WorldWideScience

Sample records for pure ni layer

  1. Ni/Ni-YSZ current collector/anode dual layer hollow fibers for micro-tubular solid oxide fuel cells

    Energy Technology Data Exchange (ETDEWEB)

    Kanawka, K.; Othman, M.H.D.; Droushiotis, N.; Wu, Z.; Kelsall, G.; Li, K. [Department of Chemical Engineering and Chemical Technology, Imperial College London, London SW7 2AZ (United Kingdom)

    2011-10-15

    A co-extrusion technique was employed to fabricate a novel dual layer NiO/NiO-YSZ hollow fiber (HF) precursor which was then co-sintered at 1,400 C and reduced at 700 C to form, respectively, a meshed porous inner Ni current collector and outer Ni-YSZ anode layers for SOFC applications. The inner thin and highly porous ''mesh-like'' pure Ni layer of approximately 50 {mu}m in thickness functions as a current collector in micro-tubular solid oxide fuel cell (SOFC), aiming at highly efficient current collection with low fuel diffusion resistance, while the thicker outer Ni-YSZ layer of 260 {mu}m acts as an anode, providing also major mechanical strength to the dual-layer HF. Achieved morphology consisted of short finger-like voids originating from the inner lumen of the HF, and a sponge-like structure filling most of the Ni-YSZ anode layer, which is considered to be suitable macrostructure for anode SOFC system. The electrical conductivity of the meshed porous inner Ni layer is measured to be 77.5 x 10{sup 5} S m{sup -1}. This result is significantly higher than previous reported results on single layer Ni-YSZ HFs, which performs not only as a catalyst for the oxidation reaction, but also as a current collector. These results highlight the advantages of this novel dual-layer HF design as a new and highly efficient way of collecting current from the lumen of micro-tubular SOFC. (Copyright copyright 2011 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim)

  2. Effect of separated layer thickness on magnetoresistance and magnetic properties of Co/Dy/Co and Ni/Dy/Ni film systems

    Science.gov (United States)

    Shabelnyk, T. M.; Shutylieva, O. V.; Vorobiov, S. I.; Pazukha, I. M.; Chornous, A. M.

    2018-01-01

    Co(5 nm)/Dy(tDy)/Co(20 nm)/S and Ni(5 nm)/Dy(tDy)/Ni(20 nm)/S trilayer films are prepared by electron-beam sputtering to investigate the influence of dysprosium layer thickness (tDy) and thermal annealing on the crystal structure, magnetoresistance (MR) and magnetic properties of thin films. The thickness of Dy layer changed in the range from 1 nm to 20 nm. The samples annealed for 20 min at 700 K. Electron diffraction patterns reveal that the as-deposited and annealed systems Co/Dy/Co and Ni/Dy/Ni had fcc-Co + hcp-Dy and fcc-Ni + hcp-Dy phase state, respectively. It is also shown that at the tDy = 15 nm the transition from amorphous to crystalline structures of Dy layer is observed. An increase in the Dy layer thickness results in changes in the MR and magnetic properties of the trilayer systems. It is shown that MR is most thermally stable against annealing to 700 K at tDy = 15 nm for Co/Dy/Co as well as for Ni/Dy/Ni. For tDy = 15 nm the, value of MR for both system increases by two times compared to those of pure ferromagnetic (FM) samples. The coercivity (Bc), remanent (Mr) and saturation (Ms) magnetization of the in-plain magnetization hysteresis loops are related to the Dy layer thickness too. The coercivity depends on the FM materials type and diffusion processes at the layer boundary. Accordingly, Mr and Ms are reduced with tDy increasing before and after annealing for both trilayer systems.

  3. Texture and microstructure analysis of epitaxial oxide layers prepared on textured Ni-12wt%Cr tapes

    Energy Technology Data Exchange (ETDEWEB)

    Huehne, R; Kursumovic, A; Tomov, R I; Glowacki, B A [Department of Materials Science and IRC in Superconductivity, University of Cambridge, Pembroke Street, Cambridge, CB2 3QZ (United Kingdom); Holzapfel, B [Institut fuer Festkoerper- und Werkstoffforschung, Helmholtzstrasse 20, 01069 Dresden (Germany); Evetts, J E [Department of Materials Science and IRC in Superconductivity, University of Cambridge, Pembroke Street, Cambridge, CB2 3QZ (United Kingdom)

    2003-05-07

    Oxide layers for the preparation of YBa{sub 2}Cu{sub 3}O{sub 7-x} coated conductors were grown on highly textured Ni-12wt%Cr tapes in pure oxygen using surface oxidation epitaxy at temperatures between 1000 deg. C and 1300 deg. C. Microstructural investigations revealed a layered oxide structure. The upper layer consists mainly of dense cube textured NiO. This is followed by a porous layer containing NiO and NiCr{sub 2}O{sub 4} particles. A detailed texture analysis showed a cube-on-cube relationship of the NiCr{sub 2}O{sub 4} spinel to the metal substrate. Untextured Cr{sub 2}O{sub 3} particles in a nickel matrix were found in a third layer arising from internal oxidation of the alloy. A high surface roughness and mechanical instability of the oxide were observed, depending on oxidation temperature and film thickness. However, mechanically stable oxide layers have been prepared using an additional annealing step in a protective atmosphere. Additionally, mechanical polishing or a second buffer layer, which grows with a higher smoothness, may be applied to reduce the surface roughness for coated conductor applications.

  4. Exchange bias variations of the seed and top NiFe layers in NiFe/FeMn/NiFe trilayer as a function of seed layer thickness

    International Nuclear Information System (INIS)

    Sankaranarayanan, V.K.; Yoon, S.M.; Kim, C.G.; Kim, C.O.

    2005-01-01

    Development of exchange bias at the seed and top NiFe layers in the NiFe (t nm)/FeMn(10 nm)/NiFe(5 nm) trilayer structure is investigated as a function of seed layer thickness, in the range of 2-20 nm. The seed NiFe layer shows maximum exchange bias at 4 nm seed layer thickness. The bias shows inverse thickness dependence with increasing thickness. The top NiFe layer on the other hand shows only half the bias of the seed layer which is retained even after the sharp fall in seed layer bias. The much smaller bias for the top NiFe layer is related to the difference in crystalline texture and spin orientations at the top FeMn/NiFe interface, in comparison to the bottom NiFe/FeMn interface which grows on a saturated NiFe layer with (1 1 1) orientation

  5. Corrosion of pure magnesium under thin electrolyte layers

    International Nuclear Information System (INIS)

    Zhang Tao; Chen Chongmu; Shao Yawei; Meng Guozhe; Wang Fuhui; Li Xiaogang; Dong Chaofang

    2008-01-01

    The corrosion behavior of pure magnesium was investigated by means of cathodic polarization curve, electrochemical impedance spectroscopy (EIS) and electrochemical noise (EN) under aerated and deaerated thin electrolyte layers (TEL) with various thicknesses. Based on shot noise theory and stochastic theory, the EN results were quantitatively analyzed by using the Weibull and Gumbel distribution function, respectively. The results show that the cathodic process of pure magnesium under thin electrolyte layer was dominated by hydrogen reduction. With the decreasing of thin electrolyte layer thickness, cathodic process was retarded slightly while the anodic process was inhibited significantly, which indicated that both the cathodic and anodic process were inhibited in the presence of oxygen. The absence of oxygen decreased the corrosion resistance of pure magnesium in case of thin electrolyte layer. The corrosion was more localized under thin electrolyte layer than that in bulk solution. The results also demonstrate that there exist two kinds of effects for thin electrolyte layer on the corrosion behavior of pure magnesium: (1) the rate of pit initiation was evidently retarded compared to that in bulk solution; (2) the probability of pit growth oppositely increased. The corrosion model of pure magnesium under thin electrolyte layer was suggested in the paper

  6. Growing imbedded Ni3C-rich layer with sharp interfaces by means of ion beam mixing of C/Ni layers

    International Nuclear Information System (INIS)

    Barna, Arpad; Kotis, Laszlo; Labar, Janos; Sulyok, Attila; Toth, Attila L; Menyhard, Miklos; Panjan, Peter

    2011-01-01

    C/Ni bilayers of various layer thicknesses (20-40 nm) were ion bombarded using Ga + and Ni + projectiles of energies 20 and 30 keV. Ion bombardment resulted in the growth of a Ni 3 C rich layer with the following features: (a) sharp carbon/Ni 3 C rich layer interface, (b) the amount of Ni 3 C produced by the irradiation proportional to the square root of the fluence and dependent on the type of projectile, (c) good correlation between the distribution of vacancies produced by the ion bombardment and the distribution of Ni 3 C. The formation of the metastable Ni 3 C compound was explained by a vacancy-assisted process. The sharp interface is the consequence of a relaxation process removing the intermixed Ni from the carbon layer. The square root of fluence dependence of the thickness of the Ni 3 C-rich layer can be explained by a usual diffusion equation considering moving boundaries.

  7. Giant magnetoimpedance effect in sputtered single layered NiFe film and meander NiFe/Cu/NiFe film

    International Nuclear Information System (INIS)

    Chen, L.; Zhou, Y.; Lei, C.; Zhou, Z.M.; Ding, W.

    2010-01-01

    Giant magnetoimpedance (GMI) effect on NiFe thin film is very promising due to its application in developing the magnetic field sensors with highly sensitivity and low cost. In this paper, the single layered NiFe thin film and NiFe/Cu/NiFe thin film with a meander structure are prepared by the MEMS technology. The influences of sputtering parameters, film structure and conductor layer width on GMI effect in NiFe single layer and meander NiFe/Cu/NiFe film are investigated. Maximum of the GMI ratio in single layer and sandwich film is 5% and 64%, respectively. The results obtained are useful for developing the high-performance magnetic sensors based on NiFe thin film.

  8. Layering and temperature-dependent magnetization and anisotropy of naturally produced Ni/NiO multilayers

    Energy Technology Data Exchange (ETDEWEB)

    Pappas, S. D.; Trachylis, D.; Velgakis, M. J. [Laboratory of High-Tech Materials, School of Engineering, University of Patras, 26504 Patras (Greece); Kapaklis, V.; Joensson, P. E.; Papaioannou, E. Th. [Department of Physics and Astronomy, Uppsala University, Box 516, SE-751 20 Uppsala (Sweden); Delimitis, A. [Chemical Process Engineering Research Institute (CPERI), Centre for Research and Technology Hellas (CERTH), 57001 Thermi, Thessaloniki (Greece); Poulopoulos, P. [Laboratory of High-Tech Materials, School of Engineering, University of Patras, 26504 Patras (Greece); Institut fuer Experimentalphysik, Freie Universitaet Berlin, Arnimallee 14, D-14195 Berlin-Dahlem (Germany); Materials Science Department, University of Patras, 26504 Patras (Greece); Fumagalli, P. [Institut fuer Experimentalphysik, Freie Universitaet Berlin, Arnimallee 14, D-14195 Berlin-Dahlem (Germany); Politis, C. [Laboratory of High-Tech Materials, School of Engineering, University of Patras, 26504 Patras (Greece); Department of Materials Science and Engineering, University of Texas at Arlington, Arlington, Texas 76019 (United States)

    2012-09-01

    Ni/NiO multilayers were grown by magnetron sputtering at room temperature, with the aid of the natural oxidation procedure. That is, at the end of the deposition of each single Ni layer, air is let to flow into the vacuum chamber through a leak valve. Then, a very thin NiO layer ({approx}1.2 nm) is formed. Simulated x-ray reflectivity patterns reveal that layering is excellent for individual Ni-layer thickness larger than 2.5 nm, which is attributed to the intercalation of amorphous NiO between the polycrystalline Ni layers. The magnetization of the films, measured at temperatures 5-300 K, has almost bulk-like value, whereas the films exhibit a trend to perpendicular magnetic anisotropy (PMA) with an unusual significant positive interface anisotropy contribution, which presents a weak temperature dependence. The power-law behavior of the multilayers indicates a non-negligible contribution of higher order anisotropies in the uniaxial anisotropy. Bloch-law fittings for the temperature dependence of the magnetization in the spin-wave regime show that the magnetization in the multilayers decreases faster as a function of temperature than the one of bulk Ni. Finally, when the individual Ni-layer thickness decreases below 2 nm, the multilayer stacking vanishes, resulting in a dramatic decrease of the interface magnetic anisotropy and consequently in a decrease of the perpendicular magnetic anisotropy.

  9. Shape effect in FMR of Ni-Co-Mn-In layers obtained by pulsed laser deposition

    Directory of Open Access Journals (Sweden)

    Dubiel Łukasz

    2017-01-01

    Full Text Available We have studied thin layers of Ni50-xCoxMn50-yIny alloys on (001 Si substrate obtained by pulsed laser deposition method (PLD using YAG Nd3+ laser operating at second harmonic. The target was bulk Ni50-xCoxMn50-yIny (x = 5, y = 14.5 alloy prepared by induction melting of pure elements under argon atmosphere. Magnetic properties were investigated on Bruker X band EPR spectrometer (9.36 GHz at room temperature. The magnetic resonance spectrum consists of non-symmetric lines with resonance field within wide field range (2500-4800 Gs depending on the orientation of the static field in the plane perpendicular to the layer. Calculated spectroscopic splitting factor g = 2.09.

  10. Ternary Pt-Ru-Ni catalytic layers for methanol electrooxidation prepared by electrodeposition and galvanic replacement

    Directory of Open Access Journals (Sweden)

    Athanasios ePapaderakis

    2014-06-01

    Full Text Available Ternary Pt-Ru-Ni deposits on glassy carbon substrates, Pt-Ru(Ni/GC, have been formed by initial electrodeposition of Ni layers onto glassy carbon electrodes, followed by their partial exchange for Pt and Ru, upon their immersion into equimolar solutions containing complex ions of the precious metals. The overall morphology and composition of the deposits has been studied by SEM microscopy and EDS spectroscopy. Continuous but nodular films have been confirmed, with a Pt÷Ru÷Ni % bulk atomic composition ratio of 37÷12÷51 (and for binary Pt-Ni control systems of 47÷53. Fine topographical details as well as film thickness have been directly recorded using AFM microscopy. The composition of the outer layers as well as the interactions of the three metals present have been studied by XPS spectroscopy and a Pt÷Ru÷Ni % surface atomic composition ratio of 61÷12÷27 (and for binary Pt-Ni control systems of 85÷15 has been found, indicating the enrichment of the outer layers in Pt; a shift of the Pt binding energy peaks to higher values was only observed in the presence of Ru and points to an electronic effect of Ru on Pt. The surface electrochemistry of the thus prepared Pt-Ru(Ni/GC and Pt(Ni/GC electrodes in deaerated acid solutions (studied by cyclic voltammetry proves the existence of a shell consisting exclusively of Pt-Ru or Pt. The activity of the Pt-Ru(Ni deposits towards methanol oxidation (studied by slow potential sweep voltammetry is higher from that of the Pt(Ni deposit and of pure Pt; this enhancement is attributed both to the well-known Ru synergistic effect due to the presence of its oxides but also (based on the XPS findings to a modification effect of Pt electronic properties.

  11. Effect of Nano-TiC Dispersed Particles and Electro-Codeposition Parameters on Morphology and Structure of Hybrid Ni/TiC Nanocomposite Layers.

    Science.gov (United States)

    Benea, Lidia; Celis, Jean-Pierre

    2016-04-06

    This research work describes the effect of dispersed titanium carbide (TiC) nanoparticles into nickel plating bath on Ni/TiC nanostructured composite layers obtained by electro-codeposition. The surface morphology of Ni/TiC nanostructured composite layers was characterized by scanning electron microscopy (SEM). The composition of coatings and the incorporation percentage of TiC nanoparticles into Ni matrix were studied and estimated by using energy dispersive X-ray analysis (EDX). X-ray diffractometer (XRD) has been applied in order to investigate the phase structure as well as the corresponding relative texture coefficients of the composite layers. The results show that the concentration of nano-TiC particles added in the nickel electrolyte affects the inclusion percentage of TiC into Ni/TiC nano strucured layers, as well as the corresponding morphology, relative texture coefficients and thickness indicating an increasing tendency with the increasing concentration of nano-TiC concentration. By increasing the amount of TiC nanoparticles in the electrolyte, their incorporation into nickel matrix also increases. The hybrid Ni/nano-TiC composite layers obtained revealed a higher roughness and higher hardness; therefore, these layers are promising superhydrophobic surfaces for special application and could be more resistant to wear than the pure Ni layers.

  12. Effect of Nano-TiC Dispersed Particles and Electro-Codeposition Parameters on Morphology and Structure of Hybrid Ni/TiC Nanocomposite Layers

    Directory of Open Access Journals (Sweden)

    Lidia Benea

    2016-04-01

    Full Text Available This research work describes the effect of dispersed titanium carbide (TiC nanoparticles into nickel plating bath on Ni/TiC nanostructured composite layers obtained by electro-codeposition. The surface morphology of Ni/TiC nanostructured composite layers was characterized by scanning electron microscopy (SEM. The composition of coatings and the incorporation percentage of TiC nanoparticles into Ni matrix were studied and estimated by using energy dispersive X-ray analysis (EDX. X-ray diffractometer (XRD has been applied in order to investigate the phase structure as well as the corresponding relative texture coefficients of the composite layers. The results show that the concentration of nano-TiC particles added in the nickel electrolyte affects the inclusion percentage of TiC into Ni/TiC nano strucured layers, as well as the corresponding morphology, relative texture coefficients and thickness indicating an increasing tendency with the increasing concentration of nano-TiC concentration. By increasing the amount of TiC nanoparticles in the electrolyte, their incorporation into nickel matrix also increases. The hybrid Ni/nano-TiC composite layers obtained revealed a higher roughness and higher hardness; therefore, these layers are promising superhydrophobic surfaces for special application and could be more resistant to wear than the pure Ni layers.

  13. Effect of solute atoms on swelling in Ni alloys and pure Ni under He + ion irradiation

    Science.gov (United States)

    Wakai, E.; Ezawa, T.; Imamura, J.; Takenaka, T.; Tanabe, T.; Oshima, R.

    2002-12-01

    The effects of solute atoms on microstructural evolutions have been investigated using Ni alloys under 25 keV He + irradiation at 500 °C. The specimens used were pure Ni, Ni-Si, Ni-Co, Ni-Cu, Ni-Mn and Ni-Pd alloys with different volume size factors. The high number densities of dislocation loops about 1.5×10 22 m -3 were formed in the specimens irradiated to 1×10 19 ions/m 2, and they were approximately equivalent, except for Ni-Si. The mean size of loops tended to increase with the volume size factor of solute atoms. In a dose of 4×10 20 ions/m 2, the swelling was changed from 0.2% to 4.5%, depending on the volume size factors. The number densities of bubbles tended to increase with the absolute values of the volume size factor, and the swelling increased with the volume size factors. This suggests that the mobility of helium and vacancy atoms may be influenced by the interaction of solute atoms with them.

  14. Some structural characteristics of gamma-irradiated pure and Li2O-doped NiO solids

    International Nuclear Information System (INIS)

    Ramadan, A.A.; Dessouki, A.M.

    1989-01-01

    The induced structural changes, due to Li 2 O-doping (2.5 mol%) and γ-irradiation (10-80 Mrad), of NiO were investigated by XRD analyses. The results obtained revealed that lithium-doping resulted in a significant increase in the internal strain and a decrease in lattice parameter. These changes were explained in terms of creation of Ni 3+ ions in the doped solids. γ-Irradiation of pure and doped solids effected a decrease in both crystallite size and microstrain upon subjecting to doses of 20 and 30 Mrad. Higher doses induced an increase in both parameters in the case of pure NiO and a further decrease in case of the doped solid. These results were attributed to splitting of the large strained crystallites and to an activated sintering of the small strained ones. γ-Irradiation effected also an increase in the lattice parameters of pure and doped solids due to removal of some excess oxygen with subsequent decrease in the concentration of Ni 3+ ions. (author)

  15. Sputtering Yields of Si and Ni from the Ni1-xSix System Studied by Rutherford Backscattering Spectrometry

    Science.gov (United States)

    Kim, Su Chol; Yamaguchi, Satoru; Kataoka, Yoshihide; Iwami, Motohiro; Hiraki, Akio; Satou, Mamoru; Fujimoto, Fuminori

    1982-01-01

    Sputtering yields of Si and Ni from thin layer films of Ni-Si compounds (Ni1-xSix), including the pure materials (Ni and Si), caused by 5 keV Ar+ ion bombardment were investigated using backscattering spectrometry. The sputtering yield for Si from Ni1-xSix increased with increasing Si concentration. However, there is an abrupt decrease in the yield for Si concentrations above NiSi2 to pure Si. This is in clear contrast to the sputtering yield of Ni from Ni1-xSix which increased with increasing Ni concentration monotonously. These results are discussed on the basis of both the difference in the atomic density and the electronic state of the alloy.

  16. Enhanced optical and electrical properties of Ni inserted ITO/Ni/AZO tri-layer structure for photoelectric applications

    Energy Technology Data Exchange (ETDEWEB)

    Kumar, M. Melvin David; Kim, Hyunki [Department of Electrical Engineering, Incheon National University, Incheon 406772 (Korea, Republic of); Park, Yun Chang [Measurement and Analysis Division, National Nanofab Center (NNFC), Daejeon 305-806 (Korea, Republic of); Kim, Joondong, E-mail: joonkim@incheon.ac.kr [Department of Electrical Engineering, Incheon National University, Incheon 406772 (Korea, Republic of)

    2015-05-15

    Highlights: • Ni-embedding transparent conductor effectively reduces the resistivity. • Ni insertion improves the carrier mobility and collection efficiencies. • ITO/Ni/AZO is effective to improve photo-responses compared to ITO/AZO. - Abstract: A thin Ni layer of 5 nm thickness was deposited in between indium-tin-oxide (ITO) and aluminum-doped-zinc oxide (AZO) layers of 50 nm thickness each. The Ni inserting tri-layer structure (ITO/Ni/AZO) showed lower resistivity of 5.51 × 10{sup −4} Ωcm which is nearly 20 times lesser than 97.9 × 10{sup −4} Ωcm of bilayer structure (ITO/AZO). A thin Ni layer in between ITO and AZO enhanced the carrier concentration, mobility and photoresponse behaviors so that figure of merit (FOM) value of ITO/Ni/AZO device was greater than that of ITO/AZO device. ITO/Ni/AZO structure showed improved quantum efficiencies over a broad range of wavelengths (∼350–950 nm) compared to that of ITO/AZO bilayer structure, resulting in enhanced photoresponses. These results show that the optical, electrical and photoresponse properties of ITO/AZO structure could be enhanced by inserting Ni layer of 5 nm thickness in between ITO and AZO layers.

  17. Soft magnetic properties of hybrid ferromagnetic films with CoFe, NiFe, and NiFeCuMo layers

    Energy Technology Data Exchange (ETDEWEB)

    Choi, Jong-Gu [Eastern-western Biomedical Engineering, Sangji University, Wonju 220-702 (Korea, Republic of); Hwang, Do-Guwn [Dept. of Oriental Biomedical Engineering, Sangji University, Wonju 220-702 (Korea, Republic of); Rhee, Jang-Roh [Dept. of Physics, Sookmyung Women' s University, Seoul 140-742 (Korea, Republic of); Lee, Sang-Suk, E-mail: sslee@sangji.ac.kr [Dept. of Oriental Biomedical Engineering, Sangji University, Wonju 220-702 (Korea, Republic of)

    2011-09-30

    Two-layered ferromagnetic alloy films (NiFe and CoFe) with intermediate NiFeCuMo soft magnetic layers of different thicknesses were investigated to understand the relationship between coercivity and magnetization process by taking into account the strength of hard-axis saturation field. The thickness dependence of H{sub EC} (easy-axis coercivity), H{sub HS} (hard-axis saturation field), and {chi} (susceptibility) of the NiFeCuMo thin films in glass/Ta(5 nm)/[CoFe or NiFe(5 nm-t/2)]/NiFeCuMo(t = 0, 4, 6, 8, 10 nm)/[CoFe or NiFe(5 nm-t/2)]/Ta(5 nm) films prepared using the ion beam deposition method was determined. The magnetic properties (H{sub EC}, H{sub HS}, and {chi}) of the ferromagnetic CoFe, NiFe three-layers with an intermediate NiFeCuMo super-soft magnetic layer were strongly dependent on the thickness of the NiFeCuMo layer.

  18. Improvement of in-plane alignment for surface oxidized NiO layer on textured Ni substrate by two-step heat-treatment

    International Nuclear Information System (INIS)

    Hasegawa, Katsuya; Izumi, Toru; Izumi, Teruo; Shiohara, Yuh; Maeda, Toshihiko

    2004-01-01

    Epitaxial growth of NiO on a textured Ni substrate as a template for an REBa 2 Cu 3 O y coated conductor was investigated. Highly in-plane aligned NiO layers were successfully fabricated using a new process of a two-step heat-treatment for oxidation. In the first-step, a highly in-plane aligned thin NiO layer was formed on a textured Ni substrate under a low driving force of oxidation. Then, in the second-step, a thick NiO layer was grown at a higher rate with maintaining its high in-plane grain alignment, as if the first NiO layer acts as a seed crystal layer. Further, growth rates and microstructures of the NiO layers were studied comparatively in the cases with and without the first layer. It was found that the oxidation rate in the case with the first layer was lower than that without the first layer. The microstructure observation revealed that the NiO without the first layer was poly-crystalline with many grain-boundaries. On the other hand, in the case with the first layer, grain-boundaries of the NiO were hardly observed. Hence, the reason for this difference of the growth rate and the microstructure of the NiO layers were discussed in view of a diffusivity path

  19. Effect of NiO inserted layer on spin-Hall magnetoresistance in Pt/NiO/YIG heterostructures

    International Nuclear Information System (INIS)

    Shang, T.; Zhan, Q. F.; Yang, H. L.; Zuo, Z. H.; Xie, Y. L.; Liu, L. P.; Zhang, S. L.; Zhang, Y.; Li, H. H.; Wang, B. M.; Li, Run-Wei; Wu, Y. H.; Zhang, S.

    2016-01-01

    We investigate spin-current transport with an antiferromagnetic insulator NiO thin layer by means of the spin-Hall magnetoresistance (SMR) over a wide range of temperature in Pt/NiO/Y_3Fe_5O_1_2 (Pt/NiO/YIG) heterostructures. The SMR signal is comparable to that without the NiO layer as long as the temperature is near or above the blocking temperature of the NiO, indicating that the magnetic fluctuation of the insulating NiO is essential for transmitting the spin current from the Pt to YIG layer. On the other hand, the SMR signal becomes negligibly small at low temperature, and both conventional anisotropic magnetoresistance and the anomalous Hall resistance are extremely small at any temperature, implying that the insertion of the NiO has completely suppressed the Pt magnetization induced by the YIG magnetic proximity effect (MPE). The dual roles of the thin NiO layer are, to suppress the magnetic interaction or MPE between Pt and YIG, and to maintain efficient spin current transmission at high temperature.

  20. Effect of W addition on the electroless deposited NiP(W) barrier layer

    International Nuclear Information System (INIS)

    Tao, Yishi; Hu, Anmin; Hang, Tao; Peng, Li; Li, Ming

    2013-01-01

    Electroless deposition of NiP, NiWP thin film on p-type Si as the barrier layer to prevent the diffusion of Cu into Si was investigated. The thermal stability of the Si/Ni(W)P/Cu layers were evaluated by measuring the changes of resistance of the samples after annealed at various temperatures. XRD was applied to detect the formation of Cu 3 Si and evaluate the barrier performance of the layers. The results of XRD of the stacked Si/NiP/Cu, Si/NiWP-1/Cu, Si/NiWP–2/Cu films reveal that Cu atom could diffuse through NiP barrier layer at 450 °C, Cu could hardly diffuse through NiWP layer at 550 °C. This means that with W added in the layer, the barrier performance is improved. Although the resistance of Si/NiWP-1 and Si/NiWP-2 are higher than that of Si/NiP, the resistance of stacked layers of Si/NiWP-1/Cu and Si/NiWP–2/Cu are close to that of Si/NiP/Cu. This means that using NiWP as barrier layer is acceptable.

  1. CoCr/NiFe double layers studied by FMR and VSM

    NARCIS (Netherlands)

    Stam, M.T.H.C.W.; Gerritsma, G.J.; Lodder, J.C.; Popma, T.J.A.

    1987-01-01

    CoCr/NiFe double layers were investigated by FMR and VSM. The FMR linewidth of NiFe of the double layer is about twice that of a single NiFe layer. The resonance field is the same in both cases. Using the VSM the coercive field of the CoCr layer of the double layer was obtained. It is approximately

  2. CoCr double-layered media with NiFe and CoZrNb soft-magnetic layers (invited)

    International Nuclear Information System (INIS)

    Bernards, J.P.C.; Schrauwen, C.P.G.; Zieren, V.; Luitjens, S.B.

    1988-01-01

    The magnetic, structural, and recording properties of CoCr double-layered media are investigated. The underlayer materials NiFe (crystalline) and CoZrNb (amorphous) were combined with two different kinds of intermediate layers: Ti (crystalline) and Ge (amorphous). Applying a bias voltage during sputtering of NiFe results in a low coercivity of the NiFe layer and in a high coercivity of the CoCr layer. The structure of the NiFe layer influences the structure of the CoCr layer. A Ti layer between the NiFe and CoCr layers decreases the in-plane remanence of the CoCr layer. The coercivity of all CoZrNb layers is low, independent of the application of a bias voltage. The orientation and structure of CoCr on CoZrNb can be improved by using a Ge intermediate layer, which results in a low coercivity of the CoCr. A Ti intermediate layer increases the coercivity. Ring heads show a dependence of spike noise on the underlayer coercivity and on the applied normal force. A probe-type head shows a dependence of its output on the CoCr coercivity, which may be understood in terms of demagnetization and writing depth

  3. Monitoring Cu nodule formation using Ni marker layers

    Energy Technology Data Exchange (ETDEWEB)

    Lafouresse, M.C., E-mail: mlafouresse@gmail.co [Department of Civil and Earth Resources Engineering, Kyoto University, Katsura, Kyoto 615-8540 (Japan); Fukunaka, Y. [Institute for Nanoscience and Nanotechnology, Waseda University, Shinjuku Ku, Tokyo 169-8555 (Japan); ISS Science Project Office, JAXA, Tsukuba-shi, Ibaraki 305-8505 (Japan); Matsuoka, T. [Department of Civil and Earth Resources Engineering, Kyoto University, Katsura, Kyoto 615-8540 (Japan); Schwarzacher, W. [H. H. Wills Physics Laboratory, Tyndall Avenue, Bristol BS8 1TL (United Kingdom)

    2011-04-30

    Highlights: {yields} Ni marker layers to monitor electrodeposited Cu nodule morphological evolution. {yields} The edges of the nodules trace out a straight line. {yields} Difference in growth between spheres and hemispheres. {yields} Nodule on nodule growth at high overpotential. {yields} No dramatic effect of the diffusion layer thickness on the film morphology. - Abstract: We have used Ni marker layers to study the evolution of the characteristic spheroidal nodule morphology in electrodeposited Cu films. Ultrathin Ni layers were electrodeposited in-between Cu layers, and cross sections prepared by electrochemical polishing. During growth of a typical spheroidal feature, the edge (i.e. where there is a discontinuity in the surface slope) traces out a straight line in the cross-sectional image. At high overpotential, the cross-sections show nodule-on-nodule growth, giving rise to the well known cauliflower morphology. Rotating disk electrode studies reveal that, surprisingly, the absolute diffusion layer thickness does not appear to play a major role in the development of spheres.

  4. Monitoring Cu nodule formation using Ni marker layers

    International Nuclear Information System (INIS)

    Lafouresse, M.C.; Fukunaka, Y.; Matsuoka, T.; Schwarzacher, W.

    2011-01-01

    Highlights: → Ni marker layers to monitor electrodeposited Cu nodule morphological evolution. → The edges of the nodules trace out a straight line. → Difference in growth between spheres and hemispheres. → Nodule on nodule growth at high overpotential. → No dramatic effect of the diffusion layer thickness on the film morphology. - Abstract: We have used Ni marker layers to study the evolution of the characteristic spheroidal nodule morphology in electrodeposited Cu films. Ultrathin Ni layers were electrodeposited in-between Cu layers, and cross sections prepared by electrochemical polishing. During growth of a typical spheroidal feature, the edge (i.e. where there is a discontinuity in the surface slope) traces out a straight line in the cross-sectional image. At high overpotential, the cross-sections show nodule-on-nodule growth, giving rise to the well known cauliflower morphology. Rotating disk electrode studies reveal that, surprisingly, the absolute diffusion layer thickness does not appear to play a major role in the development of spheres.

  5. Synthesis and charge storage properties of double-layered NiSi nanocrystals

    International Nuclear Information System (INIS)

    Yoon, Jong-Hwan

    2010-01-01

    Based on bidirectional diffusion of Ni atoms, double-layered nickel silicide (NiSi) nanocrystals (NCs) for multilevel charge storage were fabricated, and their charge storage properties were examined. The double layer was produced by long-term thermal annealing (for 4 h at 900 o C) of a sandwich structure comprised of a thin Ni film of 0.3 nm sandwiched between two silicon-rich oxide (SiO 1.36 ) layers. Transmission electron microscopic image clearly exhibits a distinct NiSi nanocrystal double layer with a gap of about 7 nm between the mean positions of particle distribution in each NC layer. Capacitance-voltage measurements on the metal/oxide/semiconductor (MOS) capacitors with the double-layered NiSi nanocrystals are shown to have the apparent two plateaus of charge storage, the large memory window of about 9 V and the improved charge retention stability.

  6. Electrochemical synthesis, structure and phase composition of nano structured amorphous thin layers of NiW and Ni-Mo

    International Nuclear Information System (INIS)

    Vitina, I.; Lubane, M.; Belmane, V.; Rubene, V.; Krumina, A.

    2006-01-01

    Full text: Nano structured Ni-W thin layers containing W 6-37 wt.% were electrodeposited on a copper substratum. The W content in the layer changes, and it is determined by the electrolyte pH in the range 8.0-9.6 and the cathode current density in the range 1.0-10.0 A/dm 2 . The atomic composition and thermal stability of structure of the electrodeposited thin layers depend for the most part on the conditions of the electrodeposition and less on the W content in the layer. Cracking of the Ni-W layers electrodeposited at the electrolyte pH 8.5 and containing 34-37 wt.% W and 8.5 wt.% W was observed. The cracking increases at heating at 400 deg C for 50 h. On the contrary, no cracking of the Ni-W layer electrodeposited at the electrolyte pH 9.0 and containing 25 wt.% W was observed. The atomic composition of the layer remains practically unchanged at heating at 400 deg C for 50 h. The layer binds oxygen up to 7 wt.%. According to X-ray diffraction, in spite of the W content 35-37 wt.% in the layer, nano structured layers rather than amorphous layers were obtained which at heating at 400 deg C depending on the W content crystallises as Ni or intermetallic compounds Ni x W y if the W content is approx. 25 wt.%. Amorphous Ni-Mo alloys containing 35-52 wt.% Mo was electrodeposited on copper substratum at the cathode current densities of 0.5-1.5 A/dm2 and the electrolyte pH 6.8-8.6. Formation of thin layer (∼1-2μm) of X-ray amorphous Ni-Mo alloy, the Mo content, the characteristics of structure depend on the electrodeposition process, the electrolyte pH, and the cathode current density. The Ni-Mo layer deposited at the electrolyte pH above 8.6 and below average 6.8 had a nanocrystalline structure rather than characteristics of amorphous structure. Ni- W and Ni-Mo alloys were electrodeposited from citrate electrolyte not containing ammonium ions

  7. Formation of nickel germanides from Ni layers with thickness below 10 nm

    Energy Technology Data Exchange (ETDEWEB)

    Jablonka, Lukas; Kubart, Tomas; Primetzhofer, Daniel; Abedin, Ahmad; Hellström, Per-Erik; Östling, Mikael; Jordan-Sweet, Jean; Lavoie, Christian; Zhang, Shi-Li; Zhang, Zhen

    2017-03-01

    The authors have studied the reaction between a Ge (100) substrate and thin layers of Ni ranging from 2 to 10 nm in thickness. The formation of metal-rich Ni5Ge3Ni5Ge3 was found to precede that of the monogermanide NiGe by means of real-time in situ x-ray diffraction during ramp-annealing and ex situ x-ray pole figure analyses for phase identification. The observed sequential growth of Ni5Ge3Ni5Ge3 and NiGe with such thin Ni layers is different from the previously reported simultaneous growth with thicker Ni layers. The phase transformation from Ni5Ge3Ni5Ge3 to NiGe was found to be nucleation-controlled for Ni thicknesses <5 nm<5 nm, which is well supported by thermodynamic considerations. Specifically, the temperature for the NiGe formation increased with decreasing Ni (rather Ni5Ge3Ni5Ge3) thickness below 5 nm. In combination with sheet resistance measurement and microscopic surface inspection of samples annealed with a standard rapid thermal processing, the temperature range for achieving morphologically stable NiGe layers was identified for this standard annealing process. As expected, it was found to be strongly dependent on the initial Ni thickness

  8. The influence of local volume forces on surface relaxation of pure metals and alloys: Applications to Ni, Al, Ni3Al

    International Nuclear Information System (INIS)

    Savino, E.J.; Farkas, D.

    1987-11-01

    We present an analysis of the relative influence of the interatomic potential, lattice structure and defect symmetry on the calculated and measured distortion for the free surfaces of alloys and pure metals. In particular, the effect of using local ''volume'' dependent interactions is studied, as opposed to simple pair interatomic forces. The dependence of the relaxation on the lattice structure is examined by comparing pure metals with ordered alloys. A Green function method for surface relaxation is presented and used for the above analysis as well as for studying the influence of different surface symmetries. Examples based on computer simulation of Ni, Al and Ni 3 Al for some surface orientations are presented. (author). 33 refs, 4 figs

  9. Thermal stability of electrodeposited Ni and Ni-Co layers; an EBSD-study

    DEFF Research Database (Denmark)

    Rasmussen, Anette Alsted; Gholinia, A.; Trimby, P.W.

    2004-01-01

    The influence of heat treatment on the microstructure and the microtexture of electrodeposited Ni and Ni-Co layers was investigated with Electron Backscatter Diffraction (EBSD) with high resolution. Samples were annealed for 1 hour at 523 K and 673 K, the temperature region wherein...

  10. Sputtering yields of Si and Ni from the Ni sub(1-x)Si sub(x) system studied by Rutherford backscattering spectrometry

    Energy Technology Data Exchange (ETDEWEB)

    Kim, S C; Yamaguchi, S; Kataoka, Y; Iwami, M; Hiraki, A [Osaka Univ., Suita (Japan). Faculty of Engineering; Satou, M; Fujimoto, F

    1982-01-01

    Sputtering yields of Si and Ni from thin layer films of Ni-Si compounds (Ni sub(1-x)Si sub(x)), including the pure materials (Ni and Si), caused by 5keV Ar/sup +/ ion bombardment were investigated using backscattering spectrometry. The sputtering yield for Si from Ni sub(1-x)Si sub(x) increased with increasing Si concentration. However, there is an abrupt decrease in the yield for Si concentrations above NiSi/sub 2/ to pure Si. This is in clear contrast to the sputtering yield of Ni from Ni sub(1-x)Si sub(x) which increased with increasing Ni concentration monotonously. These results are discussed on the basis of both the difference in the atomic density and the electronic state of the alloy.

  11. Effects of Ni{sub 3}Sn{sub 4} and (Cu,Ni){sub 6}Sn{sub 5} intermetallic layers on cross-interaction between Pd and Ni in solder joints

    Energy Technology Data Exchange (ETDEWEB)

    Baek, Yong-Ho [Department of Materials Science and Engineering, Korea University, Seoul 136-713 (Korea, Republic of); Division of Advanced Circuit Interconnect, Samsung Electro-Mechanics Co., Ltd., Suwon 443-743 (Korea, Republic of); Chung, Bo-Mook [Department of Materials Science and Engineering, Korea University, Seoul 136-713 (Korea, Republic of); Department of Research and Development, KPM TECH, Ansan 425-090 (Korea, Republic of); Choi, Young-Sik [Division of Advanced Circuit Interconnect, Samsung Electro-Mechanics Co., Ltd., Suwon 443-743 (Korea, Republic of); Choi, Jaeho [Department of Advanced Metal and Materials Engineering, Gangneung-Wonju National University, Gangneung 210-702 (Korea, Republic of); Huh, Joo-Youl, E-mail: jyhuh@korea.ac.kr [Department of Materials Science and Engineering, Korea University, Seoul 136-713 (Korea, Republic of)

    2013-12-05

    Highlights: •Ni{sub 3}Sn{sub 4} acts as a source of Ni atoms, leading to a strong cross-interaction with Pd. •(Cu,Ni){sub 6}Sn{sub 5} is an effective Ni diffusion barrier, inhibiting Pd resettlement. •Dissolution kinetics of (Pd,Ni)Sn{sub 4} was interpreted based on the Sn–Ni–Pd isotherm. •Cu addition to solder alleviates the (Pd,Ni)Sn{sub 4}-related risk of reliability deterioration. -- Abstract: We examined the effects of layers of intermetallic compound (IMC) Ni{sub 3}Sn{sub 4} and (Cu,Ni){sub 6}Sn{sub 5} formed at the solder/Ni interface, on the cross-interactions between Pd and Ni during solid-state aging and reflow soldering. Two types of diffusion couples, Pd/Sn/Ni and Pd/Sn–Cu/Ni, were aged at 150 °C to study the solid-state interactions. In contrast to the Pd/Sn/Ni couples in which a Ni{sub 3}Sn{sub 4} layer formed at the Ni interface, the Pd/Sn–Cu/Ni couple where a (Cu,Ni){sub 6}Sn{sub 5} layer formed at the Ni interface exhibited no significant interaction between Pd and Ni. The (Cu,Ni){sub 6}Sn{sub 5} layer acted as an effective barrier against Ni diffusion and thus inhibited the resettlement of (Pd,Ni)Sn{sub 4} onto the Ni interface. For the interaction during reflow, Sn–3.5Ag and Sn–3.0Ag–0.5Cu solder balls were isothermally reflowed on an electroless Ni(P)/electroless Pd/immersion Au (ENEPIG) surface finish at 250 °C, and the dissolution kinetics of the (Pd,Ni)Sn{sub 4} particles converted from the 0.2-μm-thick Pd-finish layer were examined. The spalled (Pd,Ni)Sn{sub 4} particles very quickly dissolved into the molten solder when the IMC layer formed on the Ni substrate was (Cu,Ni){sub 6}Sn{sub 5} rather than Ni{sub 3}Sn{sub 4}. The dependence of the dissolution kinetics of the spalled (Pd,Ni)Sn{sub 4} particles on the IMC layers was rationalized on the basis of a Sn–Ni–Pd isotherm at 250 °C. The present study suggests that the formation of a dense (Cu,Ni){sub 6}Sn{sub 5} layer at the solder/Ni interface can effectively

  12. Magnetization switching of NiFeSiB free layers for magnetic tunnel junctions

    International Nuclear Information System (INIS)

    Chun, B.S.; Ko, S.P.; Oh, B.S.; Hwang, J.Y.; Rhee, J.R.; Kim, T.W.; Saito, S.; Yoshimura, S.; Tsunoda, M.; Takahashi, M.; Kim, Y.K.

    2006-01-01

    Ferromagnetic amorphous Ni 16 Fe 62 Si 8 B 14 layer have been studied as free layers for magnetic tunnel junctions (MTJs) to enhance cell switching performance. Traditional MTJ free layer materials such as NiFe and CoFe were also prepared for switching comparison purposes. Both NiFeSiB and NiFe resulted in an order of magnitude smaller switching fields compared to the CoFe. The switching field was further reduced for the synthetic antiferromagnetic NiFeSiB free layered structure

  13. Detachment of CVD-grown graphene from single crystalline Ni films by a pure gas phase reaction

    Science.gov (United States)

    Zeller, Patrick; Henß, Ann-Kathrin; Weinl, Michael; Diehl, Leo; Keefer, Daniel; Lippmann, Judith; Schulz, Anne; Kraus, Jürgen; Schreck, Matthias; Wintterlin, Joost

    2016-11-01

    Despite great previous efforts there is still a high need for a simple, clean, and upscalable method for detaching epitaxial graphene from the metal support on which it was grown. We present a method based on a pure gas phase reaction that is free of solvents and polymer supports and avoids mechanical transfer steps. The graphene was grown on 150 nm thick, single crystalline Ni(111) films on Si(111) wafers with YSZ buffer layers. Its quality was monitored by using low energy electron diffraction and scanning tunneling microscopy. The gas phase etching uses a chemical transport reaction, the so-called Mond process, based on the formation of gaseous nickel tetracarbonyl in 1 bar of CO at 75 °C and by adding small amounts of sulfide catalysts. X-ray photoelectron spectroscopy, Raman spectroscopy and scanning electron microscopy were used to characterize the detached graphene. It was found that the method successfully removes the nickel from underneath the graphene layer, so that the graphene lies on the insulating oxide buffer layer. Small residual particles of nickel sulfide and cracks in the obtained graphene layer were identified. The defect concentrations were comparable to graphene samples obtained by wet chemical etching and by the bubbling transfer.

  14. Atomic Layer-Deposited TiO2 Coatings on NiTi Surface

    Science.gov (United States)

    Vokoun, D.; Racek, J.; Kadeřávek, L.; Kei, C. C.; Yu, Y. S.; Klimša, L.; Šittner, P.

    2018-02-01

    NiTi shape-memory alloys may release poisonous Ni ions at the alloys' surface. In an attempt to prepare a well-performing surface layer on an NiTi sample, the thermally grown TiO2 layer, which formed during the heat treatment of NiTi, was removed and replaced with a new TiO2 layer prepared using the atomic layer deposition (ALD) method. Using x-ray photoelectron spectroscopy, it was found that the ALD layer prepared at as low a temperature as 100 °C contained Ti in oxidation states + 4 and + 3. As for static corrosion properties of the ALD-coated NiTi samples, they further improved compared to those covered by thermally grown oxide. The corrosion rate of samples with thermally grown oxide was 1.05 × 10-5 mm/year, whereas the corrosion rate of the ALD-coated samples turned out to be about five times lower. However, cracking of the ALD coating occurred at about 1.5% strain during the superelastic mechanical loading in tension taking place via the propagation of a localized martensite band.

  15. Effect of Ti seed and spacer layers on structure and magnetic properties of FeNi thin films and FeNi-based multilayers

    Energy Technology Data Exchange (ETDEWEB)

    Svalov, A.V., E-mail: andrey.svalov@ehu.es [Departamento de Electricidad y Electrónica, Universidad del País Vasco (UPV/EHU), 48080 Bilbao (Spain); Department of Magnetism and Magnetic Nanomaterials, Ural Federal University, 620002 Ekaterinburg (Russian Federation); Larrañaga, A. [SGIker, Servicios Generales de Investigación, Universidad del País Vasco (UPV/EHU), 48080 Bilbao (Spain); Kurlyandskaya, G.V. [Departamento de Electricidad y Electrónica, Universidad del País Vasco (UPV/EHU), 48080 Bilbao (Spain); Department of Magnetism and Magnetic Nanomaterials, Ural Federal University, 620002 Ekaterinburg (Russian Federation)

    2014-10-15

    Highlights: • Fe{sub 19}Ni{sub 81} films and FeNi-based multilayers were prepared by magnetron sputtering. • The samples were deposited onto glass substrates at room temperature. • Ti/FeNi films exhibit good (1 1 1) texture and crystallinity. • The thick Cu seed increases the coercive force of the magnetic layer. • The thin Ti spacer restores the magnetic softness of the Cu/Ti/FeNi multilayers. - Abstract: The microstructure and magnetic properties of sputtered permalloy films and FeNi-based multilayers prepared by magnetron sputtering have been studied. X-ray diffraction measurements indicate that Ti/FeNi films exhibit good (1 1 1) texture and crystallinity. Ti/FeNi bilayers with high crystallographic quality have relatively low resistivity. The Ti seed layer does not influence the magnetic properties of FeNi film in Ti/FeNi bilayers, but the thick Cu seed layer leads to an increase of the coercive force of the magnetic layer. For the FeNi films deposited on thick Cu seed layer, the (0 1 0) and (0 0 2) diffraction peaks of hcp nickel were clearly observed. The thin Ti spacer between Cu and FeNi layers prevents the formation of the nickel phase and restores the magnetic softness of the FeNi layer in the Cu/Ti/FeNi sample. Obtained results can be important for the development of multilayer sensitive elements for giant magnetoimpedance or magnetoresistance detectors.

  16. Growth of intermetallics between Sn/Ni/Cu, Sn/Ag/Cu and Sn/Cu layered structures

    International Nuclear Information System (INIS)

    Horváth, Barbara; Illés, Balázs; Shinohara, Tadashi

    2014-01-01

    Intermetallic growth mechanisms and rates are investigated in Sn/Ni/Cu, Sn/Ag/Cu and Sn/Cu layer systems. An 8–10 μm thick Sn surface finish layer was electroplated onto a Cu substrate with a 1.5–2 μm thick Ni or Ag barrier layer. In order to induce intermetallic layer growth, the samples were aged in elevated temperatures: 50 °C and 125 °C. Intermetallic layer growth was checked by focused ion beam–scanning ion microscope. The microstructures and chemical compositions of the intermetallic layers were observed with a transmission electron microscope. It has been found that Ni barrier layers can effectively block the development of Cu 6 Sn 5 intermetallics. The intermetallic growth characteristics in the Sn/Cu and Sn/Ni/Cu systems are very similar. The intermetallic layer grows towards the Sn layer and forms a discrete layer. Differences were observed only in the growth gradients and surface roughness of the intermetallic layer which may explain the different tin whiskering properties. It was observed that the intermetallic layer growth mechanisms are completely different in the Ag barrier layers compared to the Ni layers. In the case of Sn/Ag/Cu systems, the Sn and Cu diffused through the Ag layer, formed Cu 6 Sn 5 intermetallics mainly at the Sn/Ag interface and consumed the Ag barrier layer. - Highlights: • Intermetallic growth was characterised in Sn/Ni/Cu, Sn/Ag/Cu and Sn/Cu layer systems. • Intermetallic growth rates and roughness are similar in the Sn/Cu and Sn/Ni/Cu systems. • Sn/Ni/Cu system contains the following intermetallic layer structure Sn–Ni3Sn4–Ni3Sn2–Ni3Sn–Ni. • In the case of Sn/Ag/Cu systems the Sn and Cu diffusion consumes the Ag barrier layer. • When Cu reaches the Sn/Ag interface a large amount of Cu 6 Sn 5 forms above the Ag layer

  17. A comparative study of humidity sensing and photocatalytic applications of pure and nickel (Ni)-doped WO{sub 3} thin films

    Energy Technology Data Exchange (ETDEWEB)

    Ramkumar, S. [Bannari Amman Institute of Technology, Department of Physics, Erode, Tamilnadu (India); Rajarajan, G. [Vidhya Mandhir Institute of Technology, Department of Physics, Erode, Tamilnadu (India)

    2017-06-15

    Nanocrystalline of pristine and nickel (Ni)-doped tungsten trioxide (WO{sub 3}) thin films was deposited by chemical bath deposition method. The concentrations of Ni ions were varied from 0 to 10 wt%. In order to improve the crystallinity of the films were annealed at 600 C for 2 h in the ambient atmosphere. X-ray diffraction results reveal that the WO{sub 3} doped with nickel crystallizes in monoclinic structure and the results are in good agreement with the standard JCPDS data (card no: 83-0951). AFM micrographs reveal that average grain size of about 27-39 nm for pure and Ni-doped WO{sub 3} thin films. In addition, the band gap of the Ni-doped WO{sub 3} nanostructures is facilely tunable by controlling the Ni contents. The humidity sensor setup was fabricated and measured for pure and Ni-doped WO{sub 3} thin film sensor with various level of RH (10-90%). The Ni-doped WO{sub 3} sensor showed fast response and high sensitivity than pure WO{sub 3}. The photocatalytic activities of the films were evaluated by degradation of methyl orange, methylene blue and phenol in an aqueous solution under visible light irradiation. The photocatalytic activity of WO{sub 3} nanostructures could be remarkably enhanced by doping the Ni impurity. (orig.)

  18. Deposition of Chitosan Layers on NiTi Shape Memory Alloy

    Directory of Open Access Journals (Sweden)

    Kowalski P.

    2015-04-01

    Full Text Available The NiTi shape memory alloys have been known from their application in medicine for implants as well as parts of medical devices. However, nickel belongs to the family of elements, which are toxic. Apart from the fact that nickel ions are bonded with titanium into intermetallic phase, their presence may cause allergy. In order to protect human body against release of nickel ions a surface of NiTi alloy can be modified with use of titanium nitrides, oxides or diamond-like layers. On the one hand the layers can play protective role but on the other hand they may influence shape memory behavior. Too stiff or too brittle layer can lead to limiting or completely blocking of the shape recovery. It was the reason to find more elastic covers for NiTi surface protection. This feature is characteristic for polymers, especially, biocompatible ones, which originate in nature. In the reported paper, the chitosan was applied as a deposited layer on surface of the NiTi shape memory alloy. Due to the fact that nature of shape memory effect is sensitive to thermo and/or mechanical treatments, the chitosan layer was deposited with use of electrophoresis carried out at room temperature. Various deposition parameters were checked and optimized. In result of that thin chitosan layer (0.45µm was received on the NiTi alloy surface. The obtained layers were characterized by means of chemical and phase composition, as well as surface quality. It was found that smooth, elastic surface without cracks and/or inclusions can be produced applying 10V and relatively short deposition time - 30 seconds.

  19. Intercalation of vanadate in Ni, Zn layered hydroxyacetates

    International Nuclear Information System (INIS)

    Rojas, Ricardo; Barriga, Cristobalina; Ulibarri, M.A.; Rives, Vicente

    2004-01-01

    Interlayer acetate anions in layered double hydroxyacetates of Ni 2+ and Zn 2+ have been exchanged by oxovanadates following three synthetic routes (at 60 deg. C, under hydrothermal conditions and after preswelling with caprylate anions) and different pH; direct exchange at room temperature was not successful. Complete exchange was achieved under adequated conditions, and the precise nature of the interlayer anion depends on the pH during exchange: at low pH (4.5), the presence of α-VO 3 chains, with anchoring (grafting) of the species to the hydroxide layers, is proposed. At higher pH (9.5) V 2 O 7 4- species are present in the interlayer. Thermal decomposition of these vanadate-intercalated products leads to formation of orthorhombic Ni 2+ and Zn 2+ vanadates, together with NiO

  20. Microstructure and mechanical behavior of a shape memory Ni-Ti bi-layer thin film

    Energy Technology Data Exchange (ETDEWEB)

    Mohri, Maryam [School of Metallurgy and Materials Engineering, College of Engineering, University of Tehran, Tehran (Iran, Islamic Republic of); Karlsruhe Institute of Technology, Institute of Nanotechnology, 76021 Karlsruhe (Germany); Nili-Ahmadabadi, Mahmoud, E-mail: nili@ut.ac.ir [School of Metallurgy and Materials Engineering, College of Engineering, University of Tehran, Tehran (Iran, Islamic Republic of); Center of Excellence for High Performance Materials, University of Tehran, Tehran (Iran, Islamic Republic of); Ivanisenko, Julia [Karlsruhe Institute of Technology, Institute of Nanotechnology, 76021 Karlsruhe (Germany); Schwaiger, Ruth [Karlsruhe Institute of Technology, Institute for Applied Materials, 76021 Karlsruhe (Germany); Hahn, Horst; Chakravadhanula, Venkata Sai Kiran [Karlsruhe Institute of Technology, Institute of Nanotechnology, 76021 Karlsruhe (Germany)

    2015-05-29

    Two different single-layers and a bi-layer Ni-Ti thin films with chemical compositions of Ni{sub 45}Ti{sub 50}Cu{sub 5}, Ni{sub 50.8}Ti{sub 49.2} and Ni{sub 50.8}Ti{sub 49.2}/Ni{sub 45}Ti{sub 50}Cu{sub 5} (numbers indicate at.%) determined by energy dispersive X-ray spectroscopy were deposited on Si (111) substrates using DC magnetron sputtering. The structures, surface morphology and transformation temperatures of annealed thin films at 500 °C for 15 min and 1 h were studied using grazing incidence X-ray diffraction, transmission electron microscopy (TEM), atomic force microscopy and differential scanning calorimetry (DSC), respectively. Nanoindentation was used to characterize the mechanical properties. The DSC and X-ray diffraction results indicated the austenitic structure of the Ni{sub 50.8}Ti{sub 49.2} and martensitic structure of the Ni{sub 45}Ti{sub 50}Cu{sub 5} thin films while the bi-layer was composed of austenitic and martensitic thin films. TEM study revealed that copper encourages crystallization in the bi-layer such that crystal structure containing nano-precipitates in the Ni{sub 45}Ti{sub 50}Cu{sub 5} layer was detected after 15 min annealing while the Ni{sub 50.8}Ti{sub 49.2} layer crystallized after 60 min at 500 °C. Furthermore, after annealing at 500 °C for 15 min, a precipitate free zone and thin layer amorphous were observed closely to the interface in the top layer. The bi-layer was completely crystallized at 500 °C for 1 h and the orientation of the Ni-rich precipitates indicated a stress gradient in the bi-layer. The bi-layer thin film showed different transformation temperatures and mechanical behavior from the single-layers. The developed bi-layer has different phase transformation temperatures, the higher temperatures of shape memory effect and lower temperature of pseudo-elastic behavior compared to the single-layers. Also, the bi-layer thin film exhibited a combined pseudo-elastic behavior and shape memory effect with a reduced

  1. Preparation and characterization of 6-layered functionally graded nickel-alumina (Ni-Al2O3) composites

    Science.gov (United States)

    Latiff, M. I. A.; Nuruzzaman, D. M.; Basri, S.; Ismail, N. M.; Jamaludin, S. N. S.; Kamaruzaman, F. F.

    2018-04-01

    The present research study deals with the preparation of 6-layered functionally graded (FG) metal-ceramic composite materials through powder metallurgy technique. Using a cylindrical die-punch set made of steel, the nickel-alumina (Ni-Al2O3) graded composite structure was fabricated. The samples consist of four gradual inter layers of varied nickel composition (80wt.%, 60wt.%, 40wt.%, 20wt.%) sandwiched with pure Ni and Al2O3 powders at the ends (100wt.% and 0wt.% nickel) were fabricated under 30 ton compaction load using a hydraulic press. After that, two-step sintering was carried out at sintering temperature 1200ºC and soaking time 3 hours was maintained in a tube furnace. The properties of the prepared samples were characterized by radial shrinkage, optical microscopy and hardness testing. Results showed that larger shrinkage occurred within the ceramic phase which proves that more porosities were eliminated in the ceramic rich layers. From the microstructural analysis, it was observed that alumina particles are almost uniformly distributed in nickel matrix, so as nickel particles in the ceramic matrix of alumina-dominant layers. From interfacial analyses, it was observed that a smooth transition in microstructure from one layer to the next confirms a good interfacial solid state bonding between metal-ceramic constituents and good compaction process. On the other hand, microhardness test results suggest that there might be increasing percentage of porosities in the graded structure as the ceramic content rises.

  2. Single-layer and double-layer microwave absorbers based on Co{sub 67}Ni{sub 33} microspheres and Ni{sub 0.6}Zn{sub 0.4}Fe{sub 2}O{sub 4} nanocrystals

    Energy Technology Data Exchange (ETDEWEB)

    Wang, Min [Engineering Technology Research Center of Magnetic Materials of Anhui Province, School of Physics & Materials Science, Anhui University, Hefei 230601 (China); Wang, Zhongzhu, E-mail: wangzz@ahu.edu.cn [Engineering Technology Research Center of Magnetic Materials of Anhui Province, School of Physics & Materials Science, Anhui University, Hefei 230601 (China); Wang, Peihong; Liao, Yanlin [Engineering Technology Research Center of Magnetic Materials of Anhui Province, School of Physics & Materials Science, Anhui University, Hefei 230601 (China); Bi, Hong [School of Chemistry and Chemical Engineering, Anhui University, Hefei 230601 (China)

    2017-03-01

    Co{sub 67}Ni{sub 33} microspheres and Ni{sub 0.6}Zn{sub 0.4}Fe{sub 2}O{sub 4} nanocrystals were synthesized by hydrothermal method. The complex permeability and complex permittivity of the as-prepared powders dispersing in wax (60 wt% powder) were measured using a vector network analyzer in 2–18 GHz frequency range. The calculated microwave absorption of single-layer and double-layer absorbers based on Co{sub 67}Ni{sub 33} microspheres and Ni{sub 0.6}Zn{sub 0.4}Fe{sub 2}O{sub 4} nanocrystals were analyzed in 2–18 GHz frequency range. The results show that the Ni{sub 0.6}Zn{sub 0.4}Fe{sub 2}O{sub 4}nanocrystals with the relatively low permittivity and Co{sub 67}Ni{sub 33} microspheres with the relatively high dielectric loss and magnetic loss can be used as proper matching layer and excellent absorption layer, respectively. The double-layer absorber with a coating thickness of 2.1 mm exhibits a maximum reflection loss of −43.8 dB as well as a bandwidth (reflection loss less than −10 dB) of 5 GHz. Moreover, their absorption peak and the absorption intensity can be adjusted easily through changing the stacking order and each layer thickness. - Highlights: • Ni-Zn ferrite nanocrystals can use as matching layer in double-layer absorbers. • Co{sub 67}Ni{sub 33} microspheres with high dielectric loss can use as absorption layer. • Double-layer absorbers exhibits an excellent microwave absorption in 2–18 GHz.

  3. Cr-Ni ALLOY ELECTRODEPOSITION AND COMPARISON WITH CONVENTIONAL PURE Cr COATING TECHNIQUE

    Directory of Open Access Journals (Sweden)

    M. Moniruzzaman

    2012-12-01

    Full Text Available Cr coating is widely used as the outer surface of precision parts due to its attractive appearance and superior corrosion resistance properties. It is obtained by electrodeposition via a conventional bath with hexavalent Cr ions. This manufacturing technique has many drawbacks, such as very low efficiency and high operating temperature and it is hazardous to health. In this work, we studied a Cr-Ni alloy deposition technique and compared the alloy coating properties to those with conventional Cr coating. Sequential two-step alloy electrodeposition was also compared. We took varying concentrations of Cr, Ni and complexing agents for the electrodeposition of Cr-Ni alloy and sequential Cr-Ni alloy coating on mild steel. Operating parameters, i.e. current density and temperature, were varied to examine their effects on the coating properties. The coatings thus obtained were characterized by visual observation, corrosion test, microhardness measurement, morphology and chemical analysis. The Cr-Ni alloy coating was found to be more corrosion resistant in 5% NaCl solution and harder than the pure Cr coating obtained by conventional electrodeposition. Toxic gas was produced in a much lower extent in the alloy coating than the conventional Cr coating technique. Again, the two-step Cr-Ni alloy coating was found better in terms of corrosion resistance as well as hardness compared to the Cr-Ni alloy coating. The process was also found to be much more environmentally friendly.

  4. Fabrication of Ni-Al/diamond composite based on layered and gradient structures of SHS system

    Directory of Open Access Journals (Sweden)

    Lu Jiafeng

    2017-01-01

    Full Text Available In this paper layered and gradient structures of Ni-Al SHS system were adopted to manufacture Ni-Al/diamond composites. The effect of the layered and the diamond mesh gradient structures of Ni-Al/diamond on the SHS process and the microstructure of the composites were investigated. It is found that with the increasing of the number of layers, the combustion wave velocity is decreased. The combustion wave velocity for diamond mesh size gradient structure of Ni-Al SHS is faster than that for the layered structure. A well bonding can be formed between diamond and the matrix in layered and gradient structure Ni-Al/diamond composites due to the melt of Ni-Cr brazing alloy.

  5. Segregation and stability at Pt3Ni(1 1 1) surfaces and Pt75Ni25 nanoparticles

    International Nuclear Information System (INIS)

    Fowler, Ben; Lucas, Christopher A.; Omer, Ahmed; Wang, Guofeng; Stamenkovic, Vojislav R.; Markovic, Nenad M.

    2008-01-01

    Using in situ surface X-ray diffraction we have determined the atomic structure and stability of a Pt 3 Ni(1 1 1) surface in the electrochemical environment. Surface segregation leads to a pure Pt(1 1 1) skin with enrichment of Ni in the sub-surface atomic layer that determines the surface electronic structure. The Pt-skin surface exhibits inward relaxation upon the adsorption of oxygenated species and this explains the surface stability compared to pure Pt(1 1 1). Using Monte Carlo calculations it is shown that nanoparticles with the same surface composition and stochiometry are energetically stable

  6. Polyhedral-Like NiMn-Layered Double Hydroxide/Porous Carbon as Electrode for Enhanced Electrochemical Performance Supercapacitors.

    Science.gov (United States)

    Yu, Mei; Liu, Ruili; Liu, Jianhua; Li, Songmei; Ma, Yuxiao

    2017-11-01

    Polyhedral-like NiMn-layered double hydroxide/porous carbon (NiMn-LDH/PC-x) composites are successfully synthesized by hydrothermal method (x = 1, 2 means different mass percent of porous carbon (PC) in composites). The NiMn-LDH/PC-1 composites possess specific capacitance 1634 F g -1 at a current density of 1 A g -1 , and it is much better than that of pure LDH (1095 F g -1 at 1 A g -1 ). Besides, the sample can retain 84.58% of original capacitance after 3000 cycles at 15 A g -1 . An asymmetric supercapacitor with NiMn-LDH/PC-1 as anode and activated carbon as cathode is fabricated, and the supercapacitor can achieve an energy density of 18.60 Wh kg -1 at a power density of 225.03 W kg -1 . The enhanced electrochemical performance attributes to the high faradaic pseudocapacitance of NiMn-LDH, the introduction of PC, and the 3D porous structure of LDH/PC-1 composites. The introduction of PC hinders serious agglomeration of LDH and further accelerates ions transport. The encouraging results indicate that these materials are one of the most potential candidates for energy storage devices. © 2017 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

  7. Comparative in vitro biocompatibility of nickel-titanium, pure nickel, pure titanium, and stainless steel: genotoxicity and atomic absorption evaluation.

    Science.gov (United States)

    Assad, M; Lemieux, N; Rivard, C H; Yahia, L H

    1999-01-01

    The genotoxicity level of nickel-titanium (NiTi) was compared to that of its pure constituents, pure nickel (Ni) and pure titanium (Ti) powders, and also to 316L stainless steel (316L SS) as clinical reference material. In order to do so, a dynamic in vitro semiphysiological extraction was performed with all metals using agitation and ISO requirements. Peripheral blood lymphocytes were then cultured in the presence of all material extracts, and their comparative genotoxicity levels were assessed using electron microscopy-in situ end-labeling (EM-ISEL) coupled to immunogold staining. Cellular chromatin exposition to pure Ni and 316L SS demonstrated a significantly stronger gold binding than exposition to NiTi, pure Ti, or the untreated control. In parallel, graphite furnace atomic absorption spectrophotometry (AAS) was also performed on all extraction media. The release of Ni atoms took the following decreasing distribution for the different resulting semiphysiological solutions: pure Ni, 316L SS, NiTi, Ti, and controls. Ti elements were detected after elution of pure titanium only. Both pure titanium and nickel-titanium specimens obtained a relative in vitro biocompatibility. Therefore, this quantitative in vitro study provides optimistic results for the eventual use of nickel-titanium alloys as surgical implant materials.

  8. Investigation on corrosion and wear behaviors of nanoparticles reinforced Ni-based composite alloying layer

    International Nuclear Information System (INIS)

    Xu Jiang; Tao Jie; Jiang Shuyun; Xu Zhong

    2008-01-01

    In order to investigate the role of amorphous SiO 2 particles in corrosion and wear resistance of Ni-based metal matrix composite alloying layer, the amorphous nano-SiO 2 particles reinforced Ni-based composite alloying layer has been prepared by double glow plasma alloying on AISI 316L stainless steel surface, where Ni/amorphous nano-SiO 2 was firstly predeposited by brush plating. The composition and microstructure of the nano-SiO 2 particles reinforced Ni-based composite alloying layer were analyzed by using SEM, TEM and XRD. The results indicated that the composite alloying layer consisted of γ-phase and amorphous nano-SiO 2 particles, and under alloying temperature (1000 deg. C) condition, the nano-SiO 2 particles were uniformly distributed in the alloying layer and still kept the amorphous structure. The corrosion resistance of composite alloying layer was investigated by an electrochemical method in 3.5%NaCl solution. Compared with single alloying layer, the amorphous nano-SiO 2 particles slightly decreased the corrosion resistance of the Ni-Cr-Mo-Cu alloying layer. X-ray photoelectron spectroscopy (XPS) revealed that the passive films formed on the composite alloying consisted of Cr 2 O 3 , MoO 3 , SiO 2 and metallic Ni and Mo. The dry wear test results showed that the composite alloying layer had excellent friction-reduced property, and the wear weight loss of composite alloying layer was less than 60% of that of Ni-Cr-Mo-Cu alloying layer

  9. Ultrathin NiO/NiFe2O4 Nanoplates Decorated Graphene Nanosheets with Enhanced Lithium Storage Properties

    International Nuclear Information System (INIS)

    Du, Dejian; Yue, Wenbo; Fan, Xialu; Tang, Kun; Yang, Xiaojing

    2016-01-01

    Highlights: • Ultrathin NiO/NiFe 2 O 4 nanoplates derived from NiFe layered double hydroxides are fabricated on the graphene. • NiO/NiFe 2 O 4 nanoplates on the graphene show superior electrochemical performance compared to pure NiO/NiFe 2 O 4 aggregates. • The effects of the content and the particle size/component of NiO/NiFe 2 O 4 on the electrochemical performances are studied. • Graphene-encapsulated NiO/NiFe 2 O 4 is prepared and shows slightly decreased performance compared to graphene-based composite. - Abstract: As anode materials for lithium-ion batteries, bicomponent metal oxide composites show high reversible capacities; but the morphology and particle size of the composites are hardly controllable, which may reduce their electrochemical properties. In this work, ultrathin NiO/NiFe 2 O 4 nanoplates with a diameter of 5 ∼ 7 nm and a thickness of ∼2 nm are controllably fabricated on the graphene derived from NiFe layered double hydroxides (NiFe-LDHs), and exhibit superior electrochemical performance compared to pure NiO/NiFe 2 O 4 aggregates without graphene. The nanosized NiO and NiFe 2 O 4 plates are separated from each other and the graphene substrate can prevent the aggregation of NiO/NiFe 2 O 4 as well as enhance the electronic conductivity of the composite, which is beneficial to improving the electrochemical performance. Moreover, the effects of the content and the particle size/component of NiO/NiFe 2 O 4 on the electrochemical performances are also studied in order to achieve optimal performance. Ultrathin NiO/NiFe 2 O 4 nanoplates are further encapsulated by graphene nanosheets and show slightly decreased performance compared to those supported by graphene nanosheets. The different electrochemical behaviors of graphene-containing composites may be attributed to the different interactions between graphene nanosheets and NiO/NiFe 2 O 4 nanoplates.

  10. NiTiCu/AlN/NiTiCu shape memory thin film heterostructures for vibration damping in MEMS

    Energy Technology Data Exchange (ETDEWEB)

    Kaur, Navjot; Kaur, Davinder, E-mail: dkaurfph@iitr.ernet.in

    2014-03-25

    Highlights: • Fabrication of NiTiCu/AlN/NiTiCu heterostructure using dc/rf magnetron sputtering. • Exhibits highest hardness (38 GPa) and elastic modulus (187 GPa). • Enhanced dissipation of mechanical energy (E{sub d} = 5.7 N J). • High damping capacity (0.052) and figure of merit (∼0.62). • Can be applied for vibration damping in MEMS. -- Abstract: Shape memory alloy (NiTiCu) thin films coupled with piezoelectric AlN layer produce an intelligent material for vibration damping. In the present study pure NiTiCu, NiTiCu/AlN and NiTiCu/AlN/NiTiCu heterostructures have been deposited on Si substrate using magnetron sputtering technique. By the use of the interfaces and shape memory effect provided by NiTiCu layers, the damping capacity can be increased along with increase in stiffness and mechanical hardness. The heterostructures were characterized in terms of structural, electrical, morphological and mechanical properties by X-ray diffraction (XRD), four probe resistivity method, atomic force microscopy, field emission scanning electron microscopy, and nanoindentation. The NiTiCu/AlN/NiTiCu heterostructure exhibit enhanced mechanical and damping properties as compared to NiTiCu/AlN and pure NiTiCu. This enhancement in hardness and damping of the heterostructure could be attributed to the shape memory effect of NiTiCu, intrinsic piezoelectricity of AlN and increased number of interfaces in heterostructure that help in dissipation of mechanical vibrations. The findings of this work provide additional impetus for the application of these heterostructures in emerging fields of nanotechnology and microelectro mechanical (MEMS) devices.

  11. NiTiCu/AlN/NiTiCu shape memory thin film heterostructures for vibration damping in MEMS

    International Nuclear Information System (INIS)

    Kaur, Navjot; Kaur, Davinder

    2014-01-01

    Highlights: • Fabrication of NiTiCu/AlN/NiTiCu heterostructure using dc/rf magnetron sputtering. • Exhibits highest hardness (38 GPa) and elastic modulus (187 GPa). • Enhanced dissipation of mechanical energy (E d = 5.7 N J). • High damping capacity (0.052) and figure of merit (∼0.62). • Can be applied for vibration damping in MEMS. -- Abstract: Shape memory alloy (NiTiCu) thin films coupled with piezoelectric AlN layer produce an intelligent material for vibration damping. In the present study pure NiTiCu, NiTiCu/AlN and NiTiCu/AlN/NiTiCu heterostructures have been deposited on Si substrate using magnetron sputtering technique. By the use of the interfaces and shape memory effect provided by NiTiCu layers, the damping capacity can be increased along with increase in stiffness and mechanical hardness. The heterostructures were characterized in terms of structural, electrical, morphological and mechanical properties by X-ray diffraction (XRD), four probe resistivity method, atomic force microscopy, field emission scanning electron microscopy, and nanoindentation. The NiTiCu/AlN/NiTiCu heterostructure exhibit enhanced mechanical and damping properties as compared to NiTiCu/AlN and pure NiTiCu. This enhancement in hardness and damping of the heterostructure could be attributed to the shape memory effect of NiTiCu, intrinsic piezoelectricity of AlN and increased number of interfaces in heterostructure that help in dissipation of mechanical vibrations. The findings of this work provide additional impetus for the application of these heterostructures in emerging fields of nanotechnology and microelectro mechanical (MEMS) devices

  12. First-principles study of oxygen evolution reaction on Co doped NiFe-layered double hydroxides

    Science.gov (United States)

    Yu, Jie; Perdew, John; Yan, Qimin

    The conversion of solar energy to renewable fuels is a grand challenge. One of the crucial steps for this energy conversion process is the discovery of efficient catalysts with lower overpotential for the oxygen evolution reaction (OER). Layered double hydroxides (LDH) with earth abundant elements such as Ni and Fe have been found as promising OER catalysts and shown to be active for water oxidation. Doping is one of the feasible ways to even lower the overpotential of host materials and breaks the linear scaling law. In this talk we'll present our study on the reaction mechanism of OER on pure and Co-doped NiFe-LDH systems in alkaline solution. We study the absorption energetics of reaction intermediate states and calculate the thermodynamic reaction energy using density functional theory with the PBE +U and the newly developed SCAN functionals. It is shown that the NiFe-LDH system with Co dopants has lower overpotential and higher activity compared with the undoped system. The improvement in activity is related to the presence of Co states in the electronic structure. The work provides a clear clue for the further improvement of the OER activity of LDH systems by chemical doping. The work was supported as part of the Center for the Computational Design of Functional Layered Materials, an Energy Frontier Research Center funded by the U.S. Department of Energy, Office of Science.

  13. Diffusion of Ni, Ga, and As in the surface layer of GaAs and characteristics of the Ni/GaAs contact

    International Nuclear Information System (INIS)

    Uskov, V.A.; Fedotov, A.B.; Erofeeva, E.A.; Rodionov, A.I.; Dzhumakulov, D.T.

    1987-01-01

    The authors investigate the low-temperature codiffusion of Ni, Ga, and As in the surface layer of gallium arsenide and study its effect on the current-voltage characteristics of a Ni/GaAs rectifier contact. The concentration distribution of atoms in the function layer of a Ni-GaAs system was investigated by the methods of layerwise radiometric and neutron-activation analyses. It was found that interdiffusion of components takes place in the Ni-GaAs system in an elastic stress field, generated by the differences in the lattice parameters and thermal-expansion coefficients of Ni, GaAs, and the intermetallic compound which form. The form and parameters of the current-voltage characteristics of a Ni/GaAs contact are determined by the phase composition and the structure of the junction layer

  14. Electroless deposition of NiCrB diffusion barrier layer film for ULSI-Cu metallization

    Energy Technology Data Exchange (ETDEWEB)

    Wang, Yuechun [School of Materials Science and Engineering, Yunnan University, Kunming (China); Chen, Xiuhua, E-mail: chenxh@ynu.edu.cn [School of Materials Science and Engineering, Yunnan University, Kunming (China); Ma, Wenhui [National Engineering Laboratory of Vacuum Metallurgy, Kunming University of Science and Technology, Kunming (China); Shang, Yudong; Lei, Zhengtao; Xiang, Fuwei [School of Materials Science and Engineering, Yunnan University, Kunming (China)

    2017-02-28

    Highlights: • In this paper, the electroless deposited NiCrB thin film was mainly in the form of NiB, CrB{sub 2} compounds and elementary Ni. • The sheet resistance of NiCrB thin film was 3.043 Ω/□, it is smaller than that of the widely used Ta, TaN and TiN diffusion barrier layers. • Annealing experiments showed that the failure temperature of NiCrB thin film regarding Cu diffusion was 900 °C. • NiCrB barrier layer crystallized after 900 °C annealing, Cu grains arrived at Si-substrate through grain boundaries, resulting in the formation of Cu{sub 3}Si. • Eelectroless deposited NiCrB film also had good oxidation resistance, it is expected to become an anti-oxidant layer of copper interconnection. - Abstract: NiCrB films were deposited on Si substrates using electroless deposition as a diffusion barrier layer for Cu interconnections. Samples of the prepared NiCrB/SiO{sub 2}/Si and NiCrB/Cu/NiCrB/SiO{sub 2}/Si were annealed at temperatures ranging from 500 °C to 900 °C. The reaction mechanism of the electroless deposition of the NiCrB film, the failure temperature and the failure mechanism of the NiCrB diffusion barrier layer were investigated. The prepared samples were subjected to XRD, XPS, FPP and AFM to determine the phases, composition, sheet resistance and surface morphology of samples before and after annealing. The results of these analyses indicated that the failure temperature of the NiCrB barrier film was 900 °C and the failure mechanism led to crystallization and grain growth of the NiCrB barrier layer after high temperature annealing. It was found that this process caused Cu grains to reach Si substrate through the grain boundaries, and then the reaction between Cu and Si resulted in the formation of highly resistive Cu{sub 3}Si.

