Degradation behavior of PVC film in aqueous solution at elevated temperatures

Energy Technology Data Exchange (ETDEWEB)

Shin, Shun-Myung; Kim, Jong-Hwa; Lee, Soo [Changwon National University, Changwon(Korea)

2001-02-28

The heat treatment of PVC film containing PVC 65%, DOP (Dioctyl Phthalate) 32% as plasticizer, Ca-Zn stearates and surface agent was performed under several conditions to study the dehydrochlorination of PVC and char production. In the case of H{sub 2}SO{sub 4}, the dehydrochlorination was ca.100% at 250 deg.C for 3h. The char involving the smaller pores was produced with hydrothermal treatment. The pore size became small with increasing the treatment time and temperature. In the case of treatment with Ca(OH){sub 2}, the sizes of pores produced in char were about sever {approx}10 {mu}m at 225 deg.C for 12h. In the case of H{sub 2}SO{sub 4}, the size of pores were about 1 {mu}m in 5M H{sub 2}SO{sub 4} for 12h. (author). 6 refs., 3 tabs., 11 figs.

Migration from PVC cling films compared with their field of application

DEFF Research Database (Denmark)

Petersen, Jens Højslev; Lillemark, L.; Lund, L.

1997-01-01

Samples of PVC cling films were taken at importers, wholesalers and retail shops, and their overall migration to the alternative food simulant iso-octane was measured, after establishment of a correlation between overall migration to olive oil at 40 degrees C in 10 days and to iso-octane in 2 h...

Biodegradation of blend films PVA/PVC, PVA/PCL in soil and soil with landfill leachate

Directory of Open Access Journals (Sweden)

Adriana de Campos

2011-12-01

Full Text Available This study investigated the biodegradation of blends films of poly(vinyl alcohol/poly(vinyl chloride (PVA/PVC and poly(vinyl alcohol/poly(caprolactone (PVA/PCL blends films prepared with dimethylformamide under a variety of conditions by respirometry, spectrophotometry (FTIR, scanning electron microscopy (SEM, and contact angle. The films were buried in the garden soil and in the soil mixed with the landfill leachate for 120 days at 28ºC. Significant levels of biodegradation were achieved in fairly short incubation times in the soil. The results indicated that PVA was the most biodegradable film in the soil and in the soil with the leachate.

The overall heat transfer of greenhouses covered with PE [polyethylene film] and PVC [polyvinyl chloride film] single layer: The heat insulation efficiency of greenhouses and their covering materials (1)

International Nuclear Information System (INIS)

Minagawa, H.; Tachibana, K.

1982-01-01

Overall heat transfer of polyethylene film (PE) and polyvinyl chloride film (PVC) were measured in the experimental greenhouses with hot-air heaters on the clear and on the cloudy nights during the period Nov. 1979 to Jan. 1980. Both films are 0.1 mm thick and have different physical properties for long-wave radiation. The heat insulation efficiency of the greenhouses covered with PE and PVC single layer was investigated, and the ratio of floor area to covering area for the experimental greenhouses, which is one of the indices for the heat insulation efficiency of greenhouses, was also taken into consideration. The results are as follows: 1. Using the ratio of the overall heat transfer and the overall heat transfer coefficients for the heat insulation efficiency, the PE-house revealed to be less efficient than the PVC-house. This can be due to PE being more transparent to long-wave radiation than PVC. The advantage in the PVC-house, however, decreased with the increasing of the inside-outside air temperature difference (Figs. 3 and 5). 2. The overall heat transfer coefficients of both greenhouses depended on the inside-outside temperature difference. As the temperature difference increased, the overall heat transfer coefficients decreased (Fig. 5). 3. The overall heat transfer coefficients of both greenhouses were smaller on the cloudy nights than that on the clear nights. When the condensation occurred at the interior film surface, the heat insulation efficiency of both greenhouses was increased, resulting in the decrease of the coefficient. The efficiency of the PE-house was more affected than the PVC-house when the condensation occurred (Figs. 6 and 7). 4. When the inside-outside air temperature difference was small, convective heat transferred from the outside air to the outside cover surface. With an increase in the inside-outside air temperature difference, convective heat flow occurred from the outside cover surface to the outside air. This phenomenon was

Photostabilizing Efficiency of PVC in the Presence of Schiff Bases as Photostabilizers

Directory of Open Access Journals (Sweden)

Emad Yousif

2015-11-01

Full Text Available The photostabilization of polyvinyl chloride (PVC films by Schiff bases was investigated. Polyvinyl chloride films containing 0.5 wt % Schiff bases were produced using the same casting method as that used for additive-free PVC films from tetrahydrofuran (THF solvent. The photostabilization activities of these compounds were determined by monitoring the carbonyl, polyene and hydroxyl indices with irradiation time. The changes in viscosity average molecular weight of PVC with irradiation time were also monitored using THF as a solvent. The quantum yield of chain scission (Φcs for the studied complexes in PVC was estimated to range between 4.72 and 8.99 × 10−8. According to the experimental results, several mechanisms were suggested, depending on the structure of the additive. Ultra violet (UV absorption, peroxide decomposition and radical scavenging were suggested as the photostabilizing mechanisms.

The development of PVC-laminated steel sheet by an electron beam curing method

International Nuclear Information System (INIS)

Masuhara, Ken-ichi; Koshiishi, Kenji; Tomosue, Takao; Mori, Koji; Honma, Nobuyuki

1988-01-01

Polyvinyl chloride (PVC) film-laminated steel sheets are used for household electric appliances and building materials. Those are produced usually by pressing a PVC film onto a steel sheet imediately after a themosetting adhesive has been applied to the sheet and curing. However, a major problem of this method is that the appearance of the PVC films such as gloss and embossment changes during pressing due to the heat that is required for causing bonding, therefore, the development of an adhesive which can be cured at lower temperature is necessary. Nisshin Steel Co., Ltd. has developed PVC film-laminated steel sheets for which electron beam (EB) curable adhesives are used to overcome this problem. The advantage of these adhesives is that they can be quickly cured at room temperature. The production procedure of PVC-laminated steel sheets by EB curing is outlined. But this method has encountered two problems: poor adhesion between substrates and adhesive due to the residual stress, and the deterioration of the PVC films due to EB irradiation. EB curable adhesives are mainly composed of acrylic ester oligomers and monomers, and thier adhesion was improved by organic pretreatment. On the other hand, EB-proof PVC films were developed. The general properties of PVC-laminated steel sheets produced by EB curing are reported. (K.I.)

Controle Sanitário de Filmes Flexíveis de PVC Comercializados no Estado do Rio de Janeiro | Sanitary Control of Flexible PVC films Commercialized in the State of Rio de Janeiro

Directory of Open Access Journals (Sweden)

Fabio Silvestre Bazilio

2015-08-01

Full Text Available Foram analisadas trinta e sete amostras de filme flexível de PVC quanto à migração específica dos plastificantes ftalato de di-(2-etil-hexila – DEHP (Nº CAS 117-81-7 e adipato de di-(2-etil-hexila – DEHA (Nº CAS 103-23-1 da embalagem para alimentos gordurosos, utilizando-se simulante. A Resolução nº 17, de 17 de março de 2008, publicada pela ANVISA, estabelece limite de migração específica para DEHP de 1,5 mg kg-1 do simulante e para o DEHA em 18 mg kg-1 do simulante. O teste de migração foi realizado por meio do contato entre 1 dm2 do filme de PVC e 100 mL de simulante de alimento, solução de etanol a 95% (v/v, por 48 h a 20ºC. As migrações dos plastificantes DEHP e DEHA foram determinadas por cromatografia a gás com detecção por ionização em chama e coluna de sílica fundida recoberta internamente com fase estacionária constituída de 5% fenilmetilsilicone. As amostras apresentaram resultados para a migração específica de DEHP entre não detectável (< 0,35 mg kg-1 e 304 mg kg-1 de simulante de alimentos e entre não detectável (< 2,23 mg kg-1 e 231 mg kg-1 de simulante de alimentos para o DEHA. Dentre as amostras ensaiadas, 95% apresentaram resultado insatisfatório para pelo menos um dos plastificantes. ----------------------------------------------------------------------------------------------- In total, 37 samples of flexible PVC films were analyzed for specific migration of di-(2-ethylhexyl phthalate (DEHP and di-(2-ethylhexyl adipate (DEHA from packaging to fatty foods, using simulant. The Resolution n. 17, of March 17, 2008, published by ANVISA, establishes specific migration limits for DEHP in 1.5 mg kg−1 of simulant and for DEHA in 18 mg kg−1 of simulant. The migration test was performed through contact between a 1-dm2 PVC film cutout and 100 mL of food simulant, ethanol 95% (v/v, for 48 h at 20ºC. The migrations of DEHP and DEHA were determined by gas chromatography with a flame ionization

Degradation of PVC/rPLA Thick Films in Soil Burial Experiment

Science.gov (United States)

Nowak, Bożena; Rusinowski, Szymon; Chmielnicki, Blazej; Kamińska-Bach, Grażyna; Bortel, Krzysztof

2016-10-01

Some of the biodegradable polymers can be blended with a synthetic polymer to facilitate their biodegradation in the environment. The objective of the study was to investigate the biodegradation of thick films of poly(vinyl chloride)/recycled polylactide (PVC/rPLA). The experiments were carried out in the garden soil or in the mixture of garden soil and hydrocarbon-contaminated soil under laboratory conditions. Since it is widely accepted that the biosurfactants secreted by microorganisms enable biotransformation of various hydrophobic substances in the environment, it was assumed that the use of contaminated soil, rich in biosurfactant producing bacteria, may accelerate biodegradation of plastics. After the experimental period, the more noticeable weight loss of polymer films was observed after incubation in the garden soil. However, more pronounced changes in the film surface morphology and chemical structure as well as decrease of tensile strength were observed after incubation of films in the mixture of garden and contaminated soil. It turned out that as a result of competition between two distinct groups of microorganisms present in the mixture of garden and hydrocarbon-contaminated soils the number of microorganisms and their activity were lower than the activity of indigenous microflora of garden soil as well as the amount of secreted biosurfactants towards plastics.

PVC cling film in contact with cheese: health aspects related to global migration and specific migration of DEHA

DEFF Research Database (Denmark)

Petersen, Jens Højslev; Naamansen, Ebbe Tubæk; Nielsen, Preben Aagård

1995-01-01

experiment samples of cheese of the types most commonly consumed in Denmark were wrapped in this 'low migration' PVC film using a procedure simulating the actual pattern of use in retail shops. After a storage time of 2 h at 5 degrees C the level of DEHA was 45 mg/kg of cheese, which after 10 days increased...... of DEHA close to or above the tolerable daily intake of 0.3 mg/kg body weight as defined by the EEC Scientific Committee for Food. Furthermore, it is stressed that measurements of global migration followed by uncritical use of reduction factors may result in erroneous evaluation of the suitability of DEHA-plasticized......Following exposure to the food simulant olive oil for 10 days at 5, 20 or 40 degrees C a global migration ranging from 20 to 30 mg/dm(2) was detected from a common 'low migration' PVC film plasticized with a mixture of di-(ethylhexyl)adipate (DEHA) and a polymeric plasticizer. In a laboratory...

A reciclagem de PVC no Brasil

OpenAIRE

Piva,Ana Magda; Bahiense Neto,Miguel; Wiebeck,Hélio

1999-01-01

Esta pesquisa discute as possibilidades práticas da reciclagem de PVC. Na reciclagem de polímeros, a do PVC representa uma importante parcela. PVC é um polímero que é usado em uma ampla faixa de produtos: filmes, fios, cabos, em compostos para uma variedade de formas. A reciclagem é uma técnica vantajosa, capaz de reproduzir as propriedades do polímero original, no polímero reciclado e isto em condições razoavelmente econômicas. A tecnologia brasileira, em relação a produtos reciclados, apres...

Utilização de filmes plásticos e comestíveis na conservação pós-colheita de melão amarelo Utilization of PVC film and edible films to extend the postharvest conservation of yellow melons

Directory of Open Access Journals (Sweden)

Patrício F Batista

2007-12-01

Full Text Available Este trabalho teve como objetivo prolongar a vida pós-colheita de melões do tipo amarelo cv. AF-682, por meio da atmosfera modificada obtida com filme plástico de PVC e filmes comestíveis à base de cera de carnaúba (50% e fécula de mandioca (1, 2 e 3%. Para o revestimento dos frutos com embalagem plástica utilizou-se filme de PVC com 10 mm de espessura, aderente e esticável, colocado em camada única, na superfície de cada fruto. Após serem revestidos pelos filmes os frutos foram armazenados em temperatura ambiente de 29± 2ºC e 64±1% UR por 20 dias, sendo em intervalos de cinco dias submetidos às avaliações: massa individual, firmeza da polpa, teor de sólidos solúveis totais, acidez titulável e pH. Utilizou-se delineamento inteiramente casualizado com seis repetições em esquema fatorial 6x4, sendo 6 tratamentos de conservação e 4 períodos de armazenamento. Nenhum dos tratamentos avaliados é recomendável para aumentar a conservação pós-colheita de melão amarelo. Os frutos revestidos com fécula de mandioca a 3% e filme de PVC apresentaram processo iniciais característicos de fermentação e podridão a partir de 15 dias de armazenamento em temperatura ambiente.This work aimed to extend the postharvest life of yellow melons cv. AF-682 through modified atmosphere techniques obtained with PVC film and edible films such as carnauba wax (50% and cassava starch (1, 2 and 3%. Fruits were wrapped with one layer of adherent and stretchable PVC film with 10 mm width. After covering, fruits were stored at 29± 2ºC and 64±1% UR for 20 days. At a 5-day interval, fruits were evaluated for individual weight, pulp firmness, total soluble solids content, titratable acidity and pH. The trial was carried out in a complete randomized design, with six replications in a factorial scheme 6x4, with six treatments and four storage periods. The use of PVC film and edible films are not recommended to extend postharvest conservation of

Chalk effect on PVC cross-linking under irradiation

International Nuclear Information System (INIS)

Chudinova, V.V.; Guzeev, V.V.; Mozzhukhin, V.B.; Pomerantseva, Eh.G.; Nozrina, F.D.; Zhil'tsov, V.V.; Zubov, V.P.

1994-01-01

Effect of nonmodified and modified chalk on curing degree of polymer matrix was studied under-irradiation of PVC-compositions. Films of the compositions (100 mass part 7 PVC, 0-100 mas.part of chalk, 2.5 - lead sulfate, 1.5 - lead stearate and 0.3 - glycerin) were irradiated up to absorbed dose 0.1 MGy in an inert medium. Content of gel-fraction after boiling in THF was determined with use of IR spectroscopy. It was established, that intensive dehydrochlorination and polymer curing took place on chalk particle surface. Network fixed strongly chalk particles. However, chalk inhibited processes of dehydrochlorination and PVC curing, increasing amount of noncured PVC in polymer matrix

Effects of 60 MeV C5+ ion irradiation on PmT-PVC and p-TSA doped PoT-PVC blends

International Nuclear Information System (INIS)

Lakshmi, G.B.V.S.; Siddiqui, Azher M.; Ali, Vazid; Kulriya, Pawan K.; Zulfequar, M.

2008-01-01

Poly(m-toluidine) (PmT) and Poly(o-toluidine) (PoT) have been synthesized from derivatives of aniline (m-toluidine), (o-toluidine) monomers by chemical oxidative polymerization method. After polymerization, PoT powder was doped with p-toluene sulphonic acid (p-TSA) and the polymer powders were blended with poly vinyl chloride (PVC) to achieve PmT and p-TSA doped PoT dispersed films. XRD, FTIR and UV-visible studies were carried out to get their structural changes and optical information. These blends were irradiated by 60 MeV C 5+ ions with different fluences. Post Irradiation XRD, FTIR and UV-visible spectroscopy were also performed on all films. On p-TSA doped PoT-PVC blends dc-conductivity measurements are also carried out before and after irradiation. The results show structural modifications which lead to changes in optical and electrical properties

Structural, optical and thermal characterization of PVC/SnO2 nanocomposites

Science.gov (United States)

Taha, T. A.; Ismail, Z.; Elhawary, M. M.

2018-04-01

The structural, optical, and thermal properties of PVC/SnO2 nanocomposites were investigated. XRD patterns were used to explore the structures of these prepared samples. Optical UV-Vis measurements were analyzed to calculate the spectroscopic optical constants of the prepared PVC/SnO2 nanocomposites. Both direct and indirect optical band gaps decreased with increasing SnO2 content. The refractive index, high frequency dielectric constant, plasma frequency, and optical conductivity values increased with SnO2. The single oscillator energy increased from 5.64 to 10.97 eV and the dispersion energy increased from 6.35 to 19.80 eV with the addition of SnO2. The other optical parameters such as optical moments, single oscillator strength, volume energy loss, and surface energy loss were calculated for different SnO2 concentrations. Raman spectra of the PVC/SnO2 nanocomposite films revealed the characteristic vibrational modes of PVC and surface phonon modes of SnO2. The thermal stability of PVC/SnO2 nanocomposite films was studied using DTA and thermogravimetric analysis. The glass transition ( T g) values abruptly changed from 46 °C for PVC to an average value of 59 °C for the polymer films doped with 2.0, 4.0, and 6.0 wt% SnO2. The weight loss decreased as the SnO2 concentration increased in the temperature range of 350-500 °C, corresponding to enhanced thermal stability.

Hoechst and Wacker plan joint venture in PVC

International Nuclear Information System (INIS)

Young, I.

1992-01-01

Restructuring of Europe's petrochemical industry has taken a further step with the announcement that Hoechst (Frankfurt) and Wacker Chemie (Munich) are planning a joint venture in polyvinyl chloride (PVC). The venture would include production, R ampersand D, sales and marketing, plus both companies' PVC recycling activities. However, their vinyl chloride monomer (VCM) plants, and Hoechst's Kalle PVC film business, have been left out. Erich Schnitzler, head of Hoechst's PVC business unit, does not anticipate problems with the European Community's competition directorate. We are both among the middle-sized European PVC producers, and together we would have a 9%-10% market share. Our joint venture would not limit competition. Both partners are hoping for approval from Brussels in first-quarter 1993. Hoechst has 255,000 m.t./year of PVC capacity at Gendorfand Knapsack, while Wacker has 365,000 m.t./year at Burghausen and Cologne. All the units, except Wacker's Cologne plant, are back integrated to VCM. The joint venture would buy VCM from the two parent companies and on the merchant market

Mechanical behavior of styrene grafted PVC films by electron beam irradiation

International Nuclear Information System (INIS)

Cardoso, Jessica R.; Moura, Eduardo; Somessari, Elisabeth S.R.; Silveira, Carlos G.; Paes, Helio A.; Souza, Carlos A.; Manzoli, Jose E.; Geraldo, Aurea B.C.

2011-01-01

The polyvinyl chloride (PVC) is a technological and low cost polymer, however it presents high sensitivity to high energy irradiation because of the weakness of carbon-chloride bond face to carbon-carbon and carbon-hydrogen bonds. Grafting is a type of co-polymerization process that can allow it an increase of mechanical characteristics. The aim of this work is to evaluate the mechanical properties of styrene grafted PVC by electron beam irradiation using mutual and pre-irradiation methods to verify the mechanical resistance changes of obtained product whether grafting process is applied from non-irradiated or from pre-irradiated substrates. The irradiation procedures were performed in atmosphere air or inert atmosphere and the irradiation conditions comprised doses from 10 kGy to 100 kGy and dose rates of 2.2 kGy/s and 22.4 kGy/s. The styrene grafted samples were analyzed by gravimetry to determinate the grafting yield; the final values have been averaged from a series of three measurements. The Mid-A TR-FTIR was the spectrophotometer technique used for qualitative/semi-quantitative analysis of grafted samples. The Young's module and tensile strength of pre-irradiated and grafted PVC samples at both methods were measured at a Lloyd LXR tensile tester at a cross-head speed of 10.00 mm/min. We observed the decrease of Young's module and tensile strength with the increase of absorbed dose at pre-irradiated PVC samples. These mechanical parameters results are discussed. (author)

Designed biocompatible nano-inhibitor based on poly(β-cyclodextrin-ester) for reduction of the DEHP migration from plasticized PVC.

Science.gov (United States)

Raeisi, Ahmad; Faghihi, Khalil; Shabanian, Meisam

2017-10-15

The easy migration of di(2-ethylhexyl) phthalate (DEHP) from the plasticized PVC (P-PVC) poses a serious threat to human health and the ecosystems. Thus, its control migration from the P-PVC products is very important. In this work, a poly(β-cyclodextrin-ester) network (β-CDP) was synthesized via reaction of β-cyclodextrin with 3,3',4,4'-benzophenone tetracarboxylic dianhydride. As a potential inhibitor for reduction of the DEHP migration, the β-CDP was grafted to Fe 3 O 4 nanoparticles. Poly(β-cyclodextrin-ester) functionalized Fe 3 O 4 nanoparticles (MNP-CDP) has been used in PVC/DEHP system as a reactive nano-inhibitor to reduce DEHP migration. Thermal stability and mechanical properties of obtained films were investigated. DEHP migration tests of the P-PVC films were also carried out by using Gas chromatography. It was found that by incorporating the small amounts of nano-inhibitor in PVC/DEHP system, the migration of DEHP effectively reduced from the P-PVC samples about 65% without any serious changes in mechanical and thermal properties of the P-PVC films. Copyright © 2017 Elsevier Ltd. All rights reserved.

Migration of dioctyladipate plasticizer from food-grade PVC film into chicken meat products: effect of gamma-radiation

International Nuclear Information System (INIS)

Goulas, A.E.; Kontominas, M.G.

1996-01-01

Food-grade PVC film containing 28.3% dioctyladipate (DOA) plasticizer was used to wrap chicken meat samples, with and without skin, contained in a polystyrene tray. Samples were then irradiated with gamma-radiation [60Co] at doses equal to 4 kGy and 9 kGy corresponding to ''cold pasteurization''. Irraddiation was carried out at 8-10 degrees C and samples were subsequently stored at 4-5 degrees C. Contaminated chicken meat samples were analysed for DOA at intervals between 7 h and 240 h of contact, using an indirect GC method. Identical non-irradiated (control) samples were also analysed for their DOA content. Results showed no statistically significant differences in migrated amounts of DOA between irradiated and non-irradiated samples. Neither were differences observed between samples irradiated at 4 kGy and 9 kGy. This was supported by identical IR spectra recorded for irradiated and non-irradiated samples and leads to the conclusion that, at such intermediate radiation doses ( < or = kGy), the migration characteristics of PVC film are not affected. DOA migration was found to be time dependent, approaching equilibrium after approximately 170 h for the chicken flesh plus skin samples and 120 h for the chicken flesh samples. The amount of DOA migrated into chicken flesh plus skin samples was significantly greater (3.2-22.3 mg/dm2) than that for chicken flesh samples (0.9-8.9 mg/dm2). After 240 h of sample/film contact under refrigeration, loss of DOA was approximately 35.6% for chicken flesh plus skin samples and 14.3% for chicken flesh samples. Sample spoilage, as demonstrated by off-odour development, occurred after approximately 120 h of refrigerated storage. Diffusion coefficients for DOA were calculated and were found to be lower for chicken flesh (1 x 10(-13) than for flesh plus skin (4.4 x 10(-13)) samples

Cell Adhesion to Plasma-Coated PVC

Directory of Open Access Journals (Sweden)

Elidiane C. Rangel

2014-01-01

Full Text Available To produce environments suitable for cell culture, thin polymer films were deposited onto commercial PVC plates from radiofrequency acetylene-argon plasmas. The proportion of argon in the plasmas, PAr, was varied from 5.3 to 65.8%. The adhesion and growth of Vero cells on the coated surfaces were examined for different incubation times. Cytotoxicity tests were performed using spectroscopic methods. Carbon, O, and N were detected in all the samples using XPS. Roughness remained almost unchanged in the samples prepared with 5.3 and 28.9% but tended to increase for the films deposited with PAr between 28.9 and 55.3%. Surface free energy increased with increasing PAr, except for the sample prepared at 28.9% of Ar, which presented the least reactive surface. Cells proliferated on all the samples, including the bare PVC. Independently of the deposition condition there was no evidence of cytotoxicity, indicating the viability of such coatings for designing biocompatible devices.

Mechanical behavior of styrene grafted PVC films by electron beam irradiation

Energy Technology Data Exchange (ETDEWEB)

Cardoso, Jessica R.; Moura, Eduardo; Somessari, Elisabeth S.R.; Silveira, Carlos G.; Paes, Helio A.; Souza, Carlos A.; Manzoli, Jose E.; Geraldo, Aurea B.C., E-mail: ageraldo@ipen.br, E-mail: jmanzoli@ipen.br [Instituto de Pesquisas Energeticas e Nucleares (IPEN/CNEN-SP), Sao Paulo, SP (Brazil)

2011-07-01

The polyvinyl chloride (PVC) is a technological and low cost polymer, however it presents high sensitivity to high energy irradiation because of the weakness of carbon-chloride bond face to carbon-carbon and carbon-hydrogen bonds. Grafting is a type of co-polymerization process that can allow it an increase of mechanical characteristics. The aim of this work is to evaluate the mechanical properties of styrene grafted PVC by electron beam irradiation using mutual and pre-irradiation methods to verify the mechanical resistance changes of obtained product whether grafting process is applied from non-irradiated or from pre-irradiated substrates. The irradiation procedures were performed in atmosphere air or inert atmosphere and the irradiation conditions comprised doses from 10 kGy to 100 kGy and dose rates of 2.2 kGy/s and 22.4 kGy/s. The styrene grafted samples were analyzed by gravimetry to determinate the grafting yield; the final values have been averaged from a series of three measurements. The Mid-A TR-FTIR was the spectrophotometer technique used for qualitative/semi-quantitative analysis of grafted samples. The Young's module and tensile strength of pre-irradiated and grafted PVC samples at both methods were measured at a Lloyd LXR tensile tester at a cross-head speed of 10.00 mm/min. We observed the decrease of Young's module and tensile strength with the increase of absorbed dose at pre-irradiated PVC samples. These mechanical parameters results are discussed. (author)

Effect of oil extracted from coffee grounds in the radiolytic stabilization of PVC

International Nuclear Information System (INIS)

Lima, Thaysa Araujo de; Aquino, Katia Aparecida da Silva; Araujo, Elmo S.

2013-01-01

Commercial Poly(vinyl chloride) (PVC) containing oil extracted from coffee grounds (OCG) at concentrations of 0.50; 1.00 and 1.50 wt% were investigated. The samples were irradiated with gamma radiation ( 60 Co) at room temperature and air atmosphere. The viscosity-average molar mass (M v ) was measured for PVC systems without and with oil. Decreases in molar mass observed when the systems were gamma irradiated reflect the random scission effects that take place in the main chain. Degradation index (DI) value was also obtained by viscosity analysis. DI results showed that the addition of OCG at 0.5 wt% into PVC matrix irradiated at dose of 25 kGy decreased the number of main chain scissions and was calculated a protection index of 67% in PVC matrix. Results about the free radical scavenger action of the OCG were obtained by use of 2,2-diphenyl-1-(2,4,6-trinitrophenyl)-hydrazyl radical (DPPH) and are discussed in this study. Decrease of 7% of Young's modulus value and a decrease of 31.5% on the elongation at break value were recorded for PVC films exposed to gamma irradiation. However, no significant changes were recorded in mechanical properties of PVC with OCG. (author)

Effect of oil extracted from coffee grounds in the radiolytic stabilization of PVC

Energy Technology Data Exchange (ETDEWEB)

Lima, Thaysa Araujo de; Aquino, Katia Aparecida da Silva; Araujo, Elmo S., E-mail: aquino@ufpe.br [Universidade Federal de Pernambuco (UFPE), Recife, PE (Brazil). Dept. de Energia Nuclear

2013-07-01

Commercial Poly(vinyl chloride) (PVC) containing oil extracted from coffee grounds (OCG) at concentrations of 0.50; 1.00 and 1.50 wt% were investigated. The samples were irradiated with gamma radiation ({sup 60}Co) at room temperature and air atmosphere. The viscosity-average molar mass (M{sub v}) was measured for PVC systems without and with oil. Decreases in molar mass observed when the systems were gamma irradiated reflect the random scission effects that take place in the main chain. Degradation index (DI) value was also obtained by viscosity analysis. DI results showed that the addition of OCG at 0.5 wt% into PVC matrix irradiated at dose of 25 kGy decreased the number of main chain scissions and was calculated a protection index of 67% in PVC matrix. Results about the free radical scavenger action of the OCG were obtained by use of 2,2-diphenyl-1-(2,4,6-trinitrophenyl)-hydrazyl radical (DPPH) and are discussed in this study. Decrease of 7% of Young's modulus value and a decrease of 31.5% on the elongation at break value were recorded for PVC films exposed to gamma irradiation. However, no significant changes were recorded in mechanical properties of PVC with OCG. (author)

Electrospinning of PVC with natural rubber

Science.gov (United States)

Othman, Muhammad Hariz; Mohamed, Mahathir; Abdullah, Ibrahim

2013-11-01

Polyvinyl chloride (PVC) was mixed with natural rubbers which are liquid natural rubber (LNR), liquid epoxidised natural rubber (LENR) and liquid epoxidised natural rubber acrylate (LENRA) for a preparation of a fine non-woven fiber's mat. PVC and each natural rubbers(PVC:LENR, PVC:LNR and PVC:LENRA) were mixed based on ratio of 70:30. Electrospinning method was used to prepare the fiber. The results show that the spinnable concentration of PVC/ natural rubber/THF solution is 16 wt%. The morphology, diameter, structure and degradation temperature of electrospun fibers were investigated by scanning electron microscopy (SEM) and thermogravimetric analysis (TGA). SEM photos showed that the morphology and diameter of the fibers were mainly affected by the addition of natural rubber. TGA results suggested that PVC electrospun fiber has higher degradation temperature than those electrospun fibers that contain natural rubber.

Electrospinning of PVC with natural rubber

International Nuclear Information System (INIS)

Othman, Muhammad Hariz; Abdullah, Ibrahim; Mohamed, Mahathir

2013-01-01

Polyvinyl chloride (PVC) was mixed with natural rubbers which are liquid natural rubber (LNR), liquid epoxidised natural rubber (LENR) and liquid epoxidised natural rubber acrylate (LENRA) for a preparation of a fine non-woven fiber’s mat. PVC and each natural rubbers(PVC:LENR, PVC:LNR and PVC:LENRA) were mixed based on ratio of 70:30. Electrospinning method was used to prepare the fiber. The results show that the spinnable concentration of PVC/ natural rubber/THF solution is 16 wt%. The morphology, diameter, structure and degradation temperature of electrospun fibers were investigated by scanning electron microscopy (SEM) and thermogravimetric analysis (TGA). SEM photos showed that the morphology and diameter of the fibers were mainly affected by the addition of natural rubber. TGA results suggested that PVC electrospun fiber has higher degradation temperature than those electrospun fibers that contain natural rubber

Electrospinning of PVC with natural rubber

Energy Technology Data Exchange (ETDEWEB)

Othman, Muhammad Hariz; Abdullah, Ibrahim [Department of Chemistry, Faculty of Science and Technology, Universiti Kebangsaan Malaysia, 43600 Bangi, Selangor (Malaysia); Mohamed, Mahathir [Radiation Processing Technology Division (BTS), Malaysian Nuclear Agency, Bangi, 43000, Kajang (Malaysia)

2013-11-27

Polyvinyl chloride (PVC) was mixed with natural rubbers which are liquid natural rubber (LNR), liquid epoxidised natural rubber (LENR) and liquid epoxidised natural rubber acrylate (LENRA) for a preparation of a fine non-woven fiber’s mat. PVC and each natural rubbers(PVC:LENR, PVC:LNR and PVC:LENRA) were mixed based on ratio of 70:30. Electrospinning method was used to prepare the fiber. The results show that the spinnable concentration of PVC/ natural rubber/THF solution is 16 wt%. The morphology, diameter, structure and degradation temperature of electrospun fibers were investigated by scanning electron microscopy (SEM) and thermogravimetric analysis (TGA). SEM photos showed that the morphology and diameter of the fibers were mainly affected by the addition of natural rubber. TGA results suggested that PVC electrospun fiber has higher degradation temperature than those electrospun fibers that contain natural rubber.

Estudo de propriedades de PVC modificado com grupos alquila e benzila Study of the properties of PVC modified through substitution by alkyl and benzyl groups

Directory of Open Access Journals (Sweden)

G. M Vinhas

2005-07-01

Full Text Available O poli(cloreto de vinila (PVC é o segundo termoplástico mais consumido em todo o mundo, sendo considerado o mais versátil dentre os plásticos. A grande versatilidade do PVC deve-se a suas propriedades e também a sua adequação aos mais variados processos de transformação. Uma vez que a resina de PVC é atóxica e inerte, a escolha de aditivos com essas mesmas características, permite a fabricação de filmes para embalagens de alimentos e produtos médico-hospitalares. Entretanto, suas propriedades podem se alterar quando submetido a qualquer processo de esterilização, especialmente por radiação gama. Neste trabalho foi realizado um estudo sobre a flexibilidade e estabilidade frente à radiação gama do PVC modificado quimicamente. O PVC foi modificado pela substituição de átomos de cloro por grupos alquila e benzila através de reações com reagentes de Grignard. Amostras de PVC modificado foram caracterizadas por espectroscopia de ressonância magnética nuclear de hidrogênio (RMN ¹H, espectroscopia na região do infravermelho com transformada de Fourier e calorimetria diferencial exploratória. A degradação do PVC modificado, quando submetido à radiação gama, foi avaliada por seus parâmetros viscosimétricos. De uma forma geral, o PVC modificado apresentou maior estabilidade à radiação gama que o original. O polímero modificado por substituição do cloro por grupo que contém um anel aromático foi o que apresentou maior estabilidade, quando submetido à dose de esterilização de 25 kGy. O PVC modificado apresentou temperaturas de transição vítrea ligeiramente mais baixas que o PVC original, indicando uma tendência ao aumento de flexibilidade pela presença de grupos alquila e benzila na cadeia do polímero.Poly(vinyl chloride (PVC ranks second among the most consumed thermoplastics in the world, and is considered the most versatile plastic. This versatility arises from its properties and suitability to a

Physico-chemical and chemical quality of acerola fruit clones coated with PVC film and conserved under refrigeration / Qualidade físico-química e química de frutos de clones de aceroleira recobertos com filme de PVC e conservados por refrigeração

Directory of Open Access Journals (Sweden)

Paulo Henrique Machado de Souza

2009-12-01

Full Text Available This work aimed to evaluate the physical, physicochemical and chemical changes in fruits of clones of acerola coated with PVC film and conserved under refrigeration. The clones BRS 235 (Apodi, BRS 236 (Cereja, BRS 237 (Roxinha, BRS 238 (Frutacor, II 47/1 and BRS 152 (Sertaneja had been harvested in the stage of commercial maturation. The fruits had been washed in chlorinated water, packed in expanded polystyrene trays, covered with film PVC and stored (10ºC during 12 days, with withdrawals of samples at the beginning of the experiment and to each three days. They had been evaluated: coloration, soluble solids, titratable acidity, soluble solids:titratable acidity relation, pH, soluble sugars, vitamin C, anthocyanins, weight lost, firmness and carotenoids. The experiment was carried through in experimental delineation completely randomized in factorial design (clones x time, with 3 repetitions (trays with 100g of fruits. Between the clones studied the II47/1 if it detached for the relative stability of the color, angle hue, and of anthocyanins, being more attractive for the consumer in the time of the purchase. However the clones Roxinha and Sertaneja had presented superior soluble solids:titratable acidity between the others in the end of the experiment, interesting characteristic for the flavor.Este trabalho objetivou avaliar as mudanças físicas, físico-químicas e químicas em frutos de clonesde aceroleira recobertos com filme de PVC e conservados sob refrigeração. Os clones 235 (Apodi, BRS 236 (Cereja, BRS 237 (Roxinha, BRS 238 (Frutacor, II 47/1 e BRS 152 (Sertaneja foram colhidos no estádio de maturação comercial. Os frutos foram lavados em água clorada, embalados em bandejas de poliestireno expandido cobertos com filme PVC e armazenados (10ºC durante 12 dias, com retiradas de amostras no início do experimento e a cada três dias. Foram avaliados: coloração, sólidos solúveis totais, acidez titulável, relação sólidos sol

Chalk effect on PVC cross-linking under irradiation; Vliyanie mela na sshivanie PVKh pri obluchenii

Energy Technology Data Exchange (ETDEWEB)

Chudinova, V V; Guzeev, V V; Mozzhukhin, V B; Pomerantseva, Eh G; Nozrina, F D; Zhil` tsov, V V; Zubov, V P

1994-12-31

Effect of nonmodified and modified chalk on curing degree of polymer matrix was studied under-irradiation of PVC-compositions. Films of the compositions (100 mass part 7 PVC, 0-100 mas.part of chalk, 2.5 - lead sulfate, 1.5 - lead stearate and 0.3 - glycerin) were irradiated up to absorbed dose 0.1 MGy in an inert medium. Content of gel-fraction after boiling in THF was determined with use of IR spectroscopy. It was established, that intensive dehydrochlorination and polymer curing took place on chalk particle surface. Network fixed strongly chalk particles. However, chalk inhibited processes of dehydrochlorination and PVC curing, increasing amount of noncured PVC in polymer matrix.

The viability of PVC/Al blister reuse and PVC property studies after ionizing radiation processing

International Nuclear Information System (INIS)

Castro, Alex Terela Pinheiro de

2008-01-01

The objective of this research was to separate, by means of a process of dissolution, the PVC and the aluminum that compose blister packs, generally used for pharmaceutical pills. We also studied the effect of the ionizing radiation on the PVC, and, finally, the mechanical recycling of the separated PVC, by a process of extrusion. The material we used in this work is the surplus of the pharmaceutical industry, i.e., packs with defects or burrs. We ground the material to facilitate the handling and the homogenization of the system. After that, we chose two bases for the dissolution of the aluminum: the sodium hydroxide and the potassium hydroxide. We used a system with two concentrations (1 and 2M) for each base, and for every solution we had also an agitated and a non-agitated process. From this method resulted eight experiments. After the dissolution, the samples of the material were submitted to ionizing radiation with doses of 50, 100, 150 and 200 kGy in the Dynamitron II electron accelerator of the CTR-IPEN/CNEN-SP. In the following, these samples were submitted to traction resistance tests to analyze which modifications the irradiation caused. The last step of the research was the recycling of the PVC separated from the Aluminum. We made the recycling in industrial equipment, a PVC tube extruder. The material was combined with lubricants, heat stabilizers and pigment in an intensive mixer and processed into the form of rigid PVC electrical conduits. After the eight experiments, the system with potassium hydroxide base, concentration of 2M and agitation presented the best relation between time of dissolution and characteristics of the resulting material, without degradation of the PVC. In the irradiated samples, the color of the material changed as well as its extension that was as larger as the dose of irradiation they received, indicating the dissociation of the PVC molecules. The extrusion of the PVC was successfully realized: about 200 kg (440 pounds) of

Degradação biológica do PVC em aterro sanitário e avaliação microbiológica Biological degradation of PVC in landfill and microbiological evaluation

Directory of Open Access Journals (Sweden)

Ana M. C. Grisa

2011-01-01

Full Text Available O poli(cloreto de vinila (PVC é um dos polímeros utilizado no campo das embalagens e no setor calçadista, e, em função da sua aplicação diversificada, apresenta elevados percentuais em aterros domésticos e industriais. É um polímero amorfo podendo apresentar diferentes teores de plastificante e outros aditivos responsáveis pela sua estabilização, os quais podem influenciar no tempo de vida útil e nas propriedades do produto final. Este trabalho apresenta o estudo da degradação química e biológica de filmes de poli(cloreto de vinila flexível (PVC-f, no aterro sanitário São Giácomo, na cidade de Caxias do Sul/RS, antes e após 330 dias de disposição. As amostras de PVC-f antes e após a disposição no aterro sanitário foram avaliadas por análise térmica (TGA, estrutural (FT-IR e morfológica (MEV e MO. Observou-se que as amostras de PVC-f dispostas no aterro sanitário (PVC-fa, apresentam um único evento de perda de massa, em relação ao PVC-f não degradado ou virgem (PVC-fv, além de um maior % de perda de massa e de mudanças estruturais. Nas amostras de PVC-fa foram observadas modificações morfológicas importantes para descrever os fenômenos de degradação como erosão da superfície, bioerosão, que propiciaram a ação das leveduras, bactérias e fungos presentes no meio no polímero aterrado.The poly (vinyl chloride (PVC is one of the polymers used in the field of packing materials and footwear sector, and due its diversified applications, it has presented in a high percentage of domestic and industrial landfills It is an amorphous polymer and may present different levels of plasticizer and other additives responsible for its stabilization, which can influence the lifetime and the properties of the final product. This work presents the study of the chemical and biological degradation of poly (vinyl chloride flexible (PVC-f films, at São Giácomo landfill, in Caxias do Sul city after 330 days of

The viability of PVC/Al blister reuse and PVC property studies after ionizing radiation processing; Viabilizacao do reaproveitamento dos 'blister' de PVC/Al e estudos das propriedades do PVC apos processamento por radiacao ionizante

Energy Technology Data Exchange (ETDEWEB)

Castro, Alex Terela Pinheiro de

2008-07-01

The objective of this research was to separate, by means of a process of dissolution, the PVC and the aluminum that compose blister packs, generally used for pharmaceutical pills. We also studied the effect of the ionizing radiation on the PVC, and, finally, the mechanical recycling of the separated PVC, by a process of extrusion. The material we used in this work is the surplus of the pharmaceutical industry, i.e., packs with defects or burrs. We ground the material to facilitate the handling and the homogenization of the system. After that, we chose two bases for the dissolution of the aluminum: the sodium hydroxide and the potassium hydroxide. We used a system with two concentrations (1 and 2M) for each base, and for every solution we had also an agitated and a non-agitated process. From this method resulted eight experiments. After the dissolution, the samples of the material were submitted to ionizing radiation with doses of 50, 100, 150 and 200 kGy in the Dynamitron II electron accelerator of the CTR-IPEN/CNEN-SP. In the following, these samples were submitted to traction resistance tests to analyze which modifications the irradiation caused. The last step of the research was the recycling of the PVC separated from the Aluminum. We made the recycling in industrial equipment, a PVC tube extruder. The material was combined with lubricants, heat stabilizers and pigment in an intensive mixer and processed into the form of rigid PVC electrical conduits. After the eight experiments, the system with potassium hydroxide base, concentration of 2M and agitation presented the best relation between time of dissolution and characteristics of the resulting material, without degradation of the PVC. In the irradiated samples, the color of the material changed as well as its extension that was as larger as the dose of irradiation they received, indicating the dissociation of the PVC molecules. The extrusion of the PVC was successfully realized: about 200 kg (440 pounds) of

Properties of lightweight aggregate concrete prepared with PVC granules derived from scraped PVC pipes.

Science.gov (United States)

Kou, S C; Lee, G; Poon, C S; Lai, W L

2009-02-01

This paper aims to investigate the fresh and hardened properties of lightweight aggregate concretes that are prepared with the use of recycled plastic waste sourced from scraped PVC pipes to replace river sand as fine aggregates. A number of laboratory prepared concrete mixes were tested, in which river sand was partially replaced by PVC plastic waste granules in percentages of 0%, 5%, 15%, 30% and 45% by volume. Two major findings are identified. The positive side shows that the concrete prepared with a partial replacement by PVC was lighter (lower density), was more ductile (greater Poisson's ratios and reduced modulus of elasticity), and had lower drying shrinkage and higher resistance to chloride ion penetration. The negative side reveals that the workability, compressive strength and tensile splitting strength of the concretes were reduced. The results gathered would form a part of useful information for recycling PVC plastic waste in lightweight concrete mixes.

Discoloration of plasticized PVC upon irradiation

International Nuclear Information System (INIS)

Kojima, Keiichi; Ueno, Keiji; Kumafuji, Hisao.

1981-01-01

The effects of the factors on the discoloration of PVC cross-linked by electron irradiation, such as irradiation dose, the polymerization degree of PVC resin, plasticizers and stabilizers, were studied. The composition of the plasticized PVC used for the experiment was 100 PHR of PVC, 50 PHR of plasticizer, 5 PHR of stabilizer and 5 PHR of cross-linking agent (TMPMA). Three samples with the different degree of polymerization of the PVC resin were used, namely 750, 1050 and 2600. As the plasticizers, phthalic acid esters (DBP, DOP, DIDP), trimellitic acid esters (TOTM, n-TOTM), fatty acid esters (DOS, DOZ), polyester and epoxy group plasticizers were used. The irradiation dose for the test was 3, 6 and 12 Mrad. The experimental results are summarized as follows. As the electron irradiation dose was higher, the resultant discoloration was more remarkable, and the optimum irradiation dose was below 6 Mrad. The degree of polymerization of the PVC resin did not affect the irradiation discoloration. However it was noticed that the cross-linking efficiency was better as the degree of polymerization was higher. The cross-linking efficiency was better as the content of plasticizer was more. The fatty acid esters and epoxy groups showed less discoloration and better cross-linking efficiency. Tin and barium-zinc stabilizers were good. (Kako, I.)

Effect of graphite loading on the electrical and mechanical properties of Poly (Ethylene Oxide)/Poly (Vinyl Chloride) polymer films

Science.gov (United States)

Hajar, M. D. S.; Supri, A. G.; Hanif, M. P. M.; Yazid, M. I. M.

2017-10-01

In this study, films consisting of a blend of poly (ethylene oxide)/poly (vinyl chloride) (PEO/PVC) and a conductive filler, graphite were prepared and characterized for their mechanical and electrical properties. Solid polymer blend films based on PEO/PVC (50/50 wt%/wt%) with different graphite loading were prepared by using solution casting technique. Electrical conductivity results discovered the conductivity increased with increasing of filler loading. However, increasing amount of graphite loading led to a decreased in tensile strength and young’s modulus of PEO/PVC/Graphite polymer films. The dispersion of graphite and mechanism of conductive path in the polymer films were also investigated by scanning electron microscopy (SEM). The morphology of the PEO/PVC/Graphite polymer films shows that agglomeration occurred to complete the connection of conductive path, thus improving the conductivity behavior of the polymer films.

Infrared studies of PVC-based electrolytes incorporated with lithium triflate and 1-butyl-3-methyl imidazolium trifluoromethanesulfonate as ionic liquid

Science.gov (United States)

Zulkepeli, Nik A. S. Nik; Winie, Tan; Subban, R. H. Y.

2017-09-01

In this work, 1-butyl-3-methylimidazolium trifluoromethanesulfonate (BMIMCF3SO3) is employed as ionic liquid in PVC-based polymer electrolyte system with lithium triflate (LiCF3SO3) as doping salt. The samples in film form were prepared by quantitatively varying the concentration of BMIMCF3SO3 to a fixed ratio of PVC-LiCF3SO3 using solution cast technique. The highest room temperature ionic conductivity of 1.120 × 10-7 Scm-1 was exhibited by PVC-LiCF3SO3-BMIMCF3SO3 containing 3 wt. % BMIMCF3SO3. FTIR spectra of the polymer electrolytes were examined to study the complexation of the PVC-based polymer electrolytes. Intensity of free ions, ion pairs, and ion aggregates were obtained from FTIR deconvolution in an attempt to correlate with ionic conductivity results. The intensity of free ions was found to be high for sample with 3 wt. % BMIMCF3SO3.

Radiation cross-linked PVC and its applications

International Nuclear Information System (INIS)

Lan Junming; Chen Ruyan; Jia Chaoxing; Li Min; Li Chengxin

1990-04-01

The radiation cross-linking technique is adopted for improving the polyvinyl chloride (PVC) heat-resistance and reducing its thermocontractibility. For examining its properties a small insulation sheath made from modified PVC material has been tested at 260 0 5 seconds. The results obtained were satisfactory

Studies of PVC/ENR blends: blend compositions

International Nuclear Information System (INIS)

Chantara Thevy Ratnam; Khairul Zaman Mohd Dahlan; Nasir, M.; Baharin, A.

2002-01-01

Blends of poly(vinyl chloride/epoxidized natural rubber (PVC/ENR) were prepared by using Bra bender Plasticorder at compositions ranging from 0-100% PVC. They were blended at 150 degree C mixing temperature, 50 rpm rotor speed and 10 minutes mixing time. The blends were characterized for tensile strength , elongation at break, glass transition temperatures and Fourier transform infra red spectroscopy (FTIR). Results revealed that as the PVC content increases the blend behaviour changes from elastomeric to glassy. However the blends found to be compatible at all compositions. (Author)

Active film of poly(vinyl chloride)/silver: synthesis, characterization and evaluation as antimicrobial active packaging; Filme ativo de poli(cloreto de vinila)/prata: sintese, caracterizacao e avaliacao como embalagem ativa antimicrobiana

Energy Technology Data Exchange (ETDEWEB)

Braga, Lilian R.; Rangel, Ellen T.; Machado, Fabricio, E-mail: lilianrodribraga@gmail.com [Universidade de Brasilia (UnB), Brasilia, DF, (Brazil)

2015-07-01

The antimicrobial films based on poly(vinyl chloride) (PVC) mediated silver (1, 2, 4 and 8 wt%) were evaluated as antimicrobial active packaging using the casting method. The structure of the active films was characterized by SEM, EDX-XRF, XRD, FTIR and TG. FTIR spectra confirmed the PVC-Ag interaction due to the presence of new bands at 1745 cm{sup -1} and 1165 cm{sup -1} bands, which are absent in the PVC control. The FRX-EDX spectrum confirmed the presence of silver ions in all the films. TG and SEM results showed that the increased concentration of silver provided an improved thermal stability and presence of pores in the active films, respectively. Antimicrobial activity was evaluated by disk diffusion method for Bacillus subtilis, Fusarium solani and Apergillus niger, which proved the efficiency of the films active. (author)

Analysis of Adipate Ester Contents in PVC Plastics

DEFF Research Database (Denmark)

Berg, Rolf W.

2006-01-01

Plasticizers are needed in flexible PVC (PolyVinylChloride) products. There is serious concern that commonly used phthalate esters may harm life reproduction systems. To avoid the problems, instead adipate di-esters (AEs) of C8 to C10 alcohols are used as higher prized alternatives; e.g. di-2......-ethylhexyl adipate or DEHA [103-23-1], also known as Adimoll® or di-octyl adipate, DOA, see Fig. 1. A widely used plasticizer in food (cling) films is DEHA, often in combination with polymers, epoxidized soya-bean oil, etcetera. DEHA also occurs in children toys. We have previously shown that the presence...... of phthalate esters in PVC can be rapidly analyzed by Fourier transform (FT-) Raman spectroscopy excited with a 1064 nm laser. Here in this project we report a similar study. The aim was to find out whether FT-Raman spectroscopy can be used to determine the presence of adipate esters (AEs) as plasticizers...

Studies on heat shrinkage PVC tubes

International Nuclear Information System (INIS)

Pyun, Hyung Chick; Kim, Ki Yup; Nho, Young Chang

1991-01-01

Radiation crosslinking of PVC was investigated for the purpose of obtaining a suitable formulation for heat shrinkable tube. PVC was not only compounded with various crosslinking agents and plasticizers to evaluate their effects on the radiation sensitivity, heat shrinkable property and other mechanical properties, but also mixed with NBR, crosslinking agents and plasticizers to obtain efficient crosslinking yield and suitable mechanical properties for heat shrinkable tube. Gel yield of PVC increased with increasing unsaturation levels per molecular weight of crosslinking agents. Among crosslinking agents tested, TMPTMA with three unsaturated groups showed highest gel yield, while PVC containing NBR was more sensitive to crosslinking than PVC itself regardless the types of crosslinking agents and plasticizers. Tensile strength was increased with increasing radiation dose and gel percent, but elongation decreased. It was found that gel percent was increased with increasing radiation dose, heat transformation was decreased with increasing gel percent. When NBR was mixed with PVC, the radiation dosage required for enhancing yield of gel percent and heat transformation were found to be much smaller comparing with the case containing no NBR. Therefore, the addition of NBR to PVC was very effective to increase heat-resisting property of PVC. Heat shrinkage was not much varied with radiation dose, the types of crosslinking agents and plasticizers, but it was increased remarkably with decreasing stretching temperature and increasing annealing temperature. (Author)

Active film of poly(vinyl chloride)/silver: synthesis, characterization and evaluation as antimicrobial active packaging

International Nuclear Information System (INIS)

Braga, Lilian R.; Rangel, Ellen T.; Machado, Fabricio

2015-01-01

The antimicrobial films based on poly(vinyl chloride) (PVC) mediated silver (1, 2, 4 and 8 wt%) were evaluated as antimicrobial active packaging using the casting method. The structure of the active films was characterized by SEM, EDX-XRF, XRD, FTIR and TG. FTIR spectra confirmed the PVC-Ag interaction due to the presence of new bands at 1745 cm"-"1 and 1165 cm"-"1 bands, which are absent in the PVC control. The FRX-EDX spectrum confirmed the presence of silver ions in all the films. TG and SEM results showed that the increased concentration of silver provided an improved thermal stability and presence of pores in the active films, respectively. Antimicrobial activity was evaluated by disk diffusion method for Bacillus subtilis, Fusarium solani and Apergillus niger, which proved the efficiency of the films active. (author)

PVC pipes in gas distribution: still going strong!

NARCIS (Netherlands)

Hermkens, Rene; Wolters, Mannes; Weller, Jeroen; Visser, Roy; Davidovski, Z.; Belloir, P.; Fumire, J.

2008-01-01

In the Netherlands (impact-modified) PVC is the preferred material for low-pressure (30 and 100 mbar) gas distribution systems. More than 50% of the total length (about 122,000 km) of this system is rigid PVC or impact-modified PVC. The installation of rigid PVC (uPVC) pipelines started about 50

Structural, thermal, dielectric spectroscopic and AC impedance properties of SiC nanoparticles doped PVK/PVC blend

Science.gov (United States)

Alghunaim, Naziha Suliman

2018-06-01

Nanocomposite films based on poly (N-vinylcarbazole)/polyvinylchloride (PVK/PVC) blend doped with different concentrations of Silicon Carbide (SiC) nanoparticles have been prepared. The X-ray diffraction, Ultra violet-visible spectroscopy, thermogravimetric analysis and electrical spectroscopic has been used to characterize these nanocomposites. The X-ray analysis confirms the semi-crystalline nature of the films. The intensity of the main X-ray peak is decreased due to the interaction between the PVK/PVC and SiC. The main SiC peaks are absent due to complete dissolution of SiC in polymeric matrices. The UV-Vis spectra indicated that the band gap optical energy is affected by adding SiC nanoparticles because the charges transfer complexes between PVK/PVC with amount of SiC. The thermal stability is improved and the estimated values of ε‧ and ε″ are increased with increasing for SiC content due to the free charge carriers which in turn increase the ionic conductivity of the doped samples. The plots of tan δ with frequency are studied. A single peak from the plot between tan δ and Log (f) is appeared and shifted towards the higher frequency confirmed the presence of relaxing dipoles moment.

A PVC/polypyrrole sensor designed for beef taste detection using electrochemical methods and sensory evaluation.

Science.gov (United States)

Zhu, Lingtao; Wang, Xiaodan; Han, Yunxiu; Cai, Yingming; Jin, Jiahui; Wang, Hongmei; Xu, Liping; Wu, Ruijia

2018-03-01

An electrochemical sensor for detection of beef taste was designed in this study. This sensor was based on the structure of polyvinyl chloride/polypyrrole (PVC/PPy), which was polymerized onto the surface of a platinum (Pt) electrode to form a Pt-PPy-PVC film. Detecting by electrochemical methods, the sensor was well characterized by electrochemical impedance spectroscopy (EIS) and cyclic voltammetry (CV). The sensor was applied to detect 10 rib-eye beef samples and the accuracy of the new sensor was validated by sensory evaluation and ion sensor detection. Several cluster analysis methods were used in the study to distinguish the beef samples. According to the obtained results, the designed sensor showed a high degree of association of electrochemical detection and sensory evaluation, which proved a fast and precise sensor for beef taste detection. Copyright © 2017 Elsevier Ltd. All rights reserved.

Australia slaps duties on PVC imports

International Nuclear Information System (INIS)

Young, I.

1992-01-01

The Australian Anti-Dumping Authority (ADA0) has imposed dumping duties on imports of polyvinyl chloride (PVC) resin from seven countries and on certain expanded polystyrene (EPS) beads from Korea and Singapore. The decisions come at the end of two separate investigations begun earlier this year. In its first finding, the ADA concluded that there has been dumping of PVC resin from Canada, China, France, Japan, Norway, Saudi Arabia, and Thailand, which has caused and threatens to cause material injury to the domestic PVC industry. An eighth country, Romania, was found not to have been exporting PVC to Australia. The case is the second of its kind in Australia focusing on PVC. In December 1991 the ADA found in favor of local producer sin a dumping complaint against Argentina, Brazil, Hungary, Israel, Korea, Mexico, Poland, Singapore, Taiwan, and the US

Electrical and spectroscopic characterization of polyaniline-polyvinyl chloride (PANI-PVC) blends doped with sodium thiosulphate

International Nuclear Information System (INIS)

Ameen, Sadia; Ali, Vazid; Zulfequar, M.; Mazharul Haq, M.; Husain, M.

2008-01-01

Polyaniline is doped with sodium thiosulphate in aqueous tetrahydrofuran (THF) and the blended films have been prepared by changing the amount of doped polyaniline (PANI) in the fixed amount of polyvinyl chloride (PVC). The electrical conductivity of various samples of polyaniline-polyvinyl chloride (PANI-PVC) blends has been studied to see the effect of dopant in the temperature range 300-400 K. Mott's parameters are used to explain the conduction mechanism. Different parameters such as pre-exponential factor (σ 0 ), activation energy (ΔE) and T 0 have also been calculated to see the effect of chemical doping. The crystallinity of the blends is explained on the basis of T 0 . The calculated values of T 0 show that crystallinity increases with an increase of doped PANI in PANI-PVC blends. Fourier transform-infrared (FTIR) spectroscopy is done to explore the nature and interaction of dopant into the polymeric chain

High Doses Gamma Radiolysis of PVC: Mechanisms of Degradation

International Nuclear Information System (INIS)

Colombani, J.

2006-01-01

PVC radiolysis leads to the formation of various degradation products: radicals, gas, oxidized products or polyenes. In order to predict the formation of the degradation products with regard to irradiation and ageing parameters, it is important to improve the understanding of the radiolysis mechanisms of PVC. Thus, we used several analytical techniques (Electron Spin Resonance, Fourier Transform Infrared spectroscopy, Nuclear Magnetic Resonance, Size Exclusion Chromatography) to get information on PVC samples irradiated at high doses (up to 4MGy) under different conditions. Gamma irradiation induces the formation of various radicals into PVC. Older studies were generally focused on the effect of low dose and/or low temperature irradiations on PVC. We present here ESR signals of PVC irradiated at high doses and at room temperature. We show that peroxyl radicals are producted by radiolysis under aerobe conditions and that polyenyl radicals are formed under anaerobe conditions. PVC radiolysis induces gas production and especially hydrogen chloride. Production of hydrogen chloride is well known until 1 MGy. We have studied by FTIR, the evolution of the quantity of HCl produced until 4 MGy. We show that higher irradiation dose leads to the lower radiolytic yield of HCl (G(HCl)). Moreover, G(HCl) obtained in aerobe conditions is about fourfold as great as G(HCl) observed in anaerobe radiolysis. Propagation and termination reactions induce degradation products: polyene sequences and crosslinking reactions are observed under anaerobe conditions; oxidized products with addition of chain scissions are formed under aerobe conditions. Although the literature about PVC radiolysis is rich, the main reacting pathways are not well established. Moreover the high doses studies are almost non-existent. We show by FTIR that aerobe radiolysis induces formation of ketons and acids. NMR experiments confirme these results but also focuse on small acids formed (with 2, 3 or 4 carbons). The

Zinc oxide nanoparticle-coated films: fabrication, characterization, and antibacterial properties

Energy Technology Data Exchange (ETDEWEB)

Jiang, Yunhong, E-mail: y.jiang@leeds.ac.uk [University of Leeds, Institute of Particle Science and Engineering (United Kingdom); O’Neill, Alex J. [University of Leeds, School of Molecular and Cellular Biology (United Kingdom); Ding, Yulong [University of Leeds, Institute of Particle Science and Engineering (United Kingdom)

2015-04-15

In this article, novel antibacterial PVC-based films coated with ZnO nanoparticles (NPs) were fabricated, characterized, and studied for their antibacterial properties. It was shown that the ZnO NPs were coated on the surface of the PVC films uniformly and that the coating process did not affect the size and shape of the NPs on the surface of PVC films. Films coated with concentrations of either 0.2 or 0.075 g/L of ZnO NPs exhibited antibacterial activity against both Gram-positive (Staphylococcus aureus) and Gram-negative (Escherichia coli) bacteria, but exhibited no antifungal activity against Aspergillus flavus and Penicillium citrinum. Smaller particles (100 nm) exhibited more potent antibacterial activity than larger particles (1000 nm). All ZnO-coated films maintained antibacterial activity after 30 days in water.

Revalidation of the method used for measurement of electron beam absorbed dose by means of a polyvinylchloride film dosimeter. Part 1

International Nuclear Information System (INIS)

Peimel-Stuglik, Z.; Fabisiak, S.

2007-01-01

The Radiation Sterilization Plant operated at the Institute of Nuclear Chemistry and Technology (INCT) is using the dosimetry method based on optical signal measurement at polyvinylchloride (PVC) film which is 30 years old. After so long storage time, a scrupulous revalidation of the method is necessary. In the report there were presented results of investigations dealing with physical parameters mainly. It was ascertained that PVC film used in the INCT belongs to different batches. Thickness scattering is low (±2%), but the transparency, sensitivity to radiation, repeatability of dosimetric signal and other parameters are changing to a wide extent. As a result, each scroll of the PVC film must be carefully checked and calibrated before its dosimetric use. (authors) [pl

Atividade antioxidante, composição química e conservação do maracujá-amarelo embalado com filme PVC

Directory of Open Access Journals (Sweden)

Maria Cristina Copello Rotili

2013-12-01

Full Text Available O objetivo deste trabalho foi avaliar as características químicas e a conservação do maracujá-amarelo embalado com filme de PVC durante o armazenamento refrigerado a 5 ºC. Atividade antioxidante (DPPH e TEAC, compostos fenólicos totais, β-caroteno e ácido ascórbico do suco do fruto foram os parâmetros químicos avaliados. As estimativas de perda de massa, enrugamento, cor e sintomas de patógenos foram utilizadas no estudo de conservação. As avaliações foram realizadas em intervalos de 10 dias, durante 40 dias. De acordo com os resultados, o teor de fenólicos totais aumentou durante o armazenamento, com variações entre 20,10 e 21,29 mg EAG 100 mL-1. O conteúdo de ácido ascórbico aumentou até o 20º dia de armazenamento (33,58 mg 100 mL-1, mas seguiu com decréscimos até o 40º dia (21,67 mg 100 mL-1. Independentemente do uso de PVC, o conteúdo de β-caroteno não variou durante o armazenamento. As atividades antioxidantes DPPH e TEAC do suco diminuíram durante o armazenamento. Não foram encontradas correlações positivas entre as atividades DPPH e TEAC e o teor de fenólicos totais, sugerindo que este último não contribui para a atividade antioxidante do suco do maracujá. O uso da embalagem de PVC não influenciou positivamente a atividade antioxidante e os teores de fenólicos totais e ácido ascórbico do suco do maracujá-amarelo durante seu armazenamento. A embalagem de PVC não inibiu sintomas de desenvolvimento de patógenos por até 30 dias de armazenamento, a 5 ºC, mas reduziu a perda de massa fresca e o enrugamento do fruto, proporcionando condições ótimas de comercialização por até 20 dias.

Biodegradable films of starch/PVOH/alginate in packaging systems for minimally processed lettuce (Lactuca sativa L.

Directory of Open Access Journals (Sweden)

Renata Paula Herrera Brandelero

Full Text Available ABSTRACT Biodegradable packaging may replace non-biodegradable materials when the shelf life of the packaged product is relatively short, as in minimally processed foods. The objective of this work was to evaluate the efficiency of biodegradable films comprising starch/polyvinyl alcohol (PVOH/alginate with the addition of 0 or 0.5% of essential oil of copaiba (EOCP or lemongrass (EOLM compared to poly-vinyl chloride (PVC films in the storage of minimally processed lettuce. Lettuce samples cut into 1-cm strips were placed in polypropylene trays wrapped with biodegradable films and stored at 6 ± 2 °C for 8 days. PVC films were used as controls. The biofilms presented 11.43-8.11 MPa resistance and 11.3-13.22% elongation, with water vapor permeability (WVP of 0.5-4.04 x 10-12 g. s-1.Pa-1.m-1; thus, the films' properties were considered suitable for the application. The lettuce stored in PVC presented minor total soluble solids (TSS, less luminosity (L, higher intensity of yellow color (b, and eight times less mass loss than that stored in biodegradable films. Multivariate analysis showed that the lettuce lost quality after 2 days of storage in PVC films, representing a different result from the other treatments. Lettuce stored in biodegradable films for 2 and 4 days showed a greater similarity with newly harvested lettuce (time zero. The films with or without the addition of essential oil showed similar characteristics. Biodegradable films were considered viable for the storage of minimally processed lettuce.

Possibility of the use of PVC plastics as a ray dosemeter

International Nuclear Information System (INIS)

Amri Ayat; Sutrisno Puspodikoro.

1978-01-01

The use of plastics as a radiation dosemeter for measurement of γ-rays is very attractive to be studied. In the work presented here commercial PVC film with the trade-mark ''Takiron'' is used for Co-60 radiation dosimetry. According to the experiments the useful dose range extends over 0.15-1.2 Mrads. Fading of the coloration with time after radiation exposure can be stabilised by heat treatment (60 deg C for 30 minutes). (author)

Recycling of PVC Waste via Environmental Friendly Vapor Treatment

Science.gov (United States)

Cui, Xin; Jin, Fangming; Zhang, Guangyi; Duan, Xiaokun

2010-11-01

This paper focused on the dechlorination of polyvinyl chloride (PVC), a plastic which is widely used in the human life and thereby is leading to serious "white pollution", via vapor treatment process to recycle PVC wastes. In the process, HCl emitted was captured into water solution to avoid hazardous gas pollution and corruption, and remaining polymers free of chlorine could be thermally degraded for further energy recovery. Optimal conditions for the dechlorination of PVC using vapor treatment was investigated, and economic feasibility of this method was also analyzed based on the experimental data. The results showed that the efficiency of dechlorination increased as the temperature increased from 200° C to 250° C, and the rate of dechlorination up to 100% was obtained at the temperature near 250° C. Meanwhile, about 12% of total organic carbon was detected in water solution, which indicated that PVC was slightly degraded in this process. The main products in solution were identified to be acetone, benzene and toluene. In addition, the effects of alkali catalysis on dechlorination were also studied in this paper, and it showed that alkali could not improve the efficiency of the dechlorination of PVC.

