fibre composite material

    DEFF Research Database (Denmark)

    Jakobsen, Johnny; Andreasen, Jens Henrik; Jensen, Martin

    2015-01-01

    A new type of specimen configuration with the purpose of introducing a well-defined biaxial residual (axisymmetric) stress field in a neat thermoset or a fibre composite material is presented. The ability to experimentally validate residual stress predictions is an increasing need for design...... engineers when they challenge the material limits in present and future thermoset and composite component. In addition to the new specimen configuration, this paper presents an analytical solution for the residual stress state in the specimen. The analytical solution assumes linear elastic and isotropic...... material behaviour. Experimental strain release measurements and the analytical solution determine the residual stress state present in the material. A demonstration on neat epoxy is conducted and residual stress predictions of high accuracy and repeatability have been achieved. The precise determination...

  13. Effects of weld residual stresses on crack-opening area analysis of pipes for LBB applications

    International Nuclear Information System (INIS)

    Dong, P.; Rahman, S.; Wilkowski, G.

    1997-01-01

    This paper summarizes four different studies undertaken to evaluate the effects of weld residual stresses on the crack-opening behavior of a circumferential through-wall crack in the center of a girth weld. The effect of weld residual stress on the crack-opening-area and leak-rate analyses of a pipe is not well understood. There are no simple analyses to account for these effects, and, therefore, they are frequently neglected. The four studies involved the following efforts: (1) Full-field thermoplastic finite element residual stress analyses of a crack in the center of a girth weld, (2) A comparison of the crack-opening displacements from a full-field thermoplastic residual stress analysis with a crack-face pressure elastic stress analysis to determine the residual stress effects on the crack-opening displacement, (3) The effects of hydrostatic testing on the residual stresses and the resulting crack-opening displacement, and (4) The effect of residual stresses on crack-opening displacement with different normal operating stresses

  14. Effects of weld residual stresses on crack-opening area analysis of pipes for LBB applications

    Energy Technology Data Exchange (ETDEWEB)

    Dong, P.; Rahman, S.; Wilkowski, G. [and others

    1997-04-01

    This paper summarizes four different studies undertaken to evaluate the effects of weld residual stresses on the crack-opening behavior of a circumferential through-wall crack in the center of a girth weld. The effect of weld residual stress on the crack-opening-area and leak-rate analyses of a pipe is not well understood. There are no simple analyses to account for these effects, and, therefore, they are frequently neglected. The four studies involved the following efforts: (1) Full-field thermoplastic finite element residual stress analyses of a crack in the center of a girth weld, (2) A comparison of the crack-opening displacements from a full-field thermoplastic residual stress analysis with a crack-face pressure elastic stress analysis to determine the residual stress effects on the crack-opening displacement, (3) The effects of hydrostatic testing on the residual stresses and the resulting crack-opening displacement, and (4) The effect of residual stresses on crack-opening displacement with different normal operating stresses.

  15. Effect of feed rate, workpiece hardness and cutting edge on subsurface residual stress in the hard turning of bearing steel using chamfer + hone cutting edge geometry

    International Nuclear Information System (INIS)

    Hua Jiang; Shivpuri, Rajiv; Cheng Xiaomin; Bedekar, Vikram; Matsumoto, Yoichi; Hashimoto, Fukuo; Watkins, Thomas R.

    2005-01-01

    Residual stress on the machined surface and the subsurface is known to influence the service quality of a component, such as fatigue life, tribological properties, and distortion. Therefore, it is essential to predict and control it for enhanced performance. In this paper, a newly proposed hardness based flow stress model is incorporated into an elastic-viscoplastic finite element model of hard turning to analyze process variables that affect the residual stress profile of the machined surface. The effects of cutting edge geometry and workpiece hardness as well as cutting conditions, such as feed rate and cutting speed, are investigated. Numerical analysis shows that hone edge plus chamfer cutting edge and aggressive feed rate help to increase both compressive residual stress and penetration depth. These predictions are validated by face turning experiments which were conducted using a chamfer with hone cutting edge for different material hardness and cutting parameters. The residual stresses under the machined surface are measured by X-ray diffraction/electropolishing method. A maximum circumferential residual stress of about 1700 MPa at a depth of 40 μm is reached for hardness of 62 HRc and feed rate of 0.56 mm/rev. This represents a significant increase from previously reported results in literatures. It is found from this analysis that using medium hone radius (0.02-0.05 mm) plus chamfer is good for keeping tool temperature and cutting force low, while obtaining desired residual stress profile