  15. Characteristics of magnetic tunnel junctions comprising ferromagnetic amorphous NiFeSiB layers

    International Nuclear Information System (INIS)

    Chun, B.S.; Kim, Y.K.; Hwang, J.Y.; Yim, H.I.; Rhee, J.R.; Kim, T.W.

    2007-01-01

    Magnetic tunnel junctions (MTJs), which consisted of amorphous ferromagnetic Ni 16 Fe 62 Si 8 B 14 free layers, were investigated. NiFeSiB has a lower saturation magnetization (M s : 800 emu/cm 3 ) than Co 90 Fe 10 and a higher anisotropy constant (K u : 2700 erg/cm 3 ) than Ni 80 Fe 20 . By increasing the free layer thickness, the tunnel magnetoresistance (TMR) ratio of up to 41% was achieved and it exhibited a much lower switching field (H sw ) than the conventionally used CoFe free layer MTJ. Furthermore, by inserting a thin CoFe layer (1 nm) at the tunnel barrier/NiFeSiB interface, the TMR ratio and switching squareness were enhanced

  16. Ultrathin highly uniform Ni(Al) germanosilicide layer with modulated B8 type Ni5(SiGe)3 phase formed on strained Si1−xGex layers

    International Nuclear Information System (INIS)

    Liu, Linjie; Xu, Dawei; Jin, Lei; Knoll, Lars; Wirths, Stephan; Nichau, Alexander; Buca, Dan; Mussler, Gregor; Holländer, Bernhard; Zhao, Qing-Tai; Mantl, Siegfried; Feng Di, Zeng; Zhang, Miao

    2013-01-01

    We present a method to form ultrathin highly uniform Ni(Al) germanosilicide layers on compressively strained Si 1−x Ge x substrates and their structural characteristics. The uniform Ni(Al) germanosilicide film is formed with Ni/Al alloy at an optimized temperature of 400 °C with an optimized Al atomic content of 20 at. %. We find only two kinds of grains in the layer. Both grains show orthogonal relationship with modified B8 type phase. The growth plane is identified to be (10-10)-type plane. After germanosilicidation the strain in the rest Si 1−x Ge x layer is conserved, which provides a great advantage for device application

  17. Preparation and characterization of self-assembled layer by layer NiCo2O4–reduced graphene oxide nanocomposite with improved electrocatalytic properties

    International Nuclear Information System (INIS)

    Srivastava, Manish; Elias Uddin, Md.; Singh, Jay; Kim, Nam Hoon; Lee, Joong Hee

    2014-01-01

    Graphical abstract: NiCo 2 O 4 were grown on RGO by in situ synthesis process. FE-SEM investigation revealed self assembled layer by layer growth of NiCo 2 O 4 –RGO nanocomposite. NiCo 2 O 4 –RGO nanocomposite exhibited synergetic effect of NiCo 2 O 4 nanoparticles and RGO on its electrochemical performance. -- Highlights: • NiCo 2 O 4 were grown on RGO by in-situ synthesis process. • FE-SEM image revealed self-assembled layer by layer growth of NiCo 2 O 4 -RGO nanocomposite. • NiCo 2 O 4 -RGO nanocomposite exhibited synergetic effects on its electrochemical performance. -- Abstract: NiCo 2 O 4 nanoparticles dispersed on reduced graphene oxide (RGO) are prepared by simultaneously reducing graphene oxide (GO), nickel and cobalt nitrate via a hydrothermal method assisted by post annealing at low temperature. The method involves formation of hydroxides on GO using ammonia under hydrothermal conditions. Subsequent thermal treatment at 300 °C led to the conversion of hydroxides into single-phase NiCo 2 O 4 atop the RGO. The synthesized products are characterized through several techniques including X-ray diffraction (XRD), ultraviolet–visible spectroscopy (UV–Vis), Fourier transform infrared spectroscopy (FT-IR), Raman spectroscopy (RS), field emission scanning electron microscopy (FE-SEM), transmission electron microscopy (TEM) and X-ray photoelectron spectroscopy (XPS). The FE-SEM investigations reveal the growth of a layer by layer assembly of NiCo 2 O 4 –RGO (2:1) nanocomposite, where the NiCo 2 O 4 nanoparticles are tightly packed between the layers of RGO. Further, the catalytic properties of the NiCo 2 O 4 –RGO nanocomposite are investigated for the oxygen evolution reaction (OER) through cyclic voltammetry (CV) measurements. It is observed that the special structural features of the NiCo 2 O 4 –RGO (2:1) nanocomposite, including layer by layer assembly, integrity and excellent dispersion of the NiCo 2 O 4 nanoparticles atop the RGO, produced

  18. Solid-state dewetting of Au-Ni bi-layer films mediated through individual layer thickness and stacking sequence

    Science.gov (United States)

    Herz, Andreas; Theska, Felix; Rossberg, Diana; Kups, Thomas; Wang, Dong; Schaaf, Peter

    2018-06-01

    In the present work, the solid-state dewetting of Au-Ni bi-layer thin films deposited on SiO2/Si is systematically studied with respect to individual layer thickness and stacking sequence. For this purpose, a rapid heat treatment at medium temperatures is applied in order to examine void formation at the early stages of the dewetting. Compositional variations are realized by changing the thickness ratio of the bi-layer films, while the total thickness is maintained at 20 nm throughout the study. In the event of Au/Ni films annealed at 500 °C, crystal voids exposing the substrate are missing regardless of chemical composition. In reverse order, the number of voids per unit area in two-phase Au-Ni thin films is found to be governed by the amount of Au-rich material. At higher temperatures up to 650 °C, a decreased probability of nucleation comes at the expense of a major portion of cavities, resulting in the formation of bubbles in 15 nm Ni/5 nm Au bi-layers. Film buckling predominantly occurred at phase boundaries crossing the bubbles.

  19. Smear layer and debris removal using manual Ni-Ti files compared with rotary Protaper Ni- Ti files - An In-Vitro SEM study.

    Science.gov (United States)

    Reddy, J M V Raghavendra; Latha, Prasanna; Gowda, Basavana; Manvikar, Varadendra; Vijayalaxmi, D Benal; Ponangi, Kalyana Chakravarthi

    2014-02-01

    Predictable successful endodontic therapy depends on correct diagnosis, effective cleaning, shaping and disinfection of the root canals and adequate obturation. Irrigation serves as a flush to remove debris, tissue solvent and lubricant from the canal irregularities; however these irregularities can restrict the complete debridement of root canal by mechanical instrumentation.Various types of hand and rotary instruments are used for the preparation of the root canal system to obtain debris free canals. The purpose of this study was to evaluate the amount of smear layer and debris removal on canal walls following the using of manual Nickel-Titanium (NiTi) files compared with rotary ProTaperNiTi files using a Scanning Electron Microscope in two individual groups. A comparative study consisting of 50 subjects randomized into two groups - 25 subjects in Group A (manual) and 25 subjects in Group B (rotary) was undertaken to investigate and compare the effects of smear layer and debris between manual and rotary NiTi instruments. Chi square test was used to find the significance of smear layer and debris removal in the coronal, middle and apical between Group A and Group B. Both systems of Rotary ProTaperNiTi and manual NiTi files used in the present study, did not create completely clean root canals. Manual NiTi files produced significantly less smear layer and debris compared to Rotary ProTaperNiTi instruments. Rotary instruments were less time consuming when compared to manual instruments. Instrument separation was not found to be significant with both the groups. Both systems of Rotary ProTaperNiTi and manual NiTi files used did not produce completely clean root canals. Manual NiTi files produced significantly less smear layer and debris compared to Rotary protaper instruments. How to cite the article: Reddy JM, Latha P, Gowda B, Manvikar V, Vijayalaxmi DB, Ponangi KC. Smear layer and debris removal using manual Ni-Ti files compared with rotary Protaper Ni-Ti files

  20. Laser-driven shock-wave propagation in pure and layered targets

    International Nuclear Information System (INIS)

    Salzmann, D.; Eliezer, S.; Krumbein, A.D.; Gitter, L.

    1983-01-01

    The propagation properties of laser-driven shock waves in pure and layered polyethylene and aluminum slab targets are studied for a set of laser intensities and pulse widths. The laser-plasma simulations were carried out by means of our one-dimensional Lagrangian hydrodynamic code. It is shown that the various parts of a laser-driven compression wave undergo different thermodynamic trajectories: The shock front portion is on the Hugoniot curve whereas the rear part is closer to an adiabat. It is found that the shock front is accelerated into the cold material till troughly-equal0.8tau (where tau is the laser pulse width) and only later is a constant velocity propagation attained. The scaling laws obtained for the pressure and temperature of the compression wave in pure targets are in good agreement with those published in other works. In layered targets, high compression and pressure were found to occur at the interface of CH 2 on Al targets due to impedance mismatch but were not found when the layers were reversed. The persistence time of the high pressure on the interface in the CH 2 on Al case is long enough relative to the characteristic times of the plasma to have an appreciable influence on the shock-wave propagation into the aluminum layer. This high pressure and compression on the interface can be optimized by adjusting the CH 2 layer thickness

  1. Fabrication of the cube textured NiO buffer layer by line-focused infrared heating for coated conductor application

    International Nuclear Information System (INIS)

    Chung, Jun-Ki; Kim, Won-Jeong; Tak, Jinsung; Kim, Cheol Jin

    2007-01-01

    Epitaxial growth of NiO on the bi-axially textured Ni-3 at.%W (Ni-3W) substrate as seed layer for coated conductor were studied. The bi-axially textured NiO was formed on the Ni-3W tapes using a line-focused infrared heater by oxidizing the surface of the substrate at 800-950 deg. C for 15-120 s in oxygen atmosphere. The thickness of the NiO layer could be controlled by changing heat-treatment, which was estimated as approximately 200-500 nm in the cross-sectional SEM micrographs of the NiO/Ni template. This thickness is enough to block the diffusion of the Ni in the substrate to the superconducting layer. The samples showed strong texture development of NiO layer. The sample oxidized at 900 deg. C with the tape transferring speed of 30 mm/h exhibited ω-scan full width at half maximum (FWHM) values for Ni-3W(2 0 0) and NiO(2 0 0) were 3.97 deg., and 3.67 deg., and φ-scan FWHM values for Ni-3W(1 1 1) and NiO(1 1 1) were 9.58 deg., and 8.79 deg., respectively. Also, the (1 1 1) pole-figure of the NiO buffer layer showed the good symmetry of the four peaks, securing the epitaxial growth of the buffer layers on the NiO layer. Also NiO layer exhibited root-mean-square roughness value of 39 nm by AFM (10 x 10 μm) investigation

  2. Magnetooptic effects and Auger electron spectroscopy of two-layer NiFe-Dy and Fe-Dy films with nonuniform layers

    International Nuclear Information System (INIS)

    Ehdel'man, I.S.; Markov, V.V.; Khudyakov, A.E.; Ivantsov, R.D.; Bondarenko, G.V.; Ovchinnikov, S.G.; Kesler, V.G.; Parshin, A.S.; Ronzhin, I.P.

    2001-01-01

    Magneto-optical effects (magnetic circular dichroism and meridional Kerr effect) and element distribution with layer thickness in two-layer NiFe-Dy and Fe-Dy films, prepared by thermal sputtering of component in ultrahigh vacuum, are investigated. It is shown, that Dy in a two-layer film in the temperature range of 80-300 K makes constant contributions to both effects investigated which are approximately equal to the values of the effects observed in an isolated Dy film only at temperatures below the temperature T c of Dy transition into a ferromagnetic state (T c ∼ 100 K for the films under study). This behaviour of magneto-optical effects is assumed to be due to the influence of a NiFe layer spin system on magnetic state of a Dy layer, this influence is enhanced by the deep penetration of Ni and Fe ions into Dy layer as it follows from the data obtained using Auger electron spectroscopy [ru

  3. Nanostructure characterization of Ni and B layers as artificial pinning centers in multilayered MgB2/Ni and MgB2/B superconducting thin films

    International Nuclear Information System (INIS)

    Sosiati, H.; Hata, S.; Doi, T.; Matsumoto, A.; Kitaguchi, H.; Nakashima, H.

    2013-01-01

    Highlights: ► Nanostructure characterization of Ni and B layers as artificial pinning centers (APCs). ► Relationship between nanostructure and J c property. ► Enhanced J c in parallel field by parallel APCs within the MgB 2 film. -- Abstract: Research on the MgB 2 /Ni and MgB 2 /B multilayer films fabricated by an electron beam (EB) evaporation technique have been extensively carried out. The critical current density, J c of MgB 2 /Ni and MgB 2 /B multilayer films in parallel fields has been suggested to be higher than that of monolayer MgB 2 film due to introducing the artificial pinning centers of nano-sized Ni and B layers. Nanostructure characterization of the artificial pinning centers in the multilayer films were examined by transmission electron microscopy (TEM) and scanning TEM (STEM-energy dispersive X-ray spectroscopy (STEM-EDS))–EDS to understand the mechanism of flux pinning. The growth of columnar MgB 2 grains along the film-thickness direction was recognized in the MgB 2 /Ni multilayer film, but not in the MgB 2 /B multilayer film. Nano-sized Ni layers were present as crystalline epitaxial layers which is interpreted that Ni atoms might be incorporated into the MgB 2 lattice to form (Mg,Ni)B 2 phase. On the other hand, nano-sized B layers were amorphous layers. Crystalline (Mg,Ni)B 2 layers worked more effectively than amorphous B-layers, providing higher flux-pinning force that resulted in higher J c of the MgB 2 /Ni multilayer film than the MgB 2 /B multilayer film

  4. Synthesis, Characterization, and Magnetic Properties of Pure and EDTA-Capped NiO Nanosized Particles

    Directory of Open Access Journals (Sweden)

    H. T. Rahal

    2017-01-01

    Full Text Available The effect of ethylenediaminetetraacetic acid (EDTA as a capping agent on the structure, morphology, optical, and magnetic properties of nickel oxide (NiO nanosized particles, synthesized by coprecipitation method, was investigated. Nickel chloride hexahydrate and sodium hydroxide (NaOH were used as precursors. The resultant nanoparticles were characterized by X-ray diffraction (XRD, transmission electron microscopy (TEM, and scanning electron microscopy (SEM. XRD patterns showed that NiO have a face-centered cubic (FCC structure. The crystallite size, estimated by Scherrer formula, has been found in the range of 28–33 nm. It is noticed that EDTA-capped NiO nanoparticles have a smaller size than pure nanoparticles. Thus, the addition of 0.1 M capping agent EDTA can form a nucleation point for nanoparticles growth. The optical and magnetic properties were investigated by Fourier transform infrared spectroscopy (FTIR and UV-vis absorption spectroscopy (UV as well as electron paramagnetic resonance (EPR and magnetization measurements. FTIR spectra indicated the presence of absorption bands in the range of 402–425 cm−1, which is a common feature of NiO. EPR for NiO nanosized particles was measured at room temperature. An EPR line with g factor ≈1.9–2 is detected for NiO nanoparticles, corresponding to Ni2+ ions. The magnetic hysteresis of NiO nanoparticles showed that EDTA capping recovers the surface magnetization of the nanoparticles.

  5. Investigation of Ni@CoO core-shell nanoparticle films synthesized by sequential layer deposition

    International Nuclear Information System (INIS)

    Spadaro, M.C.; Luches, P.; Benedetti, F.; Valeri, S.; Turchini, S.; Bertoni, G.; Ferretti, A.M.; Capetti, E.; Ponti, A.; D’Addato, S.

    2017-01-01

    Highlights: • We studied Ni/CoO core-shell nanoparticles (NP) obtained with a gas aggregation source. • The NP oxide shells were produced bye reactive deposition of Co in Oxygen atmosphere (p_O_2 ≈ 10"−"7 mbar). • XPS, SEM, STEM were used to obtain information on Ni chemical state and NP structure and morphology. • XMCD result showed evidence of remanent magnetization at room temperature. • We interpret XMCD results as due to stabilization induced by exchange bias due to AFM/FM coupling at the core/shell interface. - Abstract: Films of Ni@CoO core-shell nanoparticles (NP Ni core size d ≈ 11 nm) have been grown on Si/SiO_x and lacey carbon supports, by a sequential layer deposition method: a first layer of CoO was evaporated on the substrate, followed by the deposition of a layer of pre-formed, mass-selected Ni NPs, and finally an overlayer of CoO was added. The Ni NPs were formed by a magnetron gas aggregation source, and mass selected with a quadrupole mass filter. The morphology of the films was investigated with Scanning Electron Microscopy and Scanning Transmission Electron Microscopy. The Ni NP cores have a shape compatible with McKay icosahedron, caused by multitwinning occurring during their growth in the source, and the Ni NP layer shows the typical random paving growth mode. After the deposition of the CoO overlayer, CoO islands are observed, gradually extending and tending to merge with each other, with the formation of shells that enclose the Ni NP cores. In situ X-ray Photoelectron Spectroscopy showed that a few Ni atomic layers localized at the core-shell interface are oxidized, hinting at the possibility of creating an intermediate NiO shell between Ni and CoO, depending on the deposition conditions. Finally, X-ray Magnetic Circular Dichroism at the Ni L_2_,_3 absorption edge showed the presence of magnetization at room temperature even at remanence, revealing the possibility of magnetic stabilization of the NP film.

  6. Preparation of Copper and Chromium Alloyed Layers on Pure Titanium by Plasma Surface Alloying Technology

    Science.gov (United States)

    He, Xiaojing; Li, Meng; Wang, Huizhen; Zhang, Xiangyu; Tang, Bin

    2015-05-01

    Cu-Cr alloyed layers with different Cu and Cr contents on pure titanium were obtained by means of plasma surface alloying technology. The microstructure, chemical composition and phase composition of Cu-Cr alloyed layers were analyzed by scanning electron microscopy (SEM), energy dispersive spectrometer (EDS) and X-ray diffraction (XRD), respectively. The experimental results demonstrate that the alloyed layers are bonded strongly to pure titanium substrate and consist of unbound Ti, CuTi, Cu3Ti, CuTi3 and Cr2Ti. The thickness of Cu5Cr5 and Cu7Cr3 alloyed layer are about 18 μm and 28 μm, respectively. The antibacterial properties against gram-negative Escherichia coli (E.coli, ATCC10536) and gram-positive Staphylococcus aureus (S. aureus, ATCC6538) of untreated pure titanium and Cu-Cr alloyed specimen were investigated by live/dead fluorescence staining method. The study shows that Cu-Cr alloyed layers exhibit excellent antibacterial activities against both E.coli and S.aureus within 24 h, which may be attributed to the formation of Cu-containing phases.

  7. A facile cathode design combining Ni-rich layered oxides with Li-rich layered oxides for lithium-ion batteries

    Energy Technology Data Exchange (ETDEWEB)

    Song, Bohang; Li, Wangda; Yan, Pengfei; Oh, Seung-Min; Wang, Chong-Min; Manthiram, Arumugam

    2016-09-01

    A facile synthesis method was developed to prepare xLi2MnO3·(1-x)LiNi0.7Co0.15Mn0.15O2 (x = 0, 0.03, 0.07, 0.10, 0.20, and 0.30 as molar ratio) cathode materials, combining the advantages of high specific capacity from Ni-rich layered phase and surface chemical stability from Li-rich layered phase. X-ray diffraction (XRD), high resolution transmission electron microscope (HRTEM) and electrochemical charge/discharge performance confirm the formation of a Li-rich layered phase with C2/m symmetry. Most importantly, high-angle annular dark-field (HAADF) scanning transmission electron microscopy (STEM) reveals a spatial relationship that Li-rich nano-domain islands are integrated into a conventional Ni-rich layered matrix (R$\\bar{3}$m). This is the first time that Li-rich phase has been directly observed inside a particle at the nano-scale, when the overall composition of layered compounds (Li1+δNixMnyM1-x-y-δO2, M refers to transition metal elements) is Ni-rich (x > 0.5) rather than Mn-rich (y > 0.5). Remarkably, xLi2MnO3·(1-x)LiNi0.7Co0.15Mn0.15O2 cathode with optimized x value shows superior electrochemical performance at C/3, i.e., 170 mA h g-1 with 90.3 % of capacity retention after 400 cycles at 25 °C and 164 mA h g-1 with 81.3 % capacity retention after 200 cycles at 55 °C.

  8. Nitriding behavior of Ni and Ni-based binary alloys

    Energy Technology Data Exchange (ETDEWEB)

    Fonovic, Matej

    2015-01-15

    Gaseous nitriding is a prominent thermochemical surface treatment process which can improve various properties of metallic materials such as mechanical, tribological and/or corrosion properties. This process is predominantly performed by applying NH{sub 3}+H{sub 2} containing gas atmospheres serving as the nitrogen donating medium at temperatures between 673 K and 873 K (400 C and 600 C). NH{sub 3} decomposes at the surface of the metallic specimen and nitrogen diffuses into the surface adjacent region of the specimen whereas hydrogen remains in the gas atmosphere. One of the most important parameters characterizing a gaseous nitriding process is the so-called nitriding potential (r{sub N}) which determines the chemical potential of nitrogen provided by the gas phase. The nitriding potential is defined as r{sub N} = p{sub NH{sub 3}}/p{sub H{sub 2}{sup 3/2}} where p{sub NH{sub 3}} and p{sub H{sub 2}} are the partial pressures of the NH{sub 3} and H{sub 2} in the nitriding atmosphere. In contrast with nitriding of α-Fe where the nitriding potential is usually in the range between 0.01 and 1 atm{sup -1/2}, nitriding of Ni and Ni-based alloys requires employing nitriding potentials higher than 100 atm{sup -1/2} and even up to ∞ (nitriding in pure NH{sub 3} atmosphere). This behavior is compatible with decreased thermodynamic stability of the 3d-metal nitrides with increasing atomic number. Depending on the nitriding conditions (temperature, nitriding potential and treatment time), different phases are formed at the surface of the Ni-based alloys. By applying very high nitriding potential, formation of hexagonal Ni{sub 3}N at the surface of the specimen (known as external nitriding) leads to the development of a compound layer, which may improve tribological properties. Underneath the Ni{sub 3}N compound layer, two possibilities exist: (i) alloying element precipitation within the nitrided zone (known as internal nitriding) and/or (ii) development of metastable and

  9. 2D water layer enclathrated between Mn(II)-Ni(CN)4 coordination frameworks

    International Nuclear Information System (INIS)

    Ray, Ambarish; Bhowmick, Indrani; Sheldrick, William S.; Jana, Atish Dipankar; Ali, Mahammed

    2009-01-01

    A [Ni(CN) 4 ] 2- based two-dimensional Mn(II) coordination polymer {Mn(H 2 O) 2 [NiCN] 4 .4H 2 O}, in which the coordination layers are stacked on top of each other sandwiching 2D water layer of boat-shaped hexagonal water clusters has been synthesized. The complex exhibits high thermal decomposition temperature and reversible water absorption, which were clearly demonstrated by thermal and PXRD studies on the parent and rehydrated complex after dehydration. - Abstract: A coordination polymer, {Mn(H 2 O) 2 [NiCN] 4 .4H 2 O} n , showed that the coordination layers are stacked on top of each other sandwiching 2D ice layer of boat-shaped hexagonal water clusters . Display Omitted

  10. Preparation and estimation of thermodynamic properties of Fe(II)-, Co(II)-, Ni(II)- and Zr(IV)-containing layered double hydroxides

    Energy Technology Data Exchange (ETDEWEB)

    Rozov, Konstantin; Curtius, Hilde; Bosbach, Dirk [Forschungszentrum Juelich GmbH (Germany). Inst. for Nuclear Waste Management and Reactor Safety (IEK-6)

    2015-07-01

    The investigation of layered double hydroxides (LDHs) was performed because they and similar 'green rust' phases were identified as specific secondary phases forming during the evolution of the disposed research reactor fuel elements under nuclear repository relevant conditions. LDHs or 'hydrotalcite-like' solids are of interest in environmental geochemistry because they can substitute various cations and especially due to the anion-exchange properties and, therefore, can be considered as buffer materials for retention of mobile and hazardous radionuclides (like, {sup 14}C, {sup 129}I, {sup 36}Cl, {sup 79}Se etc.). In our study Fe{sup 2+}-, Co{sup 2+}-, Ni{sup 2+}- and Zr{sup 4+}-containing LDHs have been synthesized by co-precipitation method and characterized (PXRD, FT-IR, SEM-EDX, TGA-DSC) in order to investigate the effect of substitution of 2- and 4-valent cations on the stability of LDHs. PXRD measurements demonstrated that: (1) pure Mg-Al-Fe(II) LDHs are existing in the range of the mole fraction of iron x{sub Fe} = Fe/(Mg+Fe) between 0 and 0.13. Unit-cell parameters (a{sub o}=b{sub o}) as a function of x{sub Fe} follow Vegard's law corroborating the existence of a solid solution when x{sub Fe} = 0 - 0.13. Products of syntheses with x{sub Fe} ≥ 0.13 contain detectable amounts (≥1-2 wt%) of additional phases (like, magnetite, maghemite, lepidocrocite); (2) pure Ni{sup 2+}- and Co{sup 2+}-containing LDHs (mole fractions of Ni and Co were equal to 0.1) have been synthesized successfully; (3) Mg-Al-Zr(IV) precipitates with mole fraction of zirconium x{sub Zr} = Zr/(Zr+Al) = 0.0 - 0.5 show PXRD patterns attributed to pure LDHs and the variation of lattice parameters a{sub o}=b{sub o} as a function of x{sub Zr} is in agreement with Vegard's law demonstrating the presence of solid solution. In contrast, PXRD analyses of precipitates with x{sub Zr} ≥ 0.5 have shown the presence of additional X-ray reflexes typical for brucite. The

  11. Interphase Constituent of Laminated Composites Ti46Zr26Cu17Ni11

    Directory of Open Access Journals (Sweden)

    XU Bingtong

    2017-10-01

    Full Text Available Thermal analysis of the Ti46Zr26Cu17Ni11 amorphous ribbon prepared by melt spinning was conducted by using DSC. Accordingly the amorphous alloy was treated by vacuum heat treatment at 693 K (Tg, 753 K (Tg-Tx1 and 813 K (> Tx1 for different time to analyze the crystallization behavior. Taking Ti46Zr26Cu17Ni11 amorphous alloy, TA2 and pure Al as raw materials, laminated composites were fabricated by Gleeble-3500 thermal simulator at 873 K, 10 MPa and 8 h. The phase composition, precipitation order and properties of interface layers were investigated by SEM, TEM, micro hardness tester, combined thermodynamics and element diffusion theory. The results indicate that the glass transition temperature Tg of Ti46Zr26Cu17Ni11 amorphous is 720 K and the initial crystallization temperature Tx1 is 788 K. The I phase is crystallized from the amorphous at first, followed by a ternary or quaternary Laves phase and a TiNi phase precipited. After hot pressing, the interface between pure Al and crystallization layer is divided into two parts, which are Al3Ni with small thickness and Al3(Ti0.6Zr0.4 with fine grain and uniform microstructure. The interfaces are straight and there are no defects, with a thickness ratio of about 6.5:1 compared with interface layer between pure Ti with Al. The hardness of Al3(Ti0.6Zr0.4 and Al3Ti are 564.2HV and 579.8HV respectively. The plasticity of Al3(Ti0.6Zr0.4 layer is better.

  12. The influence of Pt redistribution on Ni1-xPtxSi growth properties

    International Nuclear Information System (INIS)

    Demeulemeester, J.; Smeets, D.; Temst, K.; Vantomme, A.; Comrie, C. M.; Van Bockstael, C.; Knaepen, W.; Detavernier, C.

    2010-01-01

    We have studied the influence of Pt on the growth of Ni silicide thin films by examining the Pt redistribution during silicide growth. Three different initial Pt configurations were investigated, i.e., a Pt alloy (Ni+Pt/ ), a Pt capping layer (Pt/Ni/ ) and a Pt interlayer (Ni/Pt/ ), all containing 7 at. % Pt relative to the Ni content. The Pt redistribution was probed using in situ real-time Rutherford backscattering spectrometry (RBS) whereas the phase sequence was monitored during the solid phase reaction (SPR) using in situ real-time x-ray diffraction. We found that the capping layer and alloy exhibit a SPR comparable to the pure Ni/ system, whereas Pt added as an interlayer has a much more drastic influence on the Ni silicide phase sequence. Nevertheless, for all initial sample configurations, Pt redistributes in an erratic way. This phenomenon can be assigned to the low solubility of Pt in Ni 2 Si compared to NiSi and the high mobility of Pt in Ni 2 Si compared to pure Ni. Real-time RBS further revealed that the crucial issue determining the growth properties of each silicide phase is the Pt concentration at the Si interface during the initial stages of phase formation. The formation of areas rich in Pt reduce the Ni silicide growth kinetics which influences the phase sequence and properties of the silicides.

  13. Interplay between out-of-plane anisotropic L1{sub 1}-type CoPt and in-plane anisotropic NiFe layers in CoPt/NiFe exchange springs

    Energy Technology Data Exchange (ETDEWEB)

    Saravanan, P. [Department of Physics, National Taiwan University, Taipei 106, Taiwan (China); Defence Metallurgical Research Laboratory, Hyderabad 500058 (India); Hsu, Jen-Hwa, E-mail: jhhsu@phys.ntu.edu.tw; Tsai, C. L. [Department of Physics, National Taiwan University, Taipei 106, Taiwan (China); Tsai, C. Y.; Lin, Y. H. [Graduate Institute of Materials Science and Engineering, National Taiwan University, Taipei 106, Taiwan (China); Kuo, C. Y.; Wu, J.-C. [Department of Physics, National Chang Hua University of Education, Chang Hua 50000, Taiwan (China); Lee, C.-M. [Graduate School of Materials Science, National Yunlin University of Science and Technology, Douliou 64002, Taiwan (China)

    2014-06-28

    Films of L1{sub 1}-type CoPt/NiFe exchange springs were grown with different NiFe (Permalloy) layer thickness (t{sub NiFe} = 0–10 nm). X-ray diffraction analysis reveals that the characteristic peak position of NiFe(111) is not affected by the CoPt-layer—confirming the absence of any inter-diffusion between the CoPt and NiFe layers. Magnetic studies indicate that the magnetization orientation of NiFe layer can be tuned through varying t{sub NiFe} and the perpendicular magnetic anisotropy of L1{sub 1}-type CoPt/NiFe films cannot sustain for t{sub NiFe} larger than 3.0 nm due to the existence of exchange interaction at the interface of L1{sub 1}-CoPt and NiFe layers. Magnetic force microscopy analysis on the as-grown samples shows the changes in morphology from maze-like domains with good contrast to hazy domains when t{sub NiFe} ≥ 3.0 nm. The three-dimensional micro-magnetic simulation results demonstrate that the magnetization orientation in NiFe layer is not uniform, which continuously increases from the interface to the top of NiFe layer. Furthermore, the tilt angle of the topmost NiFe layers can be changed over a very wide range from a small number to about 75° by varying t{sub NiFe} from 1 to 10 nm. It is worth noting that there is an abrupt change in the magnetization direction at the interface, for all the t{sub NiFe} investigated. The results of present study demonstrate that the tunable tilted exchange springs can be realized with L1{sub 1}-type CoPt/NiFe bilayers for future applications in three-axis magnetic sensors or advanced spintronic devices demanding inclined magnetic anisotropy.

  14. Thermal barrier coatings with a double-layer bond coat on Ni{sub 3}Al based single-crystal superalloy

    Energy Technology Data Exchange (ETDEWEB)

    Zhou, Xin [State Key Laboratory of Rare Earth Resource Utilization, Changchun Institute of Applied Chemistry, Chinese Academy of Sciences, Changchun 130022 (China); University of Chinese Academy of Sciences, Beijing 100049 (China); Beijing Institute of Aeronautical Materials, Department 5, P.O. Box 81-5, Beijing 100095 (China); Xu, Zhenhua; Mu, Rende [Beijing Institute of Aeronautical Materials, Department 5, P.O. Box 81-5, Beijing 100095 (China); He, Limin, E-mail: he_limin@yahoo.com [Beijing Institute of Aeronautical Materials, Department 5, P.O. Box 81-5, Beijing 100095 (China); Huang, Guanghong [Beijing Institute of Aeronautical Materials, Department 5, P.O. Box 81-5, Beijing 100095 (China); Cao, Xueqiang, E-mail: xcao@ciac.ac.cn [State Key Laboratory of Rare Earth Resource Utilization, Changchun Institute of Applied Chemistry, Chinese Academy of Sciences, Changchun 130022 (China)

    2014-04-05

    Highlights: • Thermal barrier coatings with a double-layer bond coat of (Ni,Pt)Al and NiCrAlYSi. • Good adherence at all interfaces within TBC system. • The underlying (Ni,Pt)Al layer can supply abundant Al content for the upper NiCrAlYSi layer. • Crack nucleation, propagation and coalescence lead to the failure of coating. -- Abstract: Electron-beam physical vapor deposited thermal barrier coatings (TBCs) with a double-layer bond coat of (Ni,Pt)Al and NiCrAlYSi were prepared on a Ni{sub 3}Al based single-crystal superalloy. Phase and cross-sectional microstructure of the developed coatings were studied by using X-ray diffraction (XRD) and scanning electron microscope (SEM), respectively. The experimental results show good adherence at all interfaces within this system. Furthermore, oxidation resistance and elements interdiffusion behavior of the double-layer bond coat were also investigated. The double-layer bond coat system exhibits a better scale adherence than the single layer bond coat systems since the underlying (Ni,Pt)Al layer can supply abundant Al for the upper NiCrAlYSi layer. Finally, thermal cycling behavior of the double-layer bond coat TBC was evaluated and the failure mechanism was discussed. Crack nucleation, propagation and coalescence caused by TGO growth stress and the thermal expansion mismatch stress between TGO and bond coat can be mainly responsible for the spallation of this coating.

  15. Improving the corrosion wear resistance of AISI 316L stainless steel by particulate reinforced Ni matrix composite alloying layer

    Science.gov (United States)

    Xu, Jiang; Zhuo, Chengzhi; Tao, Jie; Jiang, Shuyun; Liu, Linlin

    2009-01-01

    In order to overcome the problem of corrosion wear of AISI 316L stainless steel (SS), two kinds of composite alloying layers were prepared by a duplex treatment, consisting of Ni/nano-SiC and Ni/nano-SiO2 predeposited by brush plating, respectively, and subsequent surface alloying with Ni-Cr-Mo-Cu by a double glow process. The microstructure of the two kinds of nanoparticle reinforced Ni-based composite alloying layers was investigated by means of SEM and TEM. The electrochemical corrosion behaviour of composite alloying layers compared with the Ni-based alloying layer and 316L SS under different conditions was characterized by potentiodynamic polarization test and electrochemical impedance spectroscopy. Results showed that under alloying temperature (1000 °C) conditions, amorphous nano-SiO2 particles still retained the amorphous structure, whereas nano-SiC particles were decomposed and Ni, Cr reacted with SiC to form Cr6.5Ni2.5Si and Cr23C6. In static acidic solution, the corrosion resistance of the composite alloying layer with the brush plating Ni/nano-SiO2 particles interlayer is lower than that of the Ni-based alloying layer. However, the corrosion resistance of the composite alloying layer with the brush plating Ni/nano-SiO2 particles interlayer is prominently superior to that of the Ni-based alloying layer under acidic flow medium condition and acidic slurry flow condition. The corrosion resistance of the composite alloying layer with the brush plating Ni/nano-SiC particles interlayer is evidently lower than that of the Ni-based alloying layer, but higher than that of 316L SS under all test conditions. The results show that the highly dispersive nano-SiO2 particles are helpful in improving the corrosion wear resistance of the Ni-based alloying layer, whereas carbides and silicide phase are deleterious to that of the Ni-based alloying layer due to the fact that the preferential removal of the matrix around the precipitated phase takes place by the chemical

  16. Investigation of Ni@CoO core-shell nanoparticle films synthesized by sequential layer deposition

    Energy Technology Data Exchange (ETDEWEB)

    Spadaro, M.C., E-mail: mariachiara.spadaro@unimore.it [CNR-NANO, via G. Campi 213/a, 41125 Modena (Italy); Dipartimento FIM, Università di Modena e Reggio Emilia, via G. Campi 213/a, 41125 Modena (Italy); Luches, P. [Dipartimento FIM, Università di Modena e Reggio Emilia, via G. Campi 213/a, 41125 Modena (Italy); Benedetti, F.; Valeri, S. [CNR-NANO, via G. Campi 213/a, 41125 Modena (Italy); Dipartimento FIM, Università di Modena e Reggio Emilia, via G. Campi 213/a, 41125 Modena (Italy); Turchini, S. [CNR-ISM, Via Fosso del Cavaliere 100, 00133 Roma (Italy); Bertoni, G. [CNR-IMEM, Parco Area delle Scienze 37/a, 43124 Parma (Italy); Ferretti, A.M.; Capetti, E.; Ponti, A. [Laboratorio di Nanotecnologie, Istituto di Scienze e Tecnologie Molecolari, Consiglio Nazionale delle Ricerche, via G. Fantoli 16/15, 20138 Milano (Italy); D’Addato, S. [CNR-NANO, via G. Campi 213/a, 41125 Modena (Italy); Dipartimento FIM, Università di Modena e Reggio Emilia, via G. Campi 213/a, 41125 Modena (Italy)

    2017-02-28

    Highlights: • We studied Ni/CoO core-shell nanoparticles (NP) obtained with a gas aggregation source. • The NP oxide shells were produced bye reactive deposition of Co in Oxygen atmosphere (p{sub O2} ≈ 10{sup −7} mbar). • XPS, SEM, STEM were used to obtain information on Ni chemical state and NP structure and morphology. • XMCD result showed evidence of remanent magnetization at room temperature. • We interpret XMCD results as due to stabilization induced by exchange bias due to AFM/FM coupling at the core/shell interface. - Abstract: Films of Ni@CoO core-shell nanoparticles (NP Ni core size d ≈ 11 nm) have been grown on Si/SiO{sub x} and lacey carbon supports, by a sequential layer deposition method: a first layer of CoO was evaporated on the substrate, followed by the deposition of a layer of pre-formed, mass-selected Ni NPs, and finally an overlayer of CoO was added. The Ni NPs were formed by a magnetron gas aggregation source, and mass selected with a quadrupole mass filter. The morphology of the films was investigated with Scanning Electron Microscopy and Scanning Transmission Electron Microscopy. The Ni NP cores have a shape compatible with McKay icosahedron, caused by multitwinning occurring during their growth in the source, and the Ni NP layer shows the typical random paving growth mode. After the deposition of the CoO overlayer, CoO islands are observed, gradually extending and tending to merge with each other, with the formation of shells that enclose the Ni NP cores. In situ X-ray Photoelectron Spectroscopy showed that a few Ni atomic layers localized at the core-shell interface are oxidized, hinting at the possibility of creating an intermediate NiO shell between Ni and CoO, depending on the deposition conditions. Finally, X-ray Magnetic Circular Dichroism at the Ni L{sub 2,3} absorption edge showed the presence of magnetization at room temperature even at remanence, revealing the possibility of magnetic stabilization of the NP film.

  17. Molecular dynamics simulation of effects of twin interfaces on Cu/Ni multilayers

    International Nuclear Information System (INIS)

    Fu, Tao; Peng, Xianghe; Weng, Shayuan; Zhao, Yinbo; Gao, Fengshan; Deng, Lijun; Wang, Zhongchang

    2016-01-01

    We perform molecular dynamics simulation of the indentation on pure Cu and Ni films and Cu/Ni multilayered films with a cylindrical indenter, aimed to investigate the effects of the cubic-on-cubic interface and hetero-twin interface on their mechanical properties. We also investigate systematically the formation of twin boundary in the pure metals and the effects of the cubic-on-cubic and hetero-twin interface on mechanical properties of the multilayers. We find that the slip of the horizontal stacking fault can release the internal stress, resulting in insignificant strengthening. The change in the crystal orientation by horizontal movement of the atoms in a layer-by-layer manner is found to initiate the movement of twin boundary, and the hetero-twin interface is beneficial to the hardening of multilayers. Moreover, we also find that increasing number of hetero-twin interfaces can harden the Cu/Ni multilayers.

  18. Preparation and characterization of self-assembled layer by layer NiCo{sub 2}O{sub 4}–reduced graphene oxide nanocomposite with improved electrocatalytic properties

    Energy Technology Data Exchange (ETDEWEB)

    Srivastava, Manish; Elias Uddin, Md. [Advanced Materials Research Institute for BIN Fusion Technology (BK Plus Global Program), Department of BIN Fusion Technology, Chonbuk National University, Jeonju, Jeonbuk 561-756 (Korea, Republic of); Singh, Jay [Department of Applied Chemistry, Delhi Technological University, Shahbad Daulatpur, Main Bawana Road, Delhi 110042 (India); Kim, Nam Hoon [Advanced Materials Research Institute for BIN Fusion Technology (BK Plus Global Program), Department of BIN Fusion Technology, Chonbuk National University, Jeonju, Jeonbuk 561-756 (Korea, Republic of); Lee, Joong Hee, E-mail: jhl@chonbuk.ac.kr [Advanced Materials Research Institute for BIN Fusion Technology (BK Plus Global Program), Department of BIN Fusion Technology, Chonbuk National University, Jeonju, Jeonbuk 561-756 (Korea, Republic of); Advanced Wind Power System Research Center, Department of Polymer and Nano Engineering, Chonbuk National University, Jeonju, Jeonbuk 561-756 (Korea, Republic of)

    2014-03-25

    Graphical abstract: NiCo{sub 2}O{sub 4} were grown on RGO by in situ synthesis process. FE-SEM investigation revealed self assembled layer by layer growth of NiCo{sub 2}O{sub 4}–RGO nanocomposite. NiCo{sub 2}O{sub 4}–RGO nanocomposite exhibited synergetic effect of NiCo{sub 2}O{sub 4} nanoparticles and RGO on its electrochemical performance. -- Highlights: • NiCo{sub 2}O{sub 4} were grown on RGO by in-situ synthesis process. • FE-SEM image revealed self-assembled layer by layer growth of NiCo{sub 2}O{sub 4}-RGO nanocomposite. • NiCo{sub 2}O{sub 4}-RGO nanocomposite exhibited synergetic effects on its electrochemical performance. -- Abstract: NiCo{sub 2}O{sub 4} nanoparticles dispersed on reduced graphene oxide (RGO) are prepared by simultaneously reducing graphene oxide (GO), nickel and cobalt nitrate via a hydrothermal method assisted by post annealing at low temperature. The method involves formation of hydroxides on GO using ammonia under hydrothermal conditions. Subsequent thermal treatment at 300 °C led to the conversion of hydroxides into single-phase NiCo{sub 2}O{sub 4} atop the RGO. The synthesized products are characterized through several techniques including X-ray diffraction (XRD), ultraviolet–visible spectroscopy (UV–Vis), Fourier transform infrared spectroscopy (FT-IR), Raman spectroscopy (RS), field emission scanning electron microscopy (FE-SEM), transmission electron microscopy (TEM) and X-ray photoelectron spectroscopy (XPS). The FE-SEM investigations reveal the growth of a layer by layer assembly of NiCo{sub 2}O{sub 4}–RGO (2:1) nanocomposite, where the NiCo{sub 2}O{sub 4} nanoparticles are tightly packed between the layers of RGO. Further, the catalytic properties of the NiCo{sub 2}O{sub 4}–RGO nanocomposite are investigated for the oxygen evolution reaction (OER) through cyclic voltammetry (CV) measurements. It is observed that the special structural features of the NiCo{sub 2}O{sub 4}–RGO (2:1) nanocomposite, including

  19. Phase Equilibria of the Sn-Ni-Si Ternary System and Interfacial Reactions in Sn-(Cu)/Ni-Si Couples

    Science.gov (United States)

    Fang, Gu; Chen, Chih-chi

    2015-07-01

    Interfacial reactions in Sn/Ni-4.5 wt.%Si and Sn-Cu/Ni-4.5 wt.%Si couples at 250°C, and Sn-Ni-Si ternary phase equilibria at 250°C were investigated in this study. Ni-Si alloys, which are nonmagnetic, can be regarded as a diffusion barrier layer material in flip chip packaging. Solder/Ni-4.5 wt.%Si interfacial reactions are crucial to the reliability of soldered joints. Phase equilibria information is essential for development of solder/Ni-Si materials. No ternary compound is present in the Sn-Ni-Si ternary system at 250°C. Extended solubility of Si in the phases Ni3Sn2 and Ni3Sn is 3.8 and 6.1 at.%, respectively. As more Si dissolves in these phases their lattice constants decrease. No noticeable ternary solubility is observed for the other intermetallics. Interfacial reactions in solder/Ni-4.5 wt.%Si are similar to those for solder/Ni. Si does not alter the reaction phases. No Si solubility in the reaction phases was detected, although rates of growth of the reaction phases were reduced. Because the alloy Ni-4.5 wt.%Si reacts more slowly with solders than pure Ni, the Ni-4.5 wt.%Si alloy could be a potential new diffusion barrier layer material for flip chip packaging.

  20. Comparison of reduction agents in the synthesis of infinite-layer LaNiO2 films

    International Nuclear Information System (INIS)

    Ikeda, Ai; Manabe, Takaaki; Naito, Michio

    2014-01-01

    Highlights: • Reduction agents were compared from a viewpoint of the facility for topotactic reduction of LaNiO 3 to LaNiO 2 films. • TiH 2 and CaH 2 yielded infinite-layer LaNiO 2 with low and metallic resistivity. • H 2 released from metal hydrides plays a dominant role in the topotactic reduction. - Abstract: Reduction agents, such as activated carbon, TiH 2 , and CaH 2 , were compared from a viewpoint of the facility for the topotactic reduction of LaNiO 3 to LaNiO 2 films. Activated carbon did not yield infinite-layer LaNiO 2 whereas both of TiH 2 and CaH 2 yielded infinite-layer LaNiO 2 with low resistivity (∼1 mΩ cm at 300 K) as well as metallic behavior down to 70 K. Thermal desorption spectroscopy indicated that H 2 released from metal hydrides plays a dominant role in the topotactic reduction

  1. Biperiodic oscillatory coupling with the thickness of an embedded Ni layer in Co/Cu/Co/Ni/Co (100) and selection rules for the periods

    NARCIS (Netherlands)

    de Vries, J.J.; Vorst, van de M.T.H.; Johnson, M.T.; Jungblut, R.; Reinders, A.; Bloemen, P.J.H.; Coehoorn, R.; Jonge, de W.J.M.

    1996-01-01

    A biperiodic oscillation of the strength of the antiferromagnetic interlayer coupling as a function of the thickness of an embedded Ni layer has been observed in an epitaxial Cu(100)/Co/Cu/Co/Ni/Co sample with the Cu interlayer and the Ni layer in the form of wedges. As the effect originates from

  2. Characteristics of Ni-Cr-Fe laser clad layers on EA4T steel

    Science.gov (United States)

    Chen, Wenjing; Chen, Hui; Wang, Yongjing; Li, Congchen; Wang, Xiaoli

    2017-07-01

    The Ni-Cr-Fe metal powder was deposited on EA4T steel by laser cladding technology. The microstructure and chemical composition of the cladding layer were analyzed by optical microscopy (OM), scanning electron microscopy (SEM) and X-ray diffraction (XRD). The bonding ability between the cladding layer and the matrix was measured. The results showed that the bonding between the cladding layer and the EA4T steel was metallurgical bonding. The microstructure of cladding layer was composed of planar crystals, columnar crystals and dendrite, which consisted of Cr2Ni3, γ phase, M23C6 and Ni3B phases. When the powder feeding speed reached 4 g/min, the upper bainite occurred in the heat affected zone (HAZ). Moreover, the tensile strength of the joint increased, while the yield strength and the ductility decreased.

  3. The Application of 40Ti-35Ni-25Nb Filler Foil in Brazing Commercially Pure Titanium

    Directory of Open Access Journals (Sweden)

    Shan-Bo Wang

    2018-03-01

    Full Text Available The clad ternary 40Ti-35Ni-25Nb (wt % foil has been applied in brazing commercially pure titanium (CP-Ti. The wavelength dispersive spectroscope (WDS was utilized for quantitative chemical analyses of various phases/structures, and electron back scattered diffraction (EBSD was used for crystallographic analyses in the brazed joint. The microstructure of brazed joint relies on the Nb and Ni distributions across the joint. For the β-Ti alloyed with high Nb and low Ni contents, the brazed zone (BZ, consisting of the stabilized β-Ti at room temperature. In contrast, eutectoid decomposition of the β-Ti into Ti2Ni and α-Ti is widely observed in the transition zone (TZ of the joint. Although average shear strengths of joints brazed at different temperatures are approximately the same level, their standard deviations decreased with increasing the brazing temperature. The presence of inherent brittle Ti2Ni intermetallics results in higher standard deviation in shear test. Because the Ni content is lowered in TZ at a higher brazing temperature, the amount of eutectoid is decreased in TZ. The fracture location is changed from TZ into BZ mixed with α and β-Ti.

  4. Defect analysis of NiMnSb epitaxial layers

    Energy Technology Data Exchange (ETDEWEB)

    Nowicki, L. [Andrzej SoItan Institute for Nuclear Studies, ul. Hoza 69, 00-681 Warsaw (Poland)]. E-mail: lech.nowicki@fuw.edu.pl; Turos, A. [Andrzej SoItan Institute for Nuclear Studies, ul. Hoza 69, 00-681 Warsaw (Poland); Institute of Electronic Materials Technology, Wolczynska 133, 01-919 Warsaw (Poland); Stonert, A. [Andrzej SoItan Institute for Nuclear Studies, ul. Hoza 69, 00-681 Warsaw (Poland); Garrido, F. [Centre de Spectrometrie Nucleaire et Spectrometrie de Masse, CNRS-IN2P3-Universite Paris-Sud, 91405 Orsay (France); Molenkamp, L.W. [Department of Physics, University Wuerzburg, Am Hubland, 97074 Wuerzburg (Germany); Bach, P. [Department of Physics, University Wuerzburg, Am Hubland, 97074 Wuerzburg (Germany); Schmidt, G. [Department of Physics, University Wuerzburg, Am Hubland, 97074 Wuerzburg (Germany); Karczewski, G. [Institute of Physics, Polish Academy of Sciences, Al. Lotnikow 32/46, 02-668 Warsaw (Poland); Muecklich, A. [Forschungszentrum Rossendorf, Institut fuer Ionenstrahlphysik und Materialforschung, POB 510119, 01314 Dresden (Germany)

    2005-10-15

    NiMnSb layers grown on InP substrates with InGaAs buffer were studied by the backscattering/channeling spectrometry (RBS/C) with He beams. The nature of predominant defects observed in the layers was studied by determination of incident-energy dependence of the relative channeling yield. The defects are described as a combination of large amount of interstitial atoms and of stacking faults or grain boundaries. The presence of grains was confirmed by transmission electron microscopy.

  5. Evolution Of Lattice Structure And Chemical Composition Of The Surface Reconstruction Layer In Li1.2Ni0.2Mn0.6O2 Cathode Material For Lithium Ion Batteries

    Energy Technology Data Exchange (ETDEWEB)

    Yan, Pengfei; Nie, Anmin; Zheng, Jianming; Zhou, Yungang; Lu, Dongping; Zhang, Xiaofeng; Xu, Rui; Belharouak, Ilias; Zu, Xiaotao; Xiao, Jie; Amine, Khalil; Liu, Jun; Gao, Fei; Shahbazian-Yassar, Reza; Zhang, Jiguang; Wang, Chong M.

    2015-01-14

    Voltage and capacity fading of layer structured lithium and manganese rich (LMR) transition metal oxide is directly related to the structural and composition evolution of the material during the cycling of the battery. However, understanding such evolution at atomic level remains elusive. Based on atomic level structural imaging, elemental mapping of the pristine and cycled samples and density functional theory calculations, it is found that accompanying the hoping of Li ions is the simultaneous migration of Ni ions towards the surface from the bulk lattice, leading to the gradual depletion of Ni in the bulk lattice and thickening of a Ni enriched surface reconstruction layer (SRL). Furthermore, Ni and Mn also exhibit concentration partitions within the thin layer of SRL in the cycled samples where Ni is almost depleted at the very surface of the SRL, indicating the preferential dissolution of Ni ions in the electrolyte. Accompanying the elemental composition evolution, significant structural evolution is also observed and identified as a sequential phase transition of C2/m →I41→Spinel. For the first time, it is found that the surface facet terminated with pure cation is more stable than that with a mixture of cation and anion. These findings firmly established how the elemental species in the lattice of LMR cathode transfer from the bulk lattice to surface layer and further into the electrolyte, clarifying the long standing confusion and debate on the structure and chemistry of the surface layer and their correlation with the voltage fading and capacity decaying of LMR cathode. Therefore, this work provides critical insights for designing of cathode materials with both high capacity and voltage stability during cycling.

  6. Structural and technological formation of surface nanostructured Ti-Ni-Mo layers by high-speed gas-flame spraying

    Directory of Open Access Journals (Sweden)

    Blednova Zhesfina

    2015-01-01

    Full Text Available The article covers a complex method of forming surface-modified layers using materials with shape memory effect (SME based on TiNiMo including pre-grinding and mechanical activation of the coating material, high-speed gas-flame spraying of Ni adhesive layer and subsequent TiNiMo spraying with molybdenum content up to 2%, thermal and thermomechanical processing in a single technological cycle. This allowed forming nanostructured surface layers with a high level of functional mechanical and performance properties. We defined control parameters of surface steel modification using material with shape memory effect based on TiNiMo, which monitor the structural material state, both at the stage of spraying, and during subsequent combined treatment, which allows affecting purposefully on the functional properties of the SME surface layer. Test results of samples before coating and after surface modification with TiNiMo in the seawater indicate that surface modification brings to a slower damage accumulation and to increase of steel J91171 endurance limit in seawater by 45%. Based on complex metallophysical research of surface layers we obtained new data about nano-sized composition “steel - Ni - TiNiMo”.

  7. Interfacial mixing in as-deposited Si/Ni/Si layers analyzed by x-ray and polarized neutron reflectometry

    Energy Technology Data Exchange (ETDEWEB)

    Bhattacharya, Debarati, E-mail: debarati@barc.gov.in [Solid State Physics Division, Bhabha Atomic Research Centre, Trombay, Mumbai 400085 (India); Basu, Saibal; Singh, Surendra [Solid State Physics Division, Bhabha Atomic Research Centre, Trombay, Mumbai 400085 (India); Roy, Sumalay; Dev, Bhupendra Nath [Department of Materials Science, Indian Association for the Cultivation of Science, 2A and 2B Raja S.C. Mullick Road, Jadavpur, Kolkata 700032 (India)

    2012-12-15

    Highlights: Black-Right-Pointing-Pointer Room temperature diffusion in Si/Ni/Si trilayer detected through complementary x-ray and polarized neutron reflectometry. Black-Right-Pointing-Pointer Analyses of XPNR data generated the construction of the layered structure in terms of physical parameters along with alloy layers created by diffusion. Black-Right-Pointing-Pointer Scattering length density information from XPNR provided quantitative assessment of the stoichiometry of alloys formed at the Si/Ni and Ni/Si interfaces. - Abstract: Interdiffusion occurring across the interfaces in a Si/Ni/Si layered system during deposition at room temperature was probed using x-ray reflectivity (XRR) and polarized neutron reflectivity (PNR). Exploiting the complementarity of these techniques, both structural and magnetic characterization with nanometer depth resolution could be achieved. Suitable model fitting of the reflectivity profiles identified the formation of Ni-Si mixed alloy layers at the Si/Ni and Ni/Si interfaces. The physical parameters of the layered structure, including quantitative assessment of the stoichiometry of interfacial alloys, were obtained from the analyses of XRR and PNR patterns. In addition, PNR provided magnetic moment density profile as a function of depth in the stratified medium.

  8. Characteristics of electroplated Ni thick film on the PN junction semiconductor for beta-voltaic battery

    Energy Technology Data Exchange (ETDEWEB)

    Kim, Jin Joo; Uhm, Young Rang; Park, Keun Young; Son, Kwang Jae [Radioisotope Research Division, Korea Atomic Energy Research Institute, Daejeon (Korea, Republic of)

    2014-12-15

    Nickel (Ni) electroplating was implemented by using a metal Ni powder in order to establish a {sup 63}Ni plating condition on the PN junction semiconductor needed for production of betavoltaic battery. PN junction semiconductors with a Ni seed layer of 500 and 1000 Å were coated with Ni at current density from 10 to 50 mA cm{sup -2}. The surface roughness and average grain size of Ni deposits were investigated by XRD and SEM techniques. The roughness of Ni deposit was increased as the current density was increased, and decreased as the thickness of Ni seed layer was increased. The results showed that the optimum surface shape was obtained at a current density of 10 mA cm{sup -2} in seed layer with thickness of 500 Å, 20 mA cm{sup -2} of 1000 Å. Also, pure Ni deposit was well coated on a PN junction semiconductor without any oxide forms. Using the line width of (111) in XRD peak, the average grain size of the Ni thick firm was measured. The results showed that the average grain size was increased as the thickness of seed layer was increased.

  9. Characteristics of electroplated Ni thick film on the PN junction semiconductor for beta-voltaic battery

    International Nuclear Information System (INIS)

    Kim, Jin Joo; Uhm, Young Rang; Park, Keun Young; Son, Kwang Jae

    2014-01-01

    Nickel (Ni) electroplating was implemented by using a metal Ni powder in order to establish a 63 Ni plating condition on the PN junction semiconductor needed for production of betavoltaic battery. PN junction semiconductors with a Ni seed layer of 500 and 1000 Å were coated with Ni at current density from 10 to 50 mA cm -2 . The surface roughness and average grain size of Ni deposits were investigated by XRD and SEM techniques. The roughness of Ni deposit was increased as the current density was increased, and decreased as the thickness of Ni seed layer was increased. The results showed that the optimum surface shape was obtained at a current density of 10 mA cm -2 in seed layer with thickness of 500 Å, 20 mA cm -2 of 1000 Å. Also, pure Ni deposit was well coated on a PN junction semiconductor without any oxide forms. Using the line width of (111) in XRD peak, the average grain size of the Ni thick firm was measured. The results showed that the average grain size was increased as the thickness of seed layer was increased

  10. High-resolution electron microscopy study of Ni81Fe19 film with Co33Cr67 buffer layer

    International Nuclear Information System (INIS)

    Xu, Q.Y.; Wang, Z.M.; Shen, F.; Du, Y.W.; Zhang, Z.

    2003-01-01

    The anisotropic magnetoresistance (AMR) in permalloy Ni 81 Fe 19 film deposited on a 1.2 nm Co 33 Cr 67 buffer layer was significantly enhanced. The high-resolution electron microscopy was used to study the microstructure of Ni 81 Fe 19 film with and without Co 33 Cr 67 buffer layer. It was found that Co 33 Cr 67 buffer layer can induce good (1 1 1) texture, while without Co 33 Cr 67 buffer layer, Ni 81 Fe 19 film show randomly oriented grain structure. The Δρ/ρ enhancement is attributed to the decrease in the resistivity ρ of the Ni 81 Fe 19 film due to the formation of the large (1 1 1) textured grains in Ni 81 Fe 19 film with Co 33 Cr 67 buffer layer. However, the surface roughness of substrate may limit the (1 1 1) textured grain size and induce additional grain boundaries in Ni 81 Fe 19 film with Co 33 Cr 67 buffer layer, limit the enhancement of the AMR effect

  11. Sputtering yields of Si and Ni from the I sub(1-x)Si sub(x) system studied by Rutherford backscattering spectrometry

    International Nuclear Information System (INIS)

    Kim, Su-Chol; Yamaguchi, Satoru; Kataoka, Yoshihide; Iwami, Motohiro; Hiraki, Akio; Satou, Mamoru; Fujimoto, Fuminori.

    1982-01-01

    Sputtering yields of Si and Ni from thin layer films of Ni-Si compounds (Ni sub(1-x)Si sub(x)), including the pure materials (Ni and Si), caused by 5keV Ar + ion bombardment were investigated using backscattering spectrometry. The sputtering yield for Si from Ni sub(1-x)Si sub(x) increased with increasing Si concentration. However, there is an abrupt decrease in the yield for Si concentrations above NiSi 2 to pure Si. This is in clear contrast to the sputtering yield of Ni from Ni sub(1-x)Si sub(x) which increased with increasing Ni concentration monotonously. These results are discussed on the basis of both the difference in the atomic density and the electronic state of the alloy. (author)

  12. Anti-corrosion layer prepared by plasma electrolytic carbonitriding on pure aluminum

    International Nuclear Information System (INIS)

    Wu, Jie; Zhang, Yifan; Liu, Run; Wang, Bin; Hua, Ming; Xue, Wenbin

    2015-01-01

    Highlights: • PEC/N can be applied to low melting point metal. • The spectroscopic characterization of plasma discharge is investigated. • Electron concentration and electron temperature are evaluated for PEC/N. • Phase composition of the carbonitrided layer is determined. • PEC/N improves the corrosion resistance of aluminum greatly. - Abstract: In this paper, plasma electrolytic carbonitriding (PEC/N) method was applied to pure aluminum for the first time. The spectroscopic characterization of plasma discharge during PEC/N process was analyzed and the electron temperature was calculated in terms of optical emission spectroscopy. The results showed the discharge plasma was in local thermal equilibrium (LTE) state. Electron concentration and electron temperature were about 6 × 10 21 m −3 and 4000 K, respectively. The carbonitrided layer contained Al 4 C 3 , AlN and Al 7 C 3 N 3 phases. After PEC/N treatment, the corrosion resistance of pure aluminum was significantly improved, which was related to the formation of nitride phases. This work expands the application of plasma electrolysis technology on the surface modification of low melting point metal

  13. Magnetic Properties of Ni-Zn Ferrite Prepared with the Layered Precursor Method

    International Nuclear Information System (INIS)

    Zhou Xin; Hou Zhi-Ling; Li Feng; Qi Xin

    2010-01-01

    We prepare NiZnFe 2 O 4 soft magnetic ferrites with different molar ratios with the layered precursor method and investigate their magnetic properties. In the layered precursor, metal ions are scattered on the layer plate in a certain way on account of the effect of lowest lattice energy and lattice orientation. After high temperature calcinations, spinel ferrites with uniform structural component and single magnetic domain can be obtained, and the magnetic property is improved greatly. NiZnFe 2 O 4 ferrites prepared have the best specific saturation magnetization of 79.15 emu·g −1 , higher than that of 68 emu·g −1 prepared by the chemical co-precipitation method and that of 59 emu·g −1 prepared by the emulsion-gel method. Meanwhile the coercivity of NiZnFe 2 O 4 ferrites prepared by layered precursor method is 14 kA·m −1 , lower than that of 50 emu·g −1 prepared by the co-precipitation method and that of 59 emu·g −1 prepared by the emulsion-gel method. (condensed matter: electronic structure, electrical, magnetic, and optical properties)

  14. Characteristics of Ni-based coating layer formed by laser and plasma cladding processes

    International Nuclear Information System (INIS)

    Xu Guojian; Kutsuna, Muneharu; Liu Zhongjie; Zhang Hong

    2006-01-01

    The clad layers of Ni-based alloy were deposited on the SUS316L stainless plates by CO 2 laser and plasma cladding processes. The smooth clad bead was obtained by CO 2 laser cladding process. The phases of clad layer were investigated by an optical microscope, scanning electron microscopy (SEM), X-ray diffractometer (XRD), electron probe microanalysis (EPMA) and energy-dispersive spectrometer (EDS). The microstructures of clad layers belonged to a hypereutectic structure. Primary phases consist of boride CrB and carbide Cr 7 C 3 . The eutectic structure consists of Ni + CrB or Ni + Cr 7 C 3 . Compared with the plasma cladding, the fine microstructures, low dilutions, high Vickers hardness and excellent wear resistance were obtained by CO 2 laser cladding. All that show the laser cladding process has a higher efficiency and good cladding quality

  15. Effect of surfactant on electrodeposited Ni-P layer as an under bump metallization

    International Nuclear Information System (INIS)

    Lin, Yung-Chi; Duh, Jenq-Gong

    2007-01-01

    In the microelectronic industry, the nickel plating has been used as the under bump metallization (UBM). The electroplated process was demonstrated to be a favorable alternative approach to produce the Ni-P layer as UBM. In this study, the role of sodium dodecylsulfate (SDS) addition in electrodeposition was investigated. The variations on surface morphology and surface roughness in the SDS-added process of electroplated Ni-P were revealed with both field emission scanning electronic microscope and atomic force microscope. The influence of SDS addition process in wettability of several commercial solder pastes, including Sn-37Pb, Sn-3.5Ag, and Sn-3.0Ag-0.5Cu, on electroplated Ni-P with various phosphorous contents was evaluated. The surface morphology and the surface roughness of Ni-P layer were affected by SDS addition. It was demonstrated that modified surface morphology and surface roughness acted to enhance the wettability of electroplated Ni-P. In addition, the interfacial reactions between Sn-3.0Ag-0.5Cu and electroplated Ni-P UBM with SDS addition during deposition was also probed and discussed

  16. Influence of Ni Catalyst Layer and TiN Diffusion Barrier on Carbon Nanotube Growth Rate

    Directory of Open Access Journals (Sweden)

    Mérel Philippe

    2010-01-01

    Full Text Available Abstract Dense, vertically aligned multiwall carbon nanotubes were synthesized on TiN electrode layers for infrared sensing applications. Microwave plasma-enhanced chemical vapor deposition and Ni catalyst were used for the nanotubes synthesis. The resultant nanotubes were characterized by SEM, AFM, and TEM. Since the length of the nanotubes influences sensor characteristics, we study in details the effects of changing Ni and TiN thickness on the physical properties of the nanotubes. In this paper, we report the observation of a threshold Ni thickness of about 4 nm, when the average CNT growth rate switches from an increasing to a decreasing function of increasing Ni thickness, for a process temperature of 700°C. This behavior is likely related to a transition in the growth mode from a predominantly “base growth” to that of a “tip growth.” For Ni layer greater than 9 nm the growth rate, as well as the CNT diameter, variations become insignificant. We have also observed that a TiN barrier layer appears to favor the growth of thinner CNTs compared to a SiO2 layer.

  17. Interfacial mixing in as-deposited Si/Ni/Si layers analyzed by x-ray and polarized neutron reflectometry

    International Nuclear Information System (INIS)

    Bhattacharya, Debarati; Basu, Saibal; Singh, Surendra; Roy, Sumalay; Dev, Bhupendra Nath

    2012-01-01

    Highlights: ► Room temperature diffusion in Si/Ni/Si trilayer detected through complementary x-ray and polarized neutron reflectometry. ► Analyses of XPNR data generated the construction of the layered structure in terms of physical parameters along with alloy layers created by diffusion. ► Scattering length density information from XPNR provided quantitative assessment of the stoichiometry of alloys formed at the Si/Ni and Ni/Si interfaces. - Abstract: Interdiffusion occurring across the interfaces in a Si/Ni/Si layered system during deposition at room temperature was probed using x-ray reflectivity (XRR) and polarized neutron reflectivity (PNR). Exploiting the complementarity of these techniques, both structural and magnetic characterization with nanometer depth resolution could be achieved. Suitable model fitting of the reflectivity profiles identified the formation of Ni–Si mixed alloy layers at the Si/Ni and Ni/Si interfaces. The physical parameters of the layered structure, including quantitative assessment of the stoichiometry of interfacial alloys, were obtained from the analyses of XRR and PNR patterns. In addition, PNR provided magnetic moment density profile as a function of depth in the stratified medium.

  18. Comparison of reduction agents in the synthesis of infinite-layer LaNiO2 films

    Science.gov (United States)

    Ikeda, Ai; Manabe, Takaaki; Naito, Michio

    2014-11-01

    Reduction agents, such as activated carbon, TiH2, and CaH2, were compared from a viewpoint of the facility for the topotactic reduction of LaNiO3 to LaNiO2 films. Activated carbon did not yield infinite-layer LaNiO2 whereas both of TiH2 and CaH2 yielded infinite-layer LaNiO2 with low resistivity (∼1 mΩ cm at 300 K) as well as metallic behavior down to 70 K. Thermal desorption spectroscopy indicated that H2 released from metal hydrides plays a dominant role in the topotactic reduction.

  19. Posterior magnetic effect on the pure and doped Fe-Ni alloy under neutron irradiation

    International Nuclear Information System (INIS)

    Ferreira, Iris

    1974-01-01

    Polycrystalline specimens of unirradiated and neutron irradiated Fe-Ni alloys have been studied in the temperature range RT - 500 deg C. The study was carried out in pure (50-50) as well as in Si, A1, Cr and Mo doped samples. Initial magnetic permeability was measured in unirradiated (virgin)and in neutron irradiated samples, during isochronal and linear thermal treatments. The main results are: a magnetic After Effect (MAE) is detected in the temperature range 370 deg C - Tc, where Tc is the Curie Temperature. In this range an activation energy of 3.2 ± 0.2 eV was determined for the Cr doped Fe-Ni alloy (impurity content: 0.1%); measurements made in the irradiated samples, during a linear temperature treatment, show the existence of several MAE zones in the temperature range RT - Tc. The isochronal annealing experiments show that these MAE zones are accompanied by a decrease in the room temperature value of the magnetic permeability, for zones between RT and a certain temperature T 1 . Above this range there is a steep increase in the room temperature permeability. Activation energies were determined for pure and Mo-doped (0.1%) samples for the first MAE zone (50 deg C - 120 deg C). The values obtained 1.25 - 0.08 eV and 1.42 ± 0.09 eV, respectively; the impurity - doped samples show a different behaviour relative to the pure ones: samples with low impurity content (0.1% and 0.5% of Si, Al or Mo) present an enhancement in the amplitude and also an overlapping of the diffusion stages. On the other hand, samples with higher impurity content (2 and 4% of Mo) show a decrease in these amplitudes. (author)

  20. Comparison of reduction agents in the synthesis of infinite-layer LaNiO{sub 2} films

    Energy Technology Data Exchange (ETDEWEB)

    Ikeda, Ai [Department of Applied Physics, Tokyo University of Agriculture and Technology, Naka-cho 2-24-16, Koganei, Tokyo 184-8588 (Japan); Research Fellow of the Japan Society for the Promotion of Science, Ichiban-cho 8, Chiyoda, Tokyo 102-8472 (Japan); Manabe, Takaaki [National Institute of Advanced Industrial Science and Technology (AIST), Higashi 1-1-1, Tsukuba, Ibaraki 305-8565 (Japan); Naito, Michio, E-mail: minaito@cc.tuat.ac.jp [Department of Applied Physics, Tokyo University of Agriculture and Technology, Naka-cho 2-24-16, Koganei, Tokyo 184-8588 (Japan)

    2014-11-15

    Highlights: • Reduction agents were compared from a viewpoint of the facility for topotactic reduction of LaNiO{sub 3} to LaNiO{sub 2} films. • TiH{sub 2} and CaH{sub 2} yielded infinite-layer LaNiO{sub 2} with low and metallic resistivity. • H{sub 2} released from metal hydrides plays a dominant role in the topotactic reduction. - Abstract: Reduction agents, such as activated carbon, TiH{sub 2}, and CaH{sub 2}, were compared from a viewpoint of the facility for the topotactic reduction of LaNiO{sub 3} to LaNiO{sub 2} films. Activated carbon did not yield infinite-layer LaNiO{sub 2} whereas both of TiH{sub 2} and CaH{sub 2} yielded infinite-layer LaNiO{sub 2} with low resistivity (∼1 mΩ cm at 300 K) as well as metallic behavior down to 70 K. Thermal desorption spectroscopy indicated that H{sub 2} released from metal hydrides plays a dominant role in the topotactic reduction.

  1. P-channel transparent thin-film transistor using physical-vapor-deposited NiO layer

    Science.gov (United States)

    Lin, Chiung-Wei; Chung, Wei-Chieh; Zhang, Zhao-De; Hsu, Ming-Chih

    2018-01-01

    The effect of oxygen (O) content on the electrical properties of physical-vapor-deposited nickel oxide (PVD-NiO) was studied. When the NiO target was sputtered, introducing O2 can lead to the formation of Ni3+ ions in the deposited film. These Ni3+ ions can act as acceptors. However, there were too many Ni3+ ions that were obtained following the introduction of O atoms. It resulted in intensive p-type conduction and made the O2-introduced PVD-NiO behave as a conductor. Thus, it was possible to reduce the O content of PVD-NiO to obtain a p-type semiconductor. In this study, a transparent PVD-NiO film with a carrier concentration of 1.62 × 1017 cm-3 and a resistivity of 3.74 Ω cm was sputter-deposited within pure argon plasma. The thin-film transistor (TFT) employing this proposed PVD-NiO can result in good current switching, and even operated at very low drain-source voltage. The ON/OFF current ratio, field-effect carrier mobility, and threshold voltage of the proposed NiO TFT were 3.61 × 104, 1.09 cm2 V-1 s-1 and -3.31 V, respectively.

  2. Review on structural fatigue of NiTi shape memory alloys: Pure mechanical and thermo-mechanical ones

    Directory of Open Access Journals (Sweden)

    Guozheng Kang

    2015-11-01

    Full Text Available Structural fatigue of NiTi shape memory alloys is a key issue that should be solved in order to promote their engineering applications and utilize their unique shape memory effect and super-elasticity more sufficiently. In this paper, the latest progresses made in experimental and theoretical analyses for the structural fatigue features of NiTi shape memory alloys are reviewed. First, macroscopic experimental observations to the pure mechanical and thermo-mechanical fatigue features of the alloys are summarized; then the state-of-arts in the mechanism analysis of fatigue rupture are addressed; further, advances in the construction of fatigue failure models are provided; finally, summary and future topics are outlined.

  3. Diffusion complex layers of TiC-Ni-Mo type produced on steel during vacuum titanizing process combined with the electrolytic deposition

    International Nuclear Information System (INIS)

    Kasprzycka, E.; Krolikowski, A.

    1999-01-01

    Diffusion carbide layers produced on steel surface by means of vacuum titanizing process have been studied. A new technological process combining a vacuum titanizing with an electrolytic deposition of Ni-Mo alloy has been proposed to increase of corrosion resistance of carbide layers. The effect of preliminary electrolytic deposition of Ni-Mo alloy on the NC10 steel surface on the titanized layer structure and its corrosion resistance has ben investigated. As a result, diffusion complex layers of TiC-Ni-Mo type on NC10 steel surface have been obtained. An X-ray structural analysis of titanized surfaces on NC10 steel precovered with an electrolytic Ni-Mo alloy coating (70%Ni+30%Mo) revealed a presence of titanium carbide TiC, NiTi, MoTi and trace quantity of austenite. The image of the TiC-Ni-Mo complex layer on NC10 steel surface obtained by means of joined SEM+TEM method and diagrams of elements distribution in the layer diffusion zone have been shown. Concentration of depth profiles of Ti, Ni, Mo, Cr and Fe in the layer diffusion zone obtained by means of the joined EDS+TEM method are shown. Concentration depth profiles of Ti, Ni, Mo, Cr and Fe in the layer diffusion zone obtained by means of the X r ay microanalysis and microhardness of the layer are shown. An X-ray structural analysis of titanized surfaces on the NC10 steel, without Ni-Mo alloy layer, revealed only a substantial presence of titanium carbide TiC. For corrosion resistance tests the steel samples with various diffusion layers and without layers were used: (i) the TiC-Ni-Mo titanized complex layers on NC10 steel, (ii) the TiC titanized carbide layers on the NC10 steel, (iii) the NC10 steel without layers. Corrosion measurements of sample under test have been performed in 0.1 M H 2 SO 4 by means of potentiodynamic polarization and electrochemical impedance tests. It has been found that the corrosion resistance of titanized steel samples with the TiC and TiC-Ni-Mo layers is higher than for the steel

  4. Achievement of normally-off AlGaN/GaN high-electron mobility transistor with p-NiO{sub x} capping layer by sputtering and post-annealing

    Energy Technology Data Exchange (ETDEWEB)

    Huang, Shyh-Jer [Department of Electrical Engineering, Institute of Microelectronics and Advanced Optoelectronic Technology Center, National Cheng Kung University, Tainan, Taiwan (China); Chou, Cheng-Wei, E-mail: j2222222229@gmail.com [Department of Electrical Engineering, Institute of Microelectronics and Advanced Optoelectronic Technology Center, National Cheng Kung University, Tainan, Taiwan (China); Su, Yan-Kuin, E-mail: yksu@mail.ncku.edu.tw [Department of Electrical Engineering, Institute of Microelectronics and Advanced Optoelectronic Technology Center, National Cheng Kung University, Tainan, Taiwan (China); Lin, Jyun-Hao; Yu, Hsin-Chieh; Chen, De-Long [Department of Electrical Engineering, Institute of Microelectronics and Advanced Optoelectronic Technology Center, National Cheng Kung University, Tainan, Taiwan (China); Ruan, Jian-Long [National Chung-Shan Institute of Science and Technology, Taoyuan, Taiwan (China)

    2017-04-15

    Highlights: • A technique to fabricate normally off GaN-based high-electron mobility transistor (HEMT) by sputtering and post-annealing p-NiO{sub x} capping layer. • The V{sub th} shifts from −3 V in the conventional transistor to 0.33 V, and on/off current ratio became 10{sup 7}. • The reverse gate leakage current is 10{sup −9} A/mm, and the off-state drain-leakage current is 10{sup −8} A/mm. • The V{sub th} hysteresis is extremely small at about 33 mV. - Abstract: In this paper, we present a technique to fabricate normally off GaN-based high-electron mobility transistor (HEMT) by sputtering and post-annealing p-NiO{sub x} capping layer. The p-NiO{sub x} layer is produced by sputtering at room temperature and post-annealing at 500 °C for 30 min in pure O{sub 2} environment to achieve high hole concentration. The V{sub th} shifts from −3 V in the conventional transistor to 0.33 V, and on/off current ratio became 10{sup 7}. The forward and reverse gate breakdown increase from 3.5 V and −78 V to 10 V and −198 V, respectively. The reverse gate leakage current is 10{sup −9} A/mm, and the off-state drain-leakage current is 10{sup −8} A/mm. The V{sub th} hysteresis is extremely small at about 33 mV. We also investigate the mechanism that increases hole concentration of p-NiO{sub x} after annealing in oxygen environment resulted from the change of Ni{sup 2+} to Ni{sup 3+} and the surge of (111)-orientation.

  5. A structural study of effects of NiP seed layer on the magnetic properties of CoCrPt/Ti/NiP perpendicular magnetic films

    CERN Document Server

    Sun, C J; Wang, J P; Soo, E W; Noh, D Y; Je, J H; Hwu, Y K

    2003-01-01

    The CoCrPt/Ti/NiP films for perpendicular magnetic recording were studied using X-ray scattering and anomalous X-ray scattering. When the NiP seed layer was used, the long range order of the texture peak of the magnetic film decreased and less Co was associated with this Bragg order. The structural results were consistent with the observed increased coercivity and decreased magnetization due to the increased magnetic grain isolation caused by the presence of NiP seed layer.

  6. Multiphase layered oxide growth on pure metals. I. General formulation

    International Nuclear Information System (INIS)

    Fromhold, A.T. Jr.

