Rare earth ion controlled crystallization of mica glass-ceramics

Energy Technology Data Exchange (ETDEWEB)

Garai, Mrinmoy; Karmakar, Basudeb, E-mail: basudebk@cgcri.res.in

2016-09-05

In understanding the effects of rare earth ions to control the crystallization and microstructure of alkaline boroaluminosilicate system, the CeO{sub 2}, Nd{sub 2}O{sub 3}, Sm{sub 2}O{sub 3} and Gd{sub 2}O{sub 3} doped K{sub 2}O−MgO−B{sub 2}O{sub 3}−Al{sub 2}O{sub 3}−SiO{sub 2}−F glasses were synthesized by melt-quenching at 1550 °C. Higher density (2.82–3.06 g cm{sup −3}) and thermal stability (glass phase) is experiential on addition of rare earth content, which also affects in increasing the glass transition temperature (T{sub g}) and crystallization temperature (T{sub c}). Decrease of thermal expansion in glasses with rare earth ion content is maintained by the stabilization of glass matrix owing to their large cationic field strength. A significant change in the non-isothermal DSC thermogram observed at 750–1050 °C is attributed to fluorophlogopite crystallization. Opaque glass-ceramics were prepared from such glasses by single step heat-treatment at 1050 °C; and the predominant crystalline phases are identified as fluorophlogopite mica, KMg{sub 3}(AlSi{sub 3}O{sub 10})F{sub 2} by XRD and EDX analysis. The compact glass-ceramic microstructure by the agglomeration of fluorophlogopite mica crystallites (crystal size ∼ 100–500 nm, FESEM) is achieved in attendance of rare earth ion; and such microstructure controlled the variation of density, thermal expansion and microhardness value. Higher thermal expansion (11.11–14.08 × 10{sup −6}/K at 50–800 °C and 50–900 °C) of such glass-ceramics approve that these rare earth containing glasses can be useful for high temperature vacuum sealing application with metal or solid electrolyte. The increase of Vickers microhardness (5.27–5.61 GPa) in attendance of rare earth ions is attributed to the compact crystallinity of fluorophlogopite mica glass-ceramic microstructure. - Highlights: • Synthesis of rare earth oxide doped alkaline boroaluminosilicate glasses. • Development of opaque

Spectroscopy and Device Performance of Rare Earth Doped III-Nitrides

National Research Council Canada - National Science Library

Hommerich, Uwe

2002-01-01

.... Prime candidates for redgreen- blue (RGB) emission are the rare earth ions Eu3+ (red), Er3+ (green), and Tm3+ (blue). A full-color TFEL phosphor system based on RE doped GaN has been demonstrated with high brightness...

Sensing Using Rare-Earth-Doped Upconversion Nanoparticles

OpenAIRE

Hao, Shuwei; Chen, Guanying; Yang, Chunhui

2013-01-01

Optical sensing plays an important role in theranostics due to its capability to detect hint biochemical entities or molecular targets as well as to precisely monitor specific fundamental psychological processes. Rare-earth (RE) doped upconversion nanoparticles (UCNPs) are promising for these endeavors due to their unique frequency converting capability; they emit efficient and sharp visible or ultraviolet (UV) luminescence via use of ladder-like energy levels of RE ions when excited at near ...

Optical spectroscopy of rare earth ion-doped TiO2 nanophosphors.

Science.gov (United States)

Chen, Xueyuan; Luo, Wenqin

2010-03-01

Trivalent rare-earth (RE3+) ion-doped TiO2 nanophosphors belong to one kind of novel optical materials and have attracted increasing attention. The luminescence properties of different RE3+ ions in various TiO2 nanomaterials have been reviewed. Much attention is paid to our recent progresses on the luminescence properties of RE3+ (RE = Eu, Er, Sm, Nd) ions in anatase TiO2 nanoparticles prepared by a sol-gel-solvothermal method. Using Eu3+ as a sensitive optical probe, three significantly different luminescence centers of Eu3+ in TiO2 nanoparticles were detected by means of site-selective spectroscopy at 10 K. Based on the crystal-field (CF) splitting of Eu3+ at each site, C2v and D2 symmetries were proposed for Eu3+ incorporated at two lattice sites. A structural model for the formation of multiple sites was proposed based on the optical behaviors of Eu3+ at different sites. Similar multi-site luminescence was observed in Sm(3+)- or Nd(3+)-doped TiO2 nanoparticles. In Eu(3+)-doped TiO2 nanoparticles, only weak energy transfer from the TiO2 host to the Eu3+ ions was observed at 10 K due to the mismatch of energy between the TiO2 band-gap and the Eu3+ excited states. On the contrary, efficient host-sensitized luminescences were realized in Sm(3+)- or Nd(3+)-doped anatase TiO2 nanoparticles due to the match of energy between TiO2 band-gap and the Sm3+ and Nd3+ excited states. The excitation spectra of both Sm(3+)- and Nd(3+)-doped samples exhibit a dominant broad peak centered at approximately 340 nm, which is associated with the band-gap of TiO2, indicating that sensitized emission is much more efficient than direct excitation of the Sm3+ and Nd3+ ions. Single lattice site emission of Er3+ in TiO2 nanocrystals can be achieved by modifying the experimental conditions. Upon excitation by a Ti: sapphire laser at 978 nm, intense green upconverted luminescence was observed. The characteristic emission of Er3+ ions was obtained both in the ultraviolet-visible (UV-vis) and

Experimental demonstration of efficient and selective population transfer and qubit distillation in a rare-earth-metal-ion-doped crystal

International Nuclear Information System (INIS)

Rippe, Lars; Nilsson, Mattias; Kroell, Stefan; Klieber, Robert; Suter, Dieter

2005-01-01

In optically controlled quantum computers it may be favorable to address different qubits using light with different frequencies, since the optical diffraction does not then limit the distance between qubits. Using qubits that are close to each other enables qubit-qubit interactions and gate operations that are strong and fast in comparison to qubit-environment interactions and decoherence rates. However, as qubits are addressed in frequency space, great care has to be taken when designing the laser pulses, so that they perform the desired operation on one qubit, without affecting other qubits. Complex hyperbolic secant pulses have theoretically been shown to be excellent for such frequency-addressed quantum computing [I. Roos and K. Molmer, Phys. Rev. A 69, 022321 (2004)] - e.g., for use in quantum computers based on optical interactions in rare-earth-metal-ion-doped crystals. The optical transition lines of the rare-earth-metal-ions are inhomogeneously broadened and therefore the frequency of the excitation pulses can be used to selectively address qubit ions that are spatially separated by a distance much less than a wavelength. Here, frequency-selective transfer of qubit ions between qubit states using complex hyperbolic secant pulses is experimentally demonstrated. Transfer efficiencies better than 90% were obtained. Using the complex hyperbolic secant pulses it was also possible to create two groups of ions, absorbing at specific frequencies, where 85% of the ions at one of the frequencies was shifted out of resonance with the field when ions in the other frequency group were excited. This procedure of selecting interacting ions, called qubit distillation, was carried out in preparation for two-qubit gate operations in the rare-earth-metal-ion-doped crystals. The techniques for frequency-selective state-to-state transfer developed here may be also useful also for other quantum optics and quantum information experiments in these long-coherence-time solid

High index contrast potassium double tungstate waveguides towards efficient rare-earth ion amplification on-chip

NARCIS (Netherlands)

Sefünç, Mustafa; Segerink, Franciscus B.; García Blanco, Sonia Maria

2015-01-01

Rare-earth ion doped KY(WO4)2 amplifiers are proposed to be a good candidate for many future applications by benefiting from the excellent gain characteristics of rare-earth ions, namely high bit rate amplification (

Laser action on rare earth doped nitride semiconductor thin layers

International Nuclear Information System (INIS)

Oussif, A.; Diaf, M.

2010-01-01

Complete text of publication follows. The structure, chemical composition, properties, and their relationships in solids lay the foundation of materials science. Recently, great interest in rare-earth (RE)-doped wide-bandgap semiconductors, which combine the electronic properties of semiconductors with the unique luminescence features of RE ions, is from the fundamental standpoint of structure-composition-properties of solids. At first, a significant amount of work has been reported on the study of infrared emissions from Er 3+- doped semiconductors because Er 3+ exhibits luminescence at 1.54 μm, a wavelength used in optical communications. Since Steckl and Birkhahn first reported visible emission associated with Er from GaN:Er films, the RE-doped semiconductors have received considerable interest for possible application in light emitting devices. Molecular-beam epitaxy (MBE) and metalorganic chemical vapour deposition (MOCVD) have been used mainly to grow GaN host films. The RE dopants were typically incorporated into the host films by in situ doping during the growth or by ion implantation after the growth. GaN doped with rare-earth elements (RE) hold significant potential for applications in optical devices, since they show sharp intense luminescence which is only minimally affected by temperature variations. Among the various RE dopants, Eu seems to be the most interesting, since it yields red luminescence 622 nm which has not been realized in commercially available light emitting devices (LEDs) that use InGaN active layers. We have earlier reported single crystalline growth of Eu-doped GaN and nearly temperature independent red luminescence at 622 nm originating from the intra-4f-4f transition of the Eu 3+ ion. The red luminescence was analyzed and determined to be generated through trap-level-mediated energy transfer from the semiconductor host.

Fiber-optic thermometer application of thermal radiation from rare-earth end-doped SiO2 fiber

International Nuclear Information System (INIS)

Katsumata, Toru; Morita, Kentaro; Komuro, Shuji; Aizawa, Hiroaki

2014-01-01

Visible light thermal radiation from SiO 2 glass doped with Y, La, Ce, Pr, Nd, Eu, Tb, Dy, Ho, Er, Tm, Yb, and Lu were studied for the fiber-optic thermometer application based on the temperature dependence of thermal radiation. Thermal radiations according to Planck's law of radiation are observed from the SiO 2 fibers doped with Y, La, Ce, Pr, Eu, Tb, and Lu at the temperature above 1100 K. Thermal radiations due to f-f transitions of rare-earth ions are observed from the SiO 2 fibers doped with Nd, Dy, Ho, Er, Tm, and Yb at the temperature above 900 K. Peak intensities of thermal radiations from rare-earth doped SiO 2 fibers increase sensitively with temperature. Thermal activation energies of thermal radiations by f-f transitions seen in Nd, Dy, Ho, Er, Tm, and Yb doped SiO 2 fibers are smaller than those from SiO 2 fibers doped with Y, La, Ce, Pr, Eu, Tb, and Lu. Thermal radiation due to highly efficient f-f transitions in Nd, Dy, Ho, Er, Tm, and Yb ions emits more easily than usual thermal radiation process. Thermal radiations from rare-earth doped SiO 2 are potentially applicable for the fiber-optic thermometry above 900 K

Preparation of Rare Earth Doped Alumina-Siloxane Gel and Its ER Effect

Institute of Scientific and Technical Information of China (English)

李幼荣; 张明; 周兰香; 邱关明; 井上真一; 冈本宏

2002-01-01

Poly(methyl methacrylate) (PMMA) was used to wrap alumina-siloxane sol through emulsion polymerization. A kind of suspensions with notable ER effect was produced by fully mixing the prepared microcapsule with silicon oil. Meanwhile a series of PMMA wrapped alumina-siloxane gel doped with rare earths was obtained and its ER effect was tested, like viscosity of different rare earth ion doped samples in different powder concentrations and at different temperatures, at the same time, leak current density and dielectric constant were measured. Results show that the ER effect of this suspension is remarkable, and its stability is much better. The condition of emulsion polymerization and the mechanism of effect are discussed.

Rare-Earth Oxide Ion (Tm3+, Ho3+, and U3+) Doped Glasses and Fibres for 1.8 to 4 Micrometer Coherent and Broadband Sources

Science.gov (United States)

2006-07-24

oxide ( TeO2 ) , fluorine- containing silicate (SiOF2) and germanate (GeOF2) glass hosts for each dopant by characterising the spectroscopic properties...Earth Oxide Ion (Tm3+, Ho3+, And U3+) Doped Glasses And Fibres For 1.8 To 4 Micrometer Coherent And Broadband Sources 5c. PROGRAM ELEMENT NUMBER 5d...Rare-earth oxide ion (Tm3+, Ho3+, and U3+) doped glasses and fibres for 1.8 to 4 micrometer coherent and broadband sources Report prepared

Low-temperature liquid-phase epitaxy and optical waveguiding of rare-earth-ion-doped KY(WO4)2 thin layers

NARCIS (Netherlands)

Romanyuk, Y.E.; Utke, I.; Ehrentraut, D.; Apostolopoulos, V.; Pollnau, Markus; Garcia-Revilla, S.; Valiente, B.

2004-01-01

Crystalline $KY(WO_{4})_{2}$ thin layers doped with different rare-earth ions were grown on b-oriented, undoped $KY(WO_{4})_{2}$ substrates by liquid-phase epitaxy employing a low-temperature flux. The ternary chloride mixture of NaCl, KCl, and CsCl with a melting point of 480°C was used as a

Rare-earth-doped fluorozirconate fiber lasers

International Nuclear Information System (INIS)

Brierly, M.C.; France, P.W.; Moore, M.W.; Davey, S.T.

1988-01-01

Rare-earth-doped fiber lasers fabricated using silica-based fibers are rapidly becoming an established technology. Simultaneously, in the search for lower losses to achieve longer repeaterless communications links, another fiber technology based on fluorozirconate glasses is emerging. Fluorozirconate glass systems are known to be suitable laser hosts, and the authors have already reported Nd-doped fiber lasers using this technology. Recently the authors have used a 0.5-m length of 44-μm core fluorozirconate fiber doped with 1000 ppm of Nd 3+ ions in a longitudinally pumped Fabry-Perot cavity with a 90% output coupler. They observed lasing at 1.05 μm with a threshold of 33-mW launched power at 514 nm and a slope efficiency of 16.8%. The authors attribute this improvement to the higher dopant concentration, better fiber to mirror coupling, and more optimum output coupler reflectivity. In addition the same fiber used with two high-reflector mirrors at 1.35μm produced lasing at 1.35μm with a threshold of 60-mW launched power

Improving soft magnetic properties of Mn-Zn ferrite by rare earth ions doping

Science.gov (United States)

Zhong, X. C.; Guo, X. J.; Zou, S. Y.; Yu, H. Y.; Liu, Z. W.; Zhang, Y. F.; Wang, K. X.

2018-04-01

Mn-Zn ferrites doped with different Sm2O3, Gd2O3, Ce2O3 or Y2O3 were prepared by traditional ceramic technology using industrial pre-sintered powders. A small amount of Sm2O3, Gd2O3, Ce2O3 or Y2O3 can significantly improve the microstructure and magnetic properties. The single spinel phase structure can be maintained with the doping amount up to 0.07 wt.%. A refined grain structure and uniform grain size distribution can be obtained by doping. For all rare earth oxides, a small amount of doping can significantly increase the permeability and reduce the coercivity and magnetic core loss. The optimized doping amount for Sm2O3 or Gd2O3 is 0.01 wt.%, while for Ce2O3 or Y2O3 is 0.03 wt.%. A further increase of the doping content will lead to reduced soft magnetic properties. The ferrite sample with 0.01 wt.% Sm2O3 exhibits the good magnetic properties with permeability, loss, and coercivity of 2586, 316 W/kg, and 24A/m, respectively, at 200 mT and 100 kHz. The present results indicate that rare earth doping can be suggested to be one of the effective ways to improve the performance of soft ferrites.

Improving soft magnetic properties of Mn-Zn ferrite by rare earth ions doping

Directory of Open Access Journals (Sweden)

X. C. Zhong

2018-04-01

Full Text Available Mn-Zn ferrites doped with different Sm2O3, Gd2O3, Ce2O3 or Y2O3 were prepared by traditional ceramic technology using industrial pre-sintered powders. A small amount of Sm2O3, Gd2O3, Ce2O3 or Y2O3 can significantly improve the microstructure and magnetic properties. The single spinel phase structure can be maintained with the doping amount up to 0.07 wt.%. A refined grain structure and uniform grain size distribution can be obtained by doping. For all rare earth oxides, a small amount of doping can significantly increase the permeability and reduce the coercivity and magnetic core loss. The optimized doping amount for Sm2O3 or Gd2O3 is 0.01 wt.%, while for Ce2O3 or Y2O3 is 0.03 wt.%. A further increase of the doping content will lead to reduced soft magnetic properties. The ferrite sample with 0.01 wt.% Sm2O3 exhibits the good magnetic properties with permeability, loss, and coercivity of 2586, 316 W/kg, and 24A/m, respectively, at 200 mT and 100 kHz. The present results indicate that rare earth doping can be suggested to be one of the effective ways to improve the performance of soft ferrites.

Synthesis and sorption properties of new synthesized rare-earth-doped sodium titanate

International Nuclear Information System (INIS)

Ali, I.M.

2010-01-01

A series of rare-earth-doped sodium titanates with the chemical formula R x H y Na 4-(x+y) TiO 4 ·nH 2 O (where R = Ce 3+ , Nd 3+ and Sm 3+ ) were grown employing solid-state fusion reaction technique. The physico-chemical investigations indicated that the new materials were self engineered into large particles enough to be used in sorption process and having crystalline structures containing localized Na + ions. Equilibrium studies revealed that an enhancement in sorption efficiency of sodium titanate after rare-earth doping. The neodymium-rich sodium titanate exhibited a better exchange affinity for Cs + compared to the other studied series. Data on the kinetics of cesium exchange fit well to pseudo-second order and intra-particle diffusion models. In a separate experiment, it was reported that the R-HNaTi series showed responsible sorption affinity toward Ce, Nd and Sm ions in their solution mixture with insignificant selectivity trend which reflects the high stability of titanate matrices. (author)

Fluorescence yield in rare-earth-doped sol-gel silicate glasses

Energy Technology Data Exchange (ETDEWEB)

Silversmith, A.J., E-mail: asilvers@hamilton.ed [Physics Department, Hamilton College, 198 College Hill Road, Clinton, NY 13323 (United States); Nguyen, Nguyen T.T.; Campbell, D.L. [Physics Department, Hamilton College, 198 College Hill Road, Clinton, NY 13323 (United States); Boye, D.M.; Ortiz, C.P. [Davidson College, Davidson, NC 28035 (United States); Hoffman, K.R. [Whitman College, Walla Walla, WA 99362 (United States)

2009-12-15

We have used trivalent terbium to investigate the mechanism behind fluorescence enhancement by Al{sup 3+} co-doping. Our results indicate that rare-earth (RE) ions cluster together in aluminum-rich regions of the glass, and behave as if they were dispersed uniformly throughout these regions when the ratio of Al to RE is {approx}10 or greater. We also studied the effects of adding chemical drying agents to the precursor solution for the synthesis of sol-gel-derived silicate glasses. Such glasses can be treated at significantly higher annealing temperatures without degradation of optical quality, and have the density of melt glass. Fluorescence yield from doped RE ions improves markedly with the addition of the drying agents, and the denser glasses are not subject to rehydration.

Absorption spectroscopy of complex rare earth ion doped hybrid materials over a broad wavelength range

OpenAIRE

Dekker, R.; Worhoff, Kerstin; Stouwdam, J.W.; van Veggel, F.C.J.M.; Driessen, A.

2005-01-01

In the present work we applied a measurement setup to determine several relevant properties of rare-earth doped nanoparticles dispersed in polymer slab waveguides in a single absorption measurement: background absorption of the polymer host material, water absorption, polymer composition (overtones), rare earth concentration, and ligand contribution (increase of exponential loss trend in the UV). Furthermore, nanoparticle size and concentration in case of a refractive index mismatch (1//spl l...

Guided mode cutoff in rare-earth doped rod-type PCFs

DEFF Research Database (Denmark)

Poli, F.; Cucinotta, A.; Passaro, D.

2008-01-01

Guided mode properties of rare-earth doped photonic crystal fibers are investigated as a function of the core refractive index, showing the possibility to obtain cutoff at low normalized wavelength.......Guided mode properties of rare-earth doped photonic crystal fibers are investigated as a function of the core refractive index, showing the possibility to obtain cutoff at low normalized wavelength....

Fatigue Resistance of Filled NR with PMMA-Wrapped and Rare Earth-Doped Alumina-Siloxane Gel

Institute of Scientific and Technical Information of China (English)

无

2002-01-01

Poly (methyl methacrylate) (PMMA) was used to wrap alumina-siloxane sol which was produced by water glass, aluminum nitrate and α-methacrylic acid, and as a result, alumina-siloxane gel wrapped by PMMA was obtained. Meanwhile, rare earth ions were employed to dope in the course of reaction, and the formed rare earth doped PMMA microcapsule powder was filled into natural rubber (NR). It is found through the analysis of mechanical properties that Young′s modulus universally improves and a remarkable resistance to fatigue is displayed. Retention rate of tensile strength is twice that of the controlled sample after ten thousand times of extension fatigue.

Use of thulium-sensitized rare earth-doped low phonon energy crystalline hosts for IR sources.

Science.gov (United States)

Ganem, Joseph; Bowman, Steven R

2013-11-01

Crystalline hosts with low phonon energies enable novel energy transfer processes when doped with rare earth ions. Two applications of energy transfer for rare earth ions in thulium-sensitized low phonon energy crystals that result in infrared luminescence are discussed. One application is an endothermic, phonon-assisted cross-relaxation process in thulium-doped yttrium chloride that converts lattice phonons to infrared emission, which raises the possibility of a fundamentally new method for achieving solid-state optical cooling. The other application is an optically pumped mid-IR phosphor using thulium-praseodymium-doped potassium lead chloride that converts 805-nm diode light to broadband emission from 4,000 to 5,500 nm. These two applications in chloride crystals are discussed in terms of critical radii calculated from Forster-Dexter energy transfer theory. It is found that the critical radii for electric dipole-dipole interactions in low phonon energy chloride crystals are comparable to those in conventional oxide and fluoride crystals. It is the reduction in multi-phonon relaxation rates in chloride crystals that enable these additional energy transfer processes and infrared luminescence.

Synthesis of three-dimensional rare-earth ions doped CNTs-GO-Fe3O4 hybrid structures using one-pot hydrothermal method

International Nuclear Information System (INIS)

Gao, Guo; Zhang, Qiang; Cheng, Xin-Bing; Sun, Rongjin; Shapter, Joseph G.; Yin, Ting; Cui, Daxiang

2015-01-01

Rechargeable lithium ion batteries (LIBs) are currently the dominant power source for all sorts of electronic devices due to their low cost and high energy density. The cycling stability of LIBs is significantly compromised due to the broad satellite peak for many anode materials. Herein, we develop a facile hydrothermal process for preparing rare-earth (Er, Tm) ions doped three-dimensional (3D) transition metal oxides/carbon hybrid nanocomposites, namely CNTs-GO-Fe 3 O 4 , CNTs-GO-Fe 3 O 4 -Er and CNTs-GO-Fe 3 O 4 -Tm. The GO sheets and CNTs are interlinked by ultrafine Fe 3 O 4 nanoparticles forming three-dimensional (3D) architectures. When evaluated as anode materials for LIBs, the CNTs-GO-Fe 3 O 4 hybrid composites have a bigger broad satellite peak. As for the CNTs-GO-Fe 3 O 4 -Er and CNTs-GO-Fe 3 O 4 -Tm hybrid composites, the broad satellite peak can be completely eliminated. When the current density changes from 5 C back to 0.1 C, the capacity of CNTs-GO-Fe 3 O 4 -Tm hybrid composites can recover to 1023.9 mAhg −1 , indicating an acceptable rate capability. EIS tests show that the charge transfer resistance does not change significantly after 500 cycles, demonstrating that the cycling stability of CNTs-GO-Fe 3 O 4 -Tm hybrid composites are superior to CNTs-GO-Fe 3 O 4 and CNTs-GO-Fe 3 O 4 -Er hybrid structures. - Graphical abstract: One-pot hydrothermal method for synthesis of rare-earth ions doped CNTs-GO-Fe 3 O 4 hybrid structures as anode materials of LIBs have been reported. - Highlights: • We report the synthesis of rare-earth ions doped CNTs-GO-Fe 3 O 4 hybrid structures. • The hybrid structures can improve the cycling stability of lithium storage. • As for anode materials, the broad satellite peak can be completely eliminated. • When the rate return back to 0.1 C, the capacity can recover to 1023.9 mAhg −1 . • After 500 cycles, the hybrid structures still exhibited excellent cycling stability

Changes of fluorescent spectral features after successive rare earth doping of gadolinium oxide powders

Energy Technology Data Exchange (ETDEWEB)

Kuznik, W. [Chemical Department, Silesian University of Technology, Gliwice (Poland); Institute of Physics, University of Tartu, Riia 142, Tartu 51014 (Estonia); Brik, M.G. [Institute of Physics, University of Tartu, Riia 142, Tartu 51014 (Estonia); Cieslik, I.; Majchrowski, A.; Jaroszewicz, L. [Institute of Applied Physics, Military University of Technology, Kaliskiego 2, 00-908 Warsaw (Poland); AlZayed, N.S. [Physics and Astronomy Dept., College of Science, P.O. Box 2455, King Saud University, Riyadh 11451 (Saudi Arabia); El-Naggar, A.M. [Physics and Astronomy Dept., College of Science, P.O. Box 2455, King Saud University, Riyadh 11451 (Saudi Arabia); Permanent address: Physics department, Faculty of Science, Ain Shams University, Abassia, Cairo 11566 (Egypt); Sildos, I.; Lange, S.; Kiisk, V. [Institute of Physics, University of Tartu, Riia 142, Tartu 51014 (Estonia); Kityk, I.V., E-mail: ikityk@el.pcz.czest.pl [Electrical Engineering Department, Czestochowa University of Technology, Armii Krajowej 17, Czestochowa (Poland); Physics and Astronomy Dept., College of Science, P.O. Box 2455, King Saud University, Riyadh 11451 (Saudi Arabia)

2012-01-15

Highlights: > Principally new phosphors based on rare earth moped Gd{sub 2}O{sub 3} are obtained. > The time-resolved fluorescent spectra show drastic changes with the doping. > Temperature measurements were done. - Abstract: We present a complex fluorescence study of a series of gadolinium oxide polycrystalline powders singly, doubly and triply doped with trivalent rare earth ions (Er{sup 3+}, Tb{sup 3+}, and Dy{sup 3+}), to explore a possibility of their use as materials for white light emitting diodes. The excitation and luminescence spectra along with the decay kinetics were measured in the temperature range from 6 to 300 K. The luminescence efficiency was studied within the visible spectral range, i.e. -400 nm to 750 nm under excitation by 355 nm third harmonic Nd:YAG laser pulses. Singly doped Er{sup 3+} sample gave stronger luminescence signals, but others showed significantly larger decay lifetimes. The successive rare earths doping leads to substantial changes of the spectral positions due to the up-conversion processes. In the singly (Er{sup 3+}) doped sample, following the time resolved spectrum and decay curves, there are two different types of emissions: at 660 nm and at shorter wavelengths (below 640 nm) the red emission's lifetime is ten times longer than at shorter wavelengths. The singly doped sample shows unclear temperature-dependence of luminescence with lifetime at 550 nm (the longest at 100 K, similarly at 6 K and 300 K) and achieved luminous efficacy 73.5 lm/W.

Low-temperature photoluminescence in chalcogenide glasses doped with rare-earth ions

Czech Academy of Sciences Publication Activity Database

Kostka, Petr; Zavadil, Jiří; Iovu, M.S.; Ivanova, Z. G.; Furniss, D.; Seddon, A.B.

2015-01-01

Roč. 648, NOV 5 (2015), s. 237-243 ISSN 0925-8388 R&D Projects: GA ČR GAP106/12/2384 Institutional support: RVO:67985891 ; RVO:67985882 Keywords : chalcogenide glasses * rare earth ions * low-temperature photoluminescence * optical transmission Subject RIV: JH - Ceramics, Fire-Resistant Materials and Glass Impact factor: 3.014, year: 2015

Absorption spectroscopy of complex rare earth ion doped hybrid materials over a broad wavelength range

NARCIS (Netherlands)

Dekker, R.; Worhoff, Kerstin; Stouwdam, J.W.; van Veggel, F.C.J.M.; Driessen, A.

2005-01-01

In the present work we applied a measurement setup to determine several relevant properties of rare-earth doped nanoparticles dispersed in polymer slab waveguides in a single absorption measurement: background absorption of the polymer host material, water absorption, polymer composition

Absorption spectroscopy of complex rare earth ion doped hybrid materials over a broad wavelength range

NARCIS (Netherlands)

Dekker, R.; Worhoff, Kerstin; Stouwdam, J.W.; van Veggel, F.C.J.M.; Driessen, A.

In the present work we applied a measurement setup to determine several relevant properties of rare-earth doped nanoparticles dispersed in polymer slab waveguides in a single absorption measurement: background absorption of the polymer host material, water absorption, polymer composition

Observation of coherent population transfer in a four-level tripod system with a rare-earth-metal-ion-doped crystal

International Nuclear Information System (INIS)

Goto, Hayato; Ichimura, Kouichi

2007-01-01

Coherent population transfer in a laser-driven four-level system in a tripod configuration is experimentally investigated with a rare-earth-metal-ion-doped crystal (Pr 3+ :Y 2 SiO 5 ). The population transfers observed here indicate that a main process inducing them is not optical pumping, which is an incoherent process inducing population transfer. Moreover, numerical simulation, which well reproduces the experimental results, also shows that the process inducing the observed population transfers is similar to stimulated Raman adiabatic passage (STIRAP) in the sense that this process possesses characteristic features of STIRAP

Intense luminescence emission from rare-earth-doped MoO3 nanoplates and lamellar crystals for optoelectronic applications

International Nuclear Information System (INIS)

Vila, M; Díaz-Guerra, C; Jerez, D; Piqueras, J; Lorenz, K; Alves, E

2014-01-01

Strong and stable room-temperature photoluminescence (PL) emission is achieved in MoO 3 nanoplates and lamellar crystals doped with Er and Eu by ion implantation and subsequent annealing. Micro-Raman and PL spectroscopy reveal that optical activation of the rare earth ions and recovery of the original MoO 3 structure are achieved for shorter annealing treatments and for lower temperatures in nanoplates, as compared with lamellar crystals. Er seems to be more readily incorporated into optically active sites in the oxide lattice than Eu. The influence of the dimensionality of the host sample on the characteristics of the PL emission of both rare earth dopants is addressed. (paper)

Structural properties of lithium borate glasses doped with rare earth ions

Directory of Open Access Journals (Sweden)

Thomazini D.

2001-01-01

Full Text Available This paper presents the study on lithium triborate glass (LBO in the system (1-x|3B2O3.Li2O| (xNb2O5 yPr3+ zYb3+ wNd3+ with 0 <= x <= 20 mol% (y, z and w in mol%. The samples were studied by Raman spectroscopy, infrared absorption and differential thermal analysis. Pr3+-doped LBO and Pr3+/Yb3+-doped LBO samples show an increase of the glass transition and crystallization temperatures and a decrease of the fusion temperature associated with the increase of the praseodymium concentration in the LBO matrix. For the Nd3+-doped LBO and Pr3+/Yb3+-doped (LBO+Nb2O5 samples, a decrease of the glass transition temperature of the samples was observed. The increase of the rare earth doping leads to an increase of the difference between the glass transition and the crystallization temperatures. From infrared analysis it was possible to identify all the modes associated to the B-O structure. The NbO6 octahedra was also identified by IR spectroscopy for samples with x=5, 10, 15 and 20 mol% and y=0.05, z=1.1 mol%. Raman spectroscopy shows the presence of boroxol rings, tetrahedral and triangular coordination for boron. For samples containing niobium, the Raman spectra show the vibrational mode associated with the Nb-O bond in the niobium octahedra (NbO6.

Application of lanthanide ions doped in different glasses

International Nuclear Information System (INIS)

Dhondiyal, Charu Chandra

2015-01-01

The transfer of optical excitation energy from one ion/molecule to another ion/molecule has proved to be of potential importance in industrial application as well as research. Rare earth elements (RE) although not as rare as some of them occur more prevalently then other well known material (e.g. silver, tin, tungsten) are special group of elements of the periodic table comprising lanthanide series (from lanthanum to lutetium) and actinide series (from actinium to lawrencium). Most of the actinides are highly radioactive hence their uses are limited. Fluorescence is the particular optical property of lanthanide (RE) ions. The narrow absorption and emission lines exhibited by the RE ions in crystals, glasses and solutions have always made these ions attractive as sensitive probes of solids and liquid state and also makes them useful in laser technology, CRT displays, UV to visible converters and optical communications etc. In recent years there has been a special interest to study the properties and applications of rare earth doped in glasses. Lanthanide ions in glasses play an important role, especially by retaining their emission capabilities, in the host matrix. Glass as a dielectric material plays an important role in science and industry. Its chemical, physical and particular optical properties make it suitable for applications such as opto-electronic materials, laboratory equipment, laser gain media, etc. Photoluminescence from rare earth doped glasses are of major interest in the research area of optoelectronic device applications like phosphors, display monitors, lasers and amplifiers for communication systems. Now a days, development of optical devices based on rare-earth ions doped materials is one of the interesting fields of research. Rare earth doped glasses are widely used as laser materials, optical amplifiers, optical memory devices, magneto-optical devices, medical lasers, eye safe lasers, flat panel displays, fluorescent lamps, white LED's etc

Rare earths: harvesting basic research for technology

International Nuclear Information System (INIS)

Jagatap, B.N.

2014-01-01

In recent years, rare earths are increasingly becoming a versatile platform for basic research that presents enormous technological potentials. A variety of nano-sized inorganic matrices varying from oxides, phosphates, gallates and aluminates, tungstates, stannates, vanadates to fluorides doped with different lanthanide ions have been synthesized and their optical properties have been investigated in the Chemistry Group, BARC. Another interesting application is laser cooling of solids using rare earth doped glasses with potential applications in remote cooling of electronic devices. Combining the luminescence properties of rare earths with photonic crystals is yet another potent area with wide ranging applications. In this presentation we provide an overview of these developments with examples from the R and D programs of the Chemistry Group, BARC

Microstructure and mechanical properties of multi-components rare earth oxide-doped molybdenum alloys

International Nuclear Information System (INIS)

Zhang Guojun; Sun Yuanjun; Zuo Chao; Wei Jianfeng; Sun Jun

2008-01-01

Pure molybdenum and molybdenum alloys doped with two- or three-components rare earth oxide particles were prepared by powder metallurgy. Both the tensile property and fracture toughness of the pure molybdenum and multi-components rare earth oxide-doped molybdenum alloys were determined at room temperature. The multi-components rare earth oxide-doped molybdenum alloys are fine grained and contain a homogeneous distribution of fine particles in the submicron and nanometer size ranges, which is why the molybdenum alloys have higher strength and fracture toughness than pure molybdenum. Quantitative analysis is used to explain the increase in yield strength with respect to grain size and second phase strengthening. Furthermore, the relationship between the tensile properties and microstructural parameters is quantitatively established

Study of amorphous semiconductors doped with rare earths (Gd and Er) and conducting polymers by EPR techniques and magnetic susceptibility

International Nuclear Information System (INIS)

Sercheli, Mauricio da Silva

1999-01-01

This thesis involves the study of amorphous semiconductors and conducting polymers, which have been characterized by EPR and magnetic susceptibility measurements, and to a lesser extent by Raman spectroscopy and RBS. The semiconductors were studied using thin films of silicon doped with rare earth metals, e.g. erbium and gadolinium, which had their magnetic properties studied. Using these studies we could determine the state of valence of the rare earths as well as their concentrations in the silicon matrix. According to our results, the valence of the rare earth metal ions is 3+, and we were able to conclude that 4f electronic shells could not be used for the calculation of the conducting band in this system. Furthermore, the analysis of the data on the magnetic susceptibility of the Er 3+ ion with cubic crystalline acting field, gave us the opportunity to estimate the overall splitting of their electronic states for the first time. The conducting polymers were studied using samples of poly(3-methylthiophene) doped with ClO 4 - , which show a phase transition in the range of 230 K to 130 K. The electron paramagnetic resonance also gives important information on the crystallization, doping level and the presence of polarons or bipolarons in conducting polymers. (author)

Synthesis, structural and optical properties of pure and rare-earth ion doped TiO{sub 2} nanowire arrays by a facile hydrothermal technique

Energy Technology Data Exchange (ETDEWEB)

Bandi, Vengala Rao; Raghavan, Chinnambedu Murugesan; Grandhe, Bhaskar kumar; Kim, Sang Su [Department of Physics, Changwon National University, Changwon 641-773 (Korea, Republic of); Jang, Kiwan, E-mail: kwjang@changwon.ac.kr [Department of Physics, Changwon National University, Changwon 641-773 (Korea, Republic of); Shin, Dong-Soo [Department of Chemistry, Changwon National University, Changwon 641-773 (Korea, Republic of); Yi, Soung-Soo [Department of Photonics, Silla University, Busan 617-736 (Korea, Republic of); Jeong, Jung-Hyun [Department of Physics, Pukyong National University, Busan 608-737 (Korea, Republic of)

2013-11-29

Single crystalline pure and rare-earth metal ions (Eu{sup 3+} and Ce{sup 3+}) doped TiO{sub 2} nanowire arrays were prepared on conductive fluorine doped indium tin oxide substrates by a facile hydrothermal method. Initially the conditions and parameters were optimized to prepare the high quality TiO{sub 2} nanowire arrays in the absence of organic additives. The average diameter and length of the TiO{sub 2} nanowire were found to be ∼ 30–50 nm and ∼ 0.5–1.5 μm, respectively. The formations of rutile phase structure in all the samples were confirmed by x-ray diffractometric analysis while the transmission electron microscopy confirms the single crystallinity and the maximum orientation of growth direction along [001] for the as-grown TiO{sub 2} nanowire. The optical properties of all the samples were analyzed using photoluminescence spectroscopy. The photocatalytic properties of the pure and doped TiO{sub 2} were investigated for the decomposition of organic toludine blue-O dye under ultraviolet irradiation. The result demonstrates that the Ce{sup 3+}: TiO{sub 2} decomposed almost 90% of the organic dye within 80 min. - Highlights: • Rare-earth (RE) doped TiO{sub 2} nanowire arrays were prepared by hydrothermal method • RE doping enhanced the growth rate of TiO{sub 2} nanowire arrays • The catalysts used to check their photocatalytic activity by toludine blue-O dye • RE doped TiO2 act as unprecedented photocatalyst for organic dye decomposition.

Effect of doping rare earths on magnetostriction characteristics of CoFe2O4 prepared from spent Li-ion batteries

Science.gov (United States)

Xi, Guoxi; Zhao, Tingting; Wang, Lu; Dun, Changwei; Zhang, Ye

2018-04-01

Recovering spent Li-ion batteries is beneficial to the economy and environment. Therefore, this study synthesized nanoparticles of cobalt ferrite doped with different rare earth ions (Nd, Ce, and Pr) by a sol-gel auto-combustion method using spent Li-ion batteries. The effect of the different doping elements on grain sizes, structure, magnetic and magnetostrictive properties, and strain derivative were confirmed by X-ray diffraction, scanning election microscopy, vibrating sample magnetometer, and a magnetostrictive coefficient measuring system. Substitution of a small amount of Fe3+ with RE3+ in CoRExFe2-xO4 (x = 0.025, 0.05, and 0.1) had a large effect on magnetostrictive properties and strain derivative, which was improved compared with pure cobalt ferrite at low magnetic field. The maximum strain derivative (dλ/dH = -1.49 × 10-9 A-1 m at 18 kA m-1) was obtained for Nd, x = 0.05. Changes in the magnetostriction coefficients and strain derivatives were correlated with changes in cation distribution, microstructure, and magnetic anisotropy, which depended strongly on RE3+ substitution and distribution in the spinel structure.

Optical and structural characterization of rare earth doped niobium phosphate glasses

International Nuclear Information System (INIS)

Sene, F.F.; Martinelli, J.R.; Gomes, L.

2004-01-01

Phosphate glasses containing up to 45mol% of niobium were obtained. X-ray diffraction, infrared, Raman, and optical absorption spectroscopy were used to analyze those materials. The refractive index varies from 1.70 to 1.85 as the amount of Nb increases. Niobium phosphate glasses with optical transparence in the (400-2500nm) range were produced. The cut off varied from 342nm to 378nm as a function of the Nb concentration. The cut off is due to the charge transfer O 2 ->Nb 5+ . Glasses containing 10mol% of Nb 2 O 5 are the most promising materials to be used as rare-earth ions hosts because they are chemically resistant, and show optical transparency in the spectral range of visible to infrared. Doping the glasses with 1-5mol% of Er, Ho, Pr, and Yb ions does not change the glass structure, as measured by X-ray diffraction, infrared, and Raman spectroscopy. The fluorescence lifetimes were determined for Nd, Yb, and Er, and the absorption cross-section were determined for all ions. The energy transfer in co-doped Yb-Er system was measured, and the lifetime of excited states and the luminescence efficiency were determined to be 91% for the Er 4 I 11/2 level, in the Yb-Er co-doped glasses

Synthesis of three-dimensional rare-earth ions doped CNTs-GO-Fe{sub 3}O{sub 4} hybrid structures using one-pot hydrothermal method

Energy Technology Data Exchange (ETDEWEB)

Gao, Guo, E-mail: guogao@sjtu.edu.cn [Institute of Nano Biomedicine and Engineering, Department of Instrument Science and Technology, Key Laboratory for Thin Film and Microfabrication Technology of Ministry of Education, School of Electronic Information and Electrical Engineering, Shanghai Jiao Tong University, Shanghai 200240 (China); Zhang, Qiang; Cheng, Xin-Bing [Beijing Key Laboratory of Green Chemical Reaction Engineering and Technology, Department of Chemical Engineering, Tsinghua University, Beijing 100084 (China); Sun, Rongjin [Institute of Nano Biomedicine and Engineering, Department of Instrument Science and Technology, Key Laboratory for Thin Film and Microfabrication Technology of Ministry of Education, School of Electronic Information and Electrical Engineering, Shanghai Jiao Tong University, Shanghai 200240 (China); Shapter, Joseph G., E-mail: joe.shapter@flinders.edu.au [School of Chemical and Physical Sciences, Flinders University, Bedford Park, Adelaide 5042 (Australia); Yin, Ting [Institute of Nano Biomedicine and Engineering, Department of Instrument Science and Technology, Key Laboratory for Thin Film and Microfabrication Technology of Ministry of Education, School of Electronic Information and Electrical Engineering, Shanghai Jiao Tong University, Shanghai 200240 (China); Cui, Daxiang, E-mail: dxcui@sjtu.edu.cn [Institute of Nano Biomedicine and Engineering, Department of Instrument Science and Technology, Key Laboratory for Thin Film and Microfabrication Technology of Ministry of Education, School of Electronic Information and Electrical Engineering, Shanghai Jiao Tong University, Shanghai 200240 (China)

2015-11-15

Rechargeable lithium ion batteries (LIBs) are currently the dominant power source for all sorts of electronic devices due to their low cost and high energy density. The cycling stability of LIBs is significantly compromised due to the broad satellite peak for many anode materials. Herein, we develop a facile hydrothermal process for preparing rare-earth (Er, Tm) ions doped three-dimensional (3D) transition metal oxides/carbon hybrid nanocomposites, namely CNTs-GO-Fe{sub 3}O{sub 4}, CNTs-GO-Fe{sub 3}O{sub 4}-Er and CNTs-GO-Fe{sub 3}O{sub 4}-Tm. The GO sheets and CNTs are interlinked by ultrafine Fe{sub 3}O{sub 4} nanoparticles forming three-dimensional (3D) architectures. When evaluated as anode materials for LIBs, the CNTs-GO-Fe{sub 3}O{sub 4} hybrid composites have a bigger broad satellite peak. As for the CNTs-GO-Fe{sub 3}O{sub 4}-Er and CNTs-GO-Fe{sub 3}O{sub 4}-Tm hybrid composites, the broad satellite peak can be completely eliminated. When the current density changes from 5 C back to 0.1 C, the capacity of CNTs-GO-Fe{sub 3}O{sub 4}-Tm hybrid composites can recover to 1023.9 mAhg{sup −1}, indicating an acceptable rate capability. EIS tests show that the charge transfer resistance does not change significantly after 500 cycles, demonstrating that the cycling stability of CNTs-GO-Fe{sub 3}O{sub 4}-Tm hybrid composites are superior to CNTs-GO-Fe{sub 3}O{sub 4} and CNTs-GO-Fe{sub 3}O{sub 4}-Er hybrid structures. - Graphical abstract: One-pot hydrothermal method for synthesis of rare-earth ions doped CNTs-GO-Fe{sub 3}O{sub 4} hybrid structures as anode materials of LIBs have been reported. - Highlights: • We report the synthesis of rare-earth ions doped CNTs-GO-Fe{sub 3}O{sub 4} hybrid structures. • The hybrid structures can improve the cycling stability of lithium storage. • As for anode materials, the broad satellite peak can be completely eliminated. • When the rate return back to 0.1 C, the capacity can recover to 1023.9 mAhg{sup −1}. • After 500

Rare earth point defects in GaN

Energy Technology Data Exchange (ETDEWEB)

Sanna, S.

2007-12-14

In this work we investigate rare earth doped GaN, by means of theoretical simulations. The huge unit cells necessary to model the experimental system, where dilute amount of rare earth ions are used, are handled with the charge self consistent density-functional based-tight binding (SCC-DFTB) calculational scheme. The method has been extended to include LDA+U and simplified self interaction corrected (SIC)-like potentials for the simulation of systems with localised and strongly correlated electrons. A set of tight-binding parameters has been created to model the interaction of GaN with some dopants, including a selection of lanthanide ions interesting due to their optical or magnetic properties (Pr, Eu, Gd, Er and Tm). The f-electrons were treated as valence electrons. A qualitatively correct description of the band gap is crucial for the simulation of rare earth doped GaN, because the luminescence intensity of the implanted samples depends on the size of the host band gap and because the rare earths could introduce charge transition levels near the conduction band. In this work these levels are calculated with the Slater-Janak (SJ) transition state model, which allows an approximate calculation of the charge transition levels by analysing the Kohn-Sham eigenvalues of the DFT. (orig.)

Rare Earth Garnet Selective Emitter

Science.gov (United States)

Lowe, Roland A.; Chubb, Donald L.; Farmer, Serene C.; Good, Brian S.

1994-01-01

impurities, in the development of solid state laser crystals. Doping, dependent on the particular ion and crystal structure, may be as high as 100 at. % (complete substitution of yttrium ion with the rare earth ion). These materials have high melting points, 1940 C for YAG (Yttrium Aluminum Garnet), and low emissivity in the near infrared making them excellent candidates for a thin film selective emitter. As previously stated, the spectral emittance of a rare earth emitter is characterized by one or more well defined emission bands. Outside the emission band the emittance(absorptance) is much lower. Therefore, it is expected that emission outside the band for a thin film selective emitter will be dominated by the emitter substrate. For an efficient emitter (power in the emission band/total emitted power) the substrate must have low emittance, epsilon(sub S). This paper presents normal spectral emittance, epsilon(sub lambda), measurements of holmium(Ho) and erbium (Er) doped YAG thin film selective emitters at (1500 K), and compares those results with the theoretical spectral emittance.

Sensing using rare-earth-doped upconversion nanoparticles.

Science.gov (United States)

Hao, Shuwei; Chen, Guanying; Yang, Chunhui

2013-01-01

Optical sensing plays an important role in theranostics due to its capability to detect hint biochemical entities or molecular targets as well as to precisely monitor specific fundamental psychological processes. Rare-earth (RE) doped upconversion nanoparticles (UCNPs) are promising for these endeavors due to their unique frequency converting capability; they emit efficient and sharp visible or ultraviolet (UV) luminescence via use of ladder-like energy levels of RE ions when excited at near infrared (NIR) light that are silent to tissues. These features allow not only a high penetration depth in biological tissues but also a high detection sensitivity. Indeed, the energy transfer between UCNPs and biomolecular or chemical indicators provide opportunities for high-sensitive bio- and chemical-sensing. A temperature-sensitive change of the intensity ratio between two close UC bands promises them for use in temperature mapping of a single living cell. In this work, we review recent investigations on using UCNPs for the detection of biomolecules (avidin, ATP, etc.), ions (cyanide, mecury, etc.), small gas molecules (oxygen, carbon dioxide, ammonia, etc.), as well as for in vitro temperature sensing. We also briefly summarize chemical methods in synthesizing UCNPs of high efficiency that are important for the detection limit.

Strong broad green UV-excited photoluminescence in rare earth (RE = Ce, Eu, Dy, Er, Yb) doped barium zirconate

Energy Technology Data Exchange (ETDEWEB)

Borja-Urby, R. [Grupo de Espectroscopia de Materiales Avanzados y Nanoestructurados (EMANA), Centro de Investigaciones en Optica A. C., Leon, Gto. 37150 (Mexico); Diaz-Torres, L.A., E-mail: ditlacio@cio.mx [Grupo de Espectroscopia de Materiales Avanzados y Nanoestructurados (EMANA), Centro de Investigaciones en Optica A. C., Leon, Gto. 37150 (Mexico); Salas, P. [Centro de Fisica Aplicada y Tecnologia Avanzada, Universidad Nacional Autonoma de Mexico, A.P. 1-1010, Queretaro, Qro. 76000 (Mexico); Angeles-Chavez, C. [Instituto Mexicano del Petroleo, Ciudad de Mexico, D. F. 07730 (Mexico); Meza, O. [Grupo de Espectroscopia de Materiales Avanzados y Nanoestructurados (EMANA), Centro de Investigaciones en Optica A. C., Leon, Gto. 37150 (Mexico)

2011-10-25

Highlights: > Trivalent rare earth (RE) substitution on Zr{sup 4+} sites in BaZrO{sub 3} lead to band gap narrowing. > RE substitution lead to enhanced blue-green intrinsic emission of nanocrystalline BaZrO{sub 3} > Blue-green hue of BaZrO3:RE depends on RE dopant and excitation UV wavelength > BaZrO3: Dy{sup 3+} PL chromatic coordinates correspond to pure white color coordinates of CIE 1931 model - Abstract: The wet synthesis hydrothermal method at 100 deg. C was used to elaborate barium zirconate (BaZrO{sub 3}) unpurified with 0.5 mol% of different rare earth ions (RE = Yb, Er, Dy, Eu, Ce). Morphological, structural and UV-photoluminescence properties depend on the substituted rare earth ionic radii. While the crystalline structure of RE doped BaZrO{sub 3} remains as a cubic perovskite for all substituted RE ions, its band gap changes between 4.65 and 4.93 eV. Under 267 nm excitation the intrinsic green photoluminescence of the as synthesized BaZrO{sub 3}: RE samples is considerably improved by the substitution on RE ions. For 1000 deg. C annealed samples, under 267 nm, the photoluminescence is dominated by the intrinsic BZO emission. It is interesting to notice that Dy{sup 3+}, Er{sup 3+} and Yb{sup 3+} doped samples present whitish emissions that might be useful for white light generation under 267 nm excitation. CIE color coordinates are reported for all samples.

Complex formation constant and hydration number change of aqua-rare earth ions

International Nuclear Information System (INIS)

Kanno, H.