  16. Study of residual stresses generated in machining of AISI 4340 steel; Estudo das tensoes residuais geradas na usinagem de aco AISI 4340

    Energy Technology Data Exchange (ETDEWEB)

    Reis, W.P. dos; Fonseca, M.P. Cindra; Serrao, L.F.; Chuvas, T.C.; Oliveira, L.C., E-mail: mcindra@vm.uff.b [Universidade Federal Fluminense (PGMEC/UFF), Niteroi, RJ (Brazil). Dept. de Engenharia Mecanica

    2010-07-01

    Among the mechanical construction steels, AISI 4340 has good harden ability, while combining high strength with toughness and good fatigue strength, making it excellent for application in the metalworking industry, where it can work at different levels and types of requests. Residual stresses are generated in almost all processes of mechanical manufacturing. In this study, the residual stresses generated in different machining processes and heat treatment hardening of AISI 4340 were analyzed by X-ray diffraction, by the sen{sup 2} {psi} method, using Cr{kappa}{beta} radiation and compared. All samples, except for turned and cut by EDM, presented compressive residual stresses in the surface with various magnitudes. (author)

  17. Residual stress evaluation and curvature behavior of aluminum 7050 peen forming processed; Avaliacao da tensao residual em aluminio 7050 conformado pelo processo peen forming

    Energy Technology Data Exchange (ETDEWEB)

    Oliveira, Rene Ramos de

    2011-07-01

    Shot peening is a superficial cold work process used to increase the fatigue life evaluated by residual stress measurements. The peen forming process is a variant of the shot peening process, where a curvature in the plate is obtained by the compression of the grains near to the surface. In this paper, the influence of the parameters such as: pressure of shot, ball shot size and thickness of aluminum 7050 samples with respect to residual stress profile and resulting arc height was studied. The evaluation of the residual stress profile was obtained by sin{sup 2} {psi} method. The results show that the formation of the curvature arc height is proportional to the shot peening pressure, of spheres size and inversely proportional to the thickness of the sample, and that stress concentration factor is larger for samples shot peened with small balls. On final of this paper presents an additional study on micro strain and average crystallite size, which can evaluate the profile of the samples after blasting. (author)

  18. A comparison of residual stresses in built-up steel beams using hole-drilling method

    International Nuclear Information System (INIS)

    Nawafleh, M. A.; Hunaiti, Y. M.; Younes, R. M.

    2009-01-01

    Residual stresses have a significant effect on the stability resistance of metal building systems. An experimental program was conducted to measure these stresses in built-up steel beams using incremental hole-drilling method. The experimental results reveal that the predicted residual stress type of pattern for built-up I-sections with fillet welds on one side of the web is not the same as the pattern of residual stresses in built-up I-sections with fillet welds on both sides of the web

  19. Residual Stress Distribution in Carbon Steel Pipe Welded Joint Measured by Neutron Diffraction

    OpenAIRE

    Makoto, HAYASHI; Masayuki, ISHIWATA; Yukio, MORII; Nobuaki, MINAKAWA; ROOT, John H.; Mechanical Engineering Research Laboratory, Hitachi, Ltd.,; Nuclear Engineering Division, Hitachi Ltd.,; Tokai Establishment, Japan Atomic Energy Research Institute; Tokai Establishment, Japan Atomic Energy Research Institute; National Research Council of Canada

    2000-01-01

    In order to estimate crack growth behavior of fatigue and stress corrosion cracking in pipes, the residual stress distribution near the pipe weld region has to be measured through the wall thickness.Since the penetration depth of neutron is deep enough to pass through the thick pipe wall, the neutron diffraction technique for the residual stress measurement is effective for this purpose.At the first step the residual stress distribution near the weld region in a butt-welded carbon steel pipe ...

  20. Residual stress in sprayed Ni+5%Al coatings determined by neutron diffraction

    CERN Document Server

    Matejicek, J; Gnaeupel-Herold, T; Prask, H J

    2002-01-01

    Coatings of nickel-based alloys are used in numerous high-performance applications. Their properties and lifetimes are influenced by factors such as residual stress. Neutron diffraction is a powerful tool for nondestructive residual stress determination. In this study, through-thickness residual stress profiles in Ni+5%Al coatings on steel substrates were determined. Two examples of significantly different spraying techniques - plasma spraying and cold spraying - are highlighted. Different stress-generation mechanisms are discussed with respect to process parameters and material properties. (orig.)