Studies in cross-linking PVC footwear soling compounds using gamma-irradiation

International Nuclear Information System (INIS)

Bloom, L.I.

1983-01-01

Irradiation cross-linking of polymeric materials has been known for some time, but it is only in recent years that it has been put to commercial advantage. Well known uses are the modification of PVC for higher temperature applications. Fundamental studies were carried out on amongst other materials, plasticised PVC compounds for use in cable applications. The results of this work, encouraged the author to investigate cross-linkable PVC in areas such as footwear soling

Radiation crosslinking of PVC with polyfunctional monomers

International Nuclear Information System (INIS)

Dobo, J.; Takacs, E.; Csato, P.

1984-01-01

The radiation crosslinking of PVC in the presence of ethylene glycol dimethacrylate (EGDM) and of trimethylol propane trimethacrylate (TMPTM) was investigated. The effect of PVC powders of different types on the polymerization rate of these monomers was studied by a Calvet-type microcalorimeter. In the milled PVC sheets containing 50 part EGDM a high concentration of trapped free radicals was found by ESR after 16 months storage. (author)

Investigation of Ice-PVC separation under Flexural Loading using FEM Analysis

Directory of Open Access Journals (Sweden)

H Xue

2016-08-01

Full Text Available This paper presents the FEM technique applied in the study of ice separation over a polyvinyl chloride (PVC surface. A two layer model of ice and PVC is analysed theoretically using Euler-Bernoulli beam theory and the rule of mixtures. The physical samples are prepared by freezing ice over the PVC surfaces. The samples are tested experimentally in a four-point loading setup. The experimental results contain strain data gathered through a data acquisition system using the LabView software. The data is collected at the rate of 1 kHz per load step. A model is also coded in MATLAB® and simulated using the finite element method (FEM in ANSYS® Multiphysics. The FEM model of the ice and PVC sample is built using solid elements. The mesh is tested for sensitively. A good agreement is found between the theoretical, experimental and numerical simulation results.

Desenvolvimento de PVC reforçado com fibras de vidro longas para fabricação de produtos moldados Long glass fiber reinforcement of PVC molding compounds

Directory of Open Access Journals (Sweden)

Leandro H. Grizzo

2011-01-01

glass fibers' length and reduced the possibility of PVC resins' degradation. 20 w/w% long glass fiber reinforced rigid PVC (LGF/PVC composites were then obtained with twice as high modulus and Charpy's impact strength compared to the unreinforced rigid PVC even with the composites were formulated with a high quantity of plasticizer. As a result, PVC can be used in unrecognized high-performance applications that were not possible before.

Specific migration of di-(2-ethylhexyl)adipate (DEHA) from plasticized PVC film: results from an enforcement campaign

DEFF Research Database (Denmark)

Petersen, Jens Højslev; Breindahl, T.

1998-01-01

Units. Initially, all films were screened for the migration into isooctane (exposed 2 h at 40 degrees C) of DEHA and other potentially present low molecular weight plasticizers using full scanning mass spectrometry. Films showing a substantial migration of DEHA were further tested with olive oil...... according to the declared field of application (exposed for 10 days at 40 degrees C). In 47 of the 49 films the migrate contained a substantial amount of DEHA. In 46 films the migration exceeded the specific migration limit of 3 mg/dm(2) after use of the relevant reduction factor given in legislation......) and these films were deemed to be illegal according to their present declared field of application as given by their labelling. In a few cases, some migration of the plasticizer di-n-butyl phthalate was seen....

PVC mixtures’ mechanical properties with the addition of modified calcite as filler

Directory of Open Access Journals (Sweden)

Vučinić Dušica R.

2012-01-01

Full Text Available In this study mechanical properties of PVC mixtures (PVC, stabilizer, lubricant, filler such as tensile strength, tensile elongation, breaking strength, and breaking elongation were investigated. Unmodified calcite, as well as calcite modified by stearic acid, were used as fillers in wet and dry processes. The PVC mixtures containing the calcite modified by wet procedure have better mechanical properties compared to those with the calcite modified by the dry process. Tensile and breaking strength of the PVC mixture containing the calcite modified with 1.5% stearic acid using wet process, are higher for 2.8% and 5.2%, respectively, compared to the PVC mixture containing the calcite modified with the same amount of acid used in the dry process. The tensile strength difference between the mixtures increases with the increase of the concentration of used stearic acid up to 3%. The strength of PVC mixture with the calcite modified by wet process is 3.1% higher compared to the mixture containing calcite modified by dry process. The results showed that the bonding strength between calcite and the adsorbed organic component affected tensile strength, tensile elongation and breaking strength of the PVC mixtures. The best filler was obtained by wet modification using 1.5% stearic acid solution that provided the formation of a stearate monolayer chemisorbed on calcite. The PVC mixtures containing the calcite modified by wet process using 1.5% stearic acid solution exhibited the best mechanical properties. This calcite was completely hydrophobic with dominant chemically adsorbed surfactant, which means that stearate chemisorbed on calcite provided stronger interaction in the calcite-stearic acid-PVC system.

Physicomechanical properties of PVC radiation-modified by tridecaethyleneglycol methacrylic ester

International Nuclear Information System (INIS)

Lomonosova, N.V.

1988-01-01

A study was made on physicomechanical properties of radiation-modified system on the basis of PVC and TGM-13 oligomer (dimethacrylic ester of tridecaethyleneglycol, 43.2%). Main physical properties of the composition (maximal stresses, softening point, double refraction value, activation energy, temperature positions of the first and the second maximums on isometric heating diagram) were used to determine its isotropic and oriented states, depending on absorbed radiation dose (0-128 kGy). It is shown that radiation PVC modification by TGM-13 oligomer results in formation of linked 'soft' plastic. In terms of strength it is on a par with isotropic linear PVC, but compare favourably with it with respect to t ρ and ε

Change Spectroscopic, thermal and mechanical studies of PU/PVC blends

Energy Technology Data Exchange (ETDEWEB)

Hezma, A.M. [Spectroscopy Department, Physics Division, National Research Center, Giza (Egypt); Elashmawi, I.S. [Spectroscopy Department, Physics Division, National Research Center, Giza (Egypt); Physic Department, Faculty of Science, Taibah University, Al-Ula (Saudi Arabia); Rajeh, A., E-mail: a.rajeh88@yahoo.com [Physic Department, Faculty of Science, Amran University, Sa' dah (Yemen); Physics Department, Faculty of science, Mansoura University, Mansoura (Egypt); Kamal, Mustafa [Physics Department, Faculty of science, Mansoura University, Mansoura (Egypt)

2016-08-15

Blends of polyurethane (PU) and polyvinyl chloride (PVC) with different concentrations were prepared by casting method. The effects of PU on PVC blends was examined by Fourier transform-infrared (FTIR), Ultra-violet visible studies (UV/VIS.), X-ray diffraction (XRD), Thermogravimetric (TGA), Differential scanning calorimetry (DSC), and mechanical properties (stress–strain curve). The interaction between PU and PVC was examined by FT-IR through the absorbance of the N–H groups and was correlated to mechanical/thermal properties. Ultra-violet visible said that optical energy gap decrease with increasing concentration of PU. Differential scanning calorimetry results was observed a single glass transition temperature (T{sub g}) for blends this confirming existence miscibility within the blends. The causes for best thermal stability of some blends may be described by measurements of interactions between C=O groups of PU and the α-hydrogen of PVC or a dipole–dipole –C=O..Cl–C– interactions. Significant alterations in FTIR, X-ray and DSC examination shows an interactions between blends had good miscibility. X-ray shows some alterations in the intensity with additional PU. PU change the mechanical behavior of PVC through of the blends. When polyurethane content increase causes polyvinyl chloride tensile strength decreases and elongation at break increase.

Economic sensitivity of DAW incineration to PVC content

International Nuclear Information System (INIS)

Rossmassler, R.L.

1986-01-01

Economic analyses of the volume reduction of low level radwaste, including the incinerator of Dry Active Waste (DAW), spent resins and filter sludges, are performed using the microcomputer code VOLREDUCER. Based on BWR and PWR data taken from previous EPRI work, the sensitivity of incinerator economics to polyvinyl chloride (PVC) content in DAW is examined. An annual cost penalty associated with the presence of PVC in the waste is formulated, and the sensitivity of this penalty to a variety of parameters is determined. The alternative of sorting out PVC from the rest of the waste is compared to incineration with regard to this annual cost penalty. These penalties may range as high as $100,000 annually depending on the waste characteristics and percent of PVC

Chain radiation-chemical oxidation of aromatic amines in polyvinylchloride films

International Nuclear Information System (INIS)

Kolninov, O.V.; Lisovskaya, I.A.; Milinchuk, V.K.

1983-01-01

Radiation-chemical oxidation of tetramethyldiaminediphenylmethane in polyvinylchloride (PVC) and polystyrene (PS) films was investigated in the presence of CBr 4 at 300 K. Radiation yields (G) of 70 and 1 were obtained for an oxidized amine form (Am + ) in PVC and PS, resp. High yields of Am + in PVC matrix indicate the chain character of an oxidation reaction. Triplet states, which form exciplexes with CBr 4 were established to participate in oxidation reactions. The kinetic scheme suggested for the chain radiation oxidation of Am takes into account energy transfer, formation and degradation of the excited states of molecules resulting in the initiation and propagation of the chain on the account of active particles. (author)

Construction and demolition waste as a source of PVC for recycling.

Science.gov (United States)

Prestes, Sabrina Moretto Darbello; Mancini, Sandro Donnini; Rodolfo, Antonio; Keiroglo, Raquel Carramillo

2012-02-01

Construction and demolition waste can contain considerable amounts of polyvinyl chloride (PVC). This paper describes a study of the recycling of PVC pipes collected from such waste materials. In a sorting facility for the specific disposal of construction and demolition waste, PVC was found to represent one-third of the plastics separated by workers. Pipes were sorted carefully to preclude any possible contamination by poly(ethylene terephthalate) (PET) found in the waste. The material was ground into two distinct particle sizes (final mesh of 12.7 and 8 mm), washed, dried and recycled. The average formulation of the pipes was determined based on ash content tests and used in the fabrication of a similar compound made mainly of virgin PVC. Samples of recycled pipes and of compound based on virgin material were subjected to tensile and impact tests and provided very similar results. These results are a good indication of the application potential of the recycled material and of the fact that longer grinding to obtain finer particles is not necessarily beneficial.

Determination of Volatile Organic Compounds (VOCs from Wrapping Films and Wrapped PDO Italian Cheeses by Using HS-SPME and GC/MS

Directory of Open Access Journals (Sweden)

Sara Panseri

2014-06-01

Full Text Available Nowadays food wrapping assures attractive presentation and simplifies self-service shopping. Polyvinylchloride (PVC- and polyethylene (PE-based cling-films are widely used worldwide for wrapping cheeses. For this purpose, films used in retail possess suitable technical properties such as clinginess and unrolling capacity, that are achieved by using specific plasticizers during their manufacturing process. In the present study, the main VOCs of three cling-films (either PVC-based or PE-based for retail use were characterized by means of Solid-Phase Micro-Extraction and GC/MS. In addition, the effects of cling film type and contact time on the migration of VOCs from the films to four different PDO Italian cheeses during cold storage under light or dark were also investigated. Among the VOCs isolated from cling-films, PVC released 2-ethylhexanol and triacetin. These compounds can likely be considered as a “non-intentionally added substance”. These same compounds were also detected in cheeses wrapped in PVC films with the highest concentration found after 20 days storage. The PE cling-film was shown to possess a simpler VOC profile, lacking some molecules peculiar to PVC films. The same conclusions can be drawn for cheeses wrapped in the PE cling-film. Other VOCs found in wrapped cheeses were likely to have been released either by direct transfer from the materials used for the manufacture of cling-films or from contamination of the films. Overall, HS-SPME is shown to be a rapid and solvent free technique to screen the VOCs profile of cling-films, and to detect VOCs migration from cling-films to cheese under real retail storage conditions.

Penelitian pengaruh asam sulfat terhadap sifat fisika kekerasan atasan sepatu kerja PVC

Directory of Open Access Journals (Sweden)

Kusumo Retno Winahyu

1996-12-01

Full Text Available The Research of hardness aspect of PVC boot upper treated by sulfuric acid to detect influence of sulfuric acid to hardness upper on PVC boot upper. The method of the research has been done by immersing samples in sulfuric acid solution 30 % (v/v for 24 hours. After immersing samples examined connected with hardness physical property. The result of the research shown that hardness physical property become decreasing until 16,08 % has error standard 5,48. It is still agree with SNI 12 – 1848-1990. Sepatu bot dari PVC.

STUDY CONCERNING THE INFLUENCE OF CERTAIN HYDROPHILIC AUXILIARIES ON THE PROPERTIES OF THE PLASTICIZED POLYVINYL CHLORIDE POROUS FILMS Part II-HYGIENIC PROPERTIES

Directory of Open Access Journals (Sweden)

BĂLĂU MÎNDRU Tudorel

2015-05-01

Full Text Available The purpose of this paper was to obtain certain PVC films with improved hygienic properties, with applications both in the artificial leather industry and in other domains. This was done by introducing certain hydrophilic auxiliaries with free chemical functions into the chemical structure of the PVC films, such as: collagen hydrolysates (CH, hydroxyl-terminated polydimethylsiloxane (HTPDMS and nonylphenol ethoxylate (NPE. The use of these hydrophilic auxiliaries combined with the action of the high frequency electric fields (H.F.E.F. allows the attainment of cellular structures where the walls of the cells obtained from the expanding process display an enhanced humidity absorption. The collagen hydrolysates used to obtain the plasticized PVC porous films was obtained by electrolytic hydrolysis starting from Chamois leather powder waste resulting from buffing operation, according to a methodology described in a previous paper. The first part of this study was concerned with the influence of the addition of hydrophilic agents upon the moisture sorption of the plasticized PVC porous films. In this paper, there was investigated the water vapour and air permeability as well as the water vapour absorption of the porous films expanded in the H.F.E.F. in correlation with the nature and the recipe variant of the hydrophilic auxiliaries. The results highlighted the fact that the use of certain combinations of hydrophilic agents led to obtaining materials with adequate hygienic properties.

Self-Plasticization of PVC via click reaction of a monooctyl phthalate derivative

Directory of Open Access Journals (Sweden)

Jia Puyou

2017-09-01

Full Text Available Modified PVC (M-PVC material with suppressed migration and low glass transition temperature was prepared via click reaction of a monooctyl phthalate derivative. Chemical structure and composition of M-PVC were characterized by FT-IR, 1H NMR and element analysis. Thermal stability, glass transition temperature and migration stability of M-PVC were studied with TGA, DSC and migration tests, respectively. The study showed that M-PVC exhibited poor thermal stability, and low glass transition temperature of 66.0°C. No migration was found in distilled water, 10% (v/v ethanol, 30% (w/vacetic acid and petroleum ether. The PVC material is expected to preparing PVC products in the areas with high migration resistance requirement.

Quality control in the recycling stream of PVC from window frames by hyperspectral imaging

Science.gov (United States)

Luciani, Valentina; Serranti, Silvia; Bonifazi, Giuseppe; Di Maio, Francesco; Rem, Peter

2013-05-01

Polyvinyl chloride (PVC) is one of the most commonly used thermoplastic materials in respect to the worldwide polymer consumption. PVC is mainly used in the building and construction sector, products such as pipes, window frames, cable insulation, floors, coverings, roofing sheets, etc. are realised utilising this material. In recent years, the problem of PVC waste disposal gained increasing importance in the public discussion. The quantity of used PVC items entering the waste stream is gradually increased as progressively greater numbers of PVC products approach to the end of their useful economic lives. The quality of the recycled PVC depends on the characteristics of the recycling process and the quality of the input waste. Not all PVC-containing waste streams have the same economic value. A transparent relation between value and composition is required to decide if the recycling process is cost effective for a particular waste stream. An objective and reliable quality control technique is needed in the recycling industry for the monitoring of both recycled flow streams and final products in the plant. In this work hyperspectral imaging technique in the near infrared (NIR) range (1000-1700 nm) was applied to identify unwanted plastic contaminants and rubber present in PVC coming from windows frame waste in order to assess a quality control procedure during its recycling process. Results showed as PVC, PE and rubber can be identified adopting the NIR-HSI approach.

Conservação pós-colheita de frutos de pimentão sob diferentes condições de armazenamento e filmes Postharvest conservation of bell pepper fruits under different storage conditions and films

Directory of Open Access Journals (Sweden)

Cristiane Maria A Morgado

2008-06-01

Full Text Available Este trabalho teve como objetivo avaliar diferentes temperaturas e coberturas na conservação de frutos de pimentão 'Magali-R'. No primeiro experimento, avaliou-se o uso de filme de PVC ou cera, e os frutos foram armazenados a 20ºC e 66%UR, e no segundo experimento associou-se o filme de PVC e cera, com armazenamento a 22°C (67% UR; 12ºC (90% UR e 5ºC (87% UR. Acompanhou-se a evolução da qualidade dos frutos avaliando-se a massa fresca, a aparência, o aparecimento de podridões e os teores de sólidos solúveis, acidez titulável e ácido ascórbico. A proteção dos pimentões com cera ou filme de PVC foi favorável à manutenção da aparência e da massa fresca, e protegeu-os contra podridões, sem prejuízos aos teores de sólidos solúveis, acidez titulável e ácido ascórbico, com aumento significativo na vida útil para até 33 dias com o armazenamento a 5°C.Different temperatures and films were evaluated for the conservation of 'Magali-R' bell peppers. In the first experiment, fruits were covered with PVC film or wax, and stored under 20ºC and 66% RH. In the second, fruits covered with PVC film or wax, and stored under 22ºC (67% RH; 12ºC (90% RH; and 5ºC (87% RH. Fruits were evaluated for fresh mass, appearance, rot and soluble solids, titratable acidity and ascorbic acid content. The protection of bell peppers with wax or PVC film helped to maintain the appearance, the fresh mass and to protect against rotting, without damages to soluble solids, titratable acidity and ascorbic acid contents, with significant increase in shelf life up to 33 days with storage under 5°C.

Effect of radiation on Poly Vinyl chloride (PVC)

International Nuclear Information System (INIS)

Massaud, F.; Haraga, S.; Benfaid, N.; Benayad, S.; Kabar, Y.; Elmesmary, Y; Elwerfeli, M.; Omran, Sh.

1993-01-01

Radiation crosslinking of polymeric materials is of increasing commercial importance because of the improved thermal, electrical and mechanical properties. Poly Vinylchloride (PVC) is one of the most important polymers. Many attempts were made to study the primary reactions induced by the direct effect of radiation on PVC. In this study, powder PVC was irradiated with different doses at ambient temperature. Formation of free radicals was investigated by electron spin resonance (ESR) method and molecular weight was determined by viscosity measurements. It has been observed that hydrogen chloride was evolved because of noticeable change in color. One type of radical, Poly enyl structure was trapped at room temperature. The non-symmetric singlet structure of the ESR spectra is due to the presence of oxygen. The radical concentration increased with increase of dose. The molecular weight of irradiated PVC was found to be inversely proportional to the increase of radiation dose, which is believed to be due to the occurrence of degradation. It can be concluded that gamma radiation will be the best method for crosslinking of PVC if multi-functional groups or monomers are present. (author)

Comparative study on polyvinyl chloride film as flexible substrate for preparing free-standing polyaniline-based composite electrodes for supercapacitors.

Science.gov (United States)

Wang, Hongxing; Liu, Dong; Du, Pengcheng; Wei, Wenli; Wang, Qi; Liu, Peng

2017-11-15

The free-standing polyaniline (PANI)-based composite film electrodes were prepared with polyvinyl chloride (PVC) and the aniline modified PVC (PVC-An) films as flexible substrates for supercapacitors, via facile in-situ chemical oxidative polymerization of aniline, with conventional chemical oxidative polymerization or rapid-mixing chemical oxidative polymerization technique. Owing to the grafting of PANI from the PVC-An film as substrate and the suppression of the secondary growth of the primary PANI particles in the rapid-mixing chemical oxidative polymerization, the PVC-g-PANI-2 composite film with loose surface possessed better comprehensive performance, accompanying the high specific capacitance (645.3F/g at a current density of 1A/g), good rate capacitance (retaining 63.2% of original value at a current density of 10A/g and 52.0% at a scan rate of 100mV/s), good cycle stability (retaining 83.1% after 1000 cycles) and the improved internal resistance. Besides its excellent flexibility, it could retain 61.2% of its original specific capacitance under the stress of 8.66MPa for 1h, demonstrating a good tensile-resistance. Copyright © 2017 Elsevier Inc. All rights reserved.

Radiation effect on PVC/ENR blends

International Nuclear Information System (INIS)

Chantara Thevy Ratnam; Khairul Zaman Mohd Dahlan

1997-01-01

The effect of irradiation on the physical properties of Polyvinyl Chloride / Epoxidised Natural Rubber Blends (PVC/ENR blends) were investigated. The enhancement in tensile strength, elongation at break, hardness and aging properties of the blends have confirmed the positive effect of irradiation on the blends. It is evident from gel fraction and infra red spectroscopic studies that the blends of PVC and ENR cross-linked upon irradiation. The results also revealed that at any blend composition, the enhancement in properties depend on irradiation dose which controls the degree of radiation induced cross-linking. In an attempt to maximize the constructive effect of irradiation, the influence of various additives such as stabilizers, radiation sensitizers, fillers and processing aids on the blend properties were studied. The changes in blend properties upon irradiation with the presents of above additives were also presented in this paper

MeV ion beam interaction with polymer films containing cross-linking agents

International Nuclear Information System (INIS)

Evelyn, A. L.

1999-01-01

Polymer films containing cross linking enhancers were irradiated with MeV alpha particles to determine the effects of MeV ion beam interaction on these materials. The contributed effects from the electronic and nuclear stopping powers were separated by irradiating stacked thin films of polyvinyl chloride (PVC), polystyrene (PS) and polyethersulfone (PES). This layered system allowed most of the effects of the electronic energy deposited to be experienced by the first layers and the last layers to receive most of the effects of the nuclear stopping power. RGA, Raman microprobe analysis, RBS and FTIR measured changes in the chemical structures of the irradiated films. The characterization resolved the effects of the stopping powers on the PVC, PS and PES and the results were compared with those from previously studied polymers that did not contain any cross linking agents

Bedside identification of patients at risk for PVC-induced cardiomyopathy: Is ECG useful?

Science.gov (United States)

Garster, Noelle C; Henrikson, Charles A

2017-07-01

Premature ventricular complexes (PVCs) are an underrecognized cause of cardiomyopathy. Standard 12-lead electrocardiogram (ECG) has potential to direct attention toward at-risk patients. We performed a single-center, retrospective chart review of 1,240 patients who completed ECG and Holter monitoring at Oregon Health and Science University Hospital between January 1, 2011 and December 31, 2013 to investigate the relationship of PVC frequency on ECG with burden on Holter. Primary outcome measures included PVC quantity on ECG, mean PVC quantity on Holter, and percentage of total beats on Holter recorded as PVCs. High PVC burden was defined as ≥10% of total beats. Weighted mean percentages of total beats on Holter monitor recorded as PVCs were calculated for 0, 1, 2, and ≥3 PVCs on ECG and found to be 1.4% (n = 1,128), 3.5% (n = 32), 4.3% (n = 25), and 16.6% (n = 55), respectively, which represent statistically significant differences (P ECG for ≥10% PVC Holter burden was 58%. Negative predictive value for 0 PVCs on ECG was 98%. The sensitivity and specificity of ECG to identify high PVC burden on Holter was 72% and 93.6%, respectively, when utilizing a positive ECG result as one PVC or more, and 44% and 98.9%, respectively, with ≥3 PVCs on ECG. The positive likelihood ratio corresponding to ≥3 PVCs on ECG was 40. These findings demonstrate that the number of PVCs on ECG can be utilized for quick bedside estimation of high PVC burden. © 2017 Wiley Periodicals, Inc.

Analysis of Polyadipate Ester Content in PVC Plastics by Means of FT-Raman Spectroscopy

DEFF Research Database (Denmark)

Berg, Rolf W.

2006-01-01

Plasticizers are needed in flexible PVC (PolyVinylChloride) products. There is serious concern that commonly used phthalate esters may harm life reproduction systems. To avoid the problems, instead adipate di-esters (AEs) of C8 to C10 alcohols are used as higher prized alternatives; e.g. di-2......-ethylhexyl adipate or DEHA [103-23-1], also known as Adimoll or di-octyl adipate, DOA. A widely used plasticizer in food (cling) films is DEHA, often in combination with polymers, epoxidized soya-bean oil, etcetera. DEHA also occurs in children toys. We have previously shown that the presence of phthalate...... esters in PVC can be rapidly analyzed by Fourier transform (FT-) Raman spectroscopy excited with a 1064 nm laser. Here in this project we report a similar study. The aim was to find out whether FT-Raman spectroscopy can be used to determine the presence of adipate esters (AEs) as plasticizers...

Evaluation of the influence of water and oil derivatives absorption on PVC pipes; Avaliacao da influencia da absorcao de agua e de derivados de petroleo em tubulacoes de PVC

Energy Technology Data Exchange (ETDEWEB)

Carpio, D.C.F. del; D' Almeida, J.R.M., E-mail: dalmeida@puc-rio.b [Pontificia Univ. Catolica do Rio de Janeiro (PUC-Rio), RJ (Brazil). Dept. de Engenharia de Materiais

2010-07-01

PVC is the only polymer of large consume that is not totally obtained from petroleum, since it contains 57% of chlorine. As chlorine containing materials are resistant to bacteria rich environments, such as buried pipes, PVC is being used for fluid transportation, principally water, but it can also be considered as an alternative material for the transportation of other fluids. This work analyzes the aging behavior of PVC exposed to water, ethanol and diesel oil, using TGA, DSC, FT-IR and DR-X techniques. The results showed that the chemical structure of PVC is not affected by exposure to water and ethanol. For these fluids a dipolar interaction could be occurring, increasing at the beginning of the absorption process, the polymer thermal stability. The diesel oil caused plasticization, with reduction of the Tg since the beginning of the aging process. (author)

PVC removal from mixed plastics by triboelectrostatic separation

International Nuclear Information System (INIS)

Park, Chul-Hyun; Jeon, Ho-Seok; Park, Jai-Koo

2007-01-01

Ever increasing oil price and the constant growth in generation of waste plastics stimulate a research on material separation for recycling of waste plastics. At present, most waste plastics cause serious environmental problems due to the disposal by reclamation and incineration. Particularly, polyvinyl chloride (PVC) materials among waste plastics generates hazardous HCl gas, dioxins containing Cl, and so on, which lead to air pollution and shorten the life of incinerator, and it makes difficultly recycling of other plastics. Therefore, we designed a bench scale triboelectrostatic separator for PVC removal from mixed plastics (polyvinyl chloride/polyethylene terephthalate), and then carried out material separation tests. In triboelectrostatic separation, PVC and PET particles are charged negatively and positively, respectively, due to the difference of the work function of plastics in tribo charger of the fluidized-bed, and are separated by means of splitter through an opposite electric field. In this study, the charge efficiency of PVC and PET was strongly dependent on the tribo charger material (polypropylene), relative humidity (below 30%), air velocity (over 10 m/s), and mixture ratio (PET:PVC = 1:1). At the optimum conditions (electrode potential of 20 kV and splitter position of -2 cm), PVC rejection and PET recovery in PET products were 99.60 and 98.10%, respectively, and the reproducibility of optimal test was very good (±1%). In addition, as a change of splitter position, we developed the technique to recover high purity PET (over 99.99%) although PET recovery decreases by degrees

Polarizing PVC — A Discrepant Event

Science.gov (United States)

Headly, David; Karabatek, Mohamed

2016-01-01

Each year when teaching polarization phenomena and the Triboelectric Series in a unit on electrostatics, I would balance some rods (2-3 ft in length) made from wood, aluminum, PVC, and Plexiglas on an inverted watch glass and demonstrate to the class how a party balloon rubbed with fake rabbit fur (charging the balloon negative) would always attract the uncharged rods, causing them to rotate towards the balloon (see Fig. 1). The fact that a charged object always attracts a neutral object due to the induced dipole in the latter is a great way to test if something is in fact charged. Surprisingly, the PVC pipe would usually, but not always, repel the charged balloon and rotate away! Repulsion means that neither of the objects are electrically neutral. In a separate test, after rubbing together a Plexiglas rod with a polyethylene grocery bag (making the rod positively charged and the bag negatively charged), the PVC usually attracts the rod. With the help of a student as part of his senior project, I finally decided to investigate further the source of the negative charge that exists on PVC. Specifically, is it nothing more than static charge that builds up on the pipe from unavoidable contact with its surroundings, or is it somehow intrinsic to the manufacturing process?

Características físicas de filmes biodegradáveis produzidos a partir de amidos modificados de mandioca Physical characteristics of cassava modified starch films

Directory of Open Access Journals (Sweden)

Celina Maria Henrique

2008-03-01

, foram mais permeáveis que o PVC. Porém, quando se compara o filme biodegradável de amidos modificados com o filme comercial de PVC, ainda há muito que se trabalhar na formulação para melhorar várias propriedades deste tipo de embalagem, que tem amplo uso atualmente.Cassava starches may be used as raw materials for developing biodegradable films. Some starch modification processes can make them miscible in cold water and others can modify their film properties, making them stronger and more flexible. The aim of this study was to evaluate the physical characteristics of biodegradable films developed from cassava modified starches using the casting process (dehydration of a filmogenic solution on Petri dishes. The modified starches used were cross linked, low and high viscosity carboxymethyl starches and esterified starch. Starch viscosity is an important property to produce the filmogenic solution and it was tested using the Rapid Visco Analyser (RVA. Excepting cross linked starch, all modified starches presented cold solubility. This property enables an easier preparation of the filmogenic solutions. However, all modified starches presented a severe reduction of setback values, property associated with film formation. The cassava modified starch films were compared to commercial PVC films of 0.0208 to 0.0217 mm thickness. The cassava modified starch films presented thickness values from 0.0551 to 0.1279 mm. The minimum thickness values were observed in pre-gelatinized and cross linked films. The scanning electron microscopy analysis of the films showed differences among the starches. The resulting films were transparent and homogeneous. There was no significant interference of film thickness in water vapor permeability and the films with 5% dry matter were more permeable than the PVC film. However, when modified starch films are compared to PVC commercial films, there is still much research to be made in the formulation to improve several properties necessary to

Electron beam crosslinked PVC : structure property relationships

International Nuclear Information System (INIS)

Gupta, Neeraj K.; Sabharwal, Sunil

2001-01-01

PVC is used extensively for its insulating properties for the manufacture of wires and cables and for other applications. Its gradual degradation, oxidation and even dehydro chlorination restricts use for long lasting period in installations such as high temperature zones, underground cables, communication systems, electro-nuclear facilities, etc. The technological properties and performance characteristics of PVC based insulation can be improved via crosslinking by high-energy electrons. PVC is however a polymer, which on irradiation predominantly undergoes degradation. To avoid degradation, it needs to be compounded with sensitizing agents or multifunctional monomers so that crosslinking is the predominant reaction. Radiation cross linkable formulations are complex mixtures of resin and various additives incorporated for achieving desired technological and performance characteristics, ease of processing and improving quality. The proper choice of additives and sensitizing agents enable low dose requirements for efficient crosslinking and improvements in various technological properties. The purposes of this work was to investigate the effect of using a binary sensitizer blend of a trifunctional monomer and a rubber in PVC, and develop suitable electron beam cross linkable formulations for wire insulation. This paper presents some aspects of the investigations and development of insulation demonstrated at industrial scale

Study of microporous PVA/PVC composite polymer membrane and it application to MnO2 capacitors

International Nuclear Information System (INIS)

Yang, C.-C.; Wu, G.M.

2009-01-01

A microporous poly(vinyl alcohol)/poly(vinyl chloride) (PVA/PVC) composite polymer membrane was successfully synthesized by a solution casting method and a preferential dissolution method. The characteristic properties of PVA/PVC composite polymer membranes were systematically studied by X-ray diffraction (XRD), scanning electron microscopy (SEM), thermal gravimetric analysis (TGA), micro-Raman spectroscopy and AC impedance spectroscopy. The PVA/PVC composite polymer membrane shows excellent thermal property, dimensional stability, and the ionic conductivity; it is due to the addition of secondary PVC polymer fillers. The MnO 2 capacitors with the PVA/PVC composite polymer membrane with 1 M Na 2 SO 4 was assembled and examined. It was found that the MnO 2 capacitor based on a microporous PVA/5 wt.%PVC composite polymer electrolyte membrane exhibited the maximum specific capacitance of 238 F g -1 and the current efficiency of 99% at 25 mV s -1 after 1000 cycle test. The result demonstrates that the novel microporous PVA/PVC composite polymer membrane is a potential candidate for use on the capacitors

Preparation of modified clay with benzethonium or cetylpyridinium chloride and evaluation of their interactions with PVC

International Nuclear Information System (INIS)

Resende, Daniel K.; Dornelas, Camila B.; Moreira, Leonardo A.; Gomes, Ailton S.; Tavares, Maria I.B.; Cabral, Lucio M.; Simeoni, Luiz A.

2009-01-01

The objective of this work was the preparation of modified clays with benzethonium or cetylpyridinium to obtain organophilic silicates with good stability and evaluate the possible use of them for the preparation of nanocomposites of poly(vinyl chloride) (PVC). The reactions of modification of clays and the PVC were prepared by solution intercalation. The new clays were evaluated by X-ray diffraction (XRD) and Low field nuclear magnetic resonance (NMR). The reactions of clays with PVC were assessed by Low-field NMR, through the determination of proton spin lattice relaxation time. The stability of new organophilic clays and their reactions with PVC were evaluated by thermogravimetric analysis (TGA). High stability was observed for organophilic clays prepared. The degradation of PVC materials obtained with the organophilic clay began at temperatures above 200 deg C. If it is considered that the temperatures normally used in the processing of PVC are between 140 deg C to 180 deg C, the observed results may indicate the possibility of the use of clays for preparation of nanomaterials with PVC. (author)

Preparation and characterization of PVC /ENR/CNTs Nano composites

International Nuclear Information System (INIS)

Ratnam, C.T.; Nur Azrini Ramlee; Keong, C.C.

2011-01-01

Poly (vinyl chloride), PVC/ epoxidized natural rubber blend, ENR/ carbon nano tubes, CNTs were prepared by using melt and solution blending methods. Addition of 2 phr of CNTs found to cause a drop in the tensile strength, Ts of the 50/ 50 PVC/ ENR blend. The nano composites prepared by the melt blending method exhibited higher values of Ts compared to the nano composites prepared by solution blending. Melt blending found to be an efficient method to prepare PVC/ ENR/ CNTs nano composites. (author)

Effect of Modified Natural Rubber on PVC-ENR Electrospun Membrane: Thermal and Morphological Studies

International Nuclear Information System (INIS)

Mahathir Mohamed; Dahlan Mohd; Ratnam, C.T.; Pairu Ibrahim

2016-01-01

Electrospun fibers membrane (EFM) based on modified epoxidized natural rubber (ENR) and polyvinyl chloride (PVC) was successfully prepared by electro spinning technique. Epoxidized natural rubber was firstly prepared in solution by using 5 L flask and exposed to high intensity UV lamp for degradation. The PVC/ ENR mixture solution concentration were about 16 wt% and blended for 5 hours for homogeneity. The PVC/ ENR mixture were electro spun to form fibers membrane. The sample of electro spun fibers membrane were cured by electron beam. The resulting membranes were characterized for thermal and morphological studies. Thermal decomposition behavior of EFM was analyzed by thermogravimetric analysis (TGA). Thermo gram from TGA showed two stages of degradation for all formulation (90:10, 80:20, 70:30 PVC/ ENR) from 240 to 265 degree Celsius and 400 to 410 degree Celsius, respectively. From the DSC thermo gram of PVC/ ENR electro spun fibers showed that the addition of ENR resulted in the shifting of glass transition temperature (Tg) towards lower temperatures. The morphology of electro spun fibers was examined using scanning electron microscopy and it showed a variety of fiber morphologies. (author)

Evaluation of the influence of water and oil derivatives absorption on PVC pipes

International Nuclear Information System (INIS)

Carpio, D.C.F. del; D'Almeida, J.R.M.

2010-01-01

PVC is the only polymer of large consume that is not totally obtained from petroleum, since it contains 57% of chlorine. As chlorine containing materials are resistant to bacteria rich environments, such as buried pipes, PVC is being used for fluid transportation, principally water, but it can also be considered as an alternative material for the transportation of other fluids. This work analyzes the aging behavior of PVC exposed to water, ethanol and diesel oil, using TGA, DSC, FT-IR and DR-X techniques. The results showed that the chemical structure of PVC is not affected by exposure to water and ethanol. For these fluids a dipolar interaction could be occurring, increasing at the beginning of the absorption process, the polymer thermal stability. The diesel oil caused plasticization, with reduction of the Tg since the beginning of the aging process. (author)

Production of PVC/Abs/Nbr blend and the study of its physical and mechanical properties, thermal behaviour and its morphology

International Nuclear Information System (INIS)

Mehrabzadeh, M.; Honarkar, H.

2001-01-01

In this research a product of triplet blend of polyvinyl chloride, acrylonitrile-butadiene-styrene, acrylonitrile butadiene rubber (PVC/Abs/Nbr) is obtained. The physical, mechanical and thermal behaviour as well as morphology of the blend were studied. Results show that optimum properties in ratio PVC/Abs: 60/40 is obtained. For substituting the Nbr by a portion of Dop to modify the migration to surface, a triplet blend of PVC/Abs/Nbr was made. Experiments with constant amount of Nbr and variable Dop and vice versa were carried out. For preparation of triplet blend from PVC/Abs, a ratio of 60/40 was used. The best results were obtained for a blend with Nbr (10%) and PVC powder, 20% Nbr and PVC granules containing 34% Dop and the thermo formability of PVC/Abs/Nbr blend was examined as well

Tratamento químico superficial e metalização de ABS, PVC e blendas de PVC/ABS

Directory of Open Access Journals (Sweden)

Ana Paula Kurek

2015-04-01

Full Text Available Visando à substituição do ABS em peças cromadas, amostras de PVC e blendas de PVC/ABS, na razão mássica de 20/80, 40/60 e 60/40, foram submetidas ao pré-tratamento em solução sulfocrômica sob diferentes condições de concentração, tempo e temperatura e sendo em seguida cromadas. As modificações na superfície das peças após o condicionamento foram analisadas por microscopia eletrônica de varredura, microscopia de força atômica e rugosidade. A qualidade da deposição metálica foi avaliada por inspeção visual e teste de adesão. Os resultados mostraram que, aumentando a concentração de PVC nas peças necessitou-se de condições operacionais mais agressivas, tais como maiores temperaturas de banho, tempo de imersão e concentração de solução sulfocrômica para que ocorresse a adesão da camada metálica. De todas as condições testadas com a solução condicionante sulfocrômica no tratamento das peças de PVC e blendas PVC/ABS de 20/80 e 40/60, a concentração de 350 g/L de ácido crômico e 400 g/L de ácido sulfúrico, temperatura de 70°C e tempo de imersão de 15 minutos, ocasionou deposição do metal em toda a superfície das peças, as quais foram aprovadas nos testes de adesão e corrosão.

Improvement of PVC floor tiles by gamma radiation

International Nuclear Information System (INIS)

Plessis, T.A. du; Badenhorst, F.

1988-01-01

Gamma radiation presents a unique method of transforming highly plasticized PVC floor tiles, manufactured at high speed through injection moulding, into a high quality floor covering at a cost at least 30% less than similarly rated rubber tiles. A specially formulated PVC compound was developed in collaboration with a leading manufacturer of floor tiles. These tiles are gamma crosslinked in its shipping cartons to form a dimensionally stable product which is highly fire resistant and inert to most chemicals and solvents. These crosslinked tiles are more flexible than the highly filled conventional PVC floor tiles, scratch resistant and have a longer lifespan and increased colour fastness. These tiles are also less expensive to install than conventional rubber tiles. (author)

Development of a continuous flow model system for studies of biofilm formation on polymers and its application on PVC-C and PVC-P

DEFF Research Database (Denmark)

Corfitzen, Charlotte B.; Albrechtsen, Hans-Jørgen

could be harvested from three different combinations of flow velocity and residence time. Biofilm formation was followed by ATP analysis on test material (chlorinated polyvinylchloride, PVC-C), negative control (stainless steel) and positive control (plasticized polyvinylchloride, PVC-P) incubated......-C, while most of the very deviating values for PVC-P were between 2-13,000 pg ATP/cm2. During 43 weeks of operation of the continuous flow model systems the biofilm formation increased on all three materials, with biofilm formation on PVC-C at the same level as on the negative steel control (values of 75...... system. In this study, a continuous flow model system was developed, for investigating biofilm formation on polymers, simulating conditions in the distribution system. Commercially available pipes were used for exchangeable test pieces, which allowed for testing over prolonged time periods. Test pieces...

Strength analysis of welded corners of PVC window profiles

Science.gov (United States)

Postawa, P.; Stachowiak, T.; Gnatowski, A.

2017-08-01

The article presents the results of researches which main purpose was to define the influence of welding parameters on strength of welded corners of PVC window profile. PVC profiles of a branded name GENEO® produced by Rehau Company were used for this research. The profiles were made by using a co-extrusion method. The surface of the profile was made of PVC mixture with no additives. Its main task was to get a smooth surface resistant to a smudge. The use of an unfilled polyester provides an aesthetic look and improves the resistance of extrudate to water getting into inner layers. The profile's inner layers have been filled up with glass fibre in order to improve its stiffness and mechanical properties. Window frames with cut corners used for this research, were produced on technological line of EUROCOLOR Company based in Pyskowice (Poland). The main goal of this analysis was to evaluate the influence of the main welding parameter (temperature upsetting) on hardness of welds we received in whole process. A universal testing machine was used for the research.

D-FNN Based Modeling and BP Neural Network Decoupling Control of PVC Stripping Process

Directory of Open Access Journals (Sweden)

Shu-zhi Gao

2014-01-01

Full Text Available PVC stripping process is a kind of complicated industrial process with characteristics of highly nonlinear and time varying. Aiming at the problem of establishing the accurate mathematics model due to the multivariable coupling and big time delay, the dynamic fuzzy neural network (D-FNN is adopted to establish the PVC stripping process model based on the actual process operation datum. Then, the PVC stripping process is decoupled by the distributed neural network decoupling module to obtain two single-input-single-output (SISO subsystems (slurry flow to top tower temperature and steam flow to bottom tower temperature. Finally, the PID controller based on BP neural networks is used to control the decoupled PVC stripper system. Simulation results show the effectiveness of the proposed integrated intelligent control method.

ELECTROCHEMICAL OXIDATION OF ETHANOL USING Ni-Co-PVC COMPOSITE ELECTRODE

Directory of Open Access Journals (Sweden)

Riyanto Riyanto

2011-07-01

Full Text Available The morphological characteristics and electrochemical behavior of nickel metal foil (Ni, nickel-polyvinyl chloride (Ni-PVC and nickel-cobalt-polyvinyl chloride (Ni-Co-PVC electrodes in alkaline solution has been investigated. The morphological characteristics of the electrode surface were studied using SEM and EDS, while the electrochemical behavior of the electrodes was studied using cyclic voltammetry (CV. It was found that composite electrodes (Ni-PVC and Ni-Co-PVC have a porous, irregular and rough surface. In situ studies using electrochemical technique using those three electrodes exhibited electrochemical activity for redox system, as well as selectivity in the electrooxidation of ethanol to acetic acid. The studies also found that an electrokinetics and electrocatalytic activity behaviors of the electrodes prepared were Ni metal foil

Phthalate Migration Study from PVC Grafted by Gamma Radiation

International Nuclear Information System (INIS)

Manzoli, J.E.; Duarte, C.; Somesari, E.; Silveira, C.; Paes, H.A.; Manzoli, J.E.; Araujo, F.D.C.; Panzarini, L.C.G.A.

2009-01-01

PVC is a useful polymer used for many applications, as packaging of food, blood and in contact with body fluids. The most widely-used plasticizer, to make it flexible, is the phthalate DEHP, and its toxicity is a problem. A special radiation grafting of PVC allows an important reduction of thrombogenic properties, and it could cause changes in the DEHP migration too. In this work it is presented the methodology using gas chromatography and numerical simulation for the measurement of DEHP migration from PVC grafted with monomer DMAEMA. The grafting could be an interesting way to reduce DEHP migration

Estudo do comportamento de compostos de PVC com adição de amido Study of the behavior of PVC compounds with added starch

Directory of Open Access Journals (Sweden)

Lisandra Abatti

2011-01-01

Full Text Available Este trabalho apresenta o estudo do comportamento de compostos de PVC com adição de amido para aplicação especialmente na indústria calçadista. As propriedades mecânicas dos compostos nas proporções de 5, 7,5 e 10% foram estudadas através de ensaios de tração. Também foram verificados os índices de fluidez, alterações de propriedades quando submetidos ao envelhecimento artificial em estufa e natural ao expor às intempéries e enterrar no solo. A viabilidade da aplicação na indústria calçadista foi feita por injeção em gáspeas e tiras de sandálias, com testes de resistência, flexão e testes de campo. Os resultados demonstraram que o acréscimo de amido ao PVC provoca perda nas propriedades mecânicas, justificado pela baixa resistência mecânica do amido em relação ao PVC. Após envelhecimento em estufa o processo de retrogradação do amido deixa os compostos mais rígidos e com menor fluidez. Quando expostos às intempéries e ao solo, o PVC pode ser degradado com perda de HCl, o que leva à acidificação do solo. Nas aplicações em calçados e sandálias a resistência mecânica não atende aos requisitos do mercado. Apesar do baixo custo, o fraco comportamento mecânico dificulta sua viabilização para substituição em escala.This paper deals with the behavior of PVC compounds with addition of starch for applications, especially in the footwear industry. The mechanical properties of the compounds in the proportions of 5, 7.5 and 10% were studied using tensile tests. Also investigated were the flow rates, in addition to changes in properties when the material was subjected to artificial aging in an oven and exposed to natural weather and buried in the soil. The feasibility of application in the industry was evaluated with tests of endurance, strength and field tests in injection uppers and straps of sandals. The results showed that the addition of starch to PVC causes loss of mechanical properties, owing to

Degradation of poly(vinyl chloride) films by X-rays radiation

International Nuclear Information System (INIS)

Sbampato, M.E.; Kawano, Y.

1984-01-01

The degradation of pure poly(vinyl chloride) (PVC) films has been studied by X-rays radiation in vacuum. The films are transparent and become yellow with the exposure of radiation and this colour is enhanced with the time of irradiation. The infrared, ultraviolet and visible spectra changed in the irradiated material. The IR spectra show changes in itensities and band shifting, particularly in the region of C-Cl stretching vibrations indicating the occurrence of dehydrochlorination and a change in the conformation of the degraded PVC. The ultraviolet and visible spectra of irradiated films show a strong absorption band at 240 nm and many shoulders which are associated to dyenes, carbonyl and polyenes with few double bonds formed. The shoulder numbers increase in the spectra of samples kept for three months. This effect indicates that with irradiation, HCl is evolved resulting in the formation of polyenyl radicals, which propagate after irradiation. At the same time, should occur the reaction of these radicals with the atmospheric oxygen with formation of C=0 bonds. (Author) [pt

PVC makers study expansions to meet demand growth

International Nuclear Information System (INIS)

Hunter, D.; Coeyman, M.

1993-01-01

As prospects for the polyvinyl chloride (PVC) industry continue to improve, the next batch of capacity increases is being studied. Vista Chemical (Houston) sees an opportunity to achieve what company president James R. Ball calls the lowest-cost capacity addition in the market, by debottlenecking its PVC plants at Aberdeen, MS and Oklahoma City. That would increase capacity 40%, adding 300 million lbs/year to Vista's 830 million lbs/year. US demand for PVC grew 12.5% through the first 10 months of 1992, to 7.3 billion lbs, according to the latest figures available from the Society of the Plastics Industry. Alan Bailey, Oxy-Chem's executive v.p./polymers and plastics, predicts a good demand year in 1993 - better even than 1992, driven by an upward trend in housing starts and a recovering economy

RETGEM with polyvinylchloride (PVC) electrodes

CERN Document Server

Razin, V I; Reshetin, A I; Filippov, S N

2009-01-01

This paper presents a new design of the RETGEM (Resistive Electrode Thick GEM) based on electrodes made of a polyvinylchloride material (PVC). Our device can operate with gains of 10E5 as a conventional TGEM at low counting rates and as RPC in the case of high counting rates without of the transit to the violent sparks. The distinct feature of present RETGEM is the absent of the metal coating and lithographic technology for manufacturing of the protective dielectric rms. The electrodes from PVC permit to do the holes by a simple drilling machine. Detectors on a RETGEM basis could be useful in many fields of an application requiring a more cheap manufacturing and safe operation, for example, in a large neutrino experiments, in TPC, RICH systems.

Study on the effect of stabilizers on discoloring of PVC by irradiation

International Nuclear Information System (INIS)

Peng Chaorong; Wang Jingxia; Chen Zhuping; Liu Siyang

2009-01-01

Composites of polyvinyl chloride (PVC) filled with stabilizers was irradiated by 60 Co γ-ray. The effect of different stabilizers on the radiation-induced discoloring of PVC was investigated and the structures of irradiated PVC were characterized by ultraviolet spectrum (UV) and Fourrier transfer infrared spectrum (FT-IR). It shows that the stabilizers including calcium stearate/zinc stearate, epoxidised oil, phosphite and photostabilizer can improve the property of resistance to radiation-induced discoloring of PVC, and phosphite can improve the property of resistance to radiation-induced oxidation of PVC. Among the stabilizers, formulations with calcium stearate/zinc stearate show high transparency and excellent property of resistance to radiation at same absorbed dose. Change rate of yellow index of formulation (calcium stearate: zinc stearate=2:1) has been determined to be 8.3% at the absorbed dose of 30 kGy. It has been found that the structures of PVC with numbers of conjugated double bond or α, β-unsaturated ketone are formed after irradiation by γ-rays. (authors)

Electron beam processing of PVC insulating material in presence of additives

International Nuclear Information System (INIS)

Sharma, V.K.; Bhattacharyya, P.K.

1994-01-01

Using electron beam radiation flexible PVC (polyvinyl chloride) was cross linked in the dose range up to 15 Mrad. The effect of sensitizers and other additives on the cross linking and other physical properties like tensile strength have been investigated. It has been found that tri functional sensitizer like TMPTM (tri methyl propane tri methacrylate) is better sensitizer for PVC. In presence of TMPTM the physical properties related to crosslinking are found to be better than some of the other sensitizers used. The results are discussed. (author). 2 refs., 2 figs

Investigating the effects of polymer molecular weight and non-solvent content on the phase separation, surface morphology and hydrophobicity of polyvinyl chloride films

Science.gov (United States)

Khoryani, Zahra; Seyfi, Javad; Nekoei, Mehdi

2018-01-01

The main aim of this research is to study the effects of polymer molecular weight as well as non-solvent concentration on the phase separation, surface morphology and wettability of polyvinyl chloride (PVC) films. Gel permeation chromatography (GPC) results showed that the Mn of the used PVC grades is 6 × 104, 8.7 × 104 and 1.26 × 105 g/mol. It was found that a proper combination of polymer molecular weight and non-solvent content could result in superhydrophobic and self-cleaning behaviors. Scanning electron microscopy (SEM) results demonstrated that addition of ethanol causes the polymer chains to be severely aggregated at the films' surface forming strand-like structures decorated by nano-scale polymer spheres. The polymer molecular weight was found to affect the degree of porosity which is highly influential on the hydrophobicity of the films. The mechanism of phase separation process was also discussed and it was found that the instantaneous demixing is the dominant mechanism once higher contents of non-solvent were used. However, a delayed demixing mechanism was detected when the lower molecular weight PVC has been used which resulted in a pore-less and dense skin layer. Differential scanning calorimetry was also utilized to study the crystallization and glass transition behavior of samples.

Model-based performance and energy analyses of reverse osmosis to reuse wastewater in a PVC production site.

Science.gov (United States)

Hu, Kang; Fiedler, Thorsten; Blanco, Laura; Geissen, Sven-Uwe; Zander, Simon; Prieto, David; Blanco, Angeles; Negro, Carlos; Swinnen, Nathalie

2017-11-10

A pilot-scale reverse osmosis (RO) followed behind a membrane bioreactor (MBR) was developed for the desalination to reuse wastewater in a PVC production site. The solution-diffusion-film model (SDFM) based on the solution-diffusion model (SDM) and the film theory was proposed to describe rejections of electrolyte mixtures in the MBR effluent which consists of dominant ions (Na + and Cl - ) and several trace ions (Ca 2+ , Mg 2+ , K + and SO 4 2- ). The universal global optimisation method was used to estimate the ion permeability coefficients (B) and mass transfer coefficients (K) in SDFM. Then, the membrane performance was evaluated based on the estimated parameters which demonstrated that the theoretical simulations were in line with the experimental results for the dominant ions. Moreover, an energy analysis model with the consideration of limitation imposed by the thermodynamic restriction was proposed to analyse the specific energy consumption of the pilot-scale RO system in various scenarios.

The pvc operon regulates the expression of the Pseudomonas aeruginosa fimbrial chaperone/usher pathway (cup genes.

Directory of Open Access Journals (Sweden)

Uzma Qaisar

Full Text Available The Pseudomonas aeruginosa fimbrial structures encoded by the cup gene clusters (cupB and cupC contribute to its attachment to abiotic surfaces and biofilm formation. The P. aeruginosa pvcABCD gene cluster encodes enzymes that synthesize a novel isonitrile functionalized cumarin, paerucumarin. Paerucumarin has already been characterized chemically, but this is the first report elucidating its role in bacterial biology. We examined the relationship between the pvc operon and the cup gene clusters in the P. aeruginosa strain MPAO1. Mutations within the pvc genes compromised biofilm development and significantly reduced the expression of cupB1-6 and cupC1-3, as well as different genes of the cupB/cupC two-component regulatory systems, roc1/roc2. Adjacent to pvc is the transcriptional regulator ptxR. A ptxR mutation in MPAO1 significantly reduced the expression of the pvc genes, the cupB/cupC genes, and the roc1/roc2 genes. Overexpression of the intact chromosomally-encoded pvc operon by a ptxR plasmid significantly enhanced cupB2, cupC2, rocS1, and rocS2 expression and biofilm development. Exogenously added paerucumarin significantly increased the expression of cupB2, cupC2, rocS1 and rocS2 in the pvcA mutant. Our results suggest that pvc influences P. aeruginosa biofilm development through the cup gene clusters in a pathway that involves paerucumarin, PtxR, and different cup regulators.

PVC flooring at home and development of asthma among young children in Sweden, a 10-year follow-up.

Science.gov (United States)

Shu, H; Jönsson, B A; Larsson, M; Nånberg, E; Bornehag, C-G

2014-06-01

The incidence of asthma and allergy has increased throughout the developed world over the past decades. During the same period of time, the use of industrial chemicals such as phthalates, commonly used as plasticizers in polyvinylchloride (PVC) flooring material, has increased. The aim of this study was to investigate whether PVC flooring in the home of children in the age of 1-5 years is associated with the development of asthma in 5- and 10-year follow-up investigations (n = 3228). Dampness in Buildings and Health Study (DBH Study) commenced in 2000 in Värmland, Sweden. The current analyses included subjects who answered all baseline and follow-up questionnaires. Logistic regression analyses were applied to questionnaire results. Children who had PVC floorings in the bedroom at baseline were more likely to develop doctor-diagnosed asthma during the following 10-year period when compared with children living without. There were indications that PVC flooring in the parents' bedrooms was strongly associated with the new cases of doctor-diagnosed asthma when compared with child's bedroom. Our results suggest that PVC flooring exposure during pregnancy could be a critical period in the development of asthma in children at a later time; prenatal exposure and measurements of phthalate metabolites should be included in the future. This study has found that PVC flooring material in early life was related to incidence of asthma during the following 10 years when compared with other flooring materials and especially when comparing with wood flooring type.The study has further indicated that PVC flooring in the parents’ bedroom (proxy for prenatal exposure) was more associated with the development of asthma than PVC in the child’s bedroom was. Our results suggest that PVC flooring exposure during pregnancy could be a critical period in the development of asthma in children at a later time. In future prospective cohort study, prenatal exposure and measurements of

The role of chlorine and additives of PVC-plastic in combustion

International Nuclear Information System (INIS)

Mattila, H.

1991-01-01

The PVC differs from other common plastics due to the chlorine content. As the PVC is combusted, the chlorine is released mainly as hydrogen chloride. The content of chlorinated hydrocarbons is small, but these can also contain polychlorinated dibenzofuranes and dibenzodioxines, which are extremely poisonous. The aim of this study was to find out, what is the portion of PVC combustion in total emission of chlorinated hydrocarbons. Additionally, the amounts chlorine coming into combustion process with ordinary fuels have been estimated, and they are compared with the amounts of PVC. The chloride content of municipal wastes vary in between 0.4-0.9 %. The portion of plastics is about 30 % of the total, and the rest being from paper, food , wood and garden wastes an textiles. Both organic and inorganic chlorine form gaseous hydrogen chlorid in combustion processes. HCl can then react with oxygen and produce caseous chlorine. This can react with unreacted carbon of the smoke and produce different kinds of chlorinated hydrocarbons. The portion of PVC of the chlorine going into combustion in Finland has been estimated to be about 1-2 %. Combustion tests were made using coal and bark and plastic waste as additional fuel. It was noticed that addition of plastic decreased the amount of polyaromatic hydrocarbons in the smoke. Chlorinated dioxins and furans occurred a little less in the gases of combustion of plastic mixtures not containing PVC than in reference tests, but they increased when PVC containing plastic mixture was combusted, but more chlorinated dioxins and furans were absorbed into fly ash, so the emissions remained almost the same

Comparison of wet and dry heat transfer and pressure drop tests of smooth and rough corrugated PVC packing in cooling towers

International Nuclear Information System (INIS)

Goshayeshi, H.R.; Missenden, J.F.

1998-01-01

This paper presents the results of an experimental investigation of the performance of a cooling tower with PVC packing. The following were examined; the effect of surface roughness, the effect of the angle of roughness and the effect of packing spacing. The investigation was divided into two parts: comparison of film heat transfer with air pressure drop, without water circulation and comparison of enthalpy change and pressure drop in the model cooling tower, with circulation of water. Seven commercial packing were investigated, covering a size range of 1.1< P/D<1.70 and 1≤p/e≤5 and a discussion of the dimensionless correlation resulting is given

Synthesis of AzPhchitosan-bifenthrin-PVC to protect cables against termites.

Science.gov (United States)

Zhang, Lingkun; Cai, Weiwei; Chen, Wu-Ya; Zhang, Li; Hu, Kaikai; Guan, Yan-Qing

2016-03-30

The destruction of PVC cables by termites is a continuing and long-standing problem, which can lead to power leakage and power cut. Given the environmental demerits of insecticide overuse, alternative methods of addressing this problem are a highly desirable goal. In this study, we used photo-immobilization to develop a chitosan carrier system to help bifenthrin immobilize on the surface of the PVC substrate. The immobilization was analyzed using nuclear magnetic resonance (NMR), UV absorption, reverse-phase high-performance liquid chromatography (RP-HPLC), Raman absorption spectroscopy, and thermal gravimetric analysis (TGA). The surface structure and biological activity of the embedded and immobilized bifenthrin were examined using scanning electron microscopy (SEM), atomic force microscopy (AFM), and X-ray photon-electron spectroscopy (XPS). Its efficacy was assessed in pest experiments. The results indicate a successful embedding and immobilization of bifenthrin. Furthermore, the chemical bonding network between AzPhchitosan, bifenthrin, and PVC is stable, guaranteeing no environmental release of bifenthrin, and also providing more efficacious protection against termites. The evidence suggests that this photo-immobilization of bifenthrin-embedded chitosan on the surface of PVC substrates is a novel and environmentally friendly technique for termite control. This paper also reports a modification of chitosan with respect to its novel application in environmental protection. Copyright © 2015 Elsevier Ltd. All rights reserved.

Conservação pós-colheita de carambola sob refrigeração com recobrimento de biofilme de gelatina e PVC

Directory of Open Access Journals (Sweden)

T. A. Oliveira

2015-12-01

Full Text Available O objetivo deste trabalho foi avaliar a Conservação pós-colheita de carambola com recobrimento de gelatina e PVC. Para isto, carambolas da cultivar ‘Gigante doce’ foram colhidas na maturidade fisiológica, transportadas para o Laboratório de Pós-colheita da Universidade Federal Rural do Semiárido sendo selecionadas quanto a maturação, sanificadas, secas e separadas em três grupos para a aplicação dos recobrimentos: os frutos foram recobertos  individualmente com uma solução filmogênica de gelatina a 10% com 1% de glicerol como agente plastificante, recobertos 4 frutos com filme flexível de policloreto de vinila (PVC de 15μm por bandeja e testemunha (sem recobrimento. Os frutos foram armazenados a 10±1 ºC e 85-90% de UR, avaliados em intervalo de cinco dias durante 20 dias quanto a perda de massa, coloração da casca, firmeza de polpa, sólidos solúveis, acidez titulável, pH e ácido ascórbico. O delineamento experimental utilizado foi inteiramente casualizados, em esquema fatorial 3 x 5, com  quatro  repetições de três frutos. O recobrimento de PVC foi mais eficiente em minimizar a perda de massa dos frutos de carambola durante o armazenamento refrigerado. Enquanto, o biofilme propiciou a manutenção da coloração verde do fruto por maior período de tempo. Verificou-se aumento no teor de ácido ascórbico e decréscimo na firmeza de polpa dos frutos com o tempo de armazenamento.Postharvest conservation Star fruit refrigerated with biofilm coating gelatin and PVCAbstract: The objective of this study was to evaluate the Star fruit post-harvest preservation with coating of gelatin and PVC. For this, starfruit cultivar 'sweet Giant' were harvested at physiological maturity, transported to the Postharvest Laboratory of the Federal Rural University of the Semi-Arid being selected as maturation, sanitized, dried and separated into three groups for the implementation of coatings: the fruits were coanting individually

A Laboratory Experimental Study: An FBG-PVC Tube Integrated Device for Monitoring the Slip Surface of Landslides

Science.gov (United States)

Zhang, Shaojie; Chen, Jiang; Teng, Pengxiao; Wei, Fangqiang; Chen, Qiao

2017-01-01

A new detection device was designed by integrating fiber Bragg grating (FBG) and polyvinyl chloride (PVC) tube in order to monitor the slip surface of a landslide. Using this new FBG-based device, a corresponding slope model with a pre-set slip surface was designed, and seven tests with different soil properties were carried out in laboratory conditions. The FBG sensing fibers were fixed on the PVC tube to measure strain distributions of PVC tube at different elevation. Test results indicated that the PVC tube could keep deformation compatible with soil mass. The new device was able to monitor slip surface location before sliding occurrence, and the location of monitored slip surface was about 1–2 cm above the pre-set slip surface, which basically agreed with presupposition results. The monitoring results are expected to be used to pre-estimate landslide volume and provide a beneficial option for evaluating the potential impact of landslides on shipping safety in the Three Gorges area. PMID:29084157

Effect of gamma radiation on the spectroscopic properties of Bromocresol green-polyvinyl chloride film

International Nuclear Information System (INIS)

Bera, Anuradha; Ram, Surendra; Singh, Shailendra K.; Vaijapurkar, S.G.

2009-01-01

Bromocresol Green (BCG) - Polyvinyl chloride (PVC) film was prepared by dispersing the dye in the polymer matrix in a suitable solvent medium in the presence of an organic base and then solvent casting the formulation in the form of transparent colored film. Preliminary studies through UV-Vis Spectroscopic measurements show that the prepared PVC - dye films was sensitive to gamma radiation almost linearly in the dose range upto 8 kGy range. This spectroscopic change becomes visually distinguishable from 4 kGy onwards until 8 kGy where it finally changes color from green to yellow, beyond which no significant optical change was observed. The gamma response of the film could be tailored by varying the concentration of the pH sensitive dye and the organic base. (author)

PET and PVC Separation with Hyperspectral Imagery

Science.gov (United States)

Moroni, Monica; Mei, Alessandro; Leonardi, Alessandra; Lupo, Emanuela; La Marca, Floriana

2015-01-01

Traditional plants for plastic separation in homogeneous products employ material physical properties (for instance density). Due to the small intervals of variability of different polymer properties, the output quality may not be adequate. Sensing technologies based on hyperspectral imaging have been introduced in order to classify materials and to increase the quality of recycled products, which have to comply with specific standards determined by industrial applications. This paper presents the results of the characterization of two different plastic polymers—polyethylene terephthalate (PET) and polyvinyl chloride (PVC)—in different phases of their life cycle (primary raw materials, urban and urban-assimilated waste and secondary raw materials) to show the contribution of hyperspectral sensors in the field of material recycling. This is accomplished via near-infrared (900–1700 nm) reflectance spectra extracted from hyperspectral images acquired with a two-linear-spectrometer apparatus. Results have shown that a rapid and reliable identification of PET and PVC can be achieved by using a simple two near-infrared wavelength operator coupled to an analysis of reflectance spectra. This resulted in 100% classification accuracy. A sensor based on this identification method appears suitable and inexpensive to build and provides the necessary speed and performance required by the recycling industry. PMID:25609050

PET and PVC separation with hyperspectral imagery.

Science.gov (United States)

Moroni, Monica; Mei, Alessandro; Leonardi, Alessandra; Lupo, Emanuela; Marca, Floriana La

2015-01-20

Traditional plants for plastic separation in homogeneous products employ material physical properties (for instance density). Due to the small intervals of variability of different polymer properties, the output quality may not be adequate. Sensing technologies based on hyperspectral imaging have been introduced in order to classify materials and to increase the quality of recycled products, which have to comply with specific standards determined by industrial applications. This paper presents the results of the characterization of two different plastic polymers--polyethylene terephthalate (PET) and polyvinyl chloride (PVC)--in different phases of their life cycle (primary raw materials, urban and urban-assimilated waste and secondary raw materials) to show the contribution of hyperspectral sensors in the field of material recycling. This is accomplished via near-infrared (900-1700 nm) reflectance spectra extracted from hyperspectral images acquired with a two-linear-spectrometer apparatus. Results have shown that a rapid and reliable identification of PET and PVC can be achieved by using a simple two near-infrared wavelength operator coupled to an analysis of reflectance spectra. This resulted in 100% classification accuracy. A sensor based on this identification method appears suitable and inexpensive to build and provides the necessary speed and performance required by the recycling industry.