1998-01-01

Full text: It is now well established that the inner-sphere hydration number of aqua-rare earth ions changes from nine to eight in the middle of the rare earth series. This hydration number change greatly affects the complex formation of rare earth ions as we observe irregular variations in most series behaviours of the complex formation constant (K) in aqueous solution systems when K being plotted against 1/r or r (r is ionic radius of rare earth ion). Furthermore, it shows very anomalous concentration dependence in the sense that nona-aqua Ln 3+ ion increases in number with increase in salt concentration in aqueous rare earth salt solution (salt chloride, perchlorate). In this report, a theoretical derivation of the formation constant (K) for the inner-sphere complex formation of rare earth ions with a monodentate ligand was made by taking account of both the hydration number change in the middle of the series and its anomalous salt concentration dependence. The series behaviour of the formation constant against 1/r (or r) is successfully explained with using the empirical finding that K varies almost linearly with 1/r (or r) in the region where only one hydration number dominates. This success is also taken as evidence that the anomalous salt concentration dependence of the hydration number change is caused by the outer-sphere complex formation of rare earth ions with the condition that nona-aqua rare earth ions form outer-sphere complexes more easily than octa-aqua ions

Microhardness of epitaxial layers of GaAs doped with rare earths

International Nuclear Information System (INIS)

Kulish, U.M.; Gamidov, Z.S.; Kuznetsova, I.Yu.; Petkeeva, L.N.; Borlikova, G.V.

1989-01-01

Results of the study of microhardness of GaAS layer doped by certain rare earths - Gd, Tb, Dy - are presented. The assumption is made that the higher is the value of the first potential of rare earth impurity ionization (i.e. the higher is the filling of 4f-shell), the lower is the effect of the element on electric and mechanical properties of GaAs epitaxial layers

The electrorheological properties of nano-sized SiO2 particle materials doped with rare earths

International Nuclear Information System (INIS)

Liu Yang; Liao Fuhui; Li Junran; Zhang Shaohua; Chen Shumei; Wei Chenguan; Gao Song

2006-01-01

Electrorheological (ER) materials of pure SiO 2 and SiO 2 doped with rare earths (RE = Ce, Gd, Y) (non-metallic glasses (silicates)) were prepared using Na 2 SiO 3 and RECl 3 as starting materials. The electrorheological properties are not enhanced by all rare earth additions. The material doped with Ce exhibits the best ER performance

Rare-earth doped boron nitride nanotubes: Synthesis and characterization

Energy Technology Data Exchange (ETDEWEB)

Silva, Wellington Marcos; Sousa, Edesia Martins Barros de, E-mail: wellingtonmarcos@yahoo.com.br [Centro de Desenvolvimento da Tecnologia Nuclear (CDTN/CNEN-MG), Belo Horizonte, MG (Brazil)

2016-07-01

Full text: Boron nitride is a heat and chemically resistant refractory compound of boron and nitrogen atoms with the chemical formula BN. This structure exists in various crystalline forms that are isoelectronic to a similarly structured carbon lattice. The hexagonal form (h-BN) corresponding to graphite is the most stable and soft among BN polymorph. However, boron nitride nanotubes (BNNTs) were first time synthesized in 1995 [1] and have a type of one-dimensional (1D) nanostructure. Recently the BNNTs have attracted significant interest for scientific and technological applications due to their Wide bandgap. The Wide-bandgap semiconductors doped with rare-earth are considered as a new type of luminescent material, combining special Wide bandgap semiconducting properties with the rare-earth luminescence feature. BNNTs have a stable wide bandgap of 5.5 eV and super thermal and chemical stabilities, which make BNNTs an ideal nanosized luminescent material [2]. In this study, we report a simple and efficient route for the synthesis of BNNTs doped with samarium and europium. High quality BNNTs doped was produced via CVD technique using NH{sub 3} and N{sub 2} gases as source. Boron amorphous, catalyst and oxides rare-earth powder were used as precursor. Detailed studies involving energy-dispersive X-ray spectroscopy (EDS), X-ray diffraction (XRD), Raman spectroscopy, Fourier-transform infrared spectroscopy (FTIR), scanning electron microscope (SEM) and transmission electron microscope (TEM) were performed in order to characterize the BNNTs as grown. [1] Chopra, N. G.; Luyken, R. J. et al. Science, v. 269, p. 966-967, 1995. [2] Chen, H.; Chen, Y. et al. Adv. Matter. v. 19, p. 1845-1848, 2007. (author)

Rare-earth doped boron nitride nanotubes: Synthesis and characterization

International Nuclear Information System (INIS)

Silva, Wellington Marcos; Sousa, Edesia Martins Barros de

2016-01-01

Full text: Boron nitride is a heat and chemically resistant refractory compound of boron and nitrogen atoms with the chemical formula BN. This structure exists in various crystalline forms that are isoelectronic to a similarly structured carbon lattice. The hexagonal form (h-BN) corresponding to graphite is the most stable and soft among BN polymorph. However, boron nitride nanotubes (BNNTs) were first time synthesized in 1995 [1] and have a type of one-dimensional (1D) nanostructure. Recently the BNNTs have attracted significant interest for scientific and technological applications due to their Wide bandgap. The Wide-bandgap semiconductors doped with rare-earth are considered as a new type of luminescent material, combining special Wide bandgap semiconducting properties with the rare-earth luminescence feature. BNNTs have a stable wide bandgap of 5.5 eV and super thermal and chemical stabilities, which make BNNTs an ideal nanosized luminescent material [2]. In this study, we report a simple and efficient route for the synthesis of BNNTs doped with samarium and europium. High quality BNNTs doped was produced via CVD technique using NH 3 and N 2 gases as source. Boron amorphous, catalyst and oxides rare-earth powder were used as precursor. Detailed studies involving energy-dispersive X-ray spectroscopy (EDS), X-ray diffraction (XRD), Raman spectroscopy, Fourier-transform infrared spectroscopy (FTIR), scanning electron microscope (SEM) and transmission electron microscope (TEM) were performed in order to characterize the BNNTs as grown. [1] Chopra, N. G.; Luyken, R. J. et al. Science, v. 269, p. 966-967, 1995. [2] Chen, H.; Chen, Y. et al. Adv. Matter. v. 19, p. 1845-1848, 2007. (author)

Photo-Induced conductivity of heterojunction GaAs/Rare-Earth doped SnO2

Directory of Open Access Journals (Sweden)

Cristina de Freitas Bueno

2013-01-01

Full Text Available Rare-earth doped (Eu3+ or Ce3+ thin layers of tin dioxide (SnO2 are deposited by the sol-gel-dip-coating technique, along with gallium arsenide (GaAs films, deposited by the resistive evaporation technique. The as-built heterojunction has potential application in optoelectronic devices, because it may combine the emission from the rare-earth-doped transparent oxide, with a high mobility semiconductor. Trivalent rare-earth-doped SnO2 presents very efficient emission in a wide wavelength range, including red (in the case of Eu3+ or blue (Ce3+. The advantage of this structure is the possibility of separation of the rare-earth emission centers, from the electron scattering, leading to an indicated combination for electroluminescence. Electrical characterization of the heterojunction SnO2:Eu/GaAs shows a significant conductivity increase when compared to the conductivity of the individual films. Monochromatic light excitation shows up the role of the most external layer, which may act as a shield (top GaAs, or an ultraviolet light absorber sink (top RE-doped SnO2. The observed improvement on the electrical transport properties is probably related to the formation of short conduction channels in the semiconductors junction with two-dimensional electron gas (2DEG behavior, which are evaluated by excitation with distinct monochromatic light sources, where the samples are deposited by varying the order of layer deposition.

Influence of rare-earth ions on fluorogallate glass formation and properties

International Nuclear Information System (INIS)

Zhang Guoyin; Poulain, M.J.

1998-01-01

Various rare earths have been incorporated in a lead fluorogallate glass with the following chemical composition: 30PbF 2 -20GaF 3 -15InF 3 -20CdF 2 -15ZnF 2 (PGICZ). Selected rare earths are La, Ce, Pr, Nd, Gd, Er, Yb and Lu, and the doping level varies between 1 and 10 mol%. The influence of rare earth fluorides on glass forming ability and on physical properties is investigated. At low concentration ( 3 in a modified PGCIZ glass have been cast. Experimental results suggest that rare earths act as modifiers rather than vitrifies in this fluorogallate system. The effect of rare earths on the values of glass transition temperature, refractive index, density and thermal expansion is reported. (orig.)

Enhanced Photocatalytic Activity of Rare Earth Metal (Nd and Gd doped ZnO Nanostructures

Directory of Open Access Journals (Sweden)

P. Logamani

2017-06-01

Full Text Available Presence of harmful organic pollutants in wastewater effluents causes serious environmental problems and therefore purification of this contaminated water by a cost effective treatment method is one of the most important issue which is in urgent need of scientific research. One such promising treatment technique uses semiconductor photocatalyst for the reduction of recalcitrant pollutants in water. In the present work, rare earth metals (Nd and Gd doped ZnO nanostructured photocatalyst have been synthesized by wet chemical method. The prepared samples were characterized by X-ray diffraction (XRD, Field Emission Scanning Electron Microscopy (FESEM and energy dispersive X-ray spectroscopy (EDS. The XRD results showed that the prepared samples were well crystalline with hexagonal Wurtzite structure. The results of EDS revealed that rare earth elements were doped into ZnO structure. The effect of rare earth dopant on morphology and photocatalytic degradation properties of the prepared samples were studied and discussed. The results revealed that the rare earth metal doped ZnO samples showed enhanced visible light photocatalytic activity for the degradation of methylene blue dye than pure nano ZnO photocatalyst.

Crystal Growth and Spectroscopic characterization of chloride and bromide single crystals doped with rare earth ions for the mid infrared amplification

International Nuclear Information System (INIS)

Ferrier, A.

2007-12-01

This work is devoted to the study of low phonon energy crystals doped with rare earth ions for the realisation of diode-pumped solid state laser sources emitting in the middle infrared. For that purpose, pure and (Er 3+ or Pr 3+ ) doped single crystals of KPb 2 Cl 5 and Tl 3 PbX 5 (X=Cl, Br) have been elaborated by using the Bridgman-Stockbarger method. These non-hygroscopic and congruent melting materials have been found to exhibit phase transitions during the cooling process but which do not limit the elaboration of centimeter-size single crystals. The spectroscopic study of the Er 3+ doped compounds has been performed both at high and low temperatures. It thus appears that these systems present long fluorescence lifetimes and relatively large gain cross sections favorable for a laser emission around 4.5μm. It has been demonstrated further that the up-conversion processes resulting from excited-state absorptions of the Er 3+ ions around the pumping wavelength as well as the energy transfer processes between the Er 3+ ions do not lead to significant optical losses for the laser system. The derived parameters then have been used to build a model and simulate the laser operation of the system following diode pumping around 800 nm. In the end, the spectroscopic study of the Pr 3+ ion in various materials has allowed us to evidence large emission cross sections associated with long fluorescence lifetimes, now favorable to a laser emission around 5μm. (author)

Effect of rare-earth dopants on the growth and structural, optical, electrical and mechanical properties of L-arginine phosphate single crystals

International Nuclear Information System (INIS)

Arjunan, S.; Bhaskaran, A.; Kumar, R. Mohan; Mohan, R.; Jayavel, R.

2010-01-01

Research highlights: → Thorium, Lanthanum and Cerium rare-earth ions were doped with L-arginine phosphate material and the crystals were grown by slow evaporation technique. → The transparency of the rare-earth doped LAP crystals has enhanced compared to pure LAP. → The powder SHG measurements revealed that the SHG output of rare-earth doped LAP crystals increases considerably compared to that of LAP. → Vicker's hardness number of as-grown crystal of LAP is higher than that of rare-earth doped LAP crystals. - Abstract: Effect of Thorium, Lanthanum and Cerium rare-earth ions on the growth and properties of L-arginine phosphate single crystals has been reported. The incorporation of rare-earth dopants into the L-arginine phosphate crystals is confirmed by Inductively Coupled Plasma-Mass Spectroscopy analysis. The unit cell parameters for pure and rare-earth doped L-arginine phosphate crystals have been estimated by powder X-ray diffraction studies. UV-visible studies revealed the transmittance percentage and cut-off wavelengths of the grown crystals. Powder second harmonic generation measurement has been carried out for pure and doped L-arginine phosphate crystals. The dielectric behavior of the grown crystals was analyzed for different frequencies at room temperature. The mechanical properties have been determined for pure and the doped L-arginine phosphate crystals.

Fibre Tip Sensors for Localised Temperature Sensing Based on Rare Earth-Doped Glass Coatings

Directory of Open Access Journals (Sweden)

Erik P. Schartner

2014-11-01

Full Text Available We report the development of a point temperature sensor, based on monitoring upconversion emission from erbium:ytterbium-doped tellurite coatings on the tips of optical fibres. The dip coating technique allows multiple sensors to be fabricated simultaneously, while confining the temperature-sensitive region to a localised region on the end-face of the fibre. The strong response of the rare earth ions to changing temperature allows a resolution of 0.1–0.3 °C to be recorded over the biologically relevant range of temperatures from 23–39 °C.

Radioluminescence of rare-earth doped aluminum oxide

Energy Technology Data Exchange (ETDEWEB)

Santiago, M.; Molina, P. [Universidad Nacional del Centro de la Provincia de Buenos Aires, Instituto de Fisica Arroyo Seco, Pinto 399, 7000 Tandil (Argentina); Barros, V. S.; Khoury, H. J.; Elihimas, D. R., E-mail: msantiag@exa.unicen.edu.ar [Universidade Federal de Pernambuco, Departamento de Energia Nuclear, Av. Prof. Luiz Freire 1000, Recife, PE 50740-540 (Brazil)

2011-10-15

Carbon-doped aluminum oxide (Al{sub 2}O{sub 3}:C) is one of the most used radioluminescence (Rl) materials for fiberoptic dosimetry due to its high efficiency and commercial availability. However, this compound presents the drawback of emitting in the spectral region, where the spurious radioluminescence of fibers is also important. In this work, the radioluminescence response of rare-earth doped Al{sub 2}O{sub 3} samples has been evaluated. The samples were prepared by mixing stoichiometric amounts of aluminum nitrate, urea and dopants with different amounts of terbium, samarium, cerium and thulium nitrates varying from 0 to 0.15 mo 1%. The influence of the different activators on the Rl spectra has been investigated in order to determine the feasibility of using these compounds for Rl fiberoptic dosimetry. (Author)

Radioluminescence of rare-earth doped aluminum oxide

International Nuclear Information System (INIS)

Santiago, M.; Molina, P.; Barros, V. S.; Khoury, H. J.; Elihimas, D. R.

2011-10-01

Carbon-doped aluminum oxide (Al 2 O 3 :C) is one of the most used radioluminescence (Rl) materials for fiberoptic dosimetry due to its high efficiency and commercial availability. However, this compound presents the drawback of emitting in the spectral region, where the spurious radioluminescence of fibers is also important. In this work, the radioluminescence response of rare-earth doped Al 2 O 3 samples has been evaluated. The samples were prepared by mixing stoichiometric amounts of aluminum nitrate, urea and dopants with different amounts of terbium, samarium, cerium and thulium nitrates varying from 0 to 0.15 mo 1%. The influence of the different activators on the Rl spectra has been investigated in order to determine the feasibility of using these compounds for Rl fiberoptic dosimetry. (Author)

Growth of rare-earth doped single crystal yttrium aluminum garnet fibers

Science.gov (United States)

Bera, Subhabrata; Nie, Craig D.; Harrington, James A.; Cheng, Long; Rand, Stephen C.; Li, Yuan; Johnson, Eric G.

2018-02-01

Rare-earth doped single crystal (SC) yttrium aluminum garnet (YAG) fibers have great potential as high-power laser gain media. SC fibers combine the superior material properties of crystals with the advantages of a fiber geometry. Improving processing techniques, growth of low-loss YAG SC fibers have been reported. A low-cost technique that allows for the growth of optical quality Ho:YAG single crystal (SC) fibers with different dopant concentrations have been developed and discussed. This technique is a low-cost sol-gel based method which offers greater flexibility in terms of dopant concentration. Self-segregation of Nd ions in YAG SC fibers have been observed. Such a phenomenon can be utilized to fabricate monolithic SC fibers with graded index.

Effect of rare-earth dopants on the growth and structural, optical, electrical and mechanical properties of L-arginine phosphate single crystals

Energy Technology Data Exchange (ETDEWEB)

Arjunan, S., E-mail: arjunan_hce@yahoo.co.i [Department of Physics, Sri Ramachandra University, Porur, Chennai (India); Bhaskaran, A. [Department of Physics, Dr. Ambedkar Government College, Chennai (India); Kumar, R. Mohan; Mohan, R. [Department of Physics, Presidency College, Chennai (India); Jayavel, R. [Crystal Growth Centre, Anna University, Chennai (India)

2010-09-17

Research highlights: {yields} Thorium, Lanthanum and Cerium rare-earth ions were doped with L-arginine phosphate material and the crystals were grown by slow evaporation technique. {yields} The transparency of the rare-earth doped LAP crystals has enhanced compared to pure LAP. {yields} The powder SHG measurements revealed that the SHG output of rare-earth doped LAP crystals increases considerably compared to that of LAP. {yields} Vicker's hardness number of as-grown crystal of LAP is higher than that of rare-earth doped LAP crystals. - Abstract: Effect of Thorium, Lanthanum and Cerium rare-earth ions on the growth and properties of L-arginine phosphate single crystals has been reported. The incorporation of rare-earth dopants into the L-arginine phosphate crystals is confirmed by Inductively Coupled Plasma-Mass Spectroscopy analysis. The unit cell parameters for pure and rare-earth doped L-arginine phosphate crystals have been estimated by powder X-ray diffraction studies. UV-visible studies revealed the transmittance percentage and cut-off wavelengths of the grown crystals. Powder second harmonic generation measurement has been carried out for pure and doped L-arginine phosphate crystals. The dielectric behavior of the grown crystals was analyzed for different frequencies at room temperature. The mechanical properties have been determined for pure and the doped L-arginine phosphate crystals.

Theoretical investigation of the more suitable rare earth to achieve high gain in waveguide based on silica containing silicon nanograins doped with either Nd³+ or Er³+ ions.

Science.gov (United States)

Fafin, Alexandre; Cardin, Julien; Dufour, Christian; Gourbilleau, Fabrice

2014-05-19

We present a comparative study of the gain achievement in a waveguide whose active layer is constituted by a silica matrix containing silicon nanograins acting as sensitizer of either neodymium ions (Nd3+) or erbium ions (Er3+). By means of an auxiliary differential equation and finite difference time domain (ADE-FDTD) approach that we developed, we investigate the steady states regime of both rare earths ions and silicon nanograins levels populations as well as the electromagnetic field for different pumping powers ranging from 1 to 104 mW/mm2. Moreover, the achievable gain has been estimated in this pumping range. The Nd3+ doped waveguide shows a higher gross gain per unit length at 1064 nm (up to 30 dB/cm) than the one with Er3+ doped active layer at 1532 nm (up to 2 dB/cm). Taking into account the experimental background losses we demonstrate that a significant positive net gain can only be achieved with the Nd3+ doped waveguide.

Recent advances in rare earth doped alkali-alkaline earth borates for solid state lighting applications

Science.gov (United States)

Verma, Shefali; Verma, Kartikey; Kumar, Deepak; Chaudhary, Babulal; Som, Sudipta; Sharma, Vishal; Kumar, Vijay; Swart, Hendrik C.

2018-04-01

As a novel class of inorganic phosphor, the alkali-alkaline earth borate phosphors have gained huge attention due to their charming applications in solid-state lighting (SSL) and display devices. The current research drive shows that phosphors based on the alkali-alkaline earth borates have transformed the science and technology due to their high transparency over a broad spectral range, their flexibility in structure and durability for mechanical and high-laser applications. Recent advances in various aspects of rare-earth (RE) doped borate based phosphors and their utilizations in SSL and light emitting diodes are summarized in this review article. Moreover, the present status and upcoming scenario of RE-doped borate phosphors were reviewed in general along with the proper credential from the existing literature. It is believed that this review is a sole compilation of crucial information about the RE-doped borate phosphors in a single platform.

All-optical control of long-lived nuclear spins in rare-earth doped nanoparticles.

Science.gov (United States)

Serrano, D; Karlsson, J; Fossati, A; Ferrier, A; Goldner, P

2018-05-29

Nanoscale systems that coherently couple to light and possess spins offer key capabilities for quantum technologies. However, an outstanding challenge is to preserve properties, and especially optical and spin coherence lifetimes, at the nanoscale. Here, we report optically controlled nuclear spins with long coherence lifetimes (T 2 ) in rare-earth-doped nanoparticles. We detect spins echoes and measure a spin coherence lifetime of 2.9 ± 0.3 ms at 5 K under an external magnetic field of 9 mT, a T 2 value comparable to those obtained in bulk rare-earth crystals. Moreover, we achieve spin T 2 extension using all-optical spin dynamical decoupling and observe high fidelity between excitation and echo phases. Rare-earth-doped nanoparticles are thus the only nano-material in which optically controlled spins with millisecond coherence lifetimes have been reported. These results open the way to providing quantum light-atom-spin interfaces with long storage time within hybrid architectures.

Magnetomigration of rare-earth ions in inhomogeneous magnetic fields.

Science.gov (United States)

Franczak, Agnieszka; Binnemans, Koen; Jan Fransaer

2016-10-05

The effects of external inhomogenous (gradient) magnetic fields on the movement of the rare-earth ions: Dy 3+ , Gd 3+ and Y 3+ , in initially homogeneous aqueous solutions have been investigated. Differences in the migration of rare-earth ions in gradient magnetic fields were observed, depending on the magnetic character of the ions: paramagnetic ions of Dy 3+ and Gd 3+ move towards regions of the sample where the magnetic field gradient is the strongest, while diamagnetic ions of Y 3+ move in the opposite direction. It has been showed that the low magnetic field gradients, such the ones generated by permanent magnets, are sufficient to observe the magnetomigration effects of the ions in solution. The present work clearly establishes the behavior of magnetically different ions in initially homogeneous aqueous solutions exposed to magnetic field gradients. To this avail, a methodology for measuring the local concentration differences of metal ions in liquid samples was developed.

Laser induced adjustment of the conductivity of rare earth doped Mn-Zn nanoferrite

Directory of Open Access Journals (Sweden)

El-Dek S. I.

2017-10-01

Full Text Available Two series of Mn-Zn nanoferrites (namely Mn1-xZnxFe2O4 and Mn1-xZnxFe2-yRyO4 were synthesized using standard ceramic technique. X-ray diffraction and FT-IR were employed in the chacterization of the nanopowder. The X-ray density for each sample increased after laser irradiation which was correlated with the decrease in the unit cell volume. The study involved the thermal and frequency variation of the dielectric constant and AC conductivity of the investigated samples before and after laser irradiation. The later altered the conductivity by decreasing its value for the rare earth doped samples except for the Sm3+ doped one. The results suggested the exploitation of Mn-Zn doped rare earth nanoferrites in many technological applications demanding high resistivity.

Influence of rare earth (Nd{sup +3}) doping on structural and magnetic properties of nanocrystalline manganese-zinc ferrite

Energy Technology Data Exchange (ETDEWEB)

Naik, Pranav P., E-mail: drppn1987@gmail.com [Department of Physics, Goa University, Taleigao Plateau, Goa, 403206 (India); Tangsali, R.B. [Department of Physics, Goa University, Taleigao Plateau, Goa, 403206 (India); Meena, S.S.; Yusuf, S.M. [Solid State Physics Division, Bhabha Atomic Research Centre, Mumbai, 400085 (India)

2017-04-15

Ultrafine nanopowders of Mn{sub 0.6}Zn{sub 0.4}Fe{sub 2-x}Nd{sub x}O{sub 4} (x = 0, 0.04, 0.06, 0.08, and 0.1) were prepared using combustion method. The influence of Nd{sup +3} doping on structural parameters, morphological characteristics and magnetic properties were investigated. Formation of pure spinel phase was confirmed using X-ray powder diffraction (XRPD). Nd{sup +3} doping in Mn-Zn ferrite samples have shown remarkable influence on all the properties that were under investigation. An increase in lattice constant commensurate with increasing Nd{sup +3} concentrations was observed in the samples. The crystallite size calculated from XRPD data and grain size observed from Transmission Electron Microscope showed a proportionate decrement with increment in rare earth doping. An increase in mass density, X-ray density, particle strain and decrease in porosity were the other effects noticed on the samples as a result of Nd{sup +3} doping. The corresponding tetrahedral, octahedral bond lengths and bond angles estimated from XRPD data have also shown substantial influence of the Nd{sup +3} doping. Magnetic parameters namely saturation magnetization (M{sub S}) and net magnetic moment η{sub B}, estimated using vibrating sample magnetometer (VSM) were found to depend on the Nd{sup +3} doping. Mössbauer spectroscopy was employed to study the magnetic environment of Mössbauer active ions and detection of superparamagnetic behavior in nanocrystalline rare earth ferrite material. The isomer shift values obtained from Mössbauer spectra indicate the presence of Fe{sup +3} ions at tetrahedral site (A-site) and octahedral site (B-site), respectively. - Highlights: • Synthesis of Nd doped Mn-Zn ferrite nanoparticles using combustion method. • Successful doping of Nd{sup +3} at octahedral site in ferrite structure. • Existence of Fe{sup +3} oxidation state at both A-Site and B-site. • Enhanced saturation magnetization due to altered cation distribution by Nd doping

Synthesis and characterization of BaAl{sub 2}O{sub 4}:Eu{sup 2+} co-doped with different rare earth ions

Energy Technology Data Exchange (ETDEWEB)

Lephoto, M.A. [Department of Physics, University of the Free State, Private bag X 13, Phuthaditjaba 9866, P.O. Box 339, Bloemfontein, ZA 9300 (South Africa); Ntwaeaborwa, O.M., E-mail: ntwaeab@ufs.ac.za [Department of Physics, University of the Free State, Private bag X 13, Phuthaditjaba 9866, P.O. Box 339, Bloemfontein, ZA 9300 (South Africa); Pitale, Shreyas S.; Swart, H.C. [Department of Physics, University of the Free State, Private bag X 13, Phuthaditjaba 9866, P.O. Box 339, Bloemfontein, ZA 9300 (South Africa); Botha, J.R. [Department of Physics, Nelson Mandela Metropolitan University, Port Elizabeth, ZA 6031 (South Africa); Mothudi, B.M. [Department of Physics, University of South Africa, P.O Box 392, Pretoria, ZA 6031 (South Africa)

2012-05-15

Combustion method was used in this study to prepare BaAl{sub 2}O{sub 4}:Eu{sup 2+} phosphors co-doped with different trivalent rare-earths (Re{sup 3+}=Dy{sup 3+}, Nd{sup 3+}, Gd{sup 3+}, Sm{sup 3+}, Ce{sup 3+}, Er{sup 3+}, Pr{sup 3+} and Tb{sup 3+}) ions at an initiating temperature of 600 Degree-Sign C. The phosphors were annealed at 1000 Degree-Sign C for 3 h. As confirmed from the X-ray diffraction (XRD) data, both as prepared and post annealed samples crystallized in the well known hexagonal structure of BaAl{sub 2}O{sub 4}. All samples exhibited bluish-green emission associated with the 4f{sup 6}5d{sup 1}{yields}4f{sup 7} transitions of Eu{sup 2+} at {approx}500 nm. Although the highest intensity was observed from Er{sup 3+} co-doping, the longest afterglow (due to trapping and detrapping of charge carriers) was observed from Nd{sup 3+} followed by Dy{sup 3+} co-doping. The traps responsible for the long afterglow were studied using thermoluminescence (TL) spectroscopy.

Rare-earth-doped materials with application to optical signal processing, quantum information science, and medical imaging technology

Science.gov (United States)

Cone, R. L.; Thiel, C. W.; Sun, Y.; Böttger, Thomas; Macfarlane, R. M.

2012-02-01

Unique spectroscopic properties of isolated rare earth ions in solids offer optical linewidths rivaling those of trapped single atoms and enable a variety of recent applications. We design rare-earth-doped crystals, ceramics, and fibers with persistent or transient "spectral hole" recording properties for applications including high-bandwidth optical signal processing where light and our solids replace the high-bandwidth portion of the electronics; quantum cryptography and information science including the goal of storage and recall of single photons; and medical imaging technology for the 700-900 nm therapeutic window. Ease of optically manipulating rare-earth ions in solids enables capturing complex spectral information in 105 to 108 frequency bins. Combining spatial holography and spectral hole burning provides a capability for processing high-bandwidth RF and optical signals with sub-MHz spectral resolution and bandwidths of tens to hundreds of GHz for applications including range-Doppler radar and high bandwidth RF spectral analysis. Simply stated, one can think of these crystals as holographic recording media capable of distinguishing up to 108 different colors. Ultra-narrow spectral holes also serve as a vibration-insensitive sub-kHz frequency reference for laser frequency stabilization to a part in 1013 over tens of milliseconds. The unusual properties and applications of spectral hole burning of rare earth ions in optical materials are reviewed. Experimental results on the promising Tm3+:LiNbO3 material system are presented and discussed for medical imaging applications. Finally, a new application of these materials as dynamic optical filters for laser noise suppression is discussed along with experimental demonstrations and theoretical modeling of the process.

Yttrium and rare earths separation by ion exchange resin

International Nuclear Information System (INIS)

Pinatti, D.G.; Ayres, M.J.G.; Ribeiro, S.; Silva, G.L.J.P.; Silva, M.L.C.P.; Martins, A.H.

1988-01-01

The experimental results of yttrium and rare earths separation from Brazilian xenotime are presented. The research consist in five stage: 1) Preparation of yttrium, erbium and lutetium standard solutions, from solubilization of pure oxides 2) yttrium and rare earths separation by ion exchange chromatrography 3) Separation and recovery of EDTA 4) Precipitation and calcination and 4) Analytical control of process. (C.G.C.) [pt

Review on dielectric properties of rare earth doped barium titanate

International Nuclear Information System (INIS)

Ismail, Fatin Adila; Osman, Rozana Aina Maulat; Idris, Mohd Sobri

2016-01-01

Rare earth doped Barium Titanate (BaTiO_3) were studied due to high permittivity, excellent electrical properties and have wide usage in various applications. This paper reviewed on the electrical properties of RE doped BaTiO_3 (RE: Lanthanum (La), Erbium (Er), Samarium (Sm), Neodymium (Nd), Cerium (Ce)), processing method, phase transition occurred and solid solution range for complete study. Most of the RE doped BaTiO_3 downshifted the Curie temperature (T_C). Transition temperature also known as Curie temperature, T_C where the ceramics had a transition from ferroelectric to a paraelectric phase. In this review, the dielectric constant of La-doped BaTiO_3, Er-doped BaTiO_3, Sm-doped BaTiO_3, Nd-doped BaTiO_3 and Ce-doped BaTiO_3 had been proved to increase and the transition temperature or also known as T_C also lowered down to room temperature as for all the RE doped BaTiO_3 except for Er-doped BaTiO_3.

Luminescent features of sol–gel derived rare-earth multi-doped oxyfluoride nano-structured phosphors for white LED application

International Nuclear Information System (INIS)

Gouveia-Neto, A.S.; Silva, A.F. da; Bueno, L.A.; Costa, E.B. da

2012-01-01

Rare-earth doped oxyfluoride 75SiO 2 :25PbF 2 nano-structured phosphors for white-light-emitting diodes were synthesized by thermal treatment of precursor sol–gel derived glasses. Room temperature luminescence features of Eu 3+ , Sm 3+ , Tb 3+ , Eu 3+ /Tb 3+ , and Sm 3+ /Tb 3+ ions incorporated into low-phonon-energy PbF 2 nanocrystals dispersed in the aluminosilicate glass matrix and excited with UV light emitting diode were investigated. The luminescence spectra exhibited strong emission signals in the red (600, 610, 625, and 646 nm), green (548 and 560 nm), and blue (485 nm) wavelength regions. White-light emission was observed in Sm/Tb and Eu/Tb double-doped activated phosphors employing UV-LED excitation at 395 nm. The dependence of the luminescence emission intensities upon annealing temperature and rare-earth concentration was also examined. The results indicated that there exist optimum annealing temperature and activator ion concentration in order to obtain intense visible emission light with high color rendering index. The study suggests that the nanocomposite phosphor based upon 75SiO 2 :25PbF 2 host herein reported is a promising contender for white-light LED applications. - Highlights: ► White-light emission in double-doped activated phosphors employing UV-LED excitation. ► Luminescent features of europium, samarium, and terbium in nanocrystals dispersed in aluminosilicate glass. ► New nanocomposite phosphor host for white-light LED applications.

Electrostatic tuning of Kondo effect in a rare-earth-doped wide-band-gap oxide

KAUST Repository

Li, Yongfeng; Deng, Rui; Lin, Weinan; Tian, Yufeng; Peng, Haiyang; Yi, Jiabao; Yao, Bin; Wu, Tao

2013-01-01

As a long-lived theme in solid-state physics, the Kondo effect reflects the many-body physics involving the short-range Coulomb interactions between itinerant electrons and localized spins in metallic materials. Here we show that the Kondo effect is present in ZnO, a prototypical wide-band-gap oxide, doped with a rare-earth element (Gd). The localized 4f electrons of Gd ions do not produce remanent magnetism, but interact strongly with the host electrons, giving rise to a saturating resistance upturn and negative magnetoresistance at low temperatures. Furthermore, the Kondo temperature and resistance can be electrostatically modulated using electric-double-layer gating with liquid ionic electrolyte. Our experiments provide the experimental evidence of tunable Kondo effect in ZnO, underscoring the magnetic interactions between localized and itinerant electrons and the emergent transport behaviors in such doped wide-band-gap oxides.

Electrostatic tuning of Kondo effect in a rare-earth-doped wide-band-gap oxide

KAUST Repository

Li, Yongfeng

2013-04-29

As a long-lived theme in solid-state physics, the Kondo effect reflects the many-body physics involving the short-range Coulomb interactions between itinerant electrons and localized spins in metallic materials. Here we show that the Kondo effect is present in ZnO, a prototypical wide-band-gap oxide, doped with a rare-earth element (Gd). The localized 4f electrons of Gd ions do not produce remanent magnetism, but interact strongly with the host electrons, giving rise to a saturating resistance upturn and negative magnetoresistance at low temperatures. Furthermore, the Kondo temperature and resistance can be electrostatically modulated using electric-double-layer gating with liquid ionic electrolyte. Our experiments provide the experimental evidence of tunable Kondo effect in ZnO, underscoring the magnetic interactions between localized and itinerant electrons and the emergent transport behaviors in such doped wide-band-gap oxides.

Luminescence quenching versus enhancement in WO3-NaPO3 glasses doped with trivalent rare earth ions and containing silver nanoparticles

Science.gov (United States)

Dousti, M. Reza; Poirier, Gael Y.; Amjad, Raja J.; de Camargo, Andrea S. S.

2016-10-01

We report on the influence of silver nanoparticles (NPs) on the luminescence behavior of trivalent rare earth (RE) ion doped tungsten-phosphate glasses. In order to induce the growth of NPs, the as-prepared glass samples containing silver atoms, are exposed to heat-treatment above the glass transition temperature. The surface plasmon resonance band of the Ag NPs is observed in the visible range around 420 and 537 nm in the glasses with low and high tungsten content, respectively. Such difference in spectral shift of the plasmon band is attributed to the difference in the refractive index of the two studied glass compositions. Heat-treatment results in the general increase in number of NPs, while in the case of glasses with low tungsten content, it also imposes a shift to the Ag plasmon band. The NPs size distribution (4-10 nm) was determined in good agreement with the values obtained by using Mie theory and by transmission electron microscopy. The observed quenching in the visible luminescence of glasses doped with Eu3+, Tb3+ or Er3+is attributed to energy transfer from the RE ions to Ag species, while an enhanced near-infrared emission in Er3+ doped glasses is discussed in terms of the chemical contribution of silver, rather than the most commonly claimed enhancement of localized field or energy transfer from silver species to Er3+. The results are supported by the lifetime measurements. We believe that this study gives further insight and in-depth exploration of the somewhat controversial discussions on the influence of metallic NPs plasmonic effects in RE-doped glasses.

Effect of the kind of alkaline and rare earth ions on the structure of a glass rich in earth

International Nuclear Information System (INIS)

Quintas, Arnaud; Caurant, Daniel; Majerus, Odile; Lenoir, Marion; Dussossoy, Jean-Luc; Charpentier, Thibault; Neuville, Daniel R.; Gervais, C.

2006-01-01

In the framework of a structural study of a nuclear wastes containment glass of type alumino borosilicate and rich in rare earths, the influence of the kind of alkaline or rare earth ions is analyzed. For that, two glasses series have been prepared in which the Na + ion (respectively Ca 2+ ions) present in the standard composition is totally substituted by another alkaline ion Li + , K + , Rb + or Cs + (respectively another rare earth ion Mg 2+ , Sr 2+ or Ba 2+ ). These glasses, analyzed by optical absorption, Raman and 27 Al or 11 B NMR spectroscopies have revealed the strong impact of the kind of the modifying ion as well as the structure of the vitreous lattice (variation of the ratio BO 3 /BO 4 and local variations of the polymerization degree) than the local surroundings of the rare earth (decrease of the covalency degree of the bond Nd-O with the increase of the field force of the modifying ion). (O.M.)

Influence of Rare Earth Doping on the Structural and Catalytic Properties of Nanostructured Tin Oxide

Directory of Open Access Journals (Sweden)

Maciel Adeilton

2008-01-01

Full Text Available AbstractNanoparticles of tin oxide, doped with Ce and Y, were prepared using the polymeric precursor method. The structural variations of the tin oxide nanoparticles were characterized by means of nitrogen physisorption, carbon dioxide chemisorption, X-ray diffraction, and X-ray photoelectron spectroscopy. The synthesized samples, undoped and doped with the rare earths, were used to promote the ethanol steam reforming reaction. The SnO2-based nanoparticles were shown to be active catalysts for the ethanol steam reforming. The surface properties, such as surface area, basicity/base strength distribution, and catalytic activity/selectivity, were influenced by the rare earth doping of SnO2and also by the annealing temperatures. Doping led to chemical and micro-structural variations at the surface of the SnO2particles. Changes in the catalytic properties of the samples, such as selectivity toward ethylene, may be ascribed to different dopings and annealing temperatures.

Optical-limiting response of rare-earth metallo-phthalocyanine-doped copolymer matrix

NARCIS (Netherlands)

Aneeshkumar, B.N.; Gopinath, P.; Vallabhan, C.P.G.; Nampoori, V.P.N.; Radhakrishnan, P.; Thomas, J.

2003-01-01

The nanosecond optical-limiting characteristics (at 532 nm) of some rare-earth metallo-phthalocyanines (Sm(Pc)2, Eu(Pc)2, and LaPc) doped in a copolymer matrix of poly(Me methacrylate) and Me-2-cyanoacrylate were studied for the 1st time to the authors' knowledge. The optical-limiting response is

Factors controlling the thermoluminescence spectra of rare earth doped calcium fluoride

Energy Technology Data Exchange (ETDEWEB)

Wang, Y., E-mail: wyfemail@gmail.com [School of Science, China University of Geosciences, Beijing 100083 (China); Zhao, Y. [School of Science, China University of Geosciences, Beijing 100083 (China); White, D. [Barnsley Hospital NHS Foundation Trust, Gawber Road, Barnsley S75 2EP (United Kingdom); Finch, A.A. [Department of Earth & Environmental Sciences, University of St Andrews, Fife KY16 9AL (United Kingdom); Townsend, P.D. [Physics Building, University of Sussex, Brighton BN1 9QH (United Kingdom)

2017-04-15

Thermoluminescence spectra of rare earth doped calcium fluoride samples, both powder and single crystal, were recorded over the temperature range from 25 K to 673 K. Although some broad band features exist, the spectra are dominated by the rare earth line transitions. The glow peak temperatures are slightly sensitive both to the ionic size of the dopants and the dopant concentration. By contrast, very considerable differences are generated by heat treatments, such as annealing followed by either fast or slow cooling. Comments are included on the reasons for such sensitivity in terms of association of dopant and intrinsic defect sites and why the results of dosimetry powder differ from those from single crystals.

Structure and Magnetic Properties of Rare Earth Doped Transparent Alumina

Science.gov (United States)

Limmer, Krista; Neupane, Mahesh; Chantawansri, Tanya

Recent experimental studies of rare earth (RE) doped alumina suggest that the RE induced novel phase-dependent structural and magnetic properties. Motivated by these efforts, the effects of RE doping of alpha and theta alumina on the local structure, magnetic properties, and phase stability have been examined in this first principles study. Although a direct correlation between the magnetic field dependent materials properties observed experimentally and calculated from first principles is not feasible because of the applied field and the scale, the internal magnetic properties and other properties of the doped materials are evaluated. The RE dopants are shown to increase the substitutional site volume as well as increasingly distort the site structure as a function of ionic radii. Doping both the alpha (stable) and theta (metastable) phases enhanced the relative stability of the theta phase. The energetic doping cost and internal magnetic moment were shown to be a function of the electronic configuration of the RE-dopant, with magnetic moment directly proportional to the number of unpaired electrons and doping cost being inversely related.

Self-propagating high temperature synthesis, structural morphology and magnetic interactions in rare earth Ho{sup 3+} doped CoFe{sub 2}O{sub 4} nanoparticles

Energy Technology Data Exchange (ETDEWEB)

Lohar, K.S. [Materials Research Laboratory, Srikrishna Mahavidyalaya Gunjoti, Omerga, Osmanabad 413 613, MS (India); Pachpinde, A.M.; Langade, M.M. [Department of Chemistry, Jawahar Art Science and Commerce College Andur, Osmanabad, MS (India); Kadam, R.H. [Materials Research Laboratory, Srikrishna Mahavidyalaya Gunjoti, Omerga, Osmanabad 413 613, MS (India); Shirsath, Sagar E., E-mail: shirsathsagar@hotmail.com [Spin Device Technology Center, Department of Information Engineering, Shinshu University, Nagano 380-8553 (Japan)

2014-08-01

Highlights: • Rare earth Ho{sup 3+} substituted CoFe{sub 2}O{sub 4.} • XRD and IR spectra reveal the spinel structure. • Magnetization and coercivity increased with Ho{sup 3+} substitution. - Abstract: Substitution effect of rare earth trivalent Ho{sup 3+} ions on the composition, Ho{sub x}CoFe{sub 2−x}O{sub 4}, with x varying from 0.0 to 0.1 in steps of 0.025 using sol–gel auto combustion route has been investigated. Examination of X-ray diffraction (XRD) patterns shows that all the samples consisted of ferrite phases of typical spinel cubic structure, and when Ho{sup 3+} ion content was x ⩾ 0.075, orthoferrite–HoFeO{sub 3} phase was detected. The micro and nanostructure of the synthesized Ho doped CoFe{sub 2}O{sub 4} ferrites were investigated by scanning and transmission electron microscopy respectively. With increasing doping content of Ho{sup 3+} ions, the lattice constant, particle size and bulk density increased, and after an increase to its maximum value, the sample particle size and density dropped down. Cation distribution estimated from XRD patter revealed that the Co{sup 2+} and Ho{sup 3+} ions prefer to occupy octahedral B-site whereas Fe{sup 3+} ions are distributed over tetra- and octa-hedral site. Oxygen positional parameter shows larger values than its ideal value. The analysis of magnetic properties revealed that the saturation magnetization and coercivity of CoFe{sub 2}O{sub 4} increased with the rare earth Ho{sup 3+} substitution.

Bench scale studies on separation of rare earths by ion exchange

International Nuclear Information System (INIS)

Aroonrung-Areeya, A.

1976-01-01

The method of ion exchange was applied to the separation of mixtures of rare earth oxides into the pure components. The method consists of eluting a band of mixed rare earths adsorbed on a cation-exchange resin through a second cation-exchange bed in the copper II state. The eluent consists of an ammonia buffered solution of ethylenediamine tetraacetic acid. The mixed rare earth oxide used as testing material was obtained from the digestion of Thai monazite. The amounts varied from 1, 5 to 50 grams. The purity of the rare earth fractions were analyzed either by neutron activation of X-ray fluorescence. The Cu.EDTA was recovered by the addition of lime. It was found that gram quantities of pure rare earths could be obtained by this method

Photoluminescence of rare-earth ion (Eu3+, Tm3+, and Er3+)-doped and co-doped ZnNb2O6 for solar cells

Science.gov (United States)

Gao, Sen-Pei; Qian, Yan-Nan; Wang, Biao

2015-08-01

Visible converted emissions produced at an excitation of 286 nm in ZnNb2O6 ceramics doped with rare-earth ions (RE = Eu3+, Tm3+, Er3+ or a combination of these ions) were investigated with the aim of increasing the photovoltaic efficiency of solar cells. The structure of RE:ZnNb2O6 ceramics was confirmed by x-ray diffraction patterns. The undoped ZnNb2O6 could emit a blue emission under 286-nm excitation, which is attributed to the self-trapped excitons’ recombination of the efficient luminescence centers of edge-shared NbO6 groups. Upon 286-nm excitation, Eu:ZnNb2O6, Tm:ZnNb2O6, and Er:ZnNb2O6 ceramics showed blue, green, and red emissions, which correspond to the transitions of 5D0 → 7FJ (J = 1-4) (Eu3+), 1G4 → 3H6 (Tm3+), and 2H11/2/4S3/2 → 4I15/2 (Er3+), respectively. The calculated CIE chromaticity coordinates of Eu:ZnNb2O6, Tm:ZnNb2O6, and Er:ZnNb2O6 are (0.50, 0.31), (0.14, 0.19), and (0.29, 0.56), respectively. RE ion-co-doped ZnNb2O6 showed a combination of characteristic emissions. The chromaticity coordinates of Eu/Tm:ZnNb2O6, Eu/Er:ZnNb2O6, and Tm/Er:ZnNb2O6 were calculated to be (0.29, 0.24), (0.45, 0.37), and (0.17, 0.25). Project supported by the National Natural Science Foundation of China (Grant Nos. 10572155 and 10732100) and the Research Fund for the Doctoral Program of Ministry of Education, China (Grant No. 20130171130003).

Towards rare-earth-ion-doped Al2O3 active integrated optical devices

OpenAIRE

Ay, F.; Bradley, J.; Worhoff, Kerstin; Pollnau, Markus

2007-01-01

Aluminum oxide planar waveguides with low loss (0.11 dB/cm at 1523 nm) are fabricated. Channel waveguides are obtained by reactive ion etching. Erbium-doped layers show no upconversion luminescence, a hint that ion clustering is small.

Magnetic and magnetoelectric properties of NdCrTiO5 revealed by systematically rare-earth doping

Science.gov (United States)

Li, Qing; Feng, Zhenjie; Cheng, Cheng; Wang, Bojie; Chu, Hao; Huang, Ping; Wang, Difei; Qian, Xiaolong; Yu, Chuan; Wang, Guohua; Deng, Dongmei; Jing, Chao; Cao, Shixun; Zhang, Jincang

2018-01-01

We have systematically synthesized polycrystalline samples of Nd0.9A0.1CrTiO5 (A = Pr, Nd, Gd, Dy, Er, Tm, and Yb), and have investigated their crystal structure, polarization and magnetic susceptibility. The polarization values of doped samples are suppressed comparing to pure NdCrTiO5 sample, which indicates that the polarization is highly dependence with the magnetic moments of doping ions. The TN of Cr-Cr in Nd0.9A0.1CrTiO5 are dominated by both the suppression effect caused by doped magnetic moment increment and the enhancement effect caused by c axis contracting. We conclude that the magnetic moments in the rare-earth Nd sites play an important role in the magnetoelectric effect in NdCrTiO5 family. The substitution effect discussion here can help us well understand the intrinsic mechanism and provide a possible guidance in exploring new magnetoelectric coupling systems.

DFT Calculations using WIEN2K to determine oxygen defect structure of rare earth doped ceria

CERN Document Server

Khalife, Ali Rida

2014-01-01

We perform density functional calculations using the program WIEN2K in order to study oxygen vacancies in rare earth doped ceria. The calculation for all rare earth elements were prepared, however only those foe Cadmium and Europium were performed due to lack of time. Also a short description of my stay at CERN was presented

Rare earth sulfates

International Nuclear Information System (INIS)

Komissarova, L.N.; Shatskij, V.M.; Pokrovskij, A.N.; Chizhov, S.M.; Bal'kina, T.I.; Suponitskij, Yu.L.

1986-01-01

Results of experimental works on the study of synthesis conditions, structure and physico-chemical properties of rare earth, scandium and yttrium sulfates, have been generalized. Phase diagrams of solubility and fusibility, thermodynamic and crystallochemical characteristics, thermal stability of hydrates and anhydrous sulfates of rare earths, including normal, double (with cations of alkali and alkaline-earth metals), ternary and anion-mixed sulfates of rare earths, as well as their adducts, are considered. The state of ions of rare earths, scandium and yttrium in aqueous sulfuric acid solutions is discussed. Data on the use of rare earth sulfates are given

White emission materials from glass doped with rare Earth ions: A review

Energy Technology Data Exchange (ETDEWEB)

Yasaka, P.; Kaewkhao, J., E-mail: mink110@hotmail.com [Center of Excellence in Glass Technology and Materials Science (CEGM), Nakhon Pathom Rajabhat University, Nakhon Pathom 73000 (Thailand); Physics Program, Faculty of Science and Technology, Nakhon Pathom Rajabhat University, 73000 (Thailand)

2016-03-11

Solid State Lighting (SSL) based devices are predicted to play a crucial role in the coming years. Development of W-LED, which have an edge over traditional lighting sources due to their compact size, higher reliability, shock resistance, interesting design possibilities, higher transparency and an extremely long lifetime. Over the fifteen trivalent lanthanide ions, Dy{sup 3+} ions doped glasses are most appropriate for white light generation because of the fact that it exhibits two intense emission bands corresponds to the {sup 4}F{sub 9/2}→{sup 6}H{sub 15/2} (magnetic dipole) and {sup 4}F{sub 9/2}→{sup 6}H{sub 13/2} (electric dipole) transitions at around 480-500 nm and 580-600 nm pertaining to blue and yellow regions respectively. In this work, the developments of Dy3+ doped in several glass structures for white emitting materials application have reviewed. Properties of Dy{sup 3+} doped in glasses were discussed for use as a solid state lighting materials application.

Review- Magnetic orientation and magnetic anisotropy in paramagnetic layered oxides containing rare-earth ions

Directory of Open Access Journals (Sweden)

Shigeru Horii, Atsushi Ishihara, Takayuki Fukushima, Tetsuo Uchikoshi, Hiraku Ogino, Tohru S Suzuki, Yoshio Sakka, Jun-ichi Shimoyama and Kohji Kishio

2009-01-01

Full Text Available The magnetic anisotropies and easy axes of magnetization at room temperature were determined, and the effects of rare-earth (RE ions were clarified for RE-based cuprates, RE-doped bismuth-based cuprates and RE-doped Bi-based cobaltite regarding the grain orientation by magnetic field. The easy axis, determined from the powder orientation in a static field of 10 T, depended qualitatively on the type of RE ion for all three systems. On the other hand, the magnetization measurement of the c-axis oriented powders, aligned in static or rotating fields, revealed that the type of RE ion strongly affected not only the directions of the easy axis but also the absolute value of magnetic anisotropy, and an appropriate choice of RE ion is required to minimize the magnetic field used for grain orientation. We also studied the possibility of triaxial grain orientation in high-critical-temperature superconductors by a modulated oval magnetic field. In particular, triaxial orientation was attempted in a high-oxygen-pressure phase of orthorhombic RE-based cuprates Y2Ba4Cu7Oy. Although the experiment was performed in epoxy resin, which is not practical, in-plane alignment within 3° was achieved.

Preparation and Characterization of Rare Earth Doped Fluoride Nanoparticles

Directory of Open Access Journals (Sweden)

Timothy A. DeVol

2010-03-01

Full Text Available This paper reviews the synthesis, structure and applications of metal fluoride nanoparticles, with particular focus on rare earth (RE doped fluoride nanoparticles obtained by our research group. Nanoparticles were produced by precipitation methods using the ligand ammonium di-n-octadecyldithiophosphate (ADDP that allows the growth of shells around a core particle while simultaneously avoiding particle aggregation. Nanoparticles were characterized on their structure, morphology, and luminescent properties. We discuss the synthesis, properties, and application of heavy metal fluorides; specifically LaF3:RE and PbF2, and group IIA fluorides. Particular attention is given to the synthesis of core/shell nanoparticles, including selectively RE-doped LaF3/LaF3, and CaF2/CaF2 core/(multi-shell nanoparticles, and the CaF2-LaF3 system.

