  1. Effect of sintering temperatures on titanium matrix composites reinforced by ceramic particles

    Energy Technology Data Exchange (ETDEWEB)

    Romero, F.; Amigo, V.; Busquets, D.; Klyatskina, E. [Mechanical and Materials Engineering Department. Polytechnical University of Valencia, Valencia (Spain)

    2005-07-01

    Titanium and titanium composites have a potential use in aerospace and biotechnology industries, and nowadays in others like sports and fashion ones. In this work composite materials, based on titanium matrix reinforced with ceramic particles, have been developed. PM route is used to obtain compact and sintered samples. TiN and TiAl powders, are milled with Ti powder in different volumetric percentages in a ball mill. These mixtures are pressed in a uniaxial press and sintered in a vacuum furnace at different temperatures between 1180 to 1220 deg. C. Porosity of samples is analysed, before and after the sintering process, by Archimedes technique and by image analysis. Mechanical properties and the reinforcement particles influence in the titanium matrix are studied by flexion test in green and sintered states, and by hardness and microhardness tests. Complimentarily, a microstructural analysis is carried out by optical and electron microscopy, and the reactivity between the reinforce particles and titanium matrix are studied. (authors)

  2. Microstructure of alumina-matrix composites reinforced with nanometric titanium and titanium carbide dispersions

    OpenAIRE

    Elizabeth Refugio-García; David Hernández-Silva; Eduardo Terrés-Rojas; José Amparo Rodríguez-García; Enrique Rocha-Rangel

    2012-01-01

    The synthesis of alumina (Al2O3)-composites having different amount of very fine titanium and titanium carbide reinforcement-particles has been explored. Two experimental steps have been set for the synthesis; the first step consisted of the pressureless-sintering of Al2O3-titanium powders which were thoroughly mixed under high energy ball-milling and through the second step it was induced the formation of titanium carbide during different times at 500 ºC by the cementation packing process. S...

  3. SOLIDIFICATION CHARACTERISTIC OF TITANIUM CARBIDE PARTICULATE REINFORCED ALUMINIUM ALLOY MATRIX COMPOSITES

    Directory of Open Access Journals (Sweden)

    N. FATCHURROHMAN

    2012-04-01

    Full Text Available In this research solidification characteristic of metal matrix composites consisted of titanium carbide particulate reinforced aluminium-11.8% silicon alloy matrix is performed. Vortex mixing and permanent casting method are used as the manufacturing method to produce the specimens. Temperature measurements during the casting process are captured and solidification graphs are plotted to represent the solidification characteristic. The results show, as volume fraction of particulate reinforcement is increased, solidification time is faster. Particulate reinforcement promotes rapid solidification which will support finer grain size of the casting specimen. Hardness test is performed and confirmed that hardness number increased as more particulate are added to the system.

  4. Microstructure of alumina-matrix composites reinforced with nanometric titanium and titanium carbide dispersions

    Directory of Open Access Journals (Sweden)

    Elizabeth Refugio-García

    2012-12-01

    Full Text Available The synthesis of alumina (Al2O3-composites having different amount of very fine titanium and titanium carbide reinforcement-particles has been explored. Two experimental steps have been set for the synthesis; the first step consisted of the pressureless-sintering of Al2O3-titanium powders which were thoroughly mixed under high energy ball-milling and through the second step it was induced the formation of titanium carbide during different times at 500 ºC by the cementation packing process. SEM and EDS analysis of the microstructures obtained in both sintered and cemented bodies were performed in order to know the effect of the activated carbon used as cementing agent on the titanium for each studied composite. It was observed that a titanium carbide layer growth from the surface into the bulk and reaches different depth as the titanium content in the composites increases. On the other hand, the use of ductile titanium notably enhanced density level and fracture toughness of the composites.

  5. CNTs/TiC Reinforced Titanium Matrix Nanocomposites via Powder Metallurgy and Its Microstructural and Mechanical Properties

    Directory of Open Access Journals (Sweden)

    Katsuyoshi Kondoh

    2008-01-01

    Full Text Available By using pure titanium powder coated with unbundled multiwall carbon nanotubes (MWCNTs via wet process, powder metallurgy (P/M titanium matrix composite (TMC reinforced with the CNTs was prepared by spark plasma sintering (SPS and subsequently hot extrusion process. The microstructure and mechanical properties of P/M pure titanium and reinforced with CNTs were evaluated. The distribution of CNTs and in situ formed titanium carbide (TiC compounds during sintering was investigated by optical and scanning electron microscopy (SEM equipped with EDS analyzer. The mechanical properties of TMC were significantly improved by the additive of CNTs. For example, when employing the pure titanium composite powder coated with CNTs of 0.35 mass%, the increase of tensile strength and yield stress of the extruded TMC was 157 MPa and 169 MPa, respectively, compared to those of extruded titanium materials with no CNT additive. Fractured surfaces of tensile specimens were analyzed by SEM, and the uniform distribution of CNTs and TiC particles, being effective for the dispersion strengthening, at the surface of the TMC were obviously observed.

  6. Titanium Matrix Composite Pressure Vessel Project

    Data.gov (United States)

    National Aeronautics and Space Administration — For over 15 years, FMW Composite Systems has developed Metal Matrix Composite manufacturing methodologies for fabricating silicon-carbide-fiber-reinforced titanium...

  7. A constitutive model for particulate-reinforced titanium matrix composites subjected to high strain rates and high temperatures

    Directory of Open Access Journals (Sweden)

    Song Wei-Dong

    2013-01-01

    Full Text Available Quasi-static and dynamic tension tests were conducted to study the mechanical properties of particulate-reinforced titanium matrix composites at strain rates ranging from 0.0001/s to 1000/s and at temperatures ranging from 20 °C to 650 °C Based on the experimental results, a constitutive model, which considers the effects of strain rate and temperature on hot deformation behavior, was proposed for particulate-reinforced titanium matrix composites subjected to high strain rates and high temperatures by using Zener-Hollomon equations including Arrhenius terms. All the material constants used in the model were identified by fitting Zener-Hollomon equations against the experimental results. By comparison of theoretical predictions presented by the model with experimental results, a good agreement was achieved, which indicates that this constitutive model can give an accurate and precise estimate for high temperature flow stress for the studied titanium matrix composites and can be used for numerical simulations of hot deformation behavior of the composites.

  8. Microstructure and properties of TiB2-TiB reinforced titanium matrix composite coating by laser cladding

    Science.gov (United States)

    Lin, Yinghua; Yao, Jianhua; Lei, Yongping; Fu, Hanguang; Wang, Liang

    2016-11-01

    TiB2 particle and TiB short fiber reinforced titanium matrix composite coatings were prepared utilizing in situ synthesized technique by laser cladding on the surface of Ti6Al4V alloy. Through the experiment, it was found that the surface of the single-track coatings appeared in the depression, but it can be improved by laser track overlapping. With the increase of laser power density, the amount of TiB short fiber was increased, and the distribution of TiB2 and TiB became more uniform from the top to bottom. The micro-hardness of TiB2/TiB coating showed a gradient decreasing trend, and the average micro-hardness of the coatings was two-fold higher than that of the substrate. Due to the strengthening effect of TiB2 particle and TiB short fiber, the wear volume loss of the center of the coating was approximately 30% less than that of the Ti-6Al-4V substrate, and the wear mechanism of the coating was mild fatigue particle detachment.

  9. Titanium carbide nanoparticles reinforcing nickel matrix for improving nanohardness and fretting wear properties in wet conditions

    Science.gov (United States)

    Dănăilă, Eliza; Benea, Lidia; Caron, Nadège; Raquet, Olivier

    2016-09-01

    In this study Ni/nano-TiC functional composite coatings were produced by electro-codeposition of TiC nanoparticles (50 nm mean diameter) with nickel on 304L stainless steel support. Coatings were obtained from a Watts classical solution in which TiC nanoparticles were added. The surface morphology, chemical composition, structure, roughness and thickness, were evaluated in relation to the effect of TiC nanoparticles incorporation into Ni matrix. It was found that incorporation of TiC nanoparticles into the nickel matrix produces morphological changes in the deposit and increases the roughness. The fretting wear behavior in wet conditions of the obtained coatings was evaluated on a ball-on-plate configuration. To evaluate the wet fretting wear (tribocorrosion) behavior the open circuit potential was measured before, during and after the fretting tests at room temperature in the solution that simulates the primary water circuit of Pressurized Water Reactors. The results show that Ni/nano-TiC composite coatings exhibited a low friction coefficient, high nanohardness and fretting wear resistance in wet conditions compared with pure Ni coatings.

  10. 激光原位制备硼化钛与镍钛合金增强钛基复合涂层%LASER IN SITU SYNTHESIZED TITANIUM DIBORIDE AND NITINOL REINFORCE TITANIUM MATRIX COMPOSITE COATINGS

    Institute of Scientific and Technical Information of China (English)

    林英华; 雷永平; 符寒光; 林健

    2014-01-01

    以不同配比的Ni粉末和TiB2粉末混合物为预置层,利用激光原位技术在钛合金表面制备了bcc结构的NiTi合金、TiB短纤维与TiB2颗粒增强钛基复合涂层.运用XRD,SEM与EPMA等实验手段,对合成的钛基复合涂层进行测试分析.结果表明,随着激光功率密度与Ni粉末添加量的增加,涂层表面成型质量得到改善;然而随着Ni添加量的提高,涂层中出现了NiTi2新相,且TiB短纤维变得粗大;通过热力学计算可知,反应驱动力大小顺序为Ni3Ti>NiTi2>NiTi>TiB,并结合涂层中相种类及含量的变化规律,探讨了不同元素反应间的竞争机制.%Laser cladding is a technique in which a laser beam is used as the heating source to melt the alloy powder to be clad on the surface of titanium alloy substrate.Currently,the surface of many titanium alloy components needs repairing after a period of service in order to extend their service life.TiB and TiB2 are considered as the excellent ceramic reinforced particle for their compatible physical and thermodynamic properties,high hardness and Young's modulus of elasticity.The intermetallic compound NiTi,well-known for its shape memory effect and pseudo-elasticity,is one of the rarely few intermetallic compounds having excellent combination of high strength,ductility and toughness as well as excellent wear resistance and fabrication processing properties.An insitu TiB/TiB2 structured ceramic materials as the reinforcing phase and NiTi intermetallic phase as the matrix would be expected to have an outstanding combination of high hardness and toughness.NiTi alloy,TiB short fiber and TiB2 particulate reinforced titanium matrix composite coatings were prepared by laser in situ synthesis on titanium surface with different ratios of Ni powder and TiB2 powder mixture as a preset level.Synthesis of titanium matrix composite coating was analyzed by XRD,SEM and EPMA.The results show that the surface quality of the coating increases with

  11. Manufacturing Titanium Metal Matrix Composites by Consolidating Matrix Coated Fibres

    Institute of Scientific and Technical Information of China (English)

    Hua-Xin PENG

    2005-01-01

    Titanium metal matrix composites (TiMMCs) reinforced by continuous silicon carbide fibres are being developed for aerospace applications. TiMMCs manufactured by the consolidation of matrix-coated fibre (MCF) method offer optimum properties because of the resulting uniform fibre distribution, minimum fibre damage and fibre volume fraction control. In this paper, the consolidation of Ti-6Al-4V matrix-coated SiC fibres during vacuum hot pressing has been investigated. Experiments were carried out on multi-ply MCFs under vacuum hot pressing (VHP). In contrast to most of existing studies, the fibre arrangement has been carefully controlled either in square or hexagonal arraysthroughout the consolidated sample. This has enabled the dynamic consolidation behaviour of MCFs to be demonstrated by eliminating the fibre re-arrangement during the VHP process. The microstructural evolution of the matrix coating was reported and the deformation mechanisms involved were discussed.

  12. Microstructural characterization of titanium matrix composite coatings reinforced by in situ synthesized TiB + TiC fabricated on Ti6Al4V by laser cladding

    Institute of Scientific and Technical Information of China (English)

    LI Jun; YU Zhishui; WANG Huiping; LI Manping

    2010-01-01

    Titanium-based composite coatings reinforced by in situ synthesized TiB and TiC particles between titanium and B4C were successfully fab-ricated on Ti6A14V by laser cladding. Phase constituents of the coatings were predicted by thermodynamic calculations in the Ti-B4C-Al and Ti-B-C-Al systems, respectively, and were validated well by X-ray diffraction (XRD) analysis results. Microstructural and metallographic analyses were made by scanning electron microscopy (SEM) and electron probe micro-analysis (EPMA). The results show that the coatings are mainly composed of α-Ti cellular dendrites and the eutecticum in which a large number of needle-shaped TiB and a few equiaxial TiC particles are embedded. C is enriched in α-Ti cellular dendrites and far exceeds the theoretical maximum dissolubility, owing to the extension of saturation during laser cladding. The coatings have a good metallurgical bond with the substrate due to the existence of the dilution zone, in which a great amount of lamella β-Ti grains consisting of a thin needle-shaped martensitic microstructurc are present and grow parallel to the heat flux direction; a few TiB and TiC reinforcements are observed at the boundaries of initial β-Ti grains.

  13. Carbide-reinforced metal matrix composite by direct metal deposition

    Science.gov (United States)

    Novichenko, D.; Thivillon, L.; Bertrand, Ph.; Smurov, I.

    Direct metal deposition (DMD) is an automated 3D laser cladding technology with co-axial powder injection for industrial applications. The actual objective is to demonstrate the possibility to produce metal matrix composite objects in a single-step process. Powders of Fe-based alloy (16NCD13) and titanium carbide (TiC) are premixed before cladding. Volume content of the carbide-reinforced phase is varied. Relationships between the main laser cladding parameters and the geometry of the built-up objects (single track, 2D coating) are discussed. On the base of parametric study, a laser cladding process map for the deposition of individual tracks was established. Microstructure and composition of the laser-fabricated metal matrix composite objects are examined. Two different types of structures: (a) with the presence of undissolved and (b) precipitated titanium carbides are observed. Mechanism of formation of diverse precipitated titanium carbides is studied.

  14. Room-Temperature and High-Temperature Tensile Mechanical Properties of TA15 Titanium Alloy and TiB Whisker-Reinforced TA15 Matrix Composites Fabricated by Vacuum Hot-Pressing Sintering

    Directory of Open Access Journals (Sweden)

    Yangju Feng

    2017-04-01

    Full Text Available In this paper, the microstructure, the room-temperature and high-temperature tensile mechanical properties of monolithic TA15 alloy and TiB whisker-reinforced TA15 titanium matrix composites (TiBw/TA15 fabricated by vacuum hot-pressing sintering were investigated. The microstructure results showed that there were no obvious differences in the microstructure between monolithic TA15 alloy and TiBw/TA15 composites, except whether or not the grain boundaries contained TiBw. After sintering, the matrix microstructure presented a typical Widmanstätten structure and the size of primary β grain was consistent with the size of spherical TA15 titanium metallic powders. This result demonstrated that TiBw was not the only factor limiting grain coarsening of the primary β grain. Moreover, the grain coarsening of α colonies was obvious, and high-angle grain boundaries (HAGBs were distributed within the primary β grain. In addition, TiBw played an important role in the microstructure evolution. In the composites, TiBw were randomly distributed in the matrix and surrounded by a large number of low-angle grain boundaries (LAGBs. Globularization of α phase occurred prior, near the TiBw region, because TiBw provided the nucleation site for the equiaxed α phase. The room-temperature and high-temperature tensile results showed that TiBw distributed at the primary β grain boundaries can strengthen the grain boundary, but reduce the connectivity of the matrix. Therefore, compared to the monolithic TA15 alloy fabricated by the same process, the tensile strength of the composites increased, and the tensile elongation decreased. Moreover, with the addition of TiBw, the fracture mechanism was changed to a mixture of brittle fracture and ductile failure (composites from ductile failure (monolithic TA15 alloy. The fracture surfaces of TiBw/TA15 composites were the grain boundaries of the primary β grain where the majority of TiB whiskers distributed, i.e., the

  15. Study on Titanium Carbide Particulate Reinforced Iron Matrix Composite%碳化钛颗粒增强铁基表面复合材料的研究

    Institute of Scientific and Technical Information of China (English)

    王晓莉; 王静; 伏思静; 胡志华

    2011-01-01

    TiC particulates reinforced iron matrix surface composite was produced by cast technique and in-situ synthesis technique. The surface composite was investigated from the aspect of thermo-dynamics, microstructure, wear-resistance and oxidation-resistance. The results show that TiC particles with the content of 40% in the size of 1 ~3 μm generate in iron matrix on the surface of composite. The surface composite and gray iron exhibite excellent metallurgy-bonding. Fe-TiC surface composite shows better oxidation-resistance at 900 'C and better wear-resistance under the condition of dry sliding.%采用铸造与原位合成技术制备了TiC颗粒增强铁基表面复合材料,从热力学、微观结构、耐磨性能和抗高温氧化性方面对制备的表面复合材料进行了研究.结果表明:在表面复合材料的基体中生成了细小TiC颗粒,尺寸为1~3 μm,含量约为40vol%;表面复合材料层与灰铸铁之间有良好的冶金结合界面.在干磨损条件下,尤其在重载时,Fe-TiC表面复合材料表现出优异的耐磨性;在900℃氧化条件下,Fe-TiC表面复合材料表现出优良的抗氧化性.

  16. Continuous fiber-reinforced titanium aluminide composites

    Science.gov (United States)

    Mackay, R. A.; Brindley, P. K.; Froes, F. H.

    1991-01-01

    An account is given of the fabrication techniques, microstructural characteristics, and mechanical behavior of a lightweight, high service temperature SiC-reinforced alpha-2 Ti-14Al-21Nb intermetallic-matrix composite. Fabrication techniques under investigation to improve the low-temperature ductility and environmental resistance of this material system, while reducing manufacturing costs to competitive levels, encompass powder-cloth processing, foil-fiber-foil processing, and thermal-spray processing. Attention is given to composite microstructure problems associated with fiber distribution and fiber-matrix interfaces, as well as with mismatches of thermal-expansion coefficient; major improvements are noted to be required in tensile properties, thermal cycling effects, mechanical damage, creep, and environmental effects.

  17. Titanium Carbide Nanofibers-Reinforced Aluminum Compacts, a New Strategy to Enhance Mechanical Properties

    Directory of Open Access Journals (Sweden)

    Khalil Abdelrazek Khalil

    2016-05-01

    Full Text Available TiC nanofibers reinforced Al matrix composites were produced by High Frequency Induction Heat Sintering (HFIHS.The titanium carbide nanofibers with an average diameter of 90 nm are first prepared by electrospinning technique and high temperature calcination process. A composite solution containing polyacrylonitrile and titanium isopropoxide is first electrospun into the nanofibers, which are subsequently stabilized and then calcined to produce the desired TiC nanofibers. The X-ray diffraction pattern and transmission electron microscopy results show that the main phase of the as-synthesized nanofibers is titanium carbide. The TiC nanofibers is then mixed with the aluminum powders and introduced into high frequency induction heat sintering (HFIHS to produce composites of TiC nanofibers reinforced aluminum matrix. The potential application of the TiC nanofibers reinforced aluminum matrix composites was systematically investigated. 99.5% relative density and around 85 HV (833 MPa Vickers hardness of the Al reinforced with 5 wt % TiC nanofiber has been obtained. Furthermore, the sample of Al contains 5 wt % TiC, has the highest value of compression and yield strength of about 415 and 350 MPa, respectively. The ductility of the Al/5 wt % TiC showed increasing with increasing the TiC contents.

  18. Synthesis and Characterization of TiB2 Reinforced Aluminium Matrix Composites: A Review

    Science.gov (United States)

    Kumar, Narendra; Gautam, Gaurav; Gautam, Rakesh Kumar; Mohan, Anita; Mohan, Sunil

    2016-10-01

    Aluminium-matrix composites (AMCs) are developed to meet the demands of light weight high performance materials in aerospace, automotive, marine and other applications. The properties of AMCs can be tailored suitably by combinations of matrix, reinforcement and processing route. AMCs are one of the most attractive alternatives for the manufacturing of light weight and high strength parts due to their low density and high specific strength. There are various techniques for preparing the AMCs with different reinforcement particles. In AMCs, the reinforcements are usually in the form of metal oxides, carbides, borides, nitrides and their combination. Among the various reinforcements titanium di-boride (TiB2) is of much interest due to its excellent stiffness, hardness, and wear resistance. This paper attempts to provide an overview to explore the possibilities of synthesizing titanium di-boride reinforced AMCs with different techniques. The mechanical and tribological properties of these composites have been emphasized to project these as tribo-materials.

  19. Intermetallic and titanium matrix composite materials for hypersonic applications

    Energy Technology Data Exchange (ETDEWEB)

    Berton, B.; Surdon, G.; Colin, C. [Dassault Aviation, Saint-Cloud (France)]|[Aersopatiale Space & Defence, St Medard en Jalles (France)

    1995-09-01

    As part of the French Program of Research and Technology for Advanced Hypersonic Propulsion (PREPHA) which was launched in 1992 between Aerospatiale, Dassault Aviation, ONERA, SNECMA and SEP, an important work is specially devoted to the development of titanium and intermetallic composite materials for large airframe structures. At Dassault Aviation, starting from a long experience in Superplastic Forming - Diffusion Bonding (SPF-DB) of titanium parts, the effort is brought on the manufacturing and characterization of composites made from Timet beta 21S or IMI 834 foils and Textron SCS6 fiber fabrics. At `Aersopatiale Espace & Defence`, associated since a long time about intermetallic composite materials with university research laboratories, the principal effort is brought on plasma technology to develop the gamma titanium aluminide TiAl matrix composite reinforced by protected silicon carbide fibers (BP SM 1240 or TEXTRON SCS6). The objective, is to achieve, after 3 years of time, to elaborate a medium size integrally stiffened panel (300 x 600 sq mm).

  20. Discontinuously reinforced intermetallic matrix composites via XD synthesis. [exothermal dispersion

    Science.gov (United States)

    Kumar, K. S.; Whittenberger, J. D.

    1992-01-01

    A review is given of recent results obtained for discontinuously reinforced intermetallic matrix composites produced using the XD process. Intermetallic matrices investigated include NiAl, multiphase NiAl + Ni2AlTi, CoAl, near-gamma titanium aluminides, and Ll2 trialuminides containing minor amounts of second phase. Such mechanical properties as low and high temperature strength, compressive and tensile creep, elastic modulus, ambient ductility, and fracture toughness are discussed as functions of reinforcement size, shape, and volume fraction. Microstructures before and after deformation are examined and correlated with measured properties. An observation of interest in many of the systems examined is 'dispersion weakening' at high temperatures and high strain rates. This behavior is not specific to the XD process; rather similar observations have been reported in other discontinuous composites. Proposed mechanisms for this behavior are presented.

  1. Electrochemical process for the manufacturing of titanium alloy matrix composites

    Directory of Open Access Journals (Sweden)

    V. Soare

    2009-07-01

    Full Text Available The paper presents a new method for precursors’ synthesis of titanium alloys matrix composites through an electrochemical process in molten calcium chloride. The cathode of the cell was made from metallic oxides powders and reinforcement ceramic particles, which were pressed and sintered into disk form and the anode from graphite. The process occurred at 850 °C, in two stages, at 2,7 / 3,2 V: the ionization of the oxygen in oxides and the reduction with calcium formed by electrolysis of calcium oxide fed in the electrolyte. The obtained composite precursors, in a form of metallic sponge, were consolidated by pressing and sintering. Chemical and structural analyses on composites samples were performed.

  2. Manufacturing techniques for titanium aluminide based alloys and metal matrix composites

    Science.gov (United States)

    Kothari, Kunal B.

    -sized titanium aluminide powders were rapidly consolidated to form near-net shape titanium aluminide parts in form of small discs and tiles. The rapidly consolidated titanium aluminide parts were found to be fully dense. The microstructure morphology was found to vary with consolidation conditions. The mechanical properties were found to be significantly dependent on microstructure morphology and grain size. Due to rapid consolidation, grain growth during consolidation was limited, which in turn led to enhanced mechanical properties. The high temperature mechanical properties for the consolidated titanium aluminide samples were characterized and were found to retain good mechanical performance up to 700°C. Micron-sized titanium aluminide powders with slightly less Aluminum and small Nb, and Cr additions were rapidly consolidated into near-net shape parts. The consolidated parts were found to exhibit enhanced mechanical performance in terms of ductility and yield strength. The negative effect of Oxygen on the flexural strength at high temperatures was found to be reduced with the addition of Nb. In an effort to further reduce the grain size of the consolidated titanium aluminide samples, the as-received titanium aluminide powders were milled in an attrition mill. The average powder particle size of the powders was reduced by 60% after milling. The milled powders were then rapidly consolidated. The grain size of the consolidated parts was found to be in the sub-micrometer range. The mechanical properties were found to be significantly enhanced due to reduction of grain size in the sub-micrometer range. In order to develop a metal matrix composite based on titanium aluminide matrix reinforced with titanium boride, an experiment to study the effect of rapid consolidation on titanium diboride powders was conducted. Micron-sized titanium diboride powders were consolidated and were found to be 93% dense and exhibited minimal grain growth. The low density of the consolidated part was

  3. Titanium Implant Osseointegration Problems with Alternate Solutions Using Epoxy/Carbon-Fiber-Reinforced Composite.

    Science.gov (United States)

    Petersen, Richard C

    2014-12-01

    The aim of the article is to present recent developments in material research with bisphenyl-polymer/carbon-fiber-reinforced composite that have produced highly influential results toward improving upon current titanium bone implant clinical osseointegration success. Titanium is now the standard intra-oral tooth root/bone implant material with biocompatible interface relationships that confer potential osseointegration. Titanium produces a TiO2 oxide surface layer reactively that can provide chemical bonding through various electron interactions as a possible explanation for biocompatibility. Nevertheless, titanium alloy implants produce corrosion particles and fail by mechanisms generally related to surface interaction on bone to promote an inflammation with fibrous aseptic loosening or infection that can require implant removal. Further, lowered oxygen concentrations from poor vasculature at a foreign metal surface interface promote a build-up of host-cell-related electrons as free radicals and proton acid that can encourage infection and inflammation to greatly influence implant failure. To provide improved osseointegration many different coating processes and alternate polymer matrix composite (PMC) solutions have been considered that supply new designing potential to possibly overcome problems with titanium bone implants. Now for important consideration, PMCs have decisive biofunctional fabrication possibilities while maintaining mechanical properties from addition of high-strengthening varied fiber-reinforcement and complex fillers/additives to include hydroxyapatite or antimicrobial incorporation through thermoset polymers that cure at low temperatures. Topics/issues reviewed in this manuscript include titanium corrosion, implant infection, coatings and the new epoxy/carbon-fiber implant results discussing osseointegration with biocompatibility related to nonpolar molecular attractions with secondary bonding, carbon fiber in vivo properties, electrical

  4. Titanium Implant Osseointegration Problems with Alternate Solutions Using Epoxy/Carbon-Fiber-Reinforced Composite

    Directory of Open Access Journals (Sweden)

    Richard C. Petersen

    2014-12-01

    Full Text Available The aim of the article is to present recent developments in material research with bisphenyl-polymer/carbon-fiber-reinforced composite that have produced highly influential results toward improving upon current titanium bone implant clinical osseointegration success. Titanium is now the standard intra-oral tooth root/bone implant material with biocompatible interface relationships that confer potential osseointegration. Titanium produces a TiO2 oxide surface layer reactively that can provide chemical bonding through various electron interactions as a possible explanation for biocompatibility. Nevertheless, titanium alloy implants produce corrosion particles and fail by mechanisms generally related to surface interaction on bone to promote an inflammation with fibrous aseptic loosening or infection that can require implant removal. Further, lowered oxygen concentrations from poor vasculature at a foreign metal surface interface promote a build-up of host-cell-related electrons as free radicals and proton acid that can encourage infection and inflammation to greatly influence implant failure. To provide improved osseointegration many different coating processes and alternate polymer matrix composite (PMC solutions have been considered that supply new designing potential to possibly overcome problems with titanium bone implants. Now for important consideration, PMCs have decisive biofunctional fabrication possibilities while maintaining mechanical properties from addition of high-strengthening varied fiber-reinforcement and complex fillers/additives to include hydroxyapatite or antimicrobial incorporation through thermoset polymers that cure at low temperatures. Topics/issues reviewed in this manuscript include titanium corrosion, implant infection, coatings and the new epoxy/carbon-fiber implant results discussing osseointegration with biocompatibility related to nonpolar molecular attractions with secondary bonding, carbon fiber in vivo

  5. N2和Ar气氛下激光原位合成TiN/钛基复合涂层%N2/Ar Aiding Laser In-Situ Synthesized TiN Particle Reinforced Titanium Matrix Composite Coating

    Institute of Scientific and Technical Information of China (English)

    张晓伟; 刘洪喜; 蒋业华; 王传琦

    2012-01-01

    By utilizing the high-temperature chemical reaction between Ti and A1N, TiN reinforced titanium matrix composite coating is in-situ synthesized on TC4 alloy substrate by laser cladding technique under nitrogen and argon atmosphere, respectively. The microstructure, micro-hardness and relative oxidation resistance of treated samples are examined by X-ray diffraction, scanning electron microscopy, micro-hardness tester and air furnace. The results show that the microstructure and cross section micro-hardness distribution of laser cladding composite coating are more uniform under nitrogen atmosphere than those under argon atmosphere, and the in-situ combustion synthesis reaction is more fully. The composite coating is mainly composed of TiN and Ti3Al phase under nitrogen atmosphere, while it is mainly composed of TiN and a-Ti phase under argon atmosphere. The average micro-hardness of laser in-situ synthesized composite coating changes gradually and increases by 40. 7% under nitrogen atmosphere; however, it changes sharply under argon atmosphere. The relative oxidation resistance values of laser cladding composite coating at 600 ℃ and 800 ℃ under nitrogen atmosphere are 6. 83 and 1. 94 times of those of the TC4 alloy substrate, and increase by 17.96% and 19.75% than those under argon atmosphere, respectively.%分别以高纯N2和高纯Ar为保护气体,在TC4钛合金基材表面激光原位合成了TiN/钛基复合涂层.运用X射线衍射仪、扫描电子显微镜和显微硬度计对复合涂层的微观结构和力学性能进行了分析,通过空气电阻炉初步测试了复合涂层的相对高温耐氧化性.结果表明,Ar气氛下原位合成的复合涂层含有较多未完全反应的Ti相,组织均匀性较差,涂层截面显微硬度分布不均;而N2气氛下的原位合成反应比较充分,原位合成复合涂层主要由TiN和Ti3 Al两相组成,涂层组织均匀致密,含较多高硬度TiN相,显微硬度自基体至涂层过渡平缓,且

  6. Oxidation resistant coating for titanium alloys and titanium alloy matrix composites

    Science.gov (United States)

    Brindley, William J. (Inventor); Smialek, James L. (Inventor); Rouge, Carl J. (Inventor)

    1992-01-01

    An oxidation resistant coating for titanium alloys and titanium alloy matrix composites comprises an MCrAlX material. M is a metal selected from nickel, cobalt, and iron. X is an active element selected from Y, Yb, Zr, and Hf.

  7. Aluminum matrix composites reinforced with alumina nanoparticles

    CERN Document Server

    Casati, Riccardo

    2016-01-01

    This book describes the latest efforts to develop aluminum nanocomposites with enhanced damping and mechanical properties and good workability. The nanocomposites exhibited high strength, improved damping behavior and good ductility, making them suitable for use as wires. Since the production of metal matrix nanocomposites by conventional melting processes is considered extremely problematic (because of the poor wettability of the nanoparticles), different powder metallurgy routes were investigated, including high-energy ball milling and unconventional compaction methods. Special attention was paid to the structural characterization at the micro- and nanoscale, as uniform nanoparticle dispersion in metal matrix is of prime importance. The aluminum nanocomposites displayed an ultrafine microstructure reinforced with alumina nanoparticles produced in situ or added ex situ. The physical, mechanical and functional characteristics of the materials produced were evaluated using different mechanical tests and micros...

  8. Polypropylene matrix composites reinforced with coconut fibers

    Directory of Open Access Journals (Sweden)

    Maria Virginia Gelfuso

    2011-09-01

    Full Text Available Polypropylene matrix composites reinforced with treated coconut fibers were produced. Fibers chemically treated (alkalization-CCUV samples or mechanically treated (ultrasonic shockwave-CMUV samples were dried using UV radiation. The goal was to combine low cost and eco-friendly treatments to improve fiber-matrix adhesion. Composite samples containing up to 20 vol. (% of untreated and treated coconut fibers were taken from boxes fabricated by injection molding. Water absorption and mechanical properties were investigated according to ASTM D570-98 and ASTM D638-03, respectively. Electrical characterizations were carried out to identify applications of these composites in the electrical sector. NBR 10296-Electrical Tracking Standard (specific to industry applications and conductivity measurements were obtained applying 5 kV DC to the samples. CMUV samples containing 5 vol. (% fiber presented superior tensile strength values (σ~28 MPa compared to the untreated fibers composite (σ~22 MPa or alkali treatment (σ~24 MPa. However, CMUV composites containing 10 vol. (% fiber presented best results for the electrical tracking test and electrical resistivity (3 × 10(7 Ω.m. The results suggest that composites reinforced with mechanically treated coconut fibers are suitable for electrical applications.

  9. Evaluation the Properties of Titanium Matrix Composites by Melting Route Synthesis

    Institute of Scientific and Technical Information of China (English)

    2008-01-01

    The main purpose of this study is an in-situ synthesis of (TiB+TiC) hybrid titanium matrix composites (TMCs) by vacuum induction melting method and to verify its mechanical properties. The melting route was adopted to synthesize the commercial pure titanium (cp Ti) and granular boron carbide (B4C). The reinforcements, the fraction of 10 vol. pct, were formed by adding 1.88 wt pct B4C to cp Ti. After in-situ synthesis of TMCs, electron probe micro-analysis elemental mapping was carried out to confirm the distribution and shape of reinforcements. The cone-on-disk type sliding wear test was also done for the identification of TMCs. It is concluded that (TiB+TiC) hybrid TMCs can be in-situ synthesized and has better wear properties than H13.

  10. Texture and residual strain in SiC/Ti-6-2-4-2 titanium matrix composites

    Energy Technology Data Exchange (ETDEWEB)

    Rangaswamy, P.; Bennett, K.; Bourke, M.A.M.; Dreele, R. von; Roberts, J.A. [Los Alamos National Lab., NM (United States). Manuel Lujan Jr. Neutron Scattering Center; Jayaraman, N. [Univ. of Cincinnati, OH (United States). Dept. of Materials Science and Engineering

    1997-11-01

    Residual strain and texture variations were measured in two Titanium matrix composites reinforced with Silicon Carbide fibers (Ti/SiC) having the same composition but fabricated by dramatically different processing routes. In both specimens the Titanium matrix comprised an {alpha}/{beta} alloy (Ti-6242) containing approximately 35% by volume of continuous SiC fibers. In one case the matrix was produced by a plasma spray (PS) route and the other by a wire drawing (WD) process. The resulting textures in the matrix differ significantly, from approximately random for the PS matrix to 6.25X random in the WD matrix. No significant differences in matrix residual strains between the composites prepared by the two procedures were noted. Plane-specific elastic moduli, measured in load tests on the unreinforced matrices also showed little difference.

  11. Fatigue Crack Growth Rate in SiC Fiber Reinforced Titanium Matrix Composites%SiC维纤增强钛基复合材料的疲劳裂纹扩展速率

    Institute of Scientific and Technical Information of China (English)

    王海丽; 杨延清; 冯广海; 罗贤; 张荣军; 刘斌

    2012-01-01

    SiC fiber reinforced Ti-6Al-4V composites (TMCs) was prepared by the foil-fiber-foil method. The fatigue crack growth rate of the TMCs was investigated under the condition of f=10 Hz, R=0.1 and σmax =300 MPa, and the fracture surface of TMCs was observed by scanning electron microscopy (SEM). Results show that the crack growth rate at the stage II of crack propagation is well consistent with Gaussian function. SEM observation indicates that distinct fatigue striations exist in the stable propagation area of the fatigue crack of the Ti-6A1-4V matrix. The failure modes of TMCs include fiber breakage, matrix cracking, fiber/matrix interfacial debonding, et al under the loading condition.%用箔-纤维-箔法制备SiC纤维增强Ti-6Al-4V复合材料,研究复合材料在加载频率f=10Hz、应力比R=0.1、最大应力σmax=300 MPa条件下的疲劳裂纹扩展速率(da/dN),并采用扫描电子显微镜对疲劳破坏断口进行观察和分析.结果显示,在该加载条件下,复合材料第Ⅱ阶段疲劳裂纹扩展速率符合高斯函数.断口观察表明,复合材料的基体在裂纹稳态扩展区出现明显的疲劳条带,复合材料的疲劳损伤可以分为纤维断裂、基体开裂和纤维/基体界面脱粘等多种形式.

  12. Microstructural evolution in laser deposited nickel-titanium-carbon in situ metal matrix composites

    Energy Technology Data Exchange (ETDEWEB)

    Gopagoni, S. [Center for Advanced Research and Technology and Department of Materials Science and Engineering, University of North Texas, Denton, TX 76203 (United States); Hwang, J.Y., E-mail: Junyeon.Hwang@unt.edu [Center for Advanced Research and Technology and Department of Materials Science and Engineering, University of North Texas, Denton, TX 76203 (United States); Singh, A.R.P.; Mensah, B.A.; Bunce, N. [Center for Advanced Research and Technology and Department of Materials Science and Engineering, University of North Texas, Denton, TX 76203 (United States); Tiley, J. [Materials and Manufacturing Directorate, Air Force Research Laboratory, Dayton, OH 45433 (United States); Scharf, T.W.; Banerjee, R. [Center for Advanced Research and Technology and Department of Materials Science and Engineering, University of North Texas, Denton, TX 76203 (United States)

    2011-01-28

    Research highlights: > Laser deposition of Ni-TiC composites with a relatively low volume fraction of refined homogeneously distributed carbide precipitates resulting from an in situ reaction between elemental titanium and carbon (graphite) within the molten nickel pool. > Detailed characterization of the Ni/TiC interface using high resolution TEM. > Evaluation of the microhardness and tribological properties of this novel in situ composite with comparisons to laser deposited pure Ni. - Abstract: Laser deposition of a mixture of elemental nickel, titanium, and carbon (graphite) powders via the laser engineered net shaping (LENS) process results in an in situ titanium carbide reinforced nickel metal matrix composites. The composites have been characterized in detail using X-ray diffraction, scanning electron microscopy (including energy dispersive spectroscopy mapping), Auger electron spectroscopy, and transmission (including high resolution) electron microscopy. Both primary and eutectic titanium carbides, observed in this composite, exhibited the FCC-TiC structure (NaCl-type). Detailed characterization of the nickel/titanium carbide interface was carried out using high resolution TEM with the orientation relationship between the phases being <1 0 0> TiC//<1 1 0> Ni and (0 0 2) TiC//(1-bar 11) Ni. Mechanical and tribological testing determined that the composites exhibited a relatively high hardness of 370 VHN and a steady-state friction coefficient of {approx}0.5, both improvements in comparison to LENS deposited pure Ni.

  13. Nanoscale Reinforced, Polymer Derived Ceramic Matrix Coatings

    Energy Technology Data Exchange (ETDEWEB)

    Rajendra Bordia

    2009-07-31

    The goal of this project was to explore and develop a novel class of nanoscale reinforced ceramic coatings for high temperature (600-1000 C) corrosion protection of metallic components in a coal-fired environment. It was focused on developing coatings that are easy to process and low cost. The approach was to use high-yield preceramic polymers loaded with nano-size fillers. The complex interplay of the particles in the polymer, their role in controlling shrinkage and phase evolution during thermal treatment, resulting densification and microstructural evolution, mechanical properties and effectiveness as corrosion protection coatings were investigated. Fe-and Ni-based alloys currently used in coal-fired environments do not possess the requisite corrosion and oxidation resistance for next generation of advanced power systems. One example of this is the power plants that use ultra supercritical steam as the working fluid. The increase in thermal efficiency of the plant and decrease in pollutant emissions are only possible by changing the properties of steam from supercritical to ultra supercritical. However, the conditions, 650 C and 34.5 MPa, are too severe and result in higher rate of corrosion due to higher metal temperatures. Coating the metallic components with ceramics that are resistant to corrosion, oxidation and erosion, is an economical and immediate solution to this problem. Good high temperature corrosion protection ceramic coatings for metallic structures must have a set of properties that are difficult to achieve using established processing techniques. The required properties include ease of coating complex shapes, low processing temperatures, thermal expansion match with metallic structures and good mechanical and chemical properties. Nanoscale reinforced composite coatings in which the matrix is derived from preceramic polymers have the potential to meet these requirements. The research was focused on developing suitable material systems and

  14. Reactive Spark Plasma Sintering (SPS) of Nitride Reinforced Titanium Alloy Composites (Postprint)

    Science.gov (United States)

    2014-08-15

    ies on in situ alloying and reactions during the SPS process. A recent study on SPS processing of hafnium carbide (HfC) starting from a blend of...AFRL-RX-WP-JA-2014-0177 REACTIVE SPARK PLASMA SINTERING (SPS) OF NITRIDE REINFORCED TITANIUM ALLOY COMPOSITES (POSTPRINT) Jaimie S...SINTERING (SPS) OF NITRIDE REINFORCED TITANIUM ALLOY COMPOSITES (POSTPRINT) 5a. CONTRACT NUMBER In-House 5b. GRANT NUMBER 5c. PROGRAM ELEMENT

  15. CONSTITUTIVE RELATION OF DISCONTINUOUS REINFORCED METAL-MATRIX COMPOSITES

    Institute of Scientific and Technical Information of China (English)

    季葆华; 王自强

    2001-01-01

    A micromechanical model is developed to simulate the mechanical behaviors of discontinuous reinforced composites. The analysis for a representative unit cell is based on the assumption of a periodic array of aligned reinforcements.The minimum energy principle is used to determine the unknown coefficients of the displacement field of the unit cell. The constitutive behavior of composites is studied to obtain the relationship between the main variables of matrix and reinforcements.It is concluded that the flow strength of composites is strongly influenced by volume fraction, aspect ratio of reinforcement, and the strain hardening exponent of matrix.An analytical constitutive relation of composites is obtained. The predicted results are in agreement with the existing experimental and numerical results.

  16. Metal Matrix Composites Reinforced by Nano-Particles—A Review

    Directory of Open Access Journals (Sweden)

    Riccardo Casati

    2014-03-01

    Full Text Available Metal matrix composites reinforced by nano-particles are very promising materials, suitable for a large number of applications. These composites consist of a metal matrix filled with nano-particles featuring physical and mechanical properties very different from those of the matrix. The nano-particles can improve the base material in terms of wear resistance, damping properties and mechanical strength. Different kinds of metals, predominantly Al, Mg and Cu, have been employed for the production of composites reinforced by nano-ceramic particles such as carbides, nitrides, oxides as well as carbon nanotubes. The main issue of concern for the synthesis of these materials consists in the low wettability of the reinforcement phase by the molten metal, which does not allow the synthesis by conventional casting methods. Several alternative routes have been presented in literature for the production of nano-composites. This work is aimed at reviewing the most important manufacturing techniques used for the synthesis of bulk metal matrix nanocomposites. Moreover, the strengthening mechanisms responsible for the improvement of mechanical properties of nano-reinforced metal matrix composites have been reviewed and the main potential applications of this new class of materials are envisaged.

  17. Texture and residual strain in SiC/Ti-6-2-4-2 titanium matrix composites

    Energy Technology Data Exchange (ETDEWEB)

    Rangaswamy, P.; Bourke, M.A.M.; Von Dreele, R.; Bennett, K.; Roberts, J.A. [Los Alamos National Lab., NM (United States); Daymond, M. [Rutherford Appleton Lab., Chilton (United Kingdom); Jayaraman, N. [Univ. of Cincinnati, OH (United States). Dept. of Materials Science and Engineering

    1998-12-31

    Residual strain and texture variations were measured in two Titanium matrix composites reinforced with Silicon Carbide fibers (Ti/SiC) of similar composition but fabricated by different processing routes. Each composite comprised a Ti-6242 {alpha}/{beta} matrix alloy containing 35% by volume continuous SiC fibers. In one composite, the matrix was produced by a plasma spray (PS) route, and in the other by a wire drawing (WD) process. The PS and WD composites were reinforced with SCS-6 (SiC) and Trimarc (SiC) fibers, respectively. The texture in the titanium matrices differed significantly, from approximately {approx} 1.1x random for the monolithic and composite produced by PS route to {approx} 17x random in the monolithic and {approx}6x random in the composite produced by the WD route. No significant differences in matrix residual strains between the composites prepared by the two procedures were noted. The Trimarc (WD) fibers recorded higher ({approx}1.3x) compressive strains than the SCS-6 (PS) fibers in all the measured directions. The plane-specific elastic moduli, measured in load tests on the un-reinforced matrices, showed little difference.

  18. Preparation technique of SiCp reinforced Al matrix composite

    Institute of Scientific and Technical Information of China (English)

    HAO Bin; CUI Hua; YU Zhi-yong; TAO Kai; YANG Bin; ZHANG Ji-shan

    2006-01-01

    A new preparation technique-"block dispersal and cast" method is introduced, and three kinds of powd.er mixing methods, vertical, horizontal and inclining styles, are compared. The results demonstrate that the inclining style is the best way to mix powders. The Al and nano SiC powders are pressed into blocks, dipped into molten Al, stirred into mold so that SiC/Al matrix composites can be obtained at last. The microstructure of SiC particle reinforced Al matrix composite prepared by "block dispersal and cast" method have been studied using scanning electron microscopy (SEM). Phase analysis has also been conducted by means of X-ray diffraction (XRD). The results show that nano SiC particles can be dispersed uniformly in Al matrix. Thus, it is feasible to prepare SiC particle reinforced Al matrix composites by this method.

  19. Residual stresses in shape memory alloy fiber reinforced aluminium matrix composite

    Science.gov (United States)

    Tsz Loong, Tang; Jamian, Saifulnizan; Ismail, Al Emran; Nur, Nik Hisyammudin Muhd; Watanabe, Yoshimi

    2017-01-01

    Process-induced residual stress in shape memory alloy (SMA) fiber reinforced aluminum (Al) matrix composite was simulated by ANSYS APDL. The manufacturing process of the composite named as NiTi/Al is start with loading and unloading process of nickel titanium (NiTi) wire as SMA to generate a residual plastic strain. Then, this plastic deformed NiTi wire would be embedded into Al to become a composite. Lastly, the composite is heated form 289 K to 363 K and then cooled back to 300 K. Residual stress is generated in composite because of shape memory effect of NiTi and mismatch of thermal coefficient between NiTi wire and Al matrix of composite. ANSYS APDL has been used to simulate the distribution of residual stress and strain in this process. A sensitivity test has been done to determine the optimum number of nodes and elements used. Hence, the number of nodes and elements used are 15680 and 13680, respectively. Furthermore, the distribution of residual stress and strain of nickel fiber reinforced aluminium matrix composite (Ni/Al) and titanium fiber reinforced aluminium matrix composite (Ti/Al) under same simulation process also has been simulated by ANSYS APDL as comparison to NiTi/Al. The simulation results show that compressive residual stress is generated on Al matrix of Ni/Al, Ti/Al and NiTi/Al during heating and cooling process. Besides that, they also have similar trend of residual stress distribution but difference in term of value. For Ni/Al and Ti/Al, they are 0.4% difference on their maximum compressive residual stress at 363K. At same circumstance, NiTi/Al has higher residual stress value which is about 425% higher than Ni/Al and Ti/Al composite. This implies that shape memory effect of NiTi fiber reinforced in composite able to generated higher compressive residual stress in Al matrix, hence able to enhance tensile property of the composite.

  20. Mechanically milled aluminium matrix composites reinforced with halloysite nanotubes

    Directory of Open Access Journals (Sweden)

    L.A. Dobrzański

    2012-12-01

    Full Text Available Purpose: The present work describes fabrication of aluminium AlMg1SiCu matrix composite materials reinforced with halloysite nanotubes by powder metallurgy techniques and hot extrusion.Design/methodology/approach: Mechanical milling, compacting and hot extrusion successively are considering as a method for manufacturing metal composite powders with a controlled fine microstructure and enhanced mechanical properties. It is possible by the repeated welding and fracturing of powders particles mixture in a highly energetic ball mill.Findings: The milling process has a huge influence on the properties of powder materials, changing the spherical morphology of as-received powder during milling process to flattened one due to particle deformation followed by welding and fracturing particles of deformed and hardened enough which allows to receive equiaxial particles morphology again. The investigation shows that so called brittle mineral particles yields to plastic deformation as good as ductile aluminium alloy particles. That indicates that the halloysite powder can play a role of the accelerator during mechanical milling. High energy ball milling as a method of mechanical milling improves the distribution of the halloysite reinforcing particles throughout the aluminium matrix, simultaneously reducing the size of particles. The apparent density changes versus milling time can be used to control the composite powders production by mechanical milling and the presence of halloysite reinforcements particles accelerates the mechanical milling process.Research limitations/implications: Contributes to knowledge about technology, structure and properties of aluminium alloy matrix composite material reinforced with mineral nanoparticles.Practical implications: Conducted research shows that applied technology allows obtaining very good microstructural characteristics.Originality/value: It has been confirmed that halloysite nanotubes can be applied as an effective

  1. The synthesis of titanium carbide-reinforced carbon nanofibers.

    Science.gov (United States)

    Zhu, Pinwen; Hong, Youliang; Liu, Bingbing; Zou, Guangtian

    2009-06-24

    Tailoring hard materials into nanoscale building blocks can greatly extend the applications of hard materials and, at the same time, also represents a significant challenge in the field of nanoscale science. This work reports a novel process for the preparation of carbon-based one-dimensional hard nanomaterials. The titanium carbide-carbon composite nanofibers with an average diameter of 90 nm are prepared by an electrospinning technique and a high temperature pyrolysis process. A composite solution containing polyacrylonitrile and titanium sources is first electrospun into the composite nanofibers, which are subsequently pyrolyzed to produce the desired products. The x-ray diffraction pattern and transmission electron microscopy results show that the main phase of the as-synthesized nanofibers is titanium carbide. The Raman analyses show that the composite nanofibers have low graphite clusters in comparison with the pure carbon nanofibers originating from the electrospun polyacrylonitrile nanofibers. The mechanical property tests demonstrate that the titanium carbide-carbon nanofiber membranes have four times higher tensile strength than the carbon nanofiber membranes, and the Young's modulus of the titanium carbide-carbon nanofiber membranes increases in direct proportion to the titanium quantity.

  2. The influence of thermal-mechanical processing on residual stresses in titanium matrix composites

    Energy Technology Data Exchange (ETDEWEB)

    Rangaswamy, P. [Los Alamos National Lab., NM (United States); Bourke, M.A.M. [Los Alamos National Lab., NM (United States); Wright, P.K. [General Electric Aircraft Engines, Evendale, Cincinnati, OH (United States); Jayaraman, N. [Cincinnati Univ., OH (United States). Dept. of Materials Science and Engineering; Kartzmark, E. [Los Alamos National Lab., NM (United States); Roberts, J.A. [Los Alamos National Lab., NM (United States)

    1997-03-31

    The effects of three distinct thermo-mechanical processes on the residual stress state in a uni-directionally reinforced SCS-6/Ti-6-2-4-2 [0]{sub 6} titanium-alloy matrix composite were predicted using a finite element model. For comparison the residual stresses were measured using X-ray and neutron diffraction. Reductions in stress were predicted by the models and both experimental techniques recorded a reduction compared to the as-fabricated material. While the numerically predicted trends qualitatively agreed with the neutron measurements quantitative agreement was not achieved. In the longitudinal direction the neutron results showed closer agreement to the calculation whereas in the transverse direction the X-ray results did. Nevertheless the changes did correlate with improvement in fatigue lifetimes. (orig.)

  3. Particulate Titanium Matrix Composites Tested--Show Promise for Space Propulsion Applications

    Science.gov (United States)

    Lerch, Bradley A.; Ellis, J. Rodney; Arnold. Steven M.

    2004-01-01

    Uniformly distributed particle-strengthened titanium matrix composites (TMCs) can be manufactured at lower cost than many types of continuous-fiber composites. The innovative manufacturing technology combines cold and hot isostatic pressing procedures to produce near-final-shape components. Material stiffness is increased up to 26-percent greater than that of components made with conventional titanium materials at no significant increase in the weight. The improved mechanical performance and low-cost manufacturing capability motivated an independent review to assess the improved properties of ceramic titanium carbide (TiC) particulate-reinforced titanium at elevated temperature. Researchers at the NASA Glenn Research Center creatively designed and executed deformation and durability tests to reveal operating regimes where these materials could lower the cost and weight of space propulsion systems. The program compares the elevated-temperature performance of titanium alloy Ti-6Al-4V matrix material to an alloy containing 10 wt% of TiC particles. Initial experiments showed that at these relatively low particle concentrations the material stiffness of the TMC was improved 20 percent over that of the plain Ti-6Al-4V alloy when tested at 427 C. The proportional limit and ultimate strength of the composite in tension are 21- and 14-percent greater than those of the plain alloy. Compression tests showed that the proportional limit is about 30 percent greater for TMC than for the plain alloy. The enhanced deformation resistance of the TMC was also evident in a series of tensile and compressive stress relaxation tests that were made. Specimens were subjected to tensile or compressive strain amplitudes of 0.75 percent for 24 hr followed by a return to zero strain imposed for 24 hr. The stress relaxation data were normalized with respect to the maximum stress for each case and plotted as a function of time in the following graph. Tensile stresses relaxed 19 percent for the

  4. Corrosion and wear resistance of titanium- and aluminum-based metal matrix composites fabricated by direct metal laser deposition

    Science.gov (United States)

    Waldera, Benjamin L.

    Titanium- and Aluminum-based metal matrix composites (MMC) have shown favorable properties for aerospace applications such as airframes, reinforcement materials and joining elements. In this research, such coatings were developed by direct metal laser deposition with a powder-fed fiber coupled diode laser. The MMC formulations consisted of pure titanium and aluminum matrices with reinforcing powder blends of chromium carbide and tungsten carbide nickel alloy. Two powder formulations were investigated for each matrix material (Ti1, Ti2, Al1 and Al2). Titanium based composites were deposited onto a Ti6Al4V plate while aluminum composites were deposited onto AA 7075 and AA 5083 for Al1 and Al2, respectively. Microstructures of the MMCs were studied by optical and scanning electron microscopy. The hardness and reduced Young's modulus (Er) were assessed through depth-sensing instrumented nanoindentation. microhardness (Vickers) was also analyzed for each composite. The corrosion resistance of the MMCs were compared by monitoring open circuit potential (OCP), polarization resistance (Rp) and potentiodynamic polarization in 0.5 M NaCl to simulate exposure to seawater. The Ti-MMCs demonstrated improvements in hardness between 205% and 350% over Ti6Al4V. Al-MMCs showed improvements between 47% and 79% over AA 7075 and AA 5083. The MMCs showed an increase in anodic current density indicating the formation of a less protective surface oxide than the base metals.

  5. Fabrication of aluminum matrix composite reinforced with carbon nanotubes

    Institute of Scientific and Technical Information of China (English)

    2007-01-01

    1.0 wt.% carbon nanotube (CNT) reinforced 2024A1 matrix composite was fabricated by cold isostatic press and subsequent hot extrusion techniques. The mechanical properties of the composite were measured by a tensile test. Meanwhile, the fracture surfaces were examined using field emission scanning electron microscopy. The experimental results show that CNTs are dispersed homogeneously in the composite and that the interfaces of the Al matrix and the CNT bond well. Although the tensile strength and the Young's modulus of the composite are enhanced markedly, the elongation does not decrease when compared with the matrix material fabricated under the same process. The reasons for the increments may be the extraordinary mechanical properties of CNTs, and the bridging and pulling-out role of CNTs in the Al matrix composite.

  6. Carbon Fiber Reinforced Glass Matrix Composites for Space Based Applications.

    Science.gov (United States)

    1987-08-31

    composite plates were prepared using standard i, c-pressing procedures. The plates were cut into tensile specimens which were then subsequently notched...reinforced HMU composites were prepared using the matrix compositions and hot-pressing parameters shown in Table VI-1. The compositions are identical...shown in Figure VI-6. Traces of a- cristobalite are present in all three composites, with a noticeably larger amount present in the Nb20 5 composite. All

  7. Development of new ferritic alloys reinforced by nano titanium nitrides

    Energy Technology Data Exchange (ETDEWEB)

    Mathon, M.H., E-mail: marie-helene.mathon@cea.fr [Laboratoire Léon Brillouin, CEA-CNRS, CEA/Saclay, 91191 Gif-sur-Yvette (France); Perrut, M., E-mail: mikael.perrut@onera.fr [Laboratoire Léon Brillouin, CEA-CNRS, CEA/Saclay, 91191 Gif-sur-Yvette (France); Poirier, L., E-mail: poirier@nitruvid.com [Bodycote France and Belgium, 9 r Jean Poulmarch, 95100 Argenteuil (France); Ratti, M., E-mail: mathieu.ratti@snecma.fr [CEA, DEN, Service de Recherches Métallurgiques Appliquées, F91191 Gif-sur-Yvette (France); Hervé, N., E-mail: nicolas.herve@cea.fr [CEA, DRT, LITEN, F38054 Grenoble (France); Carlan, Y. de, E-mail: yann.decarlan@cea.fr [CEA, DEN, Service de Recherches Métallurgiques Appliquées, F91191 Gif-sur-Yvette (France)

    2015-01-15

    Nano-reinforced steels are considered for future nuclear reactors or for application at high temperature like the heat exchangers tubes or plates. Oxide Dispersion Strengthened (ODS) alloys are the most known of the nano-reinforced alloys. They exhibit high creep strength as well as high resistance to radiation damage. This article deals with the development of new nano reinforced alloys called Nitride Dispersed Strengthened (NDS). Those are also considered for nuclear applications and could exhibit higher ductility with a simplest fabrication way. Two main fabrication routes were studied: the co-milling of Fe–18Cr1W0.008N and TiH{sub 2} powders and the plasma nitration at low temperature of a Fe–18Cr1W0.8Ti powder. The materials were studied mainly by Small Angle Neutron Scattering. The feasibility of the reinforcement by nano-nitride particles is demonstrated. The final size of the nitrides can be similar (few nanometers) to the nano-oxides observed in ODS alloys. The mechanical properties of the new NDS show an amazing ductility at high temperature for a nano-reinforced alloy.

  8. Tungsten fiber reinforced copper matrix composites: A review

    Science.gov (United States)

    Mcdanels, David L.

    1989-01-01

    Tungsten fiber reinforced copper matrix (W/Cu) composites have served as an ideal model system with which to analyze the properties of metal matrix composites. A series of research programs were conducted to investigate the stress-strain behavior of W/Cu composites; the effect of fiber content on the strength, modulus, and conductivity of W/Cu composites; and the effect of alloying elements on the behavior of tungsten wire and of W/Cu composites. Later programs investigated the stress-rupture, creep, and impact behavior of these composites at elevated temperatures. Analysis of the results of these programs as allows prediction of the effects of fiber properties, matrix properties, and fiber content on the properties of W/Cu composites. These analyses form the basis for the rule-of-mixtures prediction of composite properties which was universally adopted as the criteria for measuring composite efficiency. In addition, the analyses allows extrapolation of potential properties of other metal matrix composites and are used to select candidate fibers and matrices for development of tungsten fiber reinforced superalloy composite materials for high temperature aircraft and rocket engine turbine applications. The W/Cu composite efforts are summarized, some of the results obtained are described, and an update is provided on more recent work using W/Cu composites as high strength, high thermal conductivity composite materials for high heat flux, elevated temperature applications.

  9. Preparation of SiC Fiber Reinforced Nickel Matrix Composite

    Institute of Scientific and Technical Information of China (English)

    Lu Zhang; Nanlin Shi; Jun Gong; Chao Sunt

    2012-01-01

    A method of preparing continuous(Al+Al2O3)-coated SiC fiber reinforced nickel matrix composite was presented,in which the diffusion between SiC fiber and nickel matrix could be prevented.Magnetron sputtering is used to deposit Ni coating on the surface of the(Al+Al2O3)-coated SiC fiber in preparation of the precursor wires.It is shown that the deposited Ni coating combines well with the(Al+Al2O3) coating and has little negative effect on the tensile strength of(Al+Al2O3)-coated SiC fiber.Solid-state diffusion bonding process is employed to prepare the(Al+Al2O3)-coated SiC fiber reinforced nickel matrix with 37% fibers in volume.The solid-state diffusion bonding process is optimized and the optimum parameters are temperature of 870,pressure of 50 MPa and holding time of 2 h.Under this condition,the precursor wires can diffuse well,composite of full density can be formed and the(Al+Al2O3) coating is effective to restrict the reaction between SiC fiber and nickel matrix.

  10. Matrix cracking of fiber-reinforced ceramic composites in shear

    Science.gov (United States)

    Rajan, Varun P.; Zok, Frank W.

    2014-12-01

    The mechanics of cracking in fiber-reinforced ceramic matrix composites (CMCs) under general loadings remains incomplete. The present paper addresses one outstanding aspect of this problem: the development of matrix cracks in unidirectional plies under shear loading. To this end, we develop a model based on potential energy differences upstream and downstream of a fully bridged steady-state matrix crack. Through a combination of analytical solutions and finite element simulations of the constituent stresses before and after cracking, we identify the dominant stress components that drive crack growth. We show that, when the axial slip lengths are much larger than the fiber diameter and when interfacial slip precedes cracking, the shear stresses in the constituents are largely unaffected by the presence of the crack; the changes that do occur are confined to a 'core' region within a distance of about one fiber diameter from the crack plane. Instead, the driving force for crack growth derives mainly from the axial stresses-tensile in the fibers and compressive in the matrix-that arise upon cracking. These stresses are well-approximated by solutions based on shear-lag analysis. Combining these solutions with the governing equation for crack growth yields an analytical estimate of the critical shear stress for matrix cracking. An analogous approach is used in deriving the critical stresses needed for matrix cracking under arbitrary in-plane loadings. The applicability of these results to cross-ply CMC laminates is briefly discussed.

  11. Investigation on the Effects of Titanium Diboride Particle Size on Radiation Shielding Properties of Titanium Diboride Reinforced Boron Carbide-Silicon Carbide Composites

    Directory of Open Access Journals (Sweden)

    A.O. Addemir

    2012-03-01

    Full Text Available Composite materials have wide application areas in industry. Boron Carbide is an important material for nuclear technology. Silicon carbide is a candidate material in the first wall and blankets of fusion power plants. Titanium diboride reinforced boron carbide-silicon carbide composites which were produced from different titanium diboride particle sizes and ratios were studied for searching of the behaviour against the gamma ray. Cs-137 gamma radioisotope was used as gamma source in the experiments which has a single gamma-peak at 0.662 MeV. Gamma transmission technique was used for the measurements. The effects of titanium diboride particle size on radiation attenuation of titanium diboride reinforced boron carbide-silicon carbide composites were evaluated in related with gamma transmission and the results of the experiments were interpreted and compared with each other. Composite materials have wide application areas in industry. Boron Carbide is an important material for nuclear technology. Silicon carbide is a candidate material in the first wall and blankets of fusion power plants. Titanium diboride reinforced boron carbide-silicon carbide composites which were produced from different titanium diboride particle sizes and ratios were studied for searching of the behaviour against the gamma ray. Cs-137 gamma radioisotope was used as gamma source in the experiments which has a single gamma-peak at 0.662 MeV. Gamma transmission technique was used for the measurements. The effects of titanium diboride particle size on radiation attenuation of titanium diboride reinforced boron carbide-silicon carbide composites were evaluated in related with gamma transmission and the results of the experiments were interpreted and compared with each other. Composite materials have wide application areas in industry. Boron Carbide is an important material for nuclear technology. Silicon carbide is a candidate material in the first wall and blankets of fusion

  12. Titanium implants induce expression of matrix metalloproteinases in bone during osseointegration

    National Research Council Canada - National Science Library

    Shubayev, Veronica I; Brånemark, Rickard; Steinauer, Joanne; Myers, Robert R

    2004-01-01

    ...) bond at the titanium-bone interface. In this study, we used a rodent femur model of intramedullary osseointegration to analyze the changes in immunoreactivity of ECM-controlling matrix metalloproteinases (MMPs...

  13. Bending Mechanical Behavior of Polyester Matrix Reinforced with Fique Fiber

    Science.gov (United States)

    Altoé, Giulio Rodrigues; Netto, Pedro Amoy; Barcelos, Mariana; Gomes, André; Margem, Frederico Muylaert; Monteiro, Sergio Neves

    Environmentally correct composites, made from natural fibers, are among the most investigated and applied today. In this paper, we investigate the mechanical behavior of polyester matrix composites reinforced with continuous fique fibers, through bending tensile tests. Specimens containing 0, 10, 20 and 30% in volume of fique fiber were aligned along the entire length of a mold to create plates of these composites, those plates were cut following the ASTM standard to obtained bending tests specimens. The test was conducted in a Instron Machine and the fractured specimens were analyzed by SEM, the results showed the increase in the materials tensile properties with the increase of fiber amount.

  14. A Unified Model for the Prediction of Yield Strength in Particulate-Reinforced Metal Matrix Nanocomposites

    Directory of Open Access Journals (Sweden)

    F. A. Mirza

    2015-08-01

    Full Text Available Lightweighting in the transportation industry is today recognized as one of the most important strategies to improve fuel efficiency and reduce anthropogenic climate-changing, environment-damaging, and human death-causing emissions. However, the structural applications of lightweight alloys are often limited by some inherent deficiencies such as low stiffness, high wear rate and inferior strength. These properties could be effectively enhanced by the addition of stronger and stiffer reinforcements, especially nano-sized particles, into metal matrix to form composites. In most cases three common strengthening mechanisms (load-bearing effect, mismatch of coefficients of thermal expansion, and Orowan strengthening have been considered to predict the yield strength of metal matrix nanocomposites (MMNCs. This study was aimed at developing a unified model by taking into account the matrix grain size and porosity (which is unavoidable in the materials processing such as casting and powder metallurgy in the prediction of the yield strength of MMNCs. The Zener pinning effect of grain boundaries by the nano-sized particles has also been integrated. The model was validated using the experimental data of magnesium- and titanium-based nanocomposites containing different types of nano-sized particles (namely, Al2O3, Y2O3, and carbon nanotubes. The predicted results were observed to be in good agreement with the experimental data reported in the literature.

  15. Investigation on the Effects of Titanium Diboride Particle Size on Radiation Shielding Properties of Titanium Diboride Reinforced Boron Carbide-Silicon Carbide Composites

    OpenAIRE

    A.O. Addemir; A.C. Akarsu; A.B. Tugrul; B. Buyuk

    2012-01-01

    Composite materials have wide application areas in industry. Boron Carbide is an important material for nuclear technology. Silicon carbide is a candidate material in the first wall and blankets of fusion power plants. Titanium diboride reinforced boron carbide-silicon carbide composites which were produced from different titanium diboride particle sizes and ratios were studied for searching of the behaviour against the gamma ray. Cs-137 gamma radioisotope was used as gamma source in the expe...

  16. Separation of matrix alloy and reinforcement from aluminum metal matrix composites scrap by salt flux addition

    Indian Academy of Sciences (India)

    K R Ravi; R M Pillai; B C Pai; M Chakraborty

    2007-08-01

    Separation of matrix alloy and reinforcements from pure Al–SiCp composite scrap by salt flux addition has been theoretically predicted using interface free energies. Experiments performed confirm the theoretical prediction. Complete separation of matrix aluminum and reinforcement from metal matrix composites (MMCs) scrap has been achieved by addition of 2.05 wt% of equimolar mixture of NaCl–KCl salt flux with a metal and particle yield of 84 and 50%, respectively. By adding 5 wt% of NaF to equimolar mixture of NaCl–KCl, metal and particle yield improved to 91 and 73%, respectively. Reusability of both the matrix aluminum and the SiC separated from Al–SiCp scraps has been analysed using XRD, SEM and DTA techniques. The matrix alloy separated from Al–SiCp scraps can be used possibly as a low Si content Al–Si alloy. However, the interfacial reaction that occurred during the fabrication of the composites had degraded the SiC particles.

  17. Machinability of titanium metal matrix composites (Ti-MMCs)

    Science.gov (United States)

    Aramesh, Maryam

    Titanium metal matrix composites (Ti-MMCs), as a new generation of materials, have various potential applications in aerospace and automotive industries. The presence of ceramic particles enhances the physical and mechanical properties of the alloy matrix. However, the hard and abrasive nature of these particles causes various issues in the field of their machinability. Severe tool wear and short tool life are the most important drawbacks of machining this class of materials. There is very limited work in the literature regarding the machinability of this class of materials especially in the area of tool life estimation and tool wear. By far, polycrystalline diamond (PCD) tools appear to be the best choice for machining MMCs from researchers' point of view. However, due to their high cost, economical alternatives are sought. Cubic boron nitride (CBN) inserts, as the second hardest available tools, show superior characteristics such as great wear resistance, high hardness at elevated temperatures, a low coefficient of friction and a high melting point. Yet, so far CBN tools have not been studied during machining of Ti-MMCs. In this study, a comprehensive study has been performed to explore the tool wear mechanisms of CBN inserts during turning of Ti-MMCs. The unique morphology of the worn faces of the tools was investigated for the first time, which led to new insights in the identification of chemical wear mechanisms during machining of Ti-MMCs. Utilizing the full tool life capacity of cutting tools is also very crucial, due to the considerable costs associated with suboptimal replacement of tools. This strongly motivates development of a reliable model for tool life estimation under any cutting conditions. In this study, a novel model based on the survival analysis methodology is developed to estimate the progressive states of tool wear under any cutting conditions during machining of Ti-MMCs. This statistical model takes into account the machining time in

  18. Grinding behavior and surface appearance of (TiCp+TiBw)/Ti-6Al-4V titanium matrix composites

    Institute of Scientific and Technical Information of China (English)

    Ding Wenfeng; Zhao Biao; Xu Jiuhua; Yang Changyong; Fu Yucan; Su Honghua

    2014-01-01

    (TiCp+TiBw)/Ti-6Al-4V titanium matrix composites (PTMCs) have broad application prospects in the aviation and nuclear field. However, it is a typical difficult-to-cut material due to high hardness of the reinforcements, high strength and low thermal conductivity of Ti-6Al-4V alloy matrix. Grinding experiments with vitrified CBN wheels were conducted to analyze comparatively the grinding performance of PTMCs and Ti-6Al-4V alloy. Grinding force and force ratios, specific grinding energy, grinding temperature, surface roughness, ground surface appearance were dis-cussed. The results show that the normal grinding force and the force ratios of PTMCs are much larger than that of Ti-6Al-4V alloy. Low depth of cut and high workpiece speed are generally ben-eficial to achieve the precision ground surface for PTMCs. The hard reinforcements of PTMCs are mainly removed in the ductile mode during grinding. However, the removal phenomenon of the reinforcements due to brittle fracture still exists, which contributes to the lower specific grinding energy and grinding temperature of PTMCs than Ti-6Al-4V alloy.

  19. Flexural analysis of palm fiber reinforced hybrid polymer matrix composite

    Science.gov (United States)

    Venkatachalam, G.; Gautham Shankar, A.; Raghav, Dasarath; Santhosh Kiran, R.; Mahesh, Bhargav; Kumar, Krishna

    2015-07-01

    Uncertainty in availability of fossil fuels in the future and global warming increased the need for more environment friendly materials. In this work, an attempt is made to fabricate a hybrid polymer matrix composite. The blend is a mixture of General Purpose Resin and Cashew Nut Shell Liquid, a natural resin extracted from cashew plant. Palm fiber, which has high strength, is used as reinforcement material. The fiber is treated with alkali (NaOH) solution to increase its strength and adhesiveness. Parametric study of flexure strength is carried out by varying alkali concentration, duration of alkali treatment and fiber volume. Taguchi L9 Orthogonal array is followed in the design of experiments procedure for simplification. With the help of ANOVA technique, regression equations are obtained which gives the level of influence of each parameter on the flexure strength of the composite.

  20. Modeling oxidation damage of continuous fiber reinforced ceramic matrix composites

    Institute of Scientific and Technical Information of China (English)

    Cheng-Peng Yang; Gui-Qiong Jiao; Bo Wang

    2011-01-01

    For fiber reinforced ceramic matrix composites (CMCs), oxidation of the constituents is a very important damage type for high temperature applications. During the oxidizing process, the pyrolytic carbon interphase gradually recesses from the crack site in the axial direction of the fiber into the interior of the material. Carbon fiber usually presents notch-like or local neck-shrink oxidation phenomenon, causing strength degradation. But, the reason for SiC fiber degradation is the flaw growth mechanism on its surface. A micromechanical model based on the above mechanisms was established to simulate the mechanical properties of CMCs after high temperature oxidation. The statistic and shearlag theory were applied and the calculation expressions for retained tensile modulus and strength were deduced, respectively. Meanwhile, the interphase recession and fiber strength degradation were considered. And then, the model was validated by application to a C/SiC composite.