  1. Residual Stress Analysis of an Overlay Weld on a Repair Weld

    Energy Technology Data Exchange (ETDEWEB)

    Kim, Kang Soo; Lee, Ho Jin; Lee, Bong Sang [Korea Atomic Energy Research Institute, Daejeon (Korea, Republic of); Jung, I. C.; Byeon, J. G.; Park, K. S. [Doosan Heavy Industries and Construction Co., Changwon (Korea, Republic of)

    2008-10-15

    In recent years, the dissimilar metal, Alloy 82/182 welds used to connect stainless steel piping and low alloy steel or carbon steel components in nuclear reactor piping system have experienced the cracking due to primary water stress corrosion(PWSCC). It is well known that one reason of the cracking is the residual stress by the weld. But, it is difficult to estimate the weld residual stress exactly due to many parameters of a welding. In this paper, the analysis of 3 FEM models is performed to estimate the weld residual stress on the dissimilar metal weld exactly.

  2. Residual stress analysis of an overlay weld on a dissimilar metal weld

    Energy Technology Data Exchange (ETDEWEB)

    Kim, Kang Soo; Lee, Ho Jin; Lee, Bong Sang (Korea Atomic Energy Research Institute, Daejeon (Korea)); Jung, I.C.; Byeon, J.G.; Park, K.S. (Doosan Heavy Industries and Construction Co., Changwon (Korea)), e-mail: kskim5@kaeri.re.kr

    2009-07-01

    In recent years, a dissimilar metal, Alloy 82/182 welds used to connect stainless steel piping and low alloy steel or carbon steel components in nuclear reactor piping system have experienced a cracking due to a primary water stress corrosion (PWSCC). It is well known that one reason for the cracking is the residual stress by the weld. But, it is difficult to estimate the weld residual stress exactly due to many parameters of a welding. In this paper, the analysis of 3 FEM models is performed to estimate the weld residual stress on a dissimilar metal weld exactly

  3. As-Cast Residual Stresses in an Aluminum Alloy AA6063 Billet: Neutron Diffraction Measurements and Finite Element Modeling

    Science.gov (United States)

    Drezet, J.-M.; Phillion, A. B.

    2010-12-01

    The presence of thermally induced residual stresses, created during the industrial direct chill (DC) casting process of aluminum alloys, can cause both significant safety concerns and the formation of defects during downstream processing. Although numerical models have been previously developed to compute these residual stresses, most of the computations have been validated only against measured surface distortions. Recently, the variation in residual elastic strains in the steady-state regime of casting has been measured as a function of radial position using neutron diffraction (ND) in an AA6063 grain-refined cylindrical billet. In the present study, these measurements are used to show that a well-designed thermomechanical finite element (FE) process model can reproduce relatively well the experimental results. A sensitivity analysis is then carried out to determine the relative effect of the various mechanical parameters when computing the as-cast residual stresses in a cylindrical billet. Two model parameters have been investigated: the temperature when the alloy starts to thermally contract and the plasticity behavior. It is shown that the mechanical properties at low temperatures have a much larger influence on the residual stresses than those at high temperatures.

  4. Effect of an absorbent overlay on the residual stress field induced by laser shock processing on aluminum samples

    Energy Technology Data Exchange (ETDEWEB)

    Rubio-Gonzalez, C. [Centro de Ingenieria y Desarrollo Industrial, Pie de la Cuesta No. 702, Desarrollo San Pablo, Queretaro, Qro. 76130 (Mexico)]. E-mail: crubio@cidesi.mx; Gomez-Rosas, G. [Departamento de Ciencias Exactas y Tecnologicas, Centro Universitario de los Lagos, Universidad de Guadalajara. Lagos de Moreno Jal. (Mexico); Ocana, J.L. [Departamento de Fisica Aplicada a la Ingenieria Industrial, E.T.S.I.I. Universidad Politecnica de Madrid (Spain); Molpeceres, C. [Departamento de Fisica Aplicada a la Ingenieria Industrial, E.T.S.I.I. Universidad Politecnica de Madrid (Spain); Banderas, A. [Centro de Ingenieria y Desarrollo Industrial, Pie de la Cuesta No. 702, Desarrollo San Pablo, Queretaro, Qro. 76130 (Mexico); Porro, J. [Departamento de Fisica Aplicada a la Ingenieria Industrial, E.T.S.I.I. Universidad Politecnica de Madrid (Spain); Morales, M. [Departamento de Fisica Aplicada a la Ingenieria Industrial, E.T.S.I.I. Universidad Politecnica de Madrid (Spain)