Microstructure and emission ability of rare earth oxides doped molybdenum cathodes

International Nuclear Information System (INIS)

Yang Jiancan; Nie Zuoren; Wang Yiman

2003-01-01

We adopted high-resolution transmission electron microscopy (TEM) and scanning electron microscopy (SAM) to observe and analyze the microstructure of rare earth oxide (La 2 O 3 , Sc 2 O 3 ) doped molybdenum cathodes. The results show that there are many nanometer particles in the molybdenum matrix besides some sub-micrometer particles in the crystal interfaces. All these particles are rare earth oxides as determined through calculating the electron diffraction pattern. Then we determined the electron work function and the zero-field emission current of molybdenum cathodes by the electron emission measurement. To correlate the emission data with surface composition, we use Auger electron spectroscopy (AES) to analyze the elements on the activated cathode surface and their depth profiles. We found that there were about 20 nm thick layers on an activated cathode surface, which have a high content of rare earth elements. We also use AES to analyze the elements diffusion to the cathode surface from cathode body during heating up to its operating temperature to find out which element positively affects the electron emission

Time domain optical memories using rare earth ions

International Nuclear Information System (INIS)

Sellars, M.J.; Dyke, T.; Pryde, G.J.; Manson, N.B.

1998-01-01

Full text: Rare earth doped crystals are the chosen materials for the next generation of optical memories where the process of spectral holeburning can be employed to provide an extra dimension of frequency or time to spatial dimensions and with certain rare earth ions increases of the order of 10 7 in storage capacity can be achieved over conventional optical memories. Time domain techniques are preferred over frequency domain techniques and are now well developed. In these techniques arbitrary pulse sequences are stored in the material and read out at some later time with a single read pulse using a stimulated photon echo process. Long pulse sequences will enable more data to be stored but necessitates the use of materials with long dephasing times (corresponding to narrow spectral lines) and it is this characteristic of rare earth systems that makes them the preferred material for the new time domain optical memories. The storage time can range from hours to days but in a practical device will require refreshing or re-enforcing and this puts special requirements on the stability of the laser used for storing the information. The storage process itself can also be weak and more reliable storage can be achieved by recording the data several times with the same pulse sequence. For this to be successful the laser must be at held at a constant frequency and be stable in phase over the entire duration of the pulse sequence. The procedure of reinforcing the data sequence has been proposed before and attempted without attention to the laser frequency stability. However, if the laser is not stable although some data bits will be reinforced or increased in size others will be decreased or even erased. Indeed the reliability of the memory is degraded by the introducing the rewrite process. For our work we have developed a laser with the excellent stability and able to demonstrate reproducible reinforcement of the data sequence. Thus with the rewrite sequence we are able to

Raman scattering of rare earth hexaborides

International Nuclear Information System (INIS)

Ogita, Norio; Hasegawa, Takumi; Udagawa, Masayuki; Iga, Fumitoshi; Kunii, Satoru

2009-01-01

Raman scattering spectra were measured for the rare-earth hexaborides RB 6 (R = Ce, Gd, or Dy). All Raman-active phonons due to B 6 vibrations were observed in the range 600 - 1400 cm -1 . Anomalous peaks were detected below 200 cm -1 , which correspond to vibrations of rare-earth ion excited by second-order Raman scattering process. The intensity and energy of the rare-earth mode decrease with decreasing temperature. This suggests that the rare-earth ion vibrates in a shallow and anharmonic potential due to the boron cage. Using the reported values of mean square displacement of rare-earth ion, we estimated the anharmonic contribution for the rare-earth vibrations.

Single-mode regime in large-mode-area rare-earth-doped rod-type PCFs

DEFF Research Database (Denmark)

Poli, F.; Cucinotta, A.; Passaro, D.

2009-01-01

In this paper, large-mode-area, double-cladding, rare-earth-doped photonic crystal fibers are investigated in order to understand how the refractive index distribution and the mode competition given by the amplification can assure single-mode propagation. Fibers with different core diameters, i...

Enhanced near-infrared photoacoustic imaging of silica-coated rare-earth doped nanoparticles

Energy Technology Data Exchange (ETDEWEB)

Sheng, Yang [Engineering Product Development, Singapore University of Technology and Design, 8 Somapah Road, Singapore 487372 (Singapore); School of Materials Science and Engineering, Changzhou University, Changzhou, Jiangsu 213164 (China); Liao, Lun-De [Institute of Biomedical Engineering and Nanomedicine, National Health Research Institutes, 35 Keyan Rd., Zhunan Town, Miaoli County 35053, Taiwan, ROC (China); Singapore Institute for Neurotechnology (SINAPSE), National University of Singapore, 28 Medical Drive, #05-COR, Singapore 117456 (Singapore); Bandla, Aishwarya [Singapore Institute for Neurotechnology (SINAPSE), National University of Singapore, 28 Medical Drive, #05-COR, Singapore 117456 (Singapore); Department of Biomedical Engineering, National University of Singapore, 21 Lower Kent Ridge Rd, Singapore 119077 (Singapore); Liu, Yu-Hang [Singapore Institute for Neurotechnology (SINAPSE), National University of Singapore, 28 Medical Drive, #05-COR, Singapore 117456 (Singapore); Department of Electrical and Computer Engineering, National University of Singapore, 21 Lower Kent Ridge Rd, Singapore 119077 (Singapore); Yuan, Jun [Singapore Institute for Neurotechnology (SINAPSE), National University of Singapore, 28 Medical Drive, #05-COR, Singapore 117456 (Singapore); Thakor, Nitish [Singapore Institute for Neurotechnology (SINAPSE), National University of Singapore, 28 Medical Drive, #05-COR, Singapore 117456 (Singapore); Department of Biomedical Engineering, National University of Singapore, 21 Lower Kent Ridge Rd, Singapore 119077 (Singapore); Department of Electrical and Computer Engineering, National University of Singapore, 21 Lower Kent Ridge Rd, Singapore 119077 (Singapore); Tan, Mei Chee, E-mail: meichee.tan@sutd.edu.sg [Engineering Product Development, Singapore University of Technology and Design, 8 Somapah Road, Singapore 487372 (Singapore)

2017-01-01

Near-infrared photoacoustic (PA) imaging is an emerging diagnostic technology that utilizes the tissue transparent window to achieve improved contrast and spatial resolution for deep tissue imaging. In this study, we investigated the enhancement effect of the SiO{sub 2} shell on the PA property of our core/shell rare-earth nanoparticles (REs) consisting of an active rare-earth doped core of NaYF{sub 4}:Yb,Er (REDNPs) and an undoped NaYF{sub 4} shell. We observed that the PA signal amplitude increased with SiO{sub 2} shell thickness. Although the SiO{sub 2} shell caused an observed decrease in the integrated fluorescence intensity due to the dilution effect, fluorescence quenching of the rare earth emitting ions within the REDNPs cores was successfully prevented by the undoped NaYF{sub 4} shell. Therefore, our multilayer structure consisting of an active core with successive functional layers was demonstrated to be an effective design for dual-modal fluorescence and PA imaging probes with improved PA property. The result from this work addresses a critical need for the development of dual-modal contrast agent that advances deep tissue imaging with high resolution and signal-to-noise ratio. - Graphical abstract: Illustration of multilayer structured imaging probe with REDNPs as active core, undoped NaYF{sub 4} as intermediate layer and SiO{sub 2} as outer shell. The PA signal amplitude of REs/SiO{sub 2} was increased with the SiO{sub 2} shell thickness. - Highlights: • Silica coating was demonstrated to be much more effective in enhancing the PA signal amplitude comparing to soft polymer. • PA enhancement was attributed to the increased phonon modes and phonon energy with the introduction of the SiO{sub 2} coating. • Multilayer structure was an effective design for dual-modal fluorescence and PA imaging probes with improved PA property.

Production of rare-earth atomic negative ion beams in a cesium-sputter-type negative ion source

International Nuclear Information System (INIS)

Davis, V.T.; Covington, A.M.; Duvvuri, S.S.; Kraus, R.G.; Emmons, E.D.; Kvale, T.J.; Thompson, J.S.

2007-01-01

The desire to study negative ion structure and negative ion-photon interactions has spurred the development of ion sources for use in research and industry. The many different types of negative ion sources available today differ in their characteristics and abilities to produce anions of various species. Thus the importance of choosing the correct type of negative ion source for a particular research or industrial application is clear. In this study, the results of an investigation on the production of beams composed of negatively-charged rare-earth ions from a cylindrical-cathode-geometry, cesium-sputter-type negative ion source are presented. Beams of atomic anions have been observed for most of the first-row rare-earth elements, with typical currents ranging from hundreds of picoamps to several nanoamps

Transferred hyperfine interaction between the rare-earth ions and the fluorine nuclei in rare-earth trifluorides

DEFF Research Database (Denmark)

Hansen, P. E.; Nevald, Rolf; Guggenheim, H. G.

1978-01-01

The isotropic and anisotropic transferred hyperfine interactions between F ions in the two chemically inequivalent sites and the rare-earth ions (R) have been derived from 19F NMR measurements in the temperature region 100-300 K on single crystals of TbF3 and DyF3. The isotropic interactions are ...... to vary only slightly with temperature. They are further assigned to definite R's in the unit cell, which cannot be done from macroscopic magnetic measurements....

Theoretical study of the structure and optical properties of rare-earth-doped BeF2 glass

International Nuclear Information System (INIS)

Brawer, S.; Weber, M.J.

1980-01-01

We investigate the question of whether the local structure of a glass can be deduced directly from its optical spectra by testing such a procedure on a model system. The model system was Eu 3+ -doped BeF 2 glass generated the Monte Carlo technique of statistical mechanics. The optical energy levels of Eu 3+ were calculated from a point charge model. Using the resulting spectra as data, it is shown that details of the structure of the rare-earth ion sites of the simulated glass cannot be reconstructed uniquely from the data. Based on these results, it is concluded that reliable glass structure cannot be deduced from optical spectra

Spectroscopic and visible luminescence properties of rare earth ions in lead fluoroborate glasses

Energy Technology Data Exchange (ETDEWEB)

Anjaiah, G. [Department of Physics, Osmania University, Hyderabad 500007 (India); Nayab Rasool, SK. [Department of Physics, Sri Venkateswara University, Tirupati 517502 (India); Kistaiah, P., E-mail: pkistaiah@yahoo.com [Department of Physics, Osmania University, Hyderabad 500007 (India)

2015-03-15

The lanthanide doped lead lithium calcium zinc fluoroborate glasses (LLCZFB:Ln) of composition 20PbF{sub 2}+10Li{sub 2}O+5Cao+5ZnO+59B{sub 2}O{sub 3}+1Ln{sub 2}O{sub 3} (where Ln=Sm, Eu and Dy in mol%) were prepared by conventional melt quench technique. The amorphous nature of these glasses was confirmed by X-ray diffraction studies. The glass transition temperatures (T{sub g}) were studied by DSC analysis. The glass structure and spectroscopic properties were investigated using optical absorption, vibrational and fluorescence spectra. The FT-IR spectra and Raman spectra reveal the presence of BO{sub 3}, BO{sub 4} and non-bridging oxygen's. The Judd–Ofelt intensity parameters Ω{sub λ} (λ=2, 4, 6) were determined from the spectral intensities of absorption bands. These parameters were used to calculate the radiative parameters such as radiative transition probability (A{sub R}), radiative life time (τ{sub R}) and branching ratio (β{sub r}) for various excited luminescent states of rare earth ions. The visible emission spectra for different rare earth ions were recorded by exciting the samples at different wavelengths and the decay rates for the different rare earth ions were measured. Using the emission spectra, full width half maxima (FWFM), stimulated emission cross section (σ{sup E}{sub p}) were evaluated. The nature of decay profiles of {sup 4}F{sub 9/2}, {sup 4}G{sub 5/2} and {sup 5}D{sub 0} states of Dy, Sm and Eu ions respectively are analyzed. Comparison of luminescence features of these glasses and also with those reported for different glass hosts indicates that the LLCZFB:Dy glass has strong luminescence in the visible region. - Highlights: • LLCZFB:Ln glasses are prepared with Ln: Sm, Eu and Dy. • Glasses are characterized by XRD, FTIR, Raman, absorption and emission spectra. • J–O theory is used to calculate different radiative properties. • Green, yellow and red emissions are observed. • Glasses are useful for the development

Interaction between rare-earth ions and amorphous silicon nanoclusters produced at low processing temperatures

Energy Technology Data Exchange (ETDEWEB)

Meldrum, A. [Department of Physics, University of Alberta, Edmonton, T6G2J1 (Canada)]. E-mail: ameldrum@ualberta.ca; Hryciw, A. [Department of Physics, University of Alberta, Edmonton, T6G2J1 (Canada); MacDonald, A.N. [Department of Physics, University of Alberta, Edmonton, T6G2J1 (Canada); Blois, C. [Department of Physics, University of Alberta, Edmonton, T6G2J1 (Canada); Clement, T. [Department of Electrical and Computer Engineering, University of Alberta, Edmonton, T6G2V4 (Canada); De Corby, R. [Department of Electrical and Computer Engineering, University of Alberta, Edmonton, T6G2V4 (Canada); Wang, J. [Department of Physics, Chinese University of Hong Kong, Shatin, Hong Kong (China); Li Quan [Department of Physics, Chinese University of Hong Kong, Shatin, Hong Kong (China)

2006-12-15

Temperatures of 1000 deg. C and higher are a significant problem for the incorporation of erbium-doped silicon nanocrystal devices into standard silicon technology, and make the fabrication of contacts and reflectors in light emitting devices difficult. In the present work, we use energy-filtered TEM imaging techniques to show the formation of size-controlled amorphous silicon nanoclusters in SiO films annealed between 400 and 500 deg. C. The PL properties of such films are characteristic of amorphous silicon, and the spectrum can be controlled via a statistical size effect-as opposed to quantum confinement-that has previously been proposed for porous amorphous silicon. Finally, we show that amorphous nanoclusters sensitize the luminescence from the rare-earth ions Er, Nd, Yb, and Tm with excitation cross-sections similar in magnitude to erbium-doped silicon nanocrystal composites, and with a similar nonresonant energy transfer mechanism.

Enhancing photovoltaic performance of dye-sensitized solar cell by rare-earth doped oxide of Lu2O3:(Tm3+, Yb3+)

International Nuclear Information System (INIS)

Li Qingbei; Lin Jianming; Wu Jihuai; Lan Zhang; Wang Yue; Peng Fuguo; Huang Miaoliang

2011-01-01

Highlights: → Tm 3+ /Yb 3+ codoped oxide is introduced into the TiO 2 film in dye-sensitized solar cell. → The RE improves light harvest via conversion luminescence and increases photocurrent. → The RE elevates the oxide film energy level and increases the cell photovoltage. → The cell efficiency is increased by 11.1% compared to the cell lacking of RE doping. - Abstract: In order to increase of the photocurrent, photovoltage and energy conversion efficiency of dye-sensitized solar cell (DSSC), rare-earth doped oxide of Lu 2 O 3 :(Tm 3+ , Yb 3+ ) is prepared and introduced into the TiO 2 film in the DSSC. As a luminescence medium, Lu 2 O 3 :(Tm 3+ , Yb 3+ ) improves incident light harvest via a conversion luminescence process and increases photocurrent; as a p-type dopant, the rare-earth ions elevate the energy level of the oxide film and increase the photovoltage. Under a simulated solar light irradiation of 100 mW cm -2 , the light-to-electric energy conversion efficiency of the DSSC with Lu 2 O 3 :(Tm 3+ , Yb 3+ ) doping reaches 6.63%, which is increased by 11.1% compared to the DSSC without Lu 2 O 3 :(Tm 3+ , Yb 3+ ) doping.

Study on rare earths complexes separation by means of different type of ion exchangers

International Nuclear Information System (INIS)

Hubicka, H.

1990-01-01

The applicability of different types of ion exchangers for purification and separation of rare earths complexes has been examined. The experimental work has been carried out on 14 chelating ion exchangers. The investigation results proved the great usefulness chelating ion exchangers especially of amino acid and phosphorus-type. Application of that type ion exchangers in column chromatographic process gave the excellent rare earths separation as well as enabled to obtain their preparates of high purity. 218 refs, 21 figs, 27 tabs

Solution thermodynamics of rare-earth metal ions - physicochemical study-

Energy Technology Data Exchange (ETDEWEB)

Amerkhanova, Sh K; Shlyapov, R M; Uali, A S [Buketov Karaganda state university, University str., 28, Karaganda, 100028 (Kazakhstan)], E-mail: amerkhanova_sh@mail.ru

2009-02-01

The results of the studying of interactions in multicomponent systems 'polyvinyl alcohol (PVA) - rare-earth element ion - nitrate of sodium - water' are represented. It is established that for rubidium (I) ions temperature and ionic strength is render destroying action, and for yttrium (III) ions the influence of these factors has return character which is connected with features of an electronic structure of metal ion. It is revealed that a dominating role of non-electrostatic formation composed, hence, the formation of donor-acceptor connection of 'metal - ligand' occurs through atom of oxygen.

Influence of rare-earth ions on SiO{sub 2}-Na{sub 2}O-RE{sub 2}O{sub 3} glass structure

Energy Technology Data Exchange (ETDEWEB)

Johnson, J A [Department of Materials Science and Engineering, University of Tennessee Space Institute, Tullahoma, TN 37388 (United States); Benmore, C J [X-ray Science Division, Argonne National Laboratory, Argonne, IL 60439 (United States); Holland, D [Department of Physics, University of Warwick, CV4 7AL (United Kingdom); Du, J [Department of Material Science and Engineering, University of North Texas, Denton, TX 76203 (United States); Beuneu, B [Laboratoire Leon Brillouin, CEA-CNRS, CEA/Saclay, F-91191 Gif-sur-Yvette (France); Mekki, A, E-mail: jjohnson@utsi.edu [Department of Physics, King Fahd University of Petroleum and Minerals, Dhahran 31261 (Saudi Arabia)

2011-02-16

Praseodymium and europium sodium silicate glasses of nominal composition (SiO{sub 2}){sub 0.70-x}(Na{sub 2}O){sub 0.30}(RE{sub 2}O{sub 3}){sub x}, where RE is the rare earth and 0 {<=} x {<=} 0.10, were studied by neutron and high-energy x-ray scattering and classical molecular dynamics simulations. The observation of a significant x-ray intensity in doped as compared to un-doped glasses is indicative of RE-RE correlations at a distance of {approx} 3.7-3.9 A, much shorter than would be expected for a homogeneous distribution, suggesting that clustering of the rare-earth cations occurs in both these glass systems at low concentrations. Above x = 0.075 (nominal), minimal changes in this region indicate that the RE atoms are incorporated much more randomly into the glass structure. The molecular dynamics simulations suggest that the rare-earth ions enter the sodium-rich regions in the sodium silicate glasses and act as modifiers. A cluster analysis performed on the model systems indicates that the tendency for clustering is higher in praseodymium-containing glasses than in the europium glasses.

On the single-ion Magnetic Anisotropy of the Rare-Earth Metals

DEFF Research Database (Denmark)

Kolmakova, N.P.; Tishin, A.M.; Bohr, Jakob

1996-01-01

The temperature dependences of the single-ion magnetic anisotropy constants for Tb and Dy metals are calculated in terms of the multipole moments of the rare-earth ions utilizing the available crystal-field parameters. The results are compared with the existing experimental data....

Contributed Review: A review of the investigation of rare-earth dopant profiles in optical fibers

Energy Technology Data Exchange (ETDEWEB)

Sidiroglou, F.; Baxter, G. [Optical Technology Research Laboratory, College of Engineering and Science, Victoria University, P.O. Box 14428, Melbourne, VIC 8001 (Australia); Roberts, A. [School of Physics, The University of Melbourne, Melbourne, VIC 3010 (Australia)

2016-04-15

Rare-earth doped optical fibers have captivated the interest of many researchers around the world across the past three decades. The growth of this research field has been stimulated primarily through their application in optical communications as fiber lasers and amplifiers, although rare-earth doped optical fiber based devices are now finding important uses in many other scientific and industrial areas (for example, medicine, sensing, the military, and material processing). Such wide commercial interest has provided a strong incentive for innovative fiber designs, alternative glass compositions, and novel fabrication processes. A prerequisite for the ongoing progress of this research field is developing the capacity to provide high resolution information about the rare-earth dopant distribution profiles within the optical fibers. This paper constitutes a comprehensive review of the imaging techniques that have been utilized in the analysis of the distribution of the rare-earth ion erbium within the core of optical fibers.

Dynamic population gratings in rare-earth-doped optical fibres

Energy Technology Data Exchange (ETDEWEB)

Stepanov, Serguei [Optics Department, CICESE, km.107 carr. Tijuana-Ensenada, Ensenada, 22860, BC (Mexico)], E-mail: steps@cicese.mx

2008-11-21

Dynamic Bragg gratings can be recorded in rare-earth (e.g. Er, Yb) doped optical fibres by two counter-propagating mutually coherent laser waves via local saturation of the fibre optical absorption or gain (in optically pumped fibres). Typical recording cw light power needed for efficient grating formation is of sub-mW-mW scale which results in characteristic recording/erasure times of 10-0.1 ms. This review paper discusses fundamental aspects of the population grating formation, their basic properties, relating wave-mixing processes and also considers different applications of these dynamic gratings in single-frequency fibre lasers, tunable filters, optical fibre sensors and adaptive interferometry.

Dynamic population gratings in rare-earth-doped optical fibres

International Nuclear Information System (INIS)

Stepanov, Serguei

2008-01-01

Dynamic Bragg gratings can be recorded in rare-earth (e.g. Er, Yb) doped optical fibres by two counter-propagating mutually coherent laser waves via local saturation of the fibre optical absorption or gain (in optically pumped fibres). Typical recording cw light power needed for efficient grating formation is of sub-mW-mW scale which results in characteristic recording/erasure times of 10-0.1 ms. This review paper discusses fundamental aspects of the population grating formation, their basic properties, relating wave-mixing processes and also considers different applications of these dynamic gratings in single-frequency fibre lasers, tunable filters, optical fibre sensors and adaptive interferometry.

Rare earth doped M-type hexaferrites; ferromagnetic resonance and magnetization dynamics

Directory of Open Access Journals (Sweden)

Vipul Sharma

2018-05-01

Full Text Available M-type hexagonal barium ferrites come in the category of magnetic material that plays a key role in electromagnetic wave propagation in various microwave devices. Due to their large magnetic anisotropy and large magnetization, their operating frequency exceeds above 50 GHz. Doping is a way to vary its magnetic properties to such an extent that its ferromagnetic resonance (FMR response can be tuned over a broad frequency band. We have done a complete FMR study of rare earth elements neodymium (Nd and samarium (Sm, with cobalt (Co as base, doped hexaferrite nanoparticles (NPs. X-ray diffractometry, vibrating sample magnetometer (VSM, and ferromagnetic resonance (FMR techniques were used to characterize the microstructure and magnetic properties of doped hexaferrite nanoparticles. Using proper theoretical electromagnetic models, various parameters are extracted from FMR data which play important role in designing and fabricating high-frequency microwave devices.

Crystal-field investigations of rare-earth-doped wide band gap semiconductors

CERN Multimedia

Muller, S; Wahl, U

Crystal field investigations play a central role in the studies of rare earth doped semiconductors. Optical stark level spectroscopy and lattice location studies of radioactive rare earth isotopes implanted at ISOLDE have provided important insight into these systems during the last years. It has been shown that despite a major site preference of the probe atoms in the lattice, several defect configurations do exist. These sites are visible in the optical spectra but their origin and nature aren't deducible from these spectra alone. Hyperfine measurements on the other hand should reveal these defect configurations and yield the parameters necessary for a description of the optical properties at the atomic scale. In order to study the crystal field with this alternative approach, we propose a new concept for perturbed $\\gamma\\gamma$-angular correlation (PAC) experiments at ISOLDE based on digital signal processing in contrast to earlier analog setups. The general functionality of the spectrometer is explained ...

Towards the development of new phosphors with reduced content of rare earth elements: Structural and optical characterization of Ce:Tb: Al{sub 2}SiO{sub 5}

Energy Technology Data Exchange (ETDEWEB)

Chiriu, D.; Stagi, L.; Carbonaro, C.M.; Corpino, R. [Dipartimento di Fisica, Università degli Studi di Cagliari, S.P.n°8 Km 0, 700, I-09042 Monserrato (Italy); Casula, M.F. [Dipartimento di Scienze Chimiche e Geologiche and INSTM, Università di Cagliari, S.P.n°8 Km 0, 700, I-09042 Monserrato (Italy); Ricci, P.C., E-mail: carlo.ricci@dsf.unica.it [Dipartimento di Fisica, Università degli Studi di Cagliari, S.P.n°8 Km 0, 700, I-09042 Monserrato (Italy)

2016-05-15

Highlights: • A new promising inert matrix as host of luminescent ions is proposed. • Al2SiO5 matrix is free from Rare earths (critical raw materials). • Doping the matrix with Ce and Tb we obtain an efficient green emitter. • Cerium acts as sensitizer for Terbium emission. - Abstract: A new promising inert matrix as host of luminescent ions is proposed. Al2SiO5 samples, doped with rare earths (Ce, Tb single doped and co-doped) are proposed as good prospect for the development of new UV–vis converter with reduced content of rare earths elements. Structural characterization by Raman, XRD spectroscopy and TEM imaging reveals the sillimanite phase and nano sized dimension of the investigated powders. Optical characterization by steady time and time resolved emission spectroscopy for the single doped and co-doped samples allows to identify an efficient energy transfer from Ce to Tb ions under near UV excitation wavelength. The intense green emission observed in the Ce:Tb co-doped Al2SiO5 system suggests its potential application as efficient blue pumped green emitter phosphor to be exploited for white LED: to this purpose we tested the compound in combination with a red emitting doping ion recording for Ce:Tb:Cr:ASO system a correlated color temperature of 6720 K.

Photo- and electro-luminescence of rare earth doped ZnO electroluminors at liquid nitrogen temperature

International Nuclear Information System (INIS)

Bhushan, S.; Kaza, B.R.; Pandey, A.N.

1981-01-01

Photo (PL) and electroluminescent (EL) spectra of some rare earth (La, Gd, Er or Dy) doped ZnO electroluminors have been investigated at liquid nitrogen temperature (LNT) and compared with their corresponding results at room temperature (RT). In addition to three bands observed at RT, one more band on the higher wavelength side appears in EL spectra. Spectral shift with the exciting intensity at LNT supports the donor-acceptor (DA) model in which the rare earths form the donor levels. From the temperature dependent studies of PL and EL brightness, the EL phenomenon is found to be more susceptible to traps. (author)

Radiation damage produced by swift heavy ions in rare earth phosphates

International Nuclear Information System (INIS)

Romanenko, Anton

2017-01-01

This work is devoted to the study of radiation damage produced by swift heavy ions in rare earth phosphates, materials that are considered as perspective for radioactive waste storage. Single crystals of rare earth phosphates were exposed to 2.1 GeV gold (Au) and 1.5 GeV xenon (Xe) ions of and analyzed mainly by Raman spectroscopy. All phosphates were found almost completely amorphous after the irradiation by 2.1 GeV Au ions at a fluence of 1 x 10 13 ions/cm 2 . Radiation-induced changes in the Raman spectra include the intensity decrease of all Raman bands accompanied by the appearance of broad humps and a reduction of the pronounced luminescence present in virgin samples. Analyzing the Raman peak intensities as a function of irradiation fluence allowed the calculation of the track radii for 2.1 GeV Au ions in several rare earth phosphates, which appear to be about 5.0 nm for all studied samples. Series of samples were studied to search for a trend of the track radius depending on the rare earth element (REE) cation. Among the monoclinic phosphates both Raman and small-angle X-ray scattering (SAXS) suggest no significant change of the track radius with increasing REE mass. In contrast, within the tetragonal phosphates Raman spectroscopy data suggests a possible slight decreasing trend of the track radius with the increase of REE atomic number. That finding, however, requires further investigation due to the low reliability of the qualitative Raman analysis. Detailed analysis of Raman spectra in HoPO 4 showed the increase of peak width at the initial stage of the irradiation and subsequent decrease to a steady value at higher fluences. This observation suggested the existence of a defect halo around the amorphous tracks in HoPO 4 . Raman peaks were found to initially shift to lower wavenumbers with reversing this trend at the fluence of 5 x 10 11 for NdPO 4 and 1 x 10 12 ions/cm 2 for HoPO 4 . At the next fluence steps peaks moved in the other direction, passed

Resonance electronic Raman scattering in rare earth crystals

International Nuclear Information System (INIS)

Williams, G.M.

1988-01-01

The intensities of Raman scattering transitions between electronic energy levels of trivalent rare earth ions doped into transparent crystals were measured and compared to theory. A particle emphasis was placed on the examination of the effect of intermediate state resonances on the Raman scattering intensities. Two specific systems were studied: Ce 3+ (4f 1 ) in single crystals of LuPO 4 and Er 3+ (4f 11 ) in single crystals of ErPO 4 . 134 refs., 92 figs., 33 tabs

Magnetic properties of Kramers rare earth ions in aluminium and gallium garnets

International Nuclear Information System (INIS)

Capel, H.

1964-01-01

The magnetic properties of Kramers rare earth ions in aluminium and gallium garnets (MAlG and MGaG) are discussed by means of a molecular field treatment. The symmetry properties of the space group permit to establish a parametrization for the magnetic dipolar and exchange couplings. The magnetic properties of the system can be expressed in terms of these parameters and the g factors of the rare earth ions. We have calculated the transition temperatures, the sub-lattice magnetizations, the susceptibility in the paramagnetic region and the antiferromagnetic susceptibility for a special type of magnetic ordering. The influence of the excited Kramers doublets is described by means of a generalization of the usual g tensor. (authors) [fr

Monitoring the orientation of rare-earth-doped nanorods for flow shear tomography

NARCIS (Netherlands)

Kim, J.; Michelin, S.; Hilbers, M.; Martinelli, L.; Chaudan, E.; Amselem, G.; Fradet, E.; Boilot, J.-P.; Brouwer, A.M.; Baroud, C.N.; Peretti, J.; Gacoin, T.

Rare-earth phosphors exhibit unique luminescence polarization features originating from the anisotropic symmetry of the emitter ion's chemical environment. However, to take advantage of this peculiar property, it is necessary to control and measure the ensemble orientation of the host particles with

Scintillation property of rare earth-free SnO-doped oxide glass

OpenAIRE

Masai, Hirokazu; Yanagida, Takayuki; Fujimoto, Yutaka; Koshimizu, Masanori; Yoko, Toshinobu

2012-01-01

The authors have demonstrated scintillation of rare earth (RE)-free Sn-doped oxide glass by excitation of ionizing radiation. It is notable that light emission is attained for RE-free transparent glass due to s[2]-sp transition of Sn[2+] centre and the emission correlates with the excitation band at 20 eV. We have also demonstrated that excitation band of emission centre can be tuned by the chemical composition of the host glass. The present result is valuable not only for design of RE-free i...

Red-emitting alkaline-earth rare-earth pentaoxometallates powders ...

Indian Academy of Sciences (India)

Moisture-insensitive metal carboxylates that are mostly liquids at room temperature have been first applied to ... alkaline-earth ion, or possibly even a rare-earth ion and alkali metal ... sion spectra of the powders were recorded on a fluorescent.

No Giant Two-Ion Anisotropy in the Heavy-Rare-Earth Metals

DEFF Research Database (Denmark)

Lindgård, Per-Anker

1976-01-01

A new Bose-operator expansion of tensor operators is applied to the heavy-rare-earth metals. The Er data for the cone phase have been analyzed successfully with single-ion anisotropy and isotropic exchange interaction. The Tb data can be understood on the same basis. The previously found large two......-ion anisotropy was due to an inadequate treatment of the large single-ion anisotropy leading to an incorrect expression for the spin-wave energy....

Synthesis and structure of alkaline earth and rare earth metal doped C70

International Nuclear Information System (INIS)

Takenobu, Taishi; Iwasa, Yoshihiro; Ito, Takayoshi; Mitani, Tadaoki

2001-01-01

We have investigated the structure sequence of alkaline earth (A=Ba, Sr) and rare earth metal (R=Eu) doped C 70 binary system. X-ray diffraction measurements revealed that there exist at least four stable phases at x=3, 4, 6, and 9 in A x C 70 and two stable phases at x=3, and 9 in R x C 70 . Among them, structural models are presented for Ba 4 C 70 , Sr 3 C 70 , and Eu 3 C 70 . Ba 4 C 70 takes an analogous structure to orthorhombic Ba 4 C 60 . Sr 3 C 70 and Eu 3 C 70 have monoclinic cell and their diffraction patterns are quite similar to that of Sm 3 C 70 , which involves a unique C 70 -metal-C 70 dimer structure. Preliminary results of Raman spectroscopy and magnetization measurement suggest the highly reduction state for A 9 C 70 and ferromagnetic interaction for Eu x C 70

Radiation damage produced by swift heavy ions in rare earth phosphates

Energy Technology Data Exchange (ETDEWEB)

Romanenko, Anton

2017-02-13

This work is devoted to the study of radiation damage produced by swift heavy ions in rare earth phosphates, materials that are considered as perspective for radioactive waste storage. Single crystals of rare earth phosphates were exposed to 2.1 GeV gold (Au) and 1.5 GeV xenon (Xe) ions of and analyzed mainly by Raman spectroscopy. All phosphates were found almost completely amorphous after the irradiation by 2.1 GeV Au ions at a fluence of 1 x 10{sup 13} ions/cm{sup 2}. Radiation-induced changes in the Raman spectra include the intensity decrease of all Raman bands accompanied by the appearance of broad humps and a reduction of the pronounced luminescence present in virgin samples. Analyzing the Raman peak intensities as a function of irradiation fluence allowed the calculation of the track radii for 2.1 GeV Au ions in several rare earth phosphates, which appear to be about 5.0 nm for all studied samples. Series of samples were studied to search for a trend of the track radius depending on the rare earth element (REE) cation. Among the monoclinic phosphates both Raman and small-angle X-ray scattering (SAXS) suggest no significant change of the track radius with increasing REE mass. In contrast, within the tetragonal phosphates Raman spectroscopy data suggests a possible slight decreasing trend of the track radius with the increase of REE atomic number. That finding, however, requires further investigation due to the low reliability of the qualitative Raman analysis. Detailed analysis of Raman spectra in HoPO{sub 4} showed the increase of peak width at the initial stage of the irradiation and subsequent decrease to a steady value at higher fluences. This observation suggested the existence of a defect halo around the amorphous tracks in HoPO{sub 4}. Raman peaks were found to initially shift to lower wavenumbers with reversing this trend at the fluence of 5 x 10{sup 11} for NdPO{sub 4} and 1 x 10{sup 12} ions/cm{sup 2} for HoPO{sub 4}. At the next fluence steps

Determination of aminoglycoside antibiotics using complex compounds of chromotropic acid bisazoderivatives with rare earth ions

International Nuclear Information System (INIS)

Alykov, N.M.

1981-01-01

Studies of complex formation of bisazo derivatives of chromotropic acid with rare earth ions and aminoglycoside antibiotics have made it possible to choose carboxyarsenazo, orthanyl R and carboxynitrazo as highly sensitive reagents for determining aminoglycoside antibiotics. Conditions have been found for the formation of precipitates of different-ligand complexes containing rare earth ions, bisazo derivatives of chromotropic acid and aminogylcoside antibiotics. A procedure has been worked out of determining the antibiotics in biological samples with carboxyarsenazo [ru

The operator technique in the theory of the rare earth ion interaction with ligand nuclei

International Nuclear Information System (INIS)

Anikeenok, O.A.; Eremin, M.V.; Khutsishvili, O.G.

1986-01-01

The tensor structure of the operator of rare earth ion interaction with nuclei of close ligands conditioned by virtual processes of charge transport is established. It is taken into account that virtual processes of electron transport from the ligand can take place to the non-filled 4f-, void 5d- and 6s- and preliminarily excited 5p-shells of the rare earth ion. Effects of 4f- and 5d-state mixing by the odd crystal field are considered for the first time. In contrast to the usual multipole-dipole interaction the given one is characterized by anomalously greater significance of highest multipole momenta of the rare earth ion and in the common case it does not have axial symmetry. The theory is compared with data on double electron-nuclear resonance and radiofrequency discrete saturation, taking CaF 2 :Ce 3+ impurity centers as an example

Structural and optical studies of nano-structure silica gel doped with different rare earth elements, prepared by two different sol -gel techniques

International Nuclear Information System (INIS)

Battisha, I.K.; El Beyally, A.; Seliman, S.I.; El Nahrawi, A.S.

2005-01-01

Structural and optical characteristics of pure silica gel (silica-xerogel, SiO 2 ) and doped with different concentrations ranging from 1 up to 6% of some rare earth (REEs) ions such as, praseodymium Pr +3 ,and Europium Eu +3 , Erbium Er +3 and Holmium Ho +3 , ions, in the form of thin film and monolith materials were prepared by sol - gel technique, Using tetra-ethoxysilane as precursor materials, which are of particular interest for sol-gel integrated optics applications. Some structural and optical features of sol-gel derived monolith and thin films are analyzed and compared, namely the structure of nano-particle monolith and thin film silica-gel samples, based on X-ray diffraction (XRD). The types of structural information obtainable are compared in detail. It is show that the XRD spectra of a-cristobalite are obtained for the two type materials and even by doping with the four REEs ions. Optical measurements of monolith and thin films were also studied and compared, the normal transmission and specular reflection were measured. The refractive index were calculated and discussed

Multilayer Thermal Barrier Coating (TBC) Architectures Utilizing Rare Earth Doped YSZ and Rare Earth Pyrochlores

Science.gov (United States)

Schmitt, Michael P.; Rai, Amarendra K.; Bhattacharya, Rabi; Zhu, Dongming; Wolfe, Douglas E.

2014-01-01

To allow for increased gas turbine efficiencies, new insulating thermal barrier coatings (TBCs) must be developed to protect the underlying metallic components from higher operating temperatures. This work focused on using rare earth doped (Yb and Gd) yttria stabilized zirconia (t' Low-k) and Gd2Zr2O7 pyrochlores (GZO) combined with novel nanolayered and thick layered microstructures to enable operation beyond the 1200 C stability limit of current 7 wt% yttria stabilized zirconia (7YSZ) coatings. It was observed that the layered system can reduce the thermal conductivity by approximately 45 percent with respect to YSZ after 20 hr of testing at 1316 C. The erosion rate of GZO is shown to be an order to magnitude higher than YSZ and t' Low-k, but this can be reduced by almost 57 percent when utilizing a nanolayered structure. Lastly, the thermal instability of the layered system is investigated and thought is given to optimization of layer thickness.

Contribution to the study of rare earth separation by ion exchange, using ammonium lactate

International Nuclear Information System (INIS)

Gratot, I.

1958-01-01

Using the technique of chromatography on a column of Dowex 50 resin, heated to 87 deg. C, we have studied the separation of rare earths (from holmium to praseodymium) which may be produced with the cyclotron by heavy ions, α or protons. From an ammonium lactate solution M at pH 5, separations are carried out by varying the dilution as a function of the quantity of the target rare earth and of its position during elution. When weighable quantities of the rare earth (more than 5 mg) appear towards the end of the elution, the separation is little affected this case approaches that of a tracer mixture of rare earths; if on the other hand weighable quantities of the rare earth are washed through at the beginning of the chromatogram, the dilution must be adjusted in order to obtain a good separation. (author) [fr

Thermochemistry of rare earth doped uranium oxides LnxU1-xO2-0.5x+y (Ln = La, Y, Nd)

Science.gov (United States)

Zhang, Lei; Navrotsky, Alexandra

2015-10-01

Lanthanum, yttrium, and neodymium doped uranium dioxide samples in the fluorite structure have been synthesized, characterized in terms of metal ratio and oxygen content, and their enthalpies of formation measured by high temperature oxide melt solution calorimetry. For oxides doped with 10-50 mol % rare earth (Ln) cations, the formation enthalpies from constituent oxides (LnO1.5, UO2 and UO3 in a reaction not involving oxidation or reduction) become increasingly exothermic with increasing rare earth content, while showing no significant dependence on the varying uranium oxidation state. The oxidation enthalpy of LnxU1-xO2-0.5x+y is similar to that of UO2 to UO3 for all three rare earth doped systems. Though this may suggest that the oxidized uranium in these systems is energetically similar to that in the hexavalent state, thermochemical data alone can not constrain whether the uranium is present as U5+, U6+, or a mixture of oxidation states. The formation enthalpies from elements calculated from the calorimetric data are generally consistent with those from free energy measurements.

Magnetic, dielectric and microwave absorption properties of rare earth doped Ni–Co and Ni–Co–Zn spinel ferrites

Energy Technology Data Exchange (ETDEWEB)

Stergiou, Charalampos, E-mail: stergiou@cperi.certh.gr

2017-03-15

In this article we analyze the electromagnetic properties of rare earth substituted Ni–Co and Ni–Co–Zn cubic ferrites in the microwave band, along with their performance as microwave absorbing materials. Ceramic samples with compositions Ni{sub 0.5}Co{sub 0.5}Fe{sub 2−x}R{sub x}O{sub 4} and Ni{sub 0.25}Co{sub 0.5}Zn{sub 0.25}Fe{sub 2−x}R{sub x}O{sub 4} (R=Y and La, x=0, 0.02), fabricated with the solid state reaction method, were characterized with regard to the complex permeability μ*(f) and permittivity ε*(f) up to 20 GHz. The rare earth substitutions basically affect the microwave μ*(f) spectra and the dynamic magnetization mechanisms of domain wall motion and magnetization rotation. Key parameters for this effect are the reduced magnetocrystalline anisotropy and the created crystal inhomogeneities. Moreover, permittivity is increased with the Y and La content, due to the enhancement of the dielectric orientation polarization. Regarding the electromagnetic wave attenuation, the prepared ferrites exhibit narrowband return losses (RL) by virtue of the cancellation of multiple reflections, when their thickness equals an odd multiple of quarter-wavelength. Interestingly, the zero-reflection conditions are satisfied in the vicinity of the ferromagnetic resonance. As the rare earth doping shifts this mechanism to lower frequencies, loss peaks with RL>46 dB occur at 4.1 GHz and 5 GHz for Y and La-doped Ni–Co–Zn spinels, whereas peaks with RL>40 dB appear at 18 GHz and 19 GHz for Y and La-doped Ni–Co spinels, respectively. The presented experimental findings underline the potential of cubic ferrites with high Co concentration in the suppression of electromagnetic reflections well above the 1 GHz region. - Highlights: • Due to cation distribution, magnetic anisotropy drops in Y and La doped samples. • Microwave permeability spectra shift to lower frequencies with rare earth doping. • Permittivity is increased due to crystal modifications

Spectroscopies et modélisation de verres de silice dopés d'ions de terre rare - influence du co-dopage

OpenAIRE

Alombert-Goget , Guillaume

2007-01-01

This study concerns the role of a co-doping agent on the environment of the rare earth ions in silica glass and its consequences on the spectroscopy of the luminescent element. Two different co-doping agents were studied: aluminium and hafnium ions. The samples of doped and co-doped glasses were obtained by sol-gel process and were studied by different experimental methods: luminescence spectroscopy, FLN spectroscopy, Raman spectroscopy, and EXAFS spectroscopy. In parallel some numerical simu...

PHYSICAL AND ELECTRICAL PROPERTIES ENHANCEMENT OF RARE-EARTH DOPED-POTASSIUM SODIUM NIOBATE (KNN: A REVIEW

Directory of Open Access Journals (Sweden)

Akmal Mat Harttat Maziati

2015-06-01

Full Text Available Alkaline niobate mainly potassium sodium niobate, (KxNa1-x NbO3 (abreviated as KNN has long attracted attention as piezoelectric materials as its high Curie temperature (Tc and piezoelectric properties. The volatility of alkaline element (K, Na is, however detrimental to the stoichiometry of KNN, contributing to the failure to achieve high-density structure and lead to the formation of intrinsic defects. By partially doping of several rare-earth elements, the inherent defects could be improved significantly. Therefore, considerable attempts have been made to develop doped-KNN based ceramic materials with high electrical properties. In this paper, these research activities are reviewed, including dopants type and doping role in KNN perovskite structure.

New Erbium Doped Antimony Glasses for Laser and Glass ...

African Journals Online (AJOL)

Because of the special spectroscopic properties of the rare earth ions, rare earth doped glasses are widely used in bulk and fiber lasers or amplifiers. The modelling of lasers and searching for new laser transitions require a precise knowledge of the spectroscopic properties of rare earth ions in different host glasses.

Microstructural and electrical characteristics of rare earth oxides doped ZnO varistor films

Science.gov (United States)

Jiao, Lei; Mei, Yunzhu; Xu, Dong; Zhong, Sujuan; Ma, Jia; Zhang, Lei; Bao, Li

2018-02-01

ZnO-Bi2O3 varistor films doped with two kinds of rare earth element oxides (Lu2O3 and Yb2O3) were prepared by the sol-gel method. The effects of Lu2O3/Yb2O3 doping on the microstructure and electrical characteristics of ZnO-Bi2O3 varistor films were investigated. All samples show a homogenized morphology and an improved nonlinear relationship between the electric field (E) and current density (I). Both Yb2O3 and Lu2O3 doping can decrease the grain size of ZnO-Bi2O3 varistor films and improve the electrical properties, which have a positive effect on the development of ZnO varistor ceramics. Yb2O3 doping significantly increases the dielectric constant at low frequency. 0.2 mol. % Yb2O3 doped ZnO-Bi2O3 varistor films exhibit the highest nonlinear coefficient (2.5) and the lowest leakage current (328 μA) among Lu2O3/Yb2O3 doped ZnO-Bi2O3 varistor films. Similarly, 0.1 mol. % Lu2O3 doping increases the nonlinear coefficient to 1.9 and decrease the leakage current to 462 μA.

Luminescence investigations of rare earth doped lead-free borate glasses modified by MO (M = Ca, Sr, Ba)

Energy Technology Data Exchange (ETDEWEB)

Janek, Joanna, E-mail: janek.joanna@gmail.com; Sołtys, Marta; Żur, Lidia; Pietrasik, Ewa; Pisarska, Joanna; Pisarski, Wojciech A.

2016-09-01

Series of lead-free borate glasses with different oxide modifiers and lanthanide ions were prepared. The effect of oxide modifiers MO (M = Ca, Sr, Ba) on spectroscopic properties of trivalent Ln{sup 3+} (Ln = Eu, Er, Pr) were systematically investigated. Especially, the luminescence spectra of Ln{sup 3+}-doped lead-free borate glasses are presented and discussed in relation to the impact of selective components (CaO, SrO and BaO). Several spectroscopic parameters, such as the fluorescence intensity ratio R/O (Eu{sup 3+}) and measured luminescence lifetimes for the {sup 5}D{sub 0} (Eu{sup 3+}), {sup 4}I{sub 13/2} (Er{sup 3+}) and {sup 1}D{sub 2} (Pr{sup 3+}) excited states of lanthanide ions were analyzed in details. The research proved that spectroscopic properties of trivalent Ln{sup 3+} depend significantly on kind of presence oxide modifiers MO (M = Ca, Sr, Ba) in glass host matrices. - Highlights: • Luminescence of Ln{sup 3+}-doped borate glasses was presented and discussed. • Effect of glass modifiers on spectroscopic properties of rare earths was studied. • Measured luminescence lifetimes of Ln{sup 3+} (Ln = Eu, Er, Pr) were analyzed. • Luminescence intensity ratios R/O (Eu{sup 3+}) were determined.

Structural elucidation and magnetic behavior evaluation of rare earth (La, Nd, Gd, Tb, Dy) doped BaCoNi-X hexagonal nano-sized ferrites

International Nuclear Information System (INIS)

Majeed, Abdul; Khan, Muhammad Azhar; Raheem, Faseeh ur; Hussain, Altaf; Iqbal, F.; Murtaza, Ghulam; Akhtar, Majid Niaz; Shakir, Imran; Warsi, Muhammad Farooq

2016-01-01

Rare-earth (RE=La 3+ , Nd 3+ , Gd 3+ , Tb 3+ , Dy 3+ ) doped Ba 2 NiCoRE x Fe 28−x O 46 (x=0.25) hexagonal ferrites were synthesized for the first time via micro-emulsion route, which is a fast chemistry route for obtaining nano-sized ferrite powders. These nanomaterials were investigated by X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR), as well as vibrating sample magnetometer (VSM). The XRD analysis exhibited that all the samples crystallized into single X-type hexagonal phase. The crystalline size calculated by Scherrer's formula was found in the range 7–19 nm. The variations in lattice parameters elucidated the incorporation of rare-earth cations in these nanomaterials. FTIR absorption spectra of these X-type ferrites were investigated in the wave number range 500–2400 cm −1. Each spectrum exhibited absorption bands in the low wave number range, thereby confirming the X-type hexagonal structure. The enhancement in the coercivity was observed with the doping of rare-earth cations. The saturation magnetization was lowered owing to the redistribution of rare-earth cations on the octahedral site (3b VI ). The higher values of coercivity (664–926 Oe) of these nanomaterials suggest their use in longitudinal recording media. - Graphical abstract: Nano-sized rare-earth (RE=La 3+ , Nd 3+ , Gd 3+ , Tb 3+ , Dy 3+ ) doped Ba 2 NiCoRE x Fe 28−x O 46 (x=0.25) hexagonal ferrites were synthesized for the first time via micro-emulsion route and the crystallite size was found in the range 7–19 nm. The enhancement in the coercivity was observed with the doping of rare-earth cations. The higher values of coercivity (664–926 Oe) of these nanomaterials suggest their use in longitudinal recording media. - Highlights: • Micro-emulsion route was used to synthesize Ba 2 NiCoRE x Fe 28−x O 46 ferrites. • The crystallite size was found in the range 7–19 nm. • The rare-earth incorporation enhanced the coercivity (664–926 Oe). �

Spectroscopic study of trivalent rare earth ions in calcium nitrate hydrate melt

International Nuclear Information System (INIS)

Fujii, Toshiyuki; Asano, Hideki; Kimura, Takaumi; Yamamoto, Takeshi; Uehara, Akihiro; Yamana, Hajimu

2006-01-01

Influence of the water content to chemical status of trivalent rare earth ions in calcium nitrate hydrate melt was studied by spectroscopic techniques. Fluorescence spectrometry for Eu(III) in Ca(NO 3 ) 2 .RH 2 O and electronic absorption spectrometry for Nd(III) in Ca(NO 3 ) 2 .RH 2 O were performed for analyzing the changing coordination symmetries through the changes in their hypersensitive transitions. Raman spectroscopic study and EXAFS study were performed for Y(NO 3 ) 3 solutions and Y(III) in Ca(NO 3 ) 2 .RH 2 O for analyzing the oxygen bonding to Y(III). Luminescence lifetime study of Eu(III) and Dy(III) in Ca(NO 3 ) 2 .RH 2 O was performed for evaluating the hydration number changes. Results of these spectroscopic studies indicated that, with the decrease of water content (R), the hydration number decreases while the interaction between trivalent rare earth ion and nitrate ion increases. It was also revealed that the symmetry of the coordination sphere gets distorted gradually by this interaction

Bistable luminescence of trivalent rare-earth ions in crystals

International Nuclear Information System (INIS)

Sole, Jose Garcia; Ramirez O, Maria de la; Rodenas, Airan; Jaque, Daniel; Bausa, Luisa; Bettinelli, Marco; Speghini, Adolfo; Cavalli, Enrico; Ivleva, Lioudmila

2006-01-01

In this work, we have examined three new bistable systems based on the luminescence of three different crystals activated with trivalent rare earth ions. We have focussed our attention on Yb 3+ ions activators, for which the most relevant results are obtained. The first crystal, Sr 0.6 Ba 0.4 Nb 2 O 6 , is a ferroelectric material with a relatively low phase transition temperature (∼370 K), which provides bistability in the luminescence of Yb 3+ ions due to the thermal hysteresis associated with phase transition. The second crystal, LiNbO 3 , provides an intrinsic bistability in the luminescence of Yb 3+ ions, which is driven by changes in the excitation intensity. In the third crystal, NdPO 4 , a new mechanism of excitation intensity driven bistability is obtained when activated with Yb 3+ ions, due to a interplay between the Nd 3+ ↔Yb 3+ energy transfer and back transfer processes

China's rare-earth industry

Science.gov (United States)

Tse, Pui-Kwan

2011-01-01

Introduction China's dominant position as the producer of over 95 percent of the world output of rare-earth minerals and rapid increases in the consumption of rare earths owing to the emergence of new clean-energy and defense-related technologies, combined with China's decisions to restrict exports of rare earths, have resulted in heightened concerns about the future availability of rare earths. As a result, industrial countries such as Japan, the United States, and countries of the European Union face tighter supplies and higher prices for rare earths. This paper briefly reviews China's rare-earth production, consumption, and reserves and the important policies and regulations regarding the production and trade of rare earths, including recently announced export quotas. The 15 lanthanide elements-lanthanum, cerium, praseodymium, neodymium, promethium, samarium, europium, gadolinium, terbium, dysprosium, holmium, erbium, thulium, ytterbium, and lutetium (atomic numbers 57-71)-were originally known as the rare earths from their occurrence in oxides mixtures. Recently, some researchers have included two other elements-scandium and yttrium-in their discussion of rare earths. Yttrium (atomic number 39), which lies above lanthanum in transition group III of the periodic table and has a similar 3+ ion with a noble gas core, has both atomic and ionic radii similar in size to those of terbium and dysprosium and is generally found in nature with lanthanides. Scandium (atomic number 21) has a smaller ionic radius than yttrium and the lanthanides, and its chemical behavior is intermediate between that of aluminum and the lanthanides. It is found in nature with the lanthanides and yttrium. Rare earths are used widely in high-technology and clean-energy products because they impart special properties of magnetism, luminescence, and strength. Rare earths are also used in weapon systems to obtain the same properties.