  1. Optimization of Al Matrix Reinforced with B4C Particles

    Science.gov (United States)

    Shabani, Mohsen Ostad; Mazahery, Ali

    2013-02-01

    In the current study, abrasive wear resistance and mechanical properties of A356 composite reinforced with B4C particulates were investigated. A center particle swarm optimization algorithm (CenterPSO) is proposed to predict the optimal process conditions in fabrication of aluminum matrix composites. Unlike other ordinary particles, the center particle has no explicit velocity and is set to the center of the swarm at every iteration. Other aspects of the center particle are the same as that of the ordinary particle, such as fitness evaluation and competition for the best particle of the swarm. Because the center of the swarm is a promising position, the center particle generally gets good fitness value. More importantly, due to frequent appearance as the best particle of swarm, it often attracts other particles and guides the search direction of the whole swarm.

  2. Creep Forming of Carbon-Reinforced Ceramic-Matrix Composites

    Science.gov (United States)

    Vaughn, Wallace L.; Scotti, Stephan J.; Ashe, Melissa P.; Connolly, Liz

    2007-01-01

    A set of lecture slides describes an investigation of creep forming as a means of imparting desired curvatures to initially flat stock plates of carbon-reinforced ceramic-matrix composite (C-CMC) materials. The investigation is apparently part of a continuing effort to develop improved means of applying small CCMC repair patches to reinforced carbon-carbon leading edges of aerospace vehicles (e.g., space shuttles) prior to re-entry into the atmosphere of the Earth. According to one of the slides, creep forming would be an intermediate step in a process that would yield a fully densified, finished C-CMC part having a desired size and shape (the other steps would include preliminary machining, finish machining, densification by chemical vapor infiltration, and final coating). The investigation included experiments in which C-CMC disks were creep-formed by heating them to unspecified high temperatures for time intervals of the order of 1 hour while they were clamped into single- and double-curvature graphite molds. The creep-formed disks were coated with an oxidation- protection material, then subjected to arc-jet tests, in which the disks exhibited no deterioration after exposure to high-temperature test conditions lasting 490 seconds.

  3. Tribological Properties of PVD Carbon-Copper Composite Films Reinforced by Titanium

    Directory of Open Access Journals (Sweden)

    Lungevics J.

    2016-02-01

    Full Text Available Carbon-copper composite coatings reinforced with titanium were deposited using high power magnetron sputtering technique. Tribological and metrological tests were performed using Taylor Hobson Talysurf Intra 50 measuring equipment and CSM Instruments ball-on-disk type tribometer. Friction coefficient and wear rate were determined at 2N, 4N, 6N loads. It was revealed that friction coefficient decreased at a higher Ti concentration, which was particularly expressed at bigger applied loads. However, wear volume values tended to increase in the beginning, till Ti concentration reached about 11 %, but then decreased, thus providing better nanocoating wear resistance.

  4. Microstructure of a cement matrix composite reinforced with polypropylene fibers

    Directory of Open Access Journals (Sweden)

    Rincón, J. M.

    2004-06-01

    Full Text Available The present investigation deals with the microstructural characterization of a composite material, which is comprised of polypropylene fibers in an cement matrix, by means of environmental scanning electron microscopy (ESEM and field emission scanning electron microscopy (FESEM. The microstructure of the different phases that compose the matrix is very heterogeneous, though there is a uniform distribution of the fibers inside it. The surface of this composite is different after setting, cured and hardening depending if the zone is or not in touch with the walls of the mould. The interface between the different crystalline regions of the cement matrix and the dispersed fibers shows compatibility between the matrix and the polymeric fibers. The mechanical properties (compression and bending strength have also been evaluated. The use of melamine formaldehyde as additive leads to a reinforcement of the cement matrix and to the improvement of the mechanical properties.

    Se ha llevado a cabo una observacíón microestructural detallada de un material compuesto de fibras de polipropileno embebidas en una matriz de cemento usando los nuevos tipos de microscopía electrónica de barrido, tales como: un microscopio electrónico medioambiental (acrónimo en inglés: ESEM y uno de emisión de campo (acrónimo en inglés: FESEM. La microestructura de las diferentes fases que componen la matriz es muy heterogénea, aunque hay una distribución uniforme de las fibras dentro de ellas. La superficie de este material compuesto es diferente después del fraguado, curado y endurecimiento según qué zonas estén o no en contacto con las paredes del molde. La interfase entre las diferentes fases cristalinas de la matriz de cemento y las fibras dispersadas se ha observado a diferentes aumentos, comprobándose compatibilidad entre la matriz y las fibras poliméricas. Las propiedades de resistencia mecánica (tanto a flexión como a compresión han sido tambi

  5. ASTM and VAMAS activities in titanium matrix composites test methods development

    Science.gov (United States)

    Johnson, W. S.; Harmon, D. M.; Bartolotta, P. A.; Russ, S. M.

    1994-01-01

    Titanium matrix composites (TMC's) are being considered for a number of aerospace applications ranging from high performance engine components to airframe structures in areas that require high stiffness to weight ratios at temperatures up to 400 C. TMC's exhibit unique mechanical behavior due to fiber-matrix interface failures, matrix cracks bridged by fibers, thermo-viscoplastic behavior of the matrix at elevated temperatures, and the development of significant thermal residual stresses in the composite due to fabrication. Standard testing methodology must be developed to reflect the uniqueness of this type of material systems. The purpose of this paper is to review the current activities in ASTM and Versailles Project on Advanced Materials and Standards (VAMAS) that are directed toward the development of standard test methodology for titanium matrix composites.

  6. Bisphenyl-Polymer/Carbon-Fiber-Reinforced Composite Compared to Titanium Alloy Bone Implant

    Directory of Open Access Journals (Sweden)

    Richard C. Petersen

    2011-01-01

    Full Text Available Aerospace/aeronautical thermoset bisphenyl-polymer/carbon-fiber-reinforced composites are considered as new advanced materials to replace metal bone implants. In addition to well-recognized nonpolar chemistry with related bisphenol-polymer estrogenic factors, carbon-fiber-reinforced composites can offer densities and electrical conductivity/resistivity properties close to bone with strengths much higher than metals on a per-weight basis. In vivo bone-marrow tests with Sprague-Dawley rats revealed far-reaching significant osseoconductivity increases from bisphenyl-polymer/carbon-fiber composites when compared to state-of-the-art titanium-6-4 alloy controls. Midtibial percent bone area measured from the implant surface increased when comparing the titanium alloy to the polymer composite from 10.5% to 41.6% at 0.8 mm, P<10−4, and 19.3% to 77.7% at 0.1 mm, P<10−8. Carbon-fiber fragments planned to occur in the test designs, instead of producing an inflammation, stimulated bone formation and increased bone integration to the implant. In addition, low-thermal polymer processing allows incorporation of minerals and pharmaceuticals for future major tissue-engineering potential.

  7. Mechanical behavior of Fiber Reinforced SiC/RBSN Ceramic Matrix Composites: Theory and Experiment

    Science.gov (United States)

    1991-01-01

    AD-A235 926 NASA AVSCOM Technical Memorandum 103688 Technical Report 91-C-004 Mechanical Behavior of Fiber Reinforced SiC/RBSN Ceramic Matrix Composites : Theory... CERAMIC MATRIX COMPOSITES : THEORY AND EXPERIMENT Abhisak Chulya* Department of Civil Engineering Cleveland State University Cleveland, Ohio 44115...tough and sufficiently stable continuous fiber- reinforced ceramic matrix composites (CMC) which can survive in oxidizing environ- ments at temperatures

  8. Processing of pure titanium containing titanium-based reinforcing ceramics additives using spark plasma sintering

    Directory of Open Access Journals (Sweden)

    Mondiu Olayinka DUROWOJU

    2017-06-01

    Full Text Available The densification behaviour, microstructural changes and hardness characteristics during spark plasma sintering of CP-Ti reinforced with TiC, TiN, TiCN and TiB2 were investigated. Commercially pure Ti powders were dry mixed with varied amounts (2.5 and 5 wt. % of the ceramic additives using a T2F Turbula mixer for 5 h and at a speed of 49 rpm. The blended composite powders were then sintered using spark plasma sintering system (model HHPD-25 from FCT Germany at a heating rate of 100oC min-1, dwell time of 5 min and sintering temperature of 950ºC. The sintering of CP-Ti was used as a base study to select the proper spark plasma sintering temperature for full density. Densification was monitored through analysis of the recorded punch displacement and the measured density of the sintered samples using Archimedes method. High densities ranging from 97.8% for 5% TiB2 addition to 99.6% for 5% TiCN addition were achieved at a relatively low temperature of 950°C. Microstructural analyses show a uniform distribution of the additives and finer structure showing their inhibitive effect on grain growth. An improved hardness was observed in all the cases with highest values obtained with TiCN as a result of the combined effect of TiC and TiN. A change in the fracture mode from trans granular to intergranular was also observed.

  9. Microstructure and formation mechanism of titanium matrix composites coating on Ti-6Al-4V by laser cladding

    Institute of Scientific and Technical Information of China (English)

    CAI Lifang; ZHANG Yongzhong; SHI Likai

    2007-01-01

    Laser cladding experiments were done on a 5-kW continuous wave CO2 laser to synthesize TiC and TiB reinforced titanium matrix composite coatings on Ti-6Al-4V alloy with a mixture of Ti and B4C precursor powder. The thermodynamics of the reactions were calculated and analyzed. The microstructure and phase evolution of TiB and TiC composites were investigated. The results showed that the chemical reaction between Ti and B4C would release much heat, and these compounds, TiC, TiB, and small amount of TiB2, can be formed on the surface of Ti-6Al-4V alloy if the supplied energy is sufficient to excite the reaction among the initial products. A good metallurgical bond between the coating and the substrate can be achieved. The microhardness of coating was irregular and the maximum value was approximately HV600.

  10. Wear Performance of A356 Matrix Composites Reinforced with Different Types of Reinforcing Particles

    Science.gov (United States)

    Akbari, Mostafa; Shojaeefard, Mohammad Hasan; Asadi, Parviz; Khalkhali, Abolfazl

    2017-09-01

    To improve the wear resistance of Al-Si alloys, different types of reinforcing particles such as SiC, TiC, ZrO2, and B4C were used to produce matrix composites by friction stir processing (FSP). First, microstructural properties of different locations of stir zone (SZ) in the FSPed specimens such as advancing side, retreating side, shoulder-affected area, and pin-affected area were investigated. The results demonstrate that Si particles size is not the same in different SZ subdomains. SEM investigation was performed in order to investigate the particles distribution in different areas of the SZ as well as bonding quality between particles and metal matrix. Hardness and wear tests were carried out to determine mechanical and wear properties of the composites. The pin-on-disk wear tests were performed at room temperature, with the normal applied loads of 5, 10, and 20 N and sliding speed of 1 and 2 m/s. All fabricated composites show higher resistance in wear than A356 alloy. Wear test results show, by increasing the normal load and sliding velocity, the wear loss weight of all composites increased gradually.

  11. Titanium implants induce expression of matrix metalloproteinases in bone during osseointegration.

    Science.gov (United States)

    Shubayev, Veronica I; Brånemark, Rickard; Steinauer, Joanne; Myers, Robert R

    2004-01-01

    Implanted pure titanium fixtures are able to completely integrate with bone, in part because of the formation of a strong extracellular matrix (ECM) bond at the titanium-bone interface. In this study, we used a rodent femur model of intramedullary osseointegration to analyze the changes in immunoreactivity of ECM-controlling matrix metalloproteinases (MMPs), tissue inhibitor of metalloproteinase-3 (TIMP-3), and tumor necrosis factor alpha (TNF-alpha) during osseointegration. We observed dramatic increases in MMP-2, MMP-9, MMP-7, TIMP-3, and TNF-alpha in osteocytes, osteoclasts, haversian canals, and the interface matrix in bone ipsilateral to the titanium implant. An increase in TIMP-3, MMP-9, and MMP-7 in hypertrophied chondrocytes and the vascular component of the epiphysial growth plate was also observed in experimental bone. These findings were not seen in contralateral or sham-operated bone, where the titanium fixtures were threaded into the femur and immediately removed. Our data link titanium-induced bone remodeling to changes in expression and distribution of MMPs.

  12. A review on the cords & plies reinforcement of elastomeric polymer matrix

    Science.gov (United States)

    Mahmood, S. S.; Husin, H.; Mat-Shayuti, M. S.; Hassan, Z.

    2016-06-01

    Steel, polyester, nylon and rayon are the main materials of cords & plies that have been reinforced in the natural rubber to produce quality tyres but there is few research reported on cord and plies reinforcement in silicone rubber. Taking the innovation of tyres as inspiration, this review's first objective is to compile the comprehensive studies about the cords & plies reinforcement in elastomeric polymer matrix. The second objective is to gather information about silicone rubber that has a high potential as a matrix phase for cords and plies reinforcement. All the tests and findings are gathered and compiled in sections namely processing preparation, curing, physical and mechanical properties, and adhesion between cords-polymer.

  13. On the Mechanical Properties of Hybrid Aluminium 7075 Matrix Composite Material Reinforced with SiC and TiC Produced by Powder Metallurgy Method

    Directory of Open Access Journals (Sweden)

    S. Pradeep Devaneyan

    2017-01-01

    Full Text Available Metal matrix composites are widely used in components of various components of industrial equipment because of their superior material properties like high stiffness to weight ratio and high impact strength and fracture toughness while compared to the conventional material. Due to the concepts of high strength to low weight ratio, Al 7075 was extensively applied in aircraft engine and wings. Even if Al 7075 has higher hardness, higher strength, excellent wear resistance, and high-temperature corrosion protection, it is in need of further enhancement of properties for increasing its applicability. This paper presents the mechanical behavior of aluminium 7075 reinforced with Silicon Carbide (SiC and Titanium Carbide (TiC through powder metallurgy route. These specimens were produced by powder metallurgy method. The hybrid composite was made by Al 7075 alloy as the matrix with Silicon Carbide and Titanium Carbide as reinforcement. Silicon Carbide and Titanium Carbide are mixed in different weight ratio based on the design matrix formulated through a statistical tool, namely, Response Surface Methodology (RSM. Enhanced mechanical properties have been obtained with 90% of Al 7075, 4% of TiC, and 8% of SiC composition in the composite. Coefficient of friction appears to be more which has been determined by ring compression test.

  14. Residual stress measurements in an SiC continuous fiber reinforced Ti matrix composite

    NARCIS (Netherlands)

    Willemse, P.F.; Mulder, F.M.; Wei, W.; Rekveldt, M.Th.; Knight, K.S.

    2000-01-01

    During the fabrication of ceramic fiber reinforced metal matrix composites mismatch stresses will be introduced due to differences in thermal expansion coefficients between the matrix and the fibers. Calculations, based on a coaxial cylinder model, [1 and 2] predict that, for a Ti matrix SiC

  15. Microstructure and mechanical behavior of metallic glass fiber-reinforced Al alloy matrix composites.

    Science.gov (United States)

    Wang, Z; Georgarakis, K; Nakayama, K S; Li, Y; Tsarkov, A A; Xie, G; Dudina, D; Louzguine-Luzgin, D V; Yavari, A R

    2016-04-12

    Metallic glass-reinforced metal matrix composites are an emerging class of composite materials. The metallic nature and the high mechanical strength of the reinforcing phase offers unique possibilities for improving the engineering performance of composites. Understanding the structure at the amorphous/crystalline interfaces and the deformation behavior of these composites is of vital importance for their further development and potential application. In the present work, Zr-based metallic glass fibers have been introduced in Al7075 alloy (Al-Zn-Mg-Cu) matrices using spark plasma sintering (SPS) producing composites with low porosity. The addition of metallic glass reinforcements in the Al-based matrix significantly improves the mechanical behavior of the composites in compression. High-resolution TEM observations at the interface reveal the formation of a thin interdiffusion layer able to provide good bonding between the reinforcing phase and the Al-based matrix. The deformation behavior of the composites was studied, indicating that local plastic deformation occurred in the matrix near the glassy reinforcements followed by the initiation and propagation of cracks mainly through the matrix. The reinforcing phase is seen to inhibit the plastic deformation and retard the crack propagation. The findings offer new insights into the mechanical behavior of metal matrix composites reinforced with metallic glasses.

  16. Titanium Matrix Composite Ti/TiN Produced by Diode Laser Gas Nitriding

    Directory of Open Access Journals (Sweden)

    Aleksander Lisiecki

    2015-01-01

    Full Text Available A high power direct diode laser, emitting in the range of near infrared radiation at wavelength 808–940 nm, was applied to produce a titanium matrix composite on a surface layer of titanium alloy Ti6Al4V by laser surface gas nitriding. The nitrided surface layers were produced as single stringer beads at different heat inputs, different scanning speeds, and different powers of laser beam. The influence of laser nitriding parameters on the quality, shape, and morphology of the surface layers was investigated. It was found that the nitrided surface layers consist of titanium nitride precipitations mainly in the form of dendrites embedded in the titanium alloy matrix. The titanium nitrides are produced as a result of the reaction between molten Ti and gaseous nitrogen. Solidification and subsequent growth of the TiN dendrites takes place to a large extent at the interface of the molten Ti and the nitrogen gas atmosphere. The direction of TiN dendrites growth is perpendicular to the surface of molten Ti. The roughness of the surface layers depends strongly on the heat input of laser nitriding and can be precisely controlled. In spite of high microhardness up to 2400 HV0.2, the surface layers are crack free.

  17. Biocompatibility of pure titanium modified by human endothelial cell-derived extracellular matrix

    Energy Technology Data Exchange (ETDEWEB)

    Xue Xiaoqing [Key Laboratory of Advanced Technology for Materials of Education Ministry, Southwest Jiaotong University, Chengdu 610031 (China); Wang Jin, E-mail: jinxxwang@263.net [Key Laboratory of Advanced Technology for Materials of Education Ministry, Southwest Jiaotong University, Chengdu 610031 (China); Zhu Ying; Tu Qiufen; Huang Nan [Key Laboratory of Advanced Technology for Materials of Education Ministry, Southwest Jiaotong University, Chengdu 610031 (China)

    2010-04-01

    Extracellular matrix (ECM) used to modify biomaterial surface is a promising method for improving cardiovascular material hemocompatibility. In the present work, human umbilical vein endothelial cells (HUVECs) are cultured and native ECM is obtained on pure titanium surface. Fourier infrared spectrum (FTIR) test proves the existence of amide I and amide II band on the modified titanium surface. X-ray photoelectron spectroscopy (XPS) further confirms the chemical composition and binding types of the ECM proteins on the titanium substrate. The results of light microscopy and atomic force microscopy (AFM) exhibit the morphology of HUVEC derived ECM. There are higher water contact angles on the ECM modified samples. Furthermore, some ECM components, including fibronectin (FN), laminin (LN) and type IV collagen (IV-COL) are presented on ECM-covered titanium surface by immunofluorescence staining. The biological behavior of cultured HUVECs and adherent platelets on different samples are investigated by in vitro HUVECs culture and platelet adhesion. Cells exhibit better morphology and their proliferation ability greatly improve on the ECM-covered titanium. At the same time, the platelet adhesion and spreading are inhibited on ECM-covered titanium surface. These investigations demonstrate that ECM produced by HUVECs cannot only improve adhesion and proliferation ability of endothelial cell but also inhibit adhesion and activation of platelets. Thus, the approach described here may provide a basis for preparation of modified surface in cardiovascular implants application.

  18. Adherence of extracellular matrix components to modified surfaces of titanium alloys

    Science.gov (United States)

    Stelzer, C.; Uhlmann, E.; Meinke, M.; Lademann, J.; Hansen, U.

    2009-04-01

    The adherence of biological materials on metal surfaces is of special importance in biology and medicine. The underlying interactions between surface and biological materials (e.g. extracellular matrix components or cells) are responsible for the application as a medical device. Numerous products are made of pure titanium and titanium alloys. This paper shows the influence of a laser production technology on machined surfaces of TiAl6V4 and the resulting adherence of biological material on the basis of the surface characterisation. In this study, different machined TiAl6V4 surfaces were used for coatings with extracellular matrix components. For this process, different coating with collagen I monomers and a complex mixture of extracellular matrix proteins derived from the dermal-epidermal basement membrane zone were analysed. The efficiency of the coating was analysed by different methods and the results are presented in this paper.

  19. Microstructure characterization of laser-deposited titanium carbide and zirconium-based titanium metal matrix composites

    CSIR Research Space (South Africa)

    Ochonogor, OF

    2012-09-01

    Full Text Available produced with 10, 20, and 30 vol.% reinforcing ceramic, and Zr + TiC MMCs were fabricated with 10, 20, and 30 vol.% TiC. The deposited thin walls were analysed using optical microscopy, scanning electron microscopy (SEM) with energy dispersive spectroscopy...

  20. The mechanical behavior dependence on the TiB whisker realignment during hot-working in titanium matrix composites

    Science.gov (United States)

    Ma, Fengcang; Liu, Ping; Li, Wei; Liu, Xinkuan; Chen, Xiaohong; Zhang, Ke; Pan, Deng; Lu, Weijie

    2016-10-01

    Low-cost TiB whiskers reinforced titanium matrix composite (TMCs) was fabricated with enhanced mechanical performances using in situ technologies and hot working. Morphologies observation indicates that needle-like TiB whiskers with a hexagonal transverse section grow along the [010] direction due to B27 crystal structure and its growth mechanism. Mechanical properties tests show that the mechanical behavior of the TiB whiskers reinforced TMCs is dependent on the deformation amplitudes applied in hot-working. The improvement in yield strength by hot-working is attributed to the TiB whiskers realignment and the refinement of microstructure. Models are constructed to evaluate the realignment of TiB whisker during deformation and the increase in yield strength of the composite at elevated temperatures. These models clarify the alignment effect of TiB whiskers under various deformation amplitudes applied in hot-workings and reveals the yield strength dependence on TiB whiskers orientation.

  1. Titanium dioxide anatase as matrix for matrix-assisted laser desorption/ionization analysis of small molecules.

    Science.gov (United States)

    Castro, Ana L; Madeira, Paulo J Amorim; Nunes, Manuel R; Costa, Fernanda M; Florêncio, M Helena

    2008-12-01

    The use of inorganic species as assisting materials in matrix-assisted laser desorption/ionization (MALDI) analysis is an alternative approach to avoid interfering matrix ions in the low-mass region of the mass spectra. Reports of the application of inorganic species as matrices in MALDI analysis of small molecules are, however, scarce. Nevertheless, titanium dioxide (TiO(2)) powder has been reported to be a promising matrix medium. In this study we further explore the use of TiO(2) as a matrix for the MALDI analysis of low molecular weight compounds. We present results showing that nanosized TiO(2) anatase and TiO(2) rutile perform better as MALDI matrices than a commercial TiO(2) anatase/rutile mixture. Moreover, when using nanosized TiO(2) anatase as a matrix, high-quality mass spectra can be obtained with strong analyte signals and weak or non-existing matrix interference ions. Furthermore, our results show that the phase type plays an important role in the application of TiO(2) as a MALDI matrix.

  2. A Micro Raman Investigation of Viscoelasticity in Short Fibre Reinforced Polymer Matrix Composites

    DEFF Research Database (Denmark)

    Schjødt-Thomsen, Jan

    The purpose of the present Ph.D. project is to investigate the load transfer mechanisms between the fibre and matrix and the stress/strain fields in and around single fibres in short fibre reinforced viscoelastic polymer matrix composites subjected to various loading histories. The materials...

  3. Fracture Toughness of Carbon Nanotube-Reinforced Metal- and Ceramic-Matrix Composites

    Directory of Open Access Journals (Sweden)

    Y. L. Chen

    2011-01-01

    Full Text Available Hierarchical analysis of the fracture toughness enhancement of carbon nanotube- (CNT- reinforced hard matrix composites is carried out on the basis of shear-lag theory and facture mechanics. It is found that stronger CNT/matrix interfaces cannot definitely lead to the better fracture toughness of these composites, and the optimal interfacial chemical bond density is that making the failure mode just in the transition from CNT pull-out to CNT break. For hard matrix composites, the fracture toughness of composites with weak interfaces can be improved effectively by increasing the CNT length. However, for soft matrix composite, the fracture toughness improvement due to the reinforcing CNTs quickly becomes saturated with an increase in CNT length. The proposed theoretical model is also applicable to short fiber-reinforced composites.

  4. A new method of making metal matrix fibre reinforced materials

    Energy Technology Data Exchange (ETDEWEB)

    Schaupp, J. (Inst. fuer Werkzeugmaschinen und Betriebstechnik, Univ. Karlsruhe (Germany)); Pruemmer, R. (Inst. fuer Werkzeugmaschinen und Betriebstechnik, Univ. Karlsruhe (Germany) Ernst-Mach-Inst., Freiburg (Germany))

    1993-11-01

    MMC (metal matrix composites) made of ceramic fibres and metal matrix are suitable for high strength and high temperature applications. New types of ceramic fibres usually are incorporated into a metal matrix by means of liquid infiltration or by hot pressing techniques. The disadvantage of these methods is the chemical reaction sometimes occurring between fibre and matrix, resulting in an interlayer which is degrading the mechanical properties of the MMC. A new method is described starting with an arrangement of metal powder or metal foils with ceramic fibres. Dynamic pressures, released by detonation of proper explosives, are used for consolidation. At very high strain rates during plastic deformation of the powder or metal foils hydrodynamic flow of the matrix around the ceramic fibres allows a complete consolidation and to prevent cracking. Fibres made of SiC are embedded into a metal matrix of aluminum. (orig.).

  5. Approach to microstructure-behavior relationships for ceramic matrix composites reinforced by continuous fibers

    Directory of Open Access Journals (Sweden)

    Lamon Jacques

    2015-01-01

    Full Text Available Ceramic matrix composites (CMCs reinforced with continuous fibers exhibit several features that differentiate them from homogeneous unreinforced materials. The microstructure consists of various distinct constituents: fibres, matrix, and fiber/matrix interfaces or interphases. Several entities at micro- and mesoscopic length scales can be defined depending on fiber arrangement. Furthermore, the CMCs contain flaw populations that govern matrix cracking and fiber failures. The paper describes the microstructure-behavior relations for ceramic matrix composites reinforced with continuous fibers. It focuses on matrix damage by multiple cracking, on ultimate fracture, on delayed fracture at high temperatures, and on stochastic features induced by flaw populations. Models of damage and ultimate failure are based on micromechanics and fracture probabilities. They provide a basis for a multiscale approach to composite and component design.

  6. Deformation behavior of SiC particle reinforced Al matrix composites based on EMA model

    Institute of Scientific and Technical Information of China (English)

    CHENG Nan-pu; ZENG Su-min; YU Wen-bin; LIU Zhi-yi; CHEN Zhi-qian

    2007-01-01

    Effects of the matrix properties, particle size distribution and interfacial matrix failure on the elastoplastic deformation behavior in Al matrix composites reinforced by SiC particles with an average size of 5 μm and volume fraction of 12% were quantitatively calculated by using the expanded effective assumption(EMA) model. The particle size distribution naturally brings about the variation of matrix properties and the interfacial matrix failure due to the presence of SiC particles. The theoretical results coincide well with those of the experiment. The current research indicates that the load transfer between matrix and reinforcements, grain refinement in matrix, and enhanced dislocation density originated from the thermal mismatch between SiC particles and Al matrix increase the flow stress of the composites, but the interfacial matrix failure is opposite. It also proves that the load transfer, grain refinement and dislocation strengthening are the main strengthening mechanisms, and the interfacial matrix failure and ductile fracture of matrix are the dominating fracture modes in the composites. The mechanical properties of the composites strongly depend on the metal matrix.

  7. Physical and Hydrodynamic Properties of Spherical Cellulose—Titanium Dioxide Composite Matrix for Expanded Bed Adsorption

    Institute of Scientific and Technical Information of China (English)

    雷引林; 林东强; 姚善泾; 刘坐镇; 朱自强

    2003-01-01

    Expanded bed adsorption (EBA) has been widely used in industrial downstream bioprocessing,Solid matrix is the principal pillar supporting the successful application of EBA.A novel spherical ceelulose-titanium dioxide composite matrix was prepared through the method of water-in-oil suspension thermal regeneration.Its typical physical properties were wet density 1.18g.cm-3,,diameters in the range of 100-300μm ,porosity 85.5%,and water content 72.3%.Expansion characteristics and liquid mixing performance of the matrix in expanded bed were investigated using water and 10% (by mass )glycerol solution as mobile phases,The results indicate that the custom-assembled matrix has a stable flow hydrodynamics and exhibits the same degree of liquid-phase mixing or column efficiency as the commercially available Streamline adsorbent.

  8. Mechanism and optimization of titanium carbide-reinforced iron composite formation through carbothermal reduction of hematite and anatase

    Energy Technology Data Exchange (ETDEWEB)

    Hasniyati, Md Razi; Zuhailawati, Hussain, E-mail: zuhaila@eng.usm.my; Ramakrishnan, Sivakumar; Hamid, Sheikh Abdul Rezan Sheikh Abdul

    2014-02-25

    Highlights: • Reduction mechanism of Fe{sub 2}O{sub 3} and TiO{sub 2} mixture in formation Fe–TiC composite was discovered. • Factorial design is used to define interaction between calcination temperature and FeCl{sub 3} content. • Increasing FeCl{sub 3} content and calcination temperature increased the formation of Fe and TiC phases. • Microhardness and density of the sintered composite improved noticeably. -- Abstract: This study investigated an optimization of titanium carbide-reinforced iron composite fabricated using a combination of powder metallurgy and carbothermal reduction of hematite-anatase mixture using 2{sup k} factorial design. The composite formation mechanism is described as well. Powders of hematite, anatase and graphite with mole ratio of 1:1:6 were mixed for 1 h together with 0 wt%, 1 wt% and 5 wt% FeCl{sub 3}. The mixture was pressed at 5 MPa, calcined for 1 h at 1000 °C, 1100 °C or 1200 °C and sintered at 1200 °C. X-ray diffraction of the calcined powder showed that with increasing temperature TiO{sub 2} was reduced to TiC through formation of various suboxides (Ti{sub 3}O{sub 5} and Ti{sub 2}O{sub 3}). Scanning electron microscope observation of the sintered composite indicated that addition of FeCl{sub 3} enhanced the formation of TiC in iron matrix. Consequently, microhardness and density of the sintered composite improved noticeably. Based on microhardness, green density and sintered density measurements, design of experiment analysis suggested that an increase in both FeCl{sub 3} content and calcination temperature increased the percentage of hematite and anatase reduction.

  9. Studies on natural fiber reinforced polymer matrix composites

    Science.gov (United States)

    Patel, R. H.; Kapatel, P. M.; Machchhar, A. D.; Kapatel, Y. A.

    2016-05-01

    Natural fiber reinforced composites show increasing importance in day to days applications because of their low cost, lightweight, easy availability, non-toxicity, biodegradability and environment friendly nature. But these fibers are hydrophilic in nature. Thus they have very low reactivity and poor compatibility with polymers. To overcome these limitations chemical modifications of the fibers have been carried out. Therefore, in the present work jute fibers have chemically modified by treating with sodium hydroxide (NaOH) solutions. These treated jute fibers have been used to fabricate jute fiber reinforced epoxy composites. Mechanical properties like tensile strength, flexural strength and impact strength have been found out. Alkali treated composites show better properties compare to untreated composites.

  10. Study the Effect of Different Reinforcements on the Damping Properties of the Polymer Matrix Composite

    Directory of Open Access Journals (Sweden)

    Mustafa Ziyara Shamukh

    2016-09-01

    Full Text Available In this research, damping properties for composite materials were evaluated using logarithmic decrement method to study the effect of reinforcements on the damping ratio of the epoxy matrix. Three stages of composites were prepared in this research. The first stage included preparing binary blends of epoxy (EP and different weight percentages of polysulfide rubber (PSR (0%, 2.5%, 5%, 7.5% and 10%. It was found that the weight percentage 5% of polysulfide was the best percentage, which gives the best mechanical properties for the blend matrix. The advantage of this blend matrix is that; it mediates between the brittle properties of epoxy and the flexible properties of a blend matrix with the highest percentage of PSR. The second stage included reinforcing the best blend matrix of epoxy-polysulfide (the blend matrix with the best percentage of polysulfide resulted from the previous stage, by different volume percentages of short fibers (Carbon& Glass separately and randomly. The volume percentages of fibers were (2.5%, 5%, 7.5%, and 10%. The third stage included reinforcing the blend composites with highest percentages of carbon and glass fiber, by different weight percentages of nano-particles (Red mud& Fly ash separately. The weight percentages of particles were (0.5%, 1%, 1.5%, and 2%. The experimental results showed that blending polysulfide rubber with epoxy increased the damping ratio. As for reinforcement materials, they decreased the damping ratio, where glass fiber composites have significantly higher damping ratio than other composites.

  11. Review on preparation techniques of particle reinforced metal matrix composites

    Institute of Scientific and Technical Information of China (English)

    2006-01-01

    This paper reviews the investigation status of the techniques for preparation of metal matrix composites and the research outcomes achieved recently. The mechanisms, characteristics, application ranges and levels of development of these preparatior techniques are analyzed. The advantages and the disadvantages of each technique are synthetically evaluated. Lastly, the future directions of research and the prospects for the preparation techniques of metal matrix composites are forecasted.

  12. Review on preparation techniques of particle reinforced metal matrix composites

    Directory of Open Access Journals (Sweden)

    HAO Bin

    2006-02-01

    Full Text Available This paper reviews the investigation status of the techniques for preparation of metal matrix composites and the research outcomes achieved recently. The mechanisms, characteristics, application ranges and levels of development of these preparation techniques are analyzed. The advantages and the disadvantages of each technique are synthetically evaluated. Lastly, the future directions of research and the prospects for the preparation techniques of metal matrix composites are forecasted.

  13. Microstructure and Mechanical Properties of Warm-Sprayed Titanium Coating on Carbon Fiber-Reinforced Plastic

    Science.gov (United States)

    Ganesan, Amirthan; Takuma, Okada; Yamada, Motohiro; Fukumoto, Masahiro

    2016-04-01

    Polymer materials are increasingly dominating various engineering fields. Recently, polymer-based composite materials' surface performances—in particular, surface in relative motion—have been improved markedly by thermal spray coating. Despite this recent progress, the deposition of high-strength materials—producing a coating thickness of the order of more than 500 μm—remains highly challenging. In the present work, a highly dense and thick titanium coating was successfully deposited onto the carbon fiber-reinforced plastic (CFRP) substrate using a newly developed high-pressure warm spray (WS) system. The coating properties, such as hardness (300 ± 20 HV) and adhesion strength (8.1 ± 0.5 MPa), were evaluated and correlated with the microstructures of the coating. In addition, a wipe-test and in situ particle velocity and temperature measurement were performed to validate the particle deposition behavior as a function of the nitrogen flow rate in the WS system. It was found that the microstructures, deposition efficiency, and mechanical properties of the coatings were highly sensitive to nitrogen flow rates. The coating porosity increased with increasing nitrogen flow rates; however, the highest density was observed for nitrogen flow rate of 1000 standard liters per minute (SLM) samples due to the high fraction of semi-molten particles in the spray stream.

  14. Processing, structure and flexural strength of CNT and carbon fibre reinforced, epoxy-matrix hybrid composite

    Indian Academy of Sciences (India)

    K Chandra Shekar; M Sai Priya; P K Subramanian; Anil Kumar; B Anjaneya Prasad; N Eswara Prasad

    2014-05-01

    Advanced materials such as continuous fibre-reinforced polymer matrix composites offer significant enhancements in variety of properties, as compared to their bulk, monolithic counterparts. These properties include primarily the tensile stress, flexural stress and fracture parameters. However, till date, there are hardly any scientific studies reported on carbon fibre (Cf) and carbon nanotube (CNT) reinforced hybrid epoxy matrix composites (unidirectional). The present work is an attempt to bring out the flexural strength properties along with a detailed investigation in the synthesis of reinforced hybrid composite. In this present study, the importance of alignment of fibre is comprehensively evaluated and reported. The results obtained are discussed in terms of material characteristics, microstructure and mode of failure under flexural (3-point bend) loading. The study reveals the material exhibiting exceptionally high strength values and declaring itself as a material with high strength to weight ratio when compared to other competing polymer matrix composites (PMCs); as a novel structural material for aeronautical and aerospace applications.

  15. Mechanical behavior and properties of fiber reinforced ceramic matrix composites for high temperature use

    Institute of Scientific and Technical Information of China (English)

    Chongdu Cho; Qiang Pan; Sangkyo Lee

    2007-01-01

    Ceramics can keep their mechanical characteristics up to 2 000℃ or higher.In this paper,A model to predict ultimate strength of continuous fiber-reinforced brittle matrix composites is developed.A statistical theory for the strength of a uni-axially fiber-reinforced brittle matrix composite is presented.Also a semi-empirical frictional heating method for estimating in-situ interfacial shear in fiber-reinforced ceramic matrix composites was improved.Local uneven fiber packing variation as well as uneven micro-damage during fatigue can be expected to have effects on the composites:generation of frictional heating,thermal gradients,and residual stresses around local fiber breaks.This study examined those engineering interests by the finite element method.

  16. Synthesis and Characterization of Multi Wall Carbon Nanotubes (MWCNT) Reinforced Sintered Magnesium Matrix Composites

    Science.gov (United States)

    Vijaya Bhaskar, S.; Rajmohan, T.; Palanikumar, K.; Bharath Ganesh Kumar, B.

    2016-04-01

    Metal matrix composites (MMCs) reinforced with ceramic nano particles (less than 100 nm), termed as metal matrix nano composites (MMNCs), can overcome those disadvantages associated with the conventional MMCs. MMCs containing carbon nanotubes are being developed and projected for diverse applications in various fields of engineering like automotive, avionic, electronic and bio-medical sectors. The present investigation deals with the synthesis and characterization of hybrid magnesium matrix reinforced with various different wt% (0-0.45) of multi wall carbon nano tubes (MWCNT) and micro SiC particles prepared through powder metallurgy route. Microstructure and mechanical properties such as micro hardness and density of the composites were examined. Microstructure of MMNCs have been investigated by scanning electron microscope, X-ray diffraction and energy dispersive X-ray spectroscopy (EDS) for better observation of dispersion of reinforcement. The results indicated that the increase in wt% of MWCNT improves the mechanical properties of the composite.

  17. Impact–abrasion wear characteristics of in-situ VC-reinforced austenitic steel matrix composite

    Energy Technology Data Exchange (ETDEWEB)

    Moghaddam, E.G., E-mail: emad_g_moghaddam@alum.sharif.edu [Department of Materials Science and Engineering, Sharif University of Technology, P.O. Box 11365-9466, Azadi Avenue, Tehran (Iran, Islamic Republic of); Karimzadeh, N. [Department of Materials Engineering, Islamic Azad University, Najafabad Branch, Isfahan (Iran, Islamic Republic of); Varahram, N.; Davami, P. [Department of Materials Science and Engineering, Sharif University of Technology, P.O. Box 11365-9466, Azadi Avenue, Tehran (Iran, Islamic Republic of)

    2013-11-15

    In this investigation, in-situ precipitation of vanadium carbides was employed to reinforce Fe–13Mn and Fe–13Mn–3W alloys by means of conventional melting and casting route. Microstructures were characterized by optical and scanning electron microscopy techniques. Mechanical properties of the materials were determined by hardness, impact toughness and tension tests. It was observed that tungsten improved the strength of the matrix and the reinforcements as well as tensile properties and work hardening rate of the VC-reinforced composite. Ball mill abrasion test was utilized to simulate impact–abrasion wear condition using two types of abrasive minerals. The results showed that the degree of benefit to be gained by the use of in-situ VC-reinforced composite materials depends strongly on crush strength of the abrasives. It was found that the studied particle-reinforced composite materials were only advantageous when the abrasives were relatively soft, providing low-stress abrasion condition.

  18. Synergistic Effects of Temperature and Oxidation on Matrix Cracking in Fiber-Reinforced Ceramic-Matrix Composites

    Science.gov (United States)

    Longbiao, Li

    2017-06-01

    In this paper, the synergistic effects of temperatrue and oxidation on matrix cracking in fiber-reinforced ceramic-matrix composites (CMCs) has been investigated using energy balance approach. The shear-lag model cooperated with damage models, i.e., the interface oxidation model, interface debonding model, fiber strength degradation model and fiber failure model, has been adopted to analyze microstress field in the composite. The relationships between matrix cracking stress, interface debonding and slipping, fiber fracture, oxidation temperatures and time have been established. The effects of fiber volume fraction, interface properties, fiber strength and oxidation temperatures on the evolution of matrix cracking stress versus oxidation time have been analyzed. The matrix cracking stresses of C/SiC composite with strong and weak interface bonding after unstressed oxidation at an elevated temperature of 700 °C in air condition have been predicted for different oxidation time.

  19. The influence of matrix composition and reinforcement type on the properties of polysialate composites

    Science.gov (United States)

    Hammell, James A.

    There is a critical need for the development of materials for eliminating fire as a cause of death in aircraft accidents. Currently available composites that use organic matrices not only deteriorate at temperatures above 300°C but also emit toxic fumes. The results presented in this dissertation focus on the development of an inorganic matrix that does not burn or emit toxic fumes. The matrix, known as polysialate, can withstand temperatures in excess of 1000°C. The matrix behaves like a ceramic, but does not need high curing temperatures, so it can be processed like many common organic matrices. The major parameters evaluated in this dissertation are: (i) Influence of reinforcement type, (ii) Matrix formulation for both wet-dry durability and high temperature resistance, (iii) Influence of processing variables such as moisture reduction and storage, (iv) Tensile strain capacity of modified matrices and matrices reinforced with ceramic microfibers and discrete carbon fibers, and (v) analytical modeling of mechanical properties. For the reinforcement type; carbon, glass, and stainless steel wire fabrics were investigated. Carbon fabrics with 1, 3, 12, and 50k tows were used. A matrix chemical formulation that can withstand wetting and drying was developed. This formulation was tested at high temperatures to ascertain its stability above 400°C. On the topic of processing, shelf life of prepregged fabric layers and efficient moisture removal methods were studied. An analytical model based on layered reinforcement was developed for analyzing flexural specimens. It is shown that the new inorganic matrix can withstand wetting and drying, and also high temperature. The layered reinforcement concept provides accurate prediction of strength and stiffness for composites reinforced with 1k and 3k tows. The prepregged fabric layers can be stored for 14 days at -15°C without losing strength.

  20. Thermo-oxidative stability studies of PMR-15 polymer matrix composites reinforced with various fibers

    Science.gov (United States)

    Bowles, Kenneth J.

    1990-01-01

    An experimental study was conducted to measure the thermo-oxidative stability of PMR-15 polymer matrix composites reinforced with various fibers and to observe differences in the way they degrade in air. The fibers that were studied included graphite and the thermally stable Nicalon and Nextel ceramic fibers. Weight loss rates for the different composites were assessed as a function of mechanical properties, specimen geometry, fiber sizing, and interfacial bond strength. Differences were observed in rates of weight loss, matrix cracking, geometry dependency, and fiber-sizing effects. It was shown that Celion 6000 fiber-reinforced composites do not exhibit a straight-line Arrhenius relationship at temperatures above 316 C.

  1. Microstructural study of aluminium-matrix composites reinforced with SiC

    Energy Technology Data Exchange (ETDEWEB)

    Velhinho, A.; Braz Fernandes, F.M.; Botas, J.D. [CENIMAT, Centro de Investigacao de Materiais, Caparica (Portugal)

    2002-07-01

    Rheocasting, as a semi-solid process, allows the production of aluminium matrix composites at relatively low temperatures (ca. 580 C), thus favouring a reduced reactivity at the reinforcement-metal matrix interface. When one considers the possibility of further processing (such as any treatment involving remelting, even if partial) of the material, this trait allows a more rigorous control of the interfaces. Composite samples have been produced using as matrix an Al7Si-0.3Mg alloy reinforced with SiC{sub p} (granulometry: 120 {mu}m; V{sub r}=0.30). These were rheocast at 583 C, followed by compression and subsequent water-quenching. A structural characterisation (optical microscopy and XRD) of the as-received matrix material, as well as of the reinforced and non-reinforced rheocast material was performed. The phases identification will provide a basis for the understanding of the further processing where the rheocast material will be used as a precursor to produce functionally graded metal-matrix composites by centrifugal casting. (orig.)

  2. Hardness and wear resistance of carbon nanotube reinforced aluminum-copper matrix composites.

    Science.gov (United States)

    Nam, Dong Hoon; Kim, Jae Hwang; Cha, Seung Il; Jung, Seung Il; Lee, Jong Kook; Park, Hoon Mo; Park, Hyun Dal; Hong, Hyung

    2014-12-01

    Recently, carbon nanotubes (CNTs) have been attracted to reinforcement of composite materials due to their extraordinary mechanical, thermal and electrical properties. Many researchers have attempted to develop CNT reinforced metal composites with various fabrication methods and have shown possibilities for structural and functional applications. Among them, CNT reinforced Al matrix composites have become very attractive due to their huge structural application in industry. In this study, CNT reinforced Al-Cu matrix composites with a microstructure of homogeneous dispersion of CNTs in the Al-Cu matrix are investigated. The CNT/Al-Cu composites are fabricated by mixing of CNT/Cu composite powders and Al powders by high energy ball mill process followed by hot extrusion process. The hardness and wear resistance of the CNT/Al-Cu composites are enhanced by 1.4 and 3 times, respectively, compared to those values for the Al-Cu matrix. This remarkable enhancement mainly originates from the homogeneous dispersion of CNTs in Al-Cu matrix and self-lubricant effect of CNTs.

  3. Machining of fiber reinforced composites

    Science.gov (United States)

    Komanduri, Ranga; Zhang, Bi; Vissa, Chandra M.

    Factors involved in machining of fiber-reinforced composites are reviewed. Consideration is given to properties of composites reinforced with boron filaments, glass fibers, aramid fibers, carbon fibers, and silicon carbide fibers and to polymer (organic) matrix composites, metal matrix composites, and ceramic matrix composites, as well as to the processes used in conventional machining of boron-titanium composites and of composites reinforced by each of these fibers. Particular attention is given to the methods of nonconventional machining, such as laser machining, water jet cutting, electrical discharge machining, and ultrasonic assisted machining. Also discussed are safety precautions which must be taken during machining of fiber-containing composites.

  4. Interfacial Shear Strength Measurements of SiC Fiber-Reinforced Titanium Composites

    Institute of Scientific and Technical Information of China (English)

    Yanhua LI; Nanlin SHI; Dezhi ZHANG; Rui YANG

    2005-01-01

    A continuous loading push-out test technique was used to measure the interfacial shear strength of SiC fiber reinforced Ti matrix composites. The interracial shear strength of samples as-fabricated and after heat exposed at 700 and 800℃ for 50 h was successfully determined. It has been found that the interfacial shear strength of the specimen exposed at 700℃ was higher than that of as-prepared and exposed samples at 800℃. The shear strength of the as-prepared samples was about 112.45 MPa, and increased to about 153.77 MPa after heat-treating at 700℃ for 50 h, but decreased to 133.11 MPa after treating at 800℃ for 50 h. Scanning electron microscope (SEM) was used to investigate the interfacial morphology of the samples. The brittle phase was the main products of interface for samples exposed at 800℃, and the interface was easily peeled off.

  5. Reinforcement of polyetheretherketone polymer with titanium for improved mechanical properties and in vitro biocompatibility.

    Science.gov (United States)

    Jung, Hyun-Do; Park, Hui-Sun; Kang, Min-Ho; Li, Yuanlong; Kim, Hyoun-Ee; Koh, Young-Hag; Estrin, Yuri

    2016-01-01

    Blends of ductile Ti metal with polyetheretherketone (PEEK) polymer were studied with regard to their mechanical properties and in vitro biocompatibility. PEEK/Ti composites with various Ti contents, ranging from 0 vol % to 60 vol %, were produced by compression molding at 370°C. In all composites produced, regardless of the initial Ti content, Ti particles were well distributed in the PEEK matrix. Addition of Ti led to a significant increase in mechanical properties of PEEK. Specifically, an increase in Ti content enhanced compressive strength and stiffness, while preserving ductile fracture behavior. In addition, the use of Ti for reinforcement of PEEK provided the composites with improved in vitro biocompatibility in terms of the attachment, proliferation, and differentiation of MC3T3-E1 cells. © 2015 Wiley Periodicals, Inc.

  6. Nanofiber reinforcement of a geopolymer matrix for improved composite materials mechanical performance

    Science.gov (United States)

    Rahman, AKM Samsur

    Geopolymers have the potential to cross the process performance gap between polymer matrix and ceramic matrix composites (CMC), enabling high temperature capable composites that are manufactured at relatively low temperatures. Unfortunately, the inherently low toughness of these geopolymers limits the performance of the resulting fiber reinforced geopolymer matrix composites. Toughness improvements in composites can be addressed through the adjustments in the fiber/matrix interfacial strength and through the improvements in the inherent toughness of the constituent materials. This study investigates the potential to improve the inherent toughness of the geopolymer matrix material through the addition of nanofillers, by considering physical dimensions, mechanical properties, reinforcing capability and interfacial bond strength effects. A process optimization study was first undertaken to develop the ability to produce consistent, neat geopolymer samples, a critical precursor to producing nano-filled geopolymer for toughness evaluation. After that, single edge notched bend beam fracture toughness and un-notched beam flexural strength were evaluated for silicon carbide, alumina and carbon nanofillers reinforced geopolymer samples treated at various temperatures in reactive and inert environments. Toughness results of silicon carbide and carbon nanofillers reinforced geopolymers suggested that with the improved baseline properties, high aspect ratio nanofillers with high interfacial bond strength are the most capable in further improving the toughness of geopolymers. Among the high aspect ratio nanofillers i.e. nanofibers, 2vol% silicon carbide whicker (SCW) showed the highest improvement in fracture toughness and flexural strength of ~164% & ~185%, respectively. After heat treatment at 650 °C, SCW reinforcement was found to be effective, with little reduction in the performance, while the performance of alumina nanofiber (ANF) reinforced geopolymer significantly

  7. Multiwalled carbon nanotube-reinforced ceramic matrix composites as a promising structural material

    Energy Technology Data Exchange (ETDEWEB)

    Estili, Mehdi, E-mail: mehdiestili@gmail.co [Institute for Materials Research, Tohoku University, Sendai 980-8577 (Japan); Department of Materials Processing, Graduate School of Engineering, Tohoku University, Sendai 980-8579 (Japan); Kwon, Hansang; Kawasaki, Akira; Cho, Seungchan; Takagi, Kenta; Kikuchi, Keiko [Institute for Materials Research, Tohoku University, Sendai 980-8577 (Japan); Kawai, Masayoshi [Institute of Materials Structure Science, High Energy Accelerator Research Organization, Oho, Tsukuba, Ibaraki 305-0801 (Japan)

    2010-03-15

    In this paper, we introduce fully dense, multiwalled carbon nanotube (MWCNT)-reinforced ceramic matrix composites recently processed by a novel powder technology in our laboratory to be considered as a promising potential structural materials for employment in severe working conditions. A strategy is also offered to investigate the effect of working condition on the mechanical properties of MWCNTs embedded in the ceramic matrix for a reliable material selection for the working conditions needed.

  8. Metallic-fibre-reinforced ceramic-matrix composite

    Energy Technology Data Exchange (ETDEWEB)

    Prevost, F.; Schnedecker, G.; Boncoeur, M.

    1994-12-31

    A refractory metal wire cloth is embedded in an oxide ceramic matrix, using a plasma spraying technology, in order to elaborate composite plates. When mechanically tested, the composite fails with a pseudo-ductile fracture mode whereas the ceramic alone is originally brittle. It exhibits a higher fracture strength, and remains in the form of a single piece even when straining is important. No further heat treatment is needed after the original processing to reach these characteristics. (authors). 2 figs., 2 refs.

  9. Effect of reinforcement on the cutting forces while machining metal matrix composites–An experimental approach

    Directory of Open Access Journals (Sweden)

    Ch. Shoba

    2015-12-01

    Full Text Available Hybrid metal matrix composites are of great interest for researchers in recent years, because of their attractive superior properties over traditional materials and single reinforced composites. The machinabilty of hybrid composites becomes vital for manufacturing industries. The need to study the influence of process parameters on the cutting forces in turning such hybrid composite under dry environment is essentially required. In the present study, the influence of machining parameters, e.g. cutting speed, feed and depth of cut on the cutting force components, namely feed force (Ff, cutting force (Fc, and radial force (Fd has been investigated. Investigations were performed on 0, 2, 4, 6 and 8 wt% Silicon carbide (SiC and rice husk ash (RHA reinforced composite specimens. A comparison was made between the reinforced and unreinforced composites. The results proved that all the cutting force components decrease with the increase in the weight percentage of the reinforcement: this was probably due to the dislocation densities generated from the thermal mismatch between the reinforcement and the matrix. Experimental evidence also showed that built-up edge (BUE is formed during machining of low percentage reinforced composites at high speed and high depth of cut. The formation of BUE was captured by SEM, therefore confirming the result. The decrease of cutting force components with lower cutting speed and higher feed and depth of cut was also highlighted. The related mechanisms are explained and presented.

  10. Coating of carbon fiber-reinforced polyetheretherketone implants with titanium to improve bone apposition.

    Science.gov (United States)

    Devine, Declan M; Hahn, Joachim; Richards, R Geoffery; Gruner, Heiko; Wieling, Ronald; Pearce, Simon G

    2013-05-01

    Carbon fiber-reinforced polyetheretherketone (CF/PEEK) is a thermoplastic composite biomaterial exhibiting properties suitable for load-bearing orthopedic implants. However, the hydrophobic surface of CF/PEEK implants induces the deposition of a peri-implant fibrous tissue capsule preventing bone apposition. However, if bone apposition was improved, the use of CF/PEEK in orthopedics could be increased as it has many advantages compared with metallic implants. In this study, CF/PEEK screws were coated with titanium (Ti) using two different techniques, namely vacuum plasma spraying (VPS) and physical vapor deposition (PVD) with uncoated screws as controls. These coatings were characterized and implanted in a loaded sheep tibia model. In the characterization of the screw surfaces using microscopy techniques, the uncoated screws were seen to have an irregular surface. The PVD coating appeared smooth and consistent, whereas the VPS coating appeared to be a rough coating with some inhomogeneities, which did not cover the entire surface area. Nevertheless, in the ex vivo analysis the VPS-coated screws had a screw removal torque which was statistically greater than uncoated and PVD-coated screws (p ≤ 0.002 for both comparisons). Additionally, the VPS-coated screws had a statistically higher bone contact area than the uncoated screws (p = 0.006), whereas no statistical difference was detected between VPS and PVD coating types (p = 0.11). Thereby illustrating that Ti coating of CF/PEEK screws significantly improve bone apposition and removal torque compared with uncoated CF/PEEK screws.

  11. Seamless metal-clad fiber-reinforced organic matrix composite structures and process for their manufacture

    Science.gov (United States)

    Bluck, Raymond M. (Inventor); Bush, Harold G. (Inventor); Johnson, Robert R. (Inventor)

    1990-01-01

    A metallic outer sleeve is provided which is capable of enveloping a hollow metallic inner member having continuous reinforcing fibers attached to the distal end thereof. The inner member is then introduced into outer sleeve until inner member is completely enveloped by outer sleeve. A liquid matrix member is then injected into space between inner member and outer sleeve. A pressurized heat transfer medium is flowed through the inside of inner member, thereby forming a fiber reinforced matrix composite material. The wall thicknesses of both inner member and outer sleeve are then reduced to the appropriate size by chemical etching, to adjust the thermal expansion coefficient of the metal-clad composite structure to the desired value. thereby forming a fiber reinforced matrix composite material. The wall thicknesses of both inner member and outer sleeve are then reduced to the appropriate size by chemical etching, to adjust the thermal expansion coefficient of the metal-clad composite structure to the desired value. The novelty of this invention resides in the development of a efficient method of producing seamless metal clad fiber reinforced organic matrix composite structures.

  12. Volumetric Changes in Edentulous Alveolar Ridge Sites Utilizing Guided Bone Regeneration and a Custom Titanium Ridge Augmentation Matrix (CTRAM)

    Science.gov (United States)

    2016-06-01

    Milling CBCT Cone Beam Computed Tomography CT Computed Tomography CTRAM Custom Titanium Ridge Augmentation Matrix DMLS Direct Metal Laser Sintering ...could be used by Direct Metal Laser Sintering (DMLS) to create custom titanium mesh to reconstruct a deficient maxillary alveolar anterior ridge. A pre...Sinus Augmentations. Int J Periodont Rest Dent 2005; 25:231-237. Ciocca L, Fantini M, De Crescenzio F, Corinaldesi G, Scotti R. Direct Metal

  13. Fabrication and characterization of carbon nanotube reinforced magnesium matrix composites

    Science.gov (United States)

    Mindivan, Harun; Efe, Arife; Kosatepe, A. Hadi; Kayali, E. Sabri

    2014-11-01

    In the present investigation, Mg chips are recycled to produce Mg-6 wt.% Al reinforced with 0.5, 1, 2 and 4 wt.% nanosized CNTs by mechanical ball milling, cold pressing and subsequently hot extrusion process without sintering step. The microstructure, mechanical properties and corrosion behavior of Mg/Al without CNT (base alloy) and composites were evaluated. The distribution of CNTs was analyzed using a Scanning Electron Microscopy (SEM) equipped with Energy Dispersive Spectroscopy (EDS) analyzer and a Wavelength Dispersive X-Ray Fluorescence spectrometer (WDXRF). Microstructural analysis revealed that the CNTs on the Mg chips were present throughout the extrusion direction and the uniform distribution of CNTs at the chip surface decreased with increase in the CNT content. The results of the mechanical and corrosion test showed that small addition of CNTs (0.5 wt.%) evidently improved the hardness and corrosion resistance of the composite by comparing with the base alloy, while increase in the CNT weight fraction in the initial mixture resulted in a significant decrease of hardness, compression strength, wear rate and corrosion resistance.

  14. NewIn-situ synthesis method of magnesium matrix composites reinforced with TiC particulates

    Directory of Open Access Journals (Sweden)

    Zhang Xiuqing

    2006-12-01

    Full Text Available Magnesium matrix composites reinforced with TiC particulates was prepared using a new in-situ synthesis method of remelting and dilution technique. And measurements were performed on the composites. The results of x ray diffraction (XRD analysis confirmed that TiC particulates were synthesized during the sintering process, and they retained in magnesium matrix composites after the remelting and dilution processing. From the microstructure characterization and electron probe microanalysis (EPMA, we could see that fine TiC particulates distributed uniformly in the matrix material.

  15. Determination of Material Parameters for Microbuckling Analysis of Fiber Reinforced Polymer Matrix Composites

    Directory of Open Access Journals (Sweden)

    Romanowicz M.

    2015-05-01

    Full Text Available This research focuses on studying the effect of the constitutive law adopted for a matrix material on the compressive response of a unidirectional fiber reinforced polymer matrix composite. To investigate this effect, a periodic unit cell model of a unidirectional composite with an initial fiber waviness and inelastic behavior of the matrix was used. The sensitivity of the compressive strength to the hydrostatic pressure, the flow rule and the fiber misalignment angle were presented. The model was verified against an analytical solution and experimental data. Results of this study indicate that a micromechanical model with correctly identified material parameters provides a useful alternative to theoretical models and experimentation.

  16. Determination of Material Parameters for Microbuckling Analysis of Fiber Reinforced Polymer Matrix Composites

    Science.gov (United States)

    Romanowicz, M.

    2015-05-01

    This research focuses on studying the effect of the constitutive law adopted for a matrix material on the compressive response of a unidirectional fiber reinforced polymer matrix composite. To investigate this effect, a periodic unit cell model of a unidirectional composite with an initial fiber waviness and inelastic behavior of the matrix was used. The sensitivity of the compressive strength to the hydrostatic pressure, the flow rule and the fiber misalignment angle were presented. The model was verified against an analytical solution and experimental data. Results of this study indicate that a micromechanical model with correctly identified material parameters provides a useful alternative to theoretical models and experimentation.

  17. The effect of enamel matrix proteins on the spreading, proliferation and differentiation of osteoblasts cultured on titanium surfaces.

    Science.gov (United States)

    Miron, Richard J; Oates, Christine J; Molenberg, Aart; Dard, Michel; Hamilton, Douglas W

    2010-01-01

    Modifications of implant surface topography and chemistry have proven a means to enhance osseointegration, a process that ensures the stability of bone-contacting devices, including titanium dental implants. The commercial product Emdogain is an enamel matrix derivative (EMD) extracted from porcine teeth commonly used in periodontal surgery, where it has been shown to potentiate regeneration of bone. The aim of the present study was to evaluate the effect of EMD on the attachment, proliferation and differentiation of osteoblasts on titanium surfaces in vitro. Pickled (smooth) and SLA (roughened) titanium discs were coated with EMD or left uncoated. Primary rat calvarial osteoblasts were cultured on each surface from 1h to 4 weeks. EMD significantly increased cell spreading and proliferation at time points ranging from 3 to 7 days on both topographies. Alkaline phosphatase activity was significantly increased on EMD-coated titanium compared with titanium alone. Moreover, there was a 6 fold increase in levels of mRNA encoding bone sialoprotein and osteocalcin in osteoblasts cultured on EMD-coated titanium surfaces compared with uncoated surfaces. We conclude that coating of titanium with EMD enhances the proliferation and differentiation of osteoblasts irrespective of the titanium substratum topography.

  18. Evaluation of titanium carbide metal matrix composites deposited via laser cladding

    Science.gov (United States)

    Cavanaugh, Daniel Thomas

    Metal matrix composites have been widely studied in terms of abrasion resistance, but a particular material system may behave differently as particle size, morphology, composition, and distribution of the hardening phase varies. The purpose of this thesis was to understand the mechanical and microstructural effects of combining titanium carbide with 431 series stainless steel to create a unique composite via laser cladding, particularly regarding wear properties. The most predominant effect in increasing abrasion resistance, measured via ASTM G65, was confirmed to be volume fraction of titanium carbide addition. Macrohardness was directly proportional to the amount of carbide, though there was an overall reduction in individual particle microhardness after cladding. The reduction in particle hardness was obscured by the effect of volume fraction carbide and did not substantially contribute to the wear resistance changes. A model evaluating effective mean free path of the titanium carbide particles was created and correlated to the measured data. The model proved successful in linking theoretical mean free path to overall abrasion resistance. The effects of the titanium carbide particle distributions were limited, while differences in particle size were noticeable. The mean free path model did not correlate well with the particle size, but it was shown that the fine carbides were completely removed by the coarse abrasive particles in the ASTM G65 test. The particle morphology showed indications of influencing the wear mode, but no statistical reduction was observed in the volume loss figures. Future studies may more specifically focus on particle morphology or compositional effects of the carbide particles.

  19. Multiple strengthening mechanisms in nanoparticle-reinforced copper matrix composites

    Indian Academy of Sciences (India)

    D Bozic; J Stasic; B Dimcic; M Vilotijevic; V Rajkovic

    2011-04-01

    The multiple hardening mechanisms of a copper matrix have been presented and discussed. The prealloyed ball milled Cu–3 wt.%Al and the atomized Cu–0.6 wt.%Ti–2.5 wt.%TiB2 powders have been used as starting materials. Dispersoid particles Al2O3 and TiB2 were formed in situ. The powders have been hot consolidated. Optical microscopy, SEM, TEM, and X-ray diffraction analysis were performed for microstructural characterization. Increase in microhardness of Cu–3 wt.%Al compacts is a consequence of the crystallite size refinement and the presence of Al2O3 particles. High hardening of Cu–0.6 wt.%Ti–2.5 wt.%TiB2 is a consequence of the presence of modular structure, Cu4Ti$_{(m)}$, and TiB2 particles.

  20. Fabrication of BN Nanosheet Reinforced ZrO{sub 2} Composite Pellets for Inert Matrix Fuel

    Energy Technology Data Exchange (ETDEWEB)

    Shukeir, Malik; Umer, Malik; Lee, Bin; Ryu, Ho Jin [Korea Advanced Institute of Science and Technology, Daejeon (Korea, Republic of)

    2014-10-15

    Plutonium also can be resulted from the dismantlement of nuclear weapons. This will result in the increase of the stockpile of plutonium. For that purpose many organizations are focusing their R-D work on the concept of Inert Matrix Fuel IMF, where a U-free matrix is used to eliminate the U-Pu conversion. R-D work was standardized around Zirconiabased IMF as a result of many screening and ranking studies performed on various candidates. Regardless of its outstanding radiation resistance, chemical stability and its high melting point, it has a very low thermal conductivity, which could be detrimental for the fuel matrix especially in case of accidents. A reinforcement phase could be used for the enhancement of the thermomechanical properties. Among many possible reinforcements, 2D structured nanosheets have emerged as an excellent candidate to enhance the thermal properties and mechanical properties simultaneously. In this approach Boron Nitride Nanosheets BNNS are used for that purpose. BNNS have a very low density, very high thermal conductivity, very high mechanical properties and high neutron absorption cross-section for Boron which is used frequently as a burnable poison. They have properties similar to graphene but they exhibit superior thermal stability in the oxide structure. Despite all the studies on other reinforcements, BNNS reinforced ZrO{sub 2} has not yet been reported. In this study, pure ZrO{sub 2} and partially stabilized Zirconia PSZ (using Yttria) ceramics are mixed with different volume fractions of BNNS.

  1. Effect of nanoparticle dispersion on mechanical behavior of polymer matrix and their fiber reinforced composites

    Science.gov (United States)

    Uddin, Mohammed Farid

    Fiber reinforced composites are widely used to achieve weight savings in different construction. However, their used are restricted as their matrix-dominant properties are much weaker than their fiber-dominated properties. The recent advent of nanoparticles has attracted much attention in improving the matrix properties by using various nanoparticles as reinforcements. Due to the lack of well-developed and consistent processing method, experimental results on nanocomposites show a broad spectrum of anomalies in their properties. Dispersion of nanoparticles in the polymeric precursor is often blamed for these inconsistencies in their properties which becomes even worse with high particle loading. In this research, a processing technique has been developed to fabricate very well-dispersed nanocomposite even with high particle loading in order to fully utilize the advantages of nanoparticle reinforcement. An attempt has also been made to modify the conventional sonication method to improve the dispersion by combining the sol-gel and sonication methods to fabricate hybrid nanocomposites. Transmission electronic microscopy has been employed to investigate dispersion quality of nanoparticles. Finally, mechanical characterization has been performed to evaluate the effect of different state of particle dispersion. Once the effect of dispersion is identified, a micromechanical model has been proposed to estimate the strength of particle reinforced composites based on particle/matrix interfacial crack growth. Finite element analyses were performed to validate the experimental results for microparticle reinforced composites. Using the model, effect of particle size has also been validated with experimental results. The model is then further extended to reveal the failure modes in nanocomposite with the support of some experimental evidences. Finally, an effort has been made to evaluate the potential application of the nanoparticle modified resin by fabricating unidirectional

  2. Thermo-oxidative stability studies of PMR-15 polymer matrix composites reinforced with various continuous fibers

    Science.gov (United States)

    Bowles, Kenneth J.

    1990-01-01

    An experimental study was conducted to measure the thermooxidative stability of PMR-15 composites reinforced with various fibers and to observe differences in the way they degrade in air. The fibers studied include graphite and the thermally stable Nicalon and Nextel ceramic fibers. Weight-loss rates for the different composites were assessed as a function of mechanical properties, specimen geometry, fiber sizing, and interfacial bond strength. Differences were observed in rates of weight loss, matrix cracking, geometry dependency, and fiber sizing effects. It was shown that Celion 6000 fiber-reinforced composites do not exhibit a straight-line Arrhenius relationship at temperatures above 316 C.

  3. Influence of Carbon & Glass Fiber Reinforcements on Flexural Strength of Epoxy Matrix Polymer Hybrid Composites

    Directory of Open Access Journals (Sweden)

    T.D. Jagannatha

    2015-04-01

    Full Text Available Hybrid composite materials are more attracted by the engineers because of their properties like stiffness and high specific strength which leads to the potential application in the area of aerospace, marine and automobile sectors. In the present investigation, the flexural strength and flexural modulus of carbon and glass fibers reinforced epoxy hybrid composites were studied. The vacuum bagging technique was adopted for the fabrication of polymer hybrid composite materials. The hardness, flexural strength and flexural modulus of the hybrid composites were determined as per ASTM standards. The hardness, flexural strength and flexural modulus were improved as the fiber reinforcement contents increased in the epoxy matrix material.

  4. Friction stir processing of an aluminum-magnesium alloy with pre-placing elemental titanium powder: In-situ formation of an Al{sub 3}Ti-reinforced nanocomposite and materials characterization

    Energy Technology Data Exchange (ETDEWEB)

    Khodabakhshi, F., E-mail: farzadkhodabakhshi83@gmail.com [Department of Materials Science and Engineering, School of Engineering, Shiraz University, Zand Boulevard, Shiraz (Iran, Islamic Republic of); Simchi, A. [Department of Materials Science and Engineering, Sharif University of Technology, P.O. Box 11365-9466, Azadi Avenue, 14588 Tehran (Iran, Islamic Republic of); Institute for Nanoscience and Nanotechnology, Sharif University of Technology, P.O. Box 11365-9466, Azadi Avenue, 14588 Tehran (Iran, Islamic Republic of); Kokabi, A.H. [Department of Materials Science and Engineering, Sharif University of Technology, P.O. Box 11365-9466, Azadi Avenue, 14588 Tehran (Iran, Islamic Republic of); Gerlich, A.P. [Department of Mechanical and Mechatronics Engineering, University of Waterloo, Waterloo, ON (Canada)

    2015-10-15

    A fine-grained Al–Mg/Al{sub 3}Ti nanocomposite was fabricated by friction stir processing (FSP) of an aluminum-magnesium (AA5052) alloy with pre-placed titanium powder in the stirred zone. Microstructural evolutions and formation of intermetallic phases were analyzed by optical and electron microscopic techniques across the thickness section of the processed sheets. The microstructure of the nanocomposite consisted of a fine-grained aluminum matrix (1.5 µm), un-reacted titanium particles (<40 µm) and reinforcement particles of Al{sub 3}Ti (<100 nm) and Mg{sub 2}Si (<100 nm). Detailed microstructural analysis indicated solid-state interfacial reactions between the aluminum matrix and micro-sized titanium particles to form Al{sub 3}Ti intermetallic phase. The hard inclusions were then fractured and re-distributed in the metal matrix by the severe thermo-mechanical conditions imposed by FSP. Evaluation of mechanical properties by hardness measurement and uniaxial tensile test determined significant enhancement in the mechanical strength (by 2.5 order of magnetite) with a high ductility (~22%). Based on a dislocation-based model analysis, it was suggested that the strength enhancement was governed by grain refinement and the presence of hard inclusions (4 vol%) in the metal matrix. Fractographic studies also showed a ductile-brittle fracture mode for the nanocomposite compared with fully ductile rupture of the annealed alloy as well as the FSPed specimen without pre-placing titanium particles. - Highlights: • FSP was employed to fabricate in situ nanocomposite. • The AA5052 Al alloy with pre-placed micro-sized Ti particles were utilized. • The structural analysis was revealed that the in situ formation of Al{sub 3}Ti nanophase. • The SZ grain structure was refined by PSN and ZHP mechanisms during DRX. • Hardness and tensile strength were improved up to ~2.5 times with a good ductility.

  5. Corn gluten meal as a biodegradable matrix material in wood fibre reinforced composites

    Energy Technology Data Exchange (ETDEWEB)

    Beg, M.D.H. [Department of Materials and Process Engineering, University of Waikato, Private Bag 3105, Hamilton (New Zealand); Pickering, K.L. [Department of Materials and Process Engineering, University of Waikato, Private Bag 3105, Hamilton (New Zealand)]. E-mail: klp@waikato.ac.nz; Weal, S.J. [Department of Materials and Process Engineering, University of Waikato, Private Bag 3105, Hamilton (New Zealand)

    2005-12-05

    This study was undertaken to investigate corn gluten meal (CGM) as a biodegradable matrix material for wood fibre reinforced composites. CGM was used alone, as well as hybridized with polypropylene, and reinforced with radiata pine (Pinus Radiata) fibre using a twin-screw extruder followed by injection moulding. Tensile testing, scanning electron microscopy and differential scanning calorimetry were carried out to assess the composites. For composites from CGM and wood fibres, extrusion was carried out with the aid of the following plasticizers: octanoic acid, glycerol, polyethylene glycol and water. Windows of processability for the different plasticizers were obtained for all plasticizers. These were found to lie between 20 and 50 wt.% of plasticizer with a maximum of approximately 20% wood fibre reinforcement. The best mechanical properties were obtained with a matrix containing 10 wt.% octanoic acid and 30 wt.% water, which gave a tensile strength and Young's modulus of 18.7 MPa and 4 GPa, respectively. Hybrid matrix composites were compounded with a maleated polypropylene coupling agent and benzoyl peroxide as a cross-linking agent. The highest tensile strength and Young's modulus obtained from hybrid matrix composites were 36.9 MPa and 5.8 GPa with 50 wt.% fibre.