    1982-01-01

    A general formulation for the simultaneous growth of any number of layered planar oxide phases on a pure metal under diffusion-controlled conditions has been developed. Four individual situations have been developed in detail, namely, situations in which the predominant mode of ion transport is by cation interstitials, cation vacancies, anion interstitials, or anion vacancies. The generalized formulation enables the determination of quasi-steady-state growth kinetics following step function changes in the experimental conditions such as ambient oxygen pressure or temperature. Numerical evaluation of the coupled growth equations for the individual phases is required to deduce the general predictions of the theory. In the limit of two-layer growth by cation interstitial diffusion, the present formulation reproduces the earlier results of Fromhold and Sato

  7. Anti-corrosion layer prepared by plasma electrolytic carbonitriding on pure aluminum

    Energy Technology Data Exchange (ETDEWEB)

    Wu, Jie; Zhang, Yifan; Liu, Run; Wang, Bin; Hua, Ming [Key Laboratory for Beam Technology and Materials Modification of Ministry of Education, College of Nuclear Science and Technology, Beijing Normal University, Beijing 100875 (China); Beijing Radiation Center, Beijing 100875 (China); Xue, Wenbin, E-mail: xuewb@bnu.edu.cn [Key Laboratory for Beam Technology and Materials Modification of Ministry of Education, College of Nuclear Science and Technology, Beijing Normal University, Beijing 100875 (China); Beijing Radiation Center, Beijing 100875 (China)

    2015-08-30

    Highlights: • PEC/N can be applied to low melting point metal. • The spectroscopic characterization of plasma discharge is investigated. • Electron concentration and electron temperature are evaluated for PEC/N. • Phase composition of the carbonitrided layer is determined. • PEC/N improves the corrosion resistance of aluminum greatly. - Abstract: In this paper, plasma electrolytic carbonitriding (PEC/N) method was applied to pure aluminum for the first time. The spectroscopic characterization of plasma discharge during PEC/N process was analyzed and the electron temperature was calculated in terms of optical emission spectroscopy. The results showed the discharge plasma was in local thermal equilibrium (LTE) state. Electron concentration and electron temperature were about 6 × 10{sup 21} m{sup −3} and 4000 K, respectively. The carbonitrided layer contained Al{sub 4}C{sub 3}, AlN and Al{sub 7}C{sub 3}N{sub 3} phases. After PEC/N treatment, the corrosion resistance of pure aluminum was significantly improved, which was related to the formation of nitride phases. This work expands the application of plasma electrolysis technology on the surface modification of low melting point metal.

  8. Internal carbonitriding behavior of Ni-V, Ni-Cr, and Ni-3Nb alloys

    International Nuclear Information System (INIS)

    Allen, A.T.; Douglass, D.L.

    1999-01-01

    Ni-2V, Ni-5V, Ni-12V, Ni-10Cr, Ni-20Cr, and Ni-3Nb alloys were carbonitrided in C 3 H 6 and NH 3 gas mixtures (bal H 2 ) over the range 700--1,000 C. Carbonitridation of Ni-12V and Ni-20Cr in C 3 H 6 /NH 3 /H 2 (1.5/1.5/97 v/o) and (1.5/10/88.5 v/o) produced duplex subscales consisting of near-surface nitrides with underlying carbides. Growth of each zone obeyed the parabolic rate law under most conditions. The presence of carbon generally did not effect the depth of the nitride zones compared to nitriding the alloys in NH 3 /H 2 (10/90 v/o). However, at 700 C, the nitride zones were deeper in the carbonitrided Ni-V alloys and Ni-20Cr. The presence of nitrogen generally increased the depth of the carbide zones in Ni-12V and Ni-20Cr compared to carburizing these alloys in C 3 H 6 /H 2 (1.5/98.5 v/o). VN, CrN, and NbN formed in Ni-V, Ni-Cr, and Ni-Nb alloys, respectively, whereas the underlying carbide layers contained V 4 C 3 in Ni-12V, Cr 3 C 2 above a zone of Cr 7 C 3 in Ni-20Cr, and NbC in Ni-3Nb. The solubilities and diffusivities of nitrogen and carbon in nickel were determined. Nitrogen and carbon each exhibited retrograde solubility with temperature in pure Ni in both carbonitriding environments. Nitrogen diffusion in nickel was generally lower in each carbonitriding mixture compared to nitrogen diffusion in a nitriding environment, except at 700 C when nitrogen diffusion was higher. Carbon diffusion in nickel was generally higher in the carbonitriding environments compared to carbon diffusion in a carburizing environment

  9. Preliminary Microstructural and Microscratch Results of Ni-Cr-Fe and Cr3C2-NiCr Coatings on Magnesium Substrate

    Science.gov (United States)

    Istrate, B.; Munteanu, C.; Lupescu, S.; Benchea, M.; Vizureanu, P.

    2017-06-01

    Thermal coatings have a large scale application in aerospace and automotive field, as barriers improving wear mechanical characteristics and corrosion resistance. In present research, there have been used two types of coatings, Ni-Cr-Fe, respectively Cr3C2-NiCr which were deposited on magnesium based alloys (pure magnesium and Mg-30Y master alloy). There have been investigated the microstructural aspects through scanning electronic microscopy and XRD analysis and also a series of mechanical characteristics through microscratch and indentation determinations. The results revealed the formation of some adherent layers resistant to the penetration of the metallic indenter, the coatings did not suffer major damages. Microstructural analysis highlighted the formation of Cr3C2, Cr7C3, Cr3Ni2, Cr7Ni3, FeNi3, Cr-Ni phases. Also, the apparent coefficient of friction for Ni-Cr-Fe coatings presents superior values than Cr3C2-NiCr coatings.

  10. An ac susceptibility study in capped Ni/Ni(OH)2 core-shell nanoassemblies: dual peak observations

    International Nuclear Information System (INIS)

    Godsell, Jeffrey F; Roy, Saibal; Bala, Tanushree; Ryan, Kevin M.

    2011-01-01

    In this study, the ac susceptibility (χ' and χ'') variation with temperature (10-100 K) for oleic acid (OA) capped Ni/Ni(OH) 2 core-shell nanoparticle assemblies are reported at frequencies varying from 0.1 to 1000 Hz. Nanoparticle assemblies, with two average particle diameters of ∼34 nm and ∼14 nm, were synthesized using a wet chemical synthesis approach. Two peaks in the ac susceptibility versus temperature curves are clearly discernable for each of the samples. The first, occurring at ∼22 K was attributed to the paramagnetic/antiferromagnetic transition of the Ni(OH) 2 present in the shell. The second higher temperature peak was attributed to the superparamagnetic blocking of the pure Ni situated at the core of the nanoparticles. The higher temperature peaks in both the χ' and χ'' curves were observed to increase with increasing frequency. Thus the Neel and the blocking temperatures for such core-shell nanoassemblies were clearly identified from the ac analysis, whereas they were not discernible (superimposed) even from very low dc (FC/ZFC) field measurements. Interparticle interactions within the assemblies were studied through the fitting of phenomenological laws to the experimental datasets. It is observed that even with an OA capping layer, larger Ni/Ni(OH) 2 nanoparticles experience a greater degree of sub-capping layer oxidation thus producing lower magnetic interaction strengths.

  11. Biodegradable polymer for sealing porous PEO layer on pure magnesium: An in vitro degradation study

    International Nuclear Information System (INIS)

    Alabbasi, Alyaa; Mehjabeen, Afrin; Kannan, M. Bobby; Ye, Qingsong; Blawert, Carsten

    2014-01-01

    Graphical abstract: - Highlights: • Poly(L-lactide) was used to seal the porous PEO layer on Mg. • The dual-layer coating improved the in vitro degradation resistance of Mg. • Localized degradation was inhibited in the dual-layer coated Mg. - Abstract: An attempt was made to seal the porous silicate-based plasma electrolytic oxidation (PEO) layer on pure magnesium (Mg) with a biodegradable polymer, poly(L-lactide) (PLLA), to delay the localized degradation of magnesium-based implants in body fluid for better in-service mechanical integrity. Firstly, a silicate-based PEO coating on pure magnesium was performed using a pulsed constant current method. In order to seal the pores in the PEO layer, PLLA was coated using a two-step spin coating method. The performance of the PEO–PLLA Mg was evaluated using electrochemical impedance spectroscopy (EIS) and potentiodynamic polarization. The EIS results showed that the polarization resistance (R p ) of the PEO–PLLA Mg was close to two orders of magnitude higher than that of the PEO Mg. While the corrosion current density (i corr ) of the pure Mg was reduced by 65% with the PEO coating, the PEO–PLLA coating reduced the i corr by almost 100%. As expected, the R p of the PEO–PLLA Mg decreased with increase in exposure time. However, it was noted that the R p of the PEO–PLLA Mg even after 100 h was six times higher than that of the PEO Mg after 48 h exposure, and did not show any visible localized attack

  12. Biodegradable polymer for sealing porous PEO layer on pure magnesium: An in vitro degradation study

    Energy Technology Data Exchange (ETDEWEB)

    Alabbasi, Alyaa; Mehjabeen, Afrin [Biomaterials and Engineering Materials (BEM) Laboratory, James Cook University, Townsville 4811, Queensland (Australia); Kannan, M. Bobby, E-mail: bobby.mathan@jcu.edu.au [Biomaterials and Engineering Materials (BEM) Laboratory, James Cook University, Townsville 4811, Queensland (Australia); Ye, Qingsong [Discipline of Dentistry, James Cook University, Townsville 4811, Queensland (Australia); Blawert, Carsten [Magnesium Innovation Centre, Institute of Materials Research, Helmholtz-Zentrum Geesthacht, Geesthacht 21502 (Germany)

    2014-05-01

    Graphical abstract: - Highlights: • Poly(L-lactide) was used to seal the porous PEO layer on Mg. • The dual-layer coating improved the in vitro degradation resistance of Mg. • Localized degradation was inhibited in the dual-layer coated Mg. - Abstract: An attempt was made to seal the porous silicate-based plasma electrolytic oxidation (PEO) layer on pure magnesium (Mg) with a biodegradable polymer, poly(L-lactide) (PLLA), to delay the localized degradation of magnesium-based implants in body fluid for better in-service mechanical integrity. Firstly, a silicate-based PEO coating on pure magnesium was performed using a pulsed constant current method. In order to seal the pores in the PEO layer, PLLA was coated using a two-step spin coating method. The performance of the PEO–PLLA Mg was evaluated using electrochemical impedance spectroscopy (EIS) and potentiodynamic polarization. The EIS results showed that the polarization resistance (R{sub p}) of the PEO–PLLA Mg was close to two orders of magnitude higher than that of the PEO Mg. While the corrosion current density (i{sub corr}) of the pure Mg was reduced by 65% with the PEO coating, the PEO–PLLA coating reduced the i{sub corr} by almost 100%. As expected, the R{sub p} of the PEO–PLLA Mg decreased with increase in exposure time. However, it was noted that the R{sub p} of the PEO–PLLA Mg even after 100 h was six times higher than that of the PEO Mg after 48 h exposure, and did not show any visible localized attack.

  13. Interfacial mixing in as-deposited Si/Ni/Si layers analyzed by x-ray and polarized neutron reflectometry

    Science.gov (United States)

    Bhattacharya, Debarati; Basu, Saibal; Singh, Surendra; Roy, Sumalay; Dev, Bhupendra Nath

    2012-12-01

    Interdiffusion occurring across the interfaces in a Si/Ni/Si layered system during deposition at room temperature was probed using x-ray reflectivity (XRR) and polarized neutron reflectivity (PNR). Exploiting the complementarity of these techniques, both structural and magnetic characterization with nanometer depth resolution could be achieved. Suitable model fitting of the reflectivity profiles identified the formation of Ni-Si mixed alloy layers at the Si/Ni and Ni/Si interfaces. The physical parameters of the layered structure, including quantitative assessment of the stoichiometry of interfacial alloys, were obtained from the analyses of XRR and PNR patterns. In addition, PNR provided magnetic moment density profile as a function of depth in the stratified medium.

  14. Characterizations of diverse mole of pure and Ni-doped α-Fe2O3 synthesized nanoparticles through chemical precipitation route.

    Science.gov (United States)

    Sivakumar, S; Anusuya, D; Khatiwada, Chandra Prasad; Sivasubramanian, J; Venkatesan, A; Soundhirarajan, P

    2014-07-15

    In the present study, an attempt has been made for characterization and synthesis of pure and Ni-doped α-Fe2O3 (hematite) nanoparticles by chemical precipitation method. The synthesized products have been studied by X-ray diffraction (X-RD), Fourier transform infrared (FTIR) spectroscopy, UV-Vis diffuse reflectance spectroscopy (UV-Vis DRS), vibrating sample magnetometer (VSM) and scanning electron microscopy (SEM) techniques. The estimated average diameter of α-Fe2O3 nanoparticles were calculated by using the Debye-Scherrer equation and established as 31 nm. SEM micrographs showed the surface morphology as well as structures and particles distributions of synthesized samples. The UV-Vis DRS showed the indirect and direct band gap energies of pure and Ni-doped α-Fe2O3, these were reduced from 1.9847 to 1.52 eV and 2.0503 to 1.76 eV respectively. This result suggested the dopant enhanced the semiconducting behavior of iron oxide nanoparticles to an extent proportional to its nickel doped in the α-Fe2O3. Further, the magnetic properties of the pure and doped samples were investigated by vibrating sample magnetometer (VSM) and evaluated the information of pure and doped samples exhibited saturated hysteresis loop at room temperature, which is indicating that the weak ferromagnetism in nature of our synthesized samples. In addition, it has been found from the magnetization hysteresis curves of Ni-doping, resulting from increased the saturation of magnetization and reduced the coercivity of used samples. Therefore, the present study showed the reduction in band gap energies and coercive field for α-Fe2O3 nanoparticles due to nickel doped. Copyright © 2014 Elsevier B.V. All rights reserved.

  15. Characterization of self-assembled films of NiGa layered double hydroxide nanosheets and their electrochemical properties

    International Nuclear Information System (INIS)

    Altuntasoglu, Ozge; Unal, Ugur; Ida, Shintaro; Goto, Motonobu; Matsumoto, Yasumichi

    2008-01-01

    In this study, we have demonstrated the synthesis and delamination of a rarely studied NiGa layered double hydroxide (LDH) system. Hydrothermal treatment under agitation conditions at 200 deg. C for 4 h resulted in the formation of highly crystalline NiGa LDHs in a shorter time than those synthesized without agitation. The LDH was delaminated into the individual nanosheets in formamide. The most significant finding in this study is the electrochemical behavior of interlayer ferricyanide anions intercalated with the layer-by-layer (LBL) assembly method. The morphology of LBL film with one layer is also monitored with atomic force microscopy. The cyclic voltammogram is similar to potassium metal hexacyanoferrate systems with its unique two-peak wave. Raman spectrum of the film revealed that the metal center of the interlayer cyano complex is in interaction with the Ni 2+ of the host layer. It was concluded that the two-peak cyclic voltammogram of the film is a result of two different forms of the hexacyanoferrate in the interlayer. - Graphical abstract: The thin film deposited from the nanosheets of ion-exchangeable NiGa LDH and ferricyanide molecule with LBL method gives the typical redox reaction of metal hexacyanoferrates in the interlayer. Current density depends on the number of layers

  16. Synthetic Control of Kinetic Reaction Pathway and Cationic Ordering in High-Ni Layered Oxide Cathodes

    Energy Technology Data Exchange (ETDEWEB)

    Wang, Dawei [Sustainable Energy Technologies Department, Brookhaven National Laboratory, Upton NY 11973 USA; Collaborative Innovation Center of Chemistry for Energy Materials, State Key Laboratory Physical Chemistry Solid Surfaces, Department of Chemistry, Xiamen University, Xiamen Fujian 361005 China; Kou, Ronghui [X-Ray Science Division, Advanced Photon Source, Argonne National Laboratory, Argonne IL 60439 USA; Ren, Yang [X-Ray Science Division, Advanced Photon Source, Argonne National Laboratory, Argonne IL 60439 USA; Sun, Cheng-Jun [X-Ray Science Division, Advanced Photon Source, Argonne National Laboratory, Argonne IL 60439 USA; Zhao, Hu [Sustainable Energy Technologies Department, Brookhaven National Laboratory, Upton NY 11973 USA; Zhang, Ming-Jian [Sustainable Energy Technologies Department, Brookhaven National Laboratory, Upton NY 11973 USA; School of Advanced Materials, Peking University Shenzhen Graduate School, Shenzhen Guangdong 518055 P. R. China; Li, Yan [Chemical Sciences and Engineering Division, Argonne National Laboratory, Argonne IL 60439 USA; Huq, Ashifia [Chemical and Engineering Materials Division, Oak Ridge National Laboratory, Oak Ridge TN 37831 USA; Ko, J. Y. Peter [The Cornell High Energy Synchrotron Source, Cornell University, Ithaca NY 14853 USA; Pan, Feng [School of Advanced Materials, Peking University Shenzhen Graduate School, Shenzhen Guangdong 518055 P. R. China; Sun, Yang-Kook [Department of Energy Engineering, Hanyang University, Seoul 133-791 South Korea; Yang, Yong [Collaborative Innovation Center of Chemistry for Energy Materials, State Key Laboratory Physical Chemistry Solid Surfaces, Department of Chemistry, Xiamen University, Xiamen Fujian 361005 China; Amine, Khalil [Chemical Sciences and Engineering Division, Argonne National Laboratory, Argonne IL 60439 USA; Bai, Jianming [National Synchrotron Light Source II, Brookhaven National Laboratory, Upton NY 11973 USA; Chen, Zonghai [Chemical Sciences and Engineering Division, Argonne National Laboratory, Argonne IL 60439 USA; Wang, Feng [Sustainable Energy Technologies Department, Brookhaven National Laboratory, Upton NY 11973 USA

    2017-08-25

    Nickel-rich layered transition metal oxides, LiNi1-x(MnCo)(x)O-2 (1-x >= 0.5), are appealing candidates for cathodes in next-generation lithium-ion batteries (LIBs) for electric vehicles and other large-scale applications, due to their high capacity and low cost. However, synthetic control of the structural ordering in such a complex quaternary system has been a great challenge, especially in the presence of high Ni content. Herein, synthesis reactions for preparing layered LiNi0.7Mn0.15Co0.15O2 (NMC71515) by solid-state methods are investigated through a combination of time-resolved in situ high-energy X-ray diffraction and absorption spectroscopy measurements. The real-time observation reveals a strong temperature dependence of the kinetics of cationic ordering in NMC71515 as a result of thermal-driven oxidation of transition metals and lithium/oxygen loss that concomitantly occur during heat treatment. Through synthetic control of the kinetic reaction pathway, a layered NMC71515 with low cationic disordering and a high reversible capacity is prepared in air. The findings may help to pave the way for designing high-Ni layered oxide cathodes for LIBs.

  17. Phase-pure β-NiMoO4 yolk-shell spheres for high-performance anode materials in lithium-ion batteries

    International Nuclear Information System (INIS)

    Ahn, Jee Hyun; Park, Gi Dae; Kang, Yun Chan; Lee, Jong-Heun

    2015-01-01

    Phase-pure β-NiMoO 4 yolk-shell spheres for lithium-ion battery anodes were prepared for the first time by one-pot spray pyrolysis, and their electrochemical properties were investigated. The yolk-shell-structured β-NiMoO 4 powders exhibited high initial discharge/charge capacities (1634/1253 mA h g −1 ) at a current density of 1000 mA g −1 . After 200 cycles, these powders exhibited a high discharge capacity of 1292 mA h g −1 , whereas the initial discharge capacity (1341 mA h g −1 ) of the filled structured NiMoO 4 powders was dramatically decreased to 479 mA h g −1 . The significant enhancement of the cycling performance of the β-NiMoO 4 powders with ultrafine crystallite size was attributed to the structural stability of the yolk-shell structure

  18. Improving the Electromagnetic Wave Absorption Properties of the Layered MoS2 by Cladding with Ni Nanoparticles

    Science.gov (United States)

    Zhang, Zilong; Wang, Zilin; Heng, Liuyang; Wang, Shuai; Chen, Xiqiao; Fu, Xiquan; Zou, Yanhong; Tang, Zhixiang

    2018-05-01

    MoS2 is a promising material with microwave absorption performance due to its high dielectric properties and low density. However, pure MoS2 is non-magnetic and has a bad impedance matching characteristic. In this study we prepared the Ni/MoS2 nanocomposites by cladding the MoS2 micrometer slices with magnetic Ni nanoparticles. Our results show that the microwave absorption properties of Ni/MoS2 nanocomposites have been improved obviously compared with the pure MoS2. Because of the introduction of Ni particles, the permeability of the nanocomposites has been turned from one to a complex, indicating a newly added magnetic loss. Meanwhile, the big gap between the permittivity and permeability of the Ni/MoS2 nanocomposites has been properly narrowed, which suggests an improved impedance matching. Moreover, the dielectric Cole-Cole semicircle shows that there are more Debye relaxation processes for the Ni/MoS2 nanocomposites, which further enhances the dielectric loss. Due to its improved electromagnetic properties, the minimum reflection loss (RL) value of the Ni/MoS2 nanocomposites with 60 wt % loading reaches -55 dB and the absorption bandwidth (<-10 dB) is up to 4.0 GHz (10.8-14.8 GHz) with a matching thickness of 1.5 mm. The results provide an excellent candidate for microwave absorbing materials with a broad effective absorption bandwidth at thin thicknesses.

  19. Effect of aging treatment on the in vitro nickel release from porous oxide layers on NiTi

    Energy Technology Data Exchange (ETDEWEB)

    Huan, Z.; Fratila-Apachitei, L.E., E-mail: e.l.fratila-apachitei@tudelft.nl; Apachitei, I.; Duszczyk, J.

    2013-06-01

    Despite the ability of creating porous oxide layers on nickel–titanium alloy (NiTi) surface for biofunctionalization, the use of plasma electrolytic oxidation (PEO) has raised concerns over the possible increased levels of Ni release. Therefore, the primary aim of this study was to investigate the effect of aging in boiling water on Ni release from porous NiTi surfaces that have been formed by the PEO process. Based on different oxidation conditions, e.g. electrolyte composition and electrical parameters, three kinds of oxide layers with various characteristics were prepared on NiTi substrate. The process was followed by aging in boiling water for different durations. The Ni release was assessed by immersion tests in phosphate buffer saline and the Ni concentration was measured using the flame atomic absorption spectrometry. The results showed that aging in boiling water can significantly reduce the Ni release from oxidized porous samples, given that the duration of the treatment is finely adjusted according to the parameters of the as-formed oxide layer. Surface examination of the samples before and after aging in boiling water suggested that such a treatment is non-destructive while improving the corrosion resistance of oxidized samples, as evidenced by potentiodynamic polarization tests. The results of this study indicate that water boiling may be a suitable post-treatment required to minimize Ni release from porous oxides produced on NiTi by PEO for biomedical applications.

  20. Mechanical matching and microstructural evolution at the coating/substrate interfaces of cold-sprayed Ni, Al coatings

    International Nuclear Information System (INIS)

    Lee, H.; Lee, S.; Shin, H.; Ko, K.

    2009-01-01

    The effect of mechanical hard/soft matching of raw powder and substrate in the cold gas dynamic spraying process (CDSP) on the formation of intermetallic compounds was examined. Instead of pre-alloyed materials, pure Al and Ni were selected as a soft and a hard material, respectively, and post-annealing was used for compound formation. Most of the aluminide layers were observed in the coated layer, but not in the substrate, along with the entire original interface for both Al coating on a Ni substrate and vice versa. Thickening of the compound layer depended mainly on the creation of defects during spraying and intrinsic diffusivity of atoms moving toward the coating side. When Ni was coated, the compound layer was made thicker by fast diffusion of Al, while the thickness was limited in soft Al coating on hard Ni substrate. However, the composition of the compound can be affected by relative transfer of diffusing atoms toward both the coating and the substrate. So, for Ni coating on an Al substrate, most of the intermetallic compound formed was Ni-rich and conversion of the Al-rich compound was observed after post-annealing above 500 deg. C.

  1. Thermal stability and electrical characteristics of NiSi films with electroplated Ni(W) alloy

    International Nuclear Information System (INIS)

    Xin Yuhang; Hu Anmin; Li Ming; Mao Dali

    2011-01-01

    In this study, an electroplating method to deposited Ni, crystalline NiW(c-NiW), amorphous NiW (a-NiW) films on P-type Si(1 0 0) were used to form Ni-silicide (NiSi) films. After annealed at various temperatures, sheet resistance of Ni/Cu, c-NiW/Cu and a-NiW/Cu was measured to observe the performance of those diffusion barrier layers. With W added in the barrier layer, the barrier performance was improved. The results of XRD and resistance measurement of the stacked Si/Ni(W)/Cu films reveal that Cu atom could diffuse through Ni barrier layer at 450 deg. C, could diffuse through c-NiW at 550 deg. C, but could hardly diffuse through a-NiW barrier layer. c-NiW layer has a better barrier performance than Ni layer, meanwhile the resistance is lower than a-NiW layer.

  2. Effect of the post-annealing temperature on the thermal-decomposed NiOx hole contact layer for perovskite solar cells

    Directory of Open Access Journals (Sweden)

    Yuxiao Guo

    2018-02-01

    Full Text Available A hysteresis-less inverted perovskite solar cell (PSC with power conversion efficiency (PCE of 13.57% was successfully achieved based on the thermal-decomposed NiOx hole contact layer, possessing better electron blocking and hole extraction properties for its suitable work function and high-conduction band edge position. Herein, the transparent and high-crystalline NiOx film is prepared by thermal-decomposing of the solution-derived Ni(OH2 film in our study, which is then employed as hole transport layer (HTL of the organic–inorganic hybrid PSCs. Reasonably, the post-annealing treatment, especially for the annealing temperature, could greatly affect the Ni(OH2 decomposition process and the quality of decomposed NiOx nanoparticles. The vital NiOx HTLs with discrepant morphology, crystallinity and transmission certainly lead to a wide range of device performance. As a result, an annealing process of 400∘C/2h significantly promotes the photovoltaic properties of the NiOx layer and the further device performance.

  3. Corrosion Resistance Of Electroless Ni-P/Cu/Ni-P Multilayer Coatings

    Directory of Open Access Journals (Sweden)

    Zhao G.L.

    2015-06-01

    Full Text Available Ni-P/Cu/Ni-P multilayer coatings were prepared by deposition of Cu layer between two Ni–P layers. The Cu layer was deposited by metal displacement reaction between Cu2+ and Fe atoms. Corrosion behavior of single-layer Ni-P coatings, double-layer Ni-P/Cu coatings, and three-layer Ni-P/Cu/Ni-P coatings were investigated by electrochemical tests in 3.5% NaCl solution. The three-layer coatings exhibited more positive Ecorr and decreased Icorr compared with conventional single-layer Ni-P coatings, which indicated an improved corrosion resistance. The polarization curves of the three-layer coatings were characterized by two passive regions. The improved corrosion resistance was not only attributed to the function of the blocked pores of Cu. The Cu interlayer also acted as a sacrificial layer instead of a barrier in the coatings, which altered the corrosion mechanism and further improved the corrosion resistance of the coatings.

  4. The electric double layer at a metal electrode in pure water

    Science.gov (United States)

    Brüesch, Peter; Christen, Thomas

    2004-03-01

    Pure water is a weak electrolyte that dissociates into hydronium ions and hydroxide ions. In contact with a charged electrode a double layer forms for which neither experimental nor theoretical studies exist, in contrast to electrolytes containing extrinsic ions like acids, bases, and solute salts. Starting from a self-consistent solution of the one-dimensional modified Poisson-Boltzmann equation, which takes into account activity coefficients of point-like ions, we explore the properties of the electric double layer by successive incorporation of various correction terms like finite ion size, polarization, image charge, and field dissociation. We also discuss the effect of the usual approximation of an average potential as required for the one-dimensional Poisson-Boltzmann equation, and conclude that the one-dimensional approximation underestimates the ion density. We calculate the electric potential, the ion distributions, the pH-values, the ion-size corrected activity coefficients, and the dissociation constants close to the electric double layer and compare the results for the various model corrections.

  5. Enhancement of the coercivity in Co-Ni layered double hydroxides by increasing basal spacing.

    Science.gov (United States)

    Zhang, Cuijuan; Tsuboi, Tomoya; Namba, Hiroaki; Einaga, Yasuaki; Yamamoto, Takashi

    2016-09-14

    The magnetic properties of layered double hydroxides (LDH) containing transition metal ions can still develop, compared with layered metal hydroxide salts which exhibit structure-dependent magnetism. In this article, we report the preparation of a hybrid magnet composed of Co-Ni LDH and n-alkylsulfonate anions (Co-Ni-CnSO3 LDH). As Co-Ni LDH is anion-exchangeable, we can systematically control the interlayer spacing by intercalating n-alkylsulfonates with different carbon numbers. The magnetic properties were examined with temperature- and field-dependent magnetization measurements. As a result, we have revealed that the coercive field depends on the basal spacing. It is suggested that increasing the basal spacing varies the competition between the in-plane superexchange interactions and long-range out-of-plane dipolar interactions. Moreover, a jump in the coercive field at around 20 Å of the basal spacing is assumed to be the modification of the magnetic ordering in Co-Ni-CnSO3 LDH.

  6. Effects of the thickness of NiO hole transport layer on the performance of all-inorganic quantum dot light emitting diode

    International Nuclear Information System (INIS)

    Zhang, Xiao Li; Dai, Hai Tao; Zhao, Jun Liang; Li, Chen; Wang, Shu Guo; Sun, Xiao Wei

    2014-01-01

    All-inorganic quantum dot light emitting diodes (QLEDs) have recently gained great attention owing to their high stability under oxygenic, humid environment and higher operating currents. In this work, we fabricated all-inorganic CdSe/ZnS core-shell QLEDs composed of ITO/NiO/QDs/ZnO/Al, in which NiO and ZnO thin film deposited via all-solution method were employed as hole and electron transport layer, respectively. To achieve high light emitting efficiency, the balance transport between electrons and holes play a key role. In this work, the effects of the thickness of NiO film on the performance of QLEDs were explored experimentally in details. NiO layers with various thicknesses were prepared with different rotation speeds. Experimental results showed that thinner NiO layer deposited at higher rotation speed had higher transmittance and larger band gap. Four typical NiO thickness based QLEDs were fabricated to optimize the hole transport layer. Thinner NiO layer based device performs bright emission with high current injection, which is ascribed to the reduced barrier height between hole transport layer and quantum dot. - Highlights: • All-inorganic quantum dot light emitting diodes (QLEDs) were fabricated. • Thinner NiO film can effectively enhance on–off properties of devices. • Improved performance of QLEDs is mainly attributed to energy barrier reduction

  7. Difference between Cr and Ni K-edge XANES spectra of rust layers formed on Fe-based binary alloys exposed to Cl-rich environment

    International Nuclear Information System (INIS)

    Konishi, Hiroyuki; Mizuki, Jun'ichiro; Yamashita, Masato; Uchida, Hitoshi

    2005-01-01

    The rust layer formed on weathering steel possesses a strong protective ability against corrosives in an atmospheres. This ability is related to the structure of the rust layer. The difference in the protective ability of a rust layer. The difference in the protective ability of a rust layer in a Cl-rich environment between conventional weathering steel containing Cr and advanced weathering steel containing Ni is believed to be caused by the differences in local structural and chemical properties between alloying elements. Cr and Ni, in the rust layer. In order to examine the effect of these alloying elements on the structure of the rust layer formed on steel in a Cl-rich environment, we have performed Cr and Ni K-edge X-ray absorption near-edge structure (XANES) measurements for the rust layer of Fe-Cr and Fe-Ni binary alloys exposed to a Cl-rich atmosphere using synchrotron radiation. The results of the Cr K-edge XANES measurements for the rust layer of Fe-Cr binary alloys show that the atomic geometry around Cr depends on the concentration of Cr. Therefore, it is expected that the local structure around Cr in the rust layer is unstable. On the other hand, from the results of the Ni K-edge XANES measurements for the rust layer of Fe-Ni binary alloys. Ni is considered to be positioned at a specific site in the crystal structure of a constituent of the rust layer, such as akaganeite or magnetite. As a consequence, Ni negligibly interacts with Cl - ions in the rust layer. (author)

  8. Three-dimensional electrode of Ni/Co layered double hydroxides@NiCo2S4@graphene@Ni foam for supercapacitors with outstanding electrochemical performance

    International Nuclear Information System (INIS)

    Tao, Yan; Ruiyi, Li; Lin, Zhou; Chenyang, Ma; Zaijun, Li

    2015-01-01

    We reported a new strategy for fabricating three-dimensiona electrode of Ni/Co layered double hydroxide@NiCo 2 S 4 @graphene@Ni foam for supercapacitors. The resulting 3D electrode offers a jungle-like architecture. The unique structure creates ultra fast electron transfer and electrolyte transport as well as the maximum utilization rate of the space and the surface. The electrode exhibits a prominent advantage of high specific capacitance, high-current capacitive behaviour and cycle stability. - Highlights: • The study developed a new strategy for fabricating 3D electrode of Ni/Co-LDH@NiCo 2 S 4 @G. • The as-prepared 3D electrode offers a jungle-like architecture. • The unique structure creates an efficient conduction network and high mass loading. • The electrode achieves significantly synergetic effect among different materials. • The electrode exhibits an excellent electrochemical performance for supercapacitors. - ABSTRACT: Great challenge for the fabrication of free-standing three-dimensional electrode still remains to simultaneously achieve high specific capacitance, rate performance and cycle stability. The paper reprted a new three-dimensional (3D) electrode of Ni/Co layered double hydroxide@NiCo 2 S 4 @graphene@Ni foam (Ni/Co-LDH@NiCo 2 S 4 @G) for supercapacitors. The as-prepared 3D electrode offers an unique architecture, which create an efficient conduction network and maximum utilization of space and interface. The graphene acts as well-knit and conductive skin coated on the skeleton of Ni foam for growing NiCo 2 S 4 . The conductive NiCo 2 S 4 array serves as bridge between Ni/Co-LDH and graphene, leading to ultrafast electron transfer and electrolyte transport. A slew of splits and holes existing in the NiCo 2 S 4 array play one role as the ion-reservoir to contain host of electrolyte ions. To evaluate the feasibility of 3D electrode’s application in supercapacitors, the electrochemical performance was investigated by using the three

  9. Observation of layered antiferromagnetism in self-assembled parallel NiSi nanowire arrays on Si(110) by spin-polarized scanning tunneling spectromicroscopy

    Science.gov (United States)

    Hong, Ie-Hong; Hsu, Hsin-Zan

    2018-03-01

    The layered antiferromagnetism of parallel nanowire (NW) arrays self-assembled on Si(110) have been observed at room temperature by direct imaging of both the topographies and magnetic domains using spin-polarized scanning tunneling microscopy/spectroscopy (SP-STM/STS). The topographic STM images reveal that the self-assembled unidirectional and parallel NiSi NWs grow into the Si(110) substrate along the [\\bar{1}10] direction (i.e. the endotaxial growth) and exhibit multiple-layer growth. The spatially-resolved SP-STS maps show that these parallel NiSi NWs of different heights produce two opposite magnetic domains, depending on the heights of either even or odd layers in the layer stack of the NiSi NWs. This layer-wise antiferromagnetic structure can be attributed to an antiferromagnetic interlayer exchange coupling between the adjacent layers in the multiple-layer NiSi NW with a B2 (CsCl-type) crystal structure. Such an endotaxial heterostructure of parallel magnetic NiSi NW arrays with a layered antiferromagnetic ordering in Si(110) provides a new and important perspective for the development of novel Si-based spintronic nanodevices.

  10. Layered Ni(OH)2-Co(OH)2 films prepared by electrodeposition as charge storage electrodes for hybrid supercapacitors.

    Science.gov (United States)

    Nguyen, Tuyen; Boudard, Michel; Carmezim, M João; Montemor, M Fátima

    2017-01-04

    Consecutive layers of Ni(OH) 2 and Co(OH) 2 were electrodeposited on stainless steel current collectors for preparing charge storage electrodes of high specific capacity with potential application in hybrid supercapacitors. Different electrodes were prepared consisting on films of Ni(OH) 2 , Co(OH) 2 , Ni 1/2 Co 1/2 (OH) 2 and layered films of Ni(OH) 2 on Co(OH) 2 and Co(OH) 2 on Ni(OH) 2 to highlight the advantages of the new architecture. The microscopy studies revealed the formation of nanosheets in the Co(OH) 2 films and of particles agglomerates in the Ni(OH) 2 films. Important morphological changes were observed in the double hydroxides films and layered films. Film growth by electrodeposition was governed by instantaneous nucleation mechanism. The new architecture composed of Ni(OH) 2 on Co(OH) 2 displayed a redox response characterized by the presence of two peaks in the cyclic voltammograms, arising from redox reactions of the metallic species present in the layered film. These electrodes revealed a specific capacity of 762 C g -1 at the specific current of 1 A g -1 . The hybrid cell using Ni(OH) 2 on Co(OH) 2 as positive electrode and carbon nanofoam paper as negative electrode display specific energies of 101.3 W h g -1 and 37.8 W h g -1 at specific powers of 0.2 W g -1 and 2.45 W g -1 , respectively.

  11. Characterization of corrosion resistant on NiCoCr coating layer exposed to 5%NaCl

    Science.gov (United States)

    Sugiarti, E.; Sundawa, R.; Desiati, R. D.; Zaini, K. A.

    2018-03-01

    Highly corrosion resistant of carbon steel coated NiCoCr was applied in corrosive of marine environtment. Carbon steel coated NiCoCr was prepared by a two step technique of NiCo electro-deposition and Cr pack cementation. The samples were exposed to 5 wt.% NaCl for 48 and 168 hours. The microstructure and corrosion product were characterized by scanning electron microscopy (SEM), X-ray diffraction (XRD), and transmission electron microscopy (TEM). The corrosion resistance of carbon steel coated NiCoCr was found to be better than that of carbon steel substrate without coating. The results showed the microstructure of 48 h corroded sample has duplex layer composed of inner α-(Ni,Co), α-Cr and outer Cr2O3, while a quite thin and continues protective oxide of Cr2O3 was observed in outer layer of 168 h corroded sample. The formation of oxide scale rich in Cr2O3 has contributed for the better corrosion resistance of carbon steel coated NiCoCr, whereas the formation of non protective oxide of iron might caused low corrosion resistance of carbon steel substrate.

  12. Structure and properties of nitrided surface layer produced on NiTi shape memory alloy by low temperature plasma nitriding

    International Nuclear Information System (INIS)

    Czarnowska, Elżbieta; Borowski, Tomasz; Sowińska, Agnieszka; Lelątko, Józef; Oleksiak, Justyna; Kamiński, Janusz; Tarnowski, Michał; Wierzchoń, Tadeusz

    2015-01-01

    Highlights: • Low temperature plasma nitriding process of NiTi shape memory alloy is presented. • The possibility of treatment details of sophisticated shape. • TiN surface layer has diffusive character. • TiN surface layer increases corrosion resistance of NiTi alloy. • Produced TiN layer modify the biological properties of NiTi alloy. - Abstract: NiTi shape memory alloys are used for bone and cardiological implants. However, on account of the metallosis effect, i.e. the release of the alloy elements into surrounding tissues, they are subjected to various surface treatment processes in order to improve their corrosion resistance and biocompatibility without influencing the required shape memory properties. In this paper, the microstructure, topography and morphology of TiN surface layer on NiTi alloy, and corrosion resistance, both before and after nitriding in low-temperature plasma at 290 °C, are presented. Examinations with the use of the potentiodynamic and electrochemical impedance spectroscopy methods were carried out and show an increase of corrosion resistance in Ringer's solution after glow-discharge nitriding. This surface titanium nitride layer also improved the adhesion of platelets and the proliferation of osteoblasts, which was investigated in in vitro experiments with human cells. Experimental data revealed that nitriding NiTi shape memory alloy under low-temperature plasma improves its properties for bone implant applications

  13. Structure and properties of nitrided surface layer produced on NiTi shape memory alloy by low temperature plasma nitriding

    Energy Technology Data Exchange (ETDEWEB)

    Czarnowska, Elżbieta [Children' s Memorial Health Institute, Pathology Department, Al. Dzieci Polskich 20, 04-730 Warsaw (Poland); Borowski, Tomasz [Warsaw University of Technology, Faculty of Materials Science and Engineering, Wołoska 141, 02-507 Warsaw (Poland); Sowińska, Agnieszka [Children' s Memorial Health Institute, Pathology Department, Al. Dzieci Polskich 20, 04-730 Warsaw (Poland); Lelątko, Józef [Silesia University, Faculty of Computer Science and Materials Science, 75 Pułku Piechoty 1A, 41-500 Chorzów (Poland); Oleksiak, Justyna; Kamiński, Janusz; Tarnowski, Michał [Warsaw University of Technology, Faculty of Materials Science and Engineering, Wołoska 141, 02-507 Warsaw (Poland); Wierzchoń, Tadeusz, E-mail: twierz@inmat.pw.edu.pl [Warsaw University of Technology, Faculty of Materials Science and Engineering, Wołoska 141, 02-507 Warsaw (Poland)

    2015-04-15

    Highlights: • Low temperature plasma nitriding process of NiTi shape memory alloy is presented. • The possibility of treatment details of sophisticated shape. • TiN surface layer has diffusive character. • TiN surface layer increases corrosion resistance of NiTi alloy. • Produced TiN layer modify the biological properties of NiTi alloy. - Abstract: NiTi shape memory alloys are used for bone and cardiological implants. However, on account of the metallosis effect, i.e. the release of the alloy elements into surrounding tissues, they are subjected to various surface treatment processes in order to improve their corrosion resistance and biocompatibility without influencing the required shape memory properties. In this paper, the microstructure, topography and morphology of TiN surface layer on NiTi alloy, and corrosion resistance, both before and after nitriding in low-temperature plasma at 290 °C, are presented. Examinations with the use of the potentiodynamic and electrochemical impedance spectroscopy methods were carried out and show an increase of corrosion resistance in Ringer's solution after glow-discharge nitriding. This surface titanium nitride layer also improved the adhesion of platelets and the proliferation of osteoblasts, which was investigated in in vitro experiments with human cells. Experimental data revealed that nitriding NiTi shape memory alloy under low-temperature plasma improves its properties for bone implant applications.

  14. Few-layered Ni(OH)2 nanosheets for high-performance supercapacitors

    Science.gov (United States)

    Sun, Wenping; Rui, Xianhong; Ulaganathan, Mani; Madhavi, Srinivasan; Yan, Qingyu

    2015-11-01

    Few-layered Ni(OH)2 nanosheets (4-5 nm in thickness) are synthesized towards high-performance supercapacitors. The ultrathin Ni(OH)2 nanosheets show high specific capacitance and good rate capability in both three-electrode and asymmetric devices. In the three-electrode device, the Ni(OH)2 nanosheets deliver a high capacitance of 2064 F g-1 at 2 A g-1, and the capacitance still has a retention of 1837 F g-1 at a high current density of 20 A g-1. Such excellent performance is by far one of the best for Ni(OH)2 electrodes. In the two-electrode asymmetric device, the specific capacitance is 248 F g-1 at 1 A g-1, and reaches 113 F g-1 at 20 A g-1. The capacitance of the asymmetric device maintains to be 166 F g-1 during the 4000th cycle at 2 A g-1, suggesting good cycling stability of the device. Besides, the asymmetric device exhibits gravimetric energy density of 22 Wh kg-1 at a power density of 0.8 kW kg-1. The present results demonstrate that the ultrathin Ni(OH)2 nanosheets are highly attractive electrode materials for achieving fast charging/discharging and high-capacity supercapacitors.

  15. Investigation of the Dissolution-Reformation Cycle of the Passive Oxide Layer on NiTi Orthodontic Archwires

    Science.gov (United States)

    Uzer, B.; Birer, O.; Canadinc, D.

    2017-09-01

    Dissolution-reformation cycle of the passive oxide layer on the nickel-titanium (NiTi) orthodontic archwires was investigated, which has recently been recognized as one of the key parameters dictating the biocompatibility of archwires. Specifically, commercially available NiTi orthodontic archwires were immersed in artificial saliva solutions of different pH values (2.3, 3.3, and 4.3) for four different immersion periods: 1, 7, 14, and 30 days. Characterization of the virgin and tested samples revealed that the titanium oxide layer on the NiTi archwire surfaces exhibit a dissolution-reformation cycle within the first 14 days of the immersion period: the largest amount of Ni ion release occurred within the first week of immersion, while it significantly decreased during the reformation period from day 7 to day 14. Furthermore, the oxide layer reformation was catalyzed on the grooves within the peaks and valleys due to relatively larger surface energy of these regions, which eventually decreased the surface roughness significantly within the reformation period. Overall, the current results clearly demonstrate that the analyses of dissolution-reformation cycle of the oxide layer in orthodontic archwires, surface roughness, and ion release behavior constitute utmost importance in order to ensure both the highest degree of biocompatibility and an efficient medical treatment.

  16. Martensitic transformation and shape memory effect in NiTi alloy covered by chitosan/silver layer

    Directory of Open Access Journals (Sweden)

    Goryczka Tomasz

    2015-01-01

    Full Text Available The NiTi shape memory alloy was covered with chitosan/silver layer. Coatings were deposited at room temperature using combination of processing parameters such as deposition voltage and amount of silver in colloidal suspension. Structure of layers was studied by means of X-ray diffraction. Quality of the coatings was evaluated basing on observations done in scanning electron microscopy. Transformation behaviour of coated samples was studied with use of differential scanning calorimeter. The covered sample revealed presence of the reversible martensitic transformation and ability to deformation (in bending mode up to 8%. Forward martensitic transformation, in as-received NiTi alloy and in alloy after layer deposition occurred in two steps B2-R-B19’. After deformation quality of the chitosan/silver layer remained unchanged.

  17. Ni And Co Segregations On Selective Surface Facets And Rational Design Of Layered Lithium Transition-metal Oxide Cathodes

    Energy Technology Data Exchange (ETDEWEB)

    Yan, Pengfei; Zheng, Jianming; Zheng, Jiaxin; Wang, Zhiguo; Teng, Gaofeng; Kuppan, Saravanan; Xiao, Jie; Chen, Guoying; Zhang, Jiguang; Wang, Chong M.; Pan, Feng

    2016-05-05

    The chemical processes occurring on the surface of cathode materials during battery cycling play a crucial role in determining battery’s performance. However, our understanding on such surface chemistry is far from clear due to the complexity of redox chemistry during battery charge/discharge. In this work, through intensive aberration corrected STEM investigation on eight layered oxide cathode materials, we report two important findings on the pristine oxides. First, Ni and Co show strong plane selectivity when building up their respective surface segregation layers (SSL). Specifically, Ni-SSL is exclusively developed on (200)m facet in Li-Mn-rich oxides (monoclinic C2/m symmetry) and (012)h facet in Mn-Ni equally rich oxides (hexagonal R-3m symmetry), while Co-SSL has a strong preference to (20-2)m plane with minimal Co-SSL also developed on some other planes in LMR cathodes. Structurally, Ni-SSLs tend to form spinel-like lattice while Co-SSLs are in a rock-salt-like structure. Secondly, by increasing Ni concentration in these layered oxides, Ni and Co SSLs can be suppressed and even eliminated. Our findings indicate that Ni and Co SSLs are tunable through controlling particle morphology and oxide composition, which opens up a new way for future rational design and synthesis of cathode materials.

  18. Ni Nanobuffer Layer Provides Light-Weight CNT/Cu Fibers with Superior Robustness, Conductivity, and Ampacity.

    Science.gov (United States)

    Zou, Jingyun; Liu, Dandan; Zhao, Jingna; Hou, Ligan; Liu, Tong; Zhang, Xiaohua; Zhao, Yonghao; Zhu, Yuntian T; Li, Qingwen

    2018-03-07

    Carbon nanotube (CNT) fiber has not shown its advantage as next-generation light-weight conductor due to the large contact resistance between CNTs, as reflected by its low conductivity and ampacity. Coating CNT fiber with a metal layer like Cu has become an effective solution to this problem. However, the weak CNT-Cu interfacial bonding significantly limits the mechanical and electrical performances. Here, we report that a strong CNT-Cu interface can be formed by introducing a Ni nanobuffer layer before depositing the Cu layer. The Ni nanobuffer layer remarkably promotes the load and heat transfer efficiencies between the CNT fiber and Cu layer and improves the quality of the deposited Cu layer. As a result, the new composite fiber with a 2 μm thick Cu layer can exhibit a superhigh effective strength >800 MPa, electrical conductivity >2 × 10 7 S/m, and ampacity >1 × 10 5 A/cm 2 . The composite fiber can also sustain 10 000 times of bending and continuously work for 100 h at 90% ampacity.

  19. Interfacial exchange coupling and magnetization reversal in perpendicular [Co/Ni]N/TbCo composite structures.

    Science.gov (United States)

    Tang, M H; Zhang, Zongzhi; Tian, S Y; Wang, J; Ma, B; Jin, Q Y

    2015-06-15

    Interfacial exchange coupling and magnetization reversal characteristics in the perpendicular heterostructures consisting of an amorphous ferrimagnetic (FI) TbxCo(100-x) alloy layer exchange-coupled with a ferromagnetic (FM) [Co/Ni]N multilayer have been investigated. As compared with pure TbxCo(100-x) alloy, the magnetization compensation composition of the heterostructures shift to a higher Tb content, implying Co/Ni also serves to compensate the Tb moment in TbCo layer. The net magnetization switching field Hc⊥ and interlayer interfacial coupling field Hex, are not only sensitive to the magnetization and thickness of the switched TbxCo(100-x) or [Co/Ni]N layer, but also to the perpendicular magnetic anisotropy strength of the pinning layer. By tuning the layer structure we achieve simultaneously both large Hc⊥ = 1.31 T and Hex = 2.19 T. These results, in addition to the fundamental interest, are important to understanding of the interfacial coupling interaction in the FM/FI heterostructures, which could offer the guiding of potential applications in heat-assisted magnetic recording or all-optical switching recording technique.

  20. Copper and CuNi alloys substrates for HTS coated conductor applications protected from oxidation

    Energy Technology Data Exchange (ETDEWEB)

    Segarra, M; Diaz, J; Xuriguera, H; Chimenos, J M; Espiell, F [Dept. of Chemical Engineering and Metallurgy, Univ. of Barcelona, Barcelona (Spain); Miralles, L [Lab. d' Investigacio en Formacions Geologiques. Dept. of Petrology, Geochemistry and Geological Prospecting, Univ. of Barcelona, Barcelona (Spain); Pinol, S [Inst. de Ciencia de Materials de Barcelona, Bellaterra (Spain)

    2003-07-01

    Copper is an interesting substrate for HTS coated conductors for its low cost compared to other metallic substrates, and for its low resistivity. Nevertheless, mechanical properties and resistance to oxidation should be improved in order to use it as substrate for YBCO deposition by non-vacuum techniques. Therefore, different cube textured CuNi tapes were prepared by RABIT as possible substrates for deposition of high critical current density YBCO films. Under the optimised conditions of deformation and annealing, all the studied CuNi alloys (2%, 5%, and 10% Ni) presented (100) left angle 001 right angle cube texture which is compatible for YBCO deposition. Textured CuNi alloys present higher tensile strength than pure copper. Oxidation resistance of CuNi tapes under different oxygen atmospheres was also studied by thermogravimetric analysis and compared to pure copper tapes. Although the presence of nickel improves mechanical properties of annealed copper, it does not improve its oxidation resistance. However, when a chromium buffer layer is electrodeposited on the tape, oxygen diffusion is slowed down. Chromium is, therefore, useful for protecting copper and CuNi alloys from oxidation although its recrystallisation texture, (110), is not suitable for coated conductors. (orig.)

  1. Improved conductivity of infinite-layer LaNiO2 thin films by metal organic decomposition

    International Nuclear Information System (INIS)

    Ikeda, Ai; Manabe, Takaaki; Naito, Michio

    2013-01-01

    Highlights: •LaNiO 2 films were synthesized by metal organic decomposition and topotactic reduction. •Room-temperature resistivity as low as 0.6 mΩ cm was achieved for infinite-layer LaNiO 2 . •Lattice matched substrates are important in obtaining high conductivity. -- Abstract: Infinite-layer LaNiO 2 thin films were synthesized by metal organic decomposition and subsequent topotactic reduction in hydrogen, and their transport properties were investigated. LaNiO 2 is isostructural to SrCuO 2 , the parent compound of high-T c Sr 0.9 La 0.1 CuO 2 with T c = 44 K, and has 3d 9 configuration, which is very rare in oxides but common to high-T c copper oxides. The bulk synthesis of LaNiO 2 is not easy, but we demonstrate in this article that the thin-film synthesis of LaNiO 2 is rather easy, thanks to a large-surface-to-volume ratio, which makes oxygen diffusion prompt. Our refined synthesis conditions produced highly conducting films of LaNiO 2 . The resistivity of the best film is as low as 640 μΩ cm at 295 K and decreases with temperature down to 230 K but it shows a gradual upturn at lower temperatures

  2. Nonmonotonic behaviour of superconducting critical temperature of Nb/CuNi bilayers with a nanometer range of layer thickness

    International Nuclear Information System (INIS)

    Morari, R.; Antropov, E.; Socrovisciuc, A.; Prepelitsa, A.; Zdravkov, V.I.; Tagirov, L.R.; Kupriyanov, M.Yu.; Sidorenko, A.S.

    2009-01-01

    Present work reports the result of the proximity effect investigation for superconducting Nb/CuNi-bilayers with the thickness of the ferromagnetic layer (Cu x Ni 1-x ) being in the sub-nanometer range. It was found a non-monotonic behavior of the critical temperature T c , i.e. its growth with the increasing of the ferromagnetic layer thickness dF, for the series of the samples with constant thickness of Nb layer, (d Nb = const). (authors)

  3. High resistance to sulfur poisoning of Ni with copper skin under electric field

    Energy Technology Data Exchange (ETDEWEB)

    Xu, Xiaopei; Zhang, Yanxing [College of Physics and Materials Science, Henan Normal University, Xinxiang, Henan 453007 (China); Yang, Zongxian, E-mail: yzx@henannu.edu.cn [College of Physics and Materials Science, Henan Normal University, Xinxiang, Henan 453007 (China); Collaborative Innovation Center of Nano Functional Materials and Applications, Kaifeng, Henan Province (China)

    2017-02-12

    The effects of sulfur poisoning on the (1 0 0), (1 1 0) and (1 1 1) surfaces of pure Ni and Cu/Ni alloy are studied in consideration of the effect of electric field. The effects of Cu dopants on the S poisoning characteristics are analyzed by the means of the density functional theory results in combination with thermodynamics data using the ab initio atomistic thermodynamic method. When the Cu concentration increases to 50% on the surface layer of the Cu/Ni alloy, the (1 1 0) surface becomes the most vulnerable to the sulfur poisoning. Ni with a copper skin can mostly decrease the sulfur poisoning effect. Especially under the electric field of 1.0 V/Å, the sulfur adsorption and phase transition temperature can be further reduced. We therefore propose that Ni surfaces with copper skin can be very effective to improve the resistance to sulfur poisoning of the Ni anode under high electric field. - Highlights: • The electric field and Cu dopant effects on S poisoning feature of Ni are analyzed. • The present of large electric field can enhance S tolerance. • Cu dopant concentration affect the surface electronic structure of Ni. • 100% Cu doping on surface Ni layer can mostly decrease the sulfur poison.

  4. Magnetic hybride layers. Magnetic properties of locally exchange-coupled NiFe/IrMn layers; Magnetische Hybridschichten. Magnetische Eigenschaften lokal austauschgekoppelter NiFe/IrMn-Schichten

    Energy Technology Data Exchange (ETDEWEB)

    Hamann, Christine

    2010-10-06

    By the lateral modification of the magnetic properties of exchange-coupled NiFe/IrMn layers soft-magnetic layers were produced, which show both new static and dynamic properties. As lateral structuration methods hereby the localoxidation as well as ion implantation were applied. By means of thes procedures it has been succeeded to mould specific magnetic domain configurations with strp structure into the layers. In dependence of the structure orientation as well as strip period the remagnetization behavior as well as the magnetic-resonance frequency and damping of the layers could directly be modified. The new dynamical properties are hereby discussed in the framework of the coupling via dynamical charges and the direct affection of the effective field of the artificially inserted domain state. The presented results prove by this the large potential of the lateral magneto-structuration for the tuning of specifical static as well as dynamic properties of magnetically thin layers.

  5. Investigation of oxidation resistance of Ni-Ti film used as oxygen diffusion barrier layer

    International Nuclear Information System (INIS)

    Liu, B.T.; Yan, X.B.; Zhang, X.; Zhou, Y.; Guo, Y.N.; Bian, F.; Zhang, X.Y.

    2009-01-01

    Ni-Ti films prepared at 10 W and 70 W by rf magnetron sputtering are investigated as the oxygen diffusion barrier layer, it is found that crystallinity of Ni-Ti film does not greatly depend on the deposition power. X-ray photoelectron spectroscopy indicates that Ni is still in the form of metallic state from the binding energies of both Ni 2p 3/2 and Ni 2p 1/2 spectra for the sample with 10 W prepared Ni-Ti, however, Ni is oxidized for 70 W prepared Ni-Ti film. Moreover, the (La 0.5 Sr 0.5 )CoO 3 /Pb(Zr 0.40 Ti 0.60 )O 3 /(La 0.5 Sr 0.5 )CoO 3 capacitor grown on high power prepared Ni-Ti film is leaky, however, the capacitor on low power prepared Ni-Ti film possesses very promising physical properties (i.e. remnant polarization of ∼27 μC/cm 2 at 5 V and maximum dielectric constant of 940). Leakage current density of the capacitor grown on low power prepared Ni-Ti film is further investigated, it meets ohmic behavior ( 1.0 V).

  6. Study of dipole interaction in micron-width NiFe/Cu/NiFe/NiO wire using exchange anisotropy

    International Nuclear Information System (INIS)

    Kimura, Takashi; Itagaki, Yoshio; Wakaya, Fujio; Gamo, Kenji

    2001-01-01

    The dipole interaction between a NiFe layer pinned by a NiO and a free NiFe layer in a micron-wide NiFe/Cu/NiFe/NiO wire was studied by changing the direction of the exchange bias from the NiO layer. The effect of the dipole interaction when the exchange bias was perpendicular to the wire axis was larger than that when the exchange bias was parallel to the wire axis, and was consistently explained by the stray field caused by the magnetic charges of the pinned layer. It was demonstrated that this method, using exchange anisotropy, is useful for investigating the dipole interaction between ferromagnetic materials separated by a nonmagnetic material in small-scale magnetic multilayers. [copyright] 2001 American Institute of Physics

  7. Biodegradable polymer for sealing porous PEO layer on pure magnesium: An in vitro degradation study

    Science.gov (United States)

    Alabbasi, Alyaa; Mehjabeen, Afrin; Kannan, M. Bobby; Ye, Qingsong; Blawert, Carsten

    2014-05-01

    An attempt was made to seal the porous silicate-based plasma electrolytic oxidation (PEO) layer on pure magnesium (Mg) with a biodegradable polymer, poly(L-lactide) (PLLA), to delay the localized degradation of magnesium-based implants in body fluid for better in-service mechanical integrity. Firstly, a silicate-based PEO coating on pure magnesium was performed using a pulsed constant current method. In order to seal the pores in the PEO layer, PLLA was coated using a two-step spin coating method. The performance of the PEO-PLLA Mg was evaluated using electrochemical impedance spectroscopy (EIS) and potentiodynamic polarization. The EIS results showed that the polarization resistance (Rp) of the PEO-PLLA Mg was close to two orders of magnitude higher than that of the PEO Mg. While the corrosion current density (icorr) of the pure Mg was reduced by 65% with the PEO coating, the PEO-PLLA coating reduced the icorr by almost 100%. As expected, the Rp of the PEO-PLLA Mg decreased with increase in exposure time. However, it was noted that the Rp of the PEO-PLLA Mg even after 100 h was six times higher than that of the PEO Mg after 48 h exposure, and did not show any visible localized attack.

  8. Anti-corrosive and anti-microbial properties of nanocrystalline Ni-Ag coatings

    Energy Technology Data Exchange (ETDEWEB)

    Raghupathy, Y.; Natarajan, K.A.; Srivastava, Chandan, E-mail: csrivastava@materials.iisc.ernet.in

    2016-04-15

    Graphical abstract: - Highlights: • Electrodeposition yielded phase-segregated, nanocrystalline Ni-Ag coatings. • Ni-Ag alloys exhibited smaller Ni crystals compared to pure Ni. • Ultra fine Ni grains of size 12–14 nm favoured Ni-Ag solid solution. • Nanocrystalline Ag resisted bio-fouling by Sulphate Reducing bacteria. • Ni-Ag outperformed pure Ni in corrosion and bio-corrosion tests. - Abstract: Anti-corrosive and anti-bacterial properties of electrodeposited nanocrystalline Ni-Ag coatings are illustrated. Pure Ni, Ni-7 at.% Ag, & Ni-14 at.% Ag coatings were electrodeposited on Cu substrate. Coating consisted of Ni-rich and Ag-rich solid solution phases. With increase in the Ag content, the corrosion resistance of the Ni-Ag coating initially increased and then decreased. The initial increase was due to the Ni-Ag solid solution. The subsequent decrease was due to the increased galvanic coupling between the Ag-rich and Ni-rich phases. For all Ag contents, the corrosion resistance of the Ni-Ag coating was higher than the pure Ni coating. Exposure to Sulphate Reducing Bacteria (SRB) revealed that the extent of bio-fouling decreased with increase in the Ag content. After 2 month exposure to SRB, the Ni-Ag coatings demonstrated less loss in corrosion resistance (58% for Ni-7 at.% Ag and 20% for Ni-14 at.% Ag) when compared pure Ni coating (115%).

  9. Influence of ni thickness on oscillation coupling in Cu/Ni multilayers

    Energy Technology Data Exchange (ETDEWEB)

    Gagorowska, B; Dus-Sitek, M [Institute of Physics, Czestochowa University of Technology, Al. Armii Krajowej 19, 42-200 Czestochowa (Poland)

    2007-08-15

    The results of investigation of magnetic properties of [Cu/Ni]x100 were presented. Samples were deposited by face-to-face sputtering method onto the silicon substrate, the thickness of Cu layer was constant (d{sub Cu} = 2 nm) and the thickness of Ni layer - variable (1 nm {<=} d{sub Ni} {<=} 6 nm). In Cu/Ni multilayers, for the thickness of Ni layer bigger than 2 nm antiferromagnetic coupling (A-F) were observed, for the thickness of Ni smaller than 2 nm A-F coupling is absent.

  10. Influence of ni thickness on oscillation coupling in Cu/Ni multilayers

    International Nuclear Information System (INIS)

    Gagorowska, B; Dus-Sitek, M

    2007-01-01

    The results of investigation of magnetic properties of [Cu/Ni]x100 were presented. Samples were deposited by face-to-face sputtering method onto the silicon substrate, the thickness of Cu layer was constant (d Cu = 2 nm) and the thickness of Ni layer - variable (1 nm ≤ d Ni ≤ 6 nm). In Cu/Ni multilayers, for the thickness of Ni layer bigger than 2 nm antiferromagnetic coupling (A-F) were observed, for the thickness of Ni smaller than 2 nm A-F coupling is absent

  11. Role of the antiferromagnetic pinning layer on spin wave properties in IrMn/NiFe based spin-valves

    Energy Technology Data Exchange (ETDEWEB)

    Gubbiotti, G., E-mail: gubbiotti@fisica.unipg.it; Tacchi, S. [Istituto Officina dei Materiali del CNR (IOM-CNR), Unità di Perugia, I-06123 Perugia (Italy); Del Bianco, L. [Department of Physics and Astronomy, University of Bologna, I-40127 Bologna (Italy); Department of Physics and Earth Sciences and CNISM, University of Ferrara, I-44122 Ferrara (Italy); Bonfiglioli, E.; Giovannini, L.; Spizzo, F.; Zivieri, R. [Department of Physics and Earth Sciences and CNISM, University of Ferrara, I-44122 Ferrara (Italy); Tamisari, M. [Department of Physics and Earth Sciences and CNISM, University of Ferrara, I-44122 Ferrara (Italy); Dipartimento di Fisica e Geologia, Università di Perugia, I-06123 Perugia (Italy)

    2015-05-07

    Brillouin light scattering (BLS) was exploited to study the spin wave properties of spin-valve (SV) type samples basically consisting of two 5 nm-thick NiFe layers (separated by a Cu spacer of 5 nm), differently biased through the interface exchange coupling with an antiferromagnetic IrMn layer. Three samples were investigated: a reference SV sample, without IrMn (reference); one sample with an IrMn underlayer (10 nm thick) coupled to the bottom NiFe film; one sample with IrMn underlayer and overlayer of different thickness (10 nm and 6 nm), coupled to the bottom and top NiFe film, respectively. The exchange coupling with the IrMn, causing the insurgence of the exchange bias effect, allowed the relative orientation of the NiFe magnetization vectors to be controlled by an external magnetic field, as assessed through hysteresis loop measurements by magneto-optic magnetometry. Thus, BLS spectra were acquired by sweeping the magnetic field so as to encompass both the parallel and antiparallel alignment of the NiFe layers. The BLS results, well reproduced by the presented theoretical model, clearly revealed the combined effects on the spin dynamic properties of the dipolar interaction between the two NiFe films and of the interface IrMn/NiFe exchange coupling.

  12. Non-contact evaluation of mechanical properties of electroplated wear resistant Ni-P layer from the velocity dispersion of laser SAW; Laser reiki Rayleigh ha no sokudo bunsan wo mochiita taimamo Ni-P mekkiso tokusei no hisesshoku hyoka

    Energy Technology Data Exchange (ETDEWEB)

    Morikawa, Y.; Cho, H.; Takemoto, M. [Aoyama Gakuin University, Tokyo (Japan). Faculty of Science and Engineering; Nakayama, T. [Kobe Steel Ltd., Kobe (Japan)

    1996-11-01

    We developed a new laser surface acoustic wave (SAW) system and applied this to estimate the mechanical properties of the wear-resistant Ni-P layer electroplated on a stainless steel. The velocity dispersions of Rayleigh wave of the as -plated and heat-treated Ni-P layer were obtained by the one point time domain signal processing. The Ni-P layers with excellent wear resistance produced by the heated treatment higher than 725K were found to show higher Rayleigh velocities than that of the substrate steel, while the Ni-P layer with poor wear resistance showed lower velocities. Young`s moduli of the Ni-P layer, estimated so as the computed velocity dispersion agreed with the measured one, increased with the increase of wear resistance. 10 refs., 9 figs., 2 tabs.

  13. Comparison of Corrosion Behavior of Electrochemically Deposited Nano-Cobalt-Coated Ni Sheet

    Directory of Open Access Journals (Sweden)

    Nasser Al-Aqeeli

    2013-01-01

    Full Text Available Corrosion behavior of nano-coblat-coated Ni sheet was compared with pure Ni and 20% Fe-Ni alloy sheet using potentiodynamic polarization and linear polarization technique in 0.1 M NaCl solution at room temperature. Results showed that corrosion resistance properties of nano-Co-coated Ni sheet were almost same as that of pure Ni sheet, however corrosion resistance of 20% Fe-Ni sheet was decreased significantly. Pitting potential of 20% Fe-Ni sheet was subsequently decreased as compared to pure Ni sheet as well as nano-cobalt-coated Ni sheet. SEM/EDS analysis of the corroded surfaces showed that both pure Ni and nano-coblat-coated Ni sheet did not show any appreciable corrosion however significant corrosion was observed in the case of 20% Fe-Ni sheet.

  14. Spin pumping damping and magnetic proximity effect in Pd and Pt spin-sink layers

    Science.gov (United States)

    Caminale, M.; Ghosh, A.; Auffret, S.; Ebels, U.; Ollefs, K.; Wilhelm, F.; Rogalev, A.; Bailey, W. E.

    2016-07-01

    We investigated the spin pumping damping contributed by paramagnetic layers (Pd, Pt) in both direct and indirect contact with ferromagnetic Ni81Fe19 films. We find a nearly linear dependence of the interface-related Gilbert damping enhancement Δ α on the heavy-metal spin-sink layer thicknesses tN in direct-contact Ni81Fe19 /(Pd, Pt) junctions, whereas an exponential dependence is observed when Ni81Fe19 and (Pd, Pt) are separated by 3 nm Cu. We attribute the quasilinear thickness dependence to the presence of induced moments in Pt, Pd near the interface with Ni81Fe19 , quantified using x-ray magnetic circular dichroism measurements. Our results show that the scattering of pure spin current is configuration-dependent in these systems and cannot be described by a single characteristic length.

  15. Low-temperature synthesis of the infinite-layer compound LaNiO2 by soft-chemical techniques

    International Nuclear Information System (INIS)

    Takamatsu, Tomohisa; Kato, Masatsune; Noji, Takashi; Koike, Yoji

    2010-01-01

    Bulk samples of LaNiO 2 with the so-called infinite-layer structure have successfully been synthesized. First, polycrystalline samples of LaNiO 3 with the perovskite structure were prepared using molten KOH at a temperature of 400-450degC. Then, they were finely ground with a double stoichiometric excess of reductant CaH 2 and sealed in an evacuated Pyrex tube. The sealed ampoule was then heated at 300degC for 24 h. Powder X-ray diffraction analysis has revealed that the product obtained after removing the residual CaH 2 and the byproduct CaO is of almost single phase with tetragonal symmetry, indicating the formation of the infinite-layer compound LaNiO 2 . (author)

  16. Influence of O2 plasma treatment on NiO x layer in perovskite solar cells

    Science.gov (United States)

    Nishihara, Yoshihiko; Chikamatsu, Masayuki; Kazaoui, Said; Miyadera, Tetsuhiko; Yoshida, Yuji

    2018-04-01

    We fabricated perovskite solar cells (PSCs) with an inverted p-i-n planar structure using a NiO x film as a hole-transporting layer. Since the surface of the NiO x film fabricated by sputtering is hydrophobic, O2 plasma treatment under various conditions was performed to improve its wettability. Water contact angles after the treatment under both normal and weak conditions on the NiO x film reached approximately 15°. After the treatment, the valence band level of the NiO x film was deeper by about 0.15 eV. The maximum efficiency of the NiO x -based device under the optimized O2 plasma condition reached 12.3%.

  17. Self-aligned periodic Ni nano dots embedded in nano-oxide layer

    International Nuclear Information System (INIS)

    Doi, M.; Izumi, M.; Kawasaki, S.; Miyake, K.; Sahashi, M.

    2007-01-01

    The Ni nano constriction dots embedded in the Ta-nano-oxide layer (NOL) was prepared by the ion beam sputtering (IBS) method. After the various conditions of the oxidations, the structural analyses of the NOL were performed by RHEED, AES and in situ STM/AFM observations. From the current image of the conductive AFM for NOL, the periodically aligned metallic dots with the size around 5-10 nm were successfully observed. The mechanism of the formation of the self-organized aligned Ni nano constriction dots is discussed from the standpoint of the grain size, the crystal orientation, the preferred oxidation of Ta at the diffused interface

  18. Rust Layer Formed on Low Carbon Weathering Steels with Different Mn, Ni Contents in Environment Containing Chloride Ions

    Directory of Open Access Journals (Sweden)

    Gui-qin FU

    2016-11-01

    Full Text Available The rusting evolution of low carbon weathering steels with different Mn, Ni contents under a simulated environment containing chloride ions has been investigated to clarify the correlation between Mn, Ni and the rust formed on steels. The results show that Mn contents have little impact on corrosion kinetics of experimental steels. Content increase of Ni both enhances the anti-corrosion performance of steel substrate and the rust. Increasing Ni content is beneficial to forming compact rust. Semi-quantitative XRD phase analysis shows that the quantity ratio of α/γ*(α-FeOOH/(γ-FeOOH+Fe3O4 decreases as Mn content increases but it increases as Ni content increases. Ni enhances rust layer stability but Mn content exceeding 1.06 wt.% is disadvantageous for rust layer stability. The content increase of Mn does not significantly alter the parameters of the polarization curve. However, as Ni contents increases, Ecorr has shifted to the positive along with decreased icorr values indicating smaller corrosion rate especially as Ni content increases from 0.42 wt.% to 1.50 wt.%.DOI: http://dx.doi.org/10.5755/j01.ms.22.4.12844

  19. Development of biaxially textured buffer layers on rolled-Ni substrates for high current YBa2Cu3O7-y coated conductors

    International Nuclear Information System (INIS)

    Paranthaman, M.; Goyal, A.; Norton, D.P.

    1996-01-01

    This paper describes the development of 3 buffer layer architectures with good biaxial textures on rolled-Ni substrates using vacuum processing techniques. The techniques include pulsed laser ablation, e-beam evaporation, dc and rf magnetron sputtering. The first buffer layer architecture consists of an epitaxial laminate of Ag/Pd(Pt)/Ni. The second buffer layer consists of an epitaxial laminate of CeO 2 /Pd/Ni. The third alternative buffer layer architecture consists of an epitaxial laminate of YSZ/CeO 2 /Ni. The cube (100) texture in the Ni was produced by cold rolling followed by recrystallization. Crystallographic orientations of the Pd, Ag, CeO 2 , and YSZ films grown were all (100). We recently demonstrated a critical- current density of 0.73x10 6 A/cm 2 at 77 K and zero field on 1.4 μm thick YBa 2 Cu 3 O 7-y (YBCO) film. This film was deposited by pulsed laser ablation on a YBCO/YSZ/CeO 2 /Ni substrate

  20. Improved conductivity of infinite-layer LaNiO{sub 2} thin films by metal organic decomposition

    Energy Technology Data Exchange (ETDEWEB)

    Ikeda, Ai [Department of Applied Physics, Tokyo University of Agriculture and Technology, Naka-cho 2-24-16, Koganei, Tokyo 184-8588 (Japan); Research Fellow of the Japan Society for the Promotion of Science (Japan); Manabe, Takaaki [National Institute of Advanced Industrial Science and Technology (AIST), Higashi 1-1-1, Tsukuba, Ibaraki 305-8565 (Japan); Naito, Michio, E-mail: minaito@cc.tuat.ac.jp [Department of Applied Physics, Tokyo University of Agriculture and Technology, Naka-cho 2-24-16, Koganei, Tokyo 184-8588 (Japan)

    2013-12-15

    Highlights: •LaNiO{sub 2} films were synthesized by metal organic decomposition and topotactic reduction. •Room-temperature resistivity as low as 0.6 mΩ cm was achieved for infinite-layer LaNiO{sub 2}. •Lattice matched substrates are important in obtaining high conductivity. -- Abstract: Infinite-layer LaNiO{sub 2} thin films were synthesized by metal organic decomposition and subsequent topotactic reduction in hydrogen, and their transport properties were investigated. LaNiO{sub 2} is isostructural to SrCuO{sub 2}, the parent compound of high-T{sub c} Sr{sub 0.9}La{sub 0.1}CuO{sub 2} with T{sub c} = 44 K, and has 3d{sup 9} configuration, which is very rare in oxides but common to high-T{sub c} copper oxides. The bulk synthesis of LaNiO{sub 2} is not easy, but we demonstrate in this article that the thin-film synthesis of LaNiO{sub 2} is rather easy, thanks to a large-surface-to-volume ratio, which makes oxygen diffusion prompt. Our refined synthesis conditions produced highly conducting films of LaNiO{sub 2}. The resistivity of the best film is as low as 640 μΩ cm at 295 K and decreases with temperature down to 230 K but it shows a gradual upturn at lower temperatures.

  1. NiO/nanoporous graphene composites with excellent supercapacitive performance produced by atomic layer deposition

    International Nuclear Information System (INIS)

    Chen, Caiying; Chen, Chaoqiu; Duan, Feifei; Zhao, Shichao; Qin, Yong; Huang, Peipei; Li, Ping; Fan, Jinchuan; Song, Weiguo

    2014-01-01

    Nickel oxide (NiO) is a promising electrode material for supercapacitors because of its low cost and high theoretical specific capacitance of 2573 F g −1 . However, the low electronic conductivity and poor cycling stability of NiO limit its practical applications. To overcome these limitations, an efficient atomic layer deposition (ALD) method is demonstrated here for the fabrication of NiO/nanoporous graphene (NG) composites as electrode materials for supercapacitors. ALD allows uniform deposition of NiO nanoparticles with controlled sizes on the surface of NG, thus offering a novel route to design NiO/NG composites for supercapacitor applications with high surface areas and greatly improved electrical conductivity and cycle stability. Electrochemical measurements reveal that the NiO/NG composites obtained by ALD exhibited excellent specific capacitance of up to ∼1005.8 F g −1 per mass of the composite electrode (the specific capacitance value is up to ∼1897.1 F g −1 based on the active mass of NiO), and stable performance after 1500 cycles. Furthermore, electrochemical performance of the NiO/NG composites is found to strongly depend on the size of NiO nanoparticles. (paper)

  2. A Study on Characterization of Light-Induced Electroless Plated Ni Seed Layer and Silicide Formation for Solar Cell Application

    Science.gov (United States)

    Takaloo, Ashkan Vakilipour; Joo, Seung Ki; Es, Firat; Turan, Rasit; Lee, Doo Won

    2018-03-01

    Light-induced electroless plating (LIEP) is an easy and inexpensive method that has been widely used for seed layer deposition of Nickel/Copper (Ni/Cu)-based metallization in the solar cell. In this study, material characterization aspects of the Ni seed layer and Ni silicide formation at different bath conditions and annealing temperatures on the n-side of a silicon diode structure have been examined to achieve the optimum cell contacts. The effects of morphology and chemical composition of Ni film on its electrical conductivity were evaluated and described by a quantum mechanical model. It has been found that correlation exists between the theoretical and experimental conductivity of Ni film. Residual stress and phase transformation of Ni silicide as a function of annealing temperature were evaluated using Raman and XRD techniques. Finally, transmission line measurement (TLM) technique was employed to determine the contact resistance of Ni/Si stack after thermal treatment and to understand its correlation with the chemical-structural properties. Results indicated that low electrical resistive mono-silicide (NiSi) phase as low as 5 mΩ.cm2 was obtained.

  3. Valence electronic structure of Ni in Ni Si alloys from relative K X-ray intensity studies

    Science.gov (United States)

    Kalayci, Y.; Aydinuraz, A.; Tugluoglu, B.; Mutlu, R. H.

    2007-02-01

    The Kβ-to-Kα X-ray intensity ratio of Ni in Ni 3Si, Ni 2Si and NiSi has been determined by energy dispersive X-ray fluorescence technique. It is found that the intensity ratio of Ni decreases from pure Ni to Ni 2Si and then increases from Ni 2Si to NiSi, in good agreement with the electronic structure calculations cited in the literature. We have also performed band structure calculations for pure Ni in various atomic configurations by means of linear muffin-tin orbital method and used this data with the normalized theoretical intensity ratios cited in the literature to estimate the 3d-occupation numbers of Ni in Ni-Si alloys. It is emphasized that investigation of alloying effect in terms of X-ray intensity ratios should be carried out for the stoichiometric alloys in order to make reliable and quantitative comparisons between theory and experiment in transition metal alloys.