Hydrothermal synthesis, characterization and up/down-conversion luminescence of barium rare earth fluoride nanocrystals

International Nuclear Information System (INIS)

Jia, Li-Ping; Zhang, Qiang; Yan, Bing

2014-01-01

Graphical abstract: Lanthanide ions doped bare earth rare earth fluoride nanocrystals are synthesized by hydrothermal technology and characterized. The down/up-conversion luminescence of them are discussed. - Highlights: • Mixed hydrothermal system H 2 O–OA (EDA)–O-A(LO-A) is used for synthesis. • Barium rare earth fluoride nanocrystals are synthesized comprehensively. • Luminescence for down-conversion and up-conversion are obtained for these systems. - Abstract: Mixed hydrothermal system H 2 O–OA (EDA)–O-A(LO-A) is developed to synthesize barium rare earth fluorides nanocrystals (OA = oleylamine, EDA = ethylenediamine, O-A = oleic acid and LO-A = linoleic acid). They are presented as BaREF 5 (RE = Ce, Pr, Nd, Eu, Gd, Tb, Dy, Y, Tm, Lu) and Ba 2 REF 7 (RE = La, Sm, Ho, Er, Yb). The influence of reaction parameters (rare earth species, hydrothermal system and temperature) is checked on the phase and shape evolution of the fluoride nanocrystals. It is found that reaction time and temperature of these nanocrystals using EDA (180 °C, 6 h) is lower than those of them using OA (220 °C, 10 h). The photoluminescence properties of these fluorides activated by some rare earth ions (Nd 3+ , Eu 3+ , Tb 3+ ) are studied, and especially up-conversion luminescence of the four fluoride nanocrystal systems (Ba 2 LaF 7 :Yb, Tm(Er), Ba 2 REF 7 :Yb, Tm(Er) (RE = Gd, Y, Lu)) is observed

Coprecipitation of rare earth elements with hydroxyapatite

International Nuclear Information System (INIS)

Fujino, Osamu

1979-01-01

The distribution behavior of trace rare earth elements between an aqueous phase and hydroxyapatite crystals was investigated. The apatite prepared by adding phosphate ion extremely slowly to an aqueous solution containing calcium, rare earth elements, ethylenediamine and nitrilotriacetate ion at 80 0 C. Apparently the coprecipitation reaction seems to be anomalous, because the apparent distribution coefficient did not have a constant value through the reaction. But when the true distribution coefficient was calculated by using the thermodynamic data at 80 0 C, it was revealed that rare earth ions were coprecipitated obeying logarithmic distribution law. The true distribution coefficient values of trivalent yttrium, scandium, europium and cerium ions were about 10sup(7.3), 10sup(9.8), 10sup(7.4) and 10sup(6.5) respectively. (author)

Cathodoluminescence of rare earth implanted Ga2O3 and GeO2 nanostructures.

Science.gov (United States)

Nogales, E; Hidalgo, P; Lorenz, K; Méndez, B; Piqueras, J; Alves, E

2011-07-15

Rare earth (RE) doped gallium oxide and germanium oxide micro- and nanostructures, mostly nanowires, have been obtained and their morphological and optical properties have been characterized. Undoped oxide micro- and nanostructures were grown by a thermal evaporation method and were subsequently doped with gadolinium or europium ions by ion implantation. No significant changes in the morphologies of the nanostructures were observed after ion implantation and thermal annealing. The luminescence emission properties have been studied with cathodoluminescence (CL) in a scanning electron microscope (SEM). Both β-Ga(2)O(3) and GeO(2) structures implanted with Eu show the characteristic red luminescence peak centered at around 610 nm, due to the (5)D(0)-(7)F(2) Eu(3+) intraionic transition. Sharpening of the luminescence peaks after thermal annealing is observed in Eu implanted β-Ga(2)O(3), which is assigned to the lattice recovery. Gd(3+) as-implanted samples do not show rare earth related luminescence. After annealing, optical activation of Gd(3+) is obtained in both matrices and a sharp ultraviolet peak centered at around 315 nm, associated with the Gd(3+) (6)P(7/2)-(8)S(7/2) intraionic transition, is observed. The influence of the Gd ion implantation and the annealing temperature on the gallium oxide broad intrinsic defect band has been analyzed.

Cathodoluminescence of rare earth implanted Ga2O3 and GeO2 nanostructures

International Nuclear Information System (INIS)

Nogales, E; Hidalgo, P; Mendez, B; Piqueras, J; Lorenz, K; Alves, E

2011-01-01

Rare earth (RE) doped gallium oxide and germanium oxide micro- and nanostructures, mostly nanowires, have been obtained and their morphological and optical properties have been characterized. Undoped oxide micro- and nanostructures were grown by a thermal evaporation method and were subsequently doped with gadolinium or europium ions by ion implantation. No significant changes in the morphologies of the nanostructures were observed after ion implantation and thermal annealing. The luminescence emission properties have been studied with cathodoluminescence (CL) in a scanning electron microscope (SEM). Both β-Ga 2 O 3 and GeO 2 structures implanted with Eu show the characteristic red luminescence peak centered at around 610 nm, due to the 5 D 0 - 7 F 2 Eu 3+ intraionic transition. Sharpening of the luminescence peaks after thermal annealing is observed in Eu implanted β-Ga 2 O 3 , which is assigned to the lattice recovery. Gd 3+ as-implanted samples do not show rare earth related luminescence. After annealing, optical activation of Gd 3+ is obtained in both matrices and a sharp ultraviolet peak centered at around 315 nm, associated with the Gd 3+ 6 P 7/2 - 8 S 7/2 intraionic transition, is observed. The influence of the Gd ion implantation and the annealing temperature on the gallium oxide broad intrinsic defect band has been analyzed.

Evidence of dilute ferromagnetism in rare-earth doped yttrium aluminium garnet

Energy Technology Data Exchange (ETDEWEB)

Farr, Warrick G.; Goryachev, Maxim; Le Floch, Jean-Michel; Tobar, Michael E. [ARC Centre of Excellence for Engineered Quantum Systems, University of Western Australia, 35 Stirling Highway, Crawley, Western Australia 6009 (Australia); Bushev, Pavel [Experimentalphysik, Universität des Saarlandes, D-66123 Saarbrücken (Germany)

2015-09-21

This work demonstrates strong coupling regime between an erbium ion spin ensemble and microwave hybrid cavity-whispering gallery modes in a yttrium aluminium garnet dielectric crystal. Coupling strengths of 220 MHz and mode quality factors in excess of 10{sup 6} are demonstrated. Moreover, the magnetic response of high-Q modes demonstrates behaviour which is unusual for paramagnetic systems. This behaviour includes hysteresis and memory effects. Such qualitative change of the system's magnetic field response is interpreted as a phase transition of rare earth ion impurities. This phenomenon is similar to the phenomenon of dilute ferromagnetism in semiconductors. The clear temperature dependence of the phenomenon is demonstrated.

Rare Earth Polyoxometalates.

Science.gov (United States)

Boskovic, Colette

2017-09-19

Longstanding and important applications make use of the chemical and physical properties of both rare earth metals and polyoxometalates of early transition metals. The catalytic, optical, and magnetic features of rare earth metal ions are well-known, as are the reversible multielectron redox and photoredox capabilities of polyoxomolybdates and polyoxotungstates. The combination of rare earth ions and polyoxometalates in discrete molecules and coordination polymers is of interest for the unique combination of chemical and physical properties that can arise. This Account surveys our efforts to synthesize and investigate compounds with rare earth ions and polyoxometalates (RE-POMs), sometimes with carboxylate-based organic coligands. Our general synthetic approach is "bottom-up", which affords well-defined nanoscale molecules, typically in crystalline form and amenable to single-crystal X-ray diffraction for structure determination. Our particular focus is on elucidation of the physical properties conferred by the different structural components with a view to ultimately being able to tune these properties chemically. For this purpose, we employ a variety of spectroscopic, magnetochemical, electrochemical, and scattering techniques in concert with theoretical modeling and computation. Studies of RE-POM single-molecule magnets (SMMs) have utilized magnetic susceptibility, inelastic neutron scattering, and ab initio calculations. These investigations have allowed characterization of the crystal field splitting of the rare earth(III) ions that is responsible for the SMM properties of slow magnetic relaxation and magnetization quantum tunneling. Such SMMs are promising for applications in quantum computing and molecular spintronics. Photophysical measurements of a family of hybrid RE-POMs with organic ligands have afforded insights into sensitization of Tb(III) and Eu(III) emission through both organic and polyoxometalate chromophores in the same molecule. Detailed

Rare-Earth Ions in Niobium-Based Devices as a Quantum Memory: Magneto-Optical Effects on Room Temperature Electrical Transport

Science.gov (United States)

2016-09-01

heterostructure can be used to implement cryogenic memory for superconducting digital computing. Our concept involves embedding rare-earth ions in...rare-earth neodymium by ion implantation in thin films of niobium and niobium-based heterostructure devices. We model the ion implantation process...the films and devices so they can properly designed and optimized for utility as quantum memory. We find that the magnetic field has a strong effect

Study of amorphous semiconductors doped with rare earths (Gd and Er) and conducting polymers by EPR techniques and magnetic susceptibility; Estudo de semicondutores amorfos dopados com terras raras (Gd e Er) e de polimeros condutores atraves das tecnicas de RPE e susceptibilidade magnetica

Energy Technology Data Exchange (ETDEWEB)

Sercheli, Mauricio da Silva

1999-07-01

This thesis involves the study of amorphous semiconductors and conducting polymers, which have been characterized by EPR and magnetic susceptibility measurements, and to a lesser extent by Raman spectroscopy and RBS. The semiconductors were studied using thin films of silicon doped with rare earth metals, e.g. erbium and gadolinium, which had their magnetic properties studied. Using these studies we could determine the state of valence of the rare earths as well as their concentrations in the silicon matrix. According to our results, the valence of the rare earth metal ions is 3+, and we were able to conclude that 4f electronic shells could not be used for the calculation of the conducting band in this system. Furthermore, the analysis of the data on the magnetic susceptibility of the Er{sup 3+} ion with cubic crystalline acting field, gave us the opportunity to estimate the overall splitting of their electronic states for the first time. The conducting polymers were studied using samples of poly(3-methylthiophene) doped with ClO{sub 4}{sup -}, which show a phase transition in the range of 230 K to 130 K. The electron paramagnetic resonance also gives important information on the crystallization, doping level and the presence of polarons or bipolarons in conducting polymers. (author)

Preparation and structure of carbonated calcium hydroxyapatite substituted with heavy rare earth ions

Energy Technology Data Exchange (ETDEWEB)

Yasukawa, Akemi, E-mail: yasukawa@cc.hirosaki-u.ac.jp [School of Home Economics, Faculty of Education, Hirosaki University, 1-bunkyo, Hirosaki, Aomori 036-8560 (Japan); Kandori, Kazuhiko [School of Chemistry, Osaka University of Education, 4-698-1 Asahigaoka, Kashiwara, Osaka 582-8582 (Japan); Tanaka, Hidekazu [Department of Material Science, Faculty of Science and Engineering, Shimane University, 1060 Nishikawatsu, Matsue, Shimane 690-8504 (Japan); Gotoh, Keiko [Faculty of Human Life and Environment, Nara Women' s University, Kita-uoya-nishi, Nara 630-8506 (Japan)

2012-05-15

Highlights: Black-Right-Pointing-Pointer LnCaHap solid solution particles were prepared using five types of heavy rare earth ions by a precipitation method. Black-Right-Pointing-Pointer The length and the crystallinity of the LnCaHap particles first increased and then decreased with increasing Ln{sup 3+} contents. Black-Right-Pointing-Pointer A series of YCaHap solid solution particles formed with Y/(Y + Ca) = 0-0.10 were investigated using various methods in detail. -- Abstract: Calcium hydroxyapatite (CaHap) particles substituted five types of heavy rare earth ions (Ln: Y{sup 3+}, Gd{sup 3+}, Dy{sup 3+}, Er{sup 3+} and Yb{sup 3+}) were synthesized using a precipitation method and characterized using various means. These Ln ions strongly affected the crystal phases and the structures of the products. With increasing Ln/(Ln + Ca) in the starting solution ([X{sub Ln}]), the length and the crystallinity of the particles first increased and then decreased. The rare earth metal-calcium hydroxyapatite (LnCaHap) solid solution particles were obtained at [X{sub Y}] {<=} 0.10 for substituting Y system and at [X{sub Ln}] {<=} 0.01-0.03 for substituting the other Ln systems. LnPO{sub 4} was mixed with LnCaHap at higher [X{sub Ln}] for all Ln systems. A series of yttrium-calcium hydroxyapatite (YCaHap) solid solutions with [X{sub Y}] = 0-0.10 were investigated using XRD, TEM, ICP-AES, IR and TG-DTA in detail.

Preparation and structure of carbonated calcium hydroxyapatite substituted with heavy rare earth ions

International Nuclear Information System (INIS)

Yasukawa, Akemi; Kandori, Kazuhiko; Tanaka, Hidekazu; Gotoh, Keiko

2012-01-01

Highlights: ► LnCaHap solid solution particles were prepared using five types of heavy rare earth ions by a precipitation method. ► The length and the crystallinity of the LnCaHap particles first increased and then decreased with increasing Ln 3+ contents. ► A series of YCaHap solid solution particles formed with Y/(Y + Ca) = 0–0.10 were investigated using various methods in detail. -- Abstract: Calcium hydroxyapatite (CaHap) particles substituted five types of heavy rare earth ions (Ln: Y 3+ , Gd 3+ , Dy 3+ , Er 3+ and Yb 3+ ) were synthesized using a precipitation method and characterized using various means. These Ln ions strongly affected the crystal phases and the structures of the products. With increasing Ln/(Ln + Ca) in the starting solution ([X Ln ]), the length and the crystallinity of the particles first increased and then decreased. The rare earth metal-calcium hydroxyapatite (LnCaHap) solid solution particles were obtained at [X Y ] ≤ 0.10 for substituting Y system and at [X Ln ] ≤ 0.01–0.03 for substituting the other Ln systems. LnPO 4 was mixed with LnCaHap at higher [X Ln ] for all Ln systems. A series of yttrium-calcium hydroxyapatite (YCaHap) solid solutions with [X Y ] = 0–0.10 were investigated using XRD, TEM, ICP-AES, IR and TG–DTA in detail.

Rare earths: occurrence, production and applications

International Nuclear Information System (INIS)

Murthy, T.K.S.; Mukherjee, T.K.

2002-01-01

The mining and processing of rare earth minerals, particularly of monazite, began in a modest way in 1880s for commercialized production of mantle for gas lighting. For all major applications up to mid-twentieth century- production of lighter flints, misch metal as a metallurgical alloying agent, colouring, decolourizing and polishing agents for glass, petroleum cracking catalysts and arc-carbons, unseparated or partially separated rare earths were adequate. These applications continue till today. With the development and industrial application of powerful techniques like ion exchange and solvent extraction for the separation of rare earths, the decades after 1960 saw increasing utilization of the specific properties of the individual rare earths. Some of these advanced technological applications include: special glass for optical systems including camera lenses, phosphors for colour television, cathode ray tubes and fluorescent lighting, X-ray intensification screens, high intensity permanent magnets, electro optical devices, lasers, hydrogen storage materials, hydride rechargeable batteries, photomagnetic data storage systems, autoexhaust catalysts, special ceramics of unusual toughness, artificial diamonds and nonpoisonous plastic colorants. The topics covered in the book include rare earths: their story identity, rare earth resources, processing of ores and recovery of mixed rare earths products, separation and purification of rare earths, nonmetallic applications of rare earths, rare earth metals: production and applications, rare earth alloys and their applications, analysis of rare earth, processing of rare earth resources in India by Indian Rare Earth Ltd. and availability and market conditions

Luminescence and structural properties of RbGdS.sub.2./sub. compounds doped by rare earth elements

Czech Academy of Sciences Publication Activity Database

Jarý, Vítězslav; Havlák, Lubomír; Bárta, J.; Mihóková, Eva; Nikl, Martin

2013-01-01

Roč. 35, č. 6 (2013), s. 1226-1229 ISSN 0925-3467 R&D Projects: GA TA ČR TA01011017 Institutional support: RVO:68378271 Keywords : luminescence * X-ray diffraction * crystal structure * optical materials * ternary sulfides * rare earth s doping Subject RIV: BH - Optics, Masers, Lasers Impact factor: 2.075, year: 2013

Studies on mixed ligand complexes of adenine and xanthine with some rare earth ions

International Nuclear Information System (INIS)

Rastogi, P.R.; Singh, Mamta; Nayan, Ram

1993-01-01

Interactions of 6-aminopurine (adenine, HA) and 2,6-dihydroxypurine (xanthine, HB) with trivalent rare earth ions Y, Tb, Dy, Ho, Er and Tm, have been studied by pH-titration methods in aqueous solution at 20 o (μ = 0.1 M KNO 3 ). The ligands in their mixtures with tripositive rare earth ions (M 3+ ) form a number of mixed ligand complexes, M 3+ -adenine-xanthine, M 3+ -(adenine) 2 -xanthine, M 3+ -adenine-(xanthine) 2 in addition to the binary complexes, M 3+ -(adenine), M 3+ -(adenine) 2 , M 3+ -(adenine) 3 , M 3+ -(xanthine), M 3+ -(xanthine) 2 and M 3+ -(xanthine) 3 . The stability constants of these complexes have been evaluated and the results discussed. (author). 13 refs., 1 fig., 1 tab

Structural elucidation and magnetic behavior evaluation of rare earth (La, Nd, Gd, Tb, Dy) doped BaCoNi-X hexagonal nano-sized ferrites

Energy Technology Data Exchange (ETDEWEB)

Majeed, Abdul, E-mail: abdulmajeed2276@gmail.com [Department of Physics, The Islamia University of Bahawalpur, Bahawalpur 63100 (Pakistan); Khan, Muhammad Azhar, E-mail: azhar.khan@iub.edu.pk [Department of Physics, The Islamia University of Bahawalpur, Bahawalpur 63100 (Pakistan); Raheem, Faseeh ur; Hussain, Altaf; Iqbal, F. [Department of Physics, The Islamia University of Bahawalpur, Bahawalpur 63100 (Pakistan); Murtaza, Ghulam [Centre for Advanced Studies in Physics, Government College University, Lahore 54000 (Pakistan); Akhtar, Majid Niaz [Department of Physics, COMSATS Institute of Information Technology, Lahore 54000 (Pakistan); Shakir, Imran [Deanship of Scientific Research, College of Engineering, King Saud University, PO Box 800, Riyadh 11421 (Saudi Arabia); Warsi, Muhammad Farooq [Department of Chemistry, The Islamia University of Bahawalpur, Bahawalpur 63100 (Pakistan)

2016-06-15

Rare-earth (RE=La{sup 3+}, Nd{sup 3+}, Gd{sup 3+}, Tb{sup 3+}, Dy{sup 3+}) doped Ba{sub 2}NiCoRE{sub x}Fe{sub 28−x}O{sub 46} (x=0.25) hexagonal ferrites were synthesized for the first time via micro-emulsion route, which is a fast chemistry route for obtaining nano-sized ferrite powders. These nanomaterials were investigated by X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR), as well as vibrating sample magnetometer (VSM). The XRD analysis exhibited that all the samples crystallized into single X-type hexagonal phase. The crystalline size calculated by Scherrer's formula was found in the range 7–19 nm. The variations in lattice parameters elucidated the incorporation of rare-earth cations in these nanomaterials. FTIR absorption spectra of these X-type ferrites were investigated in the wave number range 500–2400 cm{sup −1.} Each spectrum exhibited absorption bands in the low wave number range, thereby confirming the X-type hexagonal structure. The enhancement in the coercivity was observed with the doping of rare-earth cations. The saturation magnetization was lowered owing to the redistribution of rare-earth cations on the octahedral site (3b{sub VI}). The higher values of coercivity (664–926 Oe) of these nanomaterials suggest their use in longitudinal recording media. - Graphical abstract: Nano-sized rare-earth (RE=La{sup 3+}, Nd{sup 3+}, Gd{sup 3+}, Tb{sup 3+}, Dy{sup 3+}) doped Ba{sub 2}NiCoRE{sub x}Fe{sub 28−x}O{sub 46} (x=0.25) hexagonal ferrites were synthesized for the first time via micro-emulsion route and the crystallite size was found in the range 7–19 nm. The enhancement in the coercivity was observed with the doping of rare-earth cations. The higher values of coercivity (664–926 Oe) of these nanomaterials suggest their use in longitudinal recording media. - Highlights: • Micro-emulsion route was used to synthesize Ba{sub 2}NiCoRE{sub x}Fe{sub 28−x}O{sub 46} ferrites. • The crystallite size was found

Influence of rare-earth addition on microstructure and dielectric behavior of Ba0.6Sr0.4TiO3 ceramics

International Nuclear Information System (INIS)

Zhang Jingji; Zhai Jiwei; Chou Xiujian; Yao Xi

2008-01-01

Ba 0.6 Sr 0.4 TiO 3 (BST) ceramics with 0.5 mol% various trivalent rare-earth additions prepared by a solid-state route are investigated. A strong correlation is observed between the microstructure, dielectric properties and rare-earth element dopant. The results display that comparing with the lattice constants of undoped and doped rare-earth BST, the structure transforms from cubic to tetragonal structure. In addition, the dopant improves the tetragonal distortion with the ionic radius of rare earth decreasing, and then deteriorates it with further decreasing. Large ions rare-earth additions effectively suppress the grain growth of BST. It is found that the temperature-permittivity characteristics for the BSTR (R, namely, rare earth) system could be controlled using various rare-earth elements. Especially, such as Sm, Eu, Gd dopants are effective to satisfy the tunable microwave devices application due to the decrease of permittivity and the improvement of dissipation factors of BST ceramic with the accompanying high-tunability

Energies of rare-earth ion states relative to host bands in optical materials from electron photoemission spectroscopy

Science.gov (United States)

Thiel, Charles Warren

There are a vast number of applications for rare-earth-activated materials and much of today's cutting-edge optical technology and emerging innovations are enabled by their unique properties. In many of these applications, interactions between the rare-earth ion and the host material's electronic states can enhance or inhibit performance and provide mechanisms for manipulating the optical properties. Continued advances in these technologies require knowledge of the relative energies of rare-earth and crystal band states so that properties of available materials may be fully understood and new materials may be logically developed. Conventional and resonant electron photoemission techniques were used to measure 4f electron and valence band binding energies in important optical materials, including YAG, YAlO3, and LiYF4. The photoemission spectra were theoretically modeled and analyzed to accurately determine relative energies. By combining these energies with ultraviolet spectroscopy, binding energies of excited 4fN-15d and 4fN+1 states were determined. While the 4fN ground-state energies vary considerably between different trivalent ions and lie near or below the top of the valence band in optical materials, the lowest 4f N-15d states have similar energies and are near the bottom of the conduction band. As an example for YAG, the Tb3+ 4f N ground state is in the band gap at 0.7 eV above the valence band while the Lu3+ ground state is 4.7 eV below the valence band maximum; however, the lowest 4fN-15d states are 2.2 eV below the conduction band for both ions. We found that a simple model accurately describes the binding energies of the 4fN, 4fN-1 5d, and 4fN+1 states. The model's success across the entire rare-earth series indicates that measurements on two different ions in a host are sufficient to predict the energies of all rare-earth ions in that host. This information provides new insight into electron transfer transitions, luminescence quenching, and valence

Luminescence and photo-thermally stimulated defects creation processes in PbWO{sub 4} crystals doped with trivalent rare-earth ions

Energy Technology Data Exchange (ETDEWEB)

Fabeni, P. [Institute of Applied Physics “N.Carrara” (IFAC) of CNR, Via Madonna del Piano 10, 50019 Sesto Fiorentino (Firenze) (Italy); Krasnikov, A.; Kärner, T. [Institute of Physics, University of Tartu, Riia 142, 51014 Tartu (Estonia); Laguta, V.V.; Nikl, M. [Institute of Physics AS CR, Cukrovarnicka 10, 16253 Prague (Czech Republic); Pazzi, G.P. [Institute of Applied Physics “N.Carrara” (IFAC) of CNR, Via Madonna del Piano 10, 50019 Sesto Fiorentino (Firenze) (Italy); Zazubovich, S., E-mail: svet@fi.tartu.ee [Institute of Physics, University of Tartu, Riia 142, 51014 Tartu (Estonia)

2013-04-15

In PbWO{sub 4} crystals, doped with various trivalent rare-earth A{sup 3+} ions (A{sup 3+}: La{sup 3+}, Lu{sup 3+}, Y{sup 3+}, Ce{sup 3+}, Gd{sup 3+}), electron (WO{sub 4}){sup 3−} and {(WO_4)"3"−–A"3"+} centers can be created under UV irradiation not only in the host absorption region but also in the energy range around 3.85 eV (Böhm et al., 1999; Krasnikov et al., 2010). Under excitation in the same energy range, the UV emission peak at 3.05–3.20 eV is observed. In the present work, the origin of this emission is investigated in detail by low-temperature time-resolved luminescence methods. Photo-thermally stimulated creation of (WO{sub 4}){sup 3−} and {(WO_4)"3"−–A"3"+} centers is studied also in PbWO{sub 4}:Mo,A{sup 3+} crystals. Various processes, which could explain both the appearance of the UV emission and the creation of the {(WO_4)"3"−–A"3"+}-type centers under irradiation of PbWO{sub 4}: A{sup 3+} crystals in the 3.85±0.35 eV energy range, are discussed. The radiative and non-radiative decay of the excitons localized near A{sup 3+} ions is considered as the most probable mechanism to explain the observed features. -- Highlights: ► UV emission of PbWO{sub 4}: A{sup 3+} (A{sup 3+}: La{sup 3+}, Lu{sup 3+}, Y{sup 3+}, Ce{sup 3+}, and Gd{sup 3+}) crystals is studied. ► The emission is ascribed to the radiative decay of excitons localized near A{sup 3+} ions. ► The excitons are created at 3.85 eV excitation by a two-step process. ► Non-radiative decay of the excitons leads to the creation of (WO{sub 4}){sup 3−}–A{sup 3+} centers.

Order-disorder phase transformation in ion-irradiated rare earth sesquioxides

International Nuclear Information System (INIS)

Tang, M.; Valdez, J. A.; Sickafus, K. E.; Lu, P.

2007-01-01

An order-to-disorder (OD) transformation induced by ion irradiation in rare earth (RE) sesquioxides, Dy 2 O 3 , Er 2 O 3 , and Lu 2 O 3 , was studied using grazing incidence x-ray diffraction and transmission electron microscopy. These sesquioxides are characterized by a cubic C-type RE structure known as bixbyite. They were irradiated with heavy Kr ++ ions (300 keV) and light Ne + ions (150 keV) at cryogenic temperature (∼120 K). In each oxide, following a relatively low ion irradiation dose of ∼2.5 displacements per atom, the ordered bixbyite structure was transformed to a disordered, anion-deficient fluorite structure. This OD transformation was found in all three RE sesquioxides (RE=Dy, Er, and Lu) regardless of the ion type used in the irradiation. The authors discuss the irradiation-induced OD transformation process in terms of anion disordering, i.e., destruction of the oxygen order associated with the bixbyite structure

Towards atomic scale engineering of rare-earth-doped SiAlON ceramics through aberration-corrected scanning transmission electron microscopy

International Nuclear Information System (INIS)

Yurdakul, Hilmi; Idrobo, Juan C.; Pennycook, Stephen J.; Turan, Servet

2011-01-01

Direct visualization of rare earths in α- and β-SiAlON unit-cells is performed through Z-contrast imaging technique in an aberration-corrected scanning transmission electron microscope. The preferential occupation of Yb and Ce atoms in different interstitial locations of β-SiAlON lattice is demonstrated, yielding higher solubility for Yb than Ce. The triangular-like host sites in α-SiAlON unit cell accommodate more Ce atoms than hexagonal sites in β-SiAlON. We think that our results will be applicable as guidelines for many kinds of rare-earth-doped materials.

Determination of rare earths in their extraction processing

International Nuclear Information System (INIS)

You Jiannan; Zhang Yuqin

1989-01-01

A method for determination of rare earths in ores, ion-exchange resins and solution samples has been developed. The ore is molten with sodium peroxide and the molten sample is leached with triethenol amine and sodium citrate. In weak acid medium, the rare earths can be extracted by PMBP-phenol solution, and stripped with formic acid. In the acetic acidsodium acetate buffer medium of pH3, the spectrophotometric determination of rare earths with arsenazo M has been made. The rare earths in ion-exchange resins can be directly determined by spectrophotometry after being leached with hydrochloric acid and at heated condition. The rare earths with arsenazo M or a red complex. The maximum absorption of the complex is at 640 nm, and the molar absorption is 8.0 x 10 4 L centre dot mol -1 centre dot cm -1 . While the range of determination is 0.005%-0.5% and 0.001-1.0 g/L, the relative standard deviation is less than 5%, and recovery of rare earths is 98.5-105%. The method is rather simple and rapid

A new ion source for fission-yield measurements of rare-earth isotopes

International Nuclear Information System (INIS)

Pilzer, E.H.; Engler, G.

1987-01-01

A new integrated target-ion source for fission-yield measurements of rare-earth isotopes has been developed for the Soreq on-line isotope separator (SOLIS). The source is heated by electron bombardment to a temperature of 2400 0 C and ionization takes place in a rhenium hot cavity. To overcome the problem of impurities which reduce the ionization efficiency, a ZrC disk was inserted in the cavity. Calculations show that because of its high thermionic emission, ZrC enhances ionization performance considerably. For example, in the presence of 10 -5 mbar of cesium impurity, the ionization efficiency of a rhenium hot cavity for the rare-earth terbium is 6%. However, with a ZrC disk, the efficiency increases to 97%. (orig.)

Mechanism of luminescent emission in BaY2F8 scintillators doped with rare earths

International Nuclear Information System (INIS)

Santos, Ana Carolina de Mello

2013-01-01

with an analysis of X-ray absorption spectroscopy (XAS) and X-rays Excited Optical Luminescence (XEOL) allowed the development of a model for the scintillation mechanism for the rare earth doped BaYF systems. (author)

Effect of the kind of alkaline and rare earth ions on the structure of a glass rich in earth; Effet de la nature des ions alcalins et alcalino-terreux sur la structure d un verre riche en terre

Energy Technology Data Exchange (ETDEWEB)

Quintas, Arnaud; Caurant, Daniel; Majerus, Odile [Laboratoire de Chimie Appliquee de l Etat Solide, UMR 7574, ENSCP, 11 rue Pierre et Marie Curie, 75231 Paris Cedex 05, (France); Lenoir, Marion; Dussossoy, Jean-Luc [Commissariat a l Energie Atomique, Centre d Etudes de la Vallee du Rhone, DIEC/SCDV/LEBM, 30207 Bagnols-sur-Ceze, (France); Charpentier, Thibault [Service de Chimie Moleculaire, DSM/DRECAM/CEA Saclay, 91191 Gif-sur-Yvette Cedex, (France); Neuville, Daniel R. [Laboratoire de Physique des Mineraux et des Magmas, UMR 7047-CNRS-IPGP, Universite Pierre et Marie Curie, 4 place Jussieu, 75252 Paris Cedex 05, (France); Gervais, C. [Laboratoire de Chimie de la matiere condensee, UMR7574, Universite Pierre et Marie Curie, 4 place Jussieu, F-75252 Paris Cedex 05, (France)

2006-07-01

In the framework of a structural study of a nuclear wastes containment glass of type alumino borosilicate and rich in rare earths, the influence of the kind of alkaline or rare earth ions is analyzed. For that, two glasses series have been prepared in which the Na{sup +} ion (respectively Ca{sup 2+} ions) present in the standard composition is totally substituted by another alkaline ion Li{sup +}, K{sup +}, Rb{sup +} or Cs{sup +} (respectively another rare earth ion Mg{sup 2+}, Sr{sup 2+} or Ba{sup 2+}). These glasses, analyzed by optical absorption, Raman and {sup 27}Al or {sup 11}B NMR spectroscopies have revealed the strong impact of the kind of the modifying ion as well as the structure of the vitreous lattice (variation of the ratio BO{sub 3}/BO{sub 4} and local variations of the polymerization degree) than the local surroundings of the rare earth (decrease of the covalency degree of the bond Nd-O with the increase of the field force of the modifying ion). (O.M.)

Spectroscopic identification of rare earth elements in phosphate glass

Science.gov (United States)

Devangad, Praveen; Tamboli, Maktum; Muhammed Shameem, K. M.; Nayak, Rajesh; Patil, Ajeetkumar; Unnikrishnan, V. K.; Santhosh, C.; Kumar, G. A.

2018-01-01

In this work, rare earth-doped phosphate glasses were synthesized and characterized using three different spectroscopic techniques. The absorption spectra of the prepared praseodymium (Pr) and samarium (Sm) doped glasses, recorded by a UV-VIS-NIR spectrophotometer, show the characteristic absorption bands of these elements. To confirm this inference, laser-induced fluorescence spectra of Pr and Sm were obtained at a laser excitation of 442 nm. Their emission bands are reported here. The elemental analysis of these samples was carried out using a laser-induced breakdown spectroscopy (LIBS) system. Characteristic emission lines of Pr and Sm have been identified and reported by the recorded LIBS spectra of glass samples. Results prove that using these three complimentary spectroscopic techniques (absorption, fluorescence and LIBS), we can meaningfully characterize rare earth-doped glass samples.

Rare Earth-Activated Silica-Based Nanocomposites

Directory of Open Access Journals (Sweden)

C. Armellini

2007-01-01

Full Text Available Two different kinds of rare earth-activated glass-based nanocomposite photonic materials, which allow to tailor the spectroscopic properties of rare-earth ions: (i Er3+-activated SiO2-HfO2 waveguide glass ceramic, and (ii core-shell-like structures of Er3+-activated silica spheres obtained by a seed growth method, are presented.

Rare earth activated yttrium aluminate phosphors with modulated luminescence.

Science.gov (United States)

Muresan, L E; Popovici, E J; Perhaita, I; Indrea, E; Oro, J; Casan Pastor, N

2016-06-01

Yttrium aluminate (Y3 A5 O12 ) was doped with different rare earth ions (i.e. Gd(3+) , Ce(3+) , Eu(3+) and/or Tb(3+) ) in order to obtain phosphors (YAG:RE) with general formula,Y3-x-a Gdx REa Al5 O12 (x = 0; 1.485; 2.97 and a = 0.03). The synthesis of the phosphor samples was done using the simultaneous addition of reagents technique. This study reveals new aspects regarding the influence of different activator ions on the morpho-structural and luminescent characteristics of garnet type phosphor. All YAG:RE phosphors are well crystallized powders containing a cubic-Y3 Al5 O12 phase as major component along with monoclinic-Y4 Al2 O9 and orthorhombic-YAlO3 phases as the impurity. The crystallites dimensions of YAG:RE phosphors vary between 38 nm and 88 nm, while the unit cell slowly increase as the ionic radius of the activator increases. Under UV excitation, YAG:Ce exhibits yellow emission due to electron transition in Ce(3+) from the 5d level to the ground state levels ((2) F5/2 , (2) F7/2 ). The emission intensity of Ce(3+) is enhanced in the presence of the Tb(3+) ions and is decreased in the presence of Eu(3+) ions due to some radiative or non-radiative processes that take place between activator ions. By varying the rare earth ions, the emission colour can be modulated from green to white and red. Copyright © 2015 John Wiley & Sons, Ltd. Copyright © 2015 John Wiley & Sons, Ltd.

The effect of oxygen on segregation-induced redistribution of rare-earth elements in silicon layers amorphized by ion implantation

International Nuclear Information System (INIS)

Aleksandrov, O. V.

2006-01-01

A model of segregation-induced redistribution of impurities of rare-earth elements during solid-phase epitaxial crystallization of silicon layers amorphized by ion implantation is developed. This model is based on the assumption that a transition layer with a high mobility of atoms is formed at the interphase boundary on the side of a-Si; the thickness of this layer is governed by the diffusion length of vacancies in a-Si. The Er concentration profiles in Si implanted with both erbium and oxygen ions are analyzed in the context of the model. It shown that, in the case of high doses of implantation of rare-earth ions, it is necessary to take into account the formation of R m clusters (m = 4), where R denotes the atom of a rare-earth element, whereas, if oxygen ions are also implanted, formation of the complexes RO n (n = 3-6) should be taken into account; these complexes affect the transition-layer thickness and segregation coefficient

Enhanced pinning in mixed rare earth-123 films

Science.gov (United States)

Driscoll, Judith L [Los Alamos, NM; Foltyn, Stephen R [Los Alamos, NM

2009-06-16

An superconductive article and method of forming such an article is disclosed, the article including a substrate and a layer of a rare earth barium cuprate film upon the substrate, the rare earth barium cuprate film including two or more rare earth metals capable of yielding a superconductive composition where ion size variance between the two or more rare earth metals is characterized as greater than zero and less than about 10.times.10.sup.-4, and the rare earth barium cuprate film including two or more rare earth metals is further characterized as having an enhanced critical current density in comparison to a standard YBa.sub.2Cu.sub.3O.sub.y composition under identical testing conditions.

Investigation and modelling of rare-earth activated waveguide structures

International Nuclear Information System (INIS)

Wolinski, W.; Malinowski, M.; Mossakowska-Wyszynska, A.; Piramidowicz, R.; Szczepanski, P.

2005-01-01

In this paper the overview of the recent study on the rare-earth activated waveguides performed in the Optoelectronic Department of IMiO is presented. We reported on the development of rare earth-doped fluorozirconate (ZBLAN) glass fibers that allow a construction of a new family of visible and ultraviolet fiber lasers pumped by upconversion. Especially the performance of holmium devices is presented. The properties of laser planar waveguides obtained by the LPE process and the growth conditions of rare earths doped YAG layers are presented. In this paper we present also the theoretical study of the nonlinear operation of planar waveguide laser, as an example the microdisk Nd:YAG structure is discussed. We derived an approximate formula which relates the small signal gain in the Nd:YAG active medium and the laser characteristics, obtained for whispering-gallery modes and radial modes, to the output power and real parameters of the laser structure (authors)

NEW ERBIUM DOPED ANTIMONY GLASSES FOR LASER AND GLASS AMPLIFICATION

Directory of Open Access Journals (Sweden)

B. Tioua

2015-07-01

Full Text Available Because of the special spectroscopic properties of the rare earth ions, rare earth doped glasses are widely used in bulk and fiber lasers or amplifiers. The modelling of lasers and searching for new laser transitions require a precise knowledge of the spectroscopic properties of rare earth ions in different host glasses. In this poster will offer new doped erbium glasses synthesized in silicate crucibles were obtained in the combination Sb2O3-WO3-Na2O. Several properties are measured and correlated with glass compositions. The absorption spectral studies have been performed for erbium doped glasses. The intensities of various absorption bands of the doped glasses are measured and the Judd-Ofelt parameters have been computed. From the theory of Judd-Ofelt, various radiative properties, such as transition probability, branching ratio and radiative life time for various emission levels of these doped glasses have been determined and reported. These results confirm the ability of antimony glasses for glass amplification.

Determination of active oxygen content in rare earth peroxides

International Nuclear Information System (INIS)

Queiroz, Carlos A.S.; Abrao, Alcidio

1993-01-01

The content of active oxygen in rare earth peroxides have been determined after the dissolution of the samples with hydrocloridic acid in the presence of potassium iodide. The free generated iodine is titrated with sodium thiosulfate using starch as indicator. The oxidation of iodide to the free iodine indicates the presence of a higher valence state rare earth oxide, until now specifically recognized for the oxides of cerium (Ce O 2 ), praseodymium (Pr 6 O 1 1) and terbium (TB 4 O 7 ). recently the authors synthesized a new series of rare earth compounds, the peroxides. These new compounds were prepared by precipitating the rare earth elements complexed with carbonate ion by addition of hydrogen peroxide. the authors demonstrated that all rare earth elements, once solubilized by complexing with carbonate ion, are quantitatively precipitated as peroxide by addition of hydrogen peroxide. (author)

In vivo demonstration of enhanced radiotherapy using rare earth doped titania nanoparticles.

Science.gov (United States)

Townley, Helen E; Kim, Jeewon; Dobson, Peter J

2012-08-21

Radiation therapy is often limited by damage to healthy tissue and associated side-effects; restricting radiation to ineffective doses. Preferential incorporation of materials into tumour tissue can enhance the effect of radiation. Titania has precedent for use in photodynamic therapy (PDT), generating reactive oxygen species (ROS) upon photoexcitation, but is limited by the penetration depth of UV light. Optimization of a nanomaterial for interaction with X-rays could be used for deep tumour treatment. As such, titania nanoparticles were doped with gadolinium to optimize the localized energy absorption from a conventional medical X-ray, and further optimized by the addition of other rare earth (RE) elements. These elements were selected due to their large X-ray photon interaction cross-section, and potential for integration into the titania crystal structure. Specific activation of the nanoparticles by X-ray can result in generation of ROS leading to cell death in a tumour-localized manner. We show here that intratumoural injection of RE doped titania nanoparticles can enhance the efficacy of radiotherapy in vivo.

Synthesis and luminescence studies of novel rare earth activated lanthanum pentaborate

International Nuclear Information System (INIS)

Nagpure, P.A.; Bajaj, N.S.; Omanwar, S.K.; Sonekar, R.P.

2011-01-01

The lanthanum pentaborate (LaB 5 O 9 ) is a novel material which exhibits excellent luminescence when doped with rare earth ions. It was prepared by a novel technique which is a slight variation of solution combustion synthesis. The synthesis is based on the exothermic reaction between the fuel (urea) and oxidizer (ammonium nitrate). The structure of the prepared material was confirmed by powder XRD technique. The photoluminescence of rare earth ions (Ce 3+ , Eu 3+ ) and sensitized luminescence of Gd 3+ (Pr 3+ -Gd 3+ and Bi 3+ -Gd 3+ ) in LaB 5 O 9 have been studied. LaB 5 O 9 :Ce 3+ shows broad band UV emission at 317 nm and LaB 5 O 9 :Eu 3+ shows orange red emission. LaB 5 O 9 : Pr 3+ -Gd 3+ and LaB 5 O 9 : Bi 3+ -Gd 3+ exhibit efficient luminescence of Gd 3+ in narrow UVB region at 310 nm. The material (La 0.5 Pr 0.4 )B 5 O 9 :Gd 0.1 exhibits intense narrow band UVB emission at 310 nm and could be a potential candidate for UVB phosphors used in phototherapy lamps. (author)

Laser site selective spectroscopy of rare-earth defects in fluorites

International Nuclear Information System (INIS)

Murdoch, K.M.

1998-01-01

Full text: Rare-earth (R 3+ ) doped fluorites (CaF 2 , SrF 2 , and BaF 2 ) have long been a model system for investigating the defect chemistry of crystalline solids. The trivalent R 3+ ions substitute for the divalent cations of the host and are charge compensated by the inclusion of additional interstitial fluoride ions (F - j ). A variety of R 3+ centres arise, including cubic symmetry R 3+ sites remote from any F - j , single R 3+ ions associated with one neighbouring F - j , and clusters of R 3+ associated with multiple F - j . Additional R 3+ centres are produced by chemical modifications involving the substitution of host anions or cations. Numerous experimental studies have shown that the relative populations of these centres are determined by the size of the R 3+ ions, the R 3+ concentration in the crystal, the crystals thermal history, and any pressure treatments. A considerable volume of theoretical work has also been presented to interpret these results. Laser site selective spectroscopy has proved a powerful technique for probing the defect chemistry of R 3+ doped fluorites. Some of the important results and conclusions of these experiments will be reviewed. A detailed account, with references to the original studies, has also been published recently

Application of Nd/sup 3+/-doped silica fibers to radiation sensing devices

International Nuclear Information System (INIS)

Imamura, K.; Suzuki, T.; Gozen, T.; Tanaka, H.; Okamoto, S.

1987-01-01

Applications of rare-earth-ion-doped optical fibers to radiation sensing devices have been studied. It was revealed that rare-earth-ion-doped optical fibers are highly sensitive to radioactive rays such as gamma ray and thermal neutron flux and that they have little dependence on ambient temperature and optical power. An experimental distributed radiation sensing system incorporating Nd/sup 3+/-doped optical fibers, radiation resistant optical fibers and an OTDR was made and tested. The results proved that the distributed sensing system is practically adaptable to the measurement of the radioactive rays

Magnetic properties of Kramers rare earth ions in aluminium and gallium garnets; Proprietes magnetiques des ions de kramers des terres rares dans les grenats de terres rares et d'aluminium et les grenats de terres rares et de gallium

Energy Technology Data Exchange (ETDEWEB)

Capel, H [Commissariat a l' Energie Atomique, Saclay (France). Centre d' Etudes Nucleaires

1964-07-01

The magnetic properties of Kramers rare earth ions in aluminium and gallium garnets (MAlG and MGaG) are discussed by means of a molecular field treatment. The symmetry properties of the space group permit to establish a parametrization for the magnetic dipolar and exchange couplings. The magnetic properties of the system can be expressed in terms of these parameters and the g factors of the rare earth ions. We have calculated the transition temperatures, the sub-lattice magnetizations, the susceptibility in the paramagnetic region and the antiferromagnetic susceptibility for a special type of magnetic ordering. The influence of the excited Kramers doublets is described by means of a generalization of the usual g tensor. (authors) [French] Les proprietes magnetiques des ions de Kramers des terres rares dans les grenats de terre rare et d'aluminium et les grenats de terre rare et de gallium sont discutees a l'aide d'un traitement du champ moleculaire. Les proprietes de symmetrie du groupe d'espace permettent d'exprimer les couplages dipolaires et les interactions d'echange en fonction de quelques parametres. Les proprietes magnetiques peuvent etre exprimees en fonction de ces parametres et les facteurs g des ions de terre rare. Nous avons calcule les temperatures de transition, les aimantations des sous-reseaux pour 0ions non de Kramers. (auteurs)

Effect of rare earth ion Ce3+ on the lactate dehydrogenase isozyme patterns of six mouse organs

International Nuclear Information System (INIS)

Jiangyan, L.; Guojun, S.; Hengyi, L.; Yinhua, L.; Ting, W.; Yansheng, Y.

1998-01-01

Full text: Effect of rare earth ion Ce 3+ on the lactate dehydrogenase (LDH) isozyme patterns of six organs of mouse (heart, liver, kidney, muscle, stomach) were investigated by utilizing polyacrylamide gel electrophoresis (PAGE) methods. The results indicated: Ce 3+ not only can make some LDH bands disappear but also can induce some new bands. Under the action of Ce 3+ , the shades of some LDH bands were changed and the shade variations were different from organ to organ. In the muscle, it appeared the shade of LDH bands was related to the rare earth concentration in the feed. Rare earth can affect the muscle LDH patterns widely and apparently

Redox reactions in rare earth chloride molten electrolytes

International Nuclear Information System (INIS)

Khokhlov, V.A.; Novoselova, A.V.; Nikolaeva, E.V.; Tkacheva, O.Yu.; Salyulev, A.B.

2007-01-01

Rare earth (REM, Ln) solutions in chloride melts including MCI+LnCl 3 mixtures, where M - alkali metals, were investigated by potentiometry, voltammetry, conductometry in wide concentration and temperature intervals. Findings present complete and trusty information on the valent state of rare earths, structure and composition of complex ions affecting essentially on properties of electrolytes. It is demonstrated that the coexistence of rare earth ions with different oxidation level formed as a result of possible redox reactions: 2Ln 3+ + Ln ↔3Ln 2+ , Ln 2+ + Ln↔2Ln + and nM + + Ln↔nM + Ln n+ appears sharply in thermodynamic and transport properties of molten Ln-LnCl 3 and Ln-LnCl 3 -MCl systems [ru

Rare earth metals, rare earth hydrides, and rare earth oxides as thin films

International Nuclear Information System (INIS)

Gasgnier, M.

1980-01-01

The review deals with pure rare earth materials such as rare earth metals, rare earth hydrides, and rare earth oxides as thin films. Several preparation techniques, control methods, and nature of possible contaminations of thin films are described. These films can now be produced in an extremely well-known state concerning chemical composition, structure and texture. Structural, electric, magnetic, and optical properties of thin films are studied and discussed in comparison with the bulk state. The greatest contamination of metallic rare earth thin films is caused by reaction with hydrogen or with water vapour. The compound with an f.c.c. structure is the dihydride LnH 2 (Ln = lanthanides). The oxygen contamination takes place after annealing at higher temperatures. Then there appears a compound with a b.c.c. structure which is the C-type sesquioxide C-Ln 2 O 3 . At room atmosphere dihydride light rare earth thin films are converted to hydroxide Ln(OH) 3 . For heavy rare earth thin films the oxinitride LnNsub(x)Osub(y) is observed. The LnO-type compound was never seen. The present review tries to set the stage anew for the investigations to be undertaken in the future especially through the new generations of electron microscopes

Sc, Y, La-Lu - Rare Earth Elements

International Nuclear Information System (INIS)

Anon.