  6. Niobium Carbide-Reinforced Al Matrix Composites Produced by High-Energy Ball Milling

    Science.gov (United States)

    Travessa, Dilermando Nagle; Silva, Marina Judice; Cardoso, Kátia Regina

    2017-06-01

    Aluminum and its alloys are key materials for the transportation industry as they contribute to the development of lightweight structures. The dispersion of hard ceramic particles in the Al soft matrix can lead to a substantial strengthening effect, resulting in composite materials exhibiting interesting mechanical properties and inspiring their technological use in sectors like the automotive and aerospace industries. Powder metallurgy techniques are attractive to design metal matrix composites, achieving a homogeneous distribution of the reinforcement into the metal matrix. In this work, pure aluminum has been reinforced with particles of niobium carbide (NbC), an extremely hard and stable refractory ceramic. Its use as a reinforcing phase in metal matrix composites has not been deeply explored. Composite powders produced after different milling times, with 10 and 20 vol pct of NbC were produced by high-energy ball milling and characterized by scanning electron microscopy and by X-ray diffraction to establish a relationship between the milling time and size, morphology, and distribution of the particles in the composite powder. Subsequently, an Al/10 pct NbC composite powder was hot extruded into cylindrical bars. The strength of the obtained composite bars is comparable to the commercial high-strength, aeronautical-grade aluminum alloys.

  7. A STEEL MATRIX WEAR RESISTANT COMPOSITE REINFORCED BY IN-SITU GRANULAR EUTECTICS

    Institute of Scientific and Technical Information of China (English)

    Z.M. Xu; T.X. Li; J.G. Li

    2001-01-01

    A new steel matrix wear resistant composite reinforced by in situ granular eutectics can be obtained by modifying with a Si-Ce-Ti compound in the steel melt. The result indicates that the in situ granular eutectic is a pseudo-eutectic of austenite and (Fe, Mn)3C, which is formed between austenite dendrites during solidification due to the segregation of C and Mn impelled by modifying elements. The quantity of in situ granular eutectic reaches up to 8% 12%, and its grain size is in the range from 10μm to 20μm. The austenite steel matrix wear resistant composite reinforced by in situ granular eutectic (abbreviated AGE composite) and austenite-bainite steel matrix wear resistant composite reinforced by in situ granular eutectic (abbreviated ABGE composite) are obtained in the as-cast state and by air hardening, respectively. The wear resistance of the AGE and ABGE composites can be more greatly increased than that of their matrix steels under low and medium impact working condition.

  8. Finite element analysis of stress transfer mechanism from matrix to the fiber in SWCN reinforced nanocomposites

    Science.gov (United States)

    Günay, E.

    2017-02-01

    This study defined as micromechanical finite element (FE) approach examining the stress transfer mechanism in single-walled carbon nanotube (SWCN) reinforced composites. In the modeling, 3D unit-cell method was evaluated. Carbon nanotube reinforced composites were modeled as three layers which comprises CNT, interface and matrix material. Firstly; matrix, fiber and interfacial materials all together considered as three layered cylindrical nanocomposite. Secondly, the cylindrical matrix material was assumed to be isotropic and also considered as a continuous medium. Then, fiber material was represented with zigzag type SWCNs. Finally, SWCN was combined with the elastic medium by using springs with different constants. In the FE modeling of SWCN reinforced composite model springs were modeled by using ANSYS spring damper element COMBIN14. The developed interfacial van der Waals interaction effects between the continuous matrix layer and the carbon nanotube fiber layer were simulated by applying these various spring stiffness values. In this study, the layered composite cylindrical FE model was presented as the equivalent mechanical properties of SWCN structures in terms of Young's modulus. The obtained results and literature values were presented and discussed. Figures, 16, 17, and 18 of the original article PDF file, as supplied to AIP Publishing, were affected by a PDF-processing error. Consequently, a solid diamond symbol appeared instead of a Greek tau on the y axis labels for these three figures. This article was updated on 17 March 2017 to correct the PDF-processing error, with the scientific content remaining unchanged.

  9. Mechanical and moisture barrier properties of titanium dioxide nanoparticles and halloysite nanotubes reinforced polylactic acid (PLA)

    Science.gov (United States)

    Alberton, J.; Martelli, S. M.; Fakhouri, F. M.; Soldi, V.

    2014-08-01

    Polylactic acid (PLA) has been larger used in biomedical field due to its low toxicity and biodegradability. The aim of this study was to produce PLLA nanocomposites, by melt extrusion, containing Halloysite nanotubes (HNT) and/or titanium dioxide (TiO2) nanoparticles. Immediately after drying, PLLA was mechanically homogenized with the nanofillers and then melt blended using a single screw extruder (L/D = 30) at a speed of 110 rpm, with three heating zones in which the following temperatures were maintained: 150, 150 and 160°C (AX Plasticos model AX14 LD30). The film samples were obtained by compression molding in a press with a temperature profile of 235 ± 5°C for 2.5 min, after pressing, films were cooled up to room temperature. The mechanical tests were performed according to ASTM D882-09 and the water vapor permeability (WVP) was measured according to ASTM E-96, in triplicate. The tensile properties indicated that the modulus was improved with increased TiO2 content up to 1g/100g PLLA. The Young's modulus (YM) of the PLA was increased from 3047 MPa to 3222 MPa with the addition of 1g TiO2/100g PLLA. The tensile strength (TS) of films increases with the TiO2 content. In both cases, the YM and TS are achieved at the 1% content of TiO2 and is due to the reinforcing effect of nanoparticles. Pristine PLA showed a strain at break (SB) of 3.56%, while the SB of nanocomposites were significant lower, for instance the SB of composite containing 7.5 g HNT/100g PLLA was around 1.90 %. The WVP of samples was increased by increasing the nano filler content. It should be expected that an increase of nanofiller content would decrease the mass transfer of water molecules throughout the samples due to the increase in the way water molecules will have to cross to permeate the material. However, this was not observed. Therefore, this result can be explained considering the molecular structure of both fillers, which contain several hydroxyl groups in the surface, making the

  10. Dynamic Effects in Elastothermodynamic Damping of Hollow Particle Reinforced Metal-Matrix Composites

    Science.gov (United States)

    Srivastava, Sunil Kumar; Mishra, Bhanu Kumar

    2016-06-01

    The Metal-Matrix Composites (MMCs) containing hollow spherical reinforcements are under active development for the applications such as space structures, submarine hulls etc. where weight is of critical importance. When these materials are subjected to a time varying strain field, energy is dissipated because of the thermoelastic effect (Elastothermodynamic Damping or ETD). The quasi-static ETD analysis for the MMCs containing hollow spherical particles has been reported in literature. The entropic approach, which is better suited for composite materials with perfect or imperfect interfaces, is used for the analysis. In the present work, the effect of inertia forces is carried out on ETD of hollow particle-reinforced MMCs. For given particle volume fractions (V p ), the inertia forces are found to be more significant at higher value of thermal parameter (Ω T1) (alternatively, frequency of vibration if reinforcement radius is fixed), large cavity volume fraction (V h ) and low value of the parameter B1.

  11. Multi-Scale CNT-Based Reinforcing Polymer Matrix Composites for Lightweight Structures

    Science.gov (United States)

    Eberly, Daniel; Ou, Runqing; Karcz, Adam; Skandan, Ganesh; Mather, Patrick; Rodriguez, Erika

    2013-01-01

    Reinforcing critical areas in carbon polymer matrix composites (PMCs), also known as fiber reinforced composites (FRCs), is advantageous for structural durability. Since carbon nanotubes (CNTs) have extremely high tensile strength, they can be used as a functional additive to enhance the mechanical properties of FRCs. However, CNTs are not readily dispersible in the polymer matrix, which leads to lower than theoretically predicted improvement in mechanical, thermal, and electrical properties of CNT composites. The inability to align CNTs in a polymer matrix is also a known issue. The feasibility of incorporating aligned CNTs into an FRC was demonstrated using a novel, yet commercially viable nanofiber approach, termed NRMs (nanofiber-reinforcing mats). The NRM concept of reinforcement allows for a convenient and safe means of incorporating CNTs into FRC structural components specifically where they are needed during the fabrication process. NRMs, fabricated through a novel and scalable process, were incorporated into FRC test panels using layup and vacuum bagging techniques, where alternating layers of the NRM and carbon prepreg were used to form the reinforced FRC structure. Control FRC test panel coupons were also fabricated in the same manner, but comprised of only carbon prepreg. The FRC coupons were machined to size and tested for flexural, tensile, and compression properties. This effort demonstrated that FRC structures can be fabricated using the NRM concept, with an increased average load at break during flexural testing versus that of the control. The NASA applications for the developed technologies are for lightweight structures for in-space and launch vehicles. In addition, the developed technologies would find use in NASA aerospace applications such as rockets, aircraft, aircraft/spacecraft propulsion systems, and supporting facilities. The reinforcing aspect of the technology will allow for more efficient joining of fiber composite parts, thus offering

  12. Reinforcing mechanisms of starch nanocrystals in a nonvulcanized natural rubber matrix.

    Science.gov (United States)

    Mélé, Patrice; Angellier-Coussy, Hélène; Molina-Boisseau, Sonia; Dufresne, Alain

    2011-05-09

    A phenomenological modeling approach was developed to try to understand the reinforcing mechanism of starch nanocrystals in a nonvulcanized natural rubber matrix. Natural rubber was not cross-linked to maintain the biodegradability of the biosourced materials. Nonlinear dynamic mechanical experiments highlighted the significant reinforcing effect of starch nanocrystals and the presence of the Mullins and Payne effects. Two models were used to predict the Payne effect considering that either filler-filler (Kraus model) or matrix-filler (Maier and Göritz model) interactions are preponderant. The use of the Maier and Goritz model demonstrated that phenomena of adsorption and desorption of NR chains on the filler surface governed nonlinear viscoelastic properties, even if the formation of a percolating network for filler contents >6.7 vol % was evidenced by the Kraus model.

  13. Evaluation of tensile strength of hybrid fiber (jute/gongura) reinforced hybrid polymer matrix composites

    Science.gov (United States)

    Venkatachalam, G.; Gautham Shankar, A.; Vijay, Kumar V.; Chandan, Byral R.; Prabaharan, G. P.; Raghav, Dasarath

    2015-07-01

    The polymer matrix composites attract many industrial applications due to its light weight, less cost and easy for manufacturing. In this paper, an attempt is made to prepare and study of the tensile strength of hybrid (two natural) fibers reinforced hybrid (Natural + Synthetic) polymer matrix composites. The samples were prepared with hybrid reinforcement consists of two different fibers such as jute and Gongura and hybrid polymer consists of polyester and cashew nut shell resins. The hybrid composites tensile strength is evaluated to study the influence of various fiber parameters on mechanical strength. The parameters considered here are the duration of fiber treatment, the concentration of alkali in fiber treatment and nature of fiber content in the composites.

  14. Tribological properties of metal-matrix composite materials reinforced by superelastic hard carbon particles

    Science.gov (United States)

    Ushakova, I. N.; Drozdova, E. I.; Chernogorova, O. P.; Blinov, V. M.; Ekimov, E. A.

    2016-05-01

    Metal-matrix composite materials (CMs) are synthesized from a mixture of a metal powder (Ti, Fe, Co, Ni, Cu, Al-based alloy) and fullerenes (10 wt %). The thermobaric synthesis conditions (700-1000°C, 5-8 GPa) ensure the collapse of fullerene molecules and their transformation into superelastic carbon phase particles with an indentation hardness H IT = 10-37 GPa, an elastic modulus E IT = 60-260 GPa, and an elastic recovery of >80% upon indentation. After reinforcing by superelastic hard carbon, the friction coefficient of CM decreases by a factor of 2-4 as compared to the friction coefficient of the matrix metal, and the abrasive wear resistance increases by a factor of 4-200. Superelastic hard carbon particles are a unique reinforcing material for an increase in the wear resistance and a simultaneous decrease in the friction coefficient of CM.

  15. Synthesis and Characterization of Pine Needles Reinforced RF Matrix Based Biocomposites

    Directory of Open Access Journals (Sweden)

    A. S. Singha

    2008-01-01

    Full Text Available Synthesis and characterization of pine needles reinforced thermosetting resin (Resorcinol-Formaldehyde which is most suitable as composite matrix has been reported. The polycondensation reaction between resorcinol and formaldehyde (RF in different molar ratios has been applied to the synthesis of RF polymer matrix. A thermosetting resin based composite, containing approximately 10, 20, 30 and 40% of natural fiber by weight, has been obtained by adding pine needles to the Resorcinol-Formaldehyde (RF resin. The mechanical properties of randomly oriented intimately mixed particle reinforced (Pine needles composites were determined. Effect of fiber loading in terms of weight % on mechanical properties such as tensile, compressive, and flexural and wear properties have also been evaluated. The reinforcing of the resin with Pine needles was accomplished in particle size of 200 micron by employing optimized resin. Present work reveals that mechanical properties of the RF resin increases to extensive extent when reinforced with Pine needles. Thermal (TGA/DTA and morphological studies (SEM of the resin, fiber and polymer composites thus synthesized have also been carried out.

  16. Thermal expansion of multiwall carbon nanotube reinforced nanocrystalline silver matrix composite

    Energy Technology Data Exchange (ETDEWEB)

    Sharma, Manjula, E-mail: manjula.physics@gmail.com; Sharma, Vimal [Department of Physics, NIT Hamirpur - 177005, HP (India); Pal, Hemant [Department of Physics, NIT Hamirpur - 177005, HP, India and Department of Physics, Govt. College Chamba - 176310, HP (India)

    2014-04-24

    Multiwall carbon nanotube reinforced silver matrix composite was fabricated by novel molecular level mixing method, which involves nucleation of Ag ions inside carbon nanotube dispersion at the molecular level. As a result the carbon nanotubes get embedded within the powder rather than on the surfaces. Micro structural characterization by X- ray diffraction and scanning electron microscopy reveals that the nanotubes are homogeneously dispersed and anchored within the matrix. The thermal expansion of the composite with the multiwall nanotube content (0, 1.5 vol%) were investigated and it is found that coefficient of thermal expansion decreases with the addition of multiwall nanotube content and reduce to about 63% to that of pure Ag.

  17. SiC reinforced-MoSi sub 2 based matrix composites

    Energy Technology Data Exchange (ETDEWEB)

    Petrovic, J.J.; Honnell, R.E.

    1990-01-01

    SiC reinforced-MoSi{sub 2} based matrix composites possess very significant potential as high temperature structural materials for temperatures above 1200{degree}C in oxidizing environments, due to their combination of oxidation resistance, thermodynamic stability, machinability, elevated temperature ductility and strength, and ability to alloy the MoSi{sub 2} matrix with other silicides. The fabrication, microstructures, oxidation, and mechanical properties of these materials are described, and their current properties are compared to high temperature metals and structural ceramics. 22 refs., 5 figs., 2 tabs.

  18. Research on Vibration Cutting Performance of Particle Reinforced Metallic Matrix Composites SiC_p/Al

    Institute of Scientific and Technical Information of China (English)

    2002-01-01

    The cutting performance of particle reinforced meta ll ic matrix composites (PRMMCs) SiC p/Al in ultrasonic vibration cutting and comm on cutting with carbide tools and PCD tools was experimentally researched in the paper. The changing rules of chip shape, deformation coefficient, shear angle a nd surface residual stress were presented by ultrasonic vibration cutting. Resul ts show: when adopting common cutting, spiral chip with smaller curl radius will be obtained. The chip with zigzag contour is short ...

  19. Sol-gel coatings as active barriers to protect ceramic reinforcement in aluminum matrix composites

    Energy Technology Data Exchange (ETDEWEB)

    Rams, J.; Urena, A.; Campo, M. [Departamento de Tecnologia Quimica, Ambiental y de los Materiales, ESCET, Universidad Rey Juan Carlos C/ Tulipan s/nMostoles 28933 Madrid (Spain)

    2004-02-01

    Silica obtained through a sol-gel process is used as a coating for ceramic reinforcements (SiC) in aluminium matrix composite materials. The interaction between molten aluminium and the coated particles during material casting can be controlled by means of the thermal treatment given to the coating. Wettability is increased because the coating reacts with molten aluminium, and the formation of the degrading aluminium carbide is inhibited. (Abstract Copyright [2004], Wiley Periodicals, Inc.)

  20. Sodium sulfate corrosion of silicon carbide fiber-reinforced lithium aluminosilicate glass-ceramic matrix composites

    OpenAIRE

    1993-01-01

    Approved for public release; distribution is unlimited. Sodium sulfate hot corrosion of a SiC fiber-reinforced lithium aluminosilicate (LAS) glass-ceramic matrix composite was studied using Scanning Electron Microscope (SEM) and X-ray Diffraction (XRD). Changes in the microstructural chemical composition of the specimens were investigated. The samples provided by Naval Air Warfare Center (NAWC), Warminster, PA were grouped as follows: (1) as-received, (2) Na2SO4 salt-coated and heat-treate...

  1. Effect of reinforcement type and porosity on strength of metal matrix composite

    Science.gov (United States)

    Kulkarni, S. G.; Lal, Achchhe; Menghani, J. V.

    2016-05-01

    In the present work, experimental investigation and the numerical analysis are carried out for strength analysis of A356 alloy matrix composites reinforced with alumina, fly ash and hybrid particle composites. The combined strengthening effect of load bearing, Hall-Petch, Orowan, coefficient of thermal expansion mismatch and elastic modulus mismatch is studied for predicting accurate uniaxial stress-strain behavior of A356 based alloy matrix composite. The unit cell micromechanical approach and nine noded isoparametric finite element analysis (FEA) is used to investigate the yield failure load by considering material defect of porosity as fabrication errors in particulate composite. The Ramberg-Osgood approach is considered for the linear and nonlinear relationship between stress and strain of A356 based metal matrix composites containing different amounts of fly ash and alumina reinforcing particles. A numerical analysis of material porosity on the stress strain behavior of the composite is performed. The literature and experimental results exhibit the validity of this model and confirm the importance of the fly ash as the cheapest and low density reinforcement obtained as a waste by product in thermal power plants.

  2. Full incorporation of Strattice™ Reconstructive Tissue Matrix in a reinforced hiatal hernia repair: a case report

    Directory of Open Access Journals (Sweden)

    Freedman Bruce E

    2012-08-01

    Full Text Available Abstract Introduction A non-cross-linked porcine acellular dermal matrix was used to reinforce an esophageal hiatal hernia repair. A second surgery was required 11 months later to repair a slipped Nissen; this allowed for examination of the hiatal hernia repair and showed the graft to be well vascularized and fully incorporated. Case presentation A 71-year-old Caucasian woman presented with substernal burning and significant dysphagia. An upper gastrointestinal series revealed a type III complex paraesophageal hiatal hernia. She underwent laparoscopic surgery to repair a hiatal hernia that was reinforced with a xenograft (Strattice™ Reconstructive Tissue Matrix, LifeCell, Branchburg, NJ, USA along with a Nissen fundoplication. A second surgery was required to repair a slipped Nissen; this allowed for examination of the hiatal repair and graft incorporation 11 months after the initial surgery. Conclusion In this case, a porcine acellular dermal matrix was an effective tool to reinforce the crural hiatal hernia repair. The placement of the mesh and method of fixation are believed to be crucial to the success of the graft. It was found to be well vascularized 11 months after the original placement with no signs of erosion, stricture, or infection. Further studies and long-term follow-up are required to support the findings of this case report.

  3. Production of Decorative Cast Metal Matrix Composites with a Complex Relief and Nonmetal Reinforcement Phase

    Directory of Open Access Journals (Sweden)

    Daniela Spasova

    2016-02-01

    Full Text Available The present paper is relevant to the research of possibilities for the production of decorative complex relief metal matrix composites (MMCs of the “invitro” type, with unformed and unchanging reinforcement (strengthening phase in the process of creating a composite. The research on the methods of metal matrix composites development in this paper has been brought to the application of different space vacuum schemes for composite synthesisof vacuuming the space for composites synthesis by using the notion of the “capillary forming”. In this method the metal matrix (copper alloy melt was infiltrated in the space between the pellets of reinforcement phase (quartz particles – SiO2, whereas the classical method adopted for the obtaining MMCs “in vitro”, uses a mechanism of forced insertion of the reinforcement phase into the ready for use melt, followed by homogenization of the composite structure. In the particular case, because the obtained composite will have a complex relief three-dimensional surface, the conditions for compacting the building phases in the three directions x, y, z should be virtually equalized. In order to accomplish the task set, a laboratory system is developed. The experiments were conducted with laboratory equipment elaborated on the base of another equipment for "capillary forming" with extra vacuum. The structures of the obtained MMCs were tested by metallographic analysis.

  4. ECAP – New consolidation method for production of aluminium matrix composites with ceramic reinforcement

    Directory of Open Access Journals (Sweden)

    Mateja Šnajdar Musa

    2013-06-01

    Full Text Available Aluminium based metal matrix composites are rapidly developing group of materials due to their unique combination of properties that include low weight, elevated strength, improved wear and corrosion resistance and relatively good ductility. This combination of properties is a result of mixing two groups of materials with rather different properties with aluminium as ductile matrix and different oxides and carbides added as reinforcement. Al2O3, SiC and ZrO2 are the most popular choices of reinforcement material. One of the most common methods for producing this type of metal matrix composites is powder metallurgy since it has many variations and also is relatively low-cost method. Many different techniques of compacting aluminium and ceramic powders have been previously investigated. Among those techniques equal channel angular pressing (ECAP stands out due to its beneficial influence on the main problem that arises during powder compaction and that is a non-uniform distribution of reinforcement particles. This paper gives an overview on ECAP method principles, advantages and produced powder composite properties.

  5. Preliminary evaluation of adhesion strength measurement devices for ceramic/titanium matrix composite bonds

    Science.gov (United States)

    Pohlchuck, Bobby; Zeller, Mary V.

    1992-01-01

    The adhesive bond between ceramic cement and a titanium matrix composite substrate to be used in the National Aerospace Plane program is evaluated. Two commercially available adhesion testers, the Sebastian Adherence Tester and the CSEM REVETEST Scratch Tester, are evaluated to determine their suitability for quantitatively measuring adhesion strength. Various thicknesses of cements are applied to several substrates, and bond strengths are determined with both testers. The Sabastian Adherence Tester has provided limited data due to an interference from the sample mounting procedure, and has been shown to be incapable of distinguishing adhesion strength from tensile and shear properties of the cement itself. The data from the scratch tester has been found to be difficult to interpret due to the porosity and hardness of the cement. Recommendations are proposed for a more reliable adhesion test method.

  6. Tool wear during high speed turning in situ TiCp/TiBw hybrid reinforced Ti-6Al-4V matrix composite

    Directory of Open Access Journals (Sweden)

    Ge Yingfei

    2016-10-01

    Full Text Available Chipping, adhesive wear, abrasive wear and crater wear are prevalent for both the polycrystalline diamond (PCD and the carbide tools during high speed turning of TiCp/TiBw hybrid reinforced Ti-6Al-4V (TC4 matrix composite (TMCs. The combined effects of abrasive wear and diffusion wear caused the big crater on PCD and carbide tool rake face. Compared to the PCD, bigger size of crater was found on the carbide tool due to much higher cutting temperature and the violent chemical reaction between the Ti element in the workpiece and the WC in the tool. However, the marks of the abrasive wear looked much slighter or even could not be observed on the carbide tool especially when low levels of cutting parameters were used, which attributes to much lower hardness and smaller size of WC combined with more significant chemical degradation of carbide. When cutting TC4 using PCD tool, notch wear was the most significant wear pattern which was not found when cutting the TMCs. However, chipping, adhesive wear and crater wear were much milder when compared to the cutting of titanium matrix composite. Due to the absence of abrasive wear when cutting TC4, the generated titanium carbide on the PCD protected the tool from fast wear, which caused that the tool life for TC4 was 6–10 times longer than that for TMCs.

  7. Tool wear during high speed turning in situ TiCp/TiBw hybrid reinforced Ti-6Al-4V matrix composite

    Institute of Scientific and Technical Information of China (English)

    Ge Yingfei; Xu Jiuhua; Huan Haixiang

    2016-01-01

    Chipping, adhesive wear, abrasive wear and crater wear are prevalent for both the poly-crystalline diamond (PCD) and the carbide tools during high speed turning of TiCp/TiBw hybrid reinforced Ti-6Al-4V (TC4) matrix composite (TMCs). The combined effects of abrasive wear and diffusion wear caused the big crater on PCD and carbide tool rake face. Compared to the PCD, bigger size of crater was found on the carbide tool due to much higher cutting temperature and the violent chemical reaction between the Ti element in the workpiece and the WC in the tool. However, the marks of the abrasive wear looked much slighter or even could not be observed on the carbide tool especially when low levels of cutting parameters were used, which attributes to much lower hardness and smaller size of WC combined with more significant chemical degradation of car-bide. When cutting TC4 using PCD tool, notch wear was the most significant wear pattern which was not found when cutting the TMCs. However, chipping, adhesive wear and crater wear were much milder when compared to the cutting of titanium matrix composite. Due to the absence of abrasive wear when cutting TC4, the generated titanium carbide on the PCD protected the tool from fast wear, which caused that the tool life for TC4 was 6–10 times longer than that for TMCs.

  8. Sliding Wear Behavior of TiC-Reinforced Cu-4 wt.% Ni Matrix Composites

    Science.gov (United States)

    Jha, Pushkar; Gautam, R. K.; Tyagi, Rajnesh; Kumar, Devendra

    2016-10-01

    The present investigation explores the effect of TiC content on the sliding wear properties of Cu-4 wt.% Ni matrix composites. Cu-4 wt.% Ni - x wt.% TiC ( x = 0, 2, 4 and 8 wt.%) metal matrix composites were developed by powder metallurgy route. Their friction and wear was studied under dry sliding at different loads of 5, 7.5 and 10 N and constant sliding speed of 2 m/s using a pin-on-disk machine. The metallographic observations showed an almost uniform distribution of TiC particles in the matrix. Hardness of the composites increased with increasing TiC content (up to 4 wt.%). Friction and wear results of TiC-reinforced composites show better wear resistance than unreinforced matrix alloy. However, the optimum wear resistance was observed for 4 wt.% TiC-reinforced composites. Worn surfaces of specimens indicated the abrasion as the primary mechanism of wear in all the materials investigated in the study. The observed behavior has been explained on the basis of (1) the hardness which results in a decrease in real area of contact in composites containing TiC particles and (2) the formation of a transfer layer of wear debris on the surface of the composites which protects underlying substrate by inhibiting metal-metal contact.

  9. Heat-Resistance of the Powder Cobalt Alloys Reinforced by Niobium or Titanium Carbide

    Directory of Open Access Journals (Sweden)

    Cherepova, T.S.

    2016-01-01

    Full Text Available The characteristics of heat-resistance of powder cobalt alloys at 1100 °C were investigated. These alloys were developed for the protection of workers banding shelves GTE blades from wear. The alloys were prepared by hot pressing powders of cobalt, chromium, aluminum, iron and niobium or titanium carbides. The values of heat resistance alloys containing carbides between 30 and 70% (vol. depend on the type made of carbide alloys: alloys with titanium carbide superior in heat-resistant alloy of niobium carbide. The most significant factor affecting on the heat-resistant alloys, is porosity: with its increase the parameters decline regardless of the type and content of carbide. The optimum composition of powder heat resisting alloys of titanium carbide with a melting point above 1300 °C were determined for use in the aircraft engine.

  10. Simplified prediction model for elastic modulus of particulate reinforced metal matrix composites

    Institute of Scientific and Technical Information of China (English)

    WANG Wen-ming; PAN Fu-sheng; LU Yun; ZENG Su-min

    2006-01-01

    Some structural parameters of the metal matrix composite, including particulate shape and distribution do not influence the elastic modulus. A prediction model for the elastic modulus of particulate reinforced metal matrix Al composite was developed and improved. Expressions of rigidity and flexibility of the rule of mixing were proposed. A five-zone model for elasticity performance calculation of the composite was proposed. The five-zone model is thought to be able to reflect the effects of the MMC interface on elastic modulus of the composite. The model overcomes limitations of the currently-understood rigidity and flexibility of the rule of mixing. The original idea of a five-zone model is to propose particulate/interface interactive zone and matrix/interface interactive zone. By integrating organically with the law of mixing, the new model is found to be capable of predicting the engineering elastic constants of the MMC composite.

  11. Damage analysis for particle reinforced metal matrix composite by ultrasonic method

    Institute of Scientific and Technical Information of China (English)

    YANG Zhi-guo; LONG Shi-guo

    2006-01-01

    The damage characteristic of particle reinforced metal matrix composite (PMMC) was studied by ultrasonic non-destructive evaluation method. After the sample was damaged induced by tensile load,the ultrasonic wave that propagated in the sample were collected. The damage parameter was defined by ultrasonic parameter and the wave signals were analyzed by correlation method. The results show that with the increase of tensile load,the damage parameter increases and the correlation coefficient decreases. The fracture section morphologies of PMMC under tensile load were observed by SEM. It is found that there are many concaves in the metal matrix. Therefore the damage evolution can be concluded. The initial damage is induced by void nucleation,growth and subsequent coalescence in the matrix or interface separation.

  12. Comparison of residual strains measured by X-ray and neutron diffraction in a titanium (Ti-6Al-4V) matrix composite

    Energy Technology Data Exchange (ETDEWEB)

    Rangaswamy, P.; Daymond, M.; Bourke, M.A.M.; Clausen, B.; Choo, H. [Los Alamos Nat. Lab., NM (United States). Lujan Center; Prime, M.B. [ISIS, Rutherford Appleton Laboratory, Chilton, Didcot, Oxon (United Kingdom); Jayaraman, N. [Department of Materials Science and Engineering, University of Cincinnati, Cincinnati, Ohio (United States)

    1999-01-31

    This research compares matrix thermal residual strains measured in a continuous fiber reinforced SiC/Ti-6Al-4V titanium matrix composite (TMC) using X-ray and neutron diffraction with finite element predictions. The strain dependence on the strains for several reflections (105, 204, 300, 213 and 312) of the matrix were explored at the surface (X-ray) and in the bulk (neutron). To determine the longitudinal surface strains from the X-ray measurements for comparison with the neutron values, the {epsilon}{sub {phi}{psi}} versus sin{sup 2}{psi} plots were extrapolated to {psi}=90 . Continuum micro-mechanics based multi-ply finite element models (FEM) simulating rectangular and hexagonal fiber distributions were explored for calculating average surface and bulk strains. For different reflections, the experimentally determined surface measured strains ranged from +1904{+-}424 to +2974{+-}321 {mu}{epsilon} and the bulk measurements ranged from +2269{+-}421 to +3022{+-}1134 {mu}{epsilon}. These values contrast with the single valued FEM prediction of+3200 {mu}{epsilon} which was the same for both the surface and the bulk. (orig.) 24 refs.

  13. Micromechanics Fatigue Damage Analysis Modeling for Fabric Reinforced Ceramic Matrix Composites

    Science.gov (United States)

    Min, J. B.; Xue, D.; Shi, Y.

    2013-01-01

    A micromechanics analysis modeling method was developed to analyze the damage progression and fatigue failure of fabric reinforced composite structures, especially for the brittle ceramic matrix material composites. A repeating unit cell concept of fabric reinforced composites was used to represent the global composite structure. The thermal and mechanical properties of the repeating unit cell were considered as the same as those of the global composite structure. The three-phase micromechanics, the shear-lag, and the continuum fracture mechanics models were integrated with a statistical model in the repeating unit cell to predict the progressive damages and fatigue life of the composite structures. The global structure failure was defined as the loss of loading capability of the repeating unit cell, which depends on the stiffness reduction due to material slice failures and nonlinear material properties in the repeating unit cell. The present methodology is demonstrated with the analysis results evaluated through the experimental test performed with carbon fiber reinforced silicon carbide matrix plain weave composite specimens.

  14. Microstructure and hardness of WC-Co particle reinforced iron matrix surface composite

    Directory of Open Access Journals (Sweden)

    Zhang Peng

    2013-11-01

    Full Text Available In this study, a high Cr cast iron surface composite material reinforced with WC-Co particles 2-6 mm in size was prepared using a pressureless sand mold infiltration casting technique. The composition, microstructure and hardness were determined by means of energy dispersive spectrometry (EDS, electron probe microanalysis (EPMA, scanning electron microscope (SEM and Rockwell hardness measurements. It is determined that the obtained composite layer is about 15 mm thick with a WC-Co particle volumetric fraction of ~38%. During solidification, interface reaction takes place between WC-Co particles and high chromium cast iron. Melting and dissolving of prefabricated particles are also found, suggesting that local Co melting and diffusion play an important role in promoting interface metallurgical bonding. The composite layer is composed of ferrite and a series of carbides, such as (Cr, W, Fe23C6, WC, W2C, M6C and M12C. The inhomogeneous hardness in the obtained composite material shows a gradient decrease from the particle reinforced metal matrix composite layer to the matrix layer. The maximum hardness of 86.3 HRA (69.5 HRC is obtained on the particle reinforced surface, strongly indicating that the composite can be used as wear resistant material.

  15. Synthesis of Discontinously Reinforced Metal matrix Composites Using Spray Atomisation and Co injection

    Directory of Open Access Journals (Sweden)

    Enrique J. Lavernia

    1993-10-01

    Full Text Available A variety of processing techniques have evolved over the last two decades to optimize the structure and properties of particulate reinforced metal-matrix composites (MMCs. Among these, spray processes offer a unique opportunity to combine the benefits associated with fine particulate technology with in situ processing, and in some cases, near-net shape manufacturing. Spray processing generally involves mixing reinforcements and matrix under highly non-equilibrium conditions, and as a result, these processes offer the opportunity to modify the properties of existing alloy systems, and develop novel alloy compositions. In principle, such an approach will inherently avoid the extreme thermal excursions, with concomitant macrosegregation, normally associated with casting processes. Furthermore, this approach also eliminates the need to handle fine reactive particulates, normally associated with powder metallurgical processes. The present paper discusses recent developments in the area of spray atomisation and deposition processing of discontinuously reinforced MMCs, with particular emphasis on the synergism between microstructure, mechanical properties and processing.

  16. Deformation micromechanics of all-cellulose nanocomposites: comparing matrix and reinforcing components.

    Science.gov (United States)

    Pullawan, Tanittha; Wilkinson, Arthur N; Zhang, Lina N; Eichhorn, Stephen J

    2014-01-16

    All-cellulose nanocomposites, comprising two different forms of cellulose nanowhiskers dispersed in two different matrix systems, are produced. Acid hydrolysis of both tunicate (T-CNWs) and cotton cellulose (CNWs) is carried out to produce the nanowhiskers. These nanowhiskers are then dispersed in a cellulose matrix material, produced using two dissolution methods; namely lithium chloride/N,N-dimethyl acetamide (LiCl/DMAc) and sodium hydroxide/urea (NaOH/urea). Crystallinity of both nanocomposite systems increases with the addition of nanowhiskers up to a volume fraction of 15 v/v%, after which a plateau is reached. Stress-transfer mechanisms, between the matrix and the nanowhiskers in both of these nanocomposites are reported. This is achieved by following both the mechanical deformation of the materials, and by following the molecular deformation of both the nanowhiskers and matrix phases using Raman spectroscopy. In order to carry out the latter of these analyses, two spectral peaks are used which correspond to different crystal allomorphs; cellulose-I for the nanowhiskers and cellulose-II for the matrix. It is shown that composites comprising a LiCl/DMAc based matrix perform better than NaOH/urea based systems, the T-CNWs provide better reinforcement than CNWs and that an optimum loading of nanowhiskers (at 15 v/v%) is required to obtain maximum tensile strength and modulus.

  17. Modeling of stress/strain behavior of fiber-reinforced ceramic matrix composites including stress redistribution

    Science.gov (United States)

    Mital, Subodh K.; Murthy, Pappu L. N.; Chamis, Christos C.

    1994-01-01

    A computational simulation procedure is presented for nonlinear analyses which incorporates microstress redistribution due to progressive fracture in ceramic matrix composites. This procedure facilitates an accurate simulation of the stress-strain behavior of ceramic matrix composites up to failure. The nonlinearity in the material behavior is accounted for at the constituent (fiber/matrix/interphase) level. This computational procedure is a part of recent upgrades to CEMCAN (Ceramic Matrix Composite Analyzer) computer code. The fiber substructuring technique in CEMCAN is used to monitor the damage initiation and progression as the load increases. The room-temperature tensile stress-strain curves for SiC fiber reinforced reaction-bonded silicon nitride (RBSN) matrix unidirectional and angle-ply laminates are simulated and compared with experimentally observed stress-strain behavior. Comparison between the predicted stress/strain behavior and experimental stress/strain curves is good. Collectively the results demonstrate that CEMCAN computer code provides the user with an effective computational tool to simulate the behavior of ceramic matrix composites.

  18. RC beams shear-strengthened with fabric-reinforced-cementitious-matrix (FRCM) composite

    Science.gov (United States)

    Loreto, Giovanni; Babaeidarabad, Saman; Leardini, Lorenzo; Nanni, Antonio

    2015-12-01

    The interest in retrofit/rehabilitation of existing concrete structures has increased due to degradation and/or introduction of more stringent design requirements. Among the externally-bonded strengthening systems fiber-reinforced polymers is the most widely known technology. Despite its effectiveness as a material system, the presence of an organic binder has some drawbacks that could be addressed by using in its place a cementitious binder as in fabric-reinforced cementitious matrix (FRCM) systems. The purpose of this paper is to evaluate the behavior of reinforced concrete (RC) beams strengthened in shear with U-wraps made of FRCM. An extensive experimental program was undertaken in order to understand and characterize this composite when used as a strengthening system. The laboratory results demonstrate the technical viability of FRCM for shear strengthening of RC beams. Based on the experimental and analytical results, FRCM increases shear strength but not proportionally to the number of fabric plies installed. On the other hand, FRCM failure modes are related with a high consistency to the amount of external reinforcement applied. Design considerations based on the algorithms proposed by ACI guidelines are also provided.

  19. Specimen Preparation for Metal Matrix Composites with a High Volume Fraction of Reinforcing Particles for EBSD Analysis

    Science.gov (United States)

    Smirnov, A. S.; Belozerov, G. A.; Smirnova, E. O.; Konovalov, A. V.; Shveikin, V. P.; Muizemnek, O. Yu.

    2016-07-01

    The paper deals with a procedure of preparing a specimen surface for the EBSD analysis of a metal matrix composite (MMC) with a high volume fraction of reinforcing particles. Unlike standard procedures of preparing a specimen surface for the EBSD analysis, the proposed procedure is iterative with consecutive application of mechanical and electrochemical polishing. This procedure significantly improves the results of an indexed MMC matrix in comparison with the standard procedure of specimen preparation. The procedure was verified on a MMC with pure aluminum (99.8% Al) as the matrix, SiC particles being used as reinforcing elements. The average size of the SiC particles is 14 μm, and their volume fraction amounts to 50% of the total volume of the composite. It has been experimentally found that, for making the EBSD analysis of a material matrix near reinforcing particles, the difference in height between the particles and the matrix should not exceed 2 µm.

  20. Matrix free fiber reinforced polymeric composites via high-temperature high-pressure sintering

    Science.gov (United States)

    Xu, Tao

    2004-11-01

    A novel manufacturing process called high-temperature high-pressure sintering was studied and explored. Solid fiber reinforced composites are produced by consolidating and compacting layers of polymeric fabrics near their melting temperature under high pressure. There is no need to use an additional matrix as a bonding material. Partial melting and recrystallization of the fibers effectively fuse the material together. The product is called a "matrix free" fiber reinforced composite and essentially a one-polymer composite in which the fiber and the matrix have the same chemical composition. Since the matrix is eliminated in the process, it is possible to achieve a high fiber volume fraction and light weight composite. Interfacial adhesion between fibers and matrix is very good due to the molecular continuity throughout the system and the material is thermally shapeable. Plain woven Spectra RTM cloth made of SpectraRTM fiber was used to comprehensively study the process. The intrinsic properties of the material demonstrate that matrix free SpectraRTM fiber reinforced composites have the potential to make ballistic shields such as body armor and helmets. The properties and structure of the original fiber and the cloth were carefully examined. Optimization of the processing conditions started with the probing of sintering temperatures by Differential Scanning Calorimetry. Coupled with the information from structural, morphological and mechanical investigations on the samples sintered at different processing conditions, the optimal processing windows were determined to ensure that the outstanding original properties of the fibers translate into high ballistic performance of the composites. Matrix free SpectraRTM composites exhibit excellent ballistic resistance in the V50 tests conducted by the US Army. In the research, process-structure-property relationship is established and correlations between various properties and structures are understood. Thorough knowledge is

  1. Efficientcy of corrosion protection properties of epoxy resin/cashew nut shell liquid alloy reinforced with titanium dioxide

    Directory of Open Access Journals (Sweden)

    Wilaivan Loonpooht

    2014-12-01

    Full Text Available The cure behavior of epoxy resin containing cashew nut shell liquid (CNSL and corrosion protective performance of epoxy alloy reinforced with titanium dioxide (TiO2 have been investigated. According to FTIR spectra obtained from epoxy alloys, the CNSL can be employed as a curing agent. The curing process occurred when amount of CNSL was as low as 20%wt. It was found experimentally that the CNSL used for epoxy curing should not be higher than 40%wt.in order to minimize amount CNSL left after reaction. The corrosion protective performance of epoxy alloy on aluminum sheets was carried out. The results revealed that the ability of corrosion resistance increased with the amount of TiO2 introduced into the Epoxy/CNSL film investigated. In this work, the highest corrosion resistance value was found when the TiO2 concentration of 1.5 %wt was reached.

  2. Recent advances in understanding the reinforcing ability and mechanism of carbon nanotubes in ceramic matrix composites

    Science.gov (United States)

    Estili, Mehdi; Sakka, Yoshio

    2014-12-01

    Since the discovery of carbon nanotubes (CNTs), commonly referred to as ultimate reinforcement, the main purpose for fabricating CNT-ceramic matrix composites has been mainly to improve the fracture toughness and strength of the ceramic matrix materials. However, there have been many studies reporting marginal improvements or even the degradation of mechanical properties. On the other hand, those studies claiming noticeable toughening measured using indentation, which is an indirect/unreliable characterization method, have not demonstrated the responsible mechanisms applicable to the nanoscale, flexible CNTs; instead, those studies proposed those classical methods applicable to microscale fiber/whisker reinforced ceramics without showing any convincing evidence of load transfer to the CNTs. Therefore, the ability of CNTs to directly improve the macroscopic mechanical properties of structural ceramics has been strongly questioned and debated in the last ten years. In order to properly discuss the reinforcing ability (and possible mechanisms) of CNTs in a ceramic host material, there are three fundamental questions to our knowledge at both the nanoscale and macroscale levels that need to be addressed: (1) does the intrinsic load-bearing ability of CNTs change when embedded in a ceramic host matrix?; (2) when there is an intimate atomic-level interface without any chemical reaction with the matrix, could one expect any load transfer to the CNTs along with effective load bearing by them during crack propagation?; and (3) considering their nanometer-scale dimensions, flexibility and radial softness, are the CNTs able to improve the mechanical properties of the host ceramic matrix at the macroscale when individually, intimately and uniformly dispersed? If so, how? Also, what is the effect of CNT concentration in such a defect-free composite system? Here, we briefly review the recent studies addressing the above fundamental questions. In particular, we discuss the new

  3. Recent advances in understanding the reinforcing ability and mechanism of carbon nanotubes in ceramic matrix composites

    Science.gov (United States)

    Estili, Mehdi; Sakka, Yoshio

    2014-01-01

    Since the discovery of carbon nanotubes (CNTs), commonly referred to as ultimate reinforcement, the main purpose for fabricating CNT–ceramic matrix composites has been mainly to improve the fracture toughness and strength of the ceramic matrix materials. However, there have been many studies reporting marginal improvements or even the degradation of mechanical properties. On the other hand, those studies claiming noticeable toughening measured using indentation, which is an indirect/unreliable characterization method, have not demonstrated the responsible mechanisms applicable to the nanoscale, flexible CNTs; instead, those studies proposed those classical methods applicable to microscale fiber/whisker reinforced ceramics without showing any convincing evidence of load transfer to the CNTs. Therefore, the ability of CNTs to directly improve the macroscopic mechanical properties of structural ceramics has been strongly questioned and debated in the last ten years. In order to properly discuss the reinforcing ability (and possible mechanisms) of CNTs in a ceramic host material, there are three fundamental questions to our knowledge at both the nanoscale and macroscale levels that need to be addressed: (1) does the intrinsic load-bearing ability of CNTs change when embedded in a ceramic host matrix?; (2) when there is an intimate atomic-level interface without any chemical reaction with the matrix, could one expect any load transfer to the CNTs along with effective load bearing by them during crack propagation?; and (3) considering their nanometer-scale dimensions, flexibility and radial softness, are the CNTs able to improve the mechanical properties of the host ceramic matrix at the macroscale when individually, intimately and uniformly dispersed? If so, how? Also, what is the effect of CNT concentration in such a defect-free composite system? Here, we briefly review the recent studies addressing the above fundamental questions. In particular, we discuss the new

  4. Titanium

    DEFF Research Database (Denmark)

    Fage, Simon W; Muris, Joris; Jakobsen, Stig S

    2016-01-01

    Exposure to titanium (Ti) from implants and from personal care products as nanoparticles (NPs) is common. This article reviews exposure sources, ion release, skin penetration, allergenic effects, and diagnostic possibilities. We conclude that human exposure to Ti mainly derives from dental...... and medical implants, personal care products, and foods. Despite being considered to be highly biocompatible relative to other metals, Ti is released in the presence of biological fluids and tissue, especially under certain circumstances, which seem to be more likely with regard to dental implants. Although...... most of the studies reviewed have important limitations, Ti seems not to penetrate a competent skin barrier, either as pure Ti, alloy, or as Ti oxide NPs. However, there are some indications of Ti penetration through the oral mucosa. We conclude that patch testing with the available Ti preparations...

  5. Treatment of sphenoid dysplasia with a titanium-reinforced porous polyethylene implant in orbitofrontal neurofibroma: report of three cases.

    Science.gov (United States)

    Niddam, Jeremy; Bosc, Romain; Suffee, Tabrez M; Le Guerinel, Caroline; Wolkenstein, Pierre; Meningaud, Jean-Paul

    2014-12-01

    Orbital manifestations occur in less than 1% of patients with neurofibromatosis type 1 (NF1). These manifestations are frequently associated with sphenoid wing dysplasia. The typical radiologic feature is partial or total loss of the greater wing of the sphenoid bone, which leads to herniation of the temporal lobe through the orbital cavity resulting in proptosis and pulsating exophthalmos. Traditional reconstruction of this bone defect involves split bone grafting or titanium mesh. However, these techniques have some limitations due to bone resorption and infection risk. We report the use of 0.85 mm titanium-reinforced porous polyethylene implant sheet in three cases of orbital neurofibromatosis with sphenoid dysplasia. The role of this material was to create a barrier between the brain and orbital cavity. The implant sheet was modeled intraoperatively to reconstruct the orbital cavity anatomy and fitted without any screws. The malleability of the implant allows quick reconstruction of the curved orbital skeleton. Furthermore, the implant doesn't interfere with postoperative imaging and may decrease risk infection.

  6. Microstructure and Impact Wear Resistance of TiN Reinforced High Manganese Steel Matrix

    Institute of Scientific and Technical Information of China (English)

    MA You-ping; LI Xiu-lan; WANG Cheng-hui; LU Lu

    2012-01-01

    A high-manganese austenitic steel matrix (Mn13) composite reinforced with TiN ceramic particles was synthesized by means of Vacuum-Evaporation Pattern Casting (V-EPC). The composite microstructure and interface bonding of TiN/matrix were analyzed utilizing optical microscope (OM) and X-ray diffraction (XRD). The effects of different volume fraction of TiN on impact wear resistance were evaluated by MLD-10 impact wear test. The results showed that TiN was evenly distributed in composite layer and had a good interface bonding with matrix when the volume fractions of TiN were 27% and 36% respectively. However, cast defects and TiN agglomeration occurred when the TiN volume fraction increased to 48~. Compared with high-manganese austenitic steel (Mnl3), the im- pact wear resistance of the TiN-reinforced composite is better. In small impact load conditions, composite layer can effectively resist abrasives wear and TiN particles played an important role in determining impact wear resistance of composite layer. In large impact load, the synergistic roles of spalling of TiN particles and the increase of work hardening of Mn13 based material are responsible for impact wear resistance.

  7. Effect of braze processing on the microstructure and mechanical properties of SCS-6/beta21S titanium matrix composites

    Science.gov (United States)

    Hoffman, Eric K.; Bird, R. K.; Dicus, Dennis L.

    1992-01-01

    An investigation is conducted of the effects of braze processing on the microstructure and tensile properties of SiC fiber-reinforced Ti-15Mo-2.7Nb-3Al-0.25Si-matrix composite (TMC) laminates; the brazing alloy was the commercial Ti-15Cu-15Ni, in both its conventional and metglass forms. Tensile tests conducted at room temperature, 1200 F, and 1500 F showed that the braze processes (1) had little effect on tensile properties, and (2) appeared to degrade neither the reinforcing fibers not the fiber/matrix interfacial bondline.

  8. Effects of matrix porosity on the mechanical properties of fiber-reinforced oxide composites

    Science.gov (United States)

    Mattoni, Michael Anthony

    Damage tolerance in fiber-reinforced ceramic matrix composites can be achieved through weak bonding between fibers and matrix by the use of fine-scale porosity within the matrix. The effects of matrix porosity on the mechanical properties of porous-matrix, oxide composites are investigated. Porosity is systematically varied through impregnation and pyrolysis of a ceramic precursor solution, and mechanical tests are performed to identify the role of the matrix in both fiber- and matrix-dominated loadings. Two families of composites are examined in this study. The first family possesses a non-uniform porosity distribution due to precursor segregation during drying. Mechanical testing demonstrates a loss of damage tolerance and tensile strength along the fiber direction as the porosity is reduced. Concurrently some improvements in interlaminar shear strength are observed. Building upon this investigation, segregation is eliminated in subsequent studies through use of a gelation step following precursor impregnation. In this family, moderate additions of precursor-derived alumina to the matrix improve the in-plane shear and tensile strength. Concurrently, a significant increase in notch sensitivity is observed. Two theoretical frameworks are developed for the notched strength of ceramic matrix composites. The first considers composites that exhibit rising fracture resistance and is based upon established concepts of crack stability under stress-controlled loadings. The form of the resistance curve assumes that the crack tip inelastic zone is small in relation to the geometric and bridging length scales, making this framework applicable to relatively dense porous matrix composites. The results reveal salient trends in strength with notch length and specimen geometry. An assessment of the theory is made through comparison with experimental measurements. The second framework developed for notch-sensitivity explicitly accounts for large-scale inelasticity, allowing

  9. Thermal conductivity and interfacial conductance of AlN particle reinforced metal matrix composites

    Science.gov (United States)

    Kida, M.; Weber, L.; Monachon, C.; Mortensen, A.

    2011-03-01

    Aluminum nitride (AlN) particle reinforced metal-matrix-composites produced by pressure infiltration are characterized in terms of their thermal conductivity. The composites are designed to cover a wide range of phase contrast between the dispersed particles and the matrix; this is achieved by changing the matrix conductivity using Cu, Al, Sn, and Pb as the matrix. The interface thermal conductance (hc) between AlN and the matrix metals is determined by varying the size of the AlN particles using the Hasselman-Johnson approach and the differential effective medium (DEM) model to calculate hc from measured composite conductivity values. In addition, hc is measured directly at the AlN/Al interface using the transient thermoreflectance (TTR) method on thin aluminum layers deposited on flat AlN substrates to find good agreement with the value derived directly from Al/AlN composites of variable particle size and thus confirm the approach used here to measure hc. Data from the study show that hc at AlN-metal interfaces increases with the metal/AlN Debye temperature ratio; however, the increase is much less than predicted by currently accepted models.

  10. Mechanical properties study of particles reinforced aluminum matrix composites by micro-indentation experiments

    Directory of Open Access Journals (Sweden)

    Yuan Zhanwei

    2014-04-01

    Full Text Available By using instrumental micro-indentation technique, the microhardness and Young’s modulus of SiC particles reinforced aluminum matrix composites were investigated with micro-compression-tester (MCT. The micro-indentation experiments were performed with different maximum loads, and with three loading speeds of 2.231, 4.462 and 19.368 mN/s respectively. During the investigation, matrix, particle and interface were tested by micro-indentation experiments. The results exhibit that the variations of Young’s modulus and microhardness at particle, matrix and interface were highly dependent on the loading conditions (maximum load and loading speed and the locations of indentation. Micro-indentation hardness experiments of matrix show the indentation size effects, i.e. the indentation hardness decreased with the indentation depth increasing. During the analysis, the effect of loading conditions on Young’s modulus and microhardness were explained. Besides, the elastic–plastic properties of matrix were analyzed. The validity of calculated results was identified by finite element simulation. And the simulation results had been preliminarily analyzed from statistical aspect.

  11. Carbon nanotube-reinforced composites: frequency analysis theories based on the matrix stiffness

    Science.gov (United States)

    Amin, Sara Shayan; Dalir, Hamid; Farshidianfar, Anooshirvan

    2009-03-01

    Strong and versatile carbon nanotubes are finding new applications in improving conventional polymer-based fibers and films. This paper studies the influence of matrix stiffness and the intertube radial displacements on free vibration of an individual double-walled carbon nanotube (DWNT). For this, a double elastic beam model is presented for frequency analysis in a DWNT embedded in an elastic matrix. The analysis is based on both Euler-Bernoulli and Timoshenko beam theories which considers shear deformation and rotary inertia and for both concentric and non-concentric assumptions considering intertube radial displacements and the related internal degrees of freedom. New intertube resonant frequencies and the associated non-coaxial vibrational modes are calculated. Detailed results are demonstrated for the dependence of resonant frequencies and mode shapes on the matrix stiffness. The results indicate that internal radial displacement and surrounding matrix stiffness could substantially affect resonant frequencies especially for longer double-walled carbon nanotubes of larger innermost radius at higher resonant frequencies, and thus the latter does not keep the otherwise concentric structure at ultrahigh frequencies. Therefore, depending on the matrix stiffness, for carbon nanotubes reinforced composites, different analysis techniques should be used while the aspect ratio of carbon nanotubes has a little effect on the analysis theory which should be selected.

  12. Resin Matrix/Fiber Reinforced Composite Material,Ⅲ:Simulating Results

    Institute of Scientific and Technical Information of China (English)

    Li Chensha(李辰砂); Jiao Caishan; Liu Ying; Wang Zhengping; Wang Hongjie; Cao Maosheng

    2004-01-01

    According to the mathematical model which describes the curing process of composites constructed from continuous fiber-reinforced, thermosetting resin matrix prepreg materials, and the consolidation of the composite, the computer code calculates the data of the process variables of the flat-plate composites cured by a specified cure cycle, provides the variation of temperature distribution, the cure degree process, the resin variation and fibers stress inside the composite, the void variation and the residual stress distribution. The mechanism of curing process is illustrated and the cure cycle of composite material is optimized.

  13. Resin Matrix/Fiber Reinforced Composite Material, Ⅱ: Method of Solution and Computer Code

    Institute of Scientific and Technical Information of China (English)

    Li Chensha(李辰砂); Jiao Caishan; Liu Ying; Wang Zhengping; Wang Hongjie; Cao Maosheng

    2003-01-01

    According to a mathematical model which describes the curing process of composites constructed from continuous fiber-reinforced, thermosetting resin matrix prepreg materials, and the consolidation of the composites, the solution method to the model is made and a computer code is developed, which for flat-plate composites cured by a specified cure cycle, provides the variation of temperature distribution, the cure reaction process in the resin, the resin flow and fibers stress inside the composite, the void variation and the residual stress distribution.

  14. PREDICTION OF MECHANICAL PROPERTY OF WHISKER REINFORCED METAL MATRIX COMPOSITE: PART-Ⅰ. MODEL AND FORMULATION

    Institute of Scientific and Technical Information of China (English)

    2000-01-01

    Based on study of strain distribution in whisker reinforced metal matrix composites, an explicit precise stiffness tensor is derived. In the present theory, the effect of whisker orientation on the macro property of composites is considered, but the effect of random whisker position and the complicated strain field at whisker ends are averaged. The derived formula is able to predict the stiffness modulus of composites with arbitrary whisker orientation under any loading condition. Compared with the models of micro-mechanics, the present theory is competent for modulus prediction of actual engineering composites. The verification and application of the present theory are given in a subsequent paper published in the same issue.

  15. An Investigation of Laser Assisted Machining of Al_2O_3 Particle Reinforced Aluminum Matrix Composite

    Institute of Scientific and Technical Information of China (English)

    2002-01-01

    The Al 2O 3 particles reinforced aluminum matrix composite (Al 2O 3p/Al) are more and more widely used for their excellent physical and chemical properties. However, their poor machinability leads to severe tool wear and bad machined surface. In this paper laser assisted machining is adopted in machining Al 2O 3p/Al composite and good result was obtained. The result of experiment shows in machining Al 2O 3p/Al composites the cutting force is reduced in 30%~50%, the tool wear is reduced in 20%~30% an...

  16. Simplification and improvement of prediction model for elastic modulus of particulate reinforced metal matrix composite

    Institute of Scientific and Technical Information of China (English)

    WANG Wen-ming; PAN Fu-sheng; LU Yun; ZENG Su-min

    2006-01-01

    In this paper, we proposed a five-zone model to predict the elastic modulus of particulate reinforced metal matrix composite. We simplified the calculation by ignoring structural parameters including particulate shape, arrangement pattern and dimensional variance mode which have no obvious influence on the elastic modulus of a composite, and improved the precision of the method by stressing the interaction of interfaces with pariculates and maxtrix of the composite. The five- zone model can reflect effects of interface modulus on elastic modulus of composite. It overcomes limitations of expressions of rigidity mixed law and flexibility mixed law. The original idea of five zone model is to put forward the particulate/interface interactive zone and matrix/interface interactive zone. By organically integrating the rigidity mixed law and flexibility mixed law,the model can predict the engineering elastic constant of a composite effectively.

  17. Dry Sliding Friction and Wear Studies of Fly Ash Reinforced AA-6351 Metal Matrix Composites

    Directory of Open Access Journals (Sweden)

    M. Uthayakumar

    2013-01-01

    Full Text Available Fly ash particles are potentially used in metal matrix composites due to their low cost, low density, and availability in large quantities as waste by-products in thermal power plants. This study describes multifactor-based experiments that were applied to research and investigation on dry sliding wear system of stir-cast aluminum alloy 6351 with 5, 10, and 15 wt.% fly ash reinforced metal matrix composites (MMCs. The effects of parameters such as load, sliding speed, and percentage of fly ash on the sliding wear, specific wear rate, and friction coefficient were analyzed using Grey relational analysis on a pin-on-disc machine. Analysis of variance (ANOVA was also employed to investigate which design parameters significantly affect the wear behavior of the composite. The results showed that the applied load exerted the greatest effect on the dry sliding wear followed by the sliding velocity.

  18. An analytical model for particulate reinforced composites (PRCs) taking account of particle debonding and matrix cracking

    Science.gov (United States)

    Jiang, Yunpeng

    2016-10-01

    In this work, a simple micromechanics-based model was developed to describe the overall stress-strain relations of particulate reinforced composites (PRCs), taking into account both particle debonding and matrix cracking damage. Based on the secant homogenization frame, the effective compliance tensor could be firstly given for the perfect composites without any damage. The progressive interface debonding damage is controlled by a Weibull probability function, and then the volume fraction of detached particles is involved in the equivalent compliance tensor to account for the impact of particle debonding. The matrix cracking was introduced in the present model to embody the stress softening stage in the deformation of PRCs. The analytical model was firstly verified by comparing with the corresponding experiment, and then parameter analyses were conducted. This modeling will shed some light on optimizing the microstructures in effectively improving the mechanical behaviors of PRCs.

  19. Preparation and properties of Cu matrix composite reinforced by carbon nanotubes

    Institute of Scientific and Technical Information of China (English)

    CHEN Xiao-hua; LI Wen-hua; CHEN Chuan-sheng; XU Long-shan; YANG Zhi; HU Jing

    2005-01-01

    Cu matrix composites reinforced by carbon nanotubes(CNTs) were prepared. The effect of carbon nanotubes on mechanical and tribological properties of the Cu matrix composites were investigated. The chemical method for coating CNTs was reported. The morphology of the fracture surfaces and worn surface were examined by SEM.The results show that Cu/coated-CNTs composites have higher hardness, much better wear resistance and antifriction properties than those of the reference Cu alloy (Cu-10Sn) and Cu/uncoated-CNTs composite sintered under the same conditions. The optimal mechanical properties of the composites occurred at 2. 25% (mass fraction) of CNTs. The excellent wear resistance and anti-friction properties are attributed to the fiber strengthening effect of CNTs and the effect of the spherical wear debris containing carbon nanotubes on the tribo-surface.

  20. Electroless plating Ni-P matrix composite coating reinforced by carbon nanotubes

    Institute of Scientific and Technical Information of China (English)

    邓福铭; 陈小华; 陈卫祥; 李文铸

    2004-01-01

    Ni-P matrix composite coating reinforced by carbon nanotubes (CNTs) was deposited by electroless plating. The most important factors that influence the content of carbon nanotubes in deposits, such as agitation, surfactant and carbon nanotubes concentration in the plating bath were investigated. The surface morphology, structure and properties of the Ni-P-CNTs coating were examined. It is found that the maximum content of carbon nanotubes in the deposits is independent of carbon nanotubes concentration in the plating bath when it is up to 5 mg/L. The test results show that the carbon nanotubes co-deposited do not change the structure of the Ni-P matrix of the composite coating, but greatly increase the hardness and wear resistance and decrease the friction coefficient of the Ni-PCNTs composite coating with increasing content of carbon nanotubes in deposits.

  1. Vacuum brazing of high volume fraction SiC particles reinforced aluminum matrix composites

    Science.gov (United States)

    Cheng, Dongfeng; Niu, Jitai; Gao, Zeng; Wang, Peng

    2015-03-01

    This experiment chooses A356 aluminum matrix composites containing 55% SiC particle reinforcing phase as the parent metal and Al-Si-Cu-Zn-Ni alloy metal as the filler metal. The brazing process is carried out in vacuum brazing furnace at the temperature of 550°C and 560°C for 3 min, respectively. The interfacial microstructures and fracture surfaces are investigated by scanning electron microscopy (SEM), transmission electron microscopy (TEM) and energy spectrum analysis (EDS). The result shows that adequacy of element diffusion are superior when brazing at 560°C, because of higher activity and liquidity. Dislocations and twins are observed at the interface between filler and composite due to the different expansion coefficient of the aluminum alloy matrix and SiC particles. The fracture analysis shows that the brittle fracture mainly located at interface of filler and composites.

  2. 碳涂层对SiC纤维增强钛基复合材料界面显微结构及性能的影响%Interface microstructure and properties of SiC fiber coated with carbon reinforced titanium matrix composites

    Institute of Scientific and Technical Information of China (English)

    贾燕翔; 李久明; 刘祥辉; 刘利军

    2012-01-01

    研究涂碳的SiC(C)/Ti-6Al-4V和无涂碳的SiC/Ti-6Al-4V材料的界面结构以及结合强度.结果表明:碳涂层阻止了径向纤维间的相互作用,该涂层界面反应物只是TiC,这些产物包含邻近碳涂层生成的细小晶粒和邻近金属基体生成的粗大晶粒;在无涂碳界面上,相邻纤维一侧产生的是TiC薄层,毗邻金属基体产生的是TiC和Ti5Si3晶粒组成的厚混合物,晶粒的大小从纤维到基体逐渐增大.涂炭和无涂碳复合材料的界面结合强度分别是(118.2±4.24),(230±6.28) MPa,证明碳涂层在纤维和基体之间提供了一个弱结合界面.涂碳纤维复合材料的界面结合发生在涂碳层和反应层之间,而无涂碳发生在纤维和反应层之间.%Interface microstructure and bonding strength of SiC (C)/Ti-6A1-4V and SiC/Ti - 6A1 - 4V material were compared. Carbon coating prevents radial fiber interactions, and the product of SiC(C)/Ti-6Al-4V interfacial reaction is TiC, the product contains fine crystal grain formed near carbon coating and coarse grain generated near metal matrix. At the interface of SiC/Ti-6Al -4V material, TiC layer is formed at fiber side, thick mixture containing TiC and Ti5Si3 grains is produced near metal matrix. Grain size increases gradually from fiber to substrate interfacial bonding strength of SiC (C) Ti - 6A1 - 4V and SiC/Ti - 6A1 - 4V composites is (11.8 + 4.24) and (230 + 6.28) Mpa, respectively. Interface bonding of coated carbon fiber composite material occurs in the coated carbon layer and reaction layer, the interfacial combination of uncoated fiber composite is between fiber and reaction layer.

  3. Simulation of the strain rate sensitive flow behavior of SiC-particulate reinforced aluminum metal matrix composites

    OpenAIRE

    Tirtom, İsmail; Güden, Mustafa; Yıldız, Hasan

    2008-01-01

    Strain rate dependent compression mechanical behavior of an SiC-particulate reinforced Al (2024-O) metal matrix composite (MMC) with different particle volume fractions was numerically investigated at various strain rates. Calculations were performed using axisymmetric finite element unit cell model, in which an elastic SiC particle was embedded inside a strain rate sensitive viscoplastic Al matrix. Stress–strain curves of Al matrix material were derived from Split Hopkinson Pressure Bar expe...

  4. Structural and thermophysical properties characterization of continuously reinforced cast Al matrix composite

    Directory of Open Access Journals (Sweden)

    Brian Gordon

    2010-11-01

    Full Text Available In this work the process of manufacturing a continuously reinforced cast Al matrix composite and its properties are presented. The described technology permits obtaining a structural material of competitive properties compared to either heat treatable aluminum alloys or polymer composites for several types of applications. The examined thermophysical properties and structural characterization, including material anisotropy, coupled with the results of previous measurements of the mechanical properties of both Al2O3 reinforcing filaments and metallic prepregs have proven the high quality of this material and the possibility of its operation under special loading modes and environmental conditions. Microscopic examinations (LM, SEM were carried out to reveal the range of morphological homogeneity of the microstructure, the anisotropy of the filament band distribution, and simultaneously the adhesive behavior of the metal/fiber interface. The 3D morphology of the chosen microstructure components was revealed by computed tomography. The obtained results indicate that special properties of the examined prepreg materials have been strongly influenced, on the one hand, by the geometry of its internal microstructure, i.e. spatial distribution and volume fraction of the Al2O3 reinforcing filaments and, on the other hand, by a very good compatibility obtained between the individual metal prepreg components.

  5. Wear Behavior of the Lead-Free Tin Bronze Matrix Composite Reinforced by Carbon Nanotubes

    Science.gov (United States)

    Zeng, Jun; Fan, Huiqing; Wang, Yangli; Zhang, Siquan

    2011-12-01

    Copper-coated carbon nanotubes were prepared by the electroless plating route. The structure and component of copper/carbon tubes were characterized using a transmission electron microscope and energy dispersive spectrometer. The results show that the surface of the carbon tubes was covered by the copper particles. Copper/carbon tubes were used as the substitute of part of tin and all of lead in the tin bronze matrix, and the tribological properties of carbon nanotube-reinforced Cu-4 wt pct Sn-6 wt pct Zn composites were studied. The effects of the carbon nanotube volume fraction and sliding distance in unlubricated ball-on-disc wear test were investigated. The 3 vol pct carbon nanotube-reinforced Cu-4 wt pct Sn-6 wt pct Zn composite shows the Vickers hardness of 126.9, which is approximately 1.6 times higher than that of Cu-6 wt pct Sn-6 wt pct Zn-3 wt pct Pb tin bronze. The wear rate and average friction coefficients of 3 vol pct carbon nanotube-reinforced Cu-4 wt pct Sn-6 wt pct Zn composite were lower than those of the Cu-6 wt pct Sn-6 wt pct Zn-3 wt pct Pb tin bronze, respectively.

  6. Effects of heat treatment on mechanical properties and microstructure of tungsten fi ber reinforced grey cast iron matrix composites

    Directory of Open Access Journals (Sweden)

    Peng jianHong

    2009-11-01

    Full Text Available In this study, grey cast iron matrix composites reinforced by different volume fractions of tungsten fibers (Vr = 0.95 %, 1.90 %, 2.85 %, 3.80 % were investigated in as-cast and under the heat treatment temperatures of 1,000℃ and 1,100℃. The microstructure and mechanical properties of the composites were analyzed and tested by means of SEM, micro-hardness tester and three-point bend testing. The results show that with increasing of the volume fraction of tungsten fibers, the composites reinforced by the tungsten fiber have higher fl exural strength and modulus than that of cast iron without reinforcement, and the fl exural strength increases with the increasing of heat treatment temperatures. Due to diffusion reaction between matrix and reinforcing phases, the process of heat treatment, the number of graphite fl akes in the matrix seemingly becomes lower; and some hard carbide particles are formed around the residual tungsten fi bers. Not only does the hardness of both matrix and reinforcement change tremendously, but also the region of reinforcement is also extended from the original 0.11 mm to 0.19 mm in radius.

  7. Electrical response and functionality of polymer matrix-titanium carbide composites

    Directory of Open Access Journals (Sweden)

    2010-04-01

    Full Text Available The dielectric response and conductivity of polymer matrix-titanium carbide composites was examined by means of Broadband Dielectric Spectroscopy in the frequency range of 10–1–107 Hz and over the temperature range of 40–150°C, varying the filler content. Dielectric data were analyzed via the electric modulus formalism. Recorded relaxations were attributed to interfacial polarization, glass to rubber transition and local motions of polar side groups. Alternating current conductivity varies up to seven orders of magnitude with both frequency and temperature. Direct current conductivity increases with temperature, although the rate of its alteration does not remain constant in the examined temperature range. In the low temperature region (up to 60°C increases at a higher rate, while right afterwards approaches rather constant values. Finally, in the high temperature range (above 90°C conductivity raises again but at a lower rate. This behaviour adds functionality to the composites’ performance and could be exploited in developing self-current regulators.

  8. Jet Electrochemical Machining of Particle Reinforced Aluminum Matrix Composites with Different Neutral Electrolytes

    Science.gov (United States)

    Hackert-Oschätzchen, M.; Lehnert, N.; Martin, A.; Schubert, A.

    2016-03-01

    Conventional mechanical machining of particle reinforced aluminum matrix composites (AMCs) is challenging because the hard ceramic particles in the soft aluminum matrix lead to an increased tool wear. Furthermore, the mechanical and thermal impact during conventional machining affects the microstructure of the AMCs. Electrochemical machining (ECM) is an alternative method to machine AMCs. Based on anodic dissolution, ECM has a slight influence on the work piece material structure and is independent of material strength and hardness. So the microstructure of the work piece remains unaffected. One method of ECM is electrochemical machining with continuous electrolytic free jet (Jet-ECM). Hereby the electrochemical removal is localized by the geometry of the electrolyte jet. By moving the electrolyte jet micro-structures and microgeometries can be generated quickly and flexibly in metallic parts [1]. Another advantage of Jet-ECM is the low consumption of electrolyte which allows an easy and inexpensive change of electrolyte for investigations with different types of electrolyte. In this study AMCs reinforced with different amounts of SiC-particles are machined with two pH-neutral electrolytes using Jet-ECM. The results provide information about the suitability of the selected electrolytes for the machining of AMCs. In addition, the influence of the particle content on the electrochemical removal result will be evaluated.

  9. Processing and Material Characterization of Continuous Basalt Fiber Reinforced Ceramic Matrix Composites Using Polymer Derived Ceramics.

    Science.gov (United States)

    Cox, Sarah B.