Poly(vinyl chloride)-g-poly(2-(dimethylamino)ethyl methacrylate) graft copolymers templated synthesis of mesoporous TiO{sub 2} thin films for dye-sensitized solar cells

Energy Technology Data Exchange (ETDEWEB)

Patel, Rajkumar; Ahn, Sung Hoon; Seo, Jin Ah; Kim, Sang Jin; Kim, Jong Hak, E-mail: jonghak@yonsei.ac.kr [Yonsei University, Department of Chemical and Biomolecular Engineering (Korea, Republic of)

2012-07-15

A poly(vinyl chloride) (PVC) main chain was grafted with poly(2-(dimethylamino)ethyl methacrylate) (PDMAEMA) containing a quaternary amine group using atom transfer radical polymerization. The successful synthesis of a PVC-g-PDMAEMA graft copolymer was confirmed by Fourier transform infrared, nuclear magnetic resonance, thermogravimetric analysis, and transmission electron microscopy. The PVC-g-PDMAEMA graft copolymer was used as a structure-directing agent (SDA) for the fabrication of a mesoporous thin film containing a titanium dioxide (TiO{sub 2}) layer. To control the porosity of the resultant inorganic layer, the ratio of SDA to TTIP as well as the concentration of the sol-gel was varied. The structure and porosity of the mesoporous film were characterized by XRD and SEM analysis. The mesoporous TiO{sub 2} film fabricated on the FTO surface was used as a photoanode for the dye-sensitized solar cell (DSSC). DSSC performance was the greatest when using TiO{sub 2} film with a higher porosity and lower interfacial resistance. The highest energy conversion efficiency reached 3.2 % at 100 mW/cm{sup 2}, which was one of the highest reported values for a quasi-solid-state DSSC with 600-nm-thick TiO{sub 2} film.

Estado de mistura e dispersão da fase borrachosa em blendas PVC/NBR Phase separation and rubber phase dispersion in PVC/NBR blends

Directory of Open Access Journals (Sweden)

Fábio R. Passador

2006-01-01

Full Text Available Termoplásticos modificados com elastômeros têm despertado grande interesse de pesquisadores e de indústrias devido à atraente relação custo/benefício e a possibilidade de aumento significativo da tenacidade sob impacto de polímeros frágeis com a incorporação de uma fase borrachosa dispersa. Este artigo mostra a relação entre o estado de mistura e a dispersão da fase borrachosa em blendas de poli (cloreto de vinila (PVC com borracha nitrílica (NBR. O estado de mistura de blendas poliméricas é um fator muito importante a ser considerado no desenvolvimento destes tipos de materiais, uma vez que determina o nível de mistura molecular das blendas. A característica estrutural do PVC é responsável pela morfologia das blendas PVC/NBR, sendo que há uma otimização de propriedades mecânicas quando as partículas de borracha formam a morfologia "pseudo-network", ou seja, quando as partículas de borracha estão randomicamente dispersas entre as partículas primárias do PVC.Thermoplastics modified with elastomers have attracted great interest of researchers and industries due to the low cost/benefit relationship and the possibility of significant increase in the toughness of brittle polymers through the incorporation of a dispersed rubber phase. This article shows the relationship between the interaction between phases and rubber phase dispersion in poly (vinyl chloride/nitrile rubber blends. The interaction between components in polymer blends is an important factor to be considered in the development of this kind of materials because it determines the level of the mixture at the molecular level. The particulate nature of PVC and the degree of nitrile groups in the NBR are responsible to the PVC/NBR blends morphologies leading to an optimization of the mechanical properties when the rubber particles form a pseudo-network morphology with the rubber particles randomly dispersed in between the PVC primary particles.

Experimental Investigations on Combustion Behaviors of Live PVC Cables

Science.gov (United States)

Wang, Liufang; Zhang, Jiaqing; Zhang, Bosi; Liu, Min; Fan, Minghao; Li, Qiang

2018-03-01

This paper investigated the combustion behaviors of live PVC cables with overload currents experimentally. The smoke coefficient of released smoke and the released gas concentration were examined. The results indicate that the combustion of live PVC cables can be divided into four stages, i.e., core exposed with a little smoke, obvious flame, maximum smoke and smoke depress. For most cases, using blue laser is better than using rad laser, since the extinction coefficient of the rad laser was larger than that of the blue laser. The response time of the detection of the released typical gases due to cable pyrolysis decreased and the peak values of the typical gases increased with the overload currents. In addition, the time to reach the peak value of gas concentration also decreased with the overload currents.

Dosimetry of the JS-6500 industrial irradiator for the irradiation of the PVC graduated flasks; Dosimetria del irradiador industrial JS-6500 para la irradiacion de probetas de PVC

Energy Technology Data Exchange (ETDEWEB)

Castaneda F, A.; Carrasco A, H.; Martinez P, M.E. [Instituto Nacional de Investigaciones Nucleares, A.P. 18-1027, 11801 Mexico D.F. (Mexico)

2002-07-01

The dosimetry of the JS-6500 AECL irradiator was realized, outside of the industrial transportation rails to know the dose distribution, as well as its dose speed. This one with the intention of exposing to gamma radiation; plastified PVC graduated flasks and evaluating their interweavement or degradation or both. This study of dosimetry was carried out by means of a theoretical and experimental evaluation in air atmosphere. The results allow to know the irradiation conditions of the PVC graduated flasks as well as those results prove that has not a significant difference among the obtained result as theoretical as experimentally due to that the obtained result in the theoretical evaluation is 2.62 KGy/h and the result for the case of the experimental evaluation is 2.74 KGy/h. (Author)

The Paradigms They Are a-Changin': past, present and future of PVC bacteria research.

Science.gov (United States)

Rivas-Marín, Elena; Devos, Damien P

2018-06-01

These are exciting times for PVC researchers! The PVC superphylum is composed of the bacterial phyla Planctomycetes, Verrucomicrobia, Chlamydiae (those three founders giving it its name), Lentisphaerae and Kirimatiellaeota as well as some uncultured candidate phyla, such as the Candidatus Omnitrophica (previously known as OP3). Despite early debates, most of the disagreements that surround this group of bacteria have been recently resolved. In this article, we review the history of the study of PVC bacteria, with a particular focus on the misinterpretations that emerged early in the field and their resolution. We begin with a historical perspective that describes the relevant facts of PVC research from the early times when they were not yet termed PVC. Those were controversial times and we refer to them as the "discovery age" of the field. We continue by describing new discoveries due to novel techniques and data that combined with the reinterpretations of old ones have contributed to solve most of the discordances and we refer to these times as the "illumination age" of PVC research. We follow by arguing that we are just entering the "golden age" of PVC research and that the future of this growing community is looking bright. We finish by suggesting a few of the directions that PVC researches might take in the future.

Thermal stability of formulations of PVC irradiated with {gamma} of {sup 60}; Estabilidad termica de formulaciones de PVC irradiadas con {gamma} de {sup 60} Co

Energy Technology Data Exchange (ETDEWEB)

Martinez P, M.E.; Carrasco A, H. [ININ, A.P. 18-1027, 11801 Mexico D.F. (Mexico)]. E-mail: memp@nuclear.inin.mx; Castaneda F, A.; Benavides C, R.; Garcia R, S.P. [CIQA, 25100 Saltillo, Coahuila (Mexico)

2004-07-01

The industry of cables and wires frequently use cable isolations with base of formulations of PVC, in those that stabilizer has usually been used with the help of heavy metals, as the lead, which is toxic. To solve the problem, from the 2002 one has come studying in combined form in the National Institute of Nuclear Research ININ and the Center of Investigation in Applied Chemistry CIQA, the modifications induced by the radiation in formulations with the help of vinyl poly chloride PVC. In these formulations, prepared with cross linking agent, plastifying industrial grade, stuff and non toxic stabilizers of calcium estearate and zinc industrial grade, it is sought to replace the stabilizer of Pb. For this were irradiated it test tubes of PVC with gamma radiation of cobalt 60 to three different dose in atmospheres of air and argon. Later it was determined their thermal stability at different times of heating and it was measured the Young modulus by means of thermo mechanical analysis. Those results obtained together with other techniques of characterization suggest that the irradiated proposed formulation can substitute the one stabilized with lead. (Author)

Fittings of unplasticized polyvinyl chloride (PVC-U), chlorinated polyvinyl chloride (PVC-C) or acrylonitrile/butadiene/styrene (ABS) with plain sockets for pipes under pressure - Dimensions of sockets - Metric series

CERN Document Server

International Organization for Standardization. Geneva

1985-01-01

Fittings of unplasticized polyvinyl chloride (PVC-U), chlorinated polyvinyl chloride (PVC-C) or acrylonitrile/butadiene/styrene (ABS) with plain sockets for pipes under pressure - Dimensions of sockets - Metric series

Fabrication and characterization of functionalized surfaces with 3-amino propyltrimethoxysilane films for anti-infective therapy applications

Energy Technology Data Exchange (ETDEWEB)

Grumezescu, Valentina [Department of Science and Engineering of Oxide Materials and Nanomaterials, Faculty of Applied Chemistry and Materials Science, University Politehnica of Bucharest, 1–7 Polizu Street, 011061 Bucharest (Romania); Lasers Department, National Institute for Lasers, Plasma & Radiation Physics, P.O. Box MG-36, Magurele, Bucharest (Romania); Andronescu, Ecaterina [Lasers Department, National Institute for Lasers, Plasma & Radiation Physics, P.O. Box MG-36, Magurele, Bucharest (Romania); Holban, Alina Maria [Department of Science and Engineering of Oxide Materials and Nanomaterials, Faculty of Applied Chemistry and Materials Science, University Politehnica of Bucharest, 1–7 Polizu Street, 011061 Bucharest (Romania); Microbiology Immunology Department, Faculty of Biology, Research Institute of the University of Bucharest – ICUB, University of Bucharest, 1–3 Portocalelor Lane, Sector 5, 77206 Bucharest (Romania); Socol, Gabriel [Lasers Department, National Institute for Lasers, Plasma & Radiation Physics, P.O. Box MG-36, Magurele, Bucharest (Romania); Grumezescu, Alexandru Mihai, E-mail: grumezescu@yahoo.com [Department of Science and Engineering of Oxide Materials and Nanomaterials, Faculty of Applied Chemistry and Materials Science, University Politehnica of Bucharest, 1–7 Polizu Street, 011061 Bucharest (Romania); Ficai, Anton [Department of Science and Engineering of Oxide Materials and Nanomaterials, Faculty of Applied Chemistry and Materials Science, University Politehnica of Bucharest, 1–7 Polizu Street, 011061 Bucharest (Romania); Lazar, Veronica; Chifiriuc, Mariana Carmen [Microbiology Immunology Department, Faculty of Biology, Research Institute of the University of Bucharest – ICUB, University of Bucharest, 1–3 Portocalelor Lane, Sector 5, 77206 Bucharest (Romania); Trusca, Roxana [S.C Metav-CD S.A., 31 Rosetti Str., 020015 Bucharest (Romania); and others

2015-05-01

Graphical abstract: - Highlights: • Thin coatings based on 3-amino propyltrimethoxysilane with anti-adherent properties. • PVC modified surfaces with improved resistance to microbial colonization. • Firstly report on antimicrobial properties of 3-amino propyltrimethoxysilane. - Abstract: The purpose of this study was the fabrication of functionalized anti-adherent surfaces based on the polyvinyl chloride (PVC) coated with 3-amino propyltrimethoxysilane (APTMS) by matrix assisted pulsed laser evaporation (MAPLE) in order to improve the resistance of PVC based prosthetic devices to microbial colonization. Infrared microscopy (IRM) investigations of APTMS thin films proved the compositional homogeneity of the prepared thin film. Scanning electron microscopy (SEM) micrographs revealed a granular morphology with microspheres harboring a diameter between 15 and 60 nm. The microbiological assays proved that MAPLE deposited APTMS films inhibited the adherence capacity and biofilm development of Pseudomonas aeruginosa and Staphylococcus aureus strains. Furthermore, this material proved to be highly biocompatible, allowing the normal growth and development of human endothelial cells. These traits highlight the fact that the fabricated APTMS thin films may be efficiently used for improving different surfaces of medical use, including prostheses and implantable devices.

Fabrication and characterization of functionalized surfaces with 3-amino propyltrimethoxysilane films for anti-infective therapy applications

International Nuclear Information System (INIS)

Grumezescu, Valentina; Andronescu, Ecaterina; Holban, Alina Maria; Socol, Gabriel; Grumezescu, Alexandru Mihai; Ficai, Anton; Lazar, Veronica; Chifiriuc, Mariana Carmen; Trusca, Roxana

2015-01-01

Graphical abstract: - Highlights: • Thin coatings based on 3-amino propyltrimethoxysilane with anti-adherent properties. • PVC modified surfaces with improved resistance to microbial colonization. • Firstly report on antimicrobial properties of 3-amino propyltrimethoxysilane. - Abstract: The purpose of this study was the fabrication of functionalized anti-adherent surfaces based on the polyvinyl chloride (PVC) coated with 3-amino propyltrimethoxysilane (APTMS) by matrix assisted pulsed laser evaporation (MAPLE) in order to improve the resistance of PVC based prosthetic devices to microbial colonization. Infrared microscopy (IRM) investigations of APTMS thin films proved the compositional homogeneity of the prepared thin film. Scanning electron microscopy (SEM) micrographs revealed a granular morphology with microspheres harboring a diameter between 15 and 60 nm. The microbiological assays proved that MAPLE deposited APTMS films inhibited the adherence capacity and biofilm development of Pseudomonas aeruginosa and Staphylococcus aureus strains. Furthermore, this material proved to be highly biocompatible, allowing the normal growth and development of human endothelial cells. These traits highlight the fact that the fabricated APTMS thin films may be efficiently used for improving different surfaces of medical use, including prostheses and implantable devices

Study on the gamma radiolysis of poly (vinyl chloride). Application to the study on degradation by irradiation and leaching of industrial PVC

International Nuclear Information System (INIS)

Colombani, J.

2006-01-01

The works presented in this memory enter in the context of the management of plastic nuclear waste. This study was carried out on pure PVC and industrial PVC (formulated polymer). The radiolysis at high doses (up to 4 MGy) of pure PVC in anaerobic condition involves the formation of polyenyl radicals, polyenic sequences, hydrogen chloride and reactions of crosslinking. In aerobic condition, the radiolysis at high doses of pure PVC generates the formation of peroxyl radicals, hydrogen chloride, acid water, carboxylic acids, saturated or conjugated ketones and phenomena of scission. The production of HCl generated by irradiation of industrial PVC was carried out up to 40 MGy. The HCl formed by radiolysis is completely trapped by the calcic loads contained in industrial PVC and by the water produced by these reactions of trapping. A qualitative study on the formation of the products of radiolysis highlighted that the mechanisms of radiolysis of industrial PVC are different from those of pure PVC. This difference is due to the presence of additives belonging to the formulation of industrial PVC. The irradiation of plasticizers such as phthalic esters could induce the formation of radicals being able to react, by reaction of grafting, with the macro-radicals of PVC or with the polyenic sequences formed by radiolysis of PVC macromolecules. The results of leaching experiments tend to confirm this type of mechanism. (author)

Efficacy of UV-C irradiation for inactivation of food-borne pathogens on sliced cheese packaged with different types and thicknesses of plastic films.

Science.gov (United States)

Ha, Jae-Won; Back, Kyeong-Hwan; Kim, Yoon-Hee; Kang, Dong-Hyun

2016-08-01

In this study, the efficacy of using UV-C light to inactivate sliced cheese inoculated with Escherichia coli O157:H7, Salmonella Typhimurium, and Listeria monocytogenes and, packaged with 0.07 mm films of polyethylene terephthalate (PET), polyvinylchloride (PVC), polypropylene (PP), and polyethylene (PE) was investigated. The results show that compared with PET and PVC, PP and PE films showed significantly reduced levels of the three pathogens compared to inoculated but non-treated controls. Therefore, PP and PE films of different thicknesses (0.07 mm, 0.10 mm, and 0.13 mm) were then evaluated for pathogen reduction of inoculated sliced cheese samples. Compared with 0.10 and 0.13 mm, 0.07 mm thick PP and PE films did not show statistically significant reductions compared to non-packaged treated samples. Moreover, there were no statistically significant differences between the efficacy of PP and PE films. These results suggest that adjusted PP or PE film packaging in conjunction with UV-C radiation can be applied to control foodborne pathogens in the dairy industry. Copyright © 2016. Published by Elsevier Ltd.

Study of PVC membrane grafted by Acrylic Acid, Acrylonitrile and Acrylamide using preirradiation method

International Nuclear Information System (INIS)

Kattan, M.; Al-Kasseri, H.

2015-03-01

Grafting of acrylic acid, acrylamide and acrylonitrile onto poly vinyl chloride (PVC) films using gamma radiation has been carried out by both type direct and preirradiation methods. The effect of different parameter such as monomer concentration, inhibitor concentration, reaction temperature, reaction time and irradiation dose on the grafting yield were investigated. It was found that the grafting yield depends on these parameters. The grafting yield was strongly monomer dependent and grafting method: the highest was found for AAc by the preirradiation method. The samples were characterized by tensile strength measurement, swilling and ion uptake. The highest increase in swilling was observed on samples grafted with AAc by the preirradiation method.(author)

Experimental study of film media used for evaporative pre-cooling of air

International Nuclear Information System (INIS)

He, Suoying; Guan, Zhiqiang; Gurgenci, Hal; Hooman, Kamel; Lu, Yuanshen; Alkhedhair, Abdullah M.

2014-01-01

Highlights: • Two film media were experimentally studied in a low-speed wind tunnel. • Correlations for heat transfer coefficient and pressure drop were developed. • Cellulose media provide higher cooling efficiency and pressure drop than PVC media. • Water entrainment of PVC media happens even at relatively low air velocities. - Abstract: An open-circuit low-speed wind tunnel was used to study the performance of evaporative cooling with cellulose and Polyvinyl Chloride (PVC) corrugated media. These two film media were selected as part of a broader investigation on pre-cooling the entering air of natural draft dry cooling towers. The heat and mass transfer and pressure drop across the two media with three thicknesses (i.e., 100, 200 and 300 mm) were experimentally studied in the wind tunnel. The test data were non-dimensionalized and curve fitted to yield a set of correlations. It was found that the pressure drop range of the cellulose media is 1.5–101.7 Pa while the pressure drops of the PVC media are much lower with the range of 0.9–49.2 Pa, depending on the medium thickness, air velocity and water flow rate. The cooling efficiencies of the cellulose media vary from 43% to 90% while the cooling efficiencies of the PVC media are 8% to 65%, depending on the medium thickness and air velocity. The water entrainment off the media was detected by water sensitive papers, and found that the cellulose media have negligible water entrainment under the studied conditions while care must be taken in the use of PVC media as water entrainment happens even at relatively low air velocities

Polyfunctional monomers as additives for enhancing the radiation copolymerization of styrene with polyethylene, polypropylene, and PVC

International Nuclear Information System (INIS)

Ang, C.H.; Garnett, J.L.; Levot, R.; Long, M.A.

1982-01-01

Additives which can increase the yield in the radiation grafting of monomers to polymers are useful. The use of polyfunctional monomers as additives (approx. = 1% v/v) are shown to enhance significantly the copolymerization yields of styrene in methanol to films of polyethylene and polypropylene under certain radiation conditions. The results obtained when the polyolefins are replaced by PVC as backbone polymer in these accelerated grafting reactions are reported. Divinylbenzene (DVB) and trimethylolpropane triacrylate (TMPTA) were used as representative polyfunctional monomers for the enhancement effect. When polypropylene was used as backbone polymer, the inclusion of DVB significantly enhanced the radiation grafting of styrene in methanol at all monomer concentrations studied above 35%. At certain monomer concentrations (50% , 60%), the yield of graft copolymer was almost doubled by the addition of DVB. 3 tables. (DP)

Comparative Study of PVC-Free All-Solid-State, PVC Membrane, and Carbon Paste Ion-Selective Electrodes for the Determination of Dapoxetine Hydrochloride in Pharmaceutical Formulation.

Science.gov (United States)

Aziz, Azza; Khamees, Nesrin; Mohamed, Tagreed Abdel-Fattah; Derar, Abeer Rashad

2016-11-01

The potentiometric response characteristics and analytical applications of a poly(vinyl chloride) (PVC)-free all-solid-state ion-selective electrode for dapoxetine hydrochloride (DAP) are examined. The Nernstian response of the electrode was evaluated by comparison with PVC-based liquid membrane and carbon paste electrodes. The PVC-free electrode is prepared by direct incorporation of dapoxetine-tetraphenyl borate (DAP-TPB) as a sensing element into a commercial nail varnish containing cellulose acetate propionate. The composite was applied onto a 3 mm diameter graphite disk electrode. The electrode exhibited a Nernstian slope of 56.0 mV/decade in the concentration range of 1 × 10-4 to 1 × 10-2 mol/L with an LOD of 2 × 10-5 mol/L. The electrode is independent of pH in the range of 2 to 6 and showed good selectivity for DAP with respect to a large number of inorganic cations and amino acids. Comparable Nernstian slope, sensitivity, pH range, and selectivity pattern were obtained with a PVC membrane and a carbon paste incorporating DAP-TPB as a sensing element and dioctylphthalate as a solvent mediator. The electrodes were used for the determination of DAP in pure solution and in tablets without extraction with high accuracy and precision (RSD ≤ 2%). The nail varnish solid-state electrode is simple, economical, and rapid when compared with PVC membrane and carbon paste electrodes.

A new dyed poly (vinyl butyral) film for high-dose applications

International Nuclear Information System (INIS)

Eid, S.A.; Beshir, W.B.; Ebraheem, S.

2006-01-01

The polymer films under investigation are comprising a mixture of 2 dyes, namely, 2,6-dichlorophenol indophenol sodium salt (DCP), and bromo cresol green (BCG) indicator in presence of different concentrations of chloral hydrate. The color of this film changes from the blue to purple and finally to yellow, the bleaching reaction for DCP takes place in the beginning, giving the tinge of purple color, followed by the transformation of BCG to its acidic form due to the presence of chloral hydrate. The response of these films is affected by the change in chloral hydrate concentration and also the ratio of the 2 combined dyes. Accordingly, these films could be used as dosimeter in two steps color change indicators, in the dose range from 0.2 to 6 kGy. To examine their suitability for eventual application in different food radiation processing, the dosimetric parameters, e.g. dose response, effect of relative humidity during irradiation on response as well as pre-and post-irradiation stability of these film are investigated. Using the phenomenon of HCl generation from PVC under irradiation, ph-indicating dyes have been added to PVC. A chlorine-containing polymer is not necessary for this reaction to occur. A similar color change can be produced if chloro alkanes are present in the dye-containing matrix (Whittaker, 1990). Ueno (1988) developed a radiation dosimeter from acidity indicators by coating a high molecular weight polymer support (e.g. polyester film) with a composition containing a halogen-containing polymer (e.g. PVC), a pigment which changes color with the change of ph and a basic material (e.g. KOH in EtOH). For routine dose monitoring in radiation processing, the polymeric dyed flexible films are most commonly used as dosimeters and indicators for both electron beams and gamma rays (Ebraheem et al., 1999 and McLaughlin et al

Synthesis and characterization of Zn-doped MgAl-layered double hydroxide nanoparticles as PVC heat stabilizer

International Nuclear Information System (INIS)

Wang, Gongling; Yang, Mei; Li, Zhiwen; Lin, Kaifeng; Jin, Quan; Xing, Chaojian; Hu, Zhudong; Wang, Dan

2013-01-01

Zn-doped MgAl-layered double hydroxides (LDHs) with M 2+ /M 3+ = 2 and different molar ratios of Mg/Zn have been synthesized by modified homogeneous co-precipitation method and characterized by powder X-ray diffraction, Transmission electron microscopy, Fourier transform infrared spectrum and thermogravimetry, and differential thermal analysis techniques. The thermal stabilizing effects of different LDHs on PVC were studied by Congo red test and thermal aging test. All of the nanoparticles show plate-like morphology and the average diameter of particles is around 90 nm. Results show that the introduction of Zn increased the average bond length and area of the layers of LDHs, therefore enhanced the adsorption ability on HCl gas which was generated during degradation of PVC to improve the thermal stability of PVC. LDHs with molar ratio of Mg/Zn = 1.0 shows the best thermal stabilizing effect on PVC

Synthesis and characterization of Zn-doped MgAl-layered double hydroxide nanoparticles as PVC heat stabilizer

Energy Technology Data Exchange (ETDEWEB)

Wang, Gongling; Yang, Mei [Chinese Academy of Sciences, State Key Laboratory of Multiphase Complex Systems, Institute of Process Engineering (China); Li, Zhiwen; Lin, Kaifeng [Harbin Institute of Technology, Academy of Fundamental Interdisciplinary Sciences (China); Jin, Quan; Xing, Chaojian; Hu, Zhudong [Chinese Academy of Sciences, State Key Laboratory of Multiphase Complex Systems, Institute of Process Engineering (China); Wang, Dan, E-mail: danwang@mail.ipe.ac.cn [Harbin Institute of Technology, Academy of Fundamental Interdisciplinary Sciences (China)

2013-09-15

Zn-doped MgAl-layered double hydroxides (LDHs) with M{sup 2+}/M{sup 3+} = 2 and different molar ratios of Mg/Zn have been synthesized by modified homogeneous co-precipitation method and characterized by powder X-ray diffraction, Transmission electron microscopy, Fourier transform infrared spectrum and thermogravimetry, and differential thermal analysis techniques. The thermal stabilizing effects of different LDHs on PVC were studied by Congo red test and thermal aging test. All of the nanoparticles show plate-like morphology and the average diameter of particles is around 90 nm. Results show that the introduction of Zn increased the average bond length and area of the layers of LDHs, therefore enhanced the adsorption ability on HCl gas which was generated during degradation of PVC to improve the thermal stability of PVC. LDHs with molar ratio of Mg/Zn = 1.0 shows the best thermal stabilizing effect on PVC.

Electrochemical Behaviour of Ni and Ni-PVC Electrodes for the Electroxidation of Ethanol

International Nuclear Information System (INIS)

Mohd Syafiq Hamdan; Norazzizi Nordin; Siti Fathrita Mohd Amir; Riyanto; Mohamed Rozali Othman

2011-01-01

In this study, two nickel based electrodes were prepared; nickel foil and nickel-polyvinylchloride (Ni-PVC), in order to study their electrochemical behavior using cyclic voltammetry, CV and chronocoulometry, CC. Ni electrode was prepared from Ni metal foil while Ni-PVC electrode was prepared by mixing a weighed portion of Ni powder and PVC in THF solvent, swirled until the suspension was homogeneous and drying the suspension in an oven at 50 degree Celsius for 3 h. The dry sample was then placed in a 1 cm diameter stainless steel mould and pressed at 10 ton/ cm 2 . From CV data, Ni-PVC electrode showed a better electrochemical behavior compared to Ni metal foil electrode. The use of Ni-PVC electrode at higher concentration of supporting electrolyte (1.0 M KOH) was better than at lower concentration of the same supporting electrolyte in electroxidation of ethanol. In addition to acetic acid, the oxidation of ethanol also produced ethyl acetate and acetaldehyde. (author)

An Enhanced Soft Vibrotactile Actuator Based on ePVC Gel with Silicon Dioxide Nanoparticles.

Science.gov (United States)

Park, Won-Hyeong; Shin, Eun-Jae; Yun, Sungryul; Kim, Sang-Youn

2018-01-01

In this paper, we propose a soft vibrotactile actuator made by mixing silicon dioxide nanoparticles and plasticized PVC gel. The effect of the silicon dioxide nanoparticles in the plasticized PVC gel for the haptic performance is investigated in terms of electric, dielectric, and mechanical properties. Furthermore, eight soft vibrotactile actuators are prepared as a function of the content. Experiments are conducted to examine the haptic performance of the prepared eight soft vibrotactile actuators and to find the best weight ratio of the plasticized PVC gel to the nanoparticles. The experiments should show that the plasticized PVC gel with silicon dioxide nanoparticles improves the haptic performance of the plasticized PVC gel-based vibrotactile actuator, and the proposed vibrotactile actuator can create a variety of haptic sensations in a wide frequency range.

Thermal and catalytic decomposition behavior of PVC mixed plastic waste with petroleum residue

Energy Technology Data Exchange (ETDEWEB)

Ali, Mohammad Farhat; Siddiqui, Mohammad Nahid [Department of Chemistry, King Fahd University of Petroleum and Minerals, Dhahran 31261 (Saudi Arabia)

2005-08-15

The pyrolysis and hydropyrolysis of PVC mixed plastic waste alone and with petroleum residue was carried out at 150 and 350{sup o}C under N{sub 2} gas and at 430{sup o}C under 6.5MPa H{sub 2} gas pressure. The behavior of plastic waste during thermal and catalytic decomposition has also been studied in single- and two-stage reaction processes. In the individual pyrolysis process, both the petroleum residue and polystyrene (PS) undergo more than 90% conversion to liquid and gaseous products, whereas low-density polyethylene (LDPE) and high-density polyethylene (HDPE) yielded lower conversions products, and polypropylene (PP) and polyvinyl chloride (PVC) afforded somewhere a moderate to high conversion products. In a single-stage pyrolysis reaction, PVC was processed with petroleum residue at 150 and 430{sup o}C, under N{sub 2} gas for 1h at each temperature in a glass reactor. The model PVC and waste PVC showed slight variations in the products distribution obtained from the glass reactor. In two-stage process, model PVC, vacuum gas oil (VGO) and a number of different catalysts were used in a stainless steel autoclave micro tubular reactor at 350{sup o}C under the stream of N{sub 2} gas for 1h and at 430{sup o}C under 950psi (6.5MPa) H{sub 2} pressure for the duration of 2h. Significantly, different products distributions were obtained. Among the catalysts used, fluid catalytic cracking (FCC) and hydrocracking catalysts (HC-1) were most effective in producing liquid fuel (hexane soluble) materials. The study shows that the catalytic coprocessing of PVC with VGO is a feasible process by which PVC and VGO materials can be converted into transportation fuels.

Web Based ATM PVC Management

NARCIS (Netherlands)

van der Waaij, B.D.; Sprenkels, Ron; van Beijnum, Bernhard J.F.; Pras, Aiko

1998-01-01

This paper discusses the design of a public domain web based ATM PVC Management tool for the Dutch SURFnet research ATM network. The aim of this tool is to assists in the creation and deletion of PVCs through local and remote ATM network domains. The tool includes security mechanisms to restrict the

Thermogravimetric-Mass Spectrometric Study of the Pyrolysis Behavior of PVC

Institute of Scientific and Technical Information of China (English)

SUN Qing-lei; SHI Xin-gang; LIN Yun-liang; ZHU He; WANG Xiao; CHENG Chuan-ge; LIU Jian-hua

2007-01-01

The pyrolysis characteristics of PVC were systematically investigated using a Netzschne TG thermo-balance coupled to a quadrupole mass spectrometer. The pyrolysis conditions were 0.1 MPa of Ar, a heating rate of 10 ℃/min and a final temperature of 1000 ℃. Both the thermogravimetric properties and the simultaneous evolution of gaseous products during pyrolysis were studied. The TG/DTG results showed that as the pyrolysis temperature increases the weight loss and weight loss rate of PVC increases. Near 412 ℃ the weight loss rate attained its peak value. At higher temperatures the rate of loss gradually decreases. The gases evolved during thermogravimetric analysis were analyzed by a mass spectrometer, monitoring the relative intensity of HCl, C6H6, light hydrocarbon and chlorine-containing gases. The evolution curves showed that HCl, C6H6, light hydrocarbon and chlorine-containing gases all peak at about 416 ℃. This is consistent with the fact that the weight loss curves also peak at about 412 ℃. The extensive HCl evolution is consistent with the high chlorine content of PVC. The formation of these gases can be explained by considering these reactions: dehydrochlorination, intramolecular cyclization and the addition of HCl to unsaturated hydrocarbons.

Thermal stabilisation of pvc with jatropha seed, khaya seed and rubber seed oils. Effect of barium and cadmium soaps of the seed oils on the thermal degradation of pvc

International Nuclear Information System (INIS)

Okieimen, F.E.

2003-01-01

Polyvinyl chloride was mixed with barium and cadmium soaps of Jatropha seed, Khaya seed and rubber seed oils and mixtures of the metal soaps and degraded at 190 deg. C under oxidative and non oxidative conditions. The effectiveness of the additives in stabilizing PVC against thermal degradation was evaluated by comparing (a) the kinetic data measured at 1% conversion for the degradation of PVC in the presence of the additives with the corresponding values obtained in the absence of the additives (b) the intrinsic viscosity and level of unsaturation in the polymer samples degraded for the under graded polymer and (c) the thermogravimetric data obtained for the degradation of PVC in the presence of the additives at a constant heating rate of 10 degree C min/sup -1/ up to 500 degree C. It was found that the additives retarded the rate of dehydro chlorination of PVC (by up to about 50% and 1% conversion) and reduced the extent of decomposition of the polymer by as much as 60%. The mixtures of the metal soaps containing more than 70% (wt) cadmium soap showed marked synergistic stabilizing effect on the degradation of PVC. (author)

Selective flotation of PVC using gelatin and lignin alkali.

Science.gov (United States)

Yenial, Unzile; Kangal, Olgaç; Güney, Ali

2013-06-01

Recycling has become one of the most important issues as a result of increasing waste mass in present day. This is especially important for polymer wastes as they are hard to degenerate in nature. Today, most of the practical methods used for the recycling of waste mass, such as hand sorting, gravity separation, etc., cannot be performed successfully owing to close densities of polymers. Froth flotation can be used successfully and economically for this purpose. The main objective of this study was to investigate the effect of plasticizer reagents and the success of froth flotation at plastic recycling. In this study, lignin alkali and gelatin were used as plasticizer reagents. The effect of these reagents was searched with the parameters of pH, concentration, conditioning and flotation time. In the case of post-consumed polyethylene terephthalate and polyvinyl chloride (PVC), 98.9% purity of PVC was obtained at optimum conditions.

Investigation of dielectric behavior of the PVC/BaTiO3 composite in low-frequencies

Science.gov (United States)

Berrag, A.; Belkhiat, S.; Madani, L.

2018-04-01

Polyvinyl chloride (PVC) is widely used as insulator in electrical engineering especially as cable insulation sheaths. In order to improve the dielectric properties, polymers are mixed with ceramics. In this paper, PVC composites with different weight percentages 2 wt.%, 5 wt.%, 8 wt.% and 10 wt.% were prepared and investigated. Loss index (𝜀″) and dielectric constant (𝜀‧) have been measured using an impedance analyzer RLC. Fourier transform infrared (FTIR) spectroscopy, scanning electron microscopy (SEM) equipped with energy dispersive X-ray (EDX) have been used as characterization techniques. The incorporation of BaTiO3 does not modify the crystallinity and the morphology of the PVC but reduces the space charges, therefore the dielectric losses. The frequency response analysis has been followed in the frequency ranges (20-140 Hz and 115-1 MHz). Relaxation frequencies have been evaluated in each frequency range. Experimental measurements have been validated using Cole-Cole’s model. Experimental results show well that BaTiO3 as a filler improves the dielectric properties of PVC.

Thermal stability of formulations of PVC irradiated with γ of 60

International Nuclear Information System (INIS)

Martinez P, M.E.; Carrasco A, H.; Castaneda F, A.; Benavides C, R.; Garcia R, S.P.

2004-01-01

The industry of cables and wires frequently use cable isolations with base of formulations of PVC, in those that stabilizer has usually been used with the help of heavy metals, as the lead, which is toxic. To solve the problem, from the 2002 one has come studying in combined form in the National Institute of Nuclear Research ININ and the Center of Investigation in Applied Chemistry CIQA, the modifications induced by the radiation in formulations with the help of vinyl poly chloride PVC. In these formulations, prepared with cross linking agent, plastifying industrial grade, stuff and non toxic stabilizers of calcium estearate and zinc industrial grade, it is sought to replace the stabilizer of Pb. For this were irradiated it test tubes of PVC with gamma radiation of cobalt 60 to three different dose in atmospheres of air and argon. Later it was determined their thermal stability at different times of heating and it was measured the Young modulus by means of thermo mechanical analysis. Those results obtained together with other techniques of characterization suggest that the irradiated proposed formulation can substitute the one stabilized with lead. (Author)

Plastics piping systems for industrial applications : acrylonitrile-butadiene- styrene (ABS), unplasticized poly(vinyl chloride) (PVC-U) and chlorinated poly(vinyl chloride) (PVC-C) : specifications for components and the system : metric series

CERN Document Server

International Organization for Standardization. Geneva

2003-01-01

Plastics piping systems for industrial applications : acrylonitrile-butadiene- styrene (ABS), unplasticized poly(vinyl chloride) (PVC-U) and chlorinated poly(vinyl chloride) (PVC-C) : specifications for components and the system : metric series

Estimation of life of PVC cables

International Nuclear Information System (INIS)

Bora, J.S.; Babar, A.K.

1989-01-01

Life-spans at various extrapolated temperatures corresponding to early, mid and late-stage failures of PVC are quite consistent and is about 32 years at 30degC. For every 10degC rise in ambient temperature life becomes less than half. (author). 2 tabs

The synthesis of poly(vinyl chloride) nanocomposite films containing ZrO2 nanoparticles modified with vitamin B1 with the aim of improving the mechanical, thermal and optical properties.

Science.gov (United States)

Mallakpour, Shadpour; Shafiee, Elaheh

2017-01-01

In the present investigation, solution casting method was used for the preparation of nanocomposite (NC) films. At first, the surface of ZrO 2 nanoparticles (NPs) was modified with vitamin B 1 (VB 1 ) as a bioactive coupling agent to achieve a better dispersion and compatibility of NPs within the poly(vinyl chloride) (PVC) matrix. The grafting of modifier on the surface of ZrO 2 was confirmed by Fourier transform infrared spectroscopy and thermogravimetric analysis (TGA). Finally, the resulting modified ZrO 2 (ZrO 2 -VB 1 ), was used as a nano-filler and incorporated into the PVC matrix to improve its mechanical and thermal properties. These processes were carried out under ultrasonic irradiation conditions, which is an economical and eco-friendly method. The effect of ZrO 2 -VB 1 on the properties and morphology of the PVC matrix was characterized by various techniques. Field emission scanning electron microscopy and transmission electron microscopy analyses showed a good dispersion of fillers into the PVC matrix with the average diameter of 37-40 nm. UV-Vis spectroscopy was used to study optical behavior of the obtained NC films. TGA analysis has confirmed the presence of about 7 wt% VB 1 on the surface of ZrO 2 . Also, the data indicated that the thermal and mechanical properties of the NC films were enhanced.

Migration of additives from poly(vinyl chloride) (PVC) tubes into aqueous media

DEFF Research Database (Denmark)

Wang, Qian; Storm, Birgit Kjærside

2005-01-01

The stability and migration product of medical PVC tubes plasticized with polyadipates were investigated by ageing in phosphate buffer at pH 1.679 and water at different temperatures. Changes in the PVC tubes were studied by wtaer absorption, weight loss, Fourier infrared spectroscopy (FTIR.......5% and only a small amount of adipic acid migrated when a tube was aged at 37 C in water and phosphate buffer (pH 1.679), and at 70 C in water after 56 days. However, when aged at 70 and 110 C, gradual deactivation of heat stabilizer after 21 days of ageing in buffer solution and separation of plasticizer...... from PVC matrix occurred. When the tube was aged at 110 C, significant degradation of both polyadipates and PVC were observed. Adipic acid and 1,4-butanediol monomers and oligomers of polyadipate were the major migration products from polyadipates in the water ageing solution, while only a relatively...

Estudo do uso de plastificantes de fontes renovável em composições de PVC Study of the use of plasticizer from renewable sources in PVC compositions

Directory of Open Access Journals (Sweden)

Emerson Madaleno

2009-01-01

Full Text Available Polímeros sintéticos são largamente utilizados em diversos produtos devido às suas propriedades físicas, químicas e facilidade de transformação. O poli(cloreto de vinila, conhecido como PVC, é um dos polímeros mais versáteis desenvolvidos pelo homem, de grande utilidade para a sociedade moderna. Suas aplicações incluem: janelas, calhas de chuva, revestimentos de paredes, portas, papel de parede, mangueiras, brinquedos, calçados, bolsas de sangue e tubos para condução de água. Em todas estas aplicações são utilizados aditivos junto à resina de PVC, sendo que um dos aditivos mais utilizados é o plastificante. Este estudo apresenta a análise comparativa de formulações flexíveis de PVC, baseada em dois plastificantes de origem renovável (óleo vegetal modificado - OVM e óleo vegetal modificado e epoxidado - OVME, e também dois plastificantes petroquímicos convencionais, di(2-etilhexil ftalato - (DEHP ou DOP e di(2-etilhexil adipato - (DEHA ou DOA. Não foram observadas diferenças significativas entre as propriedades mecânicas das formulações. Os diferentes plastificantes demonstram influenciar na dureza e resistência química das formulações, sendo que o grupo epóxi e a maior massa molar no plastificante vegetal apresentam maior compatibilidade com a resina de PVC. A análise de MEV apresenta uma provável exudação do plastificante OVM da matriz do PVC.Synthetic polymers have been widely used in manufactured products because of their physical and chemical properties and low cost of production. Poly(vinyl chloride, called PVC, is a versatile, inexpensive plastic whose use has become pervasive in modern society. Its applications include window frames, rain gutters, wall paneling, doors, wallpapers, flooring, garden furniture, toys, blood bags and pipes. In all of these applications additives are used, with plasticizers being among the most important. This work shows a comparative study among distinct

Selective separation of virgin and post-consumer polymers (PET and PVC) by flotation method

International Nuclear Information System (INIS)

Burat, Firat; Gueney, Ali; Olgac Kangal, M.

2009-01-01

More and more polymer wastes are generated by industry and householders today. Recycling is an important process to reduce the amount of waste resulting from human activities. Currently, recycling technologies use relatively homogeneous polymers because hand-sorting waste is costly. Many promising technologies are being investigated for separating mixed thermoplastics, but they are still uneconomical and unreliable. At present, most waste polymers cause serious environmental problems. Burning polymers for recycling is not practiced since poisonous gases are released during the burning process. Particularly, polyvinyl chloride (PVC) materials among waste polymers generate hazardous HCl gas, dioxins containing Cl, etc., which lead to air pollution and shorten the life of the incinerator. In addition, they make other polymers difficult to recycle. Both polyethylene terephthalate (PET) and PVC have densities of 1.30-1.35 g/cm 3 and cannot be separated using conventional gravity separation techniques. For this reason, polymer recycling needs new techniques. Among these techniques, froth flotation, which is also used in mineral processing, can be useful because of its low cost and simplicity. The main objective of this research is to recycle PET and PVC selectively from post-consumer polymer wastes and virgin polymers by using froth flotation. According to the results, all PVC particles were floated with 98.8% efficiency in virgin polymer separation while PET particles were obtained with 99.7% purity and 57.0% efficiency in post-consumer polymer separation.

In vitro quality of apheresis platelets divided into paediatric-sized units and stored in PVC bags plasticised with TOTM, BTHC or DINCH.

Science.gov (United States)

Bashir, S; Meli, A; Cardigan, R

2018-04-11

Two of the predictive factors of the quality of small volumes of platelets suitable for paediatric use are bag size and material. This study evaluated the storage properties of paediatric platelet aliquots in TOTM-, BTHC- or DINCH-PVC bags. (i) Three apheresis platelet concentrates (PC) were pooled and split into three units. One was retained as an adult unit (control; polyolefin bag). The second and third units were split into four MacoPharma TOTM-PVC and BTHC-PVC paediatric bags, respectively. (ii) Two apheresis PC were pooled and split into two units. One PC was retained as an adult unit, and the other was split into four Fresenius DINCH-PVC paediatric bags. Testing was performed on storage for pH, blood gases, hypotonic shock response, soluble CD62P, LDH, glucose and lactate, ATP, CD62P, CD63, platelet-derived microparticles and annexin V. The volumes, platelet yields and pH of all paediatric units met local specifications. The TOTM-PVC bag showed no worse quality than the adult bag up to day 7 for all parameters studied, and it maintained pH higher than BTHC-PVC and DINCH-PVC over storage. The BTHC-PVC bag was shown to be the most gas permeable; however, it had the highest glucose consumption rates and the highest platelet activation. All bags showed an acceptable in vitro quality. Overall, the TOTM-PVC paediatric bag showed better platelet quality compared to the other storage bags, whereas storage in the BTHC-PVC bag resulted in poorer platelet quality. © 2018 British Blood Transfusion Society.

COMPORTAMIENTO DE UN CEMENTO ASFÁLTICO MODIFICADO CON UN DESECHO DE PVC

Directory of Open Access Journals (Sweden)

Fredy Alberto Reyes Lizcano

2013-06-01

Full Text Available Las propiedades físicas y reológicas a altas temperaturas de servicio de un cemento asfáltico (CA modificado con un desecho de policloruro de vinilo (PVC fueron evaluadas y son presentadas en el artículo. Adicionalmente se presenta la influencia del tiempo de mezcla del CA con el PVC y el envejecimiento a corto plazo. Un incremento notable en la rigidez y la resistencia a fluir se reporta cuando se adiciona el desecho de PVC a un CA 80-100. De la misma forma, se reporta un incremento en la temperatura máxima de operación en servicio del ligante modificado.

Discoloration of polyvinyl chloride (PVC) tape as a proxy for water-table depth in peatlands: validation and assessment of seasonal variability

Science.gov (United States)

Booth, Robert K.; Hotchkiss, Sara C.; Wilcox, Douglas A.

2005-01-01

Summary: 1. Discoloration of polyvinyl chloride (PVC) tape has been used in peatland ecological and hydrological studies as an inexpensive way to monitor changes in water-table depth and reducing conditions. 2. We investigated the relationship between depth of PVC tape discoloration and measured water-table depth at monthly time steps during the growing season within nine kettle peatlands of northern Wisconsin. Our specific objectives were to: (1) determine if PVC discoloration is an accurate method of inferring water-table depth in Sphagnum-dominated kettle peatlands of the region; (2) assess seasonal variability in the accuracy of the method; and (3) determine if systematic differences in accuracy occurred among microhabitats, PVC tape colour and peatlands. 3. Our results indicated that PVC tape discoloration can be used to describe gradients of water-table depth in kettle peatlands. However, accuracy differed among the peatlands studied, and was systematically biased in early spring and late summer/autumn. Regardless of the month when the tape was installed, the highest elevations of PVC tape discoloration showed the strongest correlation with midsummer (around July) water-table depth and average water-table depth during the growing season. 4. The PVC tape discoloration method should be used cautiously when precise estimates are needed of seasonal changes in the water-table.

Preparation of Non-Woven Fiber Mats by Mixture of PVC and Epoxidized Natural Rubber

International Nuclear Information System (INIS)

Muhammad Hariz Othman; Mahathir Mohamed; Dahlan Mohd

2014-01-01

Eletrospun non-woven fibre mats prepared from ENR modified PVC were successfully fabricated at ambient temperature by electro spinning method. Liquid epoxidized natural rubber (LENR) was used because it is easier to handle compared to dried ENR. PVC was mixed with LENR based on 3 different ratios (9:1, 8:2 and 7:3). The effect of ENR on electrospinnibality of PVC was investigated.The morphologies and thermal properties of the electro span fibre mats were characterized and assessed using scanning calorimetry (DSC). The polymer solution concentration 16 aut % formed a diameter of the fibres were mainly affected by the addition of natural rubber and weight ratio of the solution. The diameter of the fibres also decreased with increasing amount of LENR in the solution. Thermal degradation involved two-step degradation with the first degradation representing the dehydro chlorination of PVC to form polyene and followed by the decomposition of LENR and the polyene.Addition of LENR into the sample caused the T g of electro spun fibre mats of PVC/LENR to shift toward lower temperature. (author)

Effect of PVC on ionic conductivity, crystallographic structural, morphological and thermal characterizations in PMMA-PVC blend-based polymer electrolytes

International Nuclear Information System (INIS)

Ramesh, S.; Liew, Chiam-Wen; Morris, Ezra; Durairaj, R.

2010-01-01

In this paper, temperature dependence of ionic conductivity, crystallographic structural, morphological and thermal characteristics of polymer blends of PMMA and PVC with lithium bis(trifluoromethanesulfonyl) imide (LiTFSI) as a dopant salt are investigated. The study on the temperature dependence of ionic conductivity shows that these polymer blends exhibit Arrhenius behavior. The highest ionic conductivity was achieved when 70 wt% of PMMA was blended with 30 wt% of PVC. X-ray diffraction (XRD) and scanning electron microscopy (SEM) reveal the amorphous nature and surface morphology of polymer electrolytes, respectively. In DSC analysis it was found that the glass transition temperature (T g ) and melting temperature (T m ) decreased, whereas the decomposition temperature (T d ) increased. In contrast, the shift towards higher decomposition temperature and decrease in weight loss of polymer electrolytes, in TGA studies, indicates that the thermal stability of polymer electrolytes improved.

Dose Rate Effect on Grafting by Gamma Radiation of DMAEMA onto Flexible PVC

International Nuclear Information System (INIS)

Panzarini, L.C.G.A.; Araujo, F.D.C.; Martinello, V.C.; Somesari, E.; Manzoli, J.E.; Silveira, C.; Paes, H.A.; Moura, E.

2009-01-01

Intravenous tubing, blood bags and catheters stays in contact with blood and body fluids. They are normally made by flexible PVC. The contact of PVC with this fluid is not possible for long periods and there is the necessity of addition of non-thrombogenic substances into blood. This work shows the radiation grafting process to produce copolymer PVC-g-DMAEMA, a new material that allows a future grafting of Heparin on it, and will have the perspective of avoiding undesirable substances additions to blood or body fluid contact. In this preliminary work, only radiation dose rate effect on grafting was studied

[Effectiveness of the transparent sterile dressing vs standard to fix the peripheral venous catheter (PVC) on the incidence of phlebitis. A randomized controlled trial].

Science.gov (United States)

Forni, Cristiana; D'Alessandro, Fabio; Gambino, Orazio; Amodeo, Alfredo; Pignotti, Elettra; Zanotti, Enrichetta; Tremosini, Morena; Trofa, Carmela; Sabattini, Tania; Matino, Federica; Genco, Rossana; Schiavone, Miguel; Bombino, Caterina; Mini, Sandra; Rocchegiani, Laura; Notarnicola, Teresa; Capezzali, Daniela; Boschi, Rita; Loro, Loretta

2012-01-01

Effectiveness of the transparent sterile dressing vs standard to fix the peripheral venous catheter (PVC), on the incidence of phlebitis. A randomized controlled trial. The type of dressing could contribute to the incidence of phlebitis, infiltration and accidental removals but the results of the studies are contrasting and samples are limited. To compare the effectiveness of a transparent polyurethane sterile dressing on the rate of phlebitis associated to peripheral venous catheter (PVC) vs a non sterile sticking plaster in use in current practice (standard dressing). Randomized controlled trial. Participants. 1061 PVCs (703 patients, adults and children) at a research orthopedic hospital in the north of Italy; 540 PVCs allocated to receive the sterile and 521 the standard dressing. 96 PVCs were excluded for phlebitis, 48 (9.6%) in the sterile and 48 (10.1%) in the standard dressing group, RR 0.96 (95%CI 0.697 - 1.335). Accidental removal of the PVCs was more frequent with the sterile dressing (9.6% vs 6.3%) but the number of catheters removed without complications was larger in the standard dressing group (48.9% vs 54.9% P=0.0503). Eighty-five PVCs were replaced for detachment of the dressing (50, 9.2% sterile and 35, 6.7% standard dressing). The cheapest transparent sterile dressing costs 32 cents while the standard 9 cents. A sticking non sterile plasters is not influential on the rate of phlebitis and ensures an good fix of the PVC compared the transparent sterile dressing to of polyurethane film.

Influência do tipo de agente de partição da borracha nitrílica na obtenção de blendas PVC/NBR Influence of the partitioning agent on the preparation of PVC/NBR Blends

Directory of Open Access Journals (Sweden)

Fábio R. Passador

2008-09-01

Full Text Available Borrachas nitrílicas para utilização em misturas com PVC são fornecidas em forma de pó, que são recobertas com um agente de partição para evitar compactação do produto no transporte e armazenamento, além de garantir alta fluidez e livre escoamento. Neste trabalho, buscou-se estudar a influência do tipo de agente de partição da borracha nitrílica (resina de PVC e CaCO3 na obtenção de blendas PVC/NBR. As propriedades mecânicas das blendas foram avaliadas por ensaios de tração, rasgo e dureza. As blendas com NBR com agente de partição de PVC apresentaram maior tensão na ruptura e módulo elástico que as blendas em que utilizaram NBR com agente de partição de CaCO3. A morfologia foi avaliada por microscopia eletrônica de varredura sendo bastante afetada pelo tipo de agente de partição.Nitrile rubbers used in mixture with PVC resin are supplied in powder. This kind of nitrile rubber has a partitioning agent to avoid agglomeration in the particles during the transport and storage. In this study, the influence of the partitioning agent on the preparation of PVC/NBR blends was investigated. The mechanical properties of the blends were evaluated by tensile properties, tear strength and hardness. The PVC/NBR blends with partitioning agent of PVC showed an increase in the tensile stress and Young's modulus compared to the PVC/NBR blends with partitioning agent of CaCO3. The morphology of the blends examined by scanning electron microscopy demonstrated the influence of the partitioning agent.

PVC posting bags for glove boxes

International Nuclear Information System (INIS)

1976-12-01

This specification covers the materials, measurements and manufacture of unpigmented PVC posting bags for use on glove boxes, together with methods of testing the materials. These bags are used in the handling of radioactive and toxic materials of a hazardous nature and therefore must be of the highest standard of mechanical strength, leak tightness and general finish. (author)

Effect of PVC on ionic conductivity, crystallographic structural, morphological and thermal characterizations in PMMA-PVC blend-based polymer electrolytes

Energy Technology Data Exchange (ETDEWEB)

Ramesh, S., E-mail: rameshtsubra@gmail.com [Centre for Ionics University Malaya, Department of Physics, Faculty of Science, University of Malaya, Lembah Pantai, 50603 Kuala Lumpur (Malaysia); Liew, Chiam-Wen; Morris, Ezra; Durairaj, R. [Faculty of Engineering and Science, Universiti Tunku Abdul Rahman, Setapak, 53300 Kuala Lumpur (Malaysia)

2010-11-20

In this paper, temperature dependence of ionic conductivity, crystallographic structural, morphological and thermal characteristics of polymer blends of PMMA and PVC with lithium bis(trifluoromethanesulfonyl) imide (LiTFSI) as a dopant salt are investigated. The study on the temperature dependence of ionic conductivity shows that these polymer blends exhibit Arrhenius behavior. The highest ionic conductivity was achieved when 70 wt% of PMMA was blended with 30 wt% of PVC. X-ray diffraction (XRD) and scanning electron microscopy (SEM) reveal the amorphous nature and surface morphology of polymer electrolytes, respectively. In DSC analysis it was found that the glass transition temperature (T{sub g}) and melting temperature (T{sub m}) decreased, whereas the decomposition temperature (T{sub d}) increased. In contrast, the shift towards higher decomposition temperature and decrease in weight loss of polymer electrolytes, in TGA studies, indicates that the thermal stability of polymer electrolytes improved.

Plastics piping systems for industrial applications – Acrylonitrile-butadiene-styrene (ABS), unplasticized poly(vinyl chloride) (PVC-U) and chlorinated poly(vinyl chloride) (PVC-C) – Specifications for components and the system – Metric series

CERN Document Server

Deutsches Institut für Normung. Berlin

2003-01-01

Plastics piping systems for industrial applications – Acrylonitrile-butadiene-styrene (ABS), unplasticized poly(vinyl chloride) (PVC-U) and chlorinated poly(vinyl chloride) (PVC-C) – Specifications for components and the system – Metric series

Optimization of the thickness of a conducting polymer, polyaniline, deposited on the surface of poly(vinyl chloride) membranes: a new way to improve their potentiometric response.

Science.gov (United States)

Shishkanova, T V; Matejka, P; Král, V; Sedenková, I; Trchová, M; Stejskal, J

2008-08-29

Repeated depositions of polyaniline (PANI) have been used to control the thickness of the polymeric film deposited on poly(vinyl chloride) (PVC) membrane surface. The oxidation of aniline was carried out in a dispersion mode, i.e. in the presence of poly(N-vinylpyrrolidone) (PVP). Two kinds of PVC were used for this purpose: a non-plasticized PVC for the study of PANI deposition and PVC, plasticized with nitrophenyl octyl ether (NPOE), as a prototype of a liquid membrane electrode. The results of UV-visible and FTIR spectroscopies and electron microscopy showed that (1) the film thickness increased by about equal increments of approximately 40 nm after each polymerization, and (2) the interface with PVC was constituted by PANI film and adhering PANI-PVP colloidal particles. The various thicknesses of the deposited PANI films affected the potentiometric response of the NPOE/PVC membrane with and without an anion-exchanger. The potentiometric anionic response was observed with a minimal thickness of PANI film on the blank NPOE/PVC membrane. Sensitivity of the PANI film to pH occurred only with a blank NPOE/PVC membrane coated with a thick polymeric film, while it was strongly suppressed by the presence of a lipophilic anion-exchanger, tridodecylmethylammonium chloride (TDDMACl), in the membrane, regardless of the thickness of the polymer film. The thickness of the PANI film did not affect the anionic selectivity pattern of TDDMACl-based membranes to any great extent, but its presence improved and stabilized their potentiometric characteristics (sensitivity, linear-response range).

The 1st EMBO workshop on PVC bacteria-Planctomycetes-Verrucomicrobia-Chlamydiae superphylum: exceptions to the bacterial definition?

Science.gov (United States)

Devos, Damien P; Jogler, Christian; Fuerst, John A

2013-10-01

The PVC superphylum is a phylogenetically supported collection of various related bacterial phyla that comprise unusual characteristics and traits. The 'PVC' abbreviation derives from Planctomycetes, Verrucomicrobia and Chlamydiae as members of this superphylum, while additional bacterial phyla are related. There has recently been increasing and exciting interest in the cell biology, physiology and ecology of members of this superphylum, including evolutionary implications of the complex cell organization of some species. It is timely that international researchers in the PVC superphylum field met to discuss these developments. The first meeting entirely dedicated to those bacteria, the EMBO workshop "PVC superphylum: Exceptions to the bacterial definition" was held at the Heidelberg University to catalyze the formation of a vital scientific community supporting PVC-bacterial research. More than 45 investigators from more than 20 countries (PIs, senior scientists and students) attended the meeting and produced a great starting point for future collaborative research. This Special Issue will focus on the EMBO-PVC meeting. This Perspective briefly summarizes the history of PVC-research, focusing on the key findings and provides a brief summary of the meeting with a focus on the major questions that arose during discussion and that might influence the research in the years to come.

Karakteristik sifat mekanik, ketahanan api dan pembakaran, dan morfologi nanokomposit campuran PVC dan LDPE

Directory of Open Access Journals (Sweden)

Arum Yuniari

2014-06-01

Full Text Available The purpose of the study was to determine the effect of addition of low density polyethylene (LDPE and flame retardant on mechanical properties, resistant to fire and burning and morphology from the mixture of polyvinyl chloride (PVC, LDPE, flame retardant, and nanoprecipitated calcium carbonate (NPCC as filler. The materials were mixed in laboplastomill at 215 ºC, torque speed 50 rpm, for 10 minutes. Nanocomposite was prepared by PVC/LDPE variations of 100/15; 100/20; 100/25; and 100/30 phr and flame retardant variations of 30 and 35 phr. The results showed that the hihger of LDPE in nanocomposite increased the hardness and impact resistance, however, it decreased the tensile strength, elongation at break, and density. Addition of flame retardant to the nanocomposites showed good resistance to fire and burning, and optimum mechanical properties were found in using of 35 phr flame retardant.The morphology of the nanocomposite, were observed by Scanning Electron Microscope (SEM confirmed that homogeneous mixture of LDPE dispersed in the PVC matrix.

Dosimetry of the JS-6500 industrial irradiator for the irradiation of the PVC graduated flasks

International Nuclear Information System (INIS)

Castaneda F, A.; Carrasco A, H.; Martinez P, M.E.

2002-01-01

The dosimetry of the JS-6500 AECL irradiator was realized, outside of the industrial transportation rails to know the dose distribution, as well as its dose speed. This one with the intention of exposing to gamma radiation; plastified PVC graduated flasks and evaluating their interweavement or degradation or both. This study of dosimetry was carried out by means of a theoretical and experimental evaluation in air atmosphere. The results allow to know the irradiation conditions of the PVC graduated flasks as well as those results prove that has not a significant difference among the obtained result as theoretical as experimentally due to that the obtained result in the theoretical evaluation is 2.62 KGy/h and the result for the case of the experimental evaluation is 2.74 KGy/h. (Author)

A study on the improvement of radiation-induced oxidation resistance for polypropylene and PVC materials

International Nuclear Information System (INIS)

Park, K. Z.; Jeong, K. S.; Cho, S. H.; Cho, Y. H.; Seok, H. C.

2002-01-01

The object of this project is to improve the stability and the economics by reducing the radiation-induced oxidation as a factor of degradation of polymer materials used under the radiation environment. In order to attain the objective of this study and to check the effect of diamond-like carbon (DLC) coating on the anti-oxidation reaction, polymer specimens such as Polyproplyene, PVC coating DLC thin layer were exposed to high level gamma radiation, and their irradiation effects were investigated. A plasma-enhanced chemical vapor deposition method was adopted in fabricating a DLC thin film on the polymer specimens, which were irradiated with the non-DLC film deposited specimens under the gamma radiation emitted from Co-60 source from 1 x 10 5 to 1 x 10 8 rads exposure. According to the characterization of irradiated specimens from the elapsed time of minimum 4 hours to a maximum of 105 days after the irradiation, the DLC deposition on the polymer surface was revealed to contribute to the improvement on the resistance of the radiation-induced oxidation in this study

Analysis of Phthalate Ester Content in PVC Plastics by means of FT-Raman Spectroscopy

DEFF Research Database (Denmark)

Nørbygaard, Thomas; Berg, Rolf W.

2004-01-01

Polyvinyl chloride, PVC or [CH2-CHCl]n , is a common polymer used extensively for a wide range of industrial and household products. To achieve the proper material characteristics (e.g. softness, ductility), plasticizers such as phthalates are usually added to the otherwise hard and brittle PVC......, medical devices and toys may harm the e.g. reproductive organs of exposed infants. PVC is readily distinguished from other common polymers (e.g. polyethylene, polypropylene, polystyrene) by the use of Raman spectroscopy. By far the most commonly used phthalate plasticizer in PVC is di(2-ethylhexyl......-phenyl group, and as the relative intensities of the six bands vary only slightly from one phthalate ester to the next one we have obtained an identifiable, characteristic fingerprint of the phthalate ester group as a whole. By use of the set of six bands, which are common to all the measured Raman spectra, we...

Model fire tests on polyphosphazene rubber and polyvinyl chloride (PVC)/nitrile rubber foams

Science.gov (United States)

Widenor, W. M.

1978-01-01

A video tape record of model room fire tests was shown, comparing polyphosphazene (P-N) rubber and polyvinyl chloride (PVC)/nitrile rubber closed-cell foams as interior finish thermal insulation under conditions directly translatable to an actual fire situation. Flashover did not occur with the P-N foam and only moderate amounts of low density smoke were formed, whereas with the PVC/nitrile foam, flashover occurred quickly and large volumes of high density smoke were emitted. The P-N foam was produced in a pilot plant under carefully controlled conditions. The PVC/nitrile foam was a commercial product. A major phase of the overall program involved fire tests on P-N open-cell foam cushioning.

Forensic utility of the carbon isotope ratio of PVC tape backings

Science.gov (United States)

Stern, L. A.; Thompson, A. H.; Mehltretter, A. H.; McLaskey, V.; Parish, A.; Aranda, R.

2008-12-01

materials and recycling reactants during manufacture; as a result, tapes may be otherwise physically and chemical indistinguishable, but may have distinct carbon isotope ratios. We compared the carbon isotope ratios of 6 pairs of pre- and post-blast samples of PVC tapes adhered to explosive charges. The carbon isotope ratios of the post-blast samples were 0 to 0.5 ‰ higher than the corresponding pre-blast samples. Possible causes of this carbon isotope increase may be the reaction of the plasticizer and/or adhesive with the PVC backing during the explosion or the addition of debris to the tape backing during the explosion. Even with these minor explosive-induced carbon isotope alterations, the δ13C values of post-blast PVC tape backings were similar enough to the starting material to make carbon isotope ratios of post-blast tape a useful forensic tool. The range of carbon isotope ratios that would be used to exclude potential matches would have to be larger for post-blast samples, but with a 17 ‰ range in the population, this approach may still be useful for post-blast tape samples.

Mechanisms of charge transport and resistive switching in composite films of semiconducting polymers with nanoparticles of graphene and graphene oxide

Science.gov (United States)

Berestennikov, A. S.; Aleshin, A. N.

2017-11-01

We have investigated the effect of the resistive switching in the composite films based on polyfunctional polymers - PVK, PFD and PVC mixed with particles of Gr and GO with the concentration of ˜ 1 - 3 wt.%. We have developed the solution processed hybrid memory structures based on PVK and GO particles composite films. The effect of the resistive switching in Al/PVK(PFD; PVC):Gr(GO)/ITO/PET structures manifests itself as a sharp change of the electrical resistance from a low-conducting state to a relatively high-conducting state when applying a bias to Al-ITO electrodes of ˜ 0.2-0.4 V. It has been established that a sharp conductivity jump characterized by S-shaped current-voltage curves and the presence of their hysteresis occurs upon applying a voltage pulse to the Au/PVK(PFD; PVC):Gr(GO)/ITO/PET structures, with the switching time in the range from 1 to 30 μs. The mechanism of resistive switching associated with the processes of capture and accumulation of charge carriers by Gr(GO) particles introduced into the matrixes of the PVK polymer due to the reduction/oxidation processes. The possible mechanisms of energy transfer between organic and inorganic components in PVK(PFD; PVC):GO(Gr) films causes increase mobility are discussed. Incorporating of Gr (GO) particles into the polymer matrix is a promising route to enhance the performance of hybrid memory structures, as well as it is an effective medium for memory cells.