    2006-07-15

    Laser shock processing (LSP) or laser shock peening is a new technique for strengthening metals. This process induces a compressive residual stress field, which increases fatigue crack initiation life and reduces fatigue crack growth rate. Specimens of 6061-T6 aluminum alloy are used in this investigation. A convergent lens is used to deliver 2.5 J, 8 ns laser pulses by a Q-switch Nd:YAG laser, operating at 10 Hz. The pulses are focused to a diameter of 1.5 mm onto aluminum samples. Density of 2500 pulses/cm{sup 2} with infrared (1064 nm) radiation was used. The effect of an absorbent overlay on the residual stress field using this LSP setup and this energy level is evaluated. Residual stress distribution as a function of depth is assessed by the hole drilling method. It is observed that the overlay makes the compressive residual stress profile move to the surface. This effect is explained on the basis of the vaporization of the coat layer suppressing thermal effects on the metallic substrate. The effect of coating the specimen surface before LSP treatment may have advantages on improving wear and contact fatigue properties of this aluminum alloy.

  5. Assessment of Bending Fatigue Strength of Crankshaft Sections with Consideration of Quenching Residual Stress

    Science.gov (United States)

    Qin, W. J.; Dong, C.; Li, X.

    2016-03-01

    High-cycle bending fatigue is the primary failure mode of crankshafts in engines. Compressive residual stresses are often introduced by induction quenching to improve the fatigue strength of crankshafts. The residual stresses, which are commonly obtained by numerical methods, such as the finite element method (FEM), should be included in fatigue failure analysis to predict the fatigue strength of crankshafts accurately. In this study, the simulation method and theory of quenching process are presented and applied to investigate the residual stresses of a diesel engine crankshaft. The coupling calculation of temperature, microstructure, and stress fields of the crankshaft section is conducted by FEM. Then, the fatigue strength of the crankshaft section is analytically assessed by Susmel and Lazzarin's criterion based on the critical plane approach that superimposes the residual stresses onto the bending stresses. The resonant bending fatigue tests of the crankshaft sections are conducted, and the tests and analytical assessments yield consistent results.

  6. Relation Between Residual and Hoop Stresses and Rolling Bearing Fatigue Life

    Science.gov (United States)

    Oswald, Fred B.; Zaretsky, Erwin V.; Poplawski, Joseph V.

    2015-01-01

    Rolling-element bearings operated at high speed or high vibration may require a tight interference fit between the bore of the bearing and shaft to prevent rotation of the bearing bore around the shaft and fretting damage at the interfaces. Previous work showed that the hoop stresses resulting from tight interference fits can reduce bearing lives by as much as 65 percent. Where tight interference fits are required, case-carburized steel such as AISI 9310 or M50 NiL is often used because the compressive residual stresses inhibit subsurface crack formation and the ductile core inhibits inner-ring fracture. The presence of compressive residual stress and its combination with hoop stress also modifies the Hertz stress-life relation. This paper analyzes the beneficial effect of residual stresses on rolling-element bearing fatigue life in the presence of high hoop stresses for three bearing steels. These additional stresses were superimposed on Hertzian principal stresses to calculate the inner-race maximum shearing stress and the resulting fatigue life of the bearing. The load-life exponent p and Hertz stress-life exponent n increase in the presence of compressive residual stress, which yields increased life, particularly at lower stress levels. The Zaretsky life equation is described and is shown to predict longer bearing lives and greater load- and stress-life exponents, which better predicts observed life of bearings made from vacuum-processed steel.

  7. Distortion and residual stresses in structures reinforced with titanium straps for improved damage tolerance

    International Nuclear Information System (INIS)

    Liljedahl, C.D.M.; Fitzpatrick, M.E.; Edwards, L.