    2014-01-01

    The need for high performance vehicles in the aerospace industry requires materials which can withstand high loads and high temperatures. New developments in launch pads and infrastructure must also be made to handle this intense environment with lightweight, reusable, structural materials. By using more functional materials, better performance can be seen in the launch environment, and launch vehicle designs which have not been previously used can be considered. The development of high temperature structural composite materials has been very limited due to the high cost of the materials and the processing needed. Polymer matrix composites can be used for temperatures up to 260C. Ceramics can take much higher temperatures, but they are difficult to produce and form in bulk volumes. Polymer Derived Ceramics (PDCs) begin as a polymer matrix, allowing a shape to be formed and cured and then to be pyrolized in order to obtain a ceramic with the associated thermal and mechanical properties. The use of basalt in structural and high temperature applications has been under development for over 50 years, yet there has been little published research on the incorporation of basalt fibers as a reinforcement in the composites. In this study, continuous basalt fiber reinforced PDCs have been fabricated and tested for the applicability of this composite system as a high temperature structural composite material. The oxyacetylene torch testing and three point bend testing have been performed on test panels and the test results are presented.

  10. Micromechanics and Structural Response of Functionally Graded, Particulate-Matrix, Fiber-Reinforced Composites.

    Science.gov (United States)

    Genin, Guy M; Birman, Victor

    2009-05-15

    Reinforcement of fibrous composites by stiff particles embedded in the matrix offers the potential for simple, economical functional grading, enhanced response to mechanical loads, and improved functioning at high temperatures. Here, we consider laminated plates made of such a material, with spherical reinforcement tailored by layer. The moduli for this material lie within relatively narrow bounds. Two separate moduli estimates are considered: a "two-step" approach in which fibers are embedded in a homogenized particulate matrix, and the Kanaun-Jeulin (2001) approach, which we re-derive in a simple way using the Benveniste (1988) method. Optimal tailoring of a plate is explored, and functional grading is shown to improve the performance of the structures considered. In the example of a square, simply supported, cross-ply laminated panel subjected to uniform transverse pressure, a modest functional grading offers significant improvement in performance. A second example suggests superior blast resistance of the panel achieved at the expense of only a small increase in weight.

  11. Process for the manufacture of seamless metal-clad fiber-reinforced organic matrix composite structures

    Science.gov (United States)

    Bluck, Raymond M. (Inventor); Bush, Harold G. (Inventor); Johnson, Robert R. (Inventor)

    1991-01-01

    A process for producing seamless metal-clad composite structures includes providing a hollow, metallic inner member and an outer sleeve to surround the inner member and define an inner space therebetween. A plurality of continuous reinforcing fibers is attached to the distal end of the outside diameter of the inner member, and the inner member is then introduced, distal end first, into one end of the outer sleeve. The inner member is then moved, distal end first, into the outer sleeve until the inner member is completely enveloped by the outer sleeve. A liquid matrix material is then injected into the space containing the reinforcing fibers between the inner member and the outer sleeve. Next a pressurized heat transfer medium is passed through the inner member to cure the liquid matrix material. Finally, the wall thickness of both the inner member and the outer sleeve are reduced to desired dimensions by chemical etching, which adjusts the thermal expansion coefficient of the metal-clad composite structure to a desired value.

  12. Structure evolutions in a Ti–6Al–4V matrix composite reinforced with TiB, characterised using high energy X-ray diffraction

    Energy Technology Data Exchange (ETDEWEB)

    Ropars, Ludovic, E-mail: ludovic.ropars@airbus.com [Airbus Group SAS, Airbus Group Innovations, 12 rue Pasteur, BP-76, 92152 Suresnes Cedex (France); Institut Jean Lamour (IJL), SI2M Dpt., CNRS UMR 7198, Université de Lorraine, Parc de Saurupt, CS 50840, F-54011 Nancy Cedex (France); Dehmas, Moukrane, E-mail: ismoukrane.dehmas@univlorraine.fr [Institut Jean Lamour (IJL), SI2M Dpt., CNRS UMR 7198, Université de Lorraine, Parc de Saurupt, CS 50840, F-54011 Nancy Cedex (France); Laboratory of Excellence for Design of Alloy Metals for Low-mass Structures (‘DAMAS’ Labex), Université de Lorraine (France); Gourdet, Sophie; Delfosse, Jérôme [Airbus Group SAS, Airbus Group Innovations, 12 rue Pasteur, BP-76, 92152 Suresnes Cedex (France); Tricker, David [Materion AMC, RAE Road, Farnborough, Hampshire GU14 6XE (United Kingdom); Aeby-Gautier, Elisabeth [Institut Jean Lamour (IJL), SI2M Dpt., CNRS UMR 7198, Université de Lorraine, Parc de Saurupt, CS 50840, F-54011 Nancy Cedex (France); Laboratory of Excellence for Design of Alloy Metals for Low-mass Structures (‘DAMAS’ Labex), Université de Lorraine (France)

    2015-03-05

    Highlights: • In-situ high energy X-ray diffraction used during different thermal treatments. • Kinetics of phase evolutions characterised for the matrix and for the borides. • Conversion from TiB{sub 2} to TiB-B27 via a metastable structure TiB-B{sub f}. • Strong effect of the process on the matrix phases evolutions and microstructure. - Abstract: A titanium matrix composite reinforced with TiB was produced using powder metallurgy. A Ti–6Al–4V alloy was chosen to be the matrix, and 12 wt.% of TiB{sub 2} was used as the boron source for the solid state formation of TiB. The TiB{sub 2} to TiB conversion reaction was studied using an in situ high energy X-ray diffraction technique while heat treating the composite. The TiB{sub 2} (space group: P6/mmm) converts into TiB-B27 (Pnma), via TiB-B{sub f} (Cmcm). The metastable character of B{sub f} is confirmed here; it is the first phase formed during the conversion and it progressively converts into B27 during elevated temperature heat treatment. A modification of the phase transformation kinetics in the matrix and of the composite β transus temperature (T{sub β} = 1275 °C) was also observed, mainly due to gas contamination and intensive work hardening as a result of the mechanical alloying process used to manufacture the material and to a modification of the matrix equilibria.

  13. Development of microstructure in submicron particles reinforced magnesium matrix composite processed by room temperature deformation

    Energy Technology Data Exchange (ETDEWEB)

    Nie, K.B., E-mail: kaibo.nie@gmail.com [College of Materials Science and Engineering, Taiyuan University of Technology, Taiyuan 030024 (China); Deng, K.K., E-mail: jamsdk@163.com [College of Materials Science and Engineering, Taiyuan University of Technology, Taiyuan 030024 (China); Xu, F.J. [College of Materials Science and Engineering, Taiyuan University of Technology, Taiyuan 030024 (China); Wang, X.J.; Wu, K. [School of Materials Science and Engineering, Harbin Institute of Technology, Harbin 150001 (China)

    2015-01-15

    Magnesium matrix composite reinforced with submicron SiC particles was subjected to room temperature deformation. A stepped tensile method was adopted to observe the development of microstructure at different tensile strain state. The microstructure evolution determined by transmission electron microscopy showed that the existence of submicron SiC particles could promote dislocation multiplication as well as impede dislocation motion. Dislocation density around SiC particles increased with the increase of tensile strain. Compared with the matrix alloy, the composite could withstand greater external loads, which can be related to the pinning effect caused by the submicron SiC particles on the movement of grain and twin boundaries. The study of the interface between the submicron SiC particles and matrix in the composite suggested that single submicron SiC particle bonded well with the matrix alloy after tensile process. Initiation of micro-cracks usually generated in the submicron particle dense zone during tensile process, which could lead to the fracture of composite. - Highlights: • Interaction among SiCp, dislocations, grain boundaries and twinning is analyzed. • Microstructures of SiCp/AZ91 during tensile is characterized. • 0.2 μm SiCp has significant pinning effect on dislocation movement. • Interfacial bonding between 0.2 μm SiCp-Mg is analyzed.

  14. PARTICULATE SIZE EFFECTS IN THE PARTICLE-REINFORCED METAL-MATRIX COMPOSITES

    Institute of Scientific and Technical Information of China (English)

    魏悦广

    2001-01-01

    The influences of particle size on the mechanical properties of the particulate metal matrix composite are obviously displayed in the experimental observations. However, the phenomenon can not be predicted directly using the conventional elastic-plastic theory. It is because that no length scale parameters are involved in the conventional theory. In the present research, using the strain gradient plasticity theory, a systematic research of the particle size effect in the particulate metal matrix composite is carried out. The roles of many composite factors, such as: the particle size, the Young's modulus of the particle, the particle aspect ratio and volume fraction, as well as the plastic strain hardening exponent of the matrix material,are studied in detail. In order to obtain a general understanding for the composite behavior, two kinds of particle shapes, ellipsoid and cylinder, are considered to check the strength dependence of the smooth or non-smooth particle surface. Finally,the prediction results will be applied to the several experiments about the ceramic particle-reinforced metal-matrix composites. The material length scale parameter is predicted.

  15. Influence of titanium diboride reinforcements on the microstructure, mechanical properties and fracture behavior of cast zinc-aluminum composites

    Science.gov (United States)

    Dionne, Sylvie

    The objective of the present study was to examine the relationships between the microstructure, mechanical properties and failure mechanisms which control the performance of TiB2 particle reinforced Zn-8 wt.% Al (ZA-8) composites. Unreinforced ZA-8 and four composite heats with nominal particle contents of 5, 10, 20 and 30 vol.% were prepared using stir casting and permanent mold casting techniques. Tensile, compression, Charpy impact and short bar chevron-notch fracture toughness tests were conducted at room temperature. The microstructure and fracture surfaces of the specimens were characterized using optical, scanning electron, transmission electron and focused ion beam microscopy. These experimental results were compared with relevant MMC models and with published data on Zn-based composites. The TiB2/ZA-8 composites had a homogeneous distribution of particles in a matrix similar to unreinforced ZA-8. The matrix grain size decreased as the TiB2 content increased. No interfacial reaction products were detected. A good correlation was obtained between the measured composite stiffness and the values predicted using an Eshelby model. The yield strength and work hardening rate of TiB2/ZA-8 were only marginally higher than those of unreinforced ZA-8. The strength properties did not increase with the particle content as predicted by the Eshelby model. The premature activation of relaxation processes limited the extent to which particle reinforcement improved the strength of the ZA-8 matrix. Temperature-activated relaxation processes such as diffusion and dislocation motion can occur readily in ZA-8 at room temperature, which corresponds to 0.44 TM. Particle reinforcement of the ZA-8 alloy produced a degradation of the toughness which was sensitive to the loading rate. The Charpy energy of TiB 2/ZA-8 was up to 85% smaller than that of ZA-8, while the corresponding loss in fracture toughness was only 15%. The moderate fracture toughness decrease was explained by the

  16. Development of a new aluminium matrix composite reinforced with iron oxide (Fe3O4

    Directory of Open Access Journals (Sweden)

    E. Bayraktar

    2010-01-01

    Full Text Available Purpose: of this paper is to develop new aluminium matrix (intermetallic composites reinforced with iron oxide (Fe3O4 that will be used in aeronautical engineering or in electronic industry. Different parameters such as sintering time and temperature, reinforcement, compact pressure were evaluated. The final purpose of this project is going on to improve conductivity and magnetic permeability of this new composite.Design/methodology/approach: In this paper, a new alternative materials “aluminium–iron oxide (Fe3O4, naturally as the mineral magnetite powder composite” has been developed by using a microwave (in the laboratory scale sintering programme with various aspect ratios, that iron oxide (Fe3O4 particle sizes and aluminium powders together were prepared. This paper contains partially preliminary results of our going-on research project.Findings: Green density increased regularly depending on the compact pressure and percentage of the iron oxide (Fe3O4. Micro and macro porosity was not found due to very clean microwave sintering. Density after microwave sintering was higher than that of traditional sintering in an electrical oven.Research limitations/implications: This project is going on and magnetic permeability and conductivity of this composite will be improved.Practical implications: This composite is new and clean and thanks to the new microwave sintering basically will be used in aeronautical engineering. Microwave heating results in lower energy costs and decreased processing times for many industrial processes.Originality/value: Originality of this paper is to use a new reinforcement in the aluminium matrix composite; Fe3O4-iron oxide. A new method - microwave sintering- has been carried out on this composite.

  17. EFFECT OF REINFORCEMENT ALIGNMENT ON THE PROPERTIES OF POLYMER MATRIX COMPOSITE

    Directory of Open Access Journals (Sweden)

    M. R. Aeyzarq Muhammad Hadzreel

    2013-06-01

    Full Text Available EFFECT OF REINFORCEMENT ALIGNMENT ON THE PROPERTIES OF POLYMER MATRIX COMPOSITE M. R. Aeyzarq Muhammad Hadzreel1,a and I. Siti Rabiatull Aisha1,b 1Faculty of Mechanical Engineering, University Malaysia Pahang, 26600 Pekan, Pahang MalaysiaEmail: aaeyzarq89@gmail.com, brabiatull@ump.edu.myABSTRACTNumerous applications have been proposed and demonstrated for aligned-fiber composites. However, none had stated a correct procedure for aligning the fibers to optimize the properties of the polymer matrix composite (PMC, such as its strength and water absorption properties. Therefore, the aim of this study is to determine the best alignment of reinforcement material in order to optimize the properties of PMC. Woven roving fiberglass was used as the fiber and unsaturated polyester resin as its matrix material. A hand lay-up process was used to fabricate the laminated composite. The specimens were divided into four major categories with different alignments and thicknesses of fiber and matrix, which were five-layer bidirectional, five-layer multidirectional, seven-layer bidirectional, and seven-layer multidirectional. Tensile tests showed that bidirectional alignment offered better mechanical properties compared with the multidirectional alignment. The five-layer bidirectional arrangement has a higher tensile strength compared with five-layer multidirectional arrangement. The seven-layer bidirectional arrangement has higher tensile strength compared with the seven-layer multidirectional arrangement. The modulus of elasticity of the bidirectional alignment was higher than that of the multidirectional alignment. Bidirectional alignment was better because the external tensile load was distributed equally on all the fibers and transmitted along the axes of the fibers. Whereas in the case of multidirectional alignment, the fiber axes were non-parallel to the load axis, resulting in off-axis pulling on the fibers and increased stress concentration, which caused

  18. Characterization of aluminium matrix composites reinforced by Al–Cu–Fe quasicrystalline particles

    Energy Technology Data Exchange (ETDEWEB)

    Lityńska-Dobrzyńska, L.; Dutkiewicz, J.; Stan-Głowińska, K.; Wajda, W. [Institute of Metallurgy and Materials Science Polish Academy of Sciences, 30-059 Kraków, 25 Reymonta St. (Poland); Dembinski, L.; Langlade, C.; Coddet, C. [Universite de Technologie de Belfort-Montbeliard, Site de Sevenans 90010, Belfort (France)

    2015-09-15

    Highlights: • Al powder and atomised Al{sub 65}Cu{sub 20}Fe{sub 15} powder were consolidated by vacuum hot pressing. • No changes in microstructure of Al{sub 65}Cu{sub 20}Fe{sub 15} powder in 20% and 40% composites. • Al{sub 2}Cu precipitates at the interfaces and inside the matrix in the 60% composite. • Increase of microhardness and compressive strength with content of reinforcement. • The friction coefficient were in the range 0.5–0.7. - Abstract: Aluminium matrix composites were consolidated from elemental Al powder and atomised Al{sub 65}Cu{sub 20}Fe{sub 15} particles by vacuum hot pressing technique. The spherical Al{sub 65}Cu{sub 20}Fe{sub 15} particles consisted of icosahedral quasicrystalline dendrites or cells and cubic τ-AlCu(Fe) phase located in interdendritic areas. The composites with different content of the reinforcement particles (20, 40 and 60 wt%) were prepared. All composites showed density about 99% and a good bonding between the Al{sub 65}Cu{sub 20}Fe{sub 15} particles and the matrix. It was shown that the phase composition of the atomised particles did not change after consolidation for the composite containing 20% and 40% added particles while Al{sub 2}Cu precipitates formed at the Al/Al{sub 65}Cu{sub 20}Fe{sub 15} interfaces and inside the matrix in the composite with 60% of Al{sub 65}Cu{sub 20}Fe{sub 15} particles. With the increase of the volume fraction of the reinforcement in the composite the hardness as well as compressive strength increased reaching the value of 173 HV{sub 0.5} and 370 MPa, respectively for 60% of Al{sub 65}Cu{sub 20}Fe{sub 15} particles. The friction coefficient slightly varied in the range 0.5–0.7 depending on the composition.

  19. Three-point bending test comparison of fiber-reinforced composite archwires to nickel-titanium archwires.

    Science.gov (United States)

    Ballard, Richard W; Sarkar, Nikhil K; Irby, Merrell C; Armbruster, Paul C; Berzins, David W

    2012-01-01

    Various alternatives to metal orthodontic archwires have produced varied successes over the years. This study sought to evaluate the bending properties of fiber-reinforced polymeric composite (FRC) archwires compared with similarly sized nickel-titanium (Ni-Ti) archwires. Two different 0.018-inch translucent FRC orthodontic wires (Translucent Archwire I and Translucent Archwire II) were tested against 0.014-, 0.016-, and 0.018-inch nonsuperelastic nickel titanium orthodontic wires. The wires in each group (n = 10) were evaluated with three-point bending using a universal testing machine. Wire segments were deflected at midspan to 3.1 mm at a rate of 2 mm/min. Loading and unloading slope and modulus were calculated, as were force values during activation and deactivation and elastic recovery. It was found that the 0.018-inch Ni-Ti archwire demonstrated the highest force values at different deflection distances followed by Translucent Archwire II, 0.016-inch Ni-Ti, Translucent Archwire I, and finally 0.014-inch Ni-Ti. 0.016-inch Ni-Ti exhibited the highest modulus value, followed by 0.018-inch Ni-Ti, 0.014-inch Ni-Ti, Translucent Archwire II, and finally Translucent Archwire I. During deactivation, the elastic recovery of 0.014-inch Ni-Ti and 0.016-inch Ni-Ti was significantly greater than Translucent Archwire II. The bending properties of BioMer's FRC archwires were found to be comparable to Ni-Ti, as advertised by the manufacturer.

  20. Dynamic tensile deformation behavior of Zr-based amorphous alloy matrix composites reinforced with tungsten or tantalum fibers

    Science.gov (United States)

    Lee, Hyungsoo; Kim, Gyeong Su; Jeon, Changwoo; Sohn, Seok Su; Lee, Sang-Bok; Lee, Sang-Kwan; Kim, Hyoung Seop; Lee, Sunghak

    2016-07-01

    Zr-based amorphous alloy matrix composites reinforced with tungsten (W) or tantalum (Ta) continuous fibers were fabricated by liquid pressing process. Their dynamic tensile properties were investigated in relation with microstructures and deformation mechanisms by using a split Hopkinson tension bar. The dynamic tensile test results indicated that the maximum strength of the W-fiber-reinforced composite (757 MPa) was much lower than the quasi-statically measured strength, whereas the Ta-fiber-reinforced composite showed very high maximum strength (2129 MPa). In the W-fiber-reinforced composite, the fracture abruptly occurred in perpendicular to the tensile direction because W fibers did not play a role in blocking cracks propagated from the amorphous matrix, thereby resulting in abrupt fracture within elastic range and consequent low tensile strength. The very high dynamic tensile strength of the Ta-fiber-reinforced composite could be explained by the presence of ductile Ta fibers in terms of mechanisms such as (1) interrupted propagation of cracks initiated in the amorphous matrix, (2) formation of lots of cracks in the amorphous matrix, and (3) sharing of loads and severe deformation (necking) of Ta fibers in cracked regions.

  1. Microstructure and wear properties of tungsten carbide reinforced steel matrix composites

    Institute of Scientific and Technical Information of China (English)

    YOU Xian-qing; SONG Xue-feng; REN Hao; MA Jian-guo; HUANG Man-ping; ZHANG Cheng-jun

    2005-01-01

    WC(27%) reinforced steel matrix composites were produced by using an electroslag melting casting technique. The microstructure of the material was characterized using scanning electron microscopy(SEM), optical microscopy and X-ray diffraction(XRD). Energy dispersive spectroscopy(EDS) and transmission electron micro-scopy were performed to investigate the interfacial composition between WC particle and steel matrix. The results reveal that the WC particles are partially melted into the steel substrate. At the same time, a reaction layer was detected along with the periphery of WC particle, which significantly enhances the bonding strength of the interface. A slipping wear (high stress abrasion) test was utilized to understand the wear behavior of this material. Abrasive experiment displays a better wear resistance than unreinforced steel matrix when coarse WC particles are dispersed into it. The coarse particles provide greater wear-resistance than the fine particles and operatively takes on the most applied loads. Additionally, the large particles have not been peeled during the wear process for a long time, which indicates the effect of interfacial reaction on wear behavior at the ambient temperature. A double carbide (Fe, W)3C is detected in the interface zone between particles and matrices using transmission electron microscopy.

  2. EFFECTS OF MATRIX MOLECULAR WEIGHT ON STRUCTURE AND REINFORCEMENT OF HIGH DENSITY POLYETHYLENE/MICA COMPOSITES

    Institute of Scientific and Technical Information of China (English)

    Li Chen; Yu-fang Xiang; Ke Wang; Qin Zhang; Rong-ni Du; Qiang Fu

    2011-01-01

    Three types of high-density polyethylene (HDPE) with different molecular weights (high, medium and Iow) were adopted to evaluate the influence of matrix molecular weight on the structure-property relation of injection-molded HDPE/mica composites through a combination of SEM, 2d-WAXS, DSC, DMA and tensile testing. Various structural factors including orientation, filler dispersion, interfacial interaction between HDPE and mica, etc., which can impact the macroscopic mechanics, were compared in detail among the three HDPE/mica composites. The transcrystallization of HDPE on the mica surface was observed and it exhibited strong matrix molecular weight dependence. Obvious transcrystalline structure was found in the composite with Iow molecular weight HDPE, whereas it was hard to be detected in the composites with increased HDPE molecular weight. The best reinforcement effect in the composite with low molecular weight HDPE can be understood as mainly due to substantially improved interracial adhesion between matrix and mica filler, which arises from the transerystallization mechanism.

  3. Macro-mechanical material model for fiber reinforced metal matrix composites

    CERN Document Server

    Banks-Sills, L

    1999-01-01

    The stress-strain behavior of a metal matrix composite reinforced with unidirectional, continuous and periodic fibers is investigated. Three-dimensional micro-mechanical analyses of a unit cell by means of the finite element method $9 and homogenization-localization are carried out. These calculations allow the determination of material behavior of the in-plane, as well as the fiber directions. The fibers are assumed to be elastic and the matrix elasto-plastic. $9 The matrix material is governed by a von Mises yield surface, isotropic hardening and an associated flow rule. With the aid of these analyses, the foundation to a macro-mechanical material model is presented which is employed to $9 consider an elementary problem. The model includes an anisotropic yield surface with isotropic hardening and an associated flow rule. A beam in bending containing square fibers under plane strain conditions is analyzed by means of $9 the model. Two cases are considered: one in which the fibers are symmetric with respect t...

  4. Au ion irradiation of various silicon carbide fiber-reinforced SiC matrix composites

    Energy Technology Data Exchange (ETDEWEB)

    Chaâbane, Nihed, E-mail: nihed.chaabane@cea.fr [CEA, INSTN/UEPTN, F-91191 Gif-sur-Yvette (France); Flem, Marion Le [CEA, DEN/DMN/SRMA, F-91191 Gif-sur-Yvette (France); Tanguy, Morgane [CEA, INSTN/UEPTN, F-91191 Gif-sur-Yvette (France); Urvoy, Stéphane [CEA, DEN/DMN/SRMA, F-91191 Gif-sur-Yvette (France); Sandt, Christophe; Dumas, Paul [Synchrotron SOLEIL, L’Orme des Merisiers, Saint-Aubin, BP 48, 91192 Gif-sur-Yvette Cedex (France); Serruys, Yves [CEA, DEN/DMN/SRMP, Laboratoire JANNUS, F-91191 Gif-sur-Yvette (France)

    2013-08-15

    Silicon carbide fiber-reinforced SiC matrix composites are promising candidates as fuel cladding for several concepts of Generation IV reactors and as structural materials for fusion reactors. The composites used in this study were composed of a SiC matrix obtained by chemical vapor infiltration associated with various fiber types (Tyranno Type-S, Tyranno SA Grade-3 and Hi-Nicalon Type-S) and with a PyC layer as the interphase. 12 MeV Au ions were used for irradiation up to 0.05 and 1 displacement per atom (dpa) fluences at room temperature and 800 °C. Analysis of both microstructure and composition of composites were performed by scanning electron microscopy (SEM), electron probe microanalysis and Raman spectroscopy. At room temperature and low fluence, Raman spectroscopy results showed that irradiation induces a disordered/distorted state into fibers and matrix. With increasing fluence, a total amorphization of these constituents occurs. The increase in the irradiation temperature leads to a damage recovery and partial recrystallization of samples. Image analysis performed from SEM micrographs highlights no significant change in fiber diameter and shape. However, SEM analysis suggests a longitudinal shrinkage of Tyranno Type-S fibers for the composite irradiated at 1 dpa at room temperature and 800 °C. These results are in complete agreement with conclusions from neutron irradiations suggesting an appropriate relevance of irradiations with 12 MeV Au.

  5. A novel processing route for carbon nanotube reinforced glass-ceramic matrix composites

    Science.gov (United States)

    Dassios, Konstantinos G.; Bonnefont, Guillaume; Fantozzi, Gilbert; Matikas, Theodore E.

    2015-03-01

    The current study reports the establishment of a novel feasible way for processing glass- and ceramic- matrix composites reinforced with carbon nanotubes (CNTs). The technique is based on high shear compaction of glass/ceramic and CNT blends in the presence of polymeric binders for the production of flexible green bodies which are subsequently sintered and densified by spark plasma sintering. The method was successfully applied on a borosilicate glass / multi-wall CNT composite with final density identical to that of the full-dense ceramic. Preliminary non-destructive evaluation of dynamic mechanical properties such as Young's and shear modulus and Poisson's ratio by ultrasonics show that property improvement maximizes up to a certain CNT loading; after this threshold is exceeded, properties degrade with further loading increase.

  6. PREDICTION OF MECHANICAL PROPERTY OF WHISKER REINFORCED METAL MATRIX COMPOSITE:PART-Ⅱ. VERIFICATION & APPLICATION

    Institute of Scientific and Technical Information of China (English)

    2000-01-01

    The present paper continues the discussion in Part-I. Model and Formulation. Based on the theory proposed in Part-I, the formulae predicting stiffness moduli of the composites in some typical cases of whisker orientations and loading conditions are derived and compared with theoretical representatives in literatures, experimental measurement and commonly-used empirical formulae. It seems that (1) with whisker reinforcing and matrix-hardening considered, the present prediction is in well agreement with the experimental measurement; (2) the present theory can predict accurate moduli with the proper pre-calculated parameters; (3) the upper-bound and lower-bound of the present theory are just the predictions of equal strain theory and equal stress theory; (4) the present theory provides a physical explanation and theoretical base for the present commonly-used empirical formulae. Compared with the microscopic mechanical theories, the present theory is competent for modulus prediction of practical engineering composite in accuracy and simplicity.

  7. Graphene-reinforced aluminum matrix composites prepared by spark plasma sintering

    Institute of Scientific and Technical Information of China (English)

    Wen-ming Tian; Song-mei Li; Bo Wang; Xin Chen; Jian-hua Liu; Mei Yu

    2016-01-01

    Graphene-reinforced 7055 aluminum alloy composites with different contents of graphene were prepared by spark plasma sinter-ing (SPS). The structure and mechanical properties of the composites were investigated. Testing results show that the hardness, compressive strength, and yield strength of the composites are improved with the addition of 1wt% graphene. A clean, strong interface is formed between the metal matrix and graphene via metallurgical bonding on atomic scale. Harmful aluminum carbide (Al4C3) is not formed during SPS processing. Further addition of graphene (above 1wt%) results in the deterioration in mechanical properties of the composites. The agglomeration of graphene plates is exacerbated with increasing graphene content, which is the main reason for this deterioration.

  8. Cavitation-erosion mechanism of laser cladded SiC particle reinforced metal matrix composite

    Institute of Scientific and Technical Information of China (English)

    ZHANG Chun-hua; ZHANG Song; YANG Hong-gang; ZHU Sheng-long; MAN Hau-chung; CAI Qing-kui

    2005-01-01

    With 2 kW continuous wave Nd-YAG laser,SiC ceramic powder was laser-cladded on the AA6061 aluminium alloy surface.Within the range of process parameters investigated,the parameters were optimized to produce the SiCp reinforced metal matrix composites(MMC) modified layer on AA6061 alloy surface.After being treated,the modified layer is crack-free,porosity free,and has good metallurgical bond with the substrate.The microstructure and chemical composition of the modified layer were analyzed by such detection devices as scanning electronic microscope(SEM-EDX) and X-ray diffractometer(XRD).The performance of electrochemical corrosion and cavitation erosion and their mechanism were estimated by the microhardness tester,potentiostat and ultrasonicinduced cavitation device.

  9. Weibull Probability Model for Fracture Strength of Aluminium (1101)-Alumina Particle Reinforced Metal Matrix Composite

    Institute of Scientific and Technical Information of China (English)

    A.Suresh Babu; V.Jayabalan

    2009-01-01

    In recent times, conventional materials are replaced by metal matrix composites (MMCs) due to their high specific strength and modulus.Strength reliability, one of the key factors restricting wider use of composite materials in various applications, is commonly characterized by Weibull strength distribution function.In the present work, statistical analysis of the strength data of 15% volume alumina particle (mean size 15 μm)reinforced in aluminum alloy (1101 grade alloy) fabricated by stir casting method was carried out using Weibull probability model.Twelve tension tests were performed according to ASTM B577 standards and the test data, the corresponding Weibull distribution was obtained.Finally the reliability of the composite behavior in terms of its fracture strength was presented to ensure the reliability of composites for suitable applications.An important implication of the present study is that the Weibull distribution describes the experimentally measured strength data more appropriately.

  10. Investigation of different carbon nanotube reinforcements for fabricating bulk AlMg5 matrix nanocomposites

    Energy Technology Data Exchange (ETDEWEB)

    Kallip, Kaspar, E-mail: kaspar.kallip@empa.ch [Empa, Swiss Federal Laboratories for Material Science and Technology, Laboratory for Advanced Materials Processing, Feuerwerkerstrasse 39, CH-3602 Thun (Switzerland); Leparoux, Marc [Empa, Swiss Federal Laboratories for Material Science and Technology, Laboratory for Advanced Materials Processing, Feuerwerkerstrasse 39, CH-3602 Thun (Switzerland); AlOgab, Khaled A. [King Abdulaziz City for Science and Technology (KACST), National Centers for Advanced Materials, P O Box 6086, Riyadh, 11442 (Saudi Arabia); Clerc, Steve; Deguilhem, Guillaume [Empa, Swiss Federal Laboratories for Material Science and Technology, Laboratory for Advanced Materials Processing, Feuerwerkerstrasse 39, CH-3602 Thun (Switzerland); Arroyo, Yadira [Empa, Swiss Federal Laboratories for Material Science and Technology, Electron Microscopy Center, Ueberlandstrasse 129, CH-8600 Dübendorf (Switzerland); Kwon, Hansang [Empa, Swiss Federal Laboratories for Material Science and Technology, Laboratory for Advanced Materials Processing, Feuerwerkerstrasse 39, CH-3602 Thun (Switzerland); Pukyong National University, Department of Materials System Engineering, 365 Sinseon-ro, Busan 608-739 (Korea, Republic of)

    2015-10-15

    AlMg5-based metal matrix composites were successfully fabricated using high energy planetary ball-milling and hot pressing. The influence of 6 types of carbon nanotubes (CNTs) with different properties was investigated for reinforcement. Over 3 fold increase in hardness and ultimate tensile strength was achieved with maximum values of 200 HV{sub 20} and 720 MPa respectively by varying CNT content from 0.5 to 5 vol%. The state, the dispersion as well as the reactivity of the different CNTs were investigated by Raman spectroscopy, X-Ray diffraction and microscopy. The CNTs were considered to be dispersed homogeneously, but were shortened due to high energy milling. No significant differences in mechanical performances could be observed depending either on the nature or on the agglomeration initial state of the investigated CNTs. The milling time has to be however adjusted to the CNT content as higher concentrations require a longer milling time for achieving dispersion of the nano-reinforcement. - Highlights: • CNTs sustained the milling process and became homogeneously dispersed. • 3 times strengthening over unreinforced alloy achieved. • Flexible processing route for dispersing wide range of nanoparticulate materials.

  11. Fabrication Of Carbon-Boron Reinforced Dry Polymer Matrix Composite Tape

    Science.gov (United States)

    Belvin, Harry L.; Cano, Roberto J.; Treasure, Monte; Shahood, Thomas W.

    1999-01-01

    Future generation aerospace vehicles will require specialized hybrid material forms for component structure fabrication. For this reason, high temperature composite prepregs in both dry and wet forms are being developed at NASA Langley Research Center (LaRC). In an attempt to improve compressive properties of carbon fiber reinforced composites, a hybrid carbon-boron tape was developed and used to fabricate composite laminates which were subsequently cut into flexural and compression specimens and tested. The hybrid material, given the designation HYCARB, was fabricated by modifying a previously developed process for the manufacture of dry polymer matrix composite (PMC) tape at LaRC. In this work, boron fibers were processed with IM7/LaRC(TradeMark)IAX poly(amide acid) solution-coated prepreg to form a dry hybrid tape for Automated Tow Placement (ATP). Boron fibers were encapsulated between two (2) layers of reduced volatile, low fiber areal weight poly(amide acid) solution-coated prepreg. The hybrid prepreg was then fully imidized and consolidated into a dry tape suitable for ATP. The fabrication of a hybrid boron material form for tow placement aids in the reduction of the overall manufacturing cost of boron reinforced composites, while realizing the improved compression strengths. Composite specimens were press-molded from the hybrid material and exhibited excellent mechanical properties.

  12. MOORA-Based Tribological Studies on Red Mud Reinforced Aluminum Metal Matrix Composites

    Directory of Open Access Journals (Sweden)

    S. Rajesh

    2013-01-01

    Full Text Available This paper presents the findings of an experimental investigation on the effects of applied load, sliding velocity, wt.% of reinforcement and hardness of the counterface material in dry sliding wear studies performed on red mud-based aluminum metal matrix composites (MMC. The specific wear rate and the coefficient of friction are considered as the output quality characteristics. Taguchi-based L9 orthogonal array has been used to accomplish the objective of the experimental study. Analysis of variance (ANOVA is employed to find the optimal setting and the effect of each parameter on the output performance characteristics. It has been observed that optimal factor setting for each output performance is different. In order to minimize the two responses simultaneously, multiobjective optimization based on ratio analysis (MOORA is adopted. MOORA revealed that the optimal combination of the dry sliding wear parameters for the multiperformance characteristics of the red mud based aluminium is the set normal load at 20 N, sliding velocity 3 m/s, % of reinforcement 20%, and counterface hardness of the material 58 HRC.

  13. Mechanical Properties of Natural Jute Fabric/Jute Mat Fiber Reinforced Polymer Matrix Hybrid Composites

    Directory of Open Access Journals (Sweden)

    Elsayed A. Elbadry

    2012-01-01

    Full Text Available Recycled needle punched jute fiber mats as a first natural fiber reinforcement system and these jute mats used as a core needle punched with recycled jute fabric cloths as skin layers as a second natural fiber reinforcement system were used for unsaturated polyester matrix composites via modifying the hand lay-up technique with resin preimpregnation into the jute fiber in vacuum. The effect of skin jute fabric on the tensile and bending properties of jute mat composites was investigated for different fiber weight contents. Moreover, the notch sensitivity of these composites was also compared by using the characteristic distance do calculated by Finite Element Method (FEM. The results showed that the tensile and flexural properties of jute mat composites increased by increasing the fiber weight content and by adding the jute fabric as skin layers. On the other hand, by adding the skins, the characteristic distance decreased and, therefore, the notch sensitivity of the composites increased. The fracture behavior investigated by SEM showed that extensive fiber pull-out mechanism was revealed at the tension side of jute mat composites under the bending load and by adding the jute cloth, the failure mode of jute mat was changed to fiber bridge mechanism.

  14. Anodization Mechanism on SiC Nanoparticle Reinforced Al Matrix Composites Produced by Power Metallurgy

    Directory of Open Access Journals (Sweden)

    Sonia C. Ferreira

    2014-12-01

    Full Text Available Specimens of aluminum-based composites reinforced by silicon carbide nanoparticles (Al/SiCnp produced by powder metallurgy (PM were anodized under voltage control in tartaric-sulfuric acid (TSA. In this work, the influence of the amount of SiCnp on the film growth during anodizing was investigated. The current density versus time response and the morphology of the porous alumina film formed at the composite surface are compared to those concerning a commercial aluminum alloy (AA1050 anodized under the same conditions. The processing method of the aluminum alloys influences the efficiency of the anodizing process, leading to a lower thicknesses for the unreinforced Al-PM alloy regarding the AA1050. The current density versus time response is strongly dependent on the amount of SiCnp. The current peaks and the steady-state current density recorded at each voltage step increases with the SiCnp volume fraction due to the oxidation of the SiCnp. The formation mechanism of the anodic film on Al/SiCnp composites is different from that occurring in AA1050, partly due the heterogeneous distribution of the reinforcement particles in the metallic matrix, but also to the entrapment of SiCnp in the anodic film.

  15. Damage Tolerance Enhancement of Carbon Fiber Reinforced Polymer Composites by Nanoreinforcement of Matrix

    Science.gov (United States)

    Fenner, Joel Stewart

    Nanocomposites are a relatively new class of materials which incorporate exotic, engineered nanoparticles to achieve superior material properties. Because of their extremely small size and well-ordered structure, many nanoparticles possess properties that exceed those offered by a wide range of other known materials, making them attractive candidates for novel materials engineering development. Their small size is also an impediment to their practical use, as they typically cannot be employed by themselves to realize those properties in large structures. Furthermore, nanoparticles typically possess strong self-affinity, rendering them difficult to disperse uniformly into a composite. However, contemporary research has shown that, if well-dispersed, nanoparticles have great capacity to improve the mechanical properties of composites, especially damage tolerance, in the form of fracture toughness, fatigue life, and impact damage mitigation. This research focuses on the development, manufacturing, and testing of hybrid micro/nanocomposites comprised of woven carbon fibers with a carbon nanotube reinforced epoxy matrix. Material processing consisted of dispersant-and-sonication based methods to disperse nanotubes into the matrix, and a vacuum-assisted wet lay-up process to prepare the hybrid composite laminates. Various damage tolerance properties of the hybrid composite were examined, including static strength, fracture toughness, fatigue life, fatigue crack growth rate, and impact damage behavior, and compared with similarly-processed reference material produced without nanoreinforcement. Significant improvements were obtained in interlaminar shear strength (15%), Mode-I fracture toughness (180%), shear fatigue life (order of magnitude), Mode-I fatigue crack growth rate (factor of 2), and effective impact damage toughness (40%). Observations by optical microscopy, scanning electron microscopy, and ultrasonic imaging showed significant differences in failure behavior

  16. Effect of Size, Content and Shape of Reinforcements on the Behavior of Metal Matrix Composites (MMCs) Under Tension

    Science.gov (United States)

    Paknia, A.; Pramanik, A.; Dixit, A. R.; Chattopadhyaya, S.

    2016-10-01

    The objective of this research was to investigate the mechanical behavior of metal matrix composites (MMCs) 6061 aluminum, reinforced with silicon carbide particles, under unidirectional tensile loading by finite element analysis. The effects of particle's shape, size and content on the tensile properties of the composites were studied and compared with each other. In addition, stress and strain distributions and possible particle fracture or debonding were investigated. It was found that, among different shapes, a certain shape of reinforcement particle provided better tensile properties for MMCs and, within each shape category, composites with smaller particle size and higher particle content (20%) also showed better properties. It was also found that when the reinforcement content was 10%, the effects of shape and size of the particles were negligible. Not only interfacial length between the reinforcement and matrix materials, but also state of matrix material, due to the presence of the reinforcement particles, affected the stiffness of the MMCs. In almost all of the cases, except for MMCs with triangular particles, when the stress increased, with the increase in the applied positive displacement, the stress distributions remained unchanged.

  17. Effects of Interface Modification on Mechanical Behavior of Hi-Nicalon Fiber-Reinforced Celsian Matrix Composites

    Science.gov (United States)

    Bansal, Narottam P.; Eldridge, Jeffrey I.

    1997-01-01

    Unidirectional celsian matrix composites having approx. 42 volume percent of uncoated or BN/SiC-coated Hi-Nicalon fibers were tested in three-point bend at room temperature. The uncoated fiber-reinforced composites showed catastrophic failure with strength of 210 +/- 35 MPa and a flat fracture surface. In contrast, composites reinforced with BN/SiC-coated fibers exhibited graceful failure with extensive fiber pullout. Values of first matrix cracking stress and strain were 435 +/- 35 MPa and 0.27 +/- 0.01 %, respectively, with ultimate strength as high as 960 MPa. The elastic Young's modulus of the uncoated and BN/SiC-coated fiber-reinforced composites were measured as 184 q 4 GPa and 165 +/- 5 GPa, respectively. Fiber push-through tests and microscopic examination indicated no chemical reaction at the uncoated or coated fiber-matrix interface. The low strength of the uncoated fiber-reinforced composite is probably due to degradation of the fibers from mechanical surface damage during processing. Because both the coated and uncoated fiber reinforced composites exhibited weak interfaces, the beneficial effect of the BN-SiC dual layer is primarily the protection of fibers from mechanical damage during processing.

  18. Effect of surface modification on carbon fiber and its reinforced phenolic matrix composite

    Science.gov (United States)

    Yuan, Hua; Wang, Chengguo; Zhang, Shan; Lin, Xue

    2012-10-01

    In this work, polyacrylonitrile (PAN)-based carbon fiber were chemically modified with H2SO4, KClO3 and silane coupling agent (γ-aminopropyltriethoxysilane, APS), and carbon fiber reinforced phenolic matrix composites were prepared. The structural and surface characteristics of the carbon fiber were investigated by scanning electron microscopy (SEM), X-ray photoelectron spectroscopy (XPS), laser Raman scattering (LRS) and Fourier transform infrared spectroscopy (FTIR). Single fiber mechanical properties, specific surface area, composite impact properties and interfacial shear strength (ILSS) were researched to indicate the effects of surface modification on fibers and the interaction between modified fiber surface and phenolic matrix. The results showed that carbon fiber surface modification by oxidation and APS can strengthen fiber surface chemical activity and enlarge the fiber surface area as well as its roughness. When carbon fiber (CF) is oxidized treatment, the oxygen content as well as the O/C ratio will be obviously increased. Oxygen functional groups increase with oxidation time increasing. Carbon fiber treated with APS will make Csbnd Osbnd R content increase and Osbnd Cdbnd O content decrease due to surface reaction. Proper treatment of carbon fiber with acid and silane coupling agent prove an effective way to increase the interfacial adhesion and improve the mechanical and outdoor performance of the resulting fiber/resin composites.

  19. Development of quartz particulate reinforced AA6063 aluminum matrix composites via friction stir processing

    Directory of Open Access Journals (Sweden)

    S. Joyson Abraham

    2016-12-01

    Full Text Available Friction stir processing (FSP has been accepted as a potential method to produce aluminum matrix composites (AMCs without the drawbacks of liquid metallurgy methods. The present work focuses on the development of AMCs reinforced with quartz (SiO2 particles using FSP. Grooves with various dimensions were machined on AA6063 plates and compacted with quartz particles. A single pass FSP was carried out using a combination of optimized process parameters. The volume fraction of quartz particles in the AMCs was varied from 0 to 18 vol.% in steps of 6 vol.%. The developed AA6063/Quartz AMCs were characterized using optical, scanning and transmission electron microscopy. The quartz particles were distributed uniformly in the aluminum matrix irrespective of the location within the stir zone. The grains of the AA6063 were extensively refined by the combination of thermomechanical effect of FSP and the pinning effect of quartz particles. The dispersion of the quartz particles improved the microhardness and wear resistance of the AMCs. The role of quartz particles on the worn surface and wear debris is reported.

  20. Abrasive Performance of Chromium Carbide Reinforced Ni3Al Matrix Composite Cladding

    Institute of Scientific and Technical Information of China (English)

    LI Shang-ping; LUO He-li; FENG Di; CAO Xu; ZHANG Xi-e

    2009-01-01

    The Microstructure and room temperature abrasive wear resistance of chromium carbide reinforced NiM3Al matrix composite cladding at different depth on nickel base alloy were investigated. The results showed that there is a great difference in microstructure and wear resistance of the Ni3 Al matrix composite at different depth. Three kinds of tests, designed for different load and abrasive size, were used to understand the wear behaviour of this material. Under all three wear conditions, the abrasion resistance of the composite cladding at the depth of 6 mm, namely NC-M2, was much higher than that of the composite cladding at the depth of 2 mm, namely NC-M1. In addition, the wear-resistant advantage of NC-M2 was more obvious when the size of the abrasive was small. The relative wear resistance of NC-M2 increased from 1.63 times to 2.05 times when the size of the abrasive decreased from 180 μm to 50μm. The mierostructure of the composite cladding showed that the size of chromium carbide particles, which was mainly influenced by cooling rate of melting pool, was a function of distance from the interface between the coating and substrate varied gradually. The chromium carbide particles near the interface were finer than that far from inter-face, which was the main reason for the different wear resistance of the composite cladding at different depth.

  1. Classification of Structure Defects of Metal Matrix Castings with Saturated Reinforcement

    Directory of Open Access Journals (Sweden)

    K. Gawdzińska

    2012-09-01

    Full Text Available Definition of a composite [1] describes an ideal composite material with perfect structure. In real composite materials, structure isusually imperfect – composites contain various types of defects [2, 3–5], especially as the casted composites are of concern. The reason for this is a specific structure of castings, related to course of the manufacturing process. In case of metal matrix composite castings, especially regarding these manufactured by saturation, there is no classification of these defects [2, 4]. Classification of defects in castings of classic materials (cast iron, cast steel, non-ferrous alloys is insufficient and requires completion of specific defects of mentioned materials. This problem (noted during manufacturing metal matrix composite castings with saturated reinforcement in Institute of Basic Technical Sciences of Maritime University Szczecin has become a reason of starting work aimed at creating such classification. As a result, this paper was prepared. It can contribute to improvement of quality of studied materials and, as a consequence, improve the environment protection level.

  2. Columnar-to-Equiaxed Transition in Metal-Matrix Composites Reinforced with Silicon Carbide Particles

    Directory of Open Access Journals (Sweden)

    Alicia E. Ares

    2013-01-01

    Full Text Available The present work is focused on the study of the effect of directional heat extraction on the silicon-carbide (SiC distribution in zinc-aluminum matrix composites (MMCs and on the columnar-to-equiaxed (CET position in directionally solidified samples. To this end, a ZA-27 alloy matrix was reinforced with ceramic particles of SiC and vertically directionally solidified. The cooling rates, temperature gradients, and interphase velocities were then measured, and their influence on the solidification microstructure of the MMCs was analyzed. The recalescence detected and measured during the equiaxed transition was of the order of 3.5°C to 1.1°C. The values of the temperature gradients reached a minimum during the CET and were even negative in most cases (between −3.89 K and 0.06 K. The interphase velocities varied between 0.07 mm/s and 0.44 mm/s at the transition. Also, the presence of ceramic particles in ZA-27 alloys affected the thermodynamic local conditions and the kinetics of nucleation, producing a finer microstructure.

  3. Titanate nanotubes for reinforcement of a poly(ethylene oxide)/chitosan polymer matrix

    Science.gov (United States)

    Porras, R.; Bavykin, D. V.; Zekonyte, J.; Walsh, F. C.; Wood, R. J.

    2016-05-01

    Soft polyethylene oxide (PEO)/chitosan mixtures, reinforced with hard titanate nanotubes (TiNTs) by co-precipitation from aqueous solution, have been used to produce compact coatings by the ‘drop-cast’ method, using water soluble PEO polymer and stable, aqueous colloidal solutions of TiNTs. The effects of the nanotube concentration and their length on the hardness and modulus of the prepared composite have been studied using nanoindentation and nanoscratch techniques. The uniformity of TiNT dispersion within the polymer matrix has been studied using transmission electron microscopy (TEM). A remarkable increase in hardness and reduced Young’s modulus of the composites, compared to pure polymer blends, has been observed at a TiNT concentration of 25 wt %. The short (up to 30 min) ultrasound treatment of aqueous solutions containing polymers and a colloidal TiNT mixture prior to drop casting has resulted in some improvements in both hardness and reduced Young’s modulus of dry composite films, probably due to a better dispersion of ceramic nanotubes within the matrix. However, further (more than 1 h) treatment of the mixture with ultrasound resulted in a deterioration of the mechanical properties of the composite accompanied by a shortening of the nanotubes, as observed by the TEM.

  4. Classification of Structure Defects of Metal Matrix Castings with Saturated Reinforcement

    Directory of Open Access Journals (Sweden)

    Gawdzińska K.

    2012-09-01

    Full Text Available Definition of a composite [1] describes an ideal composite material with perfect structure. In real composite materials, structure is usually imperfect - composites contain various types of defects [2, 3-5], especially as the casted composites are of concern. The reason for this is a specific structure of castings, related to course of the manufacturing process. In case of metal matrix composite castings, especially regarding these manufactured by saturation, there is no classification of these defects [2, 4]. Classification of defects in castings of classic materials (cast iron, cast steel, non-ferrous alloys is insufficient and requires completion of specific defects of mentioned materials. This problem (noted during manufacturing metal matrix composite castings with saturated reinforcement in Institute of Basic Technical Sciences of Maritime University Szczecin has become a reason of starting work aimed at creating such classification. As a result, this paper was prepared. It can contribute to improvement of quality of studied materials and, as a consequence, improve the environment protection level.

  5. Using Goals, Feedback, Reinforcement, and a Performance Matrix to Improve Customer Service in a Large Department Store

    Science.gov (United States)

    Eikenhout, Nelson; Austin, John

    2005-01-01

    This study employed an ABAC and multiple baseline design to evaluate the effects of (B) feedback and (C) a package of feedback, goalsetting, and reinforcement (supervisor praise and an area-wide celebration as managed through a performance matrix, on a total of 14 various customer service behaviors for a total of 115 employees at a large…

  6. Structure-property relations for silicon nitride matrix composites reinforced with pyrolytic carbon pre-coated Hi-Nicalon fibers

    NARCIS (Netherlands)

    Kooi, B.J.; Hosson, J.Th.M. De; Olivier, C.; Veyret, J.B.

    1999-01-01

    Si3N4 matrix composites reinforced with pyrolytic carbon pre-coated Hi-Nicalon (SiC) fibers, were studied using tensile testing and transmission electron microscopy. Three types of samples were evaluated all with a nominal coating thickness of 200 nm. The composites were densified by hot pressing at

  7. Structure-property relations for silicon nitride matrix composites reinforced with pyrolytic carbon pre-coated Hi-Nicalon fibers

    NARCIS (Netherlands)

    Kooi, B.J.; Hosson, J.Th.M. De; Olivier, C.; Veyret, J.B.

    1999-01-01

    Si3N4 matrix composites reinforced with pyrolytic carbon pre-coated Hi-Nicalon (SiC) fibers, were studied using tensile testing and transmission electron microscopy. Three types of samples were evaluated all with a nominal coating thickness of 200 nm. The composites were densified by hot pressing at

  8. Microwave Rapid Sintering of Al-Metal Matrix Composites: A Review on the Effect of Reinforcements, Microstructure and Mechanical Properties

    Directory of Open Access Journals (Sweden)

    Penchal Reddy Matli

    2016-06-01

    Full Text Available Aluminum metal matrix composites (AMMCs are light-weight materials having wide-spread use in the automobile and aerospace industries due to their attractive physical and mechanical properties. The promising mechanical properties of AMMCs are ascribed to the size and distribution of the reinforcement, as well as to the grain size of the matrix. Microwave rapid sintering involves internal heating of aluminum compacts by passing microwave energy through them. The main features of the microwave sintering technique are a short processing time and a low energy consumption. The aim of this review article is to briefly present the microwave rapid sintering process and to summarize the recent published work on the sintering and properties of pure Al and Al-based matrix composites containing different reinforcements.

  9. Al6061 Hybrid Metal Matrix Composite Reinforced with Alumina and Molybdenum Disulphide

    Directory of Open Access Journals (Sweden)

    G. Pitchayyapillai

    2016-01-01

    Full Text Available Aluminum Hybrid Reinforcement Technology is a response to the dynamic ever-increasing service requirement of industries such as transportation, aerospace, automobile, and marine, due to its attractive properties like high ductility, highly conductivity, light weight, and high strength to weight ratio. In this evolution, an attempt has been made to investigate the wear rate of Al6061 hybrid metal matrix composite reinforced with the hard ceramic alumina (4, 8, and 12 wt.% of Al2O3 and soft solid lubricant of molybdenum disulphide (2, 4, and 6 wt.% of MoS2 is fabricated by using stir casting method. The unlubricated pins on disc wear tests were conducted to examine the wear behaviour of Al6061/12 wt.% of Al2O3/MoS2 composites. The sliding wear tests were carried out at various loads of 15, 30, and 45 N, sliding velocity (1.25, 2.50, and 3.25 m/sec, and different MoS2 wt.% (2, 4, and 6 wt.%. In addition, the CNC turning experiments were conducted on Al6061/12 wt.% Al2O3/6 wt.% MoS2 using CNMG 120408 uncoated carbide cutting tool under cutting of 100, 150, and 200 m/min, feed of 0.1, 0.2, and 0.3 mm/rev, and depth of cut of 1, 1.5, and 2 mm.

  10. Engineering a novel material: Nanometric titanium carbide particles in a matrix of carbon nanotubes

    CERN Document Server

    BADIE, Sylvain

    2015-01-01

    New physics studies at ISOLDE are motivated by new beams available, especially beams of exotic nuclei located at the frontier of the nuclear chart. Such beams are often short lived (in the order of milliseconds) and decay before they can be extracted from the target material, where typical diffusion times are in the order of seconds or more. Novel nanostructured and nanocomposite target materials have been developed to increase the release efficiency by reducing the diffusion paths and so the diffusion times, allowing ISOLDE to deliver new and more intense beams of exotic nuclei. 35Ca (25 ms half-life) was attempted by developing a titanium carbide and carbon black nanocomposite, but such isotope could not be extracted. A different production method with different precursors - titanium oxide and multiwall carbon nanotubes - is here proposed and expected to yield a target material which will increase the release rates of such isotope. A novel material, very porous, consisting of titanium carbide particles disp...

  11. Effect of reinforcement of AL-6063 with SiC on mechanical behavior and microstructure of metal matrix composites

    Directory of Open Access Journals (Sweden)

    M. K. Aravindan

    2014-03-01

    Full Text Available A phrase heard often in recent years, advanced composite materials like Al/SiC metal matrix composite is gradually becoming very important materials in auto and aerospace industries due to their superior properties. The present study examines the mechanical properties of aluminum (Al-6063/SiC Silicon carbide reinforced particles metal-matrix composites (MMCs by varying weight fractions of SiC. For this (Al-6063/SiC reinforced particles MMCs are fabricated by stir casting method at air atmosphere . The MMCs are prepared in the form of bars with varying the reinforced particles by weight fraction ranging from 2 %, 4 %, 6 %, 8 % and 10 %. The reinforced particles size of SiC is varying between 25-40 microns. The microstructure study shows that the distribution of particles becomes better with increasing weight fraction of SiC. The Mechanical properties like, Ultimate tensile strength (MPa, % Elongation, Hardness (HRB, Yield Strength (N.m are investigated on prepared specimens of MMCs. It was observed that the hardness of the composite is increased gradually from 2-6 % and drastically from 8-10%. The tensile strength and ultimate break load are increased with rising of reinforced weight fraction and the improvement varies between 15.8- 27 % and 2-15 % respectively.

  12. A Study of Influencing Factors on the Tensile Response of a Titanium Matrix Composite With Weak Interfacial Bonding

    Science.gov (United States)

    Goldberg, Robert K.; Arnold, Steven M.

    2000-01-01

    The generalized method of cells micromechanics model is utilized to analyze the tensile stress-strain response of a representative titanium matrix composite with weak interfacial bonding. The fiber/matrix interface is modeled through application of a displacement discontinuity between the fiber and matrix once a critical debonding stress has been exceeded. Unidirectional composites with loading parallel and perpendicular to the fibers are examined, as well as a cross-ply laminate. For each of the laminates studied, analytically obtained results are compared to experimental data. The application of residual stresses through a cool-down process was found to have a significant effect on the tensile response. For the unidirectional laminate with loading applied perpendicular to the fibers, fiber packing and fiber shape were shown to have a significant effect on the predicted tensile response. Furthermore, the interface was characterized through the use of semi-emperical parameters including an interfacial compliance and a "debond stress;" defined as the stress level across the interface which activates fiber/matrix debonding. The results in this paper demonstrate that if architectural factors are correctly accounted for and the interface is appropriately characterized, the macro-level composite behavior can be correctly predicted without modifying any of the fiber or matrix constituent properties.

  13. The erosion performance of particle reinforced metal matrix composite coatings produced by co-deposition cold gas dynamic spraying

    Science.gov (United States)

    Peat, Tom; Galloway, Alexander; Toumpis, Athanasios; McNutt, Philip; Iqbal, Naveed

    2017-02-01

    This work reports on the erosion performance of three particle reinforced metal matrix composite coatings, co-deposited with an aluminium binder via cold-gas dynamic spraying. The deposition of ceramic particles is difficult to achieve with typical cold spray techniques due to the absence of particle deformation. This issue has been overcome in the present study by simultaneously spraying the reinforcing particles with a ductile metallic binder which has led to an increased level of ceramic/cermet particles deposited on the substrate with thick (>400 μm) coatings produced. The aim of this investigation was to evaluate the erosion performance of the co-deposited coatings within a slurry environment. The study also incorporated standard metallographic characterisation techniques to evaluate the distribution of reinforcing particles within the aluminium matrix. All coatings exhibited poorer erosion performance than the uncoated material, both in terms of volume loss and mass loss. The Al2O3 reinforced coating sustained the greatest amount of damage following exposure to the slurry and recorded the greatest volume loss (approx. 2.8 mm3) out of all of the examined coatings. Despite the poor erosion performance, the WC-CoCr reinforced coating demonstrated a considerable hardness increase over the as-received AA5083 (approx. 400%) and also exhibited the smallest free space length between adjacent particles. The findings of this study reveal that the removal of the AA5083 matrix by the impinging silicon carbide particles acts as the primary wear mechanism leading to the degradation of the coating. Analysis of the wear scar has demonstrated that the damage to the soft matrix alloy takes the form of ploughing and scoring which subsequently exposes carbide/oxide particles to the impinging slurry.

  14. Effect of the percentage of reinforcement on the wear in the metal matrix composites sintered with abnormal glow discharge; Efecto del porcentaje de refuerzo frente al desgaste en compuestos de matriz metalica sinterizados con descarga luminiscente anormal

    Energy Technology Data Exchange (ETDEWEB)

    Perez-Velasquez, S.; Pineda-Triana, Y.; Aguilar-Castro, Y.; Vera-Lopez, E.

    2016-05-01

    In this study an analysis of the behavior of dry wear coefficient of a Metal Matrix Composite (MMC) in 316 stainless steel reinforced with particles of titanium carbide (TiC) according to ASTM G 99 standards, in a pin-on-disk test. In this research it is tested the effect of the percentage of reinforcement in the MMC manufactured with 3, 6 y 9% (vol.) of TiC, in samples compacted at 800 MPa, generating different values of grain size, hardness and density, they are sintered with abnormal glow discharge, at a temperature of 1200 degree centigrade ±5 degree centigrade, with a protection atmosphere H{sub 2} - N{sub 2} and a permanence time of 30 minutes. According to the results obtained it is concluded that the best condition for the MMC manufacturing, in relation to the reinforcement percentage, is the one obtained when the mixture contains 6% of TiC compacted at 800 MPa. In these conditions, it was obtained: achieving smaller grain size, the greater hardness and the lowest coefficient of friction. In this respect, it was observed that the incorporation of the ceramic particles (TiC) in a matrix of austenitic steel (316) shows significant improvements in the resistance to the wear. (Author)

  15. The effect of particle addition and fibrous reinforcement on epoxy-matrix composites for severe sliding conditions

    DEFF Research Database (Denmark)

    Larsen, Thomas Ricco Ølholm; Løgstrup Andersen, Tom; Thorning, Bent

    2008-01-01

    This paper reports production and tribological testing of epoxy-matrix composites for dry-sliding conditions. The examined composites are produced using the following components: epoxy resin (EP), glass fiber weave (G), carbon/aramid hybrid weave (CA), PTFE particles and nano-scale CuO particles...... pv conditions all tested composites show signs of decomposition. Despite this, glass fiber reinforcement has a relatively steady behavior while carbon/aramid reinforcement gives raise to a gradually increasing frictional force, which ultimately results in complete failure of the test-specimen. (c...

  16. Self-healing of damage in fibre-reinforced polymer-matrix composites.

    Science.gov (United States)

    Hayes, S A; Zhang, W; Branthwaite, M; Jones, F R

    2007-04-22

    Self-healing resin systems have been discussed for over a decade and four different technologies had been proposed. However, little work on their application as composite matrices has been published although this was one of the stated aims of the earliest work in the field. This paper reports on the optimization of a solid-state self-healing resin system and its subsequent use as a matrix for high volume fraction glass fibre-reinforced composites. The resin system was optimized using Charpy impact testing and repeated healing, while the efficiency of healing in composites was determined by analysing the growth of delaminations following repeated impacts with or without a healing cycle. To act as a reference, a non-healing resin system was subjected to the same treatments and the results are compared with the healable system. The optimized resin system displays a healing efficiency of 65% after the first healing cycle, dropping to 35 and 30% after the second and third healing cycles, respectively. Correction for any healability due to further curing showed that approximately 50% healing efficiency could be achieved with the bisphenol A-based epoxy resin containing 7.5% of polybisphenol-A-co-epichlorohydrin. The composite, on the other hand, displays a healing efficiency of approximately 30%. It is therefore clear that the solid-state self-healing system is capable of healing transverse cracks and delaminations in a composite, but that more work is needed to optimize matrix healing within a composite and to develop a methodology for assessing recovery in performance.

  17. Microstructural Evolution in Laser Deposited Nickel-Titanium-Carbon in Situ Metal-Matrix Composites (Preprint)

    Science.gov (United States)

    2010-01-01

    investigated Ni-TiC composites processed by direct laser fabrication (DLF) from a feedstock of elemental nickel and titanium carbide powders. They focused... laser fabrication using powder and wire. Mater Design 2007; 28:2040-6. 3. Y. Choi, J. K. Lee, M. E. Mullins, J. Mater. Sci 32(1997) 1717-1724. 4

  18. Manufacturing Techniques for Titanium Aluminide Based Alloys and Metal Matrix Composites

    Science.gov (United States)

    2010-01-01

    a) LPT blade casting (b) Portion of disk and some blades ready for assembly [10...the production of high-pressure aero-engine compressor blades from a TiAl ingot [30...have become front- runners in replacing Nickel-based superalloys in gas turbine engines. Replacement of Ni-based superalloys parts with titanium

  19. Fracture behavior of reinforced aluminum alloy matrix composites using thermal imaging tools

    Science.gov (United States)

    Avdelidis, N. P.; Exarchos, D.; Vazquez, P.; Ibarra-Castanedo, C.; Sfarra, S.; Maldague, X. P. V.; Matikas, T. E.

    2016-05-01

    In this work the influence of the microstructure at the vicinity of the interface on the fracture behavior of particulate-reinforced aluminum alloy matrix composites (Al/SiCp composites) is studied by using thermographic tools. In particular, infrared thermography was used to monitor the plane crack propagation behavior of the materials. The deformation of solid materials is almost always accompanied by heat release. When the material becomes deformed or is damaged and fractured, a part of the energy necessary to initiate and propagate the damage is transformed in an irreversible way into heat. The thermal camera detects the heat wave, generated by the thermo-mechanical coupling and the intrinsic dissipated energy during mechanical loading of the sample. By using an adapted detector, thermography records the two dimensional "temperature" field as it results from the infrared radiation emitted by the object. The principal advantage of infrared thermography is its noncontact, non-destructive character. This methodology is being applied to characterise the fracture behavior of the particulate composites. Infrared thermography is being used to monitor the plane crack propagation behavior of such materials. Furthermore, an innovative approach to use microscopic measurements using IR microscopic lenses was attempted, in order to enable smaller features (in the micro scale) to be imaged with accuracy and assurance.

  20. Evaluation of the Technical-Economic Potential of Particle- Reinforced Aluminum Matrix Composites and Electrochemical Machining

    Science.gov (United States)

    Schubert, A.; Götze, U.; Hackert-Oschätzchen, M.; Lehnert, N.; Herold, F.; Meichsner, G.; Schmidt, A.

    2016-03-01

    Compared to conventional cutting, the processing of materials by electrochemical machining offers some technical advantages like high surface quality, no thermal or mechanical impact on the work piece and preservation of the microstructure of the work piece material. From the economic point of view, the possibility of process parallelization and the absence of any process-related tool wear are mentionable advantages of electrochemical machining. In this study, based on experimental results, it will be evaluated to what extent the electrochemical machining is technically and economically suitable for the finish-machining of particle- reinforced aluminum matrix composites (AMCs). Initial studies showed that electrochemical machining - in contrast to other machining processes - has the potential to fulfil demanding requirements regarding precision and surface quality of products or components especially when applied to AMCs. In addition, the investigations show that processing of AMCs by electrochemical machining requires less energy than the electrochemical machining of stainless steel. Therefore, an evaluation of electrochemically machined AMCs - compared to stainless steel - from a technical and an economic perspective will be presented in this paper. The results show the potential of electro-chemically machined AMCs and contribute to the enhancement of instruments for technical-economic evaluations as well as a comprehensive innovation control.

  1. Modeling of compressive stiffness of a multilayered graphite-reinforced magnesium-matrix composite

    Energy Technology Data Exchange (ETDEWEB)

    Bhattacharya, A.K.; Hong, S.I. (Los Alamos National Lab., NM (United States))

    1993-06-01

    Short graphite fiber-reinforced magnesium-matrix composites are of considerable interest due to their superior specific strength, stiffness and low coefficient of thermal expansion. The problem of non-wetting of fibers with molten metal in these composites seems to have been considerably improved and such types of composites are now being commercially produced. However, an understanding of the mechanical properties of these composites is very limited and less amenable to rigorous analysis because of the discontinuous fiber arrangements. Also, a part of the difficulty is due to a large number of geometrical and material variables arising in the analysis. The situation is further complicated when the composites are made of layered structure, each layer having different fiber orientations. Moreover, inherent porosity and its distribution in the layered composites cause further complicacy for it to be amenable for the mathematical analysis. In this note the authors discuss a finite element approach to the analysis of compressive stiffness behavior in such a composite and compare model predictions with experimental data on the modulus of such composites.

  2. Numerical Methods Application for Reinforced Concrete Elements-Theoretical Approach for Direct Stiffness Matrix Method

    Directory of Open Access Journals (Sweden)

    Sergiu Ciprian Catinas

    2015-07-01

    Full Text Available A detailed theoretical and practical investigation of the reinforced concrete elements is due to recent techniques and method that are implemented in the construction market. More over a theoretical study is a demand for a better and faster approach nowadays due to rapid development of the calculus technique. The paper above will present a study for implementing in a static calculus the direct stiffness matrix method in order capable to address phenomena related to different stages of loading, rapid change of cross section area and physical properties. The method is a demand due to the fact that in our days the FEM (Finite Element Method is the only alternative to such a calculus and FEM are considered as expensive methods from the time and calculus resources point of view. The main goal in such a method is to create the moment-curvature diagram in the cross section that is analyzed. The paper above will express some of the most important techniques and new ideas as well in order to create the moment curvature graphic in the cross sections considered.

  3. Thermo-physical Properties of Continuous Carbon Fiber Reinforced Copper Matrix Composites

    Institute of Scientific and Technical Information of China (English)

    曹金华; 黄俊波; 陈先有

    2007-01-01

    Continuous carbon fiber reinforced copper matrix composites with 70%(volume fraction)of carbon fibers prepared by squeeze casting technique have been used for investigation of the coefficient of thermal expansion(CTE)and thermal conductivity.Thermo-physical properties have been measured in both, longitudinal and transversal directions to the fiber orientation.The results showed that Cf/Cu composites may be a suitable candidate for heat sinks because of its good thermo-physical properties e.g.the low CTE(4.18×10-6/K)in longitudinal orientation and(14.98×10-6/K)in transversal orientation at the range of 20-50℃,a good thermal conductivity(87.2 W/m·K)in longitudinal orientation and(58.2 W/m·K)in transversal orientation.Measured CTE and thermal conductivity values are compared with those predicted by several well-known models.Eshelby model gave better results for prediction of the CTE and thermal conductivity of the unidirectional composites.

  4. Mechanical properties of waste paper/jute fabric reinforced polyester resin matrix hybrid composites.

    Science.gov (United States)

    Das, Sekhar

    2017-09-15

    Hybrid composites were prepared with jute fabric and un-shredded newspaper in polyester resin matrix. The experiment was designed 1:2 weights ratio jute and unshredded newspaper to have 42 (w/w)% fibre content hybrid composites and two different sequences jute/paper/jute and paper/jute/paper of waste newspaper and jute fabric arrangement. Reinforcing material is characterized by chemically, X-ray diffraction methods, Fourier transform infrared spectroscopy and tensile testing. The tensile, flexural and interlaminar shear strength and fracture surface morphology of composites were evaluated and compared. It was found that tensile and flexural properties of the hybrid composite are higher than that of pure paper-based composite but less than pure woven jute composite. The hybridization effect of woven jute fabric and layering pattern effect on mechanical properties of newspaper/woven jute fabric hybrid composites were studied. The test results of composites were analyzed by one-way ANOVA (α=0.05), it showed significant differences among the groups. Copyright © 2017 Elsevier Ltd. All rights reserved.

  5. Aluminium Matrix Composites Reinforced with Co-continuous Interlaced Phases Aluminium-alumina Needles

    Directory of Open Access Journals (Sweden)

    Elvio de Napole Gregolin

    2002-09-01

    Full Text Available An Al-5SiO2 (5 wt% of SiO2 aluminium matrix fiber composite was produced where the reinforcement consists of fossil silica fibers needles. After being heat-treated at 600 °C, the original fiber morphology was retained but its microstructure changed from solid silica to an interconnected (Al-Si/Al2O3 interlaced structure named co-continuous composite. A technique of powder metallurgy, using commercial aluminium powder and the silica fibers as starting materials, followed by hot extrusion, was used to produce the composite. The co-continuous microstructure was obtained partially or totally on the fibers as a result of the reaction, which occurs during the heat treatment, first by solid diffusion and finally by the liquid Al-Si in local equilibrium, formed with the silicon released by reaction. The internal structure of the fibers was characterized using field emission electron microscope (FEG-SEM and optical microscopy on polished and fractured samples.

  6. Microstructure and properties of mechanical alloying particles reinforced aluminum matrix composites prepared by semisolid stirring pouring method

    Directory of Open Access Journals (Sweden)

    Yao-qiang Si

    2016-05-01

    Full Text Available Aluminum matrix composites reinforced with mechanical alloying particles (SiCp were fabricated by the semisolid stirring pouring method. The influence of mechanical alloying particles and Mg on the microstructure and mechanical properties of the composites was investigated by means of optical microscopy (OM, X-ray diffraction scanning (XRD, electron microscopy (SEM and energy dispersive spectroscopy (EDS. Results show that the addition of Mg converts the agglomerate mechanical alloying particles in ZL101 matrix composites into dispersed distribution in ZL101-Mg matrix composites, large matrix grains into fine equiaxed matrix grains, and eutectic phase into fine particles. So the mechanical properties of ZL101-Mg matrix composites are better than those of ZL101 matrix composites. The mechanical properties of ZL101/ZL101-Mg matrix composites are gradually increased with the increase of the volume fraction of mechanical alloying particles. When the volume fraction of mechanical alloying particles is 3%, the Vickers hardness and ultimate tensile strength of the ZL101/ZL101-Mg matrix composites reach their maximum values.

  7. [Expression of matrix metalloproteinases and inhibitor on the cornea tissue in rabbit after implantation of modified titanium skirt for keratoprosthesis].