Improving the Healthiness of Sustainable Construction: Example of Polyvinyl Chloride (PVC

Directory of Open Access Journals (Sweden)

Emina Kristina Petrović

2018-02-01

Full Text Available With the increasing emphasis on sustainable construction, it has become important to better understand the impacts of common materials. This is especially paramount with the introduction of the United Nations (UN Sustainable Development Goals (SDGs which call for more comprehensive evaluations, adding many aspects of social consideration to the issues of environmental sustainability, including human health. Polyvinyl chloride (PVC/vinyl can be seen as a material with potential for significant adverse effects on a multiplicity of levels, and the construction industry is its single most significant consumer. This article presents a transdisciplinary review of adverse health impacts associated with PVC showing a number of issues: some that could be eliminated through design, but also some which appear inherent to the material itself and therefore unavoidable. The totality of issues revealed in relation to PVC presents a compelling case for a call for complete elimination of use of this material in sustainable construction.

Producción y modelamiento de gliceril-ésteres como plastificantes para PVC / Production et modelisation de glycerol-esters comme plastifiants pour le PVC

OpenAIRE

Suárez Palacios, Oscar Yesid

2011-01-01

El aumento en la producción mundial de glicerina, debido al crecimiento en el uso de biodiesel, y la tendencia a reemplazar los plastificantes derivados del anhídrido ftálico en la industria del PVC, por la toxicidad de dichas sustancias, motivaron la investigación de la plastificación del PVC con gliceril-ésteres derivados de ácidos carboxílicos de cadena corta (C3 - C8) y aromáticos. En este estudio se aplicó una metodología de diseño de producto para abordar la solución a las problemáticas...

Blendas PVC/NBR por processamento reativo I: desenvolvimento do processo de vulcanização Dinâmica in situ PVC/NBR blends by reactive processing I: in situ dynamic vulcanization process

Directory of Open Access Journals (Sweden)

Fábio R. Passador

2007-06-01

Full Text Available Vulcanização dinâmica é o processo de vulcanização de um elastômero durante a mistura no estado fundido com um termoplástico, que resulta em uma classe de materiais denominada termoplásticos vulcanizados. Neste trabalho, um novo tipo de termoplástico vulcanizado foi obtido por vulcanização dinâmica in situ da blenda PVC/NBR, utilizando-se um sistema de cura a base de enxofre (S e combinação dos aceleradores 2,2-ditiomercaptobenzotiazol (MBTS e dissulfeto de tetrametiltiuram (TMTD. As blendas PVC/NBR (90/10, 80/20 e 70/30% em massa foram processadas em um reômetro de torque Haake (Rheomix 600 a 160 °C com rotação de 60 rpm. As blendas obtidas por processamento reativo foram caracterizadas por calorimetria diferencial de varredura (DSC para determinação do grau de cura. Observou-se aumento no grau de cura das blendas com o tempo de mistura sendo o sistema de cura considerado eficiente.Dynamic vulcanization is a process of vulcanization of an elastomer during melt mixing with a thermoplastic wich results in material called thermoplastic vulcanizates or TPVs. In this study, a new kind of TPV was obtained by in situ dynamic curing of poly(vinyl chloride (PVC/nitrile rubber (NBR blends. The crosslinking of PVC/NBR blends was accomplished using sulphur (S/tetramethylthiuram disulphide (TMTD and mercaptobenzthiazyl disulphide (MBTS curative system during the reactive processing. The blends of PVC/NBR at the ratio of 90/10; 80/20 and 70/30 wt. (% were melt mixed using a Haake Rheomix 600 at 160 °C and rotor speed of 60 rpm. The curing behavior of NBR was investigated by a Monsanto Rheometer and the degree of cure was calculated using differential scanning calorimetry (DSC for different mixing times. It was observed that the degree of cure increases with the mixing time and the crosslinking system used in this work was considered efficient.

Investigation of PVC physical ageing in field test specimens using ultrasonic and dielectric measurements

NARCIS (Netherlands)

Demcenko, A.; Ravanan, M.; Visser, Roy; Loendersloot, Richard; Akkerman, Remko

2013-01-01

Physical ageing in PVC is studied using two techniques: a) non-linear ultrasonic measurements based on the non-collinear wave interaction theory and b) dielectric measurements. The ultrasonic measurement results are compared with dielectric measurement results. The comparison shows that the used

Effect of Different Packaging Films on Storability of Mushroom (Agaricus bisporus

Directory of Open Access Journals (Sweden)

R. Aminzadeh

2014-02-01

Full Text Available The button mushroom is rich food full of nutrient but compared with other fruits and vegetables, mushroom has a higher respiration rate and due to the lack of protective layer to prevent water loss, decay occurs quickly. It seems that suitable coating film is the one way for increase the storage life of mushroom. Therefore present research was carried out as split plot design in farme of CRD to find the best coating film in order to increase the storage life. In this research, the treatments were: control (package with Selefon, Poly Ethylene (PE with 40 and 65 micron thickness, Biaxially Oriented Polypropylene (BOPP with 25, 35 and 40 micron thickness, Cast PolyPropylen (CPP with 25 and 40 micron thickness, Poly Ester (PET with 12 and 24 micron thickness and Poly Vinyl Chloride (PVC with 30 micron thickness. The samples were estimated after 0, 10, 15, 20 and 25 days storage at 1°C and 90 % RH in 3 replications. The results showed that the types of plastic coating had significant effects on all measured characteristics as campared to that of control. Highest firmness value, Soluble Solid Content (SSC, titratable acidity, acidity (pH, and lowest weight less and decay were observed in packet mushroom with the coating film: BOPP and CPP and the lowest amounts were observed in the mushroom packed with control, PVC, PET and PE films. The effects of time on all of the measured during the storage period, were significant too.

SYNTHESIS OF ACETIC ACID FROM ETHANOL BY ELECTROOXIDATION TECHNIQUE USING Ni-Cu-PVC ELECTRODE

Directory of Open Access Journals (Sweden)

Riyanto Riyanto

2017-11-01

Full Text Available A usage of Ni-Cu-PVC electrode for the oxidation of ethanol by electrochemical technique will be reported in this paper. In this work, the effect of electrodes on the yields of acetic acid was determined. Electrode used was made of the mixtures of Ni powder, Cu powder and of polyvinyl chloride (PVC with various percentages. Electrooxidation of 0.20 M ethanol in 0.16 M KOH  (24 mL were carried out using chrono coulometry (CC at a potential of 1050 mV for 6 hours with continious stirring. Electrooxdation result obtained was analyzed using High Performance Liquid Chromatography (HPLC. The test result shows that the composition of  Ni:Cu:PVC  at 75:20:5 have higher efficiency in the electrooxidation of ethanol to acetic acid.

PVC--as flooring material--and its association with incident asthma in a Swedish child cohort study.

Science.gov (United States)

Larsson, M; Hägerhed-Engman, L; Kolarik, B; James, P; Lundin, F; Janson, S; Sundell, J; Bornehag, C G

2010-12-01

The Dampness in Buildings and Health study (DBH) started in the year 2000 in Värmland, Sweden, with a baseline questionnaire sent to all children (n = 14,077) aged 1-6. Five years later, a follow-up questionnaire was sent to the children who were 1-3 years at baseline. A total of 4779 children participated in both the baseline and the follow-up studies and constitute the study population in this cohort study. The aim of this study was to examine the association between exposure to PVC-flooring in the child's and parent's bedroom in homes of children aged 1-3 and the incidence of asthma, rhinitis, and eczema during the following 5-year period. Adjusted analyses showed that the incidence of asthma among children was associated with PVC-flooring in the child's bedroom (AOR 1.52; 95% CI 0.99-2.35) and in the parent's bedroom (1.46; 0.96-2.23). The found risks were on borderline of significance and should therefore be interpreted with caution. There was further a positive relationship between the number of rooms with PVC-flooring and the cumulative incidence of asthma. PVC-flooring was found to be a stronger risk factor for incident asthma in multifamily homes when compared with single-family houses and in smoking families compared with non-smoking families and in women. These longitudinal data from the DBH study found an association between the presence of PVC-flooring in the home and incident asthma in children. However, earlier results from the DBH study have shown that PVC-flooring is one important source for phthalates in indoor dust, and exposure to such phthalates was found to be associated with asthma and allergy among children. This emphasizes the need for prospective studies that focus on the importance of prenatal and neonatal exposure to phthalates in the development of asthma and allergy in children. © 2010 John Wiley & Sons A/S.

Mechanical properties of oil palm empty fruit bunch (OPEFB) fiber reinforced PVC/ENR blend

International Nuclear Information System (INIS)

Gunasunderi Raju Nor Azowa Ibrahim; Mohammad Zaki Abd Rahman; Wan Md Zin Wan Yunus; Chantara Thevy Ratnam

2004-01-01

The effect of OPEFB fiber on the mechanical properties of the 50/50 PVC/ENR was investigated over a range of fiber loadings (0 to 30%). The OPEFB fiber reinforced PVC/ENR blend was prepared by using Haake Rheomixer at 150 degree C mixing temperature, 20 minutes total mixing time and 50 rpm rotor speed. The changes in tensile strength (Ts), Young's modulus, elongation break (Eb), flexural modulus, hardness and impact strength with the OPEFB fiber loadings were investigated. The results revealed that the flexural modulus, Young's modulus and hardness increased with the fiber loading. However, the impact strength, Ts and Eb found to decrease with the increase in fiber loading. (Author)

Antibacterial performance of ZnO-based fillers with mesoscale structured morphology in model medical PVC composites

Energy Technology Data Exchange (ETDEWEB)

Machovsky, Michal; Kuritka, Ivo, E-mail: ivo@kuritka.net; Bazant, Pavel; Vesela, Daniela; Saha, Petr

2014-08-01

Three different ZnO-based antibacterial fillers having different morphologies in microscale region were prepared by the use of the microwave assisted synthesis protocol created in our laboratory with additional annealing in one case. Further, PVC composites containing 0.5–5 wt.% of ZnO based antibacterial fillers were prepared by melt mixing and characterized by scanning electron microscopy (SEM) and X-ray diffractometry (XRD). Mechanical testing showed no adverse effect on the working of polymer composites due to either of the fillers used or the applied processing conditions in comparison with the neat medical grade PVC. The surface antibacterial activity of the compounded PVC composites was assessed against Escherichia coli ATCC 8739 and Staphylococcus aureus ATCC 6538P according to ISO 22196: 2007 (E). All materials at almost all filler loading levels were efficient against both species of bacteria. The material with the most expanding morphology assuring the largest contact between filler and matrix achieved an excellent level of more than 99.9999% reduction of viable cells of E. coli in comparison to untreated PVC and performed very well against S. aureus, too. A correlation between the morphology and efficacy of the filler was observed and, as a result, a general rule was formulated which links the proneness of the microparticles to perform well against bacteria to their shape and morphology. - Highlights: • ZnO-based nanostructured microparticles were prepared by microwave synthesis. • Prepared ZnO imparts excellent antibacterial activity to PVC composites. • The microparticulate character of filler makes it processable as common powders. • The inevitable disadvantages of nanoparticles are circumvented. • General rule of proneness of microparticles for antibacterial composites.

Antibacterial performance of ZnO-based fillers with mesoscale structured morphology in model medical PVC composites

International Nuclear Information System (INIS)

Machovsky, Michal; Kuritka, Ivo; Bazant, Pavel; Vesela, Daniela; Saha, Petr

2014-01-01

Three different ZnO-based antibacterial fillers having different morphologies in microscale region were prepared by the use of the microwave assisted synthesis protocol created in our laboratory with additional annealing in one case. Further, PVC composites containing 0.5–5 wt.% of ZnO based antibacterial fillers were prepared by melt mixing and characterized by scanning electron microscopy (SEM) and X-ray diffractometry (XRD). Mechanical testing showed no adverse effect on the working of polymer composites due to either of the fillers used or the applied processing conditions in comparison with the neat medical grade PVC. The surface antibacterial activity of the compounded PVC composites was assessed against Escherichia coli ATCC 8739 and Staphylococcus aureus ATCC 6538P according to ISO 22196: 2007 (E). All materials at almost all filler loading levels were efficient against both species of bacteria. The material with the most expanding morphology assuring the largest contact between filler and matrix achieved an excellent level of more than 99.9999% reduction of viable cells of E. coli in comparison to untreated PVC and performed very well against S. aureus, too. A correlation between the morphology and efficacy of the filler was observed and, as a result, a general rule was formulated which links the proneness of the microparticles to perform well against bacteria to their shape and morphology. - Highlights: • ZnO-based nanostructured microparticles were prepared by microwave synthesis. • Prepared ZnO imparts excellent antibacterial activity to PVC composites. • The microparticulate character of filler makes it processable as common powders. • The inevitable disadvantages of nanoparticles are circumvented. • General rule of proneness of microparticles for antibacterial composites

PVC gel soft actuator-based wearable assist wear for hip joint support during walking

Science.gov (United States)

Li, Yi; Hashimoto, Minoru

2017-12-01

Plasticized polyvinyl chloride (PVC) gel and mesh electrode-based soft actuators have considerable potential to provide new types of artificial muscle, exhibiting similar responsiveness to biological muscle in air, >10% deformation, >90 kPa output stress, variable stiffness, long cycle life (>5 million cycles), and low power consumption. We have designed and fabricated a prototype of walking assist wear using the PVC gel actuator in previous study. The system has several advantages compared with traditional motor-based exoskeletons, including lower weight and power consumption, and no requirement for rigid external structures that constrain the wearer’s joints. In this study, we designed and established a control and power system to making the whole system portable and wearable outdoors. And we designed two control strategies based on the characteristics of the assist wear and the biological kinematics. In a preliminary experimental evaluation, a hemiparetic stroke patient performed a 10 m to-and-fro straight line walking task with and without assist wear on the affected side. We found that the assist wear enabled natural movement, increasing step length and decreasing muscular activity during straight line walking. We demonstrated that the assistance effect could be adjusted by controlling the on-off time of the PVC gel soft actuators. The results show the effectiveness of the proposed system and suggest the feasibility of PVC gel soft actuators for developing practical soft wearable assistive devices, informing the development of future wearable robots and the other soft actuator technologies for human movement assistance and rehabilitation.

Development of peelable films for decontamination and their performances

International Nuclear Information System (INIS)

Yang Enbo; Xu Baolan; Zhao Xiuyan

1990-01-01

Two kinds of peelable films have been developed which can be coated on surface contaminated by radioactivity for decontamination purposes. Very high levels of radioactive decontamination, especially on smooth surface, are obtained after one application. 90-99% decontamination based on initial activity can be obtained for stainless steel, PVC floor and glass

Comparative study of three different kinds of geo membranes (PVC-P, HDPE, EPDM) used in the waterproofing of reservoirs; Estudio comparativo de tres geomembranas de distinta naturaleza (PVC-P, PEAD, EPDM) empleadas en la impermeabilizacion de balsas

Energy Technology Data Exchange (ETDEWEB)

Blanco Fernandez, M.; Castillo Rubi, F.; Soriano Carrillo, J.; Noval Arango, A. M.; Touze-Foltz, N.; Pargada Iglesias, L.; Rico Arnaiz, G.; Aguilar gonzalez, E.

2014-02-01

This work describes the long-term behaviour of three kinds of geo membranes which are constituted by plasticised poly vinyl chloride (PVC-P), high density polyethylene (HDPE) and terpolymer rubber of ethylene-propylene-dienic monomer (EPDM) used as the waterproofing system of the reservoirs Los Llanos de Mesa, San Isidro and El Golfo, respectively. Characteristics of the three original geo membranes and their behaviour along time are presented. Thicknesses, content and nature of the plasticizers ( in PVC-P), tensile properties dynamic and static puncture, fold ability at low temperature, shore hardness, tear resistance and carbon black ( in HDPE), joint strength (shear and peeling test) and microscopy, both optical and electronic scanning tests were carried out. Results obtained conclude with a long-term durability of geo membranes, independently of their macromolecular nature. These characteristics were determined by advanced analytical techniques in PVC-P samples, such as fourier Transform Infrared Spectroscopy (FTIR), Gas Chromatography (GC) and Mass Spectrometry (MS). Spectrometry (MS). (Author)

Desenvolvimento de PVC reforçado com resíduos de Pinus para substituir madeira convencional em diversas aplicações Development of PVC/wood composites for the replacement of conventional wood products

Directory of Open Access Journals (Sweden)

Antonio Rodolfo Jr.

2006-03-01

Full Text Available Este trabalho avalia a viabilidade técnica da obtenção de compósitos lignocelulósicos de PVC, utilizando-se resíduo de Pinus elliottii e Pinus taeda como carga reforçativa. Foi desenvolvido um processo simples e economicamente viável de tratamento de resíduos industriais desta madeira, processo este baseado na secagem e revestimento das partículas com lubrificantes funcionais e agentes de acoplamento utilizados como aditivos na indústria do PVC, bem como no uso de equipamentos tradicionais da indústria de processamento deste termoplástico. Foram avaliados os efeitos da incorporação da farinha de madeira em concentrações variáveis e do tipo de agente de tratamento superficial utilizado na processabilidade do composto de PVC, bem como em propriedades finais do compósito. Os resultados mostram que o desenvolvimento deste tipo de material compósito é uma alternativa viável para a substituição da madeira convencional em diversas aplicações.This work evaluates the technical viability of lignocellulosic vinyl composites, using residues of Pinus elliottii and Pinus taeda as the reinforcement fiber. A simple and economically viable process for the treatment of these industrial residues was developed. The process includes sieving, drying and treating the wood particles. Treatment is made with functional lubricants and coupling agents used as additives in the PVC industry. Extrusion was performed using traditional equipment available in the Brazilian PVC processing industry. The effect on the processability of the variable concentrations of the residues incorporated and the type of agent used for the treatment had been evaluated, as well as in the final properties of the composite. The results show that the development of this kind of composite material is a viable alternative for the substitution of conventional wood in diverse applications.

Effects of low dose gamma irradiation on PVC blood bags containing anticoagulant CPDA solution

International Nuclear Information System (INIS)

Mitra, D.; Varshney, Lalit; Arjun, Chanda

2006-01-01

PVC blood bags were exposed to 20Gy and 60Gy low gamma radiation dose to investigate possibility of change in leaching behavior of the plasticizer into CPDA solution and the blood. Reversed phase HPLC was used for the investigations on anti coagulant solution CPDA(citrate, phosphate, dextrose and adenine) contained in PVC bag before and after gamma irradiation. The studies were repeated using methanol as an extractant instead of CPDA solution, considering higher extractability of plasticizer by blood. Irradiation of PVC bags by gamma radiation for a dose up to 60Gy does not lead to change in leaching behavior of the plasticizer in CPDA solution and methanol indicating similar expected behavior in blood. (author)

CONTECH(R) A-2000 polyvinyl chloride (PVC) plastic pipe.

Science.gov (United States)

2015-03-01

Determine the effectiveness and long-term durability of the Contech A-2000 PVC pipe : in an irrigation application. This type of pipe may prove to be a viable alternative to : reinforced concrete pipe (RCP).

Mechanical, Spectroscopic and Micro-structural Characterization of Banana Particulate Reinforced PVC Composite as Piping Material

Directory of Open Access Journals (Sweden)

B. Dan-asabe

2016-06-01

Full Text Available A banana particulate reinforced polyvinyl chloride (PVC composite was developed with considerabley low cost materials having an overall light-weight and good mechanical properties for potential application as piping material. The specimen composite material was produced with the banana (stem particulate as reinforcement using compression molding. Results showed that density and elastic Modulus of the composite decreases and increases respectively with increasing weight fraction of the particulate reinforcement. The tensile strength increased to a maximum of 42 MPa and then decreased steadily. The composition with optimum mechanical property (42 MPa was determined at 8, 62 and 30 % formulation of banana stem particulates (reinforcement, PVC (matrix and Kankara clay (filler respectively with corresponding percentage water absorption of 0.79 %, Young’s Modulus of 1.3 GPa, flexural strength of 92 MPa and density of 1.24 g/cm3. Fourier Transform Infrared (FTIR analysis of the constituents showed identical bands within the range 4000–1000 cm-1 with renown research work. Scanning Electron Microscopy (SEM result showed fairly uniform distribution of constituents’ phases. X-Ray Fluorescence (XRF confirms the X-ray diffraction (XRD result of the presence of minerals of kaolinite, quartz, rutile and illite in the kaolin clay. Comparison with conventional piping materials showed the composite offered a price savings per meter length of 84 % and 25 % when compared with carbon steel and PVC material.

Development and characterization of a synthetic PVC/DEHP myocardial tissue analogue material for CT imaging applications.

Science.gov (United States)

Ramadan, Sherif; Paul, Narinder; Naguib, Hani E

2018-04-01

A simple myocardial analogue material has great potential to help researchers in the creation of medical CT Imaging phantoms. This work aims to outline a Bis(2-ethylhexyl) phthalate (DEHP) plasticizer/PVC material to achieve this. DEHP-PVC was manufactured in three ratios, 75, 80, and 85% DEHP by heating at 110 °C for 10 min to promote DEHP-PVC binding followed by heating at 150 °C to melt the blend. The material was then tested utilizing FTIR, tensile testing, dynamic mechanical analysis and imaged with computed tomography. The FTIR testing finds the presence of C-CL and carbonyl bonds that demonstrate the binding required in this plasticized material. The tensile testing finds a modulus of 180-20 kPa that increases with the proportion of plasticizer. The dynamic mechanical analysis finds a linear increase in viscoelastic properties with a storage/loss modulus of 6/.5-120/18 kPa. Finally, the CT number of the material increases with higher PVC content from 55 to 144HU. The 80% DEHP-PVC ratio meets the mechanical and CT properties necessary to function as a myocardial tissue analogue.

Preparation of Drug-loaded Chitosan Microspheres and Its Application in Paper-based PVC Wallpaper

Science.gov (United States)

Lin, Hui; Chen, Lihui; Yan, Guiyang; Chen, Feng; Huang, Liulian

2018-03-01

By screening through test, it was found that the drug-loaded chitosan microspheres with the average particle size of 615 nm may be prepared with NaF as the mold-proof drug, chitosan as the drug carrier and sodium tripolyphosphate as the cross-linking agent; and they can improve the aspergillus niger-proof effect if loaded onto the base paper surface of the paper-based PVC wallpaper. The results show that NaF and chitosan have mold-proof synergistic effects; the mold-proof effect of the wallpaper may be improved by increasing the dose of chitosan; when the mass ratio of NaF, sodium tripolyphosphate and chitosan was 2:7:28, the paper-based PVC wallpaper with good mold-proof property can be prepared.

The Effect of Pigment Volume Concentration on Film Formation and the Mechanical Properties of Coatings Based on Water-Dispersion Paint and Varnish Materials

Science.gov (United States)

Kasyanenko, I. M.; Kramarenko, V. Yu.

2018-01-01

The effect of pigment volume concentration (PVC) on the film formation process and properties of coatings based on the water dispersion of an Acronal 290D styrene-acrylate copolymer and a pigment/filler system used for paint materials in construction was investigated. An analysis of the results obtained is performed within the framework of the concept of the critical PVC. It is shown that the initiation and development of internal stresses occurs the faster, the higher the PVC, but the position of the maximum or the inflection point of the internal stress-drying time curve complies with a universal value of the solid volume content in the compositions. It is found that the internal stresses and Young's modulus of coatings are characterized by an extreme concentration relation that, for the reduced elastic modulus, can be described by a system of equations based on the Halpin-Tsai equation.

supplementary2.docx

Indian Academy of Sciences (India)

aaa

Figure S1. SEM micrographs of(a) PVC and (b) TiO2@PVC-5%nanocomposite film. Table S3. Tensile strength and Young's modulusof PVC and TiO2@PVC nanocomposite film. Sample, Tensile Strength (MPa), Young's modulus (MPa). PVC, 20.26, 580.27. TiO2@PVC-5%, 29.56, 601.93. TiO2@PVC-10%, 40.52, 841.77 ...

Site-selective photofragmentation of chlorinated polymeric films observed around the chlorine K-edge

Energy Technology Data Exchange (ETDEWEB)

Arantes, C., E-mail: csilva@inmetro.gov.br [Divisão de Metrologia de Materiais, Instituto Nacional de Metrologia, Qualidade e Tecnologia, Xerém 25250-020, Duque de Caxias, RJ (Brazil); Mendes, L.A.V. [Instituto de Física, Universidade Federal da Bahia, Ondina, 40210-340 Salvador, BA (Brazil); Pinho, R.R. [Departamento de Física-ICE, Universidade Federal de Juiz de Fora, Campus Universitário, 36036-330 Juiz de Fora, MG (Brazil); Ferreira, M. [PEMM/COPPE, Universidade Federal do Rio de Janeiro, Cidade Universitária, Ilha do Fundão, 21941-972 Rio de Janeiro, RJ (Brazil); Souza, G.G.B. de; Rocha, A.B.; Rocco, M.L.M. [Instituto de Química, Universidade Federal do Rio de Janeiro, Cidade Universitária, Ilha do Fundão, 21941-909 Rio de Janeiro, RJ (Brazil)

2013-03-29

Highlights: ► PVC and PVDC were studied by PSID and NEXAFS techniques at the Chlorine 1s-edge. ► PVC film presented isotope ratio of 3:1 in the PSID spectrum. ► Cl{sup +} ion yield curves reproduce the photoabsorption spectrum for both polymers. ► Site-selectivity of C–Cl bond breaking due to an efficient spectator Auger decay. - Abstract: Photon stimulated ion desorption (PSID) and Near-edge X-ray absorption fine structure (NEXAFS) studies have been performed on poly(vinyl chloride) (PVC) and poly(vinyl dichloride) (PVDC) around the chlorine 1s-edge. Experiments were performed using a synchrotron source operating in the single-bunch mode and a time-of-flight mass spectrometry for ion analysis. Cl{sup +} ion yields, as a function of the photon energy, reproduce the photoabsorption spectrum, showing significant increase at the 1s-resonance. Edge-jump ratios, defined as the ratio between edge-jumps (intensity ratio of the yields between above and below the absorption edge) of two different transitions, for Cl{sup +} ion yields were much higher than the equivalent electron yields, indicating site-selectivity in C–Cl bond breaking for both polymers, as a result of efficient spectator Auger decay. The expected isotope ratio of 3:1 for chlorine was measured for PVC. The interpretation of the NEXAFS spectrum was assisted by quantum mechanical calculations at a multireference perturbation theory level.

Conservação pós-colheita de Sorvetão (Zingiber spectabile Griff. utilizando filme plástico em diferentes pontos de colheitas.

Directory of Open Access Journals (Sweden)

Robson Assunção Cavalcante

2006-06-01

Full Text Available Hastes florais de sorvetão (Zingiber spectabile Griff. colhidas no Câmpus Experimental da Embrapa Agroindústria Tropical, situada em Fortaleza (CE,; em dois estádios de colheita: inflorescências com abertura completa e abertura incompleta na região apical, foram submetidas ao processo de limpeza e imersas em solução fúngica. Em seguida, procedeu-se ao corte basal das hastes (mantendo comprimento padrão de 40 cm e hidratação, realizada por um período de uma hora em recipientes contendo água. As hastes foram colhidas no estádio 1 (inflorescências com abertura completa na região apical e no estádio 2 (inflorescências que apresentavam abertura incompleta na região apical, embaladas ou não em filme de PVC de 15 ?m de espessura. Em seguida, colocadas em caixas de papelão, tipo telescópio, usadas comercialmente (dimensões de 1,0 m de comprimento; 0,32 m de largura e 0,2 m de altura e armazenadas em câmaras frias em temperatura de 15 ºC e 85% de UR. Diariamente foram avaliadas perda de massa, aparência visual, além da longevidade floral. O experimento foi conduzido em delineamento inteiramente casualizado em esquema fatorial 2x2, e o primeiro fator referiu-se aos dois pontos de colheita e o segundo,ao uso ou não do filme de PVC; com três repetições e cinco hastes por repetição. Não houve interação significativa entre os fatores pontos de colheita e uso ou não de filme de PVC para as variáveis estudadas. O revestimento das hastes florais com filme de PVC foi eficiente na redução da perda de massa para ambos os pontos de colheita. As maiores notas para aparência visual e maior longevidade floral foram atingidas em hastes florais colhidas no estádio 1 revestidas com filme de PVC. Não houve diferenças significativas entre os pontos de colheita para perda de massa e longevidade floral.

The Effect of Zn-Al-Hydrotalcites Composited with Calcium Stearate and β-Diketone on the Thermal Stability of PVC

Directory of Open Access Journals (Sweden)

Runjuan Wen

2011-03-01

Full Text Available A clean-route synthesis of Zn-Al-hydrotalcites (Zn-Al-LDHs using zinc oxide and sodium aluminate solution has been developed. The as-obtained materials were characterized by X-ray diffraction (XRD, Fourier transform infrared spectroscopy (FT-IR, and scanning electron microscopy (SEM. The effects of metal ions at different molar ratios on the performance of hydrotalcites were discussed. The results showed that the Zn-Al-hydrotalcites can be successfully synthesized at three different Zn/Al ratios of 3:1, 2:1 and 1:1. Thermal aging tests of polyvinyl chloride (PVC mixed with Zn-Al-LDHs, calcium stearate (CaSt2 and β-diketone were carried out in a thermal aging test box by observing the color change. The results showed that Zn-Al-LDHs can not only enhance the stability of PVC significantly due to the improved capacity of HCl-adsorption but also increase the initial stability and ensure good-initial coloring due to the presence of the Zn element. The effects of various amounts of Zn-Al-LDHs, CaSt2 and β-diketone on the thermal stability of PVC were discussed. The optimum composition was determined to be 0.1 g Zn-Al-LDHs, 0.15 g CaSt2 and 0.25 g β-diketone in 5 g PVC.

Impact of Electrostatic Assist on Halftone Mottle in Shrink Films

Directory of Open Access Journals (Sweden)

Akshay V. Joshi

2015-09-01

Full Text Available Gravure printing delivers intricate print quality and exhibit better feasibility for printing long run packaging jobs. PVC and PETG are widely used shrink films printed by gravure process. The variation in ink transfer from gravure cells on to the substrate results in print mottle. The variation is inevitable and requires close monitoring with tight control on process parameters to deliver good dot fidelity. The electrostatic assist in gravure improves the ink transfer efficiency but is greatly influenced by ESA parameters such as air gap (distance between charge bar and impression roller and voltage. Moreover, it is imperative to study the combined effect of ESA and gravure process parameters such as line screen, viscosity and speed for the minimization of half-tone mottle in shrink films. A general full factorial design was performed for the above mentioned parameters to evaluate half-tone mottle. The significant levels of both the main and interactions were studied by ANOVA approach. The statistical analysis revealed the significance of all the process parameters with viscosity, line screen and voltage being the major contributors in minimization of half-tone mottle. The optimized setting showed reduction in halftone mottle by 33% and 32% for PVC and PET-G respectively. The developed regression model was tested that showed more than 95% predictability. Furthermore, the uniformity of dot was measured by image to non-image area (ratio distribution. The result showed reduction in halftone mottle with uniform dot distribution.

Platelet storage in Fresenius/NPBI polyolefin and BTHC-PVC bags: a direct comparison.

Science.gov (United States)

Hornsey, V S; McColl, K; Drummond, O; Macgregor, I R; Prowse, C V

2008-08-01

New platelet storage systems, such as changes in the plastic of the storage bags, require validation. In this study, pooled buffy coat platelets stored in Fresenius/NPBI polyolefin bags were compared with those stored in Fresenius/NPBI butyryl-trihexyl citrate (BTHC) plasticized polyvinyl chloride (PVC). The CompoSelect thrombocyte polishing filter system (1000 mL polyolefin bag) and the CompoStop F730 system (1300 mL BTHC-PVC bag) were used to prepare paired, plasma-suspended, buffy coat platelet concentrates. Samples were taken up to day 7 for in vitro analysis. In a separate experiment, 12 units were prepared using the CompoStop F730 system and samples taken after leucofiltration for FXIIa assay. By day 7, platelet concentrates stored in BTHC-PVC demonstrated significantly higher pH levels (7.32 +/- 0.05 vs. 7.26 +/- 0.05) and a greater degree of cell lysis as shown by increased lactate dehydrogenase levels (497 +/- 107 vs. 392 +/- 81 U L(-1)). The supernatants contained higher concentrations of soluble P-selectin and the chemokine 'regulated on activation, normal T-cell expressed and presumably secreted', which are released from the alpha-granules during activation. The ATP concentrations were significantly lower in BTHC-PVC. Platelet counts, mean platelet volume and hypotonic shock response were similar for both bags. FXIIa antigen concentrations were 0.6 +/- 0.2 ng mL(-1) indicating that activation of the contact factor pathway had not occurred. Although the CompoStop F730 leucoreduction filter did not activate the contact system, platelets stored in 100% plasma in BTHC-PVC bags demonstrated different in vitro characteristics from those stored in polyolefin. Further work is required to demonstrate whether these differences will affect in vivo recovery and survival.

Residual lifetime assessment of uPVC gas pipes

NARCIS (Netherlands)

Visser, H.A.

2010-01-01

The Dutch gas distribution network consists of about 20% (22,500 km) of unplasticised poly(vinyl chloride) (uPVC) pipes, most of which have been installed from the mid-sixties up to the mid-seventies of the previous century and have been in service ever since. In the next decade the specified

Aging and characterization of PVC compound used as flat-panel of a low cost solar collector; Envelhecimento e caracterizacao de compostos de PVC usado em placas de coletores solares de baixo custo

Energy Technology Data Exchange (ETDEWEB)

Prado, Bruna R.; Pinto, Tatiana T.; Bartoli, Julio R. [Depto. de Tecnologia de Polimeros, Faculdade de Engenharia Quimica/Universidade Estadual de Campinas. FEQ/UNICAMP, SP (Brazil)], e-mail: bartoli@feq.unicamp.br; Fernandes, Elizabeth G. [Tezca P and D Celulas Solares (Brazil)

2011-07-01

Regardless the excellent amount of solar irradiation in Brazil, the development and production of solar water heating systems did not reach the low-income families yet. The relatively high cost of conventional solar water heaters is still the main reason to prevent it. The development of a low cost solar water heater (around US$ 200), easy technology, was the scope of previous work. All-plastic solar collector prototypes were developed using unplasticized Poly (vinyl chloride) ceiling panels and tubes, commodities from building engineering. Nevertheless, the main thermal and photo degradation mechanisms for PVC are well known; the unusual application of PVC as solar collector materials should need a specific investigation on environmental aging. This work presents a study on outdoor aging and characterization of PVC flat-plate absorber of solar collectors after 5 years on use. (author)

Spectroscopic analysis of PMMA/PVC blends containing CoCl2

Directory of Open Access Journals (Sweden)

N.S. Alghunaim

2015-01-01

Full Text Available Composites of polymethyl methacrylate (PMMA and polyvinyl chloride (PVC polymer blend containing different concentrations (⩽10 wt. of cobalt chloride (CoCl2 were prepared by casting techniques. The changes of the structural, spectroscopic, optical and thermal parameters of the samples are studied using different tools. FT-IR spectroscopy confirmed the complexation between the blends and Co+2-ions. The decrease or increase of IR band intensity with some shifts of other bands suggests an interaction and compatibility between PMMA/PVC blends with CoCl2 take place. The Ultra violet and visible (UV/Vis spectra indicated that the presence of band gap energy depends on increasing of CoCl2 contents. The absorption intensity of the samples doped with CoCl2 becomes faint lower than the pure blend. The values of energy gap for direct and indirect transition decreases with the increase of CoCl2 due to the presence of charge transfer between PMMA/PVC and CoCl2. The thermogravimetric analysis (TGA curves for all the samples have the same behavior and more steps of decomposition were observed. The reduction of mass loss for samples containing CoCl2 compared to the pure blend was observed and it was attributed to crosslink formation between the blend and CoCl2.

Evaluation of dosimetric characteristics of graphene oxide/PVC nanocomposite for gamma radiation applications

Energy Technology Data Exchange (ETDEWEB)

Feizi, Shahzad; Malekie, Shahryar; Ziaie, Farhood [Nuclear Science and Technology Research Institute (NSTRI), Karaj (Iran, Islamic Republic of). Radiation Application Research School; Rahighi, Reza; Tayyebi, Ahmad [Univ. of Technology, Tehran (Iran, Islamic Republic of). Dept. of Physics

2017-04-01

Graphene oxide-polyvinyl chloride composite was prepared using tetrahydrofuran solvent-assisted dispersion of characterized nano flakes of graphene oxide in polymer matrix. Electrical percolation threshold of GO/PVC nanocomposite was determined via a finite element simulation method with a 2D model and compared with experimental results. A conductive cell with two silver coated walls was designed and fabricated for exploring dosimetric properties of the composite. Some characteristics of the new nanocomposite such as linearity of dose response, repeatability, sensitivity and angular dependence are investigated. According to 2D proposed method, obtained data associated to electrical conductivity of the GO/polymer composite for PVC matrix plotted in different GO weight percentages and had good compatibility (validity) with experimental data. The dose response is linear in the 17-51 mGy dose range and it can be introduced for gamma radiation dosimetry in diagnostic activities.

Comparative study of three different kinds of geomembranes (PVC-P, HDPE, EPDM) used in the waterproofing of reservoirs

International Nuclear Information System (INIS)

Blanco Fernandez, M.; Castillo Rubi, F.; Soriano Carrillo, J.; Noval Arango, A. M.; Touze-Foltz, N.; Pargada Iglesias, L.; Rico Arnaiz, G.; Aguilar gonzalez, E.

2014-01-01

This work describes the long-term behaviour of three kinds of geomembranes which are constituted by plasticized poly vinyl chloride (PVC-P), high density polyethylene (HDPE) and terpolymer rubber of ethylene-propylene-dienic monomer (EPDM) used as the waterproofing system of the reservoirs Los Llanos de Mesa, San Isidro and El Golfo, respectively. Characteristics of the three original geomembranes and their behaviour along time are presented. Thicknesses, content and nature of the plasticizers ( in PVC-P), tensile properties dynamic and static puncture, foldability at low temperature, shore hardeness, tear resistance and carbon black ( in HDPE), joint strength (shear and peeling test) and microscopy, both optical and electronic scanning tests were carried out. Results obtained conclude with a long-term durability of geomembranes, independently of their macromolecular nature. These characteristics were determined by advanced analytical techniques in PVC-P samples, such as fourier Transform Infrared Spectroscopy (FTIR), Gas Chromatography (GC) and Mass Spectrometry (MS). Spectrometry (MS). (Author)

Effect of radiation on properties of ENR/PVC/SiO{sub 2} membrane

Energy Technology Data Exchange (ETDEWEB)

Ismail, Nur Farahein Hadina; Abdullah, Ibrahim; Daik, Rusli; Ahmad, Ishak; Jamil, Suzereen; Lazim, Mohammad Azwan Mat; Othaman, Rizafizah [School of Chemical Sciences and Food Technology, Universiti Kebangsaan Malaysia, 43600 UKM Bangi, Selangor Darul Ehsan. Malaysia (Malaysia)

2015-09-25

In this study epoxidised natural rubber (ENR)/polyvinyl chloride (PVC) matrix was prepared by melt blending. The matrix was swelled in THF and silica as a filler was introduced to the solution to generate pore formation. The ENR/PVC/10 % SiO{sub 2} membrane was prepared using a casting knife technique. The membrane was irradiated using 2 MeV electron beam accelerator at a dose range of 10-100 kGy. The effect of electron beam irradiation of the membrane was studied by undergo characterization of Scanning electron microscope (SEM) and Fourier transform infra red (FTIR). Morphological studies showed that pores generated in ENR/PVC/10 % SiO{sub 2} membrane increased with the dosage of radiation. While FTIR analysis showed the presence of peak of Si-O-Si asymmetric stretching at 834 cm{sup −1}. There are no significant changes in the functional group before and after radiation.

Influence of the use of acids and films in post-harvest lychee conservation

Directory of Open Access Journals (Sweden)

Danielle Fabíola Pereira da Silva

2012-12-01

Full Text Available Lychee (Litchi chinensis Sonn. has a high commercial value; however, it has a short shelf-life because of its rapid pericarp browning. The objective of this study was to evaluate the shelf-life of 'Bengal' lychee fruits stored after treatment with hydrochloric acid and citric acid, associated with cassava starch and plastic packaging. Uniformly red pericarp fruits were submitted to treatments: 1-(immersion in citric acid 100 mM for 5 minutes + cassava starch 30 g L-1 for 5 minutes, 2-(immersion in hydrochloric acid 1 M for 2 minutes + starch cassava 30 g L-1 for 5 minutes, 3-(immersion in citric acid 100 mM for 5 minutes + polyvinyl chloride film (PVC, 14 µm thick and 4-(immersion in hydrochloric acid 1 M for 2 minutes + PVC film. During 20 days, the fruits were evaluated for mass loss, pericarp color, pH, soluble solids and titratable acidity, vitamin C of the pulp and pericarp and activities of polyphenol oxidase and peroxidase of the pericarp. The treatment with hydrochloric acid associated with PVC was the most effective in maintaining the red color of the pericarp for a period of 20 days and best preservation of the fruit. The cassava starch associated with citric acid, and hydrochloric acid did not reduce the mass loss and did not prevent the browning of lychee fruit pericarp.

Study on application of molten salt oxidation technology (MSO) for PVC wastes treatment

International Nuclear Information System (INIS)

Tran Thu Ha; Nguyen Hong Quy; Pham Quoc Ky; Nguyen Quang Long; Vuong Thu Bac; Dang Duc Nhan

2007-01-01

The project 'Study on application of molten salt oxidation (MSO) for PVC plastic wastes treatment' aims at three followings: 1) Installation of lab-scale MSO unit with essential compositions builds up foundation for the 2) estimation of waste destruction efficiency of the technology. 3) Based on the results of testing PVC - the chlorinated organic wastes on the lab-scale unit, the ability of the technology application at pilot-scale level will be primary estimated. The adjustment and correction of some compositions in the lab-scale unit theoretically designed during experiment overcame the shortages by design and fabrication such as heat distribution regime, feeding wastes and draining spent salt. These solutions adapt to the technical requirement of operation as well as scientific requirement of the research on MSO process. PVC waste treatment was tested on the MSO lab-scale unit in different conditions of operation temperature, superficial air velocity related to air/oxygen feeding rate, waste feeding rate. The testing results showed that destruction efficiency of chlorine in MSO technology was almost absolute. HCl and Cl 2 emission were insignificant in different operation conditions. HCl and Cl 2 emission depend on resident time and nature of molten salt. However, with inherent attributes of MSO technology emission of CO is not avoided in processing waste treatment. Therefore, finding active solutions for reduction CO emission is essential to complete the technology. The experiments also were carried in conditions of single molten salt (Na 2 CO 3 ) and molten (Na 2 CO 3 - K 2 CO 3 ) eutectic. The comparison of efficiency of these tests gives idea of using molten salt eutectic to reduce operation cost in MSO technology. Based on operation parameters and scientific verification results during experiments, the introductory procedure of waste treatment by MSO process was built up. Thereby, primary estimation of development of the technology in pilot-scale is given

Multiple High Voltage Pulse Stressing of Polymer Thick Film Resistors

Directory of Open Access Journals (Sweden)

Busi Rambabu

2014-01-01

Full Text Available The purpose of this paper is to study high voltage interactions in polymer thick film resistors, namely, polyvinyl chloride- (PVC- graphite thick film resistors, and their applications in universal trimming of these resistors. High voltages in the form of impulses for various pulse durations and with different amplitudes have been applied to polymer thick film resistors and we observed the variation of resistance of these resistors with high voltages. It has been found that the resistance of polymer thick film resistors decreases in the case of higher resistivity materials and the resistance of polymer thick film resistor increases in the case of lower resistivity materials when high voltage impulses are applied to them. It has been also found that multiple high voltage pulse (MHVP stressing can be used to trim the polymer thick film resistors either upwards or downwards.

PVC flooring is related to human uptake of phthalates in infants.

Science.gov (United States)

Carlstedt, F; Jönsson, B A G; Bornehag, C-G

2013-02-01

Polyvinyl chloride (PVC) flooring material contains phthalates, and it has been shown that such materials are important sources for phthalates in indoor dust. Phthalates are suspected endocrine-disrupting chemicals (EDCs). Consecutive infants between 2 and 6 months old and their mothers were invited. A questionnaire about indoor environmental factors and family lifestyle was used. Urinary metabolites of the phthalates diethyl phthalate (DEP), dibutyl phthalate (DBP), butylbenzyl phthalate (BBzP), and dietylhexyl phthalate (DEHP) were measured in the urine of the children. Of 209 invited children, 110 (52%) participated. Urine samples were obtained from 83 of these. Urine levels of the BBzP metabolite monobenzyl phthalate (MBzP) was significantly higher in infants with PVC flooring in their bedrooms (P flooring material may increase the human uptake of phthalates in infants. Urinary levels of phthalate metabolites during early life are associated with the use of PVC flooring in the bedroom, body area, and the use of infant formula. This study shows that the uptake of phthalates is not only related to oral uptake from, for example, food but also to environmental factors such as building materials. This new information should be considered when designing indoor environment, especially for children. © 2012 John Wiley & Sons A/S.

Understanding Hydrothermal Dechlorination of PVC by Focusing on the Operating Conditions and Hydrochar Characteristics

Directory of Open Access Journals (Sweden)

Tian Li

2017-03-01

Full Text Available To remove chlorine from chlorinated wastes efficiently, the hydrothermal treatment (HT of PVC was investigated with a lower alkaline dosage in this work. Some typical operating conditions were investigated to find out the most important factor affecting the dechlorination efficiency (DE. The FTIR technique was employed to detect the functional groups in PVC and hydrochars generated to reveal the possible pathways for chlorine removal. The results show that the HT temperature was a key parameter to control the dechlorination reaction rate. At a HT temperature of 240 °C, about 94.3% of chlorine could be removed from the PVC with 1% NaOH. The usage of NaOH was helpful for chlorine removal, while a higher dosage might also hinder this process because of the surface poisoning and coverage of free sites. To some extent, the DE was increased with the residence time. At a residence time of 30 min, the DE reached a maximum of 76.74%. A longer residence time could promote the generation of pores in hydrochar which is responsible for the reduction in DE because of the re-absorption of water-soluble chlorine. According to the FTIR results, the peak intensities of both C=CH and C=C stretching vibrations in hydrochar were increased, while the peak at around 3300 cm−1 representing the –OH group was not obvious, indicating that the dehydrochlorination (elimination reaction was a main route for chlorine removal under these conditions studied in this work.

Practical problems in radiation sterilization of medical devices made from plasticized PVC

International Nuclear Information System (INIS)

Beenen, J.H.

1990-01-01

The following three methods for sterilizing medical devices made from plasticised PVC are used in the Netherlands. 1. sterilization by steam, steam-air or superheated water. 2. sterilization by electron beam or gamma irradiation. 3. ethylene oxide sterilization. IV-bags, blood bags and other bag types for similar applications made from plasticized PVC are mostly sterilized by steam-air or super heated water, especially when filled or partly filled containers are considered. More complicated products or products with components that cannot resist steam sterilization of 121 0 C are sterilized by ethylene oxide or irradiation. These last two methods also are favoured for sterilizing empty bags where sticking of the surfaces at the sterilization temperature creates a serious handicap. Moreover, steam sterilization may cause a permanent opacity of some plastics. However, we have to add that due to developments in formulations steam sterilization of empty bags is going to be of an increasing importance. proven carcinogenity of the gas ethylene oxide, difficult deaeration and retention of the gas in plasticized PVC has increased the demand for better radiation resistant plastics as an alternative for steam sterilization. (author)

Potentiometric Determination of Ketotifen Fumarate in Pharmaceutical Preparations and Urine Using Carbon Paste and PVC Membrane Selective Electrodes

Directory of Open Access Journals (Sweden)

Eman Y. Z. Frag

2011-01-01

Full Text Available This study compares between unmodified carbon paste (CPE; the paste has no ion pair and polyvinyl chloride (PVC membrane selective electrodes that were used in potentiometric determination of ketotifen fumarate (KTF, where sodium tetraphenylborate (NaTPB was used as titrant. The performance characteristics of these sensors were evaluated according to IUPAC recommendations which reveal a fast, stable, and linear response for KTF over the concentration range of 10−7 to 10−2 mol L−1. The electrodes show Nernstian slope value of 52.51±0.20 and 51.51±0.25 mV decade−1 for CPE and PVC membrane electrodes at 30∘C, respectively. The potential is nearly stable over the pH range 3.0–6.0 and 2.0–7.0 for CPE and PVC membrane electrodes, respectively. Selectivity coefficient values towards different inorganic cations, sugars, and amino acids reflect high selectivity of the prepared electrodes. The electrodes responses at different temperatures were also studied, and long operational lifetime of 12 and 5 weeks for CPE and PVC membrane electrodes, respectively, were found. These are used for determination of ketotifen fumarate using potentiometric titration, calibration, and standard addition methods in pure samples, its pharmaceutical preparations (Zaditen tablets, and biological fluid (urine. The direct potentiometric determination of KTF using the proposed sensors gave recoveries % of 98.97±0.53 and 98.62±0.74 with RSD 1.42 and 0.63% for CPE and PVC membrane selective electrodes, respectively. Validation of the method shows suitability of the proposed sensors for use in quality control assessment of KTF. The obtained results were in a good agreement with those obtained using the reported spectrophotometric method.

Potentiometric determination of ketotifen fumarate in pharmaceutical preparations and urine using carbon paste and PVC membrane selective electrodes.

Science.gov (United States)

Frag, Eman Y Z; Mohamed, Gehad G; Khalil, Mohamed M; Hwehy, Mohammad M A

2011-01-01

This study compares between unmodified carbon paste (CPE; the paste has no ion pair) and polyvinyl chloride (PVC) membrane selective electrodes that were used in potentiometric determination of ketotifen fumarate (KTF), where sodium tetraphenylborate (NaTPB) was used as titrant. The performance characteristics of these sensors were evaluated according to IUPAC recommendations which reveal a fast, stable, and linear response for KTF over the concentration range of 10(-7) to 10(-2) mol L(-1). The electrodes show Nernstian slope value of 52.51 ± 0.20 and 51.51 ± 0.25 mV decade(-1) for CPE and PVC membrane electrodes at 30°C, respectively. The potential is nearly stable over the pH range 3.0-6.0 and 2.0-7.0 for CPE and PVC membrane electrodes, respectively. Selectivity coefficient values towards different inorganic cations, sugars, and amino acids reflect high selectivity of the prepared electrodes. The electrodes responses at different temperatures were also studied, and long operational lifetime of 12 and 5 weeks for CPE and PVC membrane electrodes, respectively, were found. These are used for determination of ketotifen fumarate using potentiometric titration, calibration, and standard addition methods in pure samples, its pharmaceutical preparations (Zaditen tablets), and biological fluid (urine). The direct potentiometric determination of KTF using the proposed sensors gave recoveries % of 98.97 ± 0.53 and 98.62 ± 0.74 with RSD 1.42 and 0.63% for CPE and PVC membrane selective electrodes, respectively. Validation of the method shows suitability of the proposed sensors for use in quality control assessment of KTF. The obtained results were in a good agreement with those obtained using the reported spectrophotometric method.

Photoetching of Immobilized TiO2-ENR50-PVC Composite for Improved Photocatalytic Activity

Directory of Open Access Journals (Sweden)

M. A. Nawi

2012-01-01

Full Text Available Commercially acquired TiO2 photocatalyst (99% anatase powder was mixed with epoxidized natural rubber-50 (ENR50/polyvinyl chloride (PVC blend by ultrasonication and immobilized onto glass plates as TiO2-ENR50-PVC composite via a dip-coating method. Photoetching of the immobilized TiO2-ENR50-PVC composite was investigated under the irradiation of a 45 W compact fluorescent lamp and characterized by chemical oxygen demand (COD analysis, scanning electron microscopy-energy dispersive X-ray (SEM-EDX spectrometry, thermogravimetry analysis (TGA, and fourier transform infrared (FTIR spectroscopy. The BET surface area of the photoetched TiO2 composite was observed to be larger than the original TiO2 powder due to the systematic removal of ENR50 while PVC was retained within the composite. It also exhibited better photocatalytic efficiency than the TiO2 powder in a slurry mode and was highly reproducible and reusable. More than 98% of MB removal was consistently achieved for 10 repeated runs of the photo-etched photocatalyst system. About 93% of the 20 mg L−1 MB was mineralized over a period of 480 min. The presence of SO42−, NO3−, and Cl− anions was detected in the mineralized solution where the solution pH was reduced from 7 to 4.

Carneiro hidráulico com tubulação de alimentação em aço galvanizado e em PVC Hydraulic ram pump perfomance with PVC and steel pipes

Directory of Open Access Journals (Sweden)

Caroline Abate

2002-03-01

Full Text Available A recente crise da energia convencional tem ocasionado a exploração de fontes alternativas de energia. O bombeamento de água utilizando carneiro hidráulico é amplamente empregado em propriedades onde a energia elétrica é escassa ou inexistente. Procurando dar subsídios técnicos para a utilização do PVC nos sistemas de alimentação de um carneiro hidráulico, foi desenvolvido um experimento com objetivo de avaliar o desempenho de um carneiro hidráulico quando alimentado por uma tubulação de PVC e outra de aço galvanizado, sob três alturas de queda (2,1, 3,8 e 4,7 m. Foi utilizada a equação de D'Aubussion's para a avaliação do rendimento, calculado a partir de leituras de altura de recalque, vazão de escape, vazão de recalque e altura de alimentação. Pode-se conseguir o máximo rendimento com o carneiro hidráulico utilizando-se de tubulação de PVC com até 4,2 m de desnível; além desse valor a tubulação de aço galvanizado é mais eficiente.The recent conventional energy crisis is leading to the exploration of alternative energy sources. The pumping of water using ram pumps is widely used in farms where electric energy is scarce or inexistent. This experiment was carried out to evaluate the performance of an hydraulic ram pump utilizing two kinds of supply pipes (PVC and steel using three different supply heads (2.1, 3.8 and 4.7. Delivery head, delivery discharge, waste discharge and supply head were utilized to calculate the yield of the hydraulic ram by the equation of D'Aubussion. The maximum yield of the hydraulic ram was obtained for the PVC pipe for the 4.2 m head; for heads higher than 4.2 m the steel pipe was more efficient.

Sensory aspects and water quality impacts of chlorinated and chloraminated drinking water in contact with HDPE and cPVC pipe.

Science.gov (United States)

Heim, Timothy H; Dietrich, Andrea M

2007-02-01

Pipes constructed with high-density polyethylene (HDPE) or chlorinated polyvinyl chloride (cPVC) are commonly used in drinking water distribution systems and premise plumbing. In this comprehensive investigation, the effects on odor, organic chemical release, trihalomethane (THM) formation, free chlorine demand and monochloramine demand were determined for water exposed to HDPE and cPVC pipes. The study was conducted in accordance with the Utility Quick Test (UQT), a migration/leaching protocol for analysis of materials in contact with drinking water. The sensory panel consistently attributed a weak to moderate intensity of a "waxy/plastic/citrus" odor to the water from the HDPE pipes but not the cPVC-contacted water samples. The odor intensity generated by the HDPE pipe remained relatively constant for multiple water flushes, and the odor descriptors were affected by disinfectant type. Water samples stored in both types of pipe showed a significant increase in the leaching of organic compounds when compared to glass controls, with HDPE producing 0.14 microgTOC/cm(2) pipe surface, which was significantly greater than the TOC release from cPVC. Water stored in both types of pipe showed disinfectant demands of 0.1-0.9 microg disinfectant/cm(2) pipe surface, with HDPE exerting more demand than cPVC. No THMs were detected in chlorinated water exposed to the pipes. The results demonstrate the impact that synthetic plumbing materials can have on sensory and chemical water quality, as well as the significant variations in drinking water quality generated from different materials.

MECHANICAL, ELECTRICAL, AND THERMAL PROPERTIES OF MALEIC ANHYDRIDE MODIFIED RICE HUSK FILLED PVC COMPOSITES

OpenAIRE

Navin Chand; Bhajan Das Jhod

2008-01-01

Unmodified and modified rice husk powder filled PVC composites were prepared having different amounts of rice husk powder. Mechanical, thermal, and electrical properties of these composites were determined. The tensile strength of rice husk powder PVC composites having 0, 10, 20, 30, and 40 weight percent of rice husk powder was found to be 33.9, 19.4, 18.1, 14.6, and 9.5 MPa, respectively. Adding of maleic anhydride- modified rice husk powder improved the tensile strength of rice husk powder...

Stabilizing effect of epoxidized sunflower oil as a secondary stabilizer for Ca/Hg stabilized PVC

Directory of Open Access Journals (Sweden)

2008-01-01

Full Text Available Unsaturated triglyceride oil sunflower was epoxidized and characterized by chemical and spectroscopic methods. Epoxidized sunflower oil (ESO was used as an organic thermal co-stabilizer for rigid poly(vinyl chloride (PVC in the presence of tricalcium dicitrate (Ca3(C6H5O72 and mercury (II acetate (Hg(CH3COO2. The thermo-oxidative degradation of PVC was studied in the presence of these ternary stabilizer systems at 170, 180, 190 and 200°C in N2 atmosphere. The effects of metal carboxylate combination Ca/Hg in the absence and in the presence of epoxidized sunflower oil on static heat treatment of PVC have been studied. The formation of polyene sequences was investigated by UV-visible and FT-IR spectroscopy and by comparing viscosity data obtained in the presence and in the absence of the additives. It was found that the additives retard the rate of degradation and reduce the extent of polymer chain scission associated with the thermal degradation of poly(vinyl chloride. Synergistic effects were found when stabilizer was blended in 50:50 weight ratios with either. It was found that ESO exerted a stabilizing effect on the degradation of PVC. The activation energy for degraded PVC in absence of stabilizers was 38.6 kJ•mol–1 and in the presence of Ca/Hg and Ca/Hg/ESO were 53.3 and 64.7 kJ•mol–1 respectively. In order of compare the efficiency of the epoxidized sunflower oil with these metal soap stabilizers, thermal stabilities were evaluated on the basis of evolved hydrogen chloride determined by conductometry technique and degree of discoloration are discussed.

Functionalization of PVC membrane with ss oligonucleotides for a potentiometric biosensor.

Science.gov (United States)

Shishkanova, T V; Volf, R; Krondak, M; Král, V

2007-05-15

A novel application of a single stranded (ss) oligonucleotide as an active component of polymeric membrane in an ion-selective electrode (ISE) is described. The original oligonucleotides, oligo(dA)(15), modified by cholesterol, triphenylmethyl and hexadecyl derivatives, were immobilized into poly(vinyl chloride) (PVC) membrane using extraction protocol. In parallel, the adsorption protocol was used to immobilize unmodified oligo(dA)(15) on the PVC membrane based on tridodecylmethyammonium chloride (TDDMA(+)Cl(-)). Immobilization of ss oligonucleotide probe through spacer was more effective for the potentiometric detection of the hybridization between complementary oligonucleotides. It was found that cholesterol-oligo(dA)(15) modified membranes were sensitive toward complementary oligo(dT)(15) in the concentration range 2-80 nM at pH 7. An explanation for the detection mechanism is proposed.

Composite phase change materials prepared by encapsuling paraffin in PVC macrocapsules

International Nuclear Information System (INIS)

Chen, Yingbo; Zhang, Shifeng; Zhang, Qi; Chen, Yusheng; Zhang, Yufeng

2014-01-01

Highlights: • PVC macrocapsules coated with SiO 2 were synthesized. • Paraffin was encapsuled in the capsules. • The composite PCM has high heat capacity. • The composite PCM has no surpercooling. - Abstract: A novel phase change material capsules with SiO 2 in their surface was prepared by absorbing paraffin into PVC hollow capsules and by the polycondensation reaction of TEOS in different conditions. X-ray photoelectron spectroscopy (XPS) analysis and scanning electronic microscope (SEM) were used to determine chemical composition and microstructure of the composite capsules, respectively. Enthalpy capacity and thermal stability of the composite capsules are systematically characterized by using differential scanning calorimeter (DSC), thermogravimetric analyzer (TGA) and thermocycling tests. The composite has high heat capacity with good stability and absence of supercooling phenomena

Satisfactory reliability among nursing students using the instrument PVC ASSESS to evaluate management of peripheral venous catheters.

Science.gov (United States)

Ahlqvist, Margary; Berglund, Britta; Nordström, Gun; Klang, Birgitta; Johansson, Eva

2014-01-01

Nursing students should be given opportunities to participate in clinical audits during their education. However, audit tools are seldom tested for reliability among nursing students. The aim of this study was to present reliability among nursing students using the instrument PVC assess to assess management of peripheral venous catheters (PVCs) and PVC-related signs of thrombophlebitis. PVC assess was used to assess 67 inserted PVCs in 60 patients at ten wards at a university hospital. One group of nursing students (n=4) assessed PVCs at the bedside (inter-rater reliability) and photographs of these PVCs were taken. Another group of students (n=3) assessed the PVCs in the photographs after 4 weeks (test-retest reliability). To determine reliability, proportion of agreement [P(A)] and Cohen's kappa coefficient (κ) were calculated. For bedside assessment of PVCs, P(A) ranged from good to excellent (0.80-1.0) in 55% of the 26 PVC assess items that were tested. P(A) was poor (satisfactory reliability among nursing students. However, students need training in how to use the instrument before assessing PVCs.

Highly selective single-use fluoride ion optical sensor based on aluminum(III)-salen complex in thin polymeric film

International Nuclear Information System (INIS)

Badr, Ibrahim H.A.; Meyerhoff, Mark E.

2005-01-01

A highly selective optical sensor for fluoride ion based on the use of an aluminum(III)-salen complex as an ionophore within a thin polymeric film is described. The sensor is prepared by embedding the aluminum(III)-salen ionophore and a suitable lipophilic pH-sensitive indicator (ETH-7075) in a plasticized poly(vinyl chloride) (PVC) film. Optical response to fluoride occurs due to fluoride extraction into the polymer via formation of a strong complex with the aluminum(III)-salen species. Co-extraction of protons occurs simultaneously, with protonation of the indicator dye yielding the optical response at 529 nm. Films prepared using dioctylsebacate (DOS) are shown to exhibit better response (e.g., linear range, detection limit, and optical signal stability) compared to those prepared using ortho-nitrophenyloctyl ether (o-NPOE). Films formulated with aluminum(III)-salen and ETH-7075 indicator in 2 DOS:1 PVC, exhibit a significantly enhanced selectivity for fluoride over a wide range of lipophilic anions including salicylate, perchlorate, nitrate, and thiocyanate. The optimized films exhibit a sub-micromolar detection limit, using glycine-phosphate buffer, pH 3.00, as the test sample. The response times of the fluoride optical sensing films are in the range of 1-10 min depending on the fluoride ion concentration in the sample. The sensor exhibits very poor reversibility owing to a high co-extraction constant (log K = 8.5 ± 0.4), indicating that it can best be employed as a single-use transduction device. The utility of the aluminum(III)-salen based fluoride sensitive films as single-use sensors is demonstrated by casting polymeric films on the bottom of standard polypropylene microtiter plate wells (96 wells/plate). The modified microtiter plate optode format sensors exhibit response characteristics comparable to the classical optode films cast on quartz slides. The modified microtiter is utilized for the analysis of fluoride in diluted anti-cavity fluoride rinse

Treatment of PVC using an alternative low energy ion bombardment procedure

Science.gov (United States)

Rangel, Elidiane C.; dos Santos, Nazir M.; Bortoleto, José Roberto R.; Durrant, Steven F.; Schreiner, Wido H.; Honda, Roberto Y.; Rangel, Rita de Cássia C.; Cruz, Nilson C.

2011-12-01

increased after the treatment but such modifications were not stable after aging: the contact angle increased for all the samples, modifying the initially hydrophilic surface into a highly hydrophobic one. Consistently, the surface composition also changed after aging: there was carbon enrichment due to further losses of oxygen and chlorine. Another relevant factor for the elevation of θ was the change in morphology induced by the treatment. At greater powers, the uniform matrix of the PVC was transformed into a columnar structure containing randomly distributed sharp pillars. Interpretation of such results is proposed in terms of the total energy deposited in the solid by ionic collisions.

Treatment of PVC using an alternative low energy ion bombardment procedure

International Nuclear Information System (INIS)

Rangel, Elidiane C.; Santos, Nazir M. dos; Bortoleto, José Roberto R.; Durrant, Steven F.; Schreiner, Wido H.; Honda, Roberto Y.; Cássia C Rangel, Rita de; Cruz, Nilson C.

2011-01-01

increased after the treatment but such modifications were not stable after aging: the contact angle increased for all the samples, modifying the initially hydrophilic surface into a highly hydrophobic one. Consistently, the surface composition also changed after aging: there was carbon enrichment due to further losses of oxygen and chlorine. Another relevant factor for the elevation of θ was the change in morphology induced by the treatment. At greater powers, the uniform matrix of the PVC was transformed into a columnar structure containing randomly distributed sharp pillars. Interpretation of such results is proposed in terms of the total energy deposited in the solid by ionic collisions.

Influência do armazenamento refrigerado em associação com atmosfera modificada por filmes plásticos na qualidade de mangas 'Tommy Atkins Influence of refrigerated storage associated with plastic film-modified atmosphere in quality of 'Tommy Atkins' mangoes

Directory of Open Access Journals (Sweden)

Joaci Pereira de Sousa

2002-12-01

Full Text Available Avaliou-se a qualidade de mangas Tommy Atkins, embaladas em filmes plásticos e armazenadas sob condição refrigerada. Utilizaram-se frutos da safra 2000 obtidos na Fazenda Paulicéia Empreendimentos Ltda., situada no Pólo Agrícola Mossoró-Assu. Os frutos foram colhidos no estádio 2 (Brix 7 º e 75% verde e 25% vermelha e selecionados de acordo com o tipo 12 (12 frutos/caixa e tratados com fungicida para evitar podridões. No laboratório, os frutos foram submetidos aos seguintes tratamentos: 1 - frutos não embalados; 2 - frutos embalados individualmente em cloreto de polivinila (PVC; 3 - frutos embalados em sacola de polietileno de alta densidade (PEAD; 4 - frutos embalados em sacola de polietileno de baixa densidade (PEBD. Os frutos foram armazenados por 42 dias em condição controlada (11 ± 1°C; 85-90% UR. O armazenamento dos frutos sob condição controlada, associada à atmosfera modificada pelos filmes plásticos, reduziu-lhes a perda de matéria fresca e proporcionou-lhes a manutenção dos teores de sólidos solúveis totais, açúcares solúveis totais e acidez total titulável. A atmosfera modificada pelos filmes plásticos manteve mais regular as perdas na firmeza da polpa, possibilitando uma vida útil pós-colheita de 42 dias em ralação à testemunha. Até o final do armazenamento, o uso de PEAD promoveu o desenvolvimento da coloração da casca e da polpa dos frutos, porém o uso de PVC e PEBD reteve a coloração da casca.The quality of mangoes cv Tommy Atkins enclosed in plastic films and stored under refrigerated conditions were evaluated. Mangoes from the 2000 crop harvested at the Fazenda Paulicéia Empreendimentos Ltda., located in the Mossoró-Assu Agropole were used as experimental unity. The fruits were harvested in stage 2 ( 7º brix and 75% green, 25% red and selected for the type 12 (12 fruits/box, then treated with fungicide to prevent rots. The fruits were submited to the following treatments in the

Preparation of Carbon-Chitosan-Polyvinyl Chloride (CC-PVC) Material and its Application to Electrochemical Degradation of Methylene Blue in Sodium Chloride Solution

Science.gov (United States)

Riyanto; Prawidha, A. D.