  4. Structure and composition of layers of Ni-Co-Mn-In Heusler alloys obtained by pulsed laser deposition

    International Nuclear Information System (INIS)

    Wisz, Grzegorz; Sagan, Piotr; Stefaniuk, Ireneusz; Cieniek, Bogumil; Maziarz, Wojciech; Kuzma, Marian

    2017-01-01

    In present work we were analysing thin layers of Ni-Co-Mn-In alloys, grown by pulsed laser deposition method (PLD) on Si, NaCl and glass substrates. For target ablation the second harmonics of YAG:Nd 3+ laser was used. The target had the composition Ni 45 Co 5 Mn 34.5 In 14.5 . The morphology of the layers and composition were studied by electron microscopy TESCAN Vega3 equipped with microanalyzer EDS – Easy EdX system working with Esprit Bruker software. The X-ray diffraction measurements (XRD), performed on spectrometer Bruker XRD D8 Advance system, reveals Ni 2 -Mn-In cubic phase having lattice constant a = 6.02Å.

  5. Structural conditions of achieving maximum ductility of two-phase Ni-NiO alloys

    International Nuclear Information System (INIS)

    Grabin, V.V.; Dabizha, E.V.; Movchan, B.A.

    1984-01-01

    A study was made on possibility of increasing ductility of two-phase Ni-NiO alloys, proJuced by traditional technology: ingot smelting, rolling and corresponding annealing for production of grain with certain size. The correlation of mechanical properties of Ni-NiO alloys and pure nickel shows that completion of the structural conJition D--lambda (where D - the average grain diameter, lambda - the value of free path between particles) in two-phase alloys enables: to increase the ultimate strength 1.5 times and preserve the basic level of pure nickel plasticity - at 20 deg C; to increase plasticity 1.4-1.5 times with preserved basic level of pure nickel plasticity - at 800 deg C. The conclusions testify to possibility of controlling mechanical properties of two-phase alloys using structural D and lambda parameters It is proposed that creation of structures with more unifor m particle distribution with respect to sizes will the accompanied by further increase of plasticity under D=lambda condition

  6. Electronic structure of Ni/sub 3/Al and Ni/sub 3/Ga alloys

    CERN Document Server

    Pong, W F; Chang, Y K; Tsai, M H; Hsieh, H H; Pieh, J Y; Tseng, P K; Lee, J F; Hsu, L S

    1999-01-01

    This work investigates the charge transfer and Al(Ga) p-Ni d hybridization effects in the intermetallic Ni/sub 3/Al(Ni/sub 3/Ga) alloy using the NiL/sub 3.2/- and K-edge and Al(Ga)K X-ray absorption near edge structure (XANES) measurements. We find that the intensity of white-line features at the NiL/sub 3.2/-edge in the Ni/sub 3/Al(Ni /sub 3/Ga) alloy decreased in comparison with that of pure Ni, which can be attributed to the enhancement of Ni3d states filling and the depletion of the density of Ni 3d unoccupied states in the Ni/sub 3 /Al(Ni/sub 3/Ga) alloy. Two clear features are also observed in the Ni/sub 3/Al(Ni/sub 3/Ga) XANES spectrum at the Al(Ga) K-edge, which can be assigned to the Al(Ga) unoccupied 3p (4p) states and their hybridized states with the Ni 3d/4sp states above the Fermi level in Ni/sub 3/Al(Ni/sub 3/Ga). The threshold at Al K-edge XANES for Ni/sub 3/Al clearly shifts towards higher photon energies relative to that of pure Al, indicating that Al loses charges upon forming Ni/sub 3 /Al. ...

  7. The influence of Ni, Mo, Si, Ti on the surface alloy layer quality

    Directory of Open Access Journals (Sweden)

    A. Walasek

    2011-07-01

    Full Text Available The paper presents research results of microstructure and selected mechanical properties of alloy layer. The aim of the researches was to determine the influence of Ni, Mo, Si and Ti with high-carbon ferrochromium (added separately to pad on the alloy layer on the steel cast. Metallographic studies were made with use of light microscopy. During studies of usable properties measurements of hardness, microhardness and abrasive wear resistance of type metal-mineral for creation alloy layer were made. As thick as possible composite layer without any defects and discontinuity was required. The conducted researches allowed to take the suitable alloy addition of the pad material which improved the quality of the surface alloy layer.

  8. Self-assembled 3D flower-like Ni2+-Fe3+ layered double hydroxides and their calcined products

    International Nuclear Information System (INIS)

    Xiao Ting; Tang Yiwen; Jia Zhiyong; Li Dawei; Hu Xiaoyan; Li Bihui; Luo Lijuan

    2009-01-01

    This paper describes a facile solvothermal method to synthesize self-assembled three-dimensional (3D) Ni 2+ -Fe 3+ layered double hydroxides (LDHs). Flower-like Ni 2+ -Fe 3+ LDHs constructed of thin nanopetals were obtained using ethylene glycol (EG) as a chelating reagent and urea as a hydrolysis agent. The reaction mechanism and self-assembly process are discussed. After calcinating the as-prepared LDHs at 450 0 C in nitrogen gas, porous NiO/NiFe 2 O 4 nanosheets were obtained. This work resulted in the development of a simple, cheap, and effective route for the fabrication of large area Ni 2+ -Fe 3+ LDHs as well as porous NiO/NiFe 2 O 4 nanosheets.

  9. Dehydrogenation kinetics of pure and nickel-doped magnesium hydride investigated by in situ time-resolved powder X-ray diffraction

    DEFF Research Database (Denmark)

    Jensen, T.R.; Andreasen, A.; Vegge, Tejs

    2006-01-01

    The dehydrogenation kinetics of pure and nickel (Ni)-doped (2w/w%) magnesium hydride (MgH2) have been investigated by in situ time-resolved powder X-ray diffraction (PXD). Deactivated samples, i.e. air exposed, are investigated in order to focus on the effect of magnesium oxide (MgO) surface layers......, which might be unavoidable for magnesium (Mg)-based storage media for mobile applications. A curved position-sensitive detector covering 120 degrees in 20 and a rotating anode X-ray source provide a time resolution of 45 s and up to 90 powder pattems collected during an experiment under isothermal...... by the Johnson-Mehi-Avrami formalism in order to derive rate constants at different temperatures. The apparent activation energies for dehydrogenation of pure and Ni-doped magnesium hydride were E-A approximate to 300 and 250 kJ/mol, respectively. Differential scanning calorimetry gave, E-A = 270 k...

  10. Synthesis of novel spherical Fe_3O_4@Ni_3S_2 composite as improved anode material for rechargeable nickel-iron batteries

    International Nuclear Information System (INIS)

    Li, Jing; Guo, Litan; Shangguan, Enbo; Yue, Mingzhu; Xu, Min; Wang, Dong; Chang, Zhaorong; Li, Quanmin

    2017-01-01

    Highlights: • Fe_3O_4@Ni_3S_2 microspheres are fabricated through a facile method for the first time. • Fe_3O_4@Ni_3S_2 is firstly proposed as alkaline anode materials for Ni/Fe batteries. • Fe_3O_4@Ni_3S_2 shows enhanced high-rate capability and improved cycle stability. • Ni_3S_2 can suppress the passivation and hydrogen evolution behavior of the iron anode. - Abstract: Fe_3O_4@Ni_3S_2 microspheres as a novel alkaline anode material have been successfully fabricated through a four-step process for the first time. In this composite, Ni_3S_2 nanoparticles are coated tightly on the surface of Fe_3O_4 microspheres. Compared with the pure Fe_3O_4 and Fe_3O_4@NiO microspheres, the proposed Fe_3O_4@Ni_3S_2 delivers a significantly improved high-rate performance and enhanced cycling stability. At a high discharge rate of 1200 mA g"−"1, the specific capacity of the Fe_3O_4@Ni_3S_2 is ∼481.2 mAh g"−"1 in comparison with ∼83.7 mAh g"−"1 for the pure Fe_3O_4. After 100 cycles at 120 mA g"−"1, the Fe_3O_4@Ni_3S_2 can achieve a capacity retention of 95.1%, while the value for the pure Fe_3O_4 electrode is only 52.5%. The favorable electrochemical performance of the Fe_3O_4@Ni_3S_2 is mainly attributed to the beneficial impact of Ni_3S_2. The Ni_3S_2 layer as a useful additive is significantly conducive to lessening the formation of Fe(OH)_2 passivation layer, enhancing the electronic conductivity, improving the reaction reversibility and suppressing the hydrogen evolution reaction of the alkaline iron anode. Owing to its outstanding electrochemical properties, we believe that the novel Fe_3O_4@Ni_3S_2 composite is potentially a promising candidate for anode material of alkaline iron-based batteries.

  11. In vitro corrosion of pure magnesium and AZ91 alloy?the influence of thin electrolyte layer thickness

    OpenAIRE

    Zeng, Rong-Chang; Qi, Wei-Chen; Zhang, Fen; Li, Shuo-Qi

    2016-01-01

    In vivo degradation predication faces a huge challenge via in vitro corrosion test due to the difficulty for mimicking the complicated microenvironment with various influencing factors. A thin electrolyte layer (TEL) cell for in vitro corrosion of pure magnesium and AZ91 alloy was presented to stimulate the in vivo corrosion in the micro-environment built by the interface of the implant and its neighboring tissue. The results demonstrated that the in vivo corrosion of pure Mg and the AZ91 all...

  12. Posterior magnetic effect on the pure and doped Fe-Ni alloy under neutron irradiation; Efeito magnetico posterior na liga Fe-Ni pura e dopada, sob irradiacao neutronica

    Energy Technology Data Exchange (ETDEWEB)

    Ferreira, Iris

    1974-07-01

    Polycrystalline specimens of unirradiated and neutron irradiated Fe-Ni alloys have been studied in the temperature range RT - 500 deg C. The study was carried out in pure (50-50) as well as in Si, A1, Cr and Mo doped samples. Initial magnetic permeability was measured in unirradiated (virgin)and in neutron irradiated samples, during isochronal and linear thermal treatments. The main results are: a magnetic After Effect (MAE) is detected in the temperature range 370 deg C - Tc, where Tc is the Curie Temperature. In this range an activation energy of 3.2 {+-} 0.2 eV was determined for the Cr doped Fe-Ni alloy (impurity content: 0.1%); measurements made in the irradiated samples, during a linear temperature treatment, show the existence of several MAE zones in the temperature range RT - Tc. The isochronal annealing experiments show that these MAE zones are accompanied by a decrease in the room temperature value of the magnetic permeability, for zones between RT and a certain temperature T{sub 1}. Above this range there is a steep increase in the room temperature permeability. Activation energies were determined for pure and Mo-doped (0.1%) samples for the first MAE zone (50 deg C - 120 deg C). The values obtained 1.25 - 0.08 eV and 1.42 {+-} 0.09 eV, respectively; the impurity - doped samples show a different behaviour relative to the pure ones: samples with low impurity content (0.1% and 0.5% of Si, Al or Mo) present an enhancement in the amplitude and also an overlapping of the diffusion stages. On the other hand, samples with higher impurity content (2 and 4% of Mo) show a decrease in these amplitudes. (author)

  13. Growth and characterization of ternary Ni, Mg–Al and Ni–Al layered double hydroxides thin films deposited by pulsed laser deposition

    Energy Technology Data Exchange (ETDEWEB)

    Birjega, R. [National Institute for Lasers, Plasma and Radiation Physics, 409 Atomistilor Str., Magurele, 76900 Bucharest (Romania); Vlad, A., E-mail: angela.vlad@gmail.com [National Institute for Lasers, Plasma and Radiation Physics, 409 Atomistilor Str., Magurele, 76900 Bucharest (Romania); Matei, A.; Ion, V.; Luculescu, C.; Dinescu, M. [National Institute for Lasers, Plasma and Radiation Physics, 409 Atomistilor Str., Magurele, 76900 Bucharest (Romania); Zavoianu, R. [University of Bucharest, Faculty of Chemistry, Department of Chemical Technology and Catalysis, 4-12 Regina Elisabeta Bd., Bucharest (Romania)

    2016-09-01

    Layered double hydroxides (LDHs) are a class of layered materials consisting of positively charged brucite-like layers and exchangeable interlayer anions. Layered double hydroxides containing a transition metal which undergoes a reversible redox reaction in the useful potential range have been proposed as electrode coating materials due to their properties of charge transport and redox catalysts in basic solutions. Ni–Al,(Ni,Mg)–Al and, as reference, non-electronically conductive Mg–Al double hydroxides thin films were obtained via pulsed laser deposition technique. The thin films were deposited on different substrates (Si, glass) by using a Nd:YAG laser (1064 nm) working at a repetition rate of 10 Hz. X-ray diffraction, Atomic Force Microscopy, Energy Dispersive X-ray spectroscopy, Fourier Transform Infra-Red Spectroscopy, Secondary Ions Mass Spectrometry, Impedance Analyzer and ellipsometry were the techniques used for the as deposited thin films investigation. The optical properties of Ni based LDH thin films and the effect of the Ni amount on the structural, morphological and optical response are evidenced. The optical band gap values, covering a domain between 3.84 eV and 4.38 eV, respond to the Ni overall concentration: the higher Ni amount the lower the band gap value. - Highlights: • Ternary Ni, Mg–Al and Ni–Al layered double hydroxides thin films were deposited. • The effect of the nickel is evidenced. • The possibility to tailor the materials accompanied by an optical response is shown.

  14. Understanding the Intrinsic Electrochemistry of Ni-Rich Layered Cathodes

    Science.gov (United States)

    Sallis, Shawn

    The demand for energy is continually increasing overtime and the key to meeting future demand in a sustainable way is with energy storage. Li-ion batteries employing layered transition metal oxide cathodes are one of the most technologically important energy storage technologies. However, current Li-ion batteries are unable to access their full theoretical capacity and suffer from performance limiting degradation over time partially originating from the cathode and partially from the interface with the electrolyte. Understanding the fundamental limitations of layered transition metal oxide cathodes requires a complete understanding of the surface and bulk of the materials in their most delithiated state. In this thesis, we employ LiNi0.8Co0.15Al 0.05O2 (NCA) as a model system for Ni-rich layered oxide cathodes. Unlike its parent compound, LiCoO2, NCA is capable of high states of delithiation with minimal structural transitions. Furthermore, commercially available NCA has little to no transition metals in the Li layer. X-ray spectroscopies are an ideal tool for studying cathodes at high states of delithiation due their elemental selectivity, range of probing depths, and sensitivity to both chemical and electronic state information. The oxidation state of the transition metals at the surface can be probed via X-ray photoelectron spectroscopy (XPS) while both bulk and surface oxidation states as well as changes in metal oxygen bonding can be probed using X-ray absorption spectroscopy (XAS). Using X-ray spectroscopy in tandem with electrochemical, transport and microscopy measurements of the same materials, the impedance growth with increasing delithiation was correlated with the formation of a disordered NiO phase on the surface of NCA which was precipitated by the release of oxygen. Furthermore, the surface degradation was strongly impacted by the type of Li salt used in the electrolyte, with the standard commercial salt LiPF6 suffering from exothermic decomposition

  15. Magnetic properties of Co-Rh and Ni-Rh nanowires

    International Nuclear Information System (INIS)

    Sondon, Tristana; Saul, Andres; Guevara, Javier

    2007-01-01

    We have calculated the magnetic properties of pure Ni, Co and Rh, and alloyed Co-Rh and Ni-Rh free-standing nanowires by an ab initio method. We have found that the pure Co and Ni wires present an enhanced magnetic moment with respect to their bulk values, and we have obtained that a magnetic order appears for pure Rh wires. For concentrations up to 50% Rh, in the alloyed Ni-Rh linear chains there is an enhancement of the total magnetic moment with respect to the pure nanowires, and in the case of Co-Rh the alloying with Rh enhances the Co magnetic moment. In both systems we obtain very high Rh magnetic moments

  16. The influence of alizarin and fluorescein on the photoactivity of Ni, Pt and Ru-doped TiO2 layers

    International Nuclear Information System (INIS)

    Rosu, Marcela-Corina; Suciu, Ramona-Crina; Lazar, Mihaela D.; Bratu, I.

    2013-01-01

    Highlights: ► The Ni, Pt, Ru-doped TiO 2 materials and sensitized with alizarin and fluorescein dyes were prepared by wet chemical route. ► The samples were characterized by: UV–vis spectroscopy, spectrofluorimetry, FT/IR spectroscopy and microscopy, X-ray diffraction and N 2 physisorption measurements. ► A combined influence of the dopants and dyes was observed, leading to a beneficial effect to TiO 2 photoactivity. -- Abstract: The doping with different metal ions and sensitization with organic compounds are two well known methods used to improve the photoactivity of TiO 2 . In this respect, the metallic ions-doped TiO 2 samples were prepared by embedding Ni, Pt and Ru ions into TiO 2 crystalline network and then, each sample was sensitized with alizarin and fluorescein dyes. The qualitative evaluation of prepared TiO 2 -based materials was made by: UV–vis spectroscopy, spectrofluorimetry, FT/IR spectroscopy and microscopy, X-ray diffraction and N 2 physisorption measurements. The optoelectronic properties investigated by UV–vis spectroscopy show that the optical response of Ni-doped TiO 2 layer shifts to visible. The X-ray spectra do not show peaks of nickel, platinum and ruthenium oxide crystals or pure metals. The FT/IR spectra proved the presence of dye molecules adsorbed on titania nanoparticles surface. These results demonstrated that the studied dopants and dyes have potential to promote modified TiO 2 -based materials as good candidates to be used in photolectrocatalytic processes

  17. Growth behavior of surface oxide layer on SUS316L stainless steel at the early stage of exposure to 288degC water

    International Nuclear Information System (INIS)

    Soma, Yasutaka; Kato, Chiaki; Yamamoto, Masahiro

    2012-01-01

    Surface oxide layer on SUS316L stainless steels exposed to 288degC pure water with 2 ppm dissolved oxygen (DO) for 1-100 h were analyzed using Focused Ion Beam (FIB) and Scanning Transmission Electron Microscope (STEM) technique to understand the early stage of surface oxide layer formation. In order to analyze the multi layered surface oxide, the interfaces between the outer and the inner oxide layers and that between the inner oxide layer and SUS316L substrate were determined from Energy Dispersive X-ray Spectroscopy (EDX) line profiles. At 1 h exposure, double oxide layer which is composed of compact inner oxide layer and outer oxide layer with Fe-rich and Ni-rich oxide particles was formed. At the outermost region of the SUS316L substrate, Ni and Cr were enriched. At 100 h exposure, growth of the inner oxide layer was suppressed and the Ni and Cr enriched region at the alloy substrate was preserved underneath the Ni-rich outer oxide particles. At 1 h exposure, most of the outer oxide particles were composed of Fe-rich ones, at 10 h exposure, another Ni-rich outer oxide particles were nucleated and grew faster than Fe-rich ones. Consequently, a part of pre-formed Fe-rich outer oxide particles were covered with Ni-rich ones. (author)

  18. Interfacial mixing in double-barrier magnetic tunnel junctions with amorphous NiFeSiB layers

    International Nuclear Information System (INIS)

    Chun, B.S.; Ko, S.P.; Hwang, J.Y.; Rhee, J.R.; Kim, T.W.; Kim, Y.K.

    2007-01-01

    Double-barrier magnetic tunnel junctions (DMTJs) comprising Ta 45/Ru 9.5/IrMn 10/CoFe 7/AlO x /free layer (CoFe 4/NiFeSiB 2/CoFe 4, CoFe 10, or NiFeSiB 10)/AlO x /CoFe 7/IrMn 10/Ru 60 (nm) have been examined with an emphasis given on understanding the interfacial mixing effects. The DMTJ, consisted of NiFeSiB, shows low switching field and low bias voltage dependence because the amorphous NiFeSiB has lower M S (=800 emu/cm 3 ) and offers smoother interfaces than polycrystalline CoFe. An interesting feature observed in the CoFe/NiFeSiB/CoFe sandwich free layered DMTJ is the presence of a wavy MR transfer curve at high-resistance region. Because the polycrystalline CoFe usually grows into a columnar structure, diamagnetic CoSi, paramagnetic FeSi, and/or diamagnetic CoB might have been formed during the sputter-deposition process. By employing electron energy loss spectrometry (EELS) and Auger electron spectroscopy (AES), we were able to confirm that Si and B atoms were arranged evenly in the top and bottom portions of AlO x /CoFe interfaces. This means that the interfacial mixing resulted in a distorted magnetization reversal process

  19. Effect of Ni addition to the Cu substrate on the interfacial reaction and IMC growth with Sn3.0Ag0.5Cu solder

    Science.gov (United States)

    Zhang, Xudong; Hu, Xiaowu; Jiang, Xiongxin; Li, Yulong

    2018-04-01

    The formation and growth of intermetallic compound (IMC) layer at the interface between Sn3.0Ag0.5Cu (SAC305) solder and Cu- xNi ( x = 0, 0.5, 1.5, 5, 10 wt%) substrate during reflowing and aging were investigated. The soldering was conducted at 270 °C using reflowing method, following by aging treatment at 150 °C for up to 360 h. The experimental results indicated that the total thickness of IMC increased with increasing aging time. The scallop-like Cu6Sn5 and planar-like Cu3Sn IMC layer were observed between SAC305 solder and purely Cu substrate. As the content of Ni element in Cu substrate was 0.5% or 1.5%, the scallop-like Cu6Sn5 and planar-like Cu3Sn IMC layer were still found between solder and Cu-Ni substrate and the total thickness of IMC layer decreased with the increasing Ni content. Besides, when the Ni content was up to 5%, the long prismatic (Cu,Ni)6Sn5 phase was the only product between solder and substrate and the total thickness of IMC layer increased significantly. Interestingly, the total thickness of IMC decreased slightly as the Ni addition was up to 10%. In the end, the grains of interfacial IMC layer became coarser with aging time increasing while the addition of Ni in Cu substrate could refine IMC grains.

  20. Research on Zr50Al15-xNi10Cu25Yx amorphous alloys prepared by mechanical alloying with commercial pure element powders

    International Nuclear Information System (INIS)

    Long Woyun; Ouyang Xueqiong; Luo Zhiwei; Li Jing; Lu Anxian

    2011-01-01

    Amorphous Zr 50 Al 15-x Ni 10 Cu 25 Y x alloy powders were fabricated by mechanical alloying at low vacuum with commercial pure element powders. The effects on glass forming ability of Al partial substituted by Y in Zr 50 Al 15 Ni 10 Cu 25 and thermal stability of Si 3 N 4 powders addition were investigated. The as-milled powders were characterized by X-ray diffraction, scanning electron microscopy and differential scanning calorimeter. The results show that partial substitution of Al can improve the glass forming ability of Zr 50 Al 15 Ni 10 Cu 25 alloy. Minor Si 3 N 4 additions raise the crystallization activation energy of the amorphous phase and thus improve its thermal stability. -- Research Highlights: → ZrAlNiCu amorphous alloys can be synthesized by MA in low cost. → Appropriate amount of Al substituted by Y in ZrAlNiCu alloy can improve its glass forming ability. → A second phase particle addition helps to improve the thermal stability of the amorphous matrix.

  1. Highly effective synthesis of NiO/CNT nanohybrids by atomic layer deposition for high-rate and long-life supercapacitors.

    Science.gov (United States)

    Yu, Lei; Wang, Guilong; Wan, Gengping; Wang, Guizhen; Lin, Shiwei; Li, Xinyue; Wang, Kan; Bai, Zhiming; Xiang, Yang

    2016-09-21

    In this work, we report an atomic layer deposition (ALD) method for the fabrication of NiO/CNT hybrid structures in order to improve electronic conductivity, enhance cycling stability and increase rate capability of NiO used as supercapacitor electrodes. A uniform NiO coating can be well deposited on carbon nanotubes (CNTs) through simultaneously employing O3 and H2O as oxidizing agents in a single ALD cycle of NiO for the first time, with a high growth rate of nearly 0.3 Å per cycle. The electrochemical properties of the as-prepared NiO/CNT were then investigated. The results show that the electrochemical capacitive properties are strongly associated with the thickness of the NiO coating. The NiO/CNT composite materials with 200 cycles of NiO deposition exhibit the best electrochemical properties, involving high specific capacitance (622 F g(-1) at 2 A g(-1), 2013 F g(-1) for NiO), excellent rate capability (74% retained at 50 A g(-1)) and outstanding cycling stability. The impressive results presented here suggest a great potential for the fabrication of composite electrode materials by atomic layer deposition applied in high energy density storage systems.

  2. Microstructure of bonding zones in laser-clad Ni-alloy-based composite coatings reinforced with various ceramic powders

    International Nuclear Information System (INIS)

    Pei, Y.T.; Ouyang, J.H.; Lei, T.C.

    1996-01-01

    Microstructure of the bonding zones (BZs) between laser-clad Ni-alloy-based composite coatings and steel substrates was studied by means of scanning electron microscope (SEM) and transmission electron microscope (TEM) techniques. Observations indicate that for pure Ni-alloy coating the laser parameters selected for good interface fusion have no effect on the microstructure of the BZ except for its thickness. However, the addition of ceramic particles (TiN, SiC, or ZrO 2 ) to the Ni alloy varies the compositional or constitutional undercooling of the melt near the solid/liquid interface and consequently leads to the observed changes of microstructure of the BZs. For TiN/Ni-alloy coating the morphology of γ-Ni solid solution in the BZ changes from dendritic to planar form with increasing scanning speed. A colony structure of eutectic is found in the BZ of SiC/Ni-alloy coating in which complete dissolution of SiC particles takes place during laser cladding. The immiscible melting of ZrO 2 and Ni-alloy powders induces the stratification of ZrO 2 /Ni-alloy coating which consists of a pure ZrO 2 layer fin the upper region and a BZ composed mainly of γ-Ni dendrites adjacent to the substrate. All the BZs studied in this investigation have good metallurgical characteristics between the coatings and the substrates

  3. 4.0-nm-thick amorphous Nb–Ni film as a conducting diffusion barrier layer for integrating ferroelectric capacitor on Si

    International Nuclear Information System (INIS)

    Dai, X.H.; Guo, J.X.; Zhang, L.; Jia, D.M.; Qi, C.G.; Zhou, Y.; Li, X.H.; Shi, J.B.; Fu, Y.J.; Wang, Y.L.; Lou, J.Z.; Ma, L.X.; Zhao, H.D.; Liu, B.T.

    2015-01-01

    Highlights: • 4-nm-thick amorphous Nb–Ni film is first used as the conducting barrier layer. • No obvious interdiffusion/reaction can be found from the LSCO/PZT/LSCO/Nb–Ni/Si. • The LSCO/PZT/LSCO capacitor, measured at 5 V, possesses very good properties. • Ultrathin amorphous Nb–Ni film is ideal to fabricate silicon-based FRAM. - Abstract: We have successfully integrated La 0.5 Sr 0.5 CoO 3 /PbZr 0.4 Ti 0.6 O 3 /La 0.5 Sr 0.5 CoO 3 (LSCO/PZT/LSCO) capacitors on silicon substrate using a ∼4.0-nm-thick amorphous Nb–Ni film as the conducting diffusion barrier layer. Transmission electron microscopy technique confirms that the Nb–Ni film is still amorphous after fabrication of the capacitors, and the interfaces related to Nb–Ni are clean and sharp without any findable interdiffusion/reaction. The LSCO/PZT/LSCO capacitor, measured at 5 V, possesses very good properties, such as large remanent polarization of ∼22.1 μC/cm 2 , small coercive voltage of ∼1.27 V, good fatigue-resistance, and small pulse width dependence, implying that ultrathin amorphous Nb–Ni film is ideal as the conducting diffusion barrier layer to fabricate high-density silicon-based ferroelectric random access memories

  4. 4.0-nm-thick amorphous Nb–Ni film as a conducting diffusion barrier layer for integrating ferroelectric capacitor on Si

    Energy Technology Data Exchange (ETDEWEB)

    Dai, X.H. [Hebei Key Lab of Optic-electronic Information and Materials, College of Physics Science & Technology, Hebei University, Hebei 071002 (China); College of Electronic and Information Engineering, Hebei University of Technology, Tianjin 300401 (China); Guo, J.X.; Zhang, L.; Jia, D.M.; Qi, C.G.; Zhou, Y.; Li, X.H.; Shi, J.B.; Fu, Y.J.; Wang, Y.L.; Lou, J.Z. [Hebei Key Lab of Optic-electronic Information and Materials, College of Physics Science & Technology, Hebei University, Hebei 071002 (China); Ma, L.X. [Department of Physics, Blinn College, Bryan, TX 77805 (United States); Zhao, H.D. [College of Electronic and Information Engineering, Hebei University of Technology, Tianjin 300401 (China); Liu, B.T., E-mail: btliu@hbu.cn [Hebei Key Lab of Optic-electronic Information and Materials, College of Physics Science & Technology, Hebei University, Hebei 071002 (China)

    2015-10-05

    Highlights: • 4-nm-thick amorphous Nb–Ni film is first used as the conducting barrier layer. • No obvious interdiffusion/reaction can be found from the LSCO/PZT/LSCO/Nb–Ni/Si. • The LSCO/PZT/LSCO capacitor, measured at 5 V, possesses very good properties. • Ultrathin amorphous Nb–Ni film is ideal to fabricate silicon-based FRAM. - Abstract: We have successfully integrated La{sub 0.5}Sr{sub 0.5}CoO{sub 3}/PbZr{sub 0.4}Ti{sub 0.6}O{sub 3}/La{sub 0.5}Sr{sub 0.5}CoO{sub 3} (LSCO/PZT/LSCO) capacitors on silicon substrate using a ∼4.0-nm-thick amorphous Nb–Ni film as the conducting diffusion barrier layer. Transmission electron microscopy technique confirms that the Nb–Ni film is still amorphous after fabrication of the capacitors, and the interfaces related to Nb–Ni are clean and sharp without any findable interdiffusion/reaction. The LSCO/PZT/LSCO capacitor, measured at 5 V, possesses very good properties, such as large remanent polarization of ∼22.1 μC/cm{sup 2}, small coercive voltage of ∼1.27 V, good fatigue-resistance, and small pulse width dependence, implying that ultrathin amorphous Nb–Ni film is ideal as the conducting diffusion barrier layer to fabricate high-density silicon-based ferroelectric random access memories.

  5. Atomic-Resolution Visualization of Distinctive Chemical Mixing Behavior of Ni, Co and Mn with Li in Layered Lithium Transition-Metal Oxide Cathode Materials

    Energy Technology Data Exchange (ETDEWEB)

    Yan, Pengfei; Zheng, Jianming; Lv, Dongping; Wei, Yi; Zheng, Jiaxin; Wang, Zhiguo; Kuppan, Saravanan; Yu, Jianguo; Luo, Langli; Edwards, Danny J.; Olszta, Matthew J.; Amine, Khalil; Liu, Jun; Xiao, Jie; Pan, Feng; Chen, Guoying; Zhang, Jiguang; Wang, Chong M.

    2015-07-06

    Capacity and voltage fading of layer structured cathode based on lithium transition metal oxide is closely related to the lattice position and migration behavior of the transition metal ions. However, it is scarcely clear about the behavior of each of these transition metal ions. We report direct atomic resolution visualization of interatomic layer mixing of transition metal (Ni, Co, Mn) and lithium ions in layer structured oxide cathodes for lithium ion batteries. Using chemical imaging with aberration corrected scanning transmission electron microscope (STEM) and DFT calculations, we discovered that in the layered cathodes, Mn and Co tend to reside almost exclusively at the lattice site of transition metal (TM) layer in the structure or little interlayer mixing with Li. In contrast, Ni shows high degree of interlayer mixing with Li. The fraction of Ni ions reside in the Li layer followed a near linear dependence on total Ni concentration before reaching saturation. The observed distinctively different behavior of Ni with respect to Co and Mn provides new insights on both capacity and voltage fade in this class of cathode materials based on lithium and TM oxides, therefore providing scientific basis for selective tailoring of oxide cathode materials for enhanced performance.

  6. Ni-P/Zn-Ni compositionally modulated multilayer coatings - Part 2: Corrosion and protection mechanisms

    Science.gov (United States)

    Bahadormanesh, Behrouz; Ghorbani, Mohammad

    2018-06-01

    The Ni-P/Zn-Ni compositionally modulated multilayer coatings CMMCs were electrodeposited from a single bath by switching the deposition current density. The corrosion resistance of the deposits was studied and compared with that of monolayers of Ni-P and Zn-Ni alloys via Tafel polarization, EIS and salt spray tests. Characterization of corrosion products by means of EDS and XRD revealed more details from the corrosion mechanism of the monolayers and multilayers. The corrosion current density of Ni-P/Zn-Ni CMMCs were around one tenth of Zn-Ni monolayer. The CMMC with incomplete layers performed lower polarization resistance and higher corrosion current density compared to the CMMC with complete layers. The electrical circuit that was proposed for modeling the corrosion process based on the EIS spectrum, proved that layering reduces the porosity and consequently improves the barrier properties. Although, layering of Zn-Ni layers with Ni-P deposits increased the time to red rust in salt spray test, the time for white rust formation decreased. The corrosion mechanism of both Zn-Ni and Ni-P (containing small amount of Zn) was preferential dissolution of Zn and the corrosion products were comprised of mainly Zn hydroxychloride and Zn hydroxycarbonate. Also, Ni and P did not take part in the corrosion products. Based on the electrochemical character of the layers and the morphology of the corroded surface, the corrosion mechanism of multilayers was discussed.

  7. Effect of nickel seed layer on growth of α-V{sub 2}O{sub 5} nanostructured thin films

    Energy Technology Data Exchange (ETDEWEB)

    Sharma, Rabindar Kumar; Kant, Chandra; Kumar, Prabhat; Singh, Megha, E-mail: meghasingh-08@yahoo.com; Reddy, G. B. [Thin film Laboratory, Department of Physics, Indian Institute of Technology Delhi-110016 (India)

    2015-08-28

    In this communication, we reported the role of Ni seed layer on the growth of vanadium pentoxide (α-V{sub 2}O{sub 5}) nanostructured thin films (NSTs) using plasma assisted sublimation process (PASP). Two different substrates, simple glass substrate and the Ni coated glass substrate (Ni thickness ∼ 100 nm) are employing in the present work. The influence of seed layer on structural, morphological, and vibrational properties have been studied systematically. The structural analysis divulged that both films deposited on simple glass as well as on Ni coated glass shown purely orthorhombic phase, no other phases are detected. The morphological studies of V{sub 2}O{sub 5} film deposited on both substrates are carried out by SEM, revealed that features of V{sub 2}O{sub 5} NSTs is completely modified in presence of Ni seed layer and the film possessing the excellent growth of nanorods (NRs) on Ni coated glass rather than simple glass. The HRTEM analysis of NRs is performed at very high magnification, shows very fine fringe pattern, which confirmed the single crystalline nature of nanorods. The vibrational study of NRs is performed using micro-Raman spectroscopy, which strongly support the XRD observations.

  8. The Leakage Current Improvement of a Ni-Silicided SiGe/Si Junction Using a Si Cap Layer and the PAI Technique

    International Nuclear Information System (INIS)

    Chang Jian-Guang; Wu Chun-Bo; Ji Xiao-Li; Ma Hao-Wen; Yan Feng; Shi Yi; Zhang Rong

    2012-01-01

    We investigate the leakage current of ultra-shallow Ni-silicided SiGe/Si junctions for 45 nm CMOS technology using a Si cap layer and the pre-amorphization implantation (PAI) process. It is found that with the conventional Ni silicide method, the leakage current of a p + (SiGe)—n(Si) junction is large and attributed to band-to-band tunneling and the generation-recombination process. The two leakage contributors can be suppressed quite effectively when a Si cap layer is added in the Ni silicide method. The leakage reduction is about one order of magnitude and could be associated with the suppression of the agglomeration of the Ni germano-silicide film. In addition, the PAI process after the application of a Si cap layer has little effect on improving the junction leakage but reduces the sheet resistance of the silicide film. As a result, the novel Ni silicide method using a Si cap combined with PAI is a promising choice for SiGe junctions in advanced technology. (cross-disciplinary physics and related areas of science and technology)

  9. The influence of alizarin and fluorescein on the photoactivity of Ni, Pt and Ru-doped TiO{sub 2} layers

    Energy Technology Data Exchange (ETDEWEB)

    Rosu, Marcela-Corina, E-mail: marcela.rosu@itim-cj.ro [National Institute for Research and Development of Isotopic and Molecular Technologies, 65-103 Donath Street, 400293, Cluj-Napoca (Romania); Suciu, Ramona-Crina; Lazar, Mihaela D.; Bratu, I. [National Institute for Research and Development of Isotopic and Molecular Technologies, 65-103 Donath Street, 400293, Cluj-Napoca (Romania)

    2013-04-20

    Highlights: ► The Ni, Pt, Ru-doped TiO{sub 2} materials and sensitized with alizarin and fluorescein dyes were prepared by wet chemical route. ► The samples were characterized by: UV–vis spectroscopy, spectrofluorimetry, FT/IR spectroscopy and microscopy, X-ray diffraction and N{sub 2} physisorption measurements. ► A combined influence of the dopants and dyes was observed, leading to a beneficial effect to TiO{sub 2} photoactivity. -- Abstract: The doping with different metal ions and sensitization with organic compounds are two well known methods used to improve the photoactivity of TiO{sub 2}. In this respect, the metallic ions-doped TiO{sub 2} samples were prepared by embedding Ni, Pt and Ru ions into TiO{sub 2} crystalline network and then, each sample was sensitized with alizarin and fluorescein dyes. The qualitative evaluation of prepared TiO{sub 2}-based materials was made by: UV–vis spectroscopy, spectrofluorimetry, FT/IR spectroscopy and microscopy, X-ray diffraction and N{sub 2} physisorption measurements. The optoelectronic properties investigated by UV–vis spectroscopy show that the optical response of Ni-doped TiO{sub 2} layer shifts to visible. The X-ray spectra do not show peaks of nickel, platinum and ruthenium oxide crystals or pure metals. The FT/IR spectra proved the presence of dye molecules adsorbed on titania nanoparticles surface. These results demonstrated that the studied dopants and dyes have potential to promote modified TiO{sub 2}-based materials as good candidates to be used in photolectrocatalytic processes.

  10. Sol-gel-processed yttrium-doped NiO as hole transport layer in inverted perovskite solar cells for enhanced performance

    Science.gov (United States)

    Hu, Zijun; Chen, Da; Yang, Pan; Yang, Lijun; Qin, Laishun; Huang, Yuexiang; Zhao, Xiaochong

    2018-05-01

    In this work, high-performance inverted planar perovskite solar cells (PSCs) using sol-gel processed Y-doped NiO thin films as hole transport layer (HTL) were demonstrated. Y-doped NiO thin films containing different Y doping concentrations were successfully prepared through a simple sol-gel process. The Y doping could significantly improve the electrical conductivity of NiO thin film, and the photovoltaic performance of Y-doped NiO HTL-based PSC devices outperformed that of the pristine NiO HTL-based device. Notably, the PSC using a 5%Y-NiO HTL exhibited the champion performance with an open-circuit voltage (Voc) of 1.00 V, a short circuit current density (Jsc) of 23.82 mA cm-2, a fill factor (FF) of 68% and a power conversion efficiency (PCE) of 16.31%, resulting in a 27.62% enhancement in PCE in comparison with the NiO device. The enhanced performance of the Y-doped NiO device could be attributed to the improved hole mobility, the high quality compact active layer morphology, the more efficient charge extraction from perovskite absorber as well as the lower recombination probability of charge carriers. Thus, this work provides a simple and effective approach to improve the electrical conductivity of p-type NiO thin films for use as a promising HTL in high performance PSCs.

  11. Structure and morphology of ultrathin NiO layers on Ag(001)

    Energy Technology Data Exchange (ETDEWEB)

    Giovanardi, C.; Di Bona, A.; Altieri, S.; Luches, P.; Liberati, M.; Rossi, F.; Valeri, S

    2003-03-20

    The structure and morphology of thin NiO films prepared on Ag(001) by reactive growth at 460 K has been investigated as a function of the film thickness in the 3-20 monolayers range. Emphasis was on the study of the oxide layer misfit strain. Primary beam diffraction modulated electron emission and low energy electron diffraction experiments allowed the determination of the in-plane and out-of-plane strain in the oxide layer, while scanning tunneling microscopy, X-ray photoelectron spectroscopy and secondary electron imaging have been used to monitor the film morphology, stoichiometry and structure, respectively. The film strain begins to be removed at a critical thickness of 10 ML, while at 20 ML the film is fully relaxed. Strain analysis indicates that the Poisson ratio of the oxide layer is nearly equal to that of the bulk material.

  12. NiCo-lead zirconium titanate-NiCo trilayered magnetoelectric composites prepared by electroless deposition

    International Nuclear Information System (INIS)

    Zhou, M. H.; Wang, Y. G.; Bi, K.; Fan, H. P.; Zhao, Z. S.

    2015-01-01

    The NiCo layers with various Ni/Co atomic ratio have been successfully electroless deposited on PZT layers by varying the bath composition. As the cobalt atomic ratio in the deposited layer increases from 17.2 to 54.8 wt%, the magnetostrictive coefficient decreases. The magnetoelectric effect depends strongly on the magnetostrictive properties of magnetostrictive phase. The magnetoelectric coefficient of NiCo/PZT/NiCo trilayers increases with Ni/Co atomic ratio of the deposited NiCo layers increasing from 45:55 to 83:17. A maximum ME voltage coefficient of α E,31 = 2.8 V ⋅ cm −1 ⋅ Oe −1 is obtained at a frequency of about 88 kHz, which makes these trilayers suitable for applications in actuators, transducers and sensors

  13. Double layer films based on TiO{sub 2} and NiO{sub x} for gas detection

    Energy Technology Data Exchange (ETDEWEB)

    Kosc, I., E-mail: ivan.kosc@stuba.sk [Institute of Electronics and Photonics, Slovak University of Technology, Bratislava (Slovakia); Hotovy, I. [Institute of Electronics and Photonics, Slovak University of Technology, Bratislava (Slovakia); Roch, T.; Plecenik, T.; Gregor, M. [Faculty of Mathematics, Physics and Informatics, Comenius University, Bratislava (Slovakia); Predanocy, M. [Institute of Electronics and Photonics, Slovak University of Technology, Bratislava (Slovakia); Cehlarova, M.; Kus, P.; Plecenik, A. [Faculty of Mathematics, Physics and Informatics, Comenius University, Bratislava (Slovakia)

    2014-09-01

    Highlights: • Double layer films based on TiO{sub 2} and NiO{sub x} for gas detection were studied. • Structural, compositional and morphological properties were investigated. • XPS spectra of TiO{sub 2} and NiO{sub x} were identified. • P- and n-type of response to hydrogen were presented. • Inversion of conductivity response type was confirmed. - Abstract: Double layer films based on TiO{sub 2} and NiO{sub x} for gas detection were studied. Two layouts with opposite position of functional films were deposited via DC magnetron sputtering method and annealed at 600 °C. The compositional, structural, morphological, electrical and gas sensing parameters were investigated. The depth profiles and the chemical state of the thin films elements were explored by X-ray photoelectron spectroscopy (XPS). Differences between the surface and subsurface NiO{sub x} were confirmed. In this way the formation of surface oxides and subsurface metallic Ni were observed. The structural changes and polycrystalline character were noticed by X-ray diffraction (XRD). The atomic force microscopy (AFM) revealed nanocrystalline character of the examined surfaces (both layouts). Different position of TiO{sub 2} and NiO{sub x} functional films brought difference in the type of response to reducing gas. Moreover, inversion of response type due to different H{sub 2} concentrations was confirmed.

  14. Structural, vibrational and morphological properties of layered double hydroxides containing Ni2+, Zn2+, Al3+ and Zr4+ cations

    International Nuclear Information System (INIS)

    Bezerra, Débora M.; Rodrigues, João E.F.S.; Assaf, Elisabete M.

    2017-01-01

    Layered double hydroxides are anionic clays with formula [M II 1−x M III x (OH) 2 ] q+ [A n− ] q/n ·mH 2 O, finding possible uses as catalyst support, adsorbents and so on. In this paper, we address the phase formation of layered double hydroxides containing Ni 2+ , Zn 2+ , Al 3+ and Zr 4+ cations, namely, NiZn-Al, NiZn-AlZr and NiZn-Zr compositions obtained by the coprecipitation method. Such systems were characterized by X-ray diffraction, confirming the phase formation for NiZn-Al and NiZn-AlZr samples. Infrared and Raman spectroscopies elucidated the anion and water molecules occurrence in the interlayer. Nitrogen physisorption (BET method) determined the presence of pores and specific surface area. The isotherm shapes were Type IV, according to the IUPAC, and represent a mesoporous structure. A morphological study was performed by means of scanning and transmission electron microscopies, and particle size values of 120, 131 and 235 nm for NiZn-Al, NiZn-AlZr and NiZn-Zr, respectively, were determined. Thermogravimetric analysis of the decomposition of the systems revealed that their complete disintegration occurred at ~ 450 °C and resulted in mixed oxides.

  15. Deformation-phase transformation coupling mechanism of white layer formation in high speed machining of FGH95 Ni-based superalloy

    Energy Technology Data Exchange (ETDEWEB)

    Du, Jin [School of Mechanical and Automotive Engineering, Qilu University of Technology, Jinan, Shandong 250353 (China); Liu, Zhanqiang, E-mail: melius@sdu.edu.cn [School of Mechanical Engineering, Shandong University, Jinan, Shandong 250061 (China); Key Laboratory of High Efficiency and Clean Mechanical Manufacture, Shandong University, Ministry of Education, Shandong (China); Lv, Shaoyu [School of Mechanical Engineering, Shandong University, Jinan, Shandong 250061 (China)

    2014-02-15

    Ni-based superalloy represents a significant metal portion of the aircraft critical structural and engine components. When these critical structural components in aerospace industry are manufactured with the objective to reach high reliability levels and excellent service performance, surface integrity is one of the most relevant parameter used for evaluating the quality of finish machined surfaces. In the study of surface integrity, the formation white layer is a very important research topic. The formation of white layer on the Ni-based superalloy machined surface will reduce the machined parts service performance and fatigue life. This paper was conducted to determine the effects of cutting speed on white layer formation in high speed machining of FGH95 Ni-based superalloy. Optical microscope, scanning electron microscope and X-ray diffraction were employed to analyze the elements and microstructures of white layer and bulk materials. The statistical analysis for grain numbers was executed to study the influence of cutting speed on the grain refinement in the machined surface. The investigation results showed that white layer exhibits significantly different microstructures with the bulk materials. It shows densification, no obvious structural features characteristic. The microstructure and phase of Ni-based solid solution changed during cutting process. The increase of cutting speed causes the increase of white layer thickness when the cutting speed is less than 2000 m/min. However, white layer thickness reduces with the cutting speed further increase. The higher the cutting speed, the more serious grains refinement in machined surface. 2-D FEM for machining FGH95 were carried out to simulate the cutting process and obtained the cutting temperature field, cutting strain field and strain rate field. The impact mechanisms of cutting temperature, cutting strain and strain rates on white layer formation were analyzed. At last, deformation-phase transformation

  16. Anodized porous titanium coated with Ni-CeO{sub 2} deposits for enhancing surface toughness and wear resistance

    Energy Technology Data Exchange (ETDEWEB)

    Zhou, Xiaowei, E-mail: zhouxiaowei901@163.com; Ouyang, Chun

    2017-05-31

    Highlights: • Structural design of anodized nanoporous Ti was introduced for bonding pinholes to achieve a metallurgical bonding interface. • Anodized porous Ti substrate was activated by electroless Ni-P film to be acted as transitional layer to deposit Ni-CeO{sub 2} nanocomposite coatings. • An analytical model was validated for predicting the Ce-rich worn products as a self-lubricant phase for monitoring wear mechanisms. - Abstract: In order to make large improvements of surface toughness and wear resistance for pure titanium (Ti) substrate, anodic titanium oxide (ATO) surface with nanoporous structure was coated with the Ni-CeO{sub 2} nanocomposite coatings. Regarding TiO{sub 2} barrier layer on Ti surface to inhibit its electrochemical activity, pre-treatments were successively processed with anodizing, sensitizing, activating, and then followed by electroless Ni-P film to be acted as an activated layer for electroplating Ni-CeO{sub 2} deposits. The existing Pd atoms around ATO nanopores were expected as the heterogeneous nucleation sites for supporting the growing locations of electroless Ni-P film. The innovative of interface design using porous structure was introduced for bonding pinholes to achieve a metallurgical adhesion interface between Ti substrate and surface coatings. Besides the objectives of this work were to elucidate how effects by the adding CeO{sub 2} nanoparticles on modifying microstructures and wear mechanisms of Ni-CeO{sub 2} nanocomposite coatings. Many efforts of XRD, FE-SEM, TEM and Nanoindentation tests were devoted to comparing different wear behaviors of Ni-CeO{sub 2} coatings relative to pure nickel. Results indicated that uniform-distributed Ti nanopores with an average diameter size of ∼200 nm was achieved using the Phosphate-type anodizing solution at DC 150 V. A worn surface without fatigue cracks was observed for TAO surface coated with Ni-CeO{sub 2} deposits, showing the existing Ce-rich worn products to be acted as a

  17. Process for the manufacture of adhering NbC layers on components consisting of NiCr alloys

    International Nuclear Information System (INIS)

    Kleemann, W.

    1985-01-01

    The invention concerns a process for the manufacture of adhering NbC layers on Ni Cr alloys, whose adhesion is guaranteed in a helium atmosphere even at high temperatures (≥ 950 0 C). Differing from the conventional process in which such layers are applied by thermal spraying, and which does not provide layers adhering at high temperatures, the NbC layers are formed in situ, by applying a niobium layer on the components to be coated and by subsequent carburisation of the niobium layer by means of existing CH 4 impurities in the helium atmosphere. (orig.) [de

  18. New type ternary NiAlCe layered double hydroxide photocatalyst for efficient visible-light photoreduction of CO2 into CH4

    Science.gov (United States)

    Li, Ji; (Bill Yang, Y. J.

    2018-02-01

    New type of ternary NiAlCe layered double hydroxide photocatalyst was synthesized by a simple hydrothermal reaction. The obtained photocatalyst shows efficient visible-light activity for CO2 reduction to CH4. We have investigated the optimal Ce content in the catalyst and analyzed the mechanism by materials characterization. Additionally, a novel alkali etching method was used to construct the porous structure. The effect of the porosity and morphologies on the activity is investigated. It is found that the ternary NiAlCe layered double hydroxide photocatalyst with porosity showing the best photocatalytic activity among all the samples. Based on the characterization and first principle calculation, the detailed photocatalytic mechanism of the ternary NiAlCe layered double hydroxide photocatalyst is deduced.

  19. Electroless Ni-P/Ni-B duplex coatings: preparation and evaluation of microhardness, wear and corrosion resistance

    International Nuclear Information System (INIS)

    Narayanan, T.S.N. Sankara; Krishnaveni, K.; Seshadri, S.K.

    2003-01-01

    The present work deals with the formation of Ni-P/Ni-B duplex coatings by electroless plating process and evaluation of their hardness, wear resistance and corrosion resistance. The Ni-P/Ni-B duplex coatings were prepared using dual baths (acidic hypophosphite- and alkaline borohydride-reduced electroless nickel baths) with both Ni-P and Ni-B as inner layers and with varying single layer thickness. Scanning electron microscopy (SEM) was used to assess the duplex interface. The microhardness, wear resistance and corrosion resistance of electroless nickel duplex coatings were compared with electroless Ni-P and Ni-B coatings of similar thickness. The study reveals that the Ni-P and Ni-B coatings are amorphous in their as-plated condition and upon heat-treatment at 450 deg. C for 1 h, both Ni-P and Ni-B coatings crystallize and produce nickel, nickel phosphide and nickel borides in the respective coatings. All the three phases are formed when Ni-P/Ni-B and Ni-B/Ni-P duplex coatings are heat-treated at 450 deg. C for 1 h. The duplex coatings are uniform and the compatibility between the layers is good. The microhardness, wear resistance and corrosion resistance of the duplex coating is higher than Ni-P and Ni-B coatings of similar thickness. Among the two types of duplex coatings studied, hardness and wear resistance is higher for coatings having Ni-B coating as the outer layer whereas better corrosion resistance is offered by coatings having Ni-P coating as the outer layer

  20. NiCo-lead zirconium titanate-NiCo trilayered magnetoelectric composites prepared by electroless deposition

    Energy Technology Data Exchange (ETDEWEB)

    Zhou, M. H.; Wang, Y. G.; Bi, K., E-mail: bike@bupt.edu.cn [State Key Laboratory of Information Photonics and Optical Communications and School of Science, Beijing University of Posts and Telecommunications, Beijing 100876 (China); Fan, H. P. [School of Mechanical and Electrical Engineering, Qingdao Technological University Qindao College, Qingdao 266106 (China); Zhao, Z. S. [Shandong Engineering Consulting Institute, Jinan 250013 (China)

    2015-04-15

    The NiCo layers with various Ni/Co atomic ratio have been successfully electroless deposited on PZT layers by varying the bath composition. As the cobalt atomic ratio in the deposited layer increases from 17.2 to 54.8 wt%, the magnetostrictive coefficient decreases. The magnetoelectric effect depends strongly on the magnetostrictive properties of magnetostrictive phase. The magnetoelectric coefficient of NiCo/PZT/NiCo trilayers increases with Ni/Co atomic ratio of the deposited NiCo layers increasing from 45:55 to 83:17. A maximum ME voltage coefficient of α{sub E,31} = 2.8 V ⋅ cm{sup −1} ⋅ Oe{sup −1} is obtained at a frequency of about 88 kHz, which makes these trilayers suitable for applications in actuators, transducers and sensors.

  1. Improved conductivity of infinite-layer LaNiO2 thin films by metal organic decomposition

    Science.gov (United States)

    Ikeda, Ai; Manabe, Takaaki; Naito, Michio

    2013-12-01

    Infinite-layer LaNiO2 thin films were synthesized by metal organic decomposition and subsequent topotactic reduction in hydrogen, and their transport properties were investigated. LaNiO2 is isostructural to SrCuO2, the parent compound of high-Tc Sr0.9La0.1CuO2 with Tc = 44 K, and has 3d9 configuration, which is very rare in oxides but common to high-Tc copper oxides. The bulk synthesis of LaNiO2 is not easy, but we demonstrate in this article that the thin-film synthesis of LaNiO2 is rather easy, thanks to a large-surface-to-volume ratio, which makes oxygen diffusion prompt. Our refined synthesis conditions produced highly conducting films of LaNiO2. The resistivity of the best film is as low as 640 μΩ cm at 295 K and decreases with temperature down to 230 K but it shows a gradual upturn at lower temperatures.

  2. Atomic Resolution Structural and Chemical Imaging Revealing the Sequential Migration of Ni, Co, and Mn upon the Battery Cycling of Layered Cathode

    Energy Technology Data Exchange (ETDEWEB)

    Yan, Pengfei; Zheng, Jianming; Zhang, Ji-Guang; Wang, Chongmin

    2017-05-11

    Layered lithium transition metal oxides (LTMO) are promising candidate cathode materials for next generation high energy density lithium ion battery. The challenge for using this category of cathode is the capacity and voltage fading, which is believed to be associated with the layered structure disordering, a process that is initiated from the surface or solid-electrolyte interface and facilitated by transition metal (TM) reduction and oxygen vacancy formation. However, the atomic level dynamic mechanism of such a layered structure disordering is still not fully clear. In this work, utilizing atomic resolution electron energy loss spectroscopy (EELS), we map, for the first time at atomic scale, the spatial evolution of Ni, Co and Mn in a cycled LiNi1/3M1/3Co1/3O2 layered cathode. In combination with atomic level structural imaging, we discovered the direct correlation of TM ions migration behavior with lattice disordering, featuring the residing of TM ions in the tetrahedral site and a sequential migration of Ni, Co, and Mn upon the increased lattice disordering of the layered structure. This work highlights that Ni ions, though acting as the dominant redox species in many LTMO, are labile to migrate to cause lattice disordering upon battery cycling; while the Mn ions are more stable as compared with Ni and Co and can act as pillar to stabilize layered structure. Direct visualization of the behavior of TM ions during the battery cycling provides insight for designing of cathode with structural stability and correspondingly a superior performance.

  3. Improved efficiency of NiOx-based p-i-n perovskite solar cells by using PTEG-1 as electron transport layer

    Science.gov (United States)

    Groeneveld, Bart G. H. M.; Najafi, Mehrdad; Steensma, Bauke; Adjokatse, Sampson; Fang, Hong-Hua; Jahani, Fatemeh; Qiu, Li; ten Brink, Gert H.; Hummelen, Jan C.; Loi, Maria Antonietta

    2017-07-01

    We present efficient p-i-n type perovskite solar cells using NiOx as the hole transport layer and a fulleropyrrolidine with a triethylene glycol monoethyl ether side chain (PTEG-1) as electron transport layer. This electron transport layer leads to higher power conversion efficiencies compared to perovskite solar cells with PCBM (phenyl-C61-butyric acid methyl ester). The improved performance of PTEG-1 devices is attributed to the reduced trap-assisted recombination and improved charge extraction in these solar cells, as determined by light intensity dependence and photoluminescence measurements. Through optimization of the hole and electron transport layers, the power conversion efficiency of the NiOx/perovskite/PTEG-1 solar cells was increased up to 16.1%.

  4. Efficient carbon dots/NiFe-layered double hydroxide/BiVO4 photoanodes for photoelectrochemical water splitting

    Science.gov (United States)

    Lv, Xiaowei; Xiao, Xin; Cao, Minglei; Bu, Yi; Wang, Chuanqing; Wang, Mingkui; Shen, Yan

    2018-05-01

    Modification of semiconductor photoanodes with oxygen evolution catalyst (OEC) is an effective approach for improving photoelectrochemical (PEC) water splitting efficiency. In the configuration, how to increase the activity of OEC is crucial to further improve PEC performance. Herein, a ternary photoanode system was designed to enhance PEC efficiency of photoelectrodes through introducing carbon dots (CDs), NiFe-layered double hydroxide (NiFe-LDH) nanosheets on BiVO4 particles. Systematic research shows that NiFe-LDH serves as an OEC which accelerates oxygen evolution kinetics, while the introduction of CDs can further reduce charge transfer resistance and overpotential for oxygen evolution. Under the synergistic effect of NiFe-LDH and CDs, the photocurrent and incident photon to current conversion efficiency (IPCE) of the resulting CDs/NiFe-LDH/BiVO4 photoanode is improved significantly than those of the NiFe-LDH/BiVO4 electrode. Consequently, such a ternary heterostructure could be an alternative way to further enhance PEC water splitting performance.

  5. Flexural strength of pure Ti, Ni-Cr and Co-Cr alloys submitted to Nd:YAG laser or TIG welding.

    Science.gov (United States)

    Rocha, Rick; Pinheiro, Antônio Luiz Barbosa; Villaverde, Antonio Balbin

    2006-01-01

    Welding of metals and alloys is important to Dentistry for fabrication of dental prostheses. Several methods of soldering metals and alloys are currently used. The purpose of this study was to assess, using the flexural strength testing, the efficacy of two processes Nd:YAG laser and TIG (tungsten inert gas) for welding of pure Ti, Co-Cr and Ni-Cr alloys. Sixty cylindrical specimens were prepared (20 of each material), bisected and welded using different techniques. Four groups were formed (n=15). I: Nd:YAG laser welding; II- Nd:YAG laser welding using a filling material; III- TIG welding and IV (control): no welding (intact specimens). The specimens were tested in flexural strength and the results were analyzed statistically by one-way ANOVA. There was significant differences (pTIG and laser welding and also between laser alone and laser plus filling material. In conclusion, TIG welding yielded higher flexural strength means than Nd:YAG laser welding for the tested Ti, Co-Cr and Ni-Cr alloys.

  6. The large magnetoelectric effect in Ni-lead zirconium titanate-Ni trilayers derived by electroless deposition

    International Nuclear Information System (INIS)

    Bi, K; Wang, Y G; Wu, W; Pan, D A

    2010-01-01

    Magnetoelectric (ME) Ni-lead zirconium titanate-Ni trilayers with neither electrodes nor bonding layers have been derived by electroless deposition. The structure and magnetic properties of the electroless deposited Ni layers with different pH values are characterized by x-ray diffraction and vibrating sample magnetometer. The influence of the bias magnetic field and the magnetic field frequency (f) on ME coupling is discussed. It is seen that α E,31 depends strongly on H dc and f. The value of the ME coefficient increases as the thickness of the Ni layer and the pH of the bath increase. A maximum of the ME voltage coefficient α E,31 = 5.77 V cm -1 Oe -1 at resonance frequency with a deposited Ni layer thickness t Ni = 302 μm is obtained. The large ME coefficient makes these Ni-PZT-Ni trilayers suitable for applications in sensors, actuators and transducers. (fast track communication)

  7. General access to metal oxide (Metal = Mn, Co, Ni) double-layer nanospheres for application in lithium ion batteries and supercapacitors

    International Nuclear Information System (INIS)

    Xia, Yuan; Wang, Gang; Zhang, Xing; Wang, Beibei; Wang, Hui

    2016-01-01

    Highlights: • A series of metal oxide double layer nanospheres were prepared. • The obtained materials show excellent performances in lithium ion batteries and supercapacitors. • The unique structure of double layers is beneficial for superior electrochemical performances. - Abstract: In this work, a series of metal oxide double-layer nanospheres (DLNs), such as Mn 2 O 3 , Co 3 O 4 , NiO, NiCo 2 O 4 , and MnCo 2 O 4 have been successfully synthesized through a general template method. The layers of nanospheres were assembled by different nanostructure units and the removing of the SiO 2 template formed a void of several ten nanometers between the double layers, resulting large specific surface areas for them. The energy storage performances of the as-prepared double-layer nanospheres were further investigated in lithium ion battery and supercapacitor systems. Based on their unique nanostructures, the double-layer nanospheres exhibit excellent electrochemical performance with long cycle stability and high specific capacities or capacitances. The best of these, DLNs-NiCo 2 O 4 can deliver a reversible capacity of 1107 mAh g −1 at 0.25C after 200 cycles in lithium ion battery system, and shows a capacitance of 1088 F g −1 with capacitance loss of less than 3% at 5 A g −1 after 5000 cycles in supercapacitors.

  8. NiMn layered double hydroxide nanosheets/NiCo2O4 nanowires with surface rich high valence state metal oxide as an efficient electrocatalyst for oxygen evolution reaction

    Science.gov (United States)

    Yang, Liting; Chen, Lin; Yang, Dawen; Yu, Xu; Xue, Huaiguo; Feng, Ligang

    2018-07-01

    High valence transition metal oxide is significant for anode catalyst of proton membrane water electrolysis technique. Herein, we demonstrate NiMn layered double hydroxide nanosheets/NiCo2O4 nanowires hierarchical nanocomposite catalyst with surface rich high valence metal oxide as an efficient catalyst for oxygen evolution reaction. A low overpotential of 310 mV is needed to drive a 10 mA cm-2 with a Tafel slope of 99 mV dec-1, and a remarkable stability during 8 h is demonstrated in a chronoamperometry test. Theoretical calculation displays the change in the rate-determining step on the nanocomposite electrode in comparison to NiCo2O4 nanowires alone. It is found high valence Ni and Mn oxide in the catalyst system can efficiently facilitate the charge transport across the electrode/electrolyte interface. The enhanced electrical conductivity, more accessible active sites and synergistic effects between NiMn layered double hydroxide nanosheets and NiCo2O4 nanowires can account for the excellent oxygen evolution reaction. The catalytic performance is comparable to most of the best non-noble catalysts and IrO2 noble catalyst, indicating the promising applications in water-splitting technology. It is an important step in the development of hierarchical nanocomposites by surface valence state tuning as an alternative to noble metals for oxygen evolution reaction.

  9. Optimum conditions for intercalation of lacunary tungstophosphate(V) anions into layered Ni(II)-Zn(II) hydroxyacetate

    International Nuclear Information System (INIS)

    Ballesteros, M. Angeles; Ulibarri, M. Angeles; Rives, Vicente; Barriga, Cristobalina

    2008-01-01

    Acetate containing nickel-zinc hydroxysalts (LHS-Ni-Zn) have been synthesized by coprecipitation and hydrothermal treatment. The acetate anions were exchanged with PW 12 O 40 3- anions, and optimum conditions to attain the maximum level of W in the compound have been identified. The W intercalated compound was characterized by powder X-ray diffraction, FT-IR spectroscopy, thermogravimetric and differential thermal analyses, scanning electron microscopy and transmission electron microscopy. The exchange of LHS-Ni-Zn with PW 12 O 40 3- at pH=3 for 72 h leads to a solid with a basal spacing of 9.62 A and a W content (weight) of 37%. The hydrothermal treatment at 90 deg. C for 24 h increases this value to 48% with a W/Zn molar ratio of 1.38, which corresponds to a layered compound with lacunary tungstophosphate anions in the interlayer space. The intercalated solid is stable up to 250 deg. C, the layer structure collapses on dehydroxylation and amorphous compounds were identified at 500 deg. C. Two crystalline phases, NiO (rock salt) and a solid solution (Zn 1-x Ni x )WO 4 , were identified by powder X-ray diffraction at high temperature (ca. 1000 deg. C). - Graphical abstract: Optimum conditions for intercalation of Keggin-type anions in Ni, Zn hydroxysalts have been identified. Lacunary species are formed via partial depolymerization of the starting anion. The thermal decomposition of the intercalated phases has been also studied

  10. Indirect optical crosstalk reduction by highly-doped backside layer in PureB single-photon avalanche diode arrays

    NARCIS (Netherlands)

    Osrečki, Željko; Knežević, Tihomir; Nanver, Lis K.; Suligoj, Tomislav

    2017-01-01

    A method of reducing indirect optical crosstalk in a PureB single-photon avalanche diode (SPAD) array is investigated by TCAD simulations. The reduction is accomplished by taking advantage of the enhanced optical absorption of a highly-doped Si layer (p-type, 3×1020 cm-3) on the backside of the

  11. Densities of molten Ni-(Cr, Co, W) superalloys

    Institute of Scientific and Technical Information of China (English)

    XIAO Feng; YANG Ren-hui; FANG Liang; LIU Lan-xiao; ZHAO Hong-kai

    2008-01-01

    In order to obtain more accurate density for molten Ni-(Cr, Co, W) binary alloy, the densities of molten pure Ni and Ni-Cr, Ni-Co, Ni-W alloys were measured with a sessile drop method. It is found that the measured densities of molten pure Ni and Ni-Cr, Ni-Co, Ni-W alloys decrease with increasing temperature in the experimental temperature range. The density of alloys increases with increasing W and Co concentrations while it decreases with increasing Cr concentration in the alloy at 1 773-1 873 K. The molar volume of Ni-based alloys increases with increasing W concentration while it decreases with increasing Co concentration. The effect of Cr concentration on the molar volume of the alloy is little in the studied concentration range. The accommodation among atomic species was analyzed. The deviation of molar volume from ideal mixing shows an ideal mixing of Ni-(Cr, Co, W) binary alloys.

  12. Microstructure and mechanical properties of sputter deposited Ni/Ni{sub 3}Al multilayer films at elevated temperature

    Energy Technology Data Exchange (ETDEWEB)

    Zhang, Chao [Shanghai Key Laboratory of Materials Laser Processing and Modification, School of Materials Science and Engineering, Shanghai Jiao Tong University, Shanghai 200240 (China); Collaborative Innovation Center for Advanced Ship and Deep-Sea Exploration, Shanghai 200240 (China); Feng, Kai, E-mail: fengkai@sjtu.edu.cn [Shanghai Key Laboratory of Materials Laser Processing and Modification, School of Materials Science and Engineering, Shanghai Jiao Tong University, Shanghai 200240 (China); Collaborative Innovation Center for Advanced Ship and Deep-Sea Exploration, Shanghai 200240 (China); Li, Zhuguo, E-mail: lizg@sjtu.edu.cn [Shanghai Key Laboratory of Materials Laser Processing and Modification, School of Materials Science and Engineering, Shanghai Jiao Tong University, Shanghai 200240 (China); Collaborative Innovation Center for Advanced Ship and Deep-Sea Exploration, Shanghai 200240 (China); Lu, Fenggui; Huang, Jian; Wu, Yixiong [Shanghai Key Laboratory of Materials Laser Processing and Modification, School of Materials Science and Engineering, Shanghai Jiao Tong University, Shanghai 200240 (China); Collaborative Innovation Center for Advanced Ship and Deep-Sea Exploration, Shanghai 200240 (China)

    2016-08-15

    Highlights: • Ni/Ni{sub 3}Al multilayers are prepared by magnetron sputtering. • Both grain size and phase constitution of annealed Ni/Ni{sub 3}Al multilayers are dependent on individual layer thickness. • The hardness of annealed Ni/Ni{sub 3}Al multilayers varies with individual layer thickness and annealing temperature. • 40 nm Ni/Ni{sub 3}Al multilayer exhibits excellent hardness at elevated temperature. - Abstract: Nano-structured Ni/Ni{sub 3}Al multilayer was prepared by magnetron sputtering, with individual layer thicknesses h varying from 10 to 160 nm. The microstructure and hardness of Ni/Ni{sub 3}Al multilayer were investigated by X-ray diffraction, transmission electron microscopy and nanoindentation. The results show that the hardness increases with decreasing h for as-deposited and 500 °C annealed multilayers. When annealed at 700 °C, the hardness approach a peak value at h = 40 nm with followed by softening at smaller h. The influence of individual layer thickness, grain size as well as formation of ordered Ni{sub 3}Al on strengthening mechanisms of Ni/Ni{sub 3}Al multilayers at elevated temperature are discussed.

  13. Controlled carrier screening in p-n NiO/GaN piezoelectric generators by an Al2O3 insertion layer

    Science.gov (United States)

    Johar, Muhammad Ali; Jeong, Dae Kyung; Afifi Hassan, Mostafa; Kang, Jin-Ho; Ha, Jun-Seok; Key Lee, June; Ryu, Sang-Wan

    2017-12-01

    The performance of a piezoelectric generator (PG) depends significantly on the internal screening process inside the device. As piezoelectric charges appear on both ends of the piezoelectric crystal, internal screening starts to decrease the piezoelectric bias. Therefore, the piezoelectric energy generated by external stress is not fully utilized by external circuit, which is the most challenging aspect of high-efficiency PGs. In this work, the internal screening effect of a NiO/GaN p-n PG was analyzed and controlled with an Al2O3 insertion layer. Internal screening in the p-n diode PG was categorized into free-carrier screening in neutral regions and junction screening due to charge drift across the junction. It was observed that junction screening could be significantly suppressed by inserting an Al2O3 layer and that effect was dominant in a leaky diode PG. With this implementation, the piezoelectric bias of the NiO/GaN PG was improved by a factor of ~100 for high-leakage diodes and a factor of ~1.6 for low-leakage diodes. Consequently, NiO/Al2O3/GaN PGs under a stress of 5 MPa provided a piezoelectric bias of 12.1 V and a current density of 2.25 µA cm-2. The incorporation of a highly resistive Al2O3 layer between p-NiO and n-GaN layers in NiO/GaN heterojunctions provides an efficient means of improving the piezoelectric performance by controlling the internal screening of the piezoelectric field.

  14. Moessbauer and XRD study of pulse plated Fe-P and Fe-Ni thin layers

    International Nuclear Information System (INIS)

    Miko, Annamaria; Kuzmann, Erno; Lakatos-Varsanyi, Magda; Kakay, Attila; Nagy, Ferenc; Varga, Lajos Karoly

    2005-01-01

    57 Fe conversion electron Moessbauer spectroscopy, X-ray diffraction, electrochemical and magnetic measurements were used to study pulse electroplated Fe-P and Ni-Fe coatings. XRD and 57 Fe CEMS measurements revealed the amorphous character of the novel pulse plated Fe-P alloys. CEM spectra indicated significant differences in the short range order and in the magnetic anisotropy between the Fe-P deposits pulse plated at medium long deposition time (t on = 2 ms), with short relaxation time (t off = 9 ms) and low current density (I p = 0.05 Acm -2 ) or at short deposition time (t on = 1 ms) with long relaxation time (t off = 250 ms) and high current density (I p = 1.0 Acm -2 ). The broad peaks centred around the fcc reflections in XRD of the pulse plated Ni-22 wt.% Fe deposit reflected a microcrystalline Ni-Fe alloy with a very fine, 5-8 nm, grain size. The CEM spectrum of the pulse plated Ni-22 wt.% Fe coating corresponded to a highly disordered solid solution alloy containing a minute amount of ferrihydrite. Extreme favourable soft magnetic properties were observed with these Ni-Fe and Fe-P pulse plated thin layers.

  15. Room-temperature synthesis of three-dimensional porous ZnO@CuNi hybrid magnetic layers with photoluminescent and photocatalytic properties

    Science.gov (United States)

    Guerrero, Miguel; Zhang, Jin; Altube, Ainhoa; García-Lecina, Eva; Roldan, Mònica; Baró, Maria Dolors; Pellicer, Eva; Sort, Jordi

    2016-01-01

    Abstract A facile synthetic approach to prepare porous ZnO@CuNi hybrid films is presented. Initially, magnetic CuNi porous layers (consisting of phase separated CuNi alloys) are successfully grown by electrodeposition at different current densities using H2 bubbles as a dynamic template to generate the porosity. The porous CuNi alloys serve as parent scaffolds to be subsequently filled with a solution containing ZnO nanoparticles previously synthesized by sol-gel. The dispersed nanoparticles are deposited dropwise onto the CuNi frameworks and the solvent is left to evaporate while the nanoparticles impregnate the interior of the pores, rendering ZnO-coated CuNi 3D porous structures. No thermal annealing is required to obtain the porous films. The synthesized hybrid porous layers exhibit an interesting combination of tunable ferromagnetic and photoluminescent properties. In addition, the aqueous photocatalytic activity of the composite is studied under UV−visible light irradiation for the degradation of Rhodamine B. The proposed method represents a fast and inexpensive approach towards the implementation of devices based on metal-semiconductor porous systems, avoiding the use of post-synthesis heat treatment steps which could cause deleterious oxidation of the metallic counterpart, as well as collapse of the porous structure and loss of the ferromagnetic properties. PMID:27877868

  16. First-principles calculations for the elastic properties of Ni-base model superalloys: Ni/Ni3Al multilayers

    International Nuclear Information System (INIS)

    Yun-Jiang, Wang; Chong-Yu, Wang

    2009-01-01

    A model system consisting of Ni[001](100)/Ni 3 Al[001](100) multi-layers are studied using the density functional theory in order to explore the elastic properties of single crystal Ni-based superalloys. Simulation results are consistent with the experimental observation that rafted Ni-base superalloys virtually possess a cubic symmetry. The convergence of the elastic properties with respect to the thickness of the multilayers are tested by a series of multilayers from 2γ'+2γ to 10γ'+10γ atomic layers. The elastic properties are found to vary little with the increase of the multilayer's thickness. A Ni/Ni 3 Al multilayer with 10γ'+10γ atomic layers (3.54 nm) can be used to simulate the mechanical properties of Ni-base model superalloys. Our calculated elastic constants, bulk modulus, orientation-dependent shear modulus and Young's modulus, as well as the Zener anisotropy factor are all compatible with the measured results of Ni-base model superalloys R1 and the advanced commercial superalloys TMS-26, CMSX-4 at a low temperature. The mechanical properties as a function of the γ' phase volume fraction are calculated by varying the proportion of the γ and γ' phase in the multilayers. Besides, the mechanical properties of two-phase Ni/Ni 3 Al multilayer can be well predicted by the Voigt–Reuss–Hill rule of mixtures. (classical areas of phenomenology)

  17. One-step facile synthesis of Ni2P/C as cathode material for Ni/Zn aqueous secondary battery

    Science.gov (United States)

    Li, JiLan; Chen, ChangGuo

    2018-01-01

    Nickel phosphides/carbon(Ni2P/C) composites have been successfully synthesized via a simple one-pot hydrothermal method using glucose as carbon source for the first time. By contrast, the pure Ni2P was prepared under the same conditions without glucose. The results show that glucose not only provide the carbon source, but also prevent the aggregation of Ni2P particles. The as-obtained Ni2P/C composites and pure Ni2P were used as cathode material for alkaline Ni/Zn battery. Owing to unique Ni2P/C composites and loose, Ultra thin flower-like shape the synthesized Ni2P/C material delivers high capacity of 176 mAh g-1 at 1 A g-1 and 82 mAh g-1 at 5 A g-1 current density in Ni2P/C-Zn battery. Moreover, it shows a good cycling life that capacity fading only about 6.2% after 1500 cycles. All of these indicate that the prepared Ni2P/C composites may be a new promising cathode material for Ni-Zn rechargeable battery.

  18. Melt layer erosion of pure and lanthanum doped tungsten under VDE-like high heat flux loads

    Science.gov (United States)

    Yuan, Y.; Greuner, H.; Böswirth, B.; Luo, G.-N.; Fu, B. Q.; Xu, H. Y.; Liu, W.

    2013-07-01

    Heat loads expected for VDEs in ITER were applied in the neutral beam facility GLADIS at IPP Garching. Several ˜3 mm thick rolled pure W and W-1 wt% La2O3 plates were exposed to pulsed hydrogen beams with a central heat flux of 23 MW/m2 for 1.5-1.8 s. The melting thresholds are determined, and melt layer motion as well as material structure evolutions are shown. The melting thresholds of the two W grades are very close in this experimental setup. Lots of big bubbles with diameters from several μm to several 10 μm in the re-solidified layer of W were observed and they spread deeper with increasing heat flux. However, for W-1 wt% La2O3, no big bubbles were found in the corrugated melt layer. The underlying mechanisms referred to the melt layer motion and bubble issues are tentatively discussed based on comparison of the erosion characteristics between the two W grades.

  19. Ni-Al phase transformation of dual layer coating prepared by pack cementation and electrodeposition

    Science.gov (United States)

    Afandi, A.; Sugiarti, E.; Ekaputra, R.; Sudiro, T.; Thosin, K. A. Z.

    2018-03-01

    In this work, Fe-Cr alloys were coated via Aluminum (Al) pack cementation, followed by Nickel (Ni) electrodeposition. The process of pack cementation was done with mixing powders of Al, Al203 and NH4Cl with weight percentage of 15%, 85%, and 5% respectively. To control successful Al diffusion to the substrate, pack cementation was conducted for 7 hours with two holding temperatures treatment at 400 °C for 4 hours, and 800 ° C hours for 2 hours. Subsequently, the electrodeposition of Ni was applied with the solution consisting of NiSO4, H3BO3, and NiCl2. The samples were placed in the cathode, and then dipped in the solutions, while Ni plate used as anode. Successfully the samples were coated by dual Al-Ni layers, the samples were slowly heat treated at 900 °C for 10 hours. The inter-diffusion of Al and Ni were characterized with SEM/EDX to investigate the distribution of the elements. Mechanical properties of the coated substrates were analyzed with Hardness Vickers (HV). It was found the hardness of the substrate increased significantly, from originally 255 HV to the 1177 HV after pack cementation. The hardness of the substrates has decreased to 641 HV after Ni plating, but subsequent heat treatment has been able to increase the hardness to 842 HV. This phenomenon can be correlated to the inward Al diffusion, and outward Fe, Cr diffusion. The formation of intermetallic compounds due to Al inward and Fe, Cr outward diffusion were discussed in details.

  20. Magnetic studies on Layered solid solution Lix(Ni0.4Mn0.6)2-xO2

    Science.gov (United States)

    Nakao, K.; Nakamura, T.; Yamada, Y.; Koshiba, N.