    Science.gov (United States)

    Li, Li; Zhou, Dilys; Wang, Xiu-mei; Wang, Xiao-ping; Cui, Fu-zhai; Lu, Yu-jie; Huang, Yi-fei

    2012-01-01

    To investigate the expression of matrix metalloproteinase-2 (MMP-2) and Tissue inhibitor of matrix metalloproteinase-2 (TIMP-2) in rabbit corneas implanted with modified titanium skirt of keratoprosthesis in order to explore the potential roles. A total of 20 New Zealand white rabbits with corneal alkali burn in right eye rabbit corneas were divided into three groups. There were 6 animals in each group. Skirt of hydroxyapatite/Sandblast-Titanium and Sandblast-Titanium were inserted into the corneal stroma of rabbits in group A and group B. The group C did not insert skirt as surgical control.2 rabbits were as normal control D group. A total of 20 New Zealand white rabbits were divided into four groups with the same way. The expression of MMP-2 and TIMP-2 was determined by immunohistochemistry at 1 month, 3 months. The expression of MMP-2 and TIMP-2 mRNA level was determined by real time-polymerase chain reaction, and its protein level was determined by western blot. The optical cylinder was implanted to rabbit corneas, which were implanted with modified titanium skirt after 3 months. There was one case of corneal dissolution being found in group F. MMP-2 and TIMP-2 immunoreactivities were expressed in the normal corneas, predominantly in the corneal epithelium. After injury, immunoreactivities of both MMP-2 and TIMP-2 were increased notably in the healing corneal epithelium, infiltrating inflammatory cells, stromal fibroblasts and in growing vascular endothelial cells. The expression of MMP-2 was lower in group A and E than that in group B and F after 1 month and 3 months (t = 12.05, 2.93, 12.006, 3.781, P 0.05); MMP-2 immunoreactivities were absent or lowly expressed predominantly in the corneal epithelium of normal corneas. The expression of MMP-2, TIMP-2 mRNA level was parallel that of protein level. The expression of MMP-2 was lower in the corneal tissue sections of HA/SB-Ti skirt inserted eyes than that in the tissue sections of SB-Ti skirt inserted eyes. The

  8. Assessment of thermal shock induced damage in silicon carbide fibre reinforced glass matrix composites

    Directory of Open Access Journals (Sweden)

    Boccaccini, A. R.

    1998-09-01

    Full Text Available The development of microstructural damage in silicon carbide fibre (Nicalon™ reinforced glass matrix composite samples subjected to thermal shock was investigated by using a nondestructive forced resonance technique and fibre push out indentation tests. Thermal shock testing involved quenching samples in a water bath maintained at room temperature from a high temperature (650ºC. Changes in the Young's modulus and internal friction of the samples with increasing number of shocks were measured accurately by the forced resonance technique. Fibre push-out tests showed no significant changes in the properties of the fibre-matrix interface, indicating that damage in the composite was concentrated mainly in the development of matrix microcracking. It was also shown that the internal friction is a very sensitive parameter by which to detect the onset and development of such microcracking. A simple semi-empirical model is proposed to correlate the internal friction level with the microcracking density in the glass matrix. Finally, the relevance of detecting nondestructively the existence of microcracks in the glass matrix, before any significant interfacial degradation occurs, is emphasized, in conextion with the possibility of inducing a crack healing process by a thermal treatment (annealing, taking advantage of the viscous flow properties of the glass.

    El desarrollo de daño microestructural en materiales compuestos de matriz de vidrio reforzados con fibras de carburo de silicio (Nicalon™ sometidos a choque térmico fue investigado mediante la técnica no-destructiva de resonancia forzada y por mediciones de indentación "push-out" de fibras. Los ensayos de choque térmico involucraron el enfriamiento brusco en un baño de agua a temperatura ambiente de las piezas previamente calentadas a una temperatura elevada (650ºC. La técnica de resonancia forzada permitió medir cambios en el módulo de Young de elasticidad y en la fricci

  9. Fabrication and mechanical properties of AlCoNiCrFe high-entropy alloy particle reinforced Cu matrix composites

    Energy Technology Data Exchange (ETDEWEB)

    Chen, Jian, E-mail: chenjian@xatu.edu.cn [School of Materials Science and Chemical Engineering, Xi' an Technological University, Xi' an, Shaanxi 710021 (China); Niu, Pengyun; Wei, Ting [School of Materials Science and Chemical Engineering, Xi' an Technological University, Xi' an, Shaanxi 710021 (China); Hao, Liang [College of Architecture and Civil Engineering, Xi' an University of Science and Technology, Xi' an 710054 (China); Liu, Yunzi [School of Materials Science and Chemical Engineering, Xi' an Technological University, Xi' an, Shaanxi 710021 (China); Wang, Xianhui, E-mail: xhwang693@xaut.edu.cn [School of Materials Science and Engineering, Xi' an University of Technology, Xi' an, Shaanxi 710048 (China); Peng, Yuli [School of Materials Science and Chemical Engineering, Xi' an Technological University, Xi' an, Shaanxi 710021 (China)

    2015-11-15

    The AlCoNiCrFe high-entropy alloy was prepared by mechanical alloying and the AlCoNiCrFe high-entropy alloy reinforced Cu matrix composites were subsequently fabricated by powder metallurgy. The phase constituents and morphology of the alloying powders were characterized by X-ray diffractometer and scanning electron microscope, the microstructures of the Cu base composites were characterized by scanning electron microscope and transmission electron microscope, and the compression tests were made as well. The results show that the AlCoNiCrFe high-entropy alloy can form after milling for 24 h. During sintering process, no grain growth occurs and no intermetallic phases present in the AlCoNiCrFe high-entropy alloy in the Cu base composite. Compression tests show that the AlCoNiCrFe high-entropy alloy has a better strengthening effect than metallic glasses and the yield strength of the Cu matrix composite reinforced with the AlCoNiCrFe high-entropy alloy is close to the value predicted by the Voigt model based on the equal strain assumption. - Graphical abstract: AlCoNiCrFe HEA has a better strengthening effect than metallic glasses for particulate reinforced metal matrix composites. The yield strength of the Cu base composite reinforced with the AlCoNiCrFe HEA is close to the upper bound calculated by Voigt model. - Highlights: • AlCoNiCrFe high-entropy alloy was prepared by mechanical alloying. • A novel Cu base composite reinforced with AlCoNiCrFe was fabricated. • No grain growth and no intermetallic phase present in AlCoNiCrFe during sintering. • AlCoNiCrFe has a better strengthening effect than metallic glassy in composites.

  10. Hot Extrusion of A356 Aluminum Metal Matrix Composite with Carbon Nanotube/Al2O3 Hybrid Reinforcement

    Science.gov (United States)

    Kim, H. H.; Babu, J. S. S.; Kang, C. G.

    2014-05-01

    Over the years, the attention of material scientists and engineers has shifted from conventional composite materials to nanocomposite materials for the development of light weight and high-performance devices. Since the discovery of carbon nanotubes (CNTs), many researchers have tried to fabricate metal matrix composites (MMCs) with CNT reinforcements. However, CNTs exhibit low dispersibility in metal melts owing to their poor wettability and large surface-to-volume ratio. The use of an array of short fibers or hybrid reinforcements in a preform could overcome this problem and enhance the dispersion of CNTs in the matrix. In this study, multi-walled CNT/Al2O3 preform-based aluminum hybrid composites were fabricated using the infiltration method. Then, the composites were extruded to evaluate changes in its mechanical properties. In addition, the dispersion of reinforcements was investigated using a hardness test. The required extrusion pressure of hybrid MMCs increased as the Al2O3/CNT fraction increased. The deformation resistance of hybrid material was over two times that of the original A356 aluminum alloy material due to strengthening by the Al2O3/CNTs reinforcements. In addition, an unusual trend was detected; primary transition was induced by the hybrid reinforcements, as can be observed in the pressure-displacement curve. Increasing temperature of the material can help increase formability. In particular, temperatures under 623 K (350 °C) and over-incorporating reinforcements (Al2O3 20 pct, CNTs 3 pct) are not recommended owing to a significant increase in the brittleness of the hybrid material.

  11. In-situ fabrication of particulate reinforced aluminum matrix composites under high-frequency pulsed electromagnetic field

    Institute of Scientific and Technical Information of China (English)

    2007-01-01

    Pulsed magnetic field is generated when imposing pulse signal on high-frequency magnetic field. Distribution of the inner magnetic intensity in induction coils tends to be uniform. Furthermore oscillation and disturbance phenomena appear in the melt. Insitu Al2O3 and Al3Zr particulate reinforced aluminum matrix composites have been synthesized by direct melt reaction using Al-Zr(CO3)2 components under a foreign field. The size of reinforced particulates is 2-3 μm. They are well distributed in the matrix.Thermodynamic and kinetic analysis show that high-frequency pulsed magnetic field accelerates heat and mass transfer processes and improves the kinetic condition of in-situ fabrication.

  12. The effects of volume percent and aspect ratio of carbon fiber on fracture toughness of reinforced aluminum matrix composites

    Energy Technology Data Exchange (ETDEWEB)

    Naji, H. [Department of Materials and Metallurgical Engineering, Engineering Faculty, Ferdowsi University of Mashhad, Azadi Square, P.O. Box 91775-1111 (Iran, Islamic Republic of); Zebarjad, S.M. [Department of Materials and Metallurgical Engineering, Engineering Faculty, Ferdowsi University of Mashhad, Azadi Square, P.O. Box 91775-1111 (Iran, Islamic Republic of)], E-mail: Zebarjad@ferdowsi.um.ac.ir; Sajjadi, S.A. [Department of Materials and Metallurgical Engineering, Engineering Faculty, Ferdowsi University of Mashhad, Azadi Square, P.O. Box 91775-1111 (Iran, Islamic Republic of)

    2008-07-15

    Carbon fiber reinforced aluminum matrix composites are used as advanced materials in aerospace and electronic industries. In order to investigate role of aspect ratio of carbon fiber on fracture toughness of aluminum matrix composite, the composite was produced using stir casting. Al-8.5%Si-5%Mg selected as a matrix. The samples were prepared with three volume fractions (1, 2 and 3) and three aspect ratios (300, 500 and 800). Three-point bending test was performed on the specimens to evaluate the fracture toughness of the materials. The results showed that the fracture toughness of composites depends on both fiber volume fraction and aspect ratio. Scanning electron microscopy (SEM) was employed to elucidate the fracture behavior and crack deflection of composites. The study also, showed that the toughening mechanism depends strongly on fiber volume fraction, aspect ratio and the degree of wetting between fiber and matrix.

  13. Approach to In- Situ Producing Reinforcing Phase Within an Active-Transient Liquid Phase Bond Seam for Aluminum Matrix Composite

    Science.gov (United States)

    Zhang, Guifeng; Liao, Xianjin; Chen, Bo; Zhang, Linjie; Zhang, Jianxun

    2015-06-01

    To optimize the braze composition design route for aluminum matrix composite, the feasibility of in situ producing reinforcing phase within the transient liquid phase bond seam matrix, by adding active melting point increaser (MPI, e.g., Ti) together with general melting point depressant (MPD, e.g., Cu) into the interlayer, was demonstrated. For SiC p /A356 composite, by comparing the wettability, joint microstructure, joint shear strength, and fracture path for the developed Al-19Cu-1Ti, Al-19Cu, Al-33Cu-1Ti, Al-33Cu (wt pct), and commercial Cu foils as interlayer, the feasibility of in situ producing reinforcing phase within the bond seam by adding Ti was demonstrated. Especially for Al-19Cu-1Ti active braze, small and dispersed ternary aluminide of Al-Si-Ti phase was obtained within the bond seam as in situ reinforcement, leading to a favorable fracture path within SiC p /A356, not along the initial interface or within the bond seam. For the formation mechanism of the in situ reinforcing phase of MPI-containing intermetallic compound within the bond seam, a model of repeating concentration-precipitation-termination-engulfment during isothermal solidification is proposed.

  14. Corrosion of Continuous Fiber Reinforced Aluminum Metal Matrix Composites (CF-AMCs)

    Science.gov (United States)

    Tiwari, Shruti

    The first objective of this research is to study the atmospheric corrosion behavior of continuous reinforced aluminum matrix composites (CF-AMCs). The materials used for this research were alumina (Al2O3) and nickel (Ni) coated carbon (C) fibers reinforced AMCs. The major focus is to identify the correlation between atmospheric parameters and the corrosion rates of CF-AMCs in the multitude of microclimates and environments in Hawai'i. The micro-structures of CF-AMCs were obtained to correlate the microstructures with their corrosion performances. Also electrochemical polarization experiments were conducted in the laboratory to explain the corrosion mechanism of CF-AMCs. In addition, CF-AMCs were exposed to seven different test sites for three exposure periods. The various climatic conditions like temperature (T), relative humidity (RH), rainfall (RF), time of wetness (TOW), chloride (Cl- ) and sulfate (SO42-) deposition rate, and pH were monitored for three exposure period. Likewise, mass losses of CF-AMCs at each test site for three exposure periods were determined. The microstructure of the CF-AMCS showed that Al/C/50f MMCs contained a Ni-rich phase in the matrix, indicating that the Ni coating on the C fiber dissolved in the matrix. The intermetallic phases obtained in Al-2wt% Cu/Al 2O3/50f-T6 MMC and Al-2wt%-T6 monolith were rich in Cu and Fe. The intermetallic phases obtained in Al 7075/Al2O3/50f-T6 MMC and Al 7075-T6 monolith also contained traces of Mg, Zn, Ni, and Si. Electrochemical polarization experiment indicated that the Al/Al 2O3/50f Al-2wt% Cu/Al2O3/50f-T6 and Al 7075/Al2O3/50f-T6 MMC showed similar corrosion trends as their respective monoliths pure Al, Al-2wt%-T6 and Al 7075-T6 in both aerated and deaerated condition. Al2O3 fiber, being an insulator, did not have a great effect on the polarization behavior of the composites. Al/C/50f MMCs corroded at a much faster rate as compared to pure Al monolith due to the galvanic effect between C and Al

  15. Thermal residual stresses and stress distributions under tensile and compressive loadings of short fiber reinforced metal matrix composites

    Institute of Scientific and Technical Information of China (English)

    2001-01-01

    The thermal residual stresses and the stress distributions of short fiber reinforced metal matrix composite under tensile and compressive loadings were studied using large strain axisymmetric elasto-plastic finite element method. It is demonstrated that the thermal residual stresses can result in asymmetrical stress distributions and matrix plasticity. The thermal residual stresses decrease the stress transfer in tension and enhance the stress transfer in compression. The fiber volume fraction has more important effects on the thermal residual stresses and the stress distributions under tensile and compressive loadings than the fiber aspect ratio and the fiber end distance.

  16. Thermal diffusivity of Al-Mg based metallic matrix composite reinforced with Al2O3 ceramic particles

    Science.gov (United States)

    Cruz-Orea, A.; Morales, J. E.; Saavedra S, R.; Carrasco, C.

    2010-03-01

    Thermal diffusivities of Al-Mg based metallic matrix composite reinforced with ceramic particles of Al2O3 are reported in this article. The samples were produced by rheocasting and the studied operational condition in this case is the shear rate: 800, 1400 and 2000 rpm. Additionally, the AlMg base alloy was tested. Measurements of thermal diffusivity were performed at room temperature by using photoacoustic technique.

  17. Research on the Surface Micro-configuration in Vibration Cutting Particle Reinforced Metallic Matrix Composites SiC_p/Al

    Institute of Scientific and Technical Information of China (English)

    2002-01-01

    The cutting performance of particulate reinforced me tallic matrix composites(PRMMCs) SiC p/Al in ultrasonic vibration cutting and c ommon cutting with carbide tools and PCD tools was researched in the paper. Mic rostructure of machined surface was described, the relation between cutting para meters and surface roughness was presented, and characteristic of the surface re mained stress was also presented. Furthermore, wear regularity and abrasion resi stance ability of tools in ultrasonic vibration cut...

  18. Effect of Moisture Absorption Behavior on Mechanical Properties of Basalt Fibre Reinforced Polymer Matrix Composites

    OpenAIRE

    Amuthakkannan Pandian; Manikandan Vairavan; Winowlin Jappes Jebbas Thangaiah; Marimuthu Uthayakumar

    2014-01-01

    The study of mechanical properties of fibre reinforced polymeric materials under different environmental conditions is much important. This is because materials with superior ageing resistance can be satisfactorily durable. Moisture effects in fibre reinforced plastic composites have been widely studied. Basalt fibre reinforced unsaturated polyester resin composites were subjected to water immersion tests using both sea and normal water in order to study the effects of water absorption behavi...

  19. Synthesis of Carbon Nanotube-Reinforced Al2024 Matrix Nanocomposite Using Flake Powder Metallurgy Method

    Science.gov (United States)

    Rikhtegar, F.; Shabestari, S. G.; Saghafian, H.

    2016-12-01

    In current work, the flake powder metallurgy method was applied to achieve the uniform dispersion of carbon nanotubes (CNTs) within the Al2024 powder. For this purpose, the flake morphology of Al2024 powder with suitable diameter-to-thickness ratio ( D/ t = 85) was obtained after ball milling for 4 hours at 250 rpm and ball-to-powder ratio = 10. Then, the surface of matrix was modified by a hydrophilic polymer [polyvinyl alcohol (PVA)] to obtain the sufficient -OH group on its surface. Additionally, the refluxing of CNTs in nitric acid was performed at 393 K (120 °C) for 6 hours to functionalize the reinforcement by -COOH agent. After preparation of initial materials, the Al2024-1.5 wt pct CNTs suspension was stirred in a slurry at pH 3 until the color was changed in steady state from ink-like to transparent at pH 5. The hydrogen bonding was formed between the -OH groups of PVA coated Al2024 and -COOH groups of functionalized MWCNTs during the mixing step. Also, the temporary polarity could be considered between H+ and {{{C}}_{12}}{{{H}}_{25}}{{SO}}_4^ - ions on the surface of constituents, which led to improvement in the CNT distribution due to the changing of suspension pH. Consequently, the homogenous dispersion of CNTs in Al2024 flaky powders resulted in a chemical reaction of constituents without any destructive effects of mechanical forces. The morphological changes of Al2024 powders were studied by scanning electron microscopy (SEM), and surface treatments were evaluated by Fourier transform infrared and Raman spectroscopies. The dispersion of nanocomposite powder was investigated through field emission SEM. Also, X-ray diffraction analysis was used to investigate the initial Al2024 powder and formed phases after the ball milling process.

  20. Flax fabric reinforced arylated soy protein composites: A brittle-matrix behaviour

    CSIR Research Space (South Africa)

    Kumar, R

    2012-05-01

    Full Text Available Biocomposites were successfully prepared by the reinforcement of soy protein isolate (SPI) with different weight fractions of woven flax fabric. The flax-fabric-reinforced SPI-based composites were then arylated with 2,2-diphenyl-2-hydroxyethanoic...

  1. The Integration of EIS parameters and bulk matrix characterization in studying reinforced cement-based materials

    NARCIS (Netherlands)

    Koleva, D.A.; Van Breugel, K.

    2012-01-01

    Corrosion in reinforced concrete is a major and costly concern, arising from the higher complexity of involved phenomena on different levels of material science (e.g. electrochemistry, concrete material science) and material properties (macro/micro/ nano). Reinforced cement-based systems (e.g. reinf

  2. The integration of eis parameters and bulk matrix characteristics in studying reinforced cement-based materials

    NARCIS (Netherlands)

    Koleva, D.A.; Van Breugel, K.

    2011-01-01

    Corrosion in reinforced concrete is a major and costly concern, arising from the higher complexity of involved phenomena on different levels of material science (e.g. electrochemistry, concrete material science) and material properties (macro/micro/ nano). Reinforced cement-based systems (e.g. reinf

  3. The integration of eis parameters and bulk matrix characteristics in studying reinforced cement-based materials

    NARCIS (Netherlands)

    Koleva, D.A.; Van Breugel, K.

    2011-01-01

    Corrosion in reinforced concrete is a major and costly concern, arising from the higher complexity of involved phenomena on different levels of material science (e.g. electrochemistry, concrete material science) and material properties (macro/micro/ nano). Reinforced cement-based systems (e.g.

  4. The Integration of EIS parameters and bulk matrix characterization in studying reinforced cement-based materials

    NARCIS (Netherlands)

    Koleva, D.A.; Van Breugel, K.

    2012-01-01

    Corrosion in reinforced concrete is a major and costly concern, arising from the higher complexity of involved phenomena on different levels of material science (e.g. electrochemistry, concrete material science) and material properties (macro/micro/ nano). Reinforced cement-based systems (e.g.

  5. Fabrication of metallic reinforcement fibres for metal matrix composites by in-rotating-liquid spinning. Herstellung metallischer Verstaerkungsfasern fuer Metallmatrixverbundwerkstoffe durch Schmelzspinnen in eine rotierende Fluessigkeit

    Energy Technology Data Exchange (ETDEWEB)

    Heyder, B.; Frommeyer, G. (Max-Planck-Institut fuer Eisenforschung GmbH, Duesseldorf (Germany). Abt. Werkstofftechnik)

    1992-02-01

    The application of reinforced metal matrix composites reinforced by continuous fibres are in particular limited by the lack of inexpensive and high-strength reinforcement fibres. Starting-points for a solution offer new methods of rapid solidification technology such as the in-rotating-liquid spinning that is suitable for a broad acceptance by industry. Fundamental investigations of the influence factors and the process parameters showed the aptitude of this method. (orig.).

  6. Aluminium AA6061 Matrix Composite Reinforced with Spherical Alumina Particles Produced by Infiltration: Perspective on Aerospace Applications

    Directory of Open Access Journals (Sweden)

    Claudio Bacciarini

    2014-01-01

    Full Text Available Metal matrix composites, based on AA6061 reinforced with 60 vol% Al2O3 spherical particles, were produced by gas pressure infiltration and characterized for hardness, impulse excitation modulus, tensile properties (at room temperature and at 250°C, and machining. It was experimentally demonstrated that the novel alumina powder used in the present work does not react with the liquid Mg-containing matrix during the infiltration process. The AA6061 matrix therefore retains its ability to be strengthened by precipitation heat treatment. The latter behaviour combined with the spherical particle shape confers the studied material higher strength and better machinability in comparison with similar composites produced using standard angular alumina particles. The overall features are promising for applications in the aerospace industry, where light and strong materials are required.

  7. In Situ Synthesis Aluminum Borate Whiskers Reinforced TiB2 Matrix Composites for Application in Aluminum Reduction Cells

    Science.gov (United States)

    Zhang, Gang; Yang, Jianhong

    2013-11-01

    The TiB2 matrix ceramics reinforced by aluminum borate whiskers (Al18B4O33 w) had been prepared by the pressureless sintering method. The mechanical properties and densification behavior of the TiB2 matrix ceramics were investigated. The results showed that Al18B4O33 w was in situ synthesized by the reaction of boehmite (AlOOH) and TiB2 powders during the sintering process. Increasing the sintering temperature had benefited for densification of the TiB2 matrix ceramics. Al18B4O33 w could increase the flexural strength and Vicker's hardness. It is obtained that the maximum value Vicker's hardness with 1.81 GPa and flexural strength with 82 MPa for samples sintered at 1600°C.

  8. Polymer matrix composite materials reinforced by Tb0.3Dy0.7Fe1.9 magnetostrictive particles

    Directory of Open Access Journals (Sweden)

    L.A. Dobrzański

    2009-11-01

    Full Text Available The goal of this work was to describe manufacturing process of polymer matrix composite materials reinforced by Tb0.3Dy0.7Fe1.9 particles and to observe changes of physical properties (magnetic properties and magnetostriction of samples with randomly oriented magnetostrictive particles in epoxy matrix and with aligning these particles in the matrix during fabrication process.Design/methodology/approach: Polymer matrix composite materials reinforced by the Tb0.3Dy0.7Fe1.9 magnetostrictive particles fabricating method was developed during the investigations, making it possible to obtain materials with good physical properties. The influence of the concentration of the Td0.3Dy0.7Fe1.9 particles on magnetic and magnetostrictive properties was estimated. Metallographic examination of powder’s morphology as well as EDS and XRD analysis and observations the structure of composite materials were made.Findings: The influence of magnetic particle alignment is observed in the magnetic and magnetostriction responses. The magnetostrictive response improves when the magnetic particles are oriented in magnetic fields and reaches approximately 184 ppm for oriented composite materials with 25% volume fraction of Td0.3Dy0.7Fe1.9 particles.Practical implications: For potential applications in technological devices, such as sensors and actuators, it is desirable to form composite systems by combining magnetostrictive phases with matrix, in order to have giant magnetostrictive effect and, at the same time, to reduce disadvantages of monolithic material.Originality/value: The originality of this work is based on manufacturing process, especially of applying magnetic alignment for ordering Td0.3Dy0.7Fe1.9 particles during polymerization of epoxy matrix.

  9. Tribological Wear Behaviour and Hardness Measurement of SiC, Al2O3 Reinforced Al. Matrix Hybrid Composite

    Science.gov (United States)

    Subramanian, Senthil Murugan; Vijayan, Jegan; Muthaiah, Velmurugan

    2017-01-01

    In the present study, Aluminium Matrix Hybrid Composite (AMHC) of 6061-T6 alloy reinforced with silicon carbide (SiC) particulate and further addition of aluminium oxide (Al2O3) particulate was fabricated by stir casting process. The wear resistance and frictional properties of that AMHC were studied by performing dry sliding wear test using a pin on disk wear tester. The experiments were conducted at a constant sliding velocity of 1.57 m/s and sliding distance of 1800 m under loading conditions of 10 and 20 N. Further tests were also carried out by keeping Al2O3 percentage (7%) constant and increasing the SiC percentage (10, 15, and 20%). The results show that the reinforcement of the metal matrix with SiC and Al2O3 reduces the wear rate range and also indicate that the wear of the test specimen increases with the increasing load and sliding distance. The coefficient of friction increases with load and increasing volume content of reinforcement. The worn surfaces were examined by scanning electron microscope to study the wear mechanism. By using wear mechanism analysis, the wear surfaces and wear properties of AMHC were determined.

  10. Study on dry friction and wear resistance of a WC-Co particle reinforced iron matrix composite material

    Directory of Open Access Journals (Sweden)

    Zhang Peng

    2013-05-01

    Full Text Available In order to select a suitable material for the rolling mill guide application, the dry sliding friction and wear resistance of a tungsten carbide combining cobalt (WC-Co particle reinforced chromium cast iron composite material were studied. In particular, the wear resistance was discussed in detail. The results showed that the composite material demonstrates 25 times the wear resistance of high Cr cast iron, and 9 times the wear resistance of heat resistant steel. However, the average friction factor in the stable friction stage showed a relationship of μComposites/45 # steel > μHigh chromium cast iron/45 # steel > μHeat resistant steel/45 # steel. The wear resistance mechanism of the composite material was associated with the reinforcing particles, which protruded from the worn surface to bear the friction load when the matrix material surface was worn, thereby reducing the abrasive and adhesive wear. In addition, the matrix material possessed suitable hardness and toughness, providing a support to the reinforcements.

  11. Fundamental Studies of Low Velocity Impact Resistance of Graphite Fiber Reinforced Polymer Matrix Composites. Ph.D. Thesis

    Science.gov (United States)

    Bowles, K. J.

    1985-01-01

    A study was conducted to relate the impact resistance of graphite fiber reinforced composites with matrix properties through gaining an understanding of the basic mechanics involved in the deformation and fracture process, and the effect of the polymer matrix structure on these mechanisms. It was found that the resin matrix structure influences the composite impact resistance in at least two ways. The integration of flexibilizers into the polymer chain structure tends to reduce the T sub g and the mechanical properties of the polymer. The reduction in the mechanical properties of the matrix does not enhance the composite impact resistance because it allows matrix controlled failure to initiate impact damage. It was found that when the instrumented dropweight impact tester is used as a means for assessing resin toughness, the resin toughness is enhanced by the ability of the clamped specimen to deflect enough to produce sufficient membrane action to support a significant amount of the load. The results of this study indicate that crossplied composite impact resistance is very much dependent on the matrix mechanical properties.

  12. Demineralized bone matrix and human cancellous bone enhance fixation of titanium implants

    DEFF Research Database (Denmark)

    Babiker, Hassan; Ding, Ming; Overgaard, Søren

    Denmark, DenmarkAbstractReplacement of extensive local bone loss especially in revision joint arthroplasty and spine fusion is a significant clinical challenge. Allograft and autograft have been considered as gold standard for bone replacement. However, there are several disadvantages such as donor site...... from human tissue were included (IsoTis OrthoBiologics, Inc. USA). Both materials are commercially available. Titanium alloy implants (Biomet Inc.) of 10 mm in length and 10 mm in diameter were inserted bilaterally into the femoral condyles of 8 skeletally mature sheep. Thus four implants...... with a concentric gap of 2 mm were implanted in each sheep. The gap was filled with: DBM; DBM/CB with ratio of 1/3; DBM/allograft with ratio of 1/3; or allograft (Gold standard), respectively. Standardised surgical procedure was used1. At sacrifice, 6 weeks after surgery, both distal femurs were harvested...

  13. Investigation of Mechanical Properties of Aluminium Based Metal Matrix Composites Reinforced With Sic & Al2O3

    Directory of Open Access Journals (Sweden)

    Kamaal Haider

    2015-09-01

    Full Text Available Present study is focused on the fabrication of aluminium 6061 based metal matrix composites, Reinforced with silicon carbide and Al2O3 by stir casting technique. The percentage of one reinforcement particulate is kept constant and varying other and vice versa, namely typeI and typeII composites. The various mechanical tests like tensile strength test, hardness test, wear test and Impact strength performed on the samples obtained by stir casting technique for comparison purpose. The result indicated that the developed method is quite successful and there is an increase in the value of tensile strength, hardness value and Impact strength of newly developed composite having (SiC + Al2O3 particulates in comparison to the Aluminium.

  14. Properties of AlSi9Mg Alloy Matrix Composite Reinforced with Short Carbon Fibre after Remelting

    Directory of Open Access Journals (Sweden)

    Łągiewka M.

    2015-09-01

    Full Text Available The presented work describes the results of examination of the mechanical properties of castings made either of AlSi9Mg alloy matrix composite reinforced with short carbon fibre or of the pure AlSi9Mg alloy. The tensile strength, the yield strength, Young’s modulus, and the unit elongation were examined both for initial castings and for castings made of the remelted composite or AlSi9Mg alloy. After preparing metallographic specimens, the structure of the remelted materials was assessed. A few non-metallic inclusions were observed in the structure of the remelted composite, not occurring in the initial castings. Mechanical testing revealed that all the examined properties of the initial composite material exceed those of the non-reinforced matrix. A decrease in mechanical properties was stated both for the metal matrix and for the composite after the remelting process, but this decrease was so slight that it either does not preclude them from further use or does not restrict the range of their application.

  15. Crack initiation and propagation behavior of WC particles reinforced Fe-based metal matrix composite produced by laser melting deposition

    Science.gov (United States)

    Wang, Jiandong; Li, Liqun; Tao, Wang

    2016-08-01

    It is generally believed that cracks in metal matrix composites (MMC) parts manufacturing are crucial to the reliable material properties, especially for the reinforcement particles with high volume fraction. In this paper, WC particles (WCp) reinforced Fe-based metal matrix composites (WCp/Fe) were manufactured by laser melting deposition (LMD) technology to investigate the characteristics of cracks formation. The section morphology of composites were analyzed by optical microscope (OM), and microstructure of WCp, matrix and interface were analyzed by X-ray diffraction (XRD) and scanning electron microscopy (SEM), in order to study the crack initiation and propagation behavior under different laser process conditions. The temperature of materials during the laser melting deposition was detected by the infrared thermometer. The results showed that the cracks often appeared after five layers laser deposition in this experiment. The cracks crossed through WC particles rather than the interface, so the strength of interface obtained by the LMD was relatively large. When the thermal stress induced by high temperature gradient during LMD and the coefficient of thermal expansion mismatch between WC and matrix was larger than yield strength of WC, the cracks would initiate inside WC particle. Cracks mostly propagated along the eutectic phases whose brittleness was very large. The obtained thin interface was beneficial to transmitting the stress from particle to matrix. The influence of volume fraction of particles, laser power and scanning speed on cracks were investigated. This paper investigated the influence of WC particles size on cracks systematically, and the smallest size of cracked WC in different laser processing parameters was also researched.

  16. REINFORCED COMPOSITE PANEL

    DEFF Research Database (Denmark)

    2003-01-01

    A composite panel having front and back faces, the panel comprising facing reinforcement, backing reinforcement and matrix material binding to the facing and backing reinforcements, the facing and backing reinforcements each independently comprising one or more reinforcing sheets, the facing...... by matrix material, the facing and backing reinforcements being interconnected to resist out-of-plane relative movement. The reinforced composite panel is useful as a barrier element for shielding structures, equipment and personnel from blast and/or ballistic impact damage....

  17. REINFORCED COMPOSITE PANEL

    DEFF Research Database (Denmark)

    2003-01-01

    A composite panel having front and back faces, the panel comprising facing reinforcement, backing reinforcement and matrix material binding to the facing and backing reinforcements, the facing and backing reinforcements each independently comprising one or more reinforcing sheets, the facing rein...... by matrix material, the facing and backing reinforcements being interconnected to resist out-of-plane relative movement. The reinforced composite panel is useful as a barrier element for shielding structures, equipment and personnel from blast and/or ballistic impact damage....

  18. The effect of extracellular matrix proteins on the cellular response of HUVECS and HOBS after covalent immobilization onto titanium.

    Science.gov (United States)

    Heller, Martin; Kämmerer, Peer W; Al-Nawas, Bilal; Luszpinski, Marie-Anne; Förch, Renate; Brieger, Jürgen

    2015-06-01

    Biomimetic surface modifications are regarded as promising approach to stimulate cellular behavior at the interface of implant materials. Aim of the study was an evaluation of the cellular response of human umbilical cord cells (HUVECS) and human osteoblasts (HOBS) on titanium covalently coated with the extracellular matrix (ECM) proteins fibrinogen, collagen, laminin, and osteopontin. For the surface modification, titanium discs were first amino-functionalized by plasma polymerization of allylamine. The ECM protein conjugation was performed using the linker molecule α, ω-bis-N-hydroxysuccinimide polyethylene glycol (Di-NHS linker). For surface characterization, infrared spectroscopy and fluorescein isothiocyanate staining (FITC) were used to evaluate the presence and distribution of primary amines in the plasma polymer film. Real-time analyses of the respective protein conjugation processes were performed via surface plasmon resonance kinetic measurements. All ECM proteins were immobilized successfully. Furthermore, the biological functionality of the conjugated factors fibronectin and collagen could be proven as they led to a distinct stimulation of cell adhesion of HUVECS and HOBS when compared to the control group. The highest cell coverage of HUVECS was observed on fibronectin-modified surfaces with approximately 35% and on collagen with 33% after 24 h (PT: 9.4%). For laminin, no additional effect was observed, and for osteopontin, only a slight enhancement of cell adhesion was found. A similar, cell-stimulating tendency of fibronectin and collagen was seen as well after 3 and 7 days. Biomimetic surface modification via plasma polymerization is a powerful method for biomolecule conjugation with a high retention of biological functionality and offer promising clinical perspectives.

  19. An Investigation of Stimulating the Autoclave Curing Process of Resin Matrix/Fiber Reinforced Composite Material,Ⅰ: Process model

    Institute of Scientific and Technical Information of China (English)

    2003-01-01

    A mathematical model is made which describes the curing process of composites constructed from continuous fiber-reinforced, thermosetting resin matrix prepreg materials, and the consolidation of the composite is developed. The model provides the variation of temperature distribution, the cure reaction process in the resin, the resin flow and fibers stress inside the composite, and the void variation and the residual stress distribution. It can be used to illustrate the mechanism of curing process and optimize the cure cycle of composite material in order to ensure the quality of a product.

  20. Buttressing staples with cholecyst-derived extracellular matrix (CEM) reinforces staple lines in an ex vivo peristaltic inflation model.

    LENUS (Irish Health Repository)

    Burugapalli, Krishna

    2008-11-01

    Staple line leakage and bleeding are the most common problems associated with the use of surgical staplers for gastrointestinal resection and anastomotic procedures. These complications can be reduced by reinforcing the staple lines with buttressing materials. The current study reports the potential use of cholecyst-derived extracellular matrix (CEM) in non-crosslinked (NCEM) and crosslinked (XCEM) forms, and compares their mechanical performance with clinically available buttress materials [small intestinal submucosa (SIS) and bovine pericardium (BP)] in an ex vivo small intestine model.

  1. The Impact of Methods of Forming on the Mechanical Properties of Fiber-reinforced Polymer-matrix Composite Materials

    Directory of Open Access Journals (Sweden)

    Piernik Krzysztof

    2015-11-01

    Full Text Available The aim of this paper was to analyze how different techniques of production of fibrous composite materials affect the quality and strength properties of composite laminates. In this study, we use experimental data concerning a composite fabricated with the by hand lay-up and vacuum bagging method. The composites have a polyester matrix (Firestop 8175-w-1 reinforced with mate-glass fiber fabric [0/90/0/90] E glass fiber, respectively. The process parameters and criteria were determined before the samples were cut, namely the amount and soaking time of the composite with the polymer resin.

  2. The correlation of low-velocity impact resistance of graphite-fiber-reinforced composites with matrix properties

    Science.gov (United States)

    Bowles, K. J.

    1986-01-01

    Summarized are basic studies that were conducted to correlate the impact resistance of graphite-fiber-reinforced composites with polymer matrix properties. Three crosslinked epoxy resins and a linear polysulfone were selected as composite matrices. As a group, these resins possess a significantly large range of mechanical properties. The mechanical properties of the resins and their respective composites were measured. Neat resin specimens and unidirectional and crossply composite specimens were impact tested with an instrumented dropweight tester. Impact resistances of the specimens were assessed on the basis of loading capability, energy absorption, and extent of damage.

  3. In situ formation of titanium carbide using titanium and carbon-nanotube powders by laser cladding

    Energy Technology Data Exchange (ETDEWEB)

    Savalani, M.M., E-mail: mmfsmm@inet.polyu.edu.hk [Department of Industrial and Systems Engineering, Hong Kong Polytechnic University (Hong Kong); Ng, C.C.; Li, Q.H.; Man, H.C. [Department of Industrial and Systems Engineering, Hong Kong Polytechnic University (Hong Kong)

    2012-01-15

    Titanium metal matrix composite coatings are considered to be important candidates for high wear resistance applications. In this study, TiC reinforced Ti matrix composite layers were fabricated by laser cladding with 5, 10, 15 and 20 wt% carbon-nanotube. The effects of the carbon-nanotube content on phase composition, microstructure, micro-hardness and dry sliding wear resistance of the coating were studied. Microstructural observation using scanning electron microscopy showed that the coatings consisted of a matrix of alpha-titanium phases and the reinforcement phase of titanium carbide in the form of fine dendrites, indicating that titanium carbide was synthesized by the in situ reaction during laser irradiation. Additionally, measurements on the micro-hardness and dry sliding wear resistance of the coatings indicated that the mechanical properties were affected by the amount of carbon-nanotube in the starting precursor materials and were enhanced by increasing the carbon-nanotube content. Results indicated that the composite layers exhibit high hardness and excellent wear resistance.

  4. Effect of Moisture Absorption Behavior on Mechanical Properties of Basalt Fibre Reinforced Polymer Matrix Composites

    Directory of Open Access Journals (Sweden)

    Amuthakkannan Pandian

    2014-01-01

    Full Text Available The study of mechanical properties of fibre reinforced polymeric materials under different environmental conditions is much important. This is because materials with superior ageing resistance can be satisfactorily durable. Moisture effects in fibre reinforced plastic composites have been widely studied. Basalt fibre reinforced unsaturated polyester resin composites were subjected to water immersion tests using both sea and normal water in order to study the effects of water absorption behavior on mechanical properties. Composites specimens containing woven basalt, short basalt, and alkaline and acid treated basalt fibres were prepared. Water absorption tests were conducted by immersing specimens in water at room temperature for different time periods till they reached their saturation state. The tensile, flexural, and impact properties of water immersed specimens were conducted and compared with dry specimens as per the ASTM standard. It is concluded that the water uptake of basalt fibre is considerable loss in the mechanical properties of the composites.

  5. Numerical Simulation of Dynamic Response of Fiber Reinforced Ceramic Matrix Composite Beam with Matrix Cracks Using Multiscale Modeling

    Institute of Scientific and Technical Information of China (English)

    Gao Xiguang; Song Yingdong; Sun Zhigang; Hu Xuteng

    2010-01-01

    A multiscale method for simulating the dynamic response of ceramic matrix composite (CMC) with matrix cracks is developed.At the global level,the finite element method is employed to simulate the dynamic response ofa CMC beam.While at the local level,the multiscale mechanical method is used to estimate the stress/strain response of the material.A distributed computing system is developed to speed up the simulation.The simulation of dynamic response of a Nicalon/CAS-Ⅱ beam being subjected to harmonic loading is performed as a numerical example.The results show that both the stress/strain responses under tension and compressive loading are nonlinear.These conditions result in a different response compared with that of elastic beam,such as:1) the displacement response is not symmetric about the axis of time;2) in the condition of small external load,the response at first order natural frequency is limited within a finite range;3) decreasing the matrix crack space will increase the displacement response of the beam.

  6. Effect of thermal residual stresses on yielding behavior under tensile or compressive loading of short fiber reinforced metal matrix composite

    Institute of Scientific and Technical Information of China (English)

    丁向东; 连建设; 江中浩; 孙军

    2001-01-01

    Using large strain two-dimension axisymmetric elasto-plastic finite element method and the modified law of mixture, the effects of thermal residual stresses on the yielding behavior of short fiber reinforced metal matrix composite and their dependencies on the material structure parameters (fiber volume fraction, fiber aspect ratio and fiber end distance) were studied. It is demonstrated that the stress-strain partition parameter can be used to describe the stress transfer from the matrix to the fiber. The variation of the second derivation of the stress-strain partition parameter can be used to determine the elastic modulus, the proportion limit, the initial and final yield strengths. In the presence of thermal residual stress, these yielding properties are asymmetric and are influenced differently by the material structure parameters under tensile and compressive loadings.

  7. Effects of fibre content on mechanical properties and fracture behaviour of short carbon fibre reinforced geopolymer matrix composites

    Indian Academy of Sciences (India)

    Tiesong Lin; Dechang Jia; Meirong Wang; Peigang He; Defu Liang

    2009-02-01

    Geopolymer matrix composites reinforced with different volume fractions of short carbon fibres (Cf/geopolymer composites) were prepared and the mechanical properties, fracture behaviour and microstructure of as-prepared composites were studied and correlated with fibre content. The results show that short carbon fibres have a great strengthening and toughening effect at low volume percentages of fibres (3.5 and 4.5 vol.%). With the increase of fibre content, the strengthening and toughening effect of short carbon fibres reduce, possibly due to fibre damage, formation of high shear stresses at intersect between fibres and strong interface cohesion of fibre/matrix under higher forming pressure. The property improvements are primarily based on the network structure of short carbon fibre preform and the predominant strengthening and toughening mechanisms are attributed to the apparent fibre bridging and pulling-out effect.

  8. Development and analysis of three-dimensionally reinforced cellular matrix composites

    Science.gov (United States)

    Xu, Wei

    2000-10-01

    The objective of this research was to develop a new class of lightweight three-dimensional textile reinforced cellular matrix composite (3-D CMC) materials using a high-pressure foaming method. The scope of the research includes fabrication, experimental evaluation and mathematical modeling of the new composite materials. Principles of thermodynamics and transport phenomena involved in the cell nucleation and bubble growth in plastics using gas blowing agents were reviewed. The determinative factors for the foaming process were the foaming pressure, surface tension, viscous and inertial resistance forces. Foaming of epoxy resins by pressure quenching were carried out using a high-pressure vessel with a digital temperature controller and nitrogen gas as the blowing agent, at 100°C and 28--110.5 bar. The cure time was 2--2.5 hr., well before the time of gel point, 293 min., determined by means of dynamic mechanical spectroscopy. It was found that the foam density decreased monotonously and the average bubble radius slightly decreased, while the cell density increased, with the increasing foaming pressure. Cure time of 2 and 2.5 hours have no influence on the foam density, but have opposite influences on the bubble radius and cell density. Samples of 3-D woven carbon CMC materials were fabricated using the high-pressure foaming apparatus at a foaming pressure of 60 bar as the epoxy resin cured for 1.5--2 hr. at 100°C. Photomicrographs of cross-sections of the samples revealed that the epoxy resins in the epoxy pockets of the 3-D CMC samples were removed during foaming. Average density was found 1.009 g/cm 3 for TM samples and 1.076 g/cm3 for TS samples, corresponding to weight reduction of 36.92% and 28.37%, respectively, as compared with the 3-D RMC material, where TM and TS samples used 3-D woven carbon preforms of different weaving parameters. Tensile test, 3-point bending and high velocity projectile impact test were conducted to evaluate the mechanical

  9. Effect of fiber distribution on residual thermal stress in titanium matrix composite

    Institute of Scientific and Technical Information of China (English)

    马志军; 杨延清; 朱艳; 陈彦

    2004-01-01

    Residual thermal stresses (RTS) of SCS-6 SiC/Ti-24Al-11Nb composite were analyzed by using finite element method (FEM). Three models of fiber array in the composite and the effect of fiber distance on the RTS were discussed. In all the three models compressive stress was found in the radial direction and tensile stress in the tangential direction. It is pointed out that, in real composite system, hexagonal fiber geometry is superior because the distribution and the magnitude of the residual stress are similar to those in single fiber model. In square fiber geometry, it is easier to make the matrix crack due to the larger residual tangential stress. RTS becomes very large and changes violently when the fiber distance is less than 15μm or so, therefore too high fiber volume is apt to result in matrix crack.

  10. CNT-based Reinforcing Polymer Matrix Composites for Lightweight Structures Project

    Data.gov (United States)

    National Aeronautics and Space Administration — Carbon Polymer Matrix Composites (PMCs) are attractive structural materials for NASA applications due to their high strength to weight ratio, mechanical properties...

  11. Part I. Corrosion studies of continuous alumina fiber reinforced aluminum-matrix composites. Part II. Galvanic corrosion between continuous alumina fiber reinforced aluminum-matrix composites and 4340 steel

    Science.gov (United States)

    Zhu, Jun

    Part I. The corrosion performance of continuous alumina fiber reinforced aluminum-matrix composites (CF-AMCs) was investigated in both the laboratory and field environments by comparing them with their respective monolithic matrix alloys, i.e., pure Al, A1-2wt%Cu T6, and Al 6061 T6. The corrosion initiation sites were identified by monitoring the changes in the surface morphology. Corrosion current densities and pH profiles at localized corrosion sites were measured using the scanning-vibrating electrode technique and the scanning ion-selective electrode technique, respectively. The corrosion damage of the materials immersed in various electrolytes, as well as those exposed in a humidity chamber and outdoor environments, was evaluated. Potentiodynamic polarization behavior was also studied. The corrosion initiation for the composites in 3.15 wt% NaCl occurred primarily around the Fe-rich intermetallic particles, which preferentially existed around the fiber/matrix interface on the composites. The corrosion initiation sites were also caused by physical damage (e.g., localized deformation) to the composite surface. At localized corrosion sites, the buildup of acidity was enhanced by the formation of micro-crevices resulting from fibers left in relief as the matrix corroded. The composites that were tested in exposure experiments exhibited higher corrosion rates than their monolithic alloys. The composites and their monolithic alloys were subjected to pitting corrosion when anodically polarized in the 3.15 wt% NaCl, while they passivated when anodically polarized in 0.5 M Na2SO4. The experimental results indicated that the composites exhibited inferior corrosion resistance compared to their monolithic matrix alloys. Part II. Galvanic corrosion studies were conducted on CF-AMCs coupled to 4340 steel since CF-AMCs have low density and excellent mechanical properties and are being considered as potential jacketing materials for reinforcing steel gun barrels. Coupled and

  12. Micro/Nanostructure and Tribological Characteristics of Pressureless Sintered Carbon Nanotubes Reinforced Aluminium Matrix Composites

    Directory of Open Access Journals (Sweden)

    P. Manikandan

    2016-01-01

    Full Text Available This study reports the manufacture, microstructure, and tribological behaviour of carbon nanotube reinforced aluminium composites against pure aluminium. The specimens were fabricated using powder metallurgy method. The nanotubes in weight percentages of 0.5, 1.0, 1.5, and 2.0 were homogeneously dispersed and mechanically alloyed using a high energy ball milling. The milled powders were cold compacted and then isothermally sintered in air. The density of all samples was measured using Archimedes method and all had a relative density between 92.22% and 97.74%. Vickers hardness increased with increasing CNT fraction up to 1.5 wt% and then reduced. The microstructures and surfaces were investigated using high resolution scanning electron microscope (SEM. The tribological tests showed that the CNT reinforced composites displayed lower wear rate and friction coefficient compared to the pure aluminium under mild wear conditions. However, for severe wear conditions, the CNT reinforced composites exhibited higher friction coefficient and wear rate compared to the pure aluminium. It was also found that the friction and wear behaviour of CNT reinforced composites is significantly dependent on the applied load and there is a critical load beyond which CNTs could have adverse impact on the wear resistance of aluminium.

  13. Prediction of thermal strains in fibre reinforced plastic matrix by discretisation of the temperature exposure history

    Science.gov (United States)

    Ngoy, E. K.

    2016-07-01

    Prediction of environmental effects on fibre reinforced plastics habitually is made difficult due to the complex variability of the natural service environment. This paper suggests a method to predict thermal strain distribution over the material lifetime by discretisation of the exposure history. Laboratory results show a high correlation between predicted and experimentally measured strain distribution

  14. Strain redistribution around holes and notches in fiber-reinforced cross-woven brittle matrix composites

    DEFF Research Database (Denmark)

    Jacobsen, Torben Krogsdal; Brøndsted, Povl

    1997-01-01

    Mechanics, and an identification procedure based on a uni-axial tensile test and a shear test the strain redistribution around a hole or a notch due to matrix cracking can be predicted. Damage due to fiber breakage is not included in the model. Initial matrix damage in the C-f/SiCm material has...

  15. Titanium dioxide nanoparticles induce matrix metalloprotease 1 in human pulmonary fibroblasts partly via an interleukin-1β-dependent mechanism.

    Science.gov (United States)

    Armand, Lucie; Dagouassat, Maylis; Belade, Esther; Simon-Deckers, Angélique; Le Gouvello, Sabine; Tharabat, Chantal; Duprez, Corinne; Andujar, Pascal; Pairon, Jean-Claude; Boczkowski, Jorge; Lanone, Sophie

    2013-03-01

    Exposure to titanium dioxide (TiO2) nanoparticles (NPs) is associated with lung remodeling, but the underlying mechanisms are unknown. Matrix metalloprotease (MMP)-1 is an important actor in matrix homeostasis and could therefore participate in TiO2 NP effects. Our aim was to evaluate the effects of TiO2 NPs on MMP-1 expression and activity in lung pulmonary fibroblasts and to understand the underlying mechanisms and assess the importance of the physicochemical characteristics of the particles in these effects. Human pulmonary fibroblasts (MRC-5 cell line and primary cells) were exposed to 10 or 100 μg/cm(2) TiO2 (two anatases, two anatase/rutile mix, one rutile NP, and one micrometric) and carbon black (CB) NPs for 6 to 48 hours. We examined cell viability, MMP-1 expression and activity, and the implication of oxidative stress, transforming growth factor (TGF)-β, extracellular MMP inducer, and IL-1β in MMP-1 expression. All TiO2 NPs induced MMP-1 (mRNA and protein expression), repression of procollagen-1, and α-actin expression, but only the two anatase/rutile mix induced MMP-1 activity. Micrometric TiO2 had smaller effects than TiO2 NPs, and CB NPs did not induce MMP-1. MMP-1 induction by TiO2 NPs was not related to TGF-β, oxidative stress, or EMPRIN expression but was related to IL-1β expression, which partly drives MMP-1 induction by two TiO2 NPs (one anatase/rutile mix and the rutile one). Taken together, our results show that TiO2 NPs are potent inducers and regulators of MMP-1 expression and activity, partly via an IL-1β-dependent mechanism. This may explain TiO2 lung remodeling effects.

  16. Cathodic Polarization Coats Titanium Based Implant Materials with Enamel Matrix Derivate (EMD

    Directory of Open Access Journals (Sweden)

    Matthias J. Frank

    2014-03-01

    Full Text Available The idea of a bioactive surface coating that enhances bone healing and bone growth is a strong focus of on-going research for bone implant materials. Enamel matrix derivate (EMD is well documented to support bone regeneration and activates growth of mesenchymal tissues. Thus, it is a prime candidate for coating of existing implant surfaces. The aim of this study was to show that cathodic polarization can be used for coating commercially available implant surfaces with an immobilized but functional and bio-available surface layer of EMD. After coating, XPS revealed EMD-related bindings on the surface while SIMS showed incorporation of EMD into the surface. The hydride layer of the original surface could be activated for coating in an integrated one-step process that did not require any pre-treatment of the surface. SEM images showed nano-spheres and nano-rods on coated surfaces that were EMD-related. Moreover, the surface roughness remained unchanged after coating, as it was shown by optical profilometry. The mass peaks observed in the matrix-assisted laser desorption/ionization time-of-flight mass spectroscopy (MALDI-TOF MS analysis confirmed the integrity of EMD after coating. Assessment of the bioavailability suggested that the modified surfaces were active for osteoblast like MC3M3-E1 cells in showing enhanced Coll-1 gene expression and ALP activity.

  17. Effect of Matrix Composition on Physical Properties of Al3CON In-situ Reaction Reinforced Corundum Composite

    Institute of Scientific and Technical Information of China (English)

    YANG Dingao; YUAN Shouqian; JIANG Mingxue; ZHANG Changxi; ZHENG Jianying; LIANG De'an; ZHANG Qiye

    2008-01-01

    60% white corundum used for aggregate.5% aluminium powder for fixed additions and 35% various additives for matrix were prepared for specimens 1#,2#,3#.They were mixed uniformly with the suitable resin as a binder and pressed under pressure of 315 ton forging press,then dried at 200 ℃ for 24 h.Effects of various additives on 1500 ℃×2 h creep properties of Al3CON reinforced corundum composite were researched,The experimenal results show that creep coefficients of specimens 1#,2#,3# at 1500 ℃×2 h are 1.4×10-4,-9.4×10 4,-22.6×10-4 respectively.Crushing strength of the slide plate added with suitable additive A after fired at 1500 ℃×3 h reaches to 225 MPa,the creep rate is positive all the time from 0% to 0.014% at 1500 ℃ for 2 h.The microstructure result analysis shows that reinforced phases of Al3CON fiber composite have been formed after fired with Al powder in coke at high temperatures for specimen 1#,and the strength of the composite is increased.The hot modulus of rupture is up to 59 MPa at 1400 ℃ and the RUL is obviously higher than that at 1700 ℃.Its service life is two times as that of Al2O3-C slide plate when used in the process of pouring steel.The mechanism of creep rate resistance of the composites can be discovered by means of SEM and EDAX analysis.It is concluded that the active Al3CON and Al2O3 multiphases that were formed by N2 in gas,C,Al and Al2O3 inside the matrix of the composites during in-situ reaction,which gives the composites outstanding creep rate resistance for the dense zone resulting from Al3CON oxidation that inhibits contraction at the high temperature.Besides,the matrix will turn into the multiphase with high refractoriness,N content and its Al3CON reinforced fiber will further increase accordingly.In addition,Al3CON formed by Al2O3 and C,Al in the matrix with N2 in gas will inhibit the creep rate and also greatly improve the creep rate resistance of the composites.

  18. Research Situation and Application Prospects of Laser Cladding Metal-based Titanium Carbide Reinforced Coating%激光熔覆金属基碳化钛强化涂层的研究现状及应用前景

    Institute of Scientific and Technical Information of China (English)

    贺长林; 陈少克; 周中河; 陈琼雁; 舒俊

    2013-01-01

    介绍了激光熔覆金属基碳化钛的研究现状和应用进展.分别从直接熔覆碳化钛、原位合成碳化钛增强相及稀土对碳化钛增强相的改性作用三个方面介绍了其研究进展.从碳化钛的物理、化学性能出发,介绍了不同熔覆方法、不同熔覆粉末、不同基体对熔覆层组织和性能的影响.%The laser cladding metal based titanium carbide research present status and application development were introduced.The research progress from three respects separately:direct cladding titanium carbide,synthesis titanium carbide reinforcing phase,rare earth's modification on titanium carbide reinforced phase was introduced.From the physical and chemical properties of titanium carbide,the effects of cladding methods,cladding powders and substrates on the microstructure and properties of the cladding layer were introduced.

  19. Structure and properties of a pulp fibre-reinforced composite with regenerated cellulose matrix

    Science.gov (United States)

    Gindl, W.; Schöberl, T.; Keckes, J.

    2006-04-01

    Fully bio-based cellulose cellulose composites were produced by partly dissolving beech pulp fibres in lithium chloride/dimethylacetamide (LiCl/DMAc) and subsequent regeneration of matrix cellulose in the presence of undissolved fibres. Compared to cellulose epoxy composites produced from the same fibres, a two-fold increase in tensile strength and elastic modulus was observed for cellulose cellulose composites. From scanning electron microscopy and nanoindentation it is concluded that changes in the fibre cell wall during LiCl/DMAc treatment, improved matrix properties of regenerated cellulose compared to epoxy, and improved fibre matrix adhesion are responsible for the superior properties of cellulose cellulose composites.

  20. Interphase for ceramic matrix composites reinforced by non-oxide ceramic fibers

    Science.gov (United States)

    DiCarlo, James A. (Inventor); Bhatt, Ramakrishna (Inventor); Morscher, Gregory N. (Inventor); Yun, Hee-Mann (Inventor)

    2008-01-01

    A ceramic matrix composite material is disclosed having non-oxide ceramic fibers, which are formed in a complex fiber architecture by conventional textile processes; a thin mechanically weak interphase material, which is coated on the fibers; and a non-oxide or oxide ceramic matrix, which is formed within the interstices of the interphase-coated fiber architecture. During composite fabrication or post treatment, the interphase is allowed to debond from the matrix while still adhering to the fibers, thereby providing enhanced oxidative durability and damage tolerance to the fibers and the composite material.

  1. Synthesis of gels with basis of titanium tungstates as matrixes of radioactive generators; Sintesis de geles a base de titanio tungstenatos como matrices de generadores radiactivos

    Energy Technology Data Exchange (ETDEWEB)

    Galico C, L

    2005-07-01

    The heteropolyanions, compounds formed by the union of molybdates or tungstates polyanions with atoms of metals like zirconium, titanium, cerium, thorium, tin, etc., have been used as generator matrixes of {sup 99m} Tc or {sup 188} Re. Particularly they have been studied and produced successfully in our laboratory, generators of {sup 99} Mo/ {sup 99}m Tc at basis of gels zirconium molybdates and titanium molybdates. Considering that the molybdenum and tungsten, as well as the technetium and the rhenium, its belong to the same groups of transition metals, it is feasible that gels can be synthesized at basis of titanium tungstates, continuing a methodology similar to that of the gels titanium molybdates or zirconium molybdates, to produce generators {sup 188} W/ {sup 188} Re. The {sup 188} Re possess nuclear characteristics that make it attractive for therapeutic applications, since, it emits {beta}{sup -} particles of a great energy (2.12 MeV); joined to the possibility of being able to unite to different ligands (bifunctional agents) and biomolecules (antibodies or fragments of proteins), as it makes the {sup 99m} Tc, useful in radioimmunotherapy. Commercially the {sup 188} Re generators use a chromatographic column loaded with alumina where the {sup 188} Re, it is adsorbed and eluted the {sup 188} ReO{sub 4}{sup -} by means of a saline solution The alumina adsorbs around 0.2% of the {sup 188} Re, situation that forces to use {sup 188} Re of a high specific activity. The use of the gels technology, allows to work with medium or low specific activities of {sup 188} Re, opening the possibility of their production in countries whose nuclear capacity is medium or low. In particular, the synthesized gels with basis of titanium offer the possibility of being synthesized with non active material, for later on to be irradiated and directly produce the generator, since, the titanium {sup 51} Ti, unique radioisotope produced by the titanium, has a half life of 5.79 min. This

  2. Study on Processing Conditions of Aluminum Matrix Composites Reinforced with Boron Carbide Particles

    Institute of Scientific and Technical Information of China (English)

    Fu Xueying; Zhang Hong; Xi Huizhi; Yi Xiaosu

    2004-01-01

    Different pre-heating of boron carbide particles for reinforcement and different processing conditions were studied in this work. Being one of the most cost-effective industrial methods, conventional melt stir-casting route was utilized.Result showed that the boron carbide particles distributed well for a suitable pre-heating temperature and processed in air.No reaction product was found at the A1-B4C interfaces at the resolution limit of SEM used in that way.

  3. Microstructure and hardness of WC-Co particle reinforced iron matrix surface composite

    OpenAIRE

    Zhang Peng; Zeng Shaolian; Zhang Zhiguo

    2013-01-01

    In this study, a high Cr cast iron surface composite material reinforced with WC-Co particles 2-6 mm in size was prepared using a pressureless sand mold infiltration casting technique. The composition, microstructure and hardness were determined by means of energy dispersive spectrometry (EDS), electron probe microanalysis (EPMA), scanning electron microscope (SEM) and Rockwell hardness measurements. It is determined that the obtained composite layer is about 15 mm thick with a WC-Co particle...

  4. Damage Mechanisms of a TiB2-Reinforced Steel Matrix Composite for Lightweight Automotive Application

    Science.gov (United States)

    Li, Y. Z.; Luo, Z. C.; Yi, H. L.; Huang, M. X.

    2016-09-01

    The microscopic strain-and-stress fields related to primary and eutectic particles in a lightweight steel matrix composite (SMC) produced by in situ precipitation of TiB2 particles during solidification were investigated by means of microscale digital image correlation and finite element method. The damage process in this SMC is a sequential process of primary particles cracking, the fracture of the surrounding eutectic particles, and finally the growth and coalescence of voids in the ferrite matrix.

  5. Carbon nanofiber reinforced epoxy matrix composites and syntactic foams - mechanical, thermal, and electrical properties

    Science.gov (United States)

    Poveda, Ronald Leonel

    The tailorability of composite materials is crucial for use in a wide array of real-world applications, which range from heat-sensitive computer components to fuselage reinforcement on commercial aircraft. The mechanical, electrical, and thermal properties of composites are highly dependent on their material composition, method of fabrication, inclusion orientation, and constituent percentages. The focus of this work is to explore carbon nanofibers (CNFs) as potential nanoscale reinforcement for hollow particle filled polymer composites referred to as syntactic foams. In the present study, polymer composites with high weight fractions of CNFs, ranging from 1-10 wt.%, are used for quasi-static and high strain rate compression analysis, as well as for evaluation and characterization of thermal and electrical properties. It is shown that during compressive characterization of vapor grown carbon nanofiber (CNF)/epoxy composites in the strain rate range of 10-4-2800 s-1, a difference in the fiber failure mechanism is identified based on the strain rate. Results from compression analyses show that the addition of fractions of CNFs and glass microballoons varies the compressive strength and elastic modulus of epoxy composites by as much as 53.6% and 39.9%. The compressive strength and modulus of the syntactic foams is also shown to generally increase by a factor of 3.41 and 2.96, respectively, with increasing strain rate when quasi-static and high strain rate testing data are compared, proving strain rate sensitivity of these reinforced composites. Exposure to moisture over a 6 month period of time is found to reduce the quasi-static and high strain rate strength and modulus, with a maximum of 7% weight gain with select grades of CNF/syntactic foam. The degradation of glass microballoons due to dealkalization is found to be the primary mechanism for reduced mechanical properties, as well as moisture diffusion and weight gain. In terms of thermal analysis results, the

  6. The Microstructure-Processing-Property Relationships in an Al Matrix Composite System Reinforced by Al-Cu-Fe Alloy Particles

    Energy Technology Data Exchange (ETDEWEB)

    Tang, Fei [Iowa State Univ., Ames, IA (United States)

    2004-01-01

    Metal matrix composites (MMC), especially Al matrix composites, received a lot of attention during many years of research because of their promise for the development of automotive and aerospace materials with improved properties and performance, such as lighter weight and better structural properties, improved thermal conductivity and wear resistance. In order to make the MMC materials more viable in various applications, current research efforts on the MMCs should continue to focus on two important aspects, including improving the properties of MMCs and finding more economical techniques to produce MMCs. Solid state vacuum sintering was studied in tap densified Al powder and in hot quasi-isostatically forged samples composed of commercial inert gas atomized or high purity Al powder, generated by a gas atomization reaction synthesis (GARS) technique. The GARS process results in spherical Al powder with a far thinner surface oxide. The overall results indicated the enhanced ability of GARS-processed Al and Al alloy powders for solid state sintering, which may lead to simplification of current Al powder consolidation processing methods. Elemental Al-based composites reinforced with spherical Al-Cu-Fe alloy powders were produced by quasi-isostatic forging and vacuum hot pressing (VHP) consolidation methods. Microstructures and tensile properties of AYAl-Cu-Fe composites were characterized. It was proved that spherical Al-Cu-Fe alloy powders can serve as an effective reinforcement particulate for elemental Al-based composites, because of their high hardness and a preferred type of matrix/reinforcement interfacial bonding, with reduced strain concentration around the particles. Ultimate tensile strength and yield strength of the composites were increased over the corresponding Al matrix values, far beyond typical observations. This remarkable strengthening was achieved without precipitation hardening and without severe strain hardening during consolidation because of

  7. Mechanical properties of aluminium matrix composites reinforced with intermetallics; Propiedades mecanicas de materiales compuestos de matriz de aluminio reforzados con intermetalicos

    Energy Technology Data Exchange (ETDEWEB)

    Torres, B.; Garcia-Escorial, A.; Ibanez, J.; Lieblich, M.

    2001-07-01

    In this work 2124 aluminium matrix composites reinforced with Ni{sub 3}Al, NiAl, MoSi{sub 2} and Cr{sub 3}Si intermetallic powder particles have been investigated. For comparison purposes, un reinforced 2124 and reinforced with SiC have also been studied. In all cases, the same powder metallurgy route was used, i. e. the 2124 alloy was obtained by rapid solidification and the intermetallic particles by self-propagating high-temperature synthesis (SHS). The matrix and the intermetallics were mechanically blended, cold compacted and finally hot extruded. Tensile tests were carried out in T1 and T4 treatments. Results indicate that mechanical properties depend strongly on the tendency to form new phases at the matrix-intermetallic interface during processing and/or further thermal treatments. The materials which present better properties are those that present less reaction between matrix and intermetallic reinforcement, i. e. MoSi{sub 2} and SiC reinforced composites. (Author) 9 refs.

  8. Fatigue Life Prediction of Fiber-Reinforced Ceramic-Matrix Composites with Different Fiber Preforms at Room and Elevated Temperatures

    Directory of Open Access Journals (Sweden)

    Longbiao Li

    2016-03-01

    Full Text Available In this paper, the fatigue life of fiber-reinforced ceramic-matrix composites (CMCs with different fiber preforms, i.e., unidirectional, cross-ply, 2D (two dimensional, 2.5D and 3D CMCs at room and elevated temperatures in air and oxidative environments, has been predicted using the micromechanics approach. An effective coefficient of the fiber volume fraction along the loading direction (ECFL was introduced to describe the fiber architecture of preforms. The statistical matrix multicracking model and fracture mechanics interface debonding criterion were used to determine the matrix crack spacing and interface debonded length. Under cyclic fatigue loading, the fiber broken fraction was determined by combining the interface wear model and fiber statistical failure model at room temperature, and interface/fiber oxidation model, interface wear model and fiber statistical failure model at elevated temperatures, based on the assumption that the fiber strength is subjected to two-parameter Weibull distribution and the load carried by broken and intact fibers satisfies the Global Load Sharing (GLS criterion. When the broken fiber fraction approaches the critical value, the composites fatigue fracture.

  9. Cast microstructure and tribological properties of particulate TiC-reinforced Ni-base or stainless steel matrix composites

    Energy Technology Data Exchange (ETDEWEB)

    Skolianos, S. (Department of Mechanical Engineering, Aristoteles University of Thessaloniki, Thessaloniki (Greece)); Kattamis, T.Z. (Department of Metallurgy, Institute of Materials Science, University of Connecticut, Storrs, CT 06269-3136 (United States)); Chen, M. (Department of Metallurgy, Institute of Materials Science, University of Connecticut, Storrs, CT 06269-3136 (United States)); Chambers, B.V. (Department of Materials Science and Engineering, Massachusetts Institute of Technology, Cambridge, MA 02139 (United States))

    1994-06-15

    Particulate TiC-reinforced nickel, 304 stainless steel and IN-100 nickel-base superalloy matrix composites were processed by precipitating the carbide during solidification of a melt of appropriate composition at various cooling rates. The microstructure and tribological properties of prepared specimens were evaluated. The microstructures of these composites can be controlled by controlling melt composition and homogeneity, as well as cooling rate. The specific wear rate decreased with increasing volume fraction of carbide and decreasing carbide particle size and spacing. For given volume fraction of carbide and carbide particle size composites with a softer matrix exhibited a higher wear rate and vice versa. The difference in wear rate among the three types of composites slightly decreased with increasing volume fraction carbide. Microhardness increased with increasing volume fraction of carbide. The friction coefficient between a diamond stylus and the polished specimen surface decreased with increasing volume fraction of carbide and decreasing particle size and spacing. For given volume fraction of carbide and carbide particle size the friction coefficient decreased with increasing matrix microhardness. For all composites a lower friction coefficient corresponded to a higher wear resistance. ((orig.))

  10. Effect of monomer composition of polymer matrix on flexural properties of glass fibre-reinforced orthodontic archwire.

    Science.gov (United States)

    Ohtonen, J; Vallittu, P K; Lassila, L V J

    2013-02-01

    To compare force levels obtained from glass fibre-reinforced composite (FRC) archwires. Specifically, FRC wires were compared with polymer matrices having different dimethacrylate monomer compositions. FRC material (E-glass provided by Stick Tech Ltd, Turku, Finland) with continuous unidirectional glass fibres and four different types of dimethacrylate monomer compositions for the resin matrix were tested. Cross-sectionally round FRC archwires fitting into the 0.3 mm slot of a bracket were divided into 16 groups with six specimens in each group. Glass fibres were impregnated by the manufacturer, and they were initially light-cured by hand light-curing unit or additionally post-cured in light-curing oven. The FRC archwire specimens were tested at 37°C according to a three-point bending test in dry and wet conditions using a span length of 10 mm and a crosshead speed of 1.0 mm/minute. The wires were loaded until final failure. The data were statistically analysed using analysis of variance (ANOVA). The dry FRC archwire specimens revealed higher load values than water stored ones, regardless of the polymer matrix. A majority of the FRC archwires showed higher load values after being post-cured. ANOVA revealed that the polymer matrix, curing method, and water storage had a significant effect (P composition, curing method, and water storage affected the flexural properties and thus, force level and working range which could be obtained from the FRC archwire.

  11. Microstructure and Dry-Sliding Wear Behavior of B4C Ceramic Particulate Reinforced Al 5083 Matrix Composite

    Directory of Open Access Journals (Sweden)

    Qian Zhao

    2016-09-01

    Full Text Available B4C ceramic particulate–reinforced Al 5083 matrix composite with various B4C content was fabricated successfully via hot-press sintering under Argon atmosphere. B4C particles presented relative high wettability, bonding strength and symmetrical distribution in the Al 5083 matrix. The hardness value, friction coefficient and wear resistance of the composite were higher than those of the Al 5083 matrix. The augment of the B4C content resulted in the increase of the friction coefficient and decrease of the wear mass loss, respectively. The 30 wt % B4C/Al 5083 composite exhibited the highest wear resistance. At a low load of 50 N, the dominant wear mechanisms of the B4C/Al 5083 composite were micro-cutting and abrasive wear. At a high load of 200 N, the dominant wear mechanisms were micro-cutting and adhesion wear associated with the formation of the delamination layer which protected the composite from further wear and enhanced the wear resistance under the condition of high load.

  12. Corrosion and wear behaviour of Al–Mg–Si alloy matrix hybrid composites reinforced with rice husk ash and silicon carbide

    OpenAIRE

    Kenneth Kanayo Alaneme; Tolulope Moyosore Adewale; Peter Apata Olubambi

    2014-01-01

    The corrosion and wear behaviour of Al–Mg–Si alloy matrix hybrid composites developed with the use of rice husk ash (RHA) and silicon carbide (SiC) particulates as reinforcements were investigated. RHA and SiC mixed in weight ratios 0:1, 1:3, 1:1, 3:1, and 1:0 were utilized to prepare 5, 7.5 and 10 wt% of the reinforcing phase with Al Mg Si alloy as matrix using double stir casting process. Open circuit corrosion potential (OCP) and potentiodynamic polarization measurements were used to study...