2018-01-01

Electrochemical degradation of methylene blue using Carbon-Chitosan-Polyvinyl Chloride (CC-PVC) electrode in sodium chloride have been done. The aim of this work was to degradation of methylene blue using Carbon-Chitosan-Polyvinyl Chloride (CC-PVC). Carbon chitosan composite electrode was preparing by Carbon and Chitosan powder and PVC in 4 mL tetrahydrofuran (THF) solvent and swirled flatly to homogeneous followed by drying in an oven at 100 °C for 3 h. The mixture was placed in stainless steel mould and pressed at 10 ton/cm2. Sodium chloride was used electrolyte solution. The effects of the current and electrolysis time were investigated using spectrophotometer UV-Visible. The experimental results showed that the carbon-chitosan composite electrode have higher effect in the electrochemical degradation of methylene blue in sodium chloride. Based on UV-visible spectra analysis shows current and electrolysis time has high effect to degradation of methylene blue in sodium chloride. Chitosan and polyvinyl chloride can strengthen the bond between the carbons so that the material has the high stability and conductivity. As conclusions is Carbon-Chitosan-Polyvinyl Chloride (CC-PVC) electrode have a high electrochemical activity for degradation of methylene blue in sodium chloride.

Study on the interactions PVC/plasticizers by NMR

Energy Technology Data Exchange (ETDEWEB)

Tavares, Maria I.B.; Monteiro, Elisabeth E.C. [Universidade Federal, Rio de Janeiro, RJ (Brazil). Inst. de Macromoleculas; Harris, Robin [Durham Univ. (United Kingdom). Dept. of Chemistry

1992-12-31

The nature of the interactions between PVC and plasticizers as di-butyl phthalate and di-2-ethyl-hexyl phthalate can be investigated using proton/carbon-13 NMR techniques. The measurements of T{sub 1} for protons and carbon-13 and T{sub 1} P for protons can provide a good source of information about the complex behaviour for those two systems which were investigated. (author) 14 refs., 5 figs., 1 tab.

New polyvinyl chloride (PVC) nanocomposite consisting of aromatic polyamide and chitosan modified ZnO nanoparticles with enhanced thermal stability, low heat release rate and improved mechanical properties

Science.gov (United States)

Hajibeygi, Mohsen; Maleki, Mahdiye; Shabanian, Meisam; Ducos, Franck; Vahabi, Henri

2018-05-01

New ternary nanocomposite systems containing polylvinyl chloride (PVC), chitosan modified ZnO (CMZN) nanoparticles and new synthesized polyamide (PA) were designed and prepared by solution casting method. As a potential reinforcement, CMZN was used in PVC system combined with and without PA. Morphology, mechanical, thermal and combustion properties of the all PVC systems were studied. In the presence of the CMZN, PA showed a synergistic effect on improvement of the all investigated properties of PVC. The 5 mass% loss temperature (T5) was increased from 195 °C to 243 °C in PVC/CMZN-PA nanocomposite containing 1 mass% of each PA and CMZN (PZP 2). The peak of heat release rate was decreased from 131 W/g for PVC to 104 W/g for PVC/CMZN-PA nanocomposite containing 3 mass% of each PA and CMZN (PZP 6). According to the tensile tests, compared to the neat PVC, the tensile strength was increased from 35.4 to 53.4 MPa for PZP 6.

Cyclic Voltammetry of Biopolymer Heparin at PVC Plasticized Liquid Membrane

Czech Academy of Sciences Publication Activity Database

Samec, Zdeněk; Trojánek, Antonín; Langmaier, Jan; Samcová, E.

2003-01-01

Roč. 5, - (2003), s. 867-870 ISSN 1388-2481 R&D Projects: GA ČR GA203/04/0424 Institutional research plan: CEZ:AV0Z4040901 Keywords : cyclic voltammetry * PVC plasticized liquit membrane * heparin Subject RIV: CG - Electrochemistry Impact factor: 2.300, year: 2003

Penelitian penggunaan minarex sebagai plasticizer untuk pembuatan kompon slang PVC

Directory of Open Access Journals (Sweden)

Niken Karsiati

1995-12-01

Full Text Available The objective of the research is to find out the maximum quantity of Minarex as plasticizer which can be added in making compound PVC hose which fulfills the requirements of JIS K. 6771-77 “Flexible Vinyl Tube. Materials used are PVC resin added by additives, i.e DOP, BaCdZn, Stearic Acid, dyes and Minarex as DOP substitution. They all must be mixed and feed to two roll mill homogenizing. Temperature of operational is within 50-800C, roll speed is approximately 10 and 8,6 rpm. Then the compound is moulded into slab form using hydraulic press machine at 1700C, pressure 150 kg/cm2for 10 minutes. The slab is tested its physical properties including tensile strength, elongation at break, tensile strength after accelerated aging, and also observed organoleptically. Based on the research, compound with Minarex substitution 10 parts still conform to JIS K. 6771-77 and the appearance is good.

Feasibility study of the separation of chlorinated films from plastic packaging wastes.

Science.gov (United States)

Reddy, Mallampati Srinivasa; Yamaguchi, Takefumi; Okuda, Tetsuji; Tsai, Tsung-Yueh; Nakai, Satoshi; Nishijima, Wataru; Okada, Mitsumasa

2010-04-01

This study describes the possible separation of chlorinated plastic films (PVC and PVDC) from other heavy plastic packaging waste (PPW) by selective twist formation and gravity separation. Twists formation was mechanically induced in chlorinated plastic films, whereas twist formation did not occur in PS and PET films. After twist formation, all the films had the apparent density of less than 1.0g/cm(3) and floated in water even though the true density was more than 1.0g/cm(3). However, the apparent density of the PS and the PET films increased with agitation to more than 1.0g/cm(3), whereas that of chlorinated plastic films was kept less than 1.0g/cm(3). The main reason would be the air being held inside the chlorinated plastic films which was difficult to be removed by agitation. Simple gravity separation after twist formation was applied for artificial film with 10wt.% of the chlorinated films and real PPW films with 9wt.% of the chlorinated films. About 76wt.% of the artificial PPW films and 75wt.% of real PPW films after the removal of PP and PE were recovered as settling fraction with 4.7wt.% and 3.0wt.% of chlorinated plastic films, respectively. These results indicate that simple gravity separation process after twist formation can be used to reduce the chlorinated plastic concentration from mixed heavy PPW films. Copyright 2009 Elsevier Ltd. All rights reserved.

Feasibility study of the separation of chlorinated films from plastic packaging wastes

International Nuclear Information System (INIS)

Reddy, Mallampati Srinivasa; Yamaguchi, Takefumi; Okuda, Tetsuji; Tsai, Tsung-Yueh; Nakai, Satoshi; Nishijima, Wataru; Okada, Mitsumasa

2010-01-01

This study describes the possible separation of chlorinated plastic films (PVC and PVDC) from other heavy plastic packaging waste (PPW) by selective twist formation and gravity separation. Twists formation was mechanically induced in chlorinated plastic films, whereas twist formation did not occur in PS and PET films. After twist formation, all the films had the apparent density of less than 1.0 g/cm 3 and floated in water even though the true density was more than 1.0 g/cm 3 . However, the apparent density of the PS and the PET films increased with agitation to more than 1.0 g/cm 3 , whereas that of chlorinated plastic films was kept less than 1.0 g/cm 3 . The main reason would be the air being held inside the chlorinated plastic films which was difficult to be removed by agitation. Simple gravity separation after twist formation was applied for artificial film with 10 wt.% of the chlorinated films and real PPW films with 9 wt.% of the chlorinated films. About 76 wt.% of the artificial PPW films and 75 wt.% of real PPW films after the removal of PP and PE were recovered as settling fraction with 4.7 wt.% and 3.0 wt.% of chlorinated plastic films, respectively. These results indicate that simple gravity separation process after twist formation can be used to reduce the chlorinated plastic concentration from mixed heavy PPW films.

Resistance of particleboard panels made of agricultural residues and bonded with synthetic resins or PVC plastic to wood-rotting fungi

Directory of Open Access Journals (Sweden)

Divino Eterno Teixeira

2009-12-01

Full Text Available This study aims to evaluate the resistance of three types of particleboard panel to biodeterioration, two of which bonded with synthetic resins and one bonded with PVC plastic. Composite panels were made using sugar cane straw particles as raw material which were bonded together with urea-formaldehyde (UF, tannin-formaldehyde (TANI and PVC plastic (PVC resins. Decay tests were performed following procedures outlined in the ASTM D2017-81/1994 standard, whereby sample specimens were subjected to attack by white rot fungus Trametes versicolor and brown rot fungus Gloeophyllum trabeum using pine (Pinus sp. and embaúba (Cecropia sp. as reference timber. Panels bonded with PVC resin were rated ‘resistant’ to attack by both fungi while those bonded with UF and TANI resins were rated ‘slightly resistant’ to their attack.

Influence of the use of acids and films in post-harvest lychee conservation Influência da utilização de ácidos e filmes na conservação pós-colheita de lichia

Directory of Open Access Journals (Sweden)

Danielle Fabíola Pereira da Silva

2012-12-01

Full Text Available Lychee (Litchi chinensis Sonn. has a high commercial value; however, it has a short shelf-life because of its rapid pericarp browning. The objective of this study was to evaluate the shelf-life of 'Bengal' lychee fruits stored after treatment with hydrochloric acid and citric acid, associated with cassava starch and plastic packaging. Uniformly red pericarp fruits were submitted to treatments: 1-(immersion in citric acid 100 mM for 5 minutes + cassava starch 30 g L-1 for 5 minutes, 2-(immersion in hydrochloric acid 1 M for 2 minutes + starch cassava 30 g L-1 for 5 minutes, 3-(immersion in citric acid 100 mM for 5 minutes + polyvinyl chloride film (PVC, 14 µm thick and 4-(immersion in hydrochloric acid 1 M for 2 minutes + PVC film. During 20 days, the fruits were evaluated for mass loss, pericarp color, pH, soluble solids and titratable acidity, vitamin C of the pulp and pericarp and activities of polyphenol oxidase and peroxidase of the pericarp. The treatment with hydrochloric acid associated with PVC was the most effective in maintaining the red color of the pericarp for a period of 20 days and best preservation of the fruit. The cassava starch associated with citric acid, and hydrochloric acid did not reduce the mass loss and did not prevent the browning of lychee fruit pericarp.A lichia (Litchi chinensis Sonn. possui alto valor comercial no mercado, entretanto, apresenta vida útil pós-colheita curta, por causa do rápido escurecimento do pericarpo. O objetivo deste trabalho foi avaliar a vida útil pós-colheita de lichias 'Bengal', armazenadas após tratamento com ácido clorídrico e ácido cítrico, associados a fécula de mandioca e embalagem plástica. Frutos com pericarpos uniformemente vermelhos foram submetidos aos tratamentos: 1-( imersão em ácido cítrico 100 mM por 5 minutos + fécula de mandioca 30 g/L por 5 minutos; 2-( imersão em ácido clorídrico 1 M por 2 minutos + fécula de mandioca 30 g/L por 5 minutos; 3-( imers

Chilled water optimization at Beek INEOS PVC Plant : ammonia cycle

NARCIS (Netherlands)

Karami Alaghinloo, B.

2012-01-01

In BEEK INEOS PVC plant, polymerization takes place in a suspension process in twenty reactors in five lines. As the reaction is exothermic, a 17MW chilled water unit (CWU) removing heat from reactors which are producing different grades in batch processes. The objective of the project was to

Application of time-of-flight mass spectrometry with laser-based photoionization methods for analytical pyrolysis of PVC

Energy Technology Data Exchange (ETDEWEB)

Streibel, T.; Muehlberger, F. [GSF - Forschungszentrum fuer Umwelt und Gesundheit GmbH, Neuherberg (Germany); Adam, T.; Zimmermann, R. [Augsburg Univ. (Germany); Cao, L. [National Center for Iron and Steel, Beijing, BJ (China)

2004-09-15

Chlorinated benzenes and phenols generated from PVC pyrolysis are known to be precursors of PCDD/F formation. Therefore, selective and sensitive monitoring of these substances during PVC pyrolysis processes on an on-line, real-time basis could be very useful for the understanding of PCDD/F formation pathways. In this study, we investigated the pyrolysis gas from PVC samples derived from steel recycling by means of simultaneous single photon ionization/resonance-enhanced multiphoton ionization time-of-flight mass spectrometry (SPI/REMPI-TOFMS). The application of these soft photo-ionization techniques in mass spectrometry enables a fast and comprehensive analysis of this complex matrix without generating fragment ions, which would interfere with molecule ions making interpretation of the obtained mass spectra very difficult.

Excellent impact performance of PVC pipeline materials in gas distribution networks after many years of service (CD-rom)

NARCIS (Netherlands)

Visser, Roy; Hermkens, R.M.J.; Wolters, Mannes; Weller, J.; Warnet, Laurent; Beckervordersandforth, C.; Verberg, G.H.B.; Kramer, M.

2008-01-01

It has been about fifty years ago since the first unplasticized poly(vinyl chloride) (uPVC) pipes were installed for use in gas distribution purposes. Currently, about 22,500 km of uPVC is still in use in the Dutch gas distribution network. The pipes were originally designed for a lifetime of 50

Production of pre-basic potato seed by polyvinyl chloride PVC: articulate gutters hydroponic system

Directory of Open Access Journals (Sweden)

Jonny Everson Scherwinski-Pereira

2009-10-01

Full Text Available The development of more efficient and productive systems for pre-basic seed potato production would improve the quality of the propagative material used by the potato growers, directly affecting the crop yields. A two-year experiment was carried out to evaluate the potato pre-basic seed production by two types of hydroponic systems (fibrocement tiles and articulated PVC gutters, two cultivars (`Baronesa` and `Eliza` and two types of propagative material (plants coming from in vitro culture and minitubers. The PVC gutters system was highly efficient. When using minitubers, this system reached multiplication rates up to 74 tubers per plant. Minitubers were more productive than in vitro plants, independent of cultivar and hydroponic system utilized.Um experimento realizado por dois anos consecutivos avaliou a produção de sementes pré-básicas de batata por meio de sistemas de cultivo hidropônico. O trabalho testou a combinação de dois sistemas de cultivo (telha de fibrocimento e calhas de PVC articuladas, duas cultivares (Baronesa e Eliza e dois tipos de material propagativo (plântulas oriundas do cultivo in vitro e minitubérculos. O sistema de calhas de PVC foi altamente eficiente. Quando foi utilizado minitubérculos, este sistema alcançou taxas de multiplicação de até 74 tubérculos por planta. De modo geral, o uso de minitubérculos como material propagativo apresentou os melhores resultados de produtividade quando comparada ao material in vitro, independentemente da cultivar e sistemas hidropônicos utilizados.

Effect of complexing salt on conductivity of PVC/PEO polymer blend ...

Indian Academy of Sciences (India)

Administrator

composite polymer, a blend-based polymer electrolyte, composed of two conductive ... LiClO4 electrolytes with various methacrylic and acrylic polymers used as additives .... Z real vs Z imaginary plot for PVC : PEO : LiBF4 at room temperature.

Monitoring a PVC batch process with multivariate statistical process control charts

NARCIS (Netherlands)

Tates, A. A.; Louwerse, D. J.; Smilde, A. K.; Koot, G. L. M.; Berndt, H.

1999-01-01

Multivariate statistical process control charts (MSPC charts) are developed for the industrial batch production process of poly(vinyl chloride) (PVC). With these MSPC charts different types of abnormal batch behavior were detected on-line. With batch contribution plots, the probable causes of these

Preliminary results from film boiling destabilisation experiments

International Nuclear Information System (INIS)

Naylor, P.

1984-05-01

A series of experiments to investigate the triggered destabilisation of film boiling has been undertaken. Film boiling was established on a polished brass rod immersed in water and the effects of various triggers were investigated. Preliminary results are presented and two thresholds have been observed: an impulse threshold below which triggered destabilisation will not occur and a thermal threshold above which film boiling will re-establish following triggered destabilisation. (author)

AN INVESTIGATION OF THE IMPACT OF IMPURITIES ON THE MECHANICAL PROPERTIES OF RECYCLED PVC EXTRUSION PIPES

OpenAIRE

Adamu Alhaji Umar; Raji Olalere Fatai

2007-01-01

This work studied the effect of using recycled scraps in the production of rigid PVC extrusion pipe. Different formulations with varied percentages of scraps were extruded and various tests carried out on the sample specimen to determine their corresponding mechanical properties. It was finally discovered that among the two sources of scraps, the in-house scraps contained less impurities and blending about 10% of it with virgin PVC material in the production gave improved mechanical propertie...

Determination of HCl and VOC Emission from Thermal Degradation of PVC in the Absence and Presence of Copper, Copper(II Oxide and Copper(II Chloride

Directory of Open Access Journals (Sweden)

Ahamad J. Jafari

2009-01-01

Full Text Available Polyvinyl chloride (PVC has played a key role in the development of the plastic industry over the past 40 years. Thermal degradation of PVC leads to formation of many toxic pollutants such as HCl, aromatic and volatile organic carbon vapors. Thermal degradation of PVC and PVC in the present of copper, cupric oxide and copper(II chloride were investigated in this study using a laboratory scale electrical furnace. HCl and Cl- ion were analyzed by a Dionex ion chromatograph and VOCs compounds were analyzed using GC or GC-MS. The results showed that HCl plus Cl- ion and benzene formed about 99% and 80% respectively in the first step of thermal degradation under air atmosphere. The presence of cupric oxide increases the percentage of short chain hydrocarbons more than 184% and decreases the amount of the major aromatic hydrocarbon and HCl plus Cl- ion to 90% and 65% respectively. The total aromatic hydrocarbon emitted less than when atmosphere was air and difference was statistically significant (Pvalue<0.000

Monitoring of diisopropyl fluorophosphate hydrolysis by fluoride-selective polymeric films using absorbance spectroscopy

International Nuclear Information System (INIS)

Ramanathan, Madhumati; Wang Lin; Wild, James R.; Meyeroff, Mark E.; Simonian, Aleksandr L.

2010-01-01

In this study, a novel system for the detection and quantification of organofluorophosphonates (OFP) has been developed by using an optical sensing polymeric membrane to detect the fluoride ions produced upon OFP hydrolysis. Diisopropyl fluorophosphate (DFP), a structural analogue of type G chemical warfare agents such as Sarin (GB) and Soman (GD), is used as the surrogate target analyte. An optical sensing fluoride ion selective polymeric film was formulated from plasticized PVC containing aluminum(III) octaethyl porphyrin and ETH 7075 chromoionophore (Al[OEP]-ETH 7075). Selected formulations were used to detect the fluoride ions produced by the catalytic hydrolysis of DFP by the enzyme organophosphate hydrolase (OPH, EC 3.1.8.1). The changes in absorbance that corresponded to the deprotonated state of chromoionophore within the film results from simultaneous coextraction of fluoride and protons as DFP hydrolysis takes place in the solution phase in contact with the film. The developed sensing system demonstrates excellent sensitivity for concentrations as low as 0.1 μM DFP.

Monitoring of diisopropyl fluorophosphate hydrolysis by fluoride-selective polymeric films using absorbance spectroscopy

Energy Technology Data Exchange (ETDEWEB)

Ramanathan, Madhumati [Materials Research and Education Center, Auburn University, Auburn, AL 36849 (United States); Wang Lin [Department of Chemistry, University of Michigan, 930 North University, Ann Arbor, MI 48109 (United States); Wild, James R. [Biochemistry and Biophysics Department, Texas A and M University Texas AgriLife Research Program, College Station, TX 77843-2128 (United States); Meyeroff, Mark E. [Department of Chemistry, University of Michigan, 930 North University, Ann Arbor, MI 48109 (United States); Simonian, Aleksandr L., E-mail: simonal@auburn.edu [Materials Research and Education Center, Auburn University, Auburn, AL 36849 (United States)

2010-05-14

In this study, a novel system for the detection and quantification of organofluorophosphonates (OFP) has been developed by using an optical sensing polymeric membrane to detect the fluoride ions produced upon OFP hydrolysis. Diisopropyl fluorophosphate (DFP), a structural analogue of type G chemical warfare agents such as Sarin (GB) and Soman (GD), is used as the surrogate target analyte. An optical sensing fluoride ion selective polymeric film was formulated from plasticized PVC containing aluminum(III) octaethyl porphyrin and ETH 7075 chromoionophore (Al[OEP]-ETH 7075). Selected formulations were used to detect the fluoride ions produced by the catalytic hydrolysis of DFP by the enzyme organophosphate hydrolase (OPH, EC 3.1.8.1). The changes in absorbance that corresponded to the deprotonated state of chromoionophore within the film results from simultaneous coextraction of fluoride and protons as DFP hydrolysis takes place in the solution phase in contact with the film. The developed sensing system demonstrates excellent sensitivity for concentrations as low as 0.1 {mu}M DFP.

Flame treatment for the selective wetting and separation of PVC and PET.

Science.gov (United States)

Pascoe, R D; O'Connell, B

2003-01-01

Flame treatment has been used for many years to modify the surface of plastics to allow coatings to be added. The effect of the treatment is to produce hydrophilic species on the surface of the plastic making it water-wettable. The production of hydrophilic plastic surfaces is also required in the selective separation of plastics by froth flotation. For the process to be selective one plastic must be rendered hydrophilic while another remains hydrophobic. In this study the potential for separation of PVC and PET has been investigated. Flame treatment was shown to be very effective in producing a hydrophilic surface on both plastics, although the process was not selective under the conditions investigated. Raising the temperature of the plastics above their softening point produced a hydrophobic recovery. As the softening point of PVC was significantly lower than for PET it was possible to produce a significant difference in hydrophobicity, as judged using contact angle measurement. When immersed in water the contact angle of the PVC was found to be strongly dependent on the pH. Good separation efficiency of the two plastics was achieved by froth flotation from pH 4 to 9. One particular advantage of the technique is that no chemical reagents may be required in the flotation stage. The practicalities of designing a flake treatment system however have to be addressed before considering it to be a viable industrial process.

Flame treatment for the selective wetting and separation of PVC and PET

International Nuclear Information System (INIS)

Pascoe, R.D.; O'Connell, B.

2003-01-01

Flame treatment has been used for many years to modify the surface of plastics to allow coatings to be added. The effect of the treatment is to produce hydrophilic species on the surface of the plastic making it water-wettable. The production of hydrophilic plastic surfaces is also required in the selective separation of plastics by froth flotation. For the process to be selective one plastic must be rendered hydrophilic while another remains hydrophobic. In this study the potential for separation of PVC and PET has been investigated. Flame treatment was shown to be very effective in producing a hydrophilic surface on both plastics, although the process was not selective under the conditions investigated. Raising the temperature of the plastics above their softening point produced a hydrophobic recovery. As the softening point of PVC was significantly lower than for PET it was possible to produce a significant difference in hydrophobicity, as judged using contact angle measurement. When immersed in water the contact angle of the PVC was found to be strongly dependent on the pH. Good separation efficiency of the two plastics was achieved by froth flotation from pH 4 to 9. One particular advantage of the technique is that no chemical reagents may be required in the flotation stage. The practicalities of designing a flake treatment system however have to be addressed before considering it to be a viable industrial process

Effect analysis of material properties of picosecond laser ablation for ABS/PVC

Science.gov (United States)

Tsai, Y. H.; Ho, C. Y.; Chiou, Y. J.

2017-06-01

This paper analytically investigates the picosecond laser ablation of ABS/PVC. Laser-pulsed ablation is a wellestablished tool for polymer. However the ablation mechanism of laser processing for polymer has not been thoroughly understood yet. This study utilized a thermal transport model to analyze the relationship between the ablation rate and laser fluences. This model considered the energy balance at the decomposition interface and Arrhenius law as the ablation mechanisms. The calculated variation of the ablation rate with the logarithm of the laser fluence agrees with the measured data. It is also validated in this work that the variation of the ablation rate with the logarithm of the laser fluence obeys Beer's law for low laser fluences. The effects of material properties and processing parameters on the ablation depth per pulse are also discussed for picosecond laser processing of ABS/PVC.

Radiation graft polymerization of 4- vinylpyridine on polyvinylchloride-films. [Gamma radiation

Energy Technology Data Exchange (ETDEWEB)

Kudryavtsev, V.N.; Shapiro, A.; Endrikhovska-Bonamur, A.M.

1984-01-01

Radiation graft liquid phase polymerization of 4-vinylpyridine on PVC-films by the method of direct radiation is investigated. The samples are irradiated by Co/sup 60/ ..gamma..-source at 20 deg C and the dose rate of 39 Gy/s for 4-vinylpyridine solutions in methonol, as well as at-78 deg C and dose rate of 1.3 kGy/s for monomer solutions in hexane. Modified polyvinylchloride films with grafted poly-4-vinylpyridine chains are prepared. Being introduced in grafted polyvinylpyridine chains of ion-exchange groups, materials are characterized by good swelling in water and are good to prepare anion-exchange membranes.

The effect of light intensity and temperature on performance of photoelectrochemical solar cells of structure ITO/TiO2/PVC-LiClO4/graphite

International Nuclear Information System (INIS)

Mohd Yusri Abd Rahman; Muhammad Mat Salleh; Ibrahim Abu Talib; Muhammad Yahaya

2006-01-01

The photovoltaic characteristics of a photoelectrochemical solar cells of ITO/TiO 2 /PVC-LiCIO 4 /Graphite are reported. This paper is concerned with the effect of light intensity and temperature on performance of the device. The photoelectrochemical solar cell material was a screen-printed layer of titanium dioxide onto an ITO-covered glass substrate which was used as a working electrode of the device. The electrolyte used was PVC-LiCIO 4 that was prepared by solution casting technique. The ionic conductivity of the electrolyte as a function of temperature was obtained from impedance spectroscopy technique. The graphite film which serve as a counter electrode were prepared onto glass substrate by electron beam evaporation technique. The current-voltage, I-V characteristics of the device under illumination of 20, 40, 60, 80 and 100 mWcm -2 light from tungsten halogen lamp at 40 degree C were obtained using Keithley Voltmeter 175A and Keithley Amperemeter 197A. The current-voltage under illumination of 100 mWcm -2 at 30 degree C, 35 degree C, 40 degree C, 45 degree C and 50 degree C respectively were also obtained. It was found that efficiency of the device increases with both light intensity and temperature

Print Quality of Ink Jet Printed PVC Foils

Directory of Open Access Journals (Sweden)

Nemanja Kašiković

2015-09-01

Full Text Available Digital printing technique is used for a wide variety of substrates, one of which are PVC foils. Samples used in this research were printed by digital ink jet printing technique using Mimaki JV22 printing machine and J-Eco Subly Nano inks. As printing substrates, two different types of materials were used (ORACAL 640 - Print Vinyl and LG Hausys LP2712. A test card consisting of fields of CMYK colours was created and printed, varying the number of ink layers applied. Samples were exposed to light after the printing process. Spectrophotometric measurements were conducted before and after the light treatment. Based on spectrophotometricaly obtained data, colour differences ΔE2000 were calculated. Results showed that increasing number of layers, as well as the right choice of substrates, can improve the behaviour of printed product during exploitation.

THE STUDY OF TECHNOLOGICAL PROPERTIES OF PLASTISOLS BASED EMULSION PVC FILLED WITH CHALK GIDROFOBIZIROVANNYM

Directory of Open Access Journals (Sweden)

V. A. Sedykh

2014-01-01

Full Text Available Baby toys are made using the centrifugal molding plastisol based emulsion of polyvinyl chloride plasticized with dioctylphthalate. To reduce cost and decrease biotelemetry the dioctylphthalate on the surface of the product domestic toys than toys produced in China, there was a necessity of introduction of the filler is chalk from different manufacturers. By using a Brookfield vis-cometer PV-D was studied rheology of filled hydrophobized chalk PVC plastisols in storage conditions for up to 72 hours at temperatures of 14-20°C. It was found that the flow plastisols consistent with pseudo-plastic fluids. Given the flow rates of emulsion PVC plastisols filled to 35 % of the mass. hydrophobized chalk. The influence of the content of the plasticizer dioctylphthalate in a narrow interval (37,0 - 41,4 % of the mass. on the viscosity of polymer pastes and the kinetics of its changes during storage. Revealed a linear dependence of the viscosity of the filled hydrophobized chalk plastisols on the speed of rotation of the spindle of the viscometer and during storage. Given the rate of expansion changes the viscosity of the plastisols of the speed of rotation of the spindle of the viscometer, the rate of change in viscosity and calculation of the initial viscosity. Determined the stability of the dispersion hydrophobized chalk in a colloidal solution of PVC in dioctylphthalate during storage. We determined the variation of the content of chalk (ash with top and bottom layers plastisols height 8 cm after 24 hours storage. It is proved that the temperature of the preparation and storage of polymer pastes were determining factors in the regulation of such technological properties of PVC plastisols in the presence hydrophobized chalkas viscosity, stability of the dispersion of chalk and, consequently, the efficiency of distribution plastisols in the form of a centrifugal molding.

Effects of silica composition on gas permeability of ENR/PVC ...

African Journals Online (AJOL)

At higher SiO2 loadings, the mechanical strength of the membrane decreased due to the agglomeration of SiO2 particles. Gas permeation test was done on ENR/PVC/SiO2 membranes using NO2 gas and CO2 gas. The permeability of both gasses increased with the amount of SiO2 added to the membrane, which attributed ...

PVC membrane based potentiometric sensor for uranyl ion using thenoyl trifluoro acetone as ionophore

International Nuclear Information System (INIS)

Nanda, D.; Chouhan, H.P.S.; Maiti, B.

2004-01-01

Uranyl ion selective electrode based on thenoyl trifluoro acetone (TTA) incorporated into a polyvinyl chloride (PVC) membrane has been developed where dibutyl phthalate and sodium tetraphenyl borate have been used as plasticizer and anion excluder respectively. The PVC membrane containing the active ionophore, TTA, and the other ingredients has been directly cast a graphite electrode. The electrode shows near Nernstian response to UO 2 2+ in the concentration range of 10 -1 to 10 -6 mol. L -1 an average slope of 30 mV/decade. Alkali and alkaline earth ions do not interfere with the determination of uranyl ion. Interference of transition metal ions and Th (IV) is eliminated using EDTA. (author)

Mycelial fungi completely remediate di(2-ethylhexyl)phthalate, the hazardous plasticizer in PVC blood storage bag

Energy Technology Data Exchange (ETDEWEB)

Pradeep, S. [Enzyme Technology Laboratory, Biotechnology Division, Department of Botany, University of Calicut, Kerala 673 635 (India); Benjamin, Sailas, E-mail: sailasben@yahoo.co.in [Enzyme Technology Laboratory, Biotechnology Division, Department of Botany, University of Calicut, Kerala 673 635 (India)

2012-10-15

Highlights: Black-Right-Pointing-Pointer Three novel phthalate utilizing fungi: A. parasiticus, F. subglutinans and P. funiculosum. Black-Right-Pointing-Pointer Fungi utilize DEHP in PVC plastics in situ, in simple mineral salt medium. Black-Right-Pointing-Pointer Employing these fungi, a batch process can remediate phthalates in plastics. Black-Right-Pointing-Pointer Phthalate-free PVC can be recycled afresh. Black-Right-Pointing-Pointer Mineral salt and phthalate remediated into fungal biomass. - Abstract: This pioneering work describes how simply, inexpensively and efficiently novel fungi utilize the alarming plasticizer, di(2-ethylhexyl)phthalate (DEHP) blended in PVC blood storage bags (BB). In order to quantify total DEHP (33.5%, w/w) present in BB, it was extracted using n-hexane and confirmed by GC-MS. Three mycelial fungi, viz., Aspergillus parasiticus, Fusarium subglutinans and Penicillium funiculosum isolated in our laboratory form heavily plastics-contaminated soil - either singly or in consortium - completely consumed intact DEHP physically bound to BB by static submerged growth (28 Degree-Sign C) in simple basal salt medium (BSM). A two-stage cultivation strategy was adopted for the complete removal of DEHP from BB in situ. During the first growth stage, almost 70% DEHP contained in the BB was consumed in 2 weeks, accompanied by increased fungal biomass ({approx}0.15-0.35 g/g BB; OD {approx}7 at 600 nm) and a sharp declining (3.3) of initial pH (7.2). Spent BSM was replaced at this stagnant growth state (low pH), thus in the second stage, remaining DEHP bound to BB utilized completely (over 99%). Furthermore, A. parasiticus and F. subglutinans also grew well on scrapes of PVC water pipes in BSM. F. subglutinans was as efficient independently as consortium in completely utilizing the DEHP bound to BB, and these fungi offer great potentials for the inexpensive and eco-friendly bioremediation of phthalates in medical and allied PVC wastes on a large

Mycelial fungi completely remediate di(2-ethylhexyl)phthalate, the hazardous plasticizer in PVC blood storage bag

International Nuclear Information System (INIS)

Pradeep, S.; Benjamin, Sailas

2012-01-01

Highlights: ► Three novel phthalate utilizing fungi: A. parasiticus, F. subglutinans and P. funiculosum. ► Fungi utilize DEHP in PVC plastics in situ, in simple mineral salt medium. ► Employing these fungi, a batch process can remediate phthalates in plastics. ► Phthalate-free PVC can be recycled afresh. ► Mineral salt and phthalate remediated into fungal biomass. - Abstract: This pioneering work describes how simply, inexpensively and efficiently novel fungi utilize the alarming plasticizer, di(2-ethylhexyl)phthalate (DEHP) blended in PVC blood storage bags (BB). In order to quantify total DEHP (33.5%, w/w) present in BB, it was extracted using n-hexane and confirmed by GC–MS. Three mycelial fungi, viz., Aspergillus parasiticus, Fusarium subglutinans and Penicillium funiculosum isolated in our laboratory form heavily plastics-contaminated soil – either singly or in consortium – completely consumed intact DEHP physically bound to BB by static submerged growth (28 °C) in simple basal salt medium (BSM). A two-stage cultivation strategy was adopted for the complete removal of DEHP from BB in situ. During the first growth stage, almost 70% DEHP contained in the BB was consumed in 2 weeks, accompanied by increased fungal biomass (∼0.15–0.35 g/g BB; OD ∼7 at 600 nm) and a sharp declining (3.3) of initial pH (7.2). Spent BSM was replaced at this stagnant growth state (low pH), thus in the second stage, remaining DEHP bound to BB utilized completely (over 99%). Furthermore, A. parasiticus and F. subglutinans also grew well on scrapes of PVC water pipes in BSM. F. subglutinans was as efficient independently as consortium in completely utilizing the DEHP bound to BB, and these fungi offer great potentials for the inexpensive and eco-friendly bioremediation of phthalates in medical and allied PVC wastes on a large scale through a batch process in alleviating the plactics waste management issue.

Oil palm empty fruit bunch (OPEFB) fiber reinforced PVC/ENR blend-electron beam irradiation

International Nuclear Information System (INIS)

Ratnam, Chantara Thevy; Raju, Gunasunderi; Wan Md Zin Wan Yunus

2007-01-01

The effect of irradiation on the tensile properties of oil palm empty fruit bunch (OPEFB) fiber reinforced poly(vinyl chloride)/epoxidized natural rubber (PVC/ENR) blends were studied. The composites were prepared by mixing the fiber and the PVC/ENR blend using HAAKE Rheomixer at 150 deg. C. The composites were then irradiated by using a 3.0 MeV electron beam machine at doses ranging from 0 to 100 kGy in air and room temperature. The tensile strength, Young's modulus, elongation at break and gel fraction of the composites were measured. Comparative studies were also made by using poly(methyl acrylate) grafted OPEFB fiber in the similar blend system. An increase in tensile strength, Young's modulus and gel fraction, with a concurrent reduction in the elongation at break (Eb) of the PVC/ENR/OPEFB composites were observed upon electron beam irradiation. Studies revealed that grafting of the OPEFB fiber with methyl acrylate did not cause appreciable effect to the tensile properties and gel fraction of the composites upon irradiation. The morphology of fractured surfaces of the composites, examined by a scanning electron microscope showed an improvement in the adhesion between the fiber and the matrix was achieved upon grafting of the fiber with methyl acrylate

Utilization of Agrowaste Polymers in PVC/NBR Alloys: Tensile, Thermal, and Morphological Properties

Directory of Open Access Journals (Sweden)

Ahmad Mousa

2012-01-01

Full Text Available Poly(vinyl chloride/nitrile butadiene rubber (PVC/NBR alloys were melt-mixed using a Brabender Plasticorder at 180∘C and 50 rpm rotor speed. Alloys obtained by melt mixing from PVC and NBR were formulated with wood-flour- (WF- based olive residue, a natural byproduct from olive oil extraction industry. WF was progressively increased from 0 to 30 phr. The effects of WF loadings on the tensile properties of the fabricated samples were inspected. The torque rheometry, which is an indirect indication of the melt strength, is reported. The pattern of water uptake for the composites was checked as a function WF loading. The fracture mode and the quality of bonding of the alloy with and without filler are studied using electron scanning microscope (SEM.

Tubo de PVC liso com diferentes envoltórios como material alternativo na drenagem subterrânea Smooth PVC tube with different envelopes as an alternative material in the subsurface drainage

Directory of Open Access Journals (Sweden)

Florício P. de Almeida

2003-04-01

Full Text Available Em regiões áridas e semi-áridas irrigadas a drenagem é, freqüentemente, necessária para prevenir o encharcamento do solo e o controle da salinidade. Um dos principais obstáculos na instalação de um sistema de drenagem subterrânea é o alto custo do investimento inicial. Assim, alguma contribuição que reduza o custo da instalação dos drenos e também do material usado, é altamente vantajosa. Diante disso, o objetivo desta pesquisa foi avaliar, em condições de laboratório, o desempenho hidráulico do sistema drenante constituído pelo tubo de PVC liso, próprio para esgoto doméstico, de 50,0 mm de diâmetro nominal e área aberta de 23,0 cm² m-1, e por três tipos de envoltório. O desempenho do tubo drenante de PVC liso demonstrou que esse material é tecnicamente viável para drenagem agrícola, principalmente com o uso de brita como envoltório.In irrigated arid and semi-arid regions the drainage is, frequently, necessary to prevent the waterlogging of the soil and to control the salinity. One of the main obstacles in the installation of a subsurface drainage system is the high cost of the initial investment. Thus, some contribution that reduces the cost of the installation of the drains and also of the material used is highly advantageous. The objective of this research was to evaluate, under laboratory conditions, the hydraulic performance of the drainage system constituted by smooth PVC tube used for sewer with 50.0 mm of nominal diameter and open area of 23.0 cm² m-1 and different types of envelopes, as an alternative material for subsurface drainage. The performance of the smooth PVC tube demonstrated that this material is technically viable for agricultural drainage principally when used with single stones as envelope.

Deterioration of plasticized PVC components in Apollo spacesuits

DEFF Research Database (Denmark)

Shashoua, Yvonne; Schnell, Ulrich; Young, Lisa

2002-01-01

Spacesuits from the Apollo era are unique in their history, materials and construction. This project involved the first detailed examination of the condition of the spacesuits since their acquisition by the National Air and Space Museum in the 1970s. Plasticized polyvinyl chloride (PVC) tubing...... in the Life Support System, used to transport air and water to the astronaut, and in the Liquid Cooling Garment, used to cool the wearer of the spacesuit, exhibited high levels of deterioration. Tubing was unacceptably discoloured, tacky to the touch and surfaces were obscured by crystals. Visual examination...

"Action": Publishing Research Results in Film

Directory of Open Access Journals (Sweden)

Susan Thieme

2012-01-01

Full Text Available Researchers commonly disseminate their research findings in academic papers or books that have a selected and limited target audience. A potential method for disseminating the information other than the traditional academic is through film, but this means tailoring the material to this medium and in many cases collaborating with people who have the necessary skills. The aim of this article is to reflect on the experience of making a film from the researcher's perspective. I will in particular shed light on how the filmmaking team worked together and provide examples of the preceding research, as well as the shooting and editing of the film material. The long period of research leading up to the film was a major factor in its success. In addition, all of the people involved have to be willing to share their experiences, recognize each other's expertise and be able to compromise. The film was much more than just an extension of the ongoing multi-site qualitative research. The shooting not only provided new insights into people's lives but also forced me to think much harder about my research and "the fieldwork." The additional costs and efforts related to the film can be justified by a transdisciplinary understanding of research that requires the results to be disseminated beyond academic circles, attract attention from policymakers and activists, and also allow the subjects of the research (who generally do not read English academic articles to become an active audience. URN: http://nbn-resolving.de/urn:nbn:de:0114-fqs1201316

Molecular analysis of long-term biofilm formation on PVC and cast iron surfaces in drinking water distribution system.

Science.gov (United States)

Liu, Ruyin; Zhu, Junge; Yu, Zhisheng; Joshi, DevRaj; Zhang, Hongxun; Lin, Wenfang; Yang, Min

2014-04-01

To understand the impacts of different plumbing materials on long-term biofilm formation in water supply system, we analyzed microbial community compositions in the bulk water and biofilms on faucets with two different materials-polyvinyl chloride (PVC) and cast iron, which have been frequently used for more than10 years. Pyrosequencing was employed to describe both bacterial and eukaryotic microbial compositions. Bacterial communities in the bulk water and biofilm samples were significantly different from each other. Specific bacterial populations colonized on the surface of different materials. Hyphomicrobia and corrosion associated bacteria, such as Acidithiobacillus spp., Aquabacterium spp., Limnobacter thiooxidans, and Thiocapsa spp., were the most dominant bacteria identified in the PVC and cast iron biofilms, respectively, suggesting that bacterial colonization on the material surfaces was selective. Mycobacteria and Legionella spp. were common potential pathogenic bacteria occurred in the biofilm samples, but their abundance was different in the two biofilm bacterial communities. In contrast, the biofilm samples showed more similar eukaryotic communities than the bulk water. Notably, potential pathogenic fungi, i.e., Aspergillus spp. and Candida parapsilosis, occurred in similar abundance in both biofilms. These results indicated that microbial community, especially bacterial composition was remarkably affected by the different pipe materials (PVC and cast iron). Copyright © 2014 The Research Centre for Eco-Environmental Sciences, Chinese Academy of Sciences. Published by Elsevier B.V. All rights reserved.

MEASUREMENT AND MODELLING OF SORPTION EQUILIBRIUM CURVE OF WATER ON PA6, PP, HDPE AND PVC BY USING FLORY-HUGGINS MODEL

Directory of Open Access Journals (Sweden)

Suherman Suherman

2012-02-01

Full Text Available The sorption of water on granular polyamide-6 (PA6, granular polypropylene (PP, and powdery high density polyethylene (HDPE and powdery polyvinyl chloride (PVC were measured using a gravimetric method in a magnetic suspension balance (MSB. The Flory-Huggins model was successfully applied on the sorption equilibrium curve of all investigated polymers. The influence of temperature is low. The value of Flory-Huggins parameters(c of PA6, PVC, PP and HDPE were 1.8, 5.8, 6.3, and 8.1, respectively. The water in PA6 is mainly bound moisture, while in PP, HDPE and PVC it is mainly surface moisture.

Coated limestone as a filler for the production of PVC-products

Directory of Open Access Journals (Sweden)

Mihajlović Slavica

2005-01-01

Full Text Available The results of laboratory investigations of the possibility to obtain coated limestone for the production of PVC-products are presented in this paper. Limestone from the "Venčac" deposit (Aranđelovac, Serbia and Montenegro was used as the raw material. The investigations were carried out in two phases: obtaining the coated limestone and determination of the degree of coating. The results of the investigations showed that successful coating of the surface of the limestone particles with Ca-stearate (Ca-stearate content 3% was achieved in a vibro mill with rings and the obtained degree of coating was higher than 95%. The coating degree was determined in transmitted light by a polarization microscope applying the immersion method (water immersion.

Temperature and modified atmosphere affect the quality of okra Temperatura e atmosfera modificada influenciam a qualidade do quiabo

Directory of Open Access Journals (Sweden)

Fernando Luiz Finger

2008-01-01

Full Text Available Little information is available on the influence of temperature on plastic films wrapped okra (Albelmoschus esculentus for their postharvested conservation. This works investigated the influence of the temperature and PVC film on the development of chilling injury and storability from one of the most popular Brazilian cultivar of okra cv. Amarelinho in fruits stored at 5, 10ºC and at 25ºC. Fruits were harvest at commercial maturity stage with length ranging from 8 to 12 cm, and immediately wrapped in PVC over a polystyrene tray and than stored until visible deterioration or wilting symptoms. Lowering the temperature of storage room from 25 to 10 or 5ºC decreased the weight loss in both PVC wrapped and control fruits, with a lower rate at 5ºC. By reducing the temperature to 5 or 10ºC and wrapping the fruits in PVC film, the relative water content of the fruit pericarp was maintained throughout the storage, while at 25ºC the high weight loss was associated with significant reduction of the water content. The development of chilling symptoms was delayed by the presence of PVC film in fruits stored at 5ºC. However, at 10ºC symptoms of pitting were not developed in PVC wrapped or control fruits up to tenth day of storage. The rate of chlorophyll degradation was diminished by reducing the temperature and by wrapping the fruits with PVC film. The appearance of severe chilling symptoms at 5ºC was associated to less chlorophyll in the fruit pericarp on the control as compared to their content in the PVC wrapped fruits.Para o armazenamento do quiabo (Albelmoschus esculentus há poucas informações disponíveis sobre a influência da temperatura e filmes plásticos na conservação pós-colheita desta hortaliça. Para investigar a influência da temperatura e do filme de PVC na qualidade e desenvolvimento de sintomas de injúria por frio de uma das mais populares cultivares brasileira de quiabo cv. Amarelinho, os frutos foram armazenados a 5, 10

PET and PVC Separation with Hyperspectral Imagery

Directory of Open Access Journals (Sweden)

Monica Moroni

2015-01-01

Full Text Available Traditional plants for plastic separation in homogeneous products employ material physical properties (for instance density. Due to the small intervals of variability of different polymer properties, the output quality may not be adequate. Sensing technologies based on hyperspectral imaging have been introduced in order to classify materials and to increase the quality of recycled products, which have to comply with specific standards determined by industrial applications. This paper presents the results of the characterization of two different plastic polymers—polyethylene terephthalate (PET and polyvinyl chloride (PVC—in different phases of their life cycle (primary raw materials, urban and urban-assimilated waste and secondary raw materials to show the contribution of hyperspectral sensors in the field of material recycling. This is accomplished via near-infrared (900–1700 nm reflectance spectra extracted from hyperspectral images acquired with a two-linear-spectrometer apparatus. Results have shown that a rapid and reliable identification of PET and PVC can be achieved by using a simple two near-infrared wavelength operator coupled to an analysis of reflectance spectra. This resulted in 100% classification accuracy. A sensor based on this identification method appears suitable and inexpensive to build and provides the necessary speed and performance required by the recycling industry.

Preparation of Gas Sensor Based on Polymer Nanocomposite for Qualitative Detection of Hydrogen Sulfide

Directory of Open Access Journals (Sweden)

Elaheh Ghazizadeh

2016-11-01

Full Text Available Hydrogen sulfide (H2S, a by-product often produced in petrochemical processes, is well known as a dangerous and highly toxic gas to living organisms. The smell of H2S concentration of higher than 100 ppm can cause severe biological condition. Therefore, the detection of this gas is a crucial issue. In this work, nanocomposite porous films of polyurethane/silver (PU/Ag and poly(vinylchloride/silver (PVC/Ag consisting of 7 wt% nanoparticles were fabricated by phase inversion method and studied its qualitative detection capacity for H2S. The results indicated that after exposure to 50 ppm H2S, black points appeared on the surface of the test films within 10 min. However, the color completely disappeared when the films were left in the air for 20 min. Structural characteristics of the nanocomposites were studied by scanning electron microscopy (SEM, Fourier transform infrared spectroscopy (FTIR, X-ray diffractometry (XRD and thermal gravimetric analysis (TGA to confirm possible interactions which may have formed between the polymers and nanoparticles. According to the results, Ag nanoparticles were well dispersed in PU and PVC matrices giving particle sizes of less than 62 and 76 nm, respectively. The observations revealed that two recommended nanocomposites (PU/Ag and PVC/Ag could be used for detection of hydrogen sulfide at low level concentration. The response of Ag-embedded polymer films toward H2S vapour showed a better detection by PU/Ag compared to PVC/Ag. Therefore, the suggested silver nanoparticle-loaded PU and PVC sensor films are easily portable, simple to use and cost-less compared with other types of hydrogen sulfide sensors.

Equilibrium Relationship between SVOCs in PVC Products and the Air in Contact with the Product.

Science.gov (United States)

Eichler, Clara M A; Wu, Yaoxing; Cao, Jianping; Shi, Shanshan; Little, John C

2018-03-06

Phthalates and phthalate alternatives are semivolatile organic compounds (SVOCs) present in many PVC products as plasticizers to enhance product performance. Knowledge of the mass-transfer parameters, including the equilibrium concentration in the air in contact with the product surface ( y 0 ), will greatly improve the ability to estimate the emission rate of SVOCs from these products and to assess human exposure. The objective of this study was to measure y 0 for different PVC products and to evaluate its relationship with the material-phase concentrations ( C 0 ). Also, C 0 and y 0 data from other sources were included, resulting in a substantially larger data set ( N total = 34, T = 25 °C) than found in previous studies. The results show that the material/gas equilibrium relationship does not follow Raoult's law and that therefore the assumption of an ideal solution is invalid. Instead, Henry's law applies, and the Henry's law constant for all target SVOCs consists of the respective pure liquid vapor pressure and an activity coefficient γ, which accounts for the nonideal nature of the solution. For individual SVOCs, a simple partitioning relationship exists, but Henry's law is more generally applicable and will be of greater value in rapid exposure assessment procedures.

The use of artificial neural networks for mathematical modeling of the effect of composition and production conditions on the properties of PVC floor coverings

Directory of Open Access Journals (Sweden)

Radovanović Rajko M.

2017-01-01

Full Text Available The application of PVC floor coverings is strongly connected with their end-use properties, which depend on the composition and processing conditions. It is very difficult to estimate the proper influence of the production parameters on the characteristics of PVC floor coverings due to their complex composition and various preparation procedures. The effect of different processing variables (such as time of bowling, temperature of bowling and composition of PVC plastisol on the mechanical properties of PVC floor coverings was investigated. The influence of different input parameters on the mechanical properties was successfully determined using an artificial neural network with an optimized number of hidden neurons. The Garson and Yoon models were applied to calculate and describe the variable contributions in the artificial neural networks. [Projekat Ministarstva nauke Republike Srbije, br. III 45022

Determination of the Composition and Quantity of Phthalate Ester Additives in PVC Children's Toys. Greenpeace Research Laboratories Technical Note 06/97.

Science.gov (United States)

Stringer, Ruth; Labounskaia, Irina; Santillo, David; Johnston, Paul; Siddorn, John; Stephenson, Angela

Polyvinyl chloride (vinyl or PVC) is widely used in toys and other children's products. This study, conducted by Greenpeace, examined the composition and quantity of phthalate ester additives in children's PVC toys, used to give the toys added flexibility. Drawn from 17 countries, a total of 71 toys designed to be chewed by babies and young…

Detection of active noise control on the standard motorcycle exhaust Supra X 125 D using PVC pipe technique form Y

Science.gov (United States)

Isranuri, I.; Alfisyahrin; Nasution, A. R.

2018-02-01

This detection aims to obtain noise reduction on the supra X 125D motorcycle exhaust by using the Active Noise Control Method. The technique is done using a Y-shaped PVC pipe to be bolted on the exhaust, which then branch Y PVC is placed loudspeaker with impermeable conditions. The function of this loudspeaker is as a secondary noise to counter the primary noise of the sound of exhaust motorcycle Supra X 125D. The sound generator in this study is the ISD 4004 module, which serves to generate noise to counter the source noise. How this ISD 4004 module works is by recording source noise then recording the source noise and then reversed the phase 180° by phase reversing circuit. So that, the noise generated by the sound generator will hit the source noise and encounter or such as addition of two different phase of sound will result in noise reduction when detected at the end of the Y-shaped PVC pipe. Inverted phase reversed using feed-back resistor 1 kΩ and 2 kΩ input resistors, 16V capacitor 2500μf and as amplifier using ICL 7660 and TL 702 CP. Test results on the highest 1000 rpm rotation engine speed on the Z axis of 2 dB, and at the highest 2000 rpm rotation engine speed also occurs on the Z axis of 1.5 dB.

Immobilization of ionophore and surface characterization studies of the titanium(III) ion in a PVC-membrane sensor.

Science.gov (United States)

Rezayi, Majid; Heng, Lee Yook; Kassim, Anuar; Ahmadzadeh, Saeid; Abdollahi, Yadollah; Jahangirian, Hossein

2012-01-01

Novel ionophores comprising various hydroxide and amine structures were immobilized onto poly(vinyl chloride) (PVC) matrices, and these were examined to determine Ti(III) selectivity. To predict the selectivity of Ti(III), a PVC membrane was used to investigate the binding of Ti(III) to c-methylcalix[4]resorcinarene (CMCR). The study showed that the chelating ligand, CMCR, was coordinated selectively to Ti(III) at eight coordination sites involving the oxygen atoms at the interface of the membrane/solution. The membrane was prepared, based on CMCR as an ionophore, sodium tetrakis(4-fluorophenyl) borate (NaTFPB) as a lipophilic ionic additive, and dioctylphthalate (DOP) as a plasticizer. The immobilization of the ionophore and surface characterization studies revealed that the performance of CMCR-immobilized PVC was equivalent to that of mobile ionophores in supported liquid membranes (SLMs). The strengths of the ion-ionophore (CMCR-Ti(OH)(OH(2))(5) (2+)) interactions and the role of ionophores on membranes were studied via UV-Vis, Fourier transform infrared spectroscopy (FT-IR), scanning electron microscopy (SEM) and and X-ray diffraction (XRD).

Molecular Signatures for the PVC Clade (Planctomycetes, Verrucomicrobia, Chlamydiae and Lentisphaerae of Bacteria Provide Insights into their Evolutionary Relationships

Directory of Open Access Journals (Sweden)

Radhey S. Gupta

2012-09-01

Full Text Available The PVC superphylum is an amalgamation of species from the phyla Planctomycetes, Verrucomicrobia and Chlamydiae, along with the Lentisphaerae, Poribacteria and two other candidate divisions. The diverse species of this superphylum lack any significant marker that differentiates them from other bacteria. Recently, genome sequences for 37 species covering all of the main PVC groups of bacteria have become available. We have used these sequences to construct a phylogenetic tree based upon concatenated sequences for 16 proteins and identify molecular signatures in protein sequences that are specific for the species from these phyla or those providing molecular links among them. Of the useful molecular markers identified in the present work, 6 conserved signature indels (CSIs in the proteins Cyt c oxidase, UvrD helicase, urease and a helicase-domain containing protein are specific for the species from the Verrucomicrobia phylum; three other CSIs in an ABC transporter protein, cobyrinic acid ac-diamide synthase and SpoVG protein are specific for the Planctomycetes species. Additionally, a 3 aa insert in the RpoB protein is uniquely present in all sequenced Chlamydiae, Verrucomicrobia and Lentisphaerae species, providing evidence for the shared ancestry of the species from these three phyla. Lastly, we have also identified a conserved protein of unknown function that is exclusively found in all sequenced species from the phyla Chlamydiae, Verrucomicrobia, Lentisphaerae and Planctomycetes suggesting a specific linkage among them. The absence of this protein in Poribacteria, which branches separately from other members of the PVC clade, indicates that it is not specifically related to the PVC clade of bacteria. The molecular markers described here in addition to clarifying the evolutionary relationships among the PVC clade of bacteria also provide novel tools for their identification and for genetic and biochemical studies on these organisms.

Complicações determinadas por placas de cloreto de polivinila (PVC na estabilização da porção cervical caudal da coluna vertebral de cães Complications determined by polyvinylchloride (PVC plates in the stabilization of caudal cervical vertebral column of dogs

Directory of Open Access Journals (Sweden)

Mônica Vicky Bahr Arias

2003-12-01

Full Text Available Em 10 cães com peso médio de 14,6kg, as vértebras cervicais 5 e 6 foram cirurgicamente desestabilizadas através da secção do disco intervertebral e, em seguida, estabilizadas com placas ortopédicas confeccionadas com PVC de 2mm de espessura, para após 180 dias, proceder-se ao estudo histológico do tecido ósseo e conjuntivo circunvizinho. Constatou-se que o PVC causou alterações ósseas que podem ter favorecido o afrouxamento dos parafusos e a falha do implante. O material induziu ainda à formação de granuloma de corpo estranho e a reações inflamatórias locais que podem ter causado degradação do material implantado. Assim, placas de PVC, apesar de proporcionarem estabilidade e alinhamento da coluna vertebral, não satisfazem a maioria das propriedades necessárias a um biomaterial, não sendo recomendadaa a sua utilização em ortopedia veterinária.In ten dogs with an average mean weight of 14,6 kg, the cervical vertebra 5 and 6 were destabilized and fixed with plates of 2mm of thickness. The purpose of this work was to verify the effect of orthopedic PVC plates on the internal stabilization of the caudal cervical spine of dogs by studying the occurrence of alterations in the bone tissue and fibrous tissue adjacent to the plate after 180 days of permanence of the material in the dogs' organism. PVC causes progressive bone alterations, which, in the long term, could promote the loosening of the screws and failure of the implant. It also induces the formation of foreign body granuloma and inflammatory reactions which could cause degradation of the implant. Thus, PVC plates do not satisfy the majority of properties required of a biomaterial, its use not being recommended in veterinary orthopedics.

All-Solid-State, PVC Membrane, and Carbon Paste Ion-Selective Electrodes for Determination of Donepezil Hydrochloride in Pharmaceutical Formulation.

Science.gov (United States)

Khamees, Nesreen; Mohamed, Tagreed Abdel-Fattah; Derar, Abeer Rashad; Aziz, Azza

2017-09-01

All-solid-state, polyvinyl chloride (PVC) membrane, and carbon paste potentiometric ion-selective electrodes (ISEs) were proposed for the determination of donepezil hydrochloride (DON) in the drug substance and a pharmaceutical formulation. The potentiometric response toward DON was based on the existence of donepezil-tetraphenyl borate (DON-TPB) in a PVC membrane or a carbon paste in the presence of dioctylphthalate. In contrast, the solid-state electrode was prepared by direct incorporation of DON-TPB into a commercial nail varnish without external additives. The electrodes exhibited Nernstian slopes of 55.0, 57.0, and 53.0 mV/decade over the concentration ranges of 1 × 10-5 to 1 × 10-3, 1 × 10-4 to 10-2, and 1 × 10-4 to 5 × 10-3 for the solid-state, PVC membrane, and carbon paste electrodes, respectively. The response of the electrodes is independent of pH in the range of 2-≤8. The electrodes showed good selectivity for DON with respect to a number of inorganic cations and amino acids. The electrodes were used for the determination of DON in pure solution and in pharmaceutical tablets with high accuracy (±2%) and precision (RSD ≤2%). The solid-state electrode is simple, economical, and rapid when compared to the PVC membrane and carbon paste electrodes.

Elastic-Plastic Behaviour of Ultrasonic Assisted Compression of Polyvinyl Chloride (PVC) Foam

Science.gov (United States)

Muhalim, N. A. D.; Hassan, M. Z.; Daud, Y.

2018-04-01

The present study aims to investigate the elastic-plastic behaviour of ultrasonic assisted compression of PVC closed-cell foam. A series of static and ultrasonic compression test of PVC closed-cell foam were conducted at a constant cross head speed of 30 mm/min on dry surface condition. For quasi-static test, specimen was compressed between two rigid platens using universal testing machine. In order to evaluate the specimen behavior under ultrasonic condition, specimen was placed between a specifically design double-slotted block horn and rigid platen. The horn was designed and fabricated prior to the test as a medium to transmit the ultrasonic vibration from the ultrasonic transducer to the working specimen. It was tuned to a frequency of 19.89 kHz in longitudinal mode and provided an average oscillation amplitude at 6 µm on the uppermost surface. Following, the characteristics of stress-strain curves for quasi-static and ultrasonic compression tests were analyzed. It was found that the compressive stress was significantly reduced at the onset of superimposed ultrasonic vibration during plastic deformation.

Charge Transfer Resistance and Differential Capacity of the Plasticized PVC Membrane/Water Interface

Czech Academy of Sciences Publication Activity Database

Langmaier, Jan; Stejskalová, Květoslava; Samec, Zdeněk

2002-01-01

Roč. 521, 1/2 (2002), s. 81-86 ISSN 0022-0728 R&D Projects: GA AV ČR IAA4040902 Institutional research plan: CEZ:AV0Z4040901 Keywords : impedance * PVC plasticized membrane * ion transfer kinetics Subject RIV: CG - Electrochemistry Impact factor: 2.027, year: 2002

Roles of ionic strength and biofilm roughness on adhesion kinetics of Escherichia coli onto groundwater biofilm grown on PVC surfaces

Science.gov (United States)

Janjaroen, Dao; Ling, Fangqiong; Monroy, Guillermo; Derlon, Nicolas; Mogenroth, Eberhard; Boppart, Stephen A.; Liu, Wen-Tso; Nguyen, Thanh H.

2013-01-01

Mechanisms of Escherichia coli attachment on biofilms grown on PVC coupons were investigated. Biofilms were grown in CDC reactors using groundwater as feed solution over a period up to 27 weeks. Biofilm physical structure was characterized at the micro- and meso-scales using Scanning Electron Microscopy (SEM) and Optical Coherence Tomography (OCT), respectively. Microbial community diversity was analyzed with Terminal Restricted Fragment Length Polymorphism (T-RFLP). Both physical structure and microbial community diversity of the biofilms were shown to be changing from 2 weeks to 14 weeks, and became relatively stable after 16 weeks. A parallel plate flow chamber coupled with an inverted fluorescent microscope was also used to monitor the attachment of fluorescent microspheres and E. coli on clean PVC surfaces and biofilms grown on PVC surfaces for different ages. Two mechanisms of E. coli attachment were identified. The adhesion rate coefficients (kd) of E. coli on nascent PVC surfaces and 2-week biofilms increased with ionic strength. However, after biofilms grew for 8 weeks, the adhesion was found to be independent of solution chemistry. Instead, a positive correlation between kd and biofilm roughness as determined by OCT was obtained, indicating that the physical structure of biofilms could play an important role in facilitating the adhesion of E. coli cells. PMID:23497979

Application of electrostatic separation to the recycling of plastic wastes: separation of PVC, PET, and ABS.

Science.gov (United States)

Park, Chul-Hyun; Jeon, Ho-Seok; Yu, Hyo-Shin; Han, Oh-Hyung; Park, Jai-Koo

2008-01-01

Plastics are widely used in everyday life as a useful material, and thus their consumption is growing at a rate of about 5% per year in Korea. However, the constant generation of plastic wastes and their disposal generates environmental problems along with economic loss. In particular, mixed waste plastics are difficult to recycle because of their inferior characteristics. A laboratory-scale triboelectrostatic separator unit has been designed and assembled for this study. On the basis of the control of electrostatic charge, the separation of three kinds of mixed plastics, polyvinyl chloride (PVC), poly(ethylene terephthalate) (PET), and acrylonitrile-butadiene-styrene (ABS), in a range of similar gravities has been performed through a two-stage separation process. Polypropylene (PP) and high-impact polystyrene (HIPS) were found to be the most effective materials for a tribo-charger in the separation of PVC, PET, and ABS. The charge-to-mass ratio (nC/g) of plastics increased with increasing air velocity in the tribo charger. In the first stage, using the PP cyclone charger, the separation efficiency of particles considerably depended on the air velocity (10 m/s), the relative humidity ( 20 kV), and the splitter position (+2 cm from the center) in the triboelelctrostatic separator unit. At this time, a PVC grade of 99.40% and a recovery of 98.10% have successfully been achieved. In the second stage, using the HIPS cyclone charger, a PET grade of 97.80% and a recovery of 95.12% could be obtained under conditions of 10 m/s, over 25 kV, a central splitter position, and less than 40% relative humidity. In order to obtain 99.9% PVC grade and 99.3% PET grade, their recoveries should be sacrificed by 20.9% and 27%, respectively, with moving the splitter from the center to a (+)6 cm position.

Safety and effectiveness evaluation of a domestic peritoneal dialysis fluid packed in non-PVC bags: study protocol for a randomized controlled trial.

Science.gov (United States)

Zhou, Jianhui; Cao, Xueying; Lin, Hongli; Ni, Zhaohui; He, Yani; Chen, Menghua; Zheng, Hongguang; Chen, Xiangmei

2015-12-29

Peritoneal dialysis is an important type of renal replacement therapy for uremic patients. In peritoneal dialysis, fluids fill in and flow out of the abdominal cavity three to five times per day. Usually, the fluid is packed in a polyvinyl chloride (PVC) bag. Safety concerns have arisen over di-(2-ethylhexyl) phthalate, which is essential in the formation of PVC materials. In 2011, the National Development and Reform Commission of China released a catalog of industrial structural adjustments, mandating the elimination of PVC bags for intravenous infusion and food containers. Although bags for peritoneal dialysis fluid were not included in the elimination list, several manufacturers began to develop new materials for fluid bags. HUAREN peritoneal dialysis fluid consists of the same electrolytes and buffer agent as in Baxter fluid, but is packed in bags that do not contain PVC. This multicenter randomized controlled trial was designed to compare peritoneal dialysis fluid packed in non-PVC-containing and PVC-containing bags. Further, the study sought to determine the proper dose of peritoneal dialysis fluid and the actual survival rates of Chinese patients undergoing peritoneal dialysis. The study participants are adults undergoing continuous ambulatory peritoneal dialysis for 30 days to 6 months. All eligible patients are randomized (1:1) to peritoneal dialysis with Baxter and HUAREN dialysis fluids (initial dose, 6 l/day), with dosages adjusted according to a unified protocol. The primary outcomes are the 1-, 2-, 3-, 4-, and 5-year overall survival rates. Secondary outcome measures include technique survival rates, reductions in estimated glomerular filtration rate, nutritional status, quality of life, cardiovascular events, medical costs and drop-out rates. Safety outcome measures include adverse events, changes in vital signs and laboratory parameters, peritonitis, allergies, and quality of products. This study is the first to evaluate the long-term safety and

Photostabilizing Efficiency of Poly(vinyl chloride in the Presence of Organotin(IV Complexes as Photostabilizers

Directory of Open Access Journals (Sweden)

Mustafa M. Ali

2016-08-01

Full Text Available Three organotin complexes containing furosemide as a ligand (L, Ph3SnL, Me2SnL2 and Bu2SnL2, were synthesized and characterized. Octahedral geometry was proposed for the Me2SnL2 and Bu2SnL2, while the Ph3SnL complex has trigonal bipyramid geometry. The synthesized organotin complexes (0.5% by weight were used as additives to improve the photostability of poly(vinyl chloride, PVC, (40 μm thickness upon irradiation. The changes imposed on functional groups, weight loss and viscosity average molecular weight of PVC films were monitored. The experimental results show that the rate of photodegradation was reduced in the presence of the organotin additives. The quantum yield of the chain scission was found to be low (9.8 × 10−7 when Ph3SnL was used as a PVC photostabilizer compared to controlled PVC (5.18 × 10−6. In addition, the atomic force microscope images for the PVC films containing Ph3SnL2 after irradiation shows a smooth surface compared to the controlled films. The rate of PVC photostabilization was found to be highest for Ph3SnL followed by Bu2SnL2 and Me2SnL2. It has been suggested that the organotin complexes could act as hydrogen chloride scavengers, ultraviolet absorbers, peroxide decomposers and/or radical scavengers.