    2011-05-01

    Lix(Ni0.4Mn0.6)2-xO2 (1.09hydroxide as raw materials. All the compounds have a layered rock-salt structure, and the cation mixing degree (Ni2+ occupancy in the Li-layer) decreases with an increase in x. From the low-temperature magnetic measurement, they all have negative Weiss temperature and spontaneous magnetization, that is, they are ferromagnetic materials. Both the Curie temperature and the spontaneous magnetization at 4.2K decrease with an increase in x. These magnetic variations are attributed to the lowering of the cation mixing degree: the magnetic interaction network turns to two-dimensional one with the loss of the inert-layer coupling. These situations may be considered semi-quantitatively using the ferromagnetic cluster model. Additionally, the cation mixing degree has an influence on their electrochemical properties such as cycle fading and rate capability.

  1. NiCo_2O_4@TiN Core-shell Electrodes through Conformal Atomic Layer Deposition for All-solid-state Supercapacitors

    International Nuclear Information System (INIS)

    Wang, Ruiqi; Xia, Chuan; Wei, Nini; Alshareef, Husam N.

    2016-01-01

    Highlights: • NiCo_2O_4 nanostructures are prepared via a simple hydrothermal method. • Outer shell of TiN is then grown through conformal atomic layer deposition. • Electrodes exhibit significantly enhanced rate capability with TiN coating. • Solid-state polymer electrolyte is employed to improve cycling stability. • Full devices show a stack power density of 58.205 mW cm"−"3 at 0.061 mWh cm"−"3. - Abstract: Ternary transition metal oxides such as NiCo_2O_4 show great potential as supercapacitor electrode materials. However, the unsatisfactory rate performance of NiCo_2O_4 may prove to be a major hurdle to its commercial usage. Herein, we report the development of NiCo_2O_4@TiN core–shell nanostructures for all-solid-state supercapacitors with significantly enhanced rate capability. We demonstrate that a thin layer of TiN conformally grown by atomic layer deposition (ALD) on NiCo_2O_4 nanofiber arrays plays a key role in improving their electrical conductivity, mechanical stability, and rate performance. Fabricated using the hybrid NiCo_2O_4@TiN electrodes, the symmetric all-solid-state supercapacitor exhibited an impressive stack power density of 58.205 mW cm"−"3 at a stack energy density of 0.061 mWh cm"−"3. To the best of our knowledge, these values are the highest of any NiCo_2O_4-based all-solid-state supercapacitor reported. Additionally, the resulting NiCo_2O_4@TiN all-solid-state device displayed outstanding cycling stability by retaining 70% of its original capacitance after 20,000 cycles at a high current density of 10 mA cm"−"2. These results illustrate the promise of ALD-assisted hybrid NiCo_2O_4@TiN electrodes within sustainable and integrated energy storage applications.

  2. Improved efficiency of NiOx-based p-i-n perovskite solar cells by using PTEG-1 as electron transport layer

    NARCIS (Netherlands)

    Groeneveld, Bart G. H. M.; Najafi, Mehrdad; Steensma, Bauke; Adjokatse, Sampson; Fang, Hong-Hua; Jahani, Fatemeh; Qiu, Li; ten Brink, Gert H.; Hummelen, Jan C.; Loi, Maria Antonietta

    We present efficient p-i-n type perovskite solar cells using NiOx as the hole transport layer and a fulleropyrrolidine with a triethylene glycol monoethyl ether side chain (PTEG-1) as electron transport layer. This electron transport layer leads to higher power conversion efficiencies compared to

  3. Cavitation resistance of surface composition "Steel-Ni-TiNi-TiNiZr-cBNCo", formed by High-Velocity Oxygen-Fuel spraying

    Science.gov (United States)

    Blednova, Zh. M.; Dmitrenko, D. V.; Balaev, E. U. O.

    2018-01-01

    The object of the study is a multilayered surface composition "Steel - a Multicomponent material with Shape Memory Effect - a wear-resistant layer" under conditions of cavitation effects in sea water. Multicomponent TiNi-based coatings with addition of alloying elements such as Zr in an amount up to 10% mass, allow to create a composite material with a gradient of properties at the interface of layers, which gives new properties to coatings and improves their performance significantly. The use of materials with shape memory effect (SME) as surface layers or in the composition of surface layered compositions allows to provide an effective reaction of materials to the influence of external factors and adaptation to external influences. The surface composite layer cBN-10%Co has high hardness and strength, which ensures its resistance to shock cyclic influences of collapsing caverns. The increased roughness of the surface of a solid surface composite in the form of strong columnar structures ensures the crushing of vacuum voids, redistributing their effect on the entire surface, and not concentrating them in certain zones. In addition, the gradient structure of the multilayer composite coating TiNi-Ti33Ni49Zr18-cBN-10%Co Co makes it possible to create conditions for the relaxation of stresses created by the variable impact load of cavitation caverns and the manifestation of compensating internal forces due to thermo-elastic martensitic transformations of SME materials. The cavitation resistance of the coating TiNi-Ti33Ni49Zr18-cBN-10%Co according to the criterion of mass wear is 15-20 times higher than that of the base material without coating and 10-12 times higher than that of the TiNi-TiNiZr coating. The proposed architecture of the multifunctional gradient composition, "steel-Ni-TiNi- Ti33Ni49Zr18-cBN-10%Co", each layer of which has its functional purpose, allows to increase the service life of parts operating under conditions of cavitation-fatigue loading in

  4. Microstructural modification of NiAl layered double hydroxide electrodes by adding graphene nanosheets and their capacitative property

    International Nuclear Information System (INIS)

    Kim, Yuna; Kim, Seok

    2015-01-01

    NiAl layered double hydroxide (LDH) composite electrodes containing various contents of graphene nanosheets (GNS) were prepared by a hydrothermal method. The microstructure and morphological properties were examined by FE-SEM, FE-TEM, XRD, and FTIR. Electrochemical analysis was also carried out by cyclic voltammetry, impedance, and cycle life measurement. The as-prepared composite that contained 500 mg of graphene (denoted as NiAl/G-50) achieved the highest specific capacitance of 1147 F/g among the various NiAl LDH/GNS composites. Besides, the NiAl LDH/GNS composite exhibited the lower diffusion resistance, improved rate capability, and good cyclic stability (83% of initial capacitance after 2000 cycles). Considering the morphological data and the improved capacitative properties together, we concluded the synthesized NiAl LDH/GNS composites would be a promising electrode material for supercapacitors

  5. Microstructural modification of NiAl layered double hydroxide electrodes by adding graphene nanosheets and their capacitative property

    Energy Technology Data Exchange (ETDEWEB)

    Kim, Yuna; Kim, Seok [School of Chemical and Biomolecular Engineering, Pusan National University, Busan (Korea, Republic of)

    2015-02-15

    NiAl layered double hydroxide (LDH) composite electrodes containing various contents of graphene nanosheets (GNS) were prepared by a hydrothermal method. The microstructure and morphological properties were examined by FE-SEM, FE-TEM, XRD, and FTIR. Electrochemical analysis was also carried out by cyclic voltammetry, impedance, and cycle life measurement. The as-prepared composite that contained 500 mg of graphene (denoted as NiAl/G-50) achieved the highest specific capacitance of 1147 F/g among the various NiAl LDH/GNS composites. Besides, the NiAl LDH/GNS composite exhibited the lower diffusion resistance, improved rate capability, and good cyclic stability (83% of initial capacitance after 2000 cycles). Considering the morphological data and the improved capacitative properties together, we concluded the synthesized NiAl LDH/GNS composites would be a promising electrode material for supercapacitors.

  6. Cathodic Electrodeposition of Ni-Mo on Semiconducting NiFe2 O4 for Photoelectrochemical Hydrogen Evolution in Alkaline Media.

    Science.gov (United States)

    Wijten, Jochem H J; Jong, Ronald P H; Mul, Guido; Weckhuysen, Bert M

    2018-04-25

    Photocathodes for hydrogen evolution from water were made by electrodeposition of Ni-Mo layers on NiFe 2 O 4 substrates, deposited by spin coating on F:SnO 2 -glass. Analysis confirmed the formation of two separate layers, without significant reduction of NiFe 2 O 4 . Bare NiFe 2 O 4 was found to be unstable under alkaline conditions during (photo)electrochemistry. To improve the stability significantly, the deposition of a bifunctional Ni-Mo layer through a facile electrodeposition process was performed and the composite electrodes showed stable operation for at least 1 h. Moreover, photocurrents up to -2.1 mA cm -2 at -0.3 V vs. RHE were obtained for Ni-Mo/NiFe 2 O 4 under ambient conditions, showing that the new combination functions as both a stabilizing and catalytic layer for the photoelectrochemical evolution of hydrogen. The photoelectrochemical response of these composite electrodes decreased with increasing NiFe 2 O 4 layer thickness. Transient absorption spectroscopy showed that the lifetime of excited states is short and on the ns timescale. An increase in lifetime was observed for NiFe 2 O 4 of large layer thickness, likely explained by decreasing the defect density in the primary layer(s), as a result of repetitive annealing at elevated temperature. The photoelectrochemical and transient absorption spectroscopy results indicated that a short charge carrier lifetime limits the performance of Ni-Mo/NiFe 2 O 4 photocathodes. © 2018 Wiley-VCH Verlag GmbH & Co. KGaA, Weinheim.

  7. Numerical analysis of the influence of buffer layer thickness on the residual stresses in YBCO/La2Zr2O7/Ni superconducting materials

    International Nuclear Information System (INIS)

    Celik, Erdal; Sayman, Onur; Karakuzu, Ramazan; Ozman, Yilmaz

    2007-01-01

    The present paper addresses a numerical investigation of the influence of buffer layer thickness on the residual stress in YBCO/La 2 Zr 2 O 7 /Ni architectured materials under cryogenic conditions by using classical lamination theory (CLT) and finite element method (FEM) for coated conductor applications. YBCO/La 2 Zr 2 O 7 multilayer films were fabricated on Ni tape substrate using reel-to-reel sol-gel and pulse laser deposition (PLD) systems. The microstructural evolution of high temperature superconducting YBCO film and buffer layers with La 2 Zr 2 O 7 configuration grown on textured Ni tape substrates was investigated by using a scanning electron microscope (SEM). Thermal stress analysis of YBCO/La 2 Zr 2 O 7 /Ni multilayer sample was performed by using CLT in the temperature range of 298-175 K in liquid helium media. The YBCO/La 2 Zr 2 O 7 /Ni sample strip was solved by using FEM for linear or nonlinear cases in the temperature range of 298-3 K in liquid helium media. SEM observations revealed that crack-free, pinhole-free, continuous superconducting film and buffer layer were obtained by sol-gel and PLD systems. In addition to microstructural observations, it was found that the largest compressive stresses and failure occur in La 2 Zr 2 O 7 buffer layer due to its smallest thermal expansion coefficient. The thickness of La 2 Zr 2 O 7 buffer layer affects the failure. The stress component of σ x is the smallest in Ni tape substrate due to its largest thickness

  8. In vitro corrosion of pure magnesium and AZ91 alloy—the influence of thin electrolyte layer thickness

    Science.gov (United States)

    Zeng, Rong-Chang; Qi, Wei-Chen; Zhang, Fen; Li, Shuo-Qi

    2016-01-01

    In vivo degradation predication faces a huge challenge via in vitro corrosion test due to the difficulty for mimicking the complicated microenvironment with various influencing factors. A thin electrolyte layer (TEL) cell for in vitro corrosion of pure magnesium and AZ91 alloy was presented to stimulate the in vivo corrosion in the micro-environment built by the interface of the implant and its neighboring tissue. The results demonstrated that the in vivo corrosion of pure Mg and the AZ91 alloy was suppressed under TEL condition. The AZ91 alloy was more sensitive than pure Mg to the inhibition of corrosion under a TEL thickness of less than 200 µm. The TEL thickness limited the distribution of current, and thus localized corrosion was more preferred to occur under TEL condition than in bulk solution. The TEL cell might be an appropriate approach to simulating the in vivo degradation of magnesium and its alloys. PMID:26816655

  9. Optical properties of pure and Ce3+ doped gadolinium gallium garnet crystals and epitaxial layers

    International Nuclear Information System (INIS)

    Syvorotka, I.I.; Sugak, D.; Wierzbicka, A.; Wittlin, A.; Przybylińska, H.; Barzowska, J.; Barcz, A.; Berkowski, M.; Domagała, J.; Mahlik, S.; Grinberg, M.; Ma, Chong-Geng

    2015-01-01

    Results of X-ray diffraction and low temperature optical absorption measurements of cerium doped gadolinium gallium garnet single crystals and epitaxial layers are reported. In the region of intra-configurational 4f–4f transitions the spectra of the bulk crystals exhibit the signatures of several different Ce 3+ related centers. Apart from the dominant center, associated with Ce substituting gadolinium, at least three other centers are found, some of them attributed to the so-called antisite locations of rare-earth ions in the garnet host, i.e., in the Ga positions. X-ray diffraction data prove lattice expansion of bulk GGG crystals due to the presence of rare-earth antisites. The concentration of the additional Ce-related centers in epitaxial layers is much lower than in the bulk crystals. However, the Ce-doped layers incorporate a large amount of Pb from flux, which is the most probable source of nonradiative quenching of Ce luminescence, not observed in crystals grown by the Czochralski method. - Highlights: • Ce 3+ multicenters found in Gadolinium Gallium Garnet crystals and epitaxial layers. • High quality epitaxial layers of pure and Ce-doped GGG were grown. • Luminescence quenching of Ce 3+ by Pb ions from flux detected in GGG epitaxial layers. • X-ray diffraction allows measuring the amount of the rare-earth antisites in GGG

  10. Ni-CeO2 Cermets Synthesis by Solid State Sintering of Ni/CeO2 Multilayer

    Directory of Open Access Journals (Sweden)

    Aleksandras ILJINAS

    2013-12-01

    Full Text Available Nickel and gadolinium doped cerium oxide (GDC cermet is intensively investigated for an application as an anode material for solid oxide fuel cells based on various electrolytes. The purpose of the present investigation is to analyze morphology, microstructure, and optical properties of deposited and annealed for one hour in the temperatures from 500 ºC to 900 ºC Ni/CeO2 multilayer thin films deposited by sputtering. The crystallographic structure of thin films was investigated by X-ray diffraction. The morphology of the film cross-section was investigated with scanning electron microscope. The elemental analysis of samples was investigated by energy-dispersive X-ray spectroscopy. The fitting of the optical reflectance data was made using Abeles matrix method that is used for the design of interference coatings. The film cross-section of the post-annealed samples consisted of four layers. The first CeO2 layer (on Si had the same fine columnar structure with no features of Ni intermixing. The part of Ni (middle-layer after annealing was converted to NiO with grain size exceeding 100 nm. The CeO2 layer deposited on Ni was divided into two layers. Lower layer had small grains not exceeding 25 nm and consisting of NiO and CeO2 mixture. Upper layer consisted of CeO2 columns with approximate thickness of 50 nm. Ni sample annealed at 600 ºC was fully oxidized. The NiO thickness and refraction index were almost steady after annealing in various temperatures. The approximation of experimental reflectance data was successful only for the samples with one transparent homogeneous layer. The reflectance of the Ni/CeO2 samples annealed at intermediate temperatures could not be fitted using one-layer or three-layer model. That may show that a simplified model could not be implemented.  The real system has complicated distribution of refraction index. DOI: http://dx.doi.org/10.5755/j01.ms.19.4.3073

  11. Fabrication of Ni-5 at. %W Long Tapes with CeO2 Buffer Layer by Reel-to-Reel Method

    DEFF Research Database (Denmark)

    Ma, Lin; Tian, Hui; Yue, Zhao

    2015-01-01

    A 10-m-long homemade textured Ni-5at.%W (Ni5W) long tape with a CeO2 buffer layer has been prepared successfully by means of rolling-assisted biaxially textured substrate (RABiTS) route followed by a chemical solution deposition method in a reel-to-reel manner. Globally, the Ni5W substrate and CeO2...

  12. Studies on Me/Al-layered double hydroxides (Me = Ni and Co) as electrode materials for electrochemical capacitors

    International Nuclear Information System (INIS)

    Liu Xianming; Zhang Yihe; Zhang Xiaogang; Fu Shaoyun

    2004-01-01

    Me/Al-layered double hydroxides (Me=Ni and Co) prepared by the chemical co-precipitation method have been shown to be outstanding novel materials for electrochemical capacitors. The crystalline structure and the electrochemical properties of the electrodes have been studied by considering the effect of the mole ratio of nickel/cobalt. X-ray diffraction analysis shows that the materials belong to hexagonal system with layered structure. Cyclic voltammetric measurements indicate that Me/Al-layered double hydroxides with the Ni/Co mole ratio of 4:6 exhibit excellent capacitive properties within the potential range of 0.0-0.6 V versus Hg/HgO in 6 mol/L KOH electrolyte. Charge/discharge behaviors have been observed with the highest specific capacitance values of 960 F/g at the current density of 400 mA/g. Impedance studies show that the enhanced electrical properties and high frequency response are attributed to the presence of Co oxides

  13. Magnetic studies on Layered solid solution Lix(Ni0.4Mn0.6)2-xO2

    International Nuclear Information System (INIS)

    Nakao, K; Nakamura, T; Yamada, Y; Koshiba, N

    2011-01-01

    Li x (Ni 0.4 Mn 0.6 ) 2-x O 2 (1.09≤x≤1.23) were prepared by the solid-state reaction using LiOH and coprecipitated mixed hydroxide as raw materials. All the compounds have a layered rock-salt structure, and the cation mixing degree (Ni 2+ occupancy in the Li-layer) decreases with an increase in x. From the low-temperature magnetic measurement, they all have negative Weiss temperature and spontaneous magnetization, that is, they are ferromagnetic materials. Both the Curie temperature and the spontaneous magnetization at 4.2K decrease with an increase in x. These magnetic variations are attributed to the lowering of the cation mixing degree: the magnetic interaction network turns to two-dimensional one with the loss of the inert-layer coupling. These situations may be considered semi-quantitatively using the ferromagnetic cluster model. Additionally, the cation mixing degree has an influence on their electrochemical properties such as cycle fading and rate capability.

  14. Moessbauer and XRD study of pulse plated Fe-P and Fe-Ni thin layers

    Energy Technology Data Exchange (ETDEWEB)

    Miko, Annamaria [Bay Zoltan Institute for Material Science (Hungary); Kuzmann, Erno, E-mail: kuzmann@para.chem.elte.hu [Eoetvoes Lorand University, Research Group for Nuclear Methods in Structural Chemistry, Hungarian Academy of Sciences, Department of Nuclear Chemistry (Hungary); Lakatos-Varsanyi, Magda [Bay Zoltan Institute for Material Science (Hungary); Kakay, Attila [Research Institute for Solid State Physics and Optics (Hungary); Nagy, Ferenc [Eoetvoes Lorand University, Research Group for Nuclear Methods in Structural Chemistry, Hungarian Academy of Sciences, Department of Nuclear Chemistry (Hungary); Varga, Lajos Karoly [Research Institute for Solid State Physics and Optics (Hungary)

    2005-09-15

    {sup 57}Fe conversion electron Moessbauer spectroscopy, X-ray diffraction, electrochemical and magnetic measurements were used to study pulse electroplated Fe-P and Ni-Fe coatings. XRD and {sup 57}Fe CEMS measurements revealed the amorphous character of the novel pulse plated Fe-P alloys. CEM spectra indicated significant differences in the short range order and in the magnetic anisotropy between the Fe-P deposits pulse plated at medium long deposition time (t{sub on} = 2 ms), with short relaxation time (t{sub off} = 9 ms) and low current density (I{sub p} = 0.05 Acm{sup -2}) or at short deposition time (t{sub on} = 1 ms) with long relaxation time (t{sub off} = 250 ms) and high current density (I{sub p} = 1.0 Acm{sup -2}). The broad peaks centred around the fcc reflections in XRD of the pulse plated Ni-22 wt.% Fe deposit reflected a microcrystalline Ni-Fe alloy with a very fine, 5-8 nm, grain size. The CEM spectrum of the pulse plated Ni-22 wt.% Fe coating corresponded to a highly disordered solid solution alloy containing a minute amount of ferrihydrite. Extreme favourable soft magnetic properties were observed with these Ni-Fe and Fe-P pulse plated thin layers.

  15. NiCo2O4@TiN Core-shell Electrodes through Conformal Atomic Layer Deposition for All-solid-state Supercapacitors

    KAUST Repository

    Wang, Renqi

    2016-03-04

    Ternary transition metal oxides such as NiCo2O4 show great promise as supercapacitor electrode materials. However, the unsatisfactory rate performance of NiCo2O4 may prove to be a major hurdle to its commercial usage. Herein, we report the development of NiCo2O4@TiN core–shell nanostructures for all-solid-state supercapacitors with significantly enhanced rate capability. We demonstrate that a thin layer of TiN conformally grown by atomic layer deposition (ALD) on NiCo2O4 nanofiber arrays plays a key role in improving their electrical conductivity, mechanical stability, and rate performance. Fabricated using the hybrid NiCo2O4@TiN electrodes, the symmetric all-solid-state supercapacitor exhibited an impressive stack power density of 58.205 mW cm−3 at a stack energy density of 0.061 mWh cm−3. To the best of our knowledge, these values are the highest of any NiCo2O4-based all-solid-state supercapacitor reported. Additionally, the resulting NiCo2O4@TiN all-solid-state device displayed outstanding cycling stability by retaining 70% of its original capacitance after 20,000 cycles at a high current density of 10 mA cm−2. These results illustrate the promise of ALD-assisted hybrid NiCo2O4@TiN electrodes for sustainable and integrated energy storage applications.

  16. NiCo2O4@TiN Core-shell Electrodes through Conformal Atomic Layer Deposition for All-solid-state Supercapacitors

    KAUST Repository

    Wang, Renqi; Xia, Chuan; Wei, Nini; Alshareef, Husam N.

    2016-01-01

    Ternary transition metal oxides such as NiCo2O4 show great promise as supercapacitor electrode materials. However, the unsatisfactory rate performance of NiCo2O4 may prove to be a major hurdle to its commercial usage. Herein, we report the development of NiCo2O4@TiN core–shell nanostructures for all-solid-state supercapacitors with significantly enhanced rate capability. We demonstrate that a thin layer of TiN conformally grown by atomic layer deposition (ALD) on NiCo2O4 nanofiber arrays plays a key role in improving their electrical conductivity, mechanical stability, and rate performance. Fabricated using the hybrid NiCo2O4@TiN electrodes, the symmetric all-solid-state supercapacitor exhibited an impressive stack power density of 58.205 mW cm−3 at a stack energy density of 0.061 mWh cm−3. To the best of our knowledge, these values are the highest of any NiCo2O4-based all-solid-state supercapacitor reported. Additionally, the resulting NiCo2O4@TiN all-solid-state device displayed outstanding cycling stability by retaining 70% of its original capacitance after 20,000 cycles at a high current density of 10 mA cm−2. These results illustrate the promise of ALD-assisted hybrid NiCo2O4@TiN electrodes for sustainable and integrated energy storage applications.

  17. Ni-YSZ cermet substrate supported thin SDC and YSZ+SDC bi-layer SOFCs

    Energy Technology Data Exchange (ETDEWEB)

    Zhang, X.; Robertson, M.; Deces-Petit, C.; Xie, Y.; Hui, R.; Yick, S.; Styles, E.; Roller, J.; Kesler, O.; Qu, W.; Jankovic, J.; Tang, Z.; Perednis, D.; Maric, R.; Ghosh, D. [National Research Council of Canada, Vancouver, BC (Canada). Inst. for Fuel Cell Innovation

    2005-07-01

    One of the disadvantages of a ceria-based electrolyte is that it becomes a mixed conductor at anode conditions, which causes cell voltage loss and fuel efficiency loss due to internal shorting. Chemical and mechanical stability is another concern for long-term service. To lower manufacturing costs, efforts have been made to bring proven semiconductor manufacturing technology to Solid Oxide Fuel Cells (SOFCs). This study employed Tape casting of cermet substrates, Screen-printing of functional layers and Co-firing of cell components (TSC) to fabricate nickel (Ni)-cermet supported cells with mainly ceria-based thin electrolytes. Ni-Yttria-Stabilized Zirconia (YSZ) cermet supported cell with Samaria Doped Ceria (SDC) single layer electrolytes and YSZ+SDC bi-layer electrolytes were successfully developed for low-temperature performance characterization. The elemental distribution at the cell interface was mapped and the electrochemical performance of the cells was recorded. Many high-Zr-content micro-islands were found on the thin SDC surface. The influence of co-firing temperature and thin-film preparation methods on the Zr-islands' appearance was also investigated. Using in-situ sintered cathodes, high performance of the SDC cells was obtained. It was concluded that the bi-layer cells did show higher Open Circuit Voltage (OCV) values, with 1180 mW/cm{sup 2} at 650 degrees C, as well as good performance at 700-800 degrees C, with near OCV value. However, their performance was much lower than those of the SDC cells at low operating temperature. Zr-micro-islands formation on the SDC electrolyte was observed and investigated. 6 refs., 5 tabs., 7 figs.

  18. Signals of El Niño Modoki in the tropical tropopause layer and stratosphere

    Directory of Open Access Journals (Sweden)

    F. Xie

    2012-06-01

    Full Text Available The effects of El Niño Modoki events on the tropical tropopause layer (TTL and on the stratosphere were investigated using European Center for Medium Range Weather Forecasting (ECMWF reanalysis data, oceanic El Niño indices, and general climate model outputs. El Niño Modoki events tend to depress convective activities in the western and eastern Pacific but enhance convective activities in the central and northern Pacific. Consequently, during El Niño Modoki events, negative water vapor anomalies occur in the western and eastern Pacific upper troposphere, whereas there are positive anomalies in the central and northern Pacific upper troposphere. The spatial patterns of the outgoing longwave radiation (OLR and upper tropospheric water vapor anomalies exhibit a tripolar form. The empirical orthogonal function (EOF analysis of the OLR and upper tropospheric water vapor anomalies reveals that canonical El Niño events are associated with the leading mode of the EOF, while El Niño Modoki events correspond to the second mode. The composite analysis based on ERA-interim data indicate that El Niño Modoki events have a reverse effect on middle-high latitudes stratosphere, as compared with the effect of typical El Niño events, i.e., the northern polar vortex is stronger and colder but the southern polar vortex is weaker and warmer during El Niño Modoki events. According to the simulation' results, we found that the reverse effect on the middle-high latitudes stratosphere is resulted from a complicated interaction between quasi-biennial oscillation (QBO signal of east phase and El Niño Modoki signal. This interaction is not a simply linear overlay of QBO signal and El Niño Modoki signal in the stratosphere, it is El Niño Modoki that leads to different tropospheric zonal wind anomalies with QBO forcing from that caused by typical El Niño, thus, the planetary wave propagation from troposphere to the stratosphere during El Niño Modoki events is

  19. Room-temperature ferromagnetism in Dy films doped with Ni

    International Nuclear Information System (INIS)

    Edelman, I.; Ovchinnikov, S.; Markov, V.; Kosyrev, N.; Seredkin, V.; Khudjakov, A.; Bondarenko, G.; Kesler, V.

    2008-01-01

    Temperature, magnetic field and spectral dependences of magneto-optical effects (MOEs) in bi-layer films Dy (1-x) Ni x -Ni and Dy (1-x) (NiFe) x -NiFe were investigated, x changes from 0 to 0.06. Peculiar behavior of the MOEs was revealed at temperatures essentially exceeding the Curie temperature of bulk Dy which is explained by the magnetic ordering of the Dy layer containing Ni under the action of two factors: Ni impurities distributed homogeneously over the whole Dy layer and atomic contact of this layer with continues Ni layer. The mechanism of the magnetic ordering is suggested to be associated with the change of the density of states of the alloy Dy (1-x) Ni x owing to hybridization with narrow peaks near the Fermi level character for Ni

  20. Observation of the structural, optical and magnetic properties during the transformation from hexagonal NiS nano-compounds to cubic NiO nanostructures due to thermal oxidation

    Energy Technology Data Exchange (ETDEWEB)

    Linganiso, E.C., E-mail: elinganiso@csir.co.za [National Centre for Nano-Structured Materials, Council for Scientific and Industrial Research, P.O. Box 395, Pretoria 0001 (South Africa); DST/NRF Centre of Excellence in Strong Materials, Molecular Sciences Institute, School of Chemistry, University of the Witwatersrand, Private Bag 3, Johannesburg, Wits 2050 (South Africa); Mwakikunga, B.W., E-mail: bmwakikunga@csir.co.za [National Centre for Nano-Structured Materials, Council for Scientific and Industrial Research, P.O. Box 395, Pretoria 0001 (South Africa); Coville, N.J. [DST/NRF Centre of Excellence in Strong Materials, Molecular Sciences Institute, School of Chemistry, University of the Witwatersrand, Private Bag 3, Johannesburg, Wits 2050 (South Africa); Mhlanga, S.D. [Department of Applied Chemistry, University of Johannesburg, PO Box 17011, Doornfontein, 2028 Johannesburg (South Africa)

    2015-04-25

    Graphical abstract: The transition temperature of 350 °C for the formation of c-NiO from h-NiS oxidation was obtained from structural and optical property studies and by calculating the number of spins obtained from the EPR data. Vibrating sample magnetometry (VSM) shows that this pure NiS has both ferromagnetic ordering and paramagnetic domains. Further, the transition temperature of −9 °C of the pure α-NiS nano-alloys was confirmed by performing electrical measurements on the as-synthesized material. - Highlights: • Single hexagonal phase NiS obtained by microwave assisted hydrothermal synthesis. • NiS nanoalloys show both ferromagnetic and paramagnetic domains by VSM. • Structural evolution of annealed NiS and temperature dependent NiS oxidation presented. • Phase transition from NiS to NiO studied and correlated to the EPR spin population data and crystallite size. • Ferromagnetic and paramagnetic ordering observed for the raw NiS nanostructures. - Abstract: Single phase α-NiS nano-compounds with uniformly distributed hierarchical networks were synthesized by a microwave-assisted hydrothermal technique. The materials were evaluated for thermal stability under an oxidative environment and at temperatures between 150 °C and 600 °C. NiS materials showed stability at 300 °C and NiO formation was observed from 350 °C to 600 °C. The annealing effect on the crystalline size and IR absorption of the annealed samples is reported by XRD and FTIR studied. The EPR properties of the annealed materials were studied and compared to the oxidized materials. The transition temperature of 350 °C for the formation of NiO from NiS oxidation was confirmed by calculating the number of spins obtained from the EPR data. Vibrating sample magnetometry (VSM) shows that this pure NiS has both ferromagnetic ordering and paramagnetic domains. Further, the transition temperature of −9 °C of the pure α-NiS nano-compounds was confirmed by performing electrical

  1. Melt layer erosion of pure and lanthanum doped tungsten under VDE-like high heat flux loads

    International Nuclear Information System (INIS)

    Yuan, Y.; Greuner, H.; Böswirth, B.; Luo, G.-N.; Fu, B.Q.; Xu, H.Y.; Liu, W.

    2013-01-01

    Heat loads expected for VDEs in ITER were applied in the neutral beam facility GLADIS at IPP Garching. Several ∼3 mm thick rolled pure W and W–1 wt% La 2 O 3 plates were exposed to pulsed hydrogen beams with a central heat flux of 23 MW/m 2 for 1.5–1.8 s. The melting thresholds are determined, and melt layer motion as well as material structure evolutions are shown. The melting thresholds of the two W grades are very close in this experimental setup. Lots of big bubbles with diameters from several μm to several 10 μm in the re-solidified layer of W were observed and they spread deeper with increasing heat flux. However, for W–1 wt% La 2 O 3 , no big bubbles were found in the corrugated melt layer. The underlying mechanisms referred to the melt layer motion and bubble issues are tentatively discussed based on comparison of the erosion characteristics between the two W grades

  2. CLASSICAL AREAS OF PHENOMENOLOGY: First-principles calculations for the elastic properties of Ni-base model superalloys: Ni/Ni3Al multilayers

    Science.gov (United States)

    Wang, Yun-Jiang; Wang, Chong-Yu

    2009-10-01

    A model system consisting of Ni[001](100)/Ni3Al[001](100) multi-layers are studied using the density functional theory in order to explore the elastic properties of single crystal Ni-based superalloys. Simulation results are consistent with the experimental observation that rafted Ni-base superalloys virtually possess a cubic symmetry. The convergence of the elastic properties with respect to the thickness of the multilayers are tested by a series of multilayers from 2γ'+2γ to 10γ'+10γ atomic layers. The elastic properties are found to vary little with the increase of the multilayer's thickness. A Ni/Ni3Al multilayer with 10γ'+10γ atomic layers (3.54 nm) can be used to simulate the mechanical properties of Ni-base model superalloys. Our calculated elastic constants, bulk modulus, orientation-dependent shear modulus and Young's modulus, as well as the Zener anisotropy factor are all compatible with the measured results of Ni-base model superalloys R1 and the advanced commercial superalloys TMS-26, CMSX-4 at a low temperature. The mechanical properties as a function of the γ' phase volume fraction are calculated by varying the proportion of the γ and γ' phase in the multilayers. Besides, the mechanical properties of two-phase Ni/Ni3Al multilayer can be well predicted by the Voigt-Reuss-Hill rule of mixtures.

  3. Spectrally-resolved UV photodesorption of CH4 in pure and layered ices

    Science.gov (United States)

    Dupuy, R.; Bertin, M.; Féraud, G.; Michaut, X.; Jeseck, P.; Doronin, M.; Philippe, L.; Romanzin, C.; Fillion, J.-H.

    2017-07-01

    Context. Methane is among the main components of the ice mantles of interstellar dust grains, where it is at the start of a rich solid-phase chemical network. Quantification of the photon-induced desorption yield of these frozen molecules and understanding of the underlying processes is necessary to accurately model the observations and the chemical evolution of various regions of the interstellar medium. Aims: This study aims at experimentally determining absolute photodesorption yields for the CH4 molecule as a function of photon energy. The influence of the ice composition is also investigated. By studying the methane desorption from layered CH4:CO ice, indirect desorption processes triggered by the excitation of the CO molecules are monitored and quantified. Methods: Tunable monochromatic vacuum ultraviolet light (VUV) light from the DESIRS beamline of the SOLEIL synchrotron is used in the 7-13.6 eV (177-91 nm) range to irradiate pure CH4 or layers of CH4 deposited on top of CO ice samples. The release of species in the gas phase is monitored by quadrupole mass spectrometry, and absolute photodesorption yields of intact CH4 are deduced. Results: CH4 photodesorbs for photon energies higher than 9.1 eV ( 136 nm). The photodesorption spectrum follows the absorption spectrum of CH4, which confirms a desorption mechanism mediated by electronic transitions in the ice. When it is deposited on top of CO, CH4 desorbs between 8 and 9 eV with a pattern characteristic of CO absorption, indicating desorption induced by energy transfer from CO molecules. Conclusions: The photodesorption of CH4 from pure ice in various interstellar environments is around 2.0 ± 1.0 × 10-3 molecules per incident photon. Results on CO-induced indirect desorption of CH4 provide useful insights for the generalization of this process to other molecules co-existing with CO in ice mantles.

  4. Application of NiMoNb adhesion layer on plasma-treated polyimide substrate for flexible electronic devices

    Energy Technology Data Exchange (ETDEWEB)

    Bang, S.-H.; Kim, K.-K.; Jung, H.-Y.; Kim, T.-H.; Jeon, S.-H. [Metal and Material Technology Group, R and D Center, LS Mtron Ltd., Gyeonggi 431-080 (Korea, Republic of); Seol, Jae-Bok, E-mail: zptkfm20@hanmail.net [Max-Planck-Insititut für Eisenforschung, Max-Planck-Str. 1, D-40237 Düsseldorf (Germany)

    2014-05-02

    A thin film, NiMoNb, was introduced as an adhesion layer between the Cu metal and the insulator polyimide substrate in a flexible Cu-clad laminated structure. Using 90° peel test, we evaluated the peel strength of the system as a function of the thickness of the adhesion layer. An increase in the NiMoNb thickness from 7 to 40 nm enhanced the peel strength of the deposited systems. After plasma treatment by the roll-to-roll method, the multilayer structure showed an outstanding peel strength of ∼ 529 N/m, even after thermal annealing at 150 °C for 168 h. We also studied the role of plasma treatment of the polyimide substrate on the adhesion strength and microstructure of a flexible Cu-clad laminated structure by peel strength, atomic force microscopy, X-ray photoelectron spectroscopy, and transmission electron microscopy. These experimental observations showed that the plasma-treated polyimide substrate with the deposition of NiMoNb showed the enhanced adhesion of ∼ 656 N/m, because of the change of functional groups, which affected the bonding force and crystallinity of the thin films deposited on polyimide, rather than an increase in the surface roughness. - Highlights: • NiMoNb film on polyimide substrate was employed for higher peel strength. • Plasma-treated substrate enhances the peel strength of multilayer. • Even when annealed at 150 °C, plasma-treated films showed enhanced peel strength.

  5. Application of NiMoNb adhesion layer on plasma-treated polyimide substrate for flexible electronic devices

    International Nuclear Information System (INIS)

    Bang, S.-H.; Kim, K.-K.; Jung, H.-Y.; Kim, T.-H.; Jeon, S.-H.; Seol, Jae-Bok

    2014-01-01

    A thin film, NiMoNb, was introduced as an adhesion layer between the Cu metal and the insulator polyimide substrate in a flexible Cu-clad laminated structure. Using 90° peel test, we evaluated the peel strength of the system as a function of the thickness of the adhesion layer. An increase in the NiMoNb thickness from 7 to 40 nm enhanced the peel strength of the deposited systems. After plasma treatment by the roll-to-roll method, the multilayer structure showed an outstanding peel strength of ∼ 529 N/m, even after thermal annealing at 150 °C for 168 h. We also studied the role of plasma treatment of the polyimide substrate on the adhesion strength and microstructure of a flexible Cu-clad laminated structure by peel strength, atomic force microscopy, X-ray photoelectron spectroscopy, and transmission electron microscopy. These experimental observations showed that the plasma-treated polyimide substrate with the deposition of NiMoNb showed the enhanced adhesion of ∼ 656 N/m, because of the change of functional groups, which affected the bonding force and crystallinity of the thin films deposited on polyimide, rather than an increase in the surface roughness. - Highlights: • NiMoNb film on polyimide substrate was employed for higher peel strength. • Plasma-treated substrate enhances the peel strength of multilayer. • Even when annealed at 150 °C, plasma-treated films showed enhanced peel strength

  6. Improved coking resistance of direct ethanol solid oxide fuel cells with a Ni-Sx anode

    Science.gov (United States)

    Yan, Ning; Luo, Jing-Li; Chuang, Karl T.

    2014-03-01

    In this study, the coking resistance of anode supported direct ethanol solid oxide fuel cell with a Ni-Sx anode was investigated comparatively with the conventional cell using pure Ni catalyst. The surface catalytic properties of Ni were manipulated via depositing a layer of S atoms. It was confirmed that on the surface of Ni, a combination of S monolayer and elemental S was formed without producing Ni3S2 phase. The developed Ni-Sx cell exhibited a significantly improved coke resistivity in ethanol feed while maintaining an adequately high performance. The S species on Ni enabled the suppression of the coke formation as well as the alleviation of the metal dusting effect of the anode structure. After operating in ethanol fuel for identical period of time at 850 °C, a maximum power density of 400 mW cm-2 was sustained whereas the conventional cell performance decreased to less than 40 mW cm-2 from the original 704 mW cm-2. In an optimized stability test, the Ni-Sx cell operated at 750 °C for more than 22 h until the fuel drained without any degradation.

  7. Room-temperature ferromagnetism in Dy films doped with Ni

    Energy Technology Data Exchange (ETDEWEB)

    Edelman, I. [Kirensky Institute of Physics, Siberian Division, Russian Academy of Sciences, Akademgorodok, Krasnoyarsk 660036 (Russian Federation)], E-mail: ise@iph.krasn.ru; Ovchinnikov, S. [Kirensky Institute of Physics, Siberian Division, Russian Academy of Sciences, Akademgorodok, Krasnoyarsk 660036 (Russian Federation); Siberian Federal University, Av. Svobodnyi 71, Krasnoyarsk 660074 (Russian Federation); Markov, V.; Kosyrev, N.; Seredkin, V.; Khudjakov, A.; Bondarenko, G. [Kirensky Institute of Physics, Siberian Division, Russian Academy of Sciences, Akademgorodok, Krasnoyarsk 660036 (Russian Federation); Kesler, V. [Institute of Semiconductor Physics, Siberian Division, Russian Academy of Sciences, Av. Akademika Lavrent' eva 13, Novosibirsk 630090 (Russian Federation)

    2008-09-01

    Temperature, magnetic field and spectral dependences of magneto-optical effects (MOEs) in bi-layer films Dy{sub (1-x)}Ni{sub x}-Ni and Dy{sub (1-x)}(NiFe){sub x}-NiFe were investigated, x changes from 0 to 0.06. Peculiar behavior of the MOEs was revealed at temperatures essentially exceeding the Curie temperature of bulk Dy which is explained by the magnetic ordering of the Dy layer containing Ni under the action of two factors: Ni impurities distributed homogeneously over the whole Dy layer and atomic contact of this layer with continues Ni layer. The mechanism of the magnetic ordering is suggested to be associated with the change of the density of states of the alloy Dy{sub (1-x)}Ni{sub x} owing to hybridization with narrow peaks near the Fermi level character for Ni.

  8. Ferromagnetic resonance study of sputtered NiFe/V/NiFe heterostructures

    Energy Technology Data Exchange (ETDEWEB)

    Alayo, W., E-mail: willian.rodriguez@ufpel.edu.br [Departamento de Física – IFM, Universidade Federal de Pelotas, 96010-900 Rio Grande do Sul (Brazil); Pelegrini, F. [Instituto de Física, Universidade Federal de Goiás, Goiânia, 74001-970 (Brazil); Baggio-Saitovitch, E. [Centro Brasileiro de Pesquisas Físicas, Rio de Janeiro, RJ, 22290-180 (Brazil)

    2015-03-01

    The Ni{sub 81}Fe{sub 19}/V/Ni{sub 81}Fe{sub 19} heterostructures has been produced by magnetron sputtering and analyzed by ferromagnetic resonance. Two systems were investigated: the non symmetrical NiFe(50 Å)/V(t)/NiFe(30 Å) trilayers and the symmetrical NiFe(80 Å)/V(t)/NiFe(80 Å) trilayers, with variable ultrathin V thickness t. Ferromagnetic exchange coupling was evidenced for t below 10 Å by the excitation of the optic mode, in the case of the non symmetrical samples, and by the observation of a single resonance mode for the symmetrical trilayers. For larger V thickness, all samples exhibited two modes, which were attributed to the resonance of the individual NiFe layers with different effective magnetizations. The analysis with the equilibrium and resonance conditions provided the exchange coupling constants and effective magnetizations. - Highlights: • We present a study of symmetrical and non symmetrical NiFe/V/NiFe trilayers deposited on Si single crystals by ferromagnetic resonance (FMR) at room temperature. • For the non symmetrical trilayers, the FMR spectra show the optic and acoustic modes for samples with very thin V layer thicknesses, evidencing ferromagnetic exchange coupling, whereas, for larger V thickness, the spectra exhibited two well resolved modes associated to each independent NiFe layer. For the symmetrical trilayers, strong ferromagnetic exchange coupling is evidenced by the observation of a single resonance mode. • The analysis with the equilibrium condition and dispersion relation provides the exchange coupling constants and effective magnetizations.

  9. Two-Dimensional Layered Double Hydroxide Derived from Vermiculite Waste Water Supported Highly Dispersed Ni Nanoparticles for CO Methanation

    Directory of Open Access Journals (Sweden)

    Panpan Li

    2017-03-01

    Full Text Available Expanded multilayered vermiculite (VMT was successfully used as catalyst support and Ni/VMT synthesized by microwave irradiation assisted synthesis (MIAS exhibited excellent performance in our previous work. We also developed a two-dimensional porous SiO2 nanomesh (2D VMT-SiO2 by mixed-acid etching of VMT. Compared with three-dimensional (3D MCM-41, 2D VMT-SiO2 as a catalyst support provided a superior position for implantation of NiO species and the as-obtained catalyst exhibited excellent performance. In this paper, we successfully synthesized a layered double hydroxide (LDH using the spent liquor after mixed-acid etching of VMT, which mainly contained Mg2+ and Al3+. The as-calcined layered double oxide (LDO was used as a catalyst support for CO methanation. Compared with Ni/MgAl-LDO, Ni/VMT-LDO had smaller active component particles; therefore, in this study, it exhibited excellent catalytic performance over the whole temperature range of 250–500 °C. Ni/VMT-LDO achieved the best activity with 87.88% CO conversion, 89.97% CH4 selectivity, and 12.47 × 10−2·s−1 turn over frequency (TOF at 400 °C under a gas hourly space velocity of 20,000 mL/g/h. This study demonstrated that VMT-LDO as a catalyst support provided an efficient way to develop high-performance catalysts for synthetic natural gas (SNG from syngas.

  10. MOD approach for the growth of epitaxial CeO2 buffer layers on biaxially textured Ni-W substrates for YBCO coated conductors

    International Nuclear Information System (INIS)

    Bhuiyan, M S; Paranthaman, M; Sathyamurthy, S; Aytug, T; Kang, S; Lee, D F; Goyal, A; Payzant, E A; Salama, K

    2003-01-01

    We have grown epitaxial CeO 2 buffer layers on biaxially textured Ni-W substrates for YBCO coated conductors using a newly developed metal organic decomposition (MOD) approach. Precursor solution of 0.25 M concentration was spin coated on short samples of Ni-3 at%W (Ni-W) substrates and heat-treated at 1100 C in a gas mixture of Ar-4%H 2 for 15 min. Detailed x-ray studies indicate that CeO 2 films have good out-of-plane and in-plane textures with full-width-half-maximum values of 5.8 deg. and 7.5 deg., respectively. High temperature in situ XRD studies show that the nucleation of CeO 2 films starts at 600 C and the growth completes within 5 min when heated at 1100 C. SEM and AFM investigations of CeO 2 films reveal a fairly dense microstructure without cracks and porosity. Highly textured YSZ barrier layers and CeO 2 cap layers were deposited on MOD CeO 2 -buffered Ni-W substrates using rf-magnetron sputtering. Pulsed laser deposition (PLD) was used to grow YBCO films on these substrates. A critical current, J c , of about 1.5 MA cm -2 at 77 K and self-field was obtained on YBCO (PLD)/CeO 2 (sputtered)/YSZ (sputtered)/CeO 2 (spin-coated)/Ni-W

  11. Electrochemically synthesized large area network of Co{sub x}Ni{sub y}Al{sub z} layered triple hydroxides nanosheets: A high performance supercapacitor

    Energy Technology Data Exchange (ETDEWEB)

    Gupta, Vinay [Carbon Technology Unit, National Physical Laboratory, New Delhi 110012 (India); Art, Science and Technology Center for Cooperative Research, Kyushu University, Kasuga-shi, Fukuoka 816-8580 (Japan); Japan Science and Technology Agency, Kawaguchi-shi, Saitama 332-0012 (Japan); Gupta, Shubhra; Miura, Norio [Art, Science and Technology Center for Cooperative Research, Kyushu University, Kasuga-shi, Fukuoka 816-8580 (Japan)

    2009-04-15

    A network of Co{sub x}Ni{sub y}Al{sub z} layered triple hydroxides (LTHs) nanosheets was prepared by the potentiostatic deposition process at -1.0 V (vs. Ag/AgCl) onto stainless steel electrodes. X-ray diffraction patterns show that the Co{sub x}Ni{sub y}Al{sub z}LTHs belong to the hexagonal system with layered structure. Cyclic voltammetry and charge discharge measurements in the potential range of -0.1 to 0.5 V and 0.0-0.4 V, respectively, vs. Ag/AgCl in 1 M KOH electrolyte indicate that Co{sub x}Ni{sub y}Al{sub z}LTHs have excellent supercapacitive characteristics. The maximum specific capacitance of {proportional_to}1263 F g{sup -1} was obtained for Co{sub 0.59}Ni{sub 0.21}Al{sub 0.20}LTH. The impedance studies indicated highly conducting nature of the Co{sub x}Ni{sub y}Al{sub z}LTHs. (author)

  12. Moessbauer study of magnetic transformation of Ni3Al-(57Co+57Fe) surface layer

    International Nuclear Information System (INIS)

    Dudas, J.; Zemcik, T.

    1975-01-01

    The results of the magnetic transformation study of the Ni 3 Al-( 57 Co+ 57 Fe) surface layer by the 57 Fe Moessbauer effect in dependence on the penetration depth of ( 57 Co+ 57 Fe) are presented. These results are discussed in terms of the magnetic polarization of the Co (and Fe) atoms and the appearance of the 'giant' magnetic moment. The critical concentration of Co+Fe impurities sufficient for transformation of the originally paramagnetic surface layer into ferromagnetic at room temperature was determined to be 1.03 at.'=.. (author)

  13. Effect of laser modification of B-Ni complex layer on wear resistance and microhardness

    Science.gov (United States)

    Bartkowska, Aneta; Pertek, Aleksandra; Popławski, Mikołaj; Bartkowski, Dariusz; Przestacki, Damian; Miklaszewski, Andrzej

    2015-09-01

    The paper presents the results of microstructure observations, microhardness measurements and wear resistance tests of B-Ni complex layers. Boronickelizing is a three-step process of layer production on metallic substrate. Nickel modified boronized layers were called 'boronickelized'. Nickel plating was applied first and, as a result, nickel coatings with a varying thickness were obtained. Diffusion boronizing was carried out as a second step. Boronickelized layer was formed following the merger of galvanic and diffusion processes. In the third step the galvanic-diffusion boronickelized layer was obtained by remelting it with a CO2 laser beam. Galvanic-diffusion boronickelized layer had a dual-zone microstructure. The first zone was continuous and nickel-enriched, and characterized by reduced microhardness, whereas the second zone was characterized by needle-shaped microstructure, with microhardness similar to Fe2B iron borides. After laser modification steel specimens with the boronickelized layer consisted of remelted zone (MZ), heat affected zone (HAZ), and substrate. It was found that increasing the thickness of nickel coating leads to decreasing the microhardness of the remelted zone. Increasing thickness of nickel coating causes the reduction of wear resistance of boronickelized layer modified by laser beam. The application of a nickel coating thicker than 20 μm causes incomplete remelting of needle-shaped microstructure of boronickelized layer.

  14. Epitaxial YBa2Cu3O7 on biaxially textured (001) Ni: An approach to high critical current density superconducting tapes

    International Nuclear Information System (INIS)

    Norton, D.P.; Goyal, A.; Budai, J.D.

    1997-01-01

    In-plane aligned, c-axis oriented YBa 2 Cu 3 O 7 (YBCO) films with superconducting critical current densities, J c , as high as 700,000 amperes per square centimeter at 77 kelvin have been grown on thermo-mechanically, rolled-textured (001) Ni tapes using pulsed-laser deposition. Epitaxial growth of oxide buffer layers directly on biaxially textured Ni, formed by recrystallization of cold-rolled pure Ni, enables the growth of 1.5 micrometer-thick YBCO films with superconducting properties that are comparable to those observed for epitaxial films on single crystal oxide substrates. This result represents a viable approach for producing long-length superconducting tapes for high current, high field applications at 77 kelvin

  15. Dielectric enhancement of PbZr{sub 0.3}Ti{sub 0.7}O{sub 3}/LaNiO{sub 3} multilayer thick film

    Energy Technology Data Exchange (ETDEWEB)

    Fan, Yasong; Chen, Xiaoyang; Habibul, Arzigul; Zhang, Danyang; Yu, Ping [College of Materials Science and Engineering, Sichuan University, Chengdu, 610064 (China)

    2016-08-15

    Multilayer thick films (∝4 μm) with compositional PbZr{sub 0.3}Ti{sub 0.7}O{sub 3}/LaNiO{sub 3} layers and one-layer PZT thick films were prepared on the silicon substrate by radio-frequency magnetron sputtering. PbZr{sub 0.3}Ti{sub 0.7}O{sub 3}/LaNiO{sub 3} multilayer thick film are characterized by highly preferential (100)-oriented growth and columnar microstructure due to alternately introducing LaNiO{sub 3} seeding layers. The effects of LaNiO{sub 3} layers on microstructure and electrical properties of PbZr{sub 0.3}Ti{sub 0.7}O{sub 3} thick films were investigated in detail. The results show that both PZT and PbZr{sub 0.3}Ti{sub 0.7}O{sub 3}/LaNiO{sub 3} multilayer thick film were pure perovskite crystalline phase. The PbZr{sub 0.3}Ti{sub 0.7}O{sub 3} film texture was dense and well adhered on the LaNiO{sub 3} layer. PbZr{sub 0.3}Ti{sub 0.7}O{sub 3}/LaNiO{sub 3} multilayer thick film possessed obvious enhanced dielectric properties compared with PZT thick film: ε{sub r} ∝2450 (10 kHz) and tanδ ∝0.02 (10 kHz). Rayleigh law was used to analysis the behavior of the enhanced dielectric properties and the pinched-shaped polarization-electric field hysteresis loops. The larger Rayleigh parameter, α ∝51.1408 cm kV{sup -1} (1 kHz) indicates the larger extrinsic contribution to permittivity and strong domain-wall-defect charge interaction. The leakage current behaviors of the multilayer thick film were also investigated in detail. (copyright 2016 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim)

  16. Effect of interface intermixing on giant magnetoresistance in NiFe/Cu and Co/NiFe/Co/Cu multilayers

    International Nuclear Information System (INIS)

    Nagamine, L.C.C.M.; Biondo, A.; Pereira, L.G.; Mello, A.; Schmidt, J.E.; Chimendes, T.W.; Cunha, J.B.M.; Saitovitch, E.B.

    2003-01-01

    This article reports on the important influence of the spontaneously built-in paramagnetic interfacial layers on the magnetic and magnetoresistive properties of NiFe/Cu and Co/NiFe/Co/Cu multilayers grown by magnetron sputtering. A computational simulation, based on a semiclassical model, has been used to reproduce the variations of the resistivity and of the magnetoresistance (MR) amplitude with the thickness of the NiFe, Cu, and Co layers. We showed that the compositionally intermixed layers at NiFe/Cu interfaces, which are paramagnetic, reduce the flow of polarized electrons and produce a masking on the estimated mean-free path of both types of electrons due to the reduction of their effective values, mainly for small NiFe thickness. Moreover, the transmission coefficients for the electrons decrease when Fe buffer layers are replaced by NiFe ones. This result is interpreted in terms of the variations of the interfacial intermixing and roughness at the interfaces, leading to an increase of the paramagnetic interfacial layer thickness. The effect provoked by Co deposition at the NiFe 16 A/Cu interfaces has also been investigated. The maximum of the MR amplitudes was found at 5 A of Co, resulting in the quadruplication of the MR amplitude. This result is partially attributed to the interfacial spin-dependent scattering due to the increase of the magnetic order at interfaces. Another effect observed here was the increase of the spin-dependent scattering events in the bulk NiFe due to a larger effective NiFe thickness, since the paramagnetic interfacial layer thickness is decreased

  17. Structural Differentiation between Layered Single (Ni) and Double Metal Hydroxides (Ni–Al LDHs) Using Wavelet Transformation

    Energy Technology Data Exchange (ETDEWEB)

    Siebecker, Matthew G. [University of Delaware, Delaware Environmental Institute; Sparks, Donald L. [University of Delaware, Delaware Environmental Institute

    2017-09-07

    Layered double hydroxides (LDHs) are anionic clays important in disciplines such as environmental chemistry, geochemistry, and materials science. Developments in signal processing of extended X-ray absorption fine structure (EXAFS) data, such as wavelet transformation (WT), have been used to identify transition metals and Al present in the hydroxide sheets of LDHs. The WT plots of LDHs should be distinct from those of isostructural single metal hydroxides. However, no direct comparison of these minerals appears in the literature using WT. This work systematically analyzes a suite of Ni-rich mineral standards, including Ni–Al LDHs, single metal Ni hydroxides, and Ni-rich silicates using WT. The results illustrate that the WT plots for α-Ni(OH)2 and Ni–Al LDHs are often indistinguishable from each other, with similar two-component plots for the different mineral types. This demonstrates that the WT of the first metal shell often cannot be used to differentiate an LDH from a single metal hydroxide. Interlayer anions adsorbed to the hydroxide sheet of α-Ni(OH)2 affect the EXAFS spectra and are not visible in the FT but are clearly resolved and discrete in the WT.

  18. Structural and magnetic properties of Ni-Zn doped BaM nanocomposite via citrate precursor

    International Nuclear Information System (INIS)

    Rana, Kush; Thakur, Preeti; Thakur, Atul; Tomar, Monika; Gupta, Vinay

    2016-01-01

    Ni-Zn substituted M-type barium ferrite nanocomposite has been prepared via citrate precursor method. Nanocomposite having composition BaNi_0_._5Zn_0_._5Fe_1_1O_1_9 was sintered at 900°C for 3hrs and characterized by using different characterization techniques. X-ray diffraction (XRD) confirmed the formation of double phase with most prominent peak at (114). Average crystallite size for pure BaM and BNZFO were found to be 36 nm & 45 nm. Field emission scanning electron microscopy (FESEM) confirmed the formation of hexagonal platelets with a layered structure. Magnetic properties of these samples were investigated by using vibrating sample magnetometer (VSM). Magnetic parameters like saturation magnetization (M_s), coericivity (H_c) and squareness ratio (SQR) of nanocomposite were found to be 60 emu/g, 3663 Oe and 0.6163 respectively. These values were noticed to be higher as compared to pure BaM. Enhanced magnetic properties of nanocomposite were strongly dependent on exchange coupling. Therefore these properties make this nanocomposite a suitable candidate for magnetic recording and high frequency applications.

  19. The Ni-YSZ interface

    DEFF Research Database (Denmark)

    Jensen, Karin Vels

    The anode/electrolyte interface in solid oxide fuel cells (SOFC) is known to cause electrical losses. Geometrically simple Ni/yttria-stabilised zirconia (YSZ) interfaces were examined to gain information on the structural and chemical changes occurring during experiments at 1000°C in an atmosphere...... of 97% H2/3% H2O. Electrochemical impedance spectroscopy at open circuit voltage (OCV) and at anodic and cathodic polarisations (100 mV) was performed. A correlation of the electrical data with the structure development and the chemical composition was attempted. Nickel wires with different impurity...... between polarised and non-polarised samples. With pure nickel wires, however, the microstructures depended on the polarisation/non-polarisation conditions. At non-polarised conditions a hill and valley type structure was found. Anodic polarisation produced an up to 1 μm thick interface layer consisting...

  20. High Efficiency MAPbI3 Perovskite Solar Cell Using a Pure Thin Film of Polyoxometalate as Scaffold Layer.

    Science.gov (United States)

    Sardashti, Mohammad Khaledi; Zendehdel, Mahmoud; Nia, Narges Yaghoobi; Karimian, Davud; Sheikhi, Mohammad

    2017-10-09

    Here, we successfully used a pure layer of [SiW 11 O 39 ] 8- polyoxomethalate (POM) structure as a thin-film scaffold layer for CH 3 NH 3 PbI 3 -based perovskite solar cells (PSCs). A smooth nanoporous surface of POM causes outstanding improvement of the photocurrent density, external quantum efficiency (EQE), and overall efficiency of the PSCs compared to mesoporous TiO 2 (mp-TiO 2 ) as scaffold layer. Average power conversion efficiency (PCE) values of 15.5 % with the champion device showing 16.3 % could be achieved by using POM and a sequential deposition method with the perovskite layer. Furthermore, modified and defect-free POM/perovskite interface led to elimination of the anomalous hysteresis in the current-voltage curves. The open-circuit voltage decay study shows promising decrease of the electron recombination in the POM-based PSCs, which is also related to the modification of the POM/ perovskite interface and higher electron transport inside the POM layer. © 2017 Wiley-VCH Verlag GmbH & Co. KGaA, Weinheim.

  1. Electrosynthesized Ni-Al Layered Double Hydroxide-Pt Nanoparticles as an Inorganic Nanocomposite and Potentate Anodic Material for Methanol Electrooxidation in Alkaline Media

    Directory of Open Access Journals (Sweden)

    Biuck Habibi

    2017-04-01

    Full Text Available In this study, Ni-Al layered double hydroxide (LDH-Pt nanoparticles (PtNPs as an inorganic nano-composite was electrosynthesized on the glassy carbon electrode (GCE by a facile and fast two-step electrochemical process. Structure and physicochemical properties of PtNPs/Ni-Al LDH/GCE were characterized by X-ray diffraction, scanning electron microscopy, energy dispersive X-ray spectrometry and electrochemical methods. Then, electrocatalytic and stability characterizations of the PtNPs/Ni-Al LDH/GCE for methanol oxidation in alkaline media were investigated in detail by cyclic voltammetry, chronoamperometry, and chronopotentiometry measurements. PtNPs/Ni-Al LDH/GCE exhibited higher electrocatalytic activity than PtNPs/GCE and Ni-Al LDH/GCE. Also, the resulted chronoam-perograms indicated that the PtNPs/Ni-Al LDH/GCE has a better stability. Copyright © 2017 BCREC GROUP. All rights reserved Received: 30th March 2016; Revised: 29th July 2016; Accepted: 9th September 2016 How to Cite: Habibi, B., Ghaderi, S. (2017. Electro Synthesized Ni-Al Layered Double Hydroxide-Pt Nanoparticles as an Inorganic Nanocomposite and Potentate Anodic Material for Methanol Electro-Oxidation in Alkaline Media. Bulletin of Chemical Reaction Engineering & Catalysis, 12(1: 1-13 (doi:10.9767/bcrec.12.1.460.1-13 Permalink/DOI: http://dx.doi.org/10.9767/bcrec.12.1.460.1-13

  2. Shot Peening Effects on Subsurface Layer Properties and Fatigue Performance of Case-Hardened 18CrNiMo7-6 Steel

    Directory of Open Access Journals (Sweden)

    H. S. Ho

    2018-01-01

    Full Text Available The present study is conducted with a dual-aim: firstly, to examine the effect of several single shot peening conditions on the subsurface layer properties and fatigue performance of the case-hardened 18CrNiMo7-6 steel, and secondly, to propose an optimized peening condition for improved fatigue performance. By carrying out the subsurface integrity analysis and fatigue testing, the underlying relationships among the peening process, subsurface layer property and fatigue performance are investigated, the way peening conditions affect the fatigue life and its associated scatter for the case-hardened 18CrNiMo7-6 steel is quantitatively assessed. The in-depth study shows that dual peening can be an optimized solution, for it is able to produce a subsurface layer with enhanced properties and eventually gain a significant improvement in fatigue performance.

  3. Electroplated Ni on the PN Junction Semiconductor

    Energy Technology Data Exchange (ETDEWEB)

    Kim, Jin Joo; Uhm, Young Rang; Son, Kwang Jae; Kim, Jong Bum; Choi, Sang Moo; Park, Jong Han; Hong, Jintae [Korea Atomic Energy Research Institute, Daejeon (Korea, Republic of)

    2015-05-15

    Nickel (Ni) electroplating was implemented by using a metal Ni powder in order to establish a Ni-63 plating condition on the PN junction semiconductor needed for production of betavoltaic battery. PN junction semiconductors with a Ni seed layer of 500 and 1000 A were coated with Ni at current density from 10 to 50 mA cm{sup 2}. The surface roughness and average grain size of Ni deposits were investigated by XRD and SEM techniques. The roughness of Ni deposit was increased as the current density was increased, and decreased as the thickness of Ni seed layer was increased.

  4. Electroplated Ni on the PN Junction Semiconductor

    International Nuclear Information System (INIS)

    Kim, Jin Joo; Uhm, Young Rang; Son, Kwang Jae; Kim, Jong Bum; Choi, Sang Moo; Park, Jong Han; Hong, Jintae

    2015-01-01

    Nickel (Ni) electroplating was implemented by using a metal Ni powder in order to establish a Ni-63 plating condition on the PN junction semiconductor needed for production of betavoltaic battery. PN junction semiconductors with a Ni seed layer of 500 and 1000 A were coated with Ni at current density from 10 to 50 mA cm 2 . The surface roughness and average grain size of Ni deposits were investigated by XRD and SEM techniques. The roughness of Ni deposit was increased as the current density was increased, and decreased as the thickness of Ni seed layer was increased

  5. Ni-YSZ graded coatings produced by dipping

    International Nuclear Information System (INIS)

    Ferrari, B.; Moreno, R.

    2004-01-01

    A new colloidal processing route for the shaping of a graded Ni-YSZ composite for applications in SOFC devices is described. A Ni foil is coated by Ni/YSZ layers by dipping in aqueous suspensions with an organic binder. Behind the metal-ceramic layers introduced to improve adhesion, an outer thin layer of nanosized YSZ is formed by electrophoretic deposition. (Abstract Copyright [2004], Wiley Periodicals, Inc.)

  6. Development of efficient electrocatalysts via molecular hybridization of NiMn layered double hydroxide nanosheets and graphene

    Science.gov (United States)

    Ma, Wei; Ma, Renzhi; Wu, Jinghua; Sun, Pengzhan; Liu, Xiaohe; Zhou, Kechao; Sasaki, Takayoshi

    2016-05-01

    Ni2+Mn3+ layered double hydroxide (LDH) nanoplatelets have been hydrothermally synthesized in a homogeneous precipitation of mixed Ni2+/Mn2+ salts at a molar ratio of 2 : 1 via the hydrolysis of hexamethylenetetramine (HMT) and in situ oxidation with H2O2. After anion-exchange, NiMn LDH was exfoliated into unilamellar nanosheets. Subsequent flocculation of NiMn LDH nanosheets with (reduced) graphene oxide (GO/rGO) into superlattice composites was achieved and further tested as electrocatalysts for oxygen evolution reaction (OER). The face-to-face heteroassembly of NiMn LDH nanosheets with conductive rGO at an alternating sequence resulted in a small overpotential of 0.26 V and a Tafel slope of 46 mV per decade, which is much superior to as-exfoliated nanosheets. The analyses of electrochemical activity surface area (ECSA) and impedance spectra clearly indicated that the superlattice structure was ideal in facilitating the migration/transfer of the charge and reactants, revealing the electrochemical energetics and mechanism behind the synergistic effect arising from molecular hybridization. The proof of concept toward total water splitting using the newly developed hybrid electrocatalyst was demonstrated by an electrolysis cell powered by a single AA battery.Ni2+Mn3+ layered double hydroxide (LDH) nanoplatelets have been hydrothermally synthesized in a homogeneous precipitation of mixed Ni2+/Mn2+ salts at a molar ratio of 2 : 1 via the hydrolysis of hexamethylenetetramine (HMT) and in situ oxidation with H2O2. After anion-exchange, NiMn LDH was exfoliated into unilamellar nanosheets. Subsequent flocculation of NiMn LDH nanosheets with (reduced) graphene oxide (GO/rGO) into superlattice composites was achieved and further tested as electrocatalysts for oxygen evolution reaction (OER). The face-to-face heteroassembly of NiMn LDH nanosheets with conductive rGO at an alternating sequence resulted in a small overpotential of 0.26 V and a Tafel slope of 46 mV per decade

  7. Intercalation of Molybdate Ions into Ni/Zn Layered Double Hydroxide Salts: Synthesis, Characterization, and Preliminary Catalytic Activity in Methyl Transesterification of Soybean Oil

    OpenAIRE

    Colombo, Kamila; Maruyama, Swami A.; Yamamoto, Carlos I.; Wypych, Fernando

    2017-01-01

    This study reports the synthesis and characterization of a Ni/Zn layered double hydroxide salt intercalated with acetate ions and the subsequent replacement of the acetate ions with molybdate ions via an ion exchange reaction, conducted at two different pH values. Regardless of the pH employed during the synthesis, the basal spacing in the Ni/Zn layered double hydroxide salt decreased from 13.08 Å to approximately 9.5 Å, which agreed with intercalation of hydrated molybdate anions. The non-ca...

  8. Study of the electroplated of Ni for betavoltaic battery using PN junction without seed layer

    Energy Technology Data Exchange (ETDEWEB)

    Uhm, Young Rang; Kim, Jong Bum; Son, Kwang Jae [Korea Atomic Energy Research Institute, Daejeon (Korea, Republic of); Cho, Byoung Gun [Electronics and Telecommunications Research Institute, Daejeon (Korea, Republic of)

    2015-10-15

    The mechanism of a nuclear battery is same as the P.N junction diode for solar cell application. The photovoltaic is operated by converting photons into electrical energy in the junction. In a betavoltaic battery, beta particles are collected and converted into electrical energy with a similar principle as a photovoltaic. If a radioisotope (RI) with a long half-life (over 100 years) is used, the lifetime of the power source is extended to as long as the half-life time of the RI. Hence, the power sources we describe could extend a system's operating life by several decades or even a century, during which time the system can gain learned behavior without worrying about the power turning off. The beta spectrum of {sup 63}Ni is below the radiation damage threshold (approximately 200 keV for Si) of semiconductors such as Si and SiC. Beta particles of 63Ni were deposited by electroplating on the Ni-foil substrate and attached on the trench P-N absorber with a spacing of 50 μm. The optimum total thickness of the 63Ni layer was determined to be about 2 μm, when regarding the minimum self-shielding effect of the beta-ray (β-ray). The optimum condition of the electroplating {sup 63}Ni was determined at current density of 20 mA/cm{sup 2}.

  9. Study of the electroplated of Ni for betavoltaic battery using PN junction without seed layer

    International Nuclear Information System (INIS)

    Uhm, Young Rang; Kim, Jong Bum; Son, Kwang Jae; Cho, Byoung Gun

    2015-01-01

    The mechanism of a nuclear battery is same as the P.N junction diode for solar cell application. The photovoltaic is operated by converting photons into electrical energy in the junction. In a betavoltaic battery, beta particles are collected and converted into electrical energy with a similar principle as a photovoltaic. If a radioisotope (RI) with a long half-life (over 100 years) is used, the lifetime of the power source is extended to as long as the half-life time of the RI. Hence, the power sources we describe could extend a system's operating life by several decades or even a century, during which time the system can gain learned behavior without worrying about the power turning off. The beta spectrum of 63 Ni is below the radiation damage threshold (approximately 200 keV for Si) of semiconductors such as Si and SiC. Beta particles of 63Ni were deposited by electroplating on the Ni-foil substrate and attached on the trench P-N absorber with a spacing of 50 μm. The optimum total thickness of the 63Ni layer was determined to be about 2 μm, when regarding the minimum self-shielding effect of the beta-ray (β-ray). The optimum condition of the electroplating 63 Ni was determined at current density of 20 mA/cm 2

  10. Structural, vibrational and morphological properties of layered double hydroxides containing Ni{sup 2+}, Zn{sup 2+}, Al{sup 3+} and Zr{sup 4+} cations

    Energy Technology Data Exchange (ETDEWEB)

    Bezerra, Débora M. [Instituto de Química de São Carlos, Universidade de São Paulo, CP 780, CEP 13566-590 São Carlos, SP (Brazil); Rodrigues, João E.F.S. [Instituto de Física de São Carlos, Universidade de São Paulo, CP 780, CEP 13560-970 São Carlos, SP (Brazil); Assaf, Elisabete M., E-mail: eassaf@iqsc.usp.br [Instituto de Química de São Carlos, Universidade de São Paulo, CP 780, CEP 13566-590 São Carlos, SP (Brazil)

    2017-03-15

    Layered double hydroxides are anionic clays with formula [M{sup II}{sub 1−x} M{sup III}{sub x}(OH){sub 2}]{sup q+}[A{sup n−}]{sub q/n}·mH{sub 2}O, finding possible uses as catalyst support, adsorbents and so on. In this paper, we address the phase formation of layered double hydroxides containing Ni{sup 2+}, Zn{sup 2+}, Al{sup 3+} and Zr{sup 4+} cations, namely, NiZn-Al, NiZn-AlZr and NiZn-Zr compositions obtained by the coprecipitation method. Such systems were characterized by X-ray diffraction, confirming the phase formation for NiZn-Al and NiZn-AlZr samples. Infrared and Raman spectroscopies elucidated the anion and water molecules occurrence in the interlayer. Nitrogen physisorption (BET method) determined the presence of pores and specific surface area. The isotherm shapes were Type IV, according to the IUPAC, and represent a mesoporous structure. A morphological study was performed by means of scanning and transmission electron microscopies, and particle size values of 120, 131 and 235 nm for NiZn-Al, NiZn-AlZr and NiZn-Zr, respectively, were determined. Thermogravimetric analysis of the decomposition of the systems revealed that their complete disintegration occurred at ~ 450 °C and resulted in mixed oxides.

  11. A purely nonlinear route to transition approaching the edge of chaos in a boundary layer

    International Nuclear Information System (INIS)

    Cherubini, S; De Palma, P; Robinet, J-Ch; Bottaro, A

    2012-01-01

    The understanding of transition in shear flows has recently progressed along new paradigms based on the central role of coherent flow structures and their nonlinear interactions. We follow such paradigms to identify, by means of a nonlinear optimization of the energy growth at short time, the initial perturbation which most easily induces transition in a boundary layer. Moreover, a bisection procedure has been used to identify localized flow structures living on the edge of chaos, found to be populated by hairpin vortices and streaks. Such an edge structure appears to act as a relative attractor for the trajectory of the laminar base state perturbed by the initial finite-amplitude disturbances, mediating the route to turbulence of the flow, via the triggering of a regeneration cycle of Λ and hairpin structures at different space and time scales. These findings introduce a new, purely nonlinear scenario of transition in a boundary-layer flow. (paper)

  12. Effects of Ni particle morphology on cell performance of Na/NiCl2 battery

    Science.gov (United States)

    Kim, Mangi; Ahn, Cheol-Woo; Hahn, Byung-Dong; Jung, Keeyoung; Park, Yoon-Cheol; Cho, Nam-ung; Lee, Heesoo; Choi, Joon-Hwan

    2017-11-01

    Electrochemical reaction of Ni particle, one of active cathode materials in the Na/NiCl2 battery, occurs on the particle surface. The NiCl2 layer formed on the Ni particle surface during charging can disconnect the electron conduction path through Ni particles because the NiCl2 layer has very low conductivity. The morphology and size of Ni particles, therefore, need to be controlled to obtain high charge capacity and excellent cyclic retention. Effects of the Ni particle size on the cell performance were investigated using spherical Ni particles with diameters of 0.5 μm, 6 μm, and 50 μm. The charge capacities of the cells with spherical Ni particles increased when the Ni particle size becomes smaller because of their higher surface area but their charge capacities were significantly decreased with increasing cyclic tests owing to the disconnection of electron conduction path. The inferior cyclic retention of charge capacity was improved using reticular Ni particles which maintained the reliable connection for the electron conduction in the Na/NiCl2 battery. The charge capacity of the cell with the reticular Ni particles was higher than the cell with the small-sized spherical Ni particles approximately by 26% at 30th cycle.

  13. Role of Ta-spacer layer on tuning the tilt angle magnetic anisotropy of L1{sub 1}-CoPt/Ta/NiFe exchange springs

    Energy Technology Data Exchange (ETDEWEB)

    Saravanan, P., E-mail: psdrdo@gmail.com [Defence Metallurgical Research Laboratory, Hyderabad 500058 (India); Talapatra, A.; Mohanty, J. [Department of Physics, Indian Institute of Technology Hyderabad, Hyderabad 502285 (India); Hsu, Jen-Hwa, E-mail: jhhsu@phys.ntu.edu.tw [Department of Physics, National Taiwan University, Taipei 106, Taiwan (China); Kamat, S.V. [Defence Metallurgical Research Laboratory, Hyderabad 500058 (India)

    2017-06-15

    Highlights: • Role of Ta-spacer layer in L1{sub 1}-CoPt(10 nm)/Ta//NiFe(4 nm) trilayers was investigated. • Domain size increased at the expense of magnetic phase contrast with increasing t{sub Ta}. • Tilt angle magnetization increased from 43° to 77° upon increasing t{sub Ta} (0–2.5 nm). • Micromagnetic studies confirmed the existence of tilted magnetic anisotropy. • Ta-spacer is effective in preserving competing anisotropies of CoPt and NiFe-layers. - Abstract: L1{sub 1}-CoPt/Ta/NiFe trilayers are chosen as model films for probing the role of spacer layer on tuning the tilt angle magnetization (θ{sub M}) in such exchange springs. For this purpose, a non-magnetic layer (Ta) with varying thickness (t{sub Ta}) from 0 to 2.5 nm was inserted between 10-nm thick CoPt film exhibiting strong perpendicular magnetic anisotropy (PMA) and 4-nm thick NiFe film having in-plane magnetic anisotropy (IMA). With the insertion of Ta-spacer, the magnetic hysteresis loops become more and more tilted as t{sub Ta} increases. Upon increasing the t{sub Ta} from 0 to 2.5 nm, the estimated SQR{sub ⊥} (=M{sub r⊥}/M{sub s⊥}) from the M–H loops is found to decrease moderately; while the θ{sub M} increases significantly from 43° to 77°. MFM images revealed maze-like domain patterns and the domain size tends to increase at the expense of magnetic phase contrast with increasing t{sub Ta}. Micro-magnetic simulation of tilt in the anisotropy axis with respect to the bare CoPt-layer showed a trend similar to that of those observed with the M–H loops obtained by VSM measurements. The results of present study suggest that the insertion of Ta-spacer is not only beneficial in terms of preserving the competing anisotropies such as PMA and IMA of CoPt and NiFe-layers respectively through weakened exchange coupling; but also, act as an appropriate means for realizing tunable tilted magnetic anisotropy in the L1{sub 1}-CoPt/NiFe exchange springs.

  14. Suppression of dilution in Ni-Cr-Si-B alloy cladding layer by controlling diode laser beam profile

    Science.gov (United States)

    Tanigawa, Daichi; Funada, Yoshinori; Abe, Nobuyuki; Tsukamoto, Masahiro; Hayashi, Yoshihiko; Yamazaki, Hiroyuki; Tatsumi, Yoshihiro; Yoneyama, Mikio

    2018-02-01

    A Ni-Cr-Si-B alloy layer was produced on a type 304 stainless steel plate by laser cladding. In order to produce cladding layer with smooth surface and low dilution, influence of laser beam profile on cladding layer was investigated. A laser beam with a constant spatial intensity at the focus spot was used to suppress droplet formation during the cladding layer formation. This line spot, formed with a focussing unit designed by our group, suppressed droplet generation. The layer formed using this line spot with a constant spatial intensity had a much smoother surface compared to a layer formed using a line spot with a Gaussian-like beam. In addition, the dilution of the former layer was much smaller. These results indicated that a line spot with a constant spatial intensity was more effective in producing a cladding layer with smooth surface and low dilution because it suppressed droplet generation.

  15. The Electrochemical Atomic Layer Deposition of Pt and Pd nanoparticles on Ni foam for the electrooxidation of alcohols

    CSIR Research Space (South Africa)

    Modibedi, RM

    2012-10-01

    Full Text Available Electrodeposition of Pt and Pd metal by surface limited redox replacement reactions was performed using the electrochemical atomic layer deposition. Carbon paper and Ni foam were used as substrates for metal deposition. Supported Pt and Pd...