  13. The Dependance of Damage Accumulation in Carbon Fibre Reinforced Epoxy Composites on Matrix Properties.

    Science.gov (United States)

    1985-12-01

    Diguuibutiofl Unlimited 0- Contract U.S. AIR FORCE/ARMINES- Centre des Matdriaux No A.F.O.S.R. 84-0397 - Final Report December 1985 THE DEPENDANCE OF DAMAGE...61102F 2301 D1 185 11 TITLE (include Security Classification) THE DEPENDANCE OF DAMAGE ACCUMULATION IN CARBON FIBRE REINFORCED EPOXY COMPOSITES ON...ATN OF: LTS/Autovon 235-4299 26 March 1986 SUBJECT: EOARD-TR-86-04, Final Scientific Report, "The Dependance of Damage Accumu- lation in Carbon Fibre

  14. EFFECT OF AGING ON MECHANICAL AND WEAR PROPERTIES OF BERYL PARTICULATE REINFORCED METAL MATRIX COMPOSITES

    Directory of Open Access Journals (Sweden)

    H. N. REDDAPPA

    2014-08-01

    Full Text Available This paper describes the study of effect of aging on mechanical and wear properties of ‘hot rolled’ Al6061-10% wt. of beryl particulate reinforced composites produced by stir casting have been examined. The result shows that hardness and tensile strength of ‘90% hot rolled and aged’ composites were increased by 10.28% and 3.78% as compared to ‘hot rolled’ composites respectively. The ‘hot rolled and aged’ composite shows significant decrease in specific wear rate when compared to that of ‘hot rolled’ composites.

  15. Standard Guide for Identification of Fiber-Reinforced Polymer-Matrix Composite Materials in Databases

    CERN Document Server

    American Society for Testing and Materials. Philadelphia

    2000-01-01

    1.1 This guide establishes essential and desirable data elements for fiber-reinforced composite materials for two purposes: to establish the material identification component of data-reporting requirements for test reporting and to provide information for the design of material property databases. 1.1.1 This guide is the first part of a two-part modular approach. The first part serves to identify the material and the second part serves to describe testing procedures and variables and to record results. 1.1.2 For mechanical testing, the related document is Guide E 1434. The interaction of this guide with Guide E 1434 is emphasized by the common numbering of data elements. Data Elements A1 through G13 are included in this guide, and numbering of data elements in Guide E 1434 begins with H1 for the next data element block. This guide is most commonly used in combination with a guide for reporting the test procedures and results such as Guide E 1434. 1.2 These guidelines are specific to fiber-reinforced polyme...

  16. Microstructure and property of sub-micro WC-10%Co particulate reinforced Cu matrix composites prepared by selective laser sintering

    Institute of Scientific and Technical Information of China (English)

    GU Dong-dong; SHEN Yi-fu; DAI Peng; YANG Ming-chuan

    2006-01-01

    The WC-10%Co particulate reinforced Cu matrix composite material with a WC-Co:Cu mass ratio of 20:80 was successfully fabricated by selective laser sintering(SLS) process. The following optimal processing parameters were used: laser power of 700 W, scan speed of 0.06 m/s, scan line spacing of 0.15 mm, and powder layer thickness of 0.3 mm. The microstructure,composition, and phase of the laser processed material were investigated by scanning electron microscopy(SEM), X-ray diffraction(XRD), and energy dispersive X-ray(EDX) spectroscopy. The results show that the bonding mechanism of this process is liquid phase sintering. The Cu and Co act as the binder phase, while the WC acts as the reinforcing phase. The non-equilibrium effects induced by laser melting, such as high degrees of undercooling and high solidification rate, result in the formation of a metastable phase CoC0.25. The WC reinforcing particulates typically have three kinds of morphology. They are agglomerated and undissolved, incompletely separated and partially dissolved, separated and dissolved, which indicates that particle rearrangement acts as the dominant sintering mechanism for the larger WC, while dissolution-precipitation prevails for the smaller WC particles.Microhardness tester was used to determine the Vickers hardness across the cross-section of the laser sintered sample, with the average value being HV0.1268.5. However, the hardness varied considerably, which might be attributed to the WC segregation and the high solidification rate experienced by the molten pool.

  17. Contributions in the Preparation and Processing of Composite Material Type Silumin 3 - Reinforced Matrix with S235JR Steel Mesh

    Directory of Open Access Journals (Sweden)

    Remus Belu-Nica

    2015-07-01

    Full Text Available In the paper are presented concrete data on developing technological batches of metal composite material (MCM type Silumin 3-reinforced matrix with steel mesh S235JR, with the indicating of the parameter and of the distinct stages of work. The samples from prepared batches were cut along and across by water jet abrasive process and were subjected to a destructive testing program and microstructural examination, obtaining results in concordance with the desired quality. The abrasive material used for cut was GMA granite with the average mesh of 80, the particle size ranging between 150-300 µm, density 2300 kg/m3 and melting point 1240°C.

  18. Investigations into Deformation Characteristics during Open-Die Forging of SiCp Reinforced Aluminium Metal Matrix Composites

    Directory of Open Access Journals (Sweden)

    Deep Verma

    2013-01-01

    Full Text Available The deformation characteristics during open-die forging of silicon carbide particulate reinforced aluminium metal matrix composites (SiCp AMC at cold conditions are investigated. The material was fabricated by liquid stir casting method in which preheated SiC particles were mixed with molten LM6 aluminium casting alloy and casted in the silicon mould. Finally, preforms obtained were machined in required dimensions. Two separate cases of deformation, that is, open-die forging of solid disc and solid rectangular preforms, were considered. Both upper bound theoretical analysis and experimental investigations were performed followed by finite element simulation using DEFORM, considering composite interfacial friction law, barreling of preform vertical sides, and inertia effects, that is, effect of die velocity on various deformation characteristics like effective stress, strain, strain rate, forging load, energy dissipations, and height reduction. Results have been presented graphically and critically investigated to evaluate the concurrence among theoretical, experimental, and finite element based computational findings.

  19. Assessment Stability and Informative of Diagnostic Matrix in Analysis States of Reinforced Concrete Slab

    Directory of Open Access Journals (Sweden)

    Sokolov Vladimir

    2016-01-01

    Full Text Available In this article was examined the issues of sustainability and informative of diagnostic matrix, which are used when it is necessary to determinate the technical condition of constructions. Determination based on the mathematical instrument of technical diagnostics. One of the most widespread methods of technical diagnostics – a statistical method of Bayes is used.

  20. EVALUATION & COMPARISION OF MECHANICAL PROPERTIES OF ALUMINIUM ALLOY 5052 REINFORCED WITH SILICONCARBIDE, GRAPHITE AND FLY ASH HYBRID METAL MATRIX COMPOSITES

    Directory of Open Access Journals (Sweden)

    ANKUSH SACHDEVA

    2013-10-01

    Full Text Available The engineering fraternity has always been looking forward to develop an outstanding and wonder-materials which would fit the ever-changing demands of the world. In order to fullfill the demands various newdiscoveries have been made by scientists, engineers and resrearchers. In todays competitive world many, materials have been tried for various unexplored conditions , but the never ending demand of the world encourages the researchers to develop the new material. Now the researchers are preparing the material by the combination of different materials called hybrid composite material.. Metal Matrix Composites (MMCs have emerged as a class of materials suitable for structural, aerospace, automotive, electronic, thermal and wearapplications owing to their advantages over the conventional materials. The present study was taken up to explore the possibility of using different reinforcements (silicon carbide, fly ash and graphite to enhance the properties of aluminium alloy (Al5052 composites. Different samples were prepared from the aluminium withvarying reinforcement composition. The mechanical properties studied after the experiment were strength, hardness and elongation.Further, these composites were characterized with the help of, mechanical testing and scanning electron microscopy.

  1. Relationship Between Hysteresis Dissipated Energy and Temperature Rising in Fiber-Reinforced Ceramic-Matrix Composites Under Cyclic Loading

    Science.gov (United States)

    Longbiao, Li

    2016-06-01

    In this paper, the relationship between hysteresis dissipated energy and temperature rising of the external surface in fiber-reinforced ceramic-matrix composites (CMCs) during the application of cyclic loading has been analyzed. The temperature rise, which is caused by frictional slip of fibers within the composite, is related to the hysteresis dissipated energy. Based on the fatigue hysteresis theories considering fibers failure, the hysteresis dissipated energy and a hysteresis dissipated energy-based damage parameter changing with the increase of cycle number have been investigated. The relationship between the hysteresis dissipated energy, a hysteresis dissipated energy-based damage parameter and a temperature rise-based damage parameter have been established. The experimental temperature rise-based damage parameter of unidirectional, cross-ply and 2D woven CMCs corresponding to different fatigue peak stresses and cycle numbers have been predicted. It was found that the temperature rise-based parameter can be used to monitor the fatigue damage evolution and predict the fatigue life of fiber-reinforced CMCs.

  2. Tribological Behavior of TiAl Metal Matrix Composite Brake Disk with TiC Reinforcement Under Dry Sliding Conditions

    Science.gov (United States)

    Liaquat, Hassan; Shi, Xiaoliang; Yang, Kang; Huang, Yuchun; Liu, Xiyao; Wang, Zhihai

    2017-07-01

    In this investigation, the effect of TiC particulate reinforcement and sintering parameters on tribological behavior of TiAl metal matrix composite (TMMC) has been studied and compared with commercially conventional gray cast iron to evaluate the use of TMMC as brake disk material in an automobile. Three sample disks of TMMC containing TiC particulate reinforcement (D1-5 wt.%, D2 and D3-10 wt.%) were produced by the spark plasma sintering process. D3 compared with D2 was sintered at a higher temperature to evaluate the effect of SPS parameters on the wear characteristics of TMMC. All experiments were performed on pin-on-disk tribotester under a dry sliding condition with different loads (10-11.5 N) and sliding velocities (0.2-0.9 m/s). It is found that higher content of TiC increased TMMC hardness and density. XRD technique has been used to analyze the phase composition. Owing to the high sintering temperature, α-2 Ti3Al phase was formed which further enhanced the matrix anti-wear capability. Scanning electron microscope (SEM) was used to capture the wear track and observe wear mechanism. Energy-dispersive spectroscopy (EDS) has been used to analyze the tribofilm and wear debris. The results showed that the tribofilm for TMMC was mainly composed of metal oxides. Oxidation of Al and Ti due to frictional heat provides wear-resistant protective layer. Under almost all sliding conditions, TMMC, especially disk D3, exhibited minimum wear rate and stable friction coefficient, whereas gray cast iron exhibited lower and unstable friction coefficient as well as higher wear rate. TMMC has shown superior tribological characteristics over gray cast iron in terms of low wear rate along with stable and adequate friction coefficient which is necessary for braking operation and life of brake disk. However, further investigation on full-scale automobile conditions is needed for its practical application.

  3. Creep behaviour of a casting titanium carbide reinforced AlSi12CuNiMg piston alloy at elevated temperatures; Hochtemperaturkriechverhalten der schmelzmetallurgisch hergestellten dispersionsverstaerkten Kolbenlegierung AlSi12CuNiMg

    Energy Technology Data Exchange (ETDEWEB)

    Michel, S.; Scholz, A. [Zentrum fuer Konstruktionswerkstoffe, TU Darmstadt (Germany); Tonn, B. [Institut fuer Metallurgie, TU Clausthal (Germany); Zak, H.

    2012-03-15

    This paper deals with the creep behaviour of the titanium carbide reinforced AlSi12CuNiMg piston alloy at 350 C and its comparison to the conventional AlSi12Cu4Ni2MgTiZr piston alloy. With only 0,02 vol-% TiC reinforcement the creep strength and creep rupture strength of the AlSi12CuNiMg piston alloy are significantly improved and reach the level of the expensive AlSi12Cu4Ni2MgTiZr alloy. (Copyright copyright 2012 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim)

  4. Corrosion behaviour of TiB2 reinforced aluminium based in situ metal matrix composites

    Directory of Open Access Journals (Sweden)

    G.S. Pradeep Kumar

    2016-09-01

    Full Text Available This paper focuses on corrosion characteristics of cast and forged aluminium 6061 based composites reinforced with TiB2 particles. Composites were synthesised by in situ technique using potassium hexafluorotitanate salt (K2TiF6 and potassium tetrafluroborate (KBF4 halide salts by stir casting route at a temperature of 850 °C. Cast aluminium alloy and its in situ composites were subjected to open die drop forging at a temperature of 500 °C. Both cast and forged alloy 6061 and in situ composites were then subjected to microstructure studies, salt spray test. Salt spray test was conducted as per ASTM B117 standard test procedure using 5% sodium chloride test solution. Result reveals that, forged alloy and its in situ composites exhibited improved corrosion resistance compared to cast ones.

  5. Acoustic emission characterization of fracture toughness for fiber reinforced ceramic matrix composites

    Energy Technology Data Exchange (ETDEWEB)

    Mei, Hui, E-mail: phdhuimei@yahoo.com [Science and Technology on Thermostructure Composite Materials Laboratory, Northwestern Polytechnical University, Xi' an Shaanxi 710072 (China); Sun, Yuyao; Zhang, Lidong; Wang, Hongqin; Cheng, Laifei [Science and Technology on Thermostructure Composite Materials Laboratory, Northwestern Polytechnical University, Xi' an Shaanxi 710072 (China)

    2013-01-10

    The fracture toughness of a carbon fiber reinforced silicon carbide composite was investigated relating to classical critical stress intensity factor K{sub IC}, work of fracture, and acoustic emission energy. The K{sub IC} was obtained by the single edge notch beam method and the work of fracture was calculated using the featured area under the load-displacement curves. The K{sub IC}, work of fracture, and acoustic emission energy were compared for the composites before and after heat treatment and then analyzed associated with toughening microstructures of fiber pullout. It indicates that the work of fracture and acoustic emission energy can be more suitable to reflect the toughness rather than the traditional K{sub IC}, which has certain limitation for the fracture toughness characterization of the crack tolerant fiber ceramic composites.

  6. Numerical simulations of interfacial debonding in ductile-phase reinforced intermetallic matrix composites

    Energy Technology Data Exchange (ETDEWEB)

    Henshall, G.A.; Zywicz, E.; Strum, M.J.

    1993-08-10

    The fracture toughness of brittle intermetallic compounds can be improved by ductile-phase reinforcements. Effectiveness of the ductile phase in bridging cracks, and therefore increasing, the composite toughness, is known qualitatively to depend upon the extent of debonding, between the two phases. Numerical crack-growth simulations are used here to provide semi-quantitative predictions of the influence of interfacial debonding on the macroscopic stress-displacement behavior and, hence, the fracture toughness of an idealized Pb/glass composite. The interfacial toughness required to cause debonding, characterized by a constant critical energy release rate, is varied parametrically. As expected, higher interfacial toughness results in less interphase debonding, higher composite strength, and greater ductile-phase constraint. Consequently, the increase in ductile-phase triaxiality can potentially accelerate internal void formation and growth or facilitate cleavage fracture, either of which would likely decrease the toughness of the composite.

  7. Wear Resistance of Aluminum Matrix Composites Reinforced with Al2O3 Particles After Multiple Remelting

    Science.gov (United States)

    Klasik, Adam; Pietrzak, Krystyna; Makowska, Katarzyna; Sobczak, Jerzy; Rudnik, Dariusz; Wojciechowski, Andrzej

    2016-08-01

    Based on previous results, the commercial composites of A359 (AlSi9Mg) alloy reinforced with 22 vol.% Al2O3 particles were submitted to multiple remelting by means of gravity casting and squeeze-casting procedures. The studies were focused on tribological tests, x-ray phase analyses, and microstructural examinations. More promising results were obtained for squeeze-casting method mainly because of the reduction of the negative microstructural effects such as shrinkage porosity or other microstructural defects and discontinuities. The results showed that direct remelting may be treated as economically well-founded and alternative way compared to other recycling processes. It was underlined that the multiple remelting method must be analyzed for any material separately.

  8. Effect of heat treatment on microstructure and interface of SiC particle reinforced 2124 Al matrix composite

    Energy Technology Data Exchange (ETDEWEB)

    Mandal, Durbadal, E-mail: durbadal73@yahoo.co.in [MEF Division, CSIR-National Metallurgical Laboratory, Jamshedpur 831007 (India); Viswanathan, Srinath [Dept of Metallurgical and Materials Engineering, University of Alabama, Tuscaloosa, AL (United States)

    2013-11-15

    The microstructure and interface between metal matrix and ceramic reinforcement of a composite play an important role in improving its properties. In the present investigation, the interface and intermetallic compound present in the samples were characterized to understand structural stability at an elevated temperature. Aluminum based 2124 alloy with 10 wt.% silicon carbide (SiC) particle reinforced composite was prepared through vortex method and the solid ingot was deformed by hot rolling for better particle distribution. Heat treatment of the composite was carried out at 575 °C with varying holding time from 1 to 48 h followed by water quenching. In this study, the microstructure and interface of the SiC particle reinforced Al based composites have been studied using optical microscopy, scanning electron microscopy (SEM) coupled with energy dispersive X-ray spectroscopy (EDS), electron probe micro-analyzer (EPMA) associated with wavelength dispersive spectroscopy (WDS) and transmission electron microscopy (TEM) to identify the precipitate and intermetallic phases that are formed during heat treatment. The SiC particles are uniformly distributed in the aluminum matrix. The microstructure analyses of Al–SiC composite after heat treatment reveal that a wide range of dispersed phases are formed at grain boundary and surrounding the SiC particles. The energy dispersive X-ray spectroscopy and wavelength dispersive spectroscopy analyses confirm that finely dispersed phases are CuAl{sub 2} and CuMgAl{sub 2} intermetallic and large spherical phases are Fe{sub 2}SiAl{sub 8} or Al{sub 15}(Fe,Mn){sub 3}Si. It is also observed that a continuous layer enriched with Cu and Mg of thickness 50–80 nm is formed at the interface in between Al and SiC particles. EDS analysis also confirms that Cu and Mg are segregated at the interface of the composite while no carbide is identified at the interface. - Highlights: • The composite was successfully heat treated at 575°C for 1

  9. Plasma Transferred ARC (PTA Hardfacing of Recycled Hardmetal Reinforced Nickel-matrix Surface Composites

    Directory of Open Access Journals (Sweden)

    Arkadi ZIKIN

    2012-03-01

    Full Text Available The aim of this work was to apply coarse recycled hardmetal particles in combination with Ni-based matrix to produce wear resistant metal matrix composite (MMC thick coatings using plasma transferred arc hardfacing (PTA technology. Assignment of hardmetal waste as initial material can significantly decrease the production costs and improve the mechanical properties of coatings and, consequently, increase their wear resistance. The microstructure of MMC fabricated from a recycled powder was examined by optical and SEM/EDS microscopes, whereas quantitative analyses were performed by image analysis method. Micro-mechanical properties, including hardness and elastic modulus of features, were measured by nanoindentation. Furthermore, behaviour of materials subjected to abrasive and impact conditions was studied. Results show the recycled powder provides hardfacings of high quality which can be successfully used in the fabrication of wear resistant MMC coatings by PTA-technology.DOI: http://dx.doi.org/10.5755/j01.ms.18.1.1334

  10. Fatigue Life and Microstructure after Multiple Remelting of A359 Matrix Composites Reinforced with SiC Particles

    Directory of Open Access Journals (Sweden)

    Klasik A.

    2016-12-01

    Full Text Available The article presents the results of fatigue life tests and microstructure examinations of A359 alloy matrix composites (F3S.10S and F3S.30S containing 10 and 30wt% of SiC particles, subjected to multiple remelting by conventional gravity casting. Mechanical characteristics were determined in a modified low cycle fatigue (MLCF test, enabling rapid estimation of fatigue life and other mechanical parameters in practice of any material. Qualitative and quantitative metallographic examinations were also carried out. The quantitative evaluation of microstructure was performed by computer image analysis. A set of geometrical parameters of the reinforcing particles, pores and eutectic precipitates present in the metal matrix was determined. The relationships between the mechanical parameters, structural characteristics and the number of remelting operations were presented. It was found that up to the fourth remelting, the mechanical characteristics, including fatigue life, are slightly deteriorated but decrease gradually in the subsequent operations of remelting. The observed effect is mainly due to the shrinkage porosity occurring as a result of gravity casting. To eliminate this defect, the use of squeeze casting process was recommended. It has also been shown that multiple remelting can be an easy and economically well-founded alternative to other more expensive recycling methods.

  11. Crystallization behaviors of carbon fiber reinforced BN-Si{sub 3}N{sub 4} matrix composite

    Energy Technology Data Exchange (ETDEWEB)

    Li, Bin; Zhang, Chang-Rui; Wang, Si-Qing; Cao, Feng [State Key Laboratory of Advanced Ceramic Fibers and Composites, College of Aerospace and Materials Engineering, National University of Defense Technology, Changsha 410073 (China)

    2007-07-15

    The crystallization behaviors of a new carbon fiber reinforced composite with a hybrid matrix comprising BN and Si{sub 3}N{sub 4} prepared by precursor infiltration and pyrolysis were investigated by Fourier transform infrared spectroscopy, X-ray diffraction and scanning electron microscopy. The results show that the as-received composite is almost amorphous, and its main composition is BN and Si{sub 3}N{sub 4}. When heat treated at 1600 C, the composite is crystallized and shows a much better crystal form. When heat treated at 2100 C, Si{sub 3}N{sub 4} in the matrix is decomposed, and BN exhibits a relatively complete crystallization. The existence of B{sub 4}C and SiC is detected, which indicates the interfacial chemical reactions between nitride matrices and carbon fibers. The surface morphology of carbon fibers in the composite changed significantly when heated from 1600 to 2100 C, which also proved the occurrence of interfacial chemical reactions. (copyright 2007 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim) (orig.)

  12. Novel iron metal matrix composite reinforced by quartz sand for the effective dechlorination of aqueous 2-chlorophenol.

    Science.gov (United States)

    Zhang, Yunfei; Yang, Bo; Han, Yanni; Jiang, Chaojin; Wu, Deli; Fan, Jinhong; Ma, Luming

    2016-03-01

    In this work, we tested a novel iron metal matrix composite (MMC) synthesized by mechanically introducing quartz sand (SiO2) into an iron matrix (denoted as SiO2-Fe MMC). The pseudo-first-order reaction rate constant of the SiO2-Fe MMC (initial pH 5.0) for 20 mg/L of 2-chlorophenol (2-CP) was 0.051 × 10(-3) L/m(2)/min, which was even higher than that of some reported Pd/Fe bimetals. This extraordinary high activity was promoted by the quick iron dissolution rate, which was caused by the formation of Fe-C internal electrolysis from carbonization of process control agent (PCA) and the active reinforcement/metal interfaces during the milling process. In addition, pH has slight effect on the dechlorination rate. The SiO2-Fe MMC retained relatively stable activity, still achieving 71% removal efficiency for 2-CP after six consecutive cycles. The decrease in dechlorination efficiency can be attributed to the rapid consumption of Fe(0). A dechlorination mechanism using the SiO2-Fe MMC was proposed by a direct electron transfer from Fe(0) to 2-CP at the quartz sand/iron interface.

  13. An Experimental Study Of Aluminum Alloy Matrix Composite Reinforced SiC Made By Hot Pressing Method

    Directory of Open Access Journals (Sweden)

    Suśniak M.

    2015-06-01

    Full Text Available The present work investigates the possibility of using powder metallurgy processing for producing a metal matrix composite. Materials were prepared from AlSi5Cu2 chips with reinforcement of 10, 15, 20 wt. % silicon carbide. Aluminum alloy chips were milled with SiC powder in a high-energy ball mill by 40 hours. Mechanical alloying process lead to obtain an uniform distribution of hard SiC particles in the metallic matrix and refine the grain size. The consolidation of composite powders was performed by vacuum hot pressing at 450°C, under pressure of 600 MPa by 10 min. The results shows that the addition of SiC particles has a substantial influence on the microstructure and mechanical properties of composite powder as well as consolidated material. Hot pressing is an effective consolidation method which leads to obtain dense AlSi5Cu2/SiC composite with homogeneous structure and advanced mechanical properties.

  14. A titanium surface with nano-ordered spikes and pores enhances human dermal fibroblastic extracellular matrix production and integration of collagen fibers.

    Science.gov (United States)

    Yamada, Masahiro; Kato, Eiji; Yamamoto, Akiko; Sakurai, Kaoru

    2016-02-02

    The acquisition of substantial dermal sealing determines the prognosis of percutaneous titanium-based medical devices or prostheses. A nano-topographic titanium surface with ordered nano-spikes and pores has been shown to induce periodontal-like connective tissue attachment and activate gingival fibroblastic functions. This in vitro study aimed to determine whether an alkali-heat (AH) treatment-created nano-topographic titanium surface could enhance human dermal fibroblastic functions and binding strength to the deposited collagen on the titanium surface. The surface topographies of commercially pure titanium machined discs exposed to two different AH treatments were evaluated. Human dermal fibroblastic cultures grown on the discs were evaluated in terms of cellular morphology, proliferation, extracellular matrix (ECM) and proinflammatory cytokine synthesis, and physicochemical binding strength of surface-deposited collagen. An isotropically-patterned, shaggy nano-topography with a sponge-like inner network and numerous well-organized, anisotropically-patterned fine nano-spikes and pores were observed on each nano-topographic surface type via scanning electron microscopy. In contrast to the typical spindle-shaped cells on the machined surfaces, the isotropically- and anisotropically-patterned nano-topographic titanium surfaces had small circular/angular cells containing contractile ring-like structures and elongated, multi-shaped cells with a developed cytoskeletal network and multiple filopodia and lamellipodia, respectively. These nano-topographic surfaces enhanced dermal-related ECM synthesis at both the protein and gene levels, without proinflammatory cytokine synthesis or reduced proliferative activity. Deposited collagen fibers were included in these surfaces and sufficiently bound to the nano-topographies to resist the physical, enzymatic and chemical detachment treatments, in contrast to machined surfaces. Well-organized, isotropically

  15. Reinforcement of the bulk crowns excavator technology by dispersion hardening of titanium carbide to increase wear resistance

    Science.gov (United States)

    Chumanov, I.; Anikeev, A.; Chumanov, V.

    2017-02-01

    Dispersed particles embedded in the metal, improve the mechanical properties, particularly wear resistance. Introduction of the metal particles in a controlled and their distribution is difficult because of the density difference and the metal particles introduced. This article provides a method for the introduction of particles in the volume of metal, it contains a proposed strengthening technique described experiment course. During the experiment, the volume-reinforced castings from wear-resistant steel, the results of studies of the microstructure by optical and scanning electron microscopy, and mechanical tests of prototypes have been obtained.

  16. Microstructure and Mechanical Behaviour of Stir-Cast Al-Mg-Sl Alloy Matrix Hybrid Composite Reinforced with Corn Cob Ash and Silicon Carbide

    Directory of Open Access Journals (Sweden)

    Oluwagbenga Babajide Fatile

    2014-10-01

    Full Text Available In this present study, the microstructural and mechanical behaviour of Al-Mg-Si alloy matrix composites reinforced with silicon carbide (SiC and Corn cob ash (An agro‑waste was investigated. This research work was aimed at assessing the suitability of developing low cost- high performance Al-Mg-Si hybrid composite. Silicon carbide (SiC particulates added with 0,1,2,3 and 4 wt% Corn cob ash (CCA were utilized to prepare 10 wt% of the reinforcing phase with Al-Mg-Si alloy as matrix using two-step stir casting method. Microstructural characterization, density measurement, estimated percent porosity, tensile testing, and micro‑hardness measurement were used to characterize the composites produced. From the results obtained, CCA has great potential to serve as a complementing reinforcement for the development of low cost‑high performance aluminum hybrid composites.

  17. Sisal fibre pull-out behaviour as a guide to matrix selection for the production of sisal fibre reinforced cement matrix composites

    CSIR Research Space (South Africa)

    Mapiravana, Joe

    2011-12-01

    Full Text Available Natural fibre reinforced cement composites are promising potential materials for use in panelised construction. The structural properties of these composite materials are yet to be fully understood. As the role of the natural fibre is to reinforce...

  18. Fiber reinforced concrete: Characterization of flexural toughness and some studies on fiber-matrix bond-slip interaction

    Science.gov (United States)

    Dubey, Ashish

    One major problem associated with the testing of fiber reinforced concrete specimens under flexural loading is that the measured post-cracking response is severely affected by the stiffness of the testing machine. As a consequence, misleading results are obtained when such a flexural response is used for the characterization of composite toughness. An assessment of a new toughness characterization technique termed the Residual Strength Test Method (RSTM) has been made. In this technique, a stable narrow crack is first created in the specimen by applying a flexural load in parallel with a steel plate under controlled conditions. The plate is then removed, and the specimen is tested in a routine manner in flexure to obtain the post-crack load versus displacement response. Flexural response for a variety of fiber reinforced cementitious composites obtained using the Residual Strength Test Method has been found to correlate very well with those obtained with relatively stiffer test configurations such as closed-loop test machines. The Residual Strength Test Method is found to be effective in differentiating between different fiber types, fiber lengths, fiber configurations, fiber volume fractions, fiber geometries and fiber moduli. In particular, the technique has been found to be extremely useful for testing cement-based composites containing fibers at very low dosages (shear lag theory is introduced to study the problem of fiber pullout in fiber reinforced composites. The proposed model eliminates limitations of many earlier models and captures essential features of pullout process, including progressive interfacial debonding, Poisson's effect, and variation in interfacial properties during the fiber pullout process. Interfacial debonding is modeled using an interfacial shear strength criterion. Influence of normal contact stress at the fiber-matrix interface is considered using shrink-fit theory, and the interfacial frictional shear stress over the debonded

  19. Laser treatment of carbon fibre reinforced thermoplastic matrix for adhesive bonding

    Science.gov (United States)

    Genna, S.; Leone, C.; Ucciardello, N.; Giuliani, M.

    2016-05-01

    In the present study, laser surface treatment of CFRP made of PPS thermoplastic matrix by means of a 30 W Q-Switched Yb:YAG fiber laser, is investigated with the aim to improve adhesive bonding. The process parameters pulse power, scanning speed, hatch distance and scanning strategy, were varied to the aim to study the influence of the process condition on the first top resin layer removal and fibre damage. The operating window was experimentally determined. The effectiveness of laser treatment was verified by single lap shear test.

  20. Bibliography on Ceramic Matrix Composites and Reinforcing Whiskers, Platelets, and Fibers, 1970-1990

    Science.gov (United States)

    1993-08-01

    Saburo Shigaki, Yoshiki Rao, A. Srinivasa Cannon, W Roger Hirata, Yoshihiro Yoshimua, Masahiro Ceram. Int. Somiya, Shigeyuki 15 (3), 179-88, 1989...P. Chartier , T. Mullites and Mullite-Zirconia Composites Giry, J. P. Kubota, Y. Takagi, H. Mullite and Mullite Matrix Composites Government Industrial...Yong, J. A. 74 (1), 187-93, Jan 1991 Rawlings, R. D. Rogers , P. S. (AD D250 366) Mater. Sci. Technol. 7, 155-7, Feb 1991 7.1.0.48 (AD D250 906

  1. Separation of the Martensite in TiNi Fiber Reinforced Aluminum Matrix Composite

    Institute of Scientific and Technical Information of China (English)

    Yanjun ZHENG; Lishan CUI; Yan LI; Dazhi YANG

    2004-01-01

    The reverse martensitic transformation of TiNi shape memory alloy fibers embedded in a pure aluminum matrix was studied in this paper. Results showed that the phase composition of the TiNi alloy fibers prior to prestraining at the room temperature had a significant influence on the differential scanning calorimetry (DSC) results of the composites. By a comparison to the high temperature X-ray diffraction (XRD) results, it was confirmed that the martensite was divided into two groups: the selfaccommodating martensite (SAM) and the preferentially oriented martensite (POM). The evolving process of the separation of martensite was discussed.

  2. Martensitic Transformation of TiNi Shape Memory Alloy Fiber Reinforced Ni Matrix Composites

    Institute of Scientific and Technical Information of China (English)

    Lishan CUI; Yan LI; Yan jun ZHENG; Huibin XU

    2003-01-01

    In this paper, a TiNi shape memory alloy fiber Ni matrix composite was fabricated by an electroplating method using TiNialloy as the cathode and Ni as the anode. The constrained martensitic transformation behaviors of the TiNi alloy were studiedby differential scanning calorimeter (DSC), and the results showed that two endothermic peaks appear on the DSC heatingcurves and the reverse transformation temperatures increase with increasing prestrain levels. Moreover, comparing to the freetransformation, the temperature window of the constrained reverse transformation is widely expanded due to the influence ofrecovery stress.

  3. Studies of Matrix/Fiber Reinforced Composite Materials for the High Speed Research (HSR) Program

    Science.gov (United States)

    Orwoll, Robert A.

    1998-01-01

    The research on the curing mechanism of the phenylethynyl terminated imide matrix resins was the primary focus of this research. The ability to process high performance polymers into useful adhesives and high quality composites has been significantly advanced by synthetic techniques in which oligomers terminated with reactive groups cure or crosslink at elevated temperature after the article has been fabricated. The research used a variety of analytical techniques. Many stable products were isolated, and attempts at identification were made. This research was intended to provide fundamental insight into the molecular structure of these new engineering materials.

  4. Evaluation of two matrix materials intended for fiber-reinforced polymers.

    Science.gov (United States)

    Segerström, Susanna; Meriç, Gökçe; Knarvang, Torbjørn; Ruyter, I Eystein

    2005-10-01

    Two matrix resins for fiber composites that remain in a fluid state during storage and handling before polymerization were evaluated. The resin mixtures, based on methyl methacrylate (MMA), were produced with two different cross-linking agent systems: 1,4-butanediol dimethacrylate and ethylene glycol dimethacrylate or diethylene glycol dimethacrylate. Water sorption, water solubility, water uptake and residual MMA monomer were determined. Thermomechanical analysis was used to determine linear dimensional changes as a function of temperature. Flexural strength and modulus as well as fracture work and the maximum stress intensity factor were determined. The results revealed similar values for both matrix polymers regarding water sorption, water solubility, water uptake, residual MMA monomer (0.5 wt% (+/- 0.03)) and coefficient of linear thermal expansion. Flexural strength for polymer B was 68.7 MPa (+/- 9.8) compared to 56.0 MPa (+/- 13.3) for polymer A when tested dry and 64 MPa (+/- 6.1) compared to (54 MPa (+/- 3.3) when water-saturated. Fracture toughness tests showed higher maximum stress intensity factor values for polymer B (0.75 +/- 0.17) MPa x m1/2 than for polymer A (0.55 +/- 0.12) MPa x m1/2. The resin binders showed an appropriate consistency while remaining in a fluid state during storage and manipulation.

  5. Corrosion and wear behaviour of Al–Mg–Si alloy matrix hybrid composites reinforced with rice husk ash and silicon carbide

    Directory of Open Access Journals (Sweden)

    Kenneth Kanayo Alaneme

    2014-01-01

    Full Text Available The corrosion and wear behaviour of Al–Mg–Si alloy matrix hybrid composites developed with the use of rice husk ash (RHA and silicon carbide (SiC particulates as reinforcements were investigated. RHA and SiC mixed in weight ratios 0:1, 1:3, 1:1, 3:1, and 1:0 were utilized to prepare 5, 7.5 and 10 wt% of the reinforcing phase with Al Mg Si alloy as matrix using double stir casting process. Open circuit corrosion potential (OCP and potentiodynamic polarization measurements were used to study the corrosion behaviour while coefficient of friction was used to assess the wear behaviour of the composites. The corrosion and wear mechanisms were established with the aid of scanning electron microscopy. The results show that the effect of RHA/SiC weight ratio on the corrosion behaviour of the composites in 3.5% NaCl solution was not consistent for the different weight percent of reinforcement (5, 7.5, and 10 wt% used in developing the Al–Mg–Si based composites. It was evident that for most cases the use of hybrid reinforcement of RHA and SiC resulted in improved corrosion resistance of the composites in 3.5% NaCl solution. Preferential dissolution of the more anodic Al–Mg–Si alloy matrix around the Al–Mg–Si matrix/RHA/SiC particle interfaces was identified as the primary corrosion mechanism. The coefficient of friction and consequently the wear resistance of the hybrid composites were comparable to that of the Al–Mg–Si alloy matrix reinforced with only SiC.

  6. The interface in tungsten fiber reinforced niobium metal-matrix composites. Final Report Ph.D. Thesis - Case Western Reserve Univ., Cleveland, OH

    Science.gov (United States)

    Grobstein, Toni L.

    1989-01-01

    The creep resistance of tungsten fiber reinforced niobium metal-matrix composites was evaluated. The interface region between the fiber and matrix was characterized by microhardness and electron probe microanalysis measurements which indicated that its properties were between those of fiber and matrix. However, the measured properties of the composite exceeded those calculated by the rule of mixtures even when the interface zone was assumed to retain all the strength of the fiber. The composite structure appeared to enhance the strengths of both the fibers and the matrix above what they exhibited in stand-alone tests. The effect of fiber orientation and matrix alloy composition on the fiber/matrix interface were also evaluated. Small alloying additions of zirconium and tungsten to the niobium matrix affected the creep resistance of the composites only slightly. A decrease in the creep resistance of the composite with increasing zirconium content in the matrix was ascribed to an increase in the diffusion rate of the fiber/matrix interdiffusion reaction, and a slight increase in the creep resistance of the composite was observed with an addition of 9 w percent tungsten to the matrix. In addition, Kirkendall void formation was observed at the fiber/matrix interface; the void distribution differed depending on the fiber orientation relative to the stress axis.

  7. Three-Dimensional Nanoporous Cellulose Gels as a Flexible Reinforcement Matrix for Polymer Nanocomposites.

    Science.gov (United States)

    Shi, Zhuqun; Huang, Junchao; Liu, Chuanjun; Ding, Beibei; Kuga, Shigenori; Cai, Jie; Zhang, Lina

    2015-10-21

    With the world's focus on utilization of sustainable natural resources, the conversion of wood and plant fibers into cellulose nanowhiskers/nanofibers is essential for application of cellulose in polymer nanocomposites. Here, we present a novel fabrication method of polymer nanocomposites by in-situ polymerization of monomers in three-dimensionally nanoporous cellulose gels (NCG) prepared from aqueous alkali hydroxide/urea solution. The NCG have interconnected nanofibrillar cellulose network structure, resulting in high mechanical strength and size stability. Polymerization of the monomer gave P(MMA/BMA)/NCG, P(MMA/BA)/NCG nanocomposites with a volume fraction of NCG ranging from 15% to 78%. SEM, TEM, and XRD analyses show that the NCG are finely distributed and preserved well in the nanocomposites after polymerization. DMA analysis demonstrates a significant improvement in tensile storage modulus E' above the glass transition temperature; for instance, at 95 °C, E' is increased by over 4 orders of magnitude from 0.03 MPa of the P(MMA/BMA) up to 350 MPa of nanocomposites containing 15% v/v NCG. This reinforcement effect can be explained by the percolation model. The nanocomposites also show remarkable improvement in solvent resistance (swelling ratio of 1.3-2.2 in chloroform, acetone, and toluene), thermal stability (do not melt or decompose up to 300 °C), and low coefficients of thermal expansion (in-plane CTE of 15 ppm·K(-1)). These nanocomposites will have great promising applications in flexible display, packing, biomedical implants, and many others.

  8. Metal-Matrix Hardmetal/Cermet Reinforced Composite Powders for Thermal Spray

    Directory of Open Access Journals (Sweden)

    Dmitri GOLJANDIN

    2012-03-01

    Full Text Available Recycling of materials is becoming increasingly important as industry response to public demands, that resources must be preserved and environment protected. To produce materials competitive in cost with primary product, secondary producers have to pursue new technologies and other innovations. For these purposes different recycling technologies for composite materials (oxidation, milling, remelting etc are widely used. The current paper studies hardmetal/cermet powders produced by mechanical milling technology. The following composite materials were studied: Cr3C2-Ni cermets and WC-Co hardmetal. Different disintegrator milling systems for production of powders with determined size and shape were used. Chemical composition of produced powders was analysed.  To estimate the properties of recycled hardmetal/cermet powders, sieving analysis, laser granulometry and angularity study were conducted. To describe the angularity of milled powders, spike parameter–quadric fit (SPQ was used and experiments for determination of SPQ sensitivity and precision to characterize particles angularity were performed. Images used for calculating SPQ were taken by SEM processed with Omnimet Image Analyser 22. The graphs of grindability and angularity were composed. Composite powders based on Fe- and Ni-self-fluxing alloys for thermal spray (plasma and HVOF were produced. Technological properties of powders and properties of thermal sprayed coatings from studied powders were investigated. The properties of spray powders reinforced with recycled hardmetal and cermet particles as alternatives for cost-sensitive applications were demonstrated.DOI: http://dx.doi.org/10.5755/j01.ms.18.1.1348

  9. Design feasibility study of a divertor component reinforced with fibrous metal matrix composite laminate

    Energy Technology Data Exchange (ETDEWEB)

    You, J.-H. [Max-Planck-Institut fuer Plasmaphysik, EURATOM Association, Boltzmannstr. 2, D-85748 Garching (Germany)]. E-mail: j.h.you@ipp.mpg.de

    2005-01-01

    Fibrous metal matrix composites possess advanced mechanical properties compared to conventional alloys. It is expected that the application of these composites to a divertor component will enhance the structural reliability. A possible design concept would be a system consisting of tungsten armour, copper composite interlayer and copper heat sink where the composite interlayer is locally inserted into the highly stressed domain near the bond interface. For assessment of the design feasibility of the composite divertor concept, a non-linear multi-scale finite element analysis was performed. To this end, a micro-mechanics algorithm was implemented into a finite element code. A reactor-relevant heat flux load was assumed. Focus was placed on the evolution of stress state, plastic deformation and ductile damage on both macro- and microscopic scales. The structural response of the component and the micro-scale stress evolution of the composite laminate were investigated.

  10. On the Strength of Silicon Carbide Particulate Reinforced Aluminium Alloy Matrix Composites

    Institute of Scientific and Technical Information of China (English)

    Mingjiu ZHAO; Yue LIU; Liqing CHEN; Jing BI

    2004-01-01

    In the present study, the modified continuum model, quench strengthening and dislocation pile-up model was respectively used to estimate the yield strength of SiCp/Al composites. The experimental results showed that the modified shear lag model or quench strengthening model would underestimate the yield strength of SiCp/Al composites. However, the modified Hall-Petch correlation on the basis of the dislocation pile-up model, expressed as σcy = 244 + 371λ-1/2, fitted very well with the experimental data, which indicated that the strength increase of SiCp/Al composites might be due to the direct blocking of dislocation motion by the particulate-matrix interface.Namely, the dislocation pile-up is the most possible strengthening mechanism for SiCp/Al composites.

  11. Fabrication of single crystalline diamond reinforced aluminum matrix composite by powder metallurgy route

    Science.gov (United States)

    Kwon, Hansang; Leparoux, Marc; Heintz, Jean-Marc; Silvain, Jean-François; Kawasaki, Akira

    2011-10-01

    We have successfully fabricated highly densified aluminum (Al)-diamond composite materials by a simple hot press method. The thermal conductivity of the Al-diamond composite materials was measured. These materials had different types, sizes and fractions of diamond. These obtained values were discussed based on theoretically calculated values. The thermal conductivity of the composite materials, measured by Laser-Flash method, was found to have slightly increased compared to that of pure bulk Al. The obtained microstructures of the composite materials showed a lot of cleavage existing in the interface between the Al matrix and the diamond particles, which led to the low increment of the thermal conductivity. Moreover, Al-diamond bulk materials with different sintering temperatures in solid state, liquid phase, and transient region between solid and liquid of Al, have been synthesized.

  12. Friction and wear behavior of TiC particle reinforced ZA43 matrix composites

    Institute of Scientific and Technical Information of China (English)

    谢贤清; 张荻; 刘金水; 吴人洁

    2001-01-01

    TiC/ZA43 composites were fabricated by XDTM and stirring-casting techniques. The tribology properties of the unreinforced ZA43 alloy and the composites were studied by using a block-on-ring apparatus. Experimental results show that the incorporation of TiC particles improves the microstructure of ZA43 matrix alloy. The coefficient of friction μ and the width of worn groove decrease with the increase of TiC volume fraction φ(TiC). The width of worn groove and μ of the composite during wear testing increase with increasing the applied load. Metallographic examinations reveal that unreinforced ZA43 alloy has deep ploughing grooves with obvious adhesion phenomenon, whereas TiC/ZA43 composites have smooth worn surface. Delamination formation is related to the fatigue cracks and the shear cracks on the surface.

  13. Mechanism of laser welding of SiC reinforced LD2 aluminum metal matrix composite

    Institute of Scientific and Technical Information of China (English)

    2001-01-01

    In this paper the mechanism of SiCP/LD2 aluminum matrix composites during laser welding was investigated. The emphasis was laid on the study of the distribution of aluminum carbides in whole welds. The joint can be divided into three regions both in depth and in width. The depth is divided into severe reaction region, partial reaction region, and no reaction region. In these regions, the extent of interfacial reaction varies gradually, the shape of reactants varies from long to fine. In width it can also be divided into severe reaction region, partial reaction region, and initial reaction region from the center of the weld to about the welding junction. In the initial reaction region, nucleation and growth of the reaction products on the surface of SiC particles can be observed by using TEM. The investigation showed that the quantity and size of SiC are relative to the temperature gradient in the molten pool.

  14. Characterisation of Fibre Reinforced Titanium Matrix Composites. (La Caracterisation des Materiaux Composites a Matrice de Titane Renforces par Fibres)

    Science.gov (United States)

    1994-02-01

    egard ces applications sont importantes pour IAGARD, car elles permettent d’augmenter les capacites operationnelles des futurs syst~mes aeriens et, en...talons, sans oublicr qne les valeurs de TA6V identique A celle des Ceuillards externes d’une relatives de a12/01 IN sont les plus importantes . Enfin...Compe’: tesi Septernher I193. 23-2 are unlikely to behave as homogeneous components in service other factors become materials. The combination of elastic

  15. Signs of superconductivity at 110 K on inclusions of TiB sub k boride phases into titanium matrix

    CERN Document Server

    Volkov, V V; Berzverkhij, P P; Martynets, V G; Matizen, E V

    2002-01-01

    Verification of theoretical forecasts on the possibility of the high-temperature superconductivity of the high-temperature superconductivity (HTSC) in the TiB sub k titanium borides is accomplished. It is established that the jump-like change in the temperature dependence of the electric resistance R(T) at 110 K takes place on the titanium samples, the surfaces whereof are coated with the borides diffusion layers of the TiB sub k variable in-depth composition. This proves the presence of the borides diffusion layers are applied onto the metallic titanium by means of treating its surface with the B sub 2 H sub 6 + H sub 2 gases mixture at the temperature of 610-700 deg C with the subsequent annealing in vacuum. The boride layers composition is studied through the mass-spectrometry method

  16. Hydrophobic silica nanoparticles as reinforcing filler for poly (lactic acid polymer matrix

    Directory of Open Access Journals (Sweden)

    Pilić Branka M.

    2016-01-01

    Full Text Available Properties of poly (lactic acid (PLA and its nanocomposites, with silica nanoparticles (SiO2, as filler were investigated. Neat PLA films and PLA films with different percentage of hydrophobic fumed silica nanoparticles (0.2, 0.5, 1, 2, 3 and 5 wt. % were prepared by solution casting method. Several tools were used to characterize the influence of different silica content on crystalline behavior, and thermal, mechanical and barrier properties of PLA/SiO2 nanocomposites. Results from scanning electron microscope (SEM showed that the nanocomposite preparation and selection of specific hydrophobic spherical nano filler provide a good dispersion of the silica nanoparticles in the PLA matrix. Addition of silica nanoparticles improved mechanical properties, the most significant improvement being observed for lowest silica content (0.2wt.%. Barrier properties were improved for all measured gases at all loadings of silica nanoparticles. The degree of crystallinity for PLA slightly increased by adding 0.2 and 0.5 wt. % of nano filler. [Projekat Ministarstva nauke Republike Srbije, br. III46001

  17. Welding of SiC particle reinforced 6061 Al matrix composite with pulsed TIG

    Institute of Scientific and Technical Information of China (English)

    陈茂爱; 武传松; 高进强

    2002-01-01

    SiCp/6061Al alloy composite was welded by using TIG and pulsed-TIG welding (P-TIG) without addition of filler metal, or with addition of Al-Si or Al-Mg filler metal. The microstructure and properties of the weld were investigated with XRD, OM, TEM, and MTS-810 testing system was used to observe the effect of different welding procedure and filler metals on the microstructure and properties of the weld. Thermodynamic of SiC-Al reaction was used to analyze the tendency of the reaction between SiC particle and Al matrix during welding. The results showed that the P-TIG tends to produce less plate-like Al4C3 precipitates than TIG; when welding with P-TIG, addition of Al-Si filler metal can not only prevent from formation of Al4C3, but also decrease hot crack sensitivity of weld; the tensile strength of joint of adding Al-Si filler metal is higher than that of adding Al-Mg filler metal. The SiCp/6061Al composite can be successfully welded by P-TIG with addition of Al-Si filler metal.

  18. Effect the Grain Size on the Polymer Matrix Composites Reinforced by Reenia Particles

    Directory of Open Access Journals (Sweden)

    Kdhim khaion kahlol

    2013-01-01

    Full Text Available Synthetic polymers such as polyurethane are used widely in the field of biomedical applications such as implants or part of implant systems.This paper focuses on the preparation of base polymer matrix composite materials by (Hand Lay-Up method, and studying the effect of selected grain size (32, 53, 63, 75, and 90 µm of (Reenia particles on some properties of the prepared composite.Mechanical tests were used to evaluate the prepared system (Tensile, Compression, Impact, and Hardness tests, and a physical test of (Water absorption %, and all tests were accomplished at room temperature.Where results showed tensile test (maximum tensile strength and modulus of elasticity high at small grain size while the percentage of elongation decreased with increasing size. As the compressive strength increased with small grain size. And also the values of hardness and fracture energy affected by particle size where the hardness and fracture energy increased at small particles size of compared to larger particles size. While the percentage of water absorption increased at large particle size.In general the results showed clear improvement in properties and maximum values which get it of tensile strength, Modulus of elasticity, elongation percentage, compression strength, fracture energy, hardness and water absorption were as follows ((34.8 MPa, (10%, (268 N/mm2, ( 54.2 MPa,( o.408 J, (78.9 Shor (D, (0.2668 % at using (32µm except water absorption was at (90µm .

  19. Preparation and properties of unidirectional boron nitride fibre reinforced boron nitride matrix composites via precursor infiltration and pyrolysis route

    Energy Technology Data Exchange (ETDEWEB)

    Li Duan, E-mail: whataboutduan@gmail.com [State Key Laboratory of Advanced Ceramic Fibres and Composites, College of Aerospace and Materials Engineering, National University of Defense Technology, Changsha 410073 (China); Zhang Changrui; Li Bin; Cao Feng; Wang Siqing; Li Junsheng [State Key Laboratory of Advanced Ceramic Fibres and Composites, College of Aerospace and Materials Engineering, National University of Defense Technology, Changsha 410073 (China)

    2011-10-25

    Highlights: {yields} BN fibres degrade little when exposed at elevated temperatures. {yields} Precursor infiltration and pyrolysis route is useful to prepare BNf/BN composites. {yields} Few reports have related to the preparation and properties of BNf/BN composites. {yields} BNf/BN composites have desirable high-temperature mechanical properties. {yields} BNf/BN composites have excellent dielectric properties at 2-18 GHz. - Abstract: The unidirectional boron nitride fibre reinforced boron nitride matrix (BN{sub f}/BN) composites were prepared via the precursor infiltration and pyrolysis (PIP) route, and the structure, composition, mechanical and dielectric properties were studied. The composites have a high content and fine crystallinity of BN. The density is 1.60 g cm{sup -3} with a low open porosity of 4.66%. The composites display good mechanical properties with the average flexural strength, elastic modulus and fracture toughness being 53.8 MPa, 20.8 GPa and 6.88 MPa m{sup 1/2}, respectively. Lots of long fibres pull-out from the fracture surface, suggesting a good fibre/matrix interface. As temperature increases, both of the flexural strength and elastic modulus exhibit a decreasing trend, with the lowest values being 36.2 MPa and 8.6 GPa at 1000 deg. C, respectively. The desirable residual ratios of the flexural strength and elastic modulus at 1000 deg. C are 67.3% and 41.3%, respectively. The composites have excellent dielectric properties, with the average dielectric constant and loss tangent being 3.07 and 0.0044 at 2-18 GHz, respectively.

  20. Study of matrix micro-cracking in nano clay and acrylic tri-block-copolymer modified epoxy/basalt fiber-reinforced pressure-retaining structures

    Directory of Open Access Journals (Sweden)

    2011-10-01

    Full Text Available In fiber-reinforced polymer pressure-retaining structures, such as pipes and vessels, micro-level failure commonly causes fluid permeation due to matrix cracking. This study explores the effect of nano-reinforcements on matrix cracking in filament-wound basalt fiber/epoxy composite structures. The microstructure and mechanical properties of bulk epoxy nanocomposites and hybrid fiber-reinforced composite pipes modified with acrylic tri-block-copolymer and organophilic layered silicate clay were investigated. In cured epoxy, the tri-block-copolymer phase separated into disordered spherical micelle inclusions; an exfoliated and intercalated structure was observed for the nano-clay. Block-copolymer addition significantly enhanced epoxy fracture toughness by a mechanism of particle cavitation and matrix shear yielding, whereas toughness remained unchanged in nano-clay filled nanocomposites due to the occurrence of lower energy resistance phenomena such as crack deflection and branching.Tensile stiffness increased with nano-clay content, while it decreased slightly for block-copolymer modified epoxy. Composite pipes modified with either the organic and inorganic nanoparticles exhibited moderate improvements in leakage failure strain (i.e. matrix cracking strain; however, reductions in functional and structural failure strength were observed.

  1. Synthesis and Characterization of In Situ Dendritic/Particulate α-Al(Fe,TM)Si Phase Reinforced Al Matrix Composites

    Science.gov (United States)

    Hou, L. G.; Wang, Shuai; He, Z. B.; Zhang, D.; Wang, X. D.; Zhuang, L. Z.; Zhang, J. S.

    2016-12-01

    The strength and ductility of transition metallic element alloyed Al alloys could be inevitably and severely weakened if these elements appeared as coarse intermetallics. Present studies aimed to optimize the morphologies and sizes of these intermetallics via composition design and process selection so as to decrease their detrimental effects to the properties. It is shown that the dendritic α-Al(Fe,TM)Si phase solidified as primary phase can be refined into small dendrites or micro- and submicro-sized particles via controlling the cooling rate and alloy composition, and this phase exhibits better heat resistance. After spark plasma sintering (SPS) the atomized alloy powders, the bulk aluminum matrix composites (AMCs) were successfully prepared and well strengthened by the uniformly distributed particulate α-Al(Fe,TM)Si phase. These sintered bulk composites also possess good heat resistance that might facilitate their application for some heat-resistant parts. The transmission electron microscope (TEM) and high-resolution TEM (HRTEM) results indicate these α-Al(Fe,TM)Si phases possesses body-centered-cubic structure with a lattice constant of 1.25 to 1.27 nm. The solidification or phase formation of these alloys is discussed as well as the densification process for the SPS of powders. The present studies indicate a possibility to prepare in situ small dendritic/particulate α-Al(Fe,TM)Si phase reinforced AMCs by using the casting process and controlling the normal impurity elements in Al alloys.

  2. A study on the damping capacity of BaTiO3-reinforced Al-matrix composites

    Indian Academy of Sciences (India)

    C J XIAO

    2016-04-01

    To study the damping capacity of BaTiO$_3$/Al composites, Al composites reinforced with BaTiO$_3$ powder (average grain sizes: 100 and 1000 nm) were fabricated by the hot-pressing sintering method. The damping properties of pure Al and BaTiO$_3$/Al composites were investigated and compared based on the dynamic mechanical analysis over a wide range of temperatures (50–285$^{\\circ}$C). Compared with pure Al matrix, 1000 nm BaTiO$_3$/Al composites with 5 and 10% mass fractions of BaTiO$_3$ exhibited better damping capacity. For 100 nm BaTiO$_3$/Al composite, its damping capacity is slightly higher than that of pure Al below 145$^{\\circ}$C, while it becomes lower above this degree. The damping capacity enhancement of BaTiO$_3$/Al composites can be explained by the ferroelastic domain damping. Furthermore, 5 and 10% BaTiO$_3$/Al composites have higher bending strength and hardness than pure Al sample.

  3. Tribological Properties of a Dendrite-reinforced Ti-based Metallic Glass Matrix Composite under Different Conditions

    Institute of Scientific and Technical Information of China (English)

    Teng ZHANG; Xiao-min LIN; Hui-jun YANG; Yong LIU; Yong-sheng WANG; Jun-wei QIAO

    2016-01-01

    The tribological properties of the in-situ dendrite-reinforced metallic glass matrix composite (Ti42 Zr22 V1 4-Cu5 Be1 7 )prepared by copper mould casting were analyzed at different normal loads under the dry condition and rain-water.The results showed that the average value of the frictional coefficients and micro-hardness ascended with in-creasing the normal load,while the wear rate showed a trend of decline under the dry condition.The electrochemical test results showed that the surface of samples was pitting corroded in the rainwater.The matrices were corroded first.Then the dendrites were exposed,leading to the damage of the surface.Both the frictional coefficients and wear rate of the composite in the rainwater were larger than those under the dry condition,primarily owing to the corro-sion of chloride ions on the worn surface.The wear mechanisms of composites were mainly adhesive wear,accompa-nied by the abrasive wear under the dry condition and corrosive wear in the rainwater.The composites have higher wear resistance both under the dry condition and rainwater due to the lower wear rate.

  4. Oxidation of SiC Fiber-Reinforced SiC Matrix Composites with a BN Interphase

    Science.gov (United States)

    Opila, Elizabeth; Boyd, Meredith K.

    2010-01-01

    SiC-fiber reinforced SiC matrix composites with a BN interphase were oxidized in reduced oxygen partial pressures of oxygen to simulate the environment for hypersonic vehicle leading edge applications. The constituent fibers as well as composite coupons were oxidized in oxygen partial pressures ranging from 1000 ppm O2 to 5% O2 balance argon. Exposure temperatures ranged from 816 C to 1353 C (1500 F to 2450 F). The oxidation kinetics of the coated fibers were monitored by thermogravimetric analysis (TGA). An initial rapid transient weight gain was observed followed by parabolic kinetics. Possible mechanisms for the transient oxidation are discussed. One edge of the composite coupon seal coat was ground off to simulate damage to the composite which allowed oxygen ingress to the interior of the composite. Oxidation kinetics of the coupons were characterized by scanning electron microscopy since the weight changes were minimal. It was found that sealing of the coupon edge by silica formation occurred. Differences in the amount and morphology of the sealing silica as a function of time, temperature and oxygen partial pressure are discussed. Implications for use of these materials for hypersonic vehicle leading edge materials are summarized.

  5. Impact of long-term thermal exposure on a SiC fiber-reinforced copper matrix composite

    Energy Technology Data Exchange (ETDEWEB)

    Kimmig, S.; Elgeti, S.; You, Jeong-Ha, E-mail: you@ipp.mpg.de

    2013-11-15

    Silicon carbide long fiber-reinforced copper matrix composites offer huge potential as a heat sink material of divertor for applications at temperatures above 300 °C thanks to the beneficial combination of strong ceramic fibers and highly conductive copper. For applications at higher operation temperatures, long term thermal stability is an issue, as thermal exposure may cause a detrimental change in microstructure in terms of chemistry and integrity of the constituents leading to overall deterioration of composite strength. The aim of this study is to investigate the impact of long term thermal exposure at an elevated temperature on a Cu/SiC{sub f} composite material. To this end, composite samples were fabricated and subjected to a heat treatment at 550 °C for 400 h. Extensive tensile tests were conducted for a wide range of fibers volume fractions to evaluate the strength before and after the heat treatment. Acoustic emission was detected in situ during tensile tests for tracking the failure events. Microscopic analysis was carried out to capture the chemical change and damage. It turned out that the applied heat treatment caused significant reduction of strength. Microanalysis revealed that infiltration and diffusion of copper into the fibers via the cracks of the damaged fibers are the direct cause of the embrittlement.

  6. Impact of long-term thermal exposure on a SiC fiber-reinforced copper matrix composite

    Science.gov (United States)

    Kimmig, S.; Elgeti, S.; You, Jeong-Ha

    2013-11-01

    Silicon carbide long fiber-reinforced copper matrix composites offer huge potential as a heat sink material of divertor for applications at temperatures above 300 °C thanks to the beneficial combination of strong ceramic fibers and highly conductive copper. For applications at higher operation temperatures, long term thermal stability is an issue, as thermal exposure may cause a detrimental change in microstructure in terms of chemistry and integrity of the constituents leading to overall deterioration of composite strength. The aim of this study is to investigate the impact of long term thermal exposure at an elevated temperature on a Cu/SiCf composite material. To this end, composite samples were fabricated and subjected to a heat treatment at 550 °C for 400 h. Extensive tensile tests were conducted for a wide range of fibers volume fractions to evaluate the strength before and after the heat treatment. Acoustic emission was detected in situ during tensile tests for tracking the failure events. Microscopic analysis was carried out to capture the chemical change and damage. It turned out that the applied heat treatment caused significant reduction of strength. Microanalysis revealed that infiltration and diffusion of copper into the fibers via the cracks of the damaged fibers are the direct cause of the embrittlement.

  7. Transitions in Wear and Friction of Carbon Fiber Reinforced Copper Matrix Composite Sliding Against AISI-1045 Steel

    Institute of Scientific and Technical Information of China (English)

    2007-01-01

    The friction and wear properties of carbon fiber reinforced copper matrix composite in dry sliding against AISI-1045 steel was evaluated by a block-on-ring test machine. It was shown that the low frictional factor and wear rate of the composite block could be maintained when pressure or velocity was below a certain value. But when the pressure or velocity exceeded the critical value, the friction factor and wear rate tended to increase rapidly with pressure and sliding velocity. The morphologies, elemental compositions, and surface profile of worn composite surfaces at different wear stages were analyzed by means of scanning electron microscopy, energy dispersive spectrometry, and profile-meter. It was found that low values of friction and wear were due to a thin solid film forming on the surface of the composite block which includes carbon and copper at a mild wear stage. The film could impede adhesion and provide some degree of self-lubrication. When the film included more metal elements and were damaged, severe wear happened, and the wear rate increased sharply. As a result, a transition diagram in friction and wear was constructed, which provided pressure and velocity conditions of change from mild wear and low friction to severe wear and high friction for the wear-resisting design.

  8. Microstructure, Properties and Wear Behaviors of (Ni3Al)p Reinforced Cu Matrix Composites

    Institute of Scientific and Technical Information of China (English)

    I brahim Celikyurek; Nese O. Korpe; Tugba Olcer; Remzi Gurler

    2011-01-01

    Pure copper and its composites reinforced with Ni3Al particles were produced by powder metallurgy (PM). Ni3Al powders were produced by mechanical ball milling from vacuum arc melted compounds. The Ni3Al powders were characterized by X-ray diffraction (XRD). The microscopy examinations revealed that the Ni3Al particles were distributed uniformly in the matrix. The effects of the particle fraction on the density, electrical conductivity, strength and dry sliding wear resistance of composite were investigated. It was found that the density and electrical conductivity of the composites decrease while the compression yield strength and wear resistance of composites increase with an increase in the particle fraction. The dry sliding wear tests were performed with pin-on-disk geometry. After sliding wear tests, the worn surfaces were examined by scanning electron microscopy (SEM) equipped with an energy dispersive X-ray spectrometer (EDS). Results have shown that the wear mechanism is oxidative and adhesive.

  9. Study on in-situ WC particles/tungsten wire reinforced iron matrix composites under electromagnetic field

    Directory of Open Access Journals (Sweden)

    Niu Libin

    2010-05-01

    Full Text Available By applying electromagnetic field to a system consisting of tungsten wires and grey cast iron melt, the grey cast iron matrix composite reinforced by either in-situ WC particles or the combination of in-situ WC particles and the residual tungsten wire was obtained. By means of differential thermal analysis (DTA, the pouring temperature of iron melt was determined at 1,573 K. The microstructures of the composites were analyzed by using of X-ray diffraction (XRD, scanning electron microscopy (SEM equipped with an energy dispersive spectrum (EDS and pin-on-disc abrasive wear test. The obtained results indicated that, with the enhancing frequency of electromagnetic field, the amount of in-situ WC particles gradually increases, leading to continuous decrease of the residual tungsten wires. When the electromagnetic field frequency was up to 4 kHz, tungsten wires reacted completely with carbon atoms in grey cast iron melt, forming WC particals. The electromagnetic field appeared to accelerate the elemental diffusion in the melt, to help relatively quick formation of a series of small Fe-W-C ternary zones and to improve the kinetic condition of in-situ WC fabrication. As compared with the composite prepared without the electromagnetic field, the composite fabricated at 4 kHz presented good wear resistance.

  10. Effects of damage and thermal residual stresses on the overall elastoplastic behavior of particle-reinforced metal matrix composites

    Science.gov (United States)

    Liu, Haitao

    The objective of the present study is to investigate damage mechanisms and thermal residual stresses of composites, and to establish the frameworks to model the particle-reinforced metal matrix composites with particle-matrix interfacial debonding, particle cracking or thermal residual stresses. An evolutionary interfacial debonding model is proposed for the composites with spheroidal particles. The construction of the equivalent stiffness is based on the fact that when debonding occurs in a certain direction, the load-transfer ability will lose in that direction. By using this equivalent method, the interfacial debonding problem can be converted into a composite problem with perfectly bonded inclusions. Considering the interfacial debonding is a progressive process in which the debonding area increases in proportion to external loading, a progressive interfacial debonding model is proposed. In this model, the relation between external loading and the debonding area is established using a normal stress controlled debonding criterion. Furthermore, an equivalent orthotropic stiffness tensor is constructed based on the debonding areas. This model is able to study the composites with randomly distributed spherical particles. The double-inclusion theory is recalled to model the particle cracking problems. Cracks inside particles are treated as penny-shape particles with zero stiffness. The disturbed stress field due to the existence of a double-inclusion is expressed explicitly. Finally, a thermal mismatch eigenstrain is introduced to simulate the inconsistent expansions of the matrix and the particles due to the difference of the coefficients of thermal expansion. Micromechanical stress and strain fields are calculated due to the combination of applied external loads and the prescribed thermal mismatch eigenstrains. For all of the above models, ensemble-volume averaging procedures are employed to derive the effective yield function of the composites. Numerical

  11. Effect of Milling Time and the Consolidation Process on the Properties of Al Matrix Composites Reinforced with Fe-Based Glassy Particles

    Directory of Open Access Journals (Sweden)

    Özge Balcı

    2015-04-01

    Full Text Available Al matrix composites reinforced with 40 vol% Fe50.1Co35.1Nb7.7B4.3Si2.8 glassy particles have been produced by powder metallurgy, and their microstructure and mechanical properties have been investigated in detail. Different processing routes (hot pressing and hot extrusion are used in order to consolidate the composite powders. The homogeneous distribution of the glassy reinforcement in the Al matrix and the decrease of the particle size are obtained through ball milling. This has a positive effect on the hardness and strength of the composites. Mechanical tests show that the hardness of the hot pressed samples increases from 51–155 HV, and the strength rises from 220–630 MPa by extending the milling time from 1–50 h. The use of hot extrusion after hot pressing reduces both the strength and hardness of the composites: however, it enhances the plastic deformation significantly.

  12. Raman Study of Uncoated and p-BN/SiC-Coated Hi-Nicalon Fiber-Reinforced Celsian Matrix Composites. Part 1; Distribution and Nanostructure of Different Phases

    Science.gov (United States)

    Gouadec, Gwenael; Colomban, Philippe; Bansal, Narottam P.

    2000-01-01

    Hi-Nicalon fiber reinforced celsian matrix composites were characterized by Raman spectroscopy and imaging, using several laser wavelengths. Composite #1 is reinforced by as-received fibers while coatings of p-BN and SiC protect the fibers in composite #2. The matrix contains traces of the hexagonal phase of celsian, which is concentrated in the neighborhood of fibers in composite #1. Some free silicon was evident in the coating of composite #2 which might involve a {BN + SiC yields BNC + Si} "reaction" at the p-BN/SiC interface. Careful analysis of C-C peaks revealed no abnormal degradation of the fiber core in the composites.

  13. Thermal diffusivity of Al-Mg based metallic matrix composite reinforced with Al{sub 2}O{sub 3} ceramic particles

    Energy Technology Data Exchange (ETDEWEB)

    Cruz-Orea, A [Departamento de Fisica, Centro de Investigacion y de Estudios Avanzados del IPN. A.P. 14.740, C.P. 07360, Mexico DF (Mexico); Morales, J E; S, R Saavedra [Departamento de Fisica, Facultad de Ciencias Fisicas y Matematicas, Universidad de Concepcion, Casilla 160-C, Concepcion (Chile); Carrasco, C, E-mail: orea@fis.cinvestav.m [Departamento de IngenierIa de Materiales, Facultad de Ingenieria, Universidad de Concepcion, Casilla 160 - C, Concepcion (Chile)

    2010-03-01

    Thermal diffusivities of Al-Mg based metallic matrix composite reinforced with ceramic particles of Al{sub 2}O{sub 3} are reported in this article. The samples were produced by rheocasting and the studied operational condition in this case is the shear rate: 800, 1400 and 2000 rpm. Additionally, the AlMg base alloy was tested. Measurements of thermal diffusivity were performed at room temperature by using photoacoustic technique.

  14. Breket titanium (Titanium bracket

    Directory of Open Access Journals (Sweden)

    Sianiwati Goenharto

    2005-09-01

    Full Text Available There has been a considerable discussion in the literature about corrosion and sensitivity to the nickel present in stainless steel brackets. Titanium has been heralded as a material totally compatible in the oral environment and superior in structural integrity compared to stainless steel. Many current applications in dentistry and medicine have made titanium an obvious choice for a possible substitute material. Titanium based brackets have shown excellent corrosion resistance and possessed good biocompatibility. Evaluation of titanium brackets for orthodontic therapy showed that titanium brackets were comparable to stainless steel brackets in passive and active configuration. Study about metallographic structure, hardness, bond strength to enamel substrate, etc. showed that titanium brackets exhibited a potential for clinical application. It was concluded that titanium brackets were suitable substitute for stainless steel brackets.

  15. Demineralized bone matrix and human cancellous bone enhance fixation of porous-coated titanium implants in sheep

    DEFF Research Database (Denmark)

    Babiker, Hassan; Ding, Ming; Overgaard, Søren

    2016-01-01

    Allogenic bone graft has been considered the gold standard in connection with bone graft material in revision joint arthroplasty. However, the lack of osteogenic potential and the risk of disease transmission are clinical challenges. The use of osteoinductive materials, such as demineralized bone...... of DBM alone, DBM with CB, or allograft on the fixation of porous-coated titanium implants. DBM100 and CB produced from human tissue were included. Both materials are commercially available. DBM granules are placed in pure DBM and do not contain any other carrier. Titanium alloy implants, 10 mm long × 10...... (gold standard), respectively. A standardized surgical procedure was used. At sacrifice 6 weeks after implantation, both distal femurs were harvested. The implant fixation was evaluated by mechanical push-out testing to test shear mechanical properties between implant and the host bone...

  16. Valorization of an industrial organosolv-sugarcane bagasse lignin: Characterization and use as a matrix in biobased composites reinforced with sisal fibers.

    Science.gov (United States)

    Ramires, Elaine C; Megiatto, Jackson D; Gardrat, Christian; Castellan, Alain; Frollini, Elisabete

    2010-11-01

    In the present study, the main focus was the characterization and application of the by-product lignin isolated through an industrial organosolv acid hydrolysis process from sugarcane bagasse, aiming at the production of bioethanol. The sugarcane lignin was characterized and used to prepare phenolic-type resins. The analysis confirmed that the industrial sugarcane lignin is of HGS type, with a high proportion of the less substituted aromatic ring p-hydroxyphenyl units, which favors further reaction with formaldehyde. The lignin-formaldehyde resins were used to produce biobased composites reinforced with different proportions of randomly distributed sisal fibers. The presence of lignin moieties in both the fiber and matrix increases their mutual affinity, as confirmed by SEM images, which showed good adhesion at the biocomposite fiber/matrix interface. This in turn allowed good load transference from the matrix to the fiber, leading to biobased composites with good impact strength (near 500 J m(-1) for a 40 wt% sisal fiber-reinforced composite). The study demonstrates that sugarcane bagasse lignin obtained from a bioethanol plant can be used without excessive purification in the preparation of lignocellulosic fiber-reinforced biobased composites displaying high mechanical properties.