CORRELATION OF THE GLASS TRANSITION TEMPERATURE OF PLASTICIZED PVC USING A LATTICE FLUID MODEL

Science.gov (United States)

A model has been developed to describe the composition dependence of the glass transition temperature (Tg) of polyvinyl chloride (PVC) + plasticizer mixtures. The model is based on Sanchez-Lacombe equation of state and the Gibbs-Di Marzio criterion, which states that th...

Experimental and numerical analysis of water hammer in a large-scale PVC pipeline apparatus

NARCIS (Netherlands)

Bergant, A.; Hou, Q.; Keramat, A.; Tijsseling, A.S.; Gajic, A.; Benisek, M.; Nedeljkovic, M.

2011-01-01

This paper investigates the effects of the pipe-wall viscoelasticity on water-hammer pressures. A large-scale pipeline apparatus made of polyvinyl chloride (PVC) at Deltares, Delft, The Netherlands, has been used to carry out waterhammer experiments. Tests have been conducted in a

1H-NMR/13C-NMR studies of branched structures in PVC obtained at atmospheric pressure

International Nuclear Information System (INIS)

Braun, D.; Holzer, G.; Hjertberg, T.

1981-01-01

The 1 H-NMR-spectra of raw poly (vinyl cloride) obtained at atmospheric pressure (U-PVC) have revealed the presence of high concentrations of branches. The content of labile chlorine was determined by reaction with phenole in order to estimate the branch points with tertiary chlorine. The branch length of reductively dehalogenated U-PVC by 13 C-NMR analysis have provided evidence for both short chain branches including chloromethyl groups and 2.4-dichloro-n-butyl groups and long chain branching. For a number of U-polymers the total amount of branching ranges from 7.5 to 13.5/1000 C. The 13 C-NMR measurements point to a ratio of methyl/butyl branches of 1:1 and short chains/long chains of 6:1. (orig.)

Preparation and characterization of polymer nanocomposites based on PVDF/PVC doped with graphene nanoparticles

Directory of Open Access Journals (Sweden)

I.S. Elashmawi

Full Text Available Novel nanocomposites based on PVDF/PVC blend containing graphene oxide nanoparticles (GO were prepare using sonicator. IR analysis revealed that the addition of GO prompts a crystal transformation of α-phase of PVDF. The change of the structural before and after adding GO to PVDF/PVC were studied by X-ray diffraction. A decrease in activation energy gap from UV data was observed with increasing GO content, implying a variation of reactivity as a result of reaction extent. The variation of ε′ with frequency is nearly the same as that of ε″. At higher frequencies, the decrease of both ε′ and ε″ becomes nearly constant. The dispersion at lower frequencies ε′ of ε′ polarization is of Maxwell–Wagner interfacial polarization but at higher frequencies, it levels off. The behavior of conductivity (σAC tends to acquire constant values approaching it DC values. The values of σAC was increased after doped GO with exponential increase after the critical value of frequency. All nanocomposites behaved the same fashion revealing that a higher number of polarons were getting added to conducting pool in composites as graphene content was increased. Conduction mechanism appeared to be getting expedited with increasing frequency due to fact that increase in frequency enhances polaron hopping frequency. Keywords: Nanocomposites, Graphene oxide, FT-IR, X-ray, AC conductivity

PVC esaslı CTP kesme atığı dolgulu malzemelerin termal özelliklerinin incelenmesi

Directory of Open Access Journals (Sweden)

Arzu Özüyağlı

2016-08-01

Full Text Available Bu çalışmada, PVC üretiminde kullanılan CaCO3 dolgu malzemesi yerine, sanayi atığı kullanılması sonucu termal özelliklerdeki değişim araştırılmıştır. Kullanılan sanayi atığı CTP boru üretiminden sulu kesim sırasında çıkmakta ve SiO2, cam elyaf ve polyester reçine içermektedir. Sulu çamur halinde filtre presten çıkan atık fabrikadan alındıktan sonra kurutma ve eleme işlemleri uygulanarak toz formuna getirilmiştir. Numuneler PVC, CTP atık tozu ve prosese yardımcı maddeler mikserde karıştırılarak ekstrüzyon yöntemi ile profil şeklinde üretilmiştir. Atık toz PVC’ye oranla ağırlıkça %5-%70 oranlarında dolgu malzemesi olarak kullanılmıştır. Kalsit (CaCO3 katkılı ve katkısız PVC numuneleri de benzer proses parametreleri kullanılarak üretilmiştir. Üretilen numuneler, seramik krozeler kullanılarak DTA-TG analizleri yapılmıştır.

Polyvinyl chloride degradation by X-rays

International Nuclear Information System (INIS)

Sbampato, M.E.

1984-01-01

Degradation of film samples of pure PVC and comercial film (PVC + Polyacrylatis) with vacuum X-rays using the following techniques: infra-red, Raman, ultra violet and visible spectroscopies, eletronic paramagnetic resonance, X-rays difraction, percent measurement of transmitance and microanalysis was studied. (L.M.J.) [pt

Estudo Comparativo dos custos e aquisição de PVC no Brasil: mercado interno versus importação

Directory of Open Access Journals (Sweden)

André Bueno Borges

2015-10-01

Full Text Available A pesquisa tem por objetivo mapear o processo de aquisição analisando os custos para venda de PVC no Brasil. Portanto, foi realizado um estudo comparativo dos custos e tributações dos processos de importação. As cotações do preço do PVC são extraídas do site ICIS Pricing que é o maior fornecedor de informações de mercado petroquímico do mundo. A produção nacional do PVC é menor do que o consumo, fazendo com que a importação do produto seja frequente pelas empresas transformadoras de plástico. Pelo trabalho exposto, observa-se que os benefícios resultantes da pesquisa de preço do produto no mercado mundial. Foi demonstrado que o produto importado da China ou dos Estados Unidos apresenta valores em torno de 20% menores do que o praticado no mercado nacional.

Dehydrohalogenation during pyrolysis of brominated flame retardant containing high impact polystyrene (HIPS-Br) mixed with polyvinylchloride (PVC)

Energy Technology Data Exchange (ETDEWEB)

Uddin, M.A.; Bhaskar, T.; Kaneko, J.; Muto, A.; Sakata, Y.; Matsui, T. [Okayama University, Okayama (Japan). Dept. of Applied Chemistry, Faculty of Engineering

2002-09-01

Dehydrohalogenation during pyrolysis of brominated flame retardant containing polystyrene (brominated high impact polystyrene (HIPS-Br)) mixed with polyvinylchloride (PVC) was carried out in a laboratory scale batch process. Thermal and catalytic degradation of HIPS-Br mixed with PVBC on carbon composite of iron oxide (TR-00301) catalyst was investigated. The thermal degradation of waste plastics (HIPS-Br/PVC) yielded liquid products with 55,000 ppm bromine and 4300 ppm chlorine content in oil. Catalytic degradation (4 g; TR-00301) of HIPS-Br/PVC waste plastics at 430{degree}C produced halogen-free clean oil, which can be used as a fuel oil or chemical feedstock. The main liquid products during catalytic degradation were benzene, toluene, styrene, ethyl benzene, {alpha}-methyl styrene, butyl benzene, 1,2-dimethyl benzene etc. The average carbon number of the liquid products produced during catalytic degradation (9.3) of waste plastics was less than that of the thermal degradation (10.4) and the density of liquid products was found to be lower during the catalytic degradation than the thermal degradation. The possibility of a single step catalytic process for the conversion of halogenated waste plastics into fuel oil with the simultaneous removal of chlorine and bromine content form the oil was demonstrated. 21 refs., 7 figs., 2 tabs.

A physical probabilistic model to predict failure rates in buried PVC pipelines

International Nuclear Information System (INIS)

Davis, P.; Burn, S.; Moglia, M.; Gould, S.

2007-01-01

For older water pipeline materials such as cast iron and asbestos cement, future pipe failure rates can be extrapolated from large volumes of existing historical failure data held by water utilities. However, for newer pipeline materials such as polyvinyl chloride (PVC), only limited failure data exists and confident forecasts of future pipe failures cannot be made from historical data alone. To solve this problem, this paper presents a physical probabilistic model, which has been developed to estimate failure rates in buried PVC pipelines as they age. The model assumes that under in-service operating conditions, crack initiation can occur from inherent defects located in the pipe wall. Linear elastic fracture mechanics theory is used to predict the time to brittle fracture for pipes with internal defects subjected to combined internal pressure and soil deflection loading together with through-wall residual stress. To include uncertainty in the failure process, inherent defect size is treated as a stochastic variable, and modelled with an appropriate probability distribution. Microscopic examination of fracture surfaces from field failures in Australian PVC pipes suggests that the 2-parameter Weibull distribution can be applied. Monte Carlo simulation is then used to estimate lifetime probability distributions for pipes with internal defects, subjected to typical operating conditions. As with inherent defect size, the 2-parameter Weibull distribution is shown to be appropriate to model uncertainty in predicted pipe lifetime. The Weibull hazard function for pipe lifetime is then used to estimate the expected failure rate (per pipe length/per year) as a function of pipe age. To validate the model, predicted failure rates are compared to aggregated failure data from 17 UK water utilities obtained from the United Kingdom Water Industry Research (UKWIR) National Mains Failure Database. In the absence of actual operating pressure data in the UKWIR database, typical

Investigation of the primary plasticisers present in polyvinyl chloride (PVC) products currently authorised as food contact materials.

Science.gov (United States)

Carlos, Katherine S; de Jager, Lowri S; Begley, Timothy H

2018-03-15

PVC is a common food contact material that is usually plasticised to increase its flexibility. Phthalates are one class of chemical compounds that are often used as plasticisers in PVC in a wide range of industries. They may be used in packaging materials for foods and can also be found in components of certain food processing equipment such as conveyor belts and tubing. Transfer of plasticisers from packaging to foods can occur. In recent years, there has been increased interest in understanding the health effects of phthalates, as well as the possible human exposure levels. However, there is limited information available about the routes of exposure to phthalates. In July 2014, the Chronic Hazard Advisory Panel (CHAP) produced a report for the U.S. Consumer Product Safety Commission detailing the potential health hazards of phthalates and phthalate alternatives. This report listed diet as one factor contributing greater than or equal to 10% of total phthalate exposure. As a result of this report, the U.S. Food and Drug Administration (FDA) is interested in determining the types of the primary plasticiser present in food packaging and processing materials as well as their concentrations. An investigation was conducted of 56 different samples of PVC food packaging and food processing materials available in the US market using a solvent extraction and GC-MS analysis. Nine different plasticisers including three phthalates, di(2-ethylhexyl) phthalate, diisononyl phthalate and diisodecyl phthalate, were identified in the products tested. The plasticiser concentrations ranged from 1 to 53% depending on the types of food contact materials and the type of plasticiser. Overall, it appears that manufacturers are switching away from phthalates as their primary plasticiser to alternate compounds such as ESBO, ATBC, DEHT, DINCH, DEHA and DINA.

Comparative acute toxicity of leachates from plastic products made of polypropylene, polyethylene, PVC, acrylonitrile-butadiene-styrene, and epoxy to Daphnia magna.

Science.gov (United States)

Lithner, Delilah; Nordensvan, Ildikó; Dave, Göran

2012-06-01

The large global production of plastics and their presence everywhere in the society and the environment create a need for assessing chemical hazards and risks associated with plastic products. The aims of this study were to determine and compare the toxicity of leachates from plastic products made of five plastics types and to identify the class of compounds that is causing the toxicity. Selected plastic types were those with the largest global annual production, that is, polypropylene, polyethylene, and polyvinyl chloride (PVC), or those composed of hazardous monomers (e.g., PVC, acrylonitrile-butadiene-styrene [ABS], and epoxy). Altogether 26 plastic products were leached in deionized water (3 days at 50°C), and the water phases were tested for acute toxicity to Daphnia magna. Initial Toxicity Identification Evaluations (C18 filtration and EDTA addition) were performed on six leachates. For eleven leachates (42%) 48-h EC50s (i.e the concentration that causes effect in 50 percent of the test organisms) were below the highest test concentration, 250 g plastic/L. All leachates from plasticized PVC (5/5) and epoxy (5/5) products were toxic (48-h EC50s ranging from 2 to 235 g plastic/L). None of the leachates from polypropylene (5/5), ABS (5/5), and rigid PVC (1/1) products showed toxicity, but one of the five tested HDPE leachates was toxic (48-h EC50 17-24 g plastic/L). Toxicity Identification Evaluations indicated that mainly hydrophobic organics were causing the toxicity and that metals were the main cause for one leachate (metal release was also confirmed by chemical analysis). Toxic chemicals leached even during the short-term leaching in water, mainly from plasticized PVC and epoxy products.

Review of the use of rigid and high-impact PVC pipes in natural gas distribution systems in the Netherlands

Energy Technology Data Exchange (ETDEWEB)

Mutter, F; Benjamin, P

1974-08-01

Because of a number of instances of stress corrosion cracking or crazing occurring in PVC pipes used in Dutch gas distribution systems, VEG-GASINSTITUUT began an intensive investigation of rigid PVC pipes and high-impact pipes in distribution use under various conditions and with varying service lives. The work led to an investigation of laboratory testing techniques in which the stress-cracking phenomenon found in practice could be duplicated under controllable conditions. Pipes of various materials were examined for their resistance to stress cracking, then this resistance was compared with other long- and short-term physical properties of the material.

Preparação de argila modificada com cloreto de cetilpiridíneo e avaliação da interação desta com o PVC Preparation of modified clay with cetylpyridinium chloride and evaluation of their interaction with PVC

Directory of Open Access Journals (Sweden)

Daniel K. Resende

2010-09-01

Full Text Available Foi preparada uma argila modificada com cloreto de cetilpiridíneo a partir da argila sódica por troca de cátions em solução. Foi avaliada a quantidade de agente de modificação em relação à argila sódica e o tempo reacional. Os materiais obtidos foram caracterizados por difração de raio X (XRD, análise termogravimétrica (TGA e ressonância magnética nuclear (RMN de baixo campo. Após a caracterização foi confirmada a modificação da argila e, também, foi verificado que o produto obtido pode ser empregado na preparação de nanocompósitos de PVC, considerando que o início da degradação do material preparado ocorreu em temperatura superior às comumente utilizadas no processamento do polímero. A adição da argila modificada apresentou uma dispersão adequada no PVC e manteve o início da degradação do material em temperatura compatível com o processamento do polímero, gerando um nanocompósito com parte esfoliada e intercalada.A modified silicate with cetylpyridinium was prepared from sodium clay with cation exchange in solution. The amount of modification agent for clay and the reaction time were evaluated. The materials produced were characterized using X ray diffraction (XRD, termogravimetric analysis (TGA and low field nuclear magnetic resonance (NMR. The formation of new organic clay was confirmed, which was introduced in PVC for the formation of nanocomposites. The beginning of degradation of the new clay occurred at temperatures higher than commonly used in the processing of PVC. The nanocomposites were partially exfoliated and partially intercalated.

Heat Conductivity Resistance of Concrete Wall Panel by Water Flowing in Different Orientations of Internal PVC pipe

Science.gov (United States)

Umi, N. N.; Norazman, M. N.; Daud, N. M.; Yusof, M. A.; Yahya, M. A.; Othman, M.

2018-04-01

Green building technology and sustainability development is current focus in the world nowadays. In Malaysia and most tropical countries the maximum temperature recorded typically at 35°C. Air-conditioning system has become a necessity in occupied buildings, thereby increasing the cost of electric consumption. The aim of this study is to find out the solution in minimizing heat transfer from the external environment and intentions towards going green. In this study, the experimental work includes testing three types of concrete wall panels. The main heat intervention material in this research is 2 inch diameter Polyvinyl Chloride (PVC) pipe embedded at the center of the concrete wall panel, while the EPS foam beads were added to the cement content in the concrete mix forming the outer layer of the wall panel. Water from the rainwater harvesting system is regulated in the PVC pipe to intervene with the heat conductivity through the wall panel. Results from the experimental works show that the internal surface temperature of these heat resistance wall panels is to 3□C lower than control wall panel from plain interlocking bricks.

Degradation of polyvinyl chloride (PVC) / hydrolyzed collagen (HC) blends active sludge test.

Science.gov (United States)

Agafiţei, Gabriela-Elena; Pascu, Mihaela; Cazacu, Georgeta; Vasile, Cornelia

2008-01-01

Biodegradable polymers represent a solution for the environment protection: they decrease the landfill space, by declining the petrochemical sources, and offer also an alternative solution for the recycling. The behavior during degradation in the presence of active sludge of some polyvinyl chloride (PVC) based blends with variable content of hydrolyzed collagen (HC) has been followed. Some samples were subjected to UV irradiation, for 30 hours. The modifications induced in the environment by the polymer systems (pH variation, bacterial composition), as well as the changes of the properties of the blends (weight losses, aspect etc.) were studied. During the first moments of degradation in active sludge, all the samples absorbed water, behavior which favored the biodegradation. The bacteriological analysis of the sludge indicates the presence of some microbiological species. Generally, the populations of microorganisms decrease, excepting the sulphito-reducing anaerobic bacteria, the actinomycetes and other anaerobic bacteria. PVC/HC blends are degraded with a significant rate in active sewage sludge. More susceptible for the degradation are the UV irradiated blends. After the migration of the components with a small molecular mass in the environment, the natural polymer is degraded. The degradation effect increases with the content in the natural polymer.

Estudo do efeito da incorporação de plastificante de fonte renovável em compostos de PVC

Directory of Open Access Journals (Sweden)

Derval dos Santos Rosa

2013-01-01

Full Text Available O acúmulo de resíduos poliméricos tem crescido nos últimos anos e os subsolos dos lixões já estão saturados com resíduos plásticos. Isso possivelmente se deve à elevada produção de resíduos sólidos de plásticos (cerca de 25 mil t/dia em 2008, segundo a Lei de Resíduos. Em vista disso, este trabalho apresenta uma análise comparativa do estudo do potencial de (biodegradação de compostos de PVC utilizando um plastificante de origem vegetal renovável (PFR com estrutura de éster de milho com massa molar 296,5 g.mol- 1 e dois plastificantes sintéticos, ftalato de dioctila (DOP e adipato de dioctila (DOA, buscando inovar na obtenção de um composto de PVC com um plastificante de fonte renovável. Os resultados de FTIR evidenciaram maior interação do PFR com a resina de PVC para o teor de 30 phr, e para o teor de 40 phr observou-se que os plastificantes DOP e PFR apresentaram os mesmos valores de variação da banda atática. Já os ensaios mecânicos reforçaram os resultados de FTIR com maior compatibilidade para as composições contendo PFR. Uma maior estabilidade térmica no composto de PVC foi observada por TGA para a amostra contendo 40 phr de DOA, o que foi confirmado por RMN, e para a amostra com PFR nos teores de 30 e 40 phr. Por fim, uma perda significativa de massa foi observada nos ensaios de resistência à extração por solvente para os compostos contendo DOA, sendo que a amostra com 30 phr mostrou menor valor de extração. A biodegradação em solo simulado mostrou maior perda de massa para as amostras plastificadas com DOA (40phr e PFR (40phr. Isso indica que é viável usar plastificante de fonte renovável nos compostos de PVC, devido à compatibilidade deste com esta resina.

STUDY ON THE SYNTHESIS AND STRUCTURE OF MACRORETICULAR BEAD PAN/PVC IPN RESINS

Institute of Scientific and Technical Information of China (English)

LI Yanfeng; ZHUO Renxi

1993-01-01

Macroreticular bead PAN/PVC IPN reans with cyano and chloro groups were synthesized by interpenetrating polymerization of acrylonitrile, or acrylonitrile and divinylbenzene into a macroporous polyvinyl chloride bead. The composition and structure of the bead IPN resins have been investigated by means of FT-IR, NMR, SEM, mercury porosimetry and elemental analysis. During the process of interpenetrating polymerization, the chain propagation obeys Bernoullian statistical law, and no grafting polymerization has been observed. The content of cyano group in the resulting IPN resins can be adjusted by the amount of acrylonitrile added. The morphology of the IPN resins basically resembles that of the polyvinyl chloride bead,whereas the pore structures vary to a certain degree

Radiation crosslinking of highly plasticized PVC

Science.gov (United States)

Mendizabal, E.; Cruz, L.; Jasso, C. F.; Burillo, G.; Dakin, V. I.

1996-02-01

To improve the physical properties of highly plasticized PVC, the polymer was crosslinked by gamma irradiation using a dose rate of 91 kGy/h. The effect of plasticizer type was studied by using three different plasticizers, 2,2,4-trimethyl-1,3-pentanediol diisobutyrate (TXIB), di(2-ethyl hexyl) phthalate (DOP), and di(2-ethylhexyl terephthalate) (DOTP), and varying irradiation doses. Gel content was determined by soxhlet extraction, tensile measurements were made on a universal testing machine and the mechano-dynamic measurements were made in a dynamic rheometer. It was found that a considerable bonding of plasticizer molecules to macromolelcules takes place along with crosslinking, so that the use of the solvent extraction method for measuring the degree of crosslinking can give erroneous information. Radiation-chemical crosslinking yield ( Gc) and molecular weight of interjunctions chains ( Mc), were calculated for different systems studied. Addition of ethylene glycol dimethacrylate (EGDM) as a crosslinking coagent and dioctyl tin oxide (DOTO) as a stabilizer was also studied. Plasticizers extraction resistance was increased by irradiation treatment.

Radiation crosslinking of highly plasticized PVC

International Nuclear Information System (INIS)

Mendizabal, E.; Cruz, L.; Jasso, C.F.; Burillo, G.; Dakin, V.I.

1996-01-01

To improve the physical properties of highly plasticized PVC, the polymer was crosslinked by gamma irradiation using a dose rate of 91 kGy/h. The effect of plasticizer type was studied by using three different plasticizers, 2,2,4-trimethyl-1,3-pentanediol diisobutyrate (TXIB), di(2-ethyl hexyl) phthalate (DOP), and di(2-ethylhexyl terephthalate) (DOTP), and varying irradiation doses. Gel content was determined by soxhlet extraction, tensile measurements were made on a universal testing machine and the mechano-dynamic measurements were made in a dynamic rheometer. It was found that a considerable bonding of plasticizer molecules to macromolecules takes place along with crosslinking, so that the use of the solvent extraction method for measuring the degree of crosslinking can give erroneous information. Radiation-chemical crosslinking yield (G c ) and molecular weight of interjunctions chains (M c ), were calculated for different systems studied. Addition of ethylene glycol dimethyacrylate (EGDM) as a crosslinking coagent and dioctyl tin oxide (DOTO) as a stabilizer was also studied. Plasticizers extraction resistance was increased by irradiation treatment. (author)

Avaliação e caracterização de tubos fabricados com PVC reciclado

Directory of Open Access Journals (Sweden)

Luiz Carlos G. Pennafort Jr

2013-01-01

Full Text Available Neste trabalho foram caracterizados dois polímeros utilizados na fabricação de tubos de PVC, tendo como diferencial o uso de resina de policloreto de vinila virgem e reciclada. O uso da resina reciclada, derivada do reprocessamento de resíduos aterrados (sanitários ou industriais, foi avaliado com o objetivo de compará-la a produtos fabricados com resina virgem, os quais foram submetidos aos ensaios de Fluorescência de Raios X (FRX, Difração de Raios X (DRX e resistência à tração e alongamento. Os resultados demonstraram que houve alteração estatisticamente significativa, conforme ANOVA (5%, nas características mecânicas do produto final, tendo os tubos fabricados com PVC reciclado apresentado uma resistência mecânica menor que os fabricados com resina virgem, além da presença de metais pesados como Pb (chumbo e Cd (cádmio.

Some complementary results to the granularity of industrial X-ray films

International Nuclear Information System (INIS)

Stade, J.

1987-01-01

The granularity of industrial x-ray films was examined by measurements of the Wiener spectra. The dependence of the Weiner spectra on film density, type of film, type of developer, energy of the exposing x-radiation, and light exposure, was also investigated. The results revealed that the Weiner spectrum or related quantities were suitable as a tool for measuring the influence of different radiographic parameters on the x-ray film, as well as to characterize its properties. (UK)

Phase separation and rubber phase dispersion in PVC/NBR blends

OpenAIRE

Passador, Fábio R.; Pessan, Luiz A.; Rodolfo Jr., Antonio

2006-01-01

Termoplásticos modificados com elastômeros têm despertado grande interesse de pesquisadores e de indústrias devido à atraente relação custo/benefício e a possibilidade de aumento significativo da tenacidade sob impacto de polímeros frágeis com a incorporação de uma fase borrachosa dispersa. Este artigo mostra a relação entre o estado de mistura e a dispersão da fase borrachosa em blendas de poli (cloreto de vinila) (PVC) com borracha nitrílica (NBR). O estado de mistura de blendas poliméricas...

Effect of Low-Pressure Nitrogen DC Plasma Treatment on the Surface Properties of Biaxially Oriented Polypropylene, Poly (Methyl Methacrylate) and Polyvinyl Chloride Films

International Nuclear Information System (INIS)

Mortazavi, S. Hamideh; Ghoranneviss, Mahmood; Pilehvar, Soheil; Esmaeili, Sina; Zargham, Shamim; Hashemi, S. Ebrahim; Jodat, Hamzeh

2013-01-01

In this study, commercial biaxially oriented polypropylene (BOPP), polyvinyl chloride (PVC) and poly (methyl methacrylate) (PMMA) films were treated with nitrogen plasma over different exposure times in a Pyrex tube surrounded by a DC variable magnetic field. The chemical changes that appeared on the surface of the samples were investigated using Fourier transform infrared (FT-IR) spectroscopy and attenuated total reflectance Fourier transform infrared (ATR-FTIR) spectroscopy after treatment for 2 min, 4 min and 6 min in a nitrogen plasma chamber. Effects of the plasma treatment on the surface topographies and contact angles of the untreated and plasma treated films were also analyzed by atomic force microscopy (AFM) and a contact angle measuring system. The results show that the plasma treated films become more hydrophilic with an enhanced wettability due to the formation of some new polar groups on the surface of the treated films. Moreover, at higher exposure times, the total surface energy in all treated films increased while a reduction in contact angle occurred. The behavior of surface roughness in each sample was completely different at higher exposure times. (plasma technology)

Evaluation of the Standard Ion Transfer Potentials for PVC Plasticized Membranes from Voltammetric Measurements

Czech Academy of Sciences Publication Activity Database

Langmaier, Jan; Stejskalová, Květoslava; Samec, Zdeněk

2001-01-01

Roč. 496, č. 1 (2001), s. 143-147 ISSN 0022-0728. [Symposium in Kyoto. Kyoto, 02.03.2000] R&D Projects: GA AV ČR IAA4040902 Institutional research plan: CEZ:AV0Z4040901 Keywords : ion voltammetry * PVC plasticized membrane * standard ion transfer potential Subject RIV: CG - Electrochemistry Impact factor: 1.960, year: 2001

Materials-Product chains. Theory and an application to zinc and PVC gutters

Energy Technology Data Exchange (ETDEWEB)

Kandelaars, P.; Van den Bergh, J. [Tinbergen Inst., Rotterdam (Netherlands)

1995-12-31

A framework is presented for the analysis of economic and environmental impacts of policies applied to materials-product (MP) chains. This is based on material flows, product flows, costs, prices and optimal management of an MP chain. The main difference with other studies focusing on materials flows is that in this study the link between products of services and materials is explicitly dealt with. The framework is developed on the basis of materials balance conditions, production functions allowing for substitution, and recycling of both materials and products. After presenting theoretical MP chain-models and analytical results, an application to the problem of choosing between zinc and PVC gutters is discussed. Here optimal MP chain management decisions are presented for various policy and strategy scenarios. 3 figs., 5 tabs., 12 refs., 3 appendices

Sifat fisika dan analisis gugus fungsi karet seal o-ring dari bahan termoplastik elastomer nitrile butadiene rubber (NBR dan polyvinyl chloride (PVC

Directory of Open Access Journals (Sweden)

Arum Yuniari

2013-06-01

Full Text Available The purpose of this research was to determine the physical properties and functional groups on O-ring rubber seals made of thermoplastic elastomers blend NBR and PVC. Composition of the NBR / PVC were successively varied : 90/10; 85/15; 80/20; 75/25; 70/30 and 65/35 phr. Mixing process between NBR/PVC with additive used a two roll mill within a temperature of 60º - 80 ºC, the vulcanization process used a hydraulic press at a temperature of 170 oC and pressure of 150 kg/cm2. The physical properties were evaluated including tensile strength, elongation at break, hardness, before and after aging, hardness after immersion in isooctane and swelling while analysis of functional groups was also carried out by method of Fourier Transform Infrared Spectrophotometer (FTIR. The result of the best vulcanized was characterized by tensile strength 188.93 kg/cm2, the change of tensile strength after aging 2.50%, elongation at break of 400%, the change of elongation at break after aging was 12.5%, hardness 75 shore A, the change of hardness after aging 0%, the change of hardness after immersion in isooctane 1.3%, swelling 0.8% and functional group of vulcanisate was indicated by new peak (OH at wave band of 3468 cm-1. Those formula met the requirements of the technical specifications of ASTM D 2000 seal O-ring.

Studies in cross-linking PVC footwear soling compounds using gamma-irradiation

International Nuclear Information System (INIS)

Bloom, L.I.

1983-01-01

Irradiation cross-linking of polymeric materials has been known for some time but it is only in recent years that it has been put to commercial advantage. Well known uses are the modification of PVC for high temperature applications such as under-bonnet wiring, stove wiring, post office telecommunication wire and shrink tubing. In South Africa interest in developing commercial applications for cross-linkable polymeric materials was initially stimulated through the work of the Atomic Energy Board at Pelindaba in late 1971 using a cobalt - 60 gamma radiation unit

COMPARISON OF RESULTS OF THERMAL TESTS OF BALCONY DOORS

Directory of Open Access Journals (Sweden)

Golubev Stanislav Sergeevich

2012-10-01

Full Text Available Results of thermal tests of balcony doors are presented in the article. In the course of the research project, two types of doors were tested. The first type represents a PVC frame door (width 82 mm; it has a triple glazing (4K-16Ar-4-16Ar-K4; its blank part represents a polystyrene sandwich panel (width 40 mm. The second type represents a PVC frame door (width 82 mm, that has a triple glazing (4K-16Ar-4-16Ar-K4 and composite PVC panels. The testing procedure and processing results are described in the article. The test has demonstrated that the thermal resistance value of the balcony door of the first type exceeds the thermal resistance value of the balcony door of the second type.

INDIVIDUAL PACKAGING OF MANGOS CV. TOMMY ATKINS IN PLASTIC FILM: EFFECT ON SHELF LIFE

OpenAIRE

YAMASHITA, FÁBIO; TONZAR, ANAMARIA CALDO; FERNANDES, JOICELENA GEORGETTI; MORIYA, SUELY; BENASSI, MARTA DE TOLEDO

2001-01-01

Estudou-se o efeito da embalagem de policloreto de vinila (PVC) sobre a vida de prateleira de mangas cv. Tommy Atkins armazenadas sob refrigeração. Mangas no estádio de maturidade fisiológica, com casca verde ou levemente avermelhada, foram embaladas individualmente, com filme de 10mm de espessura, e armazenadas por 28 dias a 12ºC (80-90% UR). Frutos sem embalagem serviram de controle. Durante o período de armazenagem, foram feitas avaliações sensoriais utilizando o método de escala hedônica ...

Pyrolysis studies of PP/PE/PS/PVC/HIPS-Br plastics mixed with PET and dehalogenation (Br, Cl) of the liquid products

Energy Technology Data Exchange (ETDEWEB)

Bhaskar, Thallada; Kaneko, Jun; Muto, Akinori; Sakata, Yusaku [Department of Applied Chemistry, Faculty of Engineering, Okayama University, 3-1-1 Tsushima Naka, 700-8530 Okayama (Japan); Jakab, Emma [Research Laboratory of Materials and Environmental Chemistry, Chemical Research Center, Hungarian Academy of Sciences, P.O. Box 17, H-1525 Budapest (Hungary); Matsui, Toshiki [Toda Kogyo Co. Ltd., Hiroshima 739-0652 (Japan); Uddin, Md. Azhar [Process Safety and Environment Protection Group, School of Engineering, The University of Newcastle, Callaghan, NSW 2308 (Australia)

2004-08-01

Pyrolysis of polypropylene (PP)/polyethylene (PE)/polystyrene (PS)/poly(vinyl chloride) (PVC)/high impact polystyrene with brominated flame retardant (HIPS-Br) plastics mixed with poly(ethylene terephthalate) (PET) was performed at 430C under atmospheric pressure using a semi-batch operation. The presence of PET in the pyrolysis mixture of PP/PE/PS/PVC/HIPS-Br affected significantly the formation of decomposition products and the decomposition behavior of the plastic mixture. We observed the following effects of PET on the pyrolysis of PP/PE/PS/PVC/HIPS-Br mixed plastics: (1) the yield of liquid product decreased and the formation of gaseous products increased; (2) a waxy residue was formed in addition to the solid carbon residue; (3) the formation of SbBr{sub 3} was not detected in liquid products; (4) the yield of chlorinated branched alkanes increased as well as vinyl bromide and ethyl bromide were formed. The use of calcium carbonate carbon composite (Ca-C) completely removed the chlorine and bromine content from the liquid products during PP/PE/PS/PVC/HIPS-Br pyrolysis, however in the presence of PET, the catalytic experiment (Ca-C, 8g) yielded liquid products containing 310ppm of Br and 20ppm of Cl. In addition, the Ca-C increased the yield of liquid products about 3-6wt.%, as well as enhanced the gaseous product evolution and decreased the yield of residue. The halogen free liquid hydrocarbons can be used as a feedstock in a refinery or as a fuel.

Comparison of gamma knife validation film's analysis results of different film dose analysis software

International Nuclear Information System (INIS)

Cheng Xiaojun; Zhang Conghua; Liu Han; Dai Fuyou; Hu Chuanpeng; Liu Cheng; Yao Zhongfu

2011-01-01

Objective: To compare the analytical result of different kinds of film dose analysis software for the same gamma knife, analyze the reasons of difference caused, and explore the measurements and means for quality control and quality assurance during testing gamma knife and analyzing its result. Methods: To test the Moon Deity gamma knife with Kodak EDR2 film and γ-Star gamma knife with GAFCHROMIC® EBT film, respectively. All the validation films are scanned to proper imagine format for dose analysis software by EPSON PERFECTION V750 PRO scanner. Then imagines of Moon Deity gamma knife are analyzed with Robot Knife Adjuvant 1.09 and Fas-09 1.0, and imagines of γ-Star gamma knife with Fas-09 and MATLAB 7.0. Results: There is no significant difference in the maximum deviation of radiation field size (Full Width at Half Maximum, FWHM) and its nominal value between Robot Knife Adjuvant and Fas-09 for Moon Deity gamma knife (t=-2.133, P>0.05). The analysis on the radiation field's penumbra region width of collimators which have different sizes indicated that the differences are significant (t=-8.154, P<0.05). There is no significant difference in the maximum deviation of FWHM and its nominal value between Fas-09 and MATLAB for γ-Star gamma knife (t=-1.384, P>0.05). However, following national standards,analysis of φ4 mm width of collimators can obtain different results according to the two kinds software, and the result of Fas-09 is not qualified while MATLAB is qualified. The analysis on the radiation field's penumbra region width of collimators which have different sizes indicates that the differences are significant (t=3.074, P<0.05). The imagines are processed with Fas-09. The analysis of imagine in the pre-and the post-processing indicates that there is no significant difference in the maximum deviation of FWHM and its nominal value (t=0.647, P>0.05), and the analytical result of the radiation field's penumbra region width indicates that there is

Migration of plasticisers from PVC and other polymers

DEFF Research Database (Denmark)

Lundsgaard, Rasmus

). In this work it is shown how diffusion coefficients can be obtained by regression of experimental migration data plotted as the square root of time. This was done from plasticiser migration data of GRINDSTEDr SOFT-N-SAFE, GRINDSTEDr ACETEM 95 CO (Acetem) and Epoxidised Soybean Oil (ESBO) migrating from......The main purpose of this thesis is to investigate, from a modeling point of view, the migration of GRINDSTEDr SOFT-N-SAFE (SNS) and other plasticisers from polyvinyl chloride (PVC) and polyolefin food package materials and into foodstuff (specifically the four food simulants set by EU legislation...... coefficients at 20◦C, except at higher temperatures. Using the finite element mesh method in Matlab and COMSOL environments the migration was modeled with a diffusion coefficient able to change with local plasticiser concentration. Three different models for this plasticiser concentration dependence...

Processing of nanocomposites EVA/PVC/MMT in twin-screw extruder; Processamento de nanocompositos EVA/PVC/MMT em extrusora dupla rosca

Energy Technology Data Exchange (ETDEWEB)

Gehlen, A.; Barbutti Filho, W.R.; Francisquetti, E.L.; Andrade, M.Z.; Zattera, A.J., E-mail: ajzatter@ucs.b [Universidade de Caxias do Sul (UCS), RS (Brazil). Lab. de Polimeros

2010-07-01

Polymeric nanocomposites have some superior properties when compared to conventional polymer composites and is one of the most promising fields in the nanotechnology research. In a EVA (ethylene vinyl acetate) /PVC (poly vinyl chloride) matrix was incorporated different types of montmorillonite clays (an inorganic (Na{sup +}) and two organic modified (15A and 30B nanoclays). The mixtures were processed in a co-rotating twin-screw extruder at processing speeds of 200 and 400 rpm. Thermogravimetric analysis (TGA) shown that the inorganic and organic modified clays promoted a shift to higher temperatures in the degradation temperature., X-ray diffraction (XRD) and transmission electronic microscopy (TEM) shows a possible intercalation with the 15A clay, exfoliation with the 30B clay and formation of clusters in the Na{sup +} clay. For all clays studied, the increase in shear rate does not promote significant changes. (author)

Migration of DEHP and DINP into dust from PVC flooring products at different surface temperature.

Science.gov (United States)

Jeon, Seunghwan; Kim, Ki-Tae; Choi, Kyungho

2016-03-15

Phthalates are important endocrine disrupting chemicals that have been linked to various adverse human health effects. Phthalates are ubiquitously present in indoor environment and could enter humans. Vinyl or PVC floorings have been recognized as one of important sources of phthalate release to indoor environment including house dust. In the present study, we estimated the migration of di(2-ethylhexyl)phthalate (DEHP) and di-isononyl phthalate (DINP) from the flooring materials into the dust under different heating conditions. For this purpose, a small chamber specifically designed for the present study and a Field and Laboratory Emission Cell (FLEC) were used, and four major types of PVC flooring samples including two UV curing paint coated, an uncoated residential, and a wax-coated commercial type were tested. Migration of DEHP was observed for an uncoated residential type and a wax-coated commercial type flooring. After 14 days of incubation, the levels of DEHP in the dust sample was determined at room temperature on average (standard deviation) at 384 ± 19 and 481 ± 53 μg/g, respectively. In contrast, migration of DINP was not observed. The migration of DEHP was strongly influenced by surface characteristics such as UV curing coating. In the residential flooring coated with UV curing paint, migration of DEHP was not observed at room temperature. But under the heated condition, the release of DEHP was observed in the dust in the FLEC. Migration of DEHP from flooring materials increased when the flooring was heated (50 °C). In Korea, heated flooring system, or 'ondol', is very common mode of heating in residential setting, therefore the contribution of PVC flooring to the total indoor DEHP exposure among general population is expected to be greater especially during winter season when the floor is heated. Copyright © 2015 Elsevier B.V. All rights reserved.

Bulletin of Materials Science | Indian Academy of Sciences

Indian Academy of Sciences (India)

... various properties. The controlled uniaxial stretching of films close to the softening temperature of PVC has resulted in enhancement in the degree of crystallinity in the nanocomposites. This improvement in the structural order has also imparted increase in tensile strength and Young's modulus of the nanocomposite films.

Processos de proteção dos garfos na enxertia da mangueira

Directory of Open Access Journals (Sweden)

Jacomino Angelo Pedro

2000-01-01

Full Text Available Diferentes processos de proteção dos garfos foram pesquisados na produção de mudas por enxertia, da mangueira ?Tommy Atkins?. Os tratamentos utilizados foram os seguintes: saquinho de polietileno (testemunha, filme de PVC, parafilme, cera de abelha, parafina e parafina + vaselina. Verificou-se que o filme de PVC e o parafilme proporcionaram pegamentos de enxertia semelhantes à testemunha (40,60%, 56,62% e 48,33%, respectivamente, enquanto que para os demais tratamentos, os percentuais de pegamento foram muito baixos (< 10%. Conclui-se que o filme de PVC e o parafilme podem ser empregados como opção aos saquinhos plásticos, na proteção dos garfos da mangueira, no procedimento da enxertia.

Organophosphorus pesticide exposure in agriculture: effects of temperature, ultraviolet light and abrasion on PVC gloves

Science.gov (United States)

ISMAIL, Ismaniza; GASKIN, Sharyn; PISANIELLO, Dino; EDWARDS, John W.

2017-01-01

Elbow length PVC gloves are often recommended for protection against organophosphorus pesticide (OP) exposure in agriculture. However, performance may be reduced due to high temperature, UV exposure and abrasion. We sought to assess these impacts for two OPs under normal use and reasonable worst-case scenarios. Glove permeation tests were conducted using ASTM cells with two PVC glove brands at 23°C and 45°C for up to 8 h. Technical grade dichlorvos and formulated diazinon were used undiluted and at application strength. Breakthough of undiluted dichlorvos occurred at both 23°C and 45°C, but only at 45°C for application strength. Breakthrough of diazinon was not achieved, except when undiluted at 45°C. UV-exposed and abraded gloves showed reduced performance, with the effect being approximately two-fold for dichlorvos. Only small differences were noted between glove brands. Extra precautions should be taken when handling concentrated OPs at high temperature, or when using abraded or sunlight-exposed gloves. PMID:29199264

Flow behavior of polymers during the roll-to-roll hot embossing process

International Nuclear Information System (INIS)

Deng, Yujun; Yi, Peiyun; Peng, Linfa; Lai, Xinmin; Lin, Zhongqin

2015-01-01

The roll-to-roll (R2R) hot embossing process is a recent advancement in the micro hot embossing process and is capable of continuously fabricating micro/nano-structures on polymers, with a high efficiency and a high throughput. However, the fast forming of the R2R hot embossing process limits the time for material flow and results in complicated flow behavior in the polymers. This study presents a fundamental investigation into the flow behavior of polymers and aims towards the comprehensive understanding of the R2R hot embossing process. A three-dimensional (3D) finite element (FE) model based on the viscoelastic model of polymers is established and validated for the fabrication of micro-pyramids using the R2R hot embossing process. The deformation and recovery of micro-pyramids on poly(vinyl chloride) (PVC) film are analyzed in the filling stage and the demolding stage, respectively. Firstly, in the analysis of the filling stage, the temperature distribution on the PVC film is discussed. A large temperature gradient is observed along the thickness direction of the PVC film and the temperature of the top surface is found to be higher than that of the bottom surface, due to the poor thermal conductivity of PVC. In addition, creep strains are demonstrated to depend highly on the temperature and are also observed to concentrate on the top layer of the PVC film because of high local temperature. In the demolding stage, the recovery of the embossed micro-pyramids is obvious. The cooling process is shown to be efficient for the reduction of recovery, especially when the mold temperature is high. In conclusion, this research advances the understanding of the flow behavior of polymers in the R2R hot embossing process and might help in the development of the highly accurate and highly efficient fabrication of microstructures on polymers. (paper)

Phthalates in soft PVC products used in food production equipment and in other food contact materials on the Danish and the Nordic Market 2013-2014

DEFF Research Database (Denmark)

Petersen, Jens Højslev; Jensen, Lisbeth Krüger

2016-01-01

they were well-known endocrine disruptors. Results of the Danish Food Authorities control in 2008 and 2009 showed 23 % non-compliant samples. Critical FCMs turned out to be those made from plasticised PVC and sold as suitable for contact with fatty foodstuffs. Targeted follow up control campaigns were...

SELECTED PHYSICAL PROPERTIES OF EXTRUDED COMPOSITES TYPE OF POROUS PVC-METAL

Directory of Open Access Journals (Sweden)

Aneta Tor-Świątek

2014-09-01

Full Text Available The article presents studies of selected physical and mechanical properties of hybrid materials type of polymer-metal. In the frame of this work modification of PVC with the iron and copper powder in amount of 0, 1.5 and 3% and blowing agent in amount of 0, 0.5, 1% was done. Extrudates in a form of pipe were tested to determine density, porosity, maximum tensile stress, stress at break, modulus of elasticity and elongation with break. The samples were also observed in a microscope. The studies have shown significant influence of the added components on the properties tested.

PVC-based synthetic leather to provide more comfortable and sustainable vehicles

Science.gov (United States)

Maia, I.; Santos, J.; Abreu, MJ; Miranda, T.; Carneiro, N.; Soares, GMB

2017-10-01

Consumers are increasingly demanding the interior of cars to be comfortable even in the case of more economic commercial segments. Thus, the development of materials with thermoregulation properties has assumed renewed interest for these particular applications. An attempt has been made to prepare a multilayer PVC-based synthetic leather with paraffinic PCMs to be applied on a car seat. The thermal behaviour of the material was analysed using Alambeta apparatus, a thermo-camera and a thermal manikin. The results obtained show that the synthetic leather with incorporated PCMs gives cooler feeling and has higher reaction times regarding environmental temperature variations than the material without PCMs incorporation. Globally, the new designed material allowed greater thermal comfort to the cars´ inhabitants. In addition, the material quality was evaluated according to the standard of the customer, BMW 9,210,275; Edition / Version 4, 2010-10-01 revealing that the material meets all the requirements under test, except for the performance in terms of flexibility.

Reduced adhesion of Staphylococcus aureus to ZnO/PVC nanocomposites

Directory of Open Access Journals (Sweden)

Geilich BM

2013-03-01

Full Text Available Benjamin M Geilich,1 Thomas J Webster21Program in Bioengineering, 2Department of Chemical Engineering, College of Engineering, Northeastern University, Boston, MA, USAAbstract: In hospitals and clinics worldwide, medical device surfaces have become a rapidly growing source of nosocomial infections. In particular, patients requiring mechanical ventilation (and, thus, intubation with an endotracheal tube for extended lengths of time are faced with a high probability of contracting ventilator-associated pneumonia. Once inserted into the body, the endotracheal tube provides a surface to which bacteria can adhere and form a biofilm (a robust, sticky matrix that provides protection against the host immune system and antibiotic treatment. Adding to the severity of this problem is the spread of bacterial genetic tolerance to antibiotics, in part demonstrated by the recent and significant increase in the prevalence of methicillin-resistant Staphylococcus aureus. To combat these trends, different techniques in biomaterial design must be explored. Recent research has shown that nanomaterials (materials with at least one dimension less than 100 nm may have the potential to prevent or disrupt bacterial processes that lead to infections. In this study, polyvinyl chloride (PVC taken from a conventional endotracheal tube was embedded with varying concentrations of zinc oxide (ZnO nanoparticles. S. aureus biofilms were then grown on these nanocomposite surfaces during a 24-hour culture. Following this, biofilms were removed from the surfaces and the number of colony forming units present was assessed. Bacterial proliferation on the samples embedded with the highest concentration of ZnO nanoparticles was 87% less when compared to the control, indicating that this technique is effective at reducing biofilm formation on PVC surfaces without the use of antibiotics.Keywords: nanomaterials, endotracheal tube, biofilm, zinc oxide, nanoparticles, Staphylococcus aureus

Reaction of tomato [Lycopersicon esculentum], cucumber [Cucumis sativus] and eggplant [Solanum melongena] cultured under the film altered the ratio of red and far-red photon flux

International Nuclear Information System (INIS)

Hotta, Y.; Hayashi, G.

1998-01-01

The effects of covering films which altered the ratio of red (R 600-700nm) and far-red (FR 700-800nm) photon flux to control succulent growth of seedlings on character of tomato, cucumber and eggplant seedlings Were determined. Also the effects on growth and yield of eggplant cultured in plastic greenhouse covered with the same films were investigated. The results were as follows: 1) The stem length of tomato, cucumber and eggplant seedlings cultured under the high R/FR ratio (2.28) film which intercepted far-red photon flux in the greenhouse got shorter than for cheesecloth (1.00) which had sane level of photosynthetic photon flux transmittance, especially evident on eggplant. There was no difference in the number of leaves on these seedlings between tested film and the cheesecloth, but the top and root dry weight of these seedlings cultured under tested film got lighter than the one using cheesecloth. The leaves got smaller in eggplant too. 2) The stem of eggplant cultured under the high R/FR ratio (2.28) film got shorter and thicker than the control PVC film; but there was no difference on the yield. But eggplant cultured under the low R/FR ratio (0.66) film which intercepted red photon flux grew similarly as control, but its yield decreased

Thermal degradation and plasticizing mechanism of poly(vinyl chloride) plasticized with a novel cardanol derived plasticizer

Science.gov (United States)

Chen, J.; Nie, X. A.; Jiang, J. C.; Zhou, Y. H.

2018-01-01

A natural plasticizer cardanol derivatives glycidyl ether (CGE) was synthesized and employed as a plasticizer for the poly(vinyl chloride). The effect of CGE on thermal degradation of PVC films and its plasticizing mechanism were firstly reported. The molecular structure of CGE was characterized with Fourier transform infrared spectroscopy (FTIR). Thermal properties, degradation properties and compatibility of the PVC films were investigated by Differential scanning calorimeter analysis (DSC), Thermogravimetric analysis (TGA) and FTIR, respectively. Compared with the commercial plasticizers dioctylphthalate (DOP), CGE can endow PVC film with a decrease of 4.31 °C in glass transition temperature (Tg), an increase of 24.01 °C and 25.53 °C in 10% weight loss (T 10) and 50% weight loss (T 50) respectively, and a higher activetion energy of thermal degradation (Ea ).

Validation of formability of laminated sheet metal for deep drawing process using GTN damage model

Energy Technology Data Exchange (ETDEWEB)

Lim, Yongbin; Cha, Wan-gi; Kim, Naksoo [Department of Mechanical Engineering, Sogang University, 1 Sinsu-dong, Mapo-gu, Seoul, 121-742 (Korea, Republic of); Ko, Sangjin [Mold/die and forming technology team, Product prestige research lab, LG electronics, 222, LG-ro, Jinwi-myeon, Pyeongtaek-si, Gyeonggi-do, 451-713 (Korea, Republic of)

2013-12-16

In this study, we studied formability of PET/PVC laminated sheet metal which named VCM (Vinyl Coated Metal). VCM offers various patterns and good-looking metal steel used for appliances such as refrigerator and washing machine. But, this sheet has problems which are crack and peeling of film when the material is formed by deep drawing process. To predict the problems, we used finite element method and GTN (Gurson-Tvergaard-Needleman) damage model to represent damage of material. We divided the VCM into 3 layers (PET film, adhesive and steel added PVC) in finite element analysis model to express the crack and peeling phenomenon. The material properties of each layer are determined by reverse engineering based on tensile test result. Furthermore, we performed the simple rectangular deep drawing and simulated it. The simulation result shows good agreement with drawing experiment result in position, punch stroke of crack occurrence. Also, we studied the fracture mechanism of PET film on VCM by comparing the width direction strain of metal and PET film.

Electron Beam Damage in Poly(Vinyl Chloride) and Poly(Acrylonitrile) as Observed by Auger Electron Spectroscopy

International Nuclear Information System (INIS)

Lea, Alan S.; Engelhard, Mark H.; Baer, Donald R.

2003-01-01

AES spectra of spun-cast films of poly(vinyl chloride) (PVC) and poly(acrylonitrile) (PAN) were collected over a period of time to determine specimen damage during exposure to a 10kV electron beam. For the PVC, loss of chlorine was observed over a period of 203 minutes to the extent that the final chlorine concentration was only 20% of its original value. PAN exhibited a loss in nitrogen content over a period of 120 minutes, but the rate of damage to the polymer was significantly less than PVC. Figure 1 shows the atomic concentration in the PVC film as a function of dose (time). It takes a dose of approximately 7.0x10-5 Ccm-5 for the chlorine concentration to fall from its original value by 10% (one definition of critical dose). Figure 2 shows a similar drop in nitrogen concentration in the PAN film as a function of dose. For this polymer, it takes a dose of 1.3x10-3 Ccm-2 for the nitrogen concentration to fall by 10%

Microwave irradiation induced modifications on the interfaces in SAN/EVA/PVC and PVAc/BPA/PVP ternary polymer blends: Positron lifetime study

International Nuclear Information System (INIS)

Dinesh, Meghala; Chikkakuntappa, Ranganathaiah

2013-01-01

Ternary polymer blends of poly(styrene-co-acrylonitrile)/poly(ethylene-co-vinylacetate)/poly(vinyl chloride) (SAN/EVA/PVC) and poly(vinyl acetate)/bisphenol A/polyvinylpyrrolidone (PVAc/BPA/PVP) with different compositions have been prepared by solvent casting method and characterized by positron lifetime spectroscopy and differential scanning calorimetry DSC. Phase modifications have been induced by irradiating the blends with microwave radiation. These changes have been monitored by measuring the free-volume content in the blends. The results clearly show improved interactions between the constituent polymers of the blends upon microwave irradiation. However, the free-volume data and DSC measurements are found to be inadequate to reveal the changes at the interfaces and the interfaces determine the final properties of the blend. For this we have used hydrodynamic interaction (α ij ) approach developed by us to measure strength of hydrodynamic interaction at the interfaces. These results show that microwave irradiation stabilizes the interfaces if the blend contains strong polar groups. SAN/EVA/PVC blend shows an increased effective hydrodynamic interaction from −3.18 to −4.85 at composition 50/35/15 upon microwave irradiation and PVAc/BPA/PVP blend shows an increased effective hydrodynamic interaction from −3.81 to −7.57 at composition 20/50/30 after irradiation

Microwave irradiation induced modifications on the interfaces in SAN/EVA/PVC and PVAc/BPA/PVP ternary polymer blends: Positron lifetime study

Energy Technology Data Exchange (ETDEWEB)

Dinesh, Meghala; Chikkakuntappa, Ranganathaiah, E-mail: crang1@rediffmail.com

2013-09-01

Ternary polymer blends of poly(styrene-co-acrylonitrile)/poly(ethylene-co-vinylacetate)/poly(vinyl chloride) (SAN/EVA/PVC) and poly(vinyl acetate)/bisphenol A/polyvinylpyrrolidone (PVAc/BPA/PVP) with different compositions have been prepared by solvent casting method and characterized by positron lifetime spectroscopy and differential scanning calorimetry DSC. Phase modifications have been induced by irradiating the blends with microwave radiation. These changes have been monitored by measuring the free-volume content in the blends. The results clearly show improved interactions between the constituent polymers of the blends upon microwave irradiation. However, the free-volume data and DSC measurements are found to be inadequate to reveal the changes at the interfaces and the interfaces determine the final properties of the blend. For this we have used hydrodynamic interaction (α{sub ij}) approach developed by us to measure strength of hydrodynamic interaction at the interfaces. These results show that microwave irradiation stabilizes the interfaces if the blend contains strong polar groups. SAN/EVA/PVC blend shows an increased effective hydrodynamic interaction from −3.18 to −4.85 at composition 50/35/15 upon microwave irradiation and PVAc/BPA/PVP blend shows an increased effective hydrodynamic interaction from −3.81 to −7.57 at composition 20/50/30 after irradiation.

The influence of temperature on the emission of volatile organic compounds from PVC flooring, carpet, and paint

NARCIS (Netherlands)

Wal, J.F. van der; Hoogeveen, A.W.; Wouda, P.

1997-01-01

The influence of temperature on the emission rate of volatile organic compounds (VOC) from four indoor materials was investigated in a small dynamic test chamber. The materials investigated were two carpets, a PVC flooring and a paint; the temperature range investigated was 23-50°C. The general

Nanocomposite materials based on poly(vinyl chloride) and bovine serum albumin modified ZnO through ultrasonic irradiation as a green technique: Optical, thermal, mechanical and morphological properties.

Science.gov (United States)

Mallakpour, Shadpour; Darvishzadeh, Marzieh

2018-03-01

In this project, physicochemical properties of poly(vinyl chloride) (PVC) reinforced by ZnO nanoparticles (NPs) were studied. Firstly, ZnO NPs were modified with bovine serum albumin (BSA) as an organo-modifier and biocompatible substance through ultrasound irradiation as environmental friendly, low cost and rapid means. Nanocomposite (NC) films were prepared by loadings of various ratios of ZnO/BSA NPs (3, 6 and 9wt%) inside the PVC. Structural morphology and physical properties of the ZnO-BSA NPs and NC films were investigated via Fourier transform infrared spectroscopy, X-ray diffraction, thermogravimetric analysis (TGA), transmission electron microscopy and field emission scanning electron microscopy. According to the obtained information from the TGA, an increase in the thermal stability can be clearly observed. Also the results of contact angle analysis indicated with increasing percent of ZnO/BSA NPs into PVC the hydrophilic behaviors of NCs were increased. Copyright © 2017 Elsevier B.V. All rights reserved.

Lignin peroxidase isoenzyme: a novel approach to biodegrade the toxic synthetic polymer waste.

Science.gov (United States)

Khatoon, Nazia; Jamal, Asif; Ali, Muhammad Ishtiaq

2018-01-05

Fungal metabolites are playing an immense role in developing various sustainable waste treatment processes. The present study aimed at production and characterization of fungal lignin peroxidase (EC 1.11.1.14) with a potential to degrade Polyvinyl Chloride. Optimization studies revealed that the maximum enzyme production occurred at a temperature 25°C, pH 5 in the 4th week of the incubation period with fungal strain. Enzyme assay was performed to find out the dominating enzyme in the culture broth. The molecular weight of the enzyme was found to be 46 kDa. Partially purified lignin peroxidase from Phanerocheate chrysosporium was used for the degradation of PVC films. A significant reduction in the weight of PVC film was observed (31%) in shake flask experiment. FTIR spectra of the enzyme-treated plastic film revealed structural changes in the chemical composition, indicating a specific peak at 2943 cm -1 that corresponded to alkenyl C-H stretch. Moreover, deterioration on the surface of PVC films was confirmed by Scanning Electron Microscopy tracked through activity assay for the lignin peroxidase. Extracellular lignin peroxidases from P. chrysosporium play a significant role in the degradation of complex polymeric compounds like PVC.

Study of the use of plasticizer from renewable sources in PVC compositions

OpenAIRE

Madaleno, Emerson; Rosa, Derval dos S.; Zawadzki, Sonia F.; Pedrozo, Tiago H.; Ramos, Luiz P.

2009-01-01

Polímeros sintéticos são largamente utilizados em diversos produtos devido às suas propriedades físicas, químicas e facilidade de transformação. O poli(cloreto de vinila), conhecido como PVC, é um dos polímeros mais versáteis desenvolvidos pelo homem, de grande utilidade para a sociedade moderna. Suas aplicações incluem: janelas, calhas de chuva, revestimentos de paredes, portas, papel de parede, mangueiras, brinquedos, calçados, bolsas de sangue e tubos para condução de água. Em todas estas ...

Study of an X-ray fluorescence thin film method for the determination of uranium in low activity solutions

International Nuclear Information System (INIS)

Diaz-Guerra, J. P.

1980-01-01

The application of the X-ray fluorescence thin film technique to the uranium determination in nitric solutions for a concentration range from 1 g/l to 100 g/l and activity levels under 5 mCi/ml is studied. The most suited excitation and measurement conditions are also studied and the uranium matrix effect correction, which is performed through the double dilution, α U U interaction coefficient calculation and internal standard methods, is discussed. The specimen preparation is satisfactorily accomplished by using P.V.C. filters fixed on aluminium supports. (Author) 18 refs

Blendas PVC/NBR por processamento reativo II: caracterização físico-mecânica e morfológica PVC/NBR blends by reactive processing II: physical-mechanical and morphological characterization

Directory of Open Access Journals (Sweden)

Fábio R. Passador

2008-06-01

Full Text Available Vulcanização dinâmica é o processo de vulcanização de um elastômero durante a mistura no estado fundido com um termoplástico. Por este processo, o elastômero adquire resistência mecânica através do aumento do módulo de elasticidade, dureza, resistência à fadiga e abrasão. Neste trabalho, buscou-se avaliar as propriedades físico-mecânicas e as características morfológicas de blendas poliméricas constituídas de Poli(cloreto de Vinila e borracha nitrílica, PVC/NBR, obtidas por processamento reativo. A vulcanização dinâmica melhorou o desempenho mecânico destas blendas, notadamente pelo aumento da rigidez desses sistemas, sendo obtido um aumento de 205% no módulo elástico de blendas vulcanizadas com 10% em massa de NBR em comparação com blendas convencionais. Através de análises de MEV, revelou-se uma morfologia bifásica, sendo que a formação de ligações cruzadas deve ocorrer preferencialmente no interior das partículas do elastômero, contribuindo para o aumento na resistência mecânica final das blendas obtidas por processamento reativo.Dynamic vulcanization is a process of vulcanization of an elastomer during melt mixing with a thermoplastic. This process increases the mechanical resistance of elastomers through the increase of elastic modulus, hardness and abrasion/fatigue resistance. In this study, it was evaluated the physical-mechanical and morphological behaviors of the PVC/NBR blends obtained by reactive processing. The dynamic vulcanized blends have a better performance compared to the similar conventional ones. It was observed an increase of 205% in the elastic modulus to the dynamic vulcanized blend PVC/NBR (90/10 compared with the conventional blends. The morphology of the blends examined by scanning electron microscopy evidenced the crosslinking formation only in the elastomeric phase. The vulcanized rubber particles are responsible by the increase of stiffness and consequently displayed better

Preparation of a new gamma irradiated PVC-Olive oil cake plastic composite material

International Nuclear Information System (INIS)

Messaud, F.A.; Almsmary, Y.A.; Elwerfalli, S.M.; Benayad, S.M.; Haraga, S.O.; Benfaid, N.A.; Kabar, Y.M.

2003-01-01

This paper dealt with the investigation on preparing new plastic composite material, utilizing polyvinyl chloride polymer (a commercial product in abu-kammash chemical complex) and olive oil cake (a waste of many olive oil production factories), followed by gamma irradiation (26.3 Kg ry) o induce crosslinking of the polymer. The new material possess good, electrical and mechanical properties as compared to plastic products of (PVC plastic pipe factory), and which could be used as new construction anti corrosive material, such as special roofing and partitioning or household goods

Understanding and coming through PVC-tape-induced stress corrosion cracking in PWR piping system

International Nuclear Information System (INIS)

Shibayama, Motoaki; Shigemoto, Naoya; Noguchi, Shinji; Hirano, Shin-ichi; Takagi, Toshimitsu

2003-01-01

In October 2000, the 24 years old Ikata-1 PWR-type nuclear power plant suffered cracking in pipes of special two lines, where poly vinyl chloride (PVC) tape had been placed and had become baked over time. The existence of residual stress over 100 MPa in the pipes, a bit of chlorine and a feather like-pattern on the crack faces suggested the event was one of stress corrosion cracking. Residual chlorine on the pipes of special two lines was estimated to be 1100 mg/m 2 . A four points bending stress test was performed on the steel plates with the baked on PVC tape in humid air at 80degC. Taking the actual temperature, stress and chlorine on the pipes of the special two lines into consideration, cracking times were estimated to be 12 years and 15 years respectively, which were close to the actual cracking time of 24 years. The authors calculated damage to pipes with fluids of various temperature and duration, and graphed damage contour with a fluid temperature ordinate and a flow duration abscissa. The fluid conditions of major pipes at the Ikata-1 nuclear power plant, which had not received the full inspection, were positioned on so low area on the damage contour that the plant was estimated to be safe for the coming forty years. (author)

Volatile organic components migrating from plastic pipes (HDPE, PEX and PVC) into drinking water.

Science.gov (United States)

Skjevrak, Ingun; Due, Anne; Gjerstad, Karl Olav; Herikstad, Hallgeir

2003-04-01

High-density polyethylene pipes (HDPE), crossbonded polyethylene pipes (PEX) and polyvinyl chloride (PVC) pipes for drinking water were tested with respect to migration of volatile organic components (VOC) to water. The odour of water in contact with plastic pipes was assessed according to the quantitative threshold odour number (TON) concept. A major migrating component from HDPE pipes was 2,4-di-tert-butyl-phenol (2,4-DTBP) which is a known degradation product from antioxidants such as Irgafos 168(R). In addition, a range of esters, aldehydes, ketones, aromatic hydrocarbons and terpenoids were identified as migration products from HDPE pipes. Water in contact with HDPE pipes was assessed with respect to TON, and values > or =4 were determined for five out of seven brands of HDPE pipes. The total amount of VOC released to water during three successive test periods were fairly constant for the HDPE pipes. Corresponding migration tests carried out for PEX pipes showed that VOC migrated in significant amounts into the test water, and TON >/=5 of the test water were observed in all tests. Several of the migrated VOC were not identified. Oxygenates predominated the identified VOC in the test water from PEX pipes. Migration tests of PVC pipes revealed few volatile migrants in the test samples and no significant odour of the test water.