    2008-01-01

    Distortion and residual stresses induced during the manufacturing process of bonded crack retarders have been investigated. Titanium alloy straps were adhesively bonded to an aluminium alloy SENT specimen to promote fatigue crack growth retardation. The effect of three different strap dimensions was investigated. The spring-back of a component when released from the autoclave and the residual stresses are important factors to take into account when designing a selective reinforcement, as this may alter the local aerodynamic characteristics and reduce the crack bridging effect of the strap. The principal problem with residual stresses is that the tensile nature of the residual stresses in the primary aluminium structure has a negative impact on the crack initiation and crack propagation behaviour in the aluminium. The residual stresses were measured with neutron diffraction and the distortion of the specimens was measured with a contour measurement machine. The bonding process was simulated with a three-dimensional FE model. The residual stresses were found to be tensile close to the strap and slightly compressive on the un-bonded side. Both the distortion and the residual stresses increased with the thickness and the width of the strap. Very good agreement between the measured stresses and the measured distortion and the FE simulation was found

  8. Residual Stress Distribution and Microstructure at a Laser Spot of AISI 304 Stainless Steel Subjected to Different Laser Shock Peening Impacts

    Directory of Open Access Journals (Sweden)

    Wenquan Zhang

    2015-12-01

    Full Text Available The effects of different laser shock peening (LSP impacts on the three-dimensional displayed distributions of surface and in-depth residual stress at a laser spot of AISI 304 stainless steel were investigated by X-ray diffraction technology with the sin2φ method and MATLAB 2010a software. Microstructural evolution in the top surface subjected to multiple LSP impacts was presented by means of cross-sectional optical microscopy (OM and transmission electron microscopy (TEM observations. Experimental results and analysis indicated that residual stress distribution and microstructure at a laser spot depended strongly on the number of multiple LSP impacts, and refined grain and ultra-high strain rate play an important role in the improvement of compressive residual stress of AISI 304 stainless steel. The analysis of treatment of the extended surface was presented to obtain uniform surface properties on the top surface of AISI 304 stainless steel.

  9. Finite element analysis of residual stress in plasma-sprayed ceramic

    International Nuclear Information System (INIS)

    Mullen, R.L.; Hendricks, R.C.; McDonald, G.

    1985-01-01

    Residual stress in a ZrO 2 -Y 2 O 3 ceramic coating resulting from the plasma spraying operation is calculated. The calculations were done using the finite element method. Both thermal and mechanical analysis were performed. The resulting residual stress field was compared to the measurements obtained by Hendricks and McDonald. Reasonable agreement between the predicted and measured moment occurred. However, the resulting stress field is not in pure bending

  10. Residual Stress in Wheels: Comparison of Neutron Diffraction and Ultrasonic Methods, with Trends in RCF

    OpenAIRE

    Molyneux-Berry, Paul; Bevan, Adam; Zhang, S. Y; Kabra, S

    2014-01-01

    The critical damage mechanism on many GB passenger train wheels is Rolling Contact Fatigue (RCF) cracking in the rim. Evidence from field observations suggests that RCF damage occurs much more quickly as the wheelsets near the end of their life. Wheel manufacturing processes induce a compressive hoop stress in the wheel rim; variations in residual stress through the life of a wheel may influence the observed RCF damage rates.\\ud This paper describes experiments to measure residual stresses in...

  11. Analysis of residual stress relief mechanisms in post-weld heat treatment

    International Nuclear Information System (INIS)

    Dong, Pingsha; Song, Shaopin; Zhang, Jinmiao

    2014-01-01

    This paper presents a recent study on weld residual stress relief mechanisms associated with furnace-based uniform post-weld heat treatment (PWHT). Both finite element and analytical methods are used to quantitatively examine how plastic deformation and creep relaxation contribute to residual stress relief process at different stages of PWHT process. The key contribution of this work to an improved understanding of furnace based uniform PWHT can be summarized as follows: (1)Plastic deformation induced stress relief during PWHT can be analytically expressed by the change in material elastic deformation capacity (or elastic deformation limit) measured in terms of material yield strength to Young's modulus ratio, which has a rather limited role in overall residual stress relief during furnace based uniform PWHT. (2)The most dominant stress relief mechanism is creep strain induced stress relaxation, as expected. However, a rapid creep strain development accompanied by a rapid residual stress reduction during heating stage before reaching PWHT temperature is shown to contribute to most of the stress relief seen in overall PWHT process, suggesting PWHT hold time can be significantly reduced as far as residual stress relief is concerned. (3)A simple engineering scheme for estimating residual stress reduction is proposed based on this study by relating material type, PWHT temperature, and component wall thickness. - Highlights: • The paper clarified effects of plastic deformation and creep relaxation on weld residual stress relief during uniform PWHT. • Creep strain development is far more important than plastic strain, mostly completed even before hold time starts. • Plastic strain development is insignificant and be analytically described by a material elastic deformation capacity parameter. • An engineering estimation scheme is proposed for determining residual stress reduction resulted from furnace based PWHT