  16. Analysis of phase formation in Ni-rich alloys of the Ni-Ta-W system by calorimetry, DTA, SEM, and TEM

    Energy Technology Data Exchange (ETDEWEB)

    Witusiewicz, V.T.; Hecht, U.; Warnken, N.; Fries, S.G. [Access e.V., Aachen (Germany); Hu Weiping [Inst. fuer Metallkunde und Metallphysik der RWTH Aachen (Germany)

    2006-04-15

    The partial enthalpies of dissolution of pure Ni, W and Ta in liquid ternary Ni-Ta-W alloys have been determined at (1773 {+-} 5) K using a high temperature isoperibolic calorimeter. Measurements were performed in Ni-rich alloys (from 80 to 100 at.% Ni) along sections with constant Ta:W atomic ratios 1:0, 2:1, 1:2, and 0:1. The partial enthalpies and thereby the integral enthalpy of mixing of these ternary alloys are calculated from the partial enthalpies of dissolution using SGTE Gibbs energies for pure elements as reference. The obtained thermochemical data confirm that in the investigated Ni-rich alloys the binary interactions between Ta and W as well as the ternary Ni-Ta-W interactions are negligibly small. Due to this the variation of the integral enthalpy of mixing of the ternary alloys is well described as linear combination of the constituent Ni-Ta and Ni-W binaries. Such behaviour of the ternary liquid alloys is related to a very low probability of new ternary stable phases to occur in solid state. This prediction is confirmed by differential thermal analysis, scanning electron microscopy, and transmission electron microscopy of the as-solidified and annealed samples obtained as last alloy compositions in the series of calorimetric dissolution. (orig.)

  17. Vacancies supersaturation induced by fast neutronn irradiation in FeNi alloys

    International Nuclear Information System (INIS)

    Lucki, G.; Watanabe, S.; Chambron, W.; Verdoni, J.

    1976-01-01

    Isothermal annealings have been performed between 400 and 555 0 C with and without fast neutron (1 MeV) irradiation. Pure FeNi (50-50 at %) was irradiated in the Melousine reactor in Grenoble and FeNiMO (50-50 at % + 50 ppm.) in the IEAR 1 reactor at the Instituto de Energia Atomica in Sao Paulo. The toroidal shaped specimens were fabricated from Johnson Mathey zone refined ingots and were initially annealed at 800 0 C during 1 h in hydrogen atmosphere and then slowly cooled (4 h) inside the furnace. Magnetic After Effect Measurements (MAE) permitted the evaluation of activation energies during fast neutron irradiation (1.54eV) and without irradiation (3.14eV) for pure FeNi and respectively (1.36eV) and 2.32eV) for FeNiMO. Since the time constants of relaxation process are inversely proportional to the vacancies comcentration a quantitative evaluation of vacancies supersaturation was made it decreases from value 700 at 410 0 C to the value 40 at 190 0 C for pure FeNi and from 765 to 121 for FeNiMO in the same temperature range

  18. Evaluation of alloying effect on the formation of Ni-Fe nanosized powders by pulsed wire discharge

    International Nuclear Information System (INIS)

    Park, Gyu-Hyeon; Lee, Gwang-Yeob; Kim, Hyeon-Ah; Lee, A-Young; Oh, Hye-Ryeong; Kim, Song-Yi; Kim, Do-Hyang; Lee, Min-Ha

    2016-01-01

    Highlights: • Synthesizing Ni-Fe alloy nano-powder employing Ni-plating layer of Fe wire by PWD process. • The mean particle size is decreased with increasing the charging voltage affecting to the super heating factor (K). • The mean particle size of PWD Ni-Fe nanosized powder is accordance with applied voltage. • Uniformity of mean particel size can be controlled by adjusting charging voltage and super heating factor (K). - Abstract: This study investigates the effects of varying the explosion time and charging voltage of pulsed wire discharge (PWD) on the mean particle size, dispersibility and alloying reliability of powders produced from pure Ni and Ni-plated Fe wires. It was found that with increasing charging voltage, the mean particle size of Ni powders is reduced from 40.11 ± 0.23 to 25.63 ± 0.07 nm, which is attributed to a change in the extent of super heating with particle size. Nanosized powders of Ni-Fe alloy with a mean particle size between 25.91 ± 0.24 and 26.30 ± 0.26 nm were also successfully fabricated and found to consist of particles with a γ-(Ni/Fe) core and FeO shell. The reliability for the optimization of processing parameters to control particle sizes is also evaluated.

  19. Evaluation of alloying effect on the formation of Ni-Fe nanosized powders by pulsed wire discharge

    Energy Technology Data Exchange (ETDEWEB)

    Park, Gyu-Hyeon [Advanced Functional Materials R& D Group, Korea Institute of Industrial Technology, Incheon 406-840 (Korea, Republic of); Lee, Gwang-Yeob [Advanced Analysis Center, Korea Institute of Science and Technology, Seoul 136-791 (Korea, Republic of); Deparment of Advanced Materials Engineering, Yonsei University, Seoul 120-749 (Korea, Republic of); Kim, Hyeon-Ah [Advanced Functional Materials R& D Group, Korea Institute of Industrial Technology, Incheon 406-840 (Korea, Republic of); Deparment of Advanced Materials Engineering, Yonsei University, Seoul 120-749 (Korea, Republic of); Lee, A-Young; Oh, Hye-Ryeong; Kim, Song-Yi [Advanced Functional Materials R& D Group, Korea Institute of Industrial Technology, Incheon 406-840 (Korea, Republic of); Kim, Do-Hyang [Deparment of Advanced Materials Engineering, Yonsei University, Seoul 120-749 (Korea, Republic of); Lee, Min-Ha, E-mail: mhlee1@kitech.re.kr [Advanced Functional Materials R& D Group, Korea Institute of Industrial Technology, Incheon 406-840 (Korea, Republic of)

    2016-10-15

    Highlights: • Synthesizing Ni-Fe alloy nano-powder employing Ni-plating layer of Fe wire by PWD process. • The mean particle size is decreased with increasing the charging voltage affecting to the super heating factor (K). • The mean particle size of PWD Ni-Fe nanosized powder is accordance with applied voltage. • Uniformity of mean particel size can be controlled by adjusting charging voltage and super heating factor (K). - Abstract: This study investigates the effects of varying the explosion time and charging voltage of pulsed wire discharge (PWD) on the mean particle size, dispersibility and alloying reliability of powders produced from pure Ni and Ni-plated Fe wires. It was found that with increasing charging voltage, the mean particle size of Ni powders is reduced from 40.11 ± 0.23 to 25.63 ± 0.07 nm, which is attributed to a change in the extent of super heating with particle size. Nanosized powders of Ni-Fe alloy with a mean particle size between 25.91 ± 0.24 and 26.30 ± 0.26 nm were also successfully fabricated and found to consist of particles with a γ-(Ni/Fe) core and FeO shell. The reliability for the optimization of processing parameters to control particle sizes is also evaluated.

  20. Synthesis of Ni core NiO shell nanostructure and magnetic investigation for shell thickness determination

    International Nuclear Information System (INIS)

    Arabi, H.; Bruck, E.; Tichelaar, F.D.

    2007-01-01

    Full text: Nickel oxide has received a considerable amount of attention in recent years for its catalytic, electronic and magnetic properties. Ni nanoparticles with an average size of 8 nm were prepared by dc - arc discharge in argon atmosphere. A current of 130 A and 300 milli bar pressure of argon have been applied. The produced Ni nanoparticles were annealed for oxidizing in air at 350 for six hours to produce antiferromagnetic NiO particles. The structure of Ni and NiO nanoparticles and size estimation of them studied by means of X-ray diffraction. The size and morphology of the particles were also characterized by high resolution transmission microscopy (TEM). The Ni core NiO shell structure, resulting from the oxidation process, were studied by magnetic properties measurements. A quantum design squid magnetometer, model MPMS5S was used for measuring saturation magnetization of both nanoparticles of Ni with and without NiO layer. By knowing the density of Ni and NiO, we were able to deduce the thickness of the Ni core and NiO outer layer. They are around 3 and 5 nanometers respectively. (authors)

  1. Structure characterization of Ni/NiO and Ti/TiO2 interfaces

    International Nuclear Information System (INIS)

    Lamine, Brahim

    1983-01-01

    This research thesis reports the structure characterization of Ni-NiO and Ti-TiO 2 interfaces through an in-situ investigation of thin blade oxidation, of oxide germination and growth, and through a determination of mutual metal/oxide orientation relationships. Thin films of TiO 2 have also been characterized and the study of the influence of vacuum annealing on TiO 2 layer structure and morphology has been attempted. The examination of metal-oxide interface reveals a duplex structure of NiO and TiO 2 layers, and a preferential grain boundary oxidation of the underlying metal [fr

  2. Potentiostatically deposited nanostructured Co{sub x}Ni{sub 1-x} layered double hydroxides as electrode materials for redox-supercapacitors

    Energy Technology Data Exchange (ETDEWEB)

    Gupta, Vinay [Art, Science and Technology Center for Cooperative Research, Kyushu University, Kasuga-shi, Fukuoka 816-8580 (Japan); Japan Science and Technology Agency, Kawaguchi-shi, Saitama 332-0012 (Japan); Gupta, Shubhra; Miura, Norio [Art, Science and Technology Center for Cooperative Research, Kyushu University, Kasuga-shi, Fukuoka 816-8580 (Japan)

    2008-01-03

    Cobalt-nickel layered double hydroxides (Co{sub x}Ni{sub 1-x} LDHs) were deposited onto stainless steel electrodes by the potentiostatic deposition method at -1.0 V vs. Ag/AgCl using various molar ratios of Co(NO{sub 3}){sub 2} and Ni(NO{sub 3}){sub 2} in distilled water. Their structure and surface morphology were studied by using X-ray diffraction analysis, energy dispersive X-ray spectroscopy and scanning electron microscopy. A network of Co{sub x}Ni{sub 1-x} LDH nanosheets was obtained. The nature of the cyclic voltammetry and charge-discharge curves suggested that the Co{sub x}Ni{sub 1-x} LDHs exist in the form of solid solutions. The capacitive characteristics of the Co{sub x}Ni{sub 1-x} LDHs in 1 M KOH electrolyte showed that Co{sub 0.72}Ni{sub 0.28} LDHs had the highest specific capacitance value, 2104 F g{sup -1}, which is also the highest yet reported value for oxide materials in general. (author)

  3. Formation of anomalous eutectic in Ni-Sn alloy by laser cladding

    Science.gov (United States)

    Wang, Zhitai; Lin, Xin; Cao, Yongqing; Liu, Fencheng; Huang, Weidong

    2018-02-01

    Ni-Sn anomalous eutectic is obtained by single track laser cladding with the scanning velocity from 1 mm/s to 10 mm/s using the Ni-32.5 wt.%Sn eutectic powders. The microstructure of the cladding layer and the grain orientations of anomalous eutectic were investigated. It is found that the microstructure is transformed from primary α-Ni dendrites and the interdendritic (α-Ni + Ni3Sn) eutectic at the bottom of the cladding layer to α-Ni and β-Ni3Sn anomalous eutectic at the top of the cladding layer, whether for single layer or multilayer laser cladding. The EBSD maps and pole figures indicate that the spatially structure of α-Ni phase is discontinuous and the Ni3Sn phase is continuous in anomalous eutectic. The transformation from epitaxial growth columnar at bottom of cladding layer to free nucleation equiaxed at the top occurs, i.e., the columnar to equiaxed transition (CET) at the top of cladding layer during laser cladding processing leads to the generation of anomalous eutectic.

  4. Ni Foam-Ni3 S2 @Ni(OH)2 -Graphene Sandwich Structure Electrode Materials: Facile Synthesis and High Supercapacitor Performance.

    Science.gov (United States)

    Wang, Xiaobing; Hu, Jiangjiang; Su, Yichang; Hao, Jin; Liu, Fanggang; Han, Shuang; An, Jian; Lian, Jianshe

    2017-03-23

    A novel Ni foam-Ni 3 S 2 @Ni(OH) 2 -graphene sandwich-structured electrode (NF-NN-G) with high areal mass loading (8.33 mg cm -2 ) has been developed by sulfidation and hydrolysis reactions. The conductivity of Ni 3 S 2 and Ni(OH) 2 were both improved. The upper layer of Ni(OH) 2 , covered with a thin graphene film, is formed in situ from the surface of the lower layer of Ni 3 S 2 , whereas the Ni 3 S 2 grown on Ni foam substrate mainly acts as a rough support bridging the Ni(OH) 2 and Ni foam. The graphene stabilized the Ni(OH) 2 and the electrochemical properties were effectively enhanced. The as-synthesized NF-NN-G-5mg electrode shows a high specific capacitance (2258 F g -1 at 1 A g -1 or 18.81 F cm -2 at 8.33 mA cm -2 ) and an outstanding rate property (1010 F g -1 at 20 Ag -1 or 8.413 F cm -2 at 166.6 mA cm -2 ). This result is around double the capacitance achieved in previous research on Ni 3 S 2 @Ni(OH) 2 /3DGN composites (3DGN=three-dimensional graphene network). In addition, the as-fabricated NF-NN-G-5mg composite electrode has an excellent cycle life with no capacitance loss after 3000 cycles, indicating a potential application as an efficient electrode. © 2017 Wiley-VCH Verlag GmbH & Co. KGaA, Weinheim.

  5. One dimensional motion of interstitial clusters and void growth in Ni and Ni alloys

    Science.gov (United States)

    Yoshiie, T.; Ishizaki, T.; Xu, Q.; Satoh, Y.; Kiritani, M.

    2002-12-01

    One dimensional (1-D) motion of interstitial clusters is important for the microstructural evolution in metals. In this paper, the effect of 2 at.% alloying with elements Si (volume size factor to Ni: -5.81%), Cu (7.18%), Ge (14.76%) and Sn (74.08%) in Ni on 1-D motion of interstitial clusters and void growth was studied. In neutron irradiated pure Ni, Ni-Cu and Ni-Ge, well developed dislocation networks and voids in the matrix, and no defects near grain boundaries were observed at 573 K to a dose of 0.4 dpa by transmission electron microscopy. No voids were formed and only interstitial type dislocation loops were observed near grain boundaries in Ni-Si and Ni-Sn. The reaction kinetics analysis which included the point defect flow into planar sink revealed the existence of 1-D motion of interstitial clusters in Ni, Ni-Cu and Ni-Ge, and lack of such motion in Ni-Si and Ni-Sn. In Ni-Sn and Ni-Si, the alloying elements will trap interstitial clusters and thereby reduce the cluster mobility, which lead to the reduction in void growth.

  6. Influence of SLM on compressive response of NiTi scaffolds

    Science.gov (United States)

    Shayesteh Moghaddam, Narges; Saedi, Soheil; Amerinatanzi, Amirhesam; Jahadakbar, Ahmadreza; Saghaian, Ehsan; Karaca, Haluk; Elahinia, Mohammad

    2018-03-01

    Porous Nickel-Titanium shape memory alloys (NiTi-SMAs) have attracted much attention in biomedical applications due to their high range of pure elastic deformability (i.e., superelasticity) as well as their bone-level modulus of elasticity (E≈12-20 GPa). In recent years, Selective Laser Melting (SLM) has been used to produce complex NiTi components. The focus of this study is to investigate the superelasticity and compressive properties of SLM NiTi-SMAs. To this aim, several NiTi components with different level of porosities (32- 58%) were fabricated from Ni50.8Ti (at. %) powder via SLM PXM by Phenix/3D Systems, using optimum processing parameter (Laser power-P=250 W, scanning speed-v=1250mm/s, hatch spacing-h=120μm, layer thickness-t=30μm). To tailor the superelasticity behavior at body temperature, the samples were solution annealed and aged for 15 min at 350°C. Then, transformation temperatures (TTs), superelastic response, and cyclic behavior of NiTi samples were studied. As the porosity was increased, the irrecoverable strain was observed to be higher in the samples. At the first superelastic cycle, 3.5%, 3.5%, and 2.7% strain recovery were observed for the porosity levels of 32%, 45%, and 58%, respectively. However, after 10 cycles, the superelastic response of the samples was stabilized and full strain recovery was observed. Finally, the modulus of elasticity of dense SLM NiTi was decreased from 47 GPa to 9 GPa in the first cycle by adding 58% porosity.

  7. Thermolysis synthesis of pure phase NiO from novel sonochemical synthesized Ni(II) nano metal-organic supramolecular architecture.

    Science.gov (United States)

    Hanifehpour, Younes; Morsali, Ali; Mirtamizdoust, Babak; Joo, Sang Woo; Soltani, Behzad

    2017-07-01

    Nano-structures of a new supramolecular coordination compound of divalent nickel with the pyrazol (pzH) containing the terminal azide anions, [Ni(pzH) 2 (N 3 ) 2 ] (1), with discrete molecular architecture (DMA) in solid state was synthesized via sonochemical method. The new nanostructure was characterized by scanning electron microscopy, X-ray powder diffraction, IR, and elemental analysis. Compound 1 was structurally characterized by single crystal X-ray diffraction and the single-crystal X-ray data shows that the coordination number of Ni (II) ions is six, (NiN 6 ), with four N-donor atoms from neutral "pzH" ligands and two N-donors from two terminal azide anions. The supramolecular features in these complexes are guided and controlled by weak directional intermolecular interactions. The structure of the title complex was optimized by density functional theory calculations. Calculated structural parameters and IR spectra for the title complex are consistent with the crystal structure. The NiO nanoparticles were obtained by thermolysis of 1 at 180°C with oleic acid as a surfactant. Copyright © 2017 Elsevier B.V. All rights reserved.

  8. Thermal variation of magnetization in Ni/V multilayers

    International Nuclear Information System (INIS)

    Benkirane, K.; Elkabil, R.; Hamdoun, A.; Lassri, M.; Abid, M.; Lassri, H.; Krishnan, R.

    2004-01-01

    The magnetic properties of Ni/V multilayers, prepared by the RF sputtering method, have been systematically studied by magnetic measurements. The magnetization decreases with a decrease in Ni layer thickness tNi and the analysis of the results at 5K indicates the presence of a dead Ni layer about 12A thick. The effective anisotropy Keff of Ni/V multilayers is obtained using a torque magnetometer. The interface contribution to the magnetic anisotropy is practically negligible. A spin-wave theory has been used to explain the temperature dependence of the magnetization and the approximate values for the bulk exchange interaction Jb, surface exchange interaction JS, and the interlayer coupling strength JI for various Ni layer thicknesses have been obtained

  9. Effect of nickel oxide seed layers on annealed-amorphous titanium oxide thin films prepared using plasma-enhanced chemical vapor deposition

    International Nuclear Information System (INIS)

    Wu, Cheng-Yang; Hong, Shao-Chyang; Hwang, Fu-Tsai; Lai, Li-Wen; Lin, Tan-Wei; Liu, Day-Shan

    2011-01-01

    The effect of a nickel oxide (NiO x ) seed layer on the crystallization and photocatalytic activity of the sequentially plasma-enhanced chemical vapor deposited amorphous titanium oxide (TiO x ) thin film processed by a post-annealing process was investigated. The evolution of the crystalline structures, chemical bond configurations, and surface/cross-sectional morphologies of the annealed TiO x films, with and without a NiO x seed layer, was examined using X-ray diffractometer, Fourier transform infrared spectrometry, X-ray photoelectron spectroscopy, atomic force microscopy, and field emission scanning electron microscope measurements. Thermo- and photo-induced hydrophilicity was determined by measuring the contact angle of water droplet. Photocatalytic activity after UV light irradiation was evaluated from the decolorization of a methylene blue solution. The crystallization temperature of the TiO x film, deposited on a NiO x seed layer, was found to be lower than that of a pure TiO x film, further improving the thermo- and photo-induced surface super-hydrophilicity. The TiO x film deposited onto the NiO x seed layer, resulting in significant cluster boundaries, showed a rough surface morphology and proved to alleviate the anatase crystal growth by increasing the post-annealing temperature, which yielded a more active surface area and prohibited the recombination of photogenerated electrons and holes. The photocatalytic activity of the NiO x /TiO x system with such a textured surface therefore was enhanced and optimized through an adequate post-annealing process.

  10. Effect of nickel oxide seed layers on annealed-amorphous titanium oxide thin films prepared using plasma-enhanced chemical vapor deposition

    Energy Technology Data Exchange (ETDEWEB)

    Wu, Cheng-Yang; Hong, Shao-Chyang [Institute of Electro-Optical and Materials Science, National Formosa University, Huwei, Yunlin, 63201, Taiwan (China); Hwang, Fu-Tsai [Department of Electro-Optical Engineering, National United University, Miao-Li, 36003, Taiwan (China); Lai, Li-Wen [ITRI South, Industrial Technology Research Institute, Liujia, Tainan, 73445, Taiwan (China); Lin, Tan-Wei [Institute of Electro-Optical and Materials Science, National Formosa University, Huwei, Yunlin, 63201, Taiwan (China); Liu, Day-Shan, E-mail: dsliu@sunws.nfu.edu.tw [Institute of Electro-Optical and Materials Science, National Formosa University, Huwei, Yunlin, 63201, Taiwan (China)

    2011-10-31

    The effect of a nickel oxide (NiO{sub x}) seed layer on the crystallization and photocatalytic activity of the sequentially plasma-enhanced chemical vapor deposited amorphous titanium oxide (TiO{sub x}) thin film processed by a post-annealing process was investigated. The evolution of the crystalline structures, chemical bond configurations, and surface/cross-sectional morphologies of the annealed TiO{sub x} films, with and without a NiO{sub x} seed layer, was examined using X-ray diffractometer, Fourier transform infrared spectrometry, X-ray photoelectron spectroscopy, atomic force microscopy, and field emission scanning electron microscope measurements. Thermo- and photo-induced hydrophilicity was determined by measuring the contact angle of water droplet. Photocatalytic activity after UV light irradiation was evaluated from the decolorization of a methylene blue solution. The crystallization temperature of the TiO{sub x} film, deposited on a NiO{sub x} seed layer, was found to be lower than that of a pure TiO{sub x} film, further improving the thermo- and photo-induced surface super-hydrophilicity. The TiO{sub x} film deposited onto the NiO{sub x} seed layer, resulting in significant cluster boundaries, showed a rough surface morphology and proved to alleviate the anatase crystal growth by increasing the post-annealing temperature, which yielded a more active surface area and prohibited the recombination of photogenerated electrons and holes. The photocatalytic activity of the NiO{sub x}/TiO{sub x} system with such a textured surface therefore was enhanced and optimized through an adequate post-annealing process.

  11. Moessbauer study of corrosion products formed on Fe80B20 and Fe40Ni40 (MoB)20 amorphous alloys in an SO2-polluted atmosphere

    International Nuclear Information System (INIS)

    Davalos, J.; Marco, J.F.; Gracia, M.; Gancedo, J.R.; Greneche, J.M.

    1990-01-01

    ICEMS, XPS, XRD, and AES have been used to study the corrosion layers formed on two metallic glasses, Fe 80 B 20 and Fe 40 Ni 40 (MoB) 20 (2605 and 2826 MB, Allied Company), exposed to an SO 2 -polluted humid atmosphere. The iron-containing corrosion products are the same found for pure iron in the same environment, but different relative concentrations were clearly evidenced by ICEMS results. Elemental sulphur, Ni(OH) 2 , and B(OH) 3 , the latter enriched at the surface, were found by XPS, XRD and AES. (orig.)

  12. Photoelectrochemical Water Oxidation by GaAs Nanowire Arrays Protected with Atomic Layer Deposited NiO x Electrocatalysts

    Science.gov (United States)

    Zeng, Joy; Xu, Xiaoqing; Parameshwaran, Vijay; Baker, Jon; Bent, Stacey; Wong, H.-S. Philip; Clemens, Bruce

    2018-02-01

    Photoelectrochemical (PEC) hydrogen production makes possible the direct conversion of solar energy into chemical fuel. In this work, PEC photoanodes consisting of GaAs nanowire (NW) arrays were fabricated, characterized, and then demonstrated for the oxygen evolution reaction (OER). Uniform and periodic GaAs nanowire arrays were grown on a heavily n-doped GaAs substrates by metal-organic chemical vapor deposition selective area growth. The nanowire arrays were characterized using cyclic voltammetry and impedance spectroscopy in a non-aqueous electrochemical system using ferrocene/ferrocenium (Fc/Fc+) as a redox couple, and a maximum oxidation photocurrent of 11.1 mA/cm2 was measured. GaAs NW arrays with a 36 nm layer of nickel oxide (NiO x ) synthesized by atomic layer deposition were then used as photoanodes to drive the OER. In addition to acting as an electrocatalyst, the NiO x layer served to protect the GaAs NWs from oxidative corrosion. Using this strategy, GaAs NW photoanodes were successfully used for the oxygen evolution reaction. This is the first demonstration of GaAs NW arrays for effective OER, and the fabrication and protection strategy developed in this work can be extended to study any other nanostructured semiconductor materials systems for electrochemical solar energy conversion.

  13. Enhanced Electrocatalytic Activity for Water Splitting on NiO/Ni/Carbon Fiber Paper

    Directory of Open Access Journals (Sweden)

    Ruoyu Zhang

    2016-12-01

    Full Text Available Large-scale growth of low-cost, efficient, and durable non-noble metal-based electrocatalysts for water splitting is crucial for future renewable energy systems. Atomic layer deposition (ALD provides a promising route for depositing uniform thin coatings of electrocatalysts, which are useful in many technologies, including the splitting of water. In this communication, we report the growth of a NiO/Ni catalyst directly on carbon fiber paper by atomic layer deposition and report subsequent reduction and oxidation annealing treatments. The 10–20 nm NiO/Ni nanoparticle catalysts can reach a current density of 10 mA·cm−2 at an overpotential of 189 mV for hydrogen evolution reactions and 257 mV for oxygen evolution reactions with high stability. We further successfully achieved a water splitting current density of 10 mA·cm−2 at 1.78 V using a typical NiO/Ni coated carbon fiber paper two-electrode setup. The results suggest that nanoparticulate NiO/Ni is an active, stable, and noble-metal-free electrocatalyst, which facilitates a method for future water splitting applications.

  14. Structural and magnetic properties of Ni-Zn doped BaM nanocomposite via citrate precursor

    Energy Technology Data Exchange (ETDEWEB)

    Rana, Kush; Thakur, Preeti; Thakur, Atul, E-mail: atulphysics@gmail.com [School of Physics and Materials Science, Shoolini University, Solan, India 173212 (India); Tomar, Monika; Gupta, Vinay [Department of Physics and Astrophysics, University of Delhi, Delhi, India 110007 (India)

    2016-05-23

    Ni-Zn substituted M-type barium ferrite nanocomposite has been prepared via citrate precursor method. Nanocomposite having composition BaNi{sub 0.5}Zn{sub 0.5}Fe{sub 11}O{sub 19} was sintered at 900°C for 3hrs and characterized by using different characterization techniques. X-ray diffraction (XRD) confirmed the formation of double phase with most prominent peak at (114). Average crystallite size for pure BaM and BNZFO were found to be 36 nm & 45 nm. Field emission scanning electron microscopy (FESEM) confirmed the formation of hexagonal platelets with a layered structure. Magnetic properties of these samples were investigated by using vibrating sample magnetometer (VSM). Magnetic parameters like saturation magnetization (M{sub s}), coericivity (H{sub c}) and squareness ratio (SQR) of nanocomposite were found to be 60 emu/g, 3663 Oe and 0.6163 respectively. These values were noticed to be higher as compared to pure BaM. Enhanced magnetic properties of nanocomposite were strongly dependent on exchange coupling. Therefore these properties make this nanocomposite a suitable candidate for magnetic recording and high frequency applications.

  15. Atomistic calculations of hydrogen interactions with Ni3Al grain boundaries and Ni/Ni3Al interfaces

    International Nuclear Information System (INIS)

    Baskes, M.I.; Angelo, J.E.; Moody, N.R.

    1995-01-01

    Embedded Atom Method (EAM) potentials have been developed for the Ni/Al/H system. The potentials have been fit to numerous properties of this system. For example, these potentials represent the structural and elastic properties of bulk Ni, Al, Ni 3 Al, and NiAl quite well. In addition the potentials describe the solution and migration behavior of hydrogen in both nickel and aluminum. A number of calculations using these potentials have been performed. It is found that hydrogen strongly prefers sites in Ni 3 Al that are surrounded by 6 Ni atoms. Calculations of the trapping of hydrogen to a number of grain boundaries in Ni 3 Al have been performed as a function of hydrogen chemical potential at room temperature. The failure of these bicrystals under tensile stress has been examined and will be compared to the failure of pure Ni 3 Al boundaries. Boundaries containing a preponderance of nickel are severely weakened by hydrogen. In order to investigate the potential embrittlement of γ/γ' alloys, trapping of hydrogen to a spherical Ni 3 Al precipate in nickel as a function of chemical potential at room temperature has been calculated. It appears that the boundary is not a strong trap for hydrogen, hence embrittlement in these alloys is not primarily due to interactions of hydrogen with the γ/γ interface

  16. Bath temperature effect on magnetoelectric performance of Ni-lead zirconate titanate-Ni laminated composites synthesized by electroless deposition

    Energy Technology Data Exchange (ETDEWEB)

    Wu, W. [College of Materials Science and Technology, Nanjing University of Aeronautics and Astronautics, Nanjing 210016 (China); Wang, Y.G., E-mail: yingang.wang@nuaa.edu.c [College of Materials Science and Technology, Nanjing University of Aeronautics and Astronautics, Nanjing 210016 (China); Bi, K. [College of Materials Science and Technology, Nanjing University of Aeronautics and Astronautics, Nanjing 210016 (China)

    2011-03-15

    Magnetoelectric (ME) Ni-lead zirconate titanate-Ni laminated composites have been prepared by electroless deposition at various bath temperatures. The structure of the Ni layers deposited at various bath temperatures was characterized by X-ray diffraction, and microstructures were investigated by transmission electron microscopy. The magnetostrictive coefficients were measured by means of a resistance strain gauge. The transverse ME voltage coefficient {alpha}{sub E,31} was measured with the magnetic field applied parallel to the sample plane. The deposition rate of Ni increases with bath temperature. Ni layer with smaller grain size is obtained at higher bath temperature and shows higher piezomagnetic coefficient, promoting the ME effect of corresponding laminated composites. It is advantageous to increase the bath temperature, while trying to avoid the breaking of bath constituents. - Research Highlights: Laminated composites without interlayer are prepared by electroless deposition. Bath temperature affects the grain size of the deposited Ni layers. Higher bath temperature is beneficial to obtain stronger ME response.

  17. Controlled growth of Ni/NiO core–shell nanoparticles: Structure, morphology and tuning of magnetic properties

    Energy Technology Data Exchange (ETDEWEB)

    D’Addato, S., E-mail: sergio.daddato@unimore.it [CNR-NANO, S3, via G. Campi 213/a, Modena (Italy); Dipartimento FIM, Università di Modena e Reggio Emilia, via G. Campi 213/a, Modena (Italy); Spadaro, M.C. [CNR-NANO, S3, via G. Campi 213/a, Modena (Italy); Dipartimento FIM, Università di Modena e Reggio Emilia, via G. Campi 213/a, Modena (Italy); Luches, P. [CNR-NANO, S3, via G. Campi 213/a, Modena (Italy); Grillo, V. [CNR-NANO, S3, via G. Campi 213/a, Modena (Italy); CNR-IMEM, Parco Area delle Scienze 37/A, 43100 Parma (Italy); Frabboni, S.; Valeri, S. [CNR-NANO, S3, via G. Campi 213/a, Modena (Italy); Dipartimento FIM, Università di Modena e Reggio Emilia, via G. Campi 213/a, Modena (Italy); Ferretti, A.M.; Capetti, E.; Ponti, A. [CNR-ISTM, Laboratorio di Nanotecnologie, via G. Fantoli 16/15, 20138 Milano (Italy)

    2014-07-01

    We performed a detailed study of Ni/NiO core–shell nanoparticles (NP) obtained with a gas aggregation source. The NP oxide shells were produced by oxidizing the NP with different procedures: deposition in oxygen atmosphere, post-annealing in air, sequential deposition of (a) first NiO layer, (b) Ni NP and (c) third NiO Layer. X-ray photoelectron spectroscopy from Ni 2p core-level gave information about the chemical state of Ni in the core and in the oxide shell, while scanning electron microscopy was used for investigation of the NP morphology. High quality scanning transmission electron microscopy in high angle annular dark field mode data demonstrated core–shell structure also for NiO/Ni NP/NiO samples. Field-cooled/zero-field-cooled magnetization curves and field-cooled isothermal hysteresis cycles at T = 5 K were recorded by a SQUID magnetometer. In this way, the relation between magnetic properties and oxide shell structure was assessed, showing the role played by the control of the formation of oxide on the exchange bias and interparticle magnetic interaction.

  18. Controlled growth of Ni/NiO core–shell nanoparticles: Structure, morphology and tuning of magnetic properties

    International Nuclear Information System (INIS)

    D’Addato, S.; Spadaro, M.C.; Luches, P.; Grillo, V.; Frabboni, S.; Valeri, S.; Ferretti, A.M.; Capetti, E.; Ponti, A.

    2014-01-01

    We performed a detailed study of Ni/NiO core–shell nanoparticles (NP) obtained with a gas aggregation source. The NP oxide shells were produced by oxidizing the NP with different procedures: deposition in oxygen atmosphere, post-annealing in air, sequential deposition of (a) first NiO layer, (b) Ni NP and (c) third NiO Layer. X-ray photoelectron spectroscopy from Ni 2p core-level gave information about the chemical state of Ni in the core and in the oxide shell, while scanning electron microscopy was used for investigation of the NP morphology. High quality scanning transmission electron microscopy in high angle annular dark field mode data demonstrated core–shell structure also for NiO/Ni NP/NiO samples. Field-cooled/zero-field-cooled magnetization curves and field-cooled isothermal hysteresis cycles at T = 5 K were recorded by a SQUID magnetometer. In this way, the relation between magnetic properties and oxide shell structure was assessed, showing the role played by the control of the formation of oxide on the exchange bias and interparticle magnetic interaction.

  19. Characterization of nanostructured photosensitive (NiS)x(CdS)(1-x) composite thin films grown by successive ionic layer adsorption and reaction (SILAR) route

    International Nuclear Information System (INIS)

    Ubale, A.U.; Bargal, A.N.

    2011-01-01

    Highlights: → Thin films of (NiS) x (CdS) (1-x) with variable composition (x = 1 to 0) were deposited onto glass substrates by the successive ionic layer adsorption and reaction (SILAR) method. → The structural, surface morphological and electrical characterizations of the as deposited and annealed films were studied. → The bandgap and activation energy of annealed (NiS) x (CdS) (1-x) film decrease with improvement in photosensitive nature. -- Abstract: Recently ternary semiconductor nanostructured composite materials have attracted the interest of researchers because of their photovoltaic applications. Thin films of (NiS) x (CdS) (1-x) with variable composition (x = 1-0) had been deposited onto glass substrates by the successive ionic layer adsorption and reaction (SILAR) method. As grown and annealed films were characterised by X-ray diffraction, scanning electron microscopy and EDAX to investigate structural and morphological properties. The (NiS) x (CdS) (1-x) films were polycrystalline in nature having mixed phase of rhombohedral and hexagonal crystal structure due to NiS and CdS respectively. The optical and electrical properties of (NiS) x (CdS) (1-x) thin films were studied to determine compsition dependent bandgap, activation energy and photconductivity. The bandgap and activation energy of annealed (NiS) x (CdS) (1-x) film decrease with improvement in photosensitive nature.

  20. The Deoxygenation Pathways of Palmitic Acid into Hydrocarbons on Silica-Supported Ni12P5 and Ni2P Catalysts

    Directory of Open Access Journals (Sweden)

    Wenjun Zhou

    2018-04-01

    Full Text Available Pure Ni12P5/SiO2 and pure Ni2P/SiO2 catalysts were obtained by adjusting the Ni and P molar ratios, while Ni/SiO2 catalyst was prepared as a reference against which the deoxygenation pathways of palmitic acid were investigated. The catalysts were characterized by N2 adsorption, X-ray diffraction (XRD, X-ray photoelectron spectroscopy (XPS, transmission election microscopy (TEM, infrared spectroscopy of pyridine adsorption (Py-IR, H2-adsorption and temperature-programmed desorption of hydrogen (H2-TPD. The crystallographic planes of Ni(111, Ni12P5(400, Ni2P(111 were found mainly exposed on the above three catalysts, respectively. It was found that the deoxygenation pathway of palmitic acid mainly proceeded via direct decarboxylation (DCO2 to form C15 on Ni/SiO2. In contrast, on the Ni12P5/SiO2 catalyst, there were two main competitive pathways producing C15 and C16, one of which mainly proceeded via the decarbonylation (DCO to form C15 accompanying water formation, and the other pathway produced C16 via the dehydration of hexadecanol intermediate, and the yield of C15 was approximately twofold that of C16. Over the Ni2P/SiO2 catalyst, two main deoxygenation pathways formed C15, one of which was mainly the DCO pathway and the other was dehydration accompanying the hexadecanal intermediate and then direct decarbonylation without water formation. The turn over frequency (TOF followed the order: Ni12P5/SiO2 > Ni/SiO2 > Ni2P/SiO2.

  1. Change of texture, microdeformation and hardness in surface layer of TiNi alloy depending on the number of pulses of electron beam effects

    International Nuclear Information System (INIS)

    Meisner, L. L.; Meisner, S. N.; Markov, A. B.; Yakovlev, E. V.; Ozur, G. E.; Rotshtein, V. P.; Mironov, Yu. P.

    2015-01-01

    This work comprises a study of the influence of the pulse number of low-energy high-current electron beam (LEHCEB) exposure on the value and character of distribution of residual elastic stresses, texturing effects and the relationship between structural-phase states and physical and mechanical properties of the modified surface layers of TiNi alloy. LEHCEB processing of the surface of TiNi samples was carried out using a RITM-SP [3] installation. Energy density of electron beam was constant at E s = 3.9 ± 0.5 J/cm 2 ; pulse duration was 2.8 ± 0.3 μs. The number of pulses in the series was changeable, (n = 2–128). It was shown that as the result of multiple LEHCEB processing of TiNi samples, hierarchically organized multilayer structure is formed in the surface layer. The residual stress field of planar type is formed in the modified surface layer as following: in the direction of the normal to the surface the strain component ε ⊥ < 0 (compressing strain), and in a direction parallel to the surface, the strain component ε || > 0 (tensile deformation). Texturing effects and the level of residual stresses after LEHCEB processing of TiNi samples with equal energy density of electron beam (∼3.8 J/cm 2 ) depend on the number of pulses and increase with the rise of n > 10

  2. Alloying process of sputter-deposited Ti/Ni multilayer thin films

    International Nuclear Information System (INIS)

    Cho, H.; Kim, H.Y.; Miyazaki, S.

    2006-01-01

    Alloying process of a Ti/Ni multilayer thin film was investigated in detail by differential scanning calorimetry (DSC), X-ray diffractometry (XRD) and transmission electron microscopy (TEM). The Ti/Ni multilayer thin film was prepared by depositing Ti and Ni layers alternately on a SiO 2 /Si substrate. The number of each metal layer was 100, and the total thickness was 3 μm. The alloy composition was determined as Ti-51 at.%Ni by electron probe micro analysis (EPMA). The DSC curve exhibited three exothermic peaks at 621, 680 and 701 K during heating the as-sputtered multilayer thin film. In order to investigate the alloying process, XRD and TEM observation was carried out for the specimens heated up to various temperatures with the heating rate same as the DSC measurement. The XRD profile of the as-sputtered film revealed only diffraction peaks of Ti and Ni. But reaction layers of 3 nm in thickness were observed at the interfaces of Ti and Ni layers in cross-sectional TEM images. The reaction layer was confirmed as an amorphous phase by the nano beam diffraction analysis. The XRD profiles exhibited that the intensity of Ti diffraction peak decreased in the specimen heat-treated above 600 K. The peak from Ni became broad and shifted to lower diffraction angle. The amorphous layer thickened up to 6 nm in the specimen heated up to 640 K. The diffraction peak corresponding to Ti-Ni B2 phase appeared and the peak from Ni disappeared for the specimen heated up to 675 K. The Ti-Ni B2 crystallized from the amorphous reaction layer. After further heating above the third exothermic peak, the intensity of the peak from the Ti-Ni B2 phase increased, the peak from Ti disappeared and the peaks corresponding to Ti 2 Ni appeared. The Ti 2 Ni phase was formed by the reaction of the Ti-Ni B2 and Ti

  3. Microstructure and erosive wear behaviors of Ti6Al4V alloy treated by plasma Ni alloying

    Energy Technology Data Exchange (ETDEWEB)

    Wang, Z.X.; Wu, H.R.; Shan, X.L.; Lin, N.M.; He, Z.Y., E-mail: tyuthzy@126.com; Liu, X.P.

    2016-12-01

    Graphical abstract: The Ni modified layers were prepared on the surface of Ti6Al4V substrate by the plasma surface alloying technique. The surface and cross-section morphology, element concentration and phase composition were investigated by thermal field emission scanning electron microscopy (SEM), and glow discharge optical emission spectroscopy (GDOES), X-ray diffraction (XRD), respectively. The cross-section nano-scale hardness of Ni modified layer was measured by nano indenter. The results showed that Ni modified layers exhibited triple layers structure and continuous gradient distribution of the concentration. From the surface to the matrix, they were 2 μm Ni deposition layer, 8 μm Ni-rich alloying layer including the phases of Ni{sub 3}Ti, NiTi, Ti{sub 2}Ni, AlNi{sub 3} and 24 μm Ni-poor alloying layer forming the solid solution of nickel. With increasing of the thickness of Ni modified layer, the microhardness increased first, reached the climax, then gradient decreased. The erosion tests were performed on the surface of the untreated and treated Ti6Al4V sample using MSE (Micro-slurry-jet Erosion) method. The experiment results showed that the wear rate of every layer showed different value, and the Ni-rich alloying layer was the lowest. The strengthening mechanism of Ni modified layer was also discussed. - Highlights: • The Ni modified layers were prepared by the plasma surface alloying technique. • Triple layers structure was prepared. • Using Micro-slurry-jet Erosion method. • The erosion rate of Ni modified layer experienced the process of descending first and then ascending. • Improvement of erosion resistance performance of Ni-rich alloying layer was prominent. The wear mechanism of Ni modified layer showed micro-cutting wearing. - Abstract: The Ni modified layers were prepared on the surface of Ti6Al4V substrate by the plasma surface alloying technique. The surface and cross-section morphology, element concentration and phase composition

  4. SAE 1045 steel/WC-Co/Ni-Cu-Ni/SAE 1045 steel joints prepared by dynamic diffusion bonding: Microelectrochemical studies in 0.6 M NaCl solution

    International Nuclear Information System (INIS)

    Andreatta, Francesco; Matesanz, Laura; Akita, Adriano H.; Paussa, Luca; Fedrizzi, Lorenzo; Fugivara, Cecilio S.; Gomez de Salazar, Jose M.; Benedetti, Assis V.

    2009-01-01

    Corrosion of SAE 1045 steel/WC-Co/Ni-Cu-Ni/SAE 1045 steel interfaces was investigated in 0.6 M NaCl solution using an electrochemical microcell, which enables local electrochemical characterization at the micrometer scale. Two pieces of steel, one with a WC-Co coating covered with Ni (12 μm) and Cu (5 μm) layers, and the other with a Ni (15 μm) layer, were welded by dynamic diffusion bonding. A WC-Co coating was applied to the steel by the high velocity oxygen-fuel process, and Ni-Cu and Ni layers by electroplating. Polarization curves were recorded using an electrochemical microcell. Different regions of welded samples were investigated, including steel, cermet coating, and steel/cermet and steel/Ni-Cu-Ni/cermet interfaces. Optical and electronic microscopes were employed to study the corroded regions. Potentiodynamic polarization curves obtained using the microcell revealed that the base metal was more susceptible to corrosion than the cermet. In addition, cermet steel/cermet and steel/Ni-Cu-Ni/cermet joints exhibited different breakdown potentials. Steel was strongly corroded in the regions adjacent to the interfaces, while the cermet was less corroded. Iron oxides/hydroxides and chloride salts were the main corrosion products of steel. After removal of the superficial layer of corrosion products, iron oxides were mainly observed. Chloride ions were detected mainly on a copper-enriched layer placed between two Ni-enriched layers.

  5. Rutherford backscattering spectrometry of thin NiCr layers

    International Nuclear Information System (INIS)

    Anklam, H.J.

    1984-01-01

    The possibilities and problems of characterizing thin films of NiCr by means of Rutherford backscattering spectrometry (RBS) are demonstrated. Thin resistor films of NiCr (10 to 30 nm thick) are deposited on SiO 2 by sputtering in air or oxygen. The electrical properties depend both on integral chemical composition of films and on local distribution of elements. The determination of composition (Ni-Cr ratio, oxygen content) and of depth profiles of elements by the aid of RBS is described. For solving special analytical problems different substrates as amorphous SiO 2 , Si monocrystals, and glassy carbon are used

  6. Polymer stabilized Ni-Ag and Ni-Fe alloy nanoclusters: Structural and magnetic properties

    Energy Technology Data Exchange (ETDEWEB)

    Kabir, L.; Mandal, A.R. [Department of Physics, Visva-Bharati, Santiniketan-731 235 (India); Mandal, S.K., E-mail: sk_mandal@hotmail.co [Department of Physics, Visva-Bharati, Santiniketan-731 235 (India)

    2010-04-15

    We report here the structural and magnetic behaviors of nickel-silver (Ni-Ag) and nickel-iron (Ni-Fe) nanoclusters stabilized with polymer (polypyrrole). High resolution transmission electron microscopy (HRTEM) indicates Ni-Ag nanoclusters to stabilize in core-shell configuration while that of Ni-Fe nanoclusters in a mixed type of geometry. Structural characterizations by X-ray diffraction (XRD) reveal the possibility of alloying in such bimetallic nanoclusters to some extent even at temperatures much lower than that of bulk alloying. Electron paramagnetic resonance (EPR) spectra clearly reveal two different absorption behaviors: one is ascribed to non-isolated Ni{sup 2+} clusters surrounded by either silver or iron giving rise to a broad signal, other (very narrow signal) being due to the isolated superparamagnetic Ni{sup 2+} clusters or bimetallic alloy nanoclusters. Results obtained for Ni-Ag and Ni-Fe nanoclusters have been further compared with the behavior exhibited by pure Ni nanoclusters in polypyrrole host. Temperature dependent studies (at 300 and 77 K) of EPR parameters, e.g. linewidth, g-value, line shape and signal intensity indicating the significant influence of surrounding paramagnetic silver or ferromagnetic iron within polymer host on the EPR spectra have been presented.

  7. Polymer stabilized Ni-Ag and Ni-Fe alloy nanoclusters: Structural and magnetic properties

    Science.gov (United States)

    Kabir, L.; Mandal, A. R.; Mandal, S. K.

    2010-04-01

    We report here the structural and magnetic behaviors of nickel-silver (Ni-Ag) and nickel-iron (Ni-Fe) nanoclusters stabilized with polymer (polypyrrole). High resolution transmission electron microscopy (HRTEM) indicates Ni-Ag nanoclusters to stabilize in core-shell configuration while that of Ni-Fe nanoclusters in a mixed type of geometry. Structural characterizations by X-ray diffraction (XRD) reveal the possibility of alloying in such bimetallic nanoclusters to some extent even at temperatures much lower than that of bulk alloying. Electron paramagnetic resonance (EPR) spectra clearly reveal two different absorption behaviors: one is ascribed to non-isolated Ni 2+ clusters surrounded by either silver or iron giving rise to a broad signal, other (very narrow signal) being due to the isolated superparamagnetic Ni 2+ clusters or bimetallic alloy nanoclusters. Results obtained for Ni-Ag and Ni-Fe nanoclusters have been further compared with the behavior exhibited by pure Ni nanoclusters in polypyrrole host. Temperature dependent studies (at 300 and 77 K) of EPR parameters, e.g. linewidth, g-value, line shape and signal intensity indicating the significant influence of surrounding paramagnetic silver or ferromagnetic iron within polymer host on the EPR spectra have been presented.

  8. Polymer stabilized Ni-Ag and Ni-Fe alloy nanoclusters: Structural and magnetic properties

    International Nuclear Information System (INIS)

    Kabir, L.; Mandal, A.R.; Mandal, S.K.

    2010-01-01

    We report here the structural and magnetic behaviors of nickel-silver (Ni-Ag) and nickel-iron (Ni-Fe) nanoclusters stabilized with polymer (polypyrrole). High resolution transmission electron microscopy (HRTEM) indicates Ni-Ag nanoclusters to stabilize in core-shell configuration while that of Ni-Fe nanoclusters in a mixed type of geometry. Structural characterizations by X-ray diffraction (XRD) reveal the possibility of alloying in such bimetallic nanoclusters to some extent even at temperatures much lower than that of bulk alloying. Electron paramagnetic resonance (EPR) spectra clearly reveal two different absorption behaviors: one is ascribed to non-isolated Ni 2+ clusters surrounded by either silver or iron giving rise to a broad signal, other (very narrow signal) being due to the isolated superparamagnetic Ni 2+ clusters or bimetallic alloy nanoclusters. Results obtained for Ni-Ag and Ni-Fe nanoclusters have been further compared with the behavior exhibited by pure Ni nanoclusters in polypyrrole host. Temperature dependent studies (at 300 and 77 K) of EPR parameters, e.g. linewidth, g-value, line shape and signal intensity indicating the significant influence of surrounding paramagnetic silver or ferromagnetic iron within polymer host on the EPR spectra have been presented.

  9. Origin of superconductivity in layered centrosymmetric LaNiGa{sub 2}

    Energy Technology Data Exchange (ETDEWEB)

    Tütüncü, H. M. [Sakarya Üniversitesi, Fen-Edebiyat Fakültesi, Fizik Bölümü, 54187 Adapazarı (Turkey); Srivastava, G. P. [School of Physics, University of Exeter, Stocker Road, Exeter EX4 4QL (United Kingdom)

    2014-01-13

    We have examined the origin of superconductivity in layered centrosymmetric LaNiGa{sub 2} by employing a linear response approach based on the density functional perturbation theory. Our results indicate that this material is a conventional electron-phonon superconductor with intermediate level of coupling strength, with the electron-phonon coupling parameter of 0.70, and the superconducting critical temperature of 1.90 K in excellent accordance with experimental value of 1.97 K. The largest contribution to the electron-phonon coupling comes from the La d and Ga p electrons near the Fermi energy and the B{sub 3g} phonon branch resulting from vibrations of these atoms along the Γ-Z symmetry line in the Brillouin zone.

  10. Quantification of elemental area densities in multiple metal layers (Au/Ni/Cu) on a Cr-coated quartz glass substrate for certification of NMIJ CRM 5208-a.

    Science.gov (United States)

    Ariga, Tomoko; Zhu, Yanbei; Ito, Mika; Takatsuka, Toshiko; Terauchi, Shinya; Kurokawa, Akira; Inagaki, Kazumi

    2018-04-01

    Area densities of Au/Ni/Cu layers on a Cr-coated quartz substrate were characterized to certify a multiple-metal-layer certified reference material (NMIJ CRM5208-a) that is intended for use in the analysis of the layer area density and the thickness by an X-ray fluorescence spectrometer. The area densities of Au/Ni/Cu layers were calculated from layer mass amounts and area. The layer mass amounts were determined by using wet chemical analyses, namely inductively coupled plasma mass spectrometry (ICP-MS), isotope-dilution (ID-) ICP-MS, and inductively coupled plasma optical emission spectrometry (ICP-OES) after dissolving the layers with diluted mixture of HCl and HNO 3 (1:1, v/v). Analytical results of the layer mass amounts obtained by the methods agreed well with each another within their uncertainty ranges. The area of the layer was determined by using a high-resolution optical scanner calibrated by Japan Calibration Service System (JCSS) standard scales. The property values of area density were 1.84 ± 0.05 μg/mm 2 for Au, 8.69 ± 0.17 μg/mm 2 for Ni, and 8.80 ± 0.14 μg/mm 2 for Cu (mean ± expanded uncertainty, coverage factor k = 2). In order to assess the reliability of these values, the density of each metal layer calculated from the property values of the area density and layer thickness measured by using a scanning electron microscope were compared with available literature values and good agreement between the observed values and values obtained in previous studies.

  11. A comparative study of Ni-Mn layered double hydroxide/carbon composites with different morphologies for supercapacitors.

    Science.gov (United States)

    Li, M; Liu, F; Zhang, X B; Cheng, J P

    2016-11-02

    A variety of carbon materials varying from 0D to 2D, i.e. 0D nanoparticles, 1D carbon nanotubes (CNTs) and 2D reduced graphene oxide (rGO) are selected to in situ combine with Ni-Mn layered double hydroxide (LDH) to prepare electrode materials for supercapacitors. Through a simple solution method, hierarchical Ni-Mn LDH/carbon composites can be easily fabricated. A comparative study is carried out on the sandwich-like LDH/rGO, flower-like LDH/carbon black, turbostratic-structured LDH/CNTs and ternary LDH/CNTs/rGO for their structure, morphology, porous properties and electrochemical performances. The results show that the ternary Ni-Mn LDH/CNTs/rGO composite yields the highest specific capacitance of 1268 F g -1 in 2 M KOH electrolyte and a long lifespan, exhibiting great potential for supercapacitor applications. Meanwhile, investigation on the influence of the cation species of MOH (M = Li + , Na + or K + ) and the alkali concentration of the KOH electrolyte illustrates that increasing the concentration of the KOH electrolyte can benefit the capacitive performance of the electrode and that NaOH shows great advantages as an electrolyte for the Ni-Mn LDH/CNTs/rGO electrode due to its high capacitance and small resistance.

  12. Effect of Ta buffer and NiFe seed layers on pulsed-DC magnetron sputtered Ir{sub 20}Mn{sub 80}/Co{sub 90}Fe{sub 10} exchange bias

    Energy Technology Data Exchange (ETDEWEB)

    Oksuezoglu, Ramis Mustafa, E-mail: rmoksuzoglu@anadolu.edu.t [University of Anadolu, Faculty of Engineering and Architecture, Department of Materials Sciences and Engineering, Iki Eyluel Campus, 26555 Eskisehir (Turkey); Yildirim, Mustafa; Cinar, Hakan [University of Anadolu, Faculty of Engineering and Architecture, Department of Materials Sciences and Engineering, Iki Eyluel Campus, 26555 Eskisehir (Turkey); Hildebrandt, Erwin; Alff, Lambert [Department of Materials Sciences, Darmstadt University of Technology, Petersenstrasse 23, D-64287 Darmstadt (Germany)

    2011-07-15

    A systematic investigation has been done on the correlation between texture, grain size evolution and magnetic properties in Ta/Ni{sub 81}Fe{sub 19}/Ir{sub 20}Mn{sub 80}/Co{sub 90}Fe{sub 10}/Ta exchange bias in dependence of Ta buffer and NiFe seed layer thickness in the range of 2-10 nm, deposited by pulsed DC magnetron sputtering technique. A strong dependence of <1 1 1> texture on the Ta/NiFe thicknesses was found, where the reducing and increasing texture was correlated with exchange bias field and unidirectional anisotropy energy constant at both NiFe/IrMn and IrMn/CoFe interfaces. However, a direct correlation between average grain size in IrMn and H{sub ex} and H{sub c} was not observed. L1{sub 2} phase IrMn{sub 3} could be formed by thickness optimization of Ta/NiFe layers by deposition at room temperature, for which the maximum exchange coupling parameters were achieved. We conclude finally that the coercivity is mainly influenced by texture induced interfacial effects at NiFe/IrMn/CoFe interfaces developing with Ta/NiFe thicknesses. - Research highlights: We discussed the influence of Ta/NiFe thicknesses on structure and grain size in AF layer and texture. A direct correlation between the <1 1 1> texture and exchange coupling was found. A direct relation between average grain size and H{sub ex} and H{sub c} was not observed. L1{sub 2} phase IrMn{sub 3} was formed by deposition at room temperature for Ta (5-6 nm)/NiFe (6-8 nm). We conclude that the coercivity is influenced by order/disorder at NiFe/IrMn/CoFe interfaces.

  13. Intermediate Co/Ni-base model superalloys — Thermophysical properties, creep and oxidation

    International Nuclear Information System (INIS)

    Zenk, Christopher H.; Neumeier, Steffen; Engl, Nicole M.; Fries, Suzana G.; Dolotko, Oleksandr; Weiser, Martin; Virtanen, Sannakaisa; Göken, Mathias

    2016-01-01

    The mechanical properties of γ′-strengthened Co–Ni–Al–W–Cr model superalloys extending from pure Ni-base to pure Co-base superalloys have been assessed. Differential scanning calorimetry measurements and thermodynamic calculations match well and show that the γ′ solvus temperature decreases with increasing Co-content. The γ/γ′ lattice misfit is negative on the Ni- and positive on the Co-rich side. High Ni-contents decelerate the oxidation kinetics up to a factor of 15. The creep strength of the Ni-base alloy increases by an order of magnitude with additions of Co before it deteriorates strongly upon higher additions despite an increasing γ′ volume fraction.

  14. Electrochemical immunosensor with NiAl-layered double hydroxide/graphene nanocomposites and hollow gold nanospheres double-assisted signal amplification.

    Science.gov (United States)

    Qiao, Lu; Guo, Yemin; Sun, Xia; Jiao, Yancui; Wang, Xiangyou

    2015-08-01

    A sensitive electrochemical immunosensor based on NiAl-layered double hydroxide/graphene nanocomposites (NiAl-LDH/G) and hollow gold nanospheres (HGNs) was proposed for chlorpyrifos detection. The NiAl-LDH/G was prepared using a conventional coprecipitation process and reduction of the supporting graphene oxide. Subsequently, the nanocomposites were dispersed with chitosan (CS). The NiAl-LDH/G possessed good electrochemical behavior and high binding affinity to the electrode. The high surface areas of HGNs and the vast aminos and hydroxyls of CS provided a platform for the covalently crosslinking of antibody. Under optimal conditions, the immunosensor exhibited a wide linear range from 5 to 150 μg/mL and from 150 to 2 μg/mL, with a detection limit of 0.052 ng/mL. The detection results showed good agreement with standard gas chromatography method. The constructed immunosensor exhibited good reproducibility, high specificity, acceptable stability and regeneration performance, which provided a new promising tool for chlorpyrifos detection in real samples.

  15. Fe-based soft magnetic composites coated with NiZn ferrite prepared by a co-precipitation method

    Energy Technology Data Exchange (ETDEWEB)

    Peng, Yuandong; Yi, Yi; Li, Liya; Ai, Hengyu; Wang, Xiaoxu [State Key Laboratory of Powder Metallurgy, Central South University, Changsha 410083 (China); Chen, Lulu [Jiangsu Eagle-globe Group Co., Ltd., Nantong 226600 (China)

    2017-04-15

    Fe powder was coated with NiZn ferrite by a co-precipitation method using chlorate as the raw material. Soft magnetic composites were manufactured via compaction and heat treatment of the coated powder. The coated powder and heat treated powder were analysed using scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS), X-ray diffraction (XRD) and Raman spectroscopy. Their magnetic properties were determined using a Quantum Design-Vibrating Sample Magnetometer (QD-VSM). The composites were analysed with SEM and EDS. The permeability and magnetic loss of the composites were measured with a B-H curve analyzer. The results show that, using the co-precipitation method, the raw precipitate was successfully prepared and coated the pure Fe powder and turned into spinel NiZn ferrite treated at 600 ℃ for 1 h. After heat treatment at 500 ℃ under air, the insulation coating layer of soft magnetic composite (SMC) was not destroyed and containing Fe, Ni, Zn and oxygen. The permeabilities of the SMC are stable at edge of the 2–200 kHz frequency range and the total loss was lower. - Graphical abstract: Scanning electron microscopy (SEM) images of Fe/(NiZn)Fe{sub 2}O{sub 4} composite powder heated at 600 ℃ for 1 h. - Highlights: • Fe particles were coated with (NiZn)Fe{sub 2}O{sub 4} via a co-precipitation and calcined method. • Coating layers were uniform and dense. • The permeabilities of the SMC are stable at edge of the 2–200 kHz frequency range.

  16. Thermal Analysis and Flame-Retarded Mechanism of Composites Composed of Ethylene Vinyl Acetate and Layered Double Hydroxides Containing Transition Metals (Mn, Co, Cu, Zn

    Directory of Open Access Journals (Sweden)

    Lili Wang

    2016-05-01

    Full Text Available The effects of transition metals on the hydrophobicity of nano–structured layered double hydroxides (LDHs and the compatibility of LDHs/ethylene vinyl acetate (EVA composites have seldom been reported. NiMgAl–LDHs slightly surface–modified with stearate and doped with transition metal cations (Mn2+, Co2+, Cu2+, Zn2+ are investigated. Compared to the pure EVA, not only were the maximal degradation–rate temperatures (Tmax of the ethylene–based chains enhanced, but also the smoke production rate (SPR and the production rate of CO (COP were sharply decreased for all the composites. Most importantly, a new flame retardant mechanism was found, namely the peak heat release rate (pk-HRR time, which directly depends on the peak production rate of CO2 (pk-CO2 time for EVA and all composites by cone calorimeter test. Moreover, the Mn–doped LDH S–NiMgAl–Mn shows more uniform dispersion and better interfacial compatibility in the EVA matrix. The cone calorimetric residue of S–NiMgAl–Mn/EVA has the intumescent char layer and the compact metal oxide layer. Therefore, S–NiMgAl–Mn/EVA shows the lowest pk-HRR and the longest pk-HRR time among all the composites.

  17. Ni adsorption and Ni-Al LDH precipitation in a sandy aquifer: An experimental and mechanistic modeling study

    NARCIS (Netherlands)

    Regelink, I.C.; Temminghoff, E.J.M.

    2011-01-01

    Mining activities and industries have created nickel (Ni) contaminations in many parts of the world. The objective of this study is to increase our understanding of Ni adsorption and Nickel-Aluminium Layered Double Hydroxide (Ni-Al LDH) precipitation to reduce Ni mobility in a sandy soil aquifer. At

  18. Fabrication of a Ni nano-imprint stamp for an anti-reflective layer using an anodic aluminum oxide template.

    Science.gov (United States)

    Park, Eun-Mi; Lim, Seung-Kyu; Ra, Senug-Hyun; Suh, Su-Jung

    2013-11-01

    Aluminum anodizing can alter pore diameter, density distribution, periodicity and layer thickness in a controlled way. Because of this property, porous type anodic aluminum oxide (AAO) was used as a template for nano-structure fabrication. The alumina layer generated at a constant voltage increased the pore size from 120 nm to 205 nm according to an increasing process time from 60 min to 150 min. The resulting fabricated AAO templates had pore diameters at or less than 200 nm. Ni was sputtered as a conductive layer onto this AAO template and electroplated using DC and pulse power. Comparing these Ni stamps, those generated from electroplating using on/reverse/off pulsing had an ordered pillar array and maintained the AAO template morphology. This stamp was used for nano-imprinting on UV curable resin coated glass wafer. Surface observations via electron microscopy showed that the nano-imprinted patterned had the same shape as the AAO template. A soft mold was subsequently fabricated and nano-imprinted to form a moth-eye structure on the glass wafer. An analysis of the substrate transmittance using UV-VIS/NIR spectroscopy showed that the transmittance of the substrate with the moth-eye structure was 5% greater that the non-patterned substrate.

  19. Near-surface segregation in irradiated Ni3Si

    International Nuclear Information System (INIS)

    Wagner, W.; Rehn, L.E.; Wiedersich, H.

    1982-01-01

    The radiation-induced growth of Ni 3 Si films on the surfaces of Ni(Si) alloys containing = 3 Si phase has been observed. Post-irradiation depth profiling by Auger electron spectroscopy, as well as in situ analysis by high-resolution Rutherford backscattering spectrometry, reveals Si-enrichment at the surfaces of Ni(Si) alloys in excess of stoichiometric Ni 3 Si during irradiation. Thin, near-surface layers with silicon concentrations of 28 to 30 at.% are observed, and even higher Si enrichment is found in the first few atom layers. Transmission electron microscopy and selected area-electron diffraction were employed to characterize these Si-enriched layers. A complex, multiple-spot diffraction pattern is observed superposed on the diffraction pattern of ordered Ni 3 Si. The d-spacings obtained from the extra spots are consistent with those of the orthohexagonal intermetallic compound Ni 5 Si 2 . (author)

  20. Modification of Ni-Rich FCG NMC and NCA Cathodes by Atomic Layer Deposition: Preventing Surface Phase Transitions for High-Voltage Lithium-Ion Batteries

    Science.gov (United States)

    Mohanty, Debasish; Dahlberg, Kevin; King, David M.; David, Lamuel A.; Sefat, Athena S.; Wood, David L.; Daniel, Claus; Dhar, Subhash; Mahajan, Vishal; Lee, Myongjai; Albano, Fabio

    2016-05-01

    The energy density of current lithium-ion batteries (LIBs) based on layered LiMO2 cathodes (M = Ni, Mn, Co: NMC; M = Ni, Co, Al: NCA) needs to be improved significantly in order to compete with internal combustion engines and allow for widespread implementation of electric vehicles (EVs). In this report, we show that atomic layer deposition (ALD) of titania (TiO2) and alumina (Al2O3) on Ni-rich FCG NMC and NCA active material particles could substantially improve LIB performance and allow for increased upper cutoff voltage (UCV) during charging, which delivers significantly increased specific energy utilization. Our results show that Al2O3 coating improved the NMC cycling performance by 40% and the NCA cycling performance by 34% at 1 C/-1 C with respectively 4.35 V and 4.4 V UCV in 2 Ah pouch cells. High resolution TEM/SAED structural characterization revealed that Al2O3 coatings prevented surface-initiated layered-to-spinel phase transitions in coated materials which were prevalent in uncoated materials. EIS confirmed that Al2O3-coated materials had significantly lower increase in the charge transfer component of impedance during cycling. The ability to mitigate degradation mechanisms for Ni-rich NMC and NCA illustrated in this report provides insight into a method to enable the performance of high-voltage LIBs.

  1. Metal oxides modified NiO catalysts for oxidative dehydrogenation of ethane to ethylene

    KAUST Repository

    Zhu, Haibo; Dong, Hailin; Laveille, Paco; Saih, Youssef; Caps, Valerie; Basset, Jean-Marie

    2014-01-01

    in contrast to pure NiO. The introduction of group IV, V and VI transition metals into NiO decreases the catalytic activity in ethane ODH. However, the ethylene selectivity is enhanced with the highest level for the Ni-W-O and Ni-Ti-O catalysts. As a result

  2. Plasticity and microstructure of epitaxial Ag/Ni multilayers; Mechanische Eigenschaften und Mikrostruktur epitaktischer Ag/Ni-Multilagenschichten

    Energy Technology Data Exchange (ETDEWEB)

    Schmidt, Tobias K.

    2007-10-15

    To meet the still increasing technical demands of new materials, it is required to improve basic knowledge of thin films and multilayers. This thesis describes the microstructure and mechanical behaviour of thin epitaxial Ag/Ni-multilayers. Former investigations were only done on polycrystalline multilayers or epitaxial single layers. The manufacture of epitaxial Ag/Ni-multilayers on (111) orientated Si-substrates was performed by a magnetron sputtering technique under ultra high vacuum (UHV). The thickness of the alternating Ag- and Ni-layers varies between 100 and 400 nm, the thickness of the whole film varies between 200 and 800 nm. Hardness and flow stress of Ag/Ni-multilayers were measured with a nanoindentation technique, a substrate curvature method and by X-ray diffraction. The hardness of these multilayers varies between 1.5 and 2.0 GPa. The Ag single film hardness is 0.5 GPa and Ni film 1.8 GPa. The flow stress of the Ag/Ni-multilayers varies between 350 and 800 MPa. The Ag single layer shows a flow stress of 100 MPa and Ni of 450 MPa. Both hardness and flow stress increase with decreasing layer thickness. In situ TEM and HRTEM experiments showed a semicoherent Ag/Ni-interface. It was observed that these interfaces act as sources and sinks. Dislocation loops formed at the interface expand and shrink according to the stress state. They combine with loops from the opposite interface or with the interface itself and form threading dislocations. Dislocation loops penetrating an interface were not observed. Results were compared with various models which simulate flow stress in thin films and multilayers. The most important models are calculated by Nix-Freund, the Source-model after von Blanckenhagen and the Hall-Petch-model. (orig.)

  3. Cube textured CeO2, BaZrO3 and LaAlO3 buffer layers on Ni based Substrates

    International Nuclear Information System (INIS)

    Deinhofer, C; Gritzner, G

    2006-01-01

    CeO 2 , BaZrO 3 as well as LaAlO 3 buffer layers were deposited on {100} Ni + 5 weight-% W substrates by a wet chemical technique. The solutions were prepared by dissolving the metal nitrates or acetates and zirconiumacetylacetonate, respectively, in mixtures of acetic acid, methanol and water. The solutions were applied by dip- or spincoating, dried at 135 deg. C and annealed at temperatures between 900 and 1 400 deg. C depending on the buffer layer for 15 min. under Ar-5% H 2 gas flow. Pole-figure measurements proved the exact texture of each buffer layer. Electron microscopy showed dense and smooth buffer layers

  4. Surface free energy of TiC layers deposited by electrophoretic deposition (EPD)

    Science.gov (United States)

    Gorji, Mohammad Reza; Sanjabi, Sohrab

    2018-01-01

    In this study porous structure coatings of bare TiC (i.e. 20 nm, 0.7 µm and 5/45 µm) and core-shell structures of TiC/NiP synthesized through electroless plating were deposited by EPD. Room temperature surface free energy (i.e. γs) of TiC and TiC/NiP coatings were determined via measuring contact angles of distilled water and diiodemethane liquids. The effect of Ni-P shell on spreading behavior of pure copper on porous EPD structures was also investigated by high temperature wetting experiments. According to the results existence of a Ni-P layer around the TiC particles has led to roughness (i.e. at least 0.1 µm), and porosity mean length (i.e. at least 1 µm) increase. This might be related to various sizes of TiC agglomerates formed during electroless plating. It has been observed that room temperature γs changed from 44.49 to 54.12 mJ.m-2 as a consequence of particle size enlargement for TiC. The highest and lowest (67.25 and 44.49 mJ.m-2) γs were measured for TiC nanoparticles which showed 1.5 times increase in surface free energy after being plated with Ni-P. It was also observed that plating Ni-P altered non-spreading (θs > 100 o) behavior of TiC to full-spreading ((θs 0o)) which can be useful for preparation of hard coatings by infiltration sintering phenomenon. Zeta potential of EPD suspensions, morphology, phase structure and topography of as-EPD layers were investigated through Zetasizer, field emission scanning electron microscopy (FESEM), X-ray diffraction (XRD) and atomic force microscopy (AFM) instruments respectively.

  5. Thermal stability of Ni-Pt-Ta alloy silicides on epi-Si1-xCx

    International Nuclear Information System (INIS)

    Yoo, Jung-Ho; Chang, Hyun-Jin; Min, Byoung-Gi; Ko, Dae-Hong; Cho, Mann-Ho; Sohn, Hyunchul; Lee, Tae-Wan

    2008-01-01

    We investigated the silicide formation in Ni/epi-Si 1-x C x systems. Ni-Pt and Ni-Pt-Ta films were deposited on epi-Si 1-x C x /Si substrates by DC magnetron sputtering and processed at various temperatures. The sheet resistance of the silicide from the Ni alloy/epi-Si 1-x C x systems was maintained at low values compared to that from Ni/Si systems. By TEM and EDS analyses, we confirmed the presence of a Pt alloy layer at the top of the Ni-silicide layer. The stability of the silicide layer in the Ni alloy/epi-Si 1-x C x system is explained by not only the Pt rich layer on the top of the Ni-silicide layer, but also by the presence of a small amount of Pt in the Ni-silicide layer or at the grain boundaries. And both the thermal stability and the morphology of silicide were greatly improved by the addition of Ta in Ni-Pt films

  6. Shape and size effects on layered Ni/PZT/Ni composites magnetoelectric performance

    Energy Technology Data Exchange (ETDEWEB)

    Pan, D A; Zhang, S G; Qiao, L J [School of Materials Science and Engineering, University of Science and Technology Beijing, Beijing 100083 (China); Volinsky, Alex A [Department of Mechanical Engineering, University of South Florida, Tampa FL 33620 (United States)], E-mail: lqiao@ustb.edu.cn

    2008-09-07

    This paper presents the magnetoelectric (ME) effect in trilayered Ni/PZT/Ni composites which is related to their size and shape. The ME composites with the same interfacial areas but different geometrical shapes have different ME voltage coefficients. Longitudinal resonant modes in the rectangular and triangular trilayered ME composites were studied. One should choose optimized size, shape and working frequency of the ME composites in order to gain the maximum ME effect. This study plays a guiding role for trilayered ME composites design for real applications. (fast track communication)

  7. Defect-rich Ni-Ti layered double hydroxide as a highly efficient support for Au nanoparticles in base-free and solvent-free selective oxidation of benzyl alcohol.

    Science.gov (United States)

    Liu, Mengran; Fan, Guoli; Yu, Jiaying; Yang, Lan; Li, Feng

    2018-04-17

    Tuning the surface properties of supported metal catalysts is of vital importance for governing their catalytic performances in nanocatalysis. Here, we report highly dispersed nanometric gold nanoparticles (NPs) supported on Ni-Ti layered double hydroxides (NiTi-LDHs), which were employed in solvent-free and base-free selective oxidation of benzyl alcohol. A series of characterization techniques demonstrated that defect-rich NiTi-LDHs could efficiently stabilize Au NPs and decrease surface electron density of Au NPs. The as-formed Au/NiTi-LDH catalyst with a Ni/Ti molar ratio of 3 : 1 and an Au loading of 0.71 wt% yielded the highest turnover frequency value of ∼4981 h-1 at 120 °C among tested Au/NiTi-LDH catalysts with different Ni/Ti molar ratios, along with a high benzaldehyde selectivity of 98%. High catalytic efficiency of the catalyst was mainly correlated with surface cooperation between unique defects (i.e. defective Ti3+ species and oxygen vacancies) and abundant hydroxyl groups on the brucite-like layers of the NiTi-LDH support, which could lead to the preferential adsorption and activation of an alcohol hydroxyl moiety in benzyl alcohol and oxygen molecule, as well as the formation of more electron-deficient Ni3+ and Au0 species on the catalyst surface. Furthermore, the present Au/NiTi-LDH catalyst tolerated the oxidation of a wide variety of substrate structures into the corresponding aldehydes, acids or ketones. Our primary results illustrate that defect-rich NiTi-LDHs are promising supports which can efficiently modify surface structure and electronic properties of supported metal catalysts and consequently improve their catalytic performances.

  8. Ion-exchange mechanism of layered transition-metal oxides: case study of LiNi(0.5)Mn(0.5)O₂.

    Science.gov (United States)

    Gwon, Hyeokjo; Kim, Sung-Wook; Park, Young-Uk; Hong, Jihyun; Ceder, Gerbrand; Jeon, Seokwoo; Kang, Kisuk

    2014-08-04

    An ion-exchange process can be an effective route to synthesize new quasi-equilibrium phases with a desired crystal structure. Important layered-type battery materials, such as LiMnO2 and LiNi(0.5)Mn(0.5)O2, can be obtained through this method from a sodium-containing parent structure, and they often show electrochemical properties remarkably distinct from those of their solid-state synthesized equivalents. However, while ion exchange is generally believed to occur via a simple topotactic reaction, the detailed phase transformation mechanism during the process is not yet fully understood. For the case of layered LiNi(0.5)Mn(0.5)O2, we show through ex situ X-ray diffraction (XRD) that the ion-exchange process consists of several sequential phase transformations. By a study of the intermediate phase, it is shown that the residual sodium ions in the final structure may greatly affect the electrochemical (de)lithiation mechanism.

  9. In-situ observation of equilibrium transitions in Ni films; agglomeration and impurity effects.

    Science.gov (United States)

    Thron, Andrew M; Greene, Peter; Liu, Kai; van Benthem, Klaus

    2014-02-01

    Dewetting of ultra-thin Ni films deposited on SiO2 layers was observed, in cross-section, by in situ scanning transmission electron microscopy. Holes were observed to nucleate by voids which formed at the Ni/SiO2 interface rather than at triple junctions at the free surface of the Ni film. Ni islands were observed to retract, in attempt to reach equilibrium on the SiO2 layer. SiO2 layers with 120 nm thickness were found to limit in situ heating experiments due to poor thermal conductivity of SiO2. The formation of graphite was observed during the agglomeration of ultra-thin Ni films. Graphite was observed to wet both the free surface and the Ni/SiO2 interface of the Ni islands. Cr forms surface oxide layers on the free surface of the SiO2 layer and the Ni islands. Cr does not prevent the dewetting of Ni, however it will likely alter the equilibrium shape of the Ni islands. © 2013 Published by Elsevier B.V.

  10. Microstructure of aluminized coating on a Ni-Cr alloy after annealing treatment

    International Nuclear Information System (INIS)

    Huang, H.-L.; Gan Dershin

    2008-01-01

    The effects of annealing on the microstructure of first stage (high-Al activity pack) aluminized coating on Ni-15Cr alloy prepared by pack cementation method were analyzed by transmission electron microscope. The coating consists of a thin layer of γ'-Ni 3 Al, an interfacial zone of mixed β-NiAl and α-Cr, and a thick outer zone of β-NiAl (A layer) and mixed β-NiAl and α-Cr (B layer). Martensitic transformation was observed in the β-NiAl grains in the interfacial zone. Parallel crystallographic relationship was found at the γ/γ' interface in the substrate and the α/β interface in the interfacial zone. Cr 2 Al was found to precipitate in the β-NiAl and α-Cr grains in the B layer of the outer zone. The formation mechanisms of the coating layers, the precipitates, and the observed crystallographic relationships are discussed

  11. Tribological Properties of Surface-Textured and Plasma-Nitrided Pure Titanium Under Oil Lubrication Condition

    Science.gov (United States)

    Zhang, Baosen; Dong, Qiangsheng; Ba, Zhixin; Wang, Zhangzhong; Shi, Hancheng; Xue, Yanting

    2018-01-01

    Plasma nitriding was conducted as post-treatment for surface texture on pure titanium to obtain a continuous nitriding layer. Supersonic fine particles bombarding (SFPB) was carried out to prepare surface texture. The surface morphologies and chemical composition were analyzed using scanning electron microscope and energy disperse spectroscopy. The microstructures of modified layers were characterized by transmission electron microscope. The tribological properties of surface-textured and duplex-treated pure titanium under oil lubrication condition were systematically investigated in the ball-on-plate reciprocating mode. The effects of applied load and sliding velocity on the tribological behavior were analyzed. The results show that after duplex treatments, the grains size in modified layer becomes slightly larger, and hardness is obviously improved. Wear resistance of duplex-treated pure titanium is significantly improved referenced to untreated and surface-textured pure titanium, which is 3.22 times as much as untreated pure titanium and 2.15 times of that for surface-textured pure titanium, respectively.