Study on emission of decomposed chemicals of esters contained in PVC flooring and adhesive

Energy Technology Data Exchange (ETDEWEB)

Chino, Satoko; Ataka, Yuji [R and D Center, Yoshino Gypsum Co., Ltd., 2-1-1 Kohoku, Adachi-ku, Tokyo, 123-0872 (Japan); Kato, Shinsuke; Seo, Janghoo [Institute of Industrial Science, The University of Tokyo, 4-6-1 Komaba, Meguro-ku, Tokyo 153-8505 (Japan)

2009-07-15

2-Ethyl-1-hexanol (2E1H) is sometimes detected in indoor air at relatively high concentrations. The emission mechanism for 2E1H is considered to be that moisture with a high pH in concrete slabs and self-leveling sub-flooring material reacts with di-2-ethylhexyl phthalate (DEHP) in the polyvinyl chloride (PVC) flooring and compounds containing the 2-ethyl-1-hexyl group in the adhesive. 2E1H is considered to be one of the causes of odor in indoor air and sick building syndrome, so it is important to clarify the 2E1H emission mechanism for IAQ. However, there are few reports on any experimentation into 2E1H emission by chemical reaction involving building materials. In this study, PVC floorings are attached using various adhesives to a self-leveling sub-flooring material that contains water, and their 2E1H emission rates are measured. Furthermore, the components of the adhesives are determined using chemical analysis. It is found that 2E1H emission rates from the floor are affected by the type of adhesive used. On the other hand, some components in the adhesives may suppress the hydrolysis of esters. The hydrolysis of polymers and residual monomers in the adhesive causes 2E1H emission from the adhesive. (author)

Comparative study on the migration of di-2-ethylhexyl phthalate (DEHP) and tri-2-ethylhexyl trimellitate (TOTM) into blood from PVC tubing material of a heart-lung machine.

Science.gov (United States)

Eckert, Elisabeth; Münch, Frank; Göen, Thomas; Purbojo, Ariawan; Müller, Johannes; Cesnjevar, Robert

2016-02-01

Medical devices like blood tubing often consist of PVC material that requires the addition of plasticizers. These plasticizers may migrate into the blood leading to an exposure of the patients. In this study the migration behavior of three different blood tubing sets (PVC material with two different plasticizers and silicone as control material) applied on a heart-lung machine standardly used for cardiopulmonary bypass (CPB) in children was studied. We analyzed the total plasticizer migration by analysis of both, the parent compounds as well as their primary degradation products in blood. Additionally, the total mass loss of the tubing over perfusion time was examined. The PVC tubing plasticized with DEHP (di-2-ethylhexyl phthalate) was found to have the highest mass loss over time and showed a high plasticizer migration rate. In comparison, the migration of TOTM (tri-2-ethylhexyl trimellitate) and its primary degradation products was found to be distinctly lower (by a factor of approx. 350). Moreover, it was observed that the storage time of the tubing affects the plasticizer migration rates. In conclusion, the DEHP substitute TOTM promises to be an effective alternative plasticizer for PVC medical devices particularly regarding the decreased migration rate during medical procedures. Copyright © 2015 Elsevier Ltd. All rights reserved.

Model decontamination of PVC flooring specimens by wet method

International Nuclear Information System (INIS)

Severa, J.; Knajfl, J.; Bar, J.

1981-01-01

PVC flooring samples of 29 mm in diameter were used in experiments. The samples were degreased. Tested were the dependence of the degree of contamination on the duration of contact with the contaminant and the efficacy of decontamination by wiping with tampons and immersing in solutions. A mixture of fission products of 80 kBq/ml in specific activity was used for contamination. Higher decontamination efficacy was achieved by immersing the samples in decontamination solutions. Water was found to be the least efficacious medium; a high degree was only attained in the case when decontamination was effected within 1 minute after contamination. The highest decontamination values were achieved using solutions containing a chelating agent and a surfactant. The most efficacious solutions contained 0.5% of citric acid and 0.5% of detergents which are very potent at a concentration as low as 2 g/l. (J.P.)

Construction of Tb3+ PVC-MembraneElectrode Based on N,N’-Bis(pyrrolylmethylene-2-aminobenzylamine

Directory of Open Access Journals (Sweden)

Hassan Ali Zamani

2011-01-01

Full Text Available In this work, we report as new Tb3+-PVC membrane sensor based on N,N’-bis(pyrrolylmethylene- 2-aminobenzylamine (PMA as a suitable ion carrier. Poly vinylchloride (PVC-based membrane composed of PMA with oleic acid (OA as anionic additives and acetophenone (AP as plasticizing solvent mediators. The Tb3+ sensor exhibits a Nernstian slope of 19.7±0.4 mV per decade over the concentration range of 1.0×10-5 to 1.0×10-2 M and a detection limit of 4.6×10-6 M of Tb3+ ions. The potentiometric response of the sensor is independent of the solution pH in the range of 2.9–8.1. It has a very short response time, in the whole concentration range (∼5 s. The recommended sensor revealed comparatively good selectivity with respect to most alkali, alkaline earth, some transition and heavy metal ions. It was successfully employed as an indicator electrode in the potentiometric titration of Tb(III ions with EDTA. The electrode was also employed for the determination of the fluoride ion in two mouth wash preparations and the determination of Tb3+ ions concentration in mixtures of three different ions.

Degradation of PVC/HC blends. II. Terrestrial plant growth test.

Science.gov (United States)

Pascu, Mihaela; Agafiţei, Gabriela-Elena; Profire, Lenuţa; Vasile, Cornelia

2009-01-01

The behavior at degradation by soil burial of some plasticized polyvinyl chloride (PVC) based blends with a variable content of hydrolyzed collagen (HC) has been followed. The modifications induced in the environment by the polymer systems (pH variation, physiologic state of the plants, assimilatory pigments) were studied. Using the growth test of the terrestrial plants, we followed the development of Triticum (wheat), Helianthus annus minimus (little sunflower), Pisum sativum (pea), and Vicia X hybrida hort, during a vegetation cycle. After the harvest, for each plant, the quantities of chlorophyll and carotenoidic pigments and of trace- and macroelements were determined. It was proved that, in the presence of polymer blends, the plants do not suffer morphological and physiological modifications, the products released in the culture soil being not toxic for the plants growth.

Chemical effects of ionizing radiations and electron beam in polymers: industrial uses

International Nuclear Information System (INIS)

Yamasaki, M.C.R.; Reis, R.V.V. dos; Araujo, E.P.

1991-01-01

The results obtained from the development PVC dose indicator films, from the PE and PP hydrophilization and from the formulations of crosslink able resins and curable inks and varnishes by radiation, are herein discussed. (author)

Application of thiolterminated prepolymers for electron beam curing coating system

International Nuclear Information System (INIS)

Seko, Kenji; Isozaki, Osamu; Iwasawa, Naozumi

1988-01-01

It has been known that the mixture of an unsaturated prepolymer and a thiolated prepolymer can be cured by the relatively low dose of electron beam irradiation. As a thiolated prepolymer, polyether-polythiol prepolymer has been in the market. However, the coating films derived from the composition comprising the thiolated prepolymer do not have enough mechanical strength for practical use. In this study, the synthesis of thiolterminated urethane prepolymer and the coating composition comprising this prepolymer for obtaining the coating films having good mechanical properties were investigated. The raw materials used for the synthesis of thiolterminated urethane prepolymer are shown. Its synthesis and the measurement of thiol content, coating formation, the electron beam curing of the coatings and the testing method of coated film performance are explained. The results of the synthesis of the thiolterminated urethane prepolymer, the thermal stability, curability, physical properties and adhesion strength of the coatings are reported. The coatings can be applied to steel and PVC films, and used as the adhesive for steel-PVC film laminates. (Kako, I.)

Radicals formation in the PVC/DOP plastisol radiolysis used as equivalent-tissue in radiotherapy

International Nuclear Information System (INIS)

Pezzin, A.P.T.; Salman, K.D.; Mei, L.H.I.

1997-01-01

Recently, a tissue simulator called bolus was developed at FEQ/UNICAMP, which is made of dioctyl phthalate and poly (vinyl chloride) (DOC/PVC). This bolus has the function of displacing the maximum dose the skin surface in radiation therapy of skin and breast cancer. In this way the healthy tissues around the tumor are protected. Research at the Center for Women's Health (CAISM) of the Clinical Hospital of UNICAMP has shown that this material can be used as the tissue-equivalent of skin. In the present work, bolus samples were irradiated by gamma rays and the radicals formed were investigated by electron paramagnetic resonance at 110K. The results showed the radicals formation as a consequence of the homolytic scissions of the chemical bonds of DOP and the air presence interfere in the quantity of observed paramagnetic species. (author)

Geometric shape control of thin film ferroelectrics and resulting structures

Science.gov (United States)

McKee, Rodney A.; Walker, Frederick J.

2000-01-01

A monolithic crystalline structure and a method of making involves a semiconductor substrate, such as silicon, and a ferroelectric film, such as BaTiO.sub.3, overlying the surface of the substrate wherein the atomic layers of the ferroelectric film directly overlie the surface of the substrate. By controlling the geometry of the ferroelectric thin film, either during build-up of the thin film or through appropriate treatment of the thin film adjacent the boundary thereof, the in-plane tensile strain within the ferroelectric film is relieved to the extent necessary to permit the ferroelectric film to be poled out-of-plane, thereby effecting in-plane switching of the polarization of the underlying substrate material. The method of the invention includes the steps involved in effecting a discontinuity of the mechanical restraint at the boundary of the ferroelectric film atop the semiconductor substrate by, for example, either removing material from a ferroelectric film which has already been built upon the substrate, building up a ferroelectric film upon the substrate in a mesa-shaped geometry or inducing the discontinuity at the boundary by ion beam deposition techniques.

Fatigue characterization of Poly Vinyl Chloride (PVC) foam core sandwich composite using the G-control method

DEFF Research Database (Denmark)

Manca, Marcello; Berggreen, Christian; Carlsson, Leif A.

2016-01-01

This paper presents experimental results from cyclic crack propagation tests performed on sandwich specimens with glass/epoxy face sheets and Poly Vinyl Chloride (PVC) foam cores using the G-controlled cyclic energy release rate (ΔG) test procedure. The face material was tested in tension......, compression and shear to determine in-plane and out-of-plane mechanical properties, such as Young’s modulus, Poisson’s ratio and shear modulus. These properties were then used in an analytical model of the mixed-mode bending sandwich specimen to calculate compliance and energy release rate. Finite element...... on tested specimens, highlighting the influence of mode mixity and foam density on the crack path. Crack propagation diagrams showing da/dN versus ΔG curves were obtained to establish the Paris-Erdogan relation for each material combination tested at the two mode-mixities. Results showed constant crack...

Evaluation of column flotation results with a film flotation method; Film fusenho wo mochiita column fusen kekkan no hyoka

Energy Technology Data Exchange (ETDEWEB)

Fujimoto, H.; Matsukata, M.; Ueyama, K. [Osaka University, Osaka (Japan). Faculty of Engineering Science

1996-10-28

Change in wettability of coal particle surfaces due to kerosene adsorption was studied by using a film flotation method. The applicability of a film flotation method to coals modified by kerosene adsorption was first confirmed. In experiment, film flotation was applied to Illinois coal modified by aqueous methanol solution and kerosene adsorption, and the weight percent of residual particles on a gas-liquid interface and kerosene in aqueous methanol solution were analyzed to verify the applicability of a film flotation method. Film flotation was applied to Datong and Illinois coals modified by kerosene adsorption, and the weight percent of residual particles on a gas-liquid interface was plotted to surface tension of liquid. As a result, the weight percent of hydrophobic particles within 50mN/m in surface tension slightly increased in Datong coal and remarkably increased in Illinois coal with kerosene addition. It was thus suggested that in addition to surface tension, the distributions of hydrophilic and hydrophobic strengths on the surface of each coal particle should be considered to understand attachment of coal particles and bubbles. 6 refs., 4 figs.

Processing of nanocomposites EVA/PVC/MMT in twin-screw extruder

International Nuclear Information System (INIS)

Gehlen, A.; Barbutti Filho, W.R.; Francisquetti, E.L.; Andrade, M.Z.; Zattera, A.J.

2010-01-01

Polymeric nanocomposites have some superior properties when compared to conventional polymer composites and is one of the most promising fields in the nanotechnology research. In a EVA (ethylene vinyl acetate) /PVC (poly vinyl chloride) matrix was incorporated different types of montmorillonite clays (an inorganic (Na + ) and two organic modified (15A and 30B nanoclays). The mixtures were processed in a co-rotating twin-screw extruder at processing speeds of 200 and 400 rpm. Thermogravimetric analysis (TGA) shown that the inorganic and organic modified clays promoted a shift to higher temperatures in the degradation temperature., X-ray diffraction (XRD) and transmission electronic microscopy (TEM) shows a possible intercalation with the 15A clay, exfoliation with the 30B clay and formation of clusters in the Na + clay. For all clays studied, the increase in shear rate does not promote significant changes. (author)

Evidence of ammonium ion-exchange properties of natural bentonite and application to ammonium detection.

Science.gov (United States)

Zazoua, A; Kazane, I; Khedimallah, N; Dernane, C; Errachid, A; Jaffrezic-Renault, N

2013-12-01

Ammonium exchange with hybrid PVC-bentonite (mineral montmorillonite clay) thin film was revealed using FTIR spectroscopy, EDX, cyclic voltammetry and electrochemical impedance spectroscopy. The effect of ammonium exchange on the charge transfer resistance of PVC-bentonite hybrid thin film was attributed to a modification of the intersheet distance and hydration of bentonite crystals. The obtained impedimetric ammonium sensor shows a linear range of detection from 10(-4)M to 1M and a detection limit around 10(-6)M. © 2013.

Efficiency analysis and assessment of interlocking PVC sheet piling walls

International Nuclear Information System (INIS)

Emam, A.A.

2005-01-01

The use of PVC sheet piling in marine environments offers a number of unique advantages that include weight saving, corrosion resistance and environmentally safe material. In this study, one of the widely used classical methods as well as a finite element analysis are used to analyze such sheet piling walls. The analysis focuses on the effect of some important parameters on the wall global behavior, bending moments, stresses and deflections. The parameters include wall cross-section, wall height, embedment depth, number and spacing of anchor rods, and type of soil and loading conditions. Furthermore, the effect of the shape of the wall cross-section and the location of the interlocking joints has been studied by using plane frame and arch-like models. Results indicate that the finite element modeling is an effective tool for numerical approximation of soil-structure interaction problems. The required theoretical embedment depth is nearly 30 % of the clear wall height. Also, the modulus of subgrade reaction has a minor effect on both cantilever wall and one anchor sheet-pile wall. Finally, lateral (horizontal) action shows that deep sections tend to behave like an arch under radial loading which might increase normal stresses at some critical sections

Influence of polymer packaging films on hyperspectral imaging data in the visible-near-infrared (450-950 nm) wavelength range.

Science.gov (United States)

Gowen, A A; O'Donnell, C P; Esquerre, C; Downey, G

2010-03-01

Hyperspectral imaging (HSI) has recently emerged as a useful tool for quality analysis of consumer goods (e.g., food and pharmaceutical products). These products are typically packaged in polymeric film prior to distribution; however, HSI experiments are typically carried out on such samples ex-packaging (either prior to or after removal from packaging). This research examines the effects of polymer packaging films (polyvinyl chloride (PVC) and polyethylene terephthalate (PET)) on spectral and spatial features of HSI data in order to investigate the potential of HSI for quality evaluation of packaged goods. The effects of packaging film were studied for hyperspectral images of samples obtained in the visible-near-infrared (Vis-NIR, i.e., 450-950 nm) wavelength range, which is relevant to many food, agricultural, and pharmaceutical products. The dominant influence of the films tested in this wavelength range could be attributed to light scattering. Relative position of the light source, film, and detector were shown to be highly influential on the scattering effects observed. Detection of features on samples imaged through film was shown to be possible after some data preprocessing. This suggests that quality analysis of products packaged in polymer film is feasible using HSI. These findings would be useful in the development of quality monitoring tools for consumer products post-packaging using HSI.

Application of water flowing PVC pipe and EPS foam bead as insulation for wall panel

Science.gov (United States)

Ali, Umi Nadiah; Nor, Norazman Mohamad; Yusuf, Mohammed Alias; Othman, Maidiana; Yahya, Muhamad Azani

2018-02-01

Malaysia located in tropical climate which have a typical temperature range between 21 °C to 36 °C. Due to this, air-conditioning system for buildings become a necessity to provide comfort to occupants. In order to reduce the energy consumption of the air-conditioning system, the transmission of heat from outdoor to indoor space should be kept as minimum as possible. This article discuss about a technology to resist heat transfer through concrete wall panel using a hybrid method. In this research, PVC pipe was embedded at the center of concrete wall panel while the EPS foam beads were added about 1% of the cement content in the concrete mix forming the outer layer of the wall panel. Water is regulated in the PVC pipe from the rainwater harvesting system. The aim of this study is to minimize heat transfer from the external environment into the building. Internal building temperature which indicated in BS EN ISO 7730 or ASHRAE Standard 55 where the comfort indoor thermal is below 25°C during the daytime. Study observed that the internal surface temperature of heat resistance wall panel is up to 3°C lower than control wall panel. Therefore, we can conclude that application of heat resistance wall panel can lead to lower interior building temperature.

Biodigestão anaeróbia de dejetos de caprinos e ovinos em reator contínuo de PVC flexível Anaerobic digestion of goat and sheep wastes in a continuous reactor of flexible PVC

Directory of Open Access Journals (Sweden)

Danilo G. de Quadros

2010-03-01

Full Text Available A escassez de fontes energéticas e as altas taxas de mortalidade do rebanho são dois grandes problemas para os agricultores familiares no semiárido brasileiro. De setembro de 2006 a abril de 2007 um reator contínuo com gasômetro em PVC flexível, com 33 m³ de volume, instalado na Estação Experimental da EBDA, Jaguarari, Estado da Bahia, foi monitorado quanto aos parâmetros bioquímicos, microbiológicos e parasitários do afluente e efluente, sendo avaliadas a produção e a composição do biogás, além da utilização do biofertilizante em capim-elefante. Com o manejo adequado, o poder poluente dos dejetos foi reduzido significativamente. Microbiologicamente, a eficiência de remoção de coliformes totais e fecais se manteve acima de 98% enquanto os ovos dos principais endoparasitos foram eliminados com o tratamento. A produção de biogás foi de 0,061 m³ kg-1 de esterco. Basicamente, o biogás apresentou, em sua composição, 58 e 34% de metano e gás carbônico, respectivamente. O biofertilizante (pH 7,5 foi uma boa fonte de nutrientes, sobretudo de nitrogênio (64 g 100L-1, 80% na forma amoniacal e potássio (214 g 100L-1, aumentando a produção de forragem sem alterações significativas na composição bromatológica, digestibilidade "in vitro" da matéria seca e teor de minerais.The scarcity of energy resources and the high livestock mortality rates are perpetual problems for small farmers of the Brazilian semi-arid region. From September 2006 to April 2007 a continuous reactor, of 33 m³ with gasometer in PVC flexible film, was installed at the EBDA Experimental Station, Jaguarari, Bahia State and the affluent and effluent biochemical, microbiological, and parasitological characteristics were monitored, the biogas production and composition being evaluated, as well as the use of the biofertilizer in elephant grass. With adequate management, the pollution power of residues reduced significantly. Microbiologically, the

Recovery of Pu from PVC vials and bottles used for sample storage

International Nuclear Information System (INIS)

Purohit, Paru; Bhide, M.K.; Kulkarni, M.J.; Kumar, Mithlesh; Adya, V.C.; Hon, N.S.; Kadam, R.M.; Nathaniel, Newton; Natarajan, V.

2011-01-01

Plutonium in the form of oxide is stored in plastic vials and bottles during its analysis for trace metal as say. Due to radiation damage and moisture, small amount of oxide samples were found to be adhering to surface of vials/ bottles. This required methods for safe disposal. Methods involving wet chemical and dry cleaning procedures were evaluated for effective removal of sticking α active plutonium oxide powder from these vials for their safe disposal. Dry cleaning method for removal of plutonium activity was found to be effective method for disposal of storage vial, while wet chemical method was found to be more suitable for removal of plutonium from damaged PVC bottles. (author)

78 FR 9670 - Polyethylene Terephthalate Film, Sheet, and Strip From India: Final Results of Administrative...

Science.gov (United States)

2013-02-11

... administrative review of the antidumping duty order on polyethylene terephthalate film (PET Film) from India.\\1.... (Polyplex), and SRF Limited (SRF), producers and exporters of PET Film from India. Based on the results of... FURTHER INFORMATION CONTACT: Elfi Blum or Toni Page, AD/CVD Operations, Office 6, Import Administration...

The value of radiochromic film dosimetry around air cavities: experimental results and Monte Carlo simulations

International Nuclear Information System (INIS)

Paelinck, L; Reynaert, N; Thierens, H; Wagter, C de; Neve, W de

2003-01-01

In this study we investigate radiochromic film dosimetry around air cavities with particular focus on the perturbation of the dose distribution by the film when the film is parallel to the beam axis. We considered a layered polystyrene phantom containing an air cavity as a model for the air-soft tissue geometry that may occur after surgical resection of a paranasal sinus tumour. A radiochromic film type MD-55 was positioned within the phantom so that it intersected the cavity. Two phantom set-ups were examined. In the first case, the air cavity is at the centre of the phantom, thus the film is lying along the central beam axis. In the second case, the cavity and film are located 2 cm offset from the phantom centre and the central beam axis. In order to examine the influence of the film on the dose distribution and to interpret the film-measured results, Monte Carlo simulations were performed. The film was modelled rigorously to incorporate the composition and structure of the film. Two field configurations, a 1 x 10 cm 2 field and a 10 x 10 cm 2 field, were examined. The dose behind the air cavity is reduced by 6 to 7% for both field configurations when a film that intersects the cavity contains the central beam axis. This is due to the attenuation exerted by the film when photons cross the cavity. Offsetting the beam to the cavity and the film by 2 cm removes the dose reduction behind the air cavity completely. Another result was that the rebuild-up behind the cavity for the 10 x 10 cm 2 field, albeit less significant than for the 1 x 10 cm 2 field, could only be measured by the film that was placed offset with respect to the central beam axis. Although radiochromic film is approximately soft-tissue equivalent and energy independent as compared to radiographic films, care should be taken in the case of inhomogeneous phantoms when the film intersects air cavities and contains the beam central axis. Errors in dose measurement can be expected distal to the air cavity

Covalent immobilization of lipase, glycerol kinase, glycerol-3-phosphate oxidase & horseradish peroxidase onto plasticized polyvinyl chloride (PVC strip & its application in serum triglyceride determination

Directory of Open Access Journals (Sweden)

Nidhi Chauhan

2014-01-01

Full Text Available Background & objectives:Reusable biostrip consisting enzymes immobilized onto alkylamine glass beads affixed on plasticized PVC strip for determination of triglyceride (TG suffers from high cost of beads and their detachments during washings for reuse, leading to loss of activity. The purpose of this study was to develop a cheaper and stable biostrip for investigation of TG levels in serum. Methods: A reusable enzyme-strip was prepared for TG determination by co-immobilizing lipase, glycerol kinase (GK, glycerol-3-phosphate oxidase (GPO and peroxidase (HRP directly onto plasticized polyvinyl chloride (PVC strip through glutaraldehyde coupling. The method was evaluated by studying its recovery, precision and reusability. Results: The enzyme-strip showed optimum activity at pH 7.0, 35 o C and a linear relationship between its activity and triolein concentration in the range 0.1 to 15 mM. The strip was used for determination of serum TG. The detection limit of the method was 0.1 mM. Analytical recovery of added triolein was 96 per cent. Within and between batch coefficients of variation (CV were 2.2 and 3.7 per cent, respectively. A good correlation (r=0.99 was found between TG values by standard enzymic colrimetric method employing free enzymes and the present method. The strip lost 50 per cent of its initial activity after its 200 uses during the span of 100 days, when stored at 4 o C. Interpretation & conclusions: The nitrating acidic treatment of plasticized PVC strip led to glutaraldehyde coupling of four enzymes used for enzymic colourimetric determination of serum TG. The strip provided 200 reuses of enzymes with only 50 per cent loss of its initial activity. The method could be used for preparation of other enzyme strips also.

The microjet-film interaction: the interaction and resulting shapes of a liquid microjet impacting a soap film

Science.gov (United States)

Chan, Jau Tung; Lee, Jie Liang; Tjeng, Vincent; Yeo, Ye; Tan, Guoxian

2014-11-01

The International Young Physicists’ Tournament (IYPT) is a worldwide annual competition for high-school students. This paper is adapted from the solution to problem 8, Jet and Film, as presented by the Singapore Team at the 26th IYPT, Taipei, Taiwan. The impact of liquid microjets on stable soap films was investigated. Two steady regimes were observed: refraction (where the microjet penetrates the soap film and is deflected) and absorption (where the microjet merges with the soap film and forms vertical undulating patterns on the soap film surface). This phenomenon has potential applications in controlling the trajectory of a liquid microjet in air. Although Kirstetter et al (2012) investigated this interaction by using the same liquid for both the microjet and the soap film, this paper extends their work by using different liquids for the microjet and the soap film. In addition, the need for a small-angle approximation of Snell’s law is removed for the refraction regime, and an alternative expression is proposed for the force exerted by the soap film on the microjet in the absorption regime that accounts for the dependence of the wavelength of the undulating patterns on the angle of incidence of the microjet on the soap film. Empirical data support these improved theoretical predictions.

The microjet-film interaction: the interaction and resulting shapes of a liquid microjet impacting a soap film

International Nuclear Information System (INIS)

Chan, Jau Tung; Tan, Guoxian; Lee, Jie Liang; Tjeng, Vincent; Yeo, Ye

2014-01-01

The International Young Physicists’ Tournament (IYPT) is a worldwide annual competition for high-school students. This paper is adapted from the solution to problem 8, Jet and Film, as presented by the Singapore Team at the 26th IYPT, Taipei, Taiwan. The impact of liquid microjets on stable soap films was investigated. Two steady regimes were observed: refraction (where the microjet penetrates the soap film and is deflected) and absorption (where the microjet merges with the soap film and forms vertical undulating patterns on the soap film surface). This phenomenon has potential applications in controlling the trajectory of a liquid microjet in air. Although Kirstetter et al (2012) investigated this interaction by using the same liquid for both the microjet and the soap film, this paper extends their work by using different liquids for the microjet and the soap film. In addition, the need for a small-angle approximation of Snell’s law is removed for the refraction regime, and an alternative expression is proposed for the force exerted by the soap film on the microjet in the absorption regime that accounts for the dependence of the wavelength of the undulating patterns on the angle of incidence of the microjet on the soap film. Empirical data support these improved theoretical predictions. (paper)

Selective sensing of mercury(II) using PVC-based membranes incorporating recently synthesized 1,3-alternate thiacalix[4]crown ionophore.

Science.gov (United States)

Mahajan, Rakesh Kumar; Kamal, Ajar; Kumar, Naresh; Bhalla, Vandana; Kumar, Manoj

2013-05-01

The construction and electrodes characteristics of poly(vinylchloride) (PVC)-based polymeric membrane electrode (PME) and coated graphite electrode (CGE), incorporating 1,3-alternate thiacalix[4]crown as ionophore for estimation of Hg(II) ions, are reported here. The best potential response was observed for PME-1 having membrane composition of: ionophore (6.2 mg), PVC (100.0 mg), 2-nitrophenyl octyl ether (2-NPOE; 200.0 mg), and sodium tetraphenyl borate (NaTPB; 2.0 mg); for CGE-1 with the membrane composition: ionophore (3.5 mg), PVC (40.0 mg), 2-NPOE (80.0 mg), and NaTPB (2.0 mg). The electrodes exhibits Nernstian slope of 29.16 mV/decade with PME-1 and 30.39 mV/decade with CGE-1 for Hg(II) ions over wide concentration range, i.e., 1.0 × 10(-1) to 5.0 × 10(-6) M with PME-1 and 1.0 × 10(-1) to 5.0 × 10(-7) M with CGE-1. Lower detection limits were found to be 9.77 × 10(-6) M for PME-1 and 7.76 × 10(-7) M for CGE-1 with response time varying from 10 to 20 s. Also, these electrodes work within pH range of 2.0-6.0 for PME-1 and 1.5-6.5 for CGE-1. Overall, CGE-1 has been found to be better than PME-1. CGE-1 has been used as indicator electrode for the potentiometric titration of Hg(II) ions with EDTA as well as successfully applied for determination of Hg(II) content in wastewater, insecticide, dental amalgam, and ayurvedic medicines samples with very good performance (0.9974 correlation coefficient in the comparison against volumetric method).

Evaluation of the effectiveness of lamination for preventing discoloration and fading of radiation warning signs posted on the exterior of radiation facilities

International Nuclear Information System (INIS)

Hiroi, Tomoko; Ootaki, Masanori; Nawa, Yukino; Kuwabara, Rie; Tatsunami, Shinobu; Matsui, Hiroaki; Kumazawa, Yutaka; Yamamoto, Takio

2014-01-01

Radiation warning signs posted on the exterior of radiation facilities become faded and discolored with time. There are various types of commercially available laminating films for protecting signs from ultraviolet light. We examined the protection effect of polyvinyl chloride (PVC), acrylic resin and fluororesin films applied to the surface of radiation warning signs. The laminated signs were exposed to direct sunlight on the wall of an air filter chamber of a radiation facility for 1200 days. Simultaneously, another set of laminated signs was exposed to light from a xenon-arc weatherometer for 1200 hours. After exposure, the colors on the surface of each sign were evaluated digitally by using a spectrum colorimeter. The results indicated that lamination with a film that blocks ultraviolet light is effective for protecting the signs from fading and discoloration. For long-term protection under direct sunlight, PVC was the most effective among the three materials tested. (author)

78 FR 29700 - Polyethylene Terephthalate Film, Sheet, and Strip From the United Arab Emirates: Final Results of...

Science.gov (United States)

2013-05-21

... Film, Sheet, and Strip From the United Arab Emirates: Final Results of Antidumping Duty Administrative... (PET Film) from the United Arab Emirates.\\1\\ This review covers two producers/exporters of subject... Terephthalate Film, Sheet, and Strip from the United Arab Emirates: Preliminary Results of Antidumping Duty...

Solar radiation inside greenhouses covered with semitransparent photovoltaic film: first experimental results

Directory of Open Access Journals (Sweden)

Alvaro Marucci

2013-09-01

Full Text Available The southern Italian regions are characterized by climatic conditions with high values of solar radiation and air temperature. This has allowed the spread of protected structures both as a defense against critical winter conditions both for growing off-season. The major energy source for these greenhouses is given by solar energy and artificial energy is used rarely. So the problem in the use of greenhouses in these areas, if anything, is opposite to that of the northern areas. In these places you must try to mitigate often the solar radiation inside the greenhouses with suitable measures or abandon for a few months the cultivation inside these structures. The solar radiation intercepted by passive means can be used for other purposes through the uptake and transformation by the photovoltaic panels whose use however is problematic due to complete opacity of the cells. New photosensitive materials partially transparent to solar radiation onto flexible media, allow to glimpse the possibility of using them to greenhouses cover, getting the dual effect of partially screen the greenhouse and use the surplus to generate electricity. The research was carried out to evaluate the possibility of using a flexible photovoltaic film realized by the University of Rome Tor Vergata (research group of ECOFLECS project coordinated by prof. Andrea Reale for covering greenhouses. Two greenhouses in small scale were built: one covered with photovoltaic film and one covered with EVA film for test. In both greenhouses during the first research period it was grown a variety of dwarf tomato. The research was carried out comparing the solar radiation that enters into greenhouse in the summer (August 2012 and in winter conditions (December 2012 in both greenhouses. The result show that the average ratio between the daily global solar radiation under the photovoltaic film and outside radiation is about 37%, while between the radiation under EVA film and outside radiation

Preparation and Characterization of PVC-Al2O3-LiClO4 Composite Polymeric Electrolyte

International Nuclear Information System (INIS)

Azizan Ahmad; Mohd Yusri Abdul Rahman; Siti Aminah Mohd Noor; Mohd Reduan Abu Bakar

2009-01-01

Ionic conductivity of composite polymer electrolyte PVC-Al 2 O 3 -LiClO 4 as a function of Al 2 O 3 concentration has been studied. The electrolyte samples were prepared by solution casting technique. Their ionic conductivity was measured using impedance spectroscopy technique. It was observed that the conductivity of the electrolyte varies with Al 2 O 3 concentration. The highest room temperature conductivity of the electrolyte of 3.43 x 10 -10 S.cm -1 was obtain at 25 % by weight of Al 2 O 3 and that without Al 2 O 3 filler was found to be 2.43 x 10 -11 S.cm -1 . The glass transition temperature decreases with the increase of Al 2 O 3 percentage due to the increasing amorphous state, meanwhile the degradation temperature increases with the increase of Al 2 O 3 percentage. Both of these thermal properties influence the enhancement of the conductivity value. The morphology of the samples shows the even distribution of the Al 2 O 3 filler in the samples. However, the filler starts to agglomerate in the sample when high percentage of Al 2 O 3 is being used. In conclusion, the addition of Al 2 O 3 filler improves the ionic conductivity of PVC- Al 2 O 3 -LiCIO 4 solid polymer electrolyte. (author)

Long-term Performance of PVC and CSPE Cables used in Nuclear Power Plants: the Effect of Degradation and Plasticizer migration

International Nuclear Information System (INIS)

Ekelund, Maria

2009-10-01

that the transport of DEHP to the surrounding environment was diffusion controlled at temperatures between 120 deg C and 150 deg C, with an activation energy of 89 kJ/mol. At lower temperatures, HTML clipboard =100 deg C, the loss of plasticizer was controlled by evaporation, with an activation energy of 99 kJ/mol. Under the latter conditions, the rate of plasticizer loss from the PVC cable was very similar to that from the pure plasticizer, suggesting that a film of plasticizer was formed on the PVC surface. The evaporation of DEHP showed a clear dependence on the rate of ventilation of the gas phase surrounding the cable. The ability to monitor the condition of the installed cables is dependent on good techniques for the remaining lifetime assessment. The condition monitoring technique, Line Resonance Analysis, was applied to chlorosulfonated polyethylene cables. A clear correlation between LIRA and indenter modulus data obtained and LIRA and tensile testing results was found. This is of interest since existing lifetime criteria used in the nuclear plants are based on these two testing techniques

Long-term Performance of PVC and CSPE Cables used in Nuclear Power Plants: the Effect of Degradation and Plasticizer migration

Energy Technology Data Exchange (ETDEWEB)

Ekelund, Maria

2009-10-15

that the transport of DEHP to the surrounding environment was diffusion controlled at temperatures between 120 deg C and 150 deg C, with an activation energy of 89 kJ/mol. At lower temperatures, HTML clipboard =100 deg C, the loss of plasticizer was controlled by evaporation, with an activation energy of 99 kJ/mol. Under the latter conditions, the rate of plasticizer loss from the PVC cable was very similar to that from the pure plasticizer, suggesting that a film of plasticizer was formed on the PVC surface. The evaporation of DEHP showed a clear dependence on the rate of ventilation of the gas phase surrounding the cable. The ability to monitor the condition of the installed cables is dependent on good techniques for the remaining lifetime assessment. The condition monitoring technique, Line Resonance Analysis, was applied to chlorosulfonated polyethylene cables. A clear correlation between LIRA and indenter modulus data obtained and LIRA and tensile testing results was found. This is of interest since existing lifetime criteria used in the nuclear plants are based on these two testing techniques

Comparison of the microbiological milieu of patients randomized to either hydrophilic or conventional PVC catheters for clean intermittent catheterization.

Science.gov (United States)

Lucas, Elizabeth J; Baxter, Cheryl; Singh, Chandra; Mohamed, Ahmad Z; Li, Birong; Zhang, Jingwen; Jayanthi, Venkata R; Koff, Stephen A; VanderBrink, Brian; Justice, Sheryl S

2016-06-01

Control of bacteriuria is problematic in patients who perform clean intermittent catheterization for management of neurogenic bladder. This population is often burdened with multiple urinary tract infections (UTIs), placing them at increased risk of end-stage renal disease. Hydrophilic catheters are a potential way to improve smooth and clean insertion, reduce disruption of the urothelium, and reduce bacterial colonization. The goal of the study was to compare the type and virulence of microorganisms recovered from the urine of patients that use either a hydrophilic or conventional polyvinyl chloride (PVC) catheter. Fifty patients with an underlying diagnosis of myelomeningocele were recruited for a 12-month prospective, randomized, investigator-blinded study. Twenty-five patients were allocated to the hydrophilic catheter intervention, and 25 continued use of a PVC catheter. Cultures were performed on urine obtained by catheterization at enrollment, and 3, 6, and 12 months. Bacterial species were assigned a designation as either potentially pathogenic or non-pathogenic. Escherichia coli isolates were the most predominant and were serotyped to further stratify the pathogenicity of the strains. Lastly, patients were surveyed at enrollment, and at the two later time points evaluating their current catheter for satisfaction. A total of 232 different bacterial isolates were obtained from the 182 collected urine cultures. In addition, seven species were recovered from the two UTI reported during the study period. Bacterial growth was not detected in 29 of the samples (16%). Although not statistically significant, collectively there was a 40% decrease in the average number of potentially pathogenic species recovered from those patients using hydrophilic catheters (0.81 per urine sample) compared with PVC catheter use (1.24 per urine sample). Since E. coli species can be either pathogenic or non-pathogenic, we examined 14 of the most commonly implicated serotypes

76 FR 76941 - Polyethylene Terephthalate Film, Sheet, and Strip From Taiwan: Final Results of Antidumping Duty...

Science.gov (United States)

2011-12-09

... on polyethylene terephthalate film, sheet and strip (PET Film) from Taiwan. The period of review (POR... Halle, AD/CVD Operations, Office 6, Import Administration, International Trade Administration, U.S... Results in the Administrative Review on Polyethylene Terephthalate Film, Sheet and Strip from Taiwan (PET...

PAN-Immobilized PVC-NPOE Membrane for Environmentally Friendly Sensing of Cd(II Ions

Directory of Open Access Journals (Sweden)

Moersilah Moersilah

2017-04-01

Full Text Available A simple, cheap and environmentally friendly analytical method of Cd(II in the aqueous system has been developed by immobilization of 1-(2-pyridilazo-2-naphtol (PAN in poly vinyl chloride (PVC matrix and nitrophenyl octyl ether (NPOE as a plasticizer. Upon contact with Cd(II in solution, the color of sensor membrane changes from dark yellow to dark red, which is due to the formation of Cd(II–PAN complex. The best sensing results were obtained at pH 8.0 and λmax 558 nm. The dimension of the proposed sensor membrane was 0.8 cm x 2 cm with a thickness of 0.05 mm, the volume of sample was 2 mL with the Cd(II concentration range of  0 – 1.2 ppm. The limit of detection of the method was found to be 0.432 + 0.104 ppm, which was reversible. The proposed methods have been applied in the determination of Cd(II in water samples after addition of internal standard.

78 FR 47276 - Polyethylene Terephthalate (PET) Film, Sheet, and Strip From India: Final Results of the...

Science.gov (United States)

2013-08-05

... (PET) Film, Sheet, and Strip From India: Final Results of the Expedited Second Sunset Review of the... terephthalate (PET) film, sheet, and strip (``PET film'') from India. The Department finds that revocation of... INFORMATION CONTACT: Sean Carey or Dana Mermelstein, AD/CVD Operations, Office 6, Import Administration...

76 FR 71512 - Polyethylene Terephthalate Film, Sheet, and Strip From Korea: Final Results of Antidumping Duty...

Science.gov (United States)

2011-11-18

... terephthalate film, sheet, and strip (PET film) from Korea, covering the June 1, 2009, to May 31, 2010, period... the preliminary results. In addition, the Department is revoking the antidumping order on PET film... CONTACT: Tyler Weinhold or Robert James, AD/CVD Operations, Office 7, Import Administration, International...

Electrochemistry Study on PVC-LiClO4 Polymer Electrolyte Supported by Bengkulu Natural Bentonite for Lithium Battery

Directory of Open Access Journals (Sweden)

Ghufira

2012-04-01

Full Text Available In this research bentonite was used as filler to produce polymer electrolyte (PVCLiClO4. Some weight variation of bentonite have been made by addition, such as 0% wt/wt; 5% wt/wt ; 10% wt/wt ; 15% wt/wt ; 20% wt/wt ; and 25% wt/wt of bentonite to the mixture of 0,5 gramof PVC and 0,125 gram of LiClO4. Ionic conductivity of polymer electrolyte was tested using impedance spectroscopy. The result of the research was showed that a mixture of PVCBentonite(10% wt/wt-LiClO4 gives the highest ionic conductivity (4,86 x 10-3 S.Cm-1. This result indicated that the presence of natural bentonite can be used as a filler in the current composite polymer electrolyte and can increase the ionic conductivity of the polymer electrolyte.

Software package to automate the design and production of translucent building structures made of pvc

Directory of Open Access Journals (Sweden)

Petrova Irina Yur’evna

2016-08-01

Full Text Available The article describes the features of the design and production of translucent building structures made of PVC. The analysis of the automation systems of this process currently existing on the market is carried out, their advantages and disadvantages are identified. Basing on this analysis, a set of requirements for automation systems for the design and production of translucent building structures made of PVC is formulated; the basic entities are involved in those business processes. The necessary functions for the main application and for dealers’ application are specified. The main application is based on technological platform 1C: Enterprise 8.2. The dealers’ module is .NET application and is developed with the use of Microsoft Visual Studio and Microsoft SQL Server because these software products have client versions free for end users (.NET Framework 4.0 Client Profile and Microsoft SQL Server 2008 Express. The features of the developed software complex implementation are described; the relevant charts are given. The scheme of system deployment and protocols of data exchange between 1C server, 1C client and dealer is presented. Also the functions supported by 1C module and .NET module are described. The article describes the content of class library developed for .NET module. The specification of integration of the two applications in a single software package is given. The features of the GUI organization are described; the corresponding screenshots are given. The possible ways of further development of the described software complex are presented and a conclusion about its competitiveness and expediency of new researches is made.

Conductivity, dielectric behavior and FTIR studies of high molecular weight poly(vinylchloride)-lithium triflate polymer electrolytes

International Nuclear Information System (INIS)

Ramesh, S.; Chai, M.F.

2007-01-01

Thin films of high molecular weight polyvinyl chloride (PVC) with lithium triflate (LiCF 3 SO 3 ) salt were prepared by solution casting method. The ionic conductivity and dielectric measurements were carried out on these films over a wide frequency regime at various temperatures. The conductivity-temperature plots were found to obey classical Arrhenius relationship. The dielectric behavior was analysed using dielectric permittivity and dielectric modulus of the samples. FTIR studies show some simple overlapping and shift in peaks between high molecular weight polyvinyl chloride (PVC) with lithium triflate (LiCF 3 SO 3 ) salt in the polymer electrolyte complexes

Electrodos de PVC/TTF-TCNQ modificados. Aplicación como sensores y biosensores electroquímicos

OpenAIRE

Sánchez-Obrero, Guadalupe

2013-01-01

En este trabajo de Tesis Doctoral, se estudia el desarrollo de nuevos electrodos, basados en la modificación del electrodo compósito PVC/TTF-TCNQ, mediante nanopartículas de oro. Se pretende que estos nuevos electrodos sean susceptibles de ser empleados como sensores y/o biosensores electroquímicos, para la detección de analitos de interés. De ellos, se han elegido para su determinación la glucosa, el paracetamol y los compuestos fenólicos presentes en los vinos. La Tesis Doctoral está es...

PVC's role in dioxin emissions from open burning. New analysis of US EPA data

Energy Technology Data Exchange (ETDEWEB)

Neurath, C. [Work on Waste, Canton, NY (United States)

2004-09-15

Experimental studies have revealed high rates of dioxin emission from open burning of domestic waste. Based on these studies and estimates of activity level, the US Environmental Protection Agency (EPA) dioxin inventory now projects that open burning is the single largest source of dioxin to the atmosphere in the US. They estimate it is ten times greater than the next largest source category (incineration) and that open burning produces more airborne dioxin than all other categories combined. Beginning in 1997, the EPA has published five reports of their experimental studies on open burning emissions. The latest report includes complete data from 25 test runs. An important question the EPA set out to answer was: What conditions of open burning most affect dioxin emissions? The results of their first screening level experiments suggested that the polyvinyl chloride (PVC) plastic content of the waste might have been a key determinant of dioxin levels. The EPA also measured many variables such as temperatures and gas concentrations during the runs. They conducted statistical analysis to determine correlations between these measurements and dioxin emissions. The EPA presented three main conclusions about the role of chlorine (Cl) and PVC input in creating dioxin: ''In summary, although Cl in the waste does appear to influence emissions of PCDDs/Fs from burn barrels, [1] this effect can be observed only at high levels of Cl, atypical of household trash, [2] and is independent of the source of the Cl (organic or inorganic). [3] At moderate levels of Cl, a statistically significant effect of waste Cl concentration is not observed, because other more important variables have a much greater influence on the emissions of PCDDs/Fs.'' These three conclusions contradict the findings of other studies. Also, some EPA analyses used less powerful statistical methods than were possible. For these reasons, a re-evaluation of the EPA data was undertaken.

Effect of blending temperature on the mechanical properties of PVC/ENR blend upon irradiation

International Nuclear Information System (INIS)

Chantara Thevy Ratnam; Khairul Zaman Mohd Dahlan; Nasir, M.; Baharin, A.

2000-01-01

Poly (vinyl chloride) / epoxidized natural rubber blends were prepared with a Brabender plasticorder at 140, 150, 160, 170 and 180 degree C mixing temperatures. They were mixed at 50 rpm rotor speed for 10 min. The blends were irradiated with doses ranging from 0-200 kGy. Changes in tensile strength, modulus at 100% elongation, gel fraction and damping properties (tan δ) of the blends with increasing mixing temperatures and irradiation doses were investigated. In general, it was observed that the mixing temperature is important in maximizing the positive effect of irradiation. Results revealed that a readily miscible blend enjoy maximum benefit from irradiation meanwhile irradiation impart miscibility to a partially miscible PVC/ENR blend. The enhancement in blend properties is believed to be attributed by the irradiation-induced crosslinking along with irradiation-induced interaction between the polymers. The radiation-induced degradation found to be prominent at higher doses for blend that has undergone excessive thermal degradation. However evidence did not reveal the specific nature of radiation-induced reaction responsible for the improved interactions of the blends. (author)

Viscoelastic, Spectroscopic, and Microscopic Characterization of Novel Bio-Based Plasticized Poly(vinyl chloride Compound

Directory of Open Access Journals (Sweden)

Mei Chan Sin

2014-01-01

Full Text Available Plasticized poly(vinyl chloride (PVC is one of the most widely consumed commodity plastics. Nevertheless, the commonly used plasticizers, particularly phthalates, are found to be detrimental to the environment and human health. This study aimed to investigate the ability of an alternative greener material, medium-chain-length polyhydroxyalkanoates (mcl-PHA, a kind of biopolyester and its thermally degraded oligoesters, to act as a compatible bioplasticizer for PVC. In this study, mcl-PHA were synthesized by Pseudomonas putida PGA1 in shake flask fermentation using saponified palm kernel oil (SPKO and subsequently moderately thermodegraded to low molecular weight oligoesters (degPHA. SEM, ATR-FTIR, 1H-NMR, and DMA were conducted to study the film morphology, microstructure, miscibility, and viscoelastic properties of the PVC-PHA and PVC/degPHA binary blends. Increased height and sharpness of tan δmax⁡ peak for all binary blends reveal an increase in chain mobility in the PVC matrix and high miscibility within the system. The PVC-PHA miscibility is possibly due to the presence of specific interactions between chlorines of PVC with the C=O group of PHA as evidenced by spectroscopic analyses. Dynamic viscoelastic measurements also showed that mcl-PHA and their oligoesters could reduce the Tg of PVC, imparting elasticity to the PVC compounds and decreasing the stiffness of PVC.

A novel EIS field effect structures coated with TESUD-PPy-PVC-dibromoaza[7]helicene matrix for potassium ions detection

Energy Technology Data Exchange (ETDEWEB)

Tounsi, Moncef, E-mail: tounsi1981@live.fr [Laboratoire des Interfaces et des Matériaux Avancés (LIMA), Faculté des Sciences de Monastir, Université de Monastir (Tunisia); Université de Lyon, Institut de Sciences Analytiques (ISA) – UMR 5280, 5 rue de la Doua, 69100 Villeurbanne (France); Ben Braiek, Mourad [Laboratoire de Synthèse Organique Asymétrique et Catalyse Homogène, Faculté des Sciences, Université de Monastir, Avenue de l' environnement, 5019, Monastir (Tunisia); Barhoumi, Houcine [Laboratoire des Interfaces et des Matériaux Avancés (LIMA), Faculté des Sciences de Monastir, Université de Monastir (Tunisia); Baraket, Abdoullatif; Lee, Michael; Zine, Nadia [Université de Lyon, Institut de Sciences Analytiques (ISA) – UMR 5280, 5 rue de la Doua, 69100 Villeurbanne (France); Maaref, Abderrazak [Laboratoire des Interfaces et des Matériaux Avancés (LIMA), Faculté des Sciences de Monastir, Université de Monastir (Tunisia); Errachid, Abdelhamid, E-mail: abdelhamid.errachid-el-salhi@univ-lyon1.fr [Université de Lyon, Institut de Sciences Analytiques (ISA) – UMR 5280, 5 rue de la Doua, 69100 Villeurbanne (France)

2016-04-01

In this work, we describe the development of new Aza[7]helicene-containing PVC-based membranes for the K{sup +} ions quantification. Here, silicon nitride-based structures (Si-p/SiO{sub 2}/Si{sub 3}N{sub 4}) were developed and the surface was activated, functionalized with an aldehyde–silane (11-(Triethoxysilyl)undecanal (TESUD)), functionalized with polypyrrole (PPy), and coated with the polyvinylchloride (PVC)-membrane containing the Aza[7]helicene as ionophore. All stages of functionalization process have been thoroughly studied by contact angle measurements (CAMs) and atomic force microscopy (AFM). The developed ion-selective electrode (ISE) was then applied using electrochemical impedance spectroscopy (EIS) for the detection of potassium ions. A linear range was observed between 1.0 × 10{sup −8} M to 1.0 × 10{sup −3} M and a detection limit of 1.0 × 10{sup −8} M was observed. The EIS results have showed a good sensitivity to potassium ion using this novel technique. The target helicene exhibited good solubility and excellent thermal stability with a high decomposition temperature (Td > 300 °C) and it indicates that helicene may be a promising material as ionophore for ion-selective electrodes (ISEs) elaboration. - Highlights: • Synthesis and characterization of a new derivatives of Aza[7]helicenes • Manufacture of PPy structures on the SiO{sub 2}/Si{sub 3}N{sub 4} surface using the TESUD as cross linking agent. • The PPy fabricated microstructures can be used as support matrix in biosensing. • Impedimetric K{sup +}-ISEs was developed by using dibromoaza[7]helicene as ionophore for K{sup +} ions determination.

Reduction of hexavalent chromium collected on PVC filters.

Science.gov (United States)

Shin, Y C; Paik, N W

2000-01-01

Chromium exists at various valences, including elemental, trivalent, and hexavalent chromium, and undergoes reduction-oxidation reactions in the environment. Since hexavalent chromium is known as a human carcinogen, it is most important to evaluate the oxidation-reduction characteristics of the hexavalent chromium species. Although hexavalent chromium can be reduced to trivalent state, the detailed information on this in workplace environments is limited. The purpose of this study was to investigate hexavalent chromium reduction in time in various conditions. A pilot chrome plating operation was prepared and operated in a laboratory for this study. There was evidence that the hexavalent chromium was reduced by time after mist generation. The percentage ratio (with 95% confidence intervals in parentheses) of hexavalent chromium to total chromium was almost 100% (99.1 approximately 102.3) immediately after mist generation, and was reduced to 87.4% (84.8 approximately 89.9) at 1 hour and 81.0% (78.3 approximately 83.5) at 2 hours, respectively. Another test indicated that hexavalent chromium collected on PVC filters was also reduced by time after sampling. Hexavalent chromium was reduced to 90.8% (88.2 approximately 93.3) at 2 hours after sampling. It also was found that hexavalent chromium was reduced during storage in air. It is recommended that air samples of hexavalent chromium be protected against reduction during storage.

Empirical Study on Sustainable Opportunities Recognition. A Polyvinyl Chloride (PVC Joinery Industry Analysis Using Augmented Sustainable Development Process Model

Directory of Open Access Journals (Sweden)

Eduard-Gabriel Ceptureanu

2017-09-01

Full Text Available This paper analyzes factors influencing recognition of sustainable opportunities by using an augmented sustainability process model. The conceptual model used two main factors, Knowledge and Motivation, and one moderating variable, Social embeddedness. We investigated entrepreneurs from PVC joinery industry and concluded that while market orientation and sustainable entrepreneurial orientation definitely and positively influence sustainable opportunity recognition, others variables like knowledge of the natural/communal environment, awareness of sustainable development or focus on success have less support. Among all variables analyzed, perception of the threat of the natural/communal environment and altruism toward others have the poorest impact on opportunity recognition. Finally, we concluded that social embeddedness has a moderating effect on sustainable opportunity recognition, even though the results were mixed.

Studies on radiation-sensitive nonsilver halide materials, (1)

International Nuclear Information System (INIS)

Komizu, Hideo; Honda, Koichi; Yabe, Akira; Kawasaki, Masami; Fujii, Etsuo

1978-01-01

In order to discover new radiation-sensitive nonsilver halide materials, the coloration based on the formation of Stenhouse salts was studied in the following three systems: (a) furfural-amine/HCl aq/methanol solution, (b) furfural-amine/polyhalogenide/PMMA matrix, (c) furfural-amine/PVC matrix. Firstly, forty-five aromatic amines were surveyed to find out the amines suitable for the color precursors (reactant from furfural and amine) in the system (a). As a result, the five amines, which gave the precursors in good yields by the reaction with furfural, were selected: m-nitroaniline, N-methylaniline, m-methyl-N-methylaniline, aniline, and o-methoxyaniline. Secondly, the coloration induced by electron beam bombardment was studied in the systems (b) and (c) containing the color precursors (the reactants from these amines and furfural). Although the PMMA films containing the color precursors and polyhalogenides were sensitive to electron beam, they were not stable when standing under daylight at room temperature. The PVC films containing the color precursors were very stable and colored to reddish yellow (lambda sub(max) 498 - 545 nm) by electron beam bombardment. The PVC film containing N-methylaniline-furfural was the most sensitive and the increase in absorbance at 498 nm was 0.78 by electron beam bombardment of 60 kV - 7.5 x 10 -7 C/cm 2 . A good linear relationship existed between the degree of coloration and the amounts of electron beam bombardment in the range from 0 to 10 -6 C/cm 2 . (author)

Modeling of metal thin film growth: Linking angstrom-scale molecular dynamics results to micron-scale film topographies

Science.gov (United States)

Hansen, U.; Rodgers, S.; Jensen, K. F.

2000-07-01

A general method for modeling ionized physical vapor deposition is presented. As an example, the method is applied to growth of an aluminum film in the presence of an ionized argon flux. Molecular dynamics techniques are used to examine the surface adsorption, reflection, and sputter reactions taking place during ionized physical vapor deposition. We predict their relative probabilities and discuss their dependence on energy and incident angle. Subsequently, we combine the information obtained from molecular dynamics with a line of sight transport model in a two-dimensional feature, incorporating all effects of reemission and resputtering. This provides a complete growth rate model that allows inclusion of energy- and angular-dependent reaction rates. Finally, a level-set approach is used to describe the morphology of the growing film. We thus arrive at a computationally highly efficient and accurate scheme to model the growth of thin films. We demonstrate the capabilities of the model predicting the major differences on Al film topographies between conventional and ionized sputter deposition techniques studying thin film growth under ionized physical vapor deposition conditions with different Ar fluxes.

76 FR 22867 - Polyethylene Terephthalate Film, Sheet, and Strip From the United Arab Emirates: Final Results of...

Science.gov (United States)

2011-04-25

... Film, Sheet, and Strip From the United Arab Emirates: Final Results of Antidumping Duty Administrative...) from the United Arab Emirates. This review covers two producers/ exporters of subject merchandise: JBF... Polyethylene Terephthalate Film, Sheet, and Strip From the United Arab Emirates: Preliminary Results of...

Conductivity, dielectric behavior and FTIR studies of high molecular weight poly(vinylchloride)-lithium triflate polymer electrolytes

Energy Technology Data Exchange (ETDEWEB)

Ramesh, S. [Faculty of Engineering and Science, Universiti Tunku Abdul Rahman, Setapak, 53300 Kuala Lumpur (Malaysia)]. E-mail: ramesh@mail.utar.edu.my; Chai, M.F. [Faculty of Engineering and Science, Universiti Tunku Abdul Rahman, Setapak, 53300 Kuala Lumpur (Malaysia)

2007-05-15

Thin films of high molecular weight polyvinyl chloride (PVC) with lithium triflate (LiCF{sub 3}SO{sub 3}) salt were prepared by solution casting method. The ionic conductivity and dielectric measurements were carried out on these films over a wide frequency regime at various temperatures. The conductivity-temperature plots were found to obey classical Arrhenius relationship. The dielectric behavior was analysed using dielectric permittivity and dielectric modulus of the samples. FTIR studies show some simple overlapping and shift in peaks between high molecular weight polyvinyl chloride (PVC) with lithium triflate (LiCF{sub 3}SO{sub 3}) salt in the polymer electrolyte complexes.

Obtention of graft copolymers by ionizing radiation, characterization and study of hemo-compatible properties; Obtencao de copolimeros de enxerto via radiacao ionizante, caracterizacao e estudo de suas propriedades hemocompativeis

Energy Technology Data Exchange (ETDEWEB)

Queiroz, A A.A. de

1994-12-31

The present work had as objectives the obtention and characterization of grafting copolymers by radiation induced polymerization and the study of its hemo compatible properties. The relationship between grafting conditions and anti-trombogenicity was examined for the purpose of clearing the necessity of controlling grafting conditions to enhance the copolymers blood compatibility. Two methods were chosen to accomplish the irradiation: mutual and pre-irradiation (peroxidation) of the films in {sup 6O} Co source and electron beam accelerator. Primarily grafting parameters were studied in the systems of the monomers N, N-dimethyl acrylamide (DMAA) and acrylic acid (AA) with the polymeric films: poly (tetrafluoroethylene) (PTFE), poly (ethylene-co-tetrafluoroethylene) (PETFE), low density polyethylene (LDPE) and poly (vinyl chloride) (PVC). The simultaneous irradiation was effective in the polymerization of all the substrates above mentioned, although the peroxidation method has given better results for PETFE-DMAA, LDPE-g-DMAA, LDPE-g-AA and PVC-g-AA. In the system AA/LDPE and AA/PVC the homo polymerization was controlled by the addition of the comonomer N, N-dimethyl acrylic acid (DMA). As for the grafting parameters, low dose rate and low irradiation dose, showed to be very effective for the graftability of DMAA and AA on the substrates. (author). 129 refs, 51 figs, 7 tabs.

Obtention of graft copolymers by ionizing radiation, characterization and study of hemo-compatible properties

International Nuclear Information System (INIS)

Queiroz, A.A.A. de.

1993-01-01

The present work had as objectives the obtention and characterization of grafting copolymers by radiation induced polymerization and the study of its hemo compatible properties. The relationship between grafting conditions and anti-trombogenicity was examined for the purpose of clearing the necessity of controlling grafting conditions to enhance the copolymers blood compatibility. Two methods were chosen to accomplish the irradiation: mutual and pre-irradiation (peroxidation) of the films in 6O Co source and electron beam accelerator. Primarily grafting parameters were studied in the systems of the monomers N, N-dimethyl acrylamide (DMAA) and acrylic acid (AA) with the polymeric films: poly (tetrafluoroethylene) (PTFE), poly (ethylene-co-tetrafluoroethylene) (PETFE), low density polyethylene (LDPE) and poly (vinyl chloride) (PVC). The simultaneous irradiation was effective in the polymerization of all the substrates above mentioned, although the peroxidation method has given better results for PETFE-DMAA, LDPE-g-DMAA, LDPE-g-AA and PVC-g-AA. In the system AA/LDPE and AA/PVC the homo polymerization was controlled by the addition of the comonomer N, N-dimethyl acrylic acid (DMA). As for the grafting parameters, low dose rate and low irradiation dose, showed to be very effective for the graftability of DMAA and AA on the substrates. (author). 129 refs, 51 figs, 7 tabs

Post-harvest conservation of camu–camu fruits (Myrciaria dubia (Kunth Mc Vaugh using different temperatures and packages

Directory of Open Access Journals (Sweden)

Maria Luiza GRIGIO

2015-12-01

Full Text Available Abstract The camu-camu tree (Myrciaria dubia (Kunth Mc Vaugh is fruit-bearing tree belonging to the family Myrtaceae. This work was conducted with the purpose of evaluating the type of storage temperature and package which allow better conservation of the quality attributes of camu-camu. The experimental design utilized was the completely randomized with three replications in a factorial arrangement (3x3x8, constituted of three different storage temperatures (laboratory ambiente or 25 ± 2 °C, 15 °C and 20 °C, three types of packages (no package, PET and PVC and fourteen days’ storage, the fruits being analyzed every two days. The fruits were evaluated as to fresh mass loss, pH, soluble solids contents, titrable acidity, ascorbic acid, carotenoids, anthocyanins, chlorophylls A and B and maturation index (SS/AT. According to the results obtained, the quality attributes and ascorbic acid content were conserved for longer time in the fruits stored on PVC-film covered expanded polystyrene trays at 15 °C. It follows that the best temperature for the storage of camu-camu is 15 °C and the package that best keeps its quality attributes is the PVC-film covered expanded polystyrene tray.

Kinetic Migration of Diethylhexyl Phthalate in Functional PVC Films

International Nuclear Information System (INIS)

Fei Fei; Liu Zhongwei; Chen Qiang; Liu Fuping

2012-01-01

Plasticizers that are generally used in plastics to produce flexible food packaging materials have proved to cause reproductive system problems and women's infertility. A long-term consumption may even cause cancer diseases. Hence a nano-scale layer, named as functional barrier layer, was deposited on the plastic surface to prevent plasticizer diethylhexyl phthalate's (DEHP) migration from plastics to foods. The feasibility of functional barrier layer i.e. SiO x coating through plasma enhanced chemical vapor deposition (PECVD) process was then described in this paper. We used Fourier transform infrared spectroscopy (FTIR) to analyze the chemical composition of coatings, scanning electron microscope (SEM) to explore the topography of the coating surfaces, surface profilemeter to measure thickness of coatings, and high-performance liquid chromatography (HPLC) to evaluate the barrier properties of coatings. The results have clearly shown that the coatings can perfectly block the migration of the DEHP from plastics to their containers. It is also concluded that process parameters significantly influence the block efficiency of the coatings. When the deposition conditions of SiO x coatings were optimized, i.e. 50 W of the discharge power, 4:1 of ratio of O 2 : HMDSO, and ca.100 nm thickness of SiO x , 71.2% of the DEHP was effectively blocked.

Kinetic Migration of Diethylhexyl Phthalate in Functional PVC Films

Science.gov (United States)

Fei, Fei; Liu, Zhongwei; Chen, Qiang; Liu, Fuping

2012-02-01

Plasticizers that are generally used in plastics to produce flexible food packaging materials have proved to cause reproductive system problems and women's infertility. A long-term consumption may even cause cancer diseases. Hence a nano-scale layer, named as functional barrier layer, was deposited on the plastic surface to prevent plasticizer diethylhexyl phthalate's (DEHP) migration from plastics to foods. The feasibility of functional barrier layer i.e. SiOx coating through plasma enhanced chemical vapor deposition (PECVD) process was then described in this paper. We used Fourier transform infrared spectroscopy (FTIR) to analyze the chemical composition of coatings, scanning electron microscope (SEM) to explore the topography of the coating surfaces, surface profilemeter to measure thickness of coatings, and high-performance liquid chromatography (HPLC) to evaluate the barrier properties of coatings. The results have clearly shown that the coatings can perfectly block the migration of the DEHP from plastics to their containers. It is also concluded that process parameters significantly influence the block efficiency of the coatings. When the deposition conditions of SiOx coatings were optimized, i.e. 50 W of the discharge power, 4:1 of ratio of O2: HMDSO, and ca.100 nm thickness of SiOx, 71.2% of the DEHP was effectively blocked.

Evaluación de las Propiedades Mecánicas de una Mezcla Densa en Caliente Modificada con un Desecho de PVC

Directory of Open Access Journals (Sweden)

Hugo A. Rondón-Quintana

2011-12-01

Full Text Available El presente trabajo evaluó en laboratorio, la resistencia mecánica bajo carga monotónica, el módulo resiliente y la resistencia a la deformación permanente que experimenta una mezcla asfáltica cuando se modifica con un desecho de policloruro de vinilo (PVC por vía húmeda. Adicionalmente, fue evaluada durante 21 meses, la influencia del medio ambiente de la ciudad de Bogotá D.C. sobre las propiedades mecánicas de la mezcla modificada. De los resultados obtenidos se concluye que la resistencia mecánica de la mezcla asfáltica modificada es superior en comparación con la convencional. La tendencia general de las mezclas con el tiempo de exposición al medio ambiente de Bogotá D.C. es experimentar un aumento en los valores de rigidez debido principalmente a procesos de endurecimiento por envejecimiento del ligante asfáltico. Sin embargo, para el caso de las mezclas fabricadas con CA 60-70 y modificadas con PVC en los primeros 15 meses de exposición, la rigidez disminuye por efecto de micro-fisuración térmica.

Monitoramento in situ e em tempo real de variáveis morfológicas do poli(cloreto de vinila usando espectroscopia NIR Monitoring in situ and in real time the morphological variables of pvc using NIR spectroscopy

Directory of Open Access Journals (Sweden)

João M. de Faria Jr.