1987-01-01

At present extensive efforts are being made in completing work on system number Rare Earth Elements. Part A is devoted to the occurrence of these elements on the earth and in the universe. Part B deals with the pure metals; the 7 volumes published cover the description of the separation from the raw materials, the preparation of pure metals,their uses and toxicology, the physical properties of nuclei, atoms, molecules, and isotopes; in addition the behavior of ions in solution and the electrochemical behavior of rare earth elements are described. The compounds are described in Part C. Part D with 6 volumes has been devoted to the description of coordination compounds and is completed. The volume ''Rare Earth Elements C 10'' deals with the rare earth tellurides, oxide tellurides, tellurates, telluride halides, tellurate halides, sulfide tellurides, selenide tellurides, and alkali rare earth tellurates. Another topic of this volume are the compounds of the rare earth elements with polonium. So far as meaningful and in accordance with all earlier volumes of ''Rare Earth Elements'' Series C, comparative data are presented in sections preceding treatment of the individual compounds and systems

Lanthanide ions doped Y2Sn2O7 nano-particles: low temperature synthesis and photoluminescence study

International Nuclear Information System (INIS)

Nigam, Sandeep; Sudarsan, V.; Vatsa, R.K.

2008-01-01

During the past decade, pyrochlore-type oxides (A 2 B 2 O 7 ) have emerged as important host matrices for lanthanide doped luminescent materials due to their higher thermal stability. Up to now, conventional solid-state reaction is the most commonly used synthetic method for preparation, of rare-earth pyrochlore oxides. This synthesis route employs a solid-state reaction of metal-oxide with appropriate rare-earth oxides at high temperature (>1200 deg C) for a long time (several days). However, in present work, Y 2 Sn 2 O 7 nanoparticles co-doped with lanthanide ions Tb 3+ and Ce 3+ were prepared based on the urea hydrolysis of Y 3+ , Sn 4+ , and Ln 3+ in ethylene glycol medium at 150 deg C followed by heating at 500, 700 and 900 deg C

Computer modelling of defect structure and rare earth doping in LiCaAlF sub 6 and LiSrAlF sub 6

CERN Document Server

Amaral, J B; Valerio, M E G; Jackson, R A

2003-01-01

This paper describes a computational study of the mixed metal fluorides LiCaAlF sub 6 and LiSrAlF sub 6 , which have potential technological applications when doped with a range of elements, especially those from the rare earth series. Potentials are derived to represent the structure and properties of the undoped materials, then defect properties are calculated, and finally solution energies for rare earth elements are calculated, enabling preferred dopant sites and charge compensation mechanisms to be predicted.

Production of rare earth polishing powders in Russia

International Nuclear Information System (INIS)

Kosynkin, V.D.; Ivanov, E.N.; Kotrekhov, V.A.; Shtutza, M.G.; Grabko, A.I.

1998-01-01

Full text: Russia is a potent producer of polishing powders made of rare earth material presented as an extensive and well developed base. Considering the reserves, the facilities predisposition and the polishing agent (cerium dioxide) content the chief mineral source is loparite, apatite and monazite. The production of rare earth polishing powders is based on specially developed continuous technological processes, corrosion-proof equipment, ensuring a high and stable production quality. A special attention is paid to the radiation safety of the powders. The initial material for the rare earth polishing powders based on loparite is the fusion cake of rare earth chlorides obtained at that mineral chlorination. The technology of the polishing powder production from the REE fusion cake includes the following stages: dissolution of the REE fusion cake chlorides; - thorough cleaning of the REE fusion cake chlorides from radioactive and non-rare-earth impurities; chemical precipitation of REE carbonates, obtaining middlings with proper material and granulometric composition, thermal treatment of precipitated carbonates followed with the operations of drying and roasting; classification of roasted oxides, obtaining end products - polishing powders. The production of fluorine-containing powders includes the stage of their fluorination after the stage of carbonate precipitation. The stabilizing doping can be introduced both into the middlings during one of the technological process of powders manufacturing and into the end product. Rare earth polishing powders are manufactured in Russia by the Share Holding Company 'Chepetz Mechanical Plant' (ChMP Co.), the city of Glasov. The plant produces a number of polishing materials, such as; polishing powder Optinol, containing at least 50% by mass of cerium dioxide, used in the mass production of optical and other articles; polishing powder Optinol-10 with doping to improve the sedimentary and aggregate stability of the solid phase

Prospects for trivalent rare earth molecular vapor lasers for fusion

International Nuclear Information System (INIS)

Krupke, W.F.

1976-01-01

The dynamical properties of three types of RE 3+ molecular vapors were considered: (1) rare earth trihalogens, (2) rare earth trihalogens complexed with transition metal trihalogens, and (3) rare earth chelates. Radiative and nonradiative (unimolecular and bimolecular) transition probabilities have been calculated using phenomenological models predicted on the unique electronic structure of the triply ionized RE ion (well shielded ground electronic configuration of equivalent of electrons). Although all the lanthanide ions have been treated in some detail, specific results are presented for the Nd 3+ and Tb 3+ ions to illustrate the systematics of these vapors as a class of new laser media. Once verified, these phenomenological models will provide a powerful tool for the directed experimental exploration of these systems. Because of the structural similarity to the triply ionized actinides, comments offered here for the lanthanide rare earth series generally apply to gaseous actinide lasers which are also under consideration

Room temperature ferromagnetism with large magnetic moment at low field in rare-earth-doped BiFeO₃ thin films.

Science.gov (United States)

Kim, Tae-Young; Hong, Nguyen Hoa; Sugawara, T; Raghavender, A T; Kurisu, M

2013-05-22

Thin films of rare earth (RE)-doped BiFeO3 (where RE=Sm, Ho, Pr and Nd) were grown on LaAlO3 substrates by using the pulsed laser deposition technique. All the films show a single phase of rhombohedral structure with space group R3c. The saturated magnetization in the Ho- and Sm-doped films is much larger than the values reported in the literature, and is observed at quite a low field of 0.2 T. For Ho and Sm doping, the magnetization increases as the film becomes thinner, suggesting that the observed magnetism is mostly due to a surface effect. In the case of Nd doping, even though the thin film has a large magnetic moment, the mechanism seems to be different.

Processing of monazite at the rare earth division,Udyogamandal

International Nuclear Information System (INIS)

Narayanan, N.S.; Thulasidoss, S.; Ramachandran, T.V.; Swaminathan, T.V.; Prasad, K.R.

1988-01-01

The processing techniques adopted at the Rare Earth Division of the Indian Rare Earths Limited at Udyogamandal, for the production of rare earth compounds of various compositions and purity grades are reviewed. Over 100 different compounds are produced and marketed, and these include mixed rare earths chloride, crude thorium concentrate, cerium oxide, cerium hydrate, rare earths carbonate, didymium salts and individual rare earth oxides and salts. Also, the trisodium phosphate obtained as byproduct in the processing of monazite, is recovered and marketed. The process scheme for monazite essentially involves alkaline digestion of ground monazite, removal of the by-product trisodium phosphate, separation of thorium through preferential dissolution of rare earths hydroxide in hydrochloric acid under controlled pH and temperature conditions followed by purification, and evaporation of the chloride solution to yield pure rare earths chloride. Part of the chloride is utilised for the production of individual rare earth compounds after separation by solvent extraction and ion exchange processes. Individual rare earth compounds of 99.99 %+ purity are regularly produced to cater to the demand within the country. (author) 8 figs., 1 tab

Nuclear orientation on rare earth nickel alloys

International Nuclear Information System (INIS)

Nishimura, K.

1998-01-01

A hyperfine interaction study of the light rare earth elements, Ce, Pr, Nd and Pm, in the rare earth nickel and CeNi 2 Al 5 compounds by means of the low temperature nuclear orientation is summarised. The magnitudes and directions of the magnetic hyperfine fields obtained through measurements of γ-ray anisotropy and angular distributions reveal the magnetic structures of the ions. The experiments extracted peculiar results for the magnetic properties of the ions, and show certain novel features of the technique to the study of solid-state magnetism. Copyright (1998) Australian Journal of Physics

Spectroscopic and neutron detection properties of rare earth and titanium doped LiAlO 2 single crystals

Energy Technology Data Exchange (ETDEWEB)

Dickens, Peter T.; Marcial, José; McCloy, John; McDonald, Benjamin S.; Lynn, Kelvin G.

2017-10-01

In this study, LiAlO2 crystals doped with rare-earth elements and Ti were produced by the CZ method and spectroscopic and neutron detection properties were investigated. Photoluminescence revealed no clear luminescent activation of LiAlO2 by the rare-earth dopants though some interesting luminescence was observed from secondary phases within the crystal. Gamma-ray pulse height spectra collected using a 137Cs source exhibited only a Compton edge for the crystals. Neutron modeling using Monte Carlo N-Particle Transport Code revealed most neutrons used in the detection setup are thermalized, and while using natural lithium in the crystal growth, which contains 7.6 % 6Li, a 10 mm Ø by 10 mm sample of LiAlO2 has a 70.7 % intrinsic thermal neutron capture efficiency. Furthermore, the pulse height spectra collected using a 241Am-Be neutron source demonstrated a distinct neutron peak.

Ion exchange separation of rare earths. I

International Nuclear Information System (INIS)

Nghi, Nguyen danh; Matous, K.

1977-01-01

The optimal conditions of separating selected rare earths by two ion exchange chromatography using Ostion KS cation exchange resin were studied. The effect of acetic acid concentration in the sorption solution was investigated. The elution process was studied in dependence on the concentration of Na 2 H 2 EDTA, on the total concentration of EDTA 4- ion, on elution agent flow, and on temperature. The optimal conditions were determined by evaluating integral elution curves and changes in acid concentration for systems Y-Pr, La-Pr, Er-Pr, Eu-Pr as follows: The sorption solution requires the presence of Na 2 H 2 EDTA of 0.03M in concentration. The basic elution solution was prepared in the following way: 0.183M Na 2 Mg 2 EDTA, 9.6x10 -3 M Na 2 H 2 EDTA, 3.84x10 -3 M CH 3 COOH, 2.30x10 -2 M CH 3 COONH 4 , 2.30x10 -2 M (NH 4 ) 2 SO 4 . Approximate pH 5.7 to 6.0. The optimal elution solution was prepared by diluting the basic solution so that the total concentration of EDTA 4- equalled 0.075M. The optimal flow was determined to be 0.86 ml.cm -2 .min -1 at a temperature of 55 degC. (author)

Upconversion in rare earth ions doped TeO2-ZnO glass

International Nuclear Information System (INIS)

Mohanty, Deepak Kumar; Rai, Vineet Kumar

2012-01-01

The Er 3+ /Yb 3+ doped/codoped TeO 2 -ZnO glasses have been fabricated by conventional melt and quenching technique. The absorption spectra of the doped/codoped glasses have been performed. The visible upconversion emissions of both doped and codoped glasses have been observed using 808 nm diode laser excitation. The process involved in upconversion emissions has been discussed in detail. (author)

Ion transport under the effect of an electric field in porous medium: application to the separation of rare earths by focalization electrophoresis

International Nuclear Information System (INIS)

Vieira-Nunes, A.I.

1999-01-01

Trivalent ions of rare earth elements have very similar properties and their difficult separation each from another is usually carried out by liquid-liquid extraction or ion exchange. Focalization electrophoresis represents an alternative route to the usual techniques. The purpose of this work consisted of the fundamental investigation of ion transport phenomena in electrophoretic processes. Focalization electrophoresis is suitable for separation of amphoteric species such as rare earth ions, using a pH gradient in the cell and upon addition of a complexed agent e. g. EDTA. This technique relies upon the difference in iso-electrical points of the considered species, being under the form of free cation near the anode, and in the form of anionic complexed species closer to the cathode. Rare earth species are submitted to the antagonist effects of diffusion and migration, enabling their focalization to occur at the iso-electrical point, corresponding to nil value of their effective mobility. Following a literature survey on rare earth elements and electrophoresis processes, the document describes theoretical and experimental investigations of complexation equilibria of some rare earth elements, namely lanthanum, neodymium, praseodymium and cerium, depending on pH. Values for the iso-electrical points could be estimated. Transport and focalization phenomena in view of rare earth separation, are dealt in the last chapter. Investigations were first carried out without forced circulation of the electrolyte solution and the transient behavior of the system allowed operating conditions to be design and built-up of a continuous device, more suitable to separation, and provided with 42 potential and 42 temperature sensors: the results of the preliminary runs, in form of variable profiles, are presented and discussed. (author)

Design and length optimization of an adiabatic coupler for on-chip vertical integration of rare-earth-doped double tungstate waveguide amplifiers

NARCIS (Netherlands)

Mu, Jinfeng; Sefünç, Mustafa; García Blanco, Sonia Maria

2014-01-01

The integration of rare-earth doped double tungstate waveguide amplifiers onto passive technology platforms enables the on-chip amplification of very high bit rate signals. In this work, a methodology for the optimized design of vertical adiabatic couplers between a passive Si3N4 waveguide and the

Luminescence of rare-earth ions in Mg[sub 2]SiO[sub 4

Energy Technology Data Exchange (ETDEWEB)

Van der Voort, D; Maat-Gersdorf, I de; Blasse, G [Rijksuniversiteit Utrecht (Netherlands)

1992-01-01

The luminescence of the rare-earth ions Eu[sup 3+], Tb[sup 3+] and Ce[sup 3+] in Mg[sub 2]SiO[sub 4] is reported. The Tb[sup 3+] ion shows a change in emission colour from blue to green depending on the charge compensator. This is ascribed to a difference in coupling of the Tb[sup 3+] ion to the vibrational lattice modes. The Eu[sup 3+] ion has an average quantum efficiency under charge-transfer excitation of 60% at 4.2 and 20% at 300 K. The Ce[sup 3+] emission is situated in the blue and shows a Stokes shift of 3 500 cm[sup -1]. The relaxation of these ions in the excited state is discussed in terms of their positive effective charge and the stiffness of their surroundings.

Electrical and dielectric properties of lithium manganate nanomaterials doped with rare-earth elements

Energy Technology Data Exchange (ETDEWEB)

Iqbal, Muhammad Javed; Ahmad, Zahoor [Department of Chemistry, Quaid-i-Azam University, Islamabad 45320 (Pakistan)

2008-05-01

Substituted LiR{sub x}Mn{sub 2} {sub -} {sub x}O{sub 4} (R = La{sup 3+}, Ce{sup 3+}{sub ,} Pr{sup 3+} and x = 0.00 - 0.20) nanoparticles are prepared by the sol-gel method and the consequent changes in their lattice structure, dielectric and electrical parameters are determined by XRD, ED-XRF, SEM, LCR meter bridge and dc electrical resistivity measurements. Diffraction data show that the samples are single-phase spinel materials with crystallites sizes between 21 and 38 nm. The lattice parameter, cell volume and X-ray density are found to be affected by doping the Li-manganate with the rare-earth elements. The ED-XRF analysis confirms the stoichiometric composition of the synthesized samples and SEM reveals their morphology. Calculated values of the dielectric constant ({epsilon}) and the dielectric loss (tan {delta}) decrease with the frequency of the applied field. This is attributed to Maxwell-Wagner polarization. Replacement of manganese by the rare-earth elements results in an improvement in the structural stability of the material, which is considered to be useful for enhancement of the cycleability of the compounds when used in lithium rechargeable batteries, and increases significantly the values of {epsilon} and tan {delta} (except for Ce). Lithium manganate nanomaterials with high {epsilon} and low tan {delta} may be attractive for application in memory storage devices. (author)

Low-phonon-frequency chalcogenide crystalline hosts for rare earth lasers operating beyond three microns

Science.gov (United States)

Payne, Stephen A.; Page, Ralph H.; Schaffers, Kathleen I.; Nostrand, Michael C.; Krupke, William F.; Schunemann, Peter G.

2000-01-01

The invention comprises a RE-doped MA.sub.2 X.sub.4 crystalline gain medium, where M includes a divalent ion such as Mg, Ca, Sr, Ba, Pb, Eu, or Yb; A is selected from trivalent ions including Al, Ga, and In; X is one of the chalcogenide ions S, Se, and Te; and RE represents the trivalent rare earth ions. The MA.sub.2 X.sub.4 gain medium can be employed in a laser oscillator or a laser amplifier. Possible pump sources include diode lasers, as well as other laser pump sources. The laser wavelengths generated are greater than 3 microns, as becomes possible because of the low phonon frequency of this host medium. The invention may be used to seed optical devices such as optical parametric oscillators and other lasers.

Magnetic and optical properties of electrospun hollow nanofibers of SnO{sub 2} doped with Ce-ion

Energy Technology Data Exchange (ETDEWEB)

Mohanapriya, P.; Victor Jaya, N. [Department of Physics, Anna University, Chennai 600 025 (India); Pradeepkumar, R. [Centre for Nanoscience and Technology, Anna University, Chennai 600 025 (India); Natarajan, T. S., E-mail: tsn@physics.iitm.ac.in [Department of Physics, Indian Institute of Technology Madras, Chennai 600 036 (India)

2014-07-14

Cerium doped SnO{sub 2} hollow nanofibers were synthesized by electrospinning. High resolution scanning electron microscope (HRSEM) and transmission electron microscopy (TEM) analysis showed hollow nanofibers with diameters around ∼200 nm. The optimized substitution of Ce ion into SnO{sub 2} lattices happened above 6 mol. % doping as confirmed by Powder X-ray diffraction (XRD) studies. Optical band gap was decreased by the doping confirming the direct energy transfer between f-electrons of rare earth ion and the SnO{sub 2} conduction or valence band. The compound also exhibited room temperature ferromagnetism with the saturation magnetization of 19 × 10{sup −5} emu/g at 6 mol. %. This study demonstrates the Ce doped SnO{sub 2} hollow nanofibers for applications in magneto-optoelectronic devices.

Rare earths

Energy Technology Data Exchange (ETDEWEB)

Cranstone, D A

1979-01-01

Rare earth elements are commonly extracted from the minerals monazite, bastnaesite, and xenotine. New uses for these elements are constantly developing; they have found applications in glass polishing, television tube phosphors, high-strength low-alloy steels, magnets, catalysts, refractory ceramics, and hydrogen sponge alloys. In Canada, rare earths have been produced as byproducts of the uranium mining industry, but there was no production of rare earths in 1978 or 1979. The world sources of and markets for the rare earth elements are discussed.

Rare Earth Doped Lanthanum Calcium Borate Polycrystalline Red Phosphors

Directory of Open Access Journals (Sweden)

H. H. Xiong

2014-01-01

Full Text Available Single-phased Sm3+ doped lanthanum calcium borate (SmxLa2−xCaB10O19, SLCB, x=0.06 polycrystalline red phosphor was prepared by solid-state reaction method. The phosphor has two main excitation peaks located at 398.5 nm and 469.0 nm, which are nicely in accordance with the emitting wavelengths of commercial near-UV and blue light emitting diode chips. Under the excitation of 398.0 nm, the dominant red emission of Sm3+ in SLCB phosphor is centered at 598.0 nm corresponding to the transition of 4G5/2 → 6H7/2. The Eu3+ fluorescence in the red spectral region is applied as a spectroscopic probe to reveal the local site symmetry in the host lattice and, hence, Judd-Ofelt parameters Ωt  (t=2, 4 of Eu3+ in the phosphor matrix are derived to be 3.62×10-20 and 1.97×10-20 cm2, indicating a high asymmetrical and strong covalent environment around rare earth luminescence centers. Herein, the red phosphors are promising good candidates employed in white light emitting diodes (LEDs illumination.

Spectroscopic properties of rare earths in optical materials

CERN Document Server

Parisi, Jürgen; Osgood, R; Warlimont, Hans; Liu, Guokui; Jacquier, Bernard

2005-01-01

Aimed at researchers and graduate students, this book provides up-to-date information for understanding electronic interactions that impact the optical properties of rare earth ions in solids. Its goal is to establish a connection between fundamental principles and the materials properties of rare-earth activated luminescent and laser optical materials. The theoretical survey and introduction to spectroscopic properties include electronic energy level structure, intensities of optical transitions, ion-phonon interactions, line broadening, and energy transfer and up-conversion. An important aspect of the book lies in its deep and detailed discussions on materials properties and the potential of new applications such as optical storage, information processing, nanophotonics, and molecular probes that have been identified in recent experimental studies. This volume will be a valuable reference book on advanced topics of rare earth spectroscopy and materials science.

Luminescence properties of erbium doped sodium barium borate glass with silver nanoparticles

Science.gov (United States)

Rajeshree Patwari, D.; Eraiah, B.

2018-02-01

Alteration in the absorption features of rare earth (RE) doped glasses with silver nanoparticles is ever-challenging in photonics. Erbium (Er3+) doped glasses with composition (60-x-y)B2O3-30Na2CO3-10BaO-xEr2O3-yAgCl where (x=0.5, 1.0 and y=1.0 mol %) are synthesized using melt-quenching method. The density is determined by Archimedes principle and molar volumes are calculated. Glass samples were characterized by XRD and UV-Visible spectroscopy. UV-Visible spectra shows eleven prominent absorption peaks centred around 366, 378, 408, 442, 452, 489, 521, 547, 652, 800 and 977 nm equivalent to the rare earth (Er3+) ion transitions. The sample without rare earth shows no peaks which specifies that rare earth ion plays a spirited role in the glass matrix. The glass samples with silver and without rare earth ion shows plasmon peak on heat treatment. The energy band gap values calculated for direct and indirect transitions are in the range of 3.126-3.440eV and 2.58-3.177eV respectively. The refractive indices and Urbach energies are also determined. Photoluminescence spectra are recorded and studied for excitation of the most intense peaks of wavelengths 378 and 521nm. The luminescence of erbium ion is enhanced by the presence of silver when the concentration of rare earth ion is less than that of silver.

Resistivity and magnetoresistivity of amorphous rare-earth alloys

Science.gov (United States)

Borchi, E.; Poli, M.; De Gennaro, S.

1982-05-01

The resistivity and magnetoresistivity of amorphous rare-earth alloys are studied starting from the general approach of Van Peski-Tinbergen and Dekker. The random axial crystal-field and the magnetic correlations between the rare-earth ions are consistently taken into account. The characteristic features of the available experimental data are explained both of the case of random ferromagnetic and antiferromagnetic order.

Rare earth germanates

International Nuclear Information System (INIS)

Bondar', I.A.; Vinogradova, N.V.; Dem'yanets, L.N.

1983-01-01

Rare earth germanates attract close attention both as an independent class of compounds and analogues of a widely spread class of natural and synthetic minerals. The methods of rare earth germanate synthesis (solid-phase, hydrothermal) are considered. Systems on the basis of germanium and rare earth oxides, phase diagrams, phase transformations are studied. Using different chemical analysese the processes of rare earth germanate formation are investigated. IR spectra of alkali and rare earth metal germanates are presented, their comparative analysis being carried out. Crystal structures of the compounds, lattice parameters are studied. Fields of possible application of rare earth germanates are shown

Microstructure-property relationships of rare-earth--zinc-oxide varistors

International Nuclear Information System (INIS)

Williams, P.; Krivanek, O.L.; Thomas, G.; Yodogawa, M.

1980-01-01

The microstructure and properties of ZnO varistors containing Ba, Co, and rare-earth--metal oxides, which give values of α [α=d(log I)/d(log V)] as high as 29, are examined. Mean ZnO grain size is 11 μm, and the grains are uniformly doped with Co. The barium and rare earth metals concentrate into 1.5-μm-wide particles embedded in a matrix of ZnO grains. Within the grains and at grain boundaries, the barium and rare-earth--metal concentration is below the detection limit of the energy-dispersive spectrometer technique (about 0.5%). No intergranular films, amorphous or crystalline, are detected, to within 10 A resolution. These results are shown to be consistent with the grain boundary charge depletion model for the voltage barrier formation and breakdown

Iron corrosion inhibition by phosphonate complexes of rare earth metals

International Nuclear Information System (INIS)

Kuznetsov, Yu.I.; Raskol'nikov, A.F.; Starobinskaya, I.V.; Alekseev, V.N.

1993-01-01

Capability is shown of trivalent rare earth nitrilotrimethylphosphonates (R= Ce, Pr, Nd, Eu, Lu, Y) to retard steel corrosion in soft water due to the formation of slightly soluble hydroxides on steel surface. The protective film is produced as a result of electrophilic substitution of nascent iron cations for rare earth ions in near the surface layer. The introduction of rare earth cations into the protective film is ascertained by Auger spectroscopy in combination with the argon spraying. A quantitative interrelation between the protective effectiveness and solubility product of rare earth hydroxides is revealed

Impurity-doped micro-lasers

NARCIS (Netherlands)

Pollnau, Markus

2013-01-01

Recently rare-earth-ion-doped dielectric channel waveguides have proven their ability to generate highly efficient laser output in the fundamental mode. Here we review our recent achievements obtained in crystalline potassium double tungstates and amorphous aluminum oxide.

Isopiestic determination of the activity coefficients of some aqueous rare earth electrolyte solutions at 250C. I. The rare earth chlorides

International Nuclear Information System (INIS)

Spedding, F.H.; Weber, H.O.; Saeger, V.W.; Petheram, H.H.; Rard, J.A.; Habenschuss, A.

1976-01-01

The osmotic coefficients of the aqueous trichlorides of La, Pr, Nd, Sm, Eu, Gd, Tb, Dy, Ho, Er, Tm, Yb, Lu, and Y were determined from 0.1 M to saturation at 25 0 C. Semiempirical least-squares equations were obtained for the osmotic coefficients as a function of molality and these equations were used to calculate water activities and mean molal activity coefficients. The water activities of the light rare earth chlorides at constant molalities are higher than for the heavy rare earths, while the mean molal activity coefficients are larger for the heavy rare earths than for the light ones. The above effects are discussed in terms of changes in the cationic radii and hydration of the rare earth ions

Tunable optical properties of some rare earth elements-doped mayenite Ca12Al14O33 nanopowders elaborated by oxalate precursor route

Science.gov (United States)

Rashad, Mohamed M.; Mostafa, Ahmed G.; Mwakikunga, Bonex W.; Rayan, Diaa A.

2017-01-01

Rare earth (RE) ions-doped mayenite Ca12Al14- x RE x O33 nanopowders (where RE = La and Gd and x = 0-1.0) were synthesized using the oxalate precursor technique. The as-prepared precursors were calcined at 800 °C for 2 h. Obviously, all RE-doped Ca12Al14- x RE x O33 possessed a well-crystalline cubic mayenite phase till RE content of 0.8. The crystallo-chemical aspects including crystallite size, lattice parameters, theoretical X-ray density and bulk density were robustly on RE nature and ratio. The microstructure and the average grain size were significantly influenced by the RE kind and content. The high transparency of Ca12Al14- x RE x O33 over 80% was found to be evinced in the visible wavelength range of 400-800 nm. Besides, the incorporation of RE cation minimized the direct band gap energy from 4.42 eV for pure mayenite to 3.85 and 3.59 eV with x value 1.0 of La3+ and Gd3+ ions. The photoluminescence spectra of pure mayenite nanoparticles showed that the band edge emission ( λ exc = 248 nm) with an intense visible emission band at 360 nm was detected. Otherwise, the band edge emission showed a slight shift toward short wavelength due to the substitution Al3+ by RE3+ ions. Such results open a new avenue for application of mayenite as a good candidate for transparent low-temperature electron conductor for optoelectronics applications.

Silicon rich nitride ring resonators for rare - earth doped telecommunications-band amplifiers pumped at the O-band.

Science.gov (United States)

Xing, P; Chen, G F R; Zhao, X; Ng, D K T; Tan, M C; Tan, D T H

2017-08-22

Ring resonators on silicon rich nitride for potential use as rare-earth doped amplifiers pumped at 1310 nm with amplification at telecommunications-band are designed and characterized. The ring resonators are fabricated on 300 nm and 400 nm silicon rich nitride films and characterized at both 1310 nm and 1550 nm. We demonstrate ring resonators exhibiting similar quality factors exceeding 10,000 simultaneously at 1310 nm and 1550 nm. A Dysprosium-Erbium material system exhibiting photoluminescence at 1510 nm when pumped at 1310 nm is experimentally demonstrated. When used together with Dy-Er co-doped particles, these resonators with similar quality factors at 1310 nm and 1550 nm may be used for O-band pumped amplifiers for the telecommunications-band.

Contribution to the study of rare earth separation by ion exchange, using ammonium lactate; Contribution a l'etude de la separation des terres rares par echange d'ions a l'aide de lactate d'ammonium

Energy Technology Data Exchange (ETDEWEB)

Gratot, I [Commissariat a l' Energie Atomique, Saclay (France). Centre d' Etudes Nucleaires

1958-07-01

Using the technique of chromatography on a column of Dowex 50 resin, heated to 87 deg. C, we have studied the separation of rare earths (from holmium to praseodymium) which may be produced with the cyclotron by heavy ions, {alpha} or protons. From an ammonium lactate solution M at pH 5, separations are carried out by varying the dilution as a function of the quantity of the target rare earth and of its position during elution. When weighable quantities of the rare earth (more than 5 mg) appear towards the end of the elution, the separation is little affected this case approaches that of a tracer mixture of rare earths; if on the other hand weighable quantities of the rare earth are washed through at the beginning of the chromatogram, the dilution must be adjusted in order to obtain a good separation. (author) [French] Par chromatographie sur colonne de resine Dowex 50, chauffee a 87 deg. C, nous avons examine la separation des terres rares (de l'holmium au praseodyme) susceptibles d'etre produites au cyclotron par ions lourds, {alpha} ou protons. A partir d'une solution de lactate d'ammonium M a pH 5, nous effectuons les separations en agissant sur la dilution en fonction de la quantite de terre rare cible et de sa position au cours de l'elution. Lorsque la terre rare en quantite ponderale (superieure a 5 mg) passe en fin d'elution, la separation est peu affectee; nous sommes ramenes au cas d'un melange de terres rares traceur; par contre, si la terre rare en quantite ponderale s'elue en tete du chromatogramme, nous devons agir sur la dilution pour obtenir une bonne separation. (auteur)

Methods of Separation of Total Rare Earths in Low-Alloy Constructional Steels

Science.gov (United States)

1954-11-10

investigation of the effects of added anions upon the absorption spectra of the rare earths elements has been continued. The effects of tartrate in...complexes, the equilibrium among the di-hydrogen cupric EDTA complex, uncomplexed cupric ions, the monohydrogen rare earth- EDTA complex and rare...solutions used are described. A polaro- graphic method for determining cupric ion concentration in support- ing KNOj solutions, and thereby supporting

Equilibrium studies on interactions of rare earth ions with phytic acid

International Nuclear Information System (INIS)

Siddiqi, K.S.; Shah, S.A.; Aqra, F.M.A.M.; Tabassum, S.; Zaidi, S.A.A.; Benlian, D.

1993-01-01

The interaction between phytic acid and trivalent rare earth metal ions, viz., Ce 3+ , Pr 3+ , Nd 3+ , Sm 3+ , Gd 3+ , Tb 3+ , Dy 3+ and HO 3+ has been investigated potentiometrically at 25degC. The proton-ligand stability constants (pK Y H ) of phytic acid and the stability constants (logK) of metal complexes formed in aqueous medium (μ = 0.1 M NaClO 4 ) have been evaluated. The results indicate that eight protons of phytic acid are highly acidic, two are weakly acidic and two very weakly acidic, titrable in the pH ranges 1.2-4.9, 5.0-8.15 and 8.3-11.0 respectively. The stability of each phytic acid-lanthanide ion complex decreases with an increase in pH and follows the usual trend through the series. (author). 11 refs., 2 tabs

Equilibrium studies on mixed ligand complexes of some tripositive rare earth ions

International Nuclear Information System (INIS)

Vimal, Rashmi; Singh, Mamta; Ram Nayan

1996-01-01

Interaction of the rare earth ions, La 3+ , Ce 3+ , Pr 3+ , Nd 3+ , Sm 3+ and Eu 3+ with the pair of ligands 1-amino-2-naphthol-4-sulphonic acid (an, H 2 A) and o-aminophenol (ap, HB) have been studied in aqueous solution at 25 degC (μ=0.1 M KNO 3 /NaCl). Equilibrium constants of the reactions involving the formations of the mixed ligand species MAB, MA 2 B 2- , MB 2 A - (M = metal ion) and the binary complexes containing up to three ligand molecules have been evaluated from the pH-metric data, and coordinating behaviour of the ligands in the formation of the mixed ligand complexes has been discussed. (author). 10 refs., 1 tab., 1 fig

White upconversion luminescence in Tm3+/Ho3+/Yb3+ triply doped K+-Na+ ion-exchanged aluminum germanate glass channel waveguide

Science.gov (United States)

Liu, Xiao; Chen, Baojie; Pun, Edwin Yue Bun; Lin, Hai

2013-01-01

Rare-earth ions doped K+-Na+ ion-exchanged aluminum germanate (NMAG) glass channel waveguides have been designed and fabricated. Under 980 nm laser pumping, an intense upconversion white light transmission trace was observed in Tm3+/Ho3+/Yb3+ triply doped NMAG glass channel waveguide and a high-brightness light spot was achieved from the output end of the fiber connected to the waveguide channel. The fluorescent colors were diverse and located within or near the white region in CIE chromaticity diagram under various pumping powers. These admirable results indicate that Tm3+/Ho3+/Yb3+ triply doped NMAG channel waveguide is a promising light source for medical and high-precision processing illumination.

TL process in europium doped alkaline earth sulphate phosphors- a review

International Nuclear Information System (INIS)

Bhatt, B.C.

2003-01-01

CaSO 4 doped with the rare earth (RE) ion dysprosium or thulium is used routinely as a thermoluminescent dosimeter (TLD) to monitor personal exposure to x- and γ-radiation. The CaSO 4 :Eu phosphor is potentially important for radio photoluminescence (RPL) and ultraviolet (UV) dosimetry. Eu 3+ → Eu 2+ conversion is suggested to play a pivotal role in UV and γ-ray induced thermoluminescence. However, there is disagreement among different workers on the mechanism of gamma and UV induced TL in this phosphor system. This paper will review the work reported on CaSO 4 :Eu and make effects to project overall picture on this phosphor system. (author)

Crystal field symmetry and magnetic interactions in rare earth-silver amorphous alloys

International Nuclear Information System (INIS)

Pappa, Catherine.

1979-01-01

A study has been made of the following rare earth based amorphous alloys: Ndsub(x)Agsub(100-x), Prsub(x)Agsub(100-x), Gdsub(x)Agsub(100-x), Tlsub(x)Agsub(100-x). In rare earth based amorphous alloys, the symmetrical distribution of the crystal field is very wide and hence not very sensitive to the content of the alloys. The existence of preponderant negative magnetic interactions leads to an upset magnetic order, the magnetization of a small volume not being nil. The magnetic behaviour of alloys with a small concentration of rare earths is governed by the existence of clusters of statistical origin, within which a rare earth ion has at least one other rare earth ion in the position of first neighbour. The presence of a high anisotropy at low temperatures make the magnetic interactions between clusters inoperative [fr

Rare earth phosphors and phosphor screens

International Nuclear Information System (INIS)

Buchanan, R.A.; Maple, T.G.; Sklensky, A.F.

1981-01-01

Advances in the use of stabilized rare earth phosphors and of conversion screens using these materials are examined. In particular the new phosphors discussed in this invention consist of oxybromides of yttrium, lanthanum and gadolinium with a luminescent activator ion stabilized by an oxychloride or oxyfluoride surface layer and the conversion screens include trivalent cerium as the activator ion. (U.K.)

Upconversion improvement in KLaF{sub 4}:Yb{sup 3+}/Er{sup 3+} nanoparticles by doping Al{sup 3+} ions

Energy Technology Data Exchange (ETDEWEB)

Zhou, Haifang [Fuzhou University, School of Physics and Information Engineering, and Institute of Micro-Nano Devices and Solar Cells, Fuzhou (China); Jiangsu Collaborative Innovation Center of Photovoltaic Science and Engineering, Changzhou, Jiangsu (China); Wang, Xiechun; Lai, Yunfeng; Cheng, Shuying; Zheng, Qiao; Yu, Jinlin [Fuzhou University, School of Physics and Information Engineering, and Institute of Micro-Nano Devices and Solar Cells, Fuzhou (China)

2017-10-15

Rare-earth ion-doped upconversion (UC) materials show great potential applications in optical and optoelectronic devices due to their novel optical properties. In this work, hexagonal KLaF{sub 4}:Yb{sup 3+}/Er{sup 3+} nanoparticles (NPs) were successfully synthesized by a hydrothermal method, and remarkably enhanced upconversion luminescence in green and red emission bands in KLaF{sub 4}:Yb{sup 3+}/Er{sup 3+} NPs has been achieved by doping Al{sup 3+} ions under 980 nm excitation. Compared to the aluminum-free KLaF{sub 4}:Yb{sup 3+}/Er{sup 3+} NPs sample, the UC fluorescence intensities of the green and red emissions of NPs doped with 10 at.% Al{sup 3+} ions were significantly enhanced by 5.9 and 7.3 times, respectively. Longer lifetimes of the doped samples were observed for the {sup 4}S{sub 3/2} state and {sup 4}F{sub 9/2} state. The underlying reason for the UC enhancement by doping Al{sup 3+} ions was mainly ascribed to distortion of the local symmetry around Er{sup 3+} ions and adsorption reduction of organic ligands on the surface of NPs. In addition, the influence of doping Al{sup 3+} ions on the structure and morphology of the NPs samples was also discussed. (orig.)

Structures, stabilities, and electronic properties for rare-earth lanthanum doped gold clusters

International Nuclear Information System (INIS)

Zhao, Ya-Ru

2015-01-01

The structures, stabilities, and electronic properties of rare-earth lanthanum doped gold La 2 Au n (n = 1-9) and pure gold Au n (n ≤ 11) clusters have been investigated by using density functional theory. The optimized geometries show that the lowest energy structures of La 2 Au n clusters favour the 3D structure at n ≥ 3. The lanthanum atoms can strongly enhance the stabilities of gold clusters and tend to occupy the most highly coordinated position. By analysing the gap, vertical ionization potential, and chemical hardness, it is found that the La 2 Au 6 isomer possesses higher stability for small-sized La 2 Au n clusters (n = 1-9). The charges in the La 2 Au n clusters transfer from La atoms to the Au n host. In addition, Wiberg bond indices analysis reveals that the intensity of different bonds of La 2 Au n clusters exhibits a sequence of La-La bond > La-Au bond > Au-Au bond.

Phase Transformation and Lattice Parameter Changes of Non-trivalent Rare Earth-Doped YSZ as a Function of Temperature

Science.gov (United States)

Jiang, Shengli; Huang, Xiao; He, Zhang; Buyers, Andrew

2018-05-01

To examine the effect of doping/co-doping on high-temperature phase compositions of YSZ, stand-alone YSZ and CeO2 and Nb2O5 co-doped YSZ samples were prepared using mechanical alloy and high-temperature sintering. XRD analysis was performed on these samples from room temperature to 1100 °C. The results show that the structure for the co-doped samples tends to be thermally stable when the test temperature is higher than a critical value. Monoclinic phase was dominant in Nb2O5 co-doped YSZ at temperatures lower than 600 °C, while for the YSZ and CeO2 co-doped YSZ, cubic/tetragonal phase was dominant in the whole test temperature range. The lattice parameters for all the samples increase with increasing test temperature generally. The lattice parameters for the two non-trivalent rare earth oxides co-doped YSZ show that the lattice parameter a for the cubic phase of the Ce4+ co-doped YSZ is consistently greater than that of 7YSZ which is related to the presence of larger radius of Ce4+ in the matrix. The lattice parameters a, b, c for the monoclinic phase of Ce4+ co-doped YSZ are much closer to each other than that of the Nb5+ co-doped YSZ, indicating the former has better tendency to form cubic/tetragonal phase, which is desired for vast engineering applications.

Correlations in rare-earth transition-metal permanent magnets

International Nuclear Information System (INIS)

Skomski, R.; Manchanda, P.; Kashyap, A.

2015-01-01

It is investigated how electron-electron correlations affect the intrinsic properties of rare-earth transition-metal magnets. Focusing on orbital moment and anisotropy, we perform model calculations for 3d-4f alloys and density-functional theory (DFT) calculations for NdCo 5 . On an independent-electron level, the use of a single Slater determinant with broken spin symmetry introduces Hund's rule correlations, which govern the behavior of rare-earth ions and of alloys described by the local spin density approximation (LSDA) and LSDA + U approximations to DFT. By contrast, rare-earth ions in intermetallics involve configuration interactions between two or more Slater determinants and lead to phenomena such as spin-charge distribution. Analyzing DFT as a Legendre transformation and using Bethe's crystal-field theory, we show that the corresponding density functionals are very different from familiar LSDA-type expressions and outline the effect of spin-charge separation on the magnetocrystalline anisotropy

Correlations in rare-earth transition-metal permanent magnets

Science.gov (United States)

Skomski, R.; Manchanda, P.; Kashyap, A.

2015-05-01

It is investigated how electron-electron correlations affect the intrinsic properties of rare-earth transition-metal magnets. Focusing on orbital moment and anisotropy, we perform model calculations for 3d-4f alloys and density-functional theory (DFT) calculations for NdCo5. On an independent-electron level, the use of a single Slater determinant with broken spin symmetry introduces Hund's rule correlations, which govern the behavior of rare-earth ions and of alloys described by the local spin density approximation (LSDA) and LSDA + U approximations to DFT. By contrast, rare-earth ions in intermetallics involve configuration interactions between two or more Slater determinants and lead to phenomena such as spin-charge distribution. Analyzing DFT as a Legendre transformation and using Bethe's crystal-field theory, we show that the corresponding density functionals are very different from familiar LSDA-type expressions and outline the effect of spin-charge separation on the magnetocrystalline anisotropy.

Forced-flow chromatography of rare earths using sensitive spectrophometry

International Nuclear Information System (INIS)

Matsui, Masakazu; Aoki, Toru; Kumagai, Tetsu.

1981-01-01

The sensitive spectrophotometric method for the rare earth elements with xylenol orange in the presence of cetylpyridinium bromide was applied to the continuous detection system of liquid chromatography. Fourteen rare earth elements were completely separated within 130 min cation-exchange chromatography using 2-hydroxy-iso-butylic acid. The eluted ions were determined with absorption maxima of their complexes at around 610 nm. A linear relationship between the peak height and the amounts of rare earth elements was also obtained over the range 0.04 to 0.5 MU g. (author)

Improvement of corrosion resistance and biocompatibility of rare-earth WE43 magnesium alloy by neodymium self-ion implantation

International Nuclear Information System (INIS)

Jin, Weihong; Wu, Guosong; Feng, Hongqing; Wang, Wenhao; Zhang, Xuming; Chu, Paul K.

2015-01-01

Highlights: • Nd self-ion implantation produces a smooth and hydrophobic surface on rare-earth WE43 Mg alloy. • The implanted layer is composed of mainly Nd 2 O 3 and MgO. • Degradation is significantly retarded in simulated body fluids and cell culture medium. • The Nd-implanted WE43 alloy exhibits remarkably enhanced cell adhesion and biocompatibility. - Abstract: Without introducing extraneous elements, a small amount of Nd is introduced into rare-earth WE43 magnesium alloy by ion implantation. The surface composition, morphology, polarization, and electrochemical properties, as well as weight loss, pH, and leached ion concentrations after immersion, are systematically evaluated to determine the corrosion behavior. The cell adhesion and viability are also determined to evaluate the biological response in vitro. A relatively smooth and hydrophobic surface layer composed of mainly Nd 2 O 3 and MgO is produced and degradation of WE43 is significantly retarded. Furthermore, significantly enhanced cell adhesion and excellent biocompatibility are observed after Nd self-ion implantation

Structure, dielectric and electrical properties of cerium doped barium zirconium titanate ceramics

International Nuclear Information System (INIS)

Feng Hongjun; Hou Jungang; Qu Yuanfang; Shan Dan; Yao Guohua

2012-01-01

Highlights: ► Rare-earth doped barium zirconate titanate (BZT) ceramics, Ba(Zr 0.25 Ti 0.75 )O 3 + xCeO 2 , (x = 0–1.5 at%) were obtained by a solid state reaction route. ► Morphological analysis on sintered samples by scanning electron microscopy shows that the addition of rare-earth ions affects the growth of the grain and remarkably changes the grain morphology. ► The effect of rare-earth addition to BZT on dielectric and electrical properties is analyzed, demonstrating that the samples with x = 0.4 and x = 0.6 could be semiconducting in air atmosphere. - Abstract: Rare-earth doped barium zirconium titanate (BZT) ceramics, Ba(Zr 0.25 Ti 0.75 )O 3 + xCeO 2 , (x = 0–1.5 at%) were obtained by a solid state reaction route. Perovskite-like single-phase compounds were confirmed from X-ray diffraction data and the lattice parameters were refined by the Rietveld method. It is found that, integrating with the lattice parameters and the distortion of crystal lattice, there is an alternation of substitution preference of cerium ions for the host cations in perovskite lattice. Morphological analysis on sintered samples by scanning electron microscopy shows that the addition of rare-earth ions affects the growth of the grain and remarkably changes the grain morphology. The effect of rare-earth addition to BZT on dielectric and electrical properties is analyzed. High values of dielectric tunability are obtained for cerium doped BZT. Especially, the experimental results on the effect of the contents of rare-earth addition on the resistivity of BZT ceramics were investigated, demonstrating that the samples with x = 0.4 and x = 0.6 could be semiconducting in air atmosphere.

Extraction studies on rare earths using dinonyl phenyl phosphoric acid

International Nuclear Information System (INIS)

Anitha, M.; Singh, D.K.; Kotekar, M.K.; Vijayalakshmi, R.; Singh, H.

2011-01-01

Rare earths are widely used in phosphor materials, magnetic substances, alloys, catalyst, lasers, superconductors, solid oxide fuel cells and in nuclear applications. The high value of these elements depends on their effective separation into high purity compounds. The separation into individual rare earths is very difficult to achieve, due to the very low separation factors between two adjacent rare earths arising due to similar chemical properties. Taking the advantage of variation in basicity, the separation is generally accomplished by solvent extraction or ion exchange. There are several references on the separation of rare earth in different media employing various types of extractants such as 2-ethylhexyl 2-ethyhexylphosphonic acid (EHEHPA) and di-2-ethyl hexyl phosphoric acid (D2EHPA) which have been widely used for the separation and purification of rare earths. Dinonyl phenyl phosphoric acid (DNPPA) is an organo phosphorus extractant (pKa = 2.54) and is an aromatic analogue of D2EHPA, which extracts metal ion by cation exchange mechanism. DNPPA was explored to recover rare earths from phosphate media such as wet process phosphoric acid and merchant grade acid. However, there is no information available in literature on DNPPA for RE extraction from chloride medium. Therefore, an attempt has been made in the present study to investigate the feasibility of using DNPPA for extraction of La(III), Dy(III) and Y(III) from chloride medium

Reversed-phase thin-layer chromatography of the rare earth elements

International Nuclear Information System (INIS)

Kuroda, R.; Adachi, M.; Oguma, K.

1988-01-01

Partition chromatographic behaviour of the rare earth elements on C 18 bonded silica reversed-phase material has been investigated by thin-layer chromatography in methanol - lactate media. The rare earth lactato complexes are distributed and fractionated on bonded silica layers without ion-interaction reagents. The concentration and pH of lactate solution, methanol concentration and temperature have effects on the migration and resolution of the rare earth elements. The partition system is particularly suited to separate adjacent rare earths of middle atomic weight groups, allowing the separation of gadolinium, terbium, dysprosium, holmium, erbium and thulium to be achieved by development to 18 cm distance. (orig.)

Effect of crystalline electric fields and long-range magnetic order on superconductivity in rare earth alloys and compounds

International Nuclear Information System (INIS)

McCallum, R.W.

1977-01-01

The behavior of rare earth ions in a superconducting matrix has been studied in two distinct regimes. First, the effects of crystal field splitting of the 4f levels of a magnetic rare earth ion in the alloy system (LaPr)Sn 3 were investigated in the limit of low Pr 3+ concentration. In this system the rare earth impurity ions occupy random La sites in the crystal lattice. Second, the interaction of long-range magnetic order and superconductivity was explored in the ternary rare earth molybdenum chalcogenide systems. In these compounds the rare earth ions occupy periodic lattice sites in contrast to the random distribution of magnetic ions in dilute impurity alloy systems such as (LaPr)Sn 3

Focused-ion-beam nano-structured rib channel waveguides in KY(WO4)2 for laser applications

NARCIS (Netherlands)

Gardillou, F.; Romanyuk, Y.E.; Pavius, M.; Borca, C.N.; Salathé, R.P.; Pollnau, Markus

2006-01-01

Bulk $KY(WO_4)_2$ (hereafter KYW) laser crystals doped with rare-earth ions are recognized to be among the most promising host materials for obtaining novel solid-state lasers. The rare-earth ions $RE^{3+}$ are easily incorporated in the KYW structure by replacing the $Y{3+}$ ions, resulting in a

Effect of rare earth substitution in cobalt ferrite bulk materials

International Nuclear Information System (INIS)

Bulai, G.; Diamandescu, L.; Dumitru, I.; Gurlui, S.; Feder, M.; Caltun, O.F.

2015-01-01

The study was focused on the influence of small amounts of rare earth (RE=La, Ce, Sm, Gd, Dy, Ho, Er, Yb) addition on the microstructure, phase content and magnetic properties of cobalt ferrite bulk materials. The X-Ray diffraction measurements confirmed the formation of the spinel structure but also the presence of secondary phases of RE oxides or orthoferrite in small percentages (up to 3%). Density measurements obtained by Archimedes method revealed a ~1 g cm −3 decrease for the RE doped cobalt ferrite samples compared with stoichiometric one. Both the Mössbauer and Fourier Transform Infrared Spectrocopy analysis results confirmed the formation of the spinel phase. The saturation magnetization and coercive field values of the doped samples obtained by Vibrating Sample Magnetometry were close to those of the pure cobalt ferrite. For magnetostrictive property studies the samples were analyzed using the strain gauge method. Higher maximum magnetostriction coefficients were found for the Ho, Ce, Sm and Yb doped cobalt ferrite bulk materials as related to the stoichiometric CoFe 2 O 4 sample. Moreover, improved strain derivative was observed for these samples but at higher magnetic fields due to the low increase of the coercive field values for doped samples. - Highlights: • Substitution by a large number of rare earth elements was investigated. • First reported results on magnetostriction measurements of RE doped cobalt ferrite. • The doped samples presented an increased porosity and a decreased grain size. • Increased magnetostrctive response was observed for several doped samples

K isomerism and collectivity in neutron-rich rare-earth isotopes.

OpenAIRE

Patel, Zena

2016-01-01

Neutron-rich rare-earth isotopes were produced by in-flight fission of 238U ions at the Radioactive Isotope Beam Factory (RIBF), RIKEN, Japan. In-flight fission of a heavy, high-intensity beam of 238U ions on a light target provides the cleanest secondary beams of neutron-rich nuclei in the rare-earth region of isotopes. In-flight fission is advantageous over other methods of nuclear production, as it allows for a secondary beam to be extracted, from which the beam species can be separated an...

Preparation and luminescent properties of the novel polymer-rare earth complexes composed of Poly(ethylene-co-acrylic acid) and Europium ions

Science.gov (United States)

Wu, Yuewen; Hao, Haixia; Wu, Qingyao; Gao, Zihan; Xie, Hongde

2018-06-01

A series of novel polymer-rare earth complexes with Eu3+ ions have been synthesized and investigated successfully, including the binary complexes containing the single ligand poly(ethylene-co-acrylic acid) (EAA) and the ternary complexes using 1,10-phenanthroline (phen), dibenzoylmethane (DBM) or thenoyltrifluoroacetone (TTA) as the second ligand. Their structures have been characterized by Fourier transform infrared spectroscopy (FT-IR), elemental analysis and X-ray diffraction (XRD), which confirm that both EAA and small molecules participate in the coordination reaction with rare earth ions, and they can disperse homogeneously in the polymer matrixes. Both ultraviolet-visible (UV-vis) absorption and photoluminescence tests for the complexes have been recorded. The relationship between fluorescence intensity of polymer-rare earth complexes and the quantity of ligand EAA has been studied and discussed. The films casted from the complexes solution can emit strong characteristic red light under UV light excitation. All these results suggest that the complexes possess potential application as luminescent materials.