  12. In-situ observation of equilibrium transitions in Ni films; agglomeration and impurity effects

    Energy Technology Data Exchange (ETDEWEB)

    Thron, Andrew M., E-mail: AMThron@lbl.gov [Department of Chemical Engineering and Materials Science, University of California, Davis, CA 95616 (United States); Greene, Peter; Liu, Kai [Department of Physics, University of California, Davis, CA 95616 (United States); Benthem, Klaus van [Department of Chemical Engineering and Materials Science, University of California, Davis, CA 95616 (United States)

    2014-02-01

    Dewetting of ultra-thin Ni films deposited on SiO{sub 2} layers was observed, in cross-section, by in situ scanning transmission electron microscopy. Holes were observed to nucleate by voids which formed at the Ni/SiO{sub 2} interface rather than at triple junctions at the free surface of the Ni film. Ni islands were observed to retract, in attempt to reach equilibrium on the SiO{sub 2} layer. SiO{sub 2} layers with 120 nm thickness were found to limit in situ heating experiments due to poor thermal conductivity of SiO{sub 2}. The formation of graphite was observed during the agglomeration of ultra-thin Ni films. Graphite was observed to wet both the free surface and the Ni/SiO{sub 2} interface of the Ni islands. Cr forms surface oxide layers on the free surface of the SiO{sub 2} layer and the Ni islands. Cr does not prevent the dewetting of Ni, however it will likely alter the equilibrium shape of the Ni islands. - Highlights: • In Situ observation of dewetting in ultra-thin Ni films sputtered on SiO{sub 2} layers. • Dewetting is observed in an edge-on position by in situ STEM. • Characterization of interface structure pre and post in situ annealing by STEM and EELS. • Analyze the effects of Cr{sub 1−x}O{sub x} and graphite impurities on the Ni film agglomeration. • Examine influence of the SiO{sub 2} layers on the dewetting process.

  13. Superb adsorption capacity of hierarchical calcined Ni/Mg/Al layered double hydroxides for Congo red and Cr(VI) ions

    Energy Technology Data Exchange (ETDEWEB)

    Lei, Chunsheng [State Key Laboratory of Advanced Technology for Materials Synthesis and Processing, Wuhan University of Technology, Wuhan 430070 (China); College of Environmental & Safety Engineering, Changzhou University, Changzhou 213164 (China); Zhu, Xiaofeng [College of Environmental & Safety Engineering, Changzhou University, Changzhou 213164 (China); Zhu, Bicheng; Jiang, Chuanjia; Le, Yao [State Key Laboratory of Advanced Technology for Materials Synthesis and Processing, Wuhan University of Technology, Wuhan 430070 (China); Yu, Jiaguo, E-mail: jiaguoyu@yahoo.com [State Key Laboratory of Advanced Technology for Materials Synthesis and Processing, Wuhan University of Technology, Wuhan 430070 (China); Department of Physics, Faculty of Science, King Abdulaziz University, Jeddah 21589 (Saudi Arabia)

    2017-01-05

    Highlights: • Ni/Mg/Al layered double hydroxides (NMA-LDHs) synthesized. • NMA-LDHs with hierarchically hollow microsphere structure. • Calcined NMA-LDHs have large adsorption capacities for CR and Cr(VI) ions. - Abstract: The preparation of hierarchical porous materials as catalysts and sorbents has attracted much attention in the field of environmental pollution control. Herein, Ni/Mg/Al layered double hydroxides (NMA-LDHs) hierarchical flower-like hollow microspheres were synthesized by a hydrothermal method. After the NMA-LDHs was calcined at 600 °C, NMA-LDHs transformed into Ni/Mg/Al layered double oxides (NMA-LDOs), which maintained the hierarchical flower-like hollow structure. The crystal phase, morphology, and microstructure of the as-prepared samples were characterized by X-ray diffraction, scanning electron microscopy, transmission electron microscopy, energy-dispersive X-ray spectroscopy elemental mapping, Fourier transform infrared spectroscopy, and nitrogen adsorption−desorption methods. Both the calcined and non-calcined NMA-LDHs were examined for their performance to remove Congo red (CR) and hexavalent chromium (Cr(VI)) ions in aqueous solution. The maximum monolayer adsorption capacities of CR and Cr(VI) ions over the NMA-LDOs sample were 1250 and 103.4 mg/g at 30 °C, respectively. Thermodynamic studies indicated that the adsorption process was endothermic in nature. In addition, the addition of coexisting anions negatively influenced the adsorption capacity of Cr(VI) ions, in the following order: CO{sub 3}{sup 2−} > SO{sub 4}{sup 2−} > H{sub 2}PO{sub 4}{sup −} > Cl{sup −}. This work will provide new insight into the design and fabrication of advanced adsorption materials for water pollutant removal.

  14. The effect of an atomically deposited layer of alumina on NiO in P-type dye-sensitized solar cells.

    Science.gov (United States)

    Natu, Gayatri; Huang, Zhongjie; Ji, Zhiqiang; Wu, Yiying

    2012-01-10

    We present a systematic investigation of the fundamental effects of an atomically deposited alumina (AlO(x)H(y)) onto the NiO films in p-type dye-sensitized solar cells (p-DSCs). With P1 as the sensitizing dye and 0.1 M I(2) and 1.0 M LiI in 3-methoxypropionitrile as the electrolyte, one atomic layer deposition (ALD) cycle of alumina was used to achieve a 74% increase in the overall conversion efficiency of a NiO-based DSC. The open circuit voltage of the cells increased from 0.11 to 0.15 V, and the short circuit current density increased from 0.83 to 0.95 mA/cm(2). Adsorption isotherm studies were performed to show that the amount of dye adsorbed on the NiO-alumina film is slightly lower than the amount adsorbed on the nontreated NiO film. The increased J(sc) was therefore assigned to the increased efficiency of carrier collection at the semiconductor-FTO interface. Our study of the photocurrent onset potentials of NiO and NiO-alumina films with the chopped light measurement technique showed no definitive difference in the onset potential values. However, the DSCs based on NiO-alumina showed a higher recombination resistance value from the electrochemical impedance studies and a higher diode ideality factor from the V(oc) versus ln(light intensity) plots as compared to the DSCs based on untreated NiO. It has thus been established that the increase in V(oc) upon alumina treatment arises due to a higher resistance for electron-hole recombination across NiO surface locally.

  15. Development of small-scale electroplating system for Ni-63 electroplating onto Ni foil

    International Nuclear Information System (INIS)

    Kim, Jin Joo; Choi, Sang Mu; Son, Kwang Jae; Hong, Jintae

    2016-01-01

    Betavoltaic battery is a device that converts the decay energy of beta-emitting radioisotopes into electric energy. Ni-63 is pure betaemitter with a low energy spectrum and significantly long half-life of 100.1 years and thus is widely used as the power source of betavoltaic battery. There are several methods for the formation of a Ni deposit onto a semiconductor such as electroplating, electroless plating, and chemical vapor deposition. In this study, small-scale radioisotope electroplating system was designed and fabricated to perform electroplating with a small amount of plating buffer and minimum exposure of radioactive materials. These procedures and the manufactured electroplating device can be applied to radioactive Ni-63 electroplating for the fabrication of a betavoltaic battery. In this study, an electroplating system for small-scale Ni electroplating was designed and manufactured. The process for the fabrication of a Ni-63 foil as the energy source of a betavoltaic battery was developed using the minimum concentration of Ni. These procedures and the manufactured electroplating device can be applied to radioactive Ni-63 electroplating for the fabrication of a betavoltaic battery

  16. Development of small-scale electroplating system for Ni-63 electroplating onto Ni foil

    Energy Technology Data Exchange (ETDEWEB)

    Kim, Jin Joo; Choi, Sang Mu; Son, Kwang Jae; Hong, Jintae [Korea Atomic Energy Research Institute, Daejeon (Korea, Republic of)

    2016-10-15

    Betavoltaic battery is a device that converts the decay energy of beta-emitting radioisotopes into electric energy. Ni-63 is pure betaemitter with a low energy spectrum and significantly long half-life of 100.1 years and thus is widely used as the power source of betavoltaic battery. There are several methods for the formation of a Ni deposit onto a semiconductor such as electroplating, electroless plating, and chemical vapor deposition. In this study, small-scale radioisotope electroplating system was designed and fabricated to perform electroplating with a small amount of plating buffer and minimum exposure of radioactive materials. These procedures and the manufactured electroplating device can be applied to radioactive Ni-63 electroplating for the fabrication of a betavoltaic battery. In this study, an electroplating system for small-scale Ni electroplating was designed and manufactured. The process for the fabrication of a Ni-63 foil as the energy source of a betavoltaic battery was developed using the minimum concentration of Ni. These procedures and the manufactured electroplating device can be applied to radioactive Ni-63 electroplating for the fabrication of a betavoltaic battery.

  17. Microstructure and Corrosion Behavior of Ni-Alloy/CrN Nanolayered Coatings

    Directory of Open Access Journals (Sweden)

    Hao-Hsiang Huang

    2011-01-01

    Full Text Available The Ni-alloy/CrN nanolayered coatings, Ni-Al/CrN and Ni-P/CrN, were deposited on (100 silicon wafer and AISI 420 stainless steel substrates by dual-gun sputtering technique. The influences of the layer microstructure on corrosion behavior of the nanolayered thin films were investigated. The bilayer thickness was controlled approximately 10 nm with a total coating thickness of 1m. The single-layer Ni-alloy and CrN coatings deposited at 350∘C were also evaluated for comparison. Through phase identification, phases of Ni-P and Ni-Al compounds were observed in the single Ni-alloy layers. On the other hand, the nanolayered Ni-P/CrN and Ni-Al/CrN coatings showed an amorphous/nanocrystalline microstructure. The precipitation of Ni-Al and Ni-P intermetallic compounds was suppressed by the nanolayered configuration of Ni-alloy/CrN coatings. Through Tafel analysis, the corr and corr values ranged from –0.64 to –0.33 V and 1.42×10−5 to 1.14×10−6 A/cm2, respectively, were deduced for various coating assemblies. The corrosion mechanisms and related behaviors of the coatings were compared. The coatings with a nanolayered Ni-alloy/CrN configuration exhibited a superior corrosion resistance to single-layer alloy or nitride coatings.

  18. Effect of Ni +-ION bombardment on nickel and binary nickel alloys

    Science.gov (United States)

    Roarty, K. B.; Sprague, J. A.; Johnson, R. A.; Smidt, F. A.

    1981-03-01

    Pure nickel and four binary nickel alloys have been subjected to high energy Ni ion bombardment at 675, 625 and 525°C. After irradiation, each specimen was studied by transmission electron microscopy. The pure nickel control was found to swell appreciably (1 to 5%) and the Ni-Al and the Ni-Ti samples were found to swell at all temperatures, but to a lesser degree (0.01 to 0.35%). The Ni-Mo contained a significant density of voids only at 525° C, while swelling was suppressed at all temperatures in the Ni-Si alloy. The dislocation structure progressed from loops to tangles as temperature increased in all materials except the Ni-Ti, in which there was an absence of loops at all temperatures. Dislocation densities decreased as temperature increased in all samples. These results do not correlate well with the relative behavior of the same alloys observed after neutron irradiation at 455°C. The differences between these two sets of data appear to be caused by different mechanisms controlling void nucleation in ion and neutron irradiation of these alloys.

  19. Fabrication of low reflective nanopore-type black Si layer using one-step Ni-assisted chemical etching for Si solar cell application

    Science.gov (United States)

    Takaloo, AshkanVakilipour; Kolahdouz, Mohammadreza; Poursafar, Jafar; Es, Firat; Turan, Rasit; Ki-Joo, Seung

    2018-03-01

    Nanotextured Si fabricated through metal-assisted chemical etching (MACE) technique exhibits a promising potential for producing antireflective layer for photovoltaic (PV) application. In this study, a novel single-step nickel (Ni) assisted etching technique was applied to produce an antireflective, nonporous Si (black Si) in an aqueous solution containing hydrofluoric acid (HF), hydrogen peroxide (H2O2) and NiSO4 at 40 °C. Field emission scanning electron microscope was used to characterize different morphologies of the textured Si. Optical reflection measurements of samples were carried out to compare the reflectivity of different morphologies. Results indicated that vertical as well as horizontal pores with nanosized diameters were bored in the Si wafer after 1 h treatment in the etching solution containing different molar ratios of H2O2 to HF. Increasing H2O2 concentration in electrochemical etching solution had a considerable influence on the morphology due to higher injection of positive charges from Ni atoms onto the Si surface. Optimized concentration of H2O2 led to formation of an antireflective layer with 2.1% reflectance of incident light.

  20. Electrochemical kinetic performances of electroplating Co–Ni on La–Mg–Ni-based hydrogen storage alloys

    Energy Technology Data Exchange (ETDEWEB)

    Li, Yuan; Tao, Yang; Ke, Dandan; Ma, Yufei [Hebei Key Laboratory of Applied Chemistry, School of Environmental and Chemical Engineering, Yanshan University, Qinhuangdao 066004 (China); Han, Shumin, E-mail: hanshm@ysu.edu.cn [Hebei Key Laboratory of Applied Chemistry, School of Environmental and Chemical Engineering, Yanshan University, Qinhuangdao 066004 (China); State Key Laboratory of Metastable Materials Science and Technology, Yanshan University, Qinhuangdao 066004 (China)

    2015-12-01

    Graphical abstract: - Highlights: • The Co–Ni composite coating was prepared by electroplating. • The alloy treated at 10 mA/cm{sup 2} has superior kinetic performances. • The Co–Ni layer accelerates the charge transfer rate on the surface of the alloy. - Abstract: Electroplating Co–Ni treatment was applied to the surface of the La{sub 0.75}Mg{sub 0.25}Ni{sub 3.48} alloy electrodes in order to improve the electrochemical and kinetic performances. The Scanning electron microscope-Energy dispersive spectroscopy and X-ray diffraction results showed that the electrodes were plated with a homogeneous Co–Ni alloy film. The alloy coating significantly improved the high rate dischargeability of the alloy electrode, and the HRD value increased to 57.5% at discharge current density 1875 mA/g after the Co–Ni-coating. The exchange current density I{sub 0}, the limiting current density I{sub L} and the oxidation peak current also increased for the coated alloy. The improvement of overall electrode performances was attributed to an enhancement in electro-catalytic activity and conductivity at the alloy surface, owing to the precipitation of the Co–Ni layer.

  1. Effect of Cu Alloying on S Poisoning of Ni Surfaces and Nanoparticle Morphologies Using Ab-Initio Thermodynamics Calculations.

    Science.gov (United States)

    Kim, Ji-Su; Kim, Byung-Kook; Kim, Yeong-Cheol

    2015-10-01

    We investigated the effect of Cu alloying on S poisoning of Ni surfaces and nanoparticle morphologies using ab-initio thermodynamics calculations. Based on the Cu segregation energy and the S adsorption energy, the surface energy and nanoparticle morphology of pure Ni, pure Cu, and NiCu alloys were evaluated as functions of the chemical potential of S and the surface orientations of (100), (110), and (111). The constructed nanoparticle morphology was varied as a function of chemical potential of S. We find that the Cu added to Ni for NiCu alloys is strongly segregated into the top surface, and increases the S tolerance of the NiCu nanoparticles.

  2. Mechanical properties of highly textured Cu/Ni multilayers

    International Nuclear Information System (INIS)

    Liu, Y.; Bufford, D.; Wang, H.; Sun, C.; Zhang, X.

    2011-01-01

    We report on the synthesis of highly (1 1 1) and (1 0 0) textured Cu/Ni multilayers with individual layer thicknesses, h, varying from 1 to 200 nm. When, h, decreases to 5 nm or less, X-ray diffraction spectra show epitaxial growth of Cu/Ni multilayers. High resolution transmission electron microscopy studies show the coexistence of nanotwins and coherent layer interfaces in highly (1 1 1) textured Cu/Ni multilayers with smaller h. Hardnesses of multilayer films increase with decreasing h, approach a maximum at h of a few nanometers, and show softening thereafter at smaller h. The influence of layer interfaces as well as twin interfaces on strengthening mechanisms of multilayers and the formation of twins in Ni in multilayers are discussed.

  3. Effects of concentration of Ag nanoparticles on surface structure and in vitro biological responses of oxide layer on pure titanium via plasma electrolytic oxidation

    Energy Technology Data Exchange (ETDEWEB)

    Shin, Ki Ryong; Kim, Yeon Sung; Kim, Gye Won [Department of Materials Science and Engineering, Hanyang University, Ansan 425-791 (Korea, Republic of); Yang, Hae Woong [School of Materials Science and Engineering, Yeungnam University, Gyeongsan 712-749 (Korea, Republic of); Ko, Young Gun, E-mail: younggun@ynu.ac.kr [School of Materials Science and Engineering, Yeungnam University, Gyeongsan 712-749 (Korea, Republic of); Shin, Dong Hyuk, E-mail: dhshin@hanyang.ac.kr [Department of Materials Science and Engineering, Hanyang University, Ansan 425-791 (Korea, Republic of)

    2015-08-30

    Highlights: • Ag nanoparticles were embedded into the oxide surface without any compositional changes. • Oxide layer from the electrolyte with 0.1 g/l Ag nanoparticles could disinfect all bacteria. • With increasing Ag nanoparticles, bone-forming ability and cell proliferation rate decrease. - Abstract: This study was to investigate how Ag nanoparticles with various concentrations affect the surface structure and in vitro biological properties of oxide layers on the pure titanium produced by a plasma electrolytic oxidation (PEO) process. For this aim, PEO processes were carried out at an AC current density of 100 mA/cm{sup 2} for 300 s in potassium pyrophosphate (K{sub 4}P{sub 2}O{sub 7}) electrolytes containing 0, 0.1, 0.3 and 0.5 g/l Ag nanoparticles. Structural investigations using scanning electron microscopy evidenced that the oxide layers showed the successful incorporation of Ag nanoparticles, and the topographical deformation of the porous surface was found when the concentration of Ag nanoparticles was more than 0.1 g/l. Based on the anti-bacterial activity of all oxide layers, the Ag nanoparticles uniformly spread were of considerable importance in triggering the disinfection of E. coli bacteria. The bone forming abilities and cell (MC3T3-E1) proliferation rates of oxide layers produced in electrolytes containing 0 and 0.1 g/l Ag nanoparticles were higher than those containing 0.3 and 0.5 g/l Ag nanoparticles. Consequently, the oxide layer on pure titanium via PEO process in the electrolyte with 0.1 g/l Ag nanoparticles exhibited better the bioactivity accompanying the anti-bacterial activity.

  4. Thin NiTi Films Deposited on Graphene Substrates

    Science.gov (United States)

    Hahn, S.; Schulze, A.; Böhme, M.; Hahn, T.; Wagner, M. F.-X.

    2017-03-01

    We present experimental results on the deposition of Nickel Titanium (NiTi) films on graphene substrates using a PVD magnetron sputter process. Characterization of the 2-4 micron thick NiTi films by electron microscopy, electron backscatter diffraction, and transmission electron microscopy shows that grain size and orientation of the thin NiTi films strongly depend on the type of combination of graphene and copper layers below. Our experimental findings are supported by density functional theory calculations: a theoretical estimation of the binding energies of different NiTi-graphene interfaces is in line with the experimentally determined microstructural features of the functional NiTi top layer.

  5. Effect of copper concentration on the physical properties of copper doped NiO thin films deposited by spray pyrolysis

    Energy Technology Data Exchange (ETDEWEB)

    Mani Menaka, S., E-mail: manimenaka.phy@gmail.com [PG and Research Department of Physics, Government Arts College, Coimbatore, 641018, Tamilnadu (India); Umadevi, G. [PG and Research Department of Physics, Government Arts College, Coimbatore, 641018, Tamilnadu (India); Manickam, M. [SRMV College of Arts and Science, Coimbatore, 641020, Tamilnadu (India)

    2017-04-15

    The spray pyrolysis (SP) technique is an important and powerful method for the preparation of nickel oxide (NiO) and copper-doped nickel oxide thin films. The best films were obtained when the substrate temperature, T{sub s} = 450 °C on glass substrates. Copper (Cu) concentrations in the films were varied from 0 to 8%. The effect of Cu concentration on the structural, morphological, spectral, optical, and electrical properties of the thin films were studied by X-ray diffraction (XRD), Scanning electron microscopy (SEM), Fourier transformed infrared spectroscopy (FTIR), UV–vis–NIR spectrophotometer, Hot probe and Hall system. The X-ray diffraction result shows the polycrystalline cubic structure of sprayed films with (200) preferred orientation. The variations of the structural parameters such as lattice parameters and grain sizes were investigated. The SEM image displays the surface morphology of the NiO and Cu:NiO thin films. The FTIR of the as-deposited films were associated with chemical identification. The optical transmittance and absorbance spectra of the films were measured by UV–vis–NIR spectrophotometer. The absorption coefficient and band gaps of the films were calculated using the optical method. All the NiO and Cu:NiO films were p-type. The resistivity of the above films decreases with the increase in copper concentration and so the conductivity of the films depend on the precursor concentration. - Highlights: • Pure and Cu:NiO films were deposited by Spray pyrolysis technique. • The XRD result shows the polycrystalline nature of pure and Cu:NiO films. • The formation of pure and Cu:NiO were confirmed by FTIR analysis. • Band gap values of pure and Cu:NiO decreases. • All the pure and Cu:NiO films were p-type.

  6. Effect of copper concentration on the physical properties of copper doped NiO thin films deposited by spray pyrolysis

    International Nuclear Information System (INIS)

    Mani Menaka, S.; Umadevi, G.; Manickam, M.

    2017-01-01

    The spray pyrolysis (SP) technique is an important and powerful method for the preparation of nickel oxide (NiO) and copper-doped nickel oxide thin films. The best films were obtained when the substrate temperature, T_s = 450 °C on glass substrates. Copper (Cu) concentrations in the films were varied from 0 to 8%. The effect of Cu concentration on the structural, morphological, spectral, optical, and electrical properties of the thin films were studied by X-ray diffraction (XRD), Scanning electron microscopy (SEM), Fourier transformed infrared spectroscopy (FTIR), UV–vis–NIR spectrophotometer, Hot probe and Hall system. The X-ray diffraction result shows the polycrystalline cubic structure of sprayed films with (200) preferred orientation. The variations of the structural parameters such as lattice parameters and grain sizes were investigated. The SEM image displays the surface morphology of the NiO and Cu:NiO thin films. The FTIR of the as-deposited films were associated with chemical identification. The optical transmittance and absorbance spectra of the films were measured by UV–vis–NIR spectrophotometer. The absorption coefficient and band gaps of the films were calculated using the optical method. All the NiO and Cu:NiO films were p-type. The resistivity of the above films decreases with the increase in copper concentration and so the conductivity of the films depend on the precursor concentration. - Highlights: • Pure and Cu:NiO films were deposited by Spray pyrolysis technique. • The XRD result shows the polycrystalline nature of pure and Cu:NiO films. • The formation of pure and Cu:NiO were confirmed by FTIR analysis. • Band gap values of pure and Cu:NiO decreases. • All the pure and Cu:NiO films were p-type.

  7. Formation of defect-fluorite structured NdNiOxHy epitaxial thin films via a soft chemical route from NdNiO3 precursors.

    Science.gov (United States)

    Onozuka, T; Chikamatsu, A; Katayama, T; Fukumura, T; Hasegawa, T

    2016-07-26

    A new phase of oxyhydride NdNiOxHy with a defect-fluorite structure was obtained by a soft chemical reaction of NdNiO3 epitaxial thin films on a substrate of SrTiO3 (100) with CaH2. The epitaxial relationship of this phase relative to SrTiO3 could be controlled by changing the reaction temperature. At 240 °C, NdNiOxHy grew with a [001] orientation, forming a thin layer of infinite-layer NdNiO2 at the interface between the NdNiOxHy and the substrate. Meanwhile, a high-temperature reaction at 400 °C formed [110]-oriented NdNiOxHy without NdNiO2.

  8. In-situ confined formation of NiFe layered double hydroxide quantum dots in expanded graphite for active electrocatalytic oxygen evolution

    Science.gov (United States)

    Guo, Jinxue; Li, Xiaoyan; Sun, Yanfang; Liu, Qingyun; Quan, Zhenlan; Zhang, Xiao

    2018-06-01

    Development of noble-metal-free catalysts towards highly efficient electrochemical oxygen evolution reaction (OER) is critical but challenging in the renewable energy area. Herein, we firstly embed NiFe LDHs quantum dots (QDs) into expanded graphite (NiFe LDHs/EG) via in-situ confined formation process. The interlayer spacing of EG layers acts as nanoreactors for spatially confined formation of NiFe LDHs QDs. The QDs supply huge catalytic sites for OER. The in-situ decoration endows the strong affinity between QDs with EG, thus inducing fast charge transfer. Based on the aforementioned benefits, the designed catalyst exhibits outstanding OER properties, in terms of small overpotential (220 mV required to generate 10 mA cm-2), low Tafel slope, and good durable stability, making it a promising candidate for inexpensive OER catalyst.

  9. Surface Surgery of the Nickel-Rich Cathode Material LiNi0.815Co0.15Al0.035O2: Toward a Complete and Ordered Surface Layered Structure and Better Electrochemical Properties.

    Science.gov (United States)

    Tang, Zhongfeng; Bao, Junjie; Du, Qingxia; Shao, Yu; Gao, Minghao; Zou, Bangkun; Chen, Chunhua

    2016-12-21

    A complete and ordered layered structure on the surface of LiNi 0.815 Co 0.15 Al 0.035 O 2 (NCA) has been achieved via a facile surface-oxidation method with Na 2 S 2 O 8 . The field-emission transmission electron microscopy images clearly show that preoxidation of the hydroxide precursor can eliminate the crystal defects and convert Ni(OH) 2 into layered β-NiOOH, which leads to a highly ordered crystalline NCA, with its (006) planes perpendicular to the surface in the sintering process. X-ray photoelectron spectroscopy and Raman shift results demonstrate that the contents of Ni 2+ and Co 2+ ions are reduced with preoxidization on the surface of the hydroxide precursor. The level of Li + /Ni 2+ disordering in the modified NCA determined by the peak intensity ratio I (003) /I (104) in X-ray diffraction patterns decreases. Thanks to the complete and ordered layered structure on the surface of secondary particles, lithium ions can easily intercalate/extract in the discharging-charging process, leading to greatly improved electrochemical properties.

  10. A study on the chemical stability and electrode performance of modified NiO cathodes for molten carbonate fuel cells

    International Nuclear Information System (INIS)

    Kim, Seung-Goo; Yoon, Sung Pil; Han, Jonghee; Nam, Suk Woo; Lim, Tae Hoon; Oh, In-Hwan; Hong, Seong-Ahn

    2004-01-01

    The chemical stabilities of modified NiO cathodes doped with 1.5 mol% CoO and 1.5 mol% LiCoO 2 fabricated by a conventional tape casting method were evaluated through the real MCFC single cell operation. The heat-treated samples before oxidation had proper porosities and microstructures for a MCFC cathode. At 150 mA cm -2 in current density, the MCFC single cell using a CoO-doped NiO cathode showed stable cell voltages in the range of 0.833-0.843 V for 1000 h. In contrast, the cell using a LiCoO 2 -doped NiO cathode with a maximum of 0.836 V at 500 h degraded to 0.826 V at 1000 h due to a wet seal breakdown at the cathode side. The amounts of nickel precipitated in the electrolytes of the cells using modified NiO cathodes doped with CoO and LiCoO 2 after the operation for 1000 h were 1.2 and 1.4 wt.%, respectively, which were about 60% lower than that of the standard cells using pure NiO cathodes. The enhanced chemical stability of modified NiO cathodes seems to be attributed to the fact that the presence of cobalt increases the lithium content in the cathodes by converting Ni 2+ to Ni 3+ , resulting in stabilizing the layered crystal structure

  11. NiCoCrAl/YSZ laminate composites fabricated by EB-PVD

    International Nuclear Information System (INIS)

    Shi Guodong; Wang Zhi; Liang Jun; Wu Zhanjun

    2011-01-01

    Highlights: → The metal-ceramic laminate composites were fabricated by EB-PVD. → Both metal and ceramic layers consisted of straight columns with banded structures. → Columnar grain size was limited by the periodic layer interfaces in the laminates. → Effect of columns on fracture property was decreased by limiting layer thickness. → Laminates showed greater specific strength than monolithic metal foil. - Abstract: Two NiCoCrAl/YSZ laminate composites (A and B) with different metal-layer thickness (∼35 μm and 14 μm, respectively) were fabricated by electron beam physical vapor deposition (EB-PVD). Their microstructure was examined and their mechanical properties were compared with the 289 μm thick NiCoCrAl monolithic foil produced by EB-PVD. Both the YSZ and NiCoCrAl layers of the laminate composites had columnar grain structure. But the periodic layer interfaces limited the columnar grain size. Some pores between the columns were also observed. It was found that the strength of the laminate A was equal approximately to that of the NiCoCrAl monolithic foil, and that laminate B had the greater strength. Moreover, the density of the foils decreased with the increasing thickness ratio of YSZ/NiCoCrAl layers and the increasing the layer number. Thus, comparing with the NiCoCrAl monolithic foil, the NiCoCrAl/YSZ laminate composites not only had the equal or greater strength, but also had the much greater specific strength.

  12. Multi-layers castings

    Directory of Open Access Journals (Sweden)

    J. Szajnar

    2010-01-01

    Full Text Available In paper is presented the possibility of making of multi-layers cast steel castings in result of connection of casting and welding coating technologies. First layer was composite surface layer on the basis of Fe-Cr-C alloy, which was put directly in founding process of cast carbon steel 200–450 with use of preparation of mould cavity method. Second layer were padding welds, which were put with use of TIG – Tungsten Inert Gas surfacing by welding technology with filler on Ni matrix, Ni and Co matrix with wolfram carbides WC and on the basis on Fe-Cr-C alloy, which has the same chemical composition with alloy, which was used for making of composite surface layer. Usability for industrial applications of surface layers of castings were estimated by criterion of hardness and abrasive wear resistance of type metal-mineral.

  13. Characterization of nanostructured photosensitive (NiS){sub x}(CdS){sub (1-x)} composite thin films grown by successive ionic layer adsorption and reaction (SILAR) route

    Energy Technology Data Exchange (ETDEWEB)

    Ubale, A.U., E-mail: ashokuu@yahoo.com [Nanostructured Thin Film Materials Laboratory, Department of Physics, Govt. Vidarbha Institute of Science and Humanities, Amravati 444604, Maharashtra (India); Bargal, A.N. [Nanostructured Thin Film Materials Laboratory, Department of Physics, Govt. Vidarbha Institute of Science and Humanities, Amravati 444604, Maharashtra (India)

    2011-07-15

    Highlights: {yields} Thin films of (NiS){sub x}(CdS){sub (1-x)} with variable composition (x = 1 to 0) were deposited onto glass substrates by the successive ionic layer adsorption and reaction (SILAR) method. {yields} The structural, surface morphological and electrical characterizations of the as deposited and annealed films were studied. {yields} The bandgap and activation energy of annealed (NiS){sub x}(CdS){sub (1-x)} film decrease with improvement in photosensitive nature. -- Abstract: Recently ternary semiconductor nanostructured composite materials have attracted the interest of researchers because of their photovoltaic applications. Thin films of (NiS){sub x}(CdS){sub (1-x)} with variable composition (x = 1-0) had been deposited onto glass substrates by the successive ionic layer adsorption and reaction (SILAR) method. As grown and annealed films were characterised by X-ray diffraction, scanning electron microscopy and EDAX to investigate structural and morphological properties. The (NiS){sub x}(CdS){sub (1-x)} films were polycrystalline in nature having mixed phase of rhombohedral and hexagonal crystal structure due to NiS and CdS respectively. The optical and electrical properties of (NiS){sub x}(CdS){sub (1-x)} thin films were studied to determine compsition dependent bandgap, activation energy and photconductivity. The bandgap and activation energy of annealed (NiS){sub x}(CdS){sub (1-x)} film decrease with improvement in photosensitive nature.

  14. Study of PtNi/C catalyst for direct ethanol fuel cell; Estudo do catalisador PtNi/C para celula a combustivel de etanol direto

    Energy Technology Data Exchange (ETDEWEB)

    Moraes, L.P.R. de; Silva, E.L. da; Amico, S.C.; Malfatti, C.F., E-mail: eticiaprm@gmail.com [Universidade Federal do Rio Grande do Sul (UFRGS), Porto Alegre, RS (Brazil)

    2014-07-01

    In this work, PtNi binary catalyst and pure platin catalyst were synthesized by the impregnation-reduction method, using Vulcan XC72R as support, for direct ethanol fuel cells. The composition and structure of the catalysts were analyzed by X-ray diffraction, the electrochemical behavior was evaluated by cyclic voltammetry and morphology of the catalysts was studied by high-resolution transmission electron microscopy. The results showed that the addition of Ni to Pt led to the contraction of the crystal lattice, increased the catalytic activity compared to pure Pt and initiated the electrooxidation of ethanol at lower potential. (author)

  15. Laser alloyed Al-Ni-Fe coatings

    CSIR Research Space (South Africa)

    Pityana, SL

    2008-10-01

    Full Text Available The aim of this work was to produce crack-free thin surface layers consisting of binary (Al-Ni, Al-Fe) and ternary (Al-Ni-Fe) intermetallic phases by means of a high power laser beam. The laser surface alloying was carried out by melting Fe and Ni...

  16. Characterization of oxide layers on amorphous Mg-based alloys by Auger electron spectroscopy with sputter depth profiling

    Energy Technology Data Exchange (ETDEWEB)

    Baunack, S.; Wolff, U. [Leibniz-Institut fuer Festkoerper- und Werkstoffforschung Dresden, Postfach 270016, 01171, Dresden (Germany); Subba Rao, R.V. [Indira Ghandi Centre for Atomic Research, 603 102, Kalpakkam, Tamil Nadu (India)

    2003-04-01

    Amorphous ribbons of Mg-Y-TM-[Ag](TM: Cu, Ni), prepared by melt spinning, were subjected to electrochemical investigations. Oxide layers formed anodically under potentiostatic control in different electrolytes were investigated by AES and sputter depth profiling. Problems and specific features of characterization of the composition of oxide layers and amorphous ternary or quaternary Mg-based alloys have been investigated. In the alloys the Mg(KL{sub 23}L{sub 23}) peak exhibits a different shape compared to that in the pure element. Analysis of the peak of elastically scattered electrons proved the absence of plasmon loss features, characteristic of pure Mg, in the alloy. A different loss feature emerges in Mg(KL{sub 23}L{sub 23}) and Cu(L{sub 23}VV). The system Mg-Y-TM-[Ag] suffers preferential sputtering. Depletion of Mg and enrichment of TM and Y are found. This is attributed mainly to the preferential sputtering of Mg. Thickness and composition of the formed oxide layer depend on the electrochemical treatment. After removing the oxide by sputtering the concentration of the underlying alloy was found to be affected by the treatment. (orig.)

  17. Highly Uniform Atomic Layer-Deposited MoS2@3D-Ni-Foam: A Novel Approach To Prepare an Electrode for Supercapacitors.

    Science.gov (United States)

    Nandi, Dip K; Sahoo, Sumanta; Sinha, Soumyadeep; Yeo, Seungmin; Kim, Hyungjun; Bulakhe, Ravindra N; Heo, Jaeyeong; Shim, Jae-Jin; Kim, Soo-Hyun

    2017-11-22

    This article takes an effort to establish the potential of atomic layer deposition (ALD) technique toward the field of supercapacitors by preparing molybdenum disulfide (MoS 2 ) as its electrode. While molybdenum hexacarbonyl [Mo(CO) 6 ] serves as a novel precursor toward the low-temperature synthesis of ALD-grown MoS 2 , H 2 S plasma helps to deposit its polycrystalline phase at 200 °C. Several ex situ characterizations such as X-ray diffractometry (XRD), Raman spectroscopy, X-ray photoelectron spectroscopy (XPS), and so forth are performed in detail to study the as-grown MoS 2 film on a Si/SiO 2 substrate. While stoichiometric MoS 2 with very negligible amount of C and O impurities was evident from XPS, the XRD and high-resolution transmission electron microscopy analyses confirmed the (002)-oriented polycrystalline h-MoS 2 phase of the as-grown film. A comparative study of ALD-grown MoS 2 as a supercapacitor electrode on 2-dimensional stainless steel and on 3-dimensional (3D) Ni-foam substrates clearly reflects the advantage and the potential of ALD for growing a uniform and conformal electrode material on a 3D-scaffold layer. Cyclic voltammetry measurements showed both double-layer capacitance and capacitance contributed by the faradic reaction at the MoS 2 electrode surface. The optimum number of ALD cycles was also found out for achieving maximum capacitance for such a MoS 2 @3D-Ni-foam electrode. A record high areal capacitance of 3400 mF/cm 2 was achieved for MoS 2 @3D-Ni-foam grown by 400 ALD cycles at a current density of 3 mA/cm 2 . Moreover, the ALD-grown MoS 2 @3D-Ni-foam composite also retains high areal capacitance, even up to a high current density of 50 mA/cm 2 . Finally, this directly grown MoS 2 electrode on 3D-Ni-foam by ALD shows high cyclic stability (>80%) over 4500 charge-discharge cycles which must invoke the research community to further explore the potential of ALD for such applications.

  18. Ferromagnetic resonance study of the half-Heusler alloy NiMnSb. The benefit of using NiMnSb as a ferromagnetic layer in pseudo-spin-valve based spin-torque oscillators

    Energy Technology Data Exchange (ETDEWEB)

    Riegler, Andreas

    2011-11-25

    Since the discovery of spin torque in 1996, independently by Berger and Slonczewski, and given its potential impact on information storage and communication technologies, (e.g. through the possibility of switching the magnetic configuration of a bit by current instead of a magnetic field, or the realization of high frequency spin torque oscillators (STO)), this effect has been an important field of spintronics research. One aspect of this research focuses on ferromagnets with low damping. The lower the damping in a ferromagnet, the lower the critical current that is needed to induce switching of a spin valve or induce precession of its magnetization. In this thesis ferromagnetic resonance (FMR) studies of NiMnSb layers are presented along with experimental studies on various spin-torque (ST) devices using NiMnSb. NiMnSb, when crystallized in the half-Heusler structure, is a half-metal which is predicted to have 100% spin polarization, a consideration which further increases its potential as a candidate for memory devices based on the giant magnetoresistance (GMR) effect. The FMR measurements show an outstandingly low damping factor for NiMnSb, in low 10{sup -3} range. This is about a factor of two lower than permalloy and well comparable to lowest damping for iron grown by molecular beam epitaxy (MBE). According to theory the 100% spin polarization properties of the bulk disappear at interfaces where the break in translational symmetry causes the gap in the minority spin band to collapse but can remain in other crystal symmetries such as (111). Consequently NiMnSb layers on (111)(In,Ga)As buffer are characterized in respect of anisotropies and damping. The FMR measurements on these samples indicates a higher damping that for the 001 samples, and a thickness dependent uniaxial in-plane anisotropy. Investigations of the material for device use is pursued by considering sub-micrometer sized elements of NiMnSb on 001 substrates, which were fabricated by electron

  19. Comparative study on structure, corrosion properties and tribological behavior of pure Zn and different Zn-Ni alloy coatings

    Energy Technology Data Exchange (ETDEWEB)

    Tafreshi, M. [Department of Metallurgy and Materials Engineering, South Tehran Branch, Islamic Azad University, Tehran (Iran, Islamic Republic of); Allahkaram, S.R., E-mail: akaram@ut.ac.ir [School of Metallurgy and Materials Engineering, College of Engineering, University of Tehran, P.O.Box: 11155-4563, Tehran (Iran, Islamic Republic of); Farhangi, H. [School of Metallurgy and Materials Engineering, College of Engineering, University of Tehran, P.O.Box: 11155-4563, Tehran (Iran, Islamic Republic of)

    2016-11-01

    Zn and Zn-Ni alloy coatings were electrodeposited from sulfate based electrolytes. The effect of alloys Ni content on morphology, microstructure, corrosion properties, microhardness and tribological behavior of these coatings were investigated and the results were compared with Zn film. According to X-ray diffraction patterns, different intermediate phases (η-Ni{sub 3}Zn{sub 22}, γ-Ni{sub 5}Zn{sub 21}, β-Zn-Ni) were formed by increasing the coatings Ni content from 11 to 17 wt%. Polarization and EIS results revealed that all the alloy coatings had better corrosion resistance than the Zn film. Zn-14 wt%Ni coating had the least corrosion current density and maximum polarization resistance between all the samples. Microhardness of the coatings was improved by increasing their Ni percentage to 17%. However, Zn-14 wt%Ni coating had the lowest wear loss and friction coefficient, while Zn film had the worst wear resistance between all the coatings. - Highlights: • Effect of Ni alloying element on morphology and structure of Zn electrodeposits. • Comparing corrosion behavior of Zn and Zn-Ni coatings. • Influence of Ni content on hardness of Zn-Ni films. • A comparison of tribological behavior of Zn and different Zn-Ni electrodeposits.

  20. Effect of Ni doping on structural and optical properties of Zn{sub 1−x}Ni{sub x}O nanopowder synthesized via low cost sono-chemical method

    Energy Technology Data Exchange (ETDEWEB)

    Singh, Budhendra, E-mail: bksingh@ua.pt [TEMA-NRD, Mechanical Engineering Department, Aveiro Institute of Nanotechnology (AIN), University of Aveiro, 3810-193 Aveiro (Portugal); Kaushal, Ajay, E-mail: ajay.kaushal@ua.pt [Department of Ceramic and Glass Engineering, CICECO, University of Aveiro, 3810-193 Aveiro (Portugal); Bdikin, Igor [TEMA-NRD, Mechanical Engineering Department, Aveiro Institute of Nanotechnology (AIN), University of Aveiro, 3810-193 Aveiro (Portugal); Venkata Saravanan, K. [Department of Physics, School of Basic and Applied Sciences, Central University of Tamil Nadu, Thiruvarur 610101 (India); Ferreira, J.M.F. [Department of Ceramic and Glass Engineering, CICECO, University of Aveiro, 3810-193 Aveiro (Portugal)

    2015-10-15

    Highlights: • Pure and Ni doped ZnO nanopowders were synthesized by low cost sonochemical method. • The optical properties of Zn{sub 1−x}Ni{sub x}O nanopowders can be tuned by varying Ni content. • The results reveal the solubility limit of Ni into ZnO matrix as below 8%. - Abstract: Zn{sub 1−x}Ni{sub x}O nanopowders with different Ni contents of x = 0.0, 0.04 and 0.08 were synthesized via cost effective sonochemical reaction method. X-ray diffraction (XRD) pattern reveals pure wurtzite phase of prepared nanostructures with no additional impurity peaks. The morphology and dimensions of nanoparticles were investigated using scanning electron microscope (SEM). A sharp and strong peak for first order optical mode for wurtzite zinc oxide (ZnO) structure was observed at ∼438 cm{sup −1} in Raman spectra. The calculated optical band gap (E{sub g}) from UV–vis transmission data was found to decrease with increase in Ni content. The observed red shift in E{sub g} with increasing Ni content in ZnO nanopowders were in agreement with band gap behaviours found in their photoluminescence (PL) spectra. The synthesised ZnO nanopowders with controlled band gap on Ni doping reveals their potential for use in various electronic and optical device applications. The results were discussed in detail.

  1. Laboratory Investigations of Ni-Al Coatings Exposed to Conditions Simulating Biomass Firing

    DEFF Research Database (Denmark)

    Wu, Duoli; Okoro, Sunday Chukwudi; Dahl, Kristian Vinter

    2016-01-01

    Fireside corrosion is a key problem when using biomass fuels in power plants. A possible solution is to apply corrosion resistant coatings. The present paper studies the corrosion and interdiffusion behaviour of a Ni-Al diffusion coating on austenitic stainless steel (TP347H). Ni-Al coatings were...... prepared by electrolytic deposition of nickel followed by pack aluminizing performed at 650˚C. A uniform and dense Ni-Al coating with an outer layer of Ni2Al3 and an inner Ni layer was formed. Samples were exposed to 560°C for 168h in an atmosphere simulating biomass combustion. This resulted in localized...... corrosion attack. Interdiffusion was studied by isothermal heat treatment in static air at 650˚C or 700˚C for up to 3000h. The Ni2Al3 gradually transformed into NiAl and Ni3Al during the interdiffusion process. Porosity developed at the interface between the Ni-Al coating and the Ni layer and expanded...

  2. Vacancies supersaturation induced by fast neutron irradiation in FeNi alloys

    International Nuclear Information System (INIS)

    Lucki, G.; Chambron, W.; Watanabe, S.; Verdone, J.

    1975-01-01

    The void formation in metals and alloys during irradiation with high-energy particles is a problem of interest in physics and of paramount importance in nuclear technology. Voids are formed as a consequence of vacancy supersaturation and result in swelling as well as in changes of mechanical, electrical and magnetic properties of materials used in power reactors. Isothermal annealings were performed between 400 and 500 0 C with and without fast-neutron (1 MeV) irradiation. Pure Fe--Ni (50--50 at. percent) was irradiated in the Melousine reactor in Grenoble, and Fe--Ni(Mo) (50--50 at. percent + 50 ppM), in the IEAR-1 reactor at the Instituto de Energia Atomica in Sao Paulo. The toroidal-shaped specimens were fabricated from Johnson Mathey zone-refined ingots, and were initially annealed at 800 0 C during 1 h in hydrogen atmosphere and then slowly cooled (4 h) inside the furnace. Magnetic After Effect measurements (MAE) permitted the evaluation of activation energies during fast-neutron irradiation (1.54 eV) and without irradiation (3.14 eV) for pure Fe--Ni and respectively (1.36 eV) and (2.32 eV) for Fe--Ni(Mo). Since the time constants of the relaxation process are inversely proportional to the vacancy concentration, a quantitative evaluation of vacancy supersaturation was made; it decreases from the value 700 at 410 0 C to the value 40 at 490 0 C for pure Fe--Ni and from 765 to 121 for Fe--Ni(Mo) in the same temperature range. 3 figures, 5 tables

  3. Bimetallic Nickel/Ruthenium Catalysts Synthesized by Atomic Layer Deposition for Low-Temperature Direct Methanol Solid Oxide Fuel Cells.

    Science.gov (United States)

    Jeong, Heonjae; Kim, Jun Woo; Park, Joonsuk; An, Jihwan; Lee, Tonghun; Prinz, Fritz B; Shim, Joon Hyung

    2016-11-09

    Nickel and ruthenium bimetallic catalysts were heterogeneously synthesized via atomic layer deposition (ALD) for use as the anode of direct methanol solid oxide fuel cells (DMSOFCs) operating in a low-temperature range. The presence of highly dispersed ALD Ru islands over a porous Ni mesh was confirmed, and the Ni/ALD Ru anode microstructure was observed. Fuel cell tests were conducted using Ni-only and Ni/ALD Ru anodes with approximately 350 μm thick gadolinium-doped ceria electrolytes and platinum cathodes. The performance of fuel cells was assessed using pure methanol at operating temperatures of 300-400 °C. Micromorphological changes of the anode after cell operation were investigated, and the content of adsorbed carbon on the anode side of the operated samples was measured. The difference in the maximum power density between samples utilizing Ni/ALD Ru and Pt/ALD Ru, the latter being the best catalyst for direct methanol fuel cells, was observed to be less than 7% at 300 °C and 30% at 350 °C. The improved electrochemical activity of the Ni/ALD Ru anode compared to that of the Ni-only anode, along with the reduction of the number of catalytically active sites due to agglomeration of Ni and carbon formation on the Ni surface as compared to Pt, explains this decent performance.

  4. Resistance to sulfur poisoning of Ni-based alloy with coinage (IB) metals

    International Nuclear Information System (INIS)

    Xu, Xiaopei; Zhang, Yanxing; Yang, Zongxian

    2015-01-01

    Highlights: • The effects of IB metal dopants on the S poisoning features of Ni are analyzed. • IB metal dopants can modify the surface electronic structure of Ni. • IB metal dopants can increase the S tolerance of Ni at an optimized concentration. • Au is a preferred dopant to increase the resistance to sulfur poisoning of Ni. - Abstract: The poisoning effects of S atom on the (1 0 0), (1 1 0) and (1 1 1) metal surfaces of pure Ni and Ni-based alloy with IB (coinage) metals (Cu, Ag, Au) are systematically studied. The effects of IB metal dopants on the S poisoning features are analyzed combining the density functional theory (DFT) results with thermodynamics data using the ab initio atomistic thermodynamic method. It is found that introducing IB doping metals into Ni surface can shift the d-band center downward from the Fermi level and weaken the adsorption of S on the (1 0 0) and (1 1 0) surfaces, and the S tolerance ability increases in the order of Ni, Cu/Ni, Ag/Ni and Au/Ni. Nevertheless, on the (1 1 1) surface, the S tolerance ability increases in the order of Ag/Ni (or Cu/Ni), Ni, and Au/Ni. When we increase the coverage of the IB metal dopants, we found that not only Au, but Cu and Ag can increase its S tolerance. We therefore propose that alloying can increase its S tolerance and alloying with Au would be a better way to increase the resistance to sulfur poisoning of the Ni anode as compared with the pure Ni and the Ag- or, Cu-doped Ni materials.

  5. Electroless Ni-B plating on SiO2 with 3-aminopropyl-triethoxysilane as a barrier layer against Cu diffusion for through-Si via interconnections in a 3-dimensional multi-chip package

    International Nuclear Information System (INIS)

    Ikeda, Akihiro; Sakamoto, Atsushi; Hattori, Reiji; Kuroki, Yukinori

    2009-01-01

    Electroless Ni-B was plated on SiO 2 as a barrier layer against Cu diffusion for through-Si via (TSV) interconnections in a 3-dimensional multi-chip package. The electroless Ni-B was deposited on the entire area of the SiO 2 side wall of a deep via with vapor phase pre-deposition of 3-aminopropyl-triethoxysilane on the SiO 2 . The carrier lifetimes in the Si substrates plated with Ni-B/Cu did not decrease with an increase in annealing temperature up to 400 deg. C . The absence of degradation of carrier lifetimes indicates that Cu atoms did not diffuse into the Si through the Ni-B. The advantages of electroless Ni-B (good conformal deposition and forming an effective diffusion barrier against Cu) make it useful as a barrier layer for TSV interconnections in a 3-dimensional multi-chip package

  6. Isotopically pure single crystal epitaxial diamond films and their preparation

    International Nuclear Information System (INIS)

    Banholzer, W.F.; Anthony, T.R.; Williams, D.M.

    1992-01-01

    The present invention is directed to the production of single crystal diamond consisting of isotopically pure carbon-12 or carbon-13. In the present invention, isotopically pure single crystal diamond is grown on a single crystal substrate directly from isotopically pure carbon-12 or carbon-13. One method for forming isotopically pure single crystal diamond comprises the steps of placing in a reaction chamber a single substrate heated to an elevated diamond forming temperature. Another method for forming isotopically pure single crystal diamond comprises diffusing isotopically pure carbon-12 or carbon-13 through a metallic catalyst under high pressure to a region containing a single crystal substrate to form an isotopically pure single crystal diamond layer on said single crystal substrate

  7. An overview of NiTi shape memory alloy: Corrosion resistance and antibacterial inhibition for dental application

    Energy Technology Data Exchange (ETDEWEB)

    Fadlallah, Sahar A., E-mail: sahar.fadlallah@yahoo.com [Materials and Corrosion Lab. (MCL), Faculty of Science, Taif University, Taif (Saudi Arabia); Chemistry Department, Faculty of Science, Cairo University, Cairo (Egypt); El-Bagoury, Nader [Materials and Corrosion Lab. (MCL), Faculty of Science, Taif University, Taif (Saudi Arabia); Casting Technology Lab., Manufacturing Technology Dept., CMRDI, P.O. Box 87, Helwan, Cairo (Egypt); Gad El-Rab, Sanaa M.F. [Biotechnology Department, Faculty of Science, Taif University, Taif (Saudi Arabia); Botany Department, Faculty of Science, Asuit University, Asuit (Egypt); Ahmed, Rasha A. [Materials and Corrosion Lab. (MCL), Faculty of Science, Taif University, Taif (Saudi Arabia); Forensic Chemistry Laboratories, Medico Legal Department, Ministry of Justice, Cairo (Egypt); El-Ousamii, Ghaida [Materials and Corrosion Lab. (MCL), Faculty of Science, Taif University, Taif (Saudi Arabia)

    2014-01-15

    Highlights: • Evaluate the corrosion resistance of NiTi alloy by using electrochemical techniques. • Estimate the Antibacterial inhibition rate of NiTi alloy. • Assessment the mechanical properties of NiTi from the hardness measurements. • Comparsion the microstructures of cast NiTi with Ti, this indicate the role of Ni to change the behavior of alloy in oral environment. • Advise drinking green tea in small quantities in small quantities in the event of present NiTi alloy in the oral cavity. • Recommendation to use NiTi for dental application. -- Abstract: Nowadays, Nickel–titanium nearly equiatomic is considered as one of the best biomaterials. The aim of the present work deals with the evolution of the electrochemical behavior of NiTi in simulated oral environment. The hardness, microstructures corrosion resistance and antibacterial performance of NiTi alloy were compared with pure titanium. The hardness of NiTi is twice the hardness of pure titanium. Electrochemical techniques were used to detect the corrosion resistance of both biomaterials in Hank’s solution containing (−)-epigallocatechin gallate (EGCG) which used to simulate the oral environment. In the physiological solution selected for the present study, the impedance spectroscopy (EIS) results showed that EGCG sharply increase the corrosion resistance of NiTi from 129 kΩ cm{sup 2} to 1.10 T Ω cm{sup 2} while slowly increase the corrosion resistance of pure titanium from 9.4 kΩ cm{sup 2} to 11.3 kΩ cm{sup 2} during the duration time of immersion at 37 °C. The plate-counting method was used to evaluate the antibacterial performance against Staphylococcus aureus (ATCC 6538). Among the two specimens of biomaterials studied, the antibacterial performance results revealed that the NiTi alloy is better than the pure titanium. The morphology and chemical structure of NiTi and Ti samples were systematically investigated by scanning electron microscope (SEM) and energy dispersive X

  8. An overview of NiTi shape memory alloy: Corrosion resistance and antibacterial inhibition for dental application

    International Nuclear Information System (INIS)

    Fadlallah, Sahar A.; El-Bagoury, Nader; Gad El-Rab, Sanaa M.F.; Ahmed, Rasha A.; El-Ousamii, Ghaida

    2014-01-01

    Highlights: • Evaluate the corrosion resistance of NiTi alloy by using electrochemical techniques. • Estimate the Antibacterial inhibition rate of NiTi alloy. • Assessment the mechanical properties of NiTi from the hardness measurements. • Comparsion the microstructures of cast NiTi with Ti, this indicate the role of Ni to change the behavior of alloy in oral environment. • Advise drinking green tea in small quantities in small quantities in the event of present NiTi alloy in the oral cavity. • Recommendation to use NiTi for dental application. -- Abstract: Nowadays, Nickel–titanium nearly equiatomic is considered as one of the best biomaterials. The aim of the present work deals with the evolution of the electrochemical behavior of NiTi in simulated oral environment. The hardness, microstructures corrosion resistance and antibacterial performance of NiTi alloy were compared with pure titanium. The hardness of NiTi is twice the hardness of pure titanium. Electrochemical techniques were used to detect the corrosion resistance of both biomaterials in Hank’s solution containing (−)-epigallocatechin gallate (EGCG) which used to simulate the oral environment. In the physiological solution selected for the present study, the impedance spectroscopy (EIS) results showed that EGCG sharply increase the corrosion resistance of NiTi from 129 kΩ cm 2 to 1.10 T Ω cm 2 while slowly increase the corrosion resistance of pure titanium from 9.4 kΩ cm 2 to 11.3 kΩ cm 2 during the duration time of immersion at 37 °C. The plate-counting method was used to evaluate the antibacterial performance against Staphylococcus aureus (ATCC 6538). Among the two specimens of biomaterials studied, the antibacterial performance results revealed that the NiTi alloy is better than the pure titanium. The morphology and chemical structure of NiTi and Ti samples were systematically investigated by scanning electron microscope (SEM) and energy dispersive X-ray analysis (EDX). The

  9. Corrosion behaviour of Ni in aprotic solvents an electrochemical, XPS and AFM study

    International Nuclear Information System (INIS)

    Bellucci, F.; Monetta, T.; Capobianco, G.; Deganello, A.; Glisenti, A.; Moretti, G.

    1998-01-01

    Electrochemical and X-ray photoelectron spectroscopic (XPS) techniques have been used to study the passivation of nickel in 0.1 M H 2 SO 4 DMF and ACN solutions with different water content. Electrochemical results indicate the anodic formation of a thin, poor protective layer and the possibility of salt precipitation onto the metallic surface. ARXPS results indicate that while in the anodic film formed in DMF, Ni(OH) 2 constitute the superficial component under which a discontinuous layer of NiO and NiSO 4 is present. Ni(OH) 2 and NiSO 4 are the more superficial constituents in the passivation layer formed in ACN, while NiO becomes prevalent in the underlying layers. AFM images show that in both the solvents the sample surface is very dishomogeneous with flakes and fractures. (orig.)

  10. Hydrothermal Synthesis and Structural Characterization of NiO/SnO2 Composites and Hydrogen Sensing Properties

    Directory of Open Access Journals (Sweden)

    Chao Wei

    2015-01-01

    Full Text Available Pure SnO2 and NiO doped SnO2 nanostructures were successfully synthesized via a simple and environment-friendly hydrothermal method. X-ray powder diffraction (XRD, scanning electron microscopy (SEM, energy dispersive X-ray spectroscopy (EDS, and X-ray photoelectron spectra (XPS were used to investigate the crystalline structures, surface morphologies and microstructures, and element components and their valences of the as-synthesized samples. Furthermore, planar chemical gas sensors based on the synthesized pure SnO2 and NiO/SnO2 composites were fabricated and their sensing performances to hydrogen, an important fault characteristic gas dissolved in power transformer oil, were investigated in detail. Gas sensing experiments indicate that the NiO/SnO2 composites showed much higher gas response and lower working temperature than those of pure SnO2, which could be ascribed to the formation of p-n heterojunctions between p-type NiO and n-type SnO2. These results demonstrate that the as-synthesized NiO/SnO2 composites a promising hydrogen sensing material.

  11. Magnetoimpedance of FeNi-based asymmetric sensitive elements

    International Nuclear Information System (INIS)

    Chlenova, A.A.; Svalov, A.V.; Kurlyandskaya, G.V.; Volchkov, S.O.

    2016-01-01

    [Ti/FeNi] 5 /Ti/Cu/Ti/[FeNi/Ti] x (x=0–5) multilayers were prepared by sputtering. Their magnetic properties and magnetoimpedance were studied focusing on future technological applications. Both (ΔZ/Z) max and (ΔR/R) max values showed a tendency to decrease with a decrease of the number of magnetic layers of the top multilayer. Such a parameter as an even or odd number of layers is important for the MI value. In the field interval of technological interest all [Ti/FeNi] 5 /Ti/Cu/Ti/[FeNi/Ti] x structures show similar sensitivities of about 70%/Oe for ΔR/R ratios but the lower the number of magnetic layers in the top multilayer, the higher the operating frequency. - Highlights: • Giant magnetoimpedance effect. • Non-symmetric multilayers sructure. • Biosensing.

  12. Synthesis and characterization of n-type NiO:Al thin films for fabrication of p-n NiO homojunctions

    Science.gov (United States)

    Sun, Hui; Liao, Ming-Han; Chen, Sheng-Chi; Li, Zhi-Yue; Lin, Po-Chun; Song, Shu-Mei

    2018-03-01

    n-type NiO:Al thin films were deposited by RF magnetron sputtering. Their optoelectronic properties versus Al target power was investigated. The results show that with increasing Al target power, the conduction type of NiO films changes from p-type to n-type. The variation of the film’s electrical and optical properties depends on Al amount in the film. When Al target power is relatively low, Al3+ cations tend to enter nickel vacancy sites, which makes the lattice structure of NiO more complete. This improves the carrier mobility and film’s transmittance. However, when Al target power exceeds 40 W, Al atoms begin to enter into interstitial sites and form an Al cluster in the NiO film. This behavior is beneficial for improving the film’s n-type conductivity but degrades the film’s transmittance. Finally, Al/(p-type NiO)/(n-type NiO:Al)/ITO homojunctions were fabricated. Their performance was compared with Al/(p-type NiO)/ITO heterojunctions without an n-type NiO layer. Thanks to the better interface quality between the two NiO layers, the homojunctions present better performance.

  13. Influence of a deep-level-defect band formed in a heavily Mg-doped GaN contact layer on the Ni/Au contact to p-GaN

    International Nuclear Information System (INIS)

    Li Xiao-Jing; Zhao De-Gang; Jiang De-Sheng; Chen Ping; Zhu Jian-Jun; Liu Zong-Shun; Yang Jing; He Xiao-Guang; Yang Hui; Zhang Li-Qun; Zhang Shu-Ming; Le Ling-Cong; Liu Jian-Ping

    2015-01-01

    The influence of a deep-level-defect (DLD) band formed in a heavily Mg-doped GaN contact layer on the performance of Ni/Au contact to p-GaN is investigated. The thin heavily Mg-doped GaN (p ++ -GaN) contact layer with DLD band can effectively improve the performance of Ni/Au ohmic contact to p-GaN. The temperature-dependent I–V measurement shows that the variable-range hopping (VRH) transportation through the DLD band plays a dominant role in the ohmic contact. The thickness and Mg/Ga flow ratio of p ++ -GaN contact layer have a significant effect on ohmic contact by controlling the Mg impurity doping and the formation of a proper DLD band. When the thickness of the p ++ -GaN contact layer is 25 nm thick and the Mg/Ga flow rate ratio is 10.29%, an ohmic contact with low specific contact resistivity of 6.97× 10 −4 Ω·cm 2 is achieved. (paper)

  14. Mechanical intermixing of components in (CoMoNi)-based systems and the formation of (CoMoNi)/WC nanocomposite layers on Ti sheets under ball collisions

    Science.gov (United States)

    Romankov, S.; Park, Y. C.; Shchetinin, I. V.

    2017-11-01

    Cobalt (Co), molybdenum (Mo), and nickel (Ni) components were simultaneously introduced onto titanium (Ti) surfaces from a composed target using ball collisions. Tungsten carbide (WC) balls were selected for processing as the source of a cemented carbide reinforcement phase. During processing, ball collisions continuously introduced components from the target and the grinding media onto the Ti surface and induced mechanical intermixing of the elements, resulting in formation of a complex nanocomposite structure onto the Ti surface. The as-fabricated microstructure consisted of uniformly dispersed WC particles embedded within an integrated metallic matrix composed of an amorphous phase with nanocrystalline grains. The phase composition of the alloyed layers, atomic reactions, and the matrix grain sizes depended on the combination of components introduced onto the Ti surface during milling. The as-fabricated layer exhibited a very high hardness compared to industrial metallic alloys and tool steel materials. This approach could be used for the manufacture of both cemented carbides and amorphous matrix composite layers.

  15. Effect of zirconium on grain growth and mechanical properties of a ball-milled nanocrystalline FeNi alloy

    Energy Technology Data Exchange (ETDEWEB)

    Kotan, Hasan, E-mail: hkotan@ncsu.edu [Department of Materials Science and Engineering, NC State University, 911 Partners Way, Room 3078, Raleigh, NC 27606-7907 (United States); Darling, Kris A. [U.S. Army Research Laboratory, Weapons and Materials Research Directorate, RDRL-WMM-F, Aberdeen Proving Ground, MD 21005-5069 (United States); Saber, Mostafa; Koch, Carl C.; Scattergood, Ronald O. [Department of Materials Science and Engineering, NC State University, 911 Partners Way, Room 3078, Raleigh, NC 27606-7907 (United States)

    2013-02-25

    Highlights: Black-Right-Pointing-Pointer Pure Fe, Fe{sub 92}Ni{sub 8}, and Fe{sub 91}Ni{sub 8}Zr{sub 1} powders were hardened up to 10 GPa by ball milling. Black-Right-Pointing-Pointer Annealing of Fe and Fe{sub 92}Ni{sub 8} leads to reduced hardness and extensive grain growth. Black-Right-Pointing-Pointer The addition of Zr to Fe{sub 92}Ni{sub 8} increases its stability and strength by second phases. Black-Right-Pointing-Pointer The second phases are found to promote the stability of Fe{sub 91}Ni{sub 8}Zr{sub 1} by Zener pinning. Black-Right-Pointing-Pointer The Zr-containing precipitates contribute to the overall strength of the material. - Abstract: Grain growth of ball-milled pure Fe, Fe{sub 92}Ni{sub 8}, and Fe{sub 91}Ni{sub 8}Zr{sub 1} alloys has been studied using X-ray diffractometry (XRD), focused ion beam (FIB) microscopy and transmission electron microscopy (TEM). Mechanical properties with respect to compositional changes and annealing temperatures have been investigated using microhardness and shear punch tests. We found the rate of grain growth of the Fe{sub 91}Ni{sub 8}Zr{sub 1} alloy to be much less than that of pure Fe and the Fe{sub 92}Ni{sub 8} alloy at elevated temperatures. The microstructure of the ternary Fe{sub 91}Ni{sub 8}Zr{sub 1} alloy remains nanoscale up to 700 Degree-Sign C where only a few grains grow abnormally whereas annealing of pure iron and the Fe{sub 92}Ni{sub 8} alloy leads to extensive grain growth. The grain growth of the ternary alloy at high annealing temperatures is coupled with precipitation of Fe{sub 2}Zr. A fine dispersion of precipitated second phase is found to promote the microstructural stability at high annealing temperatures and to increase the hardness and ultimate shear strength of ternary Fe{sub 91}Ni{sub 8}Zr{sub 1} alloy drastically when the grain size is above nanoscale.

  16. Microstructure and property of directionally solidified Ni-Si hypereutectic alloy

    Science.gov (United States)

    Cui, Chunjuan; Tian, Lulu; Zhang, Jun; Yu, Shengnan; Liu, Lin; Fu, Hengzhi

    2016-03-01

    This paper investigates the influence of the solidification rate on the microstructure, solid/liquid interface, and micro-hardness of the directionally solidified Ni-Si hypereutectic alloy. Microstructure of the Ni-Si hypereutectic alloy is refined with the increase of the solidification rate. The Ni-Si hypereutectic composite is mainly composed of α-Ni matrix, Ni-Ni3Si eutectic phase, and metastable Ni31Si12 phase. The solid/liquid interface always keeps planar interface no matter how high the solidification rate is increased. This is proved by the calculation in terms of M-S interface stability criterion. Moreover, the Ni-Si hypereutectic composites present higher micro-hardness as compared with that of the pure Ni3Si compound. This is caused by the formation of the metastable Ni31Si12 phase and NiSi phase during the directional solidification process.

  17. Structural and thermal stabilities of layered Li(Ni 1/3Co 1/3Mn 1/3)O 2 materials in 18650 high power batteries

    Science.gov (United States)

    He, Yan-Bing; Ning, Feng; Yang, Quan-Hong; Song, Quan-Sheng; Li, Baohua; Su, Fangyuan; Du, Hongda; Tang, Zhi-Yuan; Kang, Feiyu

    The structural and thermal stabilities of the layered Li(Ni 1/3Co 1/3Mn 1/3)O 2 cathode materials under high rate cycling and abusive conditions are investigated using the commercial 18650 Li(Ni 1/3Co 1/3Mn 1/3)O 2/graphite high power batteries. The Li(Ni 1/3Co 1/3Mn 1/3)O 2 materials maintain their layered structure even when the power batteries are subjected to 200 cycles with 10 C discharge rate at temperatures of 25 and 50 °C, whereas their microstructure undergoes obvious distortion, which leads to the relatively poor cycling performance of power batteries at high charge/discharge rates and working temperature. Under abusive conditions, the increase in the battery temperature during overcharge is attributed to both the reactions of electrolyte solvents with overcharged graphite anode and Li(Ni 1/3Co 1/3Mn 1/3)O 2 cathode and the Joule heat that results from the great increase in the total resistance (R cell) of batteries. The reactions of fully charged Li(Ni 1/3Co 1/3Mn 1/3)O 2 cathodes and graphite anodes with electrolyte cannot be activated during short current test in the fully charged batteries. However, these reactions occur at around 140 °C in the fully charged batteries during oven test, which is much lower than the temperature of about 240 °C required for the reactions outside batteries.

  18. Thermal stability of Ni-Pt-Ta alloy silicides on epi-Si{sub 1-x}C{sub x}

    Energy Technology Data Exchange (ETDEWEB)

    Yoo, Jung-Ho; Chang, Hyun-Jin [Department of Ceramic Engineering, Yonsei University, Seoul 120-749 (Korea, Republic of); Min, Byoung-Gi [Department of Ceramic Engineering, Yonsei University, Seoul 120-749 (Korea, Republic of); Jusung Engineering Co., Ltd., 49, Neungpyeong-ri, Opo-eup, Gwangju-Si, Kyunggi-do 464-892 (Korea, Republic of); Ko, Dae-Hong [Department of Ceramic Engineering, Yonsei University, Seoul 120-749 (Korea, Republic of)], E-mail: dhko@yonsei.ac.kr; Cho, Mann-Ho [Institute of Physics and Applied Physics, Yonsei University, Seoul 120-749 (Korea, Republic of); Sohn, Hyunchul [Department of Ceramic Engineering, Yonsei University, Seoul 120-749 (Korea, Republic of); Lee, Tae-Wan [Jusung Engineering Co., Ltd., 49, Neungpyeong-ri, Opo-eup, Gwangju-Si, Kyunggi-do 464-892 (Korea, Republic of)

    2008-12-05

    We investigated the silicide formation in Ni/epi-Si{sub 1-x}C{sub x} systems. Ni-Pt and Ni-Pt-Ta films were deposited on epi-Si{sub 1-x}C{sub x}/Si substrates by DC magnetron sputtering and processed at various temperatures. The sheet resistance of the silicide from the Ni alloy/epi-Si{sub 1-x}C{sub x} systems was maintained at low values compared to that from Ni/Si systems. By TEM and EDS analyses, we confirmed the presence of a Pt alloy layer at the top of the Ni-silicide layer. The stability of the silicide layer in the Ni alloy/epi-Si{sub 1-x}C{sub x} system is explained by not only the Pt rich layer on the top of the Ni-silicide layer, but also by the presence of a small amount of Pt in the Ni-silicide layer or at the grain boundaries. And both the thermal stability and the morphology of silicide were greatly improved by the addition of Ta in Ni-Pt films.

  19. Pure spin current manipulation in antiferromagnetically exchange coupled heterostructures

    Science.gov (United States)

    Avilés-Félix, L.; Butera, A.; González-Chávez, D. E.; Sommer, R. L.; Gómez, J. E.

    2018-03-01

    We present a model to describe the spin currents generated by ferromagnet/spacer/ferromagnet exchange coupled trilayer systems and heavy metal layers with strong spin-orbit coupling. By exploiting the magnitude of the exchange coupling (oscillatory RKKY-like coupling) and the spin-flop transition in the magnetization process, it has been possible to produce spin currents polarized in arbitrary directions. The spin-flop transition of the trilayer system originates pure spin currents whose polarization vector depends on the exchange field and the magnetization equilibrium angles. We also discuss a protocol to control the polarization sign of the pure spin current injected into the metallic layer by changing the initial conditions of magnetization of the ferromagnetic layers previously to the spin pumping and inverse spin Hall effect experiments. The small differences in the ferromagnetic layers lead to a change in the magnetization vector rotation that permits the control of the sign of the induced voltage components due to the inverse spin Hall effect. Our results can lead to important advances in hybrid spintronic devices with new functionalities, particularly, the ability to control microscopic parameters such as the polarization direction and the sign of the pure spin current through the variation of macroscopic parameters, such as the external magnetic field or the thickness of the spacer in antiferromagnetic exchange coupled systems.

  20. Magnetic studies in evaporated Ni/Pd multilayers

    International Nuclear Information System (INIS)

    Chafai, K.; Salhi, H.; Lassri, H.; Yamkane, Z.; Lassri, M.; Abid, M.; Hlil, E.K.; Krishnan, R.

    2011-01-01

    The magnetic properties of Ni/Pd multilayers, prepared by sequential evaporation in ultrahigh vacuum, have been studied. The Ni thickness dependence of the magnetization and magnetic anisotropy is discussed. The temperature dependence of the spontaneous magnetization is well described by a T 3/2 law in all multilayers. A spin-wave theory has been used to explain the temperature dependence of the spontaneous magnetization, and the approximate values for the exchange interactions for various Ni layer thicknesses have been obtained. - Research highlights: → The magnetic properties of Ni/Pd multilayers, prepared by sequential evaporation in ultrahigh vacuum, have been studied. → The temperature dependence of the spontaneous magnetization is well described by a T 3/2 law in Ni/Pd multilayers. → The spin-wave constant B was observed to depend on t Ni nonmonotonically. → A spin-wave theory has been used to explain the temperature dependence of the spontaneous magnetization. → The approximate values for the exchange interactions for various Ni layer thicknesses have been obtained.

  1. Microstructural evolution of neutron-irradiated Ni-Si and Ni-Al alloys

    Science.gov (United States)

    Takahashi, H.; Garner, F. A.

    1992-10-01

    Additions of silicon and aluminum suppress the neutron-induced swelling of pure nickel but to different degrees. Silicon is much more effective initially when compared to aluminum on a per atom basis but silicon exhibits a nonmonotonic influence on swelling with increasing concentration. Silicon tends to segregate toward grain boundaries while aluminum segregates away from these boundaries. Whereas the formation of the Ni 3Si phase is frequently observed in charged particle irradiation experiments conducted at much higher displacement rates, it did not occur during neutron irradiation in this study. Precipitation also did not occur in Ni-5Al during neutron irradiation, nor has it been reported to occur during ion irradiation.

  2. Microstructural evolution of neutron-irradiated Ni-Si and Ni-Al alloys

    International Nuclear Information System (INIS)

    Takahashi, H.; Garner, F.A.

    1992-01-01

    Additions of silicon and aluminium suppress the neutron-induced swelling of pure nickel but to different degrees. Silicon is much more effective initially when compared to aluminium on a per atom basis but silicon exhibits a nonmonotonic influence on swelling with increasing concentration. Silicon tends to segregate toward grain boundaries while aluminium segregates away from these boundaries. Whereas the formation of the Ni 3 Si phase is frequently observed in charged particle irradiation experiments conducted at much higher displacement rates, it did not occur during neutron irradiation in this study. Precipitation also did not occur in Ni-5Al during neutron irradiation, nor has it been reported to occur during ion irradiation. (orig.)

  3. Characterization of Al/Ni multilayers and their application in diffusion bonding of TiAl to TiC cermet

    International Nuclear Information System (INIS)

    Cao, J.; Song, X.G.; Wu, L.Z.; Qi, J.L.; Feng, J.C.

    2012-01-01

    The Al/Ni multilayers were characterized and diffusion bonding of TiAl intermetallics to TiC cermets was carried out using the multilayers. The microstructure of Al/Ni multilayers and TiAl/TiC cermet joint was investigated. The layered structures consisting of a Ni 3 (AlTi) layer, a Ni 2 AlTi layer, a (Ni,Al,Ti) layer and a Ni diffusion layer were observed from the interlayer to the TiAl substrate. Only one AlNi 3 layer formed at the multilayer/TiC cermet interface. The reaction behaviour of Al/Ni multilayers was characterized by means of differential scanning calorimeter (DSC) and X-ray diffraction. The initial exothermic peak of the DSC curve was formed due to the formation of Al 3 Ni and Al 3 Ni 2 phases. The reaction sequence of the Al/Ni multilayers was Al 3 Ni → Al 3 Ni 2 → AlNi → AlNi 3 and the final products were AlNi and AlNi 3 phases. The shear strength of the joint was tested and the experimental results suggested that the application of Al/Ni multilayers improved the joining quality. - Highlights: ► Diffusion bonding of TiAl to TiC cermet was realized using Al/Ni multilayer. ► The reaction sequence of the Al/Ni multilayers was Al 3 Ni → Al 3 Ni 2 → AlNi → AlNi 3 . ► The interfacial microstructure of the joint was clarified. ► The application of Al/Ni multilayers improved the joining quality.

  4. Fretting and wear behaviors of Ni/nano-WC composite coatings in dry and wet conditions

    International Nuclear Information System (INIS)

    Benea, Lidia; Başa, Sorin-Bogdan; Dănăilă, Eliza; Caron, Nadège; Raquet, Olivier; Ponthiaux, Pierre; Celis, Jean-Pierre

    2015-01-01

    Highlights: • The friction and wear properties of Ni/nano-WC composite were studied. • Nano-WC reinforcement decreased friction coefficient in dry and wet conditions. • Nano-WC reinforcement fraction was seen to be 12 wt.%. • Nanohardness increased by 27% compared to nickel without WC reinforcements. • Ennoblement of OCP corresponding to the Ni/nano-WC composite coating. - Abstract: The fretting and wear behaviors of Ni/nano-WC composite coatings were studied by considering the effect of fretting frequency of 1 Hz during 10,000 cycles, at different applied loads in dry or wet conditions. The studies were performed on a ball-on-disk tribometer and the results were compared with pure Ni coating. The nanohardness of pure Ni and Ni/nano-WC composite coatings was tested by nanoindentation technique. To evaluate the wet wear (tribocorrosion) behavior the open circuit potential (OCP) was measured before, during and after the fretting tests at room temperature in the solution that simulates the primary water circuit of Pressurized Water Reactors (PWRs). The results show that Ni/nano-WC composite coatings exhibited a low friction coefficient, high nanohardness and wear resistance compared with pure Ni coatings under similar experimental conditions. Ni/nano-WC composite coatings were obtained on stainless steel support by electrochemical codeposition of nano-sized WC particles (diameter size of ∼60 nm) with nickel, from a standard nickel Watts plating bath. The surface morphology and the composition of the coatings were characterized by scanning electron microscopy (SEM) and energy dispersive spectroscopy (EDX) respectively

  5. Preparation of layered oxide Li(Co1/3Ni1/3Mn1/3)O2 via the sol-gel process

    Institute of Scientific and Technical Information of China (English)

    ZHANG Wen; LIU Hanxing; HU Chen; ZHU Xianjun; LI Yanxi

    2008-01-01

    To obtain homogenous layered oxide Li(Co1/3Ni1/3Ni1/3Mn1/3)O2 as a lithium insertion positive electrode material,the sol-gel process using citric acid as a chelating agent was applied.The material Li(Co1/3,Ni1/3Mn1/3)O2 was synthesized at different calcination temperatures.XRD experiment indicated that the hyered Li(Co1/3Ni1/3Mn1/3)O2material could he synthesized at a lower temperature of 800℃,and the oxidation state of Co,Ni,and Mn in the cathode confirmed by XPS were +3,+2,and +4,respectively.SEM observations showed that the synthesized material could form homogenous particle morphology with the particle size of about 200nm In spite of different calcination temperatures,the charge-discharge curves of all the samples for the initial cycle were similar,and the cathode synthesized at 900℃ showed a small irreversible capacity loss of 11.24% and a high discharge capacity of 212.2 mAh.g-1 in the voltage range of 2.9-4.6 V.