2009-06-01

Full Text Available Este trabalho ilustra o uso de espectroscopia do infravermelho próximo (NIRS para fins de monitoramento da polimerização em suspensão de cloreto de vinila em tempo real. Resultados inéditos mostraram que é possível acompanhar a evolução de importantes propriedades morfológicas de resinas de PVC [poli(cloreto de vinila], como por exemplo, BD (densidade aparente, CPA (absorção de plastificante a frio, DTP (distribuição de tamanho de partículas e Dp (diâmetro de partícula. Mostrou-se também, pela primeira vez, que é possível analisar quantitativamente, com o auxílio da sonda NIRS in situ, a estrutura morfológica da partícula de PVC. Com a possibilidade de predizer a evolução dinâmica dos parâmetros morfológicos em tempo real, mostrou-se que é possível injetar dispersantes e variar a velocidade de agitação durante a reação para fins de controle das variáveis BD, CPA e DTP do PVC, até que o ponto de identificação da partícula seja atingido. Por meio do monitoramento e da estratégia de controle proposta, é possível antecipar fugas de temperatura no reator, aumentar a segurança do processo, diminuir o tempo de desenvolvimento de resinas com características morfológicas diferenciadas, evitando perdas de margem oriundas da venda de produtos fora de especificação, e otimizar os recursos para o desenvolvimento de novos produtos.This work illustrates the use of near infrared spectroscopy (NIRS for monitoring of the suspension polymerization of vinyl chloride in real time. Obtained results showed that it is possible to track in situ and in real time important morphological properties of PVC resins, such as BD (bulk density, CPA (cold plasticizer absorption, PSD (particle size distribution and Dp (average particle diameter. It was also shown for the first time that it is possible to analyze quantitatively, with the help of in situ NIRS probe, the morphological structure of the PVC particles. As a consequence, it

Preparation of anion exchange membrane using polyvinyl chloride (PVC) for alkaline water electrolysis

Energy Technology Data Exchange (ETDEWEB)

Hwang, Gab-Jin; Bong, Soo-Yeon; Ryu, Cheol-Hwi [Hoseo University, Asan (Korea, Republic of); Lim, Soo-Gon [Energy and Machinery Korea Co., Ltd., Changwon (Korea, Republic of); Choi, Ho-Sang [Kyungil University, Gyeongsan (Korea, Republic of)

2015-09-15

An anion exchange membrane was prepared by the chloromethylation and the amination of polyvinyl chloride (PVC), as the base polymer. The membrane properties of the prepared anion exchange membrane, including ionic conductivity, ion exchange capacity, and water content were measured. The ionic conductivity of the prepared anion exchange membrane was in the range of 0.098x10{sup -2} -7.0x10{sup -2}S cm{sup -1}. The ranges of ion exchange capacity and water content were 1.9-3.7meq./g-dry-membrane and 35.1-63.1%, respectively. The chemical stability of the prepared anion exchange membrane was tested by soaking in 30 wt% KOH solution to determine its availability as a separator in the alkaline water electrolysis. The ionic conductivity during the chemical stability test largely did not change.

COMPORTAMIENTO DE UNA MEZCLA DENSA DE ASFALTO EN CALIENTE MODIFICADA CON DESECHO DE POLICLORURO DE VINILO (PVC

Directory of Open Access Journals (Sweden)

Hugo Alexander Rondón Quintana

2008-01-01

Full Text Available En el mundo la tecnología de los asfaltos modificados ha sido una técnicaampliamente utilizada para mejorar las características que presentan las mezclasasfálticas convencionales cuando experimentan niveles elevados de tránsito ygradientes de temperatura. Por lo general lo que se busca con este tipo detecnología es mejorar algunas de las propiedades mecánicas y reológicas de losasfaltos y las mezclas asfálticas convencionales tales como la susceptibilidad térmica, la rigidez, y la resistencia al envejecimiento, a las deformaciones plásticas ya la fatiga. El artículo presenta los resultados experimentales de ensayar una mezcla asfáltica densa en caliente modificada con desecho de policloruro de vinilo (el cual se denominará en el presente trabajo PVC. Para la evaluación del comportamiento de las mezclas asfálticas convencionales y modificadas se realizaron ensayos Marshall, módulo dinámico y deformación permanente. Para el cemento asfáltico (CA con y sin aditivo se realizaron ensayos de caracterización de asfaltos como penetración, punto de ablandamiento y viscosidad. La modificación de las mezclas se realizó por vía húmeda y seca. Adicionando desecho de PVC al cemento asfáltico y a las mezclas, se obtiene un material más rígido con mayor resistencia a la penetración y menor susceptibilidad térmica a fluir.

Preparation and characterization of a magneto-polymeric nanocomposite: Fe 3O 4 nanoparticles in a grafted, cross-linked and plasticized poly(vinyl chloride) matrix

Science.gov (United States)

Rodríguez-Fernández, Oliverio S.; Rodríguez-Calzadíaz, C. A.; Yáñez-Flores, Isaura G.; Montemayor, Sagrario M.

In this work two kind of materials: (1) grafted, cross-linked and plasticized poly(vinyl chloride) (PVC) "plastic films" and (2) magnetic plastic films "magneto-polymeric nanocomposites" were prepared. Precursor solutions or "plastisols" used to obtain the plastic films were obtained by mixing PVC (emulsion grade) as polymeric matrix, di(2-ethylhexyl)phthalate (DOP) as plasticizer, a thermal stabilizer based in Ca/Zn salts, and a cross-linking agent, 3-mercaptopropyltrimethoxysilane (MTMS) or 3-aminopropyltriethoxysilane (ATES), at several concentrations. Flexible films were obtained from the plastisols using static casting. The stress-strain behavior and the gel content (determined by Soxhlet extraction with boiling THF) of the flexible films were measured in order to evaluate the effect of the cross-linking agent and their content on the degree of cross-linking. The magneto-polymeric nanocomposites were obtained by mixing the optimum composition of the plastisols (analyzed previously) with magnetite (Fe 3O 4)-based ferrofluid and DOP. Later, flexible films were obtained by static casting of the plastisol/ferrofluid systems. The magnetic films were characterized by the above-mentioned techniques and X-ray diffraction, vibrating sample magnetometry and thermogravimetrical analysis.

Preparation and electrical-property characterization of poly(vinyl chloride)-derived carbon nanosheet by ion beam irradiation-induced carbon clustering and carbonization

Science.gov (United States)

Jung, Chan-Hee; Sohn, Joon-Yong; Kim, Hyo-Sub; Hwang, In-Tae; Lee, Hong-Joon; Shin, Junhwa; Choi, Jae-Hak

2018-05-01

In this work, we demonstrated that carbon nanosheet (CNS) can easily be produced by a room-temperature, solid-state proton irradiation-induced clustering of poly(vinyl chloride) (PVC) films followed by carbonization. The results of the optical, chemical, and structural analyses revealed that oxidized and sp2-hybridized carbon clusters were effectively created in the PVC thin film by combined dehydrochlorination and inter-coupling reactions during proton irradiation. This was further converted to pseudo-hexagonally-structured nano-crystalline CNS with 2-D symmetry and metallic transporting character by high-temperature treatment. As a result, the CNS exhibited a very high electrical conductivity (587 S/cm) without a significant change in their thickness, a low surface roughness (0.36 nm), and a high work function (5.11 eV). These findings demonstrate that the radiation-based approach opens new avenues for the design and development of 2-D CNS as a graphene allotrope for the application of electronic devices, including field-effect transistors, electric heating devices, biosensors, supercapacitors, and fuel cells.

Influence of film dimensions on film droplet formation.

Science.gov (United States)

Holmgren, Helene; Ljungström, Evert

2012-02-01

Aerosol particles may be generated from rupturing liquid films through a droplet formation mechanism. The present work was undertaken with the aim to throw some light on the influence of film dimensions on droplet formation with possible consequences for exhaled breath aerosol formation. The film droplet formation process was mimicked by using a purpose-built device, where fluid films were spanned across holes of known diameters. As the films burst, droplets were formed and the number and size distributions of the resulting droplets were determined. No general relation could be found between hole diameter and the number of droplets generated per unit surface area of fluid film. Averaged over all film sizes, a higher surface tension yielded higher concentrations of droplets. Surface tension did not influence the resulting droplet diameter, but it was found that smaller films generated smaller droplets. This study shows that small fluid films generate droplets as efficiently as large films, and that droplets may well be generated from films with diameters below 1 mm. This has implications for the formation of film droplets from reopening of closed airways because human terminal bronchioles are of similar dimensions. Thus, the results provide support for the earlier proposed mechanism where reopening of closed airways is one origin of exhaled particles.

Modification Of Poly(glycidyl Methacrylate) Grafted Onto Crosslinked Pvc With Tertiary Amine Group And Use For Removing Acidic Dyes From Water

OpenAIRE

Yorgun, Gülden

2009-01-01

In this study, glycidylmethacrylate is grafted onto partially dehydrochlorinated poly(vinyl chloride) (DHPVC) using ATRP method and polymerization kinetics of the reaction is studied. Then, the polymeric resin was interacted with excess of diethylamine, giving a tertiary amine containing sorbent. Surface initiated polymerizations have been widely used to overcome inadequate properties of poly(vinylchloride) (PVC). Epoxy group is one of the most important type to be integrated into polymers. T...

Investigation of film boiling thermal hydraulics under FCI conditions. Results of a numerical study

Energy Technology Data Exchange (ETDEWEB)

Dinh, T.N.; Dinh, A.T.; Nourgaliev, R.R.; Sehgal, B.R. [Div. of Nuclear Power Safety Royal Inst. of Tech. (RIT), Brinellvaegen 60, 10044 Stockholm (Sweden)

1998-01-01

Film boiling on the surface of a high-temperature melt jet or of a melt particle is one of key phenomena governing the physics of fuel-coolant interactions (FCIs) which may occur during the course of a severe accident in a light water reactor (LWR). A number of experimental and analytical studies have been performed, in the past, to address film boiling heat transfer and the accompanying hydrodynamic aspects. Most of the experiments have, however, been performed for temperature and heat flux conditions, which are significantly lower than the prototypic conditions. For ex-vessel FCIs, high liquid subcooling can significantly affect the FCI thermal hydraulics. Presently, there are large uncertainties in predicting natural-convection film boiling of subcooled liquids on high-temperature surfaces. In this paper, research conducted at the Division of Nuclear Power Safety, Royal Institute of Technology (RIT/NPS), Stockholm, concerning film-boiling thermal hydraulics under FCI condition is presented. Notably, the focus is placed on the effects of (1) water subcooling, (2) high-temperature steam properties, (3) the radiation heat transfer and (4) mixing zone boiling dynamics, on the vapor film characteristics. Numerical investigations are performed using a novel CFD modeling concept named as the local-homogeneous-slip model (LHSM). Results of the analytical and numerical studies are discussed with respect to boiling dynamics under FCI conditions. (author)

Effects of gamma radiation and packaging on conservation of toyonoka strawberries stored under refrigeration.; Efeito da radiacao gama e embalagem na conservacao de morangos 'toyonoka' armazenados sob refrigeracao

Energy Technology Data Exchange (ETDEWEB)

Domingues, Danielle Marinelli

2000-07-01

Strawberries have short post harvest life due to the rapid spoilage caused by fungal infections, even when stored under refrigeration. The effects of gamma radiation (0.0, 1.5, 2.0 and 2.5 kGy) and two kinds of packages (plastic boxes with or without PVC film wrapping) were evaluated using Toyonoka strawberries kept under refrigeration (3 to 6 deg C and relative humidity of 55%) for 1, 8, 15 and 22 days after irradiation, applied 1 day after harvesting. Deterioration progression and loss of weight occurred in the course of storage and although the content of ascorbic acid had also increased, total titratable acidity, p H and ratio remained constant during all the experimental period, independent of the samples treatments. The use of PVC film packing inhibited dehydration of the strawberries along the storage and also caused reduction in soluble solid content of the fruits stored for more than 8 days. The treatments with 2.0 and 2.5 kGy had caused significant losses of ascorbic acid the higher dose also significantly reduced the texture of the fruits. Sensorial analysis has been performed with 30 untrained judges to evaluate the acceptability of strawberries packed without the PVC wrapping and irradiated with doses of 0.0, 1.5 or 2.0 kGy. No irradiation effects were observed and the samples were acceptable with no significant difference between samples stored for 1 or 8 days after irradiation. PVC film packaging and irradiation were not efficient in delaying post harvest decay of Toyonoka strawberries in the conditions used in these experiments. (author)

Effects of gamma radiation and packaging on conservation of toyonoka strawberries stored under refrigeration

International Nuclear Information System (INIS)

Domingues, Danielle Marinelli

2000-01-01

Strawberries have short post harvest life due to the rapid spoilage caused by fungal infections, even when stored under refrigeration. The effects of gamma radiation (0.0, 1.5, 2.0 and 2.5 kGy) and two kinds of packages (plastic boxes with or without PVC film wrapping) were evaluated using Toyonoka strawberries kept under refrigeration (3 to 6 deg C and relative humidity of 55%) for 1, 8, 15 and 22 days after irradiation, applied 1 day after harvesting. Deterioration progression and loss of weight occurred in the course of storage and although the content of ascorbic acid had also increased, total titratable acidity, p H and ratio remained constant during all the experimental period, independent of the samples treatments. The use of PVC film packing inhibited dehydration of the strawberries along the storage and also caused reduction in soluble solid content of the fruits stored for more than 8 days. The treatments with 2.0 and 2.5 kGy had caused significant losses of ascorbic acid the higher dose also significantly reduced the texture of the fruits. Sensorial analysis has been performed with 30 untrained judges to evaluate the acceptability of strawberries packed without the PVC wrapping and irradiated with doses of 0.0, 1.5 or 2.0 kGy. No irradiation effects were observed and the samples were acceptable with no significant difference between samples stored for 1 or 8 days after irradiation. PVC film packaging and irradiation were not efficient in delaying post harvest decay of Toyonoka strawberries in the conditions used in these experiments. (author)

Failure Analysis of the HCl Column Inter Cooler Cause, Effect, Results and Economical Solution for Severe Media Case Study

International Nuclear Information System (INIS)

Zaher, A.

2004-01-01

The Egyptian Petrochemicals Co. (EPC) is located at Alexandria- Egypt, it is considered as one of the most important plants in the middle east, it consists of the following plants: PVC plant with possible expansions, VCM Plant, Cl 2 Chlorine and NaOH Caustic Soda Plant, PVC Compounding plant, Power Plant, and Utility plant. (EPC) had been established since 1987 for the production of the products (PVC Resin, PVC Compounding, Chlorine Liquid, Caustic Soda Flaks, 50% Liquid Concentration, HCl Acid 30% Concentration, and sodium hypochlorite 12%) these materials are supplied to the local market, and Exported to the European and Arabic Countries

EMBALAGEM INDIVIDUAL DE MANGAS CV. TOMMY ATKINS EM FILME PLÁSTICO: EFEITO SOBRE A VIDA DE PRATELEIRA INDIVIDUAL PACKAGING OF MANGOS CV. TOMMY ATKINS IN PLASTIC FILM: EFFECT ON SHELF LIFE

Directory of Open Access Journals (Sweden)

FÁBIO YAMASHITA

2001-08-01

Full Text Available Estudou-se o efeito da embalagem de policloreto de vinila (PVC sobre a vida de prateleira de mangas cv. Tommy Atkins armazenadas sob refrigeração. Mangas no estádio de maturidade fisiológica, com casca verde ou levemente avermelhada, foram embaladas individualmente, com filme de 10mm de espessura, e armazenadas por 28 dias a 12ºC (80-90% UR. Frutos sem embalagem serviram de controle. Durante o período de armazenagem, foram feitas avaliações sensoriais utilizando o método de escala hedônica não estruturada para aceitação da aparência e do sabor, utilizando-se de 30 provadores não treinados por sessão. Determinou-se também a perda de massa, a acidez titulável e os teores de sólidos solúveis e vitamina C ao longo da armazenagem. As mangas embaladas apresentaram uma vida de prateleira de 21 dias contra 6 dias das não embaladas, e uma taxa de perda de massa 3,5 vezes menor que as não embaladas. Em relação à taxa de degradação de vitamina C, não houve diferença entre os tratamentos. A combinação da embalagem com a armazenagem a 12ºC aumentou a vida de prateleira do produto pela redução da atividade metabólica e do desenvolvimento de podridão.Effects of packaging in polyvinyl chloride (PVC film on postharvest shelf-life of mango cv. Tommy Atkins stored under refrigeration were studied. Mangos at mature green color stage were individually sealed in 10mm thick film and stored for 28 days at 12ºC (80-90% RH. Non-sealed fruits served as control. During the storage period, sensory evaluation was carried out using an unstructured hedonic scale for overall acceptance of appearance and flavor, with 30 untrained assessors per session. Mangos were also analyzed for weight loss, titratable acidity, total soluble solids and vitamin C during storage time. The packed mangos had a shelf life of 21 days against 6 days of the control ones, and weight loss rates 3.5 times smaller than the control ones. There was no difference in

Application results of a prototype ultrasonic liquid film sensor to a 7 MPa steam-water two-phase flow experiment

International Nuclear Information System (INIS)

Aoyama, Goro; Fujimoto, Kiyoshi; Katono, Kenichi; Nagayoshi, Takuji; Baba, Atsushi; Yasuda, Kenichi

2016-01-01

A prototype ultrasonic liquid film sensor was applied to a high-temperature steam-water two-phase flow experiment. The liquid film sensor was vertically installed in a loop which was connected to HUSTLE, a multi-purpose steam source test facility. The hydraulic diameter of the measurement section was 9.4 mm. The output waveforms of the sensor were acquired with a digital oscilloscope. The fluid temperature and system pressure were kept at 288°C and 7.2 MPa, respectively, during the experiment. The pulse-echo method was used to calculate the liquid film thickness. The cross-correlation calculation was utilized to determine the time difference between the pulse reflected at the sensor surface and the pulse reflected at the liquid film surface. The time-averaged liquid film thicknesses were less than 0.055 mm in the annular flow condition. The increase of the time-averaged thickness was small with the change of the gas momentum flux. The film thicknesses measured with the sensor were compared with the past experimental results; the former were smaller than one-fourth of the thickness estimated as the mean film thickness. The comparison results suggested that the continuous liquid sublayer thickness was measured with the liquid film sensor. (author)

Analysis of the thermal performance of a solar heating system using a collector with absorbing surface in plates coated with PVC; Analise do desempenho termico de um sistema de aquecimento solar utilizando coletor com superficie absorvedora em chapas de forro de PVC

Energy Technology Data Exchange (ETDEWEB)

Reis, Edmilson Pedreira dos

2009-08-15

It is presented a solar collector to be used in a system for heating bath water, whose main characteristic is its low cost. The collector consists of five plates of PVC with 10 mm thick, 200 mm wide and 1400 mm length, with ao area equal to 1,4 square meters. The plates were connected in parallel to the ends of PVC tubes of 40 mm diameter and 32 mm diameter. The plates were coated on one side with aluminum sheets of soft drinks and beers cans open. The system worked on a thermosyphon and was tested in two configurations: the plates uncoated and coated with aluminum material, to determine the influence of material on the efficiency of the collector. For both configurations was used EPS plates below the surface to minimize heat losses from the bottom. The thermal reservoir of the heating system is, also, alternative and of low cost, since it was constructed from a polyethylene tank for storing water, with volume of 150 end 200 liters. It will be presented the thermal efficiency, heat loss, water temperature of the thermal reservoir at the end of the process and simulation of baths for a house with four residents. It will be demonstrated the thermal, economic and material viability of the proposed collector, whose main innovation is the use of recyclable materials, cans of beer and soft drinks, to increase the temperature of the absorber plate. (author)

[Experimental Methods and Result Analysis of a Variety of Spectral Reflectance Properties of the Thin Oil Film].

Science.gov (United States)

Ye, Zhou; Liu, Li; Wei, Chuan-xin; Gu, Qun; An, Ping-ao; Zhao, Yue-jiao; Yin, Da-yi

2015-06-01

In order to analysis the oil spill situation based on the obtained data in airborne aerial work, it's needed to get the spectral reflectance characteristics of the oil film of different oils and thickness as support and to select the appropriate operating band. An experiment is set up to measure the reflectance spectroscopy from ultraviolet to near-infrared for the film of five target samples, which means petrol, diesel, lubricating oil, kerosene and fossil, using spectral measurement device. The result is compared with the reflectance spectra of water in the same experimental environment, which shows that the spectral reflection characteristics of the oil film are related to the thickness and the type of the oil film. In case of the same thickness, the spectral reflectance curve of different types of film is far different, and for the same type of film, the spectral reflectance curve changes accordingly with the change of film thickness, therefore in terms of the single film, different film thickness can be distinguished by reflectance curves. It also shows that in terms of the same film thickness, the reflectance of diesel, kerosene, lubricants reaches peak around 380 nm wavelength, obviously different from the reflectance of water, and that the reflectance of crude oil is far less than that of water in more than 340 nm wavelength, and the obtained reflection spectrum can be used to distinguish between different types of oil film to some extent. The experiment covers main types of spilled oil, with data comprehensively covering commonly used detect spectral bands, and quantitative description of the spectral reflectance properties of film. It provides comprehensive theoretical and data support for the selection of airborne oil spill detection working band and the detection and analysis of water-surface oil spill.

Solid state self-healing system: Effects of using PDGEBA, PVC and PVA as linear healing agents

Science.gov (United States)

Muhamad, Noor Nabilah; Jamil, Mohd. Suzeren Md.; Abdullah, Shahrum

2014-09-01

The solid state self-healing system was obtained by employing a thermosetting epoxy resin, into which a thermoplastic is dissolved. In this study, the effect of healing efficiency was investigated by using different thermoplastic polymers which are poly(bisphenol-A-co-epichlorohydrin), polyvinyl chloride and polyvinyl alcohol as healing agents. Healing was achieved by heating the fractured resins to a specific temperature i.e. above their glass transition temperature (Tg) which obtained from dynamic mechanical analysis (DMA) to mobilize the polymeric chains of the healing agent. The curing reaction in the epoxy resins were characterized by means of Fourier transform infrared spectroscopy (FTIR). Izod impact test was been performed to demonstrate self-healing of the different specimens. Under test, it was found that healable resin with PDGEBA has highest healing efficiency followed by PVC and PVA, with 63%, 35% and 18% of average percentage healing efficiencies respectively. These results are due to the different solubility parameters of the thermoset/network and thermoplastic polymer which led to the phase separation. Morphological studies prove the fracture-healing process and morphological properties of the resins.

Stabilization of gamma-irradiated poly(vinyl chloride) by epoxy compounds. III. Conjugated double bonds and degree of unsaturation in gamma-irradiated PVC-stabilizer mixtures

International Nuclear Information System (INIS)

Lerke, G.; Lerke, I.; Szymanski, W.

1983-01-01

The concentration of conjugated polyene sequences was studied in γ-irradiated PVC with 4% admixture of four epoxy stabilizers: diglycidyl ether of 2,2-bis(4-hydroxy-3-methylphenyl)propane (I), styrene oxide (1,2-epoxy ethyl benzene) (IV), epoxidized ricinus oil (VI), and epoxidized soybean oil (Drapex 6.8) (VII). As in the former investigations (Papers I and II), the process of the formation of the polyenes occurs in two stages. The concentration of polyene sequences with n double bonds, H/sub n/ the total amount of polyene sequences, ΣH/sub n/, the average length of the polyene sequence, n, and the extents of reaction x and p, were computed. The stabilizing effect of all compounds used agrees with the increasing content of epoxy groups. The addition of stabilizers diminishes the value of n. The decrease of the fraction of long sequences and the increase of short ones occurs. Apart from the binding of evolved HCl, the protective effect towards the macromolecules of PVC consists mainly in the inhibition of growth of chain dehydrochlorination by the epoxy groups

New results in pulsed laser deposition of poly-methyl-methacrylate thin films

International Nuclear Information System (INIS)

Cristescu, R.; Socol, G.; Mihailescu, I.N.; Popescu, M.; Sava, F.; Ion, E.; Morosanu, C.O.; Stamatin, I.

2003-01-01

Thin organic films based on poly-methyl-methacrylate (PMMA) polymer have been obtained by pulsed laser deposition (PLD) on silicon substrates. The films were characterized by X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), atomic force microscopy (AFM) and Raman spectroscopy (RS). We observed that the film composition and structure depend on the laser fluence and on the temperature of the substrate during deposition

Film quality in film mammography. Pt. 2

International Nuclear Information System (INIS)

Friedrich, M.; Weskamp, P.; Freie Univ. Berlin

1976-01-01

During consideration of three film mammographic systems, the concept of signal/noise ratio is developed as a quantitative measure of film quality. The ability to recognise detail related to detail size, film blackening and exposure geometry was studied for various systems, and the quality profiles are discussed. There is a considerable difference in quality between industrial films without screens and film-screen combinations; however, exposure geometry during mammography has a considerable effect which tends to reduce the difference. Consequently, detail sizes of 200 μ to 1,000 μ (including the majority of mammographic micro-calcifications) are shown about equally well. Contrast for the lo-dose system is somewhat less than for adequately exposed industrial film. Over-exposure with the lo-dose system, contrary to industrial film, rapidly leads to unsatisfactory results. On the other hand it is often not possible to obtain an adequate exposure when using industrial film. For these reasons it is often an advantage to examine large breasts and the dense breasts of young women with a film-screen combination which requires approximately one eighth of the dose necessary for industrial film. For small or easily compressable breasts best results are obtained, using an adequate exposure by employing industril film; radiation dose it then acceptable. (orig./ORU) [de

Characterization of the surface physico-chemistry of plasticized PVC used in blood bag and infusion tubing.

Science.gov (United States)

Al Salloum, H; Saunier, J; Dazzi, A; Vigneron, J; Etcheberry, A; Marlière, C; Aymes-Chodur, C; Herry, J M; Bernard, M; Jubeli, E; Yagoubi, N

2017-06-01

Commercial infusion tubing and blood storage devices (tubing, blood and platelets bags) made of plasticized PVC were analyzed by spectroscopic, chromatographic and microscopic techniques in order to identify and quantify the additives added to the polymer (lubricants, thermal stabilizers, plasticizers) and to put into evidence their blooming onto the surface of the devices. For all the samples, deposits were observed on the surface but with different kinds of morphologies. Ethylene bis amide lubricant and metallic stearate stabilizers were implicated in the formation of these layers. In contact with aqueous media, these insoluble deposits were damaged, suggesting a possible particulate contamination of the infused solutions. Copyright © 2017 Elsevier B.V. All rights reserved.

Fracture Characterization of PVC Foam Core Sandwich Specimen Using the DCB-UBM Test Method

DEFF Research Database (Denmark)

Saseendran, Vishnu; Berggreen, Christian; Carlsson, Leif A.

coupled with experimental validation is paramount to determine the fracture resistance of the face/core interface. In this paper, the test-rig exploiting the double cantilever beam with uneven bending moments (DCB-UBM) concept is used to determine the fracture toughness of PVC foam core sandwich......Face/core debond failure in sandwich composites is a critical failure mode. Lack of cohesion between face and core will lead to loss of structural integrity. The estimation of interface fracture toughness especially at the face/core interface is extremely challenging, provided the dissimilarity...... composites. The DCB-UBM test enables fracture testing over a large range of mode-mixities as expressed by a phase angle (ψ) which is a measure of the amount of shear loading at the crack tip. A desired phase angle may be achieved by changing the moment-ratio (MR = Md/Ms)....

Study of the degradation of the insulation of HV cables with PVC insulation

International Nuclear Information System (INIS)

Quennehen, Pierre

2014-01-01

The observed decrease in the resistivity of the PVC insulation of some high voltage unipolar cables led to question their ability to perform their function. Provide answers concerning in particular the origin of the variation in resistivity and the impact on the dielectric strength were the objectives of this study. The characterizations were carried on cables withdrawn from service whose properties had changed during their use. Physico-chemical characterization (IR microscopy, UV spectroscopy, SEM - EDX and coulometry) showed that aging of the cable resulted from a mechanism of dehydro-chlorination. The presence of two modes of electric conduction in the material was observed: electronic conduction at a low temperature (≤ -10 C) and ionic conduction at room temperature and beyond. The presence of these two modes of conduction is consistent with the mechanism of dehydro-chlorination. In contrast to an Arrhenius law, artificial aging showed a threshold effect in the thermal activation of the mechanism at the origin of the resistivity drop. The dielectric strength of the cable has been confirmed by tests at voltages or temperatures well beyond the nominal values. Measurements of differential scanning calorimetry (DSC) showed occasional more or less pronounced over-heatings that correlate with the resistivity drops, and can therefore be considered as being at the origin of the observed evolutions. (author)

Beam in on curing

International Nuclear Information System (INIS)

Holl, Dr.

1981-01-01

This third part of an article on the electron beam curing of paints covers the following aspects: inertising equipment; working without inert gas; increase in temperature when irradiating; irradiating plants; laboratory plants; plant operating from coil to coil; plant for shaped parts; possible applications; decorative films, paper, PVC; packaging material; metallisation of paper films; film bonding; strengthening of flock; coating; pressure sensitive adhesives. (U.K.)

Studies of LENRA-Toughened PVC non-woven membranes prepared by electro spinning technique

International Nuclear Information System (INIS)

Dahlan Mohd; Mahathir Mohamed; Khirul Hafiz mohd Yusof

2010-01-01

Lately research in use of so-called green chemicals draws strong interest from research community due to the climate change issues. Malaysia is in strong position to take this advantage because we are among the world biggest producers of natural rubber and palm oil - the two sources of important green renewable chemical feedstock in the near future. For the last couple of years we have shown how modified natural rubbers especially liquid natural rubber and its derivatives such as liquid epoxidized natural rubber acrylate (LENRA) could be used in various applications via among others sol-gel technique and radiation curing technology. This time around we will show another application on how non-woven membranes made from PVC can be prepared by electro spinning technique using radiation curable LENRA as toughener. The electro spinning technique has great potential in producing nano fiber materials to be used in various applications to ensure sustainable energy and environments for the future. (author)

Ion implantation as a method of studying inhomogeneities in superconductors: results for indium films with embedded helium particles

International Nuclear Information System (INIS)

Fogel, N.Ya.; Moshenski, A.A.; Dmitrenko, I.M.

1978-01-01

The paper considers the applicability of ion implantation into superconductors to investigate inhomogeneity effects on their macroscopic properties. Noble-gas-ion implantation into thin superconducting films is shown to be a unique means of systematically studying these effects in a single sample. Data demonstrating the effect of inhomogeneities on the critical current, Isub(c) in the mixed state and phase-transition smearing in He + -ion-irradiated indium films are presented. First, experimental evidence was obtained to support the Larkin-Ovchinnikov theory which relates Isub(c) and the phase-transition smearing to inhomogeneities of the electron-electron interaction constant g(r) and the electron mean free path (r). Results are presented for parallel critical field anomalies in He-implanted indium films which are due to an implantation-induced anisotropy of xi(t). Changes in the critical parameters for the film resulting from the implantation are compared to structural changes. (Auth.)

Long-Term Performance of the Laguna de Barlovento Reservoir Water-Proofing using a PVC-P Geo membrane; Impermeabilizacion de la balsa de la Laguna de Barlovento con geomembrana de PVC-P: evolucion a lo largo del tiempo

Energy Technology Data Exchange (ETDEWEB)

Blanco Fernandez, M.; Leiro Lopez, A.; Soriano Carrillo, J.; Crespo Mucientes, M.; Zornberg, J.; Aguilar Gonzalez, E.; Rico Arnaiz, G.; Pargada Iglesias, L.

2014-02-01

The Laguna de Barlovento reservoir was one of the most important European hydraulic projects at the time of its construction because of its high capacity and challenging location. At the time, the designers decided to waterproof this reservoirs with a geo membrane of plasticized polyvinyl chloride (PVC-P). This paper documents the initial characteristics of the geo membrane and its performance since its installation until 2010. The material characterization includes a comprehensive testing program, the results of which are presented. They include quantification of the geo membrane thickness, amount and nature of plasticizers, tensile properties, fold ability under low temperatures, dynamic impact resistance, puncture resistance, welding strength (both in the manufacturing facility and in the field), as well as the use of techniques involving optical and scanning electron microscopy. In addition, advanced analytical techniques, such as Fourier Transform Infrared Spectroscopy (FTIR), Gas Chromatography (GC) and Mass spectrometry (MS), were used in order to identify the plasticizers used in the geo membrane formulation. Fold ability tests were found to provide early indication of degradation. Results from reflection optical and electron scanning microscopy showed that, after 19 nineteen years of installation, the geo membrane remains in good conditions, particularly on the non-exposed side. (Author)

Amorphous-tetrahedral diamondlike carbon layered structures resulting from film growth energetics

Science.gov (United States)

Siegal, M. P.; Barbour, J. C.; Provencio, P. N.; Tallant, D. R.; Friedmann, T. A.

1998-08-01

High-resolution transmission electron microscopy (HRTEM) shows that amorphous-tetrahedral diamondlike carbon (a-tC) films grown by pulsed-laser deposition on Si(100) consist of three-to-four layers, depending on the growth energetics. We estimate the density of each layer using both HRTEM image contrast and Rutherford backscattering spectrometry. The first carbon layer and final surface layer have relatively low density. The bulk of the film between these two layers has higher density. For films grown under the most energetic conditions, there exists a superdense a-tC layer between the interface and bulk layers. The density of all four layers, and the thickness of the surface and interfacial layers, correlate well with the energetics of the depositing carbon species.

Study of an X-ray fluorescence thin film method for the determination of uranium in low activity solutions; Estudio de un metodo de fluorescencia de rayos X en capa delgada para la determinacion del uranio en soluciones de baja actividad

Energy Technology Data Exchange (ETDEWEB)

Diaz-Guerra, J P

1980-07-01

The application of the X-ray fluorescence thin film technique to the uranium determination in nitric solutions for a concentration range from 1 g/l to 100 g/l and activity levels under 5 mCi/ml is studied. The most suited excitation and measurement conditions are also studied and the uranium matrix effect correction, which is performed through the double dilution, {alpha}{sub U}U interaction coefficient calculation and internal standard methods, is discussed. The specimen preparation is satisfactorily accomplished by using P.V.C. filters fixed on aluminium supports. (Author) 18 refs.

Experimental Investigation of Mechanical Properties of PVC Polymer under Different Heating and Cooling Conditions

Directory of Open Access Journals (Sweden)

Sarkawt Rostam

2016-01-01

Full Text Available Due to a widely increasing usage of polymers in various industrial applications, there should be a continuous need in doing research investigations for better understanding of their properties. These applications require the usage of the polymer in different working environments subjecting the material to various temperature ranges. In this paper, an experimental investigation of mechanical properties of polyvinyl chloride (PVC polymer under heating and cooling conditions is presented. For this purpose standard samples are prepared and tested in laboratory using universal material testing apparatus. The samples are tested under different conditions including the room temperature environment, cooling in a refrigerator, and heating at different heating temperatures. It is observed that the strength of the tested samples decreases with the increasing of heating temperature and accordingly the material becomes softer. Meanwhile the cooling environments give a clear increasing to the strength of the material.

Ground Based Experiments in Support of Microgravity Research Results-Vapor Growth of Organic Nonlinear Optical Thin Film

Science.gov (United States)

Zugrav, M. Ittu; Carswell, William E.; Haulenbeek, Glen B.; Wessling, Francis C.

2001-01-01

This work is specifically focused on explaining previous results obtained for the crystal growth of an organic material in a reduced gravity environment. On STS-59, in April 1994, two experiments were conducted with N,N-dimethyl-p-(2,2-dicyanovinyl) aniline (DCVA), a promising nonlinear optical (NLO) material. The space experiments were set to reproduce laboratory experiments that yielded small, bulk crystals of DCVA. The results of the flight experiment, however, were surprising. Rather than producing a bulk single crystal, the result was the production of two high quality, single crystalline thin films. This result was even more intriguing when it is considered that thin films are more desirable for NLO applications than are bulk single crystals. Repeated attempts on the ground to reproduce these results were fruitless. A second set of flight experiments was conducted on STS-69 in September 1995. This time eight DCVA experiments were flown, with each of seven experiments containing a slight change from the first reference experiment. The reference experiment was programmed with growth conditions identical to those of the STS-59 mission. The slight variations in each of the other seven were an attempt to understand what particular parameter was responsible for the preference of thin film growth over bulk crystal growth in microgravity. Once again the results were surprising. In all eight cases thin films were grown again, albeit with varying quality. So now we were faced with a phenomenon that not only takes place in microgravity, but also is very robust, resisting all attempts to force the growth of bulk single crystals.

Influence of both ion bombardment and chemical treatment processes on the electrical conductivity of PVC/poly aniline composites

International Nuclear Information System (INIS)

Gad, E.A.M.; Ashour, A.H.; Abdel-Hamid, H.M.; Sayed, W.M.

1999-01-01

In this article the changes in the electrical conductivity of PVC/poly aniline composites, as temperature consecutively increases, have been measured. The measurement were taken with correspondence to a control series of the composites under two processes:A. Composite samples bombarded with Ar + ions with fluence 2.44 x 10 13 beam ions /cm 2 ., sec 4 of 4 ke V beam energy where argon atoms can induce defects in the surface layer take place. Composite samples treated chemically with concentrated H 2 SO 4 as dopant which reacts with nitrogen atom in aniline. The measurements were also, done with the composites as the ratio of poly(aniline) stepped upward

Organic luminescent materials. First results on synthesis and characterization of Alq{sub 3} thin films

Energy Technology Data Exchange (ETDEWEB)

Baldacchini, G.; Gagliardi, S.; Montereali, R.M.; Pace, A. [ENEA, Centro Ricerche Frascati, Frascati, RM (Italy). Div. Fisica Applicata; Balaji Pode, R. [Nagpur University, Nagpur (India). Dept. of Physics

2000-07-01

Inorganic semiconductor diodes brought a technological revolution in the field of efficient light and laser sources in the last 20 years. New development in this field are expected from organic compounds, thanks to their low cost of synthesis and the relative easiness of growth as thin films. In particular, electrically pumped luminescent devices based on organic thin layers are among the most promising systems for next generation flat panel displays and semiconductor lasers. The tris - (8-hydroxy quinoline)-aluminium complex-Alq{sub 3} - is one of the most studied electro luminescent materials. In this paper, after a short introduction regarding historical development in the field, are reported preliminary results on the growth of Alq{sub 3} films and on their optical and spectroscopic characterization. [Italian] Negli ultimi 20 anni i diodi semiconduttori hanno portato una rivoluzione tecnologica nel campo delle sorgenti luminose e laser. Un nuovo sviluppo possibile in questo campo sono i composti organici, grazie al basso costo di sintesi e la relativa facilita' di crescerli in forma di film sottile. In particolare, dispositivi luminescenti pompati elettricamente basati su film sottili di materiali organici sono promettenti per una nuova generazione di display per schermi piatti e laser a Alq{sub 3} e' uno dei materiali elettroluminescenti piu' studiati. In questo rapporto, dopo una breve introduzione sullo sviluppo storico in questo campo, presentiamo i nostri primi risultati sulla crescita e caratterizzazione ottica di film di Alq{sub 3}.

Strontium PVC-membrane sensor based on 2-[(2-mercaptophenylimino)methyl]phenol

Energy Technology Data Exchange (ETDEWEB)

Zamani, Hassan Ali [Young Researchers Club, Quchan branch, Islamic Azad University, Quchan (Iran, Islamic Republic of)], E-mail: haszamani@yahoo.com; Ganjali, Mohammad Reza; Norouzi, Parviz [Center of Excellence in Electrochemistry, Faculty of Chemistry, University of Tehran, Tehran (Iran, Islamic Republic of); Endocrine and Metabolism Research Center, Tehran University of Medical Sciences, Tehran (Iran, Islamic Republic of); Adib, Mahdi [Center of Excellence in Electrochemistry, Faculty of Chemistry, University of Tehran, Tehran (Iran, Islamic Republic of)

2008-01-10

The 2-[(2-mercaptophenylimino)methyl]phenol (MPMP) was used as an excellent ionophore in the construction of a Sr{sup 2+} PVC-based membrane sensor. The best performance was obtained with a membrane composition of 30% poly(vinyl chloride), 62% nitrobenzen (NB), 5.5% MPMP and 2.5% sodium tetraphenyl borate (NaTBP). This sensor demonstrates a good selectivity and sensitivity towards the strontium ion for many cations, including alkali, alkaline earth, transition and heavy metal ions. The sensor revealed a great enhancement in selectivity coefficients for strontium ions in comparison with the previously reported strontium sensors. The proposed sensor exhibits a Nernstian behavior (with a slope of 29.6 {+-} 0.3 mV per decade) for the concentration range of (1.0 x 10{sup -6}-1.0 x 10{sup -1} M) with a detection limit of 5.5 x 10{sup -7} M (48.2 ng/mL). It illustrates a relatively fast response time in the whole concentration range (< 10 s) and it can be used for at least 10 weeks in a pH range of 2.8-9.6. The developed sensor was successfully used as an indicator electrode in the Sr(II) titration with EDTA and the Sr{sup 2+} ion recovery from binary mixtures.

76 FR 48122 - Polyethylene Terephthalate Film, Sheet, and Strip From Brazil: Preliminary Results of Antidumping...

Science.gov (United States)

2011-08-08

... on polyethylene terephthalate film, sheet, and strip (PET film) from Brazil. This administrative..., 2011. FOR FURTHER INFORMATION CONTACT: Deborah Scott or Robert James, AD/CVD Operations, Office 7... antidumping duty order on PET film from Brazil. See Polyethylene Terephthalate Film, Sheet, and Strip From...

Multi-directional radiation detector using photographic film

International Nuclear Information System (INIS)

Junet, L K; Majid, Z A Abdul; Sapuan, A H; Sayed, I S; Pauzi, N F

2014-01-01

Ionising radiation has always been part of our surrounding and people are continuously exposed to it. Ionising radiation is harmful to human health, thus it is vital to monitor the radiation. To monitor radiation, there are three main points that should be observed cautiously, which are energy, quantity, and direction of the radiation sources. A three dimensional (3D) dosimeter is an example of a radiation detector that provide these three main points. This dosimeter is able to record the radiation dose distribution in 3D. Applying the concept of dose detection distribution, study has been done to design a multi-directional radiation detector of different filter thicknesses. This is obtained by designing a cylinder shaped aluminum filter with several layers of different thickness. Black and white photographic material is used as a radiation-sensitive material and a PVC material has been used as the enclosure. The device is then exposed to a radiation source with different exposure factors. For exposure factor 70 kVp, 16 mAs; the results have shown that optical density (OD) value at 135° is 1.86 higher compared with an OD value at 315° which is 0.71 as the 135° area received more radiation compare to 315° region. Furthermore, with an evidence of different angle of film give different value of OD shows that this device has a multidirectional ability. Materials used to develop this device are widely available in the market, thus reducing the cost of development and making it suitable for commercialisation

Structural, microstructural and electrochemical properties of dispersed-type polymer nanocomposite films

Science.gov (United States)

Arya, Anil; Sharma, A. L.

2018-01-01

Free-standing solid polymer nanocomposite (PEO-PVC)  +  LiPF6-TiO2 films have been prepared through a standard solution-cast technique. The improvement in structural, microstructural and electrochemical properties has been observed on the dispersion of nanofiller in polymer salt complex. X-ray diffraction studies clearly reflect the formation of complex formation, as no corresponding salt peak appeared in the diffractograms. The Fourier transform infrared analysis suggested clear and convincing evidence of polymer-ion, ion-ion and polymer-ion-nanofiller interaction. The highest ionic conductivity of the prepared solid polymer electrolyte (SPE) films is ~5  ×  10-5 S cm-1 for 7 wt.% TiO2. The linear sweep voltammetry provides the electrochemical stability window of the prepared SPE films, about ~3.5 V. The ion transference number has been estimated, t ion  =  0.99 through the DC polarization technique. Dielectric spectroscopic studies were performed to understand the ion transport process in polymer electrolytes. All solid polymer electrolytes possess good thermal stability up to 300 °C. Differential scanning calorimetry analysis confirms the decrease of the melting temperature and signal of glass transition temperature with the addition of nanofiller, which indicates the decrease of crystallinity of the polymer matrix. An absolute correlation between diffusion coefficient (D), ion mobility (µ), number density (n), double-layer capacitance (C dl), glass transition temperature, melting temperature (T m), free ion area (%) and conductivity (σ) has been observed. A convincing model to study the role of nanofiller in a polymer salt complex has been proposed, which supports the experimental findings. The prepared polymer electrolyte system with significant ionic conductivity, high ionic transference number, and good thermal and voltage stability could be suggested as a potential candidate as electrolyte cum separator for the fabrication of a

The Politics of PVC: Technology and Institutions in Upland Water Management in Northern Thailand

Directory of Open Access Journals (Sweden)

Nathan Badenoch

2009-06-01

Full Text Available Conflict over water has grown in the mountainous areas of Thailand since the replacement of opium with alternative crops. PVC-sprinkler irrigation has enabled dry-season expansion of these cash crops on sloping lands, intensifying demand for water when it is most scarce. The technology and institutions that form the backbone of these irrigation systems have evolved simultaneously in a process of adaptive governance, in which local farmers draw on local social resources to balance competition and cooperation. Common conceptions of upstream – downstream conflict, pitting Thai against ethnic minorities in a struggle for resources, dominate the discourse of watersheds in Thailand. Upland water users themselves are diverse and their resource management systems are dynamic, even if they are not recognised as legitimate users of water. Understanding how upland communities create local systems of resource governance through dry-season irrigation is highly relevant for governance at higher levels, such as in the efforts to establish watershed networks and river basin organisations.

Long-Term Performance of the Laguna de Barlovento Reservoir Water-Proofing using a PVC-P Geo membrane

International Nuclear Information System (INIS)

Blanco Fernandez, M.; Leiro Lopez, A.; Soriano Carrillo, J.; Crespo Mucientes, M.; Zornberg, J.; Aguilar Gonzalez, E.; Rico Arnaiz, G.; Pargada Iglesias, L.

2014-01-01

The Laguna de Barlovento reservoir was one of the most important European hydraulic projects at the time of its construction because of its high capacity and challenging location. At the time, the designers decided to waterproof this reservoirs with a geo membrane of plasticized polyvinyl chloride (PVC-P). This paper documents the initial characteristics of the geo membrane and its performance since its installation until 2010. The material characterization includes a comprehensive testing program, the results of which are presented. They include quantification of the geo membrane thickness, amount and nature of plasticizers, tensile properties, fold ability under low temperatures, dynamic impact resistance, puncture resistance, welding strength (both in the manufacturing facility and in the field), as well as the use of techniques involving optical and scanning electron microscopy. In addition, advanced analytical techniques, such as Fourier Transform Infrared Spectroscopy (FTIR), Gas Chromatography (GC) and Mass spectrometry (MS), were used in order to identify the plasticizers used in the geo membrane formulation. Fold ability tests were found to provide early indication of degradation. Results from reflection optical and electron scanning microscopy showed that, after 19 nineteen years of installation, the geo membrane remains in good conditions, particularly on the non-exposed side. (Author)

Influence of iron substitution by selected rare-earth ions on the properties of NiZn ferrite fillers and PVC magneto-polymer composites

Science.gov (United States)

Ušák, Elemír; Ušáková, Mariana; Dosoudil, Rastislav; Šoka, Martin; Dobročka, Edmund

2018-04-01

Nickel-zinc ferrites are very important soft magnetic materials from the point of view of diverse technical applications (such as, e.g., various electronic devices and components) for their high magnetic permeability and permittivity, low core loss, high resistivity, high Curie temperature as well as mechanical strength and chemical stability. Due to their good absorbing properties, they can be used as microwave absorbing and shielding materials with the aim of decreasing the environmental pollution caused by non-ionizing microwave radiation. The ferrite material incorporated into the polymer matrix creates qualitatively new magneto-polymer composite material taking benefits from both components. The properties typical for polymers (elasticity, mouldability, etc.) are combined with good high-frequency magnetic parameters, thus allowing to utilize these materials, e.g., in high-frequency applications where especially flexibility of composite materials plays a key role. Small amounts of selected rare-earth (RE) ions, in particular Y3+, La3+, Eu3+ and Gd3+ have been embedded into the nickel-zinc ferrite that has been used as the magnetic filler in magnetic polymer composites with polyvinylchloride (PVC) acting as the polymeric matrix. The effect of various types of rare-earth ions on the structural as well as quasi-static and dynamic (electro)magnetic properties of the ferrite fillers as well as ferrite/PVC composites, in particular the frequency dispersion of the complex permeability, has been studied.

Influência de embalagens e temperatura no armazenamento de jabuticabas (Myrciaria jabuticaba (Vell Berg cv 'SABARÁ' Packaging and temperature influences on the storage of jaboticaba (Myrciaria jabuticaba (Vell Berg fruits cv.'SABARÁ'

Directory of Open Access Journals (Sweden)

Maria Amalia Brunini

2004-09-01

Full Text Available Foram avaliadas jabuticabas 'sabará' maduras, acondicionadas em bandejas de polietileno tereftalato, revestidas externamente com filme plástico de PVC, esticável e alto aderente, de 12 e 20 micras, e em bandejas de poliestireno expandido, revestidas externamente com filme plástico de PVC, esticável e alto aderente, de 12 e 20 micras. Cada bandeja recebeu 25 frutos. As bandejas foram armazenadas à temperatura de 11±1ºC com 98%UR e em condições de ambiente (23,6 a 28,3ºC com 53,7 a 68,3%UR. Como controle utilizaram-se frutos acondicionados em bandejas de polietileno tereftalato (12x20x5cm não recobertas com filme plástico. Considerando-se os resultados obtidos pode-se concluir que o uso de embalagem associada à baixa temperatura reduziu a perda de massa fresca, prolongou a vida-útil dos frutos com manutenção da aparência até 6 dias, não influenciou na evolução dos teores de acidez total titulável, sólidos solúveis totais e pH, mas interferiu na evolução de carboidratos solúveis e vitamina C. Os frutos acondicionados não recobertos com filme plástico e armazenados em condições ambiente resistiram 2 dias, mas ao final não apresentaram aparência aceitável para comercialização, pois haviam emurchecido e enrugado. As condições de refrigeração (11±1ºC melhoraram a resistência dos frutos acondicionados não recobertos com filmes plásticos, entretanto, após 4 dias apresentaram má aparência.Were evaluated mature jaboticaba 'sabará' fruits packaged into polystyrene expanded trays covered with stretching and sticking PVC plastic film, with stretching thickness of 12 and 20µm, and packaged into tereftalato polyethylene trays covered with stretching and sticking PVC plastic film, with thickness of 12 and 20µm. Into each tray were placed 25 fruits. The trays were stored at 11±1ºC with 98%UR and at environmental conditions (23,6ºC to 28,3ºC with 53,7% to 68,3%UR. Jaboticaba fruits packaged into tereftalato

Co-occurrence of invasive Cuban Treefrogs and native treefrogs in PVC pipe refugia

Science.gov (United States)

Elston, Laura M.; Waddle, J. Hardin; Rice, Kenneth G.; Percival, H. Franklin

2013-01-01

The Cuban Treefrog (Osteopilus septentrionalis) was first introduced to Florida at Key West. Since this introduction, Cuban Treefrogs have spread to Miami and are now established throughout most of peninsular Florida. Cuban Treefrogs can become very abundant in areas they colonize. Several reasons contribute to their success, including a generalist diet, high fecundity and the ability to reproduce year-round, and use of disturbed or human-modified habitats. Scientists and managers are concerned that Cuban Treefrogs may contribute to the decline of native treefrogs. Cuban Treefrogs may exclude native treefrogs through both competition and predation. Because the evidence from our study and others suggests that Green and Squirrel Treefrogs do not alter their behavior to avoid Cuban Treefrogs, there is cause for concern that sampling with PVC pipes may increase the vulnerability of the native species to predation. This possibility needs further research, including whether other species of native treefrogs sympatric to where Cuban Treefrogs have invaded are also naïve to the possible threat posed by these frogs, and also if native treefrogs eventually learn to avoid Cuban Treefrogs.

Sealing and explant types on the mangaba micropropagation Tipo de vedação e explantes na micropropagação de mangabeira

Directory of Open Access Journals (Sweden)

Aline de Jesus Sá

2012-08-01

Full Text Available In micropropagation, especially for mangaba tree botanical variety of Northeastern Brazil, limiting aspects such as ethylene accumulation in the cultivation flask and loss of vigor in subcultures have been observed. This study was aimed at assessing the technical and scientific knowledge of the in vitro propagation of botanical mangaba tree variety and at improving the micropropagation protocol, establishing the in vitro cultivation time, the best type of flask sealing and explant at different micropropagation stages. For the establishment phase and for the first and second subcultures, the MS medium with 3% sucrose and 0.6% agar, supplemented with 1 mg L-1 IAA and 1 mg L-1 BA was used. Evaluations were performed at 30, 50 and 65 days of in vitro cultivation. The best types of flask sealing for the establishment phase were the PVC film and Para-film® and for the first subculture the Para-film® seal. In the second subculture the PVC film and Para-film® seals promoted the best growth. The median and basal nodal segments presented the best performance in the first subculture. No significant effect of explant type was observed in the second subculture. The ideal subculture interval in the establishment phase and the first and second subcultures is 50 days.Na micropropagação, especialmente para mangaba, variedade botânica da árvore do Nordeste do Brasil, aspectos limitantes, como acúmulo de etileno no recipiente de cultivo e perda de vigor em subculturas têm sido observados. Neste estudo, objetivou-se avaliar o conhecimento técnico e científico da propagação in vitro de mangabeira, variedade botânica do Nordeste do Brasil, e melhorar o protocolo de micropropagação, o melhor tipo de vedação frasco e explante em diferentes etapas. Para a fase de estabelecimento e para as subculturas primeiro e segundo, foi utlizado o meio MS com 3% de sacarose e agar 0,6%, suplementado com 1 mg L-1 de AIA e 1 mg L-1 de BAP. As avaliações foram

Immobilization of tris(2 pyridyl methylamine in a PVC-Membrane Sensor and Characterization of the Membrane Properties

Directory of Open Access Journals (Sweden)

Rezayi Majid

2012-05-01

Full Text Available Abstract Background Due to the increasing industrial use of titanium compounds, its determination is the subject of considerable efforts. The ionophore or membrane active recognition is the most important component of any polymeric membrane sensor. The sensor’s response depends on the ionophore and bonding between the ionophore and the target ion. Ionophores with molecule-sized dimensions containing cavities or semi-cavities can surround the target ion. The bond between the ionophore and target ion gives different selectivity and sensitivity toward the other ions. Therefore, ionophores with different binding strengths can be used in the sensor. Results In the present work, poly (vinyl chloride (PVC based membrane incorporating tris (2 pyridyl methylamine (tpm as an ionophore has been prepared and explored as a titanium(III selective sensor. Conclusions The strengths of the ion–ionophore (Ti(OH2+-tpm interactions and the role of ionophore on membrane were tested by various techniques such as elemental analysis, UV–vis, Fourier transform infrared (FTIR spectroscopy, scanning electron microscopy (SEM, and powder X-ray diffraction (XRD. All data approved the successful incorporation of organic group via covalent bond.

Alternatif Panel Mobilya Malzemesi Olarak Polivinil Klorür (Pvc) Levhalardan Üretilmiş Kutu Mobilya Köşe Birleştirmelerinin Moment Kapasiteleri

OpenAIRE

KASAL, Ali; BAYINDIR, Fatih; DİLER, Harun; KUŞKUN, Tolga

2014-01-01

In this study, bending moment capacities of L-type corner joints farbricated from polyvinyl chloride (PVC) panels that are commonly produced and used and expected to be an alternative material for case (panel) furniture manufacturing were analyzed under the test loads and compared to the conventional wood based panels. Corner joints were connected with various techniques that encountered in case type furniture. For this purpose, in preparing the specimens, 3 different density and qualities of...

PVC Orientado: avaliação de processo de orientação e das propriedades mecânicas em função da razão de estiramento

Directory of Open Access Journals (Sweden)

Felipe Albuquerque Medeiros

2013-01-01

Full Text Available Este artigo avalia o efeito da "orientação molecular" nas propriedades mecânicas do PVC Rígido. Introduz-se o tema associando-o à aplicação do PVC Orientado em sistemas de tubulações, considerando a importância do nível de gelificação na qualidade desses produtos. É descrito e testado um método experimental de orientação mono-axial em um extrudado e materiais com diferentes razões de estiramento são produzidos para avaliação de propriedades mecânicas. Aumentando a razão de estiramento, há ganhos principalmente no limite de resistência à tração, além do módulo elástico sob tração e tenacidade. Por outro lado, a deformação na ruptura é reduzida.

A comparison of results for samples collected with bailers constructed of different materials

International Nuclear Information System (INIS)

Thomey, N.; Ogle, R.; Jackson, J.

1992-01-01

A bailer is one of the most common sampling devices used to collect ground water samples. Bailers constructed from various materials are available; teflon, polyvinyl chloride (PVC), polyethylene, and stainless steel are all commonly used. It is widely recognized that sample results can be affected by the material from which the bailer is constructed. Teflon and stainless steel are usually recommended based upon their inert properties. The cost of these bailers is significantly higher than other types. For the purposes of petroleum storage tank investigations, sampling devices that would not compromise sample quality but be more economical than teflon or stainless steel would be especially desirable. Water samples were collected using the different types of bailers; teflon, stainless steel, PVC, and polyethylene. Split samples were analyzed for benzene, toluene, ethylbenzene, total xylenes, and Total Petroleum Hydrocarbons. The analytical results were compared to determine if differences were due to normal analytical variances or due to interaction of the sample with the sampling device. No difference was noted in the results which were obtained

78 FR 48651 - Polyethylene Terephthalate Film, Sheet, and Strip From Taiwan; Preliminary Results of Antidumping...

Science.gov (United States)

2013-08-09

... duty order on polyethylene terephthalate film, sheet, and strip (PET Film) from Taiwan. The period of.... (SMTC) (collectively, Shinkong), producer and exporter of PET Film from Taiwan. The Department...: Milton Koch, AD/CVD Operations, Office 6, Import Administration, International Trade Administration, U.S...

Behaviour of Listeria monocytogenes in packaged fresh mushrooms (Agaricus bisporus).

Science.gov (United States)

González-Fandos, E; Olarte, C; Giménez, M; Sanz, S; Simón, A

2001-11-01

The aim of this study was to evaluate the potential of Listeria monocytogenes to grow in mushrooms packaged in two different types of PVC films when stored at 4 degrees C and 10 degrees C. Mushrooms were packed in two polymeric films (perforated and nonperforated PVC) and stored at 4 degrees C and 10 degrees C. The carbon dioxide and oxygen content inside the packages, aerobic mesophiles, psychrotrophs, Pseudomonas spp., Listeria monocytogenes, faecal coliforms, Escherichia coli, anaerobic spores and major sensory factors were determined. The mushrooms packaged in nonperforated film and stored at 4 degrees C had the most desirable quality parameters (texture, development stage and absence of moulds). Listeria monocytogenes was able to grow at 4 degrees C and 10 degrees C in inoculated mushrooms packaged in perforated and nonperforated films between 1 and 2 log units during the first 48 h. After 10 d of storage, the populations of L. monocytogenes were higher in mushrooms packaged in nonperforated film and stored at 10 degrees C. MAP followed by storage at 4 degrees C or 10 degrees C extends the shelf life by maintaining an acceptable appearance, but allows the growth and survival of L. monocytogenes. According to this study additional hurdles must be studied in order to prevent the growth of L. monocytogenes.

Physicochemical and microbiological characteristics of minimally processed 'Champagne' oranges (Citrus reticulata × Citrus sinensis in different packgings

Directory of Open Access Journals (Sweden)

Juliana da Silva Agostini

2013-03-01

Full Text Available The objective of this study was to investigate the influence of the level of minimal processing and modified atmosphere on the quality of 'Champagne' orange stored under refrigeration. The fruits were subjected to the following processing: a whole fruit without flavedo; b whole fruit without flavedo and albedo; and c segmented into wedges and packed as follows: uncoated packaging (control; polyethylene film; PVC film; gelatin-based edible films (3%; and polyesthyrene translucent plastic container with a lid. The minimally processed oranges were stored at 5 ± 1°C for 8 days and were subjected to physicochemical and microbiological analyses every two days. Greater weight loss occurred in fruits without flavedo and segmented, uncoated, and coated with the edible gelatin film During storage, there was a slight increase in Total Soluble Solids (TSS for the treatments with greater weight loss and reduction in acidity and ascorbic acid, regardless of the packaging type. The microbial counts did not exceed the acceptable limits in the treatments; however, higher counts were observed at the end of storage. The minimally processed fruit packed in lidded polystyrene containers and polyethylene and PVC films kept their overall fresh visual appearance with a few physicochemical and microbiological changes up to the 8th day of storage.

Stress transfer in microdroplet tensile test: PVC-coated and uncoated Kevlar-29 single fiber

Science.gov (United States)

Zhenkun, Lei; Quan, Wang; Yilan, Kang; Wei, Qiu; Xuemin, Pan

2010-11-01

The single fiber/microdroplet tensile test is applied for evaluating the interfacial mechanics between a fiber and a resin substrate. It is used to investigate the influence of a polymer coating on a Kevlar-29 fiber surface, specifically the stress transfer between the fiber and epoxy resin in a microdroplet. Unlike usual tests, this new test ensures a symmetrical axial stress on the embedded fiber and reduces the stress singularity that appears at the embedded fiber entry. Using a homemade loading device, symmetrical tensile tests are performed on a Kevlar-29 fiber with or without polyvinylchloride (PVC) coating, the surface of which is in contact with two epoxy resin microdroplets during curing. Raman spectra on the embedded fiber are recorded by micro-Raman Spectroscopy under different strain levels. Then they are transformed to the distributions of fiber axis stress based on the relationship between stress and Raman shift. The Raman results reveal that the fiber axial stresses increase with the applied loads, and the antisymmetric interfacial shear stresses, obtained by a straightforward balance of shear-to-axial forces argument, lead to the appearance of shear stress concentrations at a distance to the embedded fiber entry. The load is transferred from the outer fiber to the embedded fiber in the epoxy microdroplet. As is observed by scanning electronic microscopy (SEM), the existence of a flexible polymer coating on the fiber surface reduces the stress transfer efficiency.

Flow Injection Potentiometric Determination of Cd2+ Ions Using a Coated Graphite Plasticized PVC-Membrane Electrode Based on 1, 3-Bis(2-cyanobenzene)triazene.

Science.gov (United States)

Shamsipur, Mojtaba; Sahari, Shokat; Payehghadr, Mahmood; Alizadeh, Kamal

2011-09-01

1, 3-Bis(2-cyanobenzene)triazene, L, was used as a suitable ionophore for the fabrication of a new PVC-based polymeric membrane coated graphite electrode for selective sensing of Cd2+ ion. The electrode exhibited a selective linear Nernstian response to Cd2+ ion at an optimal pH range of 6-9 with a limit of detection of 8.0 × 10-6 M and a fast response time of about 2 s. The electrode was used as a proper detection system in flow-injection potentiometry of cadmium ion and resulted in well defined peaks for cadmium ions with stable baseline, excellent reproducibility and high sampling rates of over 100 injections per hour. It showed good stability, reproducibility and fast response time. The practical utility of the proposed system has also been reported.

Neodymium(III PVC Membrane Electrodchemical Sensor Based on N-benzoylethylidene-2-aminobenzylamine

Directory of Open Access Journals (Sweden)

Hassan Ali Zamani

2012-01-01

Full Text Available The N-benzoylethylidene-2-aminobenzylamine (BEA was used as a suitable ionophore in construction of neodymium ion selective electrode. The electrode with composition of 30% PVC, 58% solvent mediator (NB, 2% ionophore (BEA and 10% anionic additive (OA shows the best potentiometric response characteristics. The Nd3+ sensor exhibits a Nernstian slope of 21.2 ± 0.2 mV decade-1 over the concentration range of 1.0 × 10-6 to 1.0 × 10-2 mol L-1, and a detection limit of 6.3 × 10-7 mol L-1 of Nd3+ ions. The potentiometric response of the sensor is independent of the solution pH in the range of 2.4–8.5. It has a very short response time, in the whole concentration range (~7 s, and can be used for at least eight weeks. The proposed sensor revealed high selectivity with respect to all common alkali, alkaline earth, transition and heavy metal ions, including members of the lanthanide family other than Nd3+. The Nd3+ sensor was successfully applied as an indicator electrode in the potentiometric titration of Nd3+ ions with EDTA. The electrode was also employed for the determination of the fluoride ion in two mouth wash preparations.

Development of amorphous carbon protective coatings on poly(vinyl)chloride

International Nuclear Information System (INIS)

Rangel, Elidiane C.; Souza, Eduardo S. de; Moraes, Francine S. de; Marins, Nazir M.S.; Schreiner, Wido H.; Cruz, Nilson C.

2010-01-01

The great versatility of polymers has promoted their application in a series of ordinary situations. The development of specific devices from polymers, however, requires modifications to fit specific stipulations. In this work the surface properties of thin films grown onto polyvinylchloride (PVC) were investigated. Hydrogenated amorphous carbon films were deposited onto commercial PVC plates from acetylene and argon plasmas excited by radiofrequency (13.56 MHz, 70 W) power. The proportion of acetylene in the gas feed was varied against that of argon, keeping the total pressure constant at 2.5 Pa. Deposition time was 1800 s. Film elemental composition was analyzed by X-ray photoelectron spectroscopy, XPS. Water contact angle measurements were performed using the sessile drop technique. The root mean squared roughness was derived from 50 x 50 μm 2 surface topographic images, acquired by scanning probe microscopy. Nanoindentation and pin-on-disk techniques were employed on the determination of film hardness and sliding wear, respectively. Oxidation resistance was obtained through the etching rate of the samples in oxygen radiofrequency (1.3 Pa, 50 W) plasmas. From XPS analysis it was detected oxygen and nitrogen contamination in all the samples. It was also found that sp 3 /sp 2 ratio depends on the proportion of argon in the plasma. At lower argon concentrations, hardness, wear and oxidation resistances were all improved with respect to the uncoated PVC. In such conditions, the surface wettability is low indicating a moderate receptivity to water. This combination of properties, ascribed to a balance between the ion bombardment and deposition processes, is suitable for materials exposed to rigorous weathering conditions.

Subsystem for processing, storage and editing of the results of the chamber film scanning

International Nuclear Information System (INIS)

Balgansurehn, Ya.; Dirner, A.; Ivanov, V.G.

1987-01-01

A subsystem which is an element of the high-automated system for film data processing and intended for run with the scanning information is described. The subsystem consists of routines which allow to create, to edit and to print the file of scanning results both in batch and interactive mode on the CDC-6500 computer

78 FR 50029 - Polyethylene Terephthalate Film, Sheet and Strip From Brazil: Preliminary Results of Antidumping...

Science.gov (United States)

2013-08-16

... the antidumping duty order on polyethylene terephthalate film, sheet and strip (PET film) from Brazil... any reviewable entries, shipments or sales of subject PET film by Terphane during the POR, we are.... FOR FURTHER INFORMATION CONTACT: Tyler Weinhold or Robert James, AD/CVD Operations, Office 7, Import...

Comparative Effects of Ingested PVC Micro Particles With and Without Adsorbed Benzo(apyrene vs. Spiked Sediments on the Cellular and Sub Cellular Processes of the Benthic Organism Hediste diversicolor