  17. Production and Characterization of Brass-matrix Composites Reinforced with Ni59Zr20Ti16Si2Sn3 Glassy Particles

    Directory of Open Access Journals (Sweden)

    Bum Sung Kim

    2012-05-01

    Full Text Available Brass-matrix composites reinforced with 40 and 60 vol.% of Ni59Zr20Ti16Si2Sn3 glassy particles were produced by powder metallurgy. The crystallization behavior and the temperature dependence of the viscosity of the glass reinforcement were studied in detail to select the proper sintering parameters in order to avoid crystallization of the glassy phase during consolidation. The brass-glass powder mixtures were prepared through manual blending as well as by ball milling to analyze the effect of the matrix ligament size on the mechanical properties of the composites. The powder mixtures were then consolidated into highly-dense bulk specimens at temperatures within the supercooled liquid region by hot pressing followed by hot extrusion. The preparation of the powder mixtures has a strong influence on the mechanical behavior of the composites. The strength increases from 500 MPa for pure brass to 740 and 925 MPa for the blended composites with 40 and 60vol.% of glass reinforcement, while the strength increases to 1,240 and 1,640 MPa for the corresponding composites produced by ball milling. Modeling of the mechanical properties indicates that this behavior is related to the reduced matrix ligament size characterizing the milled composites.

  18. Investigation into the Mechanical Properties and Fracture Behavior of A356 Aluminum Alloy-Based ZrO2-Particle-Reinforced Metal-Matrix Composites

    Science.gov (United States)

    Abdizadeh, H.; Baghchesara, M. A.

    2013-11-01

    In the present study, an investigation has been carried out into the influence of ZrO2 content and casting temperature on the mechanical properties and fracture behavior of A356 Al/ZrO2 composites. A356 aluminum alloy matrix composites reinforced with 5, 10 and 15 vol.% ZrO2 were fabricated at 750, 850, and 95 0°C via the stir-casting method. Based on the results obtained, the optimum amount of reinforcement and casting temperature were determined by evaluating the density and mechanical properties of the composites through the use of hardness and tensile tests. The fracture surfaces of composite specimens were also studied to identify the main fracture mechanisms of the composites. The results obtained indicated that all samples fractured due to the interdendritic cracking of the matrix alloy. Reinforcing the Al matrix alloy with ZrO2 particles increased the hardness and ultimate tensile strength of the alloy to the maximum values of 70 BHN and 232 MPa, respectively. The best mechanical properties were obtained for the specimens with 15 vol.% of ZrO2 produced at 75 0°C.

  19. An investigation of adhesive/adherend and fiber/matrix interactions. Part A: Surface characterization of titanium dioxide, titantium and titanium 6% Al to 4% V powders: Interaction with water, hydrogen chloride and polymers

    Science.gov (United States)

    Siriwardane, R. V.; Wightman, J. P.

    1982-01-01

    The titanium dioxide surface is discussed. Polymer adhesive are also discussed. Titanium powders are considered. Characterization techniques are also considered. Interactions with polymers, water vapor, and HCl are reported. Adsorbents are characterized.

  20. Effect of type and percentage of reinforcement for optimization of the cutting force in turning of Aluminium matrix nanocomposites using response surface methodologies

    Energy Technology Data Exchange (ETDEWEB)

    Priyadarshi, Devinder [DAV Institute of Engineering and Technology, Jalandhar (India); Sharma, Rajesh Kumar [Institute of Technology, Hamirpur (India)

    2016-03-15

    Aluminium matrix composites (AMCs) now hold a significant share of raw materials in many applications. It is of prime importance to study the machinability of such composites so as to enhance their applicability. Sufficient work has been done for studying the machining of AMCs with particle reinforcements of micron range. This paper presents the study of AMCs with particle reinforcement of under micron range i.e. nanoparticles. This paper brings out the results of an experimental investigation of type and weight percent of nanoparticles on the tangential cutting force during turning operation. SiC, Gr and SiC-Gr (in equal proportions) were used with Al-6061 alloy as the matrix phase. The results indicate that composites with SiC require greater cutting force followed by hybrid and then Gr. Increase in the weight percent also significantly affected the magnitude of cutting force. RSM was used first to design and analyze the experiments and then to optimize the turning process and obtain optimal conditions of weight and type of reinforcements for turning operation.

  1. A prospective, multicenter study to evaluate clinical and radiographic outcomes in primary rotator cuff repair reinforced with a xenograft dermal matrix.

    Science.gov (United States)

    Lederman, Evan S; Toth, Alison P; Nicholson, Gregory P; Nowinski, Robert J; Bal, George K; Williams, Gerald R; Iannotti, Joseph P

    2016-12-01

    Minimal information is currently available on the outcome of rotator cuff repair reinforced with an extracellular matrix (ECM) graft. Therefore, the purpose of this study was to determine the clinical and radiographic outcome of repair of large rotator cuff tears with ECM graft reinforcement. This was a prospective study of 61 shoulders with large repairable rotator cuff tears (3 to 5 cm). The rotator cuff tears were surgically repaired and reinforced with a xenograft ECM graft. The average patient age was 56 years (range, 40-69 years). The average tear size was 3.8 cm. Follow-up was obtained at 6, 12, and 24 months in 58, 54, and 50 of the 61 patients, respectively. Functional outcome scores, isometric muscle strength, and active range of motion were significantly improved compared with baseline. Magnetic resonance imaging at 12 months showed retorn rotator cuff repairs in 33.9% of shoulders, using the criteria of a tear of at least 1 cm, and tears in 14.5% of the shoulders using the criteria of retear >80% of the original tear size. Three patients underwent surgical revision. Complications included 1 deep infection. Repair of large rotator cuff tears structurally reinforced with xenograft ECM resulted in improved functional outcomes scores and strength. Adverse events were uncommon, and the rate of revision surgery was low. Copyright © 2016 Journal of Shoulder and Elbow Surgery Board of Trustees. Published by Elsevier Inc. All rights reserved.

  2. Fatigue damage characterization of braided and woven fiber reinforced polymer matrix composites at room and elevated temperatures

    Science.gov (United States)

    Montesano, John

    The use of polymer matrix composites (PMC) for manufacturing primary load-bearing structural components has significantly increased in many industrial applications. Specifically in the aerospace industry, PMCs are also being considered for elevated temperature applications. Current aerospace-grade composite components subjected to fatigue loading are over-designed due to insufficient understanding of the material failure processes, and due to the lack of available generic fatigue prediction models. A comprehensive literature survey reveals that there are few fatigue studies conducted on woven and braided fabric reinforced PMC materials, and even fewer at elevated temperatures. It is therefore the objective of this study to characterize and subsequently model the elevated temperature fatigue behaviour of a triaxial braided PMC, and to investigate the elevated temperature fatigue properties of two additional woven PMCs. An extensive experimental program is conducted using a unique test protocol on the braided and woven composites, which consists of static and fatigue testing at various test temperatures. The development of mechanically-induced damage is monitored using a combination of non-destructive techniques which included infrared thermography, fiber optic sensors and edge replication. The observed microscopic damage development is quantified and correlated to the exhibited macroscopic material behaviour at all test temperatures. The fiber-dominated PMC materials considered in this study did not exhibit notable time- or temperature-dependent static properties. However, fatigue tests reveal that the local damage development is in fact notably influenced by temperature. The elevated temperature environment increases the toughness of the thermosetting polymers, which results in consistently slower fatigue crack propagation rates for the respective composite materials. This has a direct impact on the stiffness degradation rate and the fatigue lives for the braided

  3. Improving the corrosion wear resistance of AISI 316L stainless steel by particulate reinforced Ni matrix composite alloying layer

    Energy Technology Data Exchange (ETDEWEB)

    Xu Jiang; Zhuo Chengzhi; Tao Jie; Liu Linlin [Department of Material Science and Engineering, Nanjing University of Aeronautics and Astronautics, 29 Yudao Street, Nanjing 210016 (China); Jiang Shuyun [Department of Mechanical Engineering, Southeast University, 2 Sipailou, Nanjing 210096 (China)], E-mail: xujiang73@nuaa.edu.cn

    2009-01-07

    In order to overcome the problem of corrosion wear of AISI 316L stainless steel (SS), two kinds of composite alloying layers were prepared by a duplex treatment, consisting of Ni/nano-SiC and Ni/nano-SiO{sub 2} predeposited by brush plating, respectively, and subsequent surface alloying with Ni-Cr-Mo-Cu by a double glow process. The microstructure of the two kinds of nanoparticle reinforced Ni-based composite alloying layers was investigated by means of SEM and TEM. The electrochemical corrosion behaviour of composite alloying layers compared with the Ni-based alloying layer and 316L SS under different conditions was characterized by potentiodynamic polarization test and electrochemical impedance spectroscopy. Results showed that under alloying temperature (1000 deg. C) conditions, amorphous nano-SiO{sub 2} particles still retained the amorphous structure, whereas nano-SiC particles were decomposed and Ni, Cr reacted with SiC to form Cr{sub 6.5}Ni{sub 2.5}Si and Cr{sub 23}C{sub 6}. In static acidic solution, the corrosion resistance of the composite alloying layer with the brush plating Ni/nano-SiO{sub 2} particles interlayer is lower than that of the Ni-based alloying layer. However, the corrosion resistance of the composite alloying layer with the brush plating Ni/nano-SiO{sub 2} particles interlayer is prominently superior to that of the Ni-based alloying layer under acidic flow medium condition and acidic slurry flow condition. The corrosion resistance of the composite alloying layer with the brush plating Ni/nano-SiC particles interlayer is evidently lower than that of the Ni-based alloying layer, but higher than that of 316L SS under all test conditions. The results show that the highly dispersive nano-SiO{sub 2} particles are helpful in improving the corrosion wear resistance of the Ni-based alloying layer, whereas carbides and silicide phase are deleterious to that of the Ni-based alloying layer due to the fact that the preferential removal of the matrix

  4. Mechanical and Wear Properties of SiC/Graphite Reinforced Al359 Alloy-based Metal Matrix Composite

    Directory of Open Access Journals (Sweden)

    Shubhranshu Bansal

    2015-07-01

    Full Text Available Al359 alloy was reinforced with Silicon Carbide and Silicon Carbide/Graphite particles using stir casting process. Thereafter their mechanical and wear properties were investigated. It was found that the hardness of the Al359-Silicon Carbide composite is better than Al359-Silicon Carbide-Graphite composite. The Silicon Carbide/Graphite reinforced composite exhibits a superior ultimate tensile strength against Silicon Carbide reinforced composite. The wear test was conducted at different loading, sliding velocities and sliding distances conditions. Results showed that the wear resistance of Al359 alloy increased with the reinforcement of Silicon Carbide/Graphite material for higher loading, sliding velocities and sliding distance conditions. SEM images of the worn surface of the pin were examined to study their wear mechanism.Defence Science Journal, Vol. 65, No. 4, July 2015, pp. 330-338, DOI: http://dx.doi.org/10.14429/dsj.65.8676

  5. Improve Wear Resistance on Al 332 Alloy Matrix- Micro -Nano Al2O3 Particles Reinforced Composite

    Directory of Open Access Journals (Sweden)

    Rawnaq Ahmed Mohamed

    2014-03-01

    Full Text Available The wear behavior of alumina particulate reinforced A332 aluminium alloy composites produced by a stir casting process technique were investigated. A pin-on-disc type apparatus was employed for determining the sliding wear rate in composite samples at different grain size (1 µm, 12µm, 50 nm and different weight percentage (0.05-0.1-0.5-1 wt% of alumina respectively. Mechanical properties characterization which strongly depends on microstructure properties of reinforcement revealed that the presence of ( nano , micro alumina particulates lead to simultaneous increase in hardness, ultimate tensile stress (UTS, wear resistances. The results revealed that UTS, Hardness, Wear resistances increases with the increase in the percentage of reinforcement of Al2O3 when compared to the base alloy A332. The wear rates of the composites were considerably less than that of the aluminum alloy at all applied loads with increasing percentage of reinforcement when compared to the base alloy A332.

  6. Raman Study of Uncoated and P-bn/sic-coated Hi-nicalon Reinforced Celsian Matrix Composites. Part 2; Residual Stress in the Fibers

    Science.gov (United States)

    Gouadec, Gwenael; Colomban, Philippe; Bansal, Narottam P.

    2000-01-01

    Band shifts on Raman spectra were used to assess, at a microscopic scale, the residual strain existing in Hi-Nicalon fibers reinforcing celsian matrix composites. Uncoated as well as p-BN/SiC- and p-B(Si)N/SiC-coated Hi-Nicalon fibers were used as the reinforcements. We unambiguously conclude that the fibers are in a state of compressive residual stress. Quantitative determination of the residual stress was made possible by taking into account the heating induced by laser probing and by using a reference line, of fixed wavenumber. We found fiber compressive residual stress values between 110 and 960 MPa depending on the fiber/matrix coating in the composite. A stress relaxation-like phenomenon was observed at the surface of p-BN/SiC-coated Hi-Nicalon fibers whereas the uncoated or p-B(Si)N/SiC-coated Hi-Nicalon fibers did not show any stress relaxation in the Celsian matrix composites.

  7. Microstructure and Mechanical Properties of Unidirectional W Filament Reinforced Al-6Ti-6Nb and SiCp-Al-6Ti-6Nb Matrix Composites

    Institute of Scientific and Technical Information of China (English)

    2000-01-01

    Unidirectional Tungsten filament (Wf) reinforced pure Al,Al-6Ti-6Nb and SiCp-Al-6Ti-6Nb matrix composites were prepared by hot-pressing in vacuum atmosphere,their microstructure and room temperature mechanical properties were investigated. It was indicated that no reaction products appeared at Wf/Al interfaces in pure Al matrix composites. While, in Wf/Al-6Ti-6Nb and Wf/SiCp-Al-6Ti-6Nb,intermetallic WAl4 interfacial reaction products formed. Much better strengthening effect from W filament was shown in the Wf/Al-6Ti-6Nb and Wf/SiCp-Al-6Ti-6Nb composites than in the pure Al matrix composite. Their strength reached 319 and 339MPa, respectively, with only a small content of Wf(<5Vol.%). The excellent reinforcement effects could be predominantly attributed to the strong Wf/Al interfacial bonding strength due to the interfacial reaction.

  8. IN-SITU SYNTHETIC TiB2 PARTICULATE REINFORCED METAL MATRIX COMPOSITE COATING ON AA2024 ALUMINUM ALLOY BY LASER CLADDING TECHNOLOGY

    OpenAIRE

    JIANG XU; YIDE KAN; WENJIN LIU

    2005-01-01

    In order to improve the wear resistance of aluminum alloy, in-situ synthesized TiB2 and Ti3B4 peritectic composite particulate reinforced metal matrix composite, formed on a 2024 aluminum alloy by laser cladding with a powder mixture of Fe-coated Boron, Ti and Al, was successfully achieved using 3-KW CW CO2 laser. The chemical composition, microstructure and phase structure of the composite clad coating were analyzed by energy dispersive X-ray spectroscopy (EDX), SEM, AFM and XRD. The typical...

  9. Influence of the Sr and Mg Alloying Additions on the Bonding Between Matrix and Reinforcing Particles in the AlSi7Mg/SiC-Cg Hybrid Composite

    Directory of Open Access Journals (Sweden)

    Dolata A. J.

    2016-06-01

    Full Text Available The aim of the work was to perform adequate selection of the phase composition of the composite designated for permanent - mould casting air compressor pistons. The hybrid composites based on AlSi7Mg matrix alloy reinforced with mixture of silicon carbide (SiC and glassy carbon (Cg particles were fabricated by the stir casting method. It has been shown that the proper selection of chemical composition of matrix alloy and its modification by used magnesium and strontium additions gives possibility to obtain both the advantageous casting properties of composite suspensions as well as good bonding between particles reinforcements and matrix.

  10. Synergistic Effects of Stress-Rupture and Cyclic Loading on Strain Response of Fiber-Reinforced Ceramic-Matrix Composites at Elevated Temperature in Oxidizing Atmosphere

    Directory of Open Access Journals (Sweden)

    Longbiao Li

    2017-02-01

    Full Text Available In this paper, the synergistic effects of stress rupture and cyclic loading on the strain response of fiber-reinforced ceramic-matrix composites (CMCs at elevated temperature in air have been investigated. The stress-strain relationships considering interface wear and interface oxidation in the interface debonded region under stress rupture and cyclic loading have been developed to establish the relationship between the peak strain, the interface debonded length, the interface oxidation length and the interface slip lengths. The effects of the stress rupture time, stress levels, matrix crack spacing, fiber volume fraction and oxidation temperature on the peak strain and the interface slip lengths have been investigated. The experimental fatigue hysteresis loops, interface slip lengths, peak strain and interface oxidation length of cross-ply SiC/MAS (magnesium alumino-silicate, MAS composite under cyclic fatigue and stress rupture at 566 and 1093 °C in air have been predicted.

  11. Modeling Strength Degradation of Fiber-Reinforced Ceramic-Matrix Composites Subjected to Cyclic Loading at Elevated Temperatures in Oxidative Environments

    Science.gov (United States)

    Longbiao, Li

    2017-04-01

    In this paper, the strength degradation of non-oxide and oxide/oxide fiber-reinforced ceramic-matrix composites (CMCs) subjected to cyclic loading at elevated temperatures in oxidative environments has been investigated. Considering damage mechanisms of matrix cracking, interface debonding, interface wear, interface oxidation and fibers fracture, the composite residual strength model has been established by combining the micro stress field of the damaged composites, the damage models, and the fracture criterion. The relationships between the composite residual strength, fatigue peak stress, interface debonding, fibers failure and cycle number have been established. The effects of peak stress level, initial and steady-state interface shear stress, fiber Weibull modulus and fiber strength, and testing temperature on the degradation of composite strength and fibers failure have been investigated. The evolution of residual strength versus cycle number curves of non-oxide and oxide/oxide CMCs under cyclic loading at elevated temperatures in oxidative environments have been predicted.

  12. Ni添加对TiB2/TiB钛基复合涂层组织与力学性能的影响%EFFECT OF Ni ADDITION ON MICROSTRUCTURE AND MECHANICAL PROPERTIES OF TiB2/TiB TITANIUM MATRIX COMPOSITE COATINGS

    Institute of Scientific and Technical Information of China (English)

    林英华; 雷永平; 符寒光; 林健

    2014-01-01

    Titanium alloys have been known as useful materials for their superior mechanical properties,low density and high specific strength.However,the application of conventional titanium alloys on engine parts of airplane is limited by their poor wear resistance,low fatigue strength and low hardness.Particles reinforced titanium matrix composites have attracted extensive investigation in material science and engineering.Mechanical properties can be improved by reinforcing the loaded outer layer of Ti with ceramic particles.TiB and TiB2 are considered as the excellent ceramic reinforced particles for their compatible physical and thermodynamic properties,high hardness and Young's modulus of elasticity.However,TiB2 has high brittleness.The intermetallic compound NiTi,wellknown for its shape memory effect and pseudo-elasticity,is one of the rarely few intermetallic compounds having excellent combination of high strength,ductility and toughness as well as excellent wear resistance and fabrication processing properties.An in situ TiB/TiB2 structured ceramic materials as the reinforcing phase and NiTi interrnetallic phase as the matrix would be expected to have an outstanding combination of high hardness and toughness.To investigate the microstructure and properties of the cladded layers,two types of composites were prepared by laser cladding powders containing TiB2 and Ni+TiB2 as a preset level on the surface of titanium alloy.The composite coatings were analyzed by XRD,SEM,EPMA,micro hardness tester and brinell hardness.The results showed that TiB2 particulate and TiB short fiber reinforced titanium matrix composite coating were obtained,which had poor quality of coating shape when Ni was not added.The coating was mainly composed of TiB2,TiB,Ti and NiTi phase when Ni was added and surface coating quality was improved and the bcc structure of NiTi alloy was filled with TiB2 particulate and TiB short fiber surrounding.The coating was coarse with particle size of TiB2 at 3~5

  13. Tribo-Mechanisms of Carbon Nanotubes: Friction and Wear Behavior of CNT-Reinforced Nickel Matrix Composites and CNT-Coated Bulk Nickel

    Directory of Open Access Journals (Sweden)

    Leander Reinert

    2016-04-01

    Full Text Available In this study, nickel matrix composites reinforced by carbon nanotubes (CNTs are compared to unreinforced CNT-coated (by drop-casting bulk nickel samples in terms of their friction and wear behavior, thus gaining significant knowledge regarding the tribological influence of CNTs and the underlying tribo-mechanism. It has been shown that the frictional behavior is mainly influenced by the CNTs present in the contact zone, as just minor differences in the coefficient of friction between the examined samples can be observed during run-in. Consequently, the known effect of a refined microstructure, thus leading to an increased hardness of the CNT reinforced samples, seems to play a minor role in friction reduction compared to the solid lubrication effect induced by the CNTs. Additionally, a continuous supply of CNTs to the tribo-contact can be considered isolated for the reinforced composites, which provides a long-term friction reduction compared to the CNT-coated sample. Finally, it can be stated that CNTs can withstand the accumulated stress retaining to some extent their structural state for the given strain. A comprehensive study performed by complementary analytical methods is employed, including Raman spectroscopy and scanning electron microscopy to understand the involved friction and wear mechanisms.

  14. Microstructural characteristics, mechanical and wear behaviour of aluminium matrix hybrid composites reinforced with alumina, rice husk ash and graphite

    Directory of Open Access Journals (Sweden)

    Kenneth Kanayo Alaneme

    2015-09-01

    Full Text Available The microstructural characteristics, mechanical and wear behaviour of Aluminium matrix hybrid composites reinforced with alumina, rice husk ash (RHA and graphite were investigated. Alumina, RHA and graphite mixed in varied weight ratios were utilized to prepare 10 wt% hybrid reinforced Al-Mg-Si alloy based composites using two-step stir casting. Hardness, tensile properties, scanning electron microscopy, and wear tests were used to characterize the composites produced. The results show that Hardness decreases with increase in the weight ratio of RHA and graphite in the composites; and with RHA content greater than 50%, the effect of graphite on the hardness becomes less significant. The tensile strength for the composites containing o.5wt% graphite and up to 50% RHA was observed to be higher than that of the composites without graphite. The toughness values for the composites containing 0.5wt% graphite were in all cases higher than that of the composites without graphite. The % Elongation for all composites produced was within the range of 10–13% and the values were invariant to the RHA and graphite content. The tensile fracture surface morphology in all the composites produced was identical characterized with the presence of reinforcing particles housed in ductile dimples. The composites without graphite exhibited greater wear susceptibility in comparison to the composite grades containing graphite. However the wear resistance decreased with increase in the graphite content from 0.5 to 1.5 wt%.

  15. Structural evolution during mechanical milling of nanometric and micrometric Al{sub 2}O{sub 3} reinforced Al matrix composites

    Energy Technology Data Exchange (ETDEWEB)

    Hesabi, Z. Razavi [Department of Materials Science and Engineering, Sharif University of Technology, P.O. Box 11365-9466, Azadi Avenue, 14588 Tehran (Iran, Islamic Republic of); Simchi, A. [Department of Materials Science and Engineering, Sharif University of Technology, P.O. Box 11365-9466, Azadi Avenue, 14588 Tehran (Iran, Islamic Republic of) and Institute for Nanoscience and Nanotechnology, Sharif University of Technology, P.O. Box 11365-9466, Azadi Avenue, 14588 Tehran (Iran, Islamic Republic of)]. E-mail: simchi@sharif.edu; Reihani, S.M. Seyed [Department of Materials Science and Engineering, Sharif University of Technology, P.O. Box 11365-9466, Azadi Avenue, 14588 Tehran (Iran, Islamic Republic of)

    2006-07-25

    The morphological and microstructural changes during mechanical milling of Al powder mixed with 5 vol% nanoscaled alumina particles (35 nm) were studied. The milling was performed in a planetary ball mill under argon atmosphere for various times up to 24 h. The process was also conducted for Al and Al-5 vol% Al{sub 2}O{sub 3} (1 {mu}m) powders to explore the role of reinforcement nanoparticles on the mechanical milling stages. The results showed that the addition of hard particles accelerate the milling process, leading to faster work hardening rate and fracture of the aluminum matrix. Meanwhile, the structural evolution during mechanical milling of the microcomposite powder occurred faster than that of the nanocomposite powder. The result of X-ray diffraction analysis by Williamson-Hall method determined that the so-called crystallite size and lattice strain of the Al matrix of nanocomposite are smaller than that of the microcomposite. Meantime, the particle size distribution and bulk powder density of the two composites were found to be rather equal after 20 h milling, but they were significantly different from those of the unreinforced Al. The mechanisms of mechanical milling for the reinforced and unreinforced Al powders are addressed with stressing on the role of alumina particles.

  16. Fabrication of carbon nanofiber-reinforced aluminum matrix composites assisted by aluminum coating formed on nanofiber surface by in situ chemical vapor deposition

    Science.gov (United States)

    Ogawa, Fumio; Masuda, Chitoshi

    2015-01-01

    The van der Waals agglomeration of carbon nanofibers (CNFs) and the weight difference and poor wettability between CNFs and aluminum hinder the fabrication of dense CNF-reinforced aluminum matrix composites with superior properties. In this study, to improve this situation, CNFs were coated with aluminum by a simple and low-cost in situ chemical vapor deposition (in situ CVD). Iodine was used to accelerate the transport of aluminum atoms. The coating layer formed by the in situ CVD was characterized using scanning electron microscopy, transmission electron microscopy, x-ray diffraction, Fourier transform-infrared spectroscopy, and x-ray photoelectron spectroscopy. The results confirmed that the CNFs were successfully coated with aluminum. The composites were fabricated to investigate the effect of the aluminum coating formed on the CNFs. The dispersion of CNFs, density, Vickers micro-hardness and thermal conductivity of the composites fabricated by powder metallurgy were improved. Pressure-less infiltration experiments were conducted to fabricate composites by casting. The results demonstrated that the wettability and infiltration were dramatically improved by the aluminum coating layer on CNFs. The aluminum coating formed by the in situ CVD technique was proved to be effective for the fabrication of CNF-reinforced aluminum matrix composites.

  17. A new consideration on reinforcement distribution in the different planes of nanostructured metal matrix composite sheets prepared by accumulative roll bonding (ARB)

    Energy Technology Data Exchange (ETDEWEB)

    Yazdani, Ali [Department of Materials Science and Engineering, School of Engineering, Shiraz University, Zand Blvd., 7134851154 Shiraz (Iran, Islamic Republic of); Salahinejad, E., E-mail: erfan.salahinejad@gmail.com [Department of Materials Science and Engineering, School of Engineering, Shiraz University, Zand Blvd., 7134851154 Shiraz (Iran, Islamic Republic of); Moradgholi, J.; Hosseini, M. [Department of Materials Science and Engineering, School of Engineering, Shiraz University, Zand Blvd., 7134851154 Shiraz (Iran, Islamic Republic of)

    2011-09-29

    Highlights: > Al-B{sub 4}C composites can be successfully prepared by accumulative roll bonding (ARB). > TEM reveals the development of nanostructures in Al-B{sub 4}C composites processed by ARB. > The reinforcement distribution in the RD-ND planes is more uniform than the TD-ND planes. - Abstract: Recently, a number of novel methods based on accumulative roll bonding (ARB) have been introduced to produce particulate metal matrix composites. Nonetheless, the microstructure uniformity from the reinforcement distribution viewpoint in the different planes of ARBed composite sheets has not been focused up to date. This paper aims to compare the evolution of the B{sub 4}C particles distribution in nanostructured Al-10 vol.% B{sub 4}C composites prepared by ARB in the rolling direction-normal direction (RD-ND) and transverse direction-normal direction (TD-ND) planes. From optical microscopic evaluations quantified by the radial distribution function analysis, it is realized that the homogeneity in the RD-ND planes is in excess of the TD-ND planes. In addition, transmission electron microscopy reveals the development of nanostructures in the Al matrix after seven ARB passes.

  18. Development of the method of obtaining donor-acceptor complexes of titanium tetrachloride as a precursor of oxide materials based on titanium oxide and silicon matrix for the catalytically active nanoparticles of platinum group metals

    Directory of Open Access Journals (Sweden)

    A. M. Nemeryuk

    2015-12-01

    Full Text Available The method of preparation of the complex of titanium tetrachloride with dimethylformamide and reactivity when reacted with an alcohol and salts of hydrazine described. Obtained multinuclear complexes containing titanium and palladium as potential precursors of catalytically active materials.

  19. Development of an in-situ multi-component reinforced Al-based metal matrix composite by direct metal laser sintering technique — Optimization of process parameters

    Energy Technology Data Exchange (ETDEWEB)

    Ghosh, Subrata Kumar, E-mail: subratagh82@gmail.com [Department of Mechanical Engineering, National Institute of Technology Agartala, Tripura 799055 (India); Bandyopadhyay, Kaushik; Saha, Partha [Department of Mechanical Engineering, Indian Institute of Technology Kharagpur, Kharagpur 721302 (India)

    2014-07-01

    In the present investigation, an in-situ multi-component reinforced aluminum based metal matrix composite was fabricated by the combination of self-propagating high-temperature synthesis and direct metal laser sintering process. The different mixtures of Al, TiO{sub 2} and B{sub 4}C powders were used to initiate and maintain the self-propagating high-temperature synthesis by laser during the sintering process. It was found from the X-ray diffraction analysis and scanning electron microscopy that the reinforcements like Al{sub 2}O{sub 3}, TiC, and TiB{sub 2} were formed in the composite. The scanning electron microscopy revealed the distribution of the reinforcement phases in the composite and phase identities. The variable parameters such as powder layer thickness, laser power, scanning speed, hatching distance and composition of the powder mixture were optimized for higher density, lower porosity and higher microhardness using Taguchi method. Experimental investigation shows that the density of the specimen mainly depends upon the hatching distance, composition and layer thickness. On the other hand, hatching distance, layer thickness and laser power are the significant parameters which influence the porosity. The composition, laser power and layer thickness are the key influencing parameters for microhardness. - Highlights: • The reinforcements such as Al{sub 2}O{sub 3}, TiC, and TiB{sub 2} were produced in Al-MMC through SHS. • The density is mainly influenced by the material composition and hatching distance. • Hatching distance is the major influencing parameter on porosity. • The material composition is the significant parameter to enhance the microhardness. • The SEM micrographs reveal the distribution of TiC, TiB{sub 2} and Al{sub 2}O{sub 3} in the composite.

  20. Strong Surface Treatment Effects on Reinforcement Efficiency in Biocomposites Based on Cellulose Nanocrystals in Poly(vinyl acetate) Matrix.

    Science.gov (United States)

    Ansari, Farhan; Salajková, Michaela; Zhou, Qi; Berglund, Lars A

    2015-12-14

    In this work, the problem to disperse cellulose nanocrystals (CNC) in hydrophobic polymer matrices has been addressed through application of an environmentally friendly chemical modification approach inspired by clay chemistry. The objective is to compare the effects of unmodified CNC and modified CNC (modCNC) reinforcement, where degree of CNC dispersion is of interest. Hydrophobic functionalization made it possible to disperse wood-based modCNC in organic solvent and cast well-dispersed nanocomposite films of poly(vinyl acetate) (PVAc) with 1-20 wt % CNC. Composite films were studied by infrared spectroscopy (FT-IR), UV-vis spectroscopy, dynamic mechanical thermal analysis (DMTA), tensile testing, and field-emission scanning electron microscopy (FE-SEM). Strongly increased mechanical properties were observed for modCNC nanocomposites. The reinforcement efficiency was much lower in unmodified CNC composites, and specific mechanisms causing the differences are discussed.

  1. Laser-Deposited In Situ TiC-Reinforced Nickel Matrix Composites: 3D Microstructure and Tribological Properties (Postprint)

    Science.gov (United States)

    2014-04-03

    was measured using a stan- dard Vickers microhardness tester using a 300-g load. Sliding friction and wear testing was con- ducted with a Falex (Implant...exported to AvizoFire 6.3 format for 3D visualization of TiC and graphite reinforcements. Microhardness and Tribological Properties The microhardness ...Sciences) ISC-200 pin- on-disk (POD) system at room temperature. The samples were openly exposed in lab air (40% RH) during the tests . Tests were

  2. Study on dry friction and wear resistance of a WC-Co particle reinforced iron matrix composite material

    OpenAIRE

    Zhang Peng; Zeng Shaolian; Zhang Zhiguo

    2013-01-01

    In order to select a suitable material for the rolling mill guide application, the dry sliding friction and wear resistance of a tungsten carbide combining cobalt (WC-Co) particle reinforced chromium cast iron composite material were studied. In particular, the wear resistance was discussed in detail. The results showed that the composite material demonstrates 25 times the wear resistance of high Cr cast iron, and 9 times the wear resistance of heat resistant steel. However, the average frict...

  3. Preparation and performance of ZnO nanowires modified carbon fibers reinforced NiFe{sub 2}O{sub 4} ceramic matrix composite

    Energy Technology Data Exchange (ETDEWEB)

    Zhang, Lei, E-mail: jwlzl77@163.com; Jiao, Wanli

    2013-12-25

    Highlights: •Unlike existing chemical modification, the liquid growth remains fiber’s strength. •ZnO nanowires array are grown on carbon fibers with controllable morphology. •ZnO nanowires array modified carbon fibers can reinforce the strength of ceramic matrix composite. •This research will provide a means to produce multifunctional composites. -- Abstract: The surface of carbon fibers was modified by ZnO nanowires using the liquid growth method. NiFe{sub 2}O{sub 4} ceramic matrix composites reinforced by the modified carbon fibers were prepared by a high-temperature solid-state reaction method at 1300 °C for 5 h in N{sub 2} atmosphere. The influences of modified carbon fibers on the mechanical performances of NiFe{sub 2}O{sub 4} composites were investigated. The crystal structure of modified carbon fibers and the morphology of modified carbon fibers surface and the NiFe{sub 2}O{sub 4} composites fracture cross-section were observed by meaning of X-ray diffraction (XRD) and scanning electron microscope (SEM), respectively. The results showed that hexagonal wurtzite ZnO nanowires array grew from the surface of carbon fibers vertically, with nanowires diameters ranging from 170 nm to 380 nm and lengths up to 2.8 μm. Unlike existing chemical modification and high temperature oxidation method, the liquid growth allowed morphology control and maintained the single fiber tensile strength substantially unchanged under certain growth procedures. Compared to pure NiFe{sub 2}O{sub 4} ceramic and bare carbon fibers reinforced NiFe{sub 2}O{sub 4} composite, the bending strength of NiFe{sub 2}O{sub 4} composite reinforced with ZnO nanowires surface modified carbon fibers was shown to increase by up to 70% and 45%, respectively. The development of an interphase offering control over the morphology will provide a means to produce multifunctional composites.

  4. Synthesis and analysis of nanocrystalline β1-Cu3Al and β2-NiAl intermetallic-reinforced aluminum matrix composite by high energy ball milling

    Science.gov (United States)

    Nguyen, Hong-Hai; Nguyen, Minh-Thuyet; Kim, Won Joo; Kim, Jin-Chun

    2017-01-01

    Nanocrystalline β1-Cu3Al and β2-NiAl intermetallic compounds were in-situ reinforced in the aluminum matrix with the atomic composition of Al67Cu20Ni13 by the mechanical alloying of elemental powders. Both β1-Cu3Al, β2-NiAl phases that can be only co-synthesized in Cu base alloys have been obtained after 15h milling in this study. The phase evolution during milling process was investigated by X-ray diffraction. The β1-Cu3Al, β2-NiAl phases were metastable with further milling time up to 40 h. Specially, unreacted Al matrix has been totally transformed to amorphous state in the final powder. A remarkable crystalline size of 6.5 nm was reached after 15 h milling time. Thermal stability of the milled powder was also studied by differential thermal analysis. It is shown that β1-Cu3Al, β2-NiAl phases were stable up to higher than 550 °C. Moreover, the inter-diffusion between Al matrix and Cu3Al within the temperature range of 620-740 °C led to the formation of superstructure ζ1-Al3Cu4 phase.

  5. Effect of Zircon Silicate Reinforcements on the Microstructure and Properties of as Cast Al-4.5Cu Matrix Particulate Composites Synthesized via Squeeze Cast Route

    Directory of Open Access Journals (Sweden)

    E. G. Okafor

    2010-06-01

    Full Text Available The as-cast microstructure and properties of Al-4.5Cu/ZrSiO4 particulate composite synthesized via squeezed casting route was studied, varying the percentage ZrSiO4 in the range of 5-25wt%. The result obtained revealed that addition of ZrSiO4 reinforcements, increased the hardness value and apparent porosity by 107.65 and 34.23% respectively and decrease impact energy by 43.16 %. As the weight percent of ZrSiO4 increases in the matrix alloy, the yield and ultimate tensile strength increased by 156.52 and 155.81% up to a maximum of 15% ZrSiO4 addition respectively. The distribution of the brittle ZrSiO4 phase in the ductile matrix alloy led to increase strength and hardness values. These results had shown that, additions of ZrSiO4 particles to Al-4.5Cu matrix alloy improved properties.

  6. Low-Temperature Forming of Beta Titanium Alloys

    Science.gov (United States)

    Kaneko, R. S.; Woods, C. A.

    1983-01-01

    Low cost methods for titanium structural fabrication using advanced cold-formable beta alloys were investigated for application in a Mach 2.7 supersonic cruise vehicle. This work focuses on improving processing and structural efficiencies as compared with standard hot formed and riveted construction of alpha-beta alloy sheet structure. Mechanical property data and manufacturing parameters were developed for cold forming, brazing, welding, and processing Ti-15V-3Cr-3Sn-3Al sheet, and Ti-3Al-8V-6Cr-4Zr on a more limited basis. Cost and structural benefits were assessed through the fabrication and evaluation of large structural panels. The feasibility of increasing structural efficiency of beta titanium structure by selective reinforcement with metal matrix composite was also explored.

  7. 球形纤维素-钛白粉复合基质的扩张床流体混合特性%Physical and Hydrodynamic Properties of Spherical Cellulose-Titanium Dioxide Composite Matrix for Expanded Bed Adsorption

    Institute of Scientific and Technical Information of China (English)

    雷引林; 林东强; 姚善泾; 刘坐镇; 朱自强

    2003-01-01

    Expanded bed adsorption (EBA) has been widely used in industrial downstream bioprocessing. Solid matrix is the principal pillar supporting the successful application of EBA. A novel spherical cellulose-titanium dioxide composite matrix was prepared through the method of water-in-oil suspension thermal regeneration. Its typical physical properties were wet density 1.18g.cm-3, diameters in the range of 100-300μm, porosity 85.5%,and water content 72.3%. Expansion characteristics and liquid mixing performance of the matrix in expanded bed were investigated using water and 10% (by mass) glycerol solution as mobile phases. The results indicate that the custom-assembled matrix has a stable flow hydrodynamics and exhibits the same degree of liquid-phase mixing or column efficiency as the commercially available Streamline adsorbent.

  8. Microstructure and Mechanical Properties of Vacuum Hot Pressed P/M Short Steel Fiber Reinforced Aluminum Matrix Composites

    OpenAIRE

    Jain, S.; K. Chandra; Agarwala, V

    2014-01-01

    Commercial purity aluminum powder of irregular shape and ligamental morphology having average particle size of 75 µm was blended with medium carbon steel short fibers having average diameter of 100 µm and maximum length up to 1000 µm. The green compacts of pure aluminum and reinforced compositions were hot-pressed in 10−3 torr vacuum, at 723 K, 773 K, and 823 K for 5, 10, and 15 min durations under 50 MPa axial stress on Gleeble 3800 simulator. Microstructures of the sintered composites have ...

  9. Synthesis and characterization of nanocomposite powders of calcium phosphate/titanium oxide for biomedical applications

    Energy Technology Data Exchange (ETDEWEB)

    Delima, S.A.; Camargo, N.H.A.; Souza, J.C.P.; Gemelli, E., E-mail: sarahamindelima@hotmail.com, E-mail: dem2nhac@joinville.udesc.br, E-mail: souzajulio@joinville.udesc.br, E-mail: gemelli@joinville.udesc.br [Universidade do Estado de Santa Catarina (UDESC), Joinville, SC (Brazil). Centro de Ciencias Tecnologicas

    2009-07-01

    The nanostructured bioceramics of calcium phosphate are current themes of research and they are becoming important as bone matrix in regeneration of tissues in orthopedic and dental applications. Nanocomposite powders of calcium phosphate, reinforced with nanometric particles of titanium oxide, silica oxide and alumina oxid ealpha, are being widely studied because they offer new microstructures, nanostructures and interconnected microporosity with high superficial area of micropores that contribute to osteointegration and osteoinduction processes. This study is about the synthesis of nanocomposites powders of calcium phosphate reinforced with 1%, 2%, 3% and 5% in volume of titanium oxide and its characterization through the techniques of X-Ray Diffraction (XRD), Scanning Electron Microscopy (SEM), Differential Thermal Analysis (DTA), Thermogravimetry (TG) and Dilatometry. (author)

  10. Lightweight Protective Coatings For Titanium Alloys

    Science.gov (United States)

    Wiedemann, Karl E.; Taylor, Patrick J.; Clark, Ronald K.

    1992-01-01

    Lightweight coating developed to protect titanium and titanium aluminide alloys and titanium-matrix composite materials from attack by environment when used at high temperatures. Applied by sol-gel methods, and thickness less than 5 micrometers. Reaction-barrier and self-healing diffusion-barrier layers combine to protect titanium alloy against chemical attack by oxygen and nitrogen at high temperatures with very promising results. Can be extended to protection of other environmentally sensitive materials.

  11. Enhanced micro-vibration sensitive high-damping capacity and mechanical strength achieved in Al matrix composites reinforced with garnet-like lithium electrolyte

    Science.gov (United States)

    Wang, Xian-Ping; Zhang, Yi; Xia, Yu; Jiang, Wei-Bing; Liu, Hui; Liu, Wang; Gao, Yun-Xia; Zhang, Tao; Fang, Qian-Feng

    2016-12-01

    A novel micro-vibration sensitive-type high-damping Al matrix composites reinforced with Li7-xLa3Zr2-xNbxO12 (LLZNO, x = 0.25) was designed and prepared using an advanced spark plasma sintering (SPS) technique. The damping capacity and mechanical properties of LLZNO/Al composites (LLZNO content: 0-40 wt.%) were found to be greatly improved by the LLZNO addition. The maximum damping capacity and the ultimate tensile strength (UTS) of LLZNO/Al composite can be respectively up to 0.033 and 101.2 MPa in the case of 20 wt.% LLZNO addition. The enhancement of damping and mechanical properties of the composites was ascribed to the intrinsic high-damping capacity and strengthening effects of hard LLZNO particulate. This investigation provides a new insight to sensitively suppress micro-vibration of payloads in the aerospace environment.

  12. Reinforcing effect of plasma modified halloysite nanotubes in a carbon black filled natural rubber-butadien rubber matrix

    NARCIS (Netherlands)

    Poikelispaa, Minna; Das, Amit; Dierkes, Wilma; Vuorinen, Jyrki

    2011-01-01

    Rubber composites are generally produced by the direct incorporation of fillers like carbon black and/or silica into the rubber matrix. The incorporation of different types of nanofillers is the subject of recent research with the aim of preparing composites with special compositions and properties.

  13. Multi-Length Scale-Enriched Continuum-Level Material Model for Kevlar®-Fiber-Reinforced Polymer-Matrix Composites

    Science.gov (United States)

    Grujicic, M.; Pandurangan, B.; Snipes, J. S.; Yen, C.-F.; Cheeseman, B. A.

    2013-03-01

    Fiber-reinforced polymer matrix composite materials display quite complex deformation and failure behavior under ballistic/blast impact loading conditions. This complexity is generally attributed to a number of factors such as (a) hierarchical/multi-length scale architecture of the material microstructure; (b) nonlinear, rate-dependent and often pressure-sensitive mechanical response; and (c) the interplay of various intrinsic phenomena and processes such as fiber twisting, interfiber friction/sliding, etc. Material models currently employed in the computational engineering analyses of ballistic/blast impact protective structures made of this type of material do not generally include many of the aforementioned aspects of the material dynamic behavior. Consequently, discrepancies are often observed between computational predictions and their experimental counterparts. To address this problem, the results of an extensive set of molecular-level computational analyses regarding the role of various microstructural/morphological defects on the Kevlar® fiber mechanical properties are used to upgrade one of the existing continuum-level material models for fiber-reinforced composites. The results obtained show that the response of the material is significantly affected as a result of the incorporation of microstructural effects both under quasi-static simple mechanical testing condition and under dynamic ballistic-impact conditions.

  14. Effect of particle concentration on the structure and tribological properties of submicron particle SiC reinforced Ni metal matrix composite (MMC) coatings produced by electrodeposition

    Energy Technology Data Exchange (ETDEWEB)

    Guel, H., E-mail: harungul@duzce.edu.tr [Duzce University, Gumusova Vocational School, Department of Metallurgy, 81850, Duzce (Turkey); K Latin-Small-Letter-Dotless-I l Latin-Small-Letter-Dotless-I c, F.; Uysal, M.; Aslan, S.; Alp, A.; Akbulut, H. [Sakarya University, Engineering Faculty, Department of Metallurgical and Materials Engineering, Esentepe Campus, 54187, Sakarya (Turkey)

    2012-03-01

    In the present work, a nickel sulfate bath containing SiC submicron particles between 100 and 1000 nm was used as the plating electrolyte. The aim of this work is to obtain Ni-SiC metal matrix composites (MMCs) reinforced with submicron particles on steel surfaces with high hardness and wear resistance for using in anti-wear applications such as dies, tools and working parts for automobiles and vehicles. The influence of the SiC content in the electrolyte on particle distribution, microhardness and wear resistance of nano-composite coatings was studied. During the electroplating process, the proper stirring speed was also determined for sub-micron SiC deposition with Ni matrix. The Ni films were characterized by scanning electron microscopy (SEM) and X-ray diffraction (XRD) analysis. The depositions were controlled to obtain a specific thickness (between 50 and 200 {mu}m) and volume fraction of the particles in the matrix (between 0.02 and 0.10). The hardness of the coatings was measured to be 280-571 HV depending on the particle volume in the Ni matrix. The tribological behaviors of the electrodeposited SiC nanocomposite coatings sliding against an M50 steel ball (O 10 mm) were examined on a tribometer. All the friction and wear tests were performed without lubrication at room temperature and in the ambient air (with a relative humidity of 55-65%). The results showed that the wear resistance of the nanocomposites was approximately 2-2.2 times more than those of unreinforced Ni.

  15. Processing and mechanical properties of short fibers/Si{sub 3}N{sub 4p} reinforced BaO.Al{sub 2}O{sub 3}.2SiO{sub 2} ceramic matrix composites

    Energy Technology Data Exchange (ETDEWEB)

    Ma Jingmei [School of Materials Science and Engineering, Harbin Institute of Technology, Harbin 150001 (China); Ye Feng, E-mail: yf306@hit.edu.cn [School of Materials Science and Engineering, Harbin Institute of Technology, Harbin 150001 (China); Liu Limeng; Zhang Haijiao [School of Materials Science and Engineering, Harbin Institute of Technology, Harbin 150001 (China)

    2009-09-15

    Dense short silicon carbide (SiC{sub sf}) and carbon fibers (C{sub sf}) reinforced BaAl{sub 2}Si{sub 2}O{sub 8} (BAS) glass-ceramic composites with silicon nitride were fabricated by hot-pressing technique. The phase characterization, microstructure, mechanical properties and fracture behavior of the composites were investigated by X-ray diffraction, scanning electron microscopy, transmission electron microscopy and three-point bending tests. The results showed that short silicon carbide and carbon fibers disperse homogeneously in BAS matrix, and had good chemical compatibility with the glass-ceramic matrix. The addition of Si{sub 3}N{sub 4} could successfully eliminate the microcracks in the BAS matrix induced by the thermal mismatch between the fiber and matrix. Both the added short fibers could effectively reinforce the BAS glass-ceramic by the associated toughening mechanisms such as crack deflection, fiber bridging and pullout effects.

  16. Reinforcing effect of plasma modified halloysite nanotubes in a carbon black filled natural rubber-butadien rubber matrix

    OpenAIRE

    Poikelispaa, Minna; Das, Amit; Dierkes, Wilma; Vuorinen, Jyrki

    2011-01-01

    Rubber composites are generally produced by the direct incorporation of fillers like carbon black and/or silica into the rubber matrix. The incorporation of different types of nanofillers is the subject of recent research with the aim of preparing composites with special compositions and properties. A successful application of such composites depends mainly on the degree of dispersion of the nano-sized fillers. Recently, a naturally occurring clay mineral, halloysite nanotubes (HNTs), is inve...

  17. Study of the Effect of Process Parameters on Mechanical Properties and Microstructure of Al-Cu and SiCp Reinforced Metal Matrix Composite

    Directory of Open Access Journals (Sweden)

    SERAJUL HAQUE

    2012-12-01

    Full Text Available The high cost of fabrication hindered the actual application of metal matrix composite (MMC despite of their high stiffness, strength, corrosion resistance, wear resistance, non-reactivity with chemicals and so many other tailored quality which are never obtained in alloy of metals. In this study, a modest attempt has been made to find out the process parameters at which best mechanical properties of Al6061, 4%Cu and reinforced 5% SiCp ceramic MMC can be obtained. Addition of 4% Cu in Al6061 is more or less comparable to the composition of duralumin, which is widely used in aerospace applications. SiCp is hard and having linear thermal expansion at high temperature. With reinforcement of SiCp in Al-Cu alloy, it can be postulated thathardness of MMC retains at high temperature applications. An analysis of Variance (ANOVA was used for analysis of data with the help of SPSS (Version-17.0 software. Independent parameters are three levels of pouring rates (1.5cm/s, 2.5 cm/s and 3.5 cm/s, material type (Al6061+4%Cu alloy and Al+4%Cu, reinforced 5%SiCp MMC processed using stir casting technique and dependent parameters are hardness and impact strength, which is found that at different pouring rates material hardness and impact strength are highly significant. At pouring rate of 2.5 cm/s and 700±5°C pouring temperature, optimum values of hardness and impact strength are observed as compared to other values of pouring rates (1.5 cm/s and 3.5 cm/s. With reinforcement of 5% SiC trend of mechanical properties is same, buthardness and impact strength of MMCs are increased by 25% and 20% respectively. Also it is observed from scanning electron microscopy (SEM that at pouring rate 2.5 cm/s a better homogeneity can be obtained.

  18. Cure Cycle Design Methodology for Fabricating Reactive Resin Matrix Fiber Reinforced Composites: A Protocol for Producing Void-free Quality Laminates

    Science.gov (United States)

    Hou, Tan-Hung

    2014-01-01

    For the fabrication of resin matrix fiber reinforced composite laminates, a workable cure cycle (i.e., temperature and pressure profiles as a function of processing time) is needed and is critical for achieving void-free laminate consolidation. Design of such a cure cycle is not trivial, especially when dealing with reactive matrix resins. An empirical "trial and error" approach has been used as common practice in the composite industry. Such an approach is not only costly, but also ineffective at establishing the optimal processing conditions for a specific resin/fiber composite system. In this report, a rational "processing science" based approach is established, and a universal cure cycle design protocol is proposed. Following this protocol, a workable and optimal cure cycle can be readily and rationally designed for most reactive resin systems in a cost effective way. This design protocol has been validated through experimental studies of several reactive polyimide composites for a wide spectrum of usage that has been documented in the previous publications.

  19. Use of the Materials Genome Initiative (MGI approach in the design of improved-performance fiber-reinforced SiC/SiC ceramic-matrix composites (CMCs

    Directory of Open Access Journals (Sweden)

    Jennifer S. Snipes

    2016-07-01

    Full Text Available New materials are traditionally developed using costly and time-consuming trial-and-error experimental efforts. This is followed by an even lengthier material-certification process. Consequently, it takes 10 to 20 years before a newly-discovered material is commercially employed. An alternative approach to the development of new materials is the so-called materials-by-design approach within which a material is treated as a complex hierarchical system, and its design and optimization is carried out by employing computer-aided engineering analyses, predictive tools and available material databases. In the present work, the materials-by-design approach is utilized to design a grade of fiber-reinforced (FR SiC/SiC ceramic matrix composites (CMCs, the type of materials which are currently being used in stationary components, and are considered for use in rotating components, of the hot sections of gas-turbine engines. Towards that end, a number of mathematical functions and numerical models are developed which relate CMC constituents’ (fibers, fiber coating and matrix microstructure and their properties to the properties and performance of the CMC as a whole. To validate the newly-developed materials-by-design approach, comparisons are made between experimentally measured and computationally predicted selected CMC mechanical properties. Then an optimization procedure is employed to determine the chemical makeup and processing routes for the CMC constituents so that the selected mechanical properties of the CMCs are increased to a preset target level.

  20. Characterisation of titanium-titanium boride composites processed by powder metallurgy techniques

    Energy Technology Data Exchange (ETDEWEB)

    Selva Kumar, M., E-mail: sel_mcet@yahoo.co.in [Department of Mechanical Engineering, Dr. Mahalingam College of Engineering and Technology, Pollachi-642003 (India); Chandrasekar, P.; Chandramohan, P. [School of Engineering, Professional Group of Institutions, Coimbatore-641662 (India); Mohanraj, M. [Department of Mechanical Engineering, Info Institute of Engineering, Coimbatore-641107 (India)

    2012-11-15

    In this work, a detailed characterisation of titanium-titanium boride composites processed by three powder metallurgy techniques, namely, hot isostatic pressing, spark plasma sintering and vacuum sintering, was conducted. Two composites with different volume percents of titanium boride reinforcement were used for the investigation. One was titanium with 20% titanium boride, and the other was titanium with 40% titanium boride (by volume). Characterisation was performed using X-ray diffraction, electron probe micro analysis - energy dispersive spectroscopy and wavelength dispersive spectroscopy, image analysis and scanning electron microscopy. The characterisation results confirm the completion of the titanium boride reaction. The results reveal the presence of titanium boride reinforcement in different morphologies such as needle-shaped whiskers, short agglomerated whiskers and fine plates. The paper also discusses how mechanical properties such as microhardness, elastic modulus and Poisson's ratio are influenced by the processing techniques as well as the volume fraction of the titanium boride reinforcement. - Highlights: Black-Right-Pointing-Pointer Ti-TiB composites were processed by HIP, SPS and vacuum sintering. Black-Right-Pointing-Pointer The completion of Ti-TiB{sub 2} reaction was confirmed by XRD, SEM and EPMA studies. Black-Right-Pointing-Pointer Hardness and elastic properties of Ti-TiB composites were discussed. Black-Right-Pointing-Pointer Processing techniques were compared with respect to their microstructure.

  1. A Simple Model to Estimate the Yield Strength of Silicon Carbide Particulate Reinforced Aluminium Alloy Matrix Composites

    Institute of Scientific and Technical Information of China (English)

    2002-01-01

    In the present study, a modified Hall-Petch correlation on the basis of dislocation pile-up model was used to estimate the yield strength of SiCp/Al composites. The experimental results show that the modified Hall-Petch correlation expressed as σcy=244+371λ-1/2 fits very well with the experimental data, which indicated that the strength increase of SiCp/Al composites might be due to the direct blocking of dislocation motion by the particulate-matrix interface,namely, the dislocation pile-up is the most possible strengthening mechanism for SiCp/Al composites.

  2. Tribocorrosion studies in centrifugally cast Al-matrix SiC{sub p}-reinforced functionally graded composites

    Energy Technology Data Exchange (ETDEWEB)

    Velhinho, A. [CENIMAT - Materials Research Centre, FCTUNL, Caparica (Portugal); DCM - Materials Science Dept., FCTUNL, Caparica (Portugal); Botas, J.D. [DCM - Materials Science Dept., FCTUNL, Caparica (Portugal); Ariza, E. [CIICS - Research Centre on Interfaces and Surfaces Performance, Univ. of Minho, Guimaraes (Portugal); Gomes, J.R.; Rocha, L.A. [CIICS - Research Centre on Interfaces and Surfaces Performance, Univ. of Minho, Guimaraes (Portugal); DEM - Mechanical Engineering Dept., Univ. of Minho, Guimaraes (Portugal)

    2004-07-01

    The present work reports results obtained from a series of preliminary experiments aiming at complementing the current knowledge about the wear behaviour of centrifugally-cast FGM Al/SiCp composites, through concurrent corrosion processes. Precursor MMC's were prepared by rheocasting, using 118.8 {mu}m SiC particles and an Al-10Si-2.2 Mg alloy. Those MMC's were then molten and centrifugally cast in order to produce cylindrical FGMMC's. Discs machined from the top surface of each sample were tested against nodular cast iron pins, using an inverted configuration pin-on-disc tribometer. Sliding tests took place at room temperature, over a 50000 m sliding distance, with a sliding speed of 0.3 m s{sup -1}, under a 5 N normal load; both dry-sliding and water-lubricated tests were performed. In order to elucidate the mechanisms involved, the wear coefficients were calculated for each condition, and the samples were subjected to morphological characterization via SEM/EDS. Concurrently, in the case of the water-lubrication tests, the corrosion potential of the tribological pair was monitored. The results obtained show an increase in material loss for the water-lubricated cases, although variations are registered depending on reinforcing particle volume fraction. At the same time, the open circuit potential response of the tribological pair may be correlated with the events of formation/destruction of the tribolayers. (orig.)

  3. Design, preparation and microwave absorbing properties of resin matrix composites reinforced by SiC fibers with different electrical properties

    Energy Technology Data Exchange (ETDEWEB)

    Liu, Haitao, E-mail: xzddlht@163.com [Science and Technology on Advanced Ceramic Fibers and Composites Laboratory, College of Aerospace Science and Engineering, National University of Defense Technology, Changsha 410073 (China); Science and Technology on Scramjet Laboratory, College of Aerospace Science and Engineering, National University of Defense Technology, Changsha 410073 (China); Cheng, Haifeng; Tian, Hao [Science and Technology on Advanced Ceramic Fibers and Composites Laboratory, College of Aerospace Science and Engineering, National University of Defense Technology, Changsha 410073 (China)

    2014-01-15

    Highlights: • SSMASs have better microwave absorbing properties in smaller thickness. • SSMASs can be realized by SiC fibers with different electrical resistivity. • Resistivity of SiC fibers can be regulated by adjusting surface characteristics. • The bandwidth of SSMASs at reflectivity below −10 dB can reach 11.6 GHz. -- Abstract: One kind of sandwich structure microwave absorbing structures (SSMASs) derived from Salisbury absorbers is reported. The impedance characteristics of SSMASs are analyzed, and the mechanisms of broadening microwave absorbing bandwidth are interpreted by Smith chart. In order to realize SSMASs, high electrical resistivity SiC fibers with Si–C–O surface layers and low electrical resistivity SiC fibers with pyrocarbon surface layers are employed and analyzed by SEM, XPS, AES and HRTEM. The conductive model of SiC fibers with pyrocarbon layers is built and electrical resistivity simulation is done. The SSMASs are fabricated by employing plain woven SiC fiber fabrics with high and low electrical resistivity as reinforcements of dielectric layers and lossy layer, respectively. The microwave absorbing properties of SSMASs are measured and compared with simulated results. The results show that the experimental and simulated results are in good agreement, the SSMASs have better wideband microwave absorbing properties, and the microwave absorbing bandwidth at reflectivity below −10 dB can reach 11.6 GHz.

  4. Effects of trace TiB and TiC on microstructure and tensile properties of β titanium alloy

    Energy Technology Data Exchange (ETDEWEB)

    Du, Z.X.; Xiao, S.L., E-mail: xiaoshulong@hit.edu.cn; Wang, P.X.; Xu, L.J.; Chen, Y.Y.; Rahoma, H.K.S.

    2014-02-24

    In the present work, a β titanium alloy reinforced by trace TiB whiskers and TiC particles was fabricated by common casting and hot-forging. For comparative study, the unreinforced titanium matrix alloy was also fabricated by the same casting and forging process. The microstructure, room temperature, tensile properties and fracture characteristics of the composite and the matrix alloy are presented and discussed. Microstructural analysis of the composite revealed that the reinforcements were uniformly dispersed after forging. The size of the β grains in the composite was refined after solution treatment under the β field. The secondary α lath was also refined during aging heat treatment by the addition of trace boron and carbon. The results of the tensile tests show that the improvement in the strength of the composite can be attributed to the refinement in the grain size and the secondary α lath, while the remarkable reduction in the ductility can be ascribed to the cracking of the reinforcements and the decohesion at the interface between the reinforcements and the matrix.

  5. Carbon Nanotubes Reinforced Composites for Biomedical Applications

    Directory of Open Access Journals (Sweden)

    Wei Wang

    2014-01-01

    Full Text Available This review paper reported carbon nanotubes reinforced composites for biomedical applications. Several studies have found enhancement in the mechanical properties of CNTs-based reinforced composites by the addition of CNTs. CNTs reinforced composites have been intensively investigated for many aspects of life, especially being made for biomedical applications. The review introduced fabrication of CNTs reinforced composites (CNTs reinforced metal matrix composites, CNTs reinforced polymer matrix composites, and CNTs reinforced ceramic matrix composites, their mechanical properties, cell experiments in vitro, and biocompatibility tests in vivo.

  6. Carbon nanotubes reinforced composites for biomedical applications.

    Science.gov (United States)

    Wang, Wei; Zhu, Yuhe; Liao, Susan; Li, Jiajia

    2014-01-01

    This review paper reported carbon nanotubes reinforced composites for biomedical applications. Several studies have found enhancement in the mechanical properties of CNTs-based reinforced composites by the addition of CNTs. CNTs reinforced composites have been intensively investigated for many aspects of life, especially being made for biomedical applications. The review introduced fabrication of CNTs reinforced composites (CNTs reinforced metal matrix composites, CNTs reinforced polymer matrix composites, and CNTs reinforced ceramic matrix composites), their mechanical properties, cell experiments in vitro, and biocompatibility tests in vivo.

  7. Fabrication and densification enhancement of SiC-particulate-reinforced copper matrix composites prepared via the sinter-forging process

    Institute of Scientific and Technical Information of China (English)

    Mohammadmehdi Shabani; Mohammad Hossein Paydar; Mohammad Mohsen Moshksar

    2014-01-01

    The fabrication of copper (Cu) and copper matrix silicon carbide (Cu/SiCp) particulate composites via the sinter-forging process was investigated. Sintering and sinter-forging processes were performed under an inert Ar atmosphere. The influence of sinter-forging time, tempera-ture, and compressive stress on the relative density and hardness of the prepared samples was systematically investigated and subsequently com-pared with that of the samples prepared by the conventional sintering process. The relative density and hardness of the composites were enhanced when they were prepared by the sinter-forging process. The relative density values of all Cu/SiCp composite samples were observed to decrease with the increase in SiC content.

  8. Microstructure of arc brazed and diffusion bonded joints of stainless steel and SiC reinforced aluminum matrix composite

    Science.gov (United States)

    Elßner, M.; Weis, S.; Grund, T.; Wagner, G.; Habisch, S.; Mayr, P.

    2016-03-01

    Joint interfaces of aluminum and stainless steel often exhibit intermetallics of Al-Fe, which limit the joint strength. In order to reduce these brittle phases in joints of aluminum matrix composites (AMC) and stainless steel, diffusion bonding and arc brazing are used. Due to the absence of a liquid phase, diffusion welding can reduce the formation of these critical in- termetallics. For this joining technique, the influence of surface treatments and adjusted time- temperature-surface-pressure-regimes is investigated. On the other hand, arc brazing offers the advantage to combine a localized heat input with the application of a low melting filler and was conducted using the system Al-Ag-Cu. Results of the joining tests using both approaches are described and discussed with regard to the microstructure of the joints and the interfaces.

  9. Utilization of chemically treated municipal solid waste (spent coffee bean powder) as reinforcement in cellulose matrix for packaging applications.

    Science.gov (United States)

    Thiagamani, Senthil Muthu Kumar; Nagarajan, Rajini; Jawaid, Mohammad; Anumakonda, Varadarajulu; Siengchin, Suchart

    2017-07-31

    As the annual production of the solid waste generable in the form of spent coffee bean powder (SCBP) is over 6 million tons, its utilization in the generation of green energy, waste water treatment and as a filler in biocomposites is desirable. The objective of this article is to analyze the possibilities to valorize coffee bean powder as a filler in cellulose matrix. Cellulose matrix was dissolved in the relatively safer aqueous solution mixture (8% LiOH and 15% Urea) precooled to -12.5°C. To the cellulose solution (SCBP) was added in 5-25wt% and the composite films were prepared by regeneration method using ethyl alcohol as a coagulant. Some SCBP was treated with aq. 5% NaOH and the composite films were also prepared using alkali treated SCBP as a filler. The films of composites were uniform with brown in color. The cellulose/SCBP films without and with alkali treated SCBP were characterized by FTIR, XRD, optical and polarized optical microscopy, thermogravimetric analysis (TGA) and tensile tests. The maximum tensile strength of the composite films with alkali treated SCBP varied between (106-149MPa) and increased with SCBP content when compared to the composites with untreated SCBP. The thermal stability of the composite was higher at elevated temperatures when alkali treated SCBP was used. Based on the improved tensile properties and photo resistivity, the cellulose/SCBP composite films with alkali treated SCBP may be considered for packaging and wrapping of flowers and vegetables. Copyright © 2017 Elsevier Ltd. All rights reserved.

  10. Thermal, structural and morphological properties of High Density Polyethylene matrix composites reinforced with submicron agro silica particles and Titania particles

    Directory of Open Access Journals (Sweden)

    Oluyemi O. Daramola

    2017-07-01

    Full Text Available HDPE—based composites samples filled with 2, 4, 6, 8 and 10 wt.% submicron agro-waste silica particles extracted from rice husk ash (RHA at constant 0.3 wt.% Titania loading were prepared using rapra single screw extruder at temperature of 200–230 °C. The extrudates were compressed with a laboratory carver press at a temperature of 230 °C for 10 min under applied pressure of 0.2 kPa and water cooled at 20 °C min−1. Thermal, structural and morphological properties of the composites were studied. The results of the thermogravimetric analysis (TGA revealed that the composites with 10 wt.% SiO2 have the best maximum thermal degradation temperature of 438.73 °C. The crystal structure of neat HDPE, and the siliceous composites developed revealed two obvious diffractive peaks of about 21.3° and 23.7° corresponding to typical crystal plane (1 1 0 and (2 0 0 of orthorhombic phase respectively. The diffractive peaks do not shift with the addition of silica particles; this clearly indicates that the addition of silica particles did not exert much effect on the crystalline structure of HDPE. There is no much difference in the interplanar distance (d-value. Lamellar thickness (L of HDPE increases with the addition of silica particles, which implies that silica particles aid the formation of more perfect crystals. Scanning electron microscopy studies indicated that there were chains inter diffusion and entanglement between HDPE matrix and the silica particles at lower weight fraction (2–4 wt.% of submicron silica particles which resulted into homogeneous dispersion of the particles within the matrix.

  11. Obtention and dynamical mechanical behavior of polymer matrix carbon fire reinforced composites; Obtencao e comportamento mecanodinamico de compositos com matriz polimerica reforcada com fibras de carbono

    Energy Technology Data Exchange (ETDEWEB)

    Da Silva, Nelson Marques

    2001-07-01

    Polymer matrix composites reinforced with carbon fibres have been extensively used in the nuclear, aeronautics, automotive and leisure industry. This is due to their superior performance when compared to conventional materials in terms of specific strength and specific modulus (3 to 4 times higher than that of mild steels). However, these materials are anisotropic, requiring characterisation for each process and particular application. In the present work, the evaluation of epoxy resin reinforced with unidirectional and continuous carbon fibres was carried out. The composites materials were obtained by filament winding, with three different cure cycles, with two types of carbon fibres (6000 and 12000 filaments per strand) and with fibres volumetric fraction around 60 %. The evaluation of the composites was undertaken using following techniques: scanning electron microscopy (SEM); dynamic mechanical analysis (DMA); thermogravimetric analysis (TGA), and differential scanning calorimeter (DSC). These techniques allowed the evaluation and comparison of storage modulus, internal energy dissipation, glass transition region and glass transition temperature - Tg, cure cycling. Besides, void volumetric fraction was measured. The results indicate that the DMA is a good alternative technique to DSC and TGA. It provides an indication of the quality of the produced composite, both thermal and mechanical. The technique can assist the quality control of composite components by measuring mechanical and thermal properties - modulus and Tg. The DMA technique was sensitive to cure cycling evaluation. Regarding the obtained composites, the results showed the need for the development of specific cure cycle for each application, establishing a compromise between properties such as storage modulus and internal energy dissipation, and involved costs. The results demonstrated differences between the storage modulus and internal energy dissipation for the two types of used fibres. (author)

  12. Effect of Spark-Plasma-Sintering Conditions on Tensile Properties of Aluminum Matrix Composites Reinforced with Multiwalled Carbon Nanotubes (MWCNTs)

    Science.gov (United States)

    Chen, B.; Imai, H.; Umeda, J.; Takahashi, M.; Kondoh, K.

    2017-02-01

    In this study, aluminum (Al) matrix composites containing 2 wt.% multiwalled carbon nanotubes (CNTs) were fabricated by powder metallurgy using high-energy ball milling (HEBM), spark plasma sintering (SPS), and subsequent hot extrusion. The effect of SPS conditions on the tensile properties of CNT/Al composites was investigated. The results showed that composites with well-dispersed CNTs and nearly full-density CNT/Al can be obtained. During HEBM, CNTs were shortened, inserted into welded Al powder particles, bonded to Al, and still stable without CNT-Al reaction. After consolidation, Al4C3 phases formed in composites under different sintering conditions. With the increase of sintering temperature and holding time, the strength decreased. Conversely, the ductility and toughness noticeably increased. As a result, a good balance between strength (367 MPa in ultimate tensile strength) and ductility (13% in elongation) was achieved in the as-extruded CNT/Al composite sintered at 630°C with a holding time of 300 min.

  13. Al2O3-Coated Nano-SiC Particles Reinforced Al2O3 Matrix Composites

    Institute of Scientific and Technical Information of China (English)

    2002-01-01

    Properties of Al2O3-coated nano-SiC have been compared with those of as-received SiC. The isoelectric point (IEP)of SiC changed from pH3.4 to pH7.3 after coating with the alumina precursor, which is close to that of alumina.Because both surfaces of coated SiC and Al2O3 possess higher positive charge at pH=4.5~5.0, they are uniformly dispersed in the two-phase aqueous suspensions, Then a mixed powder containing nano-SiC dispersed homogeneously into the Al2O3 matrix was achieved from flocculating the two-phase suspension. Finally, Al2O3/SiC nanocomposites were obtained by coating nano-SiC with Al2O3, in which the majority of SiC particles were located within the Al2O3 grains. The observation by transmission electron microscopy (TEM) and the analysis by the X-ray photoelectron spectroscopy (XPS) showed that cracks propagated towards the intragranular SiC rather than along grain boundaries.

  14. Method Developed for the High-Temperature Nondestructive Evaluation of Fiber-Reinforced Silicon Carbide Ceramic Matrix Composites

    Science.gov (United States)

    Goldsby, Jon C.

    1998-01-01

    Ceramic matrix composites have emerged as candidate materials to allow higher operating temperatures (1000 to 1400 C) in gas turbine engines. A need, therefore, exists to develop nondestructive methods to evaluate material integrity at the material operating temperature by monitoring thermal and mechanical fatigue. These methods would also have potential as quality inspection tools. The goal of this investigation at the NASA Lewis Research Center is to survey and correlate the temperature-dependent damping and stiffness of advanced ceramic composite materials with imposed thermal and stress histories that simulate in-service turbine engine conditions. A typical sample size of 100 by 4 by 2 cubic millimeters, along with the specified stiffness and density, placed the fundamental vibration frequencies between 100 and 2000 Hz. A modified Forster apparatus seemed most applicable to simultaneously measure both damping and stiffness. Testing in vacuum reduced the effects of air on the measurements. In this method, a single composite sample is vibrated at its fundamental tone; then suddenly, the mechanical excitation is removed so that the sample's motion freely decays with time. Typical results are illlustrated in this paper.