  6. Structural and dielectric studies of LiNiPO4 and LiNi0.5Co0.5PO4 cathode materials for lithium-ion batteries

    Directory of Open Access Journals (Sweden)

    K. Vijaya Babu

    2016-09-01

    Full Text Available Olivine-type LiNiPO4 has been considered as a most competitive positive electrode active material for lithium-ion batteries. In the present paper, the LiNiPO4 and Co-doped LiNi0.5Co0.5PO4 are synthesized by solid-state reaction method under air atmosphere. All the X-ray diffraction peaks of both the compounds are indexed and it is found that the samples are well crystallized in orthorhombic olivine structure belonging to the space group Pnma. The crystallite size is calculated from the Scherrer formula and it is found to be 6.918 and 4.818 nm for pure and doped samples, respectively. The surface morphology and grain sizes of the materials are investigated through scanning electron microscope. Presence of preferred local cation environment is understood from Fourier transform infrared spectroscopy (FTIR studies. The conductivity and dielectric analysis of the samples are carried out at different temperatures and frequencies using the complex impedance spectroscopy technique. The electrical conductivity of LiNi0.5Co0.5PO4 is higher than that of pure LiNiPO4.

  7. High-power pure blue laser diodes

    Energy Technology Data Exchange (ETDEWEB)

    Ohta, M.; Ohizumi, Y.; Hoshina, Y.; Tanaka, T.; Yabuki, Y.; Goto, S.; Ikeda, M. [Development Center, Sony Shiroishi Semiconductor Inc., Miyagi (Japan); Funato, K. [Materials Laboratories, Sony Corporation, Kanagawa (Japan); Tomiya, S. [Materials Analysis Laboratory, Sony Corporation, Kanagawa (Japan)

    2007-06-15

    We successfully developed high-power and long-lived pure blue laser diodes (LDs) having an emission wavelength of 440-450 nm. The pure-blue LDs were grown by metalorganic chemical vapor deposition (MOCVD) on GaN substrates. The dislocation density was successfully reduced to {proportional_to}10{sup 6} cm{sup -2} by optimizing the MOCVD growth conditions and the active layer structure. The vertical layer structure was designed to have an absorption loss of 4.9 cm{sup -1} and an internal quantum efficiency of 91%. We also reduced the operating current density to 6 kA/cm{sup 2} under 750 mW continuous-wave operation at 35 C by optimizing the stripe width to 12 {mu}m and the cavity length to 2000 {mu}m. The half lifetimes in constant current mode are estimated to be longer than 10000 h. (copyright 2007 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim) (orig.)

  8. Hydrothermal synthesis of layered Li[Ni1/3Co1/3Mn1/3]O2 as positive electrode material for lithium secondary battery

    International Nuclear Information System (INIS)

    Myung, Seung-Taek; Lee, Myung-Hun; Komaba, Shinichi; Kumagai, Naoaki; Sun, Yang-Kook

    2005-01-01

    In attempts to prepare layered Li[Ni 1/3 Co 1/3 Mn 1/3 ]O 2 , hydrothermal method was employed. The hydrothermal precursor, [Ni 1/3 Co 1/3 Mn 1/3 ](OH) 2 , was synthesized via a coprecipitation route. The sphere-shaped powder precursor was hydrothermally reacted with LiOH aqueous solution at 170 deg. C for 4 days in autoclave. From X-ray diffraction and scanning electron microscopic studies, it was found that the as-hydrothermally prepared powders were crystallized to layered α-NaFeO 2 structure and the particles had spherical shape. The as-prepared Li[Ni 1/3 Co 1/3 Mn 1/3 ]O 2 delivered an initial discharge of about 110 mA h g -1 due to lower crystallinity. Heat treatment of the hydrothermal product at 800 deg. C was significantly effective to improve the structural integrity, which consequently affected the increase in the discharge capacity to 157 (4.3 V cut-off) and 182 mA h g -1 (4.6 V cut-off) at 25 deg. C with good reversibility

  9. Efficient single light-emitting layer pure blue phosphorescent organic light-emitting devices with wide gap host and matched interlayer

    Energy Technology Data Exchange (ETDEWEB)

    Jiang, Yunlong; Zhou, Liang, E-mail: zhoul@ciac.ac.cn; Cui, Rongzhen; Li, Yanan; Zhao, Xuesen; Zhang, Hongjie, E-mail: hongjie@ciac.ac.cn

    2015-12-15

    In this work, we report the highly efficient pure blue electroluminescent (EL) device based on bis[(3,5-difluoro-4-cyanophenyl)pyridine]picolinate iridium(III) (FCNIrpic) doped 9-(4-tert-Butylphenyl)-3,6-bis(triphenylsilyl)-9H-carbazole (CzSi) film. The matched energy levels of FCNIrpic and CzSi are helpful in facilitating the trapping of carriers, while the high triplet energy of CzSi can well avoid the undesired reverse energy transfer. More importantly, the injection of holes was further accelerated by inserting 5 nm 4,4′,4″-Tri(9-carbazoyl)triphenylamine (TcTa) film between hole transport layer and lighting-emitting layer (EML) as interlayer. Consequently, EL performances were significantly enhanced attributed to wider recombination zone and better balance of holes and electrons. Interestingly, single-EML device displayed higher performances than those of double-EMLs device. Finally, pure blue EL device with the structure of ITO/MoO{sub 3} (3 nm)/TAPC (40 nm)/TcTa (5 nm)/FCNIrpic (20%): CzSi (30 nm)/TmPyPB (40 nm)/LiF (1 nm)/Al (100 nm) realized the maximum brightness, current efficiency, power efficiency and external quantum efficiency up to 12,505 cd/m{sup 2}, 36.20 cd/A, 28.42 lm/W and 16.9%, respectively. Even at the high brightness of 1000 cd/m{sup 2}, current efficiency and external quantum efficiency up to 17.40 cd/A and 8.1%, respectively, can be retained by the same device.

  10. Ni foam supported quasi-core-shell structure of ultrathin Ti3C2 nanosheets through electrostatic layer-by-layer self-assembly as high rate-performance electrodes of supercapacitors

    Science.gov (United States)

    Tian, Yapeng; Yang, Chenhui; Que, Wenxiu; He, Yucheng; Liu, Xiaobin; Luo, Yangyang; Yin, Xingtian; Kong, Ling Bing

    2017-11-01

    Supercapacitor, as an important energy storage device, is a critical component for next generation electric power system, due to its high power density and long cycle life. In this study, a novel electrode material with quasi-core-shell structure, consisting of negatively charged few layer Ti3C2 nanosheets (FL-Ti3C2) and positively charged polyethyleneimine as building blocks, has been prepared by using an electrostatic layer-by-layer self-assembly method, with highly conductive Ni foam to be used as the skeleton. The unique quasi-core-shell structured ultrathin Ti3C2 nanosheets provide an excellent electron channel, ion transport channel and large effective contact area, thus leading to a great improvement in electrochemical performance of the material. The specific capacitance of the binder-free FL-Ti3C2@Ni foam electrodes reaches 370 F g-1 at the scan rate of 2 mV s-1 and a specific capacitance of 117 F g-1 is obtained even at the scan rate of 1000 mV s-1 in the electrolyte of Li2SO4, indicating a high rate performance. In addition, this electrode shows a long-term cyclic stability with a loss of only 13.7% after 10,000 circles. Furthermore, quantitative analysis has been conducted to ensure the relationship between the capacitive contribution and the rate performance of the as-fabricated electrode.

  11. Mn-doped NiP2 nanosheets as an efficient electrocatalyst for enhanced hydrogen evolution reaction at all pH values

    Science.gov (United States)

    Wang, Xiaodeng; Zhou, Hongpeng; Zhang, Dingke; Pi, Mingyu; Feng, Jiajia; Chen, Shijian

    2018-05-01

    Developing stable and high-efficiency hydrogen generation electrocatalysts, particularly for the cathode hydrogen evolution reaction (HER), is an urgent challenge in energy conversion technologies. In this work, we have successfully synthesized Mn-doped NiP2 nanosheets on carbon cloth (Mn-NiP2 NSs/CC), which behaves as a higher efficient three dimensional HER electrocatalyst with better stability at all pH values than pure NiP2. Electrochemical tests demonstrate that the catalytic activity of NiP2 is enhanced by Mn doping. In 0.5 M H2SO4, this Mn-NiP2 NSs/CC catalyst drives 10 mA cm-2 at an overpotential of 69 mV, which is 20 mV smaller than pure NiP2. To achieve the same current density, it demands overpotentials of 97 and 107 mV in 1.0 M KOH and phosphate-buffered saline (PBS), respectively. Compared with pure NiP2, higher HER electrocatalytic performance for Mn-NiP2 NSs/CC can be attributed to its lower thermo-neutral hydrogen adsorption free energy, which is supported by density functional theory calculations.

  12. Magnetoimpedance of FeNi-based asymmetric sensitive elements

    Energy Technology Data Exchange (ETDEWEB)

    Chlenova, A.A., E-mail: chlenova.anna@gmail.com [Ural Federal University, Laboratory of Magnetic Sensorics, Lenin Ave. 51, 620083 Ekaterinburg, Russian Ferderation (Russian Federation); Immanuel Kant Baltic Federal University, Science and Technology Park “Fabrica”, Gaidara str. 6, Kaliningrad (Russian Federation); Svalov, A.V.; Kurlyandskaya, G.V. [Ural Federal University, Laboratory of Magnetic Sensorics, Lenin Ave. 51, 620083 Ekaterinburg, Russian Ferderation (Russian Federation); Universidad del País Vasco, UPV/EHU, Departamento de Electricidad y Electrónica, P.O. Box 644, Bilbao 48080 (Spain); Volchkov, S.O. [Ural Federal University, Laboratory of Magnetic Sensorics, Lenin Ave. 51, 620083 Ekaterinburg, Russian Ferderation (Russian Federation)

    2016-10-01

    [Ti/FeNi]{sub 5}/Ti/Cu/Ti/[FeNi/Ti]{sub x} (x=0–5) multilayers were prepared by sputtering. Their magnetic properties and magnetoimpedance were studied focusing on future technological applications. Both (ΔZ/Z){sub max} and (ΔR/R){sub max} values showed a tendency to decrease with a decrease of the number of magnetic layers of the top multilayer. Such a parameter as an even or odd number of layers is important for the MI value. In the field interval of technological interest all [Ti/FeNi]{sub 5}/Ti/Cu/Ti/[FeNi/Ti]{sub x} structures show similar sensitivities of about 70%/Oe for ΔR/R ratios but the lower the number of magnetic layers in the top multilayer, the higher the operating frequency. - Highlights: • Giant magnetoimpedance effect. • Non-symmetric multilayers sructure. • Biosensing.

  13. Research on microstructure properties of the TiC/Ni-Fe-Al coating prepared by laser cladding technology

    Science.gov (United States)

    Jiao, Junke; Xu, Zifa; Zan, Shaoping; Zhang, Wenwu; Sheng, Liyuan

    2017-10-01

    In this paper, the laser cladding method was used to preparation the TiC reinforced Ni-Fe-Al coating on the Ni base superalloy. The Ti/Ni-Fe-Al powder was preset on the Ni base superalloy and the powder layer thickness is 0.5mm. A fiber laser was used the melting Ti/Ni-Fe-Al powder in an inert gas environment. The shape of the cladding layer was tested using laser scanning confocal microscope (LSCM) under different cladding parameters such as the laser power, the melting velocity and the defocused amount. The microstructure, the micro-hardness was tested by LSCM, SEM, Vickers hardness tester. The test result showed that the TiC particles was distributed uniformly in the cladding layer and hardness of the cladding layer was improved from 180HV to 320HV compared with the Ni-Fe-Al cladding layer without TiC powder reinforced, and a metallurgical bonding was produced between the cladding layer and the base metal. The TiC powder could make the Ni-Fe-Al cladding layer grain refining, and the more TiC powder added in the Ni-Fe-Al powder, the smaller grain size was in the cladding layer.

  14. Study of PtNi/C catalyst for direct ethanol fuel cell

    International Nuclear Information System (INIS)

    Moraes, L.P.R. de; Silva, E.L. da; Amico, S.C.; Malfatti, C.F.

    2014-01-01

    In this work, PtNi binary catalyst and pure platin catalyst were synthesized by the impregnation-reduction method, using Vulcan XC72R as support, for direct ethanol fuel cells. The composition and structure of the catalysts were analyzed by X-ray diffraction, the electrochemical behavior was evaluated by cyclic voltammetry and morphology of the catalysts was studied by high-resolution transmission electron microscopy. The results showed that the addition of Ni to Pt led to the contraction of the crystal lattice, increased the catalytic activity compared to pure Pt and initiated the electrooxidation of ethanol at lower potential. (author)

  15. Structural, Optical, Morphological and Elemental Analysis on Sol-gel Synthesis of Ni Doped TiO2 Nanocrystallites

    Directory of Open Access Journals (Sweden)

    T. Sakthivel

    2017-06-01

    Full Text Available Pure and Ni doped titanium dioxide nanoparticles were successfully synthesized by sol-gel method and characterized usingXRD, UV-Visible, FTIR, FESEM and EDS techniques. XRD pattern confirms the formation of tetragonal TiO2. The absorbance spectra of pure and Ni doped TiO2 showed absorption spectrum at ultra-violet region due to electronic transition between bonding and anti-bonding orbital (π-π•. Bandgap energy of Ni doped TiO2 decreased to 2.5 eV when compared to pure TiO2 (3.39 eV. FESEM study reveals agglomerated spherical shaped morphology. The functional groups of the prepared samples were identified using FTIR spectroscopy and the elemental analysis was further supported with EDS analysis.

  16. Catalytic reforming of glycerol in supercritical water over bimetallic Pt-Ni catalyst

    NARCIS (Netherlands)

    Chakinala, A.G.; van Swaaij, Willibrordus Petrus Maria; Kersten, Sascha R.A.; de Vlieger, Dennis; Seshan, Kulathuiyer; Brilman, Derk Willem Frederik

    2013-01-01

    Catalytic reforming of pure glycerol for the production of hydrogen at low temperature and short residence times in supercritical water was investigated using a bimetallic Pt–Ni catalyst supported on alumina. Initial tests were carried out to study the reforming activity of bimetallic Pt–Ni

  17. Photoelectron spectroscopy study on Li substituted NiO using PES beamline installed on Indus-1

    Science.gov (United States)

    Banerjee, A.; Chaudhari, S. M.; Phase, D. M.; Dasannacharya, B. A.

    2003-01-01

    Photoelectron spectroscopy beamline based on a toroidal grating monochromator (TGM) is recently commissioned on Indus-1 storage ring. It has been used to carry out valence band photoemission study of Li substituted NiO. In this paper initially a brief description of the beamline components and the experimental station for angle integrated photoemission experiment is presented. The later part of this paper is devoted to studies carried out on Li xNi 1- xO with x=0.0, 0.35 and 0.5 samples. Thin pellets of polycrystalline samples were used for the measurements reported here. Valence band spectra recorded on polycrystalline Li xNi 1- xO samples show drastic changes in various features as compared to that of pure NiO. The prominent changes are: (i) change in the relative contributions of Ni-3d and O-2p emissions, (ii) change in the peak position of Ni-3d from the top of the valance band of NiO and (iii) no noticeable change in the Ni satellite peak. These results are evaluated in terms of earlier findings in pure and low Li doped NiO.

  18. Room-Temperature and Solution-Processable Cu-Doped Nickel Oxide Nanoparticles for Efficient Hole-Transport Layers of Flexible Large-Area Perovskite Solar Cells.

    Science.gov (United States)

    He, Qiqi; Yao, Kai; Wang, Xiaofeng; Xia, Xuefeng; Leng, Shifeng; Li, Fan

    2017-12-06

    Flexible perovskite solar cells (PSCs) using plastic substrates have become one of the most attractive points in the field of thin-film solar cells. Low-temperature and solution-processable nanoparticles (NPs) enable the fabrication of semiconductor thin films in a simple and low-cost approach to function as charge-selective layers in flexible PSCs. Here, we synthesized phase-pure p-type Cu-doped NiO x NPs with good electrical properties, which can be processed to smooth, pinhole-free, and efficient hole transport layers (HTLs) with large-area uniformity over a wide range of film thickness using a room-temperature solution-processing technique. Such a high-quality inorganic HTL allows for the fabrication of flexible PSCs with an active area >1 cm 2 , which have a power conversion efficiency over 15.01% without hysteresis. Moreover, the Cu/NiO x NP-based flexible devices also demonstrate excellent air stability and mechanical stability compared to their counterpart fabricated on the pristine NiO x films. This work will contribute to the evolution of upscaling flexible PSCs with a simple fabrication process and high device performances.

  19. Electrodeposition and Properties of Copper Layer on NdFeB Device

    Directory of Open Access Journals (Sweden)

    LI Yue

    2017-06-01

    Full Text Available To decrease the impact of the regular Ni/Cu/Ni coating on the magnetic performance of sintered NdFeB device, alkaline system of HEDP complexing agent was applied to directly electro-deposit copper layer on NdFeB matrix, then nickel layer was electrodeposited on the copper layer and Cu/Ni coating was finally obtained to replace the regular Ni/Cu/Ni coating. The influence of concentration of HEDP complexing agent on deposition course was tested by electrochemical testing; morphology of copper layer was characterized by SEM, XRD and TEM; the binding force of copper layer and the thermal reduction of magnetic of NdFeB caused by electrodeposited coating were respectively explored through the thermal cycle test and thermal demagnetization test. The results show that the concentration of HEDP has great impact on the deposition overpotential of copper. In the initial electrodepositing stage, copper particles precipitate at the grain boundaries of NdFeB magnets with a preferred (111 orientation. The copper layer is compact and has enough binding force with the NdFeB matrix to meet the requirements in SJ 1282-1977. Furthermore, the thermal demagnetization loss rate of the sintered NdFeB with the protection of Cu/Ni coating is significantly less than that with the protection of Ni/Cu/Ni coating.

  20. Structural characterization of half-metallic Heusler compound NiMnSb

    Energy Technology Data Exchange (ETDEWEB)

    Nowicki, L. E-mail: lech.nowicki@fuw.edu.pl; Abdul-Kader, A.M.; Bach, P.; Schmidt, G.; Molenkamp, L.W.; Turos, A.; Karczewski, G

    2004-06-01

    High resolution X-ray diffraction (HRXRD) and Rutherford backscattering/channeling (RBS/c) techniques were used to characterize layers of NiMnSb grown by molecular beam epitaxy (MBE) on InP with a In{sub x}Ga{sub 1-x}As buffer. Angular scans in the channeling mode reveal that the crystal structure of NiMnSb is tetragonally deformed with c/a=1.010{+-}0.002, in agreement with HRXRD data. Although HRXRD demonstrates the good quality of the pseudomorphic NiMnSb layers the channeling studies show that about 20% of atoms in the layers do not occupy lattice sites in the [0 0 1] rows of NiMnSb. The possible mechanisms responsible for the observed disorder are discussed.

  1. Magnetoresistance and negative differential resistance in Ni/graphene/Ni vertical heterostructures driven by finite bias voltage: a first-principles study

    DEFF Research Database (Denmark)

    Saha, Kamal K.; Blom, Anders; Thygesen, Kristian S.

    2012-01-01

    Using the nonequilibrium Green's function formalism combined with density functional theory, we study finite bias quantum transport in Ni/Grn/Ni vertical heterostructures where n graphene layers are sandwiched between two semi-infinite Ni(111) electrodes. We find that the recently predicted “pess...... differential resistance as the bias voltage is increased from Vb=0 V to Vb≃0.5 V. We confirm that both of these nonequilibrium transport effects hold for different types of bonding of Gr on the Ni(111) surface while maintaining Bernal stacking between individual Gr layers....... “pessimistic” magnetoresistance of 100% for n≥5 junctions at zero bias voltage Vb→0 persists up to Vb≃0.4 V, which makes such devices promising for spin-torque-based device applications. In addition, for parallel orientations of the Ni magnetizations, the n=5 junction exhibits a pronounced negative...

  2. Corrosion Resistance of Ni/Al2O3 Nanocomposite Coatings

    Directory of Open Access Journals (Sweden)

    Beata KUCHARSKA

    2016-05-01

    Full Text Available Nickel matrix composite coatings with ceramic disperse phase have been widely investigated due to their enhanced properties, such as higher hardness and wear resistance in comparison to the pure nickel. The main aim of this research was to characterize the structure and corrosion properties of electrochemically produced Ni/Al2O3 nanocomposite coatings. The coatings were produced in a Watts bath modified by nickel grain growth inhibitor, cationic surfactant and the addition of alumina particles (low concentration 5 g/L. The process has been carried out with mechanical and ultrasonic agitation. The Ni/Al2O3 nanocomposite coatings were characterized by SEM, XRD and TEM techniques. In order to evaluate corrosion resistance of produced coatings, the corrosion studies have been carried out by the potentiodynamic method in a 0.5 M NaCl solution. The corrosion current, corrosion potential and corrosion rate were determined. Investigations of the morphology, topography and corrosion damages of the produced surface layers were performed by scanning microscope techniques. DOI: http://dx.doi.org/10.5755/j01.ms.22.1.7407

  3. A theoretical study of CH4 dissociation on pure and gold-alloyed Ni(111) surfaces

    DEFF Research Database (Denmark)

    Kratzer, P.; Hammer, Bjørk; Nørskov, Jens Kehlet

    1996-01-01

    We present a density functional theory study of the first step of CH4 adsorption on the Ni(111) surface, dissociation into adsorbed CH3 and H. The rupture of the C-H bond occurs preferentially on top of a Ni atom, with a dissociation barrier of about 100 kJ/mol (including zero point corrections......). The transition state involves considerable internal excitation of the molecule. The active C-H bond is both stretched to 1.6 Angstrom and tilted relative to the methyl group. A normal mode analysis shows that the reaction coordinate is mainly a C-H stretch, while the orientation of the C-H bond relative...... to the surface is responsible for the highest real mode. Alloying the surface with gold also affects the reactivity of the Ni atoms on adjacent surface sites. The dissociation barrier is increased by 16 and 38 kJ/mol for a Ni atom with one or two gold neighbors, respectively. We attribute these changes...

  4. Characterization of Al/Ni multilayers and their application in diffusion bonding of TiAl to TiC cermet

    Energy Technology Data Exchange (ETDEWEB)

    Cao, J., E-mail: cao_jian@hit.edu.cn [State Key Lab of Advanced Welding Production Technology, Harbin Institute of Technology, Harbin, 150001 (China); Center for Composite Materials and Structures, Harbin Institute of Technology, Harbin, 150001 (China); Song, X.G. [State Key Lab of Advanced Welding Production Technology, Harbin Institute of Technology, Harbin, 150001 (China); Wu, L.Z. [Center for Composite Materials and Structures, Harbin Institute of Technology, Harbin, 150001 (China); Qi, J.L.; Feng, J.C. [State Key Lab of Advanced Welding Production Technology, Harbin Institute of Technology, Harbin, 150001 (China)

    2012-02-29

    The Al/Ni multilayers were characterized and diffusion bonding of TiAl intermetallics to TiC cermets was carried out using the multilayers. The microstructure of Al/Ni multilayers and TiAl/TiC cermet joint was investigated. The layered structures consisting of a Ni{sub 3}(AlTi) layer, a Ni{sub 2}AlTi layer, a (Ni,Al,Ti) layer and a Ni diffusion layer were observed from the interlayer to the TiAl substrate. Only one AlNi{sub 3} layer formed at the multilayer/TiC cermet interface. The reaction behaviour of Al/Ni multilayers was characterized by means of differential scanning calorimeter (DSC) and X-ray diffraction. The initial exothermic peak of the DSC curve was formed due to the formation of Al{sub 3}Ni and Al{sub 3}Ni{sub 2} phases. The reaction sequence of the Al/Ni multilayers was Al{sub 3}Ni {yields} Al{sub 3}Ni{sub 2} {yields} AlNi {yields} AlNi{sub 3} and the final products were AlNi and AlNi{sub 3} phases. The shear strength of the joint was tested and the experimental results suggested that the application of Al/Ni multilayers improved the joining quality. - Highlights: Black-Right-Pointing-Pointer Diffusion bonding of TiAl to TiC cermet was realized using Al/Ni multilayer. Black-Right-Pointing-Pointer The reaction sequence of the Al/Ni multilayers was Al{sub 3}Ni {yields} Al{sub 3}Ni{sub 2} {yields} AlNi {yields} AlNi{sub 3}. Black-Right-Pointing-Pointer The interfacial microstructure of the joint was clarified. Black-Right-Pointing-Pointer The application of Al/Ni multilayers improved the joining quality.

  5. Microstructure and Properties of Ni and Ni/Al2O3 Coatings Electrodeposited at Various Current Densities

    Directory of Open Access Journals (Sweden)

    Góral A.

    2016-03-01

    Full Text Available The study presents investigations of an influence of various direct current densities on microstructure, residual stresses, texture, microhardness and corrosion resistance of the nickel coatings electrodeposited from modified Watt’s baths. The properties of obtained coatings were compared to the nano-crystalline composite Ni/Al2O3 coatings prepared under the same plating conditions. The similarities and differences of the obtained coatings microstructures visible on both their surfaces and cross sections and determined properties were presented. The differences in the growth character of the Ni matrix and in the microstructural properties were observed. All electrodeposited Ni and Ni/Al2O3 coatings were compact and well adhering to the steel substrates. The thickness and the microhardness of the Ni and Ni/Al2O3 deposits increased significantly with the current density in the range 2 - 6 A/dm2. Residual stresses are tensile and they reduced as the current density increased. The composite coatings revealed better protection from the corrosion of steel substrate than pure nickel in solution 1 M NaCl.

  6. An investigation of the oxidized Ni/InAs interface

    International Nuclear Information System (INIS)

    Venter, A.; Botha, J.R.; Swart, H.C.; Naidoo, S.; Olivier, E.J.

    2009-01-01

    Ni was resistively deposited onto bulk InAs and subsequently oxidized in an O 2 atmosphere. The anneal temperature and time were 450 deg. C and 2.5 h, respectively. X-ray diffraction of the oxidized Ni/InAs sample revealed the formation of In 3 Ni 2 and In 2 O 3 on the front suggesting inter diffusion of In, Ni and O. NiO was not detected by X-ray diffraction. In a preliminary study, using glass as a substrate, NiO readily formed when using these oxidation parameters. Conductivity measurements of the oxidized Ni/InAs surface revealed a conducting front and insulating rear surface while TEM of the Ni/InAs interface revealed an intermediate amorphous diffusion zone between the 'oxidized' Ni layer and the bulk InAs. A closer investigation of the intermediate layer supports the X-ray diffraction results, suggesting compound formation due to diffusion of oxygen and nickel into the substrate, and out-diffusion of In and As from the bulk of the sample. AES was used to further elucidate these results.

  7. Characterization of Sputtered Nickel-Titanium (NiTi) Stress and Thermally Actuated Cantilever Bimorphs Based on NiTi Shape Memory Alloy (SMA)

    Science.gov (United States)

    2015-11-01

    necessary anneal . Following this, a thin film of NiTi was blanket sputtered at 600 °C. This NiTi blanket layer was then wet -etch patterned using a...varying the sputter parameters during NiTi deposition, such as thickness, substrate temperature during deposition and anneal , and argon pressure during...6 Fig. 4 Surface texture comparison between NiTi sputtered at RT, then annealed at 600 °C, and NiTi

  8. Induced spin-polarization of EuS at room temperature in Ni/EuS multilayers

    Energy Technology Data Exchange (ETDEWEB)

    Poulopoulos, P., E-mail: poulop@upatras.gr [Laboratory of High-Tech Materials, School of Engineering, University of Patras, 26504 Patras (Greece); Materials Science Department, University of Patras, 26504 Patras (Greece); Goschew, A.; Straub, A.; Fumagalli, P. [Institut für Experimentalphysik, Freie Universität Berlin, Arnimallee 14, D-14195 Berlin-Dahlem (Germany); Kapaklis, V.; Wolff, M. [Department of Physics and Astronomy, Uppsala University, Box 516, SE-751 20 Uppsala (Sweden); Delimitis, A. [Chemical Process and Energy Resources Institute (CPERI), Centre for Research and Technology Hellas (CERTH), 57001 Thermi, Thessaloniki (Greece); Wilhelm, F.; Rogalev, A. [European Synchrotron Radiation Facility (ESRF), B.P.220, 38043 Grenoble (France); Pappas, S. D. [Laboratory of High-Tech Materials, School of Engineering, University of Patras, 26504 Patras (Greece); Department of Physics and Astronomy, Uppsala University, Box 516, SE-751 20 Uppsala (Sweden)

    2014-03-17

    Ni/EuS multilayers with excellent multilayer sequencing are deposited via e-beam evaporation on the native oxide of Si(100) wafers at 4 × 10{sup −9} millibars. The samples have very small surface and interface roughness and show sharp interfaces. Ni layers are nanocrystalline 4–8 nm thick and EuS layers are 2–4 nm thick and are either amorphous or nanocrystalline. Unlike for Co/EuS multilayers, all Eu ions are in divalent (ferromagnetic) state. We show a direct antiferromagnetic coupling between EuS and Ni layers. At room temperature, the EuS layers are spin-polarized due to the proximity of Ni. Therefore, Ni/EuS is a candidate for room-temperature spintronics applications.

  9. Ultraviolet light-absorbing and emitting diodes consisting of a p-type transparent-semiconducting NiO film deposited on an n-type GaN homoepitaxial layer

    Science.gov (United States)

    Nakai, Hiroshi; Sugiyama, Mutsumi; Chichibu, Shigefusa F.

    2017-05-01

    Gallium nitride (GaN) and related (Al,Ga,In)N alloys provide practical benefits in the production of light-emitting diodes (LEDs) and laser diodes operating in ultraviolet (UV) to green wavelength regions. However, obtaining low resistivity p-type AlN or AlGaN of large bandgap energies (Eg) is a critical issue in fabricating UV and deep UV-LEDs. NiO is a promising candidate for useful p-type transparent-semiconducting films because its Eg is 4.0 eV and it can be doped into p-type conductivity of sufficiently low resistivity. By using these technologies, heterogeneous junction diodes consisting of a p-type transparent-semiconducting polycrystalline NiO film on an n-type single crystalline GaN epilayer on a low threading-dislocation density, free-standing GaN substrate were fabricated. The NiO film was deposited by using the conventional RF-sputtering method, and the GaN homoepitaxial layer was grown by metalorganic vapor phase epitaxy. They exhibited a significant photovoltaic effect under UV light and also exhibited an electroluminescence peak at 3.26 eV under forward-biased conditions. From the conduction and valence band (EV) discontinuities, the NiO/GaN heterointerface is assigned to form a staggered-type (TYPE-II) band alignment with the EV of NiO higher by 2.0 eV than that of GaN. A rectifying property that is consistent with the proposed band diagram was observed in the current-voltage characteristics. These results indicate that polycrystalline NiO functions as a hole-extracting and injecting layer of UV optoelectronic devices.

  10. Characterization of thin Zn-Ni alloy coatings electrodeposited on low carbon steel

    International Nuclear Information System (INIS)

    El Hajjami, A.; Gigandet, M.P.; De Petris-Wery, M.; Catonne, J.C.; Duprat, J.J.; Thiery, L.; Raulin, F.; Pommier, N.; Starck, B.; Remy, P.

    2007-01-01

    The characteristics of initial layer formation in alkaline bath for Zn-Ni (12-15%) alloy electrodeposition on low carbon steel plates are detected in a nanometric thickness range by electron probe microanalysis (EPMA), with both bulk sample and thin film on substrate correction procedure, glow discharge optical emission spectroscopy (GDOES) and gracing incidence X-ray diffraction (GIXRD). The Zn-Ni coatings were elaborated using either intensiostatic or potentiostatic mode. A preferential deposition of Ni, in the initial thin layer, is detected by these analyses; according to EPMA and GDOES measurements, a layer rich in nickel at the interface substrate/deposit is observed (90 wt.% Ni) and approved by GIXRD; the thin layer of Ni formed in the first moments of electrolysis greatly inhibits the Zn deposition. The initial layer depends upon the relative ease of hydrogen and metal discharge and on the different substrate surfaces involved. The electrodeposition of zinc-nickel alloys in the first stage is a normal phenomenon of codeposition, whereby nickel - the more noble metal - is deposited preferentially

  11. Microwave-irradiated preparation of reduced graphene oxide-Ni nanostructures and their enhanced performance for catalytic reduction of 4-nitrophenol

    Science.gov (United States)

    Qiu, Hanxun; Qiu, Feilong; Han, Xuebin; Li, Jing; Yang, Junhe

    2017-06-01

    Here we report an environmentally friendly, one-pot strategy toward preparation of nickel nanoparticle-decorated reduced graphene-oxide (Ni-RGO) nanostructures, by employing Ni(AC)2 as nickel source and ethylene glycol as both solvent and reducing agent via a facile microwave irradiation heating approach. The results show that Ni nanoparticles with an average diameter of around 40 nm are homogeneously anchored onto the surface of RGO sheets. As compared to the pure Ni nanoparticles and RGO sheets, Ni-RGO composites with over 64 wt% loading of Ni nanoparticles possess superior catalytic activities and selectivity toward the reduction of 4-nitrophenol. The corresponding kinetic reaction rate constant (defined as κ) is even four-fold compared to pure Ni nanoparticles. Such promising composites show great potential for friendly treatment of industrial waste containing nitrophenol in a simple, sustainable and green way.

  12. First-principles modeling of interfaces between solids with large lattice mismatch: The prototypical CoO(111)/Ni(111) interface

    KAUST Repository

    Grytsiuk, Sergii

    2012-11-28

    In this work we investigate the CoO(111)/Ni(111) interface by first-principles calculations, focusing on its structure and stability. To satisfy the approximate 5:6 ratio of the CoO and Ni lattice constants, we construct a supercell with 5×5 Co (O) and 6×6 Ni atoms per layer in the bulk regions. For the interface Ni layer and the adjacent Ni layer we consider different configurations and study the binding energy. We show for an ideal CoO interface terminated by 5×5 O atoms that the structure is more stable if there are 5×5 Ni atoms next to it instead of 6×6 as in the bulk. In addition, we observe that a transition layer with 31 or 33 Ni atoms located between the interface 5×5 Ni and bulk 6×6 Ni layers (which partially reflects the structures of both these layers) enhances the stability of the CoO/Ni interface. The electronic and magnetic modifications induced by the interface formation are discussed.

  13. First-principles modeling of interfaces between solids with large lattice mismatch: The prototypical CoO(111)/Ni(111) interface

    KAUST Repository

    Grytsyuk, Sergiy; Peskov, Maxim; Schwingenschlö gl, Udo

    2012-01-01

    In this work we investigate the CoO(111)/Ni(111) interface by first-principles calculations, focusing on its structure and stability. To satisfy the approximate 5:6 ratio of the CoO and Ni lattice constants, we construct a supercell with 5×5 Co (O) and 6×6 Ni atoms per layer in the bulk regions. For the interface Ni layer and the adjacent Ni layer we consider different configurations and study the binding energy. We show for an ideal CoO interface terminated by 5×5 O atoms that the structure is more stable if there are 5×5 Ni atoms next to it instead of 6×6 as in the bulk. In addition, we observe that a transition layer with 31 or 33 Ni atoms located between the interface 5×5 Ni and bulk 6×6 Ni layers (which partially reflects the structures of both these layers) enhances the stability of the CoO/Ni interface. The electronic and magnetic modifications induced by the interface formation are discussed.

  14. Graphene synthesis from graphite/Ni composite films grown by sputtering

    International Nuclear Information System (INIS)

    Shin, Dong Hee; Yang, Seung Bum; Shin, Dong Yeol; Kim, Chang Oh; Kim, Sung; Choi, Suk Ho; Paek, Sang Hyon

    2012-01-01

    Graphite/Ni composite films have been deposited on SiO 2 /Si (100) wafers by varying their graphite concentration (n G ) and thickness (t) from 2 to 12 wt% and 40 to 400 nm, respectively, in a RF sputtering system, subsequently annealed at 900 .deg. C for 4 min, and then slowly cooled to room temperature to form graphene layers on Ni surfaces. Several structural-analysis techniques reveal the optimum nG (∼8 wt%) and t (∼160 nm) of the composite films for the synthesis of fewest-layer, defect-minimized graphene. At the annealing temperature, carbon atoms diffuse out from the composite film, followed by their precipitation as graphene on the Ni layer as the carbon solubility limit in Ni is reached during the cooling period. Based on this mechanism, the optimum conditions are explained. Our approach provides an advantage in that the number of layers can be simply tuned by varying n G and t of the composite films.

  15. Joining of Ni-TiC FGM and Ni-Al Intermetallics by Centrifugal Combustion Synthesis

    International Nuclear Information System (INIS)

    Ohmi, Tatsuya; Matsuura, Kiyotaka; Iguchi, Manabu; Mizuma, Kiminori

    2008-01-01

    A centrifugal combustion synthesis (CCS) process has been investigated to join a Ni-Al intermetallic compound and a Ni-TiC cermet. The cermet, a tubular graphite mold, and a green compact of reactants consisting of Al, Ni and NiO were set in a centrifugal caster. When the combustion synthesis reaction was induced in the centrifugal force field, a synthesized molten Ni-Al alloy flowed into the graphite mold and joined to the cermet. The soundness of the joint interface depended on the volume percentage of TiC phase in the cermet. A lot of defects were formed near the interface between the Ni-TiC cermet and the cast Ni-Al alloy when the volume percentage of TiC was 50% or higher. For this kind of cermet system, using a functionally graded cermet such as Ni-10 vol.%TiC/Ni-25 vol.%TiC/Ni-50 vol.%TiC overcame this difficulty. The four-point bending strength of the joined specimen consisting of the three-layered FGM cermet and cast Ni-29 mol%Al alloy was 1010 MPa which is close to the result for a Ni-29 mol%Al alloy specimen

  16. Reactive Ni/Ti nanolaminates

    International Nuclear Information System (INIS)

    Adams, D. P.; Bai, M. M.; Rodriguez, M. A.; McDonald, J. P.; Jones, E. Jr.; Brewer, L.; Moore, J. J.

    2009-01-01

    Nickel/titanium nanolaminates fabricated by sputter deposition exhibited rapid, high-temperature synthesis. When heated locally, self-sustained reactions were produced in freestanding Ni/Ti multilayer foils characterized by average propagation speeds between ∼0.1 and 1.4 m/s. The speed of a propagating reaction front was affected by total foil thickness and bilayer thickness (layer periodicity). In contrast to previous work with compacted Ni-Ti powders, no preheating of Ni/Ti foils was required to maintain self-propagating reactions. High-temperature synthesis was also stimulated by rapid global heating demonstrating low ignition temperatures (T ig )∼300-400 deg. C for nanolaminates. Ignition temperature was influenced by bilayer thickness with more coarse laminate designs exhibiting increased T ig . Foils reacted in a vacuum apparatus developed either as single-phase B2 cubic NiTi (austenite) or as a mixed-phase structure that was composed of monoclinic B19 ' NiTi (martensite), hexagonal NiTi 2 , and B2 NiTi. Single-phase, cubic B2 NiTi generally formed when the initial bilayer thickness was made small.

  17. Investigation of microstructural evolution and electrical properties for Ni-Sn transient liquid-phase sintering bonding

    Science.gov (United States)

    Feng, Hong-Liang; Huang, Ji-Hua; Yang, Jian; Zhou, Shao-Kun; Zhang, Rong; Wang, Yue; Chen, Shu-Hai

    2017-11-01

    Ni/Ni-Sn/Ni sandwiched simulated package structures were successfully bonded under low temperature and low pressure by Ni-Sn transient liquid-phase sintering bonding. The results show that, after isothermally holding for 240 min at 300 °C and 180 min at 340 °C, Sn was completely transformed into Ni3Sn4 intermetallic compounds. When the Ni3Sn4 phases around Ni particles were pressed together, the porosity of the bonding layer increased, which obviously differed from the normal sintering densification process. With further analysis of this phenomenon, it was found that large volume shrinkage (14.94% at 340 °C) occurred when Ni reacted with Sn to form Ni3Sn4, which caused void formation. A mechanistic model of the microstructural evolution in the bonding layer was proposed. Meanwhile, the resistivity of the bonding layer was measured and analyzed by using the four-probe method; the microstructural evolution was well reflected by the resistivity of the bonding layer. The relationship between the resistivity and microstructure was also discussed in detail.[Figure not available: see fulltext.

  18. Effect of gamma-irradiation on some structural characteristics of NiO

    International Nuclear Information System (INIS)

    El-Shabiny, A.M.; El-Shobaky, G.A.; Dessouki, A.M.; Ramadan, A.A.

    1989-01-01

    Pure NiO specimens were prepared by the thermal decomposition of pure basic nickel carbonate in air at 400 and 600 0 C. The obtained solids were exposed to different doses of γ-irradiation ranging between 10-80 Mrad. The change in residual microstrain, lattice parameter and crystallite size due to the irradiation process were investigated by X-ray diffraction analyses. The results revealed that γ-irradiation effected important changes in the structural characteristics of NiO lattice. No detectable change was observed for the crystallite size of NiO-400 0 C; however, the crystallite size of NiO-600 0 C decreased by increasing the dose up to 20 Mrad and increased at higher doses but still remaining smaller than that measured for the unirradiated specimen. The lattice parameters of NiO preheated at 400 or 600 0 C were found to increase as a function of the dose. These results were attributed to progressive removal of Ni 3+ ions acting as lattice defects in NiO solid. The microstrains in NiO specimens precalcined either at 400 or 600 0 C were found to decrease progressively by increasing the dose falling to minimum values at doses of 40 and 80 Mrad for the solids preheated at 600 and 400 0 C, respectively. The augmentation of the exposure dose above 40 Mrad for NiO-600 0 C resulted in an increase in microstrain which, however, remained always smaller than those found for the unirradiated solid. The strain-relief in NiO-600 0 C due to γ-irradiation took place, mainly, via splitting of its crystallites. On the other hand, the progressive removal of lattice defects (Ni 3+ ions) due to the irradiation process might account for the observed strain-relief in NiO-400 0 C. (author)

  19. Interdiffusion studies on high-Tc superconducting YBa2Cu3O7-δ thin films on Si(111) with a NiSi2/ZrO2 buffer layer

    DEFF Research Database (Denmark)

    Aarnink, W.A.M.; Blank, D.H.A.; Adelerhof, D.J.

    1991-01-01

    Interdiffusion studies on high-T(c) superconducting YBa2Cu3O7-delta thin films with thickness in the range of 2000-3000 angstrom, on a Si(111) substrate with a buffer layer have been performed. The buffer layer consists of a 400 angstrom thick epitaxial NiSi2 layer covered with 1200 angstrom...... of polycrystalline ZrO2. YBa2Cu3O7-delta films were prepared using laser ablation. The YBa2Cu3O7-delta films on the Si/NiSi2/ZrO2 substrates are of good quality; their critical temperatures T(c,zero) and T(c,onset) have typical values of 85 and 89 K, respectively. The critical current density j(c) at 77 K equaled 4...... x 10(4) A/cm2. With X-ray analysis (XRD), only c-axis orientation has been observed. The interdiffusion studies, using Rutherford backscattering spectrometry (RBS) and scanning Auger microscopy (SAM) show that the ZrO2 buffer layer prevents severe Si diffusion to the YBa2Cu3O7-delta layer, the Si...

  20. Mechanical and structural properties of sputtered Ni/Ti multilayers

    Energy Technology Data Exchange (ETDEWEB)

    Senthil Kumar, M.; Boeni, P.; Tixier, S.; Clemens, D.; Horisberger, M. [Paul Scherrer Inst. (PSI), Villigen (Switzerland)

    1997-09-01

    Ni/Ti bilayers have been prepared by dc-magnetron sputtering in order to study their mechanical and structural properties. A remarkable reduction of stress is observed when the Ni layers are sputtered reactively in argon with a high partial pressure of air. The high angle x-ray diffraction studies show a tendency towards amorphisation of the Ni layers with increasing air flow. The low angle measurements indicate a substantial reduction of interdiffusion resulting in smoother interfaces with increasing air content. (author) 2 figs., 2 refs.

  1. Cube Texture Formation of Cu-33at.%Ni Alloy Substrates and CeO2 Buffer Layer for YBCO Coated Conductors

    DEFF Research Database (Denmark)

    Tian, Hui; Li, Suo Hong; Ru, Liang Ya

    2014-01-01

    Cube texture formation of Cu-33 at.%Ni alloy substartes and CeO2 buffer layer prepared by chemical solution deposition on the textured substrate were investigated by electron back scattered diffraction (EBSD) and XRD technics systematically. The results shown that a strong cube textured Cu-33at...

  2. Magnetic studies of spin wave excitations in Ni/Au multilayers

    International Nuclear Information System (INIS)

    Salhi, H.; Chafai, K.; Benkirane, K.; Lassri, H.; Abid, M.; Hlil, E.K.

    2010-01-01

    Ni/Au multilayers were prepared by the electron beam evaporation method under ultra high vacuum conditions. The multilayer films have a coherent structure with (1 1 1) texture. The magnetic properties of Ni/Au multilayers are examined as a function of Ni layer thickness t Ni . The temperature dependence of the spontaneous magnetization M(T) is well described by a T 3/2 law in all multilayers. A spin wave theory has been used to explain the magnetization versus temperature. Based on this theory, the approximate values for the bulk exchange interaction J b , surface exchange interaction J S and the interlayer coupling strength J I have been obtained for various Ni layer thicknesses.

  3. Magnetron sputtered Cu{sub 3}N/NiTiCu shape memory thin film heterostructures for MEMS applications

    Energy Technology Data Exchange (ETDEWEB)

    Kaur, Navjot; Choudhary, Nitin [Indian Institute of Technology Roorkee, Roorkee, Functional Nanomaterials Research Lab, Department of Physics and Centre of Nanotechnology (India); Goyal, Rajendra N. [Indian Institute of Technology, Roorkee, Department of Chemistry (India); Viladkar, S. [Indian Institute of Technology Roorkee, Roorkee, Functional Nanomaterials Research Lab, Department of Physics and Centre of Nanotechnology (India); Matai, I.; Gopinath, P. [Indian Institute of Technology, Roorkee, Centre for Nanotechnology (India); Chockalingam, S. [Indian Institute of Technology, Guwahati, Department of Biotechnology (India); Kaur, Davinder, E-mail: dkaurfph@iitr.ernet.in [Indian Institute of Technology Roorkee, Roorkee, Functional Nanomaterials Research Lab, Department of Physics and Centre of Nanotechnology (India)

    2013-03-15

    In the present study, for the first time, Cu{sub 3}N/NiTiCu/Si heterostructures were successfully grown using magnetron sputtering technique. Nanocrystalline copper nitride (Cu{sub 3}N with thickness {approx}200 nm) thin films and copper nanodots were subsequently deposited on the surface of 2-{mu}m-thick NiTiCu shape memory thin films in order to improve the surface corrosion and nickel release properties of NiTiCu thin films. Interestingly, the phase transformation from martensite phase to austenite phase has been observed in Cu{sub 3}N/NiTiCu heterostructures with corresponding change in texture and surface morphology of top Cu{sub 3}N films. Field emission scanning electron microscopy and atomic force microscope images of the heterostructures reveals the formation of 20-nm-sized copper nanodots on NiTiCu surface at higher deposition temperature (450 Degree-Sign C) of Cu{sub 3}N. Cu{sub 3}N passivated NiTiCu films possess low corrosion current density with higher corrosion potential and, therefore, better corrosion resistance as compared to pure NiTiCu films. The concentration of Ni released from the Cu{sub 3}N/NiTiCu samples was observed to be much less than that of pure NiTiCu film. It can be reduced to the factor of about one-ninth after the surface passivation resulting in smooth, homogeneous and highly corrosion resistant surface. The antibacterial and cytotoxicity of pure and Cu{sub 3}N coated NiTiCu thin films were investigated through green fluorescent protein expressing E. coli bacteria and human embryonic kidney cells. The results show the strong antibacterial property and non cytotoxicity of Cu{sub 3}N/NiTiCu heterostructure. This work is of immense technological importance due to variety of BioMEMS applications.

  4. Influence of the alloying effect on nickel K-shell fluorescence yield in Ni Si alloys

    Science.gov (United States)

    Kalayci, Y.; Agus, Y.; Ozgur, S.; Efe, N.; Zararsiz, A.; Arikan, P.; Mutlu, R. H.

    2005-02-01

    Alloying effects on the K-shell fluorescence yield ωK of nickel in Ni-Si binary alloy system have been studied by energy dispersive X-ray fluorescence. It is found that ωK increases from pure Ni to Ni 2Si and then decreases from Ni 2Si to NiSi. These results are discussed in terms of d-occupation number on the Ni site and it is concluded that electronic configuration as a result of p-d hybridization explain qualitatively the observed variation of ωK in Ni-Si alloys.

  5. Flexible bottom-emitting white organic light-emitting diodes with semitransparent Ni/Ag/Ni anode.

    Science.gov (United States)

    Koo, Ja-Ryong; Lee, Seok Jae; Lee, Ho Won; Lee, Dong Hyung; Yang, Hyung Jin; Kim, Woo Young; Kim, Young Kwan

    2013-05-06

    We fabricated a flexible bottom-emitting white organic light-emitting diode (BEWOLED) with a structure of PET/Ni/Ag/Ni (3/6/3 nm)/ NPB (50 nm)/mCP (10 nm)/7% FIrpic:mCP (10 nm)/3% Ir(pq)(2) acac:TPBi (5 nm)/7% FIrpic:TPBi (5 nm)/TPBi (10 nm)/Liq (2 nm)/ Al (100 nm). To improve the performance of the BEWOLED, a multilayered metal stack anode of Ni/Ag/Ni treated with oxygen plasma for 60 sec was introduced into the OLED devices. The Ni/Ag/Ni anode effectively enhanced the probability of hole-electron recombination due to an efficient hole injection into and charge balance in an emitting layer. By comparing with a reference WOLED using ITO on glass, it is verified that the flexible BEWOLED showed a similar or better electroluminescence (EL) performance.

  6. When NiO@Ni Meets WS2 Nanosheet Array: A Highly Efficient and Ultrastable Electrocatalyst for Overall Water Splitting.

    Science.gov (United States)

    Wang, Dewen; Li, Qun; Han, Ce; Xing, Zhicai; Yang, Xiurong

    2018-01-24

    The development of low-cost, high-efficiency, and stable bifunctional electrocatalysts toward the hydrogen evolution reaction (HER) and oxygen evolution reaction (OER) is of paramount importance for large-scale water splitting. Here, we develop a new strategy for the first design and synthesis of a NiO@Ni decorated WS 2 nanosheet array on carbon cloth (NiO@Ni/WS 2 /CC) composite. This composite serves as a unique three-dimensional (3D) synergistic electrocatalyst that not only combines the intrinsic properties of individual NiO@Ni and WS 2 , but also exhibits significantly improved HER and OER activities when compared to that of pure NiO@Ni and WS 2 . This electrocatalyst possesses Pt-like activity for HER and exhibits better OER performance than that for commercial RuO 2 , as well as demonstrating superior long-term durability in alkaline media. Furthermore, it enables an alkaline electrolyzer with a current density of 10 mA cm -2 at a cell voltage as 1.42 V, which is the lowest one among all reported values to date. The excellent performance is mainly attributed to the unique 3D configuration and multicomponent synergies among NiO, Ni, and WS 2 . Our findings provide a new idea to design advanced bifunctional catalysts for water splitting.

  7. Nanocrystalline Ni-Co Alloy Synthesis by High Speed Electrodeposition

    OpenAIRE

    Idris, Jamaliah; Christian, Chukwuekezie; Gaius, Eyu

    2013-01-01

    Electrodeposition of nanocrystals is economically and technologically viable production path for the synthesis of pure metals and alloys both in coatings and bulk form. The study presents nanocrystalline Ni-Co alloy synthesis by high speed electrodeposition. Nanocrystalline Ni-Co alloys coatings were prepared by direct current (DC) and deposited directly on steel and aluminum substrates without any pretreatment, using high speed electrodeposition method. The influence of the electrolysis par...

  8. Layer-by-layer composite film of nickel phthalocyanine and montmorillonite clay for synergistic effect on electrochemical detection of dopamine

    Science.gov (United States)

    de Lucena, Nathalia C.; Miyazaki, Celina M.; Shimizu, Flávio M.; Constantino, Carlos J. L.; Ferreira, Marystela

    2018-04-01

    Dopamine (DA) abnormal levels are related to diseases which makes important the development of fast, reliable, low-cost and sensitive devices for diagnosis and pharmaceutical controls. Nanostructured film composite of sodium montmorillonite clay (Na+MMT) and nickel phthalocyanine (NiTsPc) was self-assembled by layer-by-layer (LbL) technique and applied as electrochemical sensor for DA in the presence of common natural interferents as ascorbic acid (AA) and uric acid (UA). Three different LbL architecture films were investigated: LbL films of clay (PEI/Na+MMT) and phthalocyanine (PEI/NiTsPc) in a bilayer structure with a conventional polyelectrolyte (PEI) and a composite film formed by both materials to verify the synergistic effect in the LbL film in a quadri-layer assembly (PEI/Na+MMT/PEI/NiTsPc). Structural characterization indicated molecular level interactions between the layers forming the LbL films. The ITO/(PEI/Na+MMT/PEI/NiTsPc)10 electrode exhibited a LOD of 1.0 μmol L-1 and linear range 5-150 μmol L-1.

  9. In-situ conversion of rGO/Ni2P composite from GO/Ni-MOF precursor with enhanced electrochemical property

    Science.gov (United States)

    Lv, Zijian; Zhong, Qin; Bu, Yunfei

    2018-05-01

    Owing to the metalloid characteristic and superior electrical conductivity, the metal phosphides have received increasing interests in energy storage systems. Here, xrGO/Ni2P composites are successfully synthesized via an In-situ phosphorization process with GO/Ni-MOF as precursors. Compared to pure Ni2P, the xrGO/Ni2P composites appear enhanced electrochemical properties in terms of the specific capacitance and cycling performance as electrodes for supercapacitors. Especially, the 2rGO/Ni2P electrode shows a highest specific capacitance of 890 F g-1 at 1 A g-1 among the obtained composites. The enhancement can be attributed to the inherited structure from Ni-MOF and the well assembled of rGO and Ni2P through the In-situ conversion process. Moreover, when applied as positive electrode in a hybrid supercapacitor, an energy density of 35.9 W h kg-1 at a power density of 752 W kg-1 has been achieved. This work provides an In-situ conversion strategy for the synthesis of rGO/Ni2P composite which might be a promising electrode material for SCs.

  10. Preparation of Ni(OH)2-graphene sheet-carbon nanotube composite as electrode material for supercapacitors

    International Nuclear Information System (INIS)

    Liu, Y.F.; Yuan, G.H.; Jiang, Z.H.; Yao, Z.P.; Yue, M.

    2015-01-01

    Highlights: • CNT is introduced into graphene to prevent restacking by solvothermal reaction. • Ethanol as a low cost and green solvent is used in solvothermal reaction. • Ni(OH) 2 nanosheets were chemically precipitated into GS-CNT to increase the capacitance. - Abstract: Ni(OH) 2 -graphene sheet-carbon nanotube composite was prepared for supercapacitance materials through a simple two-step process involving solvothermal synthesis of graphene sheet-carbon nanotube composite in ethanol and chemical precipitation of Ni(OH) 2 . According to N 2 adsorption/desorption analysis, the Brunauer–Emmett–Teller surface area of graphene sheet-carbon nanotube composite (109.07 m 2 g −1 ) was larger than that of pure graphene sheets (32.06 m 2 g −1 ), indicating that the added carbon nanotubes (15 wt.%) could prevent graphene sheets from restacking in the solvothermal reaction. The results of field emission scanning electron microscopy and transmission electron microscopy showed that Ni(OH) 2 nanosheets were uniformly loaded into the three-dimensional interconnected network of graphene sheet-carbon nanotube composite. The microstructure enhanced the rate capability and utilization of Ni(OH) 2 . The specific capacitance of Ni(OH) 2 -graphene sheet-carbon nanotube composite was 1170.38 F g −1 at a current density of 0.2 A g −1 in the 6 mol L −1 KOH solution, higher than those provided by pure Ni(OH) 2 (953.67 Fg −1 ) and graphene sheets (178.25 F g −1 ). After 20 cycles at each current density (0.2, 0.4, 0.6, 0.8, 1.0 and 1.2 A g −1 ), the capacitance of Ni(OH) 2 -graphene sheet-carbon nanotube composite decreased 26.96% of initial capacitance compared to 74.52% for pure Ni(OH) 2

  11. Properties of pure nickel after long term exposures to LiOH and vacuum at 775 K

    Science.gov (United States)

    Whittenberger, J. D.

    1991-01-01

    The solid to liquid phase transformation of LiOH at 744.3 K is considered to be an ideal candidate thermal energy storage (TES) mechanism for a Rankine heat engine based solar dynamic system operating at approximately 682 K. While pure nickel is thought to be a suitable containment material for LiOH, long term containment is of concern because molten hydroxides are usually corrosive. Two commercially pure nickel alloys, Ni-200 and Ni-201, were exposed to molten LiOH, its vapor, and vacuum at 775 K for periods ranging from 50 to 5000 h, and simple mechanical property measurements (77 to 900 K tensile and 750 K creep rupture) of exposed alloys were undertaken. The mechanical property test procedures are described and tabular lists of the test data are presented.

  12. Thermal stability study of the insulator layer in NiFe/CoFe/Al2O3/Co spin-dependent tunnel junction

    International Nuclear Information System (INIS)

    Liao, C.C.; Ho, C.H.; Huang, R.-T.; Chen, F.-R.; Kai, J.J.; Chen, L.-C.; Lin, M.-T.; Yao, Y.D.

    2002-01-01

    Spin-dependent tunnel junction, NiFe/CoFe/Al 2 O 3 /Co//Si, was fabricated to investigate the thermal stability induced diffusion behaviors. The interfacial diffusion causes the degradation of the ratio of the TMR, the enhancement of the switching field of the two magnetic electrodes, the thickness decrease of the insulator layer, and the increase of the interfacial roughness. The outward diffusion of oxygen from the insulator layer is faster than that of aluminum for samples annealed below 400 deg. C. The degradation of the ratio of TMR is attributed to the disturbance of the spin polarization in the magnetic layers, and the increase of the pinholes and spin-flip effect in the insulator layer. The relative roughness between the two interfaces of the insulator induces the surface magnetic dipoles, and hence, increases the switching field of the ferromagnetic electrodes

  13. Determination of metallic impurities in nuclearly pure uranium compounds by electrothermal spectrophotometry

    International Nuclear Information System (INIS)

    Franco, M.B.

    1986-01-01

    Atomic absorption spectrometry, with electrothermal atomization, has been used for the determination of Al, Cd, Cr, Fe, Mn and Ni in uranium oxide standards. The analysis were performed without sample dissolution and without uranium chemical separation. This technique is adequate for the qualification of nuclearly pure uranium, according to the standard specifications. (Author) [pt

  14. Oxidation of Ni(Pt)Si by molecular vs. atomic oxygen

    International Nuclear Information System (INIS)

    Manandhar, Sudha; Copp, Brian; Kelber, J.A.

    2008-01-01

    X-ray photoelectron spectroscopy (XPS) has been used to characterize the oxidation of a clean Ni(Pt)Si surface under two distinct conditions: exposure to a mixed flux of atomic and molecular oxygen (O + O 2 ; P O+O 2 = 5 x 10 -6 Torr) and pure molecular oxygen (O 2 ; P O 2 = 10 -5 Torr) at ambient temperatures. Formation of the clean, stoichiometric (nickel monosilicide) phase under vacuum conditions results in the formation of a surface layer enriched in PtSi. Oxidation of this surface in the presence of atomic oxygen initially results in formation of a silicon oxide overlayer. At higher exposures, kinetically limited oxidation of Pt results in Pt silicate formation. No passivation of oxygen uptake of the sample is observed for total O + O 2 exposure 4 L, at which point the average oxide/silicate overlayer thickness is 23 (3) A (uncertainty in the last digit in parentheses). In contrast, exposure of the clean Ni(Pt)Si surface to molecular oxygen only (maximum exposure: 5 x 10 5 L) results in slow growth of a silicon oxide overlayer, without silicate formation, and eventual passivation at a total average oxide thickness of 8(1) A, compared to a oxide average thickness of 17(2) A (no silicate formation) for the as-received sample (i.e., exposed to ambient.) The aggressive silicon oxidation by atomic oxygen, results in Ni-rich silicide formation in the substrate and the kinetically limited oxidation of the Pt

  15. A method of producing small grain Ru intermediate layers for perpendicular magnetic media

    International Nuclear Information System (INIS)

    Yuan Hua; Qin Yueling; Laughlin, David E.

    2008-01-01

    NiAl + SiO 2 thin films were used as a grain size reducing seedlayer for cobalt alloy granular perpendicular magnetic recording media. The effect of this NiAl + SiO 2 seedlayer on the microstructure and crystalline orientation of Ru intermediate layer has been investigated. By co-sputtering the composite NiAl + SiO 2 seedlayer, the smallest average grain diameter of NiAl was significantly reduced to about 2.5 nm. The grain size of the subsequent Ru intermediate layer was reduced to about 4 nm. X-ray diffraction results indicate an epitaxial orientation relationship of NiAl (110) // Ru (0002) between the two layers. Moreover, significant improvement of this epitaxial relationship was developed, which produced narrow c-axis distribution of the Ru intermediate layer with small grain size. The addition of the NiAl + SiO 2 seedlayer is a very promising approach to reduce the Ru intermediate layer grain size and eventually the magnetic layer grain size for perpendicular magnetic recording media without deterioration of other properties of thin films

  16. An investigation of the oxidized Ni/InAs interface

    Energy Technology Data Exchange (ETDEWEB)

    Venter, A., E-mail: andre.venter@nmmu.ac.z [Department of Physics, Nelson Mandela Metropolitan University, PO Box 77000, Port Elizabeth 6031 (South Africa); Botha, J.R. [Department of Physics, Nelson Mandela Metropolitan University, PO Box 77000, Port Elizabeth 6031 (South Africa); Swart, H.C. [Department of Physics, University of the Free State, PO Box 339, Bloemfontein 9300 (South Africa); Naidoo, S.; Olivier, E.J. [Department of Physics, Nelson Mandela Metropolitan University, PO Box 77000, Port Elizabeth 6031 (South Africa)

    2009-12-01

    Ni was resistively deposited onto bulk InAs and subsequently oxidized in an O{sub 2} atmosphere. The anneal temperature and time were 450 deg. C and 2.5 h, respectively. X-ray diffraction of the oxidized Ni/InAs sample revealed the formation of In{sub 3}Ni{sub 2} and In{sub 2}O{sub 3} on the front suggesting inter diffusion of In, Ni and O. NiO was not detected by X-ray diffraction. In a preliminary study, using glass as a substrate, NiO readily formed when using these oxidation parameters. Conductivity measurements of the oxidized Ni/InAs surface revealed a conducting front and insulating rear surface while TEM of the Ni/InAs interface revealed an intermediate amorphous diffusion zone between the 'oxidized' Ni layer and the bulk InAs. A closer investigation of the intermediate layer supports the X-ray diffraction results, suggesting compound formation due to diffusion of oxygen and nickel into the substrate, and out-diffusion of In and As from the bulk of the sample. AES was used to further elucidate these results.

  17. Structural features in Ni-Al alloys

    International Nuclear Information System (INIS)

    Abylkalykova, R.B.; Kveglis, L.I.; Rakhimova, U.A.; Nasokhova, Sh.B.; Tazhibaeva, G.B.

    2007-01-01

    Purpose of the work is study of structural transformations under diverse memory effect in Ni-Al alloys. Examination were conducted in following composition samples: Ni -75 at.% and Al - 25 at.%. The work is devoted to clarification reasons both formation atom-ordered structures in inter-grain boundaries of bulk samples under temperature action and static load. Revealed inter-grain inter-boundary layers in Ni-Al alloy both bulk and surface state have complicated structure

  18. Cutting NiTi with Femtosecond Laser

    Directory of Open Access Journals (Sweden)

    L. Quintino

    2013-01-01

    Full Text Available Superelastic shape memory alloys are difficult to machine by thermal processes due to the facility for Ti oxidation and by mechanical processes due to their superelastic behavior. In this study, femtosecond lasers were tested to analyze the potential for machining NiTi since femtosecond lasers allow nonthermal processing of materials by ablation. The effect of processing parameters on machining depth was studied, and material removal rates were computed. Surfaces produced were analyzed under SEM which shows a resolidified thin layer with minimal heat affected zones. However, for high cutting speeds, that is, for short interaction times, this layer was not observed. A depletion of Ni was seen which may be beneficial in biomedical applications since Ni is known to produce human tissue reactions in biophysical environments.

  19. The Ni-YSZ interface - Structure, composition and electrochemical properties at 1000 deg. C

    Energy Technology Data Exchange (ETDEWEB)

    Vels Jensen, Karin

    2002-06-01

    The anode/electrolyte interface in solid oxide fuel cells (SOFC) is known to cause electrical losses. Geometrically simple Ni/Yttria-stabilised zirconia (YSZ) interfaces were examined to gain information on the structural and chemical changes occurring during experiments at 1000 deg. C in an atmosphere of 97% H2/3% H{sub 2}O. Electrochemical impedance spectroscopy at open circuit voltage (OCV) and at anodic and cathodic polarisation (100 mV) was performed. A correlation of the electrical data with the structure development and the chemical composition was attempted. Nickel wires with different impurity content (99.8% Ni and 99.995% Ni) were used to examine the impact of impurities on the polarisation resistance and contact area morphology. The electro polished nickel wires were pressed against a polished 8 mol% YSZ surface. Extensive structural changes from a flat interface to a hill and valley structure were found to occur in the contact area with the impure nickel wire, and a ridge of impurities was built along the rim of the contact area. Impurity particles in the interfacial region were also observed. The impurity phase was described as an alkali silicate glassy phase. No differences were found between polarised and non-polarised samples. With pure nickel wires, however, the microstructures depended on the polarisation/non-polarisation conditions. At non-polarised conditions a hill and valley type structure was found. Anodic polarisation produced an up to 1 {mu}m thick interface layer consisting of nano-sized YSZ particles with some Ni present. At cathodic polarisation both a granulated structure and a hill and valley structure resembling the structure of non-polarised samples were found. Small impurity ridges were surrounding the contact areas on non-polarised and cathodically polarised samples. TOF-SIMS and XPS analyses showed the presence of impurities in both the impure and pure contact areas. The impedance spectroscopy revealed that depending on the

  20. Electrochemical properties of rapidly solidified Si-Ti-Ni(-Cu) base anode for Li-ion rechargeable batteries

    Science.gov (United States)

    Kwon, Hye Jin; Sohn, Keun Yong; Park, Won-Wook

    2013-11-01

    In this study, rapidly solidified Si-Ti-Ni-Cu alloys have been investigated as high capacity anodes for Li-ion secondary batteries. To obtain nano-sized Si particles dispersed in the inactive matrix, the alloy ribbons were fabricated using the melt spinning process. The thin ribbons were pulverized using ball-milling to make a fine powder of ˜ 4 µm average size. Coin-cell assembly was carried out under an argon gas in a glove box, in which pure lithium was used as a counter-electrode. The cells were cycled using the galvanostatic method in the potential range of 0.01 V and 1.5 V vs. Li/Li+. The microstructure and morphology were examined using an x-ray diffractometer, Field-Emission Scanning Electron Microscopy and High Resolution Transmission Electron Microscopy. Among the anode alloys, the Si70Ti15Ni15 electrodes had the highest discharge capacity (974.1 mAh/g) after the 50th cycle, and the Si60Ti16Ni16Cu8 electrode showed the best coulombic efficiency of ˜95.9% in cyclic behavior. It was revealed that the Si7Ni4Ti4 crystal phase coexisting with an amorphous phase, could more efficiently act as a buffer layer than the fully crystallized Si7Ni4Ti4 phase. Consequently, the electrochemical properties of the anode materials pronouncedly improved when the nano-sized primary Si particle was dispersed in the inactive Si7Ni4Ti4-based matrix mixed with an amorphous structure.

  1. Design and fabrication of Ni nanowires having periodically hollow nanostructures

    Science.gov (United States)

    Sada, Takao; Fujigaya, Tsuyohiko; Nakashima, Naotoshi

    2014-09-01

    We propose a concept for the design and fabrication of metal nanowires having periodically hollow nanostructures inside the pores of an anodic aluminum oxide (AAO) membrane using a sacrificial metal. In this study, nickel (Ni) and silver (Ag) were used as the base metal and the sacrificial metal, respectively. Alternating an applied potential between -0.4 and -1.0 V provided alternatively deposited Ni and Ag segments in a Ni-Ag `barcode' nanowire with a diameter of 18 or 35 nm. After etching away the Ag segments, we fabricated Ni nanowires with nanopores of 12 +/- 5.3 nm. Such nanostructure formation is explained by the formation of a Ni shell layer over the surface of the Ag segments due to the strong affinity of Ni2+ for the interior surfaces of AAO. The Ni shell layer allows the Ni segments to remain even after dissolution of the Ag segments. Because the electroplating conditions can be easily controlled, we could carefully adjust the size and pitch of the periodically hollow nanospaces. We also describe a method for the fabrication of Ni nanorods by forming an Ag shell instead of a Ni shell on the Ni-Ag barcode nanowire, in which the interior of the AAO surfaces was modified with a compound bearing a thiol group prior to electroplating.We propose a concept for the design and fabrication of metal nanowires having periodically hollow nanostructures inside the pores of an anodic aluminum oxide (AAO) membrane using a sacrificial metal. In this study, nickel (Ni) and silver (Ag) were used as the base metal and the sacrificial metal, respectively. Alternating an applied potential between -0.4 and -1.0 V provided alternatively deposited Ni and Ag segments in a Ni-Ag `barcode' nanowire with a diameter of 18 or 35 nm. After etching away the Ag segments, we fabricated Ni nanowires with nanopores of 12 +/- 5.3 nm. Such nanostructure formation is explained by the formation of a Ni shell layer over the surface of the Ag segments due to the strong affinity of Ni2+ for the

  2. Nonvolatile memory characteristics influenced by the different crystallization of Ni-Si and Ni-N nanocrystals

    International Nuclear Information System (INIS)

    Chen, W.-R.; Yeh, J.-L.; Chang, C.-Y.; Chang, T.-C.; Chen, S.-C.

    2008-01-01

    The formation of Ni-Si and Ni-N nanocrystals by sputtering a Ni 0.3 Si 0.7 target in argon and nitrogen environment were proposed in this paper. A transmission electron microscope analysis shows the nanocrystals embedded in the nitride layer. X-ray photoelectron spectroscopy and x-ray diffraction also offer the chemical material analysis of nanocrystals with surrounding dielectric and the crystallization of nanocrystals for different thermal annealing treatments. Nonvolatile Ni-Si nanocrystal memories reveal superior electrical characteristics for charge storage capacity and reliability due to the improvement of thermal annealing treatment. In addition, we used energy band diagrams to explain the significance of surrounding dielectric for reliability

  3. Electrodeposition and properties of Zn-Ni-CNT composite coatings

    International Nuclear Information System (INIS)

    Praveen, B.M.; Venkatesha, T.V.

    2009-01-01

    Zn-Ni-CNT composite coatings were prepared by electrodeposition from a sulphate bath. The effect of CNTs on the corrosion behavior, wear resistance and hardness of the composite coatings was investigated. Their corrosion properties were evaluated by polarization, impedance, weight loss and salt spray tests. The CNT particles inclusion improved the corrosion resistance, hardness and wear resistance of the coating. The grain size of the composite coating was smaller than that of a pure Zn-Ni coating with the same Zn/Ni ratio. Scanning electron microscope images and X-ray diffraction patterns of coating revealed its fine-grain nature.

  4. High-temperature brazing of X5CrNi18 10 and NiCr20TiAl using the atmospherically plasma-sprayed L-Ni2 filler metal

    International Nuclear Information System (INIS)

    Wielage, B.; Drozak, J.

    1992-01-01

    The hybrid-technological combination of the atmospheric plasma spraying for the application of a high-temperature filler metal followed by a brazing process was analyzed in terms of structure and mechanical properties of X5CrNi18 10 and NiCr20TiAl brazing joints. The thickness of the filler metal layer was minimized at [de

  5. Wetting - Dewetting Transitions of Au/Ni Bilayer Films

    Science.gov (United States)

    Cen, Xi

    Thin films deposited at low temperatures are often kinetically constrained and will dewet the underlying substrate when annealed. Solid state dewetting is driven by the minimization of the total free energy of thin film-substrate interface and free surface, and mostly occurs through surface diffusion. Dewetting is a serious concern in microelectronics reliability. However, it can also be utilized for the self-assembly of nanostructures with potentials in storage, catalysis, or transistors. Therefore, a fundamental understanding of the dewetting behavior of thin metal films is critical for improving the thermal stability of microelectronics and controlling the order of self-assembled nanostructures. Mechanisms for dewetting of single layer films have been studied extensively. However little work has been reported on multilayer or alloyed thin films. In the thesis, the solid state dewetting of Au/Ni bilayer films deposited on SiO2/Si substrates was investigated by scanning electron microscopy (SEM), transmission electron microscopy (TEM) and aberration corrected scanning TEM (STEM). Ex-situ SEM and TEM studies were performed with in-situ TEM heating characterization to identify the mechanisms during the dewetting process of Au/Ni bilayer films. The solid state dewetting of Au/Ni bilayer films from SiO2/Si substrates exhibits both homogeneous and localized dewetting of Ni and long-edge retraction for Au under isothermal annealing condition. The top Au layer retracts up to 1 mm from the edge of the substrate wafer to reduce the energetically unfavored Au/Ni interface. In contrast, Ni dewets and agglomerates locally due to its limited diffusivity compared to Au. Film morphology and local chemical composition varies significantly across hundreds of microns along the direction normal to the retracting edge. Besides long range edge receding, localized dewetting shows significant changes in film morphology and chemical distribution. Both Au and Ni shows texturing. Despite

  6. Effect of γ-(Fe,Ni) crystal-size stabilization in Fe-Ni-B amorphous ribbon

    Science.gov (United States)

    Gorshenkov, M. V.; Glezer, A. M.; Korchuganova, O. A.; Aleev, A. A.; Shurygina, N. A.

    2017-02-01

    The effect of stabilizing crystal size in a melt-quenched amorphous Fe50Ni33B17 ribbon is described upon crystallization in a temperature range of 360-400°C. The shape, size, volume fraction, and volume density have been investigated by transmission electron microscopy and X-ray diffraction methods. The formation of an amorphous layer of the Fe50Ni29B21 compound was found by means of atomic-probe tomography at the boundary of the crystallite-amorphous phase. The stabilization of crystal sizes during annealing is due to the formation of a barrier amorphous layer that has a crystallization temperature that exceeds the crystallization temperature of the matrix amorphous alloy.

  7. Improved performance of LaNi0.6Fe0.4O3 solid oxide fuel cell cathode by application of a thin interface cathode functional layer

    DEFF Research Database (Denmark)

    Molin, Sebastian; Jasinski, Piotr Z.

    2017-01-01

    In this work, novel functional layers were prepared by a low temperature spray pyrolysis method on the oxygen side of the solid oxide cells. Thin layers of Ce0.8Gd0.2O2 and LaNi0.6Fe0.4O3 are prepared between the electrolyte and the porous oxygen electrode. Additionally the influence of the sprayed...... ceria barrier layer on the zirconia based electrolyte with the new layers is evaluated. Impedance spectroscopy results show improvement in contact between the electrolyte and the porous cathode electrode. Additionally, electrochemical performance of the cathode is improved, as evidenced by a lowered...

  8. Structure determination of the ordered (2 × 1) phase of NiSi surface alloy on Ni(111) using low-energy electron diffraction

    Science.gov (United States)

    Sazzadur Rahman, Md.; Amirul Islam, Md.; Saha, Bidyut Baran; Nakagawa, Takeshi; Mizuno, Seigi

    2015-12-01

    The (2 × 1) structure of the two-dimensional nickel silicide surface alloy on Ni(111) was investigated using quantitative low-energy electron diffraction analysis. The unit cell of the determined silicide structure contains one Si and one Ni atom, corresponding to a chemical formula of NiSi. The Si atoms adopt substitutional face-centered cubic hollow sites on the Ni(111) substrate. The Ni-Si bond lengths were determined to be 2.37 and 2.34 Å. Both the alloy surface and the underlying first layers of Ni atoms exhibit slight corrugation. The Ni-Si interlayer distance is smaller than the Ni-Ni interlayer distance, which indicates that Si atoms and underlying Ni atoms strongly interact.

  9. Tunable photoelectric response in NiO-based heterostructures by various orientations

    Science.gov (United States)

    Luo, Yidong; Qiao, Lina; Zhang, Qinghua; Xu, Haomin; Shen, Yang; Lin, Yuanhua; Nan, Cewen

    2018-02-01

    We engineered various orientations of NiO layers for NiO-based heterostructures (NiO/Au/STO) to investigate their effects on the generation of hot electrons and holes. Our calculation and experimental results suggested that bandgap engineering and the orientation of the hole transport layer (NiO) were crucial elements for the optimization of photoelectric responses. The (100)-orientated NiO/Au/STO achieved the highest photo-current density (˜30 μA/cm2) compared with (111) and (110)-orientated NiO films, which was attributed to the (100) films's lowest effective mass of photogenerated holes (˜1.82 m0) and the highest efficiency of separating and transferring electron-holes of the (100)-orientated sample. Our results opened a direction to design a high efficiency photoelectric solar cell.

  10. Microwave-irradiated preparation of reduced graphene oxide-Ni nanostructures and their enhanced performance for catalytic reduction of 4-nitrophenol

    Energy Technology Data Exchange (ETDEWEB)

    Qiu, Hanxun, E-mail: hxqiu@usst.edu.cn; Qiu, Feilong; Han, Xuebin; Li, Jing; Yang, Junhe, E-mail: jhyang@usst.edu.cn

    2017-06-15

    Highlights: • Nickel nanoparticle-decorated reduced graphene-oxide nanostructures were prepared by an environmentally friendly, one-pot strategy via an efficient microwave irradiation approach. • Upon microwave irradiation, the composites could be prepared within only a few hundred seconds, much faster than using the widely used traditional hydrothermal methods that may take tens of hours generally. • The nanostructure exhibits superior catalytic activity and selectivity towards transforming the highly toxic nitroaromatic compounds to industrially useful intermediates • The corresponding kinetic reaction rate constant (κ) is even four-fold compared to pure Ni nanoparticles. - Abstract: Here we report an environmentally friendly, one-pot strategy toward preparation of nickel nanoparticle-decorated reduced graphene-oxide (Ni-RGO) nanostructures, by employing Ni(AC){sub 2} as nickel source and ethylene glycol as both solvent and reducing agent via a facile microwave irradiation heating approach. The results show that Ni nanoparticles with an average diameter of around 40 nm are homogeneously anchored onto the surface of RGO sheets. As compared to the pure Ni nanoparticles and RGO sheets, Ni-RGO composites with over 64 wt% loading of Ni nanoparticles possess superior catalytic activities and selectivity toward the reduction of 4-nitrophenol. The corresponding kinetic reaction rate constant (defined as κ) is even four-fold compared to pure Ni nanoparticles. Such promising composites show great potential for friendly treatment of industrial waste containing nitrophenol in a simple, sustainable and green way.