  12. Residual stresses and mechanical properties of Si3N4/SiC multilayered composites with different SiC layers

    International Nuclear Information System (INIS)

    Liua, S.; Lia, Y.; Chena, P.; Lia, W.; Gaoa, S.; Zhang, B.; Yeb, F.

    2017-01-01

    The effect of residual stresses on the strength, toughness and work of fracture of Si3N4/SiC multilayered composites with different SiC layers has been investigated. It may be an effective way to design and optimize the mechanical properties of Si3N4/SiC multilayered composites by controlling the properties of SiC layers. Si3N4/SiC multilayered composites with different SiC layers were fabricated by aqueous tape casting and pressureless sintering. Residual stresses were calculated by using ANSYS simulation, the maximum values of tensile and compressive stresses were 553.2MPa and −552.1MPa, respectively. Step-like fracture was observed from the fracture surfaces. Fraction of delamination layers increased with the residual stress, which can improve the reliability of the materials. Tensile residual stress was benefit to improving toughness and work of fracture, but the strength of the composites decreased. [es

  13. Characterization of micro-scale residual stress around thermal grown oxide using micro-slotting method and geometric phase analysis

    Science.gov (United States)

    Zhang, Q.; Xie, H.; Liu, Z.; Dai, X.

    2018-03-01

    Characterization of residual stress around thermal grown oxide (TGO) is important for understanding the spallation failure of thermal barrier coatings (TBCs). Cr3+ photoluminescence piezo-spectroscopy (CPLPS) is a nondestructive method for measuring the in-plane residual stress in the TGO layer. However, using CPLPS it is hard to evaluate the out-of-plane residual stress around TGO. Here, we adopted the micro-slotting method combined with geometric phase analysis (GPA) for measuring the in-plane and out-of-plane stresses around TGO, with measured areas of 6  ×  4 µm2. In the experiment, a grating and a slot were milled on the specimen surface using focused ion beam, and GPA was applied to analyze the grating structure before and after the slot milling for calculating the released displacement field. Then finite element analysis was used to infer the residual stress in the direction vertical to the micro-slot. Two experiments were performed on the in-service TBC specimen. The first experiment presented the in-plane compression in the TGO, while the second experiment presented the out-of-plane tension at the crest of the TGO/BC interface, thus validating the theoretical analysis.

  14. Influence of friction on the residual morphology, the penetration load and the residual stress distribution of a Zr-based bulk metallic glass

    Directory of Open Access Journals (Sweden)

    Hu Huang

    2013-04-01

    Full Text Available In this paper, friction between the Cube-Corner indenter and the sample surface of a Zr-based bulk metallic glass (BMG was analyzed and discussed by the experimental method, the theoretical method and the finite element simulation. Linear residua are observed on the surface of the indenter for the first time, which gives the direct evidence that strong interaction processes exist between the indenter surface and the sample surface because of strong friction and local high contact press. A simplified model was developed to correct the penetration load with the consideration of friction. Effects of friction on the penetration load-depth curves, plastic flow, surface deformation and residual stress distribution of the sample with different friction coefficients were investigated by the finite element simulation.

  15. Residual stress distribution of the soldered structure with Kovar alloy and Al2O3 ceramics

    Directory of Open Access Journals (Sweden)

    Qile Gao

    2017-03-01

    Full Text Available Residual stress distribution in soldered structure of Kovar alloy and Al2O3 ceramics was determined using XRD analyses. In order to measure the residual stress, position of the characteristic diffraction peak and stress constant were obtained using several versatile/advanced techniques after calibration. Residual stress of soldered structure was measured based on the diffraction patterns obtained for the distribution of residual stress in the soldered joint. Only diffraction peak at 149° for Kovar alloy and two diffraction peaks ranging from 140–170° for Al2O3 ceramics were found to be appropriate for the residual stress determination. It was also confirmed that for Al2O3 ceramics the XRD peak at 152° reflects the changes of stress more precisely than the one at 146°. The stress constant K of Kovar alloy and Al2O3 ceramics was found to be −197 MPa/° and −654 MPa/°, respectively. After soldering, the maximum residual stress of the soldered joint of both materials developed at 1 mm from the soldering seam, and the values within 3 mm from the soldering seam are generally significant. Thus, it is important to pay attention to the area of 3 mm from the soldering seam in practical application.