In Situ Neutron Diffraction of Rare-Earth Phosphate Proton Conductors Sr/Ca-doped LaPO4 at Elevated Temperatures

Science.gov (United States)

Al-Wahish, Amal; Al-Binni, Usama; Bridges, C. A.; Huq, A.; Bi, Z.; Paranthaman, M. P.; Tang, S.; Kaiser, H.; Mandrus, D.

Acceptor-doped lanthanum orthophosphates are potential candidate electrolytes for proton ceramic fuel cells. We combined neutron powder diffraction (NPD) at elevated temperatures up to 800° C , X-ray powder diffraction (XRD) and scanning electron microscopy (SEM) to investigate the crystal structure, defect structure, thermal stability and surface topography. NPD shows an average bond length distortion in the hydrated samples. We employed Quasi-Elastic Neutron Scattering (QENS) and electrochemical impedance spectroscopy (EIS) to study the proton dynamics of the rare-earth phosphate proton conductors 4.2% Sr/Ca-doped LaPO4. We determined the bulk diffusion and the self-diffusion coefficients. Our results show that QENS and EIS are probing fundamentally different proton diffusion processes. Supported by the U.S. Department of Energy.

Equilibrium studies on interactions of rare earth ions with phytic acid

Energy Technology Data Exchange (ETDEWEB)

Siddiqi, K S; Shah, S A; Aqra, F M.A.M.; Tabassum, S; Zaidi, S A.A. [Aligarh Muslim Univ. (India). Dept. of Chemistry; Benlian, D [Centre de St Jerome, Cedex (France). Laboratoire de Chimie de Coordination

1993-05-01

The interaction between phytic acid and trivalent rare earth metal ions, viz., Ce[sup 3+], Pr[sup 3+], Nd[sup 3+], Sm[sup 3+], Gd[sup 3+], Tb[sup 3+], Dy[sup 3+] and HO[sup 3+] has been investigated potentiometrically at 25degC. The proton-ligand stability constants (pK[sub Y][sup H]) of phytic acid and the stability constants (logK) of metal complexes formed in aqueous medium ([mu] = 0.1 M NaClO[sub 4]) have been evaluated. The results indicate that eight protons of phytic acid are highly acidic, two are weakly acidic and two very weakly acidic, titrable in the pH ranges 1.2-4.9, 5.0-8.15 and 8.3-11.0 respectively. The stability of each phytic acid-lanthanide ion complex decreases with an increase in pH and follows the usual trend through the series. (author). 11 refs., 2 tabs.

Rare earths

International Nuclear Information System (INIS)

1984-01-01

The conference was held from September 12 to 13, 1984 in Jetrichovice, Czechoslovakia. The participants heard 16 papers of which 4 were inputted in INIS. These papers dealt with industrial separation processes of rare earths, the use of chemical methods of separation from the concentrate of apatite and bastnesite, the effect of the relative permittivity of solvents in the elution of rare earth elements from a cation exchanger, and the determination of the content of different rare earth elements using X-ray fluorescence analysis and atomic absorption spectroscopy. (E.S.)

The role of rare earths in narrow energy gap semiconductors

International Nuclear Information System (INIS)

Partin, D.L.; Heremans, J.; Morelli, D.T.; Thrush, C.M.

1991-01-01

Narrow energy band gap semiconductors are potentially useful for various devices, including infrared detectors and diode lasers. Rare earth elements have been introduced into lead chalcogenide semiconductors using the molecular beam epitaxy growth process. Europium and ytterbium increase the energy band gap, and nearly lattice-matched heterojunctions have been grown. In some cases, valence changes in the rare earth element cause doping of the alloy. In this paper some initial investigations of the addition of europium to indium antimonide are reported, including the variation of lattice parameter and optical transmission with composition and a negative magnetoresistance effect

Quantum efficiency of silica-coated rare-earth doped yttrium silicate

International Nuclear Information System (INIS)

Cervantes-Vásquez, D.; Contreras, O.E.; Hirata, G.A.

2013-01-01

The photoluminescent properties of rare earth-activated white-emitting Y 2 SiO 5 :Ce,Tb nanocrystalline phosphor prepared by two different methods, pressure-assisted combustion synthesis and sol–gel, were studied. The synthesized phosphor samples were post-annealed at 1373 K and 1623 K in order to obtain the X1-Y 2 SiO 5 and X2-Y 2 SiO 5 phases, respectively, which were confirmed by X-ray diffraction measurements. Photoluminescence analysis showed the contribution of two blue-emission bands within the 380–450 nm region originating from 5d–4f transitions in Ce 3+ ions and a well-defined green emission of Tb 3+ ions located at 545 nm corresponding to 5 D 4 → 7 F 5 electronic transitions. Thereafter, Y 2 SiO 5 :Ce,Tb powders were coated with colloidal silica in order to investigate the effect of silica coatings on their luminescent properties. Absolute fluorescence quantum efficiency measurements were carefully performed, which revealed an increase of 12% of efficiency in coated compared with bare-Y 2 SiO 5 :Ce,Tb phosphor. -- Highlights: • Y 2 SiO 5 :Ce,Tb phosphor powders were successfully coated with colloidal silica. • Post-annealing treatments improved the quantum efficiency of silica-coated Y 2 SiO 5 :Ce,Tb phosphors. • Absolute fluorescence quantum efficiency measurements showed an increase of 12%

Novel laser nanomaterials based on rare-earth compounds

Energy Technology Data Exchange (ETDEWEB)

Patel, Darayas N., E-mail: dpatel@oakwood.edu [Oakwood University, Department of Mathematics and Computer Science, 7000 Adventist Blvd. Huntsville, AL 35896 (United States); Hardy, Lauren A.; Smith, Tabatha J.; Smith, Eva S.; Wright, Donald M. [Oakwood University, Department of Mathematics and Computer Science, 7000 Adventist Blvd. Huntsville, AL 35896 (United States); Sarkisov, Sergey [SSS Optical Technologies, LLC, 515 Sparkman Drive, Suite 122, Huntsville, AL 35816 (United States)

2013-01-15

We report on the infrared-to-visible upconversion luminescence in microcrystalline powders and photonic crystal fibers filled with nanocolloids of trivalent rare-earth ion co-doped NaYF{sub 4} phosphor. The phosphor was prepared using a simple co-precipitation synthetic method. Nanocolloids of the phosphor were prepared by selective precipitation in methanol and laser ablation in water. Optical dynamic scatterometry determined average particle sizes of the nanocolloids of 1.5-1.9 nm in methanol and 83.8-86.4 nm in water. Nanocolloids of these phosphors were utilized as laser filling medium in photonic crystal fibers. - Highlights: Black-Right-Pointing-Pointer Synthesize highly efficient hexagonal-phase NaYF{sub 4}:Er{sup 3+}, Yb{sup 3+} powder and nanocolloid. Black-Right-Pointing-Pointer Laser/amplifier containing the NaYF{sub 4} nanocolloid were pumped with 980 nm diode laser. Black-Right-Pointing-Pointer Emission peaks were observed at 540 nm, 654 nm and 840.4 nm from the fiber arrangement.

Raw materials for advanced ceramics: rare earths separation processes

International Nuclear Information System (INIS)

Ricci, D.R.; Nobre, J.S.M.; Paschoal, J.O.A.

1990-01-01

The importance of obtaining purified rare earths oxidesis related, mainly to the increasing use of these compounds as raw materials for advanced ceramics. Processes of rare earths separation and purification are almost always based on the solvent extraction, fractional precipitation and ion exchange chromatography techniques, whose association depends on the initial concentrate and on the desired purity. This paper describes some steps of fractionation of didymium carbonate by using the solvent extraction and fractional precipitation techniques. The experimental conditions presented here have enable the production of lantanium, neodimium - praseodimium, samarium - gadolinium and ytrium concentrates, which constitute the intermediate fractions of the overall process to obtain high purity rare earths. (author) [pt

Link between optical spectra, crystal-field parameters, and local environments of Eu3+ ions in Eu2O3-doped sodium disilicate glass

International Nuclear Information System (INIS)

Qin, T.; Mountjoy, G.; Afify, N. D.; Reid, M. F.; Yeung, Y. Y.; Speghini, A.; Bettinelli, M.

2011-01-01

Rare-earth-doped glasses are key materials for optical technology due to the luminescent properties of 4f n ions. The crystal-field model describes the effect of local environment on transitions between 4f electrons. We present a detailed modeling study of the optical spectra of sodium disilicate glass, 33Na 2 O·67SiO 2 , doped with 0.2% and 1.0 mol%Eu 2 O 3 . This study uses very large molecular dynamics models with up to 100 Eu 3+ ions, the superposition model for covalent and overlap effects on crystal-field parameters, and realistic values for homogeneous linewidth broadening. The simulated spectra are in reasonable agreement with experiment. The trends in 7 F J energy levels across different Eu 3+ ion sites have been examined and a very detailed analysis is presented that looks at how features of the spectra are related to features of the local environment of Eu 3+ ions. Increasing the crystal-field strength S total causes the 7 F 0 energy level to decrease and causes the splitting of 7 F J manifolds to increase, and this is due to increasing mixing of 4f wave functions. To a reasonable approximation the crystal-field strength components S k depend on angular positions of ligands independently of distances to ligands. The former are seen to be more significant in determining S k , which are closely related to the rotationally invariant bond-orientational order parameters Q k . The values of S 2 are approximately linear in Q 2 , and the values of Q 2 are higher for fivefold than sixfold coordinated rare-earth ions. These results can be of importance for efforts to enhance the local environment of rare-earth ions in oxide glasses for optical applications.

First-principles calculation on oxygen ion migration in alkaline-earth doped La2GeO5

International Nuclear Information System (INIS)

Thuy Linh, Tran Phan; Sakaue, Mamoru; Aspera, Susan Meñez; Alaydrus, Musa; Wungu, Triati Dewi Kencana; Hoang Linh, Nguyen; Kasai, Hideaki; Mohri, Takahiro; Ishihara, Tatsumi

2014-01-01

By using first-principles calculations based on the density functional theory, we investigated the doping effects of alkaline-earth metals (Ba, Sr and Ca) in monoclinic lanthanum germanate La 2 GeO 5 on its oxygen ion conduction. Although the lattice parameters of the doped systems changed due to the ionic radii mismatch, the crystal structures remained monoclinic. The contribution of each atomic orbital to electronic densities of states was evaluated from the partial densities of states and partial charge densities. It was confirmed that the materials behaved as ionic crystals comprising of cations of La and dopants and anions of oxygen and covalently formed GeO 4 . The doping effect on the activation barrier for oxygen hopping to the most stable oxygen vacancy site was investigated by the climbing-image nudged elastic band method. By tracing the charge density change during the hopping, it was confirmed that the oxygen motion is governed by covalent interactions. The obtained activation barriers showed excellent quantitative agreements with an experiment for the Ca- and Sr-doped systems in low temperatures as well as the qualitative trend, including the Ba-doped system. (paper)

Development of reduction technology for oxide fuel. Behaviour of rare-earth in lithium reduction process

International Nuclear Information System (INIS)

Kato, Tetsuya; Usami, Tsuyoshi; Yuda, Ryoichi; Kurata, Masateru; Moriyama, Hirotake

2000-01-01

Solubility measurements of rare-earth oxides in molten LiCl-Li 2 O salt and reduction tests of UO 2 doped with rare-earth oxides were carried out to determine the behavior of rare-earths in lithium reduction process. The solubility of rare-earth oxides increases in the order of Gd 2 O concentration. In multi-element systems including 6 rare-earth oxides, the solubility of each element is smaller than that in the individual systems. In the reduction tests, more than 90% of UO 2 was reduced within 1 hour after starting reduction and about 7% of rare-earths eluded into the LiCl molten salt bath containing Li 2 O which is formed by the reduction of UO 2 . The rare-earth concentrations in the bath were evaluated using the solubility data, assuming that rare-earth oxides in multi-element systems form solid solution as the equilibrium solid phase and that the activity coefficients in the solid phase are independent of the compositions. The calculated concentrations are consistent with the experimental ones obtained in the reduction tests. (author)

Study on Preparation and Property of Poly-Aminosilicone-Rare Earth Composite

Institute of Scientific and Technical Information of China (English)

Zhang Ming(张明); Qiu Guanming(邱关明); Chen Haiyan(陈海燕); Zhou Lanxiang(周兰香); Inoue Shinich; Okamoto Hiroshi

2003-01-01

The poly-aminosilicone-rare earth composite was prepared by poly-aminosilicone cross-linked with rare earth and active silanol. The thermal stability of the composites was studied by thermogravimetric analysis (TG). Force condition of the composites in electric field was analyzed and relative polarizability was derived. It is found that the composites containing different rare earth ions have different relative polarizability. The experiment results reveal that organosilicon materials with different electrical performance can be obtained by this way. Meanwhile, the absorption and flourescene spectrum of composites were also investigated. Compared to rare earth chloride, the spectrum properties of the composite are changed obviously. The possible reasons for these phenomena were discussed.

Study on Magnetic Responsibility of Rare Earth Ferrite/Polyacrylamide Magnetic Microsphere

Institute of Scientific and Technical Information of China (English)

Zhang Ming; Wang Zhifeng; Zhang Hong; Dai Shaojun; Qiu Guanming; Okamoto Hiroshi

2005-01-01

In inverse microemulsion, rare earth ferrite/polyacrylamide magnetic microsphere were prepared and their magnetic responsibility were studied by magnetic balance. Results indicate that the magnetic responsibility of microsphere relates to magnetic moment of rare earth ion, and it can be improved by the addition of dysprosium ion of high magnetic moment. Dysprosium content has an effect on magnetic responsibility of dysprosium ferrite/polyacrylamide magnetic microsphere. The microsphere displays strong magnetic responsibility when the molar ratio of Dy3+/iron is 0.20.

Using rare earth doped thiosilicate phosphors in white light emitting LEDs: Towards low colour temperature and high colour rendering

International Nuclear Information System (INIS)

Smet, P.F.; Korthout, K.; Haecke, J.E. van; Poelman, D.

2008-01-01

Rare earth doped thiosilicates are promising materials for use in phosphor converted light emitting diodes (pcLEDs). These phosphors (including the hosts Ca 2 SiS 4 , BaSi 2 S 5 and Ba 2 SiS 4 in combination with Ce 3+ and/or Eu 2+ doping) cover the entire visible part of the spectrum, as the emission colour can be changed from deep blue to red. The photoluminescence emission spectrum and the overlap of the excitation spectrum with the emission of pumping LEDs is evaluated. The trade-off between high colour rendering and high electrical-to-optical power efficiency is discussed by simulation with both blue and UV emitting LEDs. Finally, a phosphor combination with low colour temperature (3000 K) and high colour rendering (CRI = 93) is proposed

Extraction of rare earths from iron-rich rare earth deposits

OpenAIRE

Bisaka, K.; Thobadi, I.C.; Pawlik, C.

2017-01-01

Rare earth metals are classified as critical metals by the United Nations, as they have found wide application in the fabrication of magnets, particularly those used in green energy technologies which mitigate global warming. Processing of ores containing rare earth elements is complex, and differs according to the nature of each ore. In the conventional process, run of mine (ROM) ores are processed in a physical separation plant to produce a concentrate from which rare earth elements are ext...

Ion transport under the effect of an electric field in porous medium: application to the separation of rare earths by focalization electrophoresis; Transport d'ions sous l'effet d'un champ electrique en milieu poreux: Application a la separation de terres rares par electrophorese a focalisation

Energy Technology Data Exchange (ETDEWEB)

Vieira-Nunes, A I

1999-01-15

Trivalent ions of rare earth elements have very similar properties and their difficult separation each from another is usually carried out by liquid-liquid extraction or ion exchange. Focalization electrophoresis represents an alternative route to the usual techniques. The purpose of this work consisted of the fundamental investigation of ion transport phenomena in electrophoretic processes. Focalization electrophoresis is suitable for separation of amphoteric species such as rare earth ions, using a pH gradient in the cell and upon addition of a complexed agent e. g. EDTA. This technique relies upon the difference in iso-electrical points of the considered species, being under the form of free cation near the anode, and in the form of anionic complexed species closer to the cathode. Rare earth species are submitted to the antagonist effects of diffusion and migration, enabling their focalization to occur at the iso-electrical point, corresponding to nil value of their effective mobility. Following a literature survey on rare earth elements and electrophoresis processes, the document describes theoretical and experimental investigations of complexation equilibria of some rare earth elements, namely lanthanum, neodymium, praseodymium and cerium, depending on pH. Values for the iso-electrical points could be estimated. Transport and focalization phenomena in view of rare earth separation, are dealt in the last chapter. Investigations were first carried out without forced circulation of the electrolyte solution and the transient behavior of the system allowed operating conditions to be design and built-up of a continuous device, more suitable to separation, and provided with 42 potential and 42 temperature sensors: the results of the preliminary runs, in form of variable profiles, are presented and discussed. (author)

Multiphonon-assisted anti-Stokes and Stokes fluorescence of triply ionized rare-earth ions

International Nuclear Information System (INIS)

Auzel, F.

1976-01-01

Experimental demonstration of multiphonon-assisted anti-Stokes and Stokes excitation of rare-earth ions (R 3+ ) in different hosts, that is, in a weak-coupling ion-lattice interaction case, is obtained. An exponential behavior of excitation probabilities with respect to energy difference between excitation and electronic line is found just as for multiphonon-assisted nonradiative decay and energy transfer. Exponential parameters α/sub As/ and α/sub S/ for anti-Stokes and Stokes excitation are measured and linked to the Miyakawa-Dexter α parameter for decay, leading to estimates for Pekar-Huang-Rhys coupling parameter S 0 of about 0.04, in agreement with values obtained from one-phonon spectra or nonradiative-decay measurements. A semiempirical formula is deduced to obtain α from only one parameter, an effective phonon energy

A general theory for radioactive processes in rare earth compounds

International Nuclear Information System (INIS)

Acevedo, R.; Meruane, T.

1998-01-01

The formal theory of radiative processes in centrosymmetric coordination compounds of the Ln X 3+ is a trivalent lanthanide ion and X -1 =Cl -1 , Br -1 ) is put forward based on a symmetry vibronic crystal field-ligand polarisation model. This research considers a truncated basis set for the intermediate states of the central metal ion and have derived general master equations to account for both the overall observed spectral intensities and the measured relative vibronic intensity distributions for parity forbidden but vibronically allowed electronic transitions. In addition, a procedure which includes the closure approximation over the intermediate electronic states is included in order to estimate quantitative crystal field contribution to the total transition dipole moments of various and selected electronic transitions. This formalism is both general and flexible and it may be employed in any electronic excitations involving f N type configurations for the rare earths in centrosymmetric co-ordination compounds in cubic environments and also in doped host crystals belonging to the space group Fm 3m. (author)

Synthesis, Characterization and Comparative Luminescence Studies of Rare-Earth-Doped Gd2O3 Nanoparticles

Science.gov (United States)

Pyngrope, D.; Singh, L. R.; Prasad, A. I.; Bora, A.

2018-04-01

A facile direct precipitation method was used for the synthesis of luminescence nanomaterial. Gd2O3 doped with rare earth element Eu3+ is synthesized by polyol route. The synthesized nanoparticles show their characteristic red emission. The nanoparticles are characterized by x-ray diffractometer (XRD), Fourier transform infrared spectroscopy (FTIR), transmission electron microscopy (TEM) and photoluminescence (PL) study. The synthesized nanoparticles are spherical particles with 30 nm size. The photoluminescence studies show the characteristic Eu3+ red emission. The PL study shows the intensity of the magnetic dipole transition ( 5 D0 \\to 7 F1 ) at 592 nm compared to that of the electronic dipole transition ( 5 D0 \\to 7 F2 ) at 615 nm. The nanomaterials can show significant application in various display devices and biomedical applications for tracking.

Dispersive heterodyne probing method for laser frequency stabilization based on spectral hole burning in rare-earth doped crystals

DEFF Research Database (Denmark)

Gobron, Olivier; Jung, K.; Galland, N.

2017-01-01

Frequency-locking a laser to a spectral hole in rare-earth doped crystals at cryogenic temperature has been shown to be a promising alternative to the use of high finesse Fabry-Perot cavities when seeking a very high short term stability laser (M. J. Thorpe et al., Nature Photonics 5, 688 (2011......)). We demonstrate here a novel technique for achieving such stabilization, based on generating a heterodyne beat-note between a master laser and a slave laser whose dephasing caused by propagation near a spectral hole generate the error signal of the frequency lock. The master laser is far detuned from...

Photostability of solutions of rare earth chelates in organic solvents and polymers

International Nuclear Information System (INIS)

Karasev, V.E.; Mirochnik, A.G.; Lysun, T.V.; Vovna, V.I.

1990-01-01

Consideration is given to results of comparative study of photochemical properties of rare erath chelate complexes (adducts of rare earth β-diketonates with triphenylphosphine oxide, hexamethylphosphotriamide, phenanthroline) in organic solvents and polymers. Effect of excitation conditions, composition, solvent, nature of ligand and rare earth ion on photolysis rate was investigated. 9 refs.; 2 figs.; 4 tabs

Global recovery process of thorium and rare earths in a nitrate medium

International Nuclear Information System (INIS)

Cailly, F.; Mottot, Y.

1993-01-01

The aqueous solution of thorium and rare earth nitrates, obtained by leaching the ore with nitric acid, is extracted by an organic phosphorous compound (phosphate, phosphonate, phosphinate or phosphine oxide) and a cationic extractant chosen among phosphoric acid di-esters. Extraction of thorium and rare earths is possible even in presence of phosphate ions in the aqueous solution. Thorium and rare earths are separated by liquid-liquid extraction of the organic phase

Measurements of defect structures by positron annihilation lifetime spectroscopy of the tellurite glass TeO2-P2O5-ZnO-LiNbO3 doped with ions of rare earth elements: Er3+, Nd3+ and Gd3+

Science.gov (United States)

Golis, E.; Yousef, El. S.; Reben, M.; Kotynia, K.; Filipecki, J.

2015-12-01

The objective of the study was the structural analysis of the TeO2-P2O5-ZnO-LiNbO3 tellurite glasses doped with ions of the rare-earth elements: Er3+, Nd3+ and Gd3+ based on the PALS (Positron Annihilation Lifetime Spectroscopy) method of measuring positron lifetimes. Values of positron lifetimes and the corresponding intensities may be connected with the sizes and number of structural defects, such as vacancies, mono-vacancies, dislocations or pores, the sizes of which range from a few angstroms to a few dozen nanometres. Experimental positron lifetime spectrum revealed existence of two positron lifetime components τ1 and τ2. Their interpretation was based on two-state positron trapping model where the physical parameters are the annihilation velocity and positron trapping rate.

Science and technology of the rare earth elements

International Nuclear Information System (INIS)

Azzouz, Abdelkrim; Chegrouche, Salah; Telmoune, Sid-Ali; Layachi, Lazhar

1992-07-01

The present work studies the chemical physics properties, the different methods of analysis (neutron activation, emission spectrometry, chromatography), and the techniques of separation of rare earth (electrodeposition, thermic decomposition, salts distillation and ions exchange)

Contribution for the studies of rare earth dithionates

International Nuclear Information System (INIS)

Schmitz, L.C.

1988-01-01

The main objective of this work is the synthesis and investigation of some properties of rare earth dithionates. The rare earth dithionates were prepared from the respective sulphates, by the reaction of the latter with BaS sub(2) O sub(6) in aqueous solutions. The lanthanide ion content was estimated by complexometric titration with EDTA; analysis for H were carried out by microanalysis and the water content was determinated by Karl Fischer titration. This experimental results in addition to thermogravimetric (TG) data gave the stoichiometry of the compounds. (author)

Growth of doped and pure monocrystalline fibers and gradient crystals of REMO_4 compounds (RE = rare earths and M = Nb and Ta)

International Nuclear Information System (INIS)

Octaviano, E.S.; Levada, C.L.; Missiato, O.; Semenzato, M.J.; Silva, R.A.; Andreeta, J.P.

2009-01-01

A desirable alternative for a faster development, characterization and application of material of technological interest has been the growth of single crystal fibers by LHPG - Laser Heated Pedestal Growth. In this work it was reported the growth of pure, doped and gradient single crystal fibers of the chemical formulation REMO_4 (M = Nb e Ta, e RE= Rare Earth), characterized through primary techniques such as X-Ray and optical spectroscopy. (author)

Progress Towards Left-Handed Electromagnetic Waves in Rare-Earth Doped Crystals

Science.gov (United States)

Brewer, Nicholas Riley

In 1968 Victor Veselago determined that a material with both a negative permittivity and negative permeability would have some extraordinary properties. The index of refraction of this material would be negative and light propagating inside would be 'left-handed'. This research went relatively unnoticed until the year 2000 when John Pendry discovered that a lens with an index of refraction of n = -1 could, in principle, have infinite resolution. Since 2000, research into negative index materials has exploded. The challenging part of this research is to get a material to respond to magnetic fields at optical frequencies. Artificially created metamaterials are able to achieve this and have been the focus of most negative index research. The long term goal of our project is to produce left-handed light in an atomic system. In order to do this, an atomic transition needs to be utilized that is magnetic dipole in character. Pure magnetic dipole transitions in the optical regime are more rare and fundamentally much weaker than the electric dipole transitions typically used in atomic physics experiments. They can be found, however, in the complex atomic structure of rare-earth elements. The 7F0 → 5D 1 transition in europium doped yttrium orthosilicate (Eu3+:Y 2SiO5) has a wavelength of 527.5 nm and is a pure magnetic dipole transition. We measured its dipole moment to be (0.063 +/- 0.005)mu B via Rabi oscillations, inferring a magnetization on the order of 10 -2 A/m. Demonstrating this large magnetic response at an optical frequency is a major first step in realizing left-handed light in atomic systems.

Optical spectroscopy of Eu3+ doped Th(MoO4)2

International Nuclear Information System (INIS)

Keskar, Meera; Phatak, Rohan; Gupta, Santhosh; Natarajan, V.

2014-01-01

Eu 3+ is often used as a structural probe, because of the relative simplicity of its energy-level structure and dependence on its site symmetry in the host material. The phonon energy of the host for rare-earth ions is a crucial factor to be considered for developing luminescent materials.Thorium molybdate can satisfy both low phonon energy environment for rare-earth ions and good chemical and mechanical stabilities for practical use. Thus Eu 3+ doped Th(MoO 4 ) 2 are expected to be a good promising optical materials. To the best of our knowledge, there is no report on optical spectroscopy of Eu 3+ doped thorium molybdate and thus work has been carried out and discussed in this paper

Experimental evidence of the impact of rare-earth elements on particle growth and mechanical behaviour of silicon nitride

International Nuclear Information System (INIS)

Satet, Raphaelle L.; Hoffmann, Michael J.; Cannon, Rowland M.

2006-01-01

The impact of various rare-earth and related doping elements (R = Lu, Sc, Yb, Y, Sm, La) on the grain growth anisotropy and the mechanical properties of polycrystalline β-silicon nitride ceramics has been studied. Model experiments, in which Si 3 N 4 particles can grow freely in an R-Si-Mg-oxynitride glass matrix, show that, with increasing ionic radius of the additive, grain anisotropy increases due to non-linear growth kinetics. Toughness and strength are affected by the rare-earth element. Samples of equivalent grain sizes and morphologies yield an increasing toughness with increasing ion size of the R 3+ , reflecting an increasingly intergranular crack path. These samples are also strong and flaw tolerant, but the trends of strength and toughness do not exactly match. The choice of the rare-earth is essential to tailor microstructure, interfacial strength and mechanical properties. However, somewhat different trends for properties from IIIb and lanthanide additives indicate that more than the R 3+ size (i.e., purely ionic bond strength between R 3+ and its neighbours) is important. The electronic structure of the R-element is responsible for the type of dopant adsorption and the properties of the interface

Thermochemistry of rare earth doped uranium oxides Ln{sub x}U{sub 1−x}O{sub 2−0.5x+y} (Ln = La, Y, Nd)

Energy Technology Data Exchange (ETDEWEB)

Zhang, Lei; Navrotsky, Alexandra, E-mail: anavrotsky@ucdavis.edu

2015-10-15

Lanthanum, yttrium, and neodymium doped uranium dioxide samples in the fluorite structure have been synthesized, characterized in terms of metal ratio and oxygen content, and their enthalpies of formation measured by high temperature oxide melt solution calorimetry. For oxides doped with 10–50 mol % rare earth (Ln) cations, the formation enthalpies from constituent oxides (LnO{sub 1.5}, UO{sub 2} and UO{sub 3} in a reaction not involving oxidation or reduction) become increasingly exothermic with increasing rare earth content, while showing no significant dependence on the varying uranium oxidation state. The oxidation enthalpy of Ln{sub x}U{sub 1−x}O{sub 2−0.5x+y} is similar to that of UO{sub 2} to UO{sub 3} for all three rare earth doped systems. Though this may suggest that the oxidized uranium in these systems is energetically similar to that in the hexavalent state, thermochemical data alone can not constrain whether the uranium is present as U{sup 5+}, U{sup 6+}, or a mixture of oxidation states. The formation enthalpies from elements calculated from the calorimetric data are generally consistent with those from free energy measurements. - Highlights: • We synthesize, characterize Ln{sub x}U{sub 1−x}O{sub 2−0.5x+y} solid solutions (Ln = La, Y, Nd). • Formation enthalpies become more exothermic with increasing rare earth content. • Oxidation enthalpy of Ln{sub x}U{sub 1−x}O{sub 2−0.5x+y} is similar to that of UO{sub 2} to UO{sub 3}. • Direct calorimetric measurements are in good agreement with free energy data.

Ion transport under the effect of an electric field in porous medium: application to the separation of rare earths by focalization electrophoresis; Transport d'ions sous l'effet d'un champ electrique en milieu poreux: Application a la separation de terres rares par electrophorese a focalisation

Energy Technology Data Exchange (ETDEWEB)

Vieira-Nunes, A.I

1999-01-15

Trivalent ions of rare earth elements have very similar properties and their difficult separation each from another is usually carried out by liquid-liquid extraction or ion exchange. Focalization electrophoresis represents an alternative route to the usual techniques. The purpose of this work consisted of the fundamental investigation of ion transport phenomena in electrophoretic processes. Focalization electrophoresis is suitable for separation of amphoteric species such as rare earth ions, using a pH gradient in the cell and upon addition of a complexed agent e. g. EDTA. This technique relies upon the difference in iso-electrical points of the considered species, being under the form of free cation near the anode, and in the form of anionic complexed species closer to the cathode. Rare earth species are submitted to the antagonist effects of diffusion and migration, enabling their focalization to occur at the iso-electrical point, corresponding to nil value of their effective mobility. Following a literature survey on rare earth elements and electrophoresis processes, the document describes theoretical and experimental investigations of complexation equilibria of some rare earth elements, namely lanthanum, neodymium, praseodymium and cerium, depending on pH. Values for the iso-electrical points could be estimated. Transport and focalization phenomena in view of rare earth separation, are dealt in the last chapter. Investigations were first carried out without forced circulation of the electrolyte solution and the transient behavior of the system allowed operating conditions to be design and built-up of a continuous device, more suitable to separation, and provided with 42 potential and 42 temperature sensors: the results of the preliminary runs, in form of variable profiles, are presented and discussed. (author)

Mass separation of rare-earth elements by a high-temperature thermal ion source coupled with a He-jet system

International Nuclear Information System (INIS)

Kawase, Y.; Okano, K.; Aoki, K.

1987-01-01

By using a high-temperature thermal ion source coupled to a He-jet system, neutron-rich isotopes of rare-earth elements such as cerium, praseodymium, neodymium and promethium produced by the thermal-neutron fission of /sup 235/U were ionized and successfully separated. The temperature dependence of the ionization efficiency has been measured and found to be explained qualitatively by the vapour pressure of the relevant elements. The characteristic temperature dependence of the ionization efficiency has been utilized for Z-identification of several isobars of rare-earth elements. The heaviest isotopes of neodymium and promethium, /sup 155/Nd and /sup 156/Pm, have recently been identified

Rare earth octacyanomolybdates(4)

International Nuclear Information System (INIS)

Zubritskaya, D.I.; Sergeeva, A.N.; Pisak, Yu.V.

1980-01-01

Optimal conditions for synthesis of rare-earth octacyanomolybdates(4) of the Ln 4 [Mo(CN) 8 ] 3 xnH 2 O composition (where Ln is a rare-earth element, other than Pr, Pm, Lu, Tb) have been worked out. The synthesis has been accomplished by neutralization with octacianomolybdic acid with rare-earth carbonates. The composition and structure of the compounds synthesized have been studied by infrared-spectroscopy. It has been established that rare-earth octacyanomolybdates(4) form three isostructural groups

Rare earths and rare earth alloys electrolytic preparation process and device for this process

International Nuclear Information System (INIS)

Seon, F.; Barthole, G.

1986-01-01

Electrolysis of a molten salt of rare earth or rare earth alloy for preparation of the metal or alloy is described. The molten salt bath comprises at least a rare earth chloride, at least an alkaline or alkaline earth chloride and at least an alkaline or alkaline earth fluoride [fr

X-ray dichroism of rare earth materials

International Nuclear Information System (INIS)

Goedkoop, J.B.

1989-01-01

The theme of this thesis is the investigation of the strong polarization dependende, or dichroism, that occur in the X-ray absorption spectra of rare earth materials. The rare earth elements distinguish themselves from the other elements through the behaviour of the 4f electrons which form the valence shell. This shell lies deep inside the atom, with the result that influences from the surrounding solid are well screened off by the outer electrons, so that even in the solid the 4f shell behaves very much like a in free atom or ion, and is almost completely spherically symmetric. Perturbations from the solid environment however always disturb this symmetry to some extend, with the result that the absorption spectrum becomes dependent on the mutual orientation of the polarization vector of the radiation and the ion. Earlier the existence of a strong magnetic X-ray dichroism (MXD) in the 3d→4f transitions of rare earths. In this thesis this work is extended, to a small degree theoretically but mainly experimentally. MXD is used in experiments on bulk sample, terbium iron garnet, and on rare earth overlayers on a ferromagnetic surface, Ni(110). The results of the latter study show unequivocally the potential of the MXD technique. The second theme of the thesis concerns experimental developments in soft X-ray spectroscopy. A description is given of a double crystal monochromator beamline that was constructed by our group at LURE, France. Results of the use of an organic crystal - multilayer comination in such a monochromator is described. Also a method is described for the characterization of the resolution of soft X-ray monochromators. Finally a contribution to the characterization of the electron yield technique in the soft X-ray range is given. (author). 296 refs.; 64 figs.; 59 schemes; 9 tabs

Rare earths as a future resource

International Nuclear Information System (INIS)

Cornell, D.H.

1988-01-01

The fourteen rare earth or lanthanide elements have recently emerged as an important natural resource because of the rapidly growing demand in the electronic, chemical and metallurgical industries. The Symposium on rare earth elements as a future resource presented a multidisciplinary review of rare earth chemistry, geology, beneficiation, industrial applications and marketing. Papers by experts in many fields were presented on the following topics: chemical properties of the rare earth elements; the analysis of rare earth elements and minerals; beneficiation and extraction of rare earth elements; economic geochemistry and mineralogy of rare earths; present industrial uses of rare earth elements; the role of rare earth elements in high-temperature superconductors; the technical application of high-temperature superconductors; supply and demand for rare earth products - now and in the future, and the geology of rare earth deposits

Quantum efficiency of silica-coated rare-earth doped yttrium silicate

Energy Technology Data Exchange (ETDEWEB)

Cervantes-Vásquez, D., E-mail: dcervant@cnyn.unam.mx [Centro de Investigación Científica y de Educación Superior de Ensenada, Carretera Ensenada-Tijuana No. 3918, Zona Playitas, C.P. 22860 Ensenada, B.C., México (Mexico); Contreras, O.E.; Hirata, G.A. [Centro de Nanociencias y Nanotecnología, Universidad Nacional Autónoma de México, Km. 107 Carretera Tijuana-Ensenada, C.P. 22800 Ensenada, B.C., México (Mexico)

2013-11-15

The photoluminescent properties of rare earth-activated white-emitting Y{sub 2}SiO{sub 5}:Ce,Tb nanocrystalline phosphor prepared by two different methods, pressure-assisted combustion synthesis and sol–gel, were studied. The synthesized phosphor samples were post-annealed at 1373 K and 1623 K in order to obtain the X1-Y{sub 2}SiO{sub 5} and X2-Y{sub 2}SiO{sub 5} phases, respectively, which were confirmed by X-ray diffraction measurements. Photoluminescence analysis showed the contribution of two blue-emission bands within the 380–450 nm region originating from 5d–4f transitions in Ce{sup 3+} ions and a well-defined green emission of Tb{sup 3+} ions located at 545 nm corresponding to {sup 5}D{sub 4}→{sup 7}F{sub 5} electronic transitions. Thereafter, Y{sub 2}SiO{sub 5}:Ce,Tb powders were coated with colloidal silica in order to investigate the effect of silica coatings on their luminescent properties. Absolute fluorescence quantum efficiency measurements were carefully performed, which revealed an increase of 12% of efficiency in coated compared with bare-Y{sub 2}SiO{sub 5}:Ce,Tb phosphor. -- Highlights: • Y{sub 2}SiO{sub 5}:Ce,Tb phosphor powders were successfully coated with colloidal silica. • Post-annealing treatments improved the quantum efficiency of silica-coated Y{sub 2}SiO{sub 5}:Ce,Tb phosphors. • Absolute fluorescence quantum efficiency measurements showed an increase of 12%.

Synthesis and investigation of some physicochemical properties of rare earth nitrobarbiturates

International Nuclear Information System (INIS)

Biryulina, V.N.; Chupakhina, R.A.; Serebrennikov, V.V.

1984-01-01

Crystal depositions of L 3 MnH 2 O composition where L is anion of nitrobarbituric acid C 4 H 2 N 3 O 5 - ; M is rare earth ion excluding Ce 3+ and Pm 3+ ; n=12 are extracted under dissolution of freshly prepared hydroxides of rare earth elements (REE) in ethanol aqueous solution of nitrobarbituric acid. The method of IR spectroscopy has been applied to disclose relation of rare earth ion with groups of C=0 acid. The method of derivatography has been used to study thermolysis of REE nitrobarbiturates; dehydration proceeds in two stages with decrease of temperature of the beginning of dehydration by 20 deg C in the La 3+ → Lu 3+ series. The curve of dependence of REE nitrobarbiturate solubility in water at 25 deg C on serial number of REE passes through the minimum accounted for Sm 3+

Characterization of rare-earth doped Si 3 N4 /SiC micro/nanocomposites

Directory of Open Access Journals (Sweden)

Peter Tatarko

2010-03-01

Full Text Available Influence of various rare-earth oxide additives (La2O3, Nd2O3, Sm2O3, Y2O3, Yb2O3 and Lu2O3 on the mechanical properties of hot-pressed silicon nitride and silicon nitride/silicon carbide micro/nano-composites has been investigated. The bimodal character of microstructures was observed in all studied materials where elongated β-Si3N4 grains were embedded in the matrix of much finer Si3N4 grains. The fracture toughness values increased with decreasing ionic radius of rare-earth elements. The fracture toughness of composites was always lower than that of monoliths due to their finer Si3N4/SiC microstructures. Similarly, the hardness and bending strength values increased with decreasing ionic radius of rare-earth elements either in monoliths or composites. On the other hand, the positive influence of finer microstructure of the composites on strength was not observed due to the present defects in the form of SiC clusters and non-reacted carbon zones. Wear resistance at room temperature also increased with decreasing ionic radius of rare-earth element. Significantly improved creep resistance was observed in case either of composite materials or materials with smaller radius of RE3+.

Rare earth effect on microstructure, mechanical and tribological properties of CoCrW coatings

International Nuclear Information System (INIS)

Zhang Zhenyu; Lu Xinchun; Han Baolei; Luo Jianbin

2007-01-01

Eight different CoCrW coatings doped with rare earth oxide were deposited by supersonic plasma spraying (SPS). Environmental scanning electron microscopy, microhardness tester, X-ray diffractometer, and self-developed tribometer for high temperature were employed to investigate the properties of sprayed coatings. The results show that rare earth can refine the microstructure effectively, and make the element distribution uniform, which leads to the increase of average microhardness and the corresponding decrease of fluctuation range of sectioned surface of SPS coatings. Furthermore, the rare earth can reduce the friction coefficient between the SPS coating and glass during the sliding process at about 973 K largely, and the mechanism of anti-friction is also discussed

Rare earths 1998 market update

International Nuclear Information System (INIS)

Tourre, J.M.

1998-01-01

The rare earth industry has always been a world of rapid change with the emergence of new markets, new ores and new players, as well as the disappearance of old applications. Rare earth based products are used in a great diversity of applications such as hard disk drives, CD drives, batteries, capacitors, pigments, ceramics, polishing powders, fuel cells, flints, catalyst converter, fluid cracking catalysts, etc. South East Asia holds the largest share of the known reserve of rare earth ores and is one of the major markets for rare earth compounds; in the last ten years, China has become the largest producer of rare earth intermediates as well as an important exporter of separated rare earth elements. Today, China has approximately 150 factories producing rare earth compounds, most of which are experiencing financial difficulties due to the lack of knowledge of true market needs, lack of control of their distribution channels and production over-capacity. Recently the Chinese rare earth producers have recognized the situation and efforts are underway to rationalize rare earth production. Japan has dominated many of the major application markets, and is by far the largest market for metal and alloy products. This will remain the case for the next five years; however, new countries are emerging as significant users of rare earth products such as Korea, Taiwan and Malaysia. During the last ten years rare earth producers adjusted to several radical changes that affected the raw materials, the application mix and the price structure. New producers have emerged, especially from China; some have subsequently stopped their activities while others have focused their efforts in a specific market segment

Rare earth germanates

International Nuclear Information System (INIS)

Bondar', I.A.; Vinogradova, N.V.; Dem'yanets, L.N.

1983-01-01

From the viewpoint of structural chemistry and general regularities controlling formation reactions of compounds and phases in melts, solid and gaseous states, recent achievements in the chemistry of rare earth germanates are generalized. Methods of synthesizing germanates, systems on the base of germanium oxides and rare earths are considered. The data on crystallochemical characteristics are tabulated. Individual compounds of scandium germanate are also characterized. Processes of germanate formation using the data of IR-spectroscopy, X-ray phase analysis are studied. The structure and morphotropic series of rare earth germanates and silicates are determined. Fields of their present and possible future application are considered

On optimal length of hydrocarbon chain of fatty-acid collectors of rare earth ions

International Nuclear Information System (INIS)

Skrylev, L.D.; Sazonova, V.F.; Markina, Eh.L.

1978-01-01

The mechanism of the effect of the length of alkyl chain in fatty-acid collectors on the efficiency of flotation separation of the ions of rare earth elements (REE) collected by them has been investigated. REE flotation separation was studied on gadolinium chloride. Aqueous solutions of potassium caprinata, indecanate, laurate, tridecanate, myristate, pentadecanate and palmitate were used as collectors of Gd ions. The interaction of Gd ions with these compounds proceeds rapidly and is accompanied by stable colloidal solutions of Gd soaps being formed. Infrared spectra and radiograms of the sublates have been studied. It has been found that, with the number of carbon atoms in the collector molecule increasing from 10 to 16, the rate of flotation separation of Gd ions from solutions with pH 6 and 8 at first practically does not change (for potassium caprinate, undecanate and laurate), then drops sharply (potassium tridecanate and myristate), after which is again increases sharply (potassium pentadecanata and palmitate). The separation rate of Gd ions does not rise in solutions with pH 10. The nature of the sublate is shown to be determined by the solubility of the corresponing fatty acids and gadolinium soaps

The Chinese Society of Rare Earth is Studying The Feasibility of Marketing Rare Earth Futures

Institute of Scientific and Technical Information of China (English)

2015-01-01

Lin Donglu,secretary-general of the Chinese Society of Rare Earth recently said,the Chinese Society of Rare Earth undertook the research on subject of the National Social Science Fund Foundation on the reform of Chinese rare earth trading pricing mechanism on promoting RMB globalization,and is focusing on studying the feasibility of marketing rare earth futures variety.

A primary exploration to quasi-two-dimensional rare-earth ferromagnetic particles: holmium-doped MoS2 sheet as room-temperature magnetic semiconductor

Science.gov (United States)

Chen, Xi; Lin, Zheng-Zhe

2018-05-01

Recently, two-dimensional materials and nanoparticles with robust ferromagnetism are even of great interest to explore basic physics in nanoscale spintronics. More importantly, room-temperature magnetic semiconducting materials with high Curie temperature is essential for developing next-generation spintronic and quantum computing devices. Here, we develop a theoretical model on the basis of density functional theory calculations and the Ruderman-Kittel-Kasuya-Yoshida theory to predict the thermal stability of two-dimensional magnetic materials. Compared with other rare-earth (dysprosium (Dy) and erbium (Er)) and 3 d (copper (Cu)) impurities, holmium-doped (Ho-doped) single-layer 1H-MoS2 is proposed as promising semiconductor with robust magnetism. The calculations at the level of hybrid HSE06 functional predict a Curie temperature much higher than room temperature. Ho-doped MoS2 sheet possesses fully spin-polarized valence and conduction bands, which is a prerequisite for flexible spintronic applications.

Uses of extraction and ion exchange chromatography in the thorium and rare earths separation from industrial residue generated in thorium purification unity at IPEN. Application of rare earths as catalysts for generation of hydrogen

International Nuclear Information System (INIS)

Zini, Josiane

2010-01-01

In the 70's a pilot plant for studies of different concentrates processing obtained from the chemical processing of monazite was operated at IPEN / CNEN-SP, with a view to obtaining thorium of nuclear purity. This unity was operated on an industrial scale since 1985, generating around 25 metric tons of residue and was closed in 2002. This waste containing thorium and rare earths was named Retoter (Rejeito de Torio e Terras Raras, in portuguese) and stored in the IPEN Safeguards shed. This paper studies the treatment of the waste, aimed at environmental, radiological and technology. Were studied two cases for the chromatographic separation of thorium from rare earths. One of them was the chromatographic extraction, where the extracting agent tributyl phosphate was supported on polymeric resins Amberlite XAD16. The other method is studied for comparison purposes, since the material used in chromatographic extraction is unprecedented with regard to the separation of thorium, was the ion-exchange chromatography using DOWEX 1-X8 strong cationic resin. Was studied also the chromatographic process of extraction with the extracting agent DEHPA supported on Amberlite XAD16 for the fractionation in groups of rare earths elements. Thorium was separated with high purity for strategic purposes and rare earths recovered free from thorium, were tested as a catalyst for ethanol reforming to hydrogen obtaining which is used in fuel cells for power generation. (author)

Effect of rare earth doping on optical and spectroscopic characteristics of BaZrO3:Eu3+,Tb3+ perovskites

Science.gov (United States)

Katyayan, Shambhavi; Agrawal, Sadhana

2018-06-01

This paper reports structural investigations of rare earth doped BaZrO3 phosphors synthesized by Solid state reaction technique with varying concentrations of Eu3+ and Tb3+ from 0 mol% to 2 mol%. The synthesized phosphors show enhanced variable emissions in the visible region corresponding to different hypersensitive electronic transitions of Eu3+ and Tb3+ ions. With cubic structure confirmed in XRD analysis, the FESEM images show uniform grain connectivity and homogeneity of prepared samples. The TEM micrographs of the synthesized phosphors show agglomerated irregular structures. The synthesized phosphors were also subjected to FTIR, Raman, EDXS analysis along with studies of thermoluminescent and photoluminescent characteristics. On subjecting to 229 nm (UV) excitation, the phosphors show enhanced PL emissions corresponding to 571 nm (5D0-7F0), 591 nm (5D0-7F1), 615 nm (5D0-7F2) and 678 nm (5D0-7F4) hypersensitive transitions of Eu3+ ions and emission peaks at 489 nm (5D4-7F6), 539 nm (5D4-7F5), 589 nm (5D4-7F4) and 632 nm (5D4-7F3) accounting for electronic transitions of Tb3+ ions respectively. The computed average PL lifetime is 14.014 s. In the TL analysis, the second order of kinetics with the activation energy varying from 5.0 × 10‑1 eV to 6.6 × 10‑1 eV is reported. The maximum TL lifetime is estimated as 19.4985 min in the TL lifetime analysis.

Magnetic form factors of rare earth ions

International Nuclear Information System (INIS)

Deckman, H.W.

1976-01-01

The magnetic scattering of neutrons by atoms has been investigated by exploiting its similarity to the radiation problem in spectroscopy. Expressions for the magnetic scattering amplitude were developed for cases in whcih an atom in the l/sup n/ electronic configuration is described either by a relativistic or nonrelativistic Hamiltonian. For each of these cases, it has been shown that the magnetic scattering amplitude can be expressed in terms of relativistic or nonrelativistic matrix elements of magnetic and electric multipole operators. For a nonrelativistic atom, the calculation of these matrix elements has been separated into evaluating radial matrix elements and matrix elements of Racah tensors W/(sup 0,k)k/ and W/(sup 1,k')k/. For a relativistic atom the effective operator approach has been used to define effective multipole operators so that a relativistic result is obtained by taking matrix elements of these effective operators between nonrelativistic states of the atom. The calculation of matrix elements of these effective operators has been reduced to evaluating relativistic radial integrals and matrix elements of the Racah tensors taken between nonrelativistic states of the atom. It is shown tha for the case of elastic scattering by either a relativistic or nonrelativistic atom in single Russel-Saunders state, the magnetic scattering amplitude can be written in the conventional form p(vector q)vector q/sub m/.vector sigma. General expressions for p(vector q) as well as elastic magnetic form factorshave been obtained. The formalism has been illustrated throughout by applying it to the case of scattering by rare earth ions

Fabrication of Superhydrophobic and Luminescent Rare Earth/Polymer complex Films.

Science.gov (United States)

Wang, Zefeng; Ye, Weiwei; Luo, Xinran; Wang, Zhonggang

2016-04-18

The motivation of this work is to create luminescent rare earth/polymer films with outstanding water-resistance and superhydrophobicity. Specifically, the emulsion polymerization of styrene leads to core particles. Then core-shell-structured polymer nanoparticles are synthesized by copolymerization of styrene and acrylic acid on the core surface. The coordination reaction between carboxylic groups and rare earth ions (Eu(3+) and Tb(3+)) generates uniform spherical rare earth/polymer nanoparticles, which are subsequently complexed with PTFE microparticles to obtain micro-/nano-scaled PTFE/rare earth films with hierarchical rough morphology. The films exhibit large water contact angle up to 161° and sliding angle of about 6°, and can emit strong red and green fluorescence under UV excitation. More surprisingly, it is found that the films maintain high fluorescence intensity after submersed in water and even in aqueous salt solution for two days because of the excellent water repellent ability of surfaces.

Unusual magnetic properties of rare-earth titanium oxides RTiO3: effect of the rare earth on the magnetic moment of titanium in Lasub(x)Ysub(1-x)Ti03 and GdTi03

International Nuclear Information System (INIS)

Greedan, J.E.; MacLean, D.A.

1978-01-01

The rare-earth orthotitanites, RTi0 3 are a relatively new series of materials with properties which are strongly dependent on the identity of the rare-earth ion. Low-temperature magnetization studies on the system Lasub(x)Ysub(1-x)Ti0 3 and the compound GdTi0 3 indicate that the magnitude of the Ti 3+ spontaneous moment depends on the average size of the rare-earth ion and on its magnetic moment. For most of the phases studied except GdTi0 3 the Ti 3+ moment is very much smaller than the 'spin only' value and is non-integral, yet semiconducting behaviour is simultaneously observed. (author)

The degrees of tri-axial orientation in RE-doped Bi2212 powders aligned in a modulated rotation magnetic field

International Nuclear Information System (INIS)

Nagai, R.; Horii, S.; Maeda, T.; Haruta, M.; Shimoyama, J.