  15. Effects of Fiber Reinforcement Architecture on the Hygrothermal-Mechanical Performance of Polyimide Matrix Composites for Aeropropulsion Applications

    Science.gov (United States)

    Shin, E. Eugene; Thesken, John C.; Sutter, James K.; Chuang, Kathy; Juhas, John; Veverka, Adrienne; Inghram, Linda; Papadopoulos, Demetrios; Burke, Chris; Scheiman, Dan

    2003-01-01

    A lightweight sandwich support structure, for the combustor chamber of a new generation liquid propellant rocket engine, was designed and fabricated using a polymer matrix composite (PMC) facesheet on a Ti honeycomb core. The PMC facesheet consisted of high stiffness carbon fiber, M40JB, and high temperature Polyimides, such as PMR-II-50 and HFPE-II-52. Six different fiber architectures; four harness satin (4HS) woven fabric, uni-tape, woven-uni hybrid, stitched woven fabric, stitched uni-tape and triaxial braided structures have been investigated for optimum stiffness-thickness-weight-hygrothermal performance design criteria for the hygrothermal-mechanical propulsion service exposure conditions including rapid heating up to 200 F/sec, maximum operating temperature of 600 F, internal pressure up to 100 psi. One of the specific objectives in this study is to improve composite blistering resistance in z-direction at minimum expense of in-plane mechanical properties. An extensive property-performance database including dry-wet mechanical properties at various temperatures, thermal-physical properties, such as blistering onset condition was generated for fiber architecture down-selection and design guidelines. Various optimized process methods such as vacuum bag compression molding, solvent assistant resin transfer molding (SaRTM), resin film infusion (RFI) and autoclaving were utilized for PMC panel fabrication depending on the architecture type. In the case of stitched woven fabric architecture, the stitch pattern in terms of stitch density and yarn size was optimized based on both in-plane mechanical properties and blistering performance. Potential reduction of the in-plane properties transverse to the line of stitching was also evaluated. Efforts have been made to correlate the experimental results with theoretical micro-mechanics predictions. Changes in deformation mechanism and failure sequences in terms of fiber architecture will be discussed.

  16. Electrowinning molten titanium from titanium dioxide

    CSIR Research Space (South Africa)

    Van Vuuren, DS

    2005-10-01

    Full Text Available ; the high affinity of titanium for carbon, oxygen, and nitrogen; and physical and chemical properties of the different titanium oxide species when reducing titanium from Ti4+ to metallic titanium....

  17. Carbon Fiber with Ni-coating Reinforced Aluminum Matrix Composites%电镀镍碳纤维增强铝基复合材料

    Institute of Scientific and Technical Information of China (English)

    韩变华; 罗天骄; 梁春林; 姚广春; 刘宜汉

    2006-01-01

    提出一种碳纤维表面电镀镍的方法,通过正交实验优化了电镀镍配方及工艺条件,并研究了镀层的显微组织及镀液的成分、电流密度、电镀时间等工艺条件对沉镍速率和镀层质量的影响,并探讨了沉镍机理.用镀镍碳纤维制备铝基复合材料,观测碳纤维与铝的复合效果.%This paper introduces the process of electroplating with nickel on carbon fiber, and the technical conditions of nickel plating are obtained by orthogonal experiment. Microscopic structure of nickel coating and the effect of nickel plating rate and coating structure with the solution composition, current density and electroplating time are studied. The principle of nickel plating is also researched. The aluminum matrix composites is reinforced by carbon fiber with nickel coating, and the compound effect between aluminum and carbon fiber is observed.

  18. Research and Development of Some Advanced High Temperature Titanium Alloys for Aero-engine

    Directory of Open Access Journals (Sweden)

    CAI Jian-ming

    2016-08-01

    Full Text Available Some advanced high temperature titanium alloys are usually selected to be manufactured into blade, disc, case, blisk and bling under high temperature environment in compressor and turbine system of a new generation high thrust-mass ratio aero-engine. The latest research progress of 600℃ high temperature titanium alloy, fireproof titanium alloy, TiAl alloy, continuous SiC fiber reinforced titanium matrix composite and their application technology in recent years in China were reviewed in this paper. The key technologies need to be broken through in design, processing and application of new material and component are put forward, including industrial ingot composition of high purified and homogeneous control technology, preparation technology of the large size bar and special forgings, machining technology of blisk and bling parts, material property evaluation and application design technique. The future with the continuous application of advanced high temperature titanium alloys, will be a strong impetus to the development of China's aero-engine technology.

  19. Carbon Nanotubes Reinforced Composites for Biomedical Applications

    OpenAIRE

    Wei Wang; Yuhe Zhu; Susan Liao; Jiajia Li

    2014-01-01

    This review paper reported carbon nanotubes reinforced composites for biomedical applications. Several studies have found enhancement in the mechanical properties of CNTs-based reinforced composites by the addition of CNTs. CNTs reinforced composites have been intensively investigated for many aspects of life, especially being made for biomedical applications. The review introduced fabrication of CNTs reinforced composites (CNTs reinforced metal matrix composites, CNTs reinforced polymer matr...

  20. Effects of the Exposure to Corrosive Salts on the Frictional Behavior of Gray Cast Iron and a Titanium-Based Metal Matrix Composite

    Energy Technology Data Exchange (ETDEWEB)

    Blau, Peter Julian [ORNL; Truhan, Jr., John J [ORNL; Kenik, Edward A [ORNL

    2007-01-01

    The introduction of increasingly aggressive road-deicing chemicals has created significant and costly corrosion problems for the trucking industry. From a tribological perspective, corrosion of the sliding surfaces of brakes after exposure to road salts can create oxide scales on the surfaces that affect friction. This paper describes experiments on the effects of exposure to sodium chloride and magnesium chloride sprays on the transient frictional behavior of cast iron and a titanium-based composite sliding against a commercial brake lining material. Corrosion scales on cast iron initially act as abrasive third-bodies, then they become crushed, spread out, and behave as a solid lubricant. The composition and subsurface microstructures of the corrosion products on the cast iron were analyzed. Owing to its greater corrosion resistance, the titanium composite remained scale-free and its frictional response was markedly different. No corrosion scales were formed on the titanium composite after aggressive exposure to salts; however, a reduction in friction was still observed. Unlike the crystalline sodium chloride deposits that tended to remain dry, hygroscopic magnesium chloride deposits absorbed ambient moisture from the air, liquefied, and retained a persistent lubricating effect on the titanium surfaces.

  1. Cellular fiber–reinforced concrete

    OpenAIRE

    Isachenko S.; Kodzoev M.

    2016-01-01

    Methods disperse reinforcement of concrete matrix using polypropylene, glass, basalt and metal fibers allows to make the construction of complex configuration, solve the problem of frost products. Dispersed reinforcement reduces the overall weight of the structures. The fiber replaces the secondary reinforcement, reducing the volume of use of structural steel reinforcement. Cellular Fiber concretes are characterized by high-performance properties, especially increased bending strength and...

  2. Dry sliding wear of heat treated hybrid metal matrix composites

    Science.gov (United States)

    Naveed, Mohammed; Khan, A. R. Anwar

    2016-09-01

    In recent years, there has been an ever-increasing demand for enhancing mechanical properties of Aluminum Matrix Composites (AMCs), which are finding wide applications in the field of aerospace, automobile, defence etc,. Among all available aluminium alloys, Al6061 is extensively used owing to its excellent wear resistance and ease of processing. Newer techniques of improving the hardness and wear resistance of Al6061 by dispersing an appropriate mixture of hard ceramic powder and whiskers in the aluminium alloy are gaining popularity. The conventional aluminium based composites possess only one type of reinforcements. Addition of hard reinforcements such as silicon carbide, alumina, titanium carbide, improves hardness, strength and wear resistance of the composites. However, these composites possessing hard reinforcement do posses several problems during their machining operation. AMCs reinforced with particles of Gr have been reported to be possessing better wear characteristics owing to the reduced wear because of formation of a thin layer of Gr particles, which prevents metal to metal contact of the sliding surfaces. Further, heat treatment has a profound influence on mechanical properties of heat treatable aluminium alloys and its composites. For a solutionising temperature of 5500C, solutionising duration of 1hr, ageing temperature of 1750C, quenching media and ageing duration significantly alters mechanical properties of both aluminium alloy and its composites. In the light of the above, the present paper aims at developing aluminium based hybrid metal matrix composites containing both silicon carbide and graphite and characterize their mechanical properties by subjecting it to heat treatment. Results indicate that increase of graphite content increases wear resistance of hybrid composites reinforced with constant SiC reinforcement. Further heat treatment has a profound influence on the wear resistance of the matrix alloy as well as its hybrid composites

  3. Microstructure and Microhardness of TiC Particles Reinforced Coating In-situ Deposited on Titanium Alloy Surface by Electrospark Process%钛合金表面电火花原位沉积TiC颗粒强化层的组织与硬度

    Institute of Scientific and Technical Information of China (English)

    王忠英; 庞永平; 王坤

    2012-01-01

    以石墨为电极,采用电火花沉积工艺在BT20钛合金表面沉积了TiC颗粒得到了强化层,并对该强化层的组织和硬度进行了研究。结果表明:强化层分布不连续,厚度也不均匀,最厚处可达30μm,最薄处还不到10μm;强化层中TiC颗粒的分布不均匀,大量TiC聚集于强化层表面,内部很少,这使得强化层表面硬度达到了基体的5倍以上。%Taking the graphite as electrode, TiC particles were deposited on BT20 titanium alloy surface by eletrospark processing to form a reinforced coating. The mierostructure and microhardness of the coating were studied. The results show that the coating was discontinuous and uneven with the thickness of 10--30μa. The distribution of TiC particles in the reinforced coating was non-uniform, most of TiC existed on the reinforced coating surface and a little inside of the reinforced coating, which made the microhardness of the reinforced coating 4 times higher than that of the titanium alloy substrate.

  4. Synthesis, microstructural and mechanical properties of ex situ zircon particles (ZrSiO4 reinforced Metal Matrix Composites (MMCs: a review

    Directory of Open Access Journals (Sweden)

    Satish Kumar Thandalam

    2015-07-01

    This review article details the current development on the synthesis, microstructure and mechanical properties of zircon reinforced MMCs, with specific attention on the abrasive wear behavior of the composites. This review also summarizes the work done by various research groups on zircon reinforced MMCs in achieving higher hardness and wear resistance in these composites.

  5. Piezoresistivity of carbon fiber reinforced cement-matrix composites%碳纤维增强水泥基复合材料的压阻效应

    Institute of Scientific and Technical Information of China (English)

    赵晓华; 李国宝; 王玉林; 李庚英

    2011-01-01

    The piezoresistivity of short carbon fiber reinforced cement-matrix composites(CFRC) was experimentally studied.The whole process of transition from positive to negative piezoresistivity was observed.The results show that under continuously drying and uniaxially cyclic loading,both positive and negative piezoresistivity occur in CFRC due to the variation of moisture content in the composites.For most cases the electrical resistivity of the composites decreases monotonically upon longitudinal compression,and piezoresistivity tends to be positive.However,its magnitude varies.Lower moisture content leads to stronger piezoresistivity.When moisture content reduces to about 3.19%~4.04%,the electrical resistivity of the composites increases monotonically upon compressive strain,and piezoresistivity tends to be negative.This effect is much stronger than that of positive piezoresistivity.It is proposed that the occurrence of these phenomena is attributable to both the tunneling effect between fibers and decreasing in pore network connectivity during compression.%试验研究了短切碳纤维增强水泥基复合材料(CFRC)的压阻效应,获得了正、负两种压阻效应相互转换的全过程。从隧道效应和孔隙的连通性角度对该现象的产生机理进行了探讨。结果表明,在连续烘干和单向循环加载条件下,CFRC的压阻效应会随含水量变化而发生改变。多数情况下,CFRC的体积电阻率随压应变单调减少,压阻效应为正。含水量越少,正压阻效应越明显。当含水量减少到约3.19%~4.04%的范围时,CFRC的体积电阻率随压应变单调增加,压阻效应为负。与正压阻效应相比,负压阻效应表现更强。CFRC的正、负压阻效应及其相互转换是隧道效应和孔隙连通性两方面相互影响的必然结果。

  6. Polyester matrix composite reinforced by fiberglass: how far can have contact with oil; Composito de matriz poliester e reforco de fibra de vidro: ate onde pode ter contato com petroleo

    Energy Technology Data Exchange (ETDEWEB)

    Dantas, C.M.; Masieiro, F.R.S.; Felipe, R.C.T.S.; Felipe, R.N.B.; Medeiros, G.G. [Centro Federal de Educacao Tecnologica (CEFET), Natal, RN (Brazil)], e-mail: k1000_rn@hotmail.com

    2008-07-01

    The use of reinforced plastics (PR) in the petroleum industry is very incipient when compared to conventional materials such as steel, for example. PR are already being used in floorings and handrails, but still there is not studies about the behavior of these materials when they come into contact with oil. In this context, this work aims to obtain a composite using a matrix of polyester resin, and the fiberglass (E Glass) as material of reinforcement. After the obtention of the composite, proof bodies will be made for the determination of the mechanical properties related to the traction and bending. Some of these proof bodies will be immersed in oil for a period of 120 days. At the end of this period, they will be tested. Thus, the traction and bending of the proof bodies which was immersed will be compared to the other ones, seeking to verify the influence of this immersion on the mechanical properties of the material. (author)

  7. “IMPROVEMENT IN TRIBOLOGICAL PROPERTIES BY IMPROVING GEOMETRY OF REINFORCEMENT PARTICLES”

    Directory of Open Access Journals (Sweden)

    SHIVAJI V.GAWALI

    2011-12-01

    Full Text Available The volume fraction of the heavier Titanium Di-boride particles is controlled by inertial forces upon centrifugal force processing the semisolid composite. Titanium Di-boride particles are modeled as tetrahedron particles subject to a drag force in a Stoke flow. The equation of motion for the particles under the applied centrifugalforces is solved mathematically assuming a Gaussian diameter size distribution with a spatial uniform random distribution of particles in the sample. The effect of the geometry of the particles is also important. It is observed that the Penetration capability of reinforcement particles is dependent on the shape and the geometryof the particles. Drag force is kept at the minimum by adopting tetrahedron shape particles. It is possible to understand and control the experimental conditions to obtain an appropriate functionally-graded aluminum matrix by centrifugal casting for high wear resistance applications.

  8. Application Progress of AE in Fiber Reinforced Polymer Matrix Composites%声发射在纤维增强聚合物基复合材料中的应用进展

    Institute of Scientific and Technical Information of China (English)

    郭勇; 李大纲; 陈玉霞; 李晶晶; 杨莹; 方菲

    2013-01-01

    The recent progress in the research of application of Acoustic Emission(AE)technique to monitoring mechanical performance of fiber-reinforced polymer matrix composites was reviewed.AE technical principle in detecting polymer composites and its characteristics were analyzed,and then the applications of AE technique to analyzing damage and fracture progress of fiber reinforced polymer matrix composites with different fibers such as glass fiber,carbon fiber,plant fiber and other traditional fiber were summarized.Based on the current problems in the research of application of AE technique to monitoring mechanical performance of fiber-reinforced polymer matrix composites,its development trend was prospected.%综述了近年来声发射(AE)技术应用于监测纤维增强聚合物基复合材料力学性能的研究进展。分析了聚合物基复合材料AE技术检测原理及特性,并总结了AE技术在分析玻璃纤维、碳纤维、其他传统纤维以及植物纤维增强聚合物基复合材料损伤、断裂过程中的应用。结合AE技术在监测纤维增强聚合物基复合材料力学性能中存在的问题对其研究趋势进行了展望。

  9. Evolution of the internal friction in SIC particle reinforced 8090 Al-Li metal matrix composite; Evolucion de la friccion interna del material compuesto de matriz Al-Li 8090 reforzado con particulas de SiC

    Energy Technology Data Exchange (ETDEWEB)

    Gutierrez-Urrutia, I.; Gallego, I.; No, M. L.; San Juan, J. M.

    2001-07-01

    The present study has been undertaken to investigate the mechanisms of thermal stress relief at the range of temperatures below room temperature for the metal matrix composite Al-Li 8090/SiC. For this aim the experimental technique of internal friction has been used which has been showed up very effective. Several thermal cycles from 453 K to 100 K were used in order to measures the internal friction as well as the elastic modules of the material concluding that thermal stresses are relaxed by microplastic deformation around the reinforcements. It has been also related the variation in the elastic modules with the different levels of precipitation. (Author) 18 refs.

  10. Research on Processing Technology of Glass Fiber Reinforced Thermoplastic Resin Matrix Interlayer Composites%纤维增强热塑性树脂基夹层复合材料加工工艺研究

    Institute of Scientific and Technical Information of China (English)

    邹积洋; 孙开颜; 李军; 任万杰

    2015-01-01

    Glass fiber reinforced thermoplastic resin matrix interlayer composite which uses ethylene-vinyl acetate copolymer(EVAC) thermoplastic resin reinforced glass fiber as matrix material,and the alumina ceramicsas interlayer has the characteristics of high toughness in surface,high hardness and high brittleness in the interlayer. To meet the precision of machining process,the quality requirement of the product surface and the requirements of machining processing schedule at the same time, it is difficult to process all kinds of angles and holes. Aiming to solve the difficulties in the processing technology of the glass fiber reinforced thermoplastic resin matrix interlayer composites,the choice of machines,knife tools and the processing parameters, as well as the determination of process quality are researched. Meanwhile,the equipment specifications,blade diameter,the relationship between cutting speed and the thickness of the glass fiber reinforced thermoplastic resin matrix interlayer composite are all determined. The determination method of process quality is given by the section quality,size precision and the surface quality and other aspects.%采用玻纤增强乙烯–乙酸乙烯酯共聚物(EVAC)复合材料为基体材料,以氧化铝陶瓷为夹层材料,制备的纤维增强热塑性树脂基夹层复合材料具有表面韧性好,夹层硬度高、脆性大的特点,在同时满足纤维增强热塑性树脂基夹层复合材料加工精度、加工面质量和加工进度要求的条件下,各类角、孔的加工难度很大。针对此类复合材料的加工难点,从设备和刀具的选择、工艺参数的选定、工艺质量的判定等几个方面对复合材料的加工工艺进行了研究,确定了设备规格、刀具外径、切割进刀速度与复合材料厚度关系等关键参数,并从断面质量、尺寸精度、表面质量等方面给出了工艺质量的判定方法。

  11. Methods for producing reinforced carbon nanotubes

    Science.gov (United States)

    Ren, Zhifen; Wen, Jian Guo; Lao, Jing Y.; Li, Wenzhi

    2008-10-28

    Methods for producing reinforced carbon nanotubes having a plurality of microparticulate carbide or oxide materials formed substantially on the surface of such reinforced carbon nanotubes composite materials are disclosed. In particular, the present invention provides reinforced carbon nanotubes (CNTs) having a plurality of boron carbide nanolumps formed substantially on a surface of the reinforced CNTs that provide a reinforcing effect on CNTs, enabling their use as effective reinforcing fillers for matrix materials to give high-strength composites. The present invention also provides methods for producing such carbide reinforced CNTs.

  12. Titanium Alloys

    Directory of Open Access Journals (Sweden)

    Mark T. Whittaker

    2015-08-01

    Full Text Available Although originally discovered in the 18th century [1], the titanium industry did not experience any significant advancement until the middle of the 20th century through the development of the gas turbine engine [2]. Since then, the aerospace sector has dominated worldwide titanium use with applications in both engines and airframe structures [3]. The highly desirable combination of properties, which include excellent corrosion resistance, favourable strength to weight ratios, and an impressive resistance to fatigue, has led to an extensive range of applications [4], with only high extraction and processing costs still restricting further implementation. [...

  13. 聚合物基复合材料的增强增韧%Reinforcement and Toughening of Polymer Matrix Composites

    Institute of Scientific and Technical Information of China (English)

    董金虎

    2012-01-01

    The methods and mechanisms in the reinforcement and toughening of polymers with small organic molecules, elastomers, rigid particles, fiber, and carbon nano-tubes were reviewed. Some representative polymer/reinforcer systems were introduced. The development of reinforcement and toughening of polymers was forecast.%介绍了聚合物基复合材料增强增韧的改性方法和机理,包括有机小分子、弹性体、刚性粒子、纤维以及碳纳米管增强增韧聚合物。并介绍了一些具有代表性的聚合物/增强增韧剂体系。并对聚合物基复合材料增强增韧的发展前景进行了展望。

  14. Fibre reinforced polymer nanocomposites

    NARCIS (Netherlands)

    Vlasveld, D.P.N.

    2005-01-01

    In this thesis the results are described of the research on a combination of two types of composites: thermoplastic nanocomposites and continuous fibre composites. In this three-phase composite the main reinforcing phase are continuous glass or carbon fibres, and the matrix consists of a polyamide 6

  15. Neon-matrix spectroscopic and theoretical studies of the reactivity of titanium dimer with diatomic ligands: comparison of reactions with nitrogen and carbon monoxide.

    Science.gov (United States)

    Souvi, S M; Berkaïne, N; Alikhani, M E; Manceron, L

    2009-11-14

    The reactivity of diatomic titanium with molecular carbon monoxide has been investigated in solid neon at very low temperature. In contrast to the spontaneous reaction observed between Ti(2) and N(2), our results show that the formation of dititanium oxycarbide (OTi(2)C) from the condensation of effusive beams of Ti and CO in neon matrices involves several intermediate steps including one metastable intermediate. In the absence of electronic excitation, only formation of a Ti(2)(CO) complex occurs spontaneously during the reaction at 9 K of ground state Ti(2) and CO, as reported in solid argon by Xu, Jiang and Tsumori (Angew. Chem. Int. Ed., 2005, 44, 4338). However, during deposition or following electronic excitation, this species rearranges into a new species: the more stable, OTi(2)C oxycarbide form. Several low-lying excited states of OTi(2)C are also observed between 0.77 and 0.89 eV above the ground state, leading to a complex sequence of interacting vibronic transitions, merging into a broad continuum above 1 eV. Observations of Ti(2)(12)C(16)O, Ti(2)(13)C(16)O and Ti(2)(12)C(18)O and natural titanium isotopic data enable the identification of four fundamental vibrations in the ground electronic state and two others in the first two excited states. Quantum chemical calculations predict an open-shell (1)A(g) ground state with Ti-C and Ti-O distances close to 184 pm, and 91 degrees for the TiCTi and TiOTi bond angles, and give fundamental frequencies in good agreement with observation. The reaction paths of the Ti(2) + N(2) --> Ti(2)N(2) and Ti(2) + CO --> Ti(2)(CO) --> OTi(2)C have been investigated and a reaction scheme is proposed accounting for the similarities in nature and properties of the final products, as well as explaining the observation of a coordination complex with Ti(2) only in the case of the carbonyl ligand.

  16. Effect of fabric structure and polymer matrix on flexural strength, interlaminar shear stress, and energy dissipation of glass fiber-reinforced polymer composites

    Science.gov (United States)

    We report the effect of glass fiber structure and the epoxy polymer system on the flexural strength, interlaminar shear stress (ILSS), and energy absorption properties of glass fiber-reinforced polymer (GFRP) composites. Four different GFRP composites were fabricated from two glass fiber textiles of...

  17. Silicon ceramic reinforced by endless fibres on liquid matrix precursor (with commercial C and SiC fibres); Endlosfaser-verstaerkte Siliciumkeramik aus fluessigem Matrixprecursor (mit kommerziellen C- und SiC-Fasern)

    Energy Technology Data Exchange (ETDEWEB)

    Nieder, D.

    1991-12-13

    In this work, the possibilities of manufacture of very strong or non-brittle fracturing silicon carbide/nitride compound bodies were examined using endless ceramic fibres and liquid silazane as matrix precursor. The experiments for the selection of the different reinforcement fibres showed the good suitability of high strength C fibres HT-7 (Toho). The high module fibres HM-12 (Sigri) and the intermediate fibre T800 (Toray) were used for comparison, without reaching the same values for the compound body properties as with the high strength fibre HT-7. However, typical differences were clearly shown in the reinforcement behaviour of the high strength and high module fibres, althoug the individual types of fibres originated from different manufacturing firms. (orig.) [Deutsch] In der Arbeit wurden Herstellungsmoeglichkeiten fuer hochfeste, bzw. nicht sproedbrechende Siliciumcarbid/-nitrid-Verbundkoerper unter Verwendung keramischer Endlos-Fasern sowie fluessiger Silazane als Matrix-Precursor untersucht. Die Versuche zur Auswahl der verschiedenen Verstaerkungsfasern ergaben eine gute Eignung der Hochfest-C-Faser HT-7 (Toho). Die Hochmodulfaser HM-12 (Sigri) und die Intermediatefaser T800 (Toray) wurden fuer Vergleichszwecke eingesetzt, ohne dass mit diesen die Werte fuer die Verbundkoerpereigenschaften wie mit der Hochfestfaser HT-7 erreicht wurden. Es kamen jedoch die typischen Unterschiede im Verstaerkungsverhalten der Hochfest- und Hochmodul-Fasern deutlich zum Ausdruck, obwohl die einzelnen Fasertypen von unterschiedlichen Herstellerfirmen stammten. (orig.)

  18. Fabrication of fiber composites with a MAX phase matrix by reactive melt infiltration

    Energy Technology Data Exchange (ETDEWEB)

    Lenz, F; Krenkel, W, E-mail: Franziska.Lenz@uni-bayreuth.de [University of Bayreuth, Chair of Ceramic Materials Engineering, Ludwig-Thoma-Str. 36b, 95447 Bayreuth (Germany)

    2011-10-29

    Due to the inherent brittleness of ceramics it is very desirable to increase the damage tolerance of ceramics. The ternary MAX phases are a promising group of materials with high fracture toughness. The topic of this study is the development of ceramic matrix composites (CMCs) with a matrix containing MAX phases, to achieve a damage tolerant structural composite material. For this purpose carbon fiber reinforced preforms with a carbon-titanium carbide matrix (C/C-TiC) were developed and infiltrated with silicon by a pressureless reactive melt infiltration. Finally liquid silicon caused the formation of SiC, TiSi{sub 2} and Ti{sub 3}SiC{sub 2} in the matrix of the composite.

  19. Residual strain gradient determination in metal matrix composites by synchrotron X-ray energy dispersive diffraction

    Science.gov (United States)

    Kuntz, Todd A.; Wadley, Haydn N. G.; Black, David R.

    1993-01-01

    An X-ray technique for the measurement of internal residual strain gradients near the continuous reinforcements of metal matrix composites has been investigated. The technique utilizes high intensity white X-ray radiation from a synchrotron radiation source to obtain energy spectra from small (0.001 cu mm) volumes deep within composite samples. The viability of the technique was tested using a model system with 800 micron Al203 fibers and a commercial purity titanium matrix. Good agreement was observed between the measured residual radial and hoop strain gradients and those estimated from a simple elastic concentric cylinders model. The technique was then used to assess the strains near (SCS-6) silicon carbide fibers in a Ti-14Al-21Nb matrix after consolidation processing. Reasonable agreement between measured and calculated strains was seen provided the probe volume was located 50 microns or more from the fiber/matrix interface.

  20. Interface of Fiber-Reinforced Ceramic Matrix Composites and the Development of Toughening Mechanism%纤维增强陶瓷基复合材料界面及增韧机制的进展

    Institute of Scientific and Technical Information of China (English)

    任江; 赵英娜; 张萌

    2013-01-01

    Because of the excellent thermal stabilization, wear and tear resistant inherent resistance at high temperatures, ceramics matrix compositions are applicated in high-technique and aerospace field. The composition interface has decisive action between fiber and ceramics matrix, which is a link of fiber and matrix and also is a bridge of stress and other information. This thesis discusses respectively from the aspects of interface research for different fiber-reinforced ceramic matrix composites, and the enhance of mechanical properties between toughening mechanism and interface.%  陶瓷基复合材料以其优异的耐高温、热稳定性好、耐磨损等性能,在高技术领域和航空航天领域有重要应用。界面在纤维和陶瓷基体之间起着决定性的作用,复合材料的界面相是纤维与基体连接的纽带,也是应力及其它信息传递的桥梁。本文分别从不同复合方式、复合材料的界面研究及纤维增强基体的增韧机制和界面的力学性能等方面进行了综述。

  1. Use of a titanium mesh "shelter" combined with the soft tissue matrix expansion (tent pole) grafting in the reconstruction of a severely resorbed edentulous mandible. Technical note.

    Science.gov (United States)

    Sverzut, Cássio Edvard; Trivellato, Alexandre Elias; Sverzut, Alexander Tadeu

    2015-01-01

    Patients wearing complete dentures for a long time usually exhibit lack of bone and keratinized mucosa in the bearing area due to bone resorption. The patients suffering from this phenomenon usually have unstable and non-retentive complete denture, which result in constant trauma to the mucosa, pain, functional limitations and worsening of facial esthetics. An innovative technique has been described in which a novel surgical approach using osseointegrated dental implants as "tent poles" was applied concomitant with particulate autogenous bone graft. The authors claim that the control and maintenance of the surgically expanded soft tissue volume should prevent graft resorption in the long term. Nevertheless, resorption of the bone graft is usually more significant where the bone mass is poorer, in the mandibular body. This paper describes a case of severely resorbed edentulous mandible in which the "tent pole" technique was applied with some modifications. Use of the titanium mesh "shelters" and two additional implants was effective in "protecting" the bone graft in the posterior portion of the mandibular body increasing bone mass volume in this area. Furthermore, we believe that this kind of graft "protection" on the whole residual alveolar ridge can increase the width of bone mass gain optimizing the "tent pole" technique.

  2. Enhanced performance of a dye-sensitized solar cell with the incorporation of titanium carbide in the TiO2 matrix.

    Science.gov (United States)

    Lee, Chuan-Pei; Chen, Po-Yen; Vittal, R; Ho, Kuo-Chuan

    2010-08-28

    The effects of incorporation of various weight percentages of titanium carbide (TiC) into TiO(2) matrices on the photovoltaics of the respective dye-sensitized solar cells (DSSCs) were investigated. It is established through relevant photographs, XRD and EDX analysis that TiC was partially converted into anatase TiO(2) (a-TiO(2)) when the TiC was sintered at 450 degrees C. With the incorporation of 3.0 wt% of the TiC in the TiO(2) film, the solar-to-electricity conversion efficiency (eta) of the cell reached 7.56% from its value of 6.61% with a bare TiO(2) film. "In situ" incorporation of this TiC/a-TiO(2) composite in the commercial TiO(2) is considered as the basis for enhanced cell efficiency of the benefited cell. The variations in J(SC), FF, and V(OC) are explained by analyzing the data of dark currents, UV-absorption spectra, transparency spectra, and electrochemical impedance spectra (EIS) which were obtained under illumination and darkness. Enhancement in the V(OC) for the promoted cell is explained through pertinent electron lifetime in the TiO(2) film, which was obtained by using laser-induced photo-voltage transient studies. Electron diffusion coefficient was also measured by using laser-induced photo-current transient studies.

  3. Corrosion behaviour of groundnut shell ash and silicon carbide hybrid reinforced Al-Mg-Si alloy matrix composites in 3.5% NaCl and 0.3M H2SO4 solutions

    Directory of Open Access Journals (Sweden)

    Kenneth Kanayo ALANEME

    2015-05-01

    Full Text Available The corrosion behaviour of Al-Mg-Si alloy based composites reinforced with groundnut shell ash (GSA and silicon carbide (SiC was investigated. The aim is to assess the corrosion properties of Al-Mg-Si alloy based hybrid reinforced composites developed using different mix ratios of GSA (a cheaply processed agro waste derivative which served as partial replacement for SiC and SiC as reinforcing materials. GSA and SiC mixed in weight ratios 0:1, 1:3, 1:1, 3:1, and 1:0 were utilized to prepare 6 and 10 wt% of the reinforcing phase with Al‐Mg‐Si alloy as matrix using two‐step stir casting method. Mass loss and corrosion rate measurement was used to study the corrosion behaviour of the produced composites in 3.5% NaCl and 0.3M H2SO4 solutions. The results show that the Al-Mg-Si alloy based composites containing 6 and 10 wt% GSA and SiC in varied weight ratios were resistant to corrosion in 3.5% NaCl solution. The composites were however more susceptible to corrosion in 0.3M H2SO4 solution (in comparison with the 3.5% NaCl solution. It was noted that the Al-Mg-Si/6 wt% GSA-SiC hybrid composite grades containing GSA and SiC in weight ratio 1:3 and 3:1 respectively exhibited superior corrosion resistance in the 0.3M H2SO4 solution compared to other composites produced for this series. In the case of the Al-Mg-Si/10 wt% GSA-SiC hybrid composite grades, the corrosion resistance was relatively superior for the composites containing a greater weight ratio of GSA (75% and 100% in 0.3M H2SO4 solution.

  4. 炭纤维增强聚合物基复合材料的热氧老化机理%Thermo-oxidative aging mechanism of carbon fiber reinforced polymer matrix composites

    Institute of Scientific and Technical Information of China (English)

    樊威; 李嘉禄

    2015-01-01

    从基体、纤维和纤维/基体界面的角度,探讨了炭纤维增强聚合物基复合材料( CFRPMCs)的热氧老化机理。总结了纤维性能、纤维取向、纤维体积含量、织物结构、树脂性能、纤维/基体界面强度等因素对CFRPMCs热氧老化性能的影响规律,并简要分析了目前提高CFRPMCs热氧老化性能的方法。研究指出,立体织物增强的聚合物基复合材料能够很好地克服传统层合复合材料热氧老化后易分层的缺点,采用立体织物来增强聚合物,将会是今后提高CFRPMCs热氧稳定性的一个主要发展方向。%The thermo⁃oxidative aging mechanism of carbon fiber reinforced polymer matrix composites ( CFRPMCs) was dis⁃cussed from the perspective of matrix,fiber and the fiber/matrix interface.The influence of fiber properties,fiber orientation,fiber volume fraction,fabric structure,resin properties and fiber/matrix interface strength on the thermo⁃oxidative aging performance of CFRPMCs was investigated,and the current methods of improving the thermo⁃oxidative stability of CFRPMCs were analyzed. The study indicates that the CFRPMCs reinforced by three⁃dimensional fabrics are good at resisting the delamination as the traditional laminated composites after thermo⁃oxidative aging,and the three⁃dimensional fabric reinforced polymer composites will become an important direction of improving the thermo⁃oxidative stability of the CFRPMCs.

  5. Friction Stir Processing of Particle Reinforced Composite Materials

    Directory of Open Access Journals (Sweden)

    Daniel Solomon

    2010-01-01

    Full Text Available The objective of this article is to provide a review of friction stir processing (FSP technology and its application for microstructure modification of particle reinforced composite materials. The main focus of FSP was on aluminum based alloys and composites. Recently, many researchers have investigated this technology for treating other alloys and materials including stainless steels, magnesium, titanium, and copper. It is shown that FSP technology is very effective in microstructure modification of reinforced metal matrix composite materials. FSP has also been used in the processing and structure modification of polymeric composite materials. Compared with other manufacturing processes, friction stir processing has the advantage of reducing distortion and defects in materials. The layout of this paper is as follows. The friction stir processing technology will be presented first. Then, the application of this technology in manufacturing and structure modification of particle reinforced composite materials will be introduced. Future application of friction stir processing in energy field, for example, for vanadium alloy and composites will be discussed. Finally, the challenges for improving friction stir processing technology will be mentioned.

  6. Titanium processing using selective laser sintering

    Science.gov (United States)

    Harlan, Nicole Renee

    1999-11-01

    A materials development workstation specifically designed to test high temperature metal and metal-matrix composites for direct selective laser sintering (SLS) was constructed. Using the workstation, a titanium-aluminum alloy was sintered into single layer coupons to demonstrate the feasibility of producing titanium components using direct SLS. A combination of low temperature indirect SLS and colloidal infiltration was used to create "partially-stabilized" zirconia molds for titanium casting. The base material, stabilized zirconia mixed with a copolymer, was laser sintered into the desired mold geometry. The copolymer was pyrolyzed and replaced by a zirconia precursor. The flexural strength and surface roughness of the SLS-produced casting molds were sufficient for titanium casting trials. A laser-scanned human femur was used as the basis for a mold design and technology demonstration. Titanium castings produced from SLS molds exhibited typical as-cast microstructures and an average surface roughness (Ra) of 8 mum.

  7. Research on the Characters of the Cutting Force in Vibration Cutting Particle Reinforced Metal Matrix Composites SiC_p/Al

    Institute of Scientific and Technical Information of China (English)

    2002-01-01

    In this paper, turning experiments of machining particle reinforced metal matri x composites(PRMMCs) SiC p/Al with PCD tools have been carried out. The cutting force characteristics in ultrasonic vibration turning compared with that in com mon turning were studied. Through the single factor experiments and multiple fac tor orthogonal experiments, the influences of three kinds of cutting conditions such as cutting velocity, amount of feed and cutting depth on cutting force were analyzed in detail. Meanwh...

  8. Finite element and micromechanical modeling for investigating effective material properties of polymer-matrix nanocomposites with microfiber, reinforced by CNT arrays

    Science.gov (United States)

    Tahouneh, Vahid; Mashhadi, Mahmoud Mosavi; Naei, Mohammad Hasan

    2016-09-01

    This paper is motivated by the lack of studies to investigate the effect of fiber reinforced CNT arrays on the material properties of nanocomposites. To make a comprehensive study, this research work is conducted in two ways. Firstly, the effect of microfiber as reinforcement on the effective material properties is investigated; secondly, the study is carried on as the microfibers reinforced by CNT arrays. In both above-mentioned approaches, the results are compared to the results of generalized mixture rule which is known as a widely used micro-mechanical model. The representative volume element (RVE) is considered as a well-known method to investigate the effect of adding CNT arrays on the skin of microfibers. The results show that Generalized Mixture Rule cannot properly predict the effects of changing the length and diameter of nanotubes on the effective properties of nanocomposites. The main objective of this research work is to determine the effects of increasing nanotubes on the elastic properties which are achieved using two aforementioned methods including FE and rule of mixture. It is also absorbed; effective properties of RVE can be improved by increasing the volume fraction, length and decreasing CNT arrays diameter.

  9. Oxidation Behaviors and Oxidation Protection of Carbon Fiber Reinforced Ceramic Matrix Composites%连续碳纤维增强陶瓷基复合材料的氧化行为和氧化防护研究

    Institute of Scientific and Technical Information of China (English)

    卢国锋; 许艳

    2012-01-01

    The characteristics of the carbon fiber reinforced ceramic matrix composites (CFRCMCs) are analyzed through an overview about the oxidation behaviors of C/C and C/SiC. The four methods for oxidation protection, including the modification of the carbon fiber, the matrix antioxidation technology, the interlayer antioxidation technology and the surface coating technology, are summarized from the aspects of the fibers, matrix, interphase and exterior surface. The mechanisms and features of the four methods are analyzed.%通过叙述C/C和C/SiC两种复合材料的氧化特点分析了碳纤维增强陶瓷基复合材料(CFRCMCs)的氧化行为,分别从纤维、基体、界面层及外表面4个方面综述了碳纤维改性、基体抗氧化技术、界面层抗氧化技术和表面涂层技术4种CFRCMCs的抗氧化技术,分析了4类抗氧化技术的原理和特点.

  10. 碳纳米管/金属复合材料的研究现状与动向%Research status and trends of mental matrix composite reinforced by carbon nano-tubes

    Institute of Scientific and Technical Information of China (English)

    张坚; 李德英; 赵龙志

    2011-01-01

    Mental matrix composites reinforced by carbon nano-tubes exhibit excellent physical and chemical and mechanical properties.The research status of carbon nano-tubes metal-matrix composites,both at home and abroad,is summarized.The factors on the wide application of carbon nano-tubes metalmatrix composites are analyzed,that is ,the dispersion of carbon nano-tubes and the interfacial strength with the metal.Finally,the problems of preparing the composites and the research trends of carbon nanotubes metal-matrix composites are analyzed.%碳纳米管脸属复合材料具有优异的理化和力学性能.综述了碳纳米管金属基复合材料的国内外研究现状,分析了制约碳纳米管金属基复合材料广泛应用的因素,即碳纳米管的分散状态及其与金属基体的界面结合问题.最后,对制备碳纳米管金属基复合材料存在的问题及今后的研究动向进行了分析.

  11. Deformation Behaviors of HIPped Foil Compared with Those of Sheet Titanium Alloys

    Science.gov (United States)

    Castelli, Michael G.

    1999-01-01

    Micromechanics-based modeling of composite material behaviors requires an accurate assessment of the constituent properties and behaviors. For the specific case of continuous-fiber-reinforced metal matrix composites (MMC's) manufactured from a foil/fiber/foil process, much emphasis has been placed on characterizing foil-based matrix materials that have been fabricated in the same way as the composite. Such materials are believed to yield mechanical properties and behaviors that are representative of the matrix constituent within the composite (in situ matrix). Therefore, these materials are desired for micromechanics modeling input. Unfortunately, such foils are extremely expensive to fabricate and procure because of the labor-intensive rolling process needed to produce them. As a potential solution to this problem that would maintain appropriately representative in situ properties, the matrix constituent could be characterized with sheet-based materials, which are considerably less expensive to manufacture than foils, are more readily procured, and result in fewer plies to obtain a desired panel thickness. The critical question is, however, does the consolidated sheet material exhibit the same properties and behaviors as do the consolidated foils? Researchers at NASA Lewis Research Center's Life Prediction Branch completed a detailed experimental investigation to answer this question for three titanium alloys commonly used in metal matrix composite form.

  12. Rheocasting Al Matrix Composites

    Science.gov (United States)

    Girot, F. A.; Albingre, L.; Quenisset, J. M.; Naslain, R.

    1987-11-01

    Aluminum alloy matrix composites reinforced by SiC short fibers (or whiskers) can be prepared by rheocasting, a process which consists of the incorporation and homogeneous distribution of the reinforcement by stirring within a semi-solid alloy. Using this technique, composites containing fiber volume fractions in the range of 8-15%, have been obtained for various fibers lengths (i.e., 1 mm, 3 mm and 6 mm for SiC fibers). This paper attempts to delineate the best compocasting conditions for aluminum matrix composites reinforced by short SiC (e.g Nicalon) or SiC whiskers (e.g., Tokamax) and characterize the resulting microstructures.

  13. Preparation of Iron Matrix Composite Reinforced by In-situ Al203 Particles%自生氧化铝颗粒增强铁基复合材料的制备

    Institute of Scientific and Technical Information of China (English)

    周玉成; 魏世忠; 王利敏; 徐流杰

    2011-01-01

    Ethanol was used as reaction media, the ammonia was slowly dropped, constantly stirring into aluminum nitrate ethanol solution to neutralize. By washing with ethanol, filtering and drying, some aluminum hydroxide was obtained. Aluminum hydroxide powder and iron powder, in a certain proportion, were fully mixed. By pressing and sintering, iron matrix composite reinforced with in-situ A12O3 particle was prepared.%采用乙醇作为反应介质,将氨水滴入硝酸铝乙醇溶液中进行中和反应,经洗涤、过滤和烘干后得到氢氧化铝超细粉.将制得的超细氢氧化铝粉与铁粉按一定比例充分混合,经压制、烧结制得氧化铝颗粒增强铁基复合材料.

  14. Interfacial reaction kinetics of coated SiC fibers with various titanium alloys

    Science.gov (United States)

    Gundel, D. B.; Wawner, F. E.

    1991-01-01

    The kinetics of the reaction between the silicon carbide fibers and the titanium-based alloy matrix was investigated at temperatures from 800 to 1000 C for several titanium-based alloys (including Ti-1100 alloy and BETA 21S) and unalloyed Ti, reinforced with coated silicon carbide fiber SCS-6. The reaction zone growth kinetics was studied by exposing vacuum encapsulated samples to temperatures from 700 to 1000 C for times up to 150 hrs, followed by SAM observations of samples which were polished perpendicular to the fiber axis and etched. It was found that the reaction zone growth kinetics of the alpha (hcp) and beta (bcc) phases of unalloyed titanium reacting with SCS-6 fibers exhibited different values of the apparent activation energy and of the preexponential factor. Additions of other metals to Ti was found to slow down the reaction kinetics. Among the alloys studied, the Ti-1100 was the slowest reacting conventional alloy and the Ti-14Al-21Nb (in wt pct) was the slowest overall.

  15. TITANIUM CARBIDE CONTENT EFFECT ON EROSION IN CERMET ROCKET NOZZLES

    Science.gov (United States)

    class investigated consisted of an AISI Type 316 stainless steel matrix incorporating a hard phase of titanium carbide ranging in content from 20% to...55% by volume. The results of the study indicated that under the test conditions, increases in the titanium carbide constituents did increase the

  16. Structural and mechanical behaviour of 5% Al2O3-reinforced Fe metal matrix composites (MMCs) produced by powder metallurgy (P/M) route

    Indian Academy of Sciences (India)

    Pallav Gupta; Devendra Kumar; Om Parkash; A K Jha

    2013-10-01

    The aim of this paper is to investigate the effect of sintering temperature and time on the properties of Fe–Al2O3 composite (5 wt% Al2O3; 95 wt% Fe) prepared by powder metallurgy process. X-ray diffraction, microstructure, density, hardness and compressive strength of prepared samples have been investigated. XRD studies show the presence of Fe and Al2O3 along with iron aluminate phase. Iron aluminate is formed as a result of reactive sintering between iron and alumina particles. Microstructural examination of the specimen showed a dense structure with nanosize dispersion of the reinforcement of ceramic phase. Density as well as hardness of specimens depend on the formation of iron aluminate phase, which in turn depends on sintering temperature and time.

  17. Fabricación de compuesto de matriz epoxi reforzado con fibras largas de henequén orientadas aleatoriamente//Fabrication of a composite with epoxy matrix and henequen fibers as reinforcement long and with random orientation

    Directory of Open Access Journals (Sweden)

    Angel A. Rodríguez Soto

    2015-05-01

    Full Text Available Se obtuvo el procedimiento para la fabricación de un material compuesto con matriz de epoxi reforzado con fibras de henequén largas orientadas aleatoriamente. Fueron diseñados y elaborados seis moldes de tipo caja para la fabricación por el método de prensado en frío. Se produjeron 37 placas con 0, 6, 9, 12, 16, 22, 26 y 28 % de fibras en relación másica. La inclusión de los refuerzos fue manual y los materiales fabricados se sometieron a un proceso de cura a 70 ºC por 24 horas. Los especímenes obtenidos presentaron buena calidad estando libres de defectos y asegurando la distribución correcta de las fibras. El método de fabricación es adecuado para placas con pequeñas y grandes cantidades de fibra.Palabras claves: plásticos reforzados con fibras (PRF, fibras vegetales, compuesto de matriz termoestable, moldeo por compresión en frío.______________________________________________________________________________AbstractIs presented a procedure for the fabrication of the composite material with epoxy as matrix reinforced with henequen fibers, long and random. Was designed and fabricated six molds of box type for the manufacture of the plates using cold pressing procedure. Was make 37 plates with 0, 6, 9, 12, 16, 22, 26 and 28 % of fiber´s inclusions in mass relation. The inclusion of the reinforcements was making manually and the obtained materials was submitted to a process of cure bellow 70ºC during 24 hours. The obtained specimens showed a good quality being free of defects and guarantee the correct distribution of the fibers. The fabrication method is de adequate for plates with small and large quantities of fiber.Key words: fiber reinforced plastics (FRP, natural fibers, composite with thermoset matrix, cold compression molded.

  18. On the Mechanical Properties of Hybrid Aluminium 7075 Matrix Composite Material Reinforced with SiC and TiC Produced by Powder Metallurgy Method

    OpenAIRE

    S. Pradeep Devaneyan; R Ganesh; T. Senthilvelan

    2017-01-01

    Metal matrix composites are widely used in components of various components of industrial equipment because of their superior material properties like high stiffness to weight ratio and high impact strength and fracture toughness while compared to the conventional material. Due to the concepts of high strength to low weight ratio, Al 7075 was extensively applied in aircraft engine and wings. Even if Al 7075 has higher hardness, higher strength, excellent wear resistance, and high-temperature ...

  19. Multi-Length Scale-Enriched Continuum-Level Material Model for Kevlar (registered trademark)-Fiber-Reinforced Polymer-Matrix Composites

    Science.gov (United States)

    2013-03-01

    polymer matrix composite materials display quite complex deformation and failure behavior under ballistic/blast impact loading conditions. This complexity is generally attributed to a number of factors such as (a) hierarchical/multi-length scale architecture of the material microstructure; (b) nonlinear, rate-dependent and often pressure-sensitive mechanical response; and (c) the interplay of various intrinsic phenomena and processes such as fiber twisting, interfiber friction/sliding, etc. Material models currently employed in the computational engineering

  20. Oxidation Protection of Carbon Fiber Reinforced Ceramic Matrix Composites%碳纤维增强陶瓷基复合材料抗氧化技术研究

    Institute of Scientific and Technical Information of China (English)

    卢国锋; 侯君涛

    2012-01-01

    Carbon fiber reinforced ceramic matrix composites (CFRCMCs) are the ideal thermostructure materials owing to its perfect high - temperature mechanical property and good hot property. However, the carbon fiber in the CFRCMCs could be oxidized easily, so the oxidation protection of the CFRCMCs had attracted the interest of researchers. In this paper, the methods for oxidation protection, such as modification of the carbon fibers, oxidation protection by matrix, and oxidation protection by interphase and coat- ing technology, were discussed, and their mechanics and features were summarized. The development trend of the antioxidation technology was prospected.%碳纤维增强陶瓷基复合材料(CFRCMCs)具有良好的高温力学性能和热性能,是航空航天领域非常理想的热结构材料.但CFRCMCs中的碳纤维极易发生氧化,因此CFRCMCs的氧化防护问题一直是CFRCMCs研究的热点.文章对碳纤维改性、基体抗氧化技术、界面层抗氧化技术和表面涂层技术这四种CFRCMCs的抗氧化技术及其原理进行了评述,分析了各类抗氧化技术的特点并对其发展趋势进行了展望.

  1. Development of an in-situ synthesized multi-component reinforced Al–4.5%Cu–TiC metal matrix composite by FAS technique – Optimization of process parameters

    Directory of Open Access Journals (Sweden)

    Biswajit Das

    2016-03-01

    Full Text Available In the present investigation, an in-situ multi-component reinforced aluminium copper alloy based metal matrix composite was fabricated by the flux assisted synthesis (FAS technique. It was found from the optical microscopy analysis that TiC particles are formed in the composite. Further the present research investigates the feasibility and dry machining characteristics of Al–4.5%Cu/5TiC metal matrix composite in CNC milling machine using uncoated solid carbide end mill cutter. The effect of the machining parameters such as feed, cutting speed, depth of cut on the response parameters such as cutting force and COM is determined by using analysis of variance (ANOVA. From the analysis it was found that cutting speed and depth of cut played a major role in affecting cutting force. Multi output optimization of the process was carried out by the application of the Taguchi method with fuzzy logic, and the confirmatory test has revealed the accuracy of the developed model. For predicting the response parameters, regression equations were developed and verified with a number of test cases and it was observed that the percentage error for both responses is less than ±3%, which indicates there is a close agreement between the predicted and the measured results.

  2. Standard Test Method for Measuring the Curved Beam Strength of a Fiber-Reinforced Polymer-Matrix Composite - (View Full Text) D6416/D6416M-01(2007) Standard Test Method for Two-Dimensional Flexural Properties of Simply Supported Sandwich Composite Plates Subjected to a Distributed Load

    CERN Document Server

    American Society for Testing and Materials. Philadelphia

    2001-01-01

    Standard Test Method for Measuring the Curved Beam Strength of a Fiber-Reinforced Polymer-Matrix Composite - (View Full Text) D6416/D6416M-01(2007) Standard Test Method for Two-Dimensional Flexural Properties of Simply Supported Sandwich Composite Plates Subjected to a Distributed Load

  3. Opportunities in the electrowinning of molten titanium from titanium dioxide

    CSIR Research Space (South Africa)

    Van Vuuren, DS

    2005-10-01

    Full Text Available ; the high affinity of titanium for carbon, oxygen, and nitrogen; and physical and chemical properties of the different titanium oxide species when reducing titanium from Ti4+ to metallic titanium....

  4. FORMATION MECHANISM OF TITANIUM CARBIDE CRYSTAL IN LASER SYNTHESIZED METAL-CERAMIC COMPOSITE COATING

    OpenAIRE

    BAOSHUAI DU; ZHONGWEN. ZHANG; XINHONG WANG; ZENGDA ZOU

    2011-01-01

    In situ titanium carbide reinforced iron-based composite coating was deposited on mild carbon steel using laser surface engineering (LSE) with ferrotitanium and graphite as precursor. The microstructure and phase constituents of the deposited coating were characterized. Formation mechanism of titanium carbide crystal in the composite coating was elucidated by correlating the morphology of titanium carbide and the thermal cycle experienced by the precursor during the laser treatment. It was de...

  5. Preparation and characterisation of poly p-phenylene-2,6-benzobisoxazole fibre-reinforced resin matrix composite for endodontic post material: a preliminary study.

    Science.gov (United States)

    Hu, Chen; Wang, Feng; Yang, Huiyong; Ai, Jun; Wang, Linlin; Jing, Dongdong; Shao, Longquan; Zhou, Xingui

    2014-12-01

    Currently used fibre-reinforced composite (FRC) intracanal posts possess low flexural strength which usually causes post fracture when restoring teeth with extensive loss. To improve the flexural strength of FRC, we aimed to apply a high-performance fibre, poly p-phenylene-2, 6-benzobisoxazole (PBO), to FRCs to develop a new intracanal post material. To improve the interfacial adhesion strength, the PBO fibre was treated with coupling agent (Z-6040), argon plasma, or a combination of above two methods. The effects of the surface modifications on PBO fibre were characterised by determining the single fibre tensile strength and interfacial shear strength (IFSS). The mechanical properties of PBO FRCs were characterised by flexural strength and flexural modulus. The cytotoxicity of PBO FRC was evaluated by the MTT assay. Fibres treated with a combination of Z-6040 and argon plasma possessed a significantly higher IFSS than untreated fibres. Fibre treated with the combination of Z-6040-argon-plasma FRC had the best flexural strength (531.51 ± 26.43MPa) among all treated fibre FRCs and had sufficient flexural strength and appropriate flexural moduli to be used as intracanal post material. Furthermore, an in vitro cytotoxicity assay confirmed that PBO FRCs possessed an acceptable level of cytotoxicity. In summary, our study verified the feasibility of using PBO FRC composites as new intracanal post material. Although the mechanical property of PBO FRC still has room for improvement, our study provides a new avenue for intracanal post material development in the future. To our knowledge, this is the first study to verify the feasibility of using PBO FRC composites as new intracanal post material. Our study provided a new option for intracanal post material development. Copyright © 2014 Elsevier Ltd. All rights reserved.

  6. Taguchi design optimization of machining parameters on the CNC end milling process of halloysite nanotube with aluminium reinforced epoxy matrix (HNT/Al/Ep hybrid composite

    Directory of Open Access Journals (Sweden)

    J.S. Pang

    2014-08-01

    Full Text Available This paper introduces the application of Taguchi optimization methodology in optimizing the cutting parameters of end-milling process for machining the halloysite nanotubes (HNTs with aluminium reinforced epoxy hybrid composite material under dry condition. The machining parameters which are chosen to be evaluated in this study are the depth of cut (d, cutting speed (S and feed rate (f. While, the response factors to be measured are the surface roughness of the machined composite surface and the cutting force. An orthogonal array of the Taguchi method was set-up and used to analyse the effect of the milling parameters on the surface roughness and cutting force. The result from this study shows that the application of the Taguchi method can determine the best combination of machining parameters that can provide the optimal machining response conditions which are the lowest surface roughness and lowest cutting force value. For the best surface finish, A1–B3–C3 (d = 0.4 mm, S = 1500 rpm, f = 60 mmpm is found to be the optimized combination of levels for all the three control factors from the analysis. Meanwhile, the optimized combination of levels for all the three control factors from the analysis which provides the lowest cutting force was found to be A2–B2–C2 (d = 0.6 mm, S = 1000 rpm, f = 40 mmpm.

  7. Titanium and titanium alloys fundamentals and applications

    CERN Document Server

    Peters, Manfred

    2003-01-01

    This handbook is an excellent reference for materials scientists and engineers needing to gain more knowledge about these engineering materials. Following introductory chapters on the fundamental materials properties of titanium, readers will find comprehensive descriptions of the development, processing and properties of modern titanium alloys. There then follows detailed discussion of the applications of titanium and its alloys in aerospace, medicine, energy and automotive technology.

  8. Microstructure and mechanical properties of aluminium matrix composites reinforced by Al{sub 62}Cu{sub 25.5}Fe{sub 12.5} melt spun ribbon

    Energy Technology Data Exchange (ETDEWEB)

    Lityńska-Dobrzyńska, Lidia, E-mail: l.litynska@imim.pl; Mitka, Mikołaj; Góral, Anna; Stan-Głowińska, Katarzyna; Dutkiewicz, Jan

    2016-07-15

    Aluminium matrix composites containing 15, 30 and 50 vol.% of pulverized Al{sub 62}Cu{sub 25.5}Fe{sub 12.5} (in at.%) melt spun ribbons have been prepared by a vacuum hot pressing (T = 673 K, P = 600 MPa). The microstructure of the initial ribbon and the composites was investigated using X-ray, scanning and transmission electron microscopy. In the as-spun ribbon the quasicrystalline icosahedral phase (i-phase) coexisted with the cubic copper rich β-Al(Cu, Fe) intermetallic compound. The phase composition of Al-Cu-Fe particles changed after consolidation process and the i-phase transformed partially to the ω-Al{sub 70}Cu{sub 20}Fe{sub 10} phase. Additionally, the Θ-Al{sub 2}Cu phase formed at the α(Al)/Al-Cu-Fe particle interfaces. With an increase in volume fraction of the reinforcement the hardness of the composites increased up to HV = 180 for the highest amount of added particles. The ultimate compression strength of the same sample reached the value of 545 MPa. - Highlights: • Al and 15, 30, 50% of pulverized Al{sub 62}Cu{sub 25.5}Fe{sub 12.5} melt spun ribbon were consolidated. • The initial ribbon consisted of the icosahedral i-phase and copper rich β-Al(Cu, Fe). • The i-phase partially transforms to ω-Al{sub 7}Cu{sub 2}Fe phase in all composites. • Increase of microhardness and compressive strength with content of reinforcement • Ultimate compression strength 545 MPa for 50% of added particles.

  9. Corrosion control of cement-matrix and aluminum-matrix composites

    Science.gov (United States)

    Hou, Jiangyuan

    Corrosion control of composite materials, particularly aluminum-matrix and cement-matrix composites, was addressed by surface treatment, composite formulation and cathodic protection. Surface treatment methods studied include anodization in the case of aluminum-matrix composites and oxidation treatment (using water) in the case of steel rebar for reinforcing concrete. The effects of reinforcement species (aluminum nitride (AIN) versus silicon carbide (SiC) particles) in the aluminum-matrix composites and of admixtures (carbon fibers, silica fume, latex and methylcellulose) in concrete on the corrosion resistance of composites were addressed. Moreover, the effect of admixtures in concrete and of admixtures in mortar overlay (as anode on concrete) on the efficiency of cathodic protection of steel reinforced concrete was studied. For SiC particle filled aluminum, anodization was performed successfully in an acid electrolyte, as for most aluminum alloys. However, for AlN particle filled aluminum, anodization needs to be performed in an alkaline (0.7 N NaOH) electrolyte instead. The concentration of NaOH in the electrolyte was critical. It was found that both silica fume and latex improved the corrosion resistance of rebar in concrete in both Ca(OH)sb2 and NaCl solutions, mainly because these admixtures decreased the water absorptivity. Silica fume was more effective than latex. Methylcellulose improved the corrosion resistance of rebar in concrete a little in Ca(OH)sb2 solution. Carbon fibers decreased the corrosion resistance of rebar in concrete, but this effect could be made up for by either silica fume or latex, such that silica fume was more effective than latex. Surface treatment in the form of water immersion for two days was found to improve the corrosion resistance of rebar in concrete. This treatment resulted in a thin uniform layer of black iron oxide (containing Fesp{2+}) on the entire rebar surface except on the cross-sectional surface. Prior to the

  10. Characterization of Titanium-Containing Compounds in Gray Iron

    Institute of Scientific and Technical Information of China (English)

    ZENG Daxin; ZHANG Yuanhao; LIU Jianyong; HE Hanjun; HONG Xiaoxian

    2008-01-01

    Titanium produces different compounds in gray iron. In order to determine their characteristics, a scanning electron microscope, an energy dispersive X-ray spectroscopy, and an optical microscopy were used to analyze the morphology, distribution, and composition of titanium-containing compounds in metal-lographic specimens and machined surfaces in four gray irons. The results show that the titanium-containing compounds in the gray irons are complex compounds containing V, Nb, Mn, S, and other metals, depending on the concentration of these elements in the iron. The number of titanium-containing compounds increases with increasing Ti content in the gray iron. Most of the titanium-containing compounds are located in the peariite matrix, with some in the steadite and carbides. The results suggest that titanium-containing com-pounds reduce tool lifetime.

  11. Nano and hybrid aluminum based metal matrix composites: an overview

    Directory of Open Access Journals (Sweden)

    Muley Aniruddha V.

    2015-01-01

    Full Text Available Aluminium matrix composites (AMCs are potential light weight engineering materials with excellent properties. AMCs find application in many areas including automobile, mining, aerospace and defence, etc. Due to technological advancements, it is possible to use nano sized reinforcement in Al matrix. Nano sized reinforcements enhance the properties of Al matrix compared to micro sized reinforcements. Hybrid reinforcement imbibe superior properties to aluminium matrix composites as compared with Al composites having single reinforcement. This paper is focused on overview of development in the field of Al based metal matrix with nano and hybrid aluminium based composites.

  12. 石英纤维增强陶瓷基复合材料制孔工艺研究%Research on drilling technology of quartz fiber reinforced ceramic matrix composites

    Institute of Scientific and Technical Information of China (English)

    冉冲; 卢守相; 王东坡; 赵桐; 高航

    2016-01-01

    本试验针对目前硬质合金刀具加工石英纤维增强陶瓷基复合材料时存在的刀具磨损严重、加工质量差、效率低下等问题,对比了硬质合金刀具钻孔、PCD 刀具钻孔和电镀金刚石套料钻螺旋铣磨制孔的效果,分析了切削力对制孔质量的影响。研究结果表明:纬纱纤维对 X 向和Y 向切削力的影响明显大于经纱纤维,垂直于纬纱纤维方向的切削力较小,平行于纬纱纤维方向的切削力较大;PCD 刀具钻孔质量相对较好,刀具磨损不明显,适用于石英纤维增强陶瓷基复合材料的制孔加工。%For the existing troubles of carbide tool (serious tool wear,poor machining quality,low efficiency) when processing quartz fiber reinforced ceramic matrix composites,cutting force effect on the hole quality is analyzed in this paper by comparing the machining effects of carbide tool,PCD tool and electroplated diamond core drilling tool.The results show that the influence of weft fiber on the cutting force of X and Y direction is more obvious than that of warp fiber. The cutting force perpendicular to the weft fiber is smaller while the cutting force in parallel with the weft fiber direction is bigger.Moreover,the hole quality drilled by PCD tool is relatively better and the tool wear is not obvious,so PCD tool is suitable for processing the quartz fiber reinforced ceramic matrix composites.

  13. Chinese titanium industry

    Institute of Scientific and Technical Information of China (English)

    2010-01-01

    <正>The effects of the financial crisis on the titanium industry are visible: investment plans for titanium smelting and processing have basically come to a halt in 2009, and projects under construction were also delayed. However, the

  14. Residual microstructure associated with impact crater in Ti-6Al-4V meshes reinforced 5A06Al alloy matrix composite.

    Science.gov (United States)

    Guo, Q; Chen, G Q; Jiang, L T; Hussain, M; Han, X L; Sun, D L; Wu, G H

    2012-02-01

    In this paper, TC4(m)/5A06Al composite was hypervelocity impacted by 2024 aluminium projectile with the diameter of 2mm and with the impact velocity of 3.5 km/s. The residual microstructure was observed by scanning electron microscopy (SEM), transmission electron microscopy (TEM) and high-resolution transmission electron microscopy (HREM). The TC4-Al interface before impact was composed of TiAl(3) phase and Ti(3)Al phase. Near the pithead, separation of TC4 fibers and Al matrix occurred along the impact direction. Around the middle of the crater, TC4 fibers were sheared into several sections. Near the bottom of crater, adiabatic shear band (ASB) occurred in TC4 fiber, while the angle between shear plane and cross section was 45°. The crack propagated along TC4-Ti(3)Al interface during impact and some Ti(3)Al phase at the TC4-Al interface transformed to amorphous with few nanocrystals after hypervelocity impact. Copyright © 2011 Elsevier Ltd. All rights reserved.

  15. Evaluation of the reinforcement effect on teeth with different apical foramen diameters of retrograde or orthograde MTA application with internal matrix

    Directory of Open Access Journals (Sweden)

    Emre Bayram

    2016-01-01

    Full Text Available OBJECTIVE: The aim of this study was to determine the effect of the apical foramen diameter and different application methods of Mineral Trioxide Aggregate (MTA on the fracture resistance of simulated immature teeth using a Universal Testing Machine. MATERIALS AND METHOD: Ninety extracted human teeth were used for the fracture resistance test. The apical foramen was prepared to a diameter of 1.0 mm or 1.4 mm to simulate the open apex of immature teeth. MTA was mixed according to manufacturer's recommendations and placed into the root canals with different apical foramen diameter by four different root filling techniques: retrograde, two-phased orthograde, and ortograde with or without internal matrix. Prepared roots were marked 2 mm below the cemento-enamel junction and embedded in transparent acrylic resin in cylinder moulds. Vertical force was applied along the long axis of the tooth at a speed of 5 mm/min, and the maximum resistance to fracture for each tooth was determined in Newton. A software package was used for the statistical analysis. The data were analyzed by using one-way ANOVA and post-hoc Tukey tests. RESULTS: A statistically significant difference could not be observed between the groups (p>0.05 whereas statistically significant differences were found between the test groups and the control groups (p<0.05. CONCLUSION: There was no significant difference between different vertical root filling techniques in increasing the fracture strength of the teeth. The diameter of the apical foramen did not have a significant effect on the fracture resistance.

  16. Nanostructured composite reinforced material

    Science.gov (United States)

    Seals, Roland D [Oak Ridge, TN; Ripley, Edward B [Knoxville, TN; Ludtka, Gerard M [Oak Ridge, TN

    2012-07-31

    A family of materials wherein nanostructures and/or nanotubes are incorporated into a multi-component material arrangement, such as a metallic or ceramic alloy or composite/aggregate, producing a new material or metallic/ceramic alloy. The new material has significantly increased strength, up to several thousands of times normal and perhaps substantially more, as well as significantly decreased weight. The new materials may be manufactured into a component where the nanostructure or nanostructure reinforcement is incorporated into the bulk and/or matrix material, or as a coating where the nanostructure or nanostructure reinforcement is incorporated into the coating or surface of a "normal" substrate material. The nanostructures are incorporated into the material structure either randomly or aligned, within grains, or along or across grain boundaries.

  17. Rapid prototyped porous nickel-titanium scaffolds as bone substitutes.

    Science.gov (United States)

    Hoffmann, Waldemar; Bormann, Therese; Rossi, Antonella; Müller, Bert; Schumacher, Ralf; Martin, Ivan; de Wild, Michael; Wendt, David

    2014-01-01

    While calcium phosphate-based ceramics are currently the most widely used materials in bone repair, they generally lack tensile strength for initial load bearing. Bulk titanium is the gold standard of metallic implant materials, but does not match the mechanical properties of the surrounding bone, potentially leading to problems of fixation and bone resorption. As an alternative, nickel-titanium alloys possess a unique combination of mechanical properties including a relatively low elastic modulus, pseudoelasticity, and high damping capacity, matching the properties of bone better than any other metallic material. With the ultimate goal of fabricating porous implants for spinal, orthopedic and dental applications, nickel-titanium substrates were fabricated by means of selective laser melting. The response of human mesenchymal stromal cells to the nickel-titanium substrates was compared to mesenchymal stromal cells cultured on clinically used titanium. Selective laser melted titanium as well as surface-treated nickel-titanium and titanium served as controls. Mesenchymal stromal cells had similar proliferation rates when cultured on selective laser melted nickel-titanium, clinically used titanium, or controls. Osteogenic differentiation was similar for mesenchymal stromal cells cultured on the selected materials, as indicated by similar gene expression levels of bone sialoprotein and osteocalcin. Mesenchymal stromal cells seeded and cultured on porous three-dimensional selective laser melted nickel-titanium scaffolds homogeneously colonized the scaffold, and following osteogenic induction, filled the scaffold's pore volume with extracellular matrix. The combination of bone-related mechanical properties of selective laser melted nickel-titanium with its cytocompatibility and support of osteogenic differentiation of mesenchymal stromal cells highlights its potential as a superior bone substitute as compared to clinically used titanium.

  18. Rapid prototyped porous nickel–titanium scaffolds as bone substitutes

    Directory of Open Access Journals (Sweden)

    Waldemar Hoffmann

    2014-06-01

    Full Text Available While calcium phosphate–based ceramics are currently the most widely used materials in bone repair, they generally lack tensile strength for initial load bearing. Bulk titanium is the gold standard of metallic implant materials, but does not match the mechanical properties of the surrounding bone, potentially leading to problems of fixation and bone resorption. As an alternative, nickel–titanium alloys possess a unique combination of mechanical properties including a relatively low elastic modulus, pseudoelasticity, and high damping capacity, matching the properties of bone better than any other metallic material. With the ultimate goal of fabricating porous implants for spinal, orthopedic and dental applications, nickel–titanium substrates were fabricated by means of selective laser melting. The response of human mesenchymal stromal cells to the nickel–titanium substrates was compared to mesenchymal stromal cells cultured on clinically used titanium. Selective laser melted titanium as well as surface-treated nickel–titanium and titanium served as controls. Mesenchymal stromal cells had similar proliferation rates when cultured on selective laser melted nickel–titanium, clinically used titanium, or controls. Osteogenic differentiation was similar for mesenchymal stromal cells cultured on the selected materials, as indicated by similar gene expression levels of bone sialoprotein and osteocalcin. Mesenchymal stromal cells seeded and cultured on porous three-dimensional selective laser melted nickel–titanium scaffolds homogeneously colonized the scaffold, and following osteogenic induction, filled the scaffold’s pore volume with extracellular matrix. The combination of bone-related mechanical properties of selective laser melted nickel–titanium with its cytocompatibility and support of osteogenic differentiation of mesenchymal stromal cells highlights its potential as a superior bone substitute as compared to clinically used

  19. Synthesis of Y2O3-ZrO2-SiO2 composite coatings on carbon fiber reinforced resin matrix composite by an electro-plasma process

    Science.gov (United States)

    Zhang, Yuping; Lin, Xiang; Chen, Weiwei; Cheng, Huanwu; Wang, Lu

    2016-05-01

    In the present paper the Y2O3-ZrO2-SiO2 composite coating was successfully synthesized on carbon fiber reinforced resin matrix composite by an electro-plasma process. The deposition process, microstructures and oxidation resistance of the coatings with different SiO2 concentrations were systematically investigated. A relatively dense microstructure was observed for the Y2O3-ZrO2-SiO2 composite coating with the SiO2 concentration above 5 g/L. The coating exhibited very good oxidation resistance at 1273 K with the mass loss rate as low as ∼30 wt.%, compared to 100 wt.% of the substrate. The formation of the ceramic composites was discussed in detail based on the electrochemical mechanism and the deposition dynamics in order to explain the effect of the plasma discharge. We believe that the electro-plasma process will find wide applications in preparing ceramics and coatings in industries.

  20. 碳纤维增强热塑性树脂基复合材料的研究现状%Advance of the Research in Carbon Fiber Reinforced Thermoplastic Resin Matrix Composite

    Institute of Scientific and Technical Information of China (English)

    尹翔宇; 朱波; 刘洪正; 郑连勇; 张春雷

    2011-01-01

    综述了国内碳纤维增强聚酰胺(PA6)、聚醚砜(PES)、聚碳酸酯(PC)、聚苯硫醚(PPS)、聚醚砜酮(PPESK),聚醚醚酮(PEEK)、热塑性聚酰亚胺(PI)等热塑性树脂基复合材料研究现状,对比了热固性树脂基复合材料与热塑性树脂基复合材料性能及成型工艺方面的差异,并对碳纤维增强热塑性树脂基复合材料的成型方法,碳纤维质量分数、长度和表面处理方法对复合材料性能影响的一般规律作了总结。%The domestic situation of carbon fiber reinforced thermoplastic (PA, PES, PC, PPS, PPESK, PEEK, PI and so on) composites were synthetically discussed in the paper, meanwhile, the differences of molding process and properties between thermosetting and thermoplastic matrix composite materials were contrasted. In addition we summarized the regular influences of molding method and carbon fiber including their content, length, surface treatment on the performance of composite materials.