  16. Residual stress analysis for engineering applications by means of neutron diffraction

    International Nuclear Information System (INIS)

    Gnaeupel-Herold, T.; Brand, P.C.; Prask, H.J.

    1999-01-01

    Residual stresses originate from spatial differences in plastic deformation, temperature, or phase distribution, introduced by manufacturing processes or during service. Engineering parts and materials experience mechanical, thermal, and chemical loads during their service, and most of these loads introduce stresses that are superimposed on the already existing residual stresses. Residual stresses can therefore limit or improve life and strength of engineering parts; knowledge and understanding of these stresses is therefore critical for optimizing strength and durability. The economic and scientific importance of neutron diffraction residual stress analysis has led to an increasing number of suitable instruments worldwide. All of the major sources due in the next several years will have instruments for the sole purpose of performing residual stress and texture measurements. Recently, a dedicated, state-of-the-art diffractometer has been installed at the National Institute of Standards and Technology reactor. It has been used for a variety of measurements on basic and engineering stress problems. Among the most prominent examples that have been investigated in collaboration with industrial and academic partners are residual stresses in rails, weldments, and plasma-sprayed coatings

  17. Experimental determination of residual stress by neutron diffraction in a boiling water reactor core shroud

    International Nuclear Information System (INIS)

    Payzant, A.; Spooner, S.; Zhu, Xiaojing; Hubbard, C.R.

    1996-01-01

    Residual strains in a 51 mm (2-inch) thick 304L stainless steel plate have been measured by neutron diffraction and interpreted in terms of residual stress. The plate, measuring (300 mm) in area, was removed from a 6m (20-ft.) diameter unirradiated boiling water reactor core shroud, and included a multiple-pass horizontal weld which joined two of the cylindrical shells which comprise the core shroud. Residual stress mapping was undertaken in the heat affected zone, concentrating on the outside half of the plate thickness. Variations in residual stresses with location appeared consistent with trends expected from finite element calculations, considering that a large fraction of the residual hoop stress was released upon removal of the plate from the core shroud cylinder

  18. Effect of residual stresses on the reliability of components under fatigue

    International Nuclear Information System (INIS)

    Ruestenberg, I.

    1995-01-01

    The assurance of the reliability of mechanical components relative to a variety of failure mechanisms is of decisive technical, industrial, and economic importance. In this dissertation, the reliability, i.e. the probability that the lifetime does not fall below a given value, is examined with respect to the particularly important failure mechanisms of fracture and fatigue. The general problem of uniaxial fatigue is studied on the basis of both continuum damage mechanics and crack mechanics. In particular, the mechanisms of crack initiation, as characterized by the Coffin-Manson-Neuber local strain-life equations for notched components as well as the mechanism of crack growth, as governed by the Paris-Erdogang relation, are taken into account. The nonlinear fatigue damage accumulation process for components subjected to general, cyclic loading histories is modeled by a multilinear damage law which allows, in principle, to characterize the subsequent activation of different fatigue mechanisms. Explicit equations are developed for quintuple-, quadruple-, and triple-linear damage accumulation. Particularly promising appears the triple-linear damage approach which allows, in principle, the identification of a nucleation, an initiation, and a final growth stage up to rupture of fatigue cracks. The beneficial effect of intentionally induced compressive residual stresses on the lifetime of the component is investigated. To this end, an elasto-plastic contact problem, based on Prandtl-Reuss' constitutive equations, is numerically solved, and the residual stress field, as it is typically produced by the mechanical process of cold rolling, is established. Assessments of the effect of adaptation, i.e. the subsequent reduction of the residual stresses due to cyclic in-service loading as well as of the effect of unavoidable surface roughness, introduced by manufacturing processes like forging, are carried out. (author) figs., tabs., refs