2013-01-01

Highlights: •Tri-axial magnetic alignment of Bi2212 with rare-earth (RE) doping was attempted. •Magnetization axes depended on the type of doped RE ions. •RE-doping increased degrees of inplane orientation and inplane magnetic anisotropy. -- Abstract: We report relationship between the degrees of tri-axial orientation and doping level of rare earth (RE) ions in Bi 2 Sr 2 (Ca 1−x RE x )Cu 2 O y (RE-doped Bi2212; RE = Dy, Ho, Er and Tm) powder samples aligned under a modulated rotation magnetic field (MRF) of 10 T. Tri-axial magnetic alignment of the RE-doped Bi2212 with x = 0–0.5 was achieved by single-ion magnetic anisotropy of RE 3+ and tri-axial magnetic anisotropy induced by modulation microstructure in a grain level. The degrees of in-plane and c-axis orientation with ∼3° were achieved for the case of the Tm-doped Bi2212 with x = 0.5. The findings in the present study give us important information for the fabrication of triaxially oriented Bi-based cuprate superconductor materials by the magneto-scientific process

Photoluminescent study of Polycarbonate (PC) and Poly(9-vinylcarbazole) (PVK) doped films with europium complex

International Nuclear Information System (INIS)

Forster, Pedro Lima

2010-01-01

Polymers doped with rare earth complexes are advantaged in film production for many applications in the luminescent field. In this study luminescent polymer obtained from polycarbonate (PC) and poly(9-vinylcarbazole) films doped with diaquatris(thenoyltrifluoroacetonate)europium(III) complex [Eu(tta) 3 (H 2 0) 2 ] were prepared and their calorimetric and luminescent properties in the solid state are reported. The thermal behavior was investigated by differential scanning calorimetry (OSC) and thermogravimetry analysis (TGA). Due of the addition of rare earth Eu(tta) 3 (H 2 0) 2 ] into PC and PVK matrices, changes were observed in the thermal behavior concerning the glass transition and thermal stability. Characteristic broadened narrow bands arising from the 5 D 0 -→ 7 F J transitions (J = 0-4) of Eu 3+ ion indicate the incorporation of the Eu 3+ ions into those polymers. The luminescent films show enhancement emission intensity with an increase in the rare earth concentration in polymeric matrix accompanied by decrease in thermal stability. (author)

Rare earths and actinides

International Nuclear Information System (INIS)

Coqblin, B.

1982-01-01

This paper reviews the different properties of rare-earths and actinides, either as pure metals or as in alloys or compounds. Three different cases are considered: (i) First, in the case of 'normal' rare-earths which are characterized by a valence of 3, we discuss essentially the magnetic ordering, the coexistence between superconductivity and magnetism and the properties of amorphous rare-earth systems. (ii) Second, in the case of 'anomalous' rare-earths, we distinguish between either 'intermediate-valence' systems or 'Kondo' systems. Special emphasis is given to the problems of the 'Kondo lattice' (for compounds such as CeAl 2 ,CeAl 3 or CeB 6 ) or the 'Anderson lattice' (for compounds such as TmSe). The problem of neutron diffraction in these systems is also discussed. (iii) Third, in the case of actinides, we can separate between the d-f hybridized and almost magnetic metals at the beginning of the series and the rare-earth like the metals after americium. (orig.)

Safety aspects in rare earths recovery

International Nuclear Information System (INIS)

Bhattacharya, R.

2014-01-01

Recovery of rare earths involves mining of beach sands, mineral separation to obtain monazite and its chemical processing to obtain rare earth composites. The composites are then subjected to further chemical treatment to obtain individual rare earths. Although the separated out rare earths are not radioactive, the process for recovery of rare earths involve both radiological as well as conventional hazards. This paper highlights the safety aspects in the mining, mineral separation and chemical processing of monazite to obtain rare earths

Coprecipitation of rare earths in systems of three heterovalent ions with sulfates of alkali and alkaline-earth metals

International Nuclear Information System (INIS)

Bobrik, V.M.

1977-01-01

Co-precipitation of rare earth elements (REE) in milligram amounts (3x10 -3 -3x10 -1 M) with alkali earth (AEE) sulfates in presence of alkali metal ions has been studied, the AEE:REE ratios between the co-precipitator and a REE (up to 50:1) the latter can be co-precipitated quantitatively in presence of corresponding alkali metals linked with the AEE in the Periodic table by a diagonal, i.e. in presence of sodium in co-precipitation with calcium sulfate, potassium with strontium sulfate and rubidium with barium sulfate. Co-precipitation with sulfates of sodium and calcium occurs at temperatures above 85 deg C and presumably involves calcium semihydrate. In presence of an alkali metal REE co-precipitation with AEE becomes isomorphic, i.e. at different AEE:REE ratios the co-precipitation coefficient remains constant. In presence of corresponding alkali metals the decrease in effectiveness of co-precipitation with AEE in the La-Lu series is more pronounced

A study of the structural properties of GaN implanted by various rare-earth ions

Czech Academy of Sciences Publication Activity Database

Macková, Anna; Malinský, Petr; Sofer, Z.; Šimek, P.; Sedmidubský, D.; Mikulics, M.; Wilhelm, R. A.

2013-01-01

Roč. 307, č. 7 (2013), s. 446-451 ISSN 0168-583X. [18th International Conference on Ion Beam Modifications of Materials (IBMM). Qingdao, 02.09.2012-07.09.2012] R&D Projects: GA ČR GA106/09/0125; GA MŠk(XE) LM2011019 Institutional support: RVO:61389005 Keywords : rare earth implantation * GaN * depth profiles * RBS * Raman spectroscopy * AFM Subject RIV: BG - Nuclear, Atomic and Molecular Physics, Colliders Impact factor: 1.186, year: 2013 http://www.sciencedirect.com/science/article/pii/S0168583X13000955

Enhanced magneto-optical Kerr effect in rare earth substituted nanostructured cobalt ferrite thin film prepared by sol–gel method

Energy Technology Data Exchange (ETDEWEB)

Avazpour, L.; Toroghinejad, M.R. [Department of Materials Engineering, Isfahan University of Technology, Isfahan 84156-83111 (Iran, Islamic Republic of); Shokrollahi, H., E-mail: Shokrollahi@sutech.ac.ir [Electroceramics Group, Department of Materials Science and Engineering, Shiraz University of Technology, Shiraz 13876-71557 (Iran, Islamic Republic of)

2016-11-30

Highlights: • The nanostructured rare earth doped Co-ferrite thin film was synthesized by the sol–gel method. • The coercivity of as high as 1.8 kOe is achieved for 20% substituted cobalt ferrite. • The average particle diameter of particulate film is decreasing by increasing substitute content. • Kerr spectra of films shifted to higher energies. • Kerr rotation angle increased to 1.65° for 0.1 Eu doped thin film. - Abstract: A series of rare-earth (RE)-doped nanocrystalline Co{sub x} RE{sub (1−x)} Fe{sub 2}O{sub 4} (x = 0, 0.1, 0.2 and RE: Nd, Eu) thin films were prepared on silicon substrates by a sol–gel process, and the influences of different RE{sup 3+} ions on the microstructure, magnetism and polar magneto-optical Kerr effect of the deposited films were investigated. Also this research presents the optimization process of cobalt ferrite thin films deposited via spin coating, by studying their structural and morphological properties at different thicknesses (200, 350 nm) and various heat treatment temperatures 300–850 °C. Nanoparticulate polycrystalline thin film were formed with heat treatment above 400 °C but proper magnetic properties due to well crystallization of the film were achieved at about 650 °C. AFM results indicated that the deposited thin films were crack-free exhibiting a dense nanogranular structure. The root-mean square (RMS) roughness of the thin films was in the range of 0.2–3.2 nm. The results revealed that both of the magnetism and magneto optical Kerr (MOKE) spectra of Co{sub x} RE{sub (1−x)} Fe{sub 2}O{sub 4} films could be mediated by doping with various RE ions. The Curie temperature of substituted samples was lower than pristine cobalt ferrite thin films. In MOKE spectra both dominant peaks were blue shifted with addition of RE ions. For low concentration dopant the inter-valence charge transfer related rotation was enhanced and for higher concentration dopant the crystal field rotation peak was enhanced

The electronic structure of rare-earth luminescent centre in alkaline-earth sulphides

International Nuclear Information System (INIS)

Zheng Qingqi; Pan Wei; Huang Maichun; He Xiaoguang

1988-09-01

The cluster method is used to investigate the electronic structure of rare-earth Eu 2+ and Ce 3+ doped SrS and CaS alkaline-earth sulphides in the local density theory regime. The ground state is obtained self-consistently by the DV-X α method, while the transition state theory is used to calculate the excited states. The energy difference between ground state and excited state is 2.95 eV (420 nm) for CaS:Eu is in good agreement with the experimental data of 430 nm for the absorption peak in SrS:Cu. The composition of ground state and excited state is also calculated which can give information about the EL excitation mechanism. (author). 7 refs, 4 figs, 3 tabs

A divalent rare earth oxide semiconductor: Yttrium monoxide

Science.gov (United States)

Kaminaga, Kenichi; Sei, Ryosuke; Hayashi, Kouichi; Happo, Naohisa; Tajiri, Hiroo; Oka, Daichi; Fukumura, Tomoteru; Hasegawa, Tetsuya

Rare earth sesquioxides like Y2O3 are known as widegap insulators with the highly stable closed shell trivalent rare earth ions. On the other hand, rare earth monoxides such as YO have been recognized as gaseous phase, and only EuO and YbO were thermodynamically stable solid-phase rock salt monoxides. In this study, solid-phase rock salt yttrium monoxide, YO, was synthesized in a form of epitaxial thin film by pulsed laser deposition method. YO possesses unusual valence of Y2+ ([Kr] 4d1) . In contrast with Y2O3, YO was narrow gap semiconductor with dark-brown color. The electrical conductivity was tunable from 10-1 to 103 Ω-1 cm-1 by introducing oxygen vacancies as electron donor. Weak antilocalization behavior was observed indicating significant spin-orbit coupling owing to 4 d electron carrier. The absorption spectral shape implies the Mott-Hubbard insulator character of YO. Rare earth monoixdes will be new platform of functional oxides. This work was supported by JST-CREST, the Japan Society for the Promotion of Science (JSPS) with Grant-in-Aid for Scientific Research on Innovative Areas (Nos. 26105002 and 26105006), and Nanotechnology Platform (Project No.12024046) of MEXT, Japan.

Multilayer membranes of p-sulfonato-calix[8]arene and polyvinylamine and their use for selective enrichment of rare earth metal ions

Energy Technology Data Exchange (ETDEWEB)

Toutianoush, Ali [Institut fuer Physikalische Chemie der Universitaet zu Koeln, Luxemburger Str. 116, D-50939 Cologne (Germany); El-Hashani, Ashraf [Institut fuer Physikalische Chemie der Universitaet zu Koeln, Luxemburger Str. 116, D-50939 Cologne (Germany); Schnepf, Judit [Institut fuer Physikalische Chemie der Universitaet zu Koeln, Luxemburger Str. 116, D-50939 Cologne (Germany); Tieke, Bernd [Institut fuer Physikalische Chemie der Universitaet zu Koeln, Luxemburger Str. 116, D-50939 Cologne (Germany)]. E-mail: Tieke@Uni-Koeln.de

2005-06-30

Using alternating electrostatic layer-by-layer assembly of p-octasulfonato-calix[8]arene and polyvinylamine, multilayer assemblies were built up on porous polymer supports. The resulting composite membranes with ultrathin separation layer were studied on their permeability for various metal chloride salts in aqueous solution. The membranes were permeable for sodium chloride, but much less permeable for divalent metal chlorides such as magnesium and zinc chloride, the theoretical separation factors {alpha} (NaCl/MgCl{sub 2}) and {alpha} (NaCl/ZnCl{sub 2}) being 43 and 20. Rare earth metal chlorides LnCl{sub 3} with Ln being La, Ce, Pr and Sm and the related YCl{sub 3} were strongly rejected from the membrane, the theoretical separation factors {alpha} (NaCl/LaCl{sub 3}) and {alpha} (NaCl/YCl{sub 3}) being 138 and 160, for example. Possible origins for the selective ion transport are discussed in terms of Donnan rejection of the highly charged ions and complex formation of the rare earth metal ions with the p-sulfonato-calixarene units in the membrane.

Multilayer membranes of p-sulfonato-calix[8]arene and polyvinylamine and their use for selective enrichment of rare earth metal ions

International Nuclear Information System (INIS)

Toutianoush, Ali; El-Hashani, Ashraf; Schnepf, Judit; Tieke, Bernd

2005-01-01

Using alternating electrostatic layer-by-layer assembly of p-octasulfonato-calix[8]arene and polyvinylamine, multilayer assemblies were built up on porous polymer supports. The resulting composite membranes with ultrathin separation layer were studied on their permeability for various metal chloride salts in aqueous solution. The membranes were permeable for sodium chloride, but much less permeable for divalent metal chlorides such as magnesium and zinc chloride, the theoretical separation factors α (NaCl/MgCl 2 ) and α (NaCl/ZnCl 2 ) being 43 and 20. Rare earth metal chlorides LnCl 3 with Ln being La, Ce, Pr and Sm and the related YCl 3 were strongly rejected from the membrane, the theoretical separation factors α (NaCl/LaCl 3 ) and α (NaCl/YCl 3 ) being 138 and 160, for example. Possible origins for the selective ion transport are discussed in terms of Donnan rejection of the highly charged ions and complex formation of the rare earth metal ions with the p-sulfonato-calixarene units in the membrane

Gamma rays shielding and sensing application of some rare earth doped lead-alumino-phosphate glasses

Science.gov (United States)

Kaur, Preet; Singh, Devinder; Singh, Tejbir

2018-03-01

Seven rare earth (Sm3+, Eu3+ and Nd3+) doped lead alumino phosphate glasses were prepared. The protective and sensing measures from gamma rays were analysed in terms of parameters viz. density (ρ), refractive index, energy band gap (Eg), mean free path (mfp), effective atomic number (Zeff) and buildup factors (energy absorption EABF as well as exposure buildup factor EBF). The energy dependent parameters (mfp, Zeff, EABF and EBF) were investigated in the energy region from 15 keV to 15 MeV. EABF and EBF values were observed to be maximum in the intermediate energy region. Besides, the EABF and EBF values for the prepared samples are shown to have strong dependence on chemical composition of the glass at lower energy, whereas, it is almost independent of chemical composition in higher energy region. The prepared glass samples are found to have potential applications in radiation shielding as well as radiation sensing, which further find numerous applications in the field of medicine and industry.

Luminescence investigation of R{sup 3+}-doped alkaline earth tungstates prepared by a soft chemistry method

Energy Technology Data Exchange (ETDEWEB)

Barbosa, Helliomar P. [Instituto de Química, Universidade de São Paulo, São Paulo, SP (Brazil); Kai, Jiang [Pontifícia Universidade Católica do Rio de Janeiro, Departamento de Química, Rio de Janeiro, RJ, Brazil (Brazil); Silva, Ivan G.N.; Rodrigues, Lucas C.V. [Instituto de Química, Universidade de São Paulo, São Paulo, SP (Brazil); Felinto, Maria C.F.C. [Centro de Química e Meio Ambiente, Instituto de Pesquisas Energéticas e Nucleares, São Paulo, SP (Brazil); Hölsä, Jorma [Instituto de Química, Universidade de São Paulo, São Paulo, SP (Brazil); Department of Chemistry, University of Turku,FI-20014 Turku (Finland); Turku University Centre for Materials and Surfaces (MatSurf), Turku (Finland); Malta, Oscar L. [Departamento de Química Fundamental, Universidade Federal de Pernambuco, Recife, PE (Brazil); Brito, Hermi F., E-mail: hefbrito@iq.usp.br [Instituto de Química, Universidade de São Paulo, São Paulo, SP (Brazil)

2016-02-15

Highly luminescent rare earth (R{sup 3+}) doped alkaline-earth tungstates MWO{sub 4}:R{sup 3+} (M{sup 2+}: Ca, Sr and Ba, R{sup 3+}: Eu, Tb, Gd) were prepared with a room temperature coprecipitation method. The phosphors were characterized by X-ray powder diffraction (XPD), thermal analysis (TG), infrared absorption spectroscopy (FTIR) and UV excited photoluminescence. The as-prepared MWO{sub 4}:R{sup 3+} particles belong to the tetragonal scheelite phase, and are well crystallized and are of the average size of 16–48 nm. The excitation and emission spectra of the materials were recorded at 300 and 77 K temperatures. The luminescent materials exhibit intense red (Eu{sup 3+}) and green (Tb{sup 3+}) colors under UV excitation. The excitation spectra of the Eu{sup 3+} doped materials show broad bands arising from the ligand-to-metal charge transfer transitions (O{sup 2−}→W{sup VI} and O{sup 2−}→Eu{sup 3+}) as well as narrow bands from 4f–4f intraconfigurational transitions of Eu{sup 3+}. 4f–4f emission data of the Eu{sup 3+} and Tb{sup 3+} in the MWO{sub 4} host matrices as well as the values of emission quantum efficiencies of the {sup 5}D{sub 0} level and the 4f–4f experimental intensity parameters of Eu{sup 3+} ion are presented and discussed. - Highlights: • Highly red Europium and green Terbium doped tungstate under UV excitation. • Efficient energy transfer process from tungstate to R{sup 3+} ion. • Promising candidates for a red (Eu{sup 3+}) and green (Tb{sup 3+}) emitting phosphors. • Ligand Metal charge transfer to R{sup 3+} ion. • Charge compensation with Na{sup +}.

The lattice dynamical studies of rare earth compounds: electron-phonon interactions

International Nuclear Information System (INIS)

Jha, Prafulla K.; Sanyal, Sankar P.; Singh, R.K.

2002-01-01

During the last two decades chalcogenides and pnictides of rare earth (RE) atoms have drawn considerable attention of the solid state physicists because of their peculiar electronic, magnetic, optical and phonon properties. Some of these compounds e.g. sulphides and selenides of cerium (Ce), samarium (Sm), yttrium (Y), ytterbium (Yb), europium (Eu) and thulium (Tm) and their alloys show nonintegral valence (between 2 and 3), arising due to f-d electron hybridization at ambient temperature and pressure. The rare earth mixed valence compounds (MVC) reviewed in this article crystallize in simple cubic structure. Most of these compounds show the existence of strong electron-phonon coupling at half way to the zone boundary. This fact manifests itself through softening of the longitudinal acoustic mode, negative value of elastic constant C 12 etc. The purpose of this contribution is to review some of the recent activities in the fields of lattice dynamics and allied properties of rare earth compounds. The present article is primarily devoted to review the effect of electron-phonon interactions on the dynamical properties of rare earth compounds by using the lattice dynamical model theories based on charged density deformations and long-range many body forces. While the long range charge transfer effect arises due to f-d hybridization of nearly degenerate 4f-5d bands of rare earth ions, the density deformation comes into the picture of breathing motion of electron shells. These effects of charge transfer and charge density deformation when considered in the lattice dynamical models namely the three body force rigid ion model (TRM) and breathing shell model (BSM) are quite successful in explaining the phonon anomalies in these compounds and undoubtedly unraveled many important physical process governing the phonon anomalies in rare earth compounds

Colored cool colorants based on rare earth metal ions

Energy Technology Data Exchange (ETDEWEB)

Sreeram, Kalarical Janardhanan; Aby, Cheruvathoor Poulose; Nair, Balachandran Unni; Ramasami, Thirumalachari [Chemical Laboratory, Central Leather Research Institute, Council of Scientific and Industrial Research, Adyar, Chennai 600 020 (India)

2008-11-15

Colored pigments with high near infrared reflectance and not based on toxic metal ions like cadmium, lead and cobalt are being sought as cool colorants. Through appropriate doping two pigments Ce-Pr-Mo and Ce-Pr-Fe have been developed to offer a reddish brown and reddish orange color, respectively. These pigments have been characterized and found to be highly crystalline with an average size of 300 nm. A shift in band gap energy from 2.21 to 2.18 eV has been observed when Li{sub 2}CO{sub 3} was used as a mineralizer. Scanning electron microscope-energy dispersive X-ray analysis (SEM-EDAX) measurement indicate a uniform grind shape and distribution of metal ion, with over 65% reflectance in the NIR region, these pigments can well serve as cool colorants. (author)

Determination of contaminants in rare earth materials by prompt gamma activation analysis (PGAA)

International Nuclear Information System (INIS)

Perry, D.L.; English, G.A.; Firestone, R.B.; Molnar, G.L.; Revay, Zs.

2005-01-01

Prompt gamma activation analysis (PGAA) has been used to detect and quantify impurities in the analyses of rare earth (RE) oxides. The analytical results are discussed with respect to the importance of having a thorough identification and contaminant elements in these compounds regarding the function of the materials in their various applications. Also, the importance of using PGAA to analyze materials in support of other physico-chemical studies of the materials is discussed, including the study of extremely low concentrations of ions - such as the rare earth ions themselves - in bulk material matrices. (author)

Synthesis and luminescent properties of trivalent rare-earth (Eu{sup 3+}, Tb{sup 3+}) ions doped nanocrystalline AgLa(PO{sub 3}){sub 4} polyphosphates

Energy Technology Data Exchange (ETDEWEB)

Krishna Bharat, L.; Jeon, Yong Il; Yu, Jae Su, E-mail: jsyu@khu.ac.kr

2014-11-25

Highlights: • AgLa(PO{sub 3}){sub 4}:Eu{sup 3+}, Tb{sup 3+} nanocrystalline phosphors were prepared by a sol–gel process. • The luminescent properties were studies by near-UV excitation. • The intense MD transition indicates the presence of high inversion symmetry site. • These results suggest that the compound is a good candidate for optical applications. - Abstract: The AgLa(PO{sub 3}){sub 4} phosphors activated with trivalent rare-earth (Eu{sup 3+}, Tb{sup 3+}) ions were prepared by a sol–gel synthesis method. The crystal structure of the compound was studied by X-ray diffraction patterns and found to be crystallized in the monoclinic system with a space group P2{sub 1}/c, indicating the calculated lattice parameters of a = 10.08 Å, b = 13.12 Å, and c = 7.314 Å. The Fourier-transform infrared spectrum, photoluminescence excitation/emission spectra, and decay curves were examined to study the optical properties. The analysis of the Eu{sup 3+} ions related emission spectrum revealed the presence of highly symmetric sites for the activator ions. The Tb{sup 3+} ions related emission spectrum exhibited a {sup 5}D{sub 3} emission due to the prolonged calcination at high temperatures, which reduces the residual hydroxyl ions. The optical properties show that this host material is suitable for phosphor materials and laser crystals.

Antiferromagnetic coupling between rare earth ions and semiquinones in a series of 1:1 complexes.

Science.gov (United States)

Caneschi, Andrea; Dei, Andrea; Gatteschi, Dante; Poussereau, Sandrine; Sorace, Lorenzo

2004-04-07

We use the strategy of diamagnetic substitution for obtaining information on the crystal field effects in paramagnetic rare earth ions using the homologous series of compounds with the diamagnetic tropolonato ligand, Ln(Trp)(HBPz(3))(2), and the paramagnetic semiquinone ligand, Ln(DTBSQ)(HBPz(3))(2), (DTBSQ = 3,5-di-tert-butylsemiquinonato, Trp = tropolonate, HBPz(3)= hydrotrispyrazolylborate) for Ln = Sm(iii), Eu(iii), Gd(iii), Tb(iii), Dy(iii), Ho(iii), Er(iii) or Yb(iii). The X-ray crystal structure of a new form of tropolonate derivative is presented, which shows, as expected, a marked similarity with the structure of the semiquinonate derivative. The Ln(Trp)(HBPz(3))(2) derivatives were then used as a reference for the qualitative determination of crystal field effects in the exchange coupled semiquinone derivatives. Through magnetisation and susceptibility measurements this empirical diamagnetic substitution method evidenced for Er(iii), Tb(iii), Dy(iii) and Yb(iii) derivatives a dominating antiferromagnetic coupling. The increased antiferromagnetic contribution compared to other radical-rare earth metal complexes formed by nitronyl nitroxide ligands may be related to the increased donor strength of the semiquinone ligand.

Studies of the rare earth-iron interactions in the orthoferrites GdFeO3 and HoFeO3

International Nuclear Information System (INIS)

Sakata, T.; Enomura, A.

1979-01-01

The magnetic behaviour of GdFeO 3 and HoFeO 3 is investigated by means of a Faraday type magnetic balance in a temperature range where rare earth ions are in the paramagnetic state. The results are analyzed in terms of an effective field at a rare earth ion site. Thereby the isotropic exchange field as well as the magnetic dipole field are taken into account. By this means the exchange integral, J/k(K), between an iron ion and a rare earth ion may be estimated to be 0.23 for GdFeO 3 and 0.25 for HoFeO 3 , respectively. (author)

Quantitative analysis or rare earths by X-ray fluorescence spectrometry

International Nuclear Information System (INIS)

Taam, Isabel; Mantovano, J.L.; Gante, Valdir; Jesus, Camila S.

2013-01-01

Rare earths ores and compounds are of growing importance to the worldwide industry. Its applications range from raw material to catalysts, manufacturing of electronics and even super magnets. Therefore, the demand for quick and accurate quantitative analysis methods is continuously growing. Current quantification methods of rare earths involve the separation of these elements by ion exchange and liquid-liquid extraction prior to the analysis itself, processes both time and reagent consuming. In the present work, we propose a method that directly quantifies by XRF technique the following rare earths: La, Pr, Nd, Sm and Gd in a concentrated liquor whose matrix also contains Ca, Y, PO4, U and Th. We evaluated the analytical interference of each element present on the sample on X-rays spectrum. The studied samples are certified standards and the obtained results have been compared to EDTA titration results, an already well-established and widely trusted method.We also measured the matrix effect thus using a complex rare earths standard. Results show that quantification by XRF technique is as accurate as the results in dose titration with EDTA for the same elements, with the advantage of exempting the previous separation step from each rare earth and from other elements present in the matrix (such as U and Th). (author)

Luminescence of rare earth-doped Si-ZrO2 co-sputtered films

International Nuclear Information System (INIS)

Rozo, Carlos; Jaque, Daniel; Fonseca, Luis F.; Sole, Jose Garcia

2008-01-01

Er-doped Si-yttria-stabilized zirconia (YSZ) thin film samples were prepared by rf co-sputtering. Chemical composition of the samples was determined using energy-dispersive spectroscopy (EDS) and the structure of the films by X-ray diffraction (XRD). The samples were annealed to 700 deg. C. Photoluminescence (PL) measurements were performed for the visible and infrared. By exciting with the 488-nm-laser line the Er 3+ emissions 2 H 11/2 → 4 I 15/2 , 4 S 3/2 → 4 I 15/2 , 4 F 9/2 → 4 I 15/2 and a narrow 4 I 13/2 → 4 I 15/2 emission were observed. The 4 I 11/2 → 4 I 15/2 emissions for the same excitation wavelength were weak. Excitation wavelength dependence of the 4 I 13/2 → 4 I 15/2 emissions indicated that the emissions were due to a combination of energy transfer from Si nanoparticles (np) to Er ions and energy transfer from defects in the matrix to the Er ions for excitations resonant with the energy levels of such defects. 4 I 13/2 → 4 I 15/2 emission decay measurements show two decaying populations of Er ions according to their locations with respect to other ions or any non-radiative defects. 4 I 11/2 → 4 I 15/2 emission dependence on 4 I 13/2 → 4 I 15/2 emission showed that the former was possibly due to a combination of downconversion from higher levels of the Er ions, energy transfer from Si nanoparticles and upconversion transfer processes. We concluded that Er-doped Si-YSZ is a promising material for photonic applications being easily broadband excited using low-pumping powers

Direct observation of multivalent states and 4 f →3 d charge transfer in Ce-doped yttrium iron garnet thin films

Science.gov (United States)

Vasili, H. B.; Casals, B.; Cichelero, R.; Macià, F.; Geshev, J.; Gargiani, P.; Valvidares, M.; Herrero-Martin, J.; Pellegrin, E.; Fontcuberta, J.; Herranz, G.

2017-07-01

Due to their large magneto-optic responses, rare-earth-doped yttrium iron garnets, Y3F e5O12 (YIG), are highly regarded for their potential in photonics and magnonics. Here, we consider the case of Ce-doped YIG (Ce-YIG) thin films, in which substitutional C e3 + ions are magnetic because of their 4 f1 ground state. In order to elucidate the impact of Ce substitution on the magnetization of YIG, we have carried out soft x-ray spectroscopy measurements on Ce-YIG films. In particular, we have used the element specificity of x-ray magnetic circular dichroism to extract the individual magnetization curves linked to Ce and Fe ions. Our results show that Ce doping triggers a selective charge transfer from Ce to the Fe tetrahedral sites in the YIG structure. This, in turn, causes a disruption of the electronic and magnetic properties of the parent compound, reducing the exchange coupling between the Ce and Fe magnetic moments and causing atypical magnetic behavior. Our work is relevant for understanding magnetism in rare-earth-doped YIG and, eventually, may enable a quantitative evaluation of the magneto-optical properties of rare-earth incorporation into YIG.

Preparation of Ce- and La-Doped Li4Ti5O12 Nanosheets and Their Electrochemical Performance in Li Half Cell and Li4Ti5O12/LiFePO4 Full Cell Batteries

Directory of Open Access Journals (Sweden)

Meng Qin

2017-06-01

Full Text Available This work reports on the synthesis of rare earth-doped Li4Ti5O12 nanosheets with high electrochemical performance as anode material both in Li half and Li4Ti5O12/LiFePO4 full cell batteries. Through the combination of decreasing the particle size and doping by rare earth atoms (Ce and La, Ce and La doped Li4Ti5O12 nanosheets show the excellent electrochemical performance in terms of high specific capacity, good cycling stability and excellent rate performance in half cells. Notably, the Ce-doped Li4Ti5O12 shows good electrochemical performance as anode in a full cell which LiFePO4 was used as cathode. The superior electrochemical performance can be attributed to doping as well as the nanosized particle, which facilitates transportation of the lithium ion and electron transportation. This research shows that the rare earth doped Li4Ti5O12 nanosheets can be suitable as a high rate performance anode material in lithium-ion batteries.

Preparation of Ce- and La-Doped Li4Ti5O12 Nanosheets and Their Electrochemical Performance in Li Half Cell and Li4Ti5O12/LiFePO4 Full Cell Batteries

Science.gov (United States)

Qin, Meng; Li, Yueming; Lv, Xiao-Jun

2017-01-01

This work reports on the synthesis of rare earth-doped Li4Ti5O12 nanosheets with high electrochemical performance as anode material both in Li half and Li4Ti5O12/LiFePO4 full cell batteries. Through the combination of decreasing the particle size and doping by rare earth atoms (Ce and La), Ce and La doped Li4Ti5O12 nanosheets show the excellent electrochemical performance in terms of high specific capacity, good cycling stability and excellent rate performance in half cells. Notably, the Ce-doped Li4Ti5O12 shows good electrochemical performance as anode in a full cell which LiFePO4 was used as cathode. The superior electrochemical performance can be attributed to doping as well as the nanosized particle, which facilitates transportation of the lithium ion and electron transportation. This research shows that the rare earth doped Li4Ti5O12 nanosheets can be suitable as a high rate performance anode material in lithium-ion batteries. PMID:28632167

Nanostructured rare earth doped Nb2O5: Structural, optical properties and their correlation with photonic applications

International Nuclear Information System (INIS)

Pereira, Rafael Ramiro; Aquino, Felipe Thomaz; Ferrier, Alban; Goldner, Philippe; Gonçalves, Rogéria R.

2016-01-01

In the present work, we report on a systematic study on structural and spectroscopic properties Eu 3+ and Er 3+ -doped Nb 2 O 5 prepared by sol–gel method. The Eu 3+ ions were used as structural probe to determine the symmetry sites occupied by lanthanide ions. The Eu 3+ -doped Nb 2 O 5 nanocrystalline powders were annealed at different temperatures to verify how the different Nb 2 O 5 crystalline phases affect the structure and the luminescence properties. Er 3+ -doped Nb 2 O 5 was prepared showing an intense NIR luminescence, and, visible luminescence on the green and red, deriving from upconversion process. The synthetized materials can find widespread applicability in photonics as red luminophor for white LED (with tricolor), optical amplifiers and upconverter materials. - Highlights: • Vis and NIR emission from nanostructured lanthanide doped Nb 2 O 5 . • Eu 3+ -doped Nb 2 O 5 as Red luminophor. • Multicolor tunability of intense upconversion emission from lanthanide doped Nb 2 O 5 . • Potential application as biological markers. • Broad band NIR emission.

SURVEY OF THE SPECTRA OF THE DIVALENT RARE EARTH IONS IN CUBIC CRYSTALS

Energy Technology Data Exchange (ETDEWEB)

McClure, Donald S. [Univ. of Chicago, IL (United States); Kiss, Zoltan J. [RCA Laboratories, Princeton, NJ (United States)

1963-04-15

The rare earth ions may exist in the divalent state in suitable host crystals such as CaF/sub 2/. All of the trivalent ions from La to Yb are reduced in situ to the divalent state in CaF/sub 2/ by gamma irradiation. The spectra of most of these ions show that the ground and first few excited states derive from f/sup n/ configurations, but the wesk absorption due to these is masked at higher energies by strong broad bands of the parity permitted f/sup n/ yields f/sup n-1/ d transitions. The excitation energy of these spectra have been calculated in a first approximation as the energy difference between the Hund Rule'' single determinant states of the configurations f/sup n -1/d and f/sup n/. This procedure satisfactorily accounts for the remarkable variations in the excitation energy in passing from one ion to the next in the series with the exception of Ge/ sup 2+/ Ce/sup 2+/, and Tb/sup 2+/, Ge/sup 2+/ probably has f/sup 7/d for its ground con figuration, while Ce/sup 2+/ and Tb/sup 2+/ are borderline cases. The spectral structure probably arises chiefly from the crystal field splitting of the d-orbital, since each ion in CaF/sub 2/ has a similar spectrum, and the spectra change drastically in sites of other than cubic symmetry. (auth)

Ball-milled nano-colloids of rare-earth compounds as liquid gain media for capillary optical amplifiers and lasers

Science.gov (United States)

Patel, Darayas; Blockmon, Avery; Ochieng, Vanesa; Lewis, Ashley; Wright, Donald M.; Lewis, Danielle; Valentine, Rueben; Valentine, Maucus; Wesley, Dennis; Sarkisov, Sergey S.; Darwish, Abdalla M.; Sarkisov, Avedik S.

2017-02-01

Nano-colloids and nano-crystals doped with ions of rare-earth elements have recently attracted a lot of attention in the scientific community due to their potential applications as biomarkers, fluorescent inks, gain media for lasers and optical amplifiers. Many rare-earth doped materials of different compositions, shapes and size distribution have been prepared by different synthetic methods, such as chemical vapor deposition, sol-gel process, micro-emulsion techniques, gas phase condensation methods, hydrothermal methods and laser ablation. In this paper micro-crystalline powder of the rare-earthdoped compound NaYF4:Yb3+, Er3+ was synthesized using a simple wet process followed by baking in open air. Under 980 nm diode laser excitation strong fluorescence in the 100 nm band around 1531-nm peak was observed from the synthesized micro-powder. The micro-powder was pulverized using a ball mill and prepared in the form of nano-colloids in different liquids. The particle size of the obtained nano-colloids was measured using an atomic force microscope and a dynamic light scatterometer. The size of the nano-particles was close to 100-nm. The nano-colloids were utilized as a filling media in capillary optical amplifiers and lasers. The gain of a 7-cm-long capillary optical amplifier (150-micron inner diameter) was as high as 6 dB at 200 mW pump power. The synthesized nano-colloids and the active optical components using them can be potentially used in optical communication, signal processing, optical computing, and other applications.

Growth of Yb3+, Lu3+, Gd3+ co-doped KY(WO4)2 thin layers

NARCIS (Netherlands)

Aravazhi, S.; Geskus, D.; Pollnau, Markus; Worhoff, Kerstin; Agazzi, L.; Ismail, N.; Leijtens, X

2008-01-01

Rare-earth-ion-doped $KY(WO_4)_2 (KYW)$ is an important candidate for solid-state lasers. Its high refractive indices of the order of 2.0 make it attractive also for applications as integrated optical devices. Liquid phase epitaxy was employed for growing mono-crystalline KYW thin films co-doped

An improved ion-exchange separation of rare-earth elements for spectrographic analysis

International Nuclear Information System (INIS)

Jones, E.A.

1978-01-01

Rare-earth elements are separated from scandium and base metals by adsorption onto anion resin BIORAD AG1-X8 in the nitrate form from a mixture of 5 per cent 7M nitric acid and 95 per cent methanol. The yttrium subgroup is eluted with a mixture of 45 per cent 7M nitric acid and 55 per cent methanol, followed by elution of the cerium subgroup with 8M nitric acid. This separation facilitates the determination of the traces of the heavier yttrium subgroup of rare-earth elements

Analysis of electrical and microstructural characteristics of a ZnO-based varistor doped with rare earth oxide

International Nuclear Information System (INIS)

Andrade, J.M. de; Dias, R.; Furtado, J.G. de M.; Assuncao, F.C.R.

2010-01-01

Varistor is a semiconductor device, used in the protection of electrical systems, characterized to have a high no-linear electric resistance. Its properties are directly dependents of its chemical composition and microstructural characteristics. In this work were analyzed microstructural and electrical characteristics of a ZnO-based varistor doped with rare earth oxide, with chemical composition (mol%) 98,5.ZnO - 0,3.Pr 6 O 11 - 0,2.Dy 2 O 3 - 0,9.Co 2 O 3 - 0,1.Cr 2 O 3 . X-ray diffraction for phase characterization, scanning electron microscopy and energy dispersive X-ray spectroscopy were used for microstructural analysis. Measurement of average grain size and electrical and dielectric characteristics complete the characterization. The results show the formation of biphasic microstructure and with high densification, presenting relevant varistors characteristics but that would need improvements.(author)

Synthesis and thermoelectric properties of rare earth Yb-doped Ba8−xYbxSi30Ga16 clathrates

International Nuclear Information System (INIS)

Liu, Lihua; Li, Feng; Wei, Yuping; Chen, Ning; Bi, Shanli; Qiu, Hongmei; Cao, Guohui; Li, Yang

2014-01-01

Highlights: • Samples with the chemical formula Ba8− x Yb x Si 30 Ga 16 (x = 0, 0.5, 0.7, 1 and 1.5) were prepared. • Some Yb atoms enter the clathrate lattice to replace Ba, while other Yb atoms are oxidized as Yb 2 O 3 . • The thermal conductivity decreases with Yb-doping. • Thermoelectric figure of merit ZT significantly increased. -- Abstract: The potential thermoelectric and magnetic application of clathrate materials with rare-earth doping is the focus of much of the recent research activity in the synthetic material physics and chemistry. A series of clathrate samples with the chemical formula Ba 8−x Yb x Si 30 Ga 16 (x = 0, 0.5, 0.7, 1 and 1.5) were prepared by combining arc melting, ball milling and spark plasma sintering (SPS) techniques. X-ray diffraction and scanning electronic microscopy combined with energy-dispersive X-ray spectroscopy (EDS) analysis showed the dominant phase to be the type-I clathrate. Whereas, X-ray structural refinement and EDS analysis indicated that some Yb atoms enter the clathrate lattice to replace Ba at 2a sites, while other Yb atoms are oxidized as Yb 2 O 3 precipitated around grain boundaries. The solid solubility of Yb into clathrate lattice yielded x ∼ 0.3. Comparative analysis between Yb-doped and Yb-free clathrates showed that the thermal conductivity decreases with Yb-doping. Consequently, thermoelectric figure of merit ZT significantly increased

Fluorescence line-narrowing studies of rare earths in disordered solids

International Nuclear Information System (INIS)

Hall, D.W.

1982-01-01

This dissertation is made up of two experimental studies dealing with apparently diverse topics within the subject of rare earths (RE) in solids. The first study, described in Part II, concerns the vibrations of a disordered host material about an optically active rare-earth ion as manifested by vibrationally-assisted-electronic, or vibronic transitions. Part III of the dissertation describes an investigation of the influence of site anisotropy on the purely electronic, laser transition of Nd 3+ in glass. These two studies are bound together by the common experimental technique of laser-induced fluorescence line narrowing (FLN). By exciting fluorescence with monochromatic light of well-characterized polarization, one may select and observe the response of a single subset of the optically active ions and obtain information that is usually masked by the inhomogeneous nature of disordered solids

Metallothermic reduction of rare earth oxides

International Nuclear Information System (INIS)

Sharma, R.A.

1986-01-01

Rare earth oxides can be reduced to rare earth metals by a novel, high yield, metallothermic process. The oxides are dispersed in a suitable, molten, calcium chloride bath along with sodium metal. The sodium reacts with the calcium chloride to produce calcium metal which reduces the rare earth oxides to rare earth metals. The metals are collected in a discrete layer in the reaction vessel

Rare earth industries: Downstream business

International Nuclear Information System (INIS)

2011-01-01

The value chain of the rare earths business involves mining, extraction, processing, refining and the manufacture of an extensive range of downstream products which find wide applications in such industries including aerospace, consumer electronics, medical, military, automotive, renewable wind and solar energy and telecommunications. In fact the entire gamut of the high-tech industries depends on a sustainable supply of rare earths elements. The explosive demand in mobile phones is an excellent illustration of the massive potential that the rare earths business offers. In a matter of less than 20 years, the number of cell phones worldwide has reached a staggering 5 billion. Soon, going by the report of their growth in sales, the world demand for cell phones may even exceed the global population. Admittedly, the rare earths business does pose certain risks. Top among the risks are the health and safety risks. The mining, extraction and refining of rare earths produce residues and wastes which carry health and safety risks. The residues from the extraction and refining are radioactive, while their effluent waste streams do pose pollution risks to the receiving rivers and waterways. But, as clearly elaborated in a recent report by IAEA experts, there are technologies and systems available to efficiently mitigate such risks. The risks are Rare Earth manageable. However, it is crucial that the risk and waste management procedures are strictly followed and adhered to. This is where effective monitoring and surveillance throughout the life of all such rare earths facilities is crucial. Fortunately, Malaysia's regulatory standards on rare earths follow international standards. In some areas, Malaysia's regulatory regime is even more stringent than the international guidelines. (author)

Rare earth industries: Strategies for Malaysia

International Nuclear Information System (INIS)

2011-01-01

Evidently, many reports cite Malaysia as having reasonably substantial amounts of rare earths elements. In fact, based on the rare earths found in the residual tin deposits alone, Malaysia has about 30,000 tonnes. This does not take into account unmapped deposits which experts believe may offer more tonnages of rare earths. Brazil which is reported to have about 48,000 tonnes has announced plans to invest aggressively in the rare earths business. China has on record the largest reserves with about 36 million tonnes. This explains why China has invested heavily in the entire value chain of the rare earths business. Chinas committed investment in rare earths started many years ago when the country's foremost leaders proclaimed the strategic position of rare earths in the world economy. That forecast is now a reality where the rise in the green high-tech economy is seen driving global demand for rare earths in a big way. Malaysia needs to discover and venture into new economic growth areas. This will help fuel the country's drive to achieve a high income status by 2020 as articulated in the New Economic Model (NEM) and the many supporting Economic Transformation Plans that the Government has recently launched. Rare earths may be the new growth area for Malaysia. However, the business opportunities should not just be confined to the mining, extraction and production of rare earths elements alone if Malaysia is to maximise benefits from this industry. The industry's gold mine is in the downstream products. This is also the sector that China wants to expand. Japan which now controls about 50 % of the global market for downstream rare earths-based high-tech components is desperately looking for partners to grow their stake in the business. Malaysia needs to embark on the right strategies in order to build the rare earths industry in the country. What are the strategies? (author)

Synergism between rare earth cerium(IV) ion and vanillin on the corrosion of cold rolled steel in 1.0 M HCl solution

Energy Technology Data Exchange (ETDEWEB)

Li Xianghong [Department of Fundamental Courses, Southwest Forestry University, Kunming 650224 (China)], E-mail: xianghong-li@163.com; Deng Shuduan [Department of Wood Science and Technology, Southwest Forestry University, Kunming 650224 (China); Fu Hui [Department of Fundamental Courses, Southwest Forestry University, Kunming 650224 (China); Mu Guannan [Department of Chemistry, Yunnan University, Kunming 650091 (China)

2008-12-15

The synergism between rare earth cerium(IV) ion and vanillin on the corrosion of cold rolled steel (CRS) in 1.0 M HCl solution was first investigated by weight loss, potentiodynamic polarization, ultraviolet and visible spectrophotometer (UV-vis), X-ray photoelectron spectroscopy (XPS) and atomic force microscope (AFM). The results revealed that vanillin had a moderate inhibitive effect, and the adsorption of vanillin obeyed the Temkin adsorption isotherm. For rare earth Ce{sup 4+}, it had a negligible effect. However, incorporation of Ce{sup 4+} with vanillin significantly improved the inhibition performance, and produced strong synergistic inhibition effect. Depending on the results, the synergism mechanism was proposed.

Synergism between rare earth cerium(IV) ion and vanillin on the corrosion of cold rolled steel in 1.0 M HCl solution

International Nuclear Information System (INIS)

Li Xianghong; Deng Shuduan; Fu Hui; Mu Guannan

2008-01-01

The synergism between rare earth cerium(IV) ion and vanillin on the corrosion of cold rolled steel (CRS) in 1.0 M HCl solution was first investigated by weight loss, potentiodynamic polarization, ultraviolet and visible spectrophotometer (UV-vis), X-ray photoelectron spectroscopy (XPS) and atomic force microscope (AFM). The results revealed that vanillin had a moderate inhibitive effect, and the adsorption of vanillin obeyed the Temkin adsorption isotherm. For rare earth Ce 4+ , it had a negligible effect. However, incorporation of Ce 4+ with vanillin significantly improved the inhibition performance, and produced strong synergistic inhibition effect. Depending on the results, the synergism mechanism was proposed

Rare earth-iron-boron premanent magnets

International Nuclear Information System (INIS)

Ghendehari, M.H.

1988-01-01

This patent describes a method for producing rare earth-iron-boron permanent magnets containing added rare earth oxide, comprising the steps of: (a) mixing a particulate alloy containing at least one rare earth metal, iron, and boron with at least one particulate rare earth oxide; (b) aligning magnetic domains of the mixture in a magnetic field; (c) compacting the aligned mixture to form a shape; and (d) sintering the compacted shape

Effect of rare earth substitution on properties of barium strontium titanate ceramic and its multiferroic composite with nickel cobalt ferrite

International Nuclear Information System (INIS)

Pahuja, Poonam; Kotnala, R.K.; Tandon, R.P.

2014-01-01

Highlights: • Rare earth ions Dy 3+ , Gd 3+ and Sm 3+ have been substituted in Ba 0.95 Sr 0.05 TiO 3 (BST). • Ni 0.8 Co 0.2 Fe 2 O 4 has been used as ferrimagnetic phase to obtain composites. • Substitution of these ions increases dielectric constant of BST and composites. • Magnetoelectric coefficient of composites increases on substitution of these ions. - Abstract: Effect of substitution of rare earth ions (Dy 3+ , Gd 3+ and Sm 3+ ) on various properties of Ba 0.95 Sr 0.05 TiO 3 (BST) i.e. the composition Ba 0.95−1.5x Sr 0.05 R x TiO 3 (where x = 0.00, 0.01, 0.02, 0.03 and R are rare earths Dy, Gd, Sm) and that of their multiferroic composite with Ni 0.8 Co 0.2 Fe 2 O 4 (NCF) has been studied. Shifting of peaks corresponding to different compositions in the X-ray diffraction pattern confirmed the substitution of rare earth ions at both Ba 2+ and Ti 4+ sites in BST. It is clear from scanning electron microscopy (SEM) images that rare earth substitution in BST increases its grain size in both pure and composite samples. Substitution of rare earth ions results in increase in value of dielectric constant of pure and composite samples. Sm substitution in BST significantly decreases its Curie temperature. Dy substituted pure and composite samples possess superior ferroelectric properties as confirmed by polarization vs electric field (P–E) loops. Composite samples containing Dy, Gd and Sm substituted BST as ferroelectric phase possess lower values of remanent and saturation magnetizations in comparison to composite sample containing pure BST as ferroelectric phase (BSTC). Rare earth substituted composite samples possess higher value of magnetoelectric coefficient as compared to that for BSTC

Use of EDTA for potentiometric back titration of rare earths and analysis of their mixtures

International Nuclear Information System (INIS)

Zayed, M.A.; Rizk, M.S.; Khalifa, H.; Omer, W.F.

1987-01-01

Advantage was taken of the stoichiometric reaction between mercury(II), rare earths, alkaline earths, heavy metal ions and EDTA in urotropine buffered media to determine rare earths by back-titration of excess EDTA in the course of estimating a variety of lanthanides or analysing their binary mixture with one of the alkaline earth metals by selective control of pH; or analysing their binary mixtures with heavy metals using fluoride as a good masking agent for rare earths; or analysing their ternary mixtures with both heavy and alkaline earth metals in two steps, one by selective control of pH and the other by masking of rare earths with fluoride at lower pH to estimate the heavy metal. The procedures given are simple, rapid and extremely reliable. 19 refs. (author)

Processing of Pakistani carbonatites for separation of cerium from adjacent rare earths

International Nuclear Information System (INIS)

Akram, M.; Qazi, N.K.; Khan, M.F.; Hasan, G.H.; Ahmed, N.; Chughtai, N.A.

2003-01-01

Carbonatite rock of Loe-Shilman area in North Western Frontier Province (NWFP) of Pakistan contains rare earth elements. This rock was upgraded in terms of its rare earths content from 2,000 ppm to 10,000 ppm rare earths oxide (REO) by crushing, calcination at 1000 deg. C for 3 hrs and cold leaching with 2% HCl for 1 hr. 80% to 95% of rare earths present in carbonatite powder were digested in nitric acid at 60 deg. C after 2 hrs stirring. Tributyl phosphate (TBP), diluted with dodecane, was used as extractant for extraction of rare earths. Since extraction is dependent on pH of the aqueous feed solution, the role of nitrate ions concentration in the solvent extraction of rare earth elements (REEs) was studied. It was observed that extraction of REEs was maximum at pH 1.1. The solvent had been unable to extract REEs from high acidic feed solutions. Solvents of different molarities were also tried against aqueous phase of pH 1.1. Studies showed a poor gain at 0 M and 0.5 M of organic phase while no gain observed beyond 2 molar solvent. 1 M organic phase gave maximum yield of rare earths salt, Ln(OH)/sub 3/, when stripped solution precipitated with ammonium hydroxide solution. It was also observed that if aqueous solution of 3.0 N was treated with blank solvent (i.e. Molarity = 0), it gave almost the same result. It was further established that optimum quantity of caging agent, Al(NO/sub 3/)/sub 3/-9H/sub 2/O added to aqueous solution prior to pH adjustment (i.e. 10 gm/100 gm powder dissolved) suppressed fluoride ions (F') which were hindering the extraction of rare earths. This improved the extraction efficiency of desired elements. To optimise the process parameters like solvent dilution, aqueous to organic ratio and extraction/stripping times, a' series of experiments were performed. Recovery for the desired elements had been between 78% to 86%. The optimum extraction parameters were found to be TBP concentration 40% (v/v) for aqueous to organic ratio 1:5 and 50

Alkaline earth metal doped tin oxide as a novel oxygen storage material

Energy Technology Data Exchange (ETDEWEB)

Dong, Qiang, E-mail: dong@tagen.tohoku.ac.jp [Institute of Multidisciplinary Research for Advanced Materials, Tohoku University, 2-1-1 Katahira, Aoba-ku Sendai 980-8577 (Japan); Yin, Shu; Yoshida, Mizuki; Wu, Xiaoyong; Liu, Bin [Institute of Multidisciplinary Research for Advanced Materials, Tohoku University, 2-1-1 Katahira, Aoba-ku Sendai 980-8577 (Japan); Miura, Akira; Takei, Takahiro; Kumada, Nobuhiro [Department of Research Interdisciplinary Graduate School of Medicine and Engineering, University of Yamanashi, Miyamae cho-7, Kofu 400-8511 (Japan); Sato, Tsugio [Institute of Multidisciplinary Research for Advanced Materials, Tohoku University, 2-1-1 Katahira, Aoba-ku Sendai 980-8577 (Japan)

2015-09-15

Alkaline earth metal doped tin oxide (SnO{sub 2}) hollow nanospheres with a diameter of 50 nm have been synthesized successfully via a facial solvothermal route in a very simple system composed of only ethanol, acetic acid, SnCl{sub 4}·5H{sub 2}O and A(NO{sub 3}){sub 2}·xH{sub 2}O (A = Mg, Ca, Sr, Ba). The synthesized undoped SnO{sub 2} and A-doped SnO{sub 2} hollow nanospheres were characterized by the oxygen storage capacity (OSC), X-ray diffraction, transmission electron microscopy and the Brunauer–Emmet–Teller (BET) technique. The OSC values of all samples were measured using thermogravimetric-differential thermal analysis. The incorporation of alkaline earth metal ion into tin oxide greatly enhanced the thermal stability and OSC. Especially, Ba-doped SnO{sub 2} hollow nanospheres calcined at 1000 °C for 20 h with a BET surface area of 61 m{sup 2} g{sup −1} exhibited the considerably high OSC of 457 μmol-O g{sup −1} and good thermal stability. Alkaline earth metal doped tin oxide has the potential to be a novel oxygen storage material.

Rare Earth Elements - A New Challenge for the World Economy

Directory of Open Access Journals (Sweden)

Cristina Bumbac

2013-01-01

Full Text Available Rare Earth Elements or Rare Earth Metals (REM are a collection of seventeen chemical elements in the periodic table, namely scandium, yttrium and fifteen lanthanides. The term "rare earth" arises from the rare earth minerals from which they were first isolated. They are uncommon oxide-type minerals (earths found in Gandolinite extracted from one mine in Sweden. The first discovery was made in 1794, but it was only in 1940 that the scientist Frank Spedding developed an ion exchange procedure for separating and purifying the REM. For the next decades, they were hardly used in some "minor" industrial fields. Only after 2000 their importance grew, once the multitude of possibilities to use them was discovered due to technological progress. Now REM are incorporated into almost all modern technological devices: superconductors, magnets, electronic polishers, refining catalysts hybrid car components and military techniques. They are used in small quantities, but due to their extraordinary properties the prices are very high. The main problem is that China dominates this market, with 97% of total global supply. The highest concentration of rare earth metals are in Inner Mongolia in China, Mountain Pass in California U.S.A. and in Mount Weld in Australia. The developed countries are far behind China regarding production and are indeed depending on Chinese exports. Hence, there is a difficult situation on this particular market, with an uncertain future.

Thermal effects on light emission in Yb3+ -sensitized rare-earth doped optical glasses

International Nuclear Information System (INIS)

Gouveia, E.A.; Araujo, M.T. de; Gouveia-Neto, A.S.

2001-01-01

The temperature effect upon infrared-to-visible frequency upconversion fluorescence emission in off-resonance infrared excited Yb 3+ -sensitized rare-earth doped optical glasses is theoretically and experimentally investigated. We have examined samples of Er3+/Yb 3+ -codoped Ga 2 S 3 :La 2 O 3 chalcogenide glasses and germanosilicate optical fibers, and Ga2O3:La 2 O 3 chalcogenide and fluoroindate glasses codoped with Pr 3+ /Yb 3+ , excited off-resonance at 1.064μm. The experimental results revealed thermal induced enhancement in the visible upconversion emission intensity as the samples temperatures were increased within the range of 20 deg C to 260 deg C. The fluorescence emission enhancement is attributed to the temperature dependent multiphonon-assisted anti-Stokes excitation process of the ytterbium-sensitizer. A theoretical approach that takes into account a sensitizer temperature dependent effective absorption cross section, which depends upon the phonon occupation number in the host matrices, has proven to agree very well with the experimental data. As beneficial applications of the thermal enhancement, a temperature tunable amplifier and a fiber laser with improved power performance are presented. (author)

Optical spectroscopy of rare-earth ions doped KY(WO4)2 thin films

NARCIS (Netherlands)

García-Revilla, S.; Valiente, R.; Romanyuk, Y.E.; Utke, I.; Pollnau, Markus

KY(WO4)2 thin films doped with Dy3+, Tb3+, Yb3+, were grown onto KY(WO4)2 substrates using liquid-phase epitaxy. Spectroscopic investigations of the grown layers were performed. Obtained results were compared with spectra given for bulk crystals. Upconversion experiments after direct Yb3+ excitation

Chemical analysis of rare earth elements

International Nuclear Information System (INIS)

Tsukahara, Ryoichi; Sakoh, Takefumi; Nagai, Iwao

1994-01-01

Recently attention has been paid to ICP-AES or ICP-MS, and the reports on the analysis of rare earth elements by utilizing these methods continue to increase. These reports have become to take about 30% of the reports on rare earth analysis, and this is because these methods are highly sensitive to rare earth elements, and also these methods have spread widely. In ICP-AES and ICP-MS, mostly solution samples are measured, therefore, solids must be made into solution. At the time of quantitatively determining the rare earth elements of low concentration, separation and concentration are necessary. Referring to the literatures reported partially in 1990 and from 1991 to 1993, the progress of ICP-AES and ICP-MS is reported. Rare earth oxides and the alloys containing rare earth elements are easily decomposed with acids, but the decomposition of rocks is difficult, and its method is discussed. The separation of the rare earth elements from others in geochemical samples, cation exchange process is frequently utilized. Also solvent extraction process has been studied. For the separation of rare earth elements mutually, chromatography is used. The spectral interference in spectral analysis was studied. The comparison of these methods with other methods is reported. (K.I)

Radio-luminescence efficiency and rare-earth dispersion in Tb-doped silica glasses

Czech Academy of Sciences Publication Activity Database

Fasoli, M.; Moretti, F.; Lauria, A.; Chiodini, N.; Vedda, A.; Nikl, Martin

2007-01-01

Roč. 42, - (2007), s. 784-787 ISSN 1350-4487 Institutional research plan: CEZ:AV0Z10100521 Keywords : sol-gel * scintillators * silica * rare earths * terbium Subject RIV: BM - Solid Matter Physics ; Magnetism Impact factor: 1.054, year: 2007

Properties and structure of high erbium doped phosphate glass for short optical fibers amplifiers

International Nuclear Information System (INIS)

Seneschal, Karine; Smektala, Frederic; Bureau, Bruno; Floch, Marie Le; Jiang Shibin; Luo, Tao; Lucas, Jacques; Peyghambarian, Nasser

2005-01-01

New phosphate glasses have been developed in order to incorporate high rare-earth ions concentrations. These glasses present a great chemical stability and a high optical quality. The phosphate glass network is open, very flexible, with a linkage of the tetrahedrons very disordered and contains a larger number of non-bridging oxygens (66%). The great stability and resistance against crystallization associated with the possibility to incorporate high doping concentration of rare-earth ions in these phosphate glasses make them very good candidates for the realization of ultra short single mode amplifiers with a high gain at 1.55 μm

Luminescent rare earth vanadate nanoparticles doped with Eu3+ and Bi3 for sensing and imaging applications

Science.gov (United States)

Escudero, Alberto; Carrillo-Carrión, Carolina; Zyuzin, Mikhail; Hartmann, Raimo; Ashraf, Sumaira; Parak, Wolfgang J.

2016-03-01

Nanoparticles (NPs) are attracting interest in nanomedicine due to their potential medical applications, ranging from optical biolabels and contrast agents for magnetic resonance imaging to carriers for drug and gene delivery for disease therapy.[1] Rare earth (RE) based nanophosphors exhibit important advantages compared with other available luminescent materials, such as quantum dots and nanostructures functionalized with organic dyes, due to their lower toxicities, photostabilities, high thermal and chemical stabilities, high luminescence quantum yields, and sharp emission bands.[2] Yttrium orthovanadate NPs doped with Eu3+ and Bi3+, functionalized with poly acryl acid (PAA), and excitable by near-ultraviolet light have been synthesized by homogeneous precipitation at 120 °C from solutions of rare earth precursors (yttrium acetylacetonate and europium nitrate), bismuth nitrate, sodium orthovanadate, and PAA, in an ethylene glycol/water mixture. Quasispheres with sizes from 93 to 51 nm were obtained. The as synthesized NPs were already functionalized with PAA. The NPs showed the typical red luminescence of Eu3+, which can be excited with near-UV light through an energy transfer from the vanadate anion. The presence of Bi3+ shifts the maximum of the broad excitation band from 280 nm to 342 nm. This excitation path is much more efficient than the direct excitation of the Eu3+ electronic levels, and results in a much higher luminescence. The NPs can be uptaken by HeLa cells, and are eventually located in the lysosomes after being internalized. Finally, the functionalization with PAA provides -COOH anchors for adding functional ligands of biomedical interest that can be used for sensing applications.

The industry of metallic rare earths (R.E.)

International Nuclear Information System (INIS)

Poirier, P.

1979-01-01

The following subjects are discussed: rare earths resources (rare earths abondance and world reserves, main ores). Rare earths separation and purification (ionic exchange, solvent extraction). Metallic rare earths and their mixtures, metallothermic reduction of oxides or fluorides (Ca, Mg, Al, Si or rare earth metals), Co-reduction process for intermetallic compounds (SmCo 5 ). Industrial applications of metallic rare earths (traditional applications such as flints, nodular cast iron, steel refining, magnesium industrie, applications under development such as rare earths/cobalt magnets, LaNi 5 for hydrogen storage, special alloys (automotive post combustion), magnetostrictive alloys). Economical problems: rare earth are elements relatively abundant and often at easily accessible prices. However, this group of 15 elements are liable to certain economical restraints. It is difficult to crack ore for only one rare earth. Availability of one given rare earth must be associated with the other corresponding rare earths to absorb all the other rare earths in other applications. Rare-earth industry has a strong expanding rate. 20% per year average for 6 years with Rhone-Poulenc. Thanks to their exceptional, specific characteristics rare earths have a bright future particularly for their metals

Adducts of rare earth tris-acetylacetonates with dimethyl sulfoxide

International Nuclear Information System (INIS)

Dzyubenko, N.G.; Kalenichenko, Yu.V.; Martynenko, L.I.

1988-01-01

Adducts of rare earth and yttrium (r.e.e., M) acetylacetonates with dimethyl sulfoxide (DMSO), MA 3 xnDMSO are synthesized. The acetylacetonates of light r.e.e. (M=La-Tb) are shown by different physico-chemical methods to form diadducts of the MA 3 x2DMSOxH 2 O composition, where A - -acetylacetonate-ion, and the acetyl-acetonates of heavy r.e.e. (M=Dy-Lu, Y)-monoadducts MA 3 xDMSO. The estimation of adduct thermal stability is carried out using the values of seeming activation energy of their thermal degradation. Monoadducts are shown to give volatile forms of rare earth acetylacetonates during heating in vacuum, and diadducts do not form volatile forms of acetylacetonates

Structural, optical absorption and photoluminescence spectral studies of Sm3+ ions in Alkaline-Earth Boro Tellurite glasses

Science.gov (United States)

Siva Rama Krishna Reddy, K.; Swapna, K.; Mahamuda, Sk.; Venkateswarlu, M.; Srinivas Prasad, M. V. V. K.; Rao, A. S.; Prakash, G. Vijaya

2018-05-01

Sm3+ ions doped Alkaline-Earth Boro Tellurite (AEBT) glasses were prepared by using conventional melt quenching technique and characterized using the spectroscopic techniques such as FT-IR, optical absorption, emission and decay spectral measurements to understand their utility in optoelectronic devices. From absorption spectra, the bonding parameters, nephelauxetic ratios were determined to know the nature of bonding between Sm3+ ions and its surrounding ligands. From the measured oscillator strengths, the Judd-Ofelt (J-O) intensity parameters were evaluated and in turn used to estimate various radiative parameters for the fluorescent levels of Sm3+ ions in AEBT glasses. The PL spectra of Sm3+ ions exhibit three emission bands corresponding to the transitions 4G5/2 → 6H5/2, 6H7/2 and 6H9/2 in the visible region for which the emission cross-sections and branching ratios were evaluated. The decay spectral profiles measured for 4G5/2 → 6H7/2 transition showed single exponential for lower concentration and non-exponential for higher concentration of doped rare earth ion in the as prepared glasses. Conversion of decay spectral profiles from single to non-exponential have been analyzed using Inokuti-Hirayama (I-H) model to understand the energy transfer mechanism involved in the decay process. CIE Chromaticity coordinates were measured using emission spectral data to identify the exact region of emission from the as-prepared glasses. From the evaluated radiative parameters, emission cross-sections and quantum efficiencies, it was observed that AEBT glass with 1 mol% of Sm3+ ions is more suitable for designing optoelectronic devices.

Field-induced valence transition in rare-earth system

International Nuclear Information System (INIS)

Chattopadhaya, A.; Ghatak, S.K.

2000-01-01

The magnetic field-induced valence transition in rare-earth compound has been examined based on a pseudospin S=1 Ising model proposed earlier for valence transition. The model includes finite mixing between two pertinent ionic configurations (magnetic and non-magnetic) separated by an energy gap and with intersite interaction between rare-earth ions. Using the mean field approximation the magnetic behaviour and the critical field (H c ) for transition are obtained as a function of energy gap and temperature. The phase boundary defined in terms of reduced field H c /H co and reduced temperature T/T v (T v being valence transition temperature in absence of field) is nearly independent of energy gap. These results are in qualitative agreement with experimental observation in Yb- and Eu-compounds

Rare earth elements: end use and recyclability

Science.gov (United States)

Goonan, Thomas G.

2011-01-01

Rare earth elements are used in mature markets (such as catalysts, glassmaking, lighting, and metallurgy), which account for 59 percent of the total worldwide consumption of rare earth elements, and in newer, high-growth markets (such as battery alloys, ceramics, and permanent magnets), which account for 41 percent of the total worldwide consumption of rare earth elements. In mature market segments, lanthanum and cerium constitute about 80 percent of rare earth elements used, and in new market segments, dysprosium, neodymium, and praseodymium account for about 85 percent of rare earth elements used. Regardless of the end use, rare earth elements are not recycled in large quantities, but could be if recycling became mandated or very high prices of rare earth elements made recycling feasible.

Rare earth oxide-doped titania nanocomposites with enhanced photocatalytic activity towards the degradation of partially hydrolysis polyacrylamide

International Nuclear Information System (INIS)

Li Jinhuan; Yang Xia; Yu Xiaodan; Xu, Leilei; Kang Wanli; Yan Wenhua; Gao Hongfeng; Liu Zhonghe; Guo Yihang

2009-01-01

Rare-earth oxide-doped titania nanocomposites (RE 3+ /TiO 2 , where RE = Eu 3+ , Pr 3+ , Gd 3+ , Nd 3+ , and Y 3+ ) were prepared by a one-step sol-gel-solvothermal method. The products exhibited anatase phase structure, mesoporosity, and interesting surface compositions with three oxygen species and two titanium species. The products were used as the photocatalysts to degrade a partially hydrolysis polyacrylamide (HPAM) under UV-light irradiation, a very useful polymer in oil recovery. For comparison, Degussa P25 and as-prepared pure TiO 2 were also tested under the same conditions. The enhanced photocatalytic activity was obtained on as-prepared Eu 3+ (Gd 3+ , Pr 3+ )/TiO 2 composites, and the reasons were explained. Finally, the degradation pathway of HPAM over the RE 3+ /TiO 2 composite was put forward based on the intermediates produced during the photocatalysis procedure.

Activation analysis of trace amounts of rare earth in high purity tantalum

International Nuclear Information System (INIS)

Ishibashi, Wataru; Saito, Shinichi; Hirayama, Tooru.

1975-01-01

It is necessary to separate rare earth from tantalum by rapid methods in order to remove effects of a strong radioactivity and a short half-life. Tantalum is extracted with 10%N-lauryl (trialkylmethyl) amino-benzene pre-equilibrated with a solution of 9 M hydrochloric and 0.15 M hydrofluoric acid. A non-radioactive rare earth element is added to this aqueous solution, a precipitate of trace amounts of radioactive rare earth in aqueous solution is formed by this addition of rare earth. Some factors in the determination are: 1) the effect of the irradiation position of the sample in the atomic reactor, 2) the effect on the extraction with 10%N-lauryl (trialkylmethyl) amino-benzene for the radioactive rare earth, 3) the effect of the concentration of hydrofluoric acid, ammonia water and nitric acid on co-precipitation. As a result of the investigation we obtained the following satisfactory results: 1) Rare earth was not effected by the extraction of tantalum with 10%N-lauryl (trialkylmethyl) amino-benzene. 2) The recovery of rare earth by co-precipitation increases when an ammonium ion coexists, and when the concentration of hydrofluoric acid decreases, but the recovery decreases with the increase of nitric acid concentration. 3) The time required for the extraction is 9 hours. In case of determination for dysprosium, tantalum extracted with 10%N-lauryl (trialkylmethyl) amino-benzene before activation and the time for separation is 2 hours. (auth.)

New Trident Molecule with Phosphoric Acid Functionality for Trivalent Rare Earth Extraction

Directory of Open Access Journals (Sweden)

Keisuke Ohto

2017-11-01

Full Text Available Tripodal extraction reagent with three phosphoric acid groups, together with the corresponding monopodal molecule has been prepared to investigate some metals extraction behavior, in particular, trivalent rare earth elements (REEs. The tripodal reagent exhibited extremely high selectivity for metals with high valency such as Zr(IV, In(III, Lu(III, and Fe(III. Tripodal reagent also exhibited exceptionally high extraction ability compared with the corresponding monopodal one in the extraction of trivalent rare earths. The result for the stoichiometry of tripodal reagent to heavy rare earths showed the inflection point between Er (2:1 for a ligand with ion and Tm (1:1. The extraction reactions were determined for all rare earths with both reagents. The extraction equilibrium constants (Kex, the separation factors (β, half pH values (pH1/2, difference half pH values (ΔpH1/2 for extraction of REEs with both reagents are estimated.

Studies on the separation of rare earth elements and the nuclear decay properties of short lived rare-earth nuclides in U-235 fission products

International Nuclear Information System (INIS)

Ohyoshi, Akira; Ohyoshi, Emiko.

1980-01-01

The effect of a complex-forming agent, with which rare earths consecutively form the complexes, on the separation of a pair of adjacent rare earths by electromigration has been investigated. The relation between the separation factor for two complexes and the ligand-ion concentration was examined in the separation of La-Ce and Ce-Pr pairs with nitrilotriacetic acid. Rare earths were able to be isolated rapidly at the optimum ligand-ion concentration in lower one, and this method was applied to study the nuclear decay properties of the short lived isotopes of La, Ce, Pr, Nd and Yt formed in the fission of U-235. This method permits the direct measurement of the decay of La-144 without the interference from the radiation of other fission products. The gamma-ray spectrum of La-144 was measured with a high resolution Ge(Li) detector, and the gamma-transition was observed. From the decay plots of two strong photopeaks, the half-life of La-144 was determined. In the case of Ce fraction, the photopeaks assigned to respective isotopes were observed. In the studies on the decay properties of Pr-148 and Pr-149, the decay plot of the strong photopeak showed good linearity, and the accurate half-life of Pr-148 was determined. Similarly, the half-life of Pr-149 was longer than the previously reported value. (Kako, I.)

Crystal fields in Sc, Y, and the heavy-rare-earth metals Tb, Dy, Ho, Er, Tm, and Lu

International Nuclear Information System (INIS)

Touborg, P.

1977-01-01

Experimental investigations of the magnetic poperties of dilute alloys of the rare-earth solutes Tb, Dy, Ho, Er, and Tm in the nonmagnetic hosts Lu, Y, and Sc have been performed. These measurements, which include and supplement earlier published results, have been analyzed and crystal-field parameters for all these 15 alloy systems deduced. The consistency of the parameters was confirmed by a variety of magnetic measurements, including neutron spectroscopy. Crystal-field parameters have also been derived for the ions in pure magnetic rare-earth metals and their alloys using the results for the dilute alloys supplemented with paramagnetic measurements up to high temperatures on the concentrated systems. Mean values and standard deviations of the higher-order crystal-field parameters for all Y and Lu alloys are B 40 /β = 6.8 +- 0.9 K, B 60 /γ = 13.6 +- 0.7 K, and B 66 /γ = (9.7 +- 1.1) B 60 /γ. These values: with the inaccuracies somewhat increased: are expected to be representative also for the magnetic rare-earth metals. For rare-earth ions in the Sc host the values B 40 /β = 9.9 +- 1.9 K, B 60 /γ = 19.8 +- 1.5 K, and B 66 /γ = (9.4 +- 0.9) B 60 /γ were deduced. B 20 /α is a host-sensitive parameter which has the average values of -102.7, -53.4, and 29.5 K for rare-earth ions in Y, Lu, and Sc, respectively. There is also evidence that this parameter varies with the solute. B 20 /α for ions in the pure magnetic rare-earth metals and their alloys shows a linear variation with c/a ratio characteristic of each ion. The results indicate a contribution from anisotropic exchange to the high-temperature paramagnetic anisotropy of approximately 20% for Tb, Dy, Ho, and Er, and approximately 10% for Tm

A rare earth-based metal-organic framework for moisture removal and control in confined spaces

KAUST Repository

Eddaoudi, Mohamed

2017-04-13

A method for preparing a metal-organic framework (MOF) comprising contacting one or more of a rare earth metal ion component with one or more of a tetratopic ligand component, sufficient to form a rare earth-based MOF for controlling moisture in an environment. A method of moisture control in an environment comprising adsorbing and/or desorbing water vapor in an environment using a MOF, the MOF including one or more of a rare earth metal ion component and one or more of a tetratopic ligand component. A method of controlling moisture in an environment comprising sensing the relative humidity in the environment comprising a MOF; and adsorbing water vapor on the MOF if the relative humidity is above a first level, sufficient to control moisture in an environment. The examples relate to a MOF created from 1,2,4,5-Tetrakis(4-carboxyphenyl )benzene (BTEB) as tetratopic ligand, 2-fluorobenzoic acid and Y(NO3)3, Tb(NO3)3 and Yb(NO3)3 as rare earth metals.

High purity neodymium acetate from mixed rare earth carbonates

International Nuclear Information System (INIS)

Queiroz, Carlos A. da Silva; Rocha, Soraya M. Rizzo da; Vasconcellos, Mari E. de; Lobo, Raquel M.; Seneda, Jose A.; Pedreira, Walter dos R.

2011-01-01

A simple and economical chemical process for obtaining high purity neodymium acetate is discussed. The raw material in the form rare earth carbonate is produced industrially from the chemical treatment of Brazilian monazite. Ion exchange chromatography technique with a strong cationic resin, proper to water treatment, and without the use of retention ions was used for the fractionating of the rare earth elements (REE). In this way, it was possible to obtain 99.9% pure Nd 2 O 3 in yields greater than or equal 80%, with the elution of the REE using ammonium salt of ethylenediaminetetraacetic acid (EDTA) solution in pH controlled. The complex of EDTA-neodymium was transformed into neodymium oxide, which was subsequently dissolved in acetic acid to obtain the neodymium acetates. Molecular absorption spectrophotometry was used to monitor the neodymium content during the process and sector field inductively coupled plasma mass spectrometry was used to certify the purity of the neodymium acetates. The typical neodymium acetates obtained contain the followings contaminants in μg g -1 : Sc(5.1); Y (0.9); La (1.0); Ce (6.1); Pr (34,4); Sm (12.8); Eu (1.1); Gd (15.4); Tb (29.3); Dy (5.2), Ho(7.4); Er (14.6); Tm (0.3); Yb (2.5); Lu (1.0). The high purity neodymium acetates obtained from this procedure have been applied, replacing the imported product, in research and development area on rare earth catalysts. (author)

Recovering heavy rare earth metals from magnet scrap

Science.gov (United States)

Ott, Ryan T.; McCallum, Ralph W.; Jones, Lawrence L.

2017-08-08

A method of treating rare earth metal-bearing permanent magnet scrap, waste or other material in a manner to recover the heavy rare earth metal content separately from the light rare earth metal content. The heavy rare earth metal content can be recovered either as a heavy rare earth metal-enriched iron based alloy or as a heavy rare earth metal based alloy.

Separation of cerium and fractionation of rare earths from mixed chlorides

International Nuclear Information System (INIS)

Silva Queiroz, C.A. da; Sood, S.P.; Abrao, A.

1982-01-01

The separation of cerium from rare earths chlorides solutions by precipitation with hydrogen peroxide/air/dil. ammonium hydroxide; purification of cerium; fractionation by ion exchange and analytical control of the process are presented. (A.R.H.) [pt

Evaluation of capacity ion exchange of MMT-Na+with rare earth salts for use in polymeric nano composites

International Nuclear Information System (INIS)

Maino, Isabel B.; Scienza, Lisete C.; Piazza, Diego; Zattera, Ademir J.; Ferreira, Carlos A.

2011-01-01

The modification of the montmorillonite clay is associated with materials science, arousing interest in science and technology provide significant improvements when incorporated into polymeric materials neat and conventional composites. The process of modification of clays occurs mainly through the ion exchange of exchangeable cations in its crystal structure. In this study, we performed ion exchange of sodium montmorillonite with rare earth salts (cerium) through two routes: centrifugation and filtration. The samples were characterized by X-ray diffraction (XRD) and energy dispersive analysis by X-ray (EDS). The sample obtained by the filtration route showed an increase of basal clay by XRD, indicating the presence of salts of cerium on the structure, and corroborated by EDS analysis. (author)

A divalent rare earth oxide semiconductor: Yttrium monoxide

Energy Technology Data Exchange (ETDEWEB)

Kaminaga, Kenichi; Sei, Ryosuke [Department of Chemistry, The University of Tokyo, Tokyo 113-0033 (Japan); Department of Chemistry, Tohoku University, Sendai 980-8578 (Japan); Hayashi, Kouichi [Department of Environmental and Materials Engineering, Nagoya Institute of Technology, Nagoya 466-8555 (Japan); Happo, Naohisa [School of Information Sciences, Hiroshima City University, Hiroshima 731-3194 (Japan); Tajiri, Hiroo [Japan Synchrotron Radiation Research Institute (JASRI)/SPring-8, Sayo 679-5198 (Japan); Oka, Daichi; Fukumura, Tomoteru, E-mail: tomoteru.fukumura.e4@tohoku.ac.jp [Department of Chemistry, Tohoku University, Sendai 980-8578 (Japan); Hasegawa, Tetsuya [Department of Chemistry, The University of Tokyo, Tokyo 113-0033 (Japan)

2016-03-21

Rare earth oxides are usually widegap insulators like Y{sub 2}O{sub 3} with closed shell trivalent rare earth ions. In this study, solid phase rock salt structure yttrium monoxide, YO, with unusual valence of Y{sup 2+} (4d{sup 1}) was synthesized in a form of epitaxial thin film by pulsed laser deposition method. YO has been recognized as gaseous phase in previous studies. In contrast with Y{sub 2}O{sub 3}, YO was dark-brown colored and narrow gap semiconductor. The tunable electrical conductivity ranging from 10{sup −1} to 10{sup 3} Ω{sup −1 }cm{sup −1} was attributed to the presence of oxygen vacancies serving as electron donor. Weak antilocalization behavior observed in magnetoresistance indicated significant role of spin-orbit coupling as a manifestation of 4d electron carrier.

Hexagonal perovskites with cationic vacancies. 32. Photoluminescence of trivalent rare earth in the systems Ba/sub 2-y/Sr/sub y/La/sub 2-x/RE/sub x/MgW/sub 2/vacantO/sub 12/

Energy Technology Data Exchange (ETDEWEB)

Kemmler-Sack, S [Tuebingen Univ. (Germany, F.R.). Lehrstuhl fuer Anorganische Chemie 2

1982-06-01

In the series Ba/sub 2-y/Sr/sub y/La/sub 2-x/RE/sub x/MgW/sub 2/vacantO/sub 12/ the Ba/sup 2 +/ can be completely substituted by Sr/sup 2 +/. All compounds crystallize in the rhombohedral 12 L-type (space group R-3m; sequence (hhcc)/sub 3/). By doping the stacking polytypes with some of the trivalent rare earths efficient visible photoluminescence is obtained. The simultaneous incorporation of two different rare earth ions leads to two-color-phosphors, which, according to the excitation energy used, emit either mainly the typical spectrum from one or the other activator; the corresponding luminescence mechanism are discussed.

Optical and structural characterization of the pure and doped BaY2F8 with rare earths for application in radiation detectors and scintillators

International Nuclear Information System (INIS)

Mello, Ana Carolina Santana de

2008-01-01

In this work Barium Yttrium Fluoride (BaY 2 F 8 -BaYF) doped with different concentrations of ions Tb 3+ , Er 3+ , Tm 3+ e Nd 3+ were characterized, aiming the application in radiation detection devices that use the scintillating properties. Two types of samples were produced in the CLA-IPEN-SP, polycrystalline samples, obtained via solid state reaction of BaF 2 and YF 3 under HF atmosphere, and single crystals, obtained via the zone melting method also in a HF atmosphere. The samples were characterized using the following experimental techniques: X-ray powder diffraction, Radioluminescence (RL), Optical Absorption and Dispersive X-ray Absorption Spectroscopy (DXAS). The X-ray diffraction pattern showed the presence of the phase BaY 2 F 8 and a small amount of the phase Ba 4 Y 3 F 17 in the polycrystalline pure and Tb 3+ doped samples. The other samples showed only the desired BaY 2 F 8 phase. The radioluminescence measurements of the doped BaYF, when irradiated with X-rays, showed emission peaks in energies that are characteristics of the 4f-4f transitions of rare earths. The RL of the samples with 2 mol por cent and 3 mold of Tb 3+ showed quite intense peaks with a maximum emission peak at 545 nm. The Tm 3+ doped BYF showed that the scintillation efficiency is not directly proportional to the doping level, and the highest RL emission were obtained for the polycrystalline samples doped with 1 mol por cent, showing a maximum peak intensity at 456 nm (the blue region of the visible spectrum). All samples showed a phosphorescent decay time of the order of seconds. Single crystals of BaYF doped with 2 mol por cent of Er 3+ , in addition to one of the highest phosphorescence time, presents a quite strong Rl in the green region of the spectra. The radiation damage was evaluated by the optical absorption techniques and the results showed that the formation of the absorption bands can be connected to colors centers generated by radiation in the matrix. Measurements of

Sintered cobalt-rare earth intermetallic product

International Nuclear Information System (INIS)

Benz, M.C.

1975-01-01

A process is described for preparing novel sintered cobalt--rare earth intermetallic products which can be magnetized to form permanent magnets having stable improved magnetic properties. A cobalt--rare earth metal alloy is formed having a composition which at sintering temperature falls outside the composition covered by the single Co 5 R intermetallic phase on the rare earth richer side. The alloy contains a major amount of the Co 5 R intermetallic phase and a second solid CoR phase which is richer in rare earth metal content than the Co 5 R phase. The specific cobalt and rare earth metal content of the alloy is substantially the same as that desired in the sintered product. The alloy, in particulate form, is pressed into compacts and sintered to the desired density. The sintered product is comprised of a major amount of the Co 5 R solid intermetallic phase and up to about 35 percent of the product of the second solid CoR intermetallic phase which is richer in rare earth metal content than the Co 5 R phase

Blue photoluminescence in Ti-doped alkaline-earth stannates

International Nuclear Information System (INIS)

Yamashita, Takahiro; Ueda, Kazushige

2007-01-01

Blue photoluminescence properties of Ti-doped alkaline-earth stannates, A 2 (Sn 1- x Ti x )O 4 (A=Ca, Sr, Ba) (x=0.005-0.15), were examined at room temperature. These stannates showed intense broad emission bands peaking at 445 nm for Ca 2 SnO 4 , at 410 nm for Sr 2 SnO 4 , and at 425 nm for Ba 2 SnO 4 under UV excitation. Emission intensities were relatively insensitive to Ti concentration and no sharp concentration quenching was observed. Mixing alkaline-earth ions in the crystal structures did not increase the emission intensities in the A 2 (Sn 1- x Ti x )O 4 system. The excitation spectra of these stannates exhibited broad bands just below the fundamental absorption edges, implying that luminescence centers do not consist of the component elements in the host materials. It was suggested that the isolated TiO 6 complexes are possible luminescence centers in these materials, as previously proposed in other Ti-doped stannates such as Mg 2 SnO 4 and Y 2 Sn 2 O 7 . - Graphical abstract: Blue photoluminescence properties of Ti-doped alkaline-earth stannates, A 2 (Sn 1- x Ti x )O 4 (A=Ca, Sr, Ba) (x=0.005-0.15), were examined at room temperature. These stannates showed intense broad emission bands peaking at 445 nm for Ca 2 SnO 4 , at 410 nm for Sr 2 SnO 4 , and at 425 nm for Ba 2 SnO 4 under UV excitation

HfO2 - rare earth oxide systems in the region with high content of rare earth oxide

International Nuclear Information System (INIS)

Shevchenko, A.V.; Lopato, L.M.

1982-01-01

Using the methods of annealing and hardenings (10 2 -10 4 deg/s cooling rate) and differential thermal analysis elements of state diagrams of HfO 2 - rare earth oxide (rare earths-La, Pr, Nd, Sm, Gd, Tb, Dy, Y, Er, Yb, Lu, Sc) systems from 1800 deg C up to melting in the range of 60-100 mol% rare earth oxide concentration were constructed. Regularities of HfQ 2 addition effect on high-temperature polymorphic transformations of rare earth oxides were studied. Results of investigation were discussed from viewpoint of crystal chemistry

Production of rare earth-silicon-iron alloys

International Nuclear Information System (INIS)

Mehra, O.K.; Bose, D.K.; Gupta, C.K.

1987-01-01

At Metallurgy Division, BARC, improved procedures for producing rare earth-silicon alloys have been investigated. In these methods, reduction of mixed rare earth oxide by a ferro-silicon and aluminium mixture in combination with CaO-MgO flux/CaO-CaF 2 flux have been tried to prepare an alloy product with a higher rare earth recovery at a higher rare earth content than the present commercial production method. The rare earth recovery using CaO-CaF 2 was 85 per cent while in the case of CaO-MgO flux it was 76 per cent. The corresponding rare earth contents in the alloy correspond to 40 per cent and 55 per cent by weight respectively. (author)

Robust Visible and Infrared Light Emitting Devices Using Rare-Earth-Doped GaN

National Research Council Canada - National Science Library

Steckl, Andrew

2006-01-01

Rare earth (RE) dopants (such as Er, Eu, Tm) in the wide bandgap semiconductor (WBGS) GaN are investigated for the fabrication of robust visible and infrared light emitting devices at a variety of wavelengths...

Spectroscopy and dynamics of rare earth doped fluorides

NARCIS (Netherlands)

Ebens, Willem Omco

1995-01-01

The defect structure of RE doped Fluorides has been studied along with the conductivity properties, using a variety of techniques, both experimental and theoretical. Two systems have been studied in detail, which represent two kinds of defect states for RE doped SrFr. The system SrFr:CeF, has been

Application of liquid-liquid extraction in separation of rare earths [Paper No. : V-6

International Nuclear Information System (INIS)

Deshpande, S.M.; Krishnan, N.P.K.; Murthy, T.K.S.; Swaminathan, T.V.

1979-01-01

The rare earths consist of fifteen elements which have very similar chemical properties and are difficult to separate from each other. Since they exist together in all naturally occurring minerals their separation is one of the important and difficult aspects of their technology. Liquid-liquid extraction has proved to be an efficient technique for their separation. The two important extraction systems that find practical and large scale application, the nitric acid + tri-n-butyl phosphate, and mineral acid (particularly hydrochloric acid) + organo phosphoric acid (like di-2-ethyl hexyl phosphoric acid), are briefly reviewed. The factors affecting the extraction and separation of rare earths in the two systems are discussed. On an industrial scale the extraction process is very often employed for an initial concentration of the desired rare earths from complex mixtures. The final purification is generally achieved by the ion exchange method. The utility of the solvent extraction process for the upgrading of selected rare earths-europium, samarium and gadolinium-from a mixed rare earth chloride, derived from monazite, is illustrated by the work carried out in this laboratory and pilot plant operation at the Alwaye plant of M/s. Indian Rare Earths Ltd. (author)

Properties of poly(vinyl alcohol)-borax gel doped with neodymium and praseodymium

International Nuclear Information System (INIS)

Lawrence, Mathias B.; Desa, J.A.E.; Rai, Renu; Aswal, V.K.

2014-01-01

Neodymium and praseodymium ions, singly and in combination, have been doped into a poly(vinyl alcohol)-borax matrix. X-ray diffraction shows structural correlations from 2 to 6 Å and 15 Å, while small angle neutron scattering indicates that the rare-earth ions do not affect the nanoscale structures of the gels. Differential scanning calorimetry shows the glass transition temperature to increase with concentration of Pr in the gel. Excitation in the ultraviolet region leads to luminescent emission in the visible region. Simultaneous absorption in the visible region then leads to luminescent emission in the near infra-red region. The spectral qualities of the emission bands can be varied by choosing appropriate relative ratios of rare-earth species. (author)

Rare earth mobility in hydrothermal ore-forming systems

International Nuclear Information System (INIS)

Cornell, D.H.; Schade, J.; Scheepers, R.; Watkeys, M.K.

1988-01-01

Rocks and ores which form by magmatic processes display a range of chondrite-normalised rare earth profiles. One REE (rare earth elements) profile feature which seems unrelated to magmatic processes is the birdwing profile, in which both heavy and light rare earths are enriched relative to the middle rare earths. Birdwing rare earth profiles are an easily identified geochemical anomaly. It is proposed that rare earth geochemistry could be applied in geochemical prospecting for ore formed by hydrothermal processes. 5 figs

Optical properties of pure and Ce3+ doped gadolinium gallium garnet crystals and epitaxial layers

International Nuclear Information System (INIS)

Syvorotka, I.I.; Sugak, D.; Wierzbicka, A.; Wittlin, A.; Przybylińska, H.; Barzowska, J.; Barcz, A.; Berkowski, M.; Domagała, J.; Mahlik, S.; Grinberg, M.; Ma, Chong-Geng

2015-01-01

Results of X-ray diffraction and low temperature optical absorption measurements of cerium doped gadolinium gallium garnet single crystals and epitaxial layers are reported. In the region of intra-configurational 4f–4f transitions the spectra of the bulk crystals exhibit the signatures of several different Ce 3+ related centers. Apart from the dominant center, associated with Ce substituting gadolinium, at least three other centers are found, some of them attributed to the so-called antisite locations of rare-earth ions in the garnet host, i.e., in the Ga positions. X-ray diffraction data prove lattice expansion of bulk GGG crystals due to the presence of rare-earth antisites. The concentration of the additional Ce-related centers in epitaxial layers is much lower than in the bulk crystals. However, the Ce-doped layers incorporate a large amount of Pb from flux, which is the most probable source of nonradiative quenching of Ce luminescence, not observed in crystals grown by the Czochralski method. - Highlights: • Ce 3+ multicenters found in Gadolinium Gallium Garnet crystals and epitaxial layers. • High quality epitaxial layers of pure and Ce-doped GGG were grown. • Luminescence quenching of Ce 3+ by Pb ions from flux detected in GGG epitaxial layers. • X-ray diffraction allows measuring the amount of the rare-earth antisites in GGG

Mimicking the magnetic properties of rare earth elements using superatoms.

Science.gov (United States)

Cheng, Shi-Bo; Berkdemir, Cuneyt; Castleman, A W

2015-04-21

Rare earth elements (REs) consist of a very important group in the periodic table that is vital to many modern technologies. The mining process, however, is extremely damaging to the environment, making them low yield and very expensive. Therefore, mimicking the properties of REs in a superatom framework is especially valuable but at the same time, technically challenging and requiring advanced concepts about manipulating properties of atom/molecular complexes. Herein, by using photoelectron imaging spectroscopy, we provide original idea and direct experimental evidence that chosen boron-doped clusters could mimic the magnetic characteristics of REs. Specifically, the neutral LaB and NdB clusters are found to have similar unpaired electrons and magnetic moments as their isovalent REs (namely Nd and Eu, respectively), opening up the great possibility in accomplishing rare earth mimicry. Extension of the superatom concept into the rare earth group not only further shows the power and advance of this concept but also, will stimulate more efforts to explore new superatomic clusters to mimic the chemistry of these heavy atoms, which will be of great importance in designing novel building blocks in the application of cluster-assembled nanomaterials. Additionally, based on these experimental findings, a novel "magic boron" counting rule is proposed to estimate the numbers of unpaired electrons in diatomic LnB clusters.

The Rare Earth Magnet Industry and Rare Earth Price in China

Directory of Open Access Journals (Sweden)

Ding Kaihong

2014-07-01

Full Text Available In the past four years, the price of rare earth metal fluctuates sharply for many reasons. Currently, it has become more stable and more reasonable. This presentation is focused on the effect about the rare earth metal price. Some motor manufacturers have shifted from rare earth permanent magnet to ferrite magnet. Many motor manufacturers changed the design for the motor cooling system to make the motor function at a lower temperature. Thus the consumption of Dy can be markedly reduced. As for manufacturer of NdFeB magnet, we are also trying to optimize our process to reduce to dependence of HREE such as Dy and Tb. HS process have been introduced to solve the problem. With more and more people focusing and engaging on the REE industry, the price of REE will be more transparent without too many fluctuations. China is considering the problems of balancing the environment, energy sources, and labor sources. The application field about NdFeB such as wind turbine generator, HEV/EV, FA /OA is flourishing.

The Rare Earth Magnet Industry and Rare Earth Price in China

Science.gov (United States)

Ding, Kaihong

2014-07-01

In the past four years, the price of rare earth metal fluctuates sharply for many reasons. Currently, it has become more stable and more reasonable. This presentation is focused on the effect about the rare earth metal price. Some motor manufacturers have shifted from rare earth permanent magnet to ferrite magnet. Many motor manufacturers changed the design for the motor cooling system to make the motor function at a lower temperature. Thus the consumption of Dy can be markedly reduced. As for manufacturer of NdFeB magnet, we are also trying to optimize our process to reduce to dependence of HREE such as Dy and Tb. HS process have been introduced to solve the problem. With more and more people focusing and engaging on the REE industry, the price of REE will be more transparent without too many fluctuations. China is considering the problems of balancing the environment, energy sources, and labor sources. The application field about NdFeB such as wind turbine generator, HEV/EV, FA /OA is flourishing.

Rare earth elements behavior in Peruibe black mud

International Nuclear Information System (INIS)

Torrecilha, Jefferson K.; Carvalho, Leandro P.; Gouvea, Paulo F.M.; Silva, Paulo S.C. da

2015-01-01

Rare earth elements in sediments have been used as powerful tools for environmental studies because of their behavior during geochemical processes and are also widely accepted as reliable provenance tracers because they are largely water-immobile and thus behave conservatively during sedimentary processes. The Peruibe Black Mud (PBM) is a sedimentary deposit originated from the interactions of marine sediments and organic matter in an estuarine environment that originates a peloid currently used for medicinal purposes. The objective of this study was to examine rare earth elements pattern distribution in the Peruibe black mud sedimentary deposit as a proxy for its geochemical development. Elemental ratios such as LaN/YbN, Th/U and La/Th were determined and a normalization of the mean rare earth elements concentrations in the samples related to NASC indicates that the light (La to Eu) rare earth elements present values close to the unity while the heavy (Tb to Lu) rare earth elements are depleted related to NASC. It can be observed that the light rare earth elements present enrichment values slightly enriched over the unity while the heavy rare earth elements present values generally below the unity reflecting the enrichment of the light rare earth elements over the heavy rare earth. Rare earth elements concentrations determined in Peruibe black mud samples showed a distribution similar to that found in the NASC for the light rare earth elements and depleted for the heavy rare earth elements. (author)

Rare earth elements behavior in Peruibe black mud

Energy Technology Data Exchange (ETDEWEB)

Torrecilha, Jefferson K.; Carvalho, Leandro P.; Gouvea, Paulo F.M.; Silva, Paulo S.C. da, E-mail: jeffkoy@usp.br [Instituto de Pesquisas Energeticas e Nucleares (IPEN/CNEN-SP), Sao Paulo, SP (Brazil)

2015-07-01

Rare earth elements in sediments have been used as powerful tools for environmental studies because of their behavior during geochemical processes and are also widely accepted as reliable provenance tracers because they are largely water-immobile and thus behave conservatively during sedimentary processes. The Peruibe Black Mud (PBM) is a sedimentary deposit originated from the interactions of marine sediments and organic matter in an estuarine environment that originates a peloid currently used for medicinal purposes. The objective of this study was to examine rare earth elements pattern distribution in the Peruibe black mud sedimentary deposit as a proxy for its geochemical development. Elemental ratios such as LaN/YbN, Th/U and La/Th were determined and a normalization of the mean rare earth elements concentrations in the samples related to NASC indicates that the light (La to Eu) rare earth elements present values close to the unity while the heavy (Tb to Lu) rare earth elements are depleted related to NASC. It can be observed that the light rare earth elements present enrichment values slightly enriched over the unity while the heavy rare earth elements present values generally below the unity reflecting the enrichment of the light rare earth elements over the heavy rare earth. Rare earth elements concentrations determined in Peruibe black mud samples showed a distribution similar to that found in the NASC for the light rare earth elements and depleted for the heavy rare earth elements. (author)

Transport properties of the rare earth disordered systems (R1-xYbx)Ba2Cu3O7 (R = Y, Sm)

International Nuclear Information System (INIS)

Hwang, J.R.; Tai, M.F.; Ku, H.C.; Lii, K.H.

1989-01-01

Electrical and magnetic measurements have been carried out for the rare earth disordered superconducting copper oxide systems (Y 1-x Yb x )Ba 2 Cu 3 O 7 (substitution with large rare earth mass difference) and (Sm 1-x Yb x )Ba 2 Cu 3 O 7 (substitution with large rare earth ionic size difference). Effect of compositional variation upon room temperature electrical resistivity shows no disorder scattering contribution from the randomly distributed rare earth ions located on the (1/2, 1/2, 1/2) site of the space group Pmmm. This result indicates very low conduction electron density of states surrounding rare earth ions. On the contrary, negative deviation of electrical resistivity from the linear Vegard law was observed. This reduced conduction electron scattering was discussed through the variation of packing density, grain size and/or twin structure

High-resolution laser spectroscopy of rare-earth doped insulators: a personal perspective

International Nuclear Information System (INIS)

Macfarlane, Roger M.

2002-01-01

I offer some reflections on the past three decades of high-resolution spectroscopy of rare-earth ions in solids which was ushered in by the development of tunable lasers in the mid 1970s. A brief review is given of some of the accomplishments in the area of spectral hole-burning and coherent transient spectroscopy, emphasizing work with which the author has been associated. Spectral hole-burning has been characterized by a richness of mechanisms. These include population storage in nuclear-spin and electron-spin Zeeman sub-levels, hyperfine and superhyperfine levels and metastable optical levels with corresponding hole lifetimes from many hours to microseconds. In addition, persistent hole-burning has been seen in disordered materials and in those showing photo-ionization or photo-chemistry following excitation into zero-phonon lines. This has made hole-burning a generally useful technique for the measurement of magnetic and electric dipole moments, hyperfine interactions, spin relaxation and thermally induced line-broadening. Photon-echoes have proven to be the prime source of coherence-time information and coherence times as long as several milliseconds corresponding to optical resonance widths of less than 100 Hz have been reported. Tables summarizing these results and providing references to original work are included

Elastic, thermal and high pressure structural properties of heavy rare earth antimonides

International Nuclear Information System (INIS)

Soni, P.; Pagare, G.; Sanyal, S.P.

2009-01-01

Pressure induced structural phase transition of two heavy rare earth antimonides (RESb; RE=Ho, Er) have been studied theoretically by using an inter-ionic potential theory. This method has been found quite satisfactory in the case of pnictides of rare earth and describes the crystal properties in the framework of rigid-ion modal. The long-range Coulomb interaction, short-range repulsive interaction and van der Waals (vdW) interactions are properly incorporated in this theory. These compounds exhibit first order crystallographic phase transition from their NaCl-type structure to CsCl-type structure at 27 GPa and 33.2 GPa, respectively. The bulk moduli of RESb compounds are compared with the experimental values of elastic constants. We have also calculated the Debye temperature by incorporating the elastic constants for both the rare earth antimonides. (author)

Rare Earth Metals: Resourcefulness and Recovery

Science.gov (United States)

Wang, Shijie

2013-10-01

When we appreciate the digital revolution carried over from the twentieth century with mobile communication and the Internet, and when we enjoy our high-tech lifestyle filled with iDevices, hybrid cars, wind turbines, and solar cells in this new century, we should also appreciate that all of these advanced products depend on rare earth metals to function. Although there are only 136,000 tons of annual worldwide demand, (Cho, Rare Earth Metals, Will We Have Enough?)1 rare earth metals are becoming such hot commodities on international markets, due to not only to their increasing uses, including in most critical military hardware, but also to Chinese growth, which accounts for 95% of global rare earth metal production. Hence, the 2013 technical calendar topic, planned by the TMS/Hydrometallurgy and Electrometallurgy Committee, is particularly relevant, with four articles (including this commentary) contributed to the JOM October Issue discussing rare earth metals' resourcefulness and recovery.

PIXE studies on elemental characterization of offset printing ink tagged with rare-earth taggants

International Nuclear Information System (INIS)

Joseph, D.; Saxena, A.; Choudhury, R.K.; Maind, S.D.

2007-01-01

Proton Induced X-ray Emission Technique (PIXE) has been used for elemental characterization of offset printing ink tagged with rare-earth taggants, with a proton beam of energy 4 MeV at Folded Tandem Ion Accelerator (FOTIA) at BARC, Trombay, Mumbai, India. The offset printing ink was tagged with rare-earth (La, Pr, Nd, Sm, Eu and Gd) thenoyltrifluoroacetonate chelates at about 1000 ppm level for each element separately. Small aliquots (approximately 20 mg) of tagged inks were coated on paper supports and then analyzed. Well-resolved rare-earth L X-rays were detected using a high resolution Si(Li) detector. Satisfactory results to identify and quantify the taggants were achieved. (author)

Mass-spectrometric investigation of rare earth acetylacetonates dipivaloylmethanates and their adducts

International Nuclear Information System (INIS)

Gavrishzhuk, E.M.; Dzyubenko, N.G.; Martynenko, L.I.

1985-01-01

Peculiarities of fragmentation of molecular ions of rare earth acetylacetonates and dipivaloylmethanates under mass-spectrometric investigation of these compounds as well as their adducts with o-phenanthroline, α,α'-dipyridyl, triphenylphosphine oxide are considered in the given review. Similar data for identical derivants of some transitions metals are presented. Data on potentials of appearance and dissociation energy of basic ions in mass-spectra of the studied β-diketonates are analyzed

Preparation of rare earth fluorides from apatite